WorldWideScience

Sample records for cobalt doped zno

  1. Cobalt-doped ZnO as dilute magnetic semiconductor; Cobalt dotiertes ZnO als verduennter magnetischer Halbleiter

    Energy Technology Data Exchange (ETDEWEB)

    Gacic, Milan

    2009-04-24

    Dilute magnetic semiconductors (DMS) are technologically promising materials that show ferromagnetic as well as semiconducting properties. These are one of the crucial compounds concerning the development of spintronic devices. The main problem so far ist that for applications the Curie temperature of most of the DMS compounds is much too low. However, DMS compounds based on ZnO as Zn{sub 1-x}Co{sub x}O seem to show ferromagnetism above room temperature, but the ferromagnetic exchange is not fully understood. Intensive experimental investigations need to be done. In the course of this theses Zn{sub 0.95}Co{sub 0.05}O thin films were fabricated by pulsed laser deposition and investigated concerning their magnetic, magnetoelectric and structural properties in order to understand the ferromagnetism in this material. Different experimental methods have been used, as magnetometry, X-ray diffraction (XRD), X-ray magnetic circular dichroism (XMCD), electron spin resonance (ESR) and magnetoelectric transport measurements. At special preparation conditions, where a high defect density is induced, the samples are clearly ferromagnetic above room temperature with a saturation magnetization of 2 {mu}{sub b}/Co and a remanence of 90%. Electrical transport measurements show a clear magnetoresistance as well as a anomalous Hall effect. The anomalous Hall effect rises with the magnetization indicating intrinsic ferromagnetism and a certain degree of spin polarization. As the ferromagnetism disappears with rising charge carrier density the ferromagnetic interaction cannot be mediated by the conduction electrons. A more precise evaluation of the magnetoelectric results shows that there is an additional conducting impurity band which could even be spinpolarized. So there are indications that the ferromagnetism is due to magnetic polarons. Some of the structural and magnetometric results as well as the electron spin resonance measurements suggest an additional extrinsic contribution

  2. Effect of cobalt doping on the mechanical properties of ZnO nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Vahtrus, Mikk; Šutka, Andris [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Polyakov, Boris [Institute of Solid State Physics, University of Latvia, Kengaraga 8, LV-1063 Riga (Latvia); Oras, Sven; Antsov, Mikk [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Doebelin, Nicola [RMS Foundation, Bischmattstrasse 12, Bettlach 2544 (Switzerland); Institute of Geological Sciences, University of Bern, Baltzerstrasse 1–3, Bern 3012 (Switzerland); Lõhmus, Rünno; Nõmmiste, Ergo [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia); Vlassov, Sergei, E-mail: vlassovs@ut.ee [Institute of Physics, University of Tartu, W. Ostwaldi 1, 50412 Tartu (Estonia)

    2016-11-15

    In this work, we investigate the influence of doping on the mechanical properties of ZnO nanowires (NWs) by comparing the mechanical properties of pure and Co-doped ZnO NWs grown in similar conditions and having the same crystallographic orientation [0001]. The mechanical characterization included three-point bending tests made with atomic force microscopy and cantilever beam bending tests performed inside scanning electron microscopy. It was found that the Young's modulus of ZnO NWs containing 5% of Co was approximately a third lower than that of the pure ZnO NWs. Bending strength values were comparable for both materials and in both cases were close to theoretical strength indicating high quality of NWs. Dependence of mechanical properties on NW diameter was found for both doped and undoped ZnO NWs. - Highlights: •Effect of Co doping on the mechanical properties of ZnO nanowires is studied. •Co substitutes Zn atoms in ZnO crystal lattice. •Co addition affects crystal lattice parameters. •Co addition results in significantly decreased Young's modulus of ZnO. •Bending strength for doped and undoped wires is close to the theoretical strength.

  3. Optical and magnetic properties of Yb ion-doped cobalt-based ZnO ...

    Indian Academy of Sciences (India)

    Administrator

    The X-ray photoelectron spectral peaks for Yb 4f ions ... temperature with high coercivity due to the contribution of both 3d and 4f exchange interaction with the host ... Mn,4,5 Co,6–9 Ni2,10 Fe11–13 and Cu,2,14 and reported to .... water separately under stirring. .... different concentrations of Yb added ZnO : Co, nanopar-.

  4. Advantageous use of metallic cobalt in the target for pulsed laser deposition of cobalt-doped ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Ying, Minju, E-mail: mjying@bnu.edu.cn, E-mail: g.gehring@sheffield.ac.uk [Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH (United Kingdom); Key Laboratory of Beam Technology and Material Modification of Ministry of Education, College of Nuclear Science and Technology, Beijing Normal University, Beijing 100875 (China); Blythe, Harry J.; Gerriu, Fatma M.; Fox, A. Mark; Gehring, Gillian A., E-mail: mjying@bnu.edu.cn, E-mail: g.gehring@sheffield.ac.uk [Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH (United Kingdom); Dizayee, Wala [Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH (United Kingdom); Department of Science, Salahaddin University, Erbil (Iraq); Heald, Steve M. [Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois 60439 (United States)

    2016-08-15

    We investigate the magnetic properties of ZnCoO thin films grown by pulsed laser deposition (PLD) from targets made containing metallic Co or CoO precursors instead of the usual Co{sub 3}O{sub 4}. We find that the films grown from metallic Co precursors in an oxygen rich environment contain negligible amounts of Co metal and have a large magnetization at room temperature. Structural analysis by X-ray diffraction and magneto-optical measurements indicate that the enhanced magnetism is due, in part, from Zn vacancies that partially compensate the naturally occurring n-type defects. We conclude that strongly magnetic films of Zn{sub 0.95}Co{sub 0.05}O that do not contain metallic cobalt can be grown by PLD from Co-metal-precursor targets if the films are grown in an oxygen atmosphere.

  5. Nature of ferromagnetic coupling in Cobalt-doped ZnO; Ursache der magnetischen Kopplung in Kobalt-dotiertem ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Nielsen, K W

    2007-12-12

    Aim of this thesis was on the one hand to produce Co doped ZnO films, which exhibit a ferromagnetic signal and on the other hand to study the cause of the magnetic coupling. For this purpose Zn{sub 0.95}Co{sub 0.05} films wer fabricated by pulsed laser deposition. Three different substrate materials ((0001)ZnO, (0001)Al{sub 2}O{sub 3}, and (0001)ScAlMgO{sub 4}) were applied anf the growth temperature T{sub g} varied between 300 C and 600 C. Furthermore non-transition-metal doped films were grown at T{sub g}=320 C. By means of X-ray diffractometry the samples were studied concerning their structure, phase purity, and mosaicism. In the films on ZnO a foreign phase was detected, which can be explained by metallic Co inclusions. An estimation of the particle sizes yielded diameters between 2.2 nm and 5.4 nm. With SQID magnetometry measurements of the magnetization M were performed in dependence on the magnetic field H and the temperature T. At 300 K in all Co doped samples on ZnO and in samples on Al{sub 2}O{sub 3} and ScAlMgO{sub 4} with T{sub g}<400 C in the M(H) curves a distinct magnetic moment was observed, which cannot be explained by paramagnetic CO{sup 2+}. The magnetization measurements prove the existence of superparamegnetic nanoparticles. By means of high-resolution transmission electron microscopy it was possible to detect the Co inclusions in the Co doped film on ZnO with T{sub g}=500 C. For the Co and the non-transition-metal-doped samples on Al{sub 2}O{sub 3} and ScAlMgO{sub 4} with T{sub g}=320 C the electric trasnport properties were determined in dependence on H and T.

  6. On the role of diluted magnetic cobalt-doped ZnO electrodes in efficiency improvement of InGaN light emitters

    International Nuclear Information System (INIS)

    Liu, Hong-Ru; Wang, Shih-Yin; Ou, Sin-Liang; Wuu, Dong-Sing

    2016-01-01

    The 120-nm-thick cobalt-doped ZnO (Co-doped ZnO, CZO) dilute magnetic films deposited by pulsed laser deposition were employed as the n-electrodes for both lateral-type blue (450 nm) and green (520 nm) InGaN light emitters. In comparison to the conventional blue and green emitters, there were 15.9% and 17.7% enhancements in the output power (@350 mA) after fabricating the CZO n-electrode on the n-GaN layer. Observations on the role of CZO n-electrodes in efficiency improvement of InGaN light emitters were performed. Based on the results of Hall measurements, the carrier mobilities were 176 and 141 cm"2/V s when the electrons passed through the n-GaN and the patterned-CZO/n-GaN, respectively. By incorporating the CZO n-electrode into the InGaN light emitters, the electrons would be scattered because of the collisions between the magnetic atoms and the electrons as the device is driven, leading to the reduction of the electron mobility. Therefore, the excessively large mobility difference between electron and hole carriers occurred in the conventional InGaN light emitter can be efficiently decreased after preparing the CZO n-electrode on the n-GaN layer, resulting in the increment of carrier recombination rate and the improvement of light output power.

  7. On the role of diluted magnetic cobalt-doped ZnO electrodes in efficiency improvement of InGaN light emitters

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Hong-Ru; Wang, Shih-Yin [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Ou, Sin-Liang [Department of Materials Science and Engineering, Da-Yeh University, Changhua 51591, Taiwan (China); Wuu, Dong-Sing, E-mail: dsw@dragon.nchu.edu.tw [Department of Materials Science and Engineering, National Chung Hsing University, Taichung 40227, Taiwan (China); Department of Materials Science and Engineering, Da-Yeh University, Changhua 51591, Taiwan (China); Advanced Optoelectronic Technology Center, National Cheng Kung University, Tainan 70101, Taiwan (China)

    2016-07-11

    The 120-nm-thick cobalt-doped ZnO (Co-doped ZnO, CZO) dilute magnetic films deposited by pulsed laser deposition were employed as the n-electrodes for both lateral-type blue (450 nm) and green (520 nm) InGaN light emitters. In comparison to the conventional blue and green emitters, there were 15.9% and 17.7% enhancements in the output power (@350 mA) after fabricating the CZO n-electrode on the n-GaN layer. Observations on the role of CZO n-electrodes in efficiency improvement of InGaN light emitters were performed. Based on the results of Hall measurements, the carrier mobilities were 176 and 141 cm{sup 2}/V s when the electrons passed through the n-GaN and the patterned-CZO/n-GaN, respectively. By incorporating the CZO n-electrode into the InGaN light emitters, the electrons would be scattered because of the collisions between the magnetic atoms and the electrons as the device is driven, leading to the reduction of the electron mobility. Therefore, the excessively large mobility difference between electron and hole carriers occurred in the conventional InGaN light emitter can be efficiently decreased after preparing the CZO n-electrode on the n-GaN layer, resulting in the increment of carrier recombination rate and the improvement of light output power.

  8. Photovoltaic Properties of Co-doped ZnO Thin Film on Glass Substrate

    International Nuclear Information System (INIS)

    Sabia Aye; Zin Ma Ma; May Nwe Oo; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

    2011-12-01

    Cobalt (Co) 0.4 mol doped zinc oxide (ZnO) fine powder was prepared by solid state mixed oxide route. Phase formation and crystal structure of Co-doped ZnO (CZO) powder were examined by X-ray diffraction (XRD). Scanning Electron Microscopy (SEM) was used to observe the micro structure of Co doped ZnO powder. Energy Dispersive X-ray Fluorescent (EDXRF) technique gave the elemental content of cobalt and zinc. Co-doped ZnO film was formed on glass substrate by spin coating technique. Photovoltaic properties of CZO/glass cell were measured.

  9. Blood doping by cobalt. Should we measure cobalt in athletes?

    Directory of Open Access Journals (Sweden)

    Guidi Gian

    2006-07-01

    Full Text Available Abstract Background Blood doping is commonplace in competitive athletes who seek to enhance their aerobic performances through illicit techniques. Presentation of the hypothesis Cobalt, a naturally-occurring element with properties similar to those of iron and nickel, induces a marked and stable polycythemic response through a more efficient transcription of the erythropoietin gene. Testing the hypothesis Although little information is available so far on cobalt metabolism, reference value ranges or supplementation in athletes, there is emerging evidence that cobalt is used as a supplement and increased serum concentrations are occasionally observed in athletes. Therefore, given the athlete's connatural inclination to experiment with innovative, unfair and potentially unhealthy doping techniques, cobalt administration might soon become the most suited complement or surrogate for erythropoiesis-stimulating substances. Nevertheless, cobalt administration is not free from unsafe consequences, which involve toxic effects on heart, liver, kidney, thyroid and cancer promotion. Implications of the hypothesis Cobalt is easily purchasable, inexpensive and not currently comprehended within the World Anti-Doping Agency prohibited list. Moreover, available techniques for measuring whole blood, serum, plasma or urinary cobalt involve analytic approaches which are currently not practical for antidoping laboratories. Thus more research on cobalt metabolism in athletes is compelling, along with implementation of effective strategies to unmask this potentially deleterious doping practice

  10. Red luminescence of Zn /ZnO core–shell nanorods in a mixture of LTZA/Zinc acetate matrix: Study of the effects of Nitrogen bubbling, Cobalt doping and thioglycolic acid

    Energy Technology Data Exchange (ETDEWEB)

    Karimipour, Masoud, E-mail: masoud.karimipour@gmail.com; Kheshabnia, Alireza; Molaei, Mehdi

    2016-10-15

    Zn/ZnO core–shell nanorods were synthesized using a very simple low temperature and low pressure Solvothermal method. Effect of N{sub 2} gas bubbling, insertion of thioglycolic acid (TGA) and cobalt doping with Co/Zn=x: 0%, 0.1%, 0.3% and 0.5% was studied by means of scanning electron microscopy, transmission electron microscopy, x-ray diffraction, Furrier transformed infrared(FTIR) spectroscopy, UV–Vis spectroscopy and photoluminescence (PL) measurement. XRD analysis showed that hexagonal metallic zinc and wurtzite ZnO phases are available in all the samples. Zinc acetate crystallizes together with Zn and ZnO phases as well, but it transforms to l-thereonine zinc acetate(LTZA) after the insertion of TGA. Moreover, gas bubbling and cobalt doping do not change the crystal phases. FTIR spectroscopy also confirms the formation of zincacetate and LTZA phases. Williamson–Hall analysis indicates that with the insertion of TGA, mean crystallite size decreases and the value of microstrain is the least for x=0.1%. SEM images depict that with the insertion of TGA, the morphology of the compound changes from rounded particles to nanorods. TEM images revealed that the microstructure of the compounds is of the Zn/ZnO core–shell type. UV–vis spectroscopy demonstrates the blue shift of absorption edge and the size reduction due to insertion of TGA. PL spectroscopy shows that the samples have strong blue emission with peaks range from 316 nm up to 480 nm. Bubbling simply causes that the samples emit a narrow and sharp band peaked at 605 nm. Insertion of TGA prevents the blue emission and enhances the pure red emission band. At the presence of TGA, the optimum value of pure red emission for Co-doping was found to be 0.1% which was compatible with XRD analysis. With x>0.1%, the blue and red emission of samples started quenching and light emission for the value of x=0.5% vanished completely. The results show that the other crystal phases such as zincacetate, LTZA do not

  11. Red luminescence of Zn /ZnO core–shell nanorods in a mixture of LTZA/Zinc acetate matrix: Study of the effects of Nitrogen bubbling, Cobalt doping and thioglycolic acid

    International Nuclear Information System (INIS)

    Karimipour, Masoud; Kheshabnia, Alireza; Molaei, Mehdi

    2016-01-01

    Zn/ZnO core–shell nanorods were synthesized using a very simple low temperature and low pressure Solvothermal method. Effect of N 2 gas bubbling, insertion of thioglycolic acid (TGA) and cobalt doping with Co/Zn=x: 0%, 0.1%, 0.3% and 0.5% was studied by means of scanning electron microscopy, transmission electron microscopy, x-ray diffraction, Furrier transformed infrared(FTIR) spectroscopy, UV–Vis spectroscopy and photoluminescence (PL) measurement. XRD analysis showed that hexagonal metallic zinc and wurtzite ZnO phases are available in all the samples. Zinc acetate crystallizes together with Zn and ZnO phases as well, but it transforms to l-thereonine zinc acetate(LTZA) after the insertion of TGA. Moreover, gas bubbling and cobalt doping do not change the crystal phases. FTIR spectroscopy also confirms the formation of zincacetate and LTZA phases. Williamson–Hall analysis indicates that with the insertion of TGA, mean crystallite size decreases and the value of microstrain is the least for x=0.1%. SEM images depict that with the insertion of TGA, the morphology of the compound changes from rounded particles to nanorods. TEM images revealed that the microstructure of the compounds is of the Zn/ZnO core–shell type. UV–vis spectroscopy demonstrates the blue shift of absorption edge and the size reduction due to insertion of TGA. PL spectroscopy shows that the samples have strong blue emission with peaks range from 316 nm up to 480 nm. Bubbling simply causes that the samples emit a narrow and sharp band peaked at 605 nm. Insertion of TGA prevents the blue emission and enhances the pure red emission band. At the presence of TGA, the optimum value of pure red emission for Co-doping was found to be 0.1% which was compatible with XRD analysis. With x>0.1%, the blue and red emission of samples started quenching and light emission for the value of x=0.5% vanished completely. The results show that the other crystal phases such as zincacetate, LTZA do not affect

  12. Room temperature ferromagnetism in Co doped ZnO within an optimal doping level of 5%

    International Nuclear Information System (INIS)

    Mohapatra, J.; Mishra, D.K.; Mishra, Debabrata; Perumal, A.; Medicherla, V.R.R.; Phase, D.M.; Singh, S.K.

    2012-01-01

    Highlights: ► Zn 1−x Co x O ((0 ≤ x ≤ 0.1)) system synthesized by solid state reaction technique. ► Observation of room temperature ferromagnetism for 3 and 5% Co doped ZnO. ► XPS and EPMA studies predict the occurrence of segregated CoO clusters. ► Suppresses ferromagnetic ordering in higher doping percentage of Co (>5%). -- Abstract: We report on the structural, micro-structural and magnetic properties of Zn 1−x Co x O (0 ≤ x ≤ 0.1) system. Electron probe micro-structural analysis on 5% Co doped ZnO indicates the presence of segregated cobalt oxide which is also confirmed from the Co 2p core level X-ray photoelectron spectrum. The presence of oxygen defects in lower percentage of Co doped ZnO (≤5%) enhances the carrier mediated exchange interaction and thereby enhancing the room-temperature ferromagnetic behaviour. Higher doping percentage of cobalt (>5%) creates weak link between the grains and suppresses the carrier mediated exchange interaction. This is the reason why room temperature ferromagnetism is not observed in 7% and 10% Co doped ZnO.

  13. doped ZnO thick film resistors

    Indian Academy of Sciences (India)

    The characterization and ethanol gas sensing properties of pure and doped ZnO thick films were investigated. Thick films of pure zinc oxide were prepared by the screen printing technique. Pure zinc oxide was almost insensitive to ethanol. Thick films of Al2O3 (1 wt%) doped ZnO were observed to be highly sensitive to ...

  14. Carbon doped ZnO: Synthesis, characterization and interpretation

    International Nuclear Information System (INIS)

    Mishra, D.K.; Mohapatra, J.; Sharma, M.K.; Chattarjee, R.; Singh, S.K.; Varma, Shikha; Behera, S.N.; Nayak, Sanjeev K.; Entel, P.

    2013-01-01

    A novel thermal plasma in-flight technique has been adopted to synthesize nanocrystalline ZnO and carbon doped nanocrystalline ZnO matrix. Transmission electron microscopy (TEM) studies on these samples show the average particle sizes to be around 32 nm for ZnO and for carbon doped ZnO. An enhancement of saturation magnetization in nanosized carbon doped ZnO matrix by a factor of 3.8 has been found in comparison to ZnO nanoparticles at room temperature. Raman measurement clearly indicates the presence of Zn–C complexes surrounded by ZnO matrix in carbon doped ZnO. This indicates that the ferromagnetic signature in carbon doped ZnO arises from the creation of defects or the development of oxy-carbon clusters, in the carbon doped ZnO system. Theoretical studies based on density functional theory also support the experimental analyses. - Highlights: ► Synthesis of nanocrystalline ZnO and carbon doped ZnO matrix by inflight thermal plasma reactor. ► Enhancement of ferromagnetism in nanosized carbon doped ZnO in comparison to ZnO nanoparticles. ► Raman measurement indicates the presence of Zn–C complexes surrounded by ZnO matrix. ► Ferromagnetic signature in carbon doped ZnO arises from the development of oxy-carbon clusters. ► DFT supports experimental evidence of ferromagnetism in C doped ZnO nanoparticles.

  15. Sodium doping in ZnO crystals

    Science.gov (United States)

    Parmar, N. S.; Lynn, K. G.

    2015-01-01

    ZnO bulk single crystals were doped with sodium by thermal diffusion. Positron annihilations spectroscopy confirms the filling of zinc vacancies, to >6 μm deep in the bulk. Secondary-ion mass spectrometry measurement shows the diffusion of sodium up to 8 μm with concentration (1-3.5) × 1017 cm-3. Broad photoluminescence excitation peak at 3.1 eV, with onset appearance at 3.15 eV in Na:ZnO, is attributed to an electronic transition from a NaZn level at ˜(220-270) meV to the conduction band. Resistivity in Na doped ZnO crystals increases up to (4-5) orders of magnitude at room temperature.

  16. Sodium doping in ZnO crystals

    International Nuclear Information System (INIS)

    Parmar, N. S.; Lynn, K. G.

    2015-01-01

    ZnO bulk single crystals were doped with sodium by thermal diffusion. Positron annihilations spectroscopy confirms the filling of zinc vacancies, to >6 μm deep in the bulk. Secondary-ion mass spectrometry measurement shows the diffusion of sodium up to 8 μm with concentration (1–3.5) × 10 17  cm −3 . Broad photoluminescence excitation peak at 3.1 eV, with onset appearance at 3.15 eV in Na:ZnO, is attributed to an electronic transition from a Na Zn level at ∼(220–270) meV to the conduction band. Resistivity in Na doped ZnO crystals increases up to (4–5) orders of magnitude at room temperature

  17. Sodium doping in ZnO crystals

    Energy Technology Data Exchange (ETDEWEB)

    Parmar, N. S., E-mail: nparmar@wsu.edu; Lynn, K. G. [Center for Materials Research, Washington State University, Pullman, Washington 99164-2711 (United States)

    2015-01-12

    ZnO bulk single crystals were doped with sodium by thermal diffusion. Positron annihilations spectroscopy confirms the filling of zinc vacancies, to >6 μm deep in the bulk. Secondary-ion mass spectrometry measurement shows the diffusion of sodium up to 8 μm with concentration (1–3.5) × 10{sup 17 }cm{sup −3}. Broad photoluminescence excitation peak at 3.1 eV, with onset appearance at 3.15 eV in Na:ZnO, is attributed to an electronic transition from a Na{sub Zn} level at ∼(220–270) meV to the conduction band. Resistivity in Na doped ZnO crystals increases up to (4–5) orders of magnitude at room temperature.

  18. Structural and optical properties of Co-doped ZnO nanocrystallites prepared by a one-step solution route

    International Nuclear Information System (INIS)

    Li Ping; Wang Sha; Li Jibiao; Wei Yu

    2012-01-01

    Zinc oxide (ZnO) nanocrystallites with different Co-doping levels were successfully synthesized by a simple one-step solution route at low temperature (95 deg. C) in this study. The structure and morphology of the samples thus obtained were characterized by XRD, EDS, XPS and FESEM. Results show that cobalt ions, in the oxidation state of Co 2+ , replace Zn 2+ ions in the ZnO lattice without changing its wurtzite structure. The dopant content varies from 0.59% to 5.39%, based on Co-doping levels. The pure ZnO particles exhibit well-defined 3D flower-like morphology with an average size of 550 nm, while the particles obtained after Co-doping are mostly cauliflower-like nanoclusters with an average size of 120 nm. Both the flower-like pure ZnO and the cauliflower-like Co:ZnO nanoclusters are composed of densely arrayed nanorods. The optical properties of the ZnO nanocrystallites following Co-doping were also investigated by UV-Visible absorption and Photoluminescence spectra. Our results indicate that Co-doping can change the energy-band structure and effectively adjust the luminescence properties of ZnO nanocrystallites. - Highlights: → Co-doped ZnO nanocrystallites were synthesized via a simple one-step solution route. → Co 2+ ions incorporated into the ZnO lattice without changing its wurtzite structure. → Co-doping changed the energy band structure of ZnO. → Co-doping effectively adjusted the luminescence properties of ZnO nanocrystallites.

  19. Structural and optical properties of Co-doped ZnO nanocrystallites prepared by a one-step solution route

    Energy Technology Data Exchange (ETDEWEB)

    Li Ping, E-mail: lipingchina@yahoo.com.cn [Provincial Key Laboratory of Inorganic Nanomaterials, School of Chemistry and Materials Science, Hebei Normal University, 113 Yuhua Road, Shijiazhuang 050016, Hebei (China); Wang Sha; Li Jibiao; Wei Yu [Provincial Key Laboratory of Inorganic Nanomaterials, School of Chemistry and Materials Science, Hebei Normal University, 113 Yuhua Road, Shijiazhuang 050016, Hebei (China)

    2012-01-15

    Zinc oxide (ZnO) nanocrystallites with different Co-doping levels were successfully synthesized by a simple one-step solution route at low temperature (95 deg. C) in this study. The structure and morphology of the samples thus obtained were characterized by XRD, EDS, XPS and FESEM. Results show that cobalt ions, in the oxidation state of Co{sup 2+}, replace Zn{sup 2+} ions in the ZnO lattice without changing its wurtzite structure. The dopant content varies from 0.59% to 5.39%, based on Co-doping levels. The pure ZnO particles exhibit well-defined 3D flower-like morphology with an average size of 550 nm, while the particles obtained after Co-doping are mostly cauliflower-like nanoclusters with an average size of 120 nm. Both the flower-like pure ZnO and the cauliflower-like Co:ZnO nanoclusters are composed of densely arrayed nanorods. The optical properties of the ZnO nanocrystallites following Co-doping were also investigated by UV-Visible absorption and Photoluminescence spectra. Our results indicate that Co-doping can change the energy-band structure and effectively adjust the luminescence properties of ZnO nanocrystallites. - Highlights: > Co-doped ZnO nanocrystallites were synthesized via a simple one-step solution route. > Co{sup 2+} ions incorporated into the ZnO lattice without changing its wurtzite structure. > Co-doping changed the energy band structure of ZnO. > Co-doping effectively adjusted the luminescence properties of ZnO nanocrystallites.

  20. Room temperature ferromagnetism in Cu doped ZnO

    Science.gov (United States)

    Ali, Nasir; Singh, Budhi; Khan, Zaheer Ahmed; Ghosh, Subhasis

    2018-05-01

    We report the room temperature ferromagnetism in 2% Cu doped ZnO films grown by RF magnetron sputtering in different argon and oxygen partial pressure. X-ray photoelectron spectroscopy was used to ascertain the oxidation states of Cu in ZnO. The presence of defects within Cu-doped ZnO films can be revealed by electron paramagnetic resonance. It has been observed that saturated magnetic moment increase as we increase the zinc vacancies during deposition.

  1. Cobalt doped proangiogenic hydroxyapatite for bone tissue engineering application

    International Nuclear Information System (INIS)

    Kulanthaivel, Senthilguru; Roy, Bibhas; Agarwal, Tarun; Giri, Supratim; Pramanik, Krishna; Pal, Kunal; Ray, Sirsendu S.; Maiti, Tapas K.; Banerjee, Indranil

    2016-01-01

    ABSTRACT: The present study delineates the synthesis and characterization of cobalt doped proangiogenic–osteogenic hydroxyapatite. Hydroxyapatite samples, doped with varying concentrations of bivalent cobalt (Co"2"+) were prepared by the ammoniacal precipitation method and the extent of doping was measured by ICP–OES. The crystalline structure of the doped hydroxyapatite samples was confirmed by XRD and FTIR studies. Analysis pertaining to the effect of doped hydroxyapatite on cell cycle progression and proliferation of MG-63 cells revealed that the doping of cobalt supported the cell viability and proliferation up to a threshold limit. Furthermore, such level of doping also induced differentiation of the bone cells, which was evident from the higher expression of differentiation markers (Runx2 and Osterix) and better nodule formation (SEM study). Western blot analysis in conjugation with ELISA study confirmed that the doped HAp samples significantly increased the expression of HIF-1α and VEGF in MG-63 cells. The analysis described here confirms the proangiogenic–osteogenic properties of the cobalt doped hydroxyapatite and indicates its potential application in bone tissue engineering. - Highlights: • Cobalt (Co"+"2) doped hydroxyapatite (Co-HAp) can be prepared by the wet chemical method. • The concentration of Co"+"2 influences the physico-chemical properties of HAp. • Co-HAp was found to be biocompatible and osteogenic. • Co-HAp enhanced cellular VEGF secretion through HIF-1α stabilization. • The optimum biological performance of Co-HAp was achieved for 0.33% (w/w) Co"+"2 doping.

  2. Photoluminescence properties of Co-doped ZnO nanocrystals

    DEFF Research Database (Denmark)

    Lommens, P.; Smet, P.F.; De Mello Donega, C.

    2006-01-01

    We performed photoluminescence experiments on colloidal, Co -doped ZnO nanocrystals in order to study the electronic properties of Co in a ZnO host. Room temperature measurements showed, next to the ZnO exciton and trap emission, an additional emission related to the Co dopant. The spectral...... position and width of this emission does not depend on particle size or Co concentration. At 8 K, a series of ZnO bulk phonon replicas appear on the Co-emission band. We conclude that Co ions are strongly localized in the ZnO host, making the formation of a Co d-band unlikely. Magnetic measurements...

  3. Impacts of Co doping on ZnO transparent switching memory device characteristics

    Energy Technology Data Exchange (ETDEWEB)

    Simanjuntak, Firman Mangasa; Wei, Kung-Hwa [Department of Materials Science and Engineering, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Prasad, Om Kumar [Department of Electrical Engineering and Computer Science, National Chiao Tung University, Hsinchu 30010, Taiwan (China); Panda, Debashis [Department of Electronics Engineering, National Institute of Science and Technology, Berhampur, Odisha 761008 (India); Lin, Chun-An; Tsai, Tsung-Ling; Tseng, Tseung-Yuen, E-mail: tseng@cc.nctu.edu.tw [Department of Electronics Engineering and Institute of Electronics, National Chiao Tung University, Hsinchu 30010, Taiwan (China)

    2016-05-02

    The resistive switching characteristics of indium tin oxide (ITO)/Zn{sub 1−x}Co{sub x}O/ITO transparent resistive memory devices were investigated. An appropriate amount of cobalt dopant in ZnO resistive layer demonstrated sufficient memory window and switching stability. In contrast, pure ZnO devices demonstrated a poor memory window, and using an excessive dopant concentration led to switching instability. To achieve suitable memory performance, relying only on controlling defect concentrations is insufficient; the grain growth orientation of the resistive layer must also be considered. Stable endurance with an ON/OFF ratio of more than one order of magnitude during 5000 cycles confirmed that the Co-doped ZnO device is a suitable candidate for resistive random access memory application. Additionally, fully transparent devices with a high transmittance of up to 90% at wavelength of 550 nm have been fabricated.

  4. Cobalt doped proangiogenic hydroxyapatite for bone tissue engineering application.

    Science.gov (United States)

    Kulanthaivel, Senthilguru; Roy, Bibhas; Agarwal, Tarun; Giri, Supratim; Pramanik, Krishna; Pal, Kunal; Ray, Sirsendu S; Maiti, Tapas K; Banerjee, Indranil

    2016-01-01

    The present study delineates the synthesis and characterization of cobalt doped proangiogenic-osteogenic hydroxyapatite. Hydroxyapatite samples, doped with varying concentrations of bivalent cobalt (Co(2+)) were prepared by the ammoniacal precipitation method and the extent of doping was measured by ICP-OES. The crystalline structure of the doped hydroxyapatite samples was confirmed by XRD and FTIR studies. Analysis pertaining to the effect of doped hydroxyapatite on cell cycle progression and proliferation of MG-63 cells revealed that the doping of cobalt supported the cell viability and proliferation up to a threshold limit. Furthermore, such level of doping also induced differentiation of the bone cells, which was evident from the higher expression of differentiation markers (Runx2 and Osterix) and better nodule formation (SEM study). Western blot analysis in conjugation with ELISA study confirmed that the doped HAp samples significantly increased the expression of HIF-1α and VEGF in MG-63 cells. The analysis described here confirms the proangiogenic-osteogenic properties of the cobalt doped hydroxyapatite and indicates its potential application in bone tissue engineering. Copyright © 2015 Elsevier B.V. All rights reserved.

  5. Optoelectronic properties of doped hydrothermal ZnO thin films

    KAUST Repository

    Mughal, Asad J.; Carberry, Benjamin; Oh, Sang Ho; Myzaferi, Anisa; Speck, James S.; Nakamura, Shuji; DenBaars, Steven P.

    2017-01-01

    , or In were evaluated for their optoelectronic properties. Inductively coupled plasma atomic emission spectroscopy was used to determine the concentration of dopants within the ZnO films. While Al and Ga-doped films showed linear incorporation rates

  6. Preparation and characterization of Co-doped ZnO nanomaterials

    International Nuclear Information System (INIS)

    Yang Huaming; Nie Sha

    2009-01-01

    Freeze-drying is a convenient cryochemical powder processing method. In this paper, Co-doped ZnO nanomaterials (CZN) with Co content from 2 mol% to 10 mol% have been successfully synthesized via a novel freeze-drying route. X-ray diffraction (XRD), transmission electronic microscopy (TEM) and high-resolution TEM (HRTEM) were used to characterize the structure and morphology of the as-synthesized samples. All samples have a similar hexagonal wurtzite phase without metal cobalt, cobalt oxides or composites in the samples with Co concentration below 6 mol%. TEM image shows that CZN (4 mol% Co) is nanometer scale with average crystal size of 40 nm. Samples have a spherical morphology with moderate aggregation. The band gap energy of CZN from ultraviolet-visible (UV-vis) spectroscopy decreases with increasing the Co doping concentration

  7. Cobalt doped proangiogenic hydroxyapatite for bone tissue engineering application

    Energy Technology Data Exchange (ETDEWEB)

    Kulanthaivel, Senthilguru [Department of Biotechnology and Medical Engineering, National Institute of Technology, Rourkela, Odisha 769008 (India); Roy, Bibhas [Department of Biotechnology, Indian Institute of Technology Kharagpur, Kharagpur, West Bengal 721302 (India); Agarwal, Tarun [Department of Biotechnology and Medical Engineering, National Institute of Technology, Rourkela, Odisha 769008 (India); Giri, Supratim [Department of Chemistry, National Institute of Technology, Rourkela, Odisha 769008 (India); Pramanik, Krishna; Pal, Kunal; Ray, Sirsendu S. [Department of Biotechnology and Medical Engineering, National Institute of Technology, Rourkela, Odisha 769008 (India); Maiti, Tapas K. [Department of Biotechnology, Indian Institute of Technology Kharagpur, Kharagpur, West Bengal 721302 (India); Banerjee, Indranil, E-mail: indraniliit@gmail.com [Department of Biotechnology and Medical Engineering, National Institute of Technology, Rourkela, Odisha 769008 (India)

    2016-01-01

    ABSTRACT: The present study delineates the synthesis and characterization of cobalt doped proangiogenic–osteogenic hydroxyapatite. Hydroxyapatite samples, doped with varying concentrations of bivalent cobalt (Co{sup 2+}) were prepared by the ammoniacal precipitation method and the extent of doping was measured by ICP–OES. The crystalline structure of the doped hydroxyapatite samples was confirmed by XRD and FTIR studies. Analysis pertaining to the effect of doped hydroxyapatite on cell cycle progression and proliferation of MG-63 cells revealed that the doping of cobalt supported the cell viability and proliferation up to a threshold limit. Furthermore, such level of doping also induced differentiation of the bone cells, which was evident from the higher expression of differentiation markers (Runx2 and Osterix) and better nodule formation (SEM study). Western blot analysis in conjugation with ELISA study confirmed that the doped HAp samples significantly increased the expression of HIF-1α and VEGF in MG-63 cells. The analysis described here confirms the proangiogenic–osteogenic properties of the cobalt doped hydroxyapatite and indicates its potential application in bone tissue engineering. - Highlights: • Cobalt (Co{sup +2}) doped hydroxyapatite (Co-HAp) can be prepared by the wet chemical method. • The concentration of Co{sup +2} influences the physico-chemical properties of HAp. • Co-HAp was found to be biocompatible and osteogenic. • Co-HAp enhanced cellular VEGF secretion through HIF-1α stabilization. • The optimum biological performance of Co-HAp was achieved for 0.33% (w/w) Co{sup +2} doping.

  8. Bioactivity and mechanical behaviour of cobalt oxide-doped ...

    Indian Academy of Sciences (India)

    tive base glass and cobalt oxide-doped glass were prepared by the addition of cobalt oxide (0, ... and 1 N HCl at 37. ◦. C as compared with the ... SO2−. 4. Cl. −. Simulated body fluid. 142.0. 5.0. 1.5. 2.5. 4.2. 1.0. 0.5. 147.8. Human blood plasma ...

  9. Facile synthesis of cobalt-doped zinc oxide thin films for highly efficient visible light photocatalysts

    Energy Technology Data Exchange (ETDEWEB)

    Altintas Yildirim, Ozlem, E-mail: ozlemaltintas@gmail.com [Department of Metallurgical and Materials Engineering, Selcuk University, Konya (Turkey); Arslan, Hanife; Sönmezoğlu, Savaş [Department of Metallurgical and Materials Engineering, Karamanoglu Mehmetbey University, Karaman (Turkey); Nanotechnology R& D Laboratory, Karamanoglu Mehmetbey University, Karaman (Turkey)

    2016-12-30

    Highlights: • Photocatalytically active Co-ZnO thin film was obtained by sol-gel method. • Co{sup 2+} doping narrowed the band gap of pure ZnO to an extent of 3.18 eV. • Co-ZnO was effective in MB degradation under visible light. • Optimum dopant content to show high performance was 3 at.%. - Abstract: Cobalt-doped zinc oxide (Co:ZnO) thin films with dopant contents ranging from 0 to 5 at.% were prepared using the sol–gel method, and their structural, morphological, optical, and photocatalytic properties were characterized. The effect of the dopant content on the photocatalytic properties of the films was investigated by examining the degradation behavior of methylene blue (MB) under visible light irradiation, and a detailed investigation of their photocatalytic activities was performed by determining the apparent quantum yields (AQYs). Co{sup 2+} ions were observed to be substitutionally incorporated into Zn{sup 2+} sites in the ZnO crystal, leading to lattice parameter constriction and band gap narrowing due to the photoinduced carriers produced under the visible light irradiation. Thus, the light absorption range of the Co:ZnO films was improved compared with that of the undoped ZnO film, and the Co:ZnO films exhibited highly efficient photocatalytic activity (∼92% decomposition of MB after 60-min visible light irradiation for the 3 at.% Co:ZnO film). The AQYs of the Co:ZnO films were greatly enhanced under visible light irradiation compared with that of the undoped ZnO thin film, demonstrating the effect of the Co doping level on the photocatalytic activity of the films.

  10. Magnetic and resonance properties of ferrihydrite nanoparticles doped with cobalt

    Science.gov (United States)

    Stolyar, S. V.; Yaroslavtsev, R. N.; Iskhakov, R. S.; Bayukov, O. A.; Balaev, D. A.; Dubrovskii, A. A.; Krasikov, A. A.; Ladygina, V. P.; Vorotynov, A. M.; Volochaev, M. N.

    2017-03-01

    Powders of undoped ferrihydrite nanoparticles and ferrihydrite nanoparticles doped with cobalt in the ratio of 5: 1 have been prepared by hydrolysis of 3 d-metal salts. It has been shown using Mössbauer spectroscopy that cobalt is uniformly distributed over characteristic crystal-chemical positions of iron ions. The blocking temperatures of ferrihydrite nanoparticles have been determined. The nanoparticle sizes, magnetizations, surface anisotropy constants, and bulk anisotropy constants have been estimated. The doping of ferrihydrite nanoparticles with cobalt leads to a significant increase in the anisotropy constant of a nanoparticle and to the formation of surface rotational anisotropy with the surface anisotropy constant K u = 1.6 × 10-3 erg/cm2.

  11. Structural, optical and magnetic properties of nanocrystalline Co-doped ZnO thin films grown by sol-gel

    Energy Technology Data Exchange (ETDEWEB)

    Kayani, Zohra Nazir; Shah, Iqra; Zulfiqar, Bareera; Sabah, Aneeqa [Lahore College for Women Univ., Lahore (Pakistan); Riaz, Saira; Naseem, Shahzad [Univ. of the Punjab, Lahore (Pakistan). Centre of Excellence in Solid State Physics

    2018-04-01

    Cobalt-doped ZnO thin films have been deposited using a sol-gel route by changing the number of coats on the substrate from 6 to 18. This project deals with various film thicknesses by increasing the number of deposited coats. The effect of thickness on structural, magnetic, surface morphology and optical properties of Co-doped ZnO thin film was studied. The crystal structure of the Co-doped ZnO films was investigated by X-ray diffraction. The films have polycrystalline wurtzite hexagonal structures. A Co{sup 2+} ion takes the place of a Zn{sup 2+} ion in the lattice without creating any distortion in its hexagonal wurtzite structure. An examination of the optical transmission spectra showed that the energy band gap of the Co-doped ZnO films increased from 3.87 to 3.97 eV with an increase in the number of coatings on the substrate. Ferromagnetic behaviour was confirmed by measurements using a vibrating sample magnetometer. The surface morphology of thin films was assessed by scanning electron microscope. The grain size on the surface of thin films increased with an increase in the number of coats.

  12. Synthesis Structural and Optical Properties Of (Co, Al) co-doped ZnO Nano Particles

    Science.gov (United States)

    Swapna, P.; Venkatramana Reddy, S.

    2018-02-01

    We prepared (Co, Al) co-doped ZnO nanostructures using the method chemical co-precipitation successfully, at room temperature using PEG (Poly ethylene glycol) as stabilizing agent. Samples are prepared with different concentrations by keeping aluminium at 5 mol percent constant and varying the concentration of cobalt from 1 to 5 mol percent. After the preparation all the samples are carefully subjected to characterizations such as XRD, SEM with EDS, TEM, PL and UV-VIS-NIR. XRD pattern shows that all the samples possess hexagonal wurtzite crystal structure having no secondary phases pertaining to Al or cobalt, which shows successful dissolution of the dopents. TEM results shows the accurate size of particles and is confirmed the XRD data. SEM images of all the samples shows that particles are in nearly spherical shape, EDS spectrum reveals that incorporation of cobalt and aluminum in host lattice. PL spectrum shows that all the samples containing two prominent peaks centered at 420 nm and 446 nm. UV-VIS-NIR spectra has shown three absorptions peaks in the range of wavelength 550 nm to 700 nm, which are ascribed as typical d-d transitions of cobalt ions.

  13. Co-Doped ZnO nanoparticles: minireview.

    Science.gov (United States)

    Djerdj, Igor; Jaglicić, Zvonko; Arcon, Denis; Niederberger, Markus

    2010-07-01

    Diluted magnetic semiconductors with a Curie temperature exceeding 300 K are promising candidates for spintronic devices and spin-based electronic technologies. We review recent achievements in the field of one of them: Co-doped ZnO at the nanoparticulate scale.

  14. Atomic layer deposition of B-doped ZnO using triisopropyl borate as the boron precursor and comparison with Al-doped ZnO

    NARCIS (Netherlands)

    Garcia - Alonso, D.; Potts, S.E.; Helvoirt, van C.A.A.; Verheijen, M.A.; Kessels, W.M.M.

    2015-01-01

    Doped ZnO films are an important class of transparent conductive oxides, with many applications demanding increased growth control and low deposition temperatures. Therefore, the preparation of B-doped ZnO films by atomic layer deposition (ALD) at 150 °C was studied. The B source was triisopropyl

  15. Performance of Cr-doped ZnO for acetone sensing

    Energy Technology Data Exchange (ETDEWEB)

    Al-Hardan, N.H., E-mail: naif_imen@ukm.my [Institute of Microengineering and Nanoelectronics (IMEN), Universiti Kebangsaan Malaysia, 43600 Bangi, Selangor (Malaysia); Abdullah, M.J.; Aziz, A. Abdul [School of Physics, Universiti Sains Malaysia, 11800 USM, Penang (Malaysia)

    2013-04-01

    Zinc oxide (ZnO) doped with chromium (Cr) was synthesized by reactive co-sputtering for gas sensing applications. The effect of varying the contents of Cr (from 1 to 4 at%) on the ZnO gas sensor response was studied. X-ray diffraction analysis reveals the high orientation of c-axis of the prepared films. The optimum operating temperature of the undoped ZnO was 400 °C and shifted to 300 °C for the Cr-doped ZnO under the acetone vapour. The 1% Cr doping ZnO gas sensor was most sensitive for the acetone vapour. The ability of the 1% Cr-doped ZnO to produce repeatable results under different acetone vapour concentrations was tested. The timing properties of the doped Cr ZnO gas sensor were 70 and 95 s for the rise and recovery time respectively.

  16. Properties of Mn-doped ZnO nanopowder

    Energy Technology Data Exchange (ETDEWEB)

    Schlenker, E.; Bakin, A.; Wehmann, H.H.; Al-Suleiman, M.; Waag, A. [Technical University Braunschweig, Institute of Semiconductor Technology, Braunschweig (Germany); Schmid, H.; Mader, W. [Universitaet Bonn, Institut fuer Anorganische Chemie, Bonn (Germany); Bremers, H.; Hangleiter, A. [Technical University Braunschweig, Institute of Applied Physics, Braunschweig (Germany); Luedke, J.; Albrecht, M. [Physikalisch-Technische Bundesanstalt (PTB), Braunschweig (Germany)

    2008-06-15

    The structural and magnetic properties of Mn-doped ZnO nanopowder are investigated and compared to undoped ZnO crystals. Mn incorporation leads to an increase in the lattice constants as revealed by X-ray diffraction measurements. An inhomogeneous distribution of the Mn atoms within the nanopowder was detected by energy-dispersive X-ray and electron-energy-loss spectroscopy measurements. Magnetic features are investigated by means of SQUID magnetometry on ensembles of powder particles as well as by magnetic force microscopy to study the behavior of single grains. (orig.)

  17. Morphological transition of ZnO nanostructures influenced by magnesium doping

    International Nuclear Information System (INIS)

    Premkumar, T.; Zhou, Y.S.; Gao, Y.; Baskar, K.; Jiang, L.; Lu, Y.F.

    2012-01-01

    Wurtzite zinc oxide (ZnO) nanochains have been synthesized through high-pressure pulsed laser deposition. The chain-like ZnO nanostructures were obtained from magnesium (Mg) doped ZnO targets, whereas vertically aligned nanorods were obtained from primitive ZnO targets. The Mg doping has influenced the morphological transition of ZnO nanostructures from nanorods to nanochains. The field emission scanning electron microscope images revealed the growth of beaded ZnO nanochains. The ZnO nanochains of different diameters 40 and 120 nm were obtained. The corresponding micro-Raman spectra showed strong E 2H mode of ZnO, which confirmed the good crystallinity of the nanochains. In addition to near band edge emission at 3.28 eV, ZnO nanochains show broad deep level emission at 2.42 eV than that of ZnO nanorods.

  18. Enhanced ultraviolet photo-response in Dy doped ZnO thin film

    Science.gov (United States)

    Kumar, Pawan; Singh, Ranveer; Pandey, Praveen C.

    2018-02-01

    In the present work, a Dy doped ZnO thin film deposited by the spin coating method has been studied for its potential application in a ZnO based UV detector. The investigations on the structural property and surface morphology of the thin film ensure that the prepared samples are crystalline and exhibit a hexagonal crystal structure of ZnO. A small change in crystallite size has been observed due to Dy doping in ZnO. AFM analysis ascertains the grain growth and smooth surface of the thin films. The Dy doped ZnO thin film exhibits a significant enhancement in UV region absorption as compared to the pure ZnO thin film, which suggests that Dy doped ZnO can be used as a UV detector. Under UV irradiation of wavelength 325 nm, the photocurrent value of Dy doped ZnO is 105.54 μA at 4.5 V, which is 31 times greater than that of the un-doped ZnO thin film (3.39 μA). The calculated value of responsivity is found to increase significantly due to the incorporation of Dy in the ZnO lattice. The observed higher value of photocurrent and responsivity could be attributed to the substitution of Dy in the ZnO lattice, which enhances the conductivity, electron mobility, and defects in ZnO and benefits the UV sensing property.

  19. Activities towards p-type doping of ZnO

    International Nuclear Information System (INIS)

    Brauer, G; Kuriplach, J; Ling, C C; Djurisic, A B

    2011-01-01

    Zinc oxide (ZnO) is an interesting and promising semiconductor material for many potential applications, e.g. in opto-electronics and for sensor devices. However, its p-type doping represents a challenging problem, and the physical reasons of its mostly n-type conductivity are not perfectly clear at present. Efforts to achieve p-type conductivity by ion implantation are reviewed, and ways to achieve p-type ZnO nanorods and thin films through various growth conditions are summarized. Then, issues associated with the preparation of Schottky contacts is discussed in some detail as this is a requirement of the device formation process. Finally, the possible incorporation of hydrogen and nitrogen into structural defects, which can act as trapping sites for positrons, is discussed in the context of experimental and theoretical positron results and the estimated H and N content in a variety of ZnO materials.

  20. Activities towards p-type doping of ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Brauer, G [Institut fuer Ionenstrahlphysik und Materialforschung, Forschungszentrum Dresden-Rossendorf, Postfach 510119, D-01314 Dresden (Germany); Kuriplach, J [Department of Low Temperature Physics, Charles University, V Holetovickach 2, CZ-18000 Prague (Czech Republic); Ling, C C; Djurisic, A B, E-mail: g.brauer@fzd.de [Department of Physics, University of Hong Kong, Pokfulam Road (Hong Kong)

    2011-01-10

    Zinc oxide (ZnO) is an interesting and promising semiconductor material for many potential applications, e.g. in opto-electronics and for sensor devices. However, its p-type doping represents a challenging problem, and the physical reasons of its mostly n-type conductivity are not perfectly clear at present. Efforts to achieve p-type conductivity by ion implantation are reviewed, and ways to achieve p-type ZnO nanorods and thin films through various growth conditions are summarized. Then, issues associated with the preparation of Schottky contacts is discussed in some detail as this is a requirement of the device formation process. Finally, the possible incorporation of hydrogen and nitrogen into structural defects, which can act as trapping sites for positrons, is discussed in the context of experimental and theoretical positron results and the estimated H and N content in a variety of ZnO materials.

  1. Mn-doped ZnO nanocrystals synthesized by sonochemical method: Structural, photoluminescence, and magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Othman, A.A., E-mail: aaelho@yahoo.com [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt); Osman, M.A. [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt); Ibrahim, E.M.M. [Sohag University, Faculty of Science, Department of Physics, Sohag 82524 (Egypt); Ali, Manar A.; Abd-Elrahim, A.G. [Assiut University, Faculty of Science, Department of Physics, Assiut 71516 (Egypt)

    2017-05-15

    Highlights: • Mn-doped ZnO nanostructures were synthesized by the sonochemical method. • Structural, morphological, optical, photoluminescence and magnetic properties were investigated. • Mn-doped ZnO nanostructures reveal a blue shift of the optical band gap. • Photoluminescence spectra of Mn-doped ZnO nanostructures show quenching in the emission intensity. • Mn-doped ZnO nanostructures exhibit ferromagnetic ordering at room temperature. - Abstract: This work reports the synthesis of Mn-doped ZnO nanostructures using ice-bath assisted sonochemical technique. The impact of Mn-doping on structural, morphological, optical, and magnetic properties of ZnO nanostructures is studied. The morphological study shows that the lower doped samples possess mixtures of nanosheets and nanorods while the increase in Mn content leads to improvement of an anisotropic growth in a preferable orientation to form well-defined edge rods at Mn content of 0.04. UV–vis absorption spectra show that the exciton peak in the UV region is blue shifted due to Mn incorporation into the ZnO lattice. Doping ZnO with Mn ions leads to a reduction in the PL intensity due to a creation of more non-radiative recombination centers. The magnetic measurements show that the Mn-doped ZnO nanostructures exhibit ferromagnetic ordering at room temperature, as well as variation of the Mn content can significantly affect the ferromagnetic behavior of the samples.

  2. Positron annihilation spectroscopy in doped p-type ZnO

    Science.gov (United States)

    Majumdar, Sayanee; Sanyal, D.

    2011-07-01

    Positron annihilation lifetime (PAL) spectroscopy has been used to investigate the vacancy type defect of the Li and N doped ZnO. The mono-vacancies, shallow -vacancies and open volume defects have been found in both the Li and N doped ZnO. The mono-vacancies, shallow-vacancies and open volume defects increase in N-doped ZnO as the size of N is quite high compared to Li. Positron annihilation study showed that the doping above 1-3% Li and 3-4% N in ZnO are not required in order to achieve low resistivity, high hole concentration and good mobility.

  3. Al-doped ZnO nanofilms: Synthesis and characterization

    Energy Technology Data Exchange (ETDEWEB)

    Huczko, A.; Dabrowska, A. [Department of Chemistry, Warsaw University, Warsaw (Poland); Madhup, D.K. [Department of Physics, Kathmandu University, Dhulikhel (Nepal); College of Biomedical Engineering and Applied Sciences, Hadigaun, Kathmandu (Nepal); Subedi, D.P.; Chimouriya, S.P. [Department of Physics, Kathmandu University, Dhulikhel (Nepal)

    2010-12-15

    Al-doped and un-doped ZnO nanofilms on quartz substrate were obtained by ultrasonic spray pyrolysis of salt solutions (mole concentration of Al within 0-10%). The films were characterized by Scanning electron microscopy (SEM), X-ray diffraction (XRD), Atomic force microscopy (AFM) and UV spectroscopy to study the morphology and optical properties. The optical studies showed that the increase in Al within ZnO thin layer increases its band gap energy. The obtained value of band gap energy is very close to the determined oscillation energy. However, the dispersion energy is nearly half of band gap energy value. (Copyright copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  4. Characterization of Mn doped ZnO nanopowder

    Energy Technology Data Exchange (ETDEWEB)

    Schlenker, Eva; Bakin, Andrey; Al-Suleiman, Mohamed; Wehmann, Hergo-Heinrich; Waag, Andreas [Institute of Semiconductor Technology, TU Braunschweig (Germany); Schmid, Herbert; Mader, Werner [Institute for Inorganic Chemistry, University Bonn (Germany); Bremers, Heiko; Hangleiter, Andreas [Institute of Applied Physics, TU Braunschweig (Germany)

    2008-07-01

    In the quest of materials for spintronic applications, diluted magnetic semiconductors recently attracted much attention. The main challenge is finding a ferromagnetic material with Curie temperature T{sub c}>300 K whose magnetic properties can be controlled electrically. The interest was particularly focused on Zn(TM)O since theoretical calculations predict that ZnO containing Mn could exhibit ferromagnetism with T{sub c} above room temperature. In the present study, the structural and magnetic properties of Mn doped ZnO nanopowder are investigated and compared to undoped ZnO crystals. Doping of ZnO with Mn results in increased lattice constants as revealed by XRD. However, an inhomogeneous distribution of the Mn dopants within the nanopowder was revealed by energy-dispersive X-ray and electron energy-loss spectroscopy. Magnetic properties are investigated by means of SQUID measurements on aggregates of powder particles as well as by MFM to study the behavior of single grains. The MFM image differs significantly from the topography as imaged by AFM and suggests the existence of long-ranging magnetic signals emerging from the sample.

  5. Improving ultraviolet photodetection of ZnO nanorods by Cr doped ZnO encapsulation process

    Science.gov (United States)

    Safa, S.; Mokhtari, S.; Khayatian, A.; Azimirad, R.

    2018-04-01

    Encapsulated ZnO nanorods (NRs) with different Cr concentration (0-4.5 at.%) were prepared in two different steps. First, ZnO NRs were grown by hydrothermal method. Then, they were encapsulated by dip coating method. The prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy, and ultraviolet (UV)-visible spectrophotometer analyses. XRD analysis proved that Cr incorporated into the ZnO structure successfully. Based on optical analysis, band gap changes in the range of 2.74-3.84 eV. Finally, UV responses of all samples were deeply investigated. It revealed 0.5 at.% Cr doped sample had the most photocurrent (0.75 mA) and photoresponsivity (0.8 A/W) of all which were about three times greater than photocurrent and photoresponsivity of the undoped sample.

  6. Preparation and characterization of Ce-doped ZnO nanofibers by an electrospinning method

    Directory of Open Access Journals (Sweden)

    Jong-Pil Kim

    2011-02-01

    Full Text Available ZnO and Ce-doped ZnO Nanofibers on (111 Pt/SiO2/Si substrates were produced using an electrospinning technique. The as-prepared composite fibres were subjected to high-temperature calcination to produce inorganic fibers. After calcining at a temperature of 500 °C, the average diameter of the ZnO and Ce-doped ZnO nanofibers were determined to be 170 nm and 225 nm, respectively. The average grain size of the ZnO and Ce-doped ZnO nanofibers were about 50 nm and 57 nm, respectively. The microstructure, chemical bonding state and photoluminescence of the produced ZnO and Ce-doped ZnO nanofibers were investigated. The Ce-doped ZnO nanofiber can be assigned to the presence of Ce ions on substitutional sites of Zn ions and the Ce3+ state from X-ray photoelectron spectra. Compared with PL spectra of ZnO nanofibers, the peak position of the UV emission of the Ce-doped ZnO nanofibers is sharply suppressed while the green emission band is highly enhanced.

  7. Optoelectronic properties of doped hydrothermal ZnO thin films

    KAUST Repository

    Mughal, Asad J.

    2017-03-10

    Group III impurity doped ZnO thin films were deposited on MgAl2O3 substrates using a simple low temperature two-step deposition method involving atomic layer deposition and hydrothermal epitaxy. Films with varying concentrations of either Al, Ga, or In were evaluated for their optoelectronic properties. Inductively coupled plasma atomic emission spectroscopy was used to determine the concentration of dopants within the ZnO films. While Al and Ga-doped films showed linear incorporation rates with the addition of precursors salts in the hydrothermal growth solution, In-doped films were shown to saturate at relatively low concentrations. It was found that Ga-doped films showed the best performance in terms of electrical resistivity and optical absorbance when compared to those doped with In or Al, with a resistivity as low as 1.9 mΩ cm and an optical absorption coefficient of 441 cm−1 at 450 nm.

  8. Defects induced ferromagnetism in Mn doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Chattopadhyay, S.; Neogi, S.K. [Department of Physics, University of Calcutta, 92A P C Road, Kolkata 700009 (India); Sarkar, A. [Department of Physics, Bangabasi Morning College, Kolkata 700009 (India); Mukadam, M.D.; Yusuf, S.M. [Solid State Physics Division, Bhaba Atomic Research Centre, Mumbai 400085 (India); Banerjee, A. [Department of Physics, University of Calcutta, 92A P C Road, Kolkata 700009 (India); Bandyopadhyay, S., E-mail: sbaphy@caluniv.ac.i [Department of Physics, University of Calcutta, 92A P C Road, Kolkata 700009 (India)

    2011-02-15

    Single phase Mn doped (2 at%) ZnO samples have been synthesized by the solid-state reaction technique. Before the final sintering at 500 {sup o}C, the mixed powders have been milled for different milling periods (6, 24, 48 and 96 h). The grain sizes of the samples are very close to each other ({approx}32{+-}4 nm). However, the defective state of the samples is different from each other as manifested from the variation of magnetic properties and electrical resistivity with milling time. All the samples have been found to be ferromagnetic with clear hysteresis loops at room temperature. The maximum value for saturation magnetization (0.11 {mu}{sub B}/Mn atom) was achieved for 96 h milled sample. Electrical resistivity has been found to increase with increase in milling time. The most resistive sample bears the largest saturation magnetization. Variation of average positron lifetime with milling time bears a close similarity with that of the saturation magnetization. This indicates the key role played by open volume vacancy defects, presumably zinc vacancies near grain surfaces, in inducing ferromagnetic order in Mn doped ZnO. To attain optimum defect configuration favorable for ferromagnetism in this kind of samples proper choice of milling period and annealing conditions is required. - Research highlights: 2 at% Mn doped ZnO samples are single phase. All the samples exhibit ferromagnetism at room temperature. Correlation between saturation magnetization and positron annihilation lifetime established.

  9. Defects induced ferromagnetism in Mn doped ZnO

    International Nuclear Information System (INIS)

    Chattopadhyay, S.; Neogi, S.K.; Sarkar, A.; Mukadam, M.D.; Yusuf, S.M.; Banerjee, A.; Bandyopadhyay, S.

    2011-01-01

    Single phase Mn doped (2 at%) ZnO samples have been synthesized by the solid-state reaction technique. Before the final sintering at 500 o C, the mixed powders have been milled for different milling periods (6, 24, 48 and 96 h). The grain sizes of the samples are very close to each other (∼32±4 nm). However, the defective state of the samples is different from each other as manifested from the variation of magnetic properties and electrical resistivity with milling time. All the samples have been found to be ferromagnetic with clear hysteresis loops at room temperature. The maximum value for saturation magnetization (0.11 μ B /Mn atom) was achieved for 96 h milled sample. Electrical resistivity has been found to increase with increase in milling time. The most resistive sample bears the largest saturation magnetization. Variation of average positron lifetime with milling time bears a close similarity with that of the saturation magnetization. This indicates the key role played by open volume vacancy defects, presumably zinc vacancies near grain surfaces, in inducing ferromagnetic order in Mn doped ZnO. To attain optimum defect configuration favorable for ferromagnetism in this kind of samples proper choice of milling period and annealing conditions is required. - Research highlights: → 2 at% Mn doped ZnO samples are single phase. → All the samples exhibit ferromagnetism at room temperature. → Correlation between saturation magnetization and positron annihilation lifetime established.

  10. Cobalt-doped nanohydroxyapatite: synthesis, characterization, antimicrobial and hemolytic studies

    Energy Technology Data Exchange (ETDEWEB)

    Tank, Kashmira P., E-mail: kashmira_physics@yahoo.co.in [Saurashtra University, Crystal Growth Laboratory, Physics Department (India); Chudasama, Kiran S.; Thaker, Vrinda S. [Saurashtra University, Bioscience Department (India); Joshi, Mihir J., E-mail: mshilp24@rediffmail.com [Saurashtra University, Crystal Growth Laboratory, Physics Department (India)

    2013-05-15

    Hydroxyapatite (Ca{sub 10}(PO{sub 4}){sub 6}(OH){sub 2}; HAP) is a major mineral component of the calcified tissues, and it has various applications in medicine and dentistry. In the present investigation, cobalt-doped hydroxyapatite (Co-HAP) nanoparticles were synthesized by surfactant-mediated approach and characterized by different techniques. The EDAX was carried out to estimate the amount of doping in Co-HAP. The transmission electron microscopy result suggested the transformation of morphology from needle shaped to spherical type on increasing the doping concentration. The powder XRD study indicated the formation of a new phase of brushite for higher concentration of cobalt. The average particle size and strain were calculated using Williamson-Hall analysis. The average particle size was found to be 30-60 nm. The FTIR study confirmed the presence of various functional groups in the samples. The antimicrobial activity was evaluated against four organisms Pseudomonas aeruginosa and Shigella flexneri as Gram negative as well as Micrococcus luteus and Staphylococcus aureus as Gram positive. The hemolytic test result suggested that all samples were non-hemolytic. The photoluminescence study was carried out to identify its possible applicability as a fluorescent probe.

  11. Cobalt-doped nanohydroxyapatite: synthesis, characterization, antimicrobial and hemolytic studies

    International Nuclear Information System (INIS)

    Tank, Kashmira P.; Chudasama, Kiran S.; Thaker, Vrinda S.; Joshi, Mihir J.

    2013-01-01

    Hydroxyapatite (Ca 10 (PO 4 ) 6 (OH) 2 ; HAP) is a major mineral component of the calcified tissues, and it has various applications in medicine and dentistry. In the present investigation, cobalt-doped hydroxyapatite (Co-HAP) nanoparticles were synthesized by surfactant-mediated approach and characterized by different techniques. The EDAX was carried out to estimate the amount of doping in Co-HAP. The transmission electron microscopy result suggested the transformation of morphology from needle shaped to spherical type on increasing the doping concentration. The powder XRD study indicated the formation of a new phase of brushite for higher concentration of cobalt. The average particle size and strain were calculated using Williamson–Hall analysis. The average particle size was found to be 30–60 nm. The FTIR study confirmed the presence of various functional groups in the samples. The antimicrobial activity was evaluated against four organisms Pseudomonas aeruginosa and Shigella flexneri as Gram negative as well as Micrococcus luteus and Staphylococcus aureus as Gram positive. The hemolytic test result suggested that all samples were non-hemolytic. The photoluminescence study was carried out to identify its possible applicability as a fluorescent probe.

  12. Morphology evolution of hydrothermally grown ZnO nanostructures on gallium doping and their defect structures

    Energy Technology Data Exchange (ETDEWEB)

    Pineda-Hernandez, G. [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico); Escobedo-Morales, A., E-mail: alejandroescobedo@hotmail.com [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico); Pal, U. [Instituto de Fisica, Benemerita Universidad Autonoma de Puebla, Apdo. Postal J-48, C.P. 72570 Puebla, Pue. (Mexico); Chigo-Anota, E. [Facultad de Ingenieria Quimica, Benemerita Universidad Autonoma de Puebla, C.P. 72570 Puebla, Pue. (Mexico)

    2012-08-15

    In the present article, the effect of gallium doping on the morphology, structural, and vibrational properties of hydrothermally grown ZnO nanostructures has been studied. It has been observed that incorporated gallium plays an important role on the growth kinetics and hence on the morphology evolution of the ZnO crystals. Ga doping in high concentration results in the contraction of ZnO unit cell, mainly along c-axis. Although Ga has high solubility in ZnO, heavy doping promotes the segregation of Ga atoms as a secondary phase. Incorporated Ga atoms strongly affect the vibrational characteristics of ZnO lattice and induce anomalous Raman modes. Possible mechanisms of morphology evolution and origin of anomalous Raman modes in Ga doped ZnO nanostructures are discussed. -- Highlights: Black-Right-Pointing-Pointer Ga doped ZnO nanostructures were successfully grown by hydrothermal chemical route. Black-Right-Pointing-Pointer Ga doping has strong effect on the resulting morphology of ZnO nanostructures. Black-Right-Pointing-Pointer Anomalous vibrational modes in wurtzite ZnO lattice are induced by Ga doping. Black-Right-Pointing-Pointer Incorporated Ga atoms accommodate at preferential lattice sites.

  13. Explanation of ferromagnetism origin in C-doped ZnO by first principle calculations

    International Nuclear Information System (INIS)

    El Amiri, A.; Lassri, H.; Hlil, E.K.; Abid, M.

    2015-01-01

    By ab-initio calculations, we systematically study possible source of ferromagnetism C-doped ZnO compound. The electronic structure and magnetic properties of C-doped ZnO with / without ZnO host and C defects were investigated using the Korringa–Kohn–Rostoker (KKR) method combined with coherent potential approximation (CPA). We show that Zn vacancy and presence of C defects (substitutional, interstitial or combination of both) induce the ferromagnetism in C-doped ZnO. From density of state (DOS) analysis, we show that p–p interaction between C atoms and/or C and O atoms is the mechanism of ferromagnetic coupling in C-doped ZnO. - Highlights: • We study the effect of ZnO host and C defects on ferromagnetism in C-doped ZnO. • Details of KKR method calculations performed to investigate both magnetic and electronic structures. • Magnetic moments, total and partial DOS for C-doped ZnO are well calculated and discussed. • Based on DOS calculations we interpret a origin of ferromagnetism in C-doped ZnO. • Mechanism of ferromagnetic coupling is well proposed

  14. Explanation of ferromagnetism origin in C-doped ZnO by first principle calculations

    Energy Technology Data Exchange (ETDEWEB)

    El Amiri, A., E-mail: aelamiri@casablanca.ma [Laboratoire de Physique Fondamentale et Appliquée (LPFA), Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco); Lassri, H. [Laboratoire de Physique des Matériaux, Micro-électronique, Automatique et Thermique (LPMMAT). Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco); Hlil, E.K. [Institut Néel, CNRS et Université Joseph Fourier, BP 166, 38042 Grenoble (France); Abid, M. [Laboratoire de Physique Fondamentale et Appliquée (LPFA), Faculté des Sciences Ain Chock, Université Hassan II, B.P. 5366 Mâarif, Casablanca, Maroc (Morocco)

    2015-01-15

    By ab-initio calculations, we systematically study possible source of ferromagnetism C-doped ZnO compound. The electronic structure and magnetic properties of C-doped ZnO with / without ZnO host and C defects were investigated using the Korringa–Kohn–Rostoker (KKR) method combined with coherent potential approximation (CPA). We show that Zn vacancy and presence of C defects (substitutional, interstitial or combination of both) induce the ferromagnetism in C-doped ZnO. From density of state (DOS) analysis, we show that p–p interaction between C atoms and/or C and O atoms is the mechanism of ferromagnetic coupling in C-doped ZnO. - Highlights: • We study the effect of ZnO host and C defects on ferromagnetism in C-doped ZnO. • Details of KKR method calculations performed to investigate both magnetic and electronic structures. • Magnetic moments, total and partial DOS for C-doped ZnO are well calculated and discussed. • Based on DOS calculations we interpret a origin of ferromagnetism in C-doped ZnO. • Mechanism of ferromagnetic coupling is well proposed.

  15. Systematic approach on the fabrication of Co doped ZnO semiconducting nanoparticles by mixture of fuel approach for Antibacterial applications

    Science.gov (United States)

    Rajendar, V.; Dayakar, T.; Shobhan, K.; Srikanth, I.; Venkateswara Rao, K.

    2014-11-01

    Zinc oxide (ZnO) is a wide band gap semiconductor (3.2 eV) with a high exciton binding energy (60 meV), where it has wide applications in advanced spintronic devices. The theoretical prediction of room temperature ferromagnetism and also antibacterial activity will be possible through the investigation of diluted magnetic semiconductors (DMS), such as transition metal doped ZnO, especially Cobalt doped ZnO. The aim of the work is the synthesis of Cobalt (Co) doped ZnO nanopowders were prepared Zn1-xCoxO (0 ⩽ x ⩾ 0.09) nanopowders from Sol-Gel auto combustion method have been synthesized with precursors such as Zinc and Cobalt nitrates with the assistance Ammonium acetate & Urea as fuel by increasing the cobalt concentration in zinc oxide and their structural, morphological, optical, Thermal, magnetic and antibacterial properties were studied by X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), Transmission Electron microscope (TEM), UV-visible spectroscopy, thermo gravimetric/differential thermal analysis (TG/DTA) and vibrating sample magneto meter (VSM). From the antibacterial studies, against gram positive Bacillus subtilis bacteria is most abundant bacteria in soil and indoor atmosphere, which affects the stored spintronic devices so that the devices should be made with antibacterial activity of DMS like Co doped ZnO. In this article is found that ZnO:Co nanopowders with higher Co doping level (0.07 and 0.09 wt%) exhibit good antibacterial efficiency. The magnetization curves obtained using vibrating sample magnetometer (VSM) show a sign of strong room temperature ferromagnetic behavior when the Co doping level is 0.05 wt% and a weak room temperature ferromagnetic behavior Co doping level is below 0.07 wt%, and also they found to exhibit antiferromagnetic and paramagnetic properties, when the Co doping levels are 0.07 and 0.09 wt%, respectively, to enhance and increase the special magnetic and antibacterial property for

  16. Synthesis and characterization of Mn-doped ZnO column arrays

    International Nuclear Information System (INIS)

    Yang Mei; Guo Zhixing; Qiu Kehui; Long Jianping; Yin Guangfu; Guan Denggao; Liu Sutian; Zhou Shijie

    2010-01-01

    Mn-doped ZnO column arrays were successfully synthesized by conventional sol-gel process. Effect of Mn/Zn atomic ratio and reaction time were investigated, and the morphology, tropism and optical properties of Mn-doped ZnO column arrays were characterized by SEM, XRD and photoluminescence (PL) spectroscopy. The result shows that a Mn/Zn atomic ratio of 0.1 and growth time of 12 h are the optimal condition for the preparation of densely distributed ZnO column arrays. XRD analysis shows that Mn-doped ZnO column arrays are highly c-axis oriented. As for Mn-doped ZnO column arrays, obvious increase of photoluminescence intensity is observed at the wavelength of ∼395 nm and ∼413 nm, compared to pure ZnO column arrays.

  17. Electron paramagnetic resonance in Cu-doped ZnO

    Science.gov (United States)

    Buchheit, R.; Acosta-Humánez, F.; Almanza, O.

    2016-04-01

    In this work, ZnO and Cu-doped ZnO nanoparticles (Zn1-xCuxO, x = 3%), with a calcination temperature of 500∘C were synthesized using the sol-gel method. The particles were analyzed using atomic absorption spectroscopy (AAS), X-ray diffraction (XRD) and electron paramagnetic resonance (EPR) at X-band, measurement in a temperature range from 90 K to room temperature. AAS confirmed a good correspondence between the experimental doping concentration and the theoretical value. XRD reveals the presence of ZnO phase in hexagonal wurtzite structure and a nanoparticle size for the samples synthesized. EPR spectroscopy shows the presence of point defects in both samples with g-values of g = 1.959 for shallow donors and g = 2.004 for ionized vacancies. It is important when these materials are required have been used as catalysts, as suggested that it is not necessary prepare them at higher temperature. A simulation of the Cu EPR signal using an anisotropic spin Hamiltonian was performed and showed good coincidence with the experimental spectra. It was shown that Cu2+ ions enter interstitial octahedral sites of orthorhombic symmetry in the wurtzite crystal structure. Temperature dependence of the EPR linewidth and signal intensity shows a paramagnetic behavior of the sample in the measurement range. A Néel temperature TN = 78 ± 19 K was determined.

  18. Structural and magnetic Properties of Mn, Co, Ni doped ZnO ...

    African Journals Online (AJOL)

    It is abundant, cost effective, non-toxic and also it is used in many bio-medical applications. ... The XRD of Mn-doped ZnO nanocrystals shows hexagonal structure. ... The TM doped ZnO nanocrystals shows weak ferromagnetic properties at ...

  19. Room-temperature ferromagnetic properties of Cu-doped ZnO rod ...

    Indian Academy of Sciences (India)

    We have investigated properties of the Cu-doped ZnO crystalline film synthesized by the hydrothermal method. X-ray diffraction and X-ray ... DMSs are semiconducting alloys whose lattice is made up in part of substitutional magnetic ... investigate Cu-doped ZnO system (Hou et al 2007a, b), as. Cu is a potential magnetic ion ...

  20. Explanation of ferromagnetism origin in N-doped ZnO by first ...

    Indian Academy of Sciences (India)

    Moreover, ZnO doped with. 3d TM elements has been studied widely since the model calculation by Dietl et al predicted the possibility of ferro- magnetism in ZnO with a small amount of Mn as an impurity. [4]. However, TM doping often suffers from the problems related to precipitates or secondary phase formation undesir-.

  1. Doping of ZnO nanowires using phosphorus diffusion from a spin-on doped glass source

    International Nuclear Information System (INIS)

    Bocheux, A.; Robin, I. C.; Bonaimé, J.; Hyot, B.; Feuillet, G.; Kolobov, A. V.; Fons, P.; Mitrofanov, K. V.; Tominaga, J.; Tamenori, Y.

    2014-01-01

    In this article, we report on ZnO nanowires that were phosphorus doped using a spin on dopant glass deposition and diffusion method. Photoluminescence measurements suggest that this process yields p-doped ZnO. The spatial location of P atoms was studied using x-ray near-edge absorption structure spectroscopy and it is concluded that the doping is amphoteric with P atoms located on both Zn and O sites

  2. Pure and Sn-doped ZnO films produced by pulsed laser deposition

    DEFF Research Database (Denmark)

    Holmelund, E.; Schou, Jørgen; Tougaard, S.

    2002-01-01

    A new technique, metronome doping, has been used for doping of films during pulsed laser deposition (PLD). This technique makes it possible to dope continuously during film growth with different concentrations of a dopant in one deposition sequence. Films of pure and doped ZnO have been produced...

  3. Tungsten-doped ZnO nanocomposite: Synthesis, characterization, and highly active photocatalyst toward dye photodegradation

    Energy Technology Data Exchange (ETDEWEB)

    Moafi, Hadi Fallah, E-mail: Fallah.m@guilan.ac.ir [Department of Chemistry, Faculty of Science, University of Guilan, P.O. Box 1914, Rasht (Iran, Islamic Republic of); Zanjanchi, Mohammad Ali; Shojaie, Abdollah Fallah [Department of Chemistry, Faculty of Science, University of Guilan, P.O. Box 1914, Rasht (Iran, Islamic Republic of)

    2013-05-15

    A series of W-doped ZnO nanocomposite with different W contents were synthesized by sol–gel method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma (ICP) and BET surface area measurement. The XRD results revealed that all the W-doped samples showed a hexagonal wurtzite structure. The results of EDS and XPS revealed that W was doped into ZnO structure. The particle size of doped ZnO is much smaller as compared to that of pure ZnO. The photocatalytic activity of undoped ZnO and W-doped ZnO was evaluated by the photodegradation of methylene blue in aqueous solution. The results show that the photocatalytic activity of the W-doped ZnO is much higher than that of undoped ZnO and the optimum percentage of doped W is 4 mol%. The enhanced photocatalytic activity of the W-ZnO samples may be related to the narrowing of the band gap, increase in the charge separation efficiency, particle size reduction and increase of the surface area. Highlights: ► W-doped ZnO nanocomposites were synthesized by a sol–gel method. ► The XRD results revealed that all the materials consisting of wurtzite structure. ► The sizes of the W-ZnO nanocomposite are 5–10 nm, obtained from TEM image. ► With W doping into ZnO photoinduced charge separation rate has been enhanced. ► Photocatalytic activity of the W-ZnO is much higher than that of undoped ZnO.

  4. Tungsten-doped ZnO nanocomposite: Synthesis, characterization, and highly active photocatalyst toward dye photodegradation

    International Nuclear Information System (INIS)

    Moafi, Hadi Fallah; Zanjanchi, Mohammad Ali; Shojaie, Abdollah Fallah

    2013-01-01

    A series of W-doped ZnO nanocomposite with different W contents were synthesized by sol–gel method and characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), transmission electron microscopy (TEM), diffuse reflectance spectroscopy (DRS), X-ray photoelectron spectroscopy (XPS), inductively coupled plasma (ICP) and BET surface area measurement. The XRD results revealed that all the W-doped samples showed a hexagonal wurtzite structure. The results of EDS and XPS revealed that W was doped into ZnO structure. The particle size of doped ZnO is much smaller as compared to that of pure ZnO. The photocatalytic activity of undoped ZnO and W-doped ZnO was evaluated by the photodegradation of methylene blue in aqueous solution. The results show that the photocatalytic activity of the W-doped ZnO is much higher than that of undoped ZnO and the optimum percentage of doped W is 4 mol%. The enhanced photocatalytic activity of the W-ZnO samples may be related to the narrowing of the band gap, increase in the charge separation efficiency, particle size reduction and increase of the surface area. Highlights: ► W-doped ZnO nanocomposites were synthesized by a sol–gel method. ► The XRD results revealed that all the materials consisting of wurtzite structure. ► The sizes of the W-ZnO nanocomposite are 5–10 nm, obtained from TEM image. ► With W doping into ZnO photoinduced charge separation rate has been enhanced. ► Photocatalytic activity of the W-ZnO is much higher than that of undoped ZnO

  5. Sputter deposited gallium doped ZnO for TCO applications

    Energy Technology Data Exchange (ETDEWEB)

    Dietrich, Marc; Kronenberger, Achim; Polity, Angelika; Meyer, Bruno [I. Physikalisches Institut, Justus Liebig Universitaet Giessen (Germany); Blaesing, Juergen; Krost, Alois [FNW/IEP/AHE, Otto-von-Guericke Universitaet Magdeburg (Germany)

    2010-07-01

    Transparent conducting oxides to be used for flat panel or display applications should exhibit low electrical resistivity in line with a high optical transmission in the visible spectral range. Today indium-tin-oxide is the material which meets these requirements best. However, the limited availability of indium makes it useful to search for alternatives and ZnO doped with group III elements are promising candidates. While the Al doping in high concentrations causes problems due to the formation of insulating Al-oxides, Gallium related oxides are typically n-type conducting wide band gap semiconductors. Therefore we deposited Gallium doped ZnO thin films on quartz and sapphire substrates by radio frequency magnetron sputtering with a ZnO/Ga{sub 2}O{sub 3}(3at%) composite target. The substrate temperature and the oxygen flow during the sputtering process were varied to optimise the layer properties. Introducing oxygen to the sputtering gas allowed to vary the resistivity of the films by three orders of magnitude from about 1 {omega}cm down to less than 1 m{omega}cm.

  6. Two different mechanisms on UV emission enhancement in Ag-doped ZnO thin films

    International Nuclear Information System (INIS)

    Xu, Linhua; Zheng, Gaige; Zhao, Lilong; Pei, Shixin

    2015-01-01

    Ag-doped ZnO thin films were prepared by a sol–gel method. The structural, morphological and optical properties of the samples were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–vis and photoluminescence spectra. The results show that the Ag in the ZnO thin films annealed at 500 °C for 1 h substitutes for Zn and exists in the form of Ag + ion (Ag Zn ) while the Ag in the ZnO thin films without a post-annealing mainly exists in the form of simple substance (Ag 0 ). The incorporation of Ag indeed can improve the ultraviolet emission of ZnO thin films and suppress the visible emissions at the same time. However, the mechanisms on the ultraviolet emission enhancement in the annealed and unannealed Ag-doped ZnO thin films are very different. As for the post-annealed Ag-doped ZnO thin films, the UV emission enhancement maybe mainly results from more electron–hole pairs (excitons) due to Ag-doping while for the unannealed Ag-doped ZnO thin films; the UV emission enhancement is attributed to the resonant coupling between exciton emission in ZnO and localized surface plasmon in Ag nanoparticles. - Highlights: • Ag-doped ZnO thin films have been prepared by the sol–gel method. • Ag-doping can enhance ultraviolet emission of ZnO thin films and depress the visible emissions at the same time. • There are two different mechanisms on UV emission enhancement in Ag-doped ZnO thin films. • The UV emission enhancement from the resonant coupling between excitonic emissions and localized surface plasmon in Ag nanoparticle is very attractive

  7. Structural and magnetic properties of Co-doped ZnO thin films grown by ultrasonic spray pyrolysis method

    Science.gov (United States)

    Baghdad, R.; Lemée, N.; Lamura, G.; Zeinert, A.; Hadj-Zoubir, N.; Bousmaha, M.; Bezzerrouk, M. A.; Bouyanfif, H.; Allouche, B.; Zellama, K.

    2017-04-01

    Cobalt-doped ZnO thin films with several different percentage of Co from 0 up to 15 at% were synthesized via a cheap, simple and versatile method i.e. ultrasonic spray pyrolysis at atmospheric pressure and a substrate temperature of 350 °C. The structure of the as-prepared samples was characterized by X-ray diffraction (XRD), Raman spectroscopy and FTIR. The Co-doping effect is revealed by the presence of three additional peaks around 235, 470 and 538 cm-1 respect to the Raman spectra of the unsubstituted film. Fourier transform infrared spectroscopy (FTIR) put in evidence the decrease of the bond force constant f with increasing Co-doping. By ultra-violet visible near infrared (UV-Vis-NIR) spectroscopy on Co-doped samples it was possible to show the presence of additional absorption bands at approximately 570, 620 and 660 nm suggesting that Co2+ ions do not change their oxidation when substituted to zinc and the ZnO lattice does not change its wurtzite structure as well. Finally, all our samples exhibit a paramagnetic behavior without any trace of intrinsic room temperature ferromagnetism.

  8. Effect of shallow donors on Curie–Weiss temperature of Co-doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Guo, Shuxia, E-mail: gsx0391@sina.com [Department of Physics, Jiaozuo Teachers College, Jiaozuo 454001 (China); Key Laboratory for Special Functional Materials of Ministry of Education, Henan University, Kaifeng 475004 (China); Li, Jiwu [Department of Physics, Jiaozuo Teachers College, Jiaozuo 454001 (China); Du, Zuliang [Key Laboratory for Special Functional Materials of Ministry of Education, Henan University, Kaifeng 475004 (China)

    2014-12-15

    Co-doped ZnO and Al, Co co-doped ZnO polycrystalline powders were synthesized by co-precipitation method. The magnetization curves measured at 2 K show no hysteresis neither remanence for all samples. ZnO:Co grown at low temperature has a positive Curie–Weiss temperature Θ, and ZnO:Co grown at high temperature has a negative Θ. But Al-doped ZnO:Co grown at high temperature has a positive Θ. Positive Curie–Weiss temperature Θ was considered to have relation to the presence of shallow donors in the samples. - Highlights: • Co-doped ZnO and Al, Co co-doped ZnO polycrystalline powders were synthesized. • No hysteresis is observed for all samples. • The Curie–Weiss temperature Θ changes its sign by Al doping. • Positive Θ should be related to shallow donors.

  9. Photoluminescence quenching and enhanced spin relaxation in Fe doped ZnO nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Ovhal, Manoj M.; Santhosh Kumar, A. [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India); Khullar, Prerna [School of Materials Science and Technology, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India); Kumar, Manjeet [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India); Abhyankar, A.C., E-mail: ashutoshabhyankar@gmail.com [Department of Materials Engineering, Defence Institute of Advanced Technology, Girinagar, Pune 411025 (India)

    2017-07-01

    Cost-effective ultrasonically assisted precipitation method is utilized to synthesize Zinc oxide (ZnO) nanoparticles (NPs) at room temperature and the effect of Iron (Fe) doping on structural, optical and spin relaxation properties also presented. As-synthesized pure and Fe doped ZnO NPs possess a perfect hexagonal growth habit of wurtzite zinc oxide, along the (101) direction of preference. With Fe doping, ‘c/a’ ratio and compressive lattice strain in ZnO NPs are found to reduce and increase, respectively. Raman studies demonstrate that the E{sub 1} longitudinal optical (LO) vibrational mode is very weak in pure which remarkably enhanced with Fe doping into ZnO NPs. The direct band gap energy (E{sub g}) of the ZnO NPs has been increased from 3.02 eV to 3.11 eV with Fe doping. A slight red-shift observed with strong green emission band, in photoluminescence spectra, is strongly quenched in 6 wt.% Fe doped ZnO NPs. The field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM) reveals spherical shape of ZnO NPs with 60–70 nm, which reduces substantially on Fe doping. The energy dispersive X-ray spectrum and elemental mapping confirms the homogeneous distribution of Fe in ZnO NPs. Moreover, the specific relaxation rate (R{sub 2sp} = 1/T{sub 2}) has been measured using Carr-Purcell-Meiboom-Gill (CPMG) method and found to be maximum in 6 wt.% Fe doped ZnO NPs. Further, the correlation of structural, optical and dynamic properties is proposed. - Highlights: • Pure ZnO and Fe doped ZnO NPs were successfully prepared by cost effective ultrasonically assisted precipitation method. • The optical band gap of ZnO has been enhanced form 3.02–3.11 eV with Fe doping. • PL quenching behaviour has been observed with Fe{sup 3+} ions substitution in ZnO lattice. • Specific relaxation rate (R{sub 2sp} = 1/T{sub 2}) has been varied with Fe doping and found to be maximum in 6 wt.% Fe doped ZnO NPs.

  10. Effect of Ga doping and point defect on magnetism of ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Qingyu [College of Science, Inner Mongolia University of Technology, 010051 Hohhot (China); Zhao, Chunwang, E-mail: cwzhao@shmtu.edu.cn [College of Arts and Sciences, Shanghai Maritime University, 201306 Shanghai (China); Jia, Xiaofang; Qu, Lingfeng [College of Science, Inner Mongolia University of Technology, 010051 Hohhot (China)

    2017-02-01

    The combined influence mechanism of Ga doping and Zn vacancy or O vacancy on magnetism of ZnO is studied using the first-principle calculation. The coexistence of Ga doping and Zn vacancy can achieve a Curie temperature higher than room temperature and the Ga doped ZnO system is a p-type diluted degenerate semiconductor with metalized ferromagnetism. The magnetism of the doping system of Ga doping and Zn vacancy is mainly contributed by double-exchange interaction through the holes of Zn vacancy taking carrier as medium. However, the system of Ga doping and O vacancy is non-magnetic. In the coexistence of Ga doping and Zn vacancy or O vacancy, a close relative distance between doping and vacancy will reduce the formation energy of the doping system but increase the easiness of doping and vacancy, as well as enhance the stability of the doping system.

  11. Recent progress on doped ZnO nanostructures for visible-light photocatalysis

    International Nuclear Information System (INIS)

    Samadi, Morasae; Zirak, Mohammad; Naseri, Amene; Khorashadizade, Elham; Moshfegh, Alireza Z.

    2016-01-01

    Global environmental pollution and energy supply demand have been regarded as important concerns in recent years. Metal oxide semiconductor photocatalysts is a promising approach to apply environmental remediation as well as fuel generation from water splitting and carbon dioxide reduction. ZnO nanostructures have been shown promising photocatalytic activities due to their non-toxic, inexpensive, and highly efficient nature. However, its wide band gap hinders photo-excitation for practical photocatalytic applications under solar light as an abundant, clean and safe energy source. To overcome this barrier, many strategies have been developed in the last decade to apply ZnO nanostructured photocatalysts under visible light. In this review, we have classified different approaches to activate ZnO as a photocatalyst in visible-light spectrum. Utilization of various nonmetals, transition metals and rare-earth metals for doping in ZnO crystal lattice to create visible-light-responsive doped ZnO photocatalysts is discussed. Generation of localized energy levels within the gap in doped ZnO nanostructures has played an important role in effective photocatalytic reaction under visible-light irradiation. The effect of dopant type, ionic size and its concentration on the crystal structure, electronic property and morphology of doped ZnO with a narrower band gap is reviewed systematically. Finally, a comparative study is performed to evaluate two classes of metals and nonmetals as useful dopants for ZnO nanostructured photocatalysts under visible light. - Highlights: • Metals and nonmetals used as a dopant to shift ZnO band gap toward visible-light. • Modification of electronic structure played a crucial role in doped ZnO activity. • Correlation between dopant's characteristics and ZnO visible activity was reviewed. • Photo-degradation of doped ZnO was studied and compared for different dopants.

  12. Recent progress on doped ZnO nanostructures for visible-light photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Samadi, Morasae; Zirak, Mohammad [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Naseri, Amene [Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-8639, Tehran (Iran, Islamic Republic of); Khorashadizade, Elham [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Moshfegh, Alireza Z., E-mail: moshfegh@sharif.edu [Department of Physics, Sharif University of Technology, P.O. Box 11555-9161, Tehran (Iran, Islamic Republic of); Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-8639, Tehran (Iran, Islamic Republic of)

    2016-04-30

    Global environmental pollution and energy supply demand have been regarded as important concerns in recent years. Metal oxide semiconductor photocatalysts is a promising approach to apply environmental remediation as well as fuel generation from water splitting and carbon dioxide reduction. ZnO nanostructures have been shown promising photocatalytic activities due to their non-toxic, inexpensive, and highly efficient nature. However, its wide band gap hinders photo-excitation for practical photocatalytic applications under solar light as an abundant, clean and safe energy source. To overcome this barrier, many strategies have been developed in the last decade to apply ZnO nanostructured photocatalysts under visible light. In this review, we have classified different approaches to activate ZnO as a photocatalyst in visible-light spectrum. Utilization of various nonmetals, transition metals and rare-earth metals for doping in ZnO crystal lattice to create visible-light-responsive doped ZnO photocatalysts is discussed. Generation of localized energy levels within the gap in doped ZnO nanostructures has played an important role in effective photocatalytic reaction under visible-light irradiation. The effect of dopant type, ionic size and its concentration on the crystal structure, electronic property and morphology of doped ZnO with a narrower band gap is reviewed systematically. Finally, a comparative study is performed to evaluate two classes of metals and nonmetals as useful dopants for ZnO nanostructured photocatalysts under visible light. - Highlights: • Metals and nonmetals used as a dopant to shift ZnO band gap toward visible-light. • Modification of electronic structure played a crucial role in doped ZnO activity. • Correlation between dopant's characteristics and ZnO visible activity was reviewed. • Photo-degradation of doped ZnO was studied and compared for different dopants.

  13. Synthesis, characterization and electrochemical behavior of Sb-doped ZnO microsphere film

    Energy Technology Data Exchange (ETDEWEB)

    Li, Qian [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); Cheng, Kui, E-mail: chengkui@zju.edu.cn [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); Weng, Wenjian, E-mail: wengwj@zju.edu.cn [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China); The Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai, 200050 (China); Du, Piyi; Han, Gaorong [Department of Materials Science and Engineering, State Key Laboratory of Silicon Materials, Cyrus Tang Center for Sensor Materials and Applications, Zhejiang University, Hangzhou, 310027 (China)

    2013-10-01

    Sb-doped ZnO microsphere film was fabricated by a carboxylate ion assisted hydrothermal route coupled with a post-calcination process. The structure, chemical composition and optical band gap of the Sb-doped ZnO microsphere film were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, inductively couple plasma optical emission spectroscopy and UV–visible spectrophotometry, and compared with the un-doped ZnO microsphere film. The results suggest that the formation of zinc–antimony tartrate complex species during hydrothermal growth is the key to realize Sb-doped ZnO microstructures, and the present hydrothermal method with post-calcination is an effective way to dope Sb into ZnO. Furthermore, the Sb-doped ZnO microsphere film based electrochemical biosensor exhibits a good sensing performance for the detection of hydrogen peroxide, with a sensitivity of 271 μA mM{sup −1} cm{sup −2} which is more than three times higher than that of the un-doped ZnO biosensor. - Highlights: • Sb-doped ZnO microsphere (SZM) films were grown by hydrothermal deposition. • Carboxylate ions were used to form complex during hydrothermal growth. • The formation of Zn–Sb tartrate complex is the key to realize SZM. • The biosensors based on SZM film are feasible and sensitive to detect H{sub 2}O{sub 2}. • The Sb doping could improve the electrochemical property of ZnO.

  14. Potassium acceptor doping of ZnO crystals

    Directory of Open Access Journals (Sweden)

    Narendra S. Parmar

    2015-05-01

    Full Text Available ZnO bulk single crystals were doped with potassium by diffusion at 950°C. Positron annihilation spectroscopy confirms the filling of zinc vacancies and a different trapping center for positrons. Secondary ion mass spectroscopy measurements show the diffusion of potassium up to 10 μm with concentration ∼1 × 1016 cm−3. IR measurements show a local vibrational mode (LVM at 3226 cm−1, at a temperature of 9 K, in a potassium doped sample that was subsequently hydrogenated. The LVM is attributed to an O–H bond-stretching mode adjacent to a potassium acceptor. When deuterium substitutes for hydrogen, a peak is observed at 2378 cm−1. The O-H peak is much broader than the O-D peak, perhaps due to an unusually low vibrational lifetime. The isotopic frequency ratio is similar to values found in other hydrogen complexes. Potassium doping increases the resistivity up to 3 orders of magnitude at room temperature. The doped sample has a donor level at 0.30 eV.

  15. Potassium acceptor doping of ZnO crystals

    Science.gov (United States)

    Parmar, Narendra S.; Corolewski, Caleb D.; McCluskey, Matthew D.; Lynn, K. G.

    2015-05-01

    ZnO bulk single crystals were doped with potassium by diffusion at 950°C. Positron annihilation spectroscopy confirms the filling of zinc vacancies and a different trapping center for positrons. Secondary ion mass spectroscopy measurements show the diffusion of potassium up to 10 μm with concentration ˜1 × 1016 cm-3. IR measurements show a local vibrational mode (LVM) at 3226 cm-1, at a temperature of 9 K, in a potassium doped sample that was subsequently hydrogenated. The LVM is attributed to an O-H bond-stretching mode adjacent to a potassium acceptor. When deuterium substitutes for hydrogen, a peak is observed at 2378 cm-1. The O-H peak is much broader than the O-D peak, perhaps due to an unusually low vibrational lifetime. The isotopic frequency ratio is similar to values found in other hydrogen complexes. Potassium doping increases the resistivity up to 3 orders of magnitude at room temperature. The doped sample has a donor level at 0.30 eV.

  16. Potassium acceptor doping of ZnO crystals

    Energy Technology Data Exchange (ETDEWEB)

    Parmar, Narendra S., E-mail: nparmar@wsu.edu; Lynn, K. G. [Center for Materials Research, Washington State University, Pullman, Washington 99164-2711 (United States); Department of Physics and Astronomy, Washington State University, Pullman, Washington 99164-2814 (United States); Corolewski, Caleb D.; McCluskey, Matthew D. [Department of Physics and Astronomy, Washington State University, Pullman, Washington 99164-2814 (United States)

    2015-05-15

    ZnO bulk single crystals were doped with potassium by diffusion at 950°C. Positron annihilation spectroscopy confirms the filling of zinc vacancies and a different trapping center for positrons. Secondary ion mass spectroscopy measurements show the diffusion of potassium up to 10 μm with concentration ∼1 × 10{sup 16} cm{sup −3}. IR measurements show a local vibrational mode (LVM) at 3226 cm{sup −1}, at a temperature of 9 K, in a potassium doped sample that was subsequently hydrogenated. The LVM is attributed to an O–H bond-stretching mode adjacent to a potassium acceptor. When deuterium substitutes for hydrogen, a peak is observed at 2378 cm{sup −1}. The O-H peak is much broader than the O-D peak, perhaps due to an unusually low vibrational lifetime. The isotopic frequency ratio is similar to values found in other hydrogen complexes. Potassium doping increases the resistivity up to 3 orders of magnitude at room temperature. The doped sample has a donor level at 0.30 eV.

  17. Properties of antimony doped ZnO thin films deposited by spray pyrolysis technique

    Energy Technology Data Exchange (ETDEWEB)

    Sadananda Kumar, N., E-mail: sadanthara@gmail.com; Bangera, Kasturi V.; Shivakumar, G. K. [National Institute of Technology Karnataka, Surathkal, Thin Films Laboratory, Department of Physics (India)

    2015-07-15

    Antimony (Sb) doped zinc oxide (ZnO) thin films were deposited on the glass substrate at 450°C using spray pyrolysis technique. Effect of Sb doping on surface morphology structural, optical and electrical properties were studied. X-ray diffraction (XRD) analysis showed that both the undoped and doped ZnO thin films are polycrystalline in nature with (101) preferred orientation. SEM analysis showed a change in surface morphology of Sb doped ZnO thin films. Doping results in a marked increase in conductivity without affecting the transmittance of the films. ZnO films prepared with 3 at % Sb shows the lowest resistivity of 0.185 Ohm cm with a Hall mobility of 54.05 cm{sup 2} V{sup –1} s{sup –1}, and a hole concentration of 6.25 × 10{sup 17} cm{sup –3}.

  18. Atomic layer deposition of Al-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Tynell, Tommi; Yamauchi, Hisao; Karppinen, Maarit; Okazaki, Ryuji; Terasaki, Ichiro [Department of Chemistry, Aalto University, FI-00076 Aalto (Finland); Department of Physics, Nagoya University, Nagoya 464-8602 (Japan)

    2013-01-15

    Atomic layer deposition has been used to fabricate thin films of aluminum-doped ZnO by depositing interspersed layers of ZnO and Al{sub 2}O{sub 3} on borosilicate glass substrates. The growth characteristics of the films have been investigated through x-ray diffraction, x-ray reflection, and x-ray fluorescence measurements, and the efficacy of the Al doping has been evaluated through optical reflectivity and Seebeck coefficient measurements. The Al doping is found to affect the carrier density of ZnO up to a nominal Al dopant content of 5 at. %. At nominal Al doping levels of 10 at. % and higher, the structure of the films is found to be strongly affected by the Al{sub 2}O{sub 3} phase and no further carrier doping of ZnO is observed.

  19. Structural, optical and magnetic characterization of Ru doped ZnO nanorods

    International Nuclear Information System (INIS)

    Kumar, Sanjeev; Kaur, Palvinder; Chen, C.L.; Thangavel, R.; Dong, C.L.; Ho, Y.K.; Lee, J.F.; Chan, T.S.; Chen, T.K.; Mok, B.H.; Rao, S.M.; Wu, M.K.

    2014-01-01

    Graphical abstract: Ruthenium (Ru = 0%, 1% and 2%) doped nano-crystalline zinc oxide (ZnO) nanorods were synthesized by using well-known sol–gel technique. X-ray diffraction (XRD) results show that Ru (0%, 1% and 2%) doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). Williamson and Hall plot reveal that in the nanoscale dimensions, incorporation of Ru induced the tensile strain in ZnO host matrix. Photoluminescence (PL) and Raman studies of Ru doped ZnO nanorods show the formation of singly ionized oxygen vacancies which may account for the observed room temperature ferromagnetism (RTFM) in 2% Ru doped ZnO. X-ray absorption spectroscopy (XAS) reveals that Ru replace the Zn atoms in the host lattice and maintain the crystal symmetry with slightly lattice distortion. Highlights: • Ru doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). • PL and Raman studies show the formation of singly ionized oxygen vacancies in 2% Ru doped ZnO. • XAS reveals that Ru replace the Zn atoms in the host lattice with slightly lattice distortion. • Doping of Ru in ZnO nanostructures gives rise to RTFM ordering. -- Abstract: Ruthenium (Ru = 0%, 1% and 2%) doped nano-crystalline zinc oxide (ZnO) nanorods were synthesized by using well-known sol–gel technique. X-ray diffraction (XRD) results show that Ru (0%, 1% and 2%) doped ZnO nanorods crystallized in the wurtzite structure having space group C 3v (P6 3 mc). Williamson and Hall plot reveal that in the nanoscale dimensions, incorporation of Ru induced the tensile strain in ZnO host matrix. Photoluminescence (PL) and Raman studies of Ru doped ZnO nanorods show the formation of singly ionized oxygen vacancies which may account for the observed room temperature ferromagnetism (RTFM) in 2% Ru doped ZnO. X-ray absorption spectroscopy (XAS) reveals that Ru replace the Zn atoms in the host lattice and maintain the crystal symmetry with slightly lattice

  20. Mn{sup 2+} ions distribution in doped sol–gel deposited ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Stefan, Mariana, E-mail: mstefan@infim.ro [National Institute of Materials Physics, P.O. Box MG-7, 077125 Magurele (Romania); Ghica, Daniela; Nistor, Sergiu V.; Maraloiu, Adrian V. [National Institute of Materials Physics, P.O. Box MG-7, 077125 Magurele (Romania); Plugaru, Rodica [National Institute for R & D in Microtechnologies (IMT), Erou Iancu Nicolae Str. 126A, 077190 Bucharest (Romania)

    2017-02-28

    Highlights: • Several Mn{sup 2+} centers observed by EPR in sol–gel ZnO films. • Mn{sup 2+} ions localized at Zn{sup 2+} sites in ZnO grains and disordered ZnO phase. • Sixfold coordinated Mn{sup 2+} ions localized in inter-grain region. • Aggregated Mn in insular-like regions between ZnO grains in the ZnO:5%Mn film. • Aggregated Mn phase presence and distribution observed by EPR and EDX-STEM. - Abstract: The localization and distribution of the Mn{sup 2+} ions in two sol–gel deposited ZnO films doped with different manganese concentrations were investigated by electron paramagnetic resonance spectroscopy and analytical transmission electron microscopy. In the lightly doped sample the Mn{sup 2+} ions are mainly localized substitutionally at isolated tetrahedrally coordinated Zn{sup 2+} sites in both crystalline ZnO nanograins (34%) and surrounding disordered ZnO (52%). In the highly doped ZnO film, a much smaller proportion of manganese substitutes Zn{sup 2+} in the crystalline and disordered ZnO (10%). The main amount (85%) of manganese aggregates in a secondary phase as an insular-like distribution between the ZnO nanograins. The remaining Mn{sup 2+} ions (14% and 5% at low and high doping levels, respectively) are localized at isolated, six-fold coordinated sites, very likely in the disordered intergrain region. Annealing at 600 °C induced changes in the Mn{sup 2+} ions distribution, reflecting the increase of the ZnO crystallization degree, better observed in the lightly doped sample.

  1. Electronic Structure and Optical Properties of Co and Fe doped ZnO

    Directory of Open Access Journals (Sweden)

    Li Chunping

    2016-01-01

    Full Text Available First-principle ultrasoft pseudo potential approach of the plane wave based on density functional theory has been used for studying the electronic characterization and optical properties of ZnO and Fe, Co doped ZnO. The results show that the doping impurities change the lattice parameters a little, but bring more changes in the electronic structures. The band gaps are broadened by doping. And the Fermi level accesses to the conduction band which will lead the system to show the character of metallic properties. The dielectric function and absorption peaks are identified and the changes compared to pure ZnO are analyzed in detail.

  2. Y-Doped ZnO Nanorods by Hydrothermal Method and Their Acetone Gas Sensitivity

    Directory of Open Access Journals (Sweden)

    Peng Yu

    2013-01-01

    Full Text Available Pure and yttrium- (Y- doped (1 at%, 3 at%, and 7 at% ZnO nanorods were synthesized using a hydrothermal process. The crystallography and microstructure of the synthesized samples were characterized by X-ray diffraction (XRD, scanning electron microscopy (SEM, and energy dispersive X-ray spectroscopy (EDX. Comparing with pure ZnO nanorods, Y-doped ZnO exhibited improved acetone sensing properties. The response of 1 at% Y-doped ZnO nanorods to 100 ppm acetone is larger than that of pure ZnO nanorods. The response and recovery times of 1 at% Y-doped ZnO nanorods to 100 ppm acetone are about 30 s and 90 s, respectively. The gas sensor based on Y-doped ZnO nanorods showed good selectivity to acetone in the interfere gases of ammonia, benzene, formaldehyde, toluene, and methanol. The formation mechanism of the ZnO nanorods was briefly analyzed.

  3. Improving the conductance of ZnO thin film doping with Ti by using a cathodic vacuum arc deposition process

    International Nuclear Information System (INIS)

    Wu, Chun-Sen; Lin, Bor-Tsuen; Jean, Ming-Der

    2011-01-01

    The Ti-doped ZnO films compared to un-doped ZnO films were deposited onto Corning XG glass substrates by using a cathodic vacuum arc deposition process in a mixture of oxygen and argon gases. The structural, electrical and optical properties of un-doped and Ti-doped ZnO films have been investigated. When the Ti target power is about 750 W, the incorporation of titanium atoms into zinc oxide films is obviously effective. Additionally, the resistivity of un-doped ZnO films is high and reduces to a value of 3.48 x 10 -3 Ω-cm when Ti is incorporated. The Ti doped in the ZnO films gave rise to the improvement of the conductivity of the films obviously. The Ti-doped ZnO films have > 85% transmittance in a range of 400-700 nm.

  4. Electronic structure, magnetic and structural properties of Ni doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Kumar, Shalendra; Vats, Prashant; Gautam, S.; Gupta, V.P.; Verma, K.D.; Chae, K.H.; Hashim, Mohd; Choi, H.K.

    2014-01-01

    Highlights: • XRD, and HR-TEM results show the single phase nature of Ni doped ZnO nanoparticles. • dc magnetization results indicate the RT-FM in Ni doped ZnO nanoparticles. • Ni L 3,2 edge NEXAFS spectra infer that Ni ions are in +2 valence state. • O K edge NEXAFS spectra show that O vacancy increases with Ni doping in ZnO. - Abstract: We report structural, magnetic and electronic structural properties of Ni doped ZnO nanoparticles prepared by auto-combustion method. The prepared nanoparticles were characterized by using X-ray diffraction (XRD), high resolution transmission electron microscopy (HR-TEM), near edge X-ray absorption fine structure (NEXAFS) spectroscopy, and dc magnetization measurements. The XRD and HR-TEM results indicate that Ni doped ZnO nanoparticles have single phase nature with wurtzite lattice and exclude the presence of secondary phase. NEXAFS measurements performed at Ni L 3,2 -edges indicates that Ni ions are in +2 valence state and exclude the presence of Ni metal clusters. O K-edge NEXAFS spectra indicate an increase in oxygen vacancies with Ni-doping, while Zn L 3,2 -edge show the absence of Zn-vacancies. The magnetization measurements performed at room temperature shows that pure and Ni doped ZnO exhibits ferromagnetic behavior

  5. Enhanced room temperature ferromagnetism in electrodeposited Co-doped ZnO nanostructured thin films by controlling the oxygen vacancy defects

    Energy Technology Data Exchange (ETDEWEB)

    Simimol, A. [Nanomaterials Research Lab, Surface Engineering Division, CSIR-National Aerospace Laboratories, Post Bag No. 1779, Bangalore 560017 (India); Department of Physics, National Institute of Technology Calicut, Calicut 673601 (India); Anappara, Aji A. [Department of Physics, National Institute of Technology Calicut, Calicut 673601 (India); Greulich-Weber, S. [Department of Physics, Nanophotonic Materials, Faculty of Science, University of Paderborn, 33095 Paderborn (Germany); Chowdhury, Prasanta [Nanomaterials Research Lab, Surface Engineering Division, CSIR-National Aerospace Laboratories, Post Bag No. 1779, Bangalore 560017 (India); Barshilia, Harish C., E-mail: harish@nal.res.in

    2015-06-07

    We report the growth of un-doped and cobalt doped ZnO nanostructures fabricated on FTO coated glass substrates using electrodeposition method. A detailed study on the effects of dopant concentration on morphology, structural, optical, and magnetic properties of the ZnO nanostructures has been carried out systematically by varying the Co concentration (c.{sub Co}) from 0.01 to 1 mM. For c.{sub Co }≤ 0.2 mM, h-wurtzite phase with no secondary phases of Co were present in the ZnO nanostructures. For c.{sub Co} ≤ 0.2 mM, the photoluminescence spectra exhibited a decrease in the intensity of ultraviolet emission as well as band-gap narrowing with an increase in dopant concentration. All the doped samples displayed a broad emission in the visible range and its intensity increased with an increase in Co concentration. It was found that the defect centers such as oxygen vacancies and zinc interstitials were the source of the visible emission. The X-ray photoelectron spectroscopy studies revealed, Co was primarily in the divalent state, replacing the Zn ion inside the tetrahedral crystal site of ZnO without forming any cluster or secondary phases of Co. The un-doped ZnO nanorods exhibited diamagnetic behavior and it remained up to a c.{sub Co} of 0.05 mM, while for c.{sub Co }> 0.05 mM, the ZnO nanostructures exhibited ferromagnetic behavior at room temperature. The coercivity increased to 695 G for 0.2 mM Co-doped sample and then it decreased for c.{sub Co }> 0.2 mM. Our results illustrate that up to a threshold concentration of 0.2 mM, the strong ferromagnetism is due to the oxygen vacancy defects centers, which exist in the Co-doped ZnO nanostructures. The origin of strong ferromagnetism at room temperature in Co-doped ZnO nanostructures is attributed to the s-d exchange interaction between the localized spin moments resulting from the oxygen vacancies and d electrons of Co{sup 2+} ions. Our findings provide a new insight for tuning the

  6. Oxygen vacancy-induced ferromagnetism in un-doped ZnO thin films

    Science.gov (United States)

    Zhan, Peng; Wang, Weipeng; Liu, Can; Hu, Yang; Li, Zhengcao; Zhang, Zhengjun; Zhang, Peng; Wang, Baoyi; Cao, Xingzhong

    2012-02-01

    ZnO films became ferromagnetic when defects were introduced by thermal-annealing in flowing argon. This ferromagnetism, as shown by the photoluminescence measurement and positron annihilation analysis, was induced by the singly occupied oxygen vacancy with a saturated magnetization dependent positively on the amount of this vacancy. This study clarified the origin of the ferromagnetism of un-doped ZnO thin films and provides possibly an alternative way to prepare ferromagnetic ZnO films.

  7. Structural and Optical Properties of Eu Doped ZnO Nanorods prepared by Pulsed Laser Deposition

    KAUST Repository

    Alarawi, Abeer

    2014-01-01

    Nano structured wide band gap semiconductors have attracted attention of many researchers due to their potential electronic and optoelectronic applications. In this thesis, we report successful synthesis of well aligned Eu doped ZnO nano

  8. Al-Doped ZnO Monolayer as a Promising Transparent Electrode Material: A First-Principles Study

    Directory of Open Access Journals (Sweden)

    Mingyang Wu

    2017-03-01

    Full Text Available Al-doped ZnO has attracted much attention as a transparent electrode. The graphene-like ZnO monolayer as a two-dimensional nanostructure material shows exceptional properties compared to bulk ZnO. Here, through first-principle calculations, we found that the transparency in the visible light region of Al-doped ZnO monolayer is significantly enhanced compared to the bulk counterpart. In particular, the 12.5 at% Al-doped ZnO monolayer exhibits the highest visible transmittance of above 99%. Further, the electrical conductivity of the ZnO monolayer is enhanced as a result of Al doping, which also occurred in the bulk system. Our results suggest that Al-doped ZnO monolayer is a promising transparent conducting electrode for nanoscale optoelectronic device applications.

  9. Optical and structural properties of individual Co-doped ZnO microwires

    Science.gov (United States)

    Kolomys, O. F.; Strelchuk, V. V.; Rarata, S. V.; Hayn, R.; Savoyant, A.; Giovannelli, F.; Delorme, F.; Tkach, V.

    2018-06-01

    The Co-doped ZnO microwires (MWs) were grown using the optical furnace method. We used Scanning electron microscopy (SEM), polarized micro-Raman spectroscopy, photoluminescence (PL) and optical absorption spectroscopy to systematic investigation of the optical and structural properties of Co-doped ZnO MWs. The SEM analysis reveals that Co-doped ZnO MWs has hexagonal facets and cavity inside. The EDS results confirmed the presence and non-uniform distribution of Co impurities in the samples. Co doping of ZnO MWs leads to the decreased intensity, drastically broadening and high-energy shift of the NBE PL band. The red emission band at 1.85 eV originates from 2E(2G) → 4A2 (4F) intra-3d-transition of Co2+ in the ZnO lattice has been observed. The intense structured absorption bands within the near infrared ranges 3800-4800 and 5500-9000 cm-1 are caused by electronic spin-allowed transitions 4T2(F) ← 4A2(F) and 4T1(F) ← 4A2(F) of the tetrahedrally coordinated Co2+ (3 d7) ions substituting Zn2+ ions in Co-doped ZnO MWs. Micro-Raman studies of Co doped ZnO MWs show doping/disorder induced additional modes as compared to the undoped sample. The resonant enhancement of the additional local Co-related A1-symmetry Raman mode is observed in the parallel polarization geometry y(z , z) ybar . For the Co doped ZnO MWs, the enhancement of the additional Co-related local vibration mode with an increase in the excitation photon energy is also observed in the Raman spectra.

  10. Significant enhancement of room temperature ferromagnetism in surfactant coated polycrystalline Mn doped ZnO particles

    Energy Technology Data Exchange (ETDEWEB)

    Jayakumar, O.D. [Chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Gopalakrishnan, I.K. [Chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India)]. E-mail: ikgopal@barc.gov.in; Sudakar, C. [Department of Physics and Astronomy, Wayne State University, Detroit, MI 48201 (United States); Kadam, R.M. [Radiochemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Kulshreshtha, S.K. [Chemistry Division, Bhabha Atomic Research Centre, Mumbai 400085 (India)

    2007-07-12

    We report a surfactant assisted synthesis of Mn doped ZnO polycrystalline samples showing robust room temperature ferromagnetism as characterized by X-ray diffraction analysis, transmission electron microscopy, electron paramagnetic resonance and DC magnetization measurements. This surfactant assisted synthesis method, developed by us, is found to be highly reproducible. Further, it can also be extended to the synthesis of other transition metal doped ZnO.

  11. Nitrogen induced ferromagnetism in Cobalt doped BaTiO3

    Directory of Open Access Journals (Sweden)

    Chandrima Mitra

    2012-09-01

    Full Text Available The electronic structure and magnetism of Cobalt doped BaTiO3 (BaTi1−xCoxO3 is investigated. Substitutional Nitrogen on an Oxygen site is found to play an important role in inducing net magnetic moments in the system. The presence of a Nitrogen atom as nearest neighbour to a Cobalt atom is crucial in producing spin splitting of both the Nitrogen and Cobalt states thereby introducing a net local magnetic moment. The introduction of Nitrogen is further found to enhance ferromagnetic interactions between Cobalt atoms.

  12. Structural, optical, and LED characteristics of ZnO and Al doped ZnO thin films

    Science.gov (United States)

    Sandeep, K. M.; Bhat, Shreesha; Dharmaprakash, S. M.

    2017-05-01

    ZnO (pristine) and Al doped ZnO (AZO) films were prepared using sol-gel spin coating method. The XRD analysis showed the enhanced compressive stress in AZO film. The presence of extended states below the conduction band edge in AZO accounts for the redshift in optical bandgap. The PL spectra of AZO showed significant blue emission due to the carrier recombination from defect states. The TRPL curves showed the dominant DAP recombination in ZnO film, whereas defect related recombination in Al doped ZnO film. Color parameters viz: the dominant wavelength, color coordinates (x,y), color purity, luminous efficiency and correlated color temperature (CCT) of ZnO and AZO films are calculated using 1931 (CIE) diagram. Further, a strong blue emission with color purity more than 96% is observed in both the films. The enhanced blue emission in AZO significantly increased the luminous efficiency (22.8%) compared to ZnO film (10.8%). The prepared films may be used as blue phosphors in white light generation.

  13. Defect mediated magnetic interaction and high Tc ferromagnetism in Co doped ZnO nanoparticles.

    Science.gov (United States)

    Pal, Bappaditya; Giri, P K

    2011-10-01

    Structural, optical and magnetic studies have been carried out for the Co-doped ZnO nanoparticles (NPs). ZnO NPs are doped with 3% and 5% Co using ball milling and ferromagnetism (FM) is studied at room temperature and above. A high Curie temperature (Tc) has been observed from the Co doped ZnO NPs. X-ray diffraction and high resolution transmission electron microscopy analysis confirm the absence of metallic Co clusters or any other phase different from würtzite-type ZnO. UV-visible absorption and photoluminescence studies on the doped samples show change in band structure and oxygen vacancy defects, respectively. Micro-Raman studies of doped samples shows defect related additional strong bands at 547 and 574 cm(-1) confirming the presence of oxygen vacancy defects in ZnO lattice. The field dependence of magnetization (M-H curve) measured at room temperature exhibits the clear M-H loop with saturation magnetization and coercive field of the order of 4-6 emu/g and 260 G, respectively. Temperature dependence of magnetization measurement shows sharp ferromagnetic to paramagnetic transition with a high Tc = 791 K for 3% Co doped ZnO NPs. Ferromagnetic ordering is interpreted in terms of overlapping of polarons mediated through oxygen vacancy defects based on the bound magnetic polaron (BMP) model. We show that the observed FM data fits well with the BMP model involving localised carriers and magnetic cations.

  14. Piezoelectricity and charge trapping in ZnO and Co-doped ZnO thin films

    Directory of Open Access Journals (Sweden)

    Domenico D’Agostino

    2017-05-01

    Full Text Available Piezoelectricity and charge storage of undoped and Co-doped ZnO thin films were investigated by means of PiezoResponse Force Microscopy and Kelvin Probe Force Microscopy. We found that Co-doped ZnO exhibits a large piezoelectric response, with the mean value of piezoelectric matrix element d33 slightly lower than in the undoped sample. Moreover, we demonstrate that Co-doping affects the homogeneity of the piezoelectric response, probably as a consequence of the lower crystalline degree exhibited by the doped samples. We also investigate the nature of the interface between a metal electrode, made up of the PtIr AFM tip, and the films as well as the phenomenon of charge storage. We find Schottky contacts in both cases, with a barrier value higher in PtIr/ZnO than in PtIr/Co-doped ZnO, indicating an increase in the work function due to Co-doping.

  15. Rapid synthesis of Co, Ni co-doped ZnO nanoparticles: Optical and electrochemical properties

    Energy Technology Data Exchange (ETDEWEB)

    Romeiro, Fernanda C.; Marinho, Juliane Z.; Lemos, Samantha C.S. [Instituto de Química, Universidade Federal de Uberlândia, 38400-902 Uberlândia, MG (Brazil); Moura, Ana P. de [LIEC, Instituto de Química, Universidade Estadual Paulista, 14800-900 Araraquara, SP (Brazil); Freire, Poliana G. [Instituto de Química, Universidade Federal de Uberlândia, 38400-902 Uberlândia, MG (Brazil); Silva, Luis F. da; Longo, Elson [LIEC, Instituto de Química, Universidade Estadual Paulista, 14800-900 Araraquara, SP (Brazil); Munoz, Rodrigo A.A. [Instituto de Química, Universidade Federal de Uberlândia, 38400-902 Uberlândia, MG (Brazil); Lima, Renata C., E-mail: rclima@iqufu.ufu.br [Instituto de Química, Universidade Federal de Uberlândia, 38400-902 Uberlândia, MG (Brazil)

    2015-10-15

    We report for the first time a rapid preparation of Zn{sub 1−2x}Co{sub x}Ni{sub x}O nanoparticles via a versatile and environmentally friendly route, microwave-assisted hydrothermal (MAH) method. The Co, Ni co-doped ZnO nanoparticles present an effect on photoluminescence and electrochemical properties, exhibiting excellent electrocatalytic performance compared to undoped ZnO sample. Photoluminescence spectroscopy measurements indicated the reduction of the green–orange–red visible emission region after adding Co and Ni ions, revealing the formation of alternative pathways for the generated recombination. The presence of these metallic ions into ZnO creates different defects, contributing to a local structural disorder, as revealed by Raman spectra. Electrochemical experiments revealed that the electrocatalytic oxidation of dopamine on ZnO attached to multi-walled carbon nanotubes improved significantly in the Co, Ni co-doped ZnO samples when compared to pure ZnO. - Graphical abstract: Rapid synthesis of Co, Ni co-doped ZnO nanoparticles: optical and electrochemical properties. Co, Ni co-doped ZnO hexagonal nanoparticles with optical and electrocatalytic properties were successfully prepared for the first time using a microwave hydrothermal method at mild conditions. - Highlights: • Co{sup 2+} and Ni{sup 2+} into ZnO lattice obtained a mild and environmentally friendly process. • The heating method strongly influences in the growth and shape of the particles. • Short-range defects generated by the ions insertion affects the photoluminescence. • Doped ZnO nanoparticles improve the electrocatalytic properties of pure oxide.

  16. Structural, magnetic and electronic structure properties of Co doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Kumar, Shalendra; Song, T.K.; Gautam, Sanjeev; Chae, K.H.; Kim, S.S.; Jang, K.W.

    2015-01-01

    Highlights: • XRD and HR-TEM results show the single phase nature of Co doped ZnO nanoparticles. • XMCD and dc magnetization results indicate the RT-FM in Co doped ZnO nanoparticles. • Co L 3,2 NEXAFS spectra infer that Co ions are in 2+ valence state. • O K edge NEXAFS spectra show that O vacancy increases with Co doping in ZnO. - Abstract: We reported structural, magnetic and electronic structure studies of Co doped ZnO nanoparticles. Doping of Co ions in ZnO host matrix has been studied and confirmed using various methods; such as X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersed X-ray (EDX), high resolution transmission electron microscopy (HR-TEM), Fourier transform infrared spectroscopy (FT-IR), near edge X-ray absorption fine structure (NEXAFS) spectroscopy, magnetic hysteresis loop measurements and X-ray magnetic circular dichroism (XMCD). From the XRD and HR-TEM results, it is observed that Co doped ZnO nanoparticles have single phase nature with wurtzite structure and exclude the possibility of secondary phase formation. FE-SEM and TEM micrographs show that pure and Co doped nanoparticles are nearly spherical in shape. O K edge NEXAFS spectra indicate that O vacancies increase with Co doping. The Co L 3,2 edge NEXAFS spectra revealed that Co ions are in 2+ valence state. DC magnetization hysteresis loops and XMCD results clearly showed the intrinsic origin of temperature ferromagnetism in Co doped ZnO nanoparticles

  17. Facile hydrothermal synthesis of mn doped ZnO nanopencils for development of amperometric glucose biosensors

    Science.gov (United States)

    Shukla, Mayoorika; Pramila; Agrawal, Jitesh; Dixit, Tejendra; Palani, I. A.; Singh, Vipul

    2018-05-01

    Mn doped ZnO nanopencils were synthesized via low temperature hydrothermal process for fabrication of enzymatic electrochemical glucose biosensor. The KMnO4 was found to play a dual role in modifying morphology and inducing Mn doping. Interestingly, two different types of morphologies viz nanorods and nanopencils along with Mn doping in the later were obtained. Incorporation of Mn has shown a tremendous effect on the morphological variations, repression of defects and electrochemical charge transfer at electrode electrolyte interface. The possible reason behind obtained morphological changes has been proposed which in turn were responsible for the improvement in the different figure of merits of as fabricated enzymatic electrochemical biosensor. There has been a 17 fold enhancement in the sensitivity of the as fabricated glucose biosensor from ZnO nanorods to Mn doped ZnO nanopencils which can be attributed to morphological variation and Mn doping.

  18. Synthesis and Characterization of Molybdenum Doped ZnO Thin Films by SILAR Deposition Method

    Science.gov (United States)

    Radha, R.; Sakthivelu, A.; Pradhabhan, D.

    2016-08-01

    Molybdenum (Mo) doped zinc oxide (ZnO) thin films were deposited on the glass substrate by Successive Ionic Layer Adsorption and Reaction (SILAR) deposition method. The effect of Mo dopant concentration of 5, 6.6 and 10 mol% on the structural, morphological, optical and electrical properties of n-type Mo doped ZnO films was studied. The X-ray diffraction (XRD) results confirmed that the Mo doped ZnO thin films were polycrystalline with wurtzite structure. The field emission scanning electron microscopy (FESEM) studies shows that the surface morphology of the films changes with Mo doping. A blue shift of the optical band gap was observed in the optical studies. Effect of Mo dopant concentration on electrical conductivity was studied and it shows comparatively high electrical conductivity at 10 mol% of Mo doping concentration.

  19. The investigation of Ce doped ZnO crystal: The electronic, optical and magnetic properties

    Science.gov (United States)

    Wen, Jun-Qing; Zhang, Jian-Min; Qiu, Ze-Gang; Yang, Xu; Li, Zhi-Qin

    2018-04-01

    The electronic, optical and magnetic properties of Ce doped ZnO crystal have been studied by using first principles method. The research of formation energies show that Ce doped ZnO is energetically stable, and the formation energies reduce from 6.25% to 12.5% for Ce molar percentage. The energy band is still direct band gap after Ce doped, and band gap increases with the increase of Cesbnd Ce distance. The Fermi level moves upward into conduction band and the DOS moves to lower energy with the increase of Ce concentration, which showing the properties of n-type semiconductor. The calculated optical properties imply that Ce doped causes a red-shift of absorption peaks, and enhances the absorption of the visible light. The transition from ferromagnetic to antiferromagnetic has been found in Ce doped ZnO.

  20. Effect of Mg doping in ZnO buffer layer on ZnO thin film devices for electronic applications

    Science.gov (United States)

    Giri, Pushpa; Chakrabarti, P.

    2016-05-01

    Zinc Oxide (ZnO) thin films have been grown on p-silicon (Si) substrate using magnesium doped ZnO (Mg: ZnO) buffer layer by radio-frequency (RF) sputtering method. In this paper, we have optimized the concentration of Mg (0-5 atomic percent (at. %)) ZnO buffer layer to examine its effect on ZnO thin film based devices for electronic and optoelectronic applications. The crystalline nature, morphology and topography of the surface of the thin film have been characterized. The optical as well as electrical properties of the active ZnO film can be tailored by varying the concentration of Mg in the buffer layer. The crystallite size in the active ZnO thin film was found to increase with the Mg concentration in the buffer layer in the range of 0-3 at. % and subsequently decrease with increasing Mg atom concentration in the ZnO. The same was verified by the surface morphology and topography studies carried out with scanning electron microscope (SEM) and atomic electron microscopy (AFM) respectively. The reflectance in the visible region was measured to be less than 80% and found to decrease with increase in Mg concentration from 0 to 3 at. % in the buffer region. The optical bandgap was initially found to increase from 3.02 eV to 3.74 eV by increasing the Mg content from 0 to 3 at. % but subsequently decreases and drops down to 3.43 eV for a concentration of 5 at. %. The study of an Au:Pd/ZnO Schottky diode reveals that for optimum doping of the buffer layer the device exhibits superior rectifying behavior. The barrier height, ideality factor, rectification ratio, reverse saturation current and series resistance of the Schottky diode were extracted from the measured current voltage (I-V) characteristics.

  1. Magnetic behavior of Co–Mn co-doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Li, Hengda; Liu, Xinzhong; Zheng, Zhigong

    2014-01-01

    Here, we report on systematic studies of the magnetic properties of Co and Mn co-doped ZnO nanoparticles prepared by a sol–gel technique. The effect of the concentration of the doping ions on the magnetic properties of Co and Mn co-doped ZnO nanoparticles is presented. X-ray diffraction characterizations (XRD) of co-doped ZnO nanoparticles are all wurtzite structure. The Zn 0.96 Co 0.02 Mn 0.02 O nanoparticles and Zn 0.94 Co 0.02 Mn 0.04 O nanoparticles display ferromagnetic behavior at room temperature. Superconducting quantum interference device (SQUID) magnetometer figures show that with the concentration of the Mn ions increased, the saturation magnetic moment (M s ) increased, and the magnetic is probably due to the co-doping of the Mn ions. Our results demonstrate that the Mn ions doping concentration play an important role in the ferromagnetic properties of Co–Mn co-doped ZnO nanoparticles at room temperature. - Highlights: • The effect of the doping ions on the magnetic properties is presented. • The magnetic is probably due to the co-doping of the Mn ions. • The Mn ions concentration play an important role in the ferromagnetic properties

  2. Magnetoresistance of magnetically doped ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Behan, A J; Mokhtari, A; Blythe, H J; Fox, A M; Gehring, G A [Department of Physics and Astronomy, University of Sheffield, Sheffield S3 7RH (United Kingdom); Ziese, M, E-mail: G.A.Gehring@sheffield.ac.u [Division of Superconductivity and Magnetism, University of Leipzig, D-04103, Leipzig (Germany)

    2009-08-26

    Magnetoresistance measurements have been made at 5 K on doped ZnO thin films grown by pulsed laser deposition. ZnCoO, ZnCoAlO and ZnMnAlO samples have been investigated and compared to similar films containing no transition metal dopants. It is found that the Co-doped samples with a high carrier concentration have a small negative magnetoresistance, irrespective of their magnetic moment. On decreasing the carrier concentration, a positive contribution to the magnetoresistance appears and a further negative contribution. This second, negative contribution, which occurs at very low carrier densities, correlates with the onset of ferromagnetism due to bound magnetic polarons suggesting that the negative magnetoresistance results from the destruction of polarons by a magnetic field. An investigation of the anisotropic magnetoresistance showed that the orientation of the applied magnetic field, relative to the sample, had a large effect. The results for the ZnMnAlO samples showed less consistent trends.

  3. Transport and structural characterization of solution-processable doped ZnO nanowires

    KAUST Repository

    Noriega, Rodrigo

    2009-08-18

    The use of ZnO nanowires has become a widespread topic of interest in optoelectronics. In order to correctly assess the quality, functionality, and possible applications of such nanostructures it is important to accurately understand their electrical and optical properties. Aluminum- and gallium-doped crystalline ZnO nanowires were synthesized using a low-temperature solution-based process, achieving dopant densities of the order of 1020 cm-3. A non-contact optical technique, photothermal deflection spectroscopy, is used to characterize ensembles of ZnO nanowires. By modeling the free charge carrier absorption as a Drude metal, we are able to calculate the free carrier density and mobility. Determining the location of the dopant atoms in the ZnO lattice is important to determine the doping mechanisms of the ZnO nanowires. Solid-state NMR is used to distinguish between coordination environments of the dopant atoms.

  4. Neutron scintillator using Ga-doped ZnO phosphor with high detection efficiency

    International Nuclear Information System (INIS)

    Koyama, Shin; Kinoshita, Atsushi; Fujiwara, Akihiko; Kobayashi, Haruki; Takei, Yoshinori; Nanto, Hidehito; Katagiri, Masaki

    2009-01-01

    Zinc Oxide (ZnO) family phosphors as phosphor for neutron detector have prepared using Spark Plasma Sintering (SPS) method. The optical properties of ZnO phosphor prepared are investigated. The following results were obtained. Two dominant photoluminescence (PL) emission peaks at 395 nm and 495 nm were observed. The lifetime of the PL emission peak at 395 nm (UV emission band) is about 20 ns, which is suitable for neutron detection. The Ga (30 mol%)-doped ZnO phosphor exhibited an intense UV emission band without the visible emission band. The Ga-doped ZnO phosphor can be prepared at the atmospheric pressure of about 8 Pa using SPS method. It was found that the PL intensity of UV emission band is increased with improving the crystallinity of the ZnO phosphor. (author)

  5. Substrate effect on the room-temperature ferromagnetism in un-doped ZnO films

    Science.gov (United States)

    Zhan, Peng; Wang, Weipeng; Xie, Zheng; Li, Zhengcao; Zhang, Zhengjun; Zhang, Peng; Wang, Baoyi; Cao, Xingzhong

    2012-07-01

    Room-temperature ferromagnetism was achieved in un-doped ZnO films on silicon and quartz substrates. Photoluminescence measurement and positron annihilation analysis suggested that the ferromagnetism was originated from singly occupied oxygen vacancies (roughly estimated as ˜0.55 μB/vacancy), created in ZnO films by annealing in argon. The saturated magnetization of ZnO films was enhanced from ˜0.44 emu/g (on quartz) to ˜1.18 emu/g (on silicon) after annealing at 600 °C, as silicon acted as oxygen getter and created more oxygen vacancies in ZnO films. This study clarified the origin of ferromagnetism in un-doped ZnO and provides an idea to enhance the ferromagnetism.

  6. Variation in band gap energy and electrical analysis of double doped cobalt ferrite

    Science.gov (United States)

    Parveen, Azra; Agrawal, Shraddha; Azam, Ameer

    2018-05-01

    The Ca and Cr doped cobalt ferrite nanoparticles (Co0.9Ca0.1) (Fe0.8 Cr0.2)2O4 were synthesized by microwave gel combustion method. Microstructural studies were carried out by XRD and SEM. Structural studies suggest that the crystal system remains spinal even with the doping of calcium and chromium. The SEM image shows the spherical morphology of surface of the sample. Optical properties of Ca and Cr doped cobalt ferrite were studied by UV-visible technique in the range of 400-600 nm. The electrical conductivity of pure and doped cobalt ferrite were studied as a function of frequency and were explained on the basis of electron hopping.

  7. Characteristics of strontium-doped ZnO films on love wave filter applications

    International Nuclear Information System (INIS)

    Water, Walter; Yan, Y.-S.

    2007-01-01

    The effect of dopant concentrations in strontium-doped ZnO films on Love wave filter characteristics was investigated. Strontium-doped ZnO films with a c-axis preferred orientation were grown on ST-cut quartz by radio frequency magnetron sputtering. The crystalline structures and surface morphology of films were studied by X-ray diffraction, scanning electron microscopy and atomic force microscopy. The electromechanical coupling coefficient, dielectric constant, and temperature coefficient of frequency of filters were then determined using a network analyzer. A uniform crystalline structure and smooth surface of the ZnO films were obtained at the 1-2 mol% strontium dopant level. The electromechanical coupling coefficient of the 1 mol% strontium-doped ZnO film reaches a maximum of 0.61%, and the temperature coefficient of frequency declines to + 12.87 ppm/deg. C at a 1.5 mol% strontium dopant level

  8. Single and couple doping ZnO nanocrystals characterized by positron techniques

    International Nuclear Information System (INIS)

    Pasang, Tenzin; Namratha, Keerthiraj; Byrappa, Kullaiah; Guagliardo, Paul; Ranganathaiah, Chikkakuntappa; Samarin, S; Williams, J F

    2015-01-01

    Zinc oxide (ZnO) nanocrystals have been synthesized using a mild hydrothermal process using low temperatures and pressures with the advantages of free growth catalyst, low cost and alternative technology. Positron annihilation lifetime spectroscopy and coincidence Doppler broadening (CDB) spectroscopic methods have been used to investigate the roles of single- and co-dopants and native defects of the ZnO nanocrystals controlled by the synthesis process. It is shown that single Ag 1+ and Pd 2+ dopants occupy interstitial sites of the ZnO lattice and single Ru 3+ doping replaces Zn vacancies substitutionally with a significant effect on the CDB momentum ratio curves when compared using ZnO as the reference spectrum. The co-doping of the ZnO lattice with (Sn 4+ + Co 2+ ) shows similar CDB ratios as Ru 3+ single-doping. Also co-doping with (Ag 1+ + Pd 2+ ) or (Ag 1+ + W 6+ ) shows significant decreases in the band gap energy up to about 12.6% compared to single doping. The momentum ratio curves, referenced to undoped ZnO, indicate dopants in interstitial and substitutional sites. The presence of transition metal ions interstitially will trap electrons which resist the recombination of electrons and in turn affect the conductivity of the material. (paper)

  9. Single and couple doping ZnO nanocrystals characterized by positron techniques

    Science.gov (United States)

    Pasang, Tenzin; Namratha, Keerthiraj; Guagliardo, Paul; Byrappa, Kullaiah; Ranganathaiah, Chikkakuntappa; Samarin, S.; Williams, J. F.

    2015-04-01

    Zinc oxide (ZnO) nanocrystals have been synthesized using a mild hydrothermal process using low temperatures and pressures with the advantages of free growth catalyst, low cost and alternative technology. Positron annihilation lifetime spectroscopy and coincidence Doppler broadening (CDB) spectroscopic methods have been used to investigate the roles of single- and co-dopants and native defects of the ZnO nanocrystals controlled by the synthesis process. It is shown that single Ag1+ and Pd2+ dopants occupy interstitial sites of the ZnO lattice and single Ru3+ doping replaces Zn vacancies substitutionally with a significant effect on the CDB momentum ratio curves when compared using ZnO as the reference spectrum. The co-doping of the ZnO lattice with (Sn4+ + Co2+) shows similar CDB ratios as Ru3+ single-doping. Also co-doping with (Ag1+ + Pd2+) or (Ag1+ + W6+) shows significant decreases in the band gap energy up to about 12.6% compared to single doping. The momentum ratio curves, referenced to undoped ZnO, indicate dopants in interstitial and substitutional sites. The presence of transition metal ions interstitially will trap electrons which resist the recombination of electrons and in turn affect the conductivity of the material.

  10. Modulation-Doped In2O3/ZnO Heterojunction Transistors Processed from Solution

    KAUST Repository

    Khim, Dongyoon

    2017-03-15

    This paper reports the controlled growth of atomically sharp In2 O3 /ZnO and In2 O3 /Li-doped ZnO (In2 O3 /Li-ZnO) heterojunctions via spin-coating at 200 °C and assesses their application in n-channel thin-film transistors (TFTs). It is shown that addition of Li in ZnO leads to n-type doping and allows for the accurate tuning of its Fermi energy. In the case of In2 O3 /ZnO heterojunctions, presence of the n-doped ZnO layer results in an increased amount of electrons being transferred from its conduction band minimum to that of In2 O3 over the interface, in a process similar to modulation doping. Electrical characterization reveals the profound impact of the presence of the n-doped ZnO layer on the charge transport properties of the isotype In2 O3 /Li-ZnO heterojunctions as well as on the operating characteristics of the resulting TFTs. By judicious optimization of the In2 O3 /Li-ZnO interface microstructure, and Li concentration, significant enhancement in both the electron mobility and TFT bias stability is demonstrated.

  11. Modulation-Doped In2O3/ZnO Heterojunction Transistors Processed from Solution

    KAUST Repository

    Khim, Dongyoon; Lin, Yen-Hung; Nam, Sungho; Faber, Hendrik; Tetzner, Kornelius; Li, Ruipeng; Zhang, Qiang; Li, Jun; Zhang, Xixiang; Anthopoulos, Thomas D.

    2017-01-01

    This paper reports the controlled growth of atomically sharp In2 O3 /ZnO and In2 O3 /Li-doped ZnO (In2 O3 /Li-ZnO) heterojunctions via spin-coating at 200 °C and assesses their application in n-channel thin-film transistors (TFTs). It is shown that addition of Li in ZnO leads to n-type doping and allows for the accurate tuning of its Fermi energy. In the case of In2 O3 /ZnO heterojunctions, presence of the n-doped ZnO layer results in an increased amount of electrons being transferred from its conduction band minimum to that of In2 O3 over the interface, in a process similar to modulation doping. Electrical characterization reveals the profound impact of the presence of the n-doped ZnO layer on the charge transport properties of the isotype In2 O3 /Li-ZnO heterojunctions as well as on the operating characteristics of the resulting TFTs. By judicious optimization of the In2 O3 /Li-ZnO interface microstructure, and Li concentration, significant enhancement in both the electron mobility and TFT bias stability is demonstrated.

  12. The influence of Co content on the luminescence properties of Co-doped ZnO nanoparticles

    Science.gov (United States)

    Guo, Shuxia; Jiang, Haitao

    2018-04-01

    Co-doped ZnO nanoparticles have been synthesized by co-precipitation technique. Photoluminescence spectra change in the range from 350 nm to 600 nm and remain unchanged at about 690 nm with the Co content increase. The UV emission is assigned to exciton emission. The density of band-edge states increases with Co content. The blue emission could be ascribed to the recombination of electrons in Co+ ions and holes in the valence band, whose relative intensity and full-width at half-maximum (FWHM) increase with the increase of cobalt concentration. The red emission results from the intra-d-shell emission at Co, which is independent of Co content. The relative density and energy-level position of green emission centers are also influenced by Co content.

  13. Cobalt doped CuMnOx catalysts for the preferential oxidation of carbon monoxide

    Science.gov (United States)

    Dey, Subhashish; Dhal, Ganesh Chandra; Mohan, Devendra; Prasad, Ram; Gupta, Rajeev Nayan

    2018-05-01

    Carbon monoxide (CO) is a poisonous gas, recognized as a silent killer for the 21st century. It is produced from the partial oxidation of carbon containing compounds. The catalytic oxidation of CO receives a huge attention due to its applications in different fields. In the present work, hopcalite (CuMnOx) catalysts were synthesized using a co-precipitation method for CO oxidation purposes. Also, it was doped with the cobalt by varying concentration from 1 to 5wt%. It was observed that the addition of cobalt into the CuMnOx catalyst (by the deposition-precipitation method) improved the catalytic performance for the low-temperature CO oxidation. CuMnOx catalyst doped with 3wt% of cobalt exhibited most active performance and showed the highest activity than other cobalt concentrations. Different analytical tools (i.e. XRD, FTIR, BET, XPS and SEM-EDX) were used to characterize the as-synthesized catalysts. It was expected that the introduction of cobalt will introduce new active sites into the CuMnOx catalyst that are associated with the cobalt nano-particles. The order of calcination strategies based on the activity for cobalt doped CuMnOx catalysts was observed as: Reactive calcinations (RC) > flowing air > stagnant air. Therefore, RC (4.5% CO in air) route can be recommended for the synthesis of highly active catalysts. The catalytic activity of doped CuMnOx catalysts toward CO oxidation shows a correlation among average oxidation number of Mn and the position and the nature of the doped cobalt cation.

  14. A vanadium-doped ZnO nanosheets-polymer composite for flexible piezoelectric nanogenerators

    Science.gov (United States)

    Shin, Sung-Ho; Kwon, Yang Hyeog; Lee, Min Hyung; Jung, Joo-Yun; Seol, Jae Hun; Nah, Junghyo

    2016-01-01

    We report high performance flexible piezoelectric nanogenerators (PENGs) by employing vanadium (V)-doped ZnO nanosheets (NSs) and the polydimethylsiloxane (PDMS) composite structure. The V-doped ZnO NSs were synthesized to overcome the inherently low piezoelectric properties of intrinsic ZnO. Ferroelectric phase transition induced in the V-doped ZnO NSs contributed to significantly improve the performance of the PENGs after the poling process. Consequently, the PENGs exhibited high output voltage and current up to ~32 V and ~6.2 μA, respectively, under the applied strain, which are sufficient to directly turn on a number of light emitting diodes (LEDs). The composite approach for PENG fabrication is scalable, robust, and reproducible during periodic bending/releasing over extended cycles. The approach introduced here extends the performance limits of ZnO-based PENGs and demonstrates their potential as energy harvesting devices.We report high performance flexible piezoelectric nanogenerators (PENGs) by employing vanadium (V)-doped ZnO nanosheets (NSs) and the polydimethylsiloxane (PDMS) composite structure. The V-doped ZnO NSs were synthesized to overcome the inherently low piezoelectric properties of intrinsic ZnO. Ferroelectric phase transition induced in the V-doped ZnO NSs contributed to significantly improve the performance of the PENGs after the poling process. Consequently, the PENGs exhibited high output voltage and current up to ~32 V and ~6.2 μA, respectively, under the applied strain, which are sufficient to directly turn on a number of light emitting diodes (LEDs). The composite approach for PENG fabrication is scalable, robust, and reproducible during periodic bending/releasing over extended cycles. The approach introduced here extends the performance limits of ZnO-based PENGs and demonstrates their potential as energy harvesting devices. Electronic supplementary information (ESI) available. See DOI: 10.1039/c5nr07185b

  15. Microstructural and photoluminescence properties of sol–gel derived Tb3+ doped ZnO nanocrystals

    CSIR Research Space (South Africa)

    Kabongo, GL

    2014-04-01

    Full Text Available Un-doped and Tb(Sup3+) doped ZnO nanocrystals with different concentrations of Tb(Sup3+) were synthesized by a sol–gel method and their photoluminescence (PL) properties were investigated. The successful incorporation of Tb(sup3+) ions...

  16. Effect of iron doping concentration on magnetic properties of ZnO nanoparticles

    International Nuclear Information System (INIS)

    Sharma, Prashant K.; Dutta, Ranu K.; Pandey, Avinash C.; Layek, Samar; Verma, H.C.

    2009-01-01

    The ZnO:Fe nanoparticles of mean size 3-10 nm were synthesized at room temperature by simple co-precipitation method. The crystallite structure, morphology and size estimation were performed by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HRTEM). The wurtzite structure of ZnO gradually degrades with the increasing Fe doping concentration. The magnetic behavior of the nanoparticles of ZnO with varying Fe doping concentration was investigated using a vibrating sample magnetometer (VSM). Initially these nanoparticles showed strong ferromagnetic behavior, however at higher doping percentage of Fe, the ferromagnetic behavior was suppressed and paramagnetic nature was observed. The enhanced antiferromagnetic interaction between neighboring Fe-Fe ions suppressed the ferromagnetism at higher doping concentrations of Fe. Room-temperature Moessbauer spectroscopy investigation showed Fe 3+ nature of the iron atom in ZnO matrix.

  17. Investigations on photoelectrochemical performance of boron doped ZnO nanorods synthesized by facile hydrothermal technique

    Science.gov (United States)

    Sharma, Akash; Chakraborty, Mohua; Thangavel, R.

    2018-05-01

    Undoped and 10% Boron (B)-doped Zinc Oxide nanorods (ZnO NRs) on Tin doped Indium Oxide (ITO) coated glass substrates were synthesized using facile sol-gel, spin coating and hydrothermal method. The impact of adding Boron on the structural, optical properties, surface morphology and photoelectrochemical (PEC) performances of the ZnO NRs have been investigated. The XRD pattern confirmed the formation of pure hexagonal phase with space group P63mc (186). The same can also be clearly observed form the FESEM images. The UV-Vis study shows the narrowing in band gap from 3.22 eV to 3.19 eV with incorporation of Boron in ZnO matrix. The B-doped ZnO NRs sample shows an enhanced photocurrent density of 1.31 mA/cm2 at 0.5 V (vs. Ag/AgCl), which is more than 171% enhancement compared to bare ZnO NRs (0.483 mA/cm2) in 0.1 M Na2SO4 aqueous solution. The results clearly indicates that the boron doped ZnO NRs can be used as an efficient photoelectrode material for photoelectrochemical cell.

  18. Surfactant-assisted carbon doping in ZnO nanowires using Poly Ethylene Glycol (PEG)

    Energy Technology Data Exchange (ETDEWEB)

    Amanullah, Malik; Javed, Qurat-ul-Ain, E-mail: Quratulain@sns.nust.edu.pk; Rizwan, Syed

    2016-09-01

    Zinc Oxide (ZnO) provides unique properties owing to its wide bandgap, large resistivity range and possibility to tune the physical properties. The surfactant assisted carbon doping was made possible due to the lowering of surface energy. The ZnO and carbon doped ZnO (C-ZnO) nanowires fabricated by hydrothermal process, Poly Ethylene Glycol (PEG) is used as surfactant in hydrothermal synthesis followed by post growth annealing treatment at 600 °C–700 °C. At 5%–10% of diluted PEG carbon is doped in ZnO. The crystallinity, structural morphology and elemental composition analysis for ZnO and C-ZnO nanowires were carried out using X-ray diffraction, scanning electron microscopy and energy dispersive X-ray spectroscopy techniques respectively. Carbon doping in ZnO nanowires in the presence of different percentage of surfactant is explained by calculating the change in surface energy with respect to change in PEG molecule concentration. It was found that the surface energy per molecule modulates from 3.92 × 10{sup −8} J/m{sup 2} to 8.16 × 10{sup −7} J/m{sup 2} in the PEG concentration range between 5% and 10%. Our results provides a new theoretical calculations, implemented on real system, to observe the details of PEG-assisted Carbon doping in II-VI semiconductor nanowires. - Highlights: • ZnO and C-ZnO was synthesized by PEG assisted post growth annealing process. • At 5% and 10% of PEG successful synthesis of C-ZnO was found. • XRD, SEM and EDX characterizations confirm the successful synthesis of ZnO and C-ZnO. • Change in surface energy with respect to PEG molecule concentration was calculated.

  19. In vitro antibacterial activity of ZnO and Nd doped ZnO nanoparticles against ESBL producing Escherichia coli and Klebsiella pneumoniae

    Science.gov (United States)

    Hameed, Abdulrahman Syedahamed Haja; Karthikeyan, Chandrasekaran; Ahamed, Abdulazees Parveez; Thajuddin, Nooruddin; Alharbi, Naiyf S.; Alharbi, Sulaiman Ali; Ravi, Ganasan

    2016-04-01

    Pure ZnO and Neodymium (Nd) doped ZnO nanoparticles (NPs) were synthesized by the co-precipitation method. The synthesized nanoparticles retained the wurtzite hexagonal structure. From FESEM studies, ZnO and Nd doped ZnO NPs showed nanorod and nanoflower like morphology respectively. The FT-IR spectra confirmed the Zn-O stretching bands at 422 and 451 cm-1 for ZnO and Nd doped ZnO NPs respectively. From the UV-VIS spectroscopic measurement, the excitonic peaks were found around 373 nm and 380 nm for the respective samples. The photoluminescence measurements revealed that the broad emission was composed of ten different bands due to zinc vacancies, oxygen vacancies and surface defects. The antibacterial studies performed against extended spectrum β-lactamases (ESBLs) producing strains of Escherichia coli and Klebsiella pneumoniae showed that the Nd doped ZnO NPs possessed a greater antibacterial effect than the pure ZnO NPs. From confocal laser scanning microscopic (CLSM) analysis, the apoptotic nature of the cells was confirmed by the cell shrinkage, disorganization of cell wall and cell membrane and dead cell of the bacteria. SEM analysis revealed the existence of bacterial loss of viability due to an impairment of cell membrane integrity, which was highly consistent with the damage of cell walls.

  20. Upconversion in rare earth ions doped TeO2-ZnO glass

    International Nuclear Information System (INIS)

    Mohanty, Deepak Kumar; Rai, Vineet Kumar

    2012-01-01

    The Er 3+ /Yb 3+ doped/codoped TeO 2 -ZnO glasses have been fabricated by conventional melt and quenching technique. The absorption spectra of the doped/codoped glasses have been performed. The visible upconversion emissions of both doped and codoped glasses have been observed using 808 nm diode laser excitation. The process involved in upconversion emissions has been discussed in detail. (author)

  1. A detailed study on Sn4+ doped ZnO for enhanced photocatalytic degradation

    Science.gov (United States)

    Beura, Rosalin; Pachaiappan, R.; Thangadurai, P.

    2018-03-01

    The samples of Sn4+ doped (1, 5, 10, 15, 20 & 30%) ZnO nanostructures were synthesized by a low temperature hydrothermal method. Structural analysis by XRD and Raman spectroscopy showed the hexagonal wurtzite phase of ZnO and the formation of a secondary phase Zn2SnO4 beyond 10% doping of Sn4+. Microstructural analysis by TEM also confirmed the wurtzite ZnO with rod as well as particle like structure. Presence of various functional groups (sbnd OH, sbnd CH, Znsbnd O) were confirmed by FTIR. Optical properties were studied by UV-vis absorption, photoluminescence emission spectroscopies and lifetime measurement. Band gap of the undoped and Sn4+ doped ZnO were analyzed by Tauc plot and it was observed that the band gap of the materials had slightly decreased from 3.2 to 3.16 eV and again increased to 3.23 eV with respect to the increase in the doping concentration from 1 to 30%. A significant change was also noticed in the photoluminescence emission properties of ZnO i.e. increase in the intensity of NBE emission and decrease in DLE, on subject to Sn4+ doping. Average PL lifetime had increased from 29.45 ns for ZnO to 30.62 ns upon 1% Sn ion doping in ZnO. Electrical properties studied by solid state impedance spectroscopy showed that the conductivity had increased by one order of magnitude (from 7.48×10-8 to 2.21×10-7 S/cm) on Sn4+ doping. Photocatalytic experiments were performed on methyl orange (MO) as a model industrial dye under UV light irradiation for different irradiation times. The optimum Sn4+ content in order to achieve highest photocatalytic activity was found to be 1% Sn 4+ doping. The enhancement was achieved due to a decrease in the band gap favoring the generation of electron-hole pairs and the enhanced PL life time that delays the recombination of these charge carrier formation. The third reason was that the increased electrical conductivity that indicated the faster charge transfer in this material to enhance the photocatalytic activity. The Sn

  2. Cobalt chloride administration in athletes: a new perspective in blood doping?

    Science.gov (United States)

    Lippi, G; Franchini, M; Guidi, G C

    2005-11-01

    Blood doping is an illegal and unfair way of enhancing athletic performance by increasing the oxygen carrying capacity of the blood. Currently used methods usually involve stimulation of erythropoiesis. Gene therapy targeting the hypoxia inducible factor pathway may be an attractive alternative to traditional blood doping techniques. Hypoxia activates a large number of genes with essential roles in cell and tissue adaptation to low oxygen. Cobalt chloride is a well established chemical inducer of hypoxia-like responses such as erythropoiesis. Cobalt supplementation is not banned and therefore would not be detected by current anti-doping testing. Although there is as yet no direct or anecdotal evidence of cobalt chloride administration to athletes, its use should be warned against as being not only unfair but potentially dangerous.

  3. Improving the selective cancer killing ability of ZnO nanoparticles using Fe doping.

    Science.gov (United States)

    Thurber, Aaron; Wingett, Denise G; Rasmussen, John W; Layne, Janet; Johnson, Lydia; Tenne, Dmitri A; Zhang, Jianhui; Hanna, Charles B; Punnoose, Alex

    2012-06-01

    This work reports a new method to improve our recent demonstration of zinc oxide (ZnO) nanoparticles (NPs) selectively killing certain human cancer cells, achieved by incorporating Fe ions into the NPs. Thoroughly characterized cationic ZnO NPs (∼6 nm) doped with Fe ions (Zn(1-x )Fe (x) O, x = 0-0.15) were used in this work, applied at a concentration of 24 μg/ml. Cytotoxicity studies using flow cytometry on Jurkat leukemic cancer cells show cell viability drops from about 43% for undoped ZnO NPs to 15% for ZnO NPs doped with 7.5% Fe. However, the trend reverses and cell viability increases with higher Fe concentrations. The non-immortalized human T cells are markedly more resistant to Fe-doped ZnO NPs than cancerous T cells, confirming that Fe-doped samples still maintain selective toxicity to cancer cells. Pure iron oxide samples displayed no appreciable toxicity. Reactive oxygen species generated with NP introduction to cells increased with increasing Fe up to 7.5% and decreased for >7.5% doping.

  4. Sonochemical synthesis of Dy-doped ZnO nanostructures and their photocatalytic properties

    Energy Technology Data Exchange (ETDEWEB)

    Yayapao, Oranuch [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Thongtem, Titipun, E-mail: ttpthongtem@yahoo.com [Department of Chemistry, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Phuruangrat, Anukorn, E-mail: phuruangrat@hotmail.com [Department of Materials Science and Technology, Faculty of Science, Prince of Songkla University, Hat Yai, Songkhla 90112 (Thailand); Thongtem, Somchai [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2013-11-05

    Highlights: •Undoped and Dy-doped ZnO used as photocatalysts. •They were synthesized by sonochemistry. •The promising materials for treatment of organic pollutants. -- Abstract: Dy-doped ZnO nanostructures were synthesized by a sonochemical method. The concentration effect of Dy on their phase, morphology, optical properties and photocatalytic activities was investigated. XRD patterns indicated that the as-synthesized 0–3% Dy-doped ZnO was hexagonal wurtzite structure. SEM and TEM show that the products were nanorods with their growth direction along the c axis. The photoluminescence spectrum of 3% Dy-doped ZnO, applied by Gaussian analysis, consists of three emission peaks at 376 nm, 448 nm and 487 nm. The photocatalytic activities of the as-synthesized products were determined from the degradation of methylene blue (C{sub 16}H{sub 18}N{sub 3}SCl) by UV radiation. In this research, the 3% Dy-doped ZnO showed the highest photocatalytic activity.

  5. Sonochemical synthesis of Dy-doped ZnO nanostructures and their photocatalytic properties

    International Nuclear Information System (INIS)

    Yayapao, Oranuch; Thongtem, Titipun; Phuruangrat, Anukorn; Thongtem, Somchai

    2013-01-01

    Highlights: •Undoped and Dy-doped ZnO used as photocatalysts. •They were synthesized by sonochemistry. •The promising materials for treatment of organic pollutants. -- Abstract: Dy-doped ZnO nanostructures were synthesized by a sonochemical method. The concentration effect of Dy on their phase, morphology, optical properties and photocatalytic activities was investigated. XRD patterns indicated that the as-synthesized 0–3% Dy-doped ZnO was hexagonal wurtzite structure. SEM and TEM show that the products were nanorods with their growth direction along the c axis. The photoluminescence spectrum of 3% Dy-doped ZnO, applied by Gaussian analysis, consists of three emission peaks at 376 nm, 448 nm and 487 nm. The photocatalytic activities of the as-synthesized products were determined from the degradation of methylene blue (C 16 H 18 N 3 SCl) by UV radiation. In this research, the 3% Dy-doped ZnO showed the highest photocatalytic activity

  6. Plasma Deposition and Characterization of Copper-doped Cobalt Oxide Nanocatalysts

    Directory of Open Access Journals (Sweden)

    Jacek TYCZKOWSKI

    2013-09-01

    Full Text Available A series of pure and copper-doped cobalt oxide films was prepared by plasma-enhanced metalorganic chemical vapor deposition (PEMOCVD. The effect of Cu-doping on the chemical structure and morphology of the deposited films was investigated. Raman and FTIR spectroscopies were used to characterize the chemical structure and morphology of the produced films. The bulk composition and homogeneity of the samples were investigated by energy dispersive X-ray microanalysis (EDX, and X-ray photoelectron spectroscopy (XPS was employed to assess the surface chemical composition of pure and doped materials. The obtained results permit to affirm that the PEMOCVD technique is a simple, versatile and efficient method for providing homogeneous layers of cobalt oxides with a different content of copper. It has been found that pure cobalt oxide films mainly contain Co3O4 in the form of nanoclusters whereas the films doped with Cu are much more complex, and CoOx (also Co3O4, mixed Co-Cu oxides and CuOx nanoclusters are detected in them. Preliminary catalytical tests show that Cu-doped cobalt oxide films allow to initiate catalytic combustion of n-hexane at a lower temperature compared to the pure cobalt oxide (Co3O4 films. From what has been stated above, the plasma-deposited thin films of Cu-doped cobalt oxides pave the way towards a new class of nanomaterials with interesting catalytic properties. DOI: http://dx.doi.org/10.5755/j01.ms.19.3.2320

  7. Effect of heavy Ag doping on the physical properties of ZnO

    Science.gov (United States)

    Hou, Qingyu; Zhao, Chunwang; Jia, Xiaofang; Xu, Zhenchao

    2018-04-01

    The band structure, density of state and absorption spectrum of Zn1‑xAgxO (x = 0.02778, 0.04167) were calculated. Results indicated that a higher doping content of Ag led to a higher total energy, lower stability, higher formation energy, narrower bandgap, more significant red shift of the absorption spectrum, higher relative concentration of free hole, smaller hole effective mass, lower mobility and better conductivity. Furthermore, four types of model with the same doping content of double Ag-doped Zn1‑xAgxO (x = 0.125) but different manners of doping were established. Two types of models with different doping contents of double Ag-doped Zn1‑xAgxO (x = 0.0626, 0.0833) but the same manner of doping, were also established. Under the same doping content and different ordering occupations in Ag double doping, the doped system almost caused magnetic quenching upon the nearest neighbor -Ag-O-Ag- bonding at the direction partial to the a- or b-axis. Upon the next-nearest neighbor of -Ag-O-Zn-O-Ag- bonding at the direction partial to the c-axis, the total magnetic moment of the doped system increased, and the doped system reached a Curie temperature above the room-temperature. All these results indicated that the magnetic moments of Ag double-doped ZnO systems decreased with increased Ag doping content. Within the range of the mole number of the doping content of 0.02778-0.04167, a greater Ag doping content led to a narrower bandgap of the doped system and a more significant red shift in the absorption spectrum. The absorption spectrum of the doped ZnO system with interstitial Ag also shows a red shift.

  8. First principles study of magneto-optical properties of Fe-doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Shaoqiang, Guo [College of Science, Inner Mongolia University of Technology, Hohhot 010051 (China); Qingyu, Hou, E-mail: by0501119@126.com [College of Science, Inner Mongolia University of Technology, Hohhot 010051 (China); Zhenchao, Xu [College of Science, Inner Mongolia University of Technology, Hohhot 010051 (China); Chunwang, Zhao [College of Science, Inner Mongolia University of Technology, Hohhot 010051 (China); College of Arts and Sciences, Shanghai Maritime University, Shanghai 201306 (China)

    2016-12-15

    Studies on optical band gaps and absorption spectra of Fe-doped ZnO have conflicting conclusions, such as contradictory redshifted and blueshifted spectra. To solve this contradiction, we constructed models of un-doped and Fe-doped ZnO using first-principles theory and optimized the geometry of the three models. Electronic structures and absorption spectra were also calculated using the GGA+U method. Higher doping content of Fe resulted in larger volume of doped system, and higher total energy resulted in lower stability. Higher formation energy also led to more difficult doping. Meanwhile, the band gaps broadened and the absorption spectra exhibited an evident blue shift. The calculations were in good agreement with the experimental results. Given the unipolar structure of ZnO, four possible magnetic coupling configurations for Zn{sub 14}Fe{sub 2}O{sub 16} were calculated to investigate the magnetic properties. Results suggest that Fe doping can improve ferromagnetism in the ZnO system and that ferromagnetic stabilization was mediated by p–d exchange interaction between Fe-3d and O-2p orbitals. Therefore, the doped system is expected to obtain high stability and high Curie temperature of diluted magnetic semiconductor material, which are useful as theoretical bases for the design and preparation of the Fe-doped ZnO system’s magneto-optical properties. - Highlights: • A biomonitoring tool for the freshwater zone of template estuaries. • Water quality characterization related to nutrients and organic matter enrichment. • The percentage of a group of 24 tolerant species were capable of detecting the impairment of the water quality. • Characterization of morpho-functional traits of the selected tolerant species.

  9. ZnO doped SnO2 nanoparticles heterojunction photo-catalyst for environmental remediation

    International Nuclear Information System (INIS)

    Lamba, Randeep; Umar, Ahmad; Mehta, S.K.; Kansal, Sushil Kumar

    2015-01-01

    ZnO doped SnO 2 nanoparticles were synthesized by facile and simple hydrothermal technique and used as an effective photocatalyst for the photocatalytic degradation of harmful and toxic organic dye. The prepared nanoparticles were characterized in detail using different techniques for morphological, structural and optical properties. The characterization results revealed that the synthesized nanoparticles possess both crystal phases of tetragonal rutile phase of pure SnO 2 and wurtzite hexagonal phase of ZnO. In addition, the nanoparticles were synthesized in very high quantity with good crystallinity. The photocatalytic activity of prepared nanoparticles was evaluated by the photocatalytic degradation of methylene blue (MB) dye. Detailed photocatalytic experiments based on the effects of irradiation time, catalyst dose and pH were performed and presented in this paper. The detailed photocatalytic experiments revealed that the synthesized ZnO doped SnO 2 nanoparticles heterojunction photocatalyst exhibit best photocatalytic performance when the catalyst dose was 0.25 g/L and pH = 10. ZnO doped SnO 2 nanoparticles heterojunction photocatalyst was also compared with commercially available TiO 2 (PC-50), TiO 2 (PC-500) and SnO 2 and interestingly ZnO doped SnO 2 nanoparticles exhibited superior photocatalytic performance. The presented work demonstrates that the prepared ZnO doped SnO 2 nanoparticles are promising material for the photocatalytic degradation of organic dyes and toxic chemicals. - Highlights: • Synthesis of well-crystalline ZnO-doped SnO 2 nanoparticles. • Excellent morphological, crystalline and photoluminescent properties. • Efficient environmental remediation using ZnO-doped SnO 2 nanoparticles.

  10. Ultraviolet Sensing by Al-doped ZnO Thin Films

    International Nuclear Information System (INIS)

    Rashid, A.R.A.; Menon, P.S.; Shaari, S.

    2011-01-01

    We report the fabrication and characterization of an ultraviolet photoconductive sensing by using Al-doped ZnO films. Undoped ZnO, 1 at.% and 2 at% of Al were prepared on quartz glass by sol gel method with annealing temperature of 500 degree Celsius for 1 hour. The presence of spherical shaped nanoparticles were detected for undoped ZnO by using FESEM. The absorption edge shifted to a lower wavelength by doping with Al and excitonic peak can be observed. The band gap values increased by adding Al. I-V curves reveal an improvement in electrical properties when the samples are illuminated by ultraviolet (UV) light with a wavelength of 365 nm. At 1 at.% of Al, the film have a larger increment in photocurrent response when illuminated with UV light compared to undoped ZnO and 2 at.% Al. The thin films have a longer recovery time than response time. (author)

  11. Improvement of physical properties of ZnO thin films by tellurium doping

    Energy Technology Data Exchange (ETDEWEB)

    Sönmezoğlu, Savaş, E-mail: svssonmezoglu@kmu.edu.tr; Akman, Erdi

    2014-11-01

    Highlights: • We report the synthesis of tellurium-doped zinc oxide (Te–ZnO) thin films using sol–gel method. • Highly c-axis oriented Te-doped ZnO thin films were grown on FTO glasses as substrate. • 1.5% Te-doping ratio could improve the physical properties of ZnO thin films. - Abstract: This investigation addressed the structural, optical and morphological properties of tellurium incorporated zinc oxide (Te–ZnO) thin films. The obtained results indicated that Te-doped ZnO thin films exhibit an enhancement of band gap energy and crystallinity compared with non-doped films. The optical transmission spectra revealed a shift in the absorption edge toward lower wavelengths. X-ray diffraction measurement demonstrated that the film was crystallized in the hexagonal (wurtzite) phase and presented a preferential orientation along the c-axis. The XRD obtained patterns indicate that the crystallite size of the thin films, ranging from 23.9 to 49.1 nm, changed with the Te doping level. The scanning electron microscopy and atomic force microscopy results demonstrated that the grain size and surface roughness of the thin films increased as the Te concentration increased. Most significantly, we demonstrate that it is possible to control the structural, optical and morphological properties of ZnO thin films with the isoelectronic Te-incorporation level.

  12. Photoluminescence study of novel phosphorus-doped ZnO nanotetrapods synthesized by chemical vapour deposition

    International Nuclear Information System (INIS)

    Yu Dongqi; Hu Lizhong; Qiao Shuangshuang; Zhang Heqiu; Fu Qiang; Chen Xi; Sun Kaitong; Len, Song-En Andy; Len, L K

    2009-01-01

    Novel phosphorus-doped and undoped single crystal ZnO nanotetrapods were fabricated on sapphire by a simple chemical vapour deposition method, using phosphorus pentoxide (P 2 O 5 ) as the dopant source. The optical properties of the samples were investigated by photoluminescence (PL) spectroscopy. Low-temperature PL measurements of phosphorus-doped and undoped samples were compared, and the results indicated a decrease in deep level defects due to the incorporation of a phosphorus acceptor dopant. The PL spectrum of the phosphorus-doped sample at 10 K exhibited several acceptor-bound exciton related emission peaks. The effect of phosphorus doping on the optical characteristics of the samples was investigated by excitation intensity and temperature dependent PL spectra. The acceptor-binding energies of the phosphorus dopant were estimated to be about 120 meV, in good agreement with the corresponding theoretical and experimental values in phosphorus-doped ZnO films and nanowires.

  13. On single doping and co-doping of spray pyrolysed ZnO films: Structural, electrical and optical characterisation

    International Nuclear Information System (INIS)

    Vimalkumar, T.V.; Poornima, N.; Jinesh, K.B.; Kartha, C. Sudha; Vijayakumar, K.P.

    2011-01-01

    In this paper we present studies on ZnO thin films (prepared using Chemical Spray pyrolysis (CSP) technique) doped in two different ways; in one set, 'single doping' using indium was done while in the second set, 'co-doping' using indium and fluorine was adopted. In the former case, effect of in-situ as well as ex-situ doping using In was analyzed. Structural (XRD studies), electrical (I-V measurements) and optical characterizations (through absorption, transmission and photoluminescence studies) of the films were done. XRD analysis showed that, for spray-deposited ZnO films, ex-situ doping using Indium resulted in preferred (0 0 2) plane orientation, while in-situ doping caused preferred orientation along (1 0 0), (0 0 2), (1 0 1) planes; however for higher percentage of in-situ doping, orientation of grains changed from (0 0 2) plane to (1 0 1) plane. The co-doped films had (0 0 2) and (1 0 1) planes. Lowest resistivity (2 x 10 -3 Ω cm) was achieved for the films, doped with 1% Indium through in-situ method. Photoluminescence (PL) emissions of ex-situ doped and co-doped samples had two peaks; one was the 'near band edge' emission (NBE) and the other was the 'blue-green' emission. But interestingly the PL emission of in-situ doped samples exhibited only the 'near band edge' emission. Optical band gap of the films increased with doping percentage, in all cases of doping.

  14. Al-doped ZnO seed layer-dependent crystallographic control of ZnO nanorods by using electrochemical deposition

    Energy Technology Data Exchange (ETDEWEB)

    Son, Hyo-Soo; Choi, Nak-Jung [Department of Nano-Optical Engineering, Korea Polytechnic University, Siheung 429-793 (Korea, Republic of); Kim, Kyoung-Bo [Department of Metallurgical and Materials Engineering, Inha Technical College, Incheon 402-752 (Korea, Republic of); Kim, Moojin [Department of Renewable Energy, Jungwon University, Goesan-gun, Chungbuk 367-805 (Korea, Republic of); Lee, Sung-Nam, E-mail: snlee@kpu.ac.kr [Department of Nano-Optical Engineering, Korea Polytechnic University, Siheung 429-793 (Korea, Republic of)

    2016-10-15

    Highlights: • Polar and semipolar ZnO NRs were successfully achieved by hydrothermal synthesis. • Semipolar and polar ZnO NRs were grown on ZnO and AZO/m-sapphire, respectively. • Al % of AZO/m-sapphire enhanced the lateral growth rate of polar ZnO NRs. - Abstract: We investigated the effect of an Al-doped ZnO film on the crystallographic direction of ZnO nanorods (NRs) using electrochemical deposition. From high-solution X-ray diffraction measurements, the crystallographic plane of ZnO NRs grown on (1 0 0) ZnO/m-plane sapphire was (1 0 1). The surface grain size of the (100) Al-doped ZnO (AZO) film decreased with increasing Al content in the ZnO seed layer, implying that the Al dopant accelerated the three-dimensional (3D) growth of the AZO film. In addition, it was found that with increasing Al doping concentration of the AZO seed layer, the crystal orientation of the ZnO NRs grown on the AZO seed layer changed from [1 0 1] to [0 0 1]. With increasing Al content of the nonpolar (1 0 0) AZO seed layer, the small surface grains with a few crystallographic planes of the AZO film changed from semipolar (1 0 1) ZnO NRs to polar (0 0 1) ZnO NRs due to the increase of the vertical [0 0 1] growth rate of the ZnO NRs owing to excellent electrical properties.

  15. Room temperature ferromagnetism in Mg-doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Singh, Jaspal; Vashihth, A.; Gill, Pritampal Singh; Verma, N. K.

    2015-01-01

    Zn 1-x Mg x O (x = 0, 0,10) nanoparticles were successfully synthesized using sol-gel method. X-ray diffraction (XRD) confirms that the synthesized nanoparticles possess wurtzite phase having hexagonal structure. Morphological analysis was carried out using transmission electron microscopy (TEM) which depicts the spherical morphology of ZnO nanoparticles. Energy dispersive spectroscopy (EDS) showed the presence of Mg in ZnO nanoparticles. Electron spin resonance (ESR) signal was found to be decreasing with increasing of Mg-doping concentration. The room temperature ferromagnetism was observed in undoped and Mg-doped ZnO nanoparticles. The increase of Mg-doping concentration resulted in decrease of saturation magnetization value which could be attributed to decrease of oxygen vacancies present in host nanoparticles

  16. Magnetism in V-/Mn-doped ZnO layers fabricated on sapphire

    Energy Technology Data Exchange (ETDEWEB)

    Mofor, A.C.; El-Shaer, A.; Schlenker, E.; Bakin, A.; Waag, A. [Technical University Braunschweig, Institute of Semiconductor Technology, Braunschweig (Germany); Reuss, F.; Kling, R.; Schoch, W.; Limmer, W. [University Ulm, Department of Semiconductor Physics, Ulm (Germany); Ahlers, H.; Siegner, U.; Sievers, S.; Albrecht, M. [Physikalisch-Technische Bundesanstalt (PTB), Braunschweig (Germany); Eisenmenger, J.; Mueller, T.; Ziemann, P. [University Ulm, Department of Solid State Physics, Ulm (Germany); Huebel, A.; Denninger, G. [Universitaet Stuttgart, 2. Physkalisches Institut, Stuttgart (Germany)

    2007-07-15

    Doping ZnO with transition metals (TM) is an obvious approach to produce diluted magnetic semiconductors for magnetoelectronic and spintronic applications. We have carried out experimental studies on the fabrication and characterisation of Mn-doped ZnO layers and V-doped ZnO layers and nanorods, the results of which are reviewed in this paper. From SQUID measurements, both epitaxial and implanted ZnMnO layers show paramagnetic behaviour. Epitaxial ZnVO layers show ferromagnetic SQUID signals, but the presence of any secondary phases in the ZnVO layers may not be ruled out. We also show that the used Al{sub 2}O{sub 3} substrates produce a ferromagnetic SQUID signal, that complicates the analysis of magnetisation data and hence the confirmation of ferromagnetism only from SQUID results. (orig.)

  17. Role of vacancy defects in Al doped ZnO thin films for optoelectronic devices

    Science.gov (United States)

    Rotella, H.; Mazel, Y.; Brochen, S.; Valla, A.; Pautrat, A.; Licitra, C.; Rochat, N.; Sabbione, C.; Rodriguez, G.; Nolot, E.

    2017-12-01

    We report on the electrical, optical and photoluminescence properties of industry-ready Al doped ZnO thin films grown by physical vapor deposition, and their evolution after annealing under vacuum. Doping ZnO with Al atoms increases the carrier density but also favors the formation of Zn vacancies, thereby inducing a saturation of the conductivity mechanism at high aluminum content. The electrical and optical properties of these thin layered materials are both improved by annealing process which creates oxygen vacancies that releases charge carriers thus improving the conductivity. This study underlines the effect of the formation of extrinsic and intrinsic defects in Al doped ZnO compound during the fabrication process. The quality and the optoelectronic response of the produced films are increased (up to 1.52 mΩ \\cdotcm and 3.73 eV) and consistent with the industrial device requirements.

  18. A simple photolytic reactor employing Ag-doped ZnO nanowires for water purification

    Energy Technology Data Exchange (ETDEWEB)

    Udom, Innocent; Zhang, Yangyang [Clean Energy Research Center, College of Engineering, University of South Florida, Tampa, FL 33620 (United States); Ram, Manoj K., E-mail: mkram@usf.edu [Clean Energy Research Center, College of Engineering, University of South Florida, Tampa, FL 33620 (United States); Stefanakos, Elias K. [Clean Energy Research Center, College of Engineering, University of South Florida, Tampa, FL 33620 (United States); Hepp, Aloysius F. [Department of Chemical and Biomedical Engineering, University of South Florida, Tampa, Fl 33620 (United States); Elzein, Radwan; Schlaf, Rudy [Department of Electrical Engineering, University of South Florida, Tampa, Fl 33620 (United States); Goswami, D. Yogi [NASA Glenn Research Center, Research and Technology Directorate, MS 302-1, 21000 Brookpark Road, Cleveland, OH 44135 (United States)

    2014-08-01

    Well-aligned native zinc oxide (ZnO) and silver-doped ZnO (Ag-ZnO) films were deposited on borosilicate glass via a simple, low-cost, low-temperature, scalable hydrothermal process. The as-synthesized ZnO and Ag-ZnO films were characterized by X-ray diffraction; scanning electron microscopy, UV–visible spectroscopy, and Fourier transform infrared spectroscopy. A simple photolytic reactor was fabricated and later used to find the optimum experimental conditions for photocatalytic performance. The photodegradation of methyl orange in water was investigated using as-prepared ZnO and Ag-ZnO nanowires, and was compared to P25 (a commercial photocatalyst) in both visible and UV radiations. The P25 and Ag-ZnO showed a similar photodegradation performance under UV light, but Ag-ZnO demonstrated superior photocatalytic activity under visible irradiation. The optimized doping of Ag in Ag-ZnO enhanced photocatalytic activity in a simple reactor design and indicated potential applicability of Ag-ZnO for large-scale purification of water under solar irradiation. - Highlights: • Well-aligned zinc oxide (ZnO) and silver-doped ZnO (Ag-ZnO) nanowires were developed. • Simple and effective photolytic reactor was fabricated for water purification. • Ag-ZnO demonstrated superior photocatalytic activity under visible irradiation. • Amount of Ag atoms in Ag-ZnO nanowires is a key to increase photocatalytic activity.

  19. A simple photolytic reactor employing Ag-doped ZnO nanowires for water purification

    International Nuclear Information System (INIS)

    Udom, Innocent; Zhang, Yangyang; Ram, Manoj K.; Stefanakos, Elias K.; Hepp, Aloysius F.; Elzein, Radwan; Schlaf, Rudy; Goswami, D. Yogi

    2014-01-01

    Well-aligned native zinc oxide (ZnO) and silver-doped ZnO (Ag-ZnO) films were deposited on borosilicate glass via a simple, low-cost, low-temperature, scalable hydrothermal process. The as-synthesized ZnO and Ag-ZnO films were characterized by X-ray diffraction; scanning electron microscopy, UV–visible spectroscopy, and Fourier transform infrared spectroscopy. A simple photolytic reactor was fabricated and later used to find the optimum experimental conditions for photocatalytic performance. The photodegradation of methyl orange in water was investigated using as-prepared ZnO and Ag-ZnO nanowires, and was compared to P25 (a commercial photocatalyst) in both visible and UV radiations. The P25 and Ag-ZnO showed a similar photodegradation performance under UV light, but Ag-ZnO demonstrated superior photocatalytic activity under visible irradiation. The optimized doping of Ag in Ag-ZnO enhanced photocatalytic activity in a simple reactor design and indicated potential applicability of Ag-ZnO for large-scale purification of water under solar irradiation. - Highlights: • Well-aligned zinc oxide (ZnO) and silver-doped ZnO (Ag-ZnO) nanowires were developed. • Simple and effective photolytic reactor was fabricated for water purification. • Ag-ZnO demonstrated superior photocatalytic activity under visible irradiation. • Amount of Ag atoms in Ag-ZnO nanowires is a key to increase photocatalytic activity

  20. Highly doped ZnO films deposited by spray-pyrolysis. Design parameters for optoelectronic applications

    Energy Technology Data Exchange (ETDEWEB)

    Garcés, F.A., E-mail: felipe.garces@santafe-conicet.gov.ar [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Budini, N. [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Schmidt, J.A.; Arce, R.D. [Instituto de Física del Litoral (UNL-CONICET), Güemes 3450, Santa Fe S3000GLN (Argentina); Facultad de Ingeniería Química, Universidad Nacional del Litoral, Santiago del Estero 2829, Santa Fe S3000AOM (Argentina)

    2016-04-30

    Synthesis and preparation of ZnO films are relevant subjects for obtaining transparent and conducting layers with interesting applications in optoelectronics and photovoltaics. Optimization of parameters such as dopant type and concentration, deposition time and substrate temperature is important for obtaining ZnO layers with optimal properties. In this work we present a study about the induced effects of deposition time on optical and electrical properties of ZnO thin films. These films were deposited by spray pyrolysis of a suitable Zn precursor, obtained through the sol–gel method. The deposition time has direct incidence on internal stress in the crystal structure, generating defects that may affect transparency and electrical transport into the layers. We performed mosaicity measurements, through X-ray diffraction, and used it as a tool to get an insight on structural characteristics and homogeneity of ZnO layers. Also, through this technique, we analyzed thickness and doping effects on crystallinity and carrier transport properties. - Highlights: • Al-doped ZnO films with high conductivity and moderate Hall mobility were obtained. • Mosaicity between crystalline domains increased with film thickness. • Lattice parameters a and c diminished linearly as a function of Al concentration. • First steps for developing porous silicon/doped ZnO heterojunctions were presented.

  1. Highly doped ZnO films deposited by spray-pyrolysis. Design parameters for optoelectronic applications

    International Nuclear Information System (INIS)

    Garcés, F.A.; Budini, N.; Schmidt, J.A.; Arce, R.D.

    2016-01-01

    Synthesis and preparation of ZnO films are relevant subjects for obtaining transparent and conducting layers with interesting applications in optoelectronics and photovoltaics. Optimization of parameters such as dopant type and concentration, deposition time and substrate temperature is important for obtaining ZnO layers with optimal properties. In this work we present a study about the induced effects of deposition time on optical and electrical properties of ZnO thin films. These films were deposited by spray pyrolysis of a suitable Zn precursor, obtained through the sol–gel method. The deposition time has direct incidence on internal stress in the crystal structure, generating defects that may affect transparency and electrical transport into the layers. We performed mosaicity measurements, through X-ray diffraction, and used it as a tool to get an insight on structural characteristics and homogeneity of ZnO layers. Also, through this technique, we analyzed thickness and doping effects on crystallinity and carrier transport properties. - Highlights: • Al-doped ZnO films with high conductivity and moderate Hall mobility were obtained. • Mosaicity between crystalline domains increased with film thickness. • Lattice parameters a and c diminished linearly as a function of Al concentration. • First steps for developing porous silicon/doped ZnO heterojunctions were presented.

  2. Structural and Optical Properties of Eu Doped ZnO Nanorods prepared by Pulsed Laser Deposition

    KAUST Repository

    Alarawi, Abeer

    2014-06-23

    Nano structured wide band gap semiconductors have attracted attention of many researchers due to their potential electronic and optoelectronic applications. In this thesis, we report successful synthesis of well aligned Eu doped ZnO nano-rods prepared, for the first time to our knowledge, by pulsed laser deposition (PLD) without any catalyst. X-ray diffraction (XRD) patterns shows that these Eu doped ZnO nanorods are grown along the c-axis of ZnO wurtzite structure. We have studied the effect of the PLD growth conditions on forming vertically aligned Eu doped ZnO nanorods. The structural properties of the material are investigated using a -scanning electron microscope (SEM). The PLD parameters must be carefully controlled in order to obtain c-axis oriented ZnO nanorods on sapphire substrates, without the use of any catalyst. The experiments conducted in order to identify the optimal growth conditions confirmed that, by adjusting the target-substrate distance, substrate temperature, laser energy and deposition duration, the nanorod size could be successfully controlled. Most importantly, the results indicated that the photoluminescence (PL) properties reflect the quality of the ZnO nanorods. These parameters can change the material’s structure from one-dimensional to two-dimensional however the laser energy and frequency affect the size and the height of the nanorods; the xygen pressure changes the density of the nanorods.

  3. Synthesis and characterization of Mn-doped ZnO diluted magnetic semiconductors

    Energy Technology Data Exchange (ETDEWEB)

    Abdel-Galil, A. [Solid State Physics and Accelerators Department, NCRRT, Atomic Energy Authority, Cairo (Egypt); Balboul, M.R., E-mail: m_balboul@yahoo.com [Solid State Physics and Accelerators Department, NCRRT, Atomic Energy Authority, Cairo (Egypt); Sharaf, A. [Radiation Engineering Department, NCRRT, Atomic Energy Authority, Cairo (Egypt)

    2015-11-15

    In the present work undoped and Mn doped ZnO nanoparticles (ZnO:Mn), diluted magnetic semiconductors, were successfully synthesized by the sol–gel method at room temperature. The morphology of ZnO nanoparticles constituted by flower-like structures with hexagonal morphologies that changed significantly after the incorporation of Mn. Rietveld refinements results showed that Mn ions are successfully doped into ZnO matrix without altering its wurtzite phase. Meanwhile, Raman spectroscopy analyses confirm the wurtzite structure of undoped ZnO and ZnO:Mn nanoparticles. The lattice parameters increase with increasing Mn content due to the large ionic radius of Mn{sup 2+} compared to that of Zn{sup 2+}. Electron spin resonance measurements were performed to gain information about oxidation state and site occupancy of the magnetic Mn ions in the ZnO lattice. Moreover, UV–vis absorption spectra have been utilized to calculate the optical band gap of the undoped ZnO and ZnO:Mn nanoparticles before and after different γ-irradiation doses. The band gap of ZnO:Mn (2%) is 2.62 eV which is noticeably smaller than the 3.26 eV of undoped ZnO. The thermal decomposition properties of the prepared nanoparticle samples were also studied using simultaneous Thermogravimetric analysis in temperature range from 30 to 500 °C.

  4. Influence Al doped ZnO nanostructure on structural and optical properties

    International Nuclear Information System (INIS)

    Ramelan, Ari Handono; Wahyuningsih, Sayekti; Chasanah, Uswatul; Munawaroh, Hanik

    2016-01-01

    The preparation of Al-doped ZnO (AZO) thin films prepared by the spin-coating method was reported. Preparation of AZO was conducted by annealing treatment at a temperature of 700°C. While the spin-coating process of AZO thin films were done at 2000 and 3000 rpm respectively. The structural properties of ZnO were determined by X- ray diffraction (XRD) analysis. ZnOnanostructure was formed after annealed at atemperature of 400°C.The morphology of ZnO was determined by Scanning Electron Microscopy (SEM) showed the irregular morphology about 30-50µm in size. Al doped on ZnO influenced the optical properties of those material. Increasing Al contain on ZnO cause of shifting to the lower wavelength. The optical properties of the ZnO as well as AZO films showed that higher reflectance on the ultraviolet region so those materials were used as anti-reflecting agent.Al addition significantly enhance the optical transparency and induce the blue-shift in optical bandgap of ZnO films.

  5. Synthesis and characterization of ZnO and Ni doped ZnO nanorods by thermal decomposition method for spintronics application

    International Nuclear Information System (INIS)

    Saravanan, R.; Santhi, Kalavathy; Sivakumar, N.; Narayanan, V.; Stephen, A.

    2012-01-01

    Zinc oxide nanorods and diluted magnetic semiconducting Ni doped ZnO nanorods were prepared by thermal decomposition method. This method is simple and cost effective. The decomposition temperature of acetate and formation of oxide were determined by TGA before the actual synthesis process. The X-ray diffraction result indicates the single phase hexagonal structure of zinc oxide. The transmission electron microscopy and scanning electron microscopy images show rod like structure of ZnO and Ni doped ZnO samples with the diameter ∼ 35 nm and the length in few micrometers. The surface analysis was performed using X-ray photoelectron spectroscopic studies. The Ni doped ZnO exhibits room temperature ferromagnetism. This diluted magnetic semiconducting Ni doped ZnO nanorods finds its application in spintronics. - Highlights: ► The method used is very simple and cost effective compared to all other methods for the preparation DMS materials. ► ZnO and Ni doped ZnO nanorods ► Ferromagnetism at room temperature

  6. The crystallization and physical properties of Al-doped ZnO nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Chen, K.J. [Institute of Microelectronics and Department of Electrical Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China); Fang, T.H. [Institute of Mechanical and Electromechanical Engineering, National Formosa University, Yunlin 632, Taiwan (China); Hung, F.Y. [Institute of Nanotechnology and Microsystems Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China)], E-mail: fyhung@mail.mse.ncku.edu.tw; Ji, L.W. [Institute of Mechanical and Electromechanical Engineering, National Formosa University, Yunlin 632, Taiwan (China); Chang, S.J.; Young, S.J. [Institute of Microelectronics and Department of Electrical Engineering, Center for Micro/Nano Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China); Hsiao, Y.J. [Department of Materials Science and Engineering, National Cheng Kung University, Tainan 701, Taiwan (China)

    2008-07-15

    Un-doped Al (0-9 at.%) nanoparticles and doped ZnO powders were prepared by the sol-gel method. The nanoparticles were heated at 700-800 deg. C for 1 h in air and then analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectra and photoluminescence (PL). The results of un-doped (ZnO) and Al-doped ZnO (AZO) nanoparticles were also compared to investigate the structural characteristics and physical properties. XRD patterns of AZO powders were similar to those of ZnO powders, indicating that micro-Al ions were substituted for Zn atoms and there were no variations in the structure of the ZnO nanoparticles. From the XRD and SEM data, the grain size of the AZO nanoparticles increased from 34.41 to 40.14 nm when the annealing temperature was increased. The Raman intensity of the AZO nanoparticles (Al = 5 at.%) increased when the annealing temperature was increased. Increasing the degree of crystalline not only reduced the residual stress, but also improved the physical properties of the nanoparticles.

  7. The crystallization and physical properties of Al-doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Chen, K.J.; Fang, T.H.; Hung, F.Y.; Ji, L.W.; Chang, S.J.; Young, S.J.; Hsiao, Y.J.

    2008-01-01

    Un-doped Al (0-9 at.%) nanoparticles and doped ZnO powders were prepared by the sol-gel method. The nanoparticles were heated at 700-800 deg. C for 1 h in air and then analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectra and photoluminescence (PL). The results of un-doped (ZnO) and Al-doped ZnO (AZO) nanoparticles were also compared to investigate the structural characteristics and physical properties. XRD patterns of AZO powders were similar to those of ZnO powders, indicating that micro-Al ions were substituted for Zn atoms and there were no variations in the structure of the ZnO nanoparticles. From the XRD and SEM data, the grain size of the AZO nanoparticles increased from 34.41 to 40.14 nm when the annealing temperature was increased. The Raman intensity of the AZO nanoparticles (Al = 5 at.%) increased when the annealing temperature was increased. Increasing the degree of crystalline not only reduced the residual stress, but also improved the physical properties of the nanoparticles

  8. Growth and Characterization of Indium Doped ZnO Nano wires Using Thermal Evaporation Method

    International Nuclear Information System (INIS)

    Abrar Ismardi; Dee, C.F.; Majlis, B.Y.

    2011-01-01

    Indium doped ZnO nano wires were grown on silicon substrate using vapor thermal deposition method without using any catalyst. Morphological structures were extensively investigated using field emission scanning electron microscopy (FESEM) and show that the nano wires have uniformly hexagonal nano structures with diameters less than 100 nm and lengths from one to a few microns. The sample was measured for elemental composition with energy dispersive X-ray (EDX) spectroscopy, Zn, In and O elements were found on the sample. XRD spectrum of indium doped ZnO nano wires revealed that the nano wires have a high crystalline structure. (author)

  9. Ionized zinc vacancy mediated ferromagnetism in copper doped ZnO thin films

    Directory of Open Access Journals (Sweden)

    Shi-Yi Zhuo

    2012-03-01

    Full Text Available This paper reports the origin of ferromagnetism in Cu-doped ZnO thin films. Room-temperature ferromagnetism is obtained in all the thin films when deposited at different oxygen partial pressure. An obviously enhanced peak corresponding to zinc vacancy is observed in the photoluminescence spectra, while the electrical spin resonance measurement implies the zinc vacancy is negative charged. After excluding the possibility of direct exchange mechanisms (via free carriers, we tentatively propose a quasi-indirect exchange model (via ionized zinc vacancy for Cu-doped ZnO system.

  10. Preparation of Aligned ZnO Nanorod Arrays on Sn-Doped ZnO Thin Films by Sonicated Sol-Gel Immersion Fabricated for Dye-Sensitized Solar Cell

    Directory of Open Access Journals (Sweden)

    I. Saurdi

    2014-01-01

    Full Text Available Aligned ZnO Nanorod arrays are deposited on the Sn-doped ZnO thin film via sonicated sol-gel immersion method. The structural, optical, and electrical properties of the Sn-doped ZnO thin films were investigated. Results show that the Sn-doped ZnO thin films with small grain size (~20 nm, high average transmittance (96% in visible region, and good resistivity 7.7 × 102 Ω·cm are obtained for 2 at.% Sn doping concentration. The aligned ZnO nanorod arrays with large surface area were also obtained for 2 at.% Sn-doped ZnO thin film. They were grown on sol-gel derived Sn-doped ZnO thin film, which acts as a seed layer, via sonicated sol-gel immersion method. The grown aligned ZnO nanorod arrays show high transmittance at visible region. The fabricated dye-sensitised solar cell based on the 2.0 at.% Sn-doped ZnO thin film with aligned ZnO nanorod arrays exhibits improved current density, open-circuit voltage, fill factor, and conversion efficiency compared with the undoped ZnO and 1 at.% Sn-doped ZnO thin films.

  11. Photocatalytic degradation of the Paracetamol drug using Lanthanum doped ZnO nanoparticles and their in-vitro cytotoxicity assay

    International Nuclear Information System (INIS)

    Shakir, Mohammad; Faraz, Mohd; Sherwani, Mohd Asif; Al-Resayes, Saud I.

    2016-01-01

    The doping of semiconductor by rare earth metals nanoparticles is an effective way for increasing photocatalytic activity. Zinc oxide and Lanthanum doped Zinc oxide nanoparticles were synthesized by modifying the gel-combustion method. It was found that La can greatly enhance the cytotoxicity and photocatalytic activity of ZnO nanoparticles towards various cell lines and Paracetamol drug. These nanoparticles were characterized by various spectroscopic and other techniques which clearly revealed the presence of lanthanum ions. The absorption edge shifts towards the visible region after doping with La ions. This shift shows that the doping of La ions is favorable for absorbing the visible light. The comparative photocatalytic and cytotoxicity activity revealed that La doped ZnO nanoparticles remarkably enhanced activities as compared to the ZnO nanoparticles. The outcome of these studies offers valuable for planning La doped ZnO nanoparticles having cytotoxicity and photocatalytic activities helpful for the formulation of anticancer product and waste water remediation.

  12. Photocatalytic degradation of the Paracetamol drug using Lanthanum doped ZnO nanoparticles and their in-vitro cytotoxicity assay

    Energy Technology Data Exchange (ETDEWEB)

    Shakir, Mohammad, E-mail: shakir078@yahoo.com [Department of Chemistry, Aligarh Muslim University, Aligarh 202002 (India); Faraz, Mohd [Department of Chemistry, Aligarh Muslim University, Aligarh 202002 (India); Sherwani, Mohd Asif [Interdisciplinary Biotechnology Unit, Aligarh Muslim University, Aligarh 202002 (India); Al-Resayes, Saud I. [Department of Chemistry, College of Science, King Saud University, Riyadh 11451 (Saudi Arabia)

    2016-08-15

    The doping of semiconductor by rare earth metals nanoparticles is an effective way for increasing photocatalytic activity. Zinc oxide and Lanthanum doped Zinc oxide nanoparticles were synthesized by modifying the gel-combustion method. It was found that La can greatly enhance the cytotoxicity and photocatalytic activity of ZnO nanoparticles towards various cell lines and Paracetamol drug. These nanoparticles were characterized by various spectroscopic and other techniques which clearly revealed the presence of lanthanum ions. The absorption edge shifts towards the visible region after doping with La ions. This shift shows that the doping of La ions is favorable for absorbing the visible light. The comparative photocatalytic and cytotoxicity activity revealed that La doped ZnO nanoparticles remarkably enhanced activities as compared to the ZnO nanoparticles. The outcome of these studies offers valuable for planning La doped ZnO nanoparticles having cytotoxicity and photocatalytic activities helpful for the formulation of anticancer product and waste water remediation.

  13. The cellular magnetic response and biocompatibility of biogenic zinc- and cobalt-doped magnetite nanoparticles

    Science.gov (United States)

    Moise, Sandhya; Céspedes, Eva; Soukup, Dalibor; Byrne, James M.; El Haj, Alicia J.; Telling, Neil D.

    2017-01-01

    The magnetic moment and anisotropy of magnetite nanoparticles can be optimised by doping with transition metal cations, enabling their properties to be tuned for different biomedical applications. In this study, we assessed the suitability of bacterially synthesized zinc- and cobalt-doped magnetite nanoparticles for biomedical applications. To do this we measured cellular viability and activity in primary human bone marrow-derived mesenchymal stem cells and human osteosarcoma-derived cells. Using AC susceptibility we studied doping induced changes in the magnetic response of the nanoparticles both as stable aqueous suspensions and when associated with cells. Our findings show that the magnetic response of the particles was altered after cellular interaction with a reduction in their mobility. In particular, the strongest AC susceptibility signal measured in vitro was from cells containing high-moment zinc-doped particles, whilst no signal was observed in cells containing the high-anisotropy cobalt-doped particles. For both particle types we found that the moderate dopant levels required for optimum magnetic properties did not alter their cytotoxicity or affect osteogenic differentiation of the stem cells. Thus, despite the known cytotoxicity of cobalt and zinc ions, these results suggest that iron oxide nanoparticles can be doped to sufficiently tailor their magnetic properties without compromising cellular biocompatibility.

  14. Strong compensation hinders the p-type doping of ZnO: a glance over surface defect levels

    Science.gov (United States)

    Huang, B.

    2016-07-01

    We propose a surface doping model of ZnO to elucidate the p-type doping and compensations in ZnO nanomaterials. With an N-dopant, the effects of N on the ZnO surface demonstrate a relatively shallow acceptor level in the band gap. As the dimension of the ZnO materials decreases, the quantum confinement effects will increase and render the charge transfer on surface to influence the shifting of Fermi level, by evidence of transition level changes of the N-dopant. We report that this can overwhelm the intrinsic p-type conductivity and transport of the ZnO bulk system. This may provide a possible route of using surface doping to modify the electronic transport and conductivity of ZnO nanomaterials.

  15. Magnetic properties of sol-gel synthesized C-doped ZnO nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Dung, Nguyen Duc, E-mail: dung.nguyenduc@hust.edu.vn [Advanced Institute of Science and Technology (AIST), Hanoi University of Science and Technology, No.1 Dai Co Viet, Hanoi (Viet Nam); Son, Cao Thai; Loc, Pham Vu; Cuong, Nguyen Huu; Kien, Pham The; Huy, Pham Thanh [Advanced Institute of Science and Technology (AIST), Hanoi University of Science and Technology, No.1 Dai Co Viet, Hanoi (Viet Nam); Ha, Ngo Ngoc [International Training Institute for Materials Science (ITIMS), Hanoi University of Science and Technology, No.1 Dai Co Viet, Hanoi (Viet Nam)

    2016-05-25

    ZnO doping with Carbon (C-doped ZnO) materials were prepared by sol-gel technique following with a heat treatment process. Single phase of Wurtzite crystal structure of ZnO was concluded via x-ray diffraction (XRD) with a large amount of excess C tracking by energy dispersive X-ray spectroscopy (EDX) analysis. Two types of ZnO crystals (twinning particles) with different grain sizes and shapes were identified via scanning electron microscopy (FE-SEM). The first type has a smaller grain size of about 20 nm and hexagonal shape. And the second type has a larger grain size of about 80–120 nm and round shape. C substitutions of both Zn and O sites to form C–O and C–Zn bonds were conclusively confirmed via x-ray photoelectron spectroscope (XPS). Experimental evidences for the co-existence of different ferromagnetic phases in the materials are reported and discussed. Two Curie points at high temperatures (>500 °C) are presented. A metamagnetic transition was observed at magnetic field H = 19.2 kOe which was related to the co-existence of ferromagnetic phases. These involve in the formation of twinning C-doped ZnO nanoparticles. - Highlights: • Formation of sol-gel prepared single phase wurtzite ZnO nanoparticles. • Two morphological C-doped ZnO nanoparticles of different grain sizes. • The room temperature ferromagnetism. • An abnormal metamagnetic transition at magnetic field H = 19.2 kOe. • Two different Curie points (T{sub C}) at 500–600 °C.

  16. Microstructural and optical properties of Ca and Cr doped cobalt ferrite nanoparticles synthesized by auto combustion

    Science.gov (United States)

    Agrawal, Shraddha; Parveen, Azra; Azam, Ameer

    2018-05-01

    The Ca and Cr doped cobalt ferrite nanoparticles (Co0.8Ca0.2) (Fe0.8 Cr0.2)2O4 were synthesized by auto combustion method. Microstructural studies were carried out by X-ray diffraction (XRD). The crystalline size of synthesized nanoparticles as determined by the XRD was found to be 17.6 nm. These structural studies suggest that the crystal system remains spinal even with the doping of calcium and chromium. Optical properties of Ca and Cr doped cobalt ferrite were studied by UV-visible technique in the range of 200-800 nm. The energy band gap was calculated with the help of Tauc relationship. Ca and Cr doped cobalt ferrite annealed at 600°C exhibit significant dispersion in complex permeability. The dielectric constant and dielectric loss of cobalt ferrite were studied as a function of frequency and were explained on the basis of Koop's theory based on Maxwell Wagner two layer models and electron hopping.

  17. Crystal and electronic structure study of Mn doped wurtzite ZnO nanoparticles

    Directory of Open Access Journals (Sweden)

    O.M. Ozkendir

    2016-08-01

    Full Text Available The change in the crystal and electronic structure properties of wurtzite ZnO nanoparticles was studied according to Mn doping in the powder samples. The investigations were conducted by X-ray Absorption Fine Structure Spectroscopy (XAFS technique for the samples prepared with different heating and doping processes. Electronic analysis was carried out by the collected data from the X-ray Absorption Near-Edge Structure Spectroscopy (XANES measurements. Additional crystal structure properties were studied by Extended-XAFS (EXAFS analysis. Longer heating periods for the undoped wurtzite ZnO samples were determined to own stable crystal geometries. However, for some doped samples, the distortions in the crystal were observed as a result of the low doping amounts of Mn which was treated as an impurity. Besides, the changes in oxygen locations were determined to create defects and distortions in the samples.

  18. Optical properties of Mn doped ZnO films and wires synthesized by thermal oxidation of ZnMn alloy

    Energy Technology Data Exchange (ETDEWEB)

    Sima, M., E-mail: msima@infim.ro [National Institute of Materials Physics, 105bis Atomistilor Street, 077125 Magurele (Romania); Mihut, L. [National Institute of Materials Physics, 105bis Atomistilor Street, 077125 Magurele (Romania); Vasile, E. [University “Politehnica”of Bucharest, Faculty of Applied Chemistry and Material Science, Department of Oxide Materials and Nanomaterials, No. 1-7 Gh. Polizu Street, 011061 Bucharest (Romania); Sima, Ma.; Logofatu, C. [National Institute of Materials Physics, 105bis Atomistilor Street, 077125 Magurele (Romania)

    2015-09-01

    Mn doped ZnO films and wires, having different manganese concentrations were synthesized by thermal oxidation of the corresponding ZnMn alloy films and wires electrodeposited on a gold substrate. Structural and optical properties were addressed with scanning electron microscopy, X-ray diffraction (XRD), Raman scattering and photoluminescence (PL). To estimate the manganese concentration in Mn doped ZnO films, X-ray photoelectron spectroscopy was used. XRD patterns indicate that the incorporation of Mn{sup 2+} ions into the Zn{sup 2+} site of ZnO lattice takes place. Quenching of the ZnO PL appears due to Mn{sup 2+} ions in the ZnO lattice. Moreover, a significant decrease in the green emission of ZnO is reported in the case of the Mn doped ZnO wire array with a Mn concentration of 1.45%. The wurtzite ZnO has a total of 12 phonon modes, namely, one longitudinal acoustic (LA), two transverse acoustic (TA), three longitudinal optical (LO), and six transverse optical branches. Compared to the undoped ZnO, a gradual up-shift of the Raman lines assigned to the 2LA and A{sub 1} (LO) vibrational modes, from 482 and 567 cm{sup −1} to 532 and 580 cm{sup −1}, respectively, takes place for the Mn doped ZnO films having a Mn concentration between 2 and 15%. Additionally, in the case of the Mn doped ZnO films with 7 and 15% Mn concentration, Raman spectra show the appearance and increase in the relative intensity of the ZnO Raman line assigned to the TA + LO vibrational mode in the 600–750 cm{sup −1} spectral range. For the Mn-doped ZnO wires, the presence of the Raman line peaking at 527 cm{sup −1} confirms the insertion of Mn{sup 2+} ions in ZnO lattice. - Highlights: • Mn doped ZnO films and wires grown by thermal oxidation of ZnMn alloy • Incorporation of Mn{sup 2+} ions into Zn{sup 2+} site of ZnO lattice • Appearance of a strong Raman line in the spectral range 600–800 cm{sup −1} at high Mn concentration • Compensation of the oxygen vacancy at higher

  19. Optical properties of Mn doped ZnO films and wires synthesized by thermal oxidation of ZnMn alloy

    International Nuclear Information System (INIS)

    Sima, M.; Mihut, L.; Vasile, E.; Sima, Ma.; Logofatu, C.

    2015-01-01

    Mn doped ZnO films and wires, having different manganese concentrations were synthesized by thermal oxidation of the corresponding ZnMn alloy films and wires electrodeposited on a gold substrate. Structural and optical properties were addressed with scanning electron microscopy, X-ray diffraction (XRD), Raman scattering and photoluminescence (PL). To estimate the manganese concentration in Mn doped ZnO films, X-ray photoelectron spectroscopy was used. XRD patterns indicate that the incorporation of Mn 2+ ions into the Zn 2+ site of ZnO lattice takes place. Quenching of the ZnO PL appears due to Mn 2+ ions in the ZnO lattice. Moreover, a significant decrease in the green emission of ZnO is reported in the case of the Mn doped ZnO wire array with a Mn concentration of 1.45%. The wurtzite ZnO has a total of 12 phonon modes, namely, one longitudinal acoustic (LA), two transverse acoustic (TA), three longitudinal optical (LO), and six transverse optical branches. Compared to the undoped ZnO, a gradual up-shift of the Raman lines assigned to the 2LA and A 1 (LO) vibrational modes, from 482 and 567 cm −1 to 532 and 580 cm −1 , respectively, takes place for the Mn doped ZnO films having a Mn concentration between 2 and 15%. Additionally, in the case of the Mn doped ZnO films with 7 and 15% Mn concentration, Raman spectra show the appearance and increase in the relative intensity of the ZnO Raman line assigned to the TA + LO vibrational mode in the 600–750 cm −1 spectral range. For the Mn-doped ZnO wires, the presence of the Raman line peaking at 527 cm −1 confirms the insertion of Mn 2+ ions in ZnO lattice. - Highlights: • Mn doped ZnO films and wires grown by thermal oxidation of ZnMn alloy • Incorporation of Mn 2+ ions into Zn 2+ site of ZnO lattice • Appearance of a strong Raman line in the spectral range 600–800 cm −1 at high Mn concentration • Compensation of the oxygen vacancy at higher Mn concentration in ZnO lattice

  20. Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

    International Nuclear Information System (INIS)

    Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon; Fu, Dejun; Yoon, Hyungdo

    2011-01-01

    The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

  1. Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon [Dongguk University-Seoul, Seoul (Korea, Republic of); Fu, Dejun [Wuhan University, Wuhan (China); Yoon, Hyungdo [Korea Electronics Technology Institute, Seongnam (Korea, Republic of)

    2011-10-15

    The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

  2. Photoelectrochemical performance of N-doped ZnO branched nanowire photoanodes

    Directory of Open Access Journals (Sweden)

    Shrok Allami

    2017-10-01

    Full Text Available A ZnO branched-nanowire (BNW photoanode was doped with N for use in a photoelectrochemical cell (PEC to generate H2 from water splitting. First, ZnO BNWs were synthesized by chemical bath deposition method. Two experimental methods were used for N-doping: the time-controlled direct-current glow discharge plasma (DCGDP and the DC magnetron plasma (DCMP methods, to optimize N-doping of the NW structure. X-ray photoelectron spectroscopy (XPS provided the N distribution and atomic percentage in the BNWs. The XPS results confirmed that N distribution into ZnO BNWs occurred by N substitution of O sites in the ZnO structure and through well-screened molecular N2. The morphologies and structures of the fabricated nanostructures were investigated by field-emission scanning electron microscopy and X-ray diffraction respectively. The photoanode performance was demonstrated in photoelectrochemical studies at various power densities under both dark and illuminated conditions. Increasing the N amount in the ZnO BNWs increased the photocurrent in the PEC. Keywords: Engineering, Condensed matter physics, Nanotechnology, Materials science

  3. Synthesis and characterization of Mg-doped ZnO hollow spheres

    International Nuclear Information System (INIS)

    Hammad, Talaat M.; Salem, Jamil K.

    2011-01-01

    Mg-doped ZnO nanoparticles were synthesized by a simple chemical method at low temperature with Mg:Zn atomic ratio from 0 to 7%. The synthesis process is based on the hydrolysis of zinc acetate dihydrate and magnesium acetate tetrahydrate were heated under refluxing at 65 °C using methanol as a solvent. X-ray diffraction analysis reveals that the Mg-doped ZnO crystallizes in a wurtzite structure with crystal size of 5–12 nm. These nanocrystals self-aggregated themselves into hollow spheres of size of 800–1100 nm. High resolution transmission electron microscopy images show that each sphere is made up of numerous nanoparticles of average diameter 5–11 nm. The XRD patterns, SEM and TEM micrographs of doping of Mg in ZnO confirmed the formation of hollow spheres indicating that the Mg 2+ is successfully substituted into the ZnO host structure of the Zn 2+ site. Furthermore, the UV–Vis spectra and photoluminescence (PL) spectra of the ZnO nanoparticles were also investigated. The band gap of the nanoparticles can be tuned in the range of 3.36–3.55 eV by the use of the dopants.

  4. Efficient acetone sensor based on Ni-doped ZnO nanostructures prepared by spray pyrolysis technique

    Science.gov (United States)

    Darunkar, Swapnil S.; Acharya, Smita A.

    2018-05-01

    Ni-doped ZnO thin film was prepared by home-built spray pyrolysis unit for the detection of acetone at 300°C. Scanning electron microscopic (SEM) images of as-developed thin film of undoped ZnO exhibits large quantity of spherical, non-agglomerated particles with uniform size while in Ni-doped ZnO, particles are quite non-uniform in nature. The particle size estimated by using image J are obtained to be around 20-200 nm. Ni-doping effect on band gaps are determined by UV-vis optical spectroscopy and band gap of Ni-doped ZnO is found to be 3.046 eV. Nickel doping exceptionally enhances the sensing response of ZnO as compared to undoped ZnO system. The major role of the Ni-doping is to create more active sites for chemisorbed oxygen on the surface of sensor and correspondingly, to improve the sensing response. The 6 at.% of Ni-doped ZnO exhibits the highest response (92%) for 100 ppm acetone at 300 °C.

  5. Enhanced photovoltaic performance of ZnO nanorod-based dye-sensitized solar cells by using Ga doped ZnO seed layer

    Energy Technology Data Exchange (ETDEWEB)

    Dou, Yuanyao [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Wu, Fang, E-mail: fang01234@163.com [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Mao, Caiying [Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Fang, Liang, E-mail: lfang@cqu.edu.cn [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Guo, Shengchun [Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Zhou, Miao [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China)

    2015-06-05

    Highlights: • ZnO nanorods were grown on Ga-doped ZnO seed layers using hydrothermal method. • Using the ZnO nanorods as photoanodes for fabricated dye-sensitized solar cells. • The highest η of 1.23% can be achieved in a DSSC with 3 at.% Ga-doped in seeds. • The effects of ZnO seed layers on electron transport properties were investigated. • The enhancement performance of DSSCs contributed to higher dye loading and η{sub cc}. - Abstract: Zinc oxide (ZnO) nanorod arrays were grown on FTO substrates with a Ga-doped ZnO (GZO) seed layer by a hydrothermal method. GZO seed layers were obtained via sol–gel technology with Ga concentration in the range of 0–4 at.%. The dye sensitized solar cells (DSSCs) using ZnO nanorod arrays as the photoanode layers were prepared. The effect of Ga dopant concentrations in ZnO seed layer on the morphology features of ZnO nanorod arrays and the performance of DSSCs were systematically investigated. Results indicate that the average diameter and density of ZnO nanorod arrays decrease with increasing Ga concentration, but their length shows an opposite trend. The photocurrent density–voltage (J–V) characteristics reveal that the DSSCs with GZO seed layer exhibit significantly improved photovoltaic performance. In particular, the highest energy conversion efficiency (η) of 1.23% can be achieved in a DSSC with 3 at.% Ga doping, which is increased by 86.36% compared with that of the undoped DSSC. The external quantum efficiency (EQE) spectra and electrochemical impedance spectroscopy (EIS) were employed to explore the photon-to-electron conversion process in DSSCs. It is demonstrated that the performance enhancement of DSSCs based on GZO seed layer can be attributed to higher amount of dye loading, more efficient electron transportation and better electrons collection efficiency.

  6. Quenching of surface traps in Mn doped ZnO thin films for enhanced optical transparency

    International Nuclear Information System (INIS)

    Ilyas, Usman; Rawat, R.S.; Roshan, G.; Tan, T.L.; Lee, P.; Springham, S.V.; Zhang, Sam; Fengji Li; Chen, R.; Sun, H.D.

    2011-01-01

    The structural and photoluminescence analyses were performed on un-doped and Mn doped ZnO thin films grown on Si (1 0 0) substrate by pulsed laser deposition (PLD) and annealed at different post-deposition temperatures (500-800 deg. C). X-ray diffraction (XRD), employed to study the structural properties, showed an improved crystallinity at elevated temperatures with a consistent decrease in the lattice parameter 'c'. The peak broadening in XRD spectra and the presence of Mn 2p3/2 peak at ∼640 eV in X-ray Photoelectron Spectroscopic (XPS) spectra of the doped thin films confirmed the successful incorporation of Mn in ZnO host matrix. Extended near band edge emission (NBE) spectra indicated the reduction in the concentration of the intrinsic surface traps in comparison to the doped ones resulting in improved optical transparency. Reduced deep level emission (DLE) spectra in doped thin films with declined PL ratio validated the quenching of the intrinsic surface traps thereby improving the optical transparency and the band gap, essential for optoelectronic and spintronic applications. Furthermore, the formation and uniform distribution of nano-sized grains with improved surface features of Mn-doped ZnO thin films were observed in Field Emission Scanning Electron Microscopy (FESEM) images.

  7. Fast Response and High Sensitivity of ZnO Nanowires-Cobalt Phthalocyanine Heterojunction Based H2S Sensor.

    Science.gov (United States)

    Kumar, Ashwini; Samanta, Soumen; Singh, Ajay; Roy, Mainak; Singh, Surendra; Basu, Saibal; Chehimi, Mohmad M; Roy, Kallol; Ramgir, Niranjan; Navaneethan, M; Hayakawa, Y; Debnath, Anil K; Aswal, Dinesh K; Gupta, Shiv K

    2015-08-19

    The room temperature chemiresistive response of n-type ZnO nanowire (ZnO NWs) films modified with different thicknesses of p-type cobalt phthalocyanine (CoPc) has been studied. With increasing thickness of CoPc (>15 nm), heterojunction films exhibit a transition from n- to p-type conduction due to uniform coating of CoPc on ZnO. The heterojunction films prepared with a 25 nm thick CoPc layer exhibit the highest response (268% at 10 ppm of H2S) and the fastest response (26 s) among all samples. The X-ray photoelectron spectroscopy and work function measurements reveal that electron transfer takes place from ZnO to CoPc, resulting in formation of a p-n junction with a barrier height of 0.4 eV and a depletion layer width of ∼8.9 nm. The detailed XPS analysis suggests that these heterojunction films with 25 nm thick CoPc exhibit the least content of chemisorbed oxygen, enabling the direct interaction of H2S with the CoPc molecule, and therefore exhibit the fastest response. The improved response is attributed to the high susceptibility of the p-n junctions to the H2S gas, which manipulates the depletion layer width and controls the charge transport.

  8. Enhanced luminescence in Eu-doped ZnO nanocrystalline films

    Energy Technology Data Exchange (ETDEWEB)

    Suzuki, Keigo, E-mail: ksuzuki@murata.com; Murayama, Koji; Tanaka, Nobuhiko [Murata Manufacturing Co., Ltd., 10-1, Higashikotari 1-chome, Nagaokakyo, Kyoto 617-8555 (Japan)

    2015-07-20

    We found an enhancement of Eu{sup 3+} emissions in Eu-doped ZnO nanocrystalline films fabricated by microemulsion method. The Eu{sup 3+} emission intensities were increased by reducing annealing temperatures from 633 K to 533 K. One possible explanation for this phenomenon is that the size reduction enhances the energy transfer from ZnO nanoparticles to Eu{sup 3+} ions. Also, the shift of the charge-transfer band into the low-energy side of the absorption edge is found to be crucial, which seems to expedite the energy transfer from O atoms to Eu{sup 3+} ions. These findings will be useful for the material design of Eu-doped ZnO phosphors.

  9. Thermal growth and cathodoluminescence of Bi doped ZnO nanowires and rods

    International Nuclear Information System (INIS)

    Aleman, B; Hidalgo, P; Fernandez, P; Piqueras, J

    2009-01-01

    Bi doped ZnO nanowires and rods have been grown by a catalyst free evaporation-deposition method with precursors containing either ZnO and Bi 2 O 3 or ZnS and Bi 2 O 3 powders. The use of ZnS as a precursor was found to lead to a higher density of nano- and microstructures at lower temperatures than by using ZnO. Energy dispersive x-ray spectroscopy (EDS) shows that the Bi content in the wires and rods is in the range 0.15-0.35 at%. Bi incorporation was found to induce a red shift of the near band gap luminescence but no quantitative correlation between the shift and the amount of Bi, as measured by EDS, was observed. The I-V curves of single Bi doped wires had linear behaviour at low current and non-linear behaviour for high currents, qualitatively similar to that of undoped wires.

  10. Influence of Sc doping concentration on electronic structure and optical properties of ZnO

    International Nuclear Information System (INIS)

    Wu Yuxi; Zhang Hao; Han Long; Qu Licheng; Gu Shulin; Li Teng

    2011-01-01

    In this paper, we adopt the density functional theory (DFT) plane wave pseudopotential method to study the crystal structure, electronic structure and optical property for the different concentrations of Sc doped ZnO system. We optimize the structure of Sc and get the basis of numerical simulation. The results show that with the adoption of Sc, the lattice constants of the system increase gradually, the energy of the system becomes larger, the Fermi level enters into the conduction band, the system shows Metallic gradually and the band gap becomes wider. On the other hand, certain changes of the optical properties of doped ZnO have taken place, i. e., a new absorption peak happens in ZnO absorption spectrum and the blue shift of absorption edge with the new peak occurs in the imagery part of dielectric function. (authors)

  11. Relative Humidity Sensing Properties Of Cu2O Doped ZnO Nanocomposite

    International Nuclear Information System (INIS)

    Pandey, N. K.; Tiwari, K.; Tripathi, A.; Roy, A.; Rai, A.; Awasthi, P.

    2009-01-01

    In this paper we report application of Cu 2 O doped ZnO composite prepared by solid state reaction route as humidity sensor. Pellet samples of ZnO-Cu 2 O nanocrystalline powders with 2, 5 and 10 weight% of Cu 2 O in ZnO have been prepared. Pellets have been annealed at temperatures of 200-500 deg. C and exposed to humidity. It is observed that as relative humidity increases, resistance of the pellet decreases for the humidity from 10% to 90%. Sample with 5% of Cu 2 O doped in ZnO and annealed at 500 deg. C shows best results with sensitivity of 1.50 MΩ/%RH. In this case the hysteresis is low and the reproducibility high, making it the suitable candidate for humidity sensing.

  12. Scintillation characteristic of In, Ga-doped ZnO thin films with different dopant concentrations

    International Nuclear Information System (INIS)

    Fujimoto, Yutaka; Yanagida, Takayuki; Yokota, Yuui; Chani, Valery; Yoshikawa, Akira; Sekiwa, Hideyuki

    2011-01-01

    The present study describes the first detailed evaluation of the rise and the decay time of scintillation phenomenon in In 3+ - and Ga 3+ -doped ZnO thin films with different dopant concentrations. In 3+ -(25, 55, and 141 ppm) and Ga 3+ -(33, 67, 333, and 1374 ppm) doped ZnO films were grown by the Liquid Phase Epitaxy (LPE) method. The characterization was performed using the pulse X-ray equipped streak camera system. Both the rise and the decay times were shortened considerably with increasing content of In 3+ and Ga 3+ in the films. However, the scintillation light yield under 241 Am α-ray excitation reduced when concentration of In 3+ and Ga 3+ in the ZnO films was high. (author)

  13. Red luminescence from hydrothermally synthesized Eu-doped ZnO ...

    Indian Academy of Sciences (India)

    Administrator

    turally characterized by X-ray diffraction, transmission electron microscopy ... II–VI compound semiconductor with large exciton binding .... ions occupy a site with inversion symmetry and 617 nm ... TEM image of Eu-doped ZnO nanoparticles with (a) 1⋅2 at. .... Jacquier B, Lebrasseur E, Guy S, Belarouci A and Menchini F.

  14. Structural, chemical and magnetic properties of secondary phases in Co-doped ZnO

    DEFF Research Database (Denmark)

    Ney, A; Kovács, András; Ney, V

    2011-01-01

    , chemical and magnetic properties of Co-doped ZnO samples. It can be established on a quantitative basis that the superparamagnetic (SPM) behavior observed by integral superconducting quantum interference device magnetometry is not an intrinsic property of the material but stems from precipitations...

  15. Doping effect on the optical properties of ZnO nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Stoehr, M. [Frederick Seitz Materials Research Laboratory, University of Illinois,104 South Goodwin Avenue, Urbana, IL 61801 (United States); Institut Universitaire de Technologie, Universite de Haute Alsace, 61 rue Albert Camus, 68093 Mulhouse Cedex (France); Juillaguet, S. [Groupe d' Etude des Semi-conducteurs, Universite Montpellier II, Place Eugene Bataillon, 34095 Montpellier Cedex 5 (France); Kyaw, T.M.; Wen, J.G. [Institut Universitaire de Technologie, Universite de Haute Alsace, 61 rue Albert Camus, 68093 Mulhouse Cedex (France)

    2007-04-15

    High quality undoped and Ga{sub 2}O{sub 3} or In{sub 2}O{sub 3} doped ZnO nanostructures are grown by chemical vapor transport and condensation. The doping effect on the optical properties is investigated by photoluminescence. At room temperature, photoluminescence on Ga{sub 2}O{sub 3} doped ZnO nanostructures reveals an enhancement of the ultraviolet near band edge emission at 390 nm, while the intensity of the deep level emission at 530 nm weakens. At 5 K, an intense neutral-donor-bound exciton (D{sup 0}X) line dominates the undoped and doped ZnO photoluminescence spectra. The presence of well resolved two-electron satellite lines allow to determine the type of donors. At 5 K, the results indicate that ZnO nanostructures grown with 10% of Ga{sub 2}O{sub 3} display an excellent optical quality, proved by an intense D{sup 0}X line, a high intensity ratio between the D{sup 0}X line and the deep level emission as well as the presence of numerous phonon replicas of the main lines. (copyright 2007 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  16. Shape tunable synthesis of Eu- and Sm-doped ZnO microstructures ...

    Indian Academy of Sciences (India)

    Shape tunable synthesis of Eu- and Sm-doped ZnO microstructures: a morphological ... different microstructures material at relatively low temper- ..... Chem. C 114. 2776. 5. Gao P X and Wang Z L 2003 J. Am. Chem. Soc. 125 11299. 6.

  17. Boron-doped MnTe semiconductor-sensitized ZnO solar cells

    Indian Academy of Sciences (India)

    Administrator

    The B-doped MnTe semiconductor was grown on ZnO using two stages of the ... nanoparticles (NPs), i.e. MnTe and MnTe2 were observed with a diameter range of approximately ..... Kongkanand A, Tvrdy K, Takechi K, Kuno M and Kamat P.

  18. Properties of Nb-doped ZnO transparent conductive thin films ...

    Indian Academy of Sciences (India)

    Administrator

    by rf magnetron sputtering using a high quality ceramic target ... Guangxi Key Laboratory of Information Materials, Guilin University of Electronic ... films are highly textured along the c axis and perpendicular to the surface of the substrate. ... ZnO films; Nb-doped; magnetron sputtering; optical and electrical properties. 1.

  19. Study on Crystallographic Properties of Li Doped ZnO Thin Films

    International Nuclear Information System (INIS)

    Khine Khine Linn; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

    2008-03-01

    Li-doped ZnO film is prepared on highly polished Si substrate. The process temperature are range from 400 0 C to 600 0 C and maintained 1 hr for homogenization. According to the experimental results, it is significant that the growth chemistry is quite feasible and expected to be crystalline at above-mentioned temperatures.

  20. Pulsed laser deposition of aluminum-doped ZnO films at 355 nm

    DEFF Research Database (Denmark)

    Holmelund, E.; Schou, Jørgen; Thestrup Nielsen, Birgitte

    2004-01-01

    Conducting, transparent films of aluminium-doped ZnO (AZO) have been produced at the laser wavelength 355 nm. The most critical property, the electric resistivity, is up to a factor of 8 above that for films produced at shorter wavelengths. In contrast, the transmission of visible light through...

  1. Preparation of cadmium-doped ZnO thin films by SILAR and their ...

    Indian Academy of Sciences (India)

    Cadmium-doped zinc oxide (Cd : ZnO) thin films were deposited from sodium zincate bath .... of complex ion on the substrate followed by reaction of the .... Intensity (a.u.). 0. 500 .... trum confirmed the presence of Zn, O and Cd elements in the.

  2. Solvothermal synthesis of nanorods of ZnO, N-doped ZnO and CdO

    International Nuclear Information System (INIS)

    Varghese, Neenu; Panchakarla, L.S.; Hanapi, M.; Govindaraj, A.; Rao, C.N.R.

    2007-01-01

    ZnO nanorods with diameters in the 80-800 nm range are readily synthesized by the reaction of zinc acetate, ethanol and ethylenediamine under solvothermal conditions. The best products are obtained at 330 deg. C with a slow heating rate. Addition of the surfactant Triton -X 100 gave nanorods of uniform (300 nm) diameter. By adding a small amount of liquid NH 3 to the reaction mixture, N-doped ZnO nanorods, with distinct spectroscopic features are obtained. CdO nanorods of 80 nm diameter have been prepared under solvothermal conditions using a mixture of cadmium cupferronate, ethylenediamine and ethanol at 330 deg. C. Similarly, Zn 1-x Cd x O nanorods of a 70 nm diameter are obtained under solvothermal conditions starting with a mixture of zinc acetate, cadmium cupferronate, ethanol and ethylenediamine

  3. Cobalt Oxide on N-Doped Carbon for 1-Butene Oligomerization to Produce Linear Octenes

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Dongting [Department; Xu, Zhuoran [Department; Chada, Joseph P. [Department; Carrero, Carlos A. [Department; Rosenfeld, Devon C. [The Dow Chemical Company, 2301 N. Brazosport Boulevard, Freeport, Texas 77541-3257, United States; Rogers, Jessica L. [The Dow Chemical Company, 2301 N. Brazosport Boulevard, Freeport, Texas 77541-3257, United States; Hermans, Ive [Department; Huber, George W. [Department

    2017-10-02

    Cobalt oxide supported on N-doped carbon catalysts were investigated for 1-butene oligomerization. The materials were synthesized by treating activated carbon with nitric acid and subsequently with NH3 at 200, 400, 600, and 800 °C, followed by impregnation with cobalt. The 1-butene oligomerization selectivity increased with ammonia treatment temperature of the carbon support. The oligomerization selectivity of cobalt oxide on N-doped carbon synthesized at 800 °C (800A-CoOx/N-C) is 2.6 times higher than previously reported cobalt oxide on N-doped carbon synthesized with NH4OH (2A-CoOx/N-C). Over 70% of the butene dimers were linear C8 olefins for all catalysts. The oligomerization selectivity increased with 1-butene conversion. The catalysts were characterized by elemental analysis, N2 adsorption, X-ray diffraction (XRD), X-ray absorption spectroscopy (XAS), and X-ray photoelectron spectroscopy (XPS). The nitrogen content of the catalysts increases with ammonia treatment temperature as confirmed by elemental analysis. The surface content of pyridinic nitrogen with a binding energy of 398.4 ± 0.1 eV increased with ammonia treatment temperature as evidenced by deconvolution of N 1s XPS spectra.

  4. Enhanced piezoelectric output voltage and Ohmic behavior in Cr-doped ZnO nanorods

    International Nuclear Information System (INIS)

    Sinha, Nidhi; Ray, Geeta; Godara, Sanjay; Gupta, Manoj K.; Kumar, Binay

    2014-01-01

    Highlights: • Low cost highly crystalline Cr-doped ZnO nanorods were synthesized. • Enhancement in dielectric, piezoelectric and ferroelectric properties were observed. • A high output voltage was obtained in AFM. • Cr-doping resulted in enhanced conductivity and better Ohmic behavior in ZnO/Ag contact. - Abstract: Highly crystalline Cr-doped ZnO nanorods (NRs) were synthesized by solution technique. The size distribution was analyzed by high resolution tunneling electron microscope (HRTEM) and particle size analyzer. In atomic force microscope (AFM) studies, peak to peak 8 mV output voltage was obtained on the application of constant normal force of 25 nN. It showed high dielectric constant (980) with phase transition at 69 °C. Polarization vs. electric field (P–E) loops with remnant polarization (6.18 μC/cm 2 ) and coercive field (0.96 kV/cm) were obtained. In I–V studies, Cr-doping was found to reduce the rectifying behavior in the Ag/ZnO Schottky contact which is useful for field effect transistor (FET) and solar cell applications. With these excellent properties, Cr-doped ZnO NRs can be used in nanopiezoelectronics, charge storage and ferroelectric applications

  5. Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Yadav, Harish Kumar [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Sreenivas, K [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Katiyar, R S [Department of Physics, University of Puerto Rico, San Juan, PR 00931-3343 (Puerto Rico); Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)

    2007-10-07

    We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm{sup -1}. The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A{sub 1} (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries.

  6. Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

    International Nuclear Information System (INIS)

    Yadav, Harish Kumar; Sreenivas, K; Katiyar, R S; Gupta, Vinay

    2007-01-01

    We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm -1 . The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A 1 (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries

  7. Cobalt

    Science.gov (United States)

    Slack, John F.; Kimball, Bryn E.; Shedd, Kim B.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Cobalt is a silvery gray metal that has diverse uses based on certain key properties, including ferromagnetism, hardness and wear-resistance when alloyed with other metals, low thermal and electrical conductivity, high melting point, multiple valences, and production of intense blue colors when combined with silica. Cobalt is used mostly in cathodes in rechargeable batteries and in superalloys for turbine engines in jet aircraft. Annual global cobalt consumption was approximately 75,000 metric tons in 2011; China, Japan, and the United States (in order of consumption amount) were the top three cobalt-consuming countries. In 2011, approximately 109,000 metric tons of recoverable cobalt was produced in ores, concentrates, and intermediate products from cobalt, copper, nickel, platinum-group-element (PGE), and zinc operations. The Democratic Republic of the Congo (Congo [Kinshasa]) was the principal source of mined cobalt globally (55 percent). The United States produced a negligible amount of byproduct cobalt as an intermediate product from a PGE mining and refining operation in southeastern Montana; no U.S. production was from mines in which cobalt was the principal commodity. China was the leading refiner of cobalt, and much of its production came from cobalt ores, concentrates, and partially refined materials imported from Congo (Kinshasa).The mineralogy of cobalt deposits is diverse and includes both primary (hypogene) and secondary (supergene) phases. Principal terrestrial (land-based) deposit types, which represent most of world’s cobalt mine production, include primary magmatic Ni-Cu(-Co-PGE) sulfides, primary and secondary stratiform sediment-hosted Cu-Co sulfides and oxides, and secondary Ni-Co laterites. Seven additional terrestrial deposit types are described in this chapter. The total terrestrial cobalt resource (reserves plus other resources) plus past production, where available, is calculated to be 25.5 million metric tons. Additional resources of

  8. The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

    KAUST Repository

    Venkatesh, S.

    2016-03-24

    We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaronpercolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

  9. The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Venkatesh, S.; Baras, A.; Roqan, I. S., E-mail: Iman.roqan@kaust.edu.sa [Physical Sciences and Engineering Division, King Abdullah University of Science and Technology (KAUST), Thuwal 23955-6900 (Saudi Arabia); Lee, J.-S. [Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, Menlo Park, California 94025 (United States)

    2016-03-15

    We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaron percolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

  10. Mn doping in ZnO nanoparticles: effects investigated by positron lifetime and Doppler broadening studies

    Energy Technology Data Exchange (ETDEWEB)

    Roy, B.; Karmakar, B.; Pal, M. [Department of Physics, University of Burdwan, Golapbag, Burdwan (India); Nambissan, P.M.G. [Saha Institute of Nuclear Physics, Kolkata (India)

    2009-11-15

    Positron lifetime and Doppler broadening measurements in nanocrystalline zinc oxide (ZnO) indicated the negatively charged trivacancy-type defects V{sub Zn+O+Zn} as the predominant positron trapping sites within the nanocrystallites. They got converted to neutral divacancies (V{sub Zn+O}) on doping with manganese (Mn). Further doping resulted in the reduction of the size of the nanocrystallites. At still increased doping concentrations, a new phase ZnMn{sub 2}O{sub 4} was formed. It had a normal spinel structure with positron trapping centers at some of the tetrahedral and octahedral sites. X-ray diffraction and transmission electron micro-scopy studies confirmed these findings. (copyright 2009 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  11. Antibacterial properties of F-doped ZnO visible light photocatalyst

    Energy Technology Data Exchange (ETDEWEB)

    Podporska-Carroll, Joanna, E-mail: joannapcarroll@gmail.com [Center for Research in Engineering Surface Technology (CREST), DIT FOCAS Institute, Kevin St., Dublin (Ireland); Myles, Adam [Center for Research in Engineering Surface Technology (CREST), DIT FOCAS Institute, Kevin St., Dublin (Ireland); School of Chemical and Pharmaceutical Sciences, Dublin Institute of Technology, Kevin St., Dublin (Ireland); Quilty, Brid [School of Biotechnology, Dublin City University, Dublin (Ireland); McCormack, Declan E.; Fagan, Rachel [Center for Research in Engineering Surface Technology (CREST), DIT FOCAS Institute, Kevin St., Dublin (Ireland); School of Chemical and Pharmaceutical Sciences, Dublin Institute of Technology, Kevin St., Dublin (Ireland); Hinder, Steven J. [The Surface Analysis Laboratory, Faculty of Engineering and Physical Sciences, University of Surrey, Guildford, Surrey GU2 7XH (United Kingdom); Dionysiou, Dionysios D., E-mail: dionysios.d.dionysiou@uc.edu [Environmental Engineering and Science Program, Department of Biomedical, Chemical and Environmental Engineering (DBCEE), 705 Engineering Research Center, University of Cincinnati, Cincinnati, OH 45221-0012 (United States); Pillai, Suresh C., E-mail: Pillai.Suresh@itsligo.ie [Center for Research in Engineering Surface Technology (CREST), DIT FOCAS Institute, Kevin St., Dublin (Ireland); Nanotechnology Research Group, Department of Environmental Science, PEM Centre, Institute of Technology Sligo, Sligo (Ireland)

    2017-02-15

    Highlights: • F doped ZnO nano-powders were obtained by a modified sol–gel method. • These materials were found to be effective against S. aureus and E. coli. • Enhanced visible light photocatalytic and antimicrobial properties were obtained. • The toxic effect of ZnO on bacteria can be due to the release of zinc cations. • Production of reactive oxidation species influences bacterial viability. - Abstract: Nanocrystalline ZnO photocatalysts were prepared by a sol–gel method and modified with fluorine to improve their photocatalytic anti-bacterial activity in visible light. Pathogenic bacteria such as Escherichia coli (Gram-negative) and Staphylococcus aureus (Gram-positive) were employed to evaluate the antimicrobial properties of synthesized materials. The interaction with biological systems was assessed by analysis of the antibacterial properties of bacteria suspended in 2% (w/w) powder solutions. The F-doping was found to be effective against S. aureus (99.99% antibacterial activity) and E. coli (99.87% antibacterial activity) when irradiated with visible light. Production of reactive oxygen species is one of the major factors that negatively impact bacterial growth. In addition, the nanosize of the ZnO particles can also be toxic to microorganisms. The small size and high surface-to-volume ratio of the ZnO nanoparticles are believed to play a role in enhancing antimicrobial activity.

  12. Evaluation of gas-sensing properties of ZnO nanostructures electrochemically doped with Au nanophases

    Directory of Open Access Journals (Sweden)

    Elena Dilonardo

    2016-01-01

    Full Text Available A one-step electrochemical method based on sacrificial anode electrolysis (SAE was used to deposit stabilized gold nanoparticles (Au NPs directly on the surface of nanostructured ZnO powders, previously synthesized through a sol–gel process. The effect of thermal annealing temperatures (300 and 550 °C on chemical, morphological, and structural properties of pristine and Au-doped ZnO nancomposites (Au@ZnO was investigated. Transmission and scanning electron microscopy (TEM and SEM, as well as X-ray photoelectron spectroscopy (XPS, revealed the successful deposition of nanoscale gold on the surface of spherical and rod-like ZnO nanostructures, obtained after annealing at 300 and 550 °C, respectively. The pristine ZnO and Au@ZnO nanocomposites are proposed as active layer in chemiresistive gas sensors for low-cost processing. Gas-sensing measurements towards NO2 were collected at 300 °C, evaluating not only the Au-doping effect, but also the influence of the different ZnO nanostructures on the gas-sensing properties.

  13. Precipitated nickel doped ZnO nanoparticles with enhanced low temperature ethanol sensing properties

    Directory of Open Access Journals (Sweden)

    Umadevi Godavarti

    2017-12-01

    Full Text Available The Zn1-xNixO nanoparticles have been synthesized by novel co-precipitation method and systematically characterized by XRD, SEM, TEM and photo luminescence. The XRD patterns confirm the hexagonal wurzite structure without secondary phases in Ni substituted ZnO samples. SEM and TEM are used for the estimation of particle shape and size. In PL study there is a peak in the range of 380–390 nm in all samples that is attributed to the oxygen vacancies. Gas sensing tests reveal that Ni doped ZnO sensor has remarkably enhanced performance compared to pure ZnO detected at an optimum temperature 100 °C. It could detect ethanol gas in a wide concentration range with very high response, fast response–recovery time, good selectivity and stable repeatability. The possible sensing mechanism is discussed. The high response of ZnO Nanoparticles was attributed to large contacting surface area for electrons, oxygen, target gas molecule, and abundant channels for gas diffusion. The superior sensing features indicate the present Ni doped ZnO as a promising nanomaterial for gas sensors. The response time and recovery time of undoped is 75 s and 60 s and 0.25 at% Ni are found to be 60 s and 45 s at 100 °C respectively.

  14. Investigation on the effect of Zr doping in ZnO thin films by spray pyrolysis

    International Nuclear Information System (INIS)

    Gokulakrishnan, V.; Parthiban, S.; Jeganathan, K.; Ramamurthi, K.

    2011-01-01

    Zirconium doped zinc oxide thin films with enhanced optical transparency were prepared on Corning 1737 glass substrates at the substrate temperature of 400 o C by spray pyrolysis method for various doping concentrations of zirconium (IV) chloride in the spray solution. The X-ray diffraction studies reveal that the films exhibit hexagonal crystal structure with polycrystalline grains oriented along (0 0 2) direction. The crystalline quality of the films is found to be deteriorating with the increase of doping concentration and acquires amorphous state for higher concentration of 8 at.% in precursor solution. The average transmittance for 5 at.% (solution) zirconium doped ZnO film is significantly increased to ∼92% in the visible region of 500-800 nm. The room temperature photoluminescence (PL) spectra of films show a band edge between 3.41 and 3.2 eV and strong blue emission at 2.8 eV irrespective of doping concentration and however intensity increases consistently with doping levels. The vacuum annealing at 400 o C reduced the resistivity of the films significantly due to the coalescence of grains and the lowest resistivity of 2 x 10 -3 Ω cm is observed for 3 at.% (solution) Zr doped ZnO films which envisages that it is a good candidate for stable TCO material.

  15. Characteristics of hydrogen co-doped ZnO : Al thin films

    International Nuclear Information System (INIS)

    Lee, S H; Lee, T S; Lee, K S; Cheong, B; Kim, W M; Kim, Y D

    2008-01-01

    ZnO films co-doped with H and Al (HAZO) were prepared by sputtering ZnO targets containing 1 wt% Al 2 O 3 on Corning glass at a substrate temperature of 150 deg. C with Ar and H 2 /Ar gas mixtures. The effects of hydrogen addition to Al-doped ZnO (AZO) films with low Al content on the electrical, the optical and the structural properties of the as-grown films as well as the vacuum- and air-annealed films were examined. Secondary ion mass spectroscopy analysis showed that the hydrogen concentration increased with increasing H 2 in sputter gas. For the as-deposited films, the free carrier number increased with increasing H 2 . The Hall mobility increased at low hydrogen content, reaching a maximum before decreasing with a further increase of H 2 content in sputter gas. Annealing at 300 deg. C resulted in the removal of hydrogen, causing a decrease in the carrier concentration. It was shown that hydrogen might exist as single isolated interstitial hydrogen bound with oxygen, thereby acting like an anionic dopant. Also, it was shown that the addition of hydrogen to ZnO films doped with low metallic dopant concentration could yield transparent conducting films with very low absorption loss as well as with proper electrical properties, which is suitable for thin film solar cell applications

  16. Enhanced Photocatalytic Activity of Rare Earth Metal (Nd and Gd doped ZnO Nanostructures

    Directory of Open Access Journals (Sweden)

    P. Logamani

    2017-06-01

    Full Text Available Presence of harmful organic pollutants in wastewater effluents causes serious environmental problems and therefore purification of this contaminated water by a cost effective treatment method is one of the most important issue which is in urgent need of scientific research. One such promising treatment technique uses semiconductor photocatalyst for the reduction of recalcitrant pollutants in water. In the present work, rare earth metals (Nd and Gd doped ZnO nanostructured photocatalyst have been synthesized by wet chemical method. The prepared samples were characterized by X-ray diffraction (XRD, Field Emission Scanning Electron Microscopy (FESEM and energy dispersive X-ray spectroscopy (EDS. The XRD results showed that the prepared samples were well crystalline with hexagonal Wurtzite structure. The results of EDS revealed that rare earth elements were doped into ZnO structure. The effect of rare earth dopant on morphology and photocatalytic degradation properties of the prepared samples were studied and discussed. The results revealed that the rare earth metal doped ZnO samples showed enhanced visible light photocatalytic activity for the degradation of methylene blue dye than pure nano ZnO photocatalyst.

  17. Thermal process induced change of conductivity in As-doped ZnO

    Science.gov (United States)

    Su, S. C.; Fan, J. C.; Ling, C. C.

    2012-02-01

    Arsenic-doped ZnO films were fabricated by radio frequency magnetron sputtering method with different substrate temperature TS. Growing with the low substrate temperature of TS=200°C yielded n-type semi-insulating sample. Increasing the substrate temperature would yield p-type ZnO film and reproducible p-type film could be produced at TS~450°C. Post-growth annealing of the n-type As-doped ZnO sample grown at the low substrate temperature (TS=200°C) in air at 500°C also converted the film to p-type conductivity. Further increasing the post-growth annealing temperature would convert the p-type sample back to n-type. With the results obtained from the studies of positron annihilation spectroscopy (PAS), photoluminescence (PL), cathodoluminescence (CL), X-ray photoelectron spectroscopy (XPS), secondary ion mass spectroscopy (SIMS) and nuclear reaction analysis (NRA), we have proposed mechanisms to explain for the thermal process induced conduction type conversion as observed in the As-doped ZnO films.

  18. High-resolution photoluminescence spectroscopy of Sn-doped ZnO single crystals

    International Nuclear Information System (INIS)

    Kumar, E. Senthil; Mohammadbeigi, F.; Boatner, L.A.; Watkins, S.P.

    2016-01-01

    Group IV donors in ZnO are poorly understood, despite evidence that they are effective n-type dopants. Here we present high-resolution photoluminescence (PL) spectroscopy studies of unintentionally doped and Sn-doped ZnO single crystals grown by the chemical vapor transport method. Doped samples showed greatly increased emission from the I 10 bound exciton transition that was recently proven to be related to the incorporation of Sn impurities based on radio-isotope studies. The PL linewidths are exceptionally sharp for these samples, enabling a clear identification of several donor species. Temperature-dependent PL measurements of the I 10 line emission energy and intensity dependence reveal a behavior that is similar to other shallow donors in ZnO. Ionized donor bound-exciton and two-electron satellite transitions of the I 10 transition are unambiguously identified and yield a donor binding energy of 71 meV. In contrast to recent reports of Ge-related donors in ZnO, the spectroscopic binding energy for the Sn-related donor bound exciton follows a linear relationship with donor binding energy (Haynes rule) similar to recently observed carbon related donors, and confirming the shallow nature of this defect center, which was recently attributed to a Sn Zn double donor compensated by an unknown single acceptor.

  19. Room temperature ferromagnetism and gas sensing in ZnO nanostructures: Influence of intrinsic defects and Mn, Co, Cu doping

    Energy Technology Data Exchange (ETDEWEB)

    Mhlongo, Gugu H., E-mail: gmhlongo@csir.co.za [DST/CSIR National Centre for Nanostructured Materials, Council for Scientific and Industrial Research, Pretoria 0001 (South Africa); Shingange, Katekani; Tshabalala, Zamaswazi P.; Dhonge, Baban P. [DST/CSIR National Centre for Nanostructured Materials, Council for Scientific and Industrial Research, Pretoria 0001 (South Africa); Mahmoud, Fawzy A. [Solid State Physics Dept., National Research Centre, P.O. 12622, Dokki, Giza (Egypt); Mwakikunga, Bonex W.; Motaung, David E. [DST/CSIR National Centre for Nanostructured Materials, Council for Scientific and Industrial Research, Pretoria 0001 (South Africa)

    2016-12-30

    Highlights: • Preparation of Mn, Co, Cu doped ZnO via microwave-assisted method. • Doping alters the morphology of ZnO nanostructures. • Concentration of zinc and oxygen related defects vary with doping. • Correlation between PL and EPR was established. • Both undoped and doped ZnO nanostructures showed selectivity towards NH{sub 3}. - Abstract: Undoped and transition metal (Cu, Co and Mn) doped ZnO nanostructures were successfully prepared via a microwave-assisted hydrothermal method followed by annealing at 500 °C. Numerous characterization facilities such as X-ray powder diffraction (XRD), field emission scanning electron microscopy (FESEM), and high-resolution transmission electron microscopy (HRTEM) were employed to acquire the structural and morphological information of the prepared ZnO based products. Combination of defect structure analysis based on photoluminescence (PL) and electron paramagnetic resonance (EPR) indicated that co-existing oxygen vacancies (V{sub O}) and zinc interstitials (Zn{sub i}) defects are responsible for the observed ferromagnetism in undoped and transition metal (TM) doped ZnO systems. PL analysis demonstrated that undoped ZnO has more donor defects (V{sub O} and Zn{sub i}) which are beneficial for gas response enhancement. Undoped ZnO based sensor exhibited a higher sensor response to NH{sub 3} gas compared to its counterparts owing to high content of donor defects while transition metal doped sensors showed short response and recovery times compared to undoped ZnO.

  20. Effect of Er3+ doping on structural, morphological and photocatalytical properties of ZnO thin films

    Science.gov (United States)

    Bouhouche, S.; Bensouici, F.; Toubane, M.; Azizi, A.; Otmani, A.; Chebout, K.; Kezzoula, F.; Tala-Ighil, R.; Bououdina, M.

    2018-05-01

    In this research work, structure, microstructure, optical and photocatalytic properties of undoped and Erbium doped nanostructured ZnO thin films prepared by sol-gel dip-coating are investigated. X-ray diffraction (XRD) analysis indicates that the deposited films crystallize within the hexagonal wurtzite-type structure with a preferential growth orientation along (002) plane. Morphological observations using scanning electron microscopy (SEM) reveal important influence of Er concentration; displaying homogeneous and dense aspect for undoped to 0.3% then grid-like morphology for 0.4 and 0.5%. UV/vis/NIR transmittance spectroscopy spectra display a transmittance over 70%, and small variation in the energy gap energy 3.263–3.278 eV. Wettability test of ZnO thin films surface ranges from hydrophilic aspect for pure ZnO to hydrophobic one for Er doped ZnO, and the contact angle is found to increase from 58.7° for pure ZnO up to 98.4° for 0.4% Er doped ZnO. The photocatalytic activity measurements evaluated using the degradation of methylene blue (MB) under UV light irradiation demonstrate that undoped ZnO film shows higher photocatalytic activity compared to Er doped ZnO films, which may be attributed to the deterioration of films’crystallinity resulting in lower transmittance.

  1. Influence of Ag thickness of aluminum-doped ZnO/Ag/aluminum-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Hung-Wei, E-mail: hwwu@mail.ksu.edu.tw [Department of Computer and Communication, Kun Shan University, No. 949, Dawan Rd., Yongkang Dist., Tainan City 710, Taiwan (China); Yang, Ru-Yuan [Graduate Institute of Materials Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China); Hsiung, Chin-Min; Chu, Chien-Hsun [Department of Mechanical Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China)

    2012-10-01

    Highly conducting aluminum-doped ZnO (30 nm)/Ag (5-15 nm)/aluminum-doped ZnO (30 nm) multilayer thin films were deposited on glass substrate by rf magnetron sputtering (for top/bottom aluminum-doped ZnO films) and e-beam evaporation (for Ag film). The transmittance is more than 70% for wavelengths above 400 nm with the Ag layer thickness of 10 nm. The resistivity is 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm, which can be decreased to 3.8 Multiplication-Sign 10{sup -5} {Omega}-cm with the increase of the Ag layer thickness to 15 nm. The Haacke figure of merit has been calculated for the films with the best value being 8 Multiplication-Sign 10{sup -3} {Omega}{sup -1}. It was shown that the multilayer thin films have potential for applications in optoelectronics. - Highlights: Black-Right-Pointing-Pointer High-quality Al-doped ZnO (AZO)/Ag/AZO Transparent Conducting Oxide films. Black-Right-Pointing-Pointer AZO films (30 nm) made by RF sputtering; E-beam evaporation for Ag film (5-15 nm). Black-Right-Pointing-Pointer Influence of Ag thickness on optical and electrical properties were analyzed. Black-Right-Pointing-Pointer High quality multilayer film with optimal intermediate Ag layer thickness of 10 nm. Black-Right-Pointing-Pointer 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm resistivity, 91.89% transmittance at 470 nm obtained and reproducible.

  2. Research Update: Doping ZnO and TiO2 for solar cells

    Directory of Open Access Journals (Sweden)

    Robert L. Z. Hoye

    2013-12-01

    Full Text Available ZnO and TiO2 are two of the most commonly used n-type metal oxide semiconductors in new generation solar cells due to their abundance, low-cost, and stability. ZnO and TiO2 can be used as active layers, photoanodes, buffer layers, transparent conducting oxides, hole-blocking layers, and intermediate layers. Doping is essential to tailor the materials properties for each application. The dopants used and their impact in solar cells are reviewed. In addition, the advantages, disadvantages, and commercial potential of the various fabrication methods of these oxides are presented.

  3. The alkali and alkaline earth metal doped ZnO nanotubes: DFT studies

    International Nuclear Information System (INIS)

    Peyghan, Ali Ahmadi; Noei, Maziar

    2014-01-01

    Doping of several alkali and alkaline earth metals into sidewall of an armchair ZnO nanotube has been investigated by employing the density functional theory in terms of energetic, geometric, and electronic properties. It has been found that doping processes of the alkali and alkaline metals are endothermic and exothermic, respectively. Based on the results, contrary to the alkaline metal doping, the electronic properties of the tube are much more sensitive to alkali metal doping so that it is transformed from intrinsic semiconductor with HOMO–LUMO energy gap of 3.77 eV to an extrinsic semiconductor with the energy gap of ∼1.11–1.95 eV. The doping of alkali and alkaline metals increases and decreases the work function of the tube, respectively, which may influence the electron emission from the tube surface

  4. TUNABLE MAGNETIC AND ELECTRICAL PROPERTIES OF Co-DOPED ZnO FILMS BY VARYING OXYGEN PARTIAL PRESSURE

    OpenAIRE

    L. G. WANG; H. W. ZHANG; X. L. TANG; Y. X. LI; Z. Y. ZHONG

    2011-01-01

    High quality Co-doped ZnO films with good reproducibility have been prepared under different oxygen partial pressure by radio-frequency magnetron sputtering. These films were characterized using numerous characterization techniques including X-ray diffraction, electrical transport, and magnetization measurements. The effect of oxygen partial pressure on the structural, magnetic, and electrical properties of Co-doped ZnO films has been systematically studied. It was found that the structural, ...

  5. Low-Temperature Thermoelectric Properties of Fe2VAl with Partial Cobalt Doping

    Science.gov (United States)

    Liu, Chang; Morelli, Donald T.

    2012-06-01

    Ternary metallic alloy Fe2VAl with a pseudogap in its energy band structure has received intensive scrutiny for potential thermoelectric applications. Due to the sharp change in the density of states profile near the Fermi level, interesting transport properties can be triggered to render possible enhancement in the overall thermoelectric performance. Previously, this full-Heusler-type alloy was partially doped with cobalt at the iron sites to produce a series of compounds with n-type conductivity. Their thermoelectric properties in the temperature range of 300 K to 850 K were reported. In this research, efforts were made to extend the investigation on (Fe1- x Co x )2VAl to the low-temperature range. Alloy samples were prepared by arc-melting and annealing. Seebeck coefficient, electrical resistivity, and thermal conductivity measurements were performed from 80 K to room temperature. The effects of cobalt doping on the material's electronic and thermal properties are discussed.

  6. Effect of Ag Doping on the Electronic Structure and Optical Properties of ZnO(0001 Surface

    Directory of Open Access Journals (Sweden)

    Xiang Qian

    2018-01-01

    Full Text Available Using first-principle calculations, the geometrical structure, the electronic and optical properties of Ag-doped ZnO(0001 surface have been investigated. We found that Ag-doped ZnO(0001 surface is more easily formed on the first layer. On the other hand, the doped surface has gradually become an equipotential body, showing obvious metallic characteristics. We found that a new peak appeared in the low energy region after Ag doping, which was mainly due to the electron transition between the two orbital levels of Ag-4d and O-2p.

  7. Probing the doping mechanisms and electrical properties of Al, Ga and In doped ZnO prepared by spray pyrolysis

    KAUST Repository

    Maller, Robert

    2016-05-24

    The measured structural, optical and electrical properties of Al, Ga and In doped ZnO films deposited using spray pyrolysis are reported over the doping range 0.1 - 3 atomic percent (at. %). Over the entire doping series highly transparent, polycrystalline thin films are prepared. Using the AC Hall effect we probe the electronic properties of our doped films separating the impact of doping on the measured charge carrier concentrations and Hall mobility, with an emphasis on the low doping, < 1 at. %, range. In this doping range highly resistive films are formed and we highlight AC Hall as a reliable and highly reproducible technique for analysing the doping mechanism. The implementation of a simple, post-deposition heat treatment of our AZO films creates typical films with charge carrier concentrations exceeding > 1019 cm-3 and electron mobilities over 10 cm2/Vs. We describe in detail the nature of the defect chemistry and the role of intrinsic defects, particularly traps, and show that despite significant variations in dopant species and grain boundary concentrations that the defect chemistry dominates the electrical characteristics.

  8. Probing the doping mechanisms and electrical properties of Al, Ga and In doped ZnO prepared by spray pyrolysis

    KAUST Repository

    Maller, Robert; Porte, Yoann; Alshareef, Husam N.; McLachlan, Martyn

    2016-01-01

    The measured structural, optical and electrical properties of Al, Ga and In doped ZnO films deposited using spray pyrolysis are reported over the doping range 0.1 - 3 atomic percent (at. %). Over the entire doping series highly transparent, polycrystalline thin films are prepared. Using the AC Hall effect we probe the electronic properties of our doped films separating the impact of doping on the measured charge carrier concentrations and Hall mobility, with an emphasis on the low doping, < 1 at. %, range. In this doping range highly resistive films are formed and we highlight AC Hall as a reliable and highly reproducible technique for analysing the doping mechanism. The implementation of a simple, post-deposition heat treatment of our AZO films creates typical films with charge carrier concentrations exceeding > 1019 cm-3 and electron mobilities over 10 cm2/Vs. We describe in detail the nature of the defect chemistry and the role of intrinsic defects, particularly traps, and show that despite significant variations in dopant species and grain boundary concentrations that the defect chemistry dominates the electrical characteristics.

  9. Defect studies of ZnO single crystals electrochemically doped with hydrogen

    Science.gov (United States)

    Čížek, J.; Žaludová, N.; Vlach, M.; Daniš, S.; Kuriplach, J.; Procházka, I.; Brauer, G.; Anwand, W.; Grambole, D.; Skorupa, W.; Gemma, R.; Kirchheim, R.; Pundt, A.

    2008-03-01

    Various defect studies of hydrothermally grown (0001) oriented ZnO crystals electrochemically doped with hydrogen are presented. The hydrogen content in the crystals is determined by nuclear reaction analysis and it is found that already 0.3at.% H exists in chemically bound form in the virgin ZnO crystals. A single positron lifetime of 182ps is detected in the virgin crystals and attributed to saturated positron trapping at Zn vacancies surrounded by hydrogen atoms. It is demonstrated that a very high amount of hydrogen (up to ˜30at.%) can be introduced into the crystals by electrochemical doping. More than half of this amount is chemically bound, i.e., incorporated into the ZnO crystal lattice. This drastic increase of the hydrogen concentration is of marginal impact on the measured positron lifetime, whereas a contribution of positrons annihilated by electrons belonging to O-H bonds formed in the hydrogen doped crystal is found in coincidence Doppler broadening spectra. The formation of hexagonal shape pyramids on the surface of the hydrogen doped crystals by optical microscopy is observed and discussed.

  10. Role of Fe doping on structural and vibrational properties of ZnO nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Pandiyarajan, T.; Udayabhaskar, R.; Karthikeyan, B. [National Institute of Technology, Department of Physics, Tiruchirappalli (India)

    2012-05-15

    In this report, Raman and Fourier Transform Infrared (FTIR) measurements were carried out to study the phonon modes of pure and Fe doped ZnO nanoparticles. The nanoparticles were prepared by sol-gel technique at room temperature. The X-ray diffraction measurements reveal that the nanoparticles are in hexagonal wurtzite structure and doping makes the shrinkage of the lattice parameters, whereas there is no alteration in the unit cell. Raman measurements show both E{sub 2}{sup low} and E{sub 2}{sup High} optical phonon mode is shifted towards lower wave number with Fe incorporation and explained on the basis of force constant variation, stress measurements, respectively. In addition, Fe related local vibrational modes (LVM) were observed for higher concentration of Fe doping. FTIR spectra reveal a band at 444 cm{sup -1} which is specific to E{sub 1} (TO) mode; a red-shift of this mode in Fe doped samples and some surface phonon modes were observed. Furthermore, the observation of additional IR modes, which is considered to have an origin related to Fe dopant in the ZnO nanostructures, is also reported. These additional mode features can be regarded as an indicator for the incorporation of Fe ions into the lattice position of the ZnO nanostructures. (orig.)

  11. Formulation and Characterization of Cu Doped ZnO Thick Films as LPG Gas Sensor

    Directory of Open Access Journals (Sweden)

    A. V. PATIL

    2010-12-01

    Full Text Available Thick films of pure and various concentrations (1 wt. %, 3 wt. %, 5 wt. %, 7 wt. % and 10 wt. % of Cu-doped ZnO were prepared on alumina substrates using a screen printing technique. These films were fired at a temperature of 700ºC for two hours in an air atmosphere. Morphological, compositional and structural properties of the samples were obtained using the scanning electron microscopy (SEM, Energy dispersive spectroscopy (EDAX and X-ray diffraction techniques respectively. The LPG gas sensing properties of these thick films were investigated at different operating temperatures and LPG gas concentrations. The surface resistance of thick films decreases when exposed to LPG gas. The Cu doped films show significant sensitivity to LPG gas than pure ZnO film. 5 wt. % Cu-doped ZnO film was found to be more sensitive (87.3 % to LPG gas exposed at 300 oC than other doping concentrations with fast response and recovery time.

  12. Chitosan doped with nanoparticles of copper, nickel and cobalt.

    Science.gov (United States)

    Cárdenas-Triviño, Galo; Elgueta, Carolina; Vergara, Luis; Ojeda, Javier; Valenzuela, Ariel; Cruzat, Christian

    2017-11-01

    Metal colloids in 2 propanol using nanoparticles (NPs) of copper, nickel and cobalt were prepared by Chemical Liquid Deposition (CLD) method. The resulting colloidal dispersions were characterized by Transmission Electron Microscopy (TEM). The colloids were supported in chitosan. Then, microbiological assays were performed using E. coli and S. aureus in order to determine the bactericide/bacteriostatic activity of nanoparticles (NPs) trapped or chelated with chitosan. Finally, the toxicity of the metal colloids Cu, Ni and Co was tested. Bio-assays were conducted in three different animal species. First of all on earth warms (Eisenia foetida) to evaluate the toxicity and the biocompatibility of chitosan in lactic acid (1% and 0.5%). Secondly bio-assay done in fishes (rainbow trout), the liver toxicity of NPs in vivo was evaluated. Finally, a bio-assay was conducted in Sprange-Dawley rats of 100g weight, which were injected intraperitoneally with different solutions of chitosan metal colloids. Then, the minimum and maximum concentration were determined for copper, nickel and cobalt. The purpose of the use of chitosan was acting as a carrier for some magnetic NPs, which toxicity would allow to obtain new polymeric materials with potential applications as magnet future drugs carrier. Copyright © 2017 Elsevier B.V. All rights reserved.

  13. Synthesis and characterization of surfactant assisted Mn2+ doped ZnO nanocrystals

    Directory of Open Access Journals (Sweden)

    N. Shanmugam

    2016-09-01

    Full Text Available We report the synthesis and characterization of Mn doped ZnO nanocrystals, both in the free standing and PVP capped particle forms. The nanocrystals size could be controlled by capping them with polyvinylpyrollidone and was estimated by X-ray diffraction and transmission electron microscopy. The chemical compositions of the products were characterized by FT-IR spectroscopy. UV–Vis absorption spectroscopy measurements reveal that the capping of ZnO leads to blue shift due to quantum confinement effect. The morphology of the particles was evaluated by Scanning Electron Microscopy (SEM and Transmission Electron Microscopy (TEM. Both the Thermo Gravimetric Analysis (TGA and Differential Thermal Analysis (DTA curves of the ZnO show no further weight loss and thermal effect at a temperature above 510 °C.

  14. Experimental and ab initio study of Ta-doped ZnO semiconductor

    Energy Technology Data Exchange (ETDEWEB)

    Munoz, E. L., E-mail: munoz@fisica.unlp.edu.ar; Richard, D., E-mail: richard@fisica.unlp.edu.ar [UNLP, Departamento de Fisica and Instituto de Fisica La Plata (IFLP, CCT La Plata, CONICET), Fac. de Ciencias Exactas (Argentina); Eversheim, P. D. [Universitaet Bonn, Helmholtz-Institut fuer Strahlen-und Kernphysik (H-ISKP) (Germany); Renteria, M., E-mail: renteria@fisica.unlp.edu.ar [UNLP, Departamento de Fisica and Instituto de Fisica La Plata (IFLP, CCT La Plata, CONICET), Fac. de Ciencias Exactas (Argentina)

    2010-04-15

    In this work, we present {gamma}-{gamma} Perturbed-Angular-Correlation results in polycrystalline ZnO semiconductor implanted with {sup 181}Hf({yields}{sup 181}Ta) probes. Calculations in Ta-doped ZnO were carried out using the Full-Potential Augmented Plane Wave plus local orbital method in a supercell and varying self-consistently the charge state of the impurity. Ta is a triple donor impurity with respect to Zn{sup 2 + } in ZnO and thus it can loose 1, 2 or 3 donor electrons under certain circumstances. As expected, the comparison between the experimental Electric-Field-Gradient tensor results and our ab initio predictions shows that the Ta impurity is in an ionized charge state at room temperature.

  15. Experimental and ab initio study of Ta-doped ZnO semiconductor

    International Nuclear Information System (INIS)

    Muñoz, E. L.; Richard, D.; Eversheim, P. D.; Rentería, M.

    2010-01-01

    In this work, we present γ–γ Perturbed-Angular-Correlation results in polycrystalline ZnO semiconductor implanted with 181 Hf(→ 181 Ta) probes. Calculations in Ta-doped ZnO were carried out using the Full-Potential Augmented Plane Wave plus local orbital method in a supercell and varying self-consistently the charge state of the impurity. Ta is a triple donor impurity with respect to Zn 2 +  in ZnO and thus it can loose 1, 2 or 3 donor electrons under certain circumstances. As expected, the comparison between the experimental Electric-Field-Gradient tensor results and our ab initio predictions shows that the Ta impurity is in an ionized charge state at room temperature.

  16. Homojunction p-n photodiodes based on As-doped single ZnO nanowire

    International Nuclear Information System (INIS)

    Cho, H. D.; Zakirov, A. S.; Yuldashev, Sh. U.; Kang, T. W.; Ahn, C. W.; Yeo, Y. K.

    2013-01-01

    Photovoltaic device was successfully grown solely based on the single ZnO p-n homojunction nanowire. The ZnO nanowire p-n diode consists of an as-grown n-type segment and an in-situ arsenic doped p-type segment. This p-n homojunction acts as a good photovoltaic cell, producing a photocurrent almost 45 times larger than the dark current under reverse-biased condition. Our results demonstrate that present ZnO p-n homojunction nanowire can be used as a self-powered ultraviolet photodetector as well as a photovoltaic cell, which can also be used as an ultralow electrical power source for nano-scale electronic, optoelectronic, and medical devices

  17. Study on electrical structure and magneto-optical properties of W-doped ZnO

    Science.gov (United States)

    Li, Yong; Hou, Qingyu; Zhao, Chunwang; Xu, Zhenchao

    2018-04-01

    For W-doping amounts ranging from 0.0417 to 0.0833, experimental UV-visible absorption spectra blue shift and red shift results have been reported in the literatures. However, there is few literature reported research on magnetic mechanism. To solve this problem, this study investigates the disagreement about blue shift and red shift results and research on magnetic mechanism. The band structures, density of states, absorption spectra and magnetism have been investigated using first-principles planewave ultrasoft pseudopotential method based on the density functional theory. The calculated results showed that increased W-doping amounts first increase the volumes, and then reduce the volumes, decrease the formation energies, and stabilize the doped system. The band gaps become narrower and the absorption spectrum exhibits a significant red shift in UV and visible light emission. Moreover, the covalent bond vertical to c-axis strengthens, and the ionic bond parallel to c-axis weakens. Increased W-doping amounts decrease the magnetism of doped system. The magnetism of doped system originates from the electron exchange among W-5d, O-2p and Zn-3d orbitals of the W-doped ZnO. In W double-doped system, the ferromagnetic Curie temperature can be above room temperature when the doped system has a longer W-W distance.

  18. Enhancement of exciton radiative recombination for In-doped ZnO nanowires with aluminum cylindrical micropillars

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Jen-Cheng; Liang, Yu-Ting; Cheng, Fang-Ching; Fang, Chia-Hui; Chen, Hung-Ing; Tsai, Chung-Yuan [Graduate Institute of Electro-Optical Engineering and Department of Electronic Engineering, Chang Gung University, 259 Wen-Hwa 1st Road, Kwei-Shan, Tao-Yuan 333, Taiwan, ROC (China); Jiang, Joe-Air [Department of Bio-Industrial Mechatronics Engineering, National Taiwan University, Taipei 106, Taiwan, ROC (China); Nee, Tzer-En, E-mail: neete@mail.cgu.edu.tw [Graduate Institute of Electro-Optical Engineering and Department of Electronic Engineering, Chang Gung University, 259 Wen-Hwa 1st Road, Kwei-Shan, Tao-Yuan 333, Taiwan, ROC (China)

    2013-04-15

    Zinc oxide (ZnO) has attracted intensive research effort in recent years, due to its unique properties and versatile applications. Recent work on the conservation of surface plasmon (SP) and light through period metal arrays has elucidated the propagation of SP resonance behavior. In this paper, we discuss the enhancement of exciton radiative recombination of the ZnO nanowires with Al cylindrical micropillars. Optical characterization of exciton interacted with SP resonance for indium-doped ZnO nanowires with Al cylindrical micropillars has been also investigated. From photoluminescence spectra of In-doped ZnO nanowires, it is found that the In-doped ZnO nanowires have a blue emission at 425 nm, which resulted from the ZnO band-to-band transition. Prior to the arrays of samples were annealed, a broad green emission centered at 500 nm was observed, which is attributed to ZnO native point defects. The relatively strong green band emission results from the radiative recombination that arises from the ionized oxygen vacancy and surface-defect related luminescence. Compare the In-doped ZnO on Si substrate, the enhancement of PL intensity for In-doped ZnO with deposited Al pattern film can be attributed to strong interaction with SP resonance and exciton over a broad temperature range. These experimental results indicate that Al cylindrical micropillars can significantly enhance carrier confinement and increase the quantum efficiency of In-doped ZnO/Al heterostructures due to the interaction of SP resonance between the In-doped ZnO nanowires and Al cylindrical micropillar structures, the surface-defect related luminescence, and the auxiliary test structures with variable micropillar parameters. -- Highlights: ► We examine the exciton radiative recombination of the ZnO nanowires. ► Al cylindrical micropillars affect the carrier recombination of ZnO/Al structures. ► The interaction of SP resonance between In-doped ZnO nanowire and Al pattern film. ► The carrier

  19. Effect of B doping on optical, electrical properties and defects of ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Mao, Caiying [State Key Laboratory of Mechanical Transmission, College of Physics, Chongqing University, Chongqing, 400044 (China); Fang, Liang, E-mail: lfang@cqu.edu.cn [State Key Laboratory of Mechanical Transmission, College of Physics, Chongqing University, Chongqing, 400044 (China); Zhang, Hong; Li, Wanjun [Key Laboratory of Optoelectronic Functional Materials of Chongqing, College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331 (China); Wu, Fang, E-mail: fang01234@163.com [State Key Laboratory of Mechanical Transmission, College of Physics, Chongqing University, Chongqing, 400044 (China); Qin, Guoping [Key Laboratory of Optoelectronic Functional Materials of Chongqing, College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331 (China); Ruan, Haibo, E-mail: rhbcqu@aliyun.com [Chongqing Key Laboratory of Micro/Nano Materials Engineering and Technology, Research Center for Materials Interdisciplinary Sciences, Chongqing University of Arts and Sciences, Chongqing, 402160 (China); Kong, Chunyang, E-mail: kchy@163.com [Key Laboratory of Optoelectronic Functional Materials of Chongqing, College of Physics and Electronic Engineering, Chongqing Normal University, Chongqing 401331 (China)

    2016-08-15

    Boron doped ZnO (BZO) films with B content in the range of 0–6 at.% were deposited on quartz glass substrates by RF magnetron sputtering technique. The effects of B doping content on microstructure, optical and electrical properties of BZO films were systematically investigated by XRD, SEM, AFM, XPS, PL, UV–vis–near infrared spectrophotometer and Hall-effect measurement, respectively. It is found that the crystal quality of ZnO films can be improved as B doping content increases to no larger than 4 at.% and will be deteriorated at higher B doping content. The grain size and surface roughness of the films reduce with the increase of B doping content. The BZO films exhibit tensile stress and the stress increases with B content. The transmittance of the BZO films is revealed to be 90% in the visible region. As the B doping content increases from 0 to 6 at.%, the optical band gap of BZO films enhances from 3.28 to 3.57 eV, which is found to increase linearly with the tensile stress in the films. The lowest resistivity of 1.58 × 10{sup −3} (Ω cm) is obtained at 2 at.% B doping content. XPS and PL analyses demonstrated that B doping can promote the formation of defects of zinc interstitials (Zn{sub i}) and oxygen vacancies (V{sub O}). - Highlights: • The relationship of band gap (E{sub g}) and stress (σ) in BZO is deduced. • XPS and PL illustrate B doping can promote the formation of Zn{sub i} and V{sub O} in BZO. • The lowest resistivity (1.58 × 10{sup −3} Ω cm) is obtained at 2 at.% B content.

  20. Synthesis and characterization of single-phase Mn-doped ZnO

    Science.gov (United States)

    Chattopadhyay, S.; Dutta, S.; Banerjee, A.; Jana, D.; Bandyopadhyay, S.; Chattopadhyay, S.; Sarkar, A.

    2009-05-01

    Different samples of Zn 1-xMn xO series have been prepared using conventional solid-state sintering method. We identified up to what extent doping will enable us to synthesize single-phase polycrystalline Mn-doped ZnO sample, which is one of the prerequisites for dilute magnetic semiconductor, and we have analyzed its some other physical aspects. In synthesizing the samples, proportion of Mn varies from 1 to 5 at%. However, the milling time varied (6, 12, 24, 48 and 96 h) only for 2 at% Mn-doped samples while for other samples (1, 3, 4 and 5 at% Mn doped) the milling time has been fixed to 96 h. Room-temperature X-ray diffraction (XRD) data reveal that all of the prepared samples up to 3 at% of Mn doping exhibit wurtzite-type structure, and no segregation of Mn and/or its oxides has been found. The 4 at% Mn-doped samples show a weak peak of ZnMn 2O 4 apart from the other usual peaks of ZnO and the intensity of this impurity peak has been further increased for 5 at% of Mn doping. So beyond 3 at% doping, single-phase behavior is destroyed. Band gap for all the 2 at% Mn-doped samples has been estimated to be between 3.21 and 3.19 eV and the reason for this low band gap values has been explained through the grain boundary trapping model. The room-temperature resistivity measurement shows an increase of resistivity up to 48 h of milling and with further milling it saturates. The defect state of these samples has been investigated using the positron annihilation lifetime (PAL) spectroscopy technique. Here all the relevant lifetime parameters of positron i.e. free annihilation ( τ1) at defect site ( τ2) and average ( τav) increases with milling time.

  1. Synthesis and characterization of single-phase Mn-doped ZnO

    International Nuclear Information System (INIS)

    Chattopadhyay, S.; Dutta, S.; Banerjee, A.; Jana, D.; Bandyopadhyay, S.; Chattopadhyay, S.; Sarkar, A.

    2009-01-01

    Different samples of Zn 1-x Mn x O series have been prepared using conventional solid-state sintering method. We identified up to what extent doping will enable us to synthesize single-phase polycrystalline Mn-doped ZnO sample, which is one of the prerequisites for dilute magnetic semiconductor, and we have analyzed its some other physical aspects. In synthesizing the samples, proportion of Mn varies from 1 to 5 at%. However, the milling time varied (6, 12, 24, 48 and 96 h) only for 2 at% Mn-doped samples while for other samples (1, 3, 4 and 5 at% Mn doped) the milling time has been fixed to 96 h. Room-temperature X-ray diffraction (XRD) data reveal that all of the prepared samples up to 3 at% of Mn doping exhibit wurtzite-type structure, and no segregation of Mn and/or its oxides has been found. The 4 at% Mn-doped samples show a weak peak of ZnMn 2 O 4 apart from the other usual peaks of ZnO and the intensity of this impurity peak has been further increased for 5 at% of Mn doping. So beyond 3 at% doping, single-phase behavior is destroyed. Band gap for all the 2 at% Mn-doped samples has been estimated to be between 3.21 and 3.19 eV and the reason for this low band gap values has been explained through the grain boundary trapping model. The room-temperature resistivity measurement shows an increase of resistivity up to 48 h of milling and with further milling it saturates. The defect state of these samples has been investigated using the positron annihilation lifetime (PAL) spectroscopy technique. Here all the relevant lifetime parameters of positron i.e. free annihilation (τ 1 ) at defect site (τ 2 ) and average (τ av ) increases with milling time.

  2. Boron doped nanostructure ZnO films deposited by ultrasonic spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Karakaya, Seniye, E-mail: seniyek@ogu.edu.tr; Ozbas, Omer

    2015-02-15

    Highlights: • Nanostructure undoped and boron doped ZnO films were deposited by USP technique. • Influences of doping on the surface and optical properties of the ZnO films were investigated. • XRD spectra of the films exhibited a variation in crystalline quality depending on the B content. - Abstract: ZnO is an II–VI compound semiconductor with a wide direct band gap of 3.3 eV at room temperature. Doped with group III elements (B, Al or Ga), it becomes an attractive candidate to replace tin oxide (SnO{sub 2}) or indium tin oxide (ITO) as transparent conducting electrodes in solar cell devices and flat panel display due to competitive electrical and optical properties. In this work, ZnO and boron doped ZnO (ZnO:B) films have been deposited onto glass substrates at 350 ± 5 °C by a cost-efficient ultrasonic spray pyrolysis technique. The optical, structural, morphological and electrical properties of nanostructure undoped and ZnO:B films have been investigated. Electrical resistivity of films has been analyzed by four-probe technique. Optical properties and thicknesses of the films have been examined in the wavelength range 1200–1600 nm by using spectroscopic ellipsometry (SE) measurements. The optical constants (refractive index (n) and extinction coefficient (k)) and the thicknesses of the films have been fitted according to Cauchy model. The optical method has been used to determine the band gap value of the films. Transmission spectra have been taken by UV spectrophotometer. It is found that both ZnO and ZnO:B films have high average optical transmission (≥80%). X-ray diffraction (XRD) patterns indicate that the obtained ZnO has a hexagonal wurtzite type structure. The morphological properties of the films were studied by atomic force microscopy (AFM). The surface morphology of the nanostructure films is found to depend on the concentration of B. As a result, ZnO:B films are promising contender for their potential use as transparent window layer and

  3. Determination of chemical state of Al doping element in ZnO layer

    International Nuclear Information System (INIS)

    Csik, A.; Toth, J.; Lovics, R.; Takats, V.; Hakl, J.; Vad, K.

    2011-01-01

    Complete text of publication follows. Transparent and conducting oxides (TCO) thin films are very important from the scientific and technological point of view. The coexistence of electrical conductivity and optical transparency in these materials makes it possible to use them in modern technologies: transparent electrodes for flat panel displays and photovoltaic cells, low emissivity windows, transparent thin films transistors, light emitting diodes. One of the important TCO semiconductors is the impurity-doped zinc-oxide (ZnO) layer, for example aluminium doped zinc-oxide layer (AZO), due to its unique physical and chemical properties. It has wide band gap (3.44 eV) and large exciton binding energy (60 meV). ZnO thin layers have a great interest for potential applications in optical and optoelectronic devices. Furthermore, high quality single crystal ZnO wafers has already been available as a result of new developments in ZnO growth technologies with the capability to scale up wafer size, which is an important factor for increasing efficiency of solar cells. Nonetheless, in order to enable the use of ZnO layers with enhanced electrical properties, higher conductivities can be obtained by doping with donor elements such as aluminium, gallium, indium, boron or fluorine. Investigation of p-type doping possibilities, diffusion processes and thermal stability of these layers are in the focus of interest in the interpretation of their optical and electrical properties, and the prediction of their lifetime. In our SNMS/SIMS-XPS laboratory, experiments on TCO layered structures were carried on. Depth profile and chemical state analyses of ZnO/AlO/ZnO layered structures were performed by Secondary Neutral Mass Spectrometry (SNMS) and X-ray photoelectron spectroscopy (XPS). The samples were produced by atomic layer deposition technique with the following layered structure: between a few hundred atomic layers of ZnO was an AlO atomic layer. The SNMS was used for depth

  4. Ba-DOPED ZnO MATERIALS: A DFT SIMULATION TO INVESTIGATE THE DOPING EFFECT ON FERROELECTRICITY

    Directory of Open Access Journals (Sweden)

    Luis H. da S. Lacerda

    2016-04-01

    Full Text Available ZnO is a semiconductor material largely employed in the development of several electronic and optical devices due to its unique electronic, optical, piezo-, ferroelectric and structural properties. This study evaluates the properties of Ba-doped wurtzite-ZnO using quantum mechanical simulations based on the Density Functional Theory (DFT allied to hybrid functional B3LYP. The Ba-doping caused increase in lattice parameters and slight distortions at the unit cell angle in a wurtzite structure. In addition, the doping process presented decrease in the band-gap (Eg at low percentages suggesting band-gap engineering. For low doping amounts, the wavelength characteristic was observed in the visible range; whereas, for middle and high doping amounts, the wavelength belongs to the Ultraviolet range. The Ba atoms also influence the ferroelectric property, which is improved linearly with the doping amount, except for doping at 100% or wurtzite-BaO. The ferroelectric results indicate the ZnO:Ba is an strong option to replace perovskite materials in ferroelectric and flash-type memory devices.

  5. On the transparent conducting oxide Al doped ZnO: First Principles and Boltzmann equations study

    Energy Technology Data Exchange (ETDEWEB)

    Slassi, A. [Institute of Nanomaterials and Nanotechnology, MAScIR, Rabat (Morocco); LMPHE (URAC 12), Faculté des Sciences, Université Mohammed V-Agdal, Rabat (Morocco); Naji, S. [LMPHE (URAC 12), Faculté des Sciences, Université Mohammed V-Agdal, Rabat (Morocco); Department of Physics, Faculty of Science, Ibb University, Ibb (Yemen); Benyoussef, A. [Institute of Nanomaterials and Nanotechnology, MAScIR, Rabat (Morocco); LMPHE (URAC 12), Faculté des Sciences, Université Mohammed V-Agdal, Rabat (Morocco); Hamedoun, M., E-mail: hamedoun@hotmail.com [Institute of Nanomaterials and Nanotechnology, MAScIR, Rabat (Morocco); El Kenz, A. [LMPHE (URAC 12), Faculté des Sciences, Université Mohammed V-Agdal, Rabat (Morocco)

    2014-08-25

    Highlights: • The incorporation of Al in ZnO increases the optical band edge absorption. • Incorporated Al creates shallow donor states of Al-3s around Fermi level. • Transmittance decreases in the visible and IR regions, while it increases in the UV region. • Electrical conductivity increases and reaches almost the saturation for high concentration of Al. - Abstract: We report, in this work, a theoretical study on the electronic, optical and electrical properties of pure and Al doped ZnO with different concentrations. In fact, we investigate these properties using both First Principles calculations within TB-mBJ approximation and Boltzmann equations under the constant relaxation time approximation for charge carriers. It is found out that, the calculated lattice parameters and the optical band gap of pure ZnO are close to the experimental values and in a good agreement with the other theoretical studies. It is also observed that, the incorporations of Al in ZnO increase the optical band edge absorption which leads to a blue shift and no deep impurities levels are induced in the band gap as well. More precisely, these incorporations create shallow donor states around Fermi level in the conduction band minimum from mainly Al-3s orbital. Beside this, it is found that, the transmittance is decreased in the visible and IR regions, while it is significantly improved in UV region. Finally, our calculations show that the electrical conductivity is enhanced as a result of Al doping and it reaches almost the saturation for high concentration of Al. These features make Al doped ZnO a transparent conducting electrode for optoelectronic device applications.

  6. Formation of polar surfaces in microstructured ZnO by doping with Cu and applications in photocatalysis using visible light

    International Nuclear Information System (INIS)

    Pawar, Rajendra C.; Choi, Da-Hyun; Lee, Jai-Sung; Lee, Caroline S.

    2015-01-01

    We report the synthesis of copper-doped zinc oxide microstructures with a large amount of polar surfaces using a single-step facile chemical method by collecting powders of zinc oxide (ZnO) microstructures. It was found that rod-like morphology of ZnO transformed into disk and sphere-like structure with nanosheets. Hollow disk-like structures were formed due to the surface etching properties of Cl − ions in the copper chloride precursor. The photocatalytic degradation of methylene blue (MB) and rhodamine B (RhB) dyes was measured under irradiation with visible light using the structures as catalysts. The Cu-doped ZnO exhibited better photodegradation properties than did undoped ZnO. The enhanced performance is attributed to the existence of (001) polar surfaces, oxygen vacancies, and increased optical absorbance at visible wavelengths, which is consistent with the field emission scanning electron microscopy (FESEM), transmission electron microscopy (TEM), room temperature photoluminescence (PL), and optical absorbance measurements. These favorable photocatalytic properties of the doped microstructures demonstrate their potential for use in wastewater treatment. - Graphical abstract: Graphical abstract shows the electron transfer mechanism under visible light for Cu-doped ZnO microstructures and the photocatalytic degradation of dye. - Highlights: • Cu induced microstructures of ZnO with polar surfaces. • Methylene blue degradation under visible light irradiation. • Room temperature ferromagnetism due to oxygen vacancies in ZnO. • 7% Cu–ZnO has highest photocatalytic activity

  7. Progress in ZnO Acceptor Doping: What Is the Best Strategy?

    Directory of Open Access Journals (Sweden)

    Judith G. Reynolds

    2014-01-01

    Full Text Available This paper reviews the recent progress in acceptor doping of ZnO that has been achieved with a focus toward the optimum strategy. There are three main approaches for generating p-type ZnO: substitutional group IA elements on a zinc site, codoping of donors and acceptors, and substitution of group VA elements on an oxygen site. The relevant issues are whether there is sufficient incorporation of the appropriate dopant impurity species, does it reside on the appropriate lattice site, and lastly whether the acceptor ionization energy is sufficiently small to enable significant p-type conduction at room temperature. The potential of nitrogen doping and formation of the appropriate acceptor complexes is highlighted although theoretical calculations predict that nitrogen on an oxygen site is a deep acceptor. We show that an understanding of the growth and annealing steps to achieve the relevant acceptor defect complexes is crucial to meet requirements.

  8. Synthesis of Mn doped ZnO nanoparticles with biocompatible capping

    International Nuclear Information System (INIS)

    Sharda; Jayanthi, K.; Chawla, Santa

    2010-01-01

    Free standing nanoparticles of ZnO doped with transition metal ion Mn have been prepared by solid state reaction method at 500 deg. C. X-ray diffraction (XRD) analysis confirmed high quality monophasic wurtzite hexagonal structure with particle size of 50 nm and no signature of dopant as separate phase. Incorporation of Mn has been confirmed with EDS. Bio-inorganic interface was created by capping the nanoparticles with heteromultifunctional organic stabilizer mercaptosuccinic acid (MSA). The surface morphological studies by scanning electron microscopy (SEM) showed formation of spherical particles and the nanoballs grow in size uniformly with MSA capping. MSA capping has been confirmed with thermo gravimetric analysis (TGA) and FTIR. Photoluminescence (PL) studies show that the ZnO:Mn 2+ particles are excitable by blue light and emits in orange and red. Occurrence of room temperature ferromagnetism in Mn doped ZnO makes such biocompatible luminescent magnetic nanoparticles very promising material.

  9. Biodiesel production from castor oil using heterogeneous Ni doped ZnO nanocatalyst.

    Science.gov (United States)

    Baskar, G; Aberna Ebenezer Selvakumari, I; Aiswarya, R

    2018-02-01

    In the present study, castor oil with high free fatty acid was used for biodiesel production using heterogeneous Ni doped ZnO nanocatalyst. Ni doped ZnO nanocomposite calcinated at 800 °C has shown better catalytic activity. Process parameters on heterogeneous catalysis of castor oil into biodiesel were optimized using conventional and Response Surface Methodology (RSM). RSM was found more accurate in estimating the optimum conditions with higher biodiesel yield (95.20%). The optimum conditions for transesterification was found to be oil to methanol molar ratio of 1:8, catalyst loading 11% (w/w), reaction temperature of 55 °C for 60 min of reaction time by response surface method. The reusability studies showed that the nanocatalyst can be reused efficiently for 3 cycles. Copyright © 2017 Elsevier Ltd. All rights reserved.

  10. Luminescence and spectroscopic investigations on Gd3+ doped ZnO nanophosphor

    Directory of Open Access Journals (Sweden)

    G. Krishna Reddy

    2017-09-01

    Full Text Available The present paper describes the synthesis of 0.1 mol% Gadolinium (Gd doped Zinc oxide (ZnO nanophosphor by solution combustion method using Oxalyl dihydrazide (ODH fuel. Powder X-ray diffraction (PXRD peaks are well matched with the standard hexagonal wurtzite structure of ZnO (JCPDS card no. 36-1451. SEM and TEM analysis reveals porous morphology of as -formed sample with particles having narrow size distribution in the range ∼60–70 nm, in good agreement with XRD data. The PL spectrum of Gd doped ZnO sample exhibits an extra blue emission at 441 nm (∼2.81 eV in addition to the emission bands from undoped ZnO. From the TL data of ZnO:Gd nanophosphor with UV irradiation, it is observed that considerable amount of re-trapping is taking place in all the TL second order peaks. The EPR spectrum exhibits a number of resonance signals suggesting that Gd3+ ions are experiencing different crystal field strength and Zeeman interactions.

  11. Soluble Supercapacitors: Large and Reversible Charge Storage in Colloidal Iron-Doped ZnO Nanocrystals.

    Science.gov (United States)

    Brozek, Carl K; Zhou, Dongming; Liu, Hongbin; Li, Xiaosong; Kittilstved, Kevin R; Gamelin, Daniel R

    2018-05-09

    Colloidal ZnO semiconductor nanocrystals have previously been shown to accumulate multiple delocalized conduction-band electrons under chemical, electrochemical, or photochemical reducing conditions, leading to emergent semimetallic characteristics such as quantum plasmon resonances and raising prospects for application in multielectron redox transformations. Here, we demonstrate a dramatic enhancement in the capacitance of colloidal ZnO nanocrystals through aliovalent Fe 3+ -doping. Very high areal and volumetric capacitances (33 μF cm -2 , 233 F cm -3 ) are achieved in Zn 0.99 Fe 0.01 O nanocrystals that rival those of the best supercapacitors used in commercial energy-storage devices. The redox properties of these nanocrystals are probed by potentiometric titration and optical spectroscopy. These data indicate an equilibrium between electron localization by Fe 3+ dopants and electron delocalization within the ZnO conduction band, allowing facile reversible charge storage and removal. As "soluble supercapacitors", colloidal iron-doped ZnO nanocrystals constitute a promising class of solution-processable electronic materials with large charge-storage capacity attractive for future energy-storage applications.

  12. Low-frequency zone boundary phonons in Li doped ZnO ceramics

    Science.gov (United States)

    Yadav, Harish Kumar; Sreenivas, K.; Gupta, Vinay; Katiyar, R. S.

    2008-09-01

    Room temperature Raman spectra of Li doped ZnO (Zn1-xLixO) ceramics with varying Li concentrations (x =0.0, 0.05, 0.10, and 0.15) are investigated in this study. Four peaks were identified at 96.6, 127, 157, and 194 cm-1 in the Li doped samples. The peaks at 127, 157, and 194 cm-1 are assigned to zone boundary phonons in ZnO [J. M. Calleja and M. Cardona, Phys. Rev. B 16, 3753 (1977)], and appear due to disorder in ZnO lattice with Li incorporation. Lithium, owing to its smaller radius, adjusts itself anywhere in the ZnO lattice and breaks the crystal translational symmetry to a large extent, compared to other dopants. Disorder in the lattice is seen to be finely modulated with varying Li content. The peak at 96.6 cm-1 is hypothesized to be a projection of the vibrational motion of Li atoms at lower frequencies, which contributes in a major fashion at higher frequencies, due to its lighter mass than Zn or O atoms.

  13. A dual-colored bio-marker made of doped ZnO nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Y L; Zeng, X T [Singapore Institute of Manufacturing Technology, 71 Nanyang Drive, 638075 (Singapore); Fu, S; Kwek, L C [National Institute of Education, Nanyang Technological University, 1 Nanyang Walk, 637616 (Singapore); Tok, A I Y; Boey, F C Y [School of Materials Science and Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore); Lim, C S [School of Mechanical and Aerospace Engineering, Nanyang Technological University, 50 Nanyang Avenue, 639798 (Singapore)

    2008-08-27

    Bio-compatible ZnO nanocrystals doped with Co, Cu and Ni cations, surface capped with two types of aminosilanes and titania are synthesized by a soft chemical process. Due to the small particle size (2-5 nm), surface functional groups and the high photoluminescence emissions at the UV and blue-violet wavelength ranges, bio-imaging on human osteosarcoma (Mg-63) cells and histiocytic lymphoma U-937 monocyte cells showed blue emission at the nucleus and bright turquoise emission at the cytoplasm simultaneously. This is the first report on dual-color bio-images labeled by one semiconductor nanocrystal colloidal solution. Bright green emission was detected on mung bean seedlings labeled by all the synthesized ZnO nanocrystals. Cytotoxicity tests showed that the aminosilanes capped nanoparticles are non-toxic. Quantum yields of the nanocrystals varied from 79% to 95%. The results showed the potential of the pure ZnO and Co-doped ZnO nanocrystals for live imaging of both human cells and plant systems.

  14. High sensitivity ethanol gas sensor based on Sn - doped ZnO under visible light irradiation at low temperature

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Peishuo; Pan, Guofeng; Zhang, Bingqiang; Zhen, Jiali; Sun, Yicai, E-mail: pgf@hebut.edu.cn [Institute of Microelectronic, Hebei University of Technology, Tianjin (China)

    2014-07-15

    Pure ZnO and 5at%, 7at%, 9at% Sn - doped ZnO materials are prepared by the chemical co - precipitation method. They were annealed by furnace at temperature range of 300 - 700ºC in air for 1h. The ZnO materials are characterized by X - ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the Sn - doped ZnO materials appear rough porous structures. The maximum sensitivity can be achieved by doping the amount of 7 at%. It has much better sensing performance towards ethanol vapor under visible light irradiation. The response and recovery time are ~1s and ~5s, respectively. The mechanism for the improvement in the sensing properties can be explained with the surface adsorption theory and the photoactivation theory. (author)

  15. Enhanced local piezoelectric response in the erbium-doped ZnO nanostructures prepared by wet chemical synthesis

    Directory of Open Access Journals (Sweden)

    Reza Zamiri

    2017-03-01

    Full Text Available Pure and erbium (Er doped ZnO nanostructures were prepared by simple and cost effective wet chemical precipitation method. The successful doping with phase purity of prepared ZnO nanostructure was confirmed by X-ray diffraction (XRD and their Rietveld analysis. The change in structural morphology of nanoscale features of prepared ZnO nanopowders on Er doping was observed from their scanning electron microscopy (SEM images. The presence of Er in prepared ZnO nanopowder was further confirmed from corresponding energy dispersive X-ray spectroscopy (EDX spectra of scanned SEM images. Piezoelectric properties of before (green samples and after sintering of consolidated compact of synthesized nanopowders were successfully measured. The out-of-plane (effective longitudinal and in-plane (effective shear coefficients of the samples were estimated from the local piezoresponse.

  16. Annealed Ce{sup 3+}-doped ZnO flower-like morphology synthesized by chemical bath deposition method

    Energy Technology Data Exchange (ETDEWEB)

    Koao, Lehlohonolo F., E-mail: koaolf@ufs.ac.za [Department of Physics, University of the Free State (Qwa Qwa campus), Private Bag X13, Phuthaditjhaba 9866 (South Africa); Dejene, Francis B.; Tsega, Moges [Department of Physics, University of the Free State (Qwa Qwa campus), Private Bag X13, Phuthaditjhaba 9866 (South Africa); Swart, Hendrik C. [Department of Physics, University of the Free State, P.O. Box 339, Bloemfontein 9300 (South Africa)

    2016-01-01

    We have successfully synthesized ZnO:xmol% Ce{sup 3+} (0≤x≤10 mol%) doped nanopowders via the chemical bath deposition method (CBD) technique at low temperature (80 °C) and annealed in air at 700 °C. The X-ray diffraction patterns showed that all the undoped and Ce-doped ZnO nanopowders have a hexagonal wurtzite polycrystalline structure with an average crystallite size of about 46 nm. Weak diffraction peaks related mainly to cerium oxide were also detected at higher concentrations of Ce{sup 3+} (x=5–10 mol%). The scanning electron microscopy study revealed that the nanopowder samples were assembled in flower-shaped undoped ZnO and pyramid-shaped Ce{sup 3+}-doped ZnO nanostructures. The UV–vis spectra showed that the absorption edges shifted slightly to the longer wavelengths with the increase in the Ce{sup 3+} ions concentration. Moreover, the photoluminescence (PL) results showed a relative weak visible emission for the Ce{sup 3+}-doped ZnO nanoparticles compared to the undoped ZnO. The effects of Ce{sup 3+}-doping on the structure and PL of ZnO nanopowders are discussed in detail.

  17. Ferromagnetism in Fe-doped ZnO Nanocrystals: Experimental and Theoretical investigations

    OpenAIRE

    Karmakar, Debjani; Mandal, S. K.; Kadam, R. M.; Paulose, P. L.; Rajarajan, A. K.; Nath, T. K.; Das, A. K.; Dasgupta, I.; Das, G. P.

    2007-01-01

    Fe-doped ZnO nanocrystals are successfully synthesized and structurally characterized by using x-ray diffraction and transmission electron microscopy. Magnetization measurements on the same system reveal a ferromagnetic to paramagnetic transition temperature > 450 K with a low-temperature transition from ferromagnetic to spin-glass state due to canting of the disordered surface spins in the nanoparticle system. Local magnetic probes like EPR and Mossbauer indicate the presence of Fe in both v...

  18. Origin of the defects-induced ferromagnetism in un-doped ZnO single crystals

    Science.gov (United States)

    Zhan, Peng; Xie, Zheng; Li, Zhengcao; Wang, Weipeng; Zhang, Zhengjun; Li, Zhuoxin; Cheng, Guodong; Zhang, Peng; Wang, Baoyi; Cao, Xingzhong

    2013-02-01

    We clarified, in this Letter, that in un-doped ZnO single crystals after thermal annealing in flowing argon, the defects-induced room-temperature ferromagnetism was originated from the surface defects and specifically, from singly occupied oxygen vacancies denoted as F+, by the optical and electrical properties measurements as well as positron annihilation analysis. In addition, a positive linear relationship was observed between the ferromagnetism and the F+ concentration, which is in support with the above clarification.

  19. Cobalt-Doped Nickel Phosphite for High Performance of Electrochemical Energy Storage.

    Science.gov (United States)

    Li, Bing; Shi, Yuxin; Huang, Kesheng; Zhao, Mingming; Qiu, Jiaqing; Xue, Huaiguo; Pang, Huan

    2018-03-01

    Compared to single metallic Ni or Co phosphides, bimetallic Ni-Co phosphides own ameliorative properties, such as high electrical conductivity, remarkable rate capability, upper specific capacity, and excellent cycle performance. Here, a simple one-step solvothermal process is proposed for the synthesis of bouquet-like cobalt-doped nickel phosphite (Ni 11 (HPO 3 ) 8 (OH) 6 ), and the effect of the structure on the pseudocapacitive performance is investigated via a series of electrochemical measurements. It is found that when the cobalt content is low, the glycol/deionized water ratio is 1, and the reaction is under 200 °C for 20 h, the morphology of the sample is uniform and has the highest specific surface area. The cobalt-doped Ni 11 (HPO 3 ) 8 (OH) 6 electrode presents a maximum specific capacitance of 714.8 F g -1 . More significantly, aqueous and solid-state flexible electrochemical energy storage devices are successfully assembled. The aqueous device shows a high energy density of 15.48 mWh cm -2 at the power density of 0.6 KW cm -2 . The solid-state device shows a high energy density of 14.72 mWh cm -2 at the power density of 0.6 KW cm -2 . These excellent performances confirm that the cobalt-doped Ni 11 (HPO 3 ) 8 (OH) 6 are promising materials for applications in electrochemical energy storage devices. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  20. Structure and magnetic properties of chromium doped cobalt molybdenum nitrides

    Science.gov (United States)

    Guskos, Niko; Żołnierkiewicz, Grzegorz; Typek, Janusz; Guskos, Aleksander; Adamski, Paweł; Moszyński, Dariusz

    2016-09-01

    Four nanocomposites containing mixed phases of Co3Mo3N and Co2Mo3N doped with chromium have been prepared. A linear fit is found for relation between Co2Mo3N and chromium concentrations. The magnetization in ZFC and FC modes at different temperatures (2-300 K) and in applied magnetic fields (up to 70 kOe) have been investigated. It has been detected that many magnetic characteristics of the studied four nanocomposites correlate not with the chromium concentration but with nanocrystallite sizes. The obtained results were interpreted in terms of magnetic core-shell model of a nanoparticle involving paramagnetic core with two magnetic sublattices and a ferromagnetic shell related to chromium doping.

  1. Enhanced Raman scattering and nonlinear conductivity in Ag-doped hollow ZnO microspheres

    Energy Technology Data Exchange (ETDEWEB)

    Tringe, Joseph W.; Levie, Harold W.; McCall, Scott K.; Teslich, Nick E.; Wall, Mark A.; Orme, Christine A.; Matthews, Manyalibo J. [Lawrence Livermore National Laboratory, Livermore, CA (United States)

    2012-10-15

    Hollow spherical ZnO particles doped with Ag were synthesized with a two-step oxidation and sublimation furnace annealing process. Ag nanoparticle precipitates, as observed by transmission electron microscopy, were present in the polycrystalline ZnO matrix at Ag concentrations below 0.02 mol%, significantly below the 0.8 mol% solubility limit for Ag in ZnO. Enhanced Raman scattering of ZnO phonon modes is observed, increasing with Ag nanoparticle concentration. A further enhancement in Raman scattering due to resonance effects was observed for LO phonons excited by 2.33-eV photons as compared with Raman scattering under 1.96-eV excitation. Room-temperature photoluminescence spectra showed both a near-band-edge emission due to free exciton transitions and a mid-gap transition due to the presence of singly ionized oxygen vacancies. ZnO:Ag particles were measured electrically in a packed column and in monolithic form, and in both cases displayed nonlinear current-voltage characteristics similar to those previously observed in sintered ZnO:Ag monoliths where Ag-enhanced disorder at grain boundaries is thought to control current transport. We demonstrate therefore that Ag simultaneously modifies the electrical and optical properties of ZnO particles through the introduction of vacancies and other defects. (orig.)

  2. Highly efficient green light harvesting from Mg doped ZnO nanoparticles: Structural and optical studies

    Energy Technology Data Exchange (ETDEWEB)

    Sharma, Sarla, E-mail: mail2sarlasharma@gmail.com [Department of Physics, University of Rajasthan, Jaipur 302055 (India); Vyas, Rishi [Department of Physics, Malaviya National Institute of Technology, Jaipur 302017 (India); Sharma, Neha [Department of Physics, University of Rajasthan, Jaipur 302055 (India); Singh, Vidyadhar [Okinawa Institute of Science and Technology, Graduate University, Okinawa 9040495 (Japan); Singh, Arvind [Department of Physics, Institute of Chemical Technology, Mumbai 400 019 (India); Kataria, Vanjula; Gupta, Bipin Kumar [National Physical Laboratory (CSIR), New Delhi 110012 (India); Vijay, Y.K. [Department of Physics, University of Rajasthan, Jaipur 302055 (India)

    2013-03-05

    Graphical abstract: Demonstration of highly efficient green light emission harvesting from Mg doped ZnO nanoparticles were synthesized via facile wet chemical route with an average particle size ∼15 nm. The resulted nanoparticles exhibit intense green emission peaking at 530 nm upon 325 nm excitation. The photoluminescence (PL) intensity of visible emission depends upon the doping concentration of Mg. The PL intensity was found maximum up to 4% doping of Mg and beyond it exhibits a decrees in emission. The obtained highly luminescent green emission of ZnO nanoparticle would be an ultimate choice for next generation optoelectronics device materials. Highlights: ► Zn{sub 1−x}Mg{sub x}O nanoparticles were prepared by mechanochemical processing. ► High blue emission intensity was observed contrary to previous reports. ► Blue emission is suggested to be originating from the high density of defects. ► Defect density in as-milled condition is very high resulting in high emission. ► Mg promoted non-radiative recombination and lowered intensities. -- Abstract: Highly efficient green light emission was observed from Mg doped ZnO nanoparticles synthesized via facile wet chemical route with an average particle size ∼15 nm. The XRD analysis confirmed the growth of wurtzite phase of ZnO nanoparticles. Moreover, the optical properties of these nanoparticles were investigated by different spectroscopic techniques. The resulted nanoparticles exhibit intense green emission peaking at 530 nm (2.34 eV) upon 325 nm (3.81 eV) excitation. The photoluminescence (PL) intensity of visible emission depends upon the doping concentration of Mg. The PL intensity was found maximum up to 4% doping of Mg, and beyond it exhibits a decrees in emission. Furthermore, by varying the band gap from 3.50 to 3.61 eV, the PL spectra showed a near band edge (NBE) emission at wavelength around 370 nm (3.35 eV) and a broad deep level emission in the visible region. The obtained highly

  3. Structure and magnetic properties of chromium doped cobalt molybdenum nitrides

    Energy Technology Data Exchange (ETDEWEB)

    Guskos, Niko; Żołnierkiewicz, Grzegorz; Typek, Janusz; Guskos, Aleksander [Institute of Physics, Faculty of Mechanical Engineering and Mechatronics, West Pomeranian University of Technology, Szczecin, Piastów 48, 70-311 Szczecin (Poland); Adamski, Paweł; Moszyński, Dariusz [Institute of Inorganic Chemical Technology and Environment Engineering, West Pomeranian University of Technology, Szczecin, Pułaskiego 10, 70-322 Szczecin (Poland)

    2016-09-15

    Four nanocomposites containing mixed phases of Co{sub 3}Mo{sub 3}N and Co{sub 2}Mo{sub 3}N doped with chromium have been prepared. A linear fit is found for relation between Co{sub 2}Mo{sub 3}N and chromium concentrations. The magnetization in ZFC and FC modes at different temperatures (2–300 K) and in applied magnetic fields (up to 70 kOe) have been investigated. It has been detected that many magnetic characteristics of the studied four nanocomposites correlate not with the chromium concentration but with nanocrystallite sizes. The obtained results were interpreted in terms of magnetic core-shell model of a nanoparticle involving paramagnetic core with two magnetic sublattices and a ferromagnetic shell related to chromium doping. - Highlights: • A new chromium doped mixed Co-Mn-N nanocomposites were synthesized. • Surface ferromagnetism was detected in a wide temperature range. • Core-shell model was applied to explain nanocomposites magnetism.

  4. Ferromagnetism in Gd doped ZnO nanowires: A first principles study

    Energy Technology Data Exchange (ETDEWEB)

    Aravindh, S. Assa; Schwingenschloegl, Udo, E-mail: udo.schwingenschloegl@kaust.edu.sa, E-mail: iman.roqan@kaust.edu.sa; Roqan, Iman S., E-mail: udo.schwingenschloegl@kaust.edu.sa, E-mail: iman.roqan@kaust.edu.sa [Physical Sciences and Engineering Division, King Abdullah University of Science and Technology (KAUST), Thuwal 23955-6900 (Saudi Arabia)

    2014-12-21

    In several experimental studies, room temperature ferromagnetism in Gd-doped ZnO nanostructures has been achieved. However, the mechanism and the origin of the ferromagnetism remain controversial. We investigate the structural, magnetic, and electronic properties of Zn{sub 48}O{sub 48} nanowires doped with Gd, using density functional theory. Our findings indicate that substitutionally incorporated Gd atoms prefer occupying the surface Zn sites. Moreover, the formation energy increases with the distance between Gd atoms, signifying that no Gd-Gd segregation occurs in the nanowires within the concentration limit of ≤2%. Gd induces ferromagnetism in ZnO nanowires with magnetic coupling energy up to 21 meV in the neutral state, which increases with additional electron and O vacancy, revealing the role of carriers in magnetic exchange. The potential for achieving room temperature ferromagnetism and high T{sub C} in ZnO:Gd nanowires is evident from the large ferromagnetic coupling energy (200 meV) obtained with the O vacancy. Density of states shows that Fermi level overlaps with Gd f states with the introduction of O vacancy, indicating the possibility of s-f coupling. These results will assist in understanding experimental findings in Gd-doped ZnO nanowires.

  5. Structural and optical properties of Na-doped ZnO films

    Science.gov (United States)

    Akcan, D.; Gungor, A.; Arda, L.

    2018-06-01

    Zn1-xNaxO (x = 0.0-0.05) solutions have been synthesized by the sol-gel technique using Zinc acetate dihydrate and Sodium acetate which were dissolved into solvent and chelating agent. Na-doped ZnO nanoparticles were obtained from solutions to find phase and crystal structure. Na-doped ZnO films have been deposited onto glass substrate by using sol-gel dip coating system. The effects of dopant concentration on the structure, morphology, and optical properties of Na-doped ZnO thin films deposited on glass substrate are investigated. Characterization of Zn1-xNaxO nanoparticles and thin films are examined using differential thermal analysis (DTA)/thermogravimetric analysis (TGA), Scanning electron microscope (SEM) and X-Ray diffractometer (XRD). Optical properties of Zn1-xNaxO thin films were obtained by using PG Instruments UV-Vis-NIR spectrophotometer in 190-1100 nm range. The structure, morphology, and optical properties of thin films are presented.

  6. Ferromagnetism in Gd doped ZnO nanowires: A first principles study

    KAUST Repository

    Aravindh, S. Assa

    2014-12-19

    In several experimental studies, room temperature ferromagnetism in Gd-doped ZnO nanostructures has been achieved. However, the mechanism and the origin of the ferromagnetism remain controversial. We investigate the structural, magnetic, and electronic properties of Zn 48O48 nanowires doped with Gd, using density functional theory. Our findings indicate that substitutionally incorporated Gd atoms prefer occupying the surface Zn sites. Moreover, the formation energy increases with the distance between Gd atoms, signifying that no Gd-Gd segregation occurs in the nanowires within the concentration limit of ≤2%. Gd induces ferromagnetism in ZnO nanowires with magnetic coupling energy up to 21 meV in the neutral state, which increases with additional electron and O vacancy, revealing the role of carriers in magnetic exchange. The potential for achieving room temperature ferromagnetism and high TC in ZnO:Gd nanowires is evident from the large ferromagnetic coupling energy (200 meV) obtained with the O vacancy. Density of states shows that Fermi level overlaps with Gd f states with the introduction of O vacancy, indicating the possibility of s-f coupling. These results will assist in understanding experimental findings in Gd-doped ZnO nanowires.

  7. Structural and plasmonic properties of noble metal doped ZnO nanomaterials

    Science.gov (United States)

    Pathak, Trilok K.; Swart, H. C.; Kroon, R. E.

    2018-04-01

    Noble metal doped ZnO has been synthesized by the combustion method and the effect of different metals (Ag, Au, Pd) on the structural, morphological, optical, photoluminescence and localized surface plasmon resonance (LSPR) properties has been investigated. X-ray diffraction analysis revealed that the ZnO had a hexagonal wurtzite structure and the crystallite sizes were affected by the doping. The formation of noble metal nanoparticles (NPs) was investigated using transmission electron microscopy and diffuse reflectance spectra. The LSPR of the metallic NPs was predicted using Mie theory calculations. The absorption spectra were calculated using the Kubelka-Munk function and the optical bandgap varied from 3.06 to 3.18 eV for the different doping materials. The experimental results suggest that the origin of enhanced emission was due to direct interaction between the laser photons and the noble material NPs which in turn leads to photoemission transfer of electrons from the noble metals NPs to the conduction band of ZnO.

  8. Ferromagnetism in Gd doped ZnO nanowires: A first principles study

    KAUST Repository

    Aravindh, S. Assa; Schwingenschlö gl, Udo; Roqan, Iman S.

    2014-01-01

    In several experimental studies, room temperature ferromagnetism in Gd-doped ZnO nanostructures has been achieved. However, the mechanism and the origin of the ferromagnetism remain controversial. We investigate the structural, magnetic, and electronic properties of Zn 48O48 nanowires doped with Gd, using density functional theory. Our findings indicate that substitutionally incorporated Gd atoms prefer occupying the surface Zn sites. Moreover, the formation energy increases with the distance between Gd atoms, signifying that no Gd-Gd segregation occurs in the nanowires within the concentration limit of ≤2%. Gd induces ferromagnetism in ZnO nanowires with magnetic coupling energy up to 21 meV in the neutral state, which increases with additional electron and O vacancy, revealing the role of carriers in magnetic exchange. The potential for achieving room temperature ferromagnetism and high TC in ZnO:Gd nanowires is evident from the large ferromagnetic coupling energy (200 meV) obtained with the O vacancy. Density of states shows that Fermi level overlaps with Gd f states with the introduction of O vacancy, indicating the possibility of s-f coupling. These results will assist in understanding experimental findings in Gd-doped ZnO nanowires.

  9. Magnetic Properties of Gadolinium-Doped ZnO Films and Nanostructures

    KAUST Repository

    Roqan, Iman S.

    2016-08-29

    The magnetic properties of Gd-doped ZnO films and nanostructures are important to the development of next-generation spintronic devices. Here, we elucidate the significant role played by Gd-oxygen-deficiency defects in mediating/inducing ferromagnetic coupling in in situ Gd-doped ZnO thin films deposited at low oxygen pressure by pulsed laser deposition (PLD). Samples deposited at higher oxygen pressures exhibited diamagnetic responses. Vacuum annealing was used on these diamagnetic samples (grown at a relatively high oxygen pressures) to create oxygen- deficiency defects with the aim of demonstrating reproducibility of room-temperature ferromagnetism (RTFM). Samples annealed at oxygen environment exhibited super‐ paramagnetism and blocking-temperature effects. The samples possessed secondary phases; Gd segregation led to superparamagnetism. Theoretical studies showed a shift of the 4f level of Gd to the conduction band minimum (CBM) in Gd-doped ZnO nanowires, which led to an overlap with the Fermi level, resulting in strong exchange coupling and consequently RTFM.

  10. Cobalt

    International Nuclear Information System (INIS)

    Stolyarova, I.A.; Bunakova, N.Yu.

    1983-01-01

    The neutron-activation method for determining cobalt in rocks, polymetallic and iron ores and rockforming minerals at 2x10 -6 -5x10 -3 % content is developed. Cobalt determination is based on the formation under the effect of thermal neutrons of nuclear reactor of the 60 Co radioactive isotope by the 59 Co (n, γ) 60 Co reaction with radiation energy of the most intensive line of 1333 keV. Cobalt can be determined by the scheme of the multicomponent analysis from the sample with other elements. Co is determined in the solution after separation of all determinable by the scheme elements. The 60 Co intensity is measured by the mUltichannel gamma-spectrometer with Ge(Li)-detector

  11. Synthesis and characterization of cobalt doped nickel oxide thin films by spray pyrolysis method

    Science.gov (United States)

    Sathisha, D.; Naik, K. Gopalakrishna

    2018-05-01

    Cobalt (Co) doped nickel oxide (NiO) thin films were deposited on glass substrates at a temperature of about 400 °C by spray pyrolysis method. The effect of Co doping concentration on structural, optical and compositional properties of NiO thin films was investigated. X-ray diffraction result shows that the deposited thin films are polycrystalline in nature. Surface morphologies of the deposited thin films were observed by FESEM and AFM. EDS spectra showed the incorporation of Co dopants in NiO thin films. Optical properties of the grown thin films were characterized by UV-visible spectroscopy. It was found that the optical band gap energy and transmittance of the films decrease with increasing Co doping concentration.

  12. Synthesis characterization and sintering of cobalt-doped lanthanum chromite powders for use in SOFCs

    International Nuclear Information System (INIS)

    Yamagata, Chieko; Mello-Castanho, Sonia R.H.

    2009-01-01

    Doped lanthanum chromite is a promising as interconnect material because of its good conductivity at high temperatures and its stability in oxidizing and reducing atmospheres. Perovskite oxide powders of Co-doped lanthanum chromite were synthesized by dispersing precursor metal salt solutions in a polymer matrix followed by a thermal treatment. XRD patterns showed that a highly crystalline cobalt-doped lanthanum chromite was obtained. Fine perovskite powder with a surface area of 6.15 m 2 g -1 calcined at 700 deg C for 1 h, were obtained. After the sample sintered at 1450 deg C for 3h, the powder reached high densities exceeding 97% of the theoretical density. The proposed here has proved to be a very promising technique for the synthesis of lanthanum chromite powders. (author)

  13. Mg doping induced high structural quality of sol–gel ZnO nanocrystals: Application in photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Abed, Chayma; Bouzidi, Chaker [Laboratoire de Physico-chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, BP 95, Hammam-Lif 2050 (Tunisia); Elhouichet, Habib, E-mail: Habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, BP 95, Hammam-Lif 2050 (Tunisia); Département de Physique, Faculté des Sciences de Tunis, Université Tunis El Manar, Tunis 2092 (Tunisia); Gelloz, Bernard [Graduate School of Engineering, Nagoya University, 2-24-16 Furo-cho, Chikusa-ku, Nagoya, Aichi 464-8603 (Japan); Ferid, Mokhtar [Laboratoire de Physico-chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, BP 95, Hammam-Lif 2050 (Tunisia)

    2015-09-15

    Highlights: • ZnO nancrystals doped with Mg were prepared from sol–gel method. • Structural and optical properties of ZnO:Mg nanocrystals were investigated. • Good crystalline quality of ZnO nanocrystals was reported after Mg doping. • Good photocatalytic activity of Mg doped ZnO nanocrystals was demonstrated under sun light illumination. - Abstract: Undoped and Mg doped ZnO nanocrystals (NCs) ZnO:x%Mg (x = 1, 2, 3, and 5) were synthesized using sol–gel method. The structural and optical properties were investigated by X-ray diffraction (XRD), Raman spectroscopy, diffuse reflectivity, and photoluminescence (PL). XRD analysis demonstrates that all prepared samples present pure hexagonal wurtzite structure without any Mg related phases. The NCs size varies from 26.82 nm to 42.96 nm with Mg concentrations; it presents an optimal value for 2% of Mg. The Raman spectra are dominated by the E{sub 2high} mode. For highly Mg doping (5%), the occurrence of silent B{sub 1(low)} mode suggested that the Mg ions do substitute at Zn sites in the ZnO lattice The band gap energy was estimated from both Tauc and Urbach methods and found to be 3.39 eV for ZnO:2%Mg. The PL spectra exhibit two emission bands in the UV and visible range. Their evolution with Mg doping reveals the reduction of defect density in ZnO at low Mg doping by filling Zn vacancies. In addition, it was found that further Mg doping, above 2%, improves the photocatalytic activity of ZnO NCs for photodegradation of Rhodamine B (RhB) under sunlight irradiation. The efficient electron–hole separation is the main factor responsible for the enhancement of photocatalytic performance of Mg doped ZnO NCs. Through this work, we show that by varying the Mg contents in ZnO, this material can be a potential candidate for both optoelectronic and photocatalytic applications.

  14. Preparation, structural and luminescent properties of nanocrystalline ZnO films doped Ag by close space sublimation method

    Science.gov (United States)

    Khomchenko, Viktoriya; Mazin, Mikhail; Sopinskyy, Mykola; Lytvyn, Oksana; Dan'ko, Viktor; Piryatinskii, Yurii; Demydiuk, Pavlo

    2018-05-01

    The simple way for silver doping of ZnO films is presented. The ZnO films were prepared by reactive rf-magnetron sputtering on silicon and sapphire substrates. Ag doping is carried out by sublimation of the Ag source located at close space at atmospheric pressure in air. Then the ZnO and ZnO-Ag films were annealed in wet media. The microstructure and optical properties of the films were compared and studied by atomic force microscopy (AFM), X-ray diffraction (XRD), photoluminescence (PL) and cathodoluminescence (CL). XRD results indicated that all the ZnO films have a polycrystalline hexagonal structure and a preferred orientation with the c-axis perpendicular to the substrate. The annealing and Ag doping promote increasing grain's sizes and modification of grain size distribution. The effect of substrate temperature, substrate type, Ag doping and post-growth annealing of the films was studied by PL spectroscopy. The effect of Ag doping was obvious and identical for all the films, namely the wide visible bands of PL spectra are suppressed by Ag doping. The intensity of ultraviolet band increased 15 times as compared to their reference films on sapphire substrate. The ultraviolet/visible emission ratio was 20. The full width at half maximum (FWHM) for a 380 nm band was 14 nm, which is comparable with that of epitaxial ZnO. The data implies the high quality of ZnO-Ag films. Possible mechanisms to enhance UV emission are discussed.

  15. Structural and Magnetic Properties of Mn doped ZnO Thin Film Deposited by Pulsed Laser Deposition

    KAUST Repository

    Baras, Abdulaziz

    2011-07-01

    Diluted magnetic oxide (DMO) research is a growing field of interdisciplinary study like spintronic devices and medical imaging. A definite agreement among researchers concerning the origin of ferromagnetism in DMO has yet to be reached. This thesis presents a study on the structural and magnetic properties of DMO thin films. It attempts to contribute to the understanding of ferromagnetism (FM) origin in DMO. Pure ZnO and Mn doped ZnO thin films have been deposited by pulsed laser deposition (PLD) using different deposition conditions. This was conducted in order to correlate the change between structural and magnetic properties. Structural properties of the films were characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM). The superconducting quantum interference device (SQUID) was used to investigate the magnetic properties of these films. The structural characterizations showed that the quality of pure ZnO and Mn doped ZnO films increased as oxygen pressure (PO) increased during deposition. All samples were insulators. In Mn doped films, Mn concentration decreased as PO increased. The Mn doped ZnO samples were deposited at 600˚C and oxygen pressure from 50-500mTorr. All Mn doped films displayed room temperature ferromagnetism (RTFM). However, at 5 K a superparamagnetic (SPM) behavior was observed in these samples. This result was accounted for by the supposition that there were secondary phase(s) causing the superparamagnetic behavior. Our findings hope to strengthen existing research on DMO origins and suggest that secondary phases are the core components that suppress the ferromagnetism. Although RTFM and SPM at low temperature has been observed in other systems (e.g., Co doped ZnO), we are the first to report this behavior in Mn doped ZnO. Future research might extend the characterization and exploration of ferromagnetism in this system.

  16. Structural and optical properties of Na doped ZnO nanocrystals: Application to solar photocatalysis

    Energy Technology Data Exchange (ETDEWEB)

    Tabib, Asma; Bouslama, Wiem [Laboratoire de Physico-Chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, B.P. 95 Hammam-Lif, 2050 (Tunisia); Sieber, Brigitte; Addad, Ahmed [UMET, UMR, CNRS 8207, Université Lille 1, 59665 Villeneuve d’Ascq Cédex (France); Elhouichet, Habib, E-mail: habib.elhouichet@fst.rnu.tn [Laboratoire de Physico-Chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, B.P. 95 Hammam-Lif, 2050 (Tunisia); Département de Physique, Faculté des Sciences de Tunis, University of Tunis, ElManar 2092 (Tunisia); Férid, Mokhtar [Laboratoire de Physico-Chimie des Matériaux Minéraux et leurs Applications, Centre National de Recherches en Sciences des Matériaux, B.P. 95 Hammam-Lif, 2050 (Tunisia); Boukherroub, Rabah [Institut d’Electronique de Microélectronique et de Nanotechnologie (IEMN), UMR, CNRS, 8520 Avenue Pointcarré, BP 60069, 59652 Villeneuve d’Ascq (France)

    2017-02-28

    Highlights: • Na doped ZnO nanocrystals were prepared via sol–gel method. • A substitution of Zn{sup 2+} by Na{sup +} was demonstrated. • Low Na concentration induces higher photocatalytic activity under solar irradiation. • Oxygen vacancies guided the processes of charge separation. - Abstract: Na doped ZnO nanocrystals (NCs) were successfully produced by sol–gel process and characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution TEM (HRTEM), Raman scattering, UV–vis diffuse reflectance spectroscopy and photoluminescence (PL). XRD analysis indicated that all the prepared samples present pure hexagonal wurtzite structure without any Na related phases. The lattice distortion, calculated using Williamson hall equation, induces stress and a reduction of NCs size from 71.4 to 24.5 nm. TEM images showed NCs with hexagonal shape and a rather uniform size distribution. The selected area electron diffraction (SAED) patterns confirmed the high crystal quality along the 〈101〉 direction and is consistent with the hexagonal wurtzite structure of ZnO. The Raman spectra are dominated by E{sub 2}{sup high} mode of ZnO. High Na doping shows the occurrence of anomalous local vibrational Raman modes close to 270 and 513 cm{sup −1} that are related to intrinsic host lattice defects and distortion, respectively. Optical band gap was found to vary with Na content. Photoluminescence (PL) spectra indicate the presence of a high density of defects in ZnO NCs which are mainly oxygen vacancies. Finally, the obtained NCs were used as a photocatalyst to degrade Rhodamine B (RhB) in solution, under solar irradiation. Na doping enhances the photocatalytic activity of ZnO NCs till an optimum concentration of 0.5% where a full degradation was observed after 120 min of sun light irradiation. Furthermore, this sample presents a good cycling stability and reusability. Based on scavangers test, it was found that both superoxide and

  17. Study of defects and vacancies in structural properties of Mn, co-doped oxides: ZnO

    Science.gov (United States)

    Kumar, Harish; Kaushik, A.; Alvi, P. A.; Dalela, B.; Dalela, S.

    2018-05-01

    The paper deals with the Structural properties on Mn, Co doped oxides ZnO samples using XRD, Positron Annihilation Lifetime (PAL) Spectra and Raman Spectra. The Mn, Co doped ZnO samples crystallize in a wurtzite structure without any impurity phases in XRD Spectra. The defect state of these samples has been investigated by using positron annihilation lifetime (PAL) spectroscopy technique in which all the relevant lifetime parameters are measured for all the spectra. The results are explained in the direction of doping concentration in these samples in terms of defects structure on Zn lattice site VZn and oxygen defects Vo.

  18. Influence of cobalt doping on structural and magnetic properties of BiFeO3 nanoparticles

    Science.gov (United States)

    Khan, U.; Adeela, N.; Javed, K.; Riaz, S.; Ali, H.; Iqbal, M.; Han, X. F.; Naseem, S.

    2015-11-01

    Nanocrystalline cobalt-doped bismuth ferrites with general formula of BiFe1- δ Co δ O3 (0 ≤ δ ≤ 0.1) have been synthesized using solution evaporation method. Structure and phase identification was performed with X-ray diffraction (XRD) technique. The results confirm the formation of rhombohedral-distorted Perovskite structure with R3c symmetry. A decrease in lattice parameters and an increase in X-ray density have been observed with increasing cobalt concentration in BiFeO3. Particle size determined by transmission electron microscope was in good agreement with XRD, i.e., 39 nm. Room-temperature coercivity and saturation magnetization of nanoparticles were increased up to 7.5 % of cobalt doping. Low-temperature magnetic measurements of selected sample showed increasing behavior in saturation magnetization, coercivity, effective magnetic moments, and anisotropy constant. An increase in coercivity with decrease in temperature followed theoretical model of Kneller's law, while modified Bloch's model was employed for saturation magnetization in temperature range of 5-300 K.

  19. Magnetic studies of cobalt doped barium hexaferrite nanoparticles prepared by modified sol-gel method

    International Nuclear Information System (INIS)

    Shalini, M. Govindaraj; Sahoo, Subasa C.

    2016-01-01

    M-type barium hexaferrite (BaFe_1_2O_1_9) and cobalt doped barium hexaferrite (BaFe_1_1CoO_1_9) nanopowders were synthesized by modified sol-gel auto-combustion technique and were annealed at 900°C in air for 4 hours. The annealed powders were studied in the present work and X-ray diffraction studies showed pure phase formation after annealing. The average grain size in the nanopowder sample was decreased after doping. Magnetization value of 60 emu/g was observed at 300 K for the barium hexaferrite and was reduced to 54 emu/g after doping. The coercivity of 5586 Oe was observed at 300 K for the undoped sample and was found to be decreased in the doped sample. As the measurement temperature was decreased from 300 K to 60 K, magnetization value was increased in both the samples compared to those at 300 K. The coercivity of the undoped sample was found to decrease whereas it was increased for the doped sample at 60 K. The observed magnetic properties may be understood on the basis of modified exchange interaction and anisotropy in the doped sample compared to that of pure barium hexaferrite.

  20. Enhanced photoluminescence and Raman properties of Al-Doped ZnO nanostructures prepared using thermal chemical vapor deposition of methanol assisted with heated brass.

    Directory of Open Access Journals (Sweden)

    Tamil Many K Thandavan

    Full Text Available Vapor phase transport (VPT assisted by mixture of methanol and acetone via thermal evaporation of brass (CuZn was used to prepare un-doped and Al-doped zinc oxide (ZnO nanostructures (NSs. The structure and morphology were characterized by field emission scanning electron microscopy (FESEM and x-ray diffraction (XRD. Photoluminescence (PL properties of un-doped and Al-doped ZnO showed significant changes in the optical properties providing evidence for several types of defects such as zinc interstitials (Zni, oxygen interstitials (Oi, zinc vacancy (Vzn, singly charged zinc vacancy (VZn-, oxygen vacancy (Vo, singly charged oxygen vacancy (Vo+ and oxygen anti-site defects (OZn in the grown NSs. The Al-doped ZnO NSs have exhibited shifted PL peaks at near band edge (NBE and red luminescence compared to the un-doped ZnO. The Raman scattering results provided evidence of Al doping into the ZnO NSs due to peak shift from 145 cm-1 to an anomalous peak at 138 cm-1. Presence of enhanced Raman signal at around 274 and 743 cm-1 further confirmed Al in ZnO NSs. The enhanced D and G band in all Al-doped ZnO NSs shows possible functionalization and doping process in ZnO NSs.

  1. Enhanced photoluminescence and Raman properties of Al-Doped ZnO nanostructures prepared using thermal chemical vapor deposition of methanol assisted with heated brass.

    Science.gov (United States)

    Thandavan, Tamil Many K; Gani, Siti Meriam Abdul; San Wong, Chiow; Md Nor, Roslan

    2015-01-01

    Vapor phase transport (VPT) assisted by mixture of methanol and acetone via thermal evaporation of brass (CuZn) was used to prepare un-doped and Al-doped zinc oxide (ZnO) nanostructures (NSs). The structure and morphology were characterized by field emission scanning electron microscopy (FESEM) and x-ray diffraction (XRD). Photoluminescence (PL) properties of un-doped and Al-doped ZnO showed significant changes in the optical properties providing evidence for several types of defects such as zinc interstitials (Zni), oxygen interstitials (Oi), zinc vacancy (Vzn), singly charged zinc vacancy (VZn-), oxygen vacancy (Vo), singly charged oxygen vacancy (Vo+) and oxygen anti-site defects (OZn) in the grown NSs. The Al-doped ZnO NSs have exhibited shifted PL peaks at near band edge (NBE) and red luminescence compared to the un-doped ZnO. The Raman scattering results provided evidence of Al doping into the ZnO NSs due to peak shift from 145 cm-1 to an anomalous peak at 138 cm-1. Presence of enhanced Raman signal at around 274 and 743 cm-1 further confirmed Al in ZnO NSs. The enhanced D and G band in all Al-doped ZnO NSs shows possible functionalization and doping process in ZnO NSs.

  2. Effect of Al and Fe doping in ZnO on magnetic and magneto-transport properties

    International Nuclear Information System (INIS)

    Kumar, Santosh; Deepika; Tripathi, Malvika; Vaibhav, Pratyush; Kumar, Aman; Kumar, Ritesh; Choudhary, R.J.; Phase, D.M.

    2016-01-01

    The structural, magnetic and magneto-transport of undoped ZnO, Zn_0_._9_7Al_0_._0_3O, Zn_0_._9_5Fe_0_._0_5O and Zn_0_._9_2Al_0_._0_3Fe_0_._0_5O thin films grown on Si(100) substrate using pulsed laser deposition were investigated. The single phase nature of the films is confirmed by X-ray diffraction and Raman spectroscopy measurements. The possibility of Fe metal cluster in Fe doped/co-doped films is ruled out by Fe 2p core level photoelectron spectra. From O 1s core level spectra it is observed that oxygen vacancy is present in all the films. The undoped ZnO film shows magnetic ordering below ∼175 K, whereas Fe doped/codoped samples show magnetic ordering even at 300 K. The Al doped sample reveals paramagnetic behavior. The magneto-transport measurements suggest that the mobile carriers undergo exchange interaction with local magnetic moments. - Highlights: • Al, Fe, Al–Fe co-doped and undoped films of ZnO are deposited on Si by PLD. • Single phase (002) oriented Wurtzite ZnO phase is formed for all films. • Fe doped and Fe–Al co-doped ZnO films reveal magnetic hysteresis at 300 K. • Negative magnetoresistance is observed in undoped and Fe–Al co-doped ZnO film. • It is apparent that charge carriers are coupled with the local magnetic moment.

  3. Effect of Al and Fe doping in ZnO on magnetic and magneto-transport properties

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Santosh, E-mail: skphysics@yahoo.co.in [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Deepika [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Tripathi, Malvika [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India); Vaibhav, Pratyush [Jaypee University of Engineering and Technology, Guna 473226, Madhya Pradesh (India); Kumar, Aman [Indian Institute of Technology, Roorkee (India); Kumar, Ritesh [Department of Physics, College of Commerce, Arts & Science, Patna 800020, Bihar (India); Choudhary, R.J., E-mail: ram@csr.res.in [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India); Phase, D.M. [UGC DAE, Consortium for scientific research, Indore 452001, Madhya Pradesh (India)

    2016-12-01

    The structural, magnetic and magneto-transport of undoped ZnO, Zn{sub 0.97}Al{sub 0.03}O, Zn{sub 0.95}Fe{sub 0.05}O and Zn{sub 0.92}Al{sub 0.03}Fe{sub 0.05}O thin films grown on Si(100) substrate using pulsed laser deposition were investigated. The single phase nature of the films is confirmed by X-ray diffraction and Raman spectroscopy measurements. The possibility of Fe metal cluster in Fe doped/co-doped films is ruled out by Fe 2p core level photoelectron spectra. From O 1s core level spectra it is observed that oxygen vacancy is present in all the films. The undoped ZnO film shows magnetic ordering below ∼175 K, whereas Fe doped/codoped samples show magnetic ordering even at 300 K. The Al doped sample reveals paramagnetic behavior. The magneto-transport measurements suggest that the mobile carriers undergo exchange interaction with local magnetic moments. - Highlights: • Al, Fe, Al–Fe co-doped and undoped films of ZnO are deposited on Si by PLD. • Single phase (002) oriented Wurtzite ZnO phase is formed for all films. • Fe doped and Fe–Al co-doped ZnO films reveal magnetic hysteresis at 300 K. • Negative magnetoresistance is observed in undoped and Fe–Al co-doped ZnO film. • It is apparent that charge carriers are coupled with the local magnetic moment.

  4. Microstructural and electrical characteristics of rare earth oxides doped ZnO varistor films

    Science.gov (United States)

    Jiao, Lei; Mei, Yunzhu; Xu, Dong; Zhong, Sujuan; Ma, Jia; Zhang, Lei; Bao, Li

    2018-02-01

    ZnO-Bi2O3 varistor films doped with two kinds of rare earth element oxides (Lu2O3 and Yb2O3) were prepared by the sol-gel method. The effects of Lu2O3/Yb2O3 doping on the microstructure and electrical characteristics of ZnO-Bi2O3 varistor films were investigated. All samples show a homogenized morphology and an improved nonlinear relationship between the electric field (E) and current density (I). Both Yb2O3 and Lu2O3 doping can decrease the grain size of ZnO-Bi2O3 varistor films and improve the electrical properties, which have a positive effect on the development of ZnO varistor ceramics. Yb2O3 doping significantly increases the dielectric constant at low frequency. 0.2 mol. % Yb2O3 doped ZnO-Bi2O3 varistor films exhibit the highest nonlinear coefficient (2.5) and the lowest leakage current (328 μA) among Lu2O3/Yb2O3 doped ZnO-Bi2O3 varistor films. Similarly, 0.1 mol. % Lu2O3 doping increases the nonlinear coefficient to 1.9 and decrease the leakage current to 462 μA.

  5. Efficiency of Nb-Doped ZnO Nanoparticles Electrode for Dye-Sensitized Solar Cells Application

    Science.gov (United States)

    Anuntahirunrat, Jirapat; Sung, Youl-Moon; Pooyodying, Pattarapon

    2017-09-01

    The technological of Dye-sensitized solar cells (DSSCs) had been improved for several years. Due to its simplicity and low cost materials with belonging to the part of thin films solar cells. DSSCs have numerous advantages and benefits among the other types of solar cells. Many of the DSSC devices had use organic chemical that produce by specific method to use as thin film electrodes. The organic chemical that widely use to establish thin film electrodes are Zinc Oxide (ZnO), Titanium Dioxide (TiO2) and many other chemical substances. Zinc oxide (ZnO) nanoparticles had been used in DSSCs applications as thin film electrodes. Nanoparticles are a part of nanomaterials that are defined as a single particles 1-100 nm in diameter. From a few year ZnO widely used in DSSC applications because of its optical, electrical and many others properties. In particular, the unique properties and utility of ZnO structure. However the efficiency of ZnO nanoparticles based solar cells can be improved by doped various foreign impurity to change the structures and properties. Niobium (Nb) had been use as a dopant of metal oxide thin films. Using specification method to doped the ZnO nanoparticles thin film can improved the efficiencies of DSSCs. The efficiencies of Nb-doped ZnO can be compared by doping 0 at wt% to 5 at wt% in ZnO nanoparticles thin films that prepared by the spin coating method. The thin film electrodes doped with 3 at wt% represent a maximum efficiencies with the lowest resistivity of 8.95×10-4 Ω·cm.

  6. Exploration of Al-Doped ZnO in Photovoltaic Thin Films

    Science.gov (United States)

    Ciccarino, Christopher; Sahiner, M. Alper

    The electrical properties of Al doped ZnO-based thin films represent a potential advancement in the push for increasing solar cell efficiency. Doping with Aluminum will theoretically decrease resistivity of the film and therefore achieve this potential as a viable option in the P-N junction phase of photovoltaic cells. The n-type semi-conductive characteristics of the ZnO layer will theoretically be optimized with the addition of Aluminum carriers. In this study, Aluminum doping concentrations ranging from 1-3% by mass were produced, analyzed, and compared. Films were developed onto ITO coated glass using the Pulsed Laser Deposition technique. Target thickness was 250 nm and ellipsometry measurements showed uniformity and accuracy in this regard. Active dopant concentrations were determined using Hall Effect measurements. Efficiency measurements showed possible applications of this doped compound, with upwards of 7% efficiency measured, using a Keithley 2602 SourceMeter set-up. XRD scans showed highly crystalline structures, with effective Al intertwining of the hexagonal wurtzile ZnO molecular structure. This alone indicates a promising future of collaboration between these two materials.

  7. Assessment of the abatement of acelsulfame K using cerium doped ZnO as photocatalyst

    International Nuclear Information System (INIS)

    Calza, P.; Gionco, C.; Giletta, M.; Kalaboka, M.; Sakkas, V.A.; Albanis, T.; Paganini, M.C.

    2017-01-01

    Highlights: • Hydrothermal synthesis and characterization of Ce doped ZnO. • The abatement of ACE K is assessed in ultrapure water and in river water matrix. • Demonstrated higher degradation activity than P25 under visible light. • The degradation activity is less affected in river water than for P25. - Abstract: In the present study, we investigated the possibility to abate Acesulfame K, a persistent emerging contaminant, in aqueous media using zinc oxide based materials. For this purpose, bare and Ce-doped zinc oxide was prepared via an easy and cheap hydrothermal process using different cerium salts as precursors. Their photocatalytic performance was evaluated in different media, namely ultrapure and river water under both UV–vis and visible light. Commercial TiO_2 P25 was also employed and used as a reference photocatalyst for comparison purposes. The obtained results pointed out that cerium doped zinc oxide composites exhibit higher performance than TiO_2 P25, especially under visible light and in the presence of organic matter, when the activity of the latter is greatly depressed. In particular, ZnO doped with cerium (1%) was the most effective material, and could be a promising alternative to TiO_2 P25, especially in the treatment of natural waters.

  8. Structural and optical properties of cobalt doped multiferroics BiFeO3 nanostructure thin films

    Science.gov (United States)

    Prasannakumara, R.; Naik, K. Gopalakrishna

    2018-05-01

    Bismuth ferrite (BiFeO3) and Cobalt doped BiFeO3 (BiFe1-XCoXO3) nanostructure thin films were deposited on glass substrates by the sol-gel spin coating method. The X-ray diffraction patterns (XRD) of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films showed distorted rhombohedral structure. The shifting of peaks to higher angles was observed in cobalt doped BiFeO3. The surface morphology of the BiFeO3 and BiFe1-XCoXO3 nanostructure thin films were studied using FESEM, an increase in grain size was observed as Co concentration increases. The thickness of the nanostructure thin films was examined using FESEM cross-section. The EDX studies confirmed the elemental composition of the grown BiFeO3 and BiFe1-XCoXO3 nanostructure thin films. The optical characterizations of the grown nanostructure thin films were carried out using FTIR, it confirms the existence of Fe-O and Bi-O bands and UV-Visible spectroscopy shows the increase in optical band gap of the BiFeO3 nanostructure thin films with Co doping by ploting Tauc plot.

  9. Single cobalt sites in mesoporous N-doped carbon matrix for selective catalytic hydrogenation of nitroarenes

    KAUST Repository

    Sun, Xiaohui

    2017-11-20

    A supported cobalt catalyst with atomically dispersed Co-Nx sites (3.5 wt% Co) in a mesoporous N-doped carbon matrix (named Co@mesoNC) is synthesized by hydrolysis of tetramethyl orthosilicate (TMOS) in a Zn/Co bimetallic zeolitic imidazolate framework (BIMZIF(Co,Zn)), followed by high-temperature pyrolysis and SiO2 leaching. A combination of TEM, XRD XPS and X-ray absorption spectroscopy studies confirm the absence of cobalt nanoparticles and indicate that these highly dispersed cobalt species are present in the form of Co-Nx. The exclusive formation of Co-Nx sites in the carbon matrix is attributed to the presence of a large amount of Zn and N in the BIMZIF precursor together with the presence of SiO2 in the pore space of this framework, extending the initial spatial distance between cobalt atoms and thereby impeding their agglomeration. The presence of SiO2 during high-temperature pyrolysis is proven crucial to create mesoporosity and a high BET area and pore volume in the N-doped carbon support (1780 m2 g−1, 1.54 cm3 g−1). This heterogeneous Co@mesoNC catalyst displays high activity and selectivity (>99%) for the selective hydrogenation of nitrobenzene to aniline at mild conditions (0.5–3 MPa, 343–383 K). When more challenging substrates (functionalized nitroarenes) are hydrogenated, the catalyst Co@mesoNC displays an excellent chemoselectivity to the corresponding substituted anilines.The presence of mesoporosity improves mass transport of reactants and/or products and the accessibility of the active Co-Nx sites, and greatly reduces deactivation due to fouling.

  10. Single cobalt sites in mesoporous N-doped carbon matrix for selective catalytic hydrogenation of nitroarenes

    KAUST Repository

    Sun, Xiaohui; Olivos-Suarez, Alma I.; Osadchii, Dmitrii; Romero, Maria Jose Valero; Kapteijn, Freek; Gascon, Jorge

    2017-01-01

    A supported cobalt catalyst with atomically dispersed Co-Nx sites (3.5 wt% Co) in a mesoporous N-doped carbon matrix (named Co@mesoNC) is synthesized by hydrolysis of tetramethyl orthosilicate (TMOS) in a Zn/Co bimetallic zeolitic imidazolate framework (BIMZIF(Co,Zn)), followed by high-temperature pyrolysis and SiO2 leaching. A combination of TEM, XRD XPS and X-ray absorption spectroscopy studies confirm the absence of cobalt nanoparticles and indicate that these highly dispersed cobalt species are present in the form of Co-Nx. The exclusive formation of Co-Nx sites in the carbon matrix is attributed to the presence of a large amount of Zn and N in the BIMZIF precursor together with the presence of SiO2 in the pore space of this framework, extending the initial spatial distance between cobalt atoms and thereby impeding their agglomeration. The presence of SiO2 during high-temperature pyrolysis is proven crucial to create mesoporosity and a high BET area and pore volume in the N-doped carbon support (1780 m2 g−1, 1.54 cm3 g−1). This heterogeneous Co@mesoNC catalyst displays high activity and selectivity (>99%) for the selective hydrogenation of nitrobenzene to aniline at mild conditions (0.5–3 MPa, 343–383 K). When more challenging substrates (functionalized nitroarenes) are hydrogenated, the catalyst Co@mesoNC displays an excellent chemoselectivity to the corresponding substituted anilines.The presence of mesoporosity improves mass transport of reactants and/or products and the accessibility of the active Co-Nx sites, and greatly reduces deactivation due to fouling.

  11. Influence of Cobalt Doping on the Physical Properties of Zn0.9Cd0.1S Nanoparticles

    Directory of Open Access Journals (Sweden)

    Gupta Hari Om

    2009-01-01

    Full Text Available Abstract Zn0.9Cd0.1S nanoparticles doped with 0.005–0.24 M cobalt have been prepared by co-precipitation technique in ice bath at 280 K. For the cobalt concentration >0.18 M, XRD pattern shows unidentified phases along with Zn0.9Cd0.1S sphalerite phase. For low cobalt concentration (≤0.05 M particle size, d XRDis ~3.5 nm, while for high cobalt concentration (>0.05 M particle size decreases abruptly (~2 nm as detected by XRD. However, TEM analysis shows the similar particle size (~3.5 nm irrespective of the cobalt concentration. Local strain in the alloyed nanoparticles with cobalt concentration of 0.18 M increases ~46% in comparison to that of 0.05 M. Direct to indirect energy band-gap transition is obtained when cobalt concentration goes beyond 0.05 M. A red shift in energy band gap is also observed for both the cases. Nanoparticles with low cobalt concentrations were found to have paramagnetic nature with no antiferromagnetic coupling. A negative Curie–Weiss temperature of −75 K with antiferromagnetic coupling was obtained for the high cobalt concentration.

  12. Highly efficient cobalt-doped carbon nitride polymers for solvent-free selective oxidation of cyclohexane

    Directory of Open Access Journals (Sweden)

    Yu Fu

    2017-04-01

    Full Text Available Selective oxidation of saturated hydrocarbons with molecular oxygen has been of great interest in catalysis, and the development of highly efficient catalysts for this process is a crucial challenge. A new kind of heterogeneous catalyst, cobalt-doped carbon nitride polymer (g-C3N4, was harnessed for the selective oxidation of cyclohexane. X-ray diffraction, Fourier transform infrared spectra and high resolution transmission electron microscope revealed that Co species were highly dispersed in g-C3N4 matrix and the characteristic structure of polymeric g-C3N4 can be retained after Co-doping, although Co-doping caused the incomplete polymerization to some extent. Ultraviolet–visible, Raman and X-ray photoelectron spectroscopy further proved the successful Co doping in g-C3N4 matrix as the form of Co(IIN bonds. For the selective oxidation of cyclohexane, Co-doping can markedly promote the catalytic performance of g-C3N4 catalyst due to the synergistic effect of Co species and g-C3N4 hybrid. Furthermore, the content of Co largely affected the activity of Co-doped g-C3N4 catalysts, among which the catalyst with 9.0 wt% Co content exhibited the highest yield (9.0% of cyclohexanone and cyclohexanol, as well as a high stability. Meanwhile, the reaction mechanism over Co-doped g-C3N4 catalysts was elaborated. Keywords: Selective oxidation of cyclohexane, Oxygen oxidant, Carbon nitride, Co-doping

  13. Photocatalytic degradation of Reactive Black 5 and Malachite Green with ZnO and lanthanum doped nanoparticles

    International Nuclear Information System (INIS)

    Kaneva, N; Bojinova, A; Papazova, K

    2016-01-01

    Here we report the preparation of ZnO particles with different concentrations of La 3 + doping (0, 0.5 and 1 wt%) via sol-gel method. The nanoparticles are synthesized directly from Zn(CH 3 COO) 2 .2H 2 O in the presence of 1-propanol and triethylamine at 80°C. The conditions are optimized to obtain particles of uniform size, easy to isolate and purify. The nanoparticles are characterized by SEM, XRD and UV-Vis analysis. The photocatalytic properties of pure and La-doped ZnO are studied in the photobleaching of Malachite Green (MG) and Reactive Black 5 (RB5) dyes in aqueous solutions upon UV illumination. It is observed that the rate constant increases with the La loading up to 1 wt%. The doping helps to achieve complete mineralization of MG within a short irradiation time. 1 wt% La-doped ZnO nanoparticles show highest photocatalytic activity. The La 3+ doped ZnO particles degrade faster RB5 than MG. The reason is weaker N=N bond in comparison with the C-C bond between the central carbon atom and N,N-dimethylaminobenzyl in MG. The as-prepared ZnO particles can find practical application in photocatalytic purification of textile wastewaters. (paper)

  14. Half-metallic ferromagnetism in Cu-doped zinc-blende ZnO from first principles study

    International Nuclear Information System (INIS)

    Li, X.F.; Zhang, J.; Xu, B.; Yao, K.L.

    2012-01-01

    Electronic structures and magnetism of Cu-doped zinc-blende ZnO have been investigated by the first-principle method based on density functional theory (DFT). The results show that Cu can induce stable ferromagnetic ground state. The magnetic moment of supercell including single Cu atom is 1.0 μ B . Electronic structure shows that Cu-doped zinc-blende ZnO is a p-type half-metallic ferromagnet. The half-metal property is mainly attribute to the crystal field splitting of Cu 3d orbital, and the ferromagnetism is dominated by the hole-mediated double exchange mechanism. Therefore, Cu-doped zinc-blende ZnO should be useful in semiconductor spintronics and other applications. - Highlights: → Magnetism of Cu-doped zinc-blende ZnO. → Cu-doped zinc-blende ZnO shows interesting half-metal character. → Total energies calculations reveal that Cu can induce ferromagnetic ground state. → Ferromagnetism dominated by the hole-mediated double exchange mechanism.

  15. Phosphorus acceptor doped ZnO nanowires prepared by pulsed-laser deposition

    International Nuclear Information System (INIS)

    Cao, B Q; Lorenz, M; Rahm, A; Wenckstern, H von; Czekalla, C; Lenzner, J; Benndorf, G; Grundmann, M

    2007-01-01

    Phosphorus-doped ZnO (ZnO:P) nanowires were successfully prepared by a novel high-pressure pulsed-laser deposition process using phosphorus pentoxide as the dopant source. Detailed cathodoluminescence studies of single ZnO:P nanowires revealed characteristic phosphorus acceptor-related peaks: neutral acceptor-bound exciton emission (A 0 , X, 3.356 eV), free-to-neutral-acceptor emission (e, A 0 , 3.314 eV), and donor-to-acceptor pair emission (DAP, ∼3.24 and ∼3.04 eV). This means that stable acceptor levels with a binding energy of about 122 meV have been induced in the nanowires by phosphorus doping. Moreover, the induced acceptors are distributed homogeneously along the doped nanowires

  16. Ab-initio valence band spectra of Al, In doped ZnO

    International Nuclear Information System (INIS)

    Palacios, P.; Sanchez, K.; Wahnon, P.

    2009-01-01

    We present the structural and electronic characterization of n-doped (Aluminium or Indium) ZnO and the effect of the doping on the calculated photoelectron spectroscopy (PES) spectra. The fully-relaxed calculations have been made using the density functional theory, including a Hubbard correlation term that increases the Zn-3d states binding energy, and which matches the experimental values. The effect of Oxygen vacancies is also included in our study. Our results show that the new Al or In-donor levels appearing in the conduction band hybridize with the Oxygen-2p states and help decrease the resistivity of these doped systems as was found experimentally. The calculated PES spectra show a small enhancement in the intensity close to the chemical potential as a result of these new Al or In levels

  17. High-quality ZnO growth, doping, and polarization effect

    Science.gov (United States)

    Kun, Tang; Shulin, Gu; Jiandong, Ye; Shunming, Zhu; Rong, Zhang; Youdou, Zheng

    2016-03-01

    The authors have reported their recent progress in the research field of ZnO materials as well as the corresponding global advance. Recent results regarding (1) the development of high-quality epitaxy techniques, (2) the defect physics and the Te/N co-doping mechanism for p-type conduction, and (3) the design, realization, and properties of the ZnMgO/ZnO hetero-structures have been shown and discussed. A complete technology of the growth of high-quality ZnO epi-films and nano-crystals has been developed. The co-doping of N plus an iso-valent element to oxygen has been found to be the most hopeful path to overcome the notorious p-type hurdle. High mobility electrons have been observed in low-dimensional structures utilizing the polarization of ZnMgO and ZnO. Very different properties as well as new physics of the electrons in 2DEG and 3DES have been found as compared to the electrons in the bulk. Project supported by the National Natural Science Foundation of China (Nos. 61025020, 61274058, 61322403, 61504057, 61574075), the Natural Science Foundation of Jiangsu Province (Nos. BK2011437, BK20130013, BK20150585), the Priority Academic Program Development of Jiangsu Higher Education Institutions, and the Fundamental Research Funds for the Central Universities.

  18. Thermal growth and cathodoluminescence of Bi doped ZnO nanowires and rods

    Energy Technology Data Exchange (ETDEWEB)

    Aleman, B; Hidalgo, P; Fernandez, P; Piqueras, J, E-mail: balemanl@fis.ucm.e [Departamento de Fisica de Materiales, Facultad de Ciencias FIsicas, Universidad Complutense de Madrid, 28040 Madrid (Spain)

    2009-11-21

    Bi doped ZnO nanowires and rods have been grown by a catalyst free evaporation-deposition method with precursors containing either ZnO and Bi{sub 2}O{sub 3} or ZnS and Bi{sub 2}O{sub 3} powders. The use of ZnS as a precursor was found to lead to a higher density of nano- and microstructures at lower temperatures than by using ZnO. Energy dispersive x-ray spectroscopy (EDS) shows that the Bi content in the wires and rods is in the range 0.15-0.35 at%. Bi incorporation was found to induce a red shift of the near band gap luminescence but no quantitative correlation between the shift and the amount of Bi, as measured by EDS, was observed. The I-V curves of single Bi doped wires had linear behaviour at low current and non-linear behaviour for high currents, qualitatively similar to that of undoped wires.

  19. Synthesis and Characterization of Mg-doped ZnO Nanorods for Biomedical Applications

    Science.gov (United States)

    Gemar, H.; Das, N. C.; Wanekaya, A.; Delong, R.; Ghosh, K.

    2013-03-01

    Nanomaterials research has become a major attraction in the field of advanced materials research in the area of Physics, Chemistry, and Materials Science. Bio-compatible and chemically stable metal nanoparticles have biomedical applications that includes drug delivery, cell and DNA separation, gene cloning, magnetic resonance imaging (MRI). This research is aimed at the fabrication and characterization of Mg-doped ZnO nanorods. Hydrothermal synthesis of undoped ZnO and Mg-doped ZnO nanorods is carried out using aqueous solutions of Zn(NO3)2 .6H2O, MgSO4, and using NH4OH as hydrolytic catalyst. Nanomaterials of different sizes and shapes were synthesized by varying the process parameters such as molarity (0.15M, 0.3M, 0.5M) and pH (8-11) of the precursors, growth temperature (130°C), and annealing time during the hydrothermal Process. Structural, morphological, and optical properties are studied using various techniques such as XRD, SEM, UV-vis and PL spectroscopy. Detailed structural, and optical properties will be discussed in this presentation. This work is partially supported by National Cancer Institute (1 R15 CA139390-01).

  20. Pulsed laser deposited Al-doped ZnO thin films for optical applications

    Directory of Open Access Journals (Sweden)

    Gurpreet Kaur

    2015-02-01

    Full Text Available Highly transparent and conducting Al-doped ZnO (Al:ZnO thin films were grown on glass substrates using pulsed laser deposition technique. The profound effect of film thickness on the structural, optical and electrical properties of Al:ZnO thin films was observed. The X-ray diffraction depicts c-axis, plane (002 oriented thin films with hexagonal wurtzite crystal structure. Al-doping in ZnO introduces a compressive stress in the films which increase with the film thickness. AFM images reveal the columnar grain formation with low surface roughness. The versatile optical properties of Al:ZnO thin films are important for applications such as transparent electromagnetic interference (EMI shielding materials and solar cells. The obtained optical band gap (3.2–3.08 eV was found to be less than pure ZnO (3.37 eV films. The lowering in the band gap in Al:ZnO thin films could be attributed to band edge bending phenomena. The photoluminescence spectra gives sharp visible emission peaks, enables Al:ZnO thin films for light emitting devices (LEDs applications. The current–voltage (I–V measurements show the ohmic behavior of the films with resistivity (ρ~10−3 Ω cm.

  1. The effect of Co and In combinational or individual doping on the structural, optical and selective sensing properties of ZnO nanoparticles

    CSIR Research Space (South Africa)

    Maswanganye, MW

    2017-08-01

    Full Text Available , is found to increase the response to all stimuli to higher values than undoped or singly doped ZnO sensors at the expense of selectivity where In-Co-ZnO as well as undoped ZnO and Co-ZnO sensors have similar selectivity value of below 44% to CO. In-doped Zn...

  2. VLS-grown diffusion doped ZnO nanowires and their luminescence properties

    International Nuclear Information System (INIS)

    Roy, Pushan Guha; Dutta, Amartya; Das, Arpita; Bhattacharyya, Anirban; Sen, Sayantani; Pramanik, Pallabi

    2015-01-01

    Zinc Oxide (ZnO) nanowires were deposited by vapor–liquid–solid (VLS) method on to aluminum doped ZnO (AZO) thin films grown by sol-gel technique. For various device applications, current injection into such nanowires is critical. This is expected to be more efficient for ZnO nanowires deposited on to AZO compared to those deposited on to a foreign substrate such as silicon. In this work we compare the morphological and optical properties of nanowires grown on AZO with those grown under similar conditions on silicon (Si) wafers. For nanowires grown on silicon, diameters around 44 nm with heights around 2.2 μm were obtained. For the growth on to AZO, the diameters were around 90 nm while the heights were around 520 nm. Room temperature photoluminescence (RT-PL) measurements show improved near band-edge emission for nanowires grown on to AZO, indicating higher material quality. This is further established by low temperature photoluminescence (LT-PL) measurements where excitonic transitions with width as small as 14 meV have been obtained at 4 K for such structures. Electron energy loss spectroscopy (EELS) studies indicate the presence of Al in the nanowires, indicating a new technique for introduction of dopants into these structures. These results indicate that ZnO nanowires on sol-gel grown AZO thin films show promise in the development of various optoelectronic devices. (paper)

  3. Nanoparticles of ZnO doped with Mn: structural and morphological characteristics

    Energy Technology Data Exchange (ETDEWEB)

    Bonifacio, Maria Aparecida Ribeiro; Lira, Helio de Lucena; Gama, Lucianna, E-mail: m_aparecidaribeiro@yahoo.com.br [Universidade Federal de Campina Grande (UFCG), PB (Brazil). Departamento de Engenharia de Materiais; Neiva, Laedna Souto [Universidade Federal do Cariri (UFCA), Juazeiro do Norte, CE (Brazil). Unidade Academica de Materiais; Kiminami, Ruth H. G. A. [Universidade Federal de Sao Carlos (USCar), SP (Brazil). Departamento de Engenharia de Materiais

    2017-07-15

    In this study, the effects of dopant concentrations on the structural and morphological characteristics of Zn{sub 1-x}Mn{sub x} O powders (x= 0.025, 0.05, 0.075, and 0.1 mole) synthesized by the Pechini method has been investigated. The powder was characterized by X-ray diffraction (XRD), Brunauer-Emmet-Teller (BET) specific surface, energy dispersive X-ray (EDX), scanning electron microscopy (SEM) and Spectroscopy with Fourier transform (FTIR). An XRD analysis of the powder showed the formation of ZnO phase with a typical single phase wurtzite structure. The EDX analysis revealed Mn incorporated in the ZnO structure. The particle size calculated by BET ranged from 24 to 63 nm, confirming the nanometric size of the powder particles. The SEM analysis revealed irregular shaped particle agglomerates and the presence of nanosheets. From FTIR it was confirmed the wurtzite structure in ZnO and ZnO nanoparticles doped with Mn. (author)

  4. Investigation on Fe-doped ZnO nanostructures prepared by a chemical route

    International Nuclear Information System (INIS)

    Mishra, A.K.; Das, D.

    2010-01-01

    Zn 1-x Fe x O (x = 0.03, 0.05 and 0.07) nanoparticles synthesized by a chemical route were characterized by different techniques. The structural characterization by XRD and TEM confirmed the phase purity of the samples and indicated a reduction in particle size with increase in the dopant (Fe) concentration in ZnO. The optical characterization of the nanoparticles by FTIR, PL and UV-visible spectroscopy confirmed the formation of wurtzite structure and incorporation of Fe in the ZnO lattice. Magnetization measurements by VSM and Faraday balance techniques indicate presence of room temperature ferromagnetism in the Fe-doped ZnO samples. Local environment around the Fe atoms has been probed by 57 Fe Moessbauer spectroscopy and the measured isomer shifts confirmed the charge state of iron as Fe 3+ . Positron annihilation lifetime spectroscopy (PALS) measurements confirm the presence of cation vacancies in the nanoparticles and indicate a reduction of overall defect concentration with incorporation of Fe atoms in the ZnO structure.

  5. Investigation on Fe-doped ZnO nanostructures prepared by a chemical route

    Energy Technology Data Exchange (ETDEWEB)

    Mishra, A.K. [UGC-DAE Consortium for Scientific Research, Kolkata Centre III/LB-8, Bidhannagar, Kolkata 700098 (India); Das, D., E-mail: ddas@alpha.iuc.res.in [UGC-DAE Consortium for Scientific Research, Kolkata Centre III/LB-8, Bidhannagar, Kolkata 700098 (India)

    2010-07-25

    Zn{sub 1-x}Fe{sub x}O (x = 0.03, 0.05 and 0.07) nanoparticles synthesized by a chemical route were characterized by different techniques. The structural characterization by XRD and TEM confirmed the phase purity of the samples and indicated a reduction in particle size with increase in the dopant (Fe) concentration in ZnO. The optical characterization of the nanoparticles by FTIR, PL and UV-visible spectroscopy confirmed the formation of wurtzite structure and incorporation of Fe in the ZnO lattice. Magnetization measurements by VSM and Faraday balance techniques indicate presence of room temperature ferromagnetism in the Fe-doped ZnO samples. Local environment around the Fe atoms has been probed by {sup 57}Fe Moessbauer spectroscopy and the measured isomer shifts confirmed the charge state of iron as Fe{sup 3+}. Positron annihilation lifetime spectroscopy (PALS) measurements confirm the presence of cation vacancies in the nanoparticles and indicate a reduction of overall defect concentration with incorporation of Fe atoms in the ZnO structure.

  6. Physical properties of antiferromagnetic Mn doped ZnO samples: Role of impurity phase

    Science.gov (United States)

    Neogi, S. K.; Karmakar, R.; Misra, A. K.; Banerjee, A.; Das, D.; Bandyopadhyay, S.

    2013-11-01

    Structural, morphological, optical, and magnetic properties of nanocrystalline Zn1-xMnxO samples (x=0.01, 0.02, 0.04, 0.06, 0.08 and 0.10) prepared by the sol-gel route are studied by X-ray diffraction (XRD), Scanning electron microscopy (SEM), UV-visible absorption spectroscopy, Superconducting quantum interference device (SQUID) magnetometry and positron annihilation lifetime spectroscopy (PALS). XRD confirms formation of wurzite structure in all the Mn-substituted samples. A systematic increase in lattice constants and decrease in grain size have been observed with increase in manganese doping concentration up to 6 at% in the ZnO structure. An impurity phase (ZnMnO3) has been detected when percentage of Mn concentration is 6 at% or higher. The optical band gap of the Mn-substituted ZnO samples decrease with increase in doping concentration of manganese whereas the width of the localized states increases. The antiferromagnetic exchange interaction is strong in the samples for 2 and 4 at% of Mn doping but it reduces when the doping level increases from 6 at% and further. Positron life time components τ1 and τ2 are found to decrease when concentration of the dopant exceeds 6 at%. The changes in magnetic properties as well as positron annihilation parameters at higher manganese concentration have been assigned as due to the formation of impurity phase. Single phase structure has been observed up to 6 at% of Mn doping. Impurity phase has been developed above 6 at% of Mn doping. Antiferromagnetic and paramagnetic interactions are present in the samples. Defect parameters show sharp fall as Mn concentration above 6 at%. The magnetic and defect properties are modified by the formation of impurity phase.

  7. Physical properties of antiferromagnetic Mn doped ZnO samples: Role of impurity phase

    International Nuclear Information System (INIS)

    Neogi, S.K.; Karmakar, R.; Misra, A.K.; Banerjee, A.; Das, D.; Bandyopadhyay, S.

    2013-01-01

    Structural, morphological, optical, and magnetic properties of nanocrystalline Zn 1−x Mn x O samples (x=0.01, 0.02, 0.04, 0.06, 0.08 and 0.10) prepared by the sol–gel route are studied by X-ray diffraction (XRD), Scanning electron microscopy (SEM), UV–visible absorption spectroscopy, Superconducting quantum interference device (SQUID) magnetometry and positron annihilation lifetime spectroscopy (PALS). XRD confirms formation of wurzite structure in all the Mn-substituted samples. A systematic increase in lattice constants and decrease in grain size have been observed with increase in manganese doping concentration up to 6 at% in the ZnO structure. An impurity phase (ZnMnO 3 ) has been detected when percentage of Mn concentration is 6 at% or higher. The optical band gap of the Mn-substituted ZnO samples decrease with increase in doping concentration of manganese whereas the width of the localized states increases. The antiferromagnetic exchange interaction is strong in the samples for 2 and 4 at% of Mn doping but it reduces when the doping level increases from 6 at% and further. Positron life time components τ 1 and τ 2 are found to decrease when concentration of the dopant exceeds 6 at%. The changes in magnetic properties as well as positron annihilation parameters at higher manganese concentration have been assigned as due to the formation of impurity phase. - highlights: • Single phase structure has been observed up to 6 at% of Mn doping. • Impurity phase has been developed above 6 at% of Mn doping. • Antiferromagnetic and paramagnetic interactions are present in the samples. • Defect parameters show sharp fall as Mn concentration above 6 at%. • The magnetic and defect properties are modified by the formation of impurity phase

  8. Physical properties of antiferromagnetic Mn doped ZnO samples: Role of impurity phase

    Energy Technology Data Exchange (ETDEWEB)

    Neogi, S.K.; Karmakar, R. [Department of Physics, University of Calcutta, 92 A.P.C. Road, Kolkata 700009 (India); Misra, A.K. [UGC DAE Consortium for Scientific Research, Salt Lake, Kolkata 700064 (India); Banerjee, A. [Department of Physics, University of Calcutta, 92 A.P.C. Road, Kolkata 700009 (India); CRNN, University of Calcutta, JD 2, Sector III, Salt Lake, Kolkata 700098 (India); Das, D. [UGC DAE Consortium for Scientific Research, Salt Lake, Kolkata 700064 (India); Bandyopadhyay, S., E-mail: sbaphy@caluniv.ac.in [Department of Physics, University of Calcutta, 92 A.P.C. Road, Kolkata 700009 (India); CRNN, University of Calcutta, JD 2, Sector III, Salt Lake, Kolkata 700098 (India)

    2013-11-15

    Structural, morphological, optical, and magnetic properties of nanocrystalline Zn{sub 1−x}Mn{sub x}O samples (x=0.01, 0.02, 0.04, 0.06, 0.08 and 0.10) prepared by the sol–gel route are studied by X-ray diffraction (XRD), Scanning electron microscopy (SEM), UV–visible absorption spectroscopy, Superconducting quantum interference device (SQUID) magnetometry and positron annihilation lifetime spectroscopy (PALS). XRD confirms formation of wurzite structure in all the Mn-substituted samples. A systematic increase in lattice constants and decrease in grain size have been observed with increase in manganese doping concentration up to 6 at% in the ZnO structure. An impurity phase (ZnMnO{sub 3}) has been detected when percentage of Mn concentration is 6 at% or higher. The optical band gap of the Mn-substituted ZnO samples decrease with increase in doping concentration of manganese whereas the width of the localized states increases. The antiferromagnetic exchange interaction is strong in the samples for 2 and 4 at% of Mn doping but it reduces when the doping level increases from 6 at% and further. Positron life time components τ{sub 1} and τ{sub 2} are found to decrease when concentration of the dopant exceeds 6 at%. The changes in magnetic properties as well as positron annihilation parameters at higher manganese concentration have been assigned as due to the formation of impurity phase. - highlights: • Single phase structure has been observed up to 6 at% of Mn doping. • Impurity phase has been developed above 6 at% of Mn doping. • Antiferromagnetic and paramagnetic interactions are present in the samples. • Defect parameters show sharp fall as Mn concentration above 6 at%. • The magnetic and defect properties are modified by the formation of impurity phase.

  9. Nitrogen-Doped Carbon Encapsulated Nickel/Cobalt Nanoparticle Catalysts for Olefin Migration of Allylarenes

    DEFF Research Database (Denmark)

    Kramer, Søren; Mielby, Jerrik Jørgen; Buss, Kasper Spanggård

    2017-01-01

    Olefin migration of allylarenes is typically performed with precious metal-based homogeneous catalysts. In contrast, very limited progress has been made using cheap, earth-abundant base metals as heterogeneous catalysts for these transformations - in spite of the obvious economic and environmental...... advantages. Herein, we report on the use of an easily prepared heterogeneous catalyst material for the migration of olefins, in particular allylarenes. The catalyst material consists of nickel/cobalt alloy nanoparticles encapsulated in nitrogen-doped carbon shells. The encapsulated nanoparticles are stable...

  10. Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

    Science.gov (United States)

    Ning, Shuai; Zhan, Peng; Wang, Wei-Peng; Li, Zheng-Cao; Zhang, Zheng-Jun

    2014-12-01

    Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ~ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ~ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed.

  11. Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

    International Nuclear Information System (INIS)

    Ning Shuai; Zhan Peng; Wang Wei-Peng; Li Zheng-Cao; Zhang Zheng-Jun

    2014-01-01

    Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ∼ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ∼ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  12. Cobalt-Doped Carbon Gels as Electro-Catalysts for the Reduction of CO2 to Hydrocarbons

    Directory of Open Access Journals (Sweden)

    Abdalla Abdelwahab

    2017-01-01

    Full Text Available Two original series of carbon gels doped with different cobalt loadings and well-developed mesoporosity, aerogels and xerogels, have been prepared, exhaustively characterized, and tested as cathodes for the electro-catalytic reduction of CO2 to hydrocarbons at atmospheric pressure. Commercial cobalt and graphite sheets have also been tested as cathodes for comparison. All of the doped carbon gels catalyzed the formation of hydrocarbons, at least from type C1 to C4. The catalytic activity depends mainly on the metal loading, nevertheless, the adsorption of a part of the products in the porous structure of the carbon gel cannot be ruled out. Apparent faradaic efficiencies calculated with these developed materials were better that those obtained with a commercial cobalt sheet as a cathode, especially considering the much lower amount of cobalt contained in the Co-doped carbon gels. The cobalt-carbon phases formed in these types of doped carbon gels improve the selectivity to C3-C4 hydrocarbons formation, obtaining even more C3 hydrocarbons than CH4 in some cases.

  13. Effects of Temperature on the Microstructure and Magnetic Property of Cr-Doped ZnO DMS Prepared by Hydrothermal Route Assisted by Pulsed Magnetic Fields

    Directory of Open Access Journals (Sweden)

    Shiwei Wang

    2013-01-01

    Full Text Available In the present work, Cr-doped ZnO diluted magnetic semiconductor was synthesized by hydrothermal method under pulsed magnetic fields. The samples were characterized by XRD, SEM, VSM, Raman, and XPS techniques. Results demonstrated that Zn ions in the ZnO crystal lattice were partially displaced by Chromium (III ions. All samples show room temperature ferromagnetism which was enhanced by pulsed magnetic fields. The mechanism of ferromagnetism of Cr-doped ZnO particles was discussed.

  14. Diffusion, swelling, cross linkage study and mechanical properties of ZnO doped PVA/NaAlg blend polymer nanocomposite

    Science.gov (United States)

    Guruswamy, B.; Ravindrachary, V.; Shruthi, C.; Hegde, Shreedatta; Sagar, Rohan N.

    2018-04-01

    ZnO nano particles were synthesized using a chemical precipitation method. Pure and ZnO nano particle doped PVA-NaAlg blend composite films were prepared using solution casing method. Structural information of these composites was studied using FTIR. Diffusion kinetics of these polymer blend composite were studied using Flory-Huggins theory. Using these diffusion studies, cross-linking density and swelling properties of the films were analyzed. Mechanical properties of these composite are also studied.

  15. Electrochemical investigation of the properties of Co doped ZnO nanoparticle as a corrosion inhibitive pigment for modifying corrosion resistance of the epoxy coating

    International Nuclear Information System (INIS)

    Rostami, M.; Rasouli, S.; Ramezanzadeh, B.; Askari, A.

    2014-01-01

    Highlights: • Corrosion inhibitive pigment based on ZnOCo was synthesized through combustion method. • Doping ZnO nanoparticle with Co enhanced its inhibition properties considerably. • ZnOCo nanoparticle could enhance corrosion protective performance of epoxy coating. • Co doped ZnO nanoparticles behaved as efficient barrier and inhibitive pigment. - Abstract: Co doped ZnO nanoparticles were synthesized by combustion method. Then, the epoxy nanocomposites were prepared using various amounts of nanoparticles. Salt spray and electrochemical impedance spectroscopy (EIS) were used in order to investigate the corrosion inhibition effects of nanoparticles on the steel substrate. The morphology and composition of the films precipitated on the steel surface were investigated by scanning electron microscope (SEM) and energy dispersive spectroscopy. Results revealed that the corrosion inhibition properties of ZnO nanoparticle were significantly enhanced after doping with Co. Moreover, Co doped ZnO nanoparticles enhanced the corrosion resistance of the epoxy coating effectively

  16. Structural and room temperature ferromagnetic properties of Ni doped ZnO nanoparticles via low-temperature hydrothermal method

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Kun; Liu, Changzhen, E-mail: liuchangzhen94@163.com; Chen, Rui; Fang, Xiaoxiang; Wu, Xiuling; Liu, Jie

    2016-12-01

    A series of Zn{sub 1−x}Ni{sub x}O (x=0, 1%, 3%, 5%) nanoparticles have been synthesized via a low-temperature hydrothermal method. Influence of Ni doping concentration on the structure, morphology, optical properties and magnetism of the samples was investigated by means of X-ray diffraction, X-ray photoelectron spectroscopy, scanning electron microscopy, UV–vis spectrophotometer and vibrating sample magnetometer instruments. The results show that the undoped and doped ZnO nanoparticles are both hexagonal wurtzite structures. The surface analysis was performed using X-ray photoelectron spectroscopic studies. The images of SEM reveal that the structure of pure ZnO and Ni doped samples are nanoparticles which intended to form flakes with thickness of few nanometers, being overlain with each one to develop the network with some pores and voids. Based on the ultraviolet–visible (UV–vis) spectroscopy analysis, it indicates that the band gap energy decreases with the increasing concentration of Ni. Furthermore, The Ni doped ZnO samples didn't exhibit higher ultraviolet-light-driven photocatalytic activity compared to the undoped ZnO sample. Vibrating sample magnetometer was used for the magnetic property investigations, and the result indicates that room temperature ferromagnetism property of 3% Ni doped sample is attributed to oxygen vacancy and interaction between doped ions.

  17. The structural, electronic and optical properties of Nd doped ZnO using first-principles calculations

    Science.gov (United States)

    Wen, Jun-Qing; Zhang, Jian-Min; Chen, Guo-Xiang; Wu, Hua; Yang, Xu

    2018-04-01

    The density functional theory calculations using general gradient approximation (GGA) applying Perdew-Burke-Ernzerhof (PBE) as correlation functional have been systematically performed to research the formation energy, the electronic structures, band structures, total and partial DOS, and optical properties of Nd doping ZnO with the content from 6.25% to 12.5%. The formation energies are negative for both models, which show that two structures are energetically stable. Nd doping ZnO crystal is found to be a direct band gap semiconductor and Fermi level shifts upward into conduction band, which show the properties of n-type semiconductor. Band structures are more compact after Nd doping ZnO, implying that Nd doping induces the strong interaction between different atoms. Nd doping ZnO crystal presents occupied states at near Fermi level, which mainly comes from the Nd 4f orbital. The calculated optical properties imply that Nd doping causes a red-shift of absorption peaks, and enhances the absorption of the visible light.

  18. Aluminum doping tunes band gap energy level as well as oxidative stress-mediated cytotoxicity of ZnO nanoparticles in MCF-7 cells

    Science.gov (United States)

    Akhtar, Mohd Javed; Alhadlaq, Hisham A.; Alshamsan, Aws; Majeed Khan, M. A.; Ahamed, Maqusood

    2015-09-01

    We investigated whether Aluminum (Al) doping tunes band gap energy level as well as selective cytotoxicity of ZnO nanoparticles in human breast cancer cells (MCF-7). Pure and Al-doped ZnO nanoparticles were prepared by a simple sol-gel method. Characterization study confirmed the formation of single phase of AlxZn1-xO nanocrystals with the size range of 33-55 nm. Al-doping increased the band gap energy of ZnO nanoparticles (from 3.51 eV for pure to 3.87 eV for Al-doped ZnO). Al-doping also enhanced the cytotoxicity and oxidative stress response of ZnO nanoparticles in MCF-7 cells. The IC50 for undoped ZnO nanoparticles was 44 μg/ml while for the Al-doped ZnO counterparts was 31 μg/ml. Up-regulation of apoptotic genes (e.g. p53, bax/bcl2 ratio, caspase-3 & caspase-9) along with loss of mitochondrial membrane potential suggested that Al-doped ZnO nanoparticles induced apoptosis in MCF-7 cells through mitochondrial pathway. Importantly, Al-doping did not change the benign nature of ZnO nanoparticles towards normal cells suggesting that Al-doping improves the selective cytotoxicity of ZnO nanoparticles toward MCF-7 cells without affecting the normal cells. Our results indicated a novel approach through which the inherent selective cytotoxicity of ZnO nanoparticles against cancer cells can be further improved.

  19. Effect of nickel doping concentration on structural and magnetic properties of ultrafine diluted magnetic semiconductor ZnO nanoparticles

    International Nuclear Information System (INIS)

    Sharma, Prashant K.; Dutta, Ranu K.; Pandey, Avinash C.

    2009-01-01

    The ZnO:Ni 2+ nanoparticles of mean size 2-12 nm were synthesized at room temperature by the simple co-precipitation method. The crystallite structure, morphology and size were determined by X-ray diffraction (XRD) and high-resolution transmission electron microscopy (HRTEM). The wurtzite structure of ZnO gradually degrades with the increasing Ni doping concentration and an additional NiO-associated diffraction peak was observed above 15% of Ni 2+ doping. The change in magnetic behavior of the nanoparticles of ZnO with varying Ni 2+ doping concentration was investigated using a vibrating sample magnetometer (VSM). Initially, these nanoparticles showed strong ferromagnetic behavior, however, at higher doping percentage of Ni 2+ , the ferromagnetic behavior was suppressed and paramagnetic nature was observed. The enhanced antiferromagnetic interaction between neighboring Ni-Ni ions suppressed the ferromagnetism at higher doping concentrations of Ni 2+ .

  20. Nickel doped cobalt sulfide as a high performance counter electrode for dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Hee-Je; Kim, Chul-Woo; Punnoose, Dinah; Gopi, Chandu V.V.M.; Kim, Soo-Kyoung; Prabakar, K.; Rao, S. Srinivasa, E-mail: srinu.krs@gmail.com

    2015-02-15

    Graphical abstract: - Highlights: • First ever employment of Ni doped CoS{sub 2} counter electrode as a replacement of Pt counter electrode. • Efficiency of 5.50% was achieved using Ni doped CoS{sub 2} counter electrode in contrast to 5.21% efficiency obtained using Pt electrode. • Dependency of efficiency on Ni dopant reported for the first time. • Cost effective chemical bath deposition was used for the fabrication of the counter electrode. - Abstract: The use of cells based on cobalt sulfide (CoS{sub 2}) and nickel sulfide (NiS) has found a steep upsurge in solar cell applications and as a substitute for conventional Pt-based cells owing to their low cost, low-temperature processing ability, and promising electro-catalytic activity. In this study, CoS{sub 2}, NiS and Ni-doped CoS{sub 2} nanoparticles were incorporated on a fluorine-doped tin oxide (FTO) substrate by simple chemical bath deposition (CBD). The surface morphology of the obtained films was analyzed by scanning electron microscope. Tafel polarization, electrochemical impedance spectroscopy and cyclic voltammograms of the Ni-doped CoS{sub 2} (Ni 15%) films indicated enhanced electro-catalytic activity for I{sub 3}{sup −} reduction in dye sensitized solar cells (DSSCs) compared to a Pt CE. The Ni-doped CoS{sub 2} CE also showed an impressive photovoltaic conversion efficiency of 5.50% under full sunlight illumination (100 mW cm{sup −2}, AM 1.5 G), exceeding that of DSSCs using a Pt CE (5.21%). We show that the highest conversion efficiency mainly depends on the charge transfer resistance and adequate Ni ion doping with CoS{sub 2} nanoparticles.

  1. The electrical properties of low pressure chemical vapor deposition Ga doped ZnO thin films depending on chemical bonding configuration

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Hanearl [School of Electrical and Electronic Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 120-749 (Korea, Republic of); Kim, Doyoung [School of Electrical and Electronic Engineering, Ulsan College, 57 Daehak-ro, Nam-gu, Ulsan 680-749 (Korea, Republic of); Kim, Hyungjun, E-mail: hyungjun@yonsei.ac.kr [School of Electrical and Electronic Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 120-749 (Korea, Republic of)

    2014-04-01

    Highlights: • Undoped and Ga doped ZnO thin films were deposited using DEZ and TMGa. • Effects of Ga doping using TMGa in Ga doped ZnO were investigated. • Degraded properties from excessive doping were analyzed using chemical bondings. - Abstract: The electrical and chemical properties of low pressure chemical vapor deposition (LP-CVD) Ga doped ZnO (ZnO:Ga) films were systematically investigated using Hall measurement and X-ray photoemission spectroscopy (XPS). Diethylzinc (DEZ) and O{sub 2} gas were used as precursor and reactant gas, respectively, and trimethyl gallium (TMGa) was used as a Ga doping source. Initially, the electrical properties of undoped LP-CVD ZnO films depending on the partial pressure of DEZ and O{sub 2} ratio were investigated using X-ray diffraction (XRD) by changing partial pressure of DEZ from 40 to 140 mTorr and that of O{sub 2} from 40 to 80 mTorr. The resistivity was reduced by Ga doping from 7.24 × 10{sup −3} Ω cm for undoped ZnO to 2.05 × 10{sup −3} Ω cm for Ga doped ZnO at the TMG pressure of 8 mTorr. The change of electric properties of Ga doped ZnO with varying the amount of Ga dopants was systematically discussed based on the structural crystallinity and chemical bonding configuration, analyzed by XRD and XPS, respectively.

  2. Effect of growth time to the properties of Al-doped ZnO nanorod arrays

    Science.gov (United States)

    Ismail, A. S.; Mamat, M. H.; Malek, M. F.; Saidi, S. A.; Yusoff, M. M.; Mohamed, R.; Sin, N. D. Md; Suriani, A. B.; Rusop, M.

    2018-05-01

    Aluminum (Al)-doped zinc oxide (ZnO) nanorod array films were successfully deposited at different growth time on zinc oxide (ZnO) seed layer coated glass substrate using sol-gel immersion method. The morphology images of the films showed that the thicknesses of the films were increased parallel with the increment of growth period. The surface topology of the films displayed an increment of roughness as the growth period increased. Optical properties of the samples exposed that the percentage of transmittances reduced at higher growth time. Besides, the Urbach energy of the films slightly increased as the immersion time increased. The current-voltage (I-V) measurement indicated that the resistance increased as the immersion time increased owing to the appearance of intrinsic layer on top of the nanorods.

  3. Transition from diamagnetic to ferromagnetic state in laser ablated nitrogen doped ZnO thin films

    Directory of Open Access Journals (Sweden)

    Kajal Jindal

    2015-02-01

    Full Text Available Transition from room temperature diamagnetic to ferromagnetic state in N doped ZnO (ZnO:N films grown by pulsed laser deposition with tunable energy density has been identified. ZnO:N films deposited with moderate laser energy density of 2.5 J/cm2 are single phase and nearly defect free having N dopant substitution at O sites in ZnO lattice, exhibiting intrinsic ferromagnetism. When energy density reduces (<2.5 J/cm2, defects in ZnO:N film degrades ferromagnetism and exhibit diamagnetic phase when grown at energy density of 1.0 J/cm2. Growth kinetics, which in turn depends on laser energy density is playing important role in making transition from ferromagnetic to diamagnetic in ZnO:N films.

  4. Process dependence of H passivation and doping in H-implanted ZnO

    International Nuclear Information System (INIS)

    Zhang, Z; Brillson, L J; Look, D C; Schifano, R; Johansen, K M; Svensson, B G

    2013-01-01

    We used depth-resolved cathodoluminescence spectroscopy (DRCLS), photoluminescence (PL) spectroscopy and temperature-dependent Hall-effect (TDHE) measurements to describe the strong dependence of H passivation and doping in H-implanted ZnO on thermal treatment. Increasing H implantation dose increases passivation of Zn and oxygen vacancy-related defects, while reducing deep level emissions. Over annealing temperatures of 100-400 °C at different times, 1 h annealing at 200 °C yielded the lowest DRCLS deep level emissions, highest TDHE carrier mobility, and highest near band-edge PL emission. These results describe the systematics of dopant implantation and thermal activation on H incorporation in ZnO and their effects on its electrical properties.

  5. Heat treatment effect on the physical properties of cobalt doped TiO{sub 2} sol–gel materials

    Energy Technology Data Exchange (ETDEWEB)

    Samet, L., E-mail: lolwasamet@gmail.com [Institut Préparatoires aux Etudes d' Ingénieurs d' El-Manar, Université Tunis El Manar, Campus Universitaire, 2092 El Manar (Tunisia); Laboratoire de Photovoltaique de Semi-conducteur et de Nanostructure, Centre de Recherches et des Technologies de l' Energie, Technopole borj cedria, Bp 95, hammamm lif 2050 (Tunisia); Ben Nasseur, J.; Chtourou, R. [Laboratoire de Photovoltaique de Semi-conducteur et de Nanostructure, Centre de Recherches et des Technologies de l' Energie, Technopole borj cedria, Bp 95, hammamm lif 2050 (Tunisia); March, K.; Stephan, O. [Laboratoire de Physique des Solides, UMR 8502 CNRS - Université Paris-Sud, Bât 510, 91405 Orsay cedex (France)

    2013-11-15

    Cobalt doped and undoped TiO{sub 2} powders have been prepared by sol–gel technique and annealed at temperatures ranging from 400 °C to 1000 °C. The effects of annealing temperature on the structural, morphological and optical properties have been characterized by X-ray diffraction, transmission electron microscopy, electron energy-loss spectroscopy and diffuse reflectance spectroscopy. For all doped samples there is a general reduction of the band gap energy, in comparison with undoped samples prepared in the same conditions. More specifically, experimental results indicate that cobalt doping, occurring as Co{sup 2+} ion insertion into the TiO{sub 2} (Ti{sup 4+}) host lattice, inhibits the growth of the crystallites and delays the phase transformation from anatase to rutile. Moreover, at high temperature, a secondary phase (CoTiO{sub 3}) is found to coexist with highly crystalline rutile. These structural characteristics are discussed in relation with the observed general trends for the optical properties. - Highlights: • Cobalt doped and undoped TiO{sub 2} powders have been prepared by sol–gel route. • Doping makes the band gap narrower. • Doping delays the phase transformation from anatase to rutile. • Doping inhibits the growth of the crystallites. • At high annealing temperature a CoTiO{sub 3} phase coexists with highly crystalline rutile.

  6. The effects of ZnO buffer layers on the properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition

    International Nuclear Information System (INIS)

    Kim, K-W; Lugo, F J; Lee, J H; Norton, D P

    2012-01-01

    The properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition were examined, specifically focusing on the effects of undoped ZnO buffer layers. In particular, buffer layers were grown under different conditions; the transport properties of as-deposited and rapid thermal annealed ZnO:P films were then examined. As-deposited films showed n-type conductivity. After rapid thermal annealing, the film on buffer layer grown at a low temperature showed the conversion of carrier type to p-type for specific growth conditions while the films deposited on buffer layer grown at a high temperature remained n-type regardless of growth condition. The films deposited on buffer layer grown at a low temperature showed higher resistivity and more significant change of the transport properties upon rapid thermal annealing. These results suggest that more dopants are incorporated in films with higher defect density. This is consistent with high resolution x-ray diffraction results for phosphorus doped ZnO films on different buffer layers. In addition, the microstructure of phosphorus doped ZnO films is substantially affected by the buffer layer.

  7. Morphology-controllable of Sn doped ZnO nanorods prepared by spray pyrolysis for transparent electrode application

    Science.gov (United States)

    Hameed, M. Shahul; Princice, J. Joseph; Babu, N. Ramesh; Zahirullah, S. Syed; Deshmukh, Sampat G.; Arunachalam, A.

    2018-05-01

    Transparent conductive Sn doped ZnO nanorods have been deposited at various doping level by spray pyrolysis technique on glass substrate. The structural, surface morphological and optical properties of these films have been investigated with the help of X-ray diffraction (XRD), scanning electron microscope (SEM), atomic force microscope (AFM) and UV-Vis spectrophotometer respectively. XRD patterns revealed a successful high quality growth of single crystal ZnO nanorods with hexagonal wurtzite structure having (002) preferred orientation. The scanning electron microscope (SEM) image of the prepared films exposed the uniform distribution of Sn doped ZnO nanorod shaped grains. All these films were highly transparent in the visible region with average transmittance of 90%.

  8. Effect of Ag doping on the properties of ZnO thin films for UV stimulated emission

    Science.gov (United States)

    Razeen, Ahmed S.; Gadallah, A.-S.; El-Nahass, M. M.

    2018-06-01

    Ag doped ZnO thin films have been prepared using sol-gel spin coating method, with different doping concentrations. Structural and morphological properties of the films have been investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. Thin films have been optically pumped and stimulated emission has been observed with strong peaks in the UV region. The UV stimulated emission is found to be due to exciton-exciton scattering, and Ag doping promoted this process by increasing the excitons concentrations in the ZnO lattice. Output-input intensity relation and peak emission, FWHM, and quantum efficiency relations with pump intensity have been reported. The threshold for which stimulated emission started has been evaluated to be about 18 MW/cm2 with quantum efficiency of about 58.7%. Mechanisms explaining the role of Ag in enhancement of stimulated emission from ZnO thin films have been proposed.

  9. Doping properties of ZnO thin films for photovoltaic devices grown by URT-IP (ion plating) method

    International Nuclear Information System (INIS)

    Iwata, K.; Sakemi, T.; Yamada, A.; Fons, P.; Awai, K.; Yamamoto, T.; Matsubara, M.; Tampo, H.; Sakurai, K.; Ishizuka, S.; Niki, S.

    2004-01-01

    The Uramoto-gun with Tanaka magnetic field (URT)-ion plating (IP) method is a novel ion plating technique for thin film deposition. This method offers the advantage of low-ion damage, low deposition temperatures, large area deposition and high growth rates. Ga-doped ZnO thin films were grown using the URT-IP method, and the doping properties were evaluated. The opposing goals of low Ga composition and low resistivity are required for industrial applications of transparent conductive oxide (TCO). We have carried out a comparison between the carrier concentration and Ga atomic concentration in Ga-doped ZnO thin films and found the trade-off point for optimal TCO performance. The optimum growth conditions were obtained using a 3% Ga 2 O 3 content ZnO target

  10. First-principles research on the optical and electrical properties and mechanisms of In-doped ZnO

    Science.gov (United States)

    Hou, Qingyu; Xi, Dongmin; Li, Wenling; Jia, Xiaofang; Xu, Zhenchao

    2018-05-01

    The absorption spectra and conductivity of In-doped ZnO still exhibit differences. To resolve this contradiction, the ZnO supercell models with different In doping amounts and the Zn0.9375In0.0625(Zni)0.0625O supercell model were both constructed. When the geometrical structure of all the models was optimized, the GGA + U and GGA used to calculate the energy. In the range of In doping used in this study, the formation energy of In-doped ZnO under Zn-rich conditions is lower than that under O-rich conditions, thereby implying a more stability of In-doped ZnO under Zn-rich than that under O-rich. With the increased In doping content, the volume and the formation energy of the doped system increase, the doped systems become unstable, and doping becomes difficult. Furthermore, the band gaps are narrowed, and the red shift of absorption spectrum is enhanced. In the In doping amount ranging within 0.01389-0.05556, the electron effective mass decreases first and subsequently increases, and the electron concentration increases. The mobility and conductivity also increase first and subsequently decrease. These results are in accordance with the experimental results. The volume of Zn0.9375In0.0625(Zni)0.0625O with the coexistence of In replacing Zn and interstitial Zn is large. The band gap is widened and the absorption spectrum is blue-shifted in the UV region.

  11. Aluminium doping induced enhancement of p-d coupling in ZnO

    International Nuclear Information System (INIS)

    Cong, G W; Peng, W Q; Wei, H Y; Liu, X L; Wu, J J; Han, X X; Zhu, Q S; Wang, Z G; Ye, Z Z; Lu, J G; Zhu, L P; Qian, H J; Su, R; Hong, C H; Zhong, J; Ibrahim, K; Hu, T D

    2006-01-01

    Valence-band type Auger lines in Al doped and undoped ZnO were comparatively studied with the corresponding core level x-ray photoelectron spectrography (XPS) spectra as references. Then the shift trend of energy levels in the valence band was that p and p-s-d states move upwards but e and p-d states downwards with increasing Al concentration. The decreased energy of the Zn 3d state is larger than the increased energy of the O 2p state, indicating the lowering of total energy. This may indicate that Al doping could induce the enhancement of p-d coupling in ZnO, which originates from stronger Al-O hybridization. The shifts of these states and the mechanism were confirmed by valence band XPS spectra and O K-edge x-ray absorption spectrography (XAS) spectra. Finally, some previously reported phenomena are explained based on the Al doping induced enhancement of p-d coupling

  12. Electrical properties of fluorine-doped ZnO nanowires formed by biased plasma treatment

    Science.gov (United States)

    Wang, Ying; Chen, Yicong; Song, Xiaomeng; Zhang, Zhipeng; She, Juncong; Deng, Shaozhi; Xu, Ningsheng; Chen, Jun

    2018-05-01

    Doping is an effective method for tuning electrical properties of zinc oxide nanowires, which are used in nanoelectronic devices. Here, ZnO nanowires were prepared by a thermal oxidation method. Fluorine doping was achieved by a biased plasma treatment, with bias voltages of 100, 200, and 300 V. Transmission electron microscopy indicated that the nanowires treated at bias voltages of 100 and 200 V featured low crystallinity. When the bias voltage was 300 V, the nanowires showed single crystalline structures. Photoluminescence measurements revealed that concentrations of oxygen and surface defects decreased at high bias voltage. X-ray photoelectron spectroscopy suggested that the F content increased as the bias voltage was increased. The conductivity of the as-grown nanowires was less than 103 S/m; the conductivity of the treated nanowires ranged from 1 × 104-5 × 104, 1 × 104-1 × 105, and 1 × 103-2 × 104 S/m for bias voltage treatments at 100, 200, and 300 V, respectively. The conductivity improvements of nanowires formed at bias voltages of 100 and 200 V, were attributed to F-doping, defects and surface states. The conductivity of nanowires treated at 300 V was attributed to the presence of F ions. Thus, we provide a method of improving electrical properties of ZnO nanowires without altering their crystal structure.

  13. Electrical properties of lightly Ga-doped ZnO nanowires

    Science.gov (United States)

    Alagha, S.; Heedt, S.; Vakulov, D.; Mohammadbeigi, F.; Senthil Kumar, E.; Schäpers, Th; Isheim, D.; Watkins, S. P.; Kavanagh, K. L.

    2017-12-01

    We investigated the growth, crystal structure, elemental composition and electrical transport characteristics of ZnO nanowires, a promising candidate for optoelectronic applications in the UV-range. Nominally-undoped and Ga-doped ZnO nanowires were grown by metal-organic chemical vapor deposition. Photoluminescence measurements confirmed the incorporation of Ga via donor-bound exciton emission. With atom-probe tomography we estimated an upper limit of the Ga impurity concentration ({10}18 {{cm}}-3). We studied the electrical transport characteristics of these nanowires with a W-nanoprobe technique inside a scanning electron microscope and with lithographically-defined contacts allowing back-gated measurements. An increase in apparent resistivity by two orders of magnitude with decreasing radius was measured with both techniques with a much larger distribution width for the nanoprobe method. A drop in the effective carrier concentration and mobility was found with decreasing radius which can be attributed to carrier depletion and enhanced scattering due to surface states. Little evidence of a change in resistivity was observed with Ga doping, which indicates that the concentration of native or background dopants is higher than the Ga doping concentration.

  14. Boron doped ZnO embedded into reduced graphene oxide for electrochemical supercapacitors

    Energy Technology Data Exchange (ETDEWEB)

    Alver, Ü., E-mail: ualver@ktu.edu.tr [Karadeniz Technical University, Dept. of Metallurgical and Materials Engineering, 61080 Trabzon (Turkey); Tanrıverdi, A. [Kahramanmaras Sutcu Imam University, Department of Physics, 46100 Kahramanmaraş (Turkey)

    2016-08-15

    Highlights: • Boron doped ZnO particles are fabricated and embedded into reduced graphene oxide (RGO) by hydrothermal method. • RGO/ZnO:B composites are used as electrodes for supercapacitors. • Presence of boron in RGO/ZnO composites caused increasing the stability and specific capacitance of electrodes. - Abstract: In this work, reduced graphene oxide/boron doped zinc oxide (RGO/ZnO:B) composites were fabricated by a hydrothermal process and their electrochemical properties were investigated as a function of dopant concentration. First, boron doped ZnO (ZnO:B) particles was fabricated with different boron concentrations (5, 10, 15 and 20 wt%) and then ZnO:B particles were embedded into RGO sheets. The physical properties of sensitized composites were characterized by XRD and SEM. Characterization indicated that the ZnO:B particles with plate-like structure in the composite were dispersed on graphene sheets. The electrochemical properties of the RGO/ZnO:B composite were investigated through cyclic voltammetry, galvanostatic charge/discharge measurements in a 6 M KOH electrolyte. Electrochemical measurements show that the specific capacitance values of RGO/ZnO:B electrodes increase with increasing boron concentration. RGO/ZnO:B composite electrodes (20 wt% B) display the specific capacitance as high as 230.50 F/g at 5 mV/s, which is almost five times higher than that of RGO/ZnO (52.71 F/g).

  15. Boron doped ZnO embedded into reduced graphene oxide for electrochemical supercapacitors

    International Nuclear Information System (INIS)

    Alver, Ü.; Tanrıverdi, A.

    2016-01-01

    Highlights: • Boron doped ZnO particles are fabricated and embedded into reduced graphene oxide (RGO) by hydrothermal method. • RGO/ZnO:B composites are used as electrodes for supercapacitors. • Presence of boron in RGO/ZnO composites caused increasing the stability and specific capacitance of electrodes. - Abstract: In this work, reduced graphene oxide/boron doped zinc oxide (RGO/ZnO:B) composites were fabricated by a hydrothermal process and their electrochemical properties were investigated as a function of dopant concentration. First, boron doped ZnO (ZnO:B) particles was fabricated with different boron concentrations (5, 10, 15 and 20 wt%) and then ZnO:B particles were embedded into RGO sheets. The physical properties of sensitized composites were characterized by XRD and SEM. Characterization indicated that the ZnO:B particles with plate-like structure in the composite were dispersed on graphene sheets. The electrochemical properties of the RGO/ZnO:B composite were investigated through cyclic voltammetry, galvanostatic charge/discharge measurements in a 6 M KOH electrolyte. Electrochemical measurements show that the specific capacitance values of RGO/ZnO:B electrodes increase with increasing boron concentration. RGO/ZnO:B composite electrodes (20 wt% B) display the specific capacitance as high as 230.50 F/g at 5 mV/s, which is almost five times higher than that of RGO/ZnO (52.71 F/g).

  16. Optical, thermal and magnetic studies of pure and cobalt chloride doped L-alanine cadmium chloride

    Energy Technology Data Exchange (ETDEWEB)

    Benila, B.S., E-mail: benjane.benila@gmail.com [Department of Physics and Research Centre, Scott Christian College (Autonomous), Nagercoil 629 003 (India); Bright, K.C. [Department of Physics, St. John' s College, Anchal, Kollam 691 306 (India); Delphine, S. Mary [Department of Physics, Holy Cross College (Autonomous), Nagercoil 629 004 (India); Shabu, R. [Department of Physics and Research Centre, Scott Christian College (Autonomous), Nagercoil 629 003 (India)

    2017-03-15

    Single crystals of L-alanine cadmium chloride (LACC) and cobalt chloride (Co{sup 2+}) doped LACC have been grown by the slow evaporation solution growth technique. The grown crystals were subjected to various characterizations such as powder XRD, SXRD, FTIR, UV–vis, EDAX, TG/DTA, VSM, Dielectric and Second Harmonic Generation (SHG) measurements. The lattice parameters of the grown crystals were determined by single crystal X-ray analysis. EDAX analysis confirms the presence of Co{sup 2+} ion in the host material. The functional group and optical behavior of the crystals were identified from FTIR and UV-vis spectrum analysis. Electrical parameters such as dielectric constant, dielectric loss have been studied. The thermal stability of the compound was found out using TGA/DTA analysis. Second Harmonic Generation of the samples was confirmed by Kurtz-Perry powder technique. Magnetic properties of the crystals studied by VSM were also reported. The encouraging results show that the cobalt chloride doped LACC crystals have greater potential applications in optical devices. - Graphical abstract: Fig (a) and (b) shows the transparent, stable single crystals of pure and doped crystals were obtained using slow evaporation technique. The sizes of pure and doped crystals are 20×9×2 mm{sup 3} and 18×15×1 mm{sup 3} respectively. Fig (c) is the Hysteresis loop traced at room temperature for the pure and doped crystals explains the soft ferromagnetic nature of the doped crystal. The provision for changing the value of coercivity can be used for security, switching and sensing applications. - Highlights: • Defect free crystals of pure and Co{sup 2+} ion doped L-alanine cadmium chloride were grown. • The optical, dielectric and magnetic properties of pure crystals were enhanced by adding Co{sup 2+} ion. • High optical transmittance was obtained in the entire visible and IR region. • Addition of dopant to the pure crystal altered the coercivity. • Low dielectric

  17. Synthesis and characterization of single-phase Mn-doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Chattopadhyay, S.; Dutta, S.; Banerjee, A.; Jana, D. [Department of Physics, University of Calcutta, 92 Acharya Prafulla Chandra Road, Kolkata 700 009, West Bengal (India); Bandyopadhyay, S., E-mail: sbaphy@caluniv.ac.i [Department of Physics, University of Calcutta, 92 Acharya Prafulla Chandra Road, Kolkata 700 009, West Bengal (India); Chattopadhyay, S. [Department of Physics, Taki Government College, Taki 743 429, West Bengal (India); Sarkar, A. [Department of Physics, Bangabasi Morning College, 19 Rajkumar Chakraborty Sarani, Kolkata 700 009, West Bengal (India)

    2009-05-01

    Different samples of Zn{sub 1-x}Mn{sub x}O series have been prepared using conventional solid-state sintering method. We identified up to what extent doping will enable us to synthesize single-phase polycrystalline Mn-doped ZnO sample, which is one of the prerequisites for dilute magnetic semiconductor, and we have analyzed its some other physical aspects. In synthesizing the samples, proportion of Mn varies from 1 to 5 at%. However, the milling time varied (6, 12, 24, 48 and 96 h) only for 2 at% Mn-doped samples while for other samples (1, 3, 4 and 5 at% Mn doped) the milling time has been fixed to 96 h. Room-temperature X-ray diffraction (XRD) data reveal that all of the prepared samples up to 3 at% of Mn doping exhibit wurtzite-type structure, and no segregation of Mn and/or its oxides has been found. The 4 at% Mn-doped samples show a weak peak of ZnMn{sub 2}O{sub 4} apart from the other usual peaks of ZnO and the intensity of this impurity peak has been further increased for 5 at% of Mn doping. So beyond 3 at% doping, single-phase behavior is destroyed. Band gap for all the 2 at% Mn-doped samples has been estimated to be between 3.21 and 3.19 eV and the reason for this low band gap values has been explained through the grain boundary trapping model. The room-temperature resistivity measurement shows an increase of resistivity up to 48 h of milling and with further milling it saturates. The defect state of these samples has been investigated using the positron annihilation lifetime (PAL) spectroscopy technique. Here all the relevant lifetime parameters of positron i.e. free annihilation (tau{sub 1}) at defect site (tau{sub 2}) and average (tau{sub av}) increases with milling time.

  18. Role of nickel doping on structural, optical, magnetic properties and antibacterial activity of ZnO nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Vijayaprasath, G.; Murugan, R. [School of Physics, Alagappa University, Karaikudi 630 004, Tamil Nadu (India); Palanisamy, S.; Prabhu, N.M. [Department of Animal Health and Management, Alagappa University, Karaikudi 630 004, Tamil Nadu (India); Mahalingam, T. [Department of Electrical and Computer Engineering, Ajou University, Suwon 443-749 (Korea, Republic of); Hayakawa, Y. [Research Institute of Electronics, Shizuoka University, Hamamatsu 432-8011 (Japan); Ravi, G., E-mail: gravicrc@gmail.com [School of Physics, Alagappa University, Karaikudi 630 004, Tamil Nadu (India)

    2016-04-15

    Highlights: • The XRD analyses revealed that the synthesizes nickel doped ZnO (Zn{sub 1−x}Ni{sub x}O, x = 0.0, 0.03, 0.06 and 0.09) nanostructures have hexagonal wurtzite structure. • The photoluminescence measurements revealed that the broad emission was composed of different bands due to zinc and oxygen vacancies. • X-ray photoelectron spectroscopy (XPS) confirmed the Ni incorporation in ZnO lattice as Ni{sup 2+} ions. • Room temperature ferromagnetism was observed due to the oxygen vacancies and zinc interstitials are the main reasons for ferromagnetism in Ni doped ZnO NPs. - Abstract: Zn{sub 1−x}Ni{sub x}O nanoparticles were synthesized by co-precipitation method. The crystallite sizes of the synthesized samples found to decrease from 38 to 26 nm with increase in nickel concentration. FTIR spectra confirmed the presence of Zn−O stretching bands at 577, 573, 569 and 565 cm{sup −1} in the respective ZnO NPs. Optical absorption spectra revealed the red shifted and estimated band gap is found to decrease with increase of Ni doping concentration. The PL spectra of all the samples exhibited a broad emission at 390 nm in the visible range. The carriers (donors) bounded on the Ni sites were observed from the micro Raman spectroscopic studies. Pure and Ni doped ZnO NPs showed significant changes in the M–H loop, especially the diamagnetic behavior changed into ferromagnetic nature for Ni doped samples. The antiferromagnetic super-exchange interactions between Ni{sup 2+} ions is increased in higher Ni doped ZnO NPs and also their antibacterial activity has been studied.

  19. Improved performance of quantum dot light emitting diode by modulating electron injection with yttrium-doped ZnO nanoparticles

    Science.gov (United States)

    Li, Jingling; Guo, Qiling; Jin, Hu; Wang, Kelai; Xu, Dehua; Xu, Yongjun; Xu, Gang; Xu, Xueqing

    2017-10-01

    In a typical light emitting diode (QD-LED), with ZnO nanoparticles (NPs) serving as the electron transport layer (ETL) material, excessive electron injection driven by the matching conduction band maximum (CBM) between the QD and this oxide layer usually causes charge imbalance and degrades the device performance. To address this issue, the electronic structure of ZnO NPs is modified by the yttrium (Y) doping method. We demonstrate that the CBM of ZnO NPs has a strong dependence on the Y-doping concentration, which can be tuned from 3.55 to 2.77 eV as the Y doping content increases from 0% to 9.6%. This CBM variation generates an enlarged barrier between the cathode and this ZnO ETL benefits from the modulation of electron injection. By optimizing electron injection with the use of a low Y-doped (2%) ZnO to achieve charge balance in the QD-LED, device performance is significantly improved with maximum luminance, peak current efficiency, and maximal external quantum efficiency increase from 4918 cd/m2, 11.3 cd/A, and 4.5% to 11,171 cd/m2, 18.3 cd/A, and 7.3%, respectively. This facile strategy based on the ETL modification enriches the methodology of promoting QD-LED performance.

  20. Formulation and Characterization of Cr2O3 Doped ZnO Thick Films as H2S Gas Sensor

    Directory of Open Access Journals (Sweden)

    A. V. PATIL

    2009-09-01

    Full Text Available Cr2O3 doped ZnO thick films have been prepared by screen printing technique and firing process. These films were characterized by X-ray diffraction (XRD, Scanning electron microscopy (SEM, and EDX. H2S gas sensing properties of these films were investigated at different operating temperatures and different H2S concentrations. The 7 wt. % Cr2O3 doped ZnO thick films exhibits excellent H2S gas sensing properties with maximum sensitivity of 99.12 % at 300 oC in air atmosphere with fast response and recovery time.

  1. Structural and photoluminescence properties of aligned Sb-doped ZnO nanocolumns synthesized by the hydrothermal method

    Energy Technology Data Exchange (ETDEWEB)

    Fang Xuan [School of Science, Changchun University of Science and Technology, 7089-WeiXing Road, Changchun, 130022 (China); Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic Zone Changchun, 130033 (China); Li Jinhua [School of Science, Changchun University of Science and Technology, 7089-WeiXing Road, Changchun, 130022 (China); Zhao Dongxu, E-mail: dxzhao2000@yahoo.com.c [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic Zone Changchun, 130033 (China); Li Binghui; Zhang Zhenzhong; Shen Dezhen [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic Zone Changchun, 130033 (China); Wang Xiaohua; Wei Zhipeng [School of Science, Changchun University of Science and Technology, 7089-WeiXing Road, Changchun, 130022 (China)

    2010-08-02

    Aligned Sb-doped ZnO nanocolumns were synthesized by a simple hydrothermal method. Based on the analyses of the X-ray diffraction and photoluminescence result, it could be confirmed that the Sb has successfully doped in the ZnO crystal lattices to form an accepter energy level. At 85 K, the recombination of the acceptor-bound exciton was predominant in PL spectrum, which was attributed to the transition of the (Sb{sub Zn}-2V{sub Zn}) complex bound exciton. The acceptor binding energy had been calculated to be 123 meV.

  2. Structural and photoluminescence properties of aligned Sb-doped ZnO nanocolumns synthesized by the hydrothermal method

    International Nuclear Information System (INIS)

    Fang Xuan; Li Jinhua; Zhao Dongxu; Li Binghui; Zhang Zhenzhong; Shen Dezhen; Wang Xiaohua; Wei Zhipeng

    2010-01-01

    Aligned Sb-doped ZnO nanocolumns were synthesized by a simple hydrothermal method. Based on the analyses of the X-ray diffraction and photoluminescence result, it could be confirmed that the Sb has successfully doped in the ZnO crystal lattices to form an accepter energy level. At 85 K, the recombination of the acceptor-bound exciton was predominant in PL spectrum, which was attributed to the transition of the (Sb Zn -2V Zn ) complex bound exciton. The acceptor binding energy had been calculated to be 123 meV.

  3. Influence of Cr doping on the stability and structure of small cobalt oxide clusters

    Energy Technology Data Exchange (ETDEWEB)

    Tung, Nguyen Thanh; Lievens, Peter; Janssens, Ewald, E-mail: ewald.janssens@fys.kuleuven.be [Laboratory of Solid-State Physics and Magnetism, KU Leuven, B-3001 Leuven (Belgium); Tam, Nguyen Minh; Nguyen, Minh Tho [Department of Chemistry, KU Leuven, B-3001 Leuven (Belgium)

    2014-07-28

    The stability of mass-selected pure cobalt oxide and chromium doped cobalt oxide cluster cations, Co{sub n}O{sub m}{sup +} and Co{sub n−1}CrO{sub m}{sup +} (n = 2, 3; m = 2–6 and n = 4; m = 3–8), has been investigated using photodissociation mass spectrometry. Oxygen-rich Co{sub n}O{sub m}{sup +} clusters (m ⩾ n + 1 for n = 2, 4 and m ⩾ n + 2 for n = 3) prefer to photodissociate via the loss of an oxygen molecule, whereas oxygen poorer clusters favor the evaporation of oxygen atoms. Substituting a single Co atom by a single Cr atom alters the dissociation behavior. All investigated Co{sub n−1}CrO{sub m}{sup +} clusters, except CoCrO{sub 2}{sup +} and CoCrO{sub 3}{sup +}, prefer to decay by eliminating a neutral oxygen molecule. Co{sub 2}O{sub 2}{sup +}, Co{sub 4}O{sub 3}{sup +}, Co{sub 4}O{sub 4}{sup +}, and CoCrO{sub 2}{sup +} are found to be relatively difficult to dissociate and appear as fragmentation product of several larger clusters, suggesting that they are particularly stable. The geometric structures of pure and Cr doped cobalt oxide species are studied using density functional theory calculations. Dissociation energies for different evaporation channels are calculated and compared with the experimental observations. The influence of the dopant atom on the structure and the stability of the clusters is discussed.

  4. Effects of morphology on the thermoelectric properties of Al-doped ZnO

    DEFF Research Database (Denmark)

    Han, Li; Van Nong, Ngo; Zhang, Wei

    2014-01-01

    The nanoparticles of Al-doped ZnO were successfully grown into rod-like and platelet-like morphologies by soft chemical routes. These powders were consolidated using spark plasma sintering (SPS) technique. The samples consolidated from rods and platelets exhibited characteristic structures...... consolidated from nanoparticles exhibited fine grains and highly distributed nanoprecipitates, resulting in a ZT value of 0.3 at 1223 K due to the lower thermal conductivity resulting from nanostructuring. Using the simple parabolic band model and Debye–Callaway thermal transport model, the anisotropic...

  5. Photo- and electroluminescence of undoped and rare earth doped ZnO electroluminors

    International Nuclear Information System (INIS)

    Bhushan, S.; Pandey, A.N.; Kaza, B.R.

    1977-01-01

    A series of undoped and rare earth (Dy, Yb, Nd, Pr, Gd, La, Sm and Er) doped ZnO electroluminors have been prepared and their photo- (PL) and electroluminescence (EL) spectra at different concentrations of rare earth ions have been investigated. PL and EL spectra of undoped electroluminescence consist of three peaks. Due to the addition of the rare earth ions these peaks are shifted either to the longer or to the shorter wavelength side. The intensities are also either decreased or increased. Experimental results favour the donor-accepted model for this system. (Auth.)

  6. Defect-band mediated ferromagnetism in Gd-doped ZnO thin films

    KAUST Repository

    Venkatesh, S.

    2015-01-07

    Gd-doped ZnO thin films prepared by pulsed laser deposition with Gd concentrations varying from 0.02–0.45 atomic percent (at. %) showed deposition oxygen pressure controlled ferromagnetism. Thin films prepared with Gd dopant levels (

  7. Thermoelectric effect in nano-scaled lanthanides doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Otal, E H; Canepa, H R; Walsoee de Reca, N E [Centro de Investigacion en Solidos, CITEFA, San Juan Bautista de La Salle 4397 (B1603ALO) Villa Martelli, Buenos Aires (Argentina); Schaeuble, N; Aguirre, M H, E-mail: canepa@citefa.gov.a, E-mail: myriam.aguirre@empa.c [Solid State Chemistry and Catalysis, Empa, Swiss Federal Laboratories for Materials Testing and Research, Ueberlandstrasse 129, CH-8600 Duebendorf (Switzerland)

    2009-05-01

    Start Nano-scaled ZnO with 1% Er doping was prepared by soft chemistry methods. The synthesis was carried out in anhydrous polar solvent to achieve a crystal size of a few nanometers. Resulting particles were processed as precipitates or multi layer films. Structural characterization was evaluated by X-Ray diffraction and transmission and scanning electron microscopy. In the case of films, UV-Vis characterization was made. The thermoelectrical properties of ZnO:Er were evaluated and compared with a typical good thermoelectric material ZnO:Al. Both materials have also shown high Seebeck coefficients and they can be considered as potential compounds for thermoelectric conversion.

  8. An investigation on the In doping of ZnO thin films by spray pyrolysis

    Science.gov (United States)

    Mahesh, Devika; Kumar, M. C. Santhosh

    2018-04-01

    Indium doped zinc oxide (IGZO)thin films are gaining much interest owing to its commercial application as transparent conductive oxide thin films. In the current study thin films indium doped ZnO thin films have been deposited on glass substrates by chemical spray pyrolysis technique with an indium concentration of 1, 2.5 and 4% in Zinc source. The films show a peak shift in the X-Ray Diffraction patterns with varying indium doping concentration. The (101) peak was enhanced for the 2.5 % indium doped films and variation in grain size with the different doping levels was studied. The as-deposited films are uniform and shown high transparency (>90%) in the visible region. Average thicknesses of films are found to be 800nm, calculated using the envelope method. The film with 2.5 % of indium content was found to be highly conducting than the rest, since for the lower and higher concentrations the conductivity was possibly halted by the limit in carrier concentration and indium segregation in the grain boundaries respectively. The enhancement of mobility and carrier concentration was clearly seen in the optimum films.

  9. Addressing the selectivity issue of cobalt doped zinc oxide thin film iso-butane sensors: Conductance transients and principal component analyses

    Science.gov (United States)

    Ghosh, A.; Majumder, S. B.

    2017-07-01

    Iso-butane (i-C4H10) is one of the major components of liquefied petroleum gas which is used as fuel in domestic and industrial applications. Developing chemi-resistive selective i-C4H10 thin film sensors remains a major challenge. Two strategies were undertaken to differentiate carbon monoxide, hydrogen, and iso-butane gases from the measured conductance transients of cobalt doped zinc oxide thin films. Following the first strategy, the response and recovery transients of conductances in these gas environments are fitted using the Langmuir adsorption kinetic model to estimate the heat of adsorption, response time constant, and activation energies for adsorption (response) and desorption (recovery). Although these test gases have seemingly different vapor densities, molecular diameters, and reactivities, analyzing the estimated heat of adsorption and activation energies (for both adsorption and desorption), we could not differentiate these gases unequivocally. However, we have found that the lower the vapor density, the faster the response time irrespective of the test gas concentration. As a second strategy, we demonstrated that feature extraction of conductance transients (using fast Fourier transformation) in conjunction with the pattern recognition algorithm (principal component analysis) is more fruitful to address the cross-sensitivity of Co doped ZnO thin film sensors. We have found that although the dispersion among different concentrations of hydrogen and carbon monoxide could not be avoided, each of these three gases forms distinct clusters in the plot of principal component 2 versus 1 and therefore could easily be differentiated.

  10. Realizing luminescent downshifting in ZnO thin films by Ce doping with enhancement of photocatalytic activity

    Science.gov (United States)

    Narayanan, Nripasree; Deepak, N. K.

    2018-04-01

    ZnO thin films doped with Ce at different concentration were deposited on glass substrates by spray pyrolysis technique. XRD analysis revealed the phase purity and polycrystalline nature of the films with hexagonal wurtzite geometry and the composition analysis confirmed the incorporation of Ce in the ZnO lattice in the case of doped films. Crystalline quality and optical transmittance diminished while electrical conductivity enhanced with Ce doping. Ce doping resulted in a red-shift of optical energy gap due to the downshift of the conduction band minimum after merging with Ce related impurity bands formed below the conduction band in the forbidden gap. In the room temperature photoluminescence spectra, UV emission intensity of the doped films decreased while the intensity of the visible emission band increased drastically implying the degradation in crystallinity as well as the incorporation of defect levels capable of luminescence downshifting. Ce doping showed improvement in photocatalytic efficiency by effectively trapping the free carriers and then transferring for dye degradation. Thus Ce doped ZnO thin films are capable of acting as luminescent downshifters as well as efficient photocatalysts.

  11. A synthesis method for cobalt doped carbon aerogels with high surface area and their hydrogen storage properties

    Energy Technology Data Exchange (ETDEWEB)

    Tian, H.Y.; Buckley, C.E. [Department of Imaging and Applied Physics, Curtin University of Technology, GPO Box U 1987, Perth 6845, WA (Australia); CSIRO National Hydrogen Materials Alliance, CSIRO Energy Centre, 10 Murray Dwyer Circuit, Steel River Estate, Mayfield West, NSW 2304 (Australia); Sheppard, D.A.; Paskevicius, M. [Department of Imaging and Applied Physics, Curtin University of Technology, GPO Box U 1987, Perth 6845, WA (Australia); Hanna, N. [CSIRO Process Science and Engineering, Waterford, WA (Australia)

    2010-12-15

    Carbon aerogels doped with nanoscaled Co particles were prepared by first coating activated carbon aerogels using a wet-thin layer coating process. The resulting metal-doped carbon aerogels had a higher surface area ({proportional_to}1667 m{sup 2} g{sup -1}) and larger micropore volume ({proportional_to}0.6 cm{sup 3} g{sup -1}) than metal-doped carbon aerogels synthesised using other methods suggesting their usefulness in catalytic applications. The hydrogen adsorption behaviour of cobalt doped carbon aerogel was evaluated, displaying a high {proportional_to}4.38 wt.% H{sub 2} uptake under 4.6 MPa at -196 C. The hydrogen uptake capacity with respect to unit surface area was greater than for pure carbon aerogel and resulted in {proportional_to}1.3 H{sub 2} (wt. %) per 500 m{sup 2} g{sup -1}. However, the total hydrogen uptake was slightly reduced as compared to pure carbon aerogel due to a small reduction in surface area associated with cobalt doping. The improved adsorption per unit surface area suggests that there is a stronger interaction between the hydrogen molecules and the cobalt doped carbon aerogel than for pure carbon aerogel. (author)

  12. Effect of doping concentration on the conductivity and optical properties of p-type ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Pathak, Trilok Kumar [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India); Kumar, Vinod, E-mail: vinod.phy@gmail.com [Department of Physics, University of the Free State, Bloemfontein (South Africa); Swart, H.C., E-mail: swarthc@ufs.ac.za [Department of Physics, University of the Free State, Bloemfontein (South Africa); Purohit, L.P., E-mail: proflppurohitphys@gmail.com [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India)

    2016-01-01

    Nitrogen doped ZnO (NZO) thin films were synthesized on glass substrates by the sol–gel and spin coating method. Zinc acetate dihydrates and ammonium acetate were used as precursors for zinc and nitrogen, respectively. X-ray diffraction study showed that the thin films have a hexagonal wurtzite structure corresponding (002) peak for undoped and doped ZnO thin films. The transmittance of the films was above 80% and the band gap of the film varies from 3.21±0.03 eV for undoped and doped ZnO. The minimum resistivity of NZO thin films was obtained as 0.473 Ω cm for the 4 at% of nitrogen (N) doping with a mobility of 1.995 cm{sup 2}/V s. The NZO thin films showed p-type conductivity at 2 and 3 at% of N doping. The AC conductivity measurements that were carried out in the frequency range 10 kHz to 0.1 MHz showed localized conduction in the NZO thin films. These highly transparent ZnO films can be used as a possible window layer in solar cells.

  13. Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

    International Nuclear Information System (INIS)

    Kim, Byunggu; Leem, Jae-Young

    2017-01-01

    ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

  14. Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Byunggu; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of)

    2017-01-15

    ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

  15. Synthesis and optical properties of Co2+-doped ZnO Network prepared by new precursors

    Science.gov (United States)

    Akhtari, Fereshteh; Zorriasatein, Suzan; Farahmandjou, Majid; Elahi, Seyed Mohammad

    2018-06-01

    Pure ZnO nanoparticles (NPs) and Co/ZnO alloy NPs were synthesized with different percentages of cobalt impurity (1%, 3%, 5%, and 25%) with new precursors through the coprecipitation method. The structural results of the XRD analysis indicated that the pure and impure samples have a wurtzite hexagonal structure such that with an elevation of Co impurity up to 1%, the size of the nanocrystals declines by up to 30 nm. Furthermore, the FESEM analysis results suggest the homogeneity of the NPs such that with increased cobalt impurity, its level declines. The TEM analysis results revealed that the NPs with 5% impurity have a mean size of 32 nm in spherical form. The FTIR optical analysis results suggest a very sharp absorption peak within the wavelength ranges of 434–448 cm‑1, belonging to the Zn-O vibration bond. In addition, the absorption peak developed at the wavelength of 3428 cm‑1 is related to the activation of the OH radicals, whose absorption value grows with the addition of an impurity, thereby, causing enhanced photocatalytic activity. The UV-DRS optical analysis indicated that the absorption wavelength grows with increased impurity, causing the development of redshift and a reduction of the energy band gap. In this regard, for the pure sample, the band gap value was 3.18 eV, while for the sample with 5% impurity, the band gap was obtained as 2.68 eV. The VSM magnetic analysis suggests ferromagnetic development in the impure sample, with a saturation magnetism of 16 memu g‑1 and a coercivity field of 342 G.

  16. Influence of Te and Se doping on ZnO films growth by SILAR method

    Science.gov (United States)

    Güney, Harun; Duman, Ćaǧlar

    2016-04-01

    The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

  17. Influence of Te and Se doping on ZnO films growth by SILAR method

    International Nuclear Information System (INIS)

    Güney, Harun; Duman, Çağlar

    2016-01-01

    The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

  18. Influence of Te and Se doping on ZnO films growth by SILAR method

    Energy Technology Data Exchange (ETDEWEB)

    Güney, Harun, E-mail: harunguney25@hotmail.com [Department of Electric and Energy, Vocation High School, Ağrı İbrahim Çeçen University (Turkey); Duman, Çağlar, E-mail: caglarduman@erzurum.edu.tr [Department of Electrical and Electronic Engineering, Faculty of Engineering, Erzurum Technical University (Turkey)

    2016-04-18

    The AIP Successive ionic layer adsorption and reaction (SILAR) is an economic and simple method to growth thin films. In this study, SILAR method is used to growth Selenium (Se) and Tellurium (Te) doped zinc oxide (ZnO) thin films with different doping rates. For characterization of the films X-ray diffraction (XRD), absorbance and scanning electron microscopy (SEM) are used. XRD results are showed well-defined strongly (002) oriented crystal structure for all samples. Also, absorbance measurements show, Te and Se concentration are proportional and inversely proportional with band gap energy, respectively. SEM measurements show that the surface morphology and thickness of the material varied with Se and/or Te and varying concentrations.

  19. Comparative study of Ni and Cu doped ZnO nanoparticles: Structural and optical properties

    Science.gov (United States)

    Thakur, Shaveta; Thakur, Samita; Sharma, Jyoti; Kumar, Sanjay

    2018-05-01

    Nanoparticles of undoped and doped (0.1 M Ni2+ and Cu2+) ZnO are synthesized using chemical precipitation method. The crystallite size, morphology, chemical bonding and optical properties of as prepared nanoparticles are determined by X-ray diffraction (XRD), Scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy and UV-visible spectra. XRD analysis shows that the prepared samples are single phase and have hexagonal wurtzite structure. The crystallite size of the doped and undoped nanoparticles is determined using Scherrer method. The crystallite size is found to be increased with concentration of nickel and copper. All stretching and vibrational bands are observed at their specific positions through FTIR. The increase in band gap can be attributed to the different chemical nature of dopant and host cation.

  20. The structural, electrical and optical properties of Mg-doped ZnO with different interstitial Mg concentration

    Energy Technology Data Exchange (ETDEWEB)

    Hu, Yonghong, E-mail: hchyh@njust.edu.cn [School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100 (China); Institute of Optoelectronics & Nanomaterials, College of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094 (China); Zeng, Haibo [Institute of Optoelectronics & Nanomaterials, College of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094 (China); Du, Jifu [School of Nuclear Technology and Chemistry & Biology, Hubei University of Science and Technology, Xianning 437100 (China); Hu, Ziyu [Beijing Computational Science Research Center, Beijing 100084 (China); Zhang, Shengli [Institute of Optoelectronics & Nanomaterials, College of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094 (China)

    2016-10-01

    Through first principle calculations, we studied the structural, electronic and optical properties of ZnO doped by interstitial Mg. With the increase of Mg content (x), the derivations of lattice parameters from the wurtzite ZnO become more and more significant. The Mg-doped ZnO with x below 15.79% is found to be n-type semiconductor. The minimum of energy band gap and light transmittance in high energy region (7.5–25 eV) decrease while the conductivity and refractive index increase with increasing x. Further increasing x up to 20%, the Mg-doped ZnO is found to be direct-band-gap semiconductor with great structural derivation from wurtzite phase. The light transmittance increases while the refractive index decreases with the increase of x due to the change of geometry and electronic structure. So, it’s concluded that the electronic and optical properties of ZnO doped by interstitial Mg may be greatly influenced by Mg content. - Graphical abstract: The minimum of energy gap decreases while the corresponding relative number of electrons into the conduction bands increases when the interstitial Mg content x in Mg-doped ZnO increases (0 ≤ x ≤ 15.79%). - Highlights: • The energy band gap decreases with the increase of interstitial Mg content from 5.88% to 15.79%. • The conductivity increases with the increase of interstitial Mg content from 5.88% to 15.79%. • The Mg{sub x}Zn{sub 1-x}O (interstitial Mg content x= 20%) is found to be a direct-band-gap semiconductor. • The light transmittance decreases with the increase of interstitial Mg content from 5.88% to 15.79%. • The refractive index increases with the increase of interstitial Mg content from 5.88% to 15.79%.

  1. Effects of Cr-doping on the photoluminescence and ferromagnetism at room temperature in ZnO nanomaterials prepared by soft chemistry route

    International Nuclear Information System (INIS)

    Wang Baiqi; Iqbal, Javed; Shan Xudong; Huang Guowei; Fu Honggang; Yu Ronghai; Yu Dapeng

    2009-01-01

    The pure and Cr-doped ZnO nanomaterials were prepared by soft chemistry route. The crystallinity and morphology of as-prepared ZnO nanomaterials were studied by X-ray diffraction (XRD), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM), which show that Cr-doping could influence crystal and improve the oriented growth of ZnO nanomaterials. The amount of contents and valence state of Cr ions were investigated by energy dispersive spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS), which demonstrate that the Cr ions are uniformly doped about 2 atm% in each nanowire and are in +3 valence state in doped ZnO nanomaterials. The effect of Cr-doping on the photoluminescence (PL) and magnetic properties of as-prepared ZnO nanomaterials were principally investigated at room temperature. The Cr-doping can adjust the energy level of ZnO nanocrystal and increase the amount of defects and oxygen vacancies, which lead to shift in the emission peak position in ultraviolet (UV) region and enhance the PL performance in visible light (VL) region of ZnO nanomaterials. In addition, the presence of Cr dopant in ZnO structures establishes the room-temperature ferromagnetism, which is possibly related to the existence of defects and oxygen vacancies as well as due to exchange interaction between Cr 3d and O 2p spin moments

  2. Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

    International Nuclear Information System (INIS)

    Korhonen, E; Prozheeva, V; Tuomisto, F; Bierwagen, O; Speck, J S; White, M E; Galazka, Z; Liu, H; Izyumskaya, N; Avrutin, V; Özgür, Ü; Morkoç, H

    2015-01-01

    We present positron annihilation results on Sb-doped SnO 2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO 2 the concentrations appear too low to cause significant compensation. (invited article)

  3. Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

    Science.gov (United States)

    Korhonen, E.; Prozheeva, V.; Tuomisto, F.; Bierwagen, O.; Speck, J. S.; White, M. E.; Galazka, Z.; Liu, H.; Izyumskaya, N.; Avrutin, V.; Özgür, Ü.; Morkoç, H.

    2015-02-01

    We present positron annihilation results on Sb-doped SnO2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO2 the concentrations appear too low to cause significant compensation.

  4. First-principles study on the effect of high In doping on the conductivity of ZnO

    International Nuclear Information System (INIS)

    Hou Qing-Yu; Li Ji-Jun; Ying Chun; Zhao Chun-Wang; Zhao Er-Jun; Zhang Yue

    2013-01-01

    Based on the density functional theory (DFT), using first-principles plane-wave ultrasoft pseudopotential method, the models of the unit cell of pure ZnO and two highly In-doped supercells of Zn 0.9375 In 0.0625 O and Zn 0.875 In 0.125 O are constructed, and the geometry optimizations of the three models are carried out. The total density of states (DOS) and the band structures (BS) are also calculated. The calculation results show that in the range of high doping concentration, when the doping concentration is hihger than a specific value, the conductivity decreases with the increase of the doping concentration of In in ZnO, which is in consistence with the change trend of the experimental results

  5. Influence of lithium doping on the structural and electrical characteristics of ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Johny, T. Anto [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Kumar, Viswanathan, E-mail: vkumar10@yahoo.com [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Imai, Hideyuki; Kanno, Isaku [Micro Engineering, Kyoto University, Kyoto 606-8501 (Japan)

    2012-06-30

    Thin films of undoped and lithium-doped Zinc oxide, (Zn{sub 1-x}Li{sub x})O; x = 0, 0.05, 0.10 and 0.20 were prepared by sol-gel method using spin-coating technique on silicon substrates [(111)Pt/Ti/SiO{sub 2}/Si)]. The influence of lithium doping on the structural, electrical and microstructural characteristics have been investigated by means of X-ray diffraction, leakage current, piezoelectric measurements and scanning electron microscopy. The resistivity of the ZnO film is found to increase markedly with low levels (x {<=} 0.05) of lithium doping thereby enhancing their piezoelectric applications. The transverse piezoelectric coefficient, e{sub 31}{sup Low-Asterisk} has been determined for the thin films having the composition (Zn{sub 0.95}Li{sub 0.05})O, to study their suitability for piezoelectric applications. - Highlights: Black-Right-Pointing-Pointer Preferentially c-axis oriented (Zn{sub 1-x}Li{sub x})O films were spin-coated on glass. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films exhibit dense columnar microstructure. Black-Right-Pointing-Pointer Low levels of lithium doping, increases the electrical resistivity of ZnO thin films. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films show high values of transverse piezoelectric coefficient, e{sup Low-Asterisk }{sub 31}.

  6. Doping effects of Co2+ ions on ZnO nanorods and their photocatalytic properties

    International Nuclear Information System (INIS)

    Qiu Xiaoqing; Li Guangshe; Sun Xuefei; Li Liping; Fu Xianzhi

    2008-01-01

    A series of Zn 1-x Co x O nanorods with dopant content ranging from x = 0.00 to 0.10 was prepared by a wet chemical method. All Zn 1-x Co x O samples were investigated by x-ray diffraction, transmission electron microscopy, energy-dispersion x-ray line mapping analysis, and UV-visible absorption spectroscopy. It was found that Co 2+ ions were homogeneously substituted for Zn 2+ ions in ZnO nanorods. Rhodamine B degradation was used as a probe reaction to evaluate the effect of Co 2+ doping on ZnO nanorods and photocatalytic performance under UV light and visible light irradiation. Co 2+ ions acted as the trapping or recombination centers for electrons and holes, leading to a reduction in photodegradation efficiency under UV light illumination. Alternatively, Co 2+ ions enhanced the optical absorption and produced the photoinduced carriers under visible illumination in terms of two charge transfer transitions involving Co 2+ ions. Consequently, Co 2+ ions substituted in the lattice of ZnO nanorods significantly improved the visible light photocatalytic activity

  7. Synthesis of cadmium oxide doped ZnO nanostructures using electrochemical deposition

    International Nuclear Information System (INIS)

    Singh, Trilok; Pandya, D.K.; Singh, R.

    2011-01-01

    Research highlights: → Ternary ZnCdO alloy semiconductor nanostructures were grown using electrochemical deposition. → X-ray diffraction measurements showed that the nanostructures were of wurtzite structure and possessed a compressive stress along the c-axis direction. → The cut-off wavelength shifted from blue to red on account of the Cd incorporation in the ZnO and the average transmittance decreased by ∼31%. → The bandgap tuning for 4-16 at% Cd in the initial solution was achieved in the range of 3.08-3.32 eV (up to 0.24 eV). - Abstract: Ternary ZnCdO alloy semiconductor nanostructures were grown using electrochemical deposition. Crystalline nanostructures/nanorods with cadmium concentration ranging from 4 to 16 at% in the initial solution were electrodeposited on tin doped indium oxide (ITO) conducting glass substrates at a constant cathodic potential -0.9 V and subsequently annealed in air at 300 deg. C. X-ray diffraction measurements showed that the nanostructures were of wurtzite structure and possessed a compressive stress along the c-axis direction. The elemental composition of nanostructures was confirmed by energy dispersive spectroscopy (EDS). ZnO nanostructures were found to be highly transparent and had an average transmittance of 85% in the visible range of the spectrum. After the incorporation of Cd content into ZnO the average transmittance decreased and the bandgap tuning was also achieved.

  8. Photoactivity of N-doped ZnO nanoparticles in oxidative and reductive reactions

    Science.gov (United States)

    Oliveira, Jéssica A.; Nogueira, André E.; Gonçalves, Maria C. P.; Paris, Elaine C.; Ribeiro, Caue; Poirier, Gael Y.; Giraldi, Tania R.

    2018-03-01

    N-doped ZnO is a prospective material for photocatalytic reactions. However, only oxidative paths are well investigated in the literature. This paper describes a comparative study about ZnO and ZnO:N potential for oxidative and reductive reactions, probed by rhodamine B dye photodegradation and CO2 photoreduction. The materials were prepared by the polymeric precursor method, using urea as a nitrogen source, and different heat treatments were used to observe their effects on surface decontamination, crystallinity, particle sizes and shapes, and photocatalytic performance. ZnO and ZnO:N presented a wurtzite crystalline structure and nanometric-scale particles. Samples submitted to higher temperatures showed lower specific surface areas, but higher crystallinity and lower contents of species adsorbed on their surfaces. On the other hand, the photocatalysts annealed in shorter times presented smaller crystallite sizes and lower crystallinity. These factors influenced the photoactivity in both conditions, i.e., oxidation and reduction reactions, under the ultraviolet and visible light, indicating that structural factors influenced the adequate charge separation and consequent photocatalytic activity since the as-synthesized samples were versatile photocatalysts in both redox reactions.

  9. Photoluminescence studies of ZnO doped with stable and radioactive impurities

    CERN Document Server

    Cullen, Joseph; Martin O, Henry

    In this work the IIb-VI compound semiconductor ZnO is doped, via ion implantation of stable and radioactive isotopes, in order to investigate the chemical nature of exciton re-combinations bound to previously unidentified defects. Photo-luminescence (PL) is discussed and is used extensively as the primary investigative technique. A new defect emission feature, centred around 3.324 eV, is found to be related to Ge impurities occupying substitutional Zn sites in ZnO. This centre is investigated by temperature dependent PL, piezo-spectroscopy and Zeeman spectroscopy. The centre is donor-like in nature. Uniaxial stress measurements indicate that the defect centre has trigonal symmetry and applied magnetic field measurements reveal the neutral charge state of the centre and the donor-like binding mechanism. Subsequent to this, a study is undertaken of the iso-electronic defect Hg in ZnO studying the zero phonon feature at 3.279 eV and its associated phonon replica band. Temperature dependent measurements reveal tw...

  10. Fabrication and Characterization of Highly Oriented N-Doped ZnO Nanorods by Selective Area Epitaxy

    Directory of Open Access Journals (Sweden)

    Yang Zhang

    2015-01-01

    Full Text Available High-quality nitrogen-doped ZnO nanorods have been selectively grown on patterned and bare ZnO templates by the combination of nanoimprint lithography and chemical vapor transport methods. The grown nanorods exhibited uniformity in size and orientation as well as controllable density and surface-to-volume ratio. The structural and optical properties of ZnO nanorods and the behaviour of N dopants have been investigated by means of the scanning electron microscope, photoluminescence (PL spectra, and Raman scattering spectra. The additional vibration modes observed in Raman spectra of N-doped ZnO nanorods provided solid evidence of N incorporation in ZnO nanorods. The difference of excitonic emissions from ZnO nanorods with varied density and surface-to-volume ratio suggested the different spatial distribution of intrinsic defects. It was found that the defects giving rise to acceptor-bound exciton (A0X emission were most likely to distribute in the sidewall surface with nonpolar characteristics, while the donor bound exciton (D0X emission related defects distributed uniformly in the near top polar surface.

  11. Tri-functional Fe2O3-encased Ag-doped ZnO nanoframework: magnetically retrievable antimicrobial photocatalyst

    Science.gov (United States)

    Karunakaran, Chockalingam; Vinayagamoorthy, Pazhamalai

    2016-11-01

    Fe2O3-encased ZnO nanoframework was obtained by hydrothermal method and was doped with Ag through photoreduction process. Energy dispersive x-ray spectroscopy, transmission electron microscopy (TEM), high resolution TEM, selected area electron diffractometry, x-ray diffractometry and Raman spectroscopy were employed for the structural characterization of the synthesized material. While the charge transfer resistance of the prepared nanomaterial is larger than those of Fe2O3 and ZnO the coercivity of the nanocomposite is less than that of hydrothermally obtained Fe2O3 nanostructures. Although Fe2O3/Ag-ZnO exhibits weak visible light absorption its band gap energy does not differ from that of ZnO. The photoluminescence of the fabricated nanoframework is similar to that of ZnO. The radiative recombination of charge carriers is slightly slower in Fe2O3/Ag-ZnO than in ZnO. The synthesized Fe2O3-encased Ag-doped ZnO, under UV A light, exhibits sustainable photocatalytic activity to degrade dye and is magnetically recoverable. Also, the Fe2O3/Ag-ZnO nanocomposite disinfects bacteria effectively in absence of direct illumination.

  12. Combined effect of oxygen deficient point defects and Ni doping in radio frequency magnetron sputtering deposited ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Saha, B., E-mail: biswajit.physics@gmail.com [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India); Department of Physics, National Institute of Technology Agartala, Jirania 799046, Tripura (India); Das, N.S.; Chattopadhyay, K.K. [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India)

    2014-07-01

    Ni doped ZnO thin films with oxygen deficiency have been synthesized on glass substrates by radio frequency magnetron sputtering technique using argon plasma. The combined effect of point defects generated due to oxygen vacancies and Ni doping on the optical and electrical properties of ZnO thin films has been studied in this work. Ni doping concentrations were varied and the structural, optical and electrical properties of the films were studied as a function of doping concentrations. The films were characterized with X-ray diffractometer, UV–Vis–NIR spectrophotometer, X-ray photoelectron spectroscopy, atomic force microscopy and electrical conductivity measurements. Oxygen deficient point defects (Schottky defects) made the ZnO thin film highly conducting while incorporation of Ni dopant made it more functional regarding their electrical and optical properties. The films were found to have tunable electrical conductivity with Ni doping concentrations. - Highlights: • ZnO thin films prepared by radio frequency magnetron sputtering technique • Synthesis process was stimulated to introduce Schottky-type point defects. • Point defects and external doping of Ni made ZnO thin films more functional. • Point defect induced high electrical conductivity in ZnO thin film. • Significant shift in optical bandgap observed in ZnO with Ni doping concentrations.

  13. Structural, optical, photoluminescence and photocatalytic assessment of Sr-doped ZnO nanoparticles

    International Nuclear Information System (INIS)

    Pradeev Raj, K.; Sadaiyandi, K.; Kennedy, A.; Thamizselvi, R.

    2016-01-01

    ZnO nanoparticles (NPs) and Strontium doped ZnO nanoparticles (2–6 mol %) (SZ-NPs) were synthesized via Co-precipitation method. Synthesized samples were investigated by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Elemental dispersive spectroscopy (EDS), UV–visible, and Photoluminescence (PL) spectroscopy. Photocatalytic studies for Rhodamine B (RhB) dye in aqueous solution under UV–Vis radiation. XRD analysis confirms that all the samples have hexagonal wurtzite structure. The average crystallite size of the nanoparticles was in the range of 29–51 nm. From the Williamson –Hall (W-H) plot, a positive slope is inferred for pure and SZ-NPs, confirming the presence of tensile strain. SEM images reveal the synthesized NPs are in nanometer range with various shapes are observed. The presence of strontium (Sr) in the host lattice was confirmed by EDS spectroscopy. The optical analysis shows the absorption decreases on doping and shifts slightly towards the longer wavelength region. The band gap energy (Eg) decreases (3.32–3.03 eV) with the increase of Sr dopant concentration. The photoluminescence (PL) spectrum reveals the UV emission is strong near the band-edge region (NBE) (392 nm) and intrinsic defects resulted in series of Vis emissions around 400–560 nm. Kinetic studies on RhB dye indicates the degradation rate has increased with dopant concentration. The improved photocatalytic activity is observed due to the efficient charge separation, improved visible light absorption, inhibition of the electron-hole pair's recombination and better adsorptive of RhB dye molecule on the surface of SZ-NPs. Moreover, the reduction in the total organic carbon (TOC) results reveals the improved photocatalytic activity of strontium doped ZnO NPs. - Highlights: • Effective synthesis of ZnO and Sr−ZnO nanoparticles by co-precipitation method. • Samples were characterized by XRD, SEM, EDS, UV–Vis and PL technique. • Higher optical absorption and

  14. Structural, optical, photoluminescence and photocatalytic assessment of Sr-doped ZnO nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Pradeev Raj, K., E-mail: pradeevraj@gmail.com [Research and Development Centre, Bharathiar University, Coimbatore, 641 046, Tamilnadu (India); Department of Physics, CSI College of Engineering, Ooty, The Nilgiris, 643 215, Tamil Nadu (India); Sadaiyandi, K. [Department of Physics, Alagappa Government Arts College, Karaikudi, Sivagangai, 630 003, Tamil Nadu (India); Kennedy, A. [Department of Physics, CSI College of Engineering, Ooty, The Nilgiris, 643 215, Tamil Nadu (India); Thamizselvi, R. [Department of Chemistry, L.R.G. Govt Arts College for Women, Tirupur, 641604, Tamil Nadu (India)

    2016-11-01

    ZnO nanoparticles (NPs) and Strontium doped ZnO nanoparticles (2–6 mol %) (SZ-NPs) were synthesized via Co-precipitation method. Synthesized samples were investigated by X-ray diffraction (XRD), Scanning Electron Microscopy (SEM), Elemental dispersive spectroscopy (EDS), UV–visible, and Photoluminescence (PL) spectroscopy. Photocatalytic studies for Rhodamine B (RhB) dye in aqueous solution under UV–Vis radiation. XRD analysis confirms that all the samples have hexagonal wurtzite structure. The average crystallite size of the nanoparticles was in the range of 29–51 nm. From the Williamson –Hall (W-H) plot, a positive slope is inferred for pure and SZ-NPs, confirming the presence of tensile strain. SEM images reveal the synthesized NPs are in nanometer range with various shapes are observed. The presence of strontium (Sr) in the host lattice was confirmed by EDS spectroscopy. The optical analysis shows the absorption decreases on doping and shifts slightly towards the longer wavelength region. The band gap energy (Eg) decreases (3.32–3.03 eV) with the increase of Sr dopant concentration. The photoluminescence (PL) spectrum reveals the UV emission is strong near the band-edge region (NBE) (392 nm) and intrinsic defects resulted in series of Vis emissions around 400–560 nm. Kinetic studies on RhB dye indicates the degradation rate has increased with dopant concentration. The improved photocatalytic activity is observed due to the efficient charge separation, improved visible light absorption, inhibition of the electron-hole pair's recombination and better adsorptive of RhB dye molecule on the surface of SZ-NPs. Moreover, the reduction in the total organic carbon (TOC) results reveals the improved photocatalytic activity of strontium doped ZnO NPs. - Highlights: • Effective synthesis of ZnO and Sr−ZnO nanoparticles by co-precipitation method. • Samples were characterized by XRD, SEM, EDS, UV–Vis and PL technique. • Higher optical absorption

  15. Room temperature ferromagnetism in Eu-doped ZnO nanoparticulate powders prepared by combustion reaction method

    International Nuclear Information System (INIS)

    Franco, A.; Pessoni, H.V.S.; Soares, M.P.

    2014-01-01

    Nanoparticulate powders of Eu-doped ZnO with 1.0, 1.5, 2.0 and 3.0 at% Eu were synthesized by combustion reaction method using zinc nitrate, europium nitrate and urea as fuel without subsequent heat treatments. X-ray diffraction patterns (XRD) of all samples showed broad peaks consistent with the ZnO wurtzite structure. The absence of extra reflections in the diffraction patterns ensures the phase purity, except for x=0.03 that exhibits small reflection corresponding to Eu 2 O 3 phase. The average crystallite size determined from the most prominent (1 0 1) peak of the diffraction using Scherrer's equation was in good agreement with those determined by transmission electron microscopy (TEM); being ∼26 nm. The magnetic properties measurements were performed using a vibrating sample magnetometer (VSM) in magnetic fields up to 2.0 kOe at room temperature. The hysteresis loops, typical of magnetic behaviors, indicating that the presence of an ordered magnetic structure can exist in the Eu-doped ZnO wurtzite structure at room temperature. The room temperature ferromagnetism behavior increases with the Eu 3+ doping concentration. All samples exhibited the same Curie temperature (T C ) around ∼726 K, except for x=0.01; T C ∼643 K. High resolution transmission electron microscopy (HRTEM) images revealed defects/strain in the lattice and grain boundaries of Eu-doped ZnO nanoparticulate powders. The origin of room temperature ferromagnetism in Eu-doped ZnO nanoparticulate powders was discussed in terms of these defects, which increase with the Eu 3+ doping concentration. - Highlights: • Room-temperature ferromagnetism. • Structural and magnetic properties of nanoparticulate powders of Zn 1−x Eu x O. • Combustion reaction method

  16. Ga-doped ZnO thin film surface characterization by wavelet and fractal analysis

    Energy Technology Data Exchange (ETDEWEB)

    Jing, Chenlei; Tang, Wu, E-mail: tang@uestc.edu.cn

    2016-02-28

    Graphical abstract: - Highlights: • Multi-resolution signal decomposition of wavelet transform is applied to Ga-doped ZnO thin films with various thicknesses. • Fractal properties of GZO thin films are investigated by box counting method. • Fractal dimension is not in conformity with original RMS roughness. • Fractal dimension mainly depends on the underside diameter (grain size) and distance between adjacent grains. - Abstract: The change in roughness of various thicknesses Ga-doped ZnO (GZO) thin films deposited by magnetron reactive sputtering on glass substrates at room temperature was measured by atomic force microscopy (AFM). Multi-resolution signal decomposition based on wavelet transform and fractal geometry was applied to process surface profiles, to evaluate the roughness trend of relevant frequency resolution. The results give a six-level decomposition and the results change with deposited time and surface morphology. Also, it is found that fractal dimension is closely connected to the underside diameter (grain size) and the distance between adjacent grains that affect the change rate of surface and the increase of the defects such as abrupt changes lead to a larger value of fractal dimension.

  17. Giant coercivity in ferromagnetic Co doped ZnO single crystal thin film

    International Nuclear Information System (INIS)

    Loukya, B.; Negi, D.S.; Dileep, K.; Kumar, N.; Ghatak, Jay; Datta, R.

    2013-01-01

    The origin of ferromagnetism in ZnO doped with transition metal impurities has been discussed extensively and appeared to be a highly controversial and challenging topic in today's solid state physics. Magnetism observed in this system is generally weak and soft. We have grown Co:ZnO up to 30 at% Co in single crystal thin film form on c-plane sapphire. A composition dependent coercivity is observed in this system which reaches peak value at 25 at% Co, the values are 860 Oe and 1149 Oe with applied field along parallel and perpendicular to the film substrate interface respectively. This giant coercivity might pave the way to exploit this material as a magnetic semiconductor with novel logic functionalities. The findings are explained based on defect band itinerant ferromagnetism and its partial interaction with localized d electrons of Co through charge transfer. Besides large coercivity, an increase in the band gap with Co concentration has also been observed along with blue emission peak with long tail confirming the formation of extended point defect levels in the host lattice band gap. - Highlights: • Co doped ZnO ferromagnetic single crystal thin film. • Giant coercivity in Co:ZnO thin film which may help to turn this material into application. • Cathodoluminescence (CL) data showing increase in band gap with Co concentrations. • A theoretical proposal is made to explain the observed giant coercivity

  18. Temperature dependent dual hydrogen sensor response of Pd nanoparticle decorated Al doped ZnO surfaces

    Energy Technology Data Exchange (ETDEWEB)

    Gupta, D.; Barman, P. B.; Hazra, S. K., E-mail: surajithazra@yahoo.co.in [Department of Physics and Materials Science, Jaypee University of Information Technology, Waknaghat, Solan, Himachal Pradesh-173234 (India); Dutta, D. [IC Design and Fabrication Centre, Department of Electronics and Telecommunication Engineering, Jadavpur University, Kolkata-700032 (India); Kumar, M.; Som, T. [SUNAG Laboratory, Institute of Physics, Sachivalaya Marg, Bhubaneswar 751005 (India)

    2015-10-28

    Sputter deposited Al doped ZnO (AZO) thin films exhibit a dual hydrogen sensing response in the temperature range 40 °C–150 °C after surface modifications with palladium nanoparticles. The unmodified AZO films showed no response in hydrogen in the temperature range 40 °C–150 °C. The operational temperature windows on the low and high temperature sides have been estimated by isolating the semiconductor-to-metal transition temperature zone of the sensor device. The gas response pattern was modeled by considering various adsorption isotherms, which revealed the dominance of heterogeneous adsorption characteristics. The Arrhenius adsorption barrier showed dual variation with change in hydrogen gas concentration on either side of the semiconductor-to-metal transition. A detailed analysis of the hydrogen gas response pattern by considering the changes in nano palladium due to hydrogen adsorption, and semiconductor-to-metal transition of nanocrystalline Al doped ZnO layer due to temperature, along with material characterization studies by glancing incidence X-ray diffraction, atomic force microscopy, and transmission electron microscopy, are presented.

  19. Effect of thickness on structural and electrical properties of Al-doped ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Garcés, F.A., E-mail: felipe.garces@santafe-conicet.gov.ar [Instituto de Física del Litoral (CONICET-UNL), Güemes 3450, Santa Fe S3000GLN (Argentina); Budini, N. [Instituto de Física del Litoral (CONICET-UNL), Güemes 3450, Santa Fe S3000GLN (Argentina); Arce, R.D.; Schmidt, J.A. [Instituto de Física del Litoral (CONICET-UNL), Güemes 3450, Santa Fe S3000GLN (Argentina); Facultad de Ingeniería Química, Universidad Nacional del Litoral, Santiago del Estero 2829, Santa Fe S3000AOM (Argentina)

    2015-01-01

    In this work, we have investigated the influence of thickness on structural and electrical properties of Al-doped ZnO films. Transparent conducting oxide films were grown by the spray pyrolysis technique from precursors prepared via the sol–gel method. We determined the structural properties of the films by performing X-ray diffraction and mosaicity measurements, which evidenced an increase of disorder and inhomogeneity between crystalline domains as the films thickened. This behavior was contrasted with results obtained from electrical measurements and was attributed to plastic deformation of the films as their thickness increased. As a result, the carrier mobility, the optical gap and the activation energy are affected due to emerging grain boundaries and a higher degree of disorder. - Highlights: • Al-doped ZnO thin films on glass with different thicknesses • Film thickness affects the morphological and electrical properties. • Increasing time deposition allows modification of resistivity and Hall mobility. • Mosaicity between crystalline domains increases with film thickness.

  20. Effect of thickness on structural and electrical properties of Al-doped ZnO films

    International Nuclear Information System (INIS)

    Garcés, F.A.; Budini, N.; Arce, R.D.; Schmidt, J.A.

    2015-01-01

    In this work, we have investigated the influence of thickness on structural and electrical properties of Al-doped ZnO films. Transparent conducting oxide films were grown by the spray pyrolysis technique from precursors prepared via the sol–gel method. We determined the structural properties of the films by performing X-ray diffraction and mosaicity measurements, which evidenced an increase of disorder and inhomogeneity between crystalline domains as the films thickened. This behavior was contrasted with results obtained from electrical measurements and was attributed to plastic deformation of the films as their thickness increased. As a result, the carrier mobility, the optical gap and the activation energy are affected due to emerging grain boundaries and a higher degree of disorder. - Highlights: • Al-doped ZnO thin films on glass with different thicknesses • Film thickness affects the morphological and electrical properties. • Increasing time deposition allows modification of resistivity and Hall mobility. • Mosaicity between crystalline domains increases with film thickness

  1. Doped nanocrystalline ZnO powders for non-linear resistor applications by spray pyrolysis method.

    Science.gov (United States)

    Hembram, Kaliyan; Vijay, R; Rao, Y S; Rao, T N

    2009-07-01

    Homogeneous and doped nanocrystalline ZnO powders (30-200 nm) were synthesized by spray pyrolysis technique. The spray pyrolysed powders were calcined in the temperature range of 500-750 degrees C. Formation of insulating pyrochlore phase started from 700 degrees C during the calcination itself. The calcined powders were compacted and sintered at different temperatures ranging from 900-1200 degrees C for 0.5-4 h. The densification behavior was found to be dependent on calcination temperature of the nanopowder. The resulting discs were found to have density (5.34-5.62 g/cc) in the range of 96-99% of theoretical density. The breakdown voltage value obtained for the nanopowder based non-linear resistor is 10.3 kV/cm with low leakage current density of 0.7 microA/cm2 and coefficient of nonlinearity as high as 193. The activation energy for grain growth of the doped ZnO nanopowder powders is 449.4 +/- 15 kJ/mol.

  2. Physical and chemical properties of a Ga-doped ZnO crystal

    International Nuclear Information System (INIS)

    Stashans, Arvids; Olivos, Katia; Rivera, Richard

    2011-01-01

    First-principles calculations based on density functional theory and strengthened by Hartree-Fock computations have been performed to study a Ga-doped wurtzite-type ZnO crystal. The large 108-atom supercell used throughout this work allows one to model a single point defect within the periodic supercell model. Thus, the Ga impurity produced purely local effects on the properties of the material. The electronic band structure was obtained for both pure and impurity-doped materials. The occurrence of free electrons in the conduction band was observed after the incorporation of Ga, implying the Ga dopant's contribution to n-type electrical conductivity in the ZnO crystal, in agreement with known experimental data. An analysis of the charges on atoms and obtained atomic displacements in the region surrounding the defect showed that there is some alteration in the chemical bonding because of the presence of Ga atoms. In particular, the ionic bonding is strengthened in the defect's neighbourhood.

  3. Physical and chemical properties of a Ga-doped ZnO crystal

    Energy Technology Data Exchange (ETDEWEB)

    Stashans, Arvids; Olivos, Katia; Rivera, Richard, E-mail: arvids@utpl.edu.e [Grupo de FisicoquImica de Materiales, Universidad Tecnica Particular de Loja, Apartado 11-01-608, Loja (Ecuador)

    2011-06-01

    First-principles calculations based on density functional theory and strengthened by Hartree-Fock computations have been performed to study a Ga-doped wurtzite-type ZnO crystal. The large 108-atom supercell used throughout this work allows one to model a single point defect within the periodic supercell model. Thus, the Ga impurity produced purely local effects on the properties of the material. The electronic band structure was obtained for both pure and impurity-doped materials. The occurrence of free electrons in the conduction band was observed after the incorporation of Ga, implying the Ga dopant's contribution to n-type electrical conductivity in the ZnO crystal, in agreement with known experimental data. An analysis of the charges on atoms and obtained atomic displacements in the region surrounding the defect showed that there is some alteration in the chemical bonding because of the presence of Ga atoms. In particular, the ionic bonding is strengthened in the defect's neighbourhood.

  4. Probing magnetism and electronic structure of Fe-doped ZnO thin films

    International Nuclear Information System (INIS)

    El Amiri, A.; Moubah, R.; Lmai, F.; Abid, M.; Hassanain, N.; Hlil, E.K.; Lassri, H.

    2016-01-01

    Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

  5. Probing magnetism and electronic structure of Fe-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    El Amiri, A., E-mail: aelamiri@casablanca.ma [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Moubah, R., E-mail: reda.moubah@hotmail.fr [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Lmai, F. [LPTA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Abid, M. [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Hassanain, N. [Laboratoire de Physique des Matériaux, Faculté des Sciences, BP 1014 Rabat (Morocco); Hlil, E.K. [Institut Néel, CNRS et Université Joseph Fourier, BP 166, 38042 Grenoble (France); Lassri, H. [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco)

    2016-01-15

    Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

  6. Glancing angle deposited Al-doped ZnO nanostructures with different structural and optical properties

    Energy Technology Data Exchange (ETDEWEB)

    Yildiz, A., E-mail: yildizab@gmail.com [Department of Physics and Astronomy, University of Arkansas at Little Rock, Little Rock, AR 72204 (United States); Department of Energy Systems Engineering, Faculty of Engineering and Natural Sciences, Yıldırım Beyazıt University, Ankara (Turkey); Cansizoglu, H. [Department of Physics and Astronomy, University of Arkansas at Little Rock, Little Rock, AR 72204 (United States); Turkoz, M. [Department of Physics and Astronomy, University of Arkansas at Little Rock, Little Rock, AR 72204 (United States); Department of Electrical-Electronic Engineering, Faculty of Engineering, University of Karabuk, Karabuk (Turkey); Abdulrahman, R.; Al-Hilo, Alaa; Cansizoglu, M.F.; Demirkan, T.M.; Karabacak, T. [Department of Physics and Astronomy, University of Arkansas at Little Rock, Little Rock, AR 72204 (United States)

    2015-08-31

    Al-doped ZnO (AZO) nanostructure arrays with different shapes (tilted rods, vertical rods, spirals, and zigzags) were fabricated by utilizing glancing angle deposition (GLAD) technique in a DC sputter growth unit at room temperature. During GLAD, all the samples were tilted at an oblique angle of about 90° with respect to incoming flux direction. In order to vary the shapes of nanostructures, each sample was rotated at different speeds around the substrate normal axis. Rotation speed did not only affect the shape but also changed the microstructural and optical properties of GLAD AZO nanostructures. The experimental results reveal that GLAD AZO nanostructures of different shapes each have unique morphological, crystal structure, mechanical, and optical properties determined by scanning electron microscopy, X-ray diffraction, transmission, and reflectance measurements. Vertical nanorods display the largest grain size, minimum strain, lowest defect density, and highest optical transmittance compared to the other shapes. Growth dynamics of GLAD has been discussed to explain the dependence of structural and optical properties of nanostructures on the substrate rotation speed. - Highlights: • Al-doped ZnO (AZO) nanostructures with different shapes were fabricated. • They have unique morphological, crystal structure, and optical properties. • Vertical AZO nanorods show an enhanced optical transmittance.

  7. Enhanced Doping Efficiency of Al-Doped ZnO by Atomic Layer Deposition Using Dimethylaluminum Isopropoxide as an Alternative Aluminum Precursor

    NARCIS (Netherlands)

    Wu, Y.; Potts, S.E.; Hermkens, P.M.; Knoops, H.C.M.; Roozeboom, F.; Kessels, W.M.M.

    2013-01-01

    Atomic layer deposition offers the unique opportunity to control, at the atomic level, the 3D distribution of dopants in highly uniform and conformal thin films. Here, it is demonstrated that the maximum doping efficiency of Al in ZnO can be improved from ∼10% to almost 60% using dimethylaluminum

  8. Properties of fluorine and tin co-doped ZnO thin films deposited by sol–gel method

    International Nuclear Information System (INIS)

    Pan, Zhanchang; Zhang, Pengwei; Tian, Xinlong; Cheng, Guo; Xie, Yinghao; Zhang, Huangchu; Zeng, Xiangfu; Xiao, Chumin; Hu, Guanghui; Wei, Zhigang

    2013-01-01

    Highlights: •F and Sn co-doped ZnO thin films were synthesized by sol–gel method. •The effects of different F doping concentrations were investigated. •The co-doped nanocrystals exhibit good crystal quality. •The origin of the photoluminescence emissions was discussed. •The films showed high transmittance and low resistivity. -- Abstract: Highly transparent and conducting fluorine (F) and tin (Sn) co-doped ZnO (FTZO) thin films were deposited on glass substrates by the sol–gel processing. The structure and morphology of the films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) with various F doping concentrations. SEM images showed that the hexagonal ZnO crystals were well-arranged on the glass substrates and the HRTEM images indicated that the individual nanocrystals are highly oriented and exhibited a perfect lattice structure. Owing to its high carrier concentration and mobility, as well as good crystal quality, a minimum resistivity of 1 × 10 −3 Ω cm was obtained from the FTZO thin film with 3% F doping, and the average optical transmittance in the entire visible wavelength region was higher than 90%. The X-ray photoelectron spectroscopy (XPS) study confirmed the substitution of Zn 2+ by Sn ions and Room temperature photoluminescence (PL) observed for pure and FTZO thin films suggested the films exhibit a good crystallinity with a very low defect concentration

  9. Defect mediated ferromagnetism in Ni-doped ZnO nanocrystals evidenced by positron annihilation spectroscopy

    Science.gov (United States)

    Chen, Zhi-Yuan; Chen, Z. Q.; Zou, B.; Zhao, X. G.; Tang, Z.; Wang, S. J.

    2012-10-01

    NiO/ZnO nanocomposites with NiO content of 4 at. % and 20 at. % were annealed up to 1200 °C to get Ni doped ZnO nanocrystals. Raman scattering spectra illustrate a broad and strong band at 500-600cm-1 in all nanocomposites after annealing above 700 °C, which suggests incorporation of Ni in the ZnO lattice. However, x-ray diffraction measurements show that NiO phase can be still observed in all nanocomposites after annealing, which indicates that Ni is partially doped into the ZnO structure. Positron annihilation measurements reveal large number of vacancy defects in the interface region of all nanocomposites, and they are gradually recovered with increasing annealing temperature up to 1000 °C. Room temperature ferromagnetism can be observed in the NiO/ZnO nanocomposites, which is stronger in the 20 at. % NiO/ZnO nanocomposites, and the magnetization decreases continuously with increasing annealing temperature. This indicates that the ferromagnetism at low annealing temperatures originates from the NiO nanograins, and they become antiferromanetic after subsequent higher temperature annealing which leads to the weakening of ferromagnetism. After annealing up to 1000 °C, the ferromagnetism in both the two samples becomes nearly invisible. The disappearance of ferromagnetism shows good coincidence with the recovery of vacancy defects in NiO/ZnO nanocomposites. It can be inferred that the ferromagnetism is mediated by vacancy defects which are distributed in the interface region.

  10. Grain growth kinetics for B2O3-doped ZnO ceramics

    Directory of Open Access Journals (Sweden)

    Yuksel Berat

    2015-06-01

    Full Text Available Grain growth kinetics in 0.1 to 2 mol % B2O3-added ZnO ceramics was studied by using a simplified phenomenological grain growth kinetics equation Gn = K0 · t · exp(-Q/RT together with the physical properties of sintered samples. The samples, prepared by conventional ceramics processing techniques, were sintered at temperatures between 1050 to 1250 °C for 1, 2, 3, 5 and 10 hours in air. The kinetic grain growth exponent value (n and the activation energy for the grain growth of the 0.1 mol % B2O3-doped ZnO ceramics were found to be 2.8 and 332 kJ/mol, respectively. By increasing B2O3 content to 1 mol %, the grain growth exponent value (n and the activation energy decreased to 2 and 238 kJ/mol, respectively. The XRD study revealed the presence of a second phase, Zn3B2O6 formed when the B2O3 content was > 1 mol %. The formation of Zn3B2O6 phase gave rise to an increase of the grain growth kinetic exponent and the grain growth activation energy. The kinetic grain growth exponent value (n and the activation energy for the grain growth of the 2 mol % B2O3-doped ZnO ceramics were found to be 3 and 307 kJ/mol, respectively. This can be attributed to the second particle drag (pinning mechanism in the liquid phase sintering.

  11. Bound magnetic polaron in Zn-rich cobalt-doped ZnSe nanowires

    Science.gov (United States)

    Hou, Lipeng; Pan, Longfei; Liang, Bianbian; Liu, Yuting; Zhang, Li; Bukhtiar, Arfan; Shi, Lijie; Liu, Ruibin; Zou, Bingsuo

    2018-02-01

    The micro-luminescence spectra of the diluted magnetic semiconductor (DMS) can reflect the spin-exciton interaction and related relaxation process. Here the micro-photoluminescence (micro-PL) spectra and PL lifetime measurements have been done on an individual ferromagnetic (FM)-coupled cobalt (Co) doped zinc selenide (ZnSe) nanowire. There occurs a double-peak profile in its near bandedge emission spectrum: the first peak is from free exciton (FX) and the second comes from magnetic polaron (MP). In their temperature dependent PL spectra, the MP emission peak demonstrates obviously temperature-independent behavior, in contrast to the behaviors of FX and reported exciton MP in nanobelt. It is found that in this Co(II) doped ZnSe nanowires, this MP’s temperature-independent emission is related to the coupling between exciton and a FM nanocluster (↑↑↓). The nanocluster is likely due to the interaction of Se vacancies of the wide bandgap semiconductors with the antiferromagnetic (AFM) arrangement transition metal (TM) ions in these Se-deficient Co doped ZnSe nanowires. These results reflect that the AFM coupling TM ions pair can give rise to FM behavior with the involvement of positive charge defect, also indicating that the micro-luminescence detection can be used to study the magnetic coupling in DMS.

  12. Effects of Annealing Temperature on Properties of Ti-Ga-Doped ZnO Films Deposited on Flexible Substrates.

    Science.gov (United States)

    Chen, Tao-Hsing; Chen, Ting-You

    2015-11-03

    An investigation is performed into the optical, electrical, and microstructural properties of Ti-Ga-doped ZnO films deposited on polyimide (PI) flexible substrates and then annealed at temperatures of 300 °C, 400 °C, and 450 °C, respectively. The X-ray diffraction (XRD) analysis results show that all of the films have a strong (002) Ga doped ZnO (GZO) preferential orientation. As the annealing temperature is increased to 400 °C, the optical transmittance increases and the electrical resistivity decreases. However, as the temperature is further increased to 450 °C, the transmittance reduces and the resistivity increases due to a carbonization of the PI substrate. Finally, the crystallinity of the ZnO film improves with an increasing annealing temperature only up to 400 °C and is accompanied by a smaller crystallite size and a lower surface roughness.

  13. p-type ZnO films with solid-source phosphorus doping by molecular-beam epitaxy

    International Nuclear Information System (INIS)

    Xiu, F.X.; Yang, Z.; Mandalapu, L.J.; Liu, J.L.; Beyermann, W. P.

    2006-01-01

    Phosphorus-doped p-type ZnO films were grown on r-plane sapphire substrates using molecular-beam epitaxy with a solid-source GaP effusion cell. X-ray diffraction spectra and reflection high-energy electron diffraction patterns indicate that high-quality single crystalline (1120) ZnO films were obtained. Hall and resistivity measurements show that the phosphorus-doped ZnO films have high hole concentrations and low resistivities at room temperature. Photoluminescence (PL) measurements at 8 K reveal a dominant acceptor-bound exciton emission with an energy of 3.317 eV. The acceptor energy level of the phosphorus dopant is estimated to be 0.18 eV above the valence band from PL spectra, which is also consistent with the temperature dependence of PL measurements

  14. Magnetism in Sc-doped ZnO with zinc vacancies: A hybrid density functional and GGA + U approaches

    KAUST Repository

    Kanoun, Mohammed; Goumri-Said, Souraya; Schwingenschlö gl, Udo; Manchon, Aurelien

    2012-01-01

    We investigate the zinc vacancy effects on the electronic structures and magnetic properties of Sc-doped ZnO, by performing first-principles calculations within both GGA + U and Heyd-Scuseria-Ernzerhof hybrid functional methods. We find that Sc impurities stabilize considerably Zn vacancies. The electronic and magnetic analysis shows a half metallic ferromagnetic character with a total magnetic moment of 2.01 μ B. The magnetism mainly stems from the O 2p states around the Zn vacancies. Calculations with the hybrid density functional agree with the GGA + U results but give an accurate description of the electronic structure for pure ZnO and Sc-doped ZnO with Zn vacancies. © 2012 Elsevier B.V. All rights reserved.

  15. Nucleation, Growth Mechanism, and Controlled Coating of ZnO ALD onto Vertically Aligned N-Doped CNTs.

    Science.gov (United States)

    Silva, R M; Ferro, M C; Araujo, J R; Achete, C A; Clavel, G; Silva, R F; Pinna, N

    2016-07-19

    Zinc oxide thin films were deposited on vertically aligned nitrogen-doped carbon nanotubes (N-CNTs) by atomic layer deposition (ALD) from diethylzinc and water. The study demonstrates that doping CNTs with nitrogen is an effective approach for the "activation" of the CNTs surface for the ALD of metal oxides. Conformal ZnO coatings are already obtained after 50 ALD cycles, whereas at lower ALD cycles an island growth mode is observed. Moreover, the process allows for a uniform growth from the top to the bottom of the vertically aligned N-CNT arrays. X-ray photoelectron spectroscopy demonstrates that ZnO nucleation takes place at the N-containing species on the surface of the CNTs by the formation of the Zn-N bonds at the interface between the CNTs and the ZnO film.

  16. Effect of co-doping process on topography, optical and electrical properties of ZnO nanostructured

    Science.gov (United States)

    Mohamed, R.; Mamat, M. H.; Malek, M. F.; Ismail, A. S.; Yusoff, M. M.; Syamsir, S. A.; Khusaimi, Z.; Rusop, M.

    2018-05-01

    We investigated of Undoped ZnO and Magnesium (Mg)-Aluminium (Al) co-doped Zinc Oxide (MAZO) nanostructured films were prepared by sol gel spin coating technique. The surface topography was analyzed using Atomic Force Microscopy (AFM). Based on the AFM results, Root Mean Square (RMS) of MAZO films have rougher surface compared to pure ZnO films. The optical and electrical properties of thin film samples were characterized using Uv-Vis spectroscopy and two point probes, current-voltage (I-V) measurements. The transmittance spectra for both thin samples was above 80% in the visible wavelength. The MAZO film shows the highest conductivity compared to pure ZnO films. This result indicates that the improvement of carrier mobility throughout doping process and possibly contribute by extra ion charge.

  17. Magnetism in Sc-doped ZnO with zinc vacancies: A hybrid density functional and GGA + U approaches

    KAUST Repository

    Kanoun, Mohammed

    2012-04-01

    We investigate the zinc vacancy effects on the electronic structures and magnetic properties of Sc-doped ZnO, by performing first-principles calculations within both GGA + U and Heyd-Scuseria-Ernzerhof hybrid functional methods. We find that Sc impurities stabilize considerably Zn vacancies. The electronic and magnetic analysis shows a half metallic ferromagnetic character with a total magnetic moment of 2.01 μ B. The magnetism mainly stems from the O 2p states around the Zn vacancies. Calculations with the hybrid density functional agree with the GGA + U results but give an accurate description of the electronic structure for pure ZnO and Sc-doped ZnO with Zn vacancies. © 2012 Elsevier B.V. All rights reserved.

  18. Enhanced sintering and conductivity study of cobalt or nickel doped solid solution of barium cerate and zirconate

    DEFF Research Database (Denmark)

    Ricote, Sandrine; Bonanos, Nikolaos

    2010-01-01

    BaZr(0.9 − x)CexY(0.1 − y)CoyO(3 − δ) (with x = 0 and 0.2; y = 0.01; 0.02; 0.05) and BaZr(0.9 − x)CexY(0.1 − y)NiyO(3 − δ) (with x = 0 and 0.2; y = 0.01; 0.02) compounds have been synthesized by solid state reaction at 1400 °C and obtained as dense pellets after sintering at 1450 °C. Cobalt...... or nickel doping reduces the sintering temperature by about 250 °C. The samples are stable in a CO2 rich atmosphere at 600 °C but the 5% B site Co doped samples are aging in wet atmosphere. The conductivity has been measured for the 1 and 2% doped samples (both cobalt and nickel), in different wet...

  19. A boron and gallium co-doped ZnO intermediate layer for ZnO/Si heterojunction diodes

    Science.gov (United States)

    Lu, Yuanxi; Huang, Jian; Li, Bing; Tang, Ke; Ma, Yuncheng; Cao, Meng; Wang, Lin; Wang, Linjun

    2018-01-01

    ZnO (Zinc oxide)/Si (Silicon) heterojunctions were prepared by depositing n-type ZnO films on p-type single crystal Si substrates using magnetron sputtering. A boron and gallium co-doped ZnO (BGZO) high conductivity intermediate layer was deposited between aurum (Au) electrodes and ZnO films. The influence of the BGZO layer on the properties of Au/ZnO contacts and the performance of ZnO/Si heterojunctions was investigated. The results show an improvement in contact resistance by introducing the BGZO layer. Compared with the ZnO/Si heterojunction, the BGZO/ZnO/Si heterojunction exhibits a larger forward current, a smaller turn-on voltage and higher ratio of ultraviolet (UV) photo current/dark current.

  20. Synergistic effect of indium and gallium co-doping on the properties of RF sputtered ZnO thin films

    Science.gov (United States)

    Shaheera, M.; Girija, K. G.; Kaur, Manmeet; Geetha, V.; Debnath, A. K.; Karri, Malvika; Thota, Manoj Kumar; Vatsa, R. K.; Muthe, K. P.; Gadkari, S. C.

    2018-04-01

    ZnO thin films were synthesized using RF magnetron sputtering, with simultaneous incorporation of Indium (In) and Gallium (Ga). The structural, optical, chemical composition and surface morphology of the pure and co-doped (IGZO) thin films were characterized by X-Ray diffraction (XRD), UV-visible spectroscopy, Field Emission Scanning Electron Microscopy (FESEM), and Raman spectroscopy. XRD revealed that these films were oriented along c-axis with hexagonal wurtzite structure. The (002) diffraction peak in the co-doped sample was observed at 33.76° with a slight shift towards lower 2θ values as compared to pure ZnO. The surface morphology of the two thin films was observed to differ. For pure ZnO films, round grains were observed and for IGZO thin films round as well as rod type grains were observed. All thin films synthesized show excellent optical properties with more than 90% transmission in the visible region and band gap of the films is observed to decrease with co-doping. The co doping of In and Ga is therefore expected to provide a broad range optical and physical properties of ZnO thin films for a variety of optoelectronic applications.

  1. Negative permittivity of ZnO thin films prepared from aluminum and gallium doped ceramics via pulsed-laser deposition

    DEFF Research Database (Denmark)

    Bodea, M. A.; Sbarcea, G.; Naik, G. V.

    2013-01-01

    Aluminum and gallium doped zinc oxide thin films with negative dielectric permittivity in the near infrared spectral range are grown by pulsed laser deposition. Composite ceramics comprising ZnO and secondary phase Al2O3 or Ga2O3 are employed as targets for laser ablation. Films deposited on glass...

  2. Tuning the nanostructures and optical properties of undoped and N-doped ZnO by supercritical fluid treatment

    Science.gov (United States)

    Li, Yaping; Wang, Hui-Qiong; Chu, Tian-Jian; Li, Yu-Chiuan; Li, Xiaojun; Liao, Xiaxia; Wang, Xiaodan; Zhou, Hua; Kang, Junyong; Chang, Kuan-Chang; Chang, Ting-Chang; Tsai, Tsung-Ming; Zheng, Jin-Cheng

    2018-05-01

    Treatment of ZnO films in a supercritical fluid (SCF) has been reported to improve the performance of devices in which the treated ZnO films are incorporated; however, the mechanism of this improvement remains unclear. In this paper, we study the transformation of the surface morphologies and emission properties of ZnO films before and after SCF treatment, establishing the relationship between the treated and untreated structures and thereby enabling tuning of the catalytic or opto-electronic performance of ZnO films or ZnO-film-based devices. Both undoped and N-doped ZnO nanostructures generated by SCF treatment of films are investigated using techniques to characterize their surface morphology (scanning electron microscopy (SEM) and atomic force microscopy (AFM)) as well as room-temperature photoluminescence (RT-PL) spectroscopy. The water-mixed supercritical CO2 (W-SCCO2) technology was found to form nanostructures in ZnO films through a self-catalyzed process enabled by the Zn-rich conditions in the ZnO films. The W-SCCO2 was also found to promote the inhibition of defect luminescence by introducing -OH groups onto the films. Two models are proposed to explain the effects of the treatment with W-SCCO2. This work demonstrates that the W-SCCO2 technology can be used as an effective tool for the nanodesign and property enhancement of functional metal oxides.

  3. Effects of cobalt doping on structural, morphological, and optical properties of Zn2SiO4 nanophosphors prepared by sol-gel method

    Directory of Open Access Journals (Sweden)

    Norhafizah Mohd Rasdi

    Full Text Available In this paper, undoped and cobalt (II (3, and 5 mol % doped zinc silicate nanophosphors prepared by a sol-gel method which were heated at 1000 °C were studied in detail. From the XRD result, undoped and Co2+ doped zinc silicate sample yields α- and β-Zn2SiO4. This also shows that α-Zn2SiO4 acts as the primary phase in the crystal structure of the sample. For FESEM, the grain size decreases as the dopant increases where undoped sample indicates average grain size of 181 nm while 3 and 5 mol % exhibits containing ones 136.89 nm and 176.22 nm respectively. With FTIR transmission a major peak at range of 1100 cm−1, 880, 550, and 350 assigning as Si-O-Si asymmetric stretching, SiO4 asymmetric stretching, ZnO4 symmetric stretching, and Si-O asymmetric deformation vibration were observed respectively. The absorption band of doped Zn2SiO4 exhibited a higher absorbance intensity in the UV region compared to undoped Zn2SiO4. Besides, all the samples depict that the sample was having a red shift in which the band shifted to the longer wavelength. The energy band gap value of undoped sample shows 3.07 eV and when Co2+ dopant (3 and 5 mol % was introduced, the energy band gap started to decrease (2.46 and 2.42 eV respectively. PL emission presents two peaks at blue emissions (420 and 480 nm and a green emission (525 nm. The result present that Co2+:Zn2SiO4 is potentially good to use as blue and green phosphors for luminescent optical material. Keywords: Cobalt (II doped zinc silicate, Transition metal, Sol-gel method, Nanophosphors, Photoluminescence

  4. Epitaxial growth of Sb-doped nonpolar a-plane ZnO thin films on r-plane sapphire substrates by RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Hou-Guang, E-mail: houguang@isu.edu.tw [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China); Hung, Sung-Po [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China)

    2014-02-15

    Highlights: ► Sb-doped nonpolar a-plane ZnO layers were epitaxially grown on sapphire substrates. ► Crystallinity and electrical properties were studied upon growth condition and doping concentration. ► The out-of-plane lattice spacing of ZnO films reduces monotonically with increasing Sb doping level. ► The p-type conductivity of ZnO:Sb film is closely correlated with annealing condition and Sb doping level. -- Abstract: In this study, the epitaxial growth of Sb-doped nonpolar a-plane (112{sup ¯}0) ZnO thin films on r-plane (11{sup ¯}02) sapphire substrates was performed by radio-frequency magnetron sputtering. The influence of the sputter deposition conditions and Sb doping concentration on the microstructural and electrical properties of Sb-doped ZnO epitaxial films was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and the Hall-effect measurement. The measurement of the XRD phi-scan indicated that the epitaxial relationship between the ZnO:Sb layer and sapphire substrate was (112{sup ¯}0){sub ZnO}//(11{sup ¯}02){sub Al{sub 2O{sub 3}}} and [11{sup ¯}00]{sub ZnO}//[112{sup ¯}0]{sub Al{sub 2O{sub 3}}}. The out-of-plane a-axis lattice parameter of ZnO films was reduced monotonically with the increasing Sb doping level. The cross-sectional transmission electron microscopy (XTEM) observation confirmed the absence of any significant antimony oxide phase segregation across the thickness of the Sb-doped ZnO epitaxial film. However, the epitaxial quality of the films deteriorated as the level of Sb dopant increased. The electrical properties of ZnO:Sb film are closely correlated with post-annealing conditions and Sb doping concentrations.

  5. The effect of Ca doping on specific heat of YCoO{sub 3} cobaltate

    Energy Technology Data Exchange (ETDEWEB)

    Thakur, Rasna, E-mail: rasnathakur@yahoo.com; Thakur, Rajesh K., E-mail: thakur.rajesh2009@gmail.com; Gaur, N. K., E-mail: srl-nkgaur@yahoo.co.in [Department of Physics, Barkatullah University, Bhopal, 462026 (India)

    2016-05-06

    We have investigated the thermodynamic properties of Y{sub 1-x}Ca{sub x}CoO{sub 3} (0.0≤x≤0.1) perovskites by means of a modified rigid ion model (MRIM). The variations of specific heat at wide temperatures 1 K ≤ T ≤ 1000 K are reported. Also, the effect of lattice distortions on the elastic and thermal properties of pure and Ca doped cobaltates has been studied by an atomistic approach. Besides, we have reported bulk modulus (B), cohesive energy (ϕ), molecular force constant (f), Reststrahlen frequency (υ), Debye temperature (θ{sub D}), Gruneisen parameter (γ) and specific heat (C). It is found that the present model has a promise to predict the thermodynamic properties of other perovskites as well.

  6. Synthesis and characterization of strontium molybdate doped with copper, cobalt and zinc for purposes photocatalytic

    International Nuclear Information System (INIS)

    Dutra, F.B.; Silva, M.M.S.; Moriyama, A.L.L.; Souza, C.P.

    2016-01-01

    The broad concerns of contemporary society with environmental problems requires legislation and more effective techniques for wastewater treatment. In recent years, ceramic materials that have properties such as high melting points and high stability have been receiving great emphasis in several studies in particular heterogeneous photocatalysis, rapid and efficient method for the complete mineralization of contaminants. In this context, the present work deals with the synthesis and characterization of molybdate Strontium (SrMoO4) doped with copper, cobalt and zinc for the purpose of photocatalytic studies. The compounds were synthesized by complexation method EDTA / Citrate basic medium. The powders were characterized by Thermogravimetric Analysis (TG), X-Ray Diffraction (XRD), Particle size distribution by laser diffraction, Spectroscopy in the UV-Visible region, Energy Dispersive Spectroscopy (EDS) and Scanning Electron Microscopy (SEM), showing promising results as the crystalline phase of development and potential uses for the purpose of heterogeneous photocatalysis. (author)

  7. Optoelectronic Characterization of Ta-Doped ZnO Thin Films by Pulsed Laser Deposition.

    Science.gov (United States)

    Koo, Horng-Show; Peng, Jo-Chi; Chen, Mi; Chin, Hung-I; Chen, Jaw-Yeh; Wu, Maw-Kuen

    2015-11-01

    Transparent conductive oxide of Ta-doped ZnO (TZO) film with doping amount of 3.0 wt% have been deposited on glass substrates (Corning Eagle XG) at substrate temperatures of 100 to 500 degrees C by the pulsed laser deposition (PLD) technique. The effect of substrate temperature on the structural, optical and electronic characteristics of Ta-doped ZnO (TZO) films with 3.0 wt% dopant of tantalum oxide (Ta2O5) was measured and demonstrated in terms of X-ray diffraction (XRD), ultraviolet-visible spectrometer (UV-Vis), four-probe and Hall-effect measurements. X-ray diffraction pattern shows that TZO films grow in hexagonal crystal structure of wurtzite phase with a preferred orientation of the crystallites along (002) direction and exhibits better physical characteristics of optical transmittance, electrical conductivity, carrier concentration and mobility for the application of window layer in the optoelectronic devices of solar cells, OLEDs and LEDs. The lowest electrical resistivity (ρ) and the highest carrier concentration of the as-deposited film deposited at 300 degrees C are measured as 2.6 x 10(-3) Ω-cm and 3.87 x 10(-20) cm(-3), respectively. The highest optical transmittance of the as-deposited film deposited at 500 degrees C is shown to be 93%, compared with another films deposited below 300 degrees C. It is found that electrical and optical properties of the as-deposited TZO film are greatly dependent on substrate temperature during laser ablation deposition.

  8. Synthesis, microstructural characterization and optical properties of undoped, V and Sc doped ZnO thin films

    International Nuclear Information System (INIS)

    Amezaga-Madrid, P.; Antunez-Flores, W.; Ledezma-Sillas, J.E.; Murillo-Ramirez, J.G.; Solis-Canto, O.; Vega-Becerra, O.E.; Martinez-Sanchez, R.; Miki-Yoshida, M.

    2011-01-01

    Research highlights: → Undoped, V and Sc doped ZnO thin films by Aerosol Assisted Chemical Vapour Deposition. → Optimum substrate temperatures of 673 K and 623 K for Sc and V doped films. → Around one third of the dopants in solution were deposited into the films. → Crystallite and grain size decreased with the increase of dopant concentration. → Optical band gap increased from 3.29 to 3.32 eV for undoped to 7 Sc/Zn at. %. - Abstract: Many semiconductor oxides (ZnO, TiO 2 , SnO 2 ) when doped with a low percentage of non-magnetic (V, Sc) or magnetic 3d (Co, Mn, Ni, Fe) cation behave ferromagnetically. They have attracted a great deal of interest due to the integration of semiconducting and magnetic properties in a material. ZnO is one of the most promising materials to carry out these tasks in view of the fact that it is optically transparent and has n or p type conductivity. Here, we report the synthesis, microstructural characterization and optical properties of undoped, V and Sc doped zinc oxide thin films. ZnO based thin films with additions of V and Sc were deposited by the Aerosol Assisted Chemical Vapour Deposition method. V and Sc were incorporated separately in the precursor solution. The films were uniform, transparent and non-light scattering. The microstructure of the films was characterized by Grazing Incidence X-ray Diffraction, Scanning Electron Microscopy, and Scanning Probe Microscopy. Average grain size and surface rms roughness were estimated by the measurement of Atomic Force Microscopy. The microstructure of doped ZnO thin films depended on the type and amount of dopant material incorporated. The optical properties were determined from specular reflectance and transmittance spectra. Results were analyzed to determine the optical constant and band gap of the films. An increase in the optical band gap with the content of Sc dopant was obtained.

  9. Structural, electrical, and dielectric properties of Cr doped ZnO thin films: Role of Cr concentration

    Energy Technology Data Exchange (ETDEWEB)

    Gürbüz, Osman, E-mail: osgurbuz@yildiz.edu.tr; Okutan, Mustafa

    2016-11-30

    Highlights: • Magnetic material of Cr and semiconductor material of ZnO were grown by the magnetron sputtering co-sputter technique. • Perfect single crystalline structures were grown. • DC and AC conductivity with dielectric properties as a function of frequency (f = 5Hz–13 MHz) at room temperature were measured and compared. • Cr doped ZnO can be used in microwave, sensor and optoelectronic devices as the electrical conductivity increases while dielectric constant decreases with the Cr content. - Abstract: An undoped zinc oxide (ZnO) and different concentrations of chromium (Cr) doped ZnO Cr{sub x}ZnO{sub 1−x} (x = 3.74, 5.67, 8.10, 11.88, and 15.96) thin films were prepared using a magnetron sputtering technique at room temperature. These films were characterized by X-ray diffraction (XRD), High resolution scanning electron microscope (HR-SEM), and Energy dispersive X-ray spectrometry (EDS). XRD patterns of all the films showed that the films possess crystalline structure with preferred orientation along the (100) crystal plane. The average crystallite size obtained was found to be between 95 and 83 nm which was beneficial in high intensity recording peak. Both crystal quality and crystallite sizes decrease with increasing Cr concentration. The crystal and grain sizes of the all film were investigated using SEM analysis. The surface morphology that is grain size changes with increase Cr concentration and small grains coalesce together to form larger grains for the Cr{sub 11.88}ZnO and Cr{sub 15.96}ZnO samples. Impedance spectroscopy studies were carried out in the frequencies ranging from 5 Hz to 13 MHz at room temperature. The undoped ZnO film had the highest dielectric value, while dielectric values of other films decreased as doping concentrations increased. Besides, the dielectric constants decreased whereas the loss tangents increased with increasing Cr content. This was considered to be related to the reduction of grain size as Cr content in ZnO

  10. Magnetic and optical properties of manganese doped ZnO nanoparticles synthesized by sol-gel technique

    KAUST Repository

    Omri, Karim; El Ghoul, Jaber; Lemine, O. M.; Bououdina, M.; Zhang, Bei; El Mir, Lassaad

    2013-01-01

    Mn doped ZnO nanoparticles with different doping concentration (1, 2, 3, 4, 5 at.%) were prepared by sol-gel method using supercritical drying conditions of ethyl alcohol. The structural, morphological, optical and magnetic properties of the as-prepared nanoparticles were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV measurements and superconducting quantum interference device (SQUID). The structural properties showed that the undoped and Mn doped ZnO nanoparticles exhibit hexagonal wurtzite structure. From the optical studies, the transmittance in UV region was decreased with the increase of Mn concentration. For Mn doped ZnO nanoparticles the optical band gap varies between 3.34 eV and 3.22 eV. It was found that the doping Mn 2+ ions have a significant influence on the optical properties. The magnetic characterization of the samples with 1% and 5% Mn concentrations reveal diamagnetic behavior for the first one and the presence of both paramagnetic and ferromagnetic behavior for the second. The room ferromagnetic component is due to the presence of the secondary phase ZnOMn3 which is confirmed by XRD study. © 2013 Elsevier Ltd. All rights reserved.

  11. Magnetic and optical properties of manganese doped ZnO nanoparticles synthesized by sol-gel technique

    KAUST Repository

    Omri, Karim

    2013-08-01

    Mn doped ZnO nanoparticles with different doping concentration (1, 2, 3, 4, 5 at.%) were prepared by sol-gel method using supercritical drying conditions of ethyl alcohol. The structural, morphological, optical and magnetic properties of the as-prepared nanoparticles were investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), UV measurements and superconducting quantum interference device (SQUID). The structural properties showed that the undoped and Mn doped ZnO nanoparticles exhibit hexagonal wurtzite structure. From the optical studies, the transmittance in UV region was decreased with the increase of Mn concentration. For Mn doped ZnO nanoparticles the optical band gap varies between 3.34 eV and 3.22 eV. It was found that the doping Mn 2+ ions have a significant influence on the optical properties. The magnetic characterization of the samples with 1% and 5% Mn concentrations reveal diamagnetic behavior for the first one and the presence of both paramagnetic and ferromagnetic behavior for the second. The room ferromagnetic component is due to the presence of the secondary phase ZnOMn3 which is confirmed by XRD study. © 2013 Elsevier Ltd. All rights reserved.

  12. Investigation on structural and electrical properties of Fe doped ZnO nanoparticles synthesized by solution combustion method

    International Nuclear Information System (INIS)

    Ram, Mast; Bala, Kanchan; Sharma, Hakikat; Kumar, Arun; Negi, N. S.

    2016-01-01

    In the present study, nanoparticles of Fe doped zinc oxide (ZnO) [Zn_1_-_xFe_xO where x=0.0, 0.01, 0.02, 0.03 and 0.05] were prepared by cost effective solution combustion method. The powder X-ray diffractometry confirms the formation of single phase wurtzite structure. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to investigate the micrsostructure of Fe-doped ZnO nanoparticles. The DC electrical conductivity was found to increase with temperature and measurement was carried out in the temperature range of 300-473K. DC electrical conductivity increases with temperature and decreases with Fe doping concentration.

  13. Fabrication of Al doped ZnO films using atmospheric pressure cold plasma

    International Nuclear Information System (INIS)

    Suzaki, Yoshifumi; Miyagawa, Hayato; Yamaguchi, Kenzo; Kim, Yoon-Kee

    2012-01-01

    Under atmospheric pressure, homogeneous non-equilibrium cold plasma was generated stably by high voltage pulsed power (1 kV, 20 kHz, 38 W) excitation of a mixture of He and O 2 gases produced by a dielectric barrier discharge setup. By feeding Bis (2 methoxy‐6-methyl‐3, 5-heptanedione) Zn (Zn-MOPD, C 18 H 3 O 6 Zn) and Tris (2-methoxy‐6‐methy l‐3, 5-heptanedione) Al (Al-MOPD, C 27 H 45 O 9 Al) into this plasma with He carrier gas, transparent flat Al-doped ZnO (ZnO:Al) films about 120–240 nm thick were prepared on glass substrates directly under the slit made into the cathode. Deposition rates of the films were about 20–40 nm/min. The concentration of Al was measured by inductively coupled plasma atomic emission spectroscopy. The composition ratio of Al to Zn was 7.8 mol% when the carrier He gas flow rate of Al-MOPD was 30 cm 3 . The average transmittance of all films was more than 85% in the wavelength range from 400 to 800 nm. When the composition ratio of Al/Zn was between 1.1 and 7.8 mol%, the optical band gap of the film increased from 3.28 to 3.40 eV. The resistivity of ZnO:Al film was 2.96 Ω cm at 1.3 mol% of Al/Zn. In addition, the microstructure of the films was studied by X-ray diffraction measurement and field emission scanning electron microscope observation. It was revealed that doped Al is substituted onto the Zn site of the ZnO crystalline structure in ZnO:Al films. - Highlights: ► An atmospheric pressure cold plasma generator generated stable glow discharge. ► We fabricated Al doped ZnO films on glass substrates using cold plasma. ► Al concentration measured by inductively coupled plasma atomic emission spectroscopy. ► The transmission spectrum and the resistivity of the films were measured. ► The microstructure of the films was studied.

  14. Emission properties of Mn doped ZnO nanoparticles prepared by mechanochemical processing

    Energy Technology Data Exchange (ETDEWEB)

    Sabri, Nurul Syahidah; Yahya, Ahmad Kamal [Faculty of Applied Sciences, Universiti Teknologi MARA, Shah Alam, Selangor 40450 (Malaysia); Talari, Mahesh Kumar, E-mail: talari@gmail.com [Faculty of Applied Sciences, Universiti Teknologi MARA, Shah Alam, Selangor 40450 (Malaysia)

    2012-07-15

    Mechanochemical processing was reported to introduce lot of crystal defects which can significantly influence emission properties. Nevertheless, to the best of our knowledge, there are no reports on effect of mechanochemical processing on emission properties of transition metal ion doped ZnO. In this study, Zn{sub 1-x}Mn{sub x}O nanoparticles with different Mn content (x=0, 0.02, 0.04, 0.06, 0.08, and 0.1) were prepared by mechanochemical processing to study the effect of Mn doping and processing on emission properties. Confirmation of nanoparticles size and nanocrystalline nature of hexagonal wurtzite ZnO structure is carried out using transmission electron microscopy (TEM) and selected area electron diffraction (SAED), respectively. The samples were also characterized using Fluorescence Spectroscope before and after heat-treatment. The emission studies revealed that blue emission intensity is stronger compared to UV and green emission in contrast to the earlier reports, where other synthesis routes were employed for the ZnO nanoparticles' preparation. The blue emission originates from the zinc interstitial (Zn{sub i}) and oxygen interstitial (O{sub i}) defects, which indicate that the mechanochemical route resulted in more interstitial defects compared to oxygen substitution (O{sub Zn}) and oxygen vacancy (V{sub o}) defects which otherwise would give green emission. Mn doping resulted in shifting of near-band-edge (NBE) emission and the reduction in the intensities of NBE, blue and green emissions. The initial red shift at lower Mn content could be due to s-d and p-d exchange interactions as well as band tailing effect where as the blue shift at higher Mn content can be attributed to the Burstein-Moss shift. The reduction in emission intensity could be due to non-radiative recombination processes promoted by Mn ions with increasing Mn content. - Highlights: Black-Right-Pointing-Pointer Zn{sub 1-x}Mn{sub x}O nanoparticles were prepared by mechanochemical

  15. Effect of nickel doping on the photocatalytic activity of ZnO thin films under UV and visible light

    International Nuclear Information System (INIS)

    Kaneva, Nina V.; Dimitrov, Dimitre T.; Dushkin, Ceco D.

    2011-01-01

    Nanostructured ZnO thin films with different concentrations of Ni 2+ doping (0, 1, 5, 10 and 15 wt.%) are prepared by the sol-gel method for the first time. The thin films are prepared from zinc acetate, 2-methoxyethanol and monoethanolamine on glass substrates by using dip coating method. The films comprise of ZnO nanocrystallites with hexagonal crystal structure, as revealed by X-ray diffraction. The film surface is with characteristic ganglia-like structure as observed by Scanning Electron Microscopy. Furthermore, the Ni-doped films are tested with respect to the photocatalysis in aqueous solutions of malachite green upon UV-light illumination, visible light and in darkness. The initial concentration of malachite green and the amount of catalyst are varied during the experiments. It is found that increasing of the amount of Ni 2+ ions with respect to ZnO generally lowers the photocatalytic activity in comparison with the pure ZnO films. Nevertheless, all films exhibit a substantial activity under both, UV and visible light and in darkness as well, which is promising for the development of new ZnO photocatalysts by the sol-gel method.

  16. Influence of Fe-doping on the structural, optical and magnetic properties of ZnO nanoparticles

    International Nuclear Information System (INIS)

    Liu Changzhen; Meng Dawei; Pang Haixia; Wu Xiuling; Xie Jing; Yu Xiaohong; Chen Long; Liu Xiaoyang

    2012-01-01

    Zn 1–x Fe x O (x=0–0.05) nanoparticles were synthesized without a catalyst by a two-step method. Fe was doped into ZnO by a source of metallic Fe sheets in a solid–liquid system at 80 °C, and the Zn 1−x Fe x O nanoparticles were obtained by annealing at 300 °C. X-ray diffraction, X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy were used to characterize the structural properties of the as-grown Zn 1−x Fe x O. The optical properties were determined by Infrared and Ultraviolet–visible spectroscopy. The results confirm that the crystallinity of the ZnO is deteriorated due to Fe-doping. XPS results show that there is a mixture of Fe 0+ and the Fe 3+ in the representative Zn 0.95 Fe 0.05 O sample. The optical band gap of Zn 1−x Fe x O is enhanced with increasing of Fe-doping. Room temperature ferromagnetism was observed in all the Fe-doped ZnO samples. - Highlights: ► Zn 1−x Fe x O nanoparticles were synthesized with a simple two-step method. ► The Zn 1−x Fe x O predecessors were synthesized at a low temperature. ► Fe element was readily doped from the source of metallic Fe sheet. ► All the Fe doping ZnO samples have room temperature ferromagnetism. ► The structural and properties of the Zn 1−x Fe x O are regular with different x.

  17. Characterization of a new transparent-conducting material of ZnO doped ITO thin films

    Science.gov (United States)

    Ali, H. M.

    2005-11-01

    Thin films of indium tin oxide (ITO) doped with zinc oxide have the remarkable properties of being conductive yet still highly transparent in the visible and near-IR spectral ranges. The Electron beam deposi- tion technique is one of the simplest and least expensive ways of preparing. High-quality ITO thin films have been deposited on glass substrates by Electron beam evaporation technique. The effect of doping and substrate deposition temperature was found to have a significant effect on the structure, electrical and optical properties of ZnO doped ITO films. The average optical transmittance has been increased with in- creasing the substrate temperature. The maximum value of transmittance is greater than 84% in the visible region and 85% in the NIR region obtained for film with Zn/ITO = 0.13 at substrate temperature 200 °C. The dielectric constant, average excitation energy for electronic transitions (E o), the dispersion energy (E d), the long wavelength refractive index (n ), average oscillator wave length ( o) and oscillator strength S o for the thin films were determined and presented in this work.

  18. Optical and Magnetic Properties of Fe Doped ZnO Nanoparticles Obtained by Hydrothermal Synthesis

    Directory of Open Access Journals (Sweden)

    Xiaojuan Wu

    2014-01-01

    Full Text Available Diluted magnetic semiconductors Zn1-xFexO nanoparticles with different doping concentration (x=0, 0.01, 0.05, 0.10, and 0.20 were successfully synthesized by hydrothermal method. The crystal structure, morphology, and optical and magnetic properties of the samples were characterized by X-ray diffraction (XRD, energy dispersive spectrometer (EDS, high-resolution transmission electron microscopy (HRTEM, Raman scattering spectra (Raman, photoluminescence spectra (PL, and the vibrating sample magnetometer (VSM. The experiment results show that all samples synthesized by this method possess hexagonal wurtzite crystal structure with good crystallization, no other impurity phases are observed, and the morphology of the sample shows the presence of ellipsoidal nanoparticles. All the Fe3+ successfully substituted for the lattice site of Zn2+ and generates single-phase Zn1-xFexO. Raman spectra shows that the peak shifts to higher frequency. PL spectra exhibit a slight blue shift and the UV emission is annihilated with the increase of Fe3+ concentration. Magnetic measurements indicated that Fe-doped ZnO samples exhibit ferromagnetic behavior at room temperature and the saturation magnetization is enhanced with the increase of iron doping content.

  19. Magnetic properties of Mn-doped ZnO diluted magnetic semiconductors

    International Nuclear Information System (INIS)

    Liu Xuechao; Zhang Huawei; Zhang Tao; Chen Boyuan; Chen Zhizhan; Song Lixin; Shi Erwei

    2008-01-01

    A series of Mn-doped ZnO films have been prepared in different sputtering plasmas by using the inductively coupled plasma enhanced physical vapour deposition. The films show paramagnetic behaviour when they are deposited in an argon plasma. The Hall measurement indicates that ferromagnetism cannot be realized by increasing the electron concentration. However, the room-temperature ferromagnetism is obtained when the films are deposited in a mixed argon-nitrogen plasma. The first-principles calculations reveal that antiferromagnetic ordering is favoured in the case of the substitution of Mn 2+ for Zn 2+ without additional acceptor doping. The substitution of N for O (N O −) is necessary to induce ferromagnetic couplings in the Zn-Mn-O system. The hybridization between N 2p and Mn 3d provides an empty orbit around the Fermi level. The hopping of Mn 3d electrons through the empty orbit can induce the ferromagnetic coupling. The ferromagnetism in the N-doped Zn-Mn-O system possibly originates from the charge transfer between Mn 2+ and Mn 3+ via N O − . The key factor is the empty orbit provided by substituting N for O, rather than the conductivity type or the carrier concentration

  20. Efficient photocatalytic performance enhancement in Co-doped ZnO nanowires coupled with CuS nanoparticles

    Science.gov (United States)

    Li, Wei; Wang, Guojing; Feng, Yimeng; Li, Zhengcao

    2018-01-01

    In this research, a kind of highly efficient semiconductor photocatalyst was fabricated by depositing CuS nanoparticles uniformly on the surface of Co-doped ZnO nanowires. ZnO nanowires were synthesized by hydrothermal method and CuS nanoparticles were modified by successive ionic layer adsorption and reaction (SILAR). By conducting methyl orange (MO) degradation experiments under the illumination of visible light, the photocatalytic activity of Co-doped ZnO nanowires modified with CuS nanoparticles was found to be nearly three times active when compared to bare ZnO nanowires. Its superior photocatalytic performance has two main reasons. The doped Co2+ ions can inhibit the recombination of photo-generated electron-hole pairs and decrease the optical bandgap, while the p-n heterostructure can enhance the visible light absorption ability and promote the separation of photo-excited charge carriers. Furthermore, the effect of the amount of deposited CuS nanoparticles on the photocatalysis was also investigated. The photocatalytic efficiency firstly raised along with the increment of SILAR cycle times and reached a maximum at 10 cycles but then decreased as the cycle times continue to increase. This originates from that an excessive amount of CuS would not only cover the active reacting sites, but also serve as recombination centers. Overall, this new nanostructure is expected to work as an efficient photocatalyst.

  1. Magnetic and optical properties of Mn-doped ZnO vertically aligned nanorods synthesized by hydrothermal technique

    Energy Technology Data Exchange (ETDEWEB)

    Panda, J.; Sasmal, I.; Nath, T. K., E-mail: tnath@phy.iitkgp.ernet.in, E-mail: tapnath@gmail.com [Department of Physics, Indian Institute Technology Kharagpur, West Bengal, 721302 (India)

    2016-03-15

    In this paper we have reported the synthesis of high quality vertically aligned undoped and Mn-doped ZnO single crystalline nanorods arrays on Si (100) substrates using two steps process, namely, initial slow seed layer formation followed by solution growth employing wet chemical hydrothermal method. The shapes of the as grown single crystalline nanorods are hexagonal. The diameter and length of the as grown undoped ZnO nanorods varies in the range of 80-150 nm and 1.0 - 1.4 μm, respectively. Along with the lattice parameters of the hexagonal crystal structure, the diameter and length of Mn doped ZnO nanorods are found to increase slightly as compared to the undoped ZnO nanorods. The X-ray photoelectron spectroscopy confirms the presence of Mn atoms in Mn{sup 2+} state in the single crystalline ZnO nanorods. The recorded photoluminescence spectrum contains two emissions peaks having UV exciton emissions along with a green-yellow emission. The green-yellow emissions provide the evidence of singly ionized oxygen vacancies. The magnetic field dependent magnetization measurements [M (H)] and zero field cooled (ZFC) and field cooled (FC) magnetization [M(T)] measurements have been carried out at different isothermal conditions in the temperature range of 5-300 K. The Mn doped ZnO nanorods clearly show room temperature ferromagnetic ordering near room temperature down to 5 K. The observed magnetization may be attributed to the long range ferromagnetic interaction between bound magnetic polarons led by singly charged oxygen vacancies.

  2. Sustainable synthesis of metals-doped ZnO nanoparticles from zinc-bearing dust for photodegradation of phenol

    International Nuclear Information System (INIS)

    Wu, Zhao-Jin; Huang, Wei; Cui, Ke-Ke; Gao, Zhi-Fang; Wang, Ping

    2014-01-01

    Highlights: • Multi-doped ZnO (M-ZnO) was prepared from Zn-bearing dust for waste-cleaning-waste. • All the dopants M (Fe, Mg, Ca and Al) and Zn are recovered from the dust. • Doping by the dust-derived M expands excitability of ZnO to visible light region. • M-ZnO has good catalytic activity in the degradation of phenol under visible light. - Abstract: A novel strategy of waste-cleaning-waste is proposed in the present work. A metals-doped ZnO (M-ZnO, M = Fe, Mg, Ca and Al) nanomaterial has been prepared from a metallurgical zinc-containing solid waste “fabric filter dust” by combining sulfolysis and co-precipitation processes, and is found to be a favorable photocatalyst for photodegradation of organic substances in wastewater under visible light irradiation. All the zinc and dopants (Fe, Mg, Ca and Al) for preparing M-ZnO are recovered from the fabric filter dust, without any addition of chemical as elemental source. The dust-derived M-ZnO samples deliver single phase indexed as the hexagonal ZnO crystal, with controllable dopants species. The photocatalytic activity of the dust-derived M-ZnO samples is characterized by photodegradation of phenol aqueous solution under visible light irradiation, giving more prominent photocatalytic behaviors than undoped ZnO. Such enhancements may be attributed to incorporation of the dust-derived metal elements (Fe, Mg, Ca and Al) into ZnO structure, which lead to the modification of band gap and refinement of grain size. The results show a feasibility to utilize the industrial waste as a resource of photodegradating organic substances in wastewater treatments

  3. Title: Using Alignment and 2D Network Simulations to Study Charge Transport Through Doped ZnO Nanowire Thin Film Electrodes

    KAUST Repository

    Phadke, Sujay; Lee, Jung-Yong; West, Jack; Peumans, Peter; Salleo, Alberto

    2011-01-01

    of magnitude lower than the single nanowire resistance. Simulations suggest that the conductivity of such thin film devices could be further enhanced by using longer nanowires. Solution processed Gallium doped ZnO nanowires are aligned on substrates using

  4. Structure and Properties of Al and Ga- Doped ZnO

    Science.gov (United States)

    Temizer, Namik Kemal

    Recently there is tremendous interest in Transparent conducting oxide (TCO) research due to the unlimited and exciting application areas. Current research is mostly focused on finding alternative low cost and sustainable materials in order to replace indium tin oxide (ITO), which caused serious concern due to the increasing cost of indium and chemical stability issues of ITO. The primary aim of this research is to develop alternative TCO materials with superior properties in order to increase the efficiency in optoelectronic applications, as well as to study the properties of these materials to fully characterize them. We have grown Al and Ga-doped ZnO films with an optimized composition under different deposition conditions in order to understand the effect of processing parameters on the film properties. We report a detailed investigation on the structure-property correlations in Ga and Al codoped ZnO films on c-sapphire substrates where the thin film microstructure varies from nanocrystalline to single crystal. We have achieved highly epitaxial films with very high optical transmittance (close to 90%) and low resistivity (˜110muO-cm) values. The films grown in an ambient oxygen partial pressure (PO2 ) of 50 mTorr and at growth temperatures from room temperature to 600°C showed semiconducting behavior, whereas samples grown at a Po2 of 1 mTorr showed metallic nature. The most striking feature is the occurrence of resistivity minima at relatively high temperatures around 110 K in films deposited at high temperatures. The structure-property correlations reveal that point defects play an important role in modifying the structural, optical, electrical and magnetic properties and such changes in physical properties are controlled predominantly by the defect content. To gain a better understanding of the conduction processes in doped ZnO thin films, we have studied the temperature variation of resistivity of some selected samples that showed some interesting behavior

  5. Electrodeposition of nanoporous ZnO on Al-doped ZnO leading to a highly organized structure for integration in Dye Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Renou G.

    2010-10-01

    Full Text Available In the present study, we propose an improvement of the anode configuration in Zinc Oxide based Dye Sensitized Solar Cells (DSSC. Instead of the classical configuration, which is composed by two different metal oxides: one transparent conducting oxide (TCO for the substrate and one nanostructured metal oxide for supporting the dye, the new approach is to use ZnO as unique material. Thus, nanoporous zinc oxide films have been electrodeposited on a sputtered Al doped ZnO layers with varying thicknesses up to 6 μm. The evolution of the porosity of the structure has been studied by scanning electron microscope (SEM and electrochemical impedance spectroscopy and compared with standard nanoporous ZnO grown on fluorine doped tin oxide (SnO2:F noted FTO. This results firstly in the modification of the nanoporous structure morphology and secondly a better adhesion between the nanoporous layer and the substrate. Organization in the nanoporous material is enhanced with regular pores arrays and perpendicular to the substrate. Dye sensitized solar cells based on this simplified architecture present efficiencies up to 4.2% and 4.5% with N719 and D149 respectively as sensitizers. Higher fill factor and Voc are found in comparison with the one obtained for deposition on the classical transparent conducting oxide (FTO, which denote improved electrical transfer properties.

  6. High efficiency of transmittance and electrical conductivity of V doped ZnO used in solar cells applications

    Energy Technology Data Exchange (ETDEWEB)

    Boujnah, M., E-mail: boujnah.mourad@gmail.com [Laboratory of Magnetism and Physics of High Energies, Department of Physics, B.P. 1014, Faculty of Sciences, Mohammed V University, Rabat (Morocco); Boumdyan, M. [Laboratory of Magnetism and Physics of High Energies, Department of Physics, B.P. 1014, Faculty of Sciences, Mohammed V University, Rabat (Morocco); Naji, S. [Department of Physics, Faculty of Sciences, Ibb University, Ibb (Yemen); Benyoussef, A.; El Kenz, A.; Loulidi, M. [Laboratory of Magnetism and Physics of High Energies, Department of Physics, B.P. 1014, Faculty of Sciences, Mohammed V University, Rabat (Morocco)

    2016-06-25

    The full-potential linearized augmented plane wave method (FP-LAPW) based on the density functional theory (DFT) and Boltzmann's Transport theory, are employed to investigate theoretically the electronic structure, optical and electrical properties of vanadium -doped wurtzite ZnO with different concentrations (3.125%, 6.25%, 12.5%, 25%). The FP-LAPW based on the new potential approximation known as the Tran-Blaha modified Becke–Johnson exchange potential approximation (mBJ) was also applied with the primary goal of improving the electronic structure description specially the band gap energy. The calculated band structure and density of states (DOS) exhibit a band gap of pure ZnO (3.3 eV) closer to the experimental one. As well, our results indicate that the average transmittance in the 400–1000 nm wavelength region was 93%. We found that Zn{sub 96.875}V{sub 3.125}O is the optimized composition of the V doped ZnO, which has the highest conductivity (3.2 × 10{sup 3} (Ωcm){sup −1}) and transmittance. The high transmittance and electrical conductivity indicate that hexagonal V:ZnO system is a potential as material for solar energy applications. - Highlights: • We investigate theoretically the physical properties of V-doped wurtzite ZnO. • We used density functional calculations (DFT) and Boltzmann's Transport theory. • We examined the optical and electrical properties of different percentage of V doped ZnO.

  7. Enhanced optical and electrical properties of Y-doped ZnO nanoparticles having different Y concentrations

    Science.gov (United States)

    Üzar, Neslihan

    2018-04-01

    In this study, undoped ZnO and yttrium (Y)-doped ZnO (YZO) nanoparticles having different Y dopant concentrations (Zn1- x Y x O; x = 0.005, 0.01, 0.015, 0.02) were successfully synthesized by sol-gel dip-coating method. Structural characterizations of the obtained samples were examined with scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD) analyses. SEM analysis shows that the synthesized nanoparticles are mostly dot-like structures. The sizes of nanostructures decrease with increasing Y-doping concentration up to 2 mol % Y and XRD results show that all of samples have wurtzite hexagonal structure of ZnO with (002) c-plane orientation. According to EDS results pure YZO samples are obtained. Optical transmittances of all samples were investigated in the range of 350-750 nm at room temperature. The average optical transmittances of YZO samples in the visible region are approximately over 90%, but the transmittance starts to decrease for Zn0.98Y0.02O sample. Also, it was observed that the optical transmittances of Y-doped samples are higher than that of undoped ZnO. The electrical properties of YZO samples were obtained by resistance measurements at room temperature. The resistivity of samples was found to be 2.25 × 10-3, 1.43 × 10-3, 7.8 × 10-3, and 1.3 × 10-3 Ω-cm for Zn0.995Y0.005O, Zn0.99Y0.01O, Zn0.985Y0.015O and Zn0.98Y0.02O, respectively. All these results show that surface, structural, electrical and optical properties of ZnO samples can be improved with doping Y up to 2 mol % concentrations.

  8. Optical and structural properties of Mn-doped ZnO nanorods grown by aqueous chemical growth for spintronic applications

    Energy Technology Data Exchange (ETDEWEB)

    Strelchuk, V.V. [V. Lashkaryov Institute of Semiconductor Physics, National Academy of Sciences of Ukraine, 45 Nauky pr., 03028 Kyiv (Ukraine); Nikolenko, A.S., E-mail: nikolenko_mail@ukr.net [V. Lashkaryov Institute of Semiconductor Physics, National Academy of Sciences of Ukraine, 45 Nauky pr., 03028 Kyiv (Ukraine); Kolomys, O.F.; Rarata, S.V.; Avramenko, K.A.; Lytvyn, P.M. [V. Lashkaryov Institute of Semiconductor Physics, National Academy of Sciences of Ukraine, 45 Nauky pr., 03028 Kyiv (Ukraine); Tronc, P. [Centre National de la Recherche Scientifique, Ecole Superieure de Physique et de Chimie Industrielles de la Ville de Paris, 10 rue Vauquelin, 75005 Paris (France); Chey, Chan Oeurn; Nur, Omer; Willander, Magnus [Department of Science and Technology, Linköping University, 601 74 Norrköping (Sweden)

    2016-02-29

    The effect of Mn-doping on the structural, morphological, optical and magnetic properties of the ZnO:Mn nanorods (NRs) synthesized by aqueous chemical process is reported. Grown ZnO:Mn NRs are shown to have hexagonal end facets and the diameters increasing with nominal Mn content. Optical absorption measurements show a decrease in optical band gap with increase of Mn concentration. Raman spectroscopy revealed significant modification of the lattice vibrational properties of the ZnO matrix upon Mn doping. The additional Mn-related vibrational mode, intensity of which increases with amount of Mn can be regarded as an evidence of Mn incorporation into the host lattice of the ZnO. At high Mn concentrations, coexistence of hexagonal Zn{sub 1−x}Mn{sub x}O phase along with the secondary phases of ZnMn{sub 2}O{sub 4} cubic spinel is revealed. Magnetic properties of ZnO:Mn NRs are studied by combinatorial atomic force microscopy and magnetic force microscopy imaging, and obtained clear magnetic contrast at room temperature provides a strong evidence of ferromagnetic behavior. - Highlights: • Synthesis of Mn-doped ZnO nanorods by hydrothermal method is demonstrated. • Doping with Mn significantly changes the morphology of ZnO nanorods. • Additional Mn-induced Raman modes evidence incorporation of Mn into ZnO matrix. • Formation of secondary ZnMn{sub 2}O{sub 4} spinel phase is found at high Mn concentrations. • Contrast MFM images of ZnO:Mn nanorods indicate ferromagnetism at room temperature.

  9. Improved damp heat stability of Ga-Doped ZnO thin film by pretreatment of the polyethylene terephthalate substrate

    Science.gov (United States)

    Kim, B. B.; Seo, S. G.; Lim, Y. S.; Choi, H.-S.; Seo, W.-S.; Park, H.-H.

    2013-09-01

    A study on the damp heat stability of transparent conducting ZnO thin film grown on a polyethylene terephthalate substrate (PET) is reported. By thermal annealing of the PET substrate at 100°C with Ar flow in a vacuum chamber prior to the sputtering growth of Ga-doped ZnO (GZO) thin film, significantly enhanced damp heat stability was achieved at 60°C with a 90% relative humidity. Electrical and structural characterizations of the GZO thin films were carried out and the effects of the pretreatment on the improved damp heat stability are discussed.

  10. Soft x-ray absorption spectroscopy on Co doped ZnO: structural distortions and electronic structure

    International Nuclear Information System (INIS)

    Kowalik, I A; Guziewicz, E; Godlewski, M; Arvanitis, D

    2016-01-01

    We present soft x-ray absorption spectra from a series of Co doped ZnO films. We discuss systematic variations of the Co L-edge white line intensity and multiplet features for this series of samples. We document sizeable differences in the electronic state of the Co ionic cores, as well as in the local environment of the host lattice atoms, characterised by means of x-ray absorption spectra at the O K-edge and Zn L-edges. Model calculations allow to correlate the observed effects to small structural distortions of the ZnO lattice. (paper)

  11. Mechanical properties of Al2O3-doped (2 wt.%) ZnO films

    International Nuclear Information System (INIS)

    Kuriki, Shina; Kawashima, Toshitaka

    2007-01-01

    We report a new method of evaluating the adhesion of Al 2 O 3 -doped (2 wt.%) ZnO (AZO) thin films. The AZO films were deposited by DC reactive magnetron sputtering on plastic film (PET: polyethyleneterephthalate) at various sputtering pressures, power, and reactive gas-flow ratios. The adhesion test of the films was carried out using the nanoindentation system. The fracture point as determined by the load-displacement curve occurred at the time of separation between the thin film and the substrate. The integration value of load and displacement to the fracture point is defined as the degree of adhesion (S W ). The AZO films showed that adhesion increase as sputtering power increases and sputtering pressure decreases

  12. Synthesis of Cu Doped ZnO Nanostructures for Ultra Violet Sensing

    Directory of Open Access Journals (Sweden)

    Nazar Abbas SHAH

    2015-03-01

    Full Text Available This paper mainly focused on the synthesis of zinc oxide nanostructures, their characterization and their ultra violet light sensing response at room temperature. Nanowires, nanobelts and nanosheets were synthesized by varying doping material copper by using vapor transport technique governed by the vapor-liquid-solid or vapor-solid mechanisms. The structural, morphological and optical characterization was carried out using X-ray diffraction, scanning electron microscopy, energy dispersive X-Ray and ultra violet visible spectroscopy techniques. Finally the ultra violet light sensing response of these nanostructures was observed by using Keithley meter. The high ultra violet photosensitivity and fast response time justifies the effective utilization of these ZnO nanostructures as ultra violet sensors in different areas.

  13. Nonenzymetic glucose sensing using carbon functionalized carbon doped ZnO nanorod arrays

    Science.gov (United States)

    Chakraborty, Pinak; Majumder, Tanmoy; Dhar, Saurab; Mondal, Suvra Prakash

    2018-04-01

    Fabrication of highly sensitive, long stability and low cost glucose sensors are attractive for biomedical applications and food industries. Most of the commercial glucose sensors are based on enzymatic detection which suffers from problems underlying in enzyme activities. Development of high sensitive, enzyme free sensors is a great challenge for next generation glucose sensing applications. In our study Zinc oxide nanorod sensing electrodes have been grown using low cost hydrothermal route and their nonenzymatic glucose sensing properties have been demonstrated with carbon functionalized, carbon doped ZnO nanorods (C-ZnO NRs) in neutral medium (0.1M PBS, pH 7.4) using cyclic voltammetry and amperometry measurements. The C-ZnO NRs electrodes demonstrated glucose sensitivity˜ 13.66 µAmM-1cm-2 in the concentration range 0.7 - 14 mM.

  14. Magnetoresistance manipulation and sign reversal in Mn-doped ZnO nanowires.

    Science.gov (United States)

    Sapkota, Keshab R; Chen, Weimin; Maloney, F Scott; Poudyal, Uma; Wang, Wenyong

    2016-10-14

    We report magnetoresistance (MR) manipulation and sign reversal induced by carrier concentration modulation in Mn-doped ZnO nanowires. At low temperatures positive magnetoresistance was initially observed. When the carrier concentration was increased through the application of a gate voltage, the magnetoresistance also increased and reached a maximum value. However, further increasing the carrier concentration caused the MR to decrease, and eventually an MR sign reversal from positive to negative was observed. An MR change from a maximum positive value of 25% to a minimum negative value of 7% was observed at 5 K and 50 KOe. The observed MR behavior was modeled by considering combined effects of quantum correction to carrier conductivity and bound magnetic polarons. This work could provide important insights into the mechanisms that govern magnetotransport in dilute magnetic oxides, and it also demonstrated an effective approach to manipulating magnetoresistance in these materials that have important spintronic applications.

  15. Local fields in Co and Mn Co-doped ZnO

    Energy Technology Data Exchange (ETDEWEB)

    Sato, W., E-mail: wsato@se.kanazawa-u.ac.jp [Kanazawa University, Institute of Science and Engineering (Japan); Kano, Y.; Suzuki, T.; Nakagawa, M. [Kanazawa University, Graduate School of Natural Science and Technology (Japan); Kobayashi, Y. [The University of Electro-Communications, Department of Engineering Science (Japan)

    2016-12-15

    The magnetic properties of ZnO co-doped with 5 at. % Co and 5 at. % Mn(Zn{sub 0.90}Co{sub 0.05}Mn{sub 0.05}O) synthesized by a solid-state reaction were investigated by means of {sup 57}Co emission Mössbauer spectroscopy. The majority of the probe ions (80 %) residing in defect-free substitutional Zn sites take the oxidation state of {sup 57}Fe {sup 2+}, and the others presumably form local defects taking the state of {sup 57}Fe {sup 3+} at room temperature. Both components show doublets, and RT ferromagnetism was thus absent in the sample. For the measurement at 10 K, spectral broadening was observed, implying a possible presence of a weak magnetic component.

  16. Influences of Co doping on the structural and optical properties of ZnO nanostructured

    Science.gov (United States)

    Majeed Khan, M. A.; Wasi Khan, M.; Alhoshan, Mansour; Alsalhi, M. S.; Aldwayyan, A. S.

    2010-07-01

    Pure and Co-doped ZnO nanostructured samples have been synthesized by a chemical route. We have studied the structural and optical properties of the samples by using X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM), field-emission transmission electron microscope (FETEM), energy-dispersive X-ray (EDX) analysis and UV-VIS spectroscopy. The XRD patterns show that all the samples are hexagonal wurtzite structures. Changes in crystallite size due to mechanical activation were also determined from X-ray measurements. These results were correlated with changes in particle size followed by SEM and TEM. The average crystallite sizes obtained from XRD were between 20 to 25 nm. The TEM images showed the average particle size of undoped ZnO nanostructure was about 20 nm whereas the smallest average grain size at 3% Co was about 15 nm. Optical parameters such as absorption coefficient ( α), energy band gap ( E g ), the refractive index ( n), and dielectric constants ( σ) have been determined using different methods.

  17. Intrinsic and spatially nonuniform ferromagnetism in Co-doped ZnO films

    Science.gov (United States)

    Tseng, L. T.; Suter, A.; Wang, Y. R.; Xiang, F. X.; Bian, P.; Ding, X.; Tseng, A.; Hu, H. L.; Fan, H. M.; Zheng, R. K.; Wang, X. L.; Salman, Z.; Prokscha, T.; Suzuki, K.; Liu, R.; Li, S.; Morenzoni, E.; Yi, J. B.

    2017-09-01

    Co doped ZnO films have been deposited by a laser-molecular beam epitaxy system. X-ray diffraction and UV spectra analysis show that Co effectively substitutes the Zn site. Transmission electron microscopy (TEM) and secondary ion mass spectroscopy analysis indicate that there are no clusters. Co dopants are uniformly distributed in ZnO film. Ferromagnetic ordering is observed in all samples deposited under an oxygen partial pressure, PO2=10-3 , 10-5, and 10-7 torr, respectively. However, the magnetization of PO2=10-3 and 10-5 is very small at room temperature. At low temperature, the ferromagnetic ordering is enhanced. Muon spin relaxation (μ SR ) measurements confirm the ferromagnetism in all samples, and the results are consistent with magnetization measurements. From μ SR and TEM analysis, the film deposited under PO2=10-7 torr shows intrinsic ferromagnetism. However, the volume fraction of the ferromagnetism phase is approximately 70%, suggesting that the ferromagnetism is not carrier mediated. Resistivity versus temperature measurements indicate Efros variable range hopping dominates the conductivity. From the above results, we can confirm that a bound magnetic polaron is the origin of the ferromagnetism.

  18. Transparent conductive Ga-doped ZnO films fabricated by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Behrends, Arne; Wagner, Alexander; Al-Suleiman, Mohamed Aid Mansur; Waag, Andreas; Bakin, Andrey [Institute of Semiconductor Technology, University of Technology Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany); Lugauer, Hans-Juergen; Strassburg, Martin; Walter, Robert; Weimar, Andreas [OSRAM Opto Semiconductors GmbH, Leibnizstr. 4, 93055 Regensburg (Germany)

    2012-04-15

    Transparent conductive oxides (TCOs) are used for a variety of different applications, e.g., in solar cells and light emitting diodes (LEDs). Mostly, sputtering is used, which often results in a degradation of the underlying semiconductor material. In this work we report on a ''soft'' method for the fabrication of ZnO films as TCO layers by using metal organic chemical vapor deposition (MOCVD) at particularly low temperatures. The MOCVD approach has been studied focusing on the TCO key issues: fabrication temperature, morphology, optical, and electrical properties. Very smooth ZnO films with rms values down to 0.8 nm were fabricated at a substrate temperature of only 300 C. Ga-doping is well controllable even for high carrier concentrations up to 2 x 10{sup 20} cm{sup -3}, which is above the Mott-density leading to metallic-like behavior of the films. Furthermore all films show excellent optical transparency in the visible spectral range. As a consequence, our MOCVD approach is well suited for the soft fabrication of ZnO-based TCO layers. (Copyright copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  19. Influence of Tb doping on the luminescence characteristics of ZnO nanoparticles

    International Nuclear Information System (INIS)

    Sharma, A.; Dhar, S.; Singh, B. P.; Kundu, T.; Spasova, M.; Farle, M.

    2012-01-01

    Structural and optical properties of the Tb-doped ZnO nanoparticles with average diameter ≈4 nm have been systematically investigated. Our X-ray diffraction studies show a contraction of the ZnO lattice with the increase of the Tb mole-fraction x for x ≤ 0.02 and an expansion beyond x ≈ 0.02. The photoluminescence spectra are found to be comprised of a near band edge ultra violet luminescence (UVL) and a broad green luminescence (GL) band. Under the atmospheric condition, the intensity of the GL band is found to increase with the Tb mole-fraction over the entire doping range. On the other hand, under the vacuum condition, it has been observed that the GL intensity decreases with the increase of x up to x ≈ 0.02 but further increase of x leads to a gradual revival of the GL emission. Our study suggests that for x ≤ 0.02, GL results due to the physisorption of certain groups on the surface of the nanoparticles (GL-groups). It is also found that in this Tb mole-fraction regime, Tb incorporates mostly on the surface of the nanoparticles and affects the UVL to GL intensity ratio by influencing the attachment of the GL-groups. However, for x > 0.02, GL originates not only from the GL-groups but also from certain point defects, which are likely to be generated due to the incorporation of Tb in the core of the nanoparticles. A simple rate equation model is introduced to get a quantitative understanding about the variation of the density of the centers responsible for the GL emission as a function of x under the atmospheric and the vacuum conditions.

  20. Cobalt and sulfur co-doped nano-size TiO2 for photodegradation of various dyes and phenol

    KAUST Repository

    Siddiqa, Asima

    2015-11-01

    Various compositions of cobalt and sulfur co-doped titania nano-photocatalyst are synthesized via sol–gel method. A number of techniques including X-ray diffraction (XRD), ultraviolet–visible (UV–Vis), Rutherford backscattering spectrometry (RBS), thermal gravimetric analysis (TGA), Raman, N2 sorption, electron microscopy are used to examine composition, crystalline phase, morphology, distribution of dopants, surface area and optical properties of synthesized materials. The synthesized materials consisted of quasispherical nanoparticles of anatase phase exhibiting a high surface area and homogeneous distribution of dopants. Cobalt and sulfur co-doped titania demonstrated remarkable structural and optical properties leading to an efficient photocatalytic activity for degradation of dyes and phenol under visible light irradiations. Moreover, the effect of dye concentration, catalyst dose and pH on photodegradation behavior of environmental pollutants and recyclability of the catalyst is also examined to optimize the activity of nano-photocatalyst and gain a better understanding of the process.

  1. Cobalt and sulfur co-doped nano-size TiO2 for photodegradation of various dyes and phenol

    KAUST Repository

    Siddiqa, Asima; Masih, Dilshad; Anjum, Dalaver H.; Siddiq, Muhammad

    2015-01-01

    Various compositions of cobalt and sulfur co-doped titania nano-photocatalyst are synthesized via sol–gel method. A number of techniques including X-ray diffraction (XRD), ultraviolet–visible (UV–Vis), Rutherford backscattering spectrometry (RBS), thermal gravimetric analysis (TGA), Raman, N2 sorption, electron microscopy are used to examine composition, crystalline phase, morphology, distribution of dopants, surface area and optical properties of synthesized materials. The synthesized materials consisted of quasispherical nanoparticles of anatase phase exhibiting a high surface area and homogeneous distribution of dopants. Cobalt and sulfur co-doped titania demonstrated remarkable structural and optical properties leading to an efficient photocatalytic activity for degradation of dyes and phenol under visible light irradiations. Moreover, the effect of dye concentration, catalyst dose and pH on photodegradation behavior of environmental pollutants and recyclability of the catalyst is also examined to optimize the activity of nano-photocatalyst and gain a better understanding of the process.

  2. Enhanced room temperature ferromagnetism in Cr-doped ZnO nanoparticles prepared by auto-combustion method

    Science.gov (United States)

    Haq, Khizar-ul; Irfan, M.; Masood, Muhammad; Saleem, Murtaza; Iqbal, Tahir; Ahmad, Ishaq; Khan, M. A.; Zaffar, M.; Irfan, Muhammad

    2018-04-01

    Zn1‑x Cr x O (x = 0.00, 0.01, 0.03, 0.05, 0.07, and 0.09) nanoparticles were synthesized, by an auto-combustion method. Structural, optical, and magnetic characteristics of Cr-doped ZnO samples calcined at 600 °C have been analyzed by using X-ray diffraction (XRD), field emission scanning electron microscope (FESEM), UV–Vis spectroscopy and vibrating sample magnetometer (VSM). The XRD data confirmed the hexagonal wurtzite structure of pure and Cr-doped ZnO nanoparticles. The calculated values of grain size using Scherrer's formula are in the range of 30.7–9.2 nm. The morphology of nanopowders has been observed by FESEM, and EDS results confirmed a systematic increase of Cr content in the samples and clearly indicate with no impurity element. The band gaps, computed by UV–Vis spectroscopy, are in the range of 2.83–2.35 eV for different doping concentrations. By analyzing VSM data, significantly enhanced room temperature ferromagnetism is identified in Cr-doped ZnO samples. The value of magnetization is a 12 times increased of the value reported by Daunet al. (2010). Room temperature ferromagnetism of the nanoparticles is of vital prominence for spintronics applications. Project supported by the Office of Research, Innovation, and Commercialization (ORIC), MUST Mirpur (AJK).

  3. Theoretical study of the multiferroic properties in M-doped (M=Co, Cr, Mg) ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bahoosh, S.G. [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Apostolov, A.T. [University of Architecture, Civil Engineering and Geodesy, Faculty of Hydrotechnics, Department of Physics, 1, Hristo Smirnenski Blvd., 1046 Sofia (Bulgaria); Apostolova, I.N. [University of Forestry, Faculty of Forest Industry, 10, Kl. Ohridsky Blvd., 1756 Sofia (Bulgaria); Trimper, S. [Institute of Physics, Martin-Luther-University, D-06099 Halle (Germany); Wesselinowa, Julia M. [University of Sofia, Department of Physics, Blvd. J. Bouchier 5, 1164 Sofia (Bulgaria)

    2015-01-01

    The origin of multiferroism is still an open problem in ZnO. We propose a microscopic model to clarify the occurrence of multiferroism in this material. Using Green's function technique we study the influence of ion doping and size effects on the magnetization and polarization of ZnO thin films. The calculations for magnetic Co- and Cr-ions are based on the s–d model, the transverse Ising model in terms of pseudo-spins and a biquadratic magnetoelectric coupling, whereas in case of nonmagnetic Mg-ions the model takes into account the Coulomb interaction and an indirect coupling between the pseudo-spins via the conduction electrons. We show that the magnetization M exhibits a maximum for a fixed concentration of the doping ions. Furthermore M increases with decreasing film thickness N. The polarization increases with increasing concentration of the dopant and decreasing N. The results are in good agreement with the experimental data. - Highlights: • The paper analyzes the multiferroic properties of doped ZnO thin films by a microscopic model. • The magnetization exhibits a maximum at a fixed doping concentration. • The polarization increases with growing dopant concentration. • The ferroelectric transition temperature is enhanced for increasing dopant concentration.

  4. Structural Characterization and Magnetic Properties of Undoped and Ti-Doped ZnO Nanoparticles Prepared by Modified Oxalate Route

    Directory of Open Access Journals (Sweden)

    Ekane Peter Etape

    2018-01-01

    Full Text Available Ti-doped zinc oxide and pure zinc oxide nanoparticles were synthesized by a modified oxalate route using Averrhoa carambola fruit juice as a natural source of oxalate. The characteristics of the precursors have been investigated by FTIR, TGA, and XRD. The results from the investigation revealed that the precursors are zinc oxalate and Ti-doped zinc oxalate which readily decompose at 450°C. The as-prepared precursors were calcined at 450°C for 4 hours, and the decomposition products have been characterized by XRD, SEM, EDX, and VSM. XRD results revealed crystallinity with hexagonal wurtzite structure, while the average grain size was found to be 26 nm for Ti-doped ZnO and 29 nm for ZnO, using calculations based on Debye-Scherrer equation. Furthermore, the morphological studies by SEM showed particle agglomeration, while the presence of Ti3+ in the zinc oxide lattice is indicated by EDS analysis. Finally the hysteresis loop from VSM results shows that Ti-doped ZnO exhibits ferromagnetism.

  5. Effect of bismuth doping on the ZnO nanocomposite material and study of its photocatalytic activity under UV-light

    International Nuclear Information System (INIS)

    Chandraboss, V.L.; Natanapatham, L.; Karthikeyan, B.; Kamalakkannan, J.; Prabha, S.; Senthilvelan, S.

    2013-01-01

    Graphical abstract: The hetero-junctions that are formed between the ZnO and the Bi provide an internal electric field that facilitates separation of the electron-hole pairs and induces faster carrier migration. Thus they often enhanced photocatalytic reaction. - Highlights: • Bi-doped ZnO nanocomposite material was prepared by precipitation method. • Characterized by XRD, HR-SEM with EDX, UV–visible DRS and FT-RAMAN analysis. • Bi-doped ZnO nanocomposite material was used to photodegradation of Congo red. • Mechanism and photocatalytic effect of nanocomposite material have been discussed. - Abstract: Bismuth (Bi)-doped ZnO nanocomposite material was prepared by precipitation method with doping precursors of bismuth nitrate pentahydrate and oxalic acid, characterized by X-ray diffraction (XRD), High Resolution-Scanning Electron Microscopy (HR-SEM) with Energy Dispersive X-ray (EDX) analysis, UV–visible Diffuse Reflectance Spectroscopy (UV–visible DRS) and Fourier Transform-Raman (FT-RAMAN) analysis. The enhanced photocatalytic activity of the Bi-doped ZnO is demonstrated through photodegradation of Congo red under UV-light irradiation. The mechanism of photocatalytic effect of Bi-doped ZnO nanocomposite material has been discussed

  6. Ultrafine Cobalt Sulfide Nanoparticles Encapsulated Hierarchical N-doped Carbon Nanotubes for High-performance Lithium Storage

    International Nuclear Information System (INIS)

    Li, Xiaoyan; Fu, Nianqing; Zou, Jizhao; Zeng, Xierong; Chen, Yuming; Zhou, Limin; Lu, Wei; Huang, Haitao

    2017-01-01

    Graphical abstract: Ultrafine cobalt sulfide nanoparticles encapsulated in hierarchical N-doped carbon nanotubes show exceptional lithium ion storage as anodes. - Abstract: Nanostructured cobalt sulfide based materials with rational design are attractive for high-performance lithium-ion batteries. In this work, we report a multistep method to synthesize ultrafine cobalt sulfide nanoparticles encapsulated in hierarchical N-doped carbon nanotubes (CoS x @HNCNTs). Co-based zeolitic imidazolate framework (ZIF-67) nanotubes are obtained from the reaction between electrospun polyacrylonitrile/cobalt acetate and 2-methylimidazole, followed by the dissolution of template. Next, a combined calcination and sulfidation process is employed to convert the ZIF-67 nanotubes to CoS x @HNCNTs. Benefited from the compositional and structural features, the as-prepared nanostructured hybrid materials deliver superior lithium storage properties with high capacity of 1200 mAh g −1 at 0.25 A g −1 . More importantly, a remarkable capacity of 1086 mAh g −1 can be maintained after 100 cycles at the current density of 0.5 A g −1 . Even at a high rate of 5 A g −1 , a reversible capacity of 592 mAh g −1 after 1600 cycles can still be achieved.

  7. Electrodeposition of Cu-doped ZnO nanowire arrays and heterojunction formation with p-GaN for color tunable light emitting diode applications

    International Nuclear Information System (INIS)

    Lupan, O.; Pauporté, T.; Viana, B.; Aschehoug, P.

    2011-01-01

    Highlights: ► High quality copper-doped zinc oxide nanowires were electrochemically grown at low temperature. ► ZnO:Cu nanowires have been epitaxially grown on Mg-doped p-GaN single-crystalline layers. ► The (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction was used to fabricate a light-emitting diode structure. ► The photo- and electroluminescence emission was red-shifted to the violet spectral region compared to pure ZnO. ► The results are of importance for band-gap engineering of ZnO and for color-tunable LED. - Abstract: Copper-doped zinc oxide (ZnO:Cu) nanowires (NWs) were electrochemically deposited at low temperature on fluor-doped tin oxide (FTO) substrates. The electrochemical behavior of the Cu–Zn system for Cu-doped ZnO electrodeposition was studied and the electrochemical reaction mechanism is discussed. The synthesized ZnO arrayed layers were investigated by using SEM, XRD, EDX, photoluminescence and Raman techniques. X-ray diffraction analysis demonstrates a decrease in the lattice parameters of Cu-doped ZnO NWs. Structural analyses show that the nanomaterial is of hexagonal structure with the Cu incorporated in ZnO NWs probably by substituting zinc in the host lattice. Photoluminescence studies on pure and Cu-doped ZnO NWs shows that the near band edge emission is red-shifted by about 5 or 12 nm depending on Cu(II) concentration in the electrolytic bath solution (3 or 6 μmol l −1 ). Cu-doped ZnO NWs have been also epitaxially grown on Mg doped p-GaN single-crystalline layers and the (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction has been used to fabricate a light-emitting diode (LED) structure. The emission was red-shifted to the visible violet spectral region compared to pure ZnO. The present work demonstrates the ability of electrodeposition to produce high quality ZnO nanowires with tailored optical properties by doping. The obtained results are of great importance for further studies on bandgap engineering of ZnO, for color-tunable LED applications

  8. Nitrogen-doped carbon-supported cobalt-iron oxygen reduction catalyst

    Science.gov (United States)

    Zelenay, Piotr; Wu, Gang

    2014-04-29

    A Fe--Co hybrid catalyst for oxygen reaction reduction was prepared by a two part process. The first part involves reacting an ethyleneamine with a cobalt-containing precursor to form a cobalt-containing complex, combining the cobalt-containing complex with an electroconductive carbon supporting material, heating the cobalt-containing complex and carbon supporting material under conditions suitable to convert the cobalt-containing complex and carbon supporting material into a cobalt-containing catalyst support. The second part of the process involves polymerizing an aniline in the presence of said cobalt-containing catalyst support and an iron-containing compound under conditions suitable to form a supported, cobalt-containing, iron-bound polyaniline species, and subjecting said supported, cobalt-containing, iron bound polyaniline species to conditions suitable for producing a Fe--Co hybrid catalyst.

  9. Synthesis of High Crystalline Al-Doped ZnO Nanopowders from Al2O3 and ZnO by Radio-Frequency Thermal Plasma

    Directory of Open Access Journals (Sweden)

    Min-Kyeong Song

    2015-01-01

    Full Text Available High crystalline Al-doped ZnO (AZO nanopowders were prepared by in-flight treatment of ZnO and Al2O3 in Radio-Frequency (RF thermal plasma. Micron-sized (~1 μm ZnO and Al2O3 powders were mixed at Al/Zn ratios of 3.3 and 6.7 at.% and then injected into the RF thermal plasma torch along the centerline at a feeding rate of 6.6 g/min. The RF thermal plasma torch system was operated at the plate power level of ~140 kVA to evaporate the mixture oxides and the resultant vapor species were condensed into solid particles by the high flow rate of quenching gas (~7000 slpm. The FE-SEM images of the as-treated powders showed that the multipod shaped and the whisker type nanoparticles were mainly synthesized. In addition, these nanocrystalline structures were confirmed as the single phase AZO nanopowders with the hexagonal wurtzite ZnO structure by the XRD patterns and FE-TEM results with the SAED image. However, the composition changes of 0.3 and 1.0 at.% were checked for the as-synthesized AZO nanopowders at Al/Zn ratios of 3.3 and 6.7 at.%, respectively, by the XRF data, which can require the adjustment of Al/Zn in the mixture precursors for the applications of high Al doping concentrations.

  10. Positron annihilation studies of vacancy-type defects and room temperature ferromagnetism in chemically synthesized Li-doped ZnO nanocrystals

    International Nuclear Information System (INIS)

    Ghosh, S.; Khan, Gobinda Gopal; Mandal, K.; Thapa, Samudrajit; Nambissan, P.M.G.

    2014-01-01

    Highlights: • Evidence of zinc vacancy-induced intrinsic ferromagnetism in Li-doped ZnO. • Modification of defects and properties through alkali metal substitution. • Study of defect-modification using positron annihilation spectroscopy. • New way to prepare ZnO-based magnetic semiconductor for spintronic applications. -- Abstract: In this article, we have investigated the effects of Li incorporation on the lattice defects and room-temperature d 0 ferromagnetic behaviour in ZnO nanocrystals by correlating X-ray photoelectron, photoluminescence and positron annihilation spectroscopic study in details. It is found that at low doping level ( 1+ is an effective substituent of Zn site, but it prefers to occupy the interstitial positions when Li-doping exceeds 7 at.% resulting in lattice expansion and increase of particle sizes. The pristine ZnO nanocrystals exhibit ferromagnetic behaviour which is further enhanced significantly after few percentage of Li-doping in ZnO. The magnitude of both saturation magnetizations (M S ) as well as the Curie temperature (T C ) are found to increase considerably up to Li concentration of 10 at.% and then started to decrease on further Li-doping. The gradual enhancement of Zn vacancy (V Zn ) defects in ZnO nanocrystals due to Li substitution as confirmed from photoluminescence and positron annihilation spectroscopy measurements might be responsible to induce paramagnetic moments within ZnO host. The ferromagnetic exchange interaction between the localised moments of V Zn defects can be mediated though the holes arising due to Li-substitutional (Li Zn ) acceptor defects within ZnO. Hence, Li doping in ZnO favours in stabilizing considerable V Zn defects and thus helps to sustain long-range high-T C ferromagnetism in ZnO which can be a promising material in future spintronics

  11. Spatially Correlated, Single Nanomaterial-Level Structural and Optical Profiling of Cu-Doped ZnO Nanorods Synthesized via Multifunctional Silicides

    Directory of Open Access Journals (Sweden)

    Johnson Truong

    2018-04-01

    Full Text Available We demonstrate a straightforward and effective method to synthesize vertically oriented, Cu-doped ZnO nanorods (NRs using a novel multipurpose platform of copper silicide nanoblocks (Cu3Si NBs preformed laterally in well-defined directions on Si. The use of the surface-organized Cu3Si NBs for ZnO NR growth successfully results in densely assembled Cu-doped ZnO NRs on each NB platform, whose overall structures resemble thick bristles on a brush head. We show that Cu3Si NBs can uniquely serve as a catalyst for ZnO NRs, a local dopant source of Cu, and a prepatterned guide to aid the local assembly of the NRs on the growth substrate. We also ascertain the crystalline structures, optical properties, and spectroscopic signatures of the Cu-doped ZnO NRs produced on the NBs, both at each module of NRs/NB and at their ensemble level. Subsequently, we determine their augmented properties relative to the pristine form of undoped ZnO NRs and the source material of Cu3Si NBs. We provide spatially correlated structural and optical data for individual modules of Cu-doped ZnO NRs assembled on a Cu3Si NB by resolving them along the different positions on the NB. Ensemble-averaged versus individual behaviors of Cu-doped ZnO NRs on Cu3Si NBs are then compared. We further discuss the potential impact of such ZnO-derived NRs on their relatively unexplored biological and biomedical applications. Our efforts will be particularly useful when exploiting each integrated module of self-aligned, Cu-doped ZnO NRs on a NB as a discretely addressable, active element in solid-state sensors and miniaturized luminescent bioprobes.

  12. Positron annihilation studies of vacancy-type defects and room temperature ferromagnetism in chemically synthesized Li-doped ZnO nanocrystals

    Energy Technology Data Exchange (ETDEWEB)

    Ghosh, S., E-mail: sghoshphysics@gmail.com [S.N. Bose National Centre for Basic Sciences, Block JD, Sector III, Salt Lake, Kolkata 700098 (India); Khan, Gobinda Gopal [Centre for Research in Nanoscience and Nanotechnology, University of Calcutta, Technology Campus, Block JD2, Sector III, Salt Lake City, Kolkata 700098 (India); Mandal, K. [S.N. Bose National Centre for Basic Sciences, Block JD, Sector III, Salt Lake, Kolkata 700098 (India); Thapa, Samudrajit; Nambissan, P.M.G. [Centre for Research in Nanoscience and Nanotechnology, University of Calcutta, Technology Campus, Block JD2, Sector III, Salt Lake City, Kolkata 700098 (India); Saha Institute of Nuclear Physics, Sector 1, Block AF, Bidhannagar, Kolkata 700064 (India)

    2014-03-25

    Highlights: • Evidence of zinc vacancy-induced intrinsic ferromagnetism in Li-doped ZnO. • Modification of defects and properties through alkali metal substitution. • Study of defect-modification using positron annihilation spectroscopy. • New way to prepare ZnO-based magnetic semiconductor for spintronic applications. -- Abstract: In this article, we have investigated the effects of Li incorporation on the lattice defects and room-temperature d{sup 0} ferromagnetic behaviour in ZnO nanocrystals by correlating X-ray photoelectron, photoluminescence and positron annihilation spectroscopic study in details. It is found that at low doping level (<7 at.%), Li{sup 1+} is an effective substituent of Zn site, but it prefers to occupy the interstitial positions when Li-doping exceeds 7 at.% resulting in lattice expansion and increase of particle sizes. The pristine ZnO nanocrystals exhibit ferromagnetic behaviour which is further enhanced significantly after few percentage of Li-doping in ZnO. The magnitude of both saturation magnetizations (M{sub S}) as well as the Curie temperature (T{sub C}) are found to increase considerably up to Li concentration of 10 at.% and then started to decrease on further Li-doping. The gradual enhancement of Zn vacancy (V{sub Zn}) defects in ZnO nanocrystals due to Li substitution as confirmed from photoluminescence and positron annihilation spectroscopy measurements might be responsible to induce paramagnetic moments within ZnO host. The ferromagnetic exchange interaction between the localised moments of V{sub Zn} defects can be mediated though the holes arising due to Li-substitutional (Li{sub Zn}) acceptor defects within ZnO. Hence, Li doping in ZnO favours in stabilizing considerable V{sub Zn} defects and thus helps to sustain long-range high-T{sub C} ferromagnetism in ZnO which can be a promising material in future spintronics.

  13. A simple synthetic route of N-doped mesoporous carbon derived from casein extracted with cobalt ions for high rate performance supercapacitors

    International Nuclear Information System (INIS)

    Jia, Shaopei; Wang, Yanhui; Tian, Pengfei; Zhou, Shuyu; Cai, Haixia; Gao, Hongwei; Zang, Jianbing

    2017-01-01

    Highlights: •NMC is prepared by pyrolysis of cobalt-containing casein. •Cobalt-containing casein is extracted from the pure milk by cobalt ions. •The cobalt element increases the specific surface area and the N doping amount. •NMC exhibits high specific capacitance, high rate capability, and excellent cycling stability. -- Abstract: Nitrogen-doped mesoporous carbon (NMC) was synthesized via pyrolysis of cobalt-containing casein obtained by extraction from pure milk with the auxiliary of cobalt ions. The cobalt element in casein promoted specific surface area and N element doping amount of casein-derived porous carbon. The N-doped porous carbon obtained by carbonization at 800 °C (NPC-800) possessed a specific surface area of ∼886.7 m 2 g −1 , and the mesoporous size was centered at 2.7 and 7 nm. X-ray photoelectron spectroscopy analysis showed that the nitrogen content of NPC-800 was 3.29 at%. The NPC-800 was explored as a symmetric supercapacitor, which exhibited specific capacity of 380 F g −1 at a current density of 0.5 A g −1 , 218 F g −1 at a current density of 20 A g −1 , and high capacitance retention of 91.3% after charging/discharging 5,000 cycles.

  14. Structural and magnetic properties of cobalt-doped iron oxide nanoparticles prepared by solution combustion method for biomedical applications

    Directory of Open Access Journals (Sweden)

    Venkatesan K

    2015-10-01

    Full Text Available Kaliyamoorthy Venkatesan,1 Dhanakotti Rajan Babu,1 Mane Prabhu Kavya Bai,2 Ravi Supriya,2 Radhakrishnan Vidya,2 Saminathan Madeswaran,1 Pandurangan Anandan,3 Mukannan Arivanandhan,3 Yasuhiro Hayakawa3 1School of Advanced Sciences, 2School of Bio Sciences and Technology, VIT University, Vellore, Tamil Nadu, India; 3Research Institute of Electronics, Shizuoka University, Hamamatsu, Japan Abstract: Cobalt-doped iron oxide nanoparticles were prepared by solution combustion technique. The structural and magnetic properties of the prepared samples were also investigated. The average crystallite size of cobalt ferrite (CoFe2O4 magnetic nanoparticle was calculated using Scherrer equation, and it was found to be 16±5 nm. The particle size was measured by transmission electron microscope. This value was found to match with the crystallite size calculated by Scherrer equation corresponding to the prominent intensity peak (311 of X-ray diffraction. The high-resolution transmission electron microscope image shows clear lattice fringes and high crystallinity of cobalt ferrite magnetic nanoparticles. The synthesized magnetic nanoparticles exhibited the saturation magnetization value of 47 emu/g and coercivity of 947 Oe. The anti-microbial activity of cobalt ferrite nanoparticles showed better results as an anti-bacterial agent. The affinity constant was determined for the nanoparticles, and the cytotoxicity studies were conducted for the cobalt ferrite nanoparticles at different concentrations and the results are discussed. Keywords: cytotoxicity, HR-TEM, magnetic nanoparticles, VSM 

  15. Structural and magnetic properties of cobalt-doped iron oxide nanoparticles prepared by solution combustion method for biomedical applications.

    Science.gov (United States)

    Venkatesan, Kaliyamoorthy; Rajan Babu, Dhanakotti; Kavya Bai, Mane Prabhu; Supriya, Ravi; Vidya, Radhakrishnan; Madeswaran, Saminathan; Anandan, Pandurangan; Arivanandhan, Mukannan; Hayakawa, Yasuhiro

    2015-01-01

    Cobalt-doped iron oxide nanoparticles were prepared by solution combustion technique. The structural and magnetic properties of the prepared samples were also investigated. The average crystallite size of cobalt ferrite (CoFe2O4) magnetic nanoparticle was calculated using Scherrer equation, and it was found to be 16±5 nm. The particle size was measured by transmission electron microscope. This value was found to match with the crystallite size calculated by Scherrer equation corresponding to the prominent intensity peak (311) of X-ray diffraction. The high-resolution transmission electron microscope image shows clear lattice fringes and high crystallinity of cobalt ferrite magnetic nanoparticles. The synthesized magnetic nanoparticles exhibited the saturation magnetization value of 47 emu/g and coercivity of 947 Oe. The anti-microbial activity of cobalt ferrite nanoparticles showed better results as an anti-bacterial agent. The affinity constant was determined for the nanoparticles, and the cytotoxicity studies were conducted for the cobalt ferrite nanoparticles at different concentrations and the results are discussed.

  16. Variation in Structural and Optical Properties of Al Doped ZnO Nanoparticles Synthesized by Sol-gel Process

    Directory of Open Access Journals (Sweden)

    Vanaja Aravapalli

    2017-04-01

    Full Text Available This article focuses on analyzing structural and optical properties of Al doped ZnO (AZO synthesized with two different precursors aluminum chloride and aluminum nitrate. The nanoparticles were successfully fabricated and characterized at room temperature by sol-gel process. The objective of improving properties of ZnO nanoparticles by introducing dopants was successful with formation of nanoparticles having different crystalline sizes, optical absorption and luminescence properties. The two different sources influenced properties of ZnO. The particles with less crystalline size obtained from aluminum nitrate. Change in morphology from spherical to bar like morphology proved from SEM spectra. Presence of functional groups predicted from FTIR spectra. PL spectra proved UV emission and visible emission for AZO nanoparticles synthesized using dopant sources aluminum chloride and aluminum nitrate respectively. The obtained properties prove successful utilization of AZO nanoparticles as building materials in fabrication of optoelectronic devices.

  17. Control of N/N2 species ratio in NO plasma for p-type doping of ZnO

    International Nuclear Information System (INIS)

    Chen Xingyou; Zhang Zhenzhong; Jiang Mingming; Wang Shuangpeng; Li Binghui; Shan Chongxin; Liu Lei; Zhao Dongxu; Shen Dezhen; Yao Bin

    2011-01-01

    Nitrogen-doped ZnO thin films were grown on c-plane sapphire (Al 2 O 3 ) substrates via plasma-assisted molecular beam epitaxy using plasma activated nitric oxide (NO) as the oxygen source and dopant. X-ray diffraction measurements indicate that a small NO flux benefits the crystal quality of the thin films. Hall effect measurements indicate that the electron density of the ZnO films decreases gradually with decreasing NO flux, and the conduction reverses to p-type at a certain flux. Optical emission spectra indicate that the N atom content in the NO plasma increases with decreasing NO flux, and the origin of this is discussed. X-ray photoelectron spectroscopy measurements demonstrate that the number of N atom occupied O sites in the ZnO lattice increases correspondingly.

  18. Comparison of the influence of boron and aluminium doping on the material properties of electrochemically deposited ZnO films

    Energy Technology Data Exchange (ETDEWEB)

    Calnan, Sonya [Helmholtz-Zentrum für Materialien und Energie GmbH, Hahn-Meitner Platz 1, 14109 Berlin (Germany); Riedel, Wiebke; Gledhill, Sophie [Helmholtz-Zentrum für Materialien und Energie GmbH, Hahn-Meitner Platz 1, 14109 Berlin (Germany); Fachbereich Physik, Freie Universitaet Berlin, Arnimallee 14, 14195 Berlin (Germany); Stannowski, Bernd [Helmholtz-Zentrum für Materialien und Energie GmbH, Hahn-Meitner Platz 1, 14109 Berlin (Germany); Lux-Steiner, Martha Ch. [Helmholtz-Zentrum für Materialien und Energie GmbH, Hahn-Meitner Platz 1, 14109 Berlin (Germany); Fachbereich Physik, Freie Universitaet Berlin, Arnimallee 14, 14195 Berlin (Germany); Schlatmann, Rutger [Helmholtz-Zentrum für Materialien und Energie GmbH, Hahn-Meitner Platz 1, 14109 Berlin (Germany); Fachbereich 1 Ingenieurwissenschaften I, University of Applied Science (HTW) Berlin, Wilhelminenhofstraße 75 A, 12459 Berlin (Germany)

    2015-11-02

    The effect of varying the boron and aluminium content of the starting electrolyte for extrinsically doped ZnO films grown on SnO{sub 2}:F substrates by electrochemical deposition was investigated. The ZnO:B film surface was characterized by grains with mainly hexagonal faces exposed while the exposed faces of the ZnO:Al grains were rectangular. Whereas a B{sup 3+}/Zn{sup 2+} ratio of up to 10 at.% in the electrolyte had no significant effect on the crystalline structure of the ZnO films, an Al{sup 3+}/Zn{sup 2+} ratio above 0.25 at.% increased the disorder in the crystalline structure. All the boron doped films exhibit a strong E{sub 2}-high Raman mode related to wurtzite ZnO structure but this peak was much weaker for ZnO:Al and diminished with increasing Al incorporation in the films. Exposing the films to ultra-violet light reduced their effective sheet resistance from values beyond measurement range to values between 40 and 5000 kΩ/sq for film thicknesses of 200–550 nm. Inspection of the optical spectra near the bandgap edge and the plasma edge in the mid infrared range, showed that the Al-doping resulted in a higher carrier concentration ~ 10{sup 20} cm{sup −3} than B-doping. X-ray electron spectroscopy showed that the dopant efficiency was limited by the absence of dopant atoms near the surface of all the ZnO:B films and of the lightly doped ZnO:Al and, by the formation of aluminium oxide at the surface of the more highly doped ZnO:Al films. - Highlights: • Crystalline ZnO grown by electrochemical deposition. • Comparison of influence of H{sub 3}BO{sub 3} and Al(NO{sub 3}){sub 3} as dopant sources. • Different ZnO crystalline orientation for Al and boron doping. • Film surface chemical composition suppressed electrical conductivity.

  19. Photocatalytic activity of ZnO doped with Ag on the degradation of endocrine disrupting under UV irradiation and the investigation of its antibacterial activity

    Energy Technology Data Exchange (ETDEWEB)

    Bechambi, Olfa [Université de Tunis El Manar, Faculté des Sciences de Tunis, Laboratoire de Chimie des Matériaux et Catalyse, 2092, Tunis (Tunisia); Chalbi, Manel [Laboratoire de Bioprocédés Environnementaux, Centre de Biotechnologie de Sfax, B.P. 1177, 3018 Sfax (Tunisia); Najjar, Wahiba, E-mail: najjarwahiba2014@gmail.com [Université de Tunis El Manar, Faculté des Sciences de Tunis, Laboratoire de Chimie des Matériaux et Catalyse, 2092, Tunis (Tunisia); Sayadi, Sami [Laboratoire de Bioprocédés Environnementaux, Centre de Biotechnologie de Sfax, B.P. 1177, 3018 Sfax (Tunisia)

    2015-08-30

    Graphical abstract: - Highlights: • A series of Ag-doped ZnO were synthesized via hydrothermal method. • Effect of doping with silver on the textural, structural optical properties of ZnO. • The photocatalytic activity has been tested using bisphenol A and nonylphenol. • The highest degradation efficiency was obtained with 1% Ag. • Ag doping enhances the photocatalytic and antibacterial activities of ZnO. - Abstract: Ag-doped ZnO photocatalysts with different Ag molar content (0.0, 0.5, 1.0, 2.0 and 4.0%) were prepared via hydrothermal method. The X-ray diffraction (XRD), Nitrogen physisorption at 77 K, Fourier transformed infrared spectroscopy (FTIR), UV–-Visible spectroscopy, Photoluminescence spectra (PL) and Raman spectroscopy were used to characterize the structural, textural and optical properties of the samples. The results showed that Ag-doping does not change the average crystallite size with the Ag low content (≤1.0%) but slightly decreases with Ag high content (>1.0%). The specific surface area (S{sub BET}) increases with the increase of the Ag content. The band gap values of ZnO are decreased with the increase of the Ag doping level. The results of the photocatalytic degradation of bisphenol A (BPA) and nonylphenol (NP) in aqueous solutions under UV irradiation and in the presence of hydrogen peroxide (H{sub 2}O{sub 2}) showed that silver ions doping greatly improved the photocatalytic efficiency of ZnO. The TOC conversion BPA and NP are 72.1% and 81.08% respectively obtained using 1% Ag-doped ZnO. The enhancement of photocatalytic activity is ascribed to the fact that the modification of ZnO with an appropriate amount of Ag can increase the separation efficiency of the photogenerated electrons-holes in ZnO. The antibacterial activity of the catalysts which uses Escherichia coli as a model for Gram-negative bacteria confirmed that Ag-doped ZnO possessed more antibacterial activity than the pure ZnO.

  20. Photocatalytic activity of ZnO doped with Ag on the degradation of endocrine disrupting under UV irradiation and the investigation of its antibacterial activity

    International Nuclear Information System (INIS)

    Bechambi, Olfa; Chalbi, Manel; Najjar, Wahiba; Sayadi, Sami

    2015-01-01

    Graphical abstract: - Highlights: • A series of Ag-doped ZnO were synthesized via hydrothermal method. • Effect of doping with silver on the textural, structural optical properties of ZnO. • The photocatalytic activity has been tested using bisphenol A and nonylphenol. • The highest degradation efficiency was obtained with 1% Ag. • Ag doping enhances the photocatalytic and antibacterial activities of ZnO. - Abstract: Ag-doped ZnO photocatalysts with different Ag molar content (0.0, 0.5, 1.0, 2.0 and 4.0%) were prepared via hydrothermal method. The X-ray diffraction (XRD), Nitrogen physisorption at 77 K, Fourier transformed infrared spectroscopy (FTIR), UV–-Visible spectroscopy, Photoluminescence spectra (PL) and Raman spectroscopy were used to characterize the structural, textural and optical properties of the samples. The results showed that Ag-doping does not change the average crystallite size with the Ag low content (≤1.0%) but slightly decreases with Ag high content (>1.0%). The specific surface area (S BET ) increases with the increase of the Ag content. The band gap values of ZnO are decreased with the increase of the Ag doping level. The results of the photocatalytic degradation of bisphenol A (BPA) and nonylphenol (NP) in aqueous solutions under UV irradiation and in the presence of hydrogen peroxide (H 2 O 2 ) showed that silver ions doping greatly improved the photocatalytic efficiency of ZnO. The TOC conversion BPA and NP are 72.1% and 81.08% respectively obtained using 1% Ag-doped ZnO. The enhancement of photocatalytic activity is ascribed to the fact that the modification of ZnO with an appropriate amount of Ag can increase the separation efficiency of the photogenerated electrons-holes in ZnO. The antibacterial activity of the catalysts which uses Escherichia coli as a model for Gram-negative bacteria confirmed that Ag-doped ZnO possessed more antibacterial activity than the pure ZnO

  1. Boron doped ZnO embedded into reduced graphene oxide for electrochemical supercapacitors

    Science.gov (United States)

    Alver, Ü.; Tanrıverdi, A.

    2016-08-01

    In this work, reduced graphene oxide/boron doped zinc oxide (RGO/ZnO:B) composites were fabricated by a hydrothermal process and their electrochemical properties were investigated as a function of dopant concentration. First, boron doped ZnO (ZnO:B) particles was fabricated with different boron concentrations (5, 10, 15 and 20 wt%) and then ZnO:B particles were embedded into RGO sheets. The physical properties of sensitized composites were characterized by XRD and SEM. Characterization indicated that the ZnO:B particles with plate-like structure in the composite were dispersed on graphene sheets. The electrochemical properties of the RGO/ZnO:B composite were investigated through cyclic voltammetry, galvanostatic charge/discharge measurements in a 6 M KOH electrolyte. Electrochemical measurements show that the specific capacitance values of RGO/ZnO:B electrodes increase with increasing boron concentration. RGO/ZnO:B composite electrodes (20 wt% B) display the specific capacitance as high as 230.50 F/g at 5 mV/s, which is almost five times higher than that of RGO/ZnO (52.71 F/g).

  2. Structural and Optical Properties of Group III Doped Hydrothermal ZnO Thin Films

    KAUST Repository

    Mughal, Asad J.

    2017-01-11

    In this work, we employ a simple two-step growth technique to deposit impurity doped heteroepitaxial thin films of (0001) ZnO onto (111) MgAl2O4 spinel substrates through a combination of atomic layer deposition (ALD) and hydrothermal growth. The hydrothermal layer is doped with Al, Ga, and In through the addition of their respective nitrate salts. We evaluated the effect that varying the concentrations of these dopants has on both the structural and optical properties of these films. It was found that the epitaxial ALD layer created a ⟨111⟩MgAl2O4∥⟨0001⟩ZnO out-of-plane orientation and a ⟨1¯1¯2⟩MgAl2O4∥∥⟨011¯0⟩ZnO in-plane orientation between the film and substrate. The rocking curve line widths ranged between 0.75° and 1.80° depending on dopant concentration. The optical bandgap determined through the Tauc method was between 3.28 eV and 3.39 eV and showed a Burstein-Moss shift with increasing dopant concentration.

  3. Structural and magnetic properties of Gd-doped ZnO

    KAUST Repository

    Bantounas, Ioannis

    2014-01-01

    We use density functional theory to investigate structural and magnetic properties of Gd doped ZnO, accounting for the impurity 4f states using the GGA + U method. (i) We calculate the binding energy of forming [Gd-Gd] dimers, [VO - GdZn] and [VZn - GdZn] complexes and find that while the formation of [VZn - GdZn] is favourable, [GdZn - GdZn] and [VO - GdZn] complexes are less likely to form. Next, (ii) we investigate the spacial arrangement of two (and three) GdZn impurities in a 3 × 3 × 2 supercell and find that the magnetic impurities are energetically favourable when occupying distant lattice sites. Finally, we study the nature of interactions between the magnetic impurities (iii) for Gd in nearest-neighbour and non-nearest-neighbour Zn sites, (iv) in the presence of Zn or O vacancies, and (v) with and without additional charge carriers. Our results show mainly paramagnetic behaviour. In a few cases, e.g. magnetic impurities occupying in-plane nearest-neighbour zinc sites with n-type carrier doping, weak ferromagnetic coupling is observed. This magnetic ordering is of the order of a few meV and can be easily destroyed by thermal fluctuations. We thus expect Gd:ZnO to show paramagnetic behaviour at temperatures approaching room temperature.

  4. Genesis of flake-like morphology and dye-sensitized solar cell performance of Al-doped ZnO particles: a study

    International Nuclear Information System (INIS)

    Sengupta, D.; Mondal, B.; Mukherjee, K.

    2017-01-01

    In dye-sensitized solar cell (DSSC) application, the particulate morphologies of photo-anode facilitate efficient dye loading and thus lead to better photo-conversion efficiency than their thin film counterpart. However, till date, the electronic and optical properties as well as the DSSC application of Al-doped ZnO (AZO) particles as photo-anode material is studied less than thin films. Herein, phase formation behavior, morphology evolution, optical properties, and dye-sensitized solar cell performance of wet chemically prepared ZnO and AZO (dopant level: 1–4 mol%) particles are studied. It is found that Al doping modulates significantly the ZnO morphology which in turn results the maximum dye adsorption as well as best photo-conversion efficiency at optimum dopant concentration. Specifically, the nanoparticle of ZnO turns predominantly to flake-like morphology with a higher surface area when 2 mol% Al is doped. Such morphology modulation is expected, since the crystallinity, lattice parameters, and lattice strain of ZnO changes appreciably with Al doping. The variations of optical properties (absorbance, diffused reflectance, and band gap) of AZO materials as compared to primitive ZnO are also identified through UV-vis studies. An attempt is made here to correlate the structural features with the photovoltaic performances of ZnO and AZO.

  5. Genesis of flake-like morphology and dye-sensitized solar cell performance of Al-doped ZnO particles: a study

    Energy Technology Data Exchange (ETDEWEB)

    Sengupta, D.; Mondal, B.; Mukherjee, K., E-mail: kalisadhanm@yahoo.com [CSIR-Central Mechanical Engineering Research Institute, Centre for Advanced Materials Processing (India)

    2017-03-15

    In dye-sensitized solar cell (DSSC) application, the particulate morphologies of photo-anode facilitate efficient dye loading and thus lead to better photo-conversion efficiency than their thin film counterpart. However, till date, the electronic and optical properties as well as the DSSC application of Al-doped ZnO (AZO) particles as photo-anode material is studied less than thin films. Herein, phase formation behavior, morphology evolution, optical properties, and dye-sensitized solar cell performance of wet chemically prepared ZnO and AZO (dopant level: 1–4 mol%) particles are studied. It is found that Al doping modulates significantly the ZnO morphology which in turn results the maximum dye adsorption as well as best photo-conversion efficiency at optimum dopant concentration. Specifically, the nanoparticle of ZnO turns predominantly to flake-like morphology with a higher surface area when 2 mol% Al is doped. Such morphology modulation is expected, since the crystallinity, lattice parameters, and lattice strain of ZnO changes appreciably with Al doping. The variations of optical properties (absorbance, diffused reflectance, and band gap) of AZO materials as compared to primitive ZnO are also identified through UV-vis studies. An attempt is made here to correlate the structural features with the photovoltaic performances of ZnO and AZO.

  6. Synthesis of S-doped ZnO by the interaction of sulfur with zinc salt in PEG200

    International Nuclear Information System (INIS)

    Xie, Xin-Yuan; Zhan, Pei; Li, Li-Yun; Zhou, Dan-Jie; Guo, Dan-Yi; Meng, Jian-Xin; Bai, Yan; Zheng, Wen-Jie

    2015-01-01

    Graphical abstract: S-doped ZnO nanoparticles (S-ZnO) were synthesized via a one-step and green method by using zinc acetate dihydrate as a precursor, S powder as a dopant and PEG200 as a solvent with the number of moles of sulfur (n S ) smaller than that of zinc salt (n Zn ). A possible mechanism was proposed to elucidate the formation of S-ZnO. PL spectra show strong green emission band, which could be applied to ZnO optoelectronic devices that work in the visible spectrum. - Highlights: • A green and one-step method was developed to synthesize S-doped ZnO nanoparticles. • The molar ratio of Zn(II) and S influences the composition of the products greatly. • The interactive mechanism of S with zinc salt in PEG was elucidated. • PL spectra of S-doped ZnO nanoparticles show strong green emission band. - Abstract: S-doped ZnO nanoparticles (S-ZnO) were synthesized via a one-step and green method. In this method, zinc acetate dihydrate was used as a precursor and sulfur was the dopant. The reaction between zinc salt and S occurred in PEG200 media. X-ray diffraction, field emission scanning electron microscopy, transmission electron microscopy, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy, UV–Vis spectroscopy and room temperature photoluminescence were used to characterize the products. The results show that the molar ratio of Zn(II) and S determines the composition, structure, surface morphology, and luminescence properties of the products greatly. When the number of moles of sulfur (n S ) is smaller than that of zinc salt (n Zn ), the products are S-ZnO with diameters of 40–55 nm and they have ultraviolet absorption peaks at 363 nm. The incorporation of S into ZnO is supported by broadening and lower Bragg angle shift in XRD pattern. FTIR spectra show that PEG200 adsorbs onto the surfaces of the S-ZnO as a capping agent. PL spectra show that the effective sulfur doping

  7. Electrical, dielectric and photocatalytic properties of Fe-doped ZnO nanomaterials synthesized by sol gel method

    Directory of Open Access Journals (Sweden)

    Yacine Cherif

    2016-09-01

    Full Text Available Fe-doped ZnO nanoparticles were synthesized by sol gel technique. Fine-scale and single phase hexagonal wurtzite structure in all samples were confirmed by SEM and XRD, respectively. The band gap energy depends on the amount of Fe and was found to be in the range of 3.11–2.53 eV. The electric and dielectric properties were investigated using complex impedance spectroscopy. AC conductivity data were correlated with the barrier hopping (CBH model to evaluate the binding energy (Wm, the minimum hopping distance (Rmin and the density of states at Fermi level, N(EF. Fe doping in ZnO also improved the photocatalytic activity. Thus, the sample Zn0.95Fe0.05O showed high degradation potential towards methylene blue (MB, i.e. it degrades 90% of BM in 90 min under UV light.

  8. Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

    KAUST Repository

    Flemban, Tahani H.; Sequeira, M. C.; Zhang, Z.; Venkatesh, S.; Alves, E.; Lorenz, K.; Roqan, Iman S.

    2016-01-01

    Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

  9. Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

    KAUST Repository

    Flemban, Tahani H.

    2016-02-08

    Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

  10. Friction and wear behavior of nitrogen-doped ZnO thin films deposited via MOCVD under dry contact

    Directory of Open Access Journals (Sweden)

    U.S. Mbamara

    2016-06-01

    Full Text Available Most researches on doped ZnO thin films are tilted toward their applications in optoelectronics and semiconductor devices. Research on their tribological properties is still unfolding. In this work, nitrogen-doped ZnO thin films were deposited on 304 L stainless steel substrate from a combination of zinc acetate and ammonium acetate precursor by MOCVD technique. Compositional and structural studies of the films were done using Rutherford Backscattering Spectroscopy (RBS and X-ray Diffraction (XRD. The frictional behavior of the thin film coatings was evaluated using a ball-on-flat configuration in reciprocating sliding under dry contact condition. After friction test, the flat and ball counter-face surfaces were examined to assess the wear dimension and failure mechanism. Both friction behavior and wear (in the ball counter-face were observed to be dependent on the crystallinity and thickness of the thin film coatings.

  11. Al and Fe co-doped transparent conducting ZnO thin film for mediator-less biosensing application

    Directory of Open Access Journals (Sweden)

    Shibu Saha

    2011-12-01

    Full Text Available Highly c-axis oriented Al and Fe co-doped ZnO (ZAF thin film is prepared by pulsed laser deposition. Fe introduces redox centre along with shallow donor level while Al doping enhances conductivity of ZnO, thus removing the requirement of both mediator and bottom conducting layer in bioelectrode. Model enzyme (glucose oxidase, was immobilized on surface of ZAF matrix. Cyclic voltammetry and photometric assay show that prepared bio-electrode is sensitive to glucose concentration with enhanced response of 0.18 μAmM-1cm-2 and low Km ∼ 2.01 mM. The results illustrate that ZAF is an attractive matrix for realization of miniaturized mediator-less solid state biosensor.

  12. Characterization and Luminescence Properties of Color-Tunable Dy3+-Doped BaY2ZnO5 Nanophosphors

    Science.gov (United States)

    Sonika; Khatkar, S. P.; Khatkar, Avni; Kumar, Rajesh; Taxak, V. B.

    2015-01-01

    Dy3+-doped BaY2ZnO5 nanophosphors were successfully synthesized by use of a solution combustion process. The effects of sintering temperature and dysprosium concentration on the structural and luminescence characteristics of the phosphors were investigated. X-ray diffraction (XRD) analysis confirmed the formation of pure orthorhombic BaY2ZnO5 with the space group Pbnm at 1100°C. Morphological investigation revealed spherical nanoparticles with smooth surfaces. The luminescence features of the nanophosphor were studied by use of photoluminescence excitation (PLE) and photoluminescence emission (PL), with luminescence decay curves and color ( x, y) coordinates. On excitation at 355 nm, BaY2ZnO5 nanophosphor doped with trivalent dysprosium ion emits white light as a mixture of blue (4F9/2 → 6H15/2) and yellow (4F9/2 → 6H13/2) emission. Concentration quenching is explained on the basis of cross-relaxation between intermediate Dy3+ states. Thus, BaY2ZnO5:Dy3+ nanophosphor may be suitable for producing efficient white light for ultraviolet-light-emitting diodes (UV-LEDs), fluorescent lamps, and a variety of optical display panels.

  13. Band gap tuning of ZnO nanoparticles via Mg doping by femtosecond laser ablation in liquid environment

    International Nuclear Information System (INIS)

    Chelnokov, E.; Rivoal, M.; Colignon, Y.; Gachet, D.; Bekere, L.; Thibaudau, F.; Giorgio, S.; Khodorkovsky, V.; Marine, W.

    2012-01-01

    Highlights: ► Femtosecond laser ablation synthesis of Mg doped ZnO nanoparticles. ► Electronic properties of ZnO are modified by Mg. ► Band gap and exciton energy shifts to the blue. ► The exciton energy shift is saturated at Mg content of about 20%. ► Phase separation at Mg content is at more than 25%. ► Mechanism of exciton pinning – recombination via new surface states. - Abstract: We use multiphoton IR femtosecond laser ablation to induce non-thermal non-equilibrium conditions of the nanoparticle growth in liquids. Modifications of the electronic properties of ZnO NP were achieved by Mg ion doping of targets prepared from mixtures of Zn and Mg acetylacetonates. The nanoparticle sizes were 3–20 nm depending on the ablation conditions. X-ray fluorescence indicates that stoichiometric ablation and incorporation of Mg in nanocrystalline ZnO occurs. HRTEM observations show that nanoparticles retain their wurtzite structure, while at high Mg concentrations we detect the MgO rich domains. Exciton emissions exhibit relatively narrow bands with progressive and controlled blue shifts up to 184 meV. The exciton energy correlates to band edge absorption indicating strong modification of the NP band gaps. Stabilisation of the exciton blue shift is observed at high Mg concentration. It is accompanied by the formation of structure defects and ZnO/MgO phase separation within the nanoparticles.

  14. Effect of Ag doping on the structural, electrical and optical properties of ZnO grown by MOCVD at different substrate temperatures

    Science.gov (United States)

    Ievtushenko, A.; Karpyna, V.; Eriksson, J.; Tsiaoussis, I.; Shtepliuk, I.; Lashkarev, G.; Yakimova, R.; Khranovskyy, V.

    2018-05-01

    ZnO films and nanostructures were deposited on Si substrates by MOCVD using single source solid state zinc acetylacetonate (Zn(AA)) precursor. Doping by silver was realized in-situ via adding 1 and 10 wt. % of Ag acetylacetonate (Ag(AA)) to zinc precursor. Influence of Ag on the microstructure, electrical and optical properties of ZnO at temperature range 220-550 °C was studied by scanning, transmission electron and Kelvin probe force microscopy, photoluminescence and four-point probe electrical measurements. Ag doping affects the ZnO microstructure via changing the nucleation mode into heterogeneous and thus transforming the polycrystalline films into a matrix of highly c-axis textured hexagonally faceted nanorods. Increase of the work function value from 4.45 to 4.75 eV was observed with Ag content increase, which is attributed to Ag behaviour as a donor impurity. It was observed, that near-band edge emission of ZnO NS was enhanced with Ag doping as a result of quenching deep-level emission. Upon high doping of ZnO by Ag it tends to promote the formation of basal plane stacking faults defect, as it was observed by HR TEM and PL study in the case of 10 wt.% of Ag. Based on the results obtained, it is suggested that NS deposition at lower temperatures (220-300 °C) is more favorable for p-type doping of ZnO.

  15. Synthesis of Fe-Doped ZnO Nanorods by Rapid Mixing Hydrothermal Method and Its Application for High Performance UV Photodetector

    Directory of Open Access Journals (Sweden)

    Chan Oeurn Chey

    2014-01-01

    Full Text Available We have successfully synthesized Fe-doped ZnO nanorods by a new and simple method in which the adopted approach is by using ammonia as a continuous source of OH- for hydrolysis instead of hexamethylenetetramine (HMT. The energy dispersive X-ray (EDX spectra revealed that the Fe peaks were presented in the grown Fe-doped ZnO nanorods samples and the X-ray photoelectron spectroscopy (XPS results suggested that Fe3+ is incorporated into the ZnO lattice. Structural characterization indicated that the Fe-doped ZnO nanorods grow along the c-axis with a hexagonal wurtzite structure and have single crystalline nature without any secondary phases or clusters of FeO or Fe3O4 observed in the samples. The Fe-doped ZnO nanorods showed room temperature (300 K ferromagnetic magnetization versus field (M-H hysteresis and the magnetization increases from 2.5 μemu to 9.1 μemu for Zn0.99Fe0.01O and Zn0.95Fe0.05O, respectively. Moreover, the fabricated Au/Fe-doped ZnO Schottky diode based UV photodetector achieved 2.33 A/W of responsivity and 5 s of time response. Compared to other Au/ZnO nanorods Schottky devices, the presented responsivity is an improvement by a factor of 3.9.

  16. Effect of Co doping concentration on structural properties and optical parameters of Co-doped ZnO thin films by sol-gel dip-coating method.

    Science.gov (United States)

    Nam, Giwoong; Yoon, Hyunsik; Kim, Byunggu; Lee, Dong-Yul; Kim, Jong Su; Leem, Jae-Young

    2014-11-01

    The structural and optical properties of Co-doped ZnO thin films prepared by a sol-gel dip-coating method were investigated. X-ray diffraction analysis showed that the thin films were grown with a c-axis preferred orientation. The position of the (002) peak was almost the same in all samples, irrespective of the Co concentration. It is thus clear that Co doping had little effect on the position of the (002) peak. To confirm that Co2+ was substituted for Zn2+ in the wurtzite structure, optical measurements were conducted at room temperature by a UV-visible spectrometer. Three absorption peaks are apparent in the Co-doped ZnO thin films that do not appear for the undoped ZnO thin film. As the Co concentration was increased, absorption related to characteristic Co2+ transitions increased because three absorption band intensities and the area underneath the absorption wells between 500 and 700 nm increased with increasing Co concentration. The optical band gap and static dielectric constant decreased and the Urbach energy and extinction coefficient increased with increasing Co concentration.

  17. Preparation and characterization of antimicrobial Ce-doped ZnO nanoparticles for photocatalytic detoxification of cyanide

    International Nuclear Information System (INIS)

    Karunakaran, Chockalingam; Gomathisankar, Paramasivan; Manikandan, Govindasamy

    2010-01-01

    2% Ce-doped ZnO, prepared by sonochemical wet impregnation method and calcined at 500 deg. C, was characterized by XRD, EDS, XPS, SEM, FT-IR, UV-visible DRS, PL, EIS, and N 2 -adsorption and desorption isotherms. Doping reduces the intragranular resistance and recombination of the photogenerated electron-hole pairs. It also shifts the optical absorption edge to visible region. Under UV-A light or natural sunlight (950 ± 25 W m -2 ), the doped oxide effectively catalyzes the oxidation of cyanide and subsequently the cyanate also. The catalysis follows Langmuir-Hinshelwood kinetics. The solar photocatalysis depends on the area of catalyst bed and the UV photocatalysis enhances with the photon flux. The doped oxide is also an antibacterial agent and its bactericidal efficiency, tested with Escherichia coli in absence of any illumination, is larger than those of undoped oxides.

  18. Enhancement of two photon absorption with Ni doping in the dilute magnetic semiconductor ZnO crystalline nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Rana, Amit Kumar; Kumar, Yogendra; Arjunan, M.S.; Sen, Somaditya; Shirage, Parasharam M., E-mail: pmshirage@iiti.ac.in, E-mail: paras.shirage@gmail.com [Department of Physics, Indian Institute of Technology Indore, Simrol Campus, Khandwa Road, Indore 452020 (India); Centre of Materials Science and Engineering, Indian Institute of Technology Indore, Simrol Campus, Khandwa Road, Indore 452020 (India); J, Aneesh; Adarsh, K. V. [Department of Physics, Indian Institute of Science Education and Research, Bhopal 462023 (India)

    2015-12-07

    In this letter, we have investigated the third-order optical nonlinearities of high-quality Ni doped ZnO nanorods crystallized in wurtzite lattice, prepared by the wet chemical method. In our experiments, we found that the two photon absorption coefficient (β) increases by as much as 14 times, i.e., 7.6 ± 0.4 to 112 ± 6 cm/GW, when the Ni doping is increased from 0% to 10%. The substantial enhancement in β is discussed in terms of the bandgap scaling and Ni doping. Furthermore, we also show that the optical bandgap measured by UV-Vis and photoluminescence spectroscopies, continuously redshift with increasing Ni doping concentration. We envision that the strong nonlinear optical properties together with their dilute magnetic effects, they form an important class of materials for potential applications in magneto-optical and integrated optical chips.

  19. Enhancement of two photon absorption with Ni doping in the dilute magnetic semiconductor ZnO crystalline nanorods

    International Nuclear Information System (INIS)

    Rana, Amit Kumar; Kumar, Yogendra; Arjunan, M.S.; Sen, Somaditya; Shirage, Parasharam M.; J, Aneesh; Adarsh, K. V.

    2015-01-01

    In this letter, we have investigated the third-order optical nonlinearities of high-quality Ni doped ZnO nanorods crystallized in wurtzite lattice, prepared by the wet chemical method. In our experiments, we found that the two photon absorption coefficient (β) increases by as much as 14 times, i.e., 7.6 ± 0.4 to 112 ± 6 cm/GW, when the Ni doping is increased from 0% to 10%. The substantial enhancement in β is discussed in terms of the bandgap scaling and Ni doping. Furthermore, we also show that the optical bandgap measured by UV-Vis and photoluminescence spectroscopies, continuously redshift with increasing Ni doping concentration. We envision that the strong nonlinear optical properties together with their dilute magnetic effects, they form an important class of materials for potential applications in magneto-optical and integrated optical chips

  20. A Mössbauer and magnetic study of ball milled Fe-doped ZnO Powders

    Energy Technology Data Exchange (ETDEWEB)

    Zamora, Ligia E., E-mail: ligia.zamora@correounivalle.edu.co; Paz, J. C.; Piamba, J. F.; Tabares, J. A.; Alcázar, G. A. Pérez [Universidad del Valle, Departamento de física (Colombia)

    2015-06-15

    The structural and magnetic properties of Fe-doped ZnO are reported in this study, as obtained by mechanical alloying from elemental powders of ZnO and Fe. The properties of Zn{sub 0.90}Fe{sub 0.10}O samples alloying while varying the milling time (6, 12, 24 and 36 h) are also reported. The Rietveld refinement of X-ray Diffraction (XRD) patterns revealed that the system presents two structures: the würtzite structure of ZnO and the bcc structure of α-Fe. The Mössbauer spectra show that the samples present three components: a ferromagnetic component, associated with the Fe phase and two paramagnetic components, associated with the Fe atoms, which penetrate inside the ZnO matrix behaving as Fe{sup 3+} and Fe{sup 2+}. The milling time contributes to an increase in the paramagnetic sites, and a solubility limit of the Fe atoms in the ZnO lattice was detected. The VSM measurements at room temperature detected ferromagnetic behavior with a saturation magnetization of 11 emu/g and a coercive field of 330 Oe for the sample alloyed over 24 h. A similar behavior was shown by the other samples.

  1. Spectral features and antibacterial properties of Cu-doped ZnO nanoparticles prepared by sol-gel method

    Science.gov (United States)

    Alireza, Samavati; A, F. Ismail; Hadi, Nur; Z, Othaman; M, K. Mustafa

    2016-07-01

    Zn1-x Cu x O (x = 0.00, 0.01, 0.03, and 0.05) nanoparticles are synthesized via the sol-gel technique using gelatin and nitrate precursors. The impact of copper concentration on the structural, optical, and antibacterial properties of these nanoparticles is demonstrated. Powder x-ray diffraction investigations have illustrated the organized Cu doping into ZnO nanoparticles up to Cu concentration of 5% (x = 0.05). However, the peak corresponding to CuO for x = 0.01 is not distinguishable. The images of field emission scanning electron microscopy demonstrate the existence of a nearly spherical shape with a size in the range of 30-52 nm. Doping Cu creates the Cu-O-Zn on the surface and results in a decrease in the crystallite size. Photoluminescence and absorption spectra display that doping Cu causes an increment in the energy band gap. The antibacterial activities of the nanoparticles are examined against Escherichia coli (Gram negative bacteria) cultures using optical density at 600 nm and a comparison of the size of inhibition zone diameter. It is found that both pure and doped ZnO nanoparticles indicate appropriate antibacterial activity which rises with Cu doping. Project supported by the Universiti Teknologi Malaysia (UTM) (Grant No. R. J1300000.7809.4F626). Dr. Samavati is thankful to RMC for postdoctoral grants.

  2. Study of copper doping effects on structural, optical and electrical properties of sprayed ZnO thin films

    International Nuclear Information System (INIS)

    Mhamdi, A.; Mimouni, R.; Amlouk, A.; Amlouk, M.; Belgacem, S.

    2014-01-01

    Highlights: • The sprayed Cu-doped ZnO thin layers films were well crystallised in hexagonal wurtzite phase. • Nanoncrystallites on clusters were observed whose density decreases especially at 2% Cu content. • This parallel circuit R–C represents the contribution of the grain boundaries delineating the oriented columnar microcrystallites along c-axis. - Abstract: Copper-doped zinc oxide thin films (ZnO:Cu) at different percentages (1–3%) were deposited on glass substrates using a chemical spray technique. The effect of Cu concentration on the structural, morphology and optical properties of the ZnO:Cu thin films were investigated. XRD analysis revealed that all films consist of single phase ZnO and were well crystallised in würtzite phase with the crystallites preferentially oriented towards (0 0 2) direction parallel to c-axis. The Film surface was analyzed by contact atomic force microscopy (AFM) in order to understand the effect of the doping on the surface structure. Doping by copper resulted in a slight decrease in the optical band gap energy of the films and a noticeably change in optical constants. From the spectroscopy impedance analysis we investigated the frequency relaxation phenomenon and the circuit equivalent circuit of such thin layers. Finally, all results have been discussed in terms of the copper doping concentration

  3. Spectral features and antibacterial properties of Cu-doped ZnO nanoparticles prepared by sol-gel method

    International Nuclear Information System (INIS)

    Samavati, Alireza; Nur, Hadi; Othaman, Z; Ismail, A F; Mustafa, M K

    2016-01-01

    Zn 1−x Cu x O (x = 0.00, 0.01, 0.03, and 0.05) nanoparticles are synthesized via the sol-gel technique using gelatin and nitrate precursors. The impact of copper concentration on the structural, optical, and antibacterial properties of these nanoparticles is demonstrated. Powder x-ray diffraction investigations have illustrated the organized Cu doping into ZnO nanoparticles up to Cu concentration of 5% ( x = 0.05). However, the peak corresponding to CuO for x = 0.01 is not distinguishable. The images of field emission scanning electron microscopy demonstrate the existence of a nearly spherical shape with a size in the range of 30–52 nm. Doping Cu creates the Cu–O–Zn on the surface and results in a decrease in the crystallite size. Photoluminescence and absorption spectra display that doping Cu causes an increment in the energy band gap. The antibacterial activities of the nanoparticles are examined against Escherichia coli (Gram negative bacteria) cultures using optical density at 600 nm and a comparison of the size of inhibition zone diameter. It is found that both pure and doped ZnO nanoparticles indicate appropriate antibacterial activity which rises with Cu doping. (paper)

  4. Experimental study on structural, optoelectronic and room temperature sensing performance of Nickel doped ZnO based ethanol sensors

    Science.gov (United States)

    Sudha, M.; Radha, S.; Kirubaveni, S.; Kiruthika, R.; Govindaraj, R.; Santhosh, N.

    2018-04-01

    Nano crystalline undoped (1Z) Zinc Oxide (ZnO) and 5, 10 and 15 Wt. % (1ZN, 2ZN and 3ZN) of Nickel doped ZnO based sensors were fabricated using the hydrothermal approach on Fluorine doped Tin Oxide (FTO) glass substrates. X-ray diffraction (XRD) analysis proved the hexagonal Wurtzite structure of ZnO. Parametric variations in terms of dislocation density, bond length, lattice parameters and micro strain with respect to dopant concentration were analysed. The prominent variations in the crystallite size, optical band gap and Photoluminescence peak ratio of devices fabricated was observed. The Field Emission Scanning Electron Microscope (FESEM) images showed a change in diameter and density of the nanorods. The effect of the operating temperature, concentration of ethanol and the different doping levels of sensitivity, response and recovery time were investigated. It was inferred that 376% of sensitivity with a very quick response and recovery time of <5 s and 10 s respectively at 150 °C of 3ZN sensor has better performance compared to other three sensors. Also 3ZN sensor showed improved sensitivity of 114%, even at room temperature with response and recovery time of 35 s and 45 s respectively.

  5. Influence of annealing temperature on optical properties of Al doped ZnO nanoparticles via sol-gel methods

    Science.gov (United States)

    Rashid, Affa Rozana Abd; Hazwani, Tuan Nur; Mukhtar, Wan Maisarah; Taib, Nur Athirah Mohd

    2018-06-01

    Zinc oxide (ZnO) thin films have become technologically important materials due to their wide range of electrical and optical properties. The characteristics can be further adjusted by adequate doping processes. The effect of dopant concentration of Al, heating treatment and annealing in reducing atmosphere on the optical properties of the thin films is discussed. Undoped and aluminum-doped zinc oxide (AZO) thin films are prepared by the sol-gel method. Zinc acetate dihydrate, 2-methoxyethanol and monoethanolamine are used as precursor, solvent and stabilizer. In the case of AZO, aluminum nitrate nanohydrate is added to the precursor solution with an atomic percentage equal to 0 %, 1 %, 2 % and 3 % of Al. The multi thin layers are transformed into ZnO upon annealing at 450 °C and 500 °C. The optical properties such as transmittance, absorbance, band gap and refractive index of the thin films have been investigated by using UV-Visible Spectroscopy (UV-Vis). The results show that the effect of aluminium dopant concentration on the optical properties is depend on the post-heat treatment of the films. By doping with Al, the transmittance spectra in visible range increased and widen the band gap of ZnO which might due to Burstein-moss effects.

  6. Oriented Attachment Is a Major Control Mechanism To Form Nail-like Mn-Doped ZnO Nanocrystals.

    Science.gov (United States)

    Patterson, Samuel; Arora, Priyanka; Price, Paige; Dittmar, Jasper W; Das, Vijay Kumar; Pink, Maren; Stein, Barry; Morgan, David Gene; Losovyj, Yaroslav; Koczkur, Kallum M; Skrabalak, Sara E; Bronstein, Lyudmila M

    2017-12-26

    Here, we present a controlled synthesis of Mn-doped ZnO nanoparticles (NPs) with predominantly nail-like shapes, whose formation occurs via tip-to-base-oriented attachment of initially formed nanopyramids, followed by leveling of sharp edges that lead to smooth single-crystalline "nails". This shape is prevalent in noncoordinating solvents such as octadecene and octadecane. Yet, the double bond in the former promotes oriented attachment. By contrast, Mn-doped ZnO NP synthesis in a weakly coordinating solvent, benzyl ether, results in dendritic structures because of random attachment of initial NPs. Mn-doped ZnO NPs possess a hexagonal wurtzite structure, and in the majority of cases, the NP surface is enriched with Mn, indicating a migration of Mn 2+ ions to the NP surface during the NP formation. When the NP formation is carried out without the addition of octadecyl alcohol, which serves as a surfactant and a reaction initiator, large, concave pyramid dimers are formed whose attachment takes place via basal planes. UV-vis and photoluminescence spectra of these NPs confirm the utility of controlling the NP shape to tune electro-optical properties.

  7. High energy electron irradiation effects on Ga-doped ZnO thin films for optoelectronic space applications

    Science.gov (United States)

    Serrao, Felcy Jyothi; Sandeep, K. M.; Bhat, Shreesha; Dharmaprakash, S. M.

    2018-03-01

    Gallium-doped ZnO (GZO) thin films of thickness 394 nm were prepared by a simple, cost-effective sol-gel spin coating method. The effect of 8 MeV electron beam irradiation with different irradiation doses ranging from 0 to 10 kGy on the structural, optical and electrical properties was investigated. Electron irradiation influences the changes in the structural properties and surface morphology of GZO thin films. X-ray diffraction analysis showed that the polycrystalline nature of the GZO films is unaffected by the high energy electron irradiation. The grain size and the surface roughness were found maximum for the GZO film irradiated with 10 kGy electron dosage. The average transmittance of GZO thin films decreased after electron irradiation. The optical band gap of Ga-doped ZnO films was decreased with the increase in the electron dosage. The electrical resistivity of GZO films decreased from 4.83 × 10-3 to 8.725 × 10-4 Ω cm, when the electron dosage was increased from 0 to 10 kGy. The variation in the optical and electrical properties in the Ga-doped ZnO thin films due to electron beam irradiation in the present study is useful in deciding their compatibility in optoelectronic device applications in electron radiation environment.

  8. Nonequilibrium-Plasma-Synthesized ZnO Nanocrystals with Plasmon Resonance Tunable via Al Doping and Quantum Confinement.

    Science.gov (United States)

    Greenberg, Benjamin L; Ganguly, Shreyashi; Held, Jacob T; Kramer, Nicolaas J; Mkhoyan, K Andre; Aydil, Eray S; Kortshagen, Uwe R

    2015-12-09

    Metal oxide semiconductor nanocrystals (NCs) exhibit localized surface plasmon resonances (LSPRs) tunable within the infrared (IR) region of the electromagnetic spectrum by vacancy or impurity doping. Although a variety of these NCs have been produced using colloidal synthesis methods, incorporation and activation of dopants in the liquid phase has often been challenging. Herein, using Al-doped ZnO (AZO) NCs as an example, we demonstrate the potential of nonthermal plasma synthesis as an alternative strategy for the production of doped metal oxide NCs. Exploiting unique, thoroughly nonequilibrium synthesis conditions, we obtain NCs in which dopants are not segregated to the NC surfaces and local doping levels are high near the NC centers. Thus, we achieve overall doping levels as high as 2 × 10(20) cm(-3) in NCs with diameters ranging from 12.6 to 3.6 nm, and for the first time experimentally demonstrate a clear quantum confinement blue shift of the LSPR energy in vacancy- and impurity-doped semiconductor NCs. We propose that doping of central cores and heavy doping of small NCs are achievable via nonthermal plasma synthesis, because chemical potential differences between dopant and host atoms-which hinder dopant incorporation in colloidal synthesis-are irrelevant when NC nucleation and growth proceed via irreversible interactions among highly reactive gas-phase ions and radicals and ligand-free NC surfaces. We explore how the distinctive nucleation and growth kinetics occurring in the plasma influences dopant distribution and activation, defect structure, and impurity phase formation.

  9. Nanocrystalline Cobalt-doped SnO2 Thin Film: A Sensitive Cigarette Smoke Sensor

    Directory of Open Access Journals (Sweden)

    Patil Shriram B.

    2011-11-01

    Full Text Available This article discusses a sensitive cigarette smoke sensor based on Cobalt doped Tin oxide (Co-SnO2 thin films deposited on glass substrate by a conventional Spray Pyrolysis technique. The Co-SnO2 thin films have been characterized by X-ray Diffraction (XRD, Scanning Electron Microscopy (SEM and Energy Dispersive X-ray Spectroscopy (EDAX. The XRD spectrum shows polycrystalline nature of the film with a mixed phase comprising of SnO2 and Co3O4. The SEM image depicts uniform granular morphology covering total substrate surface. The compositional analysis derived using EDAX confirmed presence of Co in addition to Sn and O in the film. Cigarette smoke sensing characteristics of the Co-SnO2 thin film have been studied under atmospheric condition at different temperatures and smoke concentration levels. The sensing parameters such as sensitivity, response time and recovery time are observed to be temperature dependent, exhibiting better results at 330 oC.

  10. Highly transparent and conductive Sn/F and Al co-doped ZnO thin films prepared by sol–gel method

    International Nuclear Information System (INIS)

    Pan, Zhanchang; Luo, Junming; Tian, Xinlong; Wu, Shoukun; Chen, Chun;