  1. Modelling of Corrosion Cracks

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed.......Modelling of corrosion cracking of reinforced concrete structures is complicated as a great number of uncertain factors are involved. To get a reliable modelling a physical and mechanical understanding of the process behind corrosion in needed....

  2. A Fracture Probability Competition Mechanism of Stress Corrosion Cracking

    Institute of Scientific and Technical Information of China (English)

    Yanliang HUANG

    2001-01-01

    The stress corrosion cracking (SCC) of austenitic stainless steel was studied via polarization,slow strain rate and scanning electron microscope (SEM) techniques. Many SCC mechanisms have been proposed in which hydrogen embrittlement and passive film rupture-repassivation theories are generally accepted, but they can hardly explain the SCC mechanism of austenitic stainless steel in acidic chloride solution adequately, because the steel is in active dissolution state and cathodic polarization can prevent it from occurring. Our experiment shows that the anodic current increases the creep rate and decreases the plastic strength of the material on single smooth specimen as well as at the SCC crack tip. The fractured surface was characterized as brittle cleavage, while the surface crack of smooth specimen was almost vertical to the tensile strength, which can confirm that the cracks were caused by tensile stresses. A fracture probability competition mechanism of SCC was proposed on the basis of the experimental results combined with the viewpoint of ductile-brittle fracture competition. When the anodic dissolution current is increased to a certain degree, the probability of fracture by tensile stress will exceed that by shear stress, and the brittle fracture will occur. The proposed SCC mechanism can not only explain the propagation of SCC cracks but can explain the crack initiation as well. The strain on the surface distributes unevenly when a smooth specimen is deformed, so does the anodic current distribution. The crack will initiate at a point where the anodic current density is large enough to cause the material at a specific point to fracture in brittle manner.

  3. Computational modeling of the mechanism of hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals

    Science.gov (United States)

    Cendales, E. D.; Orjuela, F. A.; Chamarraví, O.

    2016-02-01

    In this article theoretical models and some existing data sets were examined in order to model the two main causes (hydrogen embrittlement and corrosion-cracking under stress) of the called environmentally assisted cracking phenomenon (EAC). Additionally, a computer simulation of flat metal plate subject to mechanical stress and cracking due both to hydrogen embrittlement and corrosion was developed. The computational simulation was oriented to evaluate the effect on the stress-strain behavior, elongation percent and the crack growth rate of AISI SAE 1040 steel due to three corrosive enviroments (H2 @ 0.06MPa; HCl, pH=1.0; HCl, pH=2.5). From the computer simulation we conclude that cracking due to internal corrosion of the material near to the crack tip limits affects more the residual strength of the flat plate than hydrogen embrittlement and generates a failure condition almost imminent of the mechanical structural element.

  4. Dissolution Condensation Mechanism of Stress Corrosion Cracking in Liquid Metals: Driving Force and Crack Kinetics

    Science.gov (United States)

    Glickman, Evgeny E.

    2011-02-01

    Stress corrosion cracking (SCC) in aqueous solution is driven by exothermic reactions of metal oxidation. This stimulus, as well as classical mechanisms of SCC, does not apply to SCC in liquid metals (LMs). In the framework of the dissolution-condensation mechanism (DCM), we analyzed the driving force and crack kinetics for this nonelectrochemical mode of SCC that is loosely called "liquid metal embrittlement" (LME). According to DCM, a stress-induced increase in chemical potential at the crack tip acts as the driving force for out-of-the-tip diffusion mass transfer that is fast because diffusion in LMs is very fast and surface energy at the solid-liquid interface is small. In this article, we review two versions of DCM mechanism, discuss the major physics behind them, and develop DCM further. The refined mechanism is applied then to the experimental data on crack velocity V vs stress intensity factor, the activation energy of LME, and alloying effects. It is concluded that DCM provides a good conceptual framework for analysis of a unified kinetic mechanism of LME and may also contribute to SCC in aqueous solutions.

  5. Research on mechanisms of stress corrosion cracking in Zircaloy

    Energy Technology Data Exchange (ETDEWEB)

    Knorr, D.B.; Pelloux, R.M.

    1981-06-01

    The results of internal gas pressurization tests, primarily at 320/sup 0/C, on cladding tubes from two suppliers, Supplier A and Supplier B, are presented. The two lots show a substantial difference in iodine SCC susceptibility so a test matrix is used to resolve the relative contributions of surface condition, residual stress, and texture. Additional tests with constant deflection split-ring specimens and with unstressed cladding segments are used to understand crack initiation and the early crack growth stages of SCC. The difference in SCC susceptibility is due to crystallographic texture. Other variables such as surface finish, stress relief temperature, and residual stress have little or no effect. Mechanical properties, crack initiation, and crack propagation all depend on texture. Both initiation and propagation features are analyzed by scanning electron microscopy. A mechanism for crack initiation consistent with most observations in this study and with the work of other investigators is proposed. At 320/sup 0/C, lifetime is crack initiation limited while several tests at 390/sup 0/C indicate that lifetime is less initiation limited at higher temperature. 31 figures, 9 tables.

  6. Mechanical factors in primary water stress corrosion cracking of cold-worked stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Hammadi, Rashid Al, E-mail: rashid.alhammadi@fanr.gov.ae [Nuclear Security Division, Federal Authority for Nuclear Regulation, Abu Dhabi (United Arab Emirates); Yi, Yongsun, E-mail: yongsun.yi@kustar.ac.ae [Department of Nuclear Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Zaki, Wael, E-mail: wael.zaki@kustar.ac.ae [Department of Mechanical Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Cho, Pyungyeon, E-mail: pyungyeon.cho@kustar.ac.ae [Department of Nuclear Engineering, Khalifa University, Abu Dhabi (United Arab Emirates); Jang, Changheui, E-mail: chjang@kaist.ac.kr [Nuclear and Quantum Engineering Department, Korea Advanced Institute of Science and Technology, Daejeon (Korea, Republic of)

    2016-05-15

    Highlights: • PWSCC of cold-worked austenitic stainless steel was studied. • Finite element analysis was performed on a compact tension specimen. • Mechanical fields near a crack tip were evaluated using FEA. • The dependence of mechanical factors on K{sub I} and yield stress was investigated. • The crack tip normal stress was identified as a main factor controlling PWSCC. - Abstract: Finite element analysis was performed on a compact tension specimen to determine the stress and strain distributions near a crack tip. Based on the results, the crack tip stain rates by crack advance and creep rates near crack tip were estimated. By comparing the dependence of the mechanical factors on the stress intensity factor and yield stress with that of the SCC crack growth rates, it was tried to identify the main mechanical factor for the primary water stress corrosion cracking (PWSCC) of cold-worked austenitic stainless steels. The analysis results showed that the crack tip normal stress could be the main mechanical factor controlling the PWSCC, suggesting that the internal oxidation mechanism might be the most probable PWSCC mechanism of cold-worked austenitic stainless steels.

  7. Mechanism of intergranular stress corrosion cracking in HAZ for super-martensitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Miyata, Yukio; Kimura, Mitsuo [Tubular Products and Casting Research Dept., JFE Steel Corporation, 1-1, Kawasaki-cho, Handa (Japan); Nakamichi, Haruo; Sato, Kaoru [Analysis and Characterization Research Dept., JFE Steel Corporation, 1-1, Minamiwatarida-cho, Kawasaki-ku, Kawasaki (Japan); Itakura, Noritsugu [Products Service and Development Dept., Chita Works, JFE Steel Corporation. 1-1, Kawasaki-cho, Handa (Japan); Masamura, Katsumi [Tubular Products Business Planning Dept., JFE Steel Corporation, 2-2-3, Uchisaiwai-sho, Chiyoda-ku, Tokyo (Japan)

    2004-07-01

    Mechanism of intergranular stress corrosion cracking (IGSCC) for heat affected zone (HAZ) of super-martensitic stainless steel was studied using two types of the steel. One was a lean grade, which was Mo free and low Ni, and the other was a high grade, which was Mo added and high Ni. Specimens received heat treatments simulating welding thermal cycles were applied to SCC tests. Cracks were observed in some specimens after U-bend SCC test under low pH environments. Thermal cycle conditions with sensitization were verified from the results. No crack was observed in the specimen with the thermal cycle simulating post welding heat treatment (PWHT) after sensitizing conditions. Therefore, PWHT was clarified to be effective to prevent the cracking. Cr carbides were observed along prior austenite grain boundary intermittently, and Cr depleted zone was confirmed on the grain boundary adjacent to carbides that precipitated on the grain boundary. It is, therefore, concluded that the cracking results from Cr depletion on prior austenite grain boundary accompanied by precipitation of Cr carbides under specific welding conditions. (authors)

  8. The mechanism of stress-corrosion cracking in 7075 aluminum alloy

    Science.gov (United States)

    Jacobs, A. J.

    1970-01-01

    Various aspects of stress-corrosion cracking in 7075 aluminum alloy are discussed. A model is proposed in which the continuous anodic path along which the metal is preferentially attacked consists of two phases which alternate as anodes.

  9. Assessment of Initial Test Conditions for Experiments to Assess Irradiation Assisted Stress Corrosion Cracking Mechanisms

    Energy Technology Data Exchange (ETDEWEB)

    Busby, Jeremy T [ORNL; Gussev, Maxim N [ORNL

    2011-04-01

    Irradiation-assisted stress corrosion cracking is a key materials degradation issue in today s nuclear power reactor fleet and affects critical structural components within the reactor core. The effects of increased exposure to irradiation, stress, and/or coolant can substantially increase susceptibility to stress-corrosion cracking of austenitic steels in high-temperature water environments. . Despite 30 years of experience, the underlying mechanisms of IASCC are unknown. Extended service conditions will increase the exposure to irradiation, stress, and corrosive environment for all core internal components. The objective of this effort within the Light Water Reactor Sustainability program is to evaluate the response and mechanisms of IASCC in austenitic stainless steels with single variable experiments. A series of high-value irradiated specimens has been acquired from the past international research programs, providing a valuable opportunity to examine the mechanisms of IASCC. This batch of irradiated specimens has been received and inventoried. In addition, visual examination and sample cleaning has been completed. Microhardness testing has been performed on these specimens. All samples show evidence of hardening, as expected, although the degree of hardening has saturated and no trend with dose is observed. Further, the change in hardening can be converted to changes in mechanical properties. The calculated yield stress is consistent with previous data from light water reactor conditions. In addition, some evidence of changes in deformation mode was identified via examination of the microhardness indents. This analysis may provide further insights into the deformation mode under larger scale tests. Finally, swelling analysis was performed using immersion density methods. Most alloys showed some evidence of swelling, consistent with the expected trends for this class of alloy. The Hf-doped alloy showed densification rather than swelling. This observation may be

  10. Corrosion and Cracking of Reinforced Concrete

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Modelling of the deterioration of reinforced concrete has in recent years changed from being a deterministic modelling based on experience to be stochastic modelling based on sound and consistent physical, chemical and mechanical principles. In this paper is presented a brief review of modern mod...... for time to initial corrosion, time to initial cracking, and time to a given crack width may be obtained....

  11. Cracking and corrosion recovery boiler

    Energy Technology Data Exchange (ETDEWEB)

    Suik, H. [Tallinn Technical University, Horizon Pulp and Paper, Tallinn (Estonia)

    1998-12-31

    The corrosion of heat surfaces and the cracking the drums are the main problems of the recovery boiler. These phenomena have been appeared during long-term operation of boiler `Mitsubishi - 315` erected at 1964. Depth of the crack is depending on the number of shutdowns and on operation time. Corrosion intensity of different heat surfaces is varying depend on the metal temperature and the conditions at place of positioning of tube. The lowest intensity of corrosion is on the bank tubes and the greatest is on the tubes of the second stage superheater and on the tubes at the openings of air ports. (orig.) 5 refs.

  12. In vivo oxide-induced stress corrosion cracking of Ti-6Al-4V in a neck-stem modular taper: Emergent behavior in a new mechanism of in vivo corrosion.

    Science.gov (United States)

    Gilbert, Jeremy L; Mali, Sachin; Urban, Robert M; Silverton, Craig D; Jacobs, Joshua J

    2012-02-01

    In vivo modular taper corrosion in orthopedic total joint replacements has been documented to occur for head-neck tapers, modular-body tapers, and neck-stem tapers. While the fretting corrosion mechanism by which this corrosion occurs has been described in the literature, this report shows new and as yet unreported mechanisms at play. A retrieved Ti-6Al-4V/Ti-6Al-4V neck-stem taper interface, implanted for 6 years is subjected to failure analysis to document taper corrosion processes that lead to oxide driven crack formation on the medial side of the taper. Metallurgical sectioning techniques and scanning electron microscopy analysis are used to document the taper corrosion processes. The results show large penetrating pitting attack of both sides of the taper interface where corrosion selectively attacks the beta phase of the microstructure and eventually consumes the alpha phase. The pitting attack evolves into plunging pits that ultimately develop into cracks where the crack propagation process is one of corrosion resulting in oxide formation and subsequent reorganization. This process drives open the crack and advances the front by a combination of oxide-driven crack opening stresses and corrosion attack at the tip. The oxide that forms has a complex evolving structure including a network of transport channels that provide access of fluid to the crack tip. This emergent behavior does not appear to require continued fretting corrosion to propagate the pitting and cracking. This new mechanism is similar to stress corrosion cracking where the crack tip stresses arise from the oxide formation in the crack and not externally applied tensile stresses.

  13. Stress Corrosion Cracking of Pipeline Steels

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    This paper provides a review of the differences between high pH and near-neutral pH stress corrosion cracking ofpipeline steels, influencing factors, and mechanisms. The characteristics and historical information on both forms ofSCC are discussed. The prospect for research in the future is also presented.

  14. Embrittlement and anodic process in stress corrosion cracking: study of the influent micro-mechanical parameters; Fragilisation et processus anodiques en corrosion sous contrainte: etude des parametres micro-mecaniques influents

    Energy Technology Data Exchange (ETDEWEB)

    Tinnes, J.Ph

    2006-11-15

    We study the influence of local mechanical parameters on crack propagation in Stress Corrosion Cracking, at the scale of the microstructure. Two systems are compared: the CuAl{sub 9}Ni{sub 3}Fe{sub 2} copper-aluminium alloy in synthetic sea water under cathodic polarization, where the crack propagation mechanism is related to strain-assisted anodic dissolution, and the 316L austenitic stainless steel in MgCl{sub 2} solution, where embrittlement mechanisms related to hydrogen effects prevail. We use micro-notched tensile specimen that allow to study isolated short cracks. These experiments are modelled by means of finite elements calculations, and further characterized by Electron Back scattered Diffraction (EBSD) in the case of the 316L alloy. In terms of the local mechanical parameters that control propagation, fundamental differences are outlined between the two systems. They are discussed from the viewpoint of the available models of Stress Corrosion Cracking. (author)

  15. A study on the mechanism of stress corrosion cracking of duplex stainless steels in hot alkaline-sulfide solution

    Science.gov (United States)

    Chasse, Kevin Robert

    Duplex stainless steels (DSS) generally have superior strength and corrosion resistance as compared to most standard austenitic and ferritic stainless grades owing to a balanced microstructure of austenite and ferrite. As a result of having favorable properties, DSS have been selected for the construction of equipment in pulp and paper, chemical processing, nuclear, oil and gas as well as other industries. The use of DSS has been restricted in some cases because of stress corrosion cracking (SCC), which can initiate and grow in either the ferrite or austenite phase depending on the environment. Thorough understanding of SCC mechanisms of DSS in chloride- and hydrogen sulfide-containing solutions has been useful for material selection in many environments. However, understanding of SCC mechanisms of DSS in sulfide-containing caustic solutions is limited, which has restricted the capacity to optimize process and equipment design in pulp and paper environments. Process environments may contain different concentrations of hydroxide, sulfide, and chloride, altering corrosion and SCC susceptibility of each phase. Crack initiation and growth behavior will also change depending on the relative phase distribution and properties of austenite and ferrite. The role of microstructure and environment on the SCC of standard grade UNS S32205 and lean grade UNS S32101 in hot alkaline-sulfide solution were evaluated in this work using electrochemical, film characterization, mechanical testing, X-ray diffraction, and microscopy techniques. Microstructural aspects, which included residual stress state, phase distribution, phase ratio, and microhardness, were related to the propensity for SCC crack initiation in different simulated alkaline pulping liquors at 170 °C. Other grades of DSS and reference austenitic and superferritic grades of stainless steel were studied using exposure coupons for comparison to understand compositional effects and individual phase susceptibility

  16. Stress-corrosion cracking of titanium alloys.

    Science.gov (United States)

    Blackburn, M. J.; Feeney, J. A.; Beck, T. R.

    1973-01-01

    In the light of research material published up to May 1970, the current understanding of the experimental variables involved in the stress-corrosion cracking (SCC) behavior of titanium and its alloys is reviewed. Following a brief summary of the metallurgy and electrochemistry of titanium alloys, the mechanical, electrochemical, and metallurgical parameters influencing SCC behavior are explored with emphasis on crack growth kinetics. Macro- and microfeatures of fractures are examined, and it is shown that many transgranular SCC failures exhibit morphological and crystallographic features similar to mechanical cleavage failures. Current SCC models are reviewed with respect to their ability to explain the observed SCC behavior of titanium and its alloys. Possible methods for eliminating or minimizing stress corrosion hazards in titanium or titanium alloy components are described.

  17. Transport and Corrosion Behavior of Cracked Reinforced Concrete

    DEFF Research Database (Denmark)

    Pease, Bradley Justin

    to enter the concrete. This is, among others, important in the corrosion of reinforcing steel. When cracks protrude to the depth of reinforcing steel, liquids containing aggressive ions (i.e. chlorides associated with salts and sea water) may rapidly access and initiate corrosion of the reinforcing...... structures. These models currently lack some of the scientific validity to fully represent actual field structures, i.e. structures containing cracks. Further understanding, therefore is needed on the effect cracks have on transport and corrosion in reinforced concrete. The fundamental mechanisms...... of transport and corrosion in cracked, reinforced concrete are not yet fully understood. The scope of this study therefore is to develop a link between concrete cracks and the relevant transport mechanism(s) under particular environmental conditions. It is envisioned that a finite element model...

  18. Numerical Study of Corrosion Crack Opening

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle; Frandsen, Henrik Lund; Svensson, Staffan

    2008-01-01

    for the corrosion crack opening. Experiments and theoretical analysis by a numerical method, FEM, support that the relation between the reduction of the reinforcement bar diameter due to corrosion and the corresponding increase in crack width for a given time interval, measured on the surface of a concrete specimen...... is proportional. More recently, the constant of proportionality, the so-called crack-corrosion index, has been studied further with respect to its dependence on the diameter of the reinforcement and the concrete cover. In the present paper the above-mentioned work is presented and extended with more realistic 3D......-models of the cracked concrete beam. The crack-corrosion index is evaluated for a variation of different parameters, i.e. bar diameter, concrete cover, crack length and type of corrosion product. This paper is an extended version of a paper by Thoft-Christensen et al. (2005) presented at the IFIP WG 7.5 Conference...

  19. Stress corrosion cracking of copper canisters

    Energy Technology Data Exchange (ETDEWEB)

    King, Fraser (Integrity Corrosion Consulting Limited (Canada)); Newman, Roger (Univ. of Toronto (Canada))

    2010-12-15

    A critical review is presented of the possibility of stress corrosion cracking (SCC) of copper canisters in a deep geological repository in the Fennoscandian Shield. Each of the four main mechanisms proposed for the SCC of pure copper are reviewed and the required conditions for cracking compared with the expected environmental and mechanical loading conditions within the repository. Other possible mechanisms are also considered, as are recent studies specifically directed towards the SCC of copper canisters. The aim of the review is to determine if and when during the evolution of the repository environment copper canisters might be susceptible to SCC. Mechanisms that require a degree of oxidation or dissolution are only possible whilst oxidant is present in the repository and then only if other environmental and mechanical loading conditions are satisfied. These constraints are found to limit the period during which the canisters could be susceptible to cracking via film rupture (slip dissolution) or tarnish rupture mechanisms to the first few years after deposition of the canisters, at which time there will be insufficient SCC agent (ammonia, acetate, or nitrite) to support cracking. During the anaerobic phase, the supply of sulphide ions to the free surface will be transport limited by diffusion through the highly compacted bentonite. Therefore, no HS. will enter the crack and cracking by either of these mechanisms during the long term anaerobic phase is not feasible. Cracking via the film-induced cleavage mechanism requires a surface film of specific properties, most often associated with a nano porous structure. Slow rates of dissolution characteristic of processes in the repository will tend to coarsen any nano porous layer. Under some circumstances, a cuprous oxide film could support film-induced cleavage, but there is no evidence that this mechanism would operate in the presence of sulphide during the long-term anaerobic period because copper sulphide

  20. Three-dimensional characterization of stress corrosion cracks

    DEFF Research Database (Denmark)

    Lozano-Perez, S.; Rodrigo, P.; Gontard, Lionel Cervera

    2011-01-01

    Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome...... the best spatial resolution. To illustrate the power of these techniques, different parts of dominant stress corrosion cracks in Ni-alloys and stainless steels have been reconstructed in 3D. All relevant microstructural features can now be studied in detail and its relative orientation respect...

  1. A Monitoring Method Based on FBG for Concrete Corrosion Cracking

    Science.gov (United States)

    Mao, Jianghong; Xu, Fangyuan; Gao, Qian; Liu, Shenglin; Jin, Weiliang; Xu, Yidong

    2016-01-01

    Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure. PMID:27428972

  2. A Monitoring Method Based on FBG for Concrete Corrosion Cracking

    Directory of Open Access Journals (Sweden)

    Jianghong Mao

    2016-07-01

    Full Text Available Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure.

  3. A Monitoring Method Based on FBG for Concrete Corrosion Cracking.

    Science.gov (United States)

    Mao, Jianghong; Xu, Fangyuan; Gao, Qian; Liu, Shenglin; Jin, Weiliang; Xu, Yidong

    2016-07-14

    Corrosion cracking of reinforced concrete caused by chloride salt is one of the main determinants of structure durability. Monitoring the entire process of concrete corrosion cracking is critical for assessing the remaining life of the structure and determining if maintenance is needed. Fiber Bragg Grating (FBG) sensing technology is extensively developed in photoelectric monitoring technology and has been used on many projects. FBG can detect the quasi-distribution of strain and temperature under corrosive environments, and thus it is suitable for monitoring reinforced concrete cracking. According to the mechanical principle that corrosion expansion is responsible for the reinforced concrete cracking, a package design of reinforced concrete cracking sensors based on FBG was proposed and investigated in this study. The corresponding relationship between the grating wavelength and strain was calibrated by an equal strength beam test. The effectiveness of the proposed method was verified by an electrically accelerated corrosion experiment. The fiber grating sensing technology was able to track the corrosion expansion and corrosion cracking in real time and provided data to inform decision-making for the maintenance and management of the engineering structure.

  4. Strain rate effects in stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Parkins, R.N. (Newcastle upon Tyne Univ. (UK). Dept. of Metallurgy and Engineering Materials)

    1990-03-01

    Slow strain rate testing (SSRT) was initially developed as a rapid, ad hoc laboratory method for assessing the propensity for metals an environments to promote stress corrosion cracking. It is now clear, however, that there are good theoretical reasons why strain rate, as opposed to stress per se, will often be the controlling parameter in determining whether or not cracks are nucleated and, if so, are propagated. The synergistic effects of the time dependence of corrosion-related reactions and microplastic strain provide the basis for mechanistic understanding of stress corrosion cracking in high-pressure pipelines and other structures. However, while this may be readily comprehended in the context of laboratory slow strain tests, its extension to service situations may be less apparent. Laboratory work involving realistic stressing conditions, including low-frequency cyclic loading, shows that strain or creep rates give good correlation with thresholds for cracking and with crack growth kinetics.

  5. Analytical Solutions for Corrosion-Induced Cohesive Concrete Cracking

    Directory of Open Access Journals (Sweden)

    Hua-Peng Chen

    2012-01-01

    Full Text Available The paper presents a new analytical model to study the evolution of radial cracking around a corroding steel reinforcement bar embedded in concrete. The concrete cover for the corroding rebar is modelled as a thick-walled cylinder subject to axisymmetrical displacement constraint at the internal boundary generated by expansive corrosion products. A bilinear softening curve reflecting realistic concrete property, together with the crack band theory for concrete fracture, is applied to model the residual tensile stress in the cracked concrete. A governing equation for directly solving the crack width in cover concrete is established for the proposed analytical model. Closed-form solutions for crack width are then obtained at various stages during the evolution of cracking in cover concrete. The propagation of crack front with corrosion progress is studied, and the time to cracking on concrete cover surface is predicted. Mechanical parameters of the model including residual tensile strength, reduced tensile stiffness, and radial pressure at the bond interface are investigated during the evolution of cover concrete cracking. Finally, the analytical predictions are examined by comparing with the published experimental data, and mechanical parameters are analysed with the progress of reinforcement corrosion and through the concrete cover.

  6. Study of alloy 600`S stress corrosion cracking mechanisms in high temperature water; Etude des mecanismes de corrosion sous contrainte de l`alliage 600 dans l`eau a haute temperature

    Energy Technology Data Exchange (ETDEWEB)

    Rios, R.

    1994-06-01

    In order to better understand the mechanisms involved in Alloy 600`s stress corrosion cracking in PWR environment, laboratory tests were performed. The influence of parameters pertinent to the mechanisms was studies : hydrogen and oxygen overpressures, local chemical composition, microstructure. The results show that neither hydrogen nor dissolution/oxidation, despite their respective roles in the process, are sufficient to account for experimental facts. SEM observation of micro-cleavage facets on specimens` fracture surfaces leads to pay attention to a new mechanism of corrosion/plasticity interactions. (author). 113 refs., 73 figs., 15 tabs., 4 annexes.

  7. Frequency dependence of fatigue and corrosion fatigue crack growth rate

    Energy Technology Data Exchange (ETDEWEB)

    Marvasti, Mohammad Hassan; Chen, Weixing [Department of Chemical and Materials Engineering, University of Alberta, Edmonton, AB (Canada); Kania, Richard; Worthingham, Robert [TransCanada Pipelines Limited, Calgary, AB (Canada); Van Boven, Gregory [Spectra Energy Transmission Limited, Vancouver, BC (Canada)

    2010-07-01

    It was in the mid-1980s that stress corrosion cracking (SCC) was first found in near-neutral pH conditions on the TransCanada pipeline system. Since then, there have been many reports of pipeline cracking in Canada in these conditions. The huge quantity of pipelines in Canada and the number of failures have brought great interest in investigation of this cracking. A study was conducted on one X52 pipeline steel. It used compact tension specimens for corrosion fatigue and fatigue tests in air. The following conclusions were drawn: 1) crack growth in near-neutral pH conditions can be explained by a factor, which reflects the combined action of the mechanical driving force and the hydrogen effects; 2) mechanical dormancy can be common when oil and gas pipelines are in operation; 3) hydrogen is a determining factor of crack growth when pipeline steels are exposed to near-neutral pH conditions.

  8. Microstructure, mechanical properties and stress corrosion cracking of Al–Zn–Mg–Zr alloy sheet with trace amount of Sc

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Xing [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Pan, Qinglin, E-mail: pql1964@126.com [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Li, Bo [School of Materials Science and Engineering, Central South University, Changsha 410083 (China); Liu, Zhiming; Huang, Zhiqi [Guangdong Fenglu Aluminum Co., Ltd, Foshan 528133 (China); Yin, Zhimin [School of Materials Science and Engineering, Central South University, Changsha 410083 (China)

    2015-11-25

    Microstructural and property evolution of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy sheet during its preparation were investigated in detail by means of optical microscopy (OM), scanning electron microscope (SEM), energy dispersive X-ray (EDX), transmission electron microscopy (TEM), Vickers micro-hardness test and room temperature tensile test. Stress corrosion cracking (SCC) behavior of the Al–Zn–Mg–0.10%Sc–0.10%Zr alloy under different heat treatments was studied using slow strain rate test. The results showed that serious dendritic segregation existed in as-cast condition. The suitable homogenization treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was 470 °C/24 h. After homogenization treatment, dissoluble Zn and Mg enriched non-equilibrium phases dissolved into α-Al matrix completely. The suitable solid solution-aging treatment for Al–Zn–Mg–0.10%Sc–0.10%Zr alloy was solution treated at 470 °C for 60 min, followed by water quenching and then aged at 120 °C for 24 h. Under this aging temper, the grain structures were composed of sub-grains, η′ phases and nanometer-sized, spherical Al{sub 3}(Sc, Zr) particles. Grain boundary precipitates (GBPs) area fraction was found to be an important parameter to evaluate the SCC susceptibility. The improved corrosion resistance from increasing aging temperature or prolonging aging time was due to the discontinuous η precipitates along the grain boundary and the high area fraction of GBPs. The main strengthening mechanisms of Al–Zn–Mg–0.10%Sc–0.10%Zr alloy are precipitation strengthening derived from η′ precipitates, dispersion strengthening, sub-grain strengthening and grain refinement caused by coherent Al{sub 3}(Sc, Zr) particles. - Highlights: • The suitable homogenization treatment of the alloy has been identified. • Evolution of microstructure and mechanical properties is investigated. • Strengthening mechanisms of the alloy has been established. • The basic mechanism has

  9. Propagation of stress corrosion cracks in alpha-brasses

    Energy Technology Data Exchange (ETDEWEB)

    Beggs, Dennis Vinton [Univ. of Illinois, Urbana-Champaign, IL (United States)

    1981-01-01

    Transgranular and intergranular stress corrosion cracks were investigated in alpha-brasses in a tarnishing ammoniacal solution. Surface observation indicated that the transgranular cracks propagated discontinuously by the sudden appearance of a fine crack extending several microns ahead of the previous crack tip, often associated with the detection of a discrete acoustic emission (AE). By periodically increasing the deflection, crack front markings were produced on the resulting fracture surfaces, showing that the discontinuous propagation of the crack trace was representative of the subsurface cracking. The intergranular crack trace appeared to propagate continuously at a relatively blunt crack tip and was not associated with discrete AE. Under load pulsing tests with a time between pulses, Δt greater than or equal to 3 s, the transgranular fracture surfaces always exhibited crack front markings which corresponded with the applied pulses. The spacing between crack front markings, Δx, decreased linearly with Δt. With Δt less than or equal to 1.5 s, the crack front markings were in a one-to-one correspondence with applied pulses only at relatively long crack lengths. In this case, Δx = Δx* which approached a limiting value of 1 μm. No crack front markings were observed on intergranular fracture surfaces produced during these tests. It is concluded that transgranular cracking occurs by discontinuous mechanical fracture of an embrittled region around the crack tip, while intergranular cracking results from a different mechanism with cracking occurring via the film-rupture mechanism.

  10. The Growth of Small Corrosion Fatigue Cracks in Alloy 7075

    Science.gov (United States)

    Piascik, Robert S.

    2015-01-01

    The corrosion fatigue crack growth characteristics of small (greater than 35 micrometers) surface and corner cracks in aluminum alloy 7075 is established. The early stage of crack growth is studied by performing in situ long focal length microscope (500×) crack length measurements in laboratory air and 1% sodium chloride (NaCl) environments. To quantify the "small crack effect" in the corrosive environment, the corrosion fatigue crack propagation behavior of small cracks is compared to long through-the-thickness cracks grown under identical experimental conditions. In salt water, long crack constant K(sub max) growth rates are similar to small crack da/dN.

  11. Application of new experimental methods to pipeline stress corrosion cracking. Annual report, March 1992-February 1993

    Energy Technology Data Exchange (ETDEWEB)

    Schmidt, C.G.; Kobayashi, T.; Becker, C.H.; Pound, B.G.; Simons, J.W.

    1993-04-01

    The objective of the investigation is to develop a physically based understanding of the mechanisms of stress corrosion cracking (SCC) in pipeline steels by applying advanced fracture surface and electrochemical characterization techniques to samples taken from fielded pipeline. The investigations found that the effect of pressure fluctuations on the propagation of stress corrosion cracks was readily evident from an analysis of the topographies of conjugate fracture surfaces. Substantial crack blunting was produced under normal pipeline operating conditions. Corrosion deposits were removed from the fracture surfaces of a stress corrosion crack in a pipeline specimen recovered from service. The topography of the underlying metal surface appears to be preserved with little corrosion damage after crack formation. This allowed the cracking process to be reconstructed from the surface topography. In some cases, deposits on the fracture surfaces of stress corrosion cracks contain significant concentrations of metallic elements that are not found in pipeline steels but are likely to be commonplace in the surrounding environment.

  12. A comparison of the stress corrosion cracking susceptibility of commercially pure titanium grade 4 in Ringer's solution and in distilled water: a fracture mechanics approach.

    Science.gov (United States)

    Roach, Michael D; Williamson, R Scott; Thomas, Joseph A; Griggs, Jason A; Zardiackas, Lyle D

    2014-01-01

    From the results of laboratory investigations reported in the literature, it has been suggested that stress corrosion cracking (SCC) mechanisms may contribute to early failures in titanium alloys that have elevated oxygen concentrations. However, the susceptibility of titanium alloys to SCC in physiological environments remains unclear. In this study, a fracture mechanics approach was used to examine the SCC susceptibility of CP titanium grade 4 in Ringer's solution and distilled de-ionized (DI) water, at 37°C. The study duration was 26 weeks, simulating the non-union declaration of a plated fracture. Four wedge loads were used corresponding to 86-95% of the alloy's ligament yield load. The longest cracks were measured to be 0.18 mm and 0.10 mm in Ringer's solution and DI water, respectively. SEM analysis revealed no evidence of extensive fluting and quasi-cleavage fracture features which, in literature reports, were attributed to SCC. We thus postulate that the Ringer's solution accelerated the wedge-loaded crack growth without producing the critical stresses needed to change the fracture mechanism. Regression analysis of the crack length results led to a significant best-fit relationship between crack growth velocity (independent variable) and test electrolyte, initial wedge load, and time of immersion of specimen in electrolyte (dependent variables).

  13. A Calculation Model for Corrosion Cracking in RC Structures

    Institute of Scientific and Technical Information of China (English)

    Xu Gang; Wei Jun; Zhang Keqiang; Zhou Xiwu

    2007-01-01

    A novel calculation model is proposed aiming at the problem of concrete cover cracking induced by reinforcement corrosion. In this article, the relationship between the corrosion depth of the bar and the thickness of the rust layer is established. By deducing the radial displacement expression of concrete, the formula for corrosion depth and corrosion pressure before cracking is proposed. The crack depth of cover in accordance with the maximum corrosion pressure is deduced; furthermore, the corrosion depth and corrosion pressure at the cracking time are obtained. Finally, the theoretical model is validated by several experiments, and the calculated values agree well with the experiment results.

  14. Three-dimensional characterization of stress corrosion cracks

    Energy Technology Data Exchange (ETDEWEB)

    Lozano-Perez, S., E-mail: sergio.lozano-perez@materials.ox.ac.u [University of Oxford, Department of Materials, Parks Road, Oxford OX1 3PH (United Kingdom); Rodrigo, P. [Universidad Rey Juan Carlos, Dpto. de Ciencia e Ingenieria de Materiales, c/ Tulipan s.n., 28933 Mostoles (Madrid) (Spain); Gontard, Lionel C. [Danish Technical University, Center for Electron Nanoscopy, Matematiktorvet Building 307, Room 115, 2800 Kogens Lyngby (Denmark)

    2011-01-31

    Understanding crack propagation and initiation is fundamental if stress corrosion cracking (SCC) mechanisms are to be understood. However, cracking is a three-dimensional (3D) phenomenon and most characterization techniques are restricted to two-dimensional (2D) observations. In order to overcome this problem, different approaches to extract 3D information have been used in the recent years. In this work we will present the benefits of using 3D focused ion beam (FIB) slicing and electron tomography. 3D FIB slicing offers a fast and high throughput characterization while electron tomography offers the best spatial resolution. To illustrate the power of these techniques, different parts of dominant stress corrosion cracks in Ni-alloys and stainless steels have been reconstructed in 3D. All relevant microstructural features can now be studied in detail and its relative orientation respect to the strain direction and grain boundary plane accurately measured.

  15. Microstructure, local mechanical properties and stress corrosion cracking susceptibility of an SA508-52M-316LN safe-end dissimilar metal weld joint by GTAW

    Energy Technology Data Exchange (ETDEWEB)

    Ming, Hongliang; Zhu, Ruolin [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); University of Chinese Academy of Sciences, 19 Yuquan Road, Beijing 100049 (China); Zhang, Zhiming [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Wang, Jianqiu, E-mail: wangjianqiu@imr.ac.cn [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Han, En.-Hou.; Ke, Wei [Key Laboratory of Nuclear Materials and Safety Assessment, Liaoning KeyLaboratory for Safety and Assessment Technique of Nuclear Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016 (China); Su, Mingxing [Shanghai Research Center for Weld and Detection Engineering Technique of Nuclear Equipment, Shanghai 201306 (China)

    2016-07-04

    The microstructure, local mechanical properties and local stress corrosion cracking susceptibility of an SA508-52M-316LN domestic dissimilar metal welded safe-end joint used for AP1000 nuclear power plant prepared by automatic gas tungsten arc welding was studied in this work by optical microscopy, scanning electron microscopy (with electron back scattering diffraction and an energy dispersive X-ray spectroscopy system), micro-hardness testing, local mechanical tensile testing and local slow strain rate tests. The micro-hardness, local mechanical properties and stress corrosion cracking susceptibility across this dissimilar metal weld joint vary because of the complex microstructure across the fusion area and the dramatic chemical composition change across the fusion lines. Briefly, Type I boundaries and Type II boundaries exist in 52Mb near the SA508-52Mb interface, a microstructure transition was found in SA508 heat affected zone, the residual strain and grain boundary character distribution changes as a function of the distance from the fusion boundary in 316LN heat affected zone, micro-hardness distribution and local mechanical properties along the DMWJ are heterogeneous, and 52Mw-316LN interface has the highest SCC susceptibility in this DMWJ while 316LN base metal has the lowest one.

  16. Sizing stress corrosion cracks using laser ultrasonics

    Energy Technology Data Exchange (ETDEWEB)

    Rehman, Hamood; McNealy, Rick; Fingerhut, Martin [Applus-RTD. Houston, TX (United States); Klein, Marvin; Ansari, Homayoon [Intelligent Optical Systems, Inc. Los Angeles, CA (United States); Kania Richard [TransCanada. Calgary, AB (Canada); Rapp, Steve [Spectra Energy, Houston, TX (United States)

    2010-07-01

    Despite various efforts, no reliable tools and techniques are available to enable an operator to quantify the impact of an SCC (Stress Corrosion Cracking) colony on the safety and integrity of a pipeline. Reliable non-destructive detection and measurement tools are not available either. There is therefore a large gap between current technology and the needs of the pipeline industry. Recent developments promise that with a concentrated effort, a comprehensive solution can be devised. This paper describes technical work performed to develop and validate both the inspection tool and the time of flight diffraction (TOFD) technique for sizing the depth of SCC. It also presents preliminary results of work on a closely related project that provides, on the basis of this technology, an integrated approach and tool for mapping, sizing, and evaluating SCC, through which significant cracks are filtered from more benign cracks within an SCC colony.

  17. Recognition and Analysis of Corrosion Failure Mechanisms

    Directory of Open Access Journals (Sweden)

    Steven Suess

    2006-02-01

    Full Text Available Corrosion has a vast impact on the global and domestic economy, and currently incurs losses of nearly $300 billion annually to the U.S. economy alone. Because of the huge impact of corrosion, it is imperative to have a systematic approach to recognizing and mitigating corrosion problems as soon as possible after they become apparent. A proper failure analysis includes collection of pertinent background data and service history, followed by visual inspection, photographic documentation, material evaluation, data review and conclusion procurement. In analyzing corrosion failures, one must recognize the wide range of common corrosion mechanisms. The features of any corrosion failure give strong clues as to the most likely cause of the corrosion. This article details a proven approach to properly determining the root cause of a failure, and includes pictographic illustrations of the most common corrosion mechanisms, including general corrosion, pitting, galvanic corrosion, dealloying, crevice corrosion, microbiologically-influenced corrosion (MIC, corrosion fatigue, stress corrosion cracking (SCC, intergranular corrosion, fretting, erosion corrosion and hydrogen damage.

  18. Concrete cover cracking with localized corrosion of reinforcing steel

    Energy Technology Data Exchange (ETDEWEB)

    Torres-Acosta, A. A.; Sagues, A. A. [South Florida Univ., Dept of Civil and Environmental Engineering, Tampa FL (United States)

    2000-07-01

    The critical amount of steel corrosion needed for concrete cover cracking of a reinforced concrete element was measured, focusing on cases where only a fraction of the steel bar length is corroding. The amount of corrosion needed to crack the concrete cover was found to range between 49 micrometre to 137 micrometre in specimens of localized corrosion. In contrast, in cases of uniform corrosion of comparable systems the corrosion needed to crack the concrete cover varied from 15 micrometre to 75 micrometer. Based on this and previous work on this problem, an empirical equation is proposed for the critical amount of steel corrosion as a function of specimen dimensions. The model proposed for estimating the critical amount of steel corrosion showed reasonable agreement between estimates of the work of corrosion expansion and the energy required to crack the concrete. 23 refs., 3 tabs., 8 figs.

  19. Corrosion-Fatigue Cracking in Al 7075 Alloys

    Science.gov (United States)

    2014-12-09

    Naval Research Laboratory Washington, DC 20375-5320 NRL/MR/6355--14-9582 Corrosion -Fatigue Cracking in Al 7075 Alloys December 9, 2014 P.S. Pao...PERSON 19b. TELEPHONE NUMBER (include area code) b. ABSTRACT c. THIS PAGE 18. NUMBER OF PAGES 17. LIMITATION OF ABSTRACT Corrosion -Fatigue Cracking in Al...Memorandum Report Corrosion -fatigue Aluminum alloys Environmental effect October 2011 – September 2014 63-2634-A4 Unclassified Unlimited Unclassified

  20. Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution

    Science.gov (United States)

    Yang, Yao; Cheng, Y. Frank

    2016-10-01

    In this work, the local corrosion at crack tip on an API 5L X46 pipeline steel specimens was investigated under various applied loads in a near-neutral pH solution. Electrochemical measurements, including potentiodynamic polarization and electrochemical impedance spectroscopy, combined with micro-electrochemical technique and surface characterization, were conducted to investigate the effect of stress on local anodic solution of the steel at the crack tip. The stress corrosion cracking of the steel was dominated by an anodic dissolution mechanism, while the effect of hydrogen was negligible. The applied load (stress) increased the corrosion rate at the crack tip, contributing to crack propagation. The deposit of corrosion products at the crack tip could protect somewhat from further corrosion. At sufficiently large applied loads such as 740 N in the work, it was possible to generate separated cathode and anode, further accelerating the crack growth.

  1. Effect of Stress on Corrosion at Crack Tip on Pipeline Steel in a Near-Neutral pH Solution

    Science.gov (United States)

    Yang, Yao; Cheng, Y. Frank

    2016-11-01

    In this work, the local corrosion at crack tip on an API 5L X46 pipeline steel specimens was investigated under various applied loads in a near-neutral pH solution. Electrochemical measurements, including potentiodynamic polarization and electrochemical impedance spectroscopy, combined with micro-electrochemical technique and surface characterization, were conducted to investigate the effect of stress on local anodic solution of the steel at the crack tip. The stress corrosion cracking of the steel was dominated by an anodic dissolution mechanism, while the effect of hydrogen was negligible. The applied load (stress) increased the corrosion rate at the crack tip, contributing to crack propagation. The deposit of corrosion products at the crack tip could protect somewhat from further corrosion. At sufficiently large applied loads such as 740 N in the work, it was possible to generate separated cathode and anode, further accelerating the crack growth.

  2. Hydrogen embrittlement and stress corrosion cracking in metals

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Cheong, Yong Mu; Im, Kyung Soo

    2004-10-15

    The objective of this report is to elucidate the mechanism for hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals. To this end, we investigate the common features between delayed hydride cracking (DHC) in zirconium alloys and HE in metals with no precipitation of hydrides including Fe base alloys, Nickel base alloys, Cu alloys and Al alloys. Surprisingly, as with the crack growth pattern for the DHC in zirconium alloy, the metals mentioned above show a discontinuous crack growth, striation lines and a strong dependence of yield strength when exposed to hydrogen internally and externally. This study, for the first time, analyzes the driving force for the HE in metals in viewpoints of Kim's DHC model that a driving force for the DHC in zirconium alloys is a supersaturated hydrogen concentration coming from a hysteresis of the terminal solid solubility of hydrogen, not by the stress gradient, As with the crack growing only along the hydride habit plane during the DHC in zirconium alloys, the metals exposed to hydrogen seem to have the crack growing by invoking the dislocation slip along the preferential planes as a result of some interactions of the dislocations with hydrogen. Therefore, it seems that the hydrogen plays a role in inducing the slip only on the preferential planes so as to cause a strain localization at the crack tip. Sulfur in metals is detrimental in causing a intergranular cracking due to a segregation of the hydrogens at the grain boundaries. In contrast, boron in excess of 500 ppm added to the Ni3Al intermetallic compound is found to be beneficial in suppressing the HE even though further details of the mechanism for the roles of boron and sulfur are required. Carbon, carbides precipitating semi-continuously along the grain boundaries and the CSL (coherent site lattice) boundaries is found to suppress the intergranular stress corrosion cracking (IGSCC) in Alloy 600. The higher the volume fraction of twin boundaries, the

  3. Hydrogen embrittlement and stress corrosion cracking in metals

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Cheong, Yong Mu; Im, Kyung Soo

    2004-10-15

    The objective of this report is to elucidate the mechanism for hydrogen embrittlement (HE) and stress corrosion cracking (SCC) in metals. To this end, we investigate the common features between delayed hydride cracking (DHC) in zirconium alloys and HE in metals with no precipitation of hydrides including Fe base alloys, Nickel base alloys, Cu alloys and Al alloys. Surprisingly, as with the crack growth pattern for the DHC in zirconium alloy, the metals mentioned above show a discontinuous crack growth, striation lines and a strong dependence of yield strength when exposed to hydrogen internally and externally. This study, for the first time, analyzes the driving force for the HE in metals in viewpoints of Kim's DHC model that a driving force for the DHC in zirconium alloys is a supersaturated hydrogen concentration coming from a hysteresis of the terminal solid solubility of hydrogen, not by the stress gradient, As with the crack growing only along the hydride habit plane during the DHC in zirconium alloys, the metals exposed to hydrogen seem to have the crack growing by invoking the dislocation slip along the preferential planes as a result of some interactions of the dislocations with hydrogen. Therefore, it seems that the hydrogen plays a role in inducing the slip only on the preferential planes so as to cause a strain localization at the crack tip. Sulfur in metals is detrimental in causing a intergranular cracking due to a segregation of the hydrogens at the grain boundaries. In contrast, boron in excess of 500 ppm added to the Ni3Al intermetallic compound is found to be beneficial in suppressing the HE even though further details of the mechanism for the roles of boron and sulfur are required. Carbon, carbides precipitating semi-continuously along the grain boundaries and the CSL (coherent site lattice) boundaries is found to suppress the intergranular stress corrosion cracking (IGSCC) in Alloy 600. The higher the volume fraction of twin boundaries, the

  4. Microbial Corrosion and Cracking in Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    1998-01-01

    and for recommendations in regards to electrochemical monitoring of MIC. The work presented here and further studies are also planned to lead to a Ph.D. thesis on "MIC monitoring based on mechanisms of corrosion".The results of laboratory experiments conducted in the period 1995 to 1997 are summarised. Conclusions...... will be based on results from the entire 3 year period, but only selected experimental data primarily from the latest experiments will be presented in detail here.Microbial corrosion of carbon steel under influence of sulphate-reducing bacteria (SRB) is characterised by the formation of both biofilm...... and corrosion products (ferrous sulphides) on the metal surface. Experiments have been conducted on carbon steel exposed in near neutral (pH 6 to 8.5) saline hydrogen sulphide environment (0 to 100 mg/l total dissolved sulphide) for a period of 14 days. Furthermore coupons have been exposed in a bioreactor...

  5. Effect of cold work on the growth rates of stress corrosion cracks in structural materials of nuclear systems

    Energy Technology Data Exchange (ETDEWEB)

    Magdowski, R.; Speidel, M.O. [Swiss Federal Inst. of Tech., Zurich (Switzerland). Inst. of Metallurgy

    1996-10-01

    The growth rates of stress corrosion cracks in austenitic stainless steels and nickel base alloy 600 exposed to simulated boiling water reactor coolant were measured by fracture mechanics testing techniques. Cold work may increase the crack growth rates up to one hundred times. In both, the annealed condition and the cold worked condition, the stress corrosion crack growth rates are independent of stress intensity over a wide K-range and crack growth rates correlate well with yield strength and hardness. In the annealed condition the fracture path is intergranular, but higher degrees of cold work introduce higher proportions of transgranular stress corrosion cracking.

  6. Preliminary study for extension and improvement on modeling of primary water stress corrosion cracking at control rod drive mechanism nozzles of pressurized water reactors

    Energy Technology Data Exchange (ETDEWEB)

    Aly, Omar F.; Mattar Neto, Miguel M. [Instituto de Pesquisas Energeticas e Nucleares (IPEN-CNEN/SP), Sao Paulo, SP (Brazil)], e-mail: ofaly@ipen.br, e-mail: mmattar@ipen.br; Schvartzman, Monica M.M.A.M. [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN), Belo Horizonte, MG (Brazil)], e-mail: monicas@cdtn.br

    2009-07-01

    This study is for to extend, to improve the existing models, and to propose a local approach to assess the primary water stress corrosion cracking in nickel-based components. It is includes a modeling of new data for Alloy 182 and new considerations about initiation and crack growth according a developing method based on EPRI-MRP-115 (2004), and USNRC NUREG/CR-6964 (2008). The experimental data is obtained from CDTN-Brazilian Nuclear Technology Development Center, by tests through slow strain rate test (SSRT) equipment. The model conception assumed is a built diagram which indicates a thermodynamic condition for the occurrence of corrosion submodes in essayed materials, through Pourbaix diagrams, for Nickel Alloys in high temperature primary water. Over them, are superimposed different models, including a semi-empiric-probabilistic one to quantify the primary water stress corrosion cracking susceptibility, and a crack growth model. These constructed models shall be validated with the experimental data. This development aims to extent some of the models obtained to weld metals like the Alloy 182, and to improve the originals obtained according methodologies exposed in above referred reports. These methodologies comprise laboratory testing procedures, data collecting, data screening, modeling procedures, assembling of data from some laboratories in the world, plotting of results, compared analysis and discussion of these results. Preliminary results for Alloy 182 will be presented. (author)

  7. Relationship among Parameters Evaluating Stress Corrosion Cracking

    Institute of Scientific and Technical Information of China (English)

    2000-01-01

    @@The threshold stress, σc, for sulfide stress corrosion cracking (SCC) of seven pipeline steels and five other steels, the critical stress, SC, for seven pipeline steels and two drill rod steels with various strengths and the susceptibility to SCC, IRA or σf(SCC)/σf, for four pipeline steels, two drill rod steels and five other steels were measured. The results showed that there are no definite elationships among σc, SC and IRA or σf(SCC)/σf. The threshold stress for hydrogen induced cracking (HIC) during charging with loading in the H2SO4 solution, σc(H), decreased linearly with logarithm of the concentration of diffusible hydrogen c0, i.e., σC(H)=A-B Inc0 for four pipeline steels. σc(H) obtained with a special cathodic current ic, which was corresponding to the diffusible hydrogen concentration during immersing in the H2S solution, were consistent with σc for sulfide SCC for four pipeline steels.Therefore, σc for sulfide SCC can be measured using dynamically charging in the H2SO4 solution with the special cathodic current ic.

  8. Evaluation of Stress Corrosion Cracking Susceptibility Using Fracture Mechanics Techniques, Part 1. [environmental tests of aluminum alloys, stainless steels, and titanium alloys

    Science.gov (United States)

    Sprowls, D. O.; Shumaker, M. B.; Walsh, J. D.; Coursen, J. W.

    1973-01-01

    Stress corrosion cracking (SSC) tests were performed on 13 aluminum alloys, 13 precipitation hardening stainless steels, and two titanium 6Al-4V alloy forgings to compare fracture mechanics techniques with the conventional smooth specimen procedures. Commercially fabricated plate and rolled or forged bars 2 to 2.5-in. thick were tested. Exposures were conducted outdoors in a seacoast atmosphere and in an inland industrial atmosphere to relate the accelerated tests with service type environments. With the fracture mechanics technique tests were made chiefly on bolt loaded fatigue precracked compact tension specimens of the type used for plane-strain fracture toughness tests. Additional tests of the aluminum alloy were performed on ring loaded compact tension specimens and on bolt loaded double cantilever beams. For the smooth specimen procedure 0.125-in. dia. tensile specimens were loaded axially in constant deformation type frames. For both aluminum and steel alloys comparative SCC growth rates obtained from tests of precracked specimens provide an additional useful characterization of the SCC behavior of an alloy.

  9. Corrosion-Induced Concrete Cracking Model Considering Corrosion-Filled Paste

    OpenAIRE

    Dong, Jianfeng; Zhao, Yuxi; Wu, Yingyao; Jin, Weiliang

    2016-01-01

    A TCP–TCL model is established to describe the relationship between the thickness of the corrosion-filled paste (CP) and that of the corrosion layer (CL). This model can describe the phenomenon that the corrosion filling in the concrete pores and accumulating at the steel/concrete interface occur synchronously. Based on the TCP–TCL model, a corrosion-induced concrete cracking model, which can quantitatively consider corrosion-filled paste at concrete/steel interface, is proposed. Combined wit...

  10. Stress corrosion cracking of AISI 321 stainless steel in acidic chloride solution

    Indian Academy of Sciences (India)

    Yanliang Huang

    2002-02-01

    The stress corrosion cracking (SCC) of AISI 321 stainless steel in acidic chloride solution was studied by slow strain rate (SSR) technique and fracture mechanics method. The fractured surface was characterized by cleavage fracture. In order to clarify the SCC mechanism, the effects of inhibitor KI on SCC behaviour were also included in this paper. A study showed that the inhibition effects of KI on SCC were mainly attributed to the anodic reaction of the corrosion process. The results of strain distribution in front of the crack tip of the fatigue pre-cracked plate specimens in air, in the blank solution (acidic chloride solution without inhibitor KI) and in the solution added with KI measured by speckle interferometry (SPI) support the unified mechanism of SCC and corrosion fatigue cracking (CFC).

  11. Some important considerations in the development of stress corrosion cracking test methods.

    Science.gov (United States)

    Wei, R. P.; Novak, S. R.; Williams, D. P.

    1972-01-01

    Discussion of some of the precaution needs the development of fracture-mechanics based test methods for studying stress corrosion cracking involves. Following a review of pertinent analytical fracture mechanics considerations and of basic test methods, the implications for test corrosion cracking studies of the time-to-failure determining kinetics of crack growth and life are examined. It is shown that the basic assumption of the linear-elastic fracture mechanics analyses must be clearly recognized and satisfied in experimentation and that the effects of incubation and nonsteady-state crack growth must also be properly taken into account in determining the crack growth kinetics, if valid data are to be obtained from fracture-mechanics based test methods.

  12. Failure analysis of corrosion cracking and simulated testing for a fluid catalytic cracking unit

    Institute of Scientific and Technical Information of China (English)

    Hua Chen; Xiaogang Li; Chaofang Dong; Ming Li; Jinwen Yang

    2005-01-01

    The failure of a fluid catalysis and cracking unit (FCCU) in a Chinese refinery was investigated by using nondestructive detection methods, fracture surface examination, hardness measurement, chemical composition and corrosion products analysis. The results showed that the failure was caused by the dew point nitrate stress corrosion cracking. For a long operation period, the wall temperature of the regenerator in the FCCU was below the fume dew point. As a result, an acid fume NOx-SOx-H2O medium presented on the surface, resulting in stress corrosion cracking of the component with high residual stress. In order to confirm the relative conclusion, simulated testing was conducted in laboratory, and the results showed similar cracking characteristics. Finally, some suggestions have been made to prevent the stress corrosion cracking of an FCCU from re-occurring in the future.

  13. The corrosion and corrosion mechanical properties evaluation for the LBB concept in VVERs

    Energy Technology Data Exchange (ETDEWEB)

    Ruscak, M.; Chvatal, P.; Karnik, D.

    1997-04-01

    One of the conditions required for Leak Before Break application is the verification that the influence of corrosion environment on the material of the component can be neglected. Both the general corrosion and/or the initiation and, growth of corrosion-mechanical cracks must not cause the degradation. The primary piping in the VVER nuclear power plant is made from austenitic steels (VVER 440) and low alloy steels protected with the austenitic cladding (VVER 1000). Inspection of the base metal and heterogeneous weldments from the VVER 440 showed that the crack growth rates are below 10 m/s if a low oxygen level is kept in the primary environment. No intergranular cracking was observed in low and high oxygen water after any type of testing, with constant or periodic loading. In the framework of the LBB assessment of the VVER 1000, the corrosion and corrosion mechanical properties were also evaluated. The corrosion and corrosion mechanical testing was oriented predominantly to three types of tests: stress corrosion cracking tests corrosion fatigue tests evaluation of the resistance against corrosion damage. In this paper, the methods used for these tests are described and the materials are compared from the point of view of response on static and periodic mechanical stress on the low alloyed steel 10GN2WA and weld metal exposed in the primary circuit environment. The slow strain rate tests and static loading of both C-rings and CT specimens were performed in order to assess the stress corrosion cracking characteristics. Cyclic loading of CT specimens was done to evaluate the kinetics of the crack growth under periodical loading. Results are shown to illustrate the approaches used. The data obtained were evaluated also from the point of view of comparison of the influence of different structure on the stress corrosion cracking appearance. The results obtained for the base metal and weld metal of the piping are presented here.

  14. Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water

    Science.gov (United States)

    Moss, Tyler; Was, Gary S.

    2017-04-01

    The objective of this study is to determine whether stress corrosion crack initiation of Alloys 600 and 690 occurs by the same mechanism in subcritical and supercritical water. Tensile bars of Alloys 690 and 600 were strained in constant extension rate tensile experiments in hydrogenated subcritical and supercritical water from 593 K to 723 K (320 °C to 450 °C), and the crack initiation behavior was characterized by high-resolution electron microscopy. Intergranular cracking was observed across the entire temperature range, and the morphology, structure, composition, and temperature dependence of initiated cracks in Alloy 690 were consistent between hydrogenated subcritical and supercritical water. Crack initiation of Alloy 600 followed an Arrhenius relationship and did not exhibit a discontinuity or change in slope after crossing the critical temperature. The measured activation energy was 121 ± 13 kJ/mol. Stress corrosion crack initiation in Alloy 690 was fit with a single activation energy of 92 ± 12 kJ/mol across the entire temperature range. Cracks were observed to propagate along grain boundaries adjacent to chromium-depleted metal, with Cr2O3 observed ahead of crack tips. All measures of the SCC behavior indicate that the mechanism for stress corrosion crack initiation of Alloy 600 and Alloy 690 is consistent between hydrogenated subcritical and supercritical water.

  15. Accelerated Stress Corrosion Crack Initiation of Alloys 600 and 690 in Hydrogenated Supercritical Water

    Science.gov (United States)

    Moss, Tyler; Was, Gary S.

    2017-01-01

    The objective of this study is to determine whether stress corrosion crack initiation of Alloys 600 and 690 occurs by the same mechanism in subcritical and supercritical water. Tensile bars of Alloys 690 and 600 were strained in constant extension rate tensile experiments in hydrogenated subcritical and supercritical water from 593 K to 723 K (320 °C to 450 °C), and the crack initiation behavior was characterized by high-resolution electron microscopy. Intergranular cracking was observed across the entire temperature range, and the morphology, structure, composition, and temperature dependence of initiated cracks in Alloy 690 were consistent between hydrogenated subcritical and supercritical water. Crack initiation of Alloy 600 followed an Arrhenius relationship and did not exhibit a discontinuity or change in slope after crossing the critical temperature. The measured activation energy was 121 ± 13 kJ/mol. Stress corrosion crack initiation in Alloy 690 was fit with a single activation energy of 92 ± 12 kJ/mol across the entire temperature range. Cracks were observed to propagate along grain boundaries adjacent to chromium-depleted metal, with Cr2O3 observed ahead of crack tips. All measures of the SCC behavior indicate that the mechanism for stress corrosion crack initiation of Alloy 600 and Alloy 690 is consistent between hydrogenated subcritical and supercritical water.

  16. Stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Statler, G. R.; Spretnak, J. W.; Beck, F. H.; Fontana, M. G.

    1974-01-01

    The effect of hydrogen on the properties of metals, including titanium and its alloys, was investigated. The basic theories of stress corrosion of titanium alloys are reviewed along with the literature concerned with the effect of absorbed hydrogen on the mechanical properties of metals. Finally, the basic modes of metal fracture and their importance to this study is considered. The experimental work was designed to determine the effects of hydrogen concentration on the critical strain at which plastic instability along pure shear directions occurs. The materials used were titanium alloys Ti-8Al-lMo-lV and Ti-5Al-2.5Sn.

  17. Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600

    Science.gov (United States)

    Panter, J.; Viguier, B.; Cloué, J.-M.; Foucault, M.; Combrade, P.; Andrieu, E.

    2006-01-01

    In the present study alloy 600 was tested in simulated pressurised water reactor (PWR) primary water, at 360 °C, under an hydrogen partial pressure of 30 kPa. These testing conditions correspond to the maximum sensitivity of alloy 600 to crack initiation. The resulting oxidised structures (corrosion scale and underlying metal) were characterised. A chromium rich oxide layer was revealed, the underlying metal being chromium depleted. In addition, analysis of the chemical composition of the metal close to the oxide scale had allowed to detect oxygen under the oxide scale and particularly in a triple grain boundary. Implication of such a finding on the crack initiation of alloy 600 is discussed. Significant diminution of the crack initiation time was observed for sample oxidised before stress corrosion tests. In view of these results, a mechanism for stress corrosion crack initiation of alloy 600 in PWR primary water was proposed.

  18. A STUDY OF CORROSION AND STRESS CORROSION CRACKING OF CARBON STEEL NUCLEAR WASTE STORAGE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER, K.D.

    2007-08-21

    The Hanford reservation Tank Farms in Washington State has 177 underground storage tanks that contain approximately 50 million gallons of liquid legacy radioactive waste from cold war plutonium production. These tanks will continue to store waste until it is treated and disposed. These nuclear wastes were converted to highly alkaline pH wastes to protect the carbon steel storage tanks from corrosion. However, the carbon steel is still susceptible to localized corrosion and stress corrosion cracking. The waste chemistry varies from tank to tank, and contains various combinations of hydroxide, nitrate, nitrite, chloride, carbonate, aluminate and other species. The effect of each of these species and any synergistic effects on localized corrosion and stress corrosion cracking of carbon steel have been investigated with electrochemical polarization, slow strain rate, and crack growth rate testing. The effect of solution chemistry, pH, temperature and applied potential are all considered and their role in the corrosion behavior will be discussed.

  19. Assessment of copper resistance to stress-corrosion cracking in nitrite solutions by means of joint analysis of acoustic emission measurements, deformation diagrams, qualitative and quantitative fractography, and non-linear fracture mechanics

    Energy Technology Data Exchange (ETDEWEB)

    Khanzhin, V.G.; Nikulin, S.A. [Moscow State Inst. of Steel and Alloys (Russian Federation)

    2005-06-01

    A study of stress-corrosion cracking (SCC) of copper in 0.1M NaNO{sub 2} aqueous solution is presented. The fracture kinetics was monitored by measuring the acoustic emission (AE) signals. Macro- and micro-fractography analysis, using scanning electron microscopy (SEM), was employed to investigate the fracture mechanisms. Estimates of stress intensity factor, KI, and J-integral were derived in order to assess the resistance of copper to stress corrosion cracking. Two kinds of SCC tests under continuous circulation of the corrosive solution were employed in the present study: 1. Constant extension rate (2x10{sup -6}/s) tests on pre-cracked, middle tension (MT) panel specimens. 2. Tests on pre-cracked, compact tension (CT) specimens at a fixed (by a fixing bolt) opening of the crack walls ({delta} = 0.3 mm, K{sub i} = 27 MPax{radical}m). The time base for these tests was about two months. After the completion of the SCC test, the CT specimen was additionally tested, under a constant-rate (0.02 mm/s) off-center extension. In the both kinds of tests, the SCC fracture kinetics is found to exhibit two typical stages: Stage 1: SCC initiation stage (after a certain incubation period, T{sub i}, measured to be T{sub i} {approx_equal} 3-4 hours for MT specimens under constant extension, the corresponding stress was {sigma} {approx_equal} 40-70 MPa, and T{sub i} {approx_equal} 200 hours for CT specimens under a fixed crack wall opening). Stage 2: Active fracture process (SCC macro-fracture) distinguished by strong AE pulses (which are registered after time T{sub 2} {approx_equal} 8 hours for MT specimens and T{sub 2} {approx_equal} 800 hours for CT specimens). Fractography analysis has shown that the zone of SCC fracture in MT specimens extends to approximately 1,500 {mu}m. A 400-700 {mu}m deep zone of brittle transgranular fracture, which included small areas showing characteristic SCC 'striations', was observed adjacent to the fatigue pre-crack area. At higher

  20. Mitigation of stress corrosion cracking in pressurized water reactor (PWR) piping systems using the mechanical stress improvement process (MSIP{sup R)} or underwater laser beam welding

    Energy Technology Data Exchange (ETDEWEB)

    Rick, Grendys; Marc, Piccolino; Cunthia, Pezze [Westinghouse Electric Company, LLC, New York (United States); Badlani, Manu [Nu Vision Engineering, New York (United States)

    2009-04-15

    A current issue facing pressurized water reactors (PWRs) is primary water stress corrosion cracking (PWSCC) of bi metallic welds. PWSCC in a PWR requires the presence of a susceptible material, an aggressive environment and a tensile stress of significant magnitude. Reducing the potential for SCC can be accomplished by eliminating any of these three elements. In the U.S., mitigation of susceptible material in the pressurizer nozzle locations has largely been completed via the structural weld overlay (SWOL) process or NuVision Engineering's Mechanical Stress Improvement Process (MSIP{sup R)}, depending on inspectability. The next most susceptible locations in Westinghouse designed power plants are the Reactor Vessel (RV) hot leg nozzle welds. However, a full SWOL Process for RV nozzles is time consuming and has a high likelihood of in process weld repairs. Therefore, Westinghouse provides two distinctive methods to mitigate susceptible material for the RV nozzle locations depending on nozzle access and utility preference. These methods are the MSIP and the Underwater Laser Beam Welding (ULBW) process. MSIP applies a load to the outside diameter of the pipe adjacent to the weld, imposing plastic strains during compression that are not reversed after unloading, thus eliminating the tensile stress component of SCC. Recently, Westinghouse and NuVision successfully applied MSIP on all eight RV nozzles at the Salem Unit 1 power plant. Another option to mitigate SCC in RV nozzles is to place a barrier between the susceptible material and the aggressive environment. The ULBW process applies a weld inlay onto the inside pipe diameter. The deposited weld metal (Alloy 52M) is resistant to PWSCC and acts as a barrier to prevent primary water from contacting the susceptible material. This paper provides information on the approval and acceptance bases for MSIP, its recent application on RV nozzles and an update on ULBW development.

  1. Stress corrosion cracking resistance of aluminum alloy 7000 series after two-step aging

    Directory of Open Access Journals (Sweden)

    Jegdić Bore V.

    2015-01-01

    Full Text Available The effect of one step-and a new (short two-step aging on the resistance to stress corrosion cracking of an aluminum alloy 7000 series was investigated, using slow strain rate test and fracture mechanics method. Aging level in the tested alloy was evaluated by means of scanning electron microscopy and measurements of electrical resistivity. It was shown that the alloy after the new two-step aging is significantly more resistant to stress corrosion cracking. Values of tensile properties and fracture toughness are similar for both thermal states. Processes that take place at the crack tip have been considered. The effect of the testing solution temperature on the crack growth rate on the plateau was determined. Two values of the apparent activation energy were obtained. These values correspond to different processes that control crack growth rate on the plateau at higher and lower temperatures. [Projekat Ministarstva nauke Republike Srbije, br. TR 34028 i br. TR 34016

  2. Computer Simulation of Intergranular Stress Corrosion Cracking via Hydrogen Embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Smith, R.W.

    2000-04-01

    Computer simulation has been applied to the investigation of intergranular stress corrosion cracking in Ni-based alloys based on a hydrogen embrittlement mechanism. The simulation employs computational modules that address (a) transport and reactions of aqueous species giving rise to hydrogen generation at the liquid-metal interface, (b) solid state transport of hydrogen via intergranular and transgranular diffusion pathways, and (c) fracture due to the embrittlement of metallic bonds by hydrogen. A key focus of the computational model development has been the role of materials microstructure (precipitate particles and grain boundaries) on hydrogen transport and embrittlement. Simulation results reveal that intergranular fracture is enhanced as grain boundaries are weakened and that microstructures with grains elongated perpendicular to the stress axis are more susceptible to cracking. The presence of intergranular precipitates may be expected to either enhance or impede cracking depending on the relative distribution of hydrogen between the grain boundaries and the precipitate-matrix interfaces. Calculations of hydrogen outgassing and in gassing demonstrate a strong effect of charging method on the fracture behavior.

  3. Investigations of the corrosion fatigue behaviour at a super pure martensitic stainless steel X5CrNiCuNb 17 4 PH in comparison to the soft martensitic stainless steel X4CrNiMo 16 5 1 ESR in chloride containing aqueous media. Pt. 2. Corrosion fatigue tests and crack initiation mechanisms

    Energy Technology Data Exchange (ETDEWEB)

    Schmitt-Thomas, K.G.; Happle, T.; Wunderlich, R.

    1989-07-01

    The following report concerns the study of the corrosion fatigue behaviour of the soft martensitic steel X4CrNiMo 16 5 1 ESR and the precipitation hardened X5CrNiCuNb 17 4 PH in sodium solution in the temperature range between 20/sup 0/ and 150/sup 0/C and the determination of their general corrosion properties and the mechanism of crack propagation. Their corrosion fatigue limits were compared with each other. A comparison was also made between an electro-slag-remelted soft martensitic steel and a charge without an ESR aftertreatment. Microfractographical fracture and crack path investigation were carried out for interpretation of the experimental results. It was observed that in both super pure steels (soft martensitic and precipitation hardened) the oxidic inclusions are not responsible for the crack initiation, as it was found in the non ESR treated steels. In the 17-4 PH steel copper containing inclusions in the crack initiation areas were observed. In concentrated sodium solution pitting corrosion was found at both steels. (orig.).

  4. Concrete cover cracking due to uniform reinforcement corrosion

    DEFF Research Database (Denmark)

    Solgaard, Anders Ole Stubbe; Michel, Alexander; Geiker, Mette Rica;

    2013-01-01

    is calculated using literature data on corrosion rate and Faraday’s law. The parameters varied comprise reinforcement diameter, concrete cover thickness and concrete material properties, viz. concrete tensile strength and ductility (plain concrete and fibre reinforced concrete). Results obtained from......Service life design (SLD) is an important tool for civil engineers to ensure that the structural integrity and functionality of the structure is not compromised within a given time frame, i.e. the service life. In SLD of reinforced concrete structures, reinforcement corrosion is of major concern...... and reinforcement de-passivation is a frequently used limit state. The present paper investigates an alternative limit state: corrosion-induced cover cracking. Results from numerical simulations of concrete cover cracking due to reinforcement corrosion are presented. The potential additional service life...

  5. Behavior of Stress Corrosion Cracking in a Magnesium Alloy

    Institute of Scientific and Technical Information of China (English)

    SONG Renguo; YANG Fanger; BLAWERT Carsten; DIETZEL Wolfgang

    2009-01-01

    Slow strain rate testing (SSRT) was employed to study the stress corrosion cracking (SCC) behavior of ZE41 magnesium alloy in 0.01 M NaCl solution. Smooth tensile specimens with different thicknesses were strained dynamically in both longitudinal and transverse direction under permanent immersions at a strain rate of 10-6 s-1. It is found that ZE41 magnesium alloy is susceptible to SCC in 0.01 M NaCl solution. The SCC susceptibility of the thinner specimen is lower than that of the thicker specimen. Also, the longitudinal specimens are slightly more susceptible to SCC than the transverse specimens. The SCC mechanism of magnesium alloy is attributed to the combination of anodic dissolution with hydrogen embrittlement.

  6. A non-destructive test method to monitor corrosion products and corrosion-induced cracking in reinforced cement based materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Peterova, Adela;

    2011-01-01

    ) was conducted to describe the impact of water-to-cement ratio and corrosion current density (i.e., corrosion rate) on the reinforcement corrosion process. Focus was placed, in particular on the determination of the corrosion accommodating region (CAR) and time to corrosion-induced cracking. Experimental results...

  7. The design of an instrumented rebar for assessment of corrosion in cracked reinforced concrete

    DEFF Research Database (Denmark)

    Pease, Bradley Justin; Geiker, Mette Rica; Stang, Henrik;

    2011-01-01

    An instrumented rebar is presented which was designed to have a realistic mechanical performance and to provide location dependent measurements to assess the environment with regards to reinforcement corrosion. The instrumented rebar was constructed from a hollowed 10 mm nominal diameter standard...... between the steel and concrete. Cracked beams with cast-in instrumented and standard rebars were ponded with a 10\\% chloride solution and the open circuit corrosion potential (OCP) of the 17 sensors was measured for up to 62 days. Measurements from the individual sensors indicate when and where active...... rebar with 17 electronically isolated corrosion sensors. Instrumented and standard rebars were cast into concrete beams and bending cracks were induced and held open using steel frames. Epoxy impregnation was used to assess and compare cracks in the concrete around the instrumented and standard rebar...

  8. De-alloying and stress-corrosion cracking. Final report

    Energy Technology Data Exchange (ETDEWEB)

    Sieradzki, K.

    1998-09-01

    This research program has had two major areas of focus that are related: (1) alloy corrosion and (2) the role of selective dissolution in the stress corrosion cracking of alloy systems. These interrelated issues were examined using model systems such as Ag-Au and Cu-Au by conventional electrochemical techniques, in situ scanning tunneling microscopy (STM), in situ small angle neutron scattering (SANS), ultrahigh speed digital photography of fracture events, and computer simulations. The STM and SANS work were specifically aimed at addressing a roughening transition known to occur in alloy systems undergoing corrosion at electrochemical potentials greater than the so-called critical potential. Analytical models of de-alloying processes including the roughening transition were developed that specifically include curvature effects that are important in alloy corrosion processes. Stress-corrosion experiments were performed on the same model systems using rapid optical and electrochemical techniques on 50 {micro}m--250 {micro}m thick sheets and small diameter wires. The primary goal of this work was to develop a fundamental understanding of the corrosion and electrochemistry of alloys and the stress-corrosion cracking processes these alloys undergo. Computer simulations and analytical work identified surface stress and an important parameter in environmentally assisted fracture. The major results of the research on this program since the summer of 1993 are briefly summarized.

  9. Chemical milling solution reveals stress corrosion cracks in titanium alloy

    Science.gov (United States)

    Braski, D. N.

    1967-01-01

    Solution of hydrogen flouride, hydrogen peroxide, and water reveals hot salt stress corrosion cracks in various titanium alloys. After the surface is rinsed in water, dried, and swabbed with the solution, it can be observed by the naked eye or at low magnification.

  10. Smeared crack modelling approach for corrosion-induced concrete damage

    DEFF Research Database (Denmark)

    Thybo, Anna Emilie Anusha; Michel, Alexander; Stang, Henrik

    2017-01-01

    compared to experimental data obtained by digital image correlation and published in the literature. Excellent agreements between experimentally observed and numerically predicted crack patterns at the micro and macro scale indicate the capability of the modelling approach to accurately capture corrosion...

  11. Effect of hydrogen on stress corrosion cracking of copper

    Institute of Scientific and Technical Information of China (English)

    Li-jie QIAO

    2008-01-01

    The effects of hydrogen on electrochemical behavior and susceptibility of stress corrosion cracking (SCC) of pure copper were studied. SCC susceptibility of pure copper in a 1 M NaNO2 solution was increased by pre-charged hydrogen. The effect of hydrogen on the sus-ceptibility is more obvious in the low stress region due to the longer fracture time, which resulted in a longer time for more hydrogen to diffuse toward the crack tip. Synergistic effects of hydrogen and stress on corrosion and SCC pro-cesses were discussed. The results showed that an inter-action between stress and hydrogen at the crack tip could increase the anodic dissolution rate remarkably.

  12. Inhibiting Corrosion Cracking: Crack Tip Chemistry and Physics.

    Science.gov (United States)

    1986-03-14

    5 5. Swuzary 113 Rferences 114 wl NO 4L iv . List of Figuring 1. Microipette pulling machine . 29 2. Anodic polarization of 7075-T6 Al alloy in dilute...environment has a strong effect on microplastic behavior at the tip of a fatigue crack. Stolz and Pelloux suggest that nitrate ion competes with chloride...Crystalline Na2 N 20 29H20 precipitates when the filtrate is placed in a vacunm desiccator over sulfuric acid. The filtered precipitate is washed

  13. Stress Corrosion Cracking and Fatigue Crack Growth Studies Pertinent to Spacecraft and Booster Pressure Vessels

    Science.gov (United States)

    Hall, L. R.; Finger, R. W.

    1972-01-01

    This experimental program was divided into two parts. The first part evaluated stress corrosion cracking in 2219-T87 aluminum and 5Al-2.5Sn (ELI) titanium alloy plate and weld metal. Both uniform height double cantilever beam and surface flawed specimens were tested in environments normally encountered during the fabrication and operation of pressure vessels in spacecraft and booster systems. The second part studied compatibility of material-environment combinations suitable for high energy upper stage propulsion systems. Surface flawed specimens having thicknesses representative of minimum gage fuel and oxidizer tanks were tested. Titanium alloys 5Al-2.5Sn (ELI), 6Al-4V annealed, and 6Al-4V STA were tested in both liquid and gaseous methane. Aluminum alloy 2219 in the T87 and T6E46 condition was tested in fluorine, a fluorine-oxygen mixture, and methane. Results were evaluated using modified linear elastic fracture mechanics parameters.

  14. Stress Corrosion Crack Growth Behavior of Titanium Alloy/Bioactive Glasses Sandwiches in Simulated Human Physiological Environment

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    Based on a series of newly developed bioactive glasses having suitable thermo-mechanical properties to allow application as fixation agents between bone and titanium alloy biomedical implants, the stress corrosion crack growth(SCCG) behavior of their interfaces with Ti6Al4V was investigated in simulated body fluid (SBF) with the objectiveof discerning the salient mechanisms of crack advance and to assess the reliability of the bonds. Results indicatedthat crack growth rates in Ti6Al4V/glass/Ti6Al4V sandwich specimens were nearly the same as or slightly lowerthan those in the bulk glasses at comparable stress intensities; indeed, cracks would prefer to propagate off theinterface, suggesting that the Ti6Al4V/glass interface has relatively good crack-growth resistance. Mechanistically,interfacial crack growth appears to be controlled by the classic stress corrosion mechanisms for silicate glasses, withno discernible effect of bioactivity on the SCCG behavior being observed.

  15. Cracking process of Fe-26Cr-1Mo during low cycle corrosion fatigue

    Energy Technology Data Exchange (ETDEWEB)

    Wang, J.Q.; Li, J.; Wang, Z.F.; Zhu, Z.Y.; Ke, W. (Academia Sinica, Shenyang (China). Corrosion Science Lab.); Zang, Q.S.; Wang, Z.G. (Academia Sinica, Shenyang (China). State Key Lab. for Fatigue and Fracture of Materials)

    1994-12-01

    The corrosion fatigue (CF) life has been divided classically into the initiation'' and propagation'' periods. Usually, the crack initiation process dominates the component lifetime under the low cycle CF condition because the crack propagates rapidly one initiated. Despite much work done on the research of the CF crack initiation mechanisms, however, a full understanding of crack initiation is still lacking. There are some limitations in explaining the CF crack initiation in an aqueous solution using the above four mechanisms individually. And, it is difficult to conduct experiments in which one mechanism along can be examined. Although CF is complicated, it is possible to reproduce a specific experiment condition which will have the dominant factor affecting the CF crack initiation. Once the cracks initiate on the smooth metal surface, their coalescence, micropropagation and macropropagation will take place successively. The initiated cracks propagate first in the range of several grains, and the behavior of the microcrack propagation is different from that of macrocrack propagation. For Fe-26Cr-1Mo ferritic stainless steel, the fundamental research work of straining electrode has been done by many investigators, but the observation of the material surface at different deformation processes has not been reported. In the present study, the detailed observation of the cracking process of the material has been carried out in low cycle CF.

  16. Stress Corrosion Cracking Behavior of X80 Pipeline Steel in Acid Soil Environment with SRB

    Science.gov (United States)

    Wang, Dan; Xie, Fei; Wu, Ming; Liu, Guangxin; Zong, Yue; Li, Xue

    2017-06-01

    Self-designed experimental device was adopted to ensure the normal growth of sulphate-reducing bacteria (SRB) in sterile simulated Yingtan soil solution. Stress corrosion cracking (SCC) behavior of X80 pipeline steel in simulated acid soil environment was investigated by electrochemical impedance spectroscopy, slow strain rate test, and scanning electron microscope. Results show that the presence of SRB could promote stress corrosion cracking susceptibility. In a growth cycle, polarization resistance first presents a decrease and subsequently an increase, which is inversely proportional to the quantities of SRB. At 8 days of growth, SRB reach their largest quantity of 1.42 × 103 cells/g. The corrosion behavior is most serious at this time point, and the SCC mechanism is hydrogen embrittlement. In other SRB growth stages, the SCC mechanism of X80 steel is anodic dissolution. With the increasing SRB quantities, X80 steel is largely prone to SCC behavior, and the effect of hydrogen is considerably obvious.

  17. Modeling of concrete cracking due to corrosion process of reinforcement bars

    Energy Technology Data Exchange (ETDEWEB)

    Bossio, Antonio, E-mail: antonio.bossio@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Monetta, Tullio, E-mail: monetta@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Bellucci, Francesco, E-mail: bellucci@unina.it [Department of Chemical Engineering, Materials and Production, University of Naples “Federico II”, Napoli, Piazzale V. Tecchio 80, I-80125 Italy (Italy); Lignola, Gian Piero, E-mail: glignola@unina.it [Department of Structures for Engineering and Architecture, University of Naples “Federico II”, Via Claudio 21, I-80125 Napoli (Italy); Prota, Andrea, E-mail: aprota@unina.it [Department of Structures for Engineering and Architecture, University of Naples “Federico II”, Via Claudio 21, I-80125 Napoli (Italy)

    2015-05-15

    The reinforcement corrosion in Reinforced Concrete (RC) is a major reason of degradation for structures and infrastructures throughout the world leading to their premature deterioration before design life was attained. The effects of corrosion of reinforcement are: (i) the reduction of the cross section of the bars, and (ii) the development of corrosion products leading to the appearance of cracks in the concrete cover and subsequent cover spalling. Due to their intrinsic complex nature, these issues require an interdisciplinary approach involving both material science and structural design knowledge also in terms on International and National codes that implemented the concept of durability and service life of structures. In this paper preliminary FEM analyses were performed in order to simulate pitting corrosion or general corrosion aimed to demonstrate the possibility to extend the results obtained for a cylindrical specimen, reinforced by a single bar, to more complex RC members in terms of geometry and reinforcement. Furthermore, a mechanical analytical model to evaluate the stresses in the concrete surrounding the reinforcement bars is proposed. In addition, a sophisticated model is presented to evaluate the non-linear development of stresses inside concrete and crack propagation when reinforcement bars start to corrode. The relationships between the cracking development (mechanical) and the reduction of the steel section (electrochemical) are provided. Finally, numerical findings reported in this paper were compared to experimental results available in the literature and satisfactory agreement was found.

  18. Microbial Corrosion and Cracking in Steel

    DEFF Research Database (Denmark)

    Hilbert, Lisbeth Rischel

    1998-01-01

    and corrosion products (ferrous sulphides) on the metal surface. Experiments have been conducted on carbon steel exposed in near neutral (pH 6 to 8.5) saline hydrogen sulphide environment (0 to 100 mg/l total dissolved sulphide) for a period of 14 days. Furthermore coupons have been exposed in a bioreactor...... for a period of up to 120 days in sulphide-producing environment controlled by biological activity of (SRB).Electrochemical studies have been conducted in order to characterise the electrochemical response of the biofilm / ferrous sulphide / metal interface and clarify whether the tested electrochemical...... and not electrochemically active film. The polarisation resistance increases with the film resistance and an small underestimation of corrosion rate is possible, if film resistance is large.· An electrochemically reactive film (ferrous sulphides) results in current contributions that will be added to the metal dissolution...

  19. Irradiation-Assisted Stress Corrosion Cracking of Austenitic Stainless Steels in BWR Environments

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Y. [Argonne National Lab. (ANL), Argonne, IL (United States); Chopra, O. K. [Argonne National Lab. (ANL), Argonne, IL (United States); Gruber, Eugene E. [Argonne National Lab. (ANL), Argonne, IL (United States); Shack, William J. [Argonne National Lab. (ANL), Argonne, IL (United States)

    2010-06-01

    The internal components of light water reactors are exposed to high-energy neutron irradiation and high-temperature reactor coolant. The exposure to neutron irradiation increases the susceptibility of austenitic stainless steels (SSs) to stress corrosion cracking (SCC) because of the elevated corrosion potential of the reactor coolant and the introduction of new embrittlement mechanisms through radiation damage. Various nonsensitized SSs and nickel alloys have been found to be prone to intergranular cracking after extended neutron exposure. Such cracks have been seen in a number of internal components in boiling water reactors (BWRs). The elevated susceptibility to SCC in irradiated materials, commonly referred to as irradiation-assisted stress corrosion cracking (IASCC), is a complex phenomenon that involves simultaneous actions of irradiation, stress, and corrosion. In recent years, as nuclear power plants have aged and irradiation dose increased, IASCC has become an increasingly important issue. Post-irradiation crack growth rate and fracture toughness tests have been performed to provide data and technical support for the NRC to address various issues related to aging degradation of reactor-core internal structures and components. This report summarizes the results of the last group of tests on compact tension specimens from the Halden-II irradiation. The IASCC susceptibility of austenitic SSs and heat-affected-zone (HAZ) materials sectioned from submerged arc and shielded metal arc welds was evaluated by conducting crack growth rate and fracture toughness tests in a simulated BWR environment. The fracture and cracking behavior of HAZ materials, thermally sensitized SSs and grain-boundary engineered SSs was investigated at several doses (≤3 dpa). These latest results were combined with previous results from Halden-I and II irradiations to analyze the effects of neutron dose, water chemistry, alloy compositions, and welding and processing conditions on IASCC

  20. Detection of corrosion processes and fatigue cracks by means of acoustic emission monitoring

    Energy Technology Data Exchange (ETDEWEB)

    Jagenbrein, Andreas; Tscheliesnig, Peter [TUEV Austria Services GmbH, Vienna (Austria); Wachsmuth, Janne; Bohse, Juergen [Bundesanstalt fuer Materialforschung und -pruefung (BAM), Berlin (Germany)

    2012-07-01

    Fatigue crack growth and active corrosion processes are the main causes for structural failures of transport products like road tankers, railway tank cars, and ships. Within the 7{sup th} EC framework programme the aim of project CORFAT is to develop a new monitoring technology based on acoustic emission testing (AT) of the structural integrity in terms of proceeding degradation. Differentiation of acoustic emission (AE) signals of real degradation processes by fatigue crack growth or active corrosion from operational or environmental background noise requires the signal classification using also pattern recognition. Therefore, a data base of AE signals related to the different source mechanisms was built up experimentally. In this article selected results of corrosion and fatigue tests in the laboratory as well as results of monitoring background noise during moving of a road tanker are described. (orig.)

  1. Stress corrosion crack initiation of alloy 182 weld metal in primary coolant - Influence of chemical composition

    Energy Technology Data Exchange (ETDEWEB)

    Calonne, O.; Foucault, M.; Steltzlen, F. [AREVA (France); Amzallag, C. [EDF SEPTEN (France)

    2011-07-01

    Nickel-base alloys 182 and 82 have been used extensively for dissimilar metal welds. Typical applications are the J-groove welds of alloy 600 vessel head penetrations, pressurizer penetrations, heater sleeves and bottom mounted instrumented nozzles as well as some safe end butt welds. While the overall performance of these weld metals has been good, during the last decade, an increasing number of cases of stress corrosion cracking of Alloy 182 weld metal have been reported in PWRs. In this context, the role of weld defects has to be examined. Their contribution in the crack initiation mechanism requires laboratory investigations with small scale characterizations. In this study, the influence of both alloy composition and weld defects on PWSCC (Stress Corrosion Cracking in Primary Water) initiation was investigated using U-bend specimens in simulated primary water at 320 C. The main results are the following: -) the chemical compositions of the weld deposits leading to a large propensity to hot cracking are not the most susceptible to PWSCC initiation, -) macroscopically, superficial defects did not evolve during successive exposures. They can be included in large corrosion cracks but their role as 'precursors' is not yet established. (authors)

  2. Susceptibility to Stress Corrosion Cracking of 254SMO SS

    Directory of Open Access Journals (Sweden)

    De Micheli Lorenzo

    2002-01-01

    Full Text Available The susceptibility to stress corrosion cracking (SCC of solubilized and sensitized 254SMO SS was studied in sodium chloride, and sodium fluoride solutions at 80 °C and sulfuric acid solutions in presence of sodium chloride at 25 °C. The influence of salt concentration, pH values and the addition of thiosulfate was examined. The susceptibility to SCC was evaluated by Slow Strain Rate Tests (SSRT, at 1.5 x 10-6 s-1 strain rate. The behavior of 254SMO was compared to those of AISI 316L SS and Hastelloy C276. 254SMO showed an excellent resistance to SCC in all conditions, except in the more acidic solutions (pH <= 1 where, in the sensitized conditions, intergranular stress corrosion cracking occurred.

  3. Stress corrosion cracking of brass in ammonia solution

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    Brass foil with a protective layer formed on one side was deflected during corrosion in an ammonia solution under various applied potentials, and then corrosion-induced stress generated at brass/dezincification layer under different potentials could be measured. At the same time, susceptibility to stress corrosion cracking(SCC) of brass in the ammonia solution under various applied potentials was measured using a single-edge notched specimen. At open-circuit potential, both corrosion-induced tensile stress and susceptibility to SCC(Iσ) had a maximum value. Both tensile stress σp and susceptibility Iσ decreased slightly under anodic polarization, but reduced steeply with the decrease in potential of cathodic polarization. At the cathodic potential of -500  mV(vs SCE), corrosion-induced stress became compressive because of copper-plating layer, correspondingly, susceptibility to SCC was zero. Therefore, the variation of SCC susceptibility with potential is consistent with that of the corrosion-induced additive stress.

  4. Laboratory evaluation of soil stress corrosion cracking and hydrogen embrittlement of API grade steels

    Energy Technology Data Exchange (ETDEWEB)

    Bueno, A.H.S.; Castro, B.B.; Ponciano, J.A.C. [Federal Univ. of Rio de Janeiro (Brazil). COPPE

    2004-07-01

    Stress corrosion cracking (SCC) in carbon steels is a form of deterioration that can occur during the service life of a pipeline that is exposed to mechanical stress and strains. A study was conducted to investigate SCC and hydrogen embrittlement (HE) of API grade steels in contact with soil. The physical, chemical and bacteriological characteristics of different soil samples were determined. Slow strain rate tests were performed using electrolytes obtained in the soil samples taken from different points near buried pipelines. Stress versus strain curves were obtained at different electrode potentials for API X46, X60 and X80 steels. The results showed the conjoint incidence of SCC and HE, depending on the potential imposed. It was revealed that HE contributes to the initiation of cracking and crack propagation. Cracking morphology was similar to the SCC found in field situations where transgranular cracking was detected in a pipeline that had collapsed as a result of land creeping. The material exhibited signs of secondary cracking and lower ductility, even under cathodic potentials. It was noted that the methodology used in this study was not able to reproduce the possible effect of microbial induced corrosion. 10 refs., 3 tabs., 3 figs.

  5. Concrete Cracking Prediction Including the Filling Proportion of Strand Corrosion Products

    Directory of Open Access Journals (Sweden)

    Lei Wang

    2016-12-01

    Full Text Available The filling of strand corrosion products during concrete crack propagation is investigated experimentally in the present paper. The effects of stirrups on the filling of corrosion products and concrete cracking are clarified. A prediction model of crack width is developed incorporating the filling proportion of corrosion products and the twisting shape of the strand. Experimental data on cracking angle, crack width, and corrosion loss obtained from accelerated corrosion tests of concrete beams are presented. The proposed model is verified by experimental data. Results show that the filling extent of corrosion products varies with crack propagation. The rust filling extent increases with the propagating crack until a critical width. Beyond the critical width, the rust-filling extent remains stable. Using stirrups can decrease the critical crack width. Stirrups can restrict crack propagation and reduce the rust filling. The tangent of the cracking angle increases with increasing corrosion loss. The prediction of corrosion-induced crack is sensitive to the rust-filling extent.

  6. Stress Corrosion Cracking of Zircaloy-4 in Halide Solutions: Effect of Temperature

    Directory of Open Access Journals (Sweden)

    Farina S.B.

    2002-01-01

    Full Text Available Zircaloy-4 was found to be susceptible to stress corrosion cracking in 1 M NaCl, 1 M KBr and 1 M KI aqueous solutions at potentials above the pitting potential. In all the solutions tested crack propagation was initially intergranular and then changed to transgranular. The effect of strain rate and temperature on the SCC propagation was investigated. An increase in the strain rate was found to lead to an increase in the crack propagation rate. The crack propagation rate increases in the three solutions tested as the temperatures increases between 20 and 90 °C. The Surface-Mobility SCC mechanism accounts for the observation made in the present work, and the activation energy predicted in iodide solutions is similar to that found in the literature.

  7. Stress corrosion cracking of several high strength ferrous and nickel alloys

    Science.gov (United States)

    Nelson, E. E.

    1971-01-01

    The stress corrosion cracking resistance of several high strength ferrous and nickel base alloys has been determined in a sodium chloride solution. Results indicate that under these test conditions Multiphase MP35N, Unitemp L605, Inconel 718, Carpenter 20Cb and 20Cb-3 are highly resistant to stress corrosion cracking. AISI 410 and 431 stainless steels, 18 Ni maraging steel (250 grade) and AISI 4130 steel are susceptible to stress corrosion cracking under some conditions.

  8. Threshold Stress Intensity of Hydrogen-Induced Cracking and Stress Corrosion Cracking of High Strength Steel

    Institute of Scientific and Technical Information of China (English)

    2001-01-01

    The threshold stress intensity of stress corrosion cracking (SCC) for 40CrMo steel in 3.5 % NaCl solution decreased exponentially with the increase of yield strength. The threshold stress intensity of hydrogen-induced cracking during dynamical charging for 40CrMo steel decreased linearly with the logarithm of the concentration of diffusible hydrogen. This equation was also applicable to SCC of high strength steel in aqueous solution. The critical hydrogen enrichment concentration necessary for SCC of high strength steel in water decreased exponentially with the increase of yield strength. Based on the results, the relationship between KISCC and σys could be deduced.

  9. FEM Modelling of the Evolution of Corrosion Cracks in Reinforced Concrete Structures

    DEFF Research Database (Denmark)

    Thoft-Christensen, Palle

    Corrosion cracks are caused by the increasing volume of corrosion products during the corrosion of the reinforcement. After corrosion initiation the rust products from the corroded reinforcement will initially fill the porous zone near the reinforcement and the result in an expansion of the concr...

  10. Statistical model of stress corrosion cracking based on extended form of Dirichlet energy

    Indian Academy of Sciences (India)

    Harry Yosh

    2013-12-01

    The mechanism of stress corrosion cracking (SCC) has been discussed for decades. Here I propose a model of SCC reflecting the feature of fracture in brittle manner based on the variational principle under approximately supposed thermal equilibrium. In that model the functionals are expressed with extended forms of Dirichlet energy, and Dirichlet principle is applied to them to solve the variational problem that represents SCC and normal extension on pipe surface. Based on the model and the maximum entropy principle, the statistical nature of SCC colony is discussed and it is indicated that the crack has discrete energy and length under ideal isotropy of materials and thermal equilibrium.

  11. The crack growth mechanism in asphaltic mixes

    NARCIS (Netherlands)

    Jacobs, .M.M.J.; Hopman, P.C.; Molenaar, A.A.A.

    1995-01-01

    The crack growth mechanism in asphalt concrete (Ac) mixes is studied. In cyclic tests on several asphaltic mixes crack growth is measured, both with crack foils and with cOD-gauges. It is found that crack growth in asphaltic mixes is described by three processes which are parallel in time: cohesive

  12. In Situ X-ray Microtomography of Stress Corrosion Cracking and Corrosion Fatigue in Aluminum Alloys

    Science.gov (United States)

    Singh, Sudhanshu S.; Stannard, Tyler J.; Xiao, Xianghui; Chawla, Nikhilesh

    2017-08-01

    Structural materials are subjected to combinations of stress and corrosive environments that work synergistically to cause premature failure. Therefore, studies on the combined effect of stress and corrosive environments on material behavior are required. Existing studies have been performed in two dimensions that are inadequate for full comprehension of the three-dimensional (3D) processes related to stress corrosion cracking (SCC) and corrosion-fatigue (CF) behavior. Recently, x-ray synchrotron tomography has evolved as an excellent technique to obtain the microstructure in 3D. Moreover, being nondestructive in nature, x-ray synchrotron tomography is well suited to study the evolution of microstructure with time (4D, or fourth dimension in time). This article presents our recent 4D studies on SCC and CF of Al 7075 alloys using x-ray synchrotron tomography.

  13. Inhibition of Ce3+ on Stress Corrosion Crack of High Strength Aluminum Alloy

    Directory of Open Access Journals (Sweden)

    LI Wen-ting

    2017-05-01

    Full Text Available The stress corrosion cracking (SCC susceptibility of 7A04 high strength aluminum alloy in 3.5% (mass fraction NaCl solution and the Ce3+ inhibition of SCC were investigated by slow stress rate test(SSRT, using constant current polarization, electrochemical noise (ECN and electrochemical impedance spectroscopy (EIS techniques. The inhibition mechanism of Ce3+ ions on the initiation and propagation of cracking was also analyzed. The results indicate that both anodic and cathodic galvanostatic polarizations can accelerate the SCC of 7A04, the former increases anodic dissolution but the latter accelerates hydrogen embrittlement of crack tip. SCC susceptibility of 7A04 can be reduced effectively by the addition of cerium ions, the fracture time is delayed and slowed down, but only during the initiation other than the propagation stage of cracking. Ce3+ ions can restrain the initiation of metastable pitting on the surface of 7A04 specimen, which therefore increase the induction time of the cracking since that the micro pits are usually the source of cracking.However, once the crack begins to propagate or the specimen is notched, the addition of cerium ions can rarely inhibit the cracking process. This is possibly attributed to that the radius of Ce3+ ion is too large to diffuse into the crack tip or it is hard to form protective CeO2 layer, Ce3+ ion therefore fails to rehabilitate the active alloy at the crack tip and further reduce the SCC developing rate of 7A04. SEM also indicates that the crack initiation of smooth 7A04 specimens is mainly induced by metastable or stable pits.

  14. Penetration of corrosion products and corrosion-induced cracking in reinforced cementitious materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Brad J.; Peterova, Adela;

    2014-01-01

    This paper describes experimental investigations on corrosion-induced deterioration in reinforced cementitious materials and the subsequent development and implementation of a novel conceptual model. Rejnforced mortar specimens of varying water-to-cement ratios were subjected to current-induced c......This paper describes experimental investigations on corrosion-induced deterioration in reinforced cementitious materials and the subsequent development and implementation of a novel conceptual model. Rejnforced mortar specimens of varying water-to-cement ratios were subjected to current......-induced corrosion (10, 50, and 100 mu A/cm(2)). X-ray attenuation measurements and visual investigations provided both qualitative and quantitative information on the penetration of solid corrosion products into the surrounding cementitious matrix. X-ray attenuation measurements provided time- and location......-dependent concentrations of corrosion products averaged through the specimen thickness. Digital image correlation (DIC) was used to measure corrosion-induced deformations including deformations between steel and cementitious matrix as well as formation and propagation of corrosion-induced cracks. Based on experimental...

  15. Towards a quantification of stress corrosion mechanisms: numerical simulations of hydrogen-dislocations at the very crack tip; Vers une quantification des mecanismes de corrosion sous contrainte: simulations numeriques des interactions hydrogene-dislocations en pointe de fissure

    Energy Technology Data Exchange (ETDEWEB)

    Chateau, J.P

    1999-01-05

    We discuss the respective roles played by anodic dissolution and hydrogen in SCC mechanisms of f.c.c. materials, by studying the fracture of copper in nitrite for which we compare the results with that previously obtained in 316L steel in hot chloride. It is surprising to note that even the crystallographies at the scale of the micron are different, the macroscopic inclination of the fracture surfaces are the same. In the case of 316L steel, the formation of strong pile-ups in the presence of hydrogen leads to a zigzag fracture along alternated slip planes in the most general case. In the absence of hydrogen, as in copper, this mechanism effectively disappears. Furthermore, numerical simulations of crack shielding by dislocations emitted on one plane predict the macroscopic inclination. It shows that it is due to the mere dissolution which confines slip activity at the very crack tip in f.c.c. materials. In order to quantify the mechanism involved in 316L steel, we developed simulations which numerically solve the coupled diffusion and elasticity equations for hydrogen in the presence of a crack and shielding dislocations. They reproduce the mechanisms of hydrogen segregation on edge dislocations and of a localised softening effect by decreasing pair interactions. These mechanisms lead to i) a localisation of hydrogen embrittlement along the activated slip planes, ii) an increase of the dislocation density in pile-ups, and iii) a decrease of the cross slip probability. These three factors enhance micro-fracture at the head of a pile-up, which is responsible of thezigzag fracture. Introducing the free surface effects for hydrogen, we point out a new mechanism: the inhibition of dislocation sources at the crack tip, which is relevant with the brittle fracture surfaces observed in some cases in 316L steel. The quantification of these different mechanisms allows to give a relation between the local fracture possibility and the macroscopic parameters. A general law for

  16. EXPERT PANEL OVERSIGHT COMMITTEE ASSESSMENT OF FY2008 CORROSION AND STRESS CORROSION CRACKING SIMULANT TESTING PROGRAM

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER KD

    2009-01-08

    The Expert Panel Oversight Committee (EPOC) has been overseeing the implementation of selected parts of Recommendation III of the final report, Expert Panel workshop for Hanford Site Double-Shell Tank Waste Chemistry Optimization, RPP-RPT-22126. Recommendation III provided four specific requirements necessary for Panel approval of a proposal to revise the chemistry control limits for the Double-Shell Tanks (DSTs). One of the more significant requirements was successful performance of an accelerated stress corrosion cracking (SCC) experimental program. This testing program has evaluated the optimization of the chemistry controls to prevent corrosion in the interstitial liquid and supernatant regions of the DSTs.

  17. Near-neutral pH Stress Corrosion Crack Initiation under Simulated Coating Disbondment

    Science.gov (United States)

    Eslami, Abdoulmajid

    This research is aimed at understanding near-neutral pH SCC initiation under disbonded coatings of pipeline steels, and the effect of different environmental and operational factors on crack initiation. Understanding near-neutral pH stress corrosion cracking (SCC) could answer many of the primary questions on crack initiation of SCC which have not yet been answered. It could also assist the development of effective mitigative measures dealing with thousands of kilometer of pipelines containing this form of cracking, in addition to preventive action for future pipeline installations. Near-neutral pH SCC usually occurs under polyethylene tape (PE tape) coated pipelines, at locations where the coating becomes disbonded and/or damaged. Ground water can then penetrate under the damaged/disbonded coating, become trapped and form a suitable environment for corrosion and cracking. Despite extensive studies on this topic the details of crack initiation mechanisms in addition to the exact role of environmental and operational factors on crack initiation are not thoroughly understood. Most previous laboratory tests have been done in aggressive loading conditions and ignored the effect of coatings and cathodic protections (CP). In order to simulate the conditions responsible for crack initiation, a novel testing setup capable of simulating the synergistic effects of coating disbondment, cathodic protection and cyclic loading was implemented. Using this setup and long term laboratory tests near-neutral pH SCC initiation mechanisms and the effect of some environmental and operational factors on crack initiation were investigated. It was found that near-neutral pH SCC initiation does not necessarily occur in near-neutral pH environments as commonly believed. Depending on the level of CP and CO2 in the underground environment, different localized environments with varying pH values from near-neutral to high values above 10 can form under the disbonded coatings. This significantly

  18. Hierarchical petascale simulation framework for stress corrosion cracking

    Science.gov (United States)

    Vashishta, P.; Kalia, R. K.; Nakano, A.; Kaxiras, E.; Grama, A.; Lu, G.; Eidenbenz, S.; Voter, A. F.; Hood, R. Q.; Moriarty, J. A.; Yang, L. H.

    2008-07-01

    We are developing a scalable parallel and distributed computational framework consisting of methods, algorithms, and integrated software tools for multi-terascle-to-petascale simulations of stress corrosion cracking (SCC) with quantum-level accuracy. We have performed multimillion- to billion-atom molecular dynamics (MD) simulations of deformation, flow, and fracture in amorphous silica with interatomic potentials and forces validated by density functional theory (DFT) calculations. Optimized potentials have been developed to study sulfur embrittlement of nickel with multimillion-to-multibillion atom MD simulations based on DFT and temperature dependent model generalized pseudopotential theory. We have also developed a quasi-continuum method embedded with quantum simulations based on DFT to reach macroscopic length scales and an accelerated molecular dynamics scheme to reach macroscopic time scales in simulations of solid-fluid interfaces that are relevant to SCC. A hybrid MD and mesoscale lattice Boltzmann simulation algorithm is being designed to study fluid flow through cracks.

  19. Literature Survey on the Stress Corrosion Cracking of Low-Alloy Steels in High Temperature Water

    Energy Technology Data Exchange (ETDEWEB)

    Seifert, H.P

    2002-02-01

    The present report is a summary of a literature survey on the stress corrosion cracking (SCC) behaviour/ mechanisms in low-alloy steels (LAS) in high-temperature water with special emphasis to primary-pressure-boundary components of boiling water reactors (BWR). A brief overview on the current state of knowledge concerning SCC of low-alloy reactor pressure vessel and piping steels under BWR conditions is given. After a short introduction on general aspects of SCC, the main influence parameter and available quantitative literature data concerning SCC of LAS in high-temperature water are discussed on a phenomenological basis followed by a summary of the most popular SCC models for this corrosion system. The BWR operating experience and service cracking incidents are discussed with respect to the existing laboratory data and background knowledge. Finally, the most important open questions and topics for further experimental investigations are outlined. (author)

  20. Study on Localized Corrosion Cracking of Alloy 600 using EN-DCPD Technique

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Yeonju; Kim, Sungwoo; Kim, Hongpyo; Hwang, Seongsik [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2013-02-15

    The object of this work is to establish an electrochemical noise(EN) measurement technique combined with a direct current potential drop(DCPD) method for monitoring of localized corrosion cracking of nickel-based alloy, and to analyze its mechanism. The electrochemical current and potential noises were measured under various conditions of applied stress to a compact tension specimen in a simulated primary water chemistry of a pressurized water reactor. The amplitude and frequency of the EN signals were evaluated in both time and frequency domains based on a shot noise theory, and then quantitatively analyzed using statistical Weibull distribution function. From the spectral analysis, the effect of the current application in DCPD was found to be effectively excluded from the EN signals generated from the localized corrosion cracking. With the aid of a microstructural analysis, the relationship between EN signals and the localized corrosion cracking mechanism was investigated by comparing the shape parameter of Weibull distribution of a mean time-to-failure.

  1. Elasto-Plasticity Critical Corrosive Ratio Model for RC Structure Corrosive Expanding Crack

    Institute of Scientific and Technical Information of China (English)

    CHEN Yueshun; LU Yiyan; LIU Li

    2007-01-01

    The parameter of filling expanding ratio n, plasticity factor k1 and deformation parameter k2 is raised, and then the elasto-plasticity critical corrosive ratio model for RC structure corrosive expanding crack based on elasto-plasticity theory is constructed in this paper. The influences of parameters such as filling expansion ratio n, plasticity factor k1, deformation parameter k2, Poisson ratio of concrete v, diameter of reinforced bar d and protective layer thickness c on the critical corrosive ratio are researched by theory analysis and experiments. The experimental results validate the accuracy of the model. According to the experimental study, the least squares solution is calculated as n=1.8,k1 =0.61,k2 =0.5.

  2. Cracks propagation by stress corrosion cracking in conditions of Boiling Water Reactor (BWR); Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua hirviente (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Fuentes C, P

    2003-07-01

    This work presents the results of the assays carried out in the Laboratory of Hot Cells of the National Institute of Nuclear Research (ININ) to a type test tube Compact Tension (CT), built in steel austenitic stainless type 304L, simulating those conditions those that it operates a Boiling Water Reactor (BWR), at temperature 288 C and pressure of 8 MPa, to determine the speed to which the cracks spread in this material that is of the one that different components of a reactor are made, among those that it highlights the reactor core vessel. The application of the Hydrogen Chemistry of the Water is presented (HWC) that is one alternative to diminish the corrosion effect low stress in the component, this is gets controlling the quantity of oxygen and of hydrogen as well as the conductivity of the water. The rehearsal is made following the principles of the Mechanics of Elastic Lineal Fracture (LEFM) that considers a crack of defined size with little plastic deformation in the tip of this; the measurement of crack advance is continued with the technique of potential drop of direct current of alternating signal, this is contained inside the standard Astm E-647 (Method of Test Standard for the Measurement of Speed of Growth of Crack by fatigue) that is the one that indicates us as carrying out this test. The specifications that should complete the test tubes that are rehearsed as for their dimensions, it forms, finish and determination of mechanical properties (tenacity to the fracture mainly) they are contained inside the norm Astm E-399, the one which it is also based on the principles of the fracture mechanics. The obtained results were part of a database to be compared with those of other rehearsals under different conditions, Normal Chemistry of the Water (NWC) and it dilutes with high content of O{sub 2}; to determine the conditions that slow more the phenomena of stress corrosion cracking, as well as the effectiveness of the used chemistry and of the method of

  3. Stress corrosion cracking in canistered waste package containers: Welds and base metals

    Energy Technology Data Exchange (ETDEWEB)

    Huang, J.S.

    1998-03-01

    The current design of waste package containers include outer barrier using corrosion allowable material (CAM) such as A516 carbon steel and inner barrier of corrosion resistant material (CRM) such as alloy 625 and C22. There is concern whether stress corrosion cracking would occur at welds or base metals. The current memo documents the results of our analysis on this topic.

  4. Report on Status of Shipment of High Fluence Austenitic Steel Samples for Characterization and Stress Corrosion Crack Testing

    Energy Technology Data Exchange (ETDEWEB)

    Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Leonard, Keith J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-09-01

    The goal of the Mechanisms of Irradiation Assisted Stress Corrosion Cracking (IASCC) task in the LWRS Program is to conduct experimental research into understanding how multiple variables influence the crack initiation and crack growth in materials subjected to stress under corrosive conditions. This includes understanding the influences of alloy composition, radiation condition, water chemistry and metallurgical starting condition (i.e., previous cold work or heat treatments and the resulting microstructure) has on the behavior of materials. Testing involves crack initiation and growth testing on irradiated specimens of single-variable alloys in simulated Light Water Reactor (LWR) environments, tensile testing, hardness testing, microstructural and microchemical analysis, and detailed efforts to characterize localized deformation. Combined, these single-variable experiments will provide mechanistic understanding that can be used to identify key operational variables to mitigate or control IASCC, optimize inspection and maintenance schedules to the most susceptible materials/locations, and, in the long-term, design IASCC-resistant materials.

  5. Sensitization, intergranular attack, stress corrosion cracking, and irradiation effects on the corrosion of iron--chromium--nickel alloys

    Energy Technology Data Exchange (ETDEWEB)

    Wu, P.C.S.

    1978-04-01

    A literature review is presented on the sensitization, intergranular attack, and stress corrosion cracking of austenitic stainless steels with emphasis on dilute solutions at temperatures below the boiling point of water. An attempt is made to list the possible sources of contaminants during manufacture, shipping, construction and all phases of operation of the sodium containing components. The susceptibility of the different materials to stress corrosion cracking in the various contaminants is discussed and suggestions to prevent serious problems are made. (GHT)

  6. Relativity between corrosion-induced stress and stress corrosion cracking of brass in an ammonia solution

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    The susceptibility to stress corrosion cracking (SCC) of brass in an ammonia solution with various pH values or under various applied potentials was measured at slow strain rate tests. The additive stress in the same solution was measured using two methods. The results indicate that the variation of the susceptibility to SCC with pH value or with potential is in an excellent agreement with the corrosion (passive film or dezincification layer)-induced stress. When pH ? 7, the corrosion-induced tensile stress and the susceptibility to SCC have maximum values and hardly change with increasing the pH value. However, when pH < 7, both the corrosion-induced tensile stress and the susceptibility to SCC reduce rapidly with decreasing the pH value. Both the corrosion-induced tensile stress and the susceptibility to SCC have maximum values at the open-circuit potential, decrease slightly under the anodic polarization, and reduce gradually to zero under the cathodic polarization.

  7. Consideration on corrosion fatigue crack life assessment; Fushoku hiro kiretsu hassei jumyo hyoka ni kansuru ichikosatsu

    Energy Technology Data Exchange (ETDEWEB)

    Yajima, H.; Yamamoto, M.; Saito, T. [Hiroshima University, Hiroshima (Japan). Faculty of Engineering; Morita, K. [Mitsubishi Heavy Industries, Ltd., Tokyo (Japan)

    1996-10-01

    Discussions were given on corrosion fatigue crack life by using corrosion fatigue crack initiation test and analysis. The test used 13Cr-based stainless steel as a test material, and aquamarine at 60{degree}C as a corrosion environment. The fatigue test was performed under a tension loading condition with a stress ratio of 0.1 and an iterative velocity of 1.7 Hz by using a 10-tonf fatigue testing machine. In the corrosion fatigue crack initiation test, a pit has been generated on a boundary of an exposed part and a painted part for masking, hence direct observation was impossible on pit growth behavior. Therefore, an intrinsic crack model was introduced from pit dimensions as observed from a fracture face, and analysis was made on corrosion fatigue crack growth by using the linear fracture dynamics, wherein clarification was made on a phenomenon occurring after the crack growth passes the pit growth until the test piece is fractured. A proposal was made to define the time when fatigue crack initiates and grows from the bottom of a pit as a result of surpassing the growth of corrosion pit as the corrosion fatigue crack life. 4 refs., 7 figs., 1 tab.

  8. Stress corrosion cracking for 316 stainless steel clips in a condensate stabilizer

    Energy Technology Data Exchange (ETDEWEB)

    Al-Awar, A.; Aldajah, S.; Harhara, A. [Department of Mechanical Engineering, United Arab Emirates University, P. O. Box 17555 Al-AIn 17555 (United Arab Emirates)

    2011-09-15

    In one of the gas processing facilities in Abu Dhabi, UAE; a case of 316L stainless steel material failure occurred in the fractionating column due to stress cracking corrosion twice in a cycle of less than 2 years. This paper studies the stress corrosion cracking behavior of the 316L stainless steel in an accelerated corrosion environment and compares it with a higher corrosion resistant nickel alloy (Inconel 625). The experimental work was designed according to ASTM G36 standard, the samples were immersed in a boiling magnesium chloride medium which provided the accelerated corrosion environment and the tested samples were shaped into U-bend specimens as they underwent both plastic and elastic stresses. The specimens were then tested to determine the time required for cracks to initiate. The results of the experimental work showed that the main mode of failure was stress corrosion cracking initiated by the proven presence of chlorides, hydrogen sulfide, and water at elevated temperatures. Inconel 625 samples placed in the controlled environment showed better corrosion resistance as it took them an average of 56 days to initiate cracks, whereas it took an average of 24 days to initiate cracks in the stainless steel 316L samples. The scanning electron microscopy (SEM) micrographs showed that the cracks in the stainless steel 316L samples were longer, wider, and deeper compared to the cracks of Inconel 625. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  9. Diffusion-Coupled Cohesive Interface Simulations of Stress Corrosion Intergranular Cracking in Polycrystalline Materials

    Energy Technology Data Exchange (ETDEWEB)

    Pu, Chao; Gao, Yanfei; Wang, Yanli; Sham, T.-L.

    2017-09-01

    To study the stress corrosion intergranular cracking mechanism, a diffusion-coupled cohesive zone model (CZM) is proposed for the simulation of the stress-assisted diffusional process along grain boundaries and the mechanical response of grain boundary sliding and separation. This simulation methodology considers the synergistic effects of impurity diffusion driven by pressure gradient and degradation of grain boundary strength by impurity concentration. The diffusion-coupled CZM is combined with crystal plasticity finite element model (CPFEM) to simulate intergranular fracture of polycrystalline material under corrosive environment. Significant heterogeneity of the stress field and extensive impurity accumulation is observed at grain boundaries and junction points. Deformation mechanism maps are constructed with respect to the grain boundary degradation factor and applied strain rate, which dictate the transition from internal to near-surface intergranular fracture modes under various strain amplitudes and grain sizes.

  10. Ultrasonic inspection reliability for intergranular stress corrosion cracks

    Energy Technology Data Exchange (ETDEWEB)

    Heasler, P G; Taylor, T T; Spanner, J C; Doctor, S R; Deffenbaugh, J D [Pacific Northwest Lab., Richland, WA (USA)

    1990-07-01

    A pipe inspection round robin entitled Mini-Round Robin'' was conducted at Pacific Northwest Laboratory from May 1985 through October 1985. The research was sponsored by the US Nuclear Regulatory Commission, Office of Nuclear Regulatory Research under a program entitled Evaluation and Improvement of NDE Reliability for Inservice Inspection of Light Water Reactors.'' The Mini-Round Robin (MRR) measured the intergranular stress corrosion (GSC) crack detection and sizing capabilities of inservice inspection (ISI) inspectors that had passed the requirements of IEB 83-02 and the Electric Power Research Institute (EPRI) sizing training course. The MRR data base was compared with an earlier Pipe Inspection Round Robin (PIRR) that had measured the performance of inservice inspection prior to 1982. Comparison of the MRR and PIRR data bases indicates no significant change in the inspection capability for detecting IGSCC. Also, when comparing detection of long and short cracks, no difference in detection capability was measured. An improvement in the ability to differentiate between shallow and deeper IGSCC was found when the MRR sizing capability was compared with an earlier sizing round robin conducted by the EPRI. In addition to the pipe inspection round robin, a human factors study was conducted in conjunction with the Mini-Round Robin. The most important result of the human factors study is that the Relative Operating Characteristics (ROC) curves provide a better methodology for describing inspector performance than only probability of detection (POD) or single-point crack/no crack data. 6 refs., 55 figs., 18 tabs.

  11. Factors affecting stress assisted corrosion cracking of carbon steel under industrial boiler conditions

    Science.gov (United States)

    Yang, Dong

    Failure of carbon steel boiler tubes from waterside has been reported in the utility boilers and industrial boilers for a long time. In industrial boilers, most waterside tube cracks are found near heavy attachment welds on the outer surface and are typically blunt, with multiple bulbous features indicating a discontinuous growth. These types of tube failures are typically referred to as stress assisted corrosion (SAC). For recovery boilers in the pulp and paper industry, these failures are particularly important as any water leak inside the furnace can potentially lead to smelt-water explosion. Metal properties, environmental variables, and stress conditions are the major factors influencing SAC crack initation and propagation in carbon steel boiler tubes. Slow strain rate tests (SSRT) were conducted under boiler water conditions to study the effect of temperature, oxygen level, and stress conditions on crack initation and propagation on SA-210 carbon steel samples machined out of boiler tubes. Heat treatments were also performed to develop various grain size and carbon content on carbon steel samples, and SSRTs were conducted on these samples to examine the effect of microstructure features on SAC cracking. Mechanisms of SAC crack initation and propagation were proposed and validated based on interrupted slow strain tests (ISSRT). Water chemistry guidelines are provided to prevent SAC and fracture mechanics model is developed to predict SAC failure on industrial boiler tubes.

  12. A non-destructive test method to monitor corrosion products and corrosion-induced cracking in reinforced cement based materials

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Peterova, Adela

    2011-01-01

    This paper introduces a non-destructive test method to monitor the development of corrosion products as well as the corrosion-induced formation and propagation of cracks in cementitious materials. A parametric experimental investigation (utilizing x-ray attenuation measurement technique...

  13. Monitoring reinforcement corrosion and corrosion-induced cracking using non-destructive x-ray attenuation measurements

    DEFF Research Database (Denmark)

    Michel, Alexander; Pease, Bradley Justin; Geiker, Mette Rica

    2011-01-01

    To test the applicability of the x-ray attenuation method to monitor the movement of corrosion products as well as the formation and propagation of cracks in cementitious materials reinforced mortar samples were prepared and tested under accelerated corrosion conditions. It is evident from...

  14. Hydrogen-related stress corrosion cracking in line pipe steel

    DEFF Research Database (Denmark)

    Nielsen, Lars Vendelbo

    1997-01-01

    A correlation between hydrogen concentration (C0) and the critical stress intensity factor for propagation of hydrogen-related cracks has been established by fracture mechanical testing of CT-specimens for the heat affected zone of an X-70 pipeline steel. This has been compared with field...

  15. Metallurgical and mechanical parameters controlling alloy 718 stress corrosion cracking resistance in PWR primary water; Facteurs metallurgiques et mecaniques controlant l'amorcage de defauts de corrosion sous contrainte dans l'alliage 718 en milieu primaire des reacteurs a eau sous pression

    Energy Technology Data Exchange (ETDEWEB)

    Deleume, J

    2007-11-15

    Improving the performance and reliability of the fuel assemblies of the pressurized water reactors requires having a perfect knowledge of the operating margins of both the components and the materials. The choice of alloy 718 as reference material for this study is justified by the industrial will to identify the first order parameters controlling the excellent resistance of this alloy to Stress Corrosion Cracking (SCC). For this purpose, a specific slow strain rate (SSR) crack initiation test using tensile specimen with a V-shaped hump in the middle of the gauge length was developed and modeled. The selectivity of such SSR tests in simulated PWR primary water at 350 C was clearly established by characterizing the SCC resistance of nine alloy 718 thin strip heats. Regardless of their origin and in spite of a similar thermo-mechanical history, they did not exhibit the same susceptibility to SCC crack initiation. All the characterized alloy 718 heats develop oxide scale of similar nature for various exposure times to PWR primary medium in the temperature range [320 C - 360 C]. {delta} phase precipitation has no impact on alloy 718 SCC initiation behavior when exposed to PWR primary water, contrary to interstitial contents and the triggering of plastic instabilities (PLC phenomenon). (author)

  16. Electrochemical studies on stress corrosion cracking of incoloy-800 in caustic solution. Part II: Precracking samples

    Directory of Open Access Journals (Sweden)

    Dinu Alice

    2006-01-01

    Full Text Available Stress corrosion cracking (SCC in a caustic medium may affect the secondary circuit tubing of a CANDU NPP cooled with river water, due to an accidental formation of a concentrated alkaline environment in the areas with restricted circulation, as a result of a leakage of cooling water from the condenser. To evaluate the susceptibility of Incoloy-800 (used to manufacture steam generator tubes for CANDU NPP to SCC, some accelerated corrosion tests were conducted in an alkaline solution (10% NaOH, pH = 13. These experiments were performed at ambient temperature and 85 °C. We used the potentiodynamic method and the potentiostatic method, simultaneously monitoring the variation of the open circuit potential during a time period (E corr/time curve. The C-ring method was used to stress the samples. In order to create stress concentrations, mechanical precracks with a depth of 100 or 250 μm were made on the outer side of the C-rings. Experimental results showed that the stressed samples were more susceptible to SCC than the unstressed samples whereas the increase in temperature and crack depth lead to an increase in SCC susceptibility. Incipient micro cracks of a depth of 30 μm were detected in the area of the highest peak of the mechanical precrack.

  17. The role of local strains from prior cold work on stress corrosion cracking

    Science.gov (United States)

    Ulaganathan, Jaganathan

    Several studies have recently reported that cold working exacerbates stress corrosion cracking (SCC) of materials in various environments, including those in which they were previously thought to be immune. While these studies usually consider cold work as a homogeneous effect, the presence of grain boundaries results in local strain concentrations that are inhomogeneously distributed within the microstructure. In order to understand the underlying mechanisms by which the local strains generated by cold work influences SCC, α-brass and Alloy 600 were used in this study. The microscopic changes in the local strains caused by cold work and by SCC were measured using electron backscatter diffraction (EBSD) and polychromatic X-ray microdiffraction (PXM). While the plastic strains were qualitatively expressed through the local misorientation calculated from the orientation data measured by both EBSD and PXM, the elastic strains were determined from the Laue patterns measured by PXM. The interaction between the local strains, and the crack initiation and propagation during SCC was studied by comparing the strain distribution from the same area measured before cold work, after cold work, and again after SCC. In this way, apart from obtaining insights on the interaction, the relative importance of pre-existing strain concentrations and those created by crack propagation can be identified. Additionally, statistical analysis of the EBSD data from uncracked and cracked grain boundaries in Alloy 600 showed the susceptibility of the boundaries to increase when they were surrounded by high local strain concentrations and when the grains sharing the boundary had similar deformation tendency, but to be independent of the grain boundary angle. Finally, one of the contributors for the changes in the strain distribution during SCC can be the corrosion process itself which was examined by intermittently measuring the changes in local strains caused by intergranular corrosion on an

  18. Corrosion and stress corrosion cracking of ferritic/martensitic steel in super critical pressurized water

    Energy Technology Data Exchange (ETDEWEB)

    Hirose, T. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan)]. E-mail: hirose.takanori@jaea.go.jp; Shiba, K. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan); Enoeda, M. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan); Akiba, M. [Naka Fusion Research Institute, JAEA, 801-1 Mukouyama, Naka, Ibaraki 311-0193 (Japan)

    2007-08-01

    A water-cooled solid breeder (WCSB) blanket cooled by high temperature SCPW (super critical pressurized water) is a practical option of DEMO reactor. Therefore, it is necessary to check the compatibility of the steel with SCPW. In this work, reduced activation ferritic/martensitic steel, F82H has been tested through slow strain rate tests (SSRT) in 23.5 MPa SCPW. And weight change behavior was measured up to 1000 h. F82H did not demonstrated stress corrosion cracking and its weight simply increased with surface oxidation. The weight change of F82H was almost same as commercial 9%-Cr steels. According to a cross-sectional analysis and weight change behavior, corrosion rate of F82H in the 823 K SCPW is estimated to be 0.04 mm/yr.

  19. Crack branching in carbon steel. Fracture mechanisms

    Science.gov (United States)

    Syromyatnikova, A. S.; Alekseev, A. A.; Levin, A. I.; Lyglaev, A. V.

    2010-04-01

    The fracture surfaces of pressure vessels made of carbon steel that form during crack branching propagation are examined by fractography. Crack branching is found to occur at a crack velocity higher than a certain critical value V > V c . In this case, the material volume that is involved in fracture and depends on the elastoplastic properties of the material and the sample width has no time to dissipate the energy released upon crack motion via the damage mechanisms intrinsic in the material under given deformation conditions (in our case, via cracking according to intragranular cleavage).

  20. Statistical model of stress corrosion cracking based on extended form of Dirichlet energy: Part 2

    Indian Academy of Sciences (India)

    HARRY YOSH

    2016-10-01

    In the previous paper ({\\it Pramana – J. Phys.} 81(6), 1009 (2013)), the mechanism of stress corrosion cracking (SCC) based on non-quadratic form of Dirichlet energy was proposed and its statistical features were discussed. Following those results, we discuss here how SCC propagates on pipe wall statistically. It reveals that SCC growth distribution is described with Cauchy problem of time-dependent first-order partial differential equation characterized by the convolution of the initial distribution of SCC over time. We also discuss the extension of the above results to the SCC in two-dimensional space and its statistical features with a simple example.

  1. Quantitative characterization of initiation and propagation in stress corrosion cracking. An approach of a phenomenological model; Caracterisation quantitative de l`amorcage et de la propagation en corrosion sous contrainte. Approche d`une modelisation phenomenologique

    Energy Technology Data Exchange (ETDEWEB)

    Raquet, O.

    1994-11-25

    A purely phenomenological study of stress corrosion cracking was performed using the couple Z2CN 18.10 (304L) austenitic stainless steel/boiling MgCl{sub 2} aqueous solution. The exploitation of the morphological information (shape of the cracks and size distribution) available after constant elongation rate tests led to the proposal of an analytical expression of the crack initiation and growth rates. This representation allowed to quantitatively characterize the influence of the applied strain rate as well as the effect of corrosion inhibitors on the crack initiation and propagation phases. It can be used in the search for the stress corrosion cracking mechanisms as a `riddle` for the determination of the rate controlling steps. As a matter of fact, no mechanistic hypothesis has been used for its development. (author).

  2. POTENTIAL FOR STRESS CORROSION CRACKING OF A537 CARBON STEEL NUCLEAR WASTE TANKS CONTAINING HIGHLY CAUSTIC SOLUTIONS

    Energy Technology Data Exchange (ETDEWEB)

    Lam, P.; Stripling, C.; Fisher, D.; Elder, J.

    2010-04-26

    The evaporator recycle streams of nuclear waste tanks may contain waste in a chemistry and temperature regime that exceeds the current corrosion control program, which imposes temperature limits to mitigate caustic stress corrosion cracking (CSCC). A review of the recent service history found that two of these A537 carbon steel tanks were operated in highly concentrated hydroxide solution at high temperature. Visual inspections, experimental testing, and a review of the tank service history have shown that CSCC has occurred in uncooled/un-stress relieved tanks of similar construction. Therefore, it appears that the efficacy of stress relief of welding residual stress is the primary corrosion-limiting mechanism. The objective of this experimental program is to test A537 carbon steel small scale welded U-bend specimens and large welded plates (30.48 x 30.38 x 2.54 cm) in a caustic solution with upper bound chemistry (12 M hydroxide and 1 M each of nitrate, nitrite, and aluminate) and temperature (125 C). These conditions simulate worst-case situations in these nuclear waste tanks. Both as-welded and stress-relieved specimens have been tested. No evidence of stress corrosion cracking was found in the U-bend specimens after 21 days of testing. The large plate test was completed after 12 weeks of immersion in a similar solution at 125 C except that the aluminate concentration was reduced to 0.3 M. Visual inspection of the plate revealed that stress corrosion cracking had not initiated from the machined crack tips in the weld or in the heat affected zone. NDE ultrasonic testing also confirmed subsurface cracking did not occur. Based on these results, it can be concluded that the environmental condition of these tests was unable to develop stress corrosion cracking within the test periods for the small welded U-bends and for the large plates, which were welded with an identical procedure as used in the construction of the actual nuclear waste tanks in the 1960s. The

  3. Crack propagation in fracture mechanical graded structures

    Directory of Open Access Journals (Sweden)

    B. Schramm

    2015-10-01

    Full Text Available The focus of manufacturing is more and more on innovative and application-oriented products considering lightweight construction. Hence, especially functional graded materials come to the fore. Due to the application-matched functional material gradation different local demands such as absorbability, abrasion and fatigue of structures are met. However, the material gradation can also have a remarkable influence on the crack propagation behavior. Therefore, this paper examines how the crack propagation behavior changes when a crack grows through regions which are characterized by different fracture mechanical material properties (e.g. different threshold values KI,th, different fracture toughness KIC. In particular, the emphasis of this paper is on the beginning of stable crack propagation, the crack velocity, the crack propagation direction as well as on the occurrence of unstable crack growth under static as well as cyclic loading. In this context, the developed TSSR-concept is presented which allows the prediction of crack propagation in fracture mechanical graded structures considering the loading situation (Mode I, Mode II and plane Mixed Mode and the material gradation. In addition, results of experimental investigations for a mode I loading situation and numerical simulations of crack growth in such graded structures confirm the theoretical findings and clarify the influence of the material gradation on the crack propagation behavior.

  4. Misunderstanding and Understanding of Primary Water Stress Corrosion Cracking of Structural Components in the Primary System of PWRs

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Young Suk; Kim, Sung Soo; Kim, Dae Whan [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2014-05-15

    All the structural components in the primary system of pressurized water reactors that are in contact with primary water are made of austenitic Ni-Cr-Fe alloys which are known to be corrosion resistant. Nevertheless, these Ni-Cr-Fe alloys such as Alloy 600, weld 182/82, austenitic stainless steels suffer from intergranular stress corrosion cracking (IGSCC) after their 10 year operation in reactors although the environment to which they have been exposed is almost pure water of pH 6.9 to 7.2, which is called primary water stress corrosion cracking (PWSCC). Given that the underlying mechanism of PWSCC remains unidentified so far, there are many misunderstandings related to PWSCC of the structural components, which may lead to unreasonable mitigation measures. The aim of this work is to highlight understanding and misunderstanding of PWSCC related to austenitic Ni-Cr-Fe alloys.

  5. Effect of proton irradiation on irradiation assisted stress corrosion cracking in PWR

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Han Ok; Hwang, Mi Jin; Kim, Sung Woo; Hwang, Seong Sik [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of)

    2014-05-15

    Irradiation assisted stress corrosion cracking (IASCC) involves the cracking and failure of materials under irradiation environment in nuclear power plant water environment. The major factors and processes governing an IASCC are suggested by others. The IASCC of the reactor core internals due to the material degradation and the water chemistry change has been reported in high stress stainless steel components, such as fuel elements (Boiling Water Reactors) in the 1960s, a control rod in the 1970s, and a baffle former bolt in recent years of light water reactors (Pressurized Water Reactors). Many irradiated stainless steels that are resistant to inergranular cracking in 288 .deg. C argon are susceptible to IG cracking in the simulated BWR environment at the same temperature. Under the circumstances, a lot works have been performed on IASCC in BWR. Recent efforts have been devoted to investigate an IASCC in a PWR, but the mechanism in a PWR is not fully understood yet as compared with that in a BWR owing to a lack of data from laboratories and fields. Therefore, it is strongly necessary to review and analyze recent researches of an IASCC in both BWR and PWR for establishing a proactive management technology for the IASCC of core internals in Korean PWRs. The objective of this research to find IASCC behavior of proton irradiated 316 stainless steels in a high-temperature water chemistry environment. The IASCC initiation susceptibility on 1, 3, 5 DPA proton irradiated 316 austenite stainless steel was evaluated in PWR environment. SCC area ratio on the fracture surface was similar regardless of irradiation level. Total crack length on the irradiated surface increases in order of specimen 1, 3, 5 DPA. The total crack length at the side surface is a better measure in evaluating IASCC initiation susceptibility for proton-irradiated samples.

  6. Strain-induced corrosion cracking in ferritic components of BWR primary circuits; Risskorrosion in druckfuehrenden ferritischen Komponenten des Primaerkreislaufes von Siedewasserreaktoren

    Energy Technology Data Exchange (ETDEWEB)

    Seifert, H.-P.; Ritter, S.; Ineichen, U.; Tschanz, U.; Gerodetti, B

    2003-04-01

    The present final report of the RIKORR project is a summary of a literature survey and of the experimental work performed by PSI on the environmentally-assisted cracking (EAC) and dynamic strain ageing (DSA) susceptibility of low-alloy steels (LAS) in high-temperature (HT) water. Within this project, the EAC crack growth behaviour of different low-alloy RPV steels, weld filler and weld heat-affected zone materials has been investigated under simulated transient and steady-state BWR/NWC power operation conditions. The strain-induced corrosion cracking (SICC) / low-frequency corrosion fatigue (CF) and stress corrosion cracking (SCC) crack growth behaviour of different low-alloy RPV steels under simulated transient and stationary BWR/NWC conditions was characterized by slow rising load / low-frequency corrosion fatigue and constant load / periodical partial unloading / ripple load tests with pre-cracked fracture mechanics specimens in oxygenated HT water at temperatures of either 288, 250, 200 or 150 {sup o}C. Modern high-temperature water loops, on-line crack growth monitoring and fractographic analysis by scanning electron microscopy (SEM) were used to quantify the cracking response. (author)

  7. Corrosion fatigue behavior of fastening hole structure and virtual crack propagation tests

    Institute of Scientific and Technical Information of China (English)

    Youhong Zhang; Xinlong Chang; Guozhi Lv; Hui Wang; Zhong Li; Yueliang Cheng

    2008-01-01

    The fatigue crack propagation behavior of the LY12CZ aluminum alloy fastener involving a central hole in air or in 3.5wt% NaC1 solution was investigated. The experimental results indicated that the corrosion fatigue crack growth rate decreased with the increasing loading frequency, and in a corrosive environment, the crack growth rate was slightly larger than that in air.Based on the experimental results, the virtual corrosion fatigue crack propagation tests were investigated and the stochastic process method and the AFGROW simulation method were presented. The normal process and lognormal process were considered for the stochastic process method based on the numerically fitted Paris equation. The distribution of crack size and the corresponding prob-abilistic model of crack length distribution for a given number of cycles can be found by integrating the stochastic process over time.Using the AFGROW software, the virtual simulation was carried out to analyze the corrosion fatigue crack growth behavior and the predicted crack growth curve was in good agreement with the experimental results.

  8. Stress corrosion cracking and hydrogen embrittlement of thick section high strength low alloy steel.

    OpenAIRE

    Needham, William Donald

    1986-01-01

    An experimental study was conducted to evaluate the corrosion performance of weldments of a high strength low alloy(HSLA) steel in a simulated seawater environment. This steel, designated HSLA80, was developed by the United States Navy for use in ship structural applications. Stress corrosion CRACKING(SCC) and hydrogen embrittlement(HEM) were investigated by conducting 42 Wedge-Opening load(WOL) tests as a function of stress intensity and corrosion potential and 33 Slow Strain Rate(SSR) tests...

  9. Effect of prior corrosion state on the fatigue small cracking behaviour of 6151-T6 aluminum alloy

    Energy Technology Data Exchange (ETDEWEB)

    Li Xudong [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Naval Aeronautical Engineering Academy Qingdao Branch, Qingdao 266000 (China); Wang Xishu, E-mail: xshwang@tsinghua.edu.cn [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Ren Huaihui; Chen Yinlong [Department of Engineering Mechanics, AML, Tsinghua University, Beijing 100084 (China); Mu Zhitao [Naval Aeronautical Engineering Academy Qingdao Branch, Qingdao 266000 (China)

    2012-02-15

    Highlights: Black-Right-Pointing-Pointer Relationship of corrosion pit and fatigue crack is established based on SEM. Black-Right-Pointing-Pointer An equivalent relationship between accelerated and natural corrosion is build up. Black-Right-Pointing-Pointer Prior corrosion damage is crucial to the subsequent fatigue cracking behaviour. Black-Right-Pointing-Pointer The prior corrosion fatigue crack growth rate is expressed by the term of k{sigma}{sub max}{sup n}a. Black-Right-Pointing-Pointer Corrosion states such as SC15, are defined based on corrosion spectrum. - Abstract: The purpose of this paper was to estimate the reliable effect of prior corrosion state on fatigue micro crack initiation and early stage propagation behaviour of aluminum alloy based on scanning electron microscopy (SEM) in situ observation. Results indicated that multi-cracks initiation occurred almost at the corrosion pits and the early stage of fatigue micro crack propagation behaviour can be described by K{sub I}/K{sub II}-mixed mode. The importance of crack-face interaction via crack-face corrosion pits interlocking/bridging was emphasised in the mixed mode. The fatigue crack growth rate in the corrosion states can be empirically expressed by the term of k{sigma}{sub max}{sup n}a.

  10. Modeling Threshold of Stress Intensity Factor in Iodine Induced Stress Corrosion Crack of Zirconium

    Institute of Scientific and Technical Information of China (English)

    SHANG; Xin-yuan; CHEN; Peng

    2013-01-01

    KISCC,which is the threshold of stress intensity factor of iodine induced stress corrosion crack(ISCC)of Zirconium,reflects the susceptibility of ISCC of zirconium.Once the stress intensity factor surpasses the threshold,the cracking propagation modality in material will transform to transgranular from intergranular immediately and the velocity of the cracking will increase rapidly.Four key factors that’s

  11. H2S Stress Corrosion Tests of Welded Joint for X65 Pipeline Steel and Finite Element Numerical Analysis of Crack Tip

    Institute of Scientific and Technical Information of China (English)

    金晓军; 霍立兴; 张玉凤; 白秉仁; 李小巍; 曹军

    2003-01-01

    The microstructure of welded joint is surveyed and the mechanical properties of X65 pipeline steel are studied in this paper, which provides experimental basis of performance effect on stress corrosion. H2S stress corrosion cracking (SCC) tests on the steel are carried out in the environment based on NACE TM-01-77 solution. The threshold stress intensity factor and crack propagation velocity for base metal and HAZ are obtained. The susceptibility of welded joint for X65 pipeline steel to H2S stress corrosion cracking is investigated. The programming package ANSYS of finite element model (FEM) is used to perform the three-dimensional elastic-plastic finite element analysis of WOL specimens. Stress field and concentration of hydrogen distribution property of the crack tip are obtained.

  12. Corrosion Fatigue Crack Growth Behavior at Notched Hole in 7075-T6 Under Biaxial and Uniaxial Fatigue with Different Phases

    Science.gov (United States)

    2015-09-17

    CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH DIFFERENT PHASES... CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH DIFFERENT PHASES THESIS...UNLIMITED AFIT-ENY-MS-15-S-065 CORROSION FATIGUE CRACK GROWTH BEHAVIOR AT NOTCHED HOLE IN 7075-T6 UNDER BIAXIAL AND UNIAXIAL FATIGUE WITH

  13. EFFECTS OF CHEMISTRY AND OTHER VARIABLES ON CORROSION AND STRESS CORROSION CRACKING IN HANFORD DOUBLE SHELL TANKS

    Energy Technology Data Exchange (ETDEWEB)

    BROWN MH

    2008-11-13

    Laboratory testing was performed to develop a comprehensive understanding of the corrosivity of the tank wastes stored in Double-Shell Tanks using simulants primarily from Tanks 241-AP-105, 241-SY-103 and 241-AW-105. Additional tests were conducted using simulants of the waste stored in 241-AZ-102, 241-SY-101, 241-AN-107, and 241-AY-101. This test program placed particular emphasis on defining the range of tank waste chemistries that do not induce the onset of localized forms of corrosion, particularly pitting and stress corrosion cracking. This document summarizes the key findings of the research program.

  14. Tensile stress corrosion cracking of type 304 stainless steel irradiated to very high dose

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Ruther, W. E.; Strain, R. V.; Shack, W. J.

    2001-09-01

    Certain safety-related core internal structural components of light water reactors, usually fabricated from Type 304 or 316 austenitic stainless steels (SSs), accumulate very high levels of irradiation damage (20--100 displacement per atom or dpa) by the end of life. The data bases and mechanistic understanding of, the degradation of such highly irradiated components, however, are not well established. A key question is the nature of irradiation-assisted intergranular cracking at very high dose, i.e., is it purely mechanical failure or is it stress-commotion cracking? In this work, hot-cell tests and microstructural characterization were performed on Type 304 SS from the hexagonal fuel can of the decommissioned EBR-11 reactor after irradiation to {approximately}50 dpa at {approximately}370 C. Slow-strain-rate tensile tests were conducted at 289 C in air and in water at several levels of electrochemical potential (ECP), and microstructural characteristics were analyzed by scanning and transmission electron microcopies. The material deformed significantly by twinning and exhibited surprisingly high ductility in air, but was susceptible to severe intergranular stress corrosion cracking (IGSCC) at high ECP. Low levels of dissolved O and ECP were effective in suppressing the susceptibility of the heavily irradiated material to IGSCC, indicating that the stress corrosion process associated with irradiation-induced grain-boundary Cr depletion, rather than purely mechanical separation of grain boundaries, plays the dominant role. However, although IGSCC was suppressed, the material was susceptible to dislocation channeling at low ECP, and this susceptibility led to poor work-hardening capability and low ductility.

  15. Environmental Cracking of Corrosion Resistant Alloys in the Chemical Process Industry - A Review

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B

    2006-12-04

    A large variety of corrosion resistant alloys are used regularly in the chemical process industry (CPI). The most common family of alloys include the iron (Fe)-based stainless steels, nickel (Ni) alloys and titanium (Ti) alloys. There also other corrosion resistant alloys but their family of alloys is not as large as for the three groups mentioned above. All ranges of corrosive environments can be found in the CPI, from caustic solutions to hot acidic environments, from highly reducing to highly oxidizing. Stainless steels are ubiquitous since numerous types of stainless steels exist, each type tailored for specific applications. In general, stainless steels suffer stress corrosion cracking (SCC) in hot chloride environments while high Ni alloys are practically immune to this type of attack. High nickel alloys are also resistant to caustic cracking. Ti alloys find application in highly oxidizing solutions. Solutions containing fluoride ions, especially acid, seem to be aggressive to almost all corrosion resistant alloys.

  16. Film-induced stress enhancing stress corrosion cracking of austenitic stainless steel

    Institute of Scientific and Technical Information of China (English)

    李金许; 陈浩; 王燕斌; 乔利杰; 褚武扬

    2001-01-01

    A constant deflection device designed for use within a transmission electron microscopy (TEM) was used to investigate the change in dislocation configuration ahead of a crack tip during stress corrosion cracking (SCC) of type 310 austenitic stainless steel in a boiling MgCl2 solution, and the initiation process of stress corrosion microcrack. Results showed that corrosion process during SCC enhanced dislocation emission, multiplication and motion. Microcracks of SCC were initiated when the corrosion-enhanced dislocation emission and motion reached critical state.   A passive film formed during corrosion of austenitic stainless steel in the boiling MgCl2 solution generated a tensile stress. During SCC, the additive tensile stress generated at the metal/passive film interface helps enhance dislocation emission and motion.

  17. Development of Fatigue and Crack Propagation Design and Analysis Methodology in a Corrosive Environment for Typical Mechanically-Fastened Joints. Volume 3. Phase II Documentation.

    Science.gov (United States)

    1984-10-01

    Schaum Publishing Co., New York, 1961, pp. 241-268. 79. J. R. Benjamin and C. A. Cornell, Probability, Statis- -* tics, and Decision for Civil... chemistry , and Engineering, ASTM STP 801, 1983, pp. 405-422. 116. T. T. Shih and R. P. Wei, "Influences of Chemical and Thermal Environments on Delay in...K-0004, November, 1984. 120. R. P. Wei, P. S. Pao, R. G. Hart, T. W. Weir and G. W. Simmons, "Fracture Mechanics and Surface Chemistry Studies of

  18. Relationship between localized strain and irradiation assisted stress corrosion cracking in an austenitic alloy

    Energy Technology Data Exchange (ETDEWEB)

    McMurtrey, M.D., E-mail: mdmcm@umich.edu [Department of Nuclear Engineering and Radiological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States); Was, G.S. [Department of Nuclear Engineering and Radiological Sciences, University of Michigan, Ann Arbor, MI 48109 (United States); Patrick, L.; Farkas, D. [Department of Materials Science and Engineering, Virginia Tech, Blacksburg, VA 24061 (United States)

    2011-04-25

    Research highlights: {yields} Austenitic steel is more susceptible to intergranular corrosion after irradiation. {yields} Simulation and experiment used to study cracking in irradiated austentic steel. {yields} Cracking occurs at random high angle boundaries normal to the tensile stress. {yields} Cracking at boundaries with high normal stress and inability to accommodate strain. {yields} Boundary type, angle, and Taylor and Schmid factors affect strain accommodation. - Abstract: Irradiation assisted stress corrosion cracking may be linked to the local slip behavior near grain boundaries that exhibit high susceptibility to cracking. Fe-13Cr-15Ni austenitic steel was irradiated with 2 MeV protons at 360 deg. C to 5 dpa and strained in 288 deg. C simulated BWR conditions. Clusters of grains from the experiment were created in an atomistic simulation and then virtually strained using molecular dynamic simulation techniques. Cracking and grain orientation data were characterized in both the experiment and the simulation. Random high angle boundaries with high surface trace angles with respect to the tensile direction were found to be the most susceptible to cracking. Grain boundary cracking susceptibility was also found to correlate strongly with slip continuity, indicating that the strain accommodation at the boundary is related to cracking resistance. Higher cracking susceptibility was also found at grain boundaries adjacent to grains with low Schmid factor or high Taylor factor. The basic trends reported here are supported by both the experiments and the simulations.

  19. Mechanisms and Kinetics of Environmentally Assisted Cracking: Current Status, Issues, and Suggestions for Further Work

    Science.gov (United States)

    Lynch, S. P.

    2013-03-01

    Mechanisms and kinetics of metal-induced embrittlement, hydrogen-embrittlement, and stress-corrosion cracking are discussed, and long-standing controversies are addressed by reviewing critical observations. Recommendations are also made regarding further work (including repetition of previous work using more advanced measurement and characterisation techniques) that should be carried out in order to resolve some of the contentious issues. The evidence to date suggests that adsorption-based mechanisms, involving weakening of substrate interatomic bonds so that dislocation emission or decohesion is facilitated, accounts for embrittlement in many systems. Embrittling adsorbed species include some metal atoms, hydrogen, and complex ions produced by de-alloying. Other viable mechanisms of embrittlement include those based on (1) dissolution of anodic grain-boundary regions, and (2) decohesion at grain boundaries owing to segregated hydrogen and impurities. The hydrogen-enhanced localised-plasticity mechanism, based on solute hydrogen facilitating dislocation activity in the plastic zone ahead of cracks, makes a contribution in some cases, but is relatively unimportant compared with these other mechanisms for most fracture modes. The film-induced cleavage mechanism, proposed especially for stress-corrosion cracking in systems involving de-alloying at crack tips, is questionable on numerous grounds, and is probably not viable. Rate-controlling processes for environmentally assisted cracking are not well established, except for solid-metal induced embrittlement where surface self-diffusion of embrittling atoms to crack tips controls cracking kinetics. In some systems, adsorption kinetics are probably rate-controlling for liquid-metal embrittlement, hydrogen-environment embrittlement, and stress-corrosion cracking. In other cases, rate-controlling processes could include the rate of anodic or cathodic reactions at and behind crack tips (responsible for producing embrittling

  20. INVESTIGATION OF THE POTENTIAL FOR CAUSTIC STRESS CORROSION CRACKING OF A537 CARBON STEEL NUCLEAR WASTE TANKS

    Energy Technology Data Exchange (ETDEWEB)

    Lam, P.

    2009-10-15

    The evaporator recycle streams contain waste in a chemistry and temperature regime that may be outside of the current waste tank corrosion control program, which imposes temperature limits to mitigate caustic stress corrosion cracking (CSCC). A review of the recent service history (1998-2008) of Tanks 30 and 32 showed that these tanks were operated in highly concentrated hydroxide solution at high temperature. Visual inspections, experimental testing, and a review of the tank service history have shown that CSCC has occurred in uncooled/un-stress relieved F-Area tanks. Therefore, for the Type III/IIIA waste tanks the efficacy of the stress relief of welding residual stress is the only corrosion-limiting mechanism. The objective of this experimental program is to test carbon steel small scale welded U-bend specimens and large welded plates (12 x 12 x 1 in.) in a caustic solution with upper bound chemistry (12 M hydroxide and 1 M each of nitrate, nitrite, and aluminate) and temperature (125 C). These conditions simulate worst-case situations in Tanks 30 and 32. Both as-welded and stress-relieved specimens have been tested. No evidence of stress corrosion cracking was found in the U-bend specimens after 21 days of testing. The large plate test is currently in progress, but no cracking has been observed after 9 weeks of immersion. Based on the preliminary results, it appears that the environmental conditions of the tests are unable to develop stress corrosion cracking within the duration of these tests.

  1. Development of chloride-induced corrosion in pre-cracked RC beams under sustained loading: Effect of load-induced cracks, concrete cover, and exposure conditions

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Linwen [Université de Toulouse, UPS, INSA, LMDC, Toulouse (France); Université de Sherbrooke, Quebec (Canada); François, Raoul, E-mail: raoul.francois@insa-toulouse.fr [Université de Toulouse, UPS, INSA, LMDC, Toulouse (France); Dang, Vu Hiep [Hanoi Architectural University, Faculty of Civil Engineering, Hanoi (Viet Nam); L' Hostis, Valérie [CEA Saclay, CEA, DEN, DPC, SECR, Laboratoire d' Etude du Comportement des Bétons et des Argiles, Gif-sur-Yvette (France); Gagné, Richard [Université de Sherbrooke, Quebec (Canada)

    2015-01-15

    This paper deals with corrosion initiation and propagation in pre-cracked reinforced concrete beams under sustained loading during exposure to a chloride environment. Specimen beams that were cast in 2010 were compared to specimens cast in 1984. The only differences between the two sets of beams were the casting direction in relation to tensile reinforcement and the exposure conditions in the salt-fog chamber. The cracking maps, corrosion maps, chloride profiles, and cross-sectional loss of one group of two beams cast in 2010 were studied and their calculated corrosion rates were compared to that of beams cast in 1984 in order to investigate the factors influencing the natural corrosion process. Experimental results show that, after rapid initiation of corrosion at the crack tip, the corrosion process practically halted and the time elapsing before corrosion resumed depended on the exposure conditions and cover depth.

  2. Pacific Northwest National Laboratory Investigation of the Stress Corrosion Cracking in Nickel-Base Alloys, Volume 2

    Energy Technology Data Exchange (ETDEWEB)

    Bruemmer, Stephen M.; Toloczko, Mychailo B.; Olszta, Matthew J.

    2012-03-01

    The objective of this program is to evaluate the primary water stress corrosion cracking (PWSCC) susceptibility of high chromium alloy 690 and its weld metals, establish quantitative measurements of crack-growth rates and determine relationships among cracking susceptibility, environmental conditions and metallurgical characteristics. Stress-corrosion, crack-growth rates have been determined for 12 alloy 690 specimens, 11 alloy 152/52/52M weld metal specimens, 4 alloy 52M/182 overlay specimens and 2 alloy 52M/82 inlay specimens in simulated PWR primary water environments. The alloy 690 test materials included three different heats of extruded control-rod-drive mechanism (CRDM) tubing with variations in the initial material condition and degree of cold work for one heat. Two cold-rolled (CR) alloy 690 plate heats were also obtained and evaluated enabling comparisons to the CR CRDM materials. Weld metal, overlay and inlay specimens were machined from industry mock ups to provide plant-representative materials for testing. Specimens have been tested for one alloy 152 weld, two alloy 52 welds and three alloy 52M welds. The overlay and inlay specimens were prepared to propagate stress-corrosion cracks from the alloy 182 or 82 material into the more resistant alloy 52M. In all cases, crack extension was monitored in situ by direct current potential drop (DCPD) with length resolution of about +1 µm making it possible to measure extremely low growth rates approaching 5x10-10 mm/s. Most SCC tests were performed at 325-360°C with hydrogen concentrations from 11-29 cc/kg; however, environmental conditions were modified during a few experiments to evaluate the influence of temperature, water chemistry or electrochemical potential on propagation rates. In addition, low-temperature (~50°C) cracking behavior was examined for selected alloy 690 and weld metal specimens. Extensive characterizations have been performed on material microstructures and stress-corrosion cracks by

  3. Numerical investigation on stress corrosion cracking behavior of dissimilar weld joints in pressurized water reactor plants

    Directory of Open Access Journals (Sweden)

    Lingyan Zhao

    2014-07-01

    Full Text Available There have been incidents recently where stress corrosion cracking (SCC observed in the dissimilar metal weld (DMW joints connecting the reactor pressure vessel (RPV nozzle with the hot leg pipe. Due to the complex microstructure and mechanical heterogeneity in the weld region, dissimilar metal weld joints are more susceptible to SCC than the bulk steels in the simulated high temperature water environment of pressurized water reactor (PWR. Tensile residual stress (RS, in addition to operating loads, has a great contribution to SCC crack growth. Limited experimental conditions, varied influence factors and diverging experimental data make it difficult to accurately predict the SCC behavior of DMW joints with complex geometry, material configuration, operating loads and crack shape. Based on the film slip/dissolution oxidation model and elastic-plastic finite element method (EPFEM, an approach is developed to quantitatively predict the SCC growth rate of a RPV outlet nozzle DMW joint. Moreover, this approach is expected to be a pre-analytical tool for SCC experiment of DMW joints in PWR primary water environment.

  4. Review on Stress Corrosion and Corrosion Fatigue Failure of Centrifugal Compressor Impeller

    Institute of Scientific and Technical Information of China (English)

    SUN Jiao; CHEN Songying; QU Yanpeng; LI Jianfeng

    2015-01-01

    Corrosion failure, especially stress corrosion cracking and corrosion fatigue, is the main cause of centrifugal compressor impeller failure. And it is concealed and destructive. This paper summarizes the main theories of stress corrosion cracking and corrosion fatigue and its latest developments, and it also points out that existing stress corrosion cracking theories can be reduced to the anodic dissolution (AD), the hydrogen-induced cracking (HIC), and the combined AD and HIC mechanisms. The corrosion behavior and the mechanism of corrosion fatigue in the crack propagation stage are similar to stress corrosion cracking. The effects of stress ratio, loading frequency, and corrosive medium on the corrosion fatigue crack propagation rate are analyzed and summarized. The corrosion behavior and the mechanism of stress corrosion cracking and corrosion fatigue in corrosive environments, which contain sulfide, chlorides, and carbonate, are analyzed. The working environments of the centrifugal compressor impeller show the behavior and the mechanism of stress corrosion cracking and corrosion fatigue in different corrosive environments. The current research methods for centrifugal compressor impeller corrosion failure are analyzed. Physical analysis, numerical simulation, and the fluid-structure interaction method play an increasingly important role in the research on impeller deformation and stress distribution caused by the joint action of aerodynamic load and centrifugal load.

  5. Stress corrosion cracking of welded joints of super-martensitic stainless steel in H{sub 2}S free environment

    Energy Technology Data Exchange (ETDEWEB)

    Hoerner, Bertrand; Bayle, Bernard; Delafosse, David [Centre Science des Materiaux et des Structures - URA CNRS 5146, ENS Mines de Saint-Etienne, 158 Cours Fauriel, 42023 Saint-Etienne cedex 02 (France); Ligier, Vincent [CRMC, INDUSTEEL Creusot, 56, rue Clemenceau, BP 56 - 71 202 Le Creusot Cedex (France)

    2004-07-01

    Due to their combination of good weldability and good mechanical properties, low carbon super-martensitic stainless steels are good candidates for oil and gas flow line applications. These alloys have already been used in slightly sour environments containing chlorides, CO{sub 2} and H{sub 2}S. The properties of a welded joint whose composition is matching or superduplex that of the base metal are investigated. The base material is the super-martensitic stainless steels medium alloy: 13Cr-4.5Ni-1.5Mo. The Heat Affected Zone (HAZ) of girth welds may be sensitive to stress corrosion cracking and presents distinct features intergranular cracking when tested in four-point bending in a sour deaerated environment at temperatures around 100 deg. C. The electrochemical properties of the medium alloy and the matching welded joint + HAZ were determined in a chloride-containing environment without H{sub 2}S. A passive film is formed on polished samples. This film is less protective for the welded joint + HAZ samples than in the base metal. Moreover, the pitting corrosion resistance is strongly decreased in the HAZ. Slow strain rate tensile tests were conducted in a de-aerated solution without H{sub 2}S. They reproduce the same type of cracking as was observed in four point bending tests in a sour environment: initiation in the HAZ and an intergranular crack with a very brittle aspect and no significant trace of corrosion. The presence H{sub 2}S is not the prevailing factor for the occurrence of cracking. Furthermore, it is not necessary to have a specific surface condition for crack initiation to occur in slow strain rate tension, as it is the case four point bend tests where initiation appears to be controlled by the surface condition (chemical and / or geometrical). Finally, a simulated PWHT strongly increase the resistance to SSC. (authors)

  6. Influence of nitrogen on the stress corrosion cracking resistance of austenitic stainless steels in chloride environment; Influence de l'azote sur la resistance a la corrosion sous contrainte d'aciers inoxydables austenitiques en milieu chlorure

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, S

    2001-11-01

    The aim of this study is to investigate the influence of nitrogen additions on the Stress Corrosion Cracking (SSC) resistance of austenitic stainless steel in chloride environment. The investigation was carried out in two part: first, an experimental investigation with model industrial steels was carried out and secondly, numerical simulations based on the Corrosion Enhanced Plasticity Model were developed. Both slow strain rate tensile tests and constant load test of the different steels in boiling MgCl{sub 2} (153 deg C) at free potential show that, for a given plastic strain rate, nitrogen addition increases the critical stress for crack initiation without influencing the crack propagation rate. We observed that the creep rate under constant load was affected by the nitrogen content. As a consequence, the SCC behaviour (cracks density and propagation rate) depends on the nitrogen content. We thus confirm that the nitrogen content influences the corrosion - deformation interaction mechanisms via its positive contribution to the flow stress. These experimental results are reproduced semi-quantitatively by means of numerical simulations at the scale of crack. - dislocation interactions. The presence of nitrogen is modelled by an increased lattice friction stress, which in turn affects the dynamics of crack tip shielding by dislocation pile-ups. We conclude that nitrogen addition in austenitic stainless steels increases the SC crack initiation stress in proportion of the increased flow stress, without penalty in terms of SC crack propagation rate. (author)

  7. Analysis of stress corrosion cracking in alloy 718 following commercial reactor exposure

    Science.gov (United States)

    Leonard, Keith J.; Gussev, Maxim N.; Stevens, Jacqueline N.; Busby, Jeremy T.

    2015-11-01

    Alloy 718 is generally considered a highly corrosion-resistant material but can still be susceptible to stress corrosion cracking (SCC). The combination of factors leading to SCC susceptibility in the alloy is not always clear enough. In the present work, alloy 718 leaf spring (LS) materials that suffered stress corrosion damage during two 24-month cycles in pressurized water reactor service, operated to >45 MWd/mtU burn-up, was investigated. Compared to archival samples fabricated through the same processing conditions, little microstructural and property changes occurred in the material with in-service irradiation, contrary to high dose rate laboratory-based experiments reported in literature. Though the lack of delta phase formation along grain boundaries would suggest a more SCC resistant microstructure, grain boundary cracking in the material was extensive. Crack propagation routes were explored through focused ion beam milling of specimens near the crack tip for transmission electron microscopy as well as in polished plan view and cross-sectional samples for electron backscatter diffraction analysis. It has been shown in this study that cracks propagated mainly along random high-angle grain boundaries, with the material around cracks displaying a high local density of dislocations. The slip lines were produced through the local deformation of the leaf spring material above their yield strength. The cause for local SCC appears to be related to oxidation of both slip lines and grain boundaries, which under the high in-service stresses resulted in crack development in the material.

  8. Corrosion Behavior of Steel Reinforcement in Concrete with Recycled Aggregates, Fly Ash and Spent Cracking Catalyst

    Directory of Open Access Journals (Sweden)

    Hebé Gurdián

    2014-04-01

    Full Text Available The main strategy to reduce the environmental impact of the concrete industry is to reuse the waste materials. This research has considered the combination of cement replacement by industrial by-products, and natural coarse aggregate substitution by recycled aggregate. The aim is to evaluate the behavior of concretes with a reduced impact on the environment by replacing a 50% of cement by industrial by-products (15% of spent fluid catalytic cracking catalyst and 35% of fly ash and a 100% of natural coarse aggregate by recycled aggregate. The concretes prepared according to these considerations have been tested in terms of mechanical strengths and the protection offered against steel reinforcement corrosion under carbonation attack and chloride-contaminated environments. The proposed concrete combinations reduced the mechanical performance of concretes in terms of elastic modulus, compressive strength, and flexural strength. In addition, an increase in open porosity due to the presence of recycled aggregate was observed, which is coherent with the changes observed in mechanical tests. Regarding corrosion tests, no significant differences were observed in the case of the resistance of these types of concretes under a natural chloride attack. In the case of carbonation attack, although all concretes did not stand the highly aggressive conditions, those concretes with cement replacement behaved worse than Portland cement concretes.

  9. Interplay of microbiological corrosion and alloy microstructure in stress corrosion cracking of weldments of advanced stainless steels

    Indian Academy of Sciences (India)

    R K Singh Raman

    2003-06-01

    This paper presents an overview of the phenomenon of stress corrosion cracking (SCC) of duplex stainless steels and their weldments in marine environments and the potential role of microbial activity in inducing SCC susceptibility. As a precursor to the topic the paper also reviews the performance of the traditional corrosion-resistant alloys and their weldments and the necessity of using duplex stainless steels (DSS), in order to alleviate corrosion problems in marine environments. Given that the performance of weldments of such steels is often unsatisfactory, this review also assesses the research needs in this area. In this context the paper also discusses the recent reports on the role of microorganisms in inducing hydrogen embrittlements and corrosion fatigue.

  10. Modeling the Time-to Corrosion Cracking of the Cover Concrete in Chloride Contaminated Reinforced Concrete Structures

    OpenAIRE

    Liu, Youping

    1996-01-01

    Significant factors on steel corrosion in chloride contaminated reinforced concrete and time-to-corrosion cracking were investigated in this study. Sixty specimens were designed with seven admixed chloride contents, three concrete cover depths, two reinforcing steel bar diameters, two exposure conditions, and a typical concrete with water to cement ratio of 0.45. Corrosion current density (corrosion rate), corrosion potential, ohmic resistance of concrete and temperature were measured monthly...

  11. Modelling of iodine-induced stress corrosion cracking in CANDU fuel

    Science.gov (United States)

    Lewis, B. J.; Thompson, W. T.; Kleczek, M. R.; Shaheen, K.; Juhas, M.; Iglesias, F. C.

    2011-01-01

    Iodine-induced stress corrosion cracking (I-SCC) is a recognized factor for fuel-element failure in the operation of nuclear reactors requiring the implementation of mitigation measures. I-SCC is believed to depend on certain factors such as iodine concentration, oxide layer type and thickness on the fuel sheath, irradiation history, metallurgical parameters related to sheath like texture and microstructure, and the mechanical properties of zirconium alloys. This work details the development of a thermodynamics and mechanistic treatment accounting for the iodine chemistry and kinetics in the fuel-to-sheath gap and its influence on I-SCC phenomena. The governing transport equations for the model are solved with a finite-element technique using the COMSOL Multiphysics® commercial software platform. Based on this analysis, this study also proposes potential remedies for I-SCC.

  12. Localized Deformation as a Primary Cause of Irradiation Assisted Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Gary S. Was

    2009-03-31

    The objective of this project is to determine whether deformation mode is a primary factor in the mechanism of irradiation assisted intergranular stress corrosion cracking of austenitic alloys in light watert reactor core components. Deformation mode will be controlled by both the stacking fault energy of the alloy and the degree of irradiation. In order to establish that localized deformation is a major factor in IASCC, the stacking fault energies of the alloys selected for study must be measured. Second, it is completely unknown how dose and SFE trade-off in terms of promoting localized deformation. Finally, it must be established that it is the localized deformation, and not some other factor that drives IASCC.

  13. Researches on corrosion cracking phenomenonthat occurs on welded of agricultural equipment

    Directory of Open Access Journals (Sweden)

    I. Sărăcin

    2015-04-01

    Full Text Available Welded construction equipments for agriculture are strongly stressed in terms of mechanics, but also in terms of environmental action and thus in many cases appears their wear by corrosion cracking phenomenon. After research it was noted that after a certain period of use of equipment, metallographic structure of welded steel structures has changed substantially and at the same time a change in the chemical composition of steel was also observed. In terms of chemical composition a reduction in carbon content was mainly observed, and an increase in sulfur content,determined mainly by the presence of large quantities of sulfur in the atmosphere. This sulfur in the atmosphere at the same time determines the acid action on metallic materials, by forming with water from precipitation of H2S.

  14. Mechanisms of metal dusting corrosion

    DEFF Research Database (Denmark)

    Hummelshøj, Thomas Strabo

    In this thesis the early stages of metal dusting corrosion is addressed; the development of carbon expanded austenite, C, and the decomposition hereof into carbides. Later stages of metal dusting corrosion are explored by a systematic study of stainless steel foils exposed to metal dusting...... influence of oxygen and carbon on the metal dusting corrosion is explored. The results indicate that exposure to metal dusting conditions have a detrimental effect on the resistance against oxidation and, conversely, that exposure to oxidation has a detrimental effect on the resistance towards metal dusting....... Consequently, a combination of carburizing and oxidizing conditions has a strong mutual catalyzing effect on the metal dusting corrosion....

  15. The Effect of Welding Residual Stress for Making Artificial Stress Corrosion Crack in the STS 304 Pipe

    Directory of Open Access Journals (Sweden)

    Jae-Seong Kim

    2015-01-01

    Full Text Available The stress corrosion crack is one of the fracture phenomena for the major structure components in nuclear power plant. During the operation of a power plant, stress corrosion cracks are initiated and grown especially in dissimilar weldment of primary loop components. In particular, stress corrosion crack usually occurs when the following three factors exist at the same time: susceptible material, corrosive environment, and tensile stress (residual stress included. Thus, residual stress becomes a critical factor for stress corrosion crack when it is difficult to improve the material corrosivity of the components and their environment under operating conditions. In this study, stress corrosion cracks were artificially produced on STS 304 pipe itself by control of welding residual stress. We used the instrumented indentation technique and 3D FEM analysis (using ANSYS 12 to evaluate the residual stress values in the GTAW area. We used the custom-made device for fabricating the stress corrosion crack in the inner STS 304 pipe wall. As the result of both FEM analysis and experiment, the stress corrosion crack was quickly generated and could be reproduced, and it could be controlled by welding residual stress.

  16. Stress-Corrosion Cracking of Metallic Materials. Part III. Hydrogen Entry and Embrittlement in Steel

    Science.gov (United States)

    1975-04-01

    Strength Steels," Stress Corrosion Cracking in High-Strength Steels and in Titanium and Altuninum Alloys, Naval Rasearch Laboratory, Washington, D.C...to pickling solutions. In all of these examples, the sulfide, cyanide, etc., caused a hydrogen-related problem that would not have existed in their...desorption reaction. In studying the pickling of low-carbon steel in various strong acids, Hudson’ 4 measured the corrosion rate and amount of hydr-ogen

  17. Probabilistic Lifetime Assessment of Marine Reinforced Concrete with Steel Corrosion and Cover Cracking

    Institute of Scientific and Technical Information of China (English)

    LU Chun-hua; JIN Wei-liang; LIU Rong-gui

    2011-01-01

    In order to study the durability behavior of marine reinforced concrete structure suffering from chloride attack, the structural service life is assumed to be divided into three critical stages, which can be characterized by steel corrosion and cover cracking. For each stage, a calculated model used to predict the lifetime is developed. Based on the definition of durability limit state, a probabilistic lifetime model and its time-dependent reliability analytical method are proposed considering the random natures of influencing factors. Then, the probabilistic lifetime prediction models are applied to a bridge pier located in the Hangzhou Bay with Monte Carlo simulation. It is found that the time to corrosion initiation to follows a lognonnal distribution, while that the time from corrosion initiation to cover cracking t and the time for crack to develop from hairline crack to a limit crack width t can be described by Weibull distributions. With the permitted failure probability of 5.0%, it is also observed that the structural durability lifetime mainly depends on the durability life to and that the percentage of participation of tbe life t to the total service life grows from 61.5% to 83.6% when the cover thickness increases from 40 mm to 80 mm. Therefore, for any part of the marine RC bridge, the lifetime predictions and maintenance efforts should also be directed toward controlling the stage of corrosion initiation induced by chloride ion.

  18. Modeling time-dependent corrosion fatigue crack propagation in 7000 series aluminum alloys

    Science.gov (United States)

    Mason, Mark E.; Gangloff, Richard P.

    1994-01-01

    Stress corrosion cracking and corrosion fatigue experiments were conducted with the susceptible S-L orientation of AA7075-T651, immersed in acidified and inhibited NaCl solution, to provide a basis for incorporating environmental effects into fatigue crack propagation life prediction codes such as NASA FLAGRO. This environment enhances da/dN by five to ten-fold compared to fatigue in moist air. Time-based crack growth rates from quasi-static load experiments are an order of magnitude too small for accurate linear superposition prediction of da/dN for loading frequencies above 0.001 Hz. Alternate methods of establishing da/dt, based on rising-load or ripple-load-enhanced crack tip strain rate, do not increase da/dt and do not improve linear superposition. Corrosion fatigue is characterized by two regimes of frequency dependence; da/dN is proportional to f(exp -1) below 0.001 Hz and to F(exp 0) to F(exp -0.1) for higher frequencies. Da/dN increases mildly both with increasing hold-time at K(sub max) and with increasing rise-time for a range of loading waveforms. The mild time-dependence is due to cycle-time-dependent corrosion fatigue growth. This behavior is identical for S-L nd L-T crack orientations. The frequency response of environmental fatigue in several 7000 series alloys is variable and depends on undefined compositional or microstructural variables. Speculative explanations are based on the effect of Mg on occluded crack chemistry and embritting hydrogen uptake, or on variable hydrogen diffusion in the crack tip process zone. Cracking in the 7075/NaCl system is adequately described for life prediction by linear superposition for prolonged load-cycle periods, and by a time-dependent upper bound relationship between da/dN and delta K for moderate loading times.

  19. Study of the Effect of Swelling on Irradiation Assisted Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, Sebastien Paul [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2016-09-01

    This report describes the methodology used to study the effect of swelling on the crack growth rate of an irradiation-assisted stress corrosion crack that is propagating in highly irradiated stainless steel 304 material irradiated to 33 dpa in the Experimental Breeder Reactor-II. The material selection, specimens design, experimental apparatus and processes are described. The results of the current test are presented.

  20. The susceptibility of 90Cu-10Ni alloy to stress corrosion cracking in seawater polluted by sulfide ions

    Science.gov (United States)

    Domiaty, A. El; Alhajji, J. N.

    1997-08-01

    Electrochemical polarization measurements and slow strain rate tests (SSRT) of a 90Cu-10Ni alloy in highly sulfide polluted seawater were conducted to investigate stress-corrosion cracking (SCC) behavior. The severity of the SCC depends on the sulfide concentration in the seawater. The severity increases as the concentration increases. Because the major time in SCC is spent in the initiation process of the propagating crack, the fracture toughness has only a minor effect in the component life failed by SCC. The SCC behavior of CDA706 is strictly linked to sulfide concentration in the range of 100 to 1000 ppm. The general corrosion of Cu-Ni alloys in low (100 ppm) sulfide polluted seawater increases due to the selective copper dissolution. Cyclic polarization measurements confirmed that the corrosion rate decreases slightly as the sulfide concentration increases. Pitting tendency was high in the low concentration range of sulfide and low in the high concentration range. The presence of stresses in SCC removes the protective layer as it increases during testing of the specimen or during the actual service of a component. The authors propose that film rupture occurred, and two proposed SCC mechanisms were operational, namely sulfide stress cracking associated with the anodic dissolution in the low sulfide concentration range and hydrogen embrittlement, which was dominant in the high sulfide concentration range. It was found that a synergism exists between sulfide and stress that enhances the effect of the latter.

  1. Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2

    Science.gov (United States)

    Ly, Thuc Hue; Zhao, Jiong; Cichocka, Magdalena Ola; Li, Lain-Jong; Lee, Young Hee

    2017-01-01

    Whether and how fracture mechanics needs to be modified for small length scales and in systems of reduced dimensionality remains an open debate. Here, employing in situ transmission electron microscopy, atomic structures and dislocation dynamics in the crack tip zone of a propagating crack in two-dimensional (2D) monolayer MoS2 membrane are observed, and atom-to-atom displacement mapping is obtained. The electron beam is used to initiate the crack; during in situ observation of crack propagation the electron beam effect is minimized. The observed high-frequency emission of dislocations is beyond previous understanding of the fracture of brittle MoS2. Strain analysis reveals dislocation emission to be closely associated with the crack propagation path in nanoscale. The critical crack tip plastic zone size of nearly perfect 2D MoS2 is between 2 and 5 nm, although it can grow to 10 nm under corrosive conditions such as ultraviolet light exposure, showing enhanced dislocation activity via defect generation.

  2. Dynamical observations on the crack tip zone and stress corrosion of two-dimensional MoS2

    KAUST Repository

    Ly, Thuc Hue

    2017-01-18

    Whether and how fracture mechanics needs to be modified for small length scales and in systems of reduced dimensionality remains an open debate. Here, employing in situ transmission electron microscopy, atomic structures and dislocation dynamics in the crack tip zone of a propagating crack in two-dimensional (2D) monolayer MoS2 membrane are observed, and atom-to-atom displacement mapping is obtained. The electron beam is used to initiate the crack; during in situ observation of crack propagation the electron beam effect is minimized. The observed high-frequency emission of dislocations is beyond previous understanding of the fracture of brittle MoS2. Strain analysis reveals dislocation emission to be closely associated with the crack propagation path in nanoscale. The critical crack tip plastic zone size of nearly perfect 2D MoS2 is between 2 and 5 nm, although it can grow to 10 nm under corrosive conditions such as ultraviolet light exposure, showing enhanced dislocation activity via defect generation.

  3. STRESS CORROSION CRACKING SUSCEPTIBILITY OF HIGH LEVEL WASTE TANKS DURING SLUDGE MASS REDUCTION

    Energy Technology Data Exchange (ETDEWEB)

    Subramanian, K

    2007-10-18

    Aluminum is a principal element in alkaline nuclear sludge waste stored in high level waste (HLW) tanks at the Savannah River Site. The mass of sludge in a HLW tank can be reduced through the caustic leaching of aluminum, i.e. converting aluminum oxides (gibbsite) and oxide-hydroxides (boehmite) into soluble hydroxides through reaction with a hot caustic solution. The temperature limits outlined by the chemistry control program for HLW tanks to prevent caustic stress corrosion cracking (CSCC) in concentrated hydroxide solutions will potentially be exceeded during the sludge mass reduction (SMR) campaign. Corrosion testing was performed to determine the potential for CSCC under expected conditions. The experimental test program, developed based upon previous test results and expected conditions during the current SMR campaign, consisted of electrochemical and mechanical testing to determine the susceptibility of ASTM A516 carbon steel to CSCC in the relevant environment. Anodic polarization test results indicated that anodic inhibition at the temperatures and concentrations of interest for SMR is not a viable, consistent technical basis for preventing CSCC. However, the mechanical testing concluded that CSCC will not occur under conditions expected during SMR for a minimum of 35 days. In addition, the stress relief for the Type III/IIIA tanks adds a level of conservatism to the estimates. The envelope for corrosion control is recommended during the SMR campaign is shown in Table 1. The underlying assumption is that solution time-in-tank is limited to the SMR campaign. The envelope recommends nitrate/aluminate intervals for discrete intervals of hydroxide concentrations, although it is recognized that a continuous interval may be developed. The limits also sets temperature limits.

  4. Hydrogen cracking and stress corrosion of pipeline steels. Contribution of the cracking mechanisms study to the understanding of the in-service damage and to the definition of a ranking test; Fissuration assistee par l'hydrogene et corrosion sous contrainte des aciers de pipelines. Apports de l'etude des mecanismes de fissuration a la comprehension de l'endommagement de service et a la definition d'un test de classification

    Energy Technology Data Exchange (ETDEWEB)

    Le Friant, D.

    2000-12-19

    This work is based on the study of the cracking of a French oil transmission pipeline protected by a cathodic protection system. The objective is to identify field parameters, which contribute to the cracks propagation, and to assess changes in the operating conditions, which could lead to a mitigation of the phenomenon. We have focused on the study of the micro-mechanisms by means of slow strain rate tests. Then, cyclic loading tests were carried out to investigate cracks propagation mechanisms. Smooth and pre-notched specimens were tested at free and cathodic potential. Hydrogen is responsible for crack advance through changes in the local steels properties. Such effects take place when two phenomenons occur: favourable conditions for hydrogen entry and, a localisation of hydrogen and its effects. In particular, we have shown the essential role of a dynamic loading in promoting hydrogen entry into the steel (especially at the very crack tip). At cathodic potential, hydrogen-related effects are exacerbated by the presence of MnS inclusions which leads to the initiation of internal cracks (HIC) and to a SOHIC-like crack morphology. At free potential, the lesser amount of available hydrogen give localisation-related effects a greater importance. Cracking is then related to a hydrogen-induced SCC mechanism. Three parameters are involved in the field cracking: operating pressure variations, period of over-protection and a sensitive steels microstructure (MnS). Cathodic protection appears to be the most efficient field parameter to mitigate the phenomenon: it requires a better control of the polarisation level. Finally, a ranking test is outlined from the study of the cracking mechanisms. (author)

  5. Investigation into the stress corrosion cracking properties of AA2099, an aluminum-lithium-copper alloy

    Science.gov (United States)

    Padgett, Barbara Nicole

    Recently developed Al-Li-Cu alloys show great potential for implementation in the aerospace industry because of the attractive mix of good mechanical properties and low density. AA2099 is an Al-Li-Cu alloy with the following composition Al-2.69wt%Cu-1.8wt%Li-0.6wt%Zn-0.3wt%Mg-0.3wt%Mn-0.08wt%Zr. The environmental assisted cracking and localized corrosion behavior of the AA2099 was investigated in this thesis. The consequences of uncontrolled grain boundary precipitation via friction stir welding on the stress corrosion cracking (SCC) behavior of AA2099 was investigated first. Using constant extension rate testing, intergranular corrosion immersion experiments, and potentiodynamic scans, the heat-affected zone on the trailing edge of the weld (HTS) was determined to be most susceptible of the weld zones. The observed SCC behavior for the HTS was linked to the dissolution of an active phase (Al2CuLi, T1) populating the grain boundary. It should be stated that the SCC properties of AA2099 in the as-received condition were determined to be good. Focus was then given to the electrochemical behavior of precipitate phases that may occupy grain and sub-grain boundaries in AA2099. The grain boundary micro-chemistry and micro-electrochemistry have been alluded to within the literature as having significant influence on the SCC behavior of Al-Li-Cu alloys. Major precipitates found in this alloy system are T1 (Al 2CuLi), T2 (Al7.5Cu4Li), T B (Al6CuLi3), and theta (Al2 Cu). These phases were produced in bulk form so that the electrochemical nature of each phase could be characterized. It was determined T1 was most active electrochemically and theta was least. When present on grain boundaries in the alloy, electrochemical behavior of the individual precipitates aligned with the observed corrosion behavior of the alloy (e.g. TB was accompanied by general pitting corrosion and T 1 was accompanied by intergranular corrosion attack). In addition to the electrochemical behavior of

  6. Crack Tip Plasticity Associated with Corrosion Assisted Fatigue.

    Science.gov (United States)

    1982-11-15

    growing. The model presented is very similar to those previously developed by Antolovich , Saxena and I Chanani[83 and by Lanteigne and BailonE9] but...in crack tip plasticity associated with environment. The model used here is conceptually similar to those formulated by * Antolovich , et al,[ and...Lankford, J. ’Fatigue-Crack-Tip I Plastic Strains by the Stereoimaging Technique’ Exp. Mech. 1980 20, 3 134-139. 8. Antolovich , S. D., Saxena, A., and

  7. Effect of Nanostructure Changes on Stress Corrosion Cracking of Proton Irradiated Nuclear Energy Structural Materials

    Directory of Open Access Journals (Sweden)

    M.N. Lunika

    2011-01-01

    Full Text Available Austenitic stainless alloys are used extensively as structural materials in the internal components of light water reactor (LWR pressure vessels because of their relatively high strength, ductility, and fracture toughness. Irradiation-assisted stress corrosion cracking (IASCC is main degradation process that affects LWR internal components exposed to radiation. The existing data on proton irradiated austenitic alloys were reviewed to evaluate the effects of key parameters such as material composition, irradiation dose on IASCC susceptibility of these materials in LWR environments. The significance of deformation nanostructure and stacking fault energy (SFE changes in the material on IASCC susceptibility is also discussed. Results show that the IASCC susceptibility of the alloys increases with increasing irradiation dose and decreasing stacking fault energy. IASCC tends to initiate at locations where slip dislocation channels intersect grain boundaries. Localized deformation in the form of grain boundary sliding due to the interaction of slip channels and grain boundaries is likely the primary cause of the observed cracking initiation. It may play a key role in the underlying mechanism of IASCC in light water reactor core components.

  8. Fundamental understanding and life prediction of stress corrosion cracking in BWRs and energy systems

    Energy Technology Data Exchange (ETDEWEB)

    Andresen, P.L.; Ford, F.P. [General Electric, Schenectady, NY (United States). Corporate Research and Development Center

    1998-03-01

    The objective of this paper is to present an approach for design and lifetime evaluation of environmental cracking based on experimental and fundamental modeling of the underlying processes operative in crack advance. In detailed this approach and its development and quantification for energy (hot water) systems, the requirements for a life prediction methodology will be highlighted and the shortcomings of the existing design and lifetime evaluation codes reviewed. Examples are identified of its use in a variety of cracking systems, such as stainless steels, low alloy steels, nickel base alloys, and irradiation assisted stress corrosion cracking in boiling water reactor (BWR) water, as well as preliminary use for low alloy steel and Alloy 600 in pressurized water reactors (PWRs) and turbine steels in steam turbines. Identification of the common aspects with environmental cracking in other hot water systems provides a secure basis for its extension to related energy systems. 166 refs., 49 figs.

  9. The role of local strains from prior cold work on stress corrosion cracking of α-brass in Mattsson's solution

    Energy Technology Data Exchange (ETDEWEB)

    Ulaganathan, Jaganathan, E-mail: jagan.ulaganathan@mail.utoronto.ca; Newman, Roger C., E-mail: roger.newman@utoronto.ca

    2014-06-01

    The dynamic strain rate ahead of a crack tip formed during stress corrosion cracking (SCC) under a static load is assumed to arise from the crack propagation. The strain surrounding the crack tip would be redistributed as the crack grows, thereby having the effect of dynamic strain. Recently, several studies have shown cold work to cause accelerated crack growth rates during SCC, and the slip-dissolution mechanism has been widely applied to account for this via a supposedly increased crack-tip strain rate in cold worked material. While these interpretations consider cold work as a homogeneous effect, dislocations are generated inhomogeneously within the microstructure during cold work. The presence of grain boundaries results in dislocation pile-ups that cause local strain concentrations. The local strains generated from cold working α-brass by tensile elongation were characterized using electron backscatter diffraction (EBSD). The role of these local strains in SCC was studied by measuring the strain distributions from the same regions of the sample before cold work, after cold work, and after SCC. Though, the cracks did not always initiate or propagate along boundaries with pre-existing local strains from the applied cold work, the local strains surrounding the cracked boundaries had contributions from both the crack propagation and the prior cold work. - Highlights: • Plastic strain localization has a complex relationship with SCC susceptibility. • Surface relief created by cold work creates its own granular strain localization. • Cold work promotes crack growth but several other factors are involved.

  10. A Global Refiability Assessment Method on Aging Offshore Platforms with Corrosion and Cracks

    Institute of Scientific and Technical Information of China (English)

    JI Chun-yan; LI Shan-shan; CHEN Ming-lu

    2009-01-01

    Corrosion and fatigue cracks are major threats to the structural integrity of aging offshore platforms.For the rational estimation of the safety levels of aging platforms,a global reliability assessment approach for aging offshore platforms with corrosion and fatigue cracks is presented in this paper.The base shear capacity is taken as the global ultimate strength of the offshore plaffoms,it is modeled as a random process that decreases with time in the presence of corrosion and fatigue crack propagation.And the corrosion and fatigue crack growth rates in the main members and key joints are modeled as random variables.A simulation method of the extreme wave loads which are applied to the structures of offshore platforms is proposed too.Furthermore,the statistics of global base shear capacity and extreme wave loads are obtained by Monte Carlo simulation method.On the basis of the limit state equation of global failure mode,the instantaneous reliability and time dependent reliability assessment methods are both presented in this paper.Finally the instantaueous reliability index and time dependent failure probability of a jacket platform are estimated with different ages in the demonstration example.

  11. Hydrogen embrittlement, grain boundary segregation, and stress corrosion cracking of alloy X-750 in low- and high-temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Mills, W. J.; Lebo, M. R.; Kearns, J. J. [Bettis Atomic Power Lab., West Mifflin, PA (United States)

    1997-04-01

    The nature of intergranular stress corrosion cracking (SCC) of alloy X-750 was characterized in low- and high-temperature water by testing as-notched and precracked fracture mechanics specimens. Materials given the AH, BH, and HTH heat treatments were studied. While all heat treatments were susceptible to rapid low-temperature crack propagation (LTCP) below 150 C, conditions AH and BH were particularly susceptible. Low-temperature tests under various loading conditions (e.g., constant displacement, constant load, and increasing load) revealed that the maximum stress intensity factors (K{sub P{sub max}}) from conventional rising load tests provide conservative estimates of the critical loading conditions in highly susceptible heats, regardless of the load path history. For resistant heats, K{sub P{sub max}} provides a reasonable, but not necessarily conservative, estimate of the critical stress intensity factor for LTCP. Testing of as-notched specimens showed that LTCP will not initiate at a smooth surface or notch, but will readily occur if a cracklike defect is present. Comparison of the cracking response in water with that for hydrogen-precharged specimens tested in air demonstrated that LTCP is associated with hydrogen embrittlement of grain boundaries. The stress corrosion crack initiation and growth does occur in high-temperature water (>250 C), but crack growth rates are orders of magnitude lower than LTCP rates. The SCC resistance of HTH heats is far superior to that of AH heats as crack initiation times are two to three orders of magnitude greater and growth rates are one to two orders of magnitude lower.

  12. Methodology to evaluate the crack growth rate by stress corrosion cracking in dissimilar metals weld in simulated environment of PWR nuclear reactor

    Energy Technology Data Exchange (ETDEWEB)

    Paula, Raphael G.; Figueiredo, Celia A.; Rabelo, Emerson G., E-mail: raphaelmecanica@gmail.com, E-mail: caf@cdtn.br, E-mail: egr@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    Inconel alloys weld metal is widely used to join dissimilar metals in nuclear reactors applications. It was recently observed failures of weld components in plants, which have triggered an international effort to determine reliable data on the stress corrosion cracking behavior of this material in reactor environment. The objective of this work is to develop a methodology to determine the crack growth rate caused by stress corrosion in Inconel alloy 182, using the specimen (Compact Tensile) in simulated PWR environment. (author)

  13. Role of pH on the stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Khokhar, M. I.; Beck, F. H.; Fontana, M. G.

    1973-01-01

    Stress corrosion cracking (SCC) experiments were conducted on Ti-8-1-1 wire specimens in hydrochloric and sulfuric acids of variable pH in order to determine the effect of pH on the susceptibility to cracking. The alloy exhibited increasing susceptibility with decreasing pH. By varying the applied potential, it was observed that susceptibility zones exist both in the cathodic and the anodic ranges. In the cathodic range, susceptibility also increased with decreasing applied potential. Corrosion potential-time data in hydrochloric acid (pH 1.7) and sulfuric acid (pH 1.7) indicate that chloride ions lower the corrosion potential of the specimen which, in turn, increases the susceptibility.

  14. Role of pH on the stress corrosion cracking of titanium alloys

    Science.gov (United States)

    Khokhar, M. I.; Beck, F. H.; Fontana, M. G.

    1973-01-01

    Stress corrosion cracking (SCC) experiments were conducted on Ti-8-1-1 wire specimens in hydrochloric and sulfuric acids of variable pH in order to determine the effect of pH on the susceptibility to cracking. The alloy exhibited increasing susceptibility with decreasing pH. By varying the applied potential, it was observed that susceptibility zones exist both in the cathodic and the anodic ranges. In the cathodic range, susceptibility also increased with decreasing applied potential. Corrosion potential-time data in hydrochloric acid (pH 1.7) and sulfuric acid (pH 1.7) indicate that chloride ions lower the corrosion potential of the specimen which, in turn, increases the susceptibility.

  15. Stress corrosion cracking in low-pressure turbine discs in an NaCl solution

    Energy Technology Data Exchange (ETDEWEB)

    Hitomi, Itoh [Mitsubishi Heavy Industries, Ltd., Takasago Research and Development Center (Japan); Takashi, Momoo [Mitsubishi Heavy Industries, Ltd., Takasago Machinery Works (Japan)

    2001-07-01

    From past research, it is known that stress corrosion cracking in low-pressure turbine discs occurs in an environment near that of deaerated pure water. Nevertheless, in units with molar ratio control, there is a possibility of NaCl concentrating as an impurity in the dry/wet boundary region. Long-term immersion tests were conducted at 373 K to 473 K with the NaCl concentration predicted to become 5%. It was found that, when FeCl{sub 3} or other oxidizer was added, corrosion increased remarkably and SCC was initiated. When cracks were initiated, they were primarily transgranular; as the test temperature was decreased, initiation was accelerated but conversely crack propagation was reduced. (author)

  16. Effects of alloy chemistry, cold work, and water chemistry on corrosion fatigue and stress corrosion cracking of nickel alloys and welds.

    Energy Technology Data Exchange (ETDEWEB)

    Chopra, O. K.; Soppet, W. K.; Shack, W. J.; Energy Technology

    2001-04-01

    Reactor vessel internal components made of nickel-base alloys are susceptible to environmentally assisted cracking (EAC). A better understanding of the causes and mechanisms of this cracking may permit less conservative estimates of damage accumulation and requirements on inspection intervals. The objective of this work is to evaluate and compare the resistance of Alloys 600 and 690 and their welds, such as Alloys 82, 182, 52, and 152, to EAC in simulated light water reactor environments. The existing crack growth rate (CGR) data for these alloys under cyclic and constant loads have been evaluated to establish the effects of alloy chemistry, cold work, and water chemistry. The experimental fatigue CGRs are compared with CGRs that would be expected in air under the same mechanical loading conditions to obtain a qualitative understanding of the degree and range of conditions for significant environmental enhancement in growth rates. The existing stress corrosion cracking (SCC) data on Alloys 600 and 690 and Alloy 82, 182, and 52 welds have been compiled and analyzed to determine the influence of key parameters on growth rates in simulated PWR and BWR environments. The SCC data for these alloys have been evaluated with correlations developed by Scott and by Ford and Andresen.

  17. Characterizing the effect of creep on stress corrosion cracking of cold worked Alloy 690 in supercritical water environment

    Science.gov (United States)

    Zhang, Lefu; Chen, Kai; Du, Donghai; Gao, Wenhua; Andresen, Peter L.; Guo, Xianglong

    2017-08-01

    The effect of creep on stress corrosion cracking (SCC) was studied by measuring crack growth rates (CGRs) of 30% cold worked (CW) Alloy 690 in supercritical water (SCW) and inert gas environments at temperatures ranging from 450 °C to 550 °C. The SCC crack growth rate under SCW environments can be regarded as the cracking induced by the combined effect of corrosion and creep, while the CGR in inert gas environment can be taken as the portion of creep induced cracking. Results showed that the CW Alloy 690 sustained high susceptibility to intergranular (IG) cracking, and creep played a dominant role in the SCC crack growth behavior, contributing more than 80% of the total crack growth rate at each testing temperature. The temperature dependence of creep induced CGRs follows an Arrhenius dependency, with an apparent activation energy (QE) of about 225 kJ/mol.

  18. The influence of modified water chemistries on metal oxide films, activity build-up and stress corrosion cracking of structural materials in nuclear power plants

    Energy Technology Data Exchange (ETDEWEB)

    Maekelae, K.; Laitinen, T.; Bojinov, M. [VTT Manufacturing Technology, Espoo (Finland)

    1999-03-01

    The primary coolant oxidises the surfaces of construction materials in nuclear power plants. The properties of the oxide films influence significantly the extent of incorporation of actuated corrosion products into the primary circuit surfaces, which may cause additional occupational doses for the maintenance personnel. The physical and chemical properties of the oxide films play also an important role in different forms of corrosion observed in power plants. This report gives a short overview of the factors influencing activity build-up and corrosion phenomena in nuclear power plants. Furthermore, the most recent modifications in the water chemistry to decrease these risks are discussed. A special focus is put on zinc water chemistry, and a preliminary discussion on the mechanism via which zinc influences activity build-up is presented. Even though the exact mechanisms by which zinc acts are not yet known, it is assumed that Zn may block the diffusion paths within the oxide film. This reduces ion transport through the oxide films leading to a reduced rate of oxide growth. Simultaneously the number of available adsorption sites for {sup 60}Co is also reduced. The current models for stress corrosion cracking assume that the anodic and the respective cathodic reactions contributing to crack growth occur partly on or in the oxide films. The rates of these reactions may control the crack propagation rate and therefore, the properties of the oxide films play a crucial role in determining the susceptibility of the material to stress corrosion cracking. Finally, attention is paid also on the novel techniques which can be used to mitigate the susceptibility of construction materials to stress corrosion cracking. (orig.) 127 refs.

  19. A Fundamental study of remedial technology development to prevent stress corrosion cracking of steam generator tubing

    Energy Technology Data Exchange (ETDEWEB)

    Park, In Gyu; Lee, Chang Soon [Sunmoon University, Asan (Korea)

    1998-04-01

    Most of the PWR Steam generators with tubes in Alloy 600 alloy are affected by Stress Corrosion Cracking, such as PWSCC(Primary Water Stress Corrosion Cracking) and ODSCC(Outside Diameter Stress Corrosion Cracking). This study was undertaken to establish the background for remedial technology development to prevent SCC. in the report are included the following topics: (1) General: (i) water chemistry related factors, (ii) Pourbaix(Potential-pH) Diagram, (iii) polarization plot, (iv) corrosion mode of Alloy 600, 690, and 800, (v) IGA/SCC growth rate, (vi) material suspetibility of IGA/SCC, (vii) carbon solubility of Alloy 600 (2) Microstructures of Alloy 600 MA, Alloy 600 TT, Alloy 600 SEN Alloy 690 TT(Optical, SEM, and TEM) (3) Influencing factors for PWSCC initiation rate of Alloy 600: (i) microstructure, (ii) water chemistry(B, Li), (iii) temperature, (iv) plastic deformation, (v) stress relief annealing (4) Influencing factors for PWSCC growth rate of Alloy 600: (i) water chemistry(B, Li), (ii) Scott Model, (iii) intergranular carbide, (iv) temperature, (v) hold time (5) Laboratory conditions for ODSCC initiation rate: 1% NaOH, 316 deg C; 1% NaOH, 343 deg C; 50% NaOH, 288 deg C; 10% NaOH, 302 deg C; 10% NaOH, 316 deg C; 50% NaOH, 343 deg C (6) Sludge effects for ODSCC initiation rate: CuO, Cr{sub 2}O{sub 3}, Fe{sub 3}O{sub 4} (7) Influencing factors for PWSCC growth rate of Alloy 600: (i) Caustic concentration effect, (ii) carbonate addition effect (8) Sulfate corrosion: (i) sulfate ratio and pH effect, (ii) wastage rate of Alloy 600 and Alloy 690 (9) Crevice corrosion: (i) experimental setup for crevice corrosion, (ii) organic effect, (iii) (Na{sub 2}SO{sub 4} + NaOH) effect (10) Remedial measures for SCC: (i) Inhibitors, (ii) ZnO effect. (author). 30 refs., 174 figs., 51 tabs.

  20. Dissolution of copper in chloride/ammonia mixtures and the implications for the stress corrosion cracking of copper containers

    Energy Technology Data Exchange (ETDEWEB)

    King, F.; Greidanus, G.; Jobe, D.J

    1999-05-01

    Stress-corrosion cracking is a possible failure mechanism for copper nuclear fuel waste disposal containers. One species known to cause the stress corrosion of copper alloys is ammonia. It is conceivable that ammonia could be produced in a disposal vault under certain, very specific conditions. There are a number of conditions, however, that mitigate against container failure by stress corrosion, one of which is the presence of chloride ions in deep Canadian Shield groundwaters. There are a number of reports in the literature that suggest that Cl{sup -} has an inhibitive effect on the stress corrosion of Cu alloys in ammonia solutions. The electrochemical behaviour of Cu in Cl{sup -}/ammonia solutions has been studied as a function of ammonia concentration, pH, the rate of mass transport and electrochemical potential. In particular, the effects of these parameters on the formation Of Cu{sub 2}O films and the steady-state dissolution behaviour have been determined. All experiments were carried out in 0.1 mol{center_dot}dm{sup -3} NaC1 as a base solution. A series of aqueous speciation and equilibrium potential/pH diagrams are also presented for the quaternary system Cu-C1{sup -}NH{sub 3}/NH{sub 4{sup +}}H{sub 2}O. These diagrams are used to interpret the results of the electrochemical experiments reported here. In addition, it is demonstrated how these diagrams could be used to predict the time-dependence of the susceptibility to stress corrosion cracking of Cu containers in a disposal vault. (author)

  1. Corrosion mechanisms of candidate structural materials for supercritical water-cooled reactor

    Institute of Scientific and Technical Information of China (English)

    Lefu ZHANG; Fawen ZHU; Rui TANG

    2009-01-01

    Nickel-based alloys, austenitic stainless steel, ferritic/martensitic heat-resistant steels, and oxide dispersion strengthened steel are presently considered to be the candidate structural or fuel-cladding materials for supercritical water-cooled reactor (SCWR), one of the promising generation IV reactor for large-scale electric power production. However, corrosion and stress corrosion cracking of these candidate alloys still remain to be a major problem in the selection of nuclear fuel cladding and other structural materials, such as water rod. Survey of literature and experimental results reveal that the general corrosion mechanism of those candidate materials exhibits quite complicated mechanism in high-temperature and high-pressure supercritical water. Formation of a stable protective oxide film is the key to the best corrosion-resistant alloys. This paper focuses on the mechanism of corrosion oxide film breakdown for SCWR candidate materials.

  2. Chloride stress corrosion cracking of Alloy 600 in boric acid solutions

    Energy Technology Data Exchange (ETDEWEB)

    Berge, Ph. [Electricite de France, 92 - Paris la Defense (France); Noel, D.; Gras, J.M.; Prieux, B. [Electricite de France, 77 - Moret-sur-Loing (France). Direction des Etudes et Recherches

    1997-10-01

    The high nickel austenitic alloys are generally considered to have good resistance to chloride stress corrosion cracking. In the standard boiling magnesium chloride solution tests, alloys with more than 40% nickel are immune. Nevertheless, more recent data show that cracking can occur in both Alloys 600 and 690 if the solution is acidified. In other low pH media, such as boric acid solution at 100 deg C, transgranular and intergranular cracking are observed in Alloy 600 in the presence of minor concentrations of sodium chloride (2g/I). In concentrated boric acid at higher temperatures (250 and 290 deg C), intergranular cracking also occurs, either when the chloride concentration is high, or at low chloride contents and high oxygen levels. The role of pH and a possible specific action of boric acid are discussed, together with the influence of electrochemical potential. (author) 21 refs.

  3. Stress-corrosion cracking of sensitized stainless steel by sulfur-containing compounds

    Energy Technology Data Exchange (ETDEWEB)

    Isaacs, H.S.; Vyas, B.; Kendig, M.W.

    1981-01-01

    The stress corrosion cracking (SCC) of sensitized Type 304 stainless steel in thiosulfate solutions has been studied using constant extension rate tests. Very low concentrations of about 6.10/sup -7/M Na/sub 2/S/sub 2/O/sub 3/ (0.1ppm) gave cracking. With boric acid added, higher concentrations (1ppm) were required. The SCC was shown to be electrochemically controlled. Below -0.5v/sub SCE/ (-0.75/sub SHE/) no SCC took place; above this potential the rate of SCC increased with potential. An induction period was required before SCC continued above -0.5v if the potential was held at or below this value for extended times. This period was associated with the build up of an aggressive solution of thiosulfate decomposition products within the crack. The cracking process has been considered to be controlled by rupture of a salt layer and not a passivating oxide.

  4. Stress corrosion crack initiation of alloy 600 in PWR primary water

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Ziqing; Toloczko, Mychailo B.; Olszta, Matthew J.; Bruemmer, Stephen M.

    2017-07-01

    Stress corrosion crack (SCC) initiation of three mill-annealed (MA) alloy 600 heats in simulated pressurized water reactor primary water has been investigated using constant load tests equipped with in-situ direct current potential drop (DCPD) measurement capabilities. SCC initiation times were greatly reduced by a small amount of cold work. Shallow intergranular (IG) attack and/or cracks were found on most high-energy grain boundaries intersecting the surface with only a small fraction evolving into larger cracks and IGSCC growth. Crack depth profiles were measured and related to DCPD-detected initiation response. Processes controlling the SCC initiation in MA alloy 600 are discussed. IN PRESS, CORRECTED PROOF, 05/02/2017 - mfl

  5. Stress Corrosion Cracking Behavior of Multipass TIG-Welded AA2219 Aluminum Alloy in 3.5 wt pct NaCl Solution

    Science.gov (United States)

    Venugopal, A.; Sreekumar, K.; Raja, V. S.

    2012-09-01

    The stress corrosion cracking (SCC) behavior of the AA2219 aluminum alloy in the single-pass (SP) and multipass (MP) welded conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using a slow-strain-rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both the BM and welded joints. The results showed that the ductility ratio ( ɛ NaCl/( ɛ air) was 0.97 and 0.96, respectively, for the BM and MP welded joint, and the same was marginally reduced to 0.9 for the SP welded joint. The fractographic examination of the failed samples revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy under all welded conditions. To understand the decrease in the ductility of the SP welded joint, preexposure SSRT followed by microstructural observations were made, which showed that the decrease in ductility ratio of the SP welded joint was caused by the electrochemical pitting that assisted the nucleation of cracks in the form of corrosion induced mechanical cracking rather than true SCC failure of the alloy. The microstructural examination and polarization tests demonstrated a clear grain boundary (GB) sensitization of the PMZ, resulting in severe galvanic corrosion of the SP weld joint, which initiated the necessary conditions for the localized corrosion and cracking along the PMZ. The absence of PMZ and a refined fusion zone (FZ) structure because of the lesser heat input and postweld heating effect improved the galvanic corrosion resistance of the MP welded joint greatly, and thus, failure occurred along the FZ.

  6. Uncertainty quantification methodologies development for stress corrosion cracking of canister welds

    Energy Technology Data Exchange (ETDEWEB)

    Dingreville, Remi Philippe Michel [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States); Bryan, Charles R. [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2016-09-30

    This letter report presents a probabilistic performance assessment model to evaluate the probability of canister failure (through-wall penetration) by SCC. The model first assesses whether environmental conditions for SCC – the presence of an aqueous film – are present at canister weld locations (where tensile stresses are likely to occur) on the canister surface. Geometry-specific storage system thermal models and weather data sets representative of U.S. spent nuclear fuel (SNF) storage sites are implemented to evaluate location-specific canister surface temperature and relative humidity (RH). As the canister cools and aqueous conditions become possible, the occurrence of corrosion is evaluated. Corrosion is modeled as a two-step process: first, pitting is initiated, and the extent and depth of pitting is a function of the chloride surface load and the environmental conditions (temperature and RH). Second, as corrosion penetration increases, the pit eventually transitions to a SCC crack, with crack initiation becoming more likely with increasing pit depth. Once pits convert to cracks, a crack growth model is implemented. The SCC growth model includes rate dependencies on both temperature and crack tip stress intensity factor, and crack growth only occurs in time steps when aqueous conditions are predicted. The model suggests that SCC is likely to occur over potential SNF interim storage intervals; however, this result is based on many modeling assumptions. Sensitivity analyses provide information on the model assumptions and parameter values that have the greatest impact on predicted storage canister performance, and provide guidance for further research to reduce uncertainties.

  7. Thermo-mechanical simulations of early-age concrete cracking with durability predictions

    Science.gov (United States)

    Havlásek, Petr; Šmilauer, Vít; Hájková, Karolina; Baquerizo, Luis

    2017-09-01

    Concrete performance is strongly affected by mix design, thermal boundary conditions, its evolving mechanical properties, and internal/external restraints with consequences to possible cracking with impaired durability. Thermo-mechanical simulations are able to capture those relevant phenomena and boundary conditions for predicting temperature, strains, stresses or cracking in reinforced concrete structures. In this paper, we propose a weakly coupled thermo-mechanical model for early age concrete with an affinity-based hydration model for thermal part, taking into account concrete mix design, cement type and thermal boundary conditions. The mechanical part uses B3/B4 model for concrete creep and shrinkage with isotropic damage model for cracking, able to predict a crack width. All models have been implemented in an open-source OOFEM software package. Validations of thermo-mechanical simulations will be presented on several massive concrete structures, showing excellent temperature predictions. Likewise, strain validation demonstrates good predictions on a restrained reinforced concrete wall and concrete beam. Durability predictions stem from induction time of reinforcement corrosion, caused by carbonation and/or chloride ingress influenced by crack width. Reinforcement corrosion in concrete struts of a bridge will serve for validation.

  8. Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions

    Directory of Open Access Journals (Sweden)

    R. K. Singh Raman

    2014-12-01

    Full Text Available This article describes the susceptibility of 316L stainless steel to stress corrosion cracking (SCC in a nitrite-containing chloride solution. Slow strain rate testing (SSRT in 30 wt. % MgCl2 solution established SCC susceptibility, as evidenced by post-SSRT fractography. Addition of nitrite to the chloride solution, which is reported to have inhibitive influence on corrosion of stainless steels, was found to increase SCC susceptibility. The susceptibility was also found to increase with nitrite concentration. This behaviour is explained on the basis of the passivation and pitting characteristics of 316L steel in chloride solution.

  9. Stress Corrosion Cracking in Al-Zn-Mg-Cu Aluminum Alloys in Saline Environments

    Science.gov (United States)

    Holroyd, N. J. Henry; Scamans, G. M.

    2013-03-01

    Stress corrosion cracking of Al-Zn-Mg-Cu (AA7xxx) aluminum alloys exposed to saline environments at temperatures ranging from 293 K to 353 K (20 °C to 80 °C) has been reviewed with particular attention to the influences of alloy composition and temper, and bulk and local environmental conditions. Stress corrosion crack (SCC) growth rates at room temperature for peak- and over-aged tempers in saline environments are minimized for Al-Zn-Mg-Cu alloys containing less than ~8 wt pct Zn when Zn/Mg ratios are ranging from 2 to 3, excess magnesium levels are less than 1 wt pct, and copper content is either less than ~0.2 wt pct or ranging from 1.3 to 2 wt pct. A minimum chloride ion concentration of ~0.01 M is required for crack growth rates to exceed those in distilled water, which insures that the local solution pH in crack-tip regions can be maintained at less than 4. Crack growth rates in saline solution without other additions gradually increase with bulk chloride ion concentrations up to around 0.6 M NaCl, whereas in solutions with sufficiently low dichromate (or chromate), inhibitor additions are insensitive to the bulk chloride concentration and are typically at least double those observed without the additions. DCB specimens, fatigue pre-cracked in air before immersion in a saline environment, show an initial period with no detectible crack growth, followed by crack growth at the distilled water rate, and then transition to a higher crack growth rate typical of region 2 crack growth in the saline environment. Time spent in each stage depends on the type of pre-crack ("pop-in" vs fatigue), applied stress intensity factor, alloy chemistry, bulk environment, and, if applied, the external polarization. Apparent activation energies ( E a) for SCC growth in Al-Zn-Mg-Cu alloys exposed to 0.6 M NaCl over the temperatures ranging from 293 K to 353 K (20 °C to 80 °C) for under-, peak-, and over-aged low-copper-containing alloys (alloys (>~0.8 wt pct), they are typically

  10. Modeling of Stress Corrosion Cracking for High Level Radioactive-Waste Packages

    Energy Technology Data Exchange (ETDEWEB)

    Lu, S C; Gordon, G M; Andresen, P L; Herrera, M L

    2003-06-20

    A stress corrosion cracking (SCC) model has been adapted for performance prediction of high level radioactive-waste packages to be emplaced in the proposed Yucca Mountain radioactive-waste repository. SCC is one form of environmentally assisted cracking due to three factors, which must be present simultaneously: metallurgical susceptibility, critical environment, and static (or sustained) tensile stresses. For waste packages of the proposed Yucca Mountain repository, the outer barrier material is Alloy 22, a highly corrosion resistant alloy, the environment is represented by the water film present on the surface of the waste package from dripping or deliquescence of soluble salts present in any surface deposits, and the stress is principally the weld induced residual stress. SCC has historically been separated into ''initiation'' and ''propagation'' phases. Initiation of SCC will not occur on a smooth surface if the surface stress is below a threshold value defined as the threshold stress. Cracks can also initiate at and propagate from flaws (or defects) resulting from manufacturing processes (such as welding). To account for crack propagation, the slip dissolution/film rupture (SDFR) model is adopted to provide mathematical formulas for prediction of the crack growth rate. Once the crack growth rate at an initiated SCC is determined, the time to through-wall penetration for the waste package can be calculated. The SDFR model relates the advance (or propagation) of cracks, subsequent to the crack initiation from bare metal surface, to the metal oxidation transients that occur when the protective film at the crack tip is continually ruptured and repassivated. A crack, however, may reach the ''arrest'' state before it enters the ''propagation'' phase. There exists a threshold stress intensity factor, which provides a criterion for determining if an initiated crack or pre

  11. Analysis of WWER 1000 collector cracking mechanisms

    Energy Technology Data Exchange (ETDEWEB)

    Matocha, K.; Wozniak, J. [Vitkovice J.S.C., Ostrava (Switzerland)

    1997-12-31

    The presentation reviews the large experimental program, started in 1993 in Vitkovice, where the main aim was: (1) a detailed study of strain and thermal ageing, dissolved oxygen content and temperature on subcritical crack growth in 10NiMo8.5 (10GN2MFA) steel, (2) a detailed study of the effect of high temperature water and tube expansion technology on fracture behaviour of ligaments between holes for heat exchange tubes, and (3) a detailed study of the effect of drilling, tube expansion technology and heat treatment on residual stresses on the surface of holes for heat exchange tubes. The aim of all these investigations was to find a dominant damage mechanism responsible for collector cracking to be able to judge the efficiency of implemented modifications and suggested countermeasures and to answer a very important question whether proper operation conditions (mainly water chemistry) make the operation of steam generators made in Vitcovice safe throughout the planned lifetime. 10 refs.

  12. Corrosion-Fatigue Cracking in HY-80 and HY-130 Steels

    Science.gov (United States)

    2015-01-22

    on HY80 steel and HY-130 steel are shown in Fig. A-13 through A-16 for various specimens tested at different load ratios and environments. Because...Naval Research Laboratory Washington, DC 20375-5320 NRL/MR/6355--15-9584 Corrosion-Fatigue Cracking in HY-80 and HY-130 Steels January 22, 2015 P.S...Cracking in HY-80 and HY-130 Steels P.S. Pao and R.L. Holtz Naval Research Laboratory 4555 Overlook Avenue, SW Washington, DC 20375-5328 Office of Naval

  13. 49 CFR 192.929 - What are the requirements for using Direct Assessment for Stress Corrosion Cracking (SCCDA)?

    Science.gov (United States)

    2010-10-01

    ... requirements for using Direct Assessment for Stress Corrosion Cracking (SCCDA)? (a) Definition. Stress..., appendix A3, and remediate the threat in accordance with ASME/ANSI B31.8S, appendix A3, section A3.4....

  14. Fracture mechanics of piezoelectric solids with interface cracks

    CERN Document Server

    Govorukha, Volodymyr; Loboda, Volodymyr; Lapusta, Yuri

    2017-01-01

    This book provides a comprehensive study of cracks situated at the interface of two piezoelectric materials. It discusses different electric boundary conditions along the crack faces, in particular the cases of electrically permeable, impermeable, partially permeable, and conducting cracks. The book also elaborates on a new technique for the determination of electromechanical fields at the tips of interface cracks in finite sized piezoceramic bodies of arbitrary shape under different load types. It solves scientific problems of solid mechanics in connection with the investigation of electromechanical fields in piezoceramic bodies with interface cracks, and develops calculation models and solution methods for plane fracture mechanical problems for piecewise homogeneous piezoceramic bodies with cracks at the interfaces. It discusses the “open” crack model, which leads to a physically unrealistic oscillating singularity at the crack tips, and the contact zone model for in-plane straight interface cracks betw...

  15. An Industrial Perspective on Environmentally Assisted Cracking of Some Commercially Used Carbon Steels and Corrosion-Resistant Alloys

    Science.gov (United States)

    Ashida, Yugo; Daigo, Yuzo; Sugahara, Katsuo

    2017-08-01

    Commercial metals and alloys like carbon steels, stainless steels, and nickel-based super alloys frequently encounter the problem of environmentally assisted cracking (EAC) and resulting failure in engineering components. This article aims to provide a perspective on three critical industrial applications having EAC issues: (1) corrosion and cracking of carbon steels in automotive applications, (2) EAC of iron- and nickel-based alloys in salt production and processing, and (3) EAC of iron- and nickel-based alloys in supercritical water. The review focuses on current industrial-level understanding with respect to corrosion fatigue, hydrogen-assisted cracking, or stress corrosion cracking, as well as the dominant factors affecting crack initiation and propagation. Furthermore, some ongoing industrial studies and directions of future research are also discussed.

  16. SRNL SHELF LIFE STUDIES - SCC STUDIES AT ROOM TEMPERTURE [stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Mickalonis, J.; Duffey, J.

    2014-11-12

    Phase II, Series 2 corrosion testing performed by the Savannah River National Laboratory (SRNL) for the Department of Energy 3013 container has been completed. The corrosion tests are part of an integrated plan conducted jointly by Los Alamos National Laboratory and the Savannah River Site. SRNL was responsible for conducting corrosion studies in small-scale vessels to address the influence of salt composition, water loading, and type of oxide/salt contact on the relative humidity inside a 3013 container and on the resulting corrosion of Type 304L and 316L stainless steel (304L and 316L). This testing was conducted in two phases: Phase I evaluated a broad spectrum of salt compositions and initial water loadings on the salt mixtures exposed to 304L and 316L and the resulting corrosion; Phase II evaluated the corrosion of 304L at specific water loadings and a single salt composition. During Phase I testing at high initial moisture levels (0.35 to 1.24 wt%)a, the roomtemperature corrosion of 304L exposed to a series of plutonium oxide/chloride salt mixtures ranged from superficial staining to pitting and stress corrosion cracking (SCC). 304L teardrop coupons that exhibited SCC were directly exposed to a mixture composed of 98 wt % PuO2, 0.9 wt % NaCl, 0.9 wt % KCl, and 0.2 wt % CaCl2. Cracking was not observed in a 316L teardrop coupon. Pitting was also observed in this environment for both 304L and 316L with depths ranging from 20 to 100 μm. Neither pitting nor SCC was observed in mixtures with a greater chloride salt concentration (5 and 28 wt%). These results demonstrated that for a corrosive solution to form a balance existed between the water loading and the salt chloride concentration. This chloride solution results from the interaction of loaded water with the hydrating CaCl2 salt. In Phase II, Series 1 tests, the SCC results were shown to be reproducible with cracking occurring in as little as 85 days. The approximate 0.5 wt% moisture level was found to

  17. Corrosion Mechanism of MgO-CaO Brick for AOD Furnace

    Institute of Scientific and Technical Information of China (English)

    WANG Jiandong; GE Changchun; SHEN Weiping

    2006-01-01

    Residual MgO-CaO brick after being used in AOD furnace was determined by OM, SEM and EDAX. Corrosion mechanism of MgO-CaO brick as furnace lining was studied. Results show that: The corrosion of MgOCaO brick is mainly attributed to the solution and infiltration of silicate liquid phase. Transverse cracks between reacted zone and original zone are parallel to the working face, which is an important factor for deteriorating the corrosion of MgO-CaO bricks.

  18. Stress Corrosion Cracking Behavior of Alloy 22 in Multi-Ionic Aqueous Environments

    Energy Technology Data Exchange (ETDEWEB)

    K.J. King; J.C. Estill; R.B. Rebak

    2002-07-15

    The US Department of Energy is characterizing a potential repository site for nuclear waste in Yucca Mountain (NV). In its current design, the nuclear waste containers consist of a double metallic layer. The external layer would be made of NO6022 or Alloy 22 (Ni-22Cr-13Mo-3W-3Fe). Since over their lifetime, the containers may be exposed to multi-ionic aqueous environments, a potential degradation mode of the outer layer could be environmentally assisted cracking (EAC) or stress corrosion cracking (SCC). In general, Alloy 22 is extremely resistant to SCC, especially in concentrated chloride solutions. Current results obtained through slow strain rate testing (SSRT) shows that Alloy 22 may suffer SCC in simulated concentrated water (SCW) at applied potentials approximately 400 mV more anodic than the corrosion potential (E{sub rr}).

  19. Crack Initiation and Growth Behavior at Corrosion Pit in 7075-T6 High Strength Aluminum Alloy

    Science.gov (United States)

    2013-06-01

    was not used to measure the transition from corrosion pit to long crack [25]. . . . . . . . . . . 22 3.1 Composition of a typical sample of 7075 -T6...lives. 24 III. Methodology 3.1 Material Research was conducted using 7075 -T6 aluminum. This alloy is commonly used in aerospace applications and as a... material properties of this alloy. It is important to note that these properties were also used in all finite element models. Table 3.1: Composition of

  20. The influence of loading on the corrosion of steel in cracked ordinary Portland cement and high performance concretes

    Science.gov (United States)

    Jaffer, Shahzma Jafferali

    Most studies that have examined chloride-induced corrosion of steel in concrete have focused on sound concrete. However, reinforced concrete is seldom uncracked and very few studies have investigated the influence of cracked concrete on rebar corrosion. Furthermore, the studies that have examined the relationship between cracks and corrosion have focused on unloaded or statically loaded cracks. However, in practice, reinforced concrete structures (e.g. bridges) are often dynamically loaded. Hence, the cracks in such structures open and close which could influence the corrosion of the reinforcing steel. Consequently, the objectives of this project were (i) to examine the effect of different types of loading on the corrosion of reinforcing steel, (ii) the influence of concrete mixture design on the corrosion behaviour and (iii) to provide data that can be used in service-life modelling of cracked reinforced concretes. In this project, cracked reinforced concrete beams made with ordinary Portland cement concrete (OPCC) and high performance concrete (HPC) were subjected to no load, static loading and dynamic loading. They were immersed in salt solution to just above the crack level at their mid-point for two weeks out of every four (wet cycle) and, for the remaining two weeks, were left in ambient laboratory conditions to dry (dry cycle). The wet cycle led to three conditions of exposure for each beam: (i) the non-submerged region, (ii) the sound, submerged region and (iii) the cracked mid-section, which was also immersed in the solution. Linear polarization resistance and galvanostatic pulse techniques were used to monitor the corrosion in the three regions. Potentiodynamic polarization, electrochemical current noise and concrete electrical resistance measurements were also performed. These measurements illustrated that (i) rebar corroded faster at cracks than in sound concrete, (ii) HPC was more protective towards the rebar than OPCC even at cracks and (iii) there

  1. Effect of dissolved oxygen content on stress corrosion cracking of a cold worked 316L stainless steel in simulated pressurized water reactor primary water environment

    Science.gov (United States)

    Zhang, Litao; Wang, Jianqiu

    2014-03-01

    Stress corrosion crack growth tests of a cold worked nuclear grade 316L stainless steel were conducted in simulated pressurized water reactor (PWR) primary water environment containing various dissolved oxygen (DO) contents but no dissolved hydrogen. The crack growth rate (CGR) increased with increasing DO content in the simulated PWR primary water. The fracture surface exhibited typical intergranular stress corrosion cracking (IGSCC) characteristics.

  2. Evaluation of the stress corrosion cracking resistance of several high strength low alloy steels

    Science.gov (United States)

    Humphries, T. S.; Nelson, E. E.

    1980-01-01

    The stress corrosion cracking resistance was studied for high strength alloy steels 4130, 4340, for H-11 at selected strength levels, and for D6AC and HY140 at a single strength. Round tensile and C-ring type specimens were stressed up to 100 percent of their yield strengths and exposed to alternate immersion in salt water, salt spray, the atmosphere at Marshall Space Flight Center, and the seacoast at Kennedy Space Center. Under the test conditions, 4130 and 4340 steels heat treated to a tensile strength of 1240 MPa (180 ksi), H-11 and D6AC heat treated to a tensile strength of 1450 MPa (210 ksi), and HY140 (1020 MPa, 148 ksi) are resistant to stress corrosion cracking because failures were not encountered at stress levels up to 75 percent of their yield strengths. A maximum exposure period of one month for alternate immersion in salt water or salt spray and three months for seacoast is indicated for alloy steel to avoid false indications of stress corrosion cracking because of failure resulting from severe pitting.

  3. Effect of Sensitization on Corrosion-Fatigue Cracking in Al 5083 Alloy

    Science.gov (United States)

    2015-01-21

    1% NaCl solution, the observed environmental effects on fatigue crack growth can be explained by the hydrogen embrittlement mechanism and are...using a superposition model and a two-parameter approach to environment- assisted cracking . The superposition model is essentially a summation of...Metall. Trans. A. Vol. 11A, 1980, pp. 151-158. 15. A. Bonakdar, F. Wang, J.J. Williams, and N. Chawla, “ Environmental Effects on Fatigue Crack

  4. Influence of CO2 corrosion on rock structure and its mechanical characteristics

    Institute of Scientific and Technical Information of China (English)

    2010-01-01

    Influence of CO2 corrosion on reservoir mineralogical composition,pore structure and their mechanical characteristics was studied using XRD,SEM,rock tri-axial machine and core flow experimental equipment.It was found that the corrosion effect was mainly attributed to rock texture and structure,fluid composition and external dynamical conditions in the experimental conditions.For cores with bedding structures,their bedding surfaces were the preferential corrosion regions,because micro-cracks would evolve at these surfaces in the pressure-releasing process.However,for cores with massive structures controlled by stable water environment,the CO2 corrosion would result in pore enlargement and secondary pore formation.The gas velocity from outlet showed sharp increase in the injection process of CO2-H2O solution.This could be explained by two changes caused by corrosion.One was the opening and closure of micro-cracks.The other was particle migration.As the corrosion time increased,both tensile strength and compressive strength decreased,which confirmed decrease of cementation strength.It should also be noted that permeability increase and micro-cracks generation would pose damage to the capacity of CO2 geological storage.

  5. Formation mechanism of cracks in saturated sand

    Institute of Scientific and Technical Information of China (English)

    Xiaobing Lu; Zhemin Zheng; Yongren Wu

    2006-01-01

    The formation mechanism of "water film" (or crack) in saturated sand is analyzed theoretically and numerically.The theoretical analysis shows that there will be no stable "water film" in the saturated sand if the strength of the skeleton is zero and no positions are choked.It is shown by numerical simulation that stable water films initiate and grow if the choking state keeps unchanged once the fluid velocities decrease to zero in the liquefied sand column.The developments of "water film" based on the model presented in this paper are compared with experimental results.

  6. Role of hydrogen in the intergranular cracking mechanism by stress corrosion in primary medium of nickel based alloys 600 and 690; Role de l'hydrogene dans le mecanisme de fissuration intergranulaire par corrosion sous contrainte en milieu primaire des alliages base nickel 600, 690

    Energy Technology Data Exchange (ETDEWEB)

    Odemer, G.; Coudurier, A.; Jambon, F.; Chene, J. [CEA Saclay, Dept. de Physico-Chimie (DEN/DANS/DPC/SCCME/LECA), 91 - Gif sur Yvette (France); Odemer, G.; Coudurier, A.; Chene, J. [Evry Univ., UMR 8587 CNRS / CEA, LAMBE, 91 (France)

    2007-07-01

    The aim of this work is to characterize the sensitivity to hydrogen embrittlement of alloys 600 and 690 in order to better understand the eventual role of hydrogen in the stress corrosion mechanism which affects these alloys when they are exposed in PWR primary medium. (O.M.)

  7. Stress corrosion cracking and its anisotropy of a PZT ferroelectric ceramics

    Institute of Scientific and Technical Information of China (English)

    2003-01-01

    Stress corrosion cracking (SCC) of a PZT ferroelectric ceramics in various media, such as moist atmosphere, silicon oil, methanol, water and formamide, and its anisotropy have been investigated at constant load test using a single-edge notched tensile specimen. The results showed that SCC could occur in all media, and the threshold stress intensity factor of SCC in water and formamide, KISCC, revealed anisotropy. The KISCC for poling direction parallel to the crack plane, was greater than that perpendicular to the crack plane, similar to the anisotropy of fracture toughness KIC; however, the anisotropy factor of KISCC, which was =1.8 (in formamide) and 2.1 (in water), was larger than that of KIC, which is =1.4. The stress-induced 90° domain switching causes the anisotropy of KIC and KISCC, besides, the resistance of SCC also has anisotropy.

  8. Potential corrosion and degradation mechanisms of Zircaloy cladding on spent nuclear fuel in a tuff repository

    Energy Technology Data Exchange (ETDEWEB)

    Rothman, A.J.

    1984-09-01

    A literature review and analysis were made of corrosion and degradation processes applicable to Zircaloy cladding on spent nuclear fuel in a tuff repository. In particular, lifetime sought for the Zircaloy is 10,000 years. Among the potential failure mechanisms examined were: oxidation by steam, air, and water, including the effects of ions whose presence is anticipated in the water; mechanical overload; stress (creep) rupture; stress-corrosion cracking (SCC); and delayed failure due to hydride cracking. The conclusion is that failure due to oxidation is not credible, although a few experiments are suggested to confirm the effect of aqueous fluoride on the Zircaloy cladding. Mechanical overload is not a problem, and failure from stress-rupture does not appear likely based on a modified Larson-Miller analysis. Analysis shows that delayed hydride cracking is not anticipated for the bulk of spent fuel pins. However, for a minority of pins under high stress, there is some uncertainty in the analysis as a result of: (1) uncertainty about crack depths in spent fuel claddings and (2) the effect of slow cooling on the formation of radially oriented hydride precipitates. Experimental resolution is called for. Finally, insufficient information is currently available on stress-corrosion cracking. While evidence is presented that SCC failure is not likely to occur, it is difficult to demonstrate this conclusively because the process is not clearly understood and data are limited. Further experimental work on SCC susceptibility is especially needed.

  9. Surface destructive mechanism on high-temperature ablation, supersonic-erosion, dreg-adherence and corrosion

    Institute of Scientific and Technical Information of China (English)

    XIAO Jun; CHEN Jian-min; ZHOU Hui-di; LI Tie-hu; ZHANG Qiu-yu

    2004-01-01

    The exhaust and flame from a supersonic airborne missile high-energy smoke-born engine (SAMHSE) may lead to high-temperature ablation, supersonic-erosion, dreg-adherence (HTASED) and corrosion on the launcher slide track, causing serious problems to the operation and decreasing the lifetime of the launcher. Therefore, it is imperative to study the destructive mechanism so as to guarantee the smooth operation and increase the lifetime of military equipments. Accordingly, HTASED and corrosion were systematically observed and analyzed with the emphasis placed on the mechanism investigations making use of a series evaluation tests, typical missile engine simulation tests, national military standard methods, scanning electron microscopy and electrochemical corrosion tests. It is found that the thermal impact of high-temperature flame and supersonic erosion of corrosive melting particle jet of the SAMHSE lead to surface defects of micro-cracks, denudation and corrosive residue. Some defects reach to metal base becoming to "corrosive channels". Repetitive HTASED may cause ablation-adhesion fatigue stress, which enhances the surface corrosion and destruction. HTASED and corrosion are related to the type of a SAMHSE fuel and experience of the launcher. Surface destruction is related to synergistic effects of the HTASED. The ablated and failed Al or steel surface is liable to electrochemical corrosion characterized by pitting in humid and salt-spray environment.

  10. Fundamental aspects of stress corrosion cracking of copper relevant to the Swedish deep geologic repository concept

    Energy Technology Data Exchange (ETDEWEB)

    Bhaskaran, Ganesh; Carcea, Anatolie; Ulaganathan, Jagan; Wang, Shengchun; Huang, Yin; Newman, Roger C. [Dept. of Chemical Engineering and Applied Chemistry, Univ. of Toronto, Toronto (Canada)

    2013-03-15

    Phosphorus-doped oxygen-free copper will be used as the outer barrier in canisters that will contain spent nuclear fuel in the proposed Swedish underground repository. The possibility of stress corrosion cracking (SCC) is a concern, in view of isolated reports of cracking or intergranular corrosion of pure copper in sulfide solutions. This concern was addressed in the present work using copper tensile specimens provided by SKB. Methods included slow strain rate testing, constant strain tensile testing, electrochemical and surface analytical studies of corrosion products, and electron backscatter diffraction analysis of grain orientation effects on corrosion. The base solutions were prepared from NaCl or synthetic sea water with addition of varying amounts of sodium sulfide at room temperature and 80 degree Celsius. No SCC was found in any of the testing, for a range of sulfide concentrations from 5-50 mM at room temperature or 8 C, including tests where small anodic or cathodic potential displacements were applied from the open-circuit (corrosion) potential. Neither was SCC found in constant-strain immersion testing with very large strain. The Cu2S corrosion product is generally very coarse, fragile, and easily spalled off in severe corrosion environments, i.e. high sulfide concentration, high temperature, less perfect de aeration, etc. But it could also consist of very fine grains, relatively compact and adherent, on particular grain orientations when it was formed on an electro polished surface in a very well-deaerated solution. These orientations have not yet been identified statistically, although some preference for thin, adherent films was noted on orientations close to (100). The notion that the corrosion reaction is always controlled by inward aqueous-phase diffusion of sulfide may thus not be unconditionally correct for this range of sulfide concentrations; however it is hard to distinguish the role of diffusion within pores in the film. In the actual

  11. Analysis of Cracking Mode of Anchor Structure of Underground Engineering Induced by Reinforcement Corrosion

    Directory of Open Access Journals (Sweden)

    Wantao Ding

    2014-02-01

    Full Text Available Based on elastic theory and assumption of maximum tensile-stress failure criterion, together with construction process of anchor structure and rust expansion critical process, this study proposed a simplified reinforcement rust expansion mechanical model of anchor structure system. Elastic criterion of different initial cracking mode was rewarded under different stress ratios. According to analysis of critical cracking mode of different medium, cracking order of mortar and surrounding rock depended on their material parameters, in-situ stress and thickness of mortar cover. Critical cracking conditions of different medium without effect of in-situ stress was the same as that of considering in-situ stress while k is equal to 3 or 1/3. And engineering example shows that three different cracking modes exist under different stress ratios. The result provides a useful reference for analysis of mechanical deterioration mechanism of anchor structure and design of support structure of underground engineering.

  12. The effect of heat treatment and test parameters on the aqueous stress corrosion cracking of D6AC steel

    Science.gov (United States)

    Gilbreath, W. P.; Adamson, M. J.

    1974-01-01

    The crack growth behavior of D6AC steel as a function of stress intensity, stress and corrosion history and test technique, under sustained load in natural seawater, 3.3 percent NaCl solution, distilled water, and high humidity air was investigated. Reported investigations of D6AC were considered with emphasis on thermal treatment, specimen configuration, fracture toughness, crack-growth rates, initiation period, threshold, and the extension of corrosion fatigue data to sustained load conditions. Stress history effects were found to be most important in that they controlled incubation period, initial crack growth rates, and apparent threshold.

  13. Microstructural investigation of vintage pipeline steels highly susceptible to stress corrosion cracking

    Science.gov (United States)

    Torres, Monica

    The use of pipelines for the transmission of gas offers not only efficiency, but a number of economic advantages. Nevertheless, pipelines are subject to aggressive operating conditions and environments which can lead to in-service degradation [1] and thus to failures. These failures can have catastrophic consequences, such as environmental damage and loss of life [2]. One of the most dangerous threats to pipeline integrity is stress corrosion cracking (SCC). Despite the substantial progress that has been achieved in the field, due to the complex nature of this phenomenon there is still not a complete understanding of this form of external corrosion. This makes its detection and prevention a challenge and therefore a risk to pipeline integrity, and most importantly, to the safety of the population. SCC cracks are the result of the interaction between a corrosive environment, applied stresses, and a susceptible microstructure. To date, what defines a susceptible microstructure remains ambiguous, as SCC has been observed in a range of steel grades, microstructures, chemical composition, and grain sizes. Therefore, in order to be able to accurately predict and prevent this hazardous form of corrosion, it is imperative to advance our knowledge on the subject and gain a better understanding on the microstructural features of highly susceptible pipeline materials, especially in the subsurface zone where crack nucleation must take place. Therefore, a microstructural characterization of the region near the surface layer was carried-out utilizing TEM. TEM analysis revealed the dislocation character, ferrite morphology, and apparent carbide precipitation in some grain boundaries. Furthermore, light microscopy, SEM, and hardness testing were performed to expand our knowledge on the microscopical features of highly SCC susceptible service components. This investigation presents a new approach to SCC characterization, which exposed the sub-surface region microscopical

  14. Effect of layerwise structural inhomogeneity on stress- corrosion cracking of steel tubes

    Science.gov (United States)

    Perlovich, Yu A.; Krymskaya, O. A.; Isaenkova, M. G.; Morozov, N. S.; Fesenko, V. A.; Ryakhovskikh, I. V.; Esiev, T. S.

    2016-04-01

    Based on X-ray texture and structure analysis data of the material of main gas pipelines it was shown that the layerwise inhomogeneity of tubes is formed during their manufacturing. The degree of this inhomogeneity affects on the tendency of tubes to stress- corrosion cracking under exploitation. Samples of tubes were cut out from gas pipelines located under various operating conditions. Herewith the study was conducted both for sections with detected stress-corrosion defects and without them. Distributions along tube wall thickness for lattice parameters and half-width of X-ray lines were constructed. Crystallographic texture analysis of external and internal tube layers was also carried out. Obtained data testifies about considerable layerwise inhomogeneity of all samples. Despite the different nature of the texture inhomogeneity of gas pipeline tubes, the more inhomogeneous distribution of texture or structure features causes the increasing of resistance to stress- corrosion. The observed effect can be explained by saturation with interstitial impurities of the surface layer of the hot-rolled sheet and obtained therefrom tube. This results in rising of lattice parameters in the external layer of tube as compared to those in underlying metal. Thus, internal layers have a compressive effect on external layers in the rolling plane that prevents cracks opening at the tube surface. Moreover, the high mutual misorientation of grains within external and internal layers of tube results in the necessity to change the moving crack plane, so that the crack growth can be inhibited when reaching the layer with a modified texture.

  15. Corrosion of steel in cracked concrete: Chloride microanalysis and service life predictions

    NARCIS (Netherlands)

    Pacheco Farias, J.

    2015-01-01

    Reinforcement corrosion is frequently considered as the predominant degradation mechanism affecting reinforced concrete structures. Reinforced concrete structures are commonly subject to harsh environmental and loading conditions in which aggressive species can penetrate. Chlorides, present in

  16. Corrosion of steel in cracked concrete: Chloride microanalysis and service life predictions

    NARCIS (Netherlands)

    Pacheco Farias, J.

    2015-01-01

    Reinforcement corrosion is frequently considered as the predominant degradation mechanism affecting reinforced concrete structures. Reinforced concrete structures are commonly subject to harsh environmental and loading conditions in which aggressive species can penetrate. Chlorides, present in seaw

  17. Prevention of stress-corrosion cracking in nuclear waste storage tanks

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R S

    1984-01-01

    Stress corrosion cracking (SCC) has occurred in the early versions of carbon steel primaries of nuclear waste tanks at the Savannah River Plant. (Secondary containment was provided by a vessel surrounding the lower portion of the primary tank.) Evaporated alkaline nitrate wastes in the form of crystallized salts are being dissolved from some of these tanks for transfer to new tanks of a different design. To prevent the SCC sequence from occurring during salt dissolution, the levels of inhibitors required to prevent cracking at yield stresses were determined. Special statistically designed experiments were performed to evaluate the probability of cracking under the combined influences of nitrate, nitrite, hydroxide, and temperature. Experimentlly, samples were tested by a potentially controlled constant extension rate test and by wedge opening loaded samples. Two equations were derived by multivariable regression analyses that correlated probability of cracking as the dependent variable to nitrate, nitrite, and hydroxide concentrations and temperature as the independent variables. From these equations, simple operating standards were developed by setting the probability of cracking equal to zero and solving for the four independent variables. 15 references, 15 figures, 8 tables.

  18. Corrosion and cracking behaviour of steel and alloys in liquid H{sub 2}S

    Energy Technology Data Exchange (ETDEWEB)

    Longaygue, X. [Institut Francais du Petrole, 1 et 4 avenue de Bois Preau 92852 Rueil-Malmaison (France); Duval, S. [Institut Francais du Petrole, BP no 3, 69390 Vernaison (France)

    2004-07-01

    When oil and gas wells with very high partial pressure of H{sub 2}S, e.g. H{sub 2}S-rich gas, are under production, the presence of liquid H{sub 2}S is highly probable in the process operations. Until now, corrosion engineers and materials designers have paid little attention to this situation because it is rarely encountered in practice. However, such a scenario recently met an increasing interest in the context of the Sprex development, a new H{sub 2}S pre-extraction process used for the treatment of very sour natural gases, which produces the separated acid gases as a liquid phase for re-injection to a disposal reservoir. It is generally accepted that pure liquid H{sub 2}S is not corrosive by itself towards carbon or low alloy steels, but the presence of water in production and reservoir fluids could make this medium much more corrosive, although this latter assumption is poorly documented. The aim of this paper is to present the corrosion and cracking behaviour of a pipeline carbon steel and of corrosion resistant alloys (CRA) (with Cr > 16%) after exposure to the following media: i) liquid H{sub 2}S saturated with water, and ii) liquid H{sub 2}O saturated with H{sub 2}S. For both solutions, the addition of solid sulphur on some specimens was considered to take into account the possible introduction of oxygen into the system, followed by a reaction with H{sub 2}S. The tests were performed at 80 deg. C in a laboratory autoclave where both phases coexisted, using U-bend specimens as well as rectangular corrosion coupons. The main conclusion of this study is that liquid H{sub 2}S is rather less critical for corrosion and cracking of construction alloys than 'classical' sour solutions, like H{sub 2}S-saturated water. As a consequence, the materials selection will be governed by the same criteria, with the following alternatives: i) use of carbon steels in conjunction with corrosion inhibitors, e.g. higher operation expense; or ii) selection of a CRA

  19. Evaluation of irradiation assisted stress corrosion cracking (IASCC) of type 316 stainless steel irradiated in FBR

    Energy Technology Data Exchange (ETDEWEB)

    Tsukada, T. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Jitsukawa, S. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Shiba, K. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan)); Sato, Y. (Power Reactor and Nuclear Fuel Development Corp., Oarai, Ibaraki (Japan)); Shibahara, I. (Power Reactor and Nuclear Fuel Development Corp., Oarai, Ibaraki (Japan)); Nakajima, H. (Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan))

    1993-12-01

    Type 316 stainless steel from the core of the experimental fast breeder reactor (FBR) JOYO was examined by the slow strain rate tensile (SSRT) test in pure, oxygenated-water and air and by the electrochemical potentiokinetic reactivation (EPR) test to evaluate a susceptibility to the irradiation assisted stress corrosion cracking (IASCC) and the radiation-induced segregation (RIS). The solution annealed and 20% cold-worked materials had been irradiated at 425 C to a neutron fluence of 8.3x10[sup 26] n/m[sup 2] (> 0.1 MeV) which is equivalent to 40 displacement per atom (dpa). Intergranular cracking was induced by the SSRT in water at 200 and 300 C, but was not observed on specimen tested in water at 60 C and in air at 300 C. This indicates that irradiation increased a susceptibility to stress corrosion cracking (SCC) in water. After the EPR test, grain boundary etching was observed in addition to grain face etching. This suggests Cr depletion may have occurred both at grain boundary and at defect clusters during the irradiation. The results are compared with the behavior of similar materials irradiated with different neutron spectrum. (orig.)

  20. Aircraft corrosion and crack inspection using advanced magneto-optic imaging technology

    Science.gov (United States)

    Thome, David K.; Fitzpatrick, Gerald L.; Skaugset, Richard L.; Shih, William C.

    1996-11-01

    A next generation magneto-optic imaging system, the MOI 303, has recently been introduced with the ability to generate real-time, complete, 2D eddy current images of cracks and corrosion in aircraft. The new imaging system described features advanced, digital remote control operation and on- screen display of setup parameters for ease of use. This instrument gives the inspector the capability to more rapidly scan large surfaces areas. The magneto-optic/eddy current imaging technology has already been formally approved for inspection of surface cracking on an aircraft fuselage. The improved magneto-optic imager is now poised to aid rapid inspection for corrosion and subsurface cracking. Previous magneto-optic imaging systems required the inspector to scan the surface twice for complete inspection coverage: a second scan was necessary with the imager rotated about 90 degrees from the orientation of the first pass. However, by providing eddy current excitation simultaneously from two orthogonal directions, complete, filled-in magneto-optic images are now generated regardless of the orientation of the imager. THese images are considerably easier to interpret and evaluate. In addition, there is a synergism obtained in applying eddy current excitation simultaneously in multiple directions: better penetration is obtained and the resulting images have better signal to noise levels compared to those produced with eddy current excitation applied only in one direction. Examples of these improved images are presented.

  1. Mitigation of Intergranular Stress Corrosion Cracking in Al-Mg by Electrochemical Potential Control

    Science.gov (United States)

    McMahon, M. E.; Scully, J. R.; Burns, J. T.

    2017-08-01

    Intergranular stress corrosion cracking in the Al-Mg alloy AA5456-H116 is suppressed via cathodic polarization in 0.6 M NaCl, saturated (5.45 M) NaCl, 2 M MgCl2, and saturated (5 M) MgCl2. Three zones of intergranular stress corrosion cracking (IG-SCC) susceptibility correlate with pitting potentials of unsensitized AA5456-H116 and pure β phase (Al3Mg2) in each solution. These critical potentials reasonably describe the influence of α Al matrix and β phase dissolution rates on IG-SCC severity. Complete inhibition occurred at applied potentials of -1.0 V and -1.1 V versus saturated calomel electrode ( V SCE) in 0.6 M NaCl. Whereas only partial mitigation of IG-SCC was achieved at -0.9 V SCE in 0.6 M NaCl and at -0.9, -1.0, and -1.1 V SCE in the more aggressive environments. Correlation of pitting potentials in bulk environments with IG-SCC behavior suggests an effect of bulk environment [Cl-] and pH on the stabilized crack tip chemistry.

  2. NASCRAC - A computer code for fracture mechanics analysis of crack growth

    Science.gov (United States)

    Harris, D. O.; Eason, E. D.; Thomas, J. M.; Bianca, C. J.; Salter, L. D.

    1987-01-01

    NASCRAC - a computer code for fracture mechanics analysis of crack growth - is described in this paper. The need for such a code is increasing as requirements grow for high reliability and low weight in aerospace components. The code is comprehensive and versatile, as well as user friendly. The major purpose of the code is calculation of fatigue, corrosion fatigue, or stress corrosion crack growth, and a variety of crack growth relations can be selected by the user. Additionally, crack retardation models are included. A very wide variety of stress intensity factor solutions are contained in the code, and extensive use is made of influence functions. This allows complex stress gradients in three-dimensional crack problems to be treated easily and economically. In cases where previous stress intensity factor solutions are not adequate, new influence functions can be calculated by the code. Additional features include incorporation of J-integral solutions from the literature and a capability for estimating elastic-plastic stress redistribution from the results of a corresponding elastic analysis. An example problem is presented which shows typical outputs from the code.

  3. Surface characteristics and mechanical properties of high-strength steel wires in corrosive conditions

    Science.gov (United States)

    Xu, Yang; Li, Shunlong; Li, Hui; Yan, Weiming

    2013-04-01

    Cables are always a critical and vulnerable type of structural components in a long-span cable-stayed bridge in normal operation conditions. This paper presents the surface characteristics and mechanical performance of high-strength steel wires in simulated corrosive conditions. Four stress level (0MPa, 300MPa, 400MPa and 500MPa) steel wires were placed under nine different corrosive exposure periods based on the Salt Spray Test Standards ISO 9227:1990. The geometric feathers of the corroded steel wire surface were illustrated by using fractal dimension analysis. The mechanical performance index including yielding strength, ultimate strength and elastic modulus at different periods and stress levels were tested. The uniform and pitting corrosion depth prediction model, strength degradation prediction model as well as the relationship between strength degradation probability distribution and corrosion crack depth would be established in this study.

  4. Intergranular stress corrosion cracking of type 304 stainless steels treated with inhibitive chemicals in high temperature pure water

    Energy Technology Data Exchange (ETDEWEB)

    Yeh, T.K. [Nuclear Science and Technology Development Center, National Tsing-Hua Univ. Taiwan (China); Lee, M.Y.; Tsai, C.H. [Department of Engineering and System Science, National Tsing-Hua Univ. Taiwan (China)

    2002-07-01

    Electrochemical potentiodynamic polarizations, electrochemical corrosion potential (ECP) measurements and slow strain rate tensile (SSRT) tests were conducted to investigate the intergranular stress corrosion cracking (IGSCC) characteristics of Type 304 stainless steels treated with inhibitive chemicals in simulated boiling water reactor (BWR) environments. A number of thermally sensitized specimens were prepared and were pre-oxidized in a 288 C environment with the presence of 300 ppb dissolved oxygen for 360 hours. Most of the specimens were then treated with various chemicals including powdered zirconium oxide (ZrO{sub 2}), powdered titanium oxide (TiO{sub 2}), and zirconyl nitrate [ZrO(NO{sub 3}){sub 2}] via static immersion at 90 C, 150 C, and 200 C. Test environments were specifically designed in a circulation loop to create a dissolved oxygen concentration of 300 ppb. Test results showed that the corrosion current densities of all treated specimens were lower than that of the untreated, pre-oxidized specimen at ambient temperature in a solution mixed with 1 mM K{sub 3}Fe(CN){sub 6} and 1 mM K{sub 4}Fe(CN){sub 6}. The ECPs of the treated specimens could be lower or higher than that of the pre-oxidized one at 288 C, depending upon the type of treating chemical and the treating temperature. In addition, IGSCC was observed on all specimens (treated or untreated) in the same environment. However, the untreated specimen exhibited lower elongation, shorter failure time, and more secondary cracks on the side surfaces. It was therefore suggested that inhibitive chemicals such as ZrO{sub 2}, TiO{sub 2}, and ZrO(NO{sub 3}){sub 2} did provide a certain degree of enhancement in improving the mechanical behavior of the treated specimens and in prolonging the IGSCC initiation time. (authors)

  5. Stress Corrosion Cracking of the Drip Shield, the Waste Package Outer Barrier, and the Stainless Steel Structural Material

    Energy Technology Data Exchange (ETDEWEB)

    G. Gordon

    2004-10-13

    Stress corrosion cracking is one of the most common corrosion-related causes for premature breach of metal structural components. Stress corrosion cracking is the initiation and propagation of cracks in structural components due to three factors that must be present simultaneously: metallurgical susceptibility, critical environment, and static (or sustained) tensile stresses. This report was prepared according to ''Technical Work Plan for: Regulatory Integration Modeling and Analysis of the Waste Form and Waste Package'' (BSC 2004 [DIRS 171583]). The purpose of this report is to provide an evaluation of the potential for stress corrosion cracking of the engineered barrier system components (i.e., the drip shield, waste package outer barrier, and waste package stainless steel inner structural cylinder) under exposure conditions consistent with the repository during the regulatory period of 10,000 years after permanent closure. For the drip shield and waste package outer barrier, the critical environment is conservatively taken as any aqueous environment contacting the metal surfaces. Appendix B of this report describes the development of the SCC-relevant seismic crack density model (SCDM). The consequence of a stress corrosion cracking breach of the drip shield, the waste package outer barrier, or the stainless steel inner structural cylinder material is the initiation and propagation of tight, sometimes branching, cracks that might be induced by the combination of an aggressive environment and various tensile stresses that can develop in the drip shields or the waste packages. The Stainless Steel Type 316 inner structural cylinder of the waste package is excluded from the stress corrosion cracking evaluation because the Total System Performance Assessment for License Application (TSPA-LA) does not take credit for the inner cylinder. This document provides a detailed description of the process-level models that can be applied to assess the

  6. Hierarchical Petascale Simulation Framework for Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Vashishta, Priya

    2014-12-01

    Reaction Dynamics in Energetic Materials: Detonation is a prototype of mechanochemistry, in which mechanically and thermally induced chemical reactions far from equilibrium exhibit vastly different behaviors. It is also one of the hardest multiscale physics problems, in which diverse length and time scales play important roles. The CACS group has performed multimillion-atom reactive MD simulations to reveal a novel two-stage reaction mechanism during the detonation of cyclotrimethylenetrinitramine (RDX) crystal. Rapid production of N2 and H2O within ~10 ps is followed by delayed production of CO molecules within ~ 1 ns. They found that further decomposition towards the final products is inhibited by the formation of large metastable C- and O-rich clusters with fractal geometry. The CACS group has also simulated the oxidation dynamics of close-packed aggregates of aluminum nanoparticles passivated by oxide shells. Their simulation results suggest an unexpectedly active role of the oxide shell as a nanoreactor.

  7. Hydrogen-increased dezincification layer-induced stress and susceptibility to stress corrosion cracking of brass

    Institute of Scientific and Technical Information of China (English)

    李会录; 高克玮; 褚武扬; 刘亚萍; 乔利杰

    2003-01-01

    Dezincification layer formed during corrosion or stress corrosion cracking (SCC) of brass in an ammonia solution could induce an additive stress. The effect of hydrogen on the dezincification layer-induced stress and the susceptibility to SCC were studied. The dezincification layer-induced stress was measured using the deflection method and the flowing stress differential method, respectively. The latter measures the difference between the flowing stress of a specimen before unloading and the yield stress of the same specimen after unloading and forming a dezincification layer. The susceptibility to SCC was measured using slow strain rate test. Results show that both the dezincification layer-induced stress and the susceptibility to SCC increase with increasing hydrogen concentration in a specimen. This implies that hydrogen-enhanced dezincification layer-induced stress is consistence with the hydrogen-increased susceptibility to SCC of brass in the ammonia solution.

  8. Estimation of elastic modulus of reinforcement corrosion products using inverse analysis of digital image correlation measurements for input in corrosion-induced cracking model

    DEFF Research Database (Denmark)

    Pease, Bradley Justin; Michel, Alexander; Thybo, Anna Emilie A.;

    2012-01-01

    A combined experimental and numerical approach for estimating the elastic modulus of reinforcement corrosion products is presented. Deformations between steel and mortar were measured using digital image correlation during accelerated corrosion testing at 100 μA/cm2 (~1.16 mm/year). Measured...... deformations were compared to a numerical corrosion model that considers electrochemical, transport, and mechanical processes, including penetration of corrosion products into a ‘corrosion-accommodating region,’ provided by the mortar’s capillary porosity, directly surrounding the steel. Comparing model...... and experimental results provides an order-of-magnitude approximation of corrosion product stiffness of 2.0 GPa....

  9. Laser Peening for Mitigation of Stress Corrosion Cracking at Welds in Marine Aluminum

    Science.gov (United States)

    2011-06-01

    Second Reader: Joseph C. Farmer THIS PAGE INTENTIONALLY LEFT BLANK i REPORT DOCUMENTATION PAGE Form Approved OMB No. 0704-0188 Public reporting burden...Advisor Joseph C. Farmer Second Reader Knox Millsaps Chair, Department of Mechanical and Aerospace Engineering iv THIS PAGE...Cruisers, in Defense News2010. p. 4. [4] K. N. Tran, M. R. Hill, et al., Welding Journal, 85 (2006) 28. [5] M. G. Fontana , Stress Corrosion, in Corrosion

  10. INHIBITION OF STRESS CORROSION CRACKING OF CARBON STEEL STORAGE TANKS AT HANFORD

    Energy Technology Data Exchange (ETDEWEB)

    BOOMER, K.D.

    2007-01-31

    The stress corrosion cracking (SCC) behavior of A537 tank steel was investigated in a series of environments designed to simulate the chemistry of legacy nuclear weapons production waste. Tests consisted of both slow strain rate tests using tensile specimens and constant load tests using compact tension specimens. Based on the tests conducted, nitrite was found to be a strong SCC inhibitor. Based on the test performed and the tank waste chemistry changes that are predicted to occur over time, the risk for SCC appears to be decreasing since the concentration of nitrate will decrease and nitrite will increase.

  11. Intergranular stress corrosion cracking of welded ferritic stainless steels in high temperature aqueous environments

    Energy Technology Data Exchange (ETDEWEB)

    Fukuzuka, Toshio; Shimogori, Kazutoshi; Fujiwara, Kazuo; Tomari, Haruo (Kobe Steel Ltd. (Japan). Central Research and Development Lab.); Kanda, Masao

    1982-07-01

    In considering the application of ferritic stainless steels to heat exchanger tubing materials for moisture separator-reheaters in LWRs, the effects of environmental conditions (temperature, chloride, dissolved oxygen, pH), thermal history, and steel composition (content of C, N, Cr and Ti) on the Inter-Granular Stress Corrosion Cracking (IGSCC) in high temperature aqueous environments, were studied. The IGSCC was proved to depend on steel composition and thermal history rather than environment. From these results, a steel was designed to prevent IGSCC of the welding HAZ for 18Cr and 13Cr steels.

  12. High-Performance Laser Peening for Effective Mitigation of Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    Hackel, L; Hao-Lin, C; Wong, F; Hill, M

    2002-10-02

    Stress corrosion cracking (SCC) in the Yucca Mountain waste package closure welds is believed to be the greatest threat to long-term containment. Use of stress mitigation to eliminate tensile stresses resulting from welding can prevent SCC. A laser technology with sufficient average power to achieve high throughput has been developed and commercially deployed with high peak power and sufficiently high average power to be an effective laser peening system. An appropriately applied version of this process could be applied to eliminate SCC in the waste package closure welds.

  13. Formation mechanism of internal cracks in continuously cast slab

    Institute of Scientific and Technical Information of China (English)

    Guosen Zhu; Xinhua Wang; Huixiang Yu; Jiongming Zhang; Wanjun Wang

    2004-01-01

    In order to make clear the formation mechanism of centerline cracks in continuously cast slabs, the form, distribution and other characteristics of the cracks were analyzed. The final solidification point, surface temperature of the slabs and strain in solidifying shell were investigated. The results were that: (1) Five relatively low temperature zones exist on slab surface below the three water spraying nozzles and near the two edges, respectively, which corresponds to the places of centerline cracks and triangle-zone cracks. (2) Centerline cracks and triangle-zone cracks occur because of weak secondary cooling, uneven cooling along slab width,and large variation of roll gap. (3) After minimizing the variation of roll gap and applying the new secondary cooling pattern, the occurring frequency of centerline and triangle-zone cracks minimizes to zero.

  14. Lead-induced stress-corrosion cracking of alloy 600 in plausible steam generator crevice environments

    Energy Technology Data Exchange (ETDEWEB)

    Wright, M.D. [Atomic Energy of Canada Limited, Chalk River, Ontario (Canada); Manolescu, A. [Ontario Hydro Technologies, Toronto, Ontario (Canada); Mirzai, M. [Ontario Hydro, Toronto, Ontario (Canada)

    1999-03-01

    Laboratory stress-corrosion cracking (SCC) test environments were developed to simulate crevice chemistries representative of Bruce Nuclear Generating Station A (BNPD A) steam generators (SGs); these test environments were used to determine the susceptibility of Alloy 600 to lead-induced SCC under plausible SG conditions. Test environments were based on plant SG hideout return data and analysis of removed tubes and deposits. Deviations from the normal near-neutral crevice pH environment were considered to simulate possible faulted excursion crevice chemistry and to bound the postulated crevice pH range of 3 to 9 (at temperature). The effect of lead contamination up to 1000 ppm, but with an emphasis on the 100- to 500-ppm range, was determined. SCC susceptibility was investigated using constant extension rate tensile (CERT) tests and encapsulated C-ring tests. CERT tests were performed at 305 degrees C on tubing representative of BNPD A SG U-bends. The C-ring test method allowed a wider test matrix, covering 3 temperatures (280 degrees C, 304 degrees C and 315 degrees C), 3 strain levels (0.2%, 2% and 4%), and tubing representative of U-bends plus tubing given a simulated stress relief to represent material at the tube sheet. The results of this test program confirmed that in the absence of lead contamination, cracking does not occur in these concentrated, 3.3 to 8.9 pH range, crevice environments. Also, it appears that the concentrated crevice environments suppress lead-induced cracking relative to that seen in all-volatile-treatment (AVT) water. For the (static) C-ring tests, lead-induced SCC was only produced in the near-neutral crevice environment and was more severe at 500 ppm than at 100 ppm PbO. This trend was also observed in CERT tests, but some cracking-grain boundary attack occurred in acidic (pH 3.3) and alkaline (pH 8.9) environments. The C-ring tests indicated that a certain amount of resistance to cracking was imparted by simulated stress relief of

  15. Origins of Negative Strain Rate Dependence of Stress Corrosion Cracking Initiation in Alloy 690, and Intergranular Crack Formation in Thermally Treated Alloy 690

    Science.gov (United States)

    Kim, Young Suk; Kim, Sung Soo

    2016-09-01

    We show that enhanced stress corrosion cracking (SCC) initiation in cold-rolled Alloy 690 with decreasing strain rate is related to the rate of short-range ordering (SRO) but not to the time-dependent corrosion process. Evidence for SRO is provided by aging tests on cold-rolled Alloy 690 at 623 K and 693 K (350 °C and 420 °C), respectively, which demonstrate its enhanced lattice contraction and hardness increase with aging temperature and time, respectively. Secondary intergranular cracks formed only in thermally treated and cold-rolled Alloy 690 during SCC tests, which are not SCC cracks, are caused by its lattice contraction by SRO before SCC tests but not by the orientation effect.

  16. Effect of pH Value on Stress Corrosion Cracking of X70 Pipeline Steel in Acidic Soil Environment

    Institute of Scientific and Technical Information of China (English)

    Zhiyong LIU; Cuiwei DU; Xin ZHANG; Fuming WANG; Xiaogang LI

    2013-01-01

    The effect of pH value on the stress corrosion cracking (SCC) of API X70 pipeline steel in simulated acidic soil solutions was investigated by using slow strain rate test,electrochemical polarization curves,electrochemical impedance spectroscopy,and scanning electron microscopy.pH plays an important role in the susceptibility and electrochemical mechanism of SCC.The pH higher than 5 has no significant effect on electrochemical processes.By contrast,the pH lower than 5 intensifies cathodic hydrogen evolution reactions,thus increasing the cathodic current and corrosion potential.Under different pH values,the SCC mechanism of X70 pipeline steel varies among anodic dissolution (AD),hydrogen embrittlement (HE),and the combination of AD and HE (AD + HE) with variations of applied potential.At-850 mVSCE,the SCC mechanism is HE if pH is less than 4 or AD + HE if pH value is more positive.

  17. Fracture Mechanical Markov Chain Crack Growth Model

    DEFF Research Database (Denmark)

    Gansted, L.; Brincker, Rune; Hansen, Lars Pilegaard

    1991-01-01

    On the basis of the B-model developed in [J. L. Bogdanoff and F. Kozin, Probabilistic Models of Cumulative Damage. John Wiley, New York (1985)] a new numerical model incorporating the physical knowledge of fatigue crack propagation is developed. The model is based on the assumption that the crack...

  18. Allowing for surface preparation in stress corrosion cracking modelling; Prise en compte de l`etat de surface dans la modelisation de la fissuration par corrosion sous contrainte

    Energy Technology Data Exchange (ETDEWEB)

    Berge, P.; Buisine, D. [Electricite de France (EDF), 92 - Clamart (France); Gelpi, A. [FRAMATOME, 92 - Paris-La-Defence (France)

    1997-12-31

    When a 600 alloy component is significantly deformed during installation, by welding, rolling, bending, its stress corrosion cracking in Pressurized Water Nuclear Reactor`s primary coolant, is significantly changed by the initial surface treatment. Therefore, the crack initiated time may be reduced by several orders of magnitude for certain surfaces preparations. Allowing for cold working of the surface, for which modelling is proposed, depends less on the degree of cold work then on the depths of the hardened layers. Honing hardens the metal over depths of about one micron for vessel head penetrations, for example, and has little influence on subsequent behaviour after the part deforms. On the other hand, coarser turning treatment produces cold worked layers which can reach several tens of microns and can very significantly reduce the initiation time compared to fine honing. So evaluation after depths of hardening is vital on test pieces for interpreting laboratory results as well as on service components for estimating their service life. Suppression by mechanical or chemical treatment of these layers, after deformation, seems to be the most appropriate solution for reducing over-stressing connected with surface treatment carried out before deformation. (author). 14 refs.

  19. Effect of a novel three-step aging on strength, stress corrosion cracking and microstructure of AA7085

    Institute of Scientific and Technical Information of China (English)

    陈送义; 陈康华; 董朋轩; 叶升平; 黄兰萍; 阳代军

    2016-01-01

    The influence of a novel three-step aging on strength, stress corrosion cracking (SCC) and microstructure of AA7085 was investigated by tensile testing and slow strain rate testing combined with transmission electron microscopy (TEM). The results indicate that with the increase of second-step aging time of two-step aging, the mechanical properties increase first and then decrease, while the SCC resistance increases. Compared with two-step aging, three-step aging treatment improves SCC resistance and the strength increases by about 5%. The effects of novel three-step aging on strength and SCC resistance are explained by the role of matrix precipitates and grain boundary precipitates, respectively.

  20. Anomalous mechanical behavior and crack growth of oxide glasses

    Science.gov (United States)

    Seaman, Jared Hilliard

    This thesis is concerned with analytically describing anomalous mechanical behaviors of glass. A new slow crack growth model is presented that considers a semi-elliptical crack in a cylindrical glass rod subjected to 4-point bending that is both loaded statically and under a time-dependent load. This model is used to explain a suppression of the loading-rate dependency of ion-exchanged strengthened glass. The stress relaxation behavior of an ion-exchanged strengthened glass is then analyzed in view of a newly observed water-assisted surface stress relaxation mechanism. By making refinements to a time-dependent Maxwell material model for stress buildup and relaxation, the anomalous subsurface compressive stress peak in ion-exchanged strengthened glass is explained. The notion of water-assisted stress relaxation is extended to the crack tip, where high tensile stresses exist. A toughening effect has historically been observed for cracks aged at subcritical stress intensity factors, where crack tip stress relaxation is hypothesized. A simple fracture mechanics model is developed that estimates a shielding stress intensity factor that is then superimposed with the far-field stress intensity factor. The model is used to estimate anomalous "restart" times for aged cracks. The same model predicts a non-linear crack growth rate for cracks loaded near the static fatigue limit. Double cantilever beam slow crack growth experiments were performed and new slow crack growth data for soda-lime silicate glass was collected. Interpretation of this new experimental slow crack growth data suggests that the origin of the static fatigue limit in glass is due to water-assisted stress relaxation. This thesis combines a number of studies that offer a new unified understanding of historical anomalous mechanical behaviors of glass. These anomalies are interpreted as simply the consequence of slow crack growth and water-assisted surface stress relaxation.

  1. Electrochemical investigation on the hydrogen permeation behavior of 7075-T6 Al alloy and its influence on stress corrosion cracking

    Science.gov (United States)

    Zheng, Chuan-bo; Yan, Bing-hao; Zhang, Ke; Yi, Guo

    2015-07-01

    The hydrogen permeation behavior and stress corrosion cracking (SCC) susceptibility of precharged 7075-T6 Al alloy were investigated in this paper. Devanthan-Stachurski (D-S) cell tests were used to measure the apparent hydrogen diffusivity and hydrogen permeation current density of specimens immersed in 3.5wt% NaCl solution. Electrochemical experiment results show that the SCC susceptibility is low during anodic polarization. Both corrosion pits and hydrogen-induced cracking are evident in scanning electron microscope images after the specimens have been charging for 24 h.

  2. Stress corrosion cracking behavior of annealed and cold worked 316L stainless steel in supercritical water

    Energy Technology Data Exchange (ETDEWEB)

    Sáez-Maderuelo, A., E-mail: alberto.saez@ciemat.es; Gómez-Briceño, D.

    2016-10-15

    Highlights: • The alloy 316L is susceptible to stress corrosion cracking in supercritical water. • The susceptibility of alloy 316L increases with temperature and plastic deformation. • Dynamic strain ageing processes may be active in the material. - Abstract: The supercritical water reactor (SCWR) is one of the more promising designs considered by the Generation IV International Forum due to its high thermal efficiency and improving security. To build this reactor, standardized structural materials used in light water reactors (LWR), like austenitic stainless steels, have been proposed. These kind of materials have shown an optimum behavior to stress corrosion cracking (SCC) under LWR conditions except when they are cold worked. It is known that physicochemical properties of water change sharply with pressure and temperature inside of the supercritical region. Owing to this situation, there are several doubts about the behavior of candidate materials like austenitic stainless steel 316L to SCC in the SCWR conditions. In this work, alloy 316L was studied in deaerated SCW at two different temperatures (400 °C and 500 °C) and at 25 MPa in order to determine how changes in this variable influence the resistance of this material to SCC. The influence of plastic deformation in the behavior of alloy 316L to SCC in SCW was also studied at both temperatures. Results obtained from these tests have shown that alloy 316L is susceptible to SCC in supercritical water reactor conditions where the susceptibility of this alloy increases with temperature. Moreover, prior plastic deformation of 316L SS increased its susceptibility to environmental cracking in SCW.

  3. Simulated Service and Stress Corrosion Cracking Testing for Friction Stir Welded Spun Formed Domes

    Science.gov (United States)

    Stewart, Thomas J.; Torres, Pablo D.; Caratus, Andrei A.; Curreri, Peter A.

    2010-01-01

    Simulated service testing (SST) development was required to help qualify a new 2195 aluminum lithium (Al-Li) alloy spin forming dome fabrication process for the National Aeronautics and Space Administration (NASA) Exploration Development Technology Program. The application for the technology is to produce high strength low weight tank components for NASA s next generation launch vehicles. Since plate material is not currently manufactured large enough to fabricate these domes, two plates are joined by means of friction stir welding. The plates are then pre-contour machined to near final thicknesses allowing for a thicker weld land and anticipating the level of stretch induced by the spin forming process. The welded plates are then placed in a spin forming tool and hot stretched using a trace method producing incremental contours. Finally the dome receives a room temperature contour stretch to final dimensions, heat treatment, quenching, and artificial aging to emulate a T-8 condition of temper. Stress corrosion cracking (SCC) tests were also performed by alternate immersion in a sodium chloride (NaCl) solution using the typical double beam assembly and with 4-point loaded specimens and use of bent-beam stress-corrosion test specimens under alternate immersion conditions. In addition, experiments were conducted to determine the threshold stress intensity factor for SCC (K(sub ISCC)) which to our knowledge has not been determined previously for Al-Li 2195 alloy. The successful simulated service and stress corrosion testing helped to provide confidence to continue to Ares 1 scale dome fabrication

  4. Report on Status of Shipment of High Fluence Austenitic Steel Samples for Characterization and Stress Corrosion Crack Testing

    Energy Technology Data Exchange (ETDEWEB)

    Clark, Scarlett R. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States); Leonard, Keith J. [Oak Ridge National Lab. (ORNL), Oak Ridge, TN (United States)

    2016-09-01

    The goal of the Mechanisms of Irradiation Assisted Stress Corrosion Cracking (IASCC) task in the LWRS Program is to conduct experimental research into understanding how multiple variables influence the crack initiation and crack growth in materials subjected to stress under corrosive conditions. This includes understanding the influences of alloy composition, radiation condition, water chemistry and metallurgical starting condition (i.e., previous cold work or heat treatments and the resulting microstructure) has on the behavior of materials. Testing involves crack initiation and growth testing on irradiated specimens of single-variable alloys in simulated Light Water Reactor (LWR) environments, tensile testing, hardness testing, microstructural and microchemical analysis, and detailed efforts to characterize localized deformation. Combined, these single-variable experiments will provide mechanistic understanding that can be used to identify key operational variables to mitigate or control IASCC, optimize inspection and maintenance schedules to the most susceptible materials/locations, and, in the long-term, design IASCC-resistant materials. In support of this research, efforts are currently underway to arrange shipment of “free” high fluence austenitic alloys available through Électricité de France (EDF) for post irradiation testing at the Oak Ridge National Laboratory (ORNL) and IASCC testing at the University of Michigan. These high fluence materials range in damage values from 45 to 125 displacements per atom (dpa). The samples identified for transport to the United States, which include nine, no-cost, 304, 308 and 316 tensile bars, were relocated from the Research Institute of Atomic Reactors (RIAR) in Dimitrovgrad, Ulyanovsk Oblast, Russia, and received at the Halden Reactor in Halden, Norway, on August 23, 2016. ORNL has been notified that a significant amount of work is required to prepare the samples for further shipment to Oak Ridge, Tennessee. The

  5. Stress corrosion cracking of austenitic weld deposits in a salt spray environment

    Science.gov (United States)

    Cai, J. B.; Yu, C.; Shiue, R. K.; Tsay, L. W.

    2015-10-01

    ER 308L and 309LMo were utilized as the filler metals for the groove and overlay welds of a 304L stainless steel substrate, which was prepared via a gas tungsten arc-welding process in multiple passes. U-bend and weight-loss tests were conducted by testing the welds in a salt spray containing 10 wt% NaCl at 120 °C. The dissolution of the skeletal structure in the fusion zone (FZ) caused the stress corrosion cracking (SCC) of the weld. The FZ in the cold-rolled condition showed the longest single crack length in the U-bend tests. Moreover, sensitization treatment at 650 °C for 10 h promoted the formation of numerous fine cracks, which resulted in a high SCC susceptibility. The weight loss of the deposits was consistent with the SCC susceptibility of the welds in a salt spray. The 309LMo deposit was superior to the 308L deposit in the salt spray.

  6. Public inquiry concerning stress corrosion cracking on Canadian oil and gas pipelines

    Energy Technology Data Exchange (ETDEWEB)

    Vollman, K.W.; Cote-Verhaaf, A.; Illing, R.

    1996-11-01

    An comprehensive inquiry was conducted into the serious problem of near-neutral pH stress corrosion cracking (SCC) in Canada`s buried oil and gas pipelines. The inquiry was prompted by evidence of the widespread nature of SCC and awareness that research was producing new insights into the problem. Two major ruptures and fires occurred on the TransCanada system in February and July of 1995. The July rupture was in a location where it was believed SCC could not occur. SCC on pipelines occurs when small cracks develop on the outside surface of the buried pipeline. With time the cracks grow large enough until the pipeline fails or ruptures. SCC results from an interaction of the following three conditions: a potent environment at the pipe surface, a susceptible pipe material, and a tensile stress. Recommendations to resolve the problem included implementation of an SCC management program by pipeline companies, changes to the design of the pipeline, continued research, establishment of an SCC database, improved emergency response practices, and information sharing. 84 refs., 8 tabs., 67 figs.

  7. Microstructural and Stress Corrosion Cracking Characteristics of Austenitic Stainless Steels Containing Silicon

    Science.gov (United States)

    Andresen, Peter L.; Chou, Peter H.; Morra, Martin M.; Lawrence Nelson, J.; Rebak, Raul B.

    2009-12-01

    Austenitic stainless steels (SSs) core internal components in nuclear light water reactors (LWRs) are susceptible to irradiation-assisted stress corrosion cracking (IASCC). One of the effects of irradiation is the hardening of the SS and a change in the dislocation distribution in the alloy. Irradiation may also alter the local chemistry of the austenitic alloys; for example, silicon may segregate and chromium may deplete at the grain boundaries. The segregation or depletion phenomena at near-grain boundaries may enhance the susceptibility of these alloys to environmentally assisted cracking (EAC). The objective of the present work was to perform laboratory tests in order to better understand the role of Si in the microstructure, properties, electrochemical behavior, and susceptibility to EAC of austenitic SSs. Type 304 SS can dissolve up to 2 pct Si in the bulk while maintaining a single austenite microstructure. Stainless steels containing 12 pct Cr can dissolve up to 5 pct bulk Si while maintaining an austenite structure. The crack growth rate (CGR) results are not conclusive about the effect of the bulk concentration of Si on the EAC behavior of SSs.

  8. Stress corrosion cracking of alloy 600 using the constant strain rate test

    Energy Technology Data Exchange (ETDEWEB)

    Bulischeck, T. S.; van Rooyen, D.

    1980-01-01

    The most recent corrosion problems experienced in nuclear steam generators tubed with Inconel alloy 600 is a phenomenon labeled ''denting''. Denting has been found in various degrees of severity in many operating pressurized water reactors. Laboratory investigations have shown that Inconel 600 exhibits intergranular SCC when subjected to high stresses and exposed to deoxygenated water at elevated temperatures. A research project was initiated at Brookhaven National Laboratory in an attempt to improve the qualitative and quantitative understanding of factors influencing SCC in high temperature service-related environments. An effort is also being made to develop an accelerated test method which could be used to predict the service life of tubes which have been deformed or are actively denting. Several heats of commercial Inconel 600 tubing were procured for testing in deaerated pure and primary water at temperatures from 290 to 365/sup 0/C. U-bend type specimens were used to determine crack initiation times which may be expected for tubes where denting has occurred but is arrested and provide baseline data for judging the accelerating effects of the slow strain rate method. Constant extension rate tests were employed to determine the crack velocities experienced in the crack propagation stage and predict failure times of tubes which are actively denting. 8 refs., 17 figs., 5 tabs.

  9. Effect of cold work and processing orientation on stress corrosion cracking behavior of alloy 600

    Energy Technology Data Exchange (ETDEWEB)

    Moshier, W.C.; Brown, C.M.

    2000-03-01

    Cold work accelerates stress corrosion cracking (SCC) growth rates in Alloy 600 (UNS N06600). However, the variation in crack growth rates generated from cold-worked material has been significant, and the effect has been difficult to quantify. A study was performed in hydrogenated water adjusted to pH 10.2 to evaluate systematically the effect of cold work on Alloy 600 as a function of temperature, amount of cold work, stress intensity factor, and processing orientation. Cold work was introduced into the material by tensile prestraining or cold-rolling plate product. Crack growth rates were determined between 252 C and 360 C, stress intensity factors between 21 MPa{radical}m and 55 MPa{radical}m, and yield strengths between 201 MPa and 827 MPa. The material with the highest yield strength was cold-rolled and tested in the longitudinal-transverse (LT) and short-transverse (ST) orientations. Crack growth rates increased with increasing temperature, stress intensity factor, and yield strength. Furthermore, crack growth rates were a strong function of the processing orientation in the cold-rolled plate, with growth rates approximately an order of magnitude greater in the ST orientation compared to the LT orientation. Crack growth rates in the LT orientation were measured between 0.003 x 10{sup {minus}9} m/s and 1.95 x 10{sup {minus}9} m/s and between 0.066 x 10{sup {minus}9} m/s and 6.3 x 10{sup {minus}9} m/s in the ST orientation. Activation energies were slightly greater in the ST orientation, ranging from 154 kcal/mol to 191 kcal/mol, compared to activation energies between 126 kJ/mol and 157 kJ/mol in the LT orientation. Results of this study demonstrated that, although cold work can be used to accelerate SCC, the orientation of crack growth significantly can affect the results and must be taken into account when analyzing data from cold-worked material.

  10. Corrosion Products and Formation Mechanism During Initial Stage of Atmospheric Corrosion of Carbon Steel

    Institute of Scientific and Technical Information of China (English)

    XIAO Kui; DONG Chao-fang; LI Xiao-gang; WANG Fu-ming

    2008-01-01

    The formation and development of corrosion products on carbon steel surface during the initial stage of atmospheric corrosion in a laboratory simulated environment have been studied by scanning electron microscopy (SEM)and Raman spectroscopy.The results showed that two different shapes of corrosion products,that is,ring and chain,were formed in the initial stage of corrosion.MnS clusters were found in the nuclei of corrosion products at the active local corrosion sites.The ring-shaped products were composed of lepidocrocite (γ-FeOOH) and maghemite(γ-Fe2 O3) transformed from lepidocrocite.The chain-type products were goethite (α-FeOOH).A formation mechanism of the corrosion products is proposed.

  11. Graphene coating for anti-corrosion and the investigation of failure mechanism

    Science.gov (United States)

    Zhu, Y. X.; Duan, C. Y.; Liu, H. Y.; Chen, Y. F.; Wang, Y.

    2017-03-01

    Graphene produced by chemical vapor deposition (CVD) methods has been considered as a promising corrosion prevention layer because of its exceptional structure and impermeability. However, the anti-corrosion performance and the failure mechanism are still controversial. In this study, graphene layers with different quality levels, crystallite sizes, and layer numbers were prepared on the surface of Cu by a CVD process. The effects of grain boundaries (GBs) on the failure of graphene layers to provide adequate protection were investigated in detail by combining graphene transfer techniques, computation, and anti-corrosion measurements. Our results reveal that corrosion rates decrease marginally upon the increase of graphene layer number, and this rather weak dependence on thickness likely arises from the aligned nature of the GBs in CVD-grown few-layer graphene. This problem can potentially be overcome by layer-by-layer graphene transfer technique, in which corrosion is found to be arrested locally when transferred graphene is present on top of the as-grown graphene. However, this advantage is not reflected in corrosion studies performed on large-scale samples, where cracks or imperfect interfaces could offset the advantages of GB misalignment. With improvements in technology, the layer-by-layer assembly technique could be used to develop an effective anti-corrosion barrier.

  12. Corrosion of steel bars in cracked concrete made with ordinary portland, slag and fly ash cements

    Energy Technology Data Exchange (ETDEWEB)

    Mohammed, T.U.; Yamaji, T.; Hamada, H. [Port and Harbor Research Inst., Ministry of Land, Infrastructure and Transport (Japan); Aoyama, T. [PS Corp. (Japan)

    2001-07-01

    A study was conducted in which the marine durability of ordinary portland cement, slag and fly ash cement was examined using 15 year old plain and reinforced concrete cylindrical specimens. The performance of these cements was then examined for pre-cracked reinforced concrete prism samples. The process of manufacturing cement emits huge amounts of carbon dioxide into the global atmosphere. Replacing a portion of the cement with by-products from the steel industry and thermal power plants (which are both huge emitters of carbon dioxide) can lower carbon dioxide emissions and also solve the disposal issue of slag and fly ash while increasing the long-term durability of concrete structures. In this study, concrete cylindrical specimens were made of ordinary portland cement, slag and fly ash cements. The specimens were 100 x 100 x 600 mm prisms of different types of cement. Water-to-cement ratios were 0.45 and 0.55. Both tap water and seawater were used as mixing water. The samples were exposed in tidal pools for 15 years to evaluate the compressive strength of the concrete, corrosion of the steel bars, and chloride-ion concentrations in the concrete. It was shown that, with the exception of fly ash cements, the compressive strength of most cements increased after 15 years of exposure compared to its 28 day strength. Type C slag cement demonstrated the best performance against chloride-ion at the surface of concrete made with slag and fly ash. Voids in the steel-concrete interface make it possible for corrosion pits to develop. The use of seawater as mixing water results in earlier strength development at 28 days and does not cause to the strength of the concrete to regress after 15-years of exposure, but it causes more corrosion of steel bars at a lower cover depth. Corrosion of steel bars is not an issue at deeper cover depths. 15 refs., 19 tabs., 13 figs.

  13. The influence of cracks on chloride-induced corrosion of reinforced concrete structures - development of the experimental set-up

    NARCIS (Netherlands)

    Blagojevic, A.; Koleva, D.A.; Walraven, J.C.

    2014-01-01

    Chloride-induced corrosion of steel reinforcement is one of the major threats to durability of reinforced concrete structures in aggressive environmental conditions. When the steel reinforcement starts to corrode, structures gradually lose integrity and service life is shortened. Cracks are inevitab

  14. Corrosion and Corrosion Control in Light Water Reactors

    Science.gov (United States)

    Gordon, Barry M.

    2013-08-01

    Serious corrosion problems have plagued the light water reactor (LWR) industry for decades. The complex corrosion mechanisms involved and the development of practical engineering solutions for their mitigation will be discussed in this article. After a brief overview of the basic designs of the boiling water reactor (BWR) and pressurized water reactor (PWR), emphasis will be placed on the general corrosion of LWR containments, flow-accelerated corrosion of carbon steel components, intergranular stress corrosion cracking (IGSCC) in BWRs, primary water stress corrosion cracking (PWSCC) in PWRs, and irradiation-assisted stress corrosion cracking (IASCC) in both systems. Finally, the corrosion future of both plants will be discussed as plants extend their period of operation for an additional 20 to 40 years.

  15. Principles of inhibiting of corrosion-static crack growth in constructional steels caused by hydrogen embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Romaniv, O.N.; Nikiforchin, G.N.; Tsirul' nik, A.T.

    1987-11-01

    The effectiveness of a range of organic and inorganic corrosion inhibitors was studied on a series of structural chromium steels--including 45KhN2MFA, 60KhS, and 30KhGSN2A--of different strength levels and certain principles are formulated for developing and selecting inhibitors based on the hydrogen mechanism of corrosive media. The inhibitors tested include monoethanol amine, urotropin, sodium benzoate, thiourea, sodium phosphates and chromates, various nitrates, and the IRT range of inhibitors.

  16. Corrosion of Steel in Concrete, Part I – Mechanisms

    DEFF Research Database (Denmark)

    Küter, André; Møller, Per; Geiker, Mette Rica

    2006-01-01

    prematurely. Reinforcement corrosion is identified to be the foremost cause of deterioration. Steel in concrete is normally protected by a passive layer due the high alkalinity of the concrete pore solution; corrosion is initiated by neutralization through atmospheric carbon dioxide and by ingress...... of depassivation ions, especially chloride ions. The background and consequences of deterioration of reinforced concrete structures caused by steel corrosion are summarized. Selected corrosion mechanisms postulated in the literature are briefly discussed and related to observations. The key factors controlling...... initiation and propagation of corrosion of steel in concrete are outlined....

  17. Thermo-Mechanical Fatigue Crack Growth of RR1000

    Directory of Open Access Journals (Sweden)

    Christopher John Pretty

    2017-01-01

    Full Text Available Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP testing produces accelerated crack growth rates compared with out-of-phase (OOP due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles.

  18. Thermo-Mechanical Fatigue Crack Growth of RR1000

    Science.gov (United States)

    Pretty, Christopher John; Whitaker, Mark Thomas; Williams, Steve John

    2017-01-01

    Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP) testing produces accelerated crack growth rates compared with out-of-phase (OOP) due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles. PMID:28772394

  19. Thermo-Mechanical Fatigue Crack Growth of RR1000.

    Science.gov (United States)

    Pretty, Christopher John; Whitaker, Mark Thomas; Williams, Steve John

    2017-01-04

    Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP) testing produces accelerated crack growth rates compared with out-of-phase (OOP) due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles.

  20. Cluster analysis of stress corrosion mechanisms for steel wires used in bridge cables through acoustic emission particle swarm optimization.

    Science.gov (United States)

    Li, Dongsheng; Yang, Wei; Zhang, Wenyao

    2017-01-18

    Stress corrosion is the major failure type of bridge cable damage. The acoustic emission (AE) technique was applied to monitor the stress corrosion process of steel wires used in bridge cable structures. The damage evolution of stress corrosion in bridge cables was obtained according to the AE characteristic parameter figure. A particle swarm optimization cluster method was developed to determine the relationship between the AE signal and stress corrosion mechanisms. Results indicate that the main AE sources of stress corrosion in bridge cables included four types: passive film breakdown and detachment of the corrosion product, crack initiation, crack extension, and cable fracture. By analyzing different types of clustering data, the mean value of each damage pattern's AE characteristic parameters was determined. Different corrosion damage source AE waveforms and the peak frequency were extracted. AE particle swarm optimization cluster analysis based on principal component analysis was also proposed. This method can completely distinguish the four types of damage sources and simplifies the determination of the evolution process of corrosion damage and broken wire signals.

  1. Microbial corrosion and cracking in steel. A concept for evaluation of hydrogen-assisted stress corrosion cracking in cathodically protected high-pressure gas transmission pipelines

    DEFF Research Database (Denmark)

    Nielsen, Lars Vendelbo

    of high-strength pipeline steel and the concentration of hydrogen present in the steel. B. Determine the degree hydrogen absorption by cathodically protected steel exposed in natural soil sediment, which include activity of sulphate-reducing bacteria (SRB). C. Compare the above points with fracture......An effort has been undertaken in order to develop a concept for evaluation of the risk of hydrogen-assisted cracking in cathodically protected gas transmission pipelines. The effort was divided into the following subtasks: A. Establish a correlation between the fracture mechanical properties...... in this steel....

  2. Irradiation Programs and Test Plans to Assess High-Fluence Irradiation Assisted Stress Corrosion Cracking Susceptibility.

    Energy Technology Data Exchange (ETDEWEB)

    Teysseyre, Sebastien [Idaho National Lab. (INL), Idaho Falls, ID (United States)

    2015-03-01

    . Irradiation assisted stress corrosion cracking (IASCC) is a known issue in current reactors. In a 60 year lifetime, reactor core internals may experience fluence levels up to 15 dpa for boiling water reactors (BWR) and 100+ dpa for pressurized water reactors (PWR). To support a safe operation of our fleet of reactors and maintain their economic viability it is important to be able to predict any evolution of material behaviors as reactors age and therefore fluence accumulated by reactor core component increases. For PWR reactors, the difficulty to predict high fluence behavior comes from the fact that there is not a consensus of the mechanism of IASCC and that little data is available. It is however possible to use the current state of knowledge on the evolution of irradiated microstructure and on the processes that influences IASCC to emit hypotheses. This report identifies several potential changes in microstructure and proposes to identify their potential impact of IASCC. The susceptibility of a component to high fluence IASCC is considered to not only depends on the intrinsic IASCC susceptibility of the component due to radiation effects on the material but to also be related to the evolution of the loading history of the material and interaction with the environment as total fluence increases. Single variation type experiments are proposed to be performed with materials that are representative of PWR condition and with materials irradiated in other conditions. To address the lack of IASCC propagation and initiation data generated with material irradiated in PWR condition, it is proposed to investigate the effect of spectrum and flux rate on the evolution of microstructure. A long term irradiation, aimed to generate a well-controlled irradiation history on a set on selected materials is also proposed for consideration. For BWR, the study of available data permitted to identify an area of concern for long term performance of component. The efficiency of

  3. Strain energy density-distance criterion for the initiation of stress corrosion cracking of alloy X-750

    Energy Technology Data Exchange (ETDEWEB)

    Hall, M.M. Jr.; Symons, D.M.

    1996-05-01

    A strain energy density-distance criterion was previously developed and used to correlate rising-load K{sub c} initiation data for notched and fatigue precracked specimens of hydrogen precharged Alloy X-750. This criterion, which was developed for hydrogen embrittlement (HE) cracking, is used here to correlate static-load stress corrosion cracking (SCC) initiation times obtained for smooth geometry, notched and fatigue precracked specimens. The onset of SCC crack growth is hypothesized to occur when a critical strain, which is due to environment-enhanced creep, is attained within the specimen interior. For notched and precracked specimens, initiation is shown by analysis to occur at a variable distance from notch and crack tips. The initiation site varies from very near the crack tip, for highly loaded sharp cracks, to a site that is one grain diameter from the notch, for lower loaded, blunt notches. The existence of hydrogen gradients, which are due to strain-induced hydrogen trapping in the strain fields of notch and crack tips, is argued to be controlling the site for initiation of cracking. By considering the sources of the hydrogen, these observations are shown to be consistent with those from the previous HE study, in which the characteristic distance for crack initiation was found to be one grain diameter from the notch tip, independent of notch radius, applied stress intensity factor and hydrogen level.

  4. Research of stress corrosion cracking of T225NG titanium alloy in loop water of high temperature and high pressure

    Institute of Scientific and Technical Information of China (English)

    Xu Jijin; Yan Keng; Chen Ligong; Jiang Chengyu

    2006-01-01

    Double cantilever beam (DCB) specimens were used to research the stress corrosion cracking of T225NG titanium alloy in loop water of high temperature and high pressure. DCB specimens were forced pre-stress, put into high pressure autoclave, and the stress corrosion and crack expansion of specimens were observed and measured in 500 h, 1 000 h and 2 000h respectively. The results show that small expansion occurred along the direction of pre-cracking. According to calculation,the speed of cracking expansion is lower than 10 -9 m/s in 500 h and the value of KIscc/KI is higher than 0. 75, which proves that T225NG has an excellent corrosion resistance in loop water. The main reason is that there is an oxide film on the surface of specimens. According to the analysis of energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD), the oxide film consists of TiO2. Therefore, the oxide film at the crack tip impedes the hydrogen separating out from the cathode to penetrate into titanium alloy and resists hydrogen embrittlement.

  5. EXPERIMENTAL STUDY OF MECHANISM AND TECHNOLOGY OF DIRECTED CRACK BLASTING

    Institute of Scientific and Technical Information of China (English)

    杨永琦; 高全臣; 于慕松; 张奇; 单仁亮; 杨仁树; 贾云峰

    1995-01-01

    The dynamic stress-fields and their distribution characteristics around boreholes in the directed crack blasting were measured with the dynamic photo-elastic laser holography apparatus and the uitradymamic measurement system. The directed crack mechanism and its mechanical model have been analysed and expounded. Through the 43 production experiments using slotted cartridges and the double triangle center cut-holes for directed crack blasting in underground rock drift, the resuits of which the rates of half-hole marks and efficiency of borehole,and the nonsmooth grades of the cut contours are 96%, 98% and 10cm respectively have been achieved.

  6. Contribution to crack sizing by phased array ultrasonic techniques: part 2: comparison with optical, magnetic particles, fracture mechanics and metallography for last significant crack tip

    Energy Technology Data Exchange (ETDEWEB)

    Ciorau, P. [Ontario Power Generation, Inc., Pickering, Ontario (Canada)

    2007-11-15

    The paper presents phased array results for 1-D linear array probes of high frequency (7-10 MHz) in L-, and S-waves for detecting the crack shape and the last significant tip. Fatigue and stress-corrosion cracks with height ranging from 1.6 mm to 20.4 mm were detected in welded samples, piping welds and straight bars with thickness between 1.6 mm to 38 mm. The results of S-scan display are compared with different methods: optical, magnetic particles, fracture mechanics and metallography. The experimental results concluded the undersizing trend of PAUT in detecting the last crack tip or closure, in spite of using dynamic depth focusing, and/or focusing on crack tip. The average undersizing error is - 0.4 mm. This error increases for cracks with depth >12 mm. The largest errors occur when the crack is sized from outer surface coupled with initiation from the outside surface with propagation towards the inside surface. These errors were reduced by a combination of shear and longitudinal waves and by increasing the angular resolution. (author)

  7. Fluid catalytic cracking : feedstocks and reaction mechanism

    NARCIS (Netherlands)

    Dupain, X.

    2006-01-01

    The Fluid Catalytic Cracking (FCC) process is one of the key units in a modern refinery. Traditionally, its design is primarily aimed for the production of gasoline from heavy oil fractions, but as co-products also diesel blends and valuable gasses (e.g. propene and butenes) are formed in

  8. DEVELOPMENT OF SOFTWARE SYSTEM FOR MONITORING OF STRESS CORROSION CRACKING OF THE PIPELINE UNDER TENSION

    Directory of Open Access Journals (Sweden)

    Z. K. Abaev

    2016-01-01

    Full Text Available The software and hardware development tendency, providing the automated monitoring and control of basic and auxiliary technological processes of gas transportation via system of main gas pipelines has been revealed. The article discusses the stages of creation of the software of system of monitoring corrosion cracking under tension (SCC. The new useful adequate regression models development determining the risk level of LCC is shown. A ranking sections algorithm of main gas pipeline (MG on the propensity to SCC is presented. Adequate developed regression equation determining the LCC risk level has been developed. To count the main gas pipeline lifetime the variable rank of the danger of SCC (RSCC on the basis of methods of fuzzy logic is proposed to use. Implementation of the fuzzy model was carried out using the graphical tools developed in MATLAB using the expansion pack Fuzzy Logic Toolbox. The working algorithm of developed program and the screen forms are presented.

  9. Characterization of the Resistance of Alloy 22 to Stress Corrosion Cracking

    Energy Technology Data Exchange (ETDEWEB)

    King, K J; Estill, J C; Rebak, R B

    2002-05-30

    In its current design, the high-level nuclear waste containers include an external layer of Alloy 22 (Ni-22Cr-13Mo-3W-3Fe). Since over their lifetime, the containers may be exposed to multi-ionic aqueous environments, a potential degradation mode of the outer layer could be environmentally assisted cracking (EAC). The objective of the current research was to characterize the effect of applied potential and temperature on the susceptibility of Alloy 22 to EAC in simulated concentrated water (SCW) using the slow strain rate test (SSRT). Results show that Alloy 22 may suffer EAC at applied potentials approximately 400 mV more anodic than the corrosion potential (E{sub corr}).

  10. Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Shack, W. J.; Energy Technology

    2006-01-31

    This report summarizes work performed at Argonne National Laboratory on irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels that were irradiated in the Halden reactor in simulation of irradiation-induced degradation of boiling water reactor (BWR) core internal components. Slow-strain-rate tensile tests in BWR-like oxidizing water were conducted on 27 austenitic stainless steel alloys that were irradiated at 288 C in helium to 0.4, 1.3, and 3.0 dpa. Fractographic analysis was conducted to determine the fracture surface morphology. Microchemical analysis by Auger electron spectroscopy was performed on BWR neutron absorber tubes to characterize grain-boundary segregation of important elements under BWR conditions. At 0.4 and 1.4 dpa, transgranular fracture was mixed with intergranular fracture. At 3 dpa, transgranular cracking was negligible, and fracture surface was either dominantly intergranular, as in field-cracked core internals, or dominantly ductile or mixed. This behavior indicates that percent intergranular stress corrosion cracking determined at {approx}3 dpa is a good measure of IASCC susceptibility. At {approx}1.4 dpa, a beneficial effect of a high concentration of Si (0.8-1.5 wt.%) was observed. At {approx}3 dpa, however, such effect was obscured by a deleterious effect of S. Excellent resistance to IASCC was observed up to {approx}3 dpa for eight heats of Types 304, 316, and 348 steel that contain very low concentrations of S. Susceptibility of Types 304 and 316 steels that contain >0.003 wt.% S increased drastically. This indicates that a sulfur related critical phenomenon plays an important role in IASCC. A sulfur content of <0.002 wt.% is the primary material factor necessary to ensure good resistance to IASCC. However, for Types 304L and 316L steel and their high-purity counterparts, a sulfur content of <0.002 wt.% alone is not a sufficient condition to ensure good resistance to IASCC. This is in distinct contrast to

  11. Irradiation-assisted stress corrosion cracking behavior of austenitic stainless steels applicable to LWR core internals.

    Energy Technology Data Exchange (ETDEWEB)

    Chung, H. M.; Shack, W. J.; Energy Technology

    2006-01-31

    This report summarizes work performed at Argonne National Laboratory on irradiation-assisted stress corrosion cracking (IASCC) of austenitic stainless steels that were irradiated in the Halden reactor in simulation of irradiation-induced degradation of boiling water reactor (BWR) core internal components. Slow-strain-rate tensile tests in BWR-like oxidizing water were conducted on 27 austenitic stainless steel alloys that were irradiated at 288 C in helium to 0.4, 1.3, and 3.0 dpa. Fractographic analysis was conducted to determine the fracture surface morphology. Microchemical analysis by Auger electron spectroscopy was performed on BWR neutron absorber tubes to characterize grain-boundary segregation of important elements under BWR conditions. At 0.4 and 1.4 dpa, transgranular fracture was mixed with intergranular fracture. At 3 dpa, transgranular cracking was negligible, and fracture surface was either dominantly intergranular, as in field-cracked core internals, or dominantly ductile or mixed. This behavior indicates that percent intergranular stress corrosion cracking determined at {approx}3 dpa is a good measure of IASCC susceptibility. At {approx}1.4 dpa, a beneficial effect of a high concentration of Si (0.8-1.5 wt.%) was observed. At {approx}3 dpa, however, such effect was obscured by a deleterious effect of S. Excellent resistance to IASCC was observed up to {approx}3 dpa for eight heats of Types 304, 316, and 348 steel that contain very low concentrations of S. Susceptibility of Types 304 and 316 steels that contain >0.003 wt.% S increased drastically. This indicates that a sulfur related critical phenomenon plays an important role in IASCC. A sulfur content of <0.002 wt.% is the primary material factor necessary to ensure good resistance to IASCC. However, for Types 304L and 316L steel and their high-purity counterparts, a sulfur content of <0.002 wt.% alone is not a sufficient condition to ensure good resistance to IASCC. This is in distinct contrast to

  12. Fracture Mechanics Analyses for Interface Crack Problems - A Review

    Science.gov (United States)

    Krueger, Ronald; Shivakumar, Kunigal; Raju, Ivatury S.

    2013-01-01

    Recent developments in fracture mechanics analyses of the interfacial crack problem are reviewed. The intent of the review is to renew the awareness of the oscillatory singularity at the crack tip of a bimaterial interface and the problems that occur when calculating mode mixity using numerical methods such as the finite element method in conjunction with the virtual crack closure technique. Established approaches to overcome the nonconvergence issue of the individual mode strain energy release rates are reviewed. In the recent literature many attempts to overcome the nonconvergence issue have been developed. Among the many approaches found only a few methods hold the promise of providing practical solutions. These are the resin interlayer method, the method that chooses the crack tip element size greater than the oscillation zone, the crack tip element method that is based on plate theory and the crack surface displacement extrapolation method. Each of the methods is validated on a very limited set of simple interface crack problems. However, their utility for a wide range of interfacial crack problems is yet to be established.

  13. Fracture model for predicting concrete cover-cracking induced by steel corrosion based on interface bond state

    Institute of Scientific and Technical Information of China (English)

    WANG Xian-li; ZHENG Jian-jun; WU Zhi-min

    2009-01-01

    Time-to-cracking of the concrete cover induced by the steel corrosion is one of the critical problems faced by engineers, operators and asset managers in making strategies for the maintenance and repairs of reinforced concrete (RC)structures affected by corrosion. In this paper, a theoretical model for predicting the time-to-cracking is derived by assuming the bond between the steel bar and the concrete as a linear combination of perfectly smooth and bonded. The model takes into account the characteristics of existing exiguous flaws and initial cracks in the concrete before the load acting on RC structures. The validity of the proposed model is preliminarily verified by comparing the obtained results with the available experimental results. A remarkable advantage of the proposed method is its application to the prediction of the service life of RC structures, made of the deformed steel bars as well as the round bars. By determining an experimental constant α, which is related to the interface bond state between the steel bar and the concrete, the service life of RC structures can be predicted using the proposed scheme. Analysis of major factors affecting the time-to-cracking demonstrates that the length of the initial crack affects the service life of RC structures significantly. Moreover, the larger cover thickness and the smaller diameter of the steel bar within a certain range are beneficial to prolonging the time-to-cracking.

  14. Slurry Chemical Corrosion and Galvanic Corrosion during Copper Chemical Mechanical Polishing

    Science.gov (United States)

    Kondo, Seiichi; Sakuma, Noriyuki; Homma, Yoshio; Ohashi, Naofumi

    2000-11-01

    Copper (Cu) corrosion during chemical mechanical polishing (CMP) was controlled in order to improve the Cu damascene interconnect process. Slurry chemical corrosion was found to be enhanced when the slurry was diluted by deionized (DI) water during rinsing just after CMP@. Since the corrosion inhibitor, benzotriazole (BTA), reduces the Cu removal rate, adding it to the rinse solution prevents chemical corrosion more effectively than adding it to the slurry. On the other hand, galvanic corrosion occurs at the interface between Cu and the barrier metal, and it can be prevented by selecting appropriate barrier metals. Because the difference between the electrochemical potentials of Cu and the barrier metal is small in the slurry, refractory metals such as Ta, TaN, and TiN were found to be appropriate barrier metals. On the other hand, W, WN, and Ti have large potential differences, so galvanic corrosion was clearly observed when Cu/W damascene interconnects were fabricated.

  15. Stress-corrosion cracking of steels in ammonia with consideration given to OTEC design: a survey

    Energy Technology Data Exchange (ETDEWEB)

    Teel, R.B.

    1980-03-01

    Carbon steel, alloy steel, and high-strength, quenched and tempered steel, when under applied or residual stress and especially when cold formed and/or welded without subsequent thermal stress relief, are subject to failure by stress-corrosion cracking (SCC) in air-contaminated dry ammonia. Water as well as hydrazine when present in small amounts have been shown to be effective inhibitors in an all steel system. Galvanic corrosion between dissimilar metals and/or accelerated failure by SCC of stressed steel as a result of galvanic coupling may be of concern. Where water has proven effective as an inhibitor of SCC in an all steel system, it may not be adequate in a mixed metal system. With aluminum tubes, the tube sheet will either have to be solid aluminum, aluminum clad steel or some nonconductive coating will be necessary to effectively remove the cathodic alloy from the galvanic circuit. Research is required to determine the severity of the coupling effect between dissimilar alloys in ammonia under OTEC conditions; especially the possibility of accelerated SCC failures of stressed steel where the presence of an inhibitor in the ammonia may not be sufficient to override the galvanic coupling effect.

  16. Corrosion resistance of a steel under an oxidizing atmosphere in a fluid catalytic cracking regenerator

    Directory of Open Access Journals (Sweden)

    Ieda Caminha

    2004-03-01

    Full Text Available In the present work, the corrosion resistance of an ASTM A 387 G11 steel was evaluated under two conditions: an oxidizing atmosphere in a fluid catalytic cracking regenerator of a petroleum processing unit and a simulated atmosphere in the laboratory, at temperatures of 650 °C and 700 °C. The characterization of the phases present in the oxidized layer was carried out by X-ray diffraction (XRD, optical microscopy (OM and scanning electron microscopy (SEM with X-ray energy dispersive analysis (EDS. Severe corrosion was observed after exposure to both the real and simulated conditions, with formation of several iron oxides (Fe2O3, Fe3O4 and FeO in the product scale layer, as well as a slight inner oxidation and sulfidation of chromium in the substrate. Internal nitridation of the silicon and the manganese was observed only in the real condition, probably related to the long-term exposure inside the regenerator.

  17. Effect of Repair Welding on Electrochemical Corrosion and Stress Corrosion Cracking Behavior of TIG Welded AA2219 Aluminum Alloy in 3.5 Wt Pct NaCl Solution

    Science.gov (United States)

    Venugopal, A.; Sreekumar, K.; Raja, V. S.

    2010-12-01

    The stress corrosion cracking (SCC) behavior of AA2219 aluminum alloy in the as-welded (AW) and repair-welded (RW) conditions was examined and compared with that of the base metal (BM) in 3.5 wt pct NaCl solution using the slow strain rate technique (SSRT). The reduction in ductility was used as a parameter to evaluate the SCC susceptibility of both BM and welded joints. The results show that the ductility ratio ( ɛ NaCl/( ɛ air)) of the BM was close to one (0.97) and reduced to 0.9 for the AW joint. This value further reduced to 0.77 after carrying out one repair welding operation. However, the RW specimen exhibited higher ductility than the single-weld specimens even in 3.5 wt pct NaCl solution. SSRT results obtained using pre-exposed samples followed by post-test metallographic observations clearly showed localized pitting corrosion along the partially melted zone (PMZ), signifying that the reduction in ductility ratio of both the AW and RW joints was more due to mechanical overload failure, caused by the localized corrosion and a consequent reduction in specimen thickness, than due to SCC. Also, the RW joint exhibited higher ductility than the AW joint both in air and the environment, although SCC index (SI) for the former is lower than that of the latter. Fractographic examination of the failed samples, in general, revealed a typical ductile cracking morphology for all the base and welded joints, indicating the good environmental cracking resistance of this alloy. Microstructural examination and polarization tests further demonstrate grain boundary melting along the PMZ, and that provided the necessary electrochemical condition for the preferential cracking on that zone of the weldment.

  18. Status report: Intergranular stress corrosion cracking of BWR core shrouds and other internal components

    Energy Technology Data Exchange (ETDEWEB)

    NONE

    1996-03-01

    On July 25, 1994, the US Nuclear Regulatory Commission (NRC) issued Generic Letter (GL) 94-03 to obtain information needed to assess compliance with regulatory requirements regarding the structural integrity of core shrouds in domestic boiling water reactors (BWRs). This report begins with a brief description of the safety significance of intergranular stress corrosion cracking (IGSCC) as it relates to the design and function of BWR core shrouds and other internal components. It then presents a brief history of shroud cracking events both in the US and abroad, followed by an indepth summary of the industry actions to address the issue of IGSCC in BWR core shrouds and other internal components. This report summarizes the staff`s basis for issuing GL 94-03, as well as the staff`s assessment of plant-specific responses to GL 94-03. The staff is continually evaluating the licensee inspection programs and the results from examinations of BWR core shrouds and other internal components. This report is representative of submittals to and evaluations by the staff as of September 30, 1995. An update of this report will be issued at a later date.

  19. Assessment of NDE Technologies for Detection and Characterization of Stress Corrosion Cracking in LWRs

    Energy Technology Data Exchange (ETDEWEB)

    Meyer, Ryan M.; Ramuhalli, Pradeep; Toloczko, Mychailo B.; Bond, Leonard J.; Montgomery, Robert O.

    2012-12-31

    Stress corrosion cracking (SCC) in light water reactors (LWRs) has been a persistent form of degradation in the nuclear industry. Examples of SCC can be found for a range of materials in boiling and pressurized water reactor environments, including carbon steels, stainless steels, and nickel-base stainless alloys. The evolution of SCC is often characterized by a long initiation stage followed by a phase of more rapid crack growth to failure. This provides a relatively short window of opportunity to detect the start of observable SCC, and it is conceivable that SCC could progress from initiation to failure between subsequent examinations when managed by applying periodic in-service inspection techniques. Implementation of advanced aging management paradigms in the current fleet of LWRs will require adaptation of existing measurement technologies and development of new technologies to perform on-line measurements during reactor operation to ensure timely detection of material degradation and to support the implementation of advanced diagnostics and prognostics. This paper considers several non-destructive examination (NDE) technologies with known sensitivity to detection of indicators for SCC initiation and/or propagation, and assesses these technologies with respect to their ability to detect and accurately characterize the significance of an SCC flaw. Potential strategies to improve SCC inspection or monitoring performance are offered to benefit management of SCC degradation in LWRs.

  20. Reconstruction of stress corrosion cracks using signals of pulsed eddy current testing

    Science.gov (United States)

    Wang, Li; Xie, Shejuan; Chen, Zhenmao; Li, Yong; Wang, Xiaowei; Takagi, Toshiyuki

    2013-06-01

    A scheme to apply signals of pulsed eddy current testing (PECT) to reconstruct a deep stress corrosion crack (SCC) is proposed on the basis of a multi-layer and multi-frequency reconstruction strategy. First, a numerical method is introduced to extract conventional eddy current testing (ECT) signals of different frequencies from the PECT responses at different scanning points, which are necessary for multi-frequency ECT inversion. Second, the conventional fast forward solver for ECT signal simulation is upgraded to calculate the single-frequency pickup signal of a magnetic field by introducing a strategy that employs a tiny search coil. Using the multiple-frequency ECT signals and the upgraded fast signal simulator, we reconstructed the shape profiles and conductivity of an SCC at different depths layer-by-layer with a hybrid inversion scheme of the conjugate gradient and particle swarm optimisation. Several modelled SCCs of rectangular or stepwise shape in an SUS304 plate are reconstructed from simulated PECT signals with artificial noise. The reconstruction results show better precision in crack depth than the conventional ECT inversion method, which demonstrates the validity and efficiency of the proposed PECT inversion scheme.

  1. Microstructural mechanisms of cyclic deformation, fatigue crack initiation and early crack growth.

    Science.gov (United States)

    Mughrabi, Haël

    2015-03-28

    In this survey, the origin of fatigue crack initiation and damage evolution in different metallic materials is discussed with emphasis on the responsible microstructural mechanisms. After a historical introduction, the stages of cyclic deformation which precede the onset of fatigue damage are reviewed. Different types of cyclic slip irreversibilities in the bulk that eventually lead to the initiation of fatigue cracks are discussed. Examples of trans- and intercrystalline fatigue damage evolution in the low cycle, high cycle and ultrahigh cycle fatigue regimes in mono- and polycrystalline face-centred cubic and body-centred cubic metals and alloys and in different engineering materials are presented, and some microstructural models of fatigue crack initiation and early crack growth are discussed. The basic difficulties in defining the transition from the initiation to the growth of fatigue cracks are emphasized. In ultrahigh cycle fatigue at very low loading amplitudes, the initiation of fatigue cracks generally occupies a major fraction of fatigue life and is hence life controlling.

  2. Precursor Evolution and Stress Corrosion Cracking Initiation of Cold-Worked Alloy 690 in Simulated Pressurized Water Reactor Primary Water

    Energy Technology Data Exchange (ETDEWEB)

    Zhai, Ziqing [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Toloczko, Mychailo [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Kruska, Karen [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.; Bruemmer, Stephen [Pacific Northwest National Laboratory, 622 Horn Rapids Road, P.O. Box 999, Richland, Washington 99352.

    2017-05-22

    Stress corrosion crack initiation of two thermally-treated, cold-worked (CW) alloy 690 (UNS N06690) materials was investigated in 360oC simulated PWR primary water using constant load tensile (CLT) tests and blunt notch compact tension (BNCT) tests equipped with direct current potential drop (DCPD) for in-situ detection of cracking. SCC initiation was not detected by DCPD for either the 21% or 31%CW CLT specimens loaded at their yield stress after ~9,220 hours, however intergranular (IG) precursor damage and isolated surface cracks were observed on the specimens. The two 31%CW BNCT specimens loaded at moderate stress intensity after several cyclic loading ramps showed DCPD-indicated crack initiation after 10,400 hours of exposure at constant stress intensity, which was resulted from significant growth of IG cracks. The 21%CW BNCT specimens only exhibited isolated small IG surface cracks and showed no apparent DCPD change throughout the test. Post-test cross-section examinations revealed many grain boundary (GB) nano-cavities in the bulk of all the CLT and BNCT specimens particularly for the 31%CW materials. Cavities were also found along GBs extending to the surface suggesting an important role in crack nucleation. This paper provides an overview of the evolution of GB cavities and discusses their effects on crack initiation in CW alloy 690.

  3. Subcritical crack growth and mechanical weathering: a new consideration of how moisture influences rock erosion rates.

    Science.gov (United States)

    Eppes, Martha-Cary; Keanini, Russell; Hancock, Gregory S.

    2016-04-01

    The contributions of moisture to the mechanical aspects of rock weathering and regolith production are poorly quantified. In particular, geomorphologists have largely overlooked the role of subcritical crack growth processes in physical weathering and the fact that moisture strongly influences the rates of those processes. This influence is irrespective of the function that moisture plays in stress loading mechanisms like freezing or hydration. Here we present a simple numerical model that explores the efficacy of subcritical crack growth in granite rock subaerially exposed under a range of moisture conditions. Because most weathering-related stress loading for rocks found at, or near, Earth's surface (hereafter surface rocks) is cyclic, we modeled crack growth using a novel combination of Paris' Law and Charles' Law. This combination allowed us to apply existing empirically-derived data for the stress corrosion index of Charles' Law to fatigue cracking. For stress, we focused on the relatively straightforward case of intergranular stresses that arise during solar-induced thermal cycling by conductive heat transfer, making the assumption that such stresses represent a universal minimum weathering stress experienced by all surface rocks. Because all other tensile weathering-related stresses would be additive in the context of crack growth, however, our model can be adapted to include other stress loading mechanisms. We validated our calculations using recently published thermal-stress-induced cracking rates. Our results demonstrate that 1) weathering-induced stresses as modeled herein, and as published by others, are sufficient to propagate fractures subcritically over long timescales with or without the presence of water 2) fracture propagation rates increase exponentially with respect to moisture, specifically relative humidity 3) fracture propagation rates driven by thermal cycling are strongly dependent on the magnitude of diurnal temperature ranges and the

  4. Online stress corrosion crack and fatigue usages factor monitoring and prognostics in light water reactor components: Probabilistic modeling, system identification and data fusion based big data analytics approach

    Energy Technology Data Exchange (ETDEWEB)

    Mohanty, Subhasish M. [Argonne National Lab. (ANL), Argonne, IL (United States); Jagielo, Bryan J. [Argonne National Lab. (ANL), Argonne, IL (United States); Oakland Univ., Rochester, MI (United States); Iverson, William I. [Argonne National Lab. (ANL), Argonne, IL (United States); Univ. of Illinois at Urbana-Champaign, Champaign, IL (United States); Bhan, Chi Bum [Argonne National Lab. (ANL), Argonne, IL (United States); Pusan National Univ., Busan (Korea, Republic of); Soppet, William S. [Argonne National Lab. (ANL), Argonne, IL (United States); Majumdar, Saurin M. [Argonne National Lab. (ANL), Argonne, IL (United States); Natesan, Ken N. [Argonne National Lab. (ANL), Argonne, IL (United States)

    2014-12-10

    Nuclear reactors in the United States account for roughly 20% of the nation's total electric energy generation, and maintaining their safety in regards to key component structural integrity is critical not only for long term use of such plants but also for the safety of personnel and the public living around the plant. Early detection of damage signature such as of stress corrosion cracking, thermal-mechanical loading related material degradation in safety-critical components is a necessary requirement for long-term and safe operation of nuclear power plant systems.

  5. Recognition and Analysis of Corrosion Failure Mechanisms

    OpenAIRE

    Steven Suess

    2006-01-01

    Corrosion has a vast impact on the global and domestic economy, and currently incurs losses of nearly $300 billion annually to the U.S. economy alone. Because of the huge impact of corrosion, it is imperative to have a systematic approach to recognizing and mitigating corrosion problems as soon as possible after they become apparent. A proper failure analysis includes collection of pertinent background data and service history, followed by visual inspection, photographic documentation, materi...

  6. Recognition and Analysis of Corrosion Failure Mechanisms

    OpenAIRE

    Steven Suess

    2006-01-01

    Corrosion has a vast impact on the global and domestic economy, and currently incurs losses of nearly $300 billion annually to the U.S. economy alone. Because of the huge impact of corrosion, it is imperative to have a systematic approach to recognizing and mitigating corrosion problems as soon as possible after they become apparent. A proper failure analysis includes collection of pertinent background data and service history, followed by visual inspection, photographic documentation, materi...

  7. The stress corrosion cracking behaviour of heat-treated Al-Zn-Mg-Cu alloy in modified salt spray fog testing

    Energy Technology Data Exchange (ETDEWEB)

    Onoro, J. [Ingenieria y Ciencia de los Materiales, Universidad Politecnica de Madrid, ETS Ingenieros Industriales, Madrid (Spain)

    2010-02-15

    The stress corrosion cracking behaviour of 7075 (Al-Zn-Mg-Cu) alloy have been studied in a salt spray fog chamber with two vapourised aqueous solutions (0 and 5% NaCl). The paper analyses the stress corrosion resistance of 7075 aluminium alloy with several precipitation-ageing heat treatments. The results are compared with that obtained in 3.5% NaCl aqueous solution at 20 C. The salt spray fog testing has permitted a good evaluation of SCC susceptibility in 7075 alloy. All temper conditions studied were susceptible to SCC in the different environments tested. 7075-T6 temper was the most susceptible, while in all the cases studied 7075-T73 temper was the least susceptible. Compared to 7075-T6, 7075-RRA temper improved the resistance against the SCC process, but the mechanical properties obtained were lower. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  8. Influence factors on stress corrosion cracking of P110 tubing steel under CO2 injection well annulus environment

    Institute of Scientific and Technical Information of China (English)

    刘然克; 贾静焕; 杜翠薇; 李晓刚

    2016-01-01

    Stress corrosion cracking (SCC) behavior of P110 tubing steel in simulated CO2 injection well annulus environments was investigated through three-point bent tests, potentiodynamic polarization and EIS measurements. The results demonstrate that SCC of P110 tubing steel could occur in acidulous simulated environment, and the sensitivity of SCC increases with the decrease of pH, as well as increase of sulfide concentration and total environmental pressure. Both anodic dissolution and hydrogen embrittlement make contributions to the SCC. Adequate concentration of corrosion inhibitor can inhibit the occurrence of SCC on account of the inhibition of localized anodic dissolution and cathodic hydrogen evolution.

  9. Role of {delta}-ferrite in stress corrosion cracking retardation near fusion boundary of 316NG welds

    Energy Technology Data Exchange (ETDEWEB)

    Abe, Hiroshi, E-mail: hiroshi.abe@qse.tohoku.ac.jp [Graduate School of Engineering, Tohoku University, 6-6-01-2, Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan); Watanabe, Yutaka [Graduate School of Engineering, Tohoku University, 6-6-01-2, Aoba, Aramaki, Aoba-ku, Sendai, Miyagi 980-8579 (Japan)

    2012-05-15

    Stress corrosion cracking (SCC) near the fusion boundary of a 316NG stainless steel (SS) welded joint in high-temperature water was investigated with emphasis on the relation to the microstructural characteristics. {delta}-Ferrite islands were distributed on the crack paths (grain boundary in the partially melted zone and cell boundary in the unmixed zone) near the fusion boundary of 316NG SS piping. SCC retardation near the fusion boundary was clearly observed in our experiments. The relative crack growth rate (CGR) at the {delta}-{gamma} interface was estimated to be 0.043 times lower than that at the {gamma}-{gamma} interface. The cracks remained for a considerable period of time just after they reached the {delta}-ferrite islands. Even those cracks that passed through an initial set of {delta}-ferrite islands were retarded when they encountered a subsequent set of {delta}-ferrite islands. High corrosion resistance due to the presence of large amounts of Cr and the island-shaped morphology of {delta}-ferrite are dominant factors in SCC retardation.

  10. Kibble-Zurek Mechanism in Microscopic Acoustic Cracking Noises

    CERN Document Server

    Ghaffari, H O; Xia, K; Young, R P

    2014-01-01

    The fast evolution of microstructure is key to understanding crackling phenomena. It has been proposed that formation of a nonlinear zone around a moving crack tip controls the crack tip velocity. Progress in understanding the physics of this critical zone has been limited due to the lack of hard data describing the detailed complex physical processes that occur within. For the first time, we show that the signature of the non-linear elastic zone around a microscopic dynamic crack maps directly to generic phases of acoustic noises, supporting the formation of a strongly weak zone [2-3,5] near the moving crack tips. We additionally show that the rate of traversing to non-linear zone controls the rate of weakening, i.e. speed of global rupture propagation. We measure the power-law dependence of nonlinear zone size on the traversing rate, and show that our observations are in agreement with the Kibble-Zurek mechanism (KZM) .

  11. Effect of deteriorated microstructures on stress corrosion cracking of X70 pipeline steel in acidic soil environment

    Institute of Scientific and Technical Information of China (English)

    2008-01-01

    In order to investigate stress corrosion cracking (SCC) of X70 pipeline steel and its weld joint area in acidic soil environmeat in China,two simulating methods were used: one was to obtain bad mierostructures in heat affected zone by annealing at 1300℃ for 10 rain and then,quenching in water; the other was to get different simulating solutions of acidic soil in Yingtan in southeast China.The SCC susceptibilities of X70 pipeline steel before and after quenching in the simulating solutions were analyzed using slow stain rate test (SSRT) and poteatiodynamic polarization technique to investigate the SCC electrochemical mechanism of different mierostruetures further.The results show that SCC appears in the original mierostrueture and the quenched mierostructure as the polarization potential decreases.Hydrogen revolution accelerates SCC of the two tested materials within the range of-850 mV to -1200 mV vs.SCE.Microstructural hardening and grain coarsening also increase SCC.The SCC mechanisms are different,anodic dissolution is the key of causing SCC as the polarization potential is higher than the null eurreat potential,and hydrogen embrittlemeat will play a more important role to SCC as the polarization potential lower than the null current potential.

  12. Improved stress corrosion cracking resistance of a novel biodegradable EW62 magnesium alloy by rapid solidification, in simulated electrolytes

    Energy Technology Data Exchange (ETDEWEB)

    Hakimi, O.; Aghion, E. [Department of Materials Engineering, Ben-Gurion University of the Negev, P.O. Box 653, Beer-Sheva 84105 (Israel); Goldman, J., E-mail: jgoldman@mtu.edu [Biomedical Engineering Department, Michigan Technological University, Houghton, MI, 49931 (United States)

    2015-06-01

    The high corrosion rate of magnesium (Mg) and Mg-alloys precludes their widespread acceptance as implantable biomaterials. Here, we investigated the potential for rapid solidification (RS) to increase the stress corrosion cracking (SCC) resistance of a novel Mg alloy, Mg–6%Nd–2%Y–0.5%Zr (EW62), in comparison to its conventionally cast (CC) counterpart. RS ribbons were extrusion consolidated in order to generate bioimplant-relevant geometries for testing and practical use. Microstructural characteristics were examined by SEM. Corrosion rates were calculated based upon hydrogen evolution during immersion testing. The surface layer of the tested alloys was analyzed by X-ray photoelectron spectroscopy (XPS). Stress corrosion resistance was assessed by slow strain rate testing and fractography. The results indicate that the corrosion resistance of the RS alloy is significantly improved relative to the CC alloy due to a supersaturated Nd enrichment that increases the Nd{sub 2}O{sub 3} content in the external oxide layer, as well as a more homogeneous structure and reduced grain size. These improvements contributed to the reduced formation of hydrogen gas and hydrogen embrittlement, which reduced the SCC sensitivity relative to the CC alloy. Therefore, EW62 in the form of a rapidly solidified extruded structure may serve as a biodegradable implant for biomedical applications. - Highlights: • Here we have evaluated the corrosion resistance of a novel Mg alloy (EW62). • Rapid solidification reduces the hydrogen gas evolution and hydrogen embrittlement. • Rapid solidification increases the stress corrosion cracking resistance of EW62. • Improvement is due to enrichment with supersaturated Nd in the external oxide film. • Rapidly solidified and extruded EW62 may serve as a biodegradable medical implant.

  13. Layer texture of hot-rolled BCC metals and its significance for stress-corrosion cracking of main gas pipelines

    Science.gov (United States)

    Perlovich, Yu. A.; Isaenkova, M. G.; Krymskaya, O. A.; Morozov, N. S.

    2016-10-01

    Based on data of X-ray texture analysis of hot-rolled BCC materials it was shown that the layerwise texture inhomogeneity of products is formed during their manufacturing. The effect can be explained by saturation with interstitial impurities of the surface layer, resulting in dynamical deformation aging (DDA). DDA prevents the dislocation slip under rolling and leads to an increase of lattice parameters in the external layer. The degree of arising inhomogeneity correlates with the tendency of hot-rolled sheets and obtained therefrom tubes to stress-corrosion cracking under exploitation, since internal layers have a compressive effect on external layers, and prevents opening of corrosion cracks at the tube surface.

  14. Effect of solution pH on the electrochemical polarization and stress corrosion cracking of Alloy 690 in 5 M NaCl at room temperature

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Y.Y. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China); Chou, L.B. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China); Shih, H.C. [Department of Materials Science and Engineering, National Tsing Hua University, 101, Sec. 2, Kuang Fu Road, Hsinchu 300, Taiwan (China)]. E-mail: hcshih@mse.nthu.edu.tw

    2005-04-15

    The effect of solution pH on the electrochemical polarization and stress corrosion cracking behaviors of the nickel-based Alloy 690 were investigated in this paper. An experimental, potential-pH diagram was constructed for Alloy 690 in a concentrated (5 M) sodium chloride (NaCl) solution at room temperature ({approx}25 deg. C), using a cyclic polarization method. The domains of immunity, general corrosion, passivation, and pitting in 5 M NaCl solutions were defined. At pH >4, the passive region subdivided into areas of perfect passivation, imperfect passivation, and pitting. After anodic polarization, the surface of each specimen was carefully examined metallographically. Pitting corrosion was observed over the entire pH range investigated (0.3-8.52) but general corrosion predominated at lower pH values (<3). On the other hand, the mechanical properties, such as ultimate tensile strength (UTS), fracture strain (FS) and the reduction in area (RA) measured by the slow strain rate test (SSRT), decreased significantly at pH <3. The SSRT results are consistent with fractography and side-view observations of the tested specimens by scanning electron microscopy (SEM)

  15. Stress corrosion cracking of X70 pipeline steel in near-neutral pH soil solution

    Energy Technology Data Exchange (ETDEWEB)

    Fang, B.Y.; Wang, J.Q.; Han, E.H.; Zhu, Z.Y.; Ke, W. [Chinese Academy of Sciences, Shenyang (China). State Key Laboratory for Corrosion and Protection, Inst. of Metal Research

    2004-07-01

    Near-neutral pH stress corrosion cracking (SCC) is characterized by wide transgranular cracks with quasi-cleavage on the fracture surface, and there is usually little evidence of general or lateral corrosion. Near-neutral pH SCC is related to dissolution and hydrogen ingress into steel pipes because discharged atomic hydrogen can enter the steel so that cracks are initiated or grown by a combination of dissolution and hydrogen-embrittlement. In this study, the SCC cracking behaviour of an X70 pipeline was investigated using slow strain rate tests (SSRT) and cyclic loading at high R and low frequency in a near-neutral pH soil solution saturated with 5 per cent carbon dioxide (CO{sub 2}) and 95 per cent nitrogen (N{sub 2}). Potentiodynamic polarization analyses and electrochemical impedance spectrum (EIS) analyses were also conducted in order to examine the effect of the concentration of bicarbonate, bubbled gas and the addition of chloride ions on polarization behaviour. Results of the SSRT tests showed that transgranular SCC occurred in the soil solution. Crack initiation was associated with pitting. The pipe's susceptibility to SCC increased with decreases in applied electrochemical potential and strain rate. Cyclic loading tests showed that crack propagation processes were dominated by SCC. At high R and low frequencies, SCC was observed on fatigued, pre-cracked specimens. Results of the electrochemical tests showed that polarization behaviours were influenced by the concentrations of bicarbonate, bubbled gas, and the addition of chloride ions. It was concluded that the addition of chloride ion can influence film stability on pipeline specimen surfaces. 22 refs., 2 tabs., 8 figs.

  16. The role of Hydrogen and Creep in Intergranular Stress Corrosion Cracking of Alloy 600 and Alloy 690 in PWR Primary Water Environments ? a Review

    Energy Technology Data Exchange (ETDEWEB)

    Rebak, R B; Hua, F H

    2004-07-12

    Intergranular attack (IGA) and intergranular stress corrosion cracking (IGSCC) of Alloy 600 in PWR steam generator environment has been extensively studied for over 30 years without rendering a clear understanding of the essential mechanisms. The lack of understanding of the IGSCC mechanism is due to a complex interaction of numerous variables such as microstructure, thermomechanical processing, strain rate, water chemistry and electrochemical potential. Hydrogen plays an important role in all these variables. The complexity, however, significantly hinders a clearer and more fundamental understanding of the mechanism of hydrogen in enhancing intergranular cracking via whatever mechanism. In this work, an attempt is made to review the role of hydrogen based on the current understanding of grain boundary structure and chemistry and intergranular fracture of nickel alloys, effect of hydrogen on electrochemical behavior of Alloy 600 and Alloy 690 (e.g. the passive film stability, polarization behavior and open-circuit potential) and effect of hydrogen on PWSCC behavior of Alloy 600 and Alloy 690. Mechanistic studies on the PWSCC are briefly reviewed. It is concluded that further studies on the role of hydrogen on intergranular cracking in both inert and primary side environments are needed. These studies should focus on the correlation of the results obtained at different laboratories by different methods on materials with different metallurgical and chemical parameters.

  17. The effects of cold rolling orientation and water chemistry on stress corrosion cracking behavior of 316L stainless steel in simulated PWR water environments

    Science.gov (United States)

    Chen, Junjie; Lu, Zhanpeng; Xiao, Qian; Ru, Xiangkun; Han, Guangdong; Chen, Zhen; Zhou, Bangxin; Shoji, Tetsuo

    2016-04-01

    Stress corrosion cracking behaviors of one-directionally cold rolled 316L stainless steel specimens in T-L and L-T orientations were investigated in hydrogenated and deaerated PWR primary water environments at 310 °C. Transgranular cracking was observed during the in situ pre-cracking procedure and the crack growth rate was almost not affected by the specimen orientation. Locally intergranular stress corrosion cracks were found on the fracture surfaces of specimens in the hydrogenated PWR water. Extensive intergranular stress corrosion cracks were found on the fracture surfaces of specimens in deaerated PWR water. More extensive cracks were found in specimen T-L orientation with a higher crack growth rate than that in the specimen L-T orientation with a lower crack growth rate. Crack branching phenomenon found in specimen L-T orientation in deaerated PWR water was synergistically affected by the applied stress direction as well as the preferential oxidation path along the elongated grain boundaries, and the latter was dominant.

  18. Equivalent Crack Size Modelling of Corrosion Pitting in an AA7050-T7451 Aluminium Alloy and its Implications for Aircraft Structural Integrity

    Science.gov (United States)

    2012-09-01

    provides a quantitative measurement of the spatial density of pits14 but there is no quantitative measurement of corrosion pit metrics without...and stress corrosion cracking in the 7075 T6 components of the RAAF C-130 Hercules...Post-Fracture Examination................................................................... 16 3.5.3 Surface Roughness Measurement

  19. A state of the art on primary side stress corrosion cracking in nuclear power plant

    Energy Technology Data Exchange (ETDEWEB)

    Kim, H. P.; Kim, J. S.; Han, J. H.; Lee, D. H.; Lim, Y. S.; Suh, J. H.; Hwang, S. S.; Hur, D. H

    1999-09-01

    A state of art on primary water stress corrosion cracking (PWSCC) of alloy 600 used as steam generator tubing of nuclear power plant and remedial action on the PWSCC were reviewed and analyzed. One of the major metallurgical factors which have effect on PWSCC is Cr carbide distribution. A semicontinuous intergranular Cr carbide distribution enhance PWSCC of alloy 600. PWSCC rate is reported to be reported to be proportional to exp(-50 cal/RT) {sigma}{sup 4}. PWSCC rate also increase with increase in hydrogen partial pressure from 0 to 150 ppm and then decreased with further increase in hydrogen partial pressure to 757 ppm. Development of PWSCC prediction technology which takes into account tubing material, fabrication process and operating history of steam generator is needed to manage PWSCC of domestic nuclear power plant. PWSCC has mainly occurred at expansion irregularities within tubesheet, expansion transitions, dented tube support plate intersections and transition and apex of U bend. Remedial actions to PWSCC are sleeving, plugging, temperature reduction, Ni plating, Ni sleeving, shot peening and steam generator replacement in worst case. Option to remedial actions depend on plant specific such as plant age, leak rate from primary to secondary, density and progression of PWSCC. Ni sleeving developed in Framatome seems to be a powerful method because it never subject to PWSCC. Remedial action should be developed and evaluated for possible PWSCC of domestic nuclear power plant. (author)

  20. Preparation Femtosecond Laser Prevention for the Cold-Worked Stress Corrosion Crackings on Reactor Grade Low Carbon Stainless Steel

    CERN Document Server

    John Minehara, Eisuke

    2004-01-01

    We report here that the femtosecond lasers like low average power Ti:Sapphire lasers, the JAERI high average power free-electron laser and others could peel off and remove two stress corrosion cracking (SCC) origins of the cold-worked and the cracking susceptible material, and residual tensile stress in hardened and stretched surface of low-carbon stainless steel cubic samples for nuclear reactor internals as a proof of principle experiment except for the third origin of corrosive environment. Because a 143 °C and 43% MgCl2 hot solution SCC test was performed for the samples to simulate the cold-worked SCC phenomena of the internals to show no crack at the laser-peered off strip on the cold-worked side and ten-thousands of cracks at the non-peeled off on the same side, it has been successfully demonstrated that the femtosecond lasers could clearly remove the two SCC origins and could resultantly prevent the cold-worked SCC.

  1. Topical Report ''Corrosion Evaluation of LLW2 Skid-B Weld Failure Mechanisms (44139-92)

    Energy Technology Data Exchange (ETDEWEB)

    JI Young Chang

    2001-05-31

    An independent investigation of pipe welding leaks from the Low-Level Waste 2 (LLW2) Skid-B System for the possibilities of improper welding (IW), microbiologically influenced corrosion (MIC), sensitization, chloride pitting corrosion (CPC), and intergranular stress corrosion cracking (IGSCC) was conducted. The results show the prevailing mechanisms that caused the leaks are identified as IW, CPC, and the improper selection of weld filler material for the base metals in an environment of the North Plateau underground water. These is no evidence of MIC, sensitization, or IGSCC. The chloride pitting corrosion mechanism that took place at all the welds are also described. All the pipelines were replaced with polyvinyl chloride (PVC) for cost saving and the LLW2 Skid B System has been successfully operating since 1999. This report summarizes the findings and recommendations associated with preventive measures for future operations. The LLW2 Facility is a replacement for an existing waste treatment system. The Facility processes two different waste streams through two different ''skids.'' After seven months of operation, one of the two skids began to leak. Extensive evaluation of the corrosion mechanisms and the contributing factors are documented in this report. This report principally evaluates the physical and chemical configurations that led to the corrosion and leaks. Chloride pitting corrosion, exacerbated by weld defects, is the corrosion mechanism. The report also discusses fabrication and Quality Assurance (QA)/Quality Control (QC) actions that would have prevented their occurrence. It is believed that in the absence of either the defects or the chloride concentrations, corrosion would not have occurred. In developing the specification for processing skids to be used in the Facility, high chloride was not identified as a parameter of concern. As such, piping fabrication and inspection standards for the system did not identify more rigorous

  2. Parameters influencing the transgranular stress corrosion cracking behaviour of austenitic stainless steels in systems conveying reactor coolant

    Energy Technology Data Exchange (ETDEWEB)

    Kilian, R.; Wesseling, U. [Framatome ANP (Germany); Wachter, O. [E.ON Kernkraft (Germany); Widera, M. [RWE Power (Germany); Brummer, G. [HEW - (Germany); Ilg, U. [EnBW - (Germany)

    2002-07-01

    During replacement of an auxiliary system in the German PWR KKS (NPP Stade) a damage was detected in a valve housing and in the connected piping both made from stabilised austenitic stainless steel. During operation stagnant conditions are present in this area. Based on the failure analysis chloride induced stress corrosion cracking (SCC) was found as the dominating root cause. In the open literature many cases of corrosion observed in the water/steam interface in valve components as well as in adjacent portions of auxiliary circuits made of un-stabilized stainless steels are mentioned. A common feature of the reported cases is that transgranular cracking was found. Extensive laboratory investigations revealed that non-stabilised austenitic stainless steels are also sensitive to transgranular cracking in boric acid solutions particularly in concentrated solutions. Often these solutions are contaminated with chlorides and/or oxygen is present. Taking into account the literature data the question could arise whether the above mentioned cracking may be also caused by boric acid attack. Thus, for stabilised stainless steels laboratory exposure tests at 80 C in saturated aerated boric acid solution and at 300 C in (at 100 C) saturated, oxygen free boric acid solution have been performed. Double-U-bend specimens and wedge loaded 1T-CT specimens made of Ti- and Nb-stabilised austenitic stainless steels were used. The results revealed no evidence of crack initiation and crack growth. Based on the laboratory results and the literature data an attempt is undertaken to separate parameters influencing chloride induced SCC from the effect of boric acid. (authors)

  3. Improvement of stress corrosion cracking (SCC) resistance by cyclic pre-straining of 316L austenitic stainless steel in an aqueous boiling MgCl{sub 2} solution; Amelioration de la tenue a la corrosion sous contrainte (CSC) de l'acier inoxydable austenitique 316L en solution bouillante de MgCl{sub 2} par application d'une predeformation cyclique

    Energy Technology Data Exchange (ETDEWEB)

    Curiere, I. de; Bayle, B.; Magnin, Th. [Ecole Nationale Superieure des Mines, URA CNRS 1884, 42 - Saint-Etienne (France)

    2000-07-01

    Improving the materials resistance to stress corrosion cracking (SCC) has become a topic of wide interest for theoretical, engineering and financial reasons. The aim of this paper is to propose a process to delay the SCC damage. Recent studies of 316L austenitic stainless steel in boiling MgCl{sub 2} solutions show an improvement in SCC resistance by cyclic pre-straining in low cycle fatigue. This improvement consists of an increase in both strain to failure and crack initiation strain, during Slow Rate Tensile (SSRT) tests in aqueous solution. This paper analyses the effect of pre-fatigue in 316L on its mechanical and electrochemical responses to better understand the delay of SCC damage in boiling MgCl{sub 2}. The explanation for this beneficial effect is related to a modification of both surface electrochemical reactions kinetics and corrosion/plasticity interactions at the crack tip, due to the particular dislocation structure. (authors)

  4. Recent progress to understand stress corrosion cracking in sodium borosilicate glasses: linking the chemical composition to structural, physical and fracture properties

    Science.gov (United States)

    Rountree, Cindy L.

    2017-08-01

    This topical review is dedicated to understanding stress corrosion cracking in oxide glasses and specifically the SiO_2{\\text-B_2O_3{\\text-}Na_2O} (SBN) ternary glass systems. Many review papers already exist on the topic of stress corrosion cracking in complex oxide glasses or overly simplified glasses (pure silica). These papers look at how systematically controlling environmental factors (pH, temperature...) alter stress corrosion cracking, while maintaining the same type of glass sample. Many questions still exist, including: What sets the environmental limit? What sets the velocity versus stress intensity factor in the slow stress corrosion regime (Region I)? Can researchers optimize these two effects to enhance a glass’ resistance to failure? To help answer these questions, this review takes a different approach. It looks at how systemically controlling the glass’ chemical composition alters the structure and physical properties. These changes are then compared and contrasted to the fracture toughness and the stress corrosion cracking properties. By taking this holistic approach, researchers can begin to understand the controlling factors in stress corrosion cracking and how to optimize glasses via the initial chemical composition.

  5. Critical issues in De-alloying and transcrystalline stress-corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Sieradzki, K.; Wagner, J.W.

    1992-03-01

    This report describes our progress since the last reporting reporting period (March 1991) and details the third year research plans on the program. The three major components of the program relate to (1) kinetic aspects of the selective dissolution in alloys and the coarsening of de-alloyed layers, (2) measurements of crack dynamics during film induced cleavage processes, and (3) mechanical properties of the intrinsic de-alloyed layers responsible for film-induced cleavage events. We discuss progress in each of these areas below.

  6. Electrochemical and Sulfide Stress Corrosion Cracking Behaviors of Tubing Steels in a H2S/CO2 Annular Environment

    Science.gov (United States)

    Liu, Z. Y.; Wang, X. Z.; Liu, R. K.; Du, C. W.; Li, X. G.

    2014-04-01

    The electrochemical and sulfide stress corrosion cracking (SSCC) behaviors of 13Cr stainless steel and P110 steel were investigated in a simulated acidic annular environment with low-temperature and high-pressure H2S/CO2 using electrochemical methods, U-bend immersion tests, and scanning electron microscopy. In the solution containing high pressure CO2, 13Cr, and P110 steels exhibited general corrosion and severe pitting, respectively. Compared with sweet corrosion, additional H2S in the solution enhanced the corrosion of 13Cr steel but inhibited the corrosion of P110 steel. By contrast, in a solution containing 4 MPa CO2 and different (0-0.3 MPa), the susceptibility of both 13Cr stainless steel and P110 steel toward SSCC was significantly promoted by increases in H2S partial pressure. The 13Cr stainless steel exhibited higher susceptibility toward SSCC than P110 steel under a H2S/CO2 environment but lower susceptibility under a pure CO2 environment.

  7. Improved stress corrosion cracking resistance of a novel biodegradable EW62 magnesium alloy by rapid solidification, in simulated electrolytes.

    Science.gov (United States)

    Hakimi, O; Aghion, E; Goldman, J

    2015-06-01

    The high corrosion rate of magnesium (Mg) and Mg-alloys precludes their widespread acceptance as implantable biomaterials. Here, we investigated the potential for rapid solidification (RS) to increase the stress corrosion cracking (SCC) resistance of a novel Mg alloy, Mg-6%Nd-2%Y-0.5%Zr (EW62), in comparison to its conventionally cast (CC) counterpart. RS ribbons were extrusion consolidated in order to generate bioimplant-relevant geometries for testing and practical use. Microstructural characteristics were examined by SEM. Corrosion rates were calculated based upon hydrogen evolution during immersion testing. The surface layer of the tested alloys was analyzed by X-ray photoelectron spectroscopy (XPS). Stress corrosion resistance was assessed by slow strain rate testing and fractography. The results indicate that the corrosion resistance of the RS alloy is significantly improved relative to the CC alloy due to a supersaturated Nd enrichment that increases the Nd2O3 content in the external oxide layer, as well as a more homogeneous structure and reduced grain size. These improvements contributed to the reduced formation of hydrogen gas and hydrogen embrittlement, which reduced the SCC sensitivity relative to the CC alloy. Therefore, EW62 in the form of a rapidly solidified extruded structure may serve as a biodegradable implant for biomedical applications.

  8. Influence of plastic strain localization on the stress corrosion cracking of austenitic stainless steels; Influence de la localisation de la deformation plastique sur la CSC d'aciers austenitiques inoxydables

    Energy Technology Data Exchange (ETDEWEB)

    Cisse, S.; Tanguy, B. [CEA Saclay, DEN, SEMI, 91 - Gif-sur-Yvette (France); Andrieu, E.; Laffont, L.; Lafont, M.Ch. [Universite de Toulouse. CIRIMAT, UPS/INPT/CNRS, 31 - Toulous (France)

    2010-03-15

    The authors present a research study of the role of strain localization on the irradiation-assisted stress corrosion cracking (IASCC) of vessel steel in PWR-type (pressurized water reactor) environment. They study the interaction between plasticity and intergranular corrosion and/or oxidation mechanisms in austenitic stainless steels with respect to sublayer microstructure transformations. The study is performed on three austenitic stainless grades which have not been sensitized by any specific thermal treatment: the A286 structurally hardened steel, and the 304L and 316L austenitic stainless steels

  9. Electrochemical investigation of crack initiation during corrosion fatigue of stainless steels in the passive state. Elektrochemische Untersuchung der Rissbildung bei Schwingungsrisskorrosion im stabil-passiven Werkstoffzustand

    Energy Technology Data Exchange (ETDEWEB)

    Spaehn, R. (Technische Hochschule Darmstadt (Germany, F.R.))

    1991-03-01

    The corrosion fatigue behaviour of three stainless steels - ferritic (12% Cr), austenitic (type 316 Ti) and austenitic-ferritic (type 31803; Duplex stainless steel) - was studied under rotating bending moments in aqueous sulphuric acid of 30deg C. An instrumental set-up for recording the transient currents of specimens during potentiostatically controlled corrosion fatigue is described. Based on this transient current signal technique, three stages on the corrosion fatigue process can be discerned. In the incubation period, small stochastic current transients are caused by the response of the passive layer to alternating stresses and environmental conditions. The appearance of sinusoidal current signals indicates crack initiation whereas the phase angle between a fixed marker - i.e. a light barrier signal -, and the anodic amplitude represents the site of initiating cracks. Finally, the crack growth period is characterized by an increasing cell current and steadily growing sinusoidal current signals caused by the interplay of microplastic and repassivation processes at the crack tip. (orig.).

  10. Study on Cracking Tendency and Mechanism of Gray Cast Iron Laser Cladding

    Institute of Scientific and Technical Information of China (English)

    YEHong; YANZhong-lin; HUANGQi; YANGHui

    2004-01-01

    In this paper, NiCrSiB and COWC35 powder has been used in laser cladding of gray cast iron. The cracking tendency has also been discussed. The cracks have been observed with a scan electron microscopy to analyze the cracking mechanism. The results show that cracks have not appeared in NiCrSiB cladding. Nevertheless, the cracking tendency of CoWC35 cladding is extremely high and there are both cold cracks and hot cracks in the cladding. The cracking tendency of laser cladding depends on physical properties of the cladding material and plasticity and roughness of the cladding.

  11. Study on Cracking Tendency and Mechanism of Gray Cast Iron Laser Cladding

    Institute of Scientific and Technical Information of China (English)

    YE Hong; YAN Zhong-lin; HUANG Qi; YANG Hui

    2004-01-01

    In this paper, NiCrSiB and CoWC35 powder has been used in laser cladding of gray cast iron. The cracking tendency has also been discussed. The cracks have been observed with a scan electron microscopy to analyze the cracking mechanism. The results show that cracks have not appeared in NiCrSiB cladding. Nevertheless, the cracking tendency of CoWC35 cladding is extremely high and there are both cold cracks and hot cracks in the cladding. The cracking tendency of laser cladding depends on physical properties of the cladding material and plasticity and roughness of the cladding.

  12. Evaluation of the resistance of API 5L-X80 girth welds to sulphide stress corrosion cracking and hydrogen embrittlement

    Energy Technology Data Exchange (ETDEWEB)

    Forero, Adriana [Pontificia Universidade Catolica (PUC-Rio), Rio de Janeiro, RJ (Brazil); Ponciano, Jose A. [Universidade Federal do Rio de Janeiro (COPPE/UFRJ), RJ (Brazil). Coordenacao dos Programas de Pos-graduacao em Engenharia; Bott, Ivani de S. [Pontificia Universidade Catolica do Rio de Janeiro (PUC-Rio), Rio de Janeiro, RJ (Brazil). Dept. de Ciencia dos Materiais e Metalurgia

    2009-07-01

    The susceptibility of pipeline steels to stress corrosion cracking (SCC) depends on a series of factors ranging from the manufacture of the steel, the pipe fabrication and the assembly of the pipeline to the type of substances to be transported. The welding procedures adopted during the production and construction of the pipelines (field welding), can modify the properties of the base metal in the heat affected zone (HAZ), potentially rendering this region susceptible to SCC. This study evaluates the resistance of girth welds, in API 5L X80 pipes, to hydrogen embrittlement and to stress corrosion cracking in the presence of sulphides. The evaluation was performed according to NACE TM0177/96, Method A, applying the criterion of fracture/no fracture, and Slow Strain Rate Tensile tests (SSRT) were undertaken using a sodium thiosulphate solution according to the ASTM G129-00 Standard. According NACE requirements, the base metal was approved. The weld metal exhibited susceptibility to SCC in the presence of sulphides, failing in a period of less than 720h. This was confirmed by SSR tensile tests, where a significant decrease in the ultimate tensile strength, the elongation and the time to fracture were observed. The mechanism of fracture was transgranular. (author)

  13. The corrosion and stress corrosion cracking behavior of a novel alumina-forming austenitic stainless steel in supercritical water

    Science.gov (United States)

    Sun, Hongying; Yang, Haijie; Wang, Man; Giron-Palomares, Benjamin; Zhou, Zhangjian; Zhang, Lefu; Zhang, Guangming

    2017-02-01

    The general corrosion and stress corrosion behavior of Fe-27Ni-15Cr-5Al-2Mo-0.4Nb alumina-forming austenitic (AFA) steel were investigated in supercritical water under different conditions. A double layer oxide structure was formed: a Fe-rich outer layer (Fe2O3 and Fe3O4) and an Al-Cr-rich inner layer. And the inner layer has a low growth rate with exposing time, which is good for improvement of corrosion resistance. Additionally, some internal nodular Al-Cr-rich oxides were also observed, which resulted in a local absence of inner layer. Stress corrosion specimens exhibited a combination of high strength, good ductility and low susceptibility. The stress strength and elongation was reduced by increasing temperature and amount of dissolved oxygen. In addition, the corresponding susceptibility was increased with decreased temperatures and increased oxygen contents.

  14. Waste incineration corrosion processes: Oxidation mechanisms by electrochemical impedance spectroscopy

    Energy Technology Data Exchange (ETDEWEB)

    Perez, F.J.; Hierro, M.P.; Nieto, J. [Departamento de Ciencia de los Materiales. Facultad de Ciencias Quimicas, Grupo de Investigacion de Ingenieria de Superficies, Universidad Complutense de Madrid, 28040 Madrid (Spain)

    2008-07-15

    Molten chloride mixtures are formed in waste incineration plants during waste firing and energy production. These mixtures are responsible for degradation processes like hot corrosion. In order to evaluate the damage of molten salt mixtures in waste incineration environments, the alloys 625 and 617 were exposed beneath a molten KCl-ZnCl{sub 2} mixture at 650 C in air. The corrosion process was monitored by electrochemical impedance spectroscopy (EIS). An extensive microscopy analysis has been done in order to correlate the electrochemical results, and to establish an electrochemical mechanism for such high temperature corrosion processes. (Abstract Copyright [2008], Wiley Periodicals, Inc.)

  15. Development of Modified 304 Stainless Steel Resistant to Stress Corrosion Cracking in Chloride Environment

    Institute of Scientific and Technical Information of China (English)

    2002-01-01

    This was a feasibility study for a modified 304 steel resistant to stress corrosion cracking (SCC) in aqueous environment containing chloride. SCC tests were conducted potentiostaticaly with spot-welded specimens, which had both crevice and residual stress, mainly in 3 % NaCl solution at various temperatures to determine the critical temperature for SCC at and below which the steel would not suffer from SCC. The effects of individual alloying element of silicon, manganese and copper on SCC of 18Cr-14Ni steels which phosphor content is 0.002 % and molybdenum content is 0.01 % were examined. Addition of 1 or 2 % of copper has beneficial effect on resistance to SCC, while increasing silicon or manganese content has no significant effect. Critical temperature of the steel with 0.002 % of phosphor and 2 % of copper is 150 ℃, which is markedly higher than 50 ℃ of 304L steel. However, the beneficial effect of copper is reduced with increasing phosphor content. From practical viewpoint, the modified steel with good SCC resistance should have 0.01 %-0.015 % of phosphor and 0.3 % or more of molybdenum, because it is very difficult to reduce phosphor content below 0.008 % industrially and such molybdenum content is inevitably introduced through cost-saving melting process using return steel. Aluminium is to be added as another alloying element and 3 % of aluminium combined with 2 % of copper has been found to negate the deleterious effects of increased phosphor and molybdenum content. As a candidate steel at this stage, 14Cr-16Ni-0.013P-2Cu-1Al-(0.3-1)Mo steel has critical temperature of 110 ℃.

  16. Mechanism for Corrosion Prevention by a Mechanical Plating of Uniform Zinc-Iron Alloy

    Science.gov (United States)

    Kasai, Naoya; Kaku, Yoshihiko; Okazaki, Shinji; Hirai, Kuninori

    2016-09-01

    In situ electrochemical monitoring with a three-electrode cell was applied to investigate the anti-corrosion properties of a mechanical zinc-iron alloy plating. Several electron probe microanalyses were also conducted to identify the chemical elements in the plating. The results indicated the formation of a Zn-Fe intermetallic compound, which allowed a mechanism for corrosion prevention to be proposed. In the proposed mechanism, Zn(OH)2 plays a significant role in the corrosion prevention of steel alloys.

  17. Hydrogen embrittlement and hydrogen induced stress corrosion cracking of high alloyed austenitic materials; Wasserstoffversproedung und wasserstoffinduzierte Spannungsrisskorrosion hochlegierter austenitischer Werkstoffe

    Energy Technology Data Exchange (ETDEWEB)

    Mummert, K.; Uhlemann, M.; Engelmann, H.J. [Institut fuer Festkoerper- und Werkstofforschung Dresden e.V. (Germany)

    1998-11-01

    The susceptiblity of high alloyed austenitic steels and nickel base alloys to hydrogen-induced cracking is particularly determined by 1. the distribution of hydrogen in the material, and 2. the microstructural deformation behaviour, which last process is determined by the effects of hydrogen with respect to the formation of dislocations and the stacking fault energy. The hydrogen has an influence on the process of slip localization in slip bands, which in turn affects the microstructural deformation behaviour. Slip localization increases with growing Ni contents of the alloys and clearly reduces the ductility of the Ni-base alloy. Although there is a local hydrogen source involved in stress corrosion cracking, emanating from the corrosion process at the cathode, crack growth is observed only in those cases when the hydrogen concentration in a small zone ahead of the crack tip reaches a critical value with respect to the stress conditions. Probability of onset of this process gets lower with growing Ni content of the alloy, due to increasing diffusion velocity of the hydrogen in the austenitic lattice. This is why particularly austenitic steels with low Ni contents are susceptible to transcrystalline stress corrosion cracking. In this case, the microstructural deformation process at the crack tip is also influenced by analogous processes, as could be observed in hydrogen-loaded specimens. (orig./CB) [Deutsch] Die Empfindlichkeit von hochlegierten austentischen Staehlen und Nickelbasislegierungen gegen wasserstoffinduziertes Risswachstum wird im wesentlichen bestimmt durch 1. die Verteilung von Wasserstoff im Werkstoff und 2. das mikrostrukturelle Verformungsverhalten. Das mikrostrukturelle Deformationsverhalten ist wiederum durch den Einfluss von Wasserstoff auf die Versetzungsbildung und die Stapelfehlerenergie charakterisiert. Das mikrostrukturelle Verformungsverhalten wird durch wasserstoffbeeinflusste Gleitlokalisierung in Gleitbaendern bestimmt. Diese nimmt mit

  18. Stress corrosion mechanisms of alloy-600 polycrystals and monocrystals in primary water: effect of hydrogen; Mecanismes de corrosion sous contrainte de l'alliage 600 polycristallin et monocristallin en milieu primaire: role de l'hydrogene

    Energy Technology Data Exchange (ETDEWEB)

    Foct, F

    1999-01-08

    The aim of this study is to identify the mechanisms involved in Alloy 600 primary water stress corrosion cracking. Therefore, this work is mainly focussed on the two following points. The first one is to understand the influence of hydrogen on SCC of industrial Alloy 600 and the second one is to study the crack initiation and propagation on polycrystals and single crystals. A cathodic potential applied during slow strain rate tests does not affect crack initiation but increases the slow crack growth rate by a factor 2 to 5. Cathodic polarisation, cold work and 25 cm{sup 3} STP/kg hydrogen content increase the slow CGR so that the K{sub ISCC} (and therefore fast CGR) is reached. The influence of hydrogenated primary water has been studied for the first time on Alloy 600 single crystals. Cracks cannot initiate on tensile specimens but they can propagate on pre-cracked specimens. Transgranular cracks present a precise crystallographic aspect which is similar to that of 316 alloy in MgCl{sub 2} solutions. Moreover, the following results improve the description of the cracking conditions. Firstly, the higher the hydrogen partial pressure, the lower the Alloy 600 passivation current transients. Since this result is not correlated with the effect of hydrogen on SCC, cracking is not caused by a direct effect of dissolved hydrogen on dissolution. Secondly, hydrogen embrittlement of Alloy 600 disappears at temperatures above 200 deg.C. Thirdly, grain boundary sliding (GBS) does not directly act on SCC but shows the mechanical weakness of grain boundaries. Regarding the proposed models for Alloy 600 SCC, it is possible to draw the following conclusions. Internal oxidation or absorbed hydrogen effects are the most probable mechanisms for initiation. Dissolution, internal oxidation and global hydrogen embrittlement models cannot explain crack propagation. On the other hand, the Corrosion Enhanced Plasticity Model gives a good description of the SCC propagation. (author)

  19. Inclusion size effect on the fatigue crack propagation mechanism and fracture mechanics of a superalloy

    Science.gov (United States)

    Denda, Takeshi; Bretz, Perter L.; Tien, John K.

    1992-02-01

    Low cycle fatigue life of nickel-base superalloys is enhanced as a consequence of inclusion reduction in the melt process; however, the functional dependencies between fatigue characteristics and inclusions have not been well investigated. In this study, the propagation mechanism of the fatigue crack initiated from inclusions is examined in fine-grained IN718, which is a representative turbine disc material for jet engines. There is a faceted-striated crack transition on the fracture surfaces. This faceted-striated transition also appears in the da/dN vs crack length curves. It is observed that the faceted crack propagation time can be more than 50 pct of total lifetime in the low cycle fatigue test. The significance of inclusion size effect is explained on the premise that the faceted fatigue crack propagation time scales with the inclusion size, which is taken as the initial crack length. A predictive protocol for determining inclusion size effect is given.

  20. Interaction of sulfuric acid corrosion and mechanical wear of iron

    Science.gov (United States)

    Rengstorff, G. W. P.; Miyoshi, K.; Buckley, D. H.

    1986-01-01

    Friction and wear experiment were conducted with elemental iron sliding on aluminum oxide in aerated sulfuric acid at concentrations ranging from very dilute (0.00007 N; i.e., 4 ppm) to very concentrated (96 percent acid). Load and reciprocating sliding speed were kept constant. With the most dilute acid concentration of 0.00007 to 0.0002 N, a complex corrosion product formed that was friable and often increased friction and wear. At slightly higher concentrations of 0.001 N, metal losses were essentially by wear alone. Because no buildup of corrosion products occurred, this acid concentration became the standard from which to separate metal loss from direct corrosion and mechanical wear losses. When the acid concentration was increased to 5 percent (1 N), the well-established high corrosion rate of iron in sulfuric acid strongly dominated the total wear loss. This strong corrosion increased to 30 percent acid and decreased somewhat to 50 percent acid in accordance with expectations. However, the low corrosion of iron expected at acid concentrations of 65 to 96 percent was not observed in the wear area. It was apparent that the normal passivating film was being worn away and a galvanic cell established that rapidly attacked the wear area. Under the conditions where direct corrosion losses were highest, the coefficient of friction was the lowest.

  1. Mechanism of selective corrosion in electrical resistance seam welded carbon steel pipe

    Energy Technology Data Exchange (ETDEWEB)

    Lopez Fajardo, Pedro; Godinez Salcedo, Jesus; Gonzalez Velasquez, Jorge L. [Instituto Politecnico Nacional, Mexico D.F., (Mexico). Escuela Superior de Ingenieria Quimica e Industrias Extractivas. Dept. de Ingenieria Metalurgica

    2009-07-01

    In this investigation the studies of the mechanism of selective corrosion in electrical resistance welded (ERW) carbon steel pipe was started. Metallographic characterizations and evaluations for inclusions were performed. The susceptibility of ERW pipe to selective corrosion in sea water (NACE 1D182, with O{sub 2} or CO{sub 2} + H{sub 2}S) was studied by the stepped potential Potentiostatic electrochemical test method in samples of 1 cm{sup 3} (ASTM G5) internal surface of the pipe (metal base-weld). The tests were looking for means for predicting the susceptibility of ERW pipe to selective corrosion, prior to placing the pipeline in service. Manganese sulfide inclusions are observed deformed by the welding process and they are close to the weld centerline. A slight decarburization at the weld line is observed, and a distinct out bent fiber pattern remains despite the post-weld seam annealing. The microstructure of the weld region consists of primarily polygonal ferrite grains mixed with small islands of pearlite. It is possible to observe the differences of sizes of grain of the present phases in the different zones. Finally, scanning electron microscopic observation revealed that the corrosion initiates with the dissolution of MnS inclusions and with small crack between the base metal and ZAC. (author)

  2. Corrosion

    Science.gov (United States)

    Slabaugh, W. H.

    1974-01-01

    Presents some materials for use in demonstration and experimentation of corrosion processes, including corrosion stimulation and inhibition. Indicates that basic concepts of electrochemistry, crystal structure, and kinetics can be extended to practical chemistry through corrosion explanation. (CC)

  3. Corrosion

    Science.gov (United States)

    Slabaugh, W. H.

    1974-01-01

    Presents some materials for use in demonstration and experimentation of corrosion processes, including corrosion stimulation and inhibition. Indicates that basic concepts of electrochemistry, crystal structure, and kinetics can be extended to practical chemistry through corrosion explanation. (CC)

  4. Effect of Pre-aging on Stress Corrosion Cracking of Spray-formed 7075 Alloy in Retrogression and Re-aging

    Science.gov (United States)

    Su, Rui-ming; Qu, Ying-dong; You, Jun-hua; de Li, Rong-

    2015-11-01

    The effects of pre-aging in retrogression and re-aging (RRA) treatment on microstructure, mechanical properties, and stress corrosion cracking (SCC) behavior of spray-formed 7075 aluminum alloy were investigated by tensile test, slow strain rate test, and transmission electron microscope. The results show that the under aging (120 °C for 16 h) as the pre-aging in RRA treatment can vastly improve the mechanical properties and the SCC resistance of the alloy, compared with early aging (120 °C for 8 h), peak aging (120 °C for 24 h), and over aging (120 °C for 32 h) treatments, the ultimate tensile strength of the alloy is 782 MPa, which is higher than that for peak aging or conventional RRA treatment; and the SCC resistance of the alloy is also excellent after RRA with under aging as pre-aging.

  5. Improved Stress Corrosion Cracking Resistance and Strength of a Two-Step Aged Al-Zn-Mg-Cu Alloy Using Taguchi Method

    Science.gov (United States)

    Lin, Lianghua; Liu, Zhiyi; Ying, Puyou; Liu, Meng

    2015-12-01

    Multi-step heat treatment effectively enhances the stress corrosion cracking (SCC) resistance but usually degrades the mechanical properties of Al-Zn-Mg-Cu alloys. With the aim to enhance SCC resistance as well as strength of Al-Zn-Mg-Cu alloys, we have optimized the process parameters during two-step aging of Al-6.1Zn-2.8Mg-1.9Cu alloy by Taguchi's L9 orthogonal array. In this work, analysis of variance (ANOVA) was performed to find out the significant heat treatment parameters. The slow strain rate testing combined with scanning electron microscope and transmission electron microscope was employed to study the SCC behaviors of Al-Zn-Mg-Cu alloy. Results showed that the contour map produced by ANOVA offered a reliable reference for selection of optimum heat treatment parameters. By using this method, a desired combination of mechanical performances and SCC resistance was obtained.

  6. Stress corrosion cracking in the vessel closure head penetrations of French PWR`s; Fissuration par corrosion sous contrainte de penetrations de couvercle de cuve de reacteur nucleaire francais a eau pressurisee

    Energy Technology Data Exchange (ETDEWEB)

    Buisine, D.; Cattant, F.; Champredonde, J.; Pichon, C.; Benhamou, C.; Gelpi, A.; Vaindirlis, M.

    1994-01-01

    During a hydrotest in September 1991, part of the statutory decennial in-service inspection, a leak was detected on the vessel head of Bugey 3, which is one of the first 900 MW 3-loop PWR`s in France. This leak was due to a cracked penetration used for a control rod drive mechanism. The investigations performed identified Primary Stress Corrosion Cracking of Alloy 600 as being the origin of this degradation. So a lot of the same design PWR`s are a concern due to this generic problem. In this case, PWSCC was linked to: - hot temperature of the vessel head; - high residual stresses due to the welding process between peripherical penetrations and the vessel head; - sensitivity of forged Alloy 600 used for penetration manufacturing. This following paper will present the cracked analysis based, in particular, on the main results obtained in France on each of these items. These results come from the operating experience, the destructive examinations and the programs which are running on stress analysis and metallurgical characterizations. (authors). 9 figs., 2 tabs.

  7. Microbiologically Influenced Corrosion: Global Phenomena, Local Mechanisms

    Science.gov (United States)

    2011-02-17

    because extent of ennoblement is affected by sample size. How rale and temperature (Little et al. 2008). Ennoblement has been measured for metals boldly...exposed, metals incorporated in crevice assemblies and polarized metals . The alloys tested include, but are not limited to: UNS S30400, S30403...fresh water, ennoblement can be the result of microbial deposition of manganese and localized corrosion has been related directly to the biomineralized

  8. Corrosion and mechanical behavior of materials for coal gasification applications

    Energy Technology Data Exchange (ETDEWEB)

    Natesan, K.

    1980-05-01

    A state-of-the-art review is presented on the corrosion and mechanical behavior of materials at elevated temperatures in coal-gasification environments. The gas atmosphere in coal-conversion processes are, in general, complex mixtures which contain sulfur-bearing components (H/sub 2/S, SO/sub 2/, and COS) as well as oxidants (CO/sub 2//CO and H/sub 2/O/H/sub 2/). The information developed over the last five years clearly shows sulfidation to be the major mode of material degradation in these environments. The corrosion behavior of structural materials in complex gas environments is examined to evaluate the interrelationships between gas chemistry, alloy chemistry, temperature, and pressure. Thermodynamic aspects of high-temperature corrosion processes that pertain to coal conversion are discussed, and kinetic data are used to compare the behavior of different commercial materials of interest. The influence of complex gas environments on the mechanical properties such as tensile, stress-rupture, and impact on selected alloys is presented. The data have been analyzed, wherever possible, to examine the role of environment on the property variation. The results from ongoing programs on char effects on corrosion and on alloy protection via coatings, cladding, and weld overlay are presented. Areas of additional research with particular emphasis on the development of a better understanding of corrosion processes in complex environments and on alloy design for improved corrosion resistance are discussed. 54 references, 65 figures, 24 tables.

  9. Electro chemical studies on stress corrosion cracking of Incoloy-800 in caustic solution, part I: As received samples

    Directory of Open Access Journals (Sweden)

    Dinu Alice

    2005-01-01

    Full Text Available Many non-volatile impurities accidentally introduced into the steam generator tend to Concentrate on its surface in restricted flow areas. In this way these impurities can lead to stress corrosion cracking (SCC on stressed tubes of the steam generator. Such impurities can be strong alkaline or acid solutions. To evaluate the effect of alkaline concentrated environments on SCC of steam generator tubes, the tests were con ducted on stressed samples of Incoloy-800 in 10% NaOH solution. To accelerate the SCC process, stressed specimens were anodically polarised in a caustic solution in an electro chemical cell. The method of stressing of Incoloy-800 tubes used in our experiments was the C-ring. Using the cathodic zone of the potentiodynamic curves it was possible to calculate the most important electrochemical parameters: the corrosion current, the corrosion rate, and the polarization resistance. We found that the value of the corrosion potential to initiate the SCC microcracks was -100 mV. The tested samples were examined using the metallographic method. The main experimental results showed that the in crease of the stress state promoted the in crease of the SCC susceptibility of Incoloy-800 samples tested under the same conditions, and that the length of the SCC-type microcracks in creased with the growth of the stress value.

  10. Effect of cracking and randomness of inputs on corrosion initiation of reinforced concrete bridge decks exposed to chlorides

    Directory of Open Access Journals (Sweden)

    P. Konecny

    2017-01-01

    Full Text Available The paper is aimed at the indicative evaluation of the effect of random scatter of input parameters in case of durability of reinforced concrete bridge deck. The time to onset of corrosion of steel reinforcement of concrete bridge deck exposed to chloride is evaluated. The effect of cracking in concrete onto chloride ingress is considered. The selected steel reinforcement protection strategies are: unprotected steel reinforcement, epoxy-coated steel reinforcement and water-proof barrier bellow asphalt overlay. The preliminary model for damage effect on chloride ion ingress through water proof membrane under penetrable asphalt overlay is used. 2-D finite element chloride ingress model is combined with Monte Carlo simulation technique. The innovative crack effect modeling via highly penetrable elements is applied. Deterministic and probabilistic calculations are compared.

  11. Stress corrosion cracking susceptibility of a high strength Mg-7%Gd-5%Y-1%Nd-0.5%Zr alloy

    Directory of Open Access Journals (Sweden)

    S.D. Wang

    2014-12-01

    Full Text Available Through performing the tensile tests with different strain rates in 3.5 wt.% NaCl solution, the stress corrosion cracking (SCC behavior and the effect of strain rate on the SCC susceptibility of an extruded Mg-7%Gd-5%Y-1%Nd-0.5%Zr (EW75 alloy have been investigated. Results demonstrate that the alloy is susceptible to SCC when the strain rate is lower than 5 × 10−6 s−1. At the strain rate of 1 × 10−6 s−1, the SCC susceptibility index (ISCC is 0.96 and the elongation-to-failure (εf is only 0.11%. Fractography indicates that the brittle quasi-cleavage feature is very obvious and become more pronounced with decreasing the strain rate. Further analysis confirms that the cracking mode is predominantly transgranular, but the partial intergranular cracking at some localized area can also occur. Meanwhile, it seems that the crack propagation path is unrelated to the existing phase particles.

  12. Study of the sulphide stress corrosion cracking (SSCC) resistance of API SL GR B and X60 pipeline steels. Evaluacion de la resistencia al agrietamiento por corrosion-tension en medios sulfhidricos (SSCC) de aceros para tuberias Calidad API 5L Grados B y X60

    Energy Technology Data Exchange (ETDEWEB)

    Bao-Iturbe, C. (Babcock and Wilcox Espaola. S.A. Bilbao (Spain)); Gutierrez de Saiz-Solabarria (Univ. Pais Vasco. Departamento Ingenieria Metalurgica y Control de Materiales. Bilbao (Spain))

    1993-01-01

    A study of the sulphide stress corrosion cracking resistance at room temperature of API 5L Cr B and X60 pipeline steels has been carried out. The theoretical mechanisms in order to explain these phenomena and several operational failures of pipeline steel due to SSCC have been reviewed and the National Association of Corrosion Engineers (NACE) standard concerning SSCC has been described. The main factors of influence of the SSCC have been analysed, results are presented and conclusions are elaborated. (Author) 32 ref.

  13. Mechanism of Irradiation Assisted Cracking of Core Components in Light Water Reactors

    Energy Technology Data Exchange (ETDEWEB)

    Was, Gary S; Atzmon, Michael; Wang, Lumin

    2003-04-28

    The overall goal of the project is to determine the mechanism of irradiation assisted stress corrosion cracking (IASCC). IASCC has been linked to hardening, microstructural and microchemical changes during irradiation. Unfortunately, all of these changes occur simultaneously and at similar rates during irradiation, making attribution of IASCC to any one of these features nearly impossible to determine. The strategy set forth in this project is to develop means to separate microstructural from microchemical changes to evaluate each separately for their effect on IASCC. In the first part, post irradiation annealing (PIA) treatments are used to anneal the irradiated microstructure, leaving only radiation induced segregation (RIS) for evaluation for its contribution to IASCC. The second part of the strategy is to use low temperature irradiation to produce a radiation damage dislocation loop microstructure without radiation induced segregation in order to evaluate the effect of the dislocation microstructure alone.

  14. C10H18N2Na2O10 inhibition and adsorption mechanism on concrete steel-reinforcement corrosion in corrosive environments

    National Research Council Canada - National Science Library

    Okeniyi, Joshua Olusegun

    2016-01-01

    C10H18N2Na2O10 (ethylenediaminetetra-acetic acid disodium salt) inhibition and adsorption mechanism on the corrosion of steel-reinforcement corrosion in concrete immersed in corrosive environments were investigated in this paper...

  15. Assessment of ultrasonic techniques for characterization of stress corrosion cracks in SG partition stubs

    Energy Technology Data Exchange (ETDEWEB)

    Sartre, B.; Banchet, J. [AREVA NP, Saint-Marcel (France); Moras, D.; Bastin, P. [Intercontrole, Rungis (France); Beroni, C. [EDF/CEIDRE, Saint-Denis (France)

    2006-07-01

    Studies by EDF and AREVA NP on Inconel zones have identified the Inconel 600 partition stubs of steam generators as potential areas of SCC, on the hot leg side. Decision was made to perform an expert assessment using ultrasonic testing (UT) techniques to be applied on the whole area of the stub showing penetrant testing (PT) techniques indications. UT techniques, probes and tools were then developed for that purpose. The aim is to size shallow defects, sizing capacity being maintained for defects propagated to a half-thickness. Although no formal qualification was required, the development was performed in view of a performance demonstration. Three mock-ups were manufactured by AREVA NP: two welded mock-ups with machined defects, surface condition and geometry representative of the ''envelope'' of situations likely to be found on the SG; one mock-up, with representative corrosion cracks Development was carried out in two phases: development of techniques and specification of probes and tooling, then development of tools, industrialization of probes, development of procedures, personnel training and performance demonstration. The basic inspection relied on TOFDT, with a contact probe; frequencies, PCS and dimensions were optimised using the results from the mock-ups. Three sets of transducers were defined: a HF transducer for flaw sizes close to the critical size, another HF transducer, with lower PCS for smaller defects, both transducers for material whose permeability was equivalent to that of the mock-ups; anticipating less permeable materials, a MF probe was added. Tests having shown that these transducers did not cover the whole plate thickness, a back-up phased-array probe was selected to scan the plate beyond halfthickness. For a better access under the TSP, a focused transducer was also added to complete the previous set. All of these transducers were operated in immersion, with the same tool: a COBRA type arm which positioned the probes

  16. Corrosion of Mechanically Alloyed Nanostructured FeAl Intermetallic Powders

    Directory of Open Access Journals (Sweden)

    A. Torres-Islas

    2012-01-01

    Full Text Available The corrosion behavior of the Fe40Al60 nanostructured intermetallic composition was studied using electrochemical impedance spectroscopy (EIS and linear polarization resistance (LPR techniques with an innovative electrochemical cell arrangement. The Fe40Al60 (% at intermetallic composition was obtained by mechanical alloying using elemental powders of Fe (99.99% and Al (99.99%. All electrochemical testing was carried out in Fe40Al60 particles that were in water with different pH values. Temperature and test time were also varied. The experimental data was analyzed as an indicator of the monitoring of the particle corrosion current density icorr. Different oxide types that were formed at surface particle were found. These oxides promote two types of surface corrosion mechanisms: (i diffusion and (ii charge transfer mechanisms, which are a function of icorr behavior of the solution, pH, temperature, and test time. The intermetallic was characterized before and after each test by transmission electron microscopy. Furthermore, the results show that at the surface particles uniform corrosion takes place. These results confirm that it is possible to sense the nanoparticle corrosion behavior by EIS and LPR conventional electrochemical techniques.

  17. Time-dependent corrosion fatique crack propagation in 7000 series aluminum alloys. M.S. Thesis

    Science.gov (United States)

    Mason, Mark E.

    1995-01-01

    The goal of this research is to characterize environmentally assisted subcritical crack growth for the susceptible short-longitudinal orientation of aluminum alloy 7075-T651, immersed in acidified and inhibited NaCl solution. This work is necessary in order to provide a basis for incorporating environmental effects into fatigue crack propagation life prediction codes such as NASA-FLAGRO (NASGRO). This effort concentrates on determining relevant inputs to a superposition model in order to more accurately model environmental fatigue crack propagation.

  18. An elucidation of the corrosion mechanism using metallographic and fractographic methods on rolled AlZnMgCu1.5 sheets; Abklaerung des Korrosionsmechanismus mittels metallographischer und fraktographischer Methoden an gewalzten AlZnMgCu1.5 Blechen

    Energy Technology Data Exchange (ETDEWEB)

    Winkler, R.; Faller, M.; Zgraggen, M. [EMPA - Eidgenoessische Materialpruefungs und Forschungsanstalt, Abt. Kurrosion und Werkstoffintegritaet, Duebendorf (Switzerland)

    2006-07-15

    Various corrosion mechanisms can result in the failure of components in high-strength aluminium alloys, depending on the states of the materials and/or environmental conditions. Those are layer corrosion, intergranular corrosion cracking, and stress corrosion cracking. For a prevention of future failure, it is necessary to elucidate the corrosion type in damaged components. Therefore, all results obtained from various examination methods require to be gathered in many cases to allow for an interpretation. The present case reports about a damage caused by corrosion to a rolled sheet made of the Al alloy 7075 (T6 condition). The suspicion that the delamination of the metal sheets was due to layer corrosion was not confirmed by metallographic examinations. The corrosive attack occurred along the grain boundaries. Likewise, intergranular corrosion cracking was successfully excluded by microfractographic examinations on the tip of the crack in a scanning electron microscope. It was only by combining the metallographic and fractographic examination methods that stress corrosion cracking was clearly proved to be the damage mechanism. (orig.)

  19. A Study on the Residual Stress Improvement of PWSCC(Primary Water Stress Corrosion Cracking) in DMW(Dissimilar Metal Weld)

    Energy Technology Data Exchange (ETDEWEB)

    Kang, Sung Sik; Kim, Seok Hun; Lee, Seung Gun [Korea Institute of Nuclear Safety, Daejeon (Korea, Republic of); Park, Heung Bae [KEPCO Engineering and Construction Company, Daejeon (Korea, Republic of)

    2010-10-15

    Since 2000s, most of the cracks are found in welds, especially in (DMW) dissimilar metal welds such as pressurizer safety relief nozzle, reactor head penetration, reactor bottom mounted instrumentation (BMI), and reactor nozzles. Even the cracks are revealed as a primary water stress corrosion cracking (PWSCC), it is difficult to find the cracks by current non destructive examination. The PWSCC is occurred by three incident factors, such as susceptible material, environmental corrosive condition, and welding residual stress. If one of the three factors can be erased or decreased, the PWSCC could be prevented. In this study, we performed residual stress analysis for DMW and several residual stress improvement methods. As the preventive methods of PWSCC, we used laser peening(IP) method, inlay weld(IW) method, and induction heating stress improvement(IHSI) method. The effect of residual stress improvement for preventive methods was compared and discussed by finite element modeling and residual stress of repaired DMW

  20. Corrosion and Nano-mechanical Behaviors of Magnetron Sputtered Al-Mo Gradient Coated Steel

    Science.gov (United States)

    Venugopal, A.; Srinath, J.; Ramesh Narayanan, P.; Sharma, S. C.; Venkitakrishnan, P. V.

    2016-11-01

    A gradient three-layer Al-Mo coating was deposited on steel using magnetron sputtering method. The corrosion and nano-mechanical properties of the coating were examined by electrochemical impedance spectroscopy and nano-indentation tests and compared with the conventional electroplated cadmium and IVD aluminum coatings. Electrochemical impedance spectroscopy was performed by immersing the coated specimens in 3.5% NaCl solution, and the impedance behavior was recorded as a function of immersion time. The mechanical properties (hardness and elastic modulus) were obtained from each indentation as a function of the penetration depth across the coating cross section. The adhesion resistance of the coatings was evaluated by scratch tests on the coated surface using nano-indentation method. The results show that the gradient Al-Mo coating exhibits better corrosion resistance than the other coatings in view of the better microstructure. The impedance results were modeled using appropriate electrical equivalent circuits for all the coated systems. The uniform, smooth and dense Al-Mo coating obtained by magnetron sputtering exhibits good adhesion with the steel substrate as per scratch test method. The poor corrosion resistance of the later coatings was shown to be due to the defects/cracks as well as the lesser adhesion of the coatings with steel. The hardness and elastic modulus of the Al-Mo coating are found to be high when compared to the other coatings.

  1. Pure mechanical wear loss measurement in corrosive wear

    Indian Academy of Sciences (India)

    Yanliang Huang; Xiaoxia Jiang; Sizuo Li

    2000-12-01

    The method for the measurement of the pure mechanical wear loss for 321 stainless steel, 1045 steel and pure iron in the study of the synergy between corrosion and wear was studied. The methods studied included the measurement in distilled water, by cathodic protection and by adding inhibitor KI, and all were compared with the wear loss in air. The experiment showed that the pure mechanical wear losses and friction coefficients obtained by the three methods were close to each other and can be used to calculate the various wear components in the study of the interaction of corrosion and wear, but the measurements in distilled water for pure iron and 1045 steel are not recommended due to their corrosion.

  2. Hydrogen diffusion into fatigue cracks of aluminium alloy 6013 in a corrosive environment; Wasserstoffeinlagerung an Ermuedungsrissen der Aluminiumlegierung 6013 unter korrosiver Umgebung

    Energy Technology Data Exchange (ETDEWEB)

    Lenk, Christian Alexander

    2009-08-13

    The author attempted a time-resolved detection of raised hydrogen concentrations in the plastic deformation region of fatigue cracks in an aluminium test piece deformed by cyclic stress in a corrosive environment. Mechanical material parameters like the crack propagation velocity under cyclic stress change dramatically in a corrosive environment. This is assumed to be caused by hydrogen diffusion, but so far there is no method that reliably measures additional hydrogen from the corrosive environment. For this reason, a special analytical configuration was set up which makes use of the thermal desorption method. First, chips with a thickness of about 20 micrometers are sawed out of the test specimen in high-vacuum conditions. The chips fall into a hot melting vessel in a UHV chamber, where the hydrogen contained in the chips is released. The resulting pressure increase is recorded by a mass spectrometer. A hydrogen profile of the test specimen is obtained by assigning the chip position to the signal. For the corrosive medium in which the test specimen is immersed during crack initiation, i.e. NaCl solution, heavy water was used. This makes it possible to distinguish between the hydrogen contained in a piece of technical aluminium alloy (AA6013) and the deuterium diffusing in from the corrosive fluid. The deuterium is found exclusively in the test piece volume in the strongly plastically deformed region surrounding the fatigue crack. (orig.) [German] Das Ziel der vorliegenden Arbeit besteht im ortsaufgeloesten Nachweis einer erhoehten Wasserstoffkonzentration im plastisch deformierten Bereich von Ermuedungsrissen einer unter korrosiver Umgebung zyklisch verformten Aluminiumprobe. Mechanische Materialparameter wie z.B. die Rissausbreitungsgeschwindigkeit unter zyklischer Belastung aendern sich drastisch in korrosiver Umgebung. Als Ursache fuer dieses Verhalten wird eine Eindiffusion von Wasserstoff vermutet, jedoch gibt es bisher keine Messung die den zusaetzlichen

  3. Mechanical Properties and Corrosion Behavior of Low Carbon Steel Weldments

    Directory of Open Access Journals (Sweden)

    Mohamed Mahdy

    2013-01-01

    Full Text Available This research involves studying the mechanical properties and corrosion behavior of “low carbon steel” (0.077wt% C before and after welding using Arc, MIG and TIG welding. The mechanical properties include testing of microhardness, tensile strength, the results indicate that microhardness of TIG, MIG welding is more than arc welding, while tensile strength in arc welding more than TIG and MIG.The corrosion behavior of low carbon weldments was performed by potentiostat at scan rate 3mV.sec-1 in 3.5% NaCl to show the polarization resistance and calculate the corrosion rate from data of linear polarization by “Tafel extrapolation method”. The results indicate that the TIG welding increase the corrosion current density and anodic Tafel slop, while decrease the polarization resistance compared with unwelded low carbon steel. Cyclic polarization were measured to show resistance of specimens to pitting corrosion and to calculate the forward and reveres potentials. The results show shifting the forward, reverse and pitting potentials toward active direction for weldments samples compared with unwelded sample.

  4. Friction Stir Welding of Al Alloy 2219-T8: Part II-Mechanical and Corrosion

    Science.gov (United States)

    Kang, Ju; Feng, Zhi-Cao; Li, Ji-Chao; Frankel, G. S.; Wang, Guo-Qing; Wu, Ai-Ping

    2016-09-01

    In Part I of this series, abnormal agglomerations of θ particles with size of about 100 to 1000 µm were observed in friction stir welded AA2219-T8 joints. In this work, the effects of these agglomerated θ particles on the mechanical and corrosion properties of the joints are studied. Tensile testing with in situ SEM imaging was utilized to monitor crack initiation and propagation in base metal and weld nugget zone (WNZ) samples. These tests showed that cracks initiated in the θ particles and at the θ/matrix interfaces, but not in the matrix. The WNZ samples containing abnormal agglomerated θ particles had a similar ultimate tensile stress but 3 pct less elongation than other WNZ samples with only normal θ particles. Measurements using the microcell technique indicated that the agglomerated θ particles acted as a cathode causing the dissolution of adjacent matrix. The abnormal θ particle agglomerations led to more severe localized attack due to the large cathode/anode ratio. Al preferential dissolution occurred in the abnormal θ particle agglomerations, which was different from the corrosion behavior of normal size θ particles.

  5. The effect of carbon content on mechanical properties, failure and corrosion resistance of deposited chromium metal

    Directory of Open Access Journals (Sweden)

    Леонід Кімович Лещинськiй

    2017-06-01

    Full Text Available It has been shown that if choosing a metal composition for surfacing rolls and rollers of continuous casting machines, both the carbon impact on the mechanical and functional properties and the critical values of the chromium concentration, which determine the corrosion resistance of the metal with regard to electrochemical corrosion theory, should be considered as well. The paper studied the effect of chromium and carbon steel the X5-X12 type on the structure, technological strength, mechanical properties, fracturing resistance and corrosion resistance of the weld metal. The composition of chromium tool steels (deposited metal (X5-used for the rolls of hot rolling mills and (X12-used for continuous casting machines rollers correspond to these values. The impact of carbon on the properties of the deposited metal containing chromium was considered by comparing the data for both types of the deposited metal. It was found that for both types of the deposited metal (X5 and X12, the limiting value of the carbon content, providing an optimal combination of strength, ductility, failure resistance is the same. If the carbon content is more than the limiting value – (0,25% the technological strength and failure resistance of the deposited metal significantly reduce. With increasing carbon content from 0,18 to 0,25% the martensite structure has a mixed morphology – lath and plate. The strength and toughness of the deposited metal grow. Of particular interest is simultaneous increase in the specific work of failure resulted from crack inhibition at the boundary with far less solid and more ductile ferrite. As for the 5% chromium metal, the X12 type composition with 0,25% C, is borderline. With a further increase in the carbon content of the metal both ductility and failure resistance sharply decrease and with 0,40% C the growth rate of fatigue crack increases by almost 1,5 times

  6. Effects of crack depth and specimen size on ductile crack growth of SENT and SENB specimens for fracture mechanics evaluation of pipeline steels

    Energy Technology Data Exchange (ETDEWEB)

    Xu, J. [Department of Structural Engineering, Norwegian University of Science and Technology (NTNU), Richard Birkelands vei 1a, N-7491 Trondheim (Norway); School of Materials Science and Engineering, University of Science and Technology Beijing (USTB), 100083 Beijing (China); Zhang, Z.L., E-mail: zhiliang.zhang@ntnu.n [Department of Structural Engineering, Norwegian University of Science and Technology (NTNU), Richard Birkelands vei 1a, N-7491 Trondheim (Norway); Ostby, E.; Nyhus, B. [SINTEF, Materials and Chemistry, N-7465 Trondheim (Norway); Sun, D.B. [School of Materials Science and Engineering, University of Science and Technology Beijing (USTB), 100083 Beijing (China)

    2009-12-15

    A strong geometry dependence of ductile crack growth resistance emerges under large scale yielding. The geometry dependence is associated with different levels of crack tip constraint conditions. However, in a recent attempt to identify appropriate fracture mechanics specimens for pipeline steels, an 'independent' relationship between the crack growth resistance curves and crack depths for SENT specimens has been observed experimentally. In this paper, we use the complete Gurson model to study the effects of crack depth and specimen size on ductile crack growth behavior. Crack growth resistance curves for plane strain, mode I crack growth under large scale yielding conditions have been computed. SENB and SENT specimens with three different specimen sizes, each specimen size with three different crack depths, have been selected. It has been found that crack tip constraint (Q-parameter) has a weak dependence on the crack depth for specimens in the low constraint regime.

  7. Mechanical behavior and failure mechanism of pre-cracked specimen under uniaxial compression

    Science.gov (United States)

    Liu, Ting; Lin, Baiquan; Yang, Wei

    2017-08-01

    As a desirable permeability enhancement method, hydraulic slotting has been widely used for enhanced coal bed methane (ECBM) recovery in China. Aiming at the problem that the action mechanism of the slot on the mechanical properties of the slotted coal is still unclear, this paper investigates the effects of flaw inclination on the strength, deformation and cracking process of the pre-cracked specimens. The result shows that the stress-strain curves can be divided into three categories based on the stress behaviors, dropping step by step or dropping sharply, after the peak. With an increase of the flaw inclination, the strength and elastic modulus of the pre-cracked specimen increases gradually, which is verified by the numerical simulation and theoretical results. Analysis of the cracking processes indicates that the initiation position of the first crack in specimens with various flaw inclinations is different, which is caused by the various distributions of tensile and compressive stress concentration zones. The distribution of the stress field controls the cracking process which will in turn affect the stress field distribution. With the propagation of the cracks, the tensile stress concentration zones expand and the concentration degree lowers gradually, while the compressive stress concentration zones show the opposite variation trend. Based on the above results, an optimized slot arrangement method has been proposed for the field application of hydraulic slotting.

  8. DEVELOPMENT OF AN EMAT IN-LINE INSPECTION SYSTEM FOR DETECTION, DISCRIMINATION, AND GRADING OF STRESS CORROSION CRACKING IN PIPELINES

    Energy Technology Data Exchange (ETDEWEB)

    Jeff Aron; Jon Gore, Roger Dalton; Stuart Eaton; Adrian Bowles; Owen Thomas; Tim Jarman

    2003-07-01

    This report describes progress, experiments, and results for a project to develop a pipeline inline inspection tool that uses electromagnetic acoustic transducers (EMATs) to detect and grade stress corrosion cracking (SCC). There is a brief introduction that gives background material about EMATs and relevant previous Tuboscope work toward a tool. This work left various choices about the modes and transducers for this project. The experimental section then describes the lab systems, improvements to these systems, and setups and techniques to narrow the choices. Improvements, which involved transducer matching networks, better magnetic biasing, and lower noise electronics, led to improved signal to noise (SNR) levels. The setups permitted transducer characterizations and interaction measurements in plates with man-made cracks, pipeline sections with SCC, and a full pipe with SCC. The latter were done with a moveable and compact EMAT setup, called a lab mouse, which is detailed. Next, the results section justifies the mode and transducer choices. These were for magnetostrictive EMATs and the use of EMAT launched modes: SH0 (at 2.1 MHz-mm) and SV1 (at 3.9 MHz-mm). This section then gives details of measurements on these modes. The measurements consisted of signal to noise ratio, insertion loss, magnetic biasing sensitivities crack reflection and transmission coefficients, beam width, standoff and tilt sensitivities. For most of the measurements the section presents analysis curves, such as reflection coefficient versus crack depth. Some notable results for the chosen modes are: that acceptable SNRs were generated in a pipe with magnetostrictive EMATs, that optimum bias for magnetostrictive transmitters and receivers is magnetic saturation, that crack reflection and transmission coefficients from crack interactions agree with 2 D simulations and seem workable for crack grading, and that the mouse has good waveform quality and so is ready for exhaustive measurement EMAT

  9. Crack growth threshold under hold time conditions in DA Inconel 718 – A transition in the crack growth mechanism

    Directory of Open Access Journals (Sweden)

    E. Fessler

    2016-01-01

    Full Text Available Aeroengine manufacturers have to demonstrate that critical components such as turbine disks, made of DA Inconel 718, meet the certification requirements in term of fatigue crack growth. In order to be more representative of the in service loading conditions, crack growth under hold time conditions is studied. Modelling crack growth under these conditions is challenging due to the combined effect of fatigue, creep and environment. Under these conditions, established models are often conservative but the degree of conservatism can be reduced by introducing the crack growth threshold in models. Here, the emphasis is laid on the characterization of crack growth rates in the low ΔK regime under hold time conditions and in particular, on the involved crack growth mechanism. Crack growth tests were carried out at high temperature (550 °C to 650 °C under hold time conditions (up to 1200 s in the low ΔK regime using a K-decreasing procedure. Scanning electron microscopy was used to identify the fracture mode involved in the low ΔK regime. EBSD analyses and BSE imaging were also carried out along the crack path for a more accurate identification of the fracture mode. A transition from intergranular to transgranular fracture was evidenced in the low ΔK regime and slip bands have also been observed at the tip of an arrested crack at low ΔK. Transgranular fracture and slip bands are usually observed under pure fatigue loading conditions. At low ΔK, hold time cycles are believed to act as equivalent pure fatigue cycles. This change in the crack growth mechanism under hold time conditions at low ΔK is discussed regarding results related to intergranular crack tip oxidation and its effect on the crack growth behaviour of Inconel 718 alloy. A concept based on an “effective oxygen partial pressure” at the crack tip is proposed to explain the transition from transgranular to intergranular fracture in the low ΔK regime.

  10. An Evaluation of the Corrosion and Mechanical Performance of Interstitially Surface-Hardened Stainless Steel

    Science.gov (United States)

    Jones, Jennifer L.; Koul, Michelle G.; Schubbe, Joel J.

    2014-06-01

    A surface hardening technique called "interstitial hardening" is commercially available, whereby interstitial carbon atoms are introduced into stainless steel surfaces without the formation of carbides. Surface hardening of machine elements such as impellors or fasteners would improve performance regarding cavitation and galling resistance, and has intensified interest in this process. However, there remains a need to characterize and validate the specific performance characteristics of the hardened materials. This paper describes experimental testing conducted on 316L stainless steel that has been surface hardened using available commercial techniques, using carbon as the interstitial atom. The corrosion performance of the hardened surface is assessed using electrochemical potentiodynamic testing to determine the breakdown potential in 3.5 wt.% NaCl solution to identify the most promising method. The hardness and thickness of the surface-hardened layer is characterized and compared using metallography and microhardness profiling. Corrosion fatigue and slow strain rate testing of untreated, hardened, and damaged, hardened surfaces exposed to ASTM seawater is conducted. Finally, critical galling stresses are determined and compared. Post-test examination of damage attempts to identify mechanisms of material failure and characterize how corrosion-assisted cracks initiate and grow in surface-hardened materials.

  11. A novel technique for measuring stress-corrosion crack-growth rates in single-crystal experiments

    Energy Technology Data Exchange (ETDEWEB)

    Lichter, B.D. [Vanderbilt Univ., Nashville, TN (United States)]|[Delft Univ. of Technology (Netherlands); Flanagan, W.F. [Vanderbilt Univ., Nashville, TN (United States)

    1994-12-31

    Crack-growth occurs discontinuously in oriented copper-gold single-crystals during slow-strain rate experiments performed under anodic polarization in aqueous NaCl solutions. Crack advance between major crack arrests is accompanied by load-drops and current-transients which can be quantitatively related to the length of the advance as well as yielding the average instantaneous rate of advance. Two independent but self-consistent methods are used: (1) mechanical analysis of the load-drops, taking into account the elastic displacement of the load-train and of the specimen, due to both the load and the crack advance, and (2) analysis of the current-transients in which it is argued that the current is proportional to the rate of new surface production. Results show that the crack velocity is on the order of 50--400{mu}/s, depending on the environment and potential, too slow to be explained by a running brittle crack, and too fast to be explained by Faradaic dissolution.

  12. Fatigue Crack Extension Model of Aluminium Alloy with Prior Corrosion Damage Based on Localised Corrosion Damage%基于局部腐蚀损伤的铝合金预腐蚀疲劳裂纹扩展模型

    Institute of Scientific and Technical Information of China (English)

    孔光明; 李旭东; 穆志韬

    2014-01-01

    目的:建立铝合金预腐蚀疲劳裂纹扩展模型。方法采用表征局部环境腐蚀损伤影响程度的参数孔蚀率对腐蚀疲劳裂纹扩展速率进行修正。结果修正后的腐蚀铝合金试件的疲劳裂纹扩展速率与试验结果吻合程度良好。结论修正后的铝合金预腐蚀疲劳裂纹扩展速率模型合理有效,试验数据和预测模型可为海军飞机结构的损伤容限设计提供参考。%Objective To establish a modified model for pre-corrosion fatigue crack growth rate of aluminum alloy. Methods Considering that the local damage around the crack tip was more reasonable for accelerating crack growth rate in corrosive environment, the pitting rate, which was a parameter characterizing the influence of corrosion in local environ-ment, was used to correct the corrosion fatigue crack growth rate. Results The experimental results were in good agreement with predictions of the amended fatigue crack growth rate model for corroded aluminum alloy specimens. Conclusion The corrected aluminum alloy pre-corrosion fatigue crack growth rate model was reasonable and effective, and the test data and the prediction model could provide a reference for the damage tolerance design of navy aircraft structure.

  13. Stress Corrosion Cracking of X80 Pipeline Steel in Near-Neutral pH Environment under Constant Load Tests with and without Preload

    Institute of Scientific and Technical Information of China (English)

    Y.Z. Jia; J.Q. Wang; E.H. Han; W. Ke1

    2011-01-01

    Constant load tests in NS4 solution purged with N2-5%CO2 gas mixture were conducted on American Petroleum Institute (API) X80 pipeline steel applied in the 2nd West-East (;as Pipeline project with and without preload. The results show that cracks could initiate and propagate in X80 pipeline steel in near-neutral pH environment under a constant load condition. The life of crack initiation and propagation increased with decreasing applied stress. Preload did not change its corrosion behavior obviously. However, preload reduced the time for crack initiation.

  14. Multifunctional Integrated Optic Sensor for Detection of Cracks and Corrosion Project

    Data.gov (United States)

    National Aeronautics and Space Administration — Los Gatos Research proposes to develop a new nondestructive inspection sensor system, capable of simultaneously measuring strain-based load and detecting crack,...

  15. Numerical analysis of confinement effect on crack propagation mechanism from a flaw in a pre-cracked rock under compression

    Institute of Scientific and Technical Information of China (English)

    Amin Manouchehrian; Mohammad Fatehi Marji

    2012-01-01

    In many situations rocks are subjected to biaxial loading and the failure process is controlled by the lateral confinement stresses.The importance of confinement stresses has been recognized in the literature by many researchers,in particular,its influence on strength and on the angle of fracture,but still there is not a clear description for the influence of confining stress on the crack propagation mechanism of rocks.This paper presents a numerical procedure for the analysis of crack propagation in rock-like materials under compressive biaxial loads.Several numerical simulations of biaxial tests on the rock specimen have been carried out by a bonded particle model (BPM) and the influence of confinement on the mechanism of crack propagation from a single flaw in rock specimens is studied.For this purpose,several biaxial compressive tests on rectangular specimens under different confinement stresses were modeled in (2 dimensional particle flow code) PFC2D.The results show that wing cracks initiate perpendicular to the flaw and trend toward the direction of major stress,however,when the lateral stresses increase,this initiation angle gets wider.Also it is concluded that in addition to the material type,the initiation direction of the secondary cracks depends on confinement stresses,too.Besides,it is understood that secondary cracks may be produced from both tensile and shear mechanisms.

  16. Fracture mechanics by three-dimensional crack-tip synchrotron X-ray microscopy.

    Science.gov (United States)

    Withers, P J

    2015-03-06

    To better understand the relationship between the nucleation and growth of defects and the local stresses and phase changes that cause them, we need both imaging and stress mapping. Here, we explore how this can be achieved by bringing together synchrotron X-ray diffraction and tomographic imaging. Conventionally, these are undertaken on separate synchrotron beamlines; however, instruments capable of both imaging and diffraction are beginning to emerge, such as ID15 at the European Synchrotron Radiation Facility and JEEP at the Diamond Light Source. This review explores the concept of three-dimensional crack-tip X-ray microscopy, bringing them together to probe the crack-tip behaviour under realistic environmental and loading conditions and to extract quantitative fracture mechanics information about the local crack-tip environment. X-ray diffraction provides information about the crack-tip stress field, phase transformations, plastic zone and crack-face tractions and forces. Time-lapse CT, besides providing information about the three-dimensional nature of the crack and its local growth rate, can also provide information as to the activation of extrinsic toughening mechanisms such as crack deflection, crack-tip zone shielding, crack bridging and crack closure. It is shown how crack-tip microscopy allows a quantitative measure of the crack-tip driving force via the stress intensity factor or the crack-tip opening displacement. Finally, further opportunities for synchrotron X-ray microscopy are explored.

  17. Use of electrochemical potential noise to detect initiation and propagation of stress corrosion cracks in a 17-4 PH steel

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez-Rodriguez, J.G. [UAEM, Cuernavaca (Mexico); Salinas-Bravo, V.M.; Garcia-Ochoa, E. [Inst. de Investigaciones Electricas, Temixco (Mexico). Dept. de Fisicoquimica Aplicada; Diaz-Sanchez, A. [Inst. Nacional de Investigaciones Nucleares, Toluca (Mexico). Dept. de Materiales

    1997-09-01

    Corrosion potential transients were associated with nucleation and propagation of stress corrosion cracks in a 17-4 precipitation-hardenable (PH) martensitic stainless steel (SS) during slow strain rate tests (SSRT) at 90 C in deaerated sodium chloride (NaCl) solutions, Test solutions included 20 wt% NaCl at pH 3 and 7, similar to normal and faulted steam turbine environments, respectively. Time series were analyzed using the fast Fourier transform method. At the beginning of straining, the consistent noise behavior was perturbed with small potential transients, probably associated with rupture of the surface oxide layer. After yielding, these transients increased in intensity. At maximum load, the transients were still higher in intensity and frequency. These potential transients were related to crack nucleation and propagation. When the steel did not fail by stress corrosion cracking (SCC), such transients were found only at the beginning of the test. The power spectra showed some differences in all cases in roll-off slope and voltage magnitude, but these were not reliable tools to monitor the initiation and propagation of stress corrosion cracks.

  18. Fracture Resistance Measurement Method for in situ Observation of Crack Mechanisms

    DEFF Research Database (Denmark)

    Sørensen, Bent F.; Horsewell, A.; Jørgensen, O.

    1998-01-01

    observation and acoustic emission, As an example, crack growth in a cubic-phase yttria-stabilized zirconia is detected easily by in situ observation of the crack-tip region, Many fracture toughness measurements are obtained for each specimen, giving high confidence in the measured fracture toughness value......, In situ observation is useful for the study of toughening mechanisms and subcritical crack-growth behavior and to sort out erroneous measurements (e.g., due to crack branching)....

  19. Variable amplitude corrosion fatigue and fracture mechanics of weldable high strength jack-up steels

    Science.gov (United States)

    Etube, Linus Sone

    The tubular welded joints used in the construction of Offshore structures can experience millions of variable amplitude wave induced stress cycles during their operational life. Fatigue has been identified as the main cause of degradation of structural integrity in these structures. As a result, fatigue is an important consideration in their design. Jack-up legs are made from a range of high strength steels with yield strengths up to TOOMPa. These steels are thought to exhibit fatigue resistance properties which are different when compared with conventional fixed platform steels such as BS 4360 50D and BS 7191 355D. The difference in their behaviour was heightened by the discovery, in the late 80s and early 90s, of extensive cracking around the spud can regions of several Jack-ups operating in the North Sea. It was thought that these steels may be more susceptible to hydrogen cracking and embrittlement. There was the additional requirement to study their behaviour under realistic loading conditions typical of the North Sea environment. This thesis contains results of an investigation undertaken to assess the performance of a typical high strength weldable Jack-up steel under realistic loading and environmental conditions. Details of the methodology employed to develop a typical Jack-up Offshore Standard load History (JOSH) are presented. The factors which influence fatigue resistance of structural steels used in the construction of Jack-up structures are highlighted. The methods used to model the relevant factors for inclusion in JOSH are presented with particular emphasis on loading and structural response interaction. Results and details of experimental variable amplitude corrosion fatigue (VACF) tests conducted using JOSH are reported and discussed with respect to crack growth mechanisms in high strength weldable Jack-up steels. Different fracture mechanics models for VACF crack growth prediction are compared and an improved generalised methodology for fast

  20. Chemical and mechanical control of corrosion product transport

    Energy Technology Data Exchange (ETDEWEB)

    Hede Larsen, O.; Blum, R. [I/S Fynsvaerket, Faelleskemikerne, Odense (Denmark); Daucik, K. [I/S Skaerbaekvaerket, Faelleskemikerne, Fredericia (Denmark)

    1996-12-01

    The corrosion products formed in the condensate and feedwater system of once-through boilers are precipitated and deposited inside the evaporator tubes mainly in the burner zone at the highest heat flux. Depositions lead to increased oxidation rate and increased metal temperature of the evaporator tubes, hereby decreasing tube lifetime. This effect is more important in the new high efficiency USC boilers due to increased feedwater temperature and hence higher thermal load on the evaporator tubes. The only way to reduce the load on the evaporator tubes is to minimise corrosion product transport to the boiler. Two general methods for minimising corrosion product transport to the boiler have been evaluated through measurement campaigns for Fe in the water/steam cycle in supercritical boilers within the ELSAM area. One method is to reduce corrosion in the low temperature condensate system by changing conditioning mode from alkaline volatile treatment (AVT) to oxygenated treatment (OT). The other method is to filtrate part of the condensate with a mechanical filter at the deaerator. The results show, that both methods are effective at minimising Fe-transport to the boiler, but changing to OT has the highest effect and should always be used, whenever high purity condensate is maintained. Whether mechanical filtration also is required, depends on the boiler, specifically the load on the evaporator. A simplified calculation model for lifetime evaluation of evaporator tubes has been developed. This model has been used for evaluating the effect of corrosion product transport to the boiler on evaporator tube lifetime. Conventional supercritical boilers generally can achieve sufficient lifetime by AVT and even better by OT, whereas all measures to reduce Fe-content of feedwater, including OT and mechanical filtration, should be taken, to ensure sufficient lifetime for the new boilers with advanced steam data - 290 bar/580 deg. C and above. (au)

  1. An Investigation of the Mechanism of IGA/SCC of Alloy 600 in Corrosion Accelerating Heated Crevice Environments. Technical Progress Report

    Energy Technology Data Exchange (ETDEWEB)

    Lumsden, Jesse

    1999-01-01

    OAK-B135 An Investigation of the Mechanism of IGA/SCC of Alloy 600 in Corrosion Accelerating Heated Crevice Environments. Technical Progress Report. This program focuses on understanding the mechanisms causing corrosion damage to steam generator tubes in a pressurized water reactor (PWR) and the effects of the proposed remedial measures. The crevice formed by the tube/tube support plate (T/TSP) intersection in a PWR steam generator is a concentration site for nonvolatile impurities (referred to as hideout) in the steam generator water. The restricted mass transport in the small crevice volume prevents the species, which concentrate during the generation of steam, from quickly dispersing into the bulk water. The concentrated solutions in crevices have been a contributing cause of several forms of corrosion of steam generator tubes including intergranular attack/stress corrosion cracking (IGA/SCC), pitting, and wastage.

  2. Monitoring of solidification crack propagation mechanism in pulsed laser welding of 6082 aluminum

    Science.gov (United States)

    von Witzendorff, P.; Kaierle, S.; Suttmann, O.; Overmeyer, L.

    2016-03-01

    Pulsed laser sources with pulse durations in the millisecond regime can be used for spot welding and seam welding of aluminum. Seam welds are generally produced with several overlapping spot welds. Hot cracking has its origin in the solidification process of individual spot welds which determines the cracking morphology along the seam welding. This study used a monitoring unit to capture the crack geometry within individual spot welds during seam welding to investigate the conditions for initiation, propagation and healing (re-melting) of solidification cracking within overlapping pulsed laser welds. The results suggest that small crack radii and high crack angles with respect to welding direction are favorable conditions for crack healing which leads to crack-free seam welds. Optimized pulse shapes were used to produce butt welds of 0.5 mm thick 6082 aluminum alloys. Tensile tests were performed to investigate the mechanical strength in the as-welded condition.

  3. APPLICABILITY OF THE CRACK FACE ELECTRICAL BOUNDARY CONDITIONS IN PIEZOELECTRIC MECHANICS

    Institute of Scientific and Technical Information of China (English)

    WangBaolin; HanJiecai; DuShanyi

    2004-01-01

    The electrical boundary conditions on the crack faces and their applicability in piezoelectric materials are discussed. A slit crack and a notch of finite thickness in piezoelectric materials subjected to combined mechanical and electrical loads is considered. Here, a crack is defined as a notch without thickness, which is filled with air or vacuum. The crack or notch is perpendicular to the poling direction of the medium. The ideal crack face electrical boundary conditions, i.e., the electrically permeable crack and the electrically impermeable crack, are investigated first. Then dependence of the field intensity factors on notch thickness at the notch tips is analyzed to obtain a closed-form. The results are compared with the ideal crack solutions.Some useful results are found.

  4. Effects of cold work on stress corrosion cracking of type 316L stainless steel in hot lithium hydroxide solution

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, J.H.; Bogaerts, W.F. (Univ. of Leuven (Belgium). Dept. of Metallurgy and Materials Engineering)

    1993-07-01

    Lithium hydroxide (LiOH) has ben chose as the lithium compound to be used in the Aqueous Lithium Salt Blanket (ALSB) concept that has been proposed as a possible driver blanket for the Next European Torus (NET), the next generation of fusion testing devices in Europe, as well as for the International Thermonuclear Experimental Reactor program (ITER). The stress corrosion cracking (SCC) behavior of cold-worked AISI type 316L stainless steel (SS) in a concentrated lithium salt solution at elevated temperature was investigated. Using the slow strain rate technique, SCC experiments were carried out on 20% and 40% cold-worked materials in a solution of 10g lithium hydroxide and 100 cm[sup 3]H[sub 2]O at 95C under conditions with controlled electrochemical potential. Observation of the fracture surfaces by scanning electron microscope indicated the SCC behavior of the cold-worked steel was essentially different from that of the solution-annealed steel. A ductile fracture of cold-worked samples occurred under open-circuit conditions ([approximately][minus]280 mV) and at 200 mV. Slight intergranular attack was found in the region near the surface of cold-worked specimens when the electrochemical potential was controlled at [minus]120 mV. SCC was observed when the experiments were conducted at +100mV. Intergranular stress corrosion cracking (IGSCC) of solution-annealed material changed into a mixed SCC mode, or a dominant transgranular SCC (TGSCC) with an increase of cold work to 20% and 40%. Compared to the SCC behavior of the solution-annealed 316L, the results showed cold work improved significantly the resistance of 316L SS to IGSCC in the hot LiOH environment. Susceptibility to TGSCC of cold-worked 316L SS increased with increasing extent of cold working. These effects were reviewed with respect to electrochemical and microstructural phenomena.

  5. Anti-corrosion mechanism of epoxy-resin and different content Fe2O3 coatings on magnesium alloy

    Science.gov (United States)

    Jin, Tao; Kong, Fan-mei; Bai, Rui-qin; Zhang, Ru-liang

    2016-10-01

    In this study, anti-corrosion coatings were prepared and coated successfully on magnesium alloy substrates by mixing nanopowders, solvent, curing agent with epoxy resin. The effect of the amount of iron trioxide (Fe2O3) on the adhesion strength and corrosion resistance on magnesium alloy was investigated with standard protocols, and electrochemical measurements were also made in 3.5 wt.% NaCl solutions. The surface morphology and corrosion mechanism after corrosion tests was characterized using FESEM analysis. Nanoparticles in matrix acted as filler, and interstitial cross-linked spaces and other coating artifacts regions (micro cracks and voids) would all affect the anti-corrosion properties of coating. The results showed the proper powder content not only provided adhesion strength to these coatings but also improved obviously their anticorrosion. Hydrogen bound to the amine nitrogen (1N) could take part in the curing process rather than hydrogen of the amide site due to the smaller ΔG and the more stable configuration.

  6. The Effect of Sensitization on the Stress Corrosion Cracking of Aluminum Alloy 5456

    Science.gov (United States)

    2012-06-01

    electrochemically active particles. (From Jones, [26]) ....................................23 Figure 16. Illustration of corrosion tunnel model. (a) Schematic of...46 Table 6. Grinding and Polishing Conditions...approaches continuity along grain boundaries. The β phase is more anodic than the surrounding material matrix and therefore is electrochemically more

  7. Review of studies on corrosion of magnesium alloys

    Institute of Scientific and Technical Information of China (English)

    ZENG Rong-chang; ZHANG jin; HUANG Wei-jiu; W. DIETZEL; K. U. KAINER; C. BLAWERT; KE Wei

    2006-01-01

    This review provided some recent progress of the research on corrosion mechanisms of magnesium and its alloys and a basis for follow-on research. Galvanic corrosion,pitting corrosion,intergranular corrosion (IGC),filiform corrosion,crevice corrosion,stress corrosion cracking (SCC),and corrosion fatigue (CF) were discussed. The influence of metallurgical factors such as alloying elements,microstructure and secondary phases,processing factors such as heat treatment and weld,and environmental factors including temperature,relative humidity,solution pH values and concentration on corrosion were discussed. In particular,a mechanism of pitting corrosion caused by AlMn particles was proposed. The corrosion properties of AZ91D weld material were investigated.

  8. Crack shape developments and leak rates for circumferential complex-cracked pipes

    Energy Technology Data Exchange (ETDEWEB)

    Brickstad, B.; Bergman, M. [SAQ Inspection Ltd., Stockholm (Sweden)

    1997-04-01

    A computerized procedure has been developed that predicts the growth of an initial circumferential surface crack through a pipe and further on to failure. The crack growth mechanism can either be fatigue or stress corrosion. Consideration is taken to complex crack shapes and for the through-wall cracks, crack opening areas and leak rates are also calculated. The procedure is based on a large number of three-dimensional finite element calculations of cracked pipes. The results from these calculations are stored in a database from which the PC-program, denoted LBBPIPE, reads all necessary information. In this paper, a sensitivity analysis is presented for cracked pipes subjected to both stress corrosion and vibration fatigue.

  9. Stress corrosion cracking behaviour in welded X-70 linepipe steel under near-neutral pH conditions

    Energy Technology Data Exchange (ETDEWEB)

    Adeleke, A.H.; Luo, J.L.; Ivey, D.G. [Alberta Univ., Edmonton, AB (Canada). Dept. of Chemical and Materials Engineering

    2005-07-01

    This study examined the relationship between the near neutral pH stress corrosion cracking (SCC) resistance and the yield strength of pipelines steels. In particular, double-edge-notched flat tensile samples of X70 steel were used for both slow strain-rate testing (SSRT) and cyclic loading testing with the notch located in the zone of interest. This included the weld metal (WM), base metal (BM) and heat-affected zone (HAZ). In all samples, the mode of failure was mostly transgranular with cleavage facets around the edges of the fracture surface. One of the objectives of this study was to better understand the microstructural effect of the relationship. The 3 main parameters that were used to assess the SCC susceptibility in a near-neutral pH environment were the elongation ratio, the estimated percentage of the fracture surface that showed brittle fractures, and the relative crack growth at a given exposure time. It was shown that resistance to near-neutral pH SCC depends greatly on the microstructure of the pipeline steels. Fine-grained bainite and ferrite structured steels were found to have a much better combination of strength and SCC resistance compared to ferrite and pearlite structures. The high-to-low sensitivity ranking of the X70 linepipe steel to SCC was established to be: WM is greater than HAZ which is greater than BM. 20 refs., 1 tab., 9 figs.

  10. Corrosion inhibitor mechanisms on reinforcing steel in Portland cement pastes

    Science.gov (United States)

    Martin, Farrel James

    2001-07-01

    The mechanisms of corrosion inhibitor interaction with reinforcing steel are investigated in the present work, with particular emphasis on effects associated with corrosion inhibitors admixed into Portland cement paste. The principal objective in reinforcing steel corrosion inhibition for Portland cement concrete is observed to be preservation of the naturally passive steel surface condition established by the alkaline environment. Introduction of chloride ions to the steel surface accelerates damage to the passive film. Excessive damage to the passive film leads to loss of passivity and a destabilization of conditions that facilitate repair of the passive film. Passive film preservation in presence of chloride ions is achieved either through stabilization of the passive film or by modification of the chemical environment near the steel surface. Availability of inhibitors to the steel surface and their tendency to stabilize passive film defects are observed to be of critical importance. Availability of admixed corrosion inhibitors to the passive film is affected by binding of inhibitors during cement paste hydration. It is determined that pore solution concentrations of inorganic admixed inhibitors tend to be lower than the admixed concentration, while pore solution concentrations of organic admixed inhibitors tend to be higher than the admixed concentration. A fundamental difference of inhibitor function is observed between film-forming and defect stabilizing corrosion inhibitors. Experiments are conducted using coupons of reinforcing steel that are exposed to environments simulating chloride-contaminated Portland cement concrete. A study of the steel/cement paste interface is also performed, and compounds forming at this interface are identified using X-Ray diffraction.

  11. Effect of cold work hardening on stress corrosion cracking of stainless steels in primary water of pressurized water reactors

    Energy Technology Data Exchange (ETDEWEB)

    Raquet, O.; Herms, E. [CEA/Saclay, DEN/DPC, 91191 Gif sur Yvette Cedex (France); Vaillant, F.; Couvant, T.; Boursier, J.M. [EDF/Les Renardieres, R and D/MMC, 77250 Moret sur Loing (France)

    2004-07-01

    A R and D program is carried out in CEA and EDF laboratories to investigate separately the effects of factors which could contribute to IASCC mechanism. In the framework of this study, the influence of cold work on SCC of ASSs in primary water is studied to supply additional knowledge concerning the contribution of radiation hardening on IASCC of ASSs. Solution annealed ASSs, essentially of type AISI 304(L) and AISI 316(L), are generally considered very resistant to SCC in nominal primary water. However, Constant Extension Rate Tests (CERTs), performed on cold pressed humped specimens in nominal primary water at 360 deg. C, reveal that these materials can exhibit a high SCC susceptibility: deepest cracks reach 1 mm (mean crack growth rate about 1 {mu}m.h{sup -1}) and propagation is mainly intergranular for 304L and mainly transgranular for 316L. Indeed, work hardening in conjunction with high localized deformation can promote SCC. The influence of the nature of the cold work (shot peening, reaming, cold rolling, counter sinking, fatigue work hardening and tensile deformation) is investigated by means of screening CERTs performed with smooth specimens in 304L at 360 deg. C. For a given cold work hardening level, the susceptibility to crack initiation strongly depends on the cold working process, and no propagation is observed for a hardness level lower than 300 {+-}10 HV(0.49N). The propagation of cracks is observed only for dynamic loadings like CERT, traction/relaxation tests and crack growth rate tests performed with CT specimens under trapezoidal loading. Although crack initiation is observed for constant load and constant deformation tests, crack propagation do not seem to occur under these mechanical solicitations for 17000 hours of testing, even for hardness levels higher than 450 HV(0.49N). The mean crack growth rate increases when the hardness increases. An important R and D program is in progress to complement these results and to develop a SCC model for

  12. Stress corrosion cracking behavior of Alloy 600 in high temperature water

    Energy Technology Data Exchange (ETDEWEB)

    Webb, G.L.; Burke, M.G.

    1995-07-01

    SCC susceptibility of Alloy 600 in deaerated water at 360 C (statically loaded U-bend specimens) is dependent on microstructure and whether the material was cold-worked and annealed (CWA) or hot-worked and annealed (HWA). All cracking was intergranular, and materials lacking grain boundary carbides were most susceptible to SCC initiation. CWA tubing materials are more susceptible to SCC initiation than HWA ring-rolled forging materials with similar microstructures (optical metallography). In CWA tubing materials, one crack dominated and grew to a visible size. HWA materials with a low hot-working finishing temperature (<925 C) and final anneals at 1010-1065 C developed both large cracks (similar to those in CWA materials) and small intergranular microcracks detectable only by destructive metallography. HWA materials with a high hot-working finishing temperature (>980 C) and a high-temperature final anneal (>1040 C), with grain boundaries that are fully decorated, developed only microcracks in all specimens. These materials did not develop large, visually detectable cracks, even after more than 300 weeks exposure. A low-temperature thermal treatment (610 C for 7h), which reduces or eliminates SCC in Alloy 600, did not eliminate microcrack formation in high temperature processed HWA materials. Conventional metallographic and analytical electron microscopy (AEM) were done on selected materials to identify the factors responsible for the observed differences in cracking behavior. Major difference between high-temperature HWA and low-temperature HWA and CWA materials was that the high temperature processing and final annealing produced predominantly ``semi-continuous`` dendritic M{sub 7}C{sub 3} carbides along grain boundaries with a minimal amount of intragranular carbides. Lower temperature processing produced intragranular M7C3 carbides, with less intergranular carbides.

  13. Numerical simulation of the detection of crack in reinforced concrete structures of NPP due to expansion of reinforcing corrosive products using Impact-Echo method

    Directory of Open Access Journals (Sweden)

    Morávka Š.

    2008-12-01

    Full Text Available Nuclear energy boom is starting nowadays. But also current nuclear power plants (NPP are duty to certify their security for regular renewal of their operating licenses. NPP security can be significantly affected by defects of large amount of ageing reinforced concrete structures. Advanced Impact-Echo method seams to be very hopeful to cooperate at performing in-service inspections such structures. Just these in-service inspections are included in the first priority group of specific technical issues according to the recommendations of OECD-Nuclear Energy Agency, Commission on Safety of Nuclear Installation in the field of ageing management.This paper continues of extensive project dealing with Impact-Echo method application. It will present method description and main results of numerical modeling of detection and localization of crack caused by corrosive product expansion. Steel reinforcing rods are subjected to corrosion due to diffusion of corrosive agents from structure surface. Corrosive products have up to 7-times larger volume than pure steel. Raised strain can cad lead up to concrete failure and crack development. We investigate whether it is possible to detect these growing cracks by Impact-Echo method in time.Experimental verification of our numerical predictions is prepared on Civil Faculty in Brno.

  14. Dynamic fracture mechanics analysis for an edge delamination crack

    Science.gov (United States)

    Rizzi, Stephen A.; Doyle, James F.

    1994-01-01

    A global/local analysis is applied to the problem of a panel with an edge delamination crack subject to an impulse loading to ascertain the dynamic J integral. The approach uses the spectral element method to obtain the global dynamic response and local resultants to obtain the J integral. The variation of J integral along the crack front is shown. The crack behavior is mixed mode (Mode 2 and Mode 3), but is dominated by the Mode 2 behavior.

  15. Stress-Corrosion Cracking in High Strength Steels and in Titanium and Aluminum Alloys

    Science.gov (United States)

    1972-01-01

    widely throughout the technical community and is not available in collected form, the authors of the chapter on titanium have included a much higher...Elements................ 22 Derivation of KI by Specimen Compliance.............. 23 Experiental Determination of Comll-!hlncc........... 24 Theoretical...101. R. T. Ault, Republic Steel Corp., private communication . 102. S. R. Novak and S. T. Rolfe, Kt, Stress-Corrosion Tests of l2Ni-5Cr-3Mo and l8Ni

  16. The Role of Stress in the Corrosion Cracking of Aluminum Alloys

    Science.gov (United States)

    2013-03-01

    orthogonal to the other two directions. This system is used for sheet, extrusions , and forgings with nonsymmetrical grain flow [18]. All testing...around the constituent particles and then spreads to the grain boundaries. It is not possible to determine from the present results if the IGC...International, 2011, pp.1-8. [30] J. R. Scully et al., " Spreading of intergranular corrosion on the surface of sensitized Al-4.4Mg alloys: A general finding

  17. Effect of flexural crack on plain concrete beam failure mechanism A numerical simulation

    Directory of Open Access Journals (Sweden)

    Abdoullah Namdar

    2016-03-01

    Full Text Available The flexural failure of plain concrete beam occurs along with development of flexural crack on beam. In this paper by using ABAQUS, mechanism failure of plain concrete beam under three steps have been simulated. The cracking moment has been analytically calculated and applied on the both sides of the fixed beam, and flexural crack has been simulated on beam. Displacement, von Mises, load reaction, displacementcrack length, von Mises-crack length and von Mises-displacement of beams have been graphical depicted. Results indicated that, the flexural crack governs beam mechanism failure and its effects on beam resistance failure. It has been found that the flexural crack in initial stage it developed slowly and changes to be fast at the final stage of collapsing beam due to reduction of the flexural resistance of beam. Increasing mechanical properties of concrete, collapse displacement is reduced.

  18. The effects of thermomechanical processing and annealing on the microstructural evolution and stress corrosion cracking of alloy 690

    Science.gov (United States)

    Miller, Cody A.

    The effects of short-range order (SRO), long-range order (LRO), and plastic strain on the microstructure and stress corrosion cracking (SCC) susceptibility of Ni-Cr-Fe Alloy 690 have been investigated in detail. First, the presence of 1/3{422} and 1/2{311} diffuse intensities in B=[111] and B=[112] selected area diffraction patterns (SADPs), previously believed to indicate the presence of SRO, has been examined in Alloy 690, a Ni-Cr binary alloy, and a number of FCC materials in an effort to determine their source. It is shown that these intensities are not due to SRO, although their source remains somewhat unclear. However, an experiment was conducted that tracked the strong {111} reflections in a B=[112] SADP as the sample was tilted (19°) towards a B=[111] zone axis. Significantly, it was noted that the {111} intensities never fully disappear and that they fall in the 1/3{422} positions within the B=[111] SADP. This indicates that these diffuse intensities are related to reflections that lie in the first order Laue zone (FOLZ) when the zone is aligned along B=[111], although theoretical calculations indicate scattering from these planes into the zero order Laue zone used to form the SADP should not occur. Thus, while calculations are inconsistent with the behavior expected, the diffuse intensities observed in a number of high index zones are consistent with projections of higher order Laue zone reflections into the zero layer, suggesting that the theory is in need of reassessment. Second, the stability of the gamma'-Ni2Cr LRO phase present on the Ni-Cr phase diagram was examined in a Ni-55Cr binary alloy. The results indicate that the gamma'-Ni2Cr phase is indeed metastable, and that the two-phase gamma-Ni + alpha-Cr phase field extends all the way to room temperature. Likewise, the sluggish formation of the gamma'-Ni 2Cr phase appears to occur only over a narrow composition and temperature range. It is speculated that this important phase in more complex

  19. Modelling of Debond and Crack Propagation in Sandwich Structures Using Fracture and Damage Mechanics

    DEFF Research Database (Denmark)

    Berggreen, C.; Simonsen, Bo Cerup; Toernqvist, Rikard

    2003-01-01

    Skin-core de-bonding or core crack propagation will often be dominating mechanisms in the collapse modes of sandwich structures. This paper presents two different methods for prediction of crack propagation in a sandwich structure: a fracture mechanics approach, where a new mode-mix method...

  20. Maintainability Improvement Through Corrosion Prediction

    Science.gov (United States)

    1997-12-01

    potential, current, pH, and chloride ion concentration were made along a simulated corrosion fatigue crack for HY80 (UNS K31820) steel in seawater...frequency range of 0.05-50 Hz, a 7075-T6 aluminium alloy and 304 and 316L stainless steels were fatigue tested in 3.0% NaCl solution. The increments...DESCRIPTORS: Conference Paper; Aluminum base alloys- Mechanical properties; Austenitic stainless steels - Mechanical properties; Corrosion fatigue

  1. An Evaluation of the Corrosion and Mechanical Performance of Interstitially Surface Hardened Stainless Steel

    Science.gov (United States)

    2013-05-10

    metallography and microhardness profiling. The corrosion performance of the hardened surface is assessed using electrochemical potentiodynamic testing to...cracking resistance, and galling performance. Metallurgical Evaluation: Microhardness testing was conducted for Processes B1 and B2, which represent...incorporated experimental testing conducted on 316L stainless steel that has been surface hardened using available commercial techniques, using both

  2. Fracture mechanics analyses of partial crack closure in shell structures

    Science.gov (United States)

    Zhao, Jun

    2007-12-01

    This thesis presents the theoretical and finite element analyses of crack-face closure behavior in shells and its effect on the stress intensity factor under a bending load condition. Various shell geometries, such as spherical shell, cylindrical shell containing an axial crack, cylindrical shell containing a circumferential crack and shell with double curvatures, are all studied. In addition, the influence of material orthotropy on the crack closure effect in shells is also considered. The theoretical formulation is developed based on the shallow shell theory of Delale and Erdogan, incorporating the effect of crack-face closure at the compressive edges. The line-contact assumption, simulating the crack-face closure at the compressive edges, is employed so that the contact force at the closure edges is introduced, which can be translated to the mid-plane of the shell, accompanied by an additional distributed bending moment. The unknown contact force is computed by solving a mixed-boundary value problem iteratively, that is, along the crack length, either the normal displacement of the crack face at the compressive edges is equal to zero or the contact pressure is equal to zero. It is found that due to the curvature effects crack closure may not always occur on the entire length of the crack, depending on the direction of the bending load and the geometry of the shell. The crack-face closure influences significantly the magnitude of the stress intensity factors; it increases the membrane component but decreases the bending component. The maximum stress intensity factor is reduced by the crack-face closure. The significant influence of geometry and material orthotropy on rack closure behavior in shells is also predicted based on the analytical solutions. Three-dimensional FEA is performed to validate the theoretical solutions. It demonstrates that the crack face closure occurs actually over an area, not on a line, but the theoretical solutions of the stress intensity

  3. SEMI-ANALYTICAL FINITE ELEMENT METHOD FOR FICTITIOUS CRACK MODEL IN FRACTURE MECHANICS OF CONCRETE

    Institute of Scientific and Technical Information of China (English)

    王承强; 郑长良

    2004-01-01

    Based on the Hamiltonian governing equations of plane elasticity for sectorial domain, the variable separation and eigenfunction expansion techniques were employed to develop a novel analytical finite element for the fictitious crack model in fracture mechanics of concrete. The new analytical element can be implemented into FEM program systems to solve fictitious crack propagation problems for concrete cracked plates with arbitrary shapes and loads. Numerical results indicate that the method is more efficient and accurate than ordinary finite element method.

  4. RESEARCH ON DEGRADATION CORROSIVE ENVIRONMENT OF SOME STEELS USED IN MANUFACTURING MINING EQUIPMENT. MECHANICAL TESTS

    Directory of Open Access Journals (Sweden)

    Florin CIOFU

    2017-05-01

    Full Text Available Simultaneous action of mechanical stress variables and the corrosive environment leads to the deterioration of structures made of steel or of other metallic materials, a process called fatigue in corrosive environment or corrosion fatigue, which has causes and effects different from degradation under the singular action, either of mechanical strain or of corrosive environment. The aim of this paper is the study of the behavior,under fatigue conditions in corrosive environment of low alloy steels meant for the construction of mining equipment used in various mining operations in Gorj county. Based on experimental research regarding sustainability in fatigue corrosion, analyses of the interaction between the mechanical and the electrochemical factors as well as microscopic analyses of the structures we aim in this paper at deeply studying the performance of degradation processes that occur in the surface layers and lead to destruction by corrosion fatigue of the steels under study.

  5. Fatigue and Corrosion in Metals

    CERN Document Server

    Milella, Pietro Paolo

    2013-01-01

    This textbook, suitable for students, researchers and engineers, gathers the experience of more than 20 years of teaching fracture mechanics, fatigue and corrosion to professional engineers and running experimental tests and verifications to solve practical problems in engineering applications. As such, it is a comprehensive blend of fundamental knowledge and technical tools to address the issues of fatigue and corrosion. The book initiates with a systematic description of fatigue from a phenomenological point of view, since the early signs of submicroscopic damage in few surface grains and continues describing, step by step, how these precursors develop to become mechanically small cracks and, eventually, macrocracks whose growth is governed by fracture mechanics. But fracture mechanics is also introduced to analyze stress corrosion and corrosion assisted fatigue in a rather advanced fashion. The author dedicates a particular attention to corrosion starting with an electrochemical treatment that mechanical e...

  6. The Mechanism and Influencing Factors of Corrosion in a Gas Heating-Furnace

    Institute of Scientific and Technical Information of China (English)

    YANG Zhi-gang; ZHANG Ning-sheng; WU Xin-min

    2005-01-01

    Natural gas should be heated and throttled for the purpose of purification and transportation at the first gas production factory of the Changqing field. The safe use and heat-transfer efficiency of a heating-furnace affect the safe and smooth production of natural gas directly. At gas collecting stations now, no measures of anticorrosion have been adopted in heating furnaces which erode and scale badly.In order to solve the corrosive problem of heating-furnaces, prolong operating life of heating-furnaces,assure safe and smooth production of natural gas, the mechanism and influencing factors of corrosion of the heating-furnace were analyzed and some corresponding measures were brought forward based on a field investigation of usage behavior and present operational status of heating-furnaces at the first gas production factory. The results show that the corrosive ion and soluble CO2 and O2 in water erode metal badly at the condition of being heated. Corrosion of a heating-furnace are mostly oxygen corrosion, corrosive ion corrosion, acid corrosion, iron encrustation corrosion, dry and wet interface corrosion, caustic corrosion, etc; The influencing factors of corrosion mainly include soluble O2 and CO2 in water, pH value, heat loading, corrosive ion, soluble solid (salinity) and non-flowing character of water, etc.

  7. Assessment of stress-corrosion cracking in a water-cooled ITER

    Energy Technology Data Exchange (ETDEWEB)

    Jones, R.H.; Bruemmer, S.M.

    1989-04-01

    Water-cooled, near-term reactors will operate under conditions at which SCC is possible; however, control of material purity and processing and coolant chemistry can either eliminate or greatly reduce the probability of this type of structural failure. This evaluation has focused on an assessment of water impurity effects on SCC of austenitic stainless steel at temperatures below 100{degree}C and on the conditions controlling sensitization in the fusion heat of Type 316 SS and the fusion materials heat of modified Type 316 SS designated as PCA. This assessment identifies the dominant effect of small concentrations of impurities in high-purity water on SCC such that crack growth rates at 25--75{degree}C in water with as little as 5--15 ppM Cl{sup {minus}} are equal to the crack growth rates at 200--300{degree}C in high-purity water. These effects are primarily for sensitized Type 304 SS, so analysis of sensitization behavior of fusion austenitic alloys was also undertaken. An SSDOS model developed at PNL was used to make these assessments, and correlation to experimental results for Type 316 SS was very good. Both the fusion heat of Type 316 SS and PCA can be severely sensitized but with proper thermal treatment it should be possible to avoid sensitization. 14 refs., 8 figs.

  8. Environmental Degradation of Materials: Surface Chemistry Related to Stress Corrosion Cracking

    Science.gov (United States)

    Schwarz, J. A.

    1985-01-01

    Parallel experiments have been performed in order to develop a comprehensive model for stress cracking (SCC) in structural materials. The central objective is to determine the relationship between the activity and selectivity of the microstructure of structural materials to their dissolution kinetics and experimentally measured SCC kinetics. Zinc was chosen as a prototype metal system. The SCC behavior of two oriented single-crystal disks of zinc in a chromic oxide/sodium sulfate solution (Palmerton solution) were determined. It was found that: (1) the dissolution rate is strongly (hkil)-dependent and proportional to the exposure time in the aggressive environment; and (2) a specific slip system is selectively active to dissolution under applied stress and this slip line controls crack initiation and propagation. As a precursor to potential microgrvity experiments, electrophoretic mobility measurements of zinc particles were obtained in solutions of sodium sulfate (0.0033 M) with concentrations of dissolved oxygen from 2 to 8 ppm. The equilibrium distribution of exposed oriented planes as well as their correlation will determine the particle mobility.

  9. Environmental Degradation of Materials: Surface Chemistry Related to Stress Corrosion Cracking

    Science.gov (United States)

    Schwarz, J. A.

    1985-01-01

    Parallel experiments have been performed in order to develop a comprehensive model for stress cracking (SCC) in structural materials. The central objective is to determine the relationship between the activity and selectivity of the microstructure of structural materials to their dissolution kinetics and experimentally measured SCC kinetics. Zinc was chosen as a prototype metal system. The SCC behavior of two oriented single-crystal disks of zinc in a chromic oxide/sodium sulfate solution (Palmerton solution) were determined. It was found that: (1) the dissolution rate is strongly (hkil)-dependent and proportional to the exposure time in the aggressive environment; and (2) a specific slip system is selectively active to dissolution under applied stress and this slip line controls crack initiation and propagation. As a precursor to potential microgrvity experiments, electrophoretic mobility measurements of zinc particles were obtained in solutions of sodium sulfate (0.0033 M) with concentrations of dissolved oxygen from 2 to 8 ppm. The equilibrium distribution of exposed oriented planes as well as their correlation will determine the particle mobility.

  10. Analysis on the internal cracking of concrete cover due to rebar uniform corrosion%混凝土保护层均匀锈胀内裂分析

    Institute of Scientific and Technical Information of China (English)

    姜慧; 喻孟雄; 刘荣桂

    2014-01-01

    钢筋锈蚀是影响钢筋混凝土结构使用寿命的重要因素,混凝土保护层锈胀内裂加速整个混凝土保护层的开裂。假定混凝土满足最大伸长线应变破坏准则,利用圆孔扩张理论对铁锈自由膨胀充满混凝土与钢筋交界面空隙后混凝土保护层内裂进行分析,建立了锈胀内裂时刻的钢筋锈蚀深度计算式。针对计算式主要影响参数的分析表明:钢筋锈蚀深度与水泥石中毛细孔体积、钢筋直径、混凝土极限拉应变成正相关,与铁锈体积膨胀率成负相关。%Rebar corrosion is an important factor affecting the service life of reinforced concrete structures.Concrete cover internal cracking induced by reinforcement corrosion accelerates cracking of all cover.Based on the assumption of concrete meet the maximum ten-sional strain failure criterion,one equation for predicting the reinforcement corrosion depth from corrosion initiation to cover internal cracking was established according to the cylindrical cavity expansion theory.By analyzing main parameters of the equation ,the results showed that the reinforcement corrosion depth was positive correlation with cement stone pore volume,diameter of rebar,concrete ulti-mate tensile strain,and negative correlation with rust rate of volume expansion.

  11. Corrosion rate of steel embedded in blended Portland and fluid catalytic cracking catalyst residue (FC3R cement mortars

    Directory of Open Access Journals (Sweden)

    Payá, J.

    2008-12-01

    Full Text Available This paper reports on a study of the corrosion levels in steel bars embedded in mortars made with a blend of Portland cement and (0-20% spent fluid catalytic cracking catalyst residue (FC3R, with a variable (0.3-0.7 water/binder (w/b ratio. The specimens were stored in the following conditions: relative humidity of 40, 80 or 100% and CO2 concentrations of 5 and 100%. The steel corrosion rate was measured with polarization resistance techniques. In the absence of aggressive agents, the steel was found to remain duly passivated in mortars with an FC3R content of up to 15% under all the conditions of relative humidity tested. The reinforcement corrosion level in mortars with a w/b ratio of 0.3 and 15% FC3R subjected to accelerated carbonation was similar to the level observed in the unblended Portland cement control mortar.En este trabajo se ha estudiado el nivel de corrosión de barras de acero embebidas en morteros de cemento Portland con relación agua/material cementante (a/mc variable (0,3-0,7, en los que parte del cemento (0-20% se sustituyó por catalizador de craqueo usado (FC3R. Las condiciones de conservación de las probetas elaboradas fueron las siguientes: distintas humedades relativas (40, 80 y 100% y dos concentraciones de CO2 (5 y 100%. La velocidad de corrosión de los aceros se midió mediante la técnica de resistencia de polarización. Se ha podido determinar que, bajo las distintas condiciones de humedad relativa y ausencia de agresivo, los aceros se mantuvieron correctamente pasivados en los morteros con contenidos de FC3R de hasta el 15%. El nivel de corrosión que presenta el refuerzo embebidos en morteros con sustitución de un 15% de cemento por FC3R y relación a/mc 0,3, al ser sometidos a un proceso de carbonatación acelerada, era muy similar al mostrado por el mortero patrón, sin FC3R.

  12. Standard Practice for Use of Mattsson's Solution of pH 7.2 to Evaluate the Stress- Corrosion Cracking Susceptibility of Copper-Zinc Alloys

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2011-01-01

    1.1 This practice covers the preparation and use of Mattsson's solution of pH 7.2 as an accelerated stress-corrosion cracking test environment for brasses (copper-zinc base alloys). The variables (to the extent that these are known at present) that require control are described together with possible means for controlling and standardizing these variables. 1.2 This practice is recommended only for brasses (copper-zinc base alloys). The use of this test environment is not recommended for other copper alloys since the results may be erroneous, providing completely misleading rankings. This is particularly true of alloys containing aluminum or nickel as deliberate alloying additions. 1.3 This practice is intended primarily where the test objective is to determine the relative stress-corrosion cracking susceptibility of different brasses under the same or different stress conditions or to determine the absolute degree of stress corrosion cracking susceptibility, if any, of a particular brass or brass component ...

  13. Time exposure studies on stress corrosion cracking of aluminum 2014-T6, 2219-T87, 2014-T651, 7075-T651, and titanium 6Al-4V

    Science.gov (United States)

    Terrell, J.

    1973-01-01

    The effect of a constant applied stress in crack initiation of aluminum 2014-T6, 2219-T87, 2014-T651, 7075-T651 and titanium 6Al-4V has been investigated. Aluminum c-ring specimens (1-inch diameter) and u-band titanium samples were exposed continuously to a 3.5% NaCl solution (pH 7) and organic fluids of ethyl, methyl, and iso-propyl alcohol (reagent purity), and demineralized distilled water. Corrosive action was observed to begin during the first and second day of constant exposure as evidenced by accumulation of hydrogen bubbles on the surface of stressed aluminum samples. However, titanium stressed specimens showed no reactions to its environment. Results of this investigation seems to suggest that aluminum 2014-T6, aluminum 7075-T651 and aluminum 2014-T651 are susceptible to stress corrosion cracking in chloride solution (NaCl), while aluminum 2219-T87 seem to resist stress corrosion cracking in sodium chloride at three levels of stress (25%, 50%, and 75% Y.S.). In organic fluids of methyl, ethyl, and iso-propyl alcohol, 2014-T6 and 7075-T651 did not fail by SCC; but 2014-T651 was susceptible to SCC in methly alcohol, but resistant in ethyl alcohol, iso-propyl alcohol and demineralized distilled water.

  14. Time exposure studies on stress corrosion cracking of aluminum 2014-T6, aluminum 7075-T651, and titanium 6Al-4V

    Science.gov (United States)

    Terrell, J.

    1972-01-01

    The effect of a constant applied stress in crack initiation of aluminum 2014-T6, 7075-T651 and titanium 6A1-4V has been investigated. Aluminum c-ring specimens (1-inch diameter) and u-band titanium samples were exposed continuously to a 3.5% NaCl solution (pH 6) and organic fluids of ethyl, methyl, and iso-propyl alcohol (reagent purity). Corrosive action was observed to begin during the first and second day of constant exposure as evidenced by accumulation of hydrogen bubbles on the surface of stressed aluminum samples. However, a similar observation was not noted for titanium stressed specimens. Results of this investigation seems to suggest that aluminum 2014-T6, aluminum 7075-T651 are susceptible to stress corrosion cracking in chloride solution (NaCl); while they (both alloys) seem to resist stress corrosion cracking in methyl alcohol, ethyl alcohol, iso-propyl alcohol, and demineralized distilled water. Titanium 6A1-4V showed some evidence of susceptibility to SCC in methanol, while no such susceptibility was exhibited in ethanol, iso-propyl alcohol and demineralized distilled water.

  15. Mechanical properties and crack growth behavior of polycrystalline copper using molecular dynamics simulation

    Science.gov (United States)

    Qiu, Ren-Zheng; Li, Chi-Chen; Fang, Te-Hua

    2017-08-01

    This study investigated the mechanical properties and crack propagation behavior of polycrystalline copper using a molecular dynamics simulation. The effects of temperature, grain size, and crack length were evaluated in terms of atomic trajectories, slip vectors, common neighbor analysis, the material’s stress-strain diagram and Young’s modulus. The simulation results show that the grain boundary of the material is more easily damaged at high temperatures and that grain boundaries will combine at the crack tip. From the stress-strain diagram, it was observed that the maximum stress increased as the temperature decreased. In contrast, the maximum stress was reduced by increasing the temperature. With regard to the effect of the grain size, when the grain size was too small, the structure of the sample deformed due to the effect of atomic interactions, which caused the grain boundary structure to be disordered in general. However, when the grain size was larger, dislocations appeared and began to move from the tip of the crack, which led to a new dislocation phenomenon. With regards to the effect of the crack length, the tip of the crack did not affect the sample’s material when the crack length was less than 5 nm. However, when the crack length was above 7.5 nm, the grain boundary was damaged, and twinning structures and dislocations appeared on both sides of the crack tip. This is because the tip of the crack was blunt at first before sharpening due to the dislocation effect.

  16. Cracks in Polymer Spherulites: Phenomenological Mechanisms in Correlation with Ring Bands

    Directory of Open Access Journals (Sweden)

    Eamor M. Woo

    2016-09-01

    Full Text Available This article reviews possible mechanisms of various crack forms and their likely correlations with interior crystal lamellae and discontinuous interfaces in spherulites. Complex yet periodically repetitive patterns of cracks in spherulites are beyond attributions via differences in thermal expansion coefficients, which would cause random and irregular cracks in the contract direction only. Cracks in brittle polymers such as poly(l-lactic acid (PLLA, or poly(4-hydroxyl butyrate (PHB, or more ductile polymers such as poly(trimethylene terephthalate (PTT are examined and illustrated, although for focus and demonstration, more discussions are spent on PLLA. The cracks can take many shapes that bear extremely striking similarity to the ring-band or lamellar patterns in the same spherulites. Crack patterns may differ significantly between the ring-banded and ringless spherulites, suggesting that the cracks may be partially shaped and governed by interfaces of lamellae and how the lamellar crystals assemble themselves in spherulites. Similarly, with some exceptions, most of the cracks patterns in PHB or PTT are also highly guided by the lamellar assembly in either ring-banded spherulites or ringless spherulites. Some exceptions of cracks in spherulites deviating from the apparent crystal birefringence patterns do exist; nevertheless, discontinuous interfaces in the initial lamellae neat the nuclei center might be hidden by top crystal over-layers of the spherulites, which might govern crack propagation.

  17. Corrosion Mechanism of Corrosion-Resistant Steel Developed for Bottom Plate of Cargo Oil Tanks

    Institute of Scientific and Technical Information of China (English)

    Feilong SUN; Xiaogang LI; Fan ZHANG; Xuequn CHENG; Cheng ZHOU; Nianchun WU; Yuqun YIN

    2013-01-01

    A new type of corrosion-resistant steel consisting of ferrite and bainite phases was developed for cargo oil tanks of crude oil tankers.The corrosion rate of this new steel was 0.22 mm/a,which was equivalent to ca.1/5 of the criterion (≤ 1 mm/a) for corrosion-resistant steels.The composition and element distribution of the corrosion products were investigated by micro-Raman spectrometry and energy dispersive spectrometer.The results demonstrated that the corrosion product was composed of α-FeOOH,Fe3O4 and a continuous Cu enrichment layer.This kind of corrosion product was protective to the steel matrix and accounted for the enhancement of the corrosion resistance of the new developed steel.

  18. Cracking and Corrosion of Composite Tubes in Black Liquor Recovery Boiler Primary Air Ports

    Energy Technology Data Exchange (ETDEWEB)

    Keiser, James R.; Singbeil, Douglas L.; Sarma, Gorti B.; Kish, Joseph R.; Yuan, Jerry; Frederick, Laurie A.; Choudhury, Kimberly A.; Gorog, J. Peter; Jetté, Francois R.; Hubbard, Camden R.; Swindeman, Robert W.; Singh, Prett M.; Maziasz, Phillip J.

    2006-10-01

    Black liquor recovery boilers are an essential part of kraft mills. Their design and operating procedures have changed over time with the goal of providing improved boiler performance. These performance improvements are frequently associated with an increase in heat flux and/or operating temperature with a subsequent increase in the demand on structural materials associated with operation at higher temperatures and/or in more corrosive environments. Improvements in structural materials have therefore been required. In most cases the alternate materials have provided acceptable solutions. However, in some cases the alternate materials have solved the original problem but introduced new issues. This report addresses the performance of materials in the tubes forming primary air port openings and, particularly, the problems associated with use of stainless steel clad carbon steel tubes and the solutions that have been identified.

  19. Cl-浓度对超级13Cr油管钢应力腐蚀开裂行为的影响%Effects of Cl- Concentration on Stress Corrosion Cracking Behaviors of Super 13Cr Tubing Steels

    Institute of Scientific and Technical Information of China (English)

    姚小飞; 谢发勤; 吴向清; 王毅飞

    2012-01-01

    Effects of Cl concentration on the stress corrosion cracking behaviors of super 13Cr tubing steels were investigated in different concentration of NaCl solution, that tensile strength, elongation rate, cracking time, stress corrosion cracking susceptibility (kscc) and fracture morphology were analyzed by the experimental method of slow strain rate tension (SSRT) stress corrosion cracking (SCO, δε curves, scanning electron microscope (SEM), energy dispersive X-ray spectrometer (EDS) and X-ray diffraction (XRD). The results showed that the degree of stress corrosion was light at below 15% NaCl solution and was severe at the concentration above 25% NaCl solution. With Cl- concentration of solution increased, super 13Cr tubing steels mechanics properties reduced, SCC resistance properties reduced, the tendency of stress corrosion cracking increased, the stress corrosion cracking susceptibility kδ and kε both increased, and the increased tendency of kε were more obviously than kδ, effects of Cl- concentration on the plastic deformation of super 13Cr tubing steels were more significantly than tensile strength.%采用慢应变速率拉伸(SSRT)应力腐蚀开裂(SCC)的实验方法,通过应力应变(σ-ε)曲线、扫描电镜( SEM)、能谱分析(EDS)和X射线衍射分析(XRD)等手段分析了超级13Cr油管钢在NaCl溶液中的抗拉强度、延伸率、断裂时间、应力腐蚀开裂敏感性指数(kscc)和断口形貌,研究了Cl-浓度对其应力腐蚀开裂行为的影响.结果显示:当NaCl溶液浓度低于15%时,超级13Cr油管钢应力腐蚀的程度较轻,抗应力腐蚀开裂性能较好;而当NaCl溶液浓度大于25%时,其应力腐蚀的程度严重,抗应力腐蚀开裂性能较差;随溶液Cl-浓度的增大,超级13Cr油管钢的力学性能降低、抗SCC性能降低、应力腐蚀开裂的倾向增大、应力腐蚀开裂敏感性指数kσ和kε均呈现增大的趋势,且kε比kσ增大的趋势更明显;Cl浓度对超级13

  20. DEVELOPMENT OF AN EMAT IN-LINE INSPECTION SYSTEM FOR DETECTION, DISCRIMINATION, AND GRADING OF STRESS CORROSION CRACKING IN PIPELINES

    Energy Technology Data Exchange (ETDEWEB)

    Jeff Aron; Jeff Jia; Bruce Vance; Wen Chang; Raymond Pohler; Jon Gore; Stuart Eaton; Adrian Bowles; Tim Jarman

    2005-02-01

    This report describes prototypes, measurements, and results for a project to develop a prototype pipeline in-line inspection (ILI) tool that uses electromagnetic acoustic transducers (EMATs) to detect and grade stress corrosion cracking (SCC). The introduction briefly provides motivation and describes SCC, gives some background on EMATs and guided ultrasonic waves, and reviews promising results of a previous project using EMATs for SCC. The experimental section then describes lab measurement techniques and equipment, the lab mouse and prototypes for a mule, and scan measurements made on SCC. The mouse was a moveable and compact EMAT setup. The prototypes were even more compact circuits intended to be pulled or used in an ILI tool. The purpose of the measurements was to determine the best modes, transduction, and processing to use, to characterize the transducers, and to prove EMATs and mule components could produce useful results. Next, the results section summarizes the measurements and describes the mouse scans, processing, prototype circuit operating parameters, and performance for SH0 scans. Results are given in terms of specifications--like SNR, power, insertion loss--and parametric curves--such as signal amplitude versus magnetic bias or standoff, reflection or transmission coefficients versus crack depth. Initially, lab results indicated magnetostrictive transducers using both SH0 and SV1 modes would be worthwhile to pursue in a practical ILI system. However, work with mule components showed that SV1 would be too dispersive, so SV1 was abandoned. The results showed that reflection measurements, when normalized by the direct arrival are sensitive to and correlated with SCC. This was not true for transmission measurements. Processing yields a high data reduction, almost 60 to 1, and permits A and C scan display techniques and software already in use for pipeline inspection. An analysis of actual SH0 scan results for SCC of known dimensions showed that length

  1. Uncommon deformation mechanisms during fatigue-crack propagation in nanocrystalline alloys.

    Science.gov (United States)

    Cheng, Sheng; Lee, Soo Yeol; Li, Li; Lei, Changhui; Almer, Jon; Wang, Xun-Li; Ungar, Tamas; Wang, Yinmin; Liaw, Peter K

    2013-03-29

    The irreversible damage at cracks during the fatigue of crystalline solids is well known. Here we report on in situ high-energy x-ray evidence of reversible fatigue behavior in a nanocrystalline NiFe alloy both in the plastic zone and around the crack tip. In the plastic zone, the deformation is fully recoverable as the crack propagates, and the plastic deformation invokes reversible interactions of dislocation and twinning in the nanograins. But around the crack tip lies a regime with reversible grain lattice reorientation promoted by a change of local stress state. These observations suggest unprecedented fatigue deformation mechanisms in nanostructured systems that are not addressed theoretically.

  2. Effects of Nitrogen and Tensile Direction on Stress Corrosion Cracking Susceptibility of Ni-Free FeCrMnC-Based Duplex Stainless Steels

    Science.gov (United States)

    Ha, Heon-Young; Lee, Chang-Hoon; Lee, Tae-Ho; Kim, Sangshik

    2017-01-01

    Stress corrosion cracking (SCC) behavior of Ni-free duplex stainless steels containing N and C (Febalance-19Cr-8Mn-0.25C-(0.03, 0.21)N, in wt %) was investigated by using a slow strain rate test (SSRT) in air and aqueous NaCl solution with different tensile directions, including parallel (longitudinal) and perpendicular (transverse) to the rolling direction. It was found that alloying N was effective in increasing the resistance to SCC, while it was higher along the longitudinal direction than the transverse direction. The SCC susceptibility of the two alloys was assessed based on the electrochemical resistance to pitting corrosion, the corrosion morphology, and the fractographic analysis. PMID:28772651

  3. Environmental and Material Influences on the Stress-Corrosion Cracking of Steel in H2O–CO–CO2 Solutions

    Directory of Open Access Journals (Sweden)

    J. W. van der Merwe

    2012-01-01

    Full Text Available The stress-corrosion cracking of A516 pressure vessel steel was investigated by the use of slow strain-rate tests. The orientation of samples to the rolling direction was investigated, and it was found that samples machined longitudinal to the rolling direction showed a slightly increased sensitivity to stress corrosion. The temperature variation showed that for different gas mixtures, the maximum sensitivity to stress corrosion was in the region of 45° to 55°C for the 25% CO gas mixture, whereas with higher CO concentrations, this temperature region of maximum sensitivity moved to higher temperatures. Surface finish showed a slight increase in sensitivity to cracking with increased surface roughness. The most significant increase was found with increased total gas pressures and when samples have been exposed to the environment for an extended period. This was as a result of the inhibition of the corrosion reaction by the passivation of the carbon monoxide, which is a time-dependent process.

  4. Atmospheric-Induced Stress Corrosion Cracking of Grade 2205 Duplex Stainless Steel—Effects of 475 °C Embrittlement and Process Orientation

    Directory of Open Access Journals (Sweden)

    Cem Örnek

    2016-07-01

    Full Text Available The effect of 475 °C embrittlement and microstructure process orientation on atmospheric-induced stress corrosion cracking (AISCC of grade 2205 duplex stainless steel has been investigated. AISCC tests were carried out under salt-laden, chloride-containing deposits, on U-bend samples manufactured in rolling (RD and transverse directions (TD. The occurrence of selective corrosion and stress corrosion cracking was observed, with samples in TD displaying higher propensity towards AISCC. Strains and tensile stresses were observed in both ferrite and austenite, with similar magnitudes in TD, whereas, larger strains and stresses in austenite in RD. The occurrence of 475 °C embrittlement was related to microstructural changes in the ferrite. Exposure to 475 °C heat treatment for 5 to 10 h resulted in better AISCC resistance, with spinodal decomposition believed to enhance the corrosion properties of the ferrite. The austenite was more susceptible to ageing treatments up to 50 h, with the ferrite becoming more susceptible with ageing in excess of 50 h. Increased susceptibility of the ferrite may be related to the formation of additional precipitates, such as R-phase. The implications of heat treatment at 475 °C and the effect of process orientation are discussed in light of microstructure development and propensity to AISCC.

  5. Controlled Mechanical Cracking of Metal Films Deposited on Polydimethylsiloxane (PDMS

    Directory of Open Access Journals (Sweden)

    Andreas Polywka

    2016-09-01

    Full Text Available Stretchable large area electronics conform to arbitrarily-shaped 3D surfaces and enables comfortable contact to the human skin and other biological tissue. There are approaches allowing for large area thin films to be stretched by tens of percent without cracking. The approach presented here does not prevent cracking, rather it aims to precisely control the crack positions and their orientation. For this purpose, the polydimethylsiloxane (PDMS is hardened by exposure to ultraviolet radiation (172 nm through an exposure mask. Only well-defined patterns are kept untreated. With these soft islands cracks at the hardened surface can be controlled in terms of starting position, direction and end position. This approach is first investigated at the hardened PDMS surface itself. It is then applied to conductive silver films deposited from the liquid phase. It is found that statistical (uncontrolled cracking of the silver films can be avoided at strain below 35%. This enables metal interconnects to be integrated into stretchable networks. The combination of controlled cracks with wrinkling enables interconnects that are stretchable in arbitrary and changing directions. The deposition and patterning does not involve vacuum processing, photolithography, or solvents.

  6. Crack propagation and the material removal mechanism of glass-ceramics by the scratch test.

    Science.gov (United States)

    Qiu, Zhongjun; Liu, Congcong; Wang, Haorong; Yang, Xue; Fang, Fengzhou; Tang, Junjie

    2016-12-01

    To eliminate the negative effects of surface flaws and subsurface damage of glass-ceramics on clinical effectiveness, crack propagation and the material removal mechanism of glass-ceramics were studied by single and double scratch experiments conducted using an ultra-precision machine. A self-manufactured pyramid shaped single-grit tool with a small tip radius was used as the scratch tool. The surface and subsurface crack propagations and interactions, surface morphology and material removal mechanism were investigated. The experimental results showed that the propagation of lateral cracks to the surface and the interaction between the lateral cracks and radial cracks are the two main types of material peeling, and the increase of the scratch depth increases the propagation angle of the radial cracks and the interaction between the cracks. In the case of a double scratch, the propagation of lateral cracks and radial cracks between paired scratches results in material peeling. The interaction between adjacent scratches depends on the scratch depth and separation distance. There is a critical separation distance where the normalized material removal volume reaches its peak. These findings can help reduce surface flaws and subsurface damage induced by the grinding process and improve the clinical effectiveness of glass-ceramics used as biological substitute and repair materials. Copyright © 2016 Elsevier Ltd. All rights reserved.

  7. Effects of Water Intrusion on Mechanical Properties of and Crack Propagation in Coal

    Science.gov (United States)

    Yao, Qiangling; Chen, Tian; Ju, Minghe; Liang, Shun; Liu, Yapeng; Li, Xuehua

    2016-12-01

    Studying the mechanical properties of and crack propagation in coal after water intrusion is necessary to tackle a number of geological engineering problems such as those associated with underground water storage in collieries and support for underground roadways in coal mines. To study the mechanical properties and crack development, 12 coal samples with moisture contents of 0, 2.37, 3.78 and 5.29 % were prepared for acoustic emission tests under uniaxial compression. Over about 6 days, the coal samples absorbed moisture from a humidifier in three different phases. In this period, uniaxial tests show that the peak stress, elastic modulus, strain softening modulus and post-peak modulus decreased with rising moisture content in the samples while the peak strain increased. It was further found that, by analysing the relationship between the stiffness and stress and the accumulated acoustic emission counts, all the phases of crack development can be evaluated. This is useful for studying the effect of water intrusion on crack propagation and for calculating the mechanical properties of the coal such as the elastic modulus. This investigation also quantifies the percentage of the stress thresholds for crack closure, crack initiation, and crack damage that constitutes the peak stress. These stress thresholds do not change with moisture content. Our results are of great significance for water storage in coal mines, for determination of pillar dimensions in coal mines, and for expanding the knowledge base of the mechanical properties of coal and the characteristics of crack propagation.

  8. The influence of long term use of inhibitors in hydrochloric acid pickling baths on hydrogen induced stress corrosion cracking

    Energy Technology Data Exchange (ETDEWEB)

    Feser, R.; Friedrich, A.; Scheide, F. [Fachhochschule Suedwestfalen, University of Applied Science, Frauenstuhlweg 31, D-58644 Iserlohn (Germany)

    2002-09-01

    The influence of commercially available inhibitors on the absorption of hydrogen by steel (St 52, StE 460, StE 690, 42CrMo4) in 15% hydrochloric acid was studied. The pickling bath aged continuously due to the chemical reaction with oxidized steel sheets. The H{sup +}- and inhibitor concentration decreased with time. The influence of this ageing process on hydrogen-induced stress corrosion cracking was tested by in-situ tensile tests in the bath solution. With increasing ageing of the bath, the reduction in fracture area was reduced and approached the values measured for non-inhibited acid baths. Furthermore hydrogen permeation was investigated. Permeation current densities rose with increasing ageing of the pickling solution. (Abstract Copyright[2002], Wiley Periodicals, Inc.) [German] Der Einfluss von kommerziell erhaeltlichen Inhibitoren auf die Wasserstoffabsorption von Stahl (St 52, StE 460, StE 690, 42CrMo4) wurde in Salzsaeure untersucht. Die Beizbaeder wurden kontinuierlich durch die chemische Reaktion mit oxidierten Stahlblechen gealtert. Die H{sup +}- und Inhibitorkonzentration nahm mit der Zeit ab. Der Einfluss dieses Alterungsprozesses auf die wasserstoffinduzierte Spannungsrisskorrosion wurde durch in-situ Zugversuche mit Badloesung untersucht. Mit zunehmender Alterung des Bades nahm die Brucheinschnuerung ab und erreichte Werte wie sie auch in der nicht inhibierten Saeure erreicht werden. Weiterhin wurde die Wasserstoff-Permeation untersucht. Die Permeationsstromdichte steigt mit zunehmender Alterung der Beizloesung. (Abstract Copyright[2002], Wiley Periodicals, Inc.)

  9. Benefits of thread rolling process to the stress corrosion cracking and fatigue resistance of high strength fasteners

    Energy Technology Data Exchange (ETDEWEB)

    Kephart, A.R.; Hayden, S.Z.

    1993-05-01

    Stress corrosion cracking (SCC) behavior of cut (machined) vice thread rolled Alloy X-750 and Alloy 625 fasteners in a simulated high temperature primary water environment has been evaluated. SCC testing at 360 and 338C included 157 small and 40 large 60{degree} Vee thread studs. Thread rolled fasteners had improved resistance relative to cut fasteners. Tests of fatigue resistance in air at room temperature and both air and primary water at 315C were conducted on smaller studs with both cut and rolled threads. Results showed rolled threads can have significantly improved fatigue lives over those of cut threads in both air and primary water. Fasteners produced by two different thread rolling methods, in-feed (radial) and through-feed (axial), revealed similar SCC initiation test results. Testing of thread rolled fasteners revealed no significant SCC or fatigue growth of rolling induced thread crest laps typical of the thread rolling process. While fatigue resistance differed between the two rolled thread supplier`s studs, neither of the suppliers studs showed SCC initiation at exposure times beyond that of cut threads with SCC. In contrast to rolling at room temperature, warm rolled (427C) threads showed no improvement over cut threads in terms of fatigue resistance. The observed improved SCC and fatigue performance of rolled threads is postulated to be due to interactive factors, including beneficial residual stresses in critically stressed thread root region, reduction of plastic strains during loading and formation of favorable microstructure.

  10. Effects of applied potential on the stress corrosion cracking behavior of 7003 aluminum alloy in acid and alkaline chloride solutions

    Science.gov (United States)

    Zhang, Xiao-yan; Song, Ren-guo; Sun, Bin; Lu, Hai; Wang, Chao

    2016-07-01

    Potentiodynamic polarization tests and slow strain rate test (SSRT) in combination with fracture morphology observations were conducted to investigate the stress corrosion cracking (SCC) behavior of 7003 aluminum alloy (AA7003) in acid and alkaline chloride solutions under various applied potentials ( E a). The results show that AA7003 is to a certain extent susceptible to SCC via anodic dissolution (AD) at open-circuit potential (OCP) and is highly susceptible to hydrogen embrittlement (HE) at high negative E a in the solutions with pH levels of 4 and 11. The susceptibility increases with negative shift in the potential when E a is less than -1000 mV vs. SCE. However, the susceptibility distinctly decreases because of the inhibition of AD when E a is equal to -1000 mV vs. SCE. In addition, the SCC susceptibility of AA7003 in the acid chloride solution is higher than that in the alkaline solution at each potential. Moreover, the effect of hydrogen on SCC increases with increasing hydrogen ion concentration.

  11. Stress Corrosion Cracking of the Drip Shield, The Waste Package Outer Barrier and the Stainless Steel Structural Material

    Energy Technology Data Exchange (ETDEWEB)

    C. Stephen

    2000-04-17

    One of the potential failure modes of the drip shield (DS), the waste package (WP) outer barrier, and the stainless structural material is the initiation and propagation of stress corrosion cracking (SCC) induced by the WP environment and various types of stresses that can develop in the DSs or the WPs. For the current design of the DS and WP, however, the DS will be excluded from the SCC evaluation because stresses that are relevant to SCC are insignificant in the DS. The major sources of stresses in the DS are loadings due to backfill and earthquakes. These stresses will not induce SCC because the stress caused by backfill is generally compressive stress and the stress caused by earthquakes is temporary in nature. The 316NG stainless steel inner barrier of the WP will also be excluded from the SCC evaluation because the SCC performance assessment will not take credit from the inner barrier. Therefore, the purpose of this document is to provide a detailed description of the process-level models that can be applied to assess the performance of the material (i.e., Alloy 22) used for the WP outer barrier subjected to the effects of SCC. As already mentioned in the development plan for the WP PMR (CRWMS M and O 1999e), this Analyses and Models Report (AMR) is to serve as a feed to the Waste Package Degradation (WPD) Total System Performance Assessment (TSPA) and Process Model Report (PMR).

  12. Electrochemical properties and stress corrosion cracking of alloys 600, 690, and 800 in solutions containing boric acid and chloride

    Energy Technology Data Exchange (ETDEWEB)

    Bae, J. H.; Won, C. H. [Chungnam Nation Univ., Taejon (Korea, Republic of); Lee, E. H.; Kim, H. P.; Kim, W. C. [KAERI, Taejon (Korea, Republic of)

    2000-10-01

    Electrochemical characteristics and stress corrosion cracking(SCC)of Alloy 600, Alloy 690 and Alloy 800 have been studied in boric acid solution with chloride. Electrochemical characteristics were measured in mixed solution of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C. SCC resistance was predicted with Parameter(P{sub SCC}) including current density ratio obtained at two different scan rates. P{sub SCC} increased with a following sequence: Alloy 600MA, 600TT, 690TT and Alloy 800. SCC test was carried out with C-ring specimens and reverse U-bend(RUB) specimens at 320 .deg. C and 350 .deg. C. Test solutions were mixture of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C and mixture of 27% H{sub 3}BO{sub 3} and 2g/l Cl{sup -} at 350 .deg. C. C-ring specimens test in the solution of 3% H{sub 3}BO{sub 3} and 0.2g/l Cl{sup -} at 320 .deg. C for 2400hrs did not show SCC. RUB specimen of Alloy600MA and 600TT showed SCC after 1920 hours exposure to the solution of 27% H{sub 3}BO{sub 3} and 0.2g/l Clat 350 .deg. C.

  13. Synergic Mechanism of an Organic Corrosion Inhibitor for Preventing Carbon Steel Corrosion in Chloride Solution

    Institute of Scientific and Technical Information of China (English)

    LIU Zhiyong; YU Lei; LI Qingzhong

    2015-01-01

    The inhibition effect of dimethylethanolamine (DMEA) and its composite with carboxylic acid was studied with the electrochemical tests. The experimental results indicate that DMEA is not a good inhibitor but the composite of DMEA with caprylic acid exhibits excellent inhibiting efficiency. The synergic mechanism of the organic corrosion inhibitors (OCIs) was studied with quantum chemical calculations. It is found that the DMEA forms a quaternary ammonium salt with the proton in carboxylic acid, and a cyclic complex formed between the salt and Fe may be responsible for the enhancement of inhibiting efficiency. The possible hydrogen bond formed between DMEA and carboxylic acid is not enough for the inhibiting effect. This work is helpful to proposing theoretical interpretation as well as developing a functional organic inhibitor to improve the durability of reinforced concrete contaminated with chloride.

  14. Modelling of Debond and Crack Propagation in Sandwich Structures Using Fracture and Damage Mechanics

    DEFF Research Database (Denmark)

    Berggreen, C.; Simonsen, Bo Cerup; Toernqvist, Rikard

    2003-01-01

    Skin-core de-bonding or core crack propagation will often be dominating mechanisms in the collapse modes of sandwich structures. This paper presents two different methods for prediction of crack propagation in a sandwich structure: a fracture mechanics approach, where a new mode-mix method...... is presented, and a local damage mechanics approach. The paper presents a real-life application example, where the superstructure in a vessel pulls the skin off the sandwich deck. The calculations show almost unstable crack growth initially followed by a stabilization, and a nearly linear relation between...

  15. The Impact of Cracked Microparticles on the Mechanical and the Fracture Behavior of Particulate Composite

    Directory of Open Access Journals (Sweden)

    Waleed K. Ahmed

    2015-10-01

    Full Text Available In this investigation a metallic composite with a cracked micro has been investigated using finite element method. Particulate reinforced composite is one of the most favorite composite due to it quit isotopic properties. While being in metallic status, the micro particles may be subjected to deterioration which lead to crack embedded initiation within the micro particle. This crack lead to degradation in the mechanical as well as the fracture behavior in the composite. Mechanical characteristics through estimating the stiffness of the composite has been studied for intact and cracked particles as well as for the fractured particles. It has been found that as long as the crack propagates in the micro particle, there is reduction in the composite stiffness and increases in the stress intensity factor (SIF.

  16. Generation mechanism of nonlinear ultrasonic Lamb waves in thin plates with randomly distributed micro-cracks.

    Science.gov (United States)

    Zhao, Youxuan; Li, Feilong; Cao, Peng; Liu, Yaolu; Zhang, Jianyu; Fu, Shaoyun; Zhang, Jun; Hu, Ning

    2017-08-01

    Since the identification of micro-cracks in engineering materials is very valuable in understanding the initial and slight changes in mechanical properties of materials under complex working environments, numerical simulations on the propagation of the low frequency S0 Lamb wave in thin plates with randomly distributed micro-cracks were performed to study the behavior of nonlinear Lamb waves. The results showed that while the influence of the randomly distributed micro-cracks on the phase velocity of the low frequency S0 fundamental waves could be neglected, significant ultrasonic nonlinear effects caused by the randomly distributed micro-cracks was discovered, which mainly presented as a second harmonic generation. By using a Monte Carlo simulation method, we found that the acoustic nonlinear parameter increased linearly with the micro-crack density and the size of micro-crack zone, and it was also related to the excitation frequency and friction coefficient of the micro-crack surfaces. In addition, it was found that the nonlinear effect of waves reflected by the micro-cracks was more noticeable than that of the transmitted waves. This study theoretically reveals that the low frequency S0 mode of Lamb waves can be used as the fundamental waves to quantitatively identify micro-cracks in thin plates. Copyright © 2017 Elsevier B.V. All rights reserved.

  17. Critical issues in De-alloying and transcrystalline stress-corrosion cracking. Progress report, March 1, 1991--February 28, 1992

    Energy Technology Data Exchange (ETDEWEB)

    Sieradzki, K.; Wagner, J.W.

    1992-03-01

    This report describes our progress since the last reporting reporting period (March 1991) and details the third year research plans on the program. The three major components of the program relate to (1) kinetic aspects of the selective dissolution in alloys and the coarsening of de-alloyed layers, (2) measurements of crack dynamics during film induced cleavage processes, and (3) mechanical properties of the intrinsic de-alloyed layers responsible for film-induced cleavage events. We discuss progress in each of these areas below.

  18. Effects of Surface State and Applied Stress on Stress Corrosion Cracking of Alloy 690TT in Lead-containing Caustic Solution

    Institute of Scientific and Technical Information of China (English)

    Zhiming Zhang; Jianqiu Wang; En-Hou Han; Wei Ke

    2012-01-01

    The effects of surface state and applied stress on the stress corrosion cracking (SCC) behaviors of thermally treated (TT) Alloy 690 in 10 wt% NaOH solution with 100 mg/L litharge at 330 ℃ were investigated using C-ring samples with four kinds of surface states and two different stress levels. Sample outer surfaces of the first three kinds were ground to 400 grit (ground), shot-peened (SP) and electro-polished (EP) and the last one was used as the as-received state. Two samples of every kind were stressed to 100% and 200% yield stress of Alloy 690TT, respectively. The results showed that the oxide film consisted of three layers whereas continuous layer rich in Cr was not found. The poor adhesive ability indicated that the oxide film could not protect the matrix from further corrosion. Lead was found in the oxide film and the oxides at the crack paths and accelerated the dissolution of thermodynamically unstable Cr in these locations and also in the matrix. The crack initiation and propagation on Alloy 690TT were effectively retarded by SP and EP treatments but were enhanced by grinding treatment, compared with the cracks on the as-received surface. The cracking severity was also enhanced by increasing the externally applied stress. The accelerated dissolution of Cr and the local tensile stress concentration in the near-surface layer caused by cold-working and higher applied stress reduced the SCC-resistance of Alloy 690TT in the studied solution.

  19. The mechanisms of cracks formation of silver-based contact materials under arc and making pressure

    Institute of Scientific and Technical Information of China (English)

    GUO Feng-yi(郭凤仪); CHEN Zhong-hua(陈忠华); ZHANG Ling-ling(张玲玲); ZHANG Ji-hua(张继华); FW Leuschner

    2004-01-01

    The arc erosion experiments on five kinds of silver-based contact materials, AgZnO (10), AgSnO2 (8.5) In2O3 (4), AgCdO (12), AgNi(10), AgWC(12)C(3) were carried out according to different breaking times, breaking currents, and making pressures. Then based on the theoretical analysis and the photographs taken by scanning electronic microscope with EDAX analyzer, the crack morphology was studied scientifically. Three types of cracks, which are cavity cracks, grain boundaries (or phase boundaries) slipping cracks, and thermal stress cracks, were put forward under arc and making pressure through establishing their physical models and discussing their formation mechanisms.

  20. Mechanical and Corrosion Properties of Magnesium-Bioceramic Nanocomposites

    Directory of Open Access Journals (Sweden)

    Kowalski K.

    2016-09-01

    Full Text Available Magnesium alloys have recently attracted much attention as a new generation of biodegradable metallic materials. In this work, Mg1Mn1Zn0.3Zr-bioceramic nanocomposites and their scaffolds were synthesized using a combination of mechanical alloying and a space-holder sintering process. The phase and microstructure analysis was carried out using X-ray diffraction, scanning electron microscopy and the properties were measured using hardness and corrosion testing equipment. Nanostructured Mg-bioceramic composites with a grain sizes below 73 nm were synthesized. The Vickers hardnesses for the bulk nanostructured Mg-based composites are two times greater than that of pure microcrystalline Mg metal (50 HV0.3. Produced Mg-based bionanomaterials can be applied in medicine.

  1. Assessment of susceptibility of Type 304 stainless steel to intergranular stress corrosion cracking in simulated Savannah River Reactor environments

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R.S.; Caskey, C.R. Jr.

    1989-12-01

    Intergranular stress corrosion cracking (IGSCC) of Type 304 stainless steel rate tests (CERT) of specimens machined was evaluated by constant extension from Savannah River Plant (SRP) decontaminated process water piping. Results from 12 preliminary CERT tests verified that IGSCC occurred over a wide range of simulated SRP envirorments. 73 specimens were tested in two statistical experimental designs of the central composite class. In one design, testing was done in environments containing hydrogen peroxide; in the other design, hydrogen peroxide was omitted but oxygen was added to the environment. Prediction equations relating IGSCC to temperature and environmental variables were formulated. Temperature was the most important independent variable. IGSCC was severe at 100 to 120C and a threshold temperature between 40C and 55C was identified below which IGSCC did not occur. In environments containing hydrogen peroxide, as in SRP operation, a reduction in chloride concentration from 30 to 2 ppB also significantly reduced IGSCC. Reduction in sulfate concentration from 50 to 7 ppB was effective in reducing IGSCC provided the chloride concentration was 30 ppB or less and temperature was 95C or higher. Presence of hydrogen peroxide in the environment increased IGSCC except when chloride concentration was 11 ppB or less. Actual concentrations of hydrogen peroxide, oxygen and carbon dioxide did not affect IGSCC. Large positive ECP values (+450 to +750 mV Standard Hydrogen Electrode (SHE)) in simulated SRP environments containing hydrogen peroxide and were good agreement with ECP measurements made in SRP reactors, indicating that the simulated environments are representative of SRP reactor environments. Overall CERT results suggest that the most effective method to reduce IGSCC is to reduce chloride and sulfate concentrations.

  2. Assessment of susceptibility of Type 304 stainless steel to intergranular stress corrosion cracking in simulated Savannah River Reactor environments

    Energy Technology Data Exchange (ETDEWEB)

    Ondrejcin, R.S.; Caskey, C.R. Jr.

    1989-12-01

    Intergranular stress corrosion cracking (IGSCC) of Type 304 stainless steel rate tests (CERT) of specimens machined was evaluated by constant extension from Savannah River Plant (SRP) decontaminated process water piping. Results from 12 preliminary CERT tests verified that IGSCC occurred over a wide range of simulated SRP envirorments. 73 specimens were tested in two statistical experimental designs of the central composite class. In one design, testing was done in environments containing hydrogen peroxide; in the other design, hydrogen peroxide was omitted but oxygen was added to the environment. Prediction equations relating IGSCC to temperature and environmental variables were formulated. Temperature was the most important independent variable. IGSCC was severe at 100 to 120C and a threshold temperature between 40C and 55C was identified below which IGSCC did not occur. In environments containing hydrogen peroxide, as in SRP operation, a reduction in chloride concentration from 30 to 2 ppB also significantly reduced IGSCC. Reduction in sulfate concentration from 50 to 7 ppB was effective in reducing IGSCC provided the chloride concentration was 30 ppB or less and temperature was 95C or higher. Presence of hydrogen peroxide in the environment increased IGSCC except when chloride concentration was 11 ppB or less. Actual concentrations of hydrogen peroxide, oxygen and carbon dioxide did not affect IGSCC. Large positive ECP values (+450 to +750 mV Standard Hydrogen Electrode (SHE)) in simulated SRP environments containing hydrogen peroxide and were good agreement with ECP measurements made in SRP reactors, indicating that the simulated environments are representative of SRP reactor environments. Overall CERT results suggest that the most effective method to reduce IGSCC is to reduce chloride and sulfate concentrations.

  3. Materials Reliability Program Resistance to Primary Water Stress Corrosion Cracking of Alloys 690, 52, and 152 in Pressurized Water Reactors (MRP-111)

    Energy Technology Data Exchange (ETDEWEB)

    Xu, H. [Framatome ANP, Inc., Lynchburg, VA (United States); Fyfitch, S. [Framatome ANP, Inc., Lynchburg, VA (United States); Scott, P. [Framatome ANP, SAS, Paris (France); Foucault, M. [Framatome ANP, SAS, Le Creusot (France); Kilian, R. [Framatome ANP, GmbH, Erlangen (Germany); Winters, M. [Framatome ANP, GmbH, Erlangen (Germany)

    2004-03-01

    Over the last thirty years, stress corrosion cracking in PWR primary water (PWSCC) has been observed in numerous Alloy 600 component items and associated welds, sometimes after relatively long incubation times. Repairs and replacements have generally utilized wrought Alloy 690 material and its compatible weld metals (Alloy 152 and Alloy 52), which have been shown to be very highly resistant to PWSCC in laboratory experiments and have been free from cracking in operating reactors over periods already up to nearly 15 years. It is nevertheless prudent for the PWR industry to attempt to quantify the longevity of these materials with respect to aging degradation by corrosion in order to provide a sound technical basis for the development of future inspection requirements for repaired or replaced component items. This document first reviews numerous laboratory tests, conducted over the last two decades, that were performed with wrought Alloy 690 and Alloy 52 or Alloy 152 weld materials under various test conditions pertinent to corrosion resistance in PWR environments. The main focus of the present review is on PWSCC, but secondary-side conditions are also briefly considered.

  4. stress corrosion cracking response of hand lay-up gry composites

    African Journals Online (AJOL)

    Dr Obe

    Nigerian Journal of Technology, Vol. 24, No. 1, March 2005 ... Department of Mechanical Engineering,. University of Nigeria ..... P.A.N Eme of the Department of Civil. Engineering ... Technology for Scientists and Engineers. Ellis Horwood ...

  5. Crack growth of 10M Ni-Mn-Ga material in cyclic mechanical loading

    Science.gov (United States)

    Aaltio, I.; Ge, Y.; Pulkkinen, H.; Sjöberg, A.; Söderberg, O.; Liu, X. W.; Hannula, S.-P.

    The 10M martensitic Ni-Mn-Ga single crystal materials are usually applied in the magneto-mechanical actuators. Therefore, it is important to know the possible effect of the long-term cyclic shape changes on their structure and behavior. This can be evaluated with the mechanical fatigue testing. In the present study, the single crystal 10M Ni-Mn-Ga samples of different compositions were applied to strain-controlled uniaxial mechanical cycling in the multivariant state at ambient temperature. The experiments revealed distinctive changes of the twin variant structure, especially in the mobile twin area, density of twin boundaries, and in the tendency for fatigue crack growth. Characterization of the crack surface showed that the cracks in the microscale grow in a step-wise manner on specific crystallographic planes, i.e, twin boundary planes, but that the macroscopic crack does not occur only along crystallographic directions.

  6. Effects of Variations in Salt-Spray Conditions on the Corrosion Mechanisms of an AE44 Magnesium Alloy

    Directory of Open Access Journals (Sweden)

    Holly J. Martin

    2010-01-01

    Full Text Available The understanding of how corrosion affects magnesium alloys is of utmost importance as the automotive and aerospace industries have become interested in the use of these lightweight alloys. However, the standardized salt-spray test does not produce adequate corrosion results when compared with field data, due to the lack of multiple exposure environments. This research explored four test combinations through three sets of cycles to determine how the corrosion mechanisms of pitting, intergranular corrosion, and general corrosion were affected by the environment. Of the four test combinations, Humidity-Drying was the least corrosive, while the most corrosive test condition was Salt Spray-Humidity-Drying. The differences in corrosivity of the test conditions are due to the various reactions needed to cause corrosion, including the presence of chloride ions to cause pit nucleation, the presence of humidity to cause galvanic corrosion, and the drying phase which trapped chloride ions beneath the corrosion by-products.

  7. The Corrosion and Corrosion Fatigue Behavior of Nickel Based Alloy Weld Overlay and Coextruded Claddings

    Science.gov (United States)

    Stockdale, Andrew

    The use of low NOx boilers in coal fired power plants has resulted in sulfidizing corrosive conditions within the boilers and a reduction in the service lifetime of the waterwall tubes. As a solution to this problem, Ni-based weld overlays are used to provide the necessary corrosion resistance however; they are susceptible to corrosion fatigue. There are several metallurgical factors which give rise to corrosion fatigue that are associated with the localized melting and solidification of the weld overlay process. Coextruded coatings offer the potential for improved corrosion fatigue resistance since coextrusion is a solid state coating process. The corrosion and corrosion fatigue behavior of alloy 622 weld overlays and coextruded claddings was investigated using a Gleeble thermo-mechanical simulator retrofitted with a retort. The experiments were conducted at a constant temperature of 600°C using a simulated combustion gas of N2-10%CO-5%CO2-0.12%H 2S. An alternating stress profile was used with a minimum tensile stress of 0 MPa and a maximum tensile stress of 300 MPa (ten minute fatigue cycles). The results have demonstrated that the Gleeble can be used to successfully simulate the known corrosion fatigue cracking mechanism of Ni-based weld overlays in service. Multilayer corrosion scales developed on each of the claddings that consisted of inner and outer corrosion layers. The scales formed by the outward diffusion of cations and the inward diffusion of sulfur and oxygen anions. The corrosion fatigue behavior was influenced by the surface finish and the crack interactions. The initiation of a large number of corrosion fatigue cracks was not necessarily detrimental to the corrosion fatigue resistance. Finally, the as-received coextruded cladding exhibited the best corrosion fatigue resistance.

  8. 氢腐蚀分层对换热器筒体承载能力的影响%Influence of bearing capacity of heat exchanger shell caused by hydrogen corrosion delaminating crack

    Institute of Scientific and Technical Information of China (English)

    何家胜; 李超; 朱晓明; 陈伟; 路远明; 杨峰

    2013-01-01

    To explore the influence of hydrogen corrosion delaminating crack on the mechanical properties and bearing capacity in operation of the layered heat exchanger shell, the material capability of layered heat exchanger shell was analyzed by using chemical constituents analysis, hardness test, tensile tests, Charpy V-notch pendulum impact test. The finite element method was used to calculate the stress distribution of heat exchanger shell and to discuss the stress intensity factors of crack tip. The results show that the Mn element is lower in the chemical constituents, other elements accord with the National Standards; the material hardness meets the requirements, but the toughness declines obviously. The material of heat layered exchanger shell is deteriorated by the hydrogen corrosion, which destroys the continuity and uniformity of the material, decreases the ultimate strength, but increases the yield-strength ratio. The film stress state is destroyed, and material resistance to crack growth decreases. The hydrogen corrosion delaminating crack causes biggish partial stress and makes bearing capacity of the heat exchanger shell decrease.%为了解换热器筒体发生氢腐蚀分层后,其简体局部材料的性能发生的变化及对换热器运行中的承载能力带来的影响,采用化学成分分析、硬度测试、拉伸试验、夏比V口冲击韧性试验等方法对换热器筒体材料的性能进行了分析;运用有限元分析方法计算了简体分层处的应力分布,并探讨了裂纹尖端应力强度因子的变化情况.研究结果表明:材料化学成分中除Mn元素的含量偏低外,其它元素含量符合国家标准;材料的硬度符合要求,材料的强度极限降低,屈强比上升,韧性明显降低.氢腐蚀分层使换热器筒体材料局部劣化,破坏了材料的均匀性和连续性,破坏了简体的薄膜应力状态,产生了较大的局部应力,使换热器筒体承载能力下降.

  9. Localized corrosion mechanism associated with precipitates containing Mg in Al alloys

    Institute of Scientific and Technical Information of China (English)

    2007-01-01

    To clarify the localized corrosion mechanism associated with precipitates containing Mg in Al alloys, the simulated bulk precipitates of S and β were synthesized through melting and casting. Their electrochemical behaviors and coupling behaviors with α(Al) in NaCl solution were measured. Meanwhile, simulated Al alloys containing S and β particles were prepared and their corrosion morphologies were observed. It's found that there exist two kinds of corrosion mechanisms associated with precipitates containing Mg. The precipitate of β is anodic to the alloy base, resulting in its anodic dissolution and corrosion during the whole corrosion process. While, there exists a corrosion conversion mechanism associated with the S precipitate, which contains active element Mg and noble element Cu simultaneously. At an initial stage, S is anodic to the alloy matrix at its periphery and the corrosion occurs on its surface. However, during its corrosion process, Mg is preferentially dissolved and noble Cu is enriched in the remnants.This makes S become cathodic to α(Al) and leads to anodic dissolution and corrosion on the alloy base at its periphery at a later stage.

  10. A phenomenological study of initiation and propagation of stress corrosion cracks. Application to AISI 304L stainless steel in magnesium chloride; Etude phenomenologique de l`amorcage et de la propagation de fissures de corrosion sous contraintes. Application a l`acier inoxydable Z 2CN 18.10 dans le chlorure de magnesium

    Energy Technology Data Exchange (ETDEWEB)

    Peyrat, C.; Raquet, O.; Helie, M.; Santarini, G. [CEA Fontenay-aux-Roses, 92 (France). Service de la Corrosion, d`Electrochimie et Chimie des Fluides

    1999-04-01

    A purely phenomenological study of Stress Corrosion Cracking (SCC) was performed using the couple AISI 304L austenitic stainless steel/boiling magnesium chloride aqueous solution. The exploitation of the morphological information (shape of the cracks and size distribution) available after constant elongation rate tests led to the apparent initiation of the cracks and to their growth rate. A law for the real initiation is proposed too and the elongation rate effect in quantitatively characterized. (authors) 8 refs.

  11. The Influence of Composition upon Surface Degradation and Stress Corrosion Cracking of the Ni-Cr-Mo Alloys in Wet Hydrofluoric Acid

    Energy Technology Data Exchange (ETDEWEB)

    Crook, P; Meck, N S; Rebak, R B

    2006-12-04

    At concentrations below 60%, wet hydrofluoric acid (HF) is extremely corrosive to steels, stainless steels and reactive metals, such as titanium, zirconium, and tantalum. In fact, only a few metallic materials will withstand wet HF at temperatures above ambient. Among these are the nickel-copper (Ni-Cu) and nickel-chromium-molybdenum (Ni-Cr-Mo) alloys. Previous work has shown that, even with these materials, there are complicating factors. For example, under certain conditions, internal attack and stress corrosion cracking (SCC) are possible with the Ni-Cr-Mo alloys, and the Ni-Cu materials can suffer intergranular attack when exposed to wet HF vapors. The purpose of this work was to study further the response of the Ni-Cr-Mo alloys to HF, in particular their external corrosion rates, susceptibility to internal attack and susceptibility to HF-induced SCC, as a function of alloy composition. As a side experiment, one of the alloys was tested in two microstructural conditions, i.e. solution annealed (the usual condition for materials of this type) and long-range ordered (this being a means of strengthening the alloy in question). The study of external corrosion rates over wide ranges of concentration and temperature revealed a strong beneficial influence of molybdenum content. However, tungsten, which is used as a partial replacement for molybdenum in some Ni-Cr-Mo alloys, appears to render the alloys more prone to internal attack. With regard to HF-induced SCC of the Ni-Cr-Mo alloys, this study suggests that only certain alloys (i.e., those containing tungsten) exhibit classical SCC. It was also discovered that high external corrosion rates inhibit HF-induced SCC, presumably due to rapid progression of the external attack front. With regard to the effects of long-range ordering, these were only evident at the highest test temperatures, where the ordered structure exhibited much higher external corrosion rates than the annealed structure.

  12. The Influence of Composition upon Surface Degradation and Stress Corrosion Cracking of the Ni-Cr-Mo Alloys in Wet Hydrofluoric Acid

    Energy Technology Data Exchange (ETDEWEB)

    Crook, P; Meck, N S; Rebak, R B

    2006-12-04

    At concentrations below 60%, wet hydrofluoric acid (HF) is extremely corrosive to steels, stainless steels and reactive metals, such as titanium, zirconium, and tantalum. In fact, only a few metallic materials will withstand wet HF at temperatures above ambient. Among these are the nickel-copper (Ni-Cu) and nickel-chromium-molybdenum (Ni-Cr-Mo) alloys. Previous work has shown that, even with these materials, there are complicating factors. For example, under certain conditions, internal attack and stress corrosion cracking (SCC) are possible with the Ni-Cr-Mo alloys, and the Ni-Cu materials can suffer intergranular attack when exposed to wet HF vapors. The purpose of this work was to study further the response of the Ni-Cr-Mo alloys to HF, in particular their external corrosion rates, susceptibility to internal attack and susceptibility to HF-induced SCC, as a function of alloy composition. As a side experiment, one of the alloys was tested in two microstructural conditions, i.e. solution annealed (the usual condition for materials of this type) and long-range ordered (this being a means of strengthening the alloy in question). The study of external corrosion rates over wide ranges of concentration and temperature revealed a strong beneficial influence of molybdenum content. However, tungsten, which is used as a partial replacement for molybdenum in some Ni-Cr-Mo alloys, appears to render the alloys more prone to internal attack. With regard to HF-induced SCC of the Ni-Cr-Mo alloys, this study suggests that only certain alloys (i.e., those containing tungsten) exhibit classical SCC. It was also discovered that high external corrosion rates inhibit HF-induced SCC, presumably due to rapid progression of the external attack front. With regard to the effects of long-range ordering, these were only evident at the highest test temperatures, where the ordered structure exhibited much higher external corrosion rates than the annealed structure.

  13. Fatigue Properties and Fracture Mechanism of Aluminum Alloy with Orifice Chamfer and Pre-corrosion Damage

    Directory of Open Access Journals (Sweden)

    ZHOU Song

    2016-06-01

    Full Text Available Fatigue fracture often occurs because of the corrosion damage to aerospace structural aluminum alloy with holes. Fatigue tests of 7075 aluminum alloy of both unchamfered and chamfered double-hole specimens under uncorrosion and 24h pre-corrosion were carried out. The influence of both pre-corrosion damage and orifice chamferer on fatigue properties and the differences of fatigue fracture characteristics were analyzed. The results show that the effect on fatigue life of pre-corrosion damage is significant. Median fatigue lives of both unchamfered and chamfered double-hole specimens under 24h pre-corrosion decrease about 31.74% and 26.92% compared with uncorrosion specimens. The orifice chamferer have a certain effect on fatigue life of both uncorrosion and 24h pre-corrosion specimens, with median fatigue lives decreased about 28.02% and 15.36% compared with unchamfered specimens, the main reason is due to the stress concentration after orifice chamfered, on the other hand, cutting marks lead to pre-damage during the orifice chamfering process which will result in an increase of the fatigue crack initiation sites and the fracture probability.

  14. The Dislocation Mechanism of Stress Corrosion Embrittlement in Ti-6Al-2Sn-4Zr-6Mo

    Science.gov (United States)

    Chapman, Tamara P.; Vorontsov, Vassili A.; Sankaran, Ananthi; Rugg, David; Lindley, Trevor C.; Dye, David

    2016-01-01

    An observation of the dislocation mechanisms operating below a naturally initiated hot-salt stress corrosion crack is presented, suggesting how hydrogen may contribute to embrittlement. The observations are consistent with the hydrogen-enhanced localized plasticity mechanism. Dislocation activity has been investigated through post-mortem examination of thin foils prepared by focused ion beam milling, lifted directly from the fracture surface. The results are in agreement with the existing studies, suggesting that hydrogen enhances dislocation motion. It is found that the presence of hydrogen in (solid) solution results in dislocation motion on slip systems that would not normally be expected to be active. A rationale is presented regarding the interplay of dislocation density and the hydrogen diffusion length.

  15. An Analytical Model for Fatigue Life Prediction Based on Fracture Mechanics and Crack Closure

    DEFF Research Database (Denmark)

    Ibsø, Jan Behrend; Agerskov, Henning

    1996-01-01

    Fatigue in steel structures subjected to stochastic loading is studied. Of special interest is the problem of fatigue damage accumulation and in this connection, a comparison between experimental results and results obtained using fracture mechanics. Fatigue test results obtained for welded plate...... test specimens are compared with fatigue life predictions using a fracture mechanics approach. In the calculation of the fatigue life, the influence of the welding residual stresses and crack closure on the fatigue crack growth is considered. A description of the crack closure model for analytical...... determination of the fatigue life is included. Furthermore, the results obtained in studies of the various parameters that have an influence on the fatigue life, are given. A very good agreement between experimental and analytical results is obtained, when the crack closure model is used in determination...

  16. The use of slow strain rate technique for studying stress corrosion cracking of an advanced silver-bearing aluminum-lithium alloy

    Science.gov (United States)

    Frefer, Abdulbaset Ali; Abosdell, Alajale M.; Raddad, Bashir S.

    2013-12-01

    In the present study, stress corrosion cracking (SCC) behavior of naturally aged advanced silver-bearing Al-Li alloy in NaCl solution was investigated using slow strain rate test (SSRT) method. The SSRT's were conducted at different strain rates and applied potentials at room temperature. The results were discussed based on percent reductions in tensile elongation in a SCC-causing environment over those in air tended to express the SCC susceptbility of the alloy under study at T3. The SCC behavior of the alloy was also discussed based on the microstructural and fractographic examinations.

  17. The use of slow strain rate technique for studying stress corrosion cracking of an advanced silver-bearing aluminum-lithium alloy

    Energy Technology Data Exchange (ETDEWEB)

    Frefer, Abdulbaset Ali; Raddad, Bashir S. [Department of Mechanical and Industrial Engineering/Tripoli University, Tripoli (Libya); Abosdell, Alajale M. [Department of Mechanical Engineering/Mergeb University, Garaboli (Libya)

    2013-12-16

    In the present study, stress corrosion cracking (SCC) behavior of naturally aged advanced silver-bearing Al-Li alloy in NaCl solution was investigated using slow strain rate test (SSRT) method. The SSRT’s were conducted at different strain rates and applied potentials at room temperature. The results were discussed based on percent reductions in tensile elongation in a SCC-causing environment over those in air tended to express the SCC susceptbility of the alloy under study at T3. The SCC behavior of the alloy was also discussed based on the microstructural and fractographic examinations.

  18. Technical Letter Report - Analysis of Ultrasonic Data on Piping Cracks at Ignalina Nuclear Power Plant Before and After Applying a Mechanical Stress Improvement Process, JCN-N6319, Task 2

    Energy Technology Data Exchange (ETDEWEB)

    Anderson, Michael T.; Cumblidge, Stephen E.; Crawford, Susan L.

    2008-02-26

    Pacific Northwest National Laboratory (PNNL) is assisting the United States Nuclear Regulatory Commission (NRC) in developing a position on the management of primary water stress corrosion cracking (PWSCC) in piping systems previously analyzed for leak-before-break (LBB). Part of this work involves determining whether inspections alone are sufficient or if inspections plus mitigation techniques are needed. The work described in this report addresses the reliability of ultrasonic phased-array (PA) examinations for inspection of cracks that have been subjected to the mitigation method of mechanical stress improvement process (MSIP). It is believed that stresses imparted during MSIP may make ultrasonic crack responses in piping welds more difficult to detect and accurately characterize. To explore this issue, data were acquired, both before and after applying MSIP, and analyzed from cracked areas in piping at the Ignalina Nuclear Power Plant (INPP) in Lithuania. This work was performed under NRC Project JCN-N6319, PWSCC in Leak-Before-Break Systems.

  19. Mechanism of Pitting Corrosion Protection of Metals and Alloys

    OpenAIRE

    Vladimir Alexandrovich Grachev; Andrei Evgenievich Rozen; Gennadii Vasilievich Kozlov; Andrei Andreievich Rozen

    2016-01-01

    In this article authors set out a principle of pitting corrosion protection, suggested a new class of multilayer materials with high corrosion resistance. They substantiated the choice of the layers for the multilayer material designed for exploitation in oxidizing and non-oxidizing environment. The sphere of application of the multilayer materials was defined.

  20. Microstructure and stress corrosion cracking of the fusion boundary region in an alloy 182-A533B low alloy steel dissimilar weld joint

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Juan [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan); State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, 62 Wencui Road, Shenyang 110016 (China); Peng, Qunjia, E-mail: qpeng@rift.mech.tohoku.ac.j [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan); Takeda, Yoichi; Kuniya, Jiro; Shoji, Tetsuo [Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579 (Japan)

    2010-12-15

    Research highlights: {yields} High-angle misorientation at FB, type-II and type-I boundaries. {yields} Highest residual strain and hardness in the zone between FB and type-II boundary. {yields} Type-II and type-I boundaries had lower resistance to SCC growth than the FB. {yields} Crack growth blunted by pitting at the FB. {yields} Reactivation of crack growth from the pitting by oxidation along the grain boundary. - Abstract: Stress corrosion cracking (SCC) in the fusion boundary (FB) region of an Alloy 182-A533B low alloy steel (LAS) dissimilar weld joint in high temperature water doped with sulfate was studied following a microstructure characterization of the FB region. The microstructure characterization suggested the type-II and type-I boundaries in the dilution zone (DZ) adjacent to the FB had lower resistance to SCC growth than the FB. Crack propagating perpendicular to the FB in the DZ was observed to be blunted by pitting at the FB, followed by the reactivation from the pitting by localized oxidation along the grain boundary in LAS.

  1. Mechanism of fracture in macro- and micro-scales in hollow centre cracked disc specimen

    Institute of Scientific and Technical Information of China (English)

    M. Eftekhari; A. Baghbanan; H. Hashemolhosseini; H. Amrollahi

    2015-01-01

    The hollow centre cracked disc (HCCD) specimen is one of the suggested alternative methods for determining the fracture toughness of rock. This work aims to investigate the fracture mechanism in HCCD in macro- and micro-scales using numerical methods, extended finite element method (X-FEM) and particle flow code (PFC) modeling, respectively. In the X-FEM, heaviside and near-tip enrichment functions are employed to consider the presence of the crack in the model. In PFC modeling the movement and interaction of stressed assemblies of rigid spherical particles are modeled using the distinct element method (DEM). A numerical code called MEX-FEM based on XFEM has been developed to simulate the problems involving crack. The models of pure modes I and II in macro-scale are simulated in micro-scale. The results show that dimensionless stress intensity factors (YI,YI) for pure modes I and II increase by increasing the crack length ratio. The angle at which the pure mode II occurs decreases by increasing the crack length ratio. In mixed mode I-II, The value ofYI decreases by increasing the crack angle, while the value ofYI increases to a given crack angle and then it decreases. Moreover, the fracture in micro-scale, unlike the macro-scale, includes a combination of different modes of fracturing.

  2. Mechanism of fracture in macro- and micro-scales in hollow centre cracked disc specimen

    Institute of Scientific and Technical Information of China (English)

    M.Eftekhari; A.Baghbanan; H.Hashemolhosseini; H.Amrollahi

    2015-01-01

    The hollow centre cracked disc(HCCD) specimen is one of the suggested alternative methods for determining the fracture toughness of rock. This work aims to investigate the fracture mechanism in HCCD in macro- and micro-scales using numerical methods, extended finite element method(X-FEM) and particle flow code(PFC) modeling, respectively. In the X-FEM, heaviside and near-tip enrichment functions are employed to consider the presence of the crack in the model. In PFC modeling the movement and interaction of stressed assemblies of rigid spherical particles are modeled using the distinct element method(DEM). A numerical code called MEX-FEM based on XFEM has been developed to simulate the problems involving crack. The models of pure modes I and Ⅱ in macro-scale are simulated in micro-scale. The results show that dimensionless stress intensity factors(YI, YⅡ) for pure modes I and Ⅱ increase by increasing the crack length ratio. The angle at which the pure mode Ⅱ occurs decreases by increasing the crack length ratio. In mixed mode I-Ⅱ, The value of YI decreases by increasing the crack angle, while the value of YⅡ increases to a given crack angle and then it decreases. Moreover, the fracture in micro-scale, unlike the macro-scale, includes a combination of different modes of fracturing.

  3. Early Age Fracture Mechanics and Cracking of Concrete

    DEFF Research Database (Denmark)

    Østergaard, Lennart

    2003-01-01

    Modern high performance concretes have low water cement ratios and do often include silica fume. Also early age high strength cements are often applied and when all these factors sum up, it turns out that the cracking sensibility is dramatically increased in com- parison with ordinary concrete...... if applied in early age. The results are only valid after 24 hours for fast and normal hardening cements and after 48 hours for slow hardening cements. This is con¯rmed in a finite element model. The fracture properties of early age concrete have been determined. The framework of the investigations has been...

  4. Effect of Stress Ratio and Loading Frequency on the Corrosion Fatigue Behavior of Smooth Steel Wire in Different Solutions

    Directory of Open Access Journals (Sweden)

    Songquan Wang

    2016-09-01

    Full Text Available In this work, the effects of loading condition and corrosion solution on the corrosion fatigue behavior of smooth steel wire were discussed. The results of polarization curves and weight loss curves showed that the corrosion of steel wire in acid solution was more severe than that in neutral and alkaline solutions. With the extension of immersion time in acid solution, the cathodic reaction of steel wire gradually changed from the reduction of hydrogen ion to the reduction of oxygen, but was always the reduction of hydrogen ion in neutral and alkaline solutions. The corrosion kinetic parameters and equivalent circuits of steel wires were also obtained by simulating the Nyquist diagrams. In corrosion fatigue test, the effect of stress ratio and loading frequency on the crack initiation mechanism was emphasized. The strong corrosivity of acid solution could accelerate the nucleation of crack tip. The initiation mechanism of crack under different conditions was summarized according to the side and fracture surface morphologies. For the crack initiation mechanism of anodic dissolution, the stronger the corrosivity of solution was, the more easily the fatigue crack source formed, while, for the crack initiation mechanism of deformation activation, the lower stress ratio and higher frequency would accelerate the generation of corrosion fatigue crack source.

  5. Fretting corrosion of CoCr alloy: Effect of load and displacement on the degradation mechanisms.

    Science.gov (United States)

    Bryant, Michael; Neville, Anne

    2017-02-01

    Fretting corrosion of medical devices is of growing concern, yet, the interactions between tribological and electrochemical parameters are not fully understood. Fretting corrosion of CoCr alloy was simulated, and the components of damage were monitored as a function of displacement and contact pressure. Free corrosion potential (Ecorr), intermittent linear polarisation resistance and cathodic potentiostatic methods were used to characterise the system. Interferometry was used to estimate material loss post rubbing. The fretting regime influenced the total material lost and the dominant degradation mechanism. At high contact pressures and low displacements, pure corrosion was dominant with wear and its synergies becoming more important as the contact pressure and displacement decreased and increased, respectively. In some cases, an antagonistic effect from the corrosion-enhanced wear contributor was observed suggesting that film formation and removal may be present. The relationship between slip mechanism and the contributors to tribocorrosion degradation is presented.

  6. Numerical Computation of Stress Intensity Factors for Bolt-hole Corner Crack in Mechanical Joints

    Institute of Scientific and Technical Information of China (English)

    Wang Liqing; Gai Bingzheng

    2008-01-01

    The three-dimensional finite element method is used to solve the problem of the quarter-elliptical comer crack of the bolt-hole in mechanical joints being subjected to remote tension. The square-root stress singularity around the corner crack front is simulated using the collapsed 20-node quarter point singular elements. The contact interaction between the bolt and the hole boundary is considered in the finite element analysis. The stress intensity factors (SIFs) along the crack front are evaluated by using the displacement correlation technique. The effects of the amount of clearance between the hole and the bolt on the SIFs are investigated. The numerical results indicate that the SIF for mode I decrease with the decreases in clearance, and in the cases of clearance being present, the corner crack is in a mix-mode, even if mode I loading is dominant.

  7. Thermo-mechanical cracking of a new and laser repair welded die casting die

    Directory of Open Access Journals (Sweden)

    D. Klobčar

    2012-07-01

    Full Text Available The paper presents the analysis of thermo-mechanical fatigue cracking of die casting die during industrial use. An innovative, production friendly approach to monitor the surface crack dimensions was introduced, which is based on measuring defect-fin on the casting part. A new four moulds die casting die was monitored 40 000 cycles in order to complete the production series. The production was stopped three times for laser repair welding of cracks since the defect-fins were not acceptable. The defect-fin heights were measured every 1 000 cycles on the castings before and after repair welding of die surface cracks. The in-service die life can be prolonged with laser repair welding for several times, even thought that in-service die life for a particular repair varies.

  8. Fracture Mechanics for a Mode Ⅲ Crack in a Piezoelectromagnetic Material

    Institute of Scientific and Technical Information of China (English)

    2005-01-01

    Analytical solutions for a Griffith crack inside an infinite piezoelectromagnetic medium under combined mechanical-electrical-magnetic loadings are formulated using integral transform method. The singular stress, electric and magnetic fields in the piezoelectromagnetic material are obtained by the theory of linear piezoelectromagneticity. Fourier transforms are used to reduce the mixed boundary value problems of the crack, which is assumed to be permeable, to dual integral equations. The solution of the dual integral equations is then expressed analytically. Expressions for strains, stresses, electric fields, electric displacements, magnetic fields and magnetic inductions in the vicinity of the crack tip are derived. Field intensity factors and energy release rate for piezoelectromagnetic material are obtained. The stresses, electric displacements and magnetic inductions at the crack tip show the traditional square root singularities; and the electric field intensity factor (EFIF) and the magnetic field intensity factor (MFIF) are always zero.

  9. Application of damage mechanics modeling to strain based design with respect to ductile crack initiation

    Energy Technology Data Exchange (ETDEWEB)

    Ishikawa, Nobuyuki; Sueyoshi, Hitoshi; Igi, Satoshi [Steel Research Laboratory, JFE Steel Corporation (Japan)

    2010-07-01

    In the oil and gas sector, with the increase in demand, more and more pipelines are now constructed in permafrost and seismic regions. When installed in such harsh environments, pipelines must be resistant to buckling and weld fracture and the strain based design methodology is preferably used. The aim of this paper is to study the critical condition for ductile crack initiation. Both notched round bar and wide plate tests were carried out on X80 and X100 steel pipes and welds; the equivalent plastic strain criterion and Gurson Tvergaard mechanical damage analysis were used. It was found that to determine ductile crack initiation that is not affected by specimen geometry, the critical equivalent plastic strain can be used as the local criterion. In addition, when ductile crack initiation is independent of specimen geometry, the void volume fraction can be used as a criterion. This paper provided useful information on which criterion to use for ductile crack initiation.

  10. Mechanics of finite cracks in dissimilar anisotropic elastic media considering interfacial elasticity

    Science.gov (United States)

    Juan, Pierre-Alexandre; Dingreville, Rémi

    2017-02-01

    Interfacial crack fields and singularities in bimaterial interfaces (i.e., grain boundaries or dissimilar materials interfaces) are considered through a general formulation for two-dimensional (2-D) anisotropic elasticity while accounting for the interfacial structure by means of an interfacial elasticity paradigm. The interfacial elasticity formulation introduces boundary conditions that are effectively equivalent to those for a weakly bounded interface. This formalism considers the 2-D crack-tip elastic fields using complex variable techniques. While the consideration of the interfacial elasticity does not affect the order of the singularity, it modifies the oscillatory effects associated with problems involving interface cracks. Constructive or destructive "interferences" are directly affected by the interface structure and its elastic response. This general formulation provides an insight on the physical significance and the obvious coupling between the interface structure and the associated mechanical fields in the vicinity of the crack tip.

  11. Degradation mechanism of rock under impact loadings by integrated investigation on crack and damage development

    Institute of Scientific and Technical Information of China (English)

    周子龙; 江益辉; 邹洋; 翁磊

    2014-01-01

    Failure of rock under impact loadings involves complex micro-fracturing and progressive damage. Strength increase and splitting failure have been observed during dynamic tests of rock materials. However, the failure mechanism still remains unclear. In this work, based on laboratory tests, numerical simulations with the particle flow code (PFC) were carried out to reproduce the micro-fracturing process of granite specimens. Shear and tensile cracks were both recorded to investigate the failure mode of rocks under different loading conditions. At the same time, a dynamic damage model based on the Weibull distribution was established to predict the deformation and degradation behavior of specimens. It is found that micro-cracks play important roles in controlling the dynamic deformation and failure process of rock under impact loadings. The sharp increase in the number of cracks may be the reason for the strength increase of rock under high strain rates. Tensile cracks tend to be the key reason for splitting failure of specimens. Numerical simulation of crack propagation by PFC can give vivid description of the failure process. However, it is not enough for evaluation of material degradation. The dynamic damage model is able to predict the stress−strain relationship of specimens reasonably well, and can be used to explain the degradation of specimens under impact loadings at macro-scale. Crack and damage can describe material degradation at different scales and can be used together to reveal the failure mechanism of rocks.

  12. Investigation of the Use of Laser Shock Peening for Enhancing Fatigue and Stress Corrosion Cracking Resistance of Nuclear Energy Materials

    Energy Technology Data Exchange (ETDEWEB)

    Vasudevan, Vijay K. [Univ. of Cincinnati, OH (United States); Jackson, John [Idaho National Lab. (INL), Idaho Falls, ID (United States); Teysseyre, Sebastien [Idaho National Lab. (INL), Idaho Falls, ID (United States); Alexandreanu, Bogdan [Argonne National Lab. (ANL), Argonne, IL (United States); Chen, Yiren [Argonne National Lab. (ANL), Argonne, IL (United States)

    2017-03-07

    The objective of this project, which includes close collaboration with scientists from INL and ANL, is to investigate and demonstrate the use of advanced mechanical surface treatments like laser shock peening (LSP) and ultrasonic nanocrystal surface modification (UNSM) and establish baseline parameters for enhancing the fatigue properties and SCC resistance of nuclear materials like nickel-based alloy 600 and 304 stainless steel. The research program includes the following key elements/tasks: 1) Procurement of Alloy 600 and 304 SS, heat treatment studies; 2) LSP and UNSM processing of base metal and welds/HAZ of alloys 600 and 304; (3) measurement and mapping of surface and sub-surface residual strains/stresses and microstructural changes as a function of process parameters using novel methods; (4) determination of thermal relaxation of residual stresses (macro and micro) and microstructure evolution with time at high temperatures typical of service conditions and modeling of the kinetics of relaxation; (5) evaluation of the effects of residual stress, near surface microstructure and temperature on SCC and fatigue resistance and associated microstructural mechanisms; and (6) studies of the effects of bulk and surface grain boundary engineering on improvements in the SCC resistance and associated microstructural and cracking mechanisms

  13. Three-Dimensional Problems in the Dynamic Fracture Mechanics of Materials with Interface Cracks (Review)

    Science.gov (United States)

    Guz, A. N.; Guz, I. A.; Men'shikov, A. V.; Men'shikov, V. A.

    2013-01-01

    Three-dimensional problems in the dynamic fracture mechanics of materials with interface cracks are considered as nonclassical problems of fracture mechanics. Physically correct results in fracture mechanics in the case where the interaction of the crack edges must be taken into account are analyzed. The linear (classical) and nonlinear (nonclassical) problems of dynamic fracture mechanics for materials with interface cracks are formulated using the above approaches. A method for solving three-dimensional linear dynamic problems based on boundary integral equations for piecewise-homogeneous materials and the boundary-element method is outlined. This method can be used for incremental solution of nonlinear problems. The method involves the regularization of hypersingular integrals. New classes of three-dimensional linear dynamic problems for circular and elliptic interface cracks are solved. Numerical values of stress intensity factors obtained with the linear problem formulation are the first step toward calculating them in the nonlinear formulation. The first results obtained in solving nonlinear dynamic problems for interface cracks with interacting faces are briefly analyzed

  14. Aluminum alloy weldability. Identification of weld solidification cracking mechanisms through novel experimental technique and model development

    Energy Technology Data Exchange (ETDEWEB)

    Coniglio, Nicolas

    2008-07-01

    The objective of the present thesis is to make advancements in understanding solidification crack formation in aluminum welds, by investigating in particular the aluminum 6060/4043 system. Alloy 6060 is typical of a family of Al-Mg-Si extrusion alloys, which are considered weldable only when using an appropriate filler alloy such as 4043 (Al-5Si). The effect of 4043 filler dilution (i.e. weld metal silicon content) on cracking sensitivity and solidification path of Alloy 6060 welds are investigated. Afterwards, cracking models are developed to propose mechanisms for solidification crack initiation and growth. Cracking Sensitivity. Building upon the concept that silicon improves weldability and that weldability can be defined by a critical strain rate, strain rate-composition combinations required for solidification crack formation in the Al- 6060/4043 system were determined using the newly developed Controlled Tensile Weldability (CTW) test utilizing local strain extensometer measurements. Results, presented in a critical strain rate - dilution map, show a crack - no crack boundary which reveals that higher local strain rates require higher 4043 filler dilution to avoid solidification cracking when arc welding Alloy 6060. Using the established crack - no crack boundary as a line of reference, additional parameters were examined and their influence on cracking characterized. These parameter influences have included studies of weld travel speed, weld pool contaminants (Fe, O, and H), and grain refiner additions (TiAl{sub 3} + Boron). Each parameter has been independently varied and its effect on cracking susceptibility quantified in terms of strain rate - composition combinations. Solidification Path. Solidification path of the Al-6060/4043 system was characterized using thermal analysis and phase identification. Increasing 4043 filler dilution from 0 to 16% in Alloy 6060 arc welds resulted in little effect on thermal arrests and microstructure, no effect on

  15. Contribution of the low cycle fatigue on ultra high purity Ni-Cr-Fe alloys and on Ni monocrystals to the understanding of the hydrogen role in stress corrosion cracking for the alloys 600 and 690; Apport de la fatigue oligocyclique sur alliages Ni-Cr-Fe d'ultra haute purete et sur monocristaux de Ni a la comprehension sous contrainte des alliages 600 et 69O

    Energy Technology Data Exchange (ETDEWEB)

    Renaudot, N

    1999-06-01

    We discuss the role of hydrogen in cracking of Ni base alloys used for pressurised water reactor (PWR) primary tubes (alloy 600 and 690). Cracking can be explained by a Stress Corrosion Cracking (SCC) phenomenon. For this purpose, Low cycle fatigue (R = - 1) under cathodic charging at room temperature is conducted to study hydrogen effects on propagation of cracks mechanically initiated by the formation of Persistent Slip Bands (PSB). Low cycle fatigue on Ultra High Purity specimens (Ni, alloy 600 and 690) reveals the very important hydrogen effect on crack propagation rate, whatever the Cr content in the Ni base alloy. If Cr seems to have an effect over-hydrogen penetration in specimens (by a protective film formation), it have no beneficial effect when hydrogen have diffused ahead of a crack tip. Propagation rates (transgranular or intergranular) are highly increased, no matter of the absence of impurities like sulphur. Then, in PWR, the difference in the behaviour of alloy 600 and 690 could be due to a slower microcrack propagation rate for alloy 690. Protective films could play an important role in this difference, which is to study. Low cycle fatigue on Ni single crystals oriented for single slip shows, for the first time on bulk specimen, a macroscopic softening which can be explained. by hydrogen-dislocation interactions. Moreover, a simple quantitative model based on these interactions results in the same softening as the one observed experimentally. These results allow to validate experimentally one of the most important steps in the 'Corrosion Enhanced Plasticity (CEP) model', i.e. the softening ahead of a stress corrosion crack tip by hydrogen dislocation interactions. This is of importance because this model can explain cracking in numerous FCC materials-environment couple. (author)

  16. White-Etching Matter in Bearing Steel. Part I: Controlled Cracking of 52100 Steel

    Science.gov (United States)

    Solano-Alvarez, W.; Bhadeshia, H. K. D. H.

    2014-10-01

    Although most of the research performed in bearing steel metallurgy aims to prevent crack nucleation and propagation, some applications require the exact opposite in order to study the role that disconnected surfaces inside the bulk material play when load is applied, or when fluids entrapped in surface cracks propagate tensile stresses or exacerbate corrosion. Four heat treatments have been designed to create controlled arrays of crack types and distributions in quenched and untempered steel normally used in the manufacture of bearings. The varieties of cracks studied include sparsely distributed martensite-plate cracks, fine-grain-boundary cracks, abundant martensite-plate cracks, and surface cracks. The intention was to create samples which can then be subjected to appropriate mechanical testing so that phenomena such as the appearance of "white-etching areas" or "white-etching cracks," crack-lubricant interactions, or hydrogen trapping can be studied further.

  17. Mimic-biology research on self-recovering mechanism of cavity-type crack

    Institute of Scientific and Technical Information of China (English)

    YUAN; Chaolong; (袁朝龙); ZHONG; Yuexian; (钟约先); MA; Qingxian; (马庆贤); CAO; Qixiang; (曹起骧)

    2002-01-01

    Modeling method was used to research the recovering law of inner cavity-type cracks during the processes of high-temperature plastic deformation. It was found that the self-recovering of cavity-type fault was similar to the self-healing of wound of skin and fracture. The self-recovering process of cavity-type fault was investigated according to the rule of self-healing of wound in human body. The recrystallization mechanism of self-recovering of cavity-type fault was discovered. A new method is presented to study the self-recovering mechanism of cavity-type cracks.

  18. Study on Microstructure and Slag Corrosion Mechanism of High Chrome Bricks for Gasifier

    Institute of Scientific and Technical Information of China (English)

    2006-01-01

    Research was focused on slag corrosion mechanism of high chrome bricks used for different types of gasifier by comparing the structure of high chrome bricks for petroleum coke gasifier and water-coal slurry gasifier with slag corroded testing brick and water coal slurry gasifier through Scanning Electron Microscope (SEM) examination and X-ray diffraction. Results show that for high chrome brick used for petroleum coke gasifier, corrosion is mainly caused by Cr2O3 in the brick and V2O5 in molten slag and liquid phase generation at low temperature; for high chrome brick used for water-coal slurry gasifier, corrosion is caused by dissolution of Cr2O3 in molten slag and corrosion of ZrO2. For LIRR-HK95 brick, it performs better petroleum coke corrosion resistance than the others due to the optimal composition and structure.

  19. Standard test method for evaluating stress-corrosion cracking of stainless alloys with different nickel content in boiling acidified sodium chloride solution

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2000-01-01

    1.1 This test method describes a procedure for conducting stress-corrosion cracking tests in an acidified boiling sodium chloride solution. This test method is performed in 25% (by mass ) sodium chloride acidified to pH 1.5 with phosphoric acid. This test method is concerned primarily with the test solution and glassware, although a specific style of U-bend test specimen is suggested. 1.2 This test method is designed to provide better correlation with chemical process industry experience for stainless steels than the more severe boiling magnesium chloride test of Practice G36. Some stainless steels which have provided satisfactory service in many environments readily crack in Practice G36, but have not cracked during interlaboratory testing using this sodium chloride test method. 1.3 This boiling sodium chloride test method was used in an interlaboratory test program to evaluate wrought stainless steels, including duplex (ferrite-austenite) stainless and an alloy with up to about 33% nickel. It may also b...

  20. Mechanism of hydrogen-induced intergranular cracking of tubular steels

    Institute of Scientific and Technical Information of China (English)

    乔利杰; 褚武扬; 于广华; 程以环

    1996-01-01

    Hydrogen could be enriched on grain boundaries by stress induction and other traps.The enriched hydrogen facilitated emission and movement of dislocations and lowered plastic work.Consequently,fracture occurred easily along grain boundary.A normalized threshold value of hydrogen-induced cracking (HIC) along grain boundary is given as (KIH/KIC)2=1-0.162×10-3 βHCc(H)GH/(2γs-γb-0.16×103∑β CiGi),where βH and βi are the enrichment factors of hydrogen and other elements on grain boundaries,respectively;Cc(H) is hydrogen concentration induced by stress;C,is the average concentration of an element in the steel;GH and Gi are factors of fracture work along grain boundary with hydrogen and other elements,and γs and γb are surface free energy and grain boundary energy of Fe.For tubular steel,the calculated KH/KIC is 0.23 while the determined value is 0.26.The theoretical threshold value is well consistent with the experimental one.

  1. Innovative Approach to Establish Root Causes for Cracking in Aggressive Reactor Environments

    Energy Technology Data Exchange (ETDEWEB)

    Bruemmer, Stephen M.; Thomas, Larry E.; Vetrano, John S.; Simonen, Edward P.

    2003-10-31

    The research focuses on the high-resolution characterization of degradation microstructures and microchemistries in specimens tested under controlled conditions for the environment and for the material where in-service complexities can be minimized. Thermodynamic and kinetic modeling of crack-tip processes is employed to analyze corrosion-induced structures and gain insights into degradation mechanisms. Novel mechanistic ''fingerprinting'' of crack-tip structures is used to isolate causes of environmental cracking in tandem with quantitative measurements of crack growth. Sample preparation methods and advanced analytical techniques are used to characterize corrosion/oxidation reactions and crack-tip structures at near atomic dimensions in order to gain insight into fundamental environmental cracking mechanisms. Reactions at buried interfaces, not accessible by conventional approaches, are being systematically interrogated. Crack-growth experiments in high-temperature water environments are evaluating and isolating the effects of material condition (matrix strength, grain boundary composition and precipitation) on stress corrosion cracking (SCC). The fundamental understanding of crack advance mechanisms will establish the basis to design new corrosion-resistant alloys for current light-water reactors and advanced reactor systems.

  2. Fracture mechanics of materials under compression along cracks (survey). Structural materials

    Science.gov (United States)

    Guz', A. N.; Nazarenko, V. M.

    1989-10-01

    The results elucidated in this paper and in [A. N. Guz' and V. M. Nazarenko, "Fracture mechanics of materials under compression along cracks (Survey). Highly-elastic material," Prikl. Mekh., 25, No. 9, 3-32 (1989)] of investigations on compression of materials along defects of crack type are exact since they are obtained within the framework of rigorous three-dimensional linearized formulations. Let us note that the fact that the mentioned result are standards for approximate approaches is of independent value. The investigations performed whose survey is represented above should be considered the beginning of a study of problems of material fracture under compression along cracks in a rigorous formulation (within the framework of the linearized mechanics of deformable bodies).

  3. An Analytical Model for Fatigue Life Prediction Based on Fracture Mechanics and Crack Closure

    DEFF Research Database (Denmark)

    Ibsø, Jan Behrend; Agerskov, Henning

    1996-01-01

    Fatigue in steel structures subjected to stochastic loading is studied. Of special interest is the problem of fatigue damage accumulation and in this connection, a comparison between experimental results and results obtained using fracture mechanics. Fatigue test results obtained for welded plate...... test specimens are compared with fatigue life predictions using a fracture mechanics approach. In the calculation of the fatigue life, the influence of the welding residual stresses and crack closure on the fatigue crack growth is considered. A description of the crack closure model for analytical...... of the analytical fatigue lives. Both the analytical and experimental results obtained show that the Miner rule may give quite unconservative predictions of the fatigue life for the types of stochastic loading studied....

  4. 钢筋锈胀引发混凝土保护层开裂破坏的细观数值研究%Meso-scale numerical study on cracking of concrete cover due to steel reinforcement corrosion

    Institute of Scientific and Technical Information of China (English)

    杜修力; 金浏

    2015-01-01

    钢筋锈蚀膨胀引起保护层混凝土开裂是影响钢筋混凝土结构耐久性和服役寿命的重要因素。考虑到混凝土细观结构组成对保护层破坏模式的影响,从细观角度出发,将混凝土看作由骨料、砂浆基质及两者间界面过渡区组成的三相复合材料,建立了描述钢筋锈胀力学行为的混凝土随机骨料模型。采用塑性损伤本构关系模型来表征砂浆基质和过渡区界面的力学行为,假定钢筋均匀锈蚀,对钢筋锈胀引起的混凝土保护层开裂破坏过程进行了细观数值研究。对比了宏观均匀模型与细观非均质模型下获得的保护层破坏模式,探讨了径厚比(c/d)、钢筋位置(中部和角区)及混凝土拉伸强度对保护层破坏模式及保护层胀裂时钢筋锈蚀水平的影响,得到了一些有益结论。%Concrete cover cracking induced by corrosion of steel reinforcement is a major influencing factor for durability and service-ability of reinforced concrete (RC)structures.Here in the study,the influence of concrete meso-structure on the failure pattern of concrete cover is accounted for.At the meso-scale, the concrete is assumed to be a three-phase composite composed of aggregate,mortar matrix and the interfacial transition zone (ITZ).A random aggregate structure of concrete is established for the study on the mechanical behavior of cover subjected to corrosion expansion of steel reinforcement.In the simulations,the plasticity damaged model is used to describe the mechanical behavior of the mortar matrix and the ITZ,and it is assumed that the corrosion of steel reinforcement is uniform.Based on the above assumptions,the cracking of concrete cover due to steel reinforcement corrosion is numerically simulated.The failure patterns obtained from the macro-scale homogeneous model and the present meso-scale heterogeneous model are compared.The effects of the ratio of cover thickness and reinforce-ment diameter (i

  5. Ultrasensitive mechanical crack-based sensor inspired by the spider sensory system.

    Science.gov (United States)

    Kang, Daeshik; Pikhitsa, Peter V; Choi, Yong Whan; Lee, Chanseok; Shin, Sung Soo; Piao, Linfeng; Park, Byeonghak; Suh, Kahp-Yang; Kim, Tae-il; Choi, Mansoo

    2014-12-11

    Recently developed flexible mechanosensors based on inorganic silicon, organic semiconductors, carbon nanotubes, graphene platelets, pressure-sensitive rubber and self-powered devices are highly sensitive and can be applied to human skin. However, the development of a multifunctional sensor satisfying the requirements of ultrahigh mechanosensitivity, flexibility and durability remains a challenge. In nature, spiders sense extremely small variations in mechanical stress using crack-shaped slit organs near their leg joints. Here we demonstrate that sensors based on nanoscale crack junctions and inspired by the geometry of a spider's slit organ can attain ultrahigh sensitivity and serve multiple purposes. The sensors are sensitive to strain (with a gauge factor of over 2,000 in the 0-2 per cent strain range) and vibration (with the ability to detect amplitudes of approximately 10 nanometres). The device is reversible, reproducible, durable and mechanically flexible, and can thus be easily mounted on human skin as an electronic multipixel array. The ultrahigh mechanosensitivity is attributed to the disconnection-reconnection process undergone by the zip-like nanoscale crack junctions under strain or vibration. The proposed theoretical model is consistent with experimental data that we report here. We also demonstrate that sensors based on nanoscale crack junctions are applicable to highly selective speech pattern recognition and the detection of physiological signals. The nanoscale crack junction-based sensory system could be useful in diverse applications requiring ultrahigh displacement sensitivity.

  6. Ultrasensitive mechanical crack-based sensor inspired by the spider sensory system

    Science.gov (United States)

    Kang, Daeshik; Pikhitsa, Peter V.; Choi, Yong Whan; Lee, Chanseok; Shin, Sung Soo; Piao, Linfeng; Park, Byeonghak; Suh, Kahp-Yang; Kim, Tae-Il; Choi, Mansoo

    2014-12-01

    Recently developed flexible mechanosensors based on inorganic silicon, organic semiconductors, carbon nanotubes, graphene platelets, pressure-sensitive rubber and self-powered devices are highly sensitive and can be applied to human skin. However, the development of a multifunctional sensor satisfying the requirements of ultrahigh mechanosensitivity, flexibility and durability remains a challenge. In nature, spiders sense extremely small variations in mechanical stress using crack-shaped slit organs near their leg joints. Here we demonstrate that sensors based on nanoscale crack junctions and inspired by the geometry of a spider's slit organ can attain ultrahigh sensitivity and serve multiple purposes. The sensors are sensitive to strain (with a gauge factor of over 2,000 in the 0-2 per cent strain range) and vibration (with the ability to detect amplitudes of approximately 10 nanometres). The device is reversible, reproducible, durable and mechanically flexible, and can thus be easily mounted on human skin as an electronic multipixel array. The ultrahigh mechanosensitivity is attributed to the disconnection-reconnection process undergone by the zip-like nanoscale crack junctions under strain or vibration. The proposed theoretical model is consistent with experimental data that we report here. We also demonstrate that sensors based on nanoscale crack junctions are applicable to highly selective speech pattern recognition and the detection of physiological signals. The nanoscale crack junction-based sensory system could be useful in diverse applications requiring ultrahigh displacement sensitivity.

  7. Corrosion resistant iron aluminides exhibiting improved mechanical properties and corrosion resistance

    Science.gov (United States)

    Liu, Chain T.; McKamey, Claudette G.; Tortorelli, Peter F.; David, Stan A.

    1994-01-01

    The specification discloses a corrosion-resistant intermetallic alloy comprising, in atomic percent, an FeAl iron aluminide containing from about 30 to about 40% aluminum alloyed with from about 0.01 to 0.4% zirconium and from 0.01 to about 0.8% boron. The alloy exhibits considerably improved room temperature ductility for enhanced usefulness in structural applications. The high temperature strength and fabricability is improved by alloying with molybdenum, carbon, chromium and vanadium.

  8. Effects of La2O3 on Mechanical Properties and Corrosion Resistance of H62 Brass

    Science.gov (United States)

    Wu, Xiangwei; Luo, Hong; Sheng, Meng; Liu, Huanchao; Xiao, Zhen; Geng, Haoran

    2017-02-01

    In this article, the effects of lanthanum oxide (La2O3) on the microstructure and mechanical properties of H62 brass were investigated by using the universal testing machine, Brinell hardness tester, optical microscope, and scanning electron microscope (SEM). Immersion corrosion and electrochemical measurements were carried out to identify the influence of La2O3 on the corrosion behavior of the H62 brass. The phase constitution, microstructure, and phase composition of the H62 brass were analyzed by x-ray diffraction, SEM, and energy-dispersive spectrometer, respectively. The results show that the microstructure of α phase changes from dendrite grains to equiaxed grains, and the content and distribution of β phase are improved significantly. When the La2O3 content reaches 0.8 wt.%, the H62 brass obtains favorable comprehensive mechanical properties and the strength and hardness decrease but elongation increases, which is conducive to plastic processing. In addition, under the optimum amount of 0.8 wt.% La2O3 content, the corrosion rate of immersion corrosion attains the minimum values: As 12.6 g m-2 h-1, it decreases by 24%; as the corrosion potential changes from -1.1327 V to -0.328 V, it increases by 70.9%; and as the corrosion current density decreases from -2.833 mA mm-2 to -3.28 mA mm-2 corrosion, it decreases by 15.78%, when compared with H62 brass.

  9. Testing the permeability and corrosion resistance of micro-mechanically interlocked joints

    DEFF Research Database (Denmark)

    Byskov-Nielsen, Jeppe; Holm, Allan Hjarbæk; Højsholt, Rune;

    2011-01-01

    Micro-mechanical interlocking (MMI) can be applied to create new and interesting composite materials. We have employed laser structuring to achieve MMI between stainless steel and plastic with extremely high joint strength. However, the water permeability and corrosion resistance of the joint must...... is conducted. The permeability seems to be consistent with the Hagen–Poiseuille equation independent of the laser structuring technique and is orders of magnitudes larger than the diffusion rate through the plastic. Two different types of corrosion tests have been undertaken, and we show that care must...... be taken in order not to degrade the corrosion resistance of the sample to an unacceptable level....

  10. Mechanical Performance versus Corrosion Damage Indicators for Corroded Steel Reinforcing Bars

    Directory of Open Access Journals (Sweden)

    Silvia Caprili

    2015-01-01

    Full Text Available The experimental results of a testing campaign including tensile and low-cycle fatigue tests on different reinforcing steel bar types in the as-delivered and corroded condition are presented. Experimental data were statistically analyzed adopting ANOVA technique; Performance Indicators (PIs, describing the mechanical performance characteristics of reinforcements, and Corrosion Damage Indicators (CDIs, describing the detrimental effects of corrosion phenomena, were determined and correlated in order to evaluate the influence of corrosion on the behaviour of reinforcing steels, providing useful information for designers in addition to what is presented in current standards.

  11. Mechanical and corrosion behaviour of EUROFER 97 steel exposed to Pb-17Li

    Energy Technology Data Exchange (ETDEWEB)

    Benamati, G.; Fazio, C. E-mail: concetta@brasimone.enea.it; Ricapito, I

    2002-12-01

    Corrosion and tensile samples of the EUROFER 97 steel were exposed to Pb-17Li in the LIFUS II loop at 480 deg. C. The specimens were extracted after 1500, 3000 and 4500 h exposure. After extraction, weight change measurements and metallurgical analysis were performed on the corrosion specimens, while tensile tests were performed at 480 deg. C. The results showed that EUROFER 97 underwent uniform corrosion and the mechanical properties seem to be unaffected or only slightly affected by the liquid metal. In this paper, the results are reported and discussed also with reference to previous similar work.

  12. Characteristics and Corrosion Behavior of Pure Titanium Subjected to Surface Mechanical Attrition

    Science.gov (United States)

    Fu, Tianlin; Wang, Xiao; Liu, Jianxiong; Li, Li; Yu, Xiaohua; Zhan, Zhaolin

    2017-08-01

    A stable passive film exhibiting good corrosion resistance in a 3.5 wt.% NaCl solution was formed on the surface of pure titanium (Ti) subjected to a surface mechanical attrition treatment (SMAT). The corrosion potential (-0.21 V) of the film was significantly higher than that (-0.92 V) of the untreated sample. Moreover, the corrosion current density was an order of magnitude lower than that of the untreated sample. SMAT resulted in a decrease in the vacancy condensation in the TiO2 film, thereby inhibiting the invasion and diffusion of Cl- in the film.

  13. Research on Aluminized Steel for Resisting Stress Corrosion Cracking and Hydrogen Embrittlement%渗铝钢抗应力腐蚀开裂及抗氢脆性能研究

    Institute of Scientific and Technical Information of China (English)

    吴昊; 李华飞

    2016-01-01

    以30CrMo钢为母体,对30CrMo钢及其渗铝钢分别进行抗硫化氢应力腐蚀开裂实验、抗氯离子应力腐蚀开裂实验,采用Devanathan双电池技术测量氢的扩散系数。实验结果表明:30CrMo钢渗铝后比渗铝前具有更好的抗硫化氢应力腐蚀开裂、抗氢脆性能;单一氯离子对30CrMo钢及其渗铝钢应力腐蚀开裂性能影响较小。%Using 30CrMo steel as the matrix, resistance to hydrogen sulfide stress corrosion cracking test and resistance to chloride ion stress corrosion cracking test were carried out respectively for 30CrMo steel and its aluminized steel.Using Devanathan double cell technology, and we measured hydrogen diffusion coefficient.Experimental results show that, aluminized steel of 30CrMo has better resistance to hydrogen sulfide stress corrosion cracking and hy-drogen embrittlement, and single chloride ion has little influence on the stress corrosion cracking for 30CrMo steel and its aluminized steel.

  14. Micro-mechanical Analysis of Fiber Reinforced Cementitious Composites using Cohesive Crack Modeling

    DEFF Research Database (Denmark)

    Dick-Nielsen, Lars; Stang, Henrik; Poulsen, Peter Noe

    2006-01-01

    This paper discusses the mechanism appearing during fiber debonding in fiber reinforced cementitious composite. The investigation is performed on the micro scale by use of a Finite Element Model. The model is 3 dimensional and the fictitious crack model and a mixed mode stress formulation...

  15. Crack Growth Rate Modeling of a Titanium-Aluminide Alloy Under Thermal-Mechanical Cycling

    Science.gov (United States)

    1991-12-01

    is integrated using Simpson’s rule. The integration of f(t) from t = ta to t = tb is: fIb f(t) dt ,,---- [f(t4 ) + 4f(tj) + f(tb)1 (5.68) ie 6 where... Knott , J.F. International Journal of Fracture Mechanics 1971, pp 462-467 101. Halliday M.D. and Beevers, C.J., ’The d.c. Electrical Potential Method for...Test Methods for Fracture and Fatigue Crack Growth ASTM STP 877, 1985, pp 67-85. 108. Ritchie, R.O., Garrett, G.G., and Knott , J.F., " Crack-Growth

  16. Corrosion and mechanical performance of AZ91 exposed to simulated inflammatory conditions.

    Science.gov (United States)

    Brooks, Emily K; Der, Stephanie; Ehrensberger, Mark T

    2016-03-01

    Magnesium (Mg) and its alloys, including Mg-9%Al-1%Zn (AZ91), are biodegradable metals with potential use as temporary orthopedic implants. Invasive orthopedic procedures can provoke an inflammatory response that produces hydrogen peroxide (H2O2) and an acidic environment near the implant. This study assessed the influence of inflammation on both the corrosion and mechanical properties of AZ91. The AZ91 samples in the inflammatory protocol were immersed for three days in a complex biologically relevant electrolyte (AMEM culture media) that contained serum proteins (FBS), 150 mM of H2O2, and was titrated to a pH of 5. The control protocol immersed AZ91 samples in the same biologically relevant electrolyte (AMEM & FBS) but without H2O2 and the acid titration. After 3 days all samples were switched into fresh AMEM & FBS for an additional 3-day immersion. During the initial immersion, inflammatory protocol samples showed increased corrosion rate determined by mass loss testing, increased Mg and Al ion released to solution, and a completely corroded surface morphology as compared to the control protocol. Although corrosion in both protocols slowed once the test electrolyte solution was replaced at 3 days, the samples originally exposed to the simulated inflammatory conditions continued to display enhanced corrosion rates as compared to the control protocol. These lingering effects may indicate the initial inflammatory corrosion processes modified components of the surface oxide and corrosion film or initiated aggressive localized processes that subsequently left the interface more vulnerable to continued enhanced corrosion. The electrochemical properties of the interfaces were also evaluated by EIS, which found that the corrosion characteristics of the AZ91 samples were potentially influenced by the role of intermediate adsorption layer processes. The increased corrosion observed for the inflammatory protocol did not affect the flexural mechanical properties of the AZ91

  17. TEM characterisation of stress corrosion cracks in nickel based alloys: effect of chromium content and chemistry of environment; Caracterisation par MET de fissures de corrosion sous contrainte d'alliages a base de nickel: influence de la teneur en chrome et de la chimie du milieu

    Energy Technology Data Exchange (ETDEWEB)

    Delabrouille, F

    2004-11-15

    Stress corrosion cracking (SCC) is a damaging mode of alloys used in pressurized water reactors, particularly of nickel based alloys constituting the vapour generator tubes. Cracks appear on both primary and secondary sides of the tubes, and more frequently in locations where the environment is not well defined. SCC sensitivity of nickel based alloys depends of their chromium content, which lead to the replacement of alloy 600 (15 % Cr) by alloy 690 (30 % Cr) but this phenomenon is not yet very well understood. The goal of this thesis is two fold: i) observe the effect of chromium content on corrosion and ii) characterize the effect of environment on the damaging process of GV tubes. For this purpose, one industrial tube and several synthetic alloys - with controlled chromium content - have been studied. Various characterisation techniques were used to study the corrosion products on the surface and within the SCC cracks: SIMS; TEM - FEG: thin foil preparation, HAADF, EELS, EDX. The effect of chromium content and surface preparation on the generalised corrosion was evidenced for synthetic alloys. Moreover, we observed the penetration of oxygen along triple junctions of grain boundaries few micrometers under the free surface. SCC tests show the positive effect of chromium for contents varying from 5 to 30 % wt. Plastic deformation induces a modification of the structure, and thus of the protective character, of the internal chromium rich oxide layer. SCC cracks which developed in different chemical environments were characterised by TEM. The oxides which are formed within the cracks are different from what is observed on the free surface, which reveals a modification of medium and electrochemical conditions in the crack. Finally we were able to evidence some structural characteristics of the corrosion products (in the cracks and on the surface) which turn to be a signature of the chemical environment. (author)

  18. Reliability Model of Corrosion Fatigue Crack Growth Rate Evaluation of LD10CS Aluminum Alloy%LD10CS腐蚀疲劳裂纹扩展速率评价的可靠性模型

    Institute of Scientific and Technical Information of China (English)

    贾明明; 李旭东; 吕航

    2014-01-01

    腐蚀损伤会加速疲劳载荷下的飞机铝合金结构裂纹的萌生和扩展,威胁结构安全性。针对腐蚀影响下的疲劳裂纹扩展的随机性本质,对预腐蚀 LD10CS 合金的预腐蚀疲劳试验进行了数据分析,提出了基于可靠性的腐蚀裂纹扩展速率表征方法,与试验结果对比表明,该方法可以给出 LD10CS 腐蚀疲劳裂纹扩展速率的上下限,进而给出该种材料铝合金构件的疲劳裂纹扩展寿命的上下限,为评估铝合金构件的寿命提供了依据。%Fatigue loadings and environmental corrosion damage can decrease the mechanical properties of LD10CS alu-minum alloy.The paper made a research on the fatigue crack growth rate (FCG)of AA LD10CS with corrosion damage, and proposed a reliability-based method to evaluate FCG.Compare of predicted FCG and experimental results indicated that the proposed method was able to give the lower and upper limit of FCG of LD10CS with corrosion damage,which provided the basis of aluminum alloy component safe life prediction.

  19. Mechanical properties and corrosion resistance of some titanium alloys in marine environment

    Directory of Open Access Journals (Sweden)

    Dupuis Jennifer

    2013-11-01

    Full Text Available Titanium alloys are used in several fields such as aerospace industry or biomedical. They are increasingly used in marine applications, a highly corrosive environment. We chose titanium alloys for their good properties such as high mechanical strength, low density and excellent corrosion resistance. This study is focused on titanium alloys potentially interesting to be used in marine transports, and mainly for the boats fittings such as a winch for example.

  20. Iodine induced stress corrosion of zirconium and zircaloy-4 mechanisms. Translation to pellet cladding interaction conditions in PWR type reactors; Mecanismes de corrosion sous contrainte par l`iode dans le zirconium et le zircaloy-4. Transposition aux conditions d`interaction pastille-gaine dans les reacteurs a eau pressurisee

    Energy Technology Data Exchange (ETDEWEB)

    Fregonese, M

    1997-10-08

    This thesis is linked to the study of the Pellet-Cladding Interaction (PCI) phenomenon in Pressurized Water Reactors, which can lead to cladding rupture by iodine Stress Corrosion Cracking (SCC) of Zircaloy-4. Results are obtained through slow tensile tests performed in iodine methanol and in iodine vapour, on reference material, neutron irradiated material, and iodine zirconium implanted material. They allow to propose an explanation of the rapidity of the ruptures observed during PCI loadings, and to make the link between laboratory SCC tests and power ramp tests. Indeed, neutron irradiation facilitates the initiation and the transgranular propagation steps of the SCC cracks, due to strain localization and hardening associated to the presence of irradiation defects. On the other hand, recoiled iodine does not seem to affect SCC susceptibility of the material. On a chemical point of view, thermally released iodine is then responsible for PCI/SCC ruptures. A detailed calculation of iodine amount created by fission and released in the gap during irradiation makes it possible to show that local iodine concentration facing the pellet-to-pellet and the radial pellet cracks regions is sufficient for SCC cracks to develop in the metal. Finally, a competition between re-passivation and cracking is underscored. This results are in good agreement with the occurrence of an iodine adsorption mechanism. Adsorption could be assisted by a corrosion-deformation interaction phenomenon, and/or by the formation of solid and gaseous zirconium iodides. (author) 132 refs.

  1. Seismic damage-cracking analysis of arch dams using different earthquake input mechanisms

    Institute of Scientific and Technical Information of China (English)

    2009-01-01

    In this study, a nonlinear model is presented for analysis of damage-cracking behavior in arch dams during strong earthquakes using different seismic input mechanisms. The nonlinear system includes a plastic-damage model for cyclic loading of concrete considering strain softening and a contact boundary model of contraction joint opening. Two different earthquake input mechanisms are used for comparison, including massless foundation input model and viscous-spring boundary model considering radiation damping due to infinite canyon. The results demonstrate that effects of seismic input mechanism and radiation damping on nonlinear response and damage-cracking of the dam are significant. Compared with the results of using massless foundation input model, the damage-cracking region and contraction joint opening are substantially reduced when using viscous-spring boundary model to take into account radiation damping. However, if the damping ratio of the dam is artificially increased to about 10%―15% for massless foundation input model, the joint opening and damage-cracking of the dam are comparable to the results obtained from the viscous-spring boundary model.

  2. Cracks path growth in turbine blades with TBC under thermo – mechanical cyclic loadings

    Directory of Open Access Journals (Sweden)

    T. Sadowski

    2016-02-01

    Full Text Available Blades of combustion turbines are extremely loaded turbojet elements, which transmit operative energy onto a rotor. Experiences of many years indicate, that cracks initiation and propagation in the blades during the operation time can cause destruction not only of the engine, but sometimes an airplane. In high temperature one of the most often occuring interactions in the turbine engine are time variable force fields, caused by non-stationary flowing of an exhaust gas and aerodynamical interaction of the engine elements. The extremal thermo-mechanical loadings initiate gradual degradation process of the blades as a result of fatigue and material creep. More often Thermal Barrier Coatings (TBCs are applied on the turbine blade surface to provide protection not only against the high temperature but also against aggressive environment. The paper presents the advantages of applying of the TBC layers for increase of the cracks resistance to gradual degradation of the turbine blades. The level of save values of thermo-mechanical loading was estimated. Analysis of critical values of loading leading to crack initiation, further growth and the final blade fragmentation was performed. The most efforted places of the turbine blades were selected and crack paths due to thermo-mechanical cyclic loading were determined.

  3. Propagation of cracks by stress corrosion in conditions of BWR type reactor; Propagacion de grietas por corrosion bajo esfuerzo en condiciones de reactor de agua en ebullicion (BWR)

    Energy Technology Data Exchange (ETDEWEB)

    Merino C, F.J. [ININ, 52045 Estado de Mexico (Mexico); Fuentes C, P. [ITT, Metepec, Estado de Mexico (Mexico)]. E-mail: fjmc@nuclear.inin.mx

    2004-07-01

    In this work, the obtained results when applying the Hydrogen Chemistry to a test tube type Compact Tension (CT), built in austenitic stainless steel 304l, simulating the conditions to those that it operates a Boiling Water Reactor (BWR), temperature 288 C and pressure of 8 MPa are presented. With the application of this water chemistry, seeks to be proven the diminution of the crack propagation speed. (Author)

  4. Mechanical Performance and Chloride Diffusivity of Cracked RC Specimens Exposed to Freeze-Thaw Cycles and Intermittent Immersion in Seawater

    Directory of Open Access Journals (Sweden)

    Bei Shen

    2016-01-01

    Full Text Available The effects of crack width on chloride ingress and mechanical behavior of reinforced concrete (RC specimens were experimentally studied after exposure to 300 cycles of freeze-thaw and seawater immersion (75 times. Cracks were induced prior to exposure by an eccentric compression load which was sustained until the end of the exposure period. The maximum cracks widths induced in the four column specimens were 0, 0.06, 0.11, and 0.15 mm, respectively. Results show that when the crack width was less than 0.06 mm, the effect of cracks on chloride ingress could be neglected. However, when the crack width was more than 0.11 mm, chloride ingress was accelerated. Results of static loading tests show that both yield load and ultimate load of RC columns decreased as crack width increased. When the crack width was 0.15 mm, yield load and ultimate load of RC column specimen decreased by 17.0% and 18.9%, respectively, compared to a specimen without cracks. It was concluded that crack width significantly promoted local chlori