WorldWideScience

Sample records for conductive core-sheath nanofibers

  1. Core-Sheath Paraffin-Wax-Loaded Nanofibers by Electrospinning for Heat Storage.

    Science.gov (United States)

    Lu, Yuan; Xiao, Xiudi; Zhan, Yongjun; Huan, Changmeng; Qi, Shuai; Cheng, Haoliang; Xu, Gang

    2018-04-18

    Paraffin wax (PW) is widely used for smart thermoregulation materials due to its good thermal performance. However, the leakage and low thermal conductivity of PW hinder its application in the heat storage field. Accordingly, developing effective methods to address these issues is of great importance. In this study, we explored a facile approach to obtain PW-loaded core-sheath structured flexible nanofibers films via coaxial electrospinning technique. The PW as the core layer was successfully encapsulated by the sheath-layer poly(methyl methacrylate). The diameter of the fiber core increased from 395 to 848 nm as the core solution speed rate increased from 0.1 to 0.5 mL/h. In addition, it can be seen that higher core solution speed rate could lead to higher PW encapsulation efficiency according to the transmission electron microscopy results. The core-sheath nanofiber films, moreover, possessed the highest latent heat of 58.25 J/g and solidifying enthalpy of -56.49 J/g. In addition, we found that after 200 thermal cycles, there was little change in latent heat, which demonstrated that it is beneficial for the PW-loaded core-sheath structure to overcome the leakage issue and enhance thermal stability properties for the thermoregulation film.

  2. A smart core-sheath nanofiber that captures and releases red blood cells from the blood

    Science.gov (United States)

    Shi, Q.; Hou, J.; Zhao, C.; Xin, Z.; Jin, J.; Li, C.; Wong, S.-C.; Yin, J.

    2016-01-01

    A smart core-sheath nanofiber for non-adherent cell capture and release is demonstrated. The nanofibers are fabricated by single-spinneret electrospinning of poly(N-isopropylacrylamide) (PNIPAAm), polycaprolactone (PCL) and nattokinase (NK) solution blends. The self-assembly of PNIPAAm and PCL blends during the electrospinning generates the core-sheath PCL/PNIPAAm nanofibers with PNIPAAm as the sheath. The PNIPAAm-based core-sheath nanofibers are switchable between hydrophobicity and hydrophilicity with temperature change and enhance stability in the blood. When the nanofibers come in contact with blood, the NK is released from the nanofibers to resist platelet adhesion on the nanofiber surface, facilitating the direct capture and isolation of red blood cells (RBCs) from the blood above phase-transition temperature of PNIPAAm. Meanwhile, the captured RBCs are readily released from the nanofibers with temperature stimuli in an undamaged manner. The release efficiency of up to 100% is obtained while maintaining cellular integrity and function. This work presents promising nanofibers to effectively capture non-adherent cells and release for subsequent molecular analysis and diagnosis of single cells.A smart core-sheath nanofiber for non-adherent cell capture and release is demonstrated. The nanofibers are fabricated by single-spinneret electrospinning of poly(N-isopropylacrylamide) (PNIPAAm), polycaprolactone (PCL) and nattokinase (NK) solution blends. The self-assembly of PNIPAAm and PCL blends during the electrospinning generates the core-sheath PCL/PNIPAAm nanofibers with PNIPAAm as the sheath. The PNIPAAm-based core-sheath nanofibers are switchable between hydrophobicity and hydrophilicity with temperature change and enhance stability in the blood. When the nanofibers come in contact with blood, the NK is released from the nanofibers to resist platelet adhesion on the nanofiber surface, facilitating the direct capture and isolation of red blood cells (RBCs) from

  3. Co-electrospinning fabrication and photocatalytic performance of TiO2/SiO2 core/sheath nanofibers with tunable sheath thickness

    International Nuclear Information System (INIS)

    Cao, Houbao; Du, Pingfan; Song, Lixin; Xiong, Jie; Yang, Junjie; Xing, Tonghai; Liu, Xin; Wu, Rongrong; Wang, Minchao; Shao, Xiaoli

    2013-01-01

    Graphical abstract: - Highlights: • The core–sheath TiO 2 /SiO 2 nanofibers were fabricated by co-electrospinning technique. • The catalytic property of nanofibers with different sheath thickness was studied. • The potential methods of improving catalytic efficiency are suggested. - Abstract: In this paper, core/sheath TiO 2 /SiO 2 nanofibers with tunable sheath thickness were directly fabricated via a facile co-electrospinning technique with subsequent calcination at 500 °C. The morphologies and structures of core/sheath TiO 2 /SiO 2 nanofibers were characterized by TGA, FESEM, TEM, FTIR, XPS and BET. It was found that the 1D core/sheath nanofibers are made up of anatase–rutile TiO 2 core and amorphous SiO 2 sheath. The influences of SiO 2 sheath and its thickness on the photoreactivity were evaluated by observing photo-degradation of methylene blue aqueous solution under the irradiation of UV light. Compared with pure TiO 2 nanofibers, the core/sheath TiO 2 /SiO 2 nanofibers performed a better catalytic performance. That was attributed to not only efficient separation of hole–electron pairs resulting from the formation of heterojunction but also larger surface area and surface silanol group which will be useful to provide higher capacity for oxygen adsorption to generate more hydroxyl radicals. And the optimized core/sheath TiO 2 /SiO 2 nanofibers with a sheath thickness of 37 nm exhibited the best photocatalytic performance

  4. Selective pH-Responsive Core-Sheath Nanofiber Membranes for Chem/Bio/Med Applications: Targeted Delivery of Functional Molecules.

    Science.gov (United States)

    Han, Daewoo; Steckl, Andrew J

    2017-12-13

    Core-sheath fibers using different Eudragit materials were successfully produced, and their controlled multi-pH responses have been demonstrated. Core-sheath fibers made of Eudragit L 100 (EL100) core and Eudragit S 100 (ES100) sheath provide protection and/or controlled release of core material at pH 6 by adjusting the sheath thickness (controlled by the flow rate of source polymer solution). The thickest sheath (∼250 nm) provides the least core release ∼1.25%/h, while the thinnest sheath (∼140 nm) provides much quicker release ∼16.75%/h. Furthermore, switching core and sheath material dramatically altered the pH response. Core-sheath fibers made of ES100 core and EL100 sheath can provide a consistent core release rate, while the sheath release rate becomes higher as the sheath layer becomes thinner. For example, the thinnest sheath (∼120 nm) provides a core and sheath release ratio of 1:2.5, while the thickest sheath (∼200 nm) shows only a ratio of 1:1.7. All core-sheath Eudragit fibers show no noticeable release at pH 5, while they are completely dissolved at pH 7. Extremely high surface area in the porous network of the fiber membranes provides much faster (>30 times) response to external pH changes as compared to that of equivalent cast films.

  5. Thermal conductivity model for nanofiber networks

    Science.gov (United States)

    Zhao, Xinpeng; Huang, Congliang; Liu, Qingkun; Smalyukh, Ivan I.; Yang, Ronggui

    2018-02-01

    Understanding thermal transport in nanofiber networks is essential for their applications in thermal management, which are used extensively as mechanically sturdy thermal insulation or high thermal conductivity materials. In this study, using the statistical theory and Fourier's law of heat conduction while accounting for both the inter-fiber contact thermal resistance and the intrinsic thermal resistance of nanofibers, an analytical model is developed to predict the thermal conductivity of nanofiber networks as a function of their geometric and thermal properties. A scaling relation between the thermal conductivity and the geometric properties including volume fraction and nanofiber length of the network is revealed. This model agrees well with both numerical simulations and experimental measurements found in the literature. This model may prove useful in analyzing the experimental results and designing nanofiber networks for both high and low thermal conductivity applications.

  6. Thermal conductivity model for nanofiber networks

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Xinpeng [Department of Mechanical Engineering, University of Colorado, Boulder, Colorado 80309, USA; Huang, Congliang [Department of Mechanical Engineering, University of Colorado, Boulder, Colorado 80309, USA; School of Electrical and Power Engineering, China University of Mining and Technology, Xuzhou 221116, China; Liu, Qingkun [Department of Physics, University of Colorado, Boulder, Colorado 80309, USA; Smalyukh, Ivan I. [Department of Physics, University of Colorado, Boulder, Colorado 80309, USA; Materials Science and Engineering Program, University of Colorado, Boulder, Colorado 80309, USA; Yang, Ronggui [Department of Mechanical Engineering, University of Colorado, Boulder, Colorado 80309, USA; Materials Science and Engineering Program, University of Colorado, Boulder, Colorado 80309, USA; Buildings and Thermal Systems Center, National Renewable Energy Laboratory, Golden, Colorado 80401, USA

    2018-02-28

    Understanding thermal transport in nanofiber networks is essential for their applications in thermal management, which are used extensively as mechanically sturdy thermal insulation or high thermal conductivity materials. In this study, using the statistical theory and Fourier's law of heat conduction while accounting for both the inter-fiber contact thermal resistance and the intrinsic thermal resistance of nanofibers, an analytical model is developed to predict the thermal conductivity of nanofiber networks as a function of their geometric and thermal properties. A scaling relation between the thermal conductivity and the geometric properties including volume fraction and nanofiber length of the network is revealed. This model agrees well with both numerical simulations and experimental measurements found in the literature. This model may prove useful in analyzing the experimental results and designing nanofiber networks for both high and low thermal conductivity applications.

  7. Thermal conductivity of electrospun polyethylene nanofibers.

    Science.gov (United States)

    Ma, Jian; Zhang, Qian; Mayo, Anthony; Ni, Zhonghua; Yi, Hong; Chen, Yunfei; Mu, Richard; Bellan, Leon M; Li, Deyu

    2015-10-28

    We report on the structure-thermal transport property relation of individual polyethylene nanofibers fabricated by electrospinning with different deposition parameters. Measurement results show that the nanofiber thermal conductivity depends on the electric field used in the electrospinning process, with a general trend of higher thermal conductivity for fibers prepared with stronger electric field. Nanofibers produced at a 45 kV electrospinning voltage and a 150 mm needle-collector distance could have a thermal conductivity of up to 9.3 W m(-1) K(-1), over 20 times higher than the typical bulk value. Micro-Raman characterization suggests that the enhanced thermal conductivity is due to the highly oriented polymer chains and enhanced crystallinity in the electrospun nanofibers.

  8. Fabrication of Conductive Polypyrrole Nanofibers by Electrospinning

    Directory of Open Access Journals (Sweden)

    Yiqun Cong

    2013-01-01

    Full Text Available Electrospinning is employed to prepare conductive polypyrrole nanofibers with uniform morphology and good mechanical strength. Soluble PPy was synthesized with NaDEHS as dopant and then applied to electrospinning with or without PEO as carrier. The PEO contents had great influence on the morphology and conductivity of the electrospun material. The results of these experiments will allow us to have a better understanding of PPy electrospun nanofibers and will permit the design of effective electrodes in the BMIs fields.

  9. Nanomembranes and Nanofibers from Biodegradable Conducting Polymers

    Directory of Open Access Journals (Sweden)

    Jordi Puiggalí

    2013-09-01

    Full Text Available This review provides a current status report of the field concerning preparation of fibrous mats based on biodegradable (e.g., aliphatic polyesters such as polylactide or polycaprolactone and conducting polymers (e.g., polyaniline, polypirrole or polythiophenes. These materials have potential biomedical applications (e.g., tissue engineering or drug delivery systems and can be combined to get free-standing nanomembranes and nanofibers that retain the better properties of their corresponding individual components. Systems based on biodegradable and conducting polymers constitute nowadays one of the most promising solutions to develop advanced materials enable to cover aspects like local stimulation of desired tissue, time controlled drug release and stimulation of either the proliferation or differentiation of various cell types. The first sections of the review are focused on a general overview of conducting and biodegradable polymers most usually employed and the explanation of the most suitable techniques for preparing nanofibers and nanomembranes (i.e., electrospinning and spin coating. Following sections are organized according to the base conducting polymer (e.g., Sections 4–6 describe hybrid systems having aniline, pyrrole and thiophene units, respectively. Each one of these sections includes specific subsections dealing with applications in a nanofiber or nanomembrane form. Finally, miscellaneous systems and concluding remarks are given in the two last sections.

  10. Enhanced thermal conductance of polymer composites through embeddingaligned carbon nanofibers

    Directory of Open Access Journals (Sweden)

    Dale K. Hensley

    2016-07-01

    Full Text Available The focus of this work is to find a more efficient method of enhancing the thermal conductance of polymer thin films. This work compares polymer thin films embedded with randomly oriented carbon nanotubes to those with vertically aligned carbon nanofibers. Thin films embedded with carbon nanofibers demonstrated a similar thermal conductance between 40–60 μm and a higher thermal conductance between 25–40 μm than films embedded with carbon nanotubes with similar volume fractions even though carbon nanotubes have a higher thermal conductivity than carbon nanofibers.

  11. Conductive Au nanowires regulated by silk fibroin nanofibers

    Science.gov (United States)

    Dong, Bo-Ju; Lu, Qiang

    2014-03-01

    Conductive Au-biopolymer composites have promising applications in tissue engineering such as nerve tissue regeneration. In this study, silk fibroin nanofibers were formed in aqueous solution by regulating silk self-assembly process and then used as template for Au nanowire fabrication. We performed the synthesis of Au seeds by repeating the seeding cycles for several times in order to increase the density of Au seeds on the nanofibers. After electroless plating, densely decorated Au seeds grew into irregularly shaped particles following silk nanofiber to fill the gaps between particles and finally form uniform continuous nanowires. The conductive property of the Au-silk fibroin nanowires was studied with current-voltage ( I-V) measurement. A typical ohmic behavior was observed, which highlighted their potential applications in nerve tissue regeneration.

  12. Highly Transparent and Conductive Metallized Nanofibers by Electrospinning and Electroplating

    Science.gov (United States)

    Yoon, Sam S.; Yarin, Alexander L.

    2017-11-01

    Transparent conducting films (TCFs) and transparent heaters (THs) are of interest for a wide variety of applications, from displays to window defrosters. Here, we demonstrate production of highly flexible, conducting, and transparent copper (Cu), nickel (Ni), platinum (Pt), and silver (Ag) nanofibers suitable for use not only in TCFs and THs but also in some other engineering applications. The merging of fibers at their intersections (i.e. self-junctioning) minimizes contact resistance in these films. These metallized nanofibers exhibited a remarkably low sheet resistance at a high optical transmittance. This low sheet resistance allows them to serve as low-voltage heaters, achieving a high heating temperature at a relatively low applied voltage. These nanofibers are free-standing, flexible, stretchable, and their mechanical reliability was confirmed through various mechanical endurance tests.

  13. Nanofiber Anisotropic Conductive Films (ACF) for Ultra-Fine-Pitch Chip-on-Glass (COG) Interconnections

    Science.gov (United States)

    Lee, Sang-Hoon; Kim, Tae-Wan; Suk, Kyung-Lim; Paik, Kyung-Wook

    2015-11-01

    Nanofiber anisotropic conductive films (ACF) were invented, by adapting nanofiber technology to ACF materials, to overcome the limitations of ultra-fine-pitch interconnection packaging, i.e. shorts and open circuits as a result of the narrow space between bumps and electrodes. For nanofiber ACF, poly(vinylidene fluoride) (PVDF) and poly(butylene succinate) (PBS) polymers were used as nanofiber polymer materials. For PVDF and PBS nanofiber ACF, conductive particles of diameter 3.5 μm were incorporated into nanofibers by electrospinning. In ultra-fine-pitch chip-on-glass assembly, insulation was significantly improved by using nanofiber ACF, because nanofibers inside the ACF suppressed the mobility of conductive particles, preventing them from flowing out during the bonding process. Capture of conductive particles was increased from 31% (conventional ACF) to 65%, and stable electrical properties and reliability were achieved by use of nanofiber ACF.

  14. Heterogeneous NiCo2O4@polypyrrole core/sheath nanowire arrays on Ni foam for high performance supercapacitors

    Science.gov (United States)

    Hu, Jing; Li, Minchan; Lv, Fucong; Yang, Mingyang; Tao, Pengpeng; Tang, Yougen; Liu, Hongtao; Lu, Zhouguang

    2015-10-01

    A novel heterogeneous NiCo2O4@PPy core/sheath nanowire arrays are directly grown on Ni foam involving three facile steps, hydrothermal synthesis and calcination of NiCo2O4 nanowire arrays and subsequent in-situ oxidative polymerization of polypyrrole (PPy). When investigated as binder- and conductive additive-free electrodes for supercapacitors (SCs) in 6 M KOH, the NiCo2O4@PPy core/sheath nanowire arrays exhibit high areal capacitance of 3.49 F cm-2 at a discharge current density of 5 mA cm-2, which is almost 1.5 times as much as the pristine NiCo2O4 (2.30 F cm-2). More importantly, it can remain 3.31 F cm-2 (94.8% retention) after 5000 cycles. The as-obtained electrode also displays excellent rate capability, whose areal capacitance can still remain 2.79 F cm-2 while the discharge current density is increased to 50 mA cm-2. The remarkable electrochemical performance is mainly attributed to the unique heterogeneous core/sheath nanowire-array architectures.

  15. Fabrication and properties of shape-memory polymer coated with conductive nanofiber paper

    Science.gov (United States)

    Lu, Haibao; Liu, Yanju; Gou, Jan; Leng, Jinsong

    2009-07-01

    A unique concept of shape-memory polymer (SMP) nanocomposites making up of carbon nanofiber paper was explored. The essential element of this method was to design and fabricate nanopaper with well-controlled and optimized network structure of carbon nanofibers. In this study, carbon nanofiber paper was prepared under ultrasonicated processing and vapor press method, while the dispersion of nanofiber was treated by BYK-191 dispersant. The morphologies of carbon nanofibers within the paper were characterized with scanning electron microscopy (SEM). In addition, the thermomechanical properties of SMP coated with carbon nanofiber paper were measured by the dynamic mechanical thermal analysis (DMTA). It was found that the glass transition temperature and thermomechanical properties of nanocomposites were strongly determined by the dispersion of polymer in conductive paper. Subsequently, the electrical conductivity of conductive paper and nanocomposites were measured, respectively. And experimental results revealed that the conductive properties of nanocoposites were significantly improved by carbon nanopaper, resulting in actuation driven by electrical resistive heating.

  16. Cellulose nanofibers/reduced graphene oxide flexible transparent conductive paper.

    Science.gov (United States)

    Gao, Kezheng; Shao, Ziqiang; Wu, Xue; Wang, Xi; Li, Jia; Zhang, Yunhua; Wang, Wenjun; Wang, Feijun

    2013-08-14

    The cellulose nanofibers (CNFs) paper exhibit high visible light transmittance, high mechanical strength, and excellent flexibility. Therefore, CNFs paper may be an excellent substrate material for flexible transparent electronic devices. In this paper, we endeavor to prepare CNFs-based flexible transparent conductive paper by layer-by-layer (LbL) assembly using divalent copper ions (Cu(2+)) as the crosslinking agent. The thickness of the reduced graphene oxide (RGO) active layer in the CNFs paper can be controlled by the cycle times of the LbL assembly. CNFs/[RGO]20 paper has the sheet resistances of ∼2.5 kΩ/□, and the transmittance of about 76% at a wavelength of 550 nm. Furthermore, CNFs/[RGO]20 paper inherits the excellent mechanical properties of CNFs paper, and the ultimate strength is about 136 MPa. CNFs-based flexible transparent conductive paper also exhibits excellent electrical stability and flexibility. Copyright © 2013. Published by Elsevier Ltd.

  17. Single flexible nanofiber to achieve simultaneous photoluminescence-electrical conductivity bifunctionality.

    Science.gov (United States)

    Sheng, Shujuan; Ma, Qianli; Dong, Xiangting; Lv, Nan; Wang, Jinxian; Yu, Wensheng; Liu, Guixia

    2015-02-01

    In order to develop new-type multifunctional composite nanofibers, Eu(BA)3 phen/PANI/PVP bifunctional composite nanofibers with simultaneous photoluminescence and electrical conductivity have been successfully fabricated via electrospinning technology. Polyvinyl pyrrolidone (PVP) is used as a matrix to construct composite nanofibers containing different amounts of Eu(BA)3 phen and polyaniline (PANI). X-Ray diffractometry (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), vibrating sample magnetometry (VSM), fluorescence spectroscopy and a Hall effect measurement system are used to characterize the morphology and properties of the composite nanofibers. The results indicate that the bifunctional composite nanofibers simultaneously possess excellent photoluminescence and electrical conductivity. Fluorescence emission peaks of Eu(3+) ions are observed in the Eu(BA)3 phen/PANI/PVP photoluminescence-electrical conductivity bifunctional composite nanofibers. The electrical conductivity reaches up to the order of 10(-3)  S/cm. The luminescent intensity and electrical conductivity of the composite nanofibers can be tuned by adjusting the amounts of Eu(BA)3 phen and PANI. The obtained photoluminescence-electrical conductivity bifunctional composite nanofibers are expected to possess many potential applications in areas such as microwave absorption, molecular electronics, biomedicine and future nanomechanics. More importantly, the design concept and construction technique are of universal significance to fabricate other bifunctional one-dimensional naonomaterials. Copyright © 2014 John Wiley & Sons, Ltd.

  18. Numerical Investigation of the Thermal Conductivity of Graphite Nanofibers

    Science.gov (United States)

    Hakak Khadem, Masoud

    The thermal conductivity of graphite nano-fibers (GNFs) with different styles is predicted computationally. GNFs are formed as basal planes of graphene stacked based on the catalytic configuration. The large GNF thermal conductivity relative to a base phase change material (PCM) may lead to improved PCM performance when embedded with GNFs. Three different types of GNFs are modeled: platelet, ribbon, and herringbone. Molecular dynamics (MD) simulations are used in this study as a means to predict the thermal conductivity tensor based on atomic behavior. The in-house MD code, Molecular Dynamics in Arbitrary Geometries (MDAG), was updated with the features required to create the predictions. To model both interlayer van-der Waals and intralayer covalent bonding of carbon atoms in GNFs, a combination of the optimized Tersoff potential function for atoms within the layers and a pairwise Lennard-Jones (LJ) potential function to model the interactions between the layers was used. Tests of energy conservation in the NVE ensemble have been performed to validate the employed potential model. Nose-Hoover, Andersen, and Berendsen thermostats were also incorporated into MDAG to enable MD simulations in NVT ensembles, where the volume, number of atoms, and temperature of the system are conserved. Equilibrium MD with Green-Kubo (GK) relations was then employed to extract the thermal conductivity tensor for symmetric GNFs (platelet and ribbon). The thermal conductivity of solid argon at different temperatures was calculated and compared to other studies to validate the GK implementation. Different heat current formulations, as a result of using the three-body Tersoff potential, were considered and the discrepancy in the calculated thermal conductivity values of graphene using each formula was resolved by employing a novel comparative technique that identifies the most accurate formulation. The effect of stacking configuration on the thermal conductivity of platelet and ribbon GNFs

  19. Design of carbon nanofiber embedded conducting epoxy resin

    International Nuclear Information System (INIS)

    Gantayat, Subhra; Sarkar, Niladri; Rout, Dibyaranjan; Swain, Sarat K.

    2017-01-01

    Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

  20. Design of carbon nanofiber embedded conducting epoxy resin

    Energy Technology Data Exchange (ETDEWEB)

    Gantayat, Subhra [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Sarkar, Niladri [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India); Rout, Dibyaranjan [School of Applied Sciences, KIIT University, Bhubaneswar 751024, Odisha (India); Swain, Sarat K., E-mail: swainsk2@yahoo.co.in [Department of Chemistry, Veer Surendra Sai University of Technology, Burla, Sambalpur 768018, Odisha (India)

    2017-01-15

    Acid treated carbon nanofiber (t-CNF) reinforced epoxy nanocomposites were fabricated by hand lay-up method with various wt % of t-CNF loadings. Pristine or unmodified carbon nano fibers (u-CNFs) were made compatible with epoxy matrix by means of mixed acid treatment. Fabricated nanocomposites were characterized with Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD) study, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM). Mechanical and thermal properties of the nanocomposites were measured as a function of t-CNF content. Effect of acid treated CNFs on to the mechanical properties of epoxy nanocomposites was justified by comparing the mechanical properties of epoxy/t-CNF and epoxy/u-CNF nanocomposites with same loading level. The electrical conductivity was achieved by epoxy resin with a threshold at 1 wt % of t-CNF. Substantial improvement in thermal, mechanical and electrical properties of the synthesized epoxy/t-CNF nanocomposites may be suitable for fabricating electronic devices. - Highlights: • Epoxy/t-CNF nanocomposites are characterized by XRD, FTIR, SEM, AFM and TEM. • Electrical conductivity was achieved by epoxy with a threshold at 1 wt% of t-CNF. • Tensile strength is enhanced by 40% due to dispersion of t-CNF. • Synthesized nanocomposites are suitable for fabricating electronic devises.

  1. Interfacial Synthesis of Electrically Conducting Polyaniline Nanofiber Composites

    National Research Council Canada - National Science Library

    Hopkins, A

    2004-01-01

    .... The in-situ polymerization technique of these PANI nanofibers in the presence of sulfonated polystyrene allowed for the growth of PANI 2-D nanostructures embedded in the polymerized sulfonated host...

  2. Iodine doping effects on the lattice thermal conductivity of oxidized polyacetylene nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Bi, Kedong, E-mail: lishi@mail.utexas.edu, E-mail: kedongbi@seu.edu.cn [Jiangsu Key Laboratory for Design and Manufacture of Micro-Nano Biomedical Instruments, School of Mechanical Engineering, Southeast University, Nanjing 211189 (China); Department of Mechanical Engineering, University of Texas at Austin, Austin, Texas 78712 (United States); Weathers, Annie; Pettes, Michael T.; Shi, Li, E-mail: lishi@mail.utexas.edu, E-mail: kedongbi@seu.edu.cn [Department of Mechanical Engineering, University of Texas at Austin, Austin, Texas 78712 (United States); Matsushita, Satoshi; Akagi, Kazuo [Department of Polymer Chemistry, Kyoto University, Kyoto 615-8510 (Japan); Goh, Munju [Department of Polymer Chemistry, Kyoto University, Kyoto 615-8510 (Japan); Institute of Advanced Composite Materials, Korea Institute of Science and Technology (KIST), Eunha-ri san 101, Bondong-eup, Wanju-gun, Jeolabuk-do 565-905 (Korea, Republic of)

    2013-11-21

    Thermal transport in oxidized polyacetylene (PA) nanofibers with diameters in the range between 74 and 126 nm is measured with the use of a suspended micro heater device. With the error due to both radiation and contact thermal resistance corrected via a differential measurement procedure, the obtained thermal conductivity of oxidized PA nanofibers varies in the range between 0.84 and 1.24 W m{sup −1} K{sup −1} near room temperature, and decreases by 40%–70% after iodine doping. It is also found that the thermal conductivity of oxidized PA nanofibers increases with temperature between 100 and 350 K. Because of exposure to oxygen during sample preparation, the PA nanofibers are oxidized to be electrically insulating before and after iodine doping. The measurement results reveal that iodine doping can result in enhanced lattice disorder and reduced lattice thermal conductivity of PA nanofibers. If the oxidation issue can be addressed via further research to increase the electrical conductivity via doping, the observed suppressed lattice thermal conductivity in doped polymer nanofibers can be useful for the development of such conducting polymer nanostructures for thermoelectric energy conversion.

  3. Iodine doping effects on the lattice thermal conductivity of oxidized polyacetylene nanofibers

    International Nuclear Information System (INIS)

    Bi, Kedong; Weathers, Annie; Pettes, Michael T.; Shi, Li; Matsushita, Satoshi; Akagi, Kazuo; Goh, Munju

    2013-01-01

    Thermal transport in oxidized polyacetylene (PA) nanofibers with diameters in the range between 74 and 126 nm is measured with the use of a suspended micro heater device. With the error due to both radiation and contact thermal resistance corrected via a differential measurement procedure, the obtained thermal conductivity of oxidized PA nanofibers varies in the range between 0.84 and 1.24 W m −1  K −1 near room temperature, and decreases by 40%–70% after iodine doping. It is also found that the thermal conductivity of oxidized PA nanofibers increases with temperature between 100 and 350 K. Because of exposure to oxygen during sample preparation, the PA nanofibers are oxidized to be electrically insulating before and after iodine doping. The measurement results reveal that iodine doping can result in enhanced lattice disorder and reduced lattice thermal conductivity of PA nanofibers. If the oxidation issue can be addressed via further research to increase the electrical conductivity via doping, the observed suppressed lattice thermal conductivity in doped polymer nanofibers can be useful for the development of such conducting polymer nanostructures for thermoelectric energy conversion

  4. Surface plasmon resonances, optical properties, and electrical conductivity thermal hystersis of silver nanofibers produced by the electrospinning technique.

    Science.gov (United States)

    Barakat, Nasser A M; Woo, Kee-Do; Kanjwal, Muzafar A; Choi, Kyung Eun; Khil, Myung Seob; Kim, Hak Yong

    2008-10-21

    In the present study, silver metal nanofibers have been successfully prepared by using the electrospinning technique. Silver nanofibers have been produced by electrospinning a sol-gel consisting of poly(vinyl alcohol) and silver nitrate. The dried nanofiber mats have been calcined at 850 degrees C in an argon atmosphere. The produced nanofibers do have distinct plasmon resonance compared with the reported silver nanoparticles. Contrary to the introduced shapes of silver nanoparticles, the nanofibers have a blue-shifted plasmon resonance at 330 nm. Moreover, the optical properties study indicated that the synthesized nanofibers have two band gap energies of 0.75 and 2.34 eV. An investigation of the electrical conductivity behavior of the obtained nanofibers shows thermal hystersis. These privileged physical features greatly widen the applications of the prepared nanofibers in various fields.

  5. A miniature microbial fuel cell with conducting nanofibers-based 3D porous biofilm

    International Nuclear Information System (INIS)

    Jiang, Huawei; Dong, Liang; Halverson, Larry J

    2015-01-01

    Miniature microbial fuel cell (MFC) technology has received growing interest due to its potential applications in high-throughput screening of bacteria and mutants to elucidate mechanisms of electricity generation. This paper reports a novel miniature MFC with an improved output power density and short startup time, utilizing electrospun conducting poly(3,4-ethylenedioxythiophene) (PEDOT) nanofibers as a 3D porous anode within a 12 μl anolyte chamber. This device results in 423 μW cm −3 power density based on the volume of the anolyte chamber, using Shewanella oneidensis MR-1 as a model biocatalyst without any optimization of bacterial culture. The device also excels in a startup time of only 1hr. The high conductivity of the electrospun nanofibers makes them suitable for efficient electron transfer. The mean pore size of the conducting nanofibers is several micrometers, which is favorable for bacterial penetration and colonization of surfaces of the nanofibers. We demonstrate that S. oneidensis can fully colonize the interior region of this nanofibers-based porous anode. This work represents a new attempt to explore the use of electrospun PEDOT nanofibers as a 3D anode material for MFCs. The presented miniature MFC potentially will provide a high-sensitivity, high-throughput tool to screen suitable bacterial species and mutant strains for use in large-size MFCs. (paper)

  6. Slit-surface electrospinning: a novel process developed for high-throughput fabrication of core-sheath fibers.

    Directory of Open Access Journals (Sweden)

    Xuri Yan

    Full Text Available In this work, we report on the development of slit-surface electrospinning--a process that co-localizes two solutions along a slit surface to spontaneously emit multiple core-sheath cone-jets at rates of up to 1 L/h. To the best of our knowledge, this is the first time that production of electrospun core-sheath fibers has been scaled to this magnitude. Fibers produced in this study were defect-free (i.e. non-beaded and core-sheath geometry was visually confirmed under scanning electron microscopy. The versatility of our system was demonstrated by fabrication of (1 fibers encapsulating a drug, (2 bicomponent fibers, (3 hollow fibers, and (4 fibers from a polymer that is not normally electrospinnable. Additionally, we demonstrate control of the process by modulating parameters such as flow rate, solution viscosity, and fixture design. The technological achievements demonstrated in this work significantly advance core-sheath electrospinning towards commercial and manufacturing viability.

  7. Damage detection and conductivity evolution in carbon nanofiber epoxy via electrical impedance tomography

    International Nuclear Information System (INIS)

    Tallman, T N; Wang, K W; Gungor, S; Bakis, C E

    2014-01-01

    Utilizing electrically conductive nanocomposites for integrated self-sensing and health monitoring is a promising area of structural health monitoring (SHM) research wherein local changes in conductivity coincide with damage. In this research we conduct proof of concept investigations using electrical impedance tomography (EIT) for damage detection by identifying conductivity changes and by imaging conductivity evolution in a carbon nanofiber (CNF) filled epoxy composite. CNF/epoxy is examined because fibrous composites can be manufactured with a CNF/epoxy matrix thereby enabling the entire matrix to become self-sensing. We also study the mechanisms of conductivity evolution in CNF/epoxy through electrical impedance spectroscopy (EIS) testing. The results of these tests indicate that thermal expansion is responsible for conductivity evolution in a CNF/epoxy composite. (paper)

  8. Effects of Surface Nitrification on Thermal Conductivity of Modified Aluminum Oxide Nanofibers-Reinforced Epoxy Matrix Nanocomposites

    International Nuclear Information System (INIS)

    Kim, Byungjoo; Bae, Kyongmin; An, Kayhyeok; Park, Soojin

    2012-01-01

    Aluminum oxide (Al 2 O 3 ) nanofibers were treated thermally under an ammonia (NH 3 ) gas stream balanced by nitrogen to form a thin aluminum nitride (AlN) layer on the nanofibers, resulting in the enhancement of thermal conductivity of Al 2 O 3 /epoxy nanocomposites. The micro-structural and morphological properties of the NH 3 -assisted thermally-treated Al 2 O 3 nanofibers were characterized by X-ray diffraction (XRD) and atomic force microscopy (AEM), respectively. The surface characteristics and pore structures were observed by X-ray photoelectron spectroscopy (XPS), Zeta-potential and N 2 /77 K isothermal adsorptions. From the results, the formation of AlN on Al 2 O 3 nanofibers was confirmed by XRD and XPS. The thermal conductivity (TC) of the modified Al 2 O 3 nanofibers/epoxy composites increased with increasing treated temperatures. On the other hand, the severely treated Al 2 O 3 /epoxy composites showed a decrease in TC, resulting from a decrease in the probability of heat-transfer networks between the filler and matrix in this system due to the aggregation of nanofiber fillers

  9. A Review of Electrospun Conductive Polyaniline Based Nanofiber Composites and Blends: Processing Features, Applications, and Future Directions

    Directory of Open Access Journals (Sweden)

    Saiful Izwan Abd Razak

    2015-01-01

    Full Text Available Electrospun polymer nanofibers with high surface area to volume ratio and tunable characteristic are formed through the application of strong electrostatic field. Electrospinning has been identified as a straight forward and viable technique to produce nanofibers from polymer solution as their initial precursor. These nanofiber materials have attracted attention of researchers due to their enhanced and exceptional nanostructural characteristics. Electrospun polyaniline (PANI based nanofiber is one of the important new materials for the rapidly growing technology development such as nanofiber based sensor devices, conductive tissue engineering scaffold materials, supercapacitors, and flexible solar cells applications. PANI however is relatively hard to process compared to that of other conventional polymers and plastics. The processing of PANI is daunting, mainly due to its rigid backbone which is related to its high level of conjugation. The challenges faced in the electrospinning processing of neat PANI have alternatively led to the development of the electrospun PANI based composites and blends. A review on the research activities of the electrospinning processing of the PANI based nanofibers, the potential prospect in various fields, and their future direction are presented.

  10. Electrically conductive carbon nanofiber/paraffin wax composites for electric thermal storage

    International Nuclear Information System (INIS)

    Zhang Kun; Han Baoguo; Yu Xun

    2012-01-01

    Highlights: ► Carbon nanofiber (CNF)/paraffin wax composite is found to be a promising electric thermal storage material. ► The thermal storage capacity of CNF/paraffin wax composite is five times of traditional electric thermal storage material. ► CNF is shown to be an effective conductive filler for the composite. - Abstract: The research of electric thermal storage (ETS) has attracted a lot of attention recently, which converts off-peak electrical energy into thermal energy and release it later at peak hours. In this study, new electric thermal storage composites are developed by employing paraffin wax as thermal storage media and carbon nanofiber (CNF) as conductive fillers. Electric heating and thermal energy release performances of the CNF/paraffin wax composites are experimentally investigated. Experimental results show that, when the composites are heated to about 70 °C, the developed electrically conductive CNF/paraffin wax composites present a thermal storage capacity of about 280 kJ/kg, which is five times of that of traditional thermal storage medium such as ceramic bricks (54 kJ/kg). The CNF/paraffin wax composites can also effectively store the thermal energy and release the thermal energy in later hours.

  11. A palladium-doped ceria@carbon core-sheath nanowire network: a promising catalyst support for alcohol electrooxidation reactions

    Science.gov (United States)

    Tan, Qiang; Du, Chunyu; Sun, Yongrong; Du, Lei; Yin, Geping; Gao, Yunzhi

    2015-08-01

    A novel palladium-doped ceria and carbon core-sheath nanowire network (Pd-CeO2@C CSNWN) is synthesized by a template-free and surfactant-free solvothermal process, followed by high temperature carbonization. This hierarchical network serves as a new class of catalyst support to enhance the activity and durability of noble metal catalysts for alcohol oxidation reactions. Its supported Pd nanoparticles, Pd/(Pd-CeO2@C CSNWN), exhibit >9 fold increase in activity toward the ethanol oxidation over the state-of-the-art Pd/C catalyst, which is the highest among the reported Pd systems. Moreover, stability tests show a virtually unchanged activity after 1000 cycles. The high activity is mainly attributed to the superior oxygen-species releasing capability of Pd-doped CeO2 nanowires by accelerating the removal of the poisoning intermediate. The unique interconnected one-dimensional core-sheath structure is revealed to facilitate immobilization of the metal catalysts, leading to the improved durability. This core-sheath nanowire network opens up a new strategy for catalyst performance optimization for next-generation fuel cells.A novel palladium-doped ceria and carbon core-sheath nanowire network (Pd-CeO2@C CSNWN) is synthesized by a template-free and surfactant-free solvothermal process, followed by high temperature carbonization. This hierarchical network serves as a new class of catalyst support to enhance the activity and durability of noble metal catalysts for alcohol oxidation reactions. Its supported Pd nanoparticles, Pd/(Pd-CeO2@C CSNWN), exhibit >9 fold increase in activity toward the ethanol oxidation over the state-of-the-art Pd/C catalyst, which is the highest among the reported Pd systems. Moreover, stability tests show a virtually unchanged activity after 1000 cycles. The high activity is mainly attributed to the superior oxygen-species releasing capability of Pd-doped CeO2 nanowires by accelerating the removal of the poisoning intermediate. The unique

  12. Small Angle Neutron Scattering (SANS) characterization of electrically conducting polyaniline nanofiber/polyimide nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Hopkins, Alan R., E-mail: alan.r.hopkins@aero.org [Aerospace Corporation, Space Materials Lab, Micro/Nano Technology Dept, Polymers Section, M2/242, Los Angeles, CA 90009-2957 (United States); Tomczak, Sandra J. [AFRL/RZSM Materials Application Branch, Space and Missile Propulsion Division 10 East Saturn Blvd., Bldg. 8451, Edwards Air Force Base, CA 93524 (United States); Vij, Vandana [ERC. Inc., AFRL/PRSM, Edwards AFB, CA (United States); Jackson, Andrew J. [National Institute of Standards and Technology (NIST) Center for Neutron Research, 100 Bureau Drive, Stop 6102, Gaithersburg, MD 20899-6102 (United States)

    2011-12-30

    Nanocomposites of polyaniline nanofibers and polyimide were fabricated and studied using small angle neutron scattering (SANS). The immiscible nature of the conformationally dissimilar polyaniline nanofiber and polyimide host is established by a series of experiments involving neutron scattering. Based on these techniques, we conclude that the crystal structure of the polyimides is not disrupted, and that there is no mixing between the two components on a molecular level. The morphology of the conducting salt component was analyzed by SANS data and was treated by two common models: Debye-Bueche (D-B) and inverse power law (IPL). Due to deviations in the linear curve fitting over a large scattering range, neither the D-B nor the IPL model could be used to characterize the size and shape of all PANI-0.5-CSA (polyaniline camphor sulfonic acid doped polymer)/polyimide blend systems. At 1 and 2% concentration, the D-B model suggested salt domains between 20 and 70 A with fractal geometries implied by the IPL model. As salt concentrations increased to 5%, the structures were observed to change, but there is no simple structural model that provides a suitable basis for comparison.

  13. Thermal conductivity predictions of herringbone graphite nanofibers using molecular dynamics simulations.

    Science.gov (United States)

    Khadem, Masoud H; Wemhoff, Aaron P

    2013-02-28

    Non-equilibrium molecular dynamics (NEMD) simulations are used to investigate the thermal conductivity of herringbone graphite nanofibers (GNFs) at room temperature by breaking down the axial and transverse conductivity values into intralayer and interlayer components. The optimized Tersoff potential is used to account for intralayer carbon-carbon interactions while the Lennard-Jones potential is used to model the interlayer carbon-carbon interactions. The intralayer thermal conductivity of the graphene layers near room temperature is calculated for different crease angles and number of layers using NEMD with a constant applied heat flux. The edge effect on a layer's thermal conductivity is investigated by computing the thermal conductivity values in both zigzag and armchair directions of the heat flow. The interlayer thermal conductivity is also predicted by imposing hot and cold Nosé-Hoover thermostats on two layers. The limiting case of a 90° crease angle is used to compare the results with those of single-layer graphene and few-layer graphene. The axial and transverse thermal conductivities are then calculated using standard trigonometric conversions of the calculated intralayer and interlayer thermal conductivities, along with calculations of few-layer graphene without a crease. The results show a large influence of the crease angle on the intralayer thermal conductivity, and the saturation of thermal conductivity occurs when number of layers is more than three. The axial thermal conductivity, transverse thermal conductivity in the crease direction, and transverse thermal conductivity normal to the crease for the case of a five-layer herringbone GNF with a 45° crease angle are calculated to be 27 W∕m K, 263 W∕m K, and 1500 W∕m K, respectively, where the axial thermal conductivity is in good agreement with experimental measurements.

  14. A nonlinear effective thermal conductivity model for carbon nanotube and nanofiber suspensions

    Energy Technology Data Exchange (ETDEWEB)

    Koo, J; Kang, Y [Department of Mechanical Engineering Kyung Hee University, 1, Seocheon-dong, Giheung-gu, Yongin-si, Gyeonggi-do 446-701 (Korea, Republic of); Kleinstreuer, C [Department of Mechanical and Aerospace Engineering, North Carolina State University, Campus Box 7910, 3211 Broughton Hall, Raleigh, NC 27695-7910 (United States)], E-mail: jmkoo@khu.ac.kr

    2008-09-17

    It has been experimentally demonstrated that suspensions of carbon nanotubes (CNTs) and nanofibers (CNFs) significantly increase the thermal conductivity of nanofluids; however, a physically sound theory of the underlying phenomenon is still missing. In this study, the nonlinear nature of the effective thermal conductivity enhancement with the particle concentration of CNT and CNF nanofluids is explained physically using the excluded volume concept. Specifically, the number of contacting CNTs and CNFs could be calculated by using the excluded volume concept, where the distance for heat to travel in a cylinder between the contacting cylinders in the thermal network of percolating CNTs and CNFs increased with the excluded volume. In contrast to the effective thermal conductivity model of Sastry et al (2008 Nanotechnology 19 055704) the present revised model could reproduce the nonlinear increase of the thermal conductivity with particle concentration, as well as the dependence on the diameter and aspect ratio of the CNTs and CNFs. It was found that the alignment of CNTs and CNFs due to the long range repulsion force decreases the excluded volume, leading to both the convex and concave nonlinear as well as linear increase of the thermal conductivity with particle concentration. The difference between various carrier fluids of the suspensions could be explained as the result of the change in the excluded volume in different base fluids.

  15. A Combination of Boron Nitride Nanotubes and Cellulose Nanofibers for the Preparation of a Nanocomposite with High Thermal Conductivity.

    Science.gov (United States)

    Zeng, Xiaoliang; Sun, Jiajia; Yao, Yimin; Sun, Rong; Xu, Jian-Bin; Wong, Ching-Ping

    2017-05-23

    With the current development of modern electronics toward miniaturization, high-degree integration and multifunctionalization, considerable heat is accumulated, which results in the thermal failure or even explosion of modern electronics. The thermal conductivity of materials has thus attracted much attention in modern electronics. Although polymer composites with enhanced thermal conductivity are expected to address this issue, achieving higher thermal conductivity (above 10 W m -1 K -1 ) at filler loadings below 50.0 wt % remains challenging. Here, we report a nanocomposite consisting of boron nitride nanotubes and cellulose nanofibers that exhibits high thermal conductivity (21.39 W m -1 K -1 ) at 25.0 wt % boron nitride nanotubes. Such high thermal conductivity is attributed to the high intrinsic thermal conductivity of boron nitride nanotubes and cellulose nanofibers, the one-dimensional structure of boron nitride nanotubes, and the reduced interfacial thermal resistance due to the strong interaction between the boron nitride nanotubes and cellulose nanofibers. Using the as-prepared nanocomposite as a flexible printed circuit board, we demonstrate its potential usefulness in electronic device-cooling applications. This thermally conductive nanocomposite has promising applications in thermal interface materials, printed circuit boards or organic substrates in electronics and could supplement conventional polymer-based materials.

  16. Dielectric properties and conductivity of carbon nanofiber/semi-crystalline polymer composites

    International Nuclear Information System (INIS)

    Sui, G.; Jana, S.; Zhong, W.H.; Fuqua, M.A.; Ulven, C.A.

    2008-01-01

    The properties of semi-crystalline polymer nanocomposites are affected by the nanofillers directly and indirectly, as two phases, i.e., crystalline and amorphous, exist in the polymer. The effects of nanofillers on the two phases could be competitive. The dielectric properties and conductivity of carbon nanofibers (CNF)/semi-crystalline polymer nanocomposites are studied in this paper. CNF/polypropylene (PP) nanocomposites are prepared in experiment by melt blending. The resulting morphology and crystalline structure are characterized by means of differential scanning calorimetry, wide angle X-ray diffraction and scanning electron microscopy. The PP nanocomposite containing 5 wt.% CNF exhibits a surprisingly high dielectric constant under wide sweep frequencies attended by low dielectric loss. Its dielectric constant is >600 under lower frequency, and remains >200 at a frequency of 4000 Hz. The electrical and thermal conductivities of the nanocomposites are studied, and enhancements are seen with increased CNF content. Theoretical analyses on the physical properties are carried out by applying the existing models. Research results indicate that a common commercial plastic with good comprehensive performance, which exhibited the potential for applications in advanced electronics, was obtained by a simple industry benign technique

  17. Biodegradable conductive composites of poly(3-hydroxybutyrate and polyaniline nanofibers: Preparation, characterization and radiolytic effects

    Directory of Open Access Journals (Sweden)

    2011-01-01

    Full Text Available Poly(3-hydroxybutyrate is a biodegradable polyester produced by microorganisms under nutrient limitation conditions. We obtained a biodegradable poly(3-hydroxybutyrate composite having 8 to 55% of chemically in situ polymerized hydrochloric acid-doped polyaniline nanofibers (70-100 nm in diameter. Fourier transform infrared spectroscopy and X-rays diffractometry data did not show evidence of significant interaction between the two components of the nanocomposite, and polyaniline semiconductivity was preserved in all studied compositions. Gamma-irradiation at 25 kGy absorbed dose on the semiconductive composite presenting 28% of doped polyaniline increased its conductivity from 4.6*10-2 to 1.1 S/m, while slightly decreasing its biodegradability. PANI-HCl biodegradation is negligible when compared to PHB biodegradability in an 80 day timeframe. Thus, this unprecedented all-polymer nanocomposite presents, at the same time, semiconductivity and biodegradability and was proven to maintain these properties after gamma irradiation. This new material has many potential applications in biological science, engineering, and medicine.

  18. Highly conductive electrospun carbon nanofiber/MnO2 coaxial nano-cables for high energy and power density supercapacitors

    Science.gov (United States)

    Zhi, Mingjia; Manivannan, Ayyakkannu; Meng, Fanke; Wu, Nianqiang

    2012-06-01

    This paper presents highly conductive carbon nanofiber/MnO2 coaxial cables in which individual electrospun carbon nanofibers are coated with an ultrathin hierarchical MnO2 layer. In the hierarchical MnO2 structure, an around 4 nm thick sheath surrounds the carbon nanofiber (CNF) in a diameter of 200 nm, and nano-whiskers grow radically outward from the sheath in view of the cross-section of the coaxial cables, giving a high specific surface area of MnO2. The CNFs are synthesized by electrospinning a precursor containing iron acetylacetonate (AAI). The addition of AAI not only enlarges the specific surface area of the CNF but also greatly enhances their electronic conductivity, which leads to a dramatic improvement in the specific capacitance and the rate capability of the CNF/MnO2 electrode. The AAI-CNF/MnO2 electrode shows a specific capacitance of 311 F g-1 for the whole electrode and 900 F g-1 for the MnO2 shell at a scan rate of 2 mV s-1. Good cycling stability, high energy density (80.2 Wh kg-1) and high power density (57.7 kW kg-1) are achieved. This work indicates that high electronic conductivity of the electrode material is crucial to achieving high power and energy density for pseudo-supercapacitors.

  19. Zero percolation threshold in electric conductivity of aluminum nanowire network fabricated by chemical etching using an electrospun nanofiber mask

    Science.gov (United States)

    Azuma, Keisuke; Sakajiri, Koichi; Okabe, Takashi; Matsumoto, Hidetoshi; Kang, Sungmin; Watanabe, Junji; Tokita, Masatoshi

    2017-09-01

    We investigated the sheet resistance (R s) and transmittance (T) of seamless two-dimensional networks of 50-nm-thick aluminum (Al) nanowires (NWs) with widths (W) ranging from 380 to 1410 nm. The Al NWs were fabricated by wet-etching of Al metalized polyester films with using polystyrene (PS) nanofibers as the mask. The PS nanofibers were deposited by the electrospinning of a PS solution and adhered to the film by annealing. W and the area coverage (φ) were increased with increasing PS solution concentration and deposition time, respectively. With increasing φ from 3 to 34%, T and R s decreased from 99 to 75% and from 800 to 10 Ω/sq, respectively, and the network with W = 878 nm at φ = 0.21 attained values of T = 91% and R s = 31 Ω/sq. The conductivity increases with φ with an exponent of 2, demonstrating that seamless NW networks are characterized by the zero percolation threshold.

  20. Electrospun Blank Nanocoating for Improved Sustained Release Profiles from Medicated Gliadin Nanofibers

    Directory of Open Access Journals (Sweden)

    Xinkuan Liu

    2018-03-01

    Full Text Available Nanomaterials providing sustained release profiles are highly desired for efficacious drug delivery. Advanced nanotechnologies are useful tools for creating elaborate nanostructure-based nanomaterials to achieve the designed functional performances. In this research, a modified coaxial electrospinning was explored to fabricate a novel core-sheath nanostructure (nanofibers F2, in which a sheath drug-free gliadin layer was successfully coated on the core ketoprofen (KET-gliadin nanocomposite. A monolithic nanocomposite (nanofibers F1 that was generated through traditional blending electrospinning of core fluid was utilized as a control. Scanning electron microscopy demonstrated that both nanofibers F1 and F2 were linear. Transmission electron microscopy verified that nanofibers F2 featured a clear core-sheath nanostructure with a thin sheath layer about 25 nm, whereas their cores and nanofibers F1 were homogeneous KET-gliadin nanocomposites. X-ray diffraction patterns verified that, as a result of fine compatibility, KET was dispersed in gliadin in an amorphous state. In vitro dissolution tests demonstrated that the thin blank nanocoating in nanofibers F2 significantly modified drug release kinetics from a traditional exponential equation of nanofibers F1 to a zero-order controlled release model, linearly freeing 95.7 ± 4.7% of the loaded cargoes over a time period of 16 h.

  1. Electrospun Blank Nanocoating for Improved Sustained Release Profiles from Medicated Gliadin Nanofibers.

    Science.gov (United States)

    Liu, Xinkuan; Shao, Wenyi; Luo, Mingyi; Bian, Jiayin; Yu, Deng-Guang

    2018-03-22

    Nanomaterials providing sustained release profiles are highly desired for efficacious drug delivery. Advanced nanotechnologies are useful tools for creating elaborate nanostructure-based nanomaterials to achieve the designed functional performances. In this research, a modified coaxial electrospinning was explored to fabricate a novel core-sheath nanostructure (nanofibers F2), in which a sheath drug-free gliadin layer was successfully coated on the core ketoprofen (KET)-gliadin nanocomposite. A monolithic nanocomposite (nanofibers F1) that was generated through traditional blending electrospinning of core fluid was utilized as a control. Scanning electron microscopy demonstrated that both nanofibers F1 and F2 were linear. Transmission electron microscopy verified that nanofibers F2 featured a clear core-sheath nanostructure with a thin sheath layer about 25 nm, whereas their cores and nanofibers F1 were homogeneous KET-gliadin nanocomposites. X-ray diffraction patterns verified that, as a result of fine compatibility, KET was dispersed in gliadin in an amorphous state. In vitro dissolution tests demonstrated that the thin blank nanocoating in nanofibers F2 significantly modified drug release kinetics from a traditional exponential equation of nanofibers F1 to a zero-order controlled release model, linearly freeing 95.7 ± 4.7% of the loaded cargoes over a time period of 16 h.

  2. Temperature dependence of the electrical conductivity of vapor grown carbon nanofiber/epoxy composites with different filler dispersion levels

    International Nuclear Information System (INIS)

    Cardoso, P.; Silva, J.; Agostinho Moreira, J.; Klosterman, D.; Hattum, F.W.J. van; Simoes, R.; Lanceros-Mendez, S.

    2012-01-01

    The influence of the dispersion of vapor grown carbon nanofibers (VGCNF) on the electrical properties of VGCNF/epoxy composites has been studied. A homogeneous dispersion of the VGCNF does not imply better electrical properties. The presence of well distributed clusters appears to be a key factor for increasing composite conductivity. It is also shown that the main conduction mechanism has an ionic nature for concentrations below the percolation threshold, while above the percolation threshold it is dominated by hopping between the fillers. Finally, using the granular system theory it is possible to explain the origin of conduction at low temperatures. -- Highlights: ► The influence of dispersion of carbon nanofibers on epoxy is investigated. ► A homogeneous dispersion does not imply better electrical properties. ► The conduction mechanism has an ionic nature below the percolation threshold. ► Above the percolation threshold it is dominated by hopping between the fillers. ► The granular system theory allows explaining conduction at low temperatures.

  3. Temperature dependence of the electrical conductivity of vapor grown carbon nanofiber/epoxy composites with different filler dispersion levels

    Energy Technology Data Exchange (ETDEWEB)

    Cardoso, P. [Center of Physics, University of Minho, Campus de Gualtar, 4710-057 Braga (Portugal); Silva, J. [Center of Physics, University of Minho, Campus de Gualtar, 4710-057 Braga (Portugal); Institute for Polymers and Composites IPC/I3N, University of Minho, Campus de Azurém, 4800-058 Guimares (Portugal); Agostinho Moreira, J. [IFIMUP and IN—Institute of Nanoscience and Nanotechnology, Department of Physics and Astronomy, Faculty of Science, University of Porto, Rua do Campo Alegre, 687, 4169-007 Porto (Portugal); Klosterman, D. [Chemical and Materials Engineering, University of Dayton, 300 College Park, Dayton, OH 45469-0246 (United States); Hattum, F.W.J. van [Institute for Polymers and Composites IPC/I3N, University of Minho, Campus de Azurém, 4800-058 Guimares (Portugal); Simoes, R. [Institute for Polymers and Composites IPC/I3N, University of Minho, Campus de Azurém, 4800-058 Guimares (Portugal); School of Technology, Polytechnic Institute of Cávado and Ave, Campus do IPCA, 4750-810 Barcelos (Portugal); Lanceros-Mendez, S., E-mail: lanceros@fisica.uminho.pt [Center of Physics, University of Minho, Campus de Gualtar, 4710-057 Braga (Portugal); INL—International Iberian Nanotechnology Laboratory, 4715-330 Braga (Portugal)

    2012-10-01

    The influence of the dispersion of vapor grown carbon nanofibers (VGCNF) on the electrical properties of VGCNF/epoxy composites has been studied. A homogeneous dispersion of the VGCNF does not imply better electrical properties. The presence of well distributed clusters appears to be a key factor for increasing composite conductivity. It is also shown that the main conduction mechanism has an ionic nature for concentrations below the percolation threshold, while above the percolation threshold it is dominated by hopping between the fillers. Finally, using the granular system theory it is possible to explain the origin of conduction at low temperatures. -- Highlights: ► The influence of dispersion of carbon nanofibers on epoxy is investigated. ► A homogeneous dispersion does not imply better electrical properties. ► The conduction mechanism has an ionic nature below the percolation threshold. ► Above the percolation threshold it is dominated by hopping between the fillers. ► The granular system theory allows explaining conduction at low temperatures.

  4. Heterogeneous in situ polymerization of polyaniline (PANI) nanofibers on cotton textiles: Improved electrical conductivity, electrical switching, and tuning properties.

    Science.gov (United States)

    Tissera, Nadeeka D; Wijesena, Ruchira N; Rathnayake, Samantha; de Silva, Rohini M; de Silva, K M Nalin

    2018-04-15

    Electrically conductive cotton fabric was fabricated by in situ one pot oxidative polymerization of aniline. Using a simple heterogeneous polymerization method, polyaniline (PANI) nano fibers with an average fiber diameter of 40-75 nm were grafted in situ onto cotton fabric. The electrical conductivity of the PANI nanofiber grafted fabric was improved 10 fold compared to fabric grafted with PANI nanoclusters having an average cluster size of 145-315 nm. The surface morphology of the cotton fibers was characterized using SEM and AFM. Electrical conductivity of PANI nanofibers on the cotton textile was further improved from 76 kΏ/cm to 1 kΏ/cm by increasing the HCl concentration from 1 M to 3 M in the polymerization medium. PANI grafted cotton fabrics were analyzed using FTIR, and the data showed the presence of polyaniline functional groups on the treated fabric. Further evidence was present for the chemical interaction of PANI with cellulose. Dopant level and morphology dependent electron transition behavior of PANI nanostructures grafted on cotton fabric was further characterized using UV-vis spectroscopy. The electrical conductivity of the PANI nano fiber grafted cotton fabric can be tuned by immersing the fabric in pH 2 and pH 6 solutions for multiple cycles. Copyright © 2018. Published by Elsevier Ltd.

  5. Electrospun Polyaniline-Based Composite Nanofibers: Tuning the Electrical Conductivity by Tailoring the Structure of Thiol-Protected Metal Nanoparticles

    Directory of Open Access Journals (Sweden)

    Filippo Pierini

    2017-01-01

    Full Text Available Composite nanofibers made of a polyaniline-based polymer blend and different thiol-capped metal nanoparticles were prepared using ex situ synthesis and electrospinning technique. The effects of the nanoparticle composition and chemical structure on the electrical properties of the nanocomposites were investigated. This study confirmed that Brust’s procedure is an effective method for the synthesis of sub-10 nm silver, gold, and silver-gold alloy nanoparticles protected with different types of thiols. Electron microscopy results demonstrated that electrospinning is a valuable technique for the production of composite nanofibers with similar morphology and revealed that nanofillers are well-dispersed into the polymer matrix. X-ray diffraction tests proved the lack of a significant influence of the nanoparticle chemical structure on the polyaniline chain arrangement. However, the introduction of conductive nanofillers in the polymer matrix influences the charge transport noticeably improving electrical conductivity. The enhancement of electrical properties is mediated by the nanoparticle capping layer structure. The metal nanoparticle core composition is a key parameter, which exerted a significant influence on the conductivity of the nanocomposites. These results prove that the proposed method can be used to tune the electrical properties of nanocomposites.

  6. Highly Conductive, Mechanically Robust, and Electrochemically Inactive TiC/C Nanofiber Scaffold for High-Performance Silicon Anode Batteries

    KAUST Repository

    Yao, Yan; Huo, Kaifu; Hu, Liangbing; Liu, Nian; Cha, Judy J.; McDowell, Matthew T.; Chu, Paul K.; Cui, Yi

    2011-01-01

    Silicon has a high specific capacity of 4200 mAh/g as lithium-ion battery anodes, but its rapid capacity fading due to >300% volume expansion and pulverization presents a significant challenge for practical applications. Here we report a core-shell TiC/C/Si inactive/active nanocomposite for Si anodes demonstrating high specific capacity and excellent electrochemical cycling. The amorphous silicon layer serves as the active material to store Li+, while the inactive TiC/C nanofibers act as a conductive and mechanically robust scaffold for electron transport during the Li-Si alloying process. The core-shell TiC/C/Si nanocomposite anode shows ∼3000 mAh g-1 discharge capacity and 92% capacity retention after 100 charge/discharge cycles. The excellent cycling stability and high rate performance could be attributed to the tapering of the nanofibers and the open structure that allows facile Li ion transport and the high conductivity and mechanical stability of the TiC/C scaffold. © 2011 American Chemical Society.

  7. Highly Conductive, Mechanically Robust, and Electrochemically Inactive TiC/C Nanofiber Scaffold for High-Performance Silicon Anode Batteries

    KAUST Repository

    Yao, Yan

    2011-10-25

    Silicon has a high specific capacity of 4200 mAh/g as lithium-ion battery anodes, but its rapid capacity fading due to >300% volume expansion and pulverization presents a significant challenge for practical applications. Here we report a core-shell TiC/C/Si inactive/active nanocomposite for Si anodes demonstrating high specific capacity and excellent electrochemical cycling. The amorphous silicon layer serves as the active material to store Li+, while the inactive TiC/C nanofibers act as a conductive and mechanically robust scaffold for electron transport during the Li-Si alloying process. The core-shell TiC/C/Si nanocomposite anode shows ∼3000 mAh g-1 discharge capacity and 92% capacity retention after 100 charge/discharge cycles. The excellent cycling stability and high rate performance could be attributed to the tapering of the nanofibers and the open structure that allows facile Li ion transport and the high conductivity and mechanical stability of the TiC/C scaffold. © 2011 American Chemical Society.

  8. Electrochemical properties for high surface area and improved electrical conductivity of platinum-embedded porous carbon nanofibers

    Science.gov (United States)

    An, Geon-Hyoung; Ahn, Hyo-Jin; Hong, Woong-Ki

    2015-01-01

    Four different types of carbon nanofibers (CNFs) for electrical double-layer capacitors (EDLCs), porous and non-porous CNFs with and without Pt metal nanoparticles, are synthesized by an electrospinning method and their performance in electrical double-layer capacitors (EDLCs) is characterized. In particular, the Pt-embedded porous CNFs (PCNFs) exhibit a high specific surface area of 670 m2 g-1, a large mesopore volume of 55.7%, and a low electrical resistance of 1.7 × 103. The synergistic effects of the high specific surface area with a large mesopore volume, and superior electrical conductivity result in an excellent specific capacitance of 130.2 F g-1, a good high-rate performance, superior cycling durability, and high energy density of 16.9-15.4 W h kg-1 for the performance of EDLCs.

  9. Highest recorded electrical conductivity and microstructure in polypropylene-carbon nanotubes composites and the effect of carbon nanofibers addition

    Science.gov (United States)

    Ramírez-Herrera, C. A.; Pérez-González, J.; Solorza-Feria, O.; Romero-Partida, N.; Flores-Vela, A.; Cabañas-Moreno, J. G.

    2018-04-01

    In the last decade, numerous investigations have been devoted to the preparation of polypropylene-multiwalled carbon nanotubes (PP/MWCNT) nanocomposites having enhanced properties, and in particular, high electrical conductivities (> 1 S cm-1). The present work establishes that the highest electrical conductivity in PP/MWCNT nanocomposites is limited by the amount of nanofiller content which can be incorporated in the polymer matrix, namely, about 20 wt%. This concentration of MWCNT in PP leads to a maximum electrical conductivity slightly lower than 8 S cm-1, but only by assuring an adequate combination of dispersion and spatial distribution of the carbon nanotubes. The realization of such an optimal microstructure depends on the characteristics of the production process of the PP/MWCNT nanocomposites; in our experiments, involving composite fabrication by melt mixing and hot pressing, a second re-processing cycle is shown to increase the electrical conductivity values by up to two orders of magnitude, depending on the MWCNT content of the nanocomposite. A modest increase of the highest electrical conductivity obtained in nanocomposites with 21.5 wt% MWCNT content has been produced by the combined use of carbon nanofibers (CNF) and MWCNT, so that the total nanofiller content was increased to 30 wt% in the nanocomposite with PP—15 wt% MWCNT—15 wt%CNF.

  10. Electrospun conducting polymer nanofibers as the active material in sensors and diodes

    International Nuclear Information System (INIS)

    Pinto, Nicholas J

    2013-01-01

    Polyaniline doped with camphorsulfonic acid (PANi-HCSA) and poly(3,4-ethylenedioxythiophene) doped with polystyrene sulfonic acid (PEDOT-PSSA) were electrospun separately to obtain individual nanofibers which were captured on Si/SiO 2 substrates and electrically characterized. The fiber resistance was recorded as a function of time in the presence of vapours of aliphatic alcohols of varying sizes. Due to the large surface to volume ratio, uniform diameter and small quantity of active material used in the construction, these sensor responses are very quick. Sensors made from individual fibers also show true saturation upon exposure to and removal of the sensing gas. A Schottky diode was also fabricated using an n-doped Si/SiO 2 substrate and a single PANi-HCSA fiber and tested in vacuum and in ammonia gas. The diode response was instantaneous upon exposure to ammonia with nearly complete recovery of the current upon pumping out the ammonia, thereby making it a reusable sensor with rectifying behaviour i.e. multifunctional.

  11. Vacuum-assisted bilayer PEDOT:PSS/cellulose nanofiber composite film for self-standing, flexible, conductive electrodes.

    Science.gov (United States)

    Ko, Youngsang; Kim, Dabum; Kim, Ung-Jin; You, Jungmok

    2017-10-01

    Sustainable cellulose nanofiber (CNF)-based composites as functional conductive materials have garnered considerable attention recently for their use in soft electronic devices. In this work, self-standing, highly flexible, and conductive PEDOT:PSS-CNF composite films were developed using a simple vacuum-assisted filtration method. Two different composite films were successfully fabricated and then tested: 1) a single-layer composite composed of a mixture of PEDOT:PSS and CNF phases and 2) a bilayer composite composed of an upper PEDOT:PSS membrane layer and a CNF matrix sub-layer. The latter composite was constructed by electrostatic/hydrogen bonding interactions between PEDOT:PSS and CNFs coupled with sequential vacuum-assisted filtration. Our results demonstrated that the resultant bilayer composite film exhibited a competitive electrical conductivity (ca. 22.6Scm -1 ) compared to those of previously reported cellulose-based composites. Furthermore, decreases in the electrical properties were not observed in the composite films when they were bent up to 100 times at an angle of 180° and bent multiple times at an angle of 90°, clearly demonstrating their excellent mechanical flexibility. This study provides a straightforward method of fabricating highly flexible, lightweight, and conductive films, which have the potential to be used in high-performance soft electronic systems. Copyright © 2017 Elsevier Ltd. All rights reserved.

  12. Alignment of Boron Nitride Nanofibers in Epoxy Composite Films for Thermal Conductivity and Dielectric Breakdown Strength Improvement.

    Science.gov (United States)

    Wang, Zhengdong; Liu, Jingya; Cheng, Yonghong; Chen, Siyu; Yang, Mengmeng; Huang, Jialiang; Wang, Hongkang; Wu, Guanglei; Wu, Hongjing

    2018-04-15

    Development of polymer-based composites with simultaneously high thermal conductivity and breakdown strength has attracted considerable attention owing to their important applications in both electronic and electric industries. In this work, boron nitride (BN) nanofibers (BNNF) are successfully prepared as fillers, which are used for epoxy composites. In addition, the BNNF in epoxy composites are aligned by using a film casting method. The composites show enhanced thermal conductivity and dielectric breakdown strength. For instance, after doping with BNNF of 2 wt%, the thermal conductivity of composites increased by 36.4% in comparison with that of the epoxy matrix. Meanwhile, the breakdown strength of the composite with 1 wt% BNNF is 122.9 kV/mm, which increased by 6.8% more than that of neat epoxy (115.1 kV/mm). Moreover, the composites have maintained a low dielectric constant and alternating current conductivity among the range of full frequency, and show a higher thermal decomposition temperature and glass-transition temperature. The composites with aligning BNNF have wide application prospects in electronic packaging material and printed circuit boards.

  13. In-situ Plasticized Cross-linked Polymer Composite Electrolyte Enhanced with Lithium-ion Conducting Nanofibers for Ambient All-Solid-State Lithium-ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Chaoyi; Zhu, Pei; Jia, Hao; Zhu, Jiadeng; Selvan, R. Kalai; Li, Ya; Dong, Xia; Du, Zhuang; Angunawela, Indunil; Wu, Nianqiang; Dirican, Mahmut

    2018-04-29

    Solid electrolytes have been gaining attention recently for the development of next-generation Li-ion batteries due to the substantial improvements in stability and safety. Among various types of solid electrolytes, composite solid electrolytes (CSEs) exhibit both high ionic conductivity and excellent interfacial contact with the electrodes. Incorporating active nanofibers into the polymer matrix demonstrates an effective method to fabricate CSEs. However, current CSEs based on traditional poly(ethylene oxide) (PEO) polymer suffer from the poor ionic conductivity of PEO and agglomeration effect of inorganic fillers at high concentrations, which limit further improvements in Li+ conductivity and electrochemical stability. Herein, we synthesize a novel PEO based cross-linked polymer (CLP) as the polymer matrix with naturally amorphous structure and high room-temperature ionic conductivity of 2.40 × 10-4 S cm-1. Li0.3La0.557TiO3 (LLTO) nanofibers incorporated composite solid electrolytes (L-CLPCSE) exhibit enhanced ionic conductivity without showing filler agglomeration. The high content of Li-conductive nanofibers improves the mechanical strength, ensures the conductive networks, and increases the total Li+ conductivity to 3.31 × 10-4 S cm-1. The all-solid-state Li|LiFePO4 batteries with L-CLPCSE are able to deliver attractive specific capacity of 147 mAh g-1 at room temperature, and no evident dendrite is found at the anode/electrolyte interface after 100 cycles.

  14. Electrical bistability in conductive hybrid composites of doped polyaniline nanofibers-gold nanoparticles capped with dodecane thiol.

    Science.gov (United States)

    Borriello, A; Agoretti, P; Cassinese, A; D'Angelo, P; Mohanraj, G T; Sanguigno, L

    2009-11-01

    A novel electrical bistable hybrid nanocomposite based on doped Polyaniline nanofibers with 1-Dodecanethiol-protected Gold nanoparticle (PAni.AuDT), 3-4 nm in size, as the conductive component and polystyrene as polymer matrix was prepared. The structural morphology of the composite and the dispersion of nanoparticles inside it were evaluated using Transmission Electron Microscopy (TEM). The thermal stability and the ratio Polyaniline/Gold nanoparticles in the composite were determined by using thermogravimetric analysis. The electrical bistability of the PAni.AuDT-PS composite, the influence of the dispersion of the PAni.AuDT conductive network and the basic operation mechanism, have been assessed by measuring the electrical response of planar device architectures, also as a function of the environmental temperature (in the range 200 K K). The basic operation mechanism of the hybrid compound has been then correlated to the combined action of the thermally-induced scattering of charge carriers and the thermal contraction of the hosting polymeric matrix. Moreover, the right compromise between these two effects in terms of the most efficient bistability has been studied, founding the concentration of the conductive component which optimizes the device on-off ratio (I(on)/ I(off)).

  15. Electrospun Nanofibers: New Concepts, Materials, and Applications.

    Science.gov (United States)

    Xue, Jiajia; Xie, Jingwei; Liu, Wenying; Xia, Younan

    2017-08-15

    Electrospinning is a simple and versatile technique that relies on the electrostatic repulsion between surface charges to continuously draw nanofibers from a viscoelastic fluid. It has been applied to successfully produce nanofibers, with diameters down to tens of nanometers, from a rich variety of materials, including polymers, ceramics, small molecules, and their combinations. In addition to solid nanofibers with a smooth surface, electrospinning has also been adapted to generate nanofibers with a number of secondary structures, including those characterized by a porous, hollow, or core-sheath structure. The surface and/or interior of such nanofibers can be further functionalized with molecular species or nanoparticles during or after an electrospinning process. In addition, electrospun nanofibers can be assembled into ordered arrays or hierarchical structures by manipulation of their alignment, stacking, and/or folding. All of these attributes make electrospun nanofibers well-suited for a broad spectrum of applications, including those related to air filtration, water purification, heterogeneous catalysis, environmental protection, smart textiles, surface coating, energy harvesting/conversion/storage, encapsulation of bioactive species, drug delivery, tissue engineering, and regenerative medicine. Over the past 15 years, our group has extensively explored the use of electrospun nanofibers for a range of applications. Here we mainly focus on two examples: (i) use of ceramic nanofibers as catalytic supports for noble-metal nanoparticles and (ii) exploration of polymeric nanofibers as scaffolding materials for tissue regeneration. Because of their high porosity, high surface area to volume ratio, well-controlled composition, and good thermal stability, nonwoven membranes made of ceramic nanofibers are terrific supports for catalysts based on noble-metal nanoparticles. We have investigated the use of ceramic nanofibers made of various oxides, including SiO 2 , TiO 2

  16. Hierarchically Three-Dimensional Nanofiber Based Textile with High Conductivity and Biocompatibility As a Microbial Fuel Cell Anode.

    Science.gov (United States)

    Tao, Yifei; Liu, Qiongzhen; Chen, Jiahui; Wang, Bo; Wang, Yuedan; Liu, Ke; Li, Mufang; Jiang, Haiqing; Lu, Zhentan; Wang, Dong

    2016-07-19

    Microbial fuel cells (MFCs) encompass complex bioelectrocatalytic reactions that converting chemical energy of organic compounds to electrical energy. Improving the anode configuration is thought to be a critical step for enhancing MFCs performance. In present study, a hierarchically structured textile polypyrrole/poly(vinyl alcohol-co-polyethylene) nanofibers/poly(ethylene terephthalate) (referred to PPy/NFs/PET) is shown to be excellent anode for MFCs. This hierarchical PPy/NFs/PET anode affords an open porous and three-dimensional interconnecting conductive scaffold with larger surface roughness, facilitating microbial colonization and electron transfer from exoelectrogens to the anode. The mediator-less MFC equipped with PPy/NFs/PET anode achieves a remarkable maximum power density of 2420 mW m(-2) with Escherichia coli as the microbial catalyst at the current density of 5500 mA m(-2), which is approximately 17 times higher compared to a reference anode PPy/PET (144 mW m(-2)). Considering the low cost, low weight, facile fabrication, and good winding, this PPy/NFs/PET textile anode promises a great potential for high-performance and cost-effective MFCs in a large scale.

  17. Cobalt Oxide Porous Nanofibers Directly Grown on Conductive Substrate as a Binder/Additive-Free Lithium-Ion Battery Anode with High Capacity.

    Science.gov (United States)

    Liu, Hao; Zheng, Zheng; Chen, Bochao; Liao, Libing; Wang, Xina

    2017-12-01

    In order to reduce the amount of inactive materials, such as binders and carbon additives in battery electrode, porous cobalt monoxide nanofibers were directly grown on conductive substrate as a binder/additive-free lithium-ion battery anode. This electrode exhibited very high specific discharging/charging capacities at various rates and good cycling stability. It was promising as high capacity anode materials for lithium-ion battery.

  18. Achieving a Collapsible, Strong, and Highly Thermally Conductive Film Based on Oriented Functionalized Boron Nitride Nanosheets and Cellulose Nanofiber.

    Science.gov (United States)

    Wu, Kai; Fang, Jinchao; Ma, Jinrui; Huang, Rui; Chai, Songgang; Chen, Feng; Fu, Qiang

    2017-09-06

    Boron nitride nanosheet (BNNS) films receive wide attention in both academia and industry because of their high thermal conductivity (TC) and good electrical insulation capability. However, the brittleness and low strength of the BNNS film largely limit its application. Herein, functionalized BNNSs (f-BNNSs) with a well-maintained in-plane crystalline structure were first prepared utilizing urea in the aqueous solution via ball-milling for the purpose of improving their stability in water and enhancing the interaction with the polymer matrix. Then, a biodegradable and highly thermally conductive film with an orderly oriented structure based on cellulose nanofibers (CNFs) and f-BNNSs was prepared just by simple vacuum-assisted filtration. The modification of the BNNS and the introduction of the CNF result in a better orientation of the f-BNNS, sufficient connection between f-BNNS themselves, and strong interaction between f-BNNS and CNF, which not only make the prepared composite film strong and tough but also possess higher in-plane TC. An increase of 70% in-plane TC, 63.2% tensile strength, and 77.8% elongation could be achieved for CNF/f-BNNS films, compared with that for CNF/BNNS films at the filler content of 70%. Although at such a high f-BNNS content, this composite film can be bended and folded. It is even more interesting to find that the in-plane TC could be greatly enhanced with the decrease of the thickness of the film, and a value of 30.25 W/m K can be achieved at the thickness of ∼30 μm for the film containing 70 wt % f-BNNS. We believe that this highly thermally conductive film with good strength and toughness could have potential applications in next-generation highly powerful and collapsible electronic devices.

  19. Biocompatibility Assessment of Conducting PANI/Chitosan Nanofibers for Wound Healing Applications

    Directory of Open Access Journals (Sweden)

    Panagiota Moutsatsou

    2017-12-01

    Full Text Available As electroactive polymers have recently presented potential in applications in the tissue engineering and biomedical field, this study is aiming at the fabrication of composite nanofibrous membranes containing conducting polyaniline and at the evaluation of their biocompatibility. For that purpose, conducting polyaniline–chitosan (PANI/CS defect free nanofibres of different ratios (1:3; 3:5 and 1:1 were produced with the electrospinning method. They were characterized as for their morphology, hydrophilicity and electrical conductivity. The membranes were then evaluated for their cellular biocompatibility in terms of cell attachment, morphology and cell proliferation. The effect of the PANI content on the membrane properties is discussed. Increase in PANI content resulted in membranes with higher hydrophobicity and higher electrical conductivity. It was found that none of the membranes showed any toxic effects on osteoblasts and fibroblasts, and that they all supported cell attachment and growth, even to a greater extent than tissue culture plastic. The membrane with the PANI/CS ratio 1:3 supports better cell attachment and proliferation for both cell lines due to a synergistic effect of hydrophilicity retention due to the high chitosan content and the conductivity that PANI introduced to the membrane.

  20. Electrospun Gallium Nitride Nanofibers

    International Nuclear Information System (INIS)

    Melendez, Anamaris; Morales, Kristle; Ramos, Idalia; Campo, Eva; Santiago, Jorge J.

    2009-01-01

    The high thermal conductivity and wide bandgap of gallium nitride (GaN) are desirable characteristics in optoelectronics and sensing applications. In comparison to thin films and powders, in the nanofiber morphology the sensitivity of GaN is expected to increase as the exposed area (proportional to the length) increases. In this work we present electrospinning as a novel technique in the fabrication of GaN nanofibers. Electrospinning, invented in the 1930s, is a simple, inexpensive, and rapid technique to produce microscopically long ultrafine fibers. GaN nanofibers are produced using gallium nitrate and dimethyl-acetamide as precursors. After electrospinning, thermal decomposition under an inert atmosphere is used to pyrolyze the polymer. To complete the preparation, the nanofibers are sintered in a tube furnace under a NH 3 flow. Both scanning electron microscopy and profilometry show that the process produces continuous and uniform fibers with diameters ranging from 20 to a few hundred nanometers, and lengths of up to a few centimeters. X-ray diffraction (XRD) analysis shows the development of GaN nanofibers with hexagonal wurtzite structure. Future work includes additional characterization using transmission electron microscopy and XRD to understand the role of precursors and nitridation in nanofiber synthesis, and the use of single nanofibers for the construction of optical and gas sensing devices.

  1. Frequency and voltage dependent profile of dielectric properties, electric modulus and ac electrical conductivity in the PrBaCoO nanofiber capacitors

    Directory of Open Access Journals (Sweden)

    S. Demirezen

    Full Text Available In this study, praseodymium barium cobalt oxide nanofiber interfacial layer was sandwiched between Au and n-Si. Frequency and voltage dependence of ε′, ε′, tanδ, electric modulus (M′ and M″ and σac of PrBaCoO nanofiber capacitor have been investigated by using impedance spectroscopy method. The obtained experimental results show that the values of ε′, ε′, tanδ, M′, M″ and σac of the PrBaCoO nanofiber capacitor are strongly dependent on frequency of applied bias voltage. The values of ε′, ε″ and tanδ show a steep decrease with increasing frequency for each forward bias voltage, whereas the values of σac and the electric modulus increase with increasing frequency. The high dispersion in ε′ and ε″ values at low frequencies may be attributed to the Maxwell–Wagner and space charge polarization. The high values of ε′ may be due to the interfacial effects within the material, PrBaCoO nanofibers interfacial layer and electron effect. The values of M′ and M″ reach a maximum constant value corresponding to M∞ ≈ 1/ε∞ due to the relaxation process at high frequencies, but both the values of M′ and M″ approach almost to zero at low frequencies. The changes in the dielectric and electrical properties with frequency can be also attributed to the existence of Nss and Rs of the capacitors. As a result, the change in the ε′, ε″, tanδ, M′, M″ and ac electric conductivity (σac is a result of restructuring and reordering of charges at the PrBaCoO/n-Si interface under an external electric field or voltage and interface polarization. Keywords: Thin films, Electrical properties, Interface/interphase

  2. The Chemical Deposition Method for the Decoration of Palladium Particles on Carbon Nanofibers with Rapid Conductivity Changes

    Directory of Open Access Journals (Sweden)

    Hoik Lee

    2016-11-01

    Full Text Available Palladium (Pd metal is well-known for hydrogen sensing material due to its high sensitivity and selectivity toward hydrogen, and is able to detect hydrogen at near room temperature. In this work, palladium-doped carbon nanofibers (Pd/CNFs were successfully produced in a facile manner via electrospinning. Well-organized and uniformly distributed Pd was observed in microscopic images of the resultant nanofibers. Hydrogen causes an increment in the volume of Pd due to the ability of hydrogen atoms to occupy the octahedral interstitial positions within its face centered cubic lattice structure, resulting in the resistance transition of Pd/CNFs. The resistance variation was around 400%, and it responded rapidly within 1 min, even in 5% hydrogen atmosphere conditions at room temperature. This fibrous hybrid material platform will open a new and practical route and stimulate further researches on the development of hydrogen sensing materials with rapid response, even to low concentrations of hydrogen in an atmosphere.

  3. Solid-state poly(ethylene glycol)-polyurethane/polymethylmethacrylate/rutile TiO2 nanofiber composite electrolyte-correlation between morphology and conducting properties

    International Nuclear Information System (INIS)

    Chilaka, Naresh; Ghosh, Sutapa

    2012-01-01

    Highlights: ► Semi IPN composite of PEG-PU/PMMA with different wt% of rutile TiO 2 is synthesized. ► Formation of nanocomposite is confirmed by SEM, XRD and IR spectroscopic analysis. ► DSC and TGA confirmed the enhanced thermal stability of the composite. ► Composite with 18 wt% rutile TiO 2 is found to be the best conducting material. - Abstract: A series of lithium electrolyte materials based on hybrid of semi Inter penetrating Polymer Network of [poly(ethylene glycol)-polyurethane-polymethylmethacrylate] [60:40] and TiO 2 nanofibers is described. TiO 2 nanofibers are made by simple solvothermal procedure. Rutile phase of TiO 2 and its fibrous morphology are confirmed by X-ray diffraction pattern and scanning electron microscopy image respectively. Semi Inter penetrating Polymer Network of polyethylene glycol-polyurethane/polymethylmethacrylate with LiClO 4 and its nanocomposite with different weight percent of TiO 2 nano fibers have been synthesized. The formation of Inter penetrating Polymer Network and its amorphous nature are confirmed by Fourier transform infrared spectra, X-ray diffraction pattern and differential scanning calorimetry results. Thermo gravimetric analysis shows enhanced thermal stability of the composite compared to the semi Inter penetrating Polymer Network system. The electrical characterizations of the nanocomposites are done by current–voltage (I–V) measurements and impedance spectroscopy. These results confirm that incorporation of TiO 2 nanofibers by 18% enhances the conductivity of the Inter penetrating Polymer Network system by ten times . The nanoscale structure of the inorganic material is found to be responsible for the bulk properties of the system, especially those that differ from the properties of similar, pure salt-in-polymer electrolytes. Further differential scanning calorimetry, scanning electron microscopy and impedance data confirm the presence of two polymeric phases in the semi Inter penetrating Polymer

  4. Fabrication of Carbon Nanotube Polymer Actuator Using Nanofiber Sheet

    Science.gov (United States)

    Kato, Hayato; Shimizu, Akikazu; Sato, Taiga; Kushida, Masahito

    2017-11-01

    Carbon nanotube polymer actuators were developed using composite nanofiber sheets fabricated by multi-walled carbon nanotubes(MWCNTs) and poly (vinylidene fluoride-co-hexafluoropropylene) (PVDF-HFP). Nanofiber sheets were fabricated by electrospinning method. The effect of flow rate and polymer concentration on nanofiber formation were verified for optimum condition for fabricating nanofiber sheets. We examined the properties of MWCNT/PVDF-HFP nanofiber sheets, as follows. Electrical conductivity and mechanical strength increased as the MWCNT weight ratio increased. We fabricated carbon nanotube polymer actuators using MWCNT/PVDF-HFP nanofiber sheets and succeeded in operating of our actuators.

  5. Conductive framework supported high rate performance of SnO2 hollow nanofibers for lithium battery anodes

    International Nuclear Information System (INIS)

    Pham-Cong, De; Kim, Ji Yoon; Park, Jung Soo; Kim, Jae Hyun; Kim, Jong-Pil; Jeong, Euh-Duck; Kim, Jinwoo; Jeong, Se-Young; Cho, Chae-Ryong

    2015-01-01

    We synthesized an electrospun SnO 2 hollow nanofibers (SnO 2 hNFs) coated with carbon and wrapped with graphene oxide layer by simple hydrothermal and electrostatic force method, respectively. Thin carbon layer as electrolyte blocking layer was formed on the SnO 2 hNFs by using glucose as a carbon source (SnO 2 @C hNFs). Also, layers of graphene oxide are wrapped on SnO 2 @C hNFs by the electrostatic interaction force (SnO 2 @C@G hNFs). At high C rate, the average capacity of the SnO 2 @C@G hNFs still kept high capacity comparing with the SnO 2 hNFs and SnO 2 @C hNFs and then increased above 250% at 3 C. It also exhibits a greatly enhanced synergic effect with an extremely high lithium storage capability up to 1,600 mA h g −1 and kept 900 mA h g −1 after 50 cycles benefiting from the advanced structural features

  6. Magnetite (Fe{sub 3}O{sub 4})-filled carbon nanofibers as electro-conducting/superparamagnetic nanohybrids and their multifunctional polymer composites

    Energy Technology Data Exchange (ETDEWEB)

    Das, Arindam; Raffi, Muhammad; Megaridis, Constantine, E-mail: cmm@uic.edu [University of Illinois at Chicago, Department of Mechanical and Industrial Engineering (United States); Fragouli, Despina [Istituto Italiano di Tecnologia, Smart Materials, Nanophysics (Italy); Innocenti, Claudia [Universita di Firenze, INSTM Research Unit and Department of Chemistry (Italy); Athanassiou, Athanassia [Istituto Italiano di Tecnologia, Smart Materials, Nanophysics (Italy)

    2015-01-15

    A mild-temperature, nonchemical technique is used to produce a nanohybrid multifunctional (electro-conducting and magnetic) powder material by intercalating iron oxide nanoparticles in large aspect ratio, open-ended, hollow-core carbon nanofibers (CNFs). Single-crystal, superparamagnetic Fe{sub 3}O{sub 4} nanoparticles (10 nm average diameter) filled the CNF internal cavity (diameter <100 nm) after successive steps starting with dispersion of CNFs and magnetite nanoparticles in aqueous or organic solvents, sequencing or combining sonication-assisted capillary imbibition and concentration-driven diffusion, and finally drying at mild temperatures. The influence of several process parameters—such as sonication type and duration, concentration of solids dispersed in solvent, CNF-to-nanoparticle mass ratio, and drying temperature—on intercalation efficiency (evaluated in terms of particle packing in the CNF cavity) was studied using electron microscopy. The magnetic CNF powder was used as a low-concentration filler in poly(methyl methacrylate) to demonstrate thin free-standing polymer films with simultaneous magnetic and electro-conducting properties. Such films could be implemented in sensors, optoelectromagnetic devices, or electromagnetic interference shields.

  7. Amorphous V-O-C composite nanofibers electrospun from solution precursors as binder- and conductive additive-free electrodes for supercapacitors with outstanding performance

    Science.gov (United States)

    Chen, Xia; Zhao, Bote; Cai, Yong; Tadé, Moses O.; Shao, Zongping

    2013-11-01

    Flexible V-O-C composite nanofibers were fabricated from solution precursors via electrospinning and were investigated as free-standing and additive-free film electrodes for supercapacitors. Specifically, composite nanofibers (V0, V5, V10 and V20) with different vanadyl acetylacetonate (VO(acac)2) contents of 0, 5, 10 and 20 wt% with respect to polyacrylonitrile (PAN) were prepared. The composite nanofibers were comparatively studied using XRD, Raman spectroscopy, XPS, N2 adsorption-desorption, FE-SEM, TEM and S-TEM. The vanadium element was found to be well-dispersed in the carbon nanofibers, free from the formation of an aggregated crystalline phase, even in the case of V20. A specific surface area of 587.9 m2 g-1 was reached for V10 after calcination, which is approximately twice that of the vanadium-free carbon nanofibers (V0, 300.9 m2 g-1). To perform as an electrode for supercapacitors in an aqueous electrolyte, the V10 film delivered a specific capacitance of 463 F g-1 at 1 A g-1. V10 was also able to retain a specific capacitance of 380 F g-1, even at a current density of 10 A g-1. Additionally, very stable cycling stability was achieved, maintaining an outstanding specific capacitance of 400 F g-1 at 5 A g-1 after charge-discharge cycling 5000 times. Thus, V-O-C composite nanofibers are highly attractive electrode materials for flexible, high-power, thin film energy storage devices and applications.Flexible V-O-C composite nanofibers were fabricated from solution precursors via electrospinning and were investigated as free-standing and additive-free film electrodes for supercapacitors. Specifically, composite nanofibers (V0, V5, V10 and V20) with different vanadyl acetylacetonate (VO(acac)2) contents of 0, 5, 10 and 20 wt% with respect to polyacrylonitrile (PAN) were prepared. The composite nanofibers were comparatively studied using XRD, Raman spectroscopy, XPS, N2 adsorption-desorption, FE-SEM, TEM and S-TEM. The vanadium element was found to be well

  8. Fabrication of high conductivity dual multi-porous poly (L-lactic acid)/polypyrrole composite micro/nanofiber film

    International Nuclear Information System (INIS)

    Yu Qiaozhen; Dai Zhengwei; Lan Ping

    2011-01-01

    Highlights: → PLLA/H 2 SO 4 -doped PPy composite micro/nano fibers dual multi-pore membranes with high conductivity were fabricated by combining electrospinning with in situ polymerization.These composite fibers have a core-shell structure, the PPy is the core and the PLLA/PPy is the shell. → The size and shape of the pores in this PPy composite fiber membrane can be tuned by polymerization parameters. The largest size of the pores is about 250 μm. → The conductivity of this composite fiber membrane can be adjusted by polymerization parameters. The highest conductivity is 179.0 S cm -1 . The PLLA fibers act as the template in the pyrrole polymerization process and contributed to the increase of the conductivity. - Abstract: Dual multi-porous PLLA (poly(L-lactic acid))/H 2 SO 4 -doped PPy (polypyrrole) composite micro/nano fiber films were fabricated by combining electrospinning with in situ polymerization. The morphologies and structures of the resulting samples were analyzed by scanning electron microscopy (SEM). It was found that the composite micro/nano fibers exhibited a core-shell structure and the composite fiber film had a dual multi-pore structure composed of pores both in the fibers and among the fibers. Semiconductor parameter analyzer was used to characterize the electrical properties of the samples. It was interesting to find that all the PLLA/H 2 SO 4 -doped PPy composite micro/nano fiber films had higher conductivity than H 2 SO 4 -doped PPy particles when the polymerization time up to 180 min. Effects of the pyrrole synthesis conditions on the pore size and the conductivity of PLLA/PPy composite fiber film were assessed. By optimizing the polymerization conditions, the max conductivity of this composite fiber film was about 179.0 S cm -1 with a pore size of about 250 μm. The possible mechanism of PLLA/H 2 SO 4 -doped PPy composite micro/nano fiber films had much higher conductivity than H 2 SO 4 -doped PPy particles was discussed.

  9. Electrical Impedance Measurements of PZT Nanofiber Sensors

    Directory of Open Access Journals (Sweden)

    Richard Galos

    2017-01-01

    Full Text Available Electrical impedance measurements of PZT nanofiber sensors were performed using a variety of methods over a frequency spectrum ranging from DC to 1.8 GHz. The nanofibers formed by electrospinning with diameters ranging from 10 to 150 nm were collected and integrated into sensors using microfabrication techniques. Special matching circuits with ultrahigh input impedance were fabricated to produce low noise, measurable sensor outputs. Material properties including resistivity and dielectric constant are derived from the impedance measurements. The resulting material properties are also compared with those of individual nanofibers being tested using conductive AFM and Scanning Conductive Microscopy.

  10. Electrochemical fabrication and electronic behavior of polypyrrole nano-fiber array devices

    International Nuclear Information System (INIS)

    Liu Ling; Zhao Yaomin; Jia Nengqin; Zhou Qin; Zhao Chongjun; Yan Manming; Jiang Zhiyu

    2006-01-01

    Electrochemically active Polypyrrole (PPy) nano-fiber array device was fabricated via electrochemical deposition method using aluminum anodic oxide (AAO) membrane as template. After alkaline treatment electrochemically active PPy nano-fiber lost electrochemical activity, and became electrochemically inactive PPy. The electronic properties of PPy nano-fiber array devices were measured by means of a simple method. It was found that for an indium-tin oxide/electrochemically inactive PPy nano-fiber device, the conductivity of nano-fiber increased with the increase of voltage applied on the two terminals of nano-fiber. The electrochemical inactive PPy nano-fiber might be used as a nano-fiber switching diode. Both Au/electrochemically active PPy and Au/electrochemically inactive PPy nano-fiber devices demonstrate rectifying behavior, and might have been used for further application as nano-rectifiers

  11. Electrochemical fabrication and electronic behavior of polypyrrole nano-fiber array devices

    Energy Technology Data Exchange (ETDEWEB)

    Ling, Liu [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China); Yaomin, Zhao [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China); Nengqin, Jia [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China); Qin, Zhou [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China); Chongjun, Zhao [Photon Craft Project, Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences and Japan Science and Technology Agency, Shanghai 201800 (China); Manming, Yan [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China); Zhiyu, Jiang [Department of Chemistry, and Shanghai Key Laboratory of Molecular Catalysis and Innovative Materials, Fudan University, Shanghai 200433 (China)

    2006-05-01

    Electrochemically active Polypyrrole (PPy) nano-fiber array device was fabricated via electrochemical deposition method using aluminum anodic oxide (AAO) membrane as template. After alkaline treatment electrochemically active PPy nano-fiber lost electrochemical activity, and became electrochemically inactive PPy. The electronic properties of PPy nano-fiber array devices were measured by means of a simple method. It was found that for an indium-tin oxide/electrochemically inactive PPy nano-fiber device, the conductivity of nano-fiber increased with the increase of voltage applied on the two terminals of nano-fiber. The electrochemical inactive PPy nano-fiber might be used as a nano-fiber switching diode. Both Au/electrochemically active PPy and Au/electrochemically inactive PPy nano-fiber devices demonstrate rectifying behavior, and might have been used for further application as nano-rectifiers.

  12. PLLA-PEG-TCH-labeled bioactive molecule nanofibers for tissue engineering

    Directory of Open Access Journals (Sweden)

    Chen J

    2011-10-01

    Full Text Available Jun Chen1,2, Beth Zhou1–3, Qi Li1,2, Jun Ouyang4, Jiming Kong2,4,5, Wen Zhong3,6, Malcolm MQ Xing1,2,4,71Department of Mechanical Engineering, Faculty of Engineering, University of Manitoba, Winnipeg, MB, Canada; 2Manitoba Institute of Child Health, Winnipeg, MB, Canada; 3Department of Textile Sciences, Faculty of Human Ecology, University of Manitoba, Winnipeg, MB, Canada; 4School of Basic Medical Science, Southern Medical University, Guangzhoug, China; 5Department of Human Anatomy and Cell Sciences, 6Department of Medical Microbiology, Faculty of Medicine, 7Department of Biochemistry and Medical Genetics, Faculty of Medicine, University of Manitoba, Winnipeg, MB, CanadaAbstract: By mimicking the native extracellular matrix, electrospun nanofibrous scaffolds (ENSs can provide both chemical and physical cues to modulate cell adherence and differentiation and to promote tissue regeneration while retaining bioresorbable and biocompatible properties. In this study, ENSs were developed to deliver multiple biomolecules by loading them into the core-sheath structure and/or by conjugating them to the nanofiber surfaces. In this work, poly(L-lactide-poly(ethylene glycol-NH2 and poly(L-lactide were emulsion electrospun into nanofibers with a core-sheath structure. A model drug, tetracycline hydrochloride, was loaded within the nanofibers. Amino and carboxyl reactive groups were then activated on the fiber surfaces using saturated water vapor exposure and base hydrolysis, respectively. These reactive groups allowed the surface of the ENS to be functionalized with two other bioactive molecules, fluorescein isothiocyanate- and rhodamine-labeled bovine serum albumins, which were used as model proteins. The ENSs were shown to retain their antimicrobial capacity after two functionalization reactions, indicating that multifunctional nanofibers can potentially be developed into functional wound dressings or periodontal membranes or used in more complicated

  13. Development of green nanocomposites reinforced by cellulose nanofibers extracted from paper sludge

    Science.gov (United States)

    Takagi, Hitoshi; Nakagaito, Antonio N.; Kusaka, Kazuya; Muneta, Yuya

    2015-03-01

    Cellulose nanofibers have been showing much greater potential to enhance the mechanical and physical properties of polymer-based composite materials. The purpose of this study is to extract the cellulose nanofibers from waste bio-resources; such as waste newspaper and paper sludge. The cellulosic raw materials were treated chemically and physically in order to extract individualized cellulose nanofiber. The combination of acid hydrolysis and following mechanical treatment resulted in the extraction of cellulose nanofibers having diameter of about 40 nm. In order to examine the reinforcing effect of the extracted cellulose nanofibers, fully biodegradable green nanocomposites were fabricated by composing polyvinyl alcohol (PVA) resin with the extracted cellulose nanofibers, and then the tensile tests were conducted. The results showed that the enhancement in mechanical properties was successfully obtained in the cellulose nanofiber/PVA green nanocomposites.

  14. Biomedical Applications of Antibacterial Nanofiber Mats Made of Electrospinning with Wire Electrodes

    Directory of Open Access Journals (Sweden)

    Yi-Jun Pan

    2016-02-01

    Full Text Available Twisted stainless steel wires are used as wire electrodes for electrospinning the polyvinyl alcohol (PVA/zinc citrate nanofiber mats. The morphology and diameter of the nanofibers in PVA/zinc citrate nanofiber mats are evaluated. We measured the antibacterial efficacy against Staphylococcus aureus (S. aureus and Escherichia coli (E. coli of the nanofiber mats. We also examined the cell adhesion affinity of mammalian tissue culture cells on these nanofiber mats. Our results indicate that an increase in zinc citrate increases the viscosity and electrical conductivity of PVA solution. In addition, increasing zinc citrate results in a smaller diameter of nanofibers that reaches below 100 nm. According to the antibacterial test results, increasing zinc citrate enlarges the inhibition zone of S. aureus but only has a bacteriostatic effect against E. coli. Finally, cell adhesion test results indicate that all nanofiber mats have satisfactory cell attachment regardless of the content of zinc citrate.

  15. Facile Synthesis of Porous Silicon Nanofibers by Magnesium Reduction for Application in Lithium Ion Batteries.

    Science.gov (United States)

    Cho, Daehwan; Kim, Moonkyoung; Hwang, Jeonghyun; Park, Jay Hoon; Joo, Yong Lak; Jeong, Youngjin

    2015-12-01

    We report a facile fabrication of porous silicon nanofibers by a simple three-stage procedure. Polymer/silicon precursor composite nanofibers are first fabricated by electrospinning, a water-based spinning dope, which undergoes subsequent heat treatment and then reduction using magnesium to be converted into porous silicon nanofibers. The porous silicon nanofibers are coated with a graphene by using a plasma-enhanced chemical vapor deposition for use as an anode material of lithium ion batteries. The porous silicon nanofibers can be mass-produced by a simple and solvent-free method, which uses an environmental-friendly polymer solution. The graphene-coated silicon nanofibers show an improved cycling performance of a capacity retention than the pure silicon nanofibers due to the suppression of the volume change and the increase of electric conductivity by the graphene.

  16. Optics of Nanofibers

    DEFF Research Database (Denmark)

    Bordo, Vladimir

    During the last decade, fabrication and investigation of submicron-sized optical fibers have been received growing attention. Such nanofibers or nanowires can be grown from both inorganic and organic semiconductor materials being arranged in mutually parallel nanoaggregates. Also, selected...

  17. Development of Protective Clothing against Nanoparticle Based on Electrospun Nanofibers

    Directory of Open Access Journals (Sweden)

    M. Faccini

    2012-01-01

    Full Text Available In this paper, the development of efficient protective clothing against nanoparticulate aerosols is presented. Nanofibrous mats of polyamide 6 (PA6 were deposited onto a nonwoven viscose substrate by electrospinning technique. The influence of electrospinning parameters, including solution concentration, viscosity, and conductivity, was studied for the production of nonwovens with controlled fiber diameter showing a size distribution ranging from 66 to 195 nm. By varying several process parameters, textiles with different thickness of the nanofiber layer and thus air permeability were obtained. A hot-press lamination process using a thermoplastic resin as glue was applied to improve the adhesion of the nanofiber layer onto the textile support. After 1500 cycles of repeated compression and torsion, the nanofiber layer was still firmly attached to the support, while mechanical damage is visible in some areas. The penetration of NaCl particles with diameter ranging from 15 to 300 nm through the electrospun textiles was found to be strongly dependent on nanofiber layer thickness. A really thin nanofiber coating provides up to 80% retention of 20 nm size particles and over 50% retention of 200 nm size nanoparticles. Increasing the thickness of the nanofiber mat, the filtration efficiency was increased to over 99% along the whole nanoparticle range. The results obtained highlight the potential of nanofibers in the development of efficient personal protective equipments against nanoparticles.

  18. Evaluation of carbon fiber composites modified by in situ incorporation of carbon nanofibers

    Directory of Open Access Journals (Sweden)

    André Navarro de Miranda

    2011-12-01

    Full Text Available Nano-carbon materials, such as carbon nanotubes and carbon nanofibers, are being thought to be used as multifunctional reinforcement in composites. The growing of carbon nanofiber at the carbon fiber/epoxy interface results in composites having better electrical properties than conventional carbon fiber/epoxy composites. In this work, carbon nanofibers were grown in situ over the surface of a carbon fiber fabric by chemical vapor deposition. Specimens of carbon fiber/nanofiber/epoxy (CF/CNF/epoxy composites were molded and electrical conductivity was measured. Also, the CF/CNF/epoxy composites were tested under flexure and interlaminar shear. The results showed an overall reduction in mechanical properties as a function of added nanofiber, although electrical conductivity increased up to 74% with the addition of nanofibers. Thus CF/CNF/epoxy composites can be used as electrical dissipation discharge materials.

  19. Single flexible nanofiber to simultaneously realize electricity-magnetism bifunctionality

    International Nuclear Information System (INIS)

    Yang, Ming; Sheng, Shujuan; Ma, Qianli; Lv, Nan; Yu, Wensheng; Wang, Jinxian; Dong, Xiangting; Liu, Guixia

    2016-01-01

    In order to develop new-typed multifunctional composite nanofibers, PANI/Fe 3 O 4 /PVP flexible bifunctional composite nanofibers with simultaneous electrical conduction and magnetism have been successfully fabricated via a facile electrospinning technology. Polyvinyl pyrrolidone (PVP) is used as a matrix to construct composite nanofibers containing different amounts of polyaniline (PANI) and Fe 3 O 4 nanoparticles (NPs). The bifunctional composite nanofibers simultaneously possess excellent electrical conductivity and magnetic properties. The electrical conductivity reaches up to the order of 10 -3 S·cm -1 . The electrical conductivity and saturation magnetization of the composite nanofibers can be respectively tuned by adding various amounts of PANI and Fe 3 O 4 NPs. The obtained electricity-magnetism bifunctional composite nanofibers are expected to possess many potential applications in areas such as electromagnetic interference shielding, special coating, microwave absorption, molecular electronics and future nanomechanics. More importantly, the design concept and construct technique are of universal significance to fabricate other bifunctional one-dimensional nanostructures. (author)

  20. Single flexible nanofiber to simultaneously realize electricity-magnetism bifunctionality

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Ming; Sheng, Shujuan; Ma, Qianli; Lv, Nan; Yu, Wensheng; Wang, Jinxian; Dong, Xiangting; Liu, Guixia, E-mail: wenshengyu2009@sina.com, E-mail: dongxiangting888@163.com [Key Laboratory of Applied Chemistry and Nanotechnology at Universities of Jilin Province, Changchun University of Science and Technology, Changchun (China)

    2016-03-15

    In order to develop new-typed multifunctional composite nanofibers, PANI/Fe{sub 3}O{sub 4}/PVP flexible bifunctional composite nanofibers with simultaneous electrical conduction and magnetism have been successfully fabricated via a facile electrospinning technology. Polyvinyl pyrrolidone (PVP) is used as a matrix to construct composite nanofibers containing different amounts of polyaniline (PANI) and Fe{sub 3}O{sub 4} nanoparticles (NPs). The bifunctional composite nanofibers simultaneously possess excellent electrical conductivity and magnetic properties. The electrical conductivity reaches up to the order of 10{sup -3} S·cm{sup -1}. The electrical conductivity and saturation magnetization of the composite nanofibers can be respectively tuned by adding various amounts of PANI and Fe{sub 3}O{sub 4} NPs. The obtained electricity-magnetism bifunctional composite nanofibers are expected to possess many potential applications in areas such as electromagnetic interference shielding, special coating, microwave absorption, molecular electronics and future nanomechanics. More importantly, the design concept and construct technique are of universal significance to fabricate other bifunctional one-dimensional nanostructures. (author)

  1. Preparation of graphene oxide/poly (3,4-ethylenedioxytriophene): Poly (styrene sulfonate) (PEDOT:PSS) electrospun nanofibers

    International Nuclear Information System (INIS)

    Efelina, Vita; Widianto, Eri; Rusdiana, Dadi; Nugroho, A. A.; Kusumaatmaja, Ahmad; Triyana, Kuwat; Santoso, Iman

    2016-01-01

    Graphene oxide (GO)/Poly (3,4-Ethylenedioxytriophene):Poly (styrene Sulfonate) (PEDOT:PSS) nanofibers have been successfully fabricated by a simple electrospinning technique to develop conductive nanofibers with polyvinyl alcohol (PVA) act as a carrier solution. Graphene oxide has been synthesized by Hummer’s method and has been confirmed by Raman Spectroscopy, FTIR and UV-Vis Spectroscopy. GO/PEDOT:PSS composite nanofibers. The structural and morphological properties were characterized by Scanning Electron Microscopy (SEM). The result of SEM show that GO/PEDOT:PSS nanofibers has a relatively uniform morphology nanofiber with diameter between 180 nm - 340 nm with smooth nanofiber surface. The produced nanofibers from this study can be utilized for various applications such as flexible, conductive and transparent electrode.

  2. Preparation of graphene oxide/poly (3,4-ethylenedioxytriophene): Poly (styrene sulfonate) (PEDOT:PSS) electrospun nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Efelina, Vita; Widianto, Eri [Department of Physics, Universitas Gadjah Mada, Sekip Utara BLS.21 Yogyakarta, 55281 Indonesia (Indonesia); Rusdiana, Dadi [Department of Physical Education, Universitas Pendidikan Indonesia, Bandung (Indonesia); Nugroho, A. A. [Department of Physics, Institut Teknologi Bandung, Jl. Ganesha 10 Bandung (Indonesia); Kusumaatmaja, Ahmad; Triyana, Kuwat; Santoso, Iman, E-mail: iman.santoso@ugm.ac.id [Department of Physics, Universitas Gadjah Mada, Sekip Utara BLS.21 Yogyakarta, 55281 Indonesia (Indonesia); Nanomaterials Research Group, Universitas Gadjah Mada,, Sekip Utara, Yogyakarta (Indonesia)

    2016-04-19

    Graphene oxide (GO)/Poly (3,4-Ethylenedioxytriophene):Poly (styrene Sulfonate) (PEDOT:PSS) nanofibers have been successfully fabricated by a simple electrospinning technique to develop conductive nanofibers with polyvinyl alcohol (PVA) act as a carrier solution. Graphene oxide has been synthesized by Hummer’s method and has been confirmed by Raman Spectroscopy, FTIR and UV-Vis Spectroscopy. GO/PEDOT:PSS composite nanofibers. The structural and morphological properties were characterized by Scanning Electron Microscopy (SEM). The result of SEM show that GO/PEDOT:PSS nanofibers has a relatively uniform morphology nanofiber with diameter between 180 nm - 340 nm with smooth nanofiber surface. The produced nanofibers from this study can be utilized for various applications such as flexible, conductive and transparent electrode.

  3. Coaxial PCL/PVA electrospun nanofibers: osseointegration enhancer and controlled drug release device

    International Nuclear Information System (INIS)

    Song, Wei; Shi, Tong; Ren, Weiping; Yu, Xiaowei; Markel, David C

    2013-01-01

    The failure of prosthesis after total joint replacement is mainly due to dysfunctional osseointegration and implant infection. There is a critical need for orthopedic implants that promote rapid osseointegration and prevent bacterial colonization, particularly when placed in bone compromised by disease or physiology of the patients. The aim of this study was to fabricate a novel coaxial electrospun polycaprolactone (PCL)/polyvinyl alcohol (PVA) core-sheath nanofiber (NF) blended with both hydroxyapatite nanorods (HA) and type I collagen (Col) (PCL Col /PVA HA ). Doxycycline (Doxy) and dexamethasone (Dex) were successfully incorporated into the PCL Col /PVA HA NFs for controlled release. The morphology, surface hydrophilicity and mechanical properties of the PCL/PVA NF mats were analyzed by scanning electron microscopy, water contact angle and atomic force microscopy. The PCL Col /PVA HA NFs are biocompatible and enhance the adhesion and proliferation of murine pre-osteoblastic MC3T3 cells. The release of Doxy and Dex from coaxial PCL Col /PVA HA NFs showed more controlled release compared with the blended NFs. Using an ex vivo porcine bone implantation model we found that the PCL Col /PVA HA NFs bind firmly on the titanium rod surface and the NFs coating remained intact on the surface of titanium rods after pullout. No disruption or delamination was observed after the pullout test. These findings indicate that PCL Col /PVA HA NFs encapsulating drugs have great potential in enhancing implant osseointegration and preventing implant infection. (paper)

  4. Coaxial PCL/PVA electrospun nanofibers: osseointegration enhancer and controlled drug release device.

    Science.gov (United States)

    Song, Wei; Yu, Xiaowei; Markel, David C; Shi, Tong; Ren, Weiping

    2013-09-01

    The failure of prosthesis after total joint replacement is mainly due to dysfunctional osseointegration and implant infection. There is a critical need for orthopedic implants that promote rapid osseointegration and prevent bacterial colonization, particularly when placed in bone compromised by disease or physiology of the patients. The aim of this study was to fabricate a novel coaxial electrospun polycaprolactone (PCL)/polyvinyl alcohol (PVA) core-sheath nanofiber (NF) blended with both hydroxyapatite nanorods (HA) and type I collagen (Col) (PCL(Col)/PVA(HA)). Doxycycline (Doxy) and dexamethasone (Dex) were successfully incorporated into the PCL(Col)/PVA(HA) NFs for controlled release. The morphology, surface hydrophilicity and mechanical properties of the PCL/PVA NF mats were analyzed by scanning electron microscopy, water contact angle and atomic force microscopy. The PCL(Col)/PVA(HA) NFs are biocompatible and enhance the adhesion and proliferation of murine pre-osteoblastic MC3T3 cells. The release of Doxy and Dex from coaxial PCL(Col)/PVA(HA) NFs showed more controlled release compared with the blended NFs. Using an ex vivo porcine bone implantation model we found that the PCL(Col)/PVA(HA) NFs bind firmly on the titanium rod surface and the NFs coating remained intact on the surface of titanium rods after pullout. No disruption or delamination was observed after the pullout test. These findings indicate that PCL(Col)/PVA(HA) NFs encapsulating drugs have great potential in enhancing implant osseointegration and preventing implant infection.

  5. Photothermal heating as a methodology for post processing of polymeric nanofibers

    Science.gov (United States)

    Gorga, Russell; Clarke, Laura; Bochinski, Jason; Viswanath, Vidya; Maity, Somsubhra; Dong, Ju; Firestone, Gabriel

    2015-03-01

    Metal nanoparticles embedded within polymeric systems can be made to act as localized heat sources thereby aiding in-situ polymer processing. This is made possible by the surface plasmon resonance (SPR) mediated photothermal effect of metal (in this case gold) nanoparticles, wherein incident light absorbed by the nanoparticle generates a non-equilibrium electron distribution which subsequently transfers this energy into the surrounding medium, resulting in a temperature increase in the immediate region around the particle. Here we demonstrate this effect in polymer nanocomposite systems, specifically electrospun polyethylene oxide nanofibrous mats, which have been annealed at temperatures above the glass transition. A non-contact temperature measurement technique utilizing embedded fluorophores (perylene) has been used to monitor the average temperature within samples. The effect of annealing methods (conventional and photothermal) and annealing conditions (temperature and time) on the fiber morphology, overall crystallinity, and mechanical properties is discussed. This methodology is further utilized in core-sheath nanofibers to crosslink the core material, which is a pre-cured epoxy thermoset. NSF Grant CMMI-1069108.

  6. Nanofiber Filters Eliminate Contaminants

    Science.gov (United States)

    2009-01-01

    With support from Phase I and II SBIR funding from Johnson Space Center, Argonide Corporation of Sanford, Florida tested and developed its proprietary nanofiber water filter media. Capable of removing more than 99.99 percent of dangerous particles like bacteria, viruses, and parasites, the media was incorporated into the company's commercial NanoCeram water filter, an inductee into the Space Foundation's Space Technology Hall of Fame. In addition to its drinking water filters, Argonide now produces large-scale nanofiber filters used as part of the reverse osmosis process for industrial water purification.

  7. Process parameter and surface morphology of pineapple leaf electrospun nanofibers (PALF)

    Science.gov (United States)

    Surip, S. N.; Aziz, F. M. A.; Bonnia, N. N.; Sekak, K. A.; Zakaria, M. N.

    2017-09-01

    In recent times, nanofibers have attracted the attention of researchers due to their pronounced micro and nano structural characteristics that enable the development of advanced materials that have sophisticated applications. The production of nanofibers by the electrospinning process is influenced both by the electrostatic forces and the viscoelastic behavior of the polymer. Process parameters, like solution feed rate, applied voltage, nozzle-collector distance, and spinning environment, and material properties, like solution concentration, viscosity, surface tension, conductivity, and solvent vapor pressure, influence the structure and properties of electrospun nanofibers. Significant work has been done to characterize the properties of PALF nanofibers as a function of process and material parameters.

  8. Development and application of biomimetic electrospun nanofibers in total joint replacement

    Science.gov (United States)

    Song, Wei

    Failure of osseointegration (direct anchorage of an implant by bone formation at the bone-implant surface) and implant infection (such as that caused by Staphylococcus aureus, S. aureus) are the two main causes of implant failure and loosening. There is a critical need for orthopedic implants that promote rapid osseointegration and prevent bacterial colonization, particularly when placed in bone compromised by disease or physiology of the patients. A better understanding of the key factors that influence cell fate decisions at the bone-implant interface is required. Our study is to develop a class of "bone-like" nanofibers (NFs) that promote osseointegration while preventing bacterial colonization and subsequent infections. This research goal is supported by our preliminary data on the preparation of coaxial electrospun NFs composed of polycaprolactone (PCL) and polyvinyl alcohol (PVA) polymers arranged in a core-sheath shape. The PCL/PVA NFs are biocompatible and biodegradable with appropriate fiber diameter, pore size and mechanical strength, leading to enhanced cell adhesion, proliferation and differentiation of osteoblast precursor cells. The objective is to develop functionalized "bone-like" PCL/PVA NFs matrix embedded with antibiotics (doxycycline (Doxy), bactericidal and anti-osteoclastic) on prosthesis surface. Through a rat tibia implantation model, the Doxy incorporated coaxial NFs has demonstrated excellent in promoting osseointegration and bacteria inhibitory efficacy. NFs coatings significantly enhanced the bonding between implant and bone remodeling within 8 weeks. The SA-induced osteomyelitis was prevented by the sustained release of Doxy from NFs. The capability of embedding numerous bio-components including proteins, growth factors, drugs, etc. enables NFs an effective solution to overcome the current challenged issue in Total joint replacement. In summary, we proposed PCL/PVA electrospun nanofibers as promising biomaterials that can be applied on

  9. High thermoelectric performance of graphite nanofibers

    OpenAIRE

    Tran, Van-Truong; Saint-Martin, Jérôme; Dollfus, Philippe; Volz, Sebastian

    2017-01-01

    Graphite nanofibers (GNFs) have been demonstrated to be a promising material for hydrogen storage and heat management in electronic devices. Here, by means of first-principles and transport simulations, we show that GNFs can also be an excellent material for thermoelectric applications thanks to the interlayer weak van der Waals interaction that induces low thermal conductance and a step-like shape in the electronic transmission with mini-gaps, which are necessary ingredients to achieve high ...

  10. Temperature dependent transport and dielectric properties of cadmium titanate nanofiber mats

    Directory of Open Access Journals (Sweden)

    Z. Imran

    2013-03-01

    Full Text Available We investigate electrical and dielectric properties of cadmium titanate (CdTiO3 nanofiber mats prepared by electrospinning. The nanofibers were polycrystalline having diameter ∼50 nm-200 nm, average length ∼100 μm and crystallite size ∼25 nm. Alternating current impedance measurements were carried out from 318 K – 498 K. The frequency of ac signal was varied from 2 – 105 Hz. The complex impedance plots revealed two depressed semicircular arcs indicating the bulk and interface contribution to overall electrical behavior of nanofiber mats. The bulk resistance was found to increase with decrease in temperature exhibiting typical semiconductor like behavior. The modulus analysis shows the non-Debye type conductivity relaxation in nanofiber mats. The ac conductivity spectrum obeyed the Jonscher power law. Analysis of frequency dependent ac conductivity revealed presence of the correlated barrier hopping (CBH in nanofiber mats over the entire temperature range.

  11. Thermal and Electrical Characterization of the Carbon Nanofibers Based Cement Composites

    Directory of Open Access Journals (Sweden)

    Agnieszka ŚLOSARCZYK

    2017-08-01

    Full Text Available The paper describes the influence of chemical modification of vapor grown carbon nanofibers (VGCnFs on the thermal and electrical properties of the cement composites. The surface modification of nanofibers was performed by means of ozone and nitric acid treatments. It was shown that the oxidized carbon nanofibers surface plays an important role in shaping the mechanical and especially electrical properties of cement composite. For cement matrix modified with carbon nanofibers subjected to oxidized treatment, the slightly increase of cement paste resistivity was observed. It confirms the better adhesion of carbon nanofibers to cement paste. However, independently of carbon nanofibers modification, the occurrence of VGCnFs in cement paste increased the electrical conductivity of the composite in comparison to the cement paste without fibers. The obtained values of electrical resistivity were comparable with values of cement composites modified with 4 mm long carbon fibers. Moreover, it was shown that the chemical modification of carbon nanofibers surface does not influence on the thermal properties of cement composites. In case of cement paste with unmodified and modified carbon nanofibers, the Seebeck voltage was proportional to the temperature difference and was independent of the oxidation degree of carbon nanofibers.DOI: http://dx.doi.org/10.5755/j01.ms.23.2.14993

  12. (Au/PANA/PVAc) nanofibers as a novel composite matrix for albumin and streptavidin immobilization

    Energy Technology Data Exchange (ETDEWEB)

    Golshaei, Rana [University of Kashan, Institute of Nano Science and Nano Technology, Kashan, P.O. Box 87317-51167, Islamic Republic of Iran (Iran, Islamic Republic of); Guler, Zeliha [Istanbul Technical University, Nanoscience and Nanoengineering, Maslak, Istanbul 34469 (Turkey); Sarac, Sezai A., E-mail: sarac@itu.edu.tr [Istanbul Technical University, Nanoscience and Nanoengineering, Maslak, Istanbul 34469 (Turkey); Istanbul Technical University, Department of Chemistry and Polymer Science and Technology, Maslak, Istanbul 34469 (Turkey)

    2016-03-01

    A novel electrospun nanofiber mat (Au/PANA/PVAc) consists of (Gold/Poly Anthranilic acid) (Au/PANA) core/shell nanostructures as a support material for protein immobilization that was developed and characterized by electrochemical impedance spectroscopy. In the core/shells, PANA served carboxyl groups (− COOH) for covalent protein immobilization and Au enhanced the electrochemical properties by acting as tiny conduction centers to facilitate electron transfer. Covalent immobilization of albumin and streptavidin as model proteins onto the (Au/PANA/PVAc) nanofibers was carried out by using 1-ethyl-3-(dimethyl-aminopropyl) carbodiimide hydrochloride (EDC)/N-hydroxyl succinimide (NHS) activation. PVAc nanofibers were compared with Au/PANA/PVAc nanofibers before and after protein immobilization. The successful covalent binding of both albumin and streptavidin onto (Au/PANA/PVAc) nanofibers was confirmed by FTIR-ATR, Electron Microscopy/Energy-Dispersive X-ray Spectroscopy SEM/EDX and Electrochemical impedance spectroscopy (EIS). The nanofibers became resistive due to protein immobilization and the higher charge transfer resistance was observed after higher amount of protein was immobilized. - Highlights: • Au/PANA/PVAc nanofibers with (COOH) groups as a suitable supports for covalent immobilization of proteins. • Increasing of the resistivity of the nanofibers after immobilization of the proteins. • Activation of Au/PANA/PVAc nanofibers by using EDC/NHS.

  13. Fabrication and Characterization of Cellulose Acetate/Montmorillonite Composite Nanofibers by Electrospinning

    Directory of Open Access Journals (Sweden)

    Se Wook Kim

    2015-01-01

    Full Text Available Nanofibers composed of cellulose acetate (CA and montmorillonite (MMT were prepared by electrospinning method. MMT was first dispersed in water and mixed with an acetic acid solution of CA. The viscosity and conductivity of the CA/MMT solutions with different MMT contents were measured to compare with those of the CA solution. The CA/MMT solutions were electrospun to fabricate the CA/MMT composite nanofibers. The morphology, thermal stability, and crystalline and mechanical properties of the composite nanofibers were characterized by scanning electron microscopy (SEM, transmission electron microscopy (TEM, energy dispersive X-ray spectroscopy (EDX, thermogravimetric analysis (TGA, X-ray diffraction (XRD, and tensile test. The average diameters of the CA/MMT composite nanofibers obtained by electrospinning 18 wt% CA/MMT solutions in a mixed acetic acid/water (75/25, w/w solvent ranged from 150~350 nm. The nanofiber diameter decreased with increasing MMT content. TEM indicated the coexistence of CA nanofibers. The CA/MMT composite nanofibers showed improved tensile strength compared to the CA nanofiber due to the physical protective barriers of the silicate clay layers. MMT could be incorporated into the CA nanofibers resulting in about 400% improvement in tensile strength for the CA sample containing 5 wt% MMT.

  14. Processing and Structure of Carbon Nanofiber Paper

    Directory of Open Access Journals (Sweden)

    Zhongfu Zhao

    2009-01-01

    Full Text Available A unique concept of making nanocomposites from carbon nanofiber paper was explored in this study. The essential element of this method was to design and manufacture carbon nanofiber paper with well-controlled and optimized network structure of carbon nanofibers. In this study, carbon nanofiber paper was prepared under various processing conditions, including different types of carbon nanofibers, solvents, dispersants, and acid treatment. The morphologies of carbon nanofibers within the nanofiber paper were characterized with scanning electron microscopy (SEM. In addition, the bulk densities of carbon nanofiber papers were measured. It was found that the densities and network structures of carbon nanofiber paper correlated to the dispersion quality of carbon nanofibers within the paper, which was significantly affected by papermaking process conditions.

  15. A novel electrospun hydroxypropyl methylcellulose/polyethylene oxide blend nanofibers: Morphology and physicochemical properties.

    Science.gov (United States)

    Aydogdu, Ayca; Sumnu, Gulum; Sahin, Serpil

    2018-02-01

    The objective of this study was to fabricate and characterize Hydroxypropyl methylcellulose (HPMC) -based homogenous nanofibers by using electrospinning method. As the concentrations of the solutions increased, viscosity and electrical conductivity of the solutions increased. The morphology of the fibers changed from the beaded structure to the uniform fiber structure by increasing the concentrations of the solutions. Water vapor permeability (WVP) of electrospun HPMC nanofibers decreased with increasing polymer concentration. The shift in wavelengths, the change in intensity of FTIR peaks and melting point depression were the evidence of miscibility of HPMC/PEO blends. Nanofibers showing both melting temperature (T m ) and glass transition temperature (T g ) had semicrystalline structure. By combining PEO with HPMC, the thermal stability of nanofibers was increased. Hence, this study suggests homogenous biopolymer-based nanofibers with low WVP and high thermal stability which can have potential applications in food packaging field. Copyright © 2017 Elsevier Ltd. All rights reserved.

  16. Binder-free Si nanoparticles@carbon nanofiber fabric as energy storage material

    International Nuclear Information System (INIS)

    Liu, Yuping; Huang, Kai; Fan, Yu; Zhang, Qing; Sun, Fu; Gao, Tian; Wang, Zhongzheng; Zhong, Jianxin

    2013-01-01

    A nonwoven nanofiber fabric with paper-like qualities composed of Si nanoparticles and carbon as binder-free anode electrode is reported. The nanofiber fabrics are prepared by convenient electrospinning technique, in which, the Si nanoparticles are uniformly confined in the carbon nanofibers. The high strength and flexibility of the nanofiber fabrics are beneficial for alleviating the structural deformation and facilitating ion transports throughout the whole composited electrodes. Due to the absence of binder, the less weight, higher energy density, and excellent electrical conductivity anodes can be attained. These traits make the composited nanofiber fabrics excellent used as a binder-free, mechanically flexible, high energy storage anode material in the next generation of rechargeable lithium ions batteries

  17. Structures and Properties of Polyacrylonitrile/Graphene Composite Nanofiber Yarns Prepared by Multi-Needle Electrospinning Device with an Auxiliary Electrode.

    Science.gov (United States)

    Yan, Tao; Pan, Zhi-Juan

    2018-06-01

    In this paper, polyacrylonitrile/graphene composite nanofiber filaments were manufactured continuously by a homemade eight-needle electrospinning device with an auxiliary electrode. The polyacrylonitrile/graphene composite nanofiber yarns were obtained continuously by plying and twisting the composite nanofiber filaments. The structures and properties of the composite nanofiber filaments with different GP mass fractions and yarns were investigated. The results demonstrated that the maximum alignment degree of the composite nanofibers along the filament axis could reach 74.3% with 1%, and the alignment degree decreased with increasing graphene mass fraction. The diameters of the composite nanofibers were considerably smaller than those of the pure polyacrylonitrile nanofiber, and the minimum diameter was 156 nm for 1%. The conductivity of the composite nanofiber filaments was significantly enhanced by seven orders of magnitude compared with that of the pure polyacrylonitrile nanofiber filament, and the maximum value was 3.73×10-7 S/cm for 1.5%. Due to graphene agglomeration, the conductivity decreased when the mass fraction was more than 1.5%. The different number of filaments and twists were examined in detail to improve the poor mechanical properties of the nanofiber filaments. With an increase in twists, the breaking stress and strain increased initially and later decreased, and the maximum breaking stress and strain were 16.54 MPa and 26.42%, respectively. This study demonstrates the possibility of continuously and stably manufacturing polyacrylonitrile/graphene composite nanofiber yarns.

  18. Mechanism of nanofiber crimp

    Directory of Open Access Journals (Sweden)

    Chen Rou-Xi

    2013-01-01

    Full Text Available Fabrication of crimped fibers has been caught much attention recently due to remarkable improvement surface-to-volume ratio. The precise mechanism of the fiber crimp is, however, rare and preliminary. This paper finds that pulsation of fibers is the key factor for fiber crimp, and its configuration (wave formation corresponds to its nature frequency after solidification. Crimping performance can be improved by temperature control of the uncrimped fibers. In the paper, polylactide/ dimethylfomamide solution is fabricated into crimped nanofibers by the bubble electrospinning, an approximate period- amplitude relationship of the wave formation is obtained.

  19. Templates for integrated nanofiber growth

    DEFF Research Database (Denmark)

    Oliveira Hansen, Roana Melina de

    the growth direction and the nanofiber length and position can be controlled by placement of nano-structured lines on the substrate. These lines can be used to guide the surface diffusion and thereby steer the self-assembly process of the organic molecules leading to morphologically well-defined molecular...... the morphology of the resulting structures leading to notably different electrical properties. The transistor design influences its electrical characteristics, and the top-gate configuration shows to have the stronger gate effect. In addition, platforms for light-emitting devices were fabricated......Para-hexaphenylene (p6P) molecules have the ability to self-assemble into organic nanofibers. These nanofibers hold unique optoelectronic properties, which make them interesting candidates as elements in electronic and optoelectronic devices. Typically these nanofibers are grown on specific single...

  20. A facile method for electrospinning of Ag nanoparticles/poly (vinyl alcohol)/carboxymethyl-chitosan nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Yinghui; Zhou, Ying [Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University, Beijing 100871 (China); Center for Biomedical Materials and Tissue Engineering, Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871 (China); Wu, Xiaomian [Center for Biomedical Materials and Tissue Engineering, Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871 (China); Department of Orthodontics College of Stomatology, Chongqing Medical University, Chongqing 401147 (China); Wang, Lu [Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University, Beijing 100871 (China); Xu, Ling, E-mail: lingxu@pku.edu.cn [Beijing Key Laboratory for Solid Waste Utilization and Management, College of Engineering, Peking University, Beijing 100871 (China); Center for Biomedical Materials and Tissue Engineering, Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871 (China); PKU-HKUST ShenZhen-HongKong Institution, Shenzhen 518057 (China); Wei, Shicheng, E-mail: sc-wei@pku.edu.cn [Center for Biomedical Materials and Tissue Engineering, Academy for Advanced Interdisciplinary Studies, Peking University, Beijing 100871 (China); Department of Oral and Maxillofacial Surgery, School and Hospital of Stomatology, Peking University, Beijing 100081 (China)

    2012-09-01

    Highlights: Black-Right-Pointing-Pointer AgNPs/PVA/CM-chitosan nanofibers were prepared via electrospinning method. Black-Right-Pointing-Pointer AgNPs were in situ synthesized in electrospinning solution via a facile method. Black-Right-Pointing-Pointer AgNPs distributed homogeneously on the surface of nanofibers. Black-Right-Pointing-Pointer The prepared nanofibers possessed certain antibacterial ability against Escherichia coli. Black-Right-Pointing-Pointer The AgNPs containing nanofibers had potential as antibacterial biomaterial. - Abstract: A facile method to prepare silver nanoparticles (AgNPs) containing nanofibers via electrospinning has been demonstrated. AgNPs were in situ synthesized in poly (vinyl alcohol) (PVA)/carboxymethyl-chitosan (CM-chitosan) blend aqueous solution before electrospinning. UV-vis spectra, viscosity and conductivity of the electrospinning solution were measured to investigate their effects on the electrospinning procedure. The morphology of AgNPs/PVA/CM-chitosan nanofibers was observed by Field Emission Scanning Electron Microscopy. The formation and morphology of AgNPs were investigated by Transmission Electron Microscopy and X-ray Photoelectron Spectroscopy. The resulted nanofibers have smooth surface and uniform diameters ranging from 295 to 343 nm. The diameters of AgNPs mainly distributed in the range of 4-14 nm, and the electrostatic interaction between AgNPs and fibers was observed. Finally, in vitro Ag release from the nanofibers was measured and the antibacterial behavior of the nanofibers against Escherichia coli was studied by bacterial growth inhibition halos and bactericidal kinetic testing. The AgNPs/PVA/CM-chitosan nanofibers possessed certain antibacterial ability, which makes them capable for antibacterial biomaterials.

  1. A facile method for electrospinning of Ag nanoparticles/poly (vinyl alcohol)/carboxymethyl-chitosan nanofibers

    International Nuclear Information System (INIS)

    Zhao, Yinghui; Zhou, Ying; Wu, Xiaomian; Wang, Lu; Xu, Ling; Wei, Shicheng

    2012-01-01

    Highlights: ► AgNPs/PVA/CM-chitosan nanofibers were prepared via electrospinning method. ► AgNPs were in situ synthesized in electrospinning solution via a facile method. ► AgNPs distributed homogeneously on the surface of nanofibers. ► The prepared nanofibers possessed certain antibacterial ability against Escherichia coli. ► The AgNPs containing nanofibers had potential as antibacterial biomaterial. - Abstract: A facile method to prepare silver nanoparticles (AgNPs) containing nanofibers via electrospinning has been demonstrated. AgNPs were in situ synthesized in poly (vinyl alcohol) (PVA)/carboxymethyl-chitosan (CM-chitosan) blend aqueous solution before electrospinning. UV–vis spectra, viscosity and conductivity of the electrospinning solution were measured to investigate their effects on the electrospinning procedure. The morphology of AgNPs/PVA/CM-chitosan nanofibers was observed by Field Emission Scanning Electron Microscopy. The formation and morphology of AgNPs were investigated by Transmission Electron Microscopy and X-ray Photoelectron Spectroscopy. The resulted nanofibers have smooth surface and uniform diameters ranging from 295 to 343 nm. The diameters of AgNPs mainly distributed in the range of 4–14 nm, and the electrostatic interaction between AgNPs and fibers was observed. Finally, in vitro Ag release from the nanofibers was measured and the antibacterial behavior of the nanofibers against Escherichia coli was studied by bacterial growth inhibition halos and bactericidal kinetic testing. The AgNPs/PVA/CM-chitosan nanofibers possessed certain antibacterial ability, which makes them capable for antibacterial biomaterials.

  2. Highly sensitive and ultrafast response surface acoustic wave humidity sensor based on electrospun polyaniline/poly(vinyl butyral) nanofibers

    International Nuclear Information System (INIS)

    Lin Qianqian; Li Yang; Yang Mujie

    2012-01-01

    Highlights: ► Polyanline/poly(vinyl butyral) nanofibers are prepared by electrospinning. ► Nanofiber-based SAW humidity sensor show high sensitivity and ultrafast response. ► The SAW sensor can detect very low humidity. - Abstract: Polyaniline (PANi) composite nanofibers were deposited on surface acoustic wave (SAW) resonator with a central frequency of 433 MHz to construct humidity sensors. Electrospun nanofibers of poly(methyl methacrylate), poly(vinyl pyrrolidone), poly(ethylene oxide), poly(vinylidene fluoride), poly(vinyl butyral) (PVB) were characterized by scanning electron microscopy, and humidity response of corresponding SAW humidity sensors were investigated. The results indicated that PVB was suitable as a matrix to form nanofibers with PANi by electrospinning (ES). Electrospun PANi/PVB nanofibers exhibited a core–sheath structure as revealed by transmittance electron microscopy. Effects of ES collection time on humidity response of SAW sensor based on PANi/PVB nanofibers were examined at room temperature. The composite nanofiber sensor exhibited very high sensitivity of ∼75 kHz/%RH from 20 to 90%RH, ultrafast response (1 s and 2 s for humidification and desiccation, respectively) and good sensing linearity. Furthermore, the sensor could detect humidity as low as 0.5%RH, suggesting its potentials for low humidity detection. Attempts were done to explain the attractive humidity sensing performance of the sensor by considering conductivity, hydrophilicity, viscoelasticity and morphology of the polymer composite nanofibers.

  3. General strategy for fabricating thoroughly mesoporous nanofibers

    KAUST Repository

    Hou, Huilin; Wang, Lin; Gao, Fengmei; Wei, Guodong; Tang, Bin; Yang, Weiyou; Wu, Tao

    2014-01-01

    mesoporous nanofibers with high purity and uniformity. Here, we report a general, simple and cost-effective strategy, namely, foaming-assisted electrospinning, for producing mesoporous nanofibers with high purity and enhanced specific surface areas. As a

  4. Printed second harmonic active organic nanofiber arrays

    DEFF Research Database (Denmark)

    Balzer, Frank; Brewer, Jonathan R.; Kjelstrup-Hansen, Jakob

    2007-01-01

    Organic nanofibers from semiconducting conjugated molecules are well suited to meet refined demands for advanced applications in future optoelectronics and nanophotonics. In contrast to their inorganic counterparts, the properties of organic nanowires can be tailored at the molecular level...... investigated nanofibers as grown via organic epitaxy. In the present work we show how chemically changing the functionalizing end groups leads to a huge increase of second order susceptibility, making the nanofibers technologically very interesting as efficient frequency doublers. For that the nanofibers have...

  5. Piezoelectric and optoelectronic properties of electrospinning hybrid PVDF and ZnO nanofibers

    Science.gov (United States)

    Ma, Jian; Zhang, Qian; Lin, Kabin; Zhou, Lei; Ni, Zhonghua

    2018-03-01

    Polyvinylidene fluoride (PVDF) is a unique ferroelectric polymer with significant promise for energy harvesting, data storage, and sensing applications. ZnO is a wide direct band gap semiconductor (3.37 eV), commonly used as ultraviolet photodetectors, nanoelectronics, photonicsand piezoelectric generators. In this study, we produced high output piezoelectric energy harvesting materials using hybrid PVDF/ZnO nanofibers deposited via electrospinning. The strong electric fields and stretching forces during the electrospinning process helps to align dipoles in the nanofiber crystal such that the nonpolar α-phase (random orientation of dipoles) is transformed into polar β-phase in produced nanofibers. The effect of the additional ZnO nanowires on the nanofiber β-phase composition and output voltage are investigated. The maximum output voltage generated by a single hybrid PVDF and ZnO nanofiber (33 wt% ZnO nanowires) is over 300% of the voltage produced by a single nanofiber made of pure PVDF. The ZnO NWs served not only as a piezoelectric material, but also as a semiconducting material. The electrical conductivity of the hybrid PVDF/ZnO nanofibers increased by more than a factor of 4 when exposed under ultraviolet (UV) light.

  6. Cashew nut shell liquid, a valuable raw material for generating semiconductive polyaniline nanofibers

    Directory of Open Access Journals (Sweden)

    Raiane Valenti Gonçalves

    2018-03-01

    Full Text Available Abstract Cashew nut shell liquid (CNSL is an abundant and renewable by-product of the cashew nut industry. It appears to be a valuable raw material for generating semiconductive polyaniline (PAni nanomaterial with enhanced thermal stability and well-defined nanofiber morphology following a polymerization dispersion process. This study confirms that CNSL acts as a soft template during PAni synthesis, leading to an improvement in the nanofiber aspect. CNSL also improves the thermal stability of the PAni nanomaterial. Moreover, CNSL is an effective surfactant that promotes and stabilizes the dispersion of PAni nanofibers within water, allowing the more ecofriendly preparation of PAni nanomaterial by substituting the commonly used organic solvent with aqueous media. Finally, although CNSL promotes the formation of the conductive emeraldine salt form of PAni, increasing CNSL concentrations appear to plasticize the PAni polymer, leading to reduced electrical conductivity. However, this reduction is not detrimental, and PAni nanofibers remain semiconductive even under high CNSL concentrations.

  7. Preparation and electrochemical properties of polyaniline nanofibers using ultrasonication

    Energy Technology Data Exchange (ETDEWEB)

    Manuel, James [Department of Chemical and Biological Engineering and Research Institute for Green Energy Convergence Technology, Gyeongsang National University, 900, Gajwa-dong, Jinju 660-701 (Korea, Republic of); Kim, Miso [Department of Materials Engineering and Convergence Technology, Gyeongsang National University, 900, Gajwa-dong, Jinju 660-701 (Korea, Republic of); Fapyane, Deby; Chang, In Seop [School of Environmental Science and Engineering, Gwangju Institute of Science and Technology, 261 Cheomdan Gwagi-ro, Buk-gu, Gwangju 500-712 (Korea, Republic of); Ahn, Hyo-Jun, E-mail: ahj@gnu.ac.kr [Department of Materials Engineering and Convergence Technology, Gyeongsang National University, 900, Gajwa-dong, Jinju 660-701 (Korea, Republic of); Ahn, Jou-Hyeon, E-mail: jhahn@gnu.ac.kr [Department of Chemical and Biological Engineering and Research Institute for Green Energy Convergence Technology, Gyeongsang National University, 900, Gajwa-dong, Jinju 660-701 (Korea, Republic of); Department of Materials Engineering and Convergence Technology, Gyeongsang National University, 900, Gajwa-dong, Jinju 660-701 (Korea, Republic of)

    2014-10-15

    Highlights: • Nanofibrous structured polyaniline (PANI) was prepared by simple ultrasonication. • PANI nanofibers prepared at 5 °C are uniform with an average diameter of 50 nm. • The conductivity is increased by 2 × 10{sup 8} times after doping with LiClO{sub 4}. • The cell with PANI-LiClO{sub 4} shows good cycle performance at high current densities. - Abstract: Polyaniline nanofibers have been successfully prepared by applying ultrasonic irradiation during oxidative polymerization of aniline in dilute hydrochloric acid and evaluated for suitability in lithium cells after doping with lithium perchlorate salt. Polyaniline nanofibers are confirmed by Fourier transform infrared spectroscopy, Fourier transform Raman spectroscopy, and transmission electron microscopy, and the efficiency of doping is confirmed by DC conductivity measurements at different temperatures. Electrochemical properties of nanofibers are evaluated, of which a remarkable increase in cycle stability is achieved when compared to polyaniline prepared by simple oxidative polymerization of aniline. The cell with nanofibrous polyaniline doped with LiClO{sub 4} delivers an initial discharge capacity value of 86 mA h g{sup −1} at 1 C-rate which is about 60% of theoretical capacity, and the capacity is slightly lowered during cycle and reaches 50% of theoretical capacity after 40 cycles. The cell delivers a stable and higher discharge capacity even at 2 C-rate compared to that of the cell prepared with bulk polyaniline doped with LiClO{sub 4}.

  8. Electrospinning of Nanofibers for Energy Applications

    Science.gov (United States)

    Sun, Guiru; Sun, Liqun; Xie, Haiming; Liu, Jia

    2016-01-01

    With global concerns about the shortage of fossil fuels and environmental issues, the development of efficient and clean energy storage devices has been drastically accelerated. Nanofibers are used widely for energy storage devices due to their high surface areas and porosities. Electrospinning is a versatile and efficient fabrication method for nanofibers. In this review, we mainly focus on the application of electrospun nanofibers on energy storage, such as lithium batteries, fuel cells, dye-sensitized solar cells and supercapacitors. The structure and properties of nanofibers are also summarized systematically. The special morphology of nanofibers prepared by electrospinning is significant to the functional materials for energy storage. PMID:28335256

  9. Electrospinning of Nanofibers for Energy Applications

    Directory of Open Access Journals (Sweden)

    Guiru Sun

    2016-07-01

    Full Text Available With global concerns about the shortage of fossil fuels and environmental issues, the development of efficient and clean energy storage devices has been drastically accelerated. Nanofibers are used widely for energy storage devices due to their high surface areas and porosities. Electrospinning is a versatile and efficient fabrication method for nanofibers. In this review, we mainly focus on the application of electrospun nanofibers on energy storage, such as lithium batteries, fuel cells, dye-sensitized solar cells and supercapacitors. The structure and properties of nanofibers are also summarized systematically. The special morphology of nanofibers prepared by electrospinning is significant to the functional materials for energy storage.

  10. Aligned Layers of Silver Nano-Fibers

    Directory of Open Access Journals (Sweden)

    Andrii B. Golovin

    2012-02-01

    Full Text Available We describe a new dichroic polarizers made by ordering silver nano-fibers to aligned layers. The aligned layers consist of nano-fibers and self-assembled molecular aggregates of lyotropic liquid crystals. Unidirectional alignment of the layers is achieved by means of mechanical shearing. Aligned layers of silver nano-fibers are partially transparent to a linearly polarized electromagnetic radiation. The unidirectional alignment and density of the silver nano-fibers determine degree of polarization of transmitted light. The aligned layers of silver nano-fibers might be used in optics, microwave applications, and organic electronics.

  11. New High-Energy Nanofiber Anode Materials

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Xiangwu [North Carolina State Univ., Raleigh, NC (United States); Fedkiw, Peter [North Carolina State Univ., Raleigh, NC (United States); Khan, Saad [North Carolina State Univ., Raleigh, NC (United States); Huang, Alex [North Carolina State Univ., Raleigh, NC (United States); Fan, Jiang [North Carolina State Univ., Raleigh, NC (United States)

    2013-11-15

    The overall goal of the proposed work was to use electrospinning technology to integrate dissimilar materials (lithium alloy and carbon) into novel composite nanofiber anodes, which simultaneously had high energy density, reduced cost, and improved abuse tolerance. The nanofiber structure allowed the anodes to withstand repeated cycles of expansion and contraction. These composite nanofibers were electrospun into nonwoven fabrics with thickness of 50 μm or more, and then directly used as anodes in a lithium-ion battery. This eliminated the presence of non-active materials (e.g., conducting carbon black and polymer binder) and resulted in high energy and power densities. The nonwoven anode structure also provided a large electrode-electrolyte interface and, hence, high rate capacity and good lowtemperature performance capability. Following are detailed objectives for three proposed project periods. During the first six months: Obtain anodes capable of initial specific capacities of 650 mAh/g and achieve ~50 full charge/discharge cycles in small laboratory scale cells (50 to 100 mAh) at the 1C rate with less than 20 percent capacity fade; In the middle of project period: Assemble, cycle, and evaluate 18650 cells using proposed anode materials, and demonstrate practical and useful cycle life (750 cycles of ~70% state of charge swing with less than 20% capacity fade) in 18650 cells with at least twice improvement in the specific capacity than that of conventional graphite electrodes; At the end of project period: Deliver 18650 cells containing proposed anode materials, and achieve specific capacities greater than 1200 mAh/g and cycle life longer than 5000 cycles of ~70% state of charge swing with less than 20% capacity fade.

  12. Oriented nanofibers embedded in a polymer matrix

    Science.gov (United States)

    Barrera, Enrique V. (Inventor); Lozano, Karen (Inventor); Rodriguez-Macias, Fernando J. (Inventor); Chibante, Luis Paulo Felipe (Inventor); Stewart, David Harris (Inventor)

    2011-01-01

    A method of forming a composite of embedded nanofibers in a polymer matrix is disclosed. The method includes incorporating nanofibers in a plastic matrix forming agglomerates, and uniformly distributing the nanofibers by exposing the agglomerates to hydrodynamic stresses. The hydrodynamic said stresses force the agglomerates to break apart. In combination or additionally elongational flow is used to achieve small diameters and alignment. A nanofiber reinforced polymer composite system is disclosed. The system includes a plurality of nanofibers that are embedded in polymer matrices in micron size fibers. A method for producing nanotube continuous fibers is disclosed. Nanofibers are fibrils with diameters of 100 nm, multiwall nanotubes, single wall nanotubes and their various functionalized and derivatized forms. The method includes mixing a nanofiber in a polymer; and inducing an orientation of the nanofibers that enables the nanofibers to be used to enhance mechanical, thermal and electrical properties. Orientation is induced by high shear mixing and elongational flow, singly or in combination. The polymer may be removed from said nanofibers, leaving micron size fibers of aligned nanofibers.

  13. Nanofibers made of globular proteins.

    Science.gov (United States)

    Dror, Yael; Ziv, Tamar; Makarov, Vadim; Wolf, Hila; Admon, Arie; Zussman, Eyal

    2008-10-01

    Strong nanofibers composed entirely of a model globular protein, namely, bovine serum albumin (BSA), were produced by electrospinning directly from a BSA solution without the use of chemical cross-linkers. Control of the spinnability and the mechanical properties of the produced nanofibers was achieved by manipulating the protein conformation, protein aggregation, and intra/intermolecular disulfide bonds exchange. In this manner, a low-viscosity globular protein solution could be modified into a polymer-like spinnable solution and easily spun into fibers whose mechanical properties were as good as those of natural fibers made of fibrous protein. We demonstrate here that newly formed disulfide bonds (intra/intermolecular) have a dominant role in both the formation of the nanofibers and in providing them with superior mechanical properties. Our approach to engineer proteins into biocompatible fibrous structures may be used in a wide range of biomedical applications such as suturing, wound dressing, and wound closure.

  14. Preparation and characterization of oriented poly(vinyl alcohol)/carbon nanotube composite nanofibers

    Science.gov (United States)

    Shimizu, Akikazu; Kato, Hayato; Sato, Taiga; Kushida, Masahito

    2017-07-01

    Oriented nanofiber mats blended with carbon nanotubes (CNTs) are expected to be applied as cell seeding scaffolds. Biomaterials that are often used for cell seeding scaffolds generally have low mechanical strength and low electrical conductivity; thus, it has been difficult to apply them to tissues such as heart and nerve. In this study, we prepared oriented poly(vinyl alcohol) (PVA) nanofiber mats blended with various CNT concentrations (up to 10 wt %) by electrospinning using the parallel plate electrodes as collectors with applied voltage. The morphology, mechanical properties, and electrical properties of the prepared oriented nanofiber mats were measured by using various techniques such as scanning electron microscopy (SEM). The tensile strength of the oriented nanofiber mats in the applied voltage direction increased from 2.5 to 9.7 MPa with CNT concentration. Furthermore, the electrical conductivity of the oriented nanofiber mats in the applied voltage direction increased from 0.67 × 10-7 to 4.3 × 10-7 S·m-1. Also, the mechanical strength and electrical conductivity of the oriented nanofiber mats in the applied voltage direction were 3-4 and 2-3 times higher than those in the perpendicular direction, respectively.

  15. Nanocontainers in and onto Nanofibers.

    Science.gov (United States)

    Jiang, Shuai; Lv, Li-Ping; Landfester, Katharina; Crespy, Daniel

    2016-05-17

    Hierarchical structure is a key feature explaining the superior properties of many materials in nature. Fibers usually serve in textiles, for structural reinforcement, or as support for other materials, whereas spherical micro- and nanoobjects can be either highly functional or also used as fillers to reinforce structure materials. Combining nanocontainers with fibers in one single object has been used to increase the functionality of fibers, for example, antibacterial and thermoregulation, when the advantageous properties given by the encapsulated materials inside the containers are transferred to the fibers. Herein we focus our discussion on how the hierarchical structure composed of nanocontainers in nanofibers yields materials displaying advantages of both types of materials and sometimes synergetical effects. Such materials can be produced by first carefully designing nanocontainers with defined morphology and chemistry and subsequently electrospinning them to fabricate nanofibers. This method, called colloid-electrospinning, allows for marrying the properties of nanocontainers and nanofibers. The obtained fibers could be successfully applied in different fields such as catalysis, optics, energy conversion and production, and biomedicine. The miniemulsion process is a convenient approach for the encapsulation of hydrophobic or hydrophilic payloads in nanocontainers. These nanocontainers can be embedded in fibers by the colloid-electrospinning technique. The combination of nanocontainers with nanofibers by colloid-electrospinning has several advantages. (1) The fiber matrix serves as support for the embedded nanocontainers. For example, through combining catalysts nanoparticles with fiber networks, the catalysts can be easily separated from the reaction media and handled visually. This combination is beneficial for the reuse of the catalyst and the purification of products. (2) Electrospun nanofibers containing nanocontainers offer the active agents inside the

  16. Ultrasound-assisted preparation of electrospun carbon nanofiber/graphene composite electrode for supercapacitors

    Science.gov (United States)

    Dong, Qiang; Wang, Gang; Hu, Han; Yang, Juan; Qian, Bingqing; Ling, Zheng; Qiu, Jieshan

    2013-12-01

    Electrospun carbon nanofiber/graphene (CNF/G) composites are prepared by in situ electrospinning polymeric nanofibers with simultaneous spraying graphene oxide, followed by heat treatment. The freestanding carbon nanofiber web acts as a framework for sustaining graphene, which helps to prevent the agglomeration of graphene and to provide a high conductivity for the efficient charge transfer to the pores. The as-obtained CNF/G composite exhibits a specific capacitance of 183 F g-1, which is approximately 1.6 times higher than that of the pristine CNF. The results have demonstrated that the high performance of the CNF/G composite is due to the novel structure and the synergic effect of graphene and the carbon nanofibers.

  17. Combined Cell Culture-Biosensing Platform Using Vertically Aligned Patterned Peptide Nanofibers for Cellular Studies

    DEFF Research Database (Denmark)

    Taskin, Mehmet B.; Sasso, Luigi; Dimaki, Maria

    2013-01-01

    it possible to avoid a loss of sensitivity because of the diffusion of the sample. The obtained results showed that the peptide nanofibers were suitable as a cell culturing substrate for PC12 cells. The peptide nanofibers could be employed as an alternative biological material to increase the adherence......This Article presents the development of a combined cell culture–biosensing platform using vertically aligned self-assembled peptide nanofibers. Peptide nanofibers were patterned on a microchip containing gold microelectrodes to provide the cells with a 3D environment enabling them to grow...... and proliferate. Gold microelectrodes were functionalized with conductive polymers for the electrochemical detection of dopamine released from PC12 cells. The combined cell culture–biosensing platform assured a close proximity of the release site, the cells and the active surface of the sensor, thereby rendering...

  18. Metal nanogrids, nanowires, and nanofibers for transparent electrodes

    KAUST Repository

    Hu, Liangbing; Wu, Hui; Cui, Yi

    2011-01-01

    Metals possess the highest conductivity among all room-temperature materials; however, ultrathin metal films demonstrate decent optical transparency but poor sheet conductance due to electron scattering from the surface and grain boundaries. This article discusses engineered metal nanostructures in the form of nanogrids, nanowires, or continuous nanofibers as efficient transparent and conductive electrodes. Metal nanogrids are discussed, as they represent an excellent platform for understanding the fundamental science. Progress toward low-cost, nano-ink-based printed silver nanowire electrodes, including silver nanowire synthesis, film fabrication, wire-wire junction resistance, optoelectronic properties, and stability, are also discussed. Another important factor for low-cost application is to use earth-abundant materials. Copper-based nanowires and nanofibers are discussed in this context. Examples of device integrations of these materials are also given. Such metal nanostructure-based transparent electrodes are particularly attractive for solar cell applications. © 2011 Materials Research Society.

  19. Metal nanogrids, nanowires, and nanofibers for transparent electrodes

    KAUST Repository

    Hu, Liangbing

    2011-10-01

    Metals possess the highest conductivity among all room-temperature materials; however, ultrathin metal films demonstrate decent optical transparency but poor sheet conductance due to electron scattering from the surface and grain boundaries. This article discusses engineered metal nanostructures in the form of nanogrids, nanowires, or continuous nanofibers as efficient transparent and conductive electrodes. Metal nanogrids are discussed, as they represent an excellent platform for understanding the fundamental science. Progress toward low-cost, nano-ink-based printed silver nanowire electrodes, including silver nanowire synthesis, film fabrication, wire-wire junction resistance, optoelectronic properties, and stability, are also discussed. Another important factor for low-cost application is to use earth-abundant materials. Copper-based nanowires and nanofibers are discussed in this context. Examples of device integrations of these materials are also given. Such metal nanostructure-based transparent electrodes are particularly attractive for solar cell applications. © 2011 Materials Research Society.

  20. Mechanical properties of organic nanofibers

    DEFF Research Database (Denmark)

    Kjelstrup-Hansen, Jakob; Hansen, Ole; Rubahn, H.R.

    2006-01-01

    Intrinsic elastic and inelastic mechanical Properties of individual, self-assembled, quasi-single-crystalline para-hexaphenylene nanofibers supported on substrates with different hydrophobicities are investigated as well as the interplay between the fibers and the underlying substrates. We find...

  1. The Electrospun Ceramic Hollow Nanofibers

    Directory of Open Access Journals (Sweden)

    Shahin Homaeigohar

    2017-11-01

    Full Text Available Hollow nanofibers are largely gaining interest from the scientific community for diverse applications in the fields of sensing, energy, health, and environment. The main reasons are: their extensive surface area that increases the possibilities of engineering, their larger accessible active area, their porosity, and their sensitivity. In particular, semiconductor ceramic hollow nanofibers show greater space charge modulation depth, higher electronic transport properties, and shorter ion or electron diffusion length (e.g., for an enhanced charging–discharging rate. In this review, we discuss and introduce the latest developments of ceramic hollow nanofiber materials in terms of synthesis approaches. Particularly, electrospinning derivatives will be highlighted. The electrospun ceramic hollow nanofibers will be reviewed with respect to their most widely studied components, i.e., metal oxides. These nanostructures have been mainly suggested for energy and environmental remediation. Despite the various advantages of such one dimensional (1D nanostructures, their fabrication strategies need to be improved to increase their practical use. The domain of nanofabrication is still advancing, and its predictable shortcomings and bottlenecks must be identified and addressed. Inconsistency of the hollow nanostructure with regard to their composition and dimensions could be one of such challenges. Moreover, their poor scalability hinders their wide applicability for commercialization and industrial use.

  2. Effect of aluminum oxide doping on the structural, electrical, and optical properties of zinc oxide (AOZO) nanofibers synthesized by electrospinning

    International Nuclear Information System (INIS)

    Lotus, A.F.; Kang, Y.C.; Walker, J.I.; Ramsier, R.D.; Chase, G.G.

    2010-01-01

    Zinc oxide nanofibers doped with aluminum oxide were prepared by sol-gel processing and electrospinning techniques using polyvinylpyrrolidone (PVP), zinc acetate and aluminum acetate as precursors. The resulting nanofibers were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), UV-Vis spectroscopy, and current-voltage (I-V) properties. The nanofibers had diameters in the range of 60-150 nm. The incorporation of aluminum oxide resulted in a decrease in the crystallite sizes of the zinc oxide nanofibers. Aluminum oxide doped zinc oxide (AOZO) nanofibers exhibited lower bandgap energies compared to undoped zinc oxide nanofibers. However, as the aluminum content (Al/(Al + Zn) x 100%) was increased from 1.70 at.% to 3.20 at.% in the electrospinning solution, the bandgap energy increased resulting in lower conductivity. The electrical conductivity of the AOZO samples was found to depend on the amount of aluminum dopant in the matrix as reflected in the changes in oxidation state elucidated from XPS data. Electrospinning was found to be a productive, simple, and easy method for tuning the bandgap energy and conductivity of zinc oxide semiconducting nanofibers.

  3. Fabricated nano-fiber diameter as liquid concentration sensors

    Science.gov (United States)

    Chyad, Radhi M.; Mat Jafri, Mohd Zubir; Ibrahim, Kamarulazizi

    Nanofiber is characterized by thin, long, and very soft silica. Taper fibers are made using an easy and low cost chemical method. Etching is conducted with a HF solution to remove cladding and then a low molarity HF solution to reduce the fiber core diameter. One approach to on-line monitoring of the etching process uses spectrophotometer with a white light source. In the aforementioned technique, this method aims to determine the diameter of the reduced core and show the evolution of the two different processes from the nanofiber regime to the fixed regime in which the mode was remote from the surrounding evanescent field, intensity can propagate outside the segment fiber when the core diameter is less than 500 nm. Manufacturing technologies of nano-fiber sensors offer a number of approved properties of optical fiber sensors utilized in various sensory applications. The nano-fiber sensor is utilized to sense the difference in the concentration of D-glucose in double-distilled deionized water and to measure the refractive index (RI) of a sugar solution. Our proposed method exhibited satisfactory capability based on bimolecular interactions in the biological system. The response of the nano-fiber sensors indicates a different kind of interaction among various groups of AAs. These results can be interpreted in terms of solute-solute and solute-solvent interactions and the structure making or breaking ability of solutes in the given solution. This study utilized spectra photonics to measure the transmission of light through different concentrations of sugar solution, employing cell cumber and nano-optical fibers as sensors.

  4. Biomimetic electrospun nanofibers for tissue regeneration

    International Nuclear Information System (INIS)

    Liao, Susan; Li Bojun; Ma Zuwei; Wei He; Chan Casey; Ramakrishna, Seeram

    2006-01-01

    Nanofibers exist widely in human tissue with different patterns. Electrospinning nanotechnology has recently gained a new impetus due to the introduction of the concept of biomimetic nanofibers for tissue regeneration. The advanced electrospinning technique is a promising method to fabricate a controllable continuous nanofiber scaffold similar to the natural extracellular matrix. Thus, the biomedical field has become a significant possible application field of electrospun fibers. Although electrospinning has developed rapidly over the past few years, electrospun nanofibers are still at a premature research stage. Further comprehensive and deep studies on electrospun nanofibers are essential for promoting their biomedical applications. Current electrospun fiber materials include natural polymers, synthetic polymers and inorganic substances. This review briefly describes several typically electrospun nanofiber materials or composites that have great potential for tissue regeneration, and describes their fabrication, advantages, drawbacks and future prospects. (topical review)

  5. Structural characterization and impedance studies of PbO nanofibers synthesized by electrospinning technique

    Energy Technology Data Exchange (ETDEWEB)

    Hari Prasad, Kamatam [Department of Physics, Pondicherry University, Puducherry, 605 014 (India); Vinoth, S. [Department of Physics, Pondicherry University, Puducherry, 605 014 (India); Centre for Nanoscience, Pondicherry University, Puducherry, 605014 (India); Jena, Paramananda [Department of Physics, Pondicherry University, Puducherry, 605 014 (India); School of Materials Science and Technology, Indian Institute of Technology(BHU), Varanasi, 221 005 (India); Venkateswarlu, M. [R & D, Amara Raja Batteries Ltd, Karakambadi, 517 520, A.P (India); Satyanarayana, N., E-mail: nallanis2011@gmail.com [Department of Physics, Pondicherry University, Puducherry, 605 014 (India)

    2017-06-15

    One-dimensional electrospun lead oxide nanofibers synthesized by a simple electrospinning technique. The prepared lead oxide nanofibers investigated by using TG/DTA, FTIR, Raman, X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) surface area analyzer, scanning electron microscopy–energy dispersive X-ray spectroscopy (SEM-EDX), atomic force microscopy (AFM), Transmission electron microscopy (TEM), and impedance spectroscopy techniques. TG/DTA results confirmed the thermal behavior of the as-spun nanofibers. XRD, FTIR, and Raman spectra results, respectively, confirm the formation of pure orthorhombic crystalline phase and structural coordination of the lead oxide (β-PbO) nanofibers. The BET specific surface area of β-PbO nanofibers sample is found to be 51.23 m{sup 2} g{sup -1}. SEM and AFM micrographs showed the formation of β-PbO nanofibers with a diameter of 85–300 nm. The impedance measurements of lead oxide nanofibers as a function of temperature, 25–150 °C, was evaluated by analyzing the measured impedance data using the winfit software. The electrical conductivity of the lead oxide (β-PbO) nanofibers evaluated by analyzing the measured impedance data using the winfit software is found to be 5.68 × 10{sup -6} S cm{sup -1} at 150 °C. Also, an activation energy (E{sub a}) for the migration of the charge carrier evaluated from the temperature dependence of conductivity plot is found to be 0.27 eV. The temperature dependence AC conductivity of β-PbO nanofibers was evaluated using the measured impedance data and sample dimension. The observed variation of high-frequency AC conductivity attributed to the hopping electrons between the adjacent sites. - Highlights: • First time, β-PbO nanofibers were successfully prepared by electrospinning technique. • Structural, morphological, roughness and electrical properties are studied. • TG/DTA, XRD, FTIR, Raman, SEM/AFM, TEM-EDX, and impedance measurements were made.

  6. Pore-Structure-Optimized CNT-Carbon Nanofibers from Starch for Rechargeable Lithium Batteries

    Directory of Open Access Journals (Sweden)

    Yongjin Jeong

    2016-12-01

    Full Text Available Porous carbon materials are used for many electrochemical applications due to their outstanding properties. However, research on controlling the pore structure and analyzing the carbon structures is still necessary to achieve enhanced electrochemical properties. In this study, mesoporous carbon nanotube (CNT-carbon nanofiber electrodes were developed by heat-treatment of electrospun starch with carbon nanotubes, and then applied as a binder-free electrochemical electrode for a lithium-ion battery. Using the unique lamellar structure of starch, mesoporous CNT-carbon nanofibers were prepared and their pore structures were controlled by manipulating the heat-treatment conditions. The activation process greatly increased the volume of micropores and mesopores of carbon nanofibers by etching carbons with CO2 gas, and the Brunauer-Emmett-Teller (BET specific area increased to about 982.4 m2·g−1. The activated CNT-carbon nanofibers exhibited a high specific capacity (743 mAh·g−1 and good cycle performance (510 mAh·g−1 after 30 cycles due to their larger specific surface area. This condition presents many adsorption sites of lithium ions, and higher electrical conductivity, compared with carbon nanofibers without CNT. The research suggests that by controlling the heat-treatment conditions and activation process, the pore structure of the carbon nanofibers made from starch could be tuned to provide the conditions needed for various applications.

  7. Tailored surface structure of LiFePO4/C nanofibers by phosphidation and their electrochemical superiority for lithium rechargeable batteries.

    Science.gov (United States)

    Lee, Yoon Cheol; Han, Dong-Wook; Park, Mihui; Jo, Mi Ru; Kang, Seung Ho; Lee, Ju Kyung; Kang, Yong-Mook

    2014-06-25

    We offer a brand new strategy for enhancing Li ion transport at the surface of LiFePO4/C nanofibers through noble Li ion conducting pathways built along reduced carbon webs by phosphorus. Pristine LiFePO4/C nanofibers composed of 1-dimensional (1D) LiFePO4 nanofibers with thick carbon coating layers on the surfaces of the nanofibers were prepared by the electrospinning technique. These dense and thick carbon layers prevented not only electrolyte penetration into the inner LiFePO4 nanofibers but also facile Li ion transport at the electrode/electrolyte interface. In contrast, the existing strong interactions between the carbon and oxygen atoms on the surface of the pristine LiFePO4/C nanofibers were weakened or partly broken by the adhesion of phosphorus, thereby improving Li ion migration through the thick carbon layers on the surfaces of the LiFePO4 nanofibers. As a result, the phosphidated LiFePO4/C nanofibers have a higher initial discharge capacity and a greatly improved rate capability when compared with pristine LiFePO4/C nanofibers. Our findings of high Li ion transport induced by phosphidation can be widely applied to other carbon-coated electrode materials.

  8. Electrospun nanofiber scaffolds: engineering soft tissues

    International Nuclear Information System (INIS)

    Kumbar, S G; Nukavarapu, S P; Laurencin, C T; James, R

    2008-01-01

    Electrospinning has emerged to be a simple, elegant and scalable technique to fabricate polymeric nanofibers. Pure polymers as well as blends and composites of both natural and synthetics have been successfully electrospun into nanofiber matrices. Physiochemical properties of nanofiber matrices can be controlled by manipulating electrospinning parameters to meet the requirements of a specific application. Such efforts include the fabrication of fiber matrices containing nanofibers, microfibers, combination of nano-microfibers and also different fiber orientation/alignments. Polymeric nanofiber matrices have been extensively investigated for diversified uses such as filtration, barrier fabrics, wipes, personal care, biomedical and pharmaceutical applications. Recently electrospun nanofiber matrices have gained a lot of attention, and are being explored as scaffolds in tissue engineering due to their properties that can modulate cellular behavior. Electrospun nanofiber matrices show morphological similarities to the natural extra-cellular matrix (ECM), characterized by ultrafine continuous fibers, high surface-to-volume ratio, high porosity and variable pore-size distribution. Efforts have been made to modify nanofiber surfaces with several bioactive molecules to provide cells with the necessary chemical cues and a more in vivo like environment. The current paper provides an overlook on such efforts in designing nanofiber matrices as scaffolds in the regeneration of various soft tissues including skin, blood vessel, tendon/ligament, cardiac patch, nerve and skeletal muscle

  9. Electrospun nanofiber scaffolds: engineering soft tissues

    Energy Technology Data Exchange (ETDEWEB)

    Kumbar, S G; Nukavarapu, S P; Laurencin, C T [Department of Orthopaedic Surgery, University of Virginia, VA 22908 (United States); James, R [Department of Biomedical Engineering, University of Virginia, VA 22908 (United States)], E-mail: laurencin@virginia.edu

    2008-09-01

    Electrospinning has emerged to be a simple, elegant and scalable technique to fabricate polymeric nanofibers. Pure polymers as well as blends and composites of both natural and synthetics have been successfully electrospun into nanofiber matrices. Physiochemical properties of nanofiber matrices can be controlled by manipulating electrospinning parameters to meet the requirements of a specific application. Such efforts include the fabrication of fiber matrices containing nanofibers, microfibers, combination of nano-microfibers and also different fiber orientation/alignments. Polymeric nanofiber matrices have been extensively investigated for diversified uses such as filtration, barrier fabrics, wipes, personal care, biomedical and pharmaceutical applications. Recently electrospun nanofiber matrices have gained a lot of attention, and are being explored as scaffolds in tissue engineering due to their properties that can modulate cellular behavior. Electrospun nanofiber matrices show morphological similarities to the natural extra-cellular matrix (ECM), characterized by ultrafine continuous fibers, high surface-to-volume ratio, high porosity and variable pore-size distribution. Efforts have been made to modify nanofiber surfaces with several bioactive molecules to provide cells with the necessary chemical cues and a more in vivo like environment. The current paper provides an overlook on such efforts in designing nanofiber matrices as scaffolds in the regeneration of various soft tissues including skin, blood vessel, tendon/ligament, cardiac patch, nerve and skeletal muscle.

  10. Investigation of needleless electrospun PAN nanofiber mats

    Science.gov (United States)

    Sabantina, Lilia; Mirasol, José Rodríguez; Cordero, Tomás; Finsterbusch, Karin; Ehrmann, Andrea

    2018-04-01

    Polyacrylonitrile (PAN) can be spun from a nontoxic solvent (DMSO, dimethyl sulfoxide) and is nevertheless waterproof, opposite to the biopolymers which are spinnable from aqueous solutions. This makes PAN an interesting material for electrospinning nanofiber mats which can be used for diverse biotechnological or medical applications, such as filters, cell growth, wound healing or tissue engineering. On the other hand, PAN is a typical base material for producing carbon nanofibers. Nevertheless, electrospinning PAN necessitates convenient spinning parameters to create nanofibers without too many membranes or agglomerations. Thus we have studied the influence of spinning parameters on the needleless electrospinning process of PAN dissolved in DMSO and the resulting nanofiber mats.

  11. Evaluation of the genotoxicity of cellulose nanofibers.

    Science.gov (United States)

    de Lima, Renata; Oliveira Feitosa, Leandro; Rodrigues Maruyama, Cintia; Abreu Barga, Mariana; Yamawaki, Patrícia Cristina; Vieira, Isolda Jesus; Teixeira, Eliangela M; Corrêa, Ana Carolina; Caparelli Mattoso, Luiz Henrique; Fernandes Fraceto, Leonardo

    2012-01-01

    Agricultural products and by products provide the primary materials for a variety of technological applications in diverse industrial sectors. Agro-industrial wastes, such as cotton and curaua fibers, are used to prepare nanofibers for use in thermoplastic films, where they are combined with polymeric matrices, and in biomedical applications such as tissue engineering, amongst other applications. The development of products containing nanofibers offers a promising alternative for the use of agricultural products, adding value to the chains of production. However, the emergence of new nanotechnological products demands that their risks to human health and the environment be evaluated. This has resulted in the creation of the new area of nanotoxicology, which addresses the toxicological aspects of these materials. Contributing to these developments, the present work involved a genotoxicological study of different nanofibers, employing chromosomal aberration and comet assays, as well as cytogenetic and molecular analyses, to obtain preliminary information concerning nanofiber safety. The methodology consisted of exposure of Allium cepa roots, and animal cell cultures (lymphocytes and fibroblasts), to different types of nanofibers. Negative controls, without nanofibers present in the medium, were used for comparison. The nanofibers induced different responses according to the cell type used. In plant cells, the most genotoxic nanofibers were those derived from green, white, and brown cotton, and curaua, while genotoxicity in animal cells was observed using nanofibers from brown cotton and curaua. An important finding was that ruby cotton nanofibers did not cause any significant DNA breaks in the cell types employed. This work demonstrates the feasibility of determining the genotoxic potential of nanofibers derived from plant cellulose to obtain information vital both for the future usage of these materials in agribusiness and for an understanding of their environmental

  12. Preparation and Characterization of Highly Aligned Carbon Nanotubes/Polyacrylonitrile Composite Nanofibers

    Directory of Open Access Journals (Sweden)

    Yanhua Song

    2017-01-01

    Full Text Available In the electrospinning process, a modified parallel electrode method (MPEM, conducted by placing a positively charged ring between the needle and the parallel electrode collector, was used to fabricate highly aligned carbon nanotubes/polyacrylonitrile (CNTs/PAN composite nanofibers. Characterizations of the samples—such as morphology, the degree of alignment, and mechanical and conductive properties—were investigated by a combination of scanning electron microscopy (SEM, transmission electron microscopy (TEM, universal testing machine, high-resistance meter, and other methods. The results showed the MPEM could improve the alignment and uniformity of electrospun CNTs/PAN composite nanofibers, and enhance their mechanical and conductive properties. This meant the successful preparation of highly aligned CNT-reinforced PAN nanofibers with enhanced physical properties, suggesting their potential application in appliances and communication areas.

  13. Vertically Aligned Carbon Nanofiber based Biosensor Platform for Glucose Sensor

    Energy Technology Data Exchange (ETDEWEB)

    Al Mamun, Khandaker A.; Tulip, Fahmida S.; MacArthur, Kimberly; McFarlane, Nicole; Islam, Syed K.; Hensley, Dale

    2014-03-01

    Vertically aligned carbon nanofibers (VACNFs) have recently become an important tool for biosensor design. Carbon nanofibers (CNF) have excellent conductive and structural properties with many irregularities and defect sites in addition to exposed carboxyl groups throughout their surfaces. These properties allow a better immobilization matrix compared to carbon nanotubes and offer better resolution when compared with the FET-based biosensors. VACNFs can be deterministically grown on silicon substrates allowing optimization of the structures for various biosensor applications. Two VACNF electrode architectures have been employed in this study and a comparison of their performances has been made in terms of sensitivity, sensing limitations, dynamic range, and response time. The usage of VACNF platform as a glucose sensor has been verified in this study by selecting an optimum architecture based on the VACNF forest density. Read More: http://www.worldscientific.com/doi/abs/10.1142/S0129156414500062

  14. Quasi one dimensional transport in individual electrospun composite nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Avnon, A., E-mail: avnon@phys.fu-berlin.de; Datsyuk, V.; Trotsenko, S. [Institut für Experimentalphysik, Freie Universität Berlin, Arnimallee 14, 14195 Berlin (Germany); Wang, B.; Zhou, S. [Research Center of Microperipheric Technologies, Technische Universität Berlin, TiB4/2-1, Gustav-Meyer-Allee 25, 13355 Berlin (Germany); Grabbert, N.; Ngo, H.-D. [Microsystem Engineering (FB I), University of Applied Sciences, Wilhelminenhofstr. 74 (C 525), 12459 Berlin (Germany)

    2014-01-15

    We present results of transport measurements of individual suspended electrospun nanofibers Poly(methyl methacrylate)-multiwalled carbon nanotubes. The nanofiber is comprised of highly aligned consecutive multiwalled carbon nanotubes. We have confirmed that at the range temperature from room temperature down to ∼60 K, the conductance behaves as power-law of temperature with an exponent of α ∼ 2.9−10.2. The current also behaves as power law of voltage with an exponent of β ∼ 2.3−8.6. The power-law behavior is a footprint for one dimensional transport. The possible models of this confined system are discussed. Using the model of Luttinger liquid states in series, we calculated the exponent for tunneling into the bulk of a single multiwalled carbon nanotube α{sub bulk} ∼ 0.06 which agrees with theoretical predictions.

  15. Electrospun Ceramic Nanofiber Mats Today: Synthesis, Properties, and Applications

    Science.gov (United States)

    Esfahani, Hamid; Ramakrishna, Seeram

    2017-01-01

    Ceramic nanofibers (NFs) have recently been developed for advanced applications due to their unique properties. In this article, we review developments in electrospun ceramic NFs with regard to their fabrication process, properties, and applications. We find that surface activity of electrospun ceramic NFs is improved by post pyrolysis, hydrothermal, and carbothermal processes. Also, when combined with another surface modification methods, electrospun ceramic NFs result in the advancement of properties and widening of the application domains. With the decrease in diameter and length of a fiber, many properties of fibrous materials are modified; characteristics of such ceramic NFs are different from their wide and long (bulk) counterparts. In this article, electrospun ceramic NFs are reviewed with an emphasis on their applications as catalysts, membranes, sensors, biomaterials, fuel cells, batteries, supercapacitors, energy harvesting systems, electric and magnetic parts, conductive wires, and wearable electronic textiles. Furthermore, properties of ceramic nanofibers, which enable the above applications, and techniques to characterize them are briefly outlined. PMID:29077074

  16. Electrospun Ceramic Nanofiber Mats Today: Synthesis, Properties, and Applications

    Directory of Open Access Journals (Sweden)

    Hamid Esfahani

    2017-10-01

    Full Text Available Ceramic nanofibers (NFs have recently been developed for advanced applications due to their unique properties. In this article, we review developments in electrospun ceramic NFs with regard to their fabrication process, properties, and applications. We find that surface activity of electrospun ceramic NFs is improved by post pyrolysis, hydrothermal, and carbothermal processes. Also, when combined with another surface modification methods, electrospun ceramic NFs result in the advancement of properties and widening of the application domains. With the decrease in diameter and length of a fiber, many properties of fibrous materials are modified; characteristics of such ceramic NFs are different from their wide and long (bulk counterparts. In this article, electrospun ceramic NFs are reviewed with an emphasis on their applications as catalysts, membranes, sensors, biomaterials, fuel cells, batteries, supercapacitors, energy harvesting systems, electric and magnetic parts, conductive wires, and wearable electronic textiles. Furthermore, properties of ceramic nanofibers, which enable the above applications, and techniques to characterize them are briefly outlined.

  17. Determination of morphology and properties of carbon nanofibers and carbon nanofiber polymer nanocomposites

    Science.gov (United States)

    Lawrence, Joseph G.

    Vapor grown carbon nanofibers which resemble carbon nanotubes in structure and properties, have been extensively manufactured and investigated in recent years. Carbon nanofibers have been used for producing multifunctional materials due to their excellent properties and low cost of production. Since, commercially available vapor grown carbon nanofibers are subjected to different processing and post processing conditions, the morphology and properties of these nanofibers are not well-known. In this study, we focus on the characterization of the morphology and properties of these nanofibers and the polymer nanocomposites made using these nanofibers as reinforcements. The morphology of the nanofibers was studied employing high resolution Transmission Electron Microscopy (TEM) images. The analysis showed that the nanofibers consist primarily of conical nanofibers, but can contain a significant amount of bamboo nanofibers. Most of the conical nanofibers were found to consist of an ordered inner layer and a disordered outer layer, with the cone angle distribution of the inner layers indicating that these cannot have a stacked cone structure but are compatible with a cone-helix structure. Nanofibers that were heat treated to temperatures above 1,500°C undergo a structural transformation with the ordered inner layers changing from a cone-helix structure to a highly ordered multiwall stacked cone structure. Due to the complexity in the structure of these nanofibers, a novel method to study the elastic properties and corresponding morphology of individual nanofibers has been developed combining Atomic Force Microscopy (AFM), TEM and Focused Ion Beam (FIB) technology. Employing the developed method, the elastic modulus of individual nanofibers and their corresponding dimensions and morphology were determined. The dependence of elastic properties on the wall thickness and the orientation of graphene sheets in the nanofibers were studied. The elastic modulus of these

  18. Preparation, process optimization and characterization of core-shell polyurethane/chitosan nanofibers as a potential platform for bioactive scaffolds.

    Science.gov (United States)

    Maleknia, Laleh; Dilamian, Mandana; Pilehrood, Mohammad Kazemi; Sadeghi-Aliabadi, Hojjat; Hekmati, Amir Houshang

    2018-06-01

    In this paper, polyurethane (PU), chitosan (Cs)/polyethylene oxide (PEO), and core-shell PU/Cs nanofibers were produced at the optimal processing conditions using electrospinning technique. Several methods including SEM, TEM, FTIR, XRD, DSC, TGA and image analysis were utilized to characterize these nanofibrous structures. SEM images exhibited that the core-shell PU/Cs nanofibers were spun without any structural imperfections at the optimized processing conditions. TEM image confirmed the PU/Cs core-shell nanofibers were formed apparently. It that seems the inclusion of Cs/PEO to the shell, did not induce the significant variations in the crystallinity in the core-shell nanofibers. DSC analysis showed that the inclusion of Cs/PEO led to the glass temperature of the composition increased significantly compared to those of neat PU nanofibers. The thermal degradation of core-shell PU/Cs was similar to PU nanofibers degradation due to the higher PU concentration compared to other components. It was hypothesized that the core-shell PU/Cs nanofibers can be used as a potential platform for the bioactive scaffolds in tissue engineering. Further biological tests should be conducted to evaluate this platform as a three dimensional scaffold with the capabilities of releasing the bioactive molecules in a sustained manner.

  19. Effect of CSA Concentration on the Ammonia Sensing Properties of CSA-Doped PA6/PANI Composite Nanofibers

    Directory of Open Access Journals (Sweden)

    Zengyuan Pang

    2014-11-01

    Full Text Available Camphor sulfonic acid (CSA-doped polyamide 6/polyaniline (PA6/PANI composite nanofibers were fabricated using in situ polymerization of aniline under different CSA concentrations (0.02, 0.04, 0.06, 0.08 and 0.10 M with electrospun PA6 nanofibers as templates. The structural, morphological and ammonia sensing properties of the prepared composite nanofibers were studied using scanning electron microscopy (SEM, Fourier transform infrared spectroscopy (FT-IR, four-point probe techniques, X-ray diffraction (XRD and a home-made gas sensing test system. All the results indicated that the CSA concentration had a great influence on the sensing properties of CSA-doped PA6/PANI composite nanofibers. The composite nanofibers doped with 0.02 M CSA showed the best ammonia sensing properties, with a significant sensitivity toward ammonia (NH3 at room temperature, superior to that of the composite nanofibers doped with 0.04–0.10 mol/L CSA. It was found that for high concentrations of CSA, the number of PANI–H+ reacted with NH3 would not make up a high proportion of all PANI–H+ within certain limits. As a result, within a certain range even though higher CSA-doped PA6/PANI nanofibers had better conductivity, their ammonia sensing performance would degrade.

  20. Electrospinning and characterization of polyamide 66 nanofibers with different molecular weights

    Directory of Open Access Journals (Sweden)

    Lilia Muller Guerrini

    2009-06-01

    Full Text Available Polyamide 66 (PA66 nanofibers of different molecular weights were obtained by electrospinning of formic acid solutions. An ionic salt, NaCl, was also added to the solutions to increase the conductivity. PA66 concentrations between 15-17 wt.(%/v and electrical fields between 2.0 and 2.5 kV/cm were the best conditions to produce the smallest nanofibers; however, the addition of NaCl increased the fibers average diameters.The characterization of the fibers was done by scanning electron microscopy (SEM, differential scanning calorimetry (DSC, wide angle X rays diffraction (WAXD and Fourier Transformed Infrared (FTIR. As the molecular weight decreased, the nanofibers average diameters also decreased; however, critical number average and weight average molecular weights were necessary for electrospinning. As the amounts of carboxyl terminal groups (CTG increased, the nanofibers average diameters decreased; however, above CTG's critical values of 8.7 x 10-5 mol.g-1 no electrospinning was possible. The addition of ionic salt increased the electrical conductivity of the solutions and increased the nanofibers' average diameters. By DSC, residual solvent in all the electrospun mats was found; two melting endotherms, one between 248 and 258 °C and the other one between 258 and 267 °C, depending on the sample were also observed. These endotherms were attributed to the melting, re-crystallization and re-melting of the PA66 α-phase. The nanofibers had low % of crystallinity compared to a textile fiber. By WAXS and FTIR, confirmation of the presence of α-phase crystals, of small dimensions and highly imperfect and of a very small amount of β and γ-phases crystals in the nanofibers structure was obtained.

  1. Electrospun MOF nanofibers as hydrogen storage media

    CSIR Research Space (South Africa)

    Ren, Jianwei

    2015-06-01

    Full Text Available showed that the incorporation of vacuum degassing was able to create visible porosity in and/or on the PAN nanofibers and the MOF nanocrystals inside the polymeric nanofibers were fully accessible by N2 and H2 gases. With 20 wt.% loading of MOF...

  2. Antibacterial properties of laser spinning glass nanofibers.

    Science.gov (United States)

    Echezarreta-López, M M; De Miguel, T; Quintero, F; Pou, J; Landin, M

    2014-12-30

    A laser-spinning technique has been used to produce amorphous, dense and flexible glass nanofibers of two different compositions with potential utility as reinforcement materials in composites, fillers in bone defects or scaffolds (3D structures) for tissue engineering. Morphological and microstructural analyses have been carried out using SEM-EDX, ATR-FTIR and TEM. Bioactivity studies allow the nanofibers with high proportion in SiO2 (S18/12) to be classified as a bioinert glass and the nanofibers with high proportion of calcium (ICIE16) as a bioactive glass. The cell viability tests (MTT) show high biocompatibility of the laser spinning glass nanofibers. Results from the antibacterial activity study carried out using dynamic conditions revealed that the bioactive glass nanofibers show a dose-dependent bactericidal effect on Sthaphylococcus aureus (S. aureus) while the bioinert glass nanofibers show a bacteriostatic effect also dose-dependent. The antibacterial activity has been related to the release of alkaline ions, the increase of pH of the medium and also the formation of needle-like aggregates of calcium phosphate at the surface of the bioactive glass nanofibers which act as a physical mechanism against bacteria. The antibacterial properties give an additional value to the laser-spinning glass nanofibers for different biomedical applications, such as treating or preventing surgery-associated infections. Copyright © 2014 Elsevier B.V. All rights reserved.

  3. Electrospun polymeric nanofibers for transdermal drug delivery

    Directory of Open Access Journals (Sweden)

    Mahya Rahmani

    2017-04-01

    Full Text Available Conventional transdermal drug delivery systems (TDDS have been designed for drug delivery through the skin. These systems use the permeability property of stratum corneum, the outermost surface layer of the skin. Applying polymeric micro and nanofibers in drug delivery has recently attracted great attention and the electrospinning technique is the preferred method for polymeric micro-nanofibers fabrication with a great potential for drug delivery. More studies in the field of nanofibers containing drug are divided two categories: first, preparation and characterization of nanofibers containing drug and second, investigation of their therapeutic applications. Drugs used in electrospun nanofibers can be categorized into three main groups, including antibiotics and antimicrobial agents, anti-inflammatory agents and vitamins with therapeutic applications. In this paper, we review the application of electrospun polymeric scaffolds in TDDS and also introduce several pharmaceutical and therapeutic agents which have been used in polymer nanofibrous patches.

  4. Growth of Y-shaped Carbon Nanofibers from Ethanol Flames

    Directory of Open Access Journals (Sweden)

    Cheng Jin

    2008-01-01

    Full Text Available Abstract Y-shaped carbon nanofibers as a multi-branched carbon nanostructure have potential applications in electronic devices. In this article, we report that several types of Y-shaped carbon nanofibers are obtained from ethanol flames. These Y-shaped carbon nanofibers have different morphologies. According to our experimental results, the growth mechanism of Y-shaped carbon nanofibers has been discussed and a possible growth model of Y-shaped carbon nanofibers has been proposed.

  5. Fabrication of PEDOT coated PVA-GO nanofiber for supercapacitor

    International Nuclear Information System (INIS)

    Mohd Abdah, Muhammad Amirul Aizat; Zubair, Nur Afifah; Azman, Nur Hawa Nabilah; Sulaiman, Yusran

    2017-01-01

    Conducting nanofibers comprised of poly(vinyl alcohol) (PVA)-graphene oxide (GO) nanofiber coated with poly(3,4-ethylenedioxythiophene) (PEDOT) for supercapacitor application was prepared through integrated techniques i.e. electrospinning and electrodeposition. The formation of smooth cross-linking nanofibers without beads proved that GO has uniformly distributed into PVA with an average diameter of 117 ± 32 nm. Field emission scanning electron microscopy (FESEM) images revealed that cauliflower-like structure of PEDOT grew well on the surface of PVA-GO nanofibers with high porosity. Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy proved the existence of PVA, GO, and PEDOT. PVA-GO/PEDOT nanocomposite showed the highest specific capacitance (224.27 F/g) compared to PEDOT (167.92 F/g) and PVA/PEDOT (182.73 F/g). PVA-GO/PEDOT nanocomposite exhibited 1.8 V wide operating potential windows which significantly can enhance its capacitive behaviour. PVA-GO/PEDOT nanocomposite has also demonstrated superior performance with the energy density and power density of 9.58 Wh/kg and 304.37 W/kg, respectively at 1.0 A/g current density. PVA-GO/PEDOT nanocomposite revealed the smallest resistance of charge transfer (R_c_t) and equivalent series resistance (ESR) indicating excellent charge propagation behaviour at the interfacial region. The composite exhibits a good capacity retention of 82.41% after 2000 CV cycles and further drops 11.27% after 5000 cycles caused by the swelling and shrinkage of the electrode material during the charging and discharging processes. - Highlights: • PVA-GO/PEDOT was prepared via electrospinning and electrodeposition. • PVA-GO/PEDOT displays high capacitance value with wide potential window of 1.8 V. • PVA-GO/PEDOT exhibits high energy and power density, low R_c_t and ESR.

  6. Fabrication of PEDOT coated PVA-GO nanofiber for supercapacitor

    Energy Technology Data Exchange (ETDEWEB)

    Mohd Abdah, Muhammad Amirul Aizat; Zubair, Nur Afifah; Azman, Nur Hawa Nabilah [Department of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400, UPM Serdang, Selangor (Malaysia); Sulaiman, Yusran, E-mail: yusran@upm.edu.my [Department of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400, UPM Serdang, Selangor (Malaysia); Functional Device Laboratory, Institute of Advanced Technology, Universiti Putra Malaysia, 43400, UPM Serdang, Selangor (Malaysia)

    2017-05-01

    Conducting nanofibers comprised of poly(vinyl alcohol) (PVA)-graphene oxide (GO) nanofiber coated with poly(3,4-ethylenedioxythiophene) (PEDOT) for supercapacitor application was prepared through integrated techniques i.e. electrospinning and electrodeposition. The formation of smooth cross-linking nanofibers without beads proved that GO has uniformly distributed into PVA with an average diameter of 117 ± 32 nm. Field emission scanning electron microscopy (FESEM) images revealed that cauliflower-like structure of PEDOT grew well on the surface of PVA-GO nanofibers with high porosity. Fourier transform infrared spectroscopy (FTIR) and Raman spectroscopy proved the existence of PVA, GO, and PEDOT. PVA-GO/PEDOT nanocomposite showed the highest specific capacitance (224.27 F/g) compared to PEDOT (167.92 F/g) and PVA/PEDOT (182.73 F/g). PVA-GO/PEDOT nanocomposite exhibited 1.8 V wide operating potential windows which significantly can enhance its capacitive behaviour. PVA-GO/PEDOT nanocomposite has also demonstrated superior performance with the energy density and power density of 9.58 Wh/kg and 304.37 W/kg, respectively at 1.0 A/g current density. PVA-GO/PEDOT nanocomposite revealed the smallest resistance of charge transfer (R{sub ct}) and equivalent series resistance (ESR) indicating excellent charge propagation behaviour at the interfacial region. The composite exhibits a good capacity retention of 82.41% after 2000 CV cycles and further drops 11.27% after 5000 cycles caused by the swelling and shrinkage of the electrode material during the charging and discharging processes. - Highlights: • PVA-GO/PEDOT was prepared via electrospinning and electrodeposition. • PVA-GO/PEDOT displays high capacitance value with wide potential window of 1.8 V. • PVA-GO/PEDOT exhibits high energy and power density, low R{sub ct} and ESR.

  7. Towards scalable binderless electrodes: carbon coated silicon nanofiber paper via Mg reduction of electrospun SiO2 nanofibers.

    Science.gov (United States)

    Favors, Zachary; Bay, Hamed Hosseini; Mutlu, Zafer; Ahmed, Kazi; Ionescu, Robert; Ye, Rachel; Ozkan, Mihrimah; Ozkan, Cengiz S

    2015-02-06

    The need for more energy dense and scalable Li-ion battery electrodes has become increasingly pressing with the ushering in of more powerful portable electronics and electric vehicles (EVs) requiring substantially longer range capabilities. Herein, we report on the first synthesis of nano-silicon paper electrodes synthesized via magnesiothermic reduction of electrospun SiO2 nanofiber paper produced by an in situ acid catalyzed polymerization of tetraethyl orthosilicate (TEOS) in-flight. Free-standing carbon-coated Si nanofiber binderless electrodes produce a capacity of 802 mAh g(-1) after 659 cycles with a Coulombic efficiency of 99.9%, which outperforms conventionally used slurry-prepared graphite anodes by over two times on an active material basis. Silicon nanofiber paper anodes offer a completely binder-free and Cu current collector-free approach to electrode fabrication with a silicon weight percent in excess of 80%. The absence of conductive powder additives, metallic current collectors, and polymer binders in addition to the high weight percent silicon all contribute to significantly increasing capacity at the cell level.

  8. Carbon nanofibers obtained from electrospinning process

    Science.gov (United States)

    Bovi de Oliveira, Juliana; Müller Guerrini, Lília; Sizuka Oishi, Silvia; Rogerio de Oliveira Hein, Luis; dos Santos Conejo, Luíza; Cerqueira Rezende, Mirabel; Cocchieri Botelho, Edson

    2018-02-01

    In recent years, reinforcements consisting of carbon nanostructures, such as carbon nanotubes, fullerenes, graphenes, and carbon nanofibers have received significant attention due mainly to their chemical inertness and good mechanical, electrical and thermal properties. Since carbon nanofibers comprise a continuous reinforcing with high specific surface area, associated with the fact that they can be obtained at a low cost and in a large amount, they have shown to be advantageous compared to traditional carbon nanotubes. The main objective of this work is the processing of carbon nanofibers, using polyacrylonitrile (PAN) as a precursor, obtained by the electrospinning process via polymer solution, with subsequent use for airspace applications as reinforcement in polymer composites. In this work, firstly PAN nanofibers were produced by electrospinning with diameters in the range of (375 ± 85) nm, using a dimethylformamide solution. Using a furnace, the PAN nanofiber was converted into carbon nanofiber. Morphologies and structures of PAN and carbon nanofibers were investigated by scanning electron microscopy, Raman Spectroscopy, thermogravimetric analyses and differential scanning calorimeter. The resulting residual weight after carbonization was approximately 38% in weight, with a diameters reduction of 50%, and the same showed a carbon yield of 25%. From the analysis of the crystalline structure of the carbonized material, it was found that the material presented a disordered structure.

  9. Biofunctionalized Nanofibers Using Arthrospira (Spirulina Biomass and Biopolymer

    Directory of Open Access Journals (Sweden)

    Michele Greque de Morais

    2015-01-01

    Full Text Available Electrospun nanofibers composed of polymers have been extensively researched because of their scientific and technical applications. Commercially available polyhydroxybutyrate (PHB and polyhydroxybutyrate-co-valerate (PHB-HV copolymers are good choices for such nanofibers. We used a highly integrated method, by adjusting the properties of the spinning solutions, where the cyanophyte Arthrospira (formally Spirulina was the single source for nanofiber biofunctionalization. We investigated nanofibers using PHB extracted from Spirulina and the bacteria Cupriavidus necator and compared the nanofibers to those made from commercially available PHB and PHB-HV. Our study assessed nanofiber formation and their selected thermal, mechanical, and optical properties. We found that nanofibers produced from Spirulina PHB and biofunctionalized with Spirulina biomass exhibited properties which were equal to or better than nanofibers made with commercially available PHB or PHB-HV. Our methodology is highly promising for nanofiber production and biofunctionalization and can be used in many industrial and life science applications.

  10. The low temperature electrochemical performances of LiFePO4/C/graphene nanofiber with 3D-bridge network structure

    International Nuclear Information System (INIS)

    Xie, Dong; Cai, Guanglan; Liu, Zhichao; Guo, Ruisong; Sun, Dandan; Zhang, Chao; Wan, Yizao; Peng, Jianhong; Jiang, Hong

    2016-01-01

    Highlights: • Highly conductive graphene nanofibers were introduced into the LiFePO 4 /C matrix. • Graphene nanofiber modification improved the discharge capacity at low temperatures. • Graphene nanofiber reduced the polarization of the electrodes at low temperatures. • Modified electrodes exhibited decreased charge-transfer resistance. • Graphene nanofiber modified samples exhibited higher diffusion coefficient of lithium ions. - Abstract: Three-dimensionally assembled LiFePO 4 /C/graphene nanofiber composites were successfully prepared via a suspension mixing method followed by heat-treatment at 400 °C. A faster electron transfer, lower electrochemical polarization as well as higher diffusion coefficient of Li + are obtained with the assistance of graphene nanofibers. The 5 wt% graphene nanofibers modified electrode (G-5) delivers the best electrochemical kinetics including the lowest charge transfer resistance and highest diffusion coefficient of Li + at 0 °C and −20 °C, respectively. Likewise, the G-5 exhibits the highest charge-discharge capability and the most stable cycling performance at low operation temperatures compared with those of LiFePO 4 /C, 3 wt% and 7 wt% graphene nanofibers modified LiFePO 4 /C (G-3 and G-7) composites. The G-5 electrode shows a capacity of 92.8 mAh g −1 with 92.0% capacity retention after 200 cycles at 1C at −20 °C. The reasons for the significant improvement of the low operation temperatures electrochemical performances can be ascribed to the enhanced conductivity and reduced agglomeration of pristine particles due to the introduction of graphene nanofibers. These excellent low temperature performances show that graphene nanofibers modified LiFePO 4 /C electrodes are promising cathode candidates for lithium-ion batteries applications at low temperatures.

  11. Advancement in organic nanofiber based transistors

    DEFF Research Database (Denmark)

    Jensen, Per Baunegaard With; Kjelstrup-Hansen, Jakob; Tavares, Luciana

    and characterization of OLETs using the organic semiconductors para-hexaphenylene (p6P), 5,5´-Di-4-biphenyl-2,2´-bithiophene (PPTTPP) and 5,5'-bis(naphth-2-yl)-2,2'-bithiophene (NaT2). These molecules can self-assemble forming molecular crystalline nanofibers. Organic nanofibers can form the basis for light......The focus of this project is to study the light emission from nanofiber based organic light-emitting transistors (OLETs) with the overall aim of developing efficient, nanoscale light sources with different colors integrated on-chip. The research performed here regards the fabrication...

  12. Synergistic tungsten oxide/organic framework hybrid nanofibers for electrochromic device application

    Science.gov (United States)

    Dulgerbaki, Cigdem; Komur, Ali Ihsan; Nohut Maslakci, Neslihan; Kuralay, Filiz; Uygun Oksuz, Aysegul

    2017-08-01

    We report the first successful applications of tungsten oxide/conducting polymer hybrid nanofiber assemblies in electrochromic devices. Poly(3,4-ethylenedioxythiophene)/tungsten oxide (PEDOT/WO3) and polypyrrole/tungsten oxide (PPy/WO3) composites were prepared by an in situ chemical oxidative polymerization of monomers in different ionic liquids; 1-butyl-3-methylimidazolium tetrafluoroborate (BMIMBF4), 1-butyl-3-methylimidazolium hexafluorophosphate (BMIMPF6), 1-butyl-3-methylimidazolium bis(trifluoromethylsulfonyl) imide (BMIMTFSI) and 1-butyl-1-methylpyrrolidinium bis(trifluoromethylsulfonyl) imide (BMPTFSI). Electrospinning process was used to form hybrid nanofibers from chemically synthesized nanostructures. The electrospun hybrid samples were compared from both morphological and electrochemical perspectives. Importantly, deposition of nanofibers from chemically synthesized hybrids can be achieved homogenously, on nanoscale dimensions. The morphologies of these assemblies were evaluated by SEM, whereas their electroactivity was characterized by cyclic voltammetry. Electrochromic devices made from hybrid nanofiber electrodes exhibited highest chromatic contrast of 37.66% for PEDOT/WO3/BMIMPF6, 40.42% for PPy/WO3/BMIMBF4 and show a strong electrochromic color change from transparent to light brown. Furthermore, the nanofiber devices exhibit outstanding stability when color switching proceeds, which may ensure a versatile platform for color displays, rear-view mirrors and smart windows.

  13. Development of sodium alginate/PVA antibacterial nanofibers by the incorporation of essential oils

    Science.gov (United States)

    Rafiq, M.; Hussain, T.; Abid, S.; Nazir, A.; Masood, R.

    2018-03-01

    Electrospinning is a well known method for the manufacturing of nanoscale fibers. Electrospun nanofibers have higher surface area to volume ratio and can be used for the incorporation of different materials. Essential oils are well known for their antimicrobial and healing properties since ancient times. The main objective of this study was to develop antibacterial nanofibers by the incorporation of essential oils in sodium alginate/PVA solution. Sodium alginate and PVA have excellent biocompatible properties which are the base of their use in wound care applications. Three different essential oils (cinnamon, clove, and lavender) at three different concentrations (0.5, 1 and 1.5%) were used to optimize the fiber forming conditions during electrospinning and then the desired antibacterial properties were evaluated. Addition of oils in PVA/SA solutions increased the viscosity but reduced the surface tension and conductivity as compared to pure PVA/sodium alginate solution. FTIR Spectra of composite fibers verified the successful incorporation of essential oils in nanofibers through electrospinning. All oil containing samples showed good antibacterial properties against staphylococcus aureus which make them a good replacement of antibiotics. Cinnamon oil loaded nanofibers showed the best results among selected oils regarding the antibacterial properties. Nanofibers with 1.5% cinnamon oil exhibited highest zone of inhabitation of 2.7 cm. Nanofibrous coated cotton gauze showed higher liquid absorptions as compared to simple cotton gauze and potential to be used as wound dressings for its improved liquid absorption and antibacterial activity.

  14. Nanofibers and nanoparticles from the insect-capturing adhesive of the Sundew (Drosera for cell attachment

    Directory of Open Access Journals (Sweden)

    Zhang Mingjun

    2010-08-01

    Full Text Available Abstract Background The search for naturally occurring nanocomposites with diverse properties for tissue engineering has been a major interest for biomaterial research. In this study, we investigated a nanofiber and nanoparticle based nanocomposite secreted from an insect-capturing plant, the Sundew, for cell attachment. The adhesive nanocomposite has demonstrated high biocompatibility and is ready to be used with minimal preparation. Results Atomic force microscopy (AFM conducted on the adhesive from three species of Sundew found that a network of nanofibers and nanoparticles with various sizes existed independent of the coated surface. AFM and light microscopy confirmed that the pattern of nanofibers corresponded to Alcian Blue staining for polysaccharide. Transmission electron microscopy identified a low abundance of nanoparticles in different pattern form AFM observations. In addition, energy-dispersive X-ray spectroscopy revealed the presence of Ca, Mg, and Cl, common components of biological salts. Study of the material properties of the adhesive yielded high viscoelasticity from the liquid adhesive, with reduced elasticity observed in the dried adhesive. The ability of PC12 neuron-like cells to attach and grow on the network of nanofibers created from the dried adhesive demonstrated the potential of this network to be used in tissue engineering, and other biomedical applications. Conclusions This discovery demonstrates how a naturally occurring nanofiber and nanoparticle based nanocomposite from the adhesive of Sundew can be used for tissue engineering, and opens the possibility for further examination of natural plant adhesives for biomedical applications.

  15. Synthesis, characterization and photocatalytic performance of SnS nanofibers and SnSe nanofibers derived from the electrospinning-made SnO{sub 2} nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Cheng, Li; Li, Dan; Dong, Xiangting; Ma, Qianli; Yu, Wensheng; Wang, Xinlu; Yu, Hui; Wang, Jinxian; Liu, Guixia, E-mail: dongxiangting888@163.com [Key Laboratory of Applied Chemistry and Nanotechnology at Universities of Jilin Province, Changchun University of Science and Technology, Changchun (China)

    2017-11-15

    SnO{sub 2} nanofibers were fabricated by calcination of the electrospun PVP/SnCl{sub 4} composite nanofibers. For the first time, SnS nanofibers and SnSe nanofibers were successfully synthesized by double crucible sulfurization and selenidation methods via inheriting the morphology of SnO{sub 2} nanofibers used as precursors, respectively. X-ray diffraction (XRD) analysis shows SnS nanofibers and SnSe nanofibers are respectively pure orthorhombic phase with space group of Pbnm and Cmcm. Scanning electron microscope (SEM) observation indicates that the diameters of SnS nanofibers and SnSe nanofibers are respectively 140.54±12.80 nm and 96.52±14.17 nm under the 95 % confidence level. The photocatalytic activities of samples were studied by using rhodamine B (Rh B) as degradation agent. When SnS or SnSe nanofibers are employed as the photocatalysts, the respective degradation rates of Rh B solution under the ultraviolet light irradiation after 200 min irradiation are 92.55 % and 92.86 %. The photocatalytic mechanism and formation process of SnS and SnSe nanofibers are also provided. More importantly, this preparation technique is of universal significance to prepare other metal chalcogenides nanofibers. (author)

  16. Polyurethane nanofibers containing copper nanoparticles as future materials

    DEFF Research Database (Denmark)

    Sheikh, Faheem A.; Kanjwal, Muzafar Ahmed; Saran, Saurabh

    2011-01-01

    nanofibers. Typically, a colloidal gel consisting of copper NPs and polyurethane has been electrospun. SEM-EDX and TEM results confirmed well oriented nanofibers and good dispersion of pure copper NPs. Copper NPs have diameter in the range of 5–10nm. The thermal stability of the synthesized nanofibers...... the antimicrobial efficacy of these nanofiber mats. Subsequently, antimicrobial tests have indicated that the prepared nanofibers do posses good bactericidal effect. Accordingly, it is noted that the obtained nanofiber mats can be used as future filter membranes with good antimicrobial activities....

  17. All-textile flexible supercapacitors using electrospun poly(3,4-ethylenedioxythiophene) nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Laforgue, Alexis [Functional Polymer Systems Group, Industrial Materials Institute, National Research Council Canada, 75, de Mortagne Blvd, Boucherville, Quebec J4B 6Y4 (Canada)

    2011-01-01

    Poly(3,4-ethylenedioxythiophene) (PEDOT) nanofibers were obtained by the combination of electrospinning and vapor-phase polymerization. The fibers had diameters around 350 nm, and were soldered at most intersections, providing a strong dimensional stability to the mats. The nanofiber mats demonstrated very high conductivity (60 {+-} 10 S cm{sup -1}, the highest value reported so far for polymer nanofibers) as well as improved electrochemical properties, due to the ultraporous nature of the electrospun mats. The mats were incorporated into all-textile flexible supercapacitors, using carbon cloths as the current collectors and electrospun polyacrylonitrile (PAN) nanofibrous membranes as the separator. The textile layers were stacked and embedded in a solid electrolyte containing an ionic liquid and PVDF-co-HFP as the host polymer. The resulting supercapacitors were totally flexible and demonstrated interesting and stable performances in ambient conditions. (author)

  18. High-performance supercapacitors based on hollow polyaniline nanofibers by electrospinning.

    Science.gov (United States)

    Miao, Yue-E; Fan, Wei; Chen, Dan; Liu, Tianxi

    2013-05-22

    Hollow polyaniline (PANI) nanofibers with controllable wall thickness are fabricated by in situ polymerization of aniline using the electrospun poly(amic acid) fiber membrane as a template. A maximum specific capacitance of 601 F g(-1) has been achieved at 1 A g(-1), suggesting the potential application of hollow PANI nanofibers for supercapacitors. The superior electrochemical performance of the hollow nanofibers is attributed to their hollow structure, thin wall thickness, and orderly pore passages, which can drastically facilitate the ion diffusion and improve the utilization of the electroactive PANI during the charge-discharge processes. Furthermore, the high flexibility of the self-standing fiber membrane template provides possibilities for the facile construction and fabrication of conducting polymers with hollow nanostructures, which may find potential applications in various high-performance electrochemical devices.

  19. Electrospun Nanofibers: Solving Global Issues

    Science.gov (United States)

    Si, Yang; Tang, Xiaomin; Yu, Jianyong; Ding, Bin

    Energy and environment will head the list of top global issues facing society for the next 50 years. Nanotechnology is responding to these challenges by designing and fabricating functional nanofibers optimized for energy and environmental applications. The route toward these nano-objects is based primarily on electrospinning: a highly versatile method that allows the fabrication of continuous fibers with diameters down to a few nanometers. The mechanism responsible for the fiber formation mainly includes the Taylor Cone theory and flight-instability theory, which can be predicted theoretically and controlled experimentally. Moreover, the electrospinning has been applied to natural polymers, synthetic polymers, ceramics, and carbon. Fibers with complex architectures, such as ribbon fiber, porous fiber, core-shell fiber, or hollow fiber, can be produced by special electrospinning methods. It is also possible to produce nanofibrous membranes with designed aggregate structure including alignment, patterning, and two-dimensional nanonets. Finally, the brief analysis of nanofibers used for advanced energy and environmental applications in the past decade indicates that their impact has been realized well and is encouraging, and will continually represent a key technology to ensure sustainable energy and preserve our environment for the future.

  20. Enhanced cell mitochondrial activity using electrospun nanofibers

    CSIR Research Space (South Africa)

    Jacobs, V

    2015-06-01

    Full Text Available Research in tissue engineering related to the improved processes using nanofiber scaffolds has seen considerable progress in the last decade in the regeneration and construction of a number of artificial tissue types. These designs are generally...

  1. Surface structure enhanced second harmonic generation in organic nanofibers

    DEFF Research Database (Denmark)

    Fiutowski, Jacek; Maibohm, Christian; Kostiučenko, Oksana

    Second-harmonic generation upon femto-second laser irradiation of nonlinearly optically active nanofibers grown from nonsymmetrically functionalized para-quarterphenylene (CNHP4) molecules is investigated. Following growth on mica templates, the nanofibers have been transferred onto lithography...

  2. Field-enhanced nonlinear optical properties of organic nanofibers

    DEFF Research Database (Denmark)

    Kostiučenko, Oksana; Fiutowski, Jacek; Brewer, Jonathan R.

    2014-01-01

    Second harmonic generation in nonlinearly optically active organic nanofibers, generated via self-assembled surface growth from nonsymmetrically functionalized para-quarterphenylene (CNHP4) molecules, has been investigated. After the growth on mica templates, nanofibers have been transferred onto...

  3. Increased thermal conductivity monolithic zeolite structures

    Science.gov (United States)

    Klett, James; Klett, Lynn; Kaufman, Jonathan

    2008-11-25

    A monolith comprises a zeolite, a thermally conductive carbon, and a binder. The zeolite is included in the form of beads, pellets, powders and mixtures thereof. The thermally conductive carbon can be carbon nano-fibers, diamond or graphite which provide thermal conductivities in excess of about 100 W/mK to more than 1,000 W/mK. A method of preparing a zeolite monolith includes the steps of mixing a zeolite dispersion in an aqueous colloidal silica binder with a dispersion of carbon nano-fibers in water followed by dehydration and curing of the binder is given.

  4. Electrospinning cellulose based nanofibers for sensor applications

    Science.gov (United States)

    Nartker, Steven

    2009-12-01

    Bacterial pathogens have recently become a serious threat to the food and water supply. A biosensor based on an electrochemical immunoassay has been developed for detecting food borne pathogens, such as Escherichia coli (E. coli) O157:H7. These sensors consist of several materials including, cellulose, cellulose nitrate, polyaniline and glass fibers. The current sensors have not been optimized in terms of microscale architecture and materials. The major problem associated with the current sensors is the limited concentration range of pathogens that provides a linear response on the concentration conductivity chart. Electrospinning is a process that can be used to create a patterned fiber mat design that will increase the linear range and lower the detection limit of these sensors by improving the microscale architecture. Using the electrospinning process to produce novel mats of cellulose nitrate will offer improved surface area, and the cellulose nitrate can be treated to further improve chemical interactions required for sensor activity. The macro and micro architecture of the sensor is critical to the performance of the sensors. Electrospinning technology can be used to create patterned architectures of nanofibers that will enhance sensor performance. To date electrospinning of cellulose nitrate has not been performed and optimization of the electrospinning process will provide novel materials suitable for applications such as filtration and sensing. The goal of this research is to identify and elucidate the primary materials and process factors necessary to produce cellulose nitrate nanofibers using the electrospinning process that will improve the performance of biosensors. Cellulose nitrate is readily dissolved in common organic solvents such as acetone, tetrahydrofuran (THF) and N,N dimethylformamide (DMF). These solvents can be mixed with other latent solvents such as ethanol and other alcohols to provide a solvent system with good electrospinning behavior

  5. Obtaining nanofibers from sisal to reinforce nanocomposites biodegradable matrixes

    International Nuclear Information System (INIS)

    Oliveira, Francieli B. de; Teixeira, Eliangela de M.; Marconcini, Jose M.; Mattoso, Luiz H.C.; Teodoro, Kelcilene B.R.

    2009-01-01

    Cellulose nanofibers have been extracted by acid hydrolysis from sisal fibers. They are seen a good source material due to availability and low cost. The nanofibers was evaluated by thermal degradation behavior using thermogravimetry (TG), crystallinity by X-ray diffraction and morphological structure was investigated by atomic force microscopy (AFM) experiments. The resulting nanofibers was shown high crystallinity and a network of rodlike cellulose elements. The nanofibers will be incorporated as reinforcement in a biodegradable matrix and evaluated. (author)

  6. Carbon Nanofiber Electrode Array for Neurochemical Monitoring

    Science.gov (United States)

    Koehne, Jessica E.

    2017-01-01

    A sensor platform based on vertically aligned carbon nanofibers (CNFs) has been developed. Their inherent nanometer scale, high conductivity, wide potential window, good biocompatibility and well-defined surface chemistry make them ideal candidates as biosensor electrodes. Here, we report using vertically aligned CNF as neurotransmitter recording electrodes for application in a smart deep brain stimulation (DBS) device. Our approach combines a multiplexed CNF electrode chip, developed at NASA Ames Research Center, with the Wireless Instantaneous Neurotransmitter Concentration Sensor (WINCS) system, developed at the Mayo Clinic. Preliminary results indicate that the CNF nanoelectrode arrays are easily integrated with WINCS for neurotransmitter detection in a multiplexed array format. In the future, combining CNF based stimulating and recording electrodes with WINCS may lay the foundation for an implantable smart therapeutic system that utilizes neurochemical feedback control while likely resulting in increased DBS application in various neuropsychiatric disorders. In total, our goal is to take advantage of the nanostructure of CNF arrays for biosensing studies requiring ultrahigh sensitivity, high-degree of miniaturization, and selective biofunctionalization.

  7. High thermoelectric performance of graphite nanofibers.

    Science.gov (United States)

    Tran, Van-Truong; Saint-Martin, Jérôme; Dollfus, Philippe; Volz, Sebastian

    2018-02-22

    Graphite nanofibers (GNFs) have been demonstrated to be a promising material for hydrogen storage and heat management in electronic devices. Here, by means of first-principles and transport simulations, we show that GNFs can also be an excellent material for thermoelectric applications thanks to the interlayer weak van der Waals interaction that induces low thermal conductance and a step-like shape in the electronic transmission with mini-gaps, which are necessary ingredients to achieve high thermoelectric performance. This study unveils that the platelet form of GNFs in which graphite layers are perpendicular to the fiber axis can exhibit outstanding thermoelectric properties with a figure of merit ZT reaching 3.55 in a 0.5 nm diameter fiber and 1.1 in a 1.1 nm diameter one. Interestingly, by introducing 14 C isotope doping, ZT can even be enhanced up to more than 5, and more than 8 if we include the effect of finite phonon mean free path, which demonstrates the amazing thermoelectric potential of GNFs.

  8. Aramid Nanofiber Composites for Energy Storage Applications

    Science.gov (United States)

    Tung, Siu on

    Lithium ion batteries and non-aqueous redox flow batteries represent two of the most important energy storage technologies to efficient electric vehicles and power grid, which are essential to decreasing U.S. dependence on fossil fuels and sustainable economic growth. Many of the developmental roadblocks for these batteries are related to the separator, an electrically insulating layer between the cathode and anode. Lithium dendrite growth has limited the performance and threatened the safety of lithium ion batteries by piercing the separator and causing internal shorts. In non-aqueous redox flow batteries, active material crossover through microporous separators and the general lack of a suitable ion conducting membrane has led to low operating efficiencies and rapid capacity fade. Developing new separators for these batteries involve the combination of different and sometimes seemingly contradictory properties, such as high ionic conductivity, mechanical stability, thermal stability, chemical stability, and selective permeability. In this dissertation, I present work on composites made from Kevlar-drived aramid nanofibers (ANF) through rational design and fabrication techniques. For lithium ion batteries, a dendrite suppressing layer-by-layer composite of ANF and polyethylene oxide is present with goals of high ionic conductivity, improved safety and thermal stability. For non-aqueous redox flow batteries, a nanoporous ANF separator with surface polyelectrolyte modification is used to achieve high coulombic efficiencies and cycle life in practical flow cells. Finally, manufacturability of ANF based separators is addressed through a prototype machine for continuous ANF separator production and a novel separator coated on anode assembly. In combination, these studies serve as a foundation for addressing the challenges in separator engineering for lithium ion batteries and redox flow batteries.

  9. Corrosion protection performance of waterborne epoxy coatings containing self-doped polyaniline nanofiber

    International Nuclear Information System (INIS)

    Qiu, Shihui; Chen, Cheng; Cui, Mingjun; Li, Wei; Zhao, Haichao; Wang, Liping

    2017-01-01

    Highlights: • Self-dopedpolyaniline (SPANi) with good conductivity and dispersibility in water was copolymerized by aniline and its derivative. • Environmental friendly SPANi/epoxy composite coating with remarkable anti-corrosion performance was prepared. • The corrosion product of pure epoxy or composite coating was characterized by X-ray diffraction pattern and scanning electron microscope (SEM). - Abstract: Self-doped sulfonated polyaniline (SPANi) nanofiber was synthesized by the copolymerization of 2-aminobenzenesulfonic acid (ASA) and aniline via a rapid mixing polymerization approach. The chemical structure of SPANi was investigated by the Fourier-transform infrared (FT-IR), Raman, X-ray photoelectron spectroscopy (XPS), UV–vis spectra and X-ray diffraction (XRD) pattern. The as-prepared SPANi nanofibers had 45 nm average diameter and length up to 750 nm as measured by scanning electron microscope (SEM) and transmission electron microscope (TEM). The self-doped SPANi nanofiber possessed excellent aqueous solubility, good conductivity (0.11 S/cm) and reversible redox activity, making it suitable as a corrosion inhibitor for waterborne coatings. The prepared SPANi/waterborne epoxy composite coatings exhibited remarkably improved corrosion protection compared with pure waterborne epoxy coating as proved by the polarization curves and electrochemical impedance spectroscopy (EIS). The passivation effect of SPANi nanofiber and the corrosion products beneath the epoxy coatings immersed in 3.5% NaCl solution as a function of time were also investigated in this study.

  10. Corrosion protection performance of waterborne epoxy coatings containing self-doped polyaniline nanofiber

    Energy Technology Data Exchange (ETDEWEB)

    Qiu, Shihui [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, 315201 (China); Faculty of Materials Science and Chemical Engineering, Ningbo University, Ningbo, 315211 (China); Chen, Cheng; Cui, Mingjun [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, 315201 (China); Li, Wei [Faculty of Materials Science and Chemical Engineering, Ningbo University, Ningbo, 315211 (China); Zhao, Haichao, E-mail: zhaohaichao@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, 315201 (China); Wang, Liping, E-mail: wangliping@nimte.ac.cn [Key Laboratory of Marine Materials and Related Technologies, Zhejiang Key Laboratory of Marine Materials and Protective Technologies, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, Ningbo, 315201 (China)

    2017-06-15

    Highlights: • Self-dopedpolyaniline (SPANi) with good conductivity and dispersibility in water was copolymerized by aniline and its derivative. • Environmental friendly SPANi/epoxy composite coating with remarkable anti-corrosion performance was prepared. • The corrosion product of pure epoxy or composite coating was characterized by X-ray diffraction pattern and scanning electron microscope (SEM). - Abstract: Self-doped sulfonated polyaniline (SPANi) nanofiber was synthesized by the copolymerization of 2-aminobenzenesulfonic acid (ASA) and aniline via a rapid mixing polymerization approach. The chemical structure of SPANi was investigated by the Fourier-transform infrared (FT-IR), Raman, X-ray photoelectron spectroscopy (XPS), UV–vis spectra and X-ray diffraction (XRD) pattern. The as-prepared SPANi nanofibers had 45 nm average diameter and length up to 750 nm as measured by scanning electron microscope (SEM) and transmission electron microscope (TEM). The self-doped SPANi nanofiber possessed excellent aqueous solubility, good conductivity (0.11 S/cm) and reversible redox activity, making it suitable as a corrosion inhibitor for waterborne coatings. The prepared SPANi/waterborne epoxy composite coatings exhibited remarkably improved corrosion protection compared with pure waterborne epoxy coating as proved by the polarization curves and electrochemical impedance spectroscopy (EIS). The passivation effect of SPANi nanofiber and the corrosion products beneath the epoxy coatings immersed in 3.5% NaCl solution as a function of time were also investigated in this study.

  11. Preparation and characterization of kefiran electrospun nanofibers.

    Science.gov (United States)

    Esnaashari, Seyedeh Sara; Rezaei, Sasan; Mirzaei, Esmaeil; Afshari, Hamed; Rezayat, Seyed Mahdi; Faridi-Majidi, Reza

    2014-09-01

    In this study, we report the first successful production of kefiran nanofibers through electrospinning process using distilled water as solvent. For this purpose, kefiran was extracted from cultured kefir grains, and homogenous kefiran solutions with different concentrations were prepared and then electrospun to obtain uniform nanofibers. The effect of main process parameters, including applied voltage, tip-to-collector distance, and feeding rate, on diameter and morphology of produced nanofibers, was studied. Scanning electron microscopy (SEM) and attenuated total reflectance Fourier transform infrared (ATR-FTIR) spectroscopy were used to characterize electrospun mats. Rheological behavior of the kefiran solution was evaluated via a cone and plate rheometer too. The results exhibited that diameter of kefiran nanofibers increased with increasing polymer concentration, applied voltage, and polymer feeding rate, while tip-to-collector distance did not have significant effect on nanofiber diameter. ATR-FTIR spectra showed that kefiran has maintained its molecular structure during electrospinning process. Flow curves also demonstrated shear thinning behavior for kefiran solutions. Copyright © 2014 Elsevier B.V. All rights reserved.

  12. Cotton nanofibers obtained by different acid conditions

    International Nuclear Information System (INIS)

    Teixeira, Eliangela de M.; Oliveira, Caue Ribeiro de; Mattoso, Luiz H.C.; Correa, Ana Carolina; Palladin, Priscila

    2009-01-01

    The thermal stability of cellulose nanofibers is related to their application and especially to polymer processing which temperatures of processing are around 200 deg C. In this work, nanofibers of commercial cotton were obtained by acid hydrolysis employing different acids: sulfuric, hydrochloric and a mixture (2:1; sulfuric acid: hydrochloric acid).The morphology of the nanofibers were characterized by transmission microscopy (TEM), crystallinity by x-ray diffraction (XRD) and thermal stability in air atmosphere by thermogravimetric analysis (TGA). The results indicated a very similar morphology and crystallinity among them. The main differences were relative to aggregation state e and thermal stability. The aggregation state of the suspensions decreases in the order HCl 2 SO 4 :HCl 2 SO 4- . The hydrolysis with a mix of HCl and H 2 SO 4 resulted in cellulose nanofibers with higher thermal stability than those hydrolyzed with H 2 SO 4 . The hydrolysis employed with a mixture of sulphuric and hydrochloric acids also showed a better dispersion than those suspensions of nanofibers obtained by hydrolysis with only HCl. (author)

  13. PANI-nanofibers/polyethylene blends: preparation and properties

    International Nuclear Information System (INIS)

    Oliveira, F.; Hubler, R.; Basso, N.R.S.; Fim, F.C.; Galland, G.B.

    2010-01-01

    In this work polyaniline nanofibers (PANI-nanofibers) were prepared via interfacial polymerization. The PANI-nanofibers were dispersed in polyethylene (PE) matrix by in situ polymerization of ethylene using Cp 2 ZrCl 2 [bis(cyclopentadienyl) zirconium(IV) dichloride)] and methylaluminoxane as catalytic system. The composites were characterized by infra-red spectroscopy, X-ray diffraction, thermal analysis, transmission electron microscopy and scanning electron microscopy. The results show that nanofibers with average diameters of 200 nm were synthesized and that it was obtained well dispersed PE/PANI nanocomposites. The PANI-nanofibers load did not affect the catalytic activity, but it decreased crystallinity degree of nanocomposites. (author)

  14. Simple patterned nanofiber scaffolds and its enhanced performance in immunoassay.

    Directory of Open Access Journals (Sweden)

    Jing Wang

    Full Text Available Cancer has become the leading cause of death worldwide; early diagnosis and treatment of cancers is critical for the survival of the patients. The concentration of cancer markers in easy-to-access biological fluids can provide great assistance in screening for occult primary cancers, distinguishing malignant from benign findings, determining prognosis and prediction for cancer patients. The multiplex detection technology of a panel of cancer markers can greatly increase the accuracy of disease diagnosis. Herein, we briefly fabricate a high-throughput micro-immunoassay based on the electrospun polystyrene (PS substrates to improve detection sensitivity. The immunoassay was evaluated by analyzing three different cancer biomarkers (AFP, CEA, VEGF. For AFP, CEA, VEGF immunofluorescence assay, the LOD of assay conducted on electrospun PS substrates before or after plasma and the conventional PS substrates were 0.42, 0.10, 1.12 ng/mL, 0.57, 0.09, 1.24 ng/mL, and 159.75, 26.19, 385.59 pg/mL, respectively (P < 0.05. Due to the high porosity and large surface area-to-volume ratio which is the foremost merit of nanostructures, and the plasma treatment which make the hydrophobic PS nanofibers hydropholic, the nanofibers substrates showed sufficient retention of immunoassay functionality and high potential for capture molecules immobilization. Consequently, the immunofluorescence assay conducted on electrospun PS substrates could significantly enhance the sensitivity and limits of detection.

  15. Fabrication of nanofiber mats from electrospinning of functionalized polymers

    Science.gov (United States)

    Oktay, Burcu; Kayaman-Apohan, Nilhan; Erdem-Kuruca, Serap

    2014-08-01

    Electrospinning technique enabled us to prepare nanofibers from synthetic and natural polymers. In this study, it was aimed to fabricate electrospun poly(vinyl alcohol) (PVA) based nanofibers by reactive electrospinning process. To improve endurance of fiber toward to many solvents, PVA was functionalized with photo-crosslinkable groups before spinning. Afterward PVA was crosslinked by UV radiation during electrospinning process. The nanofiber mats were characterized by scanning electron microscopy (SEM). The results showed that homogenous, uniform and crosslinked PVA nanofibers in diameters of about 200 nm were obtained. Thermal stability of the nanofiber mat was investigated with thermal gravimetric analysis (TGA). Also the potential use of this nanofiber mats for tissue engineering was examined. Osteosarcoma (Saos) cells were cultured on the nanofiber mats.

  16. Fabrication of nanofiber mats from electrospinning of functionalized polymers

    International Nuclear Information System (INIS)

    Oktay, Burcu; Kayaman-Apohan, Nilhan; Erdem-Kuruca, Serap

    2014-01-01

    Electrospinning technique enabled us to prepare nanofibers from synthetic and natural polymers. In this study, it was aimed to fabricate electrospun poly(vinyl alcohol) (PVA) based nanofibers by reactive electrospinning process. To improve endurance of fiber toward to many solvents, PVA was functionalized with photo-crosslinkable groups before spinning. Afterward PVA was crosslinked by UV radiation during electrospinning process. The nanofiber mats were characterized by scanning electron microscopy (SEM). The results showed that homogenous, uniform and crosslinked PVA nanofibers in diameters of about 200 nm were obtained. Thermal stability of the nanofiber mat was investigated with thermal gravimetric analysis (TGA). Also the potential use of this nanofiber mats for tissue engineering was examined. Osteosarcoma (Saos) cells were cultured on the nanofiber mats

  17. Nano-Fiber Reinforced Enhancements in Composite Polymer Matrices

    Science.gov (United States)

    Chamis, Christos C.

    2009-01-01

    Nano-fibers are used to reinforce polymer matrices to enhance the matrix dependent properties that are subsequently used in conventional structural composites. A quasi isotropic configuration is used in arranging like nano-fibers through the thickness to ascertain equiaxial enhanced matrix behavior. The nano-fiber volume ratios are used to obtain the enhanced matrix strength properties for 0.01,0.03, and 0.05 nano-fiber volume rates. These enhanced nano-fiber matrices are used with conventional fiber volume ratios of 0.3 and 0.5 to obtain the composite properties. Results show that nano-fiber enhanced matrices of higher than 0.3 nano-fiber volume ratio are degrading the composite properties.

  18. Gas Sensing Properties of Indium Tin Oxide Nanofibers

    Directory of Open Access Journals (Sweden)

    Shiyou Xu

    2009-11-01

    Full Text Available Indium Tin Oxide (ITO nanofibers were fabricated by the electrospinning process. The morphology and crystal structure of ITO nanofibers were studied by SEM, XRD, and TEM respectively. The results showed that polycrystalline ITO nanofibers with an average diameter of 80 nm were obtained. Sensors based on these nanofibers were fabricated by collecting these nanofibers on the integrated sensor platforms. The ITO nanofiber-based sensors showed very fast and high sensor responses at both room and elevated temperatures for NO2. The ratios of resistance in NO2 over that in air were 5 at room temperature and 34 at the optimal working temperature, respectively. The ITO nanofiber-based sensor can be repeatedly used. The details for the fast, enhanced sensor responses and the optimal temperature were discussed.

  19. Bioactive self-assembled peptide nanofibers for corneal stroma regeneration.

    Science.gov (United States)

    Uzunalli, G; Soran, Z; Erkal, T S; Dagdas, Y S; Dinc, E; Hondur, A M; Bilgihan, K; Aydin, B; Guler, M O; Tekinay, A B

    2014-03-01

    Defects in the corneal stroma caused by trauma or diseases such as macular corneal dystrophy and keratoconus can be detrimental for vision. Development of therapeutic methods to enhance corneal regeneration is essential for treatment of these defects. This paper describes a bioactive peptide nanofiber scaffold system for corneal tissue regeneration. These nanofibers are formed by self-assembling peptide amphiphile molecules containing laminin and fibronectin inspired sequences. Human corneal keratocyte cells cultured on laminin-mimetic peptide nanofibers retained their characteristic morphology, and their proliferation was enhanced compared with cells cultured on fibronectin-mimetic nanofibers. When these nanofibers were used for damaged rabbit corneas, laminin-mimetic peptide nanofibers increased keratocyte migration and supported stroma regeneration. These results suggest that laminin-mimetic peptide nanofibers provide a promising injectable, synthetic scaffold system for cornea stroma regeneration. Copyright © 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

  20. Nanoparticles and nanofibers for topical drug delivery

    Science.gov (United States)

    Goyal, Ritu; Macri, Lauren K.; Kaplan, Hilton M.; Kohn, Joachim

    2016-01-01

    This review provides the first comprehensive overview of the use of both nanoparticles and nanofibers for topical drug delivery. Researchers have explored the use of nanotechnology, specifically nanoparticles and nanofibers, as drug delivery systems for topical and transdermal applications. This approach employs increased drug concentration in the carrier, in order to increase drug flux into and through the skin. Both nanoparticles and nanofibers can be used to deliver hydrophobic and hydrophilic drugs and are capable of controlled release for a prolonged period of time. The examples presented provide significant evidence that this area of research has—and will continue to have — a profound impact on both clinical outcomes and the development of new products. PMID:26518723

  1. Chitosan based nanofibers in bone tissue engineering.

    Science.gov (United States)

    Balagangadharan, K; Dhivya, S; Selvamurugan, N

    2017-11-01

    Bone tissue engineering involves biomaterials, cells and regulatory factors to make biosynthetic bone grafts with efficient mineralization for regeneration of fractured or damaged bones. Out of all the techniques available for scaffold preparation, electrospinning is given priority as it can fabricate nanostructures. Also, electrospun nanofibers possess unique properties such as the high surface area to volume ratio, porosity, stability, permeability and morphological similarity to that of extra cellular matrix. Chitosan (CS) has a significant edge over other materials and as a graft material, CS can be used alone or in combination with other materials in the form of nanofibers to provide the structural and biochemical cues for acceleration of bone regeneration. Hence, this review was aimed to provide a detailed study available on CS and its composites prepared as nanofibers, and their associated properties found suitable for bone tissue engineering. Copyright © 2016 Elsevier B.V. All rights reserved.

  2. Multifunctional Nanofibers Comprised of Conducting and Ferroelectric Polymer Composites

    Science.gov (United States)

    2015-08-04

    max scale): Number of graduating undergraduates funded by a DoD funded Center of Excellence grant for Education , Research and Engineering: The...compared to the undergraduate research facilities that we provide at UPRH. We hope that this will further motivate them to seek graduate studies in STEM...and Extrinsic Parameter and their Role in Optical Sensors Calibration, Stephanie Rodriguez 20 2. Effects of Aggressive Environment in the

  3. Graphene oxide decorated electrospun gelatin nanofibers: Fabrication, properties and applications

    Energy Technology Data Exchange (ETDEWEB)

    Jalaja, K. [Department of Chemistry, Indian Institute of Space Science and Technology, Valiamala, Thiruvananthapuram, Kerala 695 547 (India); Sreehari, V.S. [Indian Institute of Science Education and Research Bhopal, Bhauri, Madhya Pradesh 462066 (India); Kumar, P.R. Anil [Tissue culture laboratory, Biomedical Technology Wing, Sree Chitra Tirunal Institute for Medical Sciences and Technology, Poojappura, Thiruvananthapuram, Kerala 695 012 (India); Nirmala, R. James, E-mail: nirmala@iist.ac.in [Department of Chemistry, Indian Institute of Space Science and Technology, Valiamala, Thiruvananthapuram, Kerala 695 547 (India)

    2016-07-01

    Gelatin nanofiber fabricated by electrospinning process is found to mimic the complex structural and functional properties of natural extracellular matrix for tissue regeneration. In order to improve the physico-chemical and biological properties of the nanofibers, graphene oxide is incorporated in the gelatin to form graphene oxide decorated gelatin nanofibers. The current research effort is focussed on the fabrication and evaluation of physico-chemical and biological properties of graphene oxide-gelatin composite nanofibers. The presence of graphene oxide in the nanofibers was established by transmission electron microscopy (TEM). We report the effect of incorporation of graphene oxide on the mechanical, thermal and biological performance of the gelatin nanofibers. The tensile strength of gelatin nanofibers was increased from 8.29 ± 0.53 MPa to 21 ± 2.03 MPa after the incorporation of GO. In order to improve the water resistance of nanofibers, natural based cross-linking agent, namely, dextran aldehyde was employed. The cross-linked composite nanofibers showed further increase in the tensile strength up to 56.4 ± 2.03 MPa. Graphene oxide incorporated gelatin nanofibers are evaluated for bacterial activity against gram positive (Staphylococcus aureus) and gram negative (Escherichia coli) bacteria and cyto compatibility using mouse fibroblast cells (L-929 cells). The results indicate that the graphene oxide incorporated gelatin nanofibers do not prevent bacterial growth, nevertheless support the L-929 cell adhesion and proliferation. - Highlights: • Graphene oxide nano reinforced gelatin nanofibers are fabricated by electrospinning. • Graphene oxide (0.5%) loading resulted in increased tensile strength. • GO/gelatin nanofibers are cross-linked with dextran aldehyde. • Composite nanofibers favoured adhesion of L-929 cells. • GO/gelatin mats do not prevent bacterial growth.

  4. Electrical conductivity retention and electrochemical activity of CSA doped graphene/gold nanoparticle@ polyaniline composites

    Directory of Open Access Journals (Sweden)

    Md. Akherul Islam

    2016-08-01

    Full Text Available This paper reports the synthesis of CTAB mediated CSA doped PANI and GN/GNP@ PANI composite nanofibers. The as synthesized composite nanofibers were examined by TEM, SEM, XRD, Raman spectroscopy; UV–visible diffused reflectance spectroscopy and TGA. The CTAB mediated CSA doped composite nanofibers showed 59% higher DC electrical conductivity at ambient temperature than that of PANI, which might be due to the enhancement in the mobility of the charge carriers and reduction in hopping distance in the composite system. The CTAB mediated CSA doped composite nanofibers compared to PANI was observed to be showing enhanced DC electrical conductivity retention after various cycles of heating, suggesting an enhancement in thermal stability of the composite structure, which could be attributed to the synergistic effect of GN, GNP and PANI. Additionally, the composite nanofibers showed greater electrochemical activity and better capacitive performance and reduced optical bandgap than that of PANI.

  5. Polyamic Acid Nanofibers Produced by Needleless Electrospinning

    Directory of Open Access Journals (Sweden)

    Oldrich Jirsak

    2010-01-01

    Full Text Available The polyimide precursor (polyamic acid produced of 4,4′-oxydiphthalic anhydride and 4,4′-oxydianiline was electrospun using needleless electrospinning method. Nonwoven layers consisting of submicron fibers with diameters in the range about 143–470 nm on the polypropylene spunbond supporting web were produced. Filtration properties of these nanofiber layers on the highly permeable polypropylene support—namely filtration effectivity and pressure drop—were evaluated. Consequently, these polyamic acid fibers were heated to receive polyimide nanofibers. The imidization process has been studied using IR spectroscopy. Some comparisons with the chemically identical polyimide prepared as the film were made.

  6. Polyaniline-coated freestanding porous carbon nanofibers as efficient hybrid electrodes for supercapacitors

    Science.gov (United States)

    Tran, Chau; Singhal, Richa; Lawrence, Daniel; Kalra, Vibha

    2015-10-01

    Three-dimensional, free-standing, hybrid supercapacitor electrodes combining polyaniline (PANI) and porous carbon nanofibers (P-CNFs) were fabricated with the aim to integrate the benefits of both electric double layer capacitors (high power, cyclability) and pseudocapacitors (high energy density). A systematic investigation of three different electropolymerization techniques, namely, potentiodynamic, potentiostatic, and galvanostatic, for electrodeposition of PANI on freestanding carbon nanofiber mats was conducted. It was found that the galvanostatic method, where the current density is kept constant and can be easily controlled facilitates conformal and uniform coating of PANI on three-dimensional carbon nanofiber substrates. The electrochemical tests indicated that the PANI-coated P-CNFs exhibit excellent specific capacitance of 366 F g-1 (vs. 140 F g-1 for uncoated porous carbon nanofibers), 140 F cm-3 volumetric capacitance, and up to 2.3 F cm-2 areal capacitance at 100 mV s-1 scan rate. Such excellent performance is attributed to a thin and conformal coating of PANI achieved using the galvanostatic electrodeposition technique, which not only provides pseudocapacitance with high rate capability, but also retains the double-layer capacitance of the underlying P-CNFs.

  7. Development of electroactive nanofibers based on thermoplastic polyurethane and poly(o-ethoxyaniline) for biological applications.

    Science.gov (United States)

    Cruz, Karina Ferreira Noronha; Formaggio, Daniela Maria Ducatti; Tada, Dayane Batista; Cristovan, Fernando Henrique; Guerrini, Lilia Müller

    2017-02-01

    Electroactive nanofibers based on thermoplastic polyurethane (TPU) and poly(alkoxy anilines) produced by electrospinning has been explored for biomaterials applications. The thermoplastic polyurethane is a biocompatible polymer with good mechanical properties. The production of TPU nanofibers requires the application of high voltage during electrospinning in order to prepare uniform mats due to its weak ability to elongate during the process. To overcome this limitation, a conductive polymer can be incorporated to the process, allowing generates mats without defects. In this study, poly(o-ethoxyaniline) POEA doped with dodecylbenzene sulfonic acid (DBSA) was blended with thermoplastic polyurethane (TPU) by solution method. Films were produced by casting and nanofibers were prepared by electrospinning. The effect of the POEA on morphology, distribution of diameter and cell viability of the nanofibers was evaluated. The results demonstrated that the incorporation of POEA in TPU provided to the mats a suitable morphology for cellular growth. © 2016 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 601-607, 2017. © 2016 Wiley Periodicals, Inc.

  8. Hydrogen storage in graphite nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Park, C.; Tan, C.D.; Hidalgo, R.; Baker, R.T.K.; Rodriguez, N.M. [Northeastern Univ., Boston, MA (United States). Chemistry Dept.

    1998-08-01

    Graphite nanofibers (GNF) are a type of material that is produced by the decomposition of carbon containing gases over metal catalyst particles at temperatures around 600 C. These molecularly engineered structures consist of graphene sheets perfectly arranged in a parallel, perpendicular or at angle orientation with respect to the fiber axis. The most important feature of the material is that only edges are exposed. Such an arrangement imparts the material with unique properties for gas adsorption because the evenly separated layers constitute the most ordered set of nanopores that can accommodate an adsorbate in the most efficient manner. In addition, the non-rigid pore walls can also expand so as to accommodate hydrogen in a multilayer conformation. Of the many varieties of structures that can be produced the authors have discovered that when gram quantities of a selected number of GNF are exposed to hydrogen at pressures of {approximately} 2,000 psi, they are capable of adsorbing and storing up to 40 wt% of hydrogen. It is believed that a strong interaction is established between hydrogen and the delocalized p-electrons present in the graphite layers and therefore a new type of chemistry is occurring within these confined structures.

  9. Functionalized graphene oxide-reinforced electrospun carbon nanofibers as ultrathin supercapacitor electrode

    Institute of Scientific and Technical Information of China (English)

    W.K.Chee; H.N.Lim; Y.Andou; Z.Zainal; A.A.B.Hamra; I.Harrison; M.Altarawneh; Z.T.Jiang; N.M.Huang

    2017-01-01

    Graphene oxide has been used widely as a starting precursor for applications that cater to the needs of tunable graphene. However, the hydrophilic characteristic limits their application, especially in a hydrophobic condition. Herein, a novel non-covalent surface modification approach towards graphene oxide was conducted via a UV-induced photo-polymerization technique that involves two major routes; a UV-sensitive initiator embedded via pi-pi interactions on the graphene planar rings, and the polymerization of hydrophobic polymeric chains along the surface. The functionalized graphene oxide successfully achieved the desired hydrophobicity as it displayed the characteristic of being readily dissolved in organic solvent. Upon its addition into a polymeric solution and subjected to an electrospinning process,non-woven random nanofibers embedded with graphene oxide sheets were obtained. The prepared polymeric nanofibers were subjected to two-step thermal treatments that eventually converted the polymeric chains into a carbon-rich conductive structure. A unique morphology was observed upon the addition of the functionalized graphene oxide, whereby the sheets were embedded and intercalated within the carbon nanofibers and formed a continuous structure. This reinforcement effectively enhanced the electrochemical performance of the carbon nanofibers by recording a specific capacitance of up to 140.10 F/g at the current density of 1 A/g, which was approximately three folds more than that of pristine nanofibers.It also retained the capacitance up to 96.2% after 1000 vigorous charge/discharge cycles. This functionalization technique opens up a new pathway in tuning the solubility nature of graphene oxide towards the synthesis of a graphene oxide-reinforced polymeric structure.

  10. The Cellulose Nanofibers for Optoelectronic Conversion and Energy Storage

    Directory of Open Access Journals (Sweden)

    Yongfeng Luo

    2014-01-01

    Full Text Available Cellulose widely exists in plant tissues. Due to the large pores between the cellulose units, the regular paper is nontransparent that cannot be used in the optoelectronic devices. But some chemical and physical methods such as 2,2,6,6-tetramethylpiperidine-1-oxyl radical (TEMPO oxidation can be used to improve the pores scale between the cellulose units to reach nanometer level. The cellulose nanofibers (CNFs have good mechanical strength, flexibility, thermostability, and low thermal expansion. The paper made of these nanofibers represent a kind of novel nanostructured material with ultrahigh transparency, ultrahigh haze, conductivity, biodegradable, reproducible, low pollution, environment friendly and so on. These advantages make the novel nanostructured paper apply in the optoelectronic device possible, such as electronics energy storage devices. This kind of paper is considered most likely to replace traditional materials like plastics and glass, which is attracting widespread attention, and the related research has also been reported. The purpose of this paper is to review CNFs which are applied in optoelectronic conversion and energy storage.

  11. UV-responsive polyvinyl alcohol nanofibers prepared by electrospinning

    Energy Technology Data Exchange (ETDEWEB)

    Khatri, Zeeshan, E-mail: zeeshan.khatri@faculty.muet.edu.pk [Department of Textile Engineering, Mehran University of Engineering and Technology, Jamshoro 76062 (Pakistan); Nano Fusion Technology Research Lab, Division of Frontier Fibers, Institute for Fiber Engineering (IFES), Interdisciplinary Cluster for Cutting Edge Research (ICCER), Shinshu University, 3-15-1, Tokida, Ueda, Nagano 386-8567 (Japan); Ali, Shamshad [Department of Textile Engineering, Mehran University of Engineering and Technology, Jamshoro 76062 (Pakistan); Department of Organic and Nano Engineering, Hanyang University, 17 Haengdang-dong, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Khatri, Imran [Department of Entomology, Sindh Agriculture University, Tandojam (Pakistan); Mayakrishnan, Gopiraman [Nano Fusion Technology Research Lab, Division of Frontier Fibers, Institute for Fiber Engineering (IFES), Interdisciplinary Cluster for Cutting Edge Research (ICCER), Shinshu University, 3-15-1, Tokida, Ueda, Nagano 386-8567 (Japan); Kim, Seong Hun [Department of Organic and Nano Engineering, Hanyang University, 17 Haengdang-dong, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Kim, Ick-Soo, E-mail: kim@shinshu-u.ac.jp [Nano Fusion Technology Research Lab, Division of Frontier Fibers, Institute for Fiber Engineering (IFES), Interdisciplinary Cluster for Cutting Edge Research (ICCER), Shinshu University, 3-15-1, Tokida, Ueda, Nagano 386-8567 (Japan)

    2015-07-01

    Graphical abstract: - Highlights: • UV responsive PVA nanofibers were prepared via electrospinning. • Quick response codes were recorded multiple times on UV responsive nanofibers. • The rate of photo-coloration was found faster than the rate of photo-reversibility. - Abstract: We report UV-responsive polyvinyl alcohol (PVA) nanofibers for potential application for recording and erasing quick response (QR) codes. We incorporate 1′-3′-dihydro-8-methoxy-1′,3′,3′-trimethyl-6-nitrospiro [2H-1-benzopyran-2,2′-(2H)-indole] (indole) and,3-dihydro-1,3,3-trimethylspiro [2H-indole-2,3′-[3H] phenanthr [9,10-b] (1,4) oxazine] (oxazine) into PVA polymer matrix via electrospinning technique. The resultant nanofibers were measured for recording–erasing, photo-coloration and thermal reversibility. The rate of photo-coloration of PVA–indole nanofibers was five times higher than the PVA–oxazine nanofibers, whereas the thermal reversibility found to be more than twice as fast as PVA–oxazine nanofibers. Results showed that the resultant nanofibers have very good capability of recording QR codes multiple times. The FTIR spectroscopy and SEM were employed to characterize the electrospun nanofibers. The UV-responsive PVA nanofibers have great potentials as a light-driven nanomaterials incorporated within sensors, sensitive displays and in optical devices such as erasable and rewritable optical storage.

  12. UV-responsive polyvinyl alcohol nanofibers prepared by electrospinning

    International Nuclear Information System (INIS)

    Khatri, Zeeshan; Ali, Shamshad; Khatri, Imran; Mayakrishnan, Gopiraman; Kim, Seong Hun; Kim, Ick-Soo

    2015-01-01

    Graphical abstract: - Highlights: • UV responsive PVA nanofibers were prepared via electrospinning. • Quick response codes were recorded multiple times on UV responsive nanofibers. • The rate of photo-coloration was found faster than the rate of photo-reversibility. - Abstract: We report UV-responsive polyvinyl alcohol (PVA) nanofibers for potential application for recording and erasing quick response (QR) codes. We incorporate 1′-3′-dihydro-8-methoxy-1′,3′,3′-trimethyl-6-nitrospiro [2H-1-benzopyran-2,2′-(2H)-indole] (indole) and,3-dihydro-1,3,3-trimethylspiro [2H-indole-2,3′-[3H] phenanthr [9,10-b] (1,4) oxazine] (oxazine) into PVA polymer matrix via electrospinning technique. The resultant nanofibers were measured for recording–erasing, photo-coloration and thermal reversibility. The rate of photo-coloration of PVA–indole nanofibers was five times higher than the PVA–oxazine nanofibers, whereas the thermal reversibility found to be more than twice as fast as PVA–oxazine nanofibers. Results showed that the resultant nanofibers have very good capability of recording QR codes multiple times. The FTIR spectroscopy and SEM were employed to characterize the electrospun nanofibers. The UV-responsive PVA nanofibers have great potentials as a light-driven nanomaterials incorporated within sensors, sensitive displays and in optical devices such as erasable and rewritable optical storage

  13. Production of silk sericin/silk fibroin blend nanofibers

    Directory of Open Access Journals (Sweden)

    Zhang Xianhua

    2011-01-01

    Full Text Available Abstract Silk sericin (SS/silk fibroin (SF blend nanofibers have been produced by electrospinning in a binary SS/SF trifluoroacetic acid (TFA solution system, which was prepared by mixing 20 wt.% SS TFA solution and 10 wt.% SF TFA solution to give different compositions. The diameters of the SS/SF nanofibers ranged from 33 to 837 nm, and they showed a round cross section. The surface of the SS/SF nanofibers was smooth, and the fibers possessed a bead-free structure. The average diameters of the SS/SF (75/25, 50/50, and 25/75 blend nanofibers were much thicker than that of SS and SF nanofibers. The SS/SF (100/0, 75/25, and 50/50 blend nanofibers were easily dissolved in water, while the SS/SF (25/75 and 0/100 blend nanofibers could not be completely dissolved in water. The SS/SF blend nanofibers could not be completely dissolved in methanol. The SS/SF blend nanofibers were characterized by Fourier transform infrared (FTIR spectroscopy, differential scanning calorimetry, and differential thermal analysis. FTIR showed that the SS/SF blend nanofibers possessed a random coil conformation and ß-sheet structure.

  14. A novel electrospun silk fibroin/hydroxyapatite hybrid nanofibers

    International Nuclear Information System (INIS)

    Ming, Jinfa; Zuo, Baoqi

    2012-01-01

    A novel electrospinning of silk fibroin/hydroxyapatite hybrid nanofibers with different composition ratios was performed with methanoic acid as a spinning solvent. The silk fibroin/hydroxyapatite hybrids containing up to 30% hydroxyapatite nanoparticles could be electrospun into the continuous fibrous structure. The electrospun silk fibroin/hydroxyapatite hybrid nanofibers showed bigger diameter and wider diameter distribution than pure silk fibroin nanofibers, and the average diameter gradually increased from 95 to 582 nm. At the same time, the secondary structure of silk fibroin/hydroxyapatite nanofibers was characterized by X-ray diffraction, Fourier transform infrared analysis, and DSC measurement. Comparing with the pure silk fibroin nanofibers, the crystal structure of silk fibroin was mainly amorphous structure in the hybrid nanofibers. X-ray diffraction results demonstrated the hydroxyapatite crystalline nature remained as evidenced from the diffraction planes (002), (211), (300), and (202) of the hydroxyapatite crystallites, which was also confirmed by Fourier transform infrared analysis. The thermal behavior of hybrid nanofibers exhibited the endothermic peak of moisture evaporation ranging from 86 to 113 °C, and the degradation peak at 286 °C appeared. The SF/HAp nanofibers mats containing 30% HAp nanoparticles showed higher breaking tenacity and extension at break for 1.1688 ± 0.0398 MPa and 6.55 ± 1.95%, respectively. Therefore, the electrospun silk fibroin/hydroxyapatite hybrid nanofibers should be provided potentially useful options for the fabrication of biomaterial scaffolds for bone tissue engineering. -- Highlights: ► The novel SF/HAp nanofibers were directly prepared by electrospinning method. ► The nanofiber diameter had significant related to the content of HAp. ► The crystal structure of silk fibroin was mainly amorphous structure in the hybrid nanofibers. ► The HAp crystals existing in the hybrid nanofibers were characterized

  15. Supercapacitors based on flexible graphene/polyaniline nanofiber composite films.

    Science.gov (United States)

    Wu, Qiong; Xu, Yuxi; Yao, Zhiyi; Liu, Anran; Shi, Gaoquan

    2010-04-27

    Composite films of chemically converted graphene (CCG) and polyaniline nanofibers (PANI-NFs) were prepared by vacuum filtration the mixed dispersions of both components. The composite film has a layered structure, and PANI-NFs are sandwiched between CCG layers. Furthermore, it is mechanically stable and has a high flexibility; thus, it can be bent into large angles or be shaped into various desired structures. The conductivity of the composite film containing 44% CCG (5.5 x 10(2) S m(-1)) is about 10 times that of a PANI-NF film. Supercapacitor devices based on this conductive flexible composite film showed large electrochemical capacitance (210 F g(-1)) at a discharge rate of 0.3 A g(-1). They also exhibited greatly improved electrochemical stability and rate performances.

  16. Oxidative stabilization of polyacrylonitrile nanofibers and carbon nanofibers containing graphene oxide (GO: a spectroscopic and electrochemical study

    Directory of Open Access Journals (Sweden)

    İlknur Gergin

    2017-08-01

    Full Text Available In this study, a precursor for carbon nanofibers (CNF was fabricated via electrospinning and carbonized through a thermal process. Before carbonization, oxidative stabilization should be applied, and the oxidation mechanism also plays an important role during carbonization. Thus, the understanding of the oxidation mechanism is an essential part of the production of CNF. The oxidation process of polyacrylonitrile was studied and nanofiber webs containing graphene oxide (GO are obtained to improve the electrochemical properties of CNF. Structural and morphological characterizations of the webs are carried out by using attenuated total reflectance Fourier transform infrared spectroscopy and Raman spectroscopy, scanning electron microscopy, atomic force microscopy and transmission electron microscopy. Mechanical tests are performed with a dynamic mechanical analyzer, and thermal studies are conducted by using thermogravimetric analysis. Electrochemical impedance spectroscopy, and cyclic voltammetry are used to investigate capacitive behavior of the products. The proposed equivalent circuit model was consistent with charge-transfer processes taking place at interior pores filled with electrolyte.

  17. Electrospun nanofibers for energy and environmental applications

    Energy Technology Data Exchange (ETDEWEB)

    Ding, Bin; Yu, Jianyong (eds.) [Donghua Univ., Shanghai (China). State Key Lab. for Modification of Chemical Fibers and Polymer Materials; Donghua Univ., Shanghai (China). Nanomaterials Research Center

    2014-10-01

    This book offers a comprehensive review of the latest advances in developing functional electrospun nanofibers for energy and environmental applications, which include fuel cells, lithium-ion batteries, solar cells, supercapacitors, energy storage materials, sensors, filtration materials, protective clothing, catalysis, structurally-colored fibers, oil spill cleanup, self-cleaning materials, adsorbents, and electromagnetic shielding.

  18. Diamond structures grown from polymer composite nanofibers

    Czech Academy of Sciences Publication Activity Database

    Potocký, Štěpán; Kromka, Alexander; Babchenko, Oleg; Rezek, Bohuslav; Martinová, L.; Pokorný, P.

    2013-01-01

    Roč. 5, č. 6 (2013), s. 519-521 ISSN 2164-6627 R&D Projects: GA ČR GAP108/12/0910; GA ČR GAP205/12/0908 Institutional support: RVO:68378271 Keywords : chemical vapour deposition * composite polymer * nanocrystalline diamond * nanofiber sheet * SEM Subject RIV: BM - Solid Matter Physics ; Magnetism

  19. Carbon nanofibers in catalytic membrane microreactors

    NARCIS (Netherlands)

    Aran, H.C.; Pacheco Benito, Sergio; Luiten-Olieman, Maria W.J.; Er, S.; Wessling, Matthias; Lefferts, Leonardus; Benes, Nieck Edwin; Lammertink, Rob G.H.

    2011-01-01

    In this study, we report on the fabrication and operation of new hybrid membrane microreactors for gas–liquid–solid (G–L–S) reactions. The presented reactors consist of porous stainless steel tubes onto which carbon nanofibers (CNFs) are grown as catalyst support, all encapsulated by a gas permeable

  20. PRODUKSI NANOFIBER DAN APLIKASINYA DALAM PENGOLAHAN AIR

    OpenAIRE

    Krisnandika, Vania Elita

    2017-01-01

    Abstrak Kebutuhan air meningkat seiring meningkatnya jumlah penduduk dan taraf kehidupan masyarakat. Pembangunan yang dilakukan secara terus-menerus dan sangat cepat di Indonesia mengakibatkan penurunan kualitas air permukaan. Teknologi membran merupakan salah satu teknologi pengolahan air yang menghasilkan produk dengan kualitas tinggi. Membran berstruktur nano, khususnya nanofiber, saat ini menjadi perhatian karena menjawab kebutuhan teknologi filtrasi yang efektif dan hemat biaya. Pr...

  1. Fluorescent Self-Assembled Polyphenylene Dendrimer Nanofibers

    NARCIS (Netherlands)

    Liu, Daojun; Feyter, Steven De; Cotlet, Mircea; Wiesler, Uwe-Martin; Weil, Tanja; Herrmann, Andreas; Müllen, Klaus; Schryver, Frans C. De

    2003-01-01

    A second-generation polyphenylene dendrimer 1 self-assembles into nanofibers on various substrates such as HOPG, silicon, glass, and mica from different solvents. The investigation with noncontact atomic force microscopy (NCAFM) and scanning electron microscopy (SEM) shows that the morphology of the

  2. Magnetic and optical properties of electrospun hollow nanofibers of SnO{sub 2} doped with Ce-ion

    Energy Technology Data Exchange (ETDEWEB)

    Mohanapriya, P.; Victor Jaya, N. [Department of Physics, Anna University, Chennai 600 025 (India); Pradeepkumar, R. [Centre for Nanoscience and Technology, Anna University, Chennai 600 025 (India); Natarajan, T. S., E-mail: tsn@physics.iitm.ac.in [Department of Physics, Indian Institute of Technology Madras, Chennai 600 036 (India)

    2014-07-14

    Cerium doped SnO{sub 2} hollow nanofibers were synthesized by electrospinning. High resolution scanning electron microscope (HRSEM) and transmission electron microscopy (TEM) analysis showed hollow nanofibers with diameters around ∼200 nm. The optimized substitution of Ce ion into SnO{sub 2} lattices happened above 6 mol. % doping as confirmed by Powder X-ray diffraction (XRD) studies. Optical band gap was decreased by the doping confirming the direct energy transfer between f-electrons of rare earth ion and the SnO{sub 2} conduction or valence band. The compound also exhibited room temperature ferromagnetism with the saturation magnetization of 19 × 10{sup −5} emu/g at 6 mol. %. This study demonstrates the Ce doped SnO{sub 2} hollow nanofibers for applications in magneto-optoelectronic devices.

  3. Development and characterization of highly oriented PAN nanofiber

    Directory of Open Access Journals (Sweden)

    M. Sadrjahani

    2010-12-01

    Full Text Available A simple and non-conventional electrospinning technique was employed for producing highly oriented Polyacrylonitrile (PAN nanofibers. The PAN nanofibers were electrospun from 14 wt% solution of PAN in dimethylformamid (DMF at 11 kv on a rotating drum with various linear speeds from 22.5 m/min to 67.7 m/min. The influence of take up velocity was investigated on the degree of alignment, internal structure and mechanical properties of collected PAN nanofibers. Using an image processing technique, the best degree of alignment was obtained for those nanofibers collected at a take up velocity of 59.5 m/min. Moreover, Raman spectroscopy was used for measuring molecular orientation of PAN nanofibers. Similarly, a maximum chain orientation parameter of 0.25 was determined for nanofibers collected at a take up velocity of 59.5 m/min.

  4. Preparation and Properties of Flexible AZO@C Nanofibers

    Directory of Open Access Journals (Sweden)

    MA Hui

    2018-01-01

    Full Text Available A new type of environmental-friendly flexible nanofibers of aluminum doped zinc oxide (AZO coated carbon (AZO@C was successfully prepared by using polyvinyl alcohol (PVA as raw materials. The as-spun PVA nanofibers were prepared via electrospinning and its water resistance was greatly improved after heat-treatment. Then, the PVA nanofibers with a layer of zinc aluminum hydroxide on the surface were synthesized by hydrothermal method. Thereafter, new AZO@C composite nanofibers was produced after sintering at 500℃ to the carbonization of PVA nanofibers and the dehydration of zinc aluminum hydroxide to form AZO nanoparticles. The structure and properties of the samples were characterized by Fourier-transform infrared spectrometer (FT-IR, thermal gravimetric analyzer (TGA and scanning electron microscope (SEM. The average diameter of the AZO@C nanofibers is (320±45nm. The photocatalytic property of the resultant composite fibers is demonstrated by degrading methyl orange under solar light.

  5. Nanofiber Nerve Guide for Peripheral Nerve Repair and Regeneration

    Science.gov (United States)

    2016-04-01

    1 Award Number: W81XWH-11-2-0047 TITLE: Nanofiber Nerve Guide for Peripheral Nerve Repair and Regeneration PRINCIPAL INVESTIGATOR: Ahmet Höke...TITLE AND SUBTITLE 5a. CONTRACT NUMBER W81XWH-11-2-0047 Nanofiber nerve guide for peripheral nerve repair and regeneration 5b. GRANT NUMBER...goal of this collaborative research project was to develop next generation engineered nerve guide conduits (NGCs) with aligned nanofibers and

  6. Modeling Temperature Dependent Singlet Exciton Dynamics in Multilayered Organic Nanofibers

    DEFF Research Database (Denmark)

    de Sousa, Leonardo Evaristo; de Oliveira Neto, Pedro Henrique; Kjelstrup-Hansen, Jakob

    2018-01-01

    Organic nanofibers have shown potential for application in optoelectronic devices because of the tunability of their optical properties. These properties are influenced by the electronic structure of the molecules that compose the nanofibers, but also by the behavior of the excitons generated...... dynamics in multilayered organic nanofibers. By simulating absorption and emission spectra, the possible Förster transitions are identified. Then, a Kinetic Monte Carlo (KMC) model is employed in combination with a genetic algorithm to theoretically reproduce time resolved photoluminescence measurements...

  7. Hydrothermal synthesis, characterization, and luminescence of Ca_2B_2O_5:RE (RE = Eu"3"+, Tb"3"+, Dy"3"+) nanofibers

    International Nuclear Information System (INIS)

    Yang, Li; Wan, Yingpeng; Li, Yuze; Pu, Yinfu; Huang, Yanlin; Chen, Cuili; Seo, Hyo Jin

    2016-01-01

    Ca_2B_2O_5:RE (RE = Eu"3"+, Tb"3"+, Dy"3"+) nanofibers were synthesized by the hydrothermal reaction method. The structural refinement was conducted on the base of the X-ray powder diffraction (XRD) measurements. The surface properties of the Ca_2B_2O_5:RE (RE = Eu"3"+, Tb"3"+, Dy"3"+) nanofibers were investigated by the measurements such as the scanning electron microscope (SEM), transmission electron microscope (TEM), and the energy dispersive spectrum (EDS). The nanofiber has a diameter of about 100 nm and a length of several micrometers. The luminescence properties such as photoluminescence excitation (PLE) and emission spectra (PL), decay lifetime, color coordinates, and the absolute internal quantum efficiency (QE) were reported. Ca_2B_2O_5:Eu"3"+ nanofibers show the red luminescence with CIE coordinates of (x = 0.41, y = 0.51) and the luminescence lifetime of 0.63 ms. The luminescence of Ca_2B_2O_5:Tb"3"+ nanofibers is green color (x = 0.29, y = 0.53) with the lifetime of 2.13 ms. However, Dy"3"+-doped Ca_2B_2O_5 nanofibers present a single-phase white-color phosphor with the fluorescence decay of 3.05 ms. Upon near-UV excitation, the absolute quantum efficiency is measured to be 65, 35, and 37 % for Eu"3"+-, Tb"3"+-, Dy"3"+-doped Ca_2B_2O_5 nanofibers, respectively. It is suggested that Ca_2B_2O_5:RE (RE = Eu"3"+, Tb"3"+, Dy"3"+) nanofibers could be an efficient phosphor for lighting and display.

  8. Effects of Sn doping on the morphology, structure, and electrical property of In{sub 2}O{sub 3} nanofiber networks

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Xu; Wang, Yihua [Zhejiang Sci-Tech University, College of Materials and Textiles, Hangzhou (China); Yang, Bin [Zhejiang Sci-Tech University, Ministry of Education, Key Laboratory of Advanced Textile Materials and Manufacturing Technology, College of Materials and Textiles, Hangzhou (China); Zhejiang Sci-Tech University, College of Materials and Textiles, Hangzhou (China)

    2014-11-15

    This paper studies the effect of Sn doping on the morphological, structural, and electrical properties of the Sn-doping In{sub 2}O{sub 3} nanofiber networks. In{sub 2}O{sub 3}-based nanofibers with various relative concentration of Sn precursor (0-20 mol%) were fabricated through the electrospinning method. Scanning electron microscopy observations show that, depending on the relative concentration of SnCl{sub 4} in the starting materials, the doped nanofibers with different morphologies, from smooth to corn-like and then to accidented, are fabricated. Transmission electron microscopy and X-ray diffraction analyses reveal that the Sn dopants influence the growth direction of seeds, resulting in doped nanoparticles having diverse shapes and sizes, which are critical for the formation of doped nanofiber with different morphology. From these nanofiber networks, we fabricated several thin sheets to characterize the effect of Sn concentration on the electrical resistivity. The resistivity of thin sheets decreased significantly before the doping concentration up to 12.5 mol%, and then increased slightly at a larger addition. This work will assist further understanding the formation of Sn-doped In{sub 2}O{sub 3} nanofibers and is expected to be extended to other transparent conductive oxides. (orig.)

  9. Synthesis and Characterization of Stable and Binder-Free Electrodes of TiO2 Nanofibers for Li-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Phontip Tammawat

    2013-01-01

    Full Text Available An electrospinning technique was used to fabricate TiO2 nanofibers for use as binder-free electrodes for lithium-ion batteries. The as-electrospun nanofibers were calcined at 400–1,000°C and characterized using X-ray diffraction (XRD, scanning electron microscopy (SEM, and transmission electron microscopy (TEM. SEM and TEM images showed that the fibers have an average diameter of ~100 nm and are composed of nanocrystallites and grains, which grow in size as the calcination temperature increases. The electrochemical properties of the nanofibers were evaluated using galvanostatic cycling and electrochemical impedance spectroscopy. The TiO2 nanofibers calcined at 400°C showed higher electronic conductivity, higher discharge capacity, and better cycling performance than the nanofibers calcined at 600, 800, and 1,000°C. The TiO2 nanofibers calcined at 400°C delivered an initial reversible capacity of 325 mAh·g−1 approaching their theoretical value at 0.1 C rate and over 175 mAh·g−1 at 0.3 C rate with limited capacity fading and Coulombic efficiency between 96 and 100%.

  10. Carbon nanofibers with highly dispersed tin and tin antimonide nanoparticles: Preparation via electrospinning and application as the anode materials for lithium-ion batteries

    Science.gov (United States)

    Li, Zhi; Zhang, Jiwei; Shu, Jie; Chen, Jianping; Gong, Chunhong; Guo, Jianhui; Yu, Laigui; Zhang, Jingwei

    2018-03-01

    One-dimensional carbon nanofibers with highly dispersed tin (Sn) and tin antimonide (SnSb) nanoparticles are prepared by electrospinning in the presence of antimony-doped tin oxide (denoted as ATO) wet gel as the precursor. The effect of ATO dosage on the microstructure and electrochemical properties of the as-fabricated Sn-SnSb/C composite nanofibers is investigated. Results indicate that ATO wet gel as the precursor can effectively improve the dispersion of Sn nanoparticles in carbon fiber and prevent them from segregation during the electrospinning and subsequent calcination processes. The as-prepared Sn-SnSb/C nanofibers as the anode materials for lithium-ion batteries exhibit high reversible capacity and stable cycle performance. Particularly, the electrode made from Sn-SnSb/C composite nanofibers obtained with 0.9 g of ATO gel has a high specific capacity of 779 mAh·g-1 and 378 mAh·g-1 at the current density of 50 mA·g-1 and 5 A·g-1, respectively, and it exhibits a capacity retention of 97% after 1200 cycles under the current density of 1 A·g-1. This is because the carbon nanofibers can form a continuous conductive network to buffer the volume change of the electrodes while Sn and Sn-SnSb nanoparticles uniformly distributed in the carbon nanofibers are free of segregation, thereby contributing to electrochemical performances of the electrodes.

  11. 2D Ti3C2Tx (MXene)-reinforced polyvinyl alcohol (PVA) nanofibers with enhanced mechanical and electrical properties.

    Science.gov (United States)

    Sobolčiak, Patrik; Ali, Adnan; Hassan, Mohammad K; Helal, Mohamed I; Tanvir, Aisha; Popelka, Anton; Al-Maadeed, Mariam A; Krupa, Igor; Mahmoud, Khaled A

    2017-01-01

    Novel 2D Ti3C2Tx (MXene)-reinforced polyvinyl alcohol (PVA) nanofibers have been successfully fabricated by an electrospinning technique. The high aspect ratio, hydrophilic surfaces, and metallic conductivity of delaminated MXene nanosheet render it promising nanofiller for high performance nanocomposites. Cellulose nanocrystals (CNC) were used to improve the mechanical properties of the nanofibers. The obtained electrospun nanofibers had diameter from 174 to 194 nm depending on ratio between PVA, CNC and MXene. Dynamic mechanical analysis demonstrated an increase in the elastic modulus from 392 MPa for neat PVA fibers to 855 MPa for fibers containing CNC and MXene at 25°C. Moreover, PVA nanofibers containing 0.14 wt. % Ti3C2Tx exhibited dc conductivity of 0.8 mS/cm conductivity which is superior compared to similar composites prepared using methods other than electrospinning. Improved mechanical and electrical characteristics of the Ti3C2Tx /CNC/PVA composites make them viable materials for high performance energy applications.

  12. Formation of inorganic nanofibers by heat-treatment of poly(vinyl alcohol-zirconium compound hybrid nanofibers

    Directory of Open Access Journals (Sweden)

    Nakane K.

    2013-01-01

    Full Text Available Poly(vinyl alcohol-zirconium compound hybrid nanofibers (precursors were formed by electrospinning employing water as a solvent for the spinning solution. The precursors were converted into oxide (ZrO2, carbide (ZrC or nitride (ZrN nanofibers by heating them in air, Ar or N2 atmospheres. Monoclinic ZrO2 nanofibers with high-specific surface area were obtained by heat-treatment of the precursors in air. ZrC and ZrN nanofibers could be obtained below theoretical temperatures calculated from thermodynamics data.

  13. Polyurethane nanofiber strain sensors via in situ polymerization of polypyrrole and application to monitoring joint flexion

    Science.gov (United States)

    Kim, Inhwan; Cho, Gilsoo

    2018-07-01

    Strain sensors made of intrinsically conductive polymers (ICPs) and nanofibers were fabricated and tested for suitability for use in wearable technology. The sensors were fabricated and evaluated based on their surface appearances, and electrical, tensile, and chemical/thermal properties. Polypyrrole (PPy) was in situ polymerized onto polyurethane (PU) nanofiber substrates by exposing pyrrole monomers to ammonium persulfate as oxidant and 2,6-naphthalenedisulfonic acid disodium salt as doping agents in an aqueous bath. The PPy treated PU nanofibers were then coated with polydimethylsiloxane (PDMS). Both pyrrole concentrations and layer numbers were significantly related to change in electrical conductivity. Specimen treated with 0.1 M of PPy and having three layered structure showed the best electrical conductivity. Regarding tensile strength, the in situ polymerization process decreased tensile strength because the oxidant chemically degraded the PU fibers. Adding layers and PDMS treatment generally improved tensile properties while adding layers created fracture parts in the stress–strain curves. The treatment condition of 0.1 M of PPy, two layered, and PDMS treated specimen showed the best tensile properties as a strain sensor. The chemical property evaluation with Fourier transform infrared and x-ray photoelectron spectroscopy tests showed successful PPy polymerization and PDMS treatments. The functional groups and chemical bonds in polyol, urethane linkage, backbone ring structure in PPy, silicon-based functional groups in PDMS, and elemental content changes by treatment at each stage were characterized. The real-time data acquired from the dummy and five human subjects with repetition of motion at three different speeds of 0.16, 0.25 and 0.5 Hz generated similar trends and tendencies. The PU nanofiber sensors based on PPy and PDMS treatments in this study point to the possibility of developing textiles based wearable strain sensors developed using ICPs.

  14. Structure and properties of slow-resorbing nanofibers obtained by (co-axial electrospinning as tissue scaffolds in regenerative medicine

    Directory of Open Access Journals (Sweden)

    Andrzej Hudecki

    2017-12-01

    Full Text Available With the rapid advancement of regenerative medicine technologies, there is an urgent need for the development of new, cell-friendly techniques for obtaining nanofibers—the raw material for an artificial extracellular matrix production. We investigated the structure and properties of PCL10 nanofibers, PCL5/PCL10 core-shell type nanofibers, as well as PCL5/PCLAg nanofibres prepared by electrospinning. For the production of the fiber variants, a 5–10% solution of polycaprolactone (PCL (Mw = 70,000–90,000, dissolved in a mixture of formic acid and acetic acid at a ratio of 70:30 m/m was used. In order to obtain fibers containing PCLAg 1% of silver nanoparticles was added. The electrospin was conducted using the above-described solutions at the electrostatic field. The subsequent bio-analysis shows that synthesis of core-shell nanofibers PCL5/PCL10, and the silver-doped variant nanofiber core shell PCL5/PCLAg, by using organic acids as solvents, is a robust technique. Furthermore, the incorporation of silver nanoparticles into PCL5/PCLAg makes such nanofibers toxic to model microbes without compromising its biocompatibility. Nanofibers obtained such way may then be used in regenerative medicine, for the preparation of extracellular scaffolds: (i for controlled bone regeneration due to the long decay time of the PCL, (ii as bioscaffolds for generation of other types of artificial tissues, (iii and as carriers of nanocapsules for local drug delivery. Furthermore, the used solvents are significantly less toxic than the solvents for polycaprolactone currently commonly used in electrospin, like for example chloroform (CHCl3, methanol (CH3OH, dimethylformamide (C3H7NO or tetrahydrofuran (C4H8O, hence the presented here electrospin technique may allow for the production of multilayer nanofibres more suitable for the use in medical field.

  15. Carbon nanofibers: a versatile catalytic support

    Directory of Open Access Journals (Sweden)

    Nelize Maria de Almeida Coelho

    2008-09-01

    Full Text Available The aim of this article is present an overview of the promising results obtained while using carbon nanofibers based composites as catalyst support for different practical applications: hydrazine decomposition, styrene synthesis, direct oxidation of H2S into elementary sulfur and as fuel-cell electrodes. We have also discussed some prospects of the use of these new materials in total combustion of methane and in ammonia decomposition. The macroscopic carbon nanofibers based composites were prepared by the CVD method (Carbon Vapor Deposition employing a gaseous mixture of hydrogen and ethane. The results showed a high catalytic activity and selectivity in comparison to the traditional catalysts employed in these reactions. The fact was attributed, mainly, to the morphology and the high external surface of the catalyst support.

  16. General strategy for fabricating thoroughly mesoporous nanofibers

    KAUST Repository

    Hou, Huilin

    2014-12-03

    Recently, preparation of mesoporous fibers has attracted extensive attentions because of their unique and broad applications in photocatalysis, optoelectronics, and biomaterials. However, it remains a great challenge to fabricate thoroughly mesoporous nanofibers with high purity and uniformity. Here, we report a general, simple and cost-effective strategy, namely, foaming-assisted electrospinning, for producing mesoporous nanofibers with high purity and enhanced specific surface areas. As a proof of concept, the as-fabricated mesoporous TiO2 fibers exhibit much higher photocatalytic activity and stability than both the conventional solid counterparts and the commercially available P25. The abundant vapors released from the introduced foaming agents are responsible for the creation of pores with uniform spatial distribution in the spun precursor fibers. The present work represents a critically important step in advancing the electrospinning technique for generating mesoporous fibers in a facile and universal manner.

  17. Antibacterial nanofiber materials activated by light

    Czech Academy of Sciences Publication Activity Database

    Jesenská, S.; Plištil, L.; Kubát, Pavel; Lang, Kamil; Brožová, Libuše; Popelka, Štěpán; Szatmáry, Lórant; Mosinger, Jiří

    99A, č. 4 (2011), s. 676-683 ISSN 1549-3296 R&D Projects: GA ČR GAP208/10/1678 Institutional research plan: CEZ:AV0Z40400503; CEZ:AV0Z40320502; CEZ:AV0Z40500505 Keywords : antibacterial nanofiber materials * photoactive * singlet oxygen Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.625, year: 2011

  18. Stress sensitive electricity based on Ag/cellulose nanofiber aerogel for self-reporting.

    Science.gov (United States)

    Yao, Qiufang; Fan, Bitao; Xiong, Ye; Wang, Chao; Wang, Hanwei; Jin, Chunde; Sun, Qingfeng

    2017-07-15

    A self-reporting aerogel toward stress sensitive slectricity (SSE) was presented using an interconnected 3D fibrous network of Ag nanoparticles/cellulose nanofiber aerogel (Ag/CNF), which was prepared via combined routes of silver mirror reaction and ultrasonication. Sphere-like Ag nanoparticles (AgNPs) with mean diameter of 74nm were tightly anchored in the cellulose nanofiber through by the coherent interfaces as the conductive materials. The as-prepared Ag/CNF as a self-reporting material for SSE not only possessed quick response and sensitivity, but also be easily recovered after 100th compressive cycles without plastic deformation or degradation in compressive strength. Consequently, Ag/CNF could play a viable role in self-reporting materials as a quick electric-stress responsive sensor. Copyright © 2017 Elsevier Ltd. All rights reserved.

  19. A study on pore-opening behaviors of graphite nanofibers by a chemical activation process.

    Science.gov (United States)

    Kim, Byung-Joo; Lee, Young-Seak; Park, Soo-Jin

    2007-02-15

    In this work, porous graphite nanofibers (GNFs) were prepared by a KOH activation method in order to manufacture porous carbon nanofibers. The process was conducted in the activation temperature range of 900-1100 degrees C, and the KOH:GNFs ratio was fixed at 3.5:1. The textural properties of the porous carbons were analyzed using N2 adsorption isotherms at 77 K. The BET, D-R, and BJH equations were used to observe the specific surface areas and the micro- and mesopore structures, respectively. From the results, it was found that the textural properties, including the specific surface area and the pore volumes, were proportionally enhanced with increasing activation temperatures. However, the activation mechanisms showed quite significant differences between the samples activated at low and high temperatures.

  20. Facile synthesis of ammonium vanadate nanofibers by using reflux in aqueous V{sub 2}O{sub 5} solution with ammonium persulfate

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Se Hun [Department of Convergence Nanoscience, Hanyang University, 222 Wangsimni-ro, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Koo, Jun Mo [Department of Organic and Nano Engineering, Hanyang University, 222 Wangsimni-ro, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Oh, Seong Geun, E-mail: seongoh@hanyang.ac.kr [Department of Chemical Engineering, Hanyang University, 222 Wangsimni-ro, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Im, Seung Soon, E-mail: imss007@hanyang.ac.kr [Department of Convergence Nanoscience, Hanyang University, 222 Wangsimni-ro, Seongdong-gu, Seoul 133-791 (Korea, Republic of); Department of Organic and Nano Engineering, Hanyang University, 222 Wangsimni-ro, Seongdong-gu, Seoul 133-791 (Korea, Republic of)

    2017-06-15

    Ammonium vanadate nanofibers were synthesized by simple reflux method in aqueous V{sub 2}O{sub 5} solution with ammonium persulfate without relying on surfactants, catalysts, harmful solvents and autoclave. The degree of intercalation by cationic ammonium ions into the crystal structure of vanadium oxide along with its change in chemical composition were analyzed by thermogravimetric analysis (TGA), X-ray photoelectron spectroscopy (XPS), infrared spectroscopy (IR). The morphological changes toward nanofiber structure, having diameter of 20–30 nm and a few μm length, were investigated using transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD). The influences of synthetic conditions, such as reaction time and concentration of sulfate (SO{sub 4}{sup 2-}), on the crystal structures and morphologies of the resulting products have investigated. As a result, the ammonium vanadate nanofiber was formed in a short reaction time through a simple reflux method and yielded comparable electrical conductivity 1.47 × 10{sup -2} S/cm. - Highlights: • Ammonium vanadate nanofiber (AVFr) was prepared by simple reflux method. • AVFr yielded comparable electrical conductivity 1.47 × 10{sup -2} S/cm. • The electrical conductivity was improved by the increased amount of ammonium ion. • Sulfate ions (SO{sub 4}{sup 2-}) play a crucial role in controlling the morphology of nanofiber.

  1. Post-Heat Treatment and Mechanical Assessment of Polyvinyl Alcohol Nanofiber Sheet Fabricated by Electrospinning Technique

    Directory of Open Access Journals (Sweden)

    Mahir Es-saheb

    2014-01-01

    Full Text Available Polyvinyl alcohol (PVA sheets based nanofibers were produced by electrospinning technique. Postheat treatment of the produced PVA sheets with temperatures both below and above Tg to improve the mechanical properties of this material is conducted. The morphology, microstructures, and thermal degradation of the nanofibers sheets produced were investigated using scanning electron microscopy (SEM, transmission electron microscope (TEM, and thermal gravimetric analysis (TGA. Produced nanofibers are compact, and entangled with each other, with diameters from around 150 to 210. Some mechanical characteristics of the successfully produced PVA sheets, and heat-treated, are then conducted and assessed employing uniaxial tensile tests at different speeds ranging from 1 mm/min to 100 mm/min. The tensile test results obtained show that the PVA sheets are strain rate sensitive with increasing strength as the speed (i.e., strain rate increases. The yield tensile stress ranges from 2.411 to 6.981 MPa, the ductility (i.e., elongation percent from ∼21 to 60%, and Young modulus ranges from 103 to 0.137 KPa. However, for heat-treated samples, it is found that the yield strength increases almost by ∼35–40% more than the values of untreated cases with values reaching up to about 3.627–9.63 MPa.

  2. Perspectives: Nanofibers and nanowires for disordered photonics

    Directory of Open Access Journals (Sweden)

    Dario Pisignano

    2017-03-01

    Full Text Available As building blocks of microscopically non-homogeneous materials, semiconductor nanowires and polymer nanofibers are emerging component materials for disordered photonics, with unique properties of light emission and scattering. Effects found in assemblies of nanowires and nanofibers include broadband reflection, significant localization of light, strong and collective multiple scattering, enhanced absorption of incident photons, synergistic effects with plasmonic particles, and random lasing. We highlight recent related discoveries, with a focus on material aspects. The control of spatial correlations in complex assemblies during deposition, the coupling of modes with efficient transmission channels provided by nanofiber waveguides, and the embedment of random architectures into individually coded nanowires will allow the potential of these photonic materials to be fully exploited, unconventional physics to be highlighted, and next-generation optical devices to be achieved. The prospects opened by this technology include enhanced random lasing and mode-locking, multi-directionally guided coupling to sensors and receivers, and low-cost encrypting miniatures for encoders and labels.

  3. Investigation of electrochemical actuation by polyaniline nanofibers

    Science.gov (United States)

    Mehraeen, Shayan; Alkan Gürsel, Selmiye; Papila, Melih; Çakmak Cebeci, Fevzi

    2017-09-01

    Polyaniline nanofibers have shown promising electrical and electrochemical properties which make them prominent candidates in the development of smart systems employing sensors and actuators. Their electrochemical actuation potential is demonstrated in this study. A trilayer composite actuator based on polyaniline nanofibers was designed and fabricated. Cross-linked polyvinyl alcohol was sandwiched between two polyaniline nanofibrous electrodes as ion-containing electrolyte gel. First, electrochemical behavior of a single electrode was studied, showing reversible redox peak pairs in 1 M HCl using a cyclic voltammetry technique. High aspect ratio polyaniline nanofibers create a porous network which facilitates ion diffusion and thus accelerates redox reactions. Bending displacement of the prepared trilayer actuator was then tested and reported under an AC potential stimulation as low as 0.5 V in a variety of frequencies from 50 to 1000 mHz, both inside 1 M HCl solution and in air. Decay of performance of the composite actuator in air is investigated and it is reported that tip displacement in a solution was stable and repeatable for 1000 s in all selected frequencies.

  4. Chitosan nanofibers for transbuccal insulin delivery.

    Science.gov (United States)

    Lancina, Michael G; Shankar, Roopa Kanakatti; Yang, Hu

    2017-05-01

    In this work, they aimed at producing chitosan based nanofiber mats capable of delivering insulin via the buccal mucosa. Chitosan was electrospun into nanofibers using poly(ethylene oxide) (PEO) as a carrier molecule in various feed ratios. The mechanical properties and degradation kinetics of the fibers were measured. Insulin release rates were determined in vitro using an ELISA assay. The bioactivity of released insulin was measured in terms of Akt activation in pre-adipocytes. Insulin permeation across the buccal mucosa was measured in an ex-vivo porcine transbuccal model. Fiber morphology, mechanical properties, and in vitro stability were dependent on PEO feed ratio. Lower PEO content blends produced smaller diameter fibers with significantly faster insulin release kinetics. Insulin showed no reduction in bioactivity due to electrospinning. Buccal permeation of insulin facilitated by high chitosan content blends was significantly higher than that of free insulin. Taken together, the work demonstrates that chitosan-based nanofibers have the potential to serve as a transbuccal insulin delivery vehicle. © 2017 Wiley Periodicals, Inc. J Biomed Mater Res Part A: 105A: 1252-1259, 2017. © 2017 Wiley Periodicals, Inc.

  5. Fabrication of NiO/zirconium oxide nanofibers by electrospinning

    Energy Technology Data Exchange (ETDEWEB)

    Sundarrajan, Subramanian, E-mail: sundarnus1@gmail.com [Department of Mechanical Engineering, NUS, 117576 (Singapore); Venkatesan, Arunachalam; Agarwal, Satya R.; Shaik Anwar Ahamed, Nabeela Nasreen [Department of Mechanical Engineering, NUS, 117576 (Singapore); Ramakrishna, Seeram, E-mail: seeram@nus.edu.sg [Department of Mechanical Engineering, NUS, 117576 (Singapore); King Saud University, Riyadh 11451 (Saudi Arabia); Institute of Materials Research and Engineering, 117602 (Singapore)

    2014-12-01

    The electrospinning technique has been used to fabricate 1D inorganic–organic composite nanofibers from solutions containing poly(vinyl alcohol) (PVA) and suitable aqueous precursors of nickel and zirconium ions. Upon calcination, nickel oxide/zirconia nanofibers retained the original morphological features of as-spun nanofibers. X-ray diffraction was used to identify the crystalline nature of the final product and analytical tools such as Fourier transform infrared (FTIR) spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and atomic force microscopy (AFM) were employed to elucidate the pathway of ceramic phase formation and the systematic evolution of morphological features in the as-spun and calcined fibers. These fibers will find potential applications in biomedical field. - Highlights: • PVA/NiO/zirconia composite nanofibers were synthesized via electrospinning. • Green processing of nanofibers using only water as solvent. • Calcination of composite nanofibers to yield ceramic nanofibers. • High aspect ratio nanofibers with diameters 106 ± 25 nm • The application of these fibers as dental composites and bone tissue engineering.

  6. Local field enhanced second-harmonic response of organic nanofibers

    DEFF Research Database (Denmark)

    Leißner, Till; Kostiučenko, Oksana; Fiutowski, Jacek

    Organic CNHP4 nanofibers showing a strong second-harmonic (SH) response have been successfully implemented as active components in a metal-organic hybrid system. Using nondestructive roll-on transfer technique nanofibers were transferred from the growing mica substrates onto electron...

  7. Fabrication of Cationic Exchange Polystyrene Nanofibers for Drug ...

    African Journals Online (AJOL)

    Purpose: To prepare polystyrene nanofiber ion exchangers (PSNIE) with surface cation exchange functionality using a new method based on electrospinning and also to optimize crosslinking and sulfonation reactions to obtain PSNIE with maximum ion exchange capacity (IEC). Method: The nanofibers were prepared from ...

  8. High performance co-polyimide nanofiber reinforced composites

    NARCIS (Netherlands)

    Yao, Jian; Li, Guang; Bastiaansen, Cees; Peijs, Ton

    2015-01-01

    Electrospun co-polyimide BPDA (3, 3′, 4, 4′-Biphenyltetracarboxylic dianhydride)/PDA (p-Phenylenediamine)/ODA (4, 4′-oxydianiline) nanofiber reinforced flexible composites were manufactured by impregnating these high performance nanofibers with styrene-butadiene-styrene (SBS) triblock copolymer

  9. Fabrication and characterization of nanofiber-nanoparticle-composites with phase change materials by electrospinning

    International Nuclear Information System (INIS)

    Babapoor, Aziz; Karimi, Gholamreza; Khorram, Mohammad

    2016-01-01

    Highlights: • Form-stable nanofibers with phase change material are produced by electrospinning. • PA6 and PEG are used as the supporting matrix and phase change material. • Various nanoparticles are used to enhance thermal properties of the fibers. • The nanofiber-nanoparticle composites exhibited desirable thermal stability. • Al 2 O 3 nanoparticles improved thermal conductivity of the composites considerably. - Graphical Abstract: Display Omitted - Abstract: Thermal energy storage has been recognized as one of the most important technologies for the utilization of renewable energy sources and conserving energy. In this investigation, through combination of polyethylene glycol (PEG) as a phase change material (PCM), polyamid6 (PA6) and various nanoparticles (SiO 2 , Al 2 O 3 , Fe 2 O 3 and ZnO) as supporting materials, novel form-stable PCMs-based composites were fabricated by single nozzle electrospinning. The structure, morphology and thermal properties of the prepared nanofiber-nanocomposite-enhanced phase change materials (NEPCMs) were characterized by Fourier transform infrared spectroscopy, scanning electron microscopy and differential scanning calorimeter, respectively. Based on the results, nanocomposites-nanofibers were successfully fabricated with high thermal stability and reliability. It is observed that in all composites, the fiber diameter is decreased by increasing the nanoparticles loading. The lowest average diameter obtained was for Fe 2 O 3 composite. Al 2 O 3 composite showed the maximum thermal conductivity enhancement. This study suggests that the fabricated nanocomposite-PCMs offer proper phase transition temperature range and high heat enthalpy values and hence, have potential for thermal energy storage applications.

  10. Electrochromic device based on electrospun WO{sub 3} nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Dulgerbaki, Cigdem; Maslakci, Neslihan Nohut; Komur, Ali Ihsan; Oksuz, Aysegul Uygun, E-mail: ayseguluygun@sdu.edu.tr

    2015-12-15

    Highlights: • WO{sub 3} electrochromic nanofibers were prepared by electrospinning technique. • WO{sub 3} nanofibers switched reversibly from transparent to blue color. • Electrochromic device was assembled using ionic liquid based gel electrolyte. • Significant optical modulation and excellent cycling stability were achieved for ECD. - Abstract: The tungsten oxide (WO{sub 3}) nanofibers were grown directly onto an ITO-coated glass via an electrospinning method for electrochromic applications. The electrochromic properties of WO{sub 3} nanofibers were investigated in the presence of different electrolytes including a series of ionic liquids and classic LiClO{sub 4}-PC system. A significant optical modulation of 20.82% at 760 nm, reversible coloration with efficiency of 64.58 cm{sup 2}/C and excellent cycling stability were achieved for the nanofiber electrochromic device (ECD) with ionic liquid based gel electrolyte.

  11. Electrospun nanofibers: New generation materials for advanced applications

    Energy Technology Data Exchange (ETDEWEB)

    Thenmozhi, S. [Inorganic & Nanomaterials Research Laboratory, Department of Chemistry, Bharathiar University, Coimbatore 641 046 (India); DRDO-BU CLS, Bharathiar University Campus, Coimbatore 641 046 (India); Dharmaraj, N., E-mail: dharmaraj@buc.edu.in [Inorganic & Nanomaterials Research Laboratory, Department of Chemistry, Bharathiar University, Coimbatore 641 046 (India); Kadirvelu, K. [DRDO-BU CLS, Bharathiar University Campus, Coimbatore 641 046 (India); Kim, Hak Yong [Department of Textile Engineering, Chonbuk National University, Chonju 561-756 (Korea, Republic of)

    2017-03-15

    Highlights: • A review covering important aspects of electrospinning technique is presented. • Applications of nanofibers in various fields are reviewed. • Possibility to up-scale electrospinning technique to industry also included. - Abstract: Electrospinning (E-spin) is a unique technique to fabricate polymeric as well as metal oxide nanofibers. Research on electrospun nanofibers is a very active field in material science owing to their novel applications in diverse domains. The main focus of this review is to provide an insight into E-spin technique by understanding the working principle, influencing parameters and applications of nanofibers in different walks of life. Several hundreds of papers are published on the preparation, modification and applications of nanofibers produced by E-spin technique in the areas like sensor development, decontamination, energy storage, biomedical and catalysis etc. Details on the industrial scale development of E-spin technique, current scenario and future developments are also covered in this review.

  12. Fluorescent and Colorimetric Electrospun Nanofibers for Heavy-Metal Sensing

    Directory of Open Access Journals (Sweden)

    Idelma A. A. Terra

    2017-12-01

    Full Text Available The accumulation of heavy metals in the human body and/or in the environment can be highly deleterious for mankind, and currently, considerable efforts have been made to develop reliable and sensitive techniques for their detection. Among the detection methods, chemical sensors appear as a promising technology, with emphasis on systems employing optically active nanofibers. Such nanofibers can be obtained by the electrospinning technique, and further functionalized with optically active chromophores such as dyes, conjugated polymers, carbon-based nanomaterials and nanoparticles, in order to produce fluorescent and colorimetric nanofibers. In this review we survey recent investigations reporting the use of optically active electrospun nanofibers in sensors aiming at the specific detection of heavy metals using colorimetry and fluorescence methods. The examples given in this review article provide sufficient evidence of the potential of optically electrospun nanofibers as a valid approach to fabricate highly selective and sensitive optical sensors for fast and low-cost detection of heavy metals.

  13. Recognition of lysozyme using surface imprinted bacterial cellulose nanofibers.

    Science.gov (United States)

    Saylan, Yeşeren; Tamahkar, Emel; Denizli, Adil

    2017-11-01

    Here, we developed the lysozyme imprinted bacterial cellulose (Lyz-MIP/BC) nanofibers via the surface imprinting strategy that was designed to recognize lysozyme. This study includes the molecular imprinting method onto the surface of bacterial cellulose nanofibers in the presence of lysozyme by metal ion coordination, as well as further characterizations methods FTIR, SEM and contact angle measurements. The maximum lysozyme adsorption capacity of Lyz-MIP/BC nanofibers was found to be 71 mg/g. The Lyz-MIP/BC nanofibers showed high selectivity for lysozyme towards bovine serum albumin and cytochrome c. Overall, the Lyz-MIP/BC nanofibers hold great potential for lysozyme recognition due to the high binding capacity, significant selectivity and excellent reusability.

  14. Biologically Active Polycaprolactone/Titanium Hybrid Electrospun Nanofibers for Hard Tissue Engineering

    DEFF Research Database (Denmark)

    Barakat, Nasser A. M.; Sheikh, Faheem A.; Al-Deyab, Salem S.

    2011-01-01

    In this study, a novel strategy to improve the bioactivity of polycaprolactone nanofibers is proposed. Incorporation of pure titanium nanoparticles into polycaprolactone nanofibers strongly enhances the precipitation of bone-like apatite materials when the doped nanofibers are soaked in a simulat...... nanofiber mats and the successful incorporation of the titanium nanoparticles make the prepared polycaprolactone nanofiber mat a proper candidate for the hard-tissue engineering applications....

  15. Bioactive thermoresponsive polyblend nanofiber formulations for wound healing

    Energy Technology Data Exchange (ETDEWEB)

    Pawar, Mahesh D. [Polymer Science and Engineering, National Chemical Laboratory, Homi Bhabha Road, Pashan, Pune 411008 (India); MAEER' s Maharashtra Institute of Pharmacy S. No. 124, MIT Campus Paud Road, Kothrud, Pune 411 038 (India); Rathna, G.V.N., E-mail: rv.gundloori@ncl.res.in [Polymer Science and Engineering, National Chemical Laboratory, Homi Bhabha Road, Pashan, Pune 411008 (India); Agrawal, Shubhang [Polymer Science and Engineering, National Chemical Laboratory, Homi Bhabha Road, Pashan, Pune 411008 (India); Kuchekar, Bhanudas S. [MAEER' s Maharashtra Institute of Pharmacy S. No. 124, MIT Campus Paud Road, Kothrud, Pune 411 038 (India)

    2015-03-01

    The rationale of this work is to develop new bioactive thermoresponsive polyblend nanofiber formulations for wound healing (topical). Various polymer compositions of thermoresponsive, poly(N-isopropylacrylamide), egg albumen and poly(ε-caprolactone) blend solutions with and without a drug [gatifloxacin hydrochloride, Gati] were prepared. Non-woven nanofibers of various compositions were fabricated using an electrospinning technique. The morphology of the nanofibers was analyzed by an environmental scanning electron microscope. The morphology was influenced by the concentration of polymer, drug, and polymer blend composition. Fourier transform infrared spectroscopy analysis showed the shift in bands due to hydrogen ion interactions between polymers and drug. Thermogram of PNIPAM/PCL/EA with Gati recorded a shift in lower critical solution temperature (LCST) and glass transition temperature (T{sub g}) of PNIPAM. Similarly T{sub g} and melting temperature (T{sub m}) of PCL were shifted. X-ray diffraction patterns recorded a decrease in the crystalline state of PCL nanofibers and transformed crystalline drug to an amorphous state. In vitro release study of nanofibers with Gati showed initial rapid release up to 10 h, followed by slow and controlled release for 696 h (29 days). Nanofiber mats with Gati exhibited antibacterial properties to Staphylococcus aureus, supported suitable controlled drug release with in vitro cell viability and in vivo wound healing. - Highlights: • Thermoresponsive and bioactive nanofiber blends of PNIPAM/EA/PCL were fabricated. • Nanofiber blends favored initial rapid release, followed by controlled release. • In vitro cell viability of pure polymers and nanofiber blends was least toxic. • In vivo studies of drug loaded nanofiber mats recorded faster tissue regeneration.

  16. Evaluation of protein adsorption onto a polyurethane nanofiber surface having different segment distributions

    Energy Technology Data Exchange (ETDEWEB)

    Morita, Yuko; Koizumi, Gaku [Frontier Fiber Technology and Science, Graduate School of Engineering, University of Fukui (Japan); Sakamoto, Hiroaki, E-mail: hi-saka@u-fukui.ac.jp [Tenure-Track Program for Innovative Research, University of Fukui (Japan); Suye, Shin-ichiro [Frontier Fiber Technology and Science, Graduate School of Engineering, University of Fukui (Japan)

    2017-02-01

    Electrospinning is well known to be an effective method for fabricating polymeric nanofibers with a diameter of several hundred nanometers. Recently, the molecular-level orientation within nanofibers has attracted particular attention. Previously, we used atomic force microscopy to visualize the phase separation between soft and hard segments of a polyurethane (PU) nanofiber surface prepared by electrospinning. The unstretched PU nanofibers exhibited irregularly distributed hard segments, whereas hard segments of stretched nanofibers prepared with a high-speed collector exhibited periodic structures along the long-axis direction. PU was originally used to inhibit protein adsorption, but because the surface segment distribution was changed in the stretched nanofiber, here, we hypothesized that the protein adsorption property on the stretched nanofiber might be affected. We investigated protein adsorption onto PU nanofibers to elucidate the effects of segment distribution on the surface properties of PU nanofibers. The amount of adsorbed protein on stretched PU nanofibers was increased compared with that of unstretched nanofibers. These results indicate that the hard segment alignment on stretched PU nanofibers mediated protein adsorption. It is therefore expected that the amount of protein adsorption can be controlled by rotation of the collector. - Highlights: • The hard segments of stretched PU nanofibers exhibit periodic structures. • The adsorbed protein on stretched PU nanofibers was increased compared with PU film. • The hard segment alignment on stretched PU nanofibers mediated protein adsorption.

  17. Process Optimization and Emperical Modelling for Electrospun Polyacrylonitrile (PAN) Nanofiber Precursor of Carbon nanofibers

    NARCIS (Netherlands)

    Gu, S.Y.; Gu, S.; Ren, J.; Vancso, Gyula J.

    2005-01-01

    Ultrafine fibers were spun from polyacrylonitrile (PAN)/N,N-dimethyl formamide (DMF) solution as a precursor of carbon nanofibers using a homemade electrospinning set-up. Fibers with diameter ranging from 200 nm to 1200 nm were obtained. Morphology of fibers and distribution of fiber diameter were

  18. Starch/PCL composite nanofibers by co-axial electrospinning technique for biomedical applications.

    Science.gov (United States)

    Komur, B; Bayrak, F; Ekren, N; Eroglu, M S; Oktar, F N; Sinirlioglu, Z A; Yucel, S; Guler, O; Gunduz, O

    2017-03-29

    In this study, starch and polycaprolactone (PCL), composite nanofibers were fabricated by co-axial needle electrospinning technique. Processing parameters such as polymer concentration, flow rate and voltage had a marked influence on the composite fiber diameter. Fourier transform infrared spectroscopy, scanning electron microscopy (SEM), mechanical and physical properties (such as density, viscosity and electrical conductivity) of the composite fibres were evaluated. Moreover, a cell culture test was performed in order to determine their cytotoxicity for wound dressing application. The effect of starch ratio in the solution on the properties and morphological structure of the fibers produced was presented. With lower starch concentration values, the fibers have greater ultimate tensile strength characteristic (mostly 4 and 5 wt%). According to SEM results, it can be figured out that the nanofibers fabricated have good spinnability and morphology. The mean diameter of the fibers is about 150 nm. According to results of cell culture study, the finding can be determined that the increase of starch in the fiber also increases the cell viability. Composite nanofibers of starch/PCL have been prepared using a co-axial needle electrospinning technique. PCL was successfully encapsulated within starch. Fiber formation was observed for different ratio of starch. With several test, analysis and measurement performed, some important parameters such as quality and effectuality of each fiber obtained for wound dressing applications were discussed in detail.

  19. Clearly Transparent Nanopaper from Highly Concentrated Cellulose Nanofiber Dispersion Using Dilution and Sonication

    Directory of Open Access Journals (Sweden)

    Takaaki Kasuga

    2018-02-01

    Full Text Available Nanopaper prepared from holocellulose pulp is one of the best substrates for flexible electronics because of its high thermal resistance and high clear transparency. However, the clearness of nanopaper decreases with increasing concentration of the starting cellulose nanofiber dispersion—with the use of a 2.2 wt % dispersion, for example—resulting in translucent nanopaper with a high haze of 44%. To overcome this problem, we show that the dilution of this high-concentration dispersion with water followed by sonication for 10 s reduces the haze to less than 10% while maintaining the high thermal resistance of the nanopaper. Furthermore, the combination of water dilution and a short sonication treatment improves the clearness of the nanopaper, which would translate into cost savings for the transportation and storage of this highly concentrated cellulose nanofiber dispersion. Finally, we demonstrate the improvement of the electrical conductivity of clear transparent nanopaper prepared from an initially high-concentration dispersion by dropping and heating silver nanowire ink on the nanopaper. These achievements will pave the way toward the realization of the mass production of nanofiber-based flexible devices.

  20. Pretreatment assisted synthesis and characterization of cellulose nanocrystals and cellulose nanofibers from absorbent cotton.

    Science.gov (United States)

    Abu-Danso, Emmanuel; Srivastava, Varsha; Sillanpää, Mika; Bhatnagar, Amit

    2017-09-01

    In this work, cellulose nanocrystals (CNCs) and cellulose nanofibers (CNFs) were synthesized from absorbent cotton. Two pretreatments viz. dewaxing and bleaching with mild alkali were applied to the precursor (cotton). Acid hydrolysis was conducted with H 2 SO 4 and dissolution of cotton was achieved with a mixture of NaOH-thiourea-urea-H 2 O at -3°C. Synthesized cellulose samples were characterized using FTIR, XRD, SEM, BET, and zeta potential. It seems that synthesis conditions contributed to negative surface charge on cellulose samples and CNCs had the higher negative surface charge compared to CNFs. Furthermore, BET surface area, pore volume and pore diameter of CNCs were found to be higher as compared to CNFs. The dewaxed cellulose nanofibers (CNF D) had a slightly higher BET surface area (0.47m 2 /g) and bigger pore diameter (59.87Å) from attenuated contraction compared to waxed cellulose nanofibers (CNFW) (0.38m 2 /g and 44.89Å). The XRD of CNCs revealed a semi-crystalline structure and the dissolution agents influenced the crystallinity of CNFs. SEM images showed the porous nature of CNFs, the flaky nature and the nano-sized width of CNCs. Synthesized CNF D showed a better potential as an adsorbent with an average lead removal efficiency of 91.49% from aqueous solution. Copyright © 2017 Elsevier B.V. All rights reserved.

  1. Plasma Modification of Poly Lactic Acid Solutions to Generate High Quality Electrospun PLA Nanofibers.

    Science.gov (United States)

    Rezaei, Fatemeh; Nikiforov, Anton; Morent, Rino; De Geyter, Nathalie

    2018-02-02

    Physical properties of pre-electrospinning polymer solutions play a key role in electrospinning as they strongly determine the morphology of the obtained electrospun nanofibers. In this work, an atmospheric-pressure argon plasma directly submerged in the liquid-phase was used to modify the physical properties of poly lactic acid (PLA) spinning solutions in an effort to improve their electrospinnability. The electrical characteristics of the plasma were investigated by two methods; V-I waveforms and Q-V Lissajous plots while the optical emission characteristics of the plasma were also determined using optical emission spectroscopy (OES). To perform a complete physical characterization of the plasma-modified polymer solutions, measurements of viscosity, surface tension, and electrical conductivity were performed for various PLA concentrations, plasma exposure times, gas flow rates, and applied voltages. Moreover, a fast intensified charge-couple device (ICCD) camera was used to image the bubble dynamics during the plasma treatments. In addition, morphological changes of PLA nanofibers generated from plasma-treated PLA solutions were observed by scanning electron microscopy (SEM). The performed plasma treatments were found to induce significant changes to the main physical properties of the PLA solutions, leading to an enhancement of electrospinnability and an improvement of PLA nanofiber formation.

  2. Coating of Silk Fabric Using PVA/Ciprofloxacin Hcl Nanofibers for Biomedical Applications

    Directory of Open Access Journals (Sweden)

    Somaye Baghersad

    2016-05-01

    Full Text Available In recent years, fabrication of polymeric antibacterial wound dressing has gained most attention in controlling wound infections. Silk is also a member of the broad family of protein-based polmers. The silk produced by the lepidopteran insect Bombyx mori is a highly accepted material due to its long history as a very valuable textile fiber. Recently, additional applications have been developed for silk, mainly in the field of biotechnology. Regarding its importance in wound healing, silk fabric was incorporated with ciprofloxacin, as an antibiotic, on its surface coated with electro-spun PVA/ciprofloxacin nanofibers. Before coating, degumming was carried out using autoclave technique and properties of the silk fabric, before and after degumming process, was investigated by SEM, FTIR, mechanical properties and moisture absorbance measurement. The results of all analyses showed a reduction in fibers diameter, mechanical strength and moisture absorption after degumming process. Electrospinning condition was optimized and diameter of the nanofibers, with and without drug, was measured before coating. The results showed that addition of the drug increased electrical conductivity of electrospinning solution and resulted in finer nanofibers. Antibacterial test was performed using "disk diffusion method" with Escherichia coli (EC and Staphylococcus aureus (SA bacteria to compare the antibacterial properties of degummed and non-degummed silk fabrics alone and coated with nanofibers. Measurement of bacterial inhibition zone diameter showed no antibacterial activity for degummed and non-degummed silk fabrics alone. However, the sample coated with PVA/ciprofloxacin showed antibacterial activity. The antibacterial property for SA in both cases was the same, but for EC, the antibacterial activity of degummed silk fabric was more than that of non-degummed material.

  3. Enhanced Electrochemical Performance of Electrospun Ag/Hollow Glassy Carbon Nanofibers as Free-standing Li-ion Battery Anode

    International Nuclear Information System (INIS)

    Shilpa; Sharma, Ashutosh

    2015-01-01

    Silver with a high theoretical capacity for lithium storage is an attractive alloy based anode for Li-ion batteries, but large volume changes associated with AgLi x alloy formation leads to electrode cracking, pulverization and rapid capacity fading. A buffer matrix, like the electrospun hollow carbon nanofibers, can reduce this problem to a great extent. Herein, we demonstrate the facile synthesis of a free-standing, binder free Ag-C hybrid electrode through co-axial electrospinning, where well dispersed Ag nanoparticles are embedded in hollow carbon nanofibers. Using this approach, the long cycle life of carbon is complemented with the high lithium storage capacity of Ag, resulting in a high performance anode. The Ag-C composite electrode delivers a capacity of 739 mAh g −1 (>conventional graphite anodes) at 50 mA g −1 , with ∼85% capacity retention after 100 cycles. In addition, the Ag-C composite nanofibers are highly porous and exhibit a large accessible surface area (∼726.9 m 2 g −1 ) with an average pore diameter of ∼6.07 nm. The encapsulation of Ag in the hollow interiors not only provides additional lithium storage sites but also enhances the electronic conductivity, which combined with the reduced lithium diffusion path lengths in the nanofibers result in faster charge-discharge kinetics and hence a high rate performance

  4. Synthesis and Property of Ag(NP)/catechin/Gelatin Nanofiber

    Science.gov (United States)

    Nasir, Muhamad; Apriani, Dita

    2017-12-01

    Nanomaterial play important role future industry such as for the medical, food, pharmaceutical and cosmetic industry. Ag (NP) and catechin exhibit antibacterial property. Ag(NP) with diameter around 15 nm was synthesis by microwaved method. We have successfully produce Ag(NP)/catechin/gelatin nanofiber composite by electrospinning process. Ag(NP)/catechin/gelatin nanofiber was synthesized by using gelatin from tuna fish, polyethylene oxide (PEO), acetic acid as solvent and silver nanoparticle(NP)/catechin as bioactive component, respectively. Morphology and structure of bioactive catechin-gelatin nanofiber were characterized by scanning electron microscopy (SEM) and fourier transform infrared spectroscopy (FTIR), respectively. SEM analysis showed that morphology of nanofiber composite was smooth and had average diameter 398.97 nm. FTIR analysis results were used to confirm structure of catechin-gelatin nanofiber. It was confirmed by FTIR that specific vibration band peak amide A (N-H) at 3286,209 cm-1, amide B (N-H) 3069,396 cm-1, amide I (C=O) at 1643,813 cm-1, amide II (N-H and CN) at 1538,949 cm-1, amide III (C-N) at 1276,789 cm-1, C-O-C from polyethylene oxide at 1146,418 cm-1, respectively. When examined to S. Aureus bacteria, Ag/catechin/gelatin nanofiber show inhabitation performance around 40.44%. Ag(NP)/catechin/gelatin nanofiber has potential application antibacterial medical application.

  5. Preparation and Electrochemical Properties of Silver Doped Hollow Carbon Nanofibers

    Directory of Open Access Journals (Sweden)

    LI Fu

    2016-11-01

    Full Text Available Silver doped PAN-based hollow carbon nanofibers were prepared combining co-electrospinning with in situ reduction technique subsequently heat treatment to improve the electrochemical performances of carbon based supercapacitor electrodes. The morphology, structure and electrochemical performances of the resulted nanofiber were studied. The results show that the silver nanoparticles can be doped on the surface of hollow carbon nanofibers and the addition of silver favors the improvement of the electrochemical performances, exhibiting the enhanced reversibility of electrode reaction and the capacitance and the reduced charge transfer impedance.

  6. Solution-blown nanofiber mats from fish sarcoplasmic protein

    DEFF Research Database (Denmark)

    Sett, S.; Boutrup Stephansen, Karen; Yarin, A.L.

    2016-01-01

    In the present work, solution-blowing was adopted to form nanofibers from fish sarcoplasmic proteins (FSPs). Nanofiber mats containing different weight ratios (up to 90/10) of FSP in the FSP/nylon 6 blended nanofibers were formed from formic acid solutions, and compared to electrospun fibers made...... that the production rate of solution-blowing was increased 30-fold in relation to electrospinning. Overall, this study reveals FSP as an interesting biopolymeric alternative to synthetic polymers, and the introduction of FSP to nylon 6 provides a composite with controlled properties....

  7. Growth and Integration of Organic Nanofibers in Devices

    DEFF Research Database (Denmark)

    Thilsing-Hansen, Kasper

    kæder af krystalliter, der tilslutter sig den allerede eksisterende P6P nanofiber. Overførsel af P6P nanofibre fra deres vækst substrat er uundgåeligt for at implementere p6P nanofibre i komponenter. Kontrolleret overførsel af 200x200μm2 nanofiber områder fra vækst substratet til præfabrikerede silicium......) exciteret med en pulserende laserstråle et guld/vakuum interface, hvilket resulterer i nanofiber lokaliseret mønstre i PEEM billederne....

  8. Wiping frictional properties of electrospun hydrophobic/hydrophilic polyurethane nanofiber-webs on soda-lime glass and silicon-wafer.

    Science.gov (United States)

    Watanabe, Kei; Wei, Kai; Nakashima, Ryu; Kim, Ick Soo; Enomoto, Yuji

    2013-04-01

    In the present work, we conducted the frictional tests of hydrophobic and hydrophilic polyurethane (PUo and PUi) nanofiber webs against engineering materials; soda-lime glass and silicon wafer. PUi/glass combination, with highest hydrophilicity, showed the highest friction coefficient which decrease with the increase of the applied load. Furthermore, the effects of fluorine coating are also investigated. The friction coefficient of fluorine coated hydrophobic PU nanofiber (PUof) shows great decrease against the silicon wafer. Finally, wiping ability and friction property are investigated when the substrate surface is contaminated. Nano-particle dusts are effectively collected into the pores by wiping with PUo and PUi nanofiber webs both on glass and silicon wafer. The friction coefficient gradually increased with the increase of the applied load.

  9. Preparation of nitrogen-doped biomass-derived carbon nanofibers/graphene aerogel as a binder-free electrode for high performance supercapacitors

    Science.gov (United States)

    Zhang, Yimei; Wang, Fei; Zhu, Hao; Zhou, Lincheng; Zheng, Xinliang; Li, Xinghua; Chen, Zhuang; Wang, Yue; Zhang, Dandan; Pan, Duo

    2017-12-01

    Carbon materials derived from various biomasses have aroused forceful interest from scientific community based on their abundant resource, low cost, environment friendly and easy fabrication. Herein, the method has been developed to prepare nitrogen-doped biomass-derived carbon nanofibers/graphene aerogel (NCGA) as the binder-free electrode for supercapacitors. Ethylenediamine (EDA) is select as nitrogen source for its high nitrogen content and strong interaction with graphene oxide (GO) and cellulose nanofibers (CNFs) via hydrothermal self-assembly method to form hybrid hydrogel, and finally converts to NCGA by freeze-drying and carbonization. After carbonization the insulated CNFs converted to high conductivity carbon nanofibers. The NCGA electrode exhibits a high specific capacitance of 289 F g-1 at 5 mV s-1 and high stability of 90.5% capacitance retention ratio after 5000 cycles at 3 A g-1. This novel biomass electrode could be potential candidate for high performance supercapacitors.

  10. Waveguiding properties of individual electrospun polymer nanofibers

    Science.gov (United States)

    Ishii, Yuya; Kaminose, Ryohei; Fukuda, Mitsuo

    2013-09-01

    Optical circuits are needed to achieve high-speed, high-capacity information processing. An optical waveguide is an essential element in optical circuits. Electrospun polymer fibers have diameters in the nanometer range and high aspect ratios, so they are prime candidates for small waveguides. In this work, we fabricate uniform electrospun polymer nanofibers and characterize their optical waveguiding properties. Poly(methyl methacrylate) (PMMA) solutions of different concentration that contain a small amount of Nile Blue A perchlorate (NBA) are electrospun. Uniform PMMA/NBA nanofibers are obtained from the 10 wt% solution. The fibers are covered with transparent cladding and their ends cut vertically. A laser beam with a wavelength of 533 nm is irradiated onto the fiber from the direction vertical to the fiber axis so that it scans along the fiber. Photoluminescence (PL) at the end face of individual fibers is then measured. The PL intensity decreases with increasing distance (d) between the end face of a fiber and irradiating point of the laser beam as ~exp(-αd) with a loss coefficient (α). Measurements of five individual fibers reveal α is in the range of 17-75 cm-1.

  11. Biosynthesis of highly porous bacterial cellulose nanofibers

    Science.gov (United States)

    Hosseini, Hadi; Kokabi, Mehrdad; Mousavi, Seyyed Mohammad

    2018-01-01

    Bacterial cellulose nanofibers (BCNFs) as a sustainable and biodegradable polymer has drawn tremendous research attention in tissue engineering, bacterial sensors and drug delivery due to its extraordinary properties such as high purity, high crystallinity, high water absorption capacity and excellent mechanical strength in the wet state. This awesome properties, is attributed to BCNFs structure, therefore its characterization is important. In this work, the bacterial strain, Gluconacetobacter xylinus (PTCC 1734, obtained from Iranian Research Organization for Science and Technology (IROST)), was used to produce BCNFs hydrogel using bacterial fermentation under static condition at 29 °C for 10 days in the incubator. Then, the biosynthesized BCNFs wet gel, were dried at ambient temperature and pressure and characterized using Brunauer-Emmett-Teller (BET) and Field emission scanning electron microscopy (FE-SEM) analysis. FESEM image displayed highly interconnected and porous structure composed of web-like continuous, nanofibers with an average diameter of 48.5±2.1 nm. BET result analysis depicted BCNFs dried at ambient conditions had IV isotherm type, according to the IUPAC classification, indicating that BCNFs dried at ambient condition is essentially mesoporous. On the other hand, BET results depicted, mesoporous structure is around 85%. In addition, Specific surface area (SBET) obtained 81.45 m2/g. These results are in accordance with the FESEM observation.

  12. Regeneration of Bombyx mori silk nanofibers and nanocomposite fibrils by the electrospinning process

    Science.gov (United States)

    Ayutsede, Jonathan Eyitouyo

    In recent years, there has been significant interest in the utilization of natural materials for novel nanoproducts such as tissue engineered scaffolds. Silkworm silk fibers represent one of the strongest natural fibers known. Silkworm silk, a protein-based natural biopolymer, has received renewed interest in recent years due to its unique properties (strength, toughness) and potential applications such as smart textiles, protective clothing and tissue engineering. The traditional 10--20 mum diameter, triangular-shaped Bombyx mori fibers have remained unchanged over the years. However, in our study, we examine the scientific implication and potential applications of reducing the diameter to the nanoscale, changing the triangular shape of the fiber and adding nanofillers in the form of single wall carbon nanotubes (SWNT) by the electrospinning process. The electrospinning process preserves the natural conformation of the silk (random and beta-sheet). The feasibility of changing the properties of the electrospun nanofibers by post processing treatments (annealing and chemical treatment) was investigated. B. mori silk fibroin solution (formic acid) was successfully electrospun to produce uniform nanofibers (as small as 12 nm). Response Surface Methodology (RSM) was applied for the first time to experimental results of electrospinning, to develop a processing window that can reproduce regenerated silk nanofibers of a predictable size (d silk multifunctional nanocomposite fibers were fabricated for the first time with anticipated properties (mechanical, thermal and electrically conductive) that may have scientific applications (nerve regeneration, stimulation of cell-scaffold interaction). In order to realize these applications, the following areas need to be addressed: a systematic investigation of the dispersion of the nanotubes in the silk matrix, a determination of new methodologies for characterizing the nanofiber properties and establishing the nature of the silk

  13. Electrospinning of poly(vinyl alcohol) nanofibers loaded with hexadecane nanodroplets.

    Science.gov (United States)

    Arecchi, A; Mannino, S; Weiss, J

    2010-08-01

    The feasibility of producing poly(vinyl alcohol) (PVA) nanofibers containing fine-disperse hexadecane droplets by electrospinning a blend of hexadecane-in-water emulsions and PVA was investigated. Hexadecane oil-in-water nanoemulsions (d(10)= 181.2 +/- 0.1 nm) were mixed with PVA at pH 4.5 to yield polymer-emulsion blends containing 0.5 to 1.5 wt% oil droplets and 8-wt% PVA. The solution properties of emulsions and emulsion-PVA blends (viscosity, conductivity, surface tension) were determined. Solutions were electrospun and the morphology and thermal properties of deposited fiber mats characterized by scanning electron microscopy and differential scanning calorimetry. Fiber mats were dissolved in buffer to liberate incorporated hexadecane droplets and the buffer solutions analyzed by optical microscopy, UV-spectroscopy, and light scattering. Analysis of dry fiber mats and their solutions showed that emulsion droplets were indeed part of the electrospun fiber structures. Depending on the concentration of hexadecane in the initial emulsion-polymer blends, droplets were dispersed in the fibers as individual droplets or in form of aggregated flocs of hexadecane droplets. Nanofibers with spindle-like perturbations or nanofibers containing bead-like structures with approximately 5 times larger than the size of droplets in the original nanoemulsion were obtained. Remarkably, incorporation of hexadecane droplets in fibers did not alter size of individual droplets, that is, no coalescence occurred. The manufacture of solid matrix containing nanodroplets could be of substantial interest for manufacturers wishing to develop encapsulation system for lipophilic functional compounds such as lipid-soluble flavors, antimicrobials, antioxidants, and bioactives with tailored release kinetics. Practical Applications: The paper describes the formation of electrospun nanofibers from hydrophilic polymers that contain fine-disperse emulsion droplets. By incorporating emulsion droplets, a

  14. Hybrid electrospun chitosan-phospholipids nanofibers for transdermal drug delivery

    DEFF Research Database (Denmark)

    Mendes, Ana Carina Loureiro; Gorzelanny, Christian; Halter, Natalia

    2016-01-01

    Chitosan (Ch) polysaccharide was mixed with phospholipids (P) to generate electrospun hybrid nanofibers intended to be used as platforms for transdermal drug delivery. Ch/P nanofibers exibithed average diameters ranging from 248 +/- 94 nm to 600 +/- 201 nm, depending on the amount of phospholipids...... used. Fourier Transformed Infra-Red (FTIR) spectroscopy and Dynamic Light Scattering (DLS) data suggested the occurrence of electrostatic interactions between amine groups of chitosan with the phospholipid counterparts. The nanofibers were shown to be stable for at least 7 days in Phosphate Buffer...... culture plate (control). The release of curcumin, diclofenac and vitamin B12, as model drugs, from Ch/P hybrid nanofibers was investigated, demonstrating their potential utilization as a transdermal drug delivery system....

  15. Improved fire retardancy of thermoset composites modified with carbon nanofibers

    International Nuclear Information System (INIS)

    Zhao Zhongfu; Gou Jan

    2009-01-01

    Multifunctional thermoset composites were made from polyester resin, glass fiber mats and carbon nanofiber sheets (CNS). Their flaming behavior was investigated with cone calorimeter under well-controlled combustion conditions. The heat release rate was lowered by pre-planting carbon nanofiber sheets on the sample surface with the total fiber content of only 0.38 wt.%. Electron microscopy showed that carbon nanofiber sheet was partly burned and charred materials were formed on the combusting surface. Both the nanofibers and charred materials acted as an excellent insulator and/or mass transport barrier, improving the fire retardancy of the composite. This behavior agrees well with the general mechanism of fire retardancy in various nanoparticle-thermoplastic composites.

  16. Method of synthesizing silica nanofibers using sound waves

    Science.gov (United States)

    Sharma, Jaswinder K.; Datskos, Panos G.

    2015-09-15

    A method for synthesizing silica nanofibers using sound waves is provided. The method includes providing a solution of polyvinyl pyrrolidone, adding sodium citrate and ammonium hydroxide to form a first mixture, adding a silica-based compound to the solution to form a second mixture, and sonicating the second mixture to synthesize a plurality of silica nanofibers having an average cross-sectional diameter of less than 70 nm and having a length on the order of at least several hundred microns. The method can be performed without heating or electrospinning, and instead includes less energy intensive strategies that can be scaled up to an industrial scale. The resulting nanofibers can achieve a decreased mean diameter over conventional fibers. The decreased diameter generally increases the tensile strength of the silica nanofibers, as defects and contaminations decrease with the decreasing diameter.

  17. Interfacial Polymerization of Polyaniline Nanofibers Grafted to Au Surfaces

    National Research Council Canada - National Science Library

    Sawall, D

    2004-01-01

    .... The in-situ polymerization technique of these PANI nanofibers in the presence of sulfonated polystyrene allowed for the growth of PANI 2-D nanostructures embedded in the polymerized sulfonated host...

  18. Multicolored Nanofiber Based Organic Light-Emitting Transistor

    DEFF Research Database (Denmark)

    With Jensen, Per Baunegaard; Kjelstrup-Hansen, Jakob; Tavares, Luciana

    For optoelectronic applications, organic semiconductors have several advantages over their inorganic counterparts such as facile synthesis, tunability via synthetic chemistry, and low temperature processing. Self-assembled, molecular crystalline nanofibers are of particular interest as they could...... form ultra-small light-emitters in future nanophotonic applications. Such organic nanofibers exhibit many interesting optical properties including polarized photo- and electroluminescence, waveguiding, and emission color tunability. We here present a first step towards a multicolored, electrically...... driven device by combining nanofibers made from two different molecules, parahexaphenylene (p6P) and 5,5´-Di-4-biphenyl-2,2´-bithiophene (PPTTPP), which emits blue and green light, respectively. The organic nanofibers are implemented on a bottom gate/bottom contact field-effect transistor platform using...

  19. A modified microemulsion method for fabrication of hydrogel Tragacanth nanofibers.

    Science.gov (United States)

    Ghayempour, Soraya; Montazer, Majid

    2018-04-09

    Tragacanth is a nontoxic, biodegradable and biocompatible polymer applied as a nanostructure form in various fields such as biomedicine and food industry. Here, hydrogel Tragacanth nanofibers were fabricated using a modified microemulsion method. The effective parameters on the fabrication of nanofibers such as emulsifier type, stirrer type, processing time and concentrations of emulsifier, Tragacanth and aluminum chloride were studied and the conditions were optimized for high quality nanofibers. SEM images indicated Tragacanth nanofiberswere successfully synthesized with average diameter of 50 nm and uniformdistribution. Appear a peak at 1110 cm -1 related to Al-C bonds and reduce intensity ofthe peaks at 1742 and 1629 cm -1 and in FT-IR spectrum of nanofibersprove the successfully synthesis. Further, the hydrogel properties of the synthesized nanofibers can be proved by the swelling of 142% and drying time of 3 h. Copyright © 2018 Elsevier B.V. All rights reserved.

  20. A review on electrospun nanofibers for oral drug delivery

    Directory of Open Access Journals (Sweden)

    Abbas Akhgari

    2017-10-01

    Full Text Available Nowadays, polymer nanofibers have gained attention due to remarkable characteristics such as high porosity and large surface area to volume ratio. Among their fabrication methods, electrospinning technique has been attracted as a simple and reproducible approach. It is a versatile, simple and cost-effective technique for the production of continuous nanofibers with acceptable characteristics such as high porosity, high surface area to volume ratio, high loading capacity and encapsulation efficiency, delivery of multiple drugs, and enhancement of drug solubility. Due to these properties electrospun nanofibers have been extensively used for different biomedical applications including wound dressing, tissue engineering, enzyme immobilization, artificial organs, and drug delivery. Different synthetic and natural polymers have been successfully electrospun into ultrafine fibers. Using electrospun nanofibers as vehicles for oral drug delivery has been investigated in different release manners- fast, biphasic or sustained release. This article presents a review on application of electrospinning technique in oral drug delivery.

  1. High temperature resistant nanofiber by bubbfil-spinning

    Directory of Open Access Journals (Sweden)

    Li Ya

    2015-01-01

    Full Text Available Heat-resisting nanofibers have many potential applications in various industries, and the bubbfil spinning is the best candidate for mass-production of such materials. Polyether sulfone/zirconia solution with a bi-solvent system is used in the experiment. Experimental result reveals that polyether sulfone/zirconia nanofibers have higher resistance to high temperature than pure polyether sulfone fibers, and can be used as high-temperature-resistant filtration materials.

  2. A review on electrospun nanofibers for oral drug delivery

    OpenAIRE

    Abbas Akhgari; Zahra Shakib; Setareh Sanati

    2017-01-01

    Nowadays, polymer nanofibers have gained attention due to remarkable characteristics such as high porosity and large surface area to volume ratio. Among their fabrication methods, electrospinning technique has been attracted as a simple and reproducible approach. It is a versatile, simple and cost-effective technique for the production of continuous nanofibers with acceptable characteristics such as high porosity, high surface area to volume ratio, high loading capacity and encapsulation effi...

  3. Polyurethane Nanofiber Membranes for Waste Water Treatment by Membrane Distillation

    OpenAIRE

    Jiříček, T.; Komárek, M.; Lederer, T.

    2017-01-01

    Self-sustained electrospun polyurethane nanofiber membranes were manufactured and tested on a direct-contact membrane distillation unit in an effort to find the optimum membrane thickness to maximize flux rate and minimize heat losses across the membrane. Also salt retention and flux at high salinities up to 100 g kg−1 were evaluated. Even though the complex structure of nanofiber layers has extreme specific surface and porosity, membrane performance was surprisingly predictable; the highest ...

  4. Improvement of air permeability of Bubbfil nanofiber membrane

    Directory of Open Access Journals (Sweden)

    Wang Fei-Yan

    2018-01-01

    Full Text Available Nanofiber membranes always have extremely high filter efficiency and remarkably low pressure drop. In order to further improve air permeability of bubbfil nanofiber membranes, the plasma technology is used for surface treatment in this paper. The results show that plasma treatment can improve air permeability by 4.45%. Under higher power plasma treatment, earthworm like etchings are produced on the membrane surface with fractal dimensions of about 1.138.

  5. Carbon nanofiber/polyethylene nanocomposite: Processing behavior, microstructure and electrical properties

    International Nuclear Information System (INIS)

    Al-Saleh, Mohammed H.; Gelves, Genaro A.; Sundararaj, Uttandaraman

    2013-01-01

    Highlights: • Electrically conductive CNF/HDPE nanocomposite were prepared by melt compounding. • The effect of processing on the nanocomposites macro and micro structures was analyzed. • 1.4 vol% CNF were required to construct a conductive network within the HDPE matrix. • An EMI SE of 42 dB was reported for 15 vol% CNF/HDPE nanocomposite. • An empirical model was developed to estimate the EMI SE. - Abstract: Electrically conductive polymer nanocomposite of high density polyethylene (HDPE) filled with carbon nanofibers (CNFs) were prepared by melt compounding in a batch mixer. The nanocomposite processing behavior was studied by monitoring the mixing torque vs. time as function of filler content. Scanning electron microscopy and optical microscopy were used to investigate the nanocomposite dispersion of nanofiller and the adhesion between the nanofiller and polymer matrix. The electrical and electromagnetic interference (EMI) shielding behaviors of the nanocomposite were reported as function of nanofibers concentration, and an empirical correlation related the EMI SE to the nanocomposite’s electrical resistivity was developed. Good level of CNF dispersion was evident despite the poor adhesion exhibited between the nanofibers and the HDPE matrix. At 1.5 vol% CNF loading, the nanocomposite exhibited an electrical volume resistivity of 10 5 Ω·cm. EMI shielding effectiveness was found to increase with increase in nanofiller concentration. In the 0.1–1.5 GHz frequency range, 2 mm thick plate made of 5 vol% CNF/HDPE nanocomposite exhibits an EMI shielding effectiveness of 20 dB

  6. Antibacterial polylactic acid/chitosan nanofibers decorated with bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Goh, Yi-fan; Akram, Muhammad; Alshemary, Ammarz [Department of Chemistry, Faculty of Science, Universiti Teknologi Malaysia, 81310 Johor Bahru, Johor (Malaysia); Hussain, Rafaqat, E-mail: rafaqat@comsats.edu.pk [Department of Physics, COMSATS Institute of Information Technology, Islamabad (Pakistan)

    2016-11-30

    Highlights: • PLA/Chitosan nanofibers were coated with functional bioglass. • Polymer/ceramic composite fibers exhibited good in-vitro bioactivity. • Nanofibers coated with Ag doped bioglass exhibited good antibacterial activity. - Abstract: In this study, we have presented the structural and in vitro characterization of electrospun polylactic acid (PLA)/Chitosan nanofibers coated with cerium, copper or silver doped bioactive glasses (CeBG/CuBG/AgBG). Bead-free, smooth surfaced nanofibers were successfully prepared by using electrospinning technique. The nanocomposite fibers were obtained using a facile dip-coating method, their antibacterial activities against E. coliE. coli (ATCC 25922 strains) were measured by the disk diffusion method after 24 h of incubation at 37 °C. CeBG and CuBG decorated PLA/Chitosan nanofibers did not develop an inhibition zone against the bacteria. On the other hand, nanofibers coated with AgBG developed an inhibition zone against the bacteria. The as-prepared nanocomposite fibers were immersed in SBF for 1, 3 and 7 days in Simulated Body Fluid (SBF) for evaluation of in vitro bioactivity. All samples induced the formation of crystallites with roughly ruffled morphology and the pores of fibers were covered with the extensive growth of crystallites. Energy Dispersive X-ray (EDX) composition analysis showed that the crystallites possessed Ca/P ratio close to 1.67, confirming the good in-vitro bioactivity of the fibers.

  7. Cellulose nanofiber extraction from grass by a modified kitchen blender

    Science.gov (United States)

    Nakagaito, Antonio Norio; Ikenaga, Koh; Takagi, Hitoshi

    2015-03-01

    Cellulose nanofibers have been used to reinforce polymers, delivering composites with strength that in some cases can be superior to that of engineering plastics. The extraction of nanofibers from plant fibers can be achieved through specialized equipment that demands high energy input, despite delivering extremely low yields. The high extraction cost confines the use of cellulose nanofibers to the laboratory and not for industrial applications. This study aims to extract nanofibers from grass by using a kitchen blender. Earlier studies have demonstrated that paper sheets made of blender-extracted nanofibers (after 5 min to 10 min of blending) have strengths on par with paper sheets made from commercially available cellulose nanofibers. By optimizing the design of the blender bottle, nanofibrillation can be achieved in shorter treatment times, reducing the energy consumption (in the present case, to half) and the overall extraction cost. The raw materials used can be extended to the residue straw of agricultural crops, as an alternative to the usual pulp fibers obtained from wood.

  8. Temperature-responsive PLLA/PNIPAM nanofibers for switchable release

    Energy Technology Data Exchange (ETDEWEB)

    Elashnikov, Roman; Slepička, Petr [Department of Solid State Engineering, University of Chemistry and Technology, Prague 166 28 (Czech Republic); Rimpelova, Silvie; Ulbrich, Pavel [Department of Biochemistry and Microbiology, University of Chemistry and Technology, 16628 Prague (Czech Republic); Švorčík, Vaclav [Department of Solid State Engineering, University of Chemistry and Technology, Prague 166 28 (Czech Republic); Lyutakov, Oleksiy, E-mail: lyutakoo@vscht.cz [Department of Solid State Engineering, University of Chemistry and Technology, Prague 166 28 (Czech Republic)

    2017-03-01

    Smart antimicrobial materials with on-demand drug release are highly desired for biomedical applications. Herein, we report about temperature-responsive poly(N-isopropylacrylamide) (PNIPAM) nanospheres doped with crystal violet (CV) and incorporated into the poly-L-lactide (PLLA) nanofibers. The nanofibers were prepared by electrospinning, using different initial polymers ratios. The morphology of the nanofibers and polymers distribution in the nanofibers were characterized by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The interaction between PNIPAM and PLLA in the nanofibers was studied by Fourier transform infrared spectroscopy (FTIR) and its effect on the PNIPAM phase transition was also investigated. It was shown that by the changing of the environmental temperature across the lower critical solution temperature (LCST) of PNIPAM, the switchable wettability and controlled CV release can be achieved. The temperature-dependent release kinetics of CV from polymer nanofibers was investigated by ultraviolet-visible spectroscopy (UV–Vis). The temperature-responsive release of antibacterial CV was also tested for triggering of antibacterial activity, which was examined on Staphylococcus epidermidis (S. epidermidis) and Escherichia coli (E. coli). Thus, the proposed material is promising value for controllable drug-release.

  9. ECM Decorated Electrospun Nanofiber for Improving Bone Tissue Regeneration

    Directory of Open Access Journals (Sweden)

    Yong Fu

    2018-03-01

    Full Text Available Optimization of nanofiber surface properties can lead to enhanced tissue regeneration outcomes in the context of bone tissue engineering. Herein, we developed a facile strategy to decorate elctrospun nanofibers using extracellular matrix (ECM in order to improve their performance for bone tissue engineering. Electrospun PLLA nanofibers (PLLA NF were seeded with MC3T3-E1 cells and allowed to grow for two weeks in order to harvest a layer of ECM on nanofiber surface. After decellularization, we found that ECM was successfully preserved on nanofiber surface while maintaining the nanostructure of electrospun fibers. ECM decorated on PLLA NF is biologically active, as evidenced by its ability to enhance mouse bone marrow stromal cells (mBMSCs adhesion, support cell proliferation and promote early stage osteogenic differentiation of mBMSCs. Compared to PLLA NF without ECM, mBMSCs grown on ECM/PLLA NF exhibited a healthier morphology, faster proliferation profile, and more robust osteogenic differentiation. Therefore, our study suggests that ECM decoration on electrospun nanofibers could serve as an efficient approach to improving their performance for bone tissue engineering.

  10. Synthesis of Keratin-based Nanofiber for Biomedical Engineering.

    Science.gov (United States)

    Thompson, Zanshe S; Rijal, Nava P; Jarvis, David; Edwards, Angela; Bhattarai, Narayan

    2016-02-07

    Electrospinning, due to its versatility and potential for applications in various fields, is being frequently used to fabricate nanofibers. Production of these porous nanofibers is of great interest due to their unique physiochemical properties. Here we elaborate on the fabrication of keratin containing poly (ε-caprolactone) (PCL) nanofibers (i.e., PCL/keratin composite fiber). Water soluble keratin was first extracted from human hair and mixed with PCL in different ratios. The blended solution of PCL/keratin was transformed into nanofibrous membranes using a laboratory designed electrospinning set up. Fiber morphology and mechanical properties of the obtained nanofiber were observed and measured using scanning electron microscopy and tensile tester. Furthermore, degradability and chemical properties of the nanofiber were studied by FTIR. SEM images showed uniform surface morphology for PCL/keratin fibers of different compositions. These PCL/keratin fibers also showed excellent mechanical properties such as Young's modulus and failure point. Fibroblast cells were able to attach and proliferate thus proving good cell viability. Based on the characteristics discussed above, we can strongly argue that the blended nanofibers of natural and synthetic polymers can represent an excellent development of composite materials that can be used for different biomedical applications.

  11. Preparation of Diethylenetriamine Modified Polyacrylonitrile Nanofibers for Cadmium Ion Adsorption

    Directory of Open Access Journals (Sweden)

    Zahra Mokhtari- shorijeh

    2016-07-01

    Full Text Available In this study, the electrospinning method was used to manufacture polyacrylonitrile (PAN nanofibers. The procedure involved spinning a solution of 10%wt PAN in dimethyl formamide (DMF in an electric field of 21 kV and with a tip to collector distance of 16 cm. The nanofibers thus obtained had an average diameter of 100 nm. Then, scanning electron microscopy (SEM images were used to investigate the morphology of the nanofibers. In the next step, the nanofiner surface was modified with diethylenetriamine and FTIR was employed to ensure the presence of amines on the nanofiber surface. The functionalized nanofibers were then used for the first time to adsorb ions of cadmium (a heavy metal with industrial applications and its adsorption capacity was evaluated. The chemical charactristics of the nanofibers and the effects of such parameters as pH, temprature, and contact time on adsorption efficiency were investigated. The results showed that maximum adsorption efficiency was achieved within the first 10 minutes of the process at a pH in the range of 5‒7 when about 80% of the cadmium ions were adsorbed.. Moreover, only slight changes were observed with longer contact times or with increasing temperature. Finally, the adsorption data fitted well with the Langmuir isotherm

  12. Effect of thermal interface on heat flow in carbon nanofiber composites.

    Science.gov (United States)

    Gardea, F; Naraghi, M; Lagoudas, D

    2014-01-22

    The thermal transport process in carbon nanofiber (CNF)/epoxy composites is addressed through combined micromechanics and finite element modeling, guided by experiments. The heat exchange between CNF constituents and matrix is studied by explicitly accounting for interface thermal resistance between the CNFs and the epoxy matrix. The effects of nanofiber orientation and discontinuity on heat flow and thermal conductivity of nanocomposites are investigated through simulation of the laser flash experiment technique and Fourier's model of heat conduction. Our results indicate that when continuous CNFs are misoriented with respect to the average temperature gradient, the presence of interfacial resistance does not affect the thermal conductivity of the nanocomposites, as most of the heat flow will be through CNFs; however, interface thermal resistance can significantly alter the patterns of heat flow within the nanocomposite. It was found that very high interface resistance leads to heat entrapment at the interface near to the heat source, which can promote interface thermal degradation. The magnitude of heat entrapment, quantified via the peak transient temperature rise at the interface, in the case of high thermal resistance interfaces becomes an order of magnitude more intense as compared to the case of low thermal resistance interfaces. Moreover, high interface thermal resistance in the case of discontinuous fibers leads to a nearly complete thermal isolation of the fibers from the matrix, which will marginalize the contribution of the CNF thermal conductivity to the heat transfer in the composite.

  13. Polycaprolactone-templated reduced-graphene oxide liquid crystal nanofibers towards biomedical applications

    DEFF Research Database (Denmark)

    Jalili-Firoozinezhad, Sasan; Hasan Mohamadzadeh Moghadam, Mohamad; Ghanian, Mohammad Hossein

    2017-01-01

    Here, we report a facile method to generate electrically conductive nanofibers by coating and subsequently chemically reducing graphene oxide (GO) liquid crystals on a polycaprolactone (PCL) mat. Ultra large GO sheets obtained are in favor of charge carrier mobility and oriented morphology...... of the GO coating. We showed that coating the reduced GO (rGO) not only retains the three-dimensional topography, fiber orientation and size of the template PCL, but also makes it electroconductive. Our preliminary in vitro assessments using mesenchymal stem cells revealed no induced cytotoxicity yet...... increased cellular metabolism on PCL-templated rGO fibers....

  14. Nanofiber-based filters as novel barrier systems for nanomaterial exposure scenarios

    Energy Technology Data Exchange (ETDEWEB)

    Faccini, M; Amantia, D; Vazquez-Campos, S; Aubouy, L [LEITAT Technological Center, Passeig 22 de Juliol, 218, 08221 Terrassa (Spain); Vaquero, C; Lopez de Ipina, J M, E-mail: mfaccini@leitat.org [Tecnalia, P.T. Alava - C/ Leonardo Da Vinci, 11, 01510 Minano (Alava) (Spain)

    2011-07-06

    In this article our latest advances in the development of efficient barrier systems against micro- and nano-particulate materials are presented. Nanofibrous polyamide 6 (PA6) mats were fabricated by electrospinning onto a nonwoven viscose substrate. The influence of electrospinning parameters including solution concentration, viscosity, and conductivity, were studied for the production of nonwovens with different fiber size distribution ranging from 74 to 261 nm in diameters. Moreover, the formation of nanowebs (30-40 nm) which are widely distributed among fibers was observed. By varying several process parameters, membranes with different thickness of the nanofiber layer and therefore air permeability and nanoparticle filtration efficiency were obtained.

  15. A super hydrophilic modification of poly(vinylidene fluoride) (PVDF) nanofibers: By in situ hydrothermal approach

    Science.gov (United States)

    Sheikh, Faheem A.; Zargar, Mohammad Afzal; Tamboli, Ashif H.; Kim, Hern

    2016-11-01

    Nanofibers fabricated from Poly(vinylidene fluoride) (PVDF) possesses potential applications in the field of filtrations, because of their excellent resistance towards harsh chemicals. However, the hydrophobicity restricts its further application. In this work, we focus on optimal parameters for post-electrospun tethering of Poly(vinyl alcohol) (PVA) as superhydrophilic domain onto each individual PVDF nanofibers by exploiting the in situ hydrothermal approach. The results indicated an increase in nanofiber diameters due to coating of PVA and improved surface wettability of PVDF nanofibers. The tensile tests of nanofibers indicated that mechanical properties of PVDF nanofibers could be sharply tuned from rigid to ductile. Furthermore, the studies strongly suggest that in situ hydrothermal treatment of post-electrospun nanofibers can improve the water contact angle and these nanofibers can be used in varied applications (e.g., in water purification systems).

  16. Ammonia Sensing Behaviors of TiO2-PANI/PA6 Composite Nanofibers

    Directory of Open Access Journals (Sweden)

    Fenglin Huang

    2012-12-01

    Full Text Available Titanium dioxide-polyaniline/polyamide 6 (TiO2-PANI/PA6 composite nanofibers were prepared by in situ polymerization of aniline in the presence of PA6 nanofibers and a sputtering-deposition process with a high purity titanium sputtering target. TiO2-PANI/PA6 composite nanofibers and PANI/PA6 composite nanofibers were fabricated for ammonia gas sensing. The ammonia sensing behaviors of the sensors were examined at room temperature. All the results indicated that the ammonia sensing property of TiO2-PANI/PA6 composite nanofibers was superior to that of PANI/PA6 composite nanofibers. TiO2-PANI/PA6 composite nanofibers had good selectivity to ammonia. It was also found that the content of TiO2 had a great influence on both the morphology and the sensing property of TiO2-PANI/PA6 composite nanofibers.

  17. The Pine-Needle-Inspired Structure of Zinc Oxide Nanorods Grown on Electrospun Nanofibers for High-Performance Flexible Supercapacitors.

    Science.gov (United States)

    Sami, Syed Kamran; Siddiqui, Saqib; Shrivastava, Sajal; Lee, Nae-Eung; Chung, Chan-Hwa

    2017-12-01

    Flexible supercapacitors with high electrochemical performance and stability along with mechanical robustness have gained immense attraction due to the substantial advancements and rampant requirements of storage devices. To meet the exponentially growing demand of microsized energy storage device, a cost-effective and durable supercapacitor is mandatory to realize their practical applications. Here, in this work, the fabrication route of novel electrode materials with high flexibility and charge-storage capability is reported using the hybrid structure of 1D zinc oxide (ZnO) nanorods and conductive polyvinylidene fluoride-tetrafluoroethylene (P(VDF-TrFE)) electrospun nanofibers. The ZnO nanorods are conformably grown on conductive P(VDF-TrFE) nanofibers to fabricate the light-weighted porous electrodes for supercapacitors. The conductive nanofibers acts as a high surface area scaffold with significant electrochemical performance, while the addition of ZnO nanorods further enhances the specific capacitance by 59%. The symmetric cell with the fabricated electrodes presents high areal capacitance of 1.22 mF cm -2 at a current density of 0.1 mA cm -2 with a power density of more than 1600 W kg -1 . Furthermore, these electrodes show outstanding flexibility and high stability with 96% and 78% retention in specific capacitance after 1000 and 5000 cycles, respectively. The notable mechanical durability and robustness of the cell acquire both good flexibility and high performance. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Nanofiber Manufacture, Properties, and Applications

    International Nuclear Information System (INIS)

    Lin, T.; Lukas, D.; Bhat, G.S.

    2013-01-01

    Nano fibers have shown many unique characteristics and enormous application potential in widely diverse areas. While considerable research has been conducted on exploring the properties and applications of nano fibers over the decade, the technology development for large-scale production of nano fibers has been hampered, which slows down the wide applications of nano fibers in practice. This special issue focuses on the recent progress in emerging nano fiber production techniques, such as needle less electro spinning, and novel properties and applications of nano fibers. It also covers unusual methods to process natural materials into nano fibrous materials. The special issue consists of four review articles and eighteen research papers. One review paper presents an overview of the recent developments in needle less electro spinning and the influences of needle less spinnerets on electro spinning process, nano fiber quality and productivity. The review also points out the challenges remaining for further research in this area. Other three reviews separately summarize the preparation, characterization and applications of ZnO nano wires and the applications of carbon nano fibers for neural electrical/chemical interfaces and for cement reinforcement. The research articles report new results of needle less electro spinning techniques, and novel methods to make bi component nano fibers, porous nano fibers, nano fiber hydrogel and chitin nan ofibrils. As Guest Editors for this special issue, we are pleased to see the progress in the applications of nano fibers, especially for sound absorption and for protective clothing, as well as the antibacterial properties of titanate nano fibers. We hope this special issue will promote further development of large-scale economically feasible nano fiber-making technologies, and also contribute to the wide use of nano fibers. We also hope that the articles collected in this special issue are well-received by the reader.

  19. Branched carbon nanofiber network synthesis at room temperature using radio frequency supported microwave plasmas

    OpenAIRE

    Boskovic, BO; Stolojan, V; Zeze, DA; Forrest, RD; Silva, SRP; Haq, S

    2004-01-01

    Carbon nanofibers have been grown at room temperature using a combination of radio frequency and microwave assisted plasma-enhanced chemical vapor deposition. The nanofibers were grown, using Ni powder catalyst, onto substrates kept at room temperature by using a purposely designed water-cooled sample holder. Branched carbon nanofiber growth was obtained without using a template resulting in interconnected carbon nanofiber network formation on substrates held at room temperatur...

  20. Single clay sheets inside electrospun polymer nanofibers

    Science.gov (United States)

    Sun, Zhaohui

    2005-03-01

    Nanofibers were prepared from polymer solution with clay sheets by electrospinning. Plasma etching, as a well controlled process, was used to supply electrically excited gas molecules from a glow discharge. To reveal the structure and arrangement of clay layers in the polymer matrix, plasma etching was used to remove the polymer by controlled gasification to expose the clay sheets due to the difference in reactivity. The shape, flexibility, and orientation of clay sheets were studied by transmission and scanning electron microscopy. Additional quantitative information on size distribution and degree of exfoliation of clay sheets were obtained by analyzing electron micrograph of sample after plasma etching. Samples in various forms including fiber, film and bulk, were thinned by plasma etching. Morphology and dispersion of inorganic fillers were studied by electron microscopy.

  1. Carbon nanofiber supercapacitors with large areal capacitances

    KAUST Repository

    McDonough, James R.

    2009-01-01

    We develop supercapacitor (SC) devices with large per-area capacitances by utilizing three-dimensional (3D) porous substrates. Carbon nanofibers (CNFs) functioning as active SC electrodes are grown on 3D nickel foam. The 3D porous substrates facilitate a mass loading of active electrodes and per-area capacitance as large as 60 mg/ cm2 and 1.2 F/ cm2, respectively. We optimize SC performance by developing an annealing-free CNF growth process that minimizes undesirable nickel carbide formation. Superior per-area capacitances described here suggest that 3D porous substrates are useful in various energy storage devices in which per-area performance is critical. © 2009 American Institute of Physics.

  2. New products made with lignocellulosic nanofibers from Brazilian amazon forest

    International Nuclear Information System (INIS)

    Bufalino, L; Mendes, L M; Tonoli, G H D; Fonseca, A; Rodrigues, A; Cunha, P I; Marconcini, J M

    2014-01-01

    The biodiversity of the Amazon forest is undoubtedly rich; hence there is considerable variety of plant fibers regarding their morphological, chemical and structural properties. The legal exploration of the Brazilian Amazon is based on sustainable management techniques, but the generation of a relevant amount of plant wastes still cant be avoided. The correct destination of such materials is a challenge that Brazilian companies have to face. In this context, the National Council of Science and Technology (CNPq) promoted the creation of investigation nets on sustainability of Brazilian agribusiness. The Brazilian Net on Lignocellulosic Composites and Nanocomposites was then created, with partnership between several national and international research institutions. Until the moment, the results showed that Amazon plant fibers that are discarded as residues have great potential to nanofiber production. Nanopapers with considerable high mechanical and physical strength, proper opacity and great crystalline index were produced by using a clean and simple mechanical method. Those materials are candidates to several uses such as packaging, substrates transparent conductive films, gas barrier films, solar cells and e-papers

  3. Highly efficient and durable TiN nanofiber electrocatalyst supports.

    Science.gov (United States)

    Kim, Hyun; Cho, Min Kyung; Kwon, Jeong An; Jeong, Yeon Hun; Lee, Kyung Jin; Kim, Na Young; Kim, Min Jung; Yoo, Sung Jong; Jang, Jong Hyun; Kim, Hyoung-Juhn; Nam, Suk Woo; Lim, Dong-Hee; Cho, EunAe; Lee, Kwan-Young; Kim, Jin Young

    2015-11-28

    To date, carbon-based materials including various carbon nanostructured materials have been extensively used as an electrocatalyst support for proton exchange membrane fuel cell (PEMFC) applications due to their practical nature. However, carbon dissolution or corrosion caused by high electrode potential in the presence of O2 and/or water has been identified as one of the main failure modes for the device operation. Here, we report the first TiN nanofiber (TNF)-based nonwoven structured materials to be constructed via electrospinning and subsequent two-step thermal treatment processes as a support for the PEMFC catalyst. Pt catalyst nanoparticles (NPs) deposited on the TNFs (Pt/TNFs) were electrochemically characterized with respect to oxygen reduction reaction (ORR) activity and durability in an acidic medium. From the electrochemical tests, the TNF-supported Pt catalyst was better and more stable in terms of its catalytic performance compared to a commercially available carbon-supported Pt catalyst. For example, the initial oxygen reduction performance was comparable for both cases, while the Pt/TNF showed much higher durability from an accelerated degradation test (ADT) configuration. It is understood that the improved catalytic roles of TNFs on the supported Pt NPs for ORR are due to the high electrical conductivity arising from the extended connectivity, high inertness to the electrochemical environment and strong catalyst-support interactions.

  4. New products made with lignocellulosic nanofibers from Brazilian amazon forest

    Science.gov (United States)

    Bufalino, L.; Mendes, L. M.; Tonoli, G. H. D.; Rodrigues, A.; Fonseca, A.; Cunha, P. I.; Marconcini, J. M.

    2014-08-01

    The biodiversity of the Amazon forest is undoubtedly rich; hence there is considerable variety of plant fibers regarding their morphological, chemical and structural properties. The legal exploration of the Brazilian Amazon is based on sustainable management techniques, but the generation of a relevant amount of plant wastes still cant be avoided. The correct destination of such materials is a challenge that Brazilian companies have to face. In this context, the National Council of Science and Technology (CNPq) promoted the creation of investigation nets on sustainability of Brazilian agribusiness. The Brazilian Net on Lignocellulosic Composites and Nanocomposites was then created, with partnership between several national and international research institutions. Until the moment, the results showed that Amazon plant fibers that are discarded as residues have great potential to nanofiber production. Nanopapers with considerable high mechanical and physical strength, proper opacity and great crystalline index were produced by using a clean and simple mechanical method. Those materials are candidates to several uses such as packaging, substrates transparent conductive films, gas barrier films, solar cells and e-papers.

  5. Flux Enhancement in Membrane Distillation Using Nanofiber Membranes

    Directory of Open Access Journals (Sweden)

    T. Jiříček

    2016-01-01

    Full Text Available Membrane distillation (MD is an emerging separation technology, whose largest application potential lies in the desalination of highly concentrated solutions, which are out of the scope of reverse osmosis. Despite many attractive features, this technology is still awaiting large industrial application. The main reason is the lack of commercially available membranes with fluxes comparable to reverse osmosis. MD is a thermal separation process driven by a partial vapour pressure difference. Flux, distillate purity, and thermal efficiency are always in conflict, all three being strictly connected with pore size, membrane hydrophobicity, and thickness. The world has not seen the ideal membrane yet, but nanofibers may offer a solution to these contradictory requirements. Membranes of electrospun PVDF were tested under various conditions on a direct contact (DCMD unit, in order to determine the optimum conditions for maximum flux. In addition, their performance was compared to commonly available PTFE, PE, and PES membranes. It was confirmed that thinner membranes have higher fluxes and a lower distillate purity and also higher energy losses via conduction across the membrane. As both mass and heat transfer are connected, it is best to develop new membranes with a target application in mind, for the specific membrane module and operational conditions.

  6. Preparation, Characterization, and Modeling of Carbon Nanofiber/Epoxy Nanocomposites

    Directory of Open Access Journals (Sweden)

    Lan-Hui Sun

    2011-01-01

    Full Text Available There is a lack of systematic investigations on both mechanical and electrical properties of carbon nanofiber (CNF-reinforced epoxy matrix nanocomposites. In this paper, an in-depth study of both static and dynamic mechanical behaviors and electrical properties of CNF/epoxy nanocomposites with various contents of CNFs is provided. A modified Halpin-Tsai equation is used to evaluate the Young's modulus and storage modulus of the nanocomposites. The values of Young's modulus predicted using this method account for the effect of the CNF agglomeration and fit well with those obtained experimentally. The results show that the highest tensile strength is found in the epoxy nanocomposite with a 1.0 wt% CNFs. The alternate-current (AC electrical properties of the CNF/epoxy nanocomposites exhibit a typical insulator-conductor transition. The conductivity increases by four orders of magnitude with the addition of 0.1 wt% (0.058 vol% CNFs and by ten orders of magnitude for nanocomposites with CNF volume fractions higher than 1.0 wt% (0.578 vol%. The percolation threshold (i.e., the critical CNF volume fraction is found to be at 0.057 vol%.

  7. The effect of filler aspect ratio on the electromagnetic properties of carbon-nanofibers reinforced composites

    Energy Technology Data Exchange (ETDEWEB)

    De Vivo, B.; Lamberti, P.; Spinelli, G., E-mail: gspinelli@unisa.it; Tucci, V. [Department of Information Engineering, Electrical Engineering and Applied Mathematics—DIEM, University of Salerno, Via Giovanni Paolo II 132, 84084 Fisciano SA (Italy); Guadagno, L.; Raimondo, M. [Department of Industrial Engineering—DIIn, University of Salerno, Via Giovanni Paolo II 132, 84084 Fisciano SA (Italy)

    2015-08-14

    The effect of filler aspect ratio on the electromagnetic properties of epoxy-amine resin reinforced with carbon nanofibers is here investigated. A heat treatment at 2500 °C of carbon nanofibers seems to increase their aspect ratio with respect to as-received ones most likely due to a lowering of structural defects and the improvement of the graphene layers within the dixie cup conformation. These morphological differences revealed by Raman's spectroscopy and scanning electron microscopy analyses may be responsible for the different electrical properties of the resulting composites. The DC characterization of the nanofilled material highlights an higher electrical conductivity and a lower electrical percolation threshold for the heat-treated carbon nanofibers based composites. In fact, the electrical conductivity is about 0.107 S/m and 1.36 × 10{sup −3} S/m for the nanocomposites reinforced with heat-treated and as received fibers, respectively, at 1 wt. % of nanofiller loading, while the electrical percolation threshold falls in the range [0.05–0.32]wt. % for the first nanocomposites and above 0.64 wt. % for the latter. Moreover, also a different frequency response is observed since the critical frequency, which is indicative of the transition from a resistive to a capacitive-type behaviour, shifts forward of about one decade at the same filler loading. The experimental results are supported by theoretical and simulation studies focused on the role of the filler aspect ratio on the electrical properties of the nanocomposites.

  8. Properties of a New Nanofiber Restorative Composite.

    Science.gov (United States)

    Yancey, E M; Lien, W; Nuttall, C S; Brewster, J A; Roberts, H W; Vandewalle, K S

    2018-04-09

    A new nanofiber-reinforced hybrid composite (NovaPro Fill, Nanova) was recently introduced with reportedly improved mechanical properties. The purpose of this study was to compare the properties (flexural strength/modulus, degree of conversion [DC], depth of cure, and polymerization shrinkage) of the nanofiber composite to those of traditional hybrid composites (Filtek Z250, 3M ESPE; Esthet-X HD, Dentsply). To determine flexural strength and modulus, composite was placed in a rectangular mold, light-cured, stored for 24 hours, and then fractured in a universal testing machine. For degree of conversion, composite was placed in a cylindrical mold, light-cured, and stored for 24 hours. Measurements were made at the top and bottom surfaces using Fourier Transform Infrared Spectroscopy. To determine depth of cure, composite was placed in a cylindrical mold and light-cured. Uncured composite was scraped until polymerized resin was reached. Remaining composite was measured and divided by two. Polymerization shrinkage was determined by placing the composite material on a pedestal in a video-imaging device while light-curing. Shrinkage was determined after 10 minutes. Data were analyzed with one-way analysis of variance and Tukey post hoc test per property (α=0.05). Compared to Filtek Z250, NovaPro Fill had significantly lower flexural strength and modulus, greater volumetric shrinkage, and similar depth of cure, but greater top and bottom DC. Compared to Esthet-X HD, NovaPro Fill had similar flexural strength, shrinkage, and top and bottom DC, but significantly greater depth of cure and flexural modulus.

  9. Growth and characterization of hydroxyapatite nanorice on TiO2 nanofibers

    KAUST Repository

    Chetibi, Loubna; Hamana, Djamel; Achour, Slimane

    2014-01-01

    with anatase TiO2 nanofibers. These nanofibers were prepared by in situ oxidation of Ti foils in a concentrated solution of H 2O2 and NaOH, followed by proton exchange and calcinations. Afterward, TiO2 nanofibers on Ti substrate were coated with HA

  10. Coaxial nanofibers containing TiO2 in the shell for water treatment applications

    Science.gov (United States)

    Kizildag, N.; Geltmeyer, J.; Ucar, N.; De Buysser, K.; De Clerck, K.

    2017-10-01

    In recent years, the basic electrospinning setup has undergone many modifications carried out to enhance the quality and improve the functionality of the resulting nanofibers. Being one of these modifications, coaxial electrospinning has attracted great attention. It enables to use different materials in nanofiber production and produce multi-layered and functional nanofibers in one step. In this study, TiO2 has been added to the shell layer of coaxial nanofibers to develop functional nanofibers which may be used in water treatment applications. The coaxial nanofibers containing TiO2 in the shell layer are compared to uniaxial nanofibers containing TiO2 in bulk fiber structure, regarding their morphology and photocatalytic activity. Uniform uniaxial and coaxial nanofibers with TiO2 were obtained. The average nanofiber diameter of coaxial nanofibers were higher. Coaxial nanofibers, which contained lower amount of TiO2, displayed similar performance to uniaxial nanofibers with TiO2 in terms of photocatalytic degradation ability against isoproturon.

  11. Antioxidant activity and haemolysis prevention efficiency of polyaniline nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Banerjee, Somik; Kumar, A [Materials Research Laboratory, Department of Physics, Tezpur University, Tezpur 784028, Assam (India); Saikia, Jyoti P; Konwar, B K, E-mail: ask@tezu.ernet.in [Department of Molecular Biology and Biotechnology, Tezpur University, Tezpur 784028, Assam (India)

    2010-01-29

    Polyaniline (PAni) nanofibers have been synthesized by interfacial polymerization using hydrochloric acid (HCl) and camphor sulfonic acid (CSA) as dopants. The powder x-ray diffraction pattern of bulk polyaniline reveals ES I structure and has been indexed in a pseudo-orthorhombic lattice. The broadening of (110) reflection in the nanofiber samples has been analysed in terms of domain length and strain using a convolution method employing a Voigt function. The increase in d spacing for the (110) reflection in HCl-doped PAni nanofibers have been assigned to the change in structural conformation due to the increase in the tilt angle of the polymer chain, which is also evident from microRaman spectra. UV-vis spectra of the PAni nanofibers exhibit a remarkable blueshift in the absorption bands attributed to {pi}-{pi}{sup *} and {pi}-polaron band transitions indicating a reduction in particle size, which is also observed in TEM micrographs. The antioxidant activity of the polyaniline nanofiber samples has been investigated using 1,1-diphenyl-2-picrylhydrazyl (DPPH) scavenging assay by employing UV-visible spectroscopy. It has also been observed that polyaniline nanofibers are able to protect the haemolysis of red blood cells (RBCs) from cytotoxic agents, namely H{sub 2}O{sub 2}. The observed enhancement in the antioxidant and haemolysis prevention activity of the PAni nanofibers as compared to bulk has been attributed to the reduction in particle size and changes in structural conformation, as evident from TEM, XRD and microRaman spectroscopy.

  12. Self-assembling peptide nanofiber hydrogels in tissue engineering and regenerative medicine: Progress, design guidelines, and applications.

    Science.gov (United States)

    Koutsopoulos, Sotirios

    2016-04-01

    Until the mid-1980s, mainly biologists were conducting peptide research. This changed with discoveries that opened new paths of research involving the use of peptides in bioengineering, biotechnology, biomedicine, nanotechnology, and bioelectronics. Peptide engineering and rational design of novel peptide sequences with unique and tailor-made properties further expanded the field. The discovery of short self-assembling peptides, which upon association form well-defined supramolecular architectures, created new and exciting areas of research. Depending on the amino acid sequence, the pH, and the type of the electrolyte in the medium, peptide self-assembly leads to the formation of nanofibers, which are further organized to form a hydrogel. In this review, the application of ionic complementary peptides which self-assemble to form nanofiber hydrogels for tissue engineering and regenerative medicine will be discussed through a selective presentation of the most important work performed during the last 25 years. © 2016 Wiley Periodicals, Inc.

  13. Multifunctional e-spun colloidal nanofiber structures from various dispersed blends of PVA/ODA-MMT with PVP/ODA-MMT, poly(VP-alt-MA and AgNPs incorporated polymer complexes as electro-active platforms

    Directory of Open Access Journals (Sweden)

    U. Bunyatova

    2016-07-01

    Full Text Available This work presented a new approach to fabricate polymer nanocomposites films with nanofiber structures from solution blends of poly(vinyl alcohol + octadecyl amine-montmorillonite (ODA-MMT (matrix with poly(N-vinylpyrrolidone + ODA-MMT (partner-1, poly(N-vinylpyrrolidone-alt-maleic anhydride ((poly(VP-alt-MA + (ODA-MMT (partner-2 and their silver (Ag-carrying polymer complexes by electrospinning. Chemical and physical structures, surface morphologies, thermal behaviors, electrical conductivity and thermal resistance parameters of nanofiber structures were investigated. Poly(VP-alt-MA was used both as a crosslinker and a donor of the hydrophilic groups such as ‒COOH and ‒NH–C=O amide from pyrrolidone ring. Reactive poly(VP-alt-MA, in situ generated Ag nanoparticles (AgNPs and original partner polymer had an significant effect on the morphology and diameter distribution of nanofibers. High and excellent conductive behaviors were observed for the homopolymer and copolymer of VP based fiber structures, respectively. Upon successive chemical cross-linking of the nanofiber structures by reactive partner copolymer, the conductivity of nanofiber films as electro-active platforms dramatically increased to 3.90·10–2 S·cm–1 at room temperature. Comparative analysis results also indicated that electrical properties strongly depended on the loaded reactive organoclay and in situ generated AgNPs.

  14. Fabrication of hierarchically porous TiO2 nanofibers by microemulsion electrospinning and their application as anode material for lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    Jin Zhang

    2017-06-01

    Full Text Available Titanium dioxide (TiO2 nanofibers have been widely applied in various fields including photocatalysis, energy storage and solar cells due to the advantages of low cost, high abundance and nontoxicity. However, the low conductivity of ions and bulk electrons hinder its rapid development in lithium-ion batteries (LIB. In order to improve the electrochemical performances of TiO2 nanomaterials as anode for LIB, hierarchically porous TiO2 nanofibers with different tetrabutyl titanate (TBT/paraffin oil ratios were prepared as anode for LIB via a versatile single-nozzle microemulsion electrospinning (ME-ES method followed by calcining. The experimental results indicated that TiO2 nanofibers with the higher TBT/paraffin oil ratio demonstrated more axially aligned channels and a larger specific surface area. Furthermore, they presented superior lithium-ion storage properties in terms of specific capacity, rate capability and cycling performance compared with solid TiO2 nanofibers for LIB. The initial discharge and charge capacity of porous TiO2 nanofibers with a TBT/paraffin oil ratio of 2.25 reached up to 634.72 and 390.42 mAh·g−1, thus resulting in a coulombic efficiency of 61.51%; and the discharge capacity maintained 264.56 mAh·g−1 after 100 cycles, which was much higher than that of solid TiO2 nanofibers. TiO2 nanofibers with TBT/paraffin oil ratio of 2.25 still obtained a high reversible capacity of 204.53 mAh·g−1 when current density returned back to 40 mA·g−1 after 60 cycles at increasing stepwise current density from 40 mA·g−1 to 800 mA·g−1. Herein, hierarchically porous TiO2 nanofibers have the potential to be applied as anode for lithium-ion batteries in practical applications.

  15. Polypropylene/Polyaniline Nanofiber/Reduced Graphene Oxide Nanocomposite with Enhanced Electrical, Dielectric, and Ferroelectric Properties for a High Energy Density Capacitor.

    Science.gov (United States)

    Cho, Sunghun; Kim, Minkyu; Lee, Jun Seop; Jang, Jyongsik

    2015-10-14

    This work demonstrates a ternary nanocomposite system, composed of polypropylene (PP), redoped PANI (r-PANI) nanofibers, and reduced graphene oxides (RGOs), for use in a high energy density capacitor. r-PANI nanofibers were fabricated by the combination methods of chemical oxidation polymerization and secondary doping processes, resulting in higher conductivity (σ≈156 S cm(-1)) than that of the primarily doped PANI nanofibers (σ≈16 S cm(-1)). RGO sheets with high electron mobility and thermal stability can enhance the conductivity of r-PANI/RGO (σ≈220 S cm(-1)) and thermal stability of PP matrix. These findings could be extended to combine the advantages of r-PANI nanofibers and RGO sheets for developing an efficient means of preparing PP/r-PANI/RGO nanocomposite. When the r-PANI/RGO cofillers (10 vol %) were added to PP matrix, the resulting PP/r-PANI/RGO nanocomposite exhibited high dielectric constant (ε'≈51.8) with small dielectric loss (ε″≈9.3×10(-3)). Furthermore, the PP/r-PANI/RGO nanocomposite was used for an energy-harvesting device, which demonstrated high energy density (Ue≈12.6 J cm(-3)) and breakdown strength (E≈5.86×10(3) kV cm(-1)).

  16. Preparation and characterization of single-crystal multiferroic nanofiber composites

    Energy Technology Data Exchange (ETDEWEB)

    Ren, Zhaohui; Xiao, Zhen; Yin, Simin; Mai, Jiangquan; Liu, Zhenya; Xu, Gang; Li, Xiang; Shen, Ge [State Key Lab of Silicon Materials, Department of Material Science and Engineering, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China); Han, Gaorong, E-mail: hgr@zju.edu.cn [State Key Lab of Silicon Materials, Department of Material Science and Engineering, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou 310027 (China)

    2013-03-05

    Graphical abstract: One-dimensional single-crystal multiferroic composites composed of PbTiO{sub 3} nanofiber-CoFe{sub 2}O{sub 4} nanodot have been prepared for the first time by a facile in situ solid state sintering method. The composites demonstrate ferroelectricity and ferromagnetism as well as strong coupling between them. Highlights: ► 1D single-crystal multiferroic PTO-CFO was prepared via in situ solid state sintering method. ► A simple epitaxial growth relation has been found between the PTO–CFO composites. ► The composites reveal ferroelectricity and ferromagnetism as well as coupling between them. -- Abstract: One-dimensional single-crystal multiferroic composites consisting of PbTiO{sub 3} (PTO) nanofiber-CoFe{sub 2}O{sub 4} (CFO) nanodot were prepared using an in situ solid state sintering method, where pre-perovskite PTO nanofibers and CFO nanodots were used as precursors. Structural analyses by using transmission electron microscopy, scanning electron microscopy and X-ray diffraction determined a epitaxial growth relation between the PTO nanofiber and the CFO nanodot. Ferromagnetism and ferroelectricity of the nanofiber composites were investigated by using vibarting sample magnetometer (VSM) and piezoresponse force microscopy (PFM)

  17. Hybrid electrospun chitosan-phospholipids nanofibers for transdermal drug delivery.

    Science.gov (United States)

    Mendes, Ana C; Gorzelanny, Christian; Halter, Natalia; Schneider, Stefan W; Chronakis, Ioannis S

    2016-08-20

    Chitosan (Ch) polysaccharide was mixed with phospholipids (P) to generate electrospun hybrid nanofibers intended to be used as platforms for transdermal drug delivery. Ch/P nanofibers exibithed average diameters ranging from 248±94nm to 600±201nm, depending on the amount of phospholipids used. Fourier Transformed Infra-Red (FTIR) spectroscopy and Dynamic Light Scattering (DLS) data suggested the occurrence of electrostatic interactions between amine groups of chitosan with the phospholipid counterparts. The nanofibers were shown to be stable for at least 7days in Phosphate Buffer Saline (PBS) solution. Cytotoxicity studies (WST-1 and LDH assays) demonstrated that the hybrid nanofibers have suitable biocompatibility. Fluorescence microscopy, also suggested that L929 cells seeded on top of the CH/P hybrid have similar metabolic activity comparatively to the cells seeded on tissue culture plate (control). The release of curcumin, diclofenac and vitamin B12, as model drugs, from Ch/P hybrid nanofibers was investigated, demonstrating their potential utilization as a transdermal drug delivery system. Copyright © 2016 Elsevier B.V. All rights reserved.

  18. Modeling, simulation, and experiments of coating growth on nanofibers

    International Nuclear Information System (INIS)

    Clemons, C. B.; Hamrick, P.; Heminger, J.; Kreider, K. L.; Young, G. W.; Buldum, A.; Evans, E.; Zhang, G.

    2008-01-01

    This work is a comparison of modeling and simulation results with experiments for an integrated experimental/modeling investigation of a procedure to coat nanofibers and core-clad nanostructures with thin film materials using plasma enhanced physical vapor deposition. In the experimental effort, electrospun polymer nanofibers are coated with metallic materials under different operating conditions to observe changes in the coating morphology. The modeling effort focuses on linking simple models at the reactor level, nanofiber level and atomic level to form a comprehensive model. The comprehensive model leads to the definition of an evolution equation for the coating free surface around an isolated nanofiber. This evolution equation was previously derived and solved under conditions of a nearly circular coating, with a concentration field that was only radially dependent and that was independent of the location of the coating free surface. These assumptions permitted the development of analytical expressions for the concentration field. The present work does not impose the above-mentioned conditions and considers numerical simulations of the concentration field that couple with level set simulations of the evolution equation for the coating free surface. Further, the cases of coating an isolated fiber as well as a multiple fiber mat are considered. Simulation results are compared with experimental results as the reactor pressure and power, as well as the nanofiber mat porosity, are varied

  19. Enhancement of Ultrahigh Performance Concrete Material Properties with Carbon Nanofiber

    Directory of Open Access Journals (Sweden)

    Libya Ahmed Sbia

    2014-01-01

    Full Text Available Ultrahigh performance concrete (UHPC realized distinctly high mechanical, impermeability, and durability characteristics by reducing the size and content of capillary pore, refining the microstructure of cement hydrates, and effectively using fiber reinforcement. The dense and fine microstructure of UHPC favor its potential to effectively disperse and interact with nanomaterials, which could complement the reinforcing action of fibers in UHPC. An optimization experimental program was implemented in order to identify the optimum combination of steel fiber and relatively low-cost carbon nanofiber in UHPC. The optimum volume fractions of steel fiber and carbon nanofiber identified for balanced improvement of flexural strength, ductility, energy sorption capacity, impact, and abrasion resistance of UHPC were 1.1% and 0.04%, respectively. Desired complementary/synergistic actions of nanofibers and steel fibers in UHPC were detected, which were attributed to their reinforcing effects at different scales, and the potential benefits of nanofibers to interfacial bonding and pull-out behavior of fibers in UHPC. Modification techniques which enhanced the hydrophilicity and bonding potential of nanofibers to cement hydrates benefited their reinforcement efficiency in UHPC.

  20. Dry adhesives from carbon nanofibers grown in an open ethanol flame

    Directory of Open Access Journals (Sweden)

    Christian Lutz

    2017-12-01

    Full Text Available Based on magnetic-field-assisted growth of carbon nanofibers in an open ethanol flame we fabricated arrays of carbon nanofibers with different degrees of orientation. Inspired by the dry adhesive system of geckos we investigated the adhesive properties of such carbon nanofiber arrays with ordered and random orientation. AFM-based force spectroscopy revealed that adhesion force and energy rise linear with preload force. Carbon nanofibers oriented by a magnetic field show a 68% higher adhesion (0.66 N/cm2 than the randomly oriented fibers. Endurance tests revealed that the carbon nanofiber arrays withstand 50.000 attachment/detachment cycles without observable wear.

  1. Facile Preparation and Enhanced Capacitance of the Ag-PEDOT:PSS/Polyaniline Nanofiber Network for Supercapacitors

    International Nuclear Information System (INIS)

    Patil, Dipali S.; Pawar, Sachin A.; Kim, Jin Hyeok; Patil, Pramod S.; Shin, Jae Cheol

    2016-01-01

    Graphical abstract: Fig. shows the steps involved in the development of the AgNW-PEDOT:PSS/PANI electrode. The bright silver nanocubes were observed onto the PANI nanofibers. This means that during the electrodeposition of PANI, there is an electrostatic interaction between AgNWs and PANI; the AgNWs are segmented into the small nanocubes. These nanocubes are distributed equally all over the interconnected network of the PANI nanofibers. This provides a continuous path for the electrons during the charge/discharge process. - Highlights: • Ag-PEDOT:PSS/PANI hybrid nanostructure was prepared. • Dip coating and electrodeposition techniques are used for electrodes preparation. • Symmetric supercapacitor based on AgNW-PEDOT:PSS/PANI was developed. • The positive synergistic effect of AgNW, PEDOT:PSS and PANI was observed. - Abstract: This paper reports the synthesis of a silver − Poly(3,4-ethylenedioxythiophene):poly(styrene sulfonate)/Polyaniline(Ag-PEDOT:PSS/PANI)hybrid nanostructure using a simple dip coating technique followed by potentiodynamic electrodeposition to achieve an electrochemical supercapacitor with excellent electrochemical performance. In this sandwich type structure, the Ag nanostructure-blended PEDOT: PSS acts as a current collector, where electrons can be transferred easily through this network to the PANI nanofibers and vice versa. The AgNW-PEDOT:PSS/PANI showed a specific capacitance of 643 Fg −1 at 10 mVs −1 and an energy density of 86.19 Whkg −1 at 0.1 mA, indicating the positive synergistic effect of silver nanowires (AgNW), PEDOT:PSS and PANI. The Ag nanostructure incorporated PEDOT:PSS helps to improve the electronic conductivity and the electrochemical stability of the PANI electrodes. Promising electrochemical properties achieved from the measurement of symmetric device demonstrate the ideal capacitive behavior of our prepared electrodes.

  2. Evaluation of proanthocyanidin-crosslinked electrospun gelatin nanofibers for drug delivering system

    International Nuclear Information System (INIS)

    Huang, Chiung-Hua; Chi, Chin-Ying; Chen, Yueh-Sheng; Chen, Kuo-Yu; Chen, Pei-Lain; Yao, Chun-Hsu

    2012-01-01

    Electrospun nanofibers are excellent candidates for various biomedical applications. We successfully fabricated proanthocyanidin‐crosslinked gelatin electrospun nanofibers. Proanthocyanidin, a low cytotoxic collagen crosslinking reagent, increased the gelatin crosslinking percentage in the nanofibers from 53% to 64%. The addition of proanthocyanidin kept the nanofibers from swelling, and, thus, made the fibers more stable in the aqueous state. The compatibility and the release behavior of the drug in the nanofibers were examined using magnesium ascorbyl phosphate as the model drug. Proanthocyanidin also promoted drug loading and kept the drug release rate constant. These properties make the proanthocyanidin‐crosslinked gelatin nanofibers an excellent material for drug delivery. In the cell culture study, L929 fibroblast cells had a significantly higher proliferation rate when cultured with the gelatin/proanthocyanidin blended nanofibers. This characteristic showed that proanthocyanidin‐crosslinked gelatin electrospun nanofibers could potentially be employed as a wound healing material by increasing cell spreading and proliferation. - Highlights: ► Proanthocyanidin‐crosslinked gelatin nanofibers (GEL/PA) is synthesized. ► Proanthocyanidin promoted drug loading and kept the drug release rate constant. ► The GEL/PA nanofibers accelerate fibroblast cell proliferation. ► The GEL/PA nanofibers increase the drug loading efficiency.

  3. Bioactive Glass Nanoparticles-Loaded Poly(ɛ-caprolactone Nanofiber as Substrate for ARPE-19 Cells

    Directory of Open Access Journals (Sweden)

    Tadeu Henrique Lima

    2016-01-01

    Full Text Available Bioactive glass nanoparticles-loaded poly(ɛ-caprolactone nanofibers (BIOG PCL nanofibers were synthesized and evaluated as substrates for ocular cells (ARPE-19. BIOG PCL nanofibers were characterized using SEM, FTIR, and DSC, and the in vitro degradation profile was also investigated. The in vitro ocular biocompatibility of nanofibers was exploited in Müller glial cells (MIO-M1 cells and in chorioallantoic membrane (CAM; and the proliferative capacity, cytotoxicity, and functionality were evaluated. Finally, ARPE-19 cells were seeded onto BIOG PCL nanofibers and they were investigated as supports for in vitro cell adhesion and proliferation. SEM images revealed the incorporation of BIOG nanoparticles into PCL nanofibers. Nanoparticles did not induce modifications in the chemical structure and semicrystalline nature of PCL in the nanofiber, as shown by FTIR and DSC. MIO-M1 cells exposed to BIOG PCL nanofibers showed viability, and they were able to proliferate and to express GFAP, indicating cellular functionality. Moreover, nanofibers were well tolerated by CAM. These findings suggested the in vitro ocular biocompatibility and absence of toxicity of these nanofibers. Finally, the BIOG nanoparticles modulated the protein adsorption, and, subsequently, ARPE-19 cells adhered and proliferated onto the nanostructured supports, establishing cell-substrate interactions. In conclusion, the biodegradable and biocompatible BIOG PCL nanofibers supported the ARPE-19 cells.

  4. Improving effects of chitosan nanofiber scaffolds on osteoblast proliferation and maturation

    Science.gov (United States)

    Ho, Ming-Hua; Liao, Mei-Hsiu; Lin, Yi-Ling; Lai, Chien-Hao; Lin, Pei-I; Chen, Ruei-Ming

    2014-01-01

    Osteoblast maturation plays a key role in regulating osteogenesis. Electrospun nanofibrous products were reported to possess a high surface area and porosity. In this study, we developed chitosan nanofibers and examined the effects of nanofibrous scaffolds on osteoblast maturation and the possible mechanisms. Macro- and micro observations of the chitosan nanofibers revealed that these nanoproducts had a flat surface and well-distributed fibers with nanoscale diameters. Mouse osteoblasts were able to attach onto the chitosan nanofiber scaffolds, and the scaffolds degraded in a time-dependent manner. Analysis by scanning electron microscopy further showed mouse osteoblasts adhered onto the scaffolds along the nanofibers, and cell–cell communication was also detected. Mouse osteoblasts grew much better on chitosan nanofiber scaffolds than on chitosan films. In addition, human osteoblasts were able to adhere and grow on the chitosan nanofiber scaffolds. Interestingly, culturing human osteoblasts on chitosan nanofiber scaffolds time-dependently increased DNA replication and cell proliferation. In parallel, administration of human osteoblasts onto chitosan nanofibers significantly induced osteopontin, osteocalcin, and alkaline phosphatase (ALP) messenger (m)RNA expression. As to the mechanism, chitosan nanofibers triggered runt-related transcription factor 2 mRNA and protein syntheses. Consequently, results of ALP-, alizarin red-, and von Kossa-staining analyses showed that chitosan nanofibers improved osteoblast mineralization. Taken together, results of this study demonstrate that chitosan nanofibers can stimulate osteoblast proliferation and maturation via runt-related transcription factor 2-mediated regulation of osteoblast-associated osteopontin, osteocalcin, and ALP gene expression. PMID:25246786

  5. Surface functionalization of carbon nanofibers by sol-gel coating of zinc oxide

    Energy Technology Data Exchange (ETDEWEB)

    Shao Dongfeng [Key Laboratory of Eco-textiles, Ministry of Education, Jiangnan University, Wuxi 214122 (China); Changzhou Textile Garment Institute, Changzhou 213164 (China); Wei Qufu [Key Laboratory of Eco-textiles, Ministry of Education, Jiangnan University, Wuxi 214122 (China)], E-mail: qfwei@jiangnan.edu.cn; Zhang Liwei; Cai Yibing; Jiang Shudong [Key Laboratory of Eco-textiles, Ministry of Education, Jiangnan University, Wuxi 214122 (China)

    2008-08-15

    In this paper the functional carbon nanofibers were prepared by the carbonization of ZnO coated PAN nanofibers to expand the potential applications of carbon nanofibers. Polyacrylonitrile (PAN) nanofibers were obtained by electrospinning. The electrospun PAN nanofibers were then used as substrates for depositing the functional layer of zinc oxide (ZnO) on the PAN nanofiber surfaces by sol-gel technique. The effects of coating, pre-oxidation and carbonization on the surface morphology and structures of the nanofibers were characterized by X-ray diffraction (XRD), Fourier transform infrared (FTIR) and Scanning electron microscopy (SEM), respectively. The results of SEM showed a significant increase of the size of ZnO nanograins on the surface of nanofibers after the treatments of coating, pre-oxidation and carbonization. The observations by SEM also revealed that ZnO nanoclusters were firmly and clearly distributed on the surface of the carbon nanofibers. FTIR examination also confirmed the deposition of ZnO on the surface of carbon nanofibers. The XRD analysis indicated that the crystal structure of ZnO nanograins on the surface of carbon nanofibers.

  6. Plasma Treatment of Carbon Nanotubes Applied to Improve the High Performance of Carbon Nanofiber Supercapacitors

    International Nuclear Information System (INIS)

    Chang, Wei-Min; Wang, Cheng-Chien; Chen, Chuh-Yung

    2015-01-01

    Graphical abstract: This article focused on improving conductivity of carbon nanofibers (CNFs) by added plasma-treatment carbon nanotubes (CNTs). The plasma modification method avoided the destruction of the length and structure of the CNTs and maintained their good electrical properties. Through this method, the relation between conductivity and surface activity site of CNFs was investigated. The results shown that he CNTs-MA added to the CNFs successfully maintained the activity sites on the surface of the CNFs and provide a good electric network to enhance the supercapacitor performance of the CNFs. - Highlights: • The plasma modification method avoided the destruction of the length and structure of the CNTs and maintained their good electrical properties. • The highest conductivity of the CNTs-MA/CNF was 5.2 s/cm at 2.5 wt.% of CNTs-MA addition. It was increased to 8.7 time. • The CNTs-MA added to the CNFs successfully maintained the activity sites on the surface of the CNFs and provide a good electric network to enhance the supercapacitor performance of the CNFs. The highest capacitance was 382 F/g. - Abstract: Plasma-treatment carbon nanotubes (CNTs) grafted with maleic anhydride (MA) were embedded in polyacryonitrile nanofibers via electrospinning and subsequently carbonizated at 800 °C to fabricate carbon nanofibers (CNFs). The grafted degree of MA on CNTs (CNTs-MA) was determined via Fourier transform infrared spectroscopy and X-ray photoelectron spectroscopy. The morphology, surface composition and conductivity of the CNTs-MA/CNF were characterized using electron microscopy, X-ray photoelectron and electrochemical impedance spectroscopy, respectively. CNTs-MA not only affected the conductivity of the CNFs but also the types of the nitrogen functional groups that could be represented as active sites on the CNFs to enhance the performance of the supercapacitors. When 2.5 wt.% CNTs-MA was embedded in the CNFs, the highest conductivity was obtained at

  7. Pulsed laser dewetting of nickel catalyst for carbon nanofiber growth

    International Nuclear Information System (INIS)

    Guan, Y F; Pearce, R C; Simpson, M L; Rack, P D; Melechko, A V; Hensley, D K

    2008-01-01

    We present a pulsed laser dewetting technique that produces single nickel catalyst particles from lithographically patterned disks for subsequent carbon nanofiber growth through plasma enhanced chemical vapor deposition. Unlike the case for standard heat treated Ni catalyst disks, for which multiple nickel particles and consequently multiple carbon nanofibers (CNFs) are observed, single vertically aligned CNFs could be obtained from the laser dewetted catalyst. Different laser dewetting parameters were tested in this study, such as the laser energy density and the laser processing time measured by the total number of laser pulses. Various nickel disk radii and thicknesses were attempted and the resultant number of carbon nanofibers was found to be a function of the initial disk dimension and the number of laser pulses

  8. Improved infiltration of stem cells on electrospun nanofibers

    International Nuclear Information System (INIS)

    Shabani, Iman; Haddadi-Asl, Vahid; Seyedjafari, Ehsan; Babaeijandaghi, Farshad; Soleimani, Masoud

    2009-01-01

    Nanofibrous scaffolds have been recently used in the field of tissue engineering because of their nano-size structure which promotes cell attachment, function, proliferation and infiltration. In this study, nanofibrous polyethersulfone (PES) scaffolds was prepared via electrospinning. The scaffolds were surface modified by plasma treatment and collagen grafting. The surface changes then investigated by contact angle measurements and FTIR-ATR. The results proved grafting of the collagen on nanofibers surface and increased hydrophilicity after plasma treatment and collagen grafting. The cell interaction study was done using stem cells because of their ability to differentiate to different kinds of cell lines. The cells had normal morphology on nanofibers and showed very high infiltration through collagen grafted PES nanofibers. This infiltration capability is very useful and needed to make 3D scaffolds in tissue engineering.

  9. Uniaxially aligned ceramic nanofibers obtained by chemical mechanical processing

    Energy Technology Data Exchange (ETDEWEB)

    Tararam, R. [Univ Estadual Paulista – UNESP – Instituto de Química, Rua Prof. Francisco Degni n° 55, CEP 14800-900 Araraquara, SP (Brazil); Foschini, C.R. [Univ Estadual Paulista – UNESP – Faculdade de Engenharia de Bauru, Dept. de Eng. Mecanica, Av. Eng. Luiz Edmundo C. Coube 14-01, CEP 17033-360 Bauru, SP (Brazil); Destro, F.B. [Univ Estadual Paulista – UNESP – Faculdade de Engenharia de Guaratinguetá, Guaratinguetá 12516-410, SP (Brazil); Simões, A.Z., E-mail: alezipo@yahoo.com [Univ Estadual Paulista – UNESP – Faculdade de Engenharia de Guaratinguetá, Guaratinguetá 12516-410, SP (Brazil); Longo, E.; Varela, J.A. [Univ Estadual Paulista – UNESP – Instituto de Química, Rua Prof. Francisco Degni n° 55, CEP 14800-900 Araraquara, SP (Brazil)

    2014-08-01

    For this study, we investigated a simple method to generate well aligned nanofibers over large areas using an organic polymer stretched over the substrate surface With this method, ZnO and CuO 3D parallel nanowire arrays were successfully prepared by calcinations of the polymer fibers. X-ray diffraction (XRD) analysis revealed that the copper oxide has a monoclinic structure while the zinc oxide has a hexagonal structure. Scanning electron microscopy (SEM) analysis showed ceramic nanofibers with an average diameter of 120 nm which were composed of small nanoparticles which are 10 nm in diameter. The ability to obtain uniaxially aligned nanofibers reveals a range of interesting properties with potential applications for sensors, catalysts and energy technologies.

  10. Bubble-electrospinning: a novel method for making nanofibers

    International Nuclear Information System (INIS)

    Liu, Y; He, J-H; Yu, J-Y

    2008-01-01

    Nanofibers produced by electrospinning are already being used in a vast array of products in many industries. However, the volume of production of nanofibers has been being a bottleneck restricting their applications. In this work we reported a novel method to fabricate continuous and uniform nanofibers by electrospinning using an aerated polymer solution in an electric field. Multiple jets, which were a prerequisite for increasing the volume of production, were found in this electrospinning process. The morphology of the deposited fibers was straight, coiled and helix observed by a scanning electron microscope (SEM) and an optical microscopy. The results showed that the product of this process was similar to that of a traditional electrospinning process and illustrated a good prospect of application

  11. Modeling and simulation of axisymmetric coating growth on nanofibers

    International Nuclear Information System (INIS)

    Moore, K.; Clemons, C. B.; Kreider, K. L.; Young, G. W.

    2007-01-01

    This work is a modeling and simulation extension of an integrated experimental/modeling investigation of a procedure to coat nanofibers and core-clad nanostructures with thin film materials using plasma enhanced physical vapor deposition. In the experimental effort, electrospun polymer nanofibers are coated with metallic materials under different operating conditions to observe changes in the coating morphology. The modeling effort focuses on linking simple models at the reactor level, nanofiber level, and atomic level to form a comprehensive model. The comprehensive model leads to the definition of an evolution equation for the coating free surface. This equation was previously derived and solved under a single-valued assumption in a polar geometry to determine the coating morphology as a function of operating conditions. The present work considers the axisymmetric geometry and solves the evolution equation without the single-valued assumption and under less restrictive assumptions on the concentration field than the previous work

  12. Functionalized carbon nanotubes and nanofibers for biosensing applications

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jun; Lin, Yuehe

    2008-07-30

    This review summarizes the recent advances of carbon nanotube (CNT) and carbon nanofiber (CNF)-based electrochemical biosensors with an emphasis on the applications of CNTs. Carbon nanotubes and carbon nanofibers have unique electric, electrocatalytic, and mechanical properties which make them efficient materials for the use in electrochemical biosensor development. In this article, the functionalization of CNTs for biosensors is simply discussed. The electrochemical biosensors based on CNT and their various applications, e.g., measurement of small biological molecules and environmental pollutants, detection of DNA, and immunosensing of disease biomarkers, are reviewed. Moreover, the development of carbon nanofiber-based electrochemical biosensors and their applications are outlined. Finally, some challenges are discussed in the conclusion.

  13. Facile Synthesis of Coaxial CNTs/MnOx-Carbon Hybrid Nanofibers and Their Greatly Enhanced Lithium Storage Performance.

    Science.gov (United States)

    Yang, Zunxian; Lv, Jun; Pang, Haidong; Yan, Wenhuan; Qian, Kun; Guo, Tailiang; Guo, Zaiping

    2015-12-01

    Carbon nanotubes (CNTs)/MnOx-Carbon hybrid nanofibers have been successfully synthesized by the combination of a liquid chemical redox reaction (LCRR) and a subsequent carbonization heat treatment. The nanostructures exhibit a unique one-dimensional core/shell architecture, with one-dimensional CNTs encapsulated inside and a MnOx-carbon composite nanoparticle layer on the outside. The particular porous characteristics with many meso/micro holes/pores, the highly conductive one-dimensional CNT core, as well as the encapsulating carbon matrix on the outside of the MnOx nanoparticles, lead to excellent electrochemical performance of the electrode. The CNTs/MnOx-Carbon hybrid nanofibers exhibit a high initial reversible capacity of 762.9 mAhg(-1), a high reversible specific capacity of 560.5 mAhg(-1) after 100 cycles, and excellent cycling stability and rate capability, with specific capacity of 396.2 mAhg(-1) when cycled at the current density of 1000 mAg(-1), indicating that the CNTs/MnOx-Carbon hybrid nanofibers are a promising anode candidate for Li-ion batteries.

  14. Stability of β-carotene in polyethylene oxide electrospun nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Peinado, I., E-mail: irpeipar@upvnet.upv.es [Free University of Bolzano, Piazza Università 5, 39100 Bolzano (Italy); Mason, M.; Romano, A. [Free University of Bolzano, Piazza Università 5, 39100 Bolzano (Italy); Biasioli, F. [Department of Food Quality and Nutrition, Research and Innovation Centre, Fondazione Edmund Mach (FEM), via E. Mach 1, 38010 San Michele all ‘Adige, TN (Italy); Scampicchio, M., E-mail: matteo.scampicchio@unibz.it [Free University of Bolzano, Piazza Università 5, 39100 Bolzano (Italy)

    2016-05-01

    Highlights: • β-carotene was incorporated into PEO-nanofibers by electrospinning. • Properties of the fibers were analyzed by SEM, color analysis, and DSC. • TGA coupled to PTR–ms resulted promising to online-monitoring thermal degradation. • Thermal stability of βc increased after encapsulation into the PEO-nanofibers. - Abstract: β-carotene (βc) was successfully incorporated into electrospun nanofibers of poly-(ethylene oxide) (PEO) with the aim of prolonging its shelf life and thermal stability. The physical and thermal properties of the βc-PEO-nanofibers were determined by scanning electron microscopy (SEM), color analysis, and differential scanning calorimetry (DSC). The nanofibers of PEO and βc-PEO exhibited average fiber diameters of 320 ± 46 and 230 ± 21 nm, with colorimetric coordinates L* = 95.7 ± 2.4 and 89.4 ± 4.6 and b* = −0.5 ± 0.1 and 6.2 ± 3.0 respectively. Thermogravimetric analysis coupled with Proton Transfer–Mass Spectroscopy (TGA/PTR–ms) demonstrated that coated βc inside PEO nanofibers increased thermal stability when compared to standard βc in powder form. In addition, β-carotene in the membranes showed higher stability during storage when compared with β-carotene in solution with a decrease in concentration of 57 ± 4% and 70 ± 2% respectively, thus should extend the shelf life of this compound. Also, TGA coupled with PTR–MS resulted in a promising technique to online-monitoring thermal degradation.

  15. Polyaniline emeraldine base nanofibers as a radiostabilizing agent for PMMA

    International Nuclear Information System (INIS)

    Araujo, Patricia L.B.; Ferreira, Carlas C.; Araujo, Elmo S.

    2007-01-01

    Polyaniline (PANI) presents antioxidant and radical-scavenging properties. Substances having these characteristics are good candidates for radioprotecting agents. Some studies have also shown results pointing out to biocompatibility and biodegradability of PANI. These characteristics are desirable for substances in contact with biological tissues and have important implications for inclusion of PANI in physical mixtures with conventional radiosterilizable polymers. In this work, nanofibers of polyaniline emeraldine doped with (±)-camphor-10-sulfonic acid (PANI-(±)-CSA) were prepared by self-assembly method. Polyaniline emeraldine base (PANI-EB) nanofibers were obtained after dedoping with NH 4 OH and used as additives in films of commercial poly (methyl methacrylate) (PMMA). In order to assess possible radiostabilizing effects of PANI-EB and its aniline monomer (An) on the PMMA matrix, films containing 0.075 and 0.15% (wt/wt) of these substances were submitted to gamma irradiation from 25 to 75 kGy doses. Variation on viscosity-average molar mass (Mv) of the PMMA matrix at 25 kGy dose showed that samples containing An and PANI-EB nanofibers in amounts of 0.15% (wt/wt) underwent less degradation than control sample. When nanofibers were used as additives, no measurable variation of Mv could be detected in PMMA samples at this dose. At 75 kGy, all composites containing PANI-EB nanofibers underwent less degradation than control samples, suggesting that these additives are able to retain their action at doses higher than standard sterilization dose. These evidences show that PANI-EB nanofibers could be useful additives in commercial PMMA used in medical applications. FTIR spectroscopic characterization and scanning electron microscopy (SEM) of PANI samples were also performed. (author)

  16. Treated Carbon Nanofibers for Storing Energy in Aqueous KOH

    Science.gov (United States)

    Firsich, David W.

    2004-01-01

    A surface treatment has been found to enhance the performances of carbon nanofibers as electrode materials for electrochemical capacitors in which aqueous solutions of potassium hydroxide are used as the electrolytes. In the treatment, sulfonic acid groups are attached to edge plane sites on carbon atoms. The treatment is applicable to a variety of carbon nanofibers, including fibrils and both single- and multiple-wall nanotubes. The reason for choosing nanofibers over powders and other forms of carbon is that nanofibers offer greater power features. In previous research, it was found that the surface treatment of carbon nanofibers increased energy-storage densities in the presence of acid electrolytes. Now, it has been found that the same treatment increases energy-storage densities of carbon nanofibers in the presence of alkaline electrolytes when the carbon is paired with a NiOOH electrode. This beneficial effect varies depending on the variety of carbon substrate to which it is applied. It has been conjectured that the sulfonic acid groups, which exist in a deprotonated state in aqueous KOH solutions, undergo reversible electro-chemical reactions that are responsible for the observed increases in energystorage capacities. The increases can be considerable: For example, in one case, nanofibers exhibited a specific capacitance of 34 Farads per gram before treatment and 172 Farads per gram (an increase of about 400 percent) after treatment. The most promising application of this development appears to lie in hybrid capacitors, which are devices designed primarily for storing energy. These devices are designed to be capable of (1) discharge at rates greater than those of batteries and (2) storing energy at densities approaching those of batteries. A hybrid capacitor includes one electrode like that of a battery and one electrode like that of an electrochemical capacitor. For example, a hybrid capacitor could contain a potassium hydroxide solution as the electrolyte

  17. Thermally driven self-healing using copper nanofiber heater

    Science.gov (United States)

    Lee, Min Wook; Jo, Hong Seok; Yoon, Sam S.; Yarin, Alexander L.

    2017-07-01

    Nano-textured transparent heaters made of copper nanofibers (CuNFs) are used to facilitate accelerated self-healing of bromobutyl rubber (BIIR). The heater and BIIR layer are separately deposited on each side of a transparent flexible polyethylene terephthalate (PET) substrate. A pre-notched crack on the BIIR layer was bridged due to heating facilitated by CuNFs. In the corrosion test, a cracked BIIR layer covered a steel substrate. An accelerated self-healing of the crack due to the transparent copper nanofiber heater facilitated an anti-corrosion protective effect of the BIIR layer.

  18. Engineered Polymer Composites Through Electrospun Nanofiber Coating of Fiber Tows

    Science.gov (United States)

    Kohlman, Lee W.; Bakis, Charles; Williams, Tiffany S.; Johnston, James C.; Kuczmarski, Maria A.; Roberts, Gary D.

    2014-01-01

    Composite materials offer significant weight savings in many aerospace applications. The toughness of the interface of fibers crossing at different angles often determines failure of composite components. A method for toughening the interface in fabric and filament wound components using directly electrospun thermoplastic nanofiber on carbon fiber tow is presented. The method was first demonstrated with limited trials, and then was scaled up to a continuous lab scale process. Filament wound tubes were fabricated and tested using unmodified baseline towpreg material and nanofiber coated towpreg.

  19. Polyamic Acid Nanofibers Produced by Needleless Electro spinning

    International Nuclear Information System (INIS)

    Jirsak, O.; Sanetrnik, F.; Hruza, J.; Chaloupek, J.; Sysel, P.

    2010-01-01

    The polyimide precursor (polyamic acid) produced of 4,4'-oxydiphthalic anhydride and 4,4'-oxydianiline was electrospun using needleless electrospinning method. Nonwoven layers consisting of submicron fibers with diameters in the range about 143-470 nm on the polypropylene spunbond supporting web were produced. Filtration properties of these nanofiber layers on the highly permeable polypropylene support namely filtration effectivity and pressure drop were evaluated. Consequently, these polyamic acid fibers were heated to receive polyimide nanofibers. The imidization process has been studied using IR spectroscopy. Some comparisons with the chemically identical polyimide prepared as the film were made.

  20. Eddy Current Assessment of Engineered Components Containing Nanofibers

    Science.gov (United States)

    Ko, Ray T.; Hoppe, Wally; Pierce, Jenny

    2009-03-01

    The eddy current approach has been used to assess engineered components containing nanofibers. Five specimens with different programmed defects were fabricated. A 4-point collinear probe was used to verify the electrical resistivity of each specimen. The liftoff component of the eddy current signal was used to test two extreme cases with different nano contents. Additional eddy current measurements were also used in detecting a missing nano layer simulating a manufacturing process error. The results of this assessment suggest that eddy current liftoff measurement can be a useful tool in evaluating the electrical properties of materials containing nanofibers.

  1. Synergetic interface between NiO/Ni3S2 nanosheets and carbon nanofiber as binder-free anode for highly reversible lithium storage

    Science.gov (United States)

    Jiang, Jialin; Ma, Chao; Yang, Yinbo; Ding, Jingjing; Ji, Hongmei; Shi, Shaojun; Yang, Gang

    2018-05-01

    A novel heterostructure of NiO/Ni3S2 nanoflake is synthesized and composited with carbon nanofibers (CNF) membrane. NiO/Ni3S2 nanoflakes are homogeneously dispersed in CNF network, herein, NiO/Ni3S2 like leaf and CNF like branch. Carbon nanofibers network efficiently prevents the pulverization and buffers the volume changes of NiO/Ni3S2, meanwhile, NiO/Ni3S2 nanoflakes through the conductive channels of carbon nanofibers own improved Li+ diffusion ability and structural stability. The capacity of NiO/Ni3S2/CNF reaches to 519.2 mA g-1 after 200 cycles at the current density of 0.5 A g-1 while NiO/Ni3S2 fades to 71 mAh g-1 after 40 cycles. Owing to the synergetic structure, the resultant binder-free electrode NiO/Ni3S2/carbon nanofibers shows an excellent reversible lithium storage capability.

  2. Preparation of MnO nanofibers by novel hydrothermal treatment of manganese acetate/PVA electrospun nanofiber mats

    Energy Technology Data Exchange (ETDEWEB)

    Barakat, Nasser A.M. [Chemical Engineering Department, Faculty of Engineering, El-Minia University, El-Minia (Egypt); Center for Healthcare Technology Development, Chonbuk National University, Jeonju 561-756 (Korea, Republic of)], E-mail: nasbarakat@yahoo.com; Park, Soo Jin [Center for Healthcare Technology Development, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Khil, Myung Seob [Department of Textile Engineering, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Kim, Hak Yong [Center for Healthcare Technology Development, Chonbuk National University, Jeonju 561-756 (Korea, Republic of); Department of Textile Engineering, Chonbuk National University, Jeonju 561-756 (Korea, Republic of)], E-mail: khy@chonbuk.ac.kr

    2009-06-15

    In the present study, manganese monoxide (MnO) which is hard to prepare because of the chemical activity of the manganese metal has been synthesized in nanofibrous form. An electrospun manganese acetate/poly(vinyl alcohol) nanofiber mats have been hydrothermally treated by novel strategy. The treatment process was based on producing of water gas (Co and H{sub 2}) to eliminate the polymer and reduced the manganese acetate to manganese monoxide. The process was carried out by heating the dried nanofiber mates at 400 deg. C for 3 h in an especial designed reactor in which a stream of water vapor was passing through a bed of an activated carbon. The obtained physiochemical characterization results indicated that the proposed hydrothermal treatment process does have the ability to produce pure MnO nanofibers with good crystallinity.

  3. Preparation of MnO nanofibers by novel hydrothermal treatment of manganese acetate/PVA electrospun nanofiber mats

    International Nuclear Information System (INIS)

    Barakat, Nasser A.M.; Park, Soo Jin; Khil, Myung Seob; Kim, Hak Yong

    2009-01-01

    In the present study, manganese monoxide (MnO) which is hard to prepare because of the chemical activity of the manganese metal has been synthesized in nanofibrous form. An electrospun manganese acetate/poly(vinyl alcohol) nanofiber mats have been hydrothermally treated by novel strategy. The treatment process was based on producing of water gas (Co and H 2 ) to eliminate the polymer and reduced the manganese acetate to manganese monoxide. The process was carried out by heating the dried nanofiber mates at 400 deg. C for 3 h in an especial designed reactor in which a stream of water vapor was passing through a bed of an activated carbon. The obtained physiochemical characterization results indicated that the proposed hydrothermal treatment process does have the ability to produce pure MnO nanofibers with good crystallinity.

  4. Surface modification of polyvinyl alcohol/malonic acid nanofibers by gaseous dielectric barrier discharge plasma for glucose oxidase immobilization

    Science.gov (United States)

    Afshari, Esmail; Mazinani, Saeedeh; Ranaei-Siadat, Seyed-Omid; Ghomi, Hamid

    2016-11-01

    Polymeric nanofiber prepares a suitable situation for enzyme immobilization for variety of applications. In this research, we have fabricated polyvinyl alcohol (PVA)/malonic acid nanofibers using electrospinning. After fabrication of nanofibers, the effect of air, nitrogen, CO2, and argon DBD (dielectric barrier discharge) plasmas on PVA/malonic acid nanofibers were analysed. Among them, air plasma had the most significant effect on glucose oxidase (GOx) immobilization. Attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectrum analysis and X-ray photoelectron spectroscopy (XPS) results revealed that in case of air plasma modified nanofibers, the carboxyl groups on the surface are increased. The scanning electron microscopy (SEM) images showed that, after GOx immobilization, the modified nanofibers with plasma has retained its nanofiber structure. Finally, we analysed reusability and storage stability of GOx immobilized on plasma modified and unmodified nanofibers. The results were more satisfactory for modified nanofibers with respect to unmodified ones.

  5. Production of green biocellulose nanofibers by Gluconacetobacter xylinus through utilizing the renewable resources of agriculture residues.

    Science.gov (United States)

    Al-Abdallah, Wahib; Dahman, Yaser

    2013-11-01

    The present study demonstrates the ability to produce green biocellulose nanofibers using the renewable resources of agriculture residues. Locally grown wheat straws (WS) were hydrolyzed under different conditions. Their hydrolysates were utilized to produce the nanofibers in separate hydrolysis fermentation process by Gluconacetobacter xylinus strain bacterium. Highest biocellulose production of ~10.6 g/L was achieved with samples that were enzymatically hydrolyzed. Moreover, acidic hydrolyzed WS produced up to 9.7 g/L, with total sugar concentrations in culture media of 43 g/L. Generally, enzymatic hydrolysis of WS resulted in more total sugar concentration than the acidic hydrolysis (i.e., 52.12 g/L), while water hydrolysis produced the least. This can be related to utilizing Xylanase in addition to Cellulase and Beta-glucosidase that helps to hydrolyse WS dry basis of cellulose and hemicelluloses. Sugar mixtures produced under all hydrolysis conditions were mainly composed of glucose and xylose with average percentages of 56 and 28 %, respectively. Acidic hydrolysis at higher acid concentration, as well as soaking WS in the acidic solution for longer time, improved the total sugar concentration in the culture media by 18 %. Conducting thermal treatment at more intense conditions of higher temperature or heating time improved the total sugar produced with acidic hydrolysis. These conditions, however, resulted in further production of furfural, which considerably affected bacterial cells proliferation. This resulted in lowest sugar consumption in the range of 62-64 % that affected final BC production.

  6. Fabrication of ultrafine manganese oxide-decorated carbon nanofibers for high-performance electrochemical capacitors

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Ying; Lee, Sungsik; Brown, Dennis E.; Zhao, Hairui; Li, Xinsong; Jiang, Daqiang; Hao, Shijie; Zhao, Yongxiang; Cong, Daoyong; Zhang, Xin; Ren, Yang

    2016-09-01

    Ultrafine manganese oxide-decorated carbon nanofibers (MnOn-CNF) as a new type of electrode materials are facilely fabricated by direct conversion of Mn, Zn-trimesic acid (H3BTC) metal organic framework fibers (Mn-ZnBTC). The construction and evolution of Mn-ZnBTC precursors are investigated by SEM and in situ high-energy XRD. The manganese oxides are highly dispersed onto the porous carbon nanofibers formed simultaneously, verified by TEM, X-ray absorption fine structure (XAFS), Raman, ICP-AES and N2 adsorption techniques. As expected, the resulting MnOn-CNF composites are highly stable, and can be cycled up to 5000 times with a high capacitance retention ratio of 98% in electrochemical capacitor measurements. They show a high capacitance of up to 179 F g–1 per mass of the composite electrode, and a remarkable capacitance of up to 18290 F g–1 per active mass of the manganese(IV) oxide, significantly exceeding the theoretical specific capacitance of manganese(IV) oxide (1370 F g–1). The maximum energy density is up to 19.7 Wh kg–1 at the current density of 0.25 A g–1, even orders higher than those of reported electric double-layer capacitors and pseudocapacitors. The excellent capacitive performance can be ascribed to the joint effect of easy accessibility, high porosity, tight contact and superior conductivity integrated in final MnOn-CNF composites.

  7. Effect of micropatterning induced surface hydrophobicity on drug release from electrospun cellulose acetate nanofibers

    Science.gov (United States)

    Adepu, Shivakalyani; Gaydhane, Mrunalini K.; Kakunuri, Manohar; Sharma, Chandra S.; Khandelwal, Mudrika; Eichhorn, Stephen J.

    2017-12-01

    Sustained release and prevention of burst release for low half-life drugs like Diclofenac sodium is crucial to prevent drug related toxicity. Electrospun nanofibers have emerged recently as potential carrier materials for controlled and sustained drug release. Here, we present a facile method to prevent burst release by tuning the surface wettability through template assisted micropatterning of drug loaded electrospun cellulose acetate (CA) nanofibers. A known amount of drug (Diclofenac sodium) was first mixed with CA and then electrospun in the form of a nanofabric. This as-spun network was hydrophilic in nature. However, when electrospinning was carried out through non-conducting templates, viz nylon meshes with 50 and 100 μm size openings, two kinds of hydrophobic micro-patterned CA nanofabrics were produced. In vitro transdermal testing of our nanofibrous mats was carried out; these tests were able to show that it would be possible to create a patch for transdermal drug release. Further, our results show that with optimized micro-patterned dimensions, a zero order sustained drug release of up to 12 h may be achieved for the transdermal system when compared to non-patterned samples. This patterning caused a change in the surface wettability, to a hydrophobic surface, resulting in a controlled diffusion of the hydrophilic drug. Patterning assisted in controlling the initial burst release, which is a significant finding especially for low half-life drugs.

  8. Facile synthesis of NiS anchored carbon nanofibers for high-performance supercapacitors

    Science.gov (United States)

    Xu, Jinling; Zhang, Li; Xu, Guancheng; Sun, Zhipeng; Zhang, Chi; Ma, Xin; Qi, Chunling; Zhang, Lu; Jia, Dianzeng

    2018-03-01

    Transition metal sulfide compounds with carbon materials are promising for high-performance supercapacitors. Carbon nanofibers (CNFs) wrapped with NiS nanoparticles were herein obtained through electrospinning and calcination. NiS nanoparticles in composite nanofibers are covered by a layer of graphitic carbon, which not only increase the conductivity but also provide active regions for nanoparticle growth to prevent aggregation. The CNFs-NiS electrode has high specific capacity of 177.1 mAh g-1 at 1 A g-1 (0.41 mAh cm-2 at a current density of 2.3 mA cm-2) and long-term cycling stability, with 88.7% capacitance retention after 5000 cycles. The excellent electrochemical activity may be attributed to the accessible specific surface, unique porous structure of CNFs and high specific capacitance of NiS. In addition, the asymmetric supercapacitor has an enhanced volumetric energy density of 13.32 mWh cm-3 at a volumetric power density of 180 mW cm-3 and high cycling stability, with 89.5% capacitance retention after 5000 cycles. It also successfully lights up a light-emitting diode. The CNFs-NiS composite has significant potential applications in supercapacitor.

  9. Electrospun polymethylacrylate nanofibers membranes for quasi-solid-state dye sensitized solar cells

    Directory of Open Access Journals (Sweden)

    M. Fathy

    2016-06-01

    Full Text Available Polymethylacrylate (PMA nanofibers membranes are fabricated by electrospinning technique and applied to the polymer matrix in quasi-solid-state electrolytes for dye sensitized solar cells (DSSCs. There is no previous studies reporting the production of PMA nanofibers. The electrospinning parameters such as polymer concentration, applied voltage, feed rate, tip to collector distance and solvent were optimized. Electrospun PMA fibrous membrane with average fiber diameter of 350 nm was prepared from a 10 wt% solution of PMA in a mixture of acetone/N,N-dimethylacetamide (6:4 v/v at an applied voltage of 20 kV. It was then activated by immersing it in 0.5 M LiI, 0.05 M I2, and 0.5 M 4-tert-butylpyridine in 3-methoxyproponitrile to obtain the corresponding membrane electrolyte with an ionic conductivity of 2.4 × 10−3 S cm−1 at 25 °C. Dye sensitized solar cells (DSSCs employing the quasi solid-state electrolyte have an open-circuit voltage (Voc of 0.65 V and a short circuit current (Jsc of 6.5 mA cm−2 and photoelectric energy conversion efficiency (η of 1.4% at an incident light intensity of 100 mW cm−2.

  10. Lysozyme-immobilized electrospun PAMA/PVA and PSSA-MA/PVA ion-exchange nanofiber for wound healing.

    Science.gov (United States)

    Tonglairoum, Prasopchai; Ngawhirunpat, Tanasait; Rojanarata, Theerasak; Opanasopit, Praneet

    2014-08-27

    Abstract This research was aimed to develop the lysozyme immobilized ion-exchange nanofiber mats for wound healing. To promote the healing process, the PSSA-MA/PVA and PAMA ion-exchange nanofiber mats were fabricated to mimic the extracellular matrix structure using electrospinning process followed by thermally crosslinked. Lysozyme was immobilized on the ion-exchane nanofibers by an adsorption method. The ion-exchange nanofibers were investigated using SEM, FTIR and XRPD. Moreover, the lysozyme-immobilized ion-exchange nanofibers were further investigated for lysozyme content and activity, lysozyme release and wound healing activity. The fiber diameters of the mats were in the nanometer range. Lysozyme was gradually absorbed into the PSSA-MA/PVA nanofiber with higher extend than that is absorbed on the PAMA/PVA nanofiber and exhibited higher activity than lysozyme-immobilized PAMA/PVA nanofiber. The total contents of lysozyme on the PSSA-MA/PVA and PAMA/PVA nanofiber were 648 and 166 µg/g, respectively. FTIR and lysozyme activity results confirmed the presence of lysozyme on the nanofiber mats. The lysozyme was released from the PSSA-MA/PVA and PAMA/PVA nanofiber in the same manner. The lysozyme-immobilized PSSA-MA/PVA nanofiber mats and lysozyme-immobilized PAMA/PVA nanofiber mats exhibited significantly faster healing rate than gauze and similar to the commercial antibacterial gauze dressing. These results suggest that these nanofiber mats could provide the promising candidate for wound healing application.

  11. Incorporation of functionalized gold nanoparticles into nanofibers for enhanced attachment and differentiation of mammalian cells

    Directory of Open Access Journals (Sweden)

    Jung Dongju

    2012-06-01

    Full Text Available Abstract Background Electrospun nanofibers have been widely used as substrata for mammalian cell culture owing to their structural similarity to natural extracellular matrices. Structurally consistent electrospun nanofibers can be produced with synthetic polymers but require chemical modification to graft cell-adhesive molecules to make the nanofibers functional. Development of a facile method of grafting functional molecules on the nanofibers will contribute to the production of diverse cell type-specific nanofiber substrata. Results Small molecules, peptides, and functionalized gold nanoparticles were successfully incorporated with polymethylglutarimide (PMGI nanofibers through electrospinning. The PMGI nanofibers functionalized by the grafted AuNPs, which were labeled with cell-adhesive peptides, enhanced HeLa cell attachment and potentiated cardiomyocyte differentiation of human pluripotent stem cells. Conclusions PMGI nanofibers can be functionalized simply by co-electrospinning with the grafting materials. In addition, grafting functionalized AuNPs enable high-density localization of the cell-adhesive peptides on the nanofiber. The results of the present study suggest that more cell type-specific synthetic substrata can be fabricated with molecule-doped nanofibers, in which diverse functional molecules are grafted alone or in combination with other molecules at different concentrations.

  12. Osteoinductive peptide-functionalized nanofibers with highly ordered structure as biomimetic scaffolds for bone tissue engineering.

    Science.gov (United States)

    Gao, Xiang; Zhang, Xiaohong; Song, Jinlin; Xu, Xiao; Xu, Anxiu; Wang, Mengke; Xie, Bingwu; Huang, Enyi; Deng, Feng; Wei, Shicheng

    2015-01-01

    The construction of functional biomimetic scaffolds that recapitulate the topographical and biochemical features of bone tissue extracellular matrix is now of topical interest in bone tissue engineering. In this study, a novel surface-functionalized electrospun polycaprolactone (PCL) nanofiber scaffold with highly ordered structure was developed to simulate the critical features of native bone tissue via a single step of catechol chemistry. Specially, under slightly alkaline aqueous solution, polydopamine (pDA) was coated on the surface of aligned PCL nanofibers after electrospinning, followed by covalent immobilization of bone morphogenetic protein-7-derived peptides onto the pDA-coated nanofiber surface. Contact angle measurement, Raman spectroscopy, and X-ray photoelectron spectroscopy confirmed the presence of pDA and peptides on PCL nanofiber surface. Our results demonstrated that surface modification with osteoinductive peptides could improve cytocompatibility of nanofibers in terms of cell adhesion, spreading, and proliferation. Most importantly, Alizarin Red S staining, quantitative real-time polymerase chain reaction, immunostaining, and Western blot revealed that human mesenchymal stem cells cultured on aligned nanofibers with osteoinductive peptides exhibited enhanced osteogenic differentiation potential than cells on randomly oriented nanofibers. Furthermore, the aligned nanofibers with osteoinductive peptides could direct osteogenic differentiation of human mesenchymal stem cells even in the absence of osteoinducting factors, suggesting superior osteogenic efficacy of biomimetic design that combines the advantages of osteoinductive peptide signal and highly ordered nanofibers on cell fate decision. The presented peptide-decorated bone-mimic nanofiber scaffolds hold a promising potential in the context of bone tissue engineering.

  13. Formation of high aspect ratio polyamide-6 nanofibers via electrically induced double layer during electrospinning

    International Nuclear Information System (INIS)

    Nirmala, R.; Nam, Ki Taek; Park, Soo-Jin; Shin, Yu-Shik; Navamathavan, R.; Kim, Hak Yong

    2010-01-01

    In the present study, the formation of high aspect ratio nanofibers in polyamide-6 was investigated as a function of applied voltage ranging from 15 to 25 kV using electrospinning technique. All other experimental parameters were kept constant. The electrospun polyamide-6 nanofibers were characterized by field-emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM) and matrix-assisted laser desorption ionization time-of-flight (MALDI-TOF). FE-SEM images of polyamide-6 nanofibers showed that the diameter of the electrospun fiber was decreased with increasing applied voltage. At the critical applied voltage, the polymer solution was completely ionized to form the dense high aspect ratio nanofibers in between the main nanofibers. The diameter of the polyamide-6 nanofibers was observed to be in the range of 75-110 nm, whereas the high aspect ratio structures consisted of regularly distributed very fine nanofibers with diameters of about 9-28 nm. Trends in fiber diameter and diameter distribution were discussed for the high aspect ratio nanofibers. TEM results revealed that the formation of double layers in polyamide-6 nanofibers and then split-up into ultrafine fibers. The electrically induced double layer in combination with the polyelectrolytic nature of solution is proposed as the suitable mechanisms for the formation of high aspect ratio nanofibers in polyamide-6.

  14. Influence of polyvinyl alcohol amount on producing in situ photo-crosslinked thioamide functionalized nanofiber membranes

    Directory of Open Access Journals (Sweden)

    Zeytuncu Bihter

    2015-01-01

    Full Text Available Poly(vinyl alcohol/maleic anhydride/acryloyl thioamide monomer (PVA/MA/ATM photo-cured nanofiber membranes and pure PVA nanofiber membranes were produced by electrospinning technique. In situ UV radiation was applied during the electrospinning in order to provide polymerization during the jet flight and promote crosslinking of ATM and MA with PVA. The cross-linking was examined by Fourier-transform infrared spectroscopy (FTIR. The morphology and thermal behavior of electrospun nanofiber were characterized by scanning electron microscope (SEM and thermogravimetric analysis (TGA, respectively. The surface area of nanofiber membranes was measured by Brunauer-Emmert-Teller (BET analysis. Furthermore, water durability test was examined. Water durability test demonstrated that in situ photo-cured PVA/MA/ATM nanofiber membrane had the least average mass loss. The surface areas of PVA/MA/ATM nanofiber membranes were 160-280 m2/g. The surface area and diameter of PVA/MA/ATM nanofibers decreased as the PVA content increased. The diameter of nanofibers was obtained less than 100 nm. The results showed that the water-insoluble nanofiber membranes with better chemical and thermal resistance were obtained. These nanofiber membranes may be a promising candidate for the usage of water treatment.

  15. Preparation of Ag/HBP/PAN Nanofiber Web and Its Antimicrobial and Filtration Property

    Directory of Open Access Journals (Sweden)

    Li-Rong Yao

    2016-01-01

    Full Text Available To widen the application of nanofibers web in the field of medical health materials, a new Ag/amino-terminated hyperbranched polymer (HBP/polyacrylonitrile (PAN nanofiber web with excellent antimicrobial activity and filtration property was produced with Ag/HBP dispersion solution and PAN nanofiber. Ag/HBP dispersion solution was prepared with HBP as reducer and stabilizer, and Ag/HBP/PAN nanofiber was prepared by modifying electrospun PAN nanofiber with Ag/HBP aqueous solution. The characterization results showed that spherical Ag nanoparticles were prepared and they had a narrow distribution in HBP aqueous solution. The results of Ag/HBP/PAN nanofiber characterized with SEM and EDS showed that the content of silver nanoparticles on the surface of PAN nanofiber was on the increase when the treating temperature rose. The bacterial reduction rates of HBP-treated PAN nanofiber against S. aureus and E. coli were about 89%, while those of the Ag/HBP/PAN nanofiber against S. aureus and E. coli were 99.9% and 99.96%, respectively, due to the cooperative effects from the amino groups in HBP and Ag nanoparticles. Moreover, the small pores and high porosity in Ag/HBP/PAN nanofiber web resulted in high filtration efficiency (99.9% for removing smaller particles (0.1 μm~0.7 μm, which was much higher than that of the gauze mask.

  16. Physico-chemical/biological properties of tripolyphosphate cross-linked chitosan based nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Sarkar, Soumi Dey [School of Medical Science and Technology, Indian Institute of Technology Kharagpur, Kharagpur-721302 (India); Farrugia, Brooke L.; Dargaville, Tim R. [Institute of Health and Biomedical Innovation, Queensland University of Technology, Kelvin Groove, Queensland-4059 (Australia); Dhara, Santanu, E-mail: sdhara@smst.iitkgp.ernet.in [School of Medical Science and Technology, Indian Institute of Technology Kharagpur, Kharagpur-721302 (India)

    2013-04-01

    In this study, chitosan-PEO blend, prepared in a 15 M acetic acid, was electrospun into nanofibers (∼ 78 nm diameter) with bead free morphology. While investigating physico-chemical parameters of blend solutions, effect of yield stress on chitosan based nanofiber fabrication was clearly evidenced. Architectural stability of nanofiber mat in aqueous medium was achieved by ionotropic cross-linking of chitosan by tripolyphosphate (TPP) ions. The TPP cross-linked nanofiber mat showed swelling up to ∼ 300% in 1 h and ∼ 40% degradation during 30 day study period. 3T3 fibroblast cells showed good attachment, proliferation and viability on TPP treated chitosan based nanofiber mats. The results indicate non-toxic nature of TPP cross-linked chitosan based nanofibers and their potential to be explored as a tissue engineering matrix. - Highlights: ► Chitosan based nanofiber fabrication through electrospinning. ► Roles of solution viscosity and yield stress on spinnability of chitosan evidenced. ► Tripolyphosphate (TPP) cross-linking rendered structural stability to nanofibers. ► TPP cross-linking also improved cellular response on chitosan based nanofibers. ► Thus, chitosan based nanofibers are suitable for tissue engineering application.

  17. Physico-chemical/biological properties of tripolyphosphate cross-linked chitosan based nanofibers

    International Nuclear Information System (INIS)

    Sarkar, Soumi Dey; Farrugia, Brooke L.; Dargaville, Tim R.; Dhara, Santanu

    2013-01-01

    In this study, chitosan-PEO blend, prepared in a 15 M acetic acid, was electrospun into nanofibers (∼ 78 nm diameter) with bead free morphology. While investigating physico-chemical parameters of blend solutions, effect of yield stress on chitosan based nanofiber fabrication was clearly evidenced. Architectural stability of nanofiber mat in aqueous medium was achieved by ionotropic cross-linking of chitosan by tripolyphosphate (TPP) ions. The TPP cross-linked nanofiber mat showed swelling up to ∼ 300% in 1 h and ∼ 40% degradation during 30 day study period. 3T3 fibroblast cells showed good attachment, proliferation and viability on TPP treated chitosan based nanofiber mats. The results indicate non-toxic nature of TPP cross-linked chitosan based nanofibers and their potential to be explored as a tissue engineering matrix. - Highlights: ► Chitosan based nanofiber fabrication through electrospinning. ► Roles of solution viscosity and yield stress on spinnability of chitosan evidenced. ► Tripolyphosphate (TPP) cross-linking rendered structural stability to nanofibers. ► TPP cross-linking also improved cellular response on chitosan based nanofibers. ► Thus, chitosan based nanofibers are suitable for tissue engineering application

  18. A nanofiber functionalized with dithizone by co-electrospinning for lead (II) adsorption from aqueous media

    International Nuclear Information System (INIS)

    Deng, Jianjun; Kang, Xuejun; Chen, Liqin; Wang, Yu; Gu, Zhongze; Lu, Zuhong

    2011-01-01

    Highlights: ► We fabricated a composite electrospun nanofiber as a selective sorbent for lead (II) in PFSPE. ► The composite nanofiber was functionalized with the dithizone by co-electrospinning of the PS solution containing unbonded dithizone. ► The nanofiber was characterized by scanning electron microscope and IR spectra. ► We applied the nanofiber by packing in a cartridge. ► The nanofiber performed well in the absorption of lead (II) and was applied successfully in aqueous samples. - Abstract: An electrospun nanofiber was utilized as a sorbent in packed fiber solid phase extraction (PFSPE) for selective separation and preconcentration of lead (II). The nanofiber had a polystyrene (PS) backbone, which was functionalized with dithizone (DZ) by co-electrospinning of a PS solution containing DZ. The nanofiber exhibited its performance in a cartridge prepared by packing 5 mg of nanofiber. The nanofiber was characterized by a scanning electron microscope and IR spectra. The diameter of the nanofiber was less than 400 nm. After being activated by 2.0 mol L −1 NaOH aqueous solution, the nanofiber quantitatively sorbed lead (II) at pH 8.5, and the metal ion could be desorbed from it by three times of elution with a small volume of 0.1 mol L −1 HNO 3 aqueous solution. The breakthrough capacity was 16 μg mg −1 . The nanofiber could be used for concentration of lead (II) from water and other aqueous media, such as plasma with stable recovery in a simple and convenient manner.

  19. Electrospun Nanofiber Scaffolds with Gradations in Fiber Organization

    Science.gov (United States)

    Khandalavala, Karl; Jiang, Jiang; Shuler, Franklin D.; Xie, Jingwei

    2015-01-01

    The goal of this protocol is to report a simple method for generating nanofiber scaffolds with gradations in fiber organization and test their possible applications in controlling cell morphology/orientation. Nanofiber organization is controlled with a new fabrication apparatus that enables the gradual decrease of fiber organization in a scaffold. Changing the alignment of fibers is achieved through decreasing deposition time of random electrospun fibers on a uniaxially aligned fiber mat. By covering the collector with a moving barrier/mask, along the same axis as fiber deposition, the organizational structure is easily controlled. For tissue engineering purposes, adipose-derived stem cells can be seeded to these scaffolds. Stem cells undergo morphological changes as a result of their position on the varied organizational structure, and can potentially differentiate into different cell types depending on their locations. Additionally, the graded organization of fibers enhances the biomimicry of nanofiber scaffolds so they more closely resemble the natural orientations of collagen nanofibers at tendon-to-bone insertion site compared to traditional scaffolds. Through nanoencapsulation, the gradated fibers also afford the possibility to construct chemical gradients in fiber scaffolds, and thereby further strengthen their potential applications in fast screening of cell-materials interaction and interfacial tissue regeneration. This technique enables the production of continuous gradient scaffolds, but it also can potentially produce fibers in discrete steps by controlling the movement of the moving barrier/mask in a discrete fashion. PMID:25938562

  20. Functionalized carbon nanofibers as solid acid catalysts for transesterification

    NARCIS (Netherlands)

    Stellwagen, D.R.; van der Klis, Frits; van Es, D.S.; de Jong, K.P.; Bitter, J.H.

    2013-01-01

    Carbon nanofibers (CNFs) were functionalized with aryl sulfonic acid groups using in situ diazonium coupling. The use of diazonium coupling yielded an acidic carbon material, in which the introduced acidic groups are readily accessible to the triglyceride substrate. The material is an efficient

  1. Functionalized carbon nanofibers as solid-acid catalysts for transesterification

    NARCIS (Netherlands)

    Stellwagen, D.R.; Klis, van der F.; Es, van D.S.; Jong, de K.P.; Bitter, J.H.

    2013-01-01

    Carbon nanofibers (CNFs) were functionalized with aryl sulfonic acid groups using in situ diazonium coupling. The use of diazonium coupling yielded an acidic carbon material, in which the introduced acidic groups are readily accessible to the triglyceride substrate. The material is an efficient

  2. Electrospun propolis/polyurethane composite nanofibers for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Jeong In [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of); Pant, Hem Raj, E-mail: hempant@jbnu.ac.kr [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of); Department of Engineering Science and Humanities, Pulchowk Campus, Tribhuvan University, Kathmandu (Nepal); Research Institute for Next Generation, Kalanki, Kathmandu (Nepal); Sim, Hyun-Jaung [Department of Bioactive Material Science, Research Center of Bioactive Material, Chonbuk National University, Jeonju, Chonbuk (Korea, Republic of); Lee, Kang Min [Department of Molecular Biology, College of Natural Science, Chonbuk National University, Jeonju, 561–756 (Korea, Republic of); Kim, Cheol Sang, E-mail: chskim@jbnu.ac.kr [Department of Bio-nano System Engineering, Chonbuk National University, Jeonju 561–756 (Korea, Republic of)

    2014-11-01

    Tissue engineering requires functional polymeric membrane for adequate space for cell migration and attachment within the nanostructure. Therefore, biocompatible propolis loaded polyurethane (propolis/PU) nanofibers were successfully prepared using electrospinning of propolis/PU blend solution. Here, composite nanofibers were subjected to detailed analysis using electron microscopy, FT-IR spectroscopy, thermal gravimetric analysis (TGA), and mechanical properties and water contact angle measurement. FE-SEM images revealed that the composite nanofibers became point-bonded with increasing amounts of propolis in the blend due to its adhesive properties. Incorporation of small amount of propolis through PU matrix could improve the hydrophilicity and mechanical strength of the fibrous membrane. In order to assay the cytocompatibility and cell behavior on the composite scaffolds, fibroblast cells were seeded on the matrix. Results suggest that the incorporation of propolis into PU fibers could increase its cell compatibility. Moreover, composite nanofibers have effective antibacterial activity. Therefore, as-synthesized nanocomposite fibrous mat has great potentiality in wound dressing and skin tissue engineering. - Highlights: • Sufficient amount of propolis is simply loaded through PU fibers. • Propolis increases the hydrophilicity and mechanical properties of PU fibers. • Composite mat shows excellent antibacterial activity. • Small amount of propolis can enhance the cell compatibility of PU fibers.

  3. Surface plasmon polariton propagation in organic nanofiber based plasmonic waveguides

    DEFF Research Database (Denmark)

    Leißner, Till; Lemke, Christoph; Jauernik, Stephan

    2013-01-01

    Plasmonic wave packet propagation is monitored in dielectric-loaded surface plasmon polariton waveguides realized from para-hexaphenylene nanofibers deposited onto a 60 nm thick gold film. Using interferometric time resolved two-photon photoemission electron microscopy we are able to determine...

  4. Reducing bleaching effects in organic nanofibers by coating

    DEFF Research Database (Denmark)

    Tavares, Luciana; Kjelstrup-Hansen, Jakob; Rubahn, Horst-Günter

    Para-hexaphenylene (p-6P) organic nanofibers emit polarized, blue light upon UV excitation with a peak wavelength of the emitted light of 425 nm [1] and a spatially anisotropic distribution of the emitted light [2]. These features could enable future (opto-)electronic applications [3], since...

  5. Nanofibers extraction from palm mesocarp fiber for biodegradable polymers incorporation

    International Nuclear Information System (INIS)

    Kuana, Vanessa A.; Rodrigues, Vanessa B.; Takahashi, Marcio C.; Campos, Adriana de; Sena Neto, Alfredo R.; Mattoso, Luiz H.C.; Marconcini, Jose M.

    2015-01-01

    The palm mesocarp fibers are residues produced by the palm oil industries. The objective of this paper is to determine an efficient treatment to extract crystal cellulose nanofibers from the palm mesocarp fibers to be incorporated in biodegradable polymeric composites. The fibers were saponified, bleached and analyzed with thermal gravimetric analysis, X-ray diffraction, Fourier transform infrared spectroscopy and scanning electron microscopy. (author)

  6. Carbon Nanofibers as Catalyst Support for Noble Metals

    NARCIS (Netherlands)

    Toebes, M.L.

    2004-01-01

    In the quest for new and well-defined support materials for heterogeneous catalysts we explored the potential of carbon nanofibers (CNF). CNF belongs to the by now extensive family of synthetic graphite-like carbon materials with advantageous and tunable physico-chemical properties. Aim of the work

  7. Electrospun propolis/polyurethane composite nanofibers for biomedical applications

    International Nuclear Information System (INIS)

    Kim, Jeong In; Pant, Hem Raj; Sim, Hyun-Jaung; Lee, Kang Min; Kim, Cheol Sang

    2014-01-01

    Tissue engineering requires functional polymeric membrane for adequate space for cell migration and attachment within the nanostructure. Therefore, biocompatible propolis loaded polyurethane (propolis/PU) nanofibers were successfully prepared using electrospinning of propolis/PU blend solution. Here, composite nanofibers were subjected to detailed analysis using electron microscopy, FT-IR spectroscopy, thermal gravimetric analysis (TGA), and mechanical properties and water contact angle measurement. FE-SEM images revealed that the composite nanofibers became point-bonded with increasing amounts of propolis in the blend due to its adhesive properties. Incorporation of small amount of propolis through PU matrix could improve the hydrophilicity and mechanical strength of the fibrous membrane. In order to assay the cytocompatibility and cell behavior on the composite scaffolds, fibroblast cells were seeded on the matrix. Results suggest that the incorporation of propolis into PU fibers could increase its cell compatibility. Moreover, composite nanofibers have effective antibacterial activity. Therefore, as-synthesized nanocomposite fibrous mat has great potentiality in wound dressing and skin tissue engineering. - Highlights: • Sufficient amount of propolis is simply loaded through PU fibers. • Propolis increases the hydrophilicity and mechanical properties of PU fibers. • Composite mat shows excellent antibacterial activity. • Small amount of propolis can enhance the cell compatibility of PU fibers

  8. Phosphopeptide enrichment with inorganic nanofibers prepared by forcespinning technology

    Czech Academy of Sciences Publication Activity Database

    Křenková, Jana; Morávková, J.; Buk, J.; Foret, František

    2016-01-01

    Roč. 1427, JAN (2016), s. 8-15 ISSN 0021-9673 R&D Projects: GA ČR(CZ) GA14-06319S; GA ČR(CZ) GBP206/12/G014 Institutional support: RVO:68081715 Keywords : nanofibers * enrichment * phosphopeptides Subject RIV: CB - Analytical Chemistry , Separation Impact factor: 3.981, year: 2016

  9. Micro-nanofibers with hierarchical structure by bubbfil-spinning

    Directory of Open Access Journals (Sweden)

    Liu Peng

    2015-01-01

    Full Text Available Bubbfil spinning is used to fabricate micro/nanofibers with hierarchical structure. The wall of a polymer film is attenuated unevenly by a blowing air. The burst of the bubble results in film fragments with different thickness, as a result, different sizes of fibers are obtained.

  10. Preparation of Biopolymeric Nanofiber Containing Silica and Antibiotic

    Directory of Open Access Journals (Sweden)

    A. Bagheri Pebdeni

    2016-01-01

    Full Text Available The biocompatible and biodegradable polymer nanofiber with high potential for anti-bacterial coating are used for: multi-functional membranes, tissue engineering, wound dressings, drug delivery, artificial organs, vascular grafts and etc. Electrospinning nanofiber made of scaffolding due to characteristics such as high surface to volume ratio, high porosity and very fine pores are used for a wide range of applications. In this study, polymer composite nanofiber Silica/chitosan/poly (ethylene oxide /cefepime antibiotic synthesis and antibacterial properties will be discussed. The optimum conditions for preparation of electrospun nanofiber were: voltage; 21 kV, feed rate; 0.5 mL/h, nozzle-collector distance; 10 cm, and chitosan/poly(ethylene oxide weight ratio 90:10 and the volume ratio of chitosan/silica is 70:30.  The antibacterial activity of composite scaffolds were tested by agar plate method by two type bacteria including Escherichia coli and Staphylococcus aureus. With the addition of the silica to chitosan, the hybrid was more biodegradable and improves the mechanical properties of biopolymer.

  11. Electrostatic Self-Assembly of Polysaccharides into Nanofibers

    DEFF Research Database (Denmark)

    Mendes, Ana Carina Loureiro; Strohmenger, Timm; Goycoolea, Francisco

    2017-01-01

    In this study, the anionic polysaccharide Xanthan gum (X) was mixed with positively charged Chitosan oligomers (ChO), and used as building blocks, to generate novel nanofibers by electrostatic self-assembly in aqueous conditions. Different concentrations, ionic strength and order of mixing of both...

  12. Silver-functionalized carbon nanofiber composite electrodes for ibuprofen detection

    NARCIS (Netherlands)

    Manea, F.; Motoc, S.; Pop, A.; Remes, A.; Schoonman, J.

    2012-01-01

    The aim of this study is to prepare and characterize two types of silver-functionalized carbon nanofiber (CNF) composite electrodes, i.e., silver-decorated CNF-epoxy and silver-modified natural zeolite-CNF-epoxy composite electrodes suitable for ibuprofen detection in aqueous solution. Ag carbon

  13. Superhydrophobic terpolymer nanofibers containing perfluoroethyl alkyl methacrylate by electrospinning

    Energy Technology Data Exchange (ETDEWEB)

    Cengiz, Ugur, E-mail: ucengiz@gyte.edu.tr [Department of Chemical Engineering, Gebze Institute of Technology, Cayirova, 41400 Kocaeli (Turkey); Avci, Merih Z. [Polymer Science and Technology, Deparment of Chemistry, Istanbul Technical University, Maslak 34469, Istanbul (Turkey); Erbil, H. Yildirim [Department of Chemical Engineering, Gebze Institute of Technology, Cayirova, 41400 Kocaeli (Turkey); Sarac, A. Sezai [Polymer Science and Technology, Deparment of Chemistry, Istanbul Technical University, Maslak 34469, Istanbul (Turkey)

    2012-05-15

    A new statistical terpolymer containing perfluoroethyl alkyl methacrylate (Zonyl-TM), methyl methacrylate and butyl acrylate, poly(Zonyl-TM-ran-MMA-ran-BA) was synthesized in supercritical carbon dioxide at 200 bar and 80 Degree-Sign C using AIBN as an initiator by heterogeneous free radical copolymerization. Nanofibers of this terpolymer were produced by electrospinning from its DMF solution. The structural and thermal properties of terpolymers and electrospun poly(Zonyl-TM-MMA-BA) nanofibers were analyzed using Fourier transform infrared spectroscopy, nuclear magnetic resonance spectroscopy and differential scanning calorimetry. Nanofiber morphology was investigated by scanning electron microscopy. Electrospun nanofiber layer was found to be superhydrophobic with a water contact angle of 172 {+-} 1 Degree-Sign and highly oleophobic with hexadecane, glycerol and ethylene glycol contact angles of 70 {+-} 1 Degree-Sign , 167 {+-} 1 Degree-Sign and 163 {+-} 1 Degree-Sign respectively. The change of the contact angle results on the electrospun fiber layer and flat terpolymer surfaces by varying feed monomer composition were compared and discussed in the text.

  14. Modeling temperature dependent singlet exciton dynamics in multilayered organic nanofibers

    Science.gov (United States)

    de Sousa, Leonardo Evaristo; de Oliveira Neto, Pedro Henrique; Kjelstrup-Hansen, Jakob; da Silva Filho, Demétrio Antônio

    2018-05-01

    Organic nanofibers have shown potential for application in optoelectronic devices because of the tunability of their optical properties. These properties are influenced by the electronic structure of the molecules that compose the nanofibers and also by the behavior of the excitons generated in the material. Exciton diffusion by means of Förster resonance energy transfer is responsible, for instance, for the change with temperature of colors in the light emitted by systems composed of different types of nanofibers. To study in detail this mechanism, we model temperature dependent singlet exciton dynamics in multilayered organic nanofibers. By simulating absorption and emission spectra, the possible Förster transitions are identified. Then, a kinetic Monte Carlo model is employed in combination with a genetic algorithm to theoretically reproduce time-resolved photoluminescence measurements for several temperatures. This procedure allows for the obtainment of different information regarding exciton diffusion in such a system, including temperature effects on the Förster transfer efficiency and the activation energy of the Förster mechanism. The method is general and may be employed for different systems where exciton diffusion plays a role.

  15. Virucidal Nanofiber Textiles Based on Photosensitized Production of Singlet Oxygen

    Czech Academy of Sciences Publication Activity Database

    Lhotáková, Y.; Plištil, L.; Morávková, A.; Kubát, Pavel; Lang, Kamil; Forstová, J.; Mosinger, J.

    2012-01-01

    Roč. 7, č. 11 (2012), e49226 E-ISSN 1932-6203 R&D Projects: GA ČR GAP208/10/1678 Institutional support: RVO:61388955 ; RVO:61388980 Keywords : photosynthesis * biomaterials * nanofiber textiles Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 3.730, year: 2012

  16. Dislocation Starvation and Exhaustion Hardening in Mo-alloy Nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Chisholm, Claire [University of California, Berkeley & LBNL; Bei, Hongbin [ORNL; Lowry, M. B. [University of California, Berkeley; Oh, Jason [Hysitron, Inc., MN; Asif, S.A. Syed [Hysitron, Inc., MN; Warren, O. [Hysitron, Inc., MN; Shan, Zhiwei [Xi' an Jiaotong University, China & Hysitron, Inc., MN; George, Easo P [ORNL; Minor, Andrew [University of California, Berkeley & LBNL

    2012-01-01

    The evolution of defects in Mo alloy nanofibers with initial dislocation densities ranging from 0 to 1.6 1014 m2 were studied using an in situ push-to-pull device in conjunction with a nanoindenter in a transmission electron microscope. Digital image correlation was used to determine stress and strain in local areas of deformation. When they had no initial dislocations the Mo alloy nanofibers suffered sudden catastrophic elongation following elastic deformation to ultrahigh stresses. At the other extreme fibers with a high dislocation density underwent sustained homogeneous deformation after yielding at much lower stresses. Between these two extremes nanofibers with intermediate dislocation densities demonstrated a clear exhaustion hardening behavior, where the progressive exhaustion of dislocations and dislocation sources increases the stress required to drive plasticity. This is consistent with the idea that mechanical size effects ( smaller is stronger ) are due to the fact that nanostructures usually have fewer defects that can operate at lower stresses. By monitoring the evolution of stress locally we find that exhaustion hardening causes the stress in the nanofibers to surpass the critical stress predicted for self-multiplication, supporting a plasticity mechanism that has been hypothesized to account for the rapid strain softening observed in nanoscale bcc materials at high stresses.

  17. Zirconium Hydroxide-coated Nanofiber Mats for Nerve Agent Decontamination.

    Science.gov (United States)

    Kim, Sohee; Ying, Wu Bin; Jung, Hyunsook; Ryu, Sam Gon; Lee, Bumjae; Lee, Kyung Jin

    2017-03-16

    Diverse innovative fabrics with specific functionalities have been developed for requirements such as self-decontamination of chemical/biological pollutants and toxic nerve agents. In this work, Zr(OH) 4 -coated nylon-6,6 nanofiber mats were fabricated for the decontamination of nerve agents. Nylon-6,6 fabric was prepared via the electrospinning process, followed by coating with Zr(OH) 4 , which was obtained by the hydrolysis of Zr(OBu) 4 by a sol-gel reaction on nanofiber surfaces. The reaction conditions were optimized by varying the amounts of Zr(OBu) 4 ,the reaction time, and the temperature of the sol-gel reaction. The composite nanofibers show high decontamination efficiency against diisopropylfluorophosphate, which is a nerve agent analogue, due to its high nucleophilicity that aids in the catalysis of the hydrolysis of the phosphonate ester bonds. Composite nanofiber mats have a large potential and can be applied in specific fields such as military and medical markets. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Morphological Characterization of Nanofibers: Methods and Application in Practice

    Directory of Open Access Journals (Sweden)

    Jakub Širc

    2012-01-01

    Full Text Available Biomedical applications such as wound dressing for skin regeneration, stem cell transplantation, or drug delivery require special demands on the three-dimensional porous scaffolds. Besides the biocompatibility and mechanical properties, the morphology is the most important attribute of the scaffold. Specific surface area, volume, and size of the pores have considerable effect on cell adhesion, growth, and proliferation. In the case of incorporated biologically active substances, their release is also influenced by the internal structure of nanofibers. Although many scientific papers are focused on the preparation of nanofibers and evaluation of biological tests, the morphological characterization was described just briefly as service methods. The aim of this paper is to summarize the methods applicable for morphological characterization of nanofibers and supplement it by the results of our research. Needleless electrospinning technique was used to prepare nanofibers from polylactide, poly(ε-caprolactone, gelatin, and polyamide. Scanning electron microscopy was used to evaluate the fiber diameters and to reveal eventual artifacts in the nanofibrous structure. Nitrogen adsorption/desorption measurements were employed to measure the specific surface areas. Mercury porosimetry was used to determine total porosities and compare pore size distributions of the prepared samples.

  19. Reusable photocatalytic titanium dioxide-cellulose nanofiber films

    Science.gov (United States)

    Alexandra Snyder; Zhenyu Bo; Robert Moon; Jean-Christophe Rochet; Lia. Stanciu

    2013-01-01

    Titanium dioxide (TiO2) is a well-studied photocatalyst that is known to break down organic molecules upon ultraviolet (UV) irradiation. Cellulose nanofibers (CNFs) act as an attractive matrix material for the suspension of photocatalytic particles due to their desirable mechanical and optical properties. In this work, TiO2...

  20. Phosphopeptide enrichment with inorganic nanofibers prepared by forcespinning technology

    Czech Academy of Sciences Publication Activity Database

    Křenková, Jana; Morávková, J.; Buk, J.; Foret, František

    2016-01-01

    Roč. 1427, JAN (2016), s. 8-15 ISSN 0021-9673 R&D Projects: GA ČR(CZ) GA14-06319S; GA ČR(CZ) GBP206/12/G014 Institutional support: RVO:68081715 Keywords : nanofibers * enrichment * phosphopeptides Subject RIV: CB - Analytical Chemistry, Separation Impact factor: 3.981, year: 2016

  1. Development of bimetal-grown multi-scale carbon micro-nanofibers as an immobilizing matrix for enzymes in biosensor applications

    Energy Technology Data Exchange (ETDEWEB)

    Hood, Amit R. [Department of Chemical Engineering, Indian Institute of Technology, Kanpur (India); Saurakhiya, Neelam; Deva, Dinesh [DST Unit on Nanosciences, Kanpur, 208016 (India); Sharma, Ashutosh [Department of Chemical Engineering, Indian Institute of Technology, Kanpur (India); DST Unit on Nanosciences, Kanpur, 208016 (India); Verma, Nishith, E-mail: nishith@iitk.ac.in [Department of Chemical Engineering, Indian Institute of Technology, Kanpur (India); Center for Environmental Science and Engineering, Kanpur 208016 (India)

    2013-10-15

    This study describes the development of a novel bimetal (Fe and Cu)-grown hierarchical web of carbon micro-nanofiber-based electrode for biosensor applications, in particular to detect glucose in liquids. Carbon nanofibers (CNFs) are grown on activated carbon microfibers (ACFs) by chemical vapor deposition (CVD) using Cu and Fe as the metal catalysts. The transition metal-fiber composite is used as the working electrode of a biosensor applied to detect glucose in liquids. In such a bi-nanometal-grown multi-scale web of ACF/CNF, Cu nanoparticles adhere to the ACF-surface, whereas Fe nanoparticles used to catalyze the growth of nanofibers attach to the CNF tips. By ultrasonication, Fe nanoparticles are dislodged from the tips of the CNFs. Glucose oxidase (GOx) is subsequently immobilized on the tips by adsorption. The dispersion of Cu nanoparticles at the substrate surface results in increased conductivity, facilitating electron transfer from the glucose solution to the ACF surface during the enzymatic reaction with glucose. The prepared Cu-ACF/CNF/GOx electrode is characterized for various surface and physicochemical properties by different analytical techniques, including scanning electron microscopy (SEM), electron dispersive X-ray analysis (EDX), Fourier-transform infrared spectroscopy (FTIR), BET surface area analysis, and transmission electron microscopy (TEM). The electrochemical tests show that the prepared electrode has fast response current, electrochemical stability, and high electron transfer rate, corroborated by CV and calibration curves. The prepared transition metal-based carbon electrode in this study is cost-effective, simple to develop, and has a stable immobilization matrix for enzymes. - Graphical abstract: A novel bimetal (Fe and Cu)-grown hierarchical web of carbon micro-nanofiber-based electrode is synthesized for biosensor applications, in particular to detect glucose in liquids. Carbon nanofibers are grown on activated carbon microfibers by

  2. Development of bimetal-grown multi-scale carbon micro-nanofibers as an immobilizing matrix for enzymes in biosensor applications

    International Nuclear Information System (INIS)

    Hood, Amit R.; Saurakhiya, Neelam; Deva, Dinesh; Sharma, Ashutosh; Verma, Nishith

    2013-01-01

    This study describes the development of a novel bimetal (Fe and Cu)-grown hierarchical web of carbon micro-nanofiber-based electrode for biosensor applications, in particular to detect glucose in liquids. Carbon nanofibers (CNFs) are grown on activated carbon microfibers (ACFs) by chemical vapor deposition (CVD) using Cu and Fe as the metal catalysts. The transition metal-fiber composite is used as the working electrode of a biosensor applied to detect glucose in liquids. In such a bi-nanometal-grown multi-scale web of ACF/CNF, Cu nanoparticles adhere to the ACF-surface, whereas Fe nanoparticles used to catalyze the growth of nanofibers attach to the CNF tips. By ultrasonication, Fe nanoparticles are dislodged from the tips of the CNFs. Glucose oxidase (GOx) is subsequently immobilized on the tips by adsorption. The dispersion of Cu nanoparticles at the substrate surface results in increased conductivity, facilitating electron transfer from the glucose solution to the ACF surface during the enzymatic reaction with glucose. The prepared Cu-ACF/CNF/GOx electrode is characterized for various surface and physicochemical properties by different analytical techniques, including scanning electron microscopy (SEM), electron dispersive X-ray analysis (EDX), Fourier-transform infrared spectroscopy (FTIR), BET surface area analysis, and transmission electron microscopy (TEM). The electrochemical tests show that the prepared electrode has fast response current, electrochemical stability, and high electron transfer rate, corroborated by CV and calibration curves. The prepared transition metal-based carbon electrode in this study is cost-effective, simple to develop, and has a stable immobilization matrix for enzymes. - Graphical abstract: A novel bimetal (Fe and Cu)-grown hierarchical web of carbon micro-nanofiber-based electrode is synthesized for biosensor applications, in particular to detect glucose in liquids. Carbon nanofibers are grown on activated carbon microfibers by

  3. Development of mats composed by TiO{sub 2} and carbon dual electrospun nanofibers: A possible anode material in microbial fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Garcia-Gomez, Nora A.; Balderas-Renteria, Isaias [Universidad Autónoma de Nuevo León, Facultad de Ciencias Químicas, Av. Universidad S/N Cd. Universitaria San Nicolás de los Garza Nuevo León, C.P. 66451 México (Mexico); Garcia-Gutierrez, Domingo I. [Universidad Autónoma de Nuevo León, Facultad de Ingeniería Mecánica y Eléctrica, Av. Universidad S/N Cd. Universitaria San Nicolás de los Garza Nuevo León, C.P. 66451 México (Mexico); Universidad Autónoma de Nuevo León, Centro de Innovación, Investigación y Desarrollo en Ingeniería y Tecnología, PIIT, Av. Universidad S/N Cd. Universitaria San Nicolás de los Garza Nuevo León, C.P. 66451 México (Mexico); Mosqueda, Hugo A. [Universidad Autónoma de Nuevo León, Facultad de Ingeniería Mecánica y Eléctrica, Av. Universidad S/N Cd. Universitaria San Nicolás de los Garza Nuevo León, C.P. 66451 México (Mexico); and others

    2015-03-15

    Highlights: • Dual nanofiber of TiO{sub 2}–C/C showed excellent electrical performance. • TiO{sub 2}–C/C dual nanofiber can host a dense biofilm of electroactivated Escherichia coli. • Dual nanofibers can be applied as anode to obtain electricity in microbial fuel cells. - Abstract: A new material based on TiO{sub 2(rutile)}–C{sub (semi-graphitic)}/C{sub (semi-graphitic)} dual nanofiber mats is presented, whose composition and synthesis methodology are fundamental factors for the development of exoelectrogenic biofilms on its surface. Therefore, this material shows the required characteristics for possible applications in the bioconversion process of an organic substrate to electricity in a microbial fuel cell. Chronoamperometry, cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), and electrical conductivity analyses showed excellent electrical performance of the material for the application intended; a resistance as low as 3.149 Ω was able to be measured on this material. Furthermore, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) studies confirmed the morphology sought on the material for the application intended, dual nanofibres TiO{sub 2(rutile)}–C{sub (semi-graphitic)}/C{sub (semi-graphitic)} with a side by side configuration. The difference in composition of the fibers forming the dual nanofibers was clearly observed and confirmed by energy dispersive X-ray spectroscopy (EDXS), and their crystal structure was evident in the results obtained from selected area electron diffraction (SAED) studies. This nanostructured material presented a high surface area and is biocompatible, given that it can host a dense biofilm of electroactivated Escherichia coli. In this study, the maximum current density obtained in a half microbial fuel cell was 8 A/m{sup 2} (0.8 mA/cm{sup 2})

  4. Interpenetrated Binary Supramolecular Nanofibers for Sensitive Fluorescence Detection of Six Classes of Explosives.

    Science.gov (United States)

    Xiong, Wei; Zhu, Qijian; Gong, Yanjun; Wang, Chen; Che, Yanke; Zhao, Jincai

    2018-04-03

    In this work, we develop a sequential self-assembly approach to fabricate interpenetrated binary supramolecular nanofibers consisting of carbazole oligomer 1-cobalt(II) (1-Co 2+ ) coordination nanofibers and oligomer 2 nanofibers for the sensitive detection of six classes of explosives. When exposed to peroxide explosives (e.g., H 2 O 2 ), Co 2+ in 1-Co 2+ coordination nanofibers can be reduced to Co + that can transfer an electron to the excited 2 nanofibers and thereby quench their fluorescence. On the other hand, when exposed to the other five classes of explosives, the excited 2 nanofibers can transfer an electron to explosives to quench their fluorescence. On the basis of the distinct fluorescence quenching mechanisms, six classes of explosives can be sensitively detected. Herein, we provide a new strategy to design broad-band fluorescence sensors for a rich identification of threats.

  5. Graft polymerization of acrylic acid onto chitin nanofiber to improve dispersibility in basic water.

    Science.gov (United States)

    Ifuku, Shinsuke; Iwasaki, Masayoshi; Morimoto, Minoru; Saimoto, Hiroyuki

    2012-09-01

    Graft copolymerization of acrylic acid (AA) on chitin nanofibers was carried out with potassium persulfate as a free radical initiator in an aqueous medium. The molar ratio of grafted AA increased with the AA concentration. The grafted chitin nanofibers were characterized by FT-IR, FE-SEM, UV-vis, XRD, and TGA. After polymerization, the characteristic morphology of chitin nanofibers was maintained. Chitin nanofibers grafted with AA were efficiently dissociated and dispersed homogeneously in basic water because of the electrostatic repulsion effect between nanofibers. AA was grafted on the surface and amorphous part of chitin nanofibers, and the original crystalline structure of α-chitin was maintained. At 330 °C, the weight residue of the graft copolymer increased with the grafted AA content. Copyright © 2012 Elsevier Ltd. All rights reserved.

  6. Dehydration driven changes in the structure and mechanical behavior of electrospun poly (vinyl alcohol) nanofibers

    International Nuclear Information System (INIS)

    Bansal, Ankita; Sinha, Arvind

    2012-01-01

    Electrospun nanofibers of poly (vinyl alcohol) (PVA) are well known for their possible application in different fields, ranging from packaging to tissue engineering. However, biomedical application of these nanofibers gets limited due to its rapid disintegration in water, causing mechanical instability. Addressing this issue, the present manuscript reports ethanol induced dehydration of electrospun PVA nanofibers, and its effects on the structure and mechanical properties of the electrospun system. A systematic variation in the structure and mechanical stability of nanofibers as a function of PVA concentration has also been established in the both hydrated and dehydrated states. - Highlights: ► Study reports structure-property correlation of dehydrated PVA nanofibers. ► Results confirm symmetrical reversal of properties in two states. ► Experimental results are in confirmation with the fusion model of nanofibers.

  7. Biocompatible Electroactive Tetra(aniline)-Conjugated Peptide Nanofibers for Neural Differentiation.

    Science.gov (United States)

    Arioz, Idil; Erol, Ozlem; Bakan, Gokhan; Dikecoglu, F Begum; Topal, Ahmet E; Urel, Mustafa; Dana, Aykutlu; Tekinay, Ayse B; Guler, Mustafa O

    2018-01-10

    Peripheral nerve injuries cause devastating problems for the quality of patients' lives, and regeneration following damage to the peripheral nervous system is limited depending on the degree of the damage. Use of nanobiomaterials can provide therapeutic approaches for the treatment of peripheral nerve injuries. Electroactive biomaterials, in particular, can provide a promising cure for the regeneration of nerve defects. Here, a supramolecular electroactive nanosystem with tetra(aniline) (TA)-containing peptide nanofibers was developed and utilized for nerve regeneration. Self-assembled TA-conjugated peptide nanofibers demonstrated electroactive behavior. The electroactive self-assembled peptide nanofibers formed a well-defined three-dimensional nanofiber network mimicking the extracellular matrix of the neuronal cells. Neurite outgrowth was improved on the electroactive TA nanofiber gels. The neural differentiation of PC-12 cells was more advanced on electroactive peptide nanofiber gels, and these biomaterials are promising for further use in therapeutic neural regeneration applications.

  8. Superhydrophilicity of a nanofiber-covered aluminum surface fabricated via pyrophosphoric acid anodizing

    Science.gov (United States)

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Suzuki, Ryosuke O.

    2016-12-01

    A superhydrophilic aluminum surface covered by numerous alumina nanofibers was fabricated via pyrophosphoric acid anodizing. High-density anodic alumina nanofibers grow on the bottom of a honeycomb oxide via anodizing in concentrated pyrophosphoric acid. The water contact angle on the nanofiber-covered aluminum surface decreased with time after a 4 μL droplet was placed on the surface, and a superhydrophilic behavior with a contact angle measuring 2.2° was observed within 2 s; this contact angle is considerably lower than those observed for electropolished and porous alumina-covered aluminum surfaces. There was no dependence of the superhydrophilicity on the density of alumina nanofibers fabricated via different constant voltage anodizing conditions. The superhydrophilic property of the surface covered by anodic alumina nanofibers was maintained during an exposure test for 359 h. The quick-drying and snow-sliding behaviors of the superhydrophilic aluminum covered with anodic alumina nanofibers were demonstrated.

  9. Electrospun polyvinyl alcohol–collagen–hydroxyapatite nanofibers: a biomimetic extracellular matrix for osteoblastic cells

    International Nuclear Information System (INIS)

    Song Wei; Shi Tong; Ren Weiping; Markel, David C; Wang Sunxi; Mao Guangzhao

    2012-01-01

    The failure of prosthesis after total joint replacement is due to the lack of early implant osseointegration. In this study polyvinyl alcohol–collagen–hydroxyapatite (PVA-Col-HA) electrospun nanofibrous meshes were fabricated as a biomimetic bone-like extracellular matrix for the modification of orthopedic prosthetic surfaces. In order to reinforce the PVA nanofibers, HA nanorods and Type I collagen were incorporated into the nanofibers. We investigated the morphology, biodegradability, mechanical properties and biocompatibility of the prepared nanofibers. Our results showed these inorganic–organic blended nanofibers to be degradable in vitro. The encapsulated nano-HA and collagen interacted with the PVA content, reinforcing the hydrolytic resistance and mechanical properties of nanofibers that provided longer lasting stability. The encapsulated nano-HA and collagen also enhanced the adhesion and proliferation of murine bone cells (MC3T3) in vitro. We propose the PVA-Col-HA nanofibers might be promising modifying materials on implant surfaces for orthopedic applications. (paper)

  10. Fabrication and Characterization of Electrospun Wool Keratin/Poly(vinyl alcohol Blend Nanofibers

    Directory of Open Access Journals (Sweden)

    Shuai Li

    2014-01-01

    Full Text Available Wool keratin/poly(vinyl alcohol (PVA blend nanofibers were fabricated using the electrospinning method in formic acid solutions with different weight ratios of keratin to PVA. The resultant blend nanofibers were characterized by scanning electron microscopy (SEM, Fourier transform infrared (FTIR, X-ray diffraction (XRD, thermal gravimetric analysis (TGA, and tensile test. SEM images showed that the diameter of the blend nanofibers was affected by the content of keratin in blend solution. FTIR and XRD analyses data demonstrated that there were good interactions between keratin and PVA in the blended nanofibers caused by possibly hydrogen bonds. The TGA study revealed that the thermal stability of the blend nanofibers was between those of keratin and PVA. Tensile test indicated that the addition of PVA was able to improve the mechanical properties of the electrospun nanofibers.

  11. Surface modification of polyvinyl alcohol/malonic acid nanofibers by gaseous dielectric barrier discharge plasma for glucose oxidase immobilization

    International Nuclear Information System (INIS)

    Afshari, Esmail; Mazinani, Saeedeh; Ranaei-Siadat, Seyed-Omid; Ghomi, Hamid

    2016-01-01

    Highlights: • We fabricated polyvinyl alcohol/malonic acid nanofibers using electrospinning. • The surface nanofibers were modified by gaseous (air, nitrogen, CO_2 and argon) dielectric barrier discharge. • Among them, air plasma had the most significant effect on glucose oxidase immobilization. • Chemical analysis showed that after modification of nanofibers by air plasma, the carboxyl group increased. • After air plasma treatment, reusability and storage stability of glucose oxidase immobilized on nanofibers improved. - Abstract: Polymeric nanofiber prepares a suitable situation for enzyme immobilization for variety of applications. In this research, we have fabricated polyvinyl alcohol (PVA)/malonic acid nanofibers using electrospinning. After fabrication of nanofibers, the effect of air, nitrogen, CO_2, and argon DBD (dielectric barrier discharge) plasmas on PVA/malonic acid nanofibers were analysed. Among them, air plasma had the most significant effect on glucose oxidase (GOx) immobilization. Attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectrum analysis and X-ray photoelectron spectroscopy (XPS) results revealed that in case of air plasma modified nanofibers, the carboxyl groups on the surface are increased. The scanning electron microscopy (SEM) images showed that, after GOx immobilization, the modified nanofibers with plasma has retained its nanofiber structure. Finally, we analysed reusability and storage stability of GOx immobilized on plasma modified and unmodified nanofibers. The results were more satisfactory for modified nanofibers with respect to unmodified ones.

  12. Surface modification of polyvinyl alcohol/malonic acid nanofibers by gaseous dielectric barrier discharge plasma for glucose oxidase immobilization

    Energy Technology Data Exchange (ETDEWEB)

    Afshari, Esmail, E-mail: e.afshari@mail.sbu.ac.ir [Laser and Plasma Research Institute, Shahid Beheshti University, Evin, 1983963113 Tehran (Iran, Islamic Republic of); Mazinani, Saeedeh [Amirkabir Nanotechnology Research Institute (ANTRI), Amirkabir University of Technology, 15875-4413, Tehran (Iran, Islamic Republic of); Ranaei-Siadat, Seyed-Omid [Protein Research Center, Shahid Beheshti University, Evin, 1983963113 Tehran (Iran, Islamic Republic of); Ghomi, Hamid [Laser and Plasma Research Institute, Shahid Beheshti University, Evin, 1983963113 Tehran (Iran, Islamic Republic of)

    2016-11-01

    Highlights: • We fabricated polyvinyl alcohol/malonic acid nanofibers using electrospinning. • The surface nanofibers were modified by gaseous (air, nitrogen, CO{sub 2} and argon) dielectric barrier discharge. • Among them, air plasma had the most significant effect on glucose oxidase immobilization. • Chemical analysis showed that after modification of nanofibers by air plasma, the carboxyl group increased. • After air plasma treatment, reusability and storage stability of glucose oxidase immobilized on nanofibers improved. - Abstract: Polymeric nanofiber prepares a suitable situation for enzyme immobilization for variety of applications. In this research, we have fabricated polyvinyl alcohol (PVA)/malonic acid nanofibers using electrospinning. After fabrication of nanofibers, the effect of air, nitrogen, CO{sub 2}, and argon DBD (dielectric barrier discharge) plasmas on PVA/malonic acid nanofibers were analysed. Among them, air plasma had the most significant effect on glucose oxidase (GOx) immobilization. Attenuated total reflectance-Fourier transform infrared (ATR-FTIR) spectrum analysis and X-ray photoelectron spectroscopy (XPS) results revealed that in case of air plasma modified nanofibers, the carboxyl groups on the surface are increased. The scanning electron microscopy (SEM) images showed that, after GOx immobilization, the modified nanofibers with plasma has retained its nanofiber structure. Finally, we analysed reusability and storage stability of GOx immobilized on plasma modified and unmodified nanofibers. The results were more satisfactory for modified nanofibers with respect to unmodified ones.

  13. Mechanical properties and cellular response of novel electrospun nanofibers for ligament tissue engineering: Effects of orientation and geometry.

    Science.gov (United States)

    Pauly, Hannah M; Kelly, Daniel J; Popat, Ketul C; Trujillo, Nathan A; Dunne, Nicholas J; McCarthy, Helen O; Haut Donahue, Tammy L

    2016-08-01

    Electrospun nanofibers are a promising material for ligamentous tissue engineering, however weak mechanical properties of fibers to date have limited their clinical usage. The goal of this work was to modify electrospun nanofibers to create a robust structure that mimics the complex hierarchy of native tendons and ligaments. The scaffolds that were fabricated in this study consisted of either random or aligned nanofibers in flat sheets or rolled nanofiber bundles that mimic the size scale of fascicle units in primarily tensile load bearing soft musculoskeletal tissues. Altering nanofiber orientation and geometry significantly affected mechanical properties; most notably aligned nanofiber sheets had the greatest modulus; 125% higher than that of random nanofiber sheets; and 45% higher than aligned nanofiber bundles. Modifying aligned nanofiber sheets to form aligned nanofiber bundles also resulted in approximately 107% higher yield stresses and 140% higher yield strains. The mechanical properties of aligned nanofiber bundles were in the range of the mechanical properties of the native ACL: modulus=158±32MPa, yield stress=57±23MPa and yield strain=0.38±0.08. Adipose derived stem cells cultured on all surfaces remained viable and proliferated extensively over a 7 day culture period and cells elongated on nanofiber bundles. The results of the study suggest that aligned nanofiber bundles may be useful for ligament and tendon tissue engineering based on their mechanical properties and ability to support cell adhesion, proliferation, and elongation. Copyright © 2016 Elsevier Ltd. All rights reserved.

  14. Tuning the conductivity and inner structure of electrospun fibers to promote cardiomyocyte elongation and synchronous beating.

    Science.gov (United States)

    Liu, Yaowen; Lu, Jinfu; Xu, Guisen; Wei, Jiaojun; Zhang, Zhibin; Li, Xiaohong

    2016-12-01

    The key to addressing the challenges facing cardiac tissue engineering is the integration of physical, chemical, and electrical cues into scaffolds. Aligned and conductive scaffolds have been fabricated as synthetic microenvironments to improve the function of cardiomyocytes. However, up to now, the influence of conductive capability and inner structure of fibrous scaffolds have not been determined on the cardiomyocyte morphologies and beating patterns. In the current study, highly aligned fibers were fabricated with loaded up to 6% of carbon nanotubes (CNTs) to modulate the electrical conductivity, while blend and coaxial electrospinning were utilized to create a bulk distribution of CNTs in fiber matrices and a spatial embedment in fiber cores, respectively. Conductive networks were formed in the fibrous scaffolds after the inoculation of over 3% CNTs, and the increase in the conductivity could maintain the cell viabilities, induce the cell elongation, enhance the production of sarcomeric α-actinin and troponin I, and promote the synchronous beating of cardiomyocytes. Although the conductivity of blend fibers is slightly higher than that of coaxial fibers with the same CNT loadings, the lower exposures to CNTs resulted in higher cell viability, elongation, extracellular matrix secretion and beating rates for cardiomyocytes on coaxial fibers. Taken altogether, core-sheath fibers with loaded 5% of CNTs in the fiber cores facilitated the cardiomyocyte growth with a production of organized contractile proteins and a pulsation frequency close to that of the atrium. It is suggested that electrospun scaffolds that couple conductivity and fibrous structure considerations may provide optimal stimuli to foster cell morphology and functions for myocardial regeneration or establishment of in vitro cardiomyocyte culture platform for drug screening. Copyright © 2016. Published by Elsevier B.V.

  15. Photocatalytic and Magnetic Behaviors Observed in BiFeO3 Nanofibers by Electrospinning

    Directory of Open Access Journals (Sweden)

    Xuehui Zhang

    2013-01-01

    Full Text Available Perovskite-type BiFeO3 nanofibers with wave nodes-like morphology were prepared by electrospinning. The nanofibers show a highly enhanced visible-light-active photocatalytic property. The results also showed that the diameter could affect the band gap and photocatalytic performances of nanofibers. Additionally, weak ferromagnetic behaviors can be observed at room temperature, which should be correlated to the size-confinement effect on the magnetic ordering of BiFeO3 structure.

  16. Size-dependent mechanical properties of PVA nanofibers reduced via air plasma treatment

    International Nuclear Information System (INIS)

    Fu Qiang; Song Xuefeng; Gao Jingyun; Han Xiaobing; Zhao Qing; Yu Dapeng; Jin Yu; Jiang Xingyu

    2010-01-01

    Organic nanowires/fibers have great potential in applications such as organic electronics and soft electronic techniques. Therefore investigation of their mechanical performance is of importance. The Young's modulus of poly(vinyl alcohol) (PVA) nanofibers was analyzed by scanning probe microscopy (SPM) methods. Air plasma treatment was used to reduce the nanofibers to different sizes. Size-dependent mechanical properties of PVA nanofibers were studied and revealed that the Young's modulus increased dramatically when the scales became very small (<80 nm).

  17. Size-dependent mechanical properties of PVA nanofibers reduced via air plasma treatment.

    Science.gov (United States)

    Fu, Qiang; Jin, Yu; Song, Xuefeng; Gao, Jingyun; Han, Xiaobing; Jiang, Xingyu; Zhao, Qing; Yu, Dapeng

    2010-03-05

    Organic nanowires/fibers have great potential in applications such as organic electronics and soft electronic techniques. Therefore investigation of their mechanical performance is of importance. The Young's modulus of poly(vinyl alcohol) (PVA) nanofibers was analyzed by scanning probe microscopy (SPM) methods. Air plasma treatment was used to reduce the nanofibers to different sizes. Size-dependent mechanical properties of PVA nanofibers were studied and revealed that the Young's modulus increased dramatically when the scales became very small (<80 nm).

  18. Fabrication of a novel aluminum surface covered by numerous high-aspect-ratio anodic alumina nanofibers

    OpenAIRE

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2015-01-01

    The formation behavior of anodic alumina nanofibers via anodizing in a concentrated pyrophosphoric acid under various conditions was investigated using electrochemical measurements and SEM/TEM observations. Pyrophosphoric acid anodizing at 293 K resulted in the formation of numerous anodic alumina nanofibers on an aluminum substrate through a thin barrier oxide and honeycomb oxide with narrow walls. However, long-term anodizing led to the chemical dissolution of the alumina nanofibers. The de...

  19. Fabrication and Characterization of Electrospun Wool Keratin/Poly(vinyl alcohol) Blend Nanofibers

    OpenAIRE

    Shuai Li; Xu-Hong Yang

    2014-01-01

    Wool keratin/poly(vinyl alcohol) (PVA) blend nanofibers were fabricated using the electrospinning method in formic acid solutions with different weight ratios of keratin to PVA. The resultant blend nanofibers were characterized by scanning electron microscopy (SEM), Fourier transform infrared (FTIR), X-ray diffraction (XRD), thermal gravimetric analysis (TGA), and tensile test. SEM images showed that the diameter of the blend nanofibers was affected by the content of keratin in blend solution...

  20. Low temperature route synthesis of SiC–Al2O3 hetero-structural nanofibers

    International Nuclear Information System (INIS)

    Dai, Xiao; Wang, Hao; Cao, Fengfeng; Yi, Qinghua; Cong, Shan; Wang, Yun; Song, Pingyuan; Zhai, Pengfei; Zou, Guifu; Dong, Chao

    2014-01-01

    SiC–Al 2 O 3 hetero-structural nanofibers have been synthesized by the chemical solution approach at 200 ° C. The diameters of nanofibers are in the range of 60–100 nm while the lengths are from tens of micrometers to hundreds of micrometers. The microstructural analysis shows that the fibers possess a like-epitaxial relationship between (104) of hexagonal Al 2 O 3 and (111) of cubic SiC. Additionally, the optical investigation of the nanofibers suggests there are some defects in the low annealing temperature synthesized SiC–Al 2 O 3 nanofibers. (paper)

  1. Novel electrospun gelatin/oxycellulose nanofibers as a suitable platform for lung disease modeling

    Energy Technology Data Exchange (ETDEWEB)

    Švachová, Veronika, E-mail: xcsvachova@fch.vutbr.cz [Institute of Materials Chemistry, Brno University of Technology (Czech Republic); Vojtová, Lucy [CEITEC – Central European Institute of Technology, Brno University of Technology (Czech Republic); SCITEG, a.s., Brno (Czech Republic); Pavliňák, David [Department of Physical Electronics, Masaryk University (Czech Republic); Vojtek, Libor [Institute of Experimental Biology, Masaryk University (Czech Republic); Sedláková, Veronika [Department of Histology and Embryology, Masaryk University (Czech Republic); International Clinical Research, St. Anne' s University Hospital, Brno (Czech Republic); Hyršl, Pavel [Institute of Experimental Biology, Masaryk University (Czech Republic); Alberti, Milan [Department of Physical Electronics, Masaryk University (Czech Republic); Jaroš, Josef; Hampl, Aleš [Department of Histology and Embryology, Masaryk University (Czech Republic); International Clinical Research, St. Anne' s University Hospital, Brno (Czech Republic); Jančář, Josef [Institute of Materials Chemistry, Brno University of Technology (Czech Republic); CEITEC – Central European Institute of Technology, Brno University of Technology (Czech Republic); SCITEG, a.s., Brno (Czech Republic)

    2016-10-01

    Novel hydrolytically stable gelatin nanofibers modified with sodium or calcium salt of oxycellulose were prepared by electrospinning method. The unique inhibitory effect of these nanofibers against Escherichia coli bacteria was examined by luminometric method. Biocompatibility of these gelatin/oxycellulose nanofibers with eukaryotic cells was tested using human lung adenocarcinoma cell line NCI-H441. Cells firmly adhered to nanofiber surface, as determined by scanning electron microscopy, and no signs of cell dying were detected by fluorescent live/dead assay. We propose that the newly developed gelatin/oxycellulose nanofibers could be used as promising scaffold for lung disease modeling and anti-cancer drug testing. - Highlights: • Novel hydrolytically stable gelatin nanofibers modified with oxycellulose were prepared by electrospinning. • ATR–FTIR spectroscopy and EDX confirmed the presence of oxycellulose in the nanofibers. • Nanofibers modified with calcium salt of oxycellulose exhibited significant antibacterial properties. • Nanofibers modified with sodium salt of oxycellulose revealed excellent biocompatibility with cell line NCI-H441.

  2. Physicochemical investigations of carbon nanofiber supported Cu/ZrO2 catalyst

    International Nuclear Information System (INIS)

    Din, Israf Ud; Shaharun, Maizatul S.; Subbarao, Duvvuri; Naeem, A.

    2014-01-01

    Zirconia-promoted copper/carbon nanofiber catalysts (Cu‐ZrO 2 /CNF) were prepared by the sequential deposition precipitation method. The Herringbone type of carbon nanofiber GNF-100 (Graphite nanofiber) was used as a catalyst support. Carbon nanofiber was oxidized to (CNF-O) with 5% and 65 % concentration of nitric acid (HNO 3 ). The CNF activated with 5% HNO 3 produced higher surface area which is 155 m 2 /g. The catalyst was characterized by X-ray Diffraction (XRD), Fourier Transform Infra-Red (FTIR) and N 2 adsorption-desorption. The results showed that increase of HNO 3 concentration reduced the surface area and porosity of the catalyst

  3. Morphology study of nanofibers produced by extraction from polymer blend fibers using image processing

    International Nuclear Information System (INIS)

    Dehghan, Neda; Tavanaie, Mohammad Ali; Payvandy, Pedram

    2015-01-01

    The morphology of nanofibers extracted from the industrial-scale produced polypropylene/polybutylene terephthalate (PP/PBT) blend fibers was studied. To study the morphology and diameter measurements of the nanofibers, image processing method was used, and the results were compared with the results of a conventional visual method. Comparing these two methods indicated the good performance of image processing methods for the measuring of nanofiber diameter. Among the various applied image processing methods, the fuzzy c-means (FCM) method was determined as the best for image thresholding. Additionally, the distance transform method was determined as the best way for measuring nanofiber diameter. According to high regression coefficient (R=0.98) resulting between the draw ratio and nanofibers diameter, the high effectiveness of draw ratio to nanofiber diameter is concluded. The spherical (drop) shapes of the PBT dispersed phase particles were eventually deformed into very thin fibrils during the drawing process. The results of measuring the nanofiber diameters showed that the diameter means of nanofibers varied from 420 nm to 175 nm with the highest draw ratio. Good uniformity for diameter of nanofibers was observed, which had not been observed in previous works.

  4. Electrospun water-stable zein/ethyl cellulose composite nanofiber and its drug release properties

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Hangyi; Wang, Qingqing; Li, Guohui [Key Laboratory of Eco-textiles, Jiangnan University, Wuxi (China); Qiu, Yuyu [Key Laboratory of Eco-textiles, Jiangnan University, Wuxi (China); Laboratory of Natural Medicine, Wuxi Medical School, Jiangnan University (China); Wei, Qufu, E-mail: qfwei@jiangnan.edu.cn [Key Laboratory of Eco-textiles, Jiangnan University, Wuxi (China)

    2017-05-01

    A simple and cost-effective way to prepare water-stable zein-based nanofibers for potential drug delivery was presented in this article. Corn protein zein was co-electrospun with hydrophobic ethyl cellulose. Indomethacin, as a model drug, was incorporated in situ into the composite nanofibers. Scanning electron microscopy and element mapping revealed the morphologies of drug-loaded nanofibers and drug distribution, respectively. Fourier transform infrared spectra confirmed the physical blending among the components. Differential scanning calorimetry and X-ray diffraction demonstrated the physical state of drug and polymers in the nanofiber matrix. The composite nanofibers showed a sustained diffusion-controlled release according to the results of in vitro dissolution tests. - Highlights: • A simple, non-toxic and cost-effective way to improve water stability of zein nanofibers was proposed. • Electrospun zein/ethyl cellulose nanofibers with improved water stability and mechanical strength were prepared. • Indomethacin was homogeneously distributed in the zein/ethyl cellulose nanofibers with no aggregation or cluster. • The zein/ethyl cellulose nanofibers presented a sustained drug release profile, following Fickican diffusion mechanism.

  5. Synthesis and Characterization of Carbon nanofibers on Co and Cu Catalysts by Chemical Vapor Deposition

    International Nuclear Information System (INIS)

    Park, Eunsil; Kim, Jongwon; Lee, Changseop

    2014-01-01

    This study reports on the synthesis of carbon nanofibers via chemical vapor deposition using Co and Cu as catalysts. In order to investigate the suitability of their catalytic activity for the growth of nanofibers, we prepared catalysts for the synthesis of carbon nanofibers with Cobalt nitrate and Copper nitrate, and found the optimum concentration of each respective catalyst. Then we made them react with Aluminum nitrate and Ammonium Molybdate to form precipitates. The precipitates were dried at a temperature of 110 .deg. C in order to be prepared into catalyst powder. The catalyst was sparsely and thinly spread on a quartz tube boat to grow carbon nanofibers via thermal chemical vapor deposition. The characteristics of the synthesized carbon nanofibers were analyzed through SEM, EDS, XRD, Raman, XPS, and TG/DTA, and the specific surface area was measured via BET. Consequently, the characteristics of the synthesized carbon nanofibers were greatly influenced by the concentration ratio of metal catalysts. In particular, uniform carbon nanofibers of 27 nm in diameter grew when the concentration ratio of Co and Cu was 6:4 at 700 .deg. C of calcination temperature; carbon nanofibers synthesized under such conditions showed the best crystallizability, compared to carbon nanofibers synthesized with metal catalysts under different concentration ratios, and revealed 1.26 high amorphicity as well as 292 m 2 g -1 high specific surface area

  6. Fabrication of a novel aluminum surface covered by numerous high-aspect-ratio anodic alumina nanofibers

    Science.gov (United States)

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2015-11-01

    The formation behavior of anodic alumina nanofibers via anodizing in a concentrated pyrophosphoric acid under various conditions was investigated using electrochemical measurements and SEM/TEM observations. Pyrophosphoric acid anodizing at 293 K resulted in the formation of numerous anodic alumina nanofibers on an aluminum substrate through a thin barrier oxide and honeycomb oxide with narrow walls. However, long-term anodizing led to the chemical dissolution of the alumina nanofibers. The density of the anodic alumina nanofibers decreased as the applied voltage increased in the 10-75 V range. However, active electrochemical dissolution of the aluminum substrate occurred at a higher voltage of 90 V. Low temperature anodizing at 273 K resulted in the formation of long alumina nanofibers measuring several micrometers in length, even though a long processing time was required due to the low current density during the low temperature anodizing. In contrast, high temperature anodizing easily resulted in the formation and chemical dissolution of alumina nanofibers. The structural nanofeatures of the anodic alumina nanofibers were controlled by choosing of the appropriate electrochemical conditions, and numerous high-aspect-ratio alumina nanofibers (>100) can be successfully fabricated. The anodic alumina nanofibers consisted of a pure amorphous aluminum oxide without anions from the employed electrolyte.

  7. Recent Advances in Cell Electrospining of Natural and Synthetic Nanofibers for Regenerative Medicine.

    Science.gov (United States)

    Zamani, Reza; Aval, Sedigheh Fekri; Pilehvar-Soltanahmadi, Younes; Nejati-Koshki, Kazem; Zarghami, Nosratollah

    2018-01-22

    The progression of nanotechnology provides opportunities to manipulate synthetic and natural materials to mimic the natural structure for tissue engineering applications. The electrospinning technique applies electrostatic principle to fabricate electrospun nanofibers. Nanofiber scaffolds are precisely similar to the native extracellular matrix (ECM) and support cell proliferation, adhesion, tendency to preserve their phenotypic shape and directed growth according to the nanofiber direction. This study reviewed both the natural and synthetic type of nanofibers and described the different properties used to trigger certain process in the tissue development. Also, the potential applications of electrospun scaffolds for regenerative medicine were summarized. © Georg Thieme Verlag KG Stuttgart · New York.

  8. Preparation of Fish Skin Gelatin-Based Nanofibers Incorporating Cinnamaldehyde by Solution Blow Spinning

    Science.gov (United States)

    Liu, Fei; Avena-Bustillos, Roberto J.; Bridges, David F.; Takeoka, Gary R.; Wu, Vivian C. H.; Chiou, Bor-Sen; McHugh, Tara H.; Zhong, Fang

    2018-01-01

    Cinnamaldehyde, a natural preservative that can non-specifically deactivate foodborne pathogens, was successfully incorporated into fish skin gelatin (FSG) solutions and blow spun into uniform nanofibers. The effects of cinnamaldehyde ratios (5–30%, w/w FSG) on physicochemical properties of fiber-forming emulsions (FFEs) and their nanofibers were investigated. Higher ratios resulted in higher values in particle size and viscosity of FFEs, as well as higher values in diameter of nanofibers. Loss of cinnamaldehyde was observed during solution blow spinning (SBS) process and cinnamaldehyde was mainly located on the surface of resultant nanofibers. Nanofibers all showed antibacterial activity by direct diffusion and vapor release against Escherichia coli O157:H7, Salmonella typhimurium, and Listeria monocytogenes. Inhibition zones increased as cinnamaldehyde ratio increased. Nanofibers showed larger inhibition effects than films prepared by casting method when S. typhimurium was exposed to the released cinnamaldehyde vapor, although films had higher remaining cinnamaldehyde than nanofibers after preparation. Lower temperature was favorable for cinnamaldehyde retention, and nanofibers added with 10% cinnamaldehyde ratio showed the highest retention over eight-weeks of storage. Results suggest that FSG nanofibers can be prepared by SBS as carriers for antimicrobials. PMID:29470390

  9. Spectroscopy, Manipulation and Trapping of Neutral Atoms, Molecules, and Other Particles Using Optical Nanofibers: A Review

    Science.gov (United States)

    Morrissey, Michael J.; Deasy, Kieran; Frawley, Mary; Kumar, Ravi; Prel, Eugen; Russell, Laura; Truong, Viet Giang; Chormaic, Síle Nic

    2013-01-01

    The use of tapered optical fibers, i.e., optical nanofibers, for spectroscopy and the detection of small numbers of particles, such as neutral atoms or molecules, has been gaining interest in recent years. In this review, we briefly introduce the optical nanofiber, its fabrication, and optical mode propagation within. We discuss recent progress on the integration of optical nanofibers into laser-cooled atom and vapor systems, paying particular attention to spectroscopy, cold atom cloud characterization, and optical trapping schemes. Next, a natural extension of this work to molecules is introduced. Finally, we consider several alternatives to optical nanofibers that display some advantages for specific applications. PMID:23945738

  10. Preparation of Fish Skin Gelatin-Based Nanofibers Incorporating Cinnamaldehyde by Solution Blow Spinning.

    Science.gov (United States)

    Liu, Fei; Türker Saricaoglu, Furkan; Avena-Bustillos, Roberto J; Bridges, David F; Takeoka, Gary R; Wu, Vivian C H; Chiou, Bor-Sen; Wood, Delilah F; McHugh, Tara H; Zhong, Fang

    2018-02-22

    Cinnamaldehyde, a natural preservative that can non-specifically deactivate foodborne pathogens, was successfully incorporated into fish skin gelatin (FSG) solutions and blow spun into uniform nanofibers. The effects of cinnamaldehyde ratios (5-30%, w / w FSG) on physicochemical properties of fiber-forming emulsions (FFEs) and their nanofibers were investigated. Higher ratios resulted in higher values in particle size and viscosity of FFEs, as well as higher values in diameter of nanofibers. Loss of cinnamaldehyde was observed during solution blow spinning (SBS) process and cinnamaldehyde was mainly located on the surface of resultant nanofibers. Nanofibers all showed antibacterial activity by direct diffusion and vapor release against Escherichia coli O157:H7 , Salmonella typhimurium , and Listeria monocytogenes . Inhibition zones increased as cinnamaldehyde ratio increased. Nanofibers showed larger inhibition effects than films prepared by casting method when S . typhimurium was exposed to the released cinnamaldehyde vapor, although films had higher remaining cinnamaldehyde than nanofibers after preparation. Lower temperature was favorable for cinnamaldehyde retention, and nanofibers added with 10% cinnamaldehyde ratio showed the highest retention over eight-weeks of storage. Results suggest that FSG nanofibers can be prepared by SBS as carriers for antimicrobials.

  11. Precisely Assembled Nanofiber Arrays as a Platform to Engineer Aligned Cell Sheets for Biofabrication

    Directory of Open Access Journals (Sweden)

    Vince Beachley

    2014-08-01

    Full Text Available A hybrid cell sheet engineering approach was developed using ultra-thin nanofiber arrays to host the formation of composite nanofiber/cell sheets. It was found that confluent aligned cell sheets could grow on uniaxially-aligned and crisscrossed nanofiber arrays with extremely low fiber densities. The porosity of the nanofiber sheets was sufficient to allow aligned linear myotube formation from differentiated myoblasts on both sides of the nanofiber sheets, in spite of single-side cell seeding. The nanofiber content of the composite cell sheets is minimized to reduce the hindrance to cell migration, cell-cell contacts, mass transport, as well as the foreign body response or inflammatory response associated with the biomaterial. Even at extremely low densities, the nanofiber component significantly enhanced the stability and mechanical properties of the composite cell sheets. In addition, the aligned nanofiber arrays imparted excellent handling properties to the composite cell sheets, which allowed easy processing into more complex, thick 3D structures of higher hierarchy. Aligned nanofiber array-based composite cell sheet engineering combines several advantages of material-free cell sheet engineering and polymer scaffold-based cell sheet engineering; and it represents a new direction in aligned cell sheet engineering for a multitude of tissue engineering applications.

  12. Fabrication of indium sulfide nanofibers via a hydrothermal method assisted by AAO template

    International Nuclear Information System (INIS)

    Zhu Xiaoyi; Ma Junfeng; Wang Yonggang; Tao Jiantao; Zhou Jun; Zhao Zhongqiang; Xie Lijin; Tian Hua

    2006-01-01

    β-In 2 S 3 nanofibers were successfully synthesized via a hydrothermal method with AAO membrane as a template at 150 deg. C for 15 h. XRD patterns indicated the perfect crystallization of β-In 2 S 3 . SEM images showed that the β-In 2 S 3 nanofibers grew up from the channel ends of the AAO template. TEM images confirmed that the nanofibers had a high aspect ratio of ca. 40-50 and diameters of about 10 nm. The room temperature photoluminescence (PL) spectrum of the β-In 2 S 3 nanofibers indicated its potential applications in light-emission devices

  13. Nanobiotechnology approach to fabricate polycaprolactone nanofibers containing solid titanium nanoparticles as future implant materials

    DEFF Research Database (Denmark)

    Sheikh, Faheem A.; Kanjwal, Muzafar Ahmed; Cha, Jaegwan

    2011-01-01

    In this study, a good combination of electrospun poly(caprolactone) nanofibers incorporated with high purity titanium nanoparticles is introduced for hard tissue engineering applications. A simple approach to utilize the colloidal properties of poly(caprolactone) and titanium nanoparticles...... nanofiber mats, they were incubated in simulated body fluid at 37 °C for 10 days. Field emission scanning electron microscopy in combination with energy-dispersive X-ray spectroscopy indicated that incorporation of titanium strongly activates precipitation of the apatite-like materials from the utilized...... simulated body fluid. Moreover, in-vivo experiments using experimental dogs revealed that nanofibers can yield good tissue regeneration on the surfaces of nanofibers....

  14. Morphology study of nanofibers produced by extraction from polymer blend fibers using image processing

    Energy Technology Data Exchange (ETDEWEB)

    Dehghan, Neda; Tavanaie, Mohammad Ali; Payvandy, Pedram [University of Yazd, Yazd (Iran, Islamic Republic of)

    2015-09-15

    The morphology of nanofibers extracted from the industrial-scale produced polypropylene/polybutylene terephthalate (PP/PBT) blend fibers was studied. To study the morphology and diameter measurements of the nanofibers, image processing method was used, and the results were compared with the results of a conventional visual method. Comparing these two methods indicated the good performance of image processing methods for the measuring of nanofiber diameter. Among the various applied image processing methods, the fuzzy c-means (FCM) method was determined as the best for image thresholding. Additionally, the distance transform method was determined as the best way for measuring nanofiber diameter. According to high regression coefficient (R=0.98) resulting between the draw ratio and nanofibers diameter, the high effectiveness of draw ratio to nanofiber diameter is concluded. The spherical (drop) shapes of the PBT dispersed phase particles were eventually deformed into very thin fibrils during the drawing process. The results of measuring the nanofiber diameters showed that the diameter means of nanofibers varied from 420 nm to 175 nm with the highest draw ratio. Good uniformity for diameter of nanofibers was observed, which had not been observed in previous works.

  15. Flexible Hybrid Membranes with Ni(OH)2 Nanoplatelets Vertically Grown on Electrospun Carbon Nanofibers for High-Performance Supercapacitors.

    Science.gov (United States)

    Zhang, Longsheng; Ding, Qianwei; Huang, Yunpeng; Gu, Huahao; Miao, Yue-E; Liu, Tianxi

    2015-10-14

    The practical applications of transition metal oxides and hydroxides for supercapacitors are restricted by their intrinsic poor conductivity, large volumetric expansion, and rapid capacitance fading upon cycling, which can be solved by optimizing these materials to nanostructures and confining them within conductive carbonaceous frameworks. In this work, flexible hybrid membranes with ultrathin Ni(OH)2 nanoplatelets vertically and uniformly anchored on the electrospun carbon nanofibers (CNF) have been facilely prepared as electrode materials for supercapacitors. The Ni(OH)2/CNF hybrid membranes with three-dimensional macroporous architectures as well as hierarchical nanostructures can provide open and continuous channels for rapid diffusion of electrolyte to access the electrochemically active Ni(OH)2 nanoplatelets. Moreover, the carbon nanofiber can act both as a conductive core to provide efficient transport of electrons for fast Faradaic redox reactions of the Ni(OH)2 sheath, and as a buffering matrix to mitigate the local volumetric expansion/contraction upon long-term cycling. As a consequence, the optimized Ni(OH)2/CNF hybrid membrane exhibits a high specific capacitance of 2523 F g(-1) (based on the mass of Ni(OH)2, that is 701 F g(-1) based on the total mass) at a scan rate of 5 mV s(-1). The Ni(OH)2/CNF hybrid membranes with high mechanical flexibility, superior electrical conductivity, and remarkably improved electrochemical capacitance are condsidered as promising flexible electrode materials for high-performance supercapacitors.

  16. Electrospun nanofiber reinforcement of dental composites with electromagnetic alignment approach

    International Nuclear Information System (INIS)

    Uyar, Tansel; Çökeliler, Dilek; Doğan, Mustafa; Koçum, Ismail Cengiz; Karatay, Okan; Denkbaş, Emir Baki

    2016-01-01

    Polymethylmethacrylate (PMMA) is commonly used as a base acrylic denture material with benefits of rapid and easy handling, however, when it is used in prosthetic dentistry, fracturing or cracking problems can be seen due to the relatively low strength issues. Besides, acrylic resin is the still prominent material for denture fabrication due to its handy and low cost features. Numerous proposed fillers that are used to produce PMMA composites, however electrospun polyvinylalcohol (PVA) nanofiber fillers for production of PMMA composite resins are not studied as much as the others. The other focus of the practice is to compare both mechanical properties and efficiency of aligned fibers versus non-aligned PVA nanofibers in PMMA based dental composites. Field-controlled electrospinning system is manufactured and provided good alignment in lab scale as one of contributions. Some novel auxiliary electrodes in controlled structure are augmented to obtain different patterns of alignment with a certain range of fiber diameters. Scanning electron microscopy is used for physical characterization to determine the range of fiber diameters. Non-woven fiber has no unique pattern due to chaotic nature of electrospinning process, but aligned fibers have round pattern or crossed lines. These produced fibers are structured as layer-by-layer form with different features, and these features are used in producing PMMA dental composites with different volume ratios. The maximum flexural strength figure shows that fiber load by weight of 0.25% w/w and above improves in the maximum level. As a result, mechanical properties of PMMA dental composites are improved by using PVA nanofibers as a filler, however the improvement was higher when aligned PVA nanofibers are used. The maximum values were 5.1 MPa (flexural strength), 0.8 GPa (elastic modulus), and 170 kJ/m 3 (toughness) in three-point bending test. In addition to the positive results of aligned and non-aligned nanofibers it was found

  17. Electrospun nanofiber reinforcement of dental composites with electromagnetic alignment approach

    Energy Technology Data Exchange (ETDEWEB)

    Uyar, Tansel [Department of Biomedical Engineering, Başkent University Bağlıca Campus, 06530 Ankara (Turkey); Çökeliler, Dilek, E-mail: cokeliler@baskent.edu.tr [Department of Biomedical Engineering, Başkent University Bağlıca Campus, 06530 Ankara (Turkey); Doğan, Mustafa [Department of Electrical and Electronics Engineering, Başkent University, Ankara 06180 (Turkey); Koçum, Ismail Cengiz [Department of Biomedical Engineering, Başkent University Bağlıca Campus, 06530 Ankara (Turkey); Karatay, Okan [Department of Electrical and Electronics Engineering, Başkent University, Ankara 06180 (Turkey); Denkbaş, Emir Baki [Department of Chemistry, Biochemistry Division, Hacettepe University, Ankara (Turkey)

    2016-05-01

    Polymethylmethacrylate (PMMA) is commonly used as a base acrylic denture material with benefits of rapid and easy handling, however, when it is used in prosthetic dentistry, fracturing or cracking problems can be seen due to the relatively low strength issues. Besides, acrylic resin is the still prominent material for denture fabrication due to its handy and low cost features. Numerous proposed fillers that are used to produce PMMA composites, however electrospun polyvinylalcohol (PVA) nanofiber fillers for production of PMMA composite resins are not studied as much as the others. The other focus of the practice is to compare both mechanical properties and efficiency of aligned fibers versus non-aligned PVA nanofibers in PMMA based dental composites. Field-controlled electrospinning system is manufactured and provided good alignment in lab scale as one of contributions. Some novel auxiliary electrodes in controlled structure are augmented to obtain different patterns of alignment with a certain range of fiber diameters. Scanning electron microscopy is used for physical characterization to determine the range of fiber diameters. Non-woven fiber has no unique pattern due to chaotic nature of electrospinning process, but aligned fibers have round pattern or crossed lines. These produced fibers are structured as layer-by-layer form with different features, and these features are used in producing PMMA dental composites with different volume ratios. The maximum flexural strength figure shows that fiber load by weight of 0.25% w/w and above improves in the maximum level. As a result, mechanical properties of PMMA dental composites are improved by using PVA nanofibers as a filler, however the improvement was higher when aligned PVA nanofibers are used. The maximum values were 5.1 MPa (flexural strength), 0.8 GPa (elastic modulus), and 170 kJ/m{sup 3} (toughness) in three-point bending test. In addition to the positive results of aligned and non-aligned nanofibers it was

  18. Extraction of cellulose nanofibers from Pinus oocarpa residues

    Energy Technology Data Exchange (ETDEWEB)

    Manrich, Anny; Martins, Maria Alice, E-mail: anny@daad-alumni.de [EMBRAPA Instrumentacao, Sao Carlos, SP (Brazil); Moraes, Jheyce Cristina; Pasquoloto, Camila [Universidade Federal de Sao Carlos (UFSCar), SP (Brazil)

    2016-07-01

    Full text: Pinus oocarpa, which wood is moderately hard and tough, is planted in Brazil for reforestation and employed for timber production used in constructions. The wood residues, such as shavings, bark and sawdust represent 30% to 50% of the total volume of wood production, of which the sawdust is 10%{sup 1}. Cellulose nanofibers is nanomaterials having a diameter between 5 nm and 20 nm and a length of up to hundreds of nm. To obtain nanofibers from cellulose sources, such as sisal and sugarcane bagasse, is used chemical processes, in which the lignocellulosic material initially undergoes pre-treatments to promote partial separation of the cellulose, such as mercerisation and bleaching thus disposing lignin and hemicellulose components. Sequentially, by controlled acid hydrolysis, amorphous regions of the cellulose are removed, and crystalline cellulose is isolated in the form of cellulose nanofibers. In this work, nanofibers from sawdust of Pinnus oocarpa, containing 44.8 wt% of cellulose 20.6 wt% hemicellulose and 30.0 wt% insoluble lignin were isolated by mercerisation (NaOH 5%, 80°C, 120 min), followed by bleaching (NaOH + acetic acid + NaClO{sub 2}, 80 deg C, 240min) and acid hydrolysis (60 wt% sulfuric acid, 45 °C, 40min). Nanofibers obtained were characterized by DRX and SEM-FEG. Results showed that, for used conditions, fiber acid hydrolysis was not complete, therefore a biphasic suspension was formed. Crystallinity index achieved was not much higher than that from pinus fiber itself, increasing from 62% to 65% and signs of cellulose type II were observed. SEM images showed elongated fibers, which have diameter of 15 ± 5 nm and length of hundreds of nm, what means that they have a large L/D aspect ratio. Nanofiber extraction yield was very low (1.3 wt% of initial residue). All steps of the process are being reviewed aiming at better results. 1) Morais, S. A. L.; Nascimento E. A. e D. C. Melo, 2005, R. Árvore, 29, 3, 461-470. (author)

  19. Preparation of Metallic and Polymer Nanoparticles, Responsive Nanogels and Nanofibers by Radiation Initiated Reactions

    Energy Technology Data Exchange (ETDEWEB)

    Lee, K. -Pill; Gopalan, A. I. [Department of Chemistry Education, Kyungpook National University (Korea, Republic of)

    2009-07-01

    Synthesis of nanomaterials have become the focus of intensive research due to their numerous applications in diverse fields such as electronics, optics, ceramics, metallurgy, pulp and paper, environmental, pharmaceutics, biotechnology and biomedical fields. Due to expanding demand for the nanomaterials with defined properties, extensive research activities have been focused on the synthesis and characterization of “functional nanomaterials”. Our research group launched into research activities on the preparation of varieties of functional materials using radiation as the source for inducing functionalities ino these new nanomaterials. Importantly, we kept final goals for specific applications. Thus, we have prepared few interesting functional nanomaterials such as metal nanoparticles decorated multi wall carbon nanotubes, pore filled functional electrospun nanofibers and nanocables based on conducting polymer and carbon nanotubes and demonstrated their applications toward electrocatalysts, polymer electrolyte in energy devices and biosensors. In the forthcoming sections, a brief outline on the use of radiation for the preparation of those functional nanomaterials are presented. (author)

  20. A novel nano-nonwoven fabric with three-dimensionally dispersed nanofibers: entrapment of carbon nanofibers within nonwovens using the wet-lay process

    International Nuclear Information System (INIS)

    Karwa, Amogh N; Davis, Virginia A; Tatarchuk, Bruce J; Barron, Troy J

    2012-01-01

    This study demonstrates, for the first time, the manufacturing of novel nano-nonwovens that are comprised of three-dimensionally distributed carbon nanofibers within the matrices of traditional wet-laid nonwovens. The preparation of these nano-nonwovens involves dispersing and flocking carbon nanofibers, and optimizing colloidal chemistry during wet-lay formation. The distribution of nanofibers within the nano-nonwoven was verified using polydispersed aerosol filtration testing, air permeability, low surface tension liquid capillary porometry, SEM and cyclic voltammetry. All these characterization techniques indicated that nanofiber flocks did not behave as large solid clumps, but retained the ‘nanoporous’ structure expected from nanofibers. These nano-nonwovens showed significant enhancements in aerosol filtration performance. The reduction–oxidation reactions of the functional groups on nanofibers and the linear variation of electric double-layer capacitance with nanofiber loading were measured using cyclic voltammetry. More than 65 m 2 (700 ft 2 ) of the composite were made during the demonstration of process scalability using a Fourdrinier-type continuous pilot papermaking machine. The scalability of the process with the control over pore size distribution makes these composites very promising for filtration and other nonwoven applications. (paper)

  1. Mussel-Inspired Anisotropic Nanocellulose and Silver Nanoparticle Composite with Improved Mechanical Properties, Electrical Conductivity and Antibacterial Activity

    Directory of Open Access Journals (Sweden)

    Hoang-Linh Nguyen

    2016-03-01

    Full Text Available Materials for wearable devices, tissue engineering and bio-sensing applications require both antibacterial activity to prevent bacterial infection and biofilm formation, and electrical conductivity to electric signals inside and outside of the human body. Recently, cellulose nanofibers have been utilized for various applications but cellulose itself has neither antibacterial activity nor conductivity. Here, an antibacterial and electrically conductive composite was formed by generating catechol mediated silver nanoparticles (AgNPs on the surface of cellulose nanofibers. The chemically immobilized catechol moiety on the nanofibrous cellulose network reduced Ag+ to form AgNPs on the cellulose nanofiber. The AgNPs cellulose composite showed excellent antibacterial efficacy against both Gram-positive and Gram-negative bacteria. In addition, the catechol conjugation and the addition of AgNP induced anisotropic self-alignment of the cellulose nanofibers which enhances electrical and mechanical properties of the composite. Therefore, the composite containing AgNPs and anisotropic aligned the cellulose nanofiber may be useful for biomedical applications.

  2. Hollow NiO nanofibers modified by citric acid and the performances as supercapacitor electrode

    International Nuclear Information System (INIS)

    Ren, Bo; Fan, Meiqing; Liu, Qi; Wang, Jun; Song, Dalei; Bai, Xuefeng

    2013-01-01

    Graphical abstract: The possible formation process of NiO nanofibers without citric acid (a), and modified by citric acid (b). When the nanofibers is modified by citric acid, the nickel citrate is produced by complexing action of citric acid and nickel nitrate. Because of the larger space steric hindrance, the structure is limited by the molecular geometry. Under high temperature, the hollow nanofibers composed of NiO slices formed after the removal of PVP. Highlights: ► The method of obtaining hollow nanofibers is raised for the first time. ► The prepared NiO nanofibers are hollow tube and comprised of many NiO sheets. ► The hollow structure facilitated the electrolyte penetration. ► The hollow NiO nanofibers have good electrochemical properties. -- Abstract: NiO nanofibers modified by citric acid (NiO/CA) for supercapacitor material have been fabricated by electrospinning process. The characterizations of the nanofibers are investigated by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Electrochemical properties are characterized by cyclic voltammetry, galvanostatic charge/discharge measurements, and electrochemical impedance spectroscopy. Results show that the NiO/CA nanofibers are hollow tube and comprised of many NiO sheets. Furthermore, the NiO/CA nanofibers have good electrochemical reversibility and display superior capacitive performance with large capacitance (336 F g −1 ), which is 2.5 times of NiO electrodes. Moreover, the NiO/CA nanofibers show excellent cyclic performance after 1000 cycles

  3. Polyvinyl alcohol/starch composite nanofibers by bubble electrospinning

    Directory of Open Access Journals (Sweden)

    Liu Zhi

    2014-01-01

    Full Text Available Bubble electrospinning exhibits profound prospect of industrialization of macro/ nano materials. Starch is the most abundant and inexpensive biopolymer. With the drawbacks of poor strength, water resistibility, thermal stability and processability of pure starch, some biodegradable synthetic polymers such as poly (lactic acid, polyvinyl alcohol were composited to electrospinning. To the best of our knowledge, composite nanofibers of polyvinyl alcohol/starch from bubble electrospinning have never been investigated. In the present study, nanofibers of polyvinyl alcohol/starch were prepared from bubble electrospinning. The processability and the morphology were affected by the weight ratio of polyvinyl alcohol and starchy. The rheological studies were in agreement with the spinnability of the electrospinning solutions.

  4. The photophysics of luminescence in multilayered organic nanofibers

    DEFF Research Database (Denmark)

    Tavares, Luciana; Quochi, Francesco; Simbrunner, Clemens

    different organic molecules (para-hexaphenyl (p6P) donor and α-sexithiophene (6T) acceptor materials). The excited donor (p6P) is able to sensitize the acceptor (6T) via resonance energy transfer (Förster) as a consequence of the overlap between the p6P photo emission spectrum and the 6T absorption spectrum......Multilayered crystalline nanofibers are exemplary model system for the study of exciton dynamics and lasing in organic materials due to their well-defined morphology, high luminescence efficiencies, and color tunability. The multi-layered nanofibers are composed of alternating layers of two...... to extract the activation energy for exciton diffusion in crystalline p6P (19 meV). The weak PL temperature dependence of the acceptor material (6T) and hence its high quantum yield in combination with the small activation energy for exciton diffusion of the donor material (p6P) explain the high efficiency...

  5. Carbon composites composites with carbon fibers, nanofibers, and nanotubes

    CERN Document Server

    Chung, Deborah D L

    2017-01-01

    Carbon Composites: Composites with Carbon Fibers, Nanofibers, and Nanotubes, Second Edition, provides the reader with information on a wide range of carbon fiber composites, including polymer-matrix, metal-matrix, carbon-matrix, ceramic-matrix and cement-matrix composites. In contrast to other books on composites, this work emphasizes materials rather than mechanics. This emphasis reflects the key role of materials science and engineering in the development of composite materials. The applications focus of the book covers both the developing range of structural applications for carbon fiber composites, including military and civil aircraft, automobiles and construction, and non-structural applications, including electromagnetic shielding, sensing/monitoring, vibration damping, energy storage, energy generation, and deicing. In addition to these new application areas, new material in this updated edition includes coverage of cement-matrix composites, carbon nanofibers, carbon matrix precursors, fiber surface ...

  6. Polyurethane Nanofiber Membranes for Waste Water Treatment by Membrane Distillation

    Directory of Open Access Journals (Sweden)

    T. Jiříček

    2017-01-01

    Full Text Available Self-sustained electrospun polyurethane nanofiber membranes were manufactured and tested on a direct-contact membrane distillation unit in an effort to find the optimum membrane thickness to maximize flux rate and minimize heat losses across the membrane. Also salt retention and flux at high salinities up to 100 g kg−1 were evaluated. Even though the complex structure of nanofiber layers has extreme specific surface and porosity, membrane performance was surprisingly predictable; the highest flux was achieved with the thinnest membranes and the best energy efficiency was achieved with the thickest membranes. All membranes had salt retention above 99%. Nanotechnology offers the potential to find modern solutions for desalination of waste waters, by introducing new materials with revolutionary properties, but new membranes must be developed according to the target application.

  7. Ethylene tetrafluoroethylene nanofibers prepared by CO2 laser supersonic drawing

    Directory of Open Access Journals (Sweden)

    A. Suzuki

    2013-06-01

    Full Text Available Ethylene tetrafluoroethylene (ETFE nanofibers were prepared by carbon dioxide (CO2 laser irradiation of asspun ETFE fibers with four different melt flow rates (MFRs in a supersonic jet that was generated by blowing air into a vacuum chamber through the fiber injection orifice. The drawability and superstructure of fibers produced by CO2 laser supersonic drawing depend on the laser power, the chamber pressure, the fiber injection speed, and the MFR. Nanofibers obtained using a laser power of 20 W, a chamber pressure of 20 kPa, and an MFR of 308 g•10 min–1 had an average diameter of 0.303 µm and a degree of crystallinity of 54%.

  8. Tuneable nanoparticle-nanofiber composite substrate for improved cellular adhesion.

    Science.gov (United States)

    Nicolini, Ariana M; Toth, Tyler D; Yoon, Jeong-Yeol

    2016-09-01

    This work presents a novel technique using a reverse potential electrospinning mode for fabricating nanoparticle-embedded composites that can be tailored to represent various fiber diameters, surface morphologies, and functional groups necessary for improved cellular adhesion. Polycaprolactone (PCL) nanofibers were electrospun in both traditional positive (PP) and reverse potential (RP) electrical fields. The fibers were incorporated with 300nm polystyrene (PS) fluorescent particles, which contained carboxyl, amine groups, and surfactants. In the unconventional RP, the charged colloidal particles and surfactants were shown to have an exaggerated effect on Taylor cone morphology and fiber diameter caused by the changes in charge density and surface tension of the bulk solution. The RP mode was shown to lead to a decrease in fiber diameter from 1200±100nm (diameter±SE) for the nanofibers made with PCL alone to 440±80nm with the incorporation of colloidal particles, compared to the PP mode ranging from 530±90nm to 350±50nm, respectively. The nanoparticle-nanofiber composite substrates were cultured with human umbilical vein endothelial cells (HUVECs) and evaluated for cellular viability and adhesion for up to 5 days. Adhesion to the nanofibrous substrates was improved by 180±10% with the addition of carboxylated particles and by 480±60% with the functionalization of an RGD ligand compared to the PCL nanofibers. The novel approach of electrospinning in the RP mode with the addition of colloids in order to alter charge density and surface tension could be utilized towards many applications, one being implantable biomaterials and tissue engineered scaffolds as demonstrated in this work. Copyright © 2016 Elsevier B.V. All rights reserved.

  9. Nanoscaled Mechanical Properties of Cement Composites Reinforced with Carbon Nanofibers

    OpenAIRE

    Barbhuiya, Salim; Chow, PengLoy

    2017-01-01

    This paper reports the effects of carbon nanofibers (CNFs) on nanoscaled mechanical properties of cement composites. CNFs were added to cement composites at the filler loading of 0.2 wt % (by wt. of cement). Micrographs based on scanning electron microscopy (SEM) show that CNFs are capable of forming strong interfacial bonding with cement matrices. Experimental results using nanoindentation reveal that the addition of CNFs in cement composites increases the proportions of high-density calcium...

  10. Cellulose nanofibers use in coated paper

    Science.gov (United States)

    Richmond, Finley

    Cellulose Nanofibers (CNF) are materials that can be obtained by the mechanical breakdown of natural fibers. CNF have the potential to be produced at low cost in a paper mill and may provide novel properties to paper, paper coatings, paints, or other products. However, suspensions have a complex rheology even at low solid contents. To be able to coat, pump, or mix CNF at moderate solids, it is critical to understand the rheology of these suspensions and how they flow in process equipment; current papers only report the rheology up to 6% solids. Few publications are available that describe the coating of CNF onto paper or the use of CNF as an additive into a paper coating. The rheology of CNF suspensions and coatings that contain CNF were characterized with parallel-disk geometry in a controlled stress rheometer. The steady shear viscosity, the complex viscosity, the storage modulus, and the yield stress were determined for the range of solids or concentrations (2.5-10.5%). CNF were coated onto paper with a laboratory rod coater, a size press and a high speed cylindrical laboratory coater (CLC). For each case, the coat weights were measures and the properties of the papers were characterized. CNF water base suspension was found to be a shear thinning with a power law index of around 0.1. Oscillatory tests showed a linear viscoelastic region at low strains and significant storage and loss moduli even at low solids. The Cox Merz rule does not hold for CNF suspensions or coating formulations that contain CNF with complex viscosities that are about 100 times larger than the steady shear viscosities. Paper coating formulations that contain CNF were found to have viscosities and storage and loss moduli that are over ten times larger than coatings that contain starch at similar solids. CNF suspensions were coated on papers with low amount transferred on paper either at high solids or high nip loadings. The amount transferred appears to be controlled by an interaction of

  11. Electrospun Metal Nanofiber Webs as High-Performance Transparent Electrode

    KAUST Repository

    Wu, Hui; Hu, Liangbing; Rowell, Michael W.; Kong, Desheng; Cha, Judy J.; McDonough, James R.; Zhu, Jia; Yang, Yuan; McGehee, Michael D.; Cui, Yi

    2010-01-01

    Transparent electrodes, indespensible in displays and solar cells, are currently dominated by indium tin oxide (ITO) films although the high price of indium, brittleness of films, and high vacuum deposition are limiting their applications. Recently, solution-processed networks of nanostructures such as carbon nanotubes (CNTs), graphene, and silver nanowires have attracted great attention as replacements. A low junction resistance between nanostructures is important for decreasing the sheet resistance. However, the junction resistances between CNTs and boundry resistances between graphene nanostructures are too high. The aspect ratios of silver nanowires are limited to ∼100, and silver is relatively expensive. Here, we show high-performance transparent electrodes with copper nanofiber networks by a low-cost and scalable electrospinning process. Copper nanofibers have ultrahigh aspect ratios of up to 100000 and fused crossing points with ultralow junction resistances, which result in high transmitance at low sheet resistance, e.g., 90% at 50 Ω/sq. The copper nanofiber networks also show great flexibility and stretchabilty. Organic solar cells using copper nanowire networks as transparent electrodes have a power efficiency of 3.0%, comparable to devices made with ITO electrodes. © 2010 American Chemical Society.

  12. Laser-induced charge separation in organic nanofibers

    DEFF Research Database (Denmark)

    Tavares, Luciana; Behn, Dino; Kjelstrup-Hansen, Jakob

    Organic semiconductors have unique properties that can be tailored via synthetic chemistry for specific applications, which combined with their low price and straight-forward processing over large areas make them interesting materials for future devices. Certain oligomers can self-assemble into c......Organic semiconductors have unique properties that can be tailored via synthetic chemistry for specific applications, which combined with their low price and straight-forward processing over large areas make them interesting materials for future devices. Certain oligomers can self......-assemble into crystalline nanofibers by vapor deposition onto muscovite mica substrates, and we have recently shown that such nanofibers can be transferred to different substrates by roll-printing and used as the active material in e.g. organic field-effect transistors (OFETs), organic light-emitting transistors (OLETs......), and organic phototransistors (OPTs). However, several device-related issues incl. charge-separation and local band structure remain poorly understood. In this work, we use electrostatic force microscopy (EFM) combined with optical microscopy to study the local surface charge of an individual organic nanofiber...

  13. Proliferation of Genetically Modified Human Cells on Electrospun Nanofiber Scaffolds

    Directory of Open Access Journals (Sweden)

    Mandula Borjigin

    2012-01-01

    Full Text Available Gene editing is a process by which single base mutations can be corrected, in the context of the chromosome, using single-stranded oligodeoxynucleotides (ssODNs. The survival and proliferation of the corrected cells bearing modified genes, however, are impeded by a phenomenon known as reduced proliferation phenotype (RPP; this is a barrier to practical implementation. To overcome the RPP problem, we utilized nanofiber scaffolds as templates on which modified cells were allowed to recover, grow, and expand after gene editing. Here, we present evidence that some HCT116-19, bearing an integrated, mutated enhanced green fluorescent protein (eGFP gene and corrected by gene editing, proliferate on polylysine or fibronectin-coated polycaprolactone (PCL nanofiber scaffolds. In contrast, no cells from the same reaction protocol plated on both regular dish surfaces and polylysine (or fibronectin-coated dish surfaces proliferate. Therefore, growing genetically modified (edited cells on electrospun nanofiber scaffolds promotes the reversal of the RPP and increases the potential of gene editing as an ex vivo gene therapy application.

  14. Electrospun Metal Nanofiber Webs as High-Performance Transparent Electrode

    KAUST Repository

    Wu, Hui

    2010-10-13

    Transparent electrodes, indespensible in displays and solar cells, are currently dominated by indium tin oxide (ITO) films although the high price of indium, brittleness of films, and high vacuum deposition are limiting their applications. Recently, solution-processed networks of nanostructures such as carbon nanotubes (CNTs), graphene, and silver nanowires have attracted great attention as replacements. A low junction resistance between nanostructures is important for decreasing the sheet resistance. However, the junction resistances between CNTs and boundry resistances between graphene nanostructures are too high. The aspect ratios of silver nanowires are limited to ∼100, and silver is relatively expensive. Here, we show high-performance transparent electrodes with copper nanofiber networks by a low-cost and scalable electrospinning process. Copper nanofibers have ultrahigh aspect ratios of up to 100000 and fused crossing points with ultralow junction resistances, which result in high transmitance at low sheet resistance, e.g., 90% at 50 Ω/sq. The copper nanofiber networks also show great flexibility and stretchabilty. Organic solar cells using copper nanowire networks as transparent electrodes have a power efficiency of 3.0%, comparable to devices made with ITO electrodes. © 2010 American Chemical Society.

  15. Light-activated polymethylmethacrylate nanofibers with antibacterial activity

    Energy Technology Data Exchange (ETDEWEB)

    Elashnikov, Roman [Department of Solid State Engineering, University of Chemistry and Technology, 16628 Prague (Czech Republic); Lyutakov, Oleksiy, E-mail: lyutakoo@vscht.cz [Department of Solid State Engineering, University of Chemistry and Technology, 16628 Prague (Czech Republic); Ulbrich, Pavel [Department of Biochemistry and Microbiology, University of Chemistry and Technology, 16628 Prague (Czech Republic); Svorcik, Vaclav [Department of Solid State Engineering, University of Chemistry and Technology, 16628 Prague (Czech Republic)

    2016-07-01

    The creation of an antibacterial material with triggerable properties enables us to avoid the overuse or misuse of antibacterial substances and, thus, prevent the emergence of resistant bacterial strains. As a potential light-activated antibacterial material, polymethylmethacrylate (PMMA) nanofibers doped with silver nanoparticles (AgNPs) and meso-tetraphenylporphyrin (TPP) were prepared by electrospinning. TPP was chosen as an effectively reactive oxygen species (ROS) producer. Antibacterial tests on Staphylococcus epidermidis (S. epidermidis) and Enterococcus faecalis (E. faecalis) showed the excellent light-triggerable antibacterial activity of the doped materials. Upon light irradiation at the wavelength corresponding to the TPP absorption peak (405 nm), antibacterial activity dramatically increased, mostly due to the release of AgNPs from the polymer matrix. Furthermore, under prolonged light irradiation, the AgNPs/TPP/PMMA nanofibers, displayed enhanced longevity and photothermal stability. Thus, our results suggest that the proposed material is a promising option for the photodynamic inactivation of bacteria. - Highlights: • The novelty of proposed work can be summared as follow: • Silver nanoparticles/meso-tetraphenylporphyrin embedded polymethylmethacrylate nanofibers were obtained for the first time. • Light triggering of PMMA fibers leads to sufficient release of AgNPs or their agglomeration, depending on the light source. • Release of AgNPs leads to appearance of pronounced antimicrobial activity, which can be switched on/off by the illumination.

  16. Preparation and Characterization of Gelatin Nanofibers Containing Silver Nanoparticles

    Science.gov (United States)

    Jeong, Lim; Park, Won Ho

    2014-01-01

    Ag nanoparticles (NPs) were synthesized in formic acid aqueous solutions through chemical reduction. Formic acid was used for a reducing agent of Ag precursor and solvent of gelatin. Silver acetate, silver tetrafluoroborate, silver nitrate, and silver phosphate were used as Ag precursors. Ag+ ions were reduced into Ag NPs by formic acid. The formation of Ag NPs was characterized by a UV-Vis spectrophotometer. Ag NPs were quickly generated within a few minutes in silver nitrate (AgNO3)/formic acid solution. As the water content of formic acid aqueous solution increased, more Ag NPs were generated, at a higher rate and with greater size. When gelatin was added to the AgNO3/formic acid solution, the Ag NPs were stabilized, resulting in smaller particles. Moreover, gelatin limits further aggregation of Ag NPs, which were effectively dispersed in solution. The amount of Ag NPs formed increased with increasing concentration of AgNO3 and aging time. Gelatin nanofibers containing Ag NPs were fabricated by electrospinning. The average diameters of gelatin nanofibers were 166.52 ± 32.72 nm, but these decreased with the addition of AgNO3. The average diameters of the Ag NPs in gelatin nanofibers ranged between 13 and 25 nm, which was confirmed by transmission electron microscopy (TEM). PMID:24758929

  17. Studies on electrospun nylon-6/chitosan complex nanofiber interactions

    International Nuclear Information System (INIS)

    Zhang Haitao; Li Shubai; Branford White, Christopher J.; Ning Xin; Nie Huali; Zhu Limin

    2009-01-01

    Composite membranes of nylon-6/chitosan nanofibers with different weight ratio of nylon-6 to chitosan were fabricated successfully using electrospinning. Morphologies of the nanofibers were investigated by scanning electron microscopy (SEM) and the intermolecular interactions of the nylon-6/chitosan complex were evaluated by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), differential scanning calorimetry (DSC) as well as mechanical testing. We found that morphology and diameter of the nanofibers were influenced by the concentration of the solution and weight ratio of the blending component materials. Furthermore FT-IR analyses on interactions between components demonstrated an IR band frequency shift that appeared to be dependent on the amount of chitosan in the complex. Observations from XRD and DSC suggested that a new fraction of γ phase crystals appeared and increased with the increasing content of chitosan in blends, this indicated that intermolecular interactions occurred between nylon-6 and chitosan. Results from performance data in mechanical showed that intermolecular interactions varied with varying chitosan content in the fibers. It was concluded that a new composite product was created and the stability of this system was attributed to strong new interactions such as hydrogen bond formation between the nylon-6 polymers and chitosan structures.

  18. Flexible piezoelectric nanogenerators based on PVDF-TrFE nanofibers

    Science.gov (United States)

    Serairi, Linda; Gu, Long; Qin, Yong; Lu, Yingxian; Basset, Philippe; Leprince-Wang, Yamin

    2018-01-01

    In this paper, electrospun piezoelectric PVDF-TrFE nanofibers were used for the fabrication of two types of flexible nanogenerator (NG) devices based on the direct piezoelectric effect, allowing the conversion of mechanical energy into electrical energy. The first one is composed of quite well aligned thin film nanofibers of about 35 μm and the second one is composed of random nanofibers of about 50 μm. The influence of the applied stress and strain rate on the output for both types of NG was studied. It is shown that the pulse peaks generated by NG increase with the applied mechanical strain frequency, the generated output is also proportional to the applied stress amplitude. The first NG loaded in bending mode can generate a maximum voltage of 270 mV. By connecting two devices in series/parallel, the voltage/current value could be multiplied by two. The second NG which was biased in compression mode using a shaker controlled by a force sensor, can generate a potential of about 7 V under 3.6 N applied force.

  19. Hydrothermal synthesis, characterization, and luminescence of Ca{sub 2}B{sub 2}O{sub 5}:RE (RE = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Li; Wan, Yingpeng; Li, Yuze; Pu, Yinfu; Huang, Yanlin, E-mail: huang@suda.edu.cn [Soochow University, State and Local Joint Engineering Laboratory for Novel Functional Polymeric Materials, College of Chemistry, Chemical Engineering and Materials Science (China); Chen, Cuili; Seo, Hyo Jin, E-mail: hjseo@pknu.ac.kr [Pukyong National University, Department of Physics and Interdisciplinary Program of Biomedical Engineering (Korea, Republic of)

    2016-04-15

    Ca{sub 2}B{sub 2}O{sub 5}:RE (RE = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanofibers were synthesized by the hydrothermal reaction method. The structural refinement was conducted on the base of the X-ray powder diffraction (XRD) measurements. The surface properties of the Ca{sub 2}B{sub 2}O{sub 5}:RE (RE = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanofibers were investigated by the measurements such as the scanning electron microscope (SEM), transmission electron microscope (TEM), and the energy dispersive spectrum (EDS). The nanofiber has a diameter of about 100 nm and a length of several micrometers. The luminescence properties such as photoluminescence excitation (PLE) and emission spectra (PL), decay lifetime, color coordinates, and the absolute internal quantum efficiency (QE) were reported. Ca{sub 2}B{sub 2}O{sub 5}:Eu{sup 3+} nanofibers show the red luminescence with CIE coordinates of (x = 0.41, y = 0.51) and the luminescence lifetime of 0.63 ms. The luminescence of Ca{sub 2}B{sub 2}O{sub 5}:Tb{sup 3+} nanofibers is green color (x = 0.29, y = 0.53) with the lifetime of 2.13 ms. However, Dy{sup 3+}-doped Ca{sub 2}B{sub 2}O{sub 5} nanofibers present a single-phase white-color phosphor with the fluorescence decay of 3.05 ms. Upon near-UV excitation, the absolute quantum efficiency is measured to be 65, 35, and 37 % for Eu{sup 3+}-, Tb{sup 3+}-, Dy{sup 3+}-doped Ca{sub 2}B{sub 2}O{sub 5} nanofibers, respectively. It is suggested that Ca{sub 2}B{sub 2}O{sub 5}:RE (RE = Eu{sup 3+}, Tb{sup 3+}, Dy{sup 3+}) nanofibers could be an efficient phosphor for lighting and display.

  20. Lecithin blended polyamide-6 high aspect ratio nanofiber scaffolds via electrospinning for human osteoblast cell culture

    Energy Technology Data Exchange (ETDEWEB)

    Nirmala, R. [Bio-nano System Engineering, College of Engineering, Chonbuk National University, Jeonju, 561 756 (Korea, Republic of); Park, Hye-Min [Department of Pharmacology and Toxicology, College of Veterinary Medicine, Chonbuk National University, Jeonju 561 756 (Korea, Republic of); Navamathavan, R. [School of Advanced Materials Engineering, Chonbuk National University, Jeonju 561 756 (Korea, Republic of); Kang, Hyung-Sub [Department of Pharmacology and Toxicology, College of Veterinary Medicine, Chonbuk National University, Jeonju 561 756 (Korea, Republic of); El-Newehy, Mohamed H. [Petrochemical Research Chair, Department of Chemistry, College of Science, King Saud University, Riyadh 11451 (Saudi Arabia); Kim, Hak Yong, E-mail: khy@jbnu.ac.kr [Petrochemical Research Chair, Department of Chemistry, College of Science, King Saud University, Riyadh 11451 (Saudi Arabia); Center for Healthcare Technology and Development, Chonbuk National University, Jeonju, 561 756 (Korea, Republic of)

    2011-03-12

    In this study, we focused on the preparation and characterization of lecithin blended polyamide-6 nanofibers via an electrospinning process for human osteoblastic (HOB) cell culture applications. The morphological, structural characterizations and thermal properties of polyamide-6/lecithin nanofibers were determined by using scanning electron microscopy (SEM), field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC) and thermogravimetry (TGA). SEM images revealed that the nanofibers were well-oriented with good incorporation of lecithin. FT-IR results indicated the presence of amino groups of lecithin in the blended nanofibers. TGA analysis revealed that the onset degradation temperature decreased with increasing lecithin content in the blended nanofibers. The morphological features of cells attached on polyamide-6/lecithin nanofibers were confirmed by SEM. The adhesion, viability and proliferation properties of osteoblast cells on the polyamide-6/lecithin blended nanofibers were analyzed by in vitro cell compatibility test. This study demonstrated the non-cytotoxic behavior of electrospun polyamide-6/lecithin nanofibers for the osteoblast cell culture.

  1. Lecithin blended polyamide-6 high aspect ratio nanofiber scaffolds via electrospinning for human osteoblast cell culture

    International Nuclear Information System (INIS)

    Nirmala, R.; Park, Hye-Min; Navamathavan, R.; Kang, Hyung-Sub; El-Newehy, Mohamed H.; Kim, Hak Yong

    2011-01-01

    In this study, we focused on the preparation and characterization of lecithin blended polyamide-6 nanofibers via an electrospinning process for human osteoblastic (HOB) cell culture applications. The morphological, structural characterizations and thermal properties of polyamide-6/lecithin nanofibers were determined by using scanning electron microscopy (SEM), field-emission scanning electron microscopy (FE-SEM), X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, differential scanning calorimetry (DSC) and thermogravimetry (TGA). SEM images revealed that the nanofibers were well-oriented with good incorporation of lecithin. FT-IR results indicated the presence of amino groups of lecithin in the blended nanofibers. TGA analysis revealed that the onset degradation temperature decreased with increasing lecithin content in the blended nanofibers. The morphological features of cells attached on polyamide-6/lecithin nanofibers were confirmed by SEM. The adhesion, viability and proliferation properties of osteoblast cells on the polyamide-6/lecithin blended nanofibers were analyzed by in vitro cell compatibility test. This study demonstrated the non-cytotoxic behavior of electrospun polyamide-6/lecithin nanofibers for the osteoblast cell culture.

  2. Reactive electrospinning and biodegradation of cross-linked methacrylated polycarbonate nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Wu Ruizhi; Zhang Jianfeng; Fan Yuwei; Xu Xiaoming [Department of Comprehensive Dentistry and Biomaterials, Louisiana State University Health Sciences Center, 1100 Florida Avenue, Box 137, New Orleans, LA 70119 (United States); Stoute, Diana; Lallier, Thomas, E-mail: xxu@lsuhsc.edu [Department of Cell Biology and Anatomy, Louisiana State University Health Science Center, 1100 Florida Avenue, Box 137, New Orleans, LA 70119 (United States)

    2011-06-15

    The objectives of this study were to fabricate cross-linked biodegradable polycarbonate nanofibers and to investigate their biodegradability by different enzymes. Poly(2,3-dihydroxycarbonate) was synthesized from naturally occurring l-tartaric acid. The hydroxyl groups on the functional polycarbonate were converted to methacrylate groups to enable the polymer to cross-link under UV irradiation. Smooth cross-linked methacrylated polycarbonate nanofibers (300-1800 nm) were fabricated by a reactive electrospinning process with in situ UV radiation from a mixed solution of linear methacrylated polycarbonate (MPC) and poly(ethylene oxide) (PEO) (MPC:PEO = 9:1) in methanol/chloroform (50/50). These cross-linked nanofibers have shown excellent solvent resistance and their solubility decreases with increasing degree of cross-linking. The thermal properties of linear and cross-linked polycarbonate nanofibers were investigated by differential scanning calorimetry and thermogravimetric analysis. The cross-linked polycarbonate nanofibers show no melting point below 200 {sup 0}C and their decomposition temperature increases with increasing cross-linking degree. Their biodegradation products by five different enzymes were analyzed using liquid chromatography-mass spectrometry (LC-MS). The biodegradability of the polycarbonate nanofibers decreases with increasing cross-linking degree. These nanofibers were found to support human fibroblast survival and to promote cell attachment. This study demonstrates that cross-linked biodegradable polycarbonate nanofibers with different chemical properties and biodegradability can be fabricated using the novel reactive electrospinning technology to meet the needs of different biomedical applications.

  3. Electrospun polyacrylonitrile nanofibers loaded with silver nanoparticles by silver mirror reaction

    Energy Technology Data Exchange (ETDEWEB)

    Shi, Yongzheng; Li, Yajing; Zhang, Jianfeng; Yu, Zhongzhen; Yang, Dongzhi, E-mail: yangdz@mail.buct.edu.cn

    2015-06-01

    The silver mirror reaction (SMR) method was selected in this paper to modify electrospun polyacrylonitrile (PAN) nanofibers, and these nanofibers loaded with silver nanoparticles showed excellent antibacterial properties. PAN nanofibers were first pretreated in AgNO{sub 3} aqueous solution before the SMR process so that the silver nanoparticles were distributed evenly on the outer surface of the nanofibers. The final PAN nanofibers were characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), transmission electron microscopy (TEM), TEM-selected area electron diffraction (SAED), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). SEM, TEM micrographs and SAED patterns confirmed homogeneous dispersion of the silver nanoparticles which were composed of monocrystals with diameters 20–30 nm. EDS and XRD results showed that these monocrystals tended to form face-centered cubic single silver. TGA test indicated that the nanoparticles loaded on the nanofibers reached above 50 wt.%. This material was also evaluated by the viable cell-counting method. The results indicated that PAN nanofibers loaded with silver nanoparticles exhibited excellent antimicrobial activities against gram-negative Escherichia coli (E. coli), gram-positive Staphylococcus aureus (S. aureus) and the fungus Monilia albicans. Thus, this material had many potential applications in biomedical fields. - Highlights: • Silver mirror reaction was used to prepare nanofibers loaded with silver nanoparticles. • The SAED patterns demonstrated the monocrystallinity of silver nanocrystals. • The XRD results showed nanoparticles tended to be face-centered cubic single silver. • The material showed excellent antimicrobial activities against bacteria and fungi.

  4. Measurement of fluorescence emission spectrum of few strongly driven atoms using an optical nanofiber.

    Science.gov (United States)

    Das, Manoj; Shirasaki, A; Nayak, K P; Morinaga, M; Le Kien, Fam; Hakuta, K

    2010-08-02

    We show that the fluorescence emission spectrum of few atoms can be measured by using an optical nanofiber combined with the optical heterodyne and photon correlation spectroscopy. The observed fluorescence spectrum of the atoms near the nanofiber shows negligible effects of the atom-surface interaction and agrees well with the Mollow triplet spectrum of free-space atoms at high excitation intensity.

  5. Force and time-dependent self-assembly, disruption and recovery of supramolecular peptide amphiphile nanofibers.

    Science.gov (United States)

    Dikecoglu, F Begum; Topal, Ahmet E; Ozkan, Alper D; Tekin, E Deniz; Tekinay, Ayse B; Guler, Mustafa O; Dana, Aykutlu

    2018-07-13

    Biological feedback mechanisms exert precise control over the initiation and termination of molecular self-assembly in response to environmental stimuli, while minimizing the formation and propagation of defects through self-repair processes. Peptide amphiphile (PA) molecules can self-assemble at physiological conditions to form supramolecular nanostructures that structurally and functionally resemble the nanofibrous proteins of the extracellular matrix, and their ability to reconfigure themselves in response to external stimuli is crucial for the design of intelligent biomaterials systems. Here, we investigated real-time self-assembly, deformation, and recovery of PA nanofibers in aqueous solution by using a force-stabilizing double-pass scanning atomic force microscopy imaging method to disrupt the self-assembled peptide nanofibers in a force-dependent manner. We demonstrate that nanofiber damage occurs at tip-sample interaction forces exceeding 1 nN, and the damaged fibers subsequently recover when the tip pressure is reduced. Nanofiber ends occasionally fail to reconnect following breakage and continue to grow as two individual nanofibers. Energy minimization calculations of nanofibers with increasing cross-sectional ellipticity (corresponding to varying levels of tip-induced fiber deformation) support our observations, with high-ellipticity nanofibers exhibiting lower stability compared to their non-deformed counterparts. Consequently, tip-mediated mechanical forces can provide an effective means of altering nanofiber integrity and visualizing the self-recovery of PA assemblies.

  6. Synthesis and characterization of crosslinked gellan/PVA nanofibers for tissue engineering application.

    Science.gov (United States)

    Vashisth, Priya; Pruthi, Vikas

    2016-10-01

    Electrospun nanofibers based on gellan are considered as promising biomaterial for tissue engineering and wound healing applications. However, major hurdles in usage of these nanofibers are their poor stability and deprived structural consistency in aqueous medium which is a prerequisite for their application in the biomedical sector. In this investigation, three dimensional nanofibers, consisting of gellan and PVA have been fabricated and then stabilized under various crosslinking conditions in order to improve their physiochemical stability. The impacts of different crosslinking procedures on the gellan/PVA nanofibers were examined in terms of changes in morphological, mechanical, swelling and biological properties. Superior tensile strength and strain was recorded in case of crosslinked nanofibers as compared to non-crosslinked nanofibers. Contact angles and swelling properties of fabricated gellan/PVA nanofibers were found to vary with the crosslinking method. All crosslinking conditions were evaluated with regard to their response towards human dermal fibroblast (3T3L1) cells. Biocompatibility studies suggested that the fabricated crosslinked gellan/PVA nanofibers hold a great prospective in the biomedical engineering arena. Copyright © 2016 Elsevier B.V. All rights reserved.

  7. Electrospun polyacrylonitrile nanofibers loaded with silver nanoparticles by silver mirror reaction

    International Nuclear Information System (INIS)

    Shi, Yongzheng; Li, Yajing; Zhang, Jianfeng; Yu, Zhongzhen; Yang, Dongzhi

    2015-01-01

    The silver mirror reaction (SMR) method was selected in this paper to modify electrospun polyacrylonitrile (PAN) nanofibers, and these nanofibers loaded with silver nanoparticles showed excellent antibacterial properties. PAN nanofibers were first pretreated in AgNO 3 aqueous solution before the SMR process so that the silver nanoparticles were distributed evenly on the outer surface of the nanofibers. The final PAN nanofibers were characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS), transmission electron microscopy (TEM), TEM-selected area electron diffraction (SAED), X-ray diffraction (XRD) and thermogravimetric analysis (TGA). SEM, TEM micrographs and SAED patterns confirmed homogeneous dispersion of the silver nanoparticles which were composed of monocrystals with diameters 20–30 nm. EDS and XRD results showed that these monocrystals tended to form face-centered cubic single silver. TGA test indicated that the nanoparticles loaded on the nanofibers reached above 50 wt.%. This material was also evaluated by the viable cell-counting method. The results indicated that PAN nanofibers loaded with silver nanoparticles exhibited excellent antimicrobial activities against gram-negative Escherichia coli (E. coli), gram-positive Staphylococcus aureus (S. aureus) and the fungus Monilia albicans. Thus, this material had many potential applications in biomedical fields. - Highlights: • Silver mirror reaction was used to prepare nanofibers loaded with silver nanoparticles. • The SAED patterns demonstrated the monocrystallinity of silver nanocrystals. • The XRD results showed nanoparticles tended to be face-centered cubic single silver. • The material showed excellent antimicrobial activities against bacteria and fungi

  8. Mirror-finished superhydrophobic aluminum surfaces modified by anodic alumina nanofibers and self-assembled monolayers

    Science.gov (United States)

    Nakajima, Daiki; Kikuchi, Tatsuya; Natsui, Shungo; Suzuki, Ryosuke O.

    2018-05-01

    We demonstrate mirror-finished superhydrophobic aluminum surfaces fabricated via the formation of anodic alumina nanofibers and subsequent modification with self-assembled monolayers (SAMs). High-density anodic alumina nanofibers were formed on the aluminum surface via anodizing in a pyrophosphoric acid solution. The alumina nanofibers became tangled and bundled by further anodizing at low temperature because of their own weight, and the aluminum surface was completely covered by the long falling nanofibers. The nanofiber-covered aluminum surface exhibited superhydrophilic behavior, with a contact angle measuring less than 10°. As the nanofiber-covered aluminum surface was modified with n-alkylphosphonic acid SAMs, the water contact angle drastically shifted to superhydrophobicity, measuring more than 150°. The contact angle increased with the applied voltage during pyrophosphoric acid anodizing, the anodizing time, and the number of carbon atoms contained in the SAM molecules modified on the alumina nanofibers. By optimizing the anodizing and SAM-modification conditions, superhydrophobic behavior could be achieved with only a brief pyrophosphoric acid anodizing period of 3 min and subsequent simple immersion in SAM solutions. The superhydrophobic aluminum surface exhibited a high reflectance, measuring approximately 99% across most of the visible spectrum, similar to that of an electropolished aluminum surface. Therefore, our mirror-finished superhydrophobic aluminum surface based on anodic alumina nanofibers and SAMs can be used as a reflective mirror in various optical applications such as concentrated solar power systems.

  9. Polyacrylonitrile (PAN)/crown ether composite nanofibers for the selective adsorption of cations

    NARCIS (Netherlands)

    Tas, Sinem; Kaynan, Ozge; Ozden-Yenigun, Elif; Nijmeijer, Dorothea C.

    2016-01-01

    In this study, we prepared electrospun polyacrylonitrile (PAN) nanofibers functionalized with dibenzo-18-crown-6 (DB18C6) crown ether and showed the potential of these fibers for the selective recovery of K+ from other both mono- and divalent ions in aqueous solutions. Nanofibers were characterized

  10. Design and Characterization of Electrospun Polyamide Nanofiber Media for Air Filtration Applications

    Directory of Open Access Journals (Sweden)

    Jonas Matulevicius

    2014-01-01

    Full Text Available Electrospun polyamide 6 (PA 6 and polyamide 6/6 (PA 6/6 nanofibers were produced in order to investigate their experimental characteristics with the goal of obtaining filtration relevant fiber media. The experimental design model of each PA nanofibers contained the following variables: polymer concentration, ratio of solvents, nanofiber media collection time, tip-to-collector distance, and the deposition voltage. The average diameter of the fibers, their morphology, basis weight, thickness, and resulting media solidity were investigated. Effects of each variable on the essential characteristics of PA 6/6 and PA 6 nanofiber media were studied. The comparative analysis of the obtained PA 6/6 and PA 6 nanofiber characteristics revealed that PA 6/6 had higher potential to be used in filtration applications. Based on the experimental results, the graphical representation—response surfaces—for obtaining nanofiber media with the desirable fiber diameter and basis weight characteristics were derived. Based on the modelling results the nanofiber filter media (mats were fabricated. Filtration results revealed that nanofiber filter media electrospun from PA6/6 8% (w/vol solutions with the smallest fiber diameters (62–66 nm had the highest filtration efficiency (PA6/6_30 = 84.9–90.9% and the highest quality factor (PA6/6_10 = 0.0486–0.0749 Pa−1.

  11. Superhydrophilicity of novel anodic alumina nanofibers films and their formation mechanism

    Science.gov (United States)

    Peng, Rong; Yang, Wulin; Fu, Licai; Zhu, Jiajun; Li, Deyi; Zhou, Lingping

    2017-06-01

    A novel anodic alumina nanofibers structure, which is different from the traditional porous anodic structure, has been quickly fabricated via anodizing in a new electrolyte, pyrophosphoric acid. The effects of the solution concentration and the anodizing time on the formation of the anodic alumina nanofibers were analyzed. The results show that the nanostructure of anodic alumina can change to the nanofiber oxide from the porous oxide by increasing the solution concentration. Prolonging the anodizing time is beneficial to obtain alumina nanofibers at high solution concentration. Growth behavior of the alumina nanofibers was also discussed by scanning electron microscopy observations. Owing to the unique hexagonal structure of anodic alumina as well as the preferential chemical dissolution between the porous anodic alumina and the anodic alumina nanotips, the slightly soluble anodic alumina nanotips could form novel alumina nanofibers during anodizing. The results show that the nanofibers-covered aluminum surface exhibits superhydrophilic property, with a near-zero water contact angle. Such alumina nanofibers with superhydrophilic property could be used for various potential applications.

  12. High-Temperature Stable Anatase Titanium Oxide Nanofibers for Lithium-Ion Battery Anodes.

    Science.gov (United States)

    Lee, Sangkyu; Eom, Wonsik; Park, Hun; Han, Tae Hee

    2017-08-02

    Control of the crystal structure of electrochemically active materials is an important approach to fabricating high-performance electrodes for lithium-ion batteries (LIBs). Here, we report a methodology for controlling the crystal structure of TiO 2 nanofibers by adding aluminum isopropoxide to a common sol-gel precursor solution utilized to create TiO 2 nanofibers. The introduction of aluminum cations impedes the phase transformation of electrospun TiO 2 nanofibers from the anatase to the rutile phase, which inevitably occurs in the typical annealing process utilized for the formation of TiO 2 crystals. As a result, high-temperature stable anatase TiO 2 nanofibers were created in which the crystal structure was well-maintained even at high annealing temperatures of up to 700 °C. Finally, the resulting anatase TiO 2 nanofibers were utilized to prepare LIB anodes, and their electrochemical performance was compared to pristine TiO 2 nanofibers that contain both anatase and rutile phases. Compared to the electrode prepared with pristine TiO 2 nanofibers, the electrode prepared with anatase TiO 2 nanofibers exhibited excellent electrochemical performances such as an initial Coulombic efficiency of 83.9%, a capacity retention of 89.5% after 100 cycles, and a rate capability of 48.5% at a current density of 10 C (1 C = 200 mA g -1 ).

  13. Electrospun Xanthan gum-Chitosan nanofibers as delivery carrier of hydrophobic bioactives

    DEFF Research Database (Denmark)

    Shekarforoush, Elhamalsadat; Ajalloueian, Fatemeh; Zeng, Guanghong

    2018-01-01

    Viscoelastic gels of xanthan gum-chitosan(X-Ch) were electrospun to produce nanofibers, stable in aqueous media, for the encapsulation and release of curcumin (Cu). After 120h, the nanofibers released lower amount of curcumin (∼20%) at pH 2.2 comparatively to the release in neutral media (∼50...

  14. Electrical properties of in-situ grown and transferred organic nanofibers

    DEFF Research Database (Denmark)

    Oliveira Hansen, Roana Melina de; Madsen, Morten; Kjelstrup-Hansen, Jakob

    2010-01-01

    Para-hexaphenylene (p6P) molecules have the ability to self-assemble into organic nanofibers, which exhibit a range of interesting optical and optoelectronic properties such as intense, polarized luminescence, waveguiding and lasing. The nanofibers are typically grown on specific single...

  15. Improvement of Polylactide Properties through Cellulose Nanocrystals Embedded in Poly(Vinyl Alcohol) Electrospun Nanofibers.

    Science.gov (United States)

    López de Dicastillo, Carol; Garrido, Luan; Alvarado, Nancy; Romero, Julio; Palma, Juan Luis; Galotto, Maria Jose

    2017-05-11

    Electrospun nanofibers of poly (vinyl alcohol) (PV) were obtained to improve dispersion of cellulose nanocrystals (CNC) within hydrophobic biopolymeric matrices, such as poly(lactic acid) (PLA). Electrospun nanofibers (PV/CNC) n were successfully obtained with a final concentration of 23% ( w / w ) of CNC. Morphological, structural and thermal properties of developed CNC and electrospun nanofibers were characterized. X-ray diffraction and thermal analysis revealed that the crystallinity of PV was reduced by the electrospinning process, and the incorporation of CNC increased the thermal stability of biodegradable nanofibers. Interactions between CNC and PV polymer also enhanced the thermal stability of CNC and improved the dispersion of CNC within the PLA matrix. PLA materials with CNC lyophilized were also casted in order to compare the properties with materials based on CNC containing nanofibers. Nanofibers and CNC were incorporated into PLA at three concentrations: 0.5%, 1% and 3% (CNC respect to polymer weight) and nanocomposites were fully characterized. Overall, nanofibers containing CNC positively modified the physical properties of PLA materials, such as the crystallinity degree of PLA which was greatly enhanced. Specifically, materials with 1% nanofiber 1PLA(PV/CNC) n presented highest improvements related to mechanical and barrier properties; elongation at break was enhanced almost four times and the permeation of oxygen was reduced by approximately 30%.

  16. Preparation of porous carbon nanofibers derived from PBI/PLLA for supercapacitor electrodes.

    Science.gov (United States)

    Jung, Kyung-Hye; Ferraris, John P

    2016-10-21

    Porous carbon nanofibers were prepared by electrospinning blend solutions of polybenzimidazole/poly-L-lactic acid (PBI/PLLA) and carbonization. During thermal treatment, PLLA was decomposed, resulting in the creation of pores in the carbon nanofibers. From SEM images, it is shown that carbon nanofibers had diameters in the range of 100-200 nm. The conversion of PBI to carbon was confirmed by Raman spectroscopy, and the surface area and pore volume of carbon nanofibers were determined using nitrogen adsorption/desorption analyses. To investigate electrochemical performances, coin-type cells were assembled using free-standing carbon nanofiber electrodes and ionic liquid electrolyte. cyclic voltammetry studies show that the PBI/PLLA-derived porous carbon nanofiber electrodes have higher capacitance due to lower electrochemical impedance compared to carbon nanofiber electrode from PBI only. These porous carbon nanofibers were activated using ammonia for further porosity improvement and annealed to remove the surface functional groups to better match the polarity of electrode and electrolyte. Ragone plots, correlating energy density with power density calculated from galvanostatic charge-discharge curves, reveal that activation/annealing further improves energy and power densities.

  17. Polyelectrolyte-Functionalized Nanofiber Mats Control the Collection and Inactivation of Escherichia coli

    Directory of Open Access Journals (Sweden)

    Katrina A. Rieger

    2016-04-01

    Full Text Available Quantifying the effect that nanofiber mat chemistry and hydrophilicity have on microorganism collection and inactivation is critical in biomedical applications. In this study, the collection and inactivation of Escherichia coli K12 was examined using cellulose nanofiber mats that were surface-functionalized using three polyelectrolytes: poly (acrylic acid (PAA, chitosan (CS, and polydiallyldimethylammonium chloride (pDADMAC. The polyelectrolyte functionalized nanofiber mats retained the cylindrical morphology and average fiber diameter (~0.84 µm of the underlying cellulose nanofibers. X-ray photoelectron spectroscopy (XPS and contact angle measurements confirmed the presence of polycations or polyanions on the surface of the nanofiber mats. Both the control cellulose and pDADMAC-functionalized nanofiber mats exhibited a high collection of E. coli K12, which suggests that mat hydrophilicity may play a larger role than surface charge on cell collection. While the minimum concentration of polycations needed to inhibit E. coli K12 was 800 µg/mL for both CS and pDADMAC, once immobilized, pDADMAC-functionalized nanofiber mats exhibited a higher inactivation of E. coli K12, (~97%. Here, we demonstrate that the collection and inactivation of microorganisms by electrospun cellulose nanofiber mats can be tailored through a facile polyelectrolyte functionalization process.

  18. Polyelectrolyte-Functionalized Nanofiber Mats Control the Collection and Inactivation of Escherichia coli

    Science.gov (United States)

    Rieger, Katrina A.; Porter, Michael; Schiffman, Jessica D.

    2016-01-01

    Quantifying the effect that nanofiber mat chemistry and hydrophilicity have on microorganism collection and inactivation is critical in biomedical applications. In this study, the collection and inactivation of Escherichia coli K12 was examined using cellulose nanofiber mats that were surface-functionalized using three polyelectrolytes: poly (acrylic acid) (PAA), chitosan (CS), and polydiallyldimethylammonium chloride (pDADMAC). The polyelectrolyte functionalized nanofiber mats retained the cylindrical morphology and average fiber diameter (~0.84 µm) of the underlying cellulose nanofibers. X-ray photoelectron spectroscopy (XPS) and contact angle measurements confirmed the presence of polycations or polyanions on the surface of the nanofiber mats. Both the control cellulose and pDADMAC-functionalized nanofiber mats exhibited a high collection of E. coli K12, which suggests that mat hydrophilicity may play a larger role than surface charge on cell collection. While the minimum concentration of polycations needed to inhibit E. coli K12 was 800 µg/mL for both CS and pDADMAC, once immobilized, pDADMAC-functionalized nanofiber mats exhibited a higher inactivation of E. coli K12, (~97%). Here, we demonstrate that the collection and inactivation of microorganisms by electrospun cellulose nanofiber mats can be tailored through a facile polyelectrolyte functionalization process. PMID:28773422

  19. Electrospun polyvinylpyrrolidone (PVP)/green tea extract composite nanofiber mats and their antioxidant activities

    Science.gov (United States)

    Pusporini, Pusporini; Edikresnha, Dhewa; Sriyanti, Ida; Suciati, Tri; Miftahul Munir, Muhammad; Khairurrijal, Khairurrijal

    2018-05-01

    Electrospinning was employed to make PVP (polyvinylpyrrolidone)/GTE (green tea extract) composite nanofiber mats. The electrospun PVP nanofiber mat as well as the PVP/GTE nanofiber mats were uniform. The average fiber diameter of PVP/GTE composite nanofiber mat decreased with increasing the GTE weight fraction (or decreasing the PVP weight fraction) in the PVP/GTE solution because the PVP/GTE solution concentration decreased. Then, the broad FTIR peak representing the stretching vibrations of O–H in hydroxyl groups of phenols and the stretching of N–H in amine groups of the GTE paste shifted to higher wavenumbers in the PVP/GTE composite nanofiber mats. These peak shifts implied that PVP and catechins of GTE in the PVP/GTE composite nanofiber mats had intermolecular interactions via hydrogen bonds between carbonyl groups of PVP and hydroxyl groups of catechins in GTE. Lastly, the antioxidant activity of the PVP/GTE composite nanofiber mat increased with reducing the average fiber diameter because the amount of catechins in the composite nanofiber mat increased with the increase of surface area due to the reduction of the average fiber diameter.

  20. Effects of Schwann cell alignment along the oriented electrospun chitosan nanofibers on nerve regeneration.

    Science.gov (United States)

    Wang, Wei; Itoh, Soichiro; Konno, Katsumi; Kikkawa, Takeshi; Ichinose, Shizuko; Sakai, Katsuyoshi; Ohkuma, Tsuneo; Watabe, Kazuhiko

    2009-12-15

    We have constructed a chitosan nonwoven nanofiber mesh tube consisting of oriented fibers by the electrospinning method. The efficacy of oriented nanofibers on Schwann cell alignment and positive effect of this tube on peripheral nerve regeneration were confirmed. The physical properties of the chitosan nanofiber mesh sheets prepared by electrospinning with or without fiber orientation were characterized. Then, immortalized Schwann cells were cultured on these sheets. Furthermore, the chitosan nanofiber mesh tubes with or without orientation, and bilayered chitosan mesh tube with an inner layer of oriented nanofibers and an outer layer of randomized nanofibers were bridgegrafted into rat sciatic nerve defect. As a result of fiber orientation, the tensile strength along the axis of the sheet increased. Because Schwann cells aligned along the nanofibers, oriented fibrous sheets could exhibit a Schwann cell column. Functional recovery and electrophysiological recovery occurred in time in the oriented group as well as in the bilayered group, and approximately matched those in the isograft. Furthermore, histological analysis revealed that the sprouting of myelinated axons occurred vigorously followed by axonal maturation in the isograft, oriented, and bilayered group in the order. The oriented chitosan nanofiber mesh tube may be a promising substitute for autogenous nerve graft.

  1. Graphene-doped carbon/Fe3O4 porous nanofibers with hierarchical band construction as high-performance anodes for lithium-ion batteries

    International Nuclear Information System (INIS)

    He, Jianxin; Zhao, Shuyuan; Lian, Yanping; Zhou, Mengjuan; Wang, Lidan; Ding, Bin; Cui, Shizhong

    2017-01-01

    Highlights: • GN@C/Fe 3 O 4 are synthesized via in-situ electrospinning and thermal treatment. • GN@C/Fe 3 O 4 show unique dark/light banding with a hierarchical porous structure. • Doped graphene induces a uniform distribution of smaller size Fe 3 O 4 nanoparticles. • Doped graphene provides more active sites and accommodate the volume change. • GN@C/Fe 3 O 4 electrode displays a reversible capacity of 872 mAh/g after 100 cycles. - Abstract: Porous graphene-doped carbon/Fe 3 O 4 (GN@C/Fe 3 O 4 ) nanofibers are synthesized via in-situ electrospinning and subsequent thermal treatment for use as lithium-ion battery anode materials. A polyacrylonitrile (PAN)/polymethyl methacrylate (PMMA) solution containing ferric acetylacetone and graphene oxide nanosheets is used as the electrospinning precursor solution. The resulting porous GN@C/Fe 3 O 4 nanofibers show unique dark/light banding and a hierarchical porous structure. These nanofibers have a Brunauer–Emmett–Teller (BET) specific surface area of 323.0 m 2 /g with a total pore volume of 0.337 cm 3 /g, which is significantly greater than that of a sample without graphene and C/Fe 3 O 4 nanofibers. The GN@C/Fe 3 O 4 nanofiber electrode displays a reversible capacity of 872 mAh/g at a current density of 100 mA/g after 100 cycles, excellent cycling stability, and superior rate capability (455 mA/g at 5 A/g). The excellent performance of porous GN@C/Fe 3 O 4 is attributed to the material’s unique structure, including its striped topography, hierarchical porous structure, and inlaid flexible graphene, which not only provides more accessible active sites for lithium-ion insertion and high-efficiency transport pathways for ions and electrons, but also accommodates the volume change associated with lithium insertion/extraction. Moreover, the zero-valent iron and graphene in the porous nanofibers enhance the conductivity of the electrodes.

  2. Poly(hydroxybutyrate)/cellulose acetate blend nanofiber scaffolds: Preparation, characterization and cytocompatibility

    Energy Technology Data Exchange (ETDEWEB)

    Zhijiang, Cai, E-mail: caizhijiang@hotmail.com [School of Textiles, Tianjin Polytechnic University, Tianjin 300387 (China); State Key Laboratory of Hollow Fiber Membrane Material and Processes, No 399 BingShuiXi Street, XiQing District, Tianjin, China, 300387 (China); Yi, Xu; Haizheng, Yang; Jia, Jianru; Liu, Yuanpei [School of Textiles, Tianjin Polytechnic University, Tianjin 300387 (China)

    2016-01-01

    Poly(hydroxybutyrate) (PHB)/cellulose acetate (CA) blend nanofiber scaffolds were fabricated by electrospinning using the blends of chloroform and DMF as solvent. The blend nanofiber scaffolds were characterized by SEM, FTIR, XRD, DSC, contact angle and tensile test. The blend nanofibers exhibited cylindrical, uniform, bead-free and random orientation with the diameter ranged from 80–680 nm. The scaffolds had very well interconnected porous fibrous network structure and large aspect surface areas. It was found that the presence of CA affected the crystallization of PHB due to formation of intermolecular hydrogen bonds, which restricted the preferential orientation of PHB molecules. The DSC result showed that the PHB and CA were miscible in the blend nanofiber. An increase in the glass transition temperature was observed with increasing CA content. Additionally, the mechanical properties of blend nanofiber scaffolds were largely influenced by the weight ratio of PHB/CA. The tensile strength, yield strength and elongation at break of the blend nanofiber scaffolds increased from 3.3 ± 0.35 MPa, 2.8 ± 0.26 MPa, and 8 ± 0.77% to 5.05 ± 0.52 MPa, 4.6 ± 0.82 MPa, and 17.6 ± 1.24% by increasing PHB content from 60% to 90%, respectively. The water contact angle of blend nanofiber scaffolds decreased about 50% from 112 ± 2.1° to 60 ± 0.75°. The biodegradability was evaluated by in vitro degradation test and the results revealed that the blend nanofiber scaffolds showed much higher degradation rates than the neat PHB. The cytocompatibility of the blend nanofiber scaffolds was preliminarily evaluated by cell adhesion studies. The cells incubated with PHB/CA blend nanofiber scaffold for 48 h were capable of forming cell adhesion and proliferation. It showed much better biocompatibility than pure PHB film. Thus, the prepared PHB/CA blend nanofiber scaffolds are bioactive and may be more suitable for cell proliferation suggesting that these scaffolds can be used for

  3. Computational analysis of electrical conduction in hybrid nanomaterials with embedded non-penetrating conductive particles

    Science.gov (United States)

    Cai, Jizhe; Naraghi, Mohammad

    2016-08-01

    In this work, a comprehensive multi-resolution two-dimensional (2D) resistor network model is proposed to analyze the electrical conductivity of hybrid nanomaterials made of insulating matrix with conductive particles such as CNT reinforced nanocomposites and thick film resistors. Unlike existing approaches, our model takes into account the impenetrability of the particles and their random placement within the matrix. Moreover, our model presents a detailed description of intra-particle conductivity via finite element analysis, which to the authors’ best knowledge has not been addressed before. The inter-particle conductivity is assumed to be primarily due to electron tunneling. The model is then used to predict the electrical conductivity of electrospun carbon nanofibers as a function of microstructural parameters such as turbostratic domain alignment and aspect ratio. To simulate the microstructure of single CNF, randomly positioned nucleation sites were seeded and grown as turbostratic particles with anisotropic growth rates. Particle growth was in steps and growth of each particle in each direction was stopped upon contact with other particles. The study points to the significant contribution of both intra-particle and inter-particle conductivity to the overall conductivity of hybrid composites. Influence of particle alignment and anisotropic growth rate ratio on electrical conductivity is also discussed. The results show that partial alignment in contrast to complete alignment can result in maximum electrical conductivity of whole CNF. High degrees of alignment can adversely affect conductivity by lowering the probability of the formation of a conductive path. The results demonstrate approaches to enhance electrical conductivity of hybrid materials through controlling their microstructure which is applicable not only to carbon nanofibers, but also many other types of hybrid composites such as thick film resistors.

  4. Fibrous guided tissue regeneration membrane loaded with anti-inflammatory agent prepared by coaxial electrospinning for the purpose of controlled release

    Energy Technology Data Exchange (ETDEWEB)

    He, Min; Xue, Jiajia [Beijing Laboratory of Biomedical Materials, Beijing University of Chemical Technology, Beijing 100029 (China); Geng, Huan; Gu, Hao [State Key Laboratory of Organic–Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029 (China); Chen, Dafu [Laboratory of Bone Tissue Engineering of Beijing Research Institute of Traumatology and Orthopaedics, Beijing 100035 (China); Shi, Rui, E-mail: sharell@126.com [Laboratory of Bone Tissue Engineering of Beijing Research Institute of Traumatology and Orthopaedics, Beijing 100035 (China); Zhang, Liqun, E-mail: zhanglq@mail.buct.edu.cn [Beijing Laboratory of Biomedical Materials, Beijing University of Chemical Technology, Beijing 100029 (China); State Key Laboratory of Organic–Inorganic Composites, Beijing University of Chemical Technology, Beijing 100029 (China)

    2015-04-30

    Graphical abstract: The metronidazole released from PCL/gelatin core/sheath nanofiber membranes can effectively inhibit the colonization of anerobic bacteria. - Highlights: • Core/sheath PCL/gelatin nanofiber membrane loaded with metronidazole in a wide range of drug loading (5–35 wt.%) were successfully fabricated in good quality. • The encapsulation of gelatin can effectively alleviate the initial burst release of drugs. • The membrane can inhibit the growth of bacteria as the drug content reaches 10% (w/w), and the bacterial inhibition ability can effectively last at least 4 weeks. • The encapsulation of gelatin can overcome the disadvantage of PCL's hydrophobicity, which can effectively promote the adhesion and proliferation of cells. - Abstract: Here, with the aim of inhibiting inflammation during guided tissue regeneration membrane (GTRM) implant surgery, coaxial electrospinning was used to fabricate drug-loaded core/sheath nanofiber GTRMs capable of controlled drug release. Various amounts of the anti-inflammatory agent metronidazole (MNA) were encapsulated into the core/sheath nanofibers (where PCL was the core, gelatin the sheath, and the gelatin shell was crosslinked with genipin) in order to establish the minimal drug content necessary to achieve the appropriate anti-inflammatory effect. By using TEM and SEM, the core/sheath structure was confirmed. In vitro drug disolution results showed that the core/sheath nanofibers exhibited sustained release profiles that were superior to those nanofibers produced by blending electrospinning. Additionally, the membrane significantly inhibited the colonization of anaerobic bacteria. Furthermore, with gelatin as a shell, the core/shell nanofiber membranes showed improved hydrophilicity, which resulted in better cell adhesion and proliferation without cytotoxicity. Therefore, in this study, a simple and effective coaxial electrospinning approach was demonstrated for the fabrication of anti

  5. Polyaniline-nylon-6 electrospun nanofibers for headspace adsorptive microextraction

    International Nuclear Information System (INIS)

    Bagheri, Habib; Aghakhani, Ali

    2012-01-01

    Highlights: ► Polyaniline–polyamide nanofiber mat was fabricated by electrospinning technology. ► Electrospun nanofiber was used for extraction of chlorobenzenes from aquatic media. ► A method based on headspace adsorptive microextraction and GC–MS was developed. - Abstract: A headspace adsorptive microextraction technique was developed using a novel polyaniline-nylon-6 (PANI-N6) nanofiber sheet, fabricated by electrospinning. The homogeneity and the porosity of the prepared PANI-N6 sheet were studied using the scanning electron microscopy (SEM) and nanofibers diameters were found to be around 200 nm. The novel nanofiber sheet was examined as an extracting medium to isolate some selected chlorobenzenes (CBs), as model compounds, from aquatic media. The extracted analytes were desorbed using μL-amounts of solvent and eventually an aliquot of extractant was injected into gas chromatography–mass spectrometry (GC–MS). Various parameters affecting the extraction and desorption processes were optimized. The developed method proved to be convenient and offers sufficient sensitivity and a good reproducibility. Limits of detection achieved for CBs with the developed analytical procedure ranged from 19 to 33 ng L −1 , while limits of quantification were from 50 to 60 ng L −1 . The relative standard deviations (RSD) at a concentration level of 0.1 ng mL −1 and 1 ng mL −1 were in the range of 8–14% and 5–11% (n = 3), respectively. The calibration curves of analytes were investigated in the range of 50–1000 ng L −1 and R 2 between 0.9739 and 0.9932 were obtained. The developed method was successfully applied to the extraction of selected CBs from tap and river water samples. The relative recovery (RR) percentage obtained for the spiked real water samples at 0.1 ng mL −1 and 1 ng mL −1 level were 93–103% and 95–104%, respectively. The whole procedure showed to be conveniently applicable and quite easy to handle.

  6. Polyaniline-nylon-6 electrospun nanofibers for headspace adsorptive microextraction

    Energy Technology Data Exchange (ETDEWEB)

    Bagheri, Habib, E-mail: bagheri@sharif.edu [Environmental and Bio-Analytical Laboratories, Department of Chemistry, Sharif University of Technology, P.O. Box 11365-9516, Tehran (Iran, Islamic Republic of); Aghakhani, Ali [Environmental and Bio-Analytical Laboratories, Department of Chemistry, Sharif University of Technology, P.O. Box 11365-9516, Tehran (Iran, Islamic Republic of)

    2012-02-03

    Highlights: Black-Right-Pointing-Pointer Polyaniline-polyamide nanofiber mat was fabricated by electrospinning technology. Black-Right-Pointing-Pointer Electrospun nanofiber was used for extraction of chlorobenzenes from aquatic media. Black-Right-Pointing-Pointer A method based on headspace adsorptive microextraction and GC-MS was developed. - Abstract: A headspace adsorptive microextraction technique was developed using a novel polyaniline-nylon-6 (PANI-N6) nanofiber sheet, fabricated by electrospinning. The homogeneity and the porosity of the prepared PANI-N6 sheet were studied using the scanning electron microscopy (SEM) and nanofibers diameters were found to be around 200 nm. The novel nanofiber sheet was examined as an extracting medium to isolate some selected chlorobenzenes (CBs), as model compounds, from aquatic media. The extracted analytes were desorbed using {mu}L-amounts of solvent and eventually an aliquot of extractant was injected into gas chromatography-mass spectrometry (GC-MS). Various parameters affecting the extraction and desorption processes were optimized. The developed method proved to be convenient and offers sufficient sensitivity and a good reproducibility. Limits of detection achieved for CBs with the developed analytical procedure ranged from 19 to 33 ng L{sup -1}, while limits of quantification were from 50 to 60 ng L{sup -1}. The relative standard deviations (RSD) at a concentration level of 0.1 ng mL{sup -1} and 1 ng mL{sup -1} were in the range of 8-14% and 5-11% (n = 3), respectively. The calibration curves of analytes were investigated in the range of 50-1000 ng L{sup -1} and R{sup 2} between 0.9739 and 0.9932 were obtained. The developed method was successfully applied to the extraction of selected CBs from tap and river water samples. The relative recovery (RR) percentage obtained for the spiked real water samples at 0.1 ng mL{sup -1} and 1 ng mL{sup -1} level were 93-103% and 95-104%, respectively. The whole procedure showed

  7. Fabrication, functionalization, and application of electrospun biopolymer nanofibers.

    Science.gov (United States)

    Kriegel, Christina; Arecchi, Alessandra; Arrechi, Alessandra; Kit, Kevin; McClements, D J; Weiss, Jochen

    2008-09-01

    The use of novel nanostructured materials has attracted considerable interest in the food industry for their utilization as highly functional ingredients, high-performance packaging materials, processing aids, and food quality and safety sensors. Most previous application interest has focused on the development of nanoparticles. However, more recently, the ability to produce non-woven mats composed of nanofibers that can be used in food applications is beginning to be investigated. Electrospinning is a novel fabrication technique that can be used to produce fibers with diameters below 100 nm from (bio-) polymer solutions. These nanofibers have been shown to possess unique properties that distinguish them from non-woven fibers produced by other methods, e.g., melt-blowing. This is because first the process involved results in a high orientation of polymers within the fibers that leads to mechanically superior properties, e.g., increased tensile strengths. Second, during the spinning of the fibers from polymer solutions, the solvent is rapidly evaporated allowing the production of fibers composed of polymer blends that would typically phase separate if spun with other processes. Third, the small dimensions of the fibers lead to very high specific surface areas. Because of this the fiber properties may be greatly influenced by surface properties giving rise to fiber functionalities not found in fibers of larger sizes. For food applications, the fibers may find uses as ingredients if they are composed solely of edible polymers and GRAS ingredients, (e.g., fibers could contain functional ingredients such as nutraceuticals, antioxidants, antimicrobials, and flavors), as active packaging materials or as processing aids (e.g., catalytic reactors, membranes, filters (Lala et al., 2007), and sensors (Manesh et al., 2007; Ren et al., 2006; Sawicka et al., 2005). This review is therefore intended to introduce interested food and agricultural scientists to the concept of nano-fiber

  8. Coaxial electrospun polyurethane core-shell nanofibers for shape memory and antibacterial nanomaterials

    Directory of Open Access Journals (Sweden)

    2011-02-01

    Full Text Available A novel kind of shape memory polyurethane (SMPU nanofibers with core-shell nanostructure is fabricated using coaxial electrospinning. Transmission electron microscopy (TEM and scanning electron microscopy (SEM results show that nanofibers with core-shell structure or bead-on-string structure can be electrospun successfully from the core solution of polycaprolactone based SMPU (CLSMPU and shell solution of pyridine containing polyurethane (PySMPU. In addition to the excellent shape memory effect with good shape fixity, excellent antibacterial activity against both gramnegative bacteria and gram-positive bacteria are achieved in the CLSMPU-PySMPU core-shell nanofiber. Finally, it is proposed that the antibacterial mechanism should be resulted from the PySMPU shell materials containing amido group in γ position and the high surface area per unit mass of nanofibers. Thus, the CLSMPU-PySMPU core shell nanofibers can be used as both shape memory nanomaterials and antibacterial nanomaterials.

  9. Ferromagnetic Behaviors in Fe-Doped NiO Nanofibers Synthesized by Electrospinning Method

    Directory of Open Access Journals (Sweden)

    Yi-Dong Luo

    2013-01-01

    Full Text Available Ni1−xFexO nanofibers with different Fe doping concentration have been synthesized by electrospinning method. An analysis of the phase composition and microstructure shows that Fe doping has no influence on the crystal structure and morphology of NiO nanofibers, which reveals that the doped Fe ions have been incorporated into the NiO host lattice. Pure NiO without Fe doping is antiferromagnetic, yet all the Fe-doped NiO nanofiber samples show obvious room-temperature ferromagnetic properties. The saturation magnetization of the nanofibers can be enhanced with increasing Fe doping concentration, which can be ascribed to the double exchange mechanism through the doped Fe ions and free charge carriers. In addition, it was found that the diameter of nanofibers has significant impact on the ferromagnetic properties, which was discussed in detail.

  10. Mechanical characterization of TiO{sub 2} nanofibers produced by different electrospinning techniques

    Energy Technology Data Exchange (ETDEWEB)

    Vahtrus, Mikk [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Šutka, Andris [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Institute of Silicate Materials, Riga Technical University, P. Valdena 3/7, Riga LV-1048 (Latvia); Institute of Technical Physics, Riga Technical University, P. Valdena 3, Riga LV-1048 (Latvia); Vlassov, Sergei, E-mail: vlassovs@ut.ee [Institute of Solid State Physics, University of Latvia, Kengaraga 8, LV-1063 Riga (Latvia); Šutka, Anna [Institute of Textile Technology and Design, Riga Technical University, Riga LV-1048 (Latvia); Laboratory of Biomass Eco-Efficient Conversation, Latvian State Institute of Wood Chemistry, Dzerbenes Street 27, Riga LV-1006 (Latvia); Polyakov, Boris [Institute of Solid State Physics, University of Latvia, Kengaraga 8, LV-1063 Riga (Latvia); Saar, Rando; Dorogin, Leonid; Lõhmus, Rünno [Institute of Physics, University of Tartu, Ravila 14c, 50412 Tartu (Estonia); Materials Technologies Competence Centre, Riia 185b, 51014 Tartu (Estonia)

    2015-02-15

    In this work TiO{sub 2} nanofibers produced by needle and needleless electrospinning processes from the same precursor were characterized and compared using Raman spectroscopy, transmission electron microscopy (TEM), scanning electron microscopy (SEM) and in situ SEM nanomechanical testing. Phase composition, morphology, Young's modulus and bending strength values were found. Weibull statistics was used to evaluate and compare uniformity of mechanical properties of nanofibers produced by two different methods. It is shown that both methods yield nanofibers with very similar properties. - Graphical abstract: Display Omitted - Highlights: • TiO{sub 2} nanofibers were produced by needle and needleless electrospinning processes. • Structure was studied by Raman spectroscopy and electron microscopy methods. • Mechanical properties were measured using advanced in situ SEM cantilevered beam bending technique. • Both methods yield nanofibers with very similar properties.

  11. Experimental Investigation of the Properties of Electrospun Nanofibers for Potential Medical Application

    Directory of Open Access Journals (Sweden)

    Anhui Wang

    2015-01-01

    Full Text Available Polymer based nanofibers using ethylene-co-vinyl alcohol (EVOH were fabricated by electrospinning technology. The nanofibers were studied for potential use as dressing materials for skin wounds treatment. Properties closely related to the clinical requirements for wound dressing were investigated, including the fluid uptake ability (FUA, the water vapour transmission rate (WVTR, the bacteria control ability of nanofibers encapsulated with different antibacterial drugs, and Ag of various concentrations. Nanofibre degradation under different environmental conditions was also studied for the prospect of long term usage. The finding confirms the potential of EVOH nanofibers for wound dressing application, including the superior performance compared to cotton gauze and the strong germ killing capacity when Ag particles are present in the nanofibers.

  12. Characterization and application of zeolitic imidazolate framework-8@polyvinyl alcohol nanofibers mats prepared by electrospinning

    Science.gov (United States)

    Fan, Xiaoxiao; Yu, Linling; Li, Lianghao; Yang, Cao; Wen, Junjie; Ye, Xiaokun; Cheng, Jianhua; Hu, Yongyou

    2017-02-01

    In this study, Zeolitic imidazolate framework-8@polyvinyl alcohol (ZIF-8@PVA) nanofibers were creatively fabricated by electrospinning technique, and the nanofibers membranes were characterized by SEM, TEM, XRD, FTIR, TG, DSC, DTA, BET. Its thermal stability, mechanical property, water stability and adsorption nature were also performed. The optimized fabrication parameter of the ZIF-8@PVA was 10 wt% and the uniform diameters of the nanofibers has been obtained. In addition, the ZIF-8@PVA nanofibers displayed unique properties such as a water stable and flexible structure. The adsorption test for Congo red treatment revealed that the nanofibers had a great adsorption performance. The results indicated that the nonwoven fiber mats had a great potential as a new type of membrane adsorbents in wastewater purification. The possible mechanism of CR adsorption onto ZIF-8@PVA was researched.

  13. Ideal asymmetric supercapacitors consisting of polyaniline nanofibers and graphene nanosheets with proper complementary potential windows

    International Nuclear Information System (INIS)

    Hung, P.-J.; Chang, K.-H.; Lee, Y.-F.; Hu, C.-C.; Lin, K.-M.

    2010-01-01

    Polyaniline (PANI) nanofibers are synthesized via a chemical method of rapid mixing for the application of asymmetric supercapacitors. The diameter and aspect ratio of PANI nanofibers is found to be controllable by varying the aniline/oxidant concentration ratio. The ideal capacitive responses of PANI nanofibers between 0.2 and 0.7 V (vs. Ag/AgCl) in concentrated acidic media are demonstrated by cyclic voltammetric (CV) and electrochemical impedance spectroscopic (EIS) analyses coupled with a schematic equivalent-circuit model. The morphologies and textures of nanofibers are examined by scanning electron microscopic (SEM), transmission electron microscopic (TEM) and Fourier transform infrared-attenuated total reflectance (FTIR-ATR) spectroscopic analyses. An aqueous asymmetric supercapacitor, consisting of a PANI nanofiber cathode and a graphene anode, with proper complementary potential windows is demonstrated in this work, which shows the device energy and power densities of 4.86 Wh kg -1 and 8.75 kW kg -1 , respectively.

  14. The fabrication and testing of electrospun silica nanofiber membranes for the detection of proteins

    International Nuclear Information System (INIS)

    Tsou, P-H; Kameoka, J; Chou, C-K; Saldana, S M; Hung, M-C

    2008-01-01

    In this study, we fabricated electrospun silica nanofiber membranes and investigated their use in biomolecular sensing. The diameter, porosity and surface-to-volume ratio of nanofiber membranes were investigated under different fabrication conditions. Using this type of nanofiber membrane, enzyme-linked immunosorbent assay (ELISA) was performed, and the results were compared with those obtained with conventional ELISA using polystyrene well plates. The minimum detectable concentration was determined as 0.19 ng ml -1 (1.6 pM), which is 32 times lower than that of conventional ELISA. In addition, the detection time for all processes for the nanofiber membrane was reduced to 1 h, compared with 1 day for conventional ELISA. The increased sensitivity, faster reaction time, and affordability of the nanofiber membrane make it well suited for bio-chip use.

  15. Branched carbon nanofiber network synthesis at room temperature using radio frequency supported microwave plasmas

    International Nuclear Information System (INIS)

    Boskovic, Bojan O.; Stolojan, Vlad; Zeze, Dagou A.; Forrest, Roy D.; Silva, S. Ravi P.; Haq, Sajad

    2004-01-01

    Carbon nanofibers have been grown at room temperature using a combination of radio frequency and microwave assisted plasma-enhanced chemical vapor deposition. The nanofibers were grown, using Ni powder catalyst, onto substrates kept at room temperature by using a purposely designed water-cooled sample holder. Branched carbon nanofiber growth was obtained without using a template resulting in interconnected carbon nanofiber network formation on substrates held at room temperature. This method would allow room-temperature direct synthesized nanofiber networks over relatively large areas, for a range of temperature sensitive substrates, such as organic materials, plastics, and other polymers of interest for nanoelectronic two-dimensional networks, nanoelectromechanical devices, nanoactuators, and composite materials

  16. Obtainment of silica nanofiber and its preliminary investigation and its effects as reinforcement in polymeric matrix

    International Nuclear Information System (INIS)

    Teixeira, R.S.; Oliveira, G.L.; Silva, F.D.C.; Teofilo, E. T.; Farias, R.C.; Menezes, R.R.

    2016-01-01

    Silica is widely used as fillers in polymers, and may confer flame retardant characteristics and improve mechanical properties. their use usually occurs as spherical nanoparticles or short fibers of. Studies using this reinforce in the form of nanofibers are promising. This analysis proposes to obtain silica nanofibers by blowspinning method in solution (SBS), and investigate its application in polymeric matrix. To synthesize the silica nanofibers it was used a precursor solution that has been subjected to SBS process and calcined for forming the silica layer. The DR-X indicated the obtainment of amorphous silica phase and SEM showed the the fibers are at the nanometer scale. Silica nanofibers were incorporated into filmogenic solution Polyamide 6. Preliminary results showed no improvement in mechanical properties. Future stages propose to verify that the surface chemical modification of silica nanofibers enables interaction charge / matrix. (author)

  17. A Pendulum-Like Motion of Nanofiber Gel Actuator Synchronized with External Periodic pH Oscillation

    Directory of Open Access Journals (Sweden)

    Shuji Hasimoto

    2011-02-01

    Full Text Available In this study, we succeeded in manufacturing a novel nanofiber hydrogel actuator that caused a bending and stretching motion synchronized with external pH oscillation, based on a bromate/sulfite/ferrocyanide reaction. The novel nanofiber gel actuator was composed of electrospun nanofibers synthesized by copolymerizing acrylic acid and hydrophobic butyl methacrylate as a solubility control site. By changing the electrospinning flow rate, the nanofiber gel actuator introduced an anisotropic internal structure into the gel. Therefore, the unsymmetrical motion of the nanofiber actuator was generated.

  18. Photocatalysis of sub-ppm limonene over multiwalled carbon nanotubes/titania composite nanofiber under visible-light irradiation

    International Nuclear Information System (INIS)

    Jo, Wan-Kuen; Kang, Hyun-Jung

    2015-01-01

    Highlights: • A multiwalled carbon nanotube/titania composite nanofiber (MTCN) was synthesized. • Photocatalytic function of visible-activated MTCN was examined using tubular reactor. • MTCNs could be effectively used for the purification of sub-ppm gas-phase limonene. • The experimental results agreed well with Langmuir–Hinshelwood model. • Certain gas-phase intermediates were determined, but not for adsorbed intermediates. - Abstract: This study was conducted under visible-light exposure to investigate the photocatalytic characteristics of a multiwalled carbon nanotube/titania (TiO 2 ) composite nanofiber (MTCN) using a continuous-flow tubular reactor. The MTCN was prepared by a sol–gel process, followed by an electrospinning technique. The photocatalytic decomposition efficiency for limonene on the MTCN was higher than those obtained from reference TiO 2 nanofibers or P25 TiO 2 , and the experimental results agreed well with the Langmuir–Hinshelwood model. The CO concentrations generated during the photocatalysis did not reach levels toxic to humans. The mineralization efficiency for limonene on the MTCN was also higher than that for P25 TiO 2 . Moreover, the mineralization efficiency obtained using the MTCN increased steeply from 8.3 to 91.1% as the residence time increased from 7.8 to 78.0 s, compared to the increase in the decomposition efficiencies for limonene from 90.1 to 99.9%. Three gas-phase intermediates (methacrolein, acetic acid, and limonene oxide) were quantitatively determined for the photocatalysis for limonene over the MTCN, whereas only two intermediates (acetic acid and limonene oxide) were quantitatively determined over P25 TiO 2 . Other provisional gas-phase intermediates included cyclopropyl methyl ketone and 2-ethylbutanal

  19. Photocatalysis of sub-ppm limonene over multiwalled carbon nanotubes/titania composite nanofiber under visible-light irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Jo, Wan-Kuen, E-mail: wkjo@knu.ac.kr; Kang, Hyun-Jung

    2015-02-11

    Highlights: • A multiwalled carbon nanotube/titania composite nanofiber (MTCN) was synthesized. • Photocatalytic function of visible-activated MTCN was examined using tubular reactor. • MTCNs could be effectively used for the purification of sub-ppm gas-phase limonene. • The experimental results agreed well with Langmuir–Hinshelwood model. • Certain gas-phase intermediates were determined, but not for adsorbed intermediates. - Abstract: This study was conducted under visible-light exposure to investigate the photocatalytic characteristics of a multiwalled carbon nanotube/titania (TiO{sub 2}) composite nanofiber (MTCN) using a continuous-flow tubular reactor. The MTCN was prepared by a sol–gel process, followed by an electrospinning technique. The photocatalytic decomposition efficiency for limonene on the MTCN was higher than those obtained from reference TiO{sub 2} nanofibers or P25 TiO{sub 2}, and the experimental results agreed well with the Langmuir–Hinshelwood model. The CO concentrations generated during the photocatalysis did not reach levels toxic to humans. The mineralization efficiency for limonene on the MTCN was also higher than that for P25 TiO{sub 2}. Moreover, the mineralization efficiency obtained using the MTCN increased steeply from 8.3 to 91.1% as the residence time increased from 7.8 to 78.0 s, compared to the increase in the decomposition efficiencies for limonene from 90.1 to 99.9%. Three gas-phase intermediates (methacrolein, acetic acid, and limonene oxide) were quantitatively determined for the photocatalysis for limonene over the MTCN, whereas only two intermediates (acetic acid and limonene oxide) were quantitatively determined over P25 TiO{sub 2}. Other provisional gas-phase intermediates included cyclopropyl methyl ketone and 2-ethylbutanal.

  20. Preparation, characterization of electrospun meso-hydroxylapatite nanofibers and their sorptions on Co(II)

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Hualin, E-mail: hlwang@hfut.edu.cn [School of Chemical Technology, Hefei University of Technology, Hefei, Anhui 230009 (China); Zhang, Peng; Ma, Xingkong; Jiang, Suwei; Huang, Yan; Zhai, Linfeng [School of Chemical Technology, Hefei University of Technology, Hefei, Anhui 230009 (China); Jiang, Shaotong [School of Biotechnology and Food Engineering, Hefei University of Technology, Hefei, Anhui 230009 (China)

    2014-01-30

    Highlights: • PVA/HA nanofibers could change into meso-HA nanofibers by calcination process. • Sorption of Co(II) on meso-HA was strongly dependent on pH and ionic strength. • Sorption kinetic data were well fitted by the pseudo-second-order rate equation. • Sorption isotherms could be well described by the Langmuir model. • Sorption process of Co(II) on meso-HA nanofibers was spontaneous and endothermic. -- Abstract: In this work, mesoporous hydroxylapatite (meso-HA) nanofibers were prepared via calcination process with polyvinyl alcohol/HA (PVA/HA) hybrid nanofibers fabricated by electrospinning technique as precursors, and the removal efficiency of meso-HA nanofibers toward Co(II) was evaluated via sorption kinetics and sorption isotherms. Furthermore, the sorption behaviors of Co(II) on meso-HA nanofibers were explored as a function of pH, ionic strength, and thermodynamic parameters. There existed hydrogen bonds between HA and PVA matrix in precursor nanofibers which could change into meso-HA nanofibers with main pore diameter at 27 nm and specific surface area at 114.26 m{sup 2}/g by calcination process. The sorption of Co(II) on meso-HA was strongly dependent on pH and ionic strength. Outer-sphere surface complexation or ion exchange was the main mechanisms of Co(II) adsorption on meso-HA at low pH, whereas inner-sphere surface complexation was the main adsorption mechanism at high pH. The sorption kinetic data were well fitted by the pseudo-second-order rate equation. The sorption isotherms could be well described by the Langmuir model. The thermodynamic parameters (ΔH°, ΔS° and ΔG°) calculated from the temperature-dependent sorption isotherms suggested that the sorption process of Co(II) on meso-HA nanofibers was spontaneous and endothermic.

  1. Electrospun PBLG/PLA nanofiber membrane for constructing in vitro 3D model of melanoma.

    Science.gov (United States)

    Wang, Yaping; Qian, Junmin; Liu, Ting; Xu, Weijun; Zhao, Na; Suo, Aili

    2017-07-01

    Though much progress in utilizing tissue engineering technology to investigate tumor development in vitro has been made, the effective management of human melanoma is still a challenge in clinic due to lack of suitable 3D culture systems. In this study, we prepared a poly(γ-benzyl-l-glutamate)/poly(lactic acid) (PBLG/PLA) nanofiber membrane by electrospinning and demonstrated its suitability as a matrix for 3D culture of melanoma cells in vitro. The electrospun PBLG/PLA nanofiber membrane displayed a smooth and uniform fibrous morphology and had a desirable water contact angle of 79.3±0.6°. The average diameter of PBLG/PLA nanofibers was 320.3±95.1nm that was less than that (516.2±163.3nm) of pure PLA nanofibers. The addition of PBLG into PLA decreased the cold crystallization peak of PLA fibers from 93 to 75°C. The in vitro biocompatibility of PBLG/PLA nanofiber membrane was evaluated with B16F10 cells using PLA nanofiber membrane as control. It was found that, compared to PLA nanofiber membrane, PBLG/PLA nanofiber membrane could better support cell viability and proliferation, as indicated by MTT assay and live-dead staining. SEM results revealed that PBLG/PLA rather than PLA nanofiber membrane promoted the generation of tumoroid-like structures. These findings clearly demonstrated that the electrospun PBLG/PLA nanofiber membrane could mimick the extracellular matrix of melanoma microenvironment and be a promising platform for 3D cell culture. Copyright © 2017 Elsevier B.V. All rights reserved.

  2. Effect of Saponification Condition on the Morphology and Diameter of the Electrospun Poly(vinyl acetate) Nanofibers for the Fabrication of Poly(vinyl alcohol) Nanofiber Mats

    OpenAIRE

    Seong Baek Yang; Jong Won Kim; Jeong Hyun Yeum

    2016-01-01

    Novel poly(vinyl alcohol) (PVA) nanofiber mats were prepared for the first time through heterogeneous saponification of electrospun poly(vinyl acetate) (PVAc) nanofibers. The effect of varying the saponification conditions, including temperature, time, and concentration of the alkaline solution, on the morphology of the saponified PVA fibers were evaluated by field-emission scanning electron microscopy. At 25 °C, the saponified PVA fibers exhibited a broad diameter distribution. The average f...

  3. Synergistic effect of carbon nanofiber and sub-micro filamentary nickel nanostrand on the shape memory polymer nanocomposite

    International Nuclear Information System (INIS)

    Lu, Haibao; Leng, Jinsong; Du, Shanyi; Gou, Jihua

    2011-01-01

    This work studies the synergistic effect of carbon nanofiber (CNF) and sub-micro filamentary nickel nanostrand on the thermal and electrical properties, as well as the electro-active shape memory behavior, of a shape memory polymer (SMP) nanocomposite. The combination of electrical CNF and electromagnetic nickel nanostrand is used to render insulating thermo-responsive SMPs conductive. Subsequently, the shape memory behavior of the SMP can be activated by the electrical resistive heating. It is shown that sub-micro filamentary nickel-coated nanostrands significantly improved the electrical conductivity to facilitate the actuation of the SMP nanocomposite despite the low nanostrand volume content and low electrical voltage. Also the CNFs are blended with the SMP resin to facilitate the dispersion of nanostrands and improve the thermal conductivity to accelerate the electro- and thermo-active responses

  4. Conducting Polymers

    Indian Academy of Sciences (India)

    would exhibit electronic conductivity, their conductivities (of compressed pellets) were indeed measured by others, and were found to be .... Polyaniline. Polyphenylene. Polypheny lene- vinylene. Table 1. G!NeRAl I ARTICl! structure. Maximum conductivity Stem Stability. Processability. ~. 1.5 x 105. Reacts with Film not n air.

  5. Electrochemical Performance of Electrospun carbon nanofibers as free-standing and binder-free anodes for Sodium-Ion and Lithium-Ion Batteries

    International Nuclear Information System (INIS)

    Jin, Juan; Shi, Zhi-qiang; Wang, Cheng-yang

    2014-01-01

    Highlights: • Electrospun carbon nanofiber webs were prepared by pyrolysis of polyacrylonitrile. • The webs as binder-free and current collector-free electrodes for SIBs and LIBs. • Different layer spacing and pore size for Li and Na lead different electrochemical behavior. • Electrochemical performances of the electrodes were high. - Abstract: A series of hard carbon nanofiber-based electrodes derived from electrospun polyacrylonitrile (PAN) nanofibers (PAN-CNFs) have been fabricated by stabilization in air at about 280 °C and then carbonization in N 2 at heat treatment temperatures (HTT) between 800 and 1500 °C. The electrochemical performances of the binder-free, current collector-free carbon nanofiber-based anodes in lithium-ion batteries and sodium-ion batteries are systematically investigated and compared. We demonstrate the presence of similar alkali metal insertion mechanisms in both cases, but just the differences of the layer spacing and pore size available for lithium and sodium ion lead the discharge capacity delivered at sloping region and plateau region to vary from the kinds of alkali elements. Although the anodes in sodium-ion batteries show poorer rate capability than that in lithium-ion batteries, they still achieve a reversible sodium intercalation capacity of 275 mAh g −1 and similar cycling stability due to the conductive 3-D network, weakly ordered turbostratic structure and a large interlayer spacing between graphene sheets. The feature of high capacity and stable cycling performance makes PAN-CNFs to be promising candidates as electrodes in rechargeable sodium-ion batteries and lithium-ion batteries

  6. Functional Nanofibers and Colloidal Gels: Key Elements to Enhance Functionality

    Science.gov (United States)

    Vogel, Nancy Amanda

    Nanomaterials bridge the gap between bulk materials and molecular structures and are known for their unique material properties and highly functional nature which make them attractive for a variety of potential applications, from energy storage and pollution sensors to agricultural and biomedical products. These potential applications, coupled with advances in nanotechnology, have generated considerable interest in nanostructure research. The work presented in this dissertation focuses on two such nanostructures, electrospun nanofibers and nanodiamond particles, with an overarching goal of tailoring the material behavior for a desired outcome. Our first research theme focuses on realizing the full potential of chitosan electrospinning by understanding the mechanism that enables fiber formation through cyclodextrin complexation as a function of solution properties, solvent types, and cyclodextrin content. We demonstrate that cyclodextrin addition not only enables chitosan fiber formation, but also extends the composition and solvent window for nanofiber synthesis while introducing a variety of mat topologies, including three-dimensional, self-supporting mats. These fiber formation improvements cannot be fully explained by conventional electrospinning parameters, but instead seem to be related to the molecular interactions between chitosan and cyclodextrin. Our second research theme entails the modification of highly water soluble, poly(vinyl alcohol) (PVA) nanofibers dissolution properties via atomic layer deposition (ALD) post treatments. In this work, we demonstrate that applying different thicknesses of aluminum oxide nano-coatings can improve the stability of PVA nanofibers in high humidity conditions and significantly decrease the solubility of electrospun PVA mats in water, from seconds to multiple weeks. Controlling mat dissolution allows for the unique opportunity to modulate small molecule, such as drug, release from nanofibers without altering the core

  7. Electrospinning of Polyacrylonitrile Nanofibers and Simulation of Electric Field via Finite Element method

    Directory of Open Access Journals (Sweden)

    Hadi Samadian

    2017-04-01

    Full Text Available Objective(s: Since the electric field is the main driving force in electrospinning systems, the modeling and analysis of electric field distribution are critical to the nanofibers production. The aim of this study was modeling of the electric field and investigating the various parameters on polyacrylonitrile (PAN nanofibers morphology and diameter. Methods: The electric field profile at the nozzle and electrospinning zone was evaluated by Finite Element Method. The morphology and diameter of nanofibers were examined by Scanning electron microscopy (SEM. Results: The results of the electric field analysis indicated that the electric field was concentrated at the tip of the nozzle. Moreover, in the spinning direction, the electric field was concentrated at the surface of the spinneret and decayed rapidly toward the surface of the collector. Increasing polymer solution concentration from 7 to 11wt.% led to increasing nanofibers diameter form 77.76 ± 19.44 to 202.42 ± 36.85. Conclusions: Base on our results, it could be concluded that concentration of the electric field at the tip of the nozzle is high and initiates jet and nanofibers formation. PAN nanofibers can be transformed to carbon nanofibers which have various applications in biomedicine.

  8. Preparation of Amidoxime Polyacrylonitrile Chelating Nanofibers and Their Application for Adsorption of Metal Ions

    Directory of Open Access Journals (Sweden)

    You-Lo Hsieh

    2013-03-01

    Full Text Available Polyacrylonitrile (PAN nanofibers were prepared by electrospinning and they were modified with hydroxylamine to synthesize amidoxime polyacrylonitrile (AOPAN chelating nanofibers, which were applied to adsorb copper and iron ions. The conversion of the nitrile group in PAN was calculated by the gravimetric method. The structure and surface morphology of the AOPAN nanofiber were characterized by a Fourier transform infrared spectrometer (FT-IR and a scanning electron microscope (SEM, respectively. The adsorption abilities of Cu2+ and Fe3+ ions onto the AOPAN nanofiber mats were evaluated. FT-IR spectra showed nitrile groups in the PAN were partly converted into amidoxime groups. SEM examination demonstrated that there were no serious cracks or sign of degradation on the surface of the PAN nanofibers after chemical modification. The adsorption capacities of both copper and iron ions onto the AOPAN nanofiber mats were higher than those into the raw PAN nanofiber mats. The adsorption data of Cu2+ and Fe3+ ions fitted particularly well with the Langmuir isotherm. The maximal adsorption capacities of Cu2+ and Fe3+ ions were 215.18 and 221.37 mg/g, respectively.

  9. Controlled Bioactive Molecules Delivery Strategies for Tendon and Ligament Tissue Engineering using Polymeric Nanofibers.

    Science.gov (United States)

    Hiong Teh, Thomas Kok; Hong Goh, James Cho; Toh, Siew Lok

    2015-01-01

    The interest in polymeric nanofibers has escalated over the past decade given its promise as tissue engineering scaffolds that can mimic the nanoscale structure of the native extracellular matrix. With functionalization of the polymeric nanofibers using bioactive molecules, localized signaling moieties can be established for the attached cells, to stimulate desired biological effects and direct cellular or tissue response. The inherently high surface area per unit mass of polymeric nanofibers can enhance cell adhesion, bioactive molecules loading and release efficiencies, and mass transfer properties. In this review article, the application of polymeric nanofibers for controlled bioactive molecules delivery will be discussed, with a focus on tendon and ligament tissue engineering. Various polymeric materials of different mechanical and degradation properties will be presented along with the nanofiber fabrication techniques explored. The bioactive molecules of interest for tendon and ligament tissue engineering, including growth factors and small molecules, will also be reviewed and compared in terms of their nanofiber incorporation strategies and release profiles. This article will also highlight and compare various innovative strategies to control the release of bioactive molecules spatiotemporally and explore an emerging tissue engineering strategy involving controlled multiple bioactive molecules sequential release. Finally, the review article concludes with challenges and future trends in the innovation and development of bioactive molecules delivery using polymeric nanofibers for tendon and ligament tissue engineering.

  10. Dynamic stability of nano-fibers self-assembled from short amphiphilic A6D peptides.

    Science.gov (United States)

    Nikoofard, Narges; Maghsoodi, Fahimeh

    2018-04-07

    Self-assembly of A 6 D amphiphilic peptides in explicit water is studied by using coarse-grained molecular dynamics simulations. It is observed that the self-assembly of randomly distributed A 6 D peptides leads to the formation of a network of nano-fibers. Two other simulations with cylindrical nano-fibers as the initial configuration show the dynamic stability of the self-assembled nano-fibers. As a striking feature, notable fluctuations occur along the axes of the nano-fibers. Depending on the number of peptides per unit length of the nano-fiber, flat-shaped bulges or spiral shapes along the nano-fiber axis are observed at the fluctuations. Analysis of the particle distribution around the nano-fiber indicates that the hydrophobic core and the hydrophilic shell of the nano-structure are preserved in both simulations. The size of the deformations and their correlation times are different in the two simulations. This study gives new insights into the dynamics of the self-assembled nano-structures of short amphiphilic peptides.

  11. Fabrication and Characterization of Aligned Flexible Lead-Free Piezoelectric Nanofibers for Wearable Device Applications

    Directory of Open Access Journals (Sweden)

    Sang Hyun Ji

    2018-03-01

    Full Text Available Flexible lead-free piezoelectric nanofibers, based on BNT-ST (0.78Bi0.5Na0.5TiO3-0.22SrTiO3 ceramic and poly(vinylidene fluoride-trifluoroethylene (PVDF-TrFE copolymers, were fabricated by an electrospinning method and the effects of the degree of alignment in the nanofibers on the piezoelectric characteristics were investigated. The microstructure of the lead-free piezoelectric nanofibers was observed by field emission scanning electron microscope (FE-SEM and the orientation was analyzed by fast Fourier transform (FFT images. X-ray diffraction (XRD analysis confirmed that the phase was not changed by the electrospinning process and maintained a perovskite phase. Polarization-electric field (P-E loops and piezoresponse force microscopy (PFM were used to investigate the piezoelectric properties of the piezoelectric nanofibers, according to the degree of alignment—the well aligned piezoelectric nanofibers had higher piezoelectric properties. Furthermore, the output voltage of the aligned lead-free piezoelectric nanofibers was measured according to the vibration frequency and the bending motion and the aligned piezoelectric nanofibers with a collector rotation speed of 1500 rpm performed the best.

  12. Electrospun single-walled carbon nanotube/polyvinyl alcohol composite nanofibers: structure-property relationships

    International Nuclear Information System (INIS)

    Naebe, Minoo; Lin Tong; Wang Xungai; Staiger, Mark P; Dai Liming

    2008-01-01

    Polyvinyl alcohol (PVA) nanofibers and single-walled carbon nanotube (SWNT)/PVA composite nanofibers have been produced by electrospinning. An apparent increase in the PVA crystallinity with a concomitant change in its main crystalline phase and a reduction in the crystalline domain size were observed in the SWNT/PVA composite nanofibers, indicating the occurrence of a SWNT-induced nucleation crystallization of the PVA phase. Both the pure PVA and SWNT/PVA composite nanofibers were subjected to the following post-electrospinning treatments: (i) soaking in methanol to increase the PVA crystallinity, and (ii) cross-linking with glutaric dialdehyde to control the PVA morphology. Effects of the PVA morphology on the tensile properties of the resultant electrospun nanofibers were examined. Dynamic mechanical thermal analyses of both pure PVA and SWNT/PVA composite electrospun nanofibers indicated that SWNT-polymer interaction facilitated the formation of crystalline domains, which can be further enhanced by soaking the nanofiber in methanol and/or cross-linking the polymer with glutaric dialdehyde

  13. Electrospun polyacrylonitrile nanofibers functionalized with EDTA for adsorption of ionic dyes

    Science.gov (United States)

    Chaúque, Eutilério F. C.; Dlamini, Langelihle N.; Adelodun, Adedeji A.; Greyling, Corinne J.; Ngila, J. Catherine

    2017-08-01

    The manipulation of nanofibers' surface chemistry could enhance their potential application toward the removal of ionic dyes in wastewater. For this purpose, surface modification of electrospun polyacrylonitrile (PAN) nanofibers with ethylenediaminetetraacetic acid (EDTA) and ethylenediamine (EDA) crosslinker was experimented. The functionalized EDTA-EDA-PAN nanofibers were characterized using Fourier transform infrared (FT-IR) spectroscopy, X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and Brunauer-Emmett-Teller (BET) technique. The impregnation of EDA and EDTA chelating agents on the surface of PAN changed the distribution of nanofibers as proximity is increased (accompanied by reduced softness), but the nanofibrous structure of the pristine PAN nanofibers was not substantially altered. Adsorption equilibrium studies were performed with Freundlich, Langmuir and Temkin isotherm models with the former providing better correlation to the experimental data. The modified PAN nanofibers showed efficient sorption of methyl orange (MO) and reactive red (RR) from aqueous synthetic samples, evinced by the maximum adsorption capacities (at 25 °C) of 99.15 and 110.0 mg g-1, respectively. The fabricated nanofibers showed appreciable removal efficiency of the target dye sorptives from wastewater. However, the presence of high metal ions content affected the overall extraction of dyes from wastewater due to the depletion of the adsorbent's active adsorptive sites.

  14. Capture of toxic radioactive and heavy metal ions from water by using titanate nanofibers

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Jiasheng, E-mail: jiashengxu@bhu.edu.cn [Liaoning Province Key Laboratory for Synthesis and Application of Functional Compounds, College of Chemistry, Chemical Engineering and Food Safety, Center of Science and Technology Experiment, Bohai University, 19 Sci-tech Road, Jinzhou 121013 (China); Zhang, He; Zhang, Jie [Liaoning Province Key Laboratory for Synthesis and Application of Functional Compounds, College of Chemistry, Chemical Engineering and Food Safety, Center of Science and Technology Experiment, Bohai University, 19 Sci-tech Road, Jinzhou 121013 (China); Kim, Eui Jung [School of Chemical Engineering and Bioengineering, University of Ulsan, Ulsan 680-749 (Korea, Republic of)

    2014-11-25

    Highlights: • Three types of titanate nanofibers were prepared via a hydrothermal porcess. • These nanofibers show availability for removal of the toxic ions from water. • The equilibrium data were fitted well with the Langmuir model. - Abstract: Three types of titanate nanofibers (sodium titanate nanofibers (TNF-A), potassium/sodium titanate nanofibers (TNF-B), potassium titanate nanofibers (TNF-C)) were prepared via a hydrothermal treatment of anatase powders in different alkali solutions at 170 °C for 96 h, respectively. The as-prepared nanofibers have large specific surface area and show availability for the removal of radioactive and heavy metal ions from water system, such as Ba{sup 2+} (as substitute of {sup 226}Ra{sup 2+}) and Pb{sup 2+} ions. The TNF-A shows a better capacity in the removal of Ba{sup 2+} and Pb{sup 2+} than TNF-B and TNF-C. Structural characterization of the materials was performed with powder X-ray diffraction (XRD), scanning electron microscopy (SEM) equipped with energy dispersive spectrometer (EDS) and with inductively coupled plasma optical emission spectrometry (ICP-OES). It is found that the equilibrium data fit well with the Langmuir model. This study highlights that nanoparticles of inorganic ion exchangers with layered structure are potential materials for efficient removal of the toxic ions from contaminated water.

  15. Ultra-High Density Single Nanometer-Scale Anodic Alumina Nanofibers Fabricated by Pyrophosphoric Acid Anodizing

    Science.gov (United States)

    Kikuchi, Tatsuya; Nishinaga, Osamu; Nakajima, Daiki; Kawashima, Jun; Natsui, Shungo; Sakaguchi, Norihito; Suzuki, Ryosuke O.

    2014-12-01

    Anodic oxide fabricated by anodizing has been widely used for nanostructural engineering, but the nanomorphology is limited to only two oxides: anodic barrier and porous oxides. Therefore, the discovery of an additional anodic oxide with a unique nanofeature would expand the applicability of anodizing. Here we demonstrate the fabrication of a third-generation anodic oxide, specifically, anodic alumina nanofibers, by anodizing in a new electrolyte, pyrophosphoric acid. Ultra-high density single nanometer-scale anodic alumina nanofibers (1010 nanofibers/cm2) consisting of an amorphous, pure aluminum oxide were successfully fabricated via pyrophosphoric acid anodizing. The nanomorphologies of the anodic nanofibers can be controlled by the electrochemical conditions. Anodic tungsten oxide nanofibers can also be fabricated by pyrophosphoric acid anodizing. The aluminum surface covered by the anodic alumina nanofibers exhibited ultra-fast superhydrophilic behavior, with a contact angle of less than 1°, within 1 second. Such ultra-narrow nanofibers can be used for various nanoapplications including catalysts, wettability control, and electronic devices.

  16. Oxolane-2,5-dione modified electrospun cellulose nanofibers for heavy metals adsorption

    International Nuclear Information System (INIS)

    Stephen, Musyoka; Catherine, Ngila; Brenda, Moodley; Andrew, Kindness; Leslie, Petrik; Corrine, Greyling

    2011-01-01

    Highlights: → Electrospun and modified cellulose nanofibers have high surface area. → Modified nanofibers showed improved adsorption of Cd and Pb from water. → Regenerated modified nanofibers had high adsorption capacity hence recyclable. - Abstract: Functionalized cellulose nanofibers have been obtained through electrospinning and modification with oxolane-2,5-dione. The application of the nanofibers for adsorption of cadmium and lead ions from model wastewater samples is presented for the first time. Physical and chemical properties of the nanofibers were characterized. Surface chemistry during preparation and functionalization was monitored using Fourier transform-infrared spectroscopy, scanning electron microscopy, carbon-13 solid state nuclear magnetic resonance spectroscopy and Brunauer Emmett and Teller. Enhanced surface area of 13.68 m 2 g -1 was recorded for the nanofibers as compared to the cellulose fibers with a surface area of 3.22 m 2 g -1 . Freundlich isotherm was found to describe the interactions better than Langmuir: K f = 1.0 and 2.91 mmol g -1 (r 2 = 0.997 and 0.988) for lead and cadmium, respectively. Regenerability of the fiber mats was investigated and the results obtained indicate sustainability in adsorption efficacy of the material.

  17. Preparation and characterization of Ce-doped ZnO nanofibers by an electrospinning method

    Directory of Open Access Journals (Sweden)

    Jong-Pil Kim

    2011-02-01

    Full Text Available ZnO and Ce-doped ZnO Nanofibers on (111 Pt/SiO2/Si substrates were produced using an electrospinning technique. The as-prepared composite fibres were subjected to high-temperature calcination to produce inorganic fibers. After calcining at a temperature of 500 °C, the average diameter of the ZnO and Ce-doped ZnO nanofibers were determined to be 170 nm and 225 nm, respectively. The average grain size of the ZnO and Ce-doped ZnO nanofibers were about 50 nm and 57 nm, respectively. The microstructure, chemical bonding state and photoluminescence of the produced ZnO and Ce-doped ZnO nanofibers were investigated. The Ce-doped ZnO nanofiber can be assigned to the presence of Ce ions on substitutional sites of Zn ions and the Ce3+ state from X-ray photoelectron spectra. Compared with PL spectra of ZnO nanofibers, the peak position of the UV emission of the Ce-doped ZnO nanofibers is sharply suppressed while the green emission band is highly enhanced.

  18. Dynamic stability of nano-fibers self-assembled from short amphiphilic A6D peptides

    Science.gov (United States)

    Nikoofard, Narges; Maghsoodi, Fahimeh

    2018-04-01

    Self-assembly of A6D amphiphilic peptides in explicit water is studied by using coarse-grained molecular dynamics simulations. It is observed that the self-assembly of randomly distributed A6D peptides leads to the formation of a network of nano-fibers. Two other simulations with cylindrical nano-fibers as the initial configuration show the dynamic stability of the self-assembled nano-fibers. As a striking feature, notable fluctuations occur along the axes of the nano-fibers. Depending on the number of peptides per unit length of the nano-fiber, flat-shaped bulges or spiral shapes along the nano-fiber axis are observed at the fluctuations. Analysis of the particle distribution around the nano-fiber indicates that the hydrophobic core and the hydrophilic shell of the nano-structure are preserved in both simulations. The size of the deformations and their correlation times are different in the two simulations. This study gives new insights into the dynamics of the self-assembled nano-structures of short amphiphilic peptides.

  19. Neurotensin-loaded PLGA/CNC composite nanofiber membranes accelerate diabetic wound healing.

    Science.gov (United States)

    Zheng, Zhifang; Liu, Yishu; Huang, Wenhua; Mo, Yunfei; Lan, Yong; Guo, Rui; Cheng, Biao

    2018-04-13

    Diabetic foot ulcers (DFUs) are a threat to human health and can lead to amputation and even death. Recently neurotensin (NT), an inflammatory modulator in wound healing, was found to be beneficial for diabetic wound healing. As we demonstrated previously, polylactide-polyglycolide (PLGA) and cellulose nanocrystals (CNCs) (PLGA/CNC) nanofiber membranes show good cytocompatibility and facilitate fibroblast adhesion, spreading and proliferation. PLGA/CNC nanofiber membranes are novel materials that have not been used previously as NT carriers in diabetic wounds. This study aims to explore the therapeutic efficacy and possible mechanisms of NT-loaded PLGA/CNC nanofiber membranes in full-thickness skin wounds in spontaneously diabetic mice. The results showed that NT could be sustained released from NT-loaded PLGA/CNC composite nanofiber membranes for 2 weeks. NT-loaded PLGA/CNC composite nanofiber membranes induced more rapid healing than other control groups. After NT exposure, the histological scores of the epidermal and dermal regeneration and the ratios of the fibrotic area to the whole area were increased. NT-loaded PLGA/CNC composite nanofiber membranes also decreased the expressions of the inflammatory cytokines IL-1β and IL-6. These results suggest that NT-loaded PLGA/CNC composite nanofiber membranes for sustained delivery of NT should effectively promote tissue regeneration for the treatment of DFUs.

  20. Morphological Effects of HA on the Cell Compatibility of Electrospun HA/PLGA Composite Nanofiber Scaffolds

    Directory of Open Access Journals (Sweden)

    Adnan Haider

    2014-01-01

    Full Text Available Tissue engineering is faced with an uphill challenge to design a platform with appropriate topography and suitable surface chemistry, which could encourage desired cellular activities and guide bone tissue regeneration. To develop such scaffolds, composite nanofiber scaffolds of nHA and sHA with PLGA were fabricated using electrospinning technique. nHA was synthesized using precipitation method, whereas sHA was purchased. The nHA and sHA were suspended in PLGA solution separately and electrospun at optimized electrospinning parameters. The composite nanofiber scaffolds were characterized by FE-SEM, EDX analysis, TEM, XRD analysis, FTIR, and X-ray photoelectron. The potential of the HA/PLGA composite nanofiber as bone scaffolds in terms of their bioactivity and biocompatibility was assessed by culturing the osteoblastic cells onto the composite nanofiber scaffolds. The results from in vitro studies revealed that the nHA/PLGA composite nanofiber scaffolds showed higher cellular adhesion, proliferation, and enhanced osteogenesis performance, along with increased Ca+2 ions release compared to the sHA/PLGA composite nanofiber scaffolds and pristine PLGA nanofiber scaffold. The results show that the structural dependent property of HA might affect its potential as bone scaffold and implantable materials in regenerative medicine and clinical tissue engineering.

  1. Electrospun curcumin loaded poly(ε-caprolactone)/gum tragacanth nanofibers for biomedical application.

    Science.gov (United States)

    Ranjbar-Mohammadi, Marziyeh; Bahrami, S Hajir

    2016-03-01

    In this work curcumin (Cur)-loaded poly(ε-caprolactone) (PCL)/gum tragacanth (GT) scaffold membranes which provided the controlled release of curcumin for over 20 days were fabricated by electrospinning. Field Emission Scanning Electron Microscopy (FESEM) analysis, Fourier Transform Infrared Spectroscopy (FTIR) and differential scanning calorimetry (DSC) were applied to characterize the produced nanofibers. These nanofibers were evaluated for water absorption capacity, in vitro drug release, biodegradation test, cell culture and MTT analysis. The water contact angle measurements indicated that addition of GT and curcumin in composition resulted in increase in the hydrophilicity of the nanofibers. Biodegradation test for the fabricated nanofibers exhibited that PCL/GT, PCL/Cur-3% and PCL/GT/Cur-3% nanofibers preserved their structure after 15 days. The in vitro release profile of curcumin showed 6.86, 14 and 30.09% burst release for PCL/GT/Cur-1%, PCL/GT/Cur-3% and PCL/Cur-3% nanofibers respectively. The effect of curcumin concentration in the nanofibers composition on the cell viability was assessed by the MTS assay. The cytotoxic effect of released curcumin on the fibroblast cells was examined. The PCL/GT/Cur-3% with suitable mechanical properties, excellent biological characteristics, and maintaining their original structure in degradation media may have potential application as a wound dressing patch for healing slow rate wounds. Copyright © 2015 Elsevier B.V. All rights reserved.

  2. Ag loading induced visible light photocatalytic activity for pervoskite SrTiO3 nanofibers

    Science.gov (United States)

    Wu, Yeqiu; He, Tao

    2018-06-01

    The synthesis and photocatalytic activities of Ag-SrTiO3 nanofibers were reported in this work. The fabricated Ag-SrTiO3 nanofibers were characterized by TG-DSC, XRD, IR, XPS, SEM, TEM, DRS and ESR techniques. The XRD and IR results show that Ag-SrTiO3 nanofibers have a perovskite structure after the heat treatment at 700 °C. The XPS result shows that Ag element exists as Ag0 in the fabricated Ag-SrTiO3 nanofibers. The SEM and TEM images indicate the obtaining of nanofibers with porous structure. The photocatalytic activity of Ag-SrTiO3 nanofibers was evaluated by degrading RhB and MB under visible light irradiation. The Ag-SrTiO3 nanofibers show excellent photocatalytic activity under visible light irradiation because of the surface plasmon resonance effect of Ag0. In the photocatalysis process of RhB and MB, lots of hydroxyl radicals were generated, which plays the key role in the decomposition of organic pollutants.

  3. Fabrication and characterization of differentiated aramid nanofibers and transparent films

    Science.gov (United States)

    Luo, Jingjing; Zhang, Meiyun; Yang, Bin; Liu, Guodong; Song, Shunxi

    2018-03-01

    Aramid nanofibers (ANFs) frequently are employed as versatile building blocks for constructing high-performance nanocomposites due to its structural and performance superiority. In this paper, the different ANFs and ANF films derived from the typical aramid yarns, chopped fiber, pulp fiber and fibrid fiber, respectively, were fabricated through deprotonation with potassium hydroxide in dimethyl sulphoxide, protonation with deionized water and vacuum-assisted filtration. The physical tests such as tensile test, ultraviolet transmittance and absorbance, thermogravimetric analysis were executed to evaluate and contrast the thermodynamic and optical performances of these differentiated ANFs and ANF films. The analytical results suggested that ANFs films prepared by the different forms of aramid macrofibers presented with differentiated properties such as mechanical behaviors, transparencies and flexibilities. And also it was found that the oversized nanofiber in length led to the formation of flocculation which was adverse for ANFs films in the formation of high strength. Whereas, small diameter just facilitated for the achievement of high stiffness and transparency. By contrast, the ANFs films made from chopped nanofiber, with aspect ratio of 200-500, exhibited good transparency, thermal stability and mechanical properties with transmittance value of 83%, TG10% around 521 °C, ultimate strength (σ) of 103.41 MPa, stiffness (E) of 4.70 GPa and strain at break of 5.56%. This work offers an alternative nanoscale building block as an effective nanofiller for preparing high-performance nanocomposites with different requirements in the potential fields such as transparent coating and flexible electrode or display materials, battery separator and microporous membrane.

  4. Flexible electrode belt for EIT using nanofiber web dry electrodes.

    Science.gov (United States)

    Oh, Tong In; Kim, Tae Eui; Yoon, Sun; Kim, Kap Jin; Woo, Eung Je; Sadleir, Rosalind J

    2012-10-01

    Efficient connection of multiple electrodes to the body for impedance measurement and voltage monitoring applications is of critical importance to measurement quality and practicality. Electrical impedance tomography (EIT) experiments have generally required a cumbersome procedure to attach the multiple electrodes needed in EIT. Once placed, these electrodes must then maintain good contact with the skin during measurements that may last several hours. There is usually also the need to manage the wires that run between the electrodes and the EIT system. These problems become more severe as the number of electrodes increases, and may limit the practicality and portability of this imaging method. There have been several trials describing human-electrode interfaces using configurations such as electrode belts, helmets or rings. In this paper, we describe an electrode belt we developed for long-term EIT monitoring of human lung ventilation. The belt included 16 embossed electrodes that were designed to make good contact with the skin. The electrodes were fabricated using an Ag-plated PVDF nanofiber web and metallic threads. A large contact area and padding were used behind each electrode to improve subject comfort and reduce contact impedances. The electrodes were incorporated, equally spaced, into an elasticated fabric belt. We tested the electrode belt in conjunction with the KHU Mark1 multi-frequency EIT system, and demonstrate time-difference images of phantoms and human subjects during normal breathing and running. We found that the Ag-plated PVDF nanofiber web electrodes were suitable for long-term measurement because of thei