Effect of alloying elements on the shape memory properties of ductile Cu-Al-Mn alloys

International Nuclear Information System (INIS)

Sutou, Y.; Kainuma, R.; Ishida, K.

1999-01-01

The effect of alloying elements on the M s temperature, ductility and the shape memory properties of Cu-Al-Mn ductile shape memory (SM) alloys was investigated by differential scanning calorimetry, cold-rolling and tensile test techniques. It was found that the addition of Au, Si and Zn to the Cu 73 -Al 17 -Mn 10 alloy stabilized the martensite (6M) phase increasing the M s temperature, while the addition of Ag, Co, Cr, Fe, Ni, Sn and Ti decreased the stability of the martensite phase, decreasing the M s temperature. The SM properties were improved by the addition of Co, Ni, Cr and Ti. (orig.)

Microstructure and Mechanical Characterization of a Dissimilar Friction-Stir-Welded CuCrZr/CuNiCrSi Butt Joint

Directory of Open Access Journals (Sweden)

Youqing Sun

2018-05-01

Full Text Available Dissimilar CuNiCrSi and CuCrZr butt joints were successfully frictionstirwelded at constant welding speed of 150 mm/min and rotational speed of 1400 rpm with the CuCrZr alloy or the CuNiCrSi alloy located on the advancing side (AS. The microstructure and mechanical properties of joints were investigated. When the CuCrZr alloy was located on the AS, the area of retreating material in the nugget zone was a little bigger. The Cr solute-rich particles were found in the nugget zone on CuCrZr side (CuCrZr-NZ while a larger density of solute-rich particles identified as the concentration of Cr and Si element was found in the nugget zone on CuNiCrSi side (CuNiCrSi-NZ. The Cr precipitates and δ-Ni2Si precipitates were found in the base metal on CuNiCrSi side (CuNiCrSi-BM but only Cr precipitates can be observed in the base metal on CuCrZr side (CuCrZr-BM. Precipitates were totally dissolved into Cu matrix in both CuCrZr-NZ and CuNiCrSi-NZ, which led to a sharp decrease in both micro-hardness and tensile strength from BM to NZ. When the CuNiCrSi was located on the AS, the tensile testing results showed the fracture occurred at the CuCrZr-NZ, while the fracture was found at the mixed zone of CuNiCrSi-NZ and CuCrZr-NZ for the other case.

Essential trace (Zn, Cu, Mn and toxic (Cd, Pb, Cr elements in the liver of birds from Eastern Poland

Directory of Open Access Journals (Sweden)

Komosa A.

2012-01-01

Full Text Available We have focused our study on the concentrations of essential heavy metals (Zn, Cu and Mn and non-essential trace metals (Pb, Cd and Cr in the livers of birds from Eastern Poland. The largest mean amount of Zn - as much as 279 mg/kg dry mass (d.m. - was found in mute swans. However, only in one of the analysed buzzard specimens the concentration of Zn, found to be 664 mg/kg d.m., exceeded the level indicative of poisoning for this element. Birds specializing in catching rodents accumulated Mn in their livers in a very narrow range of concentrations, around 5.0 mg/kg d.m. on average. The range of mean Mn concentrations (around 6.5 mg/kg d.m. was also found to be narrow for piscivorous birds. The highest mean levels of Pb were found in mute swans (2.7 mg/kg d.m., and the highest levels of Cd (2.0 mg/kg d.m. for rooks. Concentrations of total Cr above detection level were found in 22 specimens (53.7%, and concentration values were highest for rooks. Analyses showed that the concentrations of biogenic elements did not exceed the levels indicative of poisoning (except in one specimen. The study demonstrated that lead shots remain a hazard to water ecosystems. Pb, Cd and Cr levels in the livers of omnivorous and piscivorous species indicate the permanent presence of these elements in the environment and may confirm the thesis about the growing role of electronic waste, including metallic e-waste, in the emission of the total amount of contamination with these elements.

Creep and Oxidation Behavior of Modified CF8C-Plus with W, Cu, Ni, and Cr

Science.gov (United States)

Unocic, Kinga A.; Dryepondt, Sebastien; Yamamoto, Yukinori; Maziasz, Philip J.

2016-04-01

The microstructures of modified CF8C-Plus (Fe-19Cr-12Ni-0.4W-3.8Mn-0.2Mo-0.6Nb-0.5Si-0.9C) with W and Cu (CF8CPWCu) and CF8CPWCu enhanced with 21Cr + 15Ni or 22Cr + 17.5Ni were characterized in the as-cast condition and after creep testing. When imaged at lower magnifications, the as-cast microstructure was similar among all three alloys as they all contained a Nb-rich interdendritic phase and Mn-based inclusions. Transmission electron microscopy (TEM) analysis showed the presence of nanoscale Cu-rich nanoprecipitates distributed uniformly throughout the matrix of CF8CPWCu, whereas in CF8CPWCu22/17, Cu precipitates were found primarily at the grain boundaries. The presence of these nanoscale Cu-rich particles, in addition to W-rich Cr23C6, nanoscale Nb carbides, and Z-phase (Nb2Cr2N2), improved the creep strength of the CF8CPWCu steel. Modification of CF8CPWCu with Cr and Ni contents slightly decreased the creep strength but significantly improved the oxidation behavior at 1073 K (800 °C). In particular, the addition of 22Cr and 17.5Ni strongly enhanced the oxidation resistance of the stainless steel resulting in a 100 degrees or greater temperature improvement, and this composition provided the best balance between improving both mechanical properties and oxidation resistance.

A first principle study of phase stability, electronic structure and magnetic properties for Co{sub 2−x}Cr{sub x}MnAl Heusler alloys

Energy Technology Data Exchange (ETDEWEB)

Rached, H. [Laboratoire des Matériaux Magnétiques, Faculté des Sciences exactes, Université Djillali Liabès de Sidi Bel-Abbès, Sidi Bel-Abbès 22000 (Algeria); Rached, D., E-mail: rachdj@yahoo.fr [Laboratoire des Matériaux Magnétiques, Faculté des Sciences exactes, Université Djillali Liabès de Sidi Bel-Abbès, Sidi Bel-Abbès 22000 (Algeria); Khenata, R. [Laboratoire de Physique Quantique et de Modélisation Mathématique de la Matière, (LPQ3M), Université de Mascara, Mascara 29000 (Algeria); Abidri, B.; Rabah, M.; Benkhettou, N. [Laboratoire des Matériaux Magnétiques, Faculté des Sciences exactes, Université Djillali Liabès de Sidi Bel-Abbès, Sidi Bel-Abbès 22000 (Algeria); Omran, S. Bin [Department of Physics and Astronomy, College of Science, King Saud University, P.O.Box 2455, Riyadh 11451 (Saudi Arabia)

2015-04-01

The structural stabilities, electronic and magnetic properties of Co{sub 2−x}Cr{sub x}MnAl alloys with (x=0,1 and 2) were investigated using the full-potential linear muffin-tin orbital (FP-LMTO) method, in the framework of the density functional theory (DFT) within the generalized gradient approximation (GGA) for the exchange correlation functional. The ground state properties including lattice parameter, bulk modulus for the two considered crystal structures Hg{sub 2}CuTi-Type (X-Type) and Cu{sub 2}MnAl-Type (L2{sub 1}-Type) are calculated. The half-metallicity within ferromagnetic ground state starts to appear in CoCrMnAl and Cr2MnAl. In the objective for the proposition of the new HM-FM in the Full-Heusler alloys, our results classified CoCrMnAl as new HM-FM material with high spin polarization. - Highlights: • Based on DFT calculations, Co2-xCrxMnAl Heusler alloys have been investigated. • The magnetic phase stability was determined from the total energy calculations. • The LMTO calculations have classified CoCrMnAl as new HM-FM material with high spin polarization.

Cu-Cr Literature Review

Energy Technology Data Exchange (ETDEWEB)

Need, Ryan F. [Los Alamos National Laboratory

2012-08-09

Cu-Cr alloys are part of a class of face-centered cubic (FCC)-body-centered cubic (BCC) composites that includes similar alloys, such as Cu-Nb and Cu-Ta. When heavily deformed, these FCC-BCC materials create 'in situ' composites with a characteristic structure-nanoscale BCC filaments in a ductile FCC matrix. The strength of these composites is vastly greater than predicted by the rule of mixtures, and has been shown to be inversely proportional to the filament spacing. Lower raw materials costs suggest that Cu-Cr alloys may offer more economical solution to high-strength, high-conductivity wire than either their Nb or Ta counterparts. However, Cr is also more brittle and soluble in Cu than Nb or Ta. These qualities necessitate thermal treatments to remove solute atoms from the Cu matrix, improve conductivity, and maintain the ductility of the Cr filaments. Through the use of different thermomechanical processing routes or the addition of select dopants, alloys with strength in excess of 1 GPa at 70% IACS have been achieved. To date, previous research on Cu-Cr alloys has focused on a relatively small number of alloy compositions and processing methods while the effects of dopants and ageing treatments have only been studied independently. Consequently, there remains considerable opportunity for the development and optimization of these alloys as a leading high-strength, high-conductivity material.

Chemical shift of Mn and Cr K-edges in X-ray absorption ...

Indian Academy of Sciences (India)

particularly on Mn and Cr compounds (Ghatikar et al 1977;. Padalia and Nayak 1977; ... conventional X-ray sources and hence may lack reliability. 2. Experimental ..... with the result obtained by Hinge et al (2011) for Cu com- pounds and is ... Chem. 84 2200. Nietubyc R, Sobczak E and Attenkofer K E 2001 J. Alloys Compd.

Cr(III,Mn(II,Fe(III,Co(II,Ni(II,Cu(II and Zn(II Complexes with Diisobutyldithiocarbamato Ligand

Directory of Open Access Journals (Sweden)

Mohammad Tarique

2011-01-01

Full Text Available The synthesis of sulphur and nitrogen containing dithiocarbamato ligand derived from diisobutylamine as well as its coordination compounds with 3d series transition metals is presented. These synthesized compounds were characterized on the basis of elemental analysis, conductometric measurements and IR spectral studies. The analytical data showed the stoichiometry 1:2 and 1:3 for the compounds of the types ML2 {M=Mn(II, Co(II, Ni(II, Cu(II and Zn(II} and M'L3{M'=Cr(III and Fe(III} respectively. The conductometric measurements proved the non-electrolytic behaviour of all the compounds. The bidentate nature of dithiocarbamato moiety was confirmed on the basis of IR spectral data.

Electronic Topological Transitions in CuNiMnAl and CuNiMnSn under pressure from first principles study

Science.gov (United States)

Rambabu, P.; Kanchana, V.

2018-06-01

A detailed study on quaternary ordered full Heusler alloys CuNiMnAl and CuNiMnSn at ambient and under different compressions is presented using first principles electronic structure calculations. Both the compounds are found to possess ferromagnetic nature at ambient with magnetic moment of Mn being 3.14 μB and 3.35 μB respectively in CuNiMnAl and CuNiMnSn. The total magnetic moment for both the compounds is found to decrease under compression. Fermi surface (FS) topology change is observed in both compounds under pressure at V/V0 = 0.90, further leading to Electronic Topological Transitions (ETTs) and is evidenced by the anomalies visualized in density of states and elastic constants under compression.

Observations of a Cast Cu-Cr-Zr Alloy

Science.gov (United States)

Ellis, David L.

2006-01-01

Prior work has demonstrated that Cu-Cr-Nb alloys have considerable advantages over the copper alloys currently used in regeneratively cooled rocket engine liners. Observations indicated that Zr and Nb have similar chemical properties and form very similar compounds. Glazov and Zakharov et al. reported the presence of Cr2Zr in Cu-Cr-Zr alloys with up to 3.5 wt% Cr and Zr though Zeng et al. calculated that Cr2Zr could not exist in a ternary Cu-Cr-Zr alloy. A cast Cu-6.15 wt% Cr-5.25 wt% Zr alloy was examined to determine if the microstructure developed would be similar to GRCop-84 (Cu-6.65 wt% Cr-5.85 wt% Nb). It was observed that the Cu-Cr-Zr system did not form any Cr2Zr even after a thermal exposure at 875 C for 176.5 h. Instead the alloy consisted of three phases: Cu, Cu5Zr, and Cr.

Determination of Cr, Mn, Fe, Co, Ni, Cu, Zn and As in the Rimac River waters by x-ray fluorescence in total reflection; Determinacion de Cr, Mn, Fe, Co, Ni, Cu, Zn y As en aguas del Rio Rimac por fluorescencia de rayos-x en reflexion total

Energy Technology Data Exchange (ETDEWEB)

Tiznado, W [Universidad Nacional Federico Villarreal, Lima (Peru). Facultad de Ciencias Naturales y Matematicas, EP Quimica; Olivera, P [Instituto Peruano de Energia Nuclear, Lima (Peru). Departamento de Quimica

2002-07-01

Samples from thirteen stations of the Rimac River has been analyzed. Samples were performed during one-year-period (september 1998-august 1999), with a frequency of one sample per month. The X-ray fluorescence analysis in total reflection technique has been used in order to determine the Cr, Mn, Fe, Co, Ni, Cu, Zn and As elements on its dissolved phase. The results obtained show: relation of the presence of mining stations with the metal concentration level, specially in the Zn and Fe; As is present in concentrations above those of permissible maximum levels in some of the sampled stations; moreover, Ni and Cr, toxic elements, are found in very low concentrations. On the other hand, it has been proved that the analysis method used is useful as a monitoring tool of superficial water-quality due to its low detection limits and because of the fastness the analysis are made.

Phase relationships in Cu-rich corner of the Cu-Cr-Zr phase diagram

International Nuclear Information System (INIS)

Zeng, K.J.; Haemaelaeinen, M.; Lilius, K.

1995-01-01

In the available experimental information on the Cu-Cr-Zr ternary system, there exist different opinions concerning the phase relationships in the Cu-rich corner of Cu-Cr-Zr phase diagram. Glazov et al. and Zakharov et al. investigated the Cu-rich corner of the Cu-Cr-Zr phase diagram within the composition range up to 3.5 Cr and 3.5 Zr (wt. %). A quasi-eutectic reaction L → (Cu) + αCr 2 Zr was observed to occur at 1,020 C and several isothermal sections were constructed within the temperature range from 600 to 1,000 C to show the (Cu)-αCr 2 Zr two phase equilibrium. Therefore, a pseudobinary Cu-Cr 2 Zr system was supposed. Afterwards, Dawakatsu et al, Fedorov et al, and Kuznetsov et al studied the cu-rich corner of the phase diagram in a wider composition range up to 5 Cr and 20 Zr (at.%). Contrary to Glazov et al. and Zakharov et al., they found no Cr 2 Zr phase in their samples. Hence, the pseudobinary Cu-Cr 2 Zr system does not exist. In this study an experimental investigation is presented on the phase relationships in Cu-rich corner of the Cu-Cr-Zr phase diagram at 940 C in order to clear up the confusion

Health Risk Assessment of Fe, Mn, Cu, Cr in Drinking Water in some Wells and Springs of Shush and Andimeshk, Khuzestan Province, Southern Iran

Directory of Open Access Journals (Sweden)

Mohamad Sakizadeh

2016-02-01

Full Text Available Background: In the current study,the hazard quotient, the hazard index (HI and spatial variations of Fe,Mn,Cu and Cr in drinking water sources of Andimesk-Shush, Khuzestan Province, Southern Iranaquifer were assessed. Methods: We compared theconcentrations of aforementioned heavy metals in wells and springs inAndimeshk and Shush regions. The non-carcinogenic risk assessment of heavy metals was implemented usingUnited States Environmental Protection Agency (USEPA index.The spatial maps in the area were developed by geostatistical methods. Results: Mean concentrations of heavy metals in groundwater sources of the study area in decreasing order was as follows: Cu >Mn> Fe> Cr. Except for iron,mean heavy metal concentrations were higher than the standard levels. Manganese concentration in 41.5% of the samples exceeded the permissible limits. Copper was higher than the safety limit in 74% of the samples, and chromium in 54% of the cases. The spatial pattern of heavy metals concentrations indicated higher concentrations in the southern parts of the region. The mean hazard quotients of most samples for the four heavy metals were lower than one, indicating that there was no immediate threat due to the exposure to these heavy metals. The calculated accumulated hazards of these heavy metals produced different results, with hazard indices of higher than one. Conclusion: The accumulated hazard indicesfor the evaluated metals were higher than one, indicating that chronic ingestion of these waters threatens the health of local consumers on the long run.

First-principles spin-transfer torque in CuMnAs |GaP |CuMnAs junctions

Science.gov (United States)

Stamenova, Maria; Mohebbi, Razie; Seyed-Yazdi, Jamileh; Rungger, Ivan; Sanvito, Stefano

2017-02-01

We demonstrate that an all-antiferromagnetic tunnel junction with current perpendicular to the plane geometry can be used as an efficient spintronic device with potential high-frequency operation. By using state-of-the-art density functional theory combined with quantum transport, we show that the Néel vector of the electrodes can be manipulated by spin-transfer torque. This is staggered over the two different magnetic sublattices and can generate dynamics and switching. At the same time the different magnetization states of the junction can be read by standard tunneling magnetoresistance. Calculations are performed for CuMnAs |GaP |CuMnAs junctions with different surface terminations between the antiferromagnetic CuMnAs electrodes and the insulating GaP spacer. We find that the torque remains staggered regardless of the termination, while the magnetoresistance depends on the microscopic details of the interface.

Swelling of Fe-Mn and Fe-Cr-Mn alloys at high neutron fluence

International Nuclear Information System (INIS)

Garner, F.A.; Brager, H.R.

1986-06-01

Swelling data on neutron-irradiated simple Fe-Cr-Mn and Fe-Mn alloys, as well as commercial Fe-Cr-Mn base alloys are now becoming available at exposure levels approaching 50 dpa. The swelling rate decreases from the ∼1%/dpa found at lower exposures, probably due to the extensive formation of ferritic phases. As expected, commercial alloys swell less than the simple alloys

Manufacturing and High Heat Flux Testing of Brazed Flat-Type W/CuCrZr Plasma Facing Components

Science.gov (United States)

Lian, Youyun; Liu, Xiang; Feng, Fan; Chen, Lei; Cheng, Zhengkui; Wang, Jin; Chen, Jiming

2016-02-01

Water-cooled flat-type W/CuCrZr plasma facing components with an interlayer of oxygen-free copper (OFC) have been developed by using vacuum brazing route. The OFC layer for the accommodation of thermal stresses was cast onto the surface of W at a temperature range of 1150 °C-1200 °C in a vacuum furnace. The W/OFC cast tiles were vacuum brazed to a CuCrZr heat sink at 940 °C using the silver-free filler material CuMnSiCr. The microstructure, bonding strength, and high heat flux properties of the brazed W/CuCrZr joint samples were investigated. The W/Cu joint exhibits an average tensile strength of 134 MPa, which is about the same strength as pure annealed copper. High heat flux tests were performed in the electron beam facility EMS-60. Experimental results indicated that the brazed W/CuCrZr mock-up experienced screening tests of up to 15 MW/m2 and cyclic tests of 9 MW/m2 for 1000 cycles without visible damage. supported by National Natural Science Foundation of China (No. 11205049) and the National Magnetic Confinement Fusion Science Program of China (No. 2011GB110004)

Zeolite-encapsulated Co(II), Mn(II), Cu(II) and Cr(III) salen complexes as catalysts for efficient selective oxidation of benzyl alcohol

Science.gov (United States)

Li, F. H.; Bi, H.; Huang, D. X.; Zhang, M.; Song, Y. B.

2018-01-01

Co(II), Mn(II), Cu(II) and Cr(III) salen type complexes were synthesized in situ in Y zeolite by the reaction of ion-exchanged metal ions with the flexible ligand molecules that had diffused into the cavities. Data of characterization indicates the formation of metal salen complexes in the pores without affecting the zeolite framework structure, the absence of any extraneous species and the geometry of encapsulated complexes. The catalytic activity results show that Cosalcyen Y exhibited higher catalytic activity in the water phase selective oxidation of benzyl alcohol, which could be attributed to their geometry and the steric environment of the metal actives sites.

Moessbauer spectroscopy of Fe-Mn-Cu alloys

International Nuclear Information System (INIS)

Paduani, Clederson; Krause, Joao Carlos; Yoschida, M.I. Soares

2004-01-01

Full text: Although a continuous series of solid solutions exists between Cu and Mn, Fe and Cu are miscible only a few percent at higher temperatures. In moderately concentrated Cu-Mn alloys the Mn moments are bound to the long ranged antiferromagnetic order and the perpendicular components form an X-Y spin glass. Copper alloys are largely employed in various industrial applications. In this work we study the magnetic properties of iron-rich disordered Fe-Mn-Cu alloys with the bcc structure with the experimental techniques of X-ray diffraction (XRD), Moessbauer spectroscopy (MS) and thermogravimetry (TGA). We investigate the formation of a solid solution with the bcc structure as well as the effect of the composition on the structural and magnetic properties of these alloys. A Rietveld analysis of the XRD diffractograms indicate that all prepared samples are single phase and are well crystallized with a bcc structure. (author)

Mechanical properties and electrical conductivity of Cu-Cr and Cu-Cr-4% SiC nanocomposites for thermo-electric applications

International Nuclear Information System (INIS)

Mula, Suhrit; Sahani, Pankajini; Pratihar, S.K.; Mal, Siddhartha; Koch, Carl C.

2011-01-01

Highlights: → Ball-milled Cu-Cr and Cu-Cr-SiC nanopowders successfully consolidated by microwave sintering. → Addition of nanosize SiC in Cu-Cr leads to enhanced sintered density, wear and hardness. → A good combination of wear resistance, hardness and electrical conductivity resulted in Cu 94 Cr 6 -4% SiC. → Microwave suscepting SiC particles played a pivotal role in good densification retaining matrix grains 99 Cr 1 , Cu 94 Cr 6 , Cu 99 Cr 1 -4 wt.% SiC and Cu 94 Cr 6 -4 wt.% SiC (average particle size ∼30 nm). The 50 h ball-milled samples were uniaxially pressed, and then pellets were sintered at 800 deg. C, 900 deg. C and 1000 deg. C for a constant soaking period of 30 min by microwave sintering technique. Microstructural characterization was carried out by X-ray diffraction (XRD), scanning electron microscopy (SEM) and atomic force microscopy (AFM). Sintered compacts resulted a highly densified compacts (∼95% relative density) while retaining ultra-fine grains (100-200 nm) in the matrix. The mechanical properties, namely, hardness and wear resistance, and electrical conductivity of the sintered specimens were also evaluated. The best combination of mechanical properties (e.g. hardness ∼2.4 GPa) and electrical conductivity (60.3% of IACS) were obtained for Cu 94 Cr 6 -4 wt.% SiC sintered at 900 deg. C. This is possibly due to presence of ultra-fine grains in the bulk samples, good densification and proper bonding between particles. The results were analyzed in the light of interactions of microwaves between metallic matrix and microwave susceptive SiC particulates.

Elastocaloric effect in CuAlZn and CuAlMn shape memory alloys under compression

OpenAIRE

Qian, Suxin; Geng, Yunlong; Wang, Yi; Pillsbury, Thomas E.; Hada, Yoshiharu; Yamaguchi, Yuki; Fujimoto, Kenjiro; Hwang, Yunho; Radermacher, Reinhard; Cui, Jun; Yuki, Yoji; Toyotake, Koutaro; Takeuchi, Ichiro

2016-01-01

This paper reports the elastocaloric effect of two Cu-based shape memory alloys: Cu68Al16Zn16 (CuAlZn) and Cu73Al15Mn12 (CuAlMn), under compression at ambient temperature. The compression tests were conducted at two different rates to approach isothermal and adiabatic conditions. Upon unloading at a strain rate of 0.1 s−1 (adiabatic condition) from 4% strain, the highest adiabatic temperature changes (ΔTad) of 4.0 K for CuAlZn and 3.9 K for CuAlMn were obtained. The maximum stress and hystere...

Diffusivities and atomic mobilities in Cu-rich fcc Al-Cu-Mn alloys

Energy Technology Data Exchange (ETDEWEB)

Yin, Ming; Du, Yong; Cui, Senlin; Xu, Honghui; Liu, Shuhong [Central South Univ., Changsha (China). State Key Laboratory of Powder Metallurgy; Zhang, Lijun [Bochum Univ. (DE). Interdisciplinary Centre for Advanced Materials Simulation (ICAMS)

2012-07-15

Via solid-solid diffusion couples, electron probe microanalysis and the Whittle and Green method, interdiffusivities in fcc Al-Cu-Mn alloys at 1 123 K were measured. The reliability of the obtained diffusivities is validated by comparing the computed diffusivities with literature data plus constraints among the diffusivities. Through assessments of experimentally determined diffusion coefficients by means of a diffusion-controlled transformations simulation package, the atomic mobilities of Al, Cu, and Mn in fcc Al-Cu-Mn alloys are obtained. Comprehensive comparisons between the model-predicted and the experimental data indicate that the presently obtained atomic mobilities can reproduce most of the diffusivities, concentration profiles, and diffusion paths reasonably. (orig.)

Novel CuCr_2O_4 embedded CuO nanocomposites for efficient photodegradation of organic dyes

International Nuclear Information System (INIS)

Mageshwari, K.; Sathyamoorthy, R.; Lee, Jeong Yong; Park, Jinsub

2015-01-01

Graphical abstract: - Highlights: • Novel CuO–CuCr_2O_4 nanocomposites synthesized by reflux condensation method. • Methyl orange and methylene blue dye degradation studied under UV light irradiation. • Nanocomposites characterized by XRD, FESEM, TEM, EDX, UV–vis DRS and PL. • CuCr_2O_4 loading effectively enhanced the catalytic activity of CuO. - Abstract: Novel photocatalyst based on CuO–CuCr_2O_4 nanocomposites was synthesized for different Cr"3"+ concentration by reflux condensation method, and their photocatalytic activity was evaluated by monitoring the photodegradation of methyl orange (MO) and methylene blue dyes (MB) under UV light irradiation. Phase evolution by X-ray diffraction showed monoclinic CuO and tetragonal CuCr_2O_4 as the components of the prepared nanocomposites. Morphological analysis by scanning electron microscope and transmission electron microscope revealed that the incorporation of Cr"3"+ in CuO lattice alters the morphology of CuO from microsphere to cluster shape. Photoluminescence spectra of CuO–CuCr_2O_4 nanocomposites exhibited reduced PL emissions compared to pure CuO, indicating the low recombination rate of photogenerated electrons and holes. As expected, the CuCr_2O_4 loaded CuO showed enhanced photocatalytic activity for MO and MB dyes, and the kinetic studies suggest that the degradation follows pseudo-first-order kinetics. The enhanced photocatalytic activity of CuO–CuCr_2O_4 nanocomposites can be attributed to the presence of CuCr_2O_4 as an electron acceptor, which improves the effective charge separation in CuO.

Deuterium transport in Cu, CuCrZr, and Cu/Be

Science.gov (United States)

Anderl, R. A.; Hankins, M. R.; Longhurst, G. R.; Pawelko, R. J.

This paper presents the results of deuterium implantation/permeation experiments and TMAP4 simulations for a CuCrZr alloy, for OFHC-Cu and for a Cu/Be bi-layered structure at temperatures from 700 to 800 K. Experiments used a mass-analyzed, 3-keV D 3+ ion beam with particle flux densities of 5 × 10 19 to 7 × 10 19 D/m 2 s. Effective diffusivities and surface molecular recombination coefficients were derived giving Arrhenius pre-exponentials and activation energies for each material: CuCrZr alloy, (2.0 × 10 -2 m 2/s, 1.2 eV) for diffusivity and (2.9 × x10 -14 m 4/s, 1.92 eV) for surface molecular recombination coefficients; OFHC Cu, (2.1 × 10 -6 m 2/s, 0.52 eV) for diffusivity and (9.1 × 10 -18 m 4/s, 0.99 eV) for surface molecular recombination coefficients. TMAP4 simulation of permeation data measured for a Cu/Be bi-layer sample was achieved using a four-layer structure (Cu/BeO interface/Be/BeO back surface) and recommended values for diffusivity and solubility in Be, BeO and Cu.

Effects of processing parameters on Be/CuCrZr joining

International Nuclear Information System (INIS)

Park, Jeong-Yong; Lee, Jung-Suk; Choi, Byung-Kwon; Park, Sang-Yun; Hong, Bong Guen; Jeong, Yong Hwan; Jung, Ki-Jung

2007-01-01

A joining of Be/CuCrZr has been considered as the key technology for the fabrication of the ITER first wall. Among the joining methods, Hot isostatic pressing (HIP), which is one of the diffusion bonding methods, is the most feasible method to join the Be and CuCrZr alloy. In the HIP joining of Be and CuCrZr, the interlayer was used to prevent the formation of brittle intermetallic compounds in the interface. Therefore, it is crucial to select a suitable interlayer for a joining of Be and CuCrZr. On the other hand, the diffusion between Be and CuCrZr would be enhanced with an increase of the HIP joining temperature, thereby increasing the joint strength. However, the HIP joining temperature is limited by the mechanical properties of CuCrZr. During the fabrication process of the ITER first wall, CuCrZr is subjected to several thermal cycles including a solution annealing, a cooling and an aging. The HIP joining of Be and CuCrZr corresponds to the aging of CuCrZr. The HIP joining at a higher temperature would cause a degradation of the mechanical properties of CuCrZr by an overaging effect although it is preferable for an improvement of the joint strength. In this study, the effect of the cooling rate on the mechanical properties of aged CuCrZr was investigated to find the maximum HIP temperature without a degradation of the mechanical properties of CuCrZr

Crystal structure, Raman scattering and magnetic properties of CuCr2-xZrxSe4 and CuCr2-xSnxSe4 selenospinels

Science.gov (United States)

Pinto, C.; Galdámez, A.; Barahona, P.; Moris, S.; Peña, O.

2018-06-01

Selenospinels, CuCr2-xMxSe4 (M = Zr and Sn), were synthesized via conventional solid-state reactions. The crystal structure of CuCr1.5Sn0.5Se4, CuCr1.7Sn0.3Se4, CuCr1.5Zr0.5Se4, and CuCr1.8Zr0.2Se4 were determined using single-crystal X-ray diffraction. All the phases crystallized in a cubic spinel-type structure. The chemical compositions of the single-crystals were examined using energy-dispersive X-ray analysis (EDS). Powder X-ray diffraction patterns of CuCr1.3Sn0.7Se4 and CuCr1.7Sn0.3Se4 were consistent with phases belonging to the Fd 3 bar m Space group. An analysis of the vibrational properties on the single-crystals was performed using Raman scattering measurements. The magnetic properties showed a spin glass behavior with increasing Sn content and ferromagnetic order for CuCr1.7Sn0.3Se4.

Comparison of the Isothermal Oxidation Behavior of As-Cast Cu-17%Cr and Cu-17%Cr-5%Al. Part 1; Oxidation Kinetics

Science.gov (United States)

Raj. Sai V.

2008-01-01

The isothermal oxidation kinetics of as-cast Cu-17%Cr and Cu-17%Cr-5%Al in air were studied between 773 and 1173 K under atmospheric pressure. These observations reveal that Cu- 17%Cr-5%Al oxidizes at significantly slower rates than Cu-17%Cr. The rate constants for the alloys were determined from generalized analyses of the data without an a priori assumption of the nature of the oxidation kinetics. Detailed analyses of the isothermal thermogravimetric weight change data revealed that Cu-17%Cr exhibited parabolic oxidation kinetics with an activation energy of 165.9 9.5 kJ mol-1. In contrast, the oxidation kinetics for the Cu-17%Cr- 5%Al alloy exhibited a parabolic oxidation kinetics during the initial stages followed by a quartic relationship in the later stages of oxidation. Alternatively, the oxidation behavior of Cu-17%CR- 5%Al could be better represented by a logarithmic relationship. The parabolic rate constants and activation energy data for the two alloys are compared with literature data to gain insights on the nature of the oxidation mechanisms dominant in these alloys.

Synthesis, spectroscopic studies and antimicrobial activity of chelates 2-(acetyloxy)-benzoic acid with transition metals (CR+3, MN+2, NI+2 AND CU+2)

International Nuclear Information System (INIS)

Khan, B.; Mateen, B.; Ahmed, F.; Ahmed, F.

2007-01-01

2-(acetyloxy)-Benzoic acid chelates with Cr+3, Mn+2, Ni+2 and Cu+2 were synthesized and characterized by the melting point, solubility, Fourier Transform Infrared (FT-IR) Spectroscopy, Atomic Absorption Spectroscopy (AAS), X-Ray Diffraction (XRD) method and evaluated by antimicrobial activity. The functional group present in the chelates was determined by Fourier Transform Infrared Spectroscopy, by X-Ray Diffraction analysis crystal data of chelates, their inter-atomic and inter-planer spacing was also determined. The amount of metal in the chelates was estimated by Atomic Absorption Spectroscopy and their Antimicrobial Activity was studied against Pseudomonas aeruginosa, Escherisha coli and Staphylococcus aureus. (author)

The Paramagnetism of Small Amounts of Mn Dissolved in Cu-Al and Cu-Ge Alloys

Energy Technology Data Exchange (ETDEWEB)

Myers, H P; Westin, R

1963-06-15

Previous measurements of the valency of Mn in Cu-Zn alloys have been confirmed by measurements with the isoelectronic Cu-Al and Cu-Ge alloys as matrices for Mn. The valency, having the value i in pure copper, decreases slightly with increasing electron to atom ratio attaining the values 0. 9 and 0. 8 at the limiting composition in the Al and Ge alloys respectively. The apparent size of Mn in these alloys is discussed.

The Paramagnetism of Small Amounts of Mn Dissolved in Cu-Al and Cu-Ge Alloys

International Nuclear Information System (INIS)

Myers, H.P.; Westin, R.

1963-06-01

Previous measurements of the valency of Mn in Cu-Zn alloys have been confirmed by measurements with the isoelectronic Cu-Al and Cu-Ge alloys as matrices for Mn. The valency, having the value i in pure copper, decreases slightly with increasing electron to atom ratio attaining the values 0. 9 and 0. 8 at the limiting composition in the Al and Ge alloys respectively. The apparent size of Mn in these alloys is discussed

Structure of as cast L12 compounds in Al3Zr-base alloys containing Cu and Mn

International Nuclear Information System (INIS)

Virk, I.S.; Varin, R.A.

1991-01-01

It was first shown that the low symmetry, tetragonal DO 23 crystal structure of Al 3 Zr intermetallic can be changed to the related cubic L1 2 crystal structure by alloying with Ni (Al 5 NiZr 2 ) and Cu(Al 5 CuZr 2 ). It has been reported that previous work has successfully modified Al 3 Zr with Fe, Cu, Cr and Ni obtaining nearly single phase materials with L1 2 structure. However, they only studied the microstructure and mechanical properties of Fe - modified intermetallic (Al-6at% Fe-25at% Zr). The purpose of the paper is to describe and interpret experimental observations on the microstructure of Al 5 CuZr 2 and Al 66 Mn 9 Zr 25 (at.%) modifications of base Al 3 Zr intermetallic. The one modified with Mn has not been reported in literature although its Al 3 Ti - base counterpart has recently been successfully produced (3, 4)

Associations between standardized school performance tests and mixtures of Pb, Zn, Cd, Ni, Mn, Cu, Cr, Co, and V in community soils of New Orleans

International Nuclear Information System (INIS)

Zahran, Sammy; Mielke, Howard W.; Weiler, Stephan; Hempel, Lynn; Berry, Kenneth J.; Gonzales, Christopher R.

2012-01-01

In New Orleans a strong inverse association was previously identified between community soil lead and 4th grade school performance. This study extends the association to zinc, cadmium, nickel, manganese, copper, chromium, cobalt, and vanadium in community soil and their comparative effects on 4th grade school performance. Adjusting for poverty, food security, racial composition, and teacher-student ratios, regression results show that soil metals variously reduce and compress student scores. Soil metals account for 22%–24% while food insecurity accounts for 29%–37% of variation in school performance. The impact on grade point averages were Ni > Co > Mn > Cu ∼Cr ∼ Cd > Zn > Pb, but metals are mixtures in soils. The quantities of soil metal mixtures vary widely across the city with the largest totals in the inner city and smallest totals in the outer city. School grade point averages are lowest where the soil metal mixtures and food insecurity are highest. - Highlights: ► Mixtures of metals vary; largest totals in the inner city and lowest in the outer city. ► An inverse association between soil Pb and 4th grade school performance is known. ► Assuming the same exposure pathway, multiple metals are compared to performance. ► Soil metals account for 22%–24% of variation in school test performance. ► Soil metal plus food insecurity accounts for 54% of explained variance. - Controlling for potential confounding variables, the accumulation of metals (Pb, Zn, Cd, Ni, Mn, Cu, Cr, and Co) in neighborhood soils is significantly negatively associated with 4th grade school performance on standardized tests in New Orleans.

Hidden transition in multiferroic and magnetodielectric CuCrO2 evidenced by ac-susceptibility

Science.gov (United States)

Shukla, Kaushak K.; Pal, Arkadeb; Singh, Abhishek; Singh, Rahul; Saha, J.; Sinha, A. K.; Ghosh, A. K.; Patnaik, S.; Awasthi, A. M.; Chatterjee, Sandip

2017-04-01

Ferroelectric polarization, magnetic-field dependence of the dielectric constant and ac and dc magnetizations of frustrated CuCrO2 have been measured. A new spin freezing transition below 32 K is observed which is thermally driven. The nature of the spin freezing is to be a single-ion process. Dilution by the replacements of Cr ions by magnetic Mn ions showed suppression of the spin freezing transition suggesting it to be fundamentally a single-ion freezing process. The observed freezing, which is seemingly associated to geometrical spin frustration, represents a novel form of magnetic glassy behavior.

THE EFFECT OF RARE EARTH ELEMENTS ON Cr PRECIPITATIONS IN A Cu-0.8WT%Cr ALLOY

Directory of Open Access Journals (Sweden)

Gewang Shuai

2011-05-01

Full Text Available The microstructural evolution of Cu-based alloys during aging was studied using a quantitative metallographic method. Samples were cut from ingots of Cu-0.8wt%Cr and Cu-0.8wt%Cr-RE alloys. These were solution treated at 1000 ºC for 1.5h and subsequently quenched in water, then separately aged at 480 ºC for different durations. The microstructures were observed by optical microscope, and the characteristic geometric parameters of precipitated Cr phase, including volume fraction VV, face density NA, mean diameter and roundness, were measured. These data provided more details about the process of aging. The results showed that precipitation of Cr phase occurred in the form of particles during aging. Rare earth elements promoted the precipitation of Cr phase and dispersed Cr particles. The phenomenon of overaging came earlier in Cu-Cr-RE than in Cu-Cr. In the present work, the optimal aging time at 480 ºC was 2 hrs for the Cu-0.8wt%Cr-RE alloy and 3 hours for the Cu-0.8wt%Cr alloy.

Study of phase transformations in Fe-Mn-Cr Alloys

International Nuclear Information System (INIS)

Schule, W.; Panzarasa, A.; Lang, E.

1988-01-01

Nickel free alloys for fusion reactor applications are examined. Phase changes in fifteen, mainly austenitic iron-manganese-chromium-alloys of different compositions were investigated in the temperature range between -196 0 C and 1000 0 C after different thermo-mechanical treatments. A range of different physical measuring techniques was employed to investigate the structural changes occurring during heating and cooling and after cold-work: electrical resistivity techniques, differential thermal analysis, magnetic response, Vickers hardness and XRD measurement. The phase boundary between the α Fe-phase and the γ-phase of the iron manganese alloy is approximately maintained if chromium is added to the two component materials. Consequently all the alloy materials for contents of manganese smaller than about 30% Mn are not stable below 500 0 C. This concerns also the AMCR alloys. However the α Fe-phase is not formed during slow cooling from 1000 0 C to ambient temperature and is only obtained if nucleation sites are provided and after very long anneals. A cubic α Mn-type-phase is found for alloys with 18% Cr and 15% Mn, with 13% Cr and 25% Mn, with 10% Cr and 30% Mn, and with 10% Cr and 40% Mn. For these reasons the γ-phase field of the iron-chromium-manganese alloys is very small below 600 0 C and much narrower than reported in the literature. 95 figs. 22 refs

HIGH TEMPERATURE TENSILE PROPERTIES OF NEW FE-CR-MN DEVELOPED STEEL

OpenAIRE

M. Mahmoudiniya; Sh. Kheirandish; M. Asadi Asadabad

2017-01-01

Nowadays, Ni-free austenitic stainless steels are being developed rapidly and high price of nickel is one of the most important motivations for this development. At present research a new FeCrMn steel was designed and produced based on Fe-Cr-Mn-C system. Comparative studies on microstructure and high temperature mechanical properties of  new steel and AISI 316 steel were done. The results showed that new FeCrMn developed steel has single austenite phase microstructure, and its tensile st...

On the phase evolution of AlCoCrCuFeMnSix high entropy alloys prepared by mechanical alloying and arc melting route

Science.gov (United States)

Kumar, Anil; Chopkar, Manoj

2018-05-01

Effect of Si addition on phase formation of AlCoCrCuFeMnSix (x=0, 0.3, 0.6 and 0.9) high entropy alloy have been investigated in this work. The alloys are prepared by mechanical alloying and vacuum arc melting technique. The X-ray diffraction results reveals the formation of mixture of face centered and body centered cubic solid solution phases in milled powders. The addition of Si favours body centered cubic structure formation during milling process. Whereas, after melting the milled powders, body centered phases formed during milling is partial transformed into sigma phases. XRD results were also correlated with the SEM elemental mapping of as casted samples. Addition of Si favours σ phase formation in the as cast samples.

Oriented Mn-doped CuO nanowire arrays

International Nuclear Information System (INIS)

Han, Dongqiang; Wu, Zhaofeng; Wang, Zhihe; Yang, Shaoguang

2016-01-01

Using anodic aluminum oxide membranes as the nanoreactors and controller, oriented nanowire arrays of the diluted magnetic semiconductor Mn-doped CuO have been successfully fabricated using Mn(NO_3)_2 · 4H_2O and Cu(NO_3)_2 · 3H_2O as the starting materials. X-ray diffraction measurements showed that the as-prepared oriented nanowire arrays are of high purity. Scanning electron microscope and transmission electron microscope studies showed the nanowires are oriented, continuous and uniform with a diameter and length of about 170 nm and several tens of micrometers, respectively, and thus of a high aspect ratio. Low-temperature magnetic measurements showed the ferromagnetic property of the oriented Mn-doped CuO nanowire arrays with the critical temperature at around 80 K, which will endow them with great potential applications in spintronics in the future. (paper)

Electronic, magnetic, elastic and thermodynamic properties of Cu{sub 2}MnGa

Energy Technology Data Exchange (ETDEWEB)

Ghosh, Sukriti [Department of Physics, Government Kamla Raja Girls Autonomous Post Graduate College, Gwalior 474001, Madhya Pradesh (India); Condensed Matter Theory Group, School of Studies in Physics, Jiwaji University, Gwalior 474 011, Madhya Pradesh (India); Gupta, Dinesh C., E-mail: sosfizix@gmail.com [Condensed Matter Theory Group, School of Studies in Physics, Jiwaji University, Gwalior 474 011, Madhya Pradesh (India)

2016-08-01

The full-potential linearized augmented plane wave method in the stable Fm-3m phase has been implemented to investigate the structural, elastic, magnetic and electronic properties of Cu{sub 2}MnGa. The optimized equilibrium lattice parameter in stable phase is found to be 5.9495 Å. By the spin resolved density of states calculations, we have shown that the exchange splitting due to Mn atom is the main reason of ferromagnetic behavior of Cu{sub 2}MnGa. The absence of energy gap in both the spin channels predicts that the material is metallic. The total and partial density of states, elastic constants, Shear, Bulk and Young’s moduli, Zener isotropy factor, Cauchy pressure, Pugh's ductility, Kleinman parameter and Poisson's ratio are reported for the first time for the alloy. Cauchy's pressure and Pugh's index of ductility label Cu{sub 2}MnGa as ductile. Cu{sub 2}MnGa is found to be ferromagnetic and anisotropic in nature. The quasi-harmonic approximations have been employed to study the pressure and temperature dependent thermodynamic properties of Cu{sub 2}MnGa. - Highlights: • It is the first attempt to predict a variety of crystal properties of Cu{sub 2}MnGa. • Cu{sub 2}MnGa shows magnetism and hence can prove to be important in modern technology. • Cu{sub 2}MnGa is ductile and hence can attract attention of scientists and technologists.

Magnetic excitations in CuMn spin-glass alloys

International Nuclear Information System (INIS)

Tsunoda, Y.; Kunitomi, N.; Cable, J.W.

1985-01-01

Recent neutron scattering measurements have helped to clarify two important features of CuMn spin glasses. Murani and co-workers have studied the dynamical behavior of spin-glass systems and have observed characteristic ferromagnetic spin correlations with a broad distribution of relaxation times and a dynamical freezing process. By means of the polarization analysis technique, Cable and co-workers have observed the coexistence of two types of magnetic short-range order (MSRO): one is a modulated-spin structure, and the other is a ferromagnetic cluster associated with the atomic short-range order (ASRO). These ordered regions produce diffraction maxima which are found at the (1 1/2 +/- delta 0) and the (1 1/2 0) reciprocal lattice points, respectively. Both of these observations seem to be essential for understanding the CuMn spin-glass system. However, the physical relationship of these properties is not yet understood. The authors have studied the inelastic scattering of neutrons around the magnetic diffuse peak positions of a Cu/sub 78.7/Mn/sub 21.3/ single crystal. The spin-glass freezing temperature of a CuMn alloy with this Mn concentration is estimated to be T/sub f/ approx. 90 K. Most of the data were taken by scanning along the [0 1 0] direction from the (1 0 0) to the (1 1 0) reciprocal lattice points

The effect of magnetic ordering on the giant magnetoresistance of Cr-Fe-V and Cr-Fe-Mn

International Nuclear Information System (INIS)

Somsen, Ch.; Acet, M.; Nepecks, G.; Wassermann, E.F.

2000-01-01

Cr-rich Cr 1-x Fe x alloys with compositions in the vicinity of mixed ferromagnetic and antiferromagnetic exchange (x=0.18) exhibit giant magnetoresistance. In order to understand the influence of the antiferromagnetism of Cr on the giant magnetoresistance one can manipulate the antiferromagnetic exchange either by adding vanadium, which destroys the antiferromagnetism of Cr, or by adding manganese, which enhances it. Cr-Fe-V and Cr-Fe-Mn alloys also have Curie temperatures that lie between low temperatures and room temperature in the concentration region where giant magnetoresistance is observed. Therefore, they are also used as samples to study the magnetoresistance as a function of the strength of FM exchange. We discuss these points in the light of temperature and concentration-dependent magnetoresistance experiments on Cr 0.99-x Fe x V 0.01 , Cr 0.96-x Fe x V 0.04 , Cr 0.90-x Fe x Mn 0.10 and Cr 0.55 Fe x Mn 0.45-x alloys. Results indicate that the most favorable condition for a large magnetoresistance in these alloys occurs at temperatures near the Curie temperature

Microstructure and mechanical performance of depositing CuSi3 Cu alloy onto 30CrMnSi steel plate by the novel consumable and non-consumable electrodes indirect arc welding

International Nuclear Information System (INIS)

Wang, Jun; Cao, Jian; Feng, Jicai

2010-01-01

A novel consumable and non-consumable electrodes indirect arc welding (CNC-IAW) with low heat input was successfully applied in depositing CuSi 3 Cu alloy onto 30CrMnSi steel plate. The indirect arc was generated between the consumable and non-consumable welding torch. The microstructure of the deposited weld was analyzed by means of scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and optical microscopy (OM). The results showed that the dilution ratio of the bead-on-plate weld was controlled no higher than 5% and the deleterious iron picking up was effectively restrained. The deposited metal mainly consisted of ε-Cu solid solution and a small amount of Fe 2 Si phase. In the interfacial zone between the deposited metal and base metal, the thickness of the zone changed from thick to thin and the microstructure changed from complex to simple from the middle to both sides. In the middle of the interfacial zone, the microstructure presented three sub-layers consisting of Fe 3 Si (L)/Fe 3 Si (S) + ε-Cu/α-Fe. In the both sides of the interfacial zone, the microstructure presented single α-Fe layer. The formation mechanism of the interfacial zone could be successfully explained by the formation of the Fe liquid-solid phase zone adjacent to the Fe base metal and the interfusion between Fe and Si. The average compressive shear strength reached 321 MPa and its fracture morphology mainly belonged to ductile fracture.

Aging properties studies in a Cu-Ag-Cr Alloy

International Nuclear Information System (INIS)

Jia, S.G.; Zheng, M.S.; Liu, P.; Ren, F.Z.; Tian, B.H.; Zhou, G.S.; Lou, H.F.

2006-01-01

A Cu-Ag-Cr alloy was produced by means of vacuum induction melting. The effects of aging processes on microhardness and conductivity of Cu-Ag-Cr alloy were studied. The microstructure of the alloy was examined using transmission electron microscope (TEM). Aging at 450 deg. C for 4 h, the alloy has an excellent combination of microhardness and conductivity, the microhardness and conductivity reach 132 HV and 80% IACS, respectively. The precipitates responsible for the age-hardening effect are fcc Cr. The fine and dispersed precipitates are fully coherent with the Cu matrix and make the Cu-Ag-Cr alloy possesses higher hardness and conductivity

Preparation and magnetic properties of multiferroic CuMnO2 nanoparticles.

Science.gov (United States)

Kurokawa, Akinobu; Yanoh, Tkuya; Yano, Shinya; Ichiyanagi, Yuko

2014-03-01

CuMnO2 nanoparticles with diameters of 64 nm were synthesized by a novel wet chemical method. An optimized two-step annealing method was developed through the analysis of thermogravimetric differential thermal analysis (TG-DTA) measurements in order to obtain single-phase CuMnO2. A sharp exothermic peak was observed in the DTA curve at approximately 500 K where structural changes of the copper oxides and manganese oxides in the precursor are expected to occur. It is believed that Cu+ ions were oxidized to Cu2+ ions and that Mn2+ ions were oxidized to Mn3+ ions in the Cu-Mn-O system. Deoxidization reactions were also found at approximately 1200 K. The optimized annealing temperature for the first step was determined to be 623 K in air. The optimized annealing temperature for the second step was 1173 K in an Ar atmosphere. Magnetization measurements suggested an antiferromagnetic spin ordering at approximately 50 K. It was expected that Mn3+ spin interactions induced magnetic phase transition affected by definite temperature.

Ultrathin Cr added Ru film as a seedless Cu diffusion barrier for advanced Cu interconnects

Science.gov (United States)

Hsu, Kuo-Chung; Perng, Dung-Ching; Yeh, Jia-Bin; Wang, Yi-Chun

2012-07-01

A 5 nm thick Cr added Ru film has been extensively investigated as a seedless Cu diffusion barrier. High-resolution transmission electron microscopy micrograph, X-ray diffraction (XRD) pattern and Fourier transform-electron diffraction pattern reveal that a Cr contained Ru (RuCr) film has a glassy microstructure and is an amorphous-like film. XRD patterns and sheet resistance data show that the RuCr film is stable up to 650 °C, which is approximately a 200 °C improvement in thermal stability as compared to that of the pure Ru film. X-ray photoelectron spectroscopy depth profiles show that the RuCr film can successfully block Cu diffusion, even after a 30-min 650 °C annealing. The leakage current of the Cu/5 nm RuCr/porous SiOCH/Si stacked structure is about two orders of magnitude lower than that of a pristine Ru sample for electric field below 1 MV/cm. The RuCr film can be a promising Cu diffusion barrier for advanced Cu metallization.

Comparison of the Isothermal Oxidation Behavior of As-Cast Cu-17 Percent Cr and Cu-17 Percent Cr-5 Percent Al. Part 1; Oxidation Kinetics

Science.gov (United States)

Raj, S. V.

2008-01-01

The isothermal oxidation kinetics of as-cast Cu-17%Cr and Cu-17%Cr-5%Al in air were studied between 773 and 1173 K under atmospheric pressure. These observations reveal that Cu-17%Cr-5%Al oxidizes at significantly slower rates than Cu-17%Cr. The rate constants for the alloys were determined from generalized analyses of the data without an a priori assumption of the nature of the oxidation kinetics. Detailed analyses of the isothermal thermogravimetric weight change data revealed that Cu-17%Cr exhibited parabolic oxidation kinetics with an activation energy of 165.9+/-9.5 kJ/mol. In contrast, the oxidation kinetics for the Cu-17%Cr-5%Al alloy exhibited a parabolic oxidation kinetics during the initial stages followed by a quartic relationship in the later stages of oxidation. Alternatively, the oxidation behavior of Cu-17%CR-5%Al could be better represented by a logarithmic relationship. The parabolic rate constants and activation energy data for the two alloys are compared with literature data to gain insights on the nature of the oxidation mechanisms dominant in these alloys.

R&D of CuCrZr tubes for W/Cu monoblock components

Energy Technology Data Exchange (ETDEWEB)

Zhao, Sixiang, E-mail: sxzhao@impcas.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences (ASIPP), P.O. Box 1126, Hefei 230031 (China); Ma, Linsheng [State Nuclear Bao Ti Zirconium Industry Company, 206 Hi-Tech Avenue, Baoji 721013 (China); Peng, Lingjian [Advanced Technology & Materials Co., Ltd. - AT& M, Beijing 100081 (China); Gao, Bo [State Nuclear Bao Ti Zirconium Industry Company, 206 Hi-Tech Avenue, Baoji 721013 (China); Li, Chun [Laboratory of Advanced materials, School of Materials Science & Engineering, Tsinghua University, Beijing 100084 (China); Li, Qiang; Wang, Wanjing; Wei, Ran; Xu, Yuping [Institute of Plasma Physics, Chinese Academy of Sciences (ASIPP), P.O. Box 1126, Hefei 230031 (China); Pan, Ningjie; Qin, Sigui; Shi, Yingli; Liu, Guohui; Wang, Tiejun [Advanced Technology & Materials Co., Ltd. - AT& M, Beijing 100081 (China); Luo, Guang-Nan, E-mail: gnluo@ipp.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences (ASIPP), P.O. Box 1126, Hefei 230031 (China); Hefei Center for Physical Science and Technology, Hefei 230031 (China); Hefei Science Center of CAS, Hefei 230031 (China)

2016-11-15

Highlights: • CuCrZr tubes with excellent HIP performance and good resistance to grain growth have been developed. • A circumferential ductility testing manner for small-diameter tubes has been utilized in this study. • The evolution of microstructures has been revealed throughout the new tube forming processes. - Abstract: In order to avoid the occurrence of two types of longitudinal defects (strain localization and folding flaws), which were observed in the CuCrZr tubes of EAST W/Cu upper divertor components, in the future manufacturing of monoblock components using hot isostatic pressing (HIP), a new CuCrZr tube forming protocol is proposed. The evolution of Cu grains and Cr-rich particles is monitored by scanning electron microscopy throughout the new tube forming processes. The final microstructures of the newly developed tubes are totally different from those of the EAST project previously chosen tubes and the elongation of Cr-rich precipitates has been substantially suppressed by using the new tube forming protocol. The newly developed tubes show better HIP performance than the EAST previously chosen ones. Since circumferential mechanical properties, especially ductility, are of great importance, a circumferential ductility testing manner for small-diameter tubes, which might be a supplement to longitudinal tensile testing, has been utilized and the preliminary testing results are given. The recrystallization behavior of the newly developed tubes is also investigated.

Effect of Ce addition on microstructure of Al20Cu2Mn3 twin phase in an Al–Cu–Mn casting alloy

International Nuclear Information System (INIS)

Chen Zhongwei; Chen Pei; Li Shishun

2012-01-01

Highlights: ► Rare earth element Ce can retard the formation of the Al 20 Cu 2 Mn 3 twin phase in an Al–Cu–Mn casting alloy. ► Patterns of the particles of the Al 20 Cu 2 Mn 3 phase in Al–Cu–Mn free Ce alloy are more diverse. ► The symmetry of neighboring components of twins is characterized by glide reflection and reflection. ► The twins of Al 20 Cu 2 Mn 3 phase can enhance the mechanical properties of the Al–Cu–Mn casting alloys. - Abstract: Effects of Ce addition on microstructure of Al 20 Cu 2 Mn 3 twin phase and mechanical properties of an Al–Cu–Mn casting alloy were investigated by transmission electron microscopy, selected area electron diffraction, high resolution transmission electron microscopy and tensile test. The results show that rare earth element Ce can retard the formation of the Al 20 Cu 2 Mn 3 phase in the Al–Cu–Mn alloy. Compared with the Ce containing alloy, patterns of particles of the Al 20 Cu 2 Mn 3 phase in the Al–Cu–Mn free Ce alloy are more diverse. The symmetry of neighboring components of twins is characterized by glide reflection and reflection. In addition, twins of the Al 20 Cu 2 Mn 3 phase can enhance the mechanical properties of the Al–Cu–Mn alloy.

Effect of adding Cr on magnetic properties and metallic behavior in MnTe film

International Nuclear Information System (INIS)

Wang, Z.H.; Geng, D.Y.; Gong, W.J.; Li, J.; Li, Y.B.; Zhang, Z.D.

2012-01-01

Mn 1−x Cr x Te films with x = 0, 0.02, and 0.05 was synthesized by pulsed laser deposition and crystallize in hexagonal NiAs-type structure. The spin glass behavior predicted before by Monte Carlo calculation is observed in the MnTe film. This behavior is destroyed by adding Cr in the MnTe film. The temperature dependence of magnetization shows a sharp rise at around 66 K, due to the magneto-elastic coupling. Metallic behavior is observed in the MnTe film in the temperature range 120–220 K, which is ascribed to the magnetic ordering. The metallic behavior disappears with adding Cr, because adding Cr ions destroys the magnetic ordering which is mediated by the sp–d exchange interaction between the Cr ions. - Highlights: ► Mn 1−x Cr x Te films with NiAs-type structure was prepared by pulsed laser deposition. ► The spin glass behavior was observed in MnTe film at low temperature. ► The spin glass behavior was destroyed by adding Cr. ► The temperature dependence of magnetization showed a sharp rise at around 66 K. ► Metallic behavior was observed in MnTe film, which disappeared by adding Cr.

The influence of cooling rate and Fe/Cr content on the evolution of Fe-rich compounds in a secondary Al-Si-Cu diecasting alloy

Science.gov (United States)

Fabrizi, A.; Timelli, G.

2016-03-01

This study investigates the morphological evolution of primary α-Al(Fe,Mn,Cr)Si phase in a secondary Al-Si-Cu alloy with respect to the initial Fe and Cr contents as well as to the cooling rate. The solidification experiments have been designed in order to cover a wide range of cooling rates, and the Fe and Cr contents have been varied over two levels. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring at different experimental conditions. The morphological evolution of the α-Fe phase has been also analysed by observing deep etched samples. By changing the cooling rate, α-Al15(Fe,Mn,Cr)3Si2 dodecahedron crystals, as well as Chinese- script, branched structures and dendrites form, while primary coarse β-Al5(Fe,Mn)Si needles appear in the alloy with the highest Fe content at low cooling rates.

Effect of MnCuFe{sub 2}O{sub 4} content on magnetic and dielectric properties of poly (O-Phenylenediamine)/MnCuFe{sub 2}O{sub 4} nanocomposites

Energy Technology Data Exchange (ETDEWEB)

Kannapiran, Nagarajan [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India); Muthusamy, Athianna, E-mail: muthusrkv@gmail.com [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India); Chitra, Palanisamy [PG and Research Department of Chemistry, Sri Ramakrishna Mission Vidyalaya College of Arts and Science, Coimbatore 641020, Tamil Nadu (India)

2016-03-01

Poly o-phenylenediamine (PoPD)/MnCuFe{sub 2}O{sub 4} nanocomposites with three different ratios of MnCuFe{sub 2}O{sub 4} (10%, 20%, 30% w/w) were synthesized by in-situ oxidative chemical polymerization method ammonium persulphate used as oxidant, while MnCuFe{sub 2}O{sub 4} nanoparticles was prepared by auto-combustion method. The structure, morphology and magnetic properties of synthesized PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites were characterized by FT-IR, UV–visible absorption spectra, X-ray diffraction (XRD), Scanning electron microscopy (SEM), Transmission electron microscopy (TEM), Thermogravimetric analysis (TGA) and Vibrating sample magnetometer (VSM). FTIR spectra and XRD were confirmed the formation of the PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites. The morphology of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites is visualized through SEM and TEM. The spherical morphology of the PoPD was confirmed using SEM analysis. Dielectric properties of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites at different temperatures have been performed in the frequency range of 50 Hz–5 MHz. The optical absorption experiments of PoPD/MnCuFe{sub 2}O{sub 4} nanocomposites reveal that the direct transition with an energy band gap is around 2 eV. - Highlights: • Green synthesis of PoPD (the polymerization carried out only in aqueous medium) by in-situ chemical polymerization method. • For the first time, PoPD incorporated with MnCuFe{sub 2}O{sub 4} with lesser particle size. • The auto combustion reaction, support to achieve less particle size. • Ferrite content affects the magnetic properties of the nanocomposites.

Free standing CuO-MnO2 nanocomposite for room temperature ammonia sensing

Science.gov (United States)

Bhuvaneshwari, S.; Papachan, Seethal; Gopalakrishnan, N.

2017-05-01

CuO nanostructures and CuO-MnO2 nanocomposite were successfully synthesized using hydrothermal method without any aid of growth controlling agents. The synthesized CuO nanostructures have monoclinic structure. The XRD pattern of CuO-MnO2 observed with mixed phases of monoclinic CuO and birnessite-type MnO2 which confirms the formation of nanocomposite. SEM images revealed the turmeric-like morphology for CuO and intercalated sheets with flowers on the surface for CuO-MnO2. The length and breadth of turmeric-like structure is about 642.2 nm and 141.8 nm, respectively. The band gap of 1.72 eV for CuO nanostructure and 1.9 eV for CuO-MnO2 nanocomposite were observed from the absorption spectra. The free standing devices of CuO-MnO2 showed nearly a 3 fold increase sensing response to ammonia at room temperature when compared to the constituent CuO. The composite sensor showed response time of 120 s and recovered within 600 s. This enhanced response can be asserted to the peculiar morphology of the composite that provides more adsorption site for gas diffusion to take place.

High temperature superconductivity in Zn and Mn substituted (Tl,Cr)Sr2CaCu2O7

International Nuclear Information System (INIS)

Lo, S.V.; Abd Shukor, R.

1999-01-01

Samples with nominal starting composition (TICr 0 .15)Sr 2 (Ca 1-x M x )Cu 2 O 7 (TI-1212) for x=0 - 0.7 with M= Zn and Mn have been prepared and investigated by powder X-ray diffraction (XRD) and electrical resistance measurements. All sample showed a mixed phase of 1212 and 1201. Dominant 1212-phase was observed for x=0.0-0.5 and x=0.0-0.4, for Zn and Mn series, respectively. The superconducting transition temperature was suppressed when Zn and Mn are substituted at the Ca site. For the Zn series the normal state behavior is metallic throughout the doping range. For the Mn series the normal state behavior is metallic for 0.1≤x≥0.3 and semiconducting like x>0.3. The suppression of T c and formation of the TI-1212 phase are discussed in terms of the ionic radius and valence state of the substituted elements. (author)

Study on the behavior of the heavy metals Cu, Cr, Ni, Zn, Fe, Mn and 137Cs in an estuarine ecosystem using Mytilus galloprovincialis as a bioindicator species: the case of Thermaikos gulf, Greece

International Nuclear Information System (INIS)

Catsiki, Vassiliki-Angelique; Florou, H.

2006-01-01

Mussels are worldwide recognized as pollution bioindicators and used in Mussel Watch programs, because they accumulate pollutants in their tissues at elevated levels in relation to pollutant biological availability in the marine environment. The present study deals with the use of Mytilus galloprovincialis as a local bioindicator of heavy metal and 137 Cs contamination in an estuarine ecosystem (Thermaikos gulf, Greece in Eastern Mediterranean). M. galloprovincialis samples were collected monthly from two aquaculture farms during the period April to October 2000. Analyses for the heavy metals Cu, Cr, Ni, Zn, Fe, Mn and 137 Cs showed that the concentrations measured were low and similar to those from other non-polluted Mediterranean areas. In terms of the two sampling stations, there were no statistically significant differences between them. On the contrary, the seasonal evolution of either heavy metals or 137 Cs levels presented high variation. The levels were found to increase during the cold period of the year, especially for Cu, Zn, Mn and Cr which are essential for life. Stable metals were positively inter-related and moreover, metals more involved in biochemical activities seem to present more correlations than others with less significant role in the metabolism of the organisms

Cu and Cu(Mn) films deposited layer-by-layer via surface-limited redox replacement and underpotential deposition

Energy Technology Data Exchange (ETDEWEB)

Fang, J.S., E-mail: jsfang@nfu.edu.tw [Department of Materials Science and Engineering, National Formosa University, Huwei 63201, Taiwan (China); Sun, S.L. [Department of Materials Science and Engineering, National Formosa University, Huwei 63201, Taiwan (China); Cheng, Y.L. [Department of Electrical Engineering, National Chi-Nan University, Nan-Tou 54561, Taiwan (China); Chen, G.S.; Chin, T.S. [Department of Materials Science and Engineering, Feng Chia University, Taichung 40724, Taiwan (China)

2016-02-28

Graphical abstract: - Abstract: The present paper reports Cu and Cu(Mn) films prepared layer-by-layer using an electrochemical atomic layer deposition (ECALD) method. The structure and properties of the films were investigated to elucidate their suitability as Cu interconnects for microelectronics. Previous studies have used primarily a vacuum-based atomic layer deposition to form a Cu metallized film. Herein, an entirely wet chemical process was used to fabricate a Cu film using the ECALD process by combining underpotential deposition (UPD) and surface-limited redox replacement (SLRR). The experimental results indicated that an inadequate UPD of Pb affected the subsequent SLRR of Cu and lead to the formation of PbSO{sub 4}. A mechanism is proposed to explain the results. Layer-by-layer deposition of Cu(Mn) films was successfully performed by alternating the deposition cycle-ratios of SLRR-Cu and UPD-Mn. The proposed self-limiting growth method offers a layer-by-layer wet chemistry-based deposition capability for fabricating Cu interconnects.

Promising Cu-Ni-Cr-Si alloy for first wall ITER applications

International Nuclear Information System (INIS)

Ivanov, A.; Abramov, V.; Rodin, M.

1996-01-01

Precipitation-hardened Cu-Ni-Cr-Si alloy, a promising material for ITER applications, is considered. Available commercial products, chemical composition, physical and mechanical properties are presented. Embrittlement of Cu-Ni-Cr-Si alloy at 250-300 C is observed. Mechanical properties of Cu-Ni-Cr-Si alloy neutron irradiated to a dose of ∝0.2 dpa at 293 C are investigated. Embrittlement of Cu-Ni-Cr-Si alloy can be avoided by annealing. (orig.)

Reduced-activation austenitic stainless steels: The Fe--Mn--Cr--C system

International Nuclear Information System (INIS)

Klueh, R.L.; Maziasz, P.J.

1988-01-01

Nickel-free manganese-stabilized steels are being developed for fusion-reactor applications. As the first part of this effort, the austenite-stable region in the Fe--Mn--Cr--C system was determined. Results indicated that the Schaeffler diagram developed for Fe--Ni--Cr--C alloys cannot be used to predict the constituents expected for high-manganese steels. This is true because manganese is not as strong an austenite stabilizer relative to δ-ferrite formation as predicted by the diagram, but it is a stronger austenite stabilizer relative to martensite than predicted. Therefore, the austenite-stable region for Ne--Mn--Cr--C alloys occurs at lower chromium and hugher combinations of manganese and carbon than predicted by the Schaeffler diagram. Development of a manganese-stabilized stainless steel should be possible in the composition range of 20 to 25% Mn, 10 to 15% Cr, and 0.01 to 0.25%C. Tensile behavior of an Fe--20%Mn--12%Cr--0.25%C alloy was determined. The strength and ductility of this possible base composition was comparable to type 316 stainless steel in both the solution-annealed and cold-worked condition

The 52Cr(p, γ)53Mn reaction

NARCIS (Netherlands)

Vuister, P.H.

The 52Cr(p, γ)53Mn reaction was investigated in the energy region Ep = 1.36–2.26 MeV. The resonance energies, the corresponding 53Mn excitation energies and the resonance strengths of 199 resonances, assigned to this reaction, are reported. The excitation energies and gamma-ray branchings of 13

An ab initio study on the structural, electronic and mechanical properties of quaternary full-Heusler alloys FeMnCrSn and FeMnCrSb

Science.gov (United States)

Erkişi, Aytaç

2018-06-01

The quaternary full Heusler alloys FeMnCrSn and FeMnCrSb, which have face-centred cubic (FCC) crystal structure and conform to ? space group with 216 space number, have been investigated using Generalised Gradient Approximation (GGA) in the Density Functional Theory (DFT) as implemented in VASP (Vienna Ab initio Simulation Package) software. These alloys are considered in ferromagnetic (FM) order. After the investigation of structural stability of these alloys, their mechanical and thermal properties and also electronic band structures have been examined. The calculated spin-polarised electronic band structures and total electronic density of states (DOS) within GGA approximation show that these alloys can exhibit both metallic and half-metallic characters in different structural phases. The calculated formation enthalpies and the plotted energy-volume graphs show that Type-III phase is most stable structural phase for these materials. Also, FeMnCrSb alloy in Type-I/Type-III phases and FeMnCrSn alloy in Type-III phase show half-metallic behaviour with integer total magnetic moments almost 2 and 1 μB per formula unit, respectively, since there are band gaps observed in spin-down states, whereas they have metallic behaviour in majority bands. Other structural phases of both systems are also metallic. Moreover, the calculated elastic constants and the estimated anisotropy shear factors indicate that these materials are stable mechanically in all of three phases except FeMnCrSn in Type-I phase that does not satisfy Born stability criteria in this phase and have high anisotropic behaviour.

Correlation between microstructure and electrical properties of Cu{sub 1.3}Mn{sub 1.7}O{sub 4}/La{sub 2}O{sub 3} composite-coated ferritic stainless steel interconnects

Energy Technology Data Exchange (ETDEWEB)

Hosseini, N., E-mail: nazaneen_hosseini@ma.iut.ac.ir [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Karimzadeh, F.; Abbasi, M.H. [Department of Materials Engineering, Isfahan University of Technology, Isfahan 84156-83111 (Iran, Islamic Republic of); Choi, G.M. [Fuel Cell Research Center and Department of Materials Science and Engineering, Pohang University of Science and Technology, Pohang 790-784 (Korea, Republic of)

2016-07-15

The goal of this study was to investigate the effect of screen-printed Cu{sub 1.3}Mn{sub 1.7}O{sub 4}/La{sub 2}O{sub 3} composite coating on chromia scale growth and electrical behavior of AISI430 stainless steel interconnects. The coated samples were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy equipped with energy dispersive spectroscopy (FESEM-EDS) and 4-probe area specific resistance (ASR) tests. The results showed that LaCrO{sub 3} conductive perovskite is formed due to the interdiffusion between Cr{sub 2}O{sub 3} and/or CrO{sub 3} and La{sub 2}O{sub 3}. The presence of LaCrO{sub 3} through the composite coating and Cr{sub 2}O{sub 3} sub-scale accompanied by the effective role of spinel phase, acted as a barrier to mitigate the sub-scale growth preventing chromium diffusion through the coating and the cathode. Besides, LaCrO{sub 3} particles within the sub-scale provided suitable conductive paths decreasing ASR from 19.3 mΩ cm{sup 2} for spinel coated sample to 15 mΩ cm{sup 2} for composite coated sample at the end of 500 h oxidation at 750° C. - Highlights: • Cu{sub 1.3}Mn{sub 1.7}O{sub 4}/La{sub 2}O{sub 3} coating was deposited on AISI 430 by screen-printing method. • LaCrO{sub 3} perovskite was formed due to the interdiffusion between Cr species and La{sub 2}O{sub 3}. • LaCrO{sub 3} particles within the chromia provided conductive paths causing ASR reduction. • The co-existence of LaCrO{sub 3} and Cu{sub 1.3}Mn{sub 1.7}O{sub 4} noticeably retarded the chromia growth.

The influence of cooling rate and Fe/Cr content on the evolution of Fe-rich compounds in a secondary Al-Si-Cu diecasting alloy

International Nuclear Information System (INIS)

Fabrizi, A; Timelli, G

2016-01-01

This study investigates the morphological evolution of primary α-Al(Fe,Mn,Cr)Si phase in a secondary Al-Si-Cu alloy with respect to the initial Fe and Cr contents as well as to the cooling rate. The solidification experiments have been designed in order to cover a wide range of cooling rates, and the Fe and Cr contents have been varied over two levels. Metallographic and image analysis techniques have been used to quantitatively examine the microstructural changes occurring at different experimental conditions. The morphological evolution of the α-Fe phase has been also analysed by observing deep etched samples. By changing the cooling rate, α-Al 15 (Fe,Mn,Cr) 3 Si 2 dodecahedron crystals, as well as Chinese- script, branched structures and dendrites form, while primary coarse β-Al 5 (Fe,Mn)Si needles appear in the alloy with the highest Fe content at low cooling rates. (paper)

Preparation-Properties Relation of Mn-Cu Hopcalite Catalyst

OpenAIRE

Ardita Mele; Ilo Mele; Altin Mele

2012-01-01

Problem statement: The Mn-Cu hopcalite catalyst was used for the conversion of CO to CO2 at low temperatures. It was the catalyst of choice in the gas masks for respiratory protection in mines, aircrafts, military, spatial laboratories. Approach: The efficiency of hopcalite catalyst depends on its surface parameters. Its surface characteristics can be influenced from the chosen way of the MnO2 and CuO precipitation and from the pressure of pelletizing. Results: The hopcalite samples has been ...

Ductile shape memory alloys of the Cu-Al-Mn system

International Nuclear Information System (INIS)

Kainuma, R.; Takahashi, S.; Ishida, K.

1995-01-01

Cu-Al-Mn shape memory alloys with enhanced ductility have been developed by decreasing the degree of order in the β parent phase. Cu-Al-Mn alloys with Al contents lower than 18% exhibit good ductility with elongations of about 15% and excellent cold-workability arising from a lower degree of order in the Heusler (L21) β 1 parent phase, without any loss in their shape memory behavior. In this paper the mechanical and shape memory characteristics, such as the cold-workability, the Ms temperatures, the shape memory effect and the pseudo-elasticity of such ductile Cu-Al-Mn alloys are presented. (orig.)

HIGH TEMPERATURE TENSILE PROPERTIES OF NEW FE-CR-MN DEVELOPED STEEL

Directory of Open Access Journals (Sweden)

M. Mahmoudiniya

2017-03-01

Full Text Available Nowadays, Ni-free austenitic stainless steels are being developed rapidly and high price of nickel is one of the most important motivations for this development. At present research a new FeCrMn steel was designed and produced based on Fe-Cr-Mn-C system. Comparative studies on microstructure and high temperature mechanical properties of  new steel and AISI 316 steel were done. The results showed that new FeCrMn developed steel has single austenite phase microstructure, and its tensile strength and toughness were higher than those of 316 steel at 25, 200,350 and 500°C. In contrast with 316 steel, the new FeCrMn steel did not show strain induced transformation and dynamic strain aging phenomena during tensile tests that represented higher austenite stability of new developed steel. Lower density and higher strength of the new steel caused higher specific strength in comparison with the 316 one that can be considered as an important advantage in structural applications but in less corrosive environment

Defect properties of CuCrO2: A density functional theory calculation

International Nuclear Information System (INIS)

Fang Zhi-Jie; Zhu Ji-Zhen; Zhou Jiang; Mo Man

2012-01-01

Using the first-principles methods, we study the formation energetics properties of intrinsic defects, and the charge doping properties of extrinsic defects in transparent conducting oxides CuCrO 2 . Intrinsic defects, some typical acceptor-type, and donor-type extrinsic defects in their relevant charge state are considered. By systematically calculating the formation energies and transition energy, the results of calculation show that, V Cu , O i , and O Cu are the relevant intrinsic defects in CuCrO 2 ; among these intrinsic defects, V Cu is the most efficient acceptor in CuCrO 2 . It is found that all the donor-type extrinsic defects have difficulty in inducing n-conductivity in CuCrO 2 because of their deep transition energy level. For all the acceptor-type extrinsic defects, substituting Mg for Cr is the most prominent doping acceptor with relative shallow transition energy levels in CuCrO 2 . Our calculation results are expected to be a guide for preparing promising n-type and p-type materials in CuCrO 2 . (condensed matter: electronic structure, electrical, magnetic, and optical properties)

INFLUENCE OF ANNEALING ON HARDNESS OF Cr-Mn-Ni CAST IRONS

Directory of Open Access Journals (Sweden)

V. V. Netrebko

2015-01-01

Full Text Available The necessary level of material’s hardness is determined by the exploitation conditions and presence of technological operations during manufacturing of articles. Mechanical edge cutting machining of wear resistant materials is impeded because of their high hardness. It is recommended to apply annealing in order to decrease hardness and improve machinability. The purpose of the work consisted in obtaining of regression dependences of cast iron’s macrohardness on its chemical content after annealing at 730 °С. With the use of mathematical experimental design the regression dependences of cast iron’s macrohardness and structural components’ microhardness on С, Cr, Mn, Ni content have been established. The minimal hardness of 27,6 HRC after annealing at 730 °С is obtained in the cast iron containing: 3,9% С; 11,4% Cr; 0,6% Mn; 0,2% Ni. The maximal hardness of 70,4 HRC is obtained when the content is as follows: 1,1% С; 25,6% Cr; 5,4% Mn; 3,0% Ni. Annealing at 730 °С decreases the cast irons’ hardness containing the minimal amount of Cr, Mn and Ni. Annealing at 730 °С is recommended for cast irons alloyed by Mn and Ni for increasing of hardness.

27Al, 63Cu NMR spectroscopy and electrical transport in Heusler Cu-Mn-Al alloy powders

Science.gov (United States)

Nadutov, V. M.; Perekos, A. O.; Kokorin, V. V.; Trachevskii, V. V.; Konoplyuk, S. M.; Vashchuk, D. L.

2018-02-01

The ultrafine powder of the Heusler Cu-13,1Mn-12,6Al (wt.%) alloy produced by electrical spark dispersion (ESD) in ethanol and the pellets prepared by pressing of the powders and aged in various gas environment (air, Ar, vacuum) were studied by XRD, nuclear magnetic resonance, magnetic and electric transport methods. The constituent phases were identified as b.c.c. α-Cu-Mn-Al, f.c.c. γ-Cu-Mn-Al, Cu2MnAl, and oxides. The sizes of the coherently scattering domains (CSD) and the saturation magnetizations were in the range of 4-90 nm and 0-1.5 Am2/kg, respectively. 27Al and 63Cu NMR spectra of the powders and pellets have shown hyperfine structure caused by contributions from atomic nuclei of the constituent phases. The aging of pellets in different gas environments had effect on their phase composition but no effect on dispersion of the phases. In contrast to the as-cast alloy, electrical resistance of the pellets evidenced semiconducting behavior at elevated temperatures due to the presence of metal oxides formed on the surfaces of nanoparticles.

Synthesis and magnetic properties of hexagonal Y(Mn,Cu)O3 multiferroic materials

International Nuclear Information System (INIS)

Jeuvrey, L.; Peña, O.; Moure, A.; Moure, C.

2012-01-01

Single-phase hexagonal-type solid solutions based on the multiferroic YMnO 3 material were synthesized by a modified Pechini process. Copper doping at the B-site (YMn 1−x Cu x O 3 ; x 1+y MnO 3 ; y 3+ two-dimensional lattice. The magnetic transition at T N decreases from 70 K down to 49 K, when x(Cu) goes from 0 to 15 at%. Weak ferromagnetic Mn 3+ –Mn 4+ interactions created by the substitution of Mn 3+ by Cu 2+ , are visible through the coercive field and spontaneous magnetization but do not modify the overall magnetic frustration. Presence of Mn 3+ –Mn 4+ pairs leads to an increase of the electrical conductivity due to thermally-activated small-polaron hopping mechanisms. Results show that local ferromagnetic interactions can coexist within the frustrated state in the hexagonal polar structure. - Highlights: ► Hexagonal-type solid solutions of Y(Mn,Cu)O 3 synthesized by Pechini process. ► Chemical substitution at B site inhibits geometrical magnetic frustration. ► Magnetic transition decreases with Cu-doping. ► Local ferromagnetic Mn–Mn interactions coexist with the frustrated state.

Electronic, Magnetic, and Redox Properties of [MFe(3)S(4)] Clusters (M = Cd, Cu, Cr) in Pyrococcus furiosus Ferredoxin.

Science.gov (United States)

Staples, Christopher R.; Dhawan, Ish K.; Finnegan, Michael G.; Dwinell, Derek A.; Zhou, Zhi Hao; Huang, Heshu; Verhagen, Marc F. J. M.; Adams, Michael W. W.; Johnson, Michael K.

1997-12-03

The ground- and excited-state properties of heterometallic [CuFe(3)S(4)](2+,+), [CdFe(3)S(4)](2+,+), and [CrFe(3)S(4)](2+,+) cubane clusters assembled in Pyrococcus furiosus ferredoxin have been investigated by the combination of EPR and variable-temperature/variable-field magnetic circular dichroism (MCD) studies. The results indicate Cd(2+) incorporation into [Fe(3)S(4)](0,-) cluster fragments to yield S = 2 [CdFe(3)S(4)](2+) and S = (5)/(2) [CdFe(3)S(4)](+) clusters and Cu(+) incorporation into [Fe(3)S(4)](+,0) cluster fragments to yield S = (1)/(2) [CuFe(3)S(4)](2+) and S = 2 [CuFe(3)S(4)](+) clusters. This is the first report of the preparation of cubane type [CrFe(3)S(4)](2+,+) clusters, and the combination of EPR and MCD results indicates S = 0 and S = (3)/(2) ground states for the oxidized and reduced forms, respectively. Midpoint potentials for the [CdFe(3)S(4)](2+,+), [CrFe(3)S(4)](2+,+), and [CuFe(3)S(4)](2+,+) couples, E(m) = -470 +/- 15, -440 +/- 10, and +190 +/- 10 mV (vs NHE), respectively, were determined by EPR-monitored redox titrations or direct electrochemistry at a glassy carbon electrode. The trends in redox potential, ground-state spin, and electron delocalization of [MFe(3)S(4)](2+,+) clusters in P. furiosus ferredoxin are discussed as a function of heterometal (M = Cr, Mn, Fe, Co, Ni, Cu, Zn, Cd, and Tl).

Electrodeposition and Characterization of Mn-Cu-Zn Alloys for Corrosion Protection Coating

Science.gov (United States)

Tsurtsumia, Gigla; Gogoli, David; Koiava, Nana; Kakhniashvili, Izolda; Jokhadze, Nunu; Lezhava, Tinatin; Nioradze, Nikoloz; Tatishvili, Dimitri

2017-12-01

Mn-Cu-Zn alloys were electrodeposited from sulphate bath, containing citrate or EDTA and their mixtures as complexing ligands. The influence of bath composition and deposition parameters on alloys composition, cathodic current efficiency and structural and electrochemical properties were studied. At a higher current density (≥ 37.5 A dm-2) a uniform surface deposit of Mn-Cu-Zn was obtained. Optimal pH of electrolyte (0.3 mol/dm3Mn2+ + 0.6 mol/dm3 (NH4)2SO4 +0.1 mol/dm3Zn2++0.005 mol/dm3 Cu2++ 0.05mol/dm3Na3Cit + 0.15mol/dm3 EDTA; t=300C; τ=20 min) for silvery, nonporous coating of Mn-Cu-Zn alloy was within 6.5-7.5; coating composition: 71-83% Mn, 6-7.8% Cu, 11.5-20% Zn, current efficiency up to 40%. XRD patterns revealed BCT (body centred tetragonal) γ-Mn solid phase solution (lattice constants a=2.68 Å c=3.59 Å). Corrosion measurements of deposited alloys were performed in aerated 3.5% NaCl solution. The corrosion current density (icorr) of the electrodeposited alloys on carbon steel was 10 times lower than corrosion rate of pure zinc and manganese coatings. Triple alloy coatings corrosion potential (Ecorr = -1140 mV vs. Ag/AgCl) preserved negative potential value longer (more than three months) compared to carbon steel substrate (Ecorr = -670 mV vs. Ag/AgCl). Tafel polarization curves taken on Mn-Cu-Zn alloy coating in aerated 3.5% NaCl solution did not show a typical passivation behaviour which can be explained by formation oflow solubility of adherent corrosion products on the alloy surface. Corrosion test of Mn-Cu-Zn electrocoating in chlorine environment shows that it is the best cathodic protective coating for a steel product.

Effect of (Mn,Cr) co-doping on structural, electronic and magnetic properties of zinc oxide by first-principles studies

Science.gov (United States)

Aimouch, D. E.; Meskine, S.; Boukortt, A.; Zaoui, A.

2018-04-01

In this study, structural, electronic and magnetic properties of Mn doped (ZnO:Mn) and (Mn,Cr) co-doped zinc oxide (ZnO:(Mn,Cr)) have been calculated with the FP-LAPW method by using the LSDA and LSDA+U approximations. Going through three configurations of Mn,Cr co-doped ZnO corresponding to three different distances between manganese and chromium, we have analyzed that ZnO:(Mn,Cr) system is more stable in its preferred configuration2. The lattice constant of undoped ZnO that has been calculated in this study is in a good agreement with the experimental and theoretical values. It was found to be increased by doping with Mn or (Mn,Cr) impurities. The band structure calculations showed the metallic character of Mn doped and Mn,Cr co-doped ZnO. As results, by using LSDA+U (U = 6eV), we show the half-metallic character of ZnO:Mn and ZnO:Mn,Cr. We present the calculated exchange couplings d-d of Mn doped ZnO which is in a good agreement with the former FPLO calculation data and the magnetization step measurement of the experimental work. The magnetic coupling between neighboring Mn impurities in ZnO is found to be antiferromagnetic. In the case of (Mn,Cr) co-doped ZnO, the magnetic coupling between Mn and Cr impurities is found to be antiferromagnetic for configuration1 and 3, and ferromagnetic for configuration2. Thus, the ferromagnetic coupling is weak in ZnO:Mn. Chromium co-doping greatly enhance the ferromagnetism, especially when using configuration2. At last, we present the 2D and 3D spin-density distribution of ZnO:Mn and ZnO:(Mn,Cr) where the ferromagnetic state in ZnO:(Mn,Cr) comes from the strong p-d and d-d interactions between 2p-O, 3d-Mn and 3d-Cr electrons. The results of our calculations suggest that the co-doping ZnO(Mn, Cr) can be among DMS behavior for spintronic applications.

Wear behavior of Cu-Ag-Cr alloy wire under electrical sliding

International Nuclear Information System (INIS)

Jia, S.G.; Liu, P.; Ren, F.Z.; Tian, B.H.; Zheng, M.S.; Zhou, G.S.

2005-01-01

The wear behavior of a Cu-Ag-Cr alloy contact wire against a copper-base sintered alloy strip was investigated. Wear tests were conducted under laboratory conditions with a special sliding wear apparatus that simulated train motion under electrical current conditions. The initial microstructure of the Cu-Ag-Cr alloy contact wire was analyzed by transmission electron microscopy. Worn surfaces of the Cu-Ag-Cr alloy wire were analyzed by scanning electron microscopy (SEM) and energy dispersive X-ray spectrometry (EDS). The results indicate that the wear rate of the Cu-Ag-Cr wire increased with increasing electrical current and sliding. Within the studied range of electrical current, the wear rate increases with increasing electrical current and sliding speed. Compared with the Cu-Ag contact wire under the same testing conditions, the Cu-Ag-Cr alloy wire has much better wear resistance. Adhesive, abrasive, and electrical erosion wear are the dominant mechanisms during the electrical sliding processes

Binary and tertiary reaction cross-sections of V, Cr, Mn, Fe, Ni, Cu, Zr, Nb, Mo, Ta, W, Pt and their isotopes

International Nuclear Information System (INIS)

Garg, S.B.

1982-01-01

Neutron induced binary and tertiary reaction cross-sections have been evaluated for V, Cr, Mn, Fe, Ni, Cu, Zr, Nb, Mo, Ta, W, Pt and their isotopes in the 'energy range 0.5 MeV to 20 MeV using the nuclear statistical empirical model. The reactions considered are (n,n'), (n,2n), (n,3n), (n,p), (n,d), (n,t), (n, 3 He), (n,α), (n,np), (n,nd), (n,nt), (n,n 3 He), (n,nα), (n,pn), (n,2p), (n,ν), (n,αp), (n,dn) and (n,pα). Most of the above mentioned elements are used as structural materials in nuclear reactors and the measured cross-section data for the above listed reactions are seldom available for the radiation damage and safety analysis. With a view to providing these data, this nuclear model based evaluation has been undertaken. The associated uncertainties in the cross-sections and their fission averages have also been evaluated. (author)

Dislocation structure evolution and characterization in the compression deformed Mn-Cu alloy

International Nuclear Information System (INIS)

Zhong, Y.; Yin, F.; Sakaguchi, T.; Nagai, K.; Yang, K.

2007-01-01

Dislocation densities and dislocation structure arrangements in cold compressed polycrystalline commercial M2052 (Mn-20Cu-5Ni-2Fe) high damping alloy with various strains were determined in scanning mode by X-ray peak profile analysis and electron backscatter diffraction (EBSD). The results indicate that the Mn-Cu-Ni-Fe alloy has an evolution behavior quite similar to the dislocation structure in copper. The dislocation arrangement parameter shows a local minimum in the transition range between stages III and IV that can be related to the transformation of the dislocation arrangement in the cell walls from a polarized dipole wall (PDW) into a polarized tile wall (PTW) structure. This evolution is further confirmed by the results of local misorientation determined by EBSD. In addition, during deformation, the multiplication of dislocation densities in the MnCu alloy is significantly slower than that in copper, and the transition of the dislocation structure is strongly retarded in the MnCu alloy compared with copper. These results can be explained by the mechanism of elastic anisotropy on the dislocation dynamics, as the elastic anisotropy in the MnCu alloy is larger than that in copper, which can strongly retard the multiplication of the dislocation population and the transformation of the dislocation structure. These results are important for research into the plastic working behavior of Mn-Cu-Ni-Fe high damping alloy

Analysis of precipitation in a Cu-Cr-Zr alloy

Institute of Scientific and Technical Information of China (English)

Zhao Mei; Lin Guobiao; Wang Zidong; Zhang Maokui

2008-01-01

Precipites in Cu-0.42%Cr-0.21%Zr alloy were analyzed by using scanning electron microscope (SEM), energy dispersive X-ray spectroscopy (EDXS) and transmission electron microscope (TEM). After the solid solution was performed at 980℃ for 2 h, water-quenched and aged at 450℃ for 20 h, the precipite had a bimodal distribution of precipitate size. The coarse precipitates are pure Cr and Cu5Zr, the dispersed fine precipitate is CrCu2(Zr, Mg) and pure Cr ranging from 1 to 50 nm. The coarse phases formed during solidification and were left undissolved during solid solution. The fine precipitates are the hardening precipitates that form due to decomposition of the supersaturated solid solution during aging.

Deep Drawing Behavior of CoCrFeMnNi High-Entropy Alloys

Science.gov (United States)

Bae, Jae Wung; Moon, Jongun; Jang, Min Ji; Ahn, Dong-Hyun; Joo, Soo-Hyun; Jung, Jaimyun; Yim, Dami; Kim, Hyoung Seop

2017-09-01

Herein, the deep drawability and deep drawing behavior of an equiatomic CoCrFeMnNi HEA and its microstructure and texture evolution are first studied for future applications. The CoCrFeMnNi HEA is successfully drawn to a limit drawing ratio (LDR) of 2.14, while the planar anisotropy of the drawn cup specimen is negligible. The moderate combination of strain hardening exponent and strain rate sensitivity and the formation of deformation twins in the edge region play important roles in successful deep drawing. In the meanwhile, the texture evolution of CoCrFeMnNi HEA has similarities with conventional fcc metals.

Diffusion-induced quadrupole relaxation of 27Al nuclei in dilute Al-Ti, Al-Cr, Al-Mn, and Al-Cu alloys at high temperatures

International Nuclear Information System (INIS)

Bottyan, L.; Beke, D.L.; Tompa, K.

1983-01-01

The temperature dependence of the laboratory frame spin-lattice relaxation time of 27 Al nuclei is measured in 5N Al and in dilute Al-Ti, Al-Cr, Al-Mn, and Al-Cu alloys at 5.7 and 9.7 MHz resonance frequencies. The relaxation in pure aluminium is found to be purely due to the conduction electrons. An excess T 1 -relaxation contribution is detected in all Al-3d alloys investigated above 670 K. The excess relaxation rate is proportional to the impurity content and the temperature dependence of the excess contribution is of Arrhenius-type with an activation energy of (1.3 +- 0.3) eV for all of the investigated alloys. The relaxation contribution is found to be quadrupolar in origin and is caused by the relative diffusional jumps of solute atoms and Al atoms relatively far from the impurity. (author)

Using precipitated Cr on the surface of Cu-Cr alloy powders as catalyst synthesizing CNTs/Cu composite powders by water-assisted CVD

Science.gov (United States)

Zhou, Honglei; Liu, Ping; Chen, Xiaohong; Bi, Liming; Zhang, Ke; Liu, Xinkuan; Li, Wei; Ma, Fengcang

2018-02-01

Given that the conventional catalyst is easily soluble in the matrix to result in the poor performance of the CNTs/Cu composite materials, the Cr nano-particles precipitated on the surface of Cu-Cr particles are first used as catalysts to prepare the CNTs/Cu composite powders by means of water-assisted chemical vapor deposition in situ synthesis. The results show that the morphological difference of the precipitated Cr nano-particle is obvious with the change of solution and aging treatment, and the morphology, length and diameter of the synthetic CNTs are also different. The catalyst of Cr nano-particle has the best morphology and the synthesized CNTs had a good wettability with Cu particles when the Cu-Cr composite powders was solution-treated at 1023 K for 60 min and then was aged at 723 K for 120 min. The length, diameter, yield and purity of the synthesized CNTs can be also affected by the moisture content in the reaction gas. It is the most suitable for the growth of CNTs when the moisture content is 0.4%, and the high purity and defect-free CNTs with the smooth pipe wall, a diameter of 20 ˜ 30 nm and a length of up to 1800 nm can be obtained. The yield of CNTs with the moisture content of 0.4% reached to 138%, which was increased by 119% to compare with that without moisture. In this paper, a feasible technology was offered for the preparation of high performance CNTs/Cu composites.

Complex impedance spectra of chip inductor using Li-Zn-Cu-Mn ferrite

International Nuclear Information System (INIS)

Nakamura, Tatsuya; Naoe, Masayuki; Yamada, Yoshihiro

2006-01-01

A multi-layer chip inductor (MCI) was fabricated using polycrystalline Li-Zn-Cu-Mn ferrite and the green-sheet technique, and its complex impedance spectrum was evaluated with the help of numerical calculations. The complex impedance spectra of the MCI component using Ni-Zn-Cu ferrite, which have been widely used for this application, were very sensitive to the residual stress and deviated much from the calculated values; however, it was found that the complex impedance spectrum of the MCI component using Li-Zn-Cu-Mn ferrite is quite well reproduced by calculation, where the complex permittivity and permeability of the polycrystalline ferrite as well as the MCI dimensions, were used. It implied that the magneto-striction effect was negligible in case of MCI using Li-Zn-Cu-Mn ferrite, and that the difference was related to magneto-strictive coefficient of the polycrystalline ferrite. Consequently, utilization of Li-Zn-Cu-Mn ferrite enabled us to easily design the complex impedance of MCI component

Low-field spin dynamics of Cr7Ni and Cr7Ni-Cu -Cr 7Ni molecular rings as detected by μ SR

Science.gov (United States)

Sanna, S.; Arosio, P.; Bordonali, L.; Adelnia, F.; Mariani, M.; Garlatti, E.; Baines, C.; Amato, A.; Sabareesh, K. P. V.; Timco, G.; Winpenny, R. E. P.; Blundell, S. J.; Lascialfari, A.

2017-11-01

Muon spin rotation measurements were used to investigate the spin dynamics of heterometallic Cr7Ni and Cr7Ni -Cu-Cr7Ni molecular clusters. In Cr7Ni the magnetic ions are arranged in a quasiplanar ring and interact via an antiferromagnetic exchange coupling constant J , while Cr7Ni -Cu-Cr7Ni is composed of two Cr7Ni linked by a bridging moiety containing one Cu ion, that induces an inter-ring ferromagnetic interaction J'≪J . The longitudinal muon relaxation rate λ collected at low magnetic fields μ0H BPP)-like heuristic fitting model that takes into account of a distribution of electronic spin characteristic times for T >5 K, while the shoulder presented by Cr7Ni can be reproduced by a BPP function that incorporates a single electronic characteristic time theoretically predicted to dominate for T <5 K. The flattening of λ (T ) in Cr7Ni -Cu-Cr7Ni occurring at very low temperature can be tentatively attributed to field-dependent quantum effects and/or to an inelastic term in the spectral density of the electronic spin fluctuations.

Relaxation of magnetization in spinel CuCrZrS4

International Nuclear Information System (INIS)

Ito, Masakazu; Furuta, Tatsuya; Terada, Norio; Ebisu, Shuji; Nagata, Shoichi

2012-01-01

We studied time t dependence of magnetization M(t) of thiospinel CuCrZrS 4 which has a spin-glass freezing. The relaxation of M is observed below T f ≃6K and shows a logarithmic time dependence. This means that a relaxation time τ of CuCrZrS 4 is distributed in a wide time range. Randomness of an arrangement of the Cr and Zr ions in CuCrZrS 4 probably gives rise to a distribution of τ. Temperature T dependence of magnetic viscosity β(T) is understood by a conventional after-effect model with a box-type distribution function of τ.

Ostwald ripening of decomposed phases in Cu-Ni-Cr alloys

International Nuclear Information System (INIS)

Hernandez-Santiago, Felipe; Lopez-Hirata, Victor; Dorantes-Rosales, Hector J.; Saucedo-Munoz, Maribel L.; Gonzalez-Velazquez, Jorge L.; Paniagua-Mercado, Ana Ma.

2008-01-01

A study of the coarsening process of the decomposed phases was carried out in the Cu-34 wt.% Ni-4 wt.% Cr and Cu-45 wt.% Ni-10 wt.% Cr alloys using transmission electron microscopy. As aging progressed, the morphology of the coherent decomposed Ni-rich phase changed from cuboids to platelets aligned in the Cu-rich matrix directions. Prolonged aging caused the loss of coherency between the decomposed phases and the morphology of the Ni-rich phase changed to ellipsoidal. The variation of mean radius of the coherent decomposed phases with aging time followed the modified LSW theory for thermally activated growth in ternary alloy systems. The linear variation of the density number of precipitates and matrix supersaturation with aging time, also confirmed that the coarsening process followed the modified LSW theory in both alloys. The coarsening rate was faster in the symmetrical Cu-45 wt.% Ni-10 wt.% Cr alloy due to its higher volume fraction of precipitates. The activation energy for thermally activated growth was determined to be about 182 and 102 kJ mol -1 in the Cu-34 wt.% Ni-4 wt.% Cr and Cu-45 wt.% Ni-10 wt.% Cr alloys, respectively. The lower energy for the former alloy seems to be related to an increase in the atomic diffusion process as the chromium content increases. The size distributions of precipitates in the Cu-Ni-Cr alloys were broader and more symmetric than that predicted by the modified LSW theory for ternary alloys

Study of polyoxide catalysts of methane combustion on Mn, Cu, Ni, rare earth elements, alkaline earth elements base by the X-ray fluorescence analysis method

International Nuclear Information System (INIS)

Grigor'eva, V.P.; Popova, N.M.; Zheksenbaeva, Z.T.; Sass, A.S.; Salakhova, R.Kh.; Dosumov, K.D.

2002-01-01

The results of X-ray fluorescence analysis of polyoxide catalysts on of Mn, Cu, Ni, rare earth elements, alkaline earth elements base supported on 2 % Ce/θ-Al 2 O 3 are presented. This polyoxide catalysts are using for deep methane oxidation. DRON-4-7 X-ray diffractometers was applied for the analysis. It was found, that oxides in Ni-Cu-Cr catalysts after long time heating up to 1200 deg. C have been interacted with catalyst supports with Ni(Cu)Al 2 O 3 aluminates formation and due to its decomposition transformation degree of CH 4 to CO 2 are reduced. Activity of MnBaSrCeLa catalysts after heating up to 1200 deg. C does not changed

Effect of foliar applied (Zn, Fe, Cu and Mn) in citrus production

International Nuclear Information System (INIS)

Khurshid, F.; Sarwar, S.; Khattak, R.A.

2008-01-01

A study was conducted to evaluate the impact of micronutrients (Zn, Fe, Cu and Mn) on sweet orange (Citrus Sinensis L.), blood red var., on farmer's orchard at Khanpur, district Haripur, NWFP, during 2002-03. Micronutrients were applied in foliar sprays over the canopy of each tree. The main effects and interactions of Zinc sulphate (Zn), iron sulphate (Fe), Copper Sulphate (Cu) and Manganese Sulphate (Mn) were studied in factorial combinations. A basal dose of nitrogen, phosphorus and potassium was applied at the rate 1.5, 1 and 1 kg tree/sup -1/. Zn, Fe, Cu and Mn were applied alone and in various combinations at the rate 0.115, 0.057, 0.05 and 0.13 kg in 100 liters of water. Application of micronutrients significantly increased Zn, Fe, Cu and Mn concentrations in leaves, compared with control. Zn treatments significantly increased the yield, number of fruit and total sugar. Manganese treatments significantly increased the total soluble solids and reduced the acidity of fruit juice. Other quality parameters, including fruit size, percent peel, percent pulp, sugar as well as total soluble solids, were improved with the application of Zn, Fe, Cu and Mn. (author)

Enhancing the CuCrZr/316L HIP-joint by Ni electroplating

Energy Technology Data Exchange (ETDEWEB)

Wei, R. [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Science Island Branch of Graduate School, University of Science & Technology of China, Hefei, 230031 (China); Zhao, S.X., E-mail: sxzhao@impcas.ac.cn [Institute of Modern Physics, Chinese Academy of Science, Lanzhou, 730000 (China); Dong, H.; Che, H.Y. [Advanced Technology and Materials Co. Ltd., Beijing, 100081 (China); Li, Q.; Wang, W.J.; Wang, J.C.; Wang, X.L.; Sun, Z.X. [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Luo, G.-N. [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei, 230031 (China); Science Island Branch of Graduate School, University of Science & Technology of China, Hefei, 230031 (China); Hefei Center for Physical Science and Technology, Hefei, 230022 (China); Hefei Science Center of Chinese Academy of Sciences, Hefei, 230027 (China)

2017-04-15

Highlights: • The quality of CuCrZr/316L HIP-joint can be enhanced by nickel electroplating on CuCrZr and 316L. • Nickel layer can prevent the occurrence of nickel-poor region in 316L and protect CuCrZr from oxidation. • A Charpy Impact Value as high as 111.5 ± 3.3 J/cm{sup 2} can be obtained by HIP at 980 °C, 140 MPa for 2 h. • At high temperature, CuCrZr is easily oxidized even in the situation of a high vacuum degree of 2 × 10{sup −5} Pa. - Abstract: The quality of CuCrZr/316L joint is crucial for the safety of ITER hypervapotron cooling structure and hot isostatic pressing (HIP) is an important bonding technique for this structure. In this paper, the authors present a finding that the CuCrZr/316L HIP-joint can be enhanced by nickel electroplating on 316L and CuCrZr. A Charpy Impact Value as high as 111.5 ± 3.3 J/cm{sup 2}, which is more than two times the value in a published article, is obtained. The influence of nickel electroplating is twofold: (1) it can prevent the occurrence of nickel-poor region in 316L and the formation of ferrite; (2) it can protect CuCrZr from oxidation during the heating stage of HIP. However, tensile test is not as effective as Charpy Impact Test in characterizing the bonding quality of the CuCrZr/316L HIP-joint. The surface treatment employed in this study is amenable to batch-scale industrial manufacturing at low cost.

Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe2O6

International Nuclear Information System (INIS)

Batuk, Dmitry; De Dobbelaere, Christopher; Tsirlin, Alexander A.; Abakumov, Artem M.; Hardy, An; Van Bael, Marlies K.; Greenblatt, Martha; Hadermann, Joke

2013-01-01

Graphical abstract: - Highlights: • The substitution of Cr for Mn in BiMnFe 2 O 6 is possible by the solution–gel method. • The BiCr x Mn 1−x Fe 2 O 6 solid solution is obtained for the x values up to 0.3. • Increasing Cr content lowers the temperature of the antiferromagnetic ordering. - Abstract: We report the Cr 3+ for Mn 3+ substitution in the BiMnFe 2 O 6 structure. The BiCr x Mn 1−x Fe 2 O 6 solid solution is obtained by the solution–gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe 2 O 6 structure (for x = 0.3, a = 5.02010(6)Å, b = 7.06594(7)Å, c = 12.6174(1)Å, S.G. Pbcm, R I = 0.036, R P = 0.011) with only a slight decrease in the cell parameters associated with the Cr 3+ for Mn 3+ substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCr x Mn 1−x Fe 2 O 6 (x = 0.2; 0.3) and parent BiMnFe 2 O 6 . Only T N slightly decreases upon Cr doping that indicates a very subtle influence of Cr 3+ cations on the magnetic properties at the available substitution rates

High temperature strength and aging behavior of 12%Cr-15%Mn austenitic steels

International Nuclear Information System (INIS)

Miyahara, Kazuya; Bae, Dong-Su; Sakai, Hidenori; Hosoi, Yuzo

1993-01-01

High Mn-Cr austenitic steels are still considered to be an important high temperature structural material from the point of view of reduced radio-activation. The objective of the present study is to make a fundamental research of mechanical properties and microstructure of 12%Cr-15%Mn austenitic steels. Especially the effects of alloying elements of V and Ti on the mechanical properties and microstructure evolution of high Mn-Cr steels were studied. Precipitation behaviors of carbides, nitrides and σ phase are investigated and their remarkable effects on the high temperature strength are found. The addition of V was very effective for strengthening the materials with the precipitation of fine VN. Ti was also found to be beneficial for the improvement of high temperature strength properties. The results of high temperature strengths of the 12Cr-15Mn austenitic steels were compared with those of the other candidate and/or reference materials, for example, JFMS (modified 9Cr-2Mo ferritic stainless steel) and JPCAs (modified 316 austenitic stainless steels). (author)

Suppression of antiferromagnetic interactions through Cu vacancies in Mn-substituted CuInSe2 chalcopyrites

International Nuclear Information System (INIS)

Yao Jinlei; Brunetta, Carl D; Aitken, Jennifer A

2012-01-01

Stoichiometric and Cu-poor Cu 0.95-x Mn 0.05 InSe 2 (x = 0-0.20) compounds were synthesized by high-temperature, solid-state reactions. The presence of copper vacancies is revealed by Rietveld refinements of combined neutron and x-ray powder diffraction data. The antiferromagnetic interaction is depressed by the copper deficiency, which may be explained as the competition between the antiferromagnetic Mn-Se-eMn superexchange interaction and the hole-mediated ferromagnetic exchange induced by the copper vacancy. The introduction of copper vacancies is proposed to be a viable route to impart carrier-mediated ferromagnetic exchange in the chalcopyrite-based dilute magnetic semiconductors. (paper)

Formation and structure of nanocrystalline Al-Mn-Ni-Cu alloys

International Nuclear Information System (INIS)

Latuch, J.; Krasnowski, M.; Ciesielska, B.

2002-01-01

This paper reports the results of the short investigation on the effect of Cu additions upon the nanocrystallization behaviour of an Al-Mn-Ni alloy. 2 at.% Cu added to the base alloy of Al 85 Mn 10 Ni 5 alloy by substitution for Mn(mischmetal). The control of cooling rate did not cause the formation of nanocrystals of fcc-Al phase. The nanocrystalline structure fcc-Al + amorphous phase in quarternary alloy was obtained by isothermal annealing and continuous heating method, but the last technique is more effective. The volume fraction, lattice parameter, and size of Al-phase were calculated. (author)

Redox Dynamics of Mixed Metal (Mn, Cr, and Fe) Ultrafine Particles

Energy Technology Data Exchange (ETDEWEB)

Nico, Peter S.; Kumfer, Benjamin M.; Kennedy, Ian M.; Anastasio, Cort

2008-08-01

The impact of particle composition on metal oxidation state, and on changes in oxidation state with simulated atmospheric aging, are investigated experimentally in flame-generated nanoparticles containing Mn, Cr, and Fe. The results demonstrate that the initial fraction of Cr(VI) within the particles decreases with increasing total metal concentration in the flame. In contrast, the initial Mn oxidation state was only partly controlled by metal loading, suggesting the importance of other factors. Two reaction pathways, one reductive and one oxidative, were found to be operating simultaneously during simulated atmospheric aging. The oxidative pathway depended upon the presence of simulated sunlight and O{sub 3}, whereas the reductive pathway occurred in the presence of simulated sunlight alone. The reductive pathway appears to be rapid but transient, allowing the oxidative pathway to dominate with longer aging times, i.e. greater than {approx}8 hours. The presence of Mn within the particles enhanced the importance of the oxidative pathway, leading to more net Cr oxidation during aging implying that Mn can mediate oxidation by removal of electrons from other particulate metals.

NMR of Cu satellites in the Kondo alloy CuCr

International Nuclear Information System (INIS)

Azevedo, L.J.; Follstaedt, D.; Narath, A.

1978-01-01

Using pulsed NMR techniques, resonances of Cu nuclei which are near neighbors to Cr impurities (c = 100 and 200 ppM) in CuCr (theta/sub k/ approx. 3K) have been studied in the temperature range 1 to 4K and applied fields H 0 = 20 to 125 kOe. At the highest fields and lowest temperatures the satellite shifts approach saturation. Above approx. 40 kOe the spin-lattice relaxation rate T 1 -1 is proportional to T/H 0 2 , indicating that the dominant relaxation mechanism arises from transverse fluctuations of a polarized local moment. The measured rates yield a local-moment/conduction-electron exchange interaction vertical bar J 0 vertical bar/g = 0.30, where g is the Cr g-value. Below approx. 40 kOe T 1 -1 appears to be slightly enhanced in comparison with the high-field behavior, but becomes field independent below approx. 30 kOe. Both effects are attributed to Kondo anomalies

High-Strength Ultra-Fine-Grained Hypereutectic Al-Si-Fe-X (X = Cr, Mn) Alloys Prepared by Short-Term Mechanical Alloying and Spark Plasma Sintering.

Science.gov (United States)

Průša, Filip; Bláhová, Markéta; Vojtěch, Dalibor; Kučera, Vojtěch; Bernatiková, Adriana; Kubatík, Tomáš František; Michalcová, Alena

2016-11-30

In this work, Al-20Si-10Fe-6Cr and Al-20Si-10Fe-6Mn (wt %) alloys were prepared by a combination of short-term mechanical alloying and spark plasma sintering. The microstructure was composed of homogeneously dispersed intermetallic particles forming composite-like structures. X-ray diffraction analysis and TEM + EDS analysis determined that the α-Al along with α-Al 15 (Fe,Cr)₃Si₂ or α-Al 15 (Fe,Mn)₃Si₂ phases were present, with dimensions below 130 nm. The highest hardness of 380 ± 7 HV5 was observed for the Al-20Si-10Fe-6Mn alloy, exceeding the hardness of the reference as-cast Al-12Si-1Cu-1 Mg-1Ni alloy (121 ± 2 HV5) by nearly a factor of three. Both of the prepared alloys showed exceptional thermal stability with the hardness remaining almost the same even after 100 h of annealing at 400 °C. Additionally, the compressive strengths of the Al-20Si-10Fe-6Cr and Al-20Si-10Fe-6Mn alloys reached 869 MPa and 887 MPa, respectively, and had virtually the same values of 870 MPa and 865 MPa, respectively, even after 100 h of annealing. More importantly, the alloys showed an increase in ductility at 400 °C, reaching several tens of percent. Thus, both of the investigated alloys showed better mechanical properties, including superior hardness, compressive strength and thermal stability, as compared to the reference Al-10Si-1Cu-1Mg-1Ni alloy, which softened remarkably, reducing its hardness by almost 50% to 63 ± 8 HV5.

High-Strength Ultra-Fine-Grained Hypereutectic Al-Si-Fe-X (X = Cr, Mn) Alloys Prepared by Short-Term Mechanical Alloying and Spark Plasma Sintering

Science.gov (United States)

Průša, Filip; Bláhová, Markéta; Vojtěch, Dalibor; Kučera, Vojtěch; Bernatiková, Adriana; Kubatík, Tomáš František; Michalcová, Alena

2016-01-01

In this work, Al-20Si-10Fe-6Cr and Al-20Si-10Fe-6Mn (wt %) alloys were prepared by a combination of short-term mechanical alloying and spark plasma sintering. The microstructure was composed of homogeneously dispersed intermetallic particles forming composite-like structures. X-ray diffraction analysis and TEM + EDS analysis determined that the α-Al along with α-Al15(Fe,Cr)3Si2 or α-Al15(Fe,Mn)3Si2 phases were present, with dimensions below 130 nm. The highest hardness of 380 ± 7 HV5 was observed for the Al-20Si-10Fe-6Mn alloy, exceeding the hardness of the reference as-cast Al-12Si-1Cu-1 Mg-1Ni alloy (121 ± 2 HV5) by nearly a factor of three. Both of the prepared alloys showed exceptional thermal stability with the hardness remaining almost the same even after 100 h of annealing at 400 °C. Additionally, the compressive strengths of the Al-20Si-10Fe-6Cr and Al-20Si-10Fe-6Mn alloys reached 869 MPa and 887 MPa, respectively, and had virtually the same values of 870 MPa and 865 MPa, respectively, even after 100 h of annealing. More importantly, the alloys showed an increase in ductility at 400 °C, reaching several tens of percent. Thus, both of the investigated alloys showed better mechanical properties, including superior hardness, compressive strength and thermal stability, as compared to the reference Al-10Si-1Cu-1Mg-1Ni alloy, which softened remarkably, reducing its hardness by almost 50% to 63 ± 8 HV5. PMID:28774094

Microstructure and Electrical Properties of Fe,Cu Substituted (Co,Mn)3O4 Thin Films

DEFF Research Database (Denmark)

Szymczewska, Dagmara; Molin, Sebastian; Hendriksen, Peter Vang

2017-01-01

In this work, thin films (~1000 nm) of a pure MnCo2O4 spinel together with its partially substituted derivatives (MnCo1.6Cu0.2Fe0.2O4, MnCo1.6Cu0.4O4, MnCo1.6Fe0.4O4) were prepared by spray pyrolysis and were evaluated for electrical conductivity. Doping by Cu increases the electrical conductivit...

Structural and magnetic properties of Cr and Mn doped InN

International Nuclear Information System (INIS)

Ney, A.; Rajaram, R.; Arenholz, E.; Harris, J.S.; Samant, M.; Farrow, R.F.C.; Parkin, S.S.P.

2006-01-01

We present a detailed magnetic characterization of Cr and Mn doped InN films be means of superconducting quantum interference device magnetometry and X-ray magnetic circular dichroism. The InN:Cr films exhibit ferromagnetic behavior up to 300 K in a doping region from 2% to 8% without detectable phase segregation. The easy axis of magnetization is found to be in the film plane. On the contrary, Mn-doped films show signatures of phase segregation and paramagnetic behavior

Quasicrystalline and crystalline phases in Al65Cu20(Fe, Cr)15 alloys

International Nuclear Information System (INIS)

Liu, W.; Koester, U.; Mueller, F.; Rosenberg, M.

1992-01-01

Two types of icosahedral quasicrystals are observed in Al 65 Cu 20 Fe 15-x Cr x (0 ≤ x ≤ 15) alloys, the face-centred AlCuFe-type icosahedral phase with dissoluted Cr and the primitive AlCuCr-type icosahedral phase with dissoluted Fe. In the vicinity of Al 65 Cu 20 Fe 8 Cr 7 a stable decagonal phase (a=0.45 nm and c=1.23 nm) forms competitively with the icosahedral quasicrystals. All these three quasicrystalline phases can be regarded as Hume-Rothery phases stabilized by the energy band factor. The density is measured to be 4.57, 4.44, and 4.11 g/cm 3 for the icosahedral Al 65 Cu 20 Fe 15 , the decagonal Al 65 Cu 20 Fe 8 Cr 7 , and the icosahedral Al 65 Cu 20 Cr 15 alloys, respectively. Depending on the composition in the range between Al 65 Cu 20 Fe 8 Cr 7 and Al 65 Cu 20 Cr 15 , several crystalline phases are observed during the transormation of the AlCuCr-type icosahedral phase: the 1/1-3/2-type orthorhombic (o) and the 1/0-3/2-type tetragonal (t) approximants of the decagonal phase, a hexagonal (h) phase, as well as a long-range vacancy ordered τ 3 -phase derived from a CsCl-type structure with a=0.2923 nm. The structures of all the crystalline phases are closely related to those of the icosahedral (i) and decagonal (d) quasicrystals, which leads to a definite orientation relationship as follows: i5 parallel d10 parallel o[100] parallel t[100] parallel h[001] parallel τ 3 [110]. (orig.)

Cobalt doped CuMnOx catalysts for the preferential oxidation of carbon monoxide

Science.gov (United States)

Dey, Subhashish; Dhal, Ganesh Chandra; Mohan, Devendra; Prasad, Ram; Gupta, Rajeev Nayan

2018-05-01

Carbon monoxide (CO) is a poisonous gas, recognized as a silent killer for the 21st century. It is produced from the partial oxidation of carbon containing compounds. The catalytic oxidation of CO receives a huge attention due to its applications in different fields. In the present work, hopcalite (CuMnOx) catalysts were synthesized using a co-precipitation method for CO oxidation purposes. Also, it was doped with the cobalt by varying concentration from 1 to 5wt%. It was observed that the addition of cobalt into the CuMnOx catalyst (by the deposition-precipitation method) improved the catalytic performance for the low-temperature CO oxidation. CuMnOx catalyst doped with 3wt% of cobalt exhibited most active performance and showed the highest activity than other cobalt concentrations. Different analytical tools (i.e. XRD, FTIR, BET, XPS and SEM-EDX) were used to characterize the as-synthesized catalysts. It was expected that the introduction of cobalt will introduce new active sites into the CuMnOx catalyst that are associated with the cobalt nano-particles. The order of calcination strategies based on the activity for cobalt doped CuMnOx catalysts was observed as: Reactive calcinations (RC) > flowing air > stagnant air. Therefore, RC (4.5% CO in air) route can be recommended for the synthesis of highly active catalysts. The catalytic activity of doped CuMnOx catalysts toward CO oxidation shows a correlation among average oxidation number of Mn and the position and the nature of the doped cobalt cation.

Preparation of catalysts based on Cu-Mn for combustion of n-hexane

International Nuclear Information System (INIS)

Picasso, Gino; Belleza, Freddy; Zavala, Cesar; Lopez, Alcides; Sun Kou, Rosario

2014-01-01

Catalysts based on Cu-Mn mixed oxides (with molar ratio Cu/Mn in the range of 0,33 to 3) have been prepared by sol-gel method of self-combustion for removal of n-hexane. Two combustion agents, citric acid and ethylenglycol, were applied to study their influence in the final catalyst. Additionally, simple oxides have been synthesized using the same procedure for comparison reasons. The catalysts were characterized by X-ray diffraction (XRD) and sorption of N_2 (BET method). All samples depicted surfaces, preferentially assigned to mesoporosity whose values ranged from 4 to 50 m"2/g. All XRD difractograms of mixed samples showed the presence of a good crystalinity indepently of composition, with the formation of spinel-hopcalite phase meanwhile Mn and Cu simple oxide showed peaks attributed to Mn_O_3, Mn_3O_4 and CuO, respectively. Curves of activity, measured as number of VOC molecules converted per hour and per gram of catalyst, considering the specific surface, showed that mixed oxides with more Mn content were the best, additionally, the sample prepared from citric acid was more active than the corresponding values to simple oxides, probably due to the better specific surface and the better spinel-hopcalite structure obtained. (author)

X-ray attenuation coefficient measurements for photon energies 4.508-13.375 keV in Cu, Cr and their compounds and the validity of the mixture rule

International Nuclear Information System (INIS)

Turgut, Ue.; Simsek, Oe.; Bueyuekkasap, E.; Ertugrul, M.

2004-01-01

To investigate the validity of the mixture rule which is used to compute the mass attenuation coefficients in compounds, the total mass attenuation coefficients for Cu, Cr elements and Cu 2 O, CuC 2 O 4 , CuCl 2 ·2H 2 O, Cu(C 2 H 3 O 2 ) 2 ·H 2 O, Cr 2 O 3 , Cr(NO 3 ) 3 , Cr 2 (SO 4 ) 3 ·H 2 O, Cr 3 (CH 3 CO 7 )(OH) 2 compounds were measured at photon energies between 4.508 and 13.375 keV by using the secondary excitation method. Ti, Mn, Fe, Ni, Zn, Ge, As, Rb elements were used as secondary exciters. 59.5 keV gamma rays emitted from an 241 Am annular source were used to excite the secondary exciters and Kα (K-L 3 , L 2 ) rays emitted from the secondary exciter were counted by a Si(Li) detector with a resolution of 160 eV at 5.9 keV. Our measurements indicate that the mixture rule is not a suitable method for the computation of mass attenuation coefficients of compounds especially at an energy that is near the absorption edge. Obtained values were compared with theoretical values

Precise Wavelengths and Energy Levels for the Spectra of Cr I, Mn I, and Mn III, and Branching Fractions for the Spectra of Fe II and Cr II

Science.gov (United States)

Nave, Gillian

I propose to measure wavelengths and energy levels for the spectra of Cr I, Mn I, and Mn III covering the wavelength range 80 nm to 5500 nm, and oscillator strengths for Fe II and Cr II in the region 120 nm to 2500 nm. I shall also produce intensity calibrated atlases and linelists of the iron-neon and chromium-neon hollow cathode lamps that can be compared with astrophysical spectra. The spectra will be obtained from archival data from spectrometers at NIST and Kitt Peak National Observatory and additional experimental observations as necessary from Fourier transform (FT) and grating spectrometers at NIST. The wavelength uncertainty of the strong lines will be better than 1 part in 10^7. The radiometric calibration of the spectra will be improved in order to reduce the uncertainty of measured oscillator strengths in the near UV region and extend the wavelength range of these measurements down to 120 nm. These will complement and support the measurements of lifetimes and branching fractions by J. E. Lawler in the near UV region. An intensive effort by NIST and Imperial College London that was partly funded by previous NASA awards has resulted in comprehensive analyses of the spectra of Fe II, Cr II and Cu II, with similar analyses of Mn II, Ni II, and Sc II underway. The species included in this proposal will complete the analysis of the first two ionization stages of the elements titanium through nickel using the same techniques, and add the spectrum of Mn III - one of the most important doubly-ionized elements. The elements Cr I and Mn I give large numbers of spectral lines in spectra of cool stars and important absorption lines in the interstellar medium. The spectrum of Mn III is important in chemically peculiar stars and can often only be studied in the UV region. Analyses of many stellar spectra depend on comprehensive analyses of iron-group elements and are hampered by incomplete spectroscopic data. As a result of many decades of work by the group at the

Low-activation Mn-Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

Energy Technology Data Exchange (ETDEWEB)

Onozuka, M.; Saida, T.; Hirai, S. [Mitsubishi Heavy Ind. Ltd., Yokohama (Japan); Kusuhashi, M.; Sato, I.; Hatakeyama, T. [The Japan Steel Works Ltd., Chatsu-machi 4, Muroran 051-8505 (Japan)

1998-06-01

Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels. (orig.) 22 refs.

Low-activation Mn Cr austenitic stainless steel with further reduced content of long-lived radioactive elements

Science.gov (United States)

Onozuka, Masanori; Saida, Tomikane; Hirai, Shouzou; Kusuhashi, Mikio; Sato, Ikuo; Hatakeyama, Tsuyoshi

1998-06-01

Low-activation austenitic stainless steel based on Mn-Cr non-magnetic steels has been developed. The alloying elements of long-life activation, such as Ni, Mo and Co, were eliminated and substituted with Mn along with an addition of N. A Mn-Cr austenitic stainless steel, 24.5Mn-13.5Cr-0.02C-0.2N, has been developed successfully. Examined material properties, including mechanical, thermal and magnetic properties, as well as weldability and characteristics of corrosion resistance, are presented. It was found that the alloy has excellent material properties virtually equivalent to those of 316SS. In this study, the applicability of the Schaeffler, DeLong and Hull constitution diagrams for the stainless steels with low Ni and high Mn contents was also examined. The boundary conditions distinguishing the single austenite phase from the others have been identified for the Mn-Cr steels.

Revealing the Microstructural evolution in Cu-Cr nanocrystalline alloys during high pressure torsion

Energy Technology Data Exchange (ETDEWEB)

Guo, Jinming; Rosalie, Julian M.; Pippan, Reinhard; Zhang, Zaoli, E-mail: zaoli.zhang@oeaw.ac.at

2017-05-17

Usually immiscible Cu-Cr compounds in equilibrium condition were mechanically processed via high pressure torsion with large and controlled strains. A systematical investigation on 57 wt%Cu − 43 wt%Cr was carried out to get insights into the microstructural evolution of Cu-Cr nanocomposites and their dissolution process, as well as to determine the solid solubility limit of Cu and Cr elements under severe deformation. Microstructural evolution was captured with grain refinement from micron-size down to less than 20 nm as the increase of strains. A strain-saturated state in 57 wt%Cu − 43 wt%Cr bulk was achieved after 100 rotations deformation (effective strain 1360), with a stable grain size of 13.7 nm and invariable hardness of 480–495 HV. Fine scanning of X-ray diffraction and sub-nanometer scale measurements of energy-dispersive X-ray spectroscopy showed that 32 wt% Cu could be fully dissolved into Cr matrix, and conversely solubility of Cr in Cu was determined to be about 3 wt% after an enough amount of deformation. The phase fraction change associated with Cu dissolution into Cr matrix during continuous deformation was captured and accurately calculated, indicating a negative exponential phase change mode. A phenomenological intermixing mechanism based on the kinetic competition between external forcing mixing and thermal-diffusion induced decomposition was proposed, which was well accordant with the phase evolution observed from experimental results.

Effect of manganese and chromium on microstructure and toughness of Fe-Cr-Mn alloys resulting from solid-solution treatment

International Nuclear Information System (INIS)

Okazaki, Yoshimitsu; Miyahara, Kazuya; Wade, Noboru; Hosoi, Yuzo

1989-01-01

This study is aimed at making clear the effect of Mn and Cr on the microstructure and toughness of an Fe-Cr-Mn alloy which is considered as one of the candidate alloys for reduced activation materials for the first wall application of the fusion reactor. The microstructures of Fe-12% Cr-(5∼30)% Mn(mass%) alloys after solution treatment at 1373 K for 3.6 ks are markedly varied with Mn contents; α'(martensite) + δ(ferrite) in 5% Mn alloy, α' + δ + ε(martensite) + γ(austenite) in the 10% Mn alloy, α' + ε + γ in 15% Mn alloy, ε + γ in the 20% Mn alloy, and ε + γ +δ in the 25% Mn alloy, and γ + δ in the 30% Mn alloy. It is to be noted that the δ phase increases with increasing Mn content when the Fe-12% Cr alloy contains more than 25% Mn, which suggests that Mn plays the role of a ferrite former. In Fe-15% Mn-Cr alloy, the δ phase is not observed in the range of Cr contents up to 12%, whereas it is markedly increased with the addition of 16% Cr. C, N and Ni are very helpful in forming the γ phase in these alloys as generally known in Fe-Cr-Ni alloys. The toughness evaluated by the Charpy impact test at 273 K and room temperature is very low in the 5% Mn alloy which consists of the α' and δ phases. It is, however, significantly improved by a small amount of the γ phase and increases with increase of γ phase stability. (author)

Synthesis and structural stability of Cr-doped Li2MnSiO4/C cathode materials by solid-state method

Science.gov (United States)

Cheng, Hong-Mei; Zhao, Shi-Xi; Wu, Xia; Zhao, Jian-Wei; Wei, Lei; Nan, Ce-Wen

2018-03-01

The crystal structure of the Li2MnSiO4 cathode material would collapse during the charge and discharge process because of that the Mn-O coordination polyhedron changed from [MnO4] into [MnO6] in the process of Mn+2 to Mn+4, but the Cr element could remain [CrO4] crystal ligand from Cr+2 to Cr+4, so Cr element substitution was used to improve the structural stability of the Li2MnSiO4 cathode material. In this work, Li2Mn1-xCrxSiO4/C nanocomposites were synthesized by solid-state method. XRD, SEM and TEM observations show that the as-prepared Li2Mn1-xCrxSiO4/C materials presents an orthorhombic crystal structure (S.G. Pmn21), the particle size of Li2Mn1-xCrxSiO4/C powder ranges from 50 to 100 nm. The XRD and XPS results indicate that Cr+2 is successfully doped into Li2MnSiO4 lattice and has well compatibility with Li2MnSiO4. The electrochemical results display that Li2Mn92.5%Cr7.5%SiO4/C exhibits significantly enhanced cycle stability and discharge capability. The initial discharge capacity of the Li2Mn92.5%Cr7.5%SiO4/C sample is 255 mAh g-1, and the discharge capacity was still about 60 mAh g-1 after 50 cycles. Furthermore, the XRD patterns, TEM images and Raman analysis reveal that the Cr doping enhances the structural stability of Li2Mn1-xCrxSiO4/C and improves the electrochemical activity of the cathode. Thus, the Li2Mn92.5%Cr7.5%SiO4/C have shown potential applications for lithium ion batteries.

Synthesis and magnetic properties of hexagonal Y(Mn,Cu)O{sub 3} multiferroic materials

Energy Technology Data Exchange (ETDEWEB)

Jeuvrey, L., E-mail: laurent.jeuvrey@univ-rennes1.fr [Sciences Chimiques de Rennes, UMR-CNRS 6226, Universite de Rennes 1, 35042 Rennes cedex (France); Pena, O. [Sciences Chimiques de Rennes, UMR-CNRS 6226, Universite de Rennes 1, 35042 Rennes cedex (France); Moure, A.; Moure, C. [Electroceramics Department, Instituto de Ceramica y Vidrio, CSIC, C/Kelsen 5, 28049, Madrid (Spain)

2012-03-15

Single-phase hexagonal-type solid solutions based on the multiferroic YMnO{sub 3} material were synthesized by a modified Pechini process. Copper doping at the B-site (YMn{sub 1-x}Cu{sub x}O{sub 3}; x<0.15) and self-doping at the A-site (Y{sub 1+y}MnO{sub 3}; y<0.10) successfully maintained the hexagonal structure. Self-doping was limited to y(Y)=2 at% and confirmed that excess yttrium avoids formation of ferromagnetic manganese oxide impurities but creates vacancies at the Mn site. Chemical substitution at the B-site inhibits the geometrical frustration of the Mn{sup 3+} two-dimensional lattice. The magnetic transition at T{sub N} decreases from 70 K down to 49 K, when x(Cu) goes from 0 to 15 at%. Weak ferromagnetic Mn{sup 3+}-Mn{sup 4+} interactions created by the substitution of Mn{sup 3+} by Cu{sup 2+}, are visible through the coercive field and spontaneous magnetization but do not modify the overall magnetic frustration. Presence of Mn{sup 3+}-Mn{sup 4+} pairs leads to an increase of the electrical conductivity due to thermally-activated small-polaron hopping mechanisms. Results show that local ferromagnetic interactions can coexist within the frustrated state in the hexagonal polar structure. - Highlights: Black-Right-Pointing-Pointer Hexagonal-type solid solutions of Y(Mn,Cu)O{sub 3} synthesized by Pechini process. Black-Right-Pointing-Pointer Chemical substitution at B site inhibits geometrical magnetic frustration. Black-Right-Pointing-Pointer Magnetic transition decreases with Cu-doping. Black-Right-Pointing-Pointer Local ferromagnetic Mn-Mn interactions coexist with the frustrated state.

Tissue distribution, subcellular localization and endocrine disruption patterns induced by Cr and Mn in the crab Ucides cordatus

International Nuclear Information System (INIS)

Correa, Jose Dias; Ramos da Silva, Miguel; Bastos da Silva, Antonio Carlos; Araujo de Lima, Silene Maria; Malm, Olaf; Allodi, Silvana

2005-01-01

The essential trace elements Cr and Mn are toxic at high concentrations and information about low concentration is insufficient in the literature. In polluted mangroves, the crab Ucides cordatus can represent a useful tool to assess information on the potential impact of trace elements like Cr and Mn on the environment, since this species is comestible and thus, commercially negotiated. Therefore, U. cordatus crabs were exposed in vivo to different concentrations of Cr and Mn solved in seawater and had their tissue distribution and subcellular deposits evaluated. The gill, hepatopancreas and muscle concentrations were determined by atomic absorption spectroscopy and the results showed that Cr and Mn presented the highest values in the gills rather than in the hepatopancreas and muscular tissue. Electron microscopy and analytical X-ray microanalysis revealed Cr precipitates on the gill surface, co-localized with epiphyte bacteria. In addition, since Cr and Mn did not equally accumulate in most of the tissues studied, glycemic rate of animals, which received injections of extracts of eyestalks of the contaminated crabs, were measured in order to evaluate whether the studied concentrations of Cr and Mn could produce any metabolic alteration. The results indicated that extracts of the eyestalks of crabs submitted to Cr and Mn salts and injected into normal crabs markedly influenced crustacean hyperglycemic hormone synthesis and/or release. The results are discussed with respect to sensitivity of the employed methods and the possible significance of the concentrations of Cr and Mn in the organisms

Equilibrium constant and nitrogen activity and the parameters of interaction eN(N), rN(N,Cr), rN(N,Mn) in high nitrogen steels of Fe-Cr-Mn-N type

International Nuclear Information System (INIS)

Svyazhin, A.G.; Siwka, J.; Rashev, T.

1999-01-01

In the paper a description of a thermodynamic of liquid solutions of Fe-Cr-Mn-N type with using a concept of parameters of an interaction has been presented. A temperature relationship of the equilibrium constant K N(Fe) and values of self interaction parameters e N (N) , r N (N,Cr) , r N (N,Mn) and t N (N,Cr,Cr) has been determined for mean values of temperatures of liquid metal equal 1990 K and 2090 K. By application of a theory of regular solutions those values were recalculated for a temperature 1873 K. (orig.)

Magnetotransport of CaCu3Mn4O12 complex perovskite derivatives

International Nuclear Information System (INIS)

Sanchez-Benitez, J.; Andres, A. de; Garcia-Hernandez, M.; Alonso, J.A.; Martinez-Lope, M.J.

2006-01-01

Neutron powder diffraction, magnetic and magnetotransport studies were carried out on new derivatives of the CaCu 3 Mn 4 O 12 (A'A 3 B 4 O 12 ) complex perovskite. The samples were prepared in polycrystalline form under moderate pressure conditions. Substitutions at A and A' sites of CaCu 3 Mn 4 O 12 , with only Mn 4+ and insulating behavior, imply electron doping that affects the magnetic and transport properties. X-ray Absorption Spectroscopy showed that Mn 3+ /Mn 4+ valence mixing occurs only at B site, progressively filling the e g band and providing the metallic character in these compounds, as we observe in most of these samples. A semiconducting behavior is observed in samples with 50% Mn 3+ at B site. This can be understood by the opening of a gap in the conduction band corresponding to the half filling of the e g states. This is the case of the tetravalent rare earth doped samples (Ce and Th at A' site) and of the appropriate A site doped Ca(CuMn 2 )Mn 4 O 12 sample. At the strongly distorted A positions, Mn 3+ , with localized e g electrons, act as magnetic impurities at very low temperatures (<40 K) giving rise to the observed upturn in the resistivity. The magnetic origin of this scattering is evidenced by its drastic reduction under a magnetic field

The Development of the Low-Cost Titanium Alloy Containing Cr and Mn Alloying Elements

Science.gov (United States)

Zhu, Kailiang; Gui, Na; Jiang, Tao; Zhu, Ming; Lu, Xionggang; Zhang, Jieyu; Li, Chonghe

2014-04-01

The α + β-type Ti-4.5Al-6.9Cr-2.3Mn alloy has been theoretically designed on the basis of assessment of the Ti-Al-Cr-Mn thermodynamic system and the relationship between the molybdenum equivalent and mechanical properties of titanium alloys. The alloy is successfully prepared by the split water-cooled copper crucible, and its microstructures and mechanical properties at room temperature are investigated using the OM, SEM, and the universal testing machine. The results show that the Ti-4.5Al-6.9Cr-2.3Mn alloy is an α + β-type alloy which is consistent with the expectation, and its fracture strength, yield strength, and elongation reach 1191.3, 928.4 MPa, and 10.7 pct, respectively. Although there is no strong segregation of alloying elements under the condition of as-cast, the segregation of Cr and Mn is obvious at the grain boundary after thermomechanical treatment.

Intermartensitic transitions in Ni-Mn-Fe-Cu-Ga Heusler alloys

International Nuclear Information System (INIS)

Khan, Mahmud; Gautam, Bhoj; Pathak, Arjun; Dubenko, Igor; Stadler, Shane; Ali, Naushad

2008-01-01

A series of Fe doped Ni 2 Mn 0.75-x Fe x Cu 0.25 Ga Heusler alloys have been investigated by means of x-ray diffraction, magnetizations, thermal expansion, and electrical resistivity measurements. In Ni 2 Mn 0.75 Cu 0.25 Ga, martensitic and ferromagnetic transitions occur at the same temperature. Partial substitution of Mn by Fe results in a decrease of the martensitic transition temperature, T M , and an increase of the ferromagnetic transition temperature, T C , resulting in separation of the two transitions. In addition to the martensitic transition, complete thermoelastic intermartensitic transformations have been observed in the Fe doped Ni 2 Mn 0.75-x Fe x Cu 0.25 Ga samples with x>0.04. An unusual transition is observed in the alloy with x = 0.04. The magnetization curve as a function of increasing temperature shows only one first-order transition in the temperature range 5-400 K, which is identified as a typical coupled magnetostructural martensitic transformation. The magnetization curve as a function of decreasing temperature shows three different transitions, which are characterized as the ferromagnetic transition, the martensitic transition and the intermartensitic transition.

Electronic configuration of the c(2 x 2)MnCu two-dimensional alloy in layered structures supported on Cu(100)

International Nuclear Information System (INIS)

Gallego, S; Munoz, M C; Huttel, Y; Avila, J; Asensio, M C

2003-01-01

The c(2 x 2)MnCu surface alloy on Cu(100) can be considered as a purely two-dimensional magnetic system where the Mn atoms exhibit a large corrugation closely related to their high spin moment. In this paper we investigate the influence of the atomic environment on the electronic and magnetic properties of the two-dimensional alloyed layer, extending our study to the less known multilayered system made of MnCu two-dimensional alloy layers embedded in a Cu crystal. The analysis is based on angle-resolved photoelectron spectroscopy measurements and calculations using the Green function matching method, which allows us to treat exactly the projection of the three-dimensional lattice on the c(2 x 2) plane. A complete study of the valence band is performed along the two-dimensional Brillouin zone in a wide energy range. We show that the presence of Mn results in an important redistribution of the spin-polarized electronic states of the neighbouring Cu atoms. This redistribution is not accompanied by a net charge transfer between different atoms, and also the spin moment of Cu remains small. Most of the new features induced by Mn in the surface alloy are also present in the multilayered system, evidencing that they are specific to the two-dimensional alloyed layer and not surface effects

Paduan Ni-Cu-Mn Sebagai Logam Alternatif Kedokteran Gigi: Efek Perendaman dalam Larutan 0,1% Sodium Sulfida

Directory of Open Access Journals (Sweden)

Bambang Irawan

2015-09-01

Full Text Available In this study, the ternary base alloys of nickel-copper-manganese (Ni-Cu-Mn alloys are prepared and these ternary alloys systems, which were constituted from higher nickel and lower copper contents than copper-base alloy ones, were evaluated by a tarnish test. Tarnish tests conducted in a 0,1% sodium sulphide solution (pH=12 at 37◦C. All test specimens were case into square paddles of 15 mm x 20 mm x 2,5 mm using the lost-wax technique with a phosphate-bonded investment. The surface of the specimens were then prepared with abrasion papers down to a 600 grit finish. Tarnish attack was quantitatively evaluated by Fibre colorimetry. The results of tarnish test showed that ternary nickel-copper-manganese alloys, such as 40Ni-30Cu-30Mn and 50Ni-30Cu-20Mn, have superior tarnishment resistance than other alloys, e.g. 20Ni-40Cu-40Mn, 30Ni-30Cu-40Mn and 30Ni-40Cu-30Mn. It was also found that 40Ni-30Cu-30Mn and 50Ni-30Cu-20Mn alloys have lower values of colour change vector than the other alloys given above.

53Cr NMR study of CuCrO2 multiferroic

Science.gov (United States)

Smol'nikov, A. G.; Ogloblichev, V. V.; Verkhovskii, S. V.; Mikhalev, K. N.; Yakubovskii, A. Yu.; Kumagai, K.; Furukawa, Y.; Sadykov, A. F.; Piskunov, Yu. V.; Gerashchenko, A. P.; Barilo, S. N.; Shiryaev, S. V.

2015-11-01

The magnetically ordered phase of the CuCrO2 single crystal has been studied by the nuclear magnetic resonance (NMR) method on 53Cr nuclei in the absence of an external magnetic field. The 53Cr NMR spectrum is observed in the frequency range νres = 61-66 MHz. The shape of the spectrum depends on the delay tdel between pulses in the pulse sequence τπ/2- t del-τπ- t del-echo. The spin-spin and spin-lattice relaxation times have been measured. Components of the electric field gradient, hyperfine fields, and the magnetic moment on chromium atoms have been estimated.

Effect of Manganese on Microstructures and Solidification Modes of Cast Fe-Mn-Si-Cr-Ni Shape Memory Alloys

Science.gov (United States)

Peng, Huabei; Wen, Yuhua; Du, Yangyang; Yu, Qinxu; Yang, Qin

2013-10-01

We investigated microstructures and solidification modes of cast Fe-(13-27)Mn-5.5Si-8.5Cr-5Ni shape memory alloys to clarify whether Mn was an austenite former during solidification. Furthermore, we examined whether the Creq/Nieq equations (Delong, Hull, Hammer and WRC-1992 equations) and Thermo-Calc software® together with database TCFE6 were valid to predict the solidification modes of cast Fe-(13-27)Mn-5.5Si-8.5Cr-5Ni shape memory alloys. The results have shown that the solidification modes of Fe-(13-27)Mn-5.5Si-8.5Cr-5Ni alloys changed from the F mode to the FA mode with increasing the Mn concentration. Mn is an austenite former during the solidification for the cast Fe-Mn-Si-Cr-Ni shape memory alloys. The Delong, Hull, Hammer, and WRC-1992 equations as well as Thermo-Calc software® together with database TCFE6 are invalid to predict the solidification modes of cast Fe-(13-27)Mn-5.5Si-8.5Cr-5Ni SMAs. To predict the solidification modes of cast Fe-Mn-Si-Cr-Ni alloys, a new Creq/Nieq equation should be developed or the thermodynamic database of Thermo-Calc software® should be corrected.

Magnetic properties of CaCu{sub 5}-type RNi{sub 3}TSi (R=Gd and Tb, T=Mn, Fe, Co and Cu) compounds

Energy Technology Data Exchange (ETDEWEB)

Morozkin, A.V., E-mail: morozkin@tech.chem.msu.ru [Department of Chemistry, Moscow State University, Leninskie Gory, House 1, Building 3, GSP-2, Moscow 119992 (Russian Federation); Knotko, A.V. [Department of Chemistry, Moscow State University, Leninskie Gory, House 1, Building 3, GSP-2, Moscow 119992 (Russian Federation); Yapaskurt, V.O. [Department of Petrology, Geological Faculty, Moscow State University, Leninskie Gory, Moscow 119992 (Russian Federation); Yao, Jinlei [Research Center for Solid State Physics and Materials, School of Mathematics and Physics, Suzhou University of Science and Technology, Suzhou 215009 (China); Yuan, Fang; Mozharivskyj, Y. [Department of Chemistry and Chemical Biology, McMaster University, 1280 Main Street West, Hamilton, Ontario, Canada L8S 4M1 (Canada); Nirmala, R. [Indian Institute of Technology Madras, Chennai 600036 (India); Quezado, S.; Malik, S.K. [Departamento de Física Teórica e Experimental, Universidade Federal do Rio Grande do Norte, Natal 59082-970 (Brazil)

2015-12-15

Magnetic properties and magnetocaloric effect of CaCu{sub 5}-type RNi{sub 3}TSi (R=Gd and Tb, T=Mn, Fe, Co and Cu) compounds have been investigated. Magnetic measurements of RNi{sub 3}TSi display the increasing of Curie temperature and the decreasing of magnetocaloric effect and saturated magnetic moment in the row of ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’. In contrast to GdNi{sub 3}{Mn, Fe, Co}Si, TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. The coercive field increases from TbNi{sub 4}Si (~0.5 kOe) to TbNi{sub 3}CoSi (4 kOe), TbNi{sub 3}MnSi (13 kOe) and TbNi{sub 3}FeSi (16 kOe) in field of 50 kOe at 5 K, whereas TbNi{sub 3}CuSi exhibits a negligible coercive field. - Graphical abstract: Magnetic measurements of RNi{sub 3}TSi show the increasing of Curie temperature and the decreasing of magnetocaloric effect and saturated magnetic moment in the row of 'RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi'. In contrast to GdNi{sub 3}{Mn, Fe, Co}Si, TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. The coercive field increases from TbNi{sub 4}Si (~0.5 kOe) to TbNi{sub 3}CoSi (4 kOe), TbNi{sub 3}MnSi (13 kOe) and TbNi{sub 3}FeSi (16 kOe) in field of 50 kOe at 5 K, whereas TbNi{sub 3}CuSi exhibits a negligible coercive field. - Highlights: • CaCu{sub 5}-type RNi{sub 3}TSi show ferromagnetic ordering (R=Gd, Tb, T=Mn–Co, Cu). • Curie point increases in ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’ row. • MCE decreases in ‘RNi{sub 3}CuSi–RNi{sub 3}NiSi–RNi{sub 3}CoSi–RNi{sub 3}MnSi–RNi{sub 3}FeSi’ row. • TbNi{sub 3}{Mn, Fe, Co}Si exhibit significant magnetic hysteresis. • The coercive field of TbNi{sub 3}MnSi and TbNi{sub 3}FeSi reach 13 kOe and 16 kOe at 5 K.

Microstructures and Properties Evolution of Al-Cu-Mn Alloy with Addition of Vanadium

Directory of Open Access Journals (Sweden)

Fansheng Meng

2016-12-01

Full Text Available The effect of the vanadium addition on the microstructure, the precipitation behavior, and the mechanical properties of the Al-5.0Cu-0.4Mn alloy has been studied. The as-cast Al-5.0Cu-0.4Mn alloy was produced by squeeze casting and the heat treatment was carried out following the standard T6 treatment. It is shown that, with the addition of V, grain refinement of aluminum occurred. During heat treatment, the addition of V accelerates the precipitation kinetics of θ′ (Al2Cu phase along the grain boundaries, and promotes the growth rate of the θ′ in the α(Al matrix. Meanwhile, the addition of V retards the precipitation of T (Al20Cu2Mn3 phase. The tensile strength of the Al-5.0Cu-0.4Mn alloy increases with the increase of V content, which can be explained by combined effects of the solid solution strengthening and precipitate strengthening. However, excessively high V addition deteriorates the mechanical properties by forming brittle coarse intermetallic phases.

Effect of HIP temperature on microstructure and low cycle fatigue strength of CuCrZr alloy

Science.gov (United States)

Nishi, Hiroshi; Enoeda, Mikio

2011-10-01

In order to investigate the effect of the HIP cycle temperatures on the metallurgic degradation and the mechanical properties of CuCrZr alloy, assessments of the microstructure, tensile test, Charpy impact test and low cycle fatigue test are performed for various heat treated CuCrZr alloys, which were solution-annealed followed by water-quenched and aged state of CuCrZr with simulated HIP cycle at temperatures of 980 and 1045 °C. Grain growth occurred on 1045 °C HIP CuCrZr, though slightly on 980 °C HIP CuCrZr. Metallurgic degradation such as voids was not found by optical and SEM observations. There were coarse precipitates in all the CuCrZr and the precipitates did not easily dissolve at 980 °C. The low cycle fatigue strength of 1045 °C HIP CuCrZr was lower than that of other CuCrZr because of the metallurgic degradation caused by the heat cycle, while that of other CuCrZr was corresponding to the best fit curve of ITER MPH.

Effect of HIP temperature on microstructure and low cycle fatigue strength of CuCrZr alloy

Energy Technology Data Exchange (ETDEWEB)

Nishi, Hiroshi, E-mail: nishi.hiroshi88@jaea.go.jp [Japan Atomic Energy Agency, Naka-shi, Ibaraki-ken 311-0193 (Japan); Enoeda, Mikio [Japan Atomic Energy Agency, Naka-shi, Ibaraki-ken 311-0193 (Japan)

2011-10-01

In order to investigate the effect of the HIP cycle temperatures on the metallurgic degradation and the mechanical properties of CuCrZr alloy, assessments of the microstructure, tensile test, Charpy impact test and low cycle fatigue test are performed for various heat treated CuCrZr alloys, which were solution-annealed followed by water-quenched and aged state of CuCrZr with simulated HIP cycle at temperatures of 980 and 1045 deg. C. Grain growth occurred on 1045 deg. C HIP CuCrZr, though slightly on 980 deg. C HIP CuCrZr. Metallurgic degradation such as voids was not found by optical and SEM observations. There were coarse precipitates in all the CuCrZr and the precipitates did not easily dissolve at 980 deg. C. The low cycle fatigue strength of 1045 deg. C HIP CuCrZr was lower than that of other CuCrZr because of the metallurgic degradation caused by the heat cycle, while that of other CuCrZr was corresponding to the best fit curve of ITER MPH.

Effect of HIP temperature on microstructure and low cycle fatigue strength of CuCrZr alloy

International Nuclear Information System (INIS)

Nishi, Hiroshi; Enoeda, Mikio

2011-01-01

In order to investigate the effect of the HIP cycle temperatures on the metallurgic degradation and the mechanical properties of CuCrZr alloy, assessments of the microstructure, tensile test, Charpy impact test and low cycle fatigue test are performed for various heat treated CuCrZr alloys, which were solution-annealed followed by water-quenched and aged state of CuCrZr with simulated HIP cycle at temperatures of 980 and 1045 deg. C. Grain growth occurred on 1045 deg. C HIP CuCrZr, though slightly on 980 deg. C HIP CuCrZr. Metallurgic degradation such as voids was not found by optical and SEM observations. There were coarse precipitates in all the CuCrZr and the precipitates did not easily dissolve at 980 deg. C. The low cycle fatigue strength of 1045 deg. C HIP CuCrZr was lower than that of other CuCrZr because of the metallurgic degradation caused by the heat cycle, while that of other CuCrZr was corresponding to the best fit curve of ITER MPH.

HIP joining of Be/CuCrZr for fabrication of ITER first wall

International Nuclear Information System (INIS)

Park, Jeong-Yong; Choi, Byung-Kwon; Park, Sang-Yoon; Kim, Hyun-Gil; Kim, Jun-Hwan; Hong, Bong Guen; Jeong, Yong Hwan

2007-01-01

The effects of different interlayer types and the temperature have been investigated in order to optimize the HIP joining conditions of Be to CuCrZr. Ti/Cu and Cr/Cu interlayers were coated onto a Be surface before a HIP joining. HIP temperature was changed from 580 to 620 deg. C. No intermetallic compounds or defects were formed at the interface of the joint specimens. The joining strength measured by the four-point bend test and the shear test was higher in the joint specimen with Ti/Cu interlayers when compared to that with Cr/Cu interalyers and it was increased with an increase of the HIP temperature from 580 to 620 deg. C. The yield strength of the aged CuCrZr was higher than 150 MPa at 250 deg. C up to an aging temperature of 620 deg. C after a water quenching. It is therefore suggested that the HIP temperature of the Be/CuCrZr joint could be increased to 620 deg. C based on the results obtained from this study

Characterization of transparent superconductivity Fe-doped CuCrO{sub 2} delafossite oxide

Energy Technology Data Exchange (ETDEWEB)

Taddee, Chutirat [Materials Science and Nanotechnology Program, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Kamwanna, Teerasak, E-mail: teekam@kku.ac.th [Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Nanotec-KKU Center of Excellence on Advanced Nanomaterials for Energy Production and Storage, Khon Kaen 40002 (Thailand); Integrated Nanotechnology Research Center (INRC), Khon Kaen University, Khon Kaen 40002 (Thailand); Amornkitbamrung, Vittaya [Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen 40002 (Thailand); Nanotec-KKU Center of Excellence on Advanced Nanomaterials for Energy Production and Storage, Khon Kaen 40002 (Thailand); Integrated Nanotechnology Research Center (INRC), Khon Kaen University, Khon Kaen 40002 (Thailand)

2016-09-01

Graphical abstract: - Highlights: • Effect of Fe substitution on the physical properties in CuCrO{sub 2} is studied. • The substitution of Cr{sup 3+} by Fe{sup 3+} produces a mixed effect on the magnetic properties. • CuCr{sub 1−x}Fe{sub x}O{sub 2} delafossite oxides show transparent superconductivity. - Abstract: Delafossite CuCr{sub 1−x}Fe{sub x}O{sub 2} (0.0 ≤ x ≤ 0.15) semiconductors were synthesized using a self-combustion urea nitrate process. The effects of Fe concentration on its microstructural, optical, magnetic, and electrical properties were investigated. X-ray diffraction (XRD) analysis results revealed the delafossite structure in all the samples. The lattice spacing of CuCr{sub 1−x}Fe{sub x}O{sub 2} slightly increased with increasing substitution of Fe at the Cr sites. The optical properties measured at room temperature using UV–visible spectroscopy showed a weak absorbability in the visible light and near IR regions. The corresponding direct optical band gap was about 3.61 eV, exhibiting transparency in the visible region. The magnetic hysteresis loop measurements showed that the Fe-doped CuCrO{sub 2} samples exhibited ferromagnetic behavior at room temperature. This indicated that the substitution of Fe{sup 3+} for Cr{sup 3+} produced a mixed effect on the magnetic properties of CuCrO{sub 2} delafossite oxide. The temperature dependent resistivity measurements clearly revealed the presence of superconductivity in the CuCr{sub 1−x}Fe{sub x}O{sub 2} with a superconducting transition up to 118 K.

Axial strain localization of CuCrZr tubes during manufacturing of ITER-like mono-block W/Cu components using HIP

International Nuclear Information System (INIS)

Zhao, S.X.; Peng, L.J.; Li, Q.; Wang, W.J.; Wei, R.; Qin, S.G.; Shi, Y.L.; Chang, S.P.; Xu, Y.; Liu, G.H.; Wang, T.J.; Luo, G.-N.

2014-01-01

Highlights: • Axial cracking and denting of CuCrZr tubes were observed. • Annealing the as-received tubes can alleviate cracking. • Denting results in the formation bonding flaws at the Cu/CuCrZr interfaces. - Abstract: Two forms of axial strain localization of CuCrZr tubes, i.e., cracking and denting, were observed during the manufacturing of ITER-like mono-block W/Cu components for EAST employing hot isostatic pressing (HIP). Microscopic investigations indicate that the occurrence of axial strain localization correlates to the heavily deformed Cu grains and elongated Cr-rich precipitates as well as highly anisotropic microstructures, which impair the circumferential ductility. Annealing the as-received tubes at 600 °C alleviates cracking due to partial recrystallization of Cu grains. However, the annealed tubes are still sensitive to wall thinning (caused by non-uniform polishing or tube bending), which results in denting. Denting may cause bonding flaws at CuCrZr/Cu interfaces and the underlying mechanisms are discussed. To some extent, denting seems do not affect the high heat flux performance of components. In this paper, we demonstrate that testing only the axial mechanical properties is not enough for manufacturers who use HIP or hot radial pressing technologies, especially for those anisotropic tubes

Synthesis and characterization of La(Cr,Fe,Mn)O{sub 3} nanoparticles obtained by co-precipitation method

Energy Technology Data Exchange (ETDEWEB)

Fabian, F.A., E-mail: fernandafabianro@gmail.com [Universidade Federal de Sergipe, Campus Prof. Aluísio Campos, Departamento de Física, 49100-000 São Cristóvão, SE (Brazil); Pedra, P.P.; Filho, J.L.S. [Universidade Federal de Sergipe, Campus Prof. Aluísio Campos, Departamento de Física, 49100-000 São Cristóvão, SE (Brazil); Duque, J.G.S.; Meneses, C.T. [Universidade Federal de Sergipe, Campus Prof. Alberto Carvalho, Departamento de Física, 49500-000 Itabaiana, SE (Brazil)

2015-04-01

Magnetic and structural properties have been investigated in La(Cr,Fe,Mn)O{sub 3} nanoparticles obtained by co-precipitation method. The X-ray diffraction measurements allied to Rietveld method confirm the formation of LaCrO{sub 3}, LaFeO{sub 3} and LaMnO{sub 3} nanoparticles with crystal structure orthorhombic (Pbnm), orthorhombic (Pnma) and rhombohedral (R-3c), respectively. We also verified an decreasing in the average crystallite size from 73 to 26 nm, depending of the transition metal. The magnetic measurements reveal an antiferromagnetic behavior for the LaCrO{sub 3} sample with T{sub N}~289 K, and a weak ferromagnetic ordering for the LaMnO{sub 3} sample with T{sub c}~200 K. - Highlights: • La(Cr,Fe,Mn)O{sub 3} nanoparticles were synthesized by coprecipitation method. • XRD results confirm the formation single phase in the compounds studied. • Magnetic property in the La(Fe,Cr,Mn)O{sub 3} nanoparticles dependent on the TM. • La(Cr,Fe)O{sub 3} nanoparticles presented behavior antiferromagnetic and LaMnO{sub 3} ferromagnetic.

Interdiffusion coefficients and atomic mobilities in fcc Cu-Fe-Mn alloys

Directory of Open Access Journals (Sweden)

Li J.

2014-01-01

Full Text Available In the present work, the interdiffusion coefficients in fcc Cu-Fe-Mn alloys were experimentally determined via a combination of solid/solid diffusion couples, electron probe microanalysis (EPMA technique and Matano-Kirkaldy method. Based on the reliable thermodynamic description of fcc phase in the Cu-Fe-Mn system available in the literature as well as the ternary diffusion coefficients measured in the present work, the atomic mobilities in fcc Cu-Fe-Mn alloys were assessed by utilizing the DICTRA (Diffusion Controlled TRAnsformation software package. The calculated interdiffusion coefficients based on the assessed atomic mobilities agree well with most of the experimental data. The comprehensive comparison between various model-predicted diffusion properties and the measured data, including the concentration penetration profiles, interdiffusion flux profile, and diffusion paths, further verify the reliability of the presently obtained atomic mobilities.

Spectro-photometric determinations of Mn, Fe and Cu in aluminum master alloys

Science.gov (United States)

Rehan; Naveed, A.; Shan, A.; Afzal, M.; Saleem, J.; Noshad, M. A.

2016-08-01

Highly reliable, fast and cost effective Spectro-photometric methods have been developed for the determination of Mn, Fe & Cu in aluminum master alloys, based on the development of calibration curves being prepared via laboratory standards. The calibration curves are designed so as to induce maximum sensitivity and minimum instrumental error (Mn 1mg/100ml-2mg/100ml, Fe 0.01mg/100ml-0.2mg/100ml and Cu 2mg/100ml-10mg/ 100ml). The developed Spectro-photometric methods produce accurate results while analyzing Mn, Fe and Cu in certified reference materials. Particularly, these methods are suitable for all types of Al-Mn, Al-Fe and Al-Cu master alloys (5%, 10%, 50% etc. master alloys).Moreover, the sampling practices suggested herein include a reasonable amount of analytical sample, which truly represent the whole lot of a particular master alloy. Successive dilution technique was utilized to meet the calibration curve range. Furthermore, the workout methods were also found suitable for the analysis of said elements in ordinary aluminum alloys. However, it was observed that Cush owed a considerable interference with Fe, the later one may not be accurately measured in the presence of Cu greater than 0.01 %.

Effect of tellurium on machinability and mechanical property of CuAlMnZn shape memory alloy

International Nuclear Information System (INIS)

Liu Na; Li Zhou; Xu Genying; Feng Ze; Gong Shu; Zhu Lilong; Liang Shuquan

2011-01-01

Highlights: → A novel free-machining Cu-7.5Al-9.7Mn-3.4Zn-0.3Te (wt.%) shape memory alloy has been developed. → The size of dispersed particles with richer Te is 2-5 μm. → The CuAlMnZnTe alloy has good machinability which approached that of BZn15-24-1.5 due to the addition of Te. → Its shape memory property keeps the same as that of CuAlMnZn alloy with free Te. → The CuAlMnZn shape memory alloy with and without Te both have good ductile as annealed at 700 deg. C for 15 min. - Abstract: The microstructure transition, shape memory effect, machinability and mechanical property of the CuAlMnZn alloy with and without Te have been studied using X-ray diffraction analysis, chips observation and scanning electron microscopy (SEM), tensile strength test and differential scanning calorimeter (DSC), and semi-quantitative shape memory effect (SME) test. The particles with richer Te dispersedly distributed in grain interior and boundary with size of 2-5 μm. After the addition of Te, the CuAlMnZnTe alloy machinability has been effectively increased to approach that of BZn15-24-1.5 and its shape memory property remains the same as the one of CuAlMnZn alloy. The CuAlMnZn shape memory alloys with and without Te both have good ductility as annealed at 700 deg. C for 15 min.

Accumulation of Heavy Metals in Ricinus communis L. from Mn Contaminated Area

Directory of Open Access Journals (Sweden)

YI Xin-yu

2014-02-01

Full Text Available Xiangbi No. 1 and Zibi No. 7 were planted in the Mn contaminated soils to explore its potential of ecological remediation and ener-gy utilization in the areas of Mn contaminated site. The major nutrient elements and the concentrations of heavy metals(Mn, Pb, Zn, Cu and Cr in different parts(root, branch and leaf and topsoil samples were detected after entering into the period of reproductive growth.The results showed that the average content of Mn was as high as 7 884.96 mg·kg-1,which exceeded 6.5 times of national soil environmental quality standard(level 2.The mean level of Mn in tissues of Xiangbi No. 1 was found to be in the sequence of root>leaf>branch,whereas,the mean level of Mn in different parts of Zibi No. 7 was found to be in the order of leaf>fruit>branchroot respectively. The average concentration of Mn in the leaf reached the peak value(765.43 mg·kg-1,which was higher than Xiangbi No.1 about 79.53%.The leaf/root ratios of Pb, Cu, Cr contents in Zibi No. 7 were higher than those of Xiangbi No. 1 samples.The accumulation and translocation in plants was affect-ed by different heavy metal elements in soils.The results demonstrated that Zibi No. 7 had a better uptake and translocation capacity of Mn,Pb,Cu and Cr, meanwhile,plants of two species had differences in accumulation and translocation ability and were proved to possess good Mn-tolerance ability for remediation of heavy metal contaminated soils.

Synthetic, structural, spectroscopic and theoretical study of a Mn(III)-Cu(II) dimer containing a Jahn-Teller compressed Mn ion

DEFF Research Database (Denmark)

Berg, Nelly; Hooper, Thomas N.; Liu, Junjie

2013-01-01

The heterobimetallic complex [Cu(II)Mn(III)(L)(2)(py)(4)](ClO(4))·EtOH (1) built using the pro-ligand 2,2'-biphenol (LH(2)), contains a rare example of a Jahn-Teller compressed Mn(III) centre. Dc magnetic susceptibility measurements on 1 reveal a strong antiferromagnetic exchange between the Cu...

Cumulation of Cu, Zn, Cd, and Mn in Plants of Gardno Lake

Directory of Open Access Journals (Sweden)

Trojanowski J.

2013-04-01

Full Text Available In the present paper there have been shown the results of research on yhe content of Zn, Cd, Cu, Mn and Pb in chosen plants of Lake Gardno.The biggest concentration of those metals has been observed in Potamogton natans and Elodea canadensis, on average Zn – 34.9, Pb -2.77, Cd – 0.62, Cu – 3.24 and Mn – 257.4 μg g-1. It has been found that the over-ground parts of the plants under analysis cumulate several times less of heavy metals than their roots. The determined enrichment factors enabled the researchers to state that Cu in the examined plants is of natural origin while Mn, Cd and Zn – of anthropogenic origin.

Anti-wetting Cu/Cr coating with micro-posts array structure fabricated by electrochemical approaches

International Nuclear Information System (INIS)

Zhou, Yufeng; Hang, Tao; Li, Feng; Li, Ming

2013-01-01

Microposts structured Cu/Cr multilayer coating was prepared by a simple two-step approach combining electroless and electro deposition. Surface morphologies of the as-prepared Cu/Cr multilayer coating characterized by field emission scanning electron microscopy show that this multilayer coating exhibits micro-posts arrayed structure with a layer of Cr uniformly covering the circular conical surface of Cu micro-cones array. The wettability test shows that the contact angle of Cu/Cr multilayer surface with water drop can be greater than 140° by optimizing the electrodeposition time of Cr. The mechanism of hydrophobicity of both the micro-cones arrayed and micro-posts arrayed structures was briefly discussed by comparing two different wetting modes. Due to its good anti-wetting property and unique structure, the micro-posts arrayed Cu/Cr multilayer coating is expected for extensive practical applications.

Mn3O4 precipitates in Ag and Cu studied with HRTEM : orientation relations and tetragonal twinning

NARCIS (Netherlands)

Kooi, B.J.; de Hosson, J.T.M.; Sarton, LAJ; Zeedijk, HB

1997-01-01

Internal oxidation of Ag-3at.%Mn resulted in Mn3O4 precipitates and of Cu-1at.%Mn gave rise to MnO and a minor amount of Mn3O4 precipitates. In Cu Mn3O4 transformed out of MnO, whereas in Ag Mn3O4 developed directly. Predominantly, precipitates with parallel topotaxy and an octahedron shape due to 8

Crystal structure and magnetic properties of the Cr-doped spiral antiferromagnet BiMnFe{sub 2}O{sub 6}

Energy Technology Data Exchange (ETDEWEB)

Batuk, Dmitry, E-mail: Dmitry.batuk@ua.ac.be [Electron Microscopy for Materials Research (EMAT), University of Antwerp, Groenenborgerlaan 171, B-2020, Antwerp (Belgium); De Dobbelaere, Christopher [Inorganic and Physical Chemistry Group, Hasselt University, Institute for Materials Research, Agoralaan Building D, B-3590, Diepenbeek (Belgium); Tsirlin, Alexander A. [National Institute of Chemical Physics and Biophysics, 12618, Tallinn (Estonia); Abakumov, Artem M. [Electron Microscopy for Materials Research (EMAT), University of Antwerp, Groenenborgerlaan 171, B-2020, Antwerp (Belgium); Hardy, An; Van Bael, Marlies K. [Inorganic and Physical Chemistry Group, Hasselt University, Institute for Materials Research, Agoralaan Building D, B-3590, Diepenbeek (Belgium); IMEC vzw, Division IMOMEC, Agoralaan Building D, B-3590, Diepenbeek (Belgium); Greenblatt, Martha [Department of Chemistry and Chemical Biology, Rutgers, State University of New Jersey, 610 Taylor Road, Piscataway, New Jersey, 08854-8087 (United States); Hadermann, Joke [Electron Microscopy for Materials Research (EMAT), University of Antwerp, Groenenborgerlaan 171, B-2020, Antwerp (Belgium)

2013-09-01

Graphical abstract: - Highlights: • The substitution of Cr for Mn in BiMnFe{sub 2}O{sub 6} is possible by the solution–gel method. • The BiCr{sub x}Mn{sub 1−x}Fe{sub 2}O{sub 6} solid solution is obtained for the x values up to 0.3. • Increasing Cr content lowers the temperature of the antiferromagnetic ordering. - Abstract: We report the Cr{sup 3+} for Mn{sup 3+} substitution in the BiMnFe{sub 2}O{sub 6} structure. The BiCr{sub x}Mn{sub 1−x}Fe{sub 2}O{sub 6} solid solution is obtained by the solution–gel synthesis technique for the x values up to 0.3. The crystal structure investigation using a combination of X-ray powder diffraction and transmission electron microscopy demonstrates that the compounds retain the parent BiMnFe{sub 2}O{sub 6} structure (for x = 0.3, a = 5.02010(6)Å, b = 7.06594(7)Å, c = 12.6174(1)Å, S.G. Pbcm, R{sub I} = 0.036, R{sub P} = 0.011) with only a slight decrease in the cell parameters associated with the Cr{sup 3+} for Mn{sup 3+} substitution. Magnetic susceptibility measurements suggest strong similarities in the magnetic behavior of BiCr{sub x}Mn{sub 1−x}Fe{sub 2}O{sub 6} (x = 0.2; 0.3) and parent BiMnFe{sub 2}O{sub 6}. Only T{sub N} slightly decreases upon Cr doping that indicates a very subtle influence of Cr{sup 3+} cations on the magnetic properties at the available substitution rates.

Effect of alloying elements on σ phase formation in Fe-Cr-Mn alloys

International Nuclear Information System (INIS)

Okazaki, Yoshimitsu; Miyahara, Kazuya; Hosoi, Yuzo; Tanino, Mitsuru; Komatsu, Hazime.

1989-01-01

Alloys of Fe-(8∼12%) Cr-(5∼30%) Mn were solution-treated at 1373 K for 3.6 ks, followed by cold-working of 50% reduction. Both solution-treated and 50% cold-worked materials were aged in the temperature range from 773 to 973 K for 3.6 x 10 3 ks. The identification of σ phase formation was made by using X-ray diffraction from the electrolytically extracted residues of the aged specimens. The region of σ phase formation determined by the present work is wider than that on the phase diagram already reported. It is to be noted that Mn promotes markedly the σ phase formation, and that three different types of σ phase formation are observed depending on Mn content: α→γ + α→γ + α + σ in 10% Mn, α→γ + σ in 15 to 20% Mn alloys, α→χ(Chi) →χ + σ + γ in 25 to 30% Mn alloys. An average electron concentration (e/a) in the σ phase was estimated by quantitative analysis of alloying elements using EPMA. The e/a value in the σ phase formed in Fe-(12∼16%) Cr-Mn alloys aged at 873 K for 3.6 x 10 3 ks is about 7.3, which is independent of Mn content. In order to prevent σ phase formation in Fe-12% Cr-15% Mn alloy, the value of Ni * eq of 11 (Ni * eq = Ni + 30(C) + 25(N)) is required. (author)

Electrodialytic Remediation of Soil Slurry-Removal of Cu, Cr, and As

DEFF Research Database (Denmark)

Ottosen, Lisbeth M.; Jensen, Pernille Erland; Hansen, Henrik K.

2009-01-01

Severe soil contamination is often found at old wood preservation sites and a common combination of pollutants is Cu, Cr, and As. In the present work it is tested if simultaneous removal of Cu, Cr, and As can be obtained in an electrodialytic cell where the polluted soil is remediated as a stirred...... experiments; an experiment where the soil was suspended in distilled water and the remediation lasted 3 weeks with 2.5 mA and an experiment with acidification of the soil suspension with HNO3 to pH about 1.0 (2 weeks and 5 mA). The best separation of pollutants and soil was obtained in the experiment...... with suspension in distilled water. Based on soil concentrations, good Cu removal (95%) was obtained in both experiments. Removal of Cr was most efficient from the acidified soil suspension (74%). Both Cu and Cr concentrations were below the limiting values after the remediation. The As concentration, however...

Electroless deposition of NiCrB diffusion barrier layer film for ULSI-Cu metallization

Energy Technology Data Exchange (ETDEWEB)

Wang, Yuechun [School of Materials Science and Engineering, Yunnan University, Kunming (China); Chen, Xiuhua, E-mail: chenxh@ynu.edu.cn [School of Materials Science and Engineering, Yunnan University, Kunming (China); Ma, Wenhui [National Engineering Laboratory of Vacuum Metallurgy, Kunming University of Science and Technology, Kunming (China); Shang, Yudong; Lei, Zhengtao; Xiang, Fuwei [School of Materials Science and Engineering, Yunnan University, Kunming (China)

2017-02-28

Highlights: • In this paper, the electroless deposited NiCrB thin film was mainly in the form of NiB, CrB{sub 2} compounds and elementary Ni. • The sheet resistance of NiCrB thin film was 3.043 Ω/□, it is smaller than that of the widely used Ta, TaN and TiN diffusion barrier layers. • Annealing experiments showed that the failure temperature of NiCrB thin film regarding Cu diffusion was 900 °C. • NiCrB barrier layer crystallized after 900 °C annealing, Cu grains arrived at Si-substrate through grain boundaries, resulting in the formation of Cu{sub 3}Si. • Eelectroless deposited NiCrB film also had good oxidation resistance, it is expected to become an anti-oxidant layer of copper interconnection. - Abstract: NiCrB films were deposited on Si substrates using electroless deposition as a diffusion barrier layer for Cu interconnections. Samples of the prepared NiCrB/SiO{sub 2}/Si and NiCrB/Cu/NiCrB/SiO{sub 2}/Si were annealed at temperatures ranging from 500 °C to 900 °C. The reaction mechanism of the electroless deposition of the NiCrB film, the failure temperature and the failure mechanism of the NiCrB diffusion barrier layer were investigated. The prepared samples were subjected to XRD, XPS, FPP and AFM to determine the phases, composition, sheet resistance and surface morphology of samples before and after annealing. The results of these analyses indicated that the failure temperature of the NiCrB barrier film was 900 °C and the failure mechanism led to crystallization and grain growth of the NiCrB barrier layer after high temperature annealing. It was found that this process caused Cu grains to reach Si substrate through the grain boundaries, and then the reaction between Cu and Si resulted in the formation of highly resistive Cu{sub 3}Si.

Influence of manganese, carbon and nitrogen on high-temperature strength of Fe-Cr-Mn austenitic alloys

International Nuclear Information System (INIS)

Hosoi, Y.; Okazaki, Y.; Wade, N.; Miyahara, K.

1990-01-01

High Mn-Cr-Fe base alloys are candidates for the first wall material of fusion reactors because of rapid decay of radioactivity of the alloys after neutron irradiation compared with that of Ni-Cr-Fe base alloys. Their high temperature properties, however, are not clearly understood at present. In this paper, a study has been made of the effects of Mn, C and N content on the high-temperature tensile strength and creep properties of a 12% CR-Fe base alloy. Mn tends to decrease tensile strength and proof stress at intermediate temperatures. At higher temperatures in the austenite range, however, tensile properties scarcely depend on Mn content. C and N additions improve the tensile properties markedly. The combined addition of 0.2%C and 0.2%N to a 12%Cr-15%Mn-Fe base alloy makes the strength at 873K as high as that of a modified type 316 stainless steel. Combined alloying with C and N also improves the creep strength. Cold working is very useful in increasing the creep strength because of the finely dispersed precipitates in the matrix during creep. From these results, Fe-12%Cr-15%Mn-15%Mn-0.2%c-0.2%N is recommended as one of the most suitable alloys in this system for high temperature usage. (author)

L-J phase in a Cu2.2Mn0.8Al alloy

Science.gov (United States)

Jeng, S. C.; Liu, T. F.

1995-06-01

A new type of precipitate (designated L-J phase) with two variants was observed within the (DO3 + L21) matrix in a Cu2.2Mn0.8Al alloy. Transmission electron microscopy examinations indicated that the L-J phase has an orthorhombic structure with lattice parameters a = 0.413 nm, b = 0.254 nm and c = 0.728 nm. The orientation relationship between the L-J phase and the matrix is (100)L-J//(011) m , (010)L-J//(111) m and (001)L-J//(211) m . The rotation axis and rotation angle between two variants of the L-J phase are [021] and 90 deg. The L-J phase has never been observed in various Cu-Al, Cu-Mn, and Cu-Al-Mn alloy systems before.

Thermoelastic martensite and shape memory effect in ductile Cu-Al-Mn alloys

Science.gov (United States)

Kainuma, R.; Takahashi, S.; Ishida, K.

1996-08-01

Ductile shape memory (SM) alloys of the Cu-AI-Mn system have been developed by controlling the degree of order in the β phase. Additions of Mn to the binary Cu-Al alloy stabilize the β phase and widen the single-phase region to lower temperature and lower Al contents. It is shown that Cu-Al-Mn alloys with low Al contents have either the disordered A2 structure or the ordered L21 structure with a lower degree of order and that they exhibit excellent ductility. The disordered A2 phase martensitically transforms to the disordered Al phase with a high density of twins. The martensite phase formed from the ordered L21 phase has the 18R structure. The SM effect accompanies both the A2 → Al and L21 → 18R martensitic transformations. These alloys exhibit 15 pct strain to failure, 60 to 90 pct rolling reduction without cracking, and 80 to 90 pct recovery from bend test in the martensitic condition. Experimental results on the microstructure, crystal structure, mechanical properties, and shape memory behavior in the ductile Cu-AI-Mn alloys are presented and discussed.

Activity of Aniline Methylation over Fe-Cu-Cr Ternary Spinel Systems

Directory of Open Access Journals (Sweden)

Reni George

2014-03-01

Full Text Available A series of spinels having thegeneral formula CuCr2-xFexO4 with x=0.25,0.75, 1.25, 1.75 were prepared by co-precipitation method. The catalysts werecharacterized by various physico-chemical methods like XRD, BET, UV-DRS, SEM,EDX, TPD etc. The reaction of aniline with methanol was studied in a fixed-bedreactor system as a potential source for the production of various methylanilines. It was observed that systems possessing low ‘x’ values are highlyselective and active for N-monoalkylation of aniline leading toN-methylaniline. Reaction parameters were properly varied to optimize thereaction conditions for obtaining N-methylaniline selectively and in betteryield. Among the systems CuCr1.75Fe0.25O4 isremarkable due to its very high activity and excellent stability. Under theoptimized conditions N-methylaniline selectivity exceeded 91%. CuCr1.25Fe0.75O4gives better conversion than CuCr1.75Fe0.25O4in CuCr2-xFexO4 series. The Lewis acid sitesof the catalysts are mainly responsible for the good catalytic performance. © 2014 BCREC UNDIP. All rights reservedSubmitted: 18th July 2013; Revised: 5th November 2013; Accepted: 1st December 2013[How to Cite: George, R., George, K., Sugunan, S. (2014. Activity of Aniline Methylation over Fe-Cu-Cr Ternary Spinel Systems. Bulletin of Chemical Reaction Engineering & Catalysis, 9 (1: 39-44. (doi:10.9767/bcrec.9.1.5169.39-44][Permalink/DOI: http://dx.doi.org/10.9767/bcrec.9.1.5169.39-44] 

Characterization of CuCrZr and CuCrZr/SS junction strength for different blanket components manufacturing conditions

International Nuclear Information System (INIS)

Gillia, O.; Briottet, L.; Chu, I.; Lemoine, P.; Bucci, P.; Peacock, A.

2007-01-01

Full text of publication follows: This work describes studies on the strength of CuCrZr/SS joint for different manufacturing conditions foreseen for the fabrication of blanket components. In the meantime, as junction strength is expected to be strongly related to CuCrZr property, investigation on the properties of the CuCrZr itself after the different manufacturing conditions is also presented. The initial manufacturing conditions retained were made of a HIP treatment combined with a fast cooling plus a subsequent ageing treatment. For security reasons, the HIP quenching operation was not possible. It is too severe for the HIP vessel. A supplementary solutioning cycle has then been inserted to the heat treatment process just after the HIP-bonding treatment in order to have a sufficient fast cooling of the CuCrZr. The manufacturing conditions thus comprise a HIP cycle (simulated for mono-material samples), a separate solutioning cycle with controlled cooling rate and an ageing treatment. The influence of solutioning temperature has been addressed (1040 deg. C or 980 deg. C) as well as that of the cooling rate after solutioning (70 deg. C/min to water quench), the ageing temperature (480 deg. C or 560 deg. C) and the HIP temperature (1040 deg. C or 980 deg. C). Test results show that the ageing temperature is very important for keeping high strength of material whereas elongation properties are not very sensible to the manufacturing conditions. 1040 deg. C HIP or solutioning temperature gives better strength properties, as well as a higher cooling rate after solutioning. Concerning samples with junctions, it appears that CT test is more selective than other tests since tensile test does not give rupture at joint and KCU test eliminates a route without classifying other routes. A minimum value of J Q for CT test is given, but as confined plasticity requirement is not satisfied for the sample geometry, this value should only be used concomitantly with the same testing

Low-field spin dynamics of Cr₇Ni and Cr₇Ni-Cu-Cr₇Ni molecular rings as detected by μsR

OpenAIRE

Sanna, S.; Arosio, P.; Bordonali, L.; Adelnia, F.; Mariani, M.; Garlatti, E.; Baines, C.; Amato, A.; Sabareesh, K. P.V.; Timco, G.; Winpenny, R. E.P.; Blundell, S. J.; Lascialfari, A.

2017-01-01

Muon spin rotation measurements were used to investigate the spin dynamics of heterometallic Cr7Ni and Cr7Ni-Cu-Cr7Ni molecular clusters. In Cr7Ni the magnetic ions are arranged in a quasiplanar ring and interact via an antiferromagnetic exchange coupling constant J, while Cr7Ni-Cu-Cr7Ni is composed of two Cr7Ni linked by a bridging moiety containing one Cu ion, that induces an inter-ring ferromagnetic interaction J ≪ J. The longitudinal muon relaxation rate λ collected at low magnetic fields...

Room temperature magnetocaloric effect in Ni-Mn-In-Cr ferromagnetic shape memory alloy thin films

Energy Technology Data Exchange (ETDEWEB)

Akkera, Harish Sharma [Functionalnanomaterials Research Lab, Department of Physics, Indian Institute of Technology Roorkee, Uttarakhand-247667 (India); Singh, Inderdeep [Mechanical and Industrial Engineering Department, Indian Institute of Technology Roorkee, Uttarakhand-24667 (India); Kaur, Davinder, E-mail: dkaurfph@iitr.ernet.in [Functionalnanomaterials Research Lab, Department of Physics, Indian Institute of Technology Roorkee, Uttarakhand-247667 (India)

2017-02-15

The influence of Cr substitution for In on the martensitic phase transformation and magnetocaloric effect (MCE) has been investigated in Ni-Mn-Cr-In ferromagnetic shape memory alloy (FSMA) thin films fabricated by magnetron sputtering. Temperature dependent magnetization (M-T) measurements demonstrated that the martensitic transformation temperatures (T{sub M}) monotonously increase with the increase of Cr content due to change in valence electron concentration (e/a) and cell volume. From the study of isothermal magnetization curves (M-H), magnetocaloric effect around the martensitic transformation has been investigated in these FSMA thin films. The magnetic entropy change ∆S{sub M} of 7.0 mJ/cm{sup 3}-K was observed in Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5} film at 302 K in an applied field of 2 T. Further, the refrigerant capacity (RC) was also calculated for all the films in an applied field of 2 T. These findings indicate that the Cr doped Ni-Mn-In FSMA thin films are potential candidates for room temperature micro-length-scale magnetic refrigeration applications. - Highlights: • The Cr content leads to an increase in the martensitic transformation temperature. • The ∆S{sub M} =7 mJ/cm{sup 3}-K at 302 K was observed in the Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5}. • The RC =39.2 mJ/K at 2 T was obtained in Ni{sub 51.1}Mn{sub 34.9}In{sub 9.5}Cr{sub 4.5} film.

Phase transformation and microstructure study of the as-cast Cu-rich Cu-Al-Mn ternary alloys

Directory of Open Access Journals (Sweden)

Holjevac-Grgurić T.

2017-01-01

Full Text Available Four Cu-rich alloys from the ternary Cu-Al-Mn system were prepared in the electric-arc furnace and casted in cylindrical moulds with dimensions: f=8 mm and length 12 mm. Microstructural investigations of the prepared samples were performed by using optical microscopy (OM and scanning electron microscopy, equipped by energy dispersive spectroscopy (SEM-EDS. Assignation of crystalline phases was confirmed by XRD analysis. Phase transition temperatures were determined using simultaneous thermal analyzer STA DSC/TG. Phase equilibria calculation of the ternary Cu-Al-Mn system was performed using optimized thermodynamic parameters from literature. Microstructure and phase transitions of the prepared as-cast alloys were investigated and experimental results were compared with the results of thermodynamic calculations.

Solid-state reactions during mechanical alloying of ternary Fe-Al-X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems: A review

Science.gov (United States)

Hadef, Fatma

2016-12-01

The last decade has witnessed an intensive research in the field of nanocrystalline materials due to their enhanced properties. A lot of processing techniques were developed in order to synthesis these novel materials, among them mechanical alloying or high-energy ball milling. In fact, mechanical alloying is one of the most common operations in the processing of solids. It can be used to quickly and easily synthesize a variety of technologically useful materials which are very difficult to manufacture by other techniques. One advantage of MA over many other techniques is that is a solid state technique and consequently problems associated with melting and solidification are bypassed. Special attention is being paid to the synthesis of alloys through reactions mainly occurring in solid state in many metallic ternary Fe-Al-X systems, in order to improve mainly Fe-Al structural and mechanical properties. The results show that nanocrystallization is the common result occurring in all systems during MA process. The aim of this work is to illustrate the uniqueness of MA process to induce phase transformation in metallic Fe-Al-X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems.

New ternary ordered structures in CuMPt6 (M=3d elements) alloys

International Nuclear Information System (INIS)

Das, Ananda Kumar; Nakamura, Reo; Takahashi, Miwako; Ohshima, Ken-ichi; Iwasaki, Hiroshi; Shishido, Toetsu

2006-01-01

X-ray and electron diffraction measurements were performed to investigate the structure and ordering behaviour of the ternary alloys CuMPt 6 (M=Ti, V, Cr, Mn, Fe, Co, and Ni). X-ray polycrystalline diffraction patterns of all the speciments quenched from 1000degC have shown that a single phase is formed at this stoichiometric composition. The alloys with M=Cr, Mn, Co, and Ni have the face-centred cubic (fcc) structure, while in the alloys with M=Ti, V, and Fe ordering has occurred and the structure is of the Cu 3 Au type. On annealing at lower temperatures ordering has been induced in the alloys with M=Cr, Mn, and Co and the structure is of the Cu 3 Au type, though the ordering in the last alloy has remained incomplete. Detailed X-ray diffraction measurements on single crystals of the CuMnPt 6 alloy have revealed that further ordering takes place and structure changes from the Cu 3 Au type into the cubic ABC 6 type with the unit cell as large 2 x 2 x 2 as the fcc unit cell, a new observation of the double-step ordering in the ternary fcc alloy. The corresponding transition temperatures are T c =970(±5)degC and T cl =750(±5)degC. (author)

First-principle study of structural, electronic, vibrational and magnetic properties of HCN adsorbed graphene doped with Cr, Mn and Fe

International Nuclear Information System (INIS)

Shi, Li Bin; Wang, Yong Ping; Dong, Hai Kuan

2015-01-01

Graphical abstract: - Highlights: • Cr, Mn and Fe doped graphene is more active to adsorb HCN molecule than pristine graphene. • The conductivity of Fe and Mn doped graphene hardly changes after adsorption HCN molecule. • The conductivity of Cr doped graphene can be affected significantly due to HCN adsorption. • The Cr, Mn and Fe may destroy the long range order in graphene. • Phonon density of states suggests that Cr doped graphene is stable. - Abstract: The adsorption energy, electronic structure, lattice vibration and magnetic properties of Cr, Mn and Fe doped graphene with and without HCN adsorption are investigated by the first principles based on density functional theory. The physisorption and chemisorption have been identified. In the paper, Cr-NG, Mn-NG and Fe-NG denote HCN adsorption on Cr, Mn and Fe doped graphene with N atom toward the adsorption site. It is found that the adsorption energy is −1.36 eV for Fe-NG, −0.60 eV for Mn-NG and −0.86 eV for Cr-NG. The Cr-NG will convert from half-metallic behavior to semiconductor after adsorbing HCN molecule, which indicates that the conductivity changes significantly. Phonon density of states (PDOS) shows that the long range order in graphene can be destroyed by doping Fe, Mn and Cr. The imaginary frequency mode in PDOS suggests that Fe and Mn doped graphene is unstable, while Cr doped graphene is stable. The electronic properties are sensitive toward adsorbing HCN, indicating that Cr doped graphene is a promising sensor for detecting HCN molecule. This study provides a useful basis for understanding of a wide variety of physical properties on graphene

Self-Formed Barrier with Cu-Mn alloy Metallization and its Effects on Reliability

International Nuclear Information System (INIS)

Koike, J.; Wada, M.; Usui, T.; Nasu, H.; Takahashi, S.; Shimizu, N.; Yoshimaru, M.; Shibata, H.

2006-01-01

Advancement of semiconductor devices requires the realization of an ultra-thin (less than 5 nm thick) diffusion barrier layer between Cu interconnect and insulating layers. Self-forming barrier layers have been considered as an alternative barrier structure to the conventional Ta/TaN barrier layers. The present work investigated the possibility of the self-forming barrier layer using Cu-Mn alloy thin films deposited directly on SiO2. After annealing at 450 deg. C for 30 min, an amorphous oxide layer of 3-4 nm in thickness was formed uniformly at the interface. The oxide formation was accompanied by complete expulsion of Mn atoms from the Cu-Mn alloy, leading to a drastic decrease in resistivity of the film. No interdiffusion was observed between Cu and SiO2, indicating an excellent diffusion-barrier property of the interface oxide

Mn-Cr dating of Fe- and Ca-rich olivine from 'quenched' and 'plutonic' angrite meteorites using Secondary Ion Mass Spectrometry

Science.gov (United States)

McKibbin, Seann J.; Ireland, Trevor R.; Amelin, Yuri; Holden, Peter

2015-05-01

Angrite meteorites are suitable for Mn-Cr relative dating (53Mn decays to 53Cr with a half life of 3.7 Myr) using Secondary Ion Mass Spectrometry (SIMS) because they contain olivine and kirschsteinite with very high 55Mn/52Cr ratios arising from very low Cr concentrations. Discrepant Mn-Cr and U-Pb time intervals between the extrusive or 'quenched' angrite D'Orbigny and some slowly cooled or 'plutonic' angrites suggests that some have been affected by secondary disturbances, but this seems to have occurred in quenched rather than in slow-cooled plutonic angrites, where such disturbance or delay of isotopic closure might be expected. Using SIMS, we investigate the Mn-Cr systematics of quenched angrites to higher precision than previously achieved by this method and extend our investigation to non-quenched (plutonic or sub-volcanic) angrites. High values of 3.54 (±0.18) × 10-6 and 3.40 (±0.19) × 10-6 (2-sigma) are found for the initial 53Mn/55Mn of the quenched angrites D'Orbigny and Sahara 99555, which are preserved by Cr-poor olivine and kirschsteinite. The previously reported initial 53Mn/55Mn value of D'Orbigny obtained from bulk-rock and mineral separates is slightly lower and was probably controlled by Cr-rich olivine. Results can be interpreted in terms of the diffusivity of Cr in this mineral. Very low Cr concentrations in Ca-rich olivine and kirschsteinite are probably charge balanced by Al; this substitutes for Si and likely diffuses at a very slow rate because Si is the slowest-diffusing cation in olivine. Diffusion in Cr-rich Mg-Fe olivine is probably controlled by cation vacancies because of deficiency in charge-balancing Al and is therefore more prone to disturbance. The higher initial 53Mn/55Mn found by SIMS for extrusive angrites is more likely to reflect closure of Cr in kirschsteinite at the time of crystallisation, simultaneous with closure of U-Pb and Hf-W isotope systematics for these meteorites obtained from pyroxenes. For the younger

Reclamation of Cr-contaminated or Cu-contaminated agricultural soils using sunflower and chelants.

Science.gov (United States)

Cicatelli, Angela; Guarino, Francesco; Castiglione, Stefano

2017-04-01

Chromium (Cr) and copper (Cu) are pollutants with a strong environmental impact. "Green biotechnology" as phytoremediation represents a sustainability opportunity for soil reclamation. In this study, we evaluated the possibility to reclaim agricultural soils located in the Solofrana valley, contaminated by Cr or Cu. Chromium contamination derives by repeated flooding events of Solofrana rivers containing Cr because of leather tanning plants, while Cu soil pollution was due to the use of Cu-rich pesticides in agriculture. Both metals showed a very low bioavailability. In order to perform an assisted phytoremediation of polluted fields, we carried out a preliminary ex situ experimentation testing for the first time sunflowers (cv. Pretor) and chelants (ethylenediaminetetraacetic acid (EDTA) and/or ethylene diamine disuccinate (EDDS)), useful when metal bioavailability is low. No symptoms of toxicity were observed in sunflowers grown on both soils, while biomass was improved when EDDS was added. Cr and Cu bioavailability was only slightly enhanced by chelants at the end of the treatments. Both Cr and Cu were mainly accumulated in the roots; moreover, Cu was also translocated to the aboveground organs in the presence of EDTA. The ex situ experimentation demonstrated that assisted phytoremediation is a very slow process not useful in the case of persistent pollution.

Grain Refinement and Mechanical Properties of Cu-Cr-Zr Alloys with Different Nano-Sized TiCp Addition.

Science.gov (United States)

Zhang, Dongdong; Bai, Fang; Wang, Yong; Wang, Jinguo; Wang, Wenquan

2017-08-08

The TiC p /Cu master alloy was prepared via thermal explosion reaction. Afterwards, the nano-sized TiC p /Cu master alloy was dispersed by electromagnetic stirring casting into the melting Cu-Cr-Zr alloys to fabricate the nano-sized TiC p -reinforced Cu-Cr-Zr composites. Results show that nano-sized TiC p can effectively refine the grain size of Cu-Cr-Zr alloys. The morphologies of grain in Cu-Cr-Zr composites changed from dendritic grain to equiaxed crystal because of the addition and dispersion of nano-sized TiC p . The grain size decreased from 82 to 28 μm with the nano-sized TiC p content. Compared with Cu-Cr-Zr alloys, the ultimate compressive strength (σ UCS ) and yield strength (σ 0.2 ) of 4 wt% TiC p -reinforced Cu-Cr-Zr composites increased by 6.7% and 9.4%, respectively. The wear resistance of the nano-sized TiCp-reinforced Cu-Cr-Zr composites increased with the increasing nano-sized TiCp content. The wear loss of the nano-sized TiC p -reinforced Cu-Cr-Zr composites decreased with the increasing TiC p content under abrasive particles. The eletrical conductivity of Cu-Cr-Zr alloys, 2% and 4% nano-sized TiCp-reinforced Cu-Cr-Zr composites are 64.71% IACS, 56.77% IACS and 52.93% IACS, respectively.

Coupling between magnetic, dielectric properties and crystal structure in MnT2O4 (T = V, Cr, Mn)

International Nuclear Information System (INIS)

Suzuki, T; Adachi, K; Katsufuji, T

2006-01-01

We measured the temperature dependence of dielectric constant and striction for spinel MnT 2 O 4 (T = V, Cr, Mn) under magnetic field. We found critical changes of the dielectric constant and striction with ferrimagnetic ordering as well as applied magnetic field in MnV 2 O 4 and Mn 3 O 4 , which have orbital degree of freedom in the T 3+ ion. This result indicates the importance of the orbital degree of freedom for the coupling between dielectric, magnetic properties and crystal structure in these spinel compounds

Determination of Na, Mn and Cu in cocoon, raw silk and degummed silk by nondestructive activation analysis

Energy Technology Data Exchange (ETDEWEB)

Maki, Y; Ishiguro, Y [Industrial Research Inst. of Kanagawa Prefecture, Yokohama (Japan)

1976-01-01

The sodium, manganese and copper contained in cocoons, raw silk and degummed silk thread were determined by the nondestructive activation analysis. After each sample was irradiated with the thermal neutron flux of 5 x 10/sup 11/n/cm/sup 2/.sec, its ..gamma..-ray spectrum was measured with a NaI(Tl) detector. With the photoelectric peaks at 511 keV (/sup 64/Cu), 1368 keV (/sup 24/Na) and 847 keV (/sup 56/Mn), each element was quantitatively determined and its content was obtained. The measurement of the ..gamma..-ray spectra of samples with a Ge (Li) detector proved the presence of An, Sb, Fe, Zn, Cr, Sc, Co, etc. Large amounts of Na and Cu were detected in the sericin portion of cocoons, and the adhesion of Cu from a reeling-off machine to raw silk was also observed during the process of degumming cocoons to make raw silk.

Characterization of CuCrZr and CuCrZr/SS joint strength for different blanket components manufacturing conditions

Science.gov (United States)

Gillia, Olivier; Briottet, Laurent; Chu, Isabelle; Lemoine, Patrick; Rigal, Emmanuel; Peacock, Alan

2009-04-01

This work describes studies on the strength of CuCrZr/SS joints for different manufacturing conditions foreseen for the fabrication of blanket components. In the meantime, as junction strength is expected to be strongly related to CuCrZr properties, investigation on the properties of the CuCrZr itself after the different manufacturing conditions is also presented. The initial manufacturing conditions retained were made of a HIP treatment combined with a fast cooling plus a subsequent ageing treatment. For security reasons, the HIP-quenching operation was not possible. A supplementary solutionning cycle with fast cooling has thus been inserted in the heat treatment process just after the HIP bonding treatment. The influence of solutionning temperature (1040 °C or 980 °C), the cooling rate after solutionning (70 °C/min to water quench), the ageing temperature (480 °C or 560 °C) and the HIP temperature (1040 °C or 980 °C) have been addressed. Test results show that the ageing temperature is very important for keeping high strength of material whereas elongation properties are not very sensible to the manufacturing conditions. 1040 °C HIP or solutionning temperature gives better strength properties, as well as a higher cooling rate after solutionning. Concerning samples with joints, it appears that CT test is more selective than other tests since tensile test does not give rupture at joint and KCU test eliminates a route without classifying other routes.

Characterization of CuCrZr and CuCrZr/SS joint strength for different blanket components manufacturing conditions

International Nuclear Information System (INIS)

Gillia, Olivier; Briottet, Laurent; Chu, Isabelle; Lemoine, Patrick; Rigal, Emmanuel; Peacock, Alan

2009-01-01

This work describes studies on the strength of CuCrZr/SS joints for different manufacturing conditions foreseen for the fabrication of blanket components. In the meantime, as junction strength is expected to be strongly related to CuCrZr properties, investigation on the properties of the CuCrZr itself after the different manufacturing conditions is also presented. The initial manufacturing conditions retained were made of a HIP treatment combined with a fast cooling plus a subsequent ageing treatment. For security reasons, the HIP-quenching operation was not possible. A supplementary solutionning cycle with fast cooling has thus been inserted in the heat treatment process just after the HIP bonding treatment. The influence of solutionning temperature (1040 deg. C or 980 deg. C), the cooling rate after solutionning (70 deg. C/min to water quench), the ageing temperature (480 deg. C or 560 deg. C) and the HIP temperature (1040 deg. C or 980 deg. C) have been addressed. Test results show that the ageing temperature is very important for keeping high strength of material whereas elongation properties are not very sensible to the manufacturing conditions. 1040 deg. C HIP or solutionning temperature gives better strength properties, as well as a higher cooling rate after solutionning. Concerning samples with joints, it appears that CT test is more selective than other tests since tensile test does not give rupture at joint and KCU test eliminates a route without classifying other routes.

Atomistic spin dynamics simulations on Mn-doped GaAs and CuMn

Energy Technology Data Exchange (ETDEWEB)

Hellsvik, Johan, E-mail: johan.hellsvik@fysik.uu.s [Department of Physics and Materials Science, Uppsala University, Box 530, SE-751 21 Uppsala (Sweden)

2010-01-01

The magnetic dynamical behavior of two random alloys have been investigated in atomistic spin dynamics (ASD) simulations. For both materials, magnetic exchange parameters calculated with first principles electronic structure methods were used. From experiments it is well known that CuMn is a highly frustrated magnetic system and a good manifestation of a Heisenberg spin glass. In our ASD simulations the behavior of the autocorrelation function indicate spin glass behavior. The diluted magnetic semiconductor (DMS) Mn-doped GaAs is engineered with hopes of high enough Curie temperatures to operate in spintronic devices. Impurities such as As antisites and Mn interstitials change the exhange couplings from being mainly ferromagnetic to also have antiferromagnetic components. We explore how the resulting frustration affects the magnetization dynamics for a varying rate of As antisites.

Thermal behaviour of Cu-Mg-Mn and Ni-Mg-Mn layered double hydroxides and characterization of formed oxides

Czech Academy of Sciences Publication Activity Database

Kovanda, F.; Grygar, Tomáš; Dorničák, V.; Rojka, T.; Bezdička, Petr; Jirátová, Květa

2005-01-01

Roč. 28, 1-4 (2005), s. 121-136 ISSN 0169-1317 Institutional research plan: CEZ:AV0Z40320502 Keywords : Cu-Mg-Mn basic carbonates * Ni-Mg-Mn hydrotalcite Subject RIV: CA - Inorganic Chemistry Impact factor: 1.324, year: 2005

Succulent species differ substantially in their tolerance and phytoextraction potential when grown in the presence of Cd, Cr, Cu, Mn, Ni, Pb, and Zn.

Science.gov (United States)

Zhang, Chengjun; Sale, Peter W G; Clark, Gary J; Liu, Wuxing; Doronila, Augustine I; Kolev, Spas D; Tang, Caixian

2015-12-01

Plants for the phytoextraction of heavy metals should have the ability to accumulate high concentrations of such metals and exhibit multiple tolerance traits to cope with adverse conditions such as coexistence of multiple heavy metals, high salinity, and drought which are the characteristics of many contaminated soils. This study compared 14 succulent species for their phytoextraction potential of Cd, Cr, Cu, Mn, Ni, Pb, and Zn. There were species variations in metal tolerance and accumulation. Among the 14 succulent species, an Australian native halophyte Carpobrotus rossii exhibited the highest relative growth rate (20.6-26.6 mg plant(-1) day(-1)) and highest tolerance index (78-93%), whilst Sedum "Autumn Joy" had the lowest relative growth rate (8.3-13.6 mg plant(-1) day(-1)), and Crassula multicava showed the lowest tolerance indices (phytoextraction of these heavy metals than other species. These findings suggest that Carpobrotus rossii is a promising candidate for phytoextraction of multiple heavy metals, and the aquatic or semiterrestrial Crassula helmsii is suitable for phytoextraction of Cd and Zn from polluted waters or wetlands.

Effect of CeLa addition on the microstructures and mechanical properties of Al-Cu-Mn-Mg-Fe alloy

International Nuclear Information System (INIS)

Du, Jiandi; Ding, Dongyan; Xu, Zhou; Zhang, Junchao; Zhang, Wenlong; Gao, Yongjin; Chen, Guozhen; Chen, Weigao; You, Xiaohua; Chen, Renzong; Huang, Yuanwei; Tang, Jinsong

2017-01-01

Development of high strength lithium battery shell alloy is highly desired for new energy automobile industry. The microstructures and mechanical properties of Al-Cu-Mn-Mg-Fe alloy with different CeLa additions were investigated through optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Rietveld refinement and tensile testing. Experimental results indicate that Al 8 Cu 4 Ce and Al 6 Cu 6 La phases formed due to CeLa addition. Addition of 0.25 wt.% CeLa could promote the formation of denser precipitation of Al 20 Cu 2 Mn 3 and Al 6 (Mn, Fe) phases, which improved the mechanical properties of the alloy at room temperature. However, up to 0.50 wt.% CeLa addition could promote the formation of coarse Al 8 Cu 4 Ce phase, Al 6 Cu 6 La phase and Al 6 (Mn, Fe) phase, which resulted in weakened mechanical properties. - Highlights: •Al-Cu-Mn-Mg-Fe alloys with different CeLa addition were fabricated through casting and rolling. •Al 8 Cu 4 Ce and Al 6 Cu 6 La phases formed after CeLa addition. •Addition of 0.25 wt.% CeLa promoted formation of denser precipitates of Al 20 Cu 2 Mn 3 and Al 6 (Mn, Fe). •Mechanical properties of the alloy was improved after 0.25 wt.% CeLa addition.

Characteristics of oxide scale formed on Cu-bearing austenitic stainless steel during early stages of high temperature oxidation

Energy Technology Data Exchange (ETDEWEB)

Swaminathan, Srinivasan, E-mail: swaminathan@kist.re.kr [Metallurgy & Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); High Temperature Energy Materials Research Center, Korea Institute of Science and Technology, Seongbuk-gu, Seoul 136 791 (Korea, Republic of); Krishna, Nanda Gopala [Metallurgy & Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Kim, Dong-Ik, E-mail: dongikkim@kist.re.kr [High Temperature Energy Materials Research Center, Korea Institute of Science and Technology, Seongbuk-gu, Seoul 136 791 (Korea, Republic of)

2015-10-30

Highlights: • Initial oxidation characteristics of Cu-bearing austenitic stainless steel at 650 °C were studied. • Strong segregation and oxidation of Mn and Nb were found in the entire oxide scale. • Surface coverage by metallic Cu-rich precipitates increases with exposure time. • Chemical heterogeneity of oxide scale revealed initial oxidation to be non-selective. • Fe-Cr and Mn-Cr mixed oxides were realized along with binary oxides of Fe, Cr and Mn. - Abstract: Oxide scale evolution on Cu-bearing austenitic stainless steel 304H at 650 °C, in ambient air, for exposure times 100, 300, 500 and 1000 h, has been investigated. Surface morphology and chemistry of the oxide scale grown were examined using SEM/EDX and XPS. The oxidation kinetics was determined by measuring the weight change using an electronic balance. At the initial stage, up to 500 h of exposure time, the oxidation rate was rapid due to surface reactions governed primarily by oxygen ingress, and then, dropped to a low rate after prolonged oxidation for 1000 h. The diffusion of reactants through the initially formed oxide scale limits the oxidation rate at longer times, thus, the progress of reaction followed the parabolic kinetics. The formed oxide scale was enriched significantly with segregation and subsequent oxidation of Nb, and finely dispersed metallic Cu particles. Within the time frame of oxidation, the oxide scale was mainly composed of mixed oxides such as FeCr{sub 2}O{sub 4} and MnCr{sub 2}O{sub 4} along with the binary oxides of Fe, Cr and Mn. Moreover, the precipitation fraction of Cu-rich particles on the oxide scale increased markedly with increase of exposure times. The chemical heterogeneity of oxide scale suggests that the oxidation occurred in a non-selective manner.

Study of the experimental parameters for the determination of Ca, Cr, Cu, Fe, Mn and Ni on nuclear grade UO2 by X-ray fluorescence technique

International Nuclear Information System (INIS)

Salvador, V.L.R.

1982-01-01

An analytical method for the simultaneous determinations of low concentrations of Ca, Cr, Cu, Fe, Mn and Ni on the nuclear grade UO 2 by X-ray fluorescence technique, without the use of chemical treatment, is described. The optimization of the experimental conditions was established on the X-ray fluorescence spectrometer and a low limit of detection (4 - 7 μg/gU) was achieved which satisfies the requirement in the nuclear fuel specification. The samples were prepared in the form of double layer pressed pellets using boric acid as a binding agent. The characteristic first order K sub(α) line intensity of each minor component was measured and the values of its concentrations were deduced using respective standard calibrations curves. The precision, accuracy and acceptability of the method were determined for all elements. The values of the precision are in the range of 2 - 10% and the accuracy are lower than 7%. (Author) [pt

Hardening of Fe-Cr-Mn steels cold plastic working

International Nuclear Information System (INIS)

Malinov, L.S.; Konop-Lyashko, V.I.; Nikoporets, N.M.

1983-01-01

The dependence is established between the level of proper-- ties obtained after cold plastic working and development of martensite transformations when loading in Fe-Cr-Mn steels containing 0.1-0.5% C, 13% Cr, 8-12% Mn, as well as in a number of complex alloyed steels. It is shown that the highest level of mechanical properties can be obtained after cold plastic working only in steels with definite austenite stability. Cold plastic working can both activize and stabilize austenite relatively to martensite formation during loading. The first thing is found when under the effect of preliminary cold working dislocation splitting takes place, as well as the formation of a small amount of E-phase and martensite. The second thing manifests itself when under the effect of cold working performed above Md (Md<20 deg C) cell dislocation structure is formed and dislocation pinning takes place

Effect of Cu-Cr co-substitution on magnetic properties of nanocrystalline magnesium ferrite

Energy Technology Data Exchange (ETDEWEB)

Iqbal, Muhammad Javed, E-mail: mjiqauchem@yahoo.com [Surface and Solid State Chemistry Laboratory, Department of Chemistry, Quaid-I-Azam University, Islamabad 45320 (Pakistan); Ahmad, Zahoor [Surface and Solid State Chemistry Laboratory, Department of Chemistry, Quaid-I-Azam University, Islamabad 45320 (Pakistan); Melikhov, Yevgen [Wolfson Centre for Magnetics, School of Engineering, Cardiff University, Cardiff CF24 3AA (United Kingdom); Nlebedim, Ikenna Cajetan [Ames Laboratory of US Department of Energy, Ames, IA 50011 (United States)

2012-03-15

This study deals with the temperature and composition dependence of magnetization and magnetic anisotropy of Cu{sup 2+}-Cr{sup 3+} co-substituted magnesium ferrite, Mg{sub 1-x}Cu{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} (x=0.0-0.5). The synthesized materials are characterized using thermo gravimetric analysis, X-ray diffraction, scanning electron microscopy, energy dispersive X-ray fluorescence, Moessbauer spectrometer, superconducting quantum interference device magnetometer and vibrating sample magnetometer. The M-H loops measured up to 50 kOe at 300, 200 and 100 K, revealed narrow hysteresis curves with a coercive field and saturation magnetization varying for different compositions. The high field regimes of these loops are modeled using the Law of Approach to saturation to extract anisotropy information and saturation magnetization. Both the saturation magnetization and the anisotropy constant are observed to increase with the decrease in temperature while decrease with the Cu-Cr co-substituents for all the samples. Explanation of the observed behavior is proposed in terms of the preference of the co-substituent ions of Cu{sup 2+} and Cr{sup 3+} and their predominant choice to substitute into the octahedral sites of the cubic spinel lattice. - Highlights: Black-Right-Pointing-Pointer Mg{sub 1-x}Cu{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4} was synthesized by novel PEG assisted microemulsion method. Black-Right-Pointing-Pointer Present paper dealt with magnetic properties of Mg{sub 1-x}Cu{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4}. Black-Right-Pointing-Pointer XRD patterns revealed tetragonal distorted cubic structure of Mg{sub 1-x}Cu{sub x}Cr{sub x}Fe{sub 2-x}O{sub 4}. Black-Right-Pointing-Pointer Mossbauer spectroscopy confirmed that Cu-Cr occupy octahedral sites. Black-Right-Pointing-Pointer High field regime of M-H loops was modeled using Law of Approach to saturation.

Synthesis, structure and magnetic properties of crystallographically aligned CuCr_2Se_4 thin films

International Nuclear Information System (INIS)

Esters, Marco; Liebig, Andreas; Ditto, Jeffrey J.; Falmbigl, Matthias; Albrecht, Manfred; Johnson, David C.

2016-01-01

We report the low temperature synthesis of highly textured CuCr_2Se_4 thin films using the modulated elemental reactant (MER) method. The structure of CuCr_2Se_4 is determined for the first time in its thin film form and exhibits cell parameters that are smaller than found in bulk CuCr_2Se_4. X-ray diffraction and precession electron diffraction show a strong degree of crystallographic alignment of the crystallites, where the axis is oriented perpendicular to the substrate surface, while being rotationally disordered within the plane. Temperature and field dependent in-plane and out-of-plane magnetization measurements show that the film is ferromagnetic with a Curie temperature of 406 K CuCr_2Se_4 synthesized utilizing the MER method shows stronger magnetic anisotropy (effective anisotropy: 1.82 × 10"6 erg cm"−"3; shape anisotropy: 1.07 × 10"6 erg cm"−"3), with the easy axis lying out of plane, and a larger magnetic moment (6 μ_B/f.u.) than bulk CuCr_2Se_4. - Highlights: • Crystallographically aligned, phase pure CuCr_2Se_4 were synthesized. • The degree of alignment decreases with annealing time. • The films are ferromagnetic with the easy axis along the direction. • The magnetization is larger than bulk CuCr_2Se_4 or other CuCr_2Se_4 films made to date.

Investigation of thermal, mechanical and magnetic behaviors of the Cu-11%Al alloy with Ag and Mn additions

International Nuclear Information System (INIS)

Silva, R.A.G.; Paganotti, A.; Gama, S.; Adorno, A.T.; Carvalho, T.M.; Santos, C.M.A.

2013-01-01

The investigation of thermal, mechanical and magnetic behaviors of the Cu-11%Al, Cu-11%Al-3%Ag, Cu-11%Al-10%Mn and Cu-11%Al-10%Mn-3%Ag alloys was made using microhardness measurements, differential scanning calorimetry, X-ray diffractometry, scanning electron microscopy, energy dispersion X-ray spectroscopy and magnetic moment change with applied field measurement. The results indicated that the Mn addition changes the phase stability range, the microhardness values and makes undetectable the eutectoid reaction in annealed Cu-11%Al and Cu-11%Al-3%Ag alloys while the presence of Ag does not modify the phase transformation sequence neither microhardness values of the annealed Cu-11%Al and Cu-11%Al-10%Mn alloys, but it increases the magnetic moment of this latter at about 2.7 times and decreases the rates of eutectoid and peritectoid reactions of the former. - Highlights: ► The microstructure of Cu-Al alloy is modified in the Ag presence. ► (α + γ) phase is stabilized down to room temperature when Ag is added to Cu-Al alloy. ► Ag-rich phase modifies the magnetic characteristics of Cu–Al–Mn alloy.

Estudo de metais pesados (Co, Cu, Fe, Cr, Ni, Mn, Pb e Zn na Bacia do Tarumã-Açu Manaus (AM Heavy metal (Co, Cu, Fe, Cr, Ni, Mn, Pb e Zn study in the Tarumã-Açu Basin Manaus (AM

Directory of Open Access Journals (Sweden)

Genilson Pereira Santana

2007-01-01

Full Text Available Os resíduos gerados em domicílios incluem diversos produtos, como pesticidas, produtos farmacêuticos, detergentes, óleos de cozinha, metais pesados contidos em baterias e outros utensílios. Esses resíduos são lançados continuamente em aterro sanitário ou lixões em cidades como Manaus. O chorume produzido nesses aterros, quando não tratados, contamina recursos hídricos superficiais e subterrâneos. Neste estudo foi feita uma avaliação das conseqüências da liberação do chorume no sistema hídrico da bacia do Tarumã-Açu. Amostras de água e sedimento foram coletadas nos igarapés Matrinxã, Acará, Bolívia, bacia do Tarumã-Açu e dentro do aterro sanitário (Manaus - Amazonas - Brasil em março 2001. As amostras de água foram filtradas em filtro Milipore (0,45 mm de poro e, em seguida, tratadas com HNO3 concentrado. As amostras de sedimento foram peneiradas em malha de 0,053 mm e digeridas com HCl:HNO3 (1:3 a 150ºC. As concentrações de alguns metais pesados (Co, Cu, Fe, Cr, Ni, Mn, Pb e Zn foram determinadas nas amostras de água e sedimento por espectrometria de absorção atômica de chama. Os resultados revelaram que a concentração dos metais pesados é muito acima dos permitidos pela resolução 357/2005 do CONAMA em praticamente todos os locais amostrados, mostrando que o Aterro Sanitário é um dos principais responsáveis pelo impacto ambiental observado nos corpos hídricos estudados. As análises dos componentes principais (PCA e hierárquica de cluster (HCA, revelam que os pontos de coleta localizados dentro do aterro sanitário apresentam características diferentes dos outros locais amostrados. Além disso, o HCA e PCA mostraram que existe uma similaridade entre os pontos de coleta localizados fora do aterro o que permite afirmar que o chorume do aterro se dissolve por todo corpo hídrico estudado.Domestic sewage involves several products, such as pesticides, pharmaceutics products, detergents, soybean oil

Deposition of Mn-Cu-Ni-enriched sediments during glacial period in the Central Indian Basin

Digital Repository Service at National Institute of Oceanography (India)

Borole, D.V.

Two siliceous sediment cores collected from the Central Indian Basin have been analysed for organic carbon, biogenic silica, Al, Mn, Ni and Cu content. The concentrations of Mn, Cu and Ni showed one order of magnitude variation (an enrichment by a...

Satellite NMR in Cu doped with transition impurities

International Nuclear Information System (INIS)

Slichter, C.P.

1979-01-01

Measurements were made of the conduction electron spin magnetization density, M/sub sigma/(R vector) near iron group atoms (Sc through Ni) in Cu. M/sub sigma/(R vector) produces an additional effective local field which shifts the NMR frequency of nearby shells of Cu nuclei relative to Cu nuclei far from all impurities. Resonances of nearby shells appear as weak satellites to the strong resonance of distant Cu nuclei (the main line). M/sub sigma/(R vector) at a given site is proportional through know constants to the splitting of the satellite from the main line. The shell was identified giving rise to the satellite in many cases by use of single crystals. A good approximation M/sub sigma/(R vector) is proportional to the spin susceptibility chi/sub s/ of the impurity. For CuCr we find a large temperature independent chi/sub s/, in contrast to CuMn and CuFe. The results lead to a picture of the electronic structure of Cr, Mn, and Fe along the lines of Schrieffer and Hirst as ions with integral numbers of d-electrons, possessing crystal field and spin-orbit couplings

Interfacial electronic charge transfer and density of states in short period Cu/Cr multilayers; TOPICAL

International Nuclear Information System (INIS)

Barbee, T W; Bello, A F; Klepeis, J E; Van Buuren, T

1999-01-01

Nanometer period metallic multilayers are ideal structures to investigate electronic phenomena at interfaces between metal films since interfacial atoms comprise a large atomic fraction of the samples. The Cu/Cr binary pair is especially suited to study the interfaces in metals since these elements are mutually insoluble, thus eliminating mixing effects and compound formation and the lattice mismatch is very small. This allows the fabrication of high structural quality Cu/Cr multilayers that have a structure which can be approximated in calculations based on idealized atomic arrangements. The electronic structure of the Cu and the Cr layers in several samples of thin Cu/Cr multilayers were studied using x-ray absorption spectroscopy (XAS). Total electron yield was measured and used to study the white lines at the Cu L(sub 2) and L(sub 3) absorption edges. The white lines at the Cu absorption edges are strongly related to the unoccupied d-orbitals and are used to calculate the amount of charge transfer between the Cr and Cu atoms in interfaces. Analysis of the Cu white lines show a charge transfer of 0.026 electrons/interfacial Cu atom to the interfacial Cr atoms. In the Cu XAS spectra we also observe a van Hove singularity between the L(sub 2) and L(sub 3) absorption edges as expected from the structural analysis. The absorption spectra are compared to partial density of states obtained from a full-potential linear muffin-tin orbital calculation. The calculations support the presence of charge transfer and indicate that it is localized to the first two interfacial layers in both Cu and Cr

Effect of CeLa addition on the microstructures and mechanical properties of Al-Cu-Mn-Mg-Fe alloy

Energy Technology Data Exchange (ETDEWEB)

Du, Jiandi [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Ding, Dongyan, E-mail: dyding@sjtu.edu.cn [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Xu, Zhou; Zhang, Junchao; Zhang, Wenlong [School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Gao, Yongjin; Chen, Guozhen; Chen, Weigao; You, Xiaohua [Huafon NLM Al Co., Ltd, Shanghai 201506 (China); Chen, Renzong; Huang, Yuanwei; Tang, Jinsong [Shanghai Huafon Materials Technology Institute, Shanghai 201203 (China)

2017-01-15

Development of high strength lithium battery shell alloy is highly desired for new energy automobile industry. The microstructures and mechanical properties of Al-Cu-Mn-Mg-Fe alloy with different CeLa additions were investigated through optical microscopy (OM), X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), Rietveld refinement and tensile testing. Experimental results indicate that Al{sub 8}Cu{sub 4}Ce and Al{sub 6}Cu{sub 6}La phases formed due to CeLa addition. Addition of 0.25 wt.% CeLa could promote the formation of denser precipitation of Al{sub 20}Cu{sub 2}Mn{sub 3} and Al{sub 6}(Mn, Fe) phases, which improved the mechanical properties of the alloy at room temperature. However, up to 0.50 wt.% CeLa addition could promote the formation of coarse Al{sub 8}Cu{sub 4}Ce phase, Al{sub 6}Cu{sub 6}La phase and Al{sub 6}(Mn, Fe) phase, which resulted in weakened mechanical properties. - Highlights: •Al-Cu-Mn-Mg-Fe alloys with different CeLa addition were fabricated through casting and rolling. •Al{sub 8}Cu{sub 4}Ce and Al{sub 6}Cu{sub 6}La phases formed after CeLa addition. •Addition of 0.25 wt.% CeLa promoted formation of denser precipitates of Al{sub 20}Cu{sub 2}Mn{sub 3} and Al{sub 6}(Mn, Fe). •Mechanical properties of the alloy was improved after 0.25 wt.% CeLa addition.

Thermodynamic properties of Al-Mn, Al-Cu, and Al-Fe-Cu melts and their relations to liquid and quasicrystal structure

International Nuclear Information System (INIS)

Zaitsev, A I; Zaitseva, N E; Shimko, R Yu; Arutyunyan, N A; Dunaev, S F; Kraposhin, V S; Lam, Ha Thanh

2008-01-01

Thermodynamic properties of molten Al-Mn, Al-Cu and Al-Fe-Cu alloys in a wide temperature range of 1123-1878 K and the whole range of concentrations have been studied using the integral effusion method and Knudsen mass spectrometry. Thermodynamic functions of melts were described by the associated solution model. The possibility of icosahedral quasicrystal (i-QC) precipitation from liquid Al-Mn and Al-Cu-Fe alloys was found to be a consequence of the existence in liquid associates (clusters). A geometric model is suggested for the structure of associates in liquid

Relationship between Microstructure and Properties of Cu-Cr-Ag-(Ce) Alloy Using Microscopic Investigation.

Science.gov (United States)

Chen, Huiming; Yuan, Dawei; Wu, Shanjiang; Wang, Hang; Xie, Weibin; Yang, Bin

2017-01-01

Microstructure, precipitation hardening response, and mechanical and physical properties of Cu-Cr-Ag alloy and Cu-Cr-Ag-Ce alloy have been investigated using transmission electron microscopy, scanning electron microscope, optical microscope, electrical conductivity analysis, and tensile test. The influence of element Ce on the matrix refinement, impurity removal, and precipitation in the Cu-Cr-Ag alloys has been analyzed. The experimental results show that the strength and electrical conductivity of Ce containing alloys are greater than those of Ce-free alloys after each processing step. Improvement of strength and electrical conductivity of the Cu-Cr-Ag alloy by adding Ce element is attributed to removing oxygen and sulfur from as-cast alloy.

Processing of Cu-Cr alloy for combined high strength and high conductivity

Directory of Open Access Journals (Sweden)

A.O Olofinjanaa

2017-11-01

Full Text Available High strength and high conductivity (HSHC are two intrinsic properties difficult to combine in metallic alloy design because; almost all strengthening mechanisms also lead to reduced conductivity. Precipitation hardening by nano-sized precipitates had proven to be the most adequate way to achieve the optimum combination of strength and conductivity in copper based alloys. However, established precipitation strengthened Cu- alloys are limited to very dilute concentration of solutes thereby limiting the volume proportion hardening precipitates. In this work, we report the investigation of the reprocessing of higher Cr concentration Cu- based alloys via rapid solidification. It is found that the rapid solidification in the as-cast ribbon imposed combined solution extension and ultra-refinement of Cr rich phases. X-ray diffraction evidences suggest that the solid solution extension was up to 6wt%Cr. Lattice parameters determined confirmed the many folds extension of solid solution of Cr in Cu.  Thermal aging studies of the cast ribbons indicated that peak aging treatments occurred in about twenty minutes. Peak aged hardness ranged from about 200 to well over 300Hv. The maximum peak aged hardness of 380Hv was obtained for alloy containing 6wt.%Cr but with conductivity of about 50%IACS. The best combined strength/conductivity was obtained for 4wt.%Cr  alloy with hardness of 350HV and conductivity of 80% IACS. The high strengths observed are attributed to the increased volume proportion of semi-coherent Cr rich nano-sized precipitates that evolved from the supersaturated solid solution of Cu-Cr that was achieved from the high cooling rates imposed by the ribbon casting process. The rapid overaging of the high Cr concentration Cu-Cr alloy is still a cause for concern in optimising the process for reaching peak HSHC properties. It is still important to investigate a microstructural design to slow or severely restrict the overaging process. The optimum

3D-atom probe analysis of Cr and Cu added nitriding steels

International Nuclear Information System (INIS)

Takahashi, J.; Kawakami, K.; Sugiyama, M.; Kawasaki, K.

2004-01-01

Full text: Nitriding treatment is a very effective method for hardening the surface of steels and realizing improvement in wear-resistance. Although this technology has been performed for many years, the precipitation and hardening mechanisms are not completely clear. It was not easy to observe very fine precipitates which may be generated in nitriding steels. We performed a three-dimensional atom probe analysis of the nitriding steel plate in which two kinds of precipitates were generated. Hot-rolled steel plates, which mainly contained Cr 1.0wt.% and Cu 1.3wt.%, were nitrided by annealing (550-6000 o ) in a mainly NH 3 atmosphere. The material before the nitriding had a hardness of about 100 Hv. By the nitriding, the surface hardness increased to more than 700 Hv, and the inside hardness also increased to 200 Hv. The specimens were taken from 0.15 mm, 0.3 mm and 0.8 mm depth from the surface, which mostly correspond to the peak, the half and the inside hardness, respectively. In the specimen of 0.8 mm depth, prolate spheroidal Cu precipitates of more than 8 nm in diameter were observed. In the specimen of 0.3 mm depth, plate-shape nitride precipitates of 6-10 nm in diameter were observed in addition to the Cu precipitates. Each Cu precipitate made a pair with the nitride precipitate. In the 0.15 mm depth specimen, Cr nitride precipitates of high volume density in addition to the pairs consisting of a Cu precipitate and a Cr nitride precipitate were observed. The size of the nitride precipitate forming the pair was slightly larger than that of the single Cr nitride precipitates. Furthermore, the denuded zone where the nitride precipitate does not exist was observed around the pairs. From these results, it was concluded that three stages of precipitation arose as follows: By the heat treatment of nitriding processing, Cu precipitates were generated first. Then, Cr nitride nucleated at the surface of the Cu precipitates inhomogeneously, and surrounding solute Cr was

Research on aging precipitation in a Cu-Cr-Zr-Mg alloy

International Nuclear Information System (INIS)

Su Juanhua; Dong Qiming; Liu Ping; Li Hejun; Kang Buxi

2005-01-01

The effects of aging processes on the properties and microstructure of Cu-0.3Cr-0.15Zr-0.05Mg lead frame alloy were investigated. Aging precipitation phase was dealt with by transmission electronic microscope (TEM). After solid solution was treated at 920 deg. C and aged at 470 deg. C for 4 h, the fine precipitation of an ordered compound CrCu 2 (Zr, Mg) is found in copper matrix as well as fine Cr and Cu 4 Zr. Along the grain boundary, there are larger chromium. The hardness and electrical conductivity can reach 109 HV and 80% IACS, respectively. Sixty percent cold-rolled deformation prior to aging at 470 deg. C enhances the hardness of the alloy. The coherent precipitates Cr in copper matrix and the dislocations pinned by the fine precipitates are responsible for maximum strengthening of the alloy. So the hardness 165 HV and electrical conductivity 79.2% IACS are available

Niveles críticos de nutrimentos en suelos de Costa Rica utilizando la solución extractora Mehlich 3

Directory of Open Access Journals (Sweden)

Gilberto Cabalceta

2006-01-01

Full Text Available Se estudió los niveles críticos de Ca, Mg, K, P, S, Cu, Zn y Mn en Ultisoles, Inceptisoles, Vertisoles y Andisoles de Costa Rica, con la solución extractora Mehlich 3. Los niveles críticos en los Ultisoles para Ca, Mg y K fueron 4,0, 0,8 y 0,2 cmol(+ l-1, respectivamente, y para P, S, Cu, Mn y Zn 3,0, 36,0, 0,4, 4,0 y 1,5 mg l-1, respectivamente. En los Inceptisoles se encontró 3,1, 1,1 y 0,2 cmol(+ l-1 para el Ca, Mg y K, y 6,0, 32,0, 0,4, 4,0 y 1,7 mg l-1 para P, S, Cu, Mn y Zn. En los Vertisoles los valores correspondieron a 27,0, 13,0 y 0,27 cmol(+ l-1 para Ca, Mg y K, y 13,0, 32,0, 0,4, 4,0 y 3,0 mg l-1 para P, S, Cu, Mn y Zn. En los Andisoles se encontraron valores para Ca, Mg y K de 5,0, 0,75 y 0,22 cmol(+ l-1, y para P, S, Cu, Mn y Zn de 16,0, 31,0, 0,4, 4,0 y 2,5 mg l-1. Cuando se analizaron todos los suelos en conjunto se obtuvo niveles críticos de 5,0, 0,7 y 0,17 cmol(+ l-1 para Ca, Mg y K, y de 10,0, 31,0, 0,4, 4,0 y 2,0 mg l-1 para P, S, Cu, Mn y Zn.

Synthesis, structure, magnetic, electrical and electrochemical properties of Al, Cu and Mg doped MnO{sub 2}

Energy Technology Data Exchange (ETDEWEB)

Hashem, Ahmed M., E-mail: ahmedh242@yahoo.com [National Research Centre, Inorganic Chemistry Department, Behoes St., Dokki, Cairo (Egypt); Institute for Complex Materials, IFW Dresden, Helmholtzstr. 20, D-01069 Dresden (Germany); Abuzeid, Hanaa M. [National Research Centre, Inorganic Chemistry Department, Behoes St., Dokki, Cairo (Egypt); Narayanan, N. [Institute for Complex Materials, IFW Dresden, Helmholtzstr. 20, D-01069 Dresden (Germany); Ehrenberg, Helmut [Institute for Complex Materials, IFW Dresden, Helmholtzstr. 20, D-01069 Dresden (Germany); Materials Science, Technische Universitaet Darmstadt, Petersenstr. 23, D-64287 Darmstadt (Germany); Julien, C.M. [Universite Pierre et Marie Curie, Physicochimie des Electrolytes, Colloides et Sciences Analytiques (PECSA), 4 place Jussieu, 75005 Paris (France)

2011-10-17

Highlights: {yields} Al, Mg and Cu doped MnO{sub 2} as cathode in Li-ion batteries. {yields} Pure phase MnO{sub 2} for virgin and doped MnO{sub 2} were obtained. {yields} Doping elements improve the electrical conductivity of MnO{sub 2}. {yields} Electrochemical behaviour of MnO{sub 2} improved after doping by Al, Mg and Cu. - Abstract: Pure and doped manganese dioxides were prepared by wet-chemical method using fumaric acid and potassium permanganate as raw materials. X-ray diffraction patterns show that pure and Al, Cu and Mg doped manganese dioxides (d-MnO{sub 2}) crystallized in the cryptomelane-MnO{sub 2} structure. Thermal analysis show that, with the assistance of potassium ions inside the 2 x 2 tunnel, the presence of Al, Cu and Mg doping elements increases the thermal stability of d-MnO{sub 2}. The electrical conductivity of d-MnO{sub 2} increases in comparison with pure MnO{sub 2}, while Al-doped MnO{sub 2} exhibits the lower resistivity. As shown in the magnetic measurements, the value of the experimental effective magnetic moment of Mn ions decreases with introduction of dopants, which is attributed to the presence of a mixed valency of high-spin state Mn{sup 4+}/Mn{sup 3+}. Doped MnO{sub 2} materials show good capacity retention in comparison with virgin MnO{sub 2}. Al-doped MnO{sub 2} shows the best electrochemical results in terms of capacity retention and recharge efficiency.

The geochemical profile of Mn, Co, Cu and Fe in Kerteh Mangrove Forest, Terengganu

International Nuclear Information System (INIS)

Kamaruzzaman, B.Y.; Antotina, A.; Airiza, Z.; Syalindran, S.; Ong, M.C.

2007-01-01

The geochemical profile of Kerteh mangrove sediments was analyzed for the vertical and horizontal distribution. The 100 cm core sediment sample and 15 surface sediments samples were taken from the field. The geochemical elements of Mn, Co, Cu and Fe of the sediments were analyzed. Geochemical proxy of Mn, Co, Cu and Fe were analyzed by using Inductively Coupled Plasma-Mass Spectrometry (ICP-MS). The mean concentrations of Mn, Co, Cu and Fe for the vertical distribution were 210.18 μg/ g, 15.55 μg/ g, 43.65 μg/ g and 1.88 μg/ g respectively. on the other hand, the mean concentrations of the geochemical elements for horizontal distributions were 230.50 μg/ g for Mn, 17.57 μg/ g for Co, 43.381 μg/ g for Cu and 2.93 μg/ g for Fe. Enrichment factor and normalization was used to point out the level of pollution. The EF and the normalization indicated that all the geochemical elements were from the natural sources. (author)

Alloying effect on hardening of martensite stainless steels of the Fe-Cr-Ni and Fe-Cr-Co systems

International Nuclear Information System (INIS)

Fel'dgandler, Eh.G.; Savkina, L.Ya.

1975-01-01

The effect of alloying elements is considered on the γ → a-transformation and hardening of certain compositions of the ternary Fe-Cr-Ni- and Fe-Cr-Co alloy systems with the martensite structure. In martensite Fe-(10 to 14)% Cr base steels the elements Co, Cu, W, Ni, Mo, Si, Cr decrease, Mn, Si, Mo, Cu increase, and Cr, Ni, Co decrease the temperature of α → γ-transition. The tempering of martensite steels of the Fe-Cr-Ni- and Fe-Cr-Co-systems containing 10 to 14% Cr, 4 to 9% Ni, and 7 to 12% Co does not lead to hardening. Alloyage of the martensite Fe-Cr-Ni-, Fe-Cr-Co- and Fe-Cr-Ni-Co base separately with Mo, W, Si or Cu leads to a hardening during tempering, the hardening being the higher, the higher is the content of Ni and, especially, of Co. The increase in the content of Mo or Si produces the same effect as the increase in the Co content. In on Fe-Cr-Co or Fe-Cr-Ni-Co based steels alloyed with Mo or Si, two temperature ranges of ageing have been revealed which, evidently, have different hardening natures. The compositions studied could serve as the base material for producing maraging stainless steels having a complex variety of properties

A novel coping metal material CoCrCu alloy fabricated by selective laser melting with antimicrobial and antibiofilm properties

Energy Technology Data Exchange (ETDEWEB)

Ren, Ling [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016 (China); Memarzadeh, Kaveh [Institute of Dentistry, Barts and The London School of Medicine & Dentistry, Queen Mary University of London, Newark Street, London E1 2AT (United Kingdom); Zhang, Shuyuan; Sun, Ziqing; Yang, Chunguang [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016 (China); Ren, Guogang [University of Hertfordshire, Hatfield AL10 9AB (United Kingdom); Allaker, Robert P., E-mail: r.p.allaker@qmul.ac.uk [Institute of Dentistry, Barts and The London School of Medicine & Dentistry, Queen Mary University of London, Newark Street, London E1 2AT (United Kingdom); Yang, Ke, E-mail: kyang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang 110016 (China)

2016-10-01

Objective: The aim of this study was to fabricate a novel coping metal CoCrCu alloy using a selective laser melting (SLM) technique with antimicrobial and antibiofilm activities and to investigate its microstructure, mechanical properties, corrosion resistance and biocompatibility. Methods: Novel CoCrCu alloy was fabricated using SLM from a mixture of commercial CoCr based alloy and elemental Cu powders. SLM CoCr without Cu served as control. Antibacterial activity was analyzed using standard antimicrobial tests, and antibiofilm properties were investigated using confocal laser scanning microscope. Cu distribution and microstructure were determined using scanning electron microscope, optical microscopy and X-ray diffraction. Corrosion resistance was evaluated by potential dynamic polarization and biocompatibility measured using an MTT assay. Results: SLM CoCrCu alloys were found to be bactericidal and able to inhibit biofilm formation. Other factors such as microstructure, mechanical properties, corrosion resistance and biocompatibility were similar to those of SLM CoCr alloys. Significance: The addition of appropriate amounts of Cu not only maintains normal beneficial properties of CoCr based alloys, but also provides SLM CoCrCu alloys with excellent antibacterial and antibiofilm capabilities. This material has the potential to be used as a coping metal for dental applications. - Highlights: • Novel CoCrCu alloys were fabricated by using selective laser melting (SLM). • SLM CoCrCu alloys showed satisfied antimicrobial and antibiofilm activities. • SLM CoCrCu alloys have no cytotoxic effect on normal cells. • Other properties of SLM CoCrCu alloys were similar to SLM CoCr alloys. • SLM CoCrCu alloys have the potential to be used as coping metals.

A novel coping metal material CoCrCu alloy fabricated by selective laser melting with antimicrobial and antibiofilm properties

International Nuclear Information System (INIS)

Ren, Ling; Memarzadeh, Kaveh; Zhang, Shuyuan; Sun, Ziqing; Yang, Chunguang; Ren, Guogang; Allaker, Robert P.; Yang, Ke

2016-01-01

Objective: The aim of this study was to fabricate a novel coping metal CoCrCu alloy using a selective laser melting (SLM) technique with antimicrobial and antibiofilm activities and to investigate its microstructure, mechanical properties, corrosion resistance and biocompatibility. Methods: Novel CoCrCu alloy was fabricated using SLM from a mixture of commercial CoCr based alloy and elemental Cu powders. SLM CoCr without Cu served as control. Antibacterial activity was analyzed using standard antimicrobial tests, and antibiofilm properties were investigated using confocal laser scanning microscope. Cu distribution and microstructure were determined using scanning electron microscope, optical microscopy and X-ray diffraction. Corrosion resistance was evaluated by potential dynamic polarization and biocompatibility measured using an MTT assay. Results: SLM CoCrCu alloys were found to be bactericidal and able to inhibit biofilm formation. Other factors such as microstructure, mechanical properties, corrosion resistance and biocompatibility were similar to those of SLM CoCr alloys. Significance: The addition of appropriate amounts of Cu not only maintains normal beneficial properties of CoCr based alloys, but also provides SLM CoCrCu alloys with excellent antibacterial and antibiofilm capabilities. This material has the potential to be used as a coping metal for dental applications. - Highlights: • Novel CoCrCu alloys were fabricated by using selective laser melting (SLM). • SLM CoCrCu alloys showed satisfied antimicrobial and antibiofilm activities. • SLM CoCrCu alloys have no cytotoxic effect on normal cells. • Other properties of SLM CoCrCu alloys were similar to SLM CoCr alloys. • SLM CoCrCu alloys have the potential to be used as coping metals.

Magnetic refrigeration capabilities of magnetocaloric Ni2Mn:75Cu:25Ga

Science.gov (United States)

Mishra, S. K.; Jenkins, C. A.; Dubenko, I.; Samanta, T.; Ali, N.; Roy, S.

2013-03-01

Doping-driven competition between energetically similar ground states leads to many exciting materials phenomena such as the emergence of high-Tc superconductivity, diluted magnetic semiconductors, and colossal magnetoresistance. Doped Ni2MnGa Heusler alloy, which is a multifunctional ferromagnetic alloy with various exotic physical properties demonstrates this notion of rich phenomenology via modified ground spin states. Adopting this generic concept, here we will present a novel doped Ni2Mn.75Cu.25Ga alloy that offers unprecedented co-existence of the magnetocaloric effect and fully controlled ferromagnetism at room temperature. Application of site engineering enables us to manipulate the ground spin state that leads to the decrease in magnetic transition temperature and also increases the delocalization of the Mn magnetism. SQUID magnetometery suggests that Cu doping enhances the saturation magnetization, coercive field and clarity of magnetic hysteresis loops. By exploiting x-ray absorption techniques and measuring element specific magnetic hysteresis loops, here we will describe the microscopic origin of enhnaced magnetocaloric properties and d-d interaction driven charge transfer effects in Ni2Mn.75Cu.25Ga This work was supported by DOE Grant No. DE-FG02-06ER46291

Phenomenological approach to the spin glass state of (Cu-Mn, Ag-Mn, Au-Mn and Au-Fe) alloys at low temperatures

International Nuclear Information System (INIS)

Al-Jalali, Muhammad A.; Kayali, Fawaz A.

2000-01-01

Full text.The spin glass of: (Cu-Mn, Ag-Mn, Au-Mn, Au-Fe) alloys has been extensively studied. The availability of published and assured experimental data on the susceptibility x(T) of this alloys has enabled the design and application of phenomenological approach to the spin glass state of these interesting alloys. The use of and advanced (S.P.S.S) computer software has resulted revealing some important features of the spin glass in these alloys, the most important of which is that the spin glass state do not represent as phase change

Layered B-site cation ordering: A key factor in ferrimagnetism of Y{sub 2}MnCrO{sub 6}

Energy Technology Data Exchange (ETDEWEB)

Hao, Lin [Department of Physics, University of Science and Technology of China, Hefei, Anhui (China); Yang, Lei [Collaborative Innovation Center for Magnetoelectric Industry, China Three Gorges University, Yichang, Hubei (China); Lee, Ming-Hsien; Lin, Tseh-Hsing [Department of Physics, Tamkang University, Taipei, Taiwan (China); Zhang, ZhongFeng; Xie, XiangNan [Department of Physics, University of Science and Technology of China, Hefei, Anhui (China); Zhu, Hong, E-mail: zhuh@ustc.edu.cn [Department of Physics, University of Science and Technology of China, Hefei, Anhui (China)

2014-07-15

Highlights: • Rietveld refinement and first-principles calculations are performed for Y{sub 2}MnCrO{sub 6}. • The layered B-site cation ordering is a more reliable structure for Y{sub 2}MnCrO{sub 6}. • Y{sub 2}MnCrO{sub 6} has an insulating ferrimagnetism (0 0 1)-ordered ground state. • The layered ordered pattern plays a key role for the ferrimagnetism in Y{sub 2}MnCrO{sub 6}. - Abstract: We report the Rietveld refinement of powder X-ray diffraction (XRD) pattern and first-principles calculations for the half-Cr{sup 3+} doped YMnO{sub 3} compound. The Rietveld refinement results suggest that the compound has a monoclinic structure with the Mn{sup 3+}/Cr{sup 3+} layers alternately stacking along the [0 0 1] direction. The first-principles calculations show that the structure with layered B-site cation ordering has the lowest total energy; meanwhile, the insulating ferrimagnetic state is more favored compared to the ferromagnetic state, which is in agreement with the reported experimental results. Based upon Goodenough’s model of semi-covalent exchange, we argue that the anisotropic magnetic couplings between the Mn{sup 3+}/Cr{sup 3+} cations ordered in layered pattern play an important role for the ferrimagnetism in the compound.

The synthetic evaluation of CuO-MnOx-modified pinecone biochar for simultaneous removal formaldehyde and elemental mercury from simulated flue gas.

Science.gov (United States)

Yi, Yaoyao; Li, Caiting; Zhao, Lingkui; Du, Xueyu; Gao, Lei; Chen, Jiaqiang; Zhai, Yunbo; Zeng, Guangming

2018-02-01

A series of low-cost Cu-Mn-mixed oxides supported on biochar (CuMn/HBC) synthesized by an impregnation method were applied to study the simultaneous removal of formaldehyde (HCHO) and elemental mercury (Hg 0 ) at 100-300° C from simulated flue gas. The metal loading value, Cu/Mn molar ratio, flue gas components, reaction mechanism, and interrelationship between HCHO removal and Hg 0 removal were also investigated. Results suggested that 12%CuMn/HBC showed the highest removal efficiency of HCHO and Hg 0 at 175° C corresponding to 89%and 83%, respectively. The addition of NO and SO 2 exhibited inhibitive influence on HCHO removal. For the removal of Hg 0 , NO showed slightly positive influence and SO 2 had an inhibitive effect. Meanwhile, O 2 had positive impact on the removal of HCHO and Hg 0 . The samples were characterized by SEM, XRD, BET, XPS, ICP-AES, FTIR, and H 2 -TPR. The sample characterization illustrated that CuMn/HBC possessed the high pore volume and specific surface area. The chemisorbed oxygen (O β ) and the lattice oxygen (O α ) which took part in the removal reaction largely existed in CuMn/HBC. What is more, MnO 2 and CuO (or Cu 2 O) were highly dispersed on the CuMn/HBC surface. The strong synergistic effect between Cu-Mn mixed oxides was critical to the removal reaction of HCHO and Hg 0 via the redox equilibrium of Mn 4+ + Cu + ↔ Mn 3+ + Cu 2+ .

Half-metallic antiferromagnetism in double perovskite BiPbCrCuO6

International Nuclear Information System (INIS)

Weng, Ke-Chuan; Wang, Y. K.

2015-01-01

The electronic structure and magnetic properties of BiPbCrCuO 6 double perovskite are investigated based on first-principles density functional calculations with generalized gradient approximation (GGA) and GGA incorporated with Coulomb correlation interaction U (GGA + U). The results suggest the half-metallic (HM) and antiferromagnetic (AFM) properties of BiPbCrCuO 6 double perovskite. The HM-AFM property of the double perovskite is caused by the double-exchange mechanism between neighboring Cr 5+ (t 2g 1 ↓) and Cu 2+ (t 2g 3 ↑t 2g 3 ↓e g 2 ↑e g ↓) via the intermediate O 2− (2s 2 2p 6 ) ion

V, Cr, and Mn in the Earth, Moon, EPB, and SPB and the origin of the Moon: Experimental studies

International Nuclear Information System (INIS)

Drake, M.J.; Capobianco, C.J.; Newsom, H.E.

1989-01-01

The abundances of V, Cr, and Mn inferred for the mantles of the Earth and Moon decrease in that order and are similar, but are distinct from those inferred for the mantles of the Eucrite Parent Body (EPB) and Shergottite Parent Body (SPB). This similarity between Earth and Moon has been used to suggest that the Moon is derived substantially or entirely from Earth mantle material following terrestrial core formation. To test this hypothesis, the authors have determined the partitioning of V, Cr, and Mn between solid iron metal, S-rich metallic liquid, and synthetic basaltic silicate liquid at 1,260 degree C and one bar pressure. The sequence of compatibility in the metallic phases is Cr > V > Mn at high oxygen fugacity and V > Cr > Mn at low oxygen fugacities. Solubilities in liquid metal always exceed solubilities in solid metal. These partition coefficients suggest that the abundances of V, Cr, and Mn do not reflect core formation in the Earth. Rather, they are consistent with the relative volatilities of these elements. The similarity in the depletion patterns of V, Cr, and Mn inferred for the mantles of the Earth and Moon is a necessary, but not sufficient, condition for the Moon to have been derived wholly or in part from the Earth's mantle

Newly developed EMF cell with zirconia solid electrolyte for measurement of low oxygen potentials in liquid Cu-Cr and Cu-Zr alloys

Directory of Open Access Journals (Sweden)

Katayama I.

2012-01-01

Full Text Available In order to measure the very low oxygen potential by use of stabilized zirconia solid electrolyte emf method, a new cell construction was devised. The idea was based on Janke but a zirconia rod was used instead of the zirconia crucible which contacts liquid alloy electrode. The cell was used for determination of the oxygen potentials in liquid dilute Cu-Cr and Cu-Zr alloys. The reference electrode was Cr,Cr2O3. Emf measurements were performed in the temperature range of 1400-1580K and composition range of 0.198-3.10at%Cr-Cu alloys, and 1380-1465K, 0.085-0.761at%Zr-Cu alloys. The composition of liquid alloys were determined by picking up from the liquid alloys and ICP analysis. By use of the newly devised cell construction in this study, stable emf values were obtained at each temperature and alloy composition. Emf values were corrected by using the parameter for electronic contribution of the YSZ. Activity of Cr obeys Henry’s law and activity coefficient at infinitely dilute alloys of Cr in Cu-Cr alloys are: lng0 Cr =(3.80 at 1423K, (3.57 at 1473K, (3.38 at 1523K and (3.20 at 1573K. At 1423 K activity coefficient of Zr at infinitely diluted alloy is lnγo Zr = -4.0.

Giant magnetoresistance in CrFeMn alloys

International Nuclear Information System (INIS)

Xu, W.M.; Zheng, P.; Chen, Z.J.

1997-01-01

The electrical resistance and longitudinal magnetoresistance of Cr 75 (Fe x Mn 1-x ) 25 alloys, x=0.64, 0.72, are studied in the temperature range 1.5-270 K in applied field up to 7.5 T. The magnetoresistance is negative and strongly correlated with the spin reorientation. In the temperature range where the antiferromagnetic and ferromagnetic domains coexist, the samples display giant magnetoresistance which follows a H n -law at high field. (orig.)

Calculation of phase equilibria in Ti-Al-Cr-Mn quaternary system for developing lower cost titanium alloys

International Nuclear Information System (INIS)

Lu, X.G.; Li, C.H.; Chen, L.Y.; Qiu, A.T.; Ding, W.Z.

2011-01-01

Highlights: → This paper is about the concept of designing the lower cost titanium alloy. → The thermodynamic database of Ti-Al-Cr-Mn system is built up by Calphad method. → The pseudobinary sections with Cr: Mn = 3:1 and Al = 3, 4.5 and 6.0 wt% are calculated. → This may provide the theoretical support for designing the lower cost titanium alloy. - Abstract: The Ti-Al-Cr-Mn system is a potentially useful system for lower cost titanium alloy development; however, there are few reports about the experimental phase diagrams and the thermodynamical assessment for this system. In this study, the previous investigations for the thermodynamic descriptions of the sub-systems in the Ti-Al-Cr-Mn system are reviewed, our previous assessment for the related sub-systems in this quaternary system is summarized, the thermodynamical database of this quaternary system is built up by directly extrapolating from all sub-systems assessed by means of the Calphad method, then the pseudobinary sections with Cr:Mn = 3:1 and Al = 0.0, 3.0, 4.5 and 6.0 wt% are calculated, respectively. These pseudobinary phase diagrams may provide the theoretical support for designing the lower cost titanium alloys with different microstructures (α, α + β, and β titanium alloy).

Comparative toxicity of VO3-, CrO42-, Mn2+, Co2+, Ni2+, Cu2+, Zn2+, and Cd2+ to lettuce seedlings

International Nuclear Information System (INIS)

Berry, W.L.

1978-01-01

Lettuce seeds imbibed, germinated, and grown in a 0.1-strength modified Hoagland culture solution were subjected to a series of increasing concentrations of individual heavy metals up to and exceeding lethal levels. After an exposure of 5 days, seedlings were harvested, examined, and measured to determine toxic effects. A log--log plot of root length (yield) vs. heavy metal concentration was made for each metal to produce a dose response curve. The curves showed a growth plateau at low concentrations of the respective metals which was equivalent to the growth of the control. All metals inhibited root growth and caused lethal toxicity in the sub- and low-milliequivalent range. When concentrations of the tested metals exceeded their thresholds of acute toxicity, root growth was inhibited. In the zone of inhibition, between the acute toxic threshold and complete inhibition, the log--log dose response curves were approximately linear or were a series of linear steps. The threshold toxicity and the response slope were characteristic for each metal. Seedling lettuce showed a monophasic response to VO 3 - , Cu 2+ , and Zn 2+ ; a biphasic response to CrO 4 2 -, Mn 2+ , Ni 2+ , and Cd 2+ ; and a quadraphasic response to Co 2+ . The acute toxicity threshold on an equivalent basis increased according to the following sequence: Cd 2+ much less than VO 3 - 2+ 2+ 2+ 4 2- 2+ much less than Mn 2+ . On this basis, Cd 2+ is the most toxic of the trace elements tested

Microstructure and corrosion properties of CrMnFeCoNi high entropy alloy coating

Energy Technology Data Exchange (ETDEWEB)

Ye, Qingfeng [Shanghai Key laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, 200240 (China); Feng, Kai, E-mail: fengkai@sjtu.edu.cn [Shanghai Key laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, 200240 (China); Li, Zhuguo, E-mail: lizg@sjtu.edu.cn [Shanghai Key laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, 200240 (China); Lu, Fenggui [Shanghai Key laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, 200240 (China); Li, Ruifeng [School of Materials Science and Engineering, Jiangsu University of Science and Technology, Zhenjiang, Jiangsu, 212003 (China); Huang, Jian; Wu, Yixiong [Shanghai Key laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai 200240 (China); Collaborative Innovation Center for Advanced Ship and Deep-Sea Exploration, Shanghai, 200240 (China)

2017-02-28

Highlights: • Equimolar CrMnFeCoNi high entropy alloy coating are prepared by laser cladding. • The cladding layer forms a simple FCC phase solid solution with identical dendritic structure. • The cladding layer exhibits a noble corrosion resistance in both 3.5 wt.% NaCl and 0.5 M sulfuric acid. • Element segregation makes Cr-depleted interdendrites the starting point of corrosion reaction. - Abstract: Equimolar CrMnFeCoNi high entropy alloy (HEA) is one of the most notable single phase multi-component alloys up-to-date with promising mechanical properties at cryogenic temperatures. However, the study on the corrosion behavior of CrMnFeCoNi HEA coating has still been lacking. In this paper, HEA coating with a nominal composition of CrMnFeCoNi is fabricated by laser surface alloying and studied in detail. Microstructure and chemical composition are determined by X-ray diffraction (XRD), optical microscope (OM), scanning electron microscope (SEM) and energy dispersive spectrometer (EDS). Potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) are used to investigate the corrosion behavior. The coating forms a simple FCC phase with an identical dendritic structure composed of Fe/Co/Ni-rich dendrites and Mn/Ni-rich interdendrites. Both in 3.5 wt.% NaCl solution and 0.5 M sulfuric acid the coating exhibits nobler corrosion resistance than A36 steel substrate and even lower i{sub corr} than 304 stainless steel (304SS). EIS plots coupled with fitted parameters reveal that a spontaneous protective film is formed and developed during immersion in 0.5 M sulfuric acid. The fitted R{sub t} value reaches its maximum at 24 h during a 48 h’ immersion test, indicating the passive film starts to break down after that. EDS analysis conducted on a corroded surface immersed in 0.5 M H{sub 2}SO{sub 4} reveals that corrosion starts from Cr-depleted interdendrites.

N–Mg dual-acceptor co-doping in CuCrO{sub 2} studied by first-principles calculations

Energy Technology Data Exchange (ETDEWEB)

Xu, Ying, E-mail: 1080071@hnust.edu.cn [School of Physics, Hunan University of Science and Technology, Xiangtan 411201 (China); Nie, Guo-Zheng [School of Physics, Hunan University of Science and Technology, Xiangtan 411201 (China); Zou, Daifeng [School of Physics, Hunan University of Science and Technology, Xiangtan 411201 (China); Shenzhen Key Laboratory of Nanobiomechanics, Shenzhen Institutes of Advanced Technology, Chinese Academy of Science, Shenzhen 518055 (China); Tang, Jing-Wu [School of Physics, Hunan University of Science and Technology, Xiangtan 411201 (China); Ao, Zhimin, E-mail: Zhimin.Ao@gdut.edu.cn [Institute of Environmental Health and Pollution Control, School of Environmental Science and Engineering, Guangdong University of Technology, Guangzhou 510006 (China)

2016-11-25

In this paper, N–Mg dual-acceptor co-doping in CuCrO{sub 2} is investigated by first-principles calculations. The electronic structure and formation energies of Mg substituting Cr-site, N substituting O-site, and co-doping of both Mg on Cr-site and N on O-site in CuCrO{sub 2} are calculated. It is found that the structure with N and Mg codoped at the nearest sites has the lowest energy due to a modest attractive interaction between the two dopants. Compared with single N or Mg doped CuCrO{sub 2}, the N–Mg codoped CuCrO{sub 2} has a lower formation energy and shallower transition level. In addition, the total density of states (DOS) analysis shows that more hole states appear above the Fermi level and higher DOS for N–Mg co-doping is obtained in the N–Mg codoped CuCrO{sub 2}, which is good to enhance the p-type conductivity in CuCrO{sub 2}. - Highlights: • N–Mg dual-acceptor co-doping in CuCrO{sub 2} is investigated. • N–Mg complex has a lower formation energy and shallower transition level. • More hole states appear above the Fermi level for N–Mg co-doping. • N–Mg co-doping in CuCrO{sub 2} can be expected to have more stable p-type conductivity.

Immunoreactive Cu-SOD and Mn-SOD in lymphocytes sub-populations from normal and trisomy 21 subjects according to age

International Nuclear Information System (INIS)

Baeteman, M.A.; Baret, A.; Courtiere, A.; Rebuffel, P.; Mattei, J.F.

1983-01-01

Copper and manganese superoxide dismutases (Cu-SOD and Mn-SOD) were measured by radioimmunoassay in B and T lymphocytes and macrophages, in patients with trisomy 21 and in matched controls. In the controls, Cu-SOD was present in greater amounts than Mn-SOD and there were quantitative differences in the distribution in the three cellular sub-populations. In trisomy 21, levels of Cu-SOD were raised, with no change in levels of Mn-SOD, supporting the theory of a gene dosage effect. There were significant positive and negative correlations between age and Cu-SOD levels in controls, and a correlation approaching significance for Mn-SOD. In trisomy 21, there was no correlation between age and Cu-SOD levels, and the only significant correlation for Mn-SOD was for B lymphocytes

Order–disorder phenomena in layered CuCrSe2 crystals

International Nuclear Information System (INIS)

Gagor, A.; Gnida, D.; Pietraszko, A.

2014-01-01

The thermal motion of Cu + ions in a quasi-two dimensional copper ion conductor CuCrSe 2 is studied in the vicinity of the order-disorder phase transition to superionic phase, basing on a single-crystal and powder X-ray diffraction, specific heat and electrical resistivity measurements. The copper ions gradually migrate with temperature decrease to empty tetrahedral sites reaching occupancy equilibrium in the disordered high-temperature phase at T s  = 365 K. The copper migration between Cuα and Cuβ tetrahedral sites occurs through the neighboring, face-sharing octahedral holes. Disorder of Cu + ions brings perturbations in periodic potential of the crystal lattice providing additional scattering centers for electrons. - Graphical abstract: Copper migration within α and β sites. - Highlights: • Single crystals of CuCrSe 2 have been grown by vapor transport. • Thermally activated motion of Cu + ions is analyzed from T = 295 up to 420 K. • An order–disorder phase transition at T s  = 365 K leads to fast ion conducting state. • Interplay between lattice vibrations and Se polarizability accounts for Cu + hops. • Electrical resistivity near the T s shows two additional scattering centers

Cyclic Oxidation Behavior of CuCrAl Cold-Sprayed Coatings for Reusable Launch Vehicles

Science.gov (United States)

Raj, Sai; Karthikeyan, J.

2009-01-01

The next generation of reusable launch vehicles is likely to use GRCop-84 [Cu-8(at.%)Cr-4%Nb] copper alloy combustion liners. The application of protective coatings on GRCop-84 liners can minimize or eliminate many of the environmental problems experienced by uncoated liners and significantly extend their operational lives and lower operational cost. A newly developed Cu- 23 (wt.%) Cr-5% Al (CuCrAl) coating, shown to resist hydrogen attack and oxidation in an as-cast form, is currently being considered as a protective coating for GRCop-84. The coating was deposited on GRCop-84 substrates by the cold spray deposition technique, where the CuCrAl was procured as gas-atomized powders. Cyclic oxidation tests were conducted between 773 and 1,073 K to characterize the coated substrates.

Effect of pH on corrosion behavior of CuCrZr in solution without and with NaCl

Energy Technology Data Exchange (ETDEWEB)

Kwok, C.T.; Wong, P.K. [Department of Electromechanical Engineering, University of Macau (China); Man, H.C. [Department of Industrial and Systems Engineering, Hong Kong Polytechnic University (Hong Kong); Cheng, F.T., E-mail: apaftche@polyu.edu.h [Department of Applied Physics, Hong Kong Polytechnic University (Hong Kong)

2009-10-01

CuCrZr is a high copper alloy widely used as electrical and thermal conducting material, especially in heat exchangers in nuclear reactors. In this respect, the physical and fatigue properties of CuCrZr have been extensively studied. The electrochemical behavior of CuCrZr, on the other hand, has not been adequately investigated. In the present study, the effect of pH on the corrosion behavior of CuCrZr in aqueous solutions without and with chloride (0.6 M NaCl) was studied. The pH of the solutions is found to exert significant influence on the corrosion behavior of CuCrZr. In acidic solutions without chloride, the corrosion of CuCrZr is ascribed to active dissolution with soluble products. In neutral and alkaline solutions without NaCl, the presence of oxides on the surface of CuCrZr leads to a noble shift in corrosion potential and passivation results in increased corrosion resistance. In chloride solutions at various pH values, the chloride ions influence the formation of the surface layers and the anodic dissolution process during polarization. At high pH, CuCrZr shows significant passivity and high corrosion resistance due to the growth of Cu{sub 2}O/Cu(OH) film which hinders further dissolution whereas at low pH the corrosion resistance is lowered due to active dissolution of Cu.

Effect of pH on corrosion behavior of CuCrZr in solution without and with NaCl

International Nuclear Information System (INIS)

Kwok, C.T.; Wong, P.K.; Man, H.C.; Cheng, F.T.

2009-01-01

CuCrZr is a high copper alloy widely used as electrical and thermal conducting material, especially in heat exchangers in nuclear reactors. In this respect, the physical and fatigue properties of CuCrZr have been extensively studied. The electrochemical behavior of CuCrZr, on the other hand, has not been adequately investigated. In the present study, the effect of pH on the corrosion behavior of CuCrZr in aqueous solutions without and with chloride (0.6 M NaCl) was studied. The pH of the solutions is found to exert significant influence on the corrosion behavior of CuCrZr. In acidic solutions without chloride, the corrosion of CuCrZr is ascribed to active dissolution with soluble products. In neutral and alkaline solutions without NaCl, the presence of oxides on the surface of CuCrZr leads to a noble shift in corrosion potential and passivation results in increased corrosion resistance. In chloride solutions at various pH values, the chloride ions influence the formation of the surface layers and the anodic dissolution process during polarization. At high pH, CuCrZr shows significant passivity and high corrosion resistance due to the growth of Cu 2 O/Cu(OH) film which hinders further dissolution whereas at low pH the corrosion resistance is lowered due to active dissolution of Cu.

Teores de Fe, Mn, Zn, Cu, Ni E Co em solos de referência de Pernambuco Concentrations of Fe, Mn, Zn, Cu, Ni and Co in benchmark soils of Pernambuco, Brazil

Directory of Open Access Journals (Sweden)

Caroline Miranda Biondi

2011-06-01

Full Text Available Metais pesados formam um grupo de elementos com particularidades relevantes e de ocorrência natural no ambiente, como elementos acessórios na constituição de rochas. Esses elementos, apesar de associados à toxidez, exigem tratamento diferenciado em relação aos xenobióticos, uma vez que diversos metais possuem essencialidade (Fe, Mn, Cu, Zn e Ni e benefício (Co comprovados para as plantas. Nesse contexto, o objetivo deste trabalho foi determinar os teores naturais dos metais Fe, Mn, Zn, Ni, Cu e Co nos solos de referência de Pernambuco. Foram coletadas amostras de solo nas três regiões fisiográficas (Zona da Mata, Agreste e Sertão, dos dois primeiros horizontes dos 35 solos de referência do Estado de Pernambuco. A digestão das amostras baseou-se no método 3051A (USEPA, 1998, e a determinação foi efetuada em ICP-OES. Correlações significativas foram estabelecidas entre os metais e entre estes e a fração argila do solo, em ambos os horizontes, indicando a associação comum da maioria dos metais com solos mais argilosos. A maioria dos solos apresentou teores de Fe, Mn, Zn, Cu, Ni e Co menores que os de solos de outras regiões do País, com litologia mais máfica, o que corrobora o fato de que os teores desses elementos são mais diretamente relacionados aos minerais Fe-magnesianos. Os resultados indicam baixo potencial dos solos de Pernambuco em liberar Cu, Co e Ni para plantas, enquanto deficiências de Zn, Fe e Mn são menos prováveis. Os teores naturais de Fe, Mn, Zn, Cu, Ni e Co determinados podem ser utilizados como base para definição dos Valores de Referência de Qualidade para os solos de Pernambuco, de acordo com o preconizado pela legislação nacional.Heavy metals are a group of elements with specific features and natural occurrence in the environment, representing an accessory in the formation of rocks. These elements, although associated with toxicity, must be treated different from xenobiotics, since many

Magnetic properties of the CrMnFeCoNi high-entropy alloy

International Nuclear Information System (INIS)

Schneeweiss, Oldřich; Friák, Martin; Masaryk University, Brno; Dudová, Marie; Holec, David

2017-01-01

In this paper, we present experimental data showing that the equiatomic CrMnFeCoNi high-entropy alloy undergoes two magnetic transformations at temperatures below 100 K while maintaining its fcc structure down to 3 K. The first transition, paramagnetic to spin glass, was detected at 93 K and the second transition of the ferromagnetic type occurred at 38 K. Field-assisted cooling below 38 K resulted in a systematic vertical shift of the hysteresis curves. Strength and direction of the associated magnetization bias was proportional to the strength and direction of the cooling field and shows a linear dependence with a slope of 0.006 ± 0.001 emu T. The local magnetic moments of individual atoms in the CrMnFeCoNi quinary fcc random solid solution were investigated by ab initio (electronic density functional theory) calculations. Results of the numerical analysis suggest that, irrespective of the initial configuration of local magnetic moments, the magnetic moments associated with Cr atoms align antiferromagnetically with respect to a cumulative magnetic moment of their first coordination shell. The ab initio calculations further showed that the magnetic moments of Fe and Mn atoms remain strong (between 1.5 and 2 μ B ), while the local moments of Ni atoms effectively vanish. Finally, these results indicate that interactions of Mn- and/or Fe-located moments with the surrounding magnetic structure account for the observed macroscopic magnetization bias.

Enhancement strategies for Cu(II), Cr(III) and Cr(VI) remediation by a variety of seaweed species.

Science.gov (United States)

Murphy, V; Hughes, H; McLoughlin, P

2009-07-15

Various chemical treatments have been applied to six brown, red and green seaweed species with a view to enhancing their metal removal for Cu(II), Cr(III) and Cr(VI). Treatment with acetone resulted in the greatest enhancement for both cationic and anionic species with relatively low mass losses (15-35%), indicating its low risk to biomass operational stability. Cation binding was increased by 69%, while the total Cr removal was augmented by 15%. Cr(VI) binding was shown to be an adsorption-coupled reduction, whereby Cr(VI) was bound to the biomass surface at pH 2 and subsequently reduced to Cr(III). Acetone treatment also resulted in biomasses that were capable of converting up to 83% of Cr(VI) in solution to Cr(III). Blocking of carboxyl and amino functionalities had significant negative effects both on total Cr removal as well as percentage conversion of Cr(VI) to Cr(III). Results therefore indicated the significant role played by these moieties in metal binding to these seaweeds. Potentiometric titrations displayed agreement between the degree of esterification and the decrease in Cu(II) removal for Ulva spp. and Polysiphonia lanosa. FTIR analysis identified changes in biomass functionality and availability after chemical modification, the results of which were in agreement with metal removal studies. In conclusion, these biosorbents represent suitable candidates to replace conventional removal technologies for metal bearing wastewaters, in particular for the detoxification of hazardous Cr(VI) waste streams.

Ab initio electronic structure calculations for Mn linear chains deposited on CuN/Cu(001) surfaces

International Nuclear Information System (INIS)

Barral, Maria Andrea; Weht, Ruben; Lozano, Gustavo; Maria Llois, Ana

2007-01-01

In a recent experiment, scanning tunneling microscopy has been used to obtain a direct probe of the magnetic interaction in linear manganese chains arranged by atomic manipulation on thin insulating copper nitride islands grown on Cu(001). The local spin excitation spectra of these chains have been measured with inelastic electron tunneling spectroscopy. Analyzing the spectroscopic results with a Heisenberg Hamiltonian the interatomic coupling strength within the chains has been obtained. It has been found that the coupling strength depends on the deposition sites of the Mn atoms on the islands. In this contribution, we perform ab initio calculations for different arrangements of infinite Mn chains on CuN in order to understand the influence of the environment on the value of the magnetic interactions

Effect of Cr-sources on performance of Li1.05Cr0.04Mn1.96O4 cathode materials prepared by slurry spray drying method

International Nuclear Information System (INIS)

Peng, Z.D.; Jiang, Q.L.; Du, K.; Wang, W.G.; Hu, G.R.; Liu, Y.X.

2010-01-01

The effect of Cr-sources on the performance of Li 1.05 Cr 0.04 Mn 1.96 O 4 prepared by slurry spray drying method was studied by adopting three different chromic compounds, Cr 2 O 3 , Cr 2 (SO 4 ) 3 and Cr(CH 3 COO) 3 , respectively. The prepared powder materials were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), scanning electron microscopy (SEM), laser particle size analyzer and Brunauer-Emmett-Teller (BET) specific surface area test. Electrochemical performances of these cathode materials were investigated by electrochemical impedance spectroscopy (EIS) and charge-discharge tests with Li/LiCr x Mn 2-x O 4 coin-type batteries. The results indicate that porous spherical particles with average particle size of about 24 μm can be obtained by slurry spray drying process. Using Cr(CH 3 COO) 3 as Cr-source resulted in the better mixing properties, which can make the as-prepared CA-Li 1.05 Cr 0.04 Mn 1.96 O 4 having smaller lattice parameter, smaller grain size and better structure stability, and consequently the obtained sample showed low charge transfer impedance and electrochemical polarization, and exhibited good electrochemical performance at elevated temperature.

Gd3+-ESR and magnetic susceptibility of GdCu4Al8 and GdMn4Al8

International Nuclear Information System (INIS)

Coldea, R.; Coldea, M.; Pop, I.

1994-01-01

Gd ESR of GdCu 4 Al 8 and GdMn 4 Al 8 and magnetic susceptibility of GdCu 4 Al 8 , GdMn 4 Al 8 , and YMn 4 Al 8 were measured in the temperature range of 290K--460K and 90K--1050K, respectively. The occurrence of the Mn moment in YMn 4 Al 8 and GdMn 4 Al 8 is strongly correlated with the critical value of d∼2.6 angstrom of the Mn-Mn distance below which the Mn moment is not stable. The experimental data for GdMn 4 Al 8 , compared with the data for the isostructural compounds GdCu 4 Al 8 and YMn 4 Al 8 , show that near the critical value of d, the existence of Mn moment depends not only on the value of d, but also on the local magnetic surroundings. It has been revealed that the magnetic character of Mn moment in YMn 4 Al 8 and GdMn 4 Al 8 changes from an itinerant electron type to a local-moment type with increasing temperature

Structural, optical, dielectric and magnetic studies of gadolinium-added Mn-Cu nanoferrites

Science.gov (United States)

Kanna, R. Rajesh; Lenin, N.; Sakthipandi, K.; Kumar, A. Senthil

2018-05-01

Spinel ferrite with the general formula Mn1-xCuxFe1.85Gd0.15O4 (x = 0.2, 0.4, 0.6 and 0.8) was synthesized using the standard sonochemical method. The structure, optical, morphology, dielectric and magnetic properties of the prepared Mn1-xCuxFe1.85Gd0.15O4 nanoferrites were exhaustively investigated using various characterization techniques. The phase purity, secondary phase and crystallite parameters were studied from X-ray diffraction patterns. Fourier transform infrared spectra showed two absorption bands of transition metal oxides in the frequency range from 400 to 650 cm-1, which are related to asymmetric stretching modes of the spinel ferrites (AB2O4). Raman spectra have five active modes illustrating the vibration of O2- ions at both tetrahedral (A) site and octahedral (B) site ions. The wide and narrow scan spectrum from X-ray photoelectron spectroscopy results confirmed the presence of Mn, Cu, Gd, Fe, C and O elements in the composition. The oxidation state and core level of the photo electron peaks of Mn 2p, Cu 2p, Gd 3d, Fe 2p and O 1s were analyzed. The influence of the Cu2+ concentration in Mn1-xCuxFe1.85Gd0.15O4 on the morphology, varying from nanorods, nanoflakes to spherical, was explored on the basis of scanning electron microscopy images. Ultraviolet diffuse reflectance spectroscopy studies indicated that the optical bandgap (5.12-5.32 eV) of the nanoferrites showed an insulating behavior. The dielectric constant, loss tangent and complex dielectric constant values decreased with an increase in frequency with the addition of Gd3+ content. A vibrating sample magnetometer showed that the prepared nanoferrites had a soft ferromagnetic nature. The magnetic parameter changed markedly with an increase in the Cu content in Mn1-xCuxFe1.85Gd0.15O4 nanoferrites. The optical, dielectric and magnetic properties were considerably enhanced with the addition of Gd3+ ions in the spinel nanoferrites.

Spin-resolved photoelectron spectroscopy of Mn{sub 6}Cr single-molecule-magnets and of manganese compounds as reference layers

Energy Technology Data Exchange (ETDEWEB)

Helmstedt, Andreas; Gryzia, Aaron; Dohmeier, Niklas; Mueller, Norbert; Brechling, Armin; Sacher, Marc; Heinzmann, Ulrich [Faculty of Physics, Bielefeld University (Germany); Hoeke, Veronika; Glaser, Thorsten [Faculty of Chemistry, Bielefeld University (Germany); Fonin, Mikhail; Ruediger, Ulrich [Department of Physics, University of Konstanz (Germany); Neumann, Manfred [Department of Physics, Osnabrueck University (Germany)

2011-07-01

The properties of the manganese-based single-molecule-magnet (SMM) Mn{sub 6}Cr are studied. This molecule exhibits a large spin ground state of S{sub T}=21/2. It contains six manganese centres arranged in two bowl-shaped Mn{sub 3}-triplesalen building blocks linked by a hexacyanochromate. The Mn{sub 6}Cr complex can be isolated with different counterions which compensate for its triply positive charge. The spin polarization of photoelectrons emitted from the manganese centres in Mn{sub 6}Cr SMM after resonant excitation with circularly polarized synchrotron radiation has been measured at selected energies corresponding to the prominent Mn L{sub 3}VV and L{sub 3}M{sub 2,3}V Auger peaks. Spin-resolved photoelectron spectra of the reference substances MnO, Mn{sub 2}O{sub 3} and Mn(II)acetate recorded after resonant excitation at the Mn-L{sub 3}-edge around 640eV are presented as well. The spin polarization value obtained from MnO at room temperature in the paramagnetic state is compared to XMCD measurements of Mn(II)-compounds at 5K and a magnetic field of 5T.

Efeitos da suplementação de fitase sobre a disponibilidade aparente de Mg, Ca, Zn, Cu, Mn e Fe em alimentos vegetais para a tilápia-do-nilo Effects of phytase supplementation on apparent availability of Mg, Ca, Zn, Cu, Mn, and Fe of plant feedstuffs for nile tilapia

Directory of Open Access Journals (Sweden)

Giovani Sampaio Gonçalves

2005-12-01

Full Text Available Cem juvenis de tilápia-do-nilo (Oreochromis niloticus; PV = 100.0 ± 5.0 g foram distribuídos em 10 tanques-rede com o objetivo de avaliar o efeito da suplementação da enzima fitase (0, 1.000 e 2.000 UFA/kg sobre a disponibilidade de minerais em alguns alimentos energéticos (milho, milho extrusado, farelo de trigo, farelo de arroz e farelo de sorgo e protéicos (farelo de soja extrusado, farelo de soja, farelo de girassol, farelo de algodão e glúten de milho utilizados na alimentação de tilápia-do-nilo (Oreochromis niloticus. Para determinação dos coeficientes de disponibilidade aparente (CDA do cálcio (Ca, magnésio (Mg, zinco (Zn, cobre (Cu, ferro (Fe e manganês (Mn, foram confeccionadas 31 rações, marcadas com 0,10% de óxido de crômio III uma referência (ração purificada e 30 contendo os dez alimentos e os diferentes níveis de suplementação da enzima fitase. O CDA dos nutrientes foi calculado com base no teor de crômio da ração e das fezes. A fitase aumenta, nos vegetais, a disponibilidade do Mg, Cu, Zn e Mn, os quais apresentam tendência diferenciada, em razão do seu valor biológico e do nível de suplementação de enzima.One hundred Nile tilapia juveniles (Oreochromis niloticus; BW= 100.0 ± 5.0 g were assigned to 10 experimental cages to evaluate the effects of phytase supplementation (0, 1,000, and 2,000 FTU/kg on calcium (Ca, magnesium (Mg, zinc (Zn, copper (Cu, iron (Fe and manganese (Mn availability of ten feedstuffs: five energetic (corn, extruded corn, wheat meal, rice meal and low-tannin sorghum and five protein (extruded soybean, soybean meal, sunflower meal, cottonseed meal and corn gluten meal. As reference, an albumin and gelatin-based diet [with 0.10 % chromic oxide (III as external marker] was fed to the juveniles. Thirty-one diets (one reference and 30 based on all feedstuffs and increasing levels of phytase were formulated to determine the coefficients of apparent availability of minerals (Mg

The Phase Transformations in Hypoeutectoid Steels Mn-Cr-Ni

Directory of Open Access Journals (Sweden)

RoŻniata E.

2015-04-01

Full Text Available The results of a microstructure and hardness investigations of the hypoeutectoid steels Mn-Cr-Ni, imitating by its chemical composition toughening steels, are presented in the paper. The analysis of the kinetics of phase transformations of undercooled austenite of steels containing different amounts of alloying elements in their chemical composition, constitutes the aim of investigations.

Microstructure and corrosion resistance of Sm-containing Al-Mn-Si-Fe-Cu alloy

Directory of Open Access Journals (Sweden)

Han Yuyin

2017-12-01

Full Text Available Optimizing alloy composition is an effective way to improve physical and chemical properties of automobile heat exchanger materials.A Sm-containing Al-Mn-Si-Fe-Cu alloy was investigated through transmission electron microscopy,scanning electron microscopy,and electrochemical measurement.Experimental results indicated that main phases distributed in the alloy wereα-Al(Mn,FeSi,Al2Sm and Al10Cu7Sm2.Alloying with Sm element could refine the precipitated α-Al(Mn,FeSi phase.Polarization testing results indicated that the corrosion surfacewas mainly composed of pitting pits and corrosion products.Sea water acetic acid test(SWAAT showed that corrosion loss increased first and then slowed downwith increase of the corrosion time.

Study of the structural and magnetic properties and gallium exchange phenomenon in a Mn-Ga alloy doped by Cr during the milling and annealing process

Energy Technology Data Exchange (ETDEWEB)

Fariba, Nazari; Mohsen, Hakimi, E-mail: hakimi.m@yazd.ac.ir; Hossein, Mokhtari; Mohsen, Khajeh Aminian

2015-05-15

The effect of milling and annealing process on Cr doped Mn{sub 3}Ga nanocrystallite has been investigated. Phase determination analysis shows that Ga turning to get out of Mn-Ga structure and tend to make bonding to Cr and form Cr{sub 3}Ga{sub 4} product during milling process. Annealing of the new phases lead to decomposition of Cr{sub 3}Ga{sub 4} and formation of a new Mn-Ga phase in reverse direction, in the other words diffusion of Ga atoms occurs from Cr{sub 3}Ga{sub 4} to Mn phase and α-Mn and Cr{sub 3}Ga{sub 4} change to Mn{sub 3}Ga{sub 2} and Cr phases. The variation of coersivity, magnetization and magnetic state of different samples was explained according to the crystallite size of the present phases and grain boundary effects. It was also confirmed that formation of Mn-Cr clusters plays an important role in increase of saturation magnetization.

Role of W and Mn for reliable 1X nanometer-node ultra-large-scale integration Cu interconnects proved by atom probe tomography

Energy Technology Data Exchange (ETDEWEB)

Shima, K.; Shimizu, H.; Momose, T.; Shimogaki, Y. [Department of Materials Engineering, The University of Tokyo, 7-3-1, Hongo, Bunkyo-ku, Tokyo 113-8656 (Japan); Tu, Y. [The Oarai Center, Institute for Materials Research, Tohoku University, Oarai, Ibaraki 311-1313 (Japan); Key Laboratory of Polar Materials and Devices, Ministry of Education, East China Normal University, Shanghai 200241 (China); Takamizawa, H.; Shimizu, Y.; Inoue, K.; Nagai, Y. [The Oarai Center, Institute for Materials Research, Tohoku University, Oarai, Ibaraki 311-1313 (Japan)

2014-09-29

We used atom probe tomography (APT) to study the use of a Cu(Mn) as a seed layer of Cu, and a Co(W) single-layer as reliable Cu diffusion barriers for future interconnects in ultra-large-scale integration. The use of Co(W) layer enhances adhesion of Cu to prevent electromigration and stress-induced voiding failures. The use of Cu(Mn) as seed layer may enhance the diffusion barrier performance of Co(W) by stuffing the Cu diffusion pass with Mn. APT was used to visualize the distribution of W and Mn in three dimensions with sub-nanometer resolution. W was found to segregate at the grain boundaries of Co, which prevents diffusion of Cu via the grain boundaries. Mn was found to diffuse from the Cu(Mn) layer to Co(W) layer and selectively segregate at the Co(W) grain boundaries with W, reinforcing the barrier properties of Co(W) layer. Hence, a Co(W) barrier coupled with a Cu(Mn) seed layer can form a sufficient diffusion barrier with film that is less than 2.0-nm-thick. The diffusion barrier behavior was preserved following a 1-h annealing at 400 °C. The underlayer of the Cu interconnects requires a large adhesion strength with the Cu, as well as low electrical resistivity. The use of Co(W) has previously been shown to satisfy these requirements, and addition of Mn is not expected to deteriorate these properties.

Effect of Cr and Mn addition and heat treatment on AlSi3Mg casting alloy

Energy Technology Data Exchange (ETDEWEB)

Tocci, Marialaura, E-mail: m.tocci@unibs.it [Department of Mechanical and Industrial Engineering, University of Brescia, Via Branze 38, 25123 Brescia (Italy); Donnini, Riccardo, E-mail: riccardo.donnini@cnr.it [National Research Council of Italy (CNR), Institute of Condensed Matter Chemistry and Technologies for Energy (ICMATE), Via R. Cozzi 53, 20125 Milan (Italy); Angella, Giuliano, E-mail: giuliano.angella@cnr.it [National Research Council of Italy (CNR), Institute of Condensed Matter Chemistry and Technologies for Energy (ICMATE), Via R. Cozzi 53, 20125 Milan (Italy); Pola, Annalisa, E-mail: annalisa.pola@unibs.it [Department of Mechanical and Industrial Engineering, University of Brescia, Via Branze 38, 25123 Brescia (Italy)

2017-01-15

In the present paper the effect of heat treatment on an AlSi3Mg alloy with and without Cr and Mn addition was investigated. Beside the well-known modification of the morphology of Fe-containing intermetallics, it was found that Cr and Mn allowed the formation of dispersoids in the aluminium matrix after solution heat treatment at 545 °C, as shown by scanning transmission electron microscope observations. These particles were responsible of the enhanced Vickers microhardness of the aluminium matrix in comparison with the base alloy after solution treatment and quenching, according to dispersion hardening mechanism. The presence of these particles was not affected by ageing treatment, which instead allowed the precipitation of β-Mg{sub 2}Si, as shown by the elaboration of differential scanning calorimeter curves. The formation of dispersoids and the study of their effect on mechanical properties can represent an interesting development for applications at high temperatures of casting alloys due to their thermal stability compared to other strengthening phases as β-Mg{sub 2}Si. - Highlights: •Cr and Mn successfully modified the morphology of Fe-containing intermetallics. •Cr- and Mn-dispersoids formed in the aluminium matrix during solution treatment. •Dispersion hardening was detected after solution treatment for Cr-containing alloy. •The dispersion hardening effect was maintained after ageing treatment.

Studies on Electronic Structure and Magnetic Properties of an Organic Magnet with Metallic Mn2+ and Cu2+ Ions

Science.gov (United States)

Yao, Jian-Guo; Peng, Guang-Xiong

2004-11-01

The electronic structure and the magnetic properties of the non-pure organic ferromagnetic compound MnCu(pbaOH)(H2O)3 with pbaOH = 2-hydroxy-1, 3-propylenebis (oxamato) are studied by using the density-functional theory with local-spin-density approximation. The density of states, total energy, and the spin magnetic moment are calculated. The calculations reveal that the compound MnCu(pbaOH)(H20)3 has a stable metal-ferromagnetic ground state, and the spin magnetic moment per molecule is 2.208 μB, and the spin magnetic moment is mainly from Mn ion and Cu ion. An antiferromagnetic order is expected and the antiferromagnetic exchange interaction of d-electrons of Cu and Mn passes through the antiferromagnetic interaction between the adjacent C, O, and N atoms along the path linking the atoms Cu and Mn. The project supported by National Natural Science Foundation of China under Grant No. 10375074 and Hubei Automotive Industries Institute Foundation under Grant No. QY2002-16

Electronic structure and x-ray spectroscopy of Cu2MnAl1-xGax

Science.gov (United States)

Rai, D. P.; Ekuma, C. E.; Boochani, A.; Solaymani, S.; Thapa, R. K.

2018-04-01

We explore the electronic and related properties of Cu2MnAl1-xGax with a first-principles, relativistic multiscattering Green function approach. We discuss our results in relation to existing experimental data and show that the electron-core hole interaction is essential for the description of the optical spectra especially in describing the X-ray absorption and magnetic circular dichroism spectra at the L2,3 edges of Cu and Mn.

Design and characterization of FeCrNiCoAlCu and FeCrNiCo(AlCu){sub 0,5} multicomponent alloys; Previsao e caracterizacao de ligas multicomponentes FeCrNiCoAlCu e FeCrNiCo(AlCu){sub 0,5}

Energy Technology Data Exchange (ETDEWEB)

Triveno Rios, Carlos; Artacho, Victor Falcao [Universidade Federal do ABC (CECS/UFABC), Santo Andre, SP (Brazil). Engenharia de Materiais

2014-07-01

High entropy alloys using multi-element main quasi-equivalent atomic proportions and generally forms single-phase solid solution and has the ability to enhance levels of strain hardening combined with high levels of plastic deformation at room temperature. In this work two high-entropy alloys with almost similar composition were studied and the factors influencing the formation of solid solution phases (δ atomic radius difference, ΔH{sub mix} mixing enthalpy, ΔS{sub mix} mixing entropy) were evaluated. The microstructure as-cast and the compositions of phases in the two alloys were analyzed by SEM and XRD. The mechanical characterization was realized by measurements of microhardness and cold compression test. The results showed that FeCrNiCo(AlCu){sub 0,5} and FeCrNiCoAlCu alloys with δ equal to 5,7 and 4,9, respectively, form alloys with solid solutions of high entropy. However, the presence of FC and BCCC structures greatly influence the mechanical properties. (author)

Low temperature transport anomaly in Cr substituted (La{sub 0.67}Sr{sub 0.33})MnO{sub 3} manganites

Energy Technology Data Exchange (ETDEWEB)

Tank, Tejas M., E-mail: tejas.physics2020@gmail.com [Solid State Physics Laboratory, Department of Physics, Barkatullah University, Bhopal-462 026 (India); Shelke, Vilas [Solid State Physics Laboratory, Department of Physics, Barkatullah University, Bhopal-462 026 (India); Das, Sarmistha; Rana, D.S. [Department of Physics, Indian Institute of Scientific Education and Research, Bhopal-462 023 (India); Thaker, C.M. [M.V.M. Science and Home Science College, Rajkot-360 005 (India); Samatham, S.S.; Ganesan, V. [UGC-DAE Consortium for Scientific Research, Khandwa Road, Indore-452 001 (India); Sanyal, S.P. [Solid State Physics Laboratory, Department of Physics, Barkatullah University, Bhopal-462 026 (India)

2017-06-15

Highlights: • The effect of Cr substitution at the Mn-site of La{sub 0.67}Sr{sub 0.33}MnO{sub 3} has been studied. • Electrical and magnetic behaviors correlate with various theoretical models. • First time the low temperature transport anomaly has been explained in terms of e-e scattering phenomenon. • This study shows that FM interaction among Cr{sup 3+} and Mn{sup 3+} is like to the traditional Mn{sup 3+}-O{sup 2−}-Mn{sup 4+} process. - Abstract: The structural, electrical, and magnetic properties of La{sub 0.67}Sr{sub 0.33}Mn{sub 1−x}Cr{sub x}O{sub 3} (0 ≤ x ≤ 0.10) manganites have been studied by substitution of antiferromagnetic trivalent Cr ion at Mn-site. Systematic efforts have been carried out to understand the electrical resistivity behavior in the ferromagnetic metallic and paramagnetic semi-conducting phases of Cr substituted La{sub 0.67}Sr{sub 0.33}Mn{sub 1−x}Cr{sub x}O{sub 3} manganites. Polycrystalline samples show a resistivity minimum at a temperature (T{sub min}) of <40 K in the ferromagnetic metallic phase. T{sub min} shifts to higher temperatures on application of magnetic fields. The appearance of this resistivity minimum was analyzed by fittings the data according to the model that considers e-e scattering caused by enhanced Coulombic interactions. The electrical resistivity data has been best fitted in the metallic and semiconducting regime using various models. Present results suggest that intrinsic magnetic inhomogeneity like Cr{sup 3+} ions in these strongly electron-correlated manganite systems is originating due to the existence of the ferromagnetic interactions.

STUDY OF COATINGS OBTAINED FROM ALLOY Fe-Mn-C-B-Si-Ni-Cr

Directory of Open Access Journals (Sweden)

Mychajło Paszeczko

2016-09-01

Full Text Available Tribological behaviour of coatings obtained from eutectic alloy Fe-Mn-C-B-Si-Ni-Cr was studied. The coatings were obtained by the method of gas metal arc welding (GMA with use of powder wire. GMA welding method is widely used for the regeneration of machine parts. Eutectic Fe-Mn-C-B-Si-Ni-Cr alloys can be used to obtain high quality coatings resistant to wear and corrosion. Pin-on-disk dry sliding wear tests at sliding speeds 0.4 m/s and under load 10 MPa were conducted for pin specimens. During friction a typical tribological behavior was observed. The mechanism of wear was mechanical-chemical.

Improvement of the crystallographic orientation of double-layered perpendicular recording media by using CoCr (Mo)/Cu intermediate layers

International Nuclear Information System (INIS)

Tamai, Ichiro; Yamamoto, T.; Kikukawa, A.; Tanahashi, K.; Ishikawa, A.; Futamoto, M.

2001-01-01

We have introduced intermediate layers of CoCr/Cu and CoCrMo/Cu between a CoCrPtB recording layer and a soft-magnetic CoTaZr underlayer. The combination of the FCC-Cu first-intermediate layer and the HCP-CoCrMo second-intermediate layer was found to enhance the c-axis vertical orientation of the CoCrPtB recording layer. In media with intermediate layers of CoCrMo/Cu, the thickness of the intermediate layers can be reduced without sacrificing good magnetic properties, and this leads to high resolutions

Synthesis, structure and magnetic properties of crystallographically aligned CuCr{sub 2}Se{sub 4} thin films

Energy Technology Data Exchange (ETDEWEB)

Esters, Marco [Department of Chemistry, University of Oregon, Eugene, OR 97403 (United States); Liebig, Andreas [Institut für Physik, Universität Augsburg, 86159 Augsburg (Germany); Ditto, Jeffrey J.; Falmbigl, Matthias [Department of Chemistry, University of Oregon, Eugene, OR 97403 (United States); Albrecht, Manfred [Institut für Physik, Universität Augsburg, 86159 Augsburg (Germany); Johnson, David C., E-mail: davej@uoregon.edu [Department of Chemistry, University of Oregon, Eugene, OR 97403 (United States)

2016-06-25

We report the low temperature synthesis of highly textured CuCr{sub 2}Se{sub 4} thin films using the modulated elemental reactant (MER) method. The structure of CuCr{sub 2}Se{sub 4} is determined for the first time in its thin film form and exhibits cell parameters that are smaller than found in bulk CuCr{sub 2}Se{sub 4}. X-ray diffraction and precession electron diffraction show a strong degree of crystallographic alignment of the crystallites, where the <111> axis is oriented perpendicular to the substrate surface, while being rotationally disordered within the plane. Temperature and field dependent in-plane and out-of-plane magnetization measurements show that the film is ferromagnetic with a Curie temperature of 406 K CuCr{sub 2}Se{sub 4} synthesized utilizing the MER method shows stronger magnetic anisotropy (effective anisotropy: 1.82 × 10{sup 6} erg cm{sup −3}; shape anisotropy: 1.07 × 10{sup 6} erg cm{sup −3}), with the easy axis lying out of plane, and a larger magnetic moment (6 μ{sub B}/f.u.) than bulk CuCr{sub 2}Se{sub 4}. - Highlights: • Crystallographically aligned, phase pure CuCr{sub 2}Se{sub 4} were synthesized. • The degree of alignment decreases with annealing time. • The films are ferromagnetic with the easy axis along the <111> direction. • The magnetization is larger than bulk CuCr{sub 2}Se{sub 4} or other CuCr{sub 2}Se{sub 4} films made to date.

Order–disorder phenomena in layered CuCrSe{sub 2} crystals

Energy Technology Data Exchange (ETDEWEB)

Gagor, A., E-mail: a.gagor@int.pan.wroc.pl; Gnida, D.; Pietraszko, A.

2014-08-01

The thermal motion of Cu{sup +} ions in a quasi-two dimensional copper ion conductor CuCrSe{sub 2} is studied in the vicinity of the order-disorder phase transition to superionic phase, basing on a single-crystal and powder X-ray diffraction, specific heat and electrical resistivity measurements. The copper ions gradually migrate with temperature decrease to empty tetrahedral sites reaching occupancy equilibrium in the disordered high-temperature phase at T{sub s} = 365 K. The copper migration between Cuα and Cuβ tetrahedral sites occurs through the neighboring, face-sharing octahedral holes. Disorder of Cu{sup +} ions brings perturbations in periodic potential of the crystal lattice providing additional scattering centers for electrons. - Graphical abstract: Copper migration within α and β sites. - Highlights: • Single crystals of CuCrSe{sub 2} have been grown by vapor transport. • Thermally activated motion of Cu{sup +} ions is analyzed from T = 295 up to 420 K. • An order–disorder phase transition at T{sub s} = 365 K leads to fast ion conducting state. • Interplay between lattice vibrations and Se polarizability accounts for Cu{sup +} hops. • Electrical resistivity near the T{sub s} shows two additional scattering centers.

Phase stability of CuAlMn shape memory alloys

Czech Academy of Sciences Publication Activity Database

Zárubová, Niva; Novák, Václav

2004-01-01

Roč. 378, - (2004), s. 216-221 ISSN 0921-5093 Institutional research plan: CEZ:AV0Z1010914 Keywords : CuAlMn * shape memory alloys * martensitic transformation * - stress -strain tests * tension-compression cycling * history dependent phenomena Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 1.445, year: 2004

Defect-induced magnetic structure of CuMnSb

Czech Academy of Sciences Publication Activity Database

Máca, František; Kudrnovský, Josef; Drchal, Václav; Turek, I.; Stelmakhovych, O.; Beran, Přemysl; Llobet, A.; Martí, Xavier

2016-01-01

Roč. 94, č. 9 (2016), 1-9, č. článku 094407. ISSN 2469-9950 R&D Projects: GA ČR GB14-37427G Institutional support: RVO:68378271 ; RVO:61389005 Keywords : CuMnSb * electronic structure * defects * magnetic order * ab initio calculations * neutron diffraction analysis Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 3.836, year: 2016

Tuning of cu doping on phase transition and high-field phase diagram of Nd{sub 0.5}Sr{sub 0.5}Mn{sub 1−x}Cu{sub x}O{sub 3}

Energy Technology Data Exchange (ETDEWEB)

Shang, C. [Wuhan National High Magnetic Field Center, Huazhong University of Science and Technology, Wuhan 430074 (China); School of Physics, Huazhong University of Science and Technology, Wuhan 430074 (China); Xia, Z.C., E-mail: xia9020@hust.edu.cn [Wuhan National High Magnetic Field Center, Huazhong University of Science and Technology, Wuhan 430074 (China); Wei, M.; Jin, Z.; Chen, B.R.; Shi, L.R. [Wuhan National High Magnetic Field Center, Huazhong University of Science and Technology, Wuhan 430074 (China); School of Physics, Huazhong University of Science and Technology, Wuhan 430074 (China); Ouyang, Z.W. [Wuhan National High Magnetic Field Center, Huazhong University of Science and Technology, Wuhan 430074 (China); Huang, S.; Xiao, G.L. [Wuhan National High Magnetic Field Center, Huazhong University of Science and Technology, Wuhan 430074 (China); School of Physics, Huazhong University of Science and Technology, Wuhan 430074 (China)

2016-10-15

Pulsed high magnetic fields up to 52 T have been used in the systematic investigation of the magnetic properties of manganites Nd{sub 0.5}Sr{sub 0.5}Mn{sub 1−x}Cu{sub x}O{sub 3} (0≤x≤0.15). The Cu-doping dependent first-order metamagnetic transitions are observed below the charge ordering temperature, which is ascribed to both Cu-doping and field-induced collapse of the charge ordering with antiferromagnetic phase. Based on the magnetization and electrical transport measurements, a three-dimensional phase diagram with coordinate axis of temperature, magnetic field, and doping level has been obtained, in which the critical fields of the metamagnetic transitions increase with the increase in Cu content and decrease with increasing temperature. The experimental results confirm that Mn-site substitution with Cu destroys the Mn{sup 3+}–O{sup 2−}–Mn{sup 4+} bridges and weakens the double exchange interaction between Mn{sup 3+} and Mn{sup 4+} ions, which shows an obvious tuning effect on the metamagnetic transition under the external magnetic field. - Highlights: • Tuning effect of Cu-doping on the properties of Nd{sub 0.5}Sr{sub 0.5}Mn{sub 1−x}Cu{sub x}O{sub 3} was studied. • First-order metamagnetic transition was observed under high magnetic fields. • A phase diagram with temperature, magnetic field and doping level was obtained. • Cu-doping weakens the ferromagnetic coupling in Nd{sub 0.5}Sr{sub 0.5}Mn{sub 1−x}Cu{sub x}O{sub 3}.

Chemical effect on total mass attenuation coefficients of V, Cr, Mn, Co and Ni

International Nuclear Information System (INIS)

Soeguet, Oe.; Colak, S.; Bueyuekkasap, E.; Kuecuekoender, A.

2002-01-01

Detailed interpretation of data obtained from X-ray transmission measurements usually depends on the assumption that the contribution of each element is additive. This assumption yields the mixture rule for X-ray attenuation coefficients which is valid if molecular and chemical effects are negligible. Total mass attenuation coefficients of V, Cr, Mn, Co and Ni in various their compounds was measured. Absorption corrections were carried on data for ligands in the compounds. It was found that V, Cr, Mn, Co and Ni had different total mass attenuation coefficients in the different compounds. Results were compared with theoretical values of HUBBELL and SELTZER. (author)

A novel coping metal material CoCrCu alloy fabricated by selective laser melting with antimicrobial and antibiofilm properties.

Science.gov (United States)

Ren, Ling; Memarzadeh, Kaveh; Zhang, Shuyuan; Sun, Ziqing; Yang, Chunguang; Ren, Guogang; Allaker, Robert P; Yang, Ke

2016-10-01

The aim of this study was to fabricate a novel coping metal CoCrCu alloy using a selective laser melting (SLM) technique with antimicrobial and antibiofilm activities and to investigate its microstructure, mechanical properties, corrosion resistance and biocompatibility. Novel CoCrCu alloy was fabricated using SLM from a mixture of commercial CoCr based alloy and elemental Cu powders. SLM CoCr without Cu served as control. Antibacterial activity was analyzed using standard antimicrobial tests, and antibiofilm properties were investigated using confocal laser scanning microscope. Cu distribution and microstructure were determined using scanning electron microscope, optical microscopy and X-ray diffraction. Corrosion resistance was evaluated by potential dynamic polarization and biocompatibility measured using an MTT assay. SLM CoCrCu alloys were found to be bactericidal and able to inhibit biofilm formation. Other factors such as microstructure, mechanical properties, corrosion resistance and biocompatibility were similar to those of SLM CoCr alloys. The addition of appropriate amounts of Cu not only maintains normal beneficial properties of CoCr based alloys, but also provides SLM CoCrCu alloys with excellent antibacterial and antibiofilm capabilities. This material has the potential to be used as a coping metal for dental applications. Copyright © 2016 Elsevier B.V. All rights reserved.

Surface hardening of 30CrMnSiA steel using continuous electron beam

Science.gov (United States)

Fu, Yulei; Hu, Jing; Shen, Xianfeng; Wang, Yingying; Zhao, Wansheng

2017-11-01

30CrMnSiA high strength low alloy (HSLA) carbon structural steel is typically applied in equipment manufacturing and aerospace industries. In this work, the effects of continuous electron beam treatment on the surface hardening and microstructure modifications of 30CrMnSiA are investigated experimentally via a multi-purpose electron beam machine Pro-beam system. Micro hardness value in the electron beam treated area shows a double to triple increase, from 208 HV0.2 on the base metal to 520 HV0.2 on the irradiated area, while the surface roughness is relatively unchanged. Surface hardening parameters and mechanisms are clarified by investigation of the microstructural modification and the phase transformation both pre and post irradiation. The base metal is composed of ferrite and troostite. After continuous electron beam irradiation, the micro structure of the electron beam hardened area is composed of acicular lower bainite, feathered upper bainite and part of lath martensite. The optimal input energy density for 30CrMnSiA steel in this study is of 2.5 kJ/cm2 to attain the proper hardened depth and peak hardness without the surface quality deterioration. When the input irradiation energy exceeds 2.5 kJ/cm2 the convective mixing of the melted zone will become dominant. In the area with convective mixing, the cooling rate is relatively lower, thus the micro hardness is lower. The surface quality will deteriorate. Chemical composition and surface roughness pre and post electron beam treatment are also compared. The technology discussed give a picture of the potential of electron beam surface treatment for improving service life and reliability of the 30CrMnSiA steel.

Estimation of the Temperature-Dependent Nitrogen Solubility in Stainless Fe-Cr-Mn-Ni-Si-C Steel Melts During Processing

Science.gov (United States)

Wendler, Marco; Hauser, Michael; Sandig, Eckhard Frank; Volkova, Olena

2018-04-01

The influence of chemical composition, temperature, and pressure on the nitrogen solubility of various high alloy stainless steel grades, namely Fe-14Cr-(0.17-7.77)Mn-6Ni-0.5Si-0.03C [wt pct], Fe-15Cr-3Mn-4Ni-0.5Si-0.1C [wt pct], and Fe-19Cr-3Mn-4Ni-0.5Si-0.15C [wt pct], was studied in the melt. The temperature-dependent N-solubility was determined using an empirical approach proposed by Wada and Pehlke. The thus calculated N-concentrations overestimate the actual N-solubility of all the studied Fe-Cr-Mn-Ni-Si-C steel melts at a given temperature and pressure. Consequently, the calculation model has to be modified by Si and C because both elements are not recognized in the original equation. The addition of the 1st and 2nd order interaction parameters for Si and C to the model by Wada and Pehlke allows a precise estimation of the temperature-dependent nitrogen solubility in the liquid steel bath, and fits very well with the measured nitrogen concentrations during processing of the steels. Moreover, the N-solubility enhancing effect of Cr- and Mn-additions has been demonstrated.

The structural and electro-optical characteristics of AZO/Cr:Cu/AZO transparent conductive film

International Nuclear Information System (INIS)

Lin, Tien-Chai; Huang, Wen-Chang; Tsai, Fu-Chun

2015-01-01

A novel triple-layered transparent conductive film, AZO/Cr:Cu/AZO (ACCA), was presented in the paper. The structural and electro-optical properties of the ACCA film were discussed. The thickness of the middle metal layer was constant and those of the AZO layers were varied. The ACCA film shows an obvious ZnO (002) c-axis preferential growth. No diffraction peaks related to Cr and Cu were observed through x-ray diffraction analysis. The middle Cr:Cu layer showed a thickness of 8.16 nm with a continuous and amorphous structure by the observation of a high-resolution transmission electron microscopy (HR-TEM). For the electro-optical characteristic, a best figure of merit (FOM) value of 3.54 × 10 −3 Ω −1 with a corresponding transmittance of 85% was obtained at the thickness of 116 nm of ACCA film. The high FOM value of the film is due to the improvement of conductivity and small sacrifices of transparency. - Highlights: • A novel triple-layered transparent conductive film, AZO/Cr:Cu/AZO is developed. • Chromium is added to copper to reduce the oxidation–reduction reaction. • The film has a FOM of 3.54 × 10 −3 Ω −1 with a corresponding transmittance of 85%. • The Cr:Cu layer shows a continuous and amorphous structure

The structural and electro-optical characteristics of AZO/Cr:Cu/AZO transparent conductive film

Energy Technology Data Exchange (ETDEWEB)

Lin, Tien-Chai [Department of Electrical Engineering, Kun Shan University, No. 195, Kun-Da Road, Yung-Kang Dist., Tainan 71003, Taiwan, ROC (China); Huang, Wen-Chang, E-mail: wchuang@mail.ksu.edu.tw [Department of Electro-Optical Engineering, Kun Shan University, No. 195, Kun-Da Road, Yung-Kang Dist., Tainan 71003, Taiwan, ROC (China); Tsai, Fu-Chun [Department of Electro-Optical Engineering, Kun Shan University, No. 195, Kun-Da Road, Yung-Kang Dist., Tainan 71003, Taiwan, ROC (China)

2015-08-31

A novel triple-layered transparent conductive film, AZO/Cr:Cu/AZO (ACCA), was presented in the paper. The structural and electro-optical properties of the ACCA film were discussed. The thickness of the middle metal layer was constant and those of the AZO layers were varied. The ACCA film shows an obvious ZnO (002) c-axis preferential growth. No diffraction peaks related to Cr and Cu were observed through x-ray diffraction analysis. The middle Cr:Cu layer showed a thickness of 8.16 nm with a continuous and amorphous structure by the observation of a high-resolution transmission electron microscopy (HR-TEM). For the electro-optical characteristic, a best figure of merit (FOM) value of 3.54 × 10{sup −3} Ω{sup −1} with a corresponding transmittance of 85% was obtained at the thickness of 116 nm of ACCA film. The high FOM value of the film is due to the improvement of conductivity and small sacrifices of transparency. - Highlights: • A novel triple-layered transparent conductive film, AZO/Cr:Cu/AZO is developed. • Chromium is added to copper to reduce the oxidation–reduction reaction. • The film has a FOM of 3.54 × 10{sup −3} Ω{sup −1} with a corresponding transmittance of 85%. • The Cr:Cu layer shows a continuous and amorphous structure.

Effects of compositional modifications on the sensitization behavior of Fe-Cr-Mn steels

International Nuclear Information System (INIS)

Edgemon, G.L.; Tortorelli, P.F.; Bell, G.E.C.

1992-01-01

Fe-Cr-Mn steels may possibly be used in conjuction with aqueous blankets or coolants in a fusion device. Therefore, standard chemical immersion (modified Strauss) tests were conducted to characterize the effects of compositional modifications on the thermal sensitization behavior of these steels. A good correlation among weight losses, intergranular corrosion, and cracking was found. The most effective means of decreasing their susceptibility was through reduction of the carbon concentration of these steels to 0.1%, but the sensitization resistance of Fe-Cr-Mn-0.1 C compositions was still inferior to type 304L and other similar stainless steels. Alloying additions that form stable carbides did not have a very significant influence on the sensitization behavior. (orig.)

A study on the cementation of Cu, Ni and Co ions with Mn powders in chloride solution

Energy Technology Data Exchange (ETDEWEB)

Ahn, Jae-Woo [Daejin University, Pochun-gun(Korea); Ahn, Jong-Gwan [Korea Univ., Seoul(Korea); Park, Kyung-Ho [Korea Institute of Geology Mining and Materials, Taejeon (Korea)

2000-06-30

A study on the cementation for the recovery of Cu, Ni and Co with Mn metallic powders in leaching solution from the manganese nodule that have removed Fe ions was studied. The results showed that the recovery efficiencies of metal ions with Mn powders increased when the temperature, pH and the concentration of chloride ions were increased in mixed solution. And the recovery efficiencies of Cu was 98% and not changed with the addition amounts of Mn powders but, in case of Co and Ni, the recovery efficiencies were increased with the addition amounts. The particle size of precipitate was about 5 {mu}m. From the results of experiment we proposed the two-step cementation process for the recovery of Cu, Ni and Co with Mn powders. (author). 9 refs., 4 tabs., 14 figs.

Qualitative aspects of biomonitoring: Sphagnum auriculatum response vs. aerosol metal concentrations (Pb, Ca, Cr, Cu, Fe, Mn, Ni and Zn) in the Porto urban atmosphere

International Nuclear Information System (INIS)

Teresa, M.; Vasconcelos, S.D.; Tavares Laquipai, H.M.F.

2000-01-01

Bags of S. auriculatum and a low-volume aerosol sampler provided with 0.8 μm pore size filters were exposed, in parallel, to the atmosphere of Porto, at different sampling points and in different periods of time, between 1991 and 1997. The levels of lead in the moss (weekly samples) and in the filters (daily samples) were determined by atomic absorption spectrophotometry and the results were compared. Living S. auriculatum exposed in bags to the Porto atmosphere died in several weeks (about a month), but continued to sorb metals from the atmosphere for about another month. In dry weather periods (relative humidity ≤ 76%) the rate of lead uptake by moss was approximately constant and proportional to the levels of the metal in atmospheric aerosols. A converting factor [CF=parallel-Pb-parallel moss (μg/g.day)/ parallel-Pb-parallel air (μg/m 3 )] allowed conversion of the lead levels in S. auriculatum to those in the atmospheric aerosols. Because the moss fixed lead from gas, aerosol and particulate matter, the rate of sorption depends markedly on the distance to the lead sources (mainly traffic) and on surrounding obstacles which retain particles. Therefore, specific calibration by mechanic monitoring, at each sampling point is required in a first stage of biomonitoring, when moss bag samplers are used to provide quantitative information about lead levels in the atmosphere. The mean Pb levels were ≤ 0.5 μg/m 3 and approximately constants at each sample point up to January 1996. After that date it decreased about 50%, in consequence of the reduction of the Pb concentration in leaded gasoline. In wet weather periods, higher but irregular rate of lead uptake was observed. In contrast, the lead levels in atmospheric aerosols decreased when the humidity increased due to wet deposition. Therefore, no proportionality between lead levels in the moss and in air were found. For about two months, in 1994, during a dry weather period, the levels of Ca, Cr, Cu, Fe, Mn, Ni

Designing a New Ni-Mn-Sn Ferromagnetic Shape Memory Alloy with Excellent Performance by Cu Addition

Directory of Open Access Journals (Sweden)

Kun Zhang

2018-02-01

Full Text Available Both magnetic-field-induced reverse martensitic transformation (MFIRMT and a high working temperature are crucial for the application of Ni-Mn-Sn magnetic shape memory alloys. Here, by first-principles calculations, we demonstrate that the substitution of Cu for Sn is effective not only in enhancing the MFIRMT but also in increasing martensitic transformation, which is advantageous for its application. Large magnetization difference (ΔM in Ni-Mn-Sn alloy is achieved by Cu doping, which arises from the enhancement of magnetization of austenite due to the change of Mn-Mn interaction from anti-ferromagnetism to ferromagnetism. This directly leads to the enhancement of MFIRMT. Meanwhile, the martensitic transformation shifts to higher temperature, owing to the energy difference between the austenite L21 structure and the tetragonal martensite L10 structure increases by Cu doping. The results provide the theoretical data and the direction for developing a high temperature magnetic-field-induced shape memory alloy with large ΔM in the Ni-Mn-Sn Heusler alloy system.

Effect of Cr addition on the structural, magnetic and mechanical properties of magnetron sputtered Ni-Mn-In ferromagnetic shape memory alloy thin films

Energy Technology Data Exchange (ETDEWEB)

Akkera, Harish Sharma [Indian Institute of Technology Roorkee, Functional Nanomaterials Research Lab, Department of Physics, Roorkee, Uttarakhand (India); Madanapalle Institute of Technology and Science, Department of Physics, Madanapalle, Chittoor, Andhra Pradesh (India); Kaur, Davinder [Indian Institute of Technology Roorkee, Functional Nanomaterials Research Lab, Department of Physics, Roorkee, Uttarakhand (India)

2016-12-15

The effect of Cr substitution for In on the structural, martensitic phase transformation and mechanical properties of Ni-Mn-In ferromagnetic shape memory alloy (FSMA) thin films was systematically investigated. X-ray diffraction results revealed that the Ni-Mn-In-Cr thin films possessed purely austenitic cubic L2{sub 1} structure at lower content of Cr, whereas higher Cr content, the Ni-Mn-In-Cr thin films exhibited martensitic structure at room temperature. The temperature-dependent magnetization (M-T) and resistance (R-T) results confirmed that the monotonous increase in martensitic transformation temperatures (T{sub M}) with the addition of Cr content. Further, the room temperature nanoindentation studies revealed the mechanical properties such as hardness (H), elastic modulus (E), plasticity index (H/E) and resistance to plastic deformation (H{sup 3}/E {sup 2}) of all the samples. The addition of Cr content significantly enhanced the hardness (28.2 ± 2.4 GPa) and resistance to plastic deformation H{sup 3}/E{sup 2} (0.261) of Ni{sub 50.4}Mn{sub 34.96}In{sub 13.56}Cr{sub 1.08} film as compared with pure Ni-Mn-In film. As a result, the appropriate addition of Cr significantly improved the mechanical properties with a decrease in grain size, which could be further attributed to the grain boundary strengthening mechanism. These findings indicate that the Cr-doped Ni-Mn-In FSMA thin films are potential candidates for microelectromechanical systems applications. (orig.)

Kinetic and thermodynamic aspects of Cu(II) and Cr(III) removal from aqueous solutions using rose waste biomass

International Nuclear Information System (INIS)

Iftikhar, Abdur Rauf; Bhatti, Haq Nawaz; Hanif, Muhammad Asif; Nadeem, Razyia

2009-01-01

Distillation waste of rose petals was used to remove Cu(II) and Cr(III) from aqueous solutions. The results demonstrated the dependency of metal sorption on pH, sorbent dose, sorbent size, initial bulk concentration, time and temperature. A dosage of 1 g/L of rose waste biomass was found to be effective for maximum uptake of Cu(II) and Cr(III). Optimum sorption temperature and pH for Cu(II) and Cr(III) were 303 ± 1 K and 5, respectively. The Freundlich regression model and pseudo-second-order kinetic model were resulted in high correlation coefficients and described well the sorption of Cu(II) and Cr(III) on rose waste biomass. At equilibrium q max (mg/g) of Cu(II) and Cr(III) was 55.79 and 67.34, respectively. The free energy change (ΔG o ) for Cu(II) and Cr(III) sorption process was found to be -0.829 kJ/mol and -1.85 kJ/mol, respectively, which indicates the spontaneous nature of sorption process. Other thermodynamic parameters such as entropy change (ΔS o ), enthalpy (ΔH o )and activation energy (ΔE) were found to be 0.604 J mol -1 K -1 , -186.95 kJ/mol and 68.53 kJ/mol, respectively for Cu(II) and 0.397 J mol -1 K -1 , -119.79 kJ/mol and 114.45 kJ/mol, respectively for Cr(III). The main novelty of this work was the determination of shortest possible sorption time for Cu(II) and Cr(III) in comparison to earlier studies. Almost over 98% of Cu(II) and Cr(III) were removed in only first 20 min at an initial concentration of 100 mg/L

Effect of iron promoter on structure and performance of CuMnZnO catalyst for higher alcohols synthesis

Energy Technology Data Exchange (ETDEWEB)

Ding, Mingyue [Key Laboratory of Renewable Energy and Natural Gas Hydrate, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Guangzhou Institute of Energy Conversion, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Qiu, Minghuang [Key Laboratory of Renewable Energy and Natural Gas Hydrate, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Guangzhou Institute of Energy Conversion, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Graduate School of Chinese Academy of Science, Beijing 100049 (China); Wang, Tiejun [Key Laboratory of Renewable Energy and Natural Gas Hydrate, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Guangzhou Institute of Energy Conversion, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Ma, Longlong; Wu, Chuangzhi [Key Laboratory of Renewable Energy and Natural Gas Hydrate, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Guangzhou Institute of Energy Conversion, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Liu, Jianguo [Key Laboratory of Renewable Energy and Natural Gas Hydrate, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Guangzhou Institute of Energy Conversion, Chinese Academy of Science, Guangzhou Guangdong 510640 (China); Graduate School of Chinese Academy of Science, Beijing 100049 (China)

2012-09-15

Highlights: Black-Right-Pointing-Pointer Incorporation of iron promotes the dispersion of catalyst particles. Black-Right-Pointing-Pointer Adding iron facilitates the separation of CuO from the Cu-Mn solid solution. Black-Right-Pointing-Pointer Both the copper and iron carbides are well dispersed in higher iron amount. Black-Right-Pointing-Pointer The selectivity to C{sub 2}{sup +}OH is promoted by increasing iron concentration. -- Abstract: Effect of iron promoter on the microstructures of CuMnZnO catalysts was investigated by N{sub 2} physical adsorption (BET), X-ray diffraction (XRD), and temperature-programmed reduction of hydrogen (H{sub 2}-TPR). Higher alcohols synthesis (HAS) was performed in a fixed bed reactor. The characterization results indicated that incorporation of iron in the CuMnZnO catalyst resulted in the increase of BET surface area and the dispersion of catalyst particles. Adding iron facilitated the formation of Fe-Mn solid solution and reduced the interaction between copper and manganese, which promoted the separation of CuO from the Cu-Mn solid solution and the reduction of the catalyst. In the HAS reaction, the catalytic activity of CO hydrogenation and the selectivity to C{sub 2}{sup +}OH and hydrocarbons presented an increasing trend with the increase in iron concentration, which may be attributed to the synergistic effect between the dispersed copper and iron carbides.

Antibacterial property of CuCrO{sub 2} nanopowders prepared by a self-combustion glycine nitrate process

Energy Technology Data Exchange (ETDEWEB)

Nien, Yung-Tang, E-mail: ytnien@nfu.edu.tw [Deparment of Materials Science and Engineering, National Formosa University, Yunlin, 63201, Taiwan (China); Hu, Mon-Ru [Deparment of Materials Science and Engineering, National Formosa University, Yunlin, 63201, Taiwan (China); Chiu, Te-Wei [Department of Materials and Mineral Resources Engineering, National Taipei University of Technology, Taipei, 10608, Taiwan (China); Chu, Jaw-Shiow [Bioresource Collection and Research Center, Food Industry Research and Development Institute, Hsinchu, 30062, Taiwan (China)

2016-08-15

Porous CuCrO{sub 2} nanopowders were prepared via glycine nitrate process (GNP) at 175 °C in ambient air. The X-ray diffraction patterns showed a pure delafossite phase of CuCrO{sub 2} with numerous broad peaks, indicating a crystallite size of approximately 20 nm. The surface area of the CuCrO{sub 2} nanopowders was larger than 50 m{sup 2}/g, nearly 100 times greater than that of bulk powders (0.47 m{sup 2}/g). Pathogenic Gram-negative bacteria Escherichia coli (E. coli) were chosen as the antibacterial evaluation indicators for both the nanopowders and bulk powders. The results showed that 1750 ppm nanopowders inhibited the growth of E. coli. As a control, the bulk powders showed a normal growth profile. The antibacterial property of the CuCrO{sub 2} nanopowders can be attributed to the extremely large surface area, which induces rapid release of Cu ions and strong adhesion of nanopowders to bacteria. - Highlights: • CuCrO{sub 2} nanopowders was prepared by low-temperature glycine nitrate process. • 1250–1500 ppm of CuCrO{sub 2} nanopowders were found to depress the growth of Escherichia coli. • Bulk powders by the solid state reaction exhibited no antibacterial property. • The antibacterial property of nanopowders was attributed to rapid Cu ion releases. • Heavy adhesion of nanopowders to bacteria also resulted in antibacterial property.

Pressure dependence of resistivity and magnetic properties in a Mn1.9Cr0.1Sb alloy

Directory of Open Access Journals (Sweden)

D. V. Maheswar Repaka

2017-12-01

Full Text Available We report magnetic-field and hydrostatic pressure dependent electrical resistivity and magnetic properties of a Mn1.9Cr0.1Sb alloy. Upon cooling, the magnetization of Mn1.9Cr0.1Sb exhibits a first-order ferrimagnetic to antiferromagnetic transition at the exchange inversion temperature, TS = 261 K under a 0.1 T magnetic field. Our experimental results show that TS decreases with increasing magnetic field but increase with increasing hydrostatic pressure. The pressure induced transition is accompanied by a large positive baro-resistance of 30.5% for a hydrostatic pressure change of 0.69 GPa. These results show that the lattice parameters as well as the bond distance between Mn-Mn atoms play a crucial role in the magnetic and electronic transport properties of Mn1.9Cr0.1Sb. This sample also exhibits a large inverse magnetocaloric effect with a magnetic entropy change of ΔSm = +6.75 J/kg.K and negative magnetoresistance (44.5% for a field change of 5 T at TS in ambient pressure which may be useful for magnetic cooling and spintronics applications.

Structure, magnetism, and electron-transport properties of Mn2CrGa-based nanomaterials

Directory of Open Access Journals (Sweden)

Wenyong Zhang

2016-05-01

Full Text Available Mn2CrGa in the disordered cubic structure has been synthesized using rapid quenching and subsequent annealing. The cubic phase transforms to a stable tetragonal phase when a fraction of Cr or Ga is replaced by Pt or Al, respectively. All samples are ferrimagnetic with high Curie temperatures (Tc; Mn2CrGa exhibits the highest Tc of about 813 K. The tetragonal samples have appreciable values of magnetocrystalline anisotropy energy, which leads to an increase in coercivity (Hc that approaches about 10 kOe in the Pt-doped sample. The Hc linearly increases with a decrease of temperature, concomitant with the anisotropy change with temperature. All samples are metallic and show negative magnetoresistance with room-temperature resistivities on the order of 1 mΩcm. The magnetic properties including high Tc and low magnetic moment suggest that these tetragonal materials have potential for spin-transfer-torque-based devices.

Synthesis, characterization and photocatalytic activity of cubic-like CuCr2O4 for dye degradation under visible light irradiation

International Nuclear Information System (INIS)

Yuan, Wenhui; Liu, Xiaoxia; Li, Li

2014-01-01

Graphical abstract: Hydrothermal synthesis method was applied for preparation of cubic-like CuCr 2 O 4 spinel nanoparticles without template. The synthesized cubic-like CuCr 2 O 4 shows excellent photocatalytic activity for degradation of RhB and MB cationic dyes but not for MO anionic dye in the presence of H 2 O 2 under visible light irradiation. - Highlights: • The cubic-like CuCr 2 O 4 spinel nanoparticles were successfully synthesized via the hydrothermal synthesis method. • The calcination temperature has a great influence on the morphology, particle size and photocatalytic activity of CuCr 2 O 4 . • The pH at the point of zero charge (pH pzc ) of the CuCr 2 O 4 calcined at 600 °C is about 4.52. • The cubic-like CuCr 2 O 4 calcined at 600 °C exhibits excellent photocatalytic activity for RhB and MB in the presence of H 2 O 2 under visible-light irradiation. - Abstract: CuCr 2 O 4 nanoparticles with cubic-like morphology were prepared via hydrothermal synthesis method without template. The CuCr 2 O 4 samples were characterized by thermogravimetry and differential scanning calorimetry (TG–DSC), X-ray diffraction (XRD), transmission electron microscopy (TEM), X-ray photoelectron spectroscopy (XPS), UV–vis diffuse reflectance spectra (DRS) and Zeta potentials, respectively. The results indicated that cubic-like CuCr 2 O 4 could be successfully synthesized by calcining the precursor at 600 °C, and the calcination temperature greatly influenced the morphology and optical performance of CuCr 2 O 4 . The pH at the point of zero charge (pH pzc ) of the CuCr 2 O 4 calcined at 600 °C was about 4.52. The photocatalytic activity of CuCr 2 O 4 was evaluated for degradation of rhodamine B (RhB), methylene blue (MB), and methyl orange (MO) in the presence of H 2 O 2 under visible light irradiation and the effects of the calcination temperature, dosage of photocatalyst, etc., on photocatalytic activity were studied in detail. The photocatalytic results

Flower-, wire-, and sheet-like MnO2-deposited diatomites: Highly efficient absorbents for the removal of Cr(VI).

Science.gov (United States)

Du, Yucheng; Wang, Liping; Wang, Jinshu; Zheng, Guangwei; Wu, Junshu; Dai, Hongxing

2015-03-01

Flower-, wire-, and sheet-like MnO2-deposited diatomites have been prepared using a hydrothermal method with Mn(Ac)2, KMnO4 and/or MnSO4 as Mn source and diatomite as support. Physical properties of the materials were characterized by means of numerous analytical techniques, and their behaviors in the adsorption of chromium(VI) were evaluated. It is shown that the MnO2-deposited diatomite samples with different morphologies possessed high surface areas and abundant surface hydroxyl groups (especially the wire-like MnO2/diatomite sample). The wire-like MnO2/diatomite sample showed the best performance in the removal of Cr(VI), giving the maximum Cr(VI) adsorption capacity of 101 mg/g. Copyright © 2014. Published by Elsevier B.V.

Thermo-mechanical treatment of low-cost alloy Ti-4.5Al-6.9Cr-2.3Mn and microstructure and mechanical characteristics

Science.gov (United States)

Chen, Guangyao; Kang, Juyun; Wang, Shusen; Wang, Shihua; Lu, Xionggang; Li, Chonghe

2018-04-01

In this study, the thermo-mechanical treatment process for low-cost Ti-4.5Al-6.9Cr-2.3Mn alloy were designed on the basis of assessment of Ti-Al-Cr-Mn thermodynamic system. The microstructure and mechanical properties of Ti-4.5Al-6.9Cr-2.3Mn forging and sheet were investigated by using the OM, SEM and universal tensile testing machine. The results show that both the forging and sheet were consisted of α + β phase, which is consistent with the expectation, and no element Cr and Mn existed in the grain boundaries of the sheet after quenching, and the C14 laves phase was not detected. The average ultimate tensile strength (σ b), 0.2% proof strength (σ 0.2) and elongation (EI) of alloy sheet after quenching can reach 1059 MPa, 1051 MPa and 24.6 Pct., respectively. Moreover, the average ultimate tensile strength of Ti-4.5Al-6.9Cr-2.3Mn forgings can reach 1599 MPa and the average elongation can reach 11.2 Pct., and a more excellent property of Ti-4.5Al-6.9Cr-2.3Mn forging is achieved than that of TC4 forging. It provides a theoretical support for further developing this low-cost alloy.

Preliminary assessment of metal-porcelain bonding strength of CoCrW alloy after 3 wt.% Cu addition

International Nuclear Information System (INIS)

Lu, Yanjin; Zhao, Chaoqian; Ren, Ling; Guo, Sai; Gan, Yiliang; Yang, Chunguang; Wu, Songquan; Lin, Junjie; Huang, Tingting; Yang, Ke; Lin, Jinxin

2016-01-01

In this work, a novel Cu-bearing CoCrW alloy fabricated by selective laser melting for dental application has been studied. For its successful application, the bonding strength of metal-porcelain is essential to be systematically investigated. Therefore, the aim of this study was to evaluate the metal-porcelain bonding strength of CoCrWCu alloy by three-point bending test, meanwhile the Ni-free CoCrW alloy was used as control. The oxygen content was investigated by an elemental analyzer; X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical composition of CoCrW based alloy after preoxidation treatment; the fracture mode was investigated by X-ray energy spectrum analysis (EDS) and scanning electron microscope (SEM). Result from the oxygen content analysis showed that the content of oxygen dramatically increased after the Cu addition. And the XPS suggested that Co-oxidation, Cr_2O_3, CrO_2, WO_3, Cu_2O and CuO existed on the preoxidated surface of the CoCrWCu alloy; the three-point bending test showed that the bonding strength of the CoCrWCu alloy was 43.32 MPa, which was lower than that of the CoCrW group of 47.65 MPa. However, the average metal-porcelain bonding strength is significantly higher than the minimum value in the ISO 9693 standard. Results from the SEM images and EDS indicated that the fracture mode of CoCrWCu-porcelain was mixed between cohesive and adhesive. Based on the results obtained in this study, it can be indicated that the Cu-bearing CoCrW alloy fabricated by the selective laser melting is a promising candidate for use in dental application. - Highlights: • The bonding strength of metal-porcelain was slightly decreased with Cu addition; • Cu not only led to promote the diffusion of O and W element but also inhibited the diffusivity of Co in the outward direction; • The changed oxidation behavior resulted in lowering the bonding strength;

Preliminary assessment of metal-porcelain bonding strength of CoCrW alloy after 3 wt.% Cu addition

Energy Technology Data Exchange (ETDEWEB)

Lu, Yanjin; Zhao, Chaoqian [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Ren, Ling [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Guo, Sai; Gan, Yiliang [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Yang, Chunguang [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Wu, Songquan; Lin, Junjie; Huang, Tingting [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China); Yang, Ke, E-mail: kyang@imr.ac.cn [Institute of Metal Research, Chinese Academy of Sciences, 72 Wenhua Road, Shenyang (China); Lin, Jinxin, E-mail: franklin@fjirsm.ac.cn [Key Laboratory of Optoelectronic Materials Chemistry and Physics, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, 155Yangqiao Road West, Fuzhou (China)

2016-06-01

In this work, a novel Cu-bearing CoCrW alloy fabricated by selective laser melting for dental application has been studied. For its successful application, the bonding strength of metal-porcelain is essential to be systematically investigated. Therefore, the aim of this study was to evaluate the metal-porcelain bonding strength of CoCrWCu alloy by three-point bending test, meanwhile the Ni-free CoCrW alloy was used as control. The oxygen content was investigated by an elemental analyzer; X-ray photoelectron spectroscopy (XPS) was used to analyze the surface chemical composition of CoCrW based alloy after preoxidation treatment; the fracture mode was investigated by X-ray energy spectrum analysis (EDS) and scanning electron microscope (SEM). Result from the oxygen content analysis showed that the content of oxygen dramatically increased after the Cu addition. And the XPS suggested that Co-oxidation, Cr{sub 2}O{sub 3}, CrO{sub 2}, WO{sub 3}, Cu{sub 2}O and CuO existed on the preoxidated surface of the CoCrWCu alloy; the three-point bending test showed that the bonding strength of the CoCrWCu alloy was 43.32 MPa, which was lower than that of the CoCrW group of 47.65 MPa. However, the average metal-porcelain bonding strength is significantly higher than the minimum value in the ISO 9693 standard. Results from the SEM images and EDS indicated that the fracture mode of CoCrWCu-porcelain was mixed between cohesive and adhesive. Based on the results obtained in this study, it can be indicated that the Cu-bearing CoCrW alloy fabricated by the selective laser melting is a promising candidate for use in dental application. - Highlights: • The bonding strength of metal-porcelain was slightly decreased with Cu addition; • Cu not only led to promote the diffusion of O and W element but also inhibited the diffusivity of Co in the outward direction; • The changed oxidation behavior resulted in lowering the bonding strength;.

Cryogenic buffer-gas loading and magnetic trapping of CrH and MnH molecules

OpenAIRE

Stoll, M.; Bakker, J.; Steimle, T.; Meijer, G.; Peters, A.

2008-01-01

We report on the buffer-gas cooling and trapping of CrH and MnH molecules in a magnetic quadrupole trap with densities on the order of 106 cm−3 at a temperature of 650 mK. Storage times of up to 180 ms have been observed, corresponding to a 20-fold lifetime enhancement with respect to the field-free diffusion through the 3He buffer-gas. Using Monte Carlo trajectory simulations, inelastic molecule-3He collision cross sections of 1.6×10−18 and 3.1×10−17 cm2 are extracted for CrH and MnH, respec...

Magnetic properties and EXAFS study of nanocrystalline Fe2Mn0.5Cu0.5Al synthesized using mechanical alloying technique

International Nuclear Information System (INIS)

Nanto, Dwi; Yang, Dong-Seok; Yu, Seong-Cho

2014-01-01

Nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al has been synthesized by the mechanical alloying technique and studied as a function of milling time. Alloy nature of Fe 2 Mn 0.5 Cu 0.5 Al was observed in a sample milled for 96 h. The magnetic saturation is 4.0 μ B /f.u., which coincidently follows Slater–Pauling rule at 5 K. Nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al has enhanced saturate magnetization compared to any other fabrication of Fe 2 MnAl reported. Cu element plays an important role in site competes with other elements and may result in the enhancement of saturate magnetization. In accordance to the magnetic results and EXAFS pattern, it was revealed that the dynamics of magnetic properties were confirmed as structural changes of nanocrystalline Fe 2 Mn 0.5 Cu 0.5 Al

Solid-state reactions during mechanical alloying of ternary Fe–Al–X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems: A review

Energy Technology Data Exchange (ETDEWEB)

Hadef, Fatma, E-mail: hadef77@yahoo.fr [Laboratoire de Recherche sur la Physico-Chimie des Surfaces et Interfaces, LRPCSI, Université 20 Août 1955, BP 26, Route d’El-Haddaiek, Skikda 21000 (Algeria); Département de Physique, Faculté des Sciences, Université 20 Août 1955, BP 26, Route d’El-Haddaiek, Skikda 21000 (Algeria)

2016-12-01

The last decade has witnessed an intensive research in the field of nanocrystalline materials due to their enhanced properties. A lot of processing techniques were developed in order to synthesis these novel materials, among them mechanical alloying or high-energy ball milling. In fact, mechanical alloying is one of the most common operations in the processing of solids. It can be used to quickly and easily synthesize a variety of technologically useful materials which are very difficult to manufacture by other techniques. One advantage of MA over many other techniques is that is a solid state technique and consequently problems associated with melting and solidification are bypassed. Special attention is being paid to the synthesis of alloys through reactions mainly occurring in solid state in many metallic ternary Fe–Al–X systems, in order to improve mainly Fe–Al structural and mechanical properties. The results show that nanocrystallization is the common result occurring in all systems during MA process. The aim of this work is to illustrate the uniqueness of MA process to induce phase transformation in metallic Fe–Al–X (X=Ni, Mn, Cu, Ti, Cr, B, Si) systems. - Highlights: • A review of state of the art on binary Fe–Al alloys was presented. • Structural and microstructural properties of MA ternary Fe–Al–X alloys were summerized. • MA process is a powerful tool for producing metallic alloys at the nanometer scale.

Interface Resistance between FeCr Interconnects and La0.85Sr0.15Mn1.1O3

DEFF Research Database (Denmark)

Mikkelsen, Lars; Neufeld, Kai; Hendriksen, Peter Vang

2009-01-01

The long term oxidation behaviour and the electrical interface resistance between FeCr interconnects and La0,85Sr0,15Mn1,1O3 plates was studied by a DC four-point method in air at 750{degree sign}C for 10000 h. The tested FeCr alloys were: Crofer 22 APU, Sanergy HT, Plansee IT10, Plansee IT11, an....... Low degradation rates of less than 1 mcm2/1000 h were measured on all interfaces. The microstructure analysis showed that a duplex Cr2O3-(Mn,Co,Cr)3O4 oxide scale with a thickness of 3-5 µm had evolved on the alloys....

Effect of alloying elements on solidification of primary austenite in Ni-Mn-Cu cast iron

Directory of Open Access Journals (Sweden)

A. Janus

2011-04-01

Full Text Available Within the research, determined were direction and intensity of alloying elements influence on solidification way (directional orvolumetric of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu. 50 cast shafts dia. 20 mm were analysed.Chemical composition of the alloy was as follows: 1.7 to 3.3 % C, 1.4 to 3.1 % Si, 2.8 to 9.9 % Ni, 0.4 to 7.7 % Mn, 0 to 4.6 % Cu, 0.14 to0.16 % P and 0.03 to 0.04 % S. The discriminant analysis revealed that carbon influences solidification of primary austenite dendrites most intensively. It clearly increases the tendency to volumetric solidification. Influence of the other elements is much weaker. This means that the solidification way of primary austenite dendrites in hypoeutectic austenitic cast iron Ni-Mn-Cu does not differ from that in an unalloyed cast iron.

Microstructure and mechanical properties of Al-Cu-Mg-Mn-Zr alloy with trace amounts of Ag

International Nuclear Information System (INIS)

Liu Xiaoyan; Pan Qinglin; Lu Congge; He Yunbin; Li Wenbin; Liang Wenjie

2009-01-01

The microstructure and mechanical properties of Al-Cu-Mg-(Ag)-Mn-Zr alloys were studied by means of tensile testing, optical microscopy (OM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that small additions of Ag to Al-Cu-Mg-Mn-Zr alloy can accelerate the hardening effect of the aged alloy and reduce the time to peak-aged. The mechanical properties can be improved both at room temperature and at elevated temperatures, which is attributed to the fine and uniform plate-like Ω precipitates. Meanwhile the ductility of the studied alloys remains at relatively high level. The major strengthening phases of the Ag-free alloy are θ' and less S', while that of Al-Cu-Mg-Mn-Zr alloy containing trace amounts of Ag are Ω and less θ'.

Investigation of structural stability and elastic properties of CrH and MnH: A first principles study

Science.gov (United States)

Kanagaprabha, S.; Rajeswarapalanichamy, R.; Sudhapriyanga, G.; Murugan, A.; Santhosh, M.; Iyakutti, K.

2015-06-01

The structural and mechanical properties of CrH and MnH are investigated using first principles calculation based on density functional theory as implemented in VASP code with generalized gradient approximation. The calculated ground state properties are in good agreement with previous experimental and other theoretical results. A structural phase transition from NaCl to NiAs phase at a pressure of 76 GPa is predicted for both CrH and MnH.

Catalytic behavior and synergistic effect of nanostructured mesoporous CuO-MnO{sub x}-CeO{sub 2} catalysts for chlorobenzene destruction

Energy Technology Data Exchange (ETDEWEB)

He, Chi, E-mail: chi_he@mail.xjtu.edu.cn [Key Lab of Urban Environment and Health, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Department of Environmental Science and Engineering, School of Energy and Power Engineering, Xi’an Jiaotong University, Xi’an 710049 (China); Yu, Yanke [Key Lab of Urban Environment and Health, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Shen, Qun [Research Center for Greenhouse Gases and Environmental Engineering, Shanghai Advanced Research Institute, Chinese Academy of Sciences, Shanghai 201210 (China); Chen, Jinsheng, E-mail: jschen@iue.ac.cn [Key Lab of Urban Environment and Health, Institute of Urban Environment, Chinese Academy of Sciences, Xiamen 361021 (China); Qiao, Nanli [Department of Environmental Nano-materials, Research Center for Eco-Environmental Sciences, Chinese Academy of Sciences, Beijing 100085 (China)

2014-04-01

Graphical abstract: - Highlights: • Mesoporous CuO-MnO{sub x}-CeO{sub 2} oxides with enhanced reducibility and oxygen mobility. • Incorporation of Cu and Mn ions causes abundant crystal defects and oxygen vacancies. • Surface oxygen concentration and active oxygen mobility determine the catalytic efficiency. • Catalysts with conspicuous chlorobenzene low-temperature removal activity and durability. - Abstract: Mesoporous CuO-MnO{sub x}-CeO{sub 2} composite metal oxides with different copper and manganese loadings were prepared by a urea-assistant hydrothermal method, and were further adopted for the complete catalytic combustion of chlorobenzene. The effects of reaction conditions such as inlet reagent concentration and water feed concentration on chlorobenzene combustion were also studied. The structure and textural properties of the synthesized catalysts were characterized via the XRD, N{sub 2} adsorption/desorption, FE-SEM, TEM, H{sub 2}-TPR, O{sub 2}-TPD, and XPS techniques. The characterization results reveal that the presence of a small amount of Mn species can facilitate the incorporation of Cu and Mn ions into ceria lattice to form Cu-Mn-Ce-O solid solution. The synergistic effect of Cu and Mn species can reduce the redox potential of the composite catalysts, and produce large amounts of oxygen vacancies in the interface of CuO{sub x}, MnO{sub x}, and CeO{sub 2} oxides. The catalyst with Cu/Mn atomic ratio of 1/1 exhibits the best chlorobenzene elimination capability, oxidizing about 95% of the inlet chlorobenzene at 264 °C with CO{sub 2} selectivity higher than 99.5%. The concentration and mobility of the chemically adsorbed oxygen are vital for the effective removal of surface Cl species, which inhibits the dissociation of oxygen molecules and decreases the reducibility of the copper and manganese species. It can be rationally concluded that the superior catalytic performance and durability of the mesoporous CuO-MnO{sub x}-CeO{sub 2} composite

Effect of Thermomagnetic Treatment on Structure and Properties of Cu-Al-Mn Alloy.

Science.gov (United States)

Titenko, A N; Demchenko, L D; Perekos, A O; Gerasimov, O Yu

2017-12-01

The paper studies the influence of magnetic field on magnetic and mechanical properties of Cu-Mn-Al alloy under annealing. The comparative analysis of the magnetic field orientation impact on solid solution decomposition processes in a fixed annealing procedure is held using the methods of low-field magnetic susceptibility, specific magnetization, and microhardness test. The paper highlights changes in the magnetic and mechanical properties of Cu-Al-Mn alloy as the result of change in a critical size of forming precipitated ferromagnetic phase and determines correlation in the behavior of magnetic and mechanical properties of the alloy, depending on a critical nucleus size of forming precipitated ferromagnetic phase.

Positron Annihilation Spectroscopy and Small Angle Neutron Scattering Characterization of Nanostructural Features in Irradiated Fe-Cu-Mn Alloys

International Nuclear Information System (INIS)

Wirth, B D; Asoka-Kumar, P; Howell, R H; Odette, G R; Sterne, P A

2001-01-01

Radiation embrittlement of nuclear reactor pressure vessel steels results from a high number density of nanometer sized Cu-Mn-Ni rich precipitates (CRPs) and sub-nanometer matrix features, thought to be vacancy-solute cluster complexes (VSC). However, questions exist regarding both the composition of the precipitates and the defect character and composition of the matrix features. We present results of positron annihilation spectroscopy (PAS) and small angle neutron scattering (SANS) characterization of irradiated and thermally aged Fe-Cu and Fe-Cu-Mn alloys. These complementary techniques provide insight into the composition and character of both types of nanoscale features. The SANS measurements indicate populations of CRPs and VSCs in both alloys. The CRPs are coarser in the Fe-Cu alloy and the number densities of CRP and VSC increase with the addition of Mn. The PAS involved measuring both the positron lifetimes and the Doppler broadened annihilation spectra in the high momentum region to provide elemental sensitivity at the annihilation site. The spectra in Fe-Cu-Mn specimens thermally aged to peak hardness at 450 C and irradiated at 288 C are nearly identical to elemental Cu. Positron lifetime and spectrum measurements in Fe-Cu specimens irradiated at 288 C clearly show the existence of long lifetime (∼500 ps) open volume defects, which also contain Cu. Thus the SANS and PAS provide a self-consistent picture of nanostructures composed of CRPs and VSCs and tend to discount high Fe concentrations in the CRPs

Influence of elemental diffusion on low temperature formation of MgH2 in TiMn1.3T0.2-Mg (T = 3d-transition elements)

International Nuclear Information System (INIS)

Yamamoto, K.; Tanioka, S.; Tsushio, Y.; Shimizu, T.; Morishita, T.; Orimo, S.; Fujii, H.

1996-01-01

In order to examine the influence of the elemental diffusion from the host compound into the Mg region on low temperature formation of MgH 2 , we have investigated the hydriding properties and the microstructures of the composite materials TiMn 1.3 T 0.2 -Mg (T = V, Cr, Mn, Fe, Co, Ni and Cu). MgH 2 is formed at 353 K in all composite materials. Of all the substitutions, the amount of MgH 2 is the largest in the case of the Cu substitution, which originates from the existence of the Mg-Mg 2 Cu eutectic formed by Cu diffusion from the host compound TiMn 1.3 Cu 0.2 into the Mg region during the liquid phase sintering. In addition, the hydrogen capacity of TiMn 1.3 Cu 0.2 -Mg (that is TiMn 1.3 Cu 0.1 -(Mg+Mg 2 Cu) after the sintering) easily saturates in comparison with TiMn 1.5 -(Mg+Mg 2 Cu) without Cu diffusion. It is concluded that Cu diffusion promotes the mobility of hydrogen atoms at the complex interface between the host compound and the Mg region. (orig.)

Elastic properties of fcc Fe–Mn–X (X = Cr, Co, Ni, Cu) alloys studied by the combinatorial thin film approach and ab initio calculations

International Nuclear Information System (INIS)

Reeh, S; Kasprzak, M; Klusmann, C D; Stalf, F; Music, D; Schneider, J M; Ekholm, M; Abrikosov, I A

2013-01-01

The elastic properties of fcc Fe–Mn–X (X = Cr, Co, Ni, Cu) alloys with additions of up to 8 at.% X were studied by combinatorial thin film growth and characterization and by ab initio calculations using the disordered local moments (DLM) approach. The lattice parameter and Young’s modulus values change only marginally with X. The calculations and experiments are in good agreement. We demonstrate that the elastic properties of transition metal alloyed Fe–Mn can be predicted by the DLM model. (paper)

Soil Cd, Cr, Cu, Ni, Pb and Zn sorption and retention models using SVM: Variable selection and competitive model.

Science.gov (United States)

González Costa, J J; Reigosa, M J; Matías, J M; Covelo, E F

2017-09-01

The aim of this study was to model the sorption and retention of Cd, Cu, Ni, Pb and Zn in soils. To that extent, the sorption and retention of these metals were studied and the soil characterization was performed separately. Multiple stepwise regression was used to produce multivariate models with linear techniques and with support vector machines, all of which included 15 explanatory variables characterizing soils. When the R-squared values are represented, two different groups are noticed. Cr, Cu and Pb sorption and retention show a higher R-squared; the most explanatory variables being humified organic matter, Al oxides and, in some cases, cation-exchange capacity (CEC). The other group of metals (Cd, Ni and Zn) shows a lower R-squared, and clays are the most explanatory variables, including a percentage of vermiculite and slime. In some cases, quartz, plagioclase or hematite percentages also show some explanatory capacity. Support Vector Machine (SVM) regression shows that the different models are not as regular as in multiple regression in terms of number of variables, the regression for nickel adsorption being the one with the highest number of variables in its optimal model. On the other hand, there are cases where the most explanatory variables are the same for two metals, as it happens with Cd and Cr adsorption. A similar adsorption mechanism is thus postulated. These patterns of the introduction of variables in the model allow us to create explainability sequences. Those which are the most similar to the selectivity sequences obtained by Covelo (2005) are Mn oxides in multiple regression and change capacity in SVM. Among all the variables, the only one that is explanatory for all the metals after applying the maximum parsimony principle is the percentage of sand in the retention process. In the competitive model arising from the aforementioned sequences, the most intense competitiveness for the adsorption and retention of different metals appears between

A high performance quasi-solid-state supercapacitor based on CuMnO2 nanoparticles

Science.gov (United States)

Wang, Lu; Arif, Muhammad; Duan, Guorong; Chen, Shenming; Liu, Xiaoheng

2017-07-01

Mixed metal or transition metal oxides hold an unveiled potential as one of the most promising energy storage material because of their excellent stability, reliable conductivity, and convenient use. In this work, CuMnO2 nanoparticles are successfully prepared by a facile hydrothermal process with the help of dispersing agent cetyltrimethylammonium bromide (CTAB). CuMnO2 nanoparticles possess a uniform quadrilateral shape, small size (approximately 25 × 25 nm-35 × 35 nm), excellent dispersity, and large specific surface specific (56.9 m2 g-1) with an interparticle mesoporous structure. All these characteristics can bring benefit for their application in supercapacitor. A quasi-solid-state symmetric supercapacitor device is assembled by using CuMnO2 nanoparticles as both positive electrode and negative electrode. The device exhibits good supercapacitive performance with a high specific capacitance (272 F g-1), a maximum power density of 7.56 kW kg-1 and a superior cycling stability of 18,000 continuous cycles, indicating an excellent potential to be used in energy storage device.

The crystal structure of Cu9.1(1)TeSb3, a stuffed derivative of Cr3Si

DEFF Research Database (Denmark)

Søtofte, Inger; Makovicky, E.; Karup-Møller, Sven

1998-01-01

The intermetallic compound Cu9.1(1)TeSb3 prepared at 973 K is an ordered member of the solid solution Cu64Te31Sb5-Cu70Te8Sb22 which also exists, for more limited composition ranges, between 673 K and 1173 K. It is a stuffed derivative of the structure type A15 (Cr3Si). Te is surrounded by twelve 3....../4-occupied Cu-positions in the vertices of a cubically-deformed icosahedron (Cu-Te = 2.614 Å) which itself is nested in an Sb-icosahedron (Cu-Sb = 2.777 Å (x2) and 2.603 Å). The Sb array corresponds to the Cr array in Cr3Si....

Assessment of the concentration of Cr, Mn and Fe in sediment using ...

African Journals Online (AJOL)

Preferred Customer

determination of levels of Cr, Mn and Fe in sediment samples and the results have ... produced within the plasma emit radiation over a broad spectral range, from UV ... intake [36] and their oxides play important role in the soil for fixing trace ...

Relationship between firewood usage and urinary Cr, Cu and As in informal areas of Cape Town.

Science.gov (United States)

Dalvie, Mohamed Aqiel; Africa, Algernon; Naidoo, Sivapregasen

2013-09-03

The study investigated whether wood usage by informal food vendors and household residents in Cape Town results in the absorption of arsenic (As), chromium (Cr) and copper (Cu) owing to release of these metals in the burning of chromated copper arsenate (CCA)-treated wood. The participants (N=78) selected included an equal number of food vendors and non-vendors from 2 informal settlements. All participants answered a questionnaire concerning exposure and were tested for urinary Cr, Cu and As, while the urine of 29 participants was also tested for toxic As (As(tox)). Multivariate analysis showed that the time spent in close proximity to the wood, as well as the quantity of wood used for cooking and for household use, was weakly positively associated with urinary levels of As, Cr and the sum of As, Cr and Cu. The study provides evidence that use of wood likely to contain CCA as a fuel for informal food outlets and household purposes may increase the absorption of inorganic As, Cu and Cr.

Effect of Cu on microstructure, mechanical properties, corrosion resistance and cytotoxicity of CoCrW alloy fabricated by selective laser melting.

Science.gov (United States)

Lu, Yanjin; Ren, Ling; Xu, Xiongcheng; Yang, Yang; Wu, Songquan; Luo, Jiasi; Yang, Mingyu; Liu, Lingling; Zhuang, Danhong; Yang, Ke; Lin, Jinxin

2018-05-01

In the study, CoCrWCu alloys with differing Cu content (2, 3, 4 wt%) were prepared by selective laser melting using mixture powders consisting of CoCrW and Cu, aiming at investigating the effect of Cu on the microstructures, mechanical properties, corrosion behavior and cytotoxicity. The SEM observations indicated that the Cu content up to 3 wt% caused the Si-rich precipitates to segregate along grain boundaries and in the grains, and EBSD analysis suggested that the Cu addition decreased the recrystallization degree and increased the grain diameter and fraction of big grains. The tensile tests found that the increasing Cu content led to a decrease of mechanical properties compared with Cu-free CoCrW alloy. The electrochemical tests revealed that the addition of Cu shifted the corrosion potential toward nobler positive, but increased the corrosion current density. Also, a more protective passive film was formed when 2 wt% Cu content was added, but the higher Cu content up to 3 wt% was detrimental to the corrosion resistance. It was noted that there was no cytotoxicity for Cu-bearing CoCrW alloys to MG-63 cell and the cells could spread well on the surfaces of studied alloys. Meanwhile, the Cu-bearing CoCrW alloy exhibited an excellent antibacterial performance against E.coli when Cu content was up to 3 wt%. It is suggested that the feasible fabrication of Cu-bearing CoCrW alloy by SLM using mixed CoCrW and Cu powders is a promising candidate for use in antibacterial oral repair products. This current study also can aid in the further design of antibacterial Cu-containing CoCrW alloying powders. Copyright © 2018 Elsevier Ltd. All rights reserved.

CrCuAgN PVD nanocomposite coatings: Effects of annealing on coating morphology and nanostructure

Energy Technology Data Exchange (ETDEWEB)

Liu, Xingguang, E-mail: xingguangliu1@gmail.com [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Iamvasant, Chanon, E-mail: ciamvasant1@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Liu, Chang, E-mail: chang.liu@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom); Matthews, Allan, E-mail: allan.matthews@manchester.ac.uk [Pariser Building - B24 ICAM, School of Materials, The University of Manchester, Manchester, M13 9PL (United Kingdom); Leyland, Adrian, E-mail: a.leyland@sheffield.ac.uk [Department of Materials Science and Engineering, Sir Robert Hadfield Building, The University of Sheffield, Mappin Street, Sheffield, S1 3JD (United Kingdom)

2017-01-15

Highlights: • Coatings with nitrogen content up to 16 at.% exhibit a metallic Cr solid solution, even after post-coat annealing at 300 °C and 500 °C. • At higher N/Cr atomic ratios (approaching Cr{sub 2}N stoichiometry), chromium was still inclined to exist in solid solution with nitrogen, rather than as a ceramic nitride phase, even after annealing at 500 °C. • Transportation of Cu and Ag to the surface depends on annealing temperature, annealing duration, nitrogen concentration and ‘global’ Cu + Ag concentration. • Incorporation of copper appears to be a powerful strategy to enhance Ag mobility at low concentration (∼3 at.% Ag in this study) under moderately high service temperature. • A significant decrease in friction coefficient was obtained at room temperature after annealing, or during sliding wear testing at elevated temperature. - Abstract: CrCuAgN PVD nanocomposite coatings were produced using pulsed DC unbalanced magnetron sputtering. This investigation focuses on the effects of post-coat annealing on the surface morphology, phase composition and nanostructure of such coatings. In coatings with nitrogen contents up to 16 at.%, chromium exists as metallic Cr with N in supersaturated solid solution, even after 300 °C and 500 °C post-coat annealing. Annealing at 300 °C did not obviously change the phase composition of both nitrogen-free and nitrogen-containing coatings; however, 500 °C annealing resulted in significant transformation of the nitrogen-containing coatings. The formation of Ag aggregates relates to the (Cu + Ag)/Cr atomic ratio (threshold around 0.2), whereas the formation of Cu aggregates relates to the (Cu + Ag + N)/Cr atomic ratio (threshold around 0.5). The primary annealing-induced changes were reduced solubility of Cu, Ag and N in Cr, and the composition altering from a mixed ultra-fine nanocrystalline and partly amorphous phase constitution to a coarser, but still largely nanocrystalline structure. It was also

Local structure in (MnS)2x(CuInS2)1-x alloys

International Nuclear Information System (INIS)

Pietnoczka, A.; Bacewicz, R.; Schorr, S.

2006-01-01

Local structure around Mn atoms in (MnS) 2x (CuInS 2 ) 1-x alloys for x≤0.09 has been determined using near-edge and extended X-ray absorption fine structure (XANES and EXAFS) measured at the Mn K-edge. We found that for the Mn concentration up to 9 at% Mn atoms substitute preferentially for indium in the chalcopyrite lattice. The Mn-S bond length is 2.43±0.015 Aa, and is about 2% shorter than the In-S bond length. (copyright 2006 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (Abstract Copyright [2006], Wiley Periodicals, Inc.)

Mechanisms controlling Cu, Fe, Mn, and Co profiles in peat of the Filson Creek Fen, northeastern Minnesota

Science.gov (United States)

Walton-Day, K.; Filipek, L.H.; Papp, C.S.E.

1990-01-01

Filson Creek Fen, located in northeastern Minnesota, overlies a Cu-Ni sulfide deposit. A site in the fen was studied to evaluate the hydrogeochemical mechanisms governing the development of Fe, Mn, Co, and Cu profiles in the peat. At the study site, surface peat approximately 1 m thick is separated from the underlying mineralized bedrock by a 6-12 m thickness of lake and glaciofluvial sediments and till. Concentrations of Fe, Mn, Co, and Cu in peat and major elements in pore water delineate a shallow, relatively oxidized, Cu-rich zone overlying a deeper, reduced, Fe-, Mn-, and Co-rich zone within the peat. Sequential metal extractions from peat samples reveal that 40-55% of the Cu in the shallow zone is associated with organic material, whereas the remaining Cu is distributed between iron-oxide, sulfide, and residual fractions. Sixty to seventy percent of the Fe, Mn, and Co concentrated in the deeper zone occur in the residual phase. The metal profiles and associations probably result from non-steady-state input of metals and detritus into the fen during formation of the peat column. The enrichment of organic-associated Cu in the upper, oxidized zone represents a combination of Cu transported into the fen with detrital plant fragments and soluble Cu, derived from weathering of outcrop and subcrop of the mineral deposit, transported into the fen, and fixed onto organic matter in the peat. The variable stratigraphy of the peat indicates that weathering processes and surface vegetation have changed through time in the fen. The Fe, Mn, and Co maxima at the base of the peat are associated with a maximum in detrital matter content of the peat resulting from a transition between the underlying inorganic sedimentary environment to an organic sedimentary environment. The chemistry of sediments and ground water collected beneath the peat indicate that mobilization of metals from sulfide minerals in the buried mineral deposit or glacial deposits is minimal. Therefore, the

Cu{sub 1.5}Mn{sub 1.5}O{sub 4}-based ceramic spectrally selective coatings for efficient solar absorber applications

Energy Technology Data Exchange (ETDEWEB)

Ma, Pengjun [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China); University of Chinese Academy of Sciences, Beijing, 100049 (China); Geng, Qingfen; Gao, Xianghu [Research & Development Center for Eco-material and Eco-chemistry, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China); Yang, Shengrong [State Key Laboratory of Solid Lubrication, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China); Liu, Gang, E-mail: gangliu@licp.cas.cn [Research & Development Center for Eco-material and Eco-chemistry, Lanzhou Institute of Chemical Physics, Chinese Academy of Sciences, Lanzhou, 730000 (China)

2016-08-05

Cu{sub 1.5}Mn{sub 1.5}O{sub 4}-based ceramic spectrally selective (CSS) coating was deposited on aluminum substrate using a sol–gel dip-coating method. The citric acid introduced in the precursor system lowered the required calcining temperature of crystalline Cu{sub 1.5}Mn{sub 1.5}O{sub 4}. X-Ray diffraction (XRD) peaks of coatings annealed above 450 °C were found to coincide exactly with that of crystalline Cu{sub 1.5}Mn{sub 1.5}O{sub 4} in JCPDS database. By optimizing the withdrawal rate and calcining temperature, coating with spectral selectivity as good as α{sub s} = 0.876 and ε{sub 100} = 0.057 was achieved after only one dipping/annealing cycle. Subjected to an accelerated ageing test at 259 °C, the obtained CSS coating showed an excellent thermally durability with the performance criterion (PC) values below 0.05. - Highlights: • Cu{sub 1.5}Mn{sub 1.5}O{sub 4}-based CSS coating is achieved after only one dipping/annealing cycle. • Cu{sub 1.5}Mn{sub 1.5}O{sub 4} coating is obtained as the annealing temperature reaches to 450 °C. • Cu{sub 1.5}Mn{sub 1.5}O{sub 4} coating exhibits optical parameter: α{sub s} = 0.876 and ε{sub 100} = 0.057. • Cu{sub 1.5}Mn{sub 1.5}O{sub 4} coating shows the excellent stability in low to mid temperature region.

Thermodynamic properties of the solid solutions CuCr/sub 2/S/sub 4/ in Cu/sub 1///sub 2/M/sub 1///sub 2/Cr/sub 2/S/sub 4/ (M=Ga, In)

Energy Technology Data Exchange (ETDEWEB)

Titov, V.V.; Gordeev, I.V.; Kesler, Y.A.; Shchelkotunov, V.A.; Tret' yakov, Y.D.

1985-09-01

Using an adiabatic calorimeter and a quartz dilatometer, the temperature dependences of the heat capacity for the solid solutions CuCr/sub 2/S/sub 4/ in Cu/sub 1///sub 2/M/sub 1///sub 2/Cr/sub 2/S/sub 4/ (M - Ga, In) were determined, the different components of the heat capacity were evaluated, and the thermodynamic parameters of the magnetic transformation were calculated.

Effect of heat treatments on precipitate microstructure and mechanical properties of a CuCrZr alloy

DEFF Research Database (Denmark)

Edwards, D.J.; Singh, Bachu Narain; Tähtinen, S.

2007-01-01

The precipitate microstructure of prime aged CuCrZr was coarsened by overaging to see if the larger precipitates could prevent the initiation of plastic flow localization in irradiated CuCrZr. A number of tensile and fracture toughness specimens of prime aged CuCrZr alloy were given overaging...... carried out at 293, 333 and 573 K. Transmission electron microscopy was used to investigate the effects of overaging, subsequent irradiation and the effect of deformation. The results indicate that the overaging treatment of 873 K for 1 h produced a precipitate microstructure that improved the plastic...

Nanostructural evolution of Cr-rich precipitates in a Cu-Cr-Zr alloy during heat treatment studied by 3 dimensional atom probe

DEFF Research Database (Denmark)

Hatakeyama, Masahiko; Toyama, Takeshi; Nagai, Yasuyoshi

2008-01-01

Nanostructural evolution of Cr (Cr-rich) precipitates in a Cu-0.78%Cr-0.13%Zr alloy has been studied after aging and overaging (reaging) by laser assisted local electrode 3 dimensional atom probe (Laser-LEAP). This material is a candidate for the first wall and divertor components of future fusion...

Influence of Cu Content on the Microstructure and Mechanical Properties of Cr-Cu-N Coatings

Directory of Open Access Journals (Sweden)

Ji Cheng Ding

2018-01-01

Full Text Available The Cr-Cu-N coatings with various Cu contents (0–25.18 (±0.17 at.% were deposited on Si wafer and stainless steel (SUS 304 substrates in reactive Ar+N2 gas mixture by a hybrid coating system combining pulsed DC and RF magnetron sputtering techniques. The influence of Cu content on the coating composition, microstructure, and mechanical properties was investigated. The microstructure of the coatings was significantly altered by the introduction of Cu. The deposited coatings exhibit solid solution structure with different compositions in all of the samples. Addition of Cu is intensively favored for preferred orientation growth along (200 direction by restricting in (111 direction. With increasing Cu content, the surface and cross-sectional morphology of coatings were changed from triangle cone-shaped, columnar feature to broccoli-like and compact glassy microstructure, respectively. The mechanical properties including the residual stress, nanohardness, and toughness of the coatings were explored on the basis of Cu content. The highest hardness was obtained at the Cu content of 1.49 (±0.10 at.%.

Thermodynamic description of the Al-Cu-Mg-Mn-Si quinary system and its application to solidification simulation

International Nuclear Information System (INIS)

Chang, Keke; Liu, Shuhong; Zhao, Dongdong; Du, Yong; Zhou, Liangcai; Chen, Li

2011-01-01

By means of the first-principles calculations, the enthalpy of formation for the quaternary phase in the Al-Cu-Mg-Si system was computed. A set of self-consistent thermodynamic parameters for the Al-Cu-Mg-Si and Al-Cu-Mn-Si systems was then obtained using CALPHAD approach taking into account the reliable experimental data and the first-principles calculations. The thermodynamic database for the Al-Cu-Mg-Mn-Si system was developed based on the constituent binary, ternary, and quaternary systems. Comprehensive comparisons between the calculated and measured phase diagrams and invariant reactions showed that the experimental information was satisfactorily accounted for by the present thermodynamic description. The obtained database was used to describe the solidification behavior of Al alloys B319.1 (90.2Al-6Si-3.5Cu-0.3Mg, in wt.%) and B319.1 + xMn (x = 0.5-2, in wt.%) under Gulliver-Scheil non-equilibrium condition. The reliability of the present thermodynamic database was also verified by the good agreement between calculation and experiment for Gulliver-Scheil non-equilibrium solidification.

Reentrant behavior in Cr doped bilayer manganite LaSr{sub 2}Mn{sub 2}O{sub 7}

Energy Technology Data Exchange (ETDEWEB)

Bhatia, S.N., E-mail: snbhatia@phy.iitb.ac.in; Mohapatra, Niharika

2017-07-15

Highlights: • The FM and the AFM states merge into each other thereby creating an inhomogeneous state. • Cr{sup 3+} creates ferromagnetic moments which behave like FM relaxors. • Electric conduction takes via hopping of small polaron and not by variable range hopping of these polarons. - Abstract: We have studied the effect of replacing Mn{sup 3+} by Cr{sup 3+} on the structure, transport and magnetism in the bilayered manganite LaSr{sub 2}Mn{sub 2}O{sub 7}. Although no structural transition was observed in LaSr{sub 2}Mn{sub 2−y}Cr{sub y}O{sub 7} (0.1 ≤ y ≤ 0.6), the electrical transport and the magnetic properties were found to be affected significantly by this substitution. Substitution of Cr{sup 3+} reduces the conductivity by restricting the hopping of small polarons. Magnetization increases with increasing Cr{sup 3+} concentration suggesting that Cr{sup 3+}-ions induce ferromagnetic moments. The ferromagnetic and an antiferromagnetic phase observed above ∼60 K merge into an inhomogeneous phase below this temperature. Thermopower yields an essentially concentration independent charge density nearly equal to its value for chromium free composition inspite of its expected decrease with this substitution suggesting that the small charge density of the insulating AFM phase is supplemented by the free carriers in the FM phase. The inhomogeneous phase shows a relaxor type behavior which contrasts with the spin glass behavior seen in La{sub 0.46}Sr{sub 0.54}Mn{sub 0.98}Cr{sub 0.02}O{sub 3} having an identical AFM magnetic state. The difference is attributed to the non-JT character of Cr-ions which reduce the distortion of the Mn−O octahedra located within the FM domains. With a higher lattice strain in the surrounding AFM matrix the carriers remain confined within the FM domains leading to the relaxor type behavior.

General synthesis of hierarchical C/MOx@MnO2 (M=Mn, Cu, Co) composite nanofibers for high-performance supercapacitor electrodes.

Science.gov (United States)

Nie, Guangdi; Lu, Xiaofeng; Chi, Maoqiang; Gao, Mu; Wang, Ce

2018-01-01

Improving the conductivity and specific surface area of electrospun carbon nanofibers (CNFs) is beneficial to a rapid realization of their applications in energy storage field. Here, a series of one-dimensional C/MO x (M=Mn, Cu, Co) nanostructures are first prepared by a simple two-step process consisting of electrospinning and thermal treatment. The presence of low-valence MO x enhances the porosity and conductivity of nanocomposites to some extent through expanding graphitic domains or mixing metallic Cu into the CNF substrates. Next, the C/MO x frameworks are coated with MnO 2 nanosheets/nanowhiskers (C/MO x @MnO 2 ), during which process the low-valence MO x can partly reduce KMnO 4 so as to mitigate the consumption of CNFs. When used as active materials for supercapacitor electrodes, the obtained C/MO x @MnO 2 exhibit excellent electrochemical performances in comparison with the common CNFs@MnO 2 (CM) core-shell electrode due to the combination of desired functions of the individual components and the introduction of extra synergistic effect. It is believed that these results will provide an alternative way to further increase the capacitive properties of CNFs- or metal oxide-based nanomaterials and potentially stimulate the investigation on other kinds of C/MO x composite nanostructures for various applications. Copyright © 2017 Elsevier Inc. All rights reserved.

Magnetotransport in La{sub 0.7}Sr{sub 0.3}MnO{sub 3}/CuCr{sub 2}O{sub 4}/Fe{sub 3}O{sub 4} magnetic junctions

Energy Technology Data Exchange (ETDEWEB)

Iwata-Harms, Jodi M.; Suzuki, Yuri [Department of Materials Science and Engineering, University of California, Berkeley, California 94720 (United States); Department of Applied Physics and Geballe Laboratory for Advanced Materials, Stanford University, Stanford, California 94305 (United States); Chopdekar, Rajesh V. [Department of Materials Science and Engineering, University of California, Berkeley, California 94720 (United States); School of Applied and Engineering Physics, Cornell University, Ithaca, New York 14853 (United States); Wong, Franklin J. [Department of Materials Science and Engineering, University of California, Berkeley, California 94720 (United States); Materials Sciences Division, Lawrence Berkeley National Laboratory, Berkeley, California 94720 (United States); Nelson-Cheeseman, Brittany B. [Department of Materials Science and Engineering, University of California, Berkeley, California 94720 (United States); Jenkins, Catherine A.; Arenholz, Elke [Advanced Light Source, Lawrence Berkeley National Laboratory, Berkeley, California 94720 (United States)

2015-01-05

We demonstrate distinct magnetic and resistive switching with junction magnetoresistance up to −6% in magnetic tunnel junctions with a CuCr{sub 2}O{sub 4} barrier. Junction magnetoresistance is inversely related to barrier thickness and reveals a maximum at a finite applied bias that converges to zero bias at low temperatures for all barrier thicknesses. The non-monotonic bias dependence is attributed to a charge gap from the Fe{sub 3}O{sub 4} electrode and possible spin filtering from the spin-split conduction band of the ferrimagnetic CuCr{sub 2}O{sub 4} barrier.

Mechanism and kinetics of Fe, Cr, Mo and Mn atom interaction with molecular oxygen

International Nuclear Information System (INIS)

Akhmadov, U.S.; Zaslonko, I.S.; Smirnov, V.N.

1988-01-01

Rate constants of atomic interaction of some transition metals (Fe, Cr, Mo, Mn) with molecular oxygen are measured in shock waves using the resonance atomic-absorption method. A new method for determination of the parameter γ in the modified Lambert-Beer law D=ε(lN)γ is suggested and applied. Bond strength in CrO and MoO molecules is estimated

Effects of the partial substitution of Ni by Cr on the transport, magnetic, and magnetocaloric properties of Ni50Mn37In13

Directory of Open Access Journals (Sweden)

Sudip Pandey

2017-05-01

Full Text Available The structural, magnetic, and magnetotransport properties of Ni50-xCrxMn37In13 Heusler alloys have been synthesized and investigated by x-ray diffraction (XRD, field and pressure dependent magnetization, and electrical resistivity measurements. The partial substitution of Ni by Cr in Ni50Mn37In13 significantly improves the magnetocaloric effect in the vicinity of the martensitic transition (TM. This system also shows a large negative entropy change at the Curie temperature (TC, making it a candidate material for application in a refrigeration cycle that exploits both positive and negative magnetic entropy changes. The refrigeration capacity (RC values at TM and TC increase significantly by more than 20 % with Cr substitution. The application of hydrostatic pressure increases the temperature stability of the martensitic phase in Ni45Cr5Mn37In13. The influence of Cr substitution on the transport properties of Ni48Cr2Mn37In13 is discussed. An asymmetric magnetoresistance, i.e., a spin-valve-like behavior, has been observed near TM for Ni48Cr2Mn37In13.

The electronic structure and ferromagnetism of TM (TM=V, Cr, and Mn)-doped BN(5, 5) nanotube: A first-principles study

International Nuclear Information System (INIS)

He, K.H.; Zheng, G.; Chen, G.; Wan, M.; Ji, G.F.

2008-01-01

We study the electronic structure and ferromagnetism of V-, Cr-, and Mn-doped single-wall BN(5, 5) nanotube by using polarized spin calculations within first principles. The optimized structures show that the transition-metal atoms move outwards and the calculated electronic properties demonstrate that the isolated V-, Cr-, and Mn-doped BN(5, 5) nanotubes show half-metallicity. The total ferromagnetic moments are 2μ B , 3.02μ B , and 3.98μ B for V-, Cr-, and Mn-doped BN(5, 5), respectively. The study suggests that such transition-metal (TM)-doped nanotubes may be useful in spintronics and nanomagnets

Feasibility of constructed wetland planted with Leersia hexandra Swartz for removing Cr, Cu and Ni from electroplating wastewater.

Science.gov (United States)

You, Shao-Hong; Zhang, Xue-Hong; Liu, Jie; Zhu, Yi-Nian; Gu, Chen

2014-01-01

As a low-cost treatment technology for effluent, the constructed wetlands can be applied to remove the heavy metals from wastewater. Leersia hexandra Swartz is a metal-accumulating hygrophyte with great potential to remove heavy metal from water. In this study, two pilot-scale constructed wetlands planted with L. hexandra (CWL) were set up in greenhouse to treat electroplating wastewater containing Cr, Cu and Ni. The treatment performance of CWL under different hydraulic loading rates (HLR) and initial metal concentrations were also evaluated. The results showed that CWL significantly reduced the concentrations of Cr, Cu and Ni in wastewater by 84.4%, 97.1% and 94.3%, respectively. High HLR decreased the removal efficiencies of Cr, Cu and Ni; however, the heavy metal concentrations in effluent met Emission Standard of Pollutants for Electroplating in China (ESPE) at HLR less than 0.3 m3/m2 d. For the influent of 5 mg/L Cr, 10 mg/L Cu and 8 mg/L Ni, effluent concentrations were below maximum allowable concentrations in ESPE, indicating that the removal of Cr, Cu and Ni by CWL was feasible at considerably high influent metal concentrations. Mass balance showed that the primary sink for the retention of contaminants within the constructed wetland system was the sediment, which accounted for 59.5%, 83.5%, and 73.9% of the Cr, Cu and Ni, respectively. The data from the pilot wetlands support the view that CWL could be used to successfully remove Cr, Cu and Ni from electroplating wastewater.

Controlled facile synthesis of hierarchical CuO@MnO{sub 2} core–shell nanosheet arrays for high-performance lithium-ion battery

Energy Technology Data Exchange (ETDEWEB)

Chen, Qing; Heng, Bojun; Wang, Hai; Sun, Daming; Wang, Bixiao; Sun, Miao; Guan, Shunli; Fu, Ranyan; Tang, Yiwen, E-mail: ywtang@phy.ccnu.edu.cn

2015-08-25

Highlights: • We have facile synthesized the CuO@MnO{sub 2} nanosheet array directly on Cu substrate. • This core–shell structure was assembled as a full cell (vs LiCoO{sub 2}) for the first time. • The full cell exhibits a 127 mA h g{sup −1} at the 150 mA g{sup −1} after 100 cycle. • This strategy can be generalized to construct other hybrid nanostructures. - Abstract: We report a facile, rapid and low-cost two step approach to synthesize hierarchical CuO@MnO{sub 2} core–shell nanosheet arrays directly on Cu foil substrate. The as prepared CuO@MnO{sub 2} arrays can be directly used as integrated electrodes. Furthermore, the CuO@MnO{sub 2} nanosheet arrays were assembled with the commercial Li Ion Battery Cathode (LiCoO{sub 2}) as a full cell, which exhibited high capacity and good cycle stability (120 mA h g{sup −1} after 100 cycles at a rate of 150 mA g{sup −1}) and an excellent rate performance (a stable capacity of about 127 mA h g{sup −1} after 100 cycles of variable charging rate). The excellent performance of the CuO@MnO{sub 2} hybrids comes from their intelligent integration of the two compatible components into unique hierarchical architectures with a high specific capacity. Primary single-crystalline CuO nanosheet arrays directly grown on Cu substrates allow for efficient electrical and ionic transport. The secondary MnO{sub 2} shell provide enhanced surface area and high theoretical Li{sup +} storage capacity, and can also serve as volume spacers between neighboring CuO nanosheet arrays to maintain electrolyte penetration as well as reduce the aggregation during Li{sup +} intercalation, thus leading to improved electrochemical energy storage performance.

The quasicrystalline phase formation in Al-Cu-Cr alloys produced by mechanical alloying

Energy Technology Data Exchange (ETDEWEB)

Sviridova, T.A.; Shevchukov, A.P.; Shelekhov, E.V. [National University of Science and Technology ' MISIS' , Moscow 119049 (Russian Federation); Diakonov, D.L. [Bardin Central Research Institute for the Iron and Steel Industry, Moscow 105005 (Russian Federation); Tcherdyntsev, V.V.; Kaloshkin, S.D. [National University of Science and Technology ' MISIS' , Moscow 119049 (Russian Federation)

2011-06-15

Research highlights: > Formation of decagonal quasicrystalline phase in Al-Cu-Cr alloys. > Obtained decagonal phase belongs to D{sub 3} family of decagonal quasicrystals. > Decagonal phase has 1.26 nm periodicity along 10-fold axis. > Alloys were produced by combination of mechanical alloying and subsequent annealing. > Phase composition of as-milled powders depending on annealing temperature. - Abstract: Almost single-phase decagonal quasicrystal with periodicity of 1.26 nm along 10-fold axis was produced in Al{sub 69}Cu{sub 21}Cr{sub 10} and Al{sub 72.5}Cu{sub 16.5}Cr{sub 11} alloys using combination of mechanical alloying (MA) and subsequent annealing. Phase transformations of as-milled powders depending on annealing temperature in the range of 200-800 deg. C are examined. Since the transformations can be explained based on kinetic and thermodynamic reasons it seems that applied technique (short preliminary MA followed by the annealing) permits to produce the equilibrium phases rather than metastable ones.

Electronic, Structural, and Electrochemical Properties of LiNixCuyMn2-x-yO4 (0 < x < 0.5, 0 < y < 0.5) High-Voltage Spinel Materials

International Nuclear Information System (INIS)

Yang, Ming-Che; Xu, Bo; Cheng, Ju-Hsiang; Pan, Chun-Jern; Hwang, Bing-Joe; Meng, Ying S.

2011-01-01

First principles computation is carried out for investigating the electronic, structural, and electrochemical properties of LiM 1/2 Mn 3/2 O 4 (M = Ti, V, Cr, Fe, Co, Ni, and Cu). The computation results suggest that doping with Co or Cu can potentially lower Li diffusion barrier as compared to Ni doping. Our experimental research has focused on LiNi x Cu y Mn 2-x-y O 4 (0 x Cu y Mn 2-x-6 O 4 (0 0.25 Cu 0.25 Mn 1.50 O 4 , the proposed explanation of the voltage profile by the first principles computation was proven, a second plateau at 4.2 V originates from the oxidation of Cu 2+ to Cu 3+ , and the plateau at 4.95 V may originate from extra electrons provided by oxygen ions. Although the reversible discharge capacity decreases with increasing Cu amount, optimized composition such as LiCu 0.25 Ni 0.25 Mn 1.5 O 4 exhibits high capacities at high rates.

Determination of chemical activities of Fe, Cr, Ni and Mn in stainless steel 316 by Knudsen effusion cell mass spectrometry

International Nuclear Information System (INIS)

Venugopal, V.; Kulkarni, S.G.; Subbanna, C.S.; Sood, D.D.

1995-01-01

Cold-worked austenitic stainless steel of the type AISI 316 is being used as the cladding and wrapper materials in fast reactor fuel pins. Knowledge of the thermodynamic activities of the steel constituents is necessary to predict the possibility of fuel-cladding, coolant-cladding or fission product-cladding chemical reactions. The thermodynamic activities of Fe, Cr, Ni and Mn for stainless steel 316 were determined by measuring their partial pressures in the temperature range 1293-2120 K, using Knudsen effusion cell mass spectrometry. High purity Ag was used as an internal calibrant. The chemical activities of Fe (a Fe ), Cr (a Cr ), Ni (a Ni ) and Mn (a Mn ) were evaluated using literature data for the vapour pressures of pure metals. log a Fe ±0.18=-1.586+2074/T (T=1293-1872 K)log a Cr ±0.30=-2.350+2612/T (T=1293-2120 K)log a Ni ±0.20=-2.140+1794/T (T=1468-1974 K)log a Mn ±0.23=-2.041-5478/T (T=1302-1894 K) ((orig.))

Precipitation strengthened high strength, high conductivity Cu-Cr-Nb alloys produced by chill block melt spinning. Final Report Ph.D. Thesis

Science.gov (United States)

Ellis, David L.; Michal, Gary M.

1989-01-01

A series of Cu-based alloys containing 2 to 10 a/o Cr and 1 to 5 a/o Nb were produced by chill block melt spinning (CBMS). The melt spun ribbons were consolidated and hot rolled to sheet to produce a supersaturated Cu-Cr-Nb solid solution from which the high melting point intermetallic compound Cr2Nb could be precipitated to strengthen the Cu matrix. The results show that the materials possess electrical conductivities in excess of 90 percent that of pure Cu at 200 C and above. The strengths of the Cu-Cr-Nb alloys were much greater than Cu, Cu-0.6 Cr, NARloy-A, and NARloy-Z in the as-melt spun condition. The strengths of the consolidated materials were less than Cu-Cr and Cu-Cr-Zr below 500 C and 600 C respectively, but were significantly better above these temperatures. The strengths of the consolidated materials were greater than NARloy-Z, at all temperatures. The GLIDCOP possessed similar strength levels up to 750 C when the strength of the Cu-Cr-Nb alloys begins to degrade. The long term stability of the Cu-Cr-Nb alloys was measured by the microhardness of aged samples and the growth of precipitates. The microhardness measurements indicate that the alloys overage rapidly, but do not suffer much loss in strength between 10 and 100 hours which confirms the results of the electrical resistivity measurements taken during the aging of the alloys at 500 C. The loss in strength from peak strength levels is significant, but the strength remains exceptionally good. Transmission electron microscopy (TEM) of the as-melt spun samples revealed that Cr2Nb precipitates formed in the liquid Cu during the chill block melt spinning, indicating a very strong driving force for the formation of the precipitates. The TEM of the aged and consolidated materials indicates that the precipitates coarsen considerably, but remain in the submicron range.

Development of half metallicity within mixed magnetic phase of Cu1‑x Co x MnSb alloy

Science.gov (United States)

Bandyopadhyay, Abhisek; Neogi, Swarup Kumar; Paul, Atanu; Meneghini, Carlo; Bandyopadhyay, Sudipta; Dasgupta, Indra; Ray, Sugata

2018-05-01

Cubic half-Heusler Cu1‑x Co x MnSb () compounds have been investigated both experimentally and theoretically for their magnetic, transport and electronic properties in search of possible half metallic antiferromagnetism. The systems (Cu,Co)MnSb are of particular interest as the end member alloys CuMnSb and CoMnSb are semi metallic (SM) antiferromagnetic (AFM) and half metallic (HM) ferromagnetic (FM), respectively. Clearly, Co-doping at the Cu-site of CuMnSb introduces changes in the carrier concentration at the Fermi level that may lead to half metallic ground state but there remains a persistent controversy whether the AFM to FM transition occurs simultaneously. Our experimental results reveal that the AFM to FM magnetic transition occurs through a percolation mechanism where Co-substitution gradually suppresses the AFM phase and forces FM polarization around every dopant cobalt. As a result a mixed magnetic phase is realized within this composition range while a nearly HM band structure is developed already at the 10% Co-doping. Absence of T 2 dependence in the resistivity variation at low T-region serves as an indirect proof of opening up an energy gap at the Fermi surface in one of the spin channels. This is further corroborated by the ab initio electronic structure calculations that suggests that a nearly ferromagnetic half-metallic ground state is stabilized by Sb-p holes produced upon Co doping.

Kinetics of bainite precipitation in the Cu{sub 69.3}Al{sub 18.8}Mn{sub 10.3}Ag{sub 1.6} alloy

Energy Technology Data Exchange (ETDEWEB)

Motta, M.B.J.L. [Departamento de Ciências Exatas e da Terra, UNIFESP, Diadema, SP (Brazil); Adorno, A.T.; Santos, C.M.A. [Departamento de Físico-Química, IQ-UNESP, Araraquara, SP (Brazil); Silva, R.A.G., E-mail: galdino.ricardo@gmail.com [Departamento de Ciências Exatas e da Terra, UNIFESP, Diadema, SP (Brazil)

2017-02-15

In this work the kinetics of bainite precipitation in the Cu{sub 69.3}Al{sub 18.8}Mn{sub 10.3}Ag{sub 1.6} alloy was studied using measurements of microhardness change with aging time, scanning electron microscopy (SEM), energy dispersive X-ray (EDX) analyses, measurements of magnetization change with applied field and high-resolution transmission electron microscopy (HRTEM). The results showed that the bainite precipitation is responsible for the hardness increase in the Cu{sub 69.3}Al{sub 18.8}Mn{sub 10.3}Ag{sub 1.6} alloy. The activation energy value obtained for the bainite precipitation is lower than that found in the literature. This was attributed to the presence of Ag dissolved in matrix and the occurrence of the Cu{sub 3}Al(DO{sub 3}) → Cu{sub 2}AlMn(L2{sub 1}) ordering reaction together with the bainite precipitation. - Highlights: • The activation energy for the bainite precipitation in the Cu{sub 69.3}Al{sub 18.8}Mn{sub 10.3}Ag{sub 1.6} alloy is around 33 kJ/mol. • During bainite precipitation the Cu{sub 2}AlMn phase formation occurs. • The Cu{sub 3}Al(DO{sub 3}) → Cu{sub 2}AlMn(L2{sub 1}) ordering reaction interferes in the activation energy value.

Proximity effects on the spin density waves in X/Cr(001) multilayers (X = Sn, V, and Mn)

Energy Technology Data Exchange (ETDEWEB)

Amitouche, F. [Laboratoire de Physique et Chimie Quantique, Universite Mouloud Mammeri de Tizi-Ouzou, B.P. No17 RP, 15000 Tizi-Ouzou (Algeria); Bouarab, S., E-mail: bouarab_said@mail.ummto.d [Laboratoire de Physique et Chimie Quantique, Universite Mouloud Mammeri de Tizi-Ouzou, B.P. No17 RP, 15000 Tizi-Ouzou (Algeria); Tazibt, S. [Laboratoire de Physique et Chimie Quantique, Universite Mouloud Mammeri de Tizi-Ouzou, B.P. No17 RP, 15000 Tizi-Ouzou (Algeria); Vega, A. [Departamento de Fisica Teorica, Atomica y Optica, Universidad de Valladolid, Prado de la Magdalena s/n, E-47011 Valladolid (Spain); Demangeat, C. [Institut de Physique, 3 rue de l' Universite 67000 Strasbourg (France)

2011-01-03

We present ab initio density functional calculations of the electronic structure and magnetic properties of X{sub 2}/Cr{sub 36}(001) and X{sub 1}/Cr{sub 37}(001) multilayers, with X = Sn, V and Mn, to investigate the impact of the proximity effects of the X layers on the spin density waves of the Cr slab. We find different magnetic profiles corresponding to the spin density wave and to the layered antiferromagnetic configurations. The nature of the different magnetic solutions is discussed in terms of the different interfacial environments in the proximity of Sn, V or Mn. The magnetic behavior at the interface is discussed in connection with the electronic structure through the density of electronic states projected at the interfacial X and Cr sites. We compare the results with those previously obtained for Fe{sub 3}/X{sub 1}/Cr{sub 37}/X{sub 1}(001) multilayers to analyze the role played by the ferromagnetic iron slab.

Proximity effects on the spin density waves in X/Cr(001) multilayers (X = Sn, V, and Mn)

International Nuclear Information System (INIS)

Amitouche, F.; Bouarab, S.; Tazibt, S.; Vega, A.; Demangeat, C.

2011-01-01

We present ab initio density functional calculations of the electronic structure and magnetic properties of X 2 /Cr 36 (001) and X 1 /Cr 37 (001) multilayers, with X = Sn, V and Mn, to investigate the impact of the proximity effects of the X layers on the spin density waves of the Cr slab. We find different magnetic profiles corresponding to the spin density wave and to the layered antiferromagnetic configurations. The nature of the different magnetic solutions is discussed in terms of the different interfacial environments in the proximity of Sn, V or Mn. The magnetic behavior at the interface is discussed in connection with the electronic structure through the density of electronic states projected at the interfacial X and Cr sites. We compare the results with those previously obtained for Fe 3 /X 1 /Cr 37 /X 1 (001) multilayers to analyze the role played by the ferromagnetic iron slab.

Secondary ordering in ternary alloy CuMnPt6

International Nuclear Information System (INIS)

Takahashi, Miwako; Das, Ananda Kumar; Nakamura, Reo; Ohshima, Ken-ichi; Iwasaki, Hiroshi; Shishido, Toetsu

2006-01-01

Using the pulsed-neutron diffraction technique, we performed in situ measurements of structural ordering in the ternary alloy CuMnPt 6 . The diffraction patterns at various temperatures give a direct observation of a double-step ordering: disorder to Cu 3 Au type order as an ordering within the fundamental face-centered cubic lattice to subdivide the lattice into two sublattices formed by face-centered sites (first sublattice) and corner sites (second sublattice) at 968degC; and Cu 3 Au type order to ABC 6 type order as an ordering within the second to subdivide the lattice further into two sublattices formed by alternating (111) planes at 746degC. The order parameters for the ABC 6 type structure experimentally estimated by the method of static concentration waves indicate that the primary ordering developed almost completely, but the secondary ordering remained incomplete. (author)

Synthesis, Magnetization, and Electrical Transport Properties of Mn3Zn0.9Cu0.1N

Directory of Open Access Journals (Sweden)

Y. Yin

2013-01-01

Full Text Available We synthesized Mn3Zn0.9Cu0.1N by solid state reaction, and magnetic as well as electrical transport properties were investigated. It is found that Mn3Zn0.9Cu0.1N exhibits a first-order antiferromagnetism (AFM to paramagnetic (PM transition with the Néel temperature TN ~163 K, and substitution of Cu for Zn would favor ferromagnetism (FM state and weaken AFM ground state, leading to a convex curvature character of M(T curve. With high external fields 10 kOe–50 kOe, magnetic transition remains a robust AFM-PM feature while FM phase is completely suppressed. Thermal hysteresis of M(T under 500 Oe is also suppressed when the magnetic field exceeds 10 kOe. Mn3Zn0.9Cu0.1N exhibits a good metallic behavior except for a slope change around TN, which is closely related to AFM-PM magnetic transition. Compared with the first differential of resistivity with respect to temperature for (dρ/dTMn3ZnN in transition temperature range, the absolute value of (dρ/dTMn3Zn0.9Cu0.1N is much lower which is close to zero.

On the Path to Optimizing the Al-Co-Cr-Cu-Fe-Ni-Ti High Entropy Alloy Family for High Temperature Applications

Directory of Open Access Journals (Sweden)

Anna M. Manzoni

2016-03-01

Full Text Available The most commonly investigated high entropy alloy, AlCoCrCuFeNi, has been chosen for optimization of its microstructural and mechanical properties by means of compositional changes and heat treatments. Among the different available optimization paths, the decrease of segregating element Cu, the increase of oxidation protective elements Al and Cr and the approach towards a γ-γ′ microstructure like in Ni-based superalloys have been probed and compared. Microscopical observations have been made for every optimization step. Vickers microhardness measurements and/or tensile/compression test have been carried out when the alloy was appropriate. Five derived alloys AlCoCrFeNi, Al23Co15Cr23Cu8Fe15Ni16, Al8Co17Cr17Cu8Fe17Ni33, Al8Co17Cr14Cu8Fe17Ni34.8Mo0.1Ti1W0.1 and Al10Co25Cr8Fe15Ni36Ti6 (all at.% have been compared to the original AlCoCrCuFeNi and the most promising one has been selected for further investigation.

Adsorption of Cu(II) and Cr(VI) ions by chitosan: kinetics and ...

African Journals Online (AJOL)

The ability of chitosan as an adsorbent for Cu (II) and Cr (VI) ions in aqueous solution was studied. The experiments were done as batch processes. Equilibrium studies were done on both cross-linked and non-cross-linked chitosan for both metals. Cr (VI) adsorption behaviour could be described using the Langmuir ...

Anomalous superconducting spin-valve effect in NbN/FeN/Cu/FeN/FeMn multilayers

Energy Technology Data Exchange (ETDEWEB)

Hwang, Tae Jong; Kim, Dong Ho [Yeungnam University, Gyeongsan (Korea, Republic of)

2017-09-15

We have studied magnetic and transport properties of NbN/FeN/Cu/FeN/FeMn spin-valve structure. In-plane magnetic moment exhibited typical hysteresis loops of spin valves in the normal state of NbN film at 20 K. On the other hand, the magnetic hysteresis loop in the superconducting state exhibited more complex behavior in which exchange bias provided by antiferrmagnetic FeMn layer to adjacent FeN layer was disturbed by superconductivity. Because of this, the ideal superconducting spin-valve effect was not detected. Instead the stray field originated from unsaturated magnetic states dominated the transport properties of NbN/FeN/Cu/FeN/FeMn multilayer.

OPTIMIZATION OF STEEL SATURATION PROCESSES USING CARBIDE-FORMING ELEMENTS IN SYSTEMS BASED ON Cr-Ti-V AND Cr-Ti-Mn

Directory of Open Access Journals (Sweden)

A. A. Shmatov

2007-01-01

Full Text Available Optimization of saturating mixture compositions has been carried out in two three-component systems, namely: Cr-Ti-V and Cr-Ti-Mn in respect of micro-hardness and wear resistance of carbide coatings obtained by thermo-chemical treatment of high carbon steel. «Composition - properties» diagrams have been plotted using mathematical models. Treatment with optimum compositions of powder media permits to increase wear resistance of steel by factor of 30-70 as compared with untreated steel. 

Determination of Mn, Fe, and Cu in chemically-treated wood pulps by the XRF addition method

Energy Technology Data Exchange (ETDEWEB)

Raemoe, J.; Klasila, T.; Piepponen, S. [VTT Chemical Technology (Finland); Sillanpaeae, M. [Oulu Univ. (Finland)

2001-08-01

A rapid X-ray fluorescence addition method has been developed for quantification of the technically most important metals in wood pulp matrix (Mn, Fe, and Cu). Pretreatment consisted of just two steps: first, acid was added to the sample to achieve homogeneous distribution of the metals; the pulp was then pressed lightly on to Mylar film. Total analysis time was less than 10 min. The concentration range investigated was up to 15 mg kg{sup -1} for Mn and up to 5 mg kg{sup -1} for Fe and Cu. Metal concentrations in Scandinavian pulps are not expected to exceed these amounts. The quantification limit was 2 mg kg{sup -1} for all three metals. The reproducibilities and repeatabilities were concentration-dependent and varied between 3 and 19% and between 1 and 17%, respectively. The squares of the linear correlation coefficients between measured intensity and added metal concentration were 0.994, 0.950, and 0.932 for Mn, Fe, and Cu, respectively. (orig.)

Ecological modelling of a wetland for phytoremediating Cu, Zn and Mn in a gold–copper mine site using Typha domingensis (Poales: Typhaceae near Orange, NSW, Australia

Directory of Open Access Journals (Sweden)

Subrahmanyam Sreenath

2017-12-01

Full Text Available An artificial wetland was computationally modelled using STELLA®, a graphical programming tool for an Au-Cu mine site in Central-west NSW, the aim of which was to offer a predictive analysis of a proposed wetland for Cu, Zn and Mn removal using Typha domingensis as the agent. The model considers the important factors that impact phytoremediation of Cu, Zn and Mn. Simulations were performed to optimise the area of the wetland; concentration of Cu, Zn and Mn released from mine (AMD; and flow rates of water for maximum absorption of the metals. A scenario analysis indicates that at AMD = 0.75mg/L for Cu, Zn and Mn, 12.5, 8.6, and 357.9 kg of Cu, Zn and Mn, respectively, will be assimilated by the wetland in 35 years, which would be equivalent to 61 mg of Cu/kg, 70 mg of Zn/kg and 2,886 mg of Mn/kg of T. domingensis, respectively. However, should Cu, Zn and Mn in AMD increase to 3 mg/L, then 18.6 kg of Cu and 11.8 kg of Zn, respectively, will be assimilated in 35 years, whereas no substantial increase in absorption for Mn would occur. This indicates that 91 mg of Cu, 96 mg of Zn and 2917 mg of Mn will be assimilated for every kg of T. domingensis in the wetland. The best option for Cu storage would be to construct a wetland of 50,000 m2 area (AMD = 0.367 mg/L of Cu, which would capture 14.1 kg of Cu in 43 years, eventually releasing only 3.9 kg of Cu downstream. Simulations performed for a WA of 30,000 m2 indicate that for AMD = 0.367 mg/L of Zn, the wetland captures 6.2 kg, releasing only 3.5 kg downstream after 43 years; the concentration of Zn in the leachate would be 10.2 kg, making this the most efficient wetland amongst the options considered for phytoremediating Zn. This work will help mine managers and environmental researchers in developing an effective environmental management plan by focusing on phytoremediation, with a view at extracting Cu, Zn and Mn from the contaminated sites.

Tensile and high cycle fatigue behaviors of high-Mn steels at 298 and 110 K

Energy Technology Data Exchange (ETDEWEB)

Seo, Wongyu; Jeong, Daeho; Sung, Hyokyung; Kim, Sangshik, E-mail: sang@gnu.ac.kr

2017-02-15

Tensile and high cycle fatigue behaviors of high-Mn austenitic steels, including 25Mn, 25Mn0.2Al, 25Mn0.5Cu, 24Mn4Cr, 22Mn3Cr and 16Mn2Al specimens, were investigated at 298 and 110 K. Depending on the alloying elements, tensile ductility of high-Mn steels either increased or decreased with decreasing temperature from 298 to 110 K. Reasonable correlation between the tendency for martensitic tranformation, the critical twinning stress and the percent change in tensile elongation suggested that tensile deformation of high-Mn steels was strongly influenced by SFE determining TRIP and TWIP effects. Tensile strength was the most important parameter in determining the resistance to high cycle fatigue of high-Mn steels with an exceptional work hardening capability at room and cryogenic temperatures. The fatigue crack nucleation mechanism in high-Mn steels did not vary with decreasing tempertature, except Cr-added specimens with grain boundary cracking at 298 K and slip band cracking at 110 K. The EBSD (electron backscatter diffraction) analyses suggested that the deformation mechanism under fatigue loading was significantly different from tensile deformation which could be affected by TRIP and TWIP effects. - Highlights: •The resistances to HCF of various high-Mn steels were measured. •The variables affecting tensile and HCF behaviors of high-Mn steels were assessed. •The relationship between tensile and the HCF behaviors of high-Mn steels was established.

Assessment of the concentration of Cr, Mn and Fe in sediment using ...

African Journals Online (AJOL)

In the present study, laser-induced breakdown spectroscopy (LIBS) has been applied for the determination of levels of Cr, Mn and Fe in sediment samples and the results have been compared with that of flame-atomic absorption spectroscopy (F-AAS). Fourteen sediment samples were collected from Tinishu Akaki River ...

Efficient band structure modulations in two-dimensional MnPSe3/CrSiTe3 van der Waals heterostructures

Science.gov (United States)

Pei, Qi; Wang, Xiaocha; Zou, Jijun; Mi, Wenbo

2018-05-01

As a research upsurge, van der Waals (vdW) heterostructures give rise to numerous combined merits and novel applications in nanoelectronics fields. Here, we systematically investigate the electronic structure of MnPSe3/CrSiTe3 vdW heterostructures with various stacking patterns. Then, particular attention of this work is paid on the band structure modulations in MnPSe3/CrSiTe3 vdW heterostructures via biaxial strain or electric field. Under a tensile strain, the relative band edge positions of heterostructures transform from type-I (nested) to type-II (staggered). The relocation of conduction band minimum also brings about a transition from indirect to direct band gap. Under a compressive strain, the electronic properties change from semiconducting to metallic. The physical mechanism of strain-dependent band structure may be ascribed to the shifts of the energy bands impelled by different superposition of atomic orbitals. Meanwhile, our calculations manifest that band gap values of MnPSe3/CrSiTe3 heterostructures are insensitive to the electric field. Even so, by applying a suitable intensity of negative electric field, the band alignment transition from type-I to type-II can also be realized. The efficient band structure modulations via external factors endow MnPSe3/CrSiTe3 heterostructures with great potential in novel applications, such as strain sensors, photocatalysis, spintronic and photoelectronic devices.

Synthesis and Characterization of High-Entropy Alloy AlFeCoNiCuCr by Laser Cladding

Directory of Open Access Journals (Sweden)

Xiaoyang Ye

2011-01-01

Full Text Available High-entropy alloys have been recently found to have novel microstructures and unique properties. In this study, a novel AlFeCoNiCuCr high-entropy alloy was prepared by laser cladding. The microstructure, chemical composition, and constituent phases of the synthesized alloy were characterized by SEM, EDS, XRD, and TEM, respectively. High-temperature hardness was also evaluated. Experimental results demonstrate that the AlFeCoNiCuCr clad layer is composed of only BCC and FCC phases. The clad layers exhibit higher hardness at higher Al atomic content. The AlFeCoNiCuCr clad layer exhibits increased hardness at temperature between 400–700°C.

Thermoelectric properties of layered antiferromagnetic CuCrSe2

International Nuclear Information System (INIS)

Tewari, Girish C.; Tripathi, T.S.; Yamauchi, Hisao; Karppinen, Maarit

2014-01-01

Here we study thermoelectric and magnetic properties of CuCrSe 2 samples sintered at various temperatures. Structural analysis with XRD shows an order-disorder transition for Cr atoms when the sintering temperature is increased above 1273 K. Metal-like electrical resistivity and anomalously large Seebeck coefficient are found about room temperature. Analysis of electrical conductivity and Seebeck coefficient of the partially-disordered phase suggests hopping conduction of charge carriers. For both the ordered and disordered phases magnetic susceptibility follows Curie–Weiss temperature dependence at high temperatures above 150 K and shows an antiferromagnetic transition around 55 K. For the disordered phase, the effective magnetic moment is determined at 3.62 μ B ; this low value in comparison to the spin only value for Cr 3+ of 3.89 μ B indicates spin fluctuations in the paramagnetic state. The thermal conductivity in these phases is low and dominated by the lattice contribution. Values for the thermoelectric figure of merit (ZT) at room temperature are estimated to be 0.17 and 0.05 for the ordered and disordered phases, respectively. - Highlights: • Thermoelectric and magnetic properties of CuCrSe 2 samples are investigated. • The properties strongly depend on the degree of order of chromium atoms. • The degree of order is controlled by the sintering temperature. • Room-temperature figure of merit is estimated at 0.17 for the ordered phase. • For the disordered phase the figure of merit is lower

Nano-twin mediated plasticity in carbon-containing FeNiCoCrMn high entropy alloys

Energy Technology Data Exchange (ETDEWEB)

Wu, Z. [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Materials Science and Engineering Department, University of Tennessee, Knoxville, TN 37996 (United States); Parish, C.M. [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States); Bei, H., E-mail: beih@ornl.gov [Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, TN 37831 (United States)

2015-10-25

Equiatomic FeNiCoCrMn alloy has been reported to exhibit promising strength and ductility at cryogenic temperature and deformation mediated by nano-twining appeared to be one of the main reasons. We use the FeNiCoCrMn alloy as a base alloy to seek further improvement of its mechanical properties by alloying additional elements, i.e., interstitial carbon. The effects of carbon on microstructures, mechanical properties and twinning activities were investigated in two different temperatures (77 and 293 K). With addition of 0.5 at% C, the high entropy alloy still remains entirely single phase face-centered cubic (FCC) crystal structure. The materials can be cold rolled and recrystallized to produce a microstructure with equiaxed grains. Both strain hardening rate and strength are enhanced while high uniform elongations to fracture (∼70% at 77 K and ∼40% at 293 K) are still maintained. The increased strain hardening and strength could be caused by the promptness of deformation twinning in C-containing high entropy alloys. - Highlights: • Interstitial atom C was successfully added into FeNiCoCrMn high entropy alloys. • The strain hardening rate and strength are enhanced in the C-containing alloy. • The increased strain-hardening and strength are caused by the nano-twinning.

Cathodoluminescence and Thermoluminescence of Undoped LTB and LTB:A (A = Cu, Ag, Mn)

Science.gov (United States)

2013-03-01

and Mn Ions for Nonlinear Applications.” Acta Physica Polonica A 107, no. 3 (2005): 507-518. [22] Kimball Physics, Inc.. Operator’s Manual: EMG...CATHODOLUMINESCENCE AND THERMOLUMINESCENCE OF UNDOPED LTB AND LTB:A ( A = Cu, Ag, Mn) THESIS Zachary L. Hadfield, USA AFIT-ENP-13-M-13...STATEMENT A . APPROVED FOR PUBLIC RELEASE; DISTRIBUTION UNLIMITED The views expressed in this thesis are those of the author and

Kondo effect and spin-glass freezing of the magnetic impurities Cr, Mn, and Fe in superconducting palladium hydride

International Nuclear Information System (INIS)

van Dongen, J.C.M.; van Dijk, D.; Mydosh, J.A.

1981-01-01

Through low-field ac susceptibility measurements we have determined the depression of the superconducting transition temperature T/sub c/ in palladium hydride (T/sub c/0 = 9.3 K) as a function of impurity concentration x for Cr, Mn, and Fe. For Cr and Fe similar values for the initial T/sub c/ depression were found, i.e., -150 K/at. % Cr and -145 K/at. % Fe. From resistivity experiments we are able to estimate the Kondo temperatures T/sub K/, i.e., T/sub K/approx. =10 K for Cr and T/sub K/approx. =5 K for Fe. Since i.e., T/sub K/approx. =10 K for Cr and T/sub K/approx. =5 K for Fe. Since systems exhibits an enhanced pair breaking as described by the theory of Mueller-Hartmann and Zittartz. In contrast, for Mn the initial T/sub c/ depression is -21 K/at. % and T/sub K/<< T/sub c/0, as can be concluded from our resistivity measurements. This means that Mn in PdH exhibits a temperature-independent pair breaking of the Abrikosov and Gor'kov type. However, at larger Mnx values a shoulder appears in T/sub c/(x). We interpret this enhanced superconductivity, according to the theory of Soukoulis and Grest, as being due to the onset of time correlations and short-range antiferromagnetic ordering between the Mn moments. These interaction effects are a precursor to the spin-glass freezing at a lower temperature T/sub f/. Our results suggest a favorable coexistance of superconductivity with the spin-glass state

Catalytic role of Cu(II) in the reduction of Cr(VI) by citric acid under an irradiation of simulated solar light.

Science.gov (United States)

Li, Ying; Chen, Cheng; Zhang, Jing; Lan, Yeqing

2015-05-01

The catalytic role of Cu(II) in the reduction of Cr(VI) by citric acid with simulated solar light was investigated. The results demonstrated that Cu(II) could significantly accelerate Cr(VI) reduction and the reaction obeyed to pseudo zero-order kinetics with respect to Cr(VI). The removal of Cr(VI) was related to the initial concentrations of Cu(II), citric acid, and the types of organic acids. The optimal removal of Cr(VI) was achieved at pH 4, and the rates of Cu(II) photocatalytic reduction of Cr(VI) by organic acids were in the order: tartaric acid (two α-OH groups, two -COOH groups)>citric acid (one α-OH group, three -COOH groups)>malic acid (one α-OH group, two -COOH groups)>lactic acid (one α-OH group, one -COOH group)≫succinic acid (two -COOH groups), suggesting that the number of α-OH was the key factor for the reaction, followed by the number of -COOH. The formation of Cu(II)-citric acid complex could generate Cu(I) and radicals through a pathway of metal-ligand-electron transfer, promoting the reduction of Cr(VI). This study is helpful to fully understanding the conversion of Cr(VI) in the existence of both organic acids and Cu(II) with solar light in aquatic environments. Copyright © 2015 Elsevier Ltd. All rights reserved.

Magnetocaloric behavior of Mn rich Ni46Cu2Mn43In11 alloy

Science.gov (United States)

Ray, Mayukh K.; Obaidat, I. M.; Banerjee, Sangam

2018-02-01

In this work, we studied the magnetic entropy change (ΔSM) across the martensite transformation (MT) in Mn-rich Ni46Cu2Mn43ln11 alloy. This compound undergoes a MT and a magnetic phase transition around the temperatures (TM=) 272 K and (TCA=) 325 K, respectively. A large field induced shift (=0.28 K/kOe) of the MT temperatures is observed. An application of magnetic field (H =) of 50 kOe causes a large ΔSM of 20 J/kg-K and -4.4 J/kg-K around TM and TCA, respectively. We also found that the change in magnetic field induced isothermal ΔSM(H)T is mainly depends on the induced austenite phase fraction by the applied magnetic field at that temperature. Possible reasons for the observed behaviours are comprehensively discussed.

An experimental investigation of ionic transport properties in CuI-Ag2WO4 and CuI-Ag2CrO4 mixed systems

International Nuclear Information System (INIS)

Suthanthiraraj, S. Austin; Premchand, Y. Daniel

2004-01-01

The phenomenon of ionic transport in the case of two different mixed systems (CuI) (1-x) -(Ag 2 WO 4 ) x (0.15= (1-y) -(Ag 2 CrO 4 ) y (0.15= -3 Scm -1 for the composition (CuI) 0.45 -(Ag 2 WO 4 ) 0.55 and 1.1x10 -4 Scm -1 in the case of (CuI) 0.55 -(Ag 2 CrO 4 ) 0.45 at room temperature has been discussed in terms of the observed characteristics

Influence of Homogenization on Microstructural Response and Mechanical Property of Al-Cu-Mn Alloy.

Science.gov (United States)

Wang, Jian; Lu, Yalin; Zhou, Dongshuai; Sun, Lingyan; Li, Renxing; Xu, Wenting

2018-05-29

The evolution of the microstructures and properties of large direct chill (DC)-cast Al-Cu-Mn alloy ingots during homogenization was investigated. The results revealed that the Al-Cu-Mn alloy ingots had severe microsegregation and the main secondary phase was Al₂Cu, with minimal Al₇Cu₂Fe phase. Numerous primary eutectic phases existed in the grain boundary and the main elements were segregated at the interfaces along the interdendritic region. The grain boundaries became discontinuous, residual phases were effectively dissolved into the matrix, and the segregation degree of all elements was reduced dramatically during homogenization. In addition, the homogenized alloys exhibited improved microstructures with finer grain size, higher number density of dislocation networks, higher density of uniformly distributed θ' or θ phase (Al₂Cu), and higher volume fraction of high-angle grain boundaries compared to the nonhomogenized samples. After the optimal homogenization scheme treated at 535 °C for 10 h, the tensile strength and elongation% were about 24 MPa, 20.5 MPa, and 1.3% higher than those of the specimen without homogenization treatment.

Electron transport in all-Heusler Co2CrSi/Cu2CrAl/Co2CrSi device, based on ab-initio NEGF calculations

Science.gov (United States)

Mikaeilzadeh, L.; Pirgholi, M.; Tavana, A.

2018-05-01

Based on the ab-initio non-equilibrium Green's function (NEGF) formalism based on the density functional theory (DFT), we have studied the electron transport in the all-Heusler device Co2CrSi/Cu2CrAl/Co2CrSi. Results show that the calculated transmission spectra is very sensitive to the structural parameters and the interface. Also, we obtain a range for the thickness of the spacer layer for which the MR effect is optimum. Calculations also show a perfect GMR effect in this device.

Hydrogen storage properties of LaMgNi3.6M0.4 (M = Ni, Co, Mn, Cu, Al) alloys

International Nuclear Information System (INIS)

Yang, Tai; Zhai, Tingting; Yuan, Zeming; Bu, Wengang; Xu, Sheng; Zhang, Yanghuan

2014-01-01

Highlights: • La–Mg–Ni system AB 2 -type alloys were prepared by induction melting. • Structures and lattice parameters were analysed by XRD. • Hydrogen absorption/desorption performances were studied. • Mechanisms of hydrogen absorption capacity fading were investigated. - Abstract: LaMgNi 3.6 M 0.4 (M = Ni, Co, Mn, Cu, Al) alloys were prepared through induction melting process. The phase compositions and crystal structures were characterised via X-ray diffraction (XRD). The hydrogen storage properties, including activation performance, hydrogen absorption capacity, cycle stability, alloy particle pulverisation and plateau pressure, were systemically investigated. Results show that Ni, Co, Mn and Cu substitution alloys exhibit multiphase structures comprising the main phase LaMgNi 4 and the secondary phase LaNi 5 . However, the secondary phase of the Al substitution alloy changes into LaAlNi 4 . The lattice parameters and cell volumes of the LaMgNi 4 phase follow the order Ni < Co < Al < Cu < Mn. Activation is simplified through partial substitution of Ni with Al, Cu and Co. The hydrogen absorption capacities of all of the alloys are approximately 1.7 wt.% at the first activation process; however, they rapidly decrease with increasing cycle number. In addition, the stabilities of hydriding and dehydriding cycles decrease in the order Al > Co > Ni > Cu > Mn. Hydriding processes result in numerous cracks and amorphisation of the LaMgNi 4 phase in the alloys. The p–c isotherms were determined by a Sieverts-type apparatus. Two plateaus were observed for the Ni, Co and Al substitution alloys, whereas only one plateau was found for Mn and Cu. This result was caused by the amorphisation of the LaMgNi 4 phase during the hydriding cycles. Reversible absorption and desorption of hydrogen are difficult to achieve. Substitutions of Ni with Co, Mn, Cu and Al significantly influence the reduction of hysteresis between hydriding and dehydriding

Quantitative trait loci controlling Cu, Ca, Zn, Mn and Fe content in ...

Indian Academy of Sciences (India)

of essential minerals (such as Fe, Zn etc), breeding mineral- efficient crops that produce .... and seven digenic interactions were identified for Cu, Ca,. Zn, Mn and Fe, .... Eva P. 1993 Cadmium, copper and lead in wild rice from central. Canada.

Fluorescence turn-on detection of alkaline phosphatase activity based on controlled release of PEI-capped Cu nanoclusters from MnO2 nanosheets.

Science.gov (United States)

Zhang, Yunyi; Li, Yongxin; Zhang, Cuiyun; Zhang, Qingfeng; Huang, Xinan; Yang, Meiding; Shahzad, Sohail Anjum; Lo, Kenneth Kam-Wing; Yu, Cong; Jiang, Shichun

2017-08-01

A fluorescence turn-on assay for alkaline phosphatase (ALP) activity is developed through the controlled release of polyethyleneimine-capped copper nanoclusters (PEI-capped CuNCs) from the MnO 2 nanosheets. In an aqueous solution, the positively charged PEI-capped CuNCs could be adsorbed onto the surface of the negatively charged MnO 2 nanosheets. Such adsorption through favorable electrostatic interactions could efficiently quench the nanocluster fluorescence emission via resonance energy transfer from the PEI-capped CuNCs to the MnO 2 nanosheets. 2-Phospho-L-ascorbic acid (AAP) could be hydrolyzed to L-ascorbic acid (AA) in the presence of ALP. AA could reduce MnO 2 into Mn 2+ and trigger the disintegration of the MnO 2 nanosheets. As a result, the CuNCs were released and the quenched fluorescence was recovered efficiently. The detection strategy is simple, inexpensive, sensitive, selective, with low toxicity, and has better biocompatibility. The newly fabricated biosensor for ALP activity will potentially make it a robust candidate for numerous biological and biomedical applications.

Distributions of dissolved trace metals (Cd, Cu, Mn, Pb, Ag in the southeastern Atlantic and the Southern Ocean

Directory of Open Access Journals (Sweden)

M. Boye

2012-08-01

Full Text Available Comprehensive synoptic datasets (surface water down to 4000 m of dissolved cadmium (Cd, copper (Cu, manganese (Mn, lead (Pb and silver (Ag are presented along a section between 34° S and 57° S in the southeastern Atlantic Ocean and the Southern Ocean to the south off South Africa. The vertical distributions of Cu and Ag display nutrient-like profiles similar to silicic acid, and of Cd similar to phosphate. The distribution of Mn shows a subsurface maximum in the oxygen minimum zone, whereas Pb concentrations are rather invariable with depth. Dry deposition of aerosols is thought to be an important source of Pb to surface waters close to South Africa, and dry deposition and snowfall may have been significant sources of Cu and Mn at the higher latitudes. Furthermore, the advection of water masses enriched in trace metals following contact with continental margins appeared to be an important source of trace elements to the surface, intermediate and deep waters in the southeastern Atlantic Ocean and the Antarctic Circumpolar Current. Hydrothermal inputs may have formed a source of trace metals to the deep waters over the Bouvet Triple Junction ridge crest, as suggested by relatively enhanced dissolved Mn concentrations. The biological utilization of Cu and Ag was proportional to that of silicic acid across the section, suggesting that diatoms formed an important control over the removal of Cu and Ag from surface waters. However, uptake by dino- and nano-flagellates may have influenced the distribution of Cu and Ag in the surface waters of the subtropical Atlantic domain. Cadmium correlated strongly with phosphate (P, yielding lower Cd / P ratios in the subtropical surface waters where phosphate concentrations were below 0.95 μM. The greater depletion of Cd relative to P observed in the Weddell Gyre compared to the Antarctic Circumpolar Current could be due to increase Cd uptake induced by iron-limiting conditions in these high

Oxidation Characteristics and Electrical Properties of Doped Mn-Co Spinel Reaction Layer for Solid Oxide Fuel Cell Metal Interconnects

Directory of Open Access Journals (Sweden)

Pingyi Guo

2018-01-01

Full Text Available To prevent Cr poisoning of the cathode and to retain high conductivity during solid oxide fuel cell (SOFC operation, Cu or La doped Co-Mn coatings on a metallic interconnect is deposited and followed by oxidation at 750 °C. Microstructure and composition of coatings after preparation and oxidation is analyzed by X-ray diffraction (XRD and scanning electron microscopy (SEM. High energy micro arc alloying process, a low cost technique, is used to prepare Cu or La doped Co-Mn coatings with the metallurgical bond. When coatings oxidized at 750 °C in air for 20 h and 100 h, Co3O4 is the main oxide on the surface of Co-38Mn-2La and Co-40Mn coatings, and (Co,Mn3O4 spinel continues to grow with extended oxidation time. The outmost scales of Co-33Mn-17Cu are mainly composed of cubic MnCo2O4 spinel with Mn2O3 after oxidation for 20 h and 100 h. The average thickness of oxide coatings is about 60–70 μm after oxidation for 100 h, except that Co-40Mn oxide coatings are a little thicker. Area-specific resistance of Cu/La doped Co-Mn coatings are lower than that of Co-40Mn coating. (Mn,Co3O4/MnCo2O4 spinel layer is efficient at blocking the outward diffusion of chromium and iron.

Purification of hydrogen from carbon monoxide for fuel cell application over modified mesoporous CuO-CeO2 catalysts

KAUST Repository

Li, Jing

2011-08-01

Selective oxidation of CO in H2-rich streams was carried out over a series of CuO-CeO2 catalysts doped by different transition metals (Mn, Fe, Ni, Ti, Co and Cr). The effect of the dopants on the structure and catalytic properties of CuO-CeO2 catalysts was investigated by N2 adsorption/desorption, X-ray diffraction (XRD), H2 temperature-programmed reduction (H2-TPR), X-ray photoelectron spectroscopy (XPS), Raman spectra and in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) techniques. The results show that the addition of Mn and Fe plays a beneficial role in extending the low-temperature catalytic activity of CuO-CeO2 catalysts, whereas the introduction of Cr and Co leads to a negative effect on the catalytic activity and resistance against CO2 and H2O. The superior catalytic performance of CuO-CeO2 catalysts with Mn and Fe doping originates from the enhanced interaction between copper and ceria, owing to the formation of more Cu+ and oxygen vacancies in the solid solution framework. While the poor catalytic activity of the Co doped counterpart is mainly ascribed to the substitution of introduced cobalt ions for copper ions in ceria lattice, resulting in the segregation of copper ions from the ceria lattice and the consequent aggregation of copper species on the ceria surface. The doping of Cr into CuO-CeO2 structure remarkably weakens the interaction between copper and ceria, which decreases the reducibility of copper species and inhibits the formation of Cu+. It accounts for the lowest catalytic activity. © 2011 Elsevier B.V.

Purification of hydrogen from carbon monoxide for fuel cell application over modified mesoporous CuO-CeO2 catalysts

KAUST Repository

Li, Jing; Han, Yuxi; Zhu, Yihan; Zhou, Renxian

2011-01-01

Selective oxidation of CO in H2-rich streams was carried out over a series of CuO-CeO2 catalysts doped by different transition metals (Mn, Fe, Ni, Ti, Co and Cr). The effect of the dopants on the structure and catalytic properties of CuO-CeO2 catalysts was investigated by N2 adsorption/desorption, X-ray diffraction (XRD), H2 temperature-programmed reduction (H2-TPR), X-ray photoelectron spectroscopy (XPS), Raman spectra and in situ diffuse reflectance infrared Fourier transform spectroscopy (DRIFTS) techniques. The results show that the addition of Mn and Fe plays a beneficial role in extending the low-temperature catalytic activity of CuO-CeO2 catalysts, whereas the introduction of Cr and Co leads to a negative effect on the catalytic activity and resistance against CO2 and H2O. The superior catalytic performance of CuO-CeO2 catalysts with Mn and Fe doping originates from the enhanced interaction between copper and ceria, owing to the formation of more Cu+ and oxygen vacancies in the solid solution framework. While the poor catalytic activity of the Co doped counterpart is mainly ascribed to the substitution of introduced cobalt ions for copper ions in ceria lattice, resulting in the segregation of copper ions from the ceria lattice and the consequent aggregation of copper species on the ceria surface. The doping of Cr into CuO-CeO2 structure remarkably weakens the interaction between copper and ceria, which decreases the reducibility of copper species and inhibits the formation of Cu+. It accounts for the lowest catalytic activity. © 2011 Elsevier B.V.

Effect of Cu{sup 2+} and Ni{sup 2+} substitution at the Mn site in (La{sub 0.63}Ca{sub 0.37})MnO{sub 3}: A neutron powder diffraction investigation

Energy Technology Data Exchange (ETDEWEB)

Martinelli, A., E-mail: alberto.martinelli@spin.cnr.it [CNR-SPIN, C.so Perrone 24, 16152 Genova (Italy); Ferretti, M. [CNR-SPIN, C.so Perrone 24, 16152 Genova (Italy); Dipartimento di Chimica e Chimica Industriale, Università di Genova, Via Dodecaneso 31, 16146 Genova (Italy); Castellano, C. [Università degli Studi di Milano, Dipartimento di Chimica Strutturale e Stereochimica Inorganica, Via G. Venezian 21, 20133 Milano (Italy); Cimberle, M.R. [IMEM-CNR, Via Dodecaneso 33, 16146 Genova (Italy); Ritter, C. [Institute Laue—Langevin, 6 rue Jules Horowitz, 38042 Grenoble Cedex 9 (France)

2013-04-15

The crystal and magnetic structures of the (La{sub 0.63}Ca{sub 0.37})(Mn{sub 1−x}TM{sub x})O{sub 3} compounds (x=0.00, 0.03, 0.08; TM=Cu{sup 2+}, Ni{sup 2+}) were investigated between 5 K and 300 K by means of dc magnetic measurements and neutron powder diffraction analysis followed by Rietveld refinement. Both substituting cations lead to a reduction of the long range ferromagnetic ordering temperature; ferromagnetism is strongly suppressed in the 8% Cu-substituted sample, where long- and short-range FM magnetic orders coexist together with short-range A-type AFM order. This particular feature can be related to the Jahn–Teller character of Cu{sup 2+}, absent in Ni{sup 2+}, and suggests the occurrence of a quantum critical point in the (La{sub 0.63}Ca{sub 0.37})(Mn{sub 1−x}Cu{sub x})O{sub 3} system. - Graphical abstract: Rietveld refinement plot of (La{sub 0.63}Ca{sub 0.37})(Mn{sub 0.92}Cu{sub 0.08})O{sub 3} showing in the inset the coexistence of broad A-type AFM peaks with FM ones. Highlights: ► (La{sub 0.63}Ca{sub 0.37})MnO{sub 3} was substituted with Ni and Cu. ► Neutron powder diffraction and Rietveld refinement were carried out. ► A quantum critical point possibly occurs in the (La{sub 0.63}Ca{sub 0.37})(Mn{sub 1−x}Cu{sub x})O{sub 3} system.

Effect of Nickel Equivalent on Austenite Transition Ratio in Ni-Mn-Cu Cast Iron

Directory of Open Access Journals (Sweden)

Janus A.

2013-06-01

Full Text Available Determined was quantitative effect of nickel equivalent value on austenite decomposition degree during cooling-down castings of Ni-Mn- Cu cast iron. Chemical composition of the alloy was 1.8 to 5.0 % C, 1.3 to 3.0 % Si, 3.1 to 7.7 % Ni, 0.4 to 6.3 % Mn, 0.1 to 4.9 % Cu, 0.14 to 0.16 % P and 0.03 to 0.04 % S. Analysed were castings with representative wall thickness 10, 15 and 20 mm. Scope of the examination comprised chemical analysis (including WDS, microscopic observations (optical and scanning microscopy, image analyser, as well as Brinell hardness and HV microhardness measurements of structural components.

Characterization of residues from thermal treatment of treated wood and extraction of Cu, Cr, As and Zn

DEFF Research Database (Denmark)

Ottosen, Lisbeth M.; Pedersen, Anne Juul; Christensen, Iben Vernegren

2005-01-01

, that the charcoal contained a high concentration of Zn, probably from paint. Chemical extraction experiments in HNO were conducted with the charcoal and it was found that the order of extraction (in percentage) was Zn > Cu > As > Cr. A SEM/EDX investigation of the mixed ash from combustion showed the presence...... a matter to cope with when methods to avoid As emission are implemented: the residues with increased concentrations of Cu, Cr and As. In the present paper two different residues after thermal treatment are characterized: a mixed bottom and fly ash from combustion of CCA impregnated wood, and a charcoal...... form in a small layer on the surface of some matrix particles indicating condensation of volatile Cu species. Chemical extraction with inorganic acids showed the order of percentages mobilized as: As > Cu > Cr....

Chemical shift of Mn and Cr K-edges in X-ray absorption

Indian Academy of Sciences (India)

... Lecture Workshops · Refresher Courses · Symposia · Live Streaming. Home; Journals; Bulletin of Materials Science; Volume 36; Issue 6. Chemical shift of Mn and Cr K-edges in X-ray absorption spectroscopy with synchrotron radiation. D Joseph A K Yadav S N Jha D Bhattacharyya. Volume 36 Issue 6 November 2013 pp ...

The electrical conductivity of CuCrZr alloy after SPD processing

International Nuclear Information System (INIS)

Lipińska, M; Bazarnik, P; Lewandowska, M

2014-01-01

CuCrZr alloys exhibit very good relation between mechanical properties and electrical conductivity. However, for its use in some advanced applications improvement of mechanical strength while preserving high electrical conducting is required. Therefore, in this work a CuCrZr alloy was subjected to a series of thermo-mechanical treatments, including solution annealing and water quenching, SPD processing (using hydrostatic extrusion and ECAP) as well as aging in order to improve mechanical strength. The influence of these processing procedures on microstructure features and mechanical properties was determined by TEM observation and microhardness measurements, respectively. Electrical conductivity of the samples was measured by four-points method. The results have shown that it is possible to improve mechanical strength while preserving good electrical conductivity by a proper combination of SPD processing and heat treatment

Formation of Al15Mn3Si2 Phase During Solidification of a Novel Al-12%Si-4%Cu-1.2%Mn Heat-Resistant Alloy and Its Thermal Stability

Science.gov (United States)

Suo, Xiaojing; Liao, Hengcheng; Hu, Yiyun; Dixit, Uday S.; Petrov, Pavel

2018-02-01

The formation of Al15Mn3Si2 phase in Al-12Si-4Cu-1.2Mn (wt.%) alloy during solidification was investigated by adopting CALPHAD method and microstructural observation by optical microscopy, SEM-EDS, TEM-EDS/SAD and XRD analysis; SEM fixed-point observation method was applied to evaluate its thermal stability. As-cast microstructural observation consistently demonstrates the solidification sequence of the studied alloy predicted by phase diagram calculation. Based on the phase diagram calculation, SEM-EDS, TEM-EDS/SAD and XRD analysis, as well as evidences on Al-Si-Mn-Fe compounds from the literature, the primary and eutectic Mn-rich phases with different morphologies in the studied alloy are identified to be Al15Mn3Si2 that has a body-centered cubic (BCC) structure with a lattice constant of a = 1.352 nm. SEM fixed-point observation and XRD analysis indicate that Al15Mn3Si2 phase has more excellent thermal stability at high temperature than that of CuAl2 phase and can serve as the major strengthening phase in heat-resistant aluminum alloy that has to face a high-temperature working environment. Results of tension test show that addition of Mn can improve the strength of Al-Si-Cu alloy, especially at elevated temperature.

Welding of heterogeneous 12Kh2MFSR steels with the Mn-Cr-Si-Ni system

International Nuclear Information System (INIS)

Smirnov, A.N.; Belogolov, E.I.

1978-01-01

The process of welding pipes of the 12Kh2MFSR pearlitic steels and austenitic steels of the Mn-Cr-Si-Ni system was studied. The filler materials were selected, and the working capacity of welded joints was examined in ageing and cyclic heatings. The microhardness of steels was measured, and the ultimate strength of welded joints was determined. The following has been established: the composite joints of steels of the Mn-Cr-Si-Ni system and 12Kh2MFSR steel are advisable to be welded on a coating layer welded by the EhA395/9 electrodes on the surface of a pipe of the 12Kh2MFSR pearlitic steel; this guarantees the sufficient working capacity of welded joints

Structural, magnetic and transport studies of Mn0.8Cr0.2CoGe alloy

Science.gov (United States)

Das, S. C.; Dutta, P.; Pramanick, S.; Chatterjee, S.

2018-04-01

Different physical and functional properties of Mn0.8Cr0.2CoGe alloy has been investigated through structural, magnetic and electrical transport measurements. Substitution of Cr for Mn results significant decrease in both structural and magnetic transition temperature and brings them well below the room temperature. A reasonable amount of conventional magnetocaloric effect (ΔS˜ - 2.22 J/kg-K for magnetic field (H) changing from 0 to 50 kOe) with large relative cooling power (251.7 J/kg for H changing from 0 to 50 kOe) has also been observed around the region of transition. On thermal cycling through the structural transition, noticeable training effect is found to be associated with the resistivity of the alloy.

An anti CuO{sub 2}-type metal hydride square net structure in Ln{sub 2}M{sub 2}As{sub 2}H{sub x} (Ln = La or Sm, M = Ti, V, Cr, or Mn)

Energy Technology Data Exchange (ETDEWEB)

Mizoguchi, Hiroshi; Park, SangWon; Hosono, Hideo [Tokyo Institute of Technology, Yokohama (Japan). Materials Research Center for Element Strategy; Hiraka, Haruhiro; Ikeda, Kazutaka; Otomo, Toshiya [High-Energy Accelerator Research Organization (KEK), Tsukuba (Japan). Inst. of Materials Structure Science

2015-03-02

Using a high pressure technique and the strong donating nature of H{sup -}, a new series of tetragonal La{sub 2}Fe{sub 2}Se{sub 2}O{sub 3}-type layered mixed-anion arsenides, Ln{sub 2}M{sub 2}As{sub 2}H{sub x}, was synthesized (Ln=La or Sm, M=Ti, V, Cr, or Mn; x∼3). In these compounds, an unusual M{sub 2}H square net, which has anti CuO{sub 2} square net structures accompanying two As{sup 3-} ions, is sandwiched by (LaH){sub 2} fluorite layers. Notably, strong metal-metal bonding with a distance of 2.80 Aa was confirmed in La{sub 2}Ti{sub 2}As{sub 2}H{sub 2.3}, which has metallic properties. In fact, these compounds are situated near the boundary between salt-like ionic hydrides and transition-metal hydrides with metallic characters.

Teores de Fe, Mn, Zn, Cu, Ni E Co em solos de referência de Pernambuco

Directory of Open Access Journals (Sweden)

Caroline Miranda Biondi

2011-06-01

Full Text Available Metais pesados formam um grupo de elementos com particularidades relevantes e de ocorrência natural no ambiente, como elementos acessórios na constituição de rochas. Esses elementos, apesar de associados à toxidez, exigem tratamento diferenciado em relação aos xenobióticos, uma vez que diversos metais possuem essencialidade (Fe, Mn, Cu, Zn e Ni e benefício (Co comprovados para as plantas. Nesse contexto, o objetivo deste trabalho foi determinar os teores naturais dos metais Fe, Mn, Zn, Ni, Cu e Co nos solos de referência de Pernambuco. Foram coletadas amostras de solo nas três regiões fisiográficas (Zona da Mata, Agreste e Sertão, dos dois primeiros horizontes dos 35 solos de referência do Estado de Pernambuco. A digestão das amostras baseou-se no método 3051A (USEPA, 1998, e a determinação foi efetuada em ICP-OES. Correlações significativas foram estabelecidas entre os metais e entre estes e a fração argila do solo, em ambos os horizontes, indicando a associação comum da maioria dos metais com solos mais argilosos. A maioria dos solos apresentou teores de Fe, Mn, Zn, Cu, Ni e Co menores que os de solos de outras regiões do País, com litologia mais máfica, o que corrobora o fato de que os teores desses elementos são mais diretamente relacionados aos minerais Fe-magnesianos. Os resultados indicam baixo potencial dos solos de Pernambuco em liberar Cu, Co e Ni para plantas, enquanto deficiências de Zn, Fe e Mn são menos prováveis. Os teores naturais de Fe, Mn, Zn, Cu, Ni e Co determinados podem ser utilizados como base para definição dos Valores de Referência de Qualidade para os solos de Pernambuco, de acordo com o preconizado pela legislação nacional.

Low-cost, high-strength Fe--Ni--Cr alloys for high temperature exhaust valve application

Science.gov (United States)

Muralidharan, Govindarajan

2017-09-05

An Fe--Ni--Cr alloy is composed essentially of, in terms of wt. %: 2.4 to 3.7 Al, up to 1.05 Co, 14.8 to 15.9 Cr, 25 to 36 Fe, up to 1.2 Hf, up to 4 Mn, up to 0.6 Mo, up to 2.2 Nb, up to 1.05 Ta, 1.9 to 3.6 Ti, up to 0.08 W, up to 0.03 Zr, 0.18 to 0.27 C, up to 0.0015 N, balance Ni, wherein, in terms of atomic percent: 8.5.ltoreq.Al+Ti+Zr+Hf+Ta.ltoreq.11.5, 0.53.ltoreq.Al/(Al+Ti+Zr+Hf+Ta).ltoreq.0.65, and 0.16.ltoreq.Cr/(Fe+Ni+Cr+Mn).ltoreq.0.21, the alloy being essentially free of Cu, Si, and V.

Influence of Copper on the Hot Ductility of 20CrMnTi Steel

Science.gov (United States)

Peng, Hong-bing; Chen, Wei-qing; Chen, Lie; Guo, Dong

2015-02-01

The hot ductility of 20CrMnTi steel with x% copper (x = 0, 0.34) was investigated. Results show that copper can reduce its hot ductility, but there is no significant copper-segregation at the boundary tested by EPMA. The average copper content at grain boundaries and substrate is 0.352% and 0.318% respectively in steel containing 0.34% copper tensile-tested at 950 °C. The fracture morphology was examined with SEM and many small and shallow dimples were found on the fracture of steel with copper, and fine copper sulfide was found from carbon extraction replicas using TEM. Additionally, adding 0.34% copper caused an increase in the dynamic recrystallization temperature from 950 °C to 1000 °C, which indicates that copper can retard the dynamic recrystallization (DRX) of austenite. The detrimental influence of copper on hot ductility of 20CrMnTi steel is due mainly to the fine copper sulfide in the steel and its retarding the DRX.

Ferromagnetic-phase transition in the spinel-type CuCr2Te4

International Nuclear Information System (INIS)

Suzuyama, Takeshi; Awaka, Junji; Yamamoto, Hiroki; Ebisu, Shuji; Ito, Masakazu; Suzuki, Takashi; Nakama, Takao; Yagasaki, Katsuma; Nagata, Shoichi

2006-01-01

Ferromagnetic-phase transition in spinel-type CuCr 2 Te 4 has been clearly observed. CuCr 2 Te 4 is a telluride-spinel with the lattice constant a=11.134A, which has been synthesized successfully. The heat capacity exhibits a sharp peak due to the ferromagnetic-phase transition with the Curie temperature T C =326K. This value of T C corresponds exactly to that of the negative peak of dM/dT in low field of 1.0Oe. The magnetic susceptibility shows the Curie-Weiss behavior between 380 and 650K with the effective magnetic moment μ eff =4.14μ B /Cr-ion and the Weiss constant θ=+357K. The low temperature magnetization indicates the spin-wave excitations, where the existence of first term of Bloch T 3/2 law and the next T 5/2 term are verified experimentally. This spin-wave excitation is detected up to approximately 250K which is a fairly high temperature

Producing a particle-reinforced AlCuMgMn alloy by means of mechanical alloying; Herstellung einer partikelverstaerkten AlCuMgMn-Legierung durch mechanisches Legieren

Energy Technology Data Exchange (ETDEWEB)

Nestler, D.; Wielage, B. [TU Chemnitz, Institut fuer Werkstoffwissenschaft und Werkstofftechnik (Germany); Siebeck, S.

2012-07-15

High-energy ball milling (HEM) with subsequent consolidation is a suitable method to produce particle-reinforced aluminium materials. The task of HEM is to distribute the reinforcement particles as homogeneously as possible. A further application of HEM is mechanical alloying (MA). This paper deals with the combination of both applications. Pure metallic powders (Al, Cu, Mg, Mn) were milled together with SiC particles up to 10 h. The composition of the metallic powder corresponds to that of the alloy AA2017 (3.9% Cu, 0.7% Mg, 0.6% Mn). In previous experiments [1], this alloy was used in the form of atomized powder. The changes in microstructure during the formation of the composite powder have been studied by light microscopy, SEM, EDXS and XRD. The results show that the production of composite powders in a single step is possible. This not only allows the economical production of such powders, but also facilitates the use of alloy compositions that are not producible via the melting route, or only producible with difficulty via the melting route. It's possible to produce tailor-made-alloys. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Bioaccumulation of heavy metals and metalloids in luffa (luffa cylindrica l.) irrigated with domestic wastewater in jhang, pakistan: a prospect for human nutrition

International Nuclear Information System (INIS)

Khani, Z.I.; Ahmad, K.

2015-01-01

In the present study, 12 heavy metals (Cr, Mn, Ni, Cd, Co, Cu, Pb, Zn, Fe, Se, As, and Mo) were assessed in a potential vegetable Luffa cylindrica. The vegetable was collected randomly from two different sites located at Jhang, Punjab Pakistan. The analyses of variance of data collected from soil showed non-significant effect on Se, Zn, As, Cr, Ni, Mo and Pb while significant effect on Fe, Co, Mn, Cu and Cd metals. Concentrations of all 12 heavy metals in the soil samples were low at sampling site-I as compared to those at site-II except Ni. These concentrations were found below the safe limits except that of Cd. At site-I, the concentrations recorded for different heavy metals were: As > Fe > Pb > Mn > Cd > Co > Cu > Mo > Zn > Ni > Se > Cr while at site-II were: As > Fe > Mn > Pb > Co > Cd > Cu > Mo > Zn > Ni > Se > Cr. Enrichment co-efficient of Cr was higher which showed that root of luffa plant accumulated more Cr concentration from the contaminated soil. The order of enrichment co-efficient was recorded at site-I as: Cr > Zn > Mn > Cu > Fe > Ni > Mo > Pb > As > Se > Co > Cd, and at site-II Cr > Zn > Mn > Ni > Cu > Fe > Mo > Pb > Se > As > Co > Cd. The transfer co-efficient of Mn was higher which indicates that more contents of Mn were transferred from roots to upper edible part. The order of transfer co-efficient at site-I was: Ni > Se > Mo > Cr > Zn > Fe > Mn > Cd > Pb > As > Cu > Co and at site-II was Mn > Zn > As > Fe > Pb > Se > Cd > Co > Mo > Cu > Ni > Cr. Correlation analysis showed that Mn, Se, Co, Cd, Ni, Mo and Pb had positive non-significant correlation, whereas a negative and non-significant correlation for Zn, As, Fe and Cr. The order of pollution load index at site-I was Cd > Mo > Se > Pb > Cu > Co > As > Fe > Mn > Ni > Zn > Cr and at site-II: Cd > Mo > Se > Pb > Cu > Co > As > Fe > Mn > Ni > Zn > Cr. Overall, at both sites, lowest concentration of Cr and highest of As were observed which need substantial awareness. Health risk index depends on

Behavior of tungsten coatings on CuCrZr heat sink with the different interlayers under high heat flux

International Nuclear Information System (INIS)

Chong, F.L.; Chen, J.L.; Li, J.G.; Zheng, X.B.; Hu, D.Y.; Ding, C.X.

2007-01-01

In recent years, tungsten coated CuCrZr by means of vacuum plasma spraying technology was studied at Institute of Plasma Physics, Chinese Academy of Sciences (ASIPP). Plasma spraying technology is a good integration way of armor material and heat sink, which overcomes the disadvantage of heavy weight and poor workability of tungsten, and offers the ability to coat large area, even complex shapes and in situ repair of damaged parts. But tungsten coated CuCrZr is a challenge due to the larger mismatch of their thermal expansion coefficients (CTE), which will induce the stress concentration on the joint interface of plasma facing component. In order to enhance the adhesion of W coating on CuCrZr substrate and avoid the thermal stress concentration, it is necessary to use a compliant interlayer. At present, titanium (Ti), nickel-chromium-aluminum (NiCrAl) alloys and W/Cu mixtures were chosen as the compliant layers to insert between W coating and CuCrZr substrate. The adhesion strength was performed at RT. The behaviors of W/Cu mock up under high heat flux were carried out by means of the electron beam facility with actively cooling. The results indicated that the mock-ups with the interlayer architectures can withstand the higher heat flux compared to that with the sharp interface, which exhibited the effect of interlayers on reducing the maximum stress and enhancing the properties of resistant heat flux load, though the maximum surface temperature increased due to inserting the interlayers. Among three interlayers, W/Cu interlayer was much better due to its good heat removal capability and flexible W/Cu ratios. Meanwhile, the behaviors of W/Cu mock-ups with the different interlayers were analyzed and optimized by ANSYS finite element code. (authors)

Structural and magnetic properties of Nd0.67Ba0.33MnO3 manganites with partial replacement of Fe and Cu at Mn-site

Science.gov (United States)

Sudakshina, B.; Arun, B.; Chandrasekhar, K. Devi; Yang, H. D.; Vasundhara, M.

2018-06-01

We have investigated the structural and magnetic properties of Nd0.67Ba0.33MnO3 manganite and partial replacement of Mn with Fe and Cu compounds followed by X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS) and vibrating sample magnetometer (VSM). The Rietveld refinement of XRD indicates orthorhombic crystal structure with I-mma space group for all the compounds and thus obtained lattice parameters confirm the presence of co-operative Jahn-Teller effect. XRD and XAS spectra results suggests the existence of Fe3+ in Fe-substituted compound where as a mixed state of Cu2+ and Cu3+ ions in the Cu-substituted compound. The ferromagnetic (FM) to paramagnetic (PM) transition and magnetic moment is found to decrease upon the substitution of Fe and Cu atoms because of the suppression of double exchange interaction. The theoretically obtained and experimentally determined values of effective PM moment and saturation magnetic moment confirms the presence of inhomogeneous magnetic states containing FM and antiferromagnetic clusters in all the studied compounds.

Synthesis of LiMn2O4 and LiCr0.2Mn1.8O4 powders by modified Pechini process

Directory of Open Access Journals (Sweden)

Alexandre Urbano

2009-03-01

Full Text Available LiMn2O4 and LiCr0.2Mn1.8O4 powders were synthesized by Pechini process, modified in order to reduce the number of steps and to work at temperatures below or equal to 400oC. Both phases crystallize in the same spinel structure with lattice constants of 8.21 and 8.22 Å respectively. Although the annealing temperature was low, the cristallinity is good and no residual amounts of organic material were detected.

Effect of Fertilizers and Irrigation on Distribution of Mobile Forms of Mn, Zn and Cu in Typical Chernozems of the Republic of Moldova

Directory of Open Access Journals (Sweden)

Leah T. Gh.

2013-04-01

Full Text Available The paper presents the study results of mobile forms of Mn, Zn and Cu in irrigated fertilized and unfertilized chernozems typical. Irrigation affects the content and distribution of mobile forms of trace elements, increasing their removal beyond the 150 cm of soil layer. The fertilization increase the migration of Cu until 130 cm, fixed Mn and Zn in 0-60 cm of the irrigated soils. During irrigation constitutes a danger of soil contamination with Mn, Cu and Zn.

The effect of Mn substitution on the structure and magnetic properties of Se(Cu sub 1 sub - sub x Mn sub x)O sub 3 solid solution

CERN Document Server

Escamilla, R; Rosales, M I; Moran, E C; Alario-Franco, M A

2003-01-01

The effects of Mn substitution on the structure and magnetic properties of the SeMO sub 3 (M = Cu sub 1 sub - sub x Mn sub x) solid solution have been studied. Rietveld refinements of the x-ray diffraction patterns of these samples indicate that the manganese ions occupy copper sites. This replacement induces significant changes in the M-O bond lengths that give rise to abrupt decreases of the [M-O sub 6] octahedral distortion. In contrast, the M-O(1)-M and M-O(2)-M bond angles remain essentially constant. The magnetic behaviour of this solid solution was studied in the temperature range of 2 K < T < 300 K. The temperature dependence of the inverse magnetic susceptibility is well described by the Curie-Weiss law at high temperatures, in the composition range studied. We found that the substitution of Mn for Cu induces a sharp drop in the saturation moment of SeCuO sub 3. At about 10% of Mn there is a change from positive to negative Weiss constant theta sub W that is mainly due to the [M-O sub 6] octahe...

Certification of trace element contents (As, Cd, Co, Cu, Fe, Mn, Hg, Na, Pb and Zn) in a fly ash obtained from the combustion of pulverised coal

International Nuclear Information System (INIS)

Griepink, B.; Colinet, E.; Guzzi, G.; Haemers, L.; Muntau, H.

1983-01-01

The element contents of As, Cd, Co, Cu, Fe, Mn, Hg, Na, Pb and Zn of a fly ash from pulverised coal are certified. The procedures and their results for the homogenisation, the contamination and homogeneity checks and the analytical campaign are reported. The certified mass fractions and indicative values for Cr, Ni, Th, V and water soluble sulphate are given. The work was carried out within the framework of the activities of the Community Bureau of Reference (BCR) of the Commission of the European Communities. (orig.) [de

Crystal field and low energy excitations measured by high resolution RIXS at the L edge of Cu, Ni and Mn

DEFF Research Database (Denmark)

Ghiringhelli, G.; Piazzalunga, A.; Wang, X.

2009-01-01

of the 3d transition metals with unprecedented energy resolution, of the order of 100 meV for Mn, Ni and Cu. We present here some preliminary spectra on CuO, malachite, NiO, , MnO and . The dd excitations are very well resolved allowing accurate experimental evaluation of 3d state energy splitting. The low...

A better ferrimagnetic half-metal LuCu{sub 3}Mn{sub 4}O{sub 12}: Predicted from first-principles investigation

Energy Technology Data Exchange (ETDEWEB)

Lv Shuhui; Li Hongping [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Graduate School, Chinese Academy of Sciences, Beijing 100049 (China); Han Deming; Wu Zhijian [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Liu Xiaojuan, E-mail: lxjuan@ciac.jl.c [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China); Meng Jian, E-mail: jmeng@ciac.jl.c [State Key Laboratory of Rare Earth Resource Utilization, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022 (China)

2011-03-15

Electronic structure calculations based on density functional theory (DFT) within the generalized gradient approximation (GGA) and GGA+U for manganite cuprate compound LuCu{sub 3}Mn{sub 4}O{sub 12} have been performed, using the full-potential linearized augmented plane wave method. The calculated results indicate that LuCu{sub 3}Mn{sub 4}O{sub 12} is ferrimagnetic and half-metallic in both GGA and GGA+U calculations. The minority-spin band gap is 0.7 eV within GGA, which is larger than that of LaCu{sub 3}Mn{sub 4}O{sub 12} (0.3 eV), indicating its better half-metallicity. Further, the minority-spin gap enlarges from 0.7 to 2.8 eV with U taken into account, and simultaneously the Fermi level being shifted to the middle of the gap, making the half-metallic energy gap to be 1.21 eV. These results demonstrate that electronic correlation effect enhances the stability of half-metallic property. These facts make this system interesting candidates for applications in spintronic devices. - Research highlights: The electronic and magnetic properties of LuCu{sub 3}Mn{sub 4}O{sub 12} are analyzed. Both GGA and GGA+U methods are reported and compared. A better half-metal LuCu{sub 3}Mn{sub 4}O{sub 12} is obtained with large half-metallic gap. The results agree very well with the experimental data.

Novel Preparation of Nano-Composite CuO-Cr2O3 Using Ctab-Template Method and Efficient for Hydrogenation of Biomass-Derived Furfural

Science.gov (United States)

Yan, Kai; Wu, Xu; An, Xia; Xie, Xianmei

2013-02-01

A simple route to fabricate nano-composite oxides CuO-Cr2O3 using hexadecyltrimethylammonium bromide (CTAB)-templated Cu-Cr hydrotalcite as the precursor is presented. This novel method is based on CTAB-templating effect for mesostructure directing and using the cheap metal nitrate, followed by removal of CTAB. It was indicated that the nano-composite CuO-Cr2O3 was formed during the removal of CTAB. X-ray diffraction (XRD) and transitional electronic microscopy (TEM) revealed nice nano-composite oxides CuO-Cr2O3 were formed with high crystallinity. N2 adsorption and desorption indicated that a high surface area of 170.5 m2/g with a pore size of 2.7 nm of the nano-composite CuO-Cr2O3 was facilely resulted. The as-synthesized nano-composite oxides CuO-Cr2O3 display good catalytic activities for hydrogenation of furfural to furfuryl alcohol, whereas 86% selectivity was achieved at 75% conversion of furfural.

Synthesis and mechanical properties of conventionally cast icosahedral particle-reinforced Al-Mn(-Cu)-Be-Si alloys

International Nuclear Information System (INIS)

Fleury, E.; Chang, H.J.; Kim, D.H.; Kim, D.H.; Kim, W.T.

2005-01-01

The microstructure of the Al-Mn(-Cu)-Be-Si alloys analyzed by X-ray diffraction and TEM consisted of icosahedral (i) quasicrystal particles embedded in α Al matrix. The conjoint addition of Si and Be elements enabled the i-phase formation in diameter 10 mm specimens prepared by conventional casting technique. The size, volume fraction and stability of the i-phase were found to be dependent on the Mn content. The addition of 2 at.% Cu did not affect the formation and stability of the i-phase but contributed significantly to the enhancement of the mechanical properties. (orig.)

Effects of Mn, Cu doping concentration to the properties of magnetic nanoparticles and arsenic adsorption capacity in wastewater

International Nuclear Information System (INIS)

Thi, Tran Minh; Trang, Nguyen Thi Huyen; Van Anh, Nguyen Thi

2015-01-01

Highlights: • Investigation the decrease of saturate magnetic moment of Fe 3 O 4 over time. • Substitution of Mn, Cu ions into Fe position to create stable properties of materials. • Investigate the surface and mesopore structure of nanoparticles. • The arsenic adsorption capacity of Cu doped Fe 3 O 4 nanomaterials is higher than of Fe 3 O 4 and Mn doped Fe 3 O 4 nanomaterials. - Abstract: The research results of Fe 3 O 4 and Mn, Cu doped Fe 3 O 4 nanomaterials synthesized by a chemical method for As(III) wastewater treatment are presented in this paper. The X-ray diffraction patterns and transmission electron microscopy images showed that samples had the cubic spinel structure with the grain sizes were varied from 9.4 nm to 18.1 nm. The results of vibrating sample magnetometer measurements at room temperature showed that saturation magnetic moments of Fe 1−x Cu x Fe 2 O 4 and Fe 1−x Mn x Fe 2 O 4 samples decreased from 65.9 emu/g to 53.2 emu/g and 65.9 emu/g to 61.5 emu/g, respectively, with the increase of Cu, Mn concentrations from 0.0 to 0.15. The nitrogen adsorption–desorption isotherm of a typical Fe 3 O 4 sample at 77 K was studied in order to investigate the surface and porous structure of nanoparticles by BET method. The specific surface area of Fe 3 O 4 magnetic nanoparticles was calculated about of 100.2 m 2 /g. The pore size distribution of about 15–20 nm calculated by the BJH (Barrett, Joyner, and Halendar) method at a relative pressure P/P 0 of about 1. Although the saturation magnetic moments of samples decreased when the increase of doping concentration, but the arsenic adsorption capacity of Cu doped Fe 3 O 4 nanoparticles is better than that of Fe 3 O 4 and Mn doped Fe 3 O 4 nanoparticles in a solution with pH = 7. In the solution with a pH > 14, the arsenic adsorption of magnetic nanoparticles is insignificant

The efficiency of biosynthesis silica nanoparticles at removal of heavy metals Cr and Cu from aqueous solutions

Directory of Open Access Journals (Sweden)

Mohammad Hossein Sayadi

2017-05-01

Full Text Available Background and Aim: Nanotechnology considered as one of the main management strategy in reducing negative effects of water pollution, which leads to treating of water inexpensive and more effective. This study aimed to investigate the removal of Cr and Cu from aqueous solutions using nano-silicate which is synthesized by rice husk. Materials and Methods: In the present study, functionalized nano-silica with rice husk was fabricated and characterized by FT-IR، TEM, SEM and XRD. The effect of adsorbent dosage, initial concentration and equilibrium of chromium and copper and contact time in removal of mentioned heavy metals were investigated. Finally, the adsorption isotherms were analyzed. Results: The silica nanoparticles had nearly spherical morphology with a uniform size of about 80 nm. However, the obtained functionalized silica nanoparticles were spherical (about 90 nm in diameter. Results showed that optimum adsorption of Cr and Cu contaminant obtained at 100 minutes, while the optimum amount of adsorbent for Cr and Cu were 125 and 100 mg respectively. The optimal concentration of Cr and Cu was 2 mg/l. The correlation coefficients of adsorption isotherms of Cr (R2Langmuir =0.9946 and Cu (R2Langmuir =0.999 showed the good agreement between the adsorption data and Langmuir model. Conclusion: The study showed that the silica nanoparticles can be produced using agricultural waste as a inexpensive and environmentally friendly method and can be used to removing of contaminants from the aquatic environment.

Ti{sub 3}CrCu{sub 4}: A possible 2-D ferromagnetic spin fluctuating system

Energy Technology Data Exchange (ETDEWEB)

Dhar, S. K.; Kulkarni, R.; Goyal, Neeraj [Department of Condensed Matter Physics & Materials Science, T.I.F.R., Homi Bhabha Road, Colaba, Mumbai, 400005 (India); Provino, A.; Manfrinetti, P. [Department of Chemistry, University of Genova, Via Dodecaneso 31, 16146 Genova (Italy); Paudyal, D. [The Ames Laboratory, US Department of Energy, Iowa State University, Ames, IA 50011-3020 (United States)

2016-05-15

Ti{sub 3}CrCu{sub 4} is a new ternary compound which crystallizes in the tetragonal Ti{sub 3}Pd{sub 5} structure type. The Cr atoms form square nets in the a-b plane (a = 3.124 Å) which are separated by an unusually large distance c = 11.228 Å along the tetragonal axis, thus forming a -2-D Cr-sublattice. The paramagnetic susceptibility is characterized by a low effective moment, μ{sub eff} = 1.1 μ{sub B}, a low paramagnetic Curie temperature θ{sub P} (below 7 K) and a temperature independent χ{sub 0} = 6.7 x 10{sup −4} emu/mol. The magnetization at 1.8 K increases rapidly with field nearly saturating to 0.2 μ{sub B}/f.u. The zero field heat capacity C/T shows an upturn below 7 K (∼190 mJ/mol K{sup 2} at ∼0.1K) which is suppressed in applied magnetic fields and interpreted as suggesting the presence of spin fluctuations. The resistivity at low temperatures shows non-Fermi liquid behavior. Overall, the experimental data thus reveal an unusual magnetic state in Ti{sub 3}CrCu{sub 4}, which likely has its origin in the layered nature of the Cr sub-lattice and ferromagnetic spin fluctuations. Density functional theoretical calculations reveal a sharp Cr density of states peak just above the Fermi level, indicating the propensity of Ti{sub 3}CrCu{sub 4} to become magnetic.

Experimental and computational study of nitride precipitation in a CrMnN austenitic stainless steel

International Nuclear Information System (INIS)

Pettersson, Niklas; Frisk, Karin; Fluch, Rainer

2017-01-01

The austenitic CrMnN stainless steels are high-strength, tough, and non-magnetic, and are used in oil field applications. The steels have high alloying contents, and precipitation of Cr-nitrides and/or intermetallic phases can occur when cooling through the temperature region 950–700 °C. The nitride precipitates appear in the grain boundaries but can be difficult to observe in the microstructure due to their small size. However, there is an effect of precipitation on corrosion and impact strength and a modelling approach to predict precipitation is valuable for alloy and process development. In the present work precipitation simulations were applied to a CrMnN steel composition, and coupled to experimental investigations after heat treatments at 700 and 800 °C. The early stages, with short heat-treatment times, were studied. The simulations were performed using TC-PRISMA, a software for calculation of multiphase precipitation kinetics, using multicomponent nucleation and growth models. Dedicated thermodynamic and kinetic databases were used for the simulations. The main precipitate was identified by experiments and simulations to be the Cr 2 N nitride, and the precipitation during isothermal heat treatments was investigated. Isothermal precipitation diagrams are simulated, and the influence of precipitation kinetics on toughness is discussed.

Experimental and computational study of nitride precipitation in a CrMnN austenitic stainless steel

Energy Technology Data Exchange (ETDEWEB)

Pettersson, Niklas, E-mail: niklas.pettersson@swerea.se [Swerea KIMAB AB, P.O. Box 7047, 164 07 Kista (Sweden); Frisk, Karin [Swerea KIMAB AB, P.O. Box 7047, 164 07 Kista (Sweden); Fluch, Rainer [Böhler Edelstahl Gmbh, Mariazeller Strasse 25, 8605 Kapfenberg (Austria)

2017-01-27

The austenitic CrMnN stainless steels are high-strength, tough, and non-magnetic, and are used in oil field applications. The steels have high alloying contents, and precipitation of Cr-nitrides and/or intermetallic phases can occur when cooling through the temperature region 950–700 °C. The nitride precipitates appear in the grain boundaries but can be difficult to observe in the microstructure due to their small size. However, there is an effect of precipitation on corrosion and impact strength and a modelling approach to predict precipitation is valuable for alloy and process development. In the present work precipitation simulations were applied to a CrMnN steel composition, and coupled to experimental investigations after heat treatments at 700 and 800 °C. The early stages, with short heat-treatment times, were studied. The simulations were performed using TC-PRISMA, a software for calculation of multiphase precipitation kinetics, using multicomponent nucleation and growth models. Dedicated thermodynamic and kinetic databases were used for the simulations. The main precipitate was identified by experiments and simulations to be the Cr{sub 2}N nitride, and the precipitation during isothermal heat treatments was investigated. Isothermal precipitation diagrams are simulated, and the influence of precipitation kinetics on toughness is discussed.

The influence of the oxygen partial pressure on the quasi-ternary system Cr-Mn-Ti-oxide

International Nuclear Information System (INIS)

Garcia-Rosales, C.; Schulze, H.A.; Naoumidis, A.; Nickel, H.

1991-05-01

The passivation layers formed by the oxidizing corrosion of high temperature alloys consist primarily of oxides and mixed oxides of the elements chromium, manganese and titanium. For a reproducible formation and characterization of such oxide layers it is necessary to know the phase equilibria of these oxide systems at temperature and oxygen partial pressure conditions which will be relevant during their application. For the investigation of the quasi-ternary system Cr-Mn-Ti-oxide, oxide powders were prepared and annealed at 1000deg C under different oxygen partial pressures ranging from 0.21 bar to 10 -21 bar. Phase identification and determination of lattice parameter using X-ray diffraction analysis as well as the direct measurement of phase boundaries as a function of oxygen partial pressure using the emf-methode were carried out for these investigations. In the quasi-ternary system Cr-Mn-Ti-oxide the spinels play a decisive role in the oxigen partial pressure range examined. The spinel MnCr 2 O 4 may be regarded as the most significant compound. Part of the chronium can be replaced by trivalent manganese at high oxygen partial pressures and by trivalent titanium at low pressures, and the formation of a solid solution with the spinel Mn 2 TiO 4 is possible in all cases. In this way a coherent single-phase spinel region is observed which extends over the entire oxygen partial pressure range form 0.21 bar to 10 -21 bar examined at 1000deg C. (orig.) [de

Optimization of the diffusion bonding parameters for SS316L/CuCrZr with and without Nickel interlayer

Energy Technology Data Exchange (ETDEWEB)

Singh, K.P., E-mail: kpsingh@ipr.res.in; Patel, Alpesh; Bhope, Kedar; Khirwadkar, S.S.; Mehta, Mayur

2016-11-15

Highlights: • Optimization of diffusion bonding parameters for dissimilar materials SS316L with CuCrZr is proposed with and without Nickel interlayer. • Ultrasonic testing on diffusion bonded samples provides the overall information/signatures about well-bonded and de-bonded samples. • Microstructural examination confirms the diffusion of Nickel into parent materials. • Mechanical characterization such as hardness measurement and shear measurement supports the results. - Abstract: Divertor & Firstwall module of ITER like tokamak has several joints of dissimilar materials such as Tungsten (W) to Copper (Cu), Cu to CuCrZr (heat sink material) and CuCrZr to Stainless Steel (SS) materials. These Plasma Facing Components (PFC) are made of multi-layered joints, which are to be exposed to the harsh environment of Plasma with the expected heat flux of 5–10 MW/m{sup 2}. The joining of SS316L material to CuCrZr material is proposed in this paper. As SS316L/CuCrZr being dissimilar materials, direct joining of these materials is a problem, which needs a suitable fabrication process. The joining of SS316L with heat sink material (CuCrZr) requires the good thermal transfer and sound in structural joint. Diffusion bonding technique has been adopted as a process for joining of these two dissimilar materials. The primary objective of the joining study is to obtain the best diffusion bonding parameters for ITER like tokamak application. Thermo-mechanical simulator machine (Gleeble 3800) is used to perform diffusion bonding experiments at different temperatures 650 °C, 850 °C, 900 °C, 950 °C & 1000 °C, different uniaxial pressure varying from 5 MPa to 15 MPa and with the holding time of 15 min & 30 min, using pure nickel interlayer. The diffusion bonded samples have undergone Non-destructive testing (NDT) particularly the ultrasonic examination using immersion probe technique, microstructural examination by the High Resolution (HR) electron microscopy (SEM), Energy

Optimization of the diffusion bonding parameters for SS316L/CuCrZr with and without Nickel interlayer

International Nuclear Information System (INIS)

Singh, K.P.; Patel, Alpesh; Bhope, Kedar; Khirwadkar, S.S.; Mehta, Mayur

2016-01-01

Highlights: • Optimization of diffusion bonding parameters for dissimilar materials SS316L with CuCrZr is proposed with and without Nickel interlayer. • Ultrasonic testing on diffusion bonded samples provides the overall information/signatures about well-bonded and de-bonded samples. • Microstructural examination confirms the diffusion of Nickel into parent materials. • Mechanical characterization such as hardness measurement and shear measurement supports the results. - Abstract: Divertor & Firstwall module of ITER like tokamak has several joints of dissimilar materials such as Tungsten (W) to Copper (Cu), Cu to CuCrZr (heat sink material) and CuCrZr to Stainless Steel (SS) materials. These Plasma Facing Components (PFC) are made of multi-layered joints, which are to be exposed to the harsh environment of Plasma with the expected heat flux of 5–10 MW/m 2 . The joining of SS316L material to CuCrZr material is proposed in this paper. As SS316L/CuCrZr being dissimilar materials, direct joining of these materials is a problem, which needs a suitable fabrication process. The joining of SS316L with heat sink material (CuCrZr) requires the good thermal transfer and sound in structural joint. Diffusion bonding technique has been adopted as a process for joining of these two dissimilar materials. The primary objective of the joining study is to obtain the best diffusion bonding parameters for ITER like tokamak application. Thermo-mechanical simulator machine (Gleeble 3800) is used to perform diffusion bonding experiments at different temperatures 650 °C, 850 °C, 900 °C, 950 °C & 1000 °C, different uniaxial pressure varying from 5 MPa to 15 MPa and with the holding time of 15 min & 30 min, using pure nickel interlayer. The diffusion bonded samples have undergone Non-destructive testing (NDT) particularly the ultrasonic examination using immersion probe technique, microstructural examination by the High Resolution (HR) electron microscopy (SEM), Energy

Chemical speciation of Pb, Ni Cr, Cu, Co and V in two natural soils and in an antropic agricultural soil contaminated by irrigation with the polluted Rio Bogota waters in its High Basin

International Nuclear Information System (INIS)

Matamoros, Adriana; Vargas, O; Mejia, L

1999-01-01

Traditional and continuous irrigation with the highly polluted waters of Rio Bogota in its upper basin has induced in soils, grasses and crops grown next to the river, a gradually increasing accumulation of highly toxic elements like Pb, Ni, Cr, Cu, Cd, Co, V and some others, which represents a real and very high risk for public health whenever grasses and edible crops growing on them absorb these elements above critical or permissible limits. To evaluate the magnitude of this problem three different soils of the Sabana were subjected to the chemical speciation procedure proposed by Tessier (1979) in order to determine: 1) the total content of essential and/or structural elements like Al, Fe, Ca, K, P, Mn and Ti, and the trace elements Pb, Ni, Cr, Cu, Cd, Co and V accumulated through time in the soils; 2) the relative proportion on which each one of them are linked to the different components or fractions of soils (ex. exchangeable, CO 3 , Fe/Mn oxides, O.M. and sulfides, and residual fraction) and 3) the bioavailability or amount of each that could be really absorbed by plants or able to go down to the underground water. Results showed in general for all soils normal values for the essential and/or structural elements and high to very high levels of Pb, Ni, Cu, Cd, Cr, Co y V, higher in Jardines de Colombia and Las Parcelas farms soils than in el Recreo farm soils. This situation is aggravated by the relatively high mobility and high concentration and bioavailability of some of these elements, which increase the risk for public health and the possibility of its migration down to the underground waters

An anti CuO{sub 2}-type metal hydride square net structure in Ln{sub 2}M{sub 2}As{sub 2}H{sub x} (Ln = La or Sm, M = Ti, V, Cr, or Mn)

Energy Technology Data Exchange (ETDEWEB)

Mizoguchi, Hiroshi; Park, SangWon; Hosono, Hideo [Materials Research Center for Element Strategy, Tokyo Institute of Technology, Yokohama 226-8503 (Japan); Hiraka, Haruhiro; Ikeda, Kazutaka; Otomo, Toshiya [Institute of Materials Structure Science, High-Energy Accelerator Research Organization (KEK), Tsukuba 305-0801 (Japan)

2015-03-02

Using a high pressure technique and the strong donating nature of H{sup -}, a new series of tetragonal La{sub 2}Fe{sub 2}Se{sub 2}O{sub 3}-type layered mixed-anion arsenides, Ln{sub 2}M{sub 2}As{sub 2}H{sub x}, was synthesized (Ln=La or Sm, M=Ti, V, Cr, or Mn; x∼3). In these compounds, an unusual M{sub 2}H square net, which has anti CuO{sub 2} square net structures accompanying two As{sup 3-} ions, is sandwiched by (LaH){sub 2} fluorite layers. Notably, strong metal-metal bonding with a distance of 2.80 Aa was confirmed in La{sub 2}Ti{sub 2}As{sub 2}H{sub 2.3}, which has metallic properties. In fact, these compounds are situated near the boundary between salt-like ionic hydrides and transition-metal hydrides with metallic characters. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

Lattice parameter values and phase transitions for the Cu2Cd1-zMn zGeSe4 and Cu2Cd1-zFe zGeSe4 alloys

International Nuclear Information System (INIS)

Quintero, E.; Tovar, R.; Quintero, M.; Delgado, G.E.; Morocoima, M.; Caldera, D.; Ruiz, J.; Mora, A.E.; Briceno, M.; Fernandez, J.L.

2007-01-01

X-ray powder diffraction measurements and differential thermal analysis (DTA) were made on polycrystalline samples of the Cu 2 Cd 1-z Mn z GeSe 4 and Cu 2 Cd 1-z Fe z GeSe 4 alloy systems. The diffraction patterns were used to show the equilibrium conditions and to derive lattice parameter values. The effect of the annealing temperature and cooling rate to room temperature are discussed. For the Cu 2 Cd 1-z Fe z GeSe 4 system, only two single solid phase fields, the tetragonal stannite α and the wurtz-stannite δ structures were found to occur in the diagram. For the Cu 2 Cd 1-z Mn z GeSe 4 system, in addition to the tetragonal stannite α and the wurtz-stannite δ phases, MnSe was found to exist in the diagram. The DTA experiments showed that the cooling curves for both systems exhibited effects of undercooling

Correlation between electron work functions of multiphase Cu-8Mn-8Al and de-alloying corrosion

Science.gov (United States)

Punburi, P.; Tareelap, N.; Srisukhumbowornchai, N.; Euaruksakul, C.; Yordsri, V.

2018-05-01

Low energy electron emission microscopy (LEEM) was used to measure local transition energy that was directly correlated to electron work function (EWF) of multiphase manganese-aluminum bronze alloys. We developed color mapping to distinguish the EWF of multiple phases and clarified that the EWF were in the following order: EWF of α > EWF of β > EWF of κ (EWFα > EWFβ > EWFκ). De-alloying corrosion took place due to the micro-galvanic cell at grain boundaries before it propagated into the β phase that had lower EWF than the α phase. The α phase was a stable phase because it contained high Cu while the β phase contained high Al and Mn. In addition, XRD analysis showed that the texture coefficient of the β phase revealed that almost all of the grains had (2 2 0) orientation, the lowest EWF compared to (1 1 1) and (2 0 0). Furthermore, transmission electron microscopy illustrated that there were fine Cu3Mn2Al precipitates in the Cu2MnAl matrix of the β phase. These precipitates formed micro-galvanic cells which played an important role in accelerating de-alloying corrosion.

Preparation of monolayers of Mn{sub 6}Cr single-molecule-magnets on different substrates and characterization by means of nc-AFM

Energy Technology Data Exchange (ETDEWEB)

Gryzia, Aaron; Brechling, Armin; Predatsch, Hans; Heinzmann, Ulrich [Faculty of Physics, Bielefeld University, D-33615 Bielefeld (Germany); Glaser, Thorsten [Faculty of Chemistry, Bielefeld University, D-33615 Bielefeld (Germany)

2011-07-01

The preparation of a highly ordered monolayer of Single-Molecule-Magnets (SMM) is one of the main preconditions for a technical application of these molecules. The adsorption of these SMMs on surfaces is associated with difficulties due to the often low chemical stability of these molecules in the vicinity of a surface. The used Mn{sub 6}Cr-complex has a C{sub 3}-symmetry and a spin ground state of S{sub t}=21/2. This complex is a trication and needs therefore counter ions for electrical charge compensation. Tetraphenylborate, lactate and perchlorate came into consideration for this function. Mn{sub 6}Cr-SMMs were prepared on different substrates by a droplet technique in air at room temperature. The samples were characterized by means of an AFM operating in non-contact mode, using tips with cone radii of approx. 2 nm. An island-like growth was observed on SiO{sub 2}- and Si{sub 3}N{sub 4}-substrates, whereas on HOPG and mica the Mn{sub 6}Cr-SMM adsorbates preferred a layer growth. Also an influence of the used counter ions was observed on different substrates. The measured thicknesses of the layers are consistent with the Van der Waals radii of the Mn{sub 6}Cr-SMMs.

Hydrogen storage properties of LaMgNi{sub 3.6}M{sub 0.4} (M = Ni, Co, Mn, Cu, Al) alloys

Energy Technology Data Exchange (ETDEWEB)

Yang, Tai [Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081 (China); Key Laboratory of Integrated Exploitation of Baiyun Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Zhai, Tingting; Yuan, Zeming; Bu, Wengang [Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081 (China); Xu, Sheng [Key Laboratory of Integrated Exploitation of Baiyun Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou 014010 (China); Zhang, Yanghuan, E-mail: zhangyh59@sina.com [Department of Functional Material Research, Central Iron and Steel Research Institute, Beijing 100081 (China); Key Laboratory of Integrated Exploitation of Baiyun Obo Multi-Metal Resources, Inner Mongolia University of Science and Technology, Baotou 014010 (China)

2014-12-25

Highlights: • La–Mg–Ni system AB{sub 2}-type alloys were prepared by induction melting. • Structures and lattice parameters were analysed by XRD. • Hydrogen absorption/desorption performances were studied. • Mechanisms of hydrogen absorption capacity fading were investigated. - Abstract: LaMgNi{sub 3.6}M{sub 0.4} (M = Ni, Co, Mn, Cu, Al) alloys were prepared through induction melting process. The phase compositions and crystal structures were characterised via X-ray diffraction (XRD). The hydrogen storage properties, including activation performance, hydrogen absorption capacity, cycle stability, alloy particle pulverisation and plateau pressure, were systemically investigated. Results show that Ni, Co, Mn and Cu substitution alloys exhibit multiphase structures comprising the main phase LaMgNi{sub 4} and the secondary phase LaNi{sub 5}. However, the secondary phase of the Al substitution alloy changes into LaAlNi{sub 4}. The lattice parameters and cell volumes of the LaMgNi{sub 4} phase follow the order Ni < Co < Al < Cu < Mn. Activation is simplified through partial substitution of Ni with Al, Cu and Co. The hydrogen absorption capacities of all of the alloys are approximately 1.7 wt.% at the first activation process; however, they rapidly decrease with increasing cycle number. In addition, the stabilities of hydriding and dehydriding cycles decrease in the order Al > Co > Ni > Cu > Mn. Hydriding processes result in numerous cracks and amorphisation of the LaMgNi{sub 4} phase in the alloys. The p–c isotherms were determined by a Sieverts-type apparatus. Two plateaus were observed for the Ni, Co and Al substitution alloys, whereas only one plateau was found for Mn and Cu. This result was caused by the amorphisation of the LaMgNi{sub 4} phase during the hydriding cycles. Reversible absorption and desorption of hydrogen are difficult to achieve. Substitutions of Ni with Co, Mn, Cu and Al significantly influence the reduction of hysteresis between

Graphite furnace analysis of a series of metals (Cu, Mn, Pb, Zn and Cd) in ox kidney

International Nuclear Information System (INIS)

Souza, Vivianne L.B. de; Nascimento, Rizia K. do; Paiva, Ana Claudia de; Silva, Josenilda M. da; Melo, Jessica V. de

2013-01-01

The aim of this study was to create a methodology for animal tissue analysis, with the use of flame atomic absorption spectrophotometry techniques and graphite furnace analysis to determining metal concentrations in ox kidney. The organ of this animal can be considered a great nutritional food, due to the high protein and micronutrient content beyond the ability to absorb and concentrate important metals such as Zn, Fe, Mn and Se. On the other hand, there is a risk when eating this food owing to the capacity to accumulate toxic metals such as Pb and Cd. In accordance with the laboratory analysis, Zn can be analyzed by flame atomic absorption spectrophotometry, but other metals such as Cu, Mn, Pb and Cd, could only be detected by graphite furnace analysis. The results showed that there is more Zn and Cu than other metals. Such metals follows an order reported by the literature (Zn > Cu > Cd > Pb > Mn). The results showed that kidney is actually a rich source of Zn and Cu. The Cd levels in the ox kidney did not exceed the values which cause toxic effects. The adequacy of the results indicates that the proposed methodology can be used for animal tissue analysis.(author)

Graphite furnace analysis of a series of metals (Cu, Mn, Pb, Zn and Cd) in ox kidney

Energy Technology Data Exchange (ETDEWEB)

Souza, Vivianne L.B. de; Nascimento, Rizia K. do; Paiva, Ana Claudia de; Silva, Josenilda M. da, E-mail: vlsouza@cnen.gov.br, E-mail: riziakelia@hotmail.com, E-mail: acpaiva@cnen.gov.br, E-mail: jmnilda@hotmail.com [Centro Regional de Ciencias Nucleares do Nordeste (CRCN-NE/CNEN-PE), Recife, PE (Brazil); Melo, Jessica V. de, E-mail: Jessica_clorofila@hotmail.com [Universidade de Pernambuco, Recife, PE (Brazil)

2013-07-01

The aim of this study was to create a methodology for animal tissue analysis, with the use of flame atomic absorption spectrophotometry techniques and graphite furnace analysis to determining metal concentrations in ox kidney. The organ of this animal can be considered a great nutritional food, due to the high protein and micronutrient content beyond the ability to absorb and concentrate important metals such as Zn, Fe, Mn and Se. On the other hand, there is a risk when eating this food owing to the capacity to accumulate toxic metals such as Pb and Cd. In accordance with the laboratory analysis, Zn can be analyzed by flame atomic absorption spectrophotometry, but other metals such as Cu, Mn, Pb and Cd, could only be detected by graphite furnace analysis. The results showed that there is more Zn and Cu than other metals. Such metals follows an order reported by the literature (Zn > Cu > Cd > Pb > Mn). The results showed that kidney is actually a rich source of Zn and Cu. The Cd levels in the ox kidney did not exceed the values which cause toxic effects. The adequacy of the results indicates that the proposed methodology can be used for animal tissue analysis.(author)

Periodic table of 3d-metal dimers and their ions.

Science.gov (United States)

Gutsev, G L; Mochena, M D; Jena, P; Bauschlicher, C W; Partridge, H

2004-10-08

The ground states of the mixed 3d-metal dimers TiV, TiCr, TiMn, TiFe, TiCo, TiNi, TiCu, TiZn, VCr, VMn, VFe, VCo, VNi, VCu, VZn, CrMn, CrFe, CrCo, CrNi, CrCu, CrZn, MnFe, MnCo, MnNi, MnCu, MnZn, FeCo, FeNi, FeCu, FeZn, CoNi, CoCu, CoZn, NiCu, NiZn, and CuZn along with their singly negatively and positively charged ions are assigned based on the results of computations using density functional theory with generalized gradient approximation for the exchange-correlation functional. Except for TiCo and CrMn, our assignment agrees with experiment. Computed spectroscopic constants (r(e),omega(e),D(o)) are in fair agreement with experiment. The ground-state spin multiplicities of all the ions are found to differ from the spin multiplicities of the corresponding neutral parents by +/-1. Except for TiV, MnFe, and MnCu, the number of unpaired electrons, N, in a neutral ground-state dimer is either N(1)+N(2) or mid R:N(1)-N(2)mid R:, where N(1) and N(2) are the numbers of unpaired 3d electrons in the 3d(n)4s(1) occupation of the constituent atoms. Combining the present and previous results obtained at the same level of theory for homonuclear 3d-metal and ScX (X=Ti-Zn) dimers allows one to construct "periodic" tables of all 3d-metal dimers along with their singly charged ions.

Effect of Ti content on structure and properties of Al2CrFeNiCoCuTix high-entropy alloy coatings

International Nuclear Information System (INIS)