WorldWideScience

Sample records for coated magnetite nanoparticles

  1. Sonochemical coating of magnetite nanoparticles with silica.

    Science.gov (United States)

    Dang, Feng; Enomoto, Naoya; Hojo, Junichi; Enpuku, Keiji

    2010-01-01

    Magnetite nanoparticles were coated with silica through the hydrolysis and condensation of tetraethyl orthosilicate (TEOS) under ultrasonic irradiation. The ultrasonic irradiation was used to prevent the agglomeration of the magnetite particles and accelerate the hydrolysis and condensation of TEOS. TEM, DLS, XRF, VSM, TG and sedimentation test were used to characterize the silica-coated magnetite particles. The dispersibility of silica-coated magnetite particles in aqueous solution was improved significantly and the agglomerate particle size was decreased to 110 nm. It was found that the agglomerate particle size of silica-coated magnetite particles was mainly decided by the coating temperature and the pH value in the silica-coating process. The weight ratio of silica in silica-coated magnetite particles was mainly decided by the pH value in the silica-coating process. The dispersibility of silica-coated magnetite particles was mainly decided by the agglomerate particle size of the suspension. The oxidation of magnetite particles in air was limited through the coated silica. The magnetism of silica-coated magnetite particles decreased slightly after silica-coating.

  2. Cellular interactions of lauric acid and dextran-coated magnetite nanoparticles

    International Nuclear Information System (INIS)

    Pradhan, Pallab; Giri, Jyotsnendu; Banerjee, Rinti; Bellare, Jayesh; Bahadur, Dhirendra

    2007-01-01

    In vitro cytocompatibility and cellular interactions of lauric acid and dextran-coated magnetite nanoparticles were evaluated with two different cell lines (mouse fibroblast and human cervical carcinoma). Lauric acid-coated magnetite nanoparticles were less cytocompatible than dextran-coated magnetite nanoparticles and cellular uptake of lauric acid-coated magnetic nanoparticles was more than that of dextran-coated magnetite nanoparticles. Lesser cytocompatibility and higher uptake of lauric acid-coated magnetite nanoparticles as compared to dextran-coated magnetic nanoparticles may be due to different cellular interactions by coating material. Thus, coating plays an important role in modulation of biocompatibility and cellular interaction of magnetic nanoparticles

  3. Synthesis and characterization of magnetite nanoparticles coated with lauric acid

    Energy Technology Data Exchange (ETDEWEB)

    Mamani, J.B., E-mail: javierbm@einstein.br [Instituto do Cérebro-InCe, Hospital Israelita Albert Einstein-HIAE, 05651-901 São Paulo (Brazil); Costa-Filho, A.J. [Faculdade de Filosofia, Ciências e Letras de Ribeirão Preto, Universidade de São Paulo, Ribeirão Preto (Brazil); Cornejo, D.R. [Instituto de Física Universidade de São Paulo, USP, São Paulo (Brazil); Vieira, E.D. [Instituto de Física, Universidade Federal de Goiás, Goiânia (Brazil); Gamarra, L.F. [Instituto do Cérebro-InCe, Hospital Israelita Albert Einstein-HIAE, 05651-901 São Paulo (Brazil)

    2013-07-15

    Understanding the process of synthesis of magnetic nanoparticles is important for its implementation in in vitro and in vivo studies. In this work we report the synthesis of magnetic nanoparticles made from ferrous oxide through coprecipitation chemical process. The nanostructured material was coated with lauric acid and dispersed in aqueous medium containing surfactant that yielded a stable colloidal suspension. The characterization of magnetic nanoparticles with distinct physico-chemical configurations is fundamental for biomedical applications. Therefore magnetic nanoparticles were characterized in terms of their morphology by means of TEM and DLS, which showed a polydispersed set of spherical nanoparticles (average diameter of ca. 9 nm) as a result of the protocol. The structural properties were characterized by using X-ray diffraction (XRD). XRD pattern showed the presence of peaks corresponding to the spinel phase of magnetite (Fe{sub 3}O{sub 4}). The relaxivities r{sub 2} and r{sub 2}* values were determined from the transverse relaxation times T{sub 2} and T{sub 2}* at 3 T. Magnetic characterization was performed using SQUID and FMR, which evidenced the superparamagnetic properties of the nanoparticles. Thermal characterization using DSC showed exothermic events associated with the oxidation of magnetite to maghemite. - Highlights: • Synthesis of magnetic nanoparticles coated with lauric acid • Characterization of magnetic nanoparticles • Morphological, structural, magnetic, calorimetric and relaxometric characterization.

  4. Development of Antibody-Coated Magnetite Nanoparticles for Biomarker Immobilization

    Directory of Open Access Journals (Sweden)

    Christian Chapa Gonzalez

    2014-01-01

    Full Text Available Magnetic nanoparticles (MNPs have great potential in biomedical applications because of their magnetic response offers the possibility to direct them to specific areas and target biological entities. Magnetic separation of biomolecules is one of the most important applications of MNPs because their versatility in detecting cancer biomarkers. However, the effectiveness of this method depends on many factors, including the type of functionalization onto MNPs. Therefore, in this study, magnetite nanoparticles have been developed in order to separate the 5′-nucleotidase enzyme (5eNT. The 5eNT is used as a bio-indicator for diagnosing diseases such as hepatic ischaemia, liver tumor, and hepatotoxic drugs damage. Magnetic nanoparticles were covered in a core/shell type with silica, aminosilane, and a double shell of silica-aminosilane. A ScFv (fragment antibody and anti-CD73 antibody were attached to the coated nanoparticles in order to separate the enzyme. The magnetic separation of this enzyme with fragment antibody was found to be 28% higher than anti-CD73 antibody and the enzyme adsorption was improved with the double shell due to the increased length of the polymeric chain. Magnetite nanoparticles with a double shell (silica-aminosilane were also found to be more sensitive than magnetite with a single shell in the detection of biomarkers.

  5. Investigation of interactions between dendrimer-coated magnetite nanoparticles and bovine serum albumin

    International Nuclear Information System (INIS)

    Pan Bifeng; Gao Feng; Ao Limei

    2005-01-01

    We investigated the interactions between dendrimer-coated magnetite nanoparticles (MNPs) and the protein serum albumin. The investigation was based on the fluorescence quenching of tryptophan residue of serum albumin after binding with the dendrimer-coated magnetite nanoparticles. The extent of the interactions between bovine serum albumin and dendrimer-coated MNPs strongly depends on their surface groups and pH value

  6. Preparation and characterization of (3-aminopropyl)triethoxysilane-coated magnetite nanoparticles

    International Nuclear Information System (INIS)

    Yamaura, M.; Camilo, R.L.; Sampaio, L.C.; Macedo, M.A.; Nakamura, M.; Toma, H.E.

    2004-01-01

    Magnetite nanoparticles coated with (3-aminopropyl)triethoxysilane, NH 2 (CH 2 ) 3 Si(OC 2 H 5 ) 3 , were prepared by silanization reaction and characterized by X-ray diffractometry, transmission electron microscopy, atomic force microscopy, Fourier transform infrared spectroscopy and magnetization measurements. Both uncoated and organosilane-coated magnetite exhibited superparamagnetic behavior and strong magnetization at room temperature. Basic groups anchored on the external surface of the coated magnetite were observed. The superparamagnetic particles of coated magnetite are able to bind to biological molecules, drugs and metals and in this way remove them from medium by magnetic separation procedures

  7. Fabrication of magnetite-based core–shell coated nanoparticles with antibacterial properties

    International Nuclear Information System (INIS)

    Grumezescu, A M; Ficai, A; Vasile, O R; Cristescu, R; Dorcioman, G; Socol, G; Mihailescu, I N; Chifiriuc, M C; Mihaiescu, D E; Enculescu, M; Chrisey, D B

    2015-01-01

    We report the fabrication of biofunctionalized magnetite core/sodium lauryl sulfate shell/antibiotic adsorption-shell nanoparticles assembled thin coatings by matrix assisted pulsed laser evaporation for antibacterial drug-targeted delivery. Magnetite nanoparticles have been synthesized and subsequently characterized by transmission electron microscopy and x-ray diffraction. The obtained thin coatings have been investigated by FTIR and scanning electron microscope, and tested by in vitro biological assays, for their influence on in vitro bacterial biofilm development and cytotoxicity on human epidermoid carcinoma (HEp2) cells. (paper)

  8. Magnetite nanoparticles coated glass wool for As(V) removal from drinking water

    Energy Technology Data Exchange (ETDEWEB)

    Kango, Sarita; Kumar, Rajesh, E-mail: rajesh.kumar@juit.ac.in [Department of Physics and Materials Science, Jaypee University of Information Technology, Waknaghat, District Solan (H.P.)- 173 234 (India)

    2015-08-28

    Arsenic (As) removal from contaminated groundwater is a key environmental concern worldwide. In this study, glass wool was coated with magnetite nanoparticles under argon gas flow and magnetite coated glass wool have been investigated for application as an adsorbent for As(V) removal from water. The adsorbent was characterized by using Scanning Electron Microscopy (SEM) and arsenic contaminated water treated with adsorbent was analyzed by Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). The ICP-MS results showed that 10 g/L of adsorbent removed 99.4% of As(V) within 5 hours at pH-7 and initial arsenic concentration of 360µg/L. Adsorption kinetics data fitted well in pseudo-first-order kinetics model with high correlation coefficient (R{sup 2} = 0.995). As magnetite nanoparticles coated glass wool showed favorable adsorption behavior for As(V), it can be a promising tool for water purification.

  9. Magnetite nanoparticles coated glass wool for As(V) removal from drinking water

    International Nuclear Information System (INIS)

    Kango, Sarita; Kumar, Rajesh

    2015-01-01

    Arsenic (As) removal from contaminated groundwater is a key environmental concern worldwide. In this study, glass wool was coated with magnetite nanoparticles under argon gas flow and magnetite coated glass wool have been investigated for application as an adsorbent for As(V) removal from water. The adsorbent was characterized by using Scanning Electron Microscopy (SEM) and arsenic contaminated water treated with adsorbent was analyzed by Inductively Coupled Plasma Mass Spectroscopy (ICP-MS). The ICP-MS results showed that 10 g/L of adsorbent removed 99.4% of As(V) within 5 hours at pH-7 and initial arsenic concentration of 360µg/L. Adsorption kinetics data fitted well in pseudo-first-order kinetics model with high correlation coefficient (R 2 = 0.995). As magnetite nanoparticles coated glass wool showed favorable adsorption behavior for As(V), it can be a promising tool for water purification

  10. Hybrid Organometallic-Inorganic Nanomaterial: Acetyl Ferrocene Schiff base Immobilized on Silica Coated Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    M. Masteri-Farahani

    2015-10-01

    Full Text Available In  this  work,  a  new  hybrid  organometallic-inorganic  hybrid nanomaterial was prepared by immobilization of acetyl ferrocene on the  surface  of magnetite  nanoparticles. Covalent  grafting of silica coated magnetite nanoparticles (SCMNPs with 3-aminopropyl triethoxysilane gave aminopropyl-modified magnetite nanoparticles (AmpSCMNPs. Then, Schiff base condensation  of AmpSCMNPs with acetyl  ferrocene resulted in the preparation of acferro-SCMNPs hybrid nanomaterial. Characterization of the prepared nanomaterial was performed with different physicochemical methods such as Fourier transform infrared spectroscopy (FT-IR, X-ray diffraction (XRD, vibrating sample magnetometry (VSM, thermogravimetric analysis (TGA, scanning electron microscopy (SEM, and transmission electron microscopy (TEM. VSM analysis showed superparamagnetic properties of the prepared nanomaterial and TEM and SEM analyses indicated the relatively spherical nanoparticles with 15 nm average size.

  11. pH-responsive poly(aspartic acid) hydrogel-coated magnetite nanoparticles for biomedical applications.

    Science.gov (United States)

    Vega-Chacón, Jaime; Arbeláez, María Isabel Amaya; Jorge, Janaina Habib; Marques, Rodrigo Fernando C; Jafelicci, Miguel

    2017-08-01

    A novel multifunctional nanosystem formed by magnetite nanoparticles coated with pH-responsive poly(aspartic acid) hydrogel was developed. Magnetite nanoparticles (Fe 3 O 4 ) have been intensively investigated for biomedical applications due to their magnetic properties and dimensions similar to the biostructures. Poly(aspartic acid) is a water-soluble, biodegradable and biocompatible polymer, which features makes it a potential candidate for biomedical applications. The nanoparticles surface modification was carried out by crosslinking polysuccinimide on the magnetite nanoparticles surface and hydrolyzing the succinimide units in mild alkaline medium to obtain the magnetic poly(aspartic acid) hydrogel. The surface modification in each step was confirmed by DRIFTS, TEM and zeta potential measurements. The hydrodynamic diameter of the nanosystems decreases as the pH value decreases. The nanosystems showed high colloidal stability in water and no cytotoxicity was detected, which make these nanosystems suitable for biomedical applications. Copyright © 2017 Elsevier B.V. All rights reserved.

  12. Effects of AC magnetic field and carboxymethyldextran-coated magnetite nanoparticles on mice peritoneal cells

    International Nuclear Information System (INIS)

    Araujo Guedes, Maria Helena; Sadeghiani, Neda; Lima Guedes Peixoto, Danielle; Poubel Coelho, Julia; Santos Barbosa, Luzirlane; Bentes Azevedo, Ricardo; Kueckelhaus, Selma; Silva, Maria de Fatima da; Morais, Paulo Cesar; Guerrero Marques Lacava, Zulmira

    2005-01-01

    A portable apparatus was developed to perform magnetohyperthermia (MHT) assays. In order to investigate its efficiency on cell lysis, biological effects of the AC magnetic field exposure after carboxymethyldextran-coated magnetite-nanoparticles (CMDC) treatment were investigated. Phagocyte capacity, cell viability, and morphology data evidenced that the CMDC sample and the apparatus are useful to further investigate MHT in cancer therapy

  13. Stability of magnetite nanoparticles with different coatings in a simulated blood plasma

    Energy Technology Data Exchange (ETDEWEB)

    Favela-Camacho, Sarai E.; Pérez-Robles, J. Francisco [Center for Research and Advanced Studies of National Polytechnic Institute, CINVESTAV-Querétaro Unit (Mexico); García-Casillas, Perla E. [Autonomous University of Juarez, Department of Materials Science, Institute of Engineering and Technology (Mexico); Godinez-Garcia, Andrés, E-mail: andgodinez@xanum.uam.mx [Universidad Autónoma Metropolitana, Departamento de Ingeniería de Procesos e Hidráulica (Mexico)

    2016-07-15

    Magnetite nanoparticles (MNPs) have demonstrated to be a potential platform for simultaneous anticancer drug delivery and magnetic resonance imaging (MRI). However, magnetite is unstable at the blood plasma conditions. Therefore, to study their stability in a broad range of particle size, the MNPs were synthesized using two methods, the fast injection co-precipitation method (FIC) and the reflux co-precipitation method (RC). The MNPs obtained by the RC and the FIC methods have an average size of agglomerates of 200 and 45 nm respectively. They were dispersed using sodium citrate as surfactant and were coated with silica and chitosan. A total of four kind of coated MNPs were synthesized: magnetite/sodium citrate, magnetite/silica, magnetite/sodium citrate/silica and magnetite/sodium citrate/silica/chitosan. Different samples of the coated MNPs were immersed in a simulated blood plasma solution (Phosphate-Buffered Saline, PBS, Gibco{sup ®}), for periods of 24, 48 and 72 h. Inductively coupled plasma (ICP) technique was used to analyze the composition of the simulated plasma after those periods of time. The obtained results suggest that the uncoated samples showed an appreciable weight loss, and the iron composition in the simulated plasma increased. This last means that the used coatings avoid iron dissolution from the MNPs.Graphical abstract.

  14. Magnetite Nanoparticles Coated with Rifampicin and Chlortetracycline for Drug Delivery Applications

    International Nuclear Information System (INIS)

    Nadejde, Claudia; Ciurlica, Ecaterina Foca-nici; Creanga, Dorina; Carlescu, Aurelian; Badescu, Vasile

    2010-01-01

    Four types of biocompatible magnetic fluids based on superparamagnetic nanoparticles with Fe 3 O 4 cores were functionalized with antibiotics (rifampicin or chlortetracycline) as potential candidates for in vivo biomedical applications, such as magnetically controlled drug delivery. The synthesis consisted in coprecipitation of iron oxide in basic, as well as in acid medium, followed by the dispersion of the resulted magnetite nanoparticles in aqueous solution containing the antibiotic. The chosen method to prepare the magnetite-core/drug-shell systems avoided intermediate organic coating of the magnetic nanoparticles. Comparative analysis of the rheological features of the aqueous magnetic fluid samples was performed. The structural features of the coated magnetic particles were investigated by X-Ray Diffraction (XRD), Transmission Electron Microscopy (TEM) and Vibrating Sample Magnetometry (VSM). Good crystallinity and adequate stability in time were evidenced. Drug delivery curves were spectrophotometrically provided.

  15. Simultaneous hyperthermia and doxorubicin delivery from polymer-coated magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Iglesias, G.R., E-mail: iglesias@ugr.es [Department of Applied Physics, University of Granada, Granada 18071 (Spain); Delgado, A.V.; González-Caballero, F. [Department of Applied Physics, University of Granada, Granada 18071 (Spain); Ramos-Tejada, M.M. [Department of Physics, University of Jaén, Linares 23700 (Spain)

    2017-06-01

    In this work, the hyperthermia response, (i.e., heating induced by an externally applied alternating magnetic field) and the simultaneous release of an anti-cancer drug (doxorubicin) by polymer-coated magnetite nanoparticles have been investigated. After describing the setup for hyperthermia measurements in suspensions of magnetic nanoparticles, the hyperthermia (represented by the rate of suspension heating and, ultimately, by the specific absorption rate or SAR) of magnetite nanoparticles (both bare and polymer-coated as drug nanocarriers) is discussed. The effect of the applied ac magnetic field on doxorubicin release is also studied, and it is concluded that the field does not interfere with the release process, demonstrating the double functionality of the investigated particles. - Highlights: • Magnetite NPs coated with polymers are used for drug delivery and hyperthermia. • The SAR of polyelectrolyte-coated NPs is larger because of their improved stability. • The antitumor drug doxorubicin is adsorbed on the coated particles. • The release rate of the drug is not affected by the ac magnetic field used in hyperthermia.

  16. Silica coated magnetite nanoparticles for removal of heavy metal ions from polluted waters

    CERN Document Server

    Dash, Monika

    2013-01-01

    Magnetic removal of Hg2+ and other heavy metal ions like Cd2+, Pb2+ etc. using silica coated magnetite particles from polluted waters is a current topic of active research to provide efficient water recycling and long term high quality water. The technique used to study the bonding characteristics of such kind of nanoparticles with the heavy metal ions is a very sensitive hyperfine specroscopy technique called the perturbed angular correlation technique (PAC).

  17. Preparation and characterization of chondroitin‐sulfate‐A‐coated magnetite nanoparticles for biomedical applications

    International Nuclear Information System (INIS)

    Tóth, Ildikó Y.; Illés, Erzsébet; Szekeres, Márta; Tombácz, Etelka

    2015-01-01

    Polysaccharides are promising candidates for manufacturing biocompatible core–shell nanoparticles with potential in vivo use. Superparamagnetic magnetite nanoparticles (MNPs) have prospective application in both diagnosis and therapy, and so developing a novel polysaccharide shell on MNP core is of great challenge. MNPs were prepared by co-precipitation, then the surface of purified MNPs was coated with chondroitin-sulfate-A (CSA) to obtain core–shell structured magnetite nanoparticles (CSA@MNP). The effect of the added amount of CSA on the surface charging and the aggregation state of MNPs at various pHs and 10 mM NaCl was measured by electrophoresis and dynamic light scattering. The amphoteric behavior of MNPs was fundamentally modified by adsorption of CSA polyanions. A very low CSA-loading induces the aggregation of MNPs, while four times more stabilizes the dispersions over the whole pH-range studied. The coagulation kinetics experiments measured at pH=6.3±0.3 showed that salt tolerance of CSA@MNPs rises up to ~150 mM NaCl. - Highlights: • Novel CSA-coated core–shell magnetite nanoparticles were prepared successfully. • The aggregation range of MNPs was shifted gradually to the lower pHs by CSA-loading. • CSA stabilizes electrosterically the MNPs over wide pH-range relevant to biosystems. • The salt tolerance of CSA@MNP enables them to use under physiological condition

  18. Preparation and characterization of chondroitin‐sulfate‐A‐coated magnetite nanoparticles for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Tóth, Ildikó Y., E-mail: Ildiko.Toth@chem.u-szeged.hu; Illés, Erzsébet; Szekeres, Márta; Tombácz, Etelka, E-mail: tombacz@chem.u-szeged.hu

    2015-04-15

    Polysaccharides are promising candidates for manufacturing biocompatible core–shell nanoparticles with potential in vivo use. Superparamagnetic magnetite nanoparticles (MNPs) have prospective application in both diagnosis and therapy, and so developing a novel polysaccharide shell on MNP core is of great challenge. MNPs were prepared by co-precipitation, then the surface of purified MNPs was coated with chondroitin-sulfate-A (CSA) to obtain core–shell structured magnetite nanoparticles (CSA@MNP). The effect of the added amount of CSA on the surface charging and the aggregation state of MNPs at various pHs and 10 mM NaCl was measured by electrophoresis and dynamic light scattering. The amphoteric behavior of MNPs was fundamentally modified by adsorption of CSA polyanions. A very low CSA-loading induces the aggregation of MNPs, while four times more stabilizes the dispersions over the whole pH-range studied. The coagulation kinetics experiments measured at pH=6.3±0.3 showed that salt tolerance of CSA@MNPs rises up to ~150 mM NaCl. - Highlights: • Novel CSA-coated core–shell magnetite nanoparticles were prepared successfully. • The aggregation range of MNPs was shifted gradually to the lower pHs by CSA-loading. • CSA stabilizes electrosterically the MNPs over wide pH-range relevant to biosystems. • The salt tolerance of CSA@MNP enables them to use under physiological condition.

  19. Optimal size for heating efficiency of superparamagnetic dextran-coated magnetite nanoparticles for application in magnetic fluid hyperthermia

    Science.gov (United States)

    Shaterabadi, Zhila; Nabiyouni, Gholamreza; Soleymani, Meysam

    2018-06-01

    Dextran-coated magnetite (Fe3O4) nanoparticles with average particle sizes of 4 and 19 nm were synthesized through in situ and semi-two-step co-precipitation methods, respectively. The experimental results confirm the formation of pure phase of magnetite as well as the presence of dextran layer on the surface of modified magnetite nanoparticles. The results also reveal that both samples have the superparamagnetic behavior. Furthermore, calorimetric measurements show that the dextran-coated Fe3O4 nanoparticles with an average size of 4 nm cannot produce any appreciable heat under a biologically safe alternating magnetic field used in hyperthermia therapy; whereas, the larger ones (average size of 19 nm) are able to increase the temperature of their surrounding medium up to above therapeutic range. In addition, measured specific absorption rate (SAR) values confirm that magnetite nanoparticles with an average size of 19 nm are very excellent candidates for application in magnetic hyperthermia therapy.

  20. Poly(n-isopropylacrylamide)-based hydrogel coatings on magnetite nanoparticles via atom transfer radical polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Frimpong, Reynolds A; Hilt, J Zach [Department of Chemical and Materials Engineering, University of Kentucky, Lexington, KY 40506 (United States)], E-mail: hilt@engr.uky.edu

    2008-04-30

    Core magnetite (Fe{sub 3}O{sub 4}) nanoparticles have been functionalized with a model intelligent hydrogel system based on the temperature responsive polymer poly(n-isopropyl acrylamide) (PNIPAAm) to obtain magnetically responsive core-shell nanocomposites. Fe{sub 3}O{sub 4} nanoparticles were obtained from a one-pot co-precipitation method which provided either oleic acid (hydrophobic) or citric acid (hydrophilic) coated nanoparticles. Subsequent ligand exchange of these coatings with various bromine alkyl halides and a bromo silane provided initiating sites for functionalization with NIPAAm using atom transfer radical polymerization (ATRP). The bromine alkyl halides that were used were 2-bromo-2-methyl propionic acid (BMPA) and 2-bromopropionyl bromide (BPB). The bromo silane that was used was 3-bromopropyl trimethoxysilane (BPTS). The intelligent polymeric shell consists of NIPAAm crosslinked with poly(ethylene glycol) 400 dimethacrylate (PEG400DMA). Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), and transmission electron microscopy (TEM) were used to confirm the presence of the polymeric shell. Dynamic light scattering (DLS) was used to characterize the nanocomposites for particle size changes with temperature. Their magnetic and temperature responsiveness show great promise for further biomedical applications. This platform for functionalizing magnetic nanoparticles with intelligent hydrogels promises to impact a wide range of medical and biological applications of magnetic nanoparticles.

  1. Poly(n-isopropylacrylamide)-based hydrogel coatings on magnetite nanoparticles via atom transfer radical polymerization

    International Nuclear Information System (INIS)

    Frimpong, Reynolds A; Hilt, J Zach

    2008-01-01

    Core magnetite (Fe 3 O 4 ) nanoparticles have been functionalized with a model intelligent hydrogel system based on the temperature responsive polymer poly(n-isopropyl acrylamide) (PNIPAAm) to obtain magnetically responsive core-shell nanocomposites. Fe 3 O 4 nanoparticles were obtained from a one-pot co-precipitation method which provided either oleic acid (hydrophobic) or citric acid (hydrophilic) coated nanoparticles. Subsequent ligand exchange of these coatings with various bromine alkyl halides and a bromo silane provided initiating sites for functionalization with NIPAAm using atom transfer radical polymerization (ATRP). The bromine alkyl halides that were used were 2-bromo-2-methyl propionic acid (BMPA) and 2-bromopropionyl bromide (BPB). The bromo silane that was used was 3-bromopropyl trimethoxysilane (BPTS). The intelligent polymeric shell consists of NIPAAm crosslinked with poly(ethylene glycol) 400 dimethacrylate (PEG400DMA). Fourier transform infrared (FTIR) spectroscopy, thermogravimetric analysis (TGA), and transmission electron microscopy (TEM) were used to confirm the presence of the polymeric shell. Dynamic light scattering (DLS) was used to characterize the nanocomposites for particle size changes with temperature. Their magnetic and temperature responsiveness show great promise for further biomedical applications. This platform for functionalizing magnetic nanoparticles with intelligent hydrogels promises to impact a wide range of medical and biological applications of magnetic nanoparticles

  2. Preparation and characterization of chondroitin-sulfate-A-coated magnetite nanoparticles for biomedical applications

    Science.gov (United States)

    Tóth, Ildikó Y.; Illés, Erzsébet; Szekeres, Márta; Tombácz, Etelka

    2015-04-01

    Polysaccharides are promising candidates for manufacturing biocompatible core-shell nanoparticles with potential in vivo use. Superparamagnetic magnetite nanoparticles (MNPs) have prospective application in both diagnosis and therapy, and so developing a novel polysaccharide shell on MNP core is of great challenge. MNPs were prepared by co-precipitation, then the surface of purified MNPs was coated with chondroitin-sulfate-A (CSA) to obtain core-shell structured magnetite nanoparticles (CSA@MNP). The effect of the added amount of CSA on the surface charging and the aggregation state of MNPs at various pHs and 10 mM NaCl was measured by electrophoresis and dynamic light scattering. The amphoteric behavior of MNPs was fundamentally modified by adsorption of CSA polyanions. A very low CSA-loading induces the aggregation of MNPs, while four times more stabilizes the dispersions over the whole pH-range studied. The coagulation kinetics experiments measured at pH=6.3±0.3 showed that salt tolerance of CSA@MNPs rises up to ~150 mM NaCl.

  3. Chitosan-coated magnetite nanoparticles as adsorbent for the removal of molybdenum ions

    International Nuclear Information System (INIS)

    Sousa, Jose S.; Egute, Nayara S.; Yamaura, Mitiko; Freitas, Antonio A.; Holland, Helber; Lugao, Ademar B.

    2011-01-01

    Metal ions in wastewater, even at low concentrations, affect a large number of organisms due to their high degree of toxicity. Research has developed some alternative methods for metal removal from the wastewater, as adsorption using a bio sorbent of combined chitosan with magnetic particles. Chitosan is a natural bio polymer, which has a highly reactive active sites in its structure, composed of amino and hydroxyl groups with affinity to bind to metal ions. In this study, magnetic nanoparticles of coated magnetite with chitosan as an adsorbent of molybdenum(Vi) ions in aqueous medium was investigated. The adsorption experiments were performed varying the time contact from 5 to 150 min, the p H from 0.5 to 11 and the molybdenum concentrations in nitric solutions. All molybdenum analyses were carried out by gamma spectroscopy using a Hp Ge detector and 99 Mo as radioactive tracer. Results showed that the chitosan-coated magnetite particles are good adsorbent for Mo ions from aqueous medium in the range of p H from 0.5 to 9 with a removal higher than 99%. Among the studied isotherm models, the Freundlich model fitted best the equilibrium adsorption isotherm of Mo(VI) ions. (author)

  4. Facile Synthesis Polyethylene Glycol Coated Magnetite Nanoparticles for High Colloidal Stability

    Directory of Open Access Journals (Sweden)

    Mun Foong Tai

    2016-01-01

    Full Text Available Polyethylene glycol (PEG is one of the most frequently used synthetic polymers for surface modifications of magnetite nanoparticles (MNPs to provide a new opportunity for constructing high colloidal stability. Herein, a facile in situ coprecipitation technique is described for the synthesis of PEG coated MNPs using ammonium hydroxide as the precipitating agent. The structure and morphology of the prepared PEG coated MNPs samples were characterized by Fourier transform infrared (FTIR spectroscopy, X-ray spectroscopy, thermogravimetric analysis (TGA, and the high resolution transmission electron microscopy (HRTEM. In this study, all samples demonstrated hydrodynamic size in the range of 32 to 43 nm with narrow size distribution. In addition, the magnetic properties of resultant samples were investigated using a vibrating sample magnetometer (VSM to reveal the superparamagnetic behaviour with saturation magnetization. The saturation magnetization of PEG coated MNPs samples was in the range of 63 to 66 emu/g at 300 K. Interestingly, it was found that 1.0 g of PEG coated MNPs exhibited high colloidal stability in a basic solution (pH = 10 and nitrile (NBR latex up to 21 days as compared to the unmodified MNPs during the sedimentation test.

  5. Tailoring the properties of magnetite nanoparticles clusters by coating with double inorganic layers

    Energy Technology Data Exchange (ETDEWEB)

    Petran, Anca [National Institute for Research and Development of Isotopic and Molecular Technologies, 67-103 Donat Str., 400293 Cluj-Napoca (Romania); Radu, Teodora, E-mail: teodora.radu@itim-cj.ro [National Institute for Research and Development of Isotopic and Molecular Technologies, 67-103 Donat Str., 400293 Cluj-Napoca (Romania); Culic, Bogdan [Faculty of Dental Medicine,Iuliu Hatieganu University of Medicine and Pharmacy, 32 Clinicilor Str., 400006 Cluj-Napoca (Romania); Turcu, Rodica, E-mail: rodica.turcu@itim-cj.ro [National Institute for Research and Development of Isotopic and Molecular Technologies, 67-103 Donat Str., 400293 Cluj-Napoca (Romania)

    2016-12-30

    Highlights: • New magnetite clusters covered with inorganic oxides double layers. • Coating layers influence on the surface properties of the magnetic clusters. • Color parameters assessment for the inorganic oxides coated magnetic clusters. • High magnetization clusters with appropiate color for magnetic security paper. - Abstract: New magnetic nanoparticles based on Fe{sub 3}O{sub 4} clusters covered with a double layer of inorganic salts/oxides with high magnetization for incorporation in security materials such as security paper were synthesized. For the inorganic layers ZnO, SiO{sub 2} and BaSO{sub 4} were used. The microstructure and composition of the products were determined by scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray photoelectron spectroscopy (XPS). Magnetization measurements on the obtained samples show a straightforward correlation between the saturation magnetization (M{sub s}) and morphology of the samples. The results obtained from color parameter assessment are discussed in relation with the morphology and microstructure of the prepared samples.

  6. Synthesis of magnetite nanoparticles from mineral waste

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Rohit [CSIR – Institute of Minerals and Materials Technology, Bhubaneswar 751 013 (India); Sakthivel, R., E-mail: velsak_r@yahoo.com [CSIR – Institute of Minerals and Materials Technology, Bhubaneswar 751 013 (India); Behura, Reshma; Mishra, B.K. [CSIR – Institute of Minerals and Materials Technology, Bhubaneswar 751 013 (India); Das, D. [UGC-DAE Consortium, Kolkata (India)

    2015-10-05

    Highlights: • Mineral waste becomes a valuable source for the synthesis of magnetite. • Milling helps uniform mixing of reductant with iron ore tailings. • Magnetite nanoparticles exhibit saturation magnetization of 60 emu/g. • Ag coating induces antibacterial activity of magnetite. - Abstract: Magnetite nanoparticles were synthesized from iron ore tailings – a mineral waste collected from the iron ore processing plant. Mechanical milling followed by chemical route is employed to obtain the magnetite nanoparticles from the waste. The magnetite nanoparticles were characterized by X-ray diffractometer, Field Emission Scanning Electron Microscope, Fourier Transform Infrared Spectrometer and Vibrating Sample Magnetometer. X-ray diffraction pattern confirms the existence of a magnetite phase. Field Emission Scanning Electron Microscopic (FE-SEM) pictures reveal that the particle size is below 100 nm. Fourier Transform Infrared (FTIR) spectrum shows a band at 570 cm{sup −1} for the Fe–O bond vibration. Vibrating Sample Magnetometric (VSM) study shows high saturation magnetization value of 60 emu/g at low applied magnetic field. Silver coated magnetite nanoparticles exhibits antibacterial property whereas bare magnetite does not.

  7. Magnetic resonance imaging of folic acid-coated magnetite nanoparticles reflects tissue biodistribution of long-acting antiretroviral therapy.

    Science.gov (United States)

    Li, Tianyuzi; Gendelman, Howard E; Zhang, Gang; Puligujja, Pavan; McMillan, JoEllyn M; Bronich, Tatiana K; Edagwa, Benson; Liu, Xin-Ming; Boska, Michael D

    2015-01-01

    Regimen adherence, systemic toxicities, and limited drug penetrance to viral reservoirs are obstacles limiting the effectiveness of antiretroviral therapy (ART). Our laboratory's development of the monocyte-macrophage-targeted long-acting nanoformulated ART (nanoART) carriage provides a novel opportunity to simplify drug-dosing regimens. Progress has nonetheless been slowed by cumbersome, but required, pharmacokinetic (PK), pharmacodynamics, and biodistribution testing. To this end, we developed a small magnetite ART (SMART) nanoparticle platform to assess antiretroviral drug tissue biodistribution and PK using magnetic resonance imaging (MRI) scans. Herein, we have taken this technique a significant step further by determining nanoART PK with folic acid (FA) decorated magnetite (ultrasmall superparamagnetic iron oxide [USPIO]) particles and by using SMART particles. FA nanoparticles enhanced the entry and particle retention to the reticuloendothelial system over nondecorated polymers after systemic administration into mice. These data were seen by MRI testing and validated by comparison with SMART particles and direct evaluation of tissue drug levels after nanoART. The development of alendronate (ALN)-coated magnetite thus serves as a rapid initial screen for the ability of targeting ligands to enhance nanoparticle-antiretroviral drug biodistribution, underscoring the value of decorated magnetite particles as a theranostic tool for improved drug delivery.

  8. Spectroscopic and magnetic studies of highly dispersible superparamagnetic silica coated magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Tadyszak, Krzysztof [NanoBioMedical Centre, Adam Mickiewicz University, ul. Umultowska 85, 61-614 Poznań (Poland); Institute of Molecular Physics Polish Academy of Sciences, ul. Mariana Smo.luchowskiego 17, 60-179 Poznań (Poland); Kertmen, Ahmet, E-mail: ahmet.kertmen@pg.gda.pl [Department of Pharmaceutical Technology and Biochemistry, Faculty of Chemistry, Gdańsk University of Technology, Narutowicza 11/12, 80-233 Gdańsk (Poland); Coy, Emerson [NanoBioMedical Centre, Adam Mickiewicz University, ul. Umultowska 85, 61-614 Poznań (Poland); Andruszkiewicz, Ryszard; Milewski, Sławomir [Department of Pharmaceutical Technology and Biochemistry, Faculty of Chemistry, Gdańsk University of Technology, Narutowicza 11/12, 80-233 Gdańsk (Poland); Kardava, Irakli; Scheibe, Błażej; Jurga, Stefan [NanoBioMedical Centre, Adam Mickiewicz University, ul. Umultowska 85, 61-614 Poznań (Poland); Chybczyńska, Katarzyna, E-mail: katarzyna.chybczynska@ifmpan.poznan.pl [Institute of Molecular Physics Polish Academy of Sciences, ul. Mariana Smo.luchowskiego 17, 60-179 Poznań (Poland)

    2017-07-01

    Highlights: • Superparamagnetic core-shell nanoparticles of Fe{sub 2}O{sub 3}@Silica were obtained. • Magnetic response was studied by DC, AC magnetometry and EPR spectroscopy. • Nanoparticles show magnetite structure with a well-defined Verwey transition. • Samples show no inter particle magnetic interactions or agglomeration. - Abstract: Superparamagnetic behavior in aqueously well dispersible magnetite core-shell Fe{sub 3}O{sub 4}@SiO{sub 2} nanoparticles is presented. The magnetic properties of core-shell nanoparticles were measured with use of the DC, AC magnetometry and EPR spectroscopy. Particles where characterized by HR-TEM and Raman spectroscopy, showing a crystalline magnetic core of 11.5 ± 0.12 nm and an amorphous silica shell of 22 ± 1.5 nm in thickness. The DC, AC magnetic measurements confirmed the superparamagnetic nature of nanoparticles, additionally the EPR studies performed at much higher frequency than DC, AC magnetometry (9 GHz) have confirmed the paramagnetic nature of the nanoparticles. Our results show the excellent magnetic behavior of the particles with a clear magnetite structure, which are desirable properties for environmental remediation and biomedical applications.

  9. Magnetic resonance imaging of folic acid-coated magnetite nanoparticles reflects tissue biodistribution of long-acting antiretroviral therapy

    Directory of Open Access Journals (Sweden)

    Li T

    2015-06-01

    Full Text Available Tianyuzi Li,1 Howard E Gendelman,1,2 Gang Zhang,1 Pavan Puligujja,1 JoEllyn M McMillan,1 Tatiana K Bronich,2 Benson Edagwa,1 Xin-Ming Liu,1,2 Michael D Boska3 1Department of Pharmacology and Experimental Neuroscience, 2Department of Pharmaceutical Sciences, 3Department of Radiology, University of Nebraska Medical Center, Omaha, NE, USA Abstract: Regimen adherence, systemic toxicities, and limited drug penetrance to viral reservoirs are obstacles limiting the effectiveness of antiretroviral therapy (ART. Our laboratory’s development of the monocyte-macrophage-targeted long-acting nanoformulated ART (nanoART carriage provides a novel opportunity to simplify drug-dosing regimens. Progress has nonetheless been slowed by cumbersome, but required, pharmacokinetic (PK, pharmacodynamics, and biodistribution testing. To this end, we developed a small magnetite ART (SMART nanoparticle platform to assess antiretroviral drug tissue biodistribution and PK using magnetic resonance imaging (MRI scans. Herein, we have taken this technique a significant step further by determining nanoART PK with folic acid (FA decorated magnetite (ultrasmall superparamagnetic iron oxide [USPIO] particles and by using SMART particles. FA nanoparticles enhanced the entry and particle retention to the reticuloendothelial system over nondecorated polymers after systemic administration into mice. These data were seen by MRI testing and validated by comparison with SMART particles and direct evaluation of tissue drug levels after nanoART. The development of alendronate (ALN-coated magnetite thus serves as a rapid initial screen for the ability of targeting ligands to enhance nanoparticle-antiretroviral drug biodistribution, underscoring the value of decorated magnetite particles as a theranostic tool for improved drug delivery. Keywords: folic acid, decorated nanoparticles, magnetite, theranostics, magnetic resonance imaging

  10. Magnetite nanoparticles coated with alkyne-containing polyacrylates for click chemistry

    Science.gov (United States)

    Socaci, Crina; Rybka, Miriam; Magerusan, Lidia; Nan, Alexandrina; Turcu, Rodica; Liebscher, Jürgen

    2013-06-01

    New magnetic core shell nanoparticles were synthesized consisting of magnetite cores and poly-( O-propargyl acrylate) shells. Strong fixing of the shells was achieved by primary anchoring phosphates or α-dihydroxydiphosphonates containing acrylate or methacrylate functionalities. The magnetic nanoparticles are attractive as supports for a variety of function which can be easily introduced by Cu-catalyzed alkyne azide cycloaddition (CuAAC, a click reaction). In this way, also the loading of the magnetic nanoparticles with propargyl units was determined by reaction with 4-azidoacetophenone and analysis of the supernatant. In order to demonstrate the attractiveness of the magnetic nanoparticles a novel azido-containing conjugate with biotin as recognition function and dansyl as fluorescence marker was introduced by CuAAC reaction. All NP show superparamagnetic behavior with high-saturation magnetization values and were further characterized by FTIR, photoelectron spectroscopy and TEM.

  11. Magnetite nanoparticles coated with alkyne-containing polyacrylates for click chemistry

    International Nuclear Information System (INIS)

    Socaci, Crina; Rybka, Miriam; Magerusan, Lidia; Nan, Alexandrina; Turcu, Rodica; Liebscher, Jürgen

    2013-01-01

    New magnetic core shell nanoparticles were synthesized consisting of magnetite cores and poly-(O-propargyl acrylate) shells. Strong fixing of the shells was achieved by primary anchoring phosphates or α-dihydroxydiphosphonates containing acrylate or methacrylate functionalities. The magnetic nanoparticles are attractive as supports for a variety of function which can be easily introduced by Cu-catalyzed alkyne azide cycloaddition (CuAAC, a click reaction). In this way, also the loading of the magnetic nanoparticles with propargyl units was determined by reaction with 4-azidoacetophenone and analysis of the supernatant. In order to demonstrate the attractiveness of the magnetic nanoparticles a novel azido-containing conjugate with biotin as recognition function and dansyl as fluorescence marker was introduced by CuAAC reaction. All NP show superparamagnetic behavior with high-saturation magnetization values and were further characterized by FTIR, photoelectron spectroscopy and TEM.

  12. Magnetite nanoparticles coated with alkyne-containing polyacrylates for click chemistry

    Energy Technology Data Exchange (ETDEWEB)

    Socaci, Crina [National Institute of Research and Development for Isotopic and Molecular Technologies (Romania); Rybka, Miriam [Humboldt-University Berlin, Department of Chemistry (Germany); Magerusan, Lidia; Nan, Alexandrina; Turcu, Rodica; Liebscher, Juergen, E-mail: liebscher@chemie.hu-berlin.de [National Institute of Research and Development for Isotopic and Molecular Technologies (Romania)

    2013-06-15

    New magnetic core shell nanoparticles were synthesized consisting of magnetite cores and poly-(O-propargyl acrylate) shells. Strong fixing of the shells was achieved by primary anchoring phosphates or {alpha}-dihydroxydiphosphonates containing acrylate or methacrylate functionalities. The magnetic nanoparticles are attractive as supports for a variety of function which can be easily introduced by Cu-catalyzed alkyne azide cycloaddition (CuAAC, a click reaction). In this way, also the loading of the magnetic nanoparticles with propargyl units was determined by reaction with 4-azidoacetophenone and analysis of the supernatant. In order to demonstrate the attractiveness of the magnetic nanoparticles a novel azido-containing conjugate with biotin as recognition function and dansyl as fluorescence marker was introduced by CuAAC reaction. All NP show superparamagnetic behavior with high-saturation magnetization values and were further characterized by FTIR, photoelectron spectroscopy and TEM.

  13. Bioinspired synthesis of magnetite nanoparticles

    NARCIS (Netherlands)

    Mirabello, G.; Lenders, J.J.M.; Sommerdijk, N.A.J.M.

    2016-01-01

    Magnetite (Fe3O4) is a widespread magnetic iron oxide encountered in many biological and geological systems, and also in many technological applications. The magnetic properties of magnetite crystals depend strongly on the size and shape of its crystals. Hence, engineering magnetite nanoparticles

  14. Umbelliprenin-coated Fe3O4 magnetite nanoparticles: Antiproliferation evaluation on human Fibrosarcoma cell line (HT-1080)

    International Nuclear Information System (INIS)

    Khorramizadeh, M.R.; Esmail-Nazari, Z.; Zarei-Ghaane, Z.; Shakibaie, M.; Mollazadeh-Moghaddam, K.; Iranshahi, M.; Shahverdi, A.R.

    2010-01-01

    The potential applications of Fe 3 O 4 magnetite nanoparticles (MNPs) in nanomedicine as drug delivery systems are well known. In this study we prepared umbelliprenin-coated Fe 3 O 4 MNPs and evaluated the antiproliferative effect of combination in vitro. After synthesis of Fe 3 O 4 MNPs, particles were characterized by transmission electron microscopy, energy-dispersive spectroscopy, and X-ray diffraction spectroscopy techniques. The natural candidate compound - umbelliprenin- was isolated and identified and umbelliprenin-coated Fe 3 O 4 MNPs were prepared, using precipitation method. The surface chemistry of umbelliprenin-coated Fe 3 O 4 MNPs as well as their thermal decomposition characteristics was examined using Fourier transform infrared spectroscopy and Thermogravimetric Analyzer equipment, respectively. HT-1080 cells were cultured until the logarithmic phase of growth, and MTT assay was successfully carried out to evaluate the possible cytotoxic effects of umbelliprenin-coated Fe 3 O 4 MNPs in viable cells in vitro. The results demonstrated that umbelliprenin has moderate antiproliferative effects with IC 50 value of 50 μg/mL. However, the combination of umbelliprenin and Fe 3 O 4 MNPs showed the IC 50 value of 9 μg/mL. In other words, cell proliferation decreased to the remarkably-low proportion of 45% after treating cells with umbelliprenin-coated Fe 3 O 4 MNPs. This suggests that with the aid of nanoparticles as carriers, natural products may have even broader range of medical applications in future.

  15. The influence of surface modification, coating agents and pH value of aqueous solutions on physical properties of magnetite nanoparticles investigated by ESR method

    Energy Technology Data Exchange (ETDEWEB)

    Dobosz, Bernadeta, E-mail: benia@amu.edu.pl [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznań (Poland); Krzyminiewski, Ryszard [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznań (Poland); Kurczewska, Joanna; Schroeder, Grzegorz [Faculty of Chemistry, Adam Mickiewicz University, Umultowska 89B, 61-614 Poznań (Poland)

    2017-05-01

    The article presents the results of electron spin resonance (ESR) studies for aqueous solutions of functionalized superparamagnetic iron(II,III) oxide nanoparticles. The samples studied differed in type of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions. The ESR spectra of the samples were obtained at room temperature and at 230 K. The field cooling (FC) experiment was performed for selected samples, and the effective anisotropy field (H{sub K2}) and the first order magnetocrystalline anisotropy constant (K{sub 1}) was calculated. The process of the nanoparticles diffusion in different environments (human blood, human serum) forced by an inhomogeneous magnetic field was monitored and their interactions with different solvents have been discussed. It has been shown that ESR method is useful to observe the impact of organic ligands at the magnetite surface, type of coating agent and pH value of aqueous solutions on the properties of iron(II,III) oxide nanoparticles. - Highlights: • The influence of different organic ligands, coatings and pH values of aqueous solutions on the physical properties of the magnetite nanoparticles studied by ESR method. • Nanoparticles diffusion forced by inhomogeneous magnetic field monitored by ESR and explained. • A narrow line separated in ESR spectra by CREM. • The influence of different coatings and pH values of aqueous solutions on ESR spectra of TEMPO attached to the magnetite core.

  16. Synthesis of environmentally friendly highly dispersed magnetite nanoparticles based on rosin cationic surfactants as thin film coatings of steel.

    Science.gov (United States)

    Atta, Ayman M; El-Mahdy, Gamal A; Al-Lohedan, Hamad A; Al-Hussain, Sami A

    2014-04-22

    This work presents a new method to prepare monodisperse magnetite nanoparticles capping with new cationic surfactants based on rosin. Core/shell type magnetite nanoparticles were synthesized using bis-N-(3-levopimaric maleic acid adduct-2-hydroxy) propyl-triethyl ammonium chloride (LPMQA) as capping agent. Fourier transform infrared spectroscopy (FTIR) was employed to characterize the nanoparticles chemical structure. Transmittance electron microscopies (TEM) and X-ray powder diffraction (XRD) were used to examine the morphology of the modified magnetite nanoparticles. The magnetite dispersed aqueous acid solution was evaluated as an effective anticorrosion behavior of a hydrophobic surface on steel. The inhibition effect of magnetite nanoparticles on steel corrosion in 1 M HCl solution was investigated using potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS). Results obtained from both potentiodynamic polarisation and EIS measurements reveal that the magnetite nanoparticle is an effective inhibitor for the corrosion of steel in 1.0 M HCl solution. Polarization data show that magnetite nanoparticles behave as a mixed type inhibitor. The inhibition efficiencies obtained from potentiodynamic polarization and EIS methods are in good agreement.

  17. Synthesis of Environmentally Friendly Highly Dispersed Magnetite Nanoparticles Based on Rosin Cationic Surfactants as Thin Film Coatings of Steel

    Directory of Open Access Journals (Sweden)

    Ayman M. Atta

    2014-04-01

    Full Text Available This work presents a new method to prepare monodisperse magnetite nanoparticles capping with new cationic surfactants based on rosin. Core/shell type magnetite nanoparticles were synthesized using bis-N-(3-levopimaric maleic acid adduct-2-hydroxy propyl-triethyl ammonium chloride (LPMQA as capping agent. Fourier transform infrared spectroscopy (FTIR was employed to characterize the nanoparticles chemical structure. Transmittance electron microscopies (TEM and X-ray powder diffraction (XRD were used to examine the morphology of the modified magnetite nanoparticles. The magnetite dispersed aqueous acid solution was evaluated as an effective anticorrosion behavior of a hydrophobic surface on steel. The inhibition effect of magnetite nanoparticles on steel corrosion in 1 M HCl solution was investigated using potentiodynamic polarization curves and electrochemical impedance spectroscopy (EIS. Results obtained from both potentiodynamic polarisation and EIS measurements reveal that the magnetite nanoparticle is an effective inhibitor for the corrosion of steel in 1.0 M HCl solution. Polarization data show that magnetite nanoparticles behave as a mixed type inhibitor. The inhibition efficiencies obtained from potentiodynamic polarization and EIS methods are in good agreement.

  18. Preparation and characterization of 6-mercaptopurine-coated magnetite nanoparticles as a drug delivery system.

    Science.gov (United States)

    Dorniani, Dena; Hussein, Mohd Zobir Bin; Kura, Aminu Umar; Fakurazi, Sharida; Shaari, Abdul Halim; Ahmad, Zalinah

    2013-01-01

    Iron oxide nanoparticles are of considerable interest because of their use in magnetic recording tape, ferrofluid, magnetic resonance imaging, drug delivery, and treatment of cancer. The specific morphology of nanoparticles confers an ability to load, carry, and release different types of drugs. We synthesized superparamagnetic nanoparticles containing pure iron oxide with a cubic inverse spinal structure. Fourier transform infrared spectra confirmed that these Fe3O4 nanoparticles could be successfully coated with active drug, and thermogravimetric and differential thermogravimetric analyses showed that the thermal stability of iron oxide nanoparticles coated with chitosan and 6-mercaptopurine (FCMP) was markedly enhanced. The synthesized Fe3O4 nanoparticles and the FCMP nanocomposite were generally spherical, with an average diameter of 9 nm and 19 nm, respectively. The release of 6-mercaptopurine from the FCMP nanocomposite was found to be sustained and governed by pseudo-second order kinetics. In order to improve drug loading and release behavior, we prepared a novel nanocomposite (FCMP-D), ie, Fe3O4 nanoparticles containing the same amounts of chitosan and 6-mercaptopurine but using a different solvent for the drug. The results for FCMP-D did not demonstrate "burst release" and the maximum percentage release of 6-mercaptopurine from the FCMP-D nanocomposite reached about 97.7% and 55.4% within approximately 2,500 and 6,300 minutes when exposed to pH 4.8 and pH 7.4 solutions, respectively. By MTT assay, the FCMP nanocomposite was shown not to be toxic to a normal mouse fibroblast cell line. Iron oxide coated with chitosan containing 6-mercaptopurine prepared using a coprecipitation method has the potential to be used as a controlled-release formulation. These nanoparticles may serve as an alternative drug delivery system for the treatment of cancer, with the added advantage of sparing healthy surrounding cells and tissue.

  19. Magnetite nanoparticles coated with methoxy polyethylene glycol as an efficient adsorbent of diazinon pesticide from water

    Directory of Open Access Journals (Sweden)

    Mahboubeh Saeidi

    2016-12-01

    Full Text Available Methoxy polyethylene glycol modified magnetite nanoparticles (PEGMNs were synthesized and characterized by scanning electron microscopy (SEM, vibrating sample magnetometer (VSM, and X-ray diffraction (XRD. The adsorption of diazinon onto PEGMNs was investigated by UV-Vis spectrophotometry at 236 nm, through batch experiments. The effects of adsorbent dosage, solution pH, contact time, solution temperature and water impurities on the adsorption of diazinon onto PEGMNs were investigated. The process of adsorption was increased rapidly in the first contact period of 10 min. The adsorption at equilibrium (qe was found to increase with increasing pH. The results of diazinon removal at various PEGMNs dosages demonstrated that the optimum dose of PEGMNs was 1mg. The amount of adsorption of diazinon at equilibrium increased with an increasing temperature from 15°C to 45°C that indicateds an endothermic process. Therefore, PEGMNs were used as an efficient absorbent for the removal of diazinon.

  20. Preparation and characterization of 6-mercaptopurine-coated magnetite nanoparticles as a drug delivery system

    Directory of Open Access Journals (Sweden)

    Dorniani D

    2013-09-01

    Full Text Available Dena Dorniani,1 Mohd Zobir bin Hussein,1 Aminu Umar Kura,2 Sharida Fakurazi,2 Abdul Halim Shaari,3 Zalinah Ahmad4 1Materials Synthesis and Characterization Laboratory, Institute of Advanced Technology, 2Vaccines and Immunotherapeutics Laboratory, 3Physics Department, Faculty of Science, 4Chemical Pathology Unit, Department of Pathology, Faculty of Medicine and Health Sciences, Universiti Putra Malaysia, Selangor, Malaysia Background: Iron oxide nanoparticles are of considerable interest because of their use in magnetic recording tape, ferrofluid, magnetic resonance imaging, drug delivery, and treatment of cancer. The specific morphology of nanoparticles confers an ability to load, carry, and release different types of drugs. Methods and results: We synthesized superparamagnetic nanoparticles containing pure iron oxide with a cubic inverse spinal structure. Fourier transform infrared spectra confirmed that these Fe3O4 nanoparticles could be successfully coated with active drug, and thermogravimetric and differential thermogravimetric analyses showed that the thermal stability of iron oxide nanoparticles coated with chitosan and 6-mercaptopurine (FCMP was markedly enhanced. The synthesized Fe3O4 nanoparticles and the FCMP nanocomposite were generally spherical, with an average diameter of 9 nm and 19 nm, respectively. The release of 6-mercaptopurine from the FCMP nanocomposite was found to be sustained and governed by pseudo-second order kinetics. In order to improve drug loading and release behavior, we prepared a novel nanocomposite (FCMP-D, ie, Fe3O4 nanoparticles containing the same amounts of chitosan and 6-mercaptopurine but using a different solvent for the drug. The results for FCMP-D did not demonstrate “burst release” and the maximum percentage release of 6-mercaptopurine from the FCMP-D nanocomposite reached about 97.7% and 55.4% within approximately 2,500 and 6,300 minutes when exposed to pH 4.8 and pH 7.4 solutions, respectively

  1. Effects of cadmium chloride as inhibitor on stability and kinetics of immobilized Lactoperoxidase(LPO on silica-coated magnetite nanoparticles versus free LPO

    Directory of Open Access Journals (Sweden)

    Narges Babadaie Samani

    2016-10-01

    Full Text Available Objective(s: Enzyme immobilization via nanoparticles is perfectly compatible against the other chemical or biological approximate to improve enzyme functions and stability. In this study lactoperoxidase was immobilized onto silica-coated magnetite nanoparticles to improve enzyme properties in the presence of cadmium chloride as an inhibitor. Materials and Methods:  The process consists of the following steps: (1 preparing magnetic iron oxide nanoparticles using the co-precipitation method, (2 coating NP with silica (SiO2 by sol–gel reaction, (3 characterizations of NPs were examined by FT-IR, XRD, AGFM and TEM. (4 Immobilization of LPO on the magnetite NPs, (5 Study kinetic and stability of both free and immobilized LPO in the presence of various concentrations of cadmium chloride. Results:  The size of the Fe3O4 and silica-coated magnetite nanoparticles were about 9 nm and 12 nm, respectively. The results showed that the highest immobilization yield, nearly 90 %, was attained at 240 to 300 µg of LPO at 15h. It was found that the concentration of cadmium chloride directly affects the LPO activity and changes the kinetic parameters of it. Also, the results showed that immobilized LPO has better tolerance than the free LPO, so that after immobilization, Vmax of immobilized LPO was increased and Km of immobilized LPO was decreased. Conclusion: The results demonstrating that the effect of immobilized lactoperoxidase on silica-coated magnetite nanoparticles increases the stability of the LPO in the presence of cadmium chloride as inhibitor. Michaelis–Menten parameters (Km and Vmax also revealed the considerable improvement of immobilized.

  2. Magnetite nanoparticles coated with β-cyclodextrin functionalized-ionic liquid: Synthesis and its preliminary investigation as a new sensing material

    Energy Technology Data Exchange (ETDEWEB)

    Sinniah, Subathra; Mohamad, Sharifah; Manan, Ninie S.A., E-mail: niniemanan@um.edu.my

    2015-12-01

    Highlights: • A novel of β-cyclodextrin functionalized-ionic liquid coated with magnetite nanoparticles is prepared via co-precipitation method. • The architecture of the material is successfully characterized and confirmed that β-cyclodextrin-functionalized-ionic liquid, has been effectively coated onto surface of Fe{sub 3}O{sub 4} magnetite nanoparticles. • Vibration Sample Magnetometer analysis confirmed that the Fe{sub 3}O{sub 4}-β-CD-IL able to attain an excellent magnetic properties. • Preliminary electrochemical study shows that Fe{sub 3}O{sub 4}-β-CD-IL able to recognize Biphenol A. - Abstract: In this study, a novel surface of modified magnetite nanoparticles Fe{sub 3}O{sub 4} was coated with β-cyclodextrin-funclionalized ionic liquid (Fe{sub 3}O{sub 4}-β-CD-IL) via the co-precipitation method in alkaline salt medium. β-Cyclodextrin-functionalized-ionic liquid has been effectively coated onto the surface of Fe{sub 3}O{sub 4} magnetite nanoparticles. The instruments used to investigate the architecture are: Fourier Transform Infrared Spectroscopy, X-ray Powder Diffraction, Electron Microscope-Energy Dispersive X-Ray Spectrometry, Transmission Electron Microscope, Field Emission Scanning Electron Microscope, Vibrating Sample Magnetometer and Brunauer–Emmett–Teller isotherm. A Vibration Sample Magnetometer analysis verified that the Fe{sub 3}O{sub 4}-β-CD-IL attained excellent magnetic properties. The analysis of High Resolution Transmission Electron Microscope shows that the Fe{sub 3}O{sub 4}-β-CD-IL produced monodisperse particles with minimal aggregation. Moreover, electrochemical studies have revealed that this new material showed outstanding ability to recognize Bisphenol A with lower electrochemical potential at 0.5 V than other comparative materials, as well as a higher detection current. Thus, this material has promising potential as a new electrode material in sensor applications.

  3. Magnetite nanoparticles coated with β-cyclodextrin functionalized-ionic liquid: Synthesis and its preliminary investigation as a new sensing material

    International Nuclear Information System (INIS)

    Sinniah, Subathra; Mohamad, Sharifah; Manan, Ninie S.A.

    2015-01-01

    Highlights: • A novel of β-cyclodextrin functionalized-ionic liquid coated with magnetite nanoparticles is prepared via co-precipitation method. • The architecture of the material is successfully characterized and confirmed that β-cyclodextrin-functionalized-ionic liquid, has been effectively coated onto surface of Fe 3 O 4 magnetite nanoparticles. • Vibration Sample Magnetometer analysis confirmed that the Fe 3 O 4 -β-CD-IL able to attain an excellent magnetic properties. • Preliminary electrochemical study shows that Fe 3 O 4 -β-CD-IL able to recognize Biphenol A. - Abstract: In this study, a novel surface of modified magnetite nanoparticles Fe 3 O 4 was coated with β-cyclodextrin-funclionalized ionic liquid (Fe 3 O 4 -β-CD-IL) via the co-precipitation method in alkaline salt medium. β-Cyclodextrin-functionalized-ionic liquid has been effectively coated onto the surface of Fe 3 O 4 magnetite nanoparticles. The instruments used to investigate the architecture are: Fourier Transform Infrared Spectroscopy, X-ray Powder Diffraction, Electron Microscope-Energy Dispersive X-Ray Spectrometry, Transmission Electron Microscope, Field Emission Scanning Electron Microscope, Vibrating Sample Magnetometer and Brunauer–Emmett–Teller isotherm. A Vibration Sample Magnetometer analysis verified that the Fe 3 O 4 -β-CD-IL attained excellent magnetic properties. The analysis of High Resolution Transmission Electron Microscope shows that the Fe 3 O 4 -β-CD-IL produced monodisperse particles with minimal aggregation. Moreover, electrochemical studies have revealed that this new material showed outstanding ability to recognize Bisphenol A with lower electrochemical potential at 0.5 V than other comparative materials, as well as a higher detection current. Thus, this material has promising potential as a new electrode material in sensor applications.

  4. A bench-scale study on the removal and recovery of phosphate by hydrous zirconia-coated magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Zhe; Fang, Wenkan; Xing, Mingchao; Wu, Deyi, E-mail: dywu@sjtu.edu.cn

    2017-02-15

    Owing to the easy magnetic separation from water for reuse, magnetic nanoparticles have drawn great interest as adsorbents. Herein hydrous zirconia-coated magnetite nanoparticles (Fe{sub 3}O{sub 4}@ZrO{sub 2}) were created by a facile method and a bench–scale study was undertaken to evaluate its effectiveness and mechanism to remove phosphate at low concentrations. Results indicated that phosphate removal by Fe{sub 3}O{sub 4}@ZrO{sub 2} was fast (95% of phosphate removal within 10 min) and nearly complete removal could be achieved at the adsorbent dosage >0.6 g/L. In tap water or wastewater where competitive anions coexist, regulation of pH was found to be quite effective to augment the performance of phosphate removal. In pH–lowered adsorption systems, phosphate removal followed a good pattern similarly to pure water, i.e., a continuous high efficiency removal followed by a rapid saturation. Adsorption–desorption–regeneration studies showed that Fe{sub 3}O{sub 4}@ZrO{sub 2} could be repeatedly used for phosphate removal and adsorbed phosphate could be stripped for recovery. The fractionation of adsorbed phosphorus suggested that NaOH-P fraction was dominant. We also found that the adsorption reaction of phosphate with Fe{sub 3}O{sub 4}@ZrO{sub 2} shifted the isoelectric point of Fe{sub 3}O{sub 4}@ZrO{sub 2} from ~9.0 to ~3.0. FTIR measurements further showed the direct coordination of phosphate onto zirconium by replacement of hydroxyl groups. The formation of the monodentate (ZrO)PO{sub 2}(OH) complex was proposed. - Highlights: • Hydrous zirconia–coated magnetite was used for phosphate capture. • Regulation of pH was able to enhance P removal in the presence of coexisting ions. • Phosphate was coordinated onto zirconium by replacement of hydroxyl groups. • The material could be easily separated from water for reuse by a magnet. • Desorption of phosphate from the material could be achieved with NaOH treatment.

  5. Mercury Removal From Aqueous Solutions With Chitosan-Coated Magnetite Nanoparticles Optimized Using the Box-Behnken Design

    Science.gov (United States)

    Rahbar, Nadereh; Jahangiri, Alireza; Boumi, Shahin; Khodayar, Mohammad Javad

    2014-01-01

    Background: Nowadays, removal of heavy metals from the environment is an important problem due to their toxicity. Objectives: In this study, a modified method was used to synthesize chitosan-coated magnetite nanoparticles (CCMN) to be used as a low cost and nontoxic adsorbent. CCMN was then employed to remove Hg2+ from water solutions. Materials and Methods: To remove the highest percentage of mercury ions, the Box-Behnken model of response surface methodology (RSM) was applied to simultaneously optimize all parameters affecting the adsorption process. Studied parameters of the process were pH (5-8), initial metal concentration (2-8 mg/L), and the amount of damped adsorbent (0.25-0.75 g). A second-order mathematical model was developed using regression analysis of experimental data obtained from 15 batch runs. Results: The optimal conditions predicted by the model were pH = 5, initial concentration of mercury ions = 6.2 mg/L, and the amount of damped adsorbent = 0.67 g. Confirmatory testing was performed and the maximum percentage of Hg2+ removed was found to be 99.91%. Kinetic studies of the adsorption process specified the efficiency of the pseudo second-order kinetic model. The adsorption isotherm was well-fitted to both the Langmuir and Freundlich models. Conclusions: CCMN as an excellent adsorbent could remove the mercury ions from water solutions at low and moderate concentrations, which is the usual amount found in environment. PMID:24872943

  6. Magnetite nanoparticles embedded in biodegradable porous silicon

    International Nuclear Information System (INIS)

    Granitzer, P.; Rumpf, K.; Roca, A.G.; Morales, M.P.; Poelt, P.; Albu, M.

    2010-01-01

    Magnetite nanoparticles, which are coated with oleic acid in a hexane solution and exhibit an average diameter of 7.7 nm, were embedded in a porous silicon (PS) matrix by immersion under defined parameters (e.g. concentration, temperature, time). The porous silicon matrix is prepared by anodization of a highly n-doped silicon wafer in an aqueous HF-solution. Magnetic characterization of the samples has been performed by SQUID-magnetometry. The superparamagnetic behaviour of the magnetite nanoparticles is represented by temperature-dependent magnetization measurements. Zero field (ZFC)/field cooled (FC) experiments indicate magnetic interactions between the particles. For the infiltration into the PS-templates different concentrations of the magnetite nanoparticles are used and magnetization measurements are performed in respect with magnetic interactions between the particles. The achieved porous silicon/magnetite specimens are not only interesting due to their transition between superparamagnetic and ferromagnetic behaviour, and thus for magnetic applications but also because of the non-toxicity of both materials giving the opportunity to employ the system in medical applications as drug delivery or in medical diagnostics.

  7. Magnetite nanoparticles for biomedical applications

    International Nuclear Information System (INIS)

    Sora, Sergiu; Ion, Rodica Mariana

    2010-01-01

    This work aims to establish and to optimize the conditions for chemical synthesis of nanosized magnetic core-shell iron oxide. The core is magnetite and for the shell we used gold in order to obtain different nanoparticles. Iron oxides was synthesized by sonochemical process using ferrous salts, favoring the synthesis at low-temperature, low costs, high material purity and nanostructure control. After synthesis, some investigation techniques as: X-ray diffraction (XRD), atomic force microscopy (AFM), Thermogravimetric analysis (TGA), Fourier-Transform Infrared Spectroscopy (FTIR) and UVVis absorbance spectroscopy, have been used to see the characteristics of the nanoparticles. For in vitro applications, it is important to prevent any aggregation of the nanoparticles, and may also enable efficient excretion and protection of the cells from toxicity. For biomedical applications like magnetic biofunctional material vectors to target tissues, the particles obtained have to be spherical with 10 nm average diameter. Key words: magnetite, nanocomposite, core-shell, sonochemical method

  8. o-Vanillin functionalized mesoporous silica – coated magnetite nanoparticles for efficient removal of Pb(II) from water

    International Nuclear Information System (INIS)

    Culita, Daniela C.; Simonescu, Claudia Maria; Patescu, Rodica-Elena; Dragne, Mioara; Stanica, Nicolae; Oprea, Ovidiu

    2016-01-01

    o-Vanillin functionalized mesoporous silica – coated magnetite (Fe 3 O 4 @MCM-41-N-oVan) was synthesized and fully characterized by X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, N 2 adsorption–desorption technique and magnetic measurements. The capacity of Fe 3 O 4 @MCM-41-N-oVan to adsorb Pb(II) from aqueous solutions was evaluated in comparison with raw mesoporous silica – coated magnetite (Fe 3 O 4 @MCM-41) and amino – modified mesoporous silica coated magnetite (Fe 3 O 4 @MCM-41-NH 2 ). The effect of adsorption process parameters such us pH, contact time, initial Pb(II) concentration was also investigated. The adsorption data were successfully fitted with the Langmuir model, exhibiting a maximum adsorption capacity of 155.71 mg/g at pH=4.4 and T=298 K. The results revealed that the adsorption rate was very high at the beginning of the adsorption process, 80–90% of the total amount of Pb(II) being removed within the first 60 min, depending on the initial concentration. The results of the present work suggest that Fe 3 O 4 @MCM-41-N-oVan is a suitable candidate for the separation of Pb(II) from contaminated water. - Graphical abstract: A novel magnetic adsorbent based on o-vanillin functionalized mesoporous silica – coated magnetite was synthesized and fully characterized and its adsorption capacity for Pb(II) ions in aqueous solutions was evaluated. The maximum adsorption capacity for Pb(II) ions was determined to be 155.71 mg g −1 . The adsorption rate was very high at the beginning of the adsorption process, 90% of the total amount of Pb(II) being removed within the first 60 min. Display Omitted

  9. o-Vanillin functionalized mesoporous silica - coated magnetite nanoparticles for efficient removal of Pb(II) from water

    Science.gov (United States)

    Culita, Daniela C.; Simonescu, Claudia Maria; Patescu, Rodica-Elena; Dragne, Mioara; Stanica, Nicolae; Oprea, Ovidiu

    2016-06-01

    o-Vanillin functionalized mesoporous silica - coated magnetite (Fe3O4@MCM-41-N-oVan) was synthesized and fully characterized by X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, N2 adsorption-desorption technique and magnetic measurements. The capacity of Fe3O4@MCM-41-N-oVan to adsorb Pb(II) from aqueous solutions was evaluated in comparison with raw mesoporous silica - coated magnetite (Fe3O4@MCM-41) and amino - modified mesoporous silica coated magnetite (Fe3O4@MCM-41-NH2). The effect of adsorption process parameters such us pH, contact time, initial Pb(II) concentration was also investigated. The adsorption data were successfully fitted with the Langmuir model, exhibiting a maximum adsorption capacity of 155.71 mg/g at pH=4.4 and T=298 K. The results revealed that the adsorption rate was very high at the beginning of the adsorption process, 80-90% of the total amount of Pb(II) being removed within the first 60 min, depending on the initial concentration. The results of the present work suggest that Fe3O4@MCM-41-N-oVan is a suitable candidate for the separation of Pb(II) from contaminated water.

  10. Degradation of magnetite nanoparticles in biomimetic media

    Energy Technology Data Exchange (ETDEWEB)

    Briceño, Sarah; Hernandez, Ana C.; Sojo, Juan [Instituto Venezolano de Investigaciones Científicas (IVIC), Laboratorio de Materiales, Centro de Ingeniería de Materiales y Nanotecnología (Venezuela, Bolivarian Republic of); Lascano, Luis [Dpto. Física, Escuela Politécnica Nacional (Ecuador); Gonzalez, Gema, E-mail: gemagonz@ivic.gob.ve, E-mail: gema.gonzalez@epn.edu.ec [Escuela Nacional Politécnica (Ecuador)

    2017-04-15

    Magnetic nanoparticles (NPs) of magnetite Fe{sub 3}O{sub 4} obtained by coprecipitation (COP), thermal decomposition (DT), and commercial sample (CM) have been degraded in similar conditions to physiological medium at pH 4.7 and in simulated body fluid (SBF) at pH 7.4. The formation of the nanoparticles was confirmed by FTIR spectroscopy, X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). In view of medical and environmental applications, the stability of the particles was measured with dynamic light scattering. The degradation processes were followed with atomic absorption spectroscopy (EAA) and TEM. Magnetic measurements were carried out using vibrating sample magnetometry (VSM). Our results revealed that the structural and magnetic properties of the remaining nanoparticles after the degradation process were significantly different to those of the initial suspension. The degradation kinetics is affected by the pH, the coating, and the average particle size of the nanoparticles.

  11. Preparation and characterization of 6-mercaptopurine-coated magnetite nanoparticles as a drug delivery system

    OpenAIRE

    Dorniani, Dena; Zobir Hussein,Mohd; Kura,Aminu Umar; Fakurazi,Sharida; Halim Shaari,Abdul; Ahmad,Zalinah

    2013-01-01

    Dena Dorniani,1 Mohd Zobir bin Hussein,1 Aminu Umar Kura,2 Sharida Fakurazi,2 Abdul Halim Shaari,3 Zalinah Ahmad4 1Materials Synthesis and Characterization Laboratory, Institute of Advanced Technology, 2Vaccines and Immunotherapeutics Laboratory, 3Physics Department, Faculty of Science, 4Chemical Pathology Unit, Department of Pathology, Faculty of Medicine and Health Sciences, Universiti Putra Malaysia, Selangor, Malaysia Background: Iron oxide nanoparticles are of considerable interest beca...

  12. Preparation and radiolabeling of human serum albumin (HSA)-coated magnetite nanoparticles for magnetically targeted therapy

    International Nuclear Information System (INIS)

    Zhang Chunfu; Cao Jinquan; Yin Duanzhi; Wang Yongxian; Feng Yanlin; Tan Jiajue

    2004-01-01

    In this paper, we describe the preparation of human serum albumin-coated magnetic particles of about 200 nm in diameter with narrow size distribution radiolabeled with 188 Re for the purpose of magnetically targeted therapy. The optimum radiolabeling conditions are: SnCl 2 ·2H 2 O 8 mg/ml, citric acid 20 mg/ml, vitamin C 8 mg/ml, labeling volume 500 μl and a reaction time of 3 h. The stability of the radiolabeled particles is suitable for in vivo study

  13. Preparation and radiolabeling of human serum albumin (HSA)-coated magnetite nanoparticles for magnetically targeted therapy

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Chunfu E-mail: zchunfu@yahoo.com.cn; Cao Jinquan; Yin Duanzhi; Wang Yongxian; Feng Yanlin; Tan Jiajue

    2004-12-01

    In this paper, we describe the preparation of human serum albumin-coated magnetic particles of about 200 nm in diameter with narrow size distribution radiolabeled with {sup 188}Re for the purpose of magnetically targeted therapy. The optimum radiolabeling conditions are: SnCl{sub 2}{center_dot}2H{sub 2}O 8 mg/ml, citric acid 20 mg/ml, vitamin C 8 mg/ml, labeling volume 500 {mu}l and a reaction time of 3 h. The stability of the radiolabeled particles is suitable for in vivo study.

  14. A biological method for in-situ synthesis of hydroxyapatite-coated magnetite nanoparticles using Enterobacter aerogenes: Characterization and acute toxicity assessments.

    Science.gov (United States)

    Ahmadzadeh, Elham; Talebnia Rowshan, Farid; Hosseini, Morteza

    2017-04-01

    Hydroxyapatite (HA)-coated magnetite nanoparticles (MNPs) are being widely investigated for various applications in medical engineering and wastewater treatment. In this work, the MNPs were thoroughly coated by bacterial synthesized HA nanoparticles during biomineralization process using Enterobacter aerogenes. The resulting bacterial-induced precipitate was then calcined at 600°C and investigated with respect to structural characteristics, particle size and magnetic strength by XRD, FT-IR, SEM, EDS, TEM and VSM analyses. The effects of MNPs and HA-coated MNPs (HA-MNPs) on the viability of human MCF-7 cell lines were also investigated via mitochondrial activity test (MTT) and lactate dehydrogenase (LDH) assays. The powder characterization results showed appropriate structural properties for HA-MNPs samples. The particles diameter size of the MNPs and HA-MNPs were in the range of 3-25nm and 20-80nm, respectively. The biologically-synthesized HA-MNPs formed a stable suspension in water while keeping their magnetic property. The saturation magnetization (Ms) of HA-MNPs was measured at ~10emug -1 which was in good agreement with the structural composition of this sample. Finally, the results of the cell lines viability indicated that coating of toxic MNPs via biomineralization was a promising approach in order to synthesize bio-compatible magnetic nanoparticles with suitable physical and chemical structural characteristics. The toxicity level of MNPs was reduced by 10 fold when coated by bacterial-synthesized HA. Copyright © 2016 Elsevier B.V. All rights reserved.

  15. Adherence of paclitaxel drug in magnetite chitosan nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Escobar Zapata, Edna V.; Martinez Perez, Carlos A.; Rodriguez Gonzalez, Claudia A.; Castro Carmona, Javier S. [Instituto de Ingenieria y Tecnologia, Universidad Autonoma de Ciudad Juarez, Ave. Del Charro 610 norte, Col. Partido Romero, C.P. 32320, Cd. Juarez Chihuahua (Mexico); Quevedo Lopez, Manuel A. [Departamento de Polimeros y Materiales, Universidad de Sonora, Blvd. Luis Encinas y Rosales, Hermosillo, Sonora (Mexico); Garcia-Casillas, Perla E., E-mail: pegarcia@uacj.mx [Instituto de Ingenieria y Tecnologia, Universidad Autonoma de Ciudad Juarez, Ave. Del Charro 610 norte, Col. Partido Romero, C.P. 32320, Cd. Juarez Chihuahua (Mexico)

    2012-09-25

    Highlights: Black-Right-Pointing-Pointer Chitosan silica magnetite adsorbs antineoplastic drug. Black-Right-Pointing-Pointer Silica coating improve the drug adherence. - Abstract: Cancer treatment is a big challenge in medicine where chemotherapies and radiotherapies are aggressive and poorly effective having side effects as delirium, fatigue, insomnia, nausea and vomiting which are common problems for cancer patients. For this reason, during the last two decades, many researchers have developed several techniques to improve the current therapies; one of them is the functionalization of magnetic nanoparticles for drug delivery. In this work, magnetic nanoparticles with an average crystallite size 21.8 nm were covered in a core/shell type; magnetite/silica, magnetite/chitosan, and a double shell magnetite/silica/chitosan were developed for attaching an antineoplastic drug. The mechanism for the functionalization of the nanoparticles with a single and double shell was studied with Fourier transformed infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The adherence of an antineoplastic drug, paclitaxel, onto functionalized nanoparticles was analyzed with a UV-Visible spectroscopy at a wavelength of 253 nm. It was found that the adherence of the drug is improved up to 18% when magnetite nanoparticles are coated with a single chitosan shell, and when the nanoparticles are coated with a silica/chitosan shell the adherence increases up to 29%.

  16. Adherence of paclitaxel drug in magnetite chitosan nanoparticles

    International Nuclear Information System (INIS)

    Escobar Zapata, Edna V.; Martínez Pérez, Carlos A.; Rodríguez González, Claudia A.; Castro Carmona, Javier S.; Quevedo Lopez, Manuel A.; García-Casillas, Perla E.

    2012-01-01

    Highlights: ► Chitosan silica magnetite adsorbs antineoplastic drug. ► Silica coating improve the drug adherence. - Abstract: Cancer treatment is a big challenge in medicine where chemotherapies and radiotherapies are aggressive and poorly effective having side effects as delirium, fatigue, insomnia, nausea and vomiting which are common problems for cancer patients. For this reason, during the last two decades, many researchers have developed several techniques to improve the current therapies; one of them is the functionalization of magnetic nanoparticles for drug delivery. In this work, magnetic nanoparticles with an average crystallite size 21.8 nm were covered in a core/shell type; magnetite/silica, magnetite/chitosan, and a double shell magnetite/silica/chitosan were developed for attaching an antineoplastic drug. The mechanism for the functionalization of the nanoparticles with a single and double shell was studied with Fourier transformed infrared spectroscopy (FTIR) and X-ray photoelectron spectroscopy (XPS). The adherence of an antineoplastic drug, paclitaxel, onto functionalized nanoparticles was analyzed with a UV–Visible spectroscopy at a wavelength of 253 nm. It was found that the adherence of the drug is improved up to 18% when magnetite nanoparticles are coated with a single chitosan shell, and when the nanoparticles are coated with a silica/chitosan shell the adherence increases up to 29%.

  17. o-Vanillin functionalized mesoporous silica – coated magnetite nanoparticles for efficient removal of Pb(II) from water

    Energy Technology Data Exchange (ETDEWEB)

    Culita, Daniela C., E-mail: danaculita@yahoo.co.uk [“Ilie Murgulescu” Institute of Physical Chemistry, Splaiul Independentei 202, Bucharest (Romania); Simonescu, Claudia Maria; Patescu, Rodica-Elena [Politehnica University, Faculty of Applied Chemistry and Materials Science, Bucharest (Romania); Dragne, Mioara [S.C. KEMCRISTAL S.R.L., Muncii Str., No. 51, Fundulea, Călăraşi (Romania); Stanica, Nicolae [“Ilie Murgulescu” Institute of Physical Chemistry, Splaiul Independentei 202, Bucharest (Romania); Oprea, Ovidiu [Politehnica University, Faculty of Applied Chemistry and Materials Science, Bucharest (Romania)

    2016-06-15

    o-Vanillin functionalized mesoporous silica – coated magnetite (Fe{sub 3}O{sub 4}@MCM-41-N-oVan) was synthesized and fully characterized by X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, N{sub 2} adsorption–desorption technique and magnetic measurements. The capacity of Fe{sub 3}O{sub 4}@MCM-41-N-oVan to adsorb Pb(II) from aqueous solutions was evaluated in comparison with raw mesoporous silica – coated magnetite (Fe{sub 3}O{sub 4}@MCM-41) and amino – modified mesoporous silica coated magnetite (Fe{sub 3}O{sub 4}@MCM-41-NH{sub 2}). The effect of adsorption process parameters such us pH, contact time, initial Pb(II) concentration was also investigated. The adsorption data were successfully fitted with the Langmuir model, exhibiting a maximum adsorption capacity of 155.71 mg/g at pH=4.4 and T=298 K. The results revealed that the adsorption rate was very high at the beginning of the adsorption process, 80–90% of the total amount of Pb(II) being removed within the first 60 min, depending on the initial concentration. The results of the present work suggest that Fe{sub 3}O{sub 4}@MCM-41-N-oVan is a suitable candidate for the separation of Pb(II) from contaminated water. - Graphical abstract: A novel magnetic adsorbent based on o-vanillin functionalized mesoporous silica – coated magnetite was synthesized and fully characterized and its adsorption capacity for Pb(II) ions in aqueous solutions was evaluated. The maximum adsorption capacity for Pb(II) ions was determined to be 155.71 mg g{sup −1}. The adsorption rate was very high at the beginning of the adsorption process, 90% of the total amount of Pb(II) being removed within the first 60 min. Display Omitted.

  18. In Situ Mineralization of Magnetite Nanoparticles in Chitosan Hydrogel

    Science.gov (United States)

    Wang, Yongliang; Li, Baoqiang; Zhou, Yu; Jia, Dechang

    2009-09-01

    Based on chelation effect between iron ions and amino groups of chitosan, in situ mineralization of magnetite nanoparticles in chitosan hydrogel under ambient conditions was proposed. The chelation effect between iron ions and amino groups in CS-Fe complex, which led to that chitosan hydrogel exerted a crucial control on the magnetite mineralization, was proved by X-ray photoelectron spectrum. The composition, morphology and size of the mineralized magnetite nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy and thermal gravity. The mineralized nanoparticles were nonstoichiometric magnetite with a unit formula of Fe2.85O4 and coated by a thin layer of chitosan. The mineralized magnetite nanoparticles with mean diameter of 13 nm dispersed in chitosan hydrogel uniformly. Magnetization measurement indicated that superparamagnetism behavior was exhibited. These magnetite nanoparticles mineralized in chitosan hydrogel have potential applications in the field of biotechnology. Moreover, this method can also be used to synthesize other kinds of inorganic nanoparticles, such as ZnO, Fe2O3 and hydroxyapatite.

  19. In Situ Mineralization of Magnetite Nanoparticles in Chitosan Hydrogel

    Directory of Open Access Journals (Sweden)

    Wang Yongliang

    2009-01-01

    Full Text Available Abstract Based on chelation effect between iron ions and amino groups of chitosan, in situ mineralization of magnetite nanoparticles in chitosan hydrogel under ambient conditions was proposed. The chelation effect between iron ions and amino groups in CS–Fe complex, which led to that chitosan hydrogel exerted a crucial control on the magnetite mineralization, was proved by X-ray photoelectron spectrum. The composition, morphology and size of the mineralized magnetite nanoparticles were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy and thermal gravity. The mineralized nanoparticles were nonstoichiometric magnetite with a unit formula of Fe2.85O4and coated by a thin layer of chitosan. The mineralized magnetite nanoparticles with mean diameter of 13 nm dispersed in chitosan hydrogel uniformly. Magnetization measurement indicated that superparamagnetism behavior was exhibited. These magnetite nanoparticles mineralized in chitosan hydrogel have potential applications in the field of biotechnology. Moreover, this method can also be used to synthesize other kinds of inorganic nanoparticles, such as ZnO, Fe2O3and hydroxyapatite.

  20. Synthesis of Stabilized Myrrh-Capped Hydrocolloidal Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ayman M. Atta

    2014-07-01

    Full Text Available Herein we report a new method for synthesizing stabilized magnetic nanoparticle (MNP colloids. A new class of monodisperse water-soluble magnetite nano-particles was prepared by a simple and inexpensive co-precipitation method. Iron ions and iodine were prepared by the reaction between ferric chloride and potassium iodide. The ferrous and ferric ions were hydrolyzed at low temperature at pH 9 in the presence of iodine to produce iron oxide nanoparticles. The natural product myrrh gum was used as capping agent to produce highly dispersed coated magnetite nanoparticles. The structure and morphology of the magnetic nanogel was characterized by Fourier transform infrared spectroscopy (FTIR and transmission electron microscopy (TEM, and X-ray diffraction (XRD was used to examine the crystal structure of the produced magnetite nanoparticles.

  1. The synthesis and characterization of poly(γ-glutamic acid)-coated magnetite nanoparticles and their effects on antibacterial activity and cytotoxicity

    International Nuclear Information System (INIS)

    Stephen Inbaraj, B; Kao, T H; Tsai, T Y; Chiu, C P; Kumar, R; Chen, B H

    2011-01-01

    Magnetite nanoparticles (MNPs) modified with sodium and calcium salts of poly(γ-glutamic acid) (NaPGA and CaPGA) were synthesized by the coprecipitation method, followed by characterization and evaluation of their antibacterial and cytotoxic effects. Superparamagnetic MNPs are particularly attractive for magnetic driving as well as bacterial biofilm and cell targeting in in vivo applications. Characterization of synthesized MNPs by the Fourier transform infrared spectra and magnetization curves confirmed the PGA coating on MNPs. The mean diameter of NaPGA- and CaPGA-coated MNPs as determined by transmission electron microscopy was 11.8 and 14 nm, respectively, while the x-ray diffraction pattern revealed the as-synthesized MNPs to be pure magnetite. Based on agar dilution assay, both NaPGA- and CaPGA-coated MNPs showed a lower minimum inhibitory concentration in Salmonella enteritidis SE 01 than the commercial antibiotics linezolid and cefaclor, but the former was effective against Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 10832, whereas the latter was effective against Escherichia coli O157:H7 TWC 01. An in vitro cytotoxicity study in human skin fibroblast cells as measured by MTT assay implied the as-synthesized MNPs to be nontoxic. This outcome demonstrated that both γ-PGA-modified MNPs are cytocompatible and possess antibacterial activity in vitro, and thereby should be useful in in vivo studies for biomedical applications.

  2. The synthesis and characterization of poly({gamma}-glutamic acid)-coated magnetite nanoparticles and their effects on antibacterial activity and cytotoxicity

    Energy Technology Data Exchange (ETDEWEB)

    Stephen Inbaraj, B; Kao, T H; Tsai, T Y; Chiu, C P; Kumar, R; Chen, B H, E-mail: 002622@mail.fju.edu.tw [Department of Food Science, Fu Jen University, Taipei 242, Taiwan (China)

    2011-02-18

    Magnetite nanoparticles (MNPs) modified with sodium and calcium salts of poly({gamma}-glutamic acid) (NaPGA and CaPGA) were synthesized by the coprecipitation method, followed by characterization and evaluation of their antibacterial and cytotoxic effects. Superparamagnetic MNPs are particularly attractive for magnetic driving as well as bacterial biofilm and cell targeting in in vivo applications. Characterization of synthesized MNPs by the Fourier transform infrared spectra and magnetization curves confirmed the PGA coating on MNPs. The mean diameter of NaPGA- and CaPGA-coated MNPs as determined by transmission electron microscopy was 11.8 and 14 nm, respectively, while the x-ray diffraction pattern revealed the as-synthesized MNPs to be pure magnetite. Based on agar dilution assay, both NaPGA- and CaPGA-coated MNPs showed a lower minimum inhibitory concentration in Salmonella enteritidis SE 01 than the commercial antibiotics linezolid and cefaclor, but the former was effective against Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 10832, whereas the latter was effective against Escherichia coli O157:H7 TWC 01. An in vitro cytotoxicity study in human skin fibroblast cells as measured by MTT assay implied the as-synthesized MNPs to be nontoxic. This outcome demonstrated that both {gamma}-PGA-modified MNPs are cytocompatible and possess antibacterial activity in vitro, and thereby should be useful in in vivo studies for biomedical applications.

  3. Synthesis and characterization of magnetite nanoparticles from mineral magnetite

    International Nuclear Information System (INIS)

    Morel, Mauricio; Martínez, Francisco; Mosquera, Edgar

    2013-01-01

    We have synthesized magnetite nanoparticles with sizes that range from 20 to 30 nm from mineral magnetite roughly 45 μm in size. The procedure consists in the dissolution of the mineral in an acidic medium and subsequent precipitation in a basic medium in the presence of oleic acid. Two experiments were conducted in different gaseous environments. The first was carried out in an environment exposed to air (M1) and the second in an N 2 (M2) environment. The x-ray diffraction results showed a slight difference, which corresponds to the surface oxidation of magnetite. The sizes of the modified nanoparticles were determined through the Scherrer equation and transmission electron microscopy. An organic material mass loss corresponding to 18% was observed through a thermogravimetric analysis. The Fourier transform infrared spectroscopic analysis provides information about the type of bond that is formed on the surface of the nanoparticle, which corresponds to a bidentate chelate. The vibrating sample magnetometer results show a superparamagnetic behavior for sample M1. - Highlights: • A new method for synthesis of nanoparticles from mineral microparticles. • Search agreggate value to the mineral by mean nanoscience. • The stoichiometric ratio of the ions Fe 2+ and Fe 3+ from the mineral magnetite is synergistic

  4. Synthesis and characterization of magnetite nanoparticles from mineral magnetite

    Energy Technology Data Exchange (ETDEWEB)

    Morel, Mauricio, E-mail: mmorel@ing.uchile.cl [Laboratorio de Síntesis y Polímeros, Departamento de ciencias de los Materiales, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Santiago (Chile); Laboratorio de Materiales a Nanoescala, Departamento de ciencias de los Materiales, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Avenue Tupper 2069, Santiago (Chile); Martínez, Francisco, E-mail: polimart@ing.uchile.cl [Laboratorio de Síntesis y Polímeros, Departamento de ciencias de los Materiales, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Santiago (Chile); Mosquera, Edgar [Laboratorio de Materiales a Nanoescala, Departamento de ciencias de los Materiales, Facultad de Ciencias Físicas y Matemáticas, Universidad de Chile, Avenue Tupper 2069, Santiago (Chile)

    2013-10-15

    We have synthesized magnetite nanoparticles with sizes that range from 20 to 30 nm from mineral magnetite roughly 45 μm in size. The procedure consists in the dissolution of the mineral in an acidic medium and subsequent precipitation in a basic medium in the presence of oleic acid. Two experiments were conducted in different gaseous environments. The first was carried out in an environment exposed to air (M1) and the second in an N{sub 2} (M2) environment. The x-ray diffraction results showed a slight difference, which corresponds to the surface oxidation of magnetite. The sizes of the modified nanoparticles were determined through the Scherrer equation and transmission electron microscopy. An organic material mass loss corresponding to 18% was observed through a thermogravimetric analysis. The Fourier transform infrared spectroscopic analysis provides information about the type of bond that is formed on the surface of the nanoparticle, which corresponds to a bidentate chelate. The vibrating sample magnetometer results show a superparamagnetic behavior for sample M1. - Highlights: • A new method for synthesis of nanoparticles from mineral microparticles. • Search agreggate value to the mineral by mean nanoscience. • The stoichiometric ratio of the ions Fe{sup 2+} and Fe{sup 3+} from the mineral magnetite is synergistic.

  5. Aging study of the powdered magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Khan, Umar Saeed, E-mail: omar_aps@yahoo.co.uk [Department of Physics, University of Peshawar (Pakistan); Rahim, Abdur, E-mail: rahimkhan533@gmail.com [Interdisciplinary Research Centre in Biomedical Materials (IRCBM), COMSATS Institute of Information Technology, Lahore (Pakistan); Khan, Nasrullah [Department of Physics, Kohat University of Science and Technology, Kohat (Pakistan); Muhammad, Nawshad; Rehman, Fozia [Interdisciplinary Research Centre in Biomedical Materials (IRCBM), COMSATS Institute of Information Technology, Lahore (Pakistan); Ahmad, Khalid [Institute of Chemistry, State University of Campinas, PO Box 6154, 13083-970 Campinas, SP (Brazil); Iqbal, Jibran [College of Natural and Health Sciences, Zayed University, 144534 Abu Dhabi (United Arab Emirates)

    2017-03-01

    Magnetite nanoparticles were produced via co-precipitation method and then stored at room temperature for 6 years in aerobic atmosphere. Variations in the inherent solid phase and solid interfacial properties of the prepared magnetite nanoparticles were investigated. For this purpose the fresh and aged samples were characterized using transmission electron microscopy, vibrating sample magnetometer, X-ray diffractometer and energy dispersive X-ray spectrometer. The solid phase transformations of magnetite nanoparticles to maghemite nanoparticles as well as formation of other iron oxides were happened. After aging of 6 years, no change was occurred in the magnetic features; however increase in particle size from 9.6 to 18.5 measured by transmission electron microscopy was confirmed. The crystallite size and vibrating sample magnetometer values were measured before and after aging and found to increase from 8.98 nm and 47.23 emu/g to 16.18 nm and 58.36 emu/g respectively. The formation of other iron oxides, recrystallization and agglomeration during aging process, caused a significant decrease in the specific surface area from 124.43 to 45.00 m{sup 2}/g of the stored sample. - Highlights: • Magnetite nanoparticles (NPs) were produced via co-precipitation method. • Inherent solid phase and interfacial properties of NP were evaluated after 6 years. • The solid phase transformations of magnetite NPs to maghemite NPs was happened. • After aging of 6 years, no change was occurred in the magnetic features.

  6. Aging study of the powdered magnetite nanoparticles

    International Nuclear Information System (INIS)

    Khan, Umar Saeed; Rahim, Abdur; Khan, Nasrullah; Muhammad, Nawshad; Rehman, Fozia; Ahmad, Khalid; Iqbal, Jibran

    2017-01-01

    Magnetite nanoparticles were produced via co-precipitation method and then stored at room temperature for 6 years in aerobic atmosphere. Variations in the inherent solid phase and solid interfacial properties of the prepared magnetite nanoparticles were investigated. For this purpose the fresh and aged samples were characterized using transmission electron microscopy, vibrating sample magnetometer, X-ray diffractometer and energy dispersive X-ray spectrometer. The solid phase transformations of magnetite nanoparticles to maghemite nanoparticles as well as formation of other iron oxides were happened. After aging of 6 years, no change was occurred in the magnetic features; however increase in particle size from 9.6 to 18.5 measured by transmission electron microscopy was confirmed. The crystallite size and vibrating sample magnetometer values were measured before and after aging and found to increase from 8.98 nm and 47.23 emu/g to 16.18 nm and 58.36 emu/g respectively. The formation of other iron oxides, recrystallization and agglomeration during aging process, caused a significant decrease in the specific surface area from 124.43 to 45.00 m"2/g of the stored sample. - Highlights: • Magnetite nanoparticles (NPs) were produced via co-precipitation method. • Inherent solid phase and interfacial properties of NP were evaluated after 6 years. • The solid phase transformations of magnetite NPs to maghemite NPs was happened. • After aging of 6 years, no change was occurred in the magnetic features.

  7. Aqueous immune magnetite nanoparticles for immunoassay

    International Nuclear Information System (INIS)

    Zhang Guoxin; Liu Yanbo; Zhang Chunfu; Hu Weiqing; Xu Wanbang; Li Zheng; Liang Sheng; Cao Jinquan; Wang Yongxian

    2009-01-01

    Immune magnetite nanoparticles (MNPs) are prepared by four successive reactions, which are MNPs preparation, silica-coating, surface modification with amino group, and conjugation with bio-molecule, respectively. The crystal structure and morphology of intermediate products are characterized by XRD, TEM and AFM. Qualitative and quantitative assays for amino group on the MNPs' surface are made by FTIR and Organic Element Assay. Ultraviolet-visible absorption spectrum can indirectly illustrate the quantity of bio-molecule conjugated with MNPs. In addition, specific combination and nonspecific combination of immune MNPs are measured by commercial RIA box. The results show that the size of MNPs prepared is 10 ± 5 nm, and silica-coated MNPs with spinel structure have quasi-spherical morphology. Infrared absorption bands of -NH 2 are appeared around 3380-3200 cm -1 and 1650-1510 cm -1 , and the amino group content is 0.5 μmol -NH 2 per mg MNPs. The specific immune combination of immune MNPs is up to 75%, and nonspecific combination is under 5%.

  8. Study on magnetite nanoparticles synthesized by chemical method

    International Nuclear Information System (INIS)

    Pei Wenli; Kumada, H.; Natusme, T.; Saito, H.; Ishio, S.

    2007-01-01

    Magnetite nanoparticles with controlled size were synthesized by chemical method. Higher deposition temperature and a rapid-raising temperature procedure are favorable to particle size distribution and fabrication of monodisperse nanoparticles. The larger nanoparticles can be synthesized by the two-step method. The large nanoparticle (up to 25 nm) without agglomeration was successfully produced. The saturation magnetization of 11 nm magnetite particles was 45 emu/g at room temperature, which is smaller than that of bulk magnetite due to surface effect. Hysteresis of the magnetite nanoparticle was very small, indicating superparamagnetic behavior. The magnetic domains of the 11 nm magnetite nanoparticles were successfully observed by MFM

  9. Environmentally Compatible Synthesis of Superparamagnetic Magnetite (Fe3O4 Nanoparticles with Prehydrolysate from Corn Stover

    Directory of Open Access Journals (Sweden)

    Chunming Zheng

    2013-12-01

    Full Text Available An environmentally compatible and size-controlled method has been employed for synthesis of superparamagnetic magnetite nanoparticles with prehydrolysate from corn stover. Various characterizations involving X-ray diffraction (XRD, standard and high-resolution transmission electron microscopy (TEM and HRTEM, selected area electron diffraction (SAED, and thermogravimetric analysis (TGA have integrally confirmed the formation of magnetite nanoparticles with homogeneous morphology and the formation mechanism of magnetite only from ferric precursor. Organic materials in the prehydrolysate act as a bifunctional agent: (1 a reducing agent to reduce ferric ions to prepare magnetite with the coexistence of ferric and ferrous ions; and (2 a coating agent to prevent particle growth and agglomeration and to promote the formation of nanoscale and superparamagnetic magnetite. The size of the magnetite nanoparticles can be easily controlled by tailoring the reducing sugar concentration, reaction time, or hydrothermal temperature.

  10. Synthesis of magnetite nanoparticles obtained by the thermal decomposition method

    Energy Technology Data Exchange (ETDEWEB)

    Fonseca, Renilma de Sousa Pinheiro; Sinfronio, Francisco Savio Mendes; Menezes, Alan Silva de; Sharma, Surender Kumar; Silva, Fernando Carvalho, E-mail: renilma.ufma@gmail.com [Universidade Federal do Maranhao (UFMA), Sao Luis, MA (Brazil); Moscoso-Londono, Oscar; Muraca, Diego; Knobel, Marcelo [Universidade Estadual de Campinas (UNICAMP), SP (Brazil)

    2016-07-01

    Full text: Magnetite nanoparticles have found numerous applications in biomedicine such as magnetic separation, drug delivery, magnetic resonance imaging (MRI) and hyperthermia agents [1]. These features are related to their superparamagnetic behavior, low toxicity and high functionalization [2]. Thus, this work aims to obtain oleylamine-coated magnetite nanoparticles by means of thermal decomposition method at different temperatures and reaction time. All samples were characterized by FTIR, XRD and SQUID magnetometer. The infrared spectra showed two vibrational modes at 2920 and 2850 cm{sup -1}, assigned to the asymmetrical and symmetrical stretching of C-H groups of the oleic acid and oleylamine, respectively. The XRD pattern of the samples confirmed the formation of magnetite phase (ICSD 36314) at all temperatures. The average size of the crystallites was determined by Debye-Scherrer equation with values in the range of 1.1-1.5 nm. Field-cooled and zero field-cooled analysis demonstrate that the blocking temperature (T{sub B}) is below room temperature in all cases, indicating that all magnetite nanoparticles are superparamagnetic at room temperature and ferrimagnetic at low temperature. (author)

  11. Synthesis of magnetite nanoparticles obtained by the thermal decomposition method

    International Nuclear Information System (INIS)

    Fonseca, Renilma de Sousa Pinheiro; Sinfronio, Francisco Savio Mendes; Menezes, Alan Silva de; Sharma, Surender Kumar; Silva, Fernando Carvalho; Moscoso-Londono, Oscar; Muraca, Diego; Knobel, Marcelo

    2016-01-01

    Full text: Magnetite nanoparticles have found numerous applications in biomedicine such as magnetic separation, drug delivery, magnetic resonance imaging (MRI) and hyperthermia agents [1]. These features are related to their superparamagnetic behavior, low toxicity and high functionalization [2]. Thus, this work aims to obtain oleylamine-coated magnetite nanoparticles by means of thermal decomposition method at different temperatures and reaction time. All samples were characterized by FTIR, XRD and SQUID magnetometer. The infrared spectra showed two vibrational modes at 2920 and 2850 cm -1 , assigned to the asymmetrical and symmetrical stretching of C-H groups of the oleic acid and oleylamine, respectively. The XRD pattern of the samples confirmed the formation of magnetite phase (ICSD 36314) at all temperatures. The average size of the crystallites was determined by Debye-Scherrer equation with values in the range of 1.1-1.5 nm. Field-cooled and zero field-cooled analysis demonstrate that the blocking temperature (T B ) is below room temperature in all cases, indicating that all magnetite nanoparticles are superparamagnetic at room temperature and ferrimagnetic at low temperature. (author)

  12. Preconcentration of trace amounts of lead in water samples with cetyltrimethylammonium bromide coated magnetite nanoparticles and its determination by flame atomic absorption spectrometry

    Directory of Open Access Journals (Sweden)

    Mohammad Faraji

    2016-11-01

    Full Text Available A sensitive and simple magnetic solid phase extraction procedure was presented for the preconcentration of lead ions in environmental water samples. In the present study, lead ions form complexes with 1-(2-pyridilazo-2-naphthol reagent (PAN in basic medium, and then are quantitatively extracted to the surface of cetyltrimethylammonium bromide (CTAB-coated magnetite nanoparticles (Fe3O4 NPs. After magnetic separation of adsorbent, the adsorbent was eluted with 0.5% (v/v HCl in methanol prior to its analysis by flame atomic absorption spectrometry (FAAS. The pH of sample, concentrations of PAN, amounts of CTAB and Fe3O4 NPs, sample volume and desorption conditions were optimized. Under optimum conditions, the calibration curve was linear in the range of 0.05–100 ng mL−1 with R2 = 0.9996. Detection and quantification limits of the proposed method were 0.005 and 0.05 ng mL−1, respectively. Enhancement factor of 1050 was achieved using this method to extract 1000 mL of different environmental water samples. Compared with conventional solid phase extraction methods, the advantages of this method still include easy preparation of sorbents, short times of sample pre-treatment, high extraction yield, and high breakthrough volume. It shows great analytical potential in preconcentration of lead from large volume water samples.

  13. A simple and fast method based on mixed hemimicelles coated magnetite nanoparticles for simultaneous extraction of acidic and basic pollutants.

    Science.gov (United States)

    Asgharinezhad, Ali Akbar; Ebrahimzadeh, Homeira

    2016-01-01

    One of the considerable and disputable areas in analytical chemistry is a single-step simultaneous extraction of acidic and basic pollutants. In this research, a simple and fast coextraction of acidic and basic pollutants (with different polarities) with the aid of magnetic dispersive micro-solid phase extraction based on mixed hemimicelles assembly was introduced for the first time. Cetyltrimethylammonium bromide (CTAB)-coated Fe3O4 nanoparticles as an efficient sorbent was successfully applied to adsorb 4-nitrophenol and 4-chlorophenol as two acidic and chlorinated aromatic amines as basic model compounds. Using a central composite design methodology combined with desirability function approach, the optimal experimental conditions were evaluated. The opted conditions were pH = 10; concentration of CTAB = 0.86 mmol L(-1); sorbent amount = 55.5 mg; sorption time = 11.0 min; no salt addition to the sample, type, and volume of the eluent = 120 μL methanol containing 5% acetic acid and 0.01 mol L(-1) HCl; and elution time = 1.0 min. Under the optimum conditions, detection limits and linear dynamic ranges were achieved in the range of 0.05-0.1 and 0.25-500 μg L(-1), respectively. The percent of extraction recoveries and relative standard deviations (n = 5) were in the range of 71.4-98.0 and 4.5-6.5, respectively. The performance of the optimized method was certified by coextraction of other acidic and basic compounds. Ultimately, the applicability of the method was successfully confirmed by the extraction and determination of the target analytes in various water samples, and satisfactory results were obtained.

  14. Preparation of alumina-coated magnetite nanoparticle for extraction of trimethoprim from environmental water samples based on mixed hemimicelles solid-phase extraction.

    Science.gov (United States)

    Sun, Lei; Zhang, Chuanzhou; Chen, Ligang; Liu, Jun; Jin, Haiyan; Xu, Haoyan; Ding, Lan

    2009-04-13

    In this study, a new type of alumina-coated magnetite nanoparticles (Fe(3)O(4)/Al(2)O(3) NPs) modified by the surfactant sodium dodecyl sulfate (SDS) has been successfully synthesized and applied for extraction of trimethoprim (TMP) from environmental water samples based on mixed hemimicelles solid-phase extraction (MHSPE). The coating of alumina on Fe(3)O(4) NPs not only avoids the dissolving of Fe(3)O(4) NPs in acidic solution, but also extends their application without sacrificing their unique magnetization characteristics. Due to the high surface area of these new sorbents and the excellent adsorption capacity after surface modification by SDS, satisfactory concentration factor and extraction recoveries can be produced with only 0.1g Fe(3)O(4)/Al(2)O(3) NPs. Main factors affecting the adsolubilization of TMP such as the amount of SDS, pH value, standing time, desorption solvent and maximal extraction volume were optimized. Under the selected conditions, TMP could be quantitatively extracted. The recoveries of TMP by analyzing the four spiked water samples were between 67 and 86%, and the relative standard deviation (RSD) ranged from 2 to 6%. Detection and quantification limits of the proposed method were 0.09 and 0.24 microg L(-1), respectively. Concentration factor of 1000 was achieved using this method to extract 500 mL of different environmental water samples. Compared with conventional SPE methods, the advantages of this new Fe(3)O(4)/Al(2)O(3) NPs MHSPE method still include easy preparation and regeneration of sorbents, short times of sample pretreatment, high extraction yields, and high breakthrough volumes. It shows great analytical potential in preconcentration of organic compounds from large volume water samples.

  15. Improvement of interaction between PVA and chitosan via magnetite nanoparticles for drug delivery application.

    Science.gov (United States)

    Shagholani, Hamidreza; Ghoreishi, Sayed Mehdi; Mousazadeh, Mohammad

    2015-01-01

    Magnetite nanoparticles were synthesized by coprecipitation under ultrasonication followed by coating with chitosan. Polyvinyl alcohol (PVA) is then combined with the chitosan that coated the magnetite nanoparticles. The combination occurs by hydrogen binding and ionic cross-linking of the amino and hydroxyl groups of chitosan and PVA respectively. The magnetite nanoparticles have an average size of 10.62 nm that was confirmed by TEM. The VSM measurements showed that nanoparticles were superparamagnetic. The coatings on the core nanoparticles were estimated by AAS and the attachments of coating to the nanoparticles were confirmed by FT-IR analysis. Physicochemical properties of nanoparticles were measured by DLS and zeta potential. Naked magnetite, chitosan and PVA coating have zeta potential of +36.4, +48.1 and -12.5 mV respectively. The unspecific adsorption and interaction between nanoparticles and bovine serum albumin (BSA) were investigated systematically by UV-vis spectroscopy method. The nanoparticles that were modified by PVA present low protein adsorption, which makes them a practical choice for preventing opsonization in clinical application and drug delivery. Copyright © 2015. Published by Elsevier B.V.

  16. Magnetite and magnetite/silver core/shell nanoparticles with diluted magnet-like behavior

    International Nuclear Information System (INIS)

    Garza-Navarro, Marco; Torres-Castro, Alejandro; Gonzalez, Virgilio; Ortiz, Ubaldo; De la Rosa, Elder

    2010-01-01

    In the present work is reported the use of the biopolymer chitosan as template for the preparation of magnetite and magnetite/silver core/shell nanoparticles systems, following a two step procedure of magnetite nanoparticles in situ precipitation and subsequent silver ions reduction. The crystalline and morphological characteristics of both magnetite and magnetite/silver core/shell nanoparticles systems were analyzed by high resolution transmission electron microscopy (HRTEM) and nanobeam diffraction patterns (NBD). The results of these studies corroborate the core/shell morphology and the crystalline structure of the magnetite core and the silver shell. Moreover, magnetization temperature dependent, M(T), measurements show an unusual diluted magnetic behavior attributed to the dilution of the magnetic ordering in the magnetite and magnetite/silver core/shell nanoparticles systems. - Graphical abstract: Biopolymer chitosan was used as stabilization media to synthesize both magnetite and magnetite/silver core/shell nanoparticles. Results of HRTEM and NBD patterns confirm core/shell morphology of the obtained nanoparticles. It was found that the composites show diluted magnet-like behavior.

  17. Synthesis of functionalized magnetite nanoparticles to use as liver targeting MRI contrast agent

    International Nuclear Information System (INIS)

    Yazdani, Farshad; Fattahi, Bahare; Azizi, Najmodin

    2016-01-01

    The aim of this research was the preparation of functionalized magnetite nanoparticles to use as a liver targeting contrast agent in magnetic resonance imaging (MRI). For this purpose, Fe_3O_4 nanoparticles were synthesized via the co-precipitation method. The synthesized nanoparticles were coated with silica via the Stober method and finally the coated nanoparticles were functionalized with mebrofenin. Formation of crystalline magnetite particles was confirmed by X-ray diffraction (XRD) analysis. The Fourier transform infrared spectroscopy (FTIR) and energy dispersive X-ray analyzer (EDX) of the final product showed that silica had been effectively bonded onto the surface of the magnetite nanoparticles and the coated nanoparticles functionalized with mebrofenin. The magnetic resonance imaging of the functional nanoparticles showed that the Fe_3O_4–SiO_2-mebrofenin composite is an effective MRI contrast agent for liver targeting. - Highlights: • Superparamagnetic magnetite nanoparticles have been synthesized by simple and economical method. • Preperation of functional MNPs as a MRI contrast agent for liver targeting. • Gaining a good r_2 relaxivity of the coated functional nanoparticles.

  18. Synthesis and characterization of Gd-doped magnetite nanoparticles

    International Nuclear Information System (INIS)

    Zhang, Honghu; Malik, Vikash; Mallapragada, Surya; Akinc, Mufit

    2017-01-01

    Synthesis of magnetite nanoparticles has attracted increasing interest due to their importance in biomedical and technological applications. Tunable magnetic properties of magnetite nanoparticles to meet specific requirements will greatly expand the spectrum of applications. Tremendous efforts have been devoted to studying and controlling the size, shape and magnetic properties of magnetite nanoparticles. Here we investigate gadolinium (Gd) doping to influence the growth process as well as magnetic properties of magnetite nanocrystals via a simple co-precipitation method under mild conditions in aqueous media. Gd doping was found to affect the growth process leading to synthesis of controllable particle sizes under the conditions tested (0–10 at% Gd"3"+). Typically, undoped and 5 at% Gd-doped magnetite nanoparticles were found to have crystal sizes of about 18 and 44 nm, respectively, supported by X-ray diffraction and transmission electron microscopy. Our results showed that Gd-doped nanoparticles retained the magnetite crystal structure, with Gd"3"+ randomly incorporated in the crystal lattice, probably in the octahedral sites. The composition of 5 at% Gd-doped magnetite was Fe_(_3_−_x_)Gd_xO_4 (x=0.085±0.002), as determined by inductively coupled plasma mass spectrometry. 5 at% Gd-doped nanoparticles exhibited ferrimagnetic properties with small coercivity (~65 Oe) and slightly decreased magnetization at 260 K in contrast to the undoped, superparamagnetic magnetite nanoparticles. Templation by the bacterial biomineralization protein Mms6 did not appear to affect the growth of the Gd-doped magnetite particles synthesized by this method. - Highlights: • Gd-doped magnetite nanoparticles are synthesized via aqueous co-precipitation method under mild conditions. • Gd doping affects growth of magnetite nanoparticles leading to tunable particle size. • Gd-doped magnetite nanoparticles exhibit ferrimagnetic properties.

  19. Synthesis of magnetite nanoparticles using electrochemical oxidation

    Directory of Open Access Journals (Sweden)

    Ye. Ya. Levitin

    2014-08-01

    Full Text Available The monodisperse magnetite nanoparticles are promising for use in the biomedical industry for targeted drug delivery, cell separation and biochemical products, Magnetic Resonance Imaging, immunological studies, etc. Classic method for the synthesis of magnetite is the chemical condensation Elmore’s, it is simple and cheap, but it is complicated by the formation of side compounds which impair the magnetic properties of the final product. Biological and medical purposes require high purity magnetite nanoparticles. Electrochemical methods of producing nanoparticles of magnetite acquire significant spread. The kinetics of electrochemical processes are a function of a larger number of parameters than the kinetics of conventional chemical reaction, thus electrochemical reactions can be thinner and more completely adjusted to give a predetermined size nanoparticles. In the kinetics of the electrochemical oxidation and reduction the important role is played by the nature of the electrode. In many industrial processes, it is advisable to use lead dioxide anodes with titanium current lead. Purpose of the work To determine the optimum conditions of electrochemical oxidation of Fe2+ Fe3+to produce magnetite with high purity and improved magnetic characteristics. Materials and methods Electrochemical studies were carried out in a glass cell ЯСЭ-2 using a potentiostat ПИ-50-1.1 and a recording device ПДА1. Reference electrode - silver chloride ЭВЛ1М 3.1, potentials listed on the hydrogen scale. The test solution contained 80 g/ l FeSO4×7H2O and H2SO4(to pH 1. The pH of the solution was measured with a pH–meter « рН–150». Concentration ratio of Fe3+/Fe2+in the solution was measured by permanganometric method. Magnetite particle sizes were measured by an electron microscope computer ЭВМ-100Л, an increasing is 2×105. Saturation magnetization was evaluated by the magnetization curve, for the measured sample in the field with strength

  20. One step facile synthesis of ferromagnetic magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Suppiah, Durga Devi; Abd Hamid, Sharifah Bee, E-mail: sharifahbee@um.edu.my

    2016-09-15

    The ferromagnetic properties of magnetite (Fe{sub 3}O{sub 4}) were influenced by the nanoparticle size, hence importance were given to the synthesis method. This paper clearly shows that magnetite nanoparticles were successfully synthesized by employing one step controlled precipitation method using a single salt (Iron(II) sulfate) iron precursor. The acquired titration curve from this method provides vital information on the possible reaction mechanism leading to the magnetite (Fe{sub 3}O{sub 4}) nanoparticles formation. Goethite (α-FeOOH) was obtained at pH 4, while the continuous addition of hydroxyl ions (OH{sup −}) forms iron hydroxides (Fe(OH){sub 2}). This subsequently reacts with the goethite, producing magnetite (Fe{sub 3}O{sub 4}) at pH 10. Spectroscopy studies validate the magnetite phase existence while structural and morphology analysis illustrates cubic shaped magnetite with an average size of 35 nm was obtained. The synthesized magnetite might be superparamagnetic though lower saturation magnetization (67.5 emu/g) measured at room temperature as compared to bulk magnetite. However the nanoparticles surface anisotropy leads to higher remanence (12 emu/g) and coercivity (117.7 G) making the synthesized magnetite an excellent candidate to be utilized in recording devices. The understanding of the magnetite synthesis mechanism can not only be used to achieve even smaller magnetite nanoparticles but also to prepare different types of iron oxides hydroxides using different iron precursor source. - Highlights: • Magnetite strong magnetism properties make it versatile in various applications including biomedical and electromagnetic materials. • Sulfate (SO{sub 4}{sup 2−}) anion plays a major role in the structure control of iron oxide during synthesis. • Phase pure magnetite nanoparticles with high magnetism properties can be obtained using a single salt (SO{sub 4}{sup 2−}) method.

  1. Synthesis and characterization of magnetite nanoparticles via the chemical co-precipitation method

    International Nuclear Information System (INIS)

    Petcharoen, K.; Sirivat, A.

    2012-01-01

    Highlights: ► Size-controlled magnetite nanoparticles were prepared via the chemical co-precipitation method in the range of 10–40 nm. ► The electrical conductivity of the smallest particle size is 1.3 × 10 −3 S/cm which belongs to the semiconductor material group. ► The surface modification of magnetite nanoparticles can provide the suspension stability over 1 week. - Abstract: Magnetite nanoparticles were synthesized via the chemical co-precipitation method using ammonium hydroxide as the precipitating agent. The size of the magnetite nanoparticles was carefully controlled by varying the reaction temperature and through the surface modification. Herein, the hexanoic acid and oleic acid were introduced as the coating agents during the initial crystallization phase of the magnetite. Their structure and morphology were characterized by the Fourier transform infrared spectroscopy (FTIR), the X-ray diffraction (XRD) and the field-emission scanning electron microscopy (FE-SEM). Moreover, the electrical and magnetic properties were studied by using a conductivity meter and a vibrating sample magnetometer (VSM), respectively. Both of the bare magnetite and the coated magnetite were of the cubic spinel structure and the spherical-shaped morphology. The reaction temperature and the surface modification critically affected the particle size, the electrical conductivity, and the magnetic properties of these particles. The particle size of the magnetite was increased through the surface modification and reaction temperature. In this study, the particle size of the magnetite nanoparticles was successfully controlled to be in the range of 10–40 nm, suitable for various biomedical applications. The electrical conductivity of the smallest particle size was 1.3 × 10 −3 S/cm, within the semi-conductive materials range, which was higher than that of the largest particle by about 5 times. All of the magnetite nanoparticles showed the superparamagnetic behavior with

  2. Chemical and thermal stability of core-shelled magnetite nanoparticles and solid silica

    Science.gov (United States)

    Cendrowski, Krzysztof; Sikora, Pawel; Zielinska, Beata; Horszczaruk, Elzbieta; Mijowska, Ewa

    2017-06-01

    Pristine nanoparticles of magnetite were coated by solid silica shell forming core/shell structure. 20 nm thick silica coating significantly enhanced the chemical and thermal stability of the iron oxide. Chemical and thermal stability of this structure has been compared to the magnetite coated by mesoporous shell and pristine magnetite nanoparticles. It is assumed that six-membered silica rings in a solid silica shell limit the rate of oxygen diffusion during thermal treatment in air and prevent the access of HCl molecules to the core during chemical etching. Therefore, the core/shell structure with a solid shell requires a longer time to induce the oxidation of iron oxide to a higher oxidation state and, basically, even strong concentrated acid such as HCl is not able to dissolve it totally in one month. This leads to the desired performance of the material in potential applications such as catalysis and environmental protection.

  3. Brownian rotational relaxation and power absorption in magnetite nanoparticles

    International Nuclear Information System (INIS)

    Goya, G.F.; Fernandez-Pacheco, R.; Arruebo, M.; Cassinelli, N.; Ibarra, M.R.

    2007-01-01

    We present a study of the power absorption efficiency in several magnetite-based colloids, to asses their potential as magnetic inductive hyperthermia (MIH) agents. Relaxation times τ were measured through the imaginary susceptibility component χ ' '(T), and analyzed within Debye's theory of dipolar fluid. The results indicated Brownian rotational relaxation and allowed to calculate the hydrodynamic radius close to the values obtained from photon correlation. The study of the colloid performances as power absorbers showed no detectable increase of temperature for dextran-coated Fe 3 O 4 nanoparticles, whereas a second Fe 3 O 4 -based dispersion of similar concentration could be heated up to 12K after 30min under similar experimental conditions. The different power absorption efficiencies are discussed in terms of the magnetic structure of the nanoparticles

  4. Brownian rotational relaxation and power absorption in magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Goya, G.F. [Institute of Nanoscience of Aragon (INA), University of Zaragoza, 50009 Zaragoza (Spain)]. E-mail: goya@unizar.es; Fernandez-Pacheco, R. [Institute of Nanoscience of Aragon (INA), University of Zaragoza, 50009 Zaragoza (Spain); Arruebo, M. [Institute of Nanoscience of Aragon (INA), University of Zaragoza, 50009 Zaragoza (Spain); Cassinelli, N. [Electronics Division, Bauer and Associates, Buenos Aires (Argentina); Facultad de Ingenieria, UNLP (Argentina); Ibarra, M.R. [Institute of Nanoscience of Aragon (INA), University of Zaragoza, 50009 Zaragoza (Spain)

    2007-09-15

    We present a study of the power absorption efficiency in several magnetite-based colloids, to asses their potential as magnetic inductive hyperthermia (MIH) agents. Relaxation times {tau} were measured through the imaginary susceptibility component {chi}{sup '}'(T), and analyzed within Debye's theory of dipolar fluid. The results indicated Brownian rotational relaxation and allowed to calculate the hydrodynamic radius close to the values obtained from photon correlation. The study of the colloid performances as power absorbers showed no detectable increase of temperature for dextran-coated Fe{sub 3}O{sub 4} nanoparticles, whereas a second Fe{sub 3}O{sub 4}-based dispersion of similar concentration could be heated up to 12K after 30min under similar experimental conditions. The different power absorption efficiencies are discussed in terms of the magnetic structure of the nanoparticles.

  5. Nano-magnetite coated with gold: alternative oncological therapy with magnetic hyperthermia

    International Nuclear Information System (INIS)

    Cordova F, T.; Jimenez G, O.; Basurto I, G.; Martinez E, J. C.

    2017-10-01

    Localized hyperthermia performed through the use of nanoparticles is one of the most promising procedures for the cancer treatment. In this work, the synthesis of magnetite nanoparticles (Fe 2 O 3 ) was carried out using the thermal decomposition method. Subsequently, these nanoparticles were coated with gold and suspended in aqueous phase. As a result, nanoparticles capable of being heated by the application of an alternating magnetic field or through the use of infrared radiation were obtained. As an additional feature, these nanoparticles are biocompatible thanks to their golden coating. The synthesized nanoparticles can be functionalized by the conjugation of a molecule (aptamer, antibody, peptide, etc.) whose target is a cancer cell in order to adhere to it the nanoparticle-marker complex, to subsequently carry out a heating with the objective of induce cell death. In conclusion, the synthesized nanoparticles allow providing an alternative treatment for cancer through the use of localized hyperthermia, either using magnetic or infrared heating. (Author)

  6. Sonochemical preparation of magnetite nanoparticles by reverse precipitation method

    OpenAIRE

    Shuto, Tatsuya; Nakagoe, Osamu; Tanabe, Shuji

    2008-01-01

    Magnetic iron oxide nanoparticles were successfully prepared by reverse precipitation method with the assistance of ultrasound. Obtained nanoparticles were identified as magnetite (Fe_3O_4) by XRD measurement. It was found that obtained magnetite nanoparticles have small sizes (about 10.7 ±2.9 nm in diameter) and spherical shape by TEM observations. In reverse precipitation method, the dropping conditions of aqueous FeSO_4 solution affect on the sizes and uniformity of the products.

  7. Synthesis of magnetite nanoparticles in the presence of aminoacids

    International Nuclear Information System (INIS)

    Marinescu, Gabriela; Patron, Luminita; Culita, Daniela C.; Neagoe, Cristian; Lepadatu, Costinel I.; Balint, Ioan; Bessais, Lotfi; Cizmas, Corneliu Bazil

    2006-01-01

    A new synthesis route to prepare magnetite nanoparticles in only one step is described. The precipitation of magnetite is performed in the presence of aminoacid solution. The experimental protocol is original and the nanomagnetites are characterized by XRD, FTIR, TEM and SQUID magnetometry. A theoretical study of the consistent experimental results was performed using QSPR (Quantitative Structure Property Relationsheep). According with these studies the synthesized nanoparticles seem to be organized into a core-shell system, where the inner-core is formed from unit cells of magnetite. A way to control the self-assembly and the physical properties of the synthesized nanoparticles consists in their correlation with descriptors representing the aminoacid chemical structures. Using quantum chemical as well as the other simplest original descriptors it was found a relationship between the used aminoacids and the magnetization, nanoparticles diameter, magnetite core diameter and the (Fe 3 O 4 ) 8 cells in each nanoparticle core

  8. Surfactant effects in magnetite nanoparticles of controlled size

    International Nuclear Information System (INIS)

    Guardia, P.; Batlle-Brugal, B.; Roca, A.G.; Iglesias, O.; Morales, M.P.; Serna, C.J.; Labarta, A.; Batlle, X.

    2007-01-01

    Magnetite Fe 3 O 4 nanoparticles of controlled size within 6 and 20 nm in diameter were synthesised by thermal decomposition of an iron organic precursor in an organic medium. Particles were coated with oleic acid. For all samples studied, saturation magnetisation M s is size-independent, and reaches a value close to that expected for bulk magnetite, in contrast to results in small particle systems for which M s is usually much smaller due to surface spin disorder. The coercive field for the 6 nm particles is in agreement with coherent rotation, taking the bulk magnetocrystalline anisotropy into account. Both results suggest that the oleic acid molecules covalently bonded to the nanoparticle surface yield a strong reduction in the surface spin disorder. However, although the saturated state may be similar, the approach to saturation is different and, in particular, the high-field differential susceptibility is one order of magnitude larger than in bulk materials. The relevance of these results in biomedical applications is discussed

  9. Electro-precipitation of magnetite nanoparticles: an electrochemical study

    OpenAIRE

    Ibrahim, Mona; Groenen-Serrano, Karine; Noé, Laure; Garcia, Cécile; Verelst, Marc

    2009-01-01

    Nanoparticles of magnetites (Fe3O4) are synthesized with a new process based on electro-precipitation in ethanol medium. A mechanism pathway is proposed consisting of a Fe(OH)3 precipitation followed by the reduction of iron hydroxide to magnetite in the presence of hydroxyl ions which are enerated at the cathode.

  10. Structure and superparamagnetic behaviour of magnetite nanoparticles in cellulose beads

    Energy Technology Data Exchange (ETDEWEB)

    Correa, Jose R., E-mail: correa@fq.uh.cu [Department of General Chemistry, Faculty of Chemistry, University of Havana, Zapata and G, Havana City 10400 (Cuba); Bordallo, Eduardo [Sugar Cane-Cellulose Research Center, Cuba-9, Quivican (Cuba); Canetti, Dora [Department of Inorganic Chemistry, Faculty of Chemistry, University of Havana, Zapata and G, Havana City 10400 (Cuba); Leon, Vivian [Sugar Cane-Cellulose Research Center, Cuba-9, Quivican (Cuba); Otero-Diaz, Luis C. [Department of Inorganic Chemistry-1, Complutense University of Madrid, Madrid 28040 (Spain); Electron Microscopy Center, Complutense University of Madrid, Madrid 28040 (Spain); Negro, Carlos [Chemical Engineering Department, Complutense University of Madrid, Madrid 28040 (Spain); Gomez, Adrian [Electron Microscopy Center, Complutense University of Madrid, Madrid 28040 (Spain); Saez-Puche, Regino [Department of Inorganic Chemistry-1, Complutense University of Madrid, Madrid 28040 (Spain)

    2010-08-15

    Superparamagnetic magnetite nanoparticles were obtained starting from a mixture of iron(II) and iron(III) solutions in a preset total iron concentration from 0.04 to 0.8 mol l{sup -1} with ammonia at 25 and 70 {sup o}C. The regeneration of cellulose from viscose produces micrometrical spherical cellulose beads in which synthetic magnetite were embedded. The characterization of cellulose-magnetite beads by X-ray diffraction, Scanning and Transmission Electron Microscopy and magnetic measurement is reported. X-ray diffraction patterns indicate that the higher is the total iron concentration and temperature the higher is the crystal size of the magnetite obtained. Transmission Electron Microscopy studies of cellulose-magnetite beads revealed the distribution of magnetite nanoparticles inside pores of hundred nanometers. Magnetite as well as the cellulose-magnetite composites exhibit superparamagnetic characteristics. Field cooling and zero field cooling magnetic susceptibility measurements confirm the superparamagnetic behaviour and the blocking temperature for the magnetite with a mean size of 12.5 nm, which is 200 K.

  11. Release Behavior and Toxicity Profiles towards Leukemia (WEHI-3B) Cell Lines of 6-Mercaptopurine-PEG-Coated Magnetite Nanoparticles Delivery System

    OpenAIRE

    Dorniani, Dena; Kura, Aminu Umar; Hussein-Al-Ali, Samer Hasan; Hussein, Mohd Zobir bin; Fakurazi, Sharida; Shaari, Abdul Halim; Ahmad, Zalinah

    2014-01-01

    The coating of an active drug, 6-mercaptopurine, into the iron oxide nanoparticles-polyethylene glycol (FNPs-PEG) in order to form a new nanocomposite, FPEGMP-2, was accomplished using coprecipitation technique. The resulting nanosized with a narrow size distribution magnetic polymeric particles show the superparamagnetic properties with 38.6 emu/g saturation magnetization at room temperature. Fourier transform infrared spectroscopy and the thermal analysis study supported the formation of th...

  12. Synthesis and characterization of magnetite/PLGA/chitosan nanoparticles

    Science.gov (United States)

    Ibarra, Jaime; Melendres, Julio; Almada, Mario; Burboa, María G.; Taboada, Pablo; Juárez, Josué; Valdez, Miguel A.

    2015-09-01

    In this work, we report the synthesis and characterization of a new hybrid nanoparticles system performed by magnetite nanoparticles, loaded in a PLGA matrix, and stabilized by different concentrations of chitosan. Magnetite nanoparticles were hydrophobized with oleic acid and entrapped in a PLGA matrix by the emulsion solvent evaporation method, after that, magnetite/PLGA/chitosan nanoparticles were obtained by adding dropwise magnetite/PLGA nanoparticles in chitosan solutions. Magnetite/PLGA nanoparticles produced with different molar ratios did not show significant differences in size and the 3:1 molar ratio showed best spherical shapes as well as uniform particle size. Isothermal titration calorimetry studies demonstrated that the first stage of PLGA-chitosan interaction is mostly regulated by electrostatic forces. Based on a single set of identical sites model, we obtained for the average number of binding sites a value of 3.4, which can be considered as the number of chitosan chains per nanoparticle. This value was confirmed by using a model based on the DLVO theory and fitting zeta potential measurements of magnetite/PLGA/chitosan nanoparticles. From the adjusted parameters, we found that an average number of chitosan molecules of 3.6 per nanoparticle are attached onto the surface of the PLGA matrix. Finally, we evaluated the effect of surface charge of nanoparticles on a membrane model of endothelial cells performed by a mixture of three phospholipids at the air-water interface. Different isotherms and adsorption curves show that cationic surface of charged nanoparticles strongly interact with the phospholipids mixture and these results can be the basis of future experiments to understand the nanoparticles- cell membrane interaction.

  13. Synthesis and characterization of magnetite/PLGA/chitosan nanoparticles

    International Nuclear Information System (INIS)

    Ibarra, Jaime; Melendres, Julio; Almada, Mario; Juárez, Josué; Valdez, Miguel A; Burboa, María G; Taboada, Pablo

    2015-01-01

    In this work, we report the synthesis and characterization of a new hybrid nanoparticles system performed by magnetite nanoparticles, loaded in a PLGA matrix, and stabilized by different concentrations of chitosan. Magnetite nanoparticles were hydrophobized with oleic acid and entrapped in a PLGA matrix by the emulsion solvent evaporation method, after that, magnetite/PLGA/chitosan nanoparticles were obtained by adding dropwise magnetite/PLGA nanoparticles in chitosan solutions. Magnetite/PLGA nanoparticles produced with different molar ratios did not show significant differences in size and the 3:1 molar ratio showed best spherical shapes as well as uniform particle size. Isothermal titration calorimetry studies demonstrated that the first stage of PLGA-chitosan interaction is mostly regulated by electrostatic forces. Based on a single set of identical sites model, we obtained for the average number of binding sites a value of 3.4, which can be considered as the number of chitosan chains per nanoparticle. This value was confirmed by using a model based on the DLVO theory and fitting zeta potential measurements of magnetite/PLGA/chitosan nanoparticles. From the adjusted parameters, we found that an average number of chitosan molecules of 3.6 per nanoparticle are attached onto the surface of the PLGA matrix. Finally, we evaluated the effect of surface charge of nanoparticles on a membrane model of endothelial cells performed by a mixture of three phospholipids at the air–water interface. Different isotherms and adsorption curves show that cationic surface of charged nanoparticles strongly interact with the phospholipids mixture and these results can be the basis of future experiments to understand the nanoparticles- cell membrane interaction. (paper)

  14. Dodecylbenzene sulfonate-coated magnetite nanoparticles as a new adsorbent for solid phase extraction-spectrophotometric determination of ultra trace amounts of ammonium in water samples.

    Science.gov (United States)

    Eskandari, Habibollah; Shariati, Mohammad Reza

    2011-10-17

    A new method was proposed for the determination of ammonium based on the preconcentration with dodecylbenzene sulfonate modified magnetite nanoparticles. Ammonium was oxidized to nitrite by hypobromite and then the nitrite produced was determined spectrophotometrically, using sulfabenzamide and N-(1-naphthyl) ethylenediamine after solid phase extraction. The azo dye produced was desorbed by an appropriate small volume of sodium hydroxide prior to the absorbance measurement. The linear calibration graphs were obtained in the concentration range of 0.03-6.00 ng mL(-1) ammonium. The relative standard deviation and recovery percents were 1.0 and 99.0, respectively, for 1.0 ng mL(-1) ammonium, and the limit of detection was 3.2 ng L(-1) ammonium. The interfering effects of a large number of diverse ions on the determination of ammonium were studied. The method was applied to the determination of ammonium in various types of water resources. The results revealed a high efficiency for the recommended ammonium determination method. Copyright © 2011 Elsevier B.V. All rights reserved.

  15. The magnetic introduction of magnetite nanoparticles into live cells for radiosensibility enhancement

    Energy Technology Data Exchange (ETDEWEB)

    Yurenya, Anton Y., E-mail: antonyurenya@gmail.com [National Research Center “Kurchatov Institute”, Moscow (Russian Federation); Faculty of Physics, Lomonosov Moscow State University, Moscow (Russian Federation); Polikarpov, Mikhail A. [National Research Center “Kurchatov Institute”, Moscow (Russian Federation); Chukalova, Aynur A. [National Research Center “Kurchatov Institute”, Moscow (Russian Federation); Moscow Institute of Physics and Technology, Moscow (Russian Federation); Moskaleva, Elizaveta Y.; Taldenkov, Alexander N. [National Research Center “Kurchatov Institute”, Moscow (Russian Federation); Panchenko, Vladislav Y. [National Research Center “Kurchatov Institute”, Moscow (Russian Federation); Faculty of Physics, Lomonosov Moscow State University, Moscow (Russian Federation)

    2017-04-01

    Earlier we proposed a new radiotherapy enhancement method that entails the administration of {sup 57}Fe iron-oxide nanoparticles into the cells . Within this work we were prompt to investigate the capability of iron oxide nanoparticles with monolayer coating to penetrate into live cells. Magnetite particle samples were synthesized and stabilized with HCl or citric acid. The cells were incubated in the presence of nanoparticles for 1 h, washed and dried. To distinguish inside-cell particles from outside ones a set of experiments with low temperature incubation was carried out. Several cell samples were prepared in the presence of an external magnetic field in order to study the possibility of the nanoparticle uptake enhancement. To evaluate the amount of particles in each cell sample we used a SQUID-magnetometer. The nanoparticle suspension with HCl stabilization turned to be inadequate for intracellular introduction. Approximately 2·10{sup 5} particles with citric acid covering conjugated with each cell after incubation at normal conditions. An application of an external magnetic field increased this amount up to 10{sup 7} particles/cell. Most probably much of these particles penetrated into cells. - Highlights: • Uncoated magnetite nanoparticle suspension is unusable for intracellular introduction. • Magnetite particles stabilized with citric acid penetrate into cells via endocytosis. • An application of a magnetic field enhances cellular uptake of magnetite particles. • The amount of particles in cell samples can be evaluated with a SQUID-magnetometer.

  16. Synthesis of 2,4-dinitrophenylhydrazine loaded sodium dodecyl sulfate-coated magnetite nanoparticles for adsorption of Hg(II ions from an aqueous solution

    Directory of Open Access Journals (Sweden)

    Soheil Sobhanardakani

    2016-09-01

    Full Text Available Background: The rapid increase in agricultural and industrial development has made heavy metal pollution a serious environmental problem and public health threat; therefore, removal of heavy metals from water is important. The current study prepared DNPH@SDS@Fe3O4 nanoparticles as a novel and effective adsorbent for removal of Hg(II ions from an aqueous solution. Methods: A selective adsorbent for Hg(II was synthesized by coating Fe3O4 nanoparticles with sodium dodecyl sulfate which was further functionalized with 2,4-dinitrophenylhydrazine (2,4-DNPH. The synthesized nanoparticles were characterized by Fourier transform infrared spectroscopy (FTIR, x-ray diffraction (XRD, scanning electron microscopy (SEM and SEM–EDXSt. The effects of pH, dose of adsorbent and shaking time on adsorption capacity were investigated. The kinetics and equilibrium of adsorption of the metal ions were thoroughly studied. Results: SEM showed that the size of the nanoparticles was 20 to 35 nm. The maximum adsorption capacity for Hg(II was 164.0 mg g-1 for an adsorbent dose of 0.04 g at pH 7.0, 25°C and the initial metal concentration was 25 mg L-1,which was greater than for most adsorbents previously examined for Hg(II adsorption. Adsorption experimental data showed good correlation with the pseudo-secondorder model and Langmuir isotherm model. Conclusion: The results indicated that the DNPH@SDS@Fe3O4 nanoparticles are an efficient adsorbent for removal of heavy metal from wastewater.

  17. Gelatine-assisted synthesis of magnetite nanoparticles for magnetic hyperthermia

    Energy Technology Data Exchange (ETDEWEB)

    Alves, André F.; Mendo, Sofia G. [Universidade de Lisboa, Centro de Química e Bioquímica, Faculdade de Ciências (Portugal); Ferreira, Liliana P. [Universidade de Lisboa, Biosystems and Integrative Sciences Institute, Faculdade de Ciências (Portugal); Mendonça, Maria Helena [Universidade de Lisboa, Centro de Química e Bioquímica, Faculdade de Ciências (Portugal); Ferreira, Paula [University of Aveiro, Department of Materials and Ceramic Engineering, CICECO - Aveiro Institute of Materials (Portugal); Godinho, Margarida; Cruz, Maria Margarida [Universidade de Lisboa, Biosystems and Integrative Sciences Institute, Faculdade de Ciências (Portugal); Carvalho, Maria Deus, E-mail: mdcarvalho@ciencias.ulisboa.pt [Universidade de Lisboa, Centro de Química e Bioquímica, Faculdade de Ciências (Portugal)

    2016-01-15

    Magnetite nanoparticles were synthesized by the co-precipitation method exploring the use of gelatine and agar as additives. For comparison, magnetite nanoparticles were also prepared by standard co-precipitation, by co-precipitation with the addition of a surfactant (sodium dodecyl sulphate) and by the thermal decomposition method. The structure and morphology of the synthesized nanoparticles were investigated by powder X-ray diffraction and transmission electron microscopy. Their magnetic properties were studied by SQUID magnetometry and {sup 57}Fe Mössbauer spectroscopy. The nanoparticles potential for applications in magnetic hyperthermia was evaluated through heating efficiency under alternating magnetic field. The results show that all synthesis methods produce Fe{sub 3−x}O{sub 4} nanoparticles with similar sizes. The nanoparticles synthesized in the gelatine medium display the narrowest particle size distribution, the lowest oxidation degree, one of the highest saturation magnetization values and the best hyperthermia efficiency, proving that this gelatine-assisted synthesis is an efficient, environmental friendly, and low-cost method to produce magnetite nanoparticles. Graphical Abstract: A new gelatine-assisted method is an efficient and low-cost way to synthesize magnetite nanoparticles with enhanced magnetic hyperthermia.

  18. Magnetisation of magnetite nanoparticles medium with dipol-dipol interaction

    International Nuclear Information System (INIS)

    Ali-zade, R. A.

    2005-01-01

    Full text: Magnetisation expression for magnetite nanoparticles medium with dipo-dipol interaction has been obtained. We suggested, that energy magnetic dipol-dipol interaction of magnetite nanopaticles is determined by: E d-d = - m 2 /4πμ 0 r 3 (cth x -1/x) 2 where x=mH/kT. This expression has been substituted in statistical sum of magnetite nanoparticles medium. Obtained statistical sum consists the production of two statistical sums. The first statistical sum described non-interacting magnetite nanoparticle medium and from this is obtained Langevan equation. Second statistical sum is: Z 2 -∫exp(Σm 2 /4π 0 r 3 (cth x -1/x) 2 ) dΩ 2 . The second statistical sum has been expanded in Taylor's set and taken into consideration first two terms. Integration has been carried out over all volume. In this case take into account that, number twice interactions of magnetite nanoparticles in unit volume is equal to N(N-1)/2 at N>>1 to N 2 /2. We obtain expressions for magnetisation and initial magnetic susceptibility of interacting magnetite nanoparticles medium take into account that Φ=-kT ln Z, M=-dΦ/dH, χ=dM/dH: M=M Sφm (cth x -1/x)+ 1/3 M S 2 φ m 2 (1μ 0 H) ln(VM S /kT).(cth x -1/x)(-xcsch 2 x+1/x) χ 0 =1/3 (m/kT)+ 1/27 M S 2 φ m 2 (1μ 0 )ln(VM S /kT).(m/kT) 2 . Second term in the magnetisation is sufficient at weak and middle magnetic fields. At large magnetic fields, it leads to zero. The second term of magnetisation has maximum at x=1.566. The values of experimental and calculated magnetic field corresponding to magnetisation maximum for magnetite nanoparticles medium (mean diameter of nanoparticle is 9.4 nm) are 1.19 10 4 A/m and 1.25 10 4 A/m respectively. Magnetic dipol-dipol interaction influence to magnetisation of magnetite nanoparticles. Magnetite nanoparticles lined along external magnetic fields line and formatted chains. Magnetisation of medium occurs by the 'parallel' mechanism method magnetisation of chains

  19. Strong adsorption of chlorotetracycline on magnetite nanoparticles

    International Nuclear Information System (INIS)

    Zhang, Di; Niu, Hongyun; Zhang, Xiaole; Meng, Zhaofu; Cai, Yaqi

    2011-01-01

    Highlights: → Fe 3 O 4 MNPs selectively adsorb CTC through chelation between CTC and Fe atoms. → Fe 3 O 4 MNPs remain high adsorption ability to CTC in environmental water samples. → Fe 3 O 4 MNPs sorbed with CTC are easily collected from water under a magnetic field. → The collected Fe 3 O 4 MNPs are regenerated by treatment with H 2 O 2 or calcination. - Abstract: In this work, environmentally friendly magnetite nanoparticles (Fe 3 O 4 MNPs) were used to adsorb chlorotetracycline (CTC) from aqueous media. Fe 3 O 4 MNPs exhibit ultrahigh adsorption ability to this widely used antibiotic. The adsorption behavior of CTC on Fe 3 O 4 MNPs fitted the pseudo-second-order kinetics model, and the adsorption equilibrium was achieved within 10 h. The maximum Langmuir adsorption capacity of CTC on Fe 3 O 4 (476 mg g -1 ) was obtained at pH 6.5. Thermodynamic parameters calculated from the adsorption data at different temperature showed that the adsorption reaction was endothermic and spontaneous. Low concentration of NaCl and foreign divalent cations hardly affected the adsorption. Negative effect of coexisting humic acid (HA) on CTC adsorption was also observed when the concentration of HA was lower than 20 mg L -1 . But high concentration of HA (>20 mg L -1 ) increased the CTC adsorption on Fe 3 O 4 MNPs. The matrix effect of several environmental water samples on CTC adsorption was not evident. Fe 3 O 4 MNPs were regenerated by treatment with H 2 O 2 or calcination at 400 o C in N 2 atmosphere after separation from water solution by an external magnet. This research provided a high efficient and reusable adsorbent to remove CTC selectively from aqueous media.

  20. Magnetite nanoparticle (NP) uptake by wheat plants and its effect on cadmium and chromium toxicological behavior

    Energy Technology Data Exchange (ETDEWEB)

    López-Luna, J., E-mail: jlol_24@hotmail.com [Instituto de Estudios Ambientales, Universidad de la Sierra Juárez, Ixtlán de Juárez 68725, Oaxaca (Mexico); Silva-Silva, M.J. [Instituto de Estudios Ambientales, Universidad de la Sierra Juárez, Ixtlán de Juárez 68725, Oaxaca (Mexico); Martinez-Vargas, S. [Facultad de Ingeniería, Universidad Autónoma del Carmen, Ciudad del Carmen 24115, Campeche (Mexico); Mijangos-Ricardez, O.F. [Instituto de Estudios Ambientales, Universidad de la Sierra Juárez, Ixtlán de Juárez 68725, Oaxaca (Mexico); González-Chávez, M.C. [Colegio de Postgraduados en Ciencias Agrícolas, Carr. México–Texcoco km 36.5, Montecillo 56230, Estado de México (Mexico); Solís-Domínguez, F.A. [Facultad de Ingeniería, Universidad Autónoma de Baja California, Mexicali 21280, Baja California Norte (Mexico); Cuevas-Díaz, M.C. [Facultad de Ciencias Químicas, Universidad Veracruzana, Coatzacoalcos 96535, Veracruz (Mexico)

    2016-09-15

    The aim of this work was to assess the uptake of citrate-coated magnetite nanoparticles (NPs) by wheat plants and its effect on the bioaccumulation and toxicity of individual and joint Cd{sup 2+} and Cr{sup 6+} levels. Seven-day assays were conducted using quartz sand as the plant growth substrate. The endpoints measured were seed germination, root and shoot lengths, and heavy metal accumulation. Magnetite exhibited very low toxicity, regardless of the wheat seedling NP uptake and distribution into roots and shoots. The seed germination and shoot length were not sensitive enough, while the root length was a more sensitive toxicity endpoint. The root length of wheat seedlings exposed to individual metals decreased by 50% at 2.67 mg Cd{sup 2+} kg{sup −1} and 5.53 mg Cr{sup 6+} kg{sup −1}. However, when magnetite NPs (1000 mg kg{sup −1}) were added, the root length of the plants increased by 25 and 50%. Cd{sup 2+} and Cr{sup 6+} showed similar and noninteractive joint action, but strongly impaired the wheat seedlings. In contrast, an interactive infra-additive or antagonistic effect was observed upon adding magnetite NPs. Thus, cadmium and chromium accumulation in vegetable tissues was considerately diminished and the toxicity alleviated. - Highlights: • We assessed the effect of nanomagnetite on heavy metal toxicity in wheat plants. • Citrate-coated magnetite nanoparticles (NPs) exerted very low toxicity to plants. • Cadmium was more toxic than chromium and toxicity was mitigated by magnetite NPs. • Cadmium and chromium had a similar and noninteractive joint action on plants. • Metals showed an interactive infra-additive joint effect by adding magnetite NPs.

  1. Critical Parametric Study on Final Size of Magnetite Nanoparticles

    Science.gov (United States)

    Yusoff, A. H. M.; Salimi, M. N.; Jamlos, M. F.

    2018-03-01

    The great performance of magnetite nanoparticle in varsity field are mainly depended on their size since size determine the saturation magnetisation and also the phase purity. Magnetite nanoparticles were prepared using a simple co-precipitation method in order to study the influence of synthesis condition on the final size. Variable parameters include stirring rate, reaction temperature and pH of the solution can finely tuned the size of the resulting nanoparticles. Generally, any increase in these parameters had a gently reduction on particle size. But, the size was promoted to increase back at certain point due to the specific reason. Nucleation and growth processes are involved to clarify the impact of synthesis condition on the particle sizes. The result obtained give the correct conditions for pure magnetite synthesis at nanoscale size of dimensions less than 100 nm.

  2. Synthesis of magnetite nanoparticles by microwave irradiation and characterization

    International Nuclear Information System (INIS)

    Holland, Helber; Yamaura, Mitiko

    2009-01-01

    Nanometer-scale magnetic particles have been research target because of their peculiar magnetic properties as observed in magnetite nanoparticles. These nanoparticles exhibit superparamagnetic characteristics with potential applications in biomedical, environmental, and engineering fields. In this work, magnetite nanoparticles from Fe 2+ ions were obtained from two different processes, by precipitation and heating in a boiling water bath and by precipitation and heating in a domestic microwave oven. Influence of heating time of both systems for obtaining of magnetite particles was investigated. The characterization of the products was done by Scanning Electron Microscopy to determine the morphology, X-ray Diffractometry to estimate the crystal structure and the size of crystallite and Fourier Transform Infrared Spectroscopy to show the principal bands of absorption. (author)

  3. Magnetite nanoparticles as reporters for microcarrier processing in cytoplasm

    Energy Technology Data Exchange (ETDEWEB)

    Reibetanz, Uta, E-mail: uta.reibetanz@medizin.uni-leipzig.de [Translational Centre for Regenerative Medicine (TRM) Leipzig, Universitaet Leipzig, Philipp-Rosenthal-Strasse 55, 04103 Leipzig (Germany); Institute for Medical Physics and Biophysics, Medical Faculty, Universitaet Leipzig, Haertelstrasse 16-18, 04107 Leipzig (Germany); Jankuhn, Steffen, E-mail: jankuhn@uni-leipzig.de [Division of Nuclear Solid State Physics, Faculty of Physics and Geosciences, Universitaet Leipzig, Linnestrasse 5, 04103 Leipzig (Germany); Office for Environmental Protection and Occupational Safety, Universitaet Leipzig, Ritterstrasse 24, 04109 Leipzig (Germany)

    2011-10-15

    The development and therapeutic application of drug delivery systems based on colloidal microcarriers layer-by-layer coated with biopolyelectrolytes requires the investigation of their processing inside the cell for the successful and efficient transport and release of the active agents. The present study is focused on the time-dependent multilayer decomposition and the subsequent release of active agents to the cytoplasm. Magnetite nanoparticles (MNP) were used as reporter agents integrated into the protamine sulfate/dextran sulfate basis multilayer on colloidal SiO{sub 2} cores. This functionalization allows the monitoring of the multilayer decomposition due to the detection of the MNP release, visualized by means of proton-induced X-ray emission (PIXE) by elemental distribution of Si and Fe. The direct correlation between the microcarrier localization in endolysosomes and cytoplasm of HEK293T/17 cells via confocal laser scanning microscopy (CLSM) and the elemental distribution (PIXE) allows tracing the fate of the MNP-coated microcarriers in cytoplasm, and thus the processing of the multilayer. Microcarrier/cell co-incubation experiments of 6 h, 24 h, 48 h, and 72 h show that a MNP release and a slight expansion into the cytoplasm occurs after a longer co-incubation of 72 h.

  4. Starch-modified magnetite nanoparticles for impregnation into cartilage

    Energy Technology Data Exchange (ETDEWEB)

    Soshnikova, Yulia M., E-mail: yuliasoshnikova@gmail.com [Russian Academy of Sciences, Institute on Laser and Information Technologies (Russian Federation); Roman, Svetlana G.; Chebotareva, Natalia A. [A.N. Bach Institute of Biochemistry (Russian Federation); Baum, Olga I. [Russian Academy of Sciences, Institute on Laser and Information Technologies (Russian Federation); Obrezkova, Mariya V. [Lomonosov Moscow State University, Department of Chemistry (Russian Federation); Gillis, Richard B.; Harding, Stephen E. [University of Nottingham, National Centre for Macromolecular Hydrodynamics (United Kingdom); Sobol, Emil N. [Russian Academy of Sciences, Institute on Laser and Information Technologies (Russian Federation); Lunin, Valeriy V. [Lomonosov Moscow State University, Department of Chemistry (Russian Federation)

    2013-11-15

    The paper presents preparation and characterization of starch-modified Fe{sub 3}O{sub 4} nanoparticles (NPs) in aqueous dispersion after impregnation into healthy and damaged types of cartilage. We show that starch-modified dispersion has a narrower size distribution than a non‐stabilized one. The average hydrodynamic radius of magnetite NPs in a dispersion used for impregnation into cartilage is (48 ± 1) nm with the width of the distribution from 5 to 200 nm. We investigate stability of aqueous magnetite NPs dispersions during storage and with increase in temperature (up to 70 °C). We find that polydisperse magnetite NPs can penetrate into cartilage and the size and concentration of impregnated particles depend on the organization of the tissue structure. The results confirm the possibility of application of magnetite NPs in diagnostics and laser treatment of degenerative cartilage deceases.

  5. Carboxylic acid effects on the size and catalytic activity of magnetite nanoparticles.

    Science.gov (United States)

    Hosseini-Monfared, Hassan; Parchegani, Fatemeh; Alavi, Sohaila

    2015-01-01

    Magnetite nanoparticles (Fe3O4-NPs) were successfully synthesized in diethylene glycol in the presence of carboxylic acids. They were characterized using XRD, SEM and FTIR. Carboxylic acid plays a critical role in determining the morphology, particle size and size distribution of the resulting particles. The results show that as-prepared magnetite nanoparticles are monodisperse and highly crystalline. The nanoparticles can be easily dispersed in aqueous media and other polar solvents due to coated by a layer of hydrophilic polyol and carboxylic acid ligands in situ. Easily prepared Fe3O4-NPs have been shown to be an active, recyclable, and highly selective catalyst for the epoxidation of cyclic olefins with aqueous 30% H2O2. Copyright © 2014 Elsevier Inc. All rights reserved.

  6. Preparation of biodegradable magnetic microspheres with poly(lactic acid)-coated magnetite

    Energy Technology Data Exchange (ETDEWEB)

    Zhao Hong; Saatchi, Katayoun [Faculty of Pharmaceutical Sciences, University of British Columbia, 2146 East Mall, Vancouver, BC, 6T 1Z3 (Canada); Haefeli, Urs O. [Faculty of Pharmaceutical Sciences, University of British Columbia, 2146 East Mall, Vancouver, BC, V6T 1Z3 (Canada)], E-mail: uhafeli@interchange.ubc.ca

    2009-05-15

    Poly(lactic acid) (PLA)-coated magnetic nanoparticles were made using uncapped PLA with free carboxylate groups. The physical properties of these particles were compared to those of oleate-coated or oleate/sulphonate bilayer (W40) coated magnetic particles. Magnetic microspheres (MMS) with the matrix material poly(lactide-co-glycolide) (PLGA) or PLA were then formed by the emulsion solvent extraction method with encapsulation efficiencies of 40%, 83% and 96% for oleate, PLA and oleate/sulfonate-coated magnetic particles, respectively. MMS made from PLA-coated magnetite were hemocompatible and produced no hemolysis, whereas the other MMS were hemolytic above 0.3 mg/mL of blood.

  7. Preparation of biodegradable magnetic microspheres with poly(lactic acid)-coated magnetite

    International Nuclear Information System (INIS)

    Zhao Hong; Saatchi, Katayoun; Haefeli, Urs O.

    2009-01-01

    Poly(lactic acid) (PLA)-coated magnetic nanoparticles were made using uncapped PLA with free carboxylate groups. The physical properties of these particles were compared to those of oleate-coated or oleate/sulphonate bilayer (W40) coated magnetic particles. Magnetic microspheres (MMS) with the matrix material poly(lactide-co-glycolide) (PLGA) or PLA were then formed by the emulsion solvent extraction method with encapsulation efficiencies of 40%, 83% and 96% for oleate, PLA and oleate/sulfonate-coated magnetic particles, respectively. MMS made from PLA-coated magnetite were hemocompatible and produced no hemolysis, whereas the other MMS were hemolytic above 0.3 mg/mL of blood.

  8. Evaluation of magnetite nanoparticles as molybdenum ions adsorbent

    International Nuclear Information System (INIS)

    Holland, Helber; Yamaura, Mitiko; Sousa, Jose Silva; Freitas, Antonio Alves

    2011-01-01

    Molybdenum-99 is the generator radionuclide of the most used radioisotope for preparation of radiopharmaceuticals with diagnostic purposes in nuclear medicine, technetium-99m (Tc-99m). One way of Mo-99 obtaining is as fission product of irradiated uranium targets in reactor. In this work, the potential application of magnetite particles in the separation of Mo-99 from a dissolution solution of U targets was evaluated. Synthetic magnetite nanoparticles were prepared by alkaline precipitation method from Fe 2+ ions and heat-treated via microwave irradiation in a conventional household oven. Adsorption kinetics was studied. It was observed that the adsorption of Mo by magnetite nanoparticles is fast and followed the model of pseudo-second order. (author)

  9. Novel humic acid-bonded magnetite nanoparticles for protein immobilization

    Energy Technology Data Exchange (ETDEWEB)

    Bayrakci, Mevlut, E-mail: mevlutbayrakci@gmail.com [Ulukisla Vocational School, Nigde University, 51100 Ulukisla, Nigde (Turkey); Gezici, Orhan [Department of Chemistry, Nigde University, 51100 Nigde (Turkey); Bas, Salih Zeki; Ozmen, Mustafa; Maltas, Esra [Department of Chemistry, Selcuk University, 42031 Konya (Turkey)

    2014-09-01

    The present paper is the first report that introduces (i) a useful methodology for chemical immobilization of humic acid (HA) to aminopropyltriethoxysilane-functionalized magnetite iron oxide nanoparticles (APS-MNPs) and (ii) human serum albumin (HSA) binding to the obtained material (HA-APS-MNPs). The newly prepared magnetite nanoparticle was characterized by using Fourier transform infrared spectroscopy (FTIR), transmission electron microscopy (TEM), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), and elemental analysis. Results indicated that surface modification of the bare magnetite nanoparticles (MNPs) with aminopropyltriethoxysilane (APS) and HA was successfully performed. The protein binding studies that were evaluated in batch mode exhibited that HA-APS-MNPs could be efficiently used as a substrate for the binding of HSA from aqueous solutions. Usually, recovery values higher than 90% were found to be feasible by HA-APS-MNPs, while that value was around 2% and 70% in the cases of MNPs and APS-MNPs, respectively. Hence, the capacity of MNPs was found to be significantly improved by immobilization of HA. Furthermore, thermal degradation of HA-APS-MNPs and HSA bonded HA-APS-MNPs was evaluated in terms of the Horowitz–Metzger equation in order to determine kinetic parameters for thermal decomposition. Activation energies calculated for HA-APS-MNPs (20.74 kJ mol{sup −1}) and HSA bonded HA-APS-MNPs (33.42 kJ mol{sup −1}) implied chemical immobilization of HA to APS-MNPs, and tight interactions between HA and HA-APS-MNPs. - Highlights: • A new magnetite nanoparticle based humic acid was prepared for the first time. • Protein binding studies of magnetite nanoparticle based humic acid were performed. • Kinetic parameters of protein and/or humic acid bonded nanoparticles were evaluated.

  10. Release Behavior and Toxicity Profiles towards Leukemia (WEHI-3B Cell Lines of 6-Mercaptopurine-PEG-Coated Magnetite Nanoparticles Delivery System

    Directory of Open Access Journals (Sweden)

    Dena Dorniani

    2014-01-01

    Full Text Available The coating of an active drug, 6-mercaptopurine, into the iron oxide nanoparticles-polyethylene glycol (FNPs-PEG in order to form a new nanocomposite, FPEGMP-2, was accomplished using coprecipitation technique. The resulting nanosized with a narrow size distribution magnetic polymeric particles show the superparamagnetic properties with 38.6 emu/g saturation magnetization at room temperature. Fourier transform infrared spectroscopy and the thermal analysis study supported the formation of the nanocomposite and the enhancement of thermal stability in the resulting nanocomposite comparing with its counterpart in free state. The loading of 6-mercaptopurine (MP in the FPEGMP-2 nanocomposite was estimated to be about 5.6% and the kinetic experimental data properly correlated with the pseudo-second order model. Also, the release of MP from the FPEGMP-2 nanocomposite shows the sustained release manner which is remarkably lower in phosphate buffered solution at pH 7.4 than pH 4.8, due to different release mechanism. The maximum percentage release of MP from the nanocomposite reached about 60% and 97% within about 92 and 74 hours when exposed to pH 7.4 and 4.8, respectively.

  11. Release behavior and toxicity profiles towards leukemia (WEHI-3B) cell lines of 6-mercaptopurine-PEG-coated magnetite nanoparticles delivery system.

    Science.gov (United States)

    Dorniani, Dena; Kura, Aminu Umar; Hussein-Al-Ali, Samer Hasan; bin Hussein, Mohd Zobir; Fakurazi, Sharida; Shaari, Abdul Halim; Ahmad, Zalinah

    2014-01-01

    The coating of an active drug, 6-mercaptopurine, into the iron oxide nanoparticles-polyethylene glycol (FNPs-PEG) in order to form a new nanocomposite, FPEGMP-2, was accomplished using coprecipitation technique. The resulting nanosized with a narrow size distribution magnetic polymeric particles show the superparamagnetic properties with 38.6 emu/g saturation magnetization at room temperature. Fourier transform infrared spectroscopy and the thermal analysis study supported the formation of the nanocomposite and the enhancement of thermal stability in the resulting nanocomposite comparing with its counterpart in free state. The loading of 6-mercaptopurine (MP) in the FPEGMP-2 nanocomposite was estimated to be about 5.6% and the kinetic experimental data properly correlated with the pseudo-second order model. Also, the release of MP from the FPEGMP-2 nanocomposite shows the sustained release manner which is remarkably lower in phosphate buffered solution at pH 7.4 than pH 4.8, due to different release mechanism. The maximum percentage release of MP from the nanocomposite reached about 60% and 97% within about 92 and 74 hours when exposed to pH 7.4 and 4.8, respectively.

  12. Effect of magnetite nanoparticles on dye absorption properties of ...

    Indian Academy of Sciences (India)

    Magnetite@carbon (Fe 3 O 4 @C) composites were prepared using three kinds of Fe 3 O 4 nanoparticles (NPs). All the Fe 3 O 4 @C composites could be easily separated from water by an external magnet. The Fe 3 O 4 NPs synthesized by a microreactor system have the smallest size and narrowest size distribution among ...

  13. The molecular mass of dextran used to modify magnetite nanoparticles affects insulin amyloid aggregation

    Energy Technology Data Exchange (ETDEWEB)

    Siposova, Katarina [Department of Biophysics, Institute of Experimental Physics, Slovak Academy of Sciences, Kosice (Slovakia); Pospiskova, Kristyna [Regional Centre of Advanced Technologies and Materials, Palacky University, Olomouc (Czech Republic); Bednarikova, Zuzana [Department of Biophysics, Institute of Experimental Physics, Slovak Academy of Sciences, Kosice (Slovakia); Department of Biochemistry, Faculty of Science, Safarik University, Kosice (Slovakia); Safarik, Ivo [Regional Centre of Advanced Technologies and Materials, Palacky University, Olomouc (Czech Republic); Department of Nanobiotechnology, Biology Centre, ISB, CAS, Ceske Budejovice (Czech Republic); Safarikova, Mirka [Department of Nanobiotechnology, Biology Centre, ISB, CAS, Ceske Budejovice (Czech Republic); Kubovcikova, Martina; Kopcansky, Peter [Department of Magnetism, Institute of Experimental Physics, Slovak Academy of Sciences, Kosice (Slovakia); Gazova, Zuzana, E-mail: gazova@saske.sk [Department of Biophysics, Institute of Experimental Physics, Slovak Academy of Sciences, Kosice (Slovakia)

    2017-04-01

    Protein transformation from its soluble state into amyloid aggregates is associated with amyloid-related diseases. Amyloid deposits of insulin fibrils have been found in the sites of subcutaneous insulin application in patients with prolonged diabetes. Using atomic force microscopy and ThT fluorescence assay we have investigated the interference of insulin amyloid aggregation with superparamagnetic Fe{sub 3}O{sub 4}-based nanoparticles (SPIONs) coated with dextran (DEX); molecular mass of dextran was equal to 15–20, 40 or 70 kDa. The obtained data indicate that all three types of dextran coated nanoparticles (NP-FeDEXs) are able to inhibit insulin fibrillization and to destroy amyloid fibrils. The extent of anti-amyloid activities depends on the properties of NP-FeDEXs, mainly on the size of nanoparticles which is determined by molecular mass of dextran molecules. The most effective inhibiting activity was observed for the smallest nanoparticles coated with 15–20 kDa dextran. Contrary, the highest destroying activity was observed for the largest NP-FeDEX (70 kDa dextran). - Highlights: • Interference of dextran- magnetite nanoparticles with insulin amyloid aggregation. • Nanoparticles inhibited insulin fibrillization and depolymerized insulin amyloid fibrils. • Size of nanoparticles significantly influences their anti-amyloid activities. • The most effective inhibition of insulin amyloid fibrillization was detected for the smallest nanoparticles. • Contrary, DC{sub 50} values decreased with increasing size of nanoparticles.

  14. The molecular mass of dextran used to modify magnetite nanoparticles affects insulin amyloid aggregation

    International Nuclear Information System (INIS)

    Siposova, Katarina; Pospiskova, Kristyna; Bednarikova, Zuzana; Safarik, Ivo; Safarikova, Mirka; Kubovcikova, Martina; Kopcansky, Peter; Gazova, Zuzana

    2017-01-01

    Protein transformation from its soluble state into amyloid aggregates is associated with amyloid-related diseases. Amyloid deposits of insulin fibrils have been found in the sites of subcutaneous insulin application in patients with prolonged diabetes. Using atomic force microscopy and ThT fluorescence assay we have investigated the interference of insulin amyloid aggregation with superparamagnetic Fe 3 O 4 -based nanoparticles (SPIONs) coated with dextran (DEX); molecular mass of dextran was equal to 15–20, 40 or 70 kDa. The obtained data indicate that all three types of dextran coated nanoparticles (NP-FeDEXs) are able to inhibit insulin fibrillization and to destroy amyloid fibrils. The extent of anti-amyloid activities depends on the properties of NP-FeDEXs, mainly on the size of nanoparticles which is determined by molecular mass of dextran molecules. The most effective inhibiting activity was observed for the smallest nanoparticles coated with 15–20 kDa dextran. Contrary, the highest destroying activity was observed for the largest NP-FeDEX (70 kDa dextran). - Highlights: • Interference of dextran- magnetite nanoparticles with insulin amyloid aggregation. • Nanoparticles inhibited insulin fibrillization and depolymerized insulin amyloid fibrils. • Size of nanoparticles significantly influences their anti-amyloid activities. • The most effective inhibition of insulin amyloid fibrillization was detected for the smallest nanoparticles. • Contrary, DC 50 values decreased with increasing size of nanoparticles.

  15. The use of magnetite nanoparticles for implant-assisted magnetic drug targeting in thrombolytic therapy.

    Science.gov (United States)

    Kempe, Maria; Kempe, Henrik; Snowball, Ian; Wallén, Rita; Arza, Carlos Rodriguez; Götberg, Matthias; Olsson, Tommy

    2010-12-01

    Implant-assisted targeting of magnetic particles under the influence of an external magnetic field has previously been verified through mathematical modeling, in vitro studies, and in vivo studies on rat carotid arteries as a feasible method for localized drug delivery. The present study focuses on the development of nanoparticles for the treatment of in-stent thrombosis. Magnetic nanoparticles in the size-range 10-30 nm were synthesized in a one-pot procedure by precipitation of ferrous hydroxide followed by oxidation to magnetite. The nanoparticles were silanized with tetraethyl orthosilicate in the presence of triethylene glycol and/or polyethylene glycol. The surface coated magnetite nanoparticles were activated with either N-hydroxysulfosuccinimide or tresyl chloride for covalent immobilization of tissue plasminogen activator (tPA). Hysteresis loops showed saturation magnetizations of 55.8, 44.1, and 43.0 emu/g for the naked nanoparticles, the surface coated nanoparticles, and the tPA-nanoparticle conjugates, respectively. The hemolytic activity of the nanoparticles in blood was negligible. An initial in vivo biocompatibility test in pig, carried out by intravascular injection of the nanoparticles in a stented brachial artery, showed no short-term adverse effects. In vitro evaluation in a flow-through model proved that the nanoparticles were captured efficiently to the surface of a ferromagnetic coiled wire at the fluid velocities typical for human arteries. A preliminary test of the tPA-nanoparticle conjugates in a pig model suggested that the conjugates may be used for treatment of in-stent thrombosis in coronary arteries. Copyright © 2010 Elsevier Ltd. All rights reserved.

  16. Relaxometry imaging of superparamagnetic magnetite nanoparticles at ambient conditions

    Science.gov (United States)

    Finkler, Amit; Schmid-Lorch, Dominik; Häberle, Thomas; Reinhard, Friedemann; Zappe, Andrea; Slota, Michael; Bogani, Lapo; Wrachtrup, Jörg

    We present a novel technique to image superparamagnetic iron oxide nanoparticles via their fluctuating magnetic fields. The detection is based on the nitrogen-vacancy (NV) color center in diamond, which allows optically detected magnetic resonance (ODMR) measurements on its electron spin structure. In combination with an atomic-force-microscope, this atomic-sized color center maps ambient magnetic fields in a wide frequency range from DC up to several GHz, while retaining a high spatial resolution in the sub-nanometer range. We demonstrate imaging of single 10 nm sized magnetite nanoparticles using this spin noise detection technique. By fitting simulations (Ornstein-Uhlenbeck process) to the data, we are able to infer additional information on such a particle and its dynamics, like the attempt frequency and the anisotropy constant. This is of high interest to the proposed application of magnetite nanoparticles as an alternative MRI contrast agent or to the field of particle-aided tumor hyperthermia.

  17. "Clickable", trifunctional magnetite nanoparticles and their chemoselective biofunctionalization.

    Science.gov (United States)

    Das, Manasmita; Bandyopadhyay, Debarati; Mishra, Debasish; Datir, Satyajit; Dhak, Prasanta; Jain, Sanyog; Maiti, Tapas Kumar; Basak, Amit; Pramanik, Panchanan

    2011-06-15

    A multifunctional iron oxide based nanoformulation for combined cancer-targeted therapy and multimodal imaging has been meticulously designed and synthesized using a chemoselective ligation approach. Novel superparamagnetic magnetite nanoparticles simultaneously functionalized with amine, carboxyl, and azide groups were fabricated through a sequence of stoichiometrically controllable partial succinylation and Cu (II) catalyzed diazo transfer on the reactive amine termini of 2-aminoethylphosphonate grafted magnetite nanoparticles (MNPs). Functional moieties associated with MNP surface were chemoselectively conjugated with rhodamine B isothiocyanate (RITC), propargyl folate (FA), and paclitaxel (PTX) via tandem nucleophic addition of amine to isothithiocyanates, Cu (I) catalyzed azide--alkyne click chemistry and carbodiimide-promoted esterification. An extensive in vitro study established that the bioactives chemoselectively appended to the magnetite core bequeathed multifunctionality to the nanoparticles without any loss of activity of the functional molecules. Multifunctional nanoparticles, developed in the course of the study, could selectively target and induce apoptosis to folate-receptor (FR) overexpressing cancer cells with enhanced efficacy as compared to the free drug. In addition, the dual optical and magnetic properties of the synthesized nanoparticles aided in the real-time tracking of their intracellular pathways also as apoptotic events through dual fluorescence and MR-based imaging.

  18. Synthesis of magnetite nanoparticles-β-cyclodextrin complex

    International Nuclear Information System (INIS)

    Cobos Cruz, L.A.; Martinez Perez, C.A.; Monreal Romero, H.A.; Garcia Casillas, P.E.

    2008-01-01

    In this work, the synthesis and characterization of a magnetite (M) and β-cyclodextrin (CD) complex is presented. The chemical bonding between the magnetite and CD was studied as evidence of host-guest interaction; therefore the CD works like a reactor with the magnetite inside of it, as consequence the growth of the particle is restricted by the electrostatic interaction of M-CD complex. The particle size of the magnetite-cyclodextrin complex (M-CD) decreased 79.1% with 0.5% of CD. The average particle size of the M-CD complex was 10 nm. The saturation magnetization (σ s ) and intrinsic coercivity (H c ) increased 10% and 20%, respectively. In order to understand how the the CD affects the results obtained, the second derivate of remission function was obtained from the ultraviolet-visible spectra (UV-vis). Fourier transform infrared spectroscopy (FTIR) was used to elucidate the interaction between the magnetite and CD. The thermal analysis was measured by thermogravimetric and differential thermal analysis (TGA-DTA). The magnetic properties, intrinsic coercivity (H c ) and the saturation magnetization were determined by vibrating sample magnetometry (VSM); the size and shape of nanoparticles were determined by scanning electron microscopy (SEM). The identification of phases was made by X-ray diffraction

  19. Synthesis and Characterization of Novel Magnetite Nanoparticle Block Copolymer Complexes

    OpenAIRE

    Zhang, Qian

    2007-01-01

    Superparamagnetic Magnetite (Fe3O4) nanoparticles were synthesized and complexed with carboxylate-functionalized block copolymers, and aqueous dispersions of the complexes were investigated as functions of their chemical and morphological structures. The block copolymer dispersants possessed either poly(ethylene oxide), poly(ethylene oxide-co-propylene oxide), or poly(ethylene oxide-b-propylene oxide) outer blocks, and all contained a polyurethane center block with pendant carboxylate functi...

  20. The effect of polycarboxylate shell of magnetite nanoparticles on protein corona formation in blood plasma

    Energy Technology Data Exchange (ETDEWEB)

    Szekeres, Márta, E-mail: szekeres@chem.u-szeged.hu [Department of Physical Chemistry and Materials Sciences, University of Szeged, Hungary, 1 Aradi vt, 6720 Szeged (Hungary); Tóth, Ildikó Y. [Department of Physical Chemistry and Materials Sciences, University of Szeged, Hungary, 1 Aradi vt, 6720 Szeged (Hungary); Turcu, R. [National Institute R& D for Isotopic and Molecular Technology, Cluj-Napoca 400293 (Romania); Tombácz, Etelka [Department of Physical Chemistry and Materials Sciences, University of Szeged, Hungary, 1 Aradi vt, 6720 Szeged (Hungary)

    2017-04-01

    The development of protein corona around nanoparticles upon administration to the human body is responsible in a large part for their biodistribution, cell-internalization and toxicity or biocompatibility. We studied the influence of the chemical composition of polyelectrolyte shells (citric acid (CA) and poly(acrylic-co-maleic acid) (PAM)) of core-shell magnetite nanoparticles (MNPs) on the evolution of protein corona in human plasma (HP). The aggregation state and zeta potential of the particles were measured in the range of HP concentration between 1 and 80 (v/v)% 3 min and 20 h after dispersing the particles in HP diluted with Tris buffered saline. Naked MNPs aggregated in HP solution, but the carboxylated MNPs became stabilized colloidally at higher plasma concentrations. Significant differences were observed at low plasma concentration. CA@MNPs aggregated instantly while the hydrodynamic diameter of PAM@MNP increased only slightly at 1–3 v/v % HP concentrations. The observed differences in protein corona formation can be explained by the differences in the steric effects of the polycarboxylate shells. It is interesting that relatively small but systematic changes in zeta potential alter the aggregation state significantly. - Highlights: • Human plasma protein corona cannot stabilize naked and citrate-coated magnetite nanoparticles. • Polycarboxylic acid (PAM) coated MNPs are well stabilized with HP protein corona. • Stability pattern of naked, CA and PAM-coated MNPs is not predicted by zeta potential.

  1. Surface functionalization of magnetite nanoparticle: A new approach using condensation of alkoxysilanes

    Science.gov (United States)

    Rodriguez, A. F. R.; Costa, T. P.; Bini, R. A.; Faria, F. S. E. D. V.; Azevedo, R. B.; Jafelicci, M.; Coaquira, J. A. H.; Martínez, M. A. R.; Mantilla, J. C.; Marques, R. F. C.; Morais, P. C.

    2017-09-01

    In this study we report on successful production of two samples (BR15 and BR16) comprising magnetite (Fe3O4) nanoparticles ( 10 nm) surface-functionalized via hydrolysis and condensation of alkoxysilane agents, namely 3-aminopropyl-trimethoxisilane (APTS) and N-propyl-trimethoxisilane (NPTS). The as-produced samples were characterized using transmission electron microscopy (TEM), x-ray diffraction (XRD), magnetization measurements (5 K and 300 K hysteresis cycles and zero field-cooled/field-cooled measurements), and Mössbauer spectroscopy (77 and 297 K). The Mössbauer data supported the model picture of a core-shell magnetite-based system. This material system shows shell properties influenced by the surface-coating design, either APTS-coated (BR15) or APTS+NPTS-coated (sample BR16). Analyses of the Mössbauer spectra indicates that the APTS-coated sample presents Fe(III)-rich core and Fe(II)-rich shell with strong hyperfine field; whereas, the APTS+NPTS-coated sample leads to a mixture of two main nanostructures, one essentially surface-terminated with APTS whereas the other surface-terminated with NPTS, both presenting weak hyperfine fields compared with the single surface-coated sample. Magnetization measurements support the core-shell picture built from the analyses of the Mössbauer data. Our findings emphasize the capability of the Mössbauer spectroscopy in assessing subtle differences in surface-functionalized iron-based core-shell nanostructures.

  2. Surface modification of magnetite nanoparticles for biomedical applications

    International Nuclear Information System (INIS)

    Barrera, Carola; Herrera, Adriana; Zayas, Yashira; Rinaldi, Carlos

    2009-01-01

    The preparation of magnetite nanoparticles with narrow size distributions using poly(ethylene glycol) (PEG-COOH) or carboxymethyl dextran (CMDx) chains covalently attached to the particle surface using carbodiimide chemistry is described. Particles were synthesized by thermal decomposition and modified with 3-aminopropyl trimethoxysilane (APS) to render particles with reactive amine groups (-NH 2 ) on their surface. Amines were then reacted with carboxyl groups in PEG-COOH or CMDx using carbodiimide chemistry in water. The size and stability of the functionalized magnetic nanoparticles was studied as a function of pH and ionic strength using dynamic light scattering and zeta potential measurements.

  3. Efficient synthesis of superparamagnetic magnetite nanoparticles under air for biomedical applications

    Energy Technology Data Exchange (ETDEWEB)

    Saxena, Namita, E-mail: saxenanamita@yahoo.com [School of Nano Sciences, Central University of Gujarat, Gandhinagar 382030 (India); Singh, Man, E-mail: mansingh50@hotmail.com [School of Chemical Sciences, Central University of Gujarat, Gandhinagar 382030 (India)

    2017-05-01

    The facile co-precipitation process of synthesising Superparamagnetic Iron Oxide Nanoparticles (SPIONs) especially magnetite was investigated and simplified, to develop a reproducible and scaled up synthesis process under air, for producing particles with enhanced percentage of magnetite, thus eliminating the crucial and complicated need of using the inert atmosphere. Presence of magnetite was confirmed by XRD, TEM, and Raman spectroscopy. Efficiency of synthesising magnetite was increased up to approx. ∼58 wt%, under air with no other phases but maghemite present. Alkali concentration was optimised, and particles with better magnetisation values were synthesised. The approximate weight percentage of magnetite was calculated using the simple and rapid XRD peak deconvolution method. Higher pH values from 13 to14 were investigated in the study while alkali concentration was varied from 0.5 to 4 M. 1Molar NaOH with a final pH of 13.4 was found to be optimum. Well crystallised particles with approx. 6–12 nm size, narrow size distribution and cubo-spheroidal shape were synthesised. Particles were Superparamagnetic with high values of saturation magnetisation of up to 68 emu/g and negligible values of remanence and coercivity. A reaction yield of up to 62% was obtained. Hydrophilic coated particles were produced in a single, one step facile process for biomedical applications, using optimised parameters of pH and alkali concentration obtained in the study. Single domain particles with good magnetisation formed stable aqueous dispersions. FTIR, UV-Visible and DLS were used to confirm the coating and dispersion stabilities of the particles. These particles have the requisite properties required for application in different biomedical fields.

  4. Nanocomposite Membrane via Magnetite Nanoparticle Assembly

    KAUST Repository

    Xie, Yihui

    2012-07-01

    Membrane technology is one of the most promising technologies for addressing the global water crisis as well as in many other applications. One of the drawbacks of current ultra- and nanofiltration membranes is the relatively broad pore size distribution. Block copolymer membranes with ultrahigh permeability and very regular pore sizes have been recently demonstrated with pores being formed by the supramolecular assembly of core/shell micelles. Our study aimed at developing an innovative and economically efficient alternative method to fabricate isoporous membrane by self-assembly of magnetic nanoparticle with a polystyrene shell, mimicking the behavior of block copolymer micelle. Fe3O4 nanoparticles of ~13 nm diameter were prepared by co-precipitation as cores. The initiator for ATRP was covalently bonded onto the surface of magnetic nanoparticles with two strategies. Then the surface initiated ATRP of styrene was carried out to functionalize nanoparticles with polystyrene through a “grafting from” method. Finally, the nanocomposite membrane was cast from 50 wt % Fe3O4@PS brush polymer solution in DMF via non solvent phase inversion. Microscopies reveal an asymmetric membrane with a dense thin layer on top of a porous sponge-like layer. This novel class of asymmetric membrane, based on the pure assembly of functionalized nanoparticles was prepared for the first time. The nanoparticles are well distributed however with no preferential order yet in the as-cast film.I would like to thank my committee chair and advisor, Prof. Suzana Nunes, and other committee members, Prof. Klaus-Viktor Peinemann and Prof. Gary Amy, for their guidance and support throughout the course of this research. My appreciation also goes to my colleagues in our group for useful discussions and suggestions. I also want to extend my gratitude to the staff from the KAUST Core Lab for Advanced Nanofabrication, Imaging and Characterization, especially Dr. Ali Reza Behzad, Dr. Rachid Sougrat, and

  5. Remote enzyme activation using gold coated magnetite as antennae for radio frequency fields

    Science.gov (United States)

    Collins, Christian B.; Ackerson, Christopher J.

    2018-02-01

    The emerging field of remote enzyme activation, or the ability to remotely turn thermophilic increase enzyme activity, could be a valuable tool for understanding cellular processes. Through exploitation of the temperature dependence of enzymatic processes and high thermal stability of thermophilic enzymes these experiments utilize nanoparticles as `antennae' that convert radiofrequency (RF) radiation into local heat, increasing activity of the enzymes without increasing the temperature of the surrounding bulk solution. To investigate this possible tool, thermolysin, a metalloprotease was covalently conjugated to 4nm gold coated magnetite particles via peptide bond formation with the protecting ligand shell. RF stimulated protease activity at 17.76 MHz in a solenoid shaped antenna, utilizing both electric and magnetic field interactions was investigated. On average 40 percent higher protease activity was observed in the radio frequency fields then when bulk heating the sample to the same temperature. This is attributed to electrophoretic motion of the nanoparticle enzyme conjugates and local regions of heat generated by the relaxation of the magnetite cores with the oscillating field. Radio frequency local heating of nanoparticles conjugated to enzymes as demonstrated could be useful in the activation of specific enzymes in complex cellular environments.

  6. Magnetite nanoparticles coated with covalently immobilized ionic liquids as a sorbent for extraction of non-steroidal anti-inflammatory drugs from biological fluids

    International Nuclear Information System (INIS)

    Amiri, Maryam; Yadollah, Yamini; Safari, Meysam; Asiabi, Hamid

    2016-01-01

    Magnetic core-shell nanoparticles (mag-NPs) of type SiO_2-Fe_3O_4 were covalently modified with the ionic liquid dimethyl octadecyl[3-(trimethoxysilyl propyl)]ammonium chloride. The NPs were characterized via FTIR and scanning electron microscopy and evaluated with respect to the extraction of the nonsteroidal anti-inflammatory drugs (NSAIDs) tolmetin, indometacin and naproxen from blood samples. Supercritical fluid extraction was used to eliminate matrix effects before extraction with the mag-NPs. The effects of pH value of sample solution, amount of adsorbent, times of adsorption and desorption, salt effect, type and volume of suitable solvent for desorption were optimized. Under optimum conditions, magnetic solid phase extraction (MSPE) resulted in limits of detection that range between 0.1 and 0.3 μg L"−"1. In case of supercritical fluid extraction along with magnetic solid phase extraction (SFE- MSPE), the LODs ranged from 0.2 to 0.3 mg kg"−"1. The analytical ranges for all of the NSAIDs varied within 0.2–15 mg kg"-"1 and 0.1–250 μg L"−"1 in the SFE-MSPE and MSPE methods, respectively. The relative standard deviations for the extraction of the NSAIDs from blood samples via SFE-MSPE are <10.2%. (author)

  7. Structural and magnetic domains characterization of magnetite nanoparticles

    International Nuclear Information System (INIS)

    Santoyo-Salazar, J.; Castellanos-Roman, M.A.; Beatriz Gomez, L.

    2007-01-01

    Recently, important advances have been achieved in application, reproducibility and response ability of magnetic materials due to the relationships among processing, structure and nanometric size particle. Features like homogeneity of compounds and nanoparticle-sizing have improved some magnetic properties of materials and their field application. Of particular interest is the study of magnetic materials at the atomic and microstuctural level because the orientation and magnetic domains (large numbers of atoms moments coupled together in a preferential direction) can be observed. In this work, magnetite (Fe 3 O 4 ) powders which were obtained by precipitation route in alkaline medium are analyzed to identify the structure and mechanism formation of domains over the core and border of nanoparticles. Results obtained by XRD, atomic force microscopy (AFM) and magnetic force microscopy (MFM) showed a structural phase corresponding to Fe 3 O 4 and nanoparticles in a range of 20-40 nm. Samples scanned by MFM in nanometric resolution and profile images showed orientation of magnetic domains in the border and cores of the material. Finally, an analysis of repulsion and attraction in magnetic field and direction changes of domains formed by magnetite (Fe 3 O 4 ) powders were done

  8. Synthesis and characterization of nanometric magnetite coated by oleic acid and the surfactant CTAB

    Energy Technology Data Exchange (ETDEWEB)

    Celis, J. Almazán, E-mail: jony-jac-5@hotmail.com; Olea Mejía, O. F., E-mail: oleaoscar@yahoo.com [Universidad Autónoma del Estado de México, Centro Conjunto de Investigación en Química Sustentable UAEMéx-UNAM (Mexico); Cabral-Prieto, A., E-mail: agustin.cabral@inin.gob.mx; García-Sosa, I., E-mail: irma.garcia@inin.gob.mx [Instituto Nacional de Investigaciones Nucleares (Mexico); Derat-Escudero, R., E-mail: escu@unam.mx [Instituto de Investigación de materiales de la UNAM (Mexico); Baggio Saitovitch, E. M., E-mail: esaitovitch@yahoo.com.br; Alzamora Camarena, M., E-mail: mariella.alzamora@gmail.com [Centro Brasileiro de Pesquizas Físicas (Brazil)

    2017-11-15

    Nanometric magnetite (nm-Fe{sub 3}O{sub 4}) particles were prepared by the reverse co-precipitation synthesis method, obtaining particle sizes that ranged from 4 to 8.5 nm. In their synthesis, the concentration of iron salts of ferric nitrate, Fe(NO{sub 3}){sub 3}⋅9H{sub 2}O, and ferrous sulfate, FeSO{sub 4}⋅7H{sub 2}O, were varied relative to the chemical reaction volume and by using different surfactants such as oleic acid (OA) and hexadecyltrimethylammonium bromide (CTAB). The nm-Fe{sub 3}O{sub 4} particles were characterized by transmission electron microscopy (TEM), Mössbauer spectroscopy (MS), magnetic and X-ray diffraction (XRD) measurements. Typical asymmetrical and/or broad lines shapes appeared in all Mössbauer spectra of the as prepared samples suggesting strong magnetic inter-particle interactions, reducing these interactions to some extent by gentle mechanical grinding. For the smallest particles, maghemite instead of magnetite was the main preparation product as low temperature Mössbauer and magnetic measurements indicated. For the intermediate and largest particles a mixture of magnetite and maghemite phases were produced as the saturation magnetization values of M{sub S} ∼ 60 emu/g indicated; these values were measured for most samples, independently of the coating surfactant concentration, and according to the ZFC-FC curves the blocking temperatures were 225K and 275K for the smallest and largest magnetite nanoparticles, respectively. The synthesis method was highly reproducible.

  9. A comparison between acoustic properties and heat effects in biogenic (magnetosomes) and abiotic magnetite nanoparticle suspensions

    International Nuclear Information System (INIS)

    Józefczak, A.; Leszczyński, B.; Skumiel, A.; Hornowski, T.

    2016-01-01

    Magnetic nanoparticles show unique properties and find many applications because of the possibility to control their properties using magnetic field. Magnetic nanoparticles are usually synthesized chemically and modification of the particle surface is necessary. Another source of magnetic nanoparticles are various magnetotactic bacteria. These biogenic nanoparticles (magnetosomes) represent an attractive alternative to chemically synthesized iron oxide particles because of their unique characteristics and a high potential for biotechnological and biomedical applications. This work presents a comparison between acoustic properties of biogenic and abiotic magnetite nanoparticle suspensions. Experimental studies have shown the influence of a biological membrane on the ultrasound properties of magnetosomes suspension. Finally the heat effect in synthetic and biogenic magnetite nanoparticles is also discussed. The experimental study shows that magnetosomes present good heating efficiency. - Highlights: • A biogenic and abiotic magnetite nanoparticle suspensions are investigated. • A comparison between ultrasonic properties and heat effects is presented. • Magnetosomes and abiotic magnetite nanoparticles exhibit good heating efficiency.

  10. ELECTRON MICROSCOPY OF ANIONIC SURFACTANT-DIRECTED SYNTHESIS OF MAGNETITE NANOPARTICLES

    Directory of Open Access Journals (Sweden)

    Sharali Malik

    2016-06-01

    Full Text Available We have synthesized a variety of magnetite nanoparticles which appear to have biogenic signatures and could give insights into how the nanomagnetite particles form in biological systems, and how they are associated with Alzheimer’s disease. We have also synthesized mesoporous magnetite nanoparticles which have potential use in the targeted drug delivery.

  11. Synthesis, magnetic and ethanol gas sensing properties of semiconducting magnetite nanoparticles

    Science.gov (United States)

    Al-Ghamdi, Ahmed A.; Al-Hazmi, Faten; Al-Tuwirqi, R. M.; Alnowaiser, F.; Al-Hartomy, Omar A.; El-Tantawy, Farid; Yakuphanoglu, F.

    2013-05-01

    The superparamagnetic magnetite (Fe3O4) nanoparticles with an average size of 7 nm were synthesized using a rapid and facile microwave hydrothermal technique. The structure of the magnetite nanoparticles was characterized by X-ray diffraction (X-ray), field effect scanning electron microscopy (FESEM), energy dispersive X-ray spectroscopy (EDS), and transmission electron microscopy (TEM). The prepared Fe3O4 was shown to have a cubic phase of pure magnetite. Magnetization hysteresis loop shows that the synthesized magnetite exhibits no hysteretic features with a superparamagnetic behavior. The ethanol gas sensing properties of the synthesized magnetite were investigated, and it was found that the responsibility time is less than 10 s with good reproducibility for ethanol sensor. Accordingly, it is evaluated that the magnetite nanoparticles can be effectively used as a solid state ethanol sensor in industrial commercial product applications.

  12. Evidence for artificial magnetite coating on Iberian armoury

    Directory of Open Access Journals (Sweden)

    García, L.

    2011-04-01

    Full Text Available A metallographic study of two pre-roman Iberian arms, affected by a cremation process, revealed the presence of an outer magnetite layer, providing highly protective properties. This layer is extraordinarily tenacious and of very homogeneous thickness, indicating an intentional manufacturing process rather than an accidental formation during the severe heating/cooling cycles the artefact suffered. Up to date, the intentional production of these types of layers has been attributed to a welding process of three different metallic sheets, here an alternative model is proposed, allowing, as could be simulated in the laboratory, the virtually exclusive formation of a magnetite coating.

    Se presenta un estudio metalográficos de dos armas prerromanas afectadas por un proceso de cremación. Las armas poseen un recubrimiento exterior de magnetita que las confieren unas altas propiedades de protección frente a la corrosión. Esta capa es extraordinariamente tenaz y posee un espesor muy homogéneo, indicando que son producto de un proceso de fabricación intencionado más que una formación accidental durante los varios ciclos de calentamiento/ enfriamiento que han sufrido los objetos. Hasta la fecha, la producción intencional de este tipo de recubrimientos ha sido atribuida a un proceso de soldadura de tres láminas metálicas diferentes. En este trabajo se propone un modelo alternativo de formación, el cual permite una simulación en el laboratorio en la que se forma exclusivamente una capa de magnetita.

  13. Temperature-dependent structure of Tb-doped magnetite nanoparticles

    International Nuclear Information System (INIS)

    Rice, Katherine P.; Russek, Stephen E.; Shaw, Justin M.; Usselman, Robert J.; Evarts, Eric R.; Silva, Thomas J.; Nembach, Hans T.; Geiss, Roy H.; Arenholz, Elke; Idzerda, Yves U.

    2015-01-01

    High quality 5 nm cubic Tb-doped magnetite nanoparticles have been synthesized by a wet-chemical method to investigate tailoring of magnetic properties for imaging and biomedical applications. We show that the Tb is incorporated into the octahedral 3+ sites. High-angle annular dark-field microscopy shows that the dopant is well-distributed throughout the particle, and x-ray diffraction measurements show a small lattice parameter shift with the inclusion of a rare-earth dopant. Magnetization and x-ray magnetic circular dichroism data indicate that the Tb spins are unpolarized and weakly coupled to the iron spin lattice at room temperature, and begin to polarize and couple to the iron oxide lattice at temperatures below 50 K. Broadband ferromagnetic resonance measurements show no increase in magnetic damping at room temperature for Tb-doped nanoparticles relative to undoped nanoparticles, further confirming weak coupling between Fe and Tb spins at room temperature. The Gilbert damping constant, α, is remarkably low for the Tb-doped nanoparticles, with α = 0.024 ± 0.003. These nanoparticles, which have a large fixed moment, a large fluctuating moment and optically active rare-earth elements, are potential high-relaxivity T1 and T2 MRI agents with integrated optical signatures

  14. Temperature-dependent structure of Tb-doped magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Rice, Katherine P.; Russek, Stephen E., E-mail: stephen.russek@nist.gov; Shaw, Justin M.; Usselman, Robert J.; Evarts, Eric R.; Silva, Thomas J.; Nembach, Hans T. [National Institute of Standards and Technology, Boulder, Colorado 80305 (United States); Geiss, Roy H. [Colorado State University, Fort Collins, Colorado 80523 (United States); Arenholz, Elke [Lawrence Berkeley National Laboratory, Advanced Light Source, Berkeley, California 94720 (United States); Idzerda, Yves U. [Department of Physics, Montana State University, Bozeman, Montana 59717 (United States)

    2015-02-09

    High quality 5 nm cubic Tb-doped magnetite nanoparticles have been synthesized by a wet-chemical method to investigate tailoring of magnetic properties for imaging and biomedical applications. We show that the Tb is incorporated into the octahedral 3+ sites. High-angle annular dark-field microscopy shows that the dopant is well-distributed throughout the particle, and x-ray diffraction measurements show a small lattice parameter shift with the inclusion of a rare-earth dopant. Magnetization and x-ray magnetic circular dichroism data indicate that the Tb spins are unpolarized and weakly coupled to the iron spin lattice at room temperature, and begin to polarize and couple to the iron oxide lattice at temperatures below 50 K. Broadband ferromagnetic resonance measurements show no increase in magnetic damping at room temperature for Tb-doped nanoparticles relative to undoped nanoparticles, further confirming weak coupling between Fe and Tb spins at room temperature. The Gilbert damping constant, α, is remarkably low for the Tb-doped nanoparticles, with α = 0.024 ± 0.003. These nanoparticles, which have a large fixed moment, a large fluctuating moment and optically active rare-earth elements, are potential high-relaxivity T1 and T2 MRI agents with integrated optical signatures.

  15. Size-dependent reactivity of magnetite nanoparticles: a field-laboratory comparison

    Science.gov (United States)

    Swindle, Andrew L.; Elwood Madden, Andrew S.; Cozzarelli, Isabelle M.; Benamara, Mourad

    2014-01-01

    Logistic challenges make direct comparisons between laboratory- and field-based investigations into the size-dependent reactivity of nanomaterials difficult. This investigation sought to compare the size-dependent reactivity of nanoparticles in a field setting to a laboratory analog using the specific example of magnetite dissolution. Synthetic magnetite nanoparticles of three size intervals, ∼6 nm, ∼44 nm, and ∼90 nm were emplaced in the subsurface of the USGS research site at the Norman Landfill for up to 30 days using custom-made subsurface nanoparticle holders. Laboratory analog dissolution experiments were conducted using synthetic groundwater. Reaction products were analyzed via TEM and SEM and compared to initial particle characterizations. Field results indicated that an organic coating developed on the particle surfaces largely inhibiting reactivity. Limited dissolution occurred, with the amount of dissolution decreasing as particle size decreased. Conversely, the laboratory analogs without organics revealed greater dissolution of the smaller particles. These results showed that the presence of dissolved organics led to a nearly complete reversal in the size-dependent reactivity trends displayed between the field and laboratory experiments indicating that size-dependent trends observed in laboratory investigations may not be relevant in organic-rich natural systems.

  16. Comparative Cytogenetic Study on the Toxicity of Magnetite and Zinc Ferrite Nanoparticles in Sunflower Root Cells

    Science.gov (United States)

    Foca-nici, Ecaterina; Capraru, Gabriela; Creanga, Dorina

    2010-12-01

    In this experimental study the authors present their results regarding the cellular division rate and the percentage of chromosomal aberrations in the root meristematic cells of Helianthus annuus cultivated in the presence of different volume fractions of magnetic nanoparticle suspensions, ranging between 20 and 100 microl/l. The aqueous magnetic colloids were prepared from chemically co-precipitated ferrites coated in sodium oleate. Tissue samples from the root meristeme of 2-3 day old germinated seeds were taken to prepare microscope slides following Squash method combined with Fuelgen techniques. Microscope investigation (cytogenetic tests) has resulted in the evaluation of mitotic index and chromosomal aberration index that appeared diminished and respectively increased following the addition of magnetic nanoparticles in the culture medium of the young seedlings. Zinc ferrite toxic influence appeared to be higher than that of magnetite, according to both cytogenetic parameters.

  17. Fabrication of Magnetite/Silica/Titania Core-Shell Nanoparticles

    Directory of Open Access Journals (Sweden)

    Suh Cem Pang

    2012-01-01

    Full Text Available Fe3O4/SiO2/TiO2 core-shell nanoparticles were synthesized via a sol-gel method with the aid of sonication. Fe3O4 nanoparticles were being encapsulated within discrete silica nanospheres, and a layer of TiO2 shell was then coated directly onto each silica nanosphere. As-synthesized Fe3O4/SiO2/TiO2 core-shell nanoparticles showed enhanced photocatalytic properties as evidenced by the enhanced photodegradation of methylene blue under UV light irradiation.

  18. Immobilization of non-point phosphorus using stabilized magnetite nanoparticles with enhanced transportability and reactivity in soils

    International Nuclear Information System (INIS)

    Pan Gang; Li Lei; Zhao Dongye; Chen Hao

    2010-01-01

    Laboratory batch and column experiments were conducted to investigate the immobilization of phosphorus (P) in soils using synthetic magnetite nanoparticles stabilized with sodium carboxymethyl cellulose (CMC-NP). Although CMC-stabilized magnetite particles were at the nanoscale, phosphorus removal by the nanoparticles was less than that of microparticles (MP) without the stabilizer due to the reduced P reactivity caused by the coating. The P reactivity of CMC-NP was effectively recovered when cellulase was added to degrade the coating. For subsurface non-point P pollution control for a water pond, it is possible to inject CMC-NP to form an enclosed protection wall in the surrounding soils. Non-stabilized 'nanomagnetite' could not pass through the soil column under gravity because it quickly agglomerated into microparticles. The immobilized P was 30% in the control soil column, 33% when treated by non-stabilized MP, 45% when treated by CMC-NP, and 73% when treated by both CMC-NP and cellulase. - CMC-stabilized magnetite nanoparticles can effectively penetrate soil columns and immobilize phosphate in situ.

  19. Direct synthesis of magnetite nanoparticles from iron(II) carboxymethylcellulose and their performance as NMR contrast agents

    Energy Technology Data Exchange (ETDEWEB)

    Gomes da Silva, Delmarcio; Hiroshi Toma, Sergio; Menegatti de Melo, Fernando [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil); Carvalho, Larissa Vieira C.; Magalhães, Alvicler; Sabadini, Edvaldo [Instituto de Química, Universidade Estadual de Campinas – UNICAMP, Campinas, SP (Brazil); Domingues dos Santos, Antônio [Instituto de Física, Universidade de São Paulo, São Paulo, SP (Brazil); Araki, Koiti [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil); Toma, Henrique E., E-mail: henetoma@iq.usp.br [Instituto de Química, Universidade de São Paulo, São Paulo, SP (Brazil)

    2016-01-01

    Iron(II) carboxymethylcellulose (CMC) has been successfully employed in the synthesis of hydrophylic magnetite nanoparticles stabilized with a biopolymer coating, aiming applications in NMR imaging. The new method encompasses a convenient one-step synthetic procedure, allowing a good size control and yielding particles of about 10 nm (core size). In addition to the biocompatibility, the nanoparticles have promoted a drastic reduction in the transverse relaxation time (T{sub 2}) of the water protons. The relaxivity rates have been investigated as a function of the nanoparticles concentration, showing a better performance in relation to the common NMR contrast agents available in the market. - Highlights: • Stable, hydrophylic magnetic nanoparticles have been obtained. • Direct use of iron(II) carboxymethylcellulose improves the synthesis. • The magnetic nanoparticles exhibit high spin–spin relaxivity. • The particles promote dark contrast by decreasing the T{sub 2} relaxation time.

  20. Preparation and rheological studies of uncoated and PVA-coated magnetite nanofluid

    International Nuclear Information System (INIS)

    Khosroshahi, M.E.; Ghazanfari, L.

    2012-01-01

    Experimental studies of rheological behavior of uncoated magnetite nanoparticles (MNPs)U and polyvinyl alcohol (PVA) coated magnetite nanoparticles (MNPs)C were performed. A Co-precipitation technique under N 2 gas was used to prevent undesirable critical oxidation of Fe 2+ . The results showed that smaller particles can be synthesized in both cases by decreasing the NaOH concentration which in our case this corresponded to 35 nm and 7 nm using 0.9 M NaOH at 750 rpm for (MNPs)U and (MNPs)C. The stable magnetic fluid contained well-dispersed Fe 3 O 4 /PVA nanocomposites which indicated fast magnetic response. The rheological measurement of magnetic fluid indicated an apparent viscosity range (0.1–1.2) pa s at constant shear rate of 20 s −1 with a minimum value in the case of (MNPs)U at 0 T and a maximum value for (MNPs)C at 0.5 T. Also, as the shear rate increased from 20 s −1 to 150 s −1 at constant magnetic field, the apparent viscosity also decreased correspondingly. The water-based ferrofluid exhibited the non-Newtonian behavior of shear thinning under magnetic field. - Highlights: ► The stable water-based magnetic fluid with fast magnetic response was synthesized. ► The shear rate was increased from 20 S −1 to 150 S −1 at constant magnetic field. ► The viscosity of magnetic fluid decreased with increasing of shear rate. ► Viscosity range (0.1–1.2) pa s was measured for (MNPs)U and (MNPs)C. ► The ferrofluid was non-Newtonian (shear thinning) under magnetic field.

  1. Preparation of size-controlled magnetite nanoparticles with a graphene and polymeric ionic liquid coating for the quick, easy, cheap, effective, rugged and safe extraction of preservatives from vegetables.

    Science.gov (United States)

    Chen, Yaling; Cao, Shurui; Zhang, Lei; Xi, Cunxian; Li, Xianliang; Chen, Zhiqiong; Wang, Guoming

    2016-05-27

    Size-controlled magnetite nanoparticles (Fe3O4) with 200-1000nm were synthesized by co-precipitation method. Then Fe3O4@SiO2@G@PIL was synthesized and used as modified QuEChERS adsorbent for the determination of preservatives in vegetables. The size of about 200nm of Fe3O4 in Fe3O4@SiO2@G@PIL was selected as optimum size to clean-up. It not only exerted the nanometer features of magnetic nanoparticles, but also displayed the large specific surface area of graphene (G) and the solvent effects of polymeric ionic liquids (PILs). Various experimental parameters have been investigated. Under the optimized conditions, a simple, rapid and effective method for the determination of 20 preservatives residues in vegetables was established by modified QuEChERS to gas chromatography/mass spectrometry (GC-MS) analysis. The good linearity with correlation coefficients (R(2)) of 0.9972-0.9999 was obtained over the range of 0.02-2.00mg/L for 20 preservatives. The detection limits of the proposed method for 20 preservatives ranged from 0.82 to 6.64μg/kg. The adsorbent was successfully applied for extraction and determination of preservatives in vegetable samples, which thus was time-saving with keeping good clean-up performance. Copyright © 2016 Elsevier B.V. All rights reserved.

  2. Synthesis of non-aggregated nicotinic acid coated magnetite nanorods via hydrothermal technique

    Energy Technology Data Exchange (ETDEWEB)

    Attallah, Olivia A., E-mail: olivia.adly@hu.edu.eg [Center of Nanotechnology, Nile University, 12677 Giza (Egypt); Pharmaceutical Chemistry Department, Heliopolis University, 11777 El Salam, Cairo (Egypt); Girgis, E. [Solid State Physics Department, National Research Center, 12622 Dokki, Giza (Egypt); Advanced Materials and Nanotechnology Lab, CEAS, National Research Center, 12622 Dokki, Giza (Egypt); Abdel-Mottaleb, Mohamed M.S.A. [Center of Nanotechnology, Nile University, 12677 Giza (Egypt)

    2016-02-01

    Non-aggregated magnetite nanorods with average diameters of 20–30 nm and lengths of up to 350 nm were synthesized via in situ, template free hydrothermal technique. These nanorods capped with different concentrations (1, 1.5, 2 and 2.5 g) of nicotinic acid (vitamin B3); possessed good magnetic properties and easy dispersion in aqueous solutions. Our new synthesis technique maintained the uniform shape of the nanorods even with increasing the coating material concentration. The effect of nicotinic acid on the shape, particle size, chemical structure and magnetic properties of the prepared nanorods was evaluated using different characterization methods. The length of nanorods increased from 270 nm to 350 nm in nicotinic acid coated nanorods. Goethite and magnetite phases with different ratios were the dominant phases in the coated samples while a pure magnetite phase was observed in the uncoated one. Nicotinic acid coated magnetic nanorods showed a significant decrease in saturation magnetization than uncoated samples (55 emu/g) reaching 4 emu/g in 2.5 g nicotinic acid coated sample. The novel synthesis technique proved its potentiality to prepare coated metal oxides with one dimensional nanostructure which can function effectively in different biological applications. - Highlights: • We synthesize nicotinic acid coated magnetite nanorods via hydrothermal technique • Effect of nicotinic acid concentration on the nanorods properties was significant • Nanorods maintained uniform shape with increased concentration of nicotinic acid • Alterations occurred in particle size, mineral phases and magnetics of coated samples.

  3. Synthesis of non-aggregated nicotinic acid coated magnetite nanorods via hydrothermal technique

    International Nuclear Information System (INIS)

    Attallah, Olivia A.; Girgis, E.; Abdel-Mottaleb, Mohamed M.S.A.

    2016-01-01

    Non-aggregated magnetite nanorods with average diameters of 20–30 nm and lengths of up to 350 nm were synthesized via in situ, template free hydrothermal technique. These nanorods capped with different concentrations (1, 1.5, 2 and 2.5 g) of nicotinic acid (vitamin B3); possessed good magnetic properties and easy dispersion in aqueous solutions. Our new synthesis technique maintained the uniform shape of the nanorods even with increasing the coating material concentration. The effect of nicotinic acid on the shape, particle size, chemical structure and magnetic properties of the prepared nanorods was evaluated using different characterization methods. The length of nanorods increased from 270 nm to 350 nm in nicotinic acid coated nanorods. Goethite and magnetite phases with different ratios were the dominant phases in the coated samples while a pure magnetite phase was observed in the uncoated one. Nicotinic acid coated magnetic nanorods showed a significant decrease in saturation magnetization than uncoated samples (55 emu/g) reaching 4 emu/g in 2.5 g nicotinic acid coated sample. The novel synthesis technique proved its potentiality to prepare coated metal oxides with one dimensional nanostructure which can function effectively in different biological applications. - Highlights: • We synthesize nicotinic acid coated magnetite nanorods via hydrothermal technique • Effect of nicotinic acid concentration on the nanorods properties was significant • Nanorods maintained uniform shape with increased concentration of nicotinic acid • Alterations occurred in particle size, mineral phases and magnetics of coated samples.

  4. Characterization of single-core magnetite nanoparticles for magnetic imaging by SQUID relaxometry

    International Nuclear Information System (INIS)

    Adolphi, Natalie L; Huber, Dale L; Monson, Todd C; Provencio, Paula P; Bryant, Howard C; Fegan, Danielle L; Tessier, Trace E; Flynn, Edward R; Lim, JitKang; Majetich, Sara A; Trujillo, Jason E; Lovato, Debbie M; Butler, Kimberly S; Larson, Richard S; Hathaway, Helen J

    2010-01-01

    Optimizing the sensitivity of SQUID (superconducting quantum interference device) relaxometry for detecting cell-targeted magnetic nanoparticles for in vivo diagnostics requires nanoparticles with a narrow particle size distribution to ensure that the Neel relaxation times fall within the measurement timescale (50 ms-2 s, in this work). To determine the optimum particle size, single-core magnetite nanoparticles (with nominal average diameters 20, 25, 30 and 35 nm) were characterized by SQUID relaxometry, transmission electron microscopy, SQUID susceptometry, dynamic light scattering and zeta potential analysis. The SQUID relaxometry signal (detected magnetic moment/kg) from both the 25 nm and 30 nm particles was an improvement over previously studied multi-core particles. However, the detected moments were an order of magnitude lower than predicted based on a simple model that takes into account the measured size distributions (but neglects dipolar interactions and polydispersity of the anisotropy energy density), indicating that improved control of several different nanoparticle properties (size, shape and coating thickness) will be required to achieve the highest detection sensitivity. Antibody conjugation and cell incubation experiments show that single-core particles enable a higher detected moment per cell, but also demonstrate the need for improved surface treatments to mitigate aggregation and improve specificity.

  5. Characterization of single-core magnetite nanoparticles for magnetic imaging by SQUID relaxometry

    Energy Technology Data Exchange (ETDEWEB)

    Adolphi, Natalie L [Department of Biochemistry and Molecular Biology, University of New Mexico, Albuquerque, NM 87131 (United States); Huber, Dale L; Monson, Todd C; Provencio, Paula P [Sandia National Laboratories, P. O. Box 5800, Albuquerque, NM 87185 (United States); Bryant, Howard C; Fegan, Danielle L; Tessier, Trace E; Flynn, Edward R [Senior Scientific, LLC, 11109 Country Club NE, Albuquerque, NM 87111 (United States); Lim, JitKang; Majetich, Sara A [Department of Physics, Carnegie Mellon University, Pittsburgh, PA 15213 (United States); Trujillo, Jason E; Lovato, Debbie M; Butler, Kimberly S; Larson, Richard S [Department of Pathology, Cancer Research and Treatment Center, University of New Mexico, Albuquerque, NM 87131 (United States); Hathaway, Helen J, E-mail: NAdolphi@salud.unm.ed [Department of Cell Biology and Physiology, University of New Mexico, Albuquerque, NM 87131 (United States)

    2010-10-07

    Optimizing the sensitivity of SQUID (superconducting quantum interference device) relaxometry for detecting cell-targeted magnetic nanoparticles for in vivo diagnostics requires nanoparticles with a narrow particle size distribution to ensure that the Neel relaxation times fall within the measurement timescale (50 ms-2 s, in this work). To determine the optimum particle size, single-core magnetite nanoparticles (with nominal average diameters 20, 25, 30 and 35 nm) were characterized by SQUID relaxometry, transmission electron microscopy, SQUID susceptometry, dynamic light scattering and zeta potential analysis. The SQUID relaxometry signal (detected magnetic moment/kg) from both the 25 nm and 30 nm particles was an improvement over previously studied multi-core particles. However, the detected moments were an order of magnitude lower than predicted based on a simple model that takes into account the measured size distributions (but neglects dipolar interactions and polydispersity of the anisotropy energy density), indicating that improved control of several different nanoparticle properties (size, shape and coating thickness) will be required to achieve the highest detection sensitivity. Antibody conjugation and cell incubation experiments show that single-core particles enable a higher detected moment per cell, but also demonstrate the need for improved surface treatments to mitigate aggregation and improve specificity.

  6. Computer enhancement of ESR spectra of magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Dobosz, B.; Krzyminiewski, R. [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznan (Poland); Koralewski, M. [Optics Laboratory, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznan (Poland); Hałupka-Bryl, M. [Medical Physics Division, Faculty of Physics, Adam Mickiewicz University, Umultowska 85, 61-614 Poznan (Poland); The PhD Program in Nanoscience and Nanotechnology, The Nanobiomedical Centre, Umultowska 85, 61-614 Poznan (Poland)

    2016-06-01

    We present ESR measurements of non-interacting magnetic nanoparticle systems. Temperature and orientational dependence of ESR spectra were measured for Fe{sub 3}O{sub 4} nanoparticle coated by dextran or oleic acid, frozen in different magnetic field. Several parameters describing magnetic properties such as g-factor, line width, the anisotropy constant were calculated and discussed. The ESR spectra of investigated nanoparticles were also subjected to Computer Resolution Enhancement Method (CREM). This procedure allows to separate a narrow line on the background of the broad line, which presence in this type of materials was recognized in the recent literature and have been further discussed in the paper. CREM is a valuable tool for monitoring of changes on the surface of magnetic core of nanoparticles. - Highlights: • CREM – a new tool for monitoring of changes on the surface of magnetic core of nanoparticles. • CREM allows to separate a narrow line on the background of the broad line. • Temperature and orientational dependence of ESR spectra of Fe{sub 3}O{sub 4} nanoparticles were measured. • Parameters describing magnetic properties were calculated and discussed.

  7. High stable suspension of magnetite nanoparticles in ethanol by using sono-synthesized nanomagnetite in polyol medium

    International Nuclear Information System (INIS)

    Bastami, Tahereh Rohani; Entezari, Mohammad H.

    2013-01-01

    Graphical abstract: - Highlights: • The sonochemical synthesis of magnetite nanoparticles was carried out in EG without any surfactant. • The nanoparticles with sizes ∼24 nm were composed of small building blocks with sizes ∼2 nm. • The hydrophilic magnetite nanoparticles were stable in ethanol even after 8 months. • Ultrasonic intensity showed a crucial role on the obtained high stable magnetite nanoparticles in ethanol. - Abstract: The sonochemical synthesis of magnetite nanoparticles was carried out at relatively low temperature (80 °C) in ethylene glycol (EG) as a polyol solvent. The particle size was determined by transmission electron microscopy (TEM). The magnetite nanoparticles with an average size of 24 nm were composed of small building blocks with an average size of 2–3 nm and the particles exhibited nearly spherical shape. The surface characterization was investigated by using Fourier transform infrared (FTIR) spectroscopy, X-ray photoelectron spectroscopy (XPS), and thermogravimetric analysis (TGA). The stability of magnetite nanoparticles was studied in ethanol as a polar solvent. The nanoparticles showed an enhanced stability in ethanol which is due to the hydrophilic surface of the particles. The colloidal stability of magnetite nanoparticles in ethanol was monitored by UV–visible spectrophotometer. According to the results, the nanoparticles synthesized in 30 min of sonication with intensity of 35 W/cm 2 (50%) led to a maximum stability in ethanol as a polar solvent with respect to the other applied intensities. The obtained magnetite nanoparticles were stable for more than12 months

  8. A study on the effect of chemically synthesized magnetite nanoparticles on earthworm: Eudrilus eugeniae

    Science.gov (United States)

    Samrot, Antony V.; Justin, C.; Padmanaban, S.; Burman, Ujjala

    2017-02-01

    Most look into the benefits of the nanoparticles, but keeping aside the benefits; this study focuses on the impacts of nanoparticles on living systems. Improper disposal of nanoparticles into the environment is a subject of pollution or nano-pollution which in turn affects the flora and fauna in the ecosystem, particularly soil ecosystem. Thus, this study was done to understand the impacts of chemically synthesized magnetite nanoparticles on earthworm— Eudrilus eugeniae, a soil-dependent organism which acquires food and nutrition from decaying matters. The chemically synthesized magnetite nanoparticles were characterized by UV-visible spectrophotometry, Fourier transform infrared spectroscopy and field emission scanning electron microscopy. Earthworms were allowed to interact with different concentrations of synthesized nanoparticles and the effect of the nanoparticles was analysed by studying the phenotypic changes followed by histology and inductively coupled plasma optical emission spectrometry analyses.

  9. Novel environmentally friendly synthesis of superparamagnetic magnetite nanoparticles using mechanochemical effect

    International Nuclear Information System (INIS)

    Iwasaki, Tomohiro; Kosaka, Kazunori; Watano, Satoru; Yanagida, Takeshi; Kawai, Tomoji

    2010-01-01

    A novel method for synthesizing superparamagnetic magnetite nanoparticles in water system via coprecipitation under an environmentally friendly condition has been developed. In this method, an almost neutral suspension containing ferrous hydroxide and goethite is used as the starting suspension and subjected to a ball-milling treatment. The product was characterized by transmission electron microscopy, X-ray diffraction, energy dispersive X-ray spectroscopy, dynamic light scattering, superconducting quantum interference device magnetometry, and Moessbauer spectroscopy. The mechanochemical effect generated by the ball-milling treatment promoted the reaction between ferrous hydroxide and goethite even at room temperature, resulting in the formation of homogeneous magnetite nanoparticles. Simultaneously, it also contributed to crystallize the formed magnetite nanoparticles while inhibiting the particle growth. This resulted in the formation of ultrafine magnetite nanoparticles of about 10 nm having a single crystal structure. This method could provide ferromagnetic magnetite nanoparticles with superparamagnetism under the moderate condition without neither heating nor any additives such as surfactant and organic solvent.

  10. Immobilization of Thiadiazole Derivatives on Magnetite Mesoporous Silica Shell Nanoparticles in Application to Heavy Metal Removal from Biological Samples

    International Nuclear Information System (INIS)

    Emadi, Masoomeh; Shams, Esmaeil

    2010-01-01

    In this report magnetite was synthesized by a coprecipitation method, then coated with a layer of silica. Another layer of mesoporous silica was added by a sol-gel method, then 5-amino-1,3,4-thiadiazole-thiol (ATT) was immobilized onto the synthesized nanoparticles with a simple procedure. This was followed by a series of characterizations, including transmission electron microscopy (TEM), FT-IR spectrum, elemental analysis and XRD. Heavy metal uptake of the modified nanoparticles was examined by atomic absorption spectroscopy. For further investigation we chose Cu 2+ as the preferred heavy metal to evaluate the amount of adsorption, as well as the kinetics and mechanism of adsorption. Finally, the capacity of our nanoparticles for the heavy metal removal from blood was shown. We found that the kinetic rate of Cu 2+ adsorption was 0.05 g/mg/min, and the best binding model was the Freundlich isotherm.

  11. Ultrasonic-assisted synthesis of magnetite based MRI contrast agent using cysteine as the biocapping coating

    International Nuclear Information System (INIS)

    Ahmadi, Reza; Malek, Mahrooz; Hosseini, Hamid Reza Madaah; Shokrgozar, Mohammad Ali; Oghabian, Mohammad Ali; Masoudi, Afshin; Gu Ning; Zhang Yu

    2011-01-01

    Highlights: ► We used cysteine as surfactant to synthesize stable magnetite-based ferrofluids. ► pH increase from 11 to 12 led to particle size decrease from 19.58 to 10.02 nm. ► Cytotoxicity assay showed that synthesized particles were biocompatible. ► MRI results showed that magnetite particles were accumulated in lymph nodes. - Abstract: Magnetite nanoparticles (mean particle size ranging from 10 to 20 nm) were prepared by a biomolecule-assisted solution-phase approach under ultrasonic irradiation. Cysteine was used as the capping agent in the solution. The results show that cysteine could be an efficient biocapping agent in producing Fe 3 O 4 nanoparticles. The crystal structure and magnetic properties of the nanoparticles were characterized by XRD and VSM techniques, respectively. FT-IR was used to investigate the presence of cysteine on the nanoparticles surface. The influence of pH value of the solution on the size distribution and hydrodynamic size of nanoparticles were studied by TEM and DLS methods, respectively. The MTT assay performed by incubation of L929 cells, showed the good biocompability of synthesized ferrofluids. In vitro T1 and T2 relaxivity measurements along with in vivo studies, which were conducted on rats, demonstrate that synthesized nanoparticles are applicable as the contrast agents, especially for imaging of the lymphatic system.

  12. The effect of yttrium substitution on the magnetic properties of magnetite nanoparticles

    International Nuclear Information System (INIS)

    Mozaffari, M.; Amighian, J.; Tavakoli, R.

    2015-01-01

    Superparamagnetic Y-substituted magnetite (Y x Fe 3–x O 4 ,with x=0.00, 0.10, 0.15, 0.20 and 0.40) nanoparticles were synthesized via hydrothermal reduction route in the presence of citric acid. The synthesized nanoparticles were characterized by X-ray diffraction (XRD) analysis, Fourier transform infrared (FTIR) spectroscopy, field emission scanning electron microscopy (FESEM), vibrating sample magnetometry (VSM) and gradient field thermomagnetic measurement. The results showed that a minimum amount of citric acid is required to obtain single phase Y-substituted magnetite nanoparticles. Citric acid acts as a modulator and reducing agent in the formation of spinel structure and controls nanoparticle size and crystallinity. Mean crystallite sizes of the single-phase powders were estimated by Williamson–Hall method. Curie temperature measurement of the samples shows that as yttrium content increases, the Curie temperature decreases. Magnetic measurements show that the saturation magnetization of the samples decreases as x increases up to 0.15 and then increases to x=0.20 and finally decreases again for x=0.40. - Highlights: • Single phase yttrium substituted magnetite nanoparticles were synthesized by hydrothermal-reduction route. • Citric acid plays a key role in reduction of Fe 3+ to Fe 2+ , which is necessary for the formation of magnetite phase. • It is possible to substitute yttrium ions for iron ones as high as x=0.4 by hydrothermal reduction route. • Pure magnetite nanoparticles prepared by this route has a high saturation magnetization. • Yttrium substituted magnetite nanoparticles are superparamagnet at room temperature

  13. Fabrication and Characterization of Magnetoresponsive Electrospun Nanocomposite Membranes Based on Methacrylic Random Copolymers and Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ioanna Savva

    2012-01-01

    Full Text Available Magnetoresponsive polymer-based fibrous nanocomposites belonging to the broad category of stimuli-responsive materials, is a relatively new class of “soft” composite materials, consisting of magnetic nanoparticles embedded within a polymeric fibrous matrix. The presence of an externally applied magnetic field influences the properties of these materials rendering them useful in numerous technological and biomedical applications including sensing, magnetic separation, catalysis and magnetic drug delivery. This study deals with the fabrication and characterization of magnetoresponsive nanocomposite fibrous membranes consisting of methacrylic random copolymers based on methyl methacrylate (MMA and 2-(acetoacetoxyethyl methacrylate (AEMA (MMA-co-AEMA and oleic acid-coated magnetite (OA·Fe3O4 nanoparticles. The AEMA moieties containing β-ketoester side-chain functionalities were introduced for the first time in this type of materials, because of their inherent ability to bind effectively onto inorganic surfaces providing an improved stabilization. For membrane fabrication the electrospinning technique was employed and a series of nanocomposite membranes was prepared in which the polymer content was kept constant and only the inorganic (OA·Fe3O4 content varied. Further to the characterization of these materials in regards to their morphology, composition and thermal properties, assessment of their magnetic characteristics disclosed tunable superparamagnetic behaviour at ambient temperature.

  14. Electrochemical and dissolution studies on coated film and magnetite pellet in PDCA and NTA based formulations

    International Nuclear Information System (INIS)

    Srinivasan, M.P.; Sumathi, S.; Rangarajan, S.; Narasimhan, S.V.

    2000-01-01

    In water cooled nuclear reactors magnetite often exists as both mobile particulate protective film on the inner surface of the PHT system. To determine the mechanism and kinetics of dissolution from a film coated on carbon steel (CS) and magnetite pellet electrochemical measurements were carried out in 2,6-pyridine dicarboxylic acid (PDCA) and nitrilo-triacetic acid (NTA) based formulations containing ascorbic acid (AA) and citric acid (CA) at 28 degC and 60 degC. The solution redox potential arises based on the release of relative amounts of Fe 2+ and Fe 3+ . Complexation, adsorption and reduction affect the concentration of these species in solutions. On coated specimen, the pore size and rate of formation via auto reduction contribute to the observed potential. In PDCA based formulation higher percentage of magnetite dissolution with lower base metal corrosion was observed as compared to that in NTA based formulation. The base metal aided dissolution due to the pores and microcracks in the film (Auto reduction) was observed for coated film. The dominant role of surface adsorption characteristics of PDCA, AA and CA were evident in magnetite pellet dissolution studies. (author)

  15. Fabrication of amine-functionalized magnetite nanoparticles for water treatment processes

    Energy Technology Data Exchange (ETDEWEB)

    Chan, Candace C. P. [University of South Australia, Ian Wark Research Institute (Australia); Gallard, Herve [Universite de Poitiers, Laboratoire de Chimie et Microbiologie de l' Eau (LCME)-UMR CNRS 6008 (France); Majewski, Peter, E-mail: peter.majewski@unisa.edu.au [Mawson Institute, University of South Australia, School of Advanced Manufacturing and Mechanical Engineering (Australia)

    2012-03-15

    Amine-functionalized magnetite nanoparticles are synthesized by a one pot water based process using N-[3-(trimethoxysilyl)propyl]diethylenetriamine (TRIS) as surfactant. The prepared functionalised nanoparticles are characterised by BET surface area measurements, X-ray diffraction, zeta potential measurement, and X-ray photoelectron spectrometry (XPS). The results clearly show the presence of TRIS on the surface of the nanoparticles. XPS analysis indicates the presence of very small amounts of maghemite on the surface of the magnetite nanoparticles. Water treatment test shows that the prepared nanoparticles are capable to remove natural organic matter (NOM) from natural water samples. The removal of NOM by the prepared particles is characterized by analysing the dissolved organic carbon (DOC) content and UV absorbance at 254 nm (UV{sub 254}) after the treatment of the water samples at various doses and treatment times.

  16. Fabrication of amine-functionalized magnetite nanoparticles for water treatment processes

    International Nuclear Information System (INIS)

    Chan, Candace C. P.; Gallard, Hervé; Majewski, Peter

    2012-01-01

    Amine-functionalized magnetite nanoparticles are synthesized by a one pot water based process using N-[3-(trimethoxysilyl)propyl]diethylenetriamine (TRIS) as surfactant. The prepared functionalised nanoparticles are characterised by BET surface area measurements, X-ray diffraction, zeta potential measurement, and X-ray photoelectron spectrometry (XPS). The results clearly show the presence of TRIS on the surface of the nanoparticles. XPS analysis indicates the presence of very small amounts of maghemite on the surface of the magnetite nanoparticles. Water treatment test shows that the prepared nanoparticles are capable to remove natural organic matter (NOM) from natural water samples. The removal of NOM by the prepared particles is characterized by analysing the dissolved organic carbon (DOC) content and UV absorbance at 254 nm (UV 254 ) after the treatment of the water samples at various doses and treatment times.

  17. Removal of hexavalent chromium [Cr(VI)] from aqueous solutions by the diatomite-supported/unsupported magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Yuan Peng, E-mail: yuanpeng@gig.ac.cn [Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); Liu Dong; Fan Mingde; Yang Dan [Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China); Graduate School of Chinese Academy of Sciences, Beijing 100039 (China); Zhu Runliang; Ge Fei [College of Chemical Engineering, Xiangtan University, Xiangtan 411105 (China); Zhu Jianxi; He Hongping [Guangzhou Institute of Geochemistry, Chinese Academy of Sciences, Guangzhou 510640 (China)

    2010-01-15

    Diatomite-supported/unsupported magnetite nanoparticles were prepared by co-precipitation and hydrosol methods, and characterized by X-ray diffraction, nitrogen adsorption, elemental analysis, differential scanning calorimetry, transmission electron microscopy and X-ray photoelectron spectroscopy. The average sizes of the unsupported and supported magnetite nanoparticles are around 25 and 15 nm, respectively. The supported magnetite nanoparticles exist on the surface or inside the pores of diatom shells, with better dispersing and less coaggregation than the unsupported ones. The uptake of hexavalent chromium [Cr(VI)] on the synthesized magnetite nanoparticles was mainly governed by a physico-chemical process, which included an electrostatic attraction followed by a redox process in which Cr(VI) was reduced into trivalent chromium [Cr(III)]. The adsorption of Cr(VI) was highly pH-dependent and the kinetics of the adsorption followed a pseudo-second-order model. The adsorption data of diatomite-supported/unsupported magnetite fit well with the Langmuir isotherm equation. The supported magnetite showed a better adsorption capacity per unit mass of magnetite than unsupported magnetite, and was more thermally stable than their unsupported counterparts. These results indicate that the diatomite-supported/unsupported magnetite nanoparticles are readily prepared, enabling promising applications for the removal of Cr(VI) from aqueous solution.

  18. Removal of hexavalent chromium [Cr(VI)] from aqueous solutions by the diatomite-supported/unsupported magnetite nanoparticles.

    Science.gov (United States)

    Yuan, Peng; Liu, Dong; Fan, Mingde; Yang, Dan; Zhu, Runliang; Ge, Fei; Zhu, JianXi; He, Hongping

    2010-01-15

    Diatomite-supported/unsupported magnetite nanoparticles were prepared by co-precipitation and hydrosol methods, and characterized by X-ray diffraction, nitrogen adsorption, elemental analysis, differential scanning calorimetry, transmission electron microscopy and X-ray photoelectron spectroscopy. The average sizes of the unsupported and supported magnetite nanoparticles are around 25 and 15 nm, respectively. The supported magnetite nanoparticles exist on the surface or inside the pores of diatom shells, with better dispersing and less coaggregation than the unsupported ones. The uptake of hexavalent chromium [Cr(VI)] on the synthesized magnetite nanoparticles was mainly governed by a physico-chemical process, which included an electrostatic attraction followed by a redox process in which Cr(VI) was reduced into trivalent chromium [Cr(III)]. The adsorption of Cr(VI) was highly pH-dependent and the kinetics of the adsorption followed a pseudo-second-order model. The adsorption data of diatomite-supported/unsupported magnetite fit well with the Langmuir isotherm equation. The supported magnetite showed a better adsorption capacity per unit mass of magnetite than unsupported magnetite, and was more thermally stable than their unsupported counterparts. These results indicate that the diatomite-supported/unsupported magnetite nanoparticles are readily prepared, enabling promising applications for the removal of Cr(VI) from aqueous solution.

  19. Control of nanoparticle size, reactivity and magnetic properties during the bioproduction of magnetite by Geobacter sulfurreducens

    Energy Technology Data Exchange (ETDEWEB)

    Byrne, J. M.; Telling, N. D.; Coker, V. S.; Pattrick, R. A. D.; Laan, G. van der; Arenholz, E.; Tuna, F.; Lloyd, J. R.

    2011-08-02

    The bioproduction of nano-scale magnetite by Fe(III)-reducing bacteria offers a potentially tunable, environmentally benign route to magnetic nanoparticle synthesis. Here, we demonstrate that it is possible to control the size of magnetite nanoparticles produced by Geobacter sulfurreducens, by adjusting the total biomass introduced at the start of the process. The particles have a narrow size distribution and can be controlled within the range of 10-50 nm. X-ray diffraction analysis indicates that controlled production of a number of different biominerals is possible via this method including goethite, magnetite and siderite, but their formation is strongly dependent upon the rate of Fe(III) reduction and total concentration and rate of Fe(II) produced by the bacteria during the reduction process. Relative cation distributions within the structure of the nanoparticles has been investigated by X-ray magnetic circular dichroism and indicates the presence of a highly reduced surface layer which is not observed when magnetite is produced through abiotic methods. The enhanced Fe(II)-rich surface, combined with small particle size, has important environmental applications such as in the reductive bioremediation of organics, radionuclides and metals. In the case of Cr(VI), as a model high-valence toxic metal, optimised biogenic magnetite is able to reduce and sequester the toxic hexavalent chromium very efficiently in the less harmful trivalent form.

  20. Clustering of carboxylated magnetite nanoparticles through polyethylenimine: Covalent versus electrostatic approach

    Energy Technology Data Exchange (ETDEWEB)

    Tóth, Ildikó Y., E-mail: Ildiko.Toth@chem.u-szeged.hu [Department of Physical Chemistry and Materials Science, University of Szeged, Aradi vt. square 1, Szeged (Hungary); Nesztor, Dániel [Department of Physical Chemistry and Materials Science, University of Szeged, Aradi vt. square 1, Szeged (Hungary); Novák, Levente [Department of Colloid and Environmental Chemistry, University of Debrecen, Egyetem square 1, Debrecen (Hungary); Illés, Erzsébet; Szekeres, Márta; Szabó, Tamás [Department of Physical Chemistry and Materials Science, University of Szeged, Aradi vt. square 1, Szeged (Hungary); Tombácz, Etelka, E-mail: tombacz@chem.u-szeged.hu [Department of Physical Chemistry and Materials Science, University of Szeged, Aradi vt. square 1, Szeged (Hungary)

    2017-04-01

    Carboxylated magnetite nanoparticles (MNPs) are frequently used to develop materials with enhanced properties for MRI and hyperthermia. The controlled clustering of MNPs via covalent or electrostatic approaches provides opportunity to prepare high quality materials. MNPs were prepared by co-precipitation and coated by poly(acrylic acid-co-maleic acid) (PAM@MNP). The clusters were synthesized from purified PAM@MNPs and polyethylenimine (PEI) solution via electrostatic interaction and covalent bond formation (ES-cluster and CB-cluster, respectively). The electrostatic adhesion (–NH{sub 3}{sup +} and –COO{sup –}) and the formed amide bond were confirmed by ATR-FTIR. The averaged area of CB-clusters was about twice as large as that of ES-cluster, based on TEM. The SAXS results showed that the surface of MNPs was smooth and the nanoparticles were close packed in both clusters. The pH-dependent aggregation state and zeta potential of clusters were characterized by DLS and electrophoresis measurements, the clusters were colloidally stable at pH>5. In hyperthermia experiments, the values of SAR were about two times larger for the chemically bonded cluster. The MRI studies showed exceptionally high transversion relaxivities, the r{sub 2} values are 457 mM{sup −1} s{sup −1} and 691 mM{sup −1} s{sup −1} for ES-cluster and CB-cluster, respectively. Based on these results, the chemically clustered product shows greater potential for feasible biomedical applications. - Highlights: • Chemically bonded clusters (CB-cluster) were prepared from PEI and PAM-coated MNPs. • The electrostatically clustered units (ES-cluster) are smaller and more compact. • The electrostatic adhesion and the amide bond formation were confirmed by ATR-FTIR. • CB-cluster dispersions are colloidally stable under physiological conditions. • CB-cluster shows great potential for application in MRI and hyperthermia.

  1. Adsorption of uranyl ions in nanoparticles of magnetite

    International Nuclear Information System (INIS)

    Holland, Helber; Yamaura, Mitiko

    2009-01-01

    This work studied the uranium (VI) adsorption, in the form of UO 2 2+ ions, of the nitride solution by the syntetic magnetite. This solution was prepared by precipitation adding a solution of NaOH to the solution containing the ions Fe 2+ . The time of contact and the isothermal of equilibrium of ions UO 2 2+ adsorption was verified. The isothermal of equilibrium presented more concordance with the Freundlich model, which characterized a heterogeneous adsorption surface of the magnetite. The great advantage of this technology is the combination of two separation techniques, by adsorption and magnetic, resulting in a highly efficient and reusable system

  2. A study of the barrier properties of polyethylene coated with a nanocellulose/magnetite composite film

    Directory of Open Access Journals (Sweden)

    Đorđević Nenad

    2016-01-01

    Full Text Available The morphological, thermal and barrier properties of low-density polyethylene/polycaprolactone-modified nanocellulose hybrid materials were investigated in this paper. Nanonocelulose/magnetite (NC-Fe3O4 nanocomposite and maleic acid functionalized NC/magnetite (NCMA-Fe3O4 nanocomposite were prepared and used as filler at various concentrations (5, 10 and 15 wt. % in polycaprolactone (PCL layer. PE was coated with PCL/NC/magnetite layer. The addition of the filler did not unfavorably affect the inherent properties of the polymer, especially its barrier properties. Oxygen permeation measurements show that the oxygen barrier properties of magnetite enriched PCL film were improved due to chemical activity of added material. The highest level of barrier capacity was observed for PE samples coated with PCL based composite with NCMA-Fe3O4 micro/-nanofiller, which implies the significant contribution of nanocellulose surface modification with maleic anhydride residue to improved barrier properties. [Projekat Ministarstva nauke Republike Srbije, br. III45019 i br. OI172013

  3. Adsorptive removal of bisphenol A using synthesized magnetite nanoparticles

    Science.gov (United States)

    Orimolade, B. O.; Adekola, F. A.; Adebayo, G. B.

    2018-03-01

    Bisphenol A (BPA) is an organic compound which is often used as plasticizer and has been reported to be hazardous to man. In this research the efficiency of removal of BPA from water by magnetite through adsorption process was studied. The magnetite was synthesized using reverse co-precipitation method and fully characterized. Various physicochemical parameters affecting the adsorption of BPA using magnetite were studied as well. The optimum time for the adsorption process was found to be 60 min at pH of 6, adsorbent dose of 0.2 g and 50 ppm of BPA. The adsorption data were fitted by the Langmuir adsorption isotherm best with a regression value of 0.957. The R L value was 0.179 which revealed that the process is favorable. The Freundlich constant n which was 1.901 also revealed that the adsorption is normal and favorable. The data were in agreement with the pseudo-second-order kinetics with regression value of 0.98. From the thermodynamic studies, the process was found to be exothermic and the Gibb's free energy value which was negative showed that the adsorption was spontaneous. The synthesized magnetite therefore offers great potential for the remediation of bisphenol A-contaminated media.

  4. Identification and paleoclimatic significance of magnetite nanoparticles in soils

    Science.gov (United States)

    Ahmed, Imad A. M.; Maher, Barbara A.

    2018-02-01

    In the world-famous sediments of the Chinese Loess Plateau, fossil soils alternate with windblown dust layers to record monsoonal variations over the last ˜3 My. The less-weathered, weakly magnetic dust layers reflect drier, colder glaciations. The fossil soils (paleosols) contain variable concentrations of nanoscale, strongly magnetic iron oxides, formed in situ during the wetter, warmer interglaciations. Mineralogical identification of the magnetic soil oxides is essential for deciphering these key paleoclimatic records. Formation of magnetite, a mixed Fe2+/Fe3+ ferrimagnet, has been linked to soil redox oscillations, and thence to paleorainfall. An opposite hypothesis states that magnetite can only form if the soil is water saturated for significant periods in order for Fe3+ to be reduced to Fe2+, and suggests instead the temperature-dependent formation of maghemite, an Fe3+-oxide, much of which ages subsequently into hematite, typically aluminum substituted. This latter, oxidizing pathway would have been temperature, but not rainfall dependent. Here, through structural fingerprinting and scanning transmission electron microscopy and electron energy loss spectroscopy analysis, we prove that magnetite is the dominant soil-formed ferrite. Maghemite is present in lower concentrations, and shows no evidence of aluminum substitution, negating its proposed precursor role for the aluminum-substituted hematite prevalent in the paleosols. Magnetite dominance demonstrates that magnetite formation occurs in well-drained, generally oxidizing soils, and that soil wetting/drying oscillations drive the degree of soil magnetic enhancement. The magnetic variations of the Chinese Loess Plateau paleosols thus record changes in monsoonal rainfall, over timescales of millions of years.

  5. Doping of magnetite nanoparticles facilitates clean harvesting of diatom oil as biofuel for sustainable energy

    Science.gov (United States)

    Kumar, Vikas; Singh, Ramesh; Thakur, Shipra; Ballabh Joshi, Khashti; Vinayak, Vandana

    2018-04-01

    Photosynthetic unicellular brown algae diatoms are considered as photobioreactors (PBRs) that synthesize and store oil in the form of lipid droplets and the much of the crude oil we use comes from fossil diatoms. The clean extraction of this crude oil from diatoms is difficult task. The construction of green chemical protocols for the clean separation of diatom oil from cells without killing or to harm the diatom cells is still in its primitive stage. In this report we would like to propose that facile doping of magnetite on diatoms can be used for clean oil separation in PBRs. We doped magnetite nanoparticles onto the surface of diatom Diadesmis confervaceae a diatom which oozes oil naturally. Doping magnetite onto diatoms can also facilitate easy separation of oil when cells are kept in an electromagnetic field. The cell wall of diatom besides having SiOH group has 281 amino acids of which 187–188 amino acids are conserved and are known for metal binding sites. The magnetite nanoparticles bind to the SiOH groups and metal binding sites of amino acids. The presence of appropriate amine functionalized linkers forming peptide aminosilane shells can further facilitate the binding of peptide/polypeptides which can be used in drug delivery. Besides this the magnetite doped diatoms have wide applications in removal of phosphates and chromium from waste water too.

  6. Survival of Verwey transition in gadolinium-doped ultrasmall magnetite nanoparticles.

    Science.gov (United States)

    Yeo, Sunmog; Choi, Hyunkyung; Kim, Chul Sung; Lee, Gyeong Tae; Seo, Jeong Hyun; Cha, Hyung Joon; Park, Jeong Chan

    2017-09-28

    We have demonstrated that the Verwey transition, which is highly sensitive to impurities, survives in anisotropic Gd-doped magnetite nanoparticles. Transmission electron microscopy analysis shows that the nanoparticles are uniformly distributed. X-ray photoelectron spectroscopy and EDS mapping analysis confirm Gd-doping on the nanoparticles. The Verwey transition of the Gd-doped magnetite nanoparticles is robust and the temperature dependence of the magnetic moment (zero field cooling and field cooling) shows the same behaviour as that of the Verwey transition in bulk magnetite, at a lower transition temperature (∼110 K). In addition, irregularly shaped nanoparticles do not show the Verwey transition whereas square-shaped nanoparticles show the transition. Mössbauer spectral analysis shows that the slope of the magnetic hyperfine field and the electric quadrupole splitting change at the same temperature, meaning that the Verwey transition occurs at ∼110 K. These results would provide new insights into understanding the Verwey transition in nano-sized materials.

  7. Magnetic Nanoparticles Coated with a Thermosensitive Polymer with Hyperthermia Properties

    Directory of Open Access Journals (Sweden)

    Felisa Reyes-Ortega

    2017-12-01

    Full Text Available Magnetic nanoparticles (MNPs have been widely used to increase the efficacy of chemotherapeutics, largely through passive accumulation provided by the enhanced permeability and retention effect. Their incorporation into biopolymer coatings enables the preparation of magnetic field-responsive, biocompatible nanoparticles that are well dispersed in aqueous media. Here we describe a synthetic route to prepare functionalized, stable magnetite nanoparticles (MNPs coated with a temperature-responsive polymer, by means of the hydrothermal method combined with an oil/water (o/w emulsion process. The effects of both pH and temperature on the electrophoretic mobility and surface charge of these MNPs are investigated. The magnetite/polymer composition of these systems is detected by Fourier Transform Infrared Spectroscopy (FTIR and quantified by thermogravimetric analysis. The therapeutic possibilities of the designed nanostructures as effective heating agents for magnetic hyperthermia are demonstrated, and specific absorption rates as high as 150 W/g, with 20 mT magnetic field and 205 kHz frequency, are obtained. This magnetic heating response could provide a promising nanoparticle system for combined diagnostics and cancer therapy.

  8. Formation of magnetite nanoparticles at low temperature: from superparamagnetic to stable single domain particles.

    Directory of Open Access Journals (Sweden)

    Jens Baumgartner

    Full Text Available The room temperature co-precipitation of ferrous and ferric iron under alkaline conditions typically yields superparamagnetic magnetite nanoparticles below a size of 20 nm. We show that at pH  =  9 this method can be tuned to grow larger particles with single stable domain magnetic (> 20-30 nm or even multi-domain behavior (> 80 nm. The crystal growth kinetics resembles surprisingly observations of magnetite crystal formation in magnetotactic bacteria. The physicochemical parameters required for mineralization in these organisms are unknown, therefore this study provides insight into which conditions could possibly prevail in the biomineralizing vesicle compartments (magnetosomes of these bacteria.

  9. Nano-magnetite coated with gold: alternative oncological therapy with magnetic hyperthermia; Nanomagnetita recubierta de oro: terapia oncologica alternativa con hipertermia magnetica

    Energy Technology Data Exchange (ETDEWEB)

    Cordova F, T.; Jimenez G, O.; Basurto I, G. [Universidad de Guanajuato, Campus Leon, Division de Ciencias e Ingenierias, Loma del Bosque 103, Lomas del Campestre, 37150 Leon, Guanajuato (Mexico); Martinez E, J. C., E-mail: theo@fisica.ugto.mx [IPN, Unidad Profesional Interdisciplinaria de Ingenieria Campus Guanajuato, Av. Mineral de Valenciana 200, Industrial Puerto Interior, 36275 Silao de la Victoria, Guanajuato (Mexico)

    2017-10-15

    Localized hyperthermia performed through the use of nanoparticles is one of the most promising procedures for the cancer treatment. In this work, the synthesis of magnetite nanoparticles (Fe{sub 2}O{sub 3}) was carried out using the thermal decomposition method. Subsequently, these nanoparticles were coated with gold and suspended in aqueous phase. As a result, nanoparticles capable of being heated by the application of an alternating magnetic field or through the use of infrared radiation were obtained. As an additional feature, these nanoparticles are biocompatible thanks to their golden coating. The synthesized nanoparticles can be functionalized by the conjugation of a molecule (aptamer, antibody, peptide, etc.) whose target is a cancer cell in order to adhere to it the nanoparticle-marker complex, to subsequently carry out a heating with the objective of induce cell death. In conclusion, the synthesized nanoparticles allow providing an alternative treatment for cancer through the use of localized hyperthermia, either using magnetic or infrared heating. (Author)

  10. Biosynthesis and the conjugation of magnetite nanoparticles with luteinizing hormone releasing hormone (LHRH)

    Energy Technology Data Exchange (ETDEWEB)

    Obayemi, J.D. [Department of Materials Science and Engineering, African University of Science and Technology (AUST) Abuja, Federal Capital Territory (Nigeria); Department of Materials Science and Engineering, Kwara State University, Malete, Kwara State (Nigeria); Dozie-Nwachukwu, S. [Department of Materials Science and Engineering, African University of Science and Technology (AUST) Abuja, Federal Capital Territory (Nigeria); Sheda Science and Technology Complex (SHESTCO) Abuja, Federal Capital Territory (Nigeria); Danyuo, Y. [Department of Materials Science and Engineering, African University of Science and Technology (AUST) Abuja, Federal Capital Territory (Nigeria); Department of Electronics and Electricals Engineering, Nigerian Turkish Nile University, Abuja (Nigeria); Odusanya, O.S. [Department of Materials Science and Engineering, African University of Science and Technology (AUST) Abuja, Federal Capital Territory (Nigeria); Sheda Science and Technology Complex (SHESTCO) Abuja, Federal Capital Territory (Nigeria); Anuku, N. [Department of Chemistry, Bronx Community College, New York, NY 10453 (United States); Princeton Institute of Science and Technology of Materials (PRISM), Princeton, NJ 08544 (United States); Malatesta, K. [Princeton Institute of Science and Technology of Materials (PRISM), Princeton, NJ 08544 (United States); Department of Mechanical and Aerospace Engineering, Princeton University, NJ 08544 (United States); Soboyejo, W.O., E-mail: soboyejo@princeton.edu [Department of Materials Science and Engineering, African University of Science and Technology (AUST) Abuja, Federal Capital Territory (Nigeria); Princeton Institute of Science and Technology of Materials (PRISM), Princeton, NJ 08544 (United States); Department of Mechanical and Aerospace Engineering, Princeton University, NJ 08544 (United States)

    2015-01-01

    This paper presents the results of an experimental study of the biosynthesis of magnetite nanoparticles (BMNPs) with particle sizes between 10 nm and 60 nm. The biocompatible magnetic nanoparticles are produced from Magnetospirillum magneticum (M.M.) bacteria that respond to magnetic fields. M.M. bacteria were cultured and used to synthesize magnetite nanoparticles. This was done in an enriched magnetic spirillum growth medium (EMSGM) at different pH levels. The nanoparticle concentrations were characterized with UV–Visible (UV–Vis) spectroscopy, while the particle shapes were elucidated via transmission electron microscopy (TEM). The structure of the particles was studied using X-ray diffraction (XRD), while the hydrodynamic radii, particle size distributions and polydispersity of the nanoparticles were characterized using dynamic light scattering (DLS). Carbodiimide reduction was also used to functionalize the BMNPs with a molecular recognition unit (luteinizing hormone releasing hormone, LHRH) that attaches specifically to receptors that are over-expressed on the surfaces of most breast cancer cell types. The resulting nanoparticles were examined using Fourier Transform Infrared (FTIR) spectroscopy and quantitative image analysis. The implications of the results are then discussed for the potential development of magnetic nanoparticles for the specific targeting and treatment of breast cancer. - Highlights: • Biosynthesis of MNPs with clinically relevant sizes between 10 and 60 nm. • New insights into the effects of pH and processing time on nanoparticle shapes and sizes. • Successful conjugation of biosynthesized magnetite nanoparticles to LHRH ligands. • Conjugated BMNPs that are monodispersed with potential biomedical relevance. • Magnetic properties of biosynthesized MNPs suggest potential for MRI enhancement.

  11. Biosynthesis and the conjugation of magnetite nanoparticles with luteinizing hormone releasing hormone (LHRH)

    International Nuclear Information System (INIS)

    Obayemi, J.D.; Dozie-Nwachukwu, S.; Danyuo, Y.; Odusanya, O.S.; Anuku, N.; Malatesta, K.; Soboyejo, W.O.

    2015-01-01

    This paper presents the results of an experimental study of the biosynthesis of magnetite nanoparticles (BMNPs) with particle sizes between 10 nm and 60 nm. The biocompatible magnetic nanoparticles are produced from Magnetospirillum magneticum (M.M.) bacteria that respond to magnetic fields. M.M. bacteria were cultured and used to synthesize magnetite nanoparticles. This was done in an enriched magnetic spirillum growth medium (EMSGM) at different pH levels. The nanoparticle concentrations were characterized with UV–Visible (UV–Vis) spectroscopy, while the particle shapes were elucidated via transmission electron microscopy (TEM). The structure of the particles was studied using X-ray diffraction (XRD), while the hydrodynamic radii, particle size distributions and polydispersity of the nanoparticles were characterized using dynamic light scattering (DLS). Carbodiimide reduction was also used to functionalize the BMNPs with a molecular recognition unit (luteinizing hormone releasing hormone, LHRH) that attaches specifically to receptors that are over-expressed on the surfaces of most breast cancer cell types. The resulting nanoparticles were examined using Fourier Transform Infrared (FTIR) spectroscopy and quantitative image analysis. The implications of the results are then discussed for the potential development of magnetic nanoparticles for the specific targeting and treatment of breast cancer. - Highlights: • Biosynthesis of MNPs with clinically relevant sizes between 10 and 60 nm. • New insights into the effects of pH and processing time on nanoparticle shapes and sizes. • Successful conjugation of biosynthesized magnetite nanoparticles to LHRH ligands. • Conjugated BMNPs that are monodispersed with potential biomedical relevance. • Magnetic properties of biosynthesized MNPs suggest potential for MRI enhancement

  12. Solvothermal synthesis of mesoporous magnetite nanoparticles for Cr(IV) ions uptake and microwave absorption

    KAUST Repository

    Shen, Peng; Zhang, Haitao; Zhang, Suojiang; Yuan, Pei; Yang, Yang; Zhang, Qiang; Zhang, Xixiang

    2016-01-01

    Abstract: Colloidal mesoporous magnetite nanoparticles with tunable porosity were realized by a simple and scalable solvothermal route with the aid of AOT as ligands. AOT was used to induce the anisotropic crystal growth of smaller nanocrystals and restrain their tight aggregation so as to form more mesoscale pores. Morphologies and microstructures investigation by SEM and TEM revealed that the bigger nanoparticles were composed of smaller nanocrystals with an average size of 18 nm. A possible formation mechanism was proposed for the mesoporous nanoparticles. Study of nitrogen adsorption–desorption isotherm revealed that the Brunauer–Emmett–Teller (BET) specific surface area of mesoporous nanoparticles is up to 209 m2/g, resulting from the slit-shaped pores created by the aggregation of polyhedral nanocrystals. Magnetic properties study indicated that the as-prepared nanoparticles are superparamagnetic at room temperature. Optimized mesoporous magnetite nanoparticles exhibit a maximum Cr(VI) ion sorption capacity of 12.9 mmol/g, and its absorption behavior followed a Freundlich model. Microwave absorption study indicated that porous nanoparticles own higher permeability values than that of solid nanoparticles, leading to a higher dielectric loss in the frequency range of 2–18 GHz. Graphical Abstract: [Figure not available: see fulltext.] © 2016, Springer Science+Business Media Dordrecht.

  13. Solvothermal synthesis of mesoporous magnetite nanoparticles for Cr(IV) ions uptake and microwave absorption

    Energy Technology Data Exchange (ETDEWEB)

    Shen, Peng; Zhang, Haitao, E-mail: htzhang@ipe.ac.cn; Zhang, Suojiang, E-mail: sjzhang@ipe.ac.cn; Yuan, Pei [Chinese Academy of Sciences, Beijing Key Laboratory of Ionic Liquids Clean Process Institute of Process Engineering, Key Laboratory of Green Process and Engineering, Institute of Process Engineering (China); Yang, Yang [China Building Materials Academy, State Key Laboratory of Green Building Materials (China); Zhang, Qiang; Zhang, Xixiang [King Abdullah University of Science and Technology, Physical Science and Engineering (Saudi Arabia)

    2016-05-15

    Colloidal mesoporous magnetite nanoparticles with tunable porosity were realized by a simple and scalable solvothermal route with the aid of AOT as ligands. AOT was used to induce the anisotropic crystal growth of smaller nanocrystals and restrain their tight aggregation so as to form more mesoscale pores. Morphologies and microstructures investigation by SEM and TEM revealed that the bigger nanoparticles were composed of smaller nanocrystals with an average size of 18 nm. A possible formation mechanism was proposed for the mesoporous nanoparticles. Study of nitrogen adsorption–desorption isotherm revealed that the Brunauer–Emmett–Teller (BET) specific surface area of mesoporous nanoparticles is up to 209 m{sup 2}/g, resulting from the slit-shaped pores created by the aggregation of polyhedral nanocrystals. Magnetic properties study indicated that the as-prepared nanoparticles are superparamagnetic at room temperature. Optimized mesoporous magnetite nanoparticles exhibit a maximum Cr(VI) ion sorption capacity of 12.9 mmol/g, and its absorption behavior followed a Freundlich model. Microwave absorption study indicated that porous nanoparticles own higher permeability values than that of solid nanoparticles, leading to a higher dielectric loss in the frequency range of 2–18 GHz.Graphical Abstract.

  14. Solvothermal synthesis of mesoporous magnetite nanoparticles for Cr(IV) ions uptake and microwave absorption

    KAUST Repository

    Shen, Peng

    2016-05-12

    Abstract: Colloidal mesoporous magnetite nanoparticles with tunable porosity were realized by a simple and scalable solvothermal route with the aid of AOT as ligands. AOT was used to induce the anisotropic crystal growth of smaller nanocrystals and restrain their tight aggregation so as to form more mesoscale pores. Morphologies and microstructures investigation by SEM and TEM revealed that the bigger nanoparticles were composed of smaller nanocrystals with an average size of 18 nm. A possible formation mechanism was proposed for the mesoporous nanoparticles. Study of nitrogen adsorption–desorption isotherm revealed that the Brunauer–Emmett–Teller (BET) specific surface area of mesoporous nanoparticles is up to 209 m2/g, resulting from the slit-shaped pores created by the aggregation of polyhedral nanocrystals. Magnetic properties study indicated that the as-prepared nanoparticles are superparamagnetic at room temperature. Optimized mesoporous magnetite nanoparticles exhibit a maximum Cr(VI) ion sorption capacity of 12.9 mmol/g, and its absorption behavior followed a Freundlich model. Microwave absorption study indicated that porous nanoparticles own higher permeability values than that of solid nanoparticles, leading to a higher dielectric loss in the frequency range of 2–18 GHz. Graphical Abstract: [Figure not available: see fulltext.] © 2016, Springer Science+Business Media Dordrecht.

  15. Synthesis and characterization of Fe3O4 nanoparticles coated with fucan polysaccharides

    International Nuclear Information System (INIS)

    Silva, V.A.J.; Andrade, P.L.; Silva, M.P.C.; Bustamante D, A.; De Los Santos Valladares, Luis; Albino Aguiar, J.

    2013-01-01

    In this work we report the preparation of fucan-coated magnetite (Fe 3 O 4 ) nanoparticles by the co-precipitation method. These nanoparticles were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, Mössbauer spectroscopy and magnetic measurements. The nanoparticles showed quasi-spherical morphology with mean sizes around 10 nm. XRD and FT-IR confirmed the functionalization of the Fe 3 O 4 nanoparticles with the fucan polysaccharide. Room temperature magnetization measurements and Mössbauer spectroscopy showed that the nanoparticles exhibited superparamagnetic behavior at 300 K and the magnetic properties of the Fe 3 O 4 are partly screened by the coating preventing aggregation. - Highlights: • Syntheses of fucan-coated Fe 3 O 4 nanoparticles were made by co-precipitation method. • The efficiency of polysaccharide coated was analyzed by XRD and FT-IR. • The magnetic nanoparticles mean size was 10–20 nm. • The fucan-coated magnetite nanoparticles showed superparamagnetic behavior

  16. Size and surface effects on the magnetism of magnetite and maghemite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Nikiforov, V. N., E-mail: pppnvn@yandex.ru [Moscow State University (Russian Federation); Ignatenko, A. N.; Irkhin, V. Yu. [Russian Academy of Sciences, Mikheev Institute of Metal Physics, Ural Branch (Russian Federation)

    2017-02-15

    The size effects of magnetite and maghemite nanoparticles on their magnetic properties (magnetic moment, Curie temperature, blocking temperature, etc.) have been investigated. Magnetic separation and centrifugation of an aqueous solution of nanoparticles were used for their separation into fractions; their sizes were measured by atomic force microscopy, dynamic light scattering, and electron microscopy. A change in the size leads to a change in the Curie temperature and magnetic moment per formula unit. Both native nanoparticles and those covered with a bioresorbable layer have been considered. The magnetic properties have been calculated by the Monte Carlo method for the classical Heisenberg model with various bulk and surface magnetic moments.

  17. Synthesis and characterization of magnetite nanoparticles having different cover layer and investigation of cover layer effect on the adsorption of lysozyme and bovine serum albumin.

    Science.gov (United States)

    Shah, Muhammad Tariq; Alveroglu, Esra

    2017-12-01

    In this study, differently coated superparamagnetic Fe 3 O 4 (magnetite) nanoparticles were synthesized, characterized and used for lysozyme (Ly) and bovine serum albumin (BSA) adsorption. SiO 2 , carbon nanotubes (CNTs) and graphene were used for covering the readily synthesized magnetite nanoparticles to elucidate the effect of cover layer on the protein adsorption kinetics and capacities of nanostructure. XRD, FTIR, AFM, SEM, VSM and fluorescence measurements were used for the characterization of the samples and investigating the adsorption kinetics of Ly and BSA by these nanoparticles. The average particle size of the Fe 3 O 4 nanoparticles are approximately found as 10nm and VSM measurement shows that the Fe 3 O 4 particles have superparamagnetic behavior with no hysteresis and remnant. The adsorption kinetic of proteins on nanosized material is followed via fluorescence method. All the nanostructures with different cover layers obey pseudo first order kinetics and SiO 2 coated nanoparticles show the fastest kinetics and capabilities for Ly and BSA adsorption. Copyright © 2017 Elsevier B.V. All rights reserved.

  18. Chitosan-Coated Magnetic Nanoparticles Prepared in One Step by Reverse Microemulsion Precipitation

    OpenAIRE

    Hened Saade; Salvador Fernández; Ramón Díaz de León; Gilberto Hurtado; María G. Pineda; Raúl G. López; Darío Bueno

    2013-01-01

    Chitosan-coated magnetic nanoparticles (CMNP) were obtained at 70 ?C and 80 ?C in a one-step method, which comprises precipitation in reverse microemulsion in the presence of low chitosan concentration in the aqueous phase. X-ray diffractometry showed that CMNP obtained at both temperatures contain a mixture of magnetite and maghemite nanoparticles with ?4.5 nm in average diameter, determined by electron microscopy, which suggests that precipitation temperature does not affect the particle si...

  19. The effect of magnetite nanoparticles synthesis conditions on their ability to separate heavy metal ions

    Directory of Open Access Journals (Sweden)

    Bobik Magdalena

    2017-06-01

    Full Text Available Magnetite nanoparticles have become a promising material for scientific research. Among numerous technologies of their synthesis, co-precipitation seems to be the most convenient, less time-consuming and cheap method which produces fine and pure iron oxide particles applicable to environmental issues. The aim of the work was to investigate how the co-precipitation synthesis parameters, such as temperature and base volume, influence the magnetite nanoparticles ability to separate heavy metal ions. The synthesis were conducted at nine combinations of different ammonia volumes - 8 cm3, 10 cm3, 15 cm3 and temperatures - 30°C, 60°C, 90°C for each ammonia volume. Iron oxides synthesized at each combination were examined as an adsorbent of seven heavy metals: Cr(VI, Pb(II, Cr(III, Cu(II, Zn(II, Ni(II and Cd(II. The representative sample of magnetite was characterized using XRD, SEM and BET methods. It was observed that more effective sorbent for majority of ions was produced at 30°C using 10 cm3 of ammonia. The characterization of the sample produced at these reaction conditions indicate that pure magnetite with an average crystallite size of 23.2 nm was obtained (XRD, the nanosized crystallites in the sample were agglomerated (SEM and the specific surface area of the aggregates was estimated to be 55.64 m2·g-1 (BET. The general conclusion of the work is the evidence that magnetite nanoparticles have the ability to adsorb heavy metal ions from the aqueous solutions. The effectiveness of the process depends on many factors such as kind of heavy metal ion or the synthesis parameters of the sorbent.

  20. Novel hybrid coatings with controlled wettability by composite nanoparticle aggregation

    Energy Technology Data Exchange (ETDEWEB)

    Hritcu, Doina, E-mail: dhritcu@ch.tuiasi.ro; Dodi, Gianina; Iordache, Mirabela L.; Draganescu, Dan; Sava, Elena; Popa, Marcel I.

    2016-11-30

    Highlights: • Magnetite-grafted chitosan composite nanoparticles were synthesized. • The particles are able to assemble under the influence of a silane derivative. • Thin films containing composites, chitosan and hydrolyzed silane were optimized. • The novel hybrid coatings show hierarchical roughness and high wetting angle. - Abstract: The aim of this study is to evaluate novel hybrid materials as potential candidates for producing coatings with hierarchical roughness and controlled wetting behaviour. Magnetite (Fe{sub 3}O{sub 4}) nanoparticles obtained by co-precipitation were embedded in matrices synthesized by radical graft co-polymerization of butyl acrylate (BA), butyl methacrylate (BMA), hexyl acrylate (HA) or styrene (ST) with ethylene glycol di-methacrylate (EGDMA) onto previously modified chitosan bearing surface vinyl groups. The resulting composite particles were characterized regarding their average size, composition and magnetic properties. Hybrid thin films containing suspension of composite particles in ethanol and pre-hydrolysed hexadecyltrimethoxysilane (HDTS) as a coupling/crosslinking agent were deposited by spin coating or spraying. The films were cured by heating and subsequently characterized regarding their morphology (scanning electron microscopy), contact angle with water and adhesion to substrate (scratch test). The structure-property relationship is discussed.

  1. Targeting to carcinoma cells with chitosan- and starch-coated magnetic nanoparticles for magnetic hyperthermia.

    Science.gov (United States)

    Kim, Dong-Hyun; Kim, Kyoung-Nam; Kim, Kwang-Mahn; Lee, Yong-Keun

    2009-01-01

    The delivery of hyperthermic thermoseeds to a specific target site with minimal side effects is an important challenge in targeted hyperthermia, which employs magnetic method and functional polymers. An external magnetic field is used to control the site-specific targeting of the magnetic nanoparticles. Polymer-coated magnetic nanoparticles can confer a higher affinity to the biological cell membranes. In this study, uncoated, chitosan-coated, and starch-coated magnetic nanoparticles were synthesized for use as a hyperthermic thermoseed. Each sample was examined with respect to their applications to hyperthermia using XRD, VSM, and FTIR. In addition, the temperature changes under an alternating magnetic field were observed. As in vitro tests, the magnetic responsiveness of chitosan- and starch-coated magnetite was determined by a simple blood vessel model under various intensities of magnetic field. L929 normal cells and KB carcinoma cells were used to examine the cytotoxicity and affinity of each sample using the MTT method. The chitosan-coated magnetic nanoparticles generated a higher DeltaT of 23 degrees C under an AC magnetic field than the starch-coated magnetite, and the capturing rate of the particles was 96% under an external magnetic field of 0.4 T. The highest viability of L929 cells was 93.7%. Comparing the rate of KB cells capture with the rate of L929 cells capture, the rate of KB cells capture relatively increased with 10.8% in chitosan-coated magnetic nanoparticles. Hence, chitosan-coated magnetic nanoparticles are biocompatible and have a selective affinity to KB cells. The targeting of magnetic nanoparticles in hyperthermia was improved using a controlled magnetic field and a chitosan-coating. Therefore, chitosan-coated magnetic nanoparticles are expected to be promising materials for use in magnetic targeted hyperthermia. 2008 Wiley Periodicals, Inc.

  2. Preparation of size-controlled (30-100 nm) magnetite nanoparticles for biomedical applications

    International Nuclear Information System (INIS)

    Nishio, K.; Ikeda, M.; Gokon, N.; Tsubouchi, S.; Narimatsu, H.; Mochizuki, Y.; Sakamoto, S.; Sandhu, A.; Abe, M.; Handa, H.

    2007-01-01

    Size-controlled magnetite nanoparticles (MNPs) with several dozen nanometers (nm) were synthesized for biomedical applications. Nanoparticles of single-phase magnetite, as revealed by X-ray analyses and magnetic measurements, were prepared by oxidizing ferrous hydroxide (Fe(OH) 2 ) with a weak oxidant NaNO 3 in an N 2 -deaerated aqueous NaOH solution (pH=12-13) at various temperatures below 37 deg. C. As the synthesis temperature increases from 4 to 37 deg. C, the MNPs are decreased in size (d) from 102±5.6 to 31.7±4.9 nm and widened in size distribution, Δd/d increases from 5.5% to 15%. Prepared without using any surfactant, the MNPs are advantageous for immobilizing functional molecules stably on the surfaces for biomedical applications

  3. Relaxometry and Dephasing Imaging of Superparamagnetic Magnetite Nanoparticles Using a Single Qubit

    Science.gov (United States)

    Schmid-Lorch, Dominik; Häberle, Thomas; Reinhard, Friedemann; Zappe, Andrea; Slota, Michael; Bogani, Lapo; Finkler, Amit; Wrachtrup, Jörg

    2015-08-01

    To study the magnetic dynamics of superparamagnetic nanoparticles we use scanning probe relaxometry and dephasing of the nitrogen-vacancy (NV) center in diamond, characterizing the spin-noise of a single 10-nm magnetite particle. Additionally, we show the anisotropy of the NV sensitivity's dependence on the applied decoherence measurement method. By comparing the change in relaxation (T 1 ) and dephasing (T 2 ) time in the NV center when scanning a nanoparticle over it, we are able to extract the nanoparticle's diameter and distance from the NV center using an Ornstein-Uhlenbeck model for the nanoparticle's fluctuations. This scanning-probe technique can be used in the future to characterize different spin label substitutes for both medical applications and basic magnetic nanoparticle behavior.

  4. SYNTHESIS OF MAGNETITE NANOPARTICLES AND EVALUATION OF ITS EFFICIENCY FOR ARSENIC REMOVAL FROM SIMULATED INDUSTRIAL WASTEWATER

    Directory of Open Access Journals (Sweden)

    A. Khodabakhshi

    2011-09-01

    Full Text Available In this study the efficiency of magnetic nanoparticles for removal of trivalent arsenic from synthetic industrial wastewater was evaluated. The nanoparticles was prepared by sol-gel method and characterized by X-ray methods including XRD, XRF, and SEM, and vibrating sample magnetometer (VSM. The results showed that synthesized nanoparticles were in the size range of 40-300 nm, purity of about 90%, and magnetization of nanoparticles was 36.5emu/g. In initial conditions including: pH=7, As(III concentration of 10 mg/L, nanomagnetite concentration of 1g/L, shaking speed of 250 rpm and 20 minute retention time, 82% of As (III was removed. Competition from common coexisting ions such as Na+, Ni2+, Cu2+, SO42-, and Cl- was ignorable but for NO3- was significant. The adsorption data of magnetite nanoparticles fit well with Freundlich isotherm equations. The adsorption capacity of the Fe3O4 for As (III at pH=7 was obtained as 23.8 mg/g. It was concluded that magnetite nanoparticles have considerable potential in removal of As(III from synthetic industrial wastewaters.

  5. Synthesis of highly stable folic acid conjugated magnetite nanoparticles for targeting cancer cells

    International Nuclear Information System (INIS)

    Mohapatra, S; Mallick, S K; Maiti, T K; Ghosh, S K; Pramanik, P

    2007-01-01

    A new approach towards the design of folic acid conjugated magnetic nanoparticles for enhancing their site specific intracellular uptake against a folate receptor overexpressing cancer cells is reported. Magnetite nanoparticles were prepared by coprecipitation from an Fe 3+ and Fe 2+ solution followed by surface modification with 2-carboxyethyl phosphonic acid to form carboxyl group terminated nanoparticles. Then folic acid and fluorescein isothiocyanate (FITC) were conjugated with carboxylic acid functionalized magnetite nanoparticles using 2,2'-(ethylenedioxy)-bis-ethylamine. These folate-conjugated nanoparticles were characterized in terms of their size by dynamic light scattering (DLS) and transmission electron microscopy (TEM). Surface functional groups and surface composition were analyzed by Fourier transform infrared (FTIR) spectroscopy and x-ray photoelectron spectroscopy (XPS), respectively. Vibration sample magnetometry (VSM) measurements showed the superparamagnetic nature of the particles at room temperature. Folate-conjugated magnetic nanoparticles are noncytotoxic and receptor mediated internalization by HeLa and B16 melanoma F0 cancer cells was confirmed by flow cytometry and confocal microscopy

  6. Kinetic and Thermodynamic Effects on the Agglomeration of Magnetite Nanoparticles by Magnetic Field

    International Nuclear Information System (INIS)

    Jin, Daeseong; Kim, Hackjin

    2016-01-01

    The dynamics of agglomeration of magnetite nanoparticles studied by measuring the magnetic weight shows the kinetics of stretched exponential. During the growth of the magnetic weight, the structure of agglomerate fluctuates by temperature change. This fast relaxation that can be interpreted in terms of Boltzmann distribution indicates that the thermal equilibration is established promptly with the temperature change. Agglomerate of nanoparticles resembles protein in that both of them exist in complex structures of various conformations with different formation energies, which requires the energy landscape for understanding of dynamics in detail

  7. The role of polymer films on the oxidation of magnetite nanoparticles

    Science.gov (United States)

    Letti, C. J.; Paterno, L. G.; Pereira-da-Silva, M. A.; Morais, P. C.; Soler, M. A. G.

    2017-02-01

    A detailed investigation about the role of polymer films on the oxidation process of magnetite nanoparticles (∼7 nm diameter), under laser irradiation is performed employing micro Raman spectroscopy. To support this investigation, Fe3O4-np are synthesized by the co-precipitation method and assembled layer-by-layer with sodium sulfonated polystyrene (PSS). Polymer films (Fe3O4-np/PSS)n with n=2,3,5,7,10 and 25 bilayers are employed as a model system to study the oxidation process under laser irradiation. Raman data are further processed by principal component analysis. Our findings suggest that PSS protects Fe3O4-np from oxidation when compared to powder samples, even for the sample with the greater number of bilayers. Further, the oxidation of magnetite to maghemite occurs preferably for thinner films up to 7 bilayers, while the onset for the formation of the hematite phase depends on the laser intensity for thicker films. Water takes part on the oxidation processes of magnetite, the oxidation/phase transformation of Fe3O4-np is intensified in films with more bilayers, since more water is included in those films. Encapsulation of Fe3O4-np by PSS in layer-by-layer films showed to be very efficient to avoid the oxidation process in nanosized magnetite.

  8. Synthesis and characterization of cationic lipid coated magnetic nanoparticles using multiple emulsions as microreactors

    Science.gov (United States)

    Akbaba, Hasan; Karagöz, Uğur; Selamet, Yusuf; Kantarcı, A. Gülten

    2017-03-01

    The aim of this study was to develop a novel iron oxide nanoparticle synthesis method with in-situ surface coating. For this purpose multiple emulsions were used as microreactors for the first time and magnetic iron oxide particles synthesized in the core of cationic solid lipid nanoparticles. DLS, SEM, TEM, VSM, Raman Spectrometer, XRD, and XPS techniques were performed for characterization of the magnetic nanoparticles. Obtained magnetic nanoparticles are superparamagnetic and no additional process was needed for surface adjustments. They are positively charged as a result of cationic lipid coating and has appropriate particle size (<30 nm) for drug or nucleic acid delivery. Structure analysis showed that magnetic core material is in the form of magnetite. Saturation magnetization value was measured as 15-17 emu g-1 for lipid coated magnetic nanoparticles obtained by multiple emulsion method which is reasonably sufficient for magnetic targeting.

  9. Transport Modeling of Modified Magnetite Nanoparticles with Sodium Dodecyl Sulfate in a Saturated Sandy Soil

    Directory of Open Access Journals (Sweden)

    Ahmad Farrokhian Firouzi

    2017-02-01

    Full Text Available Introduction: Nanoparticles due to their large specific area and reactivity recently have been used in several environmental remediation applications such as degradation of organic compounds and pesticides and adsorption of heavy metals and inorganic anions. Because of concern over potential threats of nanoparticle releases into the soil–water environment, a number of studies have been carried out to investigate the transport, retention and deposition of nanoparticles in saturated porous media. Many of these studies are based on measurements of transport in columns packed with idealized porous media consisting of spherical glass beads or sand. The nanoparticles are usually introduced into the column and breakthrough curve concentrations are measured at the column outlet. To examine the effect of various parameters on the transport of nanoparticles in porous medium, for convenience, all the parameters considered the same in the experiments, and only one parameter in the experiments is changed and investigated. Materials and Methods: The objective of this research is quantitative study of modified magnetite nanoparticles transport in saturated sand-repacked columns. The modified magnetite nanoparticles with Sodium dodecyl sulfate were synthesized following the protocol described by Si et al. (2004. The experimental setup included a suspension reservoir, Teflon tubing, a HPLC pump, and a glass column (2.5 cm i.d. and 20 cm height. Therefore, breakthrough curves of modified magnetite nanoparticles with Sodium dodecyl sulfate and chloride were determined under saturated conditions and influence of nanoparticles concentration (0.1 and 0.5 g.L-1 and pore velocity (pressure head of 2 and 10 cm on nanoparticles transport were investigated. For each medium bed, the background solution were first pumped through the column in the up-flow mode to obtain a steady flow state. Then, a tracer test was conducted by introducing CaCl2 solution into the column

  10. The cellular magnetic response and biocompatibility of biogenic zinc- and cobalt-doped magnetite nanoparticles

    Science.gov (United States)

    Moise, Sandhya; Céspedes, Eva; Soukup, Dalibor; Byrne, James M.; El Haj, Alicia J.; Telling, Neil D.

    2017-01-01

    The magnetic moment and anisotropy of magnetite nanoparticles can be optimised by doping with transition metal cations, enabling their properties to be tuned for different biomedical applications. In this study, we assessed the suitability of bacterially synthesized zinc- and cobalt-doped magnetite nanoparticles for biomedical applications. To do this we measured cellular viability and activity in primary human bone marrow-derived mesenchymal stem cells and human osteosarcoma-derived cells. Using AC susceptibility we studied doping induced changes in the magnetic response of the nanoparticles both as stable aqueous suspensions and when associated with cells. Our findings show that the magnetic response of the particles was altered after cellular interaction with a reduction in their mobility. In particular, the strongest AC susceptibility signal measured in vitro was from cells containing high-moment zinc-doped particles, whilst no signal was observed in cells containing the high-anisotropy cobalt-doped particles. For both particle types we found that the moderate dopant levels required for optimum magnetic properties did not alter their cytotoxicity or affect osteogenic differentiation of the stem cells. Thus, despite the known cytotoxicity of cobalt and zinc ions, these results suggest that iron oxide nanoparticles can be doped to sufficiently tailor their magnetic properties without compromising cellular biocompatibility.

  11. Room Temperature Co-Precipitation Synthesis of Magnetite Nanoparticles in a Large pH Window with Different Bases.

    Science.gov (United States)

    Mascolo, Maria Cristina; Pei, Yongbing; Ring, Terry A

    2013-11-28

    Magnetite nanoparticles (Fe₃O₄) represent the most promising materials in medical applications. To favor high-drug or enzyme loading on the nanoparticles, they are incorporated into mesoporous materials to form a hybrid support with the consequent reduction of magnetization saturation. The direct synthesis of mesoporous structures appears to be of interest. To this end, magnetite nanoparticles have been synthesized using a one pot co-precipitation reaction at room temperature in the presence of different bases, such as NaOH, KOH or (C₂H₅)₄NOH. Magnetite shows characteristics of superparamagnetism at room temperature and a saturation magnetization (Ms) value depending on both the crystal size and the degree of agglomeration of individual nanoparticles. Such agglomeration appears to be responsible for the formation of mesoporous structures, which are affected by the pH, the nature of alkali, the slow or fast addition of alkaline solution and the drying modality of synthesized powders.

  12. Room Temperature Co-Precipitation Synthesis of Magnetite Nanoparticles in a Large pH Window with Different Bases

    Directory of Open Access Journals (Sweden)

    Maria Cristina Mascolo

    2013-11-01

    Full Text Available Magnetite nanoparticles (Fe3O4 represent the most promising materials in medical applications. To favor high-drug or enzyme loading on the nanoparticles, they are incorporated into mesoporous materials to form a hybrid support with the consequent reduction of magnetization saturation. The direct synthesis of mesoporous structures appears to be of interest. To this end, magnetite nanoparticles have been synthesized using a one pot co-precipitation reaction at room temperature in the presence of different bases, such as NaOH, KOH or (C2H54NOH. Magnetite shows characteristics of superparamagnetism at room temperature and a saturation magnetization (Ms value depending on both the crystal size and the degree of agglomeration of individual nanoparticles. Such agglomeration appears to be responsible for the formation of mesoporous structures, which are affected by the pH, the nature of alkali, the slow or fast addition of alkaline solution and the drying modality of synthesized powders.

  13. High pressure in-situ X-ray diffraction study on Zn-doped magnetite nanoparticles

    Science.gov (United States)

    Ferrari, S.; Bilovol, V.; Pampillo, L. G.; Grinblat, F.; Errandonea, D.

    2018-03-01

    We have performed high pressure synchrotron X-ray powder diffraction experiments on two different samples of Zn-doped magnetite nanoparticles (formula Fe(3-x)ZnxO4; x = 0.2, 0.5). The structural behavior of then a noparticles was studied up to 13.5 GPa for x = 0.2, and up to 17.4 GPa for x = 0.5. We have found that both systems remain in the cubic spinel structure as expected for this range of applied pressures. The analysis of the unit cell volume vs. pressure results in bulk modulus values lower than in both end-members, magnetite (Fe3O4) and zinc ferrite (ZnFe2O4), suggesting that chemical disorder may favor compressibility, which is expected to improve the increase of the Neel temperature under compression.

  14. Adsorption behavior of magnetite nanoparticles into the DPPC model membranes

    International Nuclear Information System (INIS)

    Hao, Changchun; Li, Junhua; Mu, Wenning; Zhu, Lingqing; Yang, Jiaxiang; Liu, Hongwei; Li, Bin; Chen, Shi; Sun, Runguang

    2016-01-01

    Graphical abstract: A represents the state when DPPC was spread on air/water interface at 5 mN/m surface pressures. DPPC is in the liquid expanded state at the interface. B represents 15 mN/m surface pressures and DPPC monolayer is in the liquid condensed state at the interface. - Highlights: • The adsorption of Fe 3 O 4 nanoparticles on DPPC monolayer has been investigated. • The lifting area/molecule of DPPC monolayers increased with Fe 3 O 4 increasing. • The π–t curves were well fitted by single exponential association equation. • AFM images depended on surface pressure and concentration in subphase. - Abstract: In this report, we have studied the adsorption behavior of Fe 3 O 4 nanoparticles into dipalmitoylphosphatidylcholine (DPPC) monolayer. Adsorption kinetics (π–t) process as well as the surface pressure (π–A) isotherms were monitored by Langmuir Wilhelmy plate. The measurement data indicated the Fe 3 O 4 nanoparticles incorporated into the monolayer at the air–water interface. The lifting area/molecule isotherms of DPPC monolayers increased with the increasing concentration of Fe 3 O 4 in the subphase, however, the values of elasticity reduced. The curves of π–t were well fitted by single exponential association equation. Observation by atomic force microscopy (AFM) on monolayers extracted at 5 mN/m and 15 mN/m suggested that the different interaction of Fe 3 O 4 with DPPC monolayer depended on surface pressure of monolayers and concentration in the subphase. The results of observations were in agreement with the fitted results.

  15. Synthesis and Evaluation of Poly(Sodium 2-Acrylamido-2-Methylpropane Sulfonate-co-Styrene/Magnetite Nanoparticle Composites as Corrosion Inhibitors for Steel

    Directory of Open Access Journals (Sweden)

    Gamal A. El-Mahdy

    2014-01-01

    Full Text Available Self-stabilized magnetic polymeric composite nanoparticles of coated poly-(sodium 2-acrylamido-2-methylpropane sulfonate-co-styrene/magnetite (PAMPS-Na-co-St/Fe3O4 were prepared by emulsifier-free miniemulsion polymerization using styrene (St as a monomer, 2-acrylamido-2-methylpropane sulfonic acid sodium salt (AMPS-Na as an ionic comonomer, N,N-methylenebisacrylamide (MBA as crosslinker, hexadecane (HD as a hydrophobic solvent, and 2,2-azodiisobutyronitrile (AIBN as an initiator in the presence of hydrophobic oleic acid coated magnetite particles. Hydrophobic oleic acid coated magnetite particles with an average size of about 7-10 nm were prepared with the new modified water-based magnetite ferrofluid, synthesized by a chemical modified coprecipitation method. The morphology and the particle size distributions of the crosslinked PAMPS-Na-co-St/Fe3O4 composite were observed and analyzed by transmission electron microscopy (TEM. The average Fe3O4 content of PAMPS-Na-co-St/Fe3O4 was determined by thermogravimetric analysis (TGA. The inhibitory action of PAMPS-Na-co-St/Fe3O4 towards steel corrosion in 1 M HCl solutions has been investigated by polarization and electrochemical impedance spectroscopy (EIS methods. Polarization measurements indicate that PAMPS-Na-co-St/Fe3O4 acts as a mixed type-inhibitor and the inhibition efficiency increases with inhibitor concentration. The results of potentiodynamic polarization and EIS measurements clearly showed that the inhibition mechanism involves blocking of the steel surface by inhibitor molecules via adsorption.

  16. Growth and characterization of magnetite-maghemite thin films by the dip coating method

    Energy Technology Data Exchange (ETDEWEB)

    Velásquez, A. A., E-mail: avelas26@eafit.edu.edu.co; Arnedo, A. [Universidad EAFIT, Grupo de Electromagnetismo Aplicado (Colombia)

    2017-11-15

    We present the process of growth and characterization of magnetite-maghemite thin films obtained by the dip coating method. The thin films were deposited on glass substrates, using a ferrofluid of nanostructured magnetite-maghemite particles as precursor solution. During the growth of the films the following parameters were controlled: number of dips of the substrates, dip velocity of the substrates and drying times. The films were characterized by Atomic Force Microscopy, Scanning Elelectron Microscopy, four-point method for resistance measurement, Room Temperature Mössbauer Spectroscopy and Hall effect. Mössbauer measurements showed the presence of a sextet attributed to maghemite (γ-Fe{sub 2}O{sub 3}) and two doublets attributed to superparamagnetic magnetite (Fe{sub 3}O{sub 4}), indicating a distribution of oxidation states of the iron as well as a particle size distribution of the magnetic phases in the films. Atomic force microscopy measurements showed that the films cover quasi uniformly the substrates, existing in them some pores with sub-micron size. Scanning Electron Microscopy measurements showed a uniform structure in the films, with spherical particles with size around 10 nm. Voltage versus current measurements showed an ohmic response of the films for currents between 0 and 100 nA. On the other hand, Hall effect measurements showed a nonlinear response of the Hall voltage with the magnetic flux density applied perpendicular to the plane of the films, however the response is fairly linear for magnetic flux densities between 0.15 and 0.35 T approximately. The results suggest that the films are promising for application as magnetic flux density sensors.

  17. Growth and characterization of magnetite-maghemite thin films by the dip coating method

    International Nuclear Information System (INIS)

    Velásquez, A. A.; Arnedo, A.

    2017-01-01

    We present the process of growth and characterization of magnetite-maghemite thin films obtained by the dip coating method. The thin films were deposited on glass substrates, using a ferrofluid of nanostructured magnetite-maghemite particles as precursor solution. During the growth of the films the following parameters were controlled: number of dips of the substrates, dip velocity of the substrates and drying times. The films were characterized by Atomic Force Microscopy, Scanning Elelectron Microscopy, four-point method for resistance measurement, Room Temperature Mössbauer Spectroscopy and Hall effect. Mössbauer measurements showed the presence of a sextet attributed to maghemite (γ-Fe_2O_3) and two doublets attributed to superparamagnetic magnetite (Fe_3O_4), indicating a distribution of oxidation states of the iron as well as a particle size distribution of the magnetic phases in the films. Atomic force microscopy measurements showed that the films cover quasi uniformly the substrates, existing in them some pores with sub-micron size. Scanning Electron Microscopy measurements showed a uniform structure in the films, with spherical particles with size around 10 nm. Voltage versus current measurements showed an ohmic response of the films for currents between 0 and 100 nA. On the other hand, Hall effect measurements showed a nonlinear response of the Hall voltage with the magnetic flux density applied perpendicular to the plane of the films, however the response is fairly linear for magnetic flux densities between 0.15 and 0.35 T approximately. The results suggest that the films are promising for application as magnetic flux density sensors.

  18. Sedimentation and aggregation of magnetite nanoparticles in water by a gradient magnetic field

    International Nuclear Information System (INIS)

    Medvedeva, I.; Bakhteeva, Yu.; Zhakov, S.; Revvo, A.; Byzov, I.; Uimin, M.; Yermakov, A.; Mysik, A.

    2013-01-01

    Magnetite (γ-Fe 3 O 4 ) nanoparticles are promising effective sorbents for water cleaning of heavy metal, radionuclides, organic and biological materials. A good sorption capacity can be achieved due to their high specific surface area. Application of gradient magnetic fields helps to separate the magnetic nanoparticles from the water suspension, which is rather hard to do using the conventional mechanical filtration and sedimentation methods without coagulants. The sedimentation dynamics of magnetite nanoparticles with sizes of 10–20 nm in aqueous media in the presence of a gradient magnetic field was studied by optical and NMR relaxometry methods. The gradient magnetic field was produced by a series of strip permanent magnets with B ≤ 0.5 T, dB/dz ≤ 0.13 T/cm and in some cases enhanced by a steel grid with sharp edges (dB/dz ≤ 5 T/cm). Dynamic Light Scattering in the water suspension with different nanoparticle concentrations (c 0  = 0.1–1 g/l) revealed the characteristic features in the aggregate formation, which is reflected in the sedimentation behavior. The sedimentation rate of the nanoparticles in water and in magnetic fields is higher for less concentrated suspensions (c 0  = 0.1 g/l) than for more concentrated ones (c 0  = 1 g/l), which might be connected with the formation of a gel structures due to a strong magnetic attraction between ferromagnetic nanoparticles. In 180 min this resulted in the reduction of the iron concentration in water down to 0.4 mg/l, which is close to hygienic and environmental norms for drinking water and fishery

  19. Room temperature synthesis of magnetite (Fe.sub.3−δ./sub.O.sub.4./sub.) nanoparticles by a simple reverse co-precipitation method

    Czech Academy of Sciences Publication Activity Database

    Mahmed, N.; Heczko, Oleg; Söderberg, O.; Hannula, S.-P.

    2011-01-01

    Roč. 18, č. 3 (2011), 032020/1-032020/4 ISSN 1757-8981 Institutional research plan: CEZ:AV0Z10100520 Keywords : ferromagnetic nanoparticles * magnetite nanoparticles synthesis * maghemi Subject RIV: BM - Solid Matter Physics ; Magnetism

  20. Effect of pH on the Structural and Magnetic Properties of Magnetite Nanoparticles Synthesised by Co-Precipitation

    International Nuclear Information System (INIS)

    Ramadan, W.; Kareem, M.; Hannoyer, B.; Saha, Sh.

    2011-01-01

    Magnetite, Fe3O4, nanoparticles were synthesized using co-precipitation aqueous method at room temperature and at different pH, from 8 to 12.5. The pH value was found to influence greatly the resulting phases and has no significant effect on the particle size. In all cases, magnetite was found to be the main phase but the contribution of Goethite phase was identified clearly with the increase in pH. Significant reduction in saturation magnetization was evident. Structural and magnetic properties of the nanoparticles were examined using; XRD, TEM, Raman Spectroscopy and SQUID. (author)

  1. Synthesis and characterization of Fe{sub 3}O{sub 4} nanoparticles coated with fucan polysaccharides

    Energy Technology Data Exchange (ETDEWEB)

    Silva, V.A.J.; Andrade, P.L. [Programa de Pós-Graduação em Ciências de Materiais, Centro de Ciências Exatas e da Natureza, Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil); Laboratório de Imunopatologia Keizo Asami (LIKA), Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil); Silva, M.P.C. [Laboratório de Imunopatologia Keizo Asami (LIKA), Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil); Departamento de Bioquímica, Universidade Federal de Pernambuco, 50670-420 Recife-PE (Brazil); Bustamante D, A. [Laboratorio de Cerámicos y Nanomateriales, Facultad de Ciencias Físicas, Universidad Nacional Mayor de San Marcos, Ap. Postal 14-0149 Lima (Peru); De Los Santos Valladares, Luis [Laboratório de Imunopatologia Keizo Asami (LIKA), Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil); Cavendish Laboratory, University of Cambridge, J.J. Thomson Avenue, Cambridge CB3 0HE (United Kingdom); Albino Aguiar, J., E-mail: albino@df.ufpe.br [Programa de Pós-Graduação em Ciências de Materiais, Centro de Ciências Exatas e da Natureza, Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil); Departamento de Física, Universidade Federal de Pernambuco, 50670-901 Recife-PE (Brazil)

    2013-10-15

    In this work we report the preparation of fucan-coated magnetite (Fe{sub 3}O{sub 4}) nanoparticles by the co-precipitation method. These nanoparticles were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction (XRD), Fourier transform infrared (FT-IR) spectroscopy, Mössbauer spectroscopy and magnetic measurements. The nanoparticles showed quasi-spherical morphology with mean sizes around 10 nm. XRD and FT-IR confirmed the functionalization of the Fe{sub 3}O{sub 4} nanoparticles with the fucan polysaccharide. Room temperature magnetization measurements and Mössbauer spectroscopy showed that the nanoparticles exhibited superparamagnetic behavior at 300 K and the magnetic properties of the Fe{sub 3}O{sub 4} are partly screened by the coating preventing aggregation. - Highlights: • Syntheses of fucan-coated Fe{sub 3}O{sub 4} nanoparticles were made by co-precipitation method. • The efficiency of polysaccharide coated was analyzed by XRD and FT-IR. • The magnetic nanoparticles mean size was 10–20 nm. • The fucan-coated magnetite nanoparticles showed superparamagnetic behavior.

  2. Effect of cerium substitution on structural and magnetic properties of magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Padalia, Diwakar, E-mail: Padalia.diwakar@gmail.com [Department of Physics, G.B.Pant University of Agriculture & Technology, Pantnagar, Uttrakhand (India); Johri, U.C. [Department of Physics, G.B.Pant University of Agriculture & Technology, Pantnagar, Uttrakhand (India); Zaidi, M.G.H. [Supercritical Fluid Processing Laboratory, Department of Chemistry, G.B.Pant University of Agriculture & Technology, Pantnagar, Uttrakhand (India)

    2016-02-01

    The current work presents the synthesis and properties of cerium doped magnetite (Fe{sub 3}O{sub 4}) nanoparticles synthesized by standard chemical co-precipitation method using NH{sub 4}OH as co-precipitating agent. The effects of cerium ion substitution on structural and magnetic properties of magnetite (Fe{sub 3}O{sub 4}) nanoparticles were reported. These materials were characterized by X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and vibrating sample magnetometer (VSM). The cerium content has a significant influence on structural and magnetic properties. The X-ray diffraction study confirmed the formation of single-phase magnetite with space group Fd3m and crystallite size ranging from 39 to 58 nm. The addition of cerium resulted in a reduction of crystallite size and an increase of cell parameters. FTIR measurements confirmed the formation of different samples and suggested that the reduction of Fe{sup +3} to Fe{sup +2} preferred on a site adjacent to Ce{sup +4}. Magnetic measurements revealed that the saturation magnetization (Ms) and remanence (M{sub r}) decreased while the coercivity (H{sub C}) and squareness (M{sub r}/M{sub S}) increased with increasing cerium content. - Highlights: • There is an increase in cell parameters and strain with Ce-content. • Samples show the presence of secondary phase after 1.0% doping level. • Ce-ions prefer octahedral sites and charge neutrality is accompanied by Fe{sup +3} → Fe{sup +2}. • Magnetization decreases due to weakening of the super exchange interactions. • Squareness and coercivity start to increase with Ce content.

  3. Magnetite Core-Shell Nanoparticles in Nondestructive Flaw Detection of Polymeric Materials.

    Science.gov (United States)

    Hetti, Mimi; Wei, Qiang; Pohl, Rainer; Casperson, Ralf; Bartusch, Matthias; Neu, Volker; Pospiech, Doris; Voit, Brigitte

    2016-10-04

    Nondestructive flaw detection in polymeric materials is important but difficult to achieve. In this research, the application of magnetite nanoparticles (MNPs) in nondestructive flaw detection is studied and realized, to the best of our knowledge, for the first time. Superparamagnetic and highly magnetic (up to 63 emu/g) magnetite core-shell nanoparticles are prepared by grafting bromo-end-group-functionalized poly(glycidyl methacrylate) (Br-PGMA) onto surface-modified Fe 3 O 4 NPs. These Fe 3 O 4 -PGMA NPs are blended into bisphenol A diglycidylether (BADGE)-based epoxy to form homogeneously distributed magnetic epoxy nanocomposites (MENCs) after curing. The core Fe 3 O 4 of the Fe 3 O 4 -PGMA NPs endows the MENCs with magnetic property, which is crucial for nondestructive flaw detection of the materials, while the shell PGMA promotes colloidal stability and prevents NP aggregation during curing. The eddy current testing (ET) technique is first applied to detect flaws in the MENCs. Through the brightness contrast of the ET image, surficial and subsurficial flaws in MENCs can be detected, even for MENCs with low content of Fe 3 O 4 -PGMA NPs (1 wt %). The incorporation of Fe 3 O 4 -PGMA NPs can be easily extended to other polymer and polymer-based composite systems and opens a new and very promising pathway toward MNP-based nondestructive flaw detection in polymeric materials.

  4. Investigation of the interaction between magnetic nanoparticles surface-coated with carboxymethyldextran and blood cells using Raman spectroscopy

    International Nuclear Information System (INIS)

    Santana, J.F.B.; Soler, M.A.G.; Silva, S.W. da; Guedes, M.H.; Lacava, Z.G.M.; Azevedo, R.B.; Morais, P.C.

    2005-01-01

    This study reports on in vitro biological tests performed with a biocompatible magnetic fluid based on carboxymethyldextran-coated magnetite nanoparticles (CMDM). Micro Raman spectroscopy was used to investigate the effect of dispersing (CMDM) nanoparticles in mice blood. We focused our investigation in the use of the Raman spectroscopy for monitoring the hemoglobin structural changes, which may be associated with the oxygen-binding process

  5. The role of polymer films on the oxidation of magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Letti, C.J. [Universidade de Brasilia, Instituto de Fisica, 70910-000 Brasilia, DF (Brazil); Paterno, L.G. [Universidade de Brasilia, Instituto de Quimica, 70910-000 Brasilia, DF (Brazil); Pereira-da-Silva, M.A. [Instituto de Fisica de São Carlos, USP, 13560-9700 São Carlos, SP (Brazil); Centro Universitario Central Paulista – UNICEP, 13563-470 São Carlos, SP (Brazil); Morais, P.C. [Universidade de Brasilia, Instituto de Fisica, 70910-000 Brasilia, DF (Brazil); Soler, M.A.G., E-mail: soler@unb.br [Universidade de Brasilia, Instituto de Fisica, 70910-000 Brasilia, DF (Brazil)

    2017-02-15

    A detailed investigation about the role of polymer films on the oxidation process of magnetite nanoparticles (∼7 nm diameter), under laser irradiation is performed employing micro Raman spectroscopy. To support this investigation, Fe{sub 3}O{sub 4}-np are synthesized by the co-precipitation method and assembled layer-by-layer with sodium sulfonated polystyrene (PSS). Polymer films (Fe{sub 3}O{sub 4}-np/PSS){sub n} with n=2,3,5,7,10 and 25 bilayers are employed as a model system to study the oxidation process under laser irradiation. Raman data are further processed by principal component analysis. Our findings suggest that PSS protects Fe{sub 3}O{sub 4}-np from oxidation when compared to powder samples, even for the sample with the greater number of bilayers. Further, the oxidation of magnetite to maghemite occurs preferably for thinner films up to 7 bilayers, while the onset for the formation of the hematite phase depends on the laser intensity for thicker films. Water takes part on the oxidation processes of magnetite, the oxidation/phase transformation of Fe{sub 3}O{sub 4}-np is intensified in films with more bilayers, since more water is included in those films. Encapsulation of Fe{sub 3}O{sub 4}-np by PSS in layer-by-layer films showed to be very efficient to avoid the oxidation process in nanosized magnetite. - Graphical abstract: Encapsulation of Fe{sub 3}O{sub 4}-np by PSS in layer-by-layer films avoids the oxidation and phase transformation of nanosized magnetite. - Highlights: • (Fe{sub 3}O{sub 4}-np/PSS){sub n} nanofilms, with n=2 up to 25, where layer-by-layer assembled. • The influence of film architecture on the Fe{sub 3}O{sub 4}-np oxidation was investigated through Raman spectroscopy. • Encapsulation of Fe{sub 3}O{sub 4}-np by PSS showed to be very efficient to avoid the Fe{sub 3}O{sub 4}-np oxidation.

  6. Selective heterogeneous catalytic hydrogenation of ketone (C═O) to alcohol (OH) by magnetite nanoparticles following Langmuir-Hinshelwood kinetic approach.

    Science.gov (United States)

    Shah, Muhammad Tariq; Balouch, Aamna; Rajar, Kausar; Sirajuddin; Brohi, Imdad Ali; Umar, Akrajas Ali

    2015-04-01

    Magnetite nanoparticles were successfully synthesized and effectively employed as heterogeneous catalyst for hydrogenation of ketone moiety to alcohol moiety by NaBH4 under the microwave radiation process. The improvement was achieved in percent recovery of isopropyl alcohol by varying and optimizing reaction time, power of microwave radiations and amount of catalyst. The catalytic study revealed that acetone would be converted into isopropyl alcohol (IPA) with 99.5% yield in short period of reaction time, using 10 μg of magnetite NPs (Fe3O4). It was observed that the catalytic hydrogenation reaction, followed second-order of reaction and the Langmuir-Hinshelwood kinetic mechanism, which elucidated that both reactants get adsorb onto the surface of silica coated magnetite nanocatalyst to react. Consequently, the rate-determining step was the surface reaction of acetone and sodium borohydride. The current study revealed an environment friendly conversion of acetone to IPA on the basis of its fast, efficient, and highly economical method of utilization of microwave irradiation process and easy catalyst recovery.

  7. MAPLE fabricated magnetite@eugenol and (3-hidroxybutyric acid-co-3-hidroxyvaleric acid)–polyvinyl alcohol microspheres coated surfaces with anti-microbial properties

    Energy Technology Data Exchange (ETDEWEB)

    Grumezescu, Valentina [Lasers Department, National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG-36, Magurele, Bucharest (Romania); Department of Science and Engineering of Oxidic Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Holban, Alina Maria [Microbiology Immunology Department, Faculty of Biology, University of Bucharest, 1–3 Portocalelor Lane, Sector 5, 77206Bucharest (Romania); Iordache, Florin [Institute of Cellular Biology and Pathology of Romanian Academy, “Nicolae Simionescu”, Department of Fetal and Adult Stem Cell Therapy, 8, B.P. Hasdeu, Bucharest 050568 (Romania); Socol, Gabriel [Lasers Department, National Institute for Lasers, Plasma and Radiation Physics, P.O. Box MG-36, Magurele, Bucharest (Romania); Mogoşanu, George Dan [Department of Pharmacognosy and Phytotherapy, Faculty of Pharmacy, University of Medicine and Pharmacy of Craiova, 2 PetruRareş Street, 200349 Craiova (Romania); Grumezescu, Alexandru Mihai, E-mail: grumezescu@yahoo.com [Department of Science and Engineering of Oxidic Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Ficai, Anton; Vasile, Bogdan Ştefan [Department of Science and Engineering of Oxidic Materials and Nanomaterials, Faculty of Applied Chemistry and Materials Science, University Politehnica of Bucharest, 1–7 Polizu Street, 011061 Bucharest (Romania); Truşcă, Roxana [S.C. Metav-CD S.A., 31Rosetti Str., 020015 Bucharest (Romania); Chifiriuc, Mariana Carmen [Microbiology Immunology Department, Faculty of Biology, University of Bucharest, 1–3 Portocalelor Lane, Sector 5, 77206Bucharest (Romania); others, and

    2014-07-01

    This study reports the biological applications of a newly fabricated water dispersible nanostructure, based on magnetite (Fe{sub 3}O{sub 4}) and eugenol (E), prepared in a well-shaped spherical form by precipitation method. The presence of Fe{sub 3}O{sub 4}@E nanoparticles has been confirmed by transmission electron microscopy (TEM). Nanoparticles have been embedded into poly(3-hidroxybutyric acid-co-3-hidroxyvaleric acid)–polyvinyl alcohol (P(3HB-3HV)–PVA) microspheres by oil-in-water emulsion technique. Functionalized P(3HB-3HV)–PVA–Fe{sub 3}O{sub 4}@E microspheres coatings have been fabricated by matrix assisted pulsed laser evaporation (MAPLE). The coatings have been characterized by infrared microscopy (IRM) and scanning electron microscopy (SEM). In vitro biofilm formation by Staphylococcus aureus and Pseudomonas aeruginosa was assessed by the viable cell counts technique. Nanomaterial biocompatibility has been investigated by analyzing the phenotypic changes of cultured eukaryotic cells. Besides their excellent anti-adherence and anti-biofilm properties, the MAPLE coatings have the advantages of using bioactive natural compounds, which are less toxic and easily biodegradable than current antibiotics. This approach could be used as a successful alternative or adjuvant method to control and prevent microbial biofilms associated infections.

  8. MAPLE fabricated magnetite@eugenol and (3-hidroxybutyric acid-co-3-hidroxyvaleric acid)–polyvinyl alcohol microspheres coated surfaces with anti-microbial properties

    International Nuclear Information System (INIS)

    Grumezescu, Valentina; Holban, Alina Maria; Iordache, Florin; Socol, Gabriel; Mogoşanu, George Dan; Grumezescu, Alexandru Mihai; Ficai, Anton; Vasile, Bogdan Ştefan; Truşcă, Roxana; Chifiriuc, Mariana Carmen

    2014-01-01

    This study reports the biological applications of a newly fabricated water dispersible nanostructure, based on magnetite (Fe 3 O 4 ) and eugenol (E), prepared in a well-shaped spherical form by precipitation method. The presence of Fe 3 O 4 @E nanoparticles has been confirmed by transmission electron microscopy (TEM). Nanoparticles have been embedded into poly(3-hidroxybutyric acid-co-3-hidroxyvaleric acid)–polyvinyl alcohol (P(3HB-3HV)–PVA) microspheres by oil-in-water emulsion technique. Functionalized P(3HB-3HV)–PVA–Fe 3 O 4 @E microspheres coatings have been fabricated by matrix assisted pulsed laser evaporation (MAPLE). The coatings have been characterized by infrared microscopy (IRM) and scanning electron microscopy (SEM). In vitro biofilm formation by Staphylococcus aureus and Pseudomonas aeruginosa was assessed by the viable cell counts technique. Nanomaterial biocompatibility has been investigated by analyzing the phenotypic changes of cultured eukaryotic cells. Besides their excellent anti-adherence and anti-biofilm properties, the MAPLE coatings have the advantages of using bioactive natural compounds, which are less toxic and easily biodegradable than current antibiotics. This approach could be used as a successful alternative or adjuvant method to control and prevent microbial biofilms associated infections.

  9. Optimization of factors affecting hexavalent chromium removal from simulated electroplating wastewater by synthesized magnetite nanoparticles.

    Science.gov (United States)

    Ataabadi, Mitra; Hoodaji, Mehran; Tahmourespour, Arezoo; Kalbasi, Mahmoud; Abdouss, Majid

    2015-01-01

    Hexavalent chromium is a mutagen and carcinogen that is of significant concern in water and wastewater. In the present study, magnetite nanoparticles (n-Mag) were investigated as a potential remediation technology for the decontamination of Cr (VI)-contaminated wastewater. Synthesized n-Mag was characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and BET-N2 technology. To screen and optimize the factors affecting Cr (VI) removal efficiency by synthesized nanoparticles, Plackett-Burman (PB) and Taguchi experimental designs were used respectively. The crystalline produced n-Mag was in the size range of 60-70 nm and had a specific surface area (SSA) of 31.55 m(2) g(-1). Results of PB design showed that the most significant factors affecting Cr (VI) removal efficiency were initial Cr (VI) concentration, pH, n-Mag dosage, and temperature. In a pH of 2, 20 mg L(-1) of Cr (VI) concentration, 4 g L(-1)of n-Mag, temperature of 40 °C, 220 rpm of shaking speed, and 60 min of contact time, the complete removal efficiency of Cr (VI) was achieved. Batch experiments revealed that the removal of Cr (VI) by n-Mag was consistent with pseudo-second order reaction kinetics. The competition from common coexisting ions such as NO₃(-), SO₄(2-), and Cl(-) were not considerable, unless in the higher concentration of SO₄(2-). These results indicated that the readily synthesized magnetite nanoparticles have promising applications for the removal of Cr (VI) from aqueous solution.

  10. Magnetite and cobalt ferrite nanoparticles used as seeds for acid mine drainage treatment

    Energy Technology Data Exchange (ETDEWEB)

    Kefeni, Kebede K., E-mail: kkefeni@gmail.com; Mamba, Bhekie B.; Msagati, Titus A.M.

    2017-07-05

    Highlights: • Presence of α-Fe{sub 2}O{sub 3} and Fe{sub 3}O{sub 4} in AMD resulted in formation of crystalline ferrite. • Increasing settling time improved removal of Mg, Ca, Mn and Na from AMD. • Mixtures of ferrite nanoparticles were produced from AMD. • Formations of crystalline ferrite were more favored in the presence of heat. - Abstract: In this study, magnetite and cobalt ferrite nanoparticles were used as seeds for acid mine drainage (AMD) treatment at pH of 7.05 ± 0.35. Duplicate samples of AMD, one without heating and another with heating at 60 °C was treated under continuous stirring for 1 h. The filtrate analysis results from ICP-OES have shown complete removal of Al, Mg, and Mn, while for Fe, Ni and Zn over 90% removals were recorded. Particularly, settling time has significant effect on the removal of Mg, Ca and Na. The results from SQUID have shown superparamagnetic properties of the synthesised magnetic nanoparticles and ferrite sludge. The recovered nanoparticles from AMD are economically important and reduce the cost of waste disposal.

  11. Fine tuning of size and morphology of magnetite nanoparticles synthesized by microemulsion

    Science.gov (United States)

    Singh, Pinki; Upadhyay, Chandan

    2018-05-01

    The synthesis parameters crucially affect the physical and chemical parameters of nanoparticles. Magnetite (Fe3O4) nanoparticles were synthesized using microemulsion method. This method does not require high temperature synthesis, nitrogen environment and/or pH regulation during synthesis process. We are presenting here a systematic study on role of different associated parameters of microemulsion synthesis method on the formation of Fe3O4 nanoparticles. From X-ray Diffraction and Transmission Electron Micoscopy data analysis the size of synthesized particles were observed to be <10 nm. The critical concentration of ferrous-ferric solution to obtain particles in single phase has been found to be ≤0.09 M and ≤0.184 M, respectively. The variation of molar concentration (0.01 M ≤x≤ 0.1 M) of CTAB leads to formation of Fe3O4 nano-scale particles of distinct morphologies e.g. nano-cubes, pentagons and spheres. The number of ferrous and ferric ions involved in the formation decides the size of the nanoparticles. The single crystallographic phase is obtained in reaction temperature range of 65° C

  12. Shape-control by microwave-assisted hydrothermal method for the synthesis of magnetite nanoparticles using organic additives

    Energy Technology Data Exchange (ETDEWEB)

    Rizzuti, Antonino [Politecnico di Bari, Dipartimento di Ingegneria Civile, Ambientale, del Territorio, Edile e di Chimica (Italy); Dassisti, Michele [Politecnico di Bari, Dipartimento di Meccanica, Management e Matematica (Italy); Mastrorilli, Piero, E-mail: p.mastrorilli@poliba.it [Politecnico di Bari, Dipartimento di Ingegneria Civile, Ambientale, del Territorio, Edile e di Chimica (Italy); Sportelli, Maria C.; Cioffi, Nicola; Picca, Rosaria A. [Università di Bari, Dipartimento di Chimica (Italy); Agostinelli, Elisabetta; Varvaro, Gaspare [Consiglio Nazionale delle Ricerche, Istituto di Struttura della Materia (Italy); Caliandro, Rocco [Consiglio Nazionale delle Ricerche, Istituto di Cristallografia (Italy)

    2015-10-15

    A simple and fast microwave-assisted hydrothermal method is proposed for the synthesis of magnetite nanoparticles. The addition of different surfactants (polyvinylpyrrolidone, oleic acid, or trisodium citrate) was studied to investigate the effect on size distribution, morphology, and functionalization of the magnetite nanoparticles. Microwave irradiation at 150 °C for 2 h of aqueous ferrous chloride and hydrazine without additives resulted in hexagonal magnetite nanoplatelets with a facet-to-facet distance of 116 nm and a thickness of 40 nm having a saturation magnetization of ∼65 Am{sup 2} kg{sup −1}. The use of polyvinylpyrrolidone led to hexagonal nanoparticles with a facet-to-facet distance of 120 nm and a thickness of 53 nm with a saturation magnetization of ∼54 Am{sup 2} kg{sup −1}. Additives such as oleic acid and trisodium citrate yielded quasi-spherical nanoparticles of 25 nm in size with a saturation magnetization of ∼70 Am{sup 2} kg{sup −1} and spheroidal nanoparticles of 60 nm in size with a saturation magnetization up to ∼82 Am{sup 2} kg{sup −1}, respectively. A kinetic control of the crystal growth is believed to be responsible for the hexagonal habit of the nanoparticles obtained without additive. Conversely, a thermodynamic control of the crystal growth, leading to spheroidal nanoparticles, seems to occur when additives which strongly interact with the nanoparticle surface are used. A thorough characterization of the materials was performed. Magnetic properties were investigated by Superconducting Quantum Interference Device and Vibrating Sample magnetometers. Based on the observed magnetic properties, the magnetite obtained using citrate appears to be a promising support for magnetically transportable catalysts.

  13. Chitosan-coated magnetic nanoparticles prepared in one step by reverse microemulsion precipitation.

    Science.gov (United States)

    López, Raúl G; Pineda, María G; Hurtado, Gilberto; León, Ramón Díaz de; Fernández, Salvador; Saade, Hened; Bueno, Darío

    2013-09-27

    Chitosan-coated magnetic nanoparticles (CMNP) were obtained at 70 °C and 80 °C in a one-step method, which comprises precipitation in reverse microemulsion in the presence of low chitosan concentration in the aqueous phase. X-ray diffractometry showed that CMNP obtained at both temperatures contain a mixture of magnetite and maghemite nanoparticles with ≈4.5 nm in average diameter, determined by electron microscopy, which suggests that precipitation temperature does not affect the particle size. The chitosan coating on nanoparticles was inferred from Fourier transform infrared spectrometry measurements; furthermore, the carbon concentration in the nanoparticles allowed an estimation of chitosan content in CMNP of 6%-7%. CMNP exhibit a superparamagnetic behavior with relatively high final magnetization values (≈49-53 emu/g) at 20 kOe and room temperature, probably due to a higher magnetite content in the mixture of magnetic nanoparticles. In addition, a slight direct effect of precipitation temperature on magnetization was identified, which was ascribed to a possible higher degree of nanoparticles crystallinity as temperature at which they are obtained increases. Tested for Pb2+ removal from a Pb(NO3)2 aqueous solution, CMNP showed a recovery efficacy of 100%, which makes them attractive for using in heavy metals ion removal from waste water.

  14. Magnetite nanoparticles inhibit tumor growth and upregulate the expression of p53/p16 in Ehrlich solid carcinoma bearing mice.

    Directory of Open Access Journals (Sweden)

    Heba Bassiony

    Full Text Available BACKGROUND: Magnetite nanoparticles (MNPs have been widely used as contrast agents and have promising approaches in cancer treatment. In the present study we used Ehrlich solid carcinoma (ESC bearing mice as a model to investigate MNPs antitumor activity, their effect on expression of p53 and p16 genes as an indicator for apoptotic induction in tumor tissues. METHOD: MNPs coated with ascorbic acid (size: 25.0±5.0 nm were synthesized by co-precipitation method and characterized. Ehrlich mice model were treated with MNPs using 60 mg/Kg day by day for 14 injections; intratumorally (IT or intraperitoneally (IP. Tumor size, pathological changes and iron content in tumor and normal muscle tissues were assessed. We also assessed changes in expression levels of p53 and p16 genes in addition to p53 protein level by immunohistochemistry. RESULTS: Our results revealed that tumor growth was significantly reduced by IT and IP MNPs injection compared to untreated tumor. A significant increase in p53 and p16 mRNA expression was detected in Ehrlich solid tumors of IT and IP treated groups compared to untreated Ehrlich solid tumor. This increase was accompanied with increase in p53 protein expression. It is worth mentioning that no significant difference in expression of p53 and p16 could be detected between IT ESC and control group. CONCLUSION: MNPs might be more effective in breast cancer treatment if injected intratumorally to be directed to the tumor tissues.

  15. Chemical modification of magnetite nanoparticles and preparation of acrylic-base magnetic nanocomposite particles via miniemulsion polymerization

    Energy Technology Data Exchange (ETDEWEB)

    Mahdieh, Athar; Mahdavian, Ali Reza, E-mail: a.mahdavian@ippi.ac.ir; Salehi-Mobarakeh, Hamid

    2017-03-15

    Nowadays, magnetic nanocomposite particles have attracted many interests because of their versatile applications. A new method for chemical modification of Fe{sub 3}O{sub 4} nanoparticles with polymerizable groups is presented here. After synthesis of Fe{sub 3}O{sub 4} nanoparticles by co-precipitation method, they were modified sequentially with 3-aminopropyl triethoxysilane (APTES), acryloyl chloride (AC) and benzoyl chloride (BC) and all were characterized by FTIR, XRD, SEM and TGA analyses. Then the modified magnetite nanoparticles with unsaturated acrylic groups were copolymerized with methyl methacrylate (MMA), butyl acrylate (BA) and acrylic acid (AA) through miniemulsion polymerization. Although several reports exist on preparation of magnetite-base polymer particles, but the efficiency of magnetite encapsulationwith reasonable content and obtaining final stable latexes with limited aggregation ofFe{sub 3}O{sub 4} are still important issues. These were considered here by controlling reaction parameters. Hence, a seriesofmagneticnanocomposites latex particlescontaining different amounts of Fe{sub 3}O{sub 4} nanoparticles (0–10 wt%) were prepared with core-shell morphology and diameter below 200 nm and were characterized by FT-IR, DSC and TGA analyses. Their morphology and size distribution were studied by SEM, TEM and DLS analyses too. Magnetic properties of all products were also measuredby VSM analysis and the results revealed almost superparamagnetic properties for the obtained nanocomposite particles. - Highlights: • Chemical modification of magnetite nanoparticles. • Encapsulation of modified magnetite with acrylic copolymer. • Superparamagnetic Fe3O4/polyacrylic nanocomposite particles.

  16. Study on optimum conditions for Mo-99 adsorption by magnetite nanoparticles

    International Nuclear Information System (INIS)

    Holland, Helber; Yamaura, Mitiko; Damasceno, Marcos O.; Santos, Jacinete L.

    2013-01-01

    Radioisotopes play an important role in the peaceful uses of atomic energy. Technetium-99m is the most used radioisotope for diagnosis imaging in nuclear medicine and it is the decay product of Mo-99. One route to obtaining Mo-99 is in the form of fission product from Uranium targets irradiated in reactor. Uranium targets are dissolved by alkaline or acid process and the obtained solution is submitted to separation and purification steps of Mo-99 from the other fission products. Traditional separation techniques are inadequate for removing large volumes containing low concentrations metals due to the low operating efficiency and high costs processes. Therefore, alternative methods are being investigated as adsorption. Adsorption advantages over other techniques is low waste generation, easy metals recovery and reusability of adsorbents. Inorganic oxides are known for their ability to bind to metal ions in solution. At nanoscale range, this characteristic is highly potentialized. Thus, the use of nanoparticles has attracted attention for metal ions recovery by adsorption. Magnetite, Fe3O4, is an oxide formed by iron ions of valence 2+ and 3+. Due to the superparamagnetic behavior that arises in this material at nanoscale and crystal structure itself which favors surface adsorption, magnetite can be used as an adsorber agent to remove metal ions in solution. In this work, adsorption studies were performed to investigate best conditions for Mo-99 removal in solution. Influence of pH, stirring speed, contact time and initial concentration of Mo were studied. (author)

  17. Bone tissue engineering with human mesenchymal stem cell sheets constructed using magnetite nanoparticles and magnetic force.

    Science.gov (United States)

    Shimizu, Kazunori; Ito, Akira; Yoshida, Tatsuro; Yamada, Yoichi; Ueda, Minoru; Honda, Hiroyuki

    2007-08-01

    An in vitro reconstruction of three-dimensional (3D) tissues without the use of scaffolds may be an alternative strategy for tissue engineering. We have developed a novel tissue engineering strategy, termed magnetic force-based tissue engineering (Mag-TE), in which magnetite cationic liposomes (MCLs) with a positive charge at the liposomal surface, and magnetic force were used to construct 3D tissue without scaffolds. In this study, human mesenchymal stem cells (MSCs) magnetically labeled with MCLs were seeded onto an ultra-low attachment culture surface, and a magnet (4000 G) was placed on the reverse side. The MSCs formed multilayered sheet-like structures after a 24-h culture period. MSCs in the sheets constructed by Mag-TE maintained an in vitro ability to differentiate into osteoblasts, adipocytes, or chondrocytes after a 21-day culture period using each induction medium. Using an electromagnet, MSC sheets constructed by Mag-TE were harvested and transplanted into the bone defect in the crania of nude rats. Histological observation revealed that new bone surrounded by osteoblast-like cells was formed in the defect area 14 days after transplantation with MSC sheets, whereas no bone formation was observed in control rats without the transplant. These results indicated that Mag-TE could be used for the transplantation of MSC sheets using magnetite nanoparticles and magnetic force, providing novel methodology for bone tissue engineering.

  18. Ionic Copolymer-Magnetite Complexes for Magnetic Resonance Imaging and Drug Delivery

    OpenAIRE

    Zhang, Rui

    2015-01-01

    This thesis is focused on the design, synthesis and characterization of magnetite-ionic copolymer complexes as nanocarriers for drug delivery and magnetic resonance imaging. The polymers included phosphonate and carboxylate-containing graft and block copolymers. Oleic-acid coated magnetite nanoparticles (8-nm and 16-nm diameters) were investigated. Cisplatin and carboplatin were used as sample drugs. The potentials of the magnetite-ionomer complexes as dual drug delivery carriers and magneti...

  19. Synthesis and characterization of cationic lipid coated magnetic nanoparticles using multiple emulsions as microreactors

    Energy Technology Data Exchange (ETDEWEB)

    Akbaba, Hasan; Karagöz, Uğur [Ege University, Faculty of Pharmacy, Department of Pharmaceutical Biotechnology, 35100 Izmir (Turkey); Selamet, Yusuf [Izmir Institute of Technology, Faculty of Science, Department of Physics, 35433 Izmir (Turkey); Kantarcı, A. Gülten, E-mail: gulten.kantarci@ege.edu.tr [Ege University, Faculty of Pharmacy, Department of Pharmaceutical Biotechnology, 35100 Izmir (Turkey)

    2017-03-15

    The aim of this study was to develop a novel iron oxide nanoparticle synthesis method with in-situ surface coating. For this purpose multiple emulsions were used as microreactors for the first time and magnetic iron oxide particles synthesized in the core of cationic solid lipid nanoparticles. DLS, SEM, TEM, VSM, Raman Spectrometer, XRD, and XPS techniques were performed for characterization of the magnetic nanoparticles. Obtained magnetic nanoparticles are superparamagnetic and no additional process was needed for surface adjustments. They are positively charged as a result of cationic lipid coating and has appropriate particle size (<30 nm) for drug or nucleic acid delivery. Structure analysis showed that magnetic core material is in the form of magnetite. Saturation magnetization value was measured as 15–17 emu g{sup −1} for lipid coated magnetic nanoparticles obtained by multiple emulsion method which is reasonably sufficient for magnetic targeting. - Highlights: • A novel iron oxide nanoparticle synthesis method with in-situ surface coating. • Combining advantages of microemulsions and multiple emulsion methods. • Multiple emulsions were used as microreactors for magnetic nanoparticle synthesis. • Superparamagnetic iron oxide particles synthesized in the core of cationic lipids. • Possible delivery systems for nucleic acids, oil soluble compounds or drugs.

  20. TEA controllable preparation of magnetite nanoparticles (Fe3O4 NPs) with excellent magnetic properties

    Science.gov (United States)

    Han, Chengliang; Zhu, Dejie; Wu, Hanzhao; Li, Yao; Cheng, Lu; Hu, Kunhong

    2016-06-01

    A fast and controllable synthesis method for superparamagnetic magnetite nanoparticles (Fe3O4 NPs) was developed in Fe(III)-triethanolamine (TEA) solution. The phase structure, morphology and particle size of the as-synthesized samples were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results showed that the magnetic particles were pure Fe3O4 with mean sizes of approximately 10 nm. The used TEA has key effects on the formation of well dispersing Fe3O4 NPs. Vibrating sample magnetometer (VSM) result indicated that the as-obtained Fe3O4 NPs exhibited superparamagnetic behavior and the saturation magnetization (Ms) was about 70 emu/g, which had potential applications in magnetic science and technology.

  1. Anionic magnetite nanoparticle conjugated with pyrrolidinyl peptide nucleic acid for DNA base discrimination

    Energy Technology Data Exchange (ETDEWEB)

    Khadsai, Sudarat; Rutnakornpituk, Boonjira [Naresuan University, Department of Chemistry and Center of Excellence in Biomaterials, Faculty of Science (Thailand); Vilaivan, Tirayut [Chulalongkorn University, Department of Chemistry, Organic Synthesis Research Unit, Faculty of Science (Thailand); Nakkuntod, Maliwan [Naresuan University, Department of Biology, Faculty of Science (Thailand); Rutnakornpituk, Metha, E-mail: methar@nu.ac.th [Naresuan University, Department of Chemistry and Center of Excellence in Biomaterials, Faculty of Science (Thailand)

    2016-09-15

    Magnetite nanoparticles (MNPs) were surface modified with anionic poly(N-acryloyl glycine) (PNAG) and streptavidin for specific interaction with biotin-conjugated pyrrolidinyl peptide nucleic acid (PNA). Hydrodynamic size (D{sub h}) of PNAG-grafted MNPs varied from 334 to 496 nm depending on the loading ratio of the MNP to NAG in the reaction. UV–visible and fluorescence spectrophotometries were used to confirm the successful immobilization of streptavidin and PNA on the MNPs. About 291 pmol of the PNA/mg MNP was immobilized on the particle surface. The PNA-functionalized MNPs were effectively used as solid supports to differentiate between fully complementary and non-complementary/single-base mismatch DNA using the PNA probe. These novel anionic MNPs can be efficiently applicable for use as a magnetically guidable support for DNA base discrimination.Graphical Abstract.

  2. MHD convective flow of magnetite-Fe3O4 nanoparticles by curved stretching sheet

    Directory of Open Access Journals (Sweden)

    Tasawar Hayat

    Full Text Available Present work is devoted to convective flow of ferrofluid due to non linear stretching curved sheet. Electrically conducting fluid is considered in the presence of uniform magnetic field. Nanofluid comprises water and magnetite-Fe3O4 as nanoparticles. Thermal radiation and heat generation/absorption are explained. Homotopy concept is utilized for the development of solutions. Highly nonlinear partial differential systems are reduced into the nonlinear ordinary differential system. Impact of non-dimensional radius of curvature and power law index on the physical quantities like fluid pressure, velocity and temperature field are examined. Computations for surface shear stress and heat transfer rate also analyzed. Keywords: MHD nanofluid, Thermal radiation, Porous medium, Convective boundary conditions, Non-linear curved stretching sheet

  3. Uranium removal by chitosan impregnated with magnetite nanoparticles: adsorption and desorption

    International Nuclear Information System (INIS)

    Stopa, Luiz Claudio Barbosa; Yamaura, Mitiko

    2009-01-01

    A magnetic biosorbent composed of nanoparticles of magnetite covered with chitosan, denominated magnetic chitosan, was prepared. The magnetic chitosan has showed a magnetic response of intense attraction in the presence of a magnetic field without however to become magnetic, a typical behavior of superparamagnetic material. Its adsorption performance was evaluated by the adsorption isotherm models of Langmuir and Freundlich for uranium ions and the desorption behavior using carbonate and oxalate ions was investigated. The adsorption equilibrium data fitted well to the Langmuir model, being the maximum adsorption capacity equal 42 mg g -1 . In the desorption studies, 94% of recovered UO 2 2+ with carbonate ion were verified under the conditions studied. The chitosan, available as a byproduct of marine food processing, is environmentally safe and can be a low cost adsorbent for U removal from waterwaste. The magnetic chitosan as adsorbent of U to treat radioactive waterwaste is a sustainable technology. (author)

  4. Anionic magnetite nanoparticle conjugated with pyrrolidinyl peptide nucleic acid for DNA base discrimination

    International Nuclear Information System (INIS)

    Khadsai, Sudarat; Rutnakornpituk, Boonjira; Vilaivan, Tirayut; Nakkuntod, Maliwan; Rutnakornpituk, Metha

    2016-01-01

    Magnetite nanoparticles (MNPs) were surface modified with anionic poly(N-acryloyl glycine) (PNAG) and streptavidin for specific interaction with biotin-conjugated pyrrolidinyl peptide nucleic acid (PNA). Hydrodynamic size (D h ) of PNAG-grafted MNPs varied from 334 to 496 nm depending on the loading ratio of the MNP to NAG in the reaction. UV–visible and fluorescence spectrophotometries were used to confirm the successful immobilization of streptavidin and PNA on the MNPs. About 291 pmol of the PNA/mg MNP was immobilized on the particle surface. The PNA-functionalized MNPs were effectively used as solid supports to differentiate between fully complementary and non-complementary/single-base mismatch DNA using the PNA probe. These novel anionic MNPs can be efficiently applicable for use as a magnetically guidable support for DNA base discrimination.Graphical Abstract

  5. Synthesis, characterization and a.c. magnetic analysis of magnetite nanoparticles

    International Nuclear Information System (INIS)

    Riani, P.; Napoletano, M.; Canepa, F.

    2011-01-01

    In the last years, the study of Fe-based magnetic nanoparticles (MNP) has attracted increasing interest either for the physical properties shown by nanosized materials (electric and magnetic properties are strongly affected by dimension and surface effects) either for the different technological applications of these materials (catalysis, drug delivery, magnetic resonance imaging, contaminants removal from groundwater, new exchange coupled magnets, soft nanomagnets for high frequency applications, etc.). In this article, the results obtained in the synthesis and characterization of the Fe 3 O 4 MNP is reported. The magnetite nanoparticles were synthesized by a modified Massart method. Structural characterization was performed using X-ray diffraction analysis and a complete morphological and dimensional study was carried out by means of Transmission Electron Microscopy, and a.c. magnetic susceptibility measured as a function of the frequency of the applied magnetic field. Diameters of the superparamagnetic Fe 3 O 4 nanoparticles are ranging from 2 to 10 nm, as evidenced by all the techniques employed. The size distribution of the hydrated aggregates in solution has been obtained by quantitative analysis of the frequency dependence of the a.c. susceptibility. The mathematical approach adopted will be described and all the obtained results will be compared and discussed.

  6. Phytosynthesis and photocatalytic activity of magnetite (Fe_3O_4) nanoparticles using the Andean blackberry leaf

    International Nuclear Information System (INIS)

    Kumar, Brajesh; Smita, Kumari; Cumbal, Luis; Debut, Alexis; Galeas, Salome; Guerrero, Victor H.

    2016-01-01

    In the present study, a simple, low cost, and ecofriendly synthesis of magnetite nanoparticles (Fe_3O_4 NPs) has been developed using Andean blackberry leaf extract. UV–vis spectroscopy technique were used to study the initial formation of Fe_3O_4 NPs. Morphology, crystallinity and surface properties of nanoparticles were studied using transmission electron microscopy (TEM), Dynamic light scattering (DLS), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Thermal gravimetric (TG) techniques. TEM and DLS characterization indicated the formation of spherical Fe_3O_4 NPs of average size 54.5 ± 24.6 nm. XRD and FTIR studies confirmed the existence of the cubic spinel phase of Fe_3O_4 NPs and Fe−O peak at 570 cm"−"1, whereas TG analysis indicated that the nanoparticles contain 94% metal and 6% capping ligand. It has been observed that, as-synthesized Fe_3O_4 NPs exhibited photocatalytic activity for degradation of organic dyes such as methylene blue (k = 0.0105475 min"−"1), congo red (k = 0.0043240 min"−"1), and methyl orange (k = 0.0028930 min"−"1), efficiently. The antioxidant activity of Fe_3O_4 NPs against 1, 1-diphenyl-2-picrylhydrazyl were also evaluated. - Highlights: • We report extracellular phytosynthesis of Fe_3O_4 nanoparticles using the Andean blackberry leaf. • The synthesized Fe_3O_4 nanoparticles are spherical and average size is 54.5 ± 24.6 nm. • It showed enhanced photocatalytic activity and weak antioxidant efficacy. • Environmentally benign, non-toxic and cost-effective method is suggested.

  7. Structural determination of Bi-doped magnetite multifunctional nanoparticles for contrast imaging.

    Science.gov (United States)

    Laguna-Marco, M A; Piquer, C; Roca, A G; Boada, R; Andrés-Vergés, M; Veintemillas-Verdaguer, S; Serna, C J; Iadecola, A; Chaboy, J

    2014-09-14

    To determine with precision how Bi atoms are distributed in Bi-doped iron oxide nanoparticles their structural characterization has been carried out by X-ray absorption spectroscopy (XAS) recorded at the K edge of Fe and at the L3 edge of Bi. The inorganic nanoparticles are nominally hybrid structures integrating an iron oxide core and a bismuth oxide shell. Fe K-edge XAS indicates the formation of a structurally ordered, non-stoichiometric magnetite (Fe3-δO4) phase for all the nanoparticles. The XAS spectra show that, in the samples synthesized by precipitation in aqueous media and laser pyrolysis, the Bi atoms neither enter into the iron oxide spinel lattice nor form any other mixed Bi-Fe oxides. No modification of the local structure around the Fe atoms induced by the Bi atoms is observed at the Fe K edge. In addition, contrary to expectations, our results indicate that the Bi atoms do not form a well-defined Bi oxide structure. The XAS study at the Bi L3 edge indicates that the environment around Bi atoms is highly disordered and only a first oxygen coordination shell is observed. Indefinite [BiO6-x(OH)x] units (isolated or aggregated forming tiny amorphous clusters) bonded through hydroxyl bridges to the nanoparticle, rather than a well defined Bi2O3 shell, surround the nanoparticle. On the other hand, the XAS study indicates that, in the samples synthesized by thermal decomposition, the Bi atoms are embedded in a longer range ordered structure showing the first and second neighbors.

  8. The effect of coating on heat generation properties of Iron oxide nanoparticles

    Science.gov (United States)

    Yuan, Yuan

    Magnetic nanoparticles have attracted more and more attention for their potential application as heating agents in cancer hyperthermia. The effectiveness of cancer hyperthermia can be increased by using particles that have a higher heat generation rate, quantified by specific absorption rate (SAR), at a smaller applied field. In order to optimize the functionality of nanoparticles as heating agents, it is essential to have a comprehensive understanding of factors that may influence SAR including coating and aggregation. In all biomedical applications, the magnetic particles are coated with surfactants and polymers to enhance biocompatibility, prevent agglomeration and add functionality. Coatings may profoundly influence particles' clustering behavior and magnetic properties. Yet its effect on the heat generation rate of the nanoparticles has been scarcely investigated. In this context, a systematic investigation was carried out in this dissertation in order to understand the impact of the surface coating of magnetic nanoparticles on their heat generation rate. The study also includes investigation of normal nerve cell viability in presence of biofunctionalized magnetic nanoparticles with and without exposure to magnetic heating. Commercially available suspensions of iron oxide nanoparticles with a diameter of approximately 10 nm and different coatings relevant to biomedical applications such as aminosilane, carboxymethyl-dextran, protein A, biotin were extensively characterized. First of all, magnetic phase reduction of magnetite nanoparticles was examined by studying the discrepancy between the volume fraction of magnetic phase calculated from magnetization curve and the magnetic core concentration obtained from Tiron chelation test. The findings indicated that coatings might interact with the surface atoms of the magnetic core and form a magnetically disordered layer reducing the total amount of the magnetic phase. Secondly, the impact of coating and aggregation

  9. Magnetite nanoparticles prepared by co-precipitation method in different conditions

    Energy Technology Data Exchange (ETDEWEB)

    Aphesteguy, J.C., E-mail: caphestegu@fi.uba.ar [LAFMACEL-INTECIN, Facultad de Ingeniería, UBA, Paseo Colón 850, C1063EHA Buenos Aires (Argentina); Kurlyandskaya, G.V. [Universidad del País Vasco UPV-EHU, Dept. Electricidad y Electronica, 48940 Leioa (Spain); Ural Federal University, Dept. Magnetism and Magnetic Nanomaterials, 620000 Ekaterinburg (Russian Federation); Celis, J.P. de [National Technology University (UTN), Facultad Regional Avellaneda, Department of Chemistry (Argentina); Safronov, A.P. [Ural Federal University, Dept. Magnetism and Magnetic Nanomaterials, 620000 Ekaterinburg (Russian Federation); Institute of Electrophysics UD RAS, Ekaterinburg 620016 (Russian Federation); Schegoleva, N.N. [Institute of Metal Physics UD RAS, Ekaterinburg 620044 (Russian Federation)

    2015-07-01

    Magnetic nanoparticles (MNPs) of pure magnetite (Fe{sub 3}O{sub 4}) were prepared in an aqueous solution (sample M−I) and in a water-ethyl alcohol mixture (sample M−II) by the co-precipitation method. The structure and magnetic properties of both samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), magnetic (M−H) and microwave measurements (FMR). The mean average particle diameter and particle size distribution was evaluated by the Dynamic Light Scattering (DLS) and Brunauer- Emmett-Teller techniques (BET). The Quantitative chemical analysis of iron was performed by Inductively Coupled Plasma (ICP)- Atomic Emission Spectroscopy (AES) technique. The MNPs prepared in aqueous solution show a higher grain than those prepared in the water-ethyl alcohol mixture. The type of phase structure in both cases can be defined as “defective spinel”. The shape of the majority of M−I MNPs is octahedral. The shape of the majority of M−II MNPs is cubic. The specific surface area of MNPs was as high as 14.4 m{sup 2}/g for M−I sample and 77.8 m{sup 2}/g for sample M–II. The obtained saturation magnetization values of 75 emu/g (M−I) and 68 emu/g (M−II) are consistent with expected values for magnetite MNPs of observed sizes. Ferromagnetic resonance (FMR) measurements confirmed that MNPs of both types are magnetically homogeneous materials. FMR lines' position and line widths can be understood by invoking the local dipolar fields, deviations from sphericity, magnetocrystalline anisotropy and stresses. M−I sample shows sizeable zero field microwave absorption which is absent in the M−II case. The differences in microwave behaviour of M−I and M−II MNPs can be used in the design of microwave radiation absorbing multilayers. - Highlights: • Magnetite nanoparticles were prepared in two different conditions. • Specific surface area of sample prepared in water- ethanol mix is

  10. Dynamic effects of dipolar interactions on the magnetic behavior of magnetite nanoparticles

    Science.gov (United States)

    Allia, Paolo; Tiberto, Paola

    2011-12-01

    Isothermal magnetization and initial dc susceptibility of spheroidal, nearly monodisperse magnetite nanoparticles (typical diameter: 8 nm) prepared by a standard thermo-chemical route have been measured between 10 and 300 K. The samples contained magnetite nanoparticles in the form of either a dried powder (each nanoparticle being surrounded by a stable oleic acid shell as a result of the preparation procedure) or a solid dispersion in PEGDA-600 polymer; different nanoparticle (NP) concentrations in the polymer were studied. In all samples the NPs were not tightly agglomerated nor their ferromagnetic cores were directly touching. The high-temperature inverse magnetic susceptibility is always found to follow a linear law as a function of T, crossing the horizontal axis at negative temperatures ranging from 175 to about 1,000 K. The deviation from the standard superparamagnetic behavior is related to dipolar interaction among NPs; however, a careful analysis makes it hard to conclude that such a behavior originates from a dominant antiferromagnetic character of the interaction. The results are well explained considering that the studied samples are in the interacting superparamagnetic (ISP) regime. The ISP model is basically a mean field theory which allows one to straightforwardly account for the role of magnetic dipolar interaction in a NP system. The model predicts the existence of specific scaling laws for the reduced magnetization which have been confirmed in all studied samples. The interaction of each magnetic dipole moment with the local, random dipolar field produced by the other dipoles results in the presence of a large fluctuating energy term whose magnitude is comparable to the static barrier for magnetization reversal/rotation related to magnetic anisotropy. On the basis of the existing theories on thermal crossing of a barrier whose height randomly fluctuates in time it is predicted that the rate of barrier crossing is substantially driven by the rate

  11. In Vitro Sustained Release Study of Gallic Acid Coated with Magnetite-PEG and Magnetite-PVA for Drug Delivery System

    Science.gov (United States)

    Kura, Aminu Umar; Hussein-Al-Ali, Samer Hasan; Bin Hussein, Mohd Zobir; Fakurazi, Sharida; Shaari, Abdul Halim; Ahmad, Zalinah

    2014-01-01

    The efficacy of two nanocarriers polyethylene glycol and polyvinyl alcohol magnetic nanoparticles coated with gallic acid (GA) was accomplished via X-ray diffraction, infrared spectroscopy, magnetic measurements, thermal analysis, and TEM. X-ray diffraction and TEM results showed that Fe3O4 nanoparticles were pure iron oxide having spherical shape with the average diameter of 9 nm, compared with 31 nm and 35 nm after coating with polyethylene glycol-GA (FPEGG) and polyvinyl alcohol-GA (FPVAG), respectively. Thermogravimetric analyses proved that after coating the thermal stability was markedly enhanced. Magnetic measurements and Fourier transform infrared (FTIR) revealed that superparamagnetic iron oxide nanoparticles could be successfully coated with two polymers (PEG and PVA) and gallic acid as an active drug. Release behavior of gallic acid from two nanocomposites showed that FPEGG and FPVAG nanocomposites were found to be sustained and governed by pseudo-second-order kinetics. Anticancer activity of the two nanocomposites shows that the FPEGG demonstrated higher anticancer effect on the breast cancer cell lines in almost all concentrations tested compared to FPVAG. PMID:24737969

  12. In Vitro Sustained Release Study of Gallic Acid Coated with Magnetite-PEG and Magnetite-PVA for Drug Delivery System

    Directory of Open Access Journals (Sweden)

    Dena Dorniani

    2014-01-01

    Full Text Available The efficacy of two nanocarriers polyethylene glycol and polyvinyl alcohol magnetic nanoparticles coated with gallic acid (GA was accomplished via X-ray diffraction, infrared spectroscopy, magnetic measurements, thermal analysis, and TEM. X-ray diffraction and TEM results showed that Fe3O4 nanoparticles were pure iron oxide having spherical shape with the average diameter of 9 nm, compared with 31 nm and 35 nm after coating with polyethylene glycol-GA (FPEGG and polyvinyl alcohol-GA (FPVAG, respectively. Thermogravimetric analyses proved that after coating the thermal stability was markedly enhanced. Magnetic measurements and Fourier transform infrared (FTIR revealed that superparamagnetic iron oxide nanoparticles could be successfully coated with two polymers (PEG and PVA and gallic acid as an active drug. Release behavior of gallic acid from two nanocomposites showed that FPEGG and FPVAG nanocomposites were found to be sustained and governed by pseudo-second-order kinetics. Anticancer activity of the two nanocomposites shows that the FPEGG demonstrated higher anticancer effect on the breast cancer cell lines in almost all concentrations tested compared to FPVAG.

  13. Nanoparticle/Polymer Nanocomposite Bond Coat or Coating

    Science.gov (United States)

    Miller, Sandi G.

    2011-01-01

    This innovation addresses the problem of coatings (meant to reduce gas permeation) applied to polymer matrix composites spalling off in service due to incompatibility with the polymer matrix. A bond coat/coating has been created that uses chemically functionalized nanoparticles (either clay or graphene) to create a barrier film that bonds well to the matrix resin, and provides an outstanding barrier to gas permeation. There is interest in applying clay nanoparticles as a coating/bond coat to a polymer matrix composite. Often, nanoclays are chemically functionalized with an organic compound intended to facilitate dispersion of the clay in a matrix. That organic modifier generally degrades at the processing temperature of many high-temperature polymers, rendering the clay useless as a nano-additive to high-temperature polymers. However, this innovation includes the use of organic compounds compatible with hightemperature polymer matrix, and is suitable for nanoclay functionalization, the preparation of that clay into a coating/bondcoat for high-temperature polymers, the use of the clay as a coating for composites that do not have a hightemperature requirement, and a comparable approach to the preparation of graphene coatings/bond coats for polymer matrix composites.

  14. The molecular mass of dextran used to modify magnetite nanoparticles affects insulin amyloid aggregation

    Science.gov (United States)

    Siposova, Katarina; Pospiskova, Kristyna; Bednarikova, Zuzana; Safarik, Ivo; Safarikova, Mirka; Kubovcikova, Martina; Kopcansky, Peter; Gazova, Zuzana

    2017-04-01

    Protein transformation from its soluble state into amyloid aggregates is associated with amyloid-related diseases. Amyloid deposits of insulin fibrils have been found in the sites of subcutaneous insulin application in patients with prolonged diabetes. Using atomic force microscopy and ThT fluorescence assay we have investigated the interference of insulin amyloid aggregation with superparamagnetic Fe3O4-based nanoparticles (SPIONs) coated with dextran (DEX); molecular mass of dextran was equal to 15-20, 40 or 70 kDa. The obtained data indicate that all three types of dextran coated nanoparticles (NP-FeDEXs) are able to inhibit insulin fibrillization and to destroy amyloid fibrils. The extent of anti-amyloid activities depends on the properties of NP-FeDEXs, mainly on the size of nanoparticles which is determined by molecular mass of dextran molecules. The most effective inhibiting activity was observed for the smallest nanoparticles coated with 15-20 kDa dextran. Contrary, the highest destroying activity was observed for the largest NP-FeDEX (70 kDa dextran).

  15. Sol-gel synthesis of 8 nm magnetite (Fe 3O 4) nanoparticles and their magnetic properties

    KAUST Repository

    Lemine, O. M.

    2012-10-01

    Magnetite (Fe 3O 4) nanoparticles were successfully synthesized by a sol-gel method. The obtained nanoparticles were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive analysis by X-ray (EDAX), transmission electron microscopy (TEM), superconducting quantum interference device (SQUID) and Mössbauer spectrometry. XRD and Mössbauer measurements indicate that the obtained nanoparticles are single phase. TEM analysis shows the presence of spherical nanoparticles with homogeneous size distribution of about 8 nm. Room temperature ferromagnetics behavior was confirmed by SQUID measurements. The mechanism of nanoparticles formation and the comparison with recent results are discussed. Finally, the synthesized nanoparticles present a potential candidate for hyperthermia application given their saturation magnetization. © 2012 Elsevier Ltd. All rights reserved.

  16. Sol-gel synthesis of 8 nm magnetite (Fe 3O 4) nanoparticles and their magnetic properties

    KAUST Repository

    Lemine, O. M.; Omri, Karim; Zhang, Bei; El Mir, Lassaad; Sajieddine, Mohammed; Alyamani, Ahmed Y.; Bououdina, M.

    2012-01-01

    Magnetite (Fe 3O 4) nanoparticles were successfully synthesized by a sol-gel method. The obtained nanoparticles were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), energy dispersive analysis by X-ray (EDAX), transmission electron microscopy (TEM), superconducting quantum interference device (SQUID) and Mössbauer spectrometry. XRD and Mössbauer measurements indicate that the obtained nanoparticles are single phase. TEM analysis shows the presence of spherical nanoparticles with homogeneous size distribution of about 8 nm. Room temperature ferromagnetics behavior was confirmed by SQUID measurements. The mechanism of nanoparticles formation and the comparison with recent results are discussed. Finally, the synthesized nanoparticles present a potential candidate for hyperthermia application given their saturation magnetization. © 2012 Elsevier Ltd. All rights reserved.

  17. Study of Cr(VI) adsorption onto magnetite nanoparticles using synchrotron-based X-ray absorption spectroscopy

    Science.gov (United States)

    Chen, Yen-Hua; Liu, Dian-Yu; Lee, Jyh-Fu

    2018-04-01

    In this study, the efficiency of Cr(VI) adsorption onto nano-magnetite was examined by batch experiments, and the Cr(VI) adsorption mechanism was investigated using synchrotron-based X-ray absorption spectroscopy. Magnetite nanoparticles with a mean diameter of 10 nm were synthesized using an inexpensive and simple co-precipitation method. It shows a saturation magnetization of 54.3 emu/g, which can be recovered with an external magnetic field. The adsorption data fitted the Langmuir adsorption isotherm well, implying a monolayer adsorption behavior of Cr(VI) onto nano-magnetite. X-ray absorption spectroscopy results indicate that the adsorption mechanism involves electron transfer between Fe(II) in nano-magnetite (Fe2+OFe3+ 2O3) and Cr(VI) to transform into Cr(III), which may exist as an Fe(III)-Cr(III) mixed solid phase. Moreover, the Cr(III)/Cr(VI) ratio in the final products can be determined by the characteristic pre-edge peak area of Cr(VI) in the Cr K-edge spectrum. These findings suggest that nano-magnetite is effective for Cr(VI) removal from wastewater because it can transform highly poisonous Cr(VI) species into nontoxic Cr(III) compounds, which are highly insoluble and immobile under environmental conditions.

  18. Effect of initial pH and temperature of iron salt solutions on formation of magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Gnanaprakash, G. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Mahadevan, S. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Jayakumar, T. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Kalyanasundaram, P. [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India); Philip, John [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India)]. E-mail: philip@igcar.gov.in; Raj, Baldev [Metallurgy and Materials Group, Indira Gandhi Centre for Atomic Research, Kalpakkam 603 102 (India)

    2007-05-15

    We report the effect of initial pH and temperature of iron salt solutions on formation of magnetite (Fe{sub 3}O{sub 4}) nanoparticles during co-precipitation. We synthesized nanoparticles by keeping the initial pH at 0.7, 1.5, 3.0, 4.7, 5.7, 6.7 for two different temperatures of 30 and 60 deg. C. When the initial pH (prior to alkali addition) of the salt solution was below 5, the nanoparticles formed were 100% spinel iron oxide. Average size of the magnetite particles increases with initial pH until ferrihydrite is formed at a pH of 3 and the size remains the same till 4.7 pH. The percentage of goethite formed along with non-stoichiometric magnetite was 35 and 78%, respectively, when the initial pH of the solution was 5.7 and 6.7. As the reaction temperature was increased to 60 deg. C, maintaining a pH of 6.7, the amount of goethite increased from 78 to 100%. These results show that the initial pH and temperature of the ferrous and ferric salt solution before initiation of the precipitation reaction are critical parameters controlling the composition and size of nanoparticles formed. We characterize the samples using X-ray diffraction, transmission electron microscopy and vibrating sample magnetometer. The results of the present work provide the right conditions to synthesis pure magnetite nanoparticles, without goethite impurities, through co-precipitation technique for ferrofluid applications.

  19. Aqueous U(VI) interaction with magnetite nanoparticles in a mixed flow reactor system: HR-XANES study

    International Nuclear Information System (INIS)

    Pidchenko, I; Heberling, F; Finck, N; Schild, D; Bohnert, E; Schäfer, T; Rothe, J; Geckeis, H; Vitova, T; Kvashnina, KO

    2016-01-01

    The redox variations and changes in local atomic environment of uranium (U) interacted with the magnetite nanoparticles were studied in a proof of principle experiment by the U L 3 and M 4 edges high energy resolution X-ray absorption near edge structure (HR-XANES) technique. We designed and applied a mixed flow reactor (MFR) set-up to maintain dynamic flow conditions during U-magnetite interactions. Formation of hydrolyzed, bi- and poly-nuclear U species were excluded by slow continuous injection of U(VI) (10 -6 M) and pH control integrated in the MFR set-up. The applied U HR-XANES technique is more sensitive to minor changes in the U redox states and bonding compared to the conventional XANES method. Major U(VI) contribution in uranyl type of bonding is found in the magnetite nanoparticles after three days operation time of the MFR. Indications for shortening of the U-O axial bond length for the magnetite compared to the maghemite system are present too. (paper)

  20. Effect of nanoparticle and aggregate size on the relaxometric properties of MR contrast agents based on high quality magnetite nanoparticles.

    Science.gov (United States)

    Roca, Alejandro G; Veintemillas-Verdaguer, Sabino; Port, Marc; Robic, Caroline; Serna, Carlos J; Morales, Maria P

    2009-05-14

    Colloidal dispersions of monodispersed and high-crystalline magnetite nanoparticles have been used to establish a relationship between magnetic properties and magnetic resonance (MR) relaxometric parameters in vitro. Magnetite nanoparticles with diameters between 4 and 14 nm were synthesized by thermal decomposition of Fe(acac)3 in different organic solvents and transformed to hydrophilic by changing oleic acid for dimercaptosuccinic acid (DMSA). A final treatment in alkaline water was critical to make the suspension stable at pH 7 with xi-potential values of -45 mV and hydrodynamic sizes as low as 50 nm. Samples showed superparamagnetic behavior at room temperature, which is an important parameter for biomedical applications. Susceptibility increased with both particle and aggregate size, and for particles larger than 9 nm, the aggregate size was the key factor controlling the susceptibility. Relaxivity values followed the same trend as the suspension susceptibilities, indicating that the aggregate size is an important factor above a certain particle size governing the proton relaxation times. The highest relaxivity value, r2=317 s(-1) mM(-1), much higher than those for commercial contrast agents with similar hydrodynamic size, was obtained for a suspension consisting of 9 nm particles and 70 nm of hydrodynamic size, and it was assigned to the higher particle crystallinity in comparison to particles prepared by coprecipitation. Therefore, it can be concluded that in addition to the sample crystallinity, both particle size and aggregate size should be considered in order to explain the magnetic and relaxivity values of a suspension.

  1. Plasmonic and silicon spherical nanoparticle antireflective coatings

    Science.gov (United States)

    Baryshnikova, K. V.; Petrov, M. I.; Babicheva, V. E.; Belov, P. A.

    2016-03-01

    Over the last decade, plasmonic antireflecting nanostructures have been extensively studied to be utilized in various optical and optoelectronic systems such as lenses, solar cells, photodetectors, and others. The growing interest to all-dielectric photonics as an alternative optical technology along with plasmonics motivates us to compare antireflective properties of plasmonic and all-dielectric nanoparticle coatings based on silver and crystalline silicon respectively. Our simulation results for spherical nanoparticles array on top of amorphous silicon show that both silicon and silver coatings demonstrate strong antireflective properties in the visible spectral range. For the first time, we show that zero reflectance from the structure with silicon coatings originates from the destructive interference of electric- and magnetic-dipole responses of nanoparticle array with the wave reflected from the substrate, and we refer to this reflection suppression as substrate-mediated Kerker effect. We theoretically compare the silicon and silver coating effectiveness for the thin-film photovoltaic applications. Silver nanoparticles can be more efficient, enabling up to 30% increase of the overall absorbance in semiconductor layer. Nevertheless, silicon coatings allow up to 64% absorbance increase in the narrow band spectral range because of the substrate-mediated Kerker effect, and band position can be effectively tuned by varying the nanoparticles sizes.

  2. SERS Detection of Penicillin G Using Magnetite Decorated with Gold Nanoparticles

    Directory of Open Access Journals (Sweden)

    Paula C. Pinheiro

    2017-10-01

    Full Text Available Sensitive and reliable procedures for detecting vestigial antibiotics are of great relevance for water quality monitoring due to the occurrence of such emergent pollutants in the aquatic environment. As such, we describe here research concerning the use of multifunctional nanomaterials combining magnetic and plasmonic components. These nanomaterials have been prepared by decorating magnetite nanoparticles (MNP with colloidal gold nanoparticles (Au NPs of distinct particle size distributions. Several analytical conditions were investigated in order to optimize the surface enhanced Raman scattering (SERS detection of penicillin G (PG dissolved in water. In particular, the dependence of the SERS signal by using distinct sized Au NPs adsorbed at the MNP was investigated. Additionally, microscopic methods, including Raman confocal microscopy, were employed to characterize the SERS substrates and then to qualitatively detect penicillin G using such substrates. For example, magnetic–plasmonic nanocomposites can be employed for magnetically concentrate analyte molecules and their removal from solution. As a proof of concept, we applied magneto-plasmonic nanosorbents in the removal of aqueous penicillin G and demonstrate the possibility of SERS sensing this antibiotic.

  3. Green Synthesis of Magnetite (Fe3O4) Nanoparticles Using Seaweed ( Kappaphycus alvarezii) Extract

    Science.gov (United States)

    Yew, Yen Pin; Shameli, Kamyar; Miyake, Mikio; Kuwano, Noriyuki; Bt Ahmad Khairudin, Nurul Bahiyah; Bt Mohamad, Shaza Eva; Lee, Kar Xin

    2016-06-01

    In this study, a simple, rapid, and eco-friendly green method was introduced to synthesize magnetite nanoparticles (Fe3O4-NPs) successfully. Seaweed Kappaphycus alvarezii ( K. alvarezii) was employed as a green reducing and stabilizing agents. The synthesized Fe3O4-NPs were characterized with X-ray diffraction (XRD), ultraviolet-visible spectroscopy (UV-Vis), Fourier transform infrared (FT-IR), and transmission electron microscopy (TEM) techniques. The X-ray diffraction planes at (220), (311), (400), (422), (511), (440), and (533) were corresponding to the standard Fe3O4 patterns, which showed the high purity and crystallinity of Fe3O4-NPs had been synthesized. Based on FT-IR analysis, two characteristic absorption peaks were observed at 556 and 423 cm-1, which proved the existence of Fe3O4 in the prepared nanoparticles. TEM image displayed the synthesized Fe3O4-NPs were mostly in spherical shape with an average size of 14.7 nm.

  4. Self-organization of magnetite nanoparticles in providing Saccharomyces cerevisiae Yeasts with magnetic properties

    International Nuclear Information System (INIS)

    Gorobets, S.V.; Yu, Gorobets O.; Demianenko, I.V.; Nikolaenko, R.N.

    2013-01-01

    The compared analyze of four methods of the magnetic nanoparticles clusters parameters estimation were developed and performed, such as, method, which takes into account two magneto-force scans of surface for calculation, geometry distance measurement between two centers of clusters in chains using the functions of NOVA-program, which is the standard computer equipment for scanning probe microscopy SOLVER PRO-M and the model, which takes into account the table meaning of magnetite magnetization and atomic-force microscopy. The magnetically-controllable biosorbent based on the culture of Saccharomyces cerevisiae was used as a model object for adequacy analyze of these models. As the result of the work we get the information about the depth of clusters penetration inside biomembrane, the typical sizes of clusters and the dispersion of magnetic clusters sizes. This analyze shows that all four methods can be used for single magnetic clusters, but for clusters, which lay in chains with small distance between their centers, the mode, which takes into account the table meaning of magnetite magnetization, cannot be used, because this model does not take into account the nearest neighbors contribution of interaction of magnetic fields dipole with magnetic probe. - Highlights: ► We have developed a mathematical model to determine the localization of magnetic phase in the vicinity of the membrane. ► We tried out this model on magnetically-based biosorbent yeast S. cerevisiae. ► We used magnetic force microscopy for the detection of magnetic phase in the biosorbent. ► As a result, it was shown that the magnetic phase is located on the membrane surface, which in turn allows us to estimate its size

  5. The processing of polyelectrolyte-covered magnetite nanoparticles in the form of nanostructured thin films

    International Nuclear Information System (INIS)

    Marangoni, Valéria S.; Martins, Marccus Victor A.; Souza, José A.; Oliveira, Osvaldo N.; Zucolotto, Valtencir; Crespilho, Frank N.

    2012-01-01

    Magnetic nanoparticles are promising for a variety of applications, such as biomedical devices, spin electronics, magnetic data storage media, to name a few. However, these goals may only be reached if stable and organized structures are fabricated. In this article, we report on a single-step synthetic route with the coprecipitation method, in which iron oxide magnetic nanoparticles (Fe 3 O 4 NPs) were stabilized in aqueous media using the poly(diallyldimethylammonium chloride) (PDAC) polyelectrolyte. The Fe 3 O 4 NPs had a diameter of ca. 5 nm, according to transmission electron microscopy (TEM) images, being arranged in an inverse spinel structure typical of magnetite. An investigation with infrared spectroscopy indicated that the mechanisms of stabilization in the polymer matrix were based on the interaction between quaternary amide groups from PDAC and the nanoparticle surface. The Fe 3 O 4 -PDAC NPs exhibited considerable magnetic susceptibility, with a monotonic increase in the magnetization with decreasing temperature. These Fe 3 O 4 -PDAC NPs were immobilized in layer-by-layer (LbL) films, being alternated with layers of poly(vinylsulfonic acid) (PVS). The LbL films were much rougher than typical films made with polyelectrolytes, and Fe 3 O 4 -PDAC NPs have been responsible for the high electrocatalytic activity toward H 2 O 2 reduction, with an overpotential shift of 0.69 V. Overall, the stability, magnetic properties and film-forming ability indicate that the Fe 3 O 4 -PDAC NPs may be used for nanoelectronics and bioelectrochemical devices requiring reversible and magnetic redox materials.

  6. Aloe vera plant-extracted solution hydrothermal synthesis and magnetic properties of magnetite (Fe3O4) nanoparticles

    Science.gov (United States)

    Phumying, Santi; Labuayai, Sarawuth; Thomas, Chunpen; Amornkitbamrung, Vittaya; Swatsitang, Ekaphan; Maensiri, Santi

    2013-06-01

    Magnetite (Fe3O4) nanoparticles have been successfully synthesized by a novel hydrothermal method using ferric acetylacetonate (Fe(C5H8O2)3) and aloe vera plant-extracted solution. The influences of different reaction temperatures and times on the structure and magnetic properties of the synthesized Fe3O4 nanoparticles were investigated. The synthesized nanoparticles are crystalline and have particle sizes of ˜6-30 nm, as revealed by transmission electron microscopy (TEM). The results of X-ray diffraction (XRD), High resolution TEM (HRTEM) and selected area electron diffraction (SAED) indicate that the synthesized Fe3O4 nanoparticles have the inverse cubic spinel structure without the presence of any other phase impurities. The hysteresis loops of the Fe3O4 nanoparticles at room temperature show superparamagnetic behavior and the saturation magnetization of the Fe3O4 samples increases with increasing reaction temperature and time.

  7. Magnetite nanoparticles enhance the performance of a combined bioelectrode-UASB reactor for reductive transformation of 2,4-dichloronitrobenzene.

    Science.gov (United States)

    Wang, Caiqin; Ye, Lu; Jin, Jie; Chen, Hui; Xu, Xiangyang; Zhu, Liang

    2017-09-04

    Direct interspecies electron transfer (DIET) among the cometabolism microbes plays a key role in the anaerobic degradation of persistent organic pollutants and stability of anaerobic bioreactor. In this study, the COD removal efficiency increased to 99.0% during the start-up stage in the combined bioelectrode-UASB system (R1) with magnetite nanoparticles addition, which was higher than those in the coupled bioelectrode-UASB (R2; 83.2%) and regular UASB (R3; 71.0%). During the stable stage, the increase of 2,4-dichloronitrobenzene (2,4-DClNB) concentration from 25 mg L -1 to 200 mg L -1 did not affect the COD removal efficiencies in R1 and R2, whereas the performance of R3 was deteriorated obviously. Further intermediates analysis indicated that magnetite nanoparticles enhanced the reductive dechlorination of 2,4-DClNB. High-throughput sequencing results showed that the functional microbes like Syntrophobacter and Syntrophomonas which have been reported to favor the DIET, were predominant on the cathode surface of R1 reactor. It is speculated that the addition of magnetite nanoparticles favors the cooperative metabolism of dechlorinating microbes and electricigens during 2,4-DClNB degradation process in the combined bioelectrode-UASB reactor. This study may provide a new strategy to improve the performance of microbial electrolysis cells and enhance the pollutant removal efficiency.

  8. Susceptibility investigation of the nanoparticle coating-layer effect on the particle interaction in biocompatible magnetic fluids

    International Nuclear Information System (INIS)

    Morais, P.C.; Santos, J.G.; Silveira, L.B.; Gansau, C.; Buske, N.; Nunes, W.C.; Sinnecker, J.P.

    2004-01-01

    AC susceptibility was used to investigate the effect of the surface-coating layer in two biocompatible, magnetite-based, magnetic fluid samples. Dextran and dimercaptosuccinic acid (DMSA) were the surface coating species. The temperature and frequency dependence of the peak susceptibility was discussed using the Vogel-Fulcher relation, from which the typical energy barrier (temperature correction) values of 1340±20 K (70±3 K) and 1230±30 K (86±5 K) were obtained for the dextran- and DMSA-coated nanoparticles, respectively

  9. Mechanosynthesis, structural, thermal and magnetic characteristics of oleic acid coated Fe{sub 3}O{sub 4} nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Marinca, T.F., E-mail: traian.marinca@stm.utcluj.ro [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca (Romania); Chicinaş, H.F.; Neamţu, B.V. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca (Romania); Isnard, O. [Université Grenoble Alpes, Inst NEEL, F-38042 Grenoble (France); CNRS, Institut NEEL, 25 rue des Martyrs, BP166, F-38042 Grenoble (France); Pascuta, P. [Physics and Chemistry Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca (Romania); Lupu, N.; Stoian, G. [National Institute of Research & Development for Technical Physics, 47 Mangeron Boulevard, Iasi 700050 (Romania); Chicinaş, I. [Materials Science and Engineering Department, Technical University of Cluj-Napoca, 103-105, Muncii Avenue, 400641 Cluj-Napoca (Romania)

    2016-03-01

    Oleic acid coated iron ferrite-magnetite nanoparticles (Fe{sub 3}O{sub 4}) have been synthesized via a new combined route, ceramic method and subsequent wet mechanical milling, starting from a stoichiometric mixture of the easily accessible Fe and Fe{sub 2}O{sub 3} precursors. In the first step, the magnetite has been obtained in well crystallised state by heat treatment of precursor's mixture. In the second step, the as obtained magnetite powder has been wet milled in a high energy planetary ball mill using oleic acid as process control agent. Using the same conditions dry milled magnetite samples have been obtained for comparison. The as obtained powders have been characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), magnetic measurements M = f(H), scanning electron microscopy (SEM) and differential scanning calorimetry (DSC). According to XRD analysis two different processing mechanisms are observed for dry and wet milling modes. The magnetite mean crystallite size is 19 nm according to XRD after 240 min of wet mechanical milling. The High Resolution SEM confirmed that the powder consists in nanoparticles that have particles with the size up to 30 nm. The bond of the oleic acid to the magnetite nanoparticles has been observed by FTIR and DSC investigations. The presence of free and bonded oleic acid is revealed and the free oleic acid can be removed controlled by heat treatment. The magnetisation of the milled samples is lower as compared to the magnetisation of the un-milled sample due to several causes such as disordered structure, finite size effect and powder contamination. A powder contamination with iron occurs during milling and this leads to the formation of a wüstite-FeO phase for the dry milled samples. In the case of the wet milled samples, due to an oleic acid layer the FeO phase formation is prevented. - Highlights: • Oleic acid coated magnetite has been synthetized by a new combined route. • XRD

  10. Biomolecule-coated metal nanoparticles on titanium.

    Science.gov (United States)

    Christensen, Stephen L; Chatt, Amares; Zhang, Peng

    2012-02-07

    Immobilizations of nanoparticles and biomolecules on biocompatible substrates such as titanium are two promising approaches to bringing new functionalities to Ti-based biomaterials. Herein, we used a variety of X-ray spectroscopic techniques to study and better understand metal-thiolate interactions in biofunctionalized metal nanoparticle systems supported on Ti substrates. Using a facile one-step procedure, a series of Au nanoparticle samples with varied biomolecule coatings ((2-mercatopropionyl)glycine (MPG) and bovine serum albumin (BSA)) and biomolecule concentrations are prepared. Ag and Pd systems are also studied to observe change with varying metal composition. The structure and properties of these biomolecule-coated nanoparticles are investigated with scanning electron microscopy (SEM) and element-specific X-ray techniques, including extended X-ray absorption fine structure (Au L(3)-edge), X-ray absorption near-edge structure (Au L(3), Ag L(3), Pd L(3), and S K-edge), and X-ray photoelectron spectroscopy (Au 4f, Ag 3d, Pd 3d, and S 2p core level). It was found that, by comparison of SEM and X-ray spectroscopy results, the coating of metal nanoparticles with varying model biomolecule systems can have a significant effect on both surface coverage and organization. This work offers a facile chemical method for bio- and nanofunctionalization of Ti substrates as well as provides a physical picture of the structure and bonding of biocoated metal nanoparticles, which may lead to useful applications in orthopedics and biomedicine.

  11. Semi-Biosynthesis of Magnetite-Gold Composite Nanoparticles Using an Ethanol Extract of Eucalyptus camaldulensis and Study of the Surface Chemistry

    Directory of Open Access Journals (Sweden)

    Emad al din Haratifar

    2009-01-01

    Full Text Available Green synthesis of metal nanoparticles, such as silver or gold nanoparticles, has been attracting increasing attention in recent years. Functionalized magnetite nanoparticles have many uses in various applications, including nanoelectronic devices, molecular recognition, biomedical applications, drug delivery targeting, and optical devices. In this investigation, magnetic cores (Fe3O4 were synthesized using a fabrication method involving coprecipitation of Fe2+ and Fe3+. In the next step, magnetite-gold composite nanoparticles were synthesized with size ranging from 6–20 nm, using an ethanol extract of Eucalyptus camaldulensis as a natural reducing agent. Transmission electron microscopy, energy-dispersive spectroscopy, X-ray diffraction spectroscopy, and visible absorption spectroscopy confirmed the fabrication of magnetite-gold composite nanoparticles. In the UV spectra diagram, a red-shift of the surface plasmon of the Au was evidence that contact between gold and Fe3O4 had occurred. The surface chemistry of the as-prepared magnetite-gold nanoparticles was studied using infrared spectroscopy. The presence of organic compounds with a carboxyl moiety was confirmed on the surface of the magnetite-gold nanoparticles fabricated by this combined chemical and biological reducing process, which we have designated as a semi-biosynthesis method.

  12. Chromium(VI Removal from Aqueous Solution by Magnetite Coated by a Polymeric Ionic Liquid-Based Adsorbent

    Directory of Open Access Journals (Sweden)

    Thania Alexandra Ferreira

    2017-05-01

    Full Text Available An evaluation of the chromium(VI adsorption capacity of four magnetite sorbents coated with a polymer phase containing polymethacrylic acid or polyallyl-3-methylimidazolium is presented. Factors that influence the chromium(VI removal such as solution pH and contact time were investigated in batch experiments and in stirred tank reactor mode. Affinity and rate constants increased with the molar ratio of the imidazolium. The highest adsorption was obtained at pH 2.0 due to the contribution of electrostatic interactions.

  13. Chromium(VI) Removal from Aqueous Solution by Magnetite Coated by a Polymeric Ionic Liquid-Based Adsorbent

    Science.gov (United States)

    Ferreira, Thania Alexandra; Rodriguez, Jose Antonio; Paez-Hernandez, María Elena; Guevara-Lara, Alfredo; Barrado, Enrique; Hernandez, Prisciliano

    2017-01-01

    An evaluation of the chromium(VI) adsorption capacity of four magnetite sorbents coated with a polymer phase containing polymethacrylic acid or polyallyl-3-methylimidazolium is presented. Factors that influence the chromium(VI) removal such as solution pH and contact time were investigated in batch experiments and in stirred tank reactor mode. Affinity and rate constants increased with the molar ratio of the imidazolium. The highest adsorption was obtained at pH 2.0 due to the contribution of electrostatic interactions. PMID:28772865

  14. Surface modification of magnetite nanoparticle with azobenzene-containing water dispersible polymer

    International Nuclear Information System (INIS)

    Theamdee, Pawinee; Traiphol, Rakchart; Rutnakornpituk, Boonjira; Wichai, Uthai; Rutnakornpituk, Metha

    2011-01-01

    We here report the synthesis of magnetite nanoparticle (MNP) grafted with poly (ethylene glycol) methyl ether methacrylate (PEGMA)-azobenzene acrylate (ABA) statistical copolymer via atom transfer radical polymerization (ATRP) for drug entrapment and photocontrolled release. MNP was synthesized via thermal decomposition of iron (III) acetylacetonate in benzyl alcohol and surface functionalized to obtain ATRP initiating sites. Molar compositions of the copolymer on MNP surface were systematically varied (100:0, 90:10, 70:30, and 50:50 of PEGMA:ABA, respectively) to obtain water dispersible particles with various amounts of azobenzene. The presence of polymeric shell on MNP core was evidenced by transmission electron microscopy (TEM). Drug loading and entrapment efficiencies as well as drug release behavior of the copolymer–MNP complexes were investigated. It was found that when percent of ABA in the copolymers was increased, entrapment and loading efficiencies of prednisolone model drug were enhanced. Releasing rate and percent of the released prednisolone of the complex exposed in UV light were slightly enhanced as compared to the system without UV irradiation. This copolymer–MNP complex with photocontrollable drug release and magnetic field-directed properties is warranted for further studies for potential uses as a novel drug delivery vehicle.

  15. Adsorptive desulfurization of model oil using untreated, acid activated and magnetite nanoparticle loaded bentonite as adsorbent

    Directory of Open Access Journals (Sweden)

    Muhammad Ishaq

    2017-02-01

    Full Text Available The present research work focuses on a novel ultraclean desulfurization process of model oil by the adsorption method using untreated, acid activated and magnetite nanoparticle loaded bentonite as adsorbent. The parameters investigated are effect of contact time, adsorbent dose, initial dibenzothiophene (DBT concentration and temperature. Experimental tests were conducted in batch process. Pseudo first and second order kinetic equations were used to examine the experimental data. It was found that pseudo second order kinetic equation described the data of the DBT adsorption onto all types of adsorbents very well. The isotherm data were analyzed using Langmuir and Freundlich isotherm models. The Langmuir isotherm model fits the data very well for the adsorption of DBT onto all three forms of adsorbents. The adsorption of DBT was also investigated at different adsorbent doses and was found that the percentage adsorption of DBT was increased with increasing the adsorbent dose, while the adsorption in mg/g was decreased with increasing the adsorbent dose. The prepared adsorbents were analyzed by scanning electron microscopy (SEM, energy dispersive X-ray spectrometry (EDX and X-ray diffraction (XRD.

  16. Application of biocompatible magnetite nanoparticles for the removal of arsenic and copper from water

    Science.gov (United States)

    Iconaru, S. L.; Beuran, M.; Turculet, C. S.; Negoi, I.; Teleanu, G.; Prodan, A. M.; Motelica-Heino, M.; Guégan, R.; Ciobanu, C. S.; Jiga, G.; Predoi, Daniela

    2018-02-01

    The progress of nanotechnology made possible the use of nanomaterials as adsorbents and magnetic iron oxides represents one of the first generations of nanoscale materials used in environment technologies [1]. A systematic characterization of commercial magnetite (Fe3O4) is presented in this research. The commercial (Fe3O4) magnetic adsorbents were characterized by various characterizations methods such as X-ray diffraction (XRD), Scanning Electron Microscopy (SEM) and Energy Dispersive X-ray analysis (EDX). This study was also focused on the study of adsorption isotherms and the kinetics evaluation. X-ray studies indicated that As3+ and Cu2+ removed by Fe3O4 did not seem to alter the structure of Fe3O4 but they were highlighted in the EDX analysis. In addition, the SEM studies were consistent with the XRD results. The rate of adsorption of contaminants, in contaminated solutions decreases when the amount of contaminant increases in all experiments performed. The results revealed that Fe3O4 nanoparticles are promising candidates which could be used as sorbents for the removal of arsenic from the marine environment, for site remediation and groundwater treatment.

  17. Phosphate removal and recovery from water using nanocomposite of immobilized magnetite nanoparticles on cationic polymer.

    Science.gov (United States)

    Abo Markeb, Ahmad; Alonso, Amanda; Dorado, Antonio David; Sánchez, Antoni; Font, Xavier

    2016-08-01

    A novel nanocomposite (NC) based on magnetite nanoparticles (Fe3O4-NPs) immobilized on the surface of a cationic exchange polymer, C100, using a modification of the co-precipitation method was developed to obtain magnetic NCs for phosphate removal and recovery from water. High-resolution transmission electron microscopy-energy-dispersive spectroscopy, scanning electron microscopy , X-ray diffraction, and inductively coupled plasma optical emission spectrometry were used to characterize the NCs. Continuous adsorption process by the so-called breakthrough curves was used to determine the adsorption capacity of the Fe3O4-based NC. The adsorption capacity conditions were studied under different conditions (pH, phosphate concentration, and concentration of nanoparticles). The optimum concentration of iron in the NC for phosphate removal was 23.59 mgFe/gNC. The sorption isotherms of this material were performed at pH 5 and 7. Taking into account the real application of this novel material in real water, the experiments were performed at pH 7, achieving an adsorption capacity higher than 4.9 mgPO4-P/gNC. Moreover, Freundlich, Langmuir, and a combination of them fit the experimental data and were used for interpreting the influence of pH on the sorption and the adsorption mechanism for this novel material. Furthermore, regeneration and reusability of the NC were tested, obtaining 97.5% recovery of phosphate for the first cycle, and at least seven cycles of adsorption-desorption were carried out with more than 40% of recovery. Thus, this work described a novel magnetic nanoadsorbent with properties for phosphate recovery in wastewater.

  18. Cadmium Immobilization in Soil using Sodium Dodecyl Sulfate Stabilized Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    Ahmad Farrokhian Firouzi

    2017-06-01

    Full Text Available Introduction Some methods of contaminated soils remediation reduces the mobile fraction of trace elements, which could contaminate groundwater or be taken up by soil organisms. Cadmium (Cd as a heavy metal has received much attention in the past few decades due to its potential toxic impact on soil organism activity and compositions. Cadmium is a soil pollutant of no known essential biological functions, and may pose threats to soil-dwelling organisms and human health. Soil contamination with Cd usually originates from mining and smelting activities, atmospheric deposition from metallurgical industries, incineration of plastics and batteries, land application of sewage sludge, and burning of fossil fuels. Heavy metal immobilization using amendments is a simple and rapid method for the reduction of heavy metal pollution. One way of the assessment of contaminated soils is sequential extraction procedure. Sequential extraction of heavy metals in soils is an appropriate way to determine soil metal forms including soluble, exchangeable, carbonate, oxides of iron and manganese, and the residual. Its results are valuable in prediction of bioavailability, leaching rate and elements transformation in contaminated agricultural soils. Materials and Methods The objective of this study was to synthesize magnetite nanoparticles (Fe3O4 stabilized with sodium dodecyl sulfate (SDS and to investigate the effect of its different percentages (0, 1, 2.5, 5, and 10% on the different fractions of cadmium in soil by sequential extraction method. The nanoparticles were synthesized following the protocol described by Si et al. (19. The investigations were carried out with a loamy sand topsoil. Before use, the soil was air-dried, homogenized and sieved (

  19. Coatings of nanoparticles applied to brachytherapy treatments

    International Nuclear Information System (INIS)

    Gonzalez, Andreza A.D.C.C.; Rostelato, Maria Elisa C.M.; Souza, Carla D.; Rodrigues, Bruna T.; Souza, Daiane C.B.; Zeituni, Carlos A.; Nogueira, Beatriz R.

    2017-01-01

    Brachytherapy is a treatment for cancer in which the radiation is placed close or in contact with the region to be treated saving the surrounding healthy tissues. Nanotechnology is the science that studies the properties of nanometric materials. Nanobrachytherapy in a new field that unites the advantages of brachytherapy with the small size in the nanoparticle, resulting in an even less invasive treatment. In view of the synthesis of the nanoparticles and their use, there is a fundamental role that is made by the coatings, which not only have the function of avoiding the aggregation of particles, but also stabilize and control their functional properties. Among the range of coatings, the most outstanding are polyethylene glycol (PEG) and gum arabica (GA). PEG improves the surface properties of nanoparticles and presents high stability under biomedical conditions. After the synthesis of gold nanoparticles was developed, PEG and gum arabica were successfully incorporated into the surface. In a vial of pyrex, 1 ml of coating agent and 1 ml of nanoparticles was left under gentle shaking for 2 hours. Incorporation was confirmed by DLS and HRTEM. GA requires further study. (author)

  20. Coatings of nanoparticles applied to brachytherapy treatments

    Energy Technology Data Exchange (ETDEWEB)

    Gonzalez, Andreza A.D.C.C.; Rostelato, Maria Elisa C.M.; Souza, Carla D.; Rodrigues, Bruna T.; Souza, Daiane C.B.; Zeituni, Carlos A.; Nogueira, Beatriz R., E-mail: ccg.andreza@gmail.com, E-mail: elisaros@ipen.br [Instituto de Pesquisas Energeticas e Nucleares (IPEN/CNEN-SP), Sao Paulo, SP (Brazil)

    2017-07-01

    Brachytherapy is a treatment for cancer in which the radiation is placed close or in contact with the region to be treated saving the surrounding healthy tissues. Nanotechnology is the science that studies the properties of nanometric materials. Nanobrachytherapy in a new field that unites the advantages of brachytherapy with the small size in the nanoparticle, resulting in an even less invasive treatment. In view of the synthesis of the nanoparticles and their use, there is a fundamental role that is made by the coatings, which not only have the function of avoiding the aggregation of particles, but also stabilize and control their functional properties. Among the range of coatings, the most outstanding are polyethylene glycol (PEG) and gum arabica (GA). PEG improves the surface properties of nanoparticles and presents high stability under biomedical conditions. After the synthesis of gold nanoparticles was developed, PEG and gum arabica were successfully incorporated into the surface. In a vial of pyrex, 1 ml of coating agent and 1 ml of nanoparticles was left under gentle shaking for 2 hours. Incorporation was confirmed by DLS and HRTEM. GA requires further study. (author)

  1. Electromagnetics of active coated nano-particles

    DEFF Research Database (Denmark)

    Arslanagic, Samel

    2013-01-01

    This work reviews the fundamental properties of several spherical and cylindrical active coated nano-particles excited by their respective single and/or multiple sources of radiation at optical frequencies. Particular attention is devoted to the influence of the source location and orientation, t......, the optical gain constant and the nano-particle material composition on the electric and magnetic near fields, the power flow density, the radiated power as well as the directivities. Resonant as well as quasi-transparent states will be emphasized in the discussion.......This work reviews the fundamental properties of several spherical and cylindrical active coated nano-particles excited by their respective single and/or multiple sources of radiation at optical frequencies. Particular attention is devoted to the influence of the source location and orientation...

  2. The effect of polymer coatings on proton transverse relaxivities of aqueous suspensions of magnetic nanoparticles

    International Nuclear Information System (INIS)

    Carroll, Matthew R J; House, Michael J; Woodward, Robert C; St Pierre, Timothy G; Huffstetler, Phillip P; Miles, William C; Goff, Jonathon D; Davis, Richey M; Riffle, Judy S

    2011-01-01

    Iron oxide magnetic nanoparticles are good candidates for magnetic resonance imaging (MRI) contrast agents due to their high magnetic susceptibilities. Here we investigate 19 polyether-coated magnetite nanoparticle systems comprising three series. All systems were synthesized from the same batch of magnetite nanoparticles. A different polyether was used for each series. Each series comprised systems with systematically varied polyether loadings per particle. A highly significant (p < 0.0001) linear correlation (r = 0.956) was found between the proton relaxivity and the intensity-weighted average diameter measured by dynamic light scattering in the 19 particle systems studied. The intensity-weighted average diameter measured by dynamic light scattering is sensitive to small number fractions of larger particles/aggregates. We conclude that the primary effect leading to differences in proton relaxivity between systems arises from the small degree of aggregation within the samples, which appears to be determined by the nature of the polymer and, for one system, the degree of polymer loading of the particles. For the polyether coatings used in this study, any changes in relaxivity from differences in water exclusion or diffusion rates caused by the polymer are minor in comparison with the changes in relaxivity resulting from variations in the degree of aggregation.

  3. The effect of polymer coatings on proton transverse relaxivities of aqueous suspensions of magnetic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Carroll, Matthew R J; House, Michael J; Woodward, Robert C; St Pierre, Timothy G [School of Physics, University of Western Australia, 35 Stirling Hwy, Crawley, WA 6009 (Australia); Huffstetler, Phillip P; Miles, William C; Goff, Jonathon D; Davis, Richey M; Riffle, Judy S, E-mail: stpierre@physics.uwa.edu.au [Macromolecules and Interfaces Institute, Virginia Polytechnic Institute and State University, Blacksburg, VA 24061 (United States)

    2011-08-12

    Iron oxide magnetic nanoparticles are good candidates for magnetic resonance imaging (MRI) contrast agents due to their high magnetic susceptibilities. Here we investigate 19 polyether-coated magnetite nanoparticle systems comprising three series. All systems were synthesized from the same batch of magnetite nanoparticles. A different polyether was used for each series. Each series comprised systems with systematically varied polyether loadings per particle. A highly significant (p < 0.0001) linear correlation (r = 0.956) was found between the proton relaxivity and the intensity-weighted average diameter measured by dynamic light scattering in the 19 particle systems studied. The intensity-weighted average diameter measured by dynamic light scattering is sensitive to small number fractions of larger particles/aggregates. We conclude that the primary effect leading to differences in proton relaxivity between systems arises from the small degree of aggregation within the samples, which appears to be determined by the nature of the polymer and, for one system, the degree of polymer loading of the particles. For the polyether coatings used in this study, any changes in relaxivity from differences in water exclusion or diffusion rates caused by the polymer are minor in comparison with the changes in relaxivity resulting from variations in the degree of aggregation.

  4. Doxorubicin loaded PVA coated iron oxide nanoparticles for targeted drug delivery

    International Nuclear Information System (INIS)

    Kayal, S.; Ramanujan, R.V.

    2010-01-01

    Magnetic drug targeting is a drug delivery system that can be used in locoregional cancer treatment. Coated magnetic particles, called carriers, are very useful for delivering chemotherapeutic drugs. Magnetic carriers were synthesized by coprecipitation of iron oxide followed by coating with polyvinyl alcohol (PVA). Characterization was carried out using X-ray diffraction, TEM, TGA, FTIR and VSM techniques. The magnetic core of the carriers was magnetite (Fe 3 O 4 ), with average size of 10 nm. The room temperature VSM measurements showed that magnetic particles were superparamagnetic. The amount of PVA bound to the iron oxide nanoparticles were estimated by thermogravimetric analysis (TGA) and the attachment of PVA to the iron oxide nanoparticles was confirmed by FTIR analysis. Doxorubicin (DOX) drug loading and release profiles of PVA coated iron oxide nanoparticles showed that up to 45% of adsorbed drug was released in 80 h, the drug release followed the Fickian diffusion-controlled process. The binding of DOX to the PVA was confirmed by FTIR analysis. The present findings show that DOX loaded PVA coated iron oxide nanoparticles are promising for magnetically targeted drug delivery.

  5. Influence of Magnetite Nanoparticles on the Dielectric Properties of Metal Oxide/Polymer Nanocomposites Based on Polypropylene

    Science.gov (United States)

    Maharramov, A. A.; Ramazanov, M. A.; Di Palma, Luca; Shirinova, H. A.; Hajiyeva, F. V.

    2018-01-01

    Structure and dielectric properties of polymer nanocomposites based on isotactic polypropylene and iron oxide (Fe3O4) nanoparticles are studied. Distribution of magnetite nanoparticles in a polymer matrix was studied by scanning electron microscopy (SEM, Carl Zeiss). Dielectric properties of nanocomposites were examined by means of E7-21 impedance spectrometer in the frequency range of 102-106 Hz and temperature interval of 298-433 K. The frequency and temperature dependences of the dielectric permittivity ɛ, as well as the temperature dependence of log (ρ) were constructed. It is shown that introduction of the magnetite (Fe3O4) nanoparticles into a polypropylene matrix increases the dielectric permittivity of nanocomposites. An increase in the dielectric permittivity is explained by the increase in the polarization ability of nanocomposites. It is found that a decrease in the specific resistance with increasing temperature up to 318 K is associated with an increase in the ionic conductivity of nanocomposites. An increase in the resistance at temperatures higher than 358 K is due to the destruction of the crystalline phase of the polymer, as a result of which the distance between the Fe3O4 nanoparticles increases.

  6. Supercritical CO2-Assisted Spray Drying of Strawberry-Like Gold-Coated Magnetite Nanocomposites in Chitosan Powders for Inhalation

    Directory of Open Access Journals (Sweden)

    Marta C. Silva

    2017-01-01

    Full Text Available Lung cancer is one of the leading causes of death worldwide. Therefore, it is of extreme importance to develop new systems that can deliver anticancer drugs into the site of action when initiating a treatment. Recently, the use of nanotechnology and particle engineering has enabled the development of new drug delivery platforms for pulmonary delivery. In this work, POXylated strawberry-like gold-coated magnetite nanocomposites and ibuprofen (IBP were encapsulated into a chitosan matrix using Supercritical Assisted Spray Drying (SASD. The dry powder formulations showed adequate morphology and aerodynamic performances (fine particle fraction 48%–55% and aerodynamic diameter of 2.6–2.8 µm for deep lung deposition through the pulmonary route. Moreover, the release kinetics of IBP was also investigated showing a faster release of the drug at pH 6.8, the pH of lung cancer. POXylated strawberry-like gold-coated magnetite nanocomposites proved to have suitable sizes for cellular internalization and their fluorescent capabilities enable their future use in in vitro cell based assays. As a proof-of-concept, the reported results show that these nano-in-micro formulations could be potential drug vehicles for pulmonary administration.

  7. β-Cyclodextrin/thermosensitive containing polymer brushes grafted onto magnetite nano-particles for extraction and determination of venlafaxine in biological and pharmaceutical samples.

    Science.gov (United States)

    Ahmad Panahi, Homayon; Alaei, Haniyeh Sadat

    2014-12-10

    In this paper, a novel nano-sorbent is fabricated by the surface grafting of poly[β-CD/allylamine-co-N-isopropylacrylamide] onto modified magnetite nano-particles by 3-mercaptopropyltrimethoxysilane. The polymer grafted magnetite nano-particles was characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, elemental analysis, scanning electron microscopy, and transmission electron microscopy. The feasibility of employing this nano-sorbent for extraction of trace venlafaxine in pharmaceutical samples and human biological fluids are investigated. The effect of various parameters such as pH, reaction temperature, and contact time was evaluated. The result revealed that the best sorption of venlafaxine by the magnetite nano-sorbent occurred at 35 °C at an optimum pH of 5. The kinetics of the venlafaxine shows accessibility of active sites in the grafted polymer onto the drug. The equilibrium data of venlafaxine by grafted magnetite nano-sorbent are well represented by the Langmuir and Freundlich isotherm models. The adsorption capacity of venlafaxine is found 142.8 mg g(-1) and indicated the homogeneous sites onto polymer grafted magnetite nano-sorbent surface. Nearly 80% of venlafaxine was released in simulated intestinal fluid, pH 7.4, in 30 h and 90% in simulated gastric fluid, pH 1.2, in 1 h. The venlafaxine loaded-polymer grafted magnetite nano-particles were successfully applied for the extraction in urine and pharmaceutical samples. Copyright © 2014 Elsevier B.V. All rights reserved.

  8. Gold-coated nanoparticles for use in biotechnology applications

    Science.gov (United States)

    Berning, Douglas E [Los Alamos, NM; Kraus, Jr., Robert H.; Atcher, Robert W [Los Alamos, NM; Schmidt, Jurgen G [Los Alamos, NM

    2009-07-07

    A process of preparing gold-coated magnetic nanoparticles is disclosed and includes forming a suspension of magnetic nanoparticles within a suitable liquid, adding an amount of a reducible gold compound and a reducing agent to the suspension, and, maintaining the suspension for time sufficient to form gold-coated magnetic nanoparticles.

  9. Mechanism of in situ surface polymerization of gallic acid in an environmental-inspired preparation of carboxylated core-shell magnetite nanoparticles.

    Science.gov (United States)

    Tóth, Ildikó Y; Szekeres, Márta; Turcu, Rodica; Sáringer, Szilárd; Illés, Erzsébet; Nesztor, Dániel; Tombácz, Etelka

    2014-12-30

    Magnetite nanoparticles (MNPs) with biocompatible coatings are good candidates for MRI (magnetic resonance imaging) contrasting, magnetic hyperthermia treatments, and drug delivery systems. The spontaneous surface induced polymerization of dissolved organic matter on environmental mineral particles inspired us to prepare carboxylated core-shell MNPs by using a ubiquitous polyphenolic precursor. Through the adsorption and in situ surface polymerization of gallic acid (GA), a polygallate (PGA) coating is formed on the nanoparticles (PGA@MNP) with possible antioxidant capacity. The present work explores the mechanism of polymerization with the help of potentiometric acid-base titration, dynamic light scattering (for particle size and zeta potential determination), UV-vis (UV-visible light spectroscopy), FTIR-ATR (Fourier-transformed infrared spectroscopy by attenuated total reflection), and XPS (X-ray photoelectron spectroscopy) techniques. We observed the formation of ester and ether linkages between gallate monomers both in solution and in the adsorbed state. Higher polymers were formed in the course of several weeks both on the surface of nanoparticles and in the dispersion medium. The ratio of the absorbances of PGA supernatants at 400 and 600 nm (i.e., the E4/E6 ratio commonly used to characterize the degree of polymerization of humic materials) was determined to be 4.3, similar to that of humic acids. Combined XPS, dynamic light scattering, and FTIR-ATR results revealed that, prior to polymerization, the GA monomers became oxidized to poly(carboxylic acid)s due to ring opening while Fe(3+) ions reduced to Fe(2+). Our published results on the colloidal and chemical stability of PGA@MNPs are referenced thoroughly in the present work. Detailed studies on biocompatibility, antioxidant property, and biomedical applicability of the particles will be published.

  10. Effects of coating molecules on the magnetic heating properties of Au-Fe3O4 heterodimer nanoparticles

    Science.gov (United States)

    Yamamoto, Y.; Ogasawara, J.; Himukai, H.; Itoh, T.

    2016-10-01

    In this paper, we report the heating properties of gold-magnetite (Au-Fe3O4) heterodimer nanoparticles (NPs) subjected to an alternating magnetic field. The Au-Fe3O4 NPs coated with oleic acid and oleylamine (OA) were synthesized through a method that combines seed mediation and high-temperature decomposition. The coating was replaced with dimercaptosuccinic acid (DMSA) by the ligand-exchange method. The specific absorption rates (SARs) for the OA- and DMSA-coated Au-Fe3O4 NPs coated with OA and DMSA at room temperature were determined through the calorimetric and magnetometric methods. SAR depended on the square of the magnetic field H up to an H value of 4 kA/m. The absolute value of the SAR for DMSA-coated NPs is about fivefold higher than that of the OA-coated NPs. The AC magnetic hysteresis measurements showed the recovery of the magnetic volume and the decrease in the magnetic anisotropy of the DMSA-coated NPs relative to those of the OA-coated NPs. These results suggest that the protective agent influences the magnetic properties of magnetite NPs via gold NPs.

  11. Progress in the synthesis and characterization of magnetite nanoparticles with amino groups on the surface

    International Nuclear Information System (INIS)

    Durdureanu-Angheluta, A.; Dascalu, A.; Fifere, A.; Coroaba, A.; Pricop, L.; Chiriac, H.; Tura, V.; Pinteala, M.; Simionescu, B.C.

    2012-01-01

    This manuscript deals with the synthesis of new hydrophilic magnetite particles by employing a two-step method: in the first step magnetite particles with hydrophobic shell formed in presence of oleic acid–oleylamine complex through a synthesis in mass, without solvent, in a mortar with pestle were obtained; while in the second step the hydrophobic shell was interchanged with an aminosilane monomer. The influence of the Fe 2+ /Fe 3+ molar ratio on the dimension of the particles of high importance for their potential applications was carefully investigated. This paper, also presents an alternative method of synthesis of new core-shell magnetite particles and the complete study of their structure and morphology by FT-IR, XPS, TGA, ESEM and TEM techniques. The rheological properties and magnetization analysis of high importance for magnetic particles were also investigated. - Highlights: ► Magnetite particles are superparamagnetic materials. ► Magnetite has significant role in nanotechnology due to surface properties and applicability in physical and chemical processes. ► We used an ecological method of synthesis, a reaction in mass, without solvent, in a mortar with pestle. ► We prepared hydrophilic magnetite particles, precursors for biomedical applications.

  12. Progress in the synthesis and characterization of magnetite nanoparticles with amino groups on the surface

    Energy Technology Data Exchange (ETDEWEB)

    Durdureanu-Angheluta, A.; Dascalu, A.; Fifere, A.; Coroaba, A.; Pricop, L. [Centre of Advanced Research in Bionanoconjugates and Biopolymers, ' ' Petru Poni' ' Institute of Macromolecular Chemistry of Romanian Academy, 41A Aleea Grigore Ghica Voda, 700487 Iasi (Romania); Chiriac, H. [National Institute of Research and Development in Technical Physics, 700050 Iasi (Romania); Tura, V. [Faculty of Physics, ' ' Al. I. Cuza' ' University, B-dul Carol I, no. 11, 700506 Iasi (Romania); Pinteala, M., E-mail: pinteala@icmpp.ro [Centre of Advanced Research in Bionanoconjugates and Biopolymers, ' ' Petru Poni' ' Institute of Macromolecular Chemistry of Romanian Academy, 41A Aleea Grigore Ghica Voda, 700487 Iasi (Romania); Simionescu, B.C. [Centre of Advanced Research in Bionanoconjugates and Biopolymers, ' ' Petru Poni' ' Institute of Macromolecular Chemistry of Romanian Academy, 41A Aleea Grigore Ghica Voda, 700487 Iasi (Romania); Department of Natural and Synthetic Polymers, ' ' Gh. Asachi' ' Technical University of Iasi, 73 Mangeron Blvd, 700050 Iasi (Romania)

    2012-05-15

    This manuscript deals with the synthesis of new hydrophilic magnetite particles by employing a two-step method: in the first step magnetite particles with hydrophobic shell formed in presence of oleic acid-oleylamine complex through a synthesis in mass, without solvent, in a mortar with pestle were obtained; while in the second step the hydrophobic shell was interchanged with an aminosilane monomer. The influence of the Fe{sup 2+}/Fe{sup 3+} molar ratio on the dimension of the particles of high importance for their potential applications was carefully investigated. This paper, also presents an alternative method of synthesis of new core-shell magnetite particles and the complete study of their structure and morphology by FT-IR, XPS, TGA, ESEM and TEM techniques. The rheological properties and magnetization analysis of high importance for magnetic particles were also investigated. - Highlights: Black-Right-Pointing-Pointer Magnetite particles are superparamagnetic materials. Black-Right-Pointing-Pointer Magnetite has significant role in nanotechnology due to surface properties and applicability in physical and chemical processes. Black-Right-Pointing-Pointer We used an ecological method of synthesis, a reaction in mass, without solvent, in a mortar with pestle. Black-Right-Pointing-Pointer We prepared hydrophilic magnetite particles, precursors for biomedical applications.

  13. Synthesis of nanoparticles of magnetite by sol-gel and precipitation methods: study of chemical composition and structure

    International Nuclear Information System (INIS)

    Picasso, Gino; Vega, Jaime; Uzuriaga, Rosario; Ruiz, Gean Pieer

    2012-01-01

    In this work, nanoparticles based on magnetite have been prepared by sol-gel and precipitation methods. In the first case two variants have been applied: by growing of sol starting from nitrate precursor and ethylene glycol as solvent and to control the reduction process and force hydrolysis and steric control prepared from ferrum sulfate precursor and sodium citrate. In the second case the starting material was sulfate precursor, ammonium hydroxide as precipitaing agent and ethylene glycol as surfactant. The samples have been characterized by X-ray diffraction technique (XRD), adsorption-desorption of N 2 (BET equation model) and Moessbauer spectroscopy. XRD patterns of all samples showed typical peaks of magnetite which were detected in the following positions: 30,06 o , 35,42 o , 62,55 o . Average specific surface quantified by BET method was ranging from 40 to 50 m 2 /g with isotherm type IV corresponding to mesoporous surface. Moessbauer spectra of sample prepared from sol-gel (gel growing) carried out at home temperature detected the presence of 2 sextets consisting in 2 type of sites: first one due to octahedral positions (Fe 2+ , Fe 3+ ) and the second one due to tetrahedral positions (Fe 3+ ). Grain size of magnetite samples, evaluated by Scherrer equation and specific surface area, was ranging from 2 to 20 nm. (author).

  14. A novel method for the functionalization of aminoacids L-glycine, L-glutamic acid and L-arginine on maghemite/magnetite nanoparticles

    Science.gov (United States)

    Bruno, A. J.; Correa, J. R.; Peláez-Abellán, E.; Urones-Garrote, E.

    2018-06-01

    Nanoparticles of maghemite/magnetite functionalized with L-glycine, L-glutamic acid and L-arginine were synthesized by a novel method. The novel procedure consists in an alternative of that reported by Massart for the precipitation of magnetite in which the aminoacid is added in the carboxylate form. The amounts of aminoacid in the initial molar concentrations were 35%, 45% and 65% with respect to the ferrophase. The obtained nanoparticles were characterized by several techniques: X-ray diffraction (XRD), Fourier transform IR spectroscopy (FT-IR), transmission electron microscopy (TEM), Electron energy-loss spectroscopy (EELS) and magnetometry. The IR spectroscopy confirmed that the selected aminoacids were functionalized on the surface of iron oxide. XRD and EELS confirm that iron oxide consists of a maghemite-magnetite intermediate phase with an average particle size about 6 nm, which was measured by transmission electron microscopy. The superparamagnetic character of the nanoparticles was evaluated by magnetometry.

  15. Modified magnetite nanoparticles with cetyltrimethylammonium bromide as superior adsorbent for rapid removal of the disperse dyes from wastewater of textile companies

    Directory of Open Access Journals (Sweden)

    Ali Asghar Rajabi

    2016-01-01

    Full Text Available This paper reports application of cetyltrimethylammonium bromide (CTAB coated magnetite nanoparticles (Fe3O4 NPs as a novel adsorbent for removal of two types of disperse dyes, including disperse red 167, and disperse blue 183, from wastewater of textile companies. The effect of parameters including type of surfactant, pH of solution, surfactant concentration, and amount of salt, was investigated and optimized. The obtained results showed that the ratio of initial dye concentration to CTAB amounts has critical effect on removal processes so that removal efficiencies higher than 95% can be achieved even at high concentration of dyes as high as 500 mg l-1 when the ratio is optimum. Removal of dyes is very fast, and equilibrium is reached at times less than 10 min even for high concentration of the dyes. Very high adsorbent capacity (as high as 2000 mg g-1 was yielded for maximum tested concentration of the dyes (500 mg g-1. The obtained result was confirmed by thermogravimetric analysis data. This study showed that CTAB coated Fe3O4 NPs is a very efficient adsorbent for removal of dyes from wastewater of textile companies and has high capacity under optimum conditions.

  16. Surface-Initiated Atom Transfer Radical Polymerization of Magnetite Nanoparticles with Statistical Poly(tert-butyl acrylate-poly(poly(ethylene glycol methyl ether methacrylate Copolymers

    Directory of Open Access Journals (Sweden)

    Patcharin Kanhakeaw

    2015-01-01

    Full Text Available This work presented the surface modification of magnetite nanoparticle (MNP with poly[(t-butyl acrylate-stat-(poly(ethylene glycol methyl ether methacrylate] copolymers (P[(t-BA-stat-PEGMA] via a surface-initiated “grafting from” atom transfer radical polymerization (ATRP. Loading molar ratio of t-BA to PEGMA was systematically varied (100 : 0, 75 : 25, 50 : 50, and 25 : 75, resp. such that the degree of hydrophilicity of the copolymers, affecting the particle dispersibility in water, can be fine-tuned. The reaction progress in each step of the synthesis was monitored via Fourier transform infrared spectroscopy (FTIR. The studies in the reaction kinetics indicated that PEGMA had higher reactivity than that of t-BA in the copolymerizations. Gel permeation chromatography (GPC indicated that the molecular weights of the copolymers increased with the increase of the monomer conversion. Transmission electron microscopy (TEM revealed that the particles were spherical with averaged size of 8.1 nm in diameter. Dispersibility of the particles in water was apparently improved when the copolymers were coated as compared to P(t-BA homopolymer coating. The percentages of MNP and the copolymer in the composites were determined via thermogravimetric analysis (TGA and their magnetic properties were investigated via vibrating sample magnetometry (VSM.

  17. Tannic acid- and natural organic matter-coated magnetite as green Fenton-like catalysts for the removal of water pollutants

    International Nuclear Information System (INIS)

    Nadejde, C.; Neamtu, M.; Hodoroaba, V.-D.; Schneider, R. J.; Paul, A.; Ababei, G.; Panne, U.

    2015-01-01

    The use of magnetic materials as heterogeneous catalysts has attracted increasing attention in the last years since they proved to be promising candidates for water treatment. In the present study, two types of surface-modified magnetite (Fe 3 O 4 ) nanoparticles, coated with non-hazardous naturally occurring agents—either tannic acid (TA) or dissolved natural organic matter—were evaluated as magnetic heterogeneous catalysts. Chemical synthesis (co-precipitation) was chosen to yield the nanocatalysts due to its well-established simplicity and efficiency. Subsequently, the properties of the final products were fully assessed by various characterization techniques. The catalytic activity in heterogeneous oxidation of aqueous solutions containing a model pollutant, Bisphenol A (BPA), was comparatively studied. The effect of operational parameters (catalyst loading, H 2 O 2 dosage, and UV light irradiation) on the degradation performance of the oxidation process was investigated. The optimum experimental parameters were found to be 1.0 g/L of catalysts and 10 mM H 2 O 2 , under UV irradiation. The highest mineralization rates were observed for Fe 3 O 4 -TA catalyst. More than 80 % of BPA was removed after 30 min of reaction time under the specified experimental conditions. The obtained results showed that the two catalysts studied here are suitable candidates for the removal of pollutants in wastewaters by means of heterogeneous reaction using a green sustainable treatment method

  18. Synthesis and characterization of water-dispersible core/shell Mn-doped magnetite/Au nanoparticles for proton radiotherapy

    International Nuclear Information System (INIS)

    Park, Jeong Chan

    2015-01-01

    The surface modification of the nanomaterials is required for the biomedical use to give physiological stability, surface reactivity and targeting properties. Among many approaches for the surface modification with materials, such as polymers, organic ligands and metals, one of the most attractive ways is to employ metals. The fabrication of metal-based, monolayer coated magnetic nanoparticles has been intensively studied. However, the synthesis of metal-capped magnetic nanoparticles with monodispersities and controllable sizes is still challenged. Recently, gold-capped magnetic nanoparticles have been reported to increase stability and to provide biocompatibility. Gold-coated magnetic nanoparticles are an attractive system, which can be stabilized in biological conditions and readily functionalized through well-established surface modification chemistry. In addition, the Au coating offers plasmonic properties to magnetic nanoparticles. This makes the magnetic/Au core/shell combinations interesting for magnetic and optical applications. The monodisperse Mn:Fe3O4/Au nanoparticles have been prepared in organic solvent first and then transferred from an organic phase to an aqueous solution. The resulting core/shell-structured nanoparticles may be an attractive system for biomedical applications, which are needed both magnetic resonance imaging and optical imaging. In addition, the resulting nanoparticles may be useful for proton radiotherapy due to the enhanced therapeutic effects of secondary radiation stemmed from gold and proton beam bombardment

  19. Quantitation of Surface Coating on Nanoparticles Using Thermogravimetric Analysis.

    Science.gov (United States)

    Dongargaonkar, Alpana A; Clogston, Jeffrey D

    2018-01-01

    Nanoparticles are critical components in nanomedicine and nanotherapeutic applications. Some nanoparticles, such as metallic nanoparticles, consist of a surface coating or surface modification to aid in its dispersion and stability. This surface coating may affect the behavior of nanoparticles in a biological environment, thus it is important to measure. Thermogravimetric analysis (TGA) can be used to determine the amount of coating on the surface of the nanoparticle. TGA experiments run under inert atmosphere can also be used to determine residual metal content present in the sample. In this chapter, the TGA technique and experimental method are described.

  20. Magneto-electro-responsive material based on magnetite nanoparticles/polyurethane composites

    Energy Technology Data Exchange (ETDEWEB)

    Petcharoen, Karat; Sirivat, Anuvat, E-mail: anuvat.s@chula.ac.th

    2016-04-01

    Multi-functional materials in actuator applications have been developed toward reversibility and sensitivity under various actuating fields. In this work, magneto-electro-responsive materials consisting of a polyurethane (PU) matrix and its composites embedded with magnetite nanoparticles (MNP) as a dispersed phase were fabricated to tailor the electromechanical properties and bending performance under electric, magnetic, and electromagnetic fields. Due to the superior characteristics of MNP over other magnetic materials, the composites fabricated with electronic polarization were highly responsive under electric field. The highest storage modulus sensitivity belonged to the 1.0% v/v MNP/PU composite which possessed the value of 3.46 at the electric field 2 kV mm{sup −1}. Moreover, all of the PU composites behaved as an electrostrictive material in which the stress depended quadratically on the electric field. It was demonstrated that the PU composites also possessed very good recoverability, fast response (< 15 s) and large bending angle relative to that of pristine PU under applied electric field. Interestingly, the steady state storage modulus response was attained within the first electrical actuation cycle and the PU composite was a fully reversible material. In addition, it was shown that superparamagnetism was a common characteristic of all fabricated composites under magnetic field. The 3.0%v/v MNP/PU composite provided the largest bending distance up to 23.60 mm, and 14.10 mm under the magnetic field of 5000 G, and the electromagnetic field of 320 G, respectively. In summary, the MNP/PU composite material is a potential candidate to be used as a smart material under the influences of electric and/or magnetic fields over other existing dielectric materials. - Highlights: • MNP/PU composites exhibit a superparamagnetic behavior. • MNP/PU composites show full reversibility under electric field. • 1.0% v/v MNP/PU composite provides the highest

  1. Magneto-electro-responsive material based on magnetite nanoparticles/polyurethane composites

    International Nuclear Information System (INIS)

    Petcharoen, Karat; Sirivat, Anuvat

    2016-01-01

    Multi-functional materials in actuator applications have been developed toward reversibility and sensitivity under various actuating fields. In this work, magneto-electro-responsive materials consisting of a polyurethane (PU) matrix and its composites embedded with magnetite nanoparticles (MNP) as a dispersed phase were fabricated to tailor the electromechanical properties and bending performance under electric, magnetic, and electromagnetic fields. Due to the superior characteristics of MNP over other magnetic materials, the composites fabricated with electronic polarization were highly responsive under electric field. The highest storage modulus sensitivity belonged to the 1.0% v/v MNP/PU composite which possessed the value of 3.46 at the electric field 2 kV mm"−"1. Moreover, all of the PU composites behaved as an electrostrictive material in which the stress depended quadratically on the electric field. It was demonstrated that the PU composites also possessed very good recoverability, fast response (< 15 s) and large bending angle relative to that of pristine PU under applied electric field. Interestingly, the steady state storage modulus response was attained within the first electrical actuation cycle and the PU composite was a fully reversible material. In addition, it was shown that superparamagnetism was a common characteristic of all fabricated composites under magnetic field. The 3.0%v/v MNP/PU composite provided the largest bending distance up to 23.60 mm, and 14.10 mm under the magnetic field of 5000 G, and the electromagnetic field of 320 G, respectively. In summary, the MNP/PU composite material is a potential candidate to be used as a smart material under the influences of electric and/or magnetic fields over other existing dielectric materials. - Highlights: • MNP/PU composites exhibit a superparamagnetic behavior. • MNP/PU composites show full reversibility under electric field. • 1.0% v/v MNP/PU composite provides the highest sensitivity

  2. Experimental Investigation of the Coprecipitation Method: An Approach to Obtain Magnetite and Maghemite Nanoparticles with Improved Properties

    Directory of Open Access Journals (Sweden)

    Wilson Sacchi Peternele

    2014-01-01

    Full Text Available Iron oxides that exhibit magnetic properties have been widely studied not only from an academic standpoint, but also for numerous applications in different fields of knowledge, such as biomedical and technological research. In this work, magnetite and maghemite nanoparticles were synthesized by chemical coprecipitation of FeCl2·4H2O and FeCl3·6H2O (proportion of 1 : 2 in three different cases using two bases (sodium hydroxide and hydroxide ammonium as precipitants. The chemical coprecipitation method was selected for its simplicity, convenience, reproducibility, and low cost in the use of glassware. The nanostructured materials were characterized by transmission electron microscopy (TEM, X-ray diffraction (XRD and magnetometry (VSM. The objective of this work is to study the variation in the morphological characteristics and physical properties of nanoparticles magnetic as a function of the different production processes. As observed by TEM, the materials obtained from the precipitating agent NH4OH are more uniform than those obtained with NaOH. From XRD pattern analysis, it appears that the obtained materials correspond to magnetite and maghemite and, from magnetometry VSM analysis, show high magnetization as a function of the magnetic field at room temperature, indicating that these materials are superparamagnetic.

  3. Synthesis and characterization of dextran-coated iron oxide nanoparticles

    Science.gov (United States)

    Predescu, Andra Mihaela; Matei, Ecaterina; Berbecaru, Andrei Constantin; Pantilimon, Cristian; Drăgan, Claudia; Vidu, Ruxandra; Predescu, Cristian; Kuncser, Victor

    2018-03-01

    Synthesis and characterization of iron oxide nanoparticles coated with a large molar weight dextran for environmental applications are reported. The first experiments involved the synthesis of iron oxide nanoparticles which were coated with dextran at different concentrations. The synthesis was performed by a co-precipitation technique, while the coating of iron oxide nanoparticles was carried out in solution. The obtained nanoparticles were characterized by using scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction spectrometry, Fourier transform infrared spectroscopy and superconducting quantum interference device magnetometry. The results demonstrated a successful coating of iron oxide nanoparticles with large molar weight dextran, of which agglomeration tendency depended on the amount of dextran in the coating solution. SEM and TEM observations have shown that the iron oxide nanoparticles are of about 7 nm in size.

  4. Progress in the synthesis and characterization of magnetite nanoparticles with amino groups on the surface

    Science.gov (United States)

    Durdureanu-Angheluta, A.; Dascalu, A.; Fifere, A.; Coroaba, A.; Pricop, L.; Chiriac, H.; Tura, V.; Pinteala, M.; Simionescu, B. C.

    2012-05-01

    This manuscript deals with the synthesis of new hydrophilic magnetite particles by employing a two-step method: in the first step magnetite particles with hydrophobic shell formed in presence of oleic acid-oleylamine complex through a synthesis in mass, without solvent, in a mortar with pestle were obtained; while in the second step the hydrophobic shell was interchanged with an aminosilane monomer. The influence of the Fe2+/Fe3+ molar ratio on the dimension of the particles of high importance for their potential applications was carefully investigated. This paper, also presents an alternative method of synthesis of new core-shell magnetite particles and the complete study of their structure and morphology by FT-IR, XPS, TGA, ESEM and TEM techniques. The rheological properties and magnetization analysis of high importance for magnetic particles were also investigated.

  5. Novel methods for the synthesis of magnetite nanoparticles with special morphologies and textured assemblages

    Energy Technology Data Exchange (ETDEWEB)

    Nyiro-Kosa, Ilona, E-mail: kosaili@gmail.com [University of Pannonia, Department of Material Engineering (Hungary); Recnik, Aleksander [Jozef Stefan Institute, Department for Nanostructured Materials (Slovenia); Posfai, Mihaly [University of Pannonia, Department of Earth and Environmental Sciences (Hungary)

    2012-10-15

    There is an increasing technological demand for magnetic nanocrystals with special morphologies and controlled sizes. Several approaches are used for the synthesis of magnetite crystals with irregular or octahedral shapes; however, the room-temperature synthesis of nanocrystals with specific morphologies is not yet established. Here, we describe the synthesis of magnetite crystals (100-300 nm) at a relatively low temperature ({approx}70 Degree-Sign C) from organic precursors, including Fe(II) oxalate or Fe(II) sulfate, and study the effects of ethylene glycol and tetraethylene glycol on the final physical and chemical properties of the crystals. The magnetite crystals formed from different precursor materials (sulfate or oxalate green rust) show specific morphological and textural features. We show that octahedral magnetite crystals can be produced from Fe(II) oxalate via a simple co-precipitation process. Using different kinds and amounts of polyols, various types of particle morphologies and nanocrystal textures can be produced, including hexagonal-shaped clusters of elongated crystals and porous and solid, large, rounded polycrystalline aggregates.

  6. Novel methods for the synthesis of magnetite nanoparticles with special morphologies and textured assemblages

    International Nuclear Information System (INIS)

    Nyirő-Kósa, Ilona; Rečnik, Aleksander; Pósfai, Mihály

    2012-01-01

    There is an increasing technological demand for magnetic nanocrystals with special morphologies and controlled sizes. Several approaches are used for the synthesis of magnetite crystals with irregular or octahedral shapes; however, the room-temperature synthesis of nanocrystals with specific morphologies is not yet established. Here, we describe the synthesis of magnetite crystals (100–300 nm) at a relatively low temperature (∼70 °C) from organic precursors, including Fe(II) oxalate or Fe(II) sulfate, and study the effects of ethylene glycol and tetraethylene glycol on the final physical and chemical properties of the crystals. The magnetite crystals formed from different precursor materials (sulfate or oxalate green rust) show specific morphological and textural features. We show that octahedral magnetite crystals can be produced from Fe(II) oxalate via a simple co-precipitation process. Using different kinds and amounts of polyols, various types of particle morphologies and nanocrystal textures can be produced, including hexagonal-shaped clusters of elongated crystals and porous and solid, large, rounded polycrystalline aggregates.

  7. Highly efficient removal of arsenic metal ions with high superficial area hollow magnetite nanoparticles synthetized by AACVD method

    Energy Technology Data Exchange (ETDEWEB)

    Monárrez-Cordero, B.; Amézaga-Madrid, P.; Antúnez-Flores, W.; Leyva-Porras, C.; Pizá-Ruiz, P. [Centro de Investigación en Materiales Avanzados S.C., and Laboratorio Nacional de Nanotecnología, Miguel de Cervantes 120, Chihuahua, Chih. C.P. 31109 (Mexico); Miki-Yoshida, M., E-mail: mario.miki@cimav.edu.mx [Centro de Investigación en Materiales Avanzados S.C., and Laboratorio Nacional de Nanotecnología, Miguel de Cervantes 120, Chihuahua, Chih. C.P. 31109 (Mexico)

    2014-02-15

    Highlights: ► Fast and high arsenic removal efficiency, almost 100% in one minute. ► Successful synthesis of high purity magnetite hollow nanoparticles is reported. ► They were synthesized by one step aerosol assisted CVD technique. ► Detailed microstructural characterization by electron microscopy was performed. -- Abstract: New nanotechnology alternatives and methodologies have been developed in order to overcome the limitations of conventional techniques for metal ions removal from water. Currently, the removal of heavy metals requires multiple steps which include the separation and post-treatment of the generated sludge. Usually, this sludge is composed of dangerous environmental pollutants mixed with the material used for removing the metal ion. Thus, the removal of these metals becomes a challenging task. Herein we report the synthesis of magnetite nanoparticles with high specific area by the aerosol assisted chemical vapour deposition method. Deposition temperature were fixed at 450 °C and a mixture of Ar–air were used as a carrier gas, a flow of 1.0 and 0.015 L min{sup −1} were used for Ar and air, respectively. The precursor solution was a dilution of Fe (II) chloride in methanol, with different concentration 0.01, 0.05 and 0.1 mol dm{sup −3}. The crystalline structure of the nanoparticles was characterized by grazing incidence X-ray diffraction. Morphology and microstructure were analyzed by field emission scanning electron microscopy, scanning probe microscopy and transmission electron microscopy. Magnetic properties were evaluated with a vibrating sample magnetometer and specific area was measured by the Brunauer–Emmett–Teller method. To determine the removal efficiency of arsenic ion from water, several tests were carried out at six exposition times 1, 3, 5, 10, 20 and 30 min. Results showed high removal efficiency, more than 99%, in less than 1 min.

  8. Thermally stable silica-coated hydrophobic gold nanoparticles.

    Science.gov (United States)

    Kanehara, Masayuki; Watanabe, Yuka; Teranishi, Toshiharu

    2009-01-01

    We have successfully developed a method for silica coating on hydrophobic dodecanethiol-protected Au nanoparticles with coating thickness ranging from 10 to 40 nm. The formation of silica-coated Au nanoparticles could be accomplished via the preparation of hydrophilic Au nanoparticle micelles by cationic surfactant encapsulation in aqueous phase, followed by hydrolysis of tetraethylorthosilicate on the hydrophilic surface of gold nanoparticle micelles. Silica-coated Au nanoparticles exhibited quite high thermal stability, that is, no agglomeration of the Au cores could be observed after annealing at 600 degrees C for 30 min. Silica-coated Au nanoparticles could serve as a template to derive hollow nanoparticles. An addition of NaCN solution to silica-coated Au nanoparticles led the formation of hollow silica nanoparticles, which were redispersible in deionized water. The formation of the hollow silica nanoparticles results from the mesoporous structures of the silica shell and such a mesoporous structure is applicable to both catalyst support and drug delivery.

  9. Magnetic solid-phase extraction based on mesoporous silica-coated magnetic nanoparticles for analysis of oral antidiabetic drugs in human plasma

    Energy Technology Data Exchange (ETDEWEB)

    Souza, Karynne Cristina de; Andrade, Gracielle Ferreira [Centro de Desenvolvimento da Tecnologia Nuclear, CDTN/CNEN, Rua Professor Mário Werneck, s/n. Campus Universitário, Belo Horizonte, MG CEP 30.123-970 (Brazil); Vasconcelos, Ingrid; Oliveira Viana, Iara Maíra de; Fernandes, Christian [Departamento de Produtos Farmacêuticos, Faculdade de Farmácia, Universidade Federal de Minas Gerais, Belo Horizonte, MG (Brazil); Martins Barros de Sousa, Edésia, E-mail: sousaem@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear, CDTN/CNEN, Rua Professor Mário Werneck, s/n. Campus Universitário, Belo Horizonte, MG CEP 30.123-970 (Brazil)

    2014-07-01

    In the present work, magnetic nanoparticles embedded into mesoporous silica were prepared in two steps: first, magnetite was synthesized by oxidation–precipitation method, and next, the magnetic nanoparticles were coated with mesoporous silica by using nonionic block copolymer surfactants as structure-directing agents. The mesoporous SiO{sub 2}-coated Fe{sub 3}O{sub 4} samples were functionalized using octadecyltrimethoxysilane as silanizing agent. The pure and functionalized silica nanoparticles were physicochemically and morphologically characterized by X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), N{sub 2} adsorption, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The resultant magnetic silica nanoparticles were applied as sorbents for magnetic solid-phase extraction (MSPE) of oral antidiabetic drugs in human plasma. Our results revealed that the magnetite nanoparticles were completely coated by well-ordered mesoporous silica with free pores and stable pore walls, and that the structural and magnetic properties of the Fe{sub 3}O{sub 4} nanoparticles were preserved in the applied synthesis route. Indeed, the sorbent material was capable of extracting the antidiabetic drugs from human plasma, being useful for the sample preparation in biological matrices. - Highlights: • SBA-15/Fe{sub 3}O{sub 4} was synthesized and functionalized with octadecyltrimethoxysilane. • Magnetite nanoparticles were completely coated by well-ordered mesoporous silica. • The samples were used as sorbent for magnetic solid-phase extraction (MSPE). • The sorbent material was capable of extracting drugs from human plasma. • The extraction ability makes the material a candidate to be employed as MSPE.

  10. Corrosion Prevention of Aluminum Nanoparticles by a Polyurethane Coating.

    Science.gov (United States)

    Nishimura, Toshiyasu; Raman, Vedarajan

    2014-06-19

    In order to prevent corrosion, aluminum nanoparticles were coated with a polyurethane polymer. The coverage of the polyurethane polymer was controlled from 0 to 100%, which changed the corrosion rate of the nanoparticles quantitatively. The surface of the polymer coating was investigated by Transmission Electron Microscopy (TEM) and Atomic Force Microscopy (AFM), and the corrosion resistance of the nanoparticles was estimated by a wet/dry corrosion test on a Pt plate with a NaCl solution. From a TEM with EDAX analysis, the 10 mass% polymer coated Al particles in the synthesis were almost 100% covered on the surface by a polymer film of 10 nm thick. On the other hand, the 3 mass% polymer coated Al was almost 40% covered by a film. In the AFM, the potential around the Al particles had a relatively low value with the polymer coating, which indicated that the conductivity of the Al was isolated from the Pt plate by the polymer. Both the corrosion and H₂ evolution reaction rates were quantitatively reduced by the mass% of polymer coating. In the case of the 10 mass% coated sample, there was no corrosion of Al nanoparticles. This fact suggested that the electrochemical reaction was suppressed by the polymer coating. Moreover, the reaction rate of Al nanoparticles was suppressed in proportion to the coverage percentage of the coating. Thus, to conclude, it was found that the corrosion rate of Al nanoparticles could be quantitatively suppressed by the coverage percentage of the polymer coating.

  11. Separation/Preconcentration and Speciation Analysis of Trace Amounts of Arsenate and Arsenite in Water Samples Using Modified Magnetite Nanoparticles and Molybdenum Blue Method

    Directory of Open Access Journals (Sweden)

    Mohammad Ali Karimi

    2014-01-01

    Full Text Available A new, simple, and fast method for the separation/preconcentration and speciation analysis of arsenate and arsenite ions using cetyltrimethyl ammonium bromide immobilized on alumina-coated magnetite nanoparticles (CTAB@ACMNPs followed by molybdenum blue method is proposed. The method is based on the adsorption of arsenate on CTAB@ACMNPs. Total arsenic in different samples was determined as As(V after oxidation of As(III to As(V using potassium permanganate. The arsenic concentration has been determined by UV-Visible spectrometric technique based on molybdenum blue method and amount of As(III was calculated by subtracting the concentration of As(V from total arsenic concentration. MNPs and ACMNPs were characterized by VSM, XRD, SEM, and FT-IR spectroscopy. Under the optimal experimental conditions, the preconcentration factor, detection limit, linear range, and relative standard deviation (RSD of arsenate were 175 (for 350 mL of sample solution, 0.028 μg mL−1, 0.090–4.0 μg mL−1, and 2.8% (for 2.0 μg mL−1, n=7, respectively. This method avoided the time-consuming column-passing process of loading large volume samples in traditional SPE through the rapid isolation of CTAB@ACMNPs with an adscititious magnet. The proposed method was successfully applied to the determination and speciation of arsenic in different water samples and suitable recoveries were obtained.

  12. Influence of synthesis experimental parameters on the formation of nanoparticles of magnetite prepared by thermal decomposition method

    International Nuclear Information System (INIS)

    Vega, Jaime; Picasso, Gino; Lopez, Alcides; Aviles Felix, Luis

    2013-01-01

    In this work, nanoparticles based on magnetite have been synthesized by thermal decomposition via solvent-controlled synthesis in polyols, using triethylene glycol (TREG). The starting precursor were solutions of nitrate and acetylacetonate of Fe. The samples have been characterized by X-ray diffraction technique (XRD), adsorption-desorption of N 2 (BET equation model), scanning electronic microscopy (SEM), thermogravimetric analysis (TGA), vibration sample magnetometry (VSM) and Moessbauer spectroscopy. XRD diffractogram revealed the majority presence of spinel-like structural phases of magnetite in all samples. SEM micrographs showed morphological differences; the samples prepared from acetylacetonate presented good dispersion of particles whereas the ones prepared from nitrate-small agglomerations. BET isotherms of samples depicted a mesoporous profile which corresponded to IV type. TGA thermogram showed two defined regions which corresponded to vaporization of polyol light fractions and TREG. Zero coercivity on the magnetization curve of acetylacetonate precursor samples have been observed by VSM, which indicates superparamagnetic behavior. Moessbauer spectra of samples detected the presence of 4 doublet-like subspectra due to the presence of 4 sites occupied by Fe in paramagnetic or superparamagnetic state. (author)

  13. Definitive identification of magnetite nanoparticles in the abdomen of the honeybee Apis mellifera

    Energy Technology Data Exchange (ETDEWEB)

    Desoil, M [Biological Physics Department, University of Mons-Hainaut (Belgium); Gillis, P [Biological Physics Department, University of Mons-Hainaut (Belgium); Gossuin, Y [Biological Physics Department, University of Mons-Hainaut (Belgium); Pankhurst, Q A [London Centre for Nanotechnology, University College London, London WC1E 7HN (United Kingdom); Hautot, D [London Centre for Nanotechnology, University College London, London WC1E 7HN (United Kingdom); Institute for Science and Technology in Medicine, Keele University, Thornburrow Drive, Hartshill, Stoke-en-Trent, ST4 7QB (United Kingdom)

    2005-01-01

    The biogenic magnetic properties of the honeybee Apis mellifera were investigated with a view to understanding the bee's physiological response to magnetic fields. The magnetisations of bee abdomens on one hand, and heads and thoraxes on the other hand, were measured separately as functions of temperature and field. Both the antiferromagnetic responses of the ferrihydrite cores of the iron storage protein ferritin, and the ferrimagnetic responses of nanoscale magnetite (Fe{sub 3}O{sub 4}) particles, were observed. Relatively large magnetite particles (ca. 30 nm or more), capable of retaining a remanent magnetisation at room temperature, were found in the abdomens, but were absent in the heads and thoraxes. In both samples, more than 98% of the iron atoms were due to ferritin.

  14. Definitive identification of magnetite nanoparticles in the abdomen of the honeybee Apis mellifera

    Science.gov (United States)

    Desoil, M.; Gillis, P.; Gossuin, Y.; Pankhurst, Q. A.; Hautot, D.

    2005-01-01

    The biogenic magnetic properties of the honeybee Apis mellifera were investigated with a view to understanding the bee's physiological response to magnetic fields. The magnetisations of bee abdomens on one hand, and heads and thoraxes on the other hand, were measured separately as functions of temperature and field. Both the antiferromagnetic responses of the ferrihydrite cores of the iron storage protein ferritin, and the ferrimagnetic responses of nanoscale magnetite (Fe3O4) particles, were observed. Relatively large magnetite particles (ca. 30 nm or more), capable of retaining a remanent magnetisation at room temperature, were found in the abdomens, but were absent in the heads and thoraxes. In both samples, more than 98% of the iron atoms were due to ferritin.

  15. Definitive identification of magnetite nanoparticles in the abdomen of the honeybee Apis mellifera

    International Nuclear Information System (INIS)

    Desoil, M; Gillis, P; Gossuin, Y; Pankhurst, Q A; Hautot, D

    2005-01-01

    The biogenic magnetic properties of the honeybee Apis mellifera were investigated with a view to understanding the bee's physiological response to magnetic fields. The magnetisations of bee abdomens on one hand, and heads and thoraxes on the other hand, were measured separately as functions of temperature and field. Both the antiferromagnetic responses of the ferrihydrite cores of the iron storage protein ferritin, and the ferrimagnetic responses of nanoscale magnetite (Fe 3 O 4 ) particles, were observed. Relatively large magnetite particles (ca. 30 nm or more), capable of retaining a remanent magnetisation at room temperature, were found in the abdomens, but were absent in the heads and thoraxes. In both samples, more than 98% of the iron atoms were due to ferritin

  16. Silane-coated magnetic nanoparticles with surface thiol functions for conjugation with gold nanostars

    KAUST Repository

    Pallavicini, Piersandro

    2015-11-10

    Small (d ∼ 8 nm) magnetite nanoparticles, FeONP, are prepared and coated with mercaptopropyl trimethoxysilane (MPTS) to form FeONP@MPTS. In the coating step controlled MPTS/FeONP molar ratios are used, ranging from 1 to 7.8 × 10. The total quantity of MPTS per FeONP is determined by SEM-EDS analysis and the average number of free, reactive -SH groups per FeONP is calculated by a colorimetric method. At very low molar ratios MPTS forms a submonolayer on the FeONP surface with all -SH free to react, while on increasing the MPTS/FeONP molar ratio the (CHO)Si- groups of MPTS polymerize, forming a progressively thicker shell, in which only a small fraction of the -SH groups, positioned on the shell surface, is available for further reaction. The MPTS shell reduces the magnetic interactions occurring between the magnetite cores, lowering the occurrence and strength of collective magnetic states, with FeONP@MPTS showing the typical behaviour expected for a sample with a mono-modal size distribution of superparamagnetic nanoparticles. Interaction of FeONP@MPTS with gold nanostars (GNS) was tested, using both FeONP@MPTS with a MPTS submonolayer and with increasing shell thickness. Provided that a good balance is used between the number of available -SH and the overall size of FeONP@MPTS, the free thiols of such nanoparticles bind GNS decorating their surface, as shown by UV-Vis spectroscopy and TEM imaging.

  17. Synthesis and surface modification of hydrophobic magnetite to processible magnetite at silica-propylamine

    Energy Technology Data Exchange (ETDEWEB)

    Woo, Kyoungja [Korea Institute of Science and Technology, Nanomaterials Research Center, P.O. Box 131, Cheongryang, Seoul 130-650 (Korea, Republic of)]. E-mail: kjwoo@kist.re.kr; Hong, Jangwon [Korea Institute of Science and Technology, Nanomaterials Research Center, P.O. Box 131, Cheongryang, Seoul 130-650 (Korea, Republic of); Ahn, Jae-Pyoung [Korea Institute of Science and Technology, Nanomaterials Research Center, P.O. Box 131, Cheongryang, Seoul 130-650 (Korea, Republic of)

    2005-05-15

    Hydrophobic magnetite nanoparticles with a narrow size distribution were prepared by thermal decomposition of Fe(CO){sub 5} in octyl ether solution of oleic acid and by consecutive aeration. The nanoparticles were converted into magnetite core/silica shell (magnetite at silica) structured particles with hydrophilic and processible aminopropyl groups on their surfaces.

  18. The Effect of Vacuum Annealing of Magnetite and Zero-Valent Iron Nanoparticles on the Removal of Aqueous Uranium

    Directory of Open Access Journals (Sweden)

    R. A. Crane

    2013-01-01

    Full Text Available As-formed and vacuum annealed zero-valent iron nanoparticles (nano-Fe0 and magnetite nanoparticles (nano-Fe3O4 were tested for the removal of uranium from carbonate-rich mine water. Nanoparticles were introduced to batch systems containing the mine water under oxygen conditions representative of near-surface waters, with a uranyl solution studied as a simple comparator system. Despite the vacuum annealed nano-Fe0 having a 64.6% lower surface area than the standard nano-Fe0, similar U removal (>98% was recorded during the initial stages of reaction with the mine water. In contrast, ≤15% U removal was recorded for the mine water treated with both as-formed and vacuum annealed nano-Fe3O4. Over extended reaction periods (>1 week, appreciable U rerelease was recorded for the mine water solutions treated using nano-Fe0, whilst the vacuum annealed material maintained U at <50 μg L−1 until 4 weeks reaction. XPS analysis of reacted nanoparticulate solids confirmed the partial chemical reduction of UVI to UIV in both nano-Fe0 water treatment systems, but with a greater amount of UIV detected on the vacuum annealed particles. Results suggest that vacuum annealing can enhance the aqueous reactivity of nano-Fe0 and, for waters of complex chemistry, can improve the longevity of aqueous U removal.

  19. Cellular uptake of magnetite nanoparticles enhanced by NdFeB magnets in staggered arrangement

    Science.gov (United States)

    Lu, Yi-Ching; Chang, Fan-Yu; Tu, Shu-Ju; Chen, Jyh-Ping; Ma, Yunn-Hwa

    2017-04-01

    Magnetic force may greatly enhance uptake of magnetic nanoparticles (MNPs) by cultured cells; however, the effects of non-uniformity of magnetic field/ magnetic gradient on MNP internalization in culture has not been elucidated. Cellular uptake of polyacrylic acid coated-MNP by LN229 cells was measured with cylindrical NdFeB magnets arranged in a staggered pattern. The magnetic field generated by placing a magnet underneath (H-field) elicited a homogenous distribution of MNPs on the cells in culture; whereas the field without magnet underneath (L-field) resulted in MNP distribution along the edge of the wells. Cell-associated MNP (MNPcell) appeared to be magnetic field- and concentration-dependent. In H-field, MNPcell reached plateau within one hour of exposure to MNP with only one-min application of the magnetic force in the beginning of incubation; continuous presence of the magnet for 2 h did not further increase MNPcell, suggesting that magnetic force-induced uptake may be primarily contributed to enhanced MNP sedimentation. Although MNP distribution was much inhomogeneous in L-field, averaged MNPcell in the L-field may reach as high as 80% of that in H-field during 1-6 h incubation, suggesting high capacity of MNP internalization. In addition, no significant difference was observed in MNPcell analyzed by flow cytometry with the application of H-field of staggered plate vs. filled magnet plate. Therefore, biological variation may dominate MNP internalization even under relatively uniformed magnetic field; whereas non-uniformed magnetic field may serve as a model for tumor targeting with MNPs in vivo.

  20. Tannic acid- and natural organic matter-coated magnetite as green Fenton-like catalysts for the removal of water pollutants

    Energy Technology Data Exchange (ETDEWEB)

    Nadejde, C., E-mail: claudianadejde@gmail.com; Neamtu, M., E-mail: mariana.neamtu@uaic.ro [‘Alexandru Ioan Cuza’ University, Interdisciplinary Research Department – Field Science (Romania); Hodoroaba, V.-D.; Schneider, R. J.; Paul, A. [BAM Federal Institute for Materials Research and Testing (Germany); Ababei, G. [National Institute of Research and Development for Technical Physics (Romania); Panne, U. [BAM Federal Institute for Materials Research and Testing (Germany)

    2015-12-15

    The use of magnetic materials as heterogeneous catalysts has attracted increasing attention in the last years since they proved to be promising candidates for water treatment. In the present study, two types of surface-modified magnetite (Fe{sub 3}O{sub 4}) nanoparticles, coated with non-hazardous naturally occurring agents—either tannic acid (TA) or dissolved natural organic matter—were evaluated as magnetic heterogeneous catalysts. Chemical synthesis (co-precipitation) was chosen to yield the nanocatalysts due to its well-established simplicity and efficiency. Subsequently, the properties of the final products were fully assessed by various characterization techniques. The catalytic activity in heterogeneous oxidation of aqueous solutions containing a model pollutant, Bisphenol A (BPA), was comparatively studied. The effect of operational parameters (catalyst loading, H{sub 2}O{sub 2} dosage, and UV light irradiation) on the degradation performance of the oxidation process was investigated. The optimum experimental parameters were found to be 1.0 g/L of catalysts and 10 mM H{sub 2}O{sub 2}, under UV irradiation. The highest mineralization rates were observed for Fe{sub 3}O{sub 4}-TA catalyst. More than 80 % of BPA was removed after 30 min of reaction time under the specified experimental conditions. The obtained results showed that the two catalysts studied here are suitable candidates for the removal of pollutants in wastewaters by means of heterogeneous reaction using a green sustainable treatment method.

  1. A nanocomposite consisting of silica-coated magnetite and phenyl-functionalized graphene oxide for extraction of polycyclic aromatic hydrocarbon from aqueous matrices.

    Science.gov (United States)

    Mahpishanian, Shokouh; Sereshti, Hassan; Ahmadvand, Mohammad

    2017-05-01

    In this study, graphene oxide was covalently immobilized on silica-coated magnetite and then modified with 2-phenylethylamine to give a nanocomposite of type Fe 3 O 4 @SiO 2 @GO-PEA that can be applied to the magnetic solid-phase extraction of polycyclic aromatic hydrocarbons (PAHs) from water samples. The resulting microspheres (Fe 3 O 4 @SiO 2 @GO-PEA) were characterized by Fourier transform-infrared spectroscopy (FT-IR), scanning electron microscopy (SEM), CHNS elemental analysis, and vibrating sample magnetometry (VSM) techniques. The adsorbent possesses the magnetic properties of Fe 3 O 4 nanoparticles that allow them easily to be separated by an external magnetic field. They also have the high specific surface area of graphene oxide which improves adsorption capacity. Desorption conditions, extraction time, amount of adsorbent, salt concentration, and pH were investigated and optimized. Following desorption, the PAHs were quantified by gas chromatography with flame ionization detection (GC-FID). The limits of detection (at an S/N ratio of 3) were achieved from 0.005 to 0.1μg/L with regression coefficients (R 2 ) higher than 0.9954. The relative standard deviations (RSDs) were below 5.8% (intraday) and 6.2% (inter-day), respectively. The method was successfully applied to the analysis of PAHs in environmental water samples where it showed recoveries in the range between 71.7% and 106.7% (with RSDs of 1.6% to 8.4%, for n=3). The results indicated that the Fe 3 O 4 @SiO 2 @GO-PEA microspheres had a great promise to extraction of PAHs from different water samples. Copyright © 2016. Published by Elsevier B.V.

  2. Synthesis, characterization and magnetic property of maghemite (γ-Fe{sub 2}O{sub 3}) nanoparticles and their protective coating with pepsin for bio-functionalization

    Energy Technology Data Exchange (ETDEWEB)

    Bandhu, A.; Sutradhar, S.; Mukherjee, S. [Solid State Research Laboratory, Department of Physics, Burdwan University, Burdwan 713104, West Bengal (India); Greneche, J.M. [Laboratoire de Physique de l’Etat Condensé – UMR CNRS 6087, Université du Maine, 72085, Le Mans Cedex 9 (France); Chakrabarti, P.K., E-mail: pabitra_c@hotmail.com [Solid State Research Laboratory, Department of Physics, Burdwan University, Burdwan 713104, West Bengal (India)

    2015-10-15

    Highlights: • Maghemite nanoparticles were prepared by a modified co-precipitation method. • Nanoparticles were then successfully coated with pepsin for bio-functionlization. • XRD and Mössbauer spectra confirmed the maghemite phase of the nanoparticles. • Magnetic data were analysed to evaluate particle size, anisotropy etc. - Abstract: Maghemite nanoparticles (γ-Fe{sub 2}O{sub 3}) are prepared by co-precipitation method. To obtain bio-functionalized magnetic nanoparticles for magnetically controlled drug delivery, the prepared nanoparticles are successfully coated with pepsin, a bio-compatible polymer and digestive enzyme. Crystallographic phase of the nanoparticles is confirmed by X-ray diffractograms (XRD), high resolution transmission electron microscopy (HRTEM) and {sup 57}Fe Mössbauer spectrometry. The average size of nanoparticles/nanocrystallites is estimated from the (3 1 1) peak of the XRD pattern using Debye–Scherrer formula. Results of HRTEM of coated and bare samples are in good agreement with those extracted from the XRD analysis. The dynamic magnetic properties are observed and different quantities viz., coercive field, magnetization, remanence, hysteresis losses etc., are estimated, which confirmed the presence of superparamagnetic relaxation of nanoparticles. Mössbauer spectra of the samples recorded at both 300 and 77 K, confirmed that the majority of particles are maghemite together with a very small fraction of magnetite nanoparticles.

  3. Synthesis, characterization and magnetic property of maghemite (γ-Fe2O3) nanoparticles and their protective coating with pepsin for bio-functionalization

    International Nuclear Information System (INIS)

    Bandhu, A.; Sutradhar, S.; Mukherjee, S.; Greneche, J.M.; Chakrabarti, P.K.

    2015-01-01

    Highlights: • Maghemite nanoparticles were prepared by a modified co-precipitation method. • Nanoparticles were then successfully coated with pepsin for bio-functionlization. • XRD and Mössbauer spectra confirmed the maghemite phase of the nanoparticles. • Magnetic data were analysed to evaluate particle size, anisotropy etc. - Abstract: Maghemite nanoparticles (γ-Fe 2 O 3 ) are prepared by co-precipitation method. To obtain bio-functionalized magnetic nanoparticles for magnetically controlled drug delivery, the prepared nanoparticles are successfully coated with pepsin, a bio-compatible polymer and digestive enzyme. Crystallographic phase of the nanoparticles is confirmed by X-ray diffractograms (XRD), high resolution transmission electron microscopy (HRTEM) and 57 Fe Mössbauer spectrometry. The average size of nanoparticles/nanocrystallites is estimated from the (3 1 1) peak of the XRD pattern using Debye–Scherrer formula. Results of HRTEM of coated and bare samples are in good agreement with those extracted from the XRD analysis. The dynamic magnetic properties are observed and different quantities viz., coercive field, magnetization, remanence, hysteresis losses etc., are estimated, which confirmed the presence of superparamagnetic relaxation of nanoparticles. Mössbauer spectra of the samples recorded at both 300 and 77 K, confirmed that the majority of particles are maghemite together with a very small fraction of magnetite nanoparticles

  4. Sustained release of doxorubicin from zeolite-magnetite nanocomposites prepared by mechanical activation

    International Nuclear Information System (INIS)

    Arruebo, Manuel; Fernandez-Pacheco, Rodrigo; Irusta, Silvia; Arbiol, Jordi; Ibarra, M Ricardo; SantamarIa, Jesus

    2006-01-01

    Nanocomposites consisting of magnetite and FAU zeolite with a high surface area and adsorption capacity have been prepared by mechanical activation using high-energy milling at room temperature. FTIR results, as well as HRTEM, EFTEM, and XPS measurements, show that the resulting magnetic nanoparticles are covered by a thin aluminosilicate coating. A saturation magnetization as high as 16 emu g -1 and 94.2 Oe of coercivity were observed for the obtained composites. The main advantages of this synthesis procedure are (i) simplicity of the preparation procedure (ii) prevention of agglomeration of the magnetite nanoparticles to a large extent, and (iii) absence of free magnetite outside the zeolitic matrix. In addition, in vitro experiments revealed that the nanoparticles prepared were able to store and release substantial amounts of doxorubicin. In view of these advantages, these magnetic nanoparticles can be considered as potential candidates for drug-delivery applications

  5. Cellular uptake of magnetite nanoparticles enhanced by NdFeB magnets in staggered arrangement

    International Nuclear Information System (INIS)

    Lu, Yi-Ching; Chang, Fan-Yu; Tu, Shu-Ju; Chen, Jyh-Ping; Ma, Yunn-Hwa

    2017-01-01

    Magnetic force may greatly enhance uptake of magnetic nanoparticles (MNPs) by cultured cells; however, the effects of non-uniformity of magnetic field/ magnetic gradient on MNP internalization in culture has not been elucidated. Cellular uptake of polyacrylic acid coated-MNP by LN229 cells was measured with cylindrical NdFeB magnets arranged in a staggered pattern. The magnetic field generated by placing a magnet underneath (H-field) elicited a homogenous distribution of MNPs on the cells in culture; whereas the field without magnet underneath (L-field) resulted in MNP distribution along the edge of the wells. Cell-associated MNP (MNP cell ) appeared to be magnetic field- and concentration-dependent. In H-field, MNP cell reached plateau within one hour of exposure to MNP with only one-min application of the magnetic force in the beginning of incubation; continuous presence of the magnet for 2 h did not further increase MNP cell , suggesting that magnetic force-induced uptake may be primarily contributed to enhanced MNP sedimentation. Although MNP distribution was much inhomogeneous in L-field, averaged MNP cell in the L-field may reach as high as 80% of that in H-field during 1–6 h incubation, suggesting high capacity of MNP internalization. In addition, no significant difference was observed in MNP cell analyzed by flow cytometry with the application of H-field of staggered plate vs. filled magnet plate. Therefore, biological variation may dominate MNP internalization even under relatively uniformed magnetic field; whereas non-uniformed magnetic field may serve as a model for tumor targeting with MNPs in vivo. - Graphical abstract: Averaged MNP uptake by glioma cells in the low and non-uniformed magnetic field reached as high as 80% of that in uniformed magnetic field, which is probably due to both heterogeneous distributions of MNPs in the non-uniformed magnetic field and high capacity of the MNP uptake by these cells. - Highlights: • Enhanced sedimentation

  6. Cellular uptake of magnetite nanoparticles enhanced by NdFeB magnets in staggered arrangement

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Yi-Ching; Chang, Fan-Yu [Department of Physiology and Pharmacology & Healthy Aging Research Center, Guishan, Taoyuan City 33302, Taiwan, ROC (China); Tu, Shu-Ju [Department of Medical Imaging and Radiological Sciences, Chang Gung University, Guishan, Taoyuan City 33302, Taiwan, ROC (China); Chen, Jyh-Ping [Department of Chemical and Materials Engineering, Chang Gung University, Guishan, Taoyuan City 33302, Taiwan, ROC (China); Ma, Yunn-Hwa, E-mail: yhma@mail.cgu.edu.tw [Department of Physiology and Pharmacology & Healthy Aging Research Center, Guishan, Taoyuan City 33302, Taiwan, ROC (China); Department of Neurology, Chang Gung Memorial Hospital, Guishan, Taoyuan City 33305, Taiwan, ROC (China)

    2017-04-01

    Magnetic force may greatly enhance uptake of magnetic nanoparticles (MNPs) by cultured cells; however, the effects of non-uniformity of magnetic field/ magnetic gradient on MNP internalization in culture has not been elucidated. Cellular uptake of polyacrylic acid coated-MNP by LN229 cells was measured with cylindrical NdFeB magnets arranged in a staggered pattern. The magnetic field generated by placing a magnet underneath (H-field) elicited a homogenous distribution of MNPs on the cells in culture; whereas the field without magnet underneath (L-field) resulted in MNP distribution along the edge of the wells. Cell-associated MNP (MNP{sub cell}) appeared to be magnetic field- and concentration-dependent. In H-field, MNP{sub cell} reached plateau within one hour of exposure to MNP with only one-min application of the magnetic force in the beginning of incubation; continuous presence of the magnet for 2 h did not further increase MNP{sub cell}, suggesting that magnetic force-induced uptake may be primarily contributed to enhanced MNP sedimentation. Although MNP distribution was much inhomogeneous in L-field, averaged MNP{sub cell} in the L-field may reach as high as 80% of that in H-field during 1–6 h incubation, suggesting high capacity of MNP internalization. In addition, no significant difference was observed in MNP{sub cell} analyzed by flow cytometry with the application of H-field of staggered plate vs. filled magnet plate. Therefore, biological variation may dominate MNP internalization even under relatively uniformed magnetic field; whereas non-uniformed magnetic field may serve as a model for tumor targeting with MNPs in vivo. - Graphical abstract: Averaged MNP uptake by glioma cells in the low and non-uniformed magnetic field reached as high as 80% of that in uniformed magnetic field, which is probably due to both heterogeneous distributions of MNPs in the non-uniformed magnetic field and high capacity of the MNP uptake by these cells. - Highlights:

  7. Encapsulated magnetite particles for biomedical application

    CERN Document Server

    Landfester, K

    2003-01-01

    The process of miniemulsification allows the generation of small, homogeneous, and stable droplets containing monomer or polymer precursors and magnetite which are then transferred by polymer reactions to the final polymer latexes, keeping their particular identity without serious exchange kinetics involved. It is shown that the miniemulsion process can excellently be used for the formulation of polymer-coated magnetic nanoparticles which can further be used for biomedical applications. The use of high shear, appropriate surfactants, and the addition of a hydrophobe in order to suppress the influence of Ostwald ripening are key factors for the formation of the small and stable droplets in miniemulsion and will be discussed. Two different approaches based on miniemulsion processes for the encapsulation of magnetite into polymer particles will be presented in detail.

  8. Synthesis and functionalization of magnetite nanoparticles with different amino-functional alkoxysilanes

    International Nuclear Information System (INIS)

    Bini, Rafael A.; Marques, Rodrigo Fernando C.; Santos, Francisco J.; Chaker, Juliano A.; Jafelicci, Miguel

    2012-01-01

    Superparamagnetic iron oxide (SPIO) nanoparticles show great promise for many biotechnological applications. This paper addresses the synthesis and characterization of SPIO nanoparticles grafted with three different alkoxysilanes: 3-aminopropyl-triethoxysilane (APTES), 3-aminopropyl-ethyl-diethoxysilane (APDES) and 3-aminopropyl-diethy-ethoxysilane (APES). SPIO nanoparticles with an average particle diameter of 10 nm were prepared by chemical sonoprecipitation. As confirmed by Fourier transform infrared (FTIR) spectroscopy, silylation of these nanoparticles occurs through a two-step process. Decreasing the number of alkoxide groups reduced the concentration of free amino groups on the SPIO surface ([SPIO-NH 2 ]-APTES>APDES>APES). This phenomenon results from steric contributions and the formation of H-bonded amines provided by the ethyl groups present in the APDES and APES molecules. A simulation of SPIO nanoparticles in a saline physiologic solution shows that the ethyl groups impart larger steric stability onto the ferrofluids, which reduces aggregation. The magnetization (M) versus magnetic field (H) curves show that the synthesized iron oxide nanoparticles display superparamagnetic behavior. The zero-field cooling (ZFC) and field cooling (FC) curves show that the changes in the blocking temperature depend on the alkoxysilane-functionalized particle surface. - Highlights: → Superparamagnetic iron oxide nanoparticles were grafted with different alkoxysilanes. → The decrease of alkoxide group number reduced the concentration of free amino group. → We correlate the influence of the amino and ethyl groups with their colloidal property. → Inter-particles aggregation analyzed by magnetic measurement.

  9. Melanoma-Targeted Chemothermotherapy and In Situ Peptide Immunotherapy through HSP Production by Using Melanogenesis Substrate, NPrCAP, and Magnetite Nanoparticles

    Directory of Open Access Journals (Sweden)

    Kowichi Jimbow

    2013-01-01

    Full Text Available Exploitation of biological properties unique to cancer cells may provide a novel approach to overcome difficult challenges to the treatment of advanced melanoma. In order to develop melanoma-targeted chemothermoimmunotherapy, a melanogenesis substrate, N-propionyl-4-S-cysteaminylphenol (NPrCAP, sulfur-amine analogue of tyrosine, was conjugated with magnetite nanoparticles. NPrCAP was exploited from melanogenesis substrates, which are expected to be selectively incorporated into melanoma cells and produce highly reactive free radicals through reacting with tyrosinase, resulting in chemotherapeutic and immunotherapeutic effects by oxidative stress and apoptotic cell death. Magnetite nanoparticles were conjugated with NPrCAP to introduce thermotherapeutic and immunotherapeutic effects through nonapoptotic cell death and generation of heat shock protein (HSP upon exposure to alternating magnetic field (AMF. During these therapeutic processes, NPrCAP was also expected to provide melanoma-targeted drug delivery system.

  10. Determination of nanoparticle surface coatings and nanoparticle purity using microscale thermogravimetric analysis.

    Science.gov (United States)

    Mansfield, Elisabeth; Tyner, Katherine M; Poling, Christopher M; Blacklock, Jenifer L

    2014-02-04

    The use of nanoparticles in some applications (i.e., nanomedical, nanofiltration, or nanoelectronic) requires small samples with well-known purities and composition. In addition, when nanoparticles are introduced into complex environments (e.g., biological fluids), the particles may become coated with matter, such as proteins or lipid layers. Many of today's analytical techniques are not able to address small-scale samples of nanoparticles to determine purity and the presence of surface coatings. Through the use of an elevated-temperature quartz crystal microbalance (QCM) method we call microscale thermogravimetric analysis, or μ-TGA, the nanoparticle purity, as well as the presence of any surface coatings of nanomaterials, can be measured. Microscale thermogravimetric analysis is used to determine the presence and amount of surface-bound ligand coverage on gold nanoparticles and confirm the presence of a poly(ethylene glycol) coating on SiO2 nanoparticles. Results are compared to traditional analytical techniques to demonstrate reproducibility and validity of μ-TGA for determining the presence of nanoparticle surface coatings. Carbon nanotube samples are also analyzed and compared to conventional TGA. The results demonstrate μ-TGA is a valid method for quantitative determination of the coatings on nanoparticles, and in some cases, can provide purity and compositional data of the nanoparticles themselves.

  11. Phytosynthesis and photocatalytic activity of magnetite (Fe{sub 3}O{sub 4}) nanoparticles using the Andean blackberry leaf

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Brajesh, E-mail: krmbraj@gmail.com [Centro de Nanociencia y Nanotecnologia, Universidad de las Fuerzas Armadas ESPE, Av. Gral. Rumiñahui s/n, Sangolqui, P.O. BOX 171-5-231B (Ecuador); Department of Chemistry, TATA College, Kolhan University, Chaibasa, 833202, Jharkhand (India); Smita, Kumari; Cumbal, Luis; Debut, Alexis [Centro de Nanociencia y Nanotecnologia, Universidad de las Fuerzas Armadas ESPE, Av. Gral. Rumiñahui s/n, Sangolqui, P.O. BOX 171-5-231B (Ecuador); Galeas, Salome; Guerrero, Victor H. [Laboratorio de Nuevos Materiales, Departamento de Materiales, Escuela Politécnica Nacional, Quito (Ecuador)

    2016-08-15

    In the present study, a simple, low cost, and ecofriendly synthesis of magnetite nanoparticles (Fe{sub 3}O{sub 4} NPs) has been developed using Andean blackberry leaf extract. UV–vis spectroscopy technique were used to study the initial formation of Fe{sub 3}O{sub 4} NPs. Morphology, crystallinity and surface properties of nanoparticles were studied using transmission electron microscopy (TEM), Dynamic light scattering (DLS), X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR) and Thermal gravimetric (TG) techniques. TEM and DLS characterization indicated the formation of spherical Fe{sub 3}O{sub 4} NPs of average size 54.5 ± 24.6 nm. XRD and FTIR studies confirmed the existence of the cubic spinel phase of Fe{sub 3}O{sub 4} NPs and Fe−O peak at 570 cm{sup −1}, whereas TG analysis indicated that the nanoparticles contain 94% metal and 6% capping ligand. It has been observed that, as-synthesized Fe{sub 3}O{sub 4} NPs exhibited photocatalytic activity for degradation of organic dyes such as methylene blue (k = 0.0105475 min{sup −1}), congo red (k = 0.0043240 min{sup −1}), and methyl orange (k = 0.0028930 min{sup −1}), efficiently. The antioxidant activity of Fe{sub 3}O{sub 4} NPs against 1, 1-diphenyl-2-picrylhydrazyl were also evaluated. - Highlights: • We report extracellular phytosynthesis of Fe{sub 3}O{sub 4} nanoparticles using the Andean blackberry leaf. • The synthesized Fe{sub 3}O{sub 4} nanoparticles are spherical and average size is 54.5 ± 24.6 nm. • It showed enhanced photocatalytic activity and weak antioxidant efficacy. • Environmentally benign, non-toxic and cost-effective method is suggested.

  12. Multifunctional PEG-carboxylate copolymer coated superparamagnetic iron oxide nanoparticles for biomedical application

    Science.gov (United States)

    Illés, Erzsébet; Szekeres, Márta; Tóth, Ildikó Y.; Szabó, Ákos; Iván, Béla; Turcu, Rodica; Vékás, Ladislau; Zupkó, István; Jaics, György; Tombácz, Etelka

    2018-04-01

    Biocompatible magnetite nanoparticles (MNPs) were prepared by post-coating the magnetic nanocores with a synthetic polymer designed specifically to shield the particles from non-specific interaction with cells. Poly(ethylene glycol) methyl ether methacrylate (PEGMA) macromonomers and acrylic acid (AA) small molecular monomers were chemically coupled by quasi-living atom transfer radical polymerization (ATRP) to a comb-like copolymer, P(PEGMA-co-AA) designated here as P(PEGMA-AA). The polymer contains pendant carboxylate moieties near the backbone and PEG side chains. It is able to bind spontaneously to MNPs; stabilize the particles electrostatically via the carboxylate moieties and sterically via the PEG moieties; provide high protein repellency via the structured PEG layer; and anchor bioactive proteins via peptide bond formation with the free carboxylate groups. The presence of the P(PEGMA-AA) coating was verified in XPS experiments. The electrosteric (i.e., combined electrostatic and steric) stabilization is efficient down to pH 4 (at 10 mM ionic strength). Static magnetization and AC susceptibility measurements showed that the P(PEGMA-AA)@MNPs are superparamagnetic with a saturation magnetization value of 55 emu/g and that both single core nanoparticles and multicore structures are present in the samples. The multicore components make our product well suited for magnetic hyperthermia applications (SAR values up to 17.44 W/g). In vitro biocompatibility, cell internalization, and magnetic hyperthermia studies demonstrate the excellent theranostic potential of our product.

  13. A Novel Method of Coating Orthodontic Archwires with Nanoparticles

    Science.gov (United States)

    Syed, Shibli S; Kulkarni, Dinraj; Todkar, Rohit; Bagul, Ravikiran S; Parekh, Kreena; Bhujbal, Nikita

    2015-01-01

    Background: The major hazard to the orthodontic tooth movement is the friction developing at the bracket wire interface. In the past, there have been various attempts to reduce this friction. We believe that coating the commercially available orthodontic wires with nanoparticles can result in a successful reduction of this friction. The objective of this study is to develop a novel method of coating orthodontic archwires with nanoparticles. Materials and Methods: Stainless steel (Ormco, CA, USA), titanium molybdenum alloy (Ormco, CA, USA) and nickel-titanium (G and H Wire Company, USA) orthodontic wires with a rectangular cross-section dimension of 0.019”× 0.025”, were selected. The wires were later coated with a uniform and smooth nanoparticle film using 100 ml nanocremics. The coating procedure described in this article is a sol-gel thin film dip coating method. Results: The coating procedure was verified by comparing the surface topography of nanocoated archwires with the commercially available archwires in an environmental scanning electron microscope (ESEM). The ESEM images prove that the surface topography of the coated wires was found to be smoother with less surface deteriorations as compared to the commercially available wires. Conclusion: Commercially available orthodontic wires can be successfully coated using a novel method of sol-gel thin film dip coating method. PMID:26028899

  14. Synthetic and biogenic magnetite nanoparticles for tracking of stem cells and dendritic cells

    International Nuclear Information System (INIS)

    Schwarz, Sebastian; Fernandes, Fabiana; Sanroman, Laura; Hodenius, Michael; Lang, Claus; Himmelreich, Uwe; Schmitz-Rode, Thomas; Schueler, Dirk; Hoehn, Mathias

    2009-01-01

    Accurate delivery of cells to target organs is critical for success of cell-based therapies with stem cells or immune cells such as antigen-presenting dendritic cells (DC). Labeling with contrast agents before implantation provides a powerful means for monitoring cellular migration using magnetic resonance imaging (MRI). In this study, we investigated the uptake of fully synthesized or bacterial magnetic nanoparticles (MNPs) into hematopoietic Flt3 + stem cells and DC from mouse bone marrow. We show that (i) uptake of both synthetic and biogenic nanoparticles into cells endow magnetic activity and (ii) low numbers of MNP-loaded cells are readily detected by MRI.

  15. Facile integration of multiple magnetite nanoparticles for theranostics combining efficient MRI and thermal therapy

    Science.gov (United States)

    Huang, Guoming; Zhu, Xianglong; Li, Hui; Wang, Lirong; Chi, Xiaoqin; Chen, Jiahe; Wang, Xiaomin; Chen, Zhong; Gao, Jinhao

    2015-01-01

    Multifunctional nanostructures with both diagnostic and therapeutic capabilities have attracted considerable attention in biomedical research because they can offer great advantages in disease management and prognosis. In this work, a facile way to transfer the hydrophobic iron oxide (IO) nanoparticles into aqueous media by employing carboxylic graphene oxide (GO-COOH) as the transferring agent has been reported. In this one-step process, IO nanoparticles adhere to GO-COOH and form water-dispersible clusters via hydrophobic interactions between the hydrophobic ligands of IO nanoparticles and the basal plane of GO-COOH. The multiple IO nanoparticles on GO-COOH sheets (IO/GO-COOH) present a significant increase in T2 contrast enhancement. Moreover, the IO/GO-COOH nanoclusters also display a high photothermal conversion efficiency and can effectively inhibit tumor growth through the photothermal effects. It is envisioned that such IO/GO-COOH nanocomposites combining efficient MRI and photothermal therapy hold great promise in theranostic applications.Multifunctional nanostructures with both diagnostic and therapeutic capabilities have attracted considerable attention in biomedical research because they can offer great advantages in disease management and prognosis. In this work, a facile way to transfer the hydrophobic iron oxide (IO) nanoparticles into aqueous media by employing carboxylic graphene oxide (GO-COOH) as the transferring agent has been reported. In this one-step process, IO nanoparticles adhere to GO-COOH and form water-dispersible clusters via hydrophobic interactions between the hydrophobic ligands of IO nanoparticles and the basal plane of GO-COOH. The multiple IO nanoparticles on GO-COOH sheets (IO/GO-COOH) present a significant increase in T2 contrast enhancement. Moreover, the IO/GO-COOH nanoclusters also display a high photothermal conversion efficiency and can effectively inhibit tumor growth through the photothermal effects. It is envisioned

  16. Partial slip effect in flow of magnetite-Fe{sub 3}O{sub 4} nanoparticles between rotating stretchable disks

    Energy Technology Data Exchange (ETDEWEB)

    Hayat, Tasawar [Department of Mathematics, Quaid-I-Azam University 45320, Islamabad 44000 (Pakistan); Nonlinear Analysis and Applied Mathematics (NAAM) Research Group, Department of Mathematics, Faculty of Science, King Abdulaziz University, Jeddah 21589 (Saudi Arabia); Qayyum, Sumaira [Department of Mathematics, Quaid-I-Azam University 45320, Islamabad 44000 (Pakistan); Imtiaz, Maria, E-mail: mi_qau@yahoo.com [Department of Mathematics, Quaid-I-Azam University 45320, Islamabad 44000 (Pakistan); Alzahrani, Faris; Alsaedi, Ahmed [Nonlinear Analysis and Applied Mathematics (NAAM) Research Group, Department of Mathematics, Faculty of Science, King Abdulaziz University, Jeddah 21589 (Saudi Arabia)

    2016-09-01

    This paper addresses the flow of magnetic nanofluid (ferrofluid) between two parallel rotating stretchable disks with different rotating and stretching velocities. Water based fluid comprising magnetite-Fe{sub 3}O{sub 4} nanoparticles is addressed. Velocity slip and temperature jump at solid–fluid interface are also taken into account. Appropriate transformations reduce the nonlinear partial differential system to ordinary differential system. Convergent series solutions are obtained. Effects of various pertinent parameters on the velocity and temperature profiles are shown and evaluated. Computations for skin friction coefficient and Nusselt number are presented and examined for the influence of involved parameters. It is noted that tangential velocity of fluid decreases for larger velocity slip parameter. Fluid temperature also reduces for increasing value of thermal slip parameter. Surface drag force and heat transfer rate at lower disk are enhanced when magnetic field strength is increased. - Highlights: • Flow and heat transfer of ferrofluid induced by two stretchable rotating disks with velocity and thermal slips are explored. • Fluid temperature increases for larger solid volume fraction of nanofluid. • Heat transfer rate decreases for increasing values of thermal slip parameter.

  17. TEA controllable preparation of magnetite nanoparticles (Fe{sub 3}O{sub 4} NPs) with excellent magnetic properties

    Energy Technology Data Exchange (ETDEWEB)

    Han, Chengliang, E-mail: clhan@issp.ac.cn [Department of Chemical and Material Engineering, Hefei University, Hefei 230601 (China); Zhu, Dejie [State Key Laboratory of Structural Chemistry, Fujian Institute of Research on the Structure of Matter, Chinese Academy of Sciences, Fuzhou 350002 (China); Wu, Hanzhao; Li, Yao; Cheng, Lu; Hu, Kunhong [Department of Chemical and Material Engineering, Hefei University, Hefei 230601 (China)

    2016-06-15

    A fast and controllable synthesis method for superparamagnetic magnetite nanoparticles (Fe{sub 3}O{sub 4} NPs) was developed in Fe(III)-triethanolamine (TEA) solution. The phase structure, morphology and particle size of the as-synthesized samples were characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM). The results showed that the magnetic particles were pure Fe{sub 3}O{sub 4} with mean sizes of approximately 10 nm. The used TEA has key effects on the formation of well dispersing Fe{sub 3}O{sub 4} NPs. Vibrating sample magnetometer (VSM) result indicated that the as-obtained Fe{sub 3}O{sub 4} NPs exhibited superparamagnetic behavior and the saturation magnetization (M{sub s}) was about 70 emu/g, which had potential applications in magnetic science and technology. - Highlights: • The Fe{sub 3}O{sub 4} NPs are synthesized by a simple and low-cost hydrothermal approach. • The triethanolamine (TEA) played vital roles in the formation of Fe{sub 3}O{sub 4} NPs. • Our samples exhibited superparamagnetic and excellent dispersing properties in water.

  18. Magnetic Solid Phase Extraction and Removal of Five Cationic Dyes from Aqueous Solution Using Magnetite Nanoparticle Loaded Platanusorientalis Waste Leaves

    Directory of Open Access Journals (Sweden)

    Elaheh Madrakian

    2016-12-01

    Full Text Available This paper reports on synthesis of a magnetic adsorbent for wastewater treatment purposes. In this regard, platanus orientalis waste leaves were chosen as a cheap material for preparing the magnetic adsorbent by loading magnetite nanoparticles on it. The synthesized adsorbent was characterized using scanning electron microscope and X-ray diffractometer. Then, it was used for magnetic solid phase extraction and removal of five cationic dyes including methyl violet (MV, methylene blue (MB, malachite green (MG, crystal violet (CV, and neutral red (NR from aqueous solution as a model application. Different important factors affecting the adsorption process were optimized, and the results showed that under the optimized conditions (pH 10 for CV, MV, MB, and MG; pH 6 for NR; adsorbent dosage, 20 mg; agitation time, 25 min efficient removal of the investigated dyes (adsorption capacities between of 89-133 mg g-1 is achievable using the synthesized adsorbent. Furthermore, the reusability experiments showed that the adsorbent could be reused at least ten cycles without any significant loss in its sorption behavior.

  19. Physiological effects of magnetite (Fe3O4) nanoparticles on perennial ryegrass (Lolium perenne L.) and pumpkin (Cucurbita mixta) plants.

    Science.gov (United States)

    Wang, Huanhua; Kou, Xiaoming; Pei, Zhiguo; Xiao, John Q; Shan, Xiaoquan; Xing, Baoshan

    2011-03-01

    To date, knowledge gaps and associated uncertainties remain unaddressed on the effects of nanoparticles (NPs) on plants. This study was focused on revealing some of the physiological effects of magnetite (Fe(3)O(4)) NPs on perennial ryegrass (Lolium perenne L.) and pumpkin (Cucurbita mixta cv. white cushaw) plants under hydroponic conditions. This study for the first time reports that Fe(3)O(4) NPs often induced more oxidative stress than Fe(3)O(4) bulk particles in the ryegrass and pumpkin roots and shoots as indicated by significantly increased: (i) superoxide dismutase and catalase enzyme activities, and (ii) lipid peroxidation. However, tested Fe(3)O(4) NPs appear unable to be translocated in the ryegrass and pumpkin plants. This was supported by the following data: (i) No magnetization was detected in the shoots of either plant treated with 30, 100 and 500 mg l(-1) Fe(3)O(4) NPs; (ii) Fe K-edge X-ray absorption spectroscopic study confirmed that the coordination environment of Fe in these plant shoots was similar to that of Fe-citrate complexes, but not to that of Fe(3)O(4) NPs; and (iii) total Fe content in the ryegrass and pumpkin shoots treated with Fe(3)O(4) NPs was not significantly increased compared to that in the control shoots.

  20. Production of High-purity Magnetite Nanoparticles from a Low-grade Iron Ore via Solvent Extraction

    Energy Technology Data Exchange (ETDEWEB)

    Suh, Yong Jae; Kil, Dae Sup; Jang, Hee Dong [Korea Institute of Geoscience and Mineral Resources, Daejeon (Korea, Republic of); Do, Thi May [Korea University of Science and Technology, Daejeon (Korea, Republic of); Cho, Kuk [Pusan National University, Busan (Korea, Republic of)

    2015-02-15

    We produced magnetite nanoparticles (MNPs) and a Mg-rich solution as a nano-adsorbent and a coagulant for water treatment, respectively, using a low-grade iron ore. The ore was leached with aqueous hydrochloric acid and its impurities were removed by solvent extraction of the leachate using tri-n-butyl phosphate as an extractant. The content of Si and Mg, which inhibit the formation of MNPs, was reduced from 10.3 wt% and 15.5 wt% to 28.1 mg/L and < 1.4 mg/L, respectively. Consequently, the Fe content increased from 68.6 wt% to 99.8 wt%. The high-purity Fe{sup 3+} solution recovered was used to prepare 5-15-nm MNPs by coprecipitation. The wastewater produced contained a large amount of Mg{sup 2+} and can be used to precipitate struvite in sewage treatment. This process helps reduce the cost of both sewage and iron-ore-wastewater treatments, as well as in the economic production of the nano-adsorbent.

  1. The molecular mass of dextran used to modify magnetite nanoparticles affects insulin amyloid aggregation

    Czech Academy of Sciences Publication Activity Database

    Sipošová, K.; Pospíšková, K.; Bednáriková, Z.; Šafařík, Ivo; Šafaříková, Miroslava; Kubovčíková, M.; Kopčanský, P.; Gázová, Z.

    2017-01-01

    Roč. 427, April (2017), s. 48-53 ISSN 0304-8853 Institutional support: RVO:60077344 Keywords : amyloid aggregation * nanoparticles * magnetic fluid * dextran * insulin Subject RIV: CE - Biochemistry OBOR OECD: Biochemistry and molecular biology Impact factor: 2.630, year: 2016

  2. Synthesis of calix[4]arene-grafted magnetite nanoparticles and Evaluation of their arsenate as well as dichromate removal efficiency

    Energy Technology Data Exchange (ETDEWEB)

    Sayin, Serkan; Ozcan, Fatih; Yilmaz, Mustafa; Cengeloglu, Yunus [Department of Chemistry, Selcuk University, Konya (Turkey); Tor, Ali [Department of Environmental Engineering, Selcuk University, Konya (Turkey); Memon, Shahabuddin [National Center of Excellence in Analytical Chemistry, University of Sindh, Jamshoro (Pakistan)

    2010-07-15

    In this study, 5,17-bis-[(4-benzylpiperidine)methyl]-25,26,27,28-tetrahydroxy-calix[4]arene (3) has been prepared by the treatment of calix[4]arene with a secondary amine (4-benzylpiperidine) and formaldehyde by means of Mannich reaction. The prepared Mannich base (3) has been grafted onto [3-(2,3-epoxypropoxy)-propyl]-trimethoxysilane-modified Fe{sub 3}O{sub 4} magnetite nanoparticles (EPPTMS-MN) in order to obtain 5,17-bis-[(4-benzylpiperidine)methyl]-25,26,27,28-tetrahydroxy calix[4]arene-grafted EPPTMS-MN (BP-calix[4]arene-grafted Fe{sub 3}O{sub 4}). All new compounds were characterized by a combination of FTIR and {sup 1}H-NMR analyses. The morphology of the magnetic nanoparticles was examined by transmission electron microscopy. Moreover, the studies regarding the removal of arsenate and dichromate ions from the aqueous solutions were also carried out by using 5,17-bis-[(4-benzylpiperidine)methyl]-25,26,27,28-tetrahydroxy-calix[4]arene in liquid-liquid extraction and BP-calix[4]arene-grafted Fe{sub 3}O{sub 4} (4) in solid-liquid extraction experiments. The extraction results indicated that 3 is protonated at proton-switchable binding sites in acidic conditions. Hence, facilitating binding of arsenate and dichromate is resulted from both electrostatic interactions and hydrogen bonding. To understand the selectivity of 3, the retention of dichromate anions in the presence of Cl{sup -}, NO{sub 3}{sup -}, and SO{sub 4}{sup 2-} anions at pH 1.5 was also examined. (Abstract Copyright [2010], Wiley Periodicals, Inc.)

  3. Antimony (Sb) sorption studies on zircaloy, carbon steel (CS) and magnetite coated CS (MCS) surfaces in aqueous medium at pH 10.2 and 280℃

    International Nuclear Information System (INIS)

    Keny, S.J.; Kumbhar, A.G.; Achary, S.N.; Basu, Saibal

    2014-01-01

    Antimony sorption studies on zircaloy, CS and magnetite coated carbon steel (MCS) at primary heat transport temperature (290℃) of pressurised heavy water reactor (PHWR) are of direct relevance in investigating Sb activity problem faced in Indian PHWRs. Sb impregnated PHT pump carbon bearing releases Sb to reactor core. This Sb activates, and redeposit on out-of-core surfaces and results in exposure and apparent high decontamination factors. This Sb is not amenable to normal decantation. The form and state of deposited Sb is not yet fully known. This works attempts for this

  4. Porphyrin-magnetite nanoconjugates for biological imaging

    LENUS (Irish Health Repository)

    Nowostawska, Malgorzata

    2011-04-08

    Abstract Background The use of silica coated magnetic nanoparticles as contrast agents has resulted in the production of highly stable, non-toxic solutions that can be manipulated via an external magnetic field. As a result, the interaction of these nanocomposites with cells is of vital importance in understanding their behaviour and biocompatibility. Here we report the preparation, characterisation and potential application of new "two-in-one" magnetic fluorescent nanocomposites composed of silica-coated magnetite nanoparticles covalently linked to a porphyrin moiety. Method The experiments were performed by administering porphyrin functionalised silica-coated magnetite nanoparticles to THP-1 cells, a human acute monocytic leukaemia cell line. Cells were cultured in RPMI 1640 medium with 25 mM HEPES supplemented with heat-inactivated foetal bovine serum (FBS). Results We have synthesised, characterised and analysed in vitro, a new multimodal (magnetic and fluorescent) porphyrin magnetic nanoparticle composite (PMNC). Initial co-incubation experiments performed with THP-1 macrophage cells were promising; however the PMNC photobleached under confocal microscopy study. β-mercaptoethanol (β-ME) was employed to counteract this problem and resulted not only in enhanced fluorescence emission, but also allowed for elongated imaging and increased exposure times of the PMNC in a cellular environment. Conclusion Our experiments have demonstrated that β-ME visibly enhances the emission intensity. No deleterious effects to the cells were witnessed upon co-incubation with β-ME alone and no increases in background fluorescence were recorded. These results should present an interest for further development of in vitro biological imaging techniques.

  5. Size selectivity of magnetite core- (Ag/Au) shell nanoparticles for multimodal imaging applications

    Science.gov (United States)

    Singh, Pinki; Upadhyay, Chandan

    2017-10-01

    The magnetic and optical properties of nanomaterials play a significant role in the selection of the materials to be used for contrast enhancement in different biological and cell imaging techniques. These nanoparticles can also be used as drug delivery agents. The calculation of absorption efficiency and surface plasmon resonance wavelength has been performed using Mie theory and MATLAB programs. The study of spectrum calculated indicates the dependence of several optical properties such as resonance and absorption efficiency peak on ratio of core radius to the thickness of shell. A systematic study on the effect of nanoparticle dimension has been presented which clearly indicates that the optical properties can be modulated across the visible and near infrared range by changing these parameters. These properties of nanomaterials make them suitable for their application as multimodal imaging agents as they are also magnetically active and biocompatible.

  6. Glass frits coated with silver nanoparticles for silicon solar cells

    International Nuclear Information System (INIS)

    Li, Yingfen; Gan, Weiping; Zhou, Jian; Li, Biyuan

    2015-01-01

    Graphical abstract: - Highlights: • Silver-coated glass frits for solar cells were prepared by electroless plating. • Gum Arabic was used as the activating agent of glass frits. • Silver-coated glass frits can improve the photovoltaic performances of solar cells. - Abstract: Glass frits coated with silver nanoparticles were prepared by electroless plating. Gum Arabic (GA) was used as the activating agent of glass frits without the assistance of stannous chloride or palladium chloride. The silver-coated glass frits prepared with different GA dosages were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and thermogravimetric analysis (TGA). The characterization results indicated that silver-coated glass frits had the structures of both glass and silver. Spherical silver nanoparticles were distributed on the glass frits evenly. The density and particle size of silver nanoparticles on the glass frits can be controlled by adjusting the GA dosage. The silver-coated glass frits were applied to silver pastes to act as both the densification promoter and silver crystallite formation aid in the silver electrodes. The prepared silver-coated glass frits can improve the photovoltaic performances of solar cells

  7. Glass frits coated with silver nanoparticles for silicon solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Li, Yingfen, E-mail: lyf350857423@163.com; Gan, Weiping; Zhou, Jian; Li, Biyuan

    2015-06-30

    Graphical abstract: - Highlights: • Silver-coated glass frits for solar cells were prepared by electroless plating. • Gum Arabic was used as the activating agent of glass frits. • Silver-coated glass frits can improve the photovoltaic performances of solar cells. - Abstract: Glass frits coated with silver nanoparticles were prepared by electroless plating. Gum Arabic (GA) was used as the activating agent of glass frits without the assistance of stannous chloride or palladium chloride. The silver-coated glass frits prepared with different GA dosages were characterized by X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), and thermogravimetric analysis (TGA). The characterization results indicated that silver-coated glass frits had the structures of both glass and silver. Spherical silver nanoparticles were distributed on the glass frits evenly. The density and particle size of silver nanoparticles on the glass frits can be controlled by adjusting the GA dosage. The silver-coated glass frits were applied to silver pastes to act as both the densification promoter and silver crystallite formation aid in the silver electrodes. The prepared silver-coated glass frits can improve the photovoltaic performances of solar cells.

  8. Polymer Coated Echogenic Lipid Nanoparticles with Dual Release Triggers

    Science.gov (United States)

    Nahire, Rahul; Haldar, Manas K.; Paul, Shirshendu; Mergoum, Anaas; Ambre, Avinash H.; Katti, Kalpana S.; Gange, Kara N.; Srivastava, D. K.; Sarkar, Kausik; Mallik, Sanku

    2013-01-01

    Although lipid nanoparticles are promising drug delivery vehicles, passive release of encapsulated contents at the target site is often slow. Herein, we report contents release from targeted, polymer coated, echogenic lipid nanoparticles in the cell cytoplasm by redox trigger and simultaneously enhanced by diagnostic frequency ultrasound. The lipid nanoparticles were polymerized on the external leaflet using a disulfide cross-linker. In the presence of cytosolic concentrations of glutathione, the lipid nanoparticles released 76% of encapsulated contents. Plasma concentrations of glutathione failed to release the encapsulated contents. Application of 3 MHz ultrasound for 2 minutes simultaneously with the reducing agent enhanced the release to 96%. Folic acid conjugated, doxorubicin loaded nanoparticles showed enhanced uptake and higher cytotoxicity in cancer cells overexpressing the folate receptor (compared to the control). With further developments, these lipid nanoparticles have the potential to be used as multimodal nanocarriers for simultaneous targeted drug delivery and ultrasound imaging. PMID:23394107

  9. Stabilization of temperature during magnetic hyperthermia by Ce substituted magnetite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Shaw, S.K.; Alla, S.K. [Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India); Meena, S.S. [Solid State Physics Division, Bhabha Atomic Research Centre, Mumbai 400085 (India); Mandal, R.K. [Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India); Prasad, N.K., E-mail: nandkp.met@iitbhu.ac.in [Department of Metallurgical Engineering, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India)

    2017-07-15

    Highlights: • Ce{sub x}Fe{sub 3−x}O{sub 4} (0.01 ≤ x ≤ 0.5) nanoparticles below 15 nm were synthesized by microwave refluxing method. • The saturation magnetization decreased with increased Ce concentration. • The sample displayed stabilization of temperature near 42 °C during magnetic hyperthermia. - Abstract: We report here magnetic hyperthermia using nanoparticles of Ce{sub x}Fe{sub 3−x}O{sub 4} (x = 0.01, 0.05, 0.1, 0.3 and 0.5) during which temperature was found to be stabilizing near 42 °C. This happens despite of their high saturation magnetization (M{sub S}) and Curie temperature (T{sub C}) values. It was observed that by selecting an appropriate magnetic field the temperature can be rose exactly near the therapeutic temperature and thus it will help to selectively kill the cancerous cells leaving normal cells unaffected. These nanoparticles (size around 8–15 nm) were produced by single step microwave refluxing technique. X-ray diffraction (XRD) analysis demonstrates that samples were essentially single phase except for x = 0.5 sample. The X-ray photoelectron spectroscopy (XPS) study for the samples demonstrated that Ce was present in both Ce{sup 3+} and Ce{sup 4+} states. The saturation magnetization value of the samples decreased sharply from 62 Am{sup 2}/kg for x = 0.01 to 19 Am{sup 2}/kg for x = 0.1. This value further decreased with increased Ce doping.

  10. Synthesis of Copper Nanoparticles Coated with Nitrogen Ligands

    Directory of Open Access Journals (Sweden)

    Rubén Sierra-Ávila

    2014-01-01

    Full Text Available The synthesis of copper nanoparticles was studied by wet chemical methods using copper sulfate pentahydrate (CuSO4·5H2O and nitrogen ligands allylamine (AAm and polyallylamine (PAAm as stabilizers. The results suggest that the use of these ligands leads to the exclusive formation of metallic copper nanoparticles (Cu-NPs. The use of partially crosslinked polyallylamine (PAAmc leads to nanoparticles (NPs with low yields and high coating content, while linear PAAm leads to NPs with high yields and low coating content. The chemical composition of the particles was determined by XRD and average particle diameters were determined by the Debye-Scherrer equation. TGA analysis provided evidence of the content and thermal stability of the coating on the nanoparticles and PAAm. The morphology, particle size distribution, and presence of PAAm coating were observed through TEM. The use of AAm in the synthesis of NPs could be a good alternative to reduce costs. By using TGA, TEM, and DSC techniques, it was determined that synthesized NPs with AAm presented a coating with similar characteristics to NPs with PAAm, suggesting that AAm underwent polymerization during the synthesis.

  11. Gentamicin coated iron oxide nanoparticles as novel antibacterial agents

    Science.gov (United States)

    Bhattacharya, Proma; Neogi, Sudarsan

    2017-09-01

    Applications of different types of magnetic nanoparticles for biomedical purposes started a long time back. The concept of surface functionalization of the iron oxide nanoparticles with antibiotics is a novel technique which paves the path for further application of these nanoparticles by virtue of their property of superparamagnetism. In this paper, we have synthesized novel iron oxide nanoparticles surface functionalized with Gentamicin. The average size of the particles, concluded from the HR-TEM images, came to be around 14 nm and 10 nm for unmodified and modified nanoparticles, respectively. The magnetization curve M(H) obtained for these nanoparticles are typical of superparamagnetic nature and having almost zero values of coercivity and remanance. The release properties of the drug coated nanoparticles were studied; obtaining an S shaped profile, indicating the initial burst effect followed by gradual sustained release. In vitro investigations against various gram positive and gram negative strains viz Staphylococcus aureus, Escherichia coli, Pseudomonas aeruginosa and Bacillus subtilis indicated significant antibacterial efficiency of the drug-nanoparticle conjugate. The MIC values indicated that a small amount like 0.2 mg ml-1 of drug capped particles induce about 98% bacterial death. The novelty of the work lies in the drug capping of the nanoparticles, which retains the superparamagnetic nature of the iron oxide nanoparticles and the medical properties of the drug simultaneously, which is found to extremely blood compatible.

  12. Greener synthesis of magnetite nanoparticles using green tea extract and their magnetic properties

    Science.gov (United States)

    Karade, V. C.; Waifalkar, P. P.; Dongle, T. D.; Sahoo, Subasa C.; Kollu, P.; Patil, P. S.; Patil, P. B.

    2017-09-01

    The facile green synthesis method has been employed for the synthesis of biocompatible Fe3O4 magnetic nanoparticles (MNPs) using green tea extract. The effective reduction of ferric ions (Fe3+) were done using an aqueous green tea extract where it acts as reducing as well as capping agent. The effect of iron precursor to green tea extract ratio and reaction temperature was studied. The MNPs were characterized by x-ray diffraction, Fourier transform infrared spectroscopy, field-emission scanning electron microscopy, dynamic light scattering and vibrating sample magnetometer. It was observed that the reaction temperature strongly affects the magnetic and structural properties of MNPs. The magnetic measurements study showed that Fe3O4 MNPs are superparamagnetic at 300 K, while at 60 K have ferromagnetic as well as superparamagnetic contributions.

  13. Structural characterization of mesoporous magnetite nanoparticles synthesized using the leaf extract of Calliandra haematocephala and their photocatalytic degradation of malachite green dye

    Science.gov (United States)

    Sirdeshpande, Karthikey Devadatta; Sridhar, Anushka; Cholkar, Kedar Mohan; Selvaraj, Raja

    2018-03-01

    A simple method for the synthesis of magnetite nanoparticles using the leaf extract of Calliandra haematocephala has been developed. UV-Vis spectrum showed a characteristic strong absorption band. SEM image revealed the bead-like spherical nanoparticles. EDS showed the prominent peaks for elemental iron and oxygen. PXRD patterns confirmed the crystalline nature and the average crystallite size of 7.45 nm. In addition, the lattice parameter value was calculated to be 8.413 Å, close to Fe3O4 nanoparticles. BET analysis disclosed the total specific surface area of the nanoparticles as 63.89 m2/g and the mesoporous structure of the nanoparticles with a pore radius of 34.18 Å. FTIR studies showed the specific bands at 599.82 and 472.53 cm-1, typical for Fe3O4 nanoparticles. The photocatalytic efficacy of the nanoparticles was demonstrated against the degradation of malachite green dye under sunlight irradiation and the photocatalytic degradation constant was calculated as 0.0621 min-1.

  14. Precursor-Less Coating of Nanoparticles in the Gas Phase

    Directory of Open Access Journals (Sweden)

    Tobias V. Pfeiffer

    2015-03-01

    Full Text Available This article introduces a continuous, gas-phase method for depositing thin metallic coatings onto (nanoparticles using a type of physical vapor deposition (PVD at ambient pressure and temperature. An aerosol of core particles is mixed with a metal vapor cloud formed by spark ablation by passing the aerosol through the spark zone using a hollow electrode configuration. The mixing process rapidly quenches the vapor, which condenses onto the core particles at a timescale of several tens of milliseconds in a manner that can be modeled as bimodal coagulation. Gold was deposited onto core nanoparticles consisting of silver or polystyrene latex, and silver was deposited onto gold nanoparticles. The coating morphology depends on the relative surface energies of the core and coating materials, similar to the growth mechanisms known for thin films: a coating made of a substance having a high surface energy typically results in a patchy coverage, while a coating material with a low surface energy will normally “wet” the surface of a core particle. The coated particles remain gas-borne, allowing further processing.

  15. Nanogeochemistry of hydrothermal magnetite

    Science.gov (United States)

    Deditius, Artur P.; Reich, Martin; Simon, Adam C.; Suvorova, Alexandra; Knipping, Jaayke; Roberts, Malcolm P.; Rubanov, Sergey; Dodd, Aaron; Saunders, Martin

    2018-06-01

    Magnetite from hydrothermal ore deposits can contain up to tens of thousands of parts per million (ppm) of elements such as Ti, Si, V, Al, Ca, Mg, Na, which tend to either structurally incorporate into growth and sector zones or form mineral micro- to nano-sized particles. Here, we report micro- to nano-structural and chemical data of hydrothermal magnetite from the Los Colorados iron oxide-apatite deposit in Chile, where magnetite displays both types of trace element incorporation. Three generations of magnetites (X-Z) were identified with concentrations of minor and trace elements that vary significantly: SiO2, from below detection limit (bdl) to 3.1 wt%; Al2O3, 0.3-2.3 wt%; CaO, bdl-0.9 wt%; MgO, 0.02-2.5 wt%; TiO2, 0.1-0.4 wt%; MnO, 0.04-0.2 wt%; Na2O, bdl-0.4 wt%; and K2O, bdl-0.4 wt%. An exception is V2O3, which is remarkably constant, ranging from 0.3 to 0.4 wt%. Six types of crystalline nanoparticles (NPs) were identified by means of transmission electron microscopy in the trace element-rich zones, which are each a few micrometres wide: (1) diopside, (2) clinoenstatite; (3) amphibole, (4) mica, (5) ulvöspinel, and (6) Ti-rich magnetite. In addition, Al-rich nanodomains, which contain 2-3 wt% of Al, occur within a single crystal of magnetite. The accumulation of NPs in the trace element-rich zones suggest that they form owing to supersaturation from a hydrothermal fluid, followed by entrapment during continuous growth of the magnetite surface. It is also concluded that mineral NPs promote exsolution of new phases from the mineral host, otherwise preserved as structurally bound trace elements. The presence of abundant mineral NPs in magnetite points to a complex incorporation of trace elements during growth, and provides a cautionary note on the interpretation of micron-scale chemical data of magnetite.

  16. Theoretical and experimental influence of aerosol assisted CVD parameters on the microstructural properties of magnetite nanoparticles and their response on the removal efficiency of arsenic

    Energy Technology Data Exchange (ETDEWEB)

    Hernández-Salcedo, P.G.; Amézaga-Madrid, P., E-mail: patricia.amezaga@cimav.edu.mx; Monárrez-Cordero, B.E.; Antúnez-Flores, W.; Pizá-Ruiz, P.; Leyva-Porras, C.; Ornelas-Gutiérrez, C.; Miki-Yoshida, M.

    2015-09-15

    The development and optimization of methodologies to generate magnetite nanoparticles is currently an innovation topic. For a desired application such as arsenic removal from waste water, the generation of these nanostructures with specific microstructural properties is determinant. Therefore, it is necessary to understand the phenomenon during the nanoparticles formation process. Thus, in this work it is reported the influence of synthesis parameters of AACVD technique on the formation of magnetite nanoparticles. Parameters were according to: (1) synthesis temperature, (2) tubular reactor diameter, (3) concentration of the precursor solution and type of solvent, (4) carrier gas flow and (5) solvent type in the collection process. The effect of these synthesis parameters on the morphology, size and microstructure are discussed in detail and related with the mechanism of formation of the particles. Theoretical simulations were performed on two of these parameters (1 and 4). The microstructure and surface morphology of the different nanostructures obtained were characterized by field emission scanning electron and transmission electron microscopy. Subsequently two materials, were selected for further microstructural analysis. Finally, to determine the removal efficiency in the two materials the arsenic adsorption was evaluated. A major contribution of this work was the calculation of the number of spherical particles formed from a single drop of precursor solution. This calculation matched with the value found experimentally.

  17. Preparation of amine coated silver nanoparticles using ...

    Indian Academy of Sciences (India)

    Administrator

    concentrations without the precipitation of particles. In this work, an analysis of the temperature influ- ence on the precipitation of silver nanoparticles was carried out. Also, the nanoparticles were func- tionalized using triethylenetetramine in order to im- prove the adhesion between the epoxy resin and the filler.

  18. Synthesis and characterization of magnetite nanoparticles encapsulated in a bovine hemoglobin microgel

    Science.gov (United States)

    Mody, Puja J.

    This study shows the successful synthesis and characterization of a novel material that is composed of iron oxide particles within a protein gel. During the synthesis, bovine hemoglobin surrounds the forming Fe 3O4 nanoparticles, resulting in a biocompatible hydrogel, which has the potential to be used as a targeted drug delivery vehicle and as an MRI contrast agent. The structure, size, and thermal stability of these hydrogel complexes were analyzed using a range of techniques. Powder x-ray diffraction and infrared spectroscopy indicated the presence of Fe3O 4 and hemoglobin without significant interactions between particles in the solid state. Microscopy analysis determined the average size of these microgel complexes to be 4-9 mum2 in area (˜2-3 mum in diameter), and DSC analysis indicated that none of the microgels exhibited a denaturing or unfolding transition below 54°C regardless of the iron: hemoglobin ratio. Initial testing has been performed on the ability of these materials to act as magnetically activated drug delivery vehicles. Other pertinent tests (for magnetic properties and MRI applicability) are currently proceeding at external labs.

  19. Surface spins disorder in uncoated and SiO2 coated maghemite nanoparticles

    International Nuclear Information System (INIS)

    Zeb, F.; Nadeem, K.; Shah, S. Kamran Ali; Kamran, M.; Gul, I. Hussain; Ali, L.

    2017-01-01

    We studied the surface spins disorder in uncoated and silica (SiO 2 ) coated maghemite (γ-Fe 2 O 3 ) nanoparticles using temperature and time dependent magnetization. The average crystallite size for SiO 2 coated and uncoated nanoparticles was about 12 and 29 nm, respectively. Scanning electron microscopy (SEM) showed that the nanoparticles are spherical in shape and well separated. Temperature scans of zero field cooled (ZFC)/field cooled (FC) magnetization measurements showed lower average blocking temperature (T B ) for SiO 2 coated maghemite nanoparticles as compared to uncoated nanoparticles. The saturation magnetization (M s ) of SiO 2 coated maghemite nanoparticles was also lower than the uncoated nanoparticles and is attributed to smaller average crystallite size of SiO 2 coated nanoparticles. For saturation magnetization vs. temperature data, Bloch's law (M(T)= M(0).(1− BT b )) was fitted well for both uncoated and SiO 2 coated nanoparticles and yields: B =3×10 −7 K -b , b=2.22 and B=0.0127 K -b , b=0.57 for uncoated and SiO 2 coated nanoparticles, respectively. Higher value of B for SiO 2 coated nanoparticles depicts decrease in exchange coupling due to enhanced surface spins disorder (broken surface bonds) as compared to uncoated nanoparticles. The Bloch's exponent b was decreased for SiO 2 coated nanoparticles which is due to their smaller average crystallite size or finite size effects. Furthermore, a sharp increase of coercivity at low temperatures (<25 K) was observed for SiO 2 coated nanoparticles which is also due to contribution of increased surface anisotropy or frozen surface spins in these smaller nanoparticles. The FC magnetic relaxation data was fitted to stretched exponential law which revealed slower magnetic relaxation for SiO 2 coated nanoparticles. All these measurements revealed smaller average crystallite size and enhanced surface spins disorder in SiO 2 coated nanoparticles than in uncoated γ-Fe 2 O 3 nanoparticles

  20. Studies on the role of unsaturation in the fatty acid surfactant molecule on the thermal conductivity of magnetite nanofluids.

    Science.gov (United States)

    Lenin, Ramanujam; Joy, Pattayil Alias

    2017-11-15

    To study the role of unsaturation in the surfactant molecule on the thermal conductivity of magnetite nanofluids, four different fatty acid (stearic, oleic, linoleic, and linolenic acids with different degree of unsaturation) coated magnetite nanoparticles of comparable size are prepared and dispersed in toluene. It is found that the nanofluid with the saturated fatty acid coated nanoparticles show larger viscosity than the fluid with the unsaturated fatty acid coated particles at all concentrations. Thermal conductivity studies show enhancement only above a critical concentration for all fluids. The critical concentration for thermal conductivity enhancement varies with the surfactant, possibly due to the difference in the degree of aggregation of the nanoparticles in the fluid, because of the difference in the conformation of the surfactant molecules on the nanoparticle's surface. The experimental thermal conductivity follows the Maxwell model at higher concentrations. From the overall studies, it is observed that the thermal conductivity of the fluids with aggregated or assembled nanoparticles shows slightly larger enhancement than that of the fluids with isolated particles. However, in the presence of a magnetic field, the fluids with isolated nanoparticles showed relatively larger enhancement, possibly due to the easy response of the isolated magnetite nanoparticles to the applied field. Copyright © 2017 Elsevier Inc. All rights reserved.

  1. Silica coated ionic liquid templated mesoporous silica nanoparticles ...

    African Journals Online (AJOL)

    A series of long chain pyridinium based ionic liquids 1-tetradecylpyridinium bromide, 1-hexadecylpyridinium bromide and 1-1-octadecylpyridinium bromide were used as templates to prepare silica coated mesoporous silica nanoparticles via condensation method under basic condition. The effects of alkyl chain length on ...

  2. Silica coating of nanoparticles by the sonogel process.

    Science.gov (United States)

    Chen, Quan; Boothroyd, Chris; Tan, Gim Hong; Sutanto, Nelvi; Soutar, Andrew McIntosh; Zeng, Xian Ting

    2008-02-05

    A modified aqueous sol-gel route was developed using ultrasonic power for the silica coating of indium tin oxide (ITO) nanoparticles. In this approach, organosilane with an amino functional group was first used to cover the surface of as-received nanoparticles. Subsequent silica coating was initiated and sustained under power ultrasound irradiation in an aqueous mixture of surface-treated particles and epoxy silane. This process resulted in a thin but homogeneous coverage of silica on the particle surface. Particles coated with a layer of silica show better dispersability in aqueous and organic media compared with the untreated powder. Samples were characterized by high-resolution transmission electron microscopy (HRTEM), X-ray photoelectron spectroscopy (XPS), and the zeta potential.

  3. Structural characterization of copolymer embedded magnetic nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Nedelcu, G.G., E-mail: ggnedelcu@yahoo.com [Faculty of Physics, University “Alexandru Ioan Cuza”, Carol I Bulevard, Nr.11, 700506 Iasi (Romania); Nastro, A.; Filippelli, L. [Department of Chemistry and Chemical Technology, University of Calabria, Via P. Bucci, 87036 Arcavacata di Rende, Cosenza (Italy); Cazacu, M.; Iacob, M. [Institute of Macromolecular Chemistry “Petru Poni”, Aleea Grigore Ghica Voda, nr. 41A, 700487 Iasi (Romania); Rossi, C. Oliviero [Department of Chemistry and Chemical Technology, University of Calabria, Via P. Bucci, 87036 Arcavacata di Rende, Cosenza (Italy); Popa, A.; Toloman, D. [National Institute for Research and Development of Isotopic and Molecular Technologies, 65-103 Donath Str., 400293 Cluj-Napoca 5 (Romania); Dobromir, M.; Iacomi, F. [Faculty of Physics, University “Alexandru Ioan Cuza”, Carol I Bulevard, Nr.11, 700506 Iasi (Romania)

    2015-10-15

    Highlights: • The emulsion polymerization method was used to synthesize three samples of poly(methyl methacrylate-co-acrylic acid) coated magnetite obtained before through co-precipitation technique. • Poly(methyl methacrylate-co-acrylic acid) coated magnetite nanoparticles were prepared having spherical shape and dimensions between 13 and 16 nm without agglomerations. • Fourier transform infrared spectra have found that the magnetite was pure and spectral characteristics of PMMA-co-AAc were present. • The electron spin resonance spectra revealed that interactions between nanoparticles are very weak due to the fact that the nanoparticles have been individually embedded in polymer. • The resonance field values as function of temperature demonstrate that the presence of polymer has not modified essentially its magnetic properties, except that at temperatures below 140 K there was a change due to decreasing of the magnetic anisotropy. - Abstract: Small magnetic nanoparticles (Fe{sub 3}O{sub 4}) were synthesized by co-precipitation and coated by emulsion polymerization with poly(methyl methacrylate-co-acrylic acid) (PMMA-co-AAc) to create surface functional groups that can attach drug molecules and other biomolecules. The coated and uncoated magnetite nanoparticles were stored for two years in normal closed ships and than characterized by Fourier transform infrared spectroscopy, X-ray diffraction, transmission electron microscopy, vibrating sample magnetometry, and electron paramagnetic resonance spectroscopy. The solid phase transformation of magnetite to maghemite, as well as an increase in particle size were evidenced for the uncoated nanoparticles. The coated nanoparticles preserved their magnetite structure and magnetic properties. The influences of monomers and surfactant layers on interactions between the magnetic nanoparticles evidenced that the thickness of the polymer has a significant effect on magnetic properties.

  4. Tribological behavior of polytetrafluoroethylene coating reinforced with black phosphorus nanoparticles

    Science.gov (United States)

    Peng, Shiguang; Guo, Yue; Xie, Guoxin; Luo, Jianbin

    2018-05-01

    This study compares the tribological performance of polytetrafluoroethylene (PTFE) thin film coating reinforced with black phosphorus (BP) or ball-milled graphite (BMG) nanoparticles, so as to elucidate their mechanism of action under reciprocating sliding test conditions. PTFE coatings with 0.5 wt.% BMG (BMG/PTFE) and 0.5 wt.% BP (BP/PTFE) were prepared on GCr15 bearing steel disk by using a spin coater. The friction and wear tests were carried out by using the ball-on-disk tribometer under a normal load of 1 N (contact pressure: 780 MPa), a frequency of 2 Hz, and 4.2 mm sliding displacement amplitude. The surface roughness, wear volume and surface morphology of the coatings were characterized by the three-dimensional white light, and Energy Dispersive X-ray Detector (EDX) analysis coupled with environmental scanning electron microscope (ESEM). It is found that BP/PTFE coating has better anti-wear and anti-friction performances than those of pure PTFE or BMG/PTFE coating. The coating with BP nanoparticles shows excellent tribological properties with the wear volume decreased from 3.52 × 106 μm3 to 1.64 × 106 μm3 and the coefficient of friction (COF) decreased from 0.117 to 0.046. More importantly, the BP layer probably expands and absorbs much energy due to its negative Poisson's ratio phenomenon under reciprocating sliding, and effectively reducing furrow and adhesive wear.

  5. Substrates coated with silver nanoparticles as a neuronal regenerative material

    Directory of Open Access Journals (Sweden)

    Alon N

    2014-05-01

    Full Text Available Noa Alon,1,3,* Yana Miroshnikov,2,3,* Nina Perkas,2,3 Ifat Nissan,2,3 Aharon Gedanken,2,3 Orit Shefi1,31Faculty of Engineering, 2Department of Chemistry, 3Bar-Ilan Institute of Nanotechnology and Advanced Materials, Bar-Ilan University, Ramat Gan, Israel*These authors contributed equally to this workAbstract: Much effort has been devoted to the design of effective biomaterials for nerve regeneration. Here, we report the novel use of silver nanoparticles (AgNPs as regenerative agents to promote neuronal growth. We grew neuroblastoma cells on surfaces coated with AgNPs and studied the effect on the development of the neurites during the initiation and the elongation growth phases. We find that the AgNPs function as favorable anchoring sites, and the growth on the AgNP-coated substrates leads to a significantly enhanced neurite outgrowth. Cells grown on substrates coated with AgNPs have initiated three times more neurites than cells grown on uncoated substrates, and two times more than cells grown on substrates sputtered with a plain homogenous layer of silver. The growth of neurites on AgNPs in the elongation phase was enhanced as well. A comparison with substrates coated with gold nanoparticles (AuNPs and zinc oxide nanoparticles (ZnONPs demonstrated a clear silver material-driven promoting effect, in addition to the nanotopography. The growth on substrates coated with AgNPs has led to a significantly higher number of initiating neurites when compared to substrates coated with AuNPs or ZnONPs. All nanoparticle-coated substrates affected and promoted the elongation of neurites, with a significant positive maximal effect for the AgNPs. Our results, combined with the well-known antibacterial effect of AgNPs, suggest the use of AgNPs as an attractive nanomaterial – with dual activity – for neuronal repair studies.Keywords: nerve regeneration, nanotopography, antibacterial material, neuroblastoma, gold nanoparticles, zinc oxide nanoparticles

  6. Stability of polyvinyl alcohol-coated biochar nanoparticles in brine

    Energy Technology Data Exchange (ETDEWEB)

    Griffith, Christopher, E-mail: cgriffith@utexas.edu; Daigle, Hugh [University of Texas at Austin, Department of Petroleum and Geosystems Engineering (United States)

    2017-01-15

    This paper reports on the dispersion stability of 150 nm polyvinyl alcohol coated biochar nanoparticles in brine water. Biochar is a renewable, carbon based material that is of significant interest for enhanced oil recovery operations primarily due to its wide ranging surface properties, low cost of synthesis, and low environmental toxicity. Nanoparticles used as stabilizing agents for foams (and emulsions) or in nanofluids have emerged as potential alternatives to surfactants for subsurface applications due to their improved stability at reservoir conditions. If, however, the particles are not properly designed, they are susceptible to aggregation because of the high salinity brines typical of oil and gas reservoirs. Attachment of polymers to the nanoparticle surface, through covalent bonds, provides steric stabilization, and is a necessary step. Our results show that as the graft density of polyvinyl alcohol increases, so too does the stability of nanoparticles in brine solutions. A maximum of 34 wt% of 50,000 Da polyvinyl alcohol was grafted to the particle surface, and the size of the particles was reduced from ~3500 nm (no coating) to 350 nm in brine. After 24 h, the particles had a size of ~500 nm, and after 48 h completely aggregated. 100,000 Da PVA coated at 24 wt% on the biochar particles were stable in brine for over 1 month with no change in mean particle size of ~330 nm.

  7. Optical Fiber Sensors Based on Nanoparticle-Embedded Coatings

    Directory of Open Access Journals (Sweden)

    Aitor Urrutia

    2015-01-01

    Full Text Available The use of nanoparticles (NPs in scientific applications has attracted the attention of many researchers in the last few years. The use of NPs can help researchers to tune the physical characteristics of the sensing coating (thickness, roughness, specific area, refractive index, etc. leading to enhanced sensors with response time or sensitivity better than traditional sensing coatings. Additionally, NPs also offer other special properties that depend on their nanometric size, and this is also a source of new sensing applications. This review focuses on the current status of research in the use of NPs within coatings in optical fiber sensing. Most used sensing principles in fiber optics are briefly described and classified into several groups: absorbance-based sensors, interferometric sensors, fluorescence-based sensors, fiber grating sensors, and resonance-based sensors, among others. For each sensor group, specific examples of the utilization of NP-embedded coatings in their sensing structure are reported.

  8. Synthesis and characterization of pHLIP® coated gold nanoparticles.

    Science.gov (United States)

    Daniels, Jennifer L; Crawford, Troy M; Andreev, Oleg A; Reshetnyak, Yana K

    2017-07-01

    Novel approaches in synthesis of spherical and multispiked gold nanoparticles coated with polyethylene glycol (PEG) and pH Low Insertion Peptide (pHLIP ® ) were introduced. The presence of a tumor-targeting pHLIP ® peptide in the nanoparticle coating enhances the stability of particles in solution and promotes a pH-dependent cellular uptake. The spherical particles were prepared with sodium citrate as a gold reducing agent to form particles of 7.0±2.5 nm in mean metallic core diameter and ∼43 nm in mean hydrodynamic diameter. The particles that were injected into tumors in mice (21 µg of gold) were homogeneously distributed within a tumor mass with no staining of the muscle tissue adjacent to the tumor. Up to 30% of the injected gold dose remained within the tumor one hour post-injection. The multispiked gold nanoparticles with a mean metallic core diameter of 146.0±50.4 nm and a mean hydrodynamic size of ~161 nm were prepared using ascorbic acid as a reducing agent and disk-like bicelles as a template. Only the presence of a soft template, like bicelles, ensured the appearance of spiked nanoparticles with resonance in the near infrared region. The irradiation of spiked gold nanoparticles by an 805 nm laser led to the time- and concentration-dependent increase of temperature. Both pHLIP ® and PEG coated gold spherical and multispiked nanoparticles might find application in radiation and thermal therapies of tumors.

  9. Synthesis and characterization of pHLIP® coated gold nanoparticles

    Directory of Open Access Journals (Sweden)

    Jennifer L. Daniels

    2017-07-01

    Full Text Available Novel approaches in synthesis of spherical and multispiked gold nanoparticles coated with polyethylene glycol (PEG and pH Low Insertion Peptide (pHLIP® were introduced. The presence of a tumor-targeting pHLIP® peptide in the nanoparticle coating enhances the stability of particles in solution and promotes a pH-dependent cellular uptake. The spherical particles were prepared with sodium citrate as a gold reducing agent to form particles of 7.0±2.5 nm in mean metallic core diameter and ∼43 nm in mean hydrodynamic diameter. The particles that were injected into tumors in mice (21 µg of gold were homogeneously distributed within a tumor mass with no staining of the muscle tissue adjacent to the tumor. Up to 30% of the injected gold dose remained within the tumor one hour post-injection. The multispiked gold nanoparticles with a mean metallic core diameter of 146.0±50.4 nm and a mean hydrodynamic size of ~161 nm were prepared using ascorbic acid as a reducing agent and disk-like bicelles as a template. Only the presence of a soft template, like bicelles, ensured the appearance of spiked nanoparticles with resonance in the near infrared region. The irradiation of spiked gold nanoparticles by an 805 nm laser led to the time- and concentration-dependent increase of temperature. Both pHLIP® and PEG coated gold spherical and multispiked nanoparticles might find application in radiation and thermal therapies of tumors.

  10. Sectorial oscillation of acoustically levitated nanoparticle-coated droplet

    Science.gov (United States)

    Zang, Duyang; Chen, Zhen; Geng, Xingguo

    2016-01-01

    We have investigated the dynamics of a third mode sectorial oscillation of nanoparticle-coated droplets using acoustic levitation in combination with active modulation. The presence of nanoparticles at the droplet surface changes its oscillation amplitude and frequency. A model linking the interfacial rheology and oscillation dynamics has been proposed in which the compression modulus ɛ of the particle layer is introduced into the analysis. The ɛ obtained with the model is in good agreement with that obtained by the Wilhelmy plate approach, highlighting the important role of interfacial rheological properties in the sectorial oscillation of droplets.

  11. The polymerisation of oligo(ethylene glycol methyl ether) methacrylate from a multifunctional poly(ethylene imine) derived amide : a stabiliser for the synthesis and dispersion of magnetite nanoparticles

    NARCIS (Netherlands)

    Kleine, A.; Altan, C.L.; Yarar, U.E.; Sommerdijk, N.A.J.M.; Bucak, S.; Holder, S.J.

    2014-01-01

    A facile synthetic route to poly(ethylene imine)-graft-poly(oligo(ethylene glycol methyl ether)) (PEI-graft-POEGMA) functionalised superparamagnetic magnetite nanoparticles is described. The polymerisation of OEGMA from a model molecular amide demonstrated the feasibility of POEGMA synthesis under

  12. Wet milling versus co-precipitation in magnetite ferrofluid preparation

    Directory of Open Access Journals (Sweden)

    Almásy László

    2015-01-01

    Full Text Available Various uses of ferrofluids for technical applications continuously raise the interest in improvement and optimization of preparation methods. This paper deals with preparation of finely granulated magnetite particles coated with oleic acid in hydrocarbon suspensions following either chemical co-precipitation from iron salt precursors or wet milling of micron size magnetite powder with the goal to compare the benefits and disadvantages of each method. Microstructural measurements showed that both methods gave similar magnetite particle size of 10-15 nm. Higher saturation magnetization was achieved for the wet-milled magnetite suspension compared to relatively rapid co-precipitation synthesis. Different efficacies of ferrophase incorporation into kerosene could be related to the different mechanisms of oleic acid bonding to nanoparticle surface. The comparative data show that wet milling represents a practicable alternative to the traditional co-precipitation since despite of longer processing time, chemicals impact on environment can be avoided as well as the remnant water in the final product.

  13. Photoluminescent polysaccharide-coated germanium(IV) oxide nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Lobaz, Volodymyr; Rabyk, Mariia; Pánek, Jiří; Doris, E.; Nallet, F.; Štěpánek, Petr; Hrubý, Martin

    2016-01-01

    Roč. 294, č. 7 (2016), s. 1225-1235 ISSN 0303-402X R&D Projects: GA MŠk(CZ) 7AMB14FR027; GA ČR(CZ) GA13-08336S; GA MZd(CZ) NV15-25781A Institutional support: RVO:61389013 Keywords : germanium oxide nanoparticles * polysaccharide coating * photoluminescent label Subject RIV: CD - Macromolecular Chemistry Impact factor: 1.723, year: 2016

  14. Thermal Stability and Magnetic Properties of Polyvinylidene Fluoride/Magnetite Nanocomposites

    OpenAIRE

    Ouyang, Zen-Wei; Chen, Erh-Chiang; Wu, Tzong-Ming

    2015-01-01

    This work describes the thermal stability and magnetic properties of polyvinylidene fluoride (PVDF)/magnetite nanocomposites fabricated using the solution mixing technique. The image of transmission electron microscopy for PVDF/magnetite nanocomposites reveals that the 13 nm magnetite nanoparticles are well distributed in PVDF matrix. The electroactive β-phase and piezoelectric responses of PVDF/magnetite nanocomposites are increased as the loading of magnetite nanoparticles increases. The pi...

  15. Surface modified superparamagnetic nanoparticles: Interaction with fibroblasts in primary cell culture

    Energy Technology Data Exchange (ETDEWEB)

    Chapa Gonzalez, Christian; Roacho Pérez, Jorge A.; Martínez Pérez, Carlos A.; Olivas Armendáriz, Imelda [Instituto de Ingeniería y Tecnología, Universidad Autónoma de Ciudad Juárez, Ave. Del Charro #610 norte, Col. Partido Romero, C.P. 32320 Cd. Juárez, Chihuahua, México (Mexico); Jimenez Vega, Florinda [Instituto de Ciencias Biomédicas, Universidad Autónoma de Ciudad Juárez, Anillo envolvente del PRONAF y Estocolmo, C.P. 32320 Cd. Juárez, Chihuahua, México (Mexico); Castrejon Parga, Karen Y. [Instituto de Ingeniería y Tecnología, Universidad Autónoma de Ciudad Juárez, Ave. Del Charro #610 norte, Col. Partido Romero, C.P. 32320 Cd. Juárez, Chihuahua, México (Mexico); Garcia Casillas, Perla E., E-mail: pegarcia@uacj.mx [Instituto de Ingeniería y Tecnología, Universidad Autónoma de Ciudad Juárez, Ave. Del Charro #610 norte, Col. Partido Romero, C.P. 32320 Cd. Juárez, Chihuahua, México (Mexico)

    2014-12-05

    Highlights: • An inorganic layer before an organic material shell onto MNPs improves cell viability. • The coating type and the concentration of nanoparticles directly affect cell viability. • Modified magnetite nanoparticles with organic and inorganic materials was developed. - Abstract: The development of a variety of medical applications such as drug delivery, cell labeling, and medical imaging have been possible owing to the unique features exhibited by magnetic nanoparticles. Nanoparticle–cell interaction is related to the surface aspects of nanoparticle, which may be described based on their chemistry or inorganic/organic characteristics. The coating on particle surface reduces the inter-particle interactions and provides properties such as biocompatibility. Among the coating materials used for nanoparticles employed in biomedical applications, oleic acid is one of the most utilized due to its biocompatibility. However, a major drawback with this naturally occurring fatty acid is that it is easily oxidized by cells and this reduces their performance in biomedical applications. In order to avoid the direct contact of the cell with the magnetite particle, coating with an inorganic material prior to the oleic acid shell would be effective. This would retard the magnetite dissociation thereby improve the cell viability. Here we report our investigation on the effect of surface modified magnetite nanoparticles (MNPs) on the cell viability using primary cultures incubated with those particles. We prepared magnetite nanoparticles by chemical co-precipitation method; nanoparticle surface was first modified by silanol condensation followed by chemisorption of oleic acid. All nanostructures have a particle size less than 100 nm, depending on the material coating and superparamagnetic behavior. The saturated magnetizations (M{sub s}) of the magnetite samples coated with oleic acid (MAO; 49.15 emu/g) and double shell silica-oleic acid (MSAO; 46.16 emu/g) are

  16. Laser-assisted one-pot fabrication of calcium phosphate-based submicrospheres with internally crystallized magnetite nanoparticles through chemical precipitation.

    Science.gov (United States)

    Nakamura, Maki; Oyane, Ayako; Sakamaki, Ikuko; Ishikawa, Yoshie; Shimizu, Yoshiki; Kawaguchi, Kenji

    2015-04-14

    In this paper, we have further developed our simple (one-pot) and rapid (short irradiation time) laser fabrication process of submicrometer spheres composed of amorphous calcium iron phosphate. In our previous process, laser irradiation was applied to a calcium phosphate (CaP) reaction mixture supplemented with ferric ions (Fe(3+)) as a light-absorbing agent. Because the intention of the present study was to fabricate magnetite-encapsulated CaP-based submicrometer spheres, ferrous ions (Fe(2+)) were used as a light-absorbing agent rather than ferric ions. The ferrous ions served as a light-absorbing agent and facilitated the fabrication of submicrometer and micrometer spheres of amorphous calcium iron phosphate. The sphere formation and growth were better promoted by the use of ferrous ions as compared with the use of ferric ions. The chemical composition of the spheres was controllable through adjustment of the experimental conditions. By the addition of sodium hydroxide to the CaP reaction mixture supplemented with ferrous ions, fabrication of CaP-based magnetic submicrometer spheres was successfully achieved. Numerous magnetite and wüstite nanoparticles were coprecipitated or segregated into the CaP-based spherical amorphous matrix via light-material interaction during the CaP precipitation process. The magnetic properties of the magnetite and wüstite formed in the CaP-based spheres were investigated by magnetization measurements. The present process and the resulting CaP-based spheres are expected to have great potential for biomedical applications.

  17. Precipitation synthesis and magnetic properties of self-assembled magnetite-chitosan nanostructures

    Energy Technology Data Exchange (ETDEWEB)

    Bezdorozhev, Oleksii; Kolodiazhnyi, Taras; Vasylkiv, Oleg, E-mail: oleg.vasylkiv@nims.go.jp

    2017-04-15

    This paper reports the synthesis and magnetic properties of unique magnetite-chitosan nanostructures synthesized by the chemical precipitation of magnetite nanoparticles in the presence of chitosan. The influence of varying synthesis parameters on the morphology of the magnetic composites is determined. Depending on the synthesis parameters, magnetite-chitosan nanostructures of spherical (9–18 nm), rice-seed-like (75–290 nm) and lumpy (75–150 nm) shapes were obtained via self-assembly. Spherical nanostructures encapsulated by a 9–15 nm chitosan layer were assembled as well. The prospective morphology of the nanostructures is combined with their excellent magnetic characteristics. It was found that magnetite-chitosan nanostructures are ferromagnetic and pseudo-single domain. Rice-seed-like nanostructures exhibited a coercivity of 140 Oe and saturation magnetization of 56.7 emu/g at 300 K. However, a drop in the magnetic properties was observed for chitosan-coated spherical nanostructures due to the higher volume fraction of chitosan. - Highlights: • Magnetite-chitosan nanostructures are synthesized via self-assembly. • Different morphology can be obtained by adjusting the synthesis parameters. • An attractive combination of magnetic properties and morphology is obtained. • Magnetite-chitosan nanostructures are ferrimagnetic and pseudo-single domain.

  18. Precipitation synthesis and magnetic properties of self-assembled magnetite-chitosan nanostructures

    International Nuclear Information System (INIS)

    Bezdorozhev, Oleksii; Kolodiazhnyi, Taras; Vasylkiv, Oleg

    2017-01-01

    This paper reports the synthesis and magnetic properties of unique magnetite-chitosan nanostructures synthesized by the chemical precipitation of magnetite nanoparticles in the presence of chitosan. The influence of varying synthesis parameters on the morphology of the magnetic composites is determined. Depending on the synthesis parameters, magnetite-chitosan nanostructures of spherical (9–18 nm), rice-seed-like (75–290 nm) and lumpy (75–150 nm) shapes were obtained via self-assembly. Spherical nanostructures encapsulated by a 9–15 nm chitosan layer were assembled as well. The prospective morphology of the nanostructures is combined with their excellent magnetic characteristics. It was found that magnetite-chitosan nanostructures are ferromagnetic and pseudo-single domain. Rice-seed-like nanostructures exhibited a coercivity of 140 Oe and saturation magnetization of 56.7 emu/g at 300 K. However, a drop in the magnetic properties was observed for chitosan-coated spherical nanostructures due to the higher volume fraction of chitosan. - Highlights: • Magnetite-chitosan nanostructures are synthesized via self-assembly. • Different morphology can be obtained by adjusting the synthesis parameters. • An attractive combination of magnetic properties and morphology is obtained. • Magnetite-chitosan nanostructures are ferrimagnetic and pseudo-single domain.

  19. Molecular Simulations of Gold Nanoparticles Coated With Self-Assembled Alkanethiolate Monolayers

    National Research Council Canada - National Science Library

    Henz, Brian J; Fischer, James W; Zachariah, Michael R

    2006-01-01

    In order to utilize the novel electrical, magnetic, optical, and physical properties of coated metal nanoparticles, one must be able to efficiently predict the nanoparticle size-dependent properties...

  20. Antimicrobial activity of tantalum oxide coatings decorated with Ag nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Cao, Huiliang, E-mail: hlc@mail.sic.ac.cn; Meng, Fanhao; Liu, Xuanyong, E-mail: xyliu@mail.sic.ac.cn [State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050 (China)

    2016-07-15

    Silver plasma immersion ion implantation was used to decorate silver nanoparticles (Ag NPs) on tantalum oxide (TO) coatings. The coatings acted against bacterial cells (Staphylococcus epidermidis) in the dark by disrupting their integrity. The action was independent of silver release and likely driven by the electron storage capability of the Schottky barriers established at the interfaces between Ag NPs and the TO support. Moreover, no apparent side effect on the adhesion and differentiation of rat bone mesenchymal stem cells was detected when using Ag NPs-modified TO coatings. These results demonstrate that decoration of tantalum oxide using Ag NPs could be a promising procedure for improving the antibacterial properties for orthopedic and dental implants.

  1. Microwave-assisted silica coating and photocatalytic activities of ZnO nanoparticles

    International Nuclear Information System (INIS)

    Siddiquey, Iqbal Ahmed; Furusawa, Takeshi; Sato, Masahide; Suzuki, Noboru

    2008-01-01

    A new and rapid method for silica coating of ZnO nanoparticles by the simple microwave irradiation technique is reported. Silica-coated ZnO nanoparticles were characterized by X-ray photoelectron spectroscopy (XPS), Fourier transform infrared spectroscopy (FT-IR), high-resolution transmission electron microscopy (HR-TEM), CHN elemental analysis and zeta potential measurements. The FT-IR spectra and XPS clearly confirmed the silica coating on ZnO nanoparticles. The results of XPS analysis showed that the elements in the coating at the surface of the ZnO nanoparticles were Zn, O and Si. HR-TEM micrographs revealed a continuous and uniform dense silica coating layer of about 3 nm in thickness on the surface of ZnO nanoparticles. In addition, the silica coating on the ZnO nanoparticles was confirmed by the agreement in the zeta potential of the silica-coated ZnO nanoparticles with that of SiO 2 . The results of the photocatalytic degradation of methylene blue (MB) in aqueous solution showed that silica coating effectively reduced the photocatalytic activity of ZnO nanoparticles. Silica-coated ZnO nanoparticles showed excellent UV shielding ability and visible light transparency

  2. Surface plasmon resonance enhanced light absorption and wavelength tuneable in gold-coated iron oxide spherical nanoparticle

    Science.gov (United States)

    Dasri, Thananchai; Chingsungnoen, Artit

    2018-06-01

    Surface plasmon in nano-sized particles, such as gold, silver, copper and their composites, has recently attracted a great deal of attention due to its possible uses in many applications, especially in life sciences. It is desirable for application devices with a tenability of surface plasmon wavelength and optical properties enhancement. This article presents enhanced optical light absorption and tunable wavelength in gold-coated magnetite (Fe3O4@Au core-shell) nanoparticles embedded in water using the theoretical method of discrete dipole approximation (DDA). The absorption spectra in the wavelengths from 350 to 900 nm were found to be the spectra obtained from Fe3O4@Au core-shell nanoparticles, and when compared with pure Fe3O4 nanoparticles, the surface plasmon resonance can be enhanced and tuned over the entire visible spectrum (viz. 350-800 nm) of the electromagnetic spectrum by varying the Au shell thickness (2-5 nm). Similarly, the Faraday rotation spectra can also be obtained.

  3. On modifying the magnetite films with complexonates

    International Nuclear Information System (INIS)

    Kuznetsov, Yu.I.; Bardasheva, T.I.

    1992-01-01

    Formation of magnetite layers on the surface of low-carbon steels and in neutral ammonium-nitrade eelctrolytes containing complexonate type inhibitors is studied to improve protection corrosion resistance of oxide coatings by means of electrochemical and gravimetrical techniques. Phosphonates are determined to affect kinetics and thickness of magnetite film formation, to increase protection properties of oxide layers. Complexonate-modified oxide coating is characterized by increased corrosion-resistance including that to chloride activating action

  4. In vivo integrity of polymer-coated gold nanoparticles

    Science.gov (United States)

    Kreyling, Wolfgang G.; Abdelmonem, Abuelmagd M.; Ali, Zulqurnain; Alves, Frauke; Geiser, Marianne; Haberl, Nadine; Hartmann, Raimo; Hirn, Stephanie; de Aberasturi, Dorleta Jimenez; Kantner, Karsten; Khadem-Saba, Gülnaz; Montenegro, Jose-Maria; Rejman, Joanna; Rojo, Teofilo; de Larramendi, Idoia Ruiz; Ufartes, Roser; Wenk, Alexander; Parak, Wolfgang J.

    2015-07-01

    Inorganic nanoparticles are frequently engineered with an organic surface coating to improve their physicochemical properties, and it is well known that their colloidal properties may change upon internalization by cells. While the stability of such nanoparticles is typically assayed in simple in vitro tests, their stability in a mammalian organism remains unknown. Here, we show that firmly grafted polymer shells around gold nanoparticles may degrade when injected into rats. We synthesized monodisperse radioactively labelled gold nanoparticles (198Au) and engineered an 111In-labelled polymer shell around them. Upon intravenous injection into rats, quantitative biodistribution analyses performed independently for 198Au and 111In showed partial removal of the polymer shell in vivo. While 198Au accumulates mostly in the liver, part of the 111In shows a non-particulate biodistribution similar to intravenous injection of chelated 111In. Further in vitro studies suggest that degradation of the polymer shell is caused by proteolytic enzymes in the liver. Our results show that even nanoparticles with high colloidal stability can change their physicochemical properties in vivo.

  5. Synthesis of Fulvic Acid-Coated Magnetite (Fe3O4–FA and Its Application for the Reductive Adsorption of [AuCl4]–

    Directory of Open Access Journals (Sweden)

    Philip Anggo Krisbiantoro

    2017-11-01

    Full Text Available Fulvic acid-coated magnetite (Fe3O4–FA has been synthesized through coprecipitation method using NH4OH. Synthesis conducted by cheap and environmentally friendly preparation used iron salts and extracted fulvic acid (FA from Peat soil of Rawa Pening, Central Java, Indonesia. Characterization using FT–IR indicated that the coating of FA on Fe3O4 occurred through the formation of chemical bond between iron of Fe3O4 and carboxyl group of FA. The XRD measurement indicated that coated Fe3O4 successfully dispersed in smaller size than uncoated Fe3O4, i.e. from 16.67 to 14.84 nm for Fe3O4 and Fe3O4–FA, respectively. Synthesized Fe3O4–FA has pHPZC 6.37 and stable at pH > 3.0. The extracted FA has total acidity 866.61 cmol kg–1, –COOH content 229.77 cmol kg–1 and –OH content 636.84 cmol kg–1. Fe3O4–FA has total acidity 494.86 cmol kg–1, –COOH content 67.80 cmol kg–1 and –OH content 427.06 cmol kg–1. The adsorption rate constant (k of [AuCl4]– on Fe3O4–A according to the Ho kinetic model was 8006.53 g mol–1 min–1. The adsorption capacity (qmax according to Langmuir isotherm model was 1.24 × 10–4 mol g–1. The presence of reduction towards the adsorbed [AuCl4]– was shown by the appearance of peaks at 2θ: 37.41; 43.66; 64.25, and 76.67° in the XRD diffractogram.

  6. Monte Carlo simulation of dose distribution in water around {sup 57}Fe{sub 3}O{sub 4} magnetite nanoparticle in the nuclear gamma resonance condition

    Energy Technology Data Exchange (ETDEWEB)

    Gabbasov, R.; Polikarpov, M. [National Research Centre Kurchatov Institute (Russian Federation); Safronov, V. [Shubnikov Institute of Crystallography, Research Center Space Materials Science (Russian Federation); Sozontov, E.; Yurenya, A., E-mail: antonyurenya@gmail.com; Panchenko, V. [National Research Centre Kurchatov Institute (Russian Federation)

    2016-12-15

    In this work was proposed a new radiotherapy enhancement method consisting of the administration of magnetic nanoparticles into the cells with further irradiation with a gamma-ray beam. As a result, adjusting the energy distribution of a gamma-ray beam and {sup 57}Fe abundance it is possible to achieve an extremely intensive electron emission because of a nuclear resonance. The produced conversion and Auger electrons can be used as an effective tool for DNA lesions production. We developed a Monte Carlo model for an electron and gamma emission by {sup 57}Fe nucleus using the Geant4 program package. The parameters of a resonant absorption were taken from Mössbauer spectra of magnetite nanoparticles synthesized for the administration into live cells. The space distribution of the radiation dose showed an increase in the dose of 2–2.5 times in the case of the natural abundance and more than 50 times in the case of the 66 % enrichment of the nanoparticles.

  7. Probing influence of rare earth ions (Er3+, Dy3+ and Gd3+) on structural, magnetic and optical properties of magnetite nanoparticles

    Science.gov (United States)

    Jain, Richa; Luthra, Vandna; Gokhale, Shubha

    2018-06-01

    Fe3-xRExO4 (RE = Er, Dy and Gd) nanoparticles with x varying from 0 to 0.1 were synthesized using co-precipitation method. The synthesized nanoparticles were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM) and UV-Vis spectroscopy techniques. TEM images reveal round shaped particles of ∼8-14 nm diameter in case of undoped magnetite (Fe3O4) nanoparticles whereas there is evolution of rod like structures by the doping of RE ions with aspect ratio in the range of 6-16. The room temperature saturation magnetization (Ms) values show gradual increase with doping till a critical doping level which is found to depend on the ionic radius of dopant ion (x = 0.01 for Er, 0.03 for Dy and 0.04 for Gd). There is a variation in the maximum value of saturation magnetization which is directly proportional to the number of unpaired 4f electrons in the dopant element. Low temperature magnetization study, carried out at 5 K and 120 K reveal an increase in the value of Ms as well as coercivity. The direct bandgaps calculated from UV-Visible data are found to decrease with increasing number of unpaired electrons in the dopant ions.

  8. Magnetic nanoparticles coated with polyaniline to stabilize immobilized trypsin

    Energy Technology Data Exchange (ETDEWEB)

    Maciel, J. C., E-mail: jackeline-maciel@hotmail.com [Universidade Federal de Roraima (Brazil); Mercês, A. A. D.; Cabrera, M. [Universidade Federal de Pernambuco, Laboratório de Imunopatologia Keizo Asami (Brazil); Shigeyosi, W. T. [Universidade Federal de São Carlos, Departamento de Física (Brazil); Souza, S. D. de; Olzon-Dionysio, M.; Fabris, J. D. [Universidade Federal dos Vales de Jequitinhonha e Mucuri (Brazil); Cardoso, C. A. [Universidade Federal de São Carlos, Departamento de Física (Brazil); Neri, D. F. M. [Universidade Federal do Vale do São Francisco (Brazil); Silva, M. P. C.; Carvalho, L. B. [Universidade Federal de Pernambuco, Laboratório de Imunopatologia Keizo Asami (Brazil)

    2016-12-15

    It is reported the synthesis of magnetic nanoparticles via the chemical co-precipitation of Fe {sup 3+} ions and their preparation by coating them with polyaniline. The electronic micrograph analysis showed that the mean diameter for the nanoparticles is ∼15 nm. FTIR, powder X-ray diffraction and Mössbauer spectroscopy were used to understand the chemical, crystallographic and {sup 57}Fe hyperfine structures for the two samples. The nanoparticles, which exhibited magnetic behavior with relatively high spontaneous magnetization at room temperature, were identified as being mainly formed by maghemite (γFe{sub 2}O{sub 3}). The coated magnetic nanoparticles (sample labeled “mPANI”) presented a real ability to bind biological molecules such as trypsin, forming the magnetic enzyme derivative (sample “mPANIG-Trypsin”). The amount of protein and specific activity of the immobilized trypsin were found to be 13±5 μg of protein/mg of mPANI (49.3 % of immobilized protein) and 24.1±0.7 U/mg of immobilized protein, respectively. After 48 days of storage at 4 {sup ∘}C, the activity of the immobilized trypsin was found to be 89 % of its initial activity. This simple, fast and low-cost procedure was revealed to be a promising way to prepare mPANI nanoparticles if technological applications addressed to covalently link biomolecules are envisaged. This route yields chemically stable derivatives, which can be easily recovered from the reaction mixture with a magnetic field and recyclable reused.

  9. Cylindrical and Spherical Active Coated Nanoparticles as Nanoantennas: Active nanoparticles as nanoantennas

    DEFF Research Database (Denmark)

    Arslanagic, Samel; Ziolkowski, Richard W.

    2017-01-01

    In this article, we review the fundamental properties of several spherical and cylindrical, passive, and active coated nanoparticles (CNPs) with an emphasis on their potential for nanoantenna and nanoamplifier synthesis. For the spherical geometries, the nanoparticles are excited by an electric...... Hertzian dipole (EHD), which represents, e.g., a stimulated atom or molecule. The cylindrical nanoparticles are excited by a magnetic line source (MLS). In the active cases, gain is added to the core region of the particle. For simplicity, it is represented by a canonical, frequency-independent gain model....... We demonstrate that specific CNPs can be designed to be resonant and well matched to their respective excitation sources. With active cores, these designs can lead to extremely large total radiated powers. For both configurations, insights into the effects of the nanoparticle material composition...

  10. Photo-crosslinked hyaluronic acid coated upconverting nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Mrazek, Jiri, E-mail: jiri.mrazek@contipro.com; Kettou, Sofiane; Matuska, Vit; Svozil, Vit; Huerta-Angeles, Gloria; Pospisilova, Martina; Nesporova, Kristina; Velebny, Vladimir [Contipro a. s. (Czech Republic)

    2017-02-15

    Hyaluronic acid (HA)-coated inorganic nanoparticles display enhanced interaction with the CD44 receptors which are overexpressed in many types of cancer cells. Here, we describe a modification of core-shell β-NaY{sub 0.80}Yb{sub 0.18}Er{sub 0.02}F{sub 4}@NaYF{sub 4} nanoparticles (UCNP) by HA derivative bearing photo-reactive groups. UCNP capped with oleic acid were firstly transferred to aqueous phase by an improved protocol using hydrochloric acid or lactic acid treatment. Subsequently, HA bearing furanacryloyl moieties (HA-FU) was adsorbed on the nanoparticle surface and crosslinked by UV irradiation. The crosslinking resulted in stable HA coating, and no polymer desorption was observed. As-prepared UCNP@HA-FU show a hydrodynamic diameter of about 180 nm and are colloidally stable in water and cell culture media. The cellular uptake by normal human fibroblasts and MDA MB-231 cancer cell line was investigated by upconversion luminescence imaging.

  11. Synthesis, Characterization, and Applications of Magnetic Nanoparticles Featuring Polyzwitterionic Coatings

    Directory of Open Access Journals (Sweden)

    Philip Biehl

    2018-01-01

    Full Text Available Throughout the last decades, magnetic nanoparticles (MNP have gained tremendous interest in different fields of applications like biomedicine (e.g., magnetic resonance imaging (MRI, drug delivery, hyperthermia, but also more technical applications (e.g., catalysis, waste water treatment have been pursued. Different surfactants and polymers are extensively used for surface coating of MNP to passivate the surface and avoid or decrease agglomeration, decrease or modulate biomolecule absorption, and in most cases increase dispersion stability. For this purpose, electrostatic or steric repulsion can be exploited and, in that regard, surface charge is the most important (hybrid particle property. Therefore, polyelectrolytes are of great interest for nanoparticle coating, as they are able to stabilize the particles in dispersion by electrostatic repulsion due to their high charge densities. In this review article, we focus on polyzwitterions as a subclass of polyelectrolytes and their use as coating materials for MNP. In the context of biomedical applications, polyzwitterions are widely used as they exhibit antifouling properties and thus can lead to minimized protein adsorption and also long circulation times.

  12. Impact of the organic coating on nanoparticles stability and reactivity

    Science.gov (United States)

    Gelabert, A.; Sivry, Y.; Ould Boualy, L.; Roselyne, F.; Juillot, F.; Menguy, N.; Benedetti, M. F.

    2010-12-01

    The strong increase in the use of engineered nanoparticles (NPs) during the last decade may ultimately result in their release in environmental settings, as predicted for different types of NPs by Gottshalk et al.. Most of these NPs incorporate functionalized coatings to gain industrial benefits, which in turn may play a critical rule for the whole NPs reactivity. Thus, along with stability studies focusing on the fate of NPs in natural systems, an accurate understanding of the coating impacts on the NPs behaviour and reactivity is highly required. This study aims to estimate the impact of three different coatings on the NPs dissolution rates in natural water (Seine river water), and their sorption properties onto a model mineral substrate. In this work, ZnO NPs have been coated, either with triethoxycaprylylsilane (hydrophobic), methacryloxypropyltrimethoxysilane (hydrophilic), or aminopropyltriethoxusilane (cationic). The dissolution rates were determined using two protocols: the Donnan Membrane Technique to measure the remaining free metal concentration in solution, and a 1 kDa ultrafiltration procedure to access both the free metal and small organic complexes part. For all three coating types, a fast dissolution step is reached in less than one day, followed by a slow precipitation of new mineral phases to finally reach a steady state. No major differences in the dissolution rates and profiles have been observed. Sorption studies on synthetic microsized goethite have been conducted at pH 7.5. The sorption ratio has been estimated as a function of initial NPs concentrations (from 10-7 M to 10-3 M), and follows a Langmuir shape for the hydrophobic and hydrophilic coatings at concentrations lower than 2.10-4 M. Interestingly, those two NPs exhibit high sorption capacities (10 times higher) compared to free Zn2+ sorption. On the other hand, at those concentrations, the cationic coating only induces a weak sorption without any defined trend. Moreover, for the

  13. Curcumin coated gold nanoparticles: synthesis, characterization, cytotoxicity, antioxidant activity and its comparison with citrate coated gold nanoparticles

    Directory of Open Access Journals (Sweden)

    Elnaz Shaabani

    2017-04-01

    Full Text Available Objective(s: Biological applications of gold nanoparticles have limitations because of the toxic chemicals used in their synthesis. Curcumin can be used as reducing as well as capping agent in synthesis of GNPs to eliminate the cytotoxicity. Conjugation of curcumin to gold also helps in increasing its solubility and bioavailability. Materials and Methods: Here we report synthesis of gold nanoparticles coated with citrate and curcumin and of two different sizes via chemical routes. UV-Vis absorbance spectroscopy, Dynamic Light Scattering and Transmission Electron Microscopy were applied to study the average particle size, size stability of the samples and zeta potential. Fourier transform infrared, Raman Spectroscopy and Fluorescence Spectroscopy were applied for detection of curcumin on the surface of GNPs. The antioxidant activity was evaluated using DPPH assay and Cytotoxicity was evaluated by MTT assay.Results: Particles were synthesized of 6 and 16 nm size. The average particle size was found to be 21.7 ± 5.7 by TEM. The zeta potential on the surface of Cur-GNPs was negative and larger than 25 mV which is a sign of their high stability. The stability of these particles (with different coatings but with similar sizes at different time intervals (up to 3 months and also in different media like cell culture medium, different buffers, glucose and at different pH conditions have been investigated thoroughly. Appearance of functional groups assigned to curcumin in FTIR and SERS spectra are sign of presence of curcumin in the sample. The quenching of the fluorescence in the presence of GNPs reveals the clear indication of the capping and binding of curcumin with GNPs. Cur-GNP1 (16 nm were found to exhibit highest antioxidant activity than other gold nanoparticles. Cytotoxicity evaluation using MTT assay on L929 cell line proved curcumin coated gold nanoparticles were non-toxic up to 40 ppm.Conclusion: The results revealed that larger curcumin

  14. Multifunctional EuYVO4 nanoparticles coated with mesoporous silica

    International Nuclear Information System (INIS)

    Justino, Larissa G.; Nigoghossian, Karina; Capote, Ticiana S.O.; Scarel-Caminaga, Raquel M.; Ribeiro, Sidney J.L.; Caiut, José Maurício A.

    2016-01-01

    Mesoporous structures are interesting materials for the incorporation of dyes, drugs, and luminescent systems, leading to materials with important multifunctionalities. In a very unique way, these guest/host materials combine the high stability of inorganic systems, new guest-structuring features, and adsorption mechanisms in their well-defined pores. This work evaluates the luminescent properties of rare earth-doped YVO 4 nanoparticles coated with a mesoporous silica shell. The use of two different synthesis methodologies allowed for particle size control. The crystalline phase emerged without further heat treatment. The mesoporous shell decreased undesirable quenching effects on YVO 4 :Eu 3+ nanoparticles and rendered them biocompatible. The materials prepared herein could have interesting applications as luminescent markers or drug release systems.

  15. Generation of drugs coated iron nanoparticles through high energy ball milling

    Energy Technology Data Exchange (ETDEWEB)

    Radhika Devi, A.; Murty, B. S. [Department of Metallurgical and Materials Engineering, Indian Institute of Technology Madras, Chennai 600036 (India); Chelvane, J. A. [Defence Metallurgical Research Laboratory, Hyderabad 500058 (India); Prabhakar, P. K.; Padma Priya, P. V.; Doble, Mukesh [Department of Biotechnology, Indian Institute of Technology Madras, Chennai 600036 (India)

    2014-03-28

    The iron nanoparticles coated with oleic acid and drugs such as folic acid/Amoxicillin were synthesized by high energy ball milling and characterized by X-ray diffraction, Transmission electron microscope, zeta potential, dynamic light scattering, Fourier Transform Infra red (FT-IR) measurements, and thermo gravimetric analysis (TGA). FT-IR and TGA measurements show good adsorption of drugs on oleic acid coated nanoparticles. Magnetic measurements indicate that saturation magnetization is larger for amoxicillin coated particles compared to folic acid coated particles. The biocompatibility of the magnetic nanoparticles prepared was evaluated by in vitro cytotoxicity assay using L929 cells as model cells.

  16. Surface spins disorder in uncoated and SiO{sub 2} coated maghemite nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Zeb, F. [Nanoscience and Technology Laboratory, International Islamic University, H-10, 44000 Islamabad (Pakistan); Nadeem, K., E-mail: kashif.nadeem@iiu.edu.pk [Nanoscience and Technology Laboratory, International Islamic University, H-10, 44000 Islamabad (Pakistan); Shah, S. Kamran Ali; Kamran, M. [Nanoscience and Technology Laboratory, International Islamic University, H-10, 44000 Islamabad (Pakistan); Gul, I. Hussain [School of Chemical & Materials Engineering, National University of Sciences and Technology (NUST), H-12, 44000 Islamabad, Pakistan (Pakistan); Ali, L. [Materials Research Laboratory, International Islamic University, H-10, 44000 Islamabad (Pakistan)

    2017-05-01

    We studied the surface spins disorder in uncoated and silica (SiO{sub 2}) coated maghemite (γ-Fe{sub 2}O{sub 3}) nanoparticles using temperature and time dependent magnetization. The average crystallite size for SiO{sub 2} coated and uncoated nanoparticles was about 12 and 29 nm, respectively. Scanning electron microscopy (SEM) showed that the nanoparticles are spherical in shape and well separated. Temperature scans of zero field cooled (ZFC)/field cooled (FC) magnetization measurements showed lower average blocking temperature (T{sub B}) for SiO{sub 2} coated maghemite nanoparticles as compared to uncoated nanoparticles. The saturation magnetization (M{sub s}) of SiO{sub 2} coated maghemite nanoparticles was also lower than the uncoated nanoparticles and is attributed to smaller average crystallite size of SiO{sub 2} coated nanoparticles. For saturation magnetization vs. temperature data, Bloch's law (M(T)= M(0).(1− BT{sup b})) was fitted well for both uncoated and SiO{sub 2} coated nanoparticles and yields: B =3×10{sup −7} K{sup -b}, b=2.22 and B=0.0127 K{sup -b}, b=0.57 for uncoated and SiO{sub 2} coated nanoparticles, respectively. Higher value of B for SiO{sub 2} coated nanoparticles depicts decrease in exchange coupling due to enhanced surface spins disorder (broken surface bonds) as compared to uncoated nanoparticles. The Bloch's exponent b was decreased for SiO{sub 2} coated nanoparticles which is due to their smaller average crystallite size or finite size effects. Furthermore, a sharp increase of coercivity at low temperatures (<25 K) was observed for SiO{sub 2} coated nanoparticles which is also due to contribution of increased surface anisotropy or frozen surface spins in these smaller nanoparticles. The FC magnetic relaxation data was fitted to stretched exponential law which revealed slower magnetic relaxation for SiO{sub 2} coated nanoparticles. All these measurements revealed smaller average crystallite size and enhanced surface

  17. Synthesis and Biochemical effects of magnetite nanoparticle by surfactant-free electrochemical method in an aqueous system:the current density effect

    Directory of Open Access Journals (Sweden)

    Mousa Aliahmad

    2016-07-01

    Full Text Available Obejective(s: In this research, magnetite nanoparticles with an average size of 23-36 nm were successfully synthesized via surfactant-free electrochemical method using iron as the anode and water as the electrolyte in a closed aqueous system in the presence of NaOH at room temperature. Methods: The effect of the current density on product formation and particle size was investigated. Particle size was controlled by adjusting the current density. It was found that particle size decreases by decreasing the current density. In addition, the effect of current density  on the structural and optical properties of nanostructures were studied by X-ray diffraction, Field emission scanning electron microscopy, Fourier transformed infrared, and vibrating sample magnetometer techniques.  Results: The results obtained from the magnetization property study of samples at room temperature showed coactivity and saturation manetization of 0-100 Oe and 27.2- 40.5 emu. g-1, respectively. Finally, the results of biological activity study of nanoparticles on liver and kidney function in male wistar rats demonstrated that oral administration of NPs caused significant alterations to the levels of aspartate transaminase, alanine transaminase, and alkaline phosphatase in serum. Conclusions: No significant changes were detected in the groups treated with 10 and 100 ppm/ day nanostructure (P>0.05. There was a significant increase in the serum level of creatinine and blood urea nitrogen level (p

  18. Kinetic and isotherm analyses for thorium (IV) adsorptive removal from aqueous solutions by modified magnetite nanoparticle using response surface methodology (RSM)

    Energy Technology Data Exchange (ETDEWEB)

    Karimi, Mohammad, E-mail: m.karimi407@alumni.ut.ac.ir [School of Chemical Engineering, College of Engineering, University of Tehran, P.O. Box: 11365-4563, Tehran (Iran, Islamic Republic of); Milani, Saeid Alamdar [Nuclear Fuel Cycle Research School, Nuclear Science and Technology Research Institute, AEOI, P.O. Box: 14893-836, Tehran (Iran, Islamic Republic of); Abolgashemi, Hossein [School of Chemical Engineering, College of Engineering, University of Tehran, P.O. Box: 11365-4563, Tehran (Iran, Islamic Republic of)

    2016-10-15

    In this study, the ability and the adsorption capacity of magnetite/aminopropyltriethoxysilane/glutaraldehyde (Fe{sub 3}O{sub 4}/APTES/GA) adsorbent were evaluated for the adsorption of thorium (IV) ions from aqueous solutions. The influence of the several variables such as pH (1–5), Th (IV) initial concentration (50–300 mg L{sup −1}) and adsorbent concentration (1–5 g L{sup −1}) on the Th (IV) adsorption were investigated by response surface methodology (RSM). The results showed that the highest absorption capacity (q) was 107.23 mg g{sup −1} with respect to pH = 4.5, initial concentration of 250 mg L{sup −1} and adsorbent concentration of 1 g L{sup −1} for 90 min. Modeling equilibrium sorption data with the Langmuir, Freundlich and Dubinin–Radushkevich models pointed out that the results were in good agreement with Langmuir model. The experimental kinetic data were well fitted to pseudo-second-order equation with R{sup 2} = 0.9739. Also thermodynamic parameters (ΔG{sup o}, ΔH{sup o}, ΔS{sup o}) declared that the Th (IV) adsorption was endothermic and spontaneous. - Highlights: • Thorium ions were removed from aqueous solutions by modified magnetite nanoparticle. • The effects of process variables on adsorption capacity were investigated by RSM. • Thermodynamic parameters showed that the adsorption was endothermic and spontaneous. • The equilibrium data for the adsorption of Thorium followed the Langmuir isotherm. • The experimental kinetic data were described by the pseudo-second-order equation.

  19. Solvent-assisted dispersive micro-SPE by using aminopropyl-functionalized magnetite nanoparticle followed by GC-PID for quantification of parabens in aqueous matrices.

    Science.gov (United States)

    Abbasghorbani, Maryam; Attaran, Abdolmohammad; Payehghadr, Mahmood

    2013-01-01

    In this research, solvent-assisted dispersive micro-SPE was introduced as a simple modified technique for the determination of parabens in water and cosmetic samples. Aminopropyl-functionalized magnetite nanoparticles (MNPs) were successfully synthesized and applied. GC with photoionization detector was used for the separation and detection of parabens. In this method, hexylacetate (15 μL) as a solvent and aminopropyl-functionalized MNPs (5 μg) as a sorbent were added to an aqueous sample (10 mL) and then the sample was sonicated. Dispersed magnetite was collected in the bottom of the conical tube by using a strong magnet and then ACN was added as a desorption solvent. Forty microliters of this solvent was transferred into a microvial and then acetic anhydride and pyridine were added, thus derivatization was performed by acetic anhydride. After evaporation, 1 μL of derivatized sample was injected into a gas chromatograph for analysis. Several important parameters, such as kind of organic solvent, desorption solvent and volume, amount of aminopropyl-functionalized MNPs and effect of salt addition were investigated. Under optimum conditions, the limits of detection achieved were between 50 and 300 ng/L, with RSDs (n = 5) lower than 8%. Under the optimum conditions, the enrichment factors ranged from 217 to 1253 and the extraction recoveries ranged from 10 to 62%. The recoveries were obtained for the analytes in river water and mouthwash solution and hand cream in the range of 87-103%. The advantages of proposed method are simplicity of operation, rapidity, high extraction yields, and environmental friendly character. © 2012 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  20. Studies on polyethylene glycol coating on NiFe2O4 nanoparticles for biomedical applications

    International Nuclear Information System (INIS)

    Phadatare, M.R.; Khot, V.M.; Salunkhe, A.B.; Thorat, N.D.; Pawar, S.H.

    2012-01-01

    The NiFe 2 O 4 nanoparticles were prepared by the combustion method and these nanoparticles were successfully coated with polyethylene glycol (PEG) for the possible biomedical applications such as magnetic resonance imaging, drug delivery, tissue repair, magnetic fluid hyperthermia etc. The structural and magnetic characterizations of NiFe 2 O 4 nanoparticles were carried out by x-ray diffraction and vibrating sample magnetometry techniques, respectively. The morphology of the uncoated and coated nanoparticles was studied by scanning electron microscopy. The existence of PEG layer on NiFe 2 O 4 nanoparticles was confirmed by fourier transform infrared spectroscopy technique. - Highlights: ► Synthesis of nanocrystalline NiFe 2 O 4 by the combustion method. ► Magnetic properties of the NiFe 2 O 4 nanoparticles at room temperature. ► Coating of NiFe 2 O 4 nanoparticles by Polyethylene glycol (PEG).

  1. Mammalian cell growth on gold nanoparticle-decorated substrates is influenced by the nanoparticle coating

    Directory of Open Access Journals (Sweden)

    Christina Rosman

    2014-12-01

    Full Text Available In this work, we study epithelial cell growth on substrates decorated with gold nanorods that are functionalized either with a positively charged cytotoxic surfactant or with a biocompatible polymer exhibiting one of two different end groups, resulting in a neutral or negative surface charge of the particle. Upon observation of cell growth for three days by live cell imaging using optical dark field microscopy, it was found that all particles supported cell adhesion while no directed cell migration and no significant particle internalization occurred. Concerning cell adhesion and spreading as compared to cell growth on bare substrates after 3 days of incubation, a reduction by 45% and 95%, respectively, for the surfactant particle coating was observed, whereas the amino-terminated polymer induced a reduction by 30% and 40%, respectively, which is absent for the carboxy-terminated polymer. Furthermore, interface-sensitive impedance spectroscopy (electric cell–substrate impedance sensing, ECIS was employed in order to investigate the micromotility of cells added to substrates decorated with various amounts of surfactant-coated particles. A surface density of 65 particles/µm2 (which corresponds to 0.5% of surface coverage with nanoparticles diminishes micromotion by 25% as compared to bare substrates after 35 hours of incubation. We conclude that the surface coating of the gold nanorods, which were applied to the basolateral side of the cells, has a recognizable influence on the growth behavior and thus the coating should be carefully selected for biomedical applications of nanoparticles.

  2. Purification of rhamnolipid using colloidal magnetic nanoparticles ...

    African Journals Online (AJOL)

    Phospholipid-coated colloidal magnetic nanoparticles with mean magnetite core size of 9 nm are shown to be effective ion exchange media for the recovery and purification of Rhaminolipid from culture mixtures. These particles have high adsorption capacity for purification (an order of magnitude larger than the best ...

  3. Coating of gold nanoparticles for medical application: UV-VIS

    Science.gov (United States)

    Martínez Espinosa, Juan Carlos; Ramírez, Nayem Amtanus Chequer; Funes Oliva, Luis Enrique; Córdova Fraga, Teodoro; Bernal Alvarado, Jesús; Reyes Pablo, Aldelmo; Núñez, Anita Rosa Elvira

    2014-11-01

    The use of nanostructured materials has gained strength in recent years in the biomedical area; new applications such as the detection of components in living cells have been used in pharmaceutical area, specifically to study the interaction of various antitumor drugs in living tissues, the detection of genes that are closely related to some type of cancer, as well as the detections of protein biomarkers for diseases also have been studied in various research laboratories around of the world. In this work, we characterize the variation of the absorbance of gold nanoparticles (GNPs) coated with different concentration of Bovine Serum Albumin (BSA) protein. We use GNPS of 60 nm of the trademark-TED PELLA, the BSA protein trademark of Sigma Aldrich and based on that proposed protocol by Chithrani et al., 2009 with purposes to obtain an alternative model to determine the optimal stability of the nanoparticles coated with the protein. The colloidal solutions were prepared with BSA at different concentrations (0.25, 0.5, 0.75 and 1% M/V), and were centrifuged at 15,000 rpm for 90 minutes (centrifuge Model Z383K) and a constant temperature of 25 °C. All the spectra sets were obtained within the range from 400 to 700 nm using an UV-VIS spectrophotometer (Thermo Scientific Model 51118650). The results showed a R2 of 0.99 for an exponential curve correlation between the concentration of BSA, and the absorbance measured. We found at higher concentrations of BSA, there is a decrease in the intensity of the absorption spectra in the plasmon resonance. This preliminary model obtained can be used in the stabilization of gold nanoparticles with different proteins of biomedical interest in future experiments and support for functionalization of GNPs with specific membrane markers.

  4. Influence of natural organic matter (NOM) coatings on nanoparticle adsorption onto supported lipid bilayers.

    Science.gov (United States)

    Bo, Zhang; Avsar, Saziye Yorulmaz; Corliss, Michael K; Chung, Minsub; Cho, Nam-Joon

    2017-10-05

    As the worldwide usage of nanoparticles in commercial products continues to increase, there is growing concern about the environmental risks that nanoparticles pose to biological systems, including potential damage to cellular membranes. A detailed understanding of how different types of nanoparticles behave in environmentally relevant conditions is imperative for predicting and mitigating potential membrane-associated toxicities. Herein, we investigated the adsorption of two popular nanoparticles (silver and buckminsterfullerene) onto biomimetic supported lipid bilayers of varying membrane charge (positive and negative). The quartz crystal microbalance-dissipation (QCM-D) measurement technique was employed to track the adsorption kinetics. Particular attention was focused on understanding how natural organic matter (NOM) coatings affect nanoparticle-bilayer interactions. Both types of nanoparticles preferentially adsorbed onto the positively charged bilayers, although NOM coatings on the nanoparticle and lipid bilayer surfaces could either inhibit or promote adsorption in certain electrolyte conditions. While past findings showed that NOM coatings inhibit membrane adhesion, our findings demonstrate that the effects of NOM coatings are more nuanced depending on the type of nanoparticle and electrolyte condition. Taken together, the results demonstrate that NOM coatings can modulate the lipid membrane interactions of various nanoparticles, suggesting a possible way to improve the environmental safety of nanoparticles. Copyright © 2017 Elsevier B.V. All rights reserved.

  5. Hydroxyapatite-silver nanoparticles coatings on porous polyurethane scaffold.

    Science.gov (United States)

    Ciobanu, Gabriela; Ilisei, Simona; Luca, Constantin

    2014-02-01

    The present paper is focused on a study regarding the possibility of obtaining hydroxyapatite-silver nanoparticle coatings on porous polyurethane scaffold. The method applied is based on a combined strategy involving hydroxyapatite biomimetic deposition on polyurethane surface using a Supersaturated Calcification Solution (SCS), combined with silver ions reduction and in-situ crystallization processes on hydroxyapatite-polyurethane surface by sample immersing in AgNO3 solution. The morphology, composition and phase structure of the prepared samples were characterized by scanning electron microscopy coupled with energy dispersive X-ray spectroscopy (SEM-EDX), X-ray diffraction (XRD), UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS) measurements. The data obtained show that a layer of hydroxyapatite was deposited on porous polyurethane support and the silver nanoparticles (average size 34.71 nm) were dispersed among and even on the hydroxyapatite crystals. Hydroxyapatite/polyurethane surface acts as a reducer and a stabilizing agent for silver ions. The surface plasmon resonance peak in UV-Vis absorption spectra showed an absorption maximum at 415 nm, indicating formation of silver nanoparticles. The hydroxyapatite-silver polyurethane scaffolds were tested against Staphylococcus aureus and Escherichia coli and the obtained data were indicative of good antibacterial properties of the materials. © 2013.

  6. Transport of citrate-coated silver nanoparticles in unsaturated sand

    Science.gov (United States)

    Kumahor, Samuel; Hron, Pavel; Metreveli, George; Schaumann, Gabriele; Vogel, Hans-Jörg

    2015-04-01

    Chemical factors and physical constraints lead to coupled effects during particle transport in unsaturated porous media. Unlike for saturated transport, studies on unsaturated transport as typical for soil are currently scarce. We investigated the mobility of citrate-coated Ag NPs in unsaturated sand (grain diameter: 0.1-0.3 mm). For three flux rates and a given pore-water ionic strength (1 mM KNO3), the citrate-coated Ag NPs were less mobile at pH = 5 compared to pH = 9. The classic Derjaguin-Landau-Verwey-Overbeek (DLVO) theory suggests unfavorable deposition conditions at both, the air-water interface and solid-water interface. Breakthrough curves measured under quasi-steady state unsaturated flow showed retardation of the citrate-coated Ag NPs compared to inert solute (KBr). After flushing with nanoparticle-free 1 mM KNO3 solution (pH-adjusted), retention was much lower in deeper depths compared to the surface where the particles entered the flow field. The results show a non-linear dependence of nanoparticle (NP) mobility on flux rate and water content. Especially the observed retardation similar to equilibrium sorption is in contrast to observations under saturated flow conditions. A convection-dispersion and reaction model that combines a reversible equilibrium process and a non-equilibrium interaction process reproduced the measured breakthrough curves reasonably well. From comparison between saturated and unsaturated experiments we conclude that the air-water interface is responsible for the reversible equilibrium process while the water-solid interface accounts for irreversible soption.

  7. Functional Magnetic Nanoparticles

    Science.gov (United States)

    Gass, James

    Nanoparticle system research and characterization is the focal point of this research and dissertation. In the research presented here, magnetite, cobalt, and ferrite nanoparticle systems have been explored in regard to their magnetocaloric effect (MCE) properties, as well as for use in polymer composites. Both areas of study have potential applications across a wide variety of interdisciplinary fields. Magnetite nanoparticles have been successfully dispersed in a polymer. The surface chemistry of the magnetic nanoparticle proves critical to obtaining a homogenous and well separated high density dispersion in PMMA. Theoretical studies found in the literature have indicated that surface interface energy is a critical component in dispersion. Oleic acid is used to alter the surface of magnetite nanoparticles and successfully achieve good dispersion in a PMMA thin film. Polypyrrole is then coated onto the PMMA composite layer. The bilayer is characterized using cross-sectional TEM, cross-sectional SEM, magnetic characterization, and low frequency conductivity. The results show that the superparmagnetic properties of the as synthesized particles are maintained in the composite. With further study of the properties of these nanoparticles for real and functional uses, MCE is studied on a variety of magnetic nanoparticle systems. Magnetite, manganese zinc ferrite, and cobalt ferrite systems show significant broadening of the MCE and the ability to tune the peak temperature of MCE by varying the size of the nanoparticles. Four distinct systems are studied including cobalt, cobalt core silver shell nanoparticles, nickel ferrite, and ball milled zinc ferrite. The results demonstrate the importance of surface characteristics on MCE. Surface spin disorder appears to have a large influence on the low temperature magnetic and magnetocalorie characteristics of these nanoparticle systems.

  8. Behavior of Ag nanoparticles in soil: Effects of particle surface coating, aging and sewage sludge amendment

    International Nuclear Information System (INIS)

    Whitley, Annie R.; Levard, Clément; Oostveen, Emily; Bertsch, Paul M.; Matocha, Chris J.; Kammer, Frank von der; Unrine, Jason M.

    2013-01-01

    This study addressed the relative importance of particle coating, sewage sludge amendment, and aging on aggregation and dissolution of manufactured Ag nanoparticles (Ag MNPs) in soil pore water. Ag MNPs with citrate (CIT) or polyvinylpyrrolidone (PVP) coatings were incubated with soil or municipal sewage sludge which was then amended to soil (1% or 3% sludge (w/w)). Pore waters were extracted after 1 week and 2 and 6 months and analyzed for chemical speciation, aggregation state and dissolution. Ag MNP coating had profound effects on aggregation state and partitioning to pore water in the absence of sewage sludge, but pre-incubation with sewage sludge negated these effects. This suggests that Ag MNP coating does not need to be taken into account to understand fate of AgMNPs applied to soil through biosolids amendment. Aging of soil also had profound effects that depended on Ag MNP coating and sludge amendment. -- Highlights: •Silver nanoparticle coating affects fate in unamended soils. •Citrated coated silver nanoparticles could be found in pore water for up to six months. •Pre-incubation of silver nanoparticles in sewage sludge negated effects of surface coating. •Weathered or reprecipitated particles found in pore water for up to two months in sludge amended soils. •Particle surface coating, sewage sludge amendment and aging all have important impacts. -- Behavior of manufactured silver nanoparticles in soil depends on surface coating, contact with sewage sludge, and aging

  9. Polyelectrolyte coating of ferumoxytol nanoparticles for labeling of dendritic cells

    Energy Technology Data Exchange (ETDEWEB)

    Celikkin, Nehar; Jakubcová, Lucie; Zenke, Martin [Institute for Biomedical Engineering, Department of Cell Biology, RWTH Aachen University Hospital, Pauwelsstrasse 30, 52074 Aachen (Germany); Helmholtz Institute for Biomedical Engineering, RWTH Aachen University, Pauwelsstrasse 20, 52074 Aachen (Germany); Hoss, Mareike [Institute of Pathology, Electron Microscopy Facility, RWTH Aachen University Hospital, Pauwelsstrasse 30, 52074 Aachen (Germany); Wong, John Erik, E-mail: John.Wong@avt.rwth-aachen.de [Chemical Process Engineering, RWTH Aachen University, Turmstrasse 46, 52056 Aachen (Germany); DWI – Leibniz Institute for Interactive Materials Research, Forckenbeckstrasse 50, Aachen (Germany); Hieronymus, Thomas, E-mail: thomas.hieronymus@rwth-aachen.de [Institute for Biomedical Engineering, Department of Cell Biology, RWTH Aachen University Hospital, Pauwelsstrasse 30, 52074 Aachen (Germany); Helmholtz Institute for Biomedical Engineering, RWTH Aachen University, Pauwelsstrasse 20, 52074 Aachen (Germany)

    2015-04-15

    Engineered magnetic nanoparticles (MNPs) are emerging to be used as cell tracers, drug delivery vehicles, and contrast agents for magnetic resonance imaging (MRI) for enhanced theragnostic applications in biomedicine. In vitro labeling of target cell populations with MNPs and their implantation into animal models and patients shows promising outcomes in monitoring successful cell engraftment, differentiation and migration by using MRI. Dendritic cells (DCs) are professional antigen-presenting cells that initiate adaptive immune responses. Thus, DCs have been the focus of cellular immunotherapy and are increasingly applied in clinical trials. Here, we addressed the coating of different polyelectrolytes (PE) around ferumoxytol particles using the layer-by-layer technique. The impact of PE-coated ferumoxytol particles for labeling of DCs and Flt3{sup +} DC progenitors was then investigated. The results from our studies revealed that PE-coated ferumoxytol particles can be readily employed for labeling of DC and DC progenitors and thus are potentially suitable as contrast agents for MRI tracking.

  10. Simple and Rapid Synthesis of Magnetite/Hydroxyapatite Composites for Hyperthermia Treatments via a Mechanochemical Route

    Science.gov (United States)

    Iwasaki, Tomohiro; Nakatsuka, Ryo; Murase, Kenya; Takata, Hiroshige; Nakamura, Hideya; Watano, Satoru

    2013-01-01

    This paper presents a simple method for the rapid synthesis of magnetite/hydroxyapatite composite particles. In this method, superparamagnetic magnetite nanoparticles are first synthesized by coprecipitation using ferrous chloride and ferric chloride. Immediately following the synthesis, carbonate-substituted (B-type) hydroxyapatite particles are mechanochemically synthesized by wet milling dicalcium phosphate dihydrate and calcium carbonate in a dispersed suspension of magnetite nanoparticles, during which the magnetite nanoparticles are incorporated into the hydroxyapatite matrix. We observed that the resultant magnetite/hydroxyapatite composites possessed a homogeneous dispersion of magnetite nanoparticles, characterized by an absence of large aggregates. When this material was subjected to an alternating magnetic field, the heat generated increased with increasing magnetite concentration. For a magnetite concentration of 30 mass%, a temperature increase greater than 20 K was achieved in less than 50 s. These results suggest that our composites exhibit good hyperthermia properties and are promising candidates for hyperthermia treatments. PMID:23629669

  11. Simple and Rapid Synthesis of Magnetite/Hydroxyapatite Composites for Hyperthermia Treatments via a Mechanochemical Route

    Directory of Open Access Journals (Sweden)

    Tomohiro Iwasaki

    2013-04-01

    Full Text Available This paper presents a simple method for the rapid synthesis of magnetite/hydroxyapatite composite particles. In this method, superparamagnetic magnetite nanoparticles are first synthesized by coprecipitation using ferrous chloride and ferric chloride. Immediately following the synthesis, carbonate-substituted (B-type hydroxyapatite particles are mechanochemically synthesized by wet milling dicalcium phosphate dihydrate and calcium carbonate in a dispersed suspension of magnetite nanoparticles, during which the magnetite nanoparticles are incorporated into the hydroxyapatite matrix. We observed that the resultant magnetite/hydroxyapatite composites possessed a homogeneous dispersion of magnetite nanoparticles, characterized by an absence of large aggregates. When this material was subjected to an alternating magnetic field, the heat generated increased with increasing magnetite concentration. For a magnetite concentration of 30 mass%, a temperature increase greater than 20 K was achieved in less than 50 s. These results suggest that our composites exhibit good hyperthermia properties and are promising candidates for hyperthermia treatments.

  12. Effective extraction and simultaneous determination of Sudan dyes from tomato sauce and chili-containing foods using magnetite/reduced graphene oxide nanoparticles coupled with high-performance liquid chromatography.

    Science.gov (United States)

    Zhang, Ming-Yue; Wang, Man-Man; Hao, Yu-Lan; Shi, Xin-Ran; Wang, Xue-Sheng

    2016-05-01

    A simple, effective, and robust magnetic solid-phase extraction method was developed using magnetite/reduced graphene oxide nanoparticles as the adsorbent for the simultaneous determination of Sudan dyes (I, II, III, and IV) in foodstuffs. The magnetite/reduced graphene oxide nanoparticles were characterized by X-ray diffraction, scanning electron microscopy, and vibrating sample magnetometry. The extraction parameters including extraction time, elution solution, and elution time and volume were investigated in detail. Such magnetite/reduced graphene oxide nanoparticles based magnetic solid-phase extraction in combination with high-performance liquid chromatography and variable wavelength detection gave the detection limits of 3-6 μg/kg for Sudan I-IV in chili sauce, tomato sauce, chili powder, and chili flake samples. The recoveries were 79.6-108% at three spiked levels with the intra- and inter-day relative standard deviations of 1.2-8.6 and 4.5-9.6%, respectively. The feasibility was further performed by a comparison with commercial alumina-N. This method is suitable for the routine analysis of Sudan dyes due to its sensitivity, simplicity, and low cost. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Inulin hydrolysis by inulinase immobilized covalently on magnetic nanoparticles prepared with wheat gluten hydrolysates

    OpenAIRE

    Homa Torabizadeh; Asieh Mahmoudi

    2018-01-01

    Inulinase can produce a high amount of fructose syrup from inulin in a one-step enzymatic process. Inulinase from Aspergillus niger was immobilized covalently on Fe3O4 magnetic nanoparticles functionalized with wheat gluten hydrolysates (WGHs). Wheat gluten was enzymatically hydrolyzed by two endopeptidases Alcalase and Neutrase and related nanoparticles were prepared by desolvation method. Magnetite nanoparticles were coated with WGHs nanoparticles and then inulinase was immobilized onto it ...

  14. Preparation and characterization of iron oxide (Fe3O4) nanoparticles coated with polyvinylpyrrolidone/polyethylenimine through a facile one-pot deposition route

    Science.gov (United States)

    Karimzadeh, Isa; Aghazadeh, Mustafa; Ganjali, Mohammad Reza; Doroudi, Taher; Kolivand, Peir Hossein

    2017-07-01

    In this article, we report the electrochemical synthesis and simultaneous in situ coating of magnetic iron oxide nanoparticles (MNPs) with polyvinylpyrrolidone (PVP) and polyethylenimine (PEI). The cathodic deposition was carried out through electro-generation of OH- on the surface of cathode. An aqueous solution of Fe(NO3)3·9H2O (3.4 g/L) and FeCl2·4H2O (1.6 g/L) was used as the deposition bath. The electrochemical precipitation experiments were performed in the direct current mode under a 10 mA cm-2 current density for 30 min. Polymer coating was performed in an identical deposition bath containing of 0.5 g PVP and 0.5 g PEI. The deposited uncoated and PVP-PEI coated MNPs were characterized through powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), thermogravimetric analysis (TGA), dynamic light scattering (DLS), vibrating sample magnetometer (VSM), and field-emission scanning and transmission electron microscopies (FE-SEM and TEM). Structural XRD and IR analyses revealed both samples to be composed of pure crystalline magnetite (Fe3O4). Morphological observations through FE-SEM and TEM proved the product to be spherical nanoparticles in the range of 10-15 nm. The presence of two coating polymers (i.e. PVP and PEI) on the surface of the electro-synthesized MNPs was proved by FTIR and DLS results. The percentage of the polymer coating (31.8%) on the MNPs surface was also determined based on DSC-TGA data. The high magnetization value, coercivity and remanence values measured by VSM indicated the superparamagnetic nature of both prepared MNPs. The obtained results confirmed that the prepared Fe3O4 nanoparticles had suitable physico-chemical and magnetic properties for biomedical applications.

  15. Hydroxyapatite-silver nanoparticles coatings on porous polyurethane scaffold

    International Nuclear Information System (INIS)

    Ciobanu, Gabriela; Ilisei, Simona; Luca, Constantin

    2014-01-01

    The present paper is focused on a study regarding the possibility of obtaining hydroxyapatite-silver nanoparticle coatings on porous polyurethane scaffold. The method applied is based on a combined strategy involving hydroxyapatite biomimetic deposition on polyurethane surface using a Supersaturated Calcification Solution (SCS), combined with silver ions reduction and in-situ crystallization processes on hydroxyapatite-polyurethane surface by sample immersing in AgNO 3 solution. The morphology, composition and phase structure of the prepared samples were characterized by scanning electron microscopy coupled with energy dispersive X-ray spectroscopy (SEM-EDX), X-ray diffraction (XRD), UV-Vis spectroscopy and X-ray photoelectron spectroscopy (XPS) measurements. The data obtained show that a layer of hydroxyapatite was deposited on porous polyurethane support and the silver nanoparticles (average size 34.71 nm) were dispersed among and even on the hydroxyapatite crystals. Hydroxyapatite/polyurethane surface acts as a reducer and a stabilizing agent for silver ions. The surface plasmon resonance peak in UV-Vis absorption spectra showed an absorption maximum at 415 nm, indicating formation of silver nanoparticles. The hydroxyapatite-silver polyurethane scaffolds were tested against Staphylococcus aureus and Escherichia coli and the obtained data were indicative of good antibacterial properties of the materials. - Highlights: • The hydroxyapatite and silver nanoparticles were grown on the polyurethane scaffold • The hydroxyapatite/polyurethane acts as reducing agent, stabilizer and matrix for Ag • The samples were well characterized by SEM-EDX, XRD, XPS, UV-visible spectroscopy • The hydroxyapatite/silver polyurethane scaffold shows antibacterial property

  16. Hybrid, silica-coated, Janus-like plasmonic-magnetic nanoparticles

    OpenAIRE

    Sotiriou, Georgios A.; Hirt, Ann M.; Lozach, Pierre-Yves; Teleki, Alexandra; Krumeich, Frank; Pratsinis, Sotiris E.

    2011-01-01

    Hybrid plasmonic-magnetic nanoparticles possess properties that are attractive in bioimaging, targeted drug delivery, in vivo diagnosis and therapy. The stability and toxicity, however, of such nanoparticles challenge their safe use today. Here, biocompatible, SiO2-coated, Janus-like Ag/Fe2O3 nanoparticles are prepared by one-step, scalable flame aerosol technology. A nanothin SiO2 shell around these multifunctional nanoparticles leaves intact their morphology, magnetic and plasmonic properti...

  17. Separation and preconcentration of riboflavin from human plasma using polythionine coated magnetite/hydroxyapatite nanocomposite prior to analysis by surfactant-enhanced fluorimetry

    Science.gov (United States)

    Farzin, Leila; Shamsipur, Mojtaba

    2017-09-01

    The exploration of novel adsorption properties of conductive polymers based on hybridization with biocompatible nanomaterials receives an increasing interest. In this regard, hydroxyapatite (HA) bioceramic is of critical importance mainly owing to its facile synthesis, high surface area, economic and low toxicity in biological environments. In this work, we first prepared and characterized a magnetite/hydroxyapatite (Fe3O4/HA) nanocomposite using the bio-waste chicken eggshell via an attractive green way that involved low cost and irrespective of toxicity. Then, polythionine as a novel class of conductive polymers was in situ coated on the synthesized magnetic bioceramic for the separation and preconcentration of riboflavin (vitamin B2) in human plasma before its fluorimetric determination. Considering the putative role of riboflavin in protecting against cancer and cardiovascular diseases, it is essential to evaluate this vitamin in biological fluids. The described method possesses a linear range of 0.75-262.5 μg L- 1 (R2 = 0.9985) and a detection limit of 0.20 μg L- 1 (signal-to-noise ratio of 3). The relative standard deviations (RSDs) for single-sorbent repeatability and sorbent-to-sorbent reproducibility were less than 4.0% and 7.6% (n = 5), respectively. The respective enrichment factor and extraction recovery of the method found to be 35.7 and 98.4%. The analytical performance of method for riboflavin was characterized by good consistency of the results with those obtained by the enzyme-linked immunosorbent assay (ELISA) conventional method (p-value of < 0.05). The optimized protocol intended for control determinations of riboflavin in human subjects and is addressed to clinical laboratories.

  18. Silica Nanoparticles Functionalized with Zwitterionic Sulfobetaine Siloxane for Application as a Versatile Antifouling Coating System.

    Science.gov (United States)

    Knowles, Brianna R; Wagner, Pawel; Maclaughlin, Shane; Higgins, Michael J; Molino, Paul J

    2017-06-07

    The growing need to develop surfaces able to effectively resist biological fouling has resulted in the widespread investigation of nanomaterials with potential antifouling properties. However, the preparation of effective antifouling coatings is limited by the availability of reactive surface functional groups and our ability to carefully control and organize chemistries at a materials' interface. Here, we present two methods of preparing hydrophilic low-fouling surface coatings through reaction of silica-nanoparticle suspensions and predeposited silica-nanoparticle films with zwitterionic sulfobetaine (SB). Silica-nanoparticle suspensions were functionalized with SB across three pH conditions and deposited as thin films via a simple spin-coating process to generate hydrophilic antifouling coatings. In addition, coatings of predeposited silica nanoparticles were surface functionalized via exposure to zwitterionic solutions. Quartz crystal microgravimetry with dissipation monitoring was employed as a high throughput technique for monitoring and optimizing reaction to the silica-nanoparticle surfaces. Functionalization of nanoparticle films was rapid and could be achieved over a wide pH range and at low zwitterion concentrations. All functionalized particle surfaces presented a high degree of wettability and resulted in large reductions in adsorption of bovine serum albumin protein. Particle coatings also showed a reduction in adhesion of fungal spores (Epicoccum nigrum) and bacteria (Escherichia coli) by up to 87 and 96%, respectively. These results indicate the potential for functionalized nanosilicas to be further developed as versatile fouling-resistant coatings for widespread coating applications.

  19. Porous palladium coated conducting polymer nanoparticles for ultrasensitive hydrogen sensors

    Science.gov (United States)

    Lee, Jun Seop; Kim, Sung Gun; Cho, Sunghun; Jang, Jyongsik

    2015-12-01

    Hydrogen, a clean-burning fuel, is of key importance to various industrial applications, including fuel cells and in the aerospace and automotive industries. However, hydrogen gas is odorless, colorless, and highly flammable; thus appropriate safety protocol implementation and monitoring are essential. Highly sensitive hydrogen leak detection and surveillance sensor systems are needed; additionally, the ability to maintain uniformity through repetitive hydrogen sensing is becoming increasingly important. In this report, we detail the fabrication of porous palladium coated conducting polymer (3-carboxylate polypyrrole) nanoparticles (Pd@CPPys) to detect hydrogen gas. The Pd@CPPys are produced by means of facile alkyl functionalization and chemical reduction of a pristine 3-carboxylate polypyrrole nanoparticle-contained palladium precursor (PdCl2) solution. The resulting Pd@CPPy-based sensor electrode exhibits ultrahigh sensitivity (0.1 ppm) and stability toward hydrogen gas at room temperature due to the palladium sensing layer.Hydrogen, a clean-burning fuel, is of key importance to various industrial applications, including fuel cells and in the aerospace and automotive industries. However, hydrogen gas is odorless, colorless, and highly flammable; thus appropriate safety protocol implementation and monitoring are essential. Highly sensitive hydrogen leak detection and surveillance sensor systems are needed; additionally, the ability to maintain uniformity through repetitive hydrogen sensing is becoming increasingly important. In this report, we detail the fabrication of porous palladium coated conducting polymer (3-carboxylate polypyrrole) nanoparticles (Pd@CPPys) to detect hydrogen gas. The Pd@CPPys are produced by means of facile alkyl functionalization and chemical reduction of a pristine 3-carboxylate polypyrrole nanoparticle-contained palladium precursor (PdCl2) solution. The resulting Pd@CPPy-based sensor electrode exhibits ultrahigh sensitivity (0.1 ppm

  20. SiO2 coating of silver nanoparticles by photoinduced chemical vapor deposition

    International Nuclear Information System (INIS)

    Boies, Adam M; Girshick, Steven L; Roberts, Jeffrey T; Zhang Bin; Nakamura, Toshitaka; Mochizuki, Amane

    2009-01-01

    Gas-phase silver nanoparticles were coated with silicon dioxide (SiO 2 ) by photoinduced chemical vapor deposition (photo-CVD). Silver nanoparticles, produced by inert gas condensation, and a SiO 2 precursor, tetraethylorthosilicate (TEOS), were exposed to vacuum ultraviolet (VUV) radiation at atmospheric pressure and varying temperatures. The VUV photons dissociate the TEOS precursor, initiating a chemical reaction that forms SiO 2 coatings on the particle surfaces. Coating thicknesses were measured for a variety of operation parameters using tandem differential mobility analysis and transmission electron microscopy. The chemical composition of the particle coatings was analyzed using energy dispersive x-ray spectrometry and Fourier transform infrared spectroscopy. The highest purity films were produced at 300-400 0 C with low flow rates of additional oxygen. The photo-CVD coating technique was shown to effectively coat nanoparticles and limit core particle agglomeration at concentrations up to 10 7 particles cm -3 .

  1. Preparation and Characterization of Chitosan-coated Fe3O4 Nanoparticles using Ex-Situ Co-Precipitation Method and Tripolyphosphate/Sulphate as Dual Crosslinkers

    Science.gov (United States)

    Wulandari, Ika O.; Mardila, Vita T.; Santjojo, D. J. Djoko H.; Sabarudin, Akhmad

    2018-01-01

    The unique properties of nanomaterial provide great opportunities to develop in several fields. Several types of nanoparticles have been proven beneficial for biomedical and therapeutic agent development. Particularly for clinical use, nanoparticles must be biocompatible and non-toxic. Iron oxide nanoparticles consist of either magnetite (Fe3O4) or maghemite (γ-Fe2O3) was eligible to use for in vivo application including targeting drug delivery. Due to their distinct properties, these nanoparticles could be directed to the specific target under external magnetic field. However, nanoparticles have a tendency to form agglomeration. Therefore, surface modification was required to reduce the agglomeration. In this study, nanoparticles of Fe3O4 were produced and coated by biomaterial (chitosan) using ex-situ co-precipitation method. Nanoparticles of Fe3O4 were synthesized by adding ammonia water into iron ferric and ferrous solution. Synthesis process of Fe3O4 was conducted prior to adding chitosan. Chitosan was then cross-linked by a combination of tripolyphosphate/sulphate. The different composition ratio and crosslinking time provide the different physical and magnetic characteristics of nanoparticles. Particle and crystallite size was determined by using Scanning Electron Microscopy (SEM) and X-Ray Diffraction (XRD) respectively, whereas magnetic characteristic was determined by Electron Spin Resonance (ESR). The results showed that the ratio enhancement between chitosan: Fe3O4 increase the particle size, while decreased the crystallite size. Morphology and particle size were influenced by the ratio of crosslinkers. It was found that the higher tripolyphosphate content was contributed to the small size and more spherical morphology. In addition, the influence of crosslinking time toward crystallite size was determined by altering stirring time. The longer duration of crosslinking time, provide the larger crystallite size of chitosan-Fe3O4. There was an interesting

  2. Pyrolytic carbon coating for cytocompatibility of titanium oxide nanoparticles: a promising candidate for medical applications

    International Nuclear Information System (INIS)

    Behzadi, Shahed; Simchi, Abdolreza; Imani, Mohammad; Yousefi, Mohammad; Galinetto, Pietro; Amiri, Houshang; Stroeve, Pieter; Mahmoudi, Morteza

    2012-01-01

    Nanoparticles for biomedical use must be cytocompatible with the biological environment that they are exposed to. Current research has focused on the surface functionalization of nanoparticles by using proteins, polymers, thiols and other organic compounds. Here we show that inorganic nanoparticles such as titanium oxide can be coated by pyrolytic carbon (PyC) and that the coating has cytocompatible properties. Pyrolization and condensation of methane formed a thin layer of pyrolytic carbon on the titanium oxide core. The formation of the PyC shell retards coalescence and sintering of the ceramic phase. Our MTT assay shows that the PyC-coated particles are cytocompatible at employed doses. (paper)

  3. Accumulation of magnetic iron oxide nanoparticles coated with variably sized polyethylene glycol in murine tumors

    DEFF Research Database (Denmark)

    Larsen, Esben Kjær Unmack; Nielsen, Thomas; Wittenborn, Thomas

    2012-01-01

    Iron oxide nanoparticles have found widespread applications in different areas including cell separation, drug delivery and as contrast agents. Due to water insolubility and stability issues, nanoparticles utilized for biological applications require coatings such as the commonly employed...... polyethylene glycol (PEG). Despite its frequent use, the influence of PEG coatings on the physicochemical and biological properties of iron nanoparticles has hitherto not been studied in detail. To address this, we studied the effect of 333–20 000 Da PEG coatings that resulted in larger hydrodynamic size...

  4. Comparison of cell uptake, biodistribution and tumor retention of folate-coated and PEG-coated gadolinium nanoparticles in tumor-bearing mice.

    Science.gov (United States)

    Oyewumi, Moses O; Yokel, Robert A; Jay, Michael; Coakley, Tricia; Mumper, Russell J

    2004-03-24

    The purpose of these studies was to compare the cell uptake, biodistribution and tumor retention of folate-coated and PEG-coated gadolinium (Gd) nanoparticles. Gd is a potential agent for neutron capture therapy (NCT) of tumors. Gd nanoparticles were engineered from oil-in-water microemulsion templates. To obtain folate-coated nanoparticles, a folate ligand [folic acid chemically linked to distearoylphosphatidylethanolamine (DSPE) via a PEG spacer MW 3350] was included in nanoparticle preparations. Similarly, control nanoparticles were coated with DSPE-PEG-MW 3350 (PEG-coated). Nanoparticles were characterized based on size, size distribution, morphology, biocompatibility and tumor cell uptake. In vivo studies were carried out in KB (human nasopharyngeal carcinoma) tumor-bearing athymic mice. Biodistribution and tumor retention studies were carried out at pre-determined time intervals after injection of nanoparticles (10 mg/kg). Gd nanoparticles did not aggregate platelets or activate neutrophils. The retention of nanoparticles in the blood 8, 16 and 24 h post-injection was 60%, 13% and 11% of the injected dose (ID), respectively. A maximum Gd tumor localization of 33+/-7 microg Gd/g was achieved. Both folate-coated and PEG-coated nanoparticles had comparable tumor accumulation. However, the cell uptake and tumor retention of folate-coated nanoparticles was significantly enhanced over PEG-coated nanoparticles. Thus, the benefits of folate ligand coating were to facilitate tumor cell internalization and retention of Gd-nanoparticles in the tumor tissue. The engineered nanoparticles may have potential in tumor-targeted delivery of Gd thereby enhancing the therapeutic success of NCT.

  5. Magnetite (Fe3O4 Nanoparticles Alleviate Growth Inhibition and Oxidative Stress Caused by Heavy Metals in Young Seedlings of Cucumber (Cucumis Sativus L

    Directory of Open Access Journals (Sweden)

    Konate Alexandre

    2017-01-01

    Full Text Available Accumulation of heavy metals in the ecosystem and their toxic effects through food chain can cause serious ecological and health problems. In the present study, experiments were performed to understand how the addition of magnetite (Fe3O4 nanoparticles reduces the toxicity caused by Cd, Pb, Cu, and Zn in cucumber plants. Plant growth parameters, lipid peroxidation, and antioxidant enzymes were measured in seedling samples treated with either metals or metals supplemented with Fe3O4 to demonstrate the reduction in metal-induced oxidative stress conferred by Fe3O4. Results showed that the toxic effect of metals on seedling growth parameters can be arranged in the rank order of inhibition as follows: Cu > Cd > Zn > Pb. Exposure to metals significantly decreased the seedlings growth, the activities of superoxide dismutase (SOD and peroxidases (POD, while the malondialdehyde (MDA content significantly increased in cucumber seedlings. The reducing activity of nano-Fe3O4 against heavy metals stresses was confirmed in this study by the decrease in MDA content. The correlation between the decrease of MDA concentration and the increase in SOD and POD activities in the presence of nano-Fe3O4 suggest that the MDA reduction in the tested seedlings can result from the increased enzyme activity.

  6. Dialkylamide as Both Capping Agent and Surfactant in a Direct Solvothermal Synthesis of Magnetite and Titania Nanoparticles

    Czech Academy of Sciences Publication Activity Database

    Cara, C.; Musinu, A.; Mameli, V.; Ardu, A.; Nižňanský, D.; Buršík, Josef; Scorciapino, M. A.; Manzo, G.; Cannas, C.

    2015-01-01

    Roč. 15, č. 5 (2015), s. 2364-2372 ISSN 1528-7483 R&D Projects: GA ČR(CZ) GA14-18392S Institutional support: RVO:61388980 Keywords : Nanomagnetics * Nanoparticles * Nuclear magnetic resonance * Fourier transform infrared spectroscopy Subject RIV: CA - Inorganic Chemistry Impact factor: 4.425, year: 2015

  7. Monitoring of the aging of magnetic nanoparticles using Mössbauer spectroscopy

    Science.gov (United States)

    Rümenapp, Christine; Wagner, Friedrich E.; Gleich, Bernhard

    2015-04-01

    Magnetic nanoparticles made of magnetite have the advantage to be biocompatible and to have a good saturation magnetisation. In this work we show that magnetite nanoparticles change their magnetic and chemical characteristics over time, depending on their storage conditions. To determine the oxidation state of the iron in the core of the nanoparticles Mössbauer spectroscopy was used at 4.2 K. This method is very accurate, especially in distinguishing maghemite and magnetite. The nanoparticles prepared by a co-precipitation method and peptized using acidic media had a core diameter of 5-7 nm. The aging process was monitored until the core was completely oxidised to maghemite and no further change occurred. The greatest change in the magnetite content of the particles was seen during the first 12 h after preparation. To preserve the good magnetic characteristics of magnetite nanoparticles a coating that prevents oxidation is therefore essential. Our results show that the point in time of the characterisation of small magnetic nanoparticles is crucial for the results. Even though magnetite nanoparticles have been formed nearly stoichiometrically, their chemical properties change over time.

  8. Synthesis and Characterization of Fe3O4 Nanoparticles using Polyvinyl Alcohol (PVA) as Capping Agent and Glutaraldehyde (GA) as Crosslinker

    Science.gov (United States)

    Budi Hutami Rahayu, Lale; Oktavia Wulandari, Ika; Herry Santjojo, Djoko; Sabarudin, Akhmad

    2018-01-01

    The use of polyvinyl alcohol (PVA) as a capping agent and glutaraldehyde (GA) as a crosslinker for a synthesis of magnetite (Fe3O4) nanoparticles is able to reduce agglomeration of produced Fe3O4. Additionally, oxidation of Fe3O4 by air could be avoided. The synthesis is carried out in two steps: first step, magnetite (Fe3O4) nanoparticles were prepared by dissolving the FeCl3.6H2O and FeCl2.4H2O in alkaline media (NH3.H2O). The second step, magnetite nanoparticles were coated with polyvinyl alcohol (PVA) and glutaraldehyde (GA) to obtain Fe3O4-PVA-GA. The latter material was then characterized by FTIR to determine the typical functional groups of magnetite coated with PVA-GA. X-ray Diffraction analysis was used to determine structure and size of crystal as well as the percentage of magnetite produced. It was found that the produced nanoparticles have crystal sizes around 4-9 nm with the cubic crystal structure. The percentage of magnetite phase increases when the amount of glutaraldehyde increased. SEM-EDX was employed to assess the surface morphology and elemental composition of the resulted nanoparticles. The magnetic character of the magnetite and Fe3O4- PVA-GA were studied using Electron Spin Resonance.

  9. Surface functionalization of dopamine coated iron oxide nanoparticles for various surface functionalities

    Energy Technology Data Exchange (ETDEWEB)

    Sherwood, Jennifer; Xu, Yaolin; Lovas, Kira [Chemical and Biological Engineering, The University of Alabama, Tuscaloosa , AL 35487 (United States); Qin, Ying [Alabama Innovation and Mentoring of Entrepreneurs, The University of Alabama, Tuscaloosa, AL 35487 (United States); Bao, Yuping, E-mail: ybao@eng.ua.edu [Chemical and Biological Engineering, The University of Alabama, Tuscaloosa , AL 35487 (United States)

    2017-04-01

    We present effective conjugation of four small molecules (glutathione, cysteine, lysine, and Tris(hydroxymethyl)aminomethane) onto dopamine-coated iron oxide nanoparticles. Conjugation of these molecules could improve the surface functionality of nanoparticles for more neutral surface charge at physiological pH and potentially reduce non-specific adsorption of proteins to nanoparticles surfaces. The success of conjugation was evaluated with dynamic light scattering by measuring the surface charge changes and Fourier transform infrared spectroscopy for surface chemistry analysis. The stability of dopamine-coated nanoparticles and the ability of conjugated nanoparticles to reduce the formation of protein corona were evaluated by measuring the size and charge of the nanoparticles in biological medium. This facile conjugation method opens up possibilities for attaching various surface functionalities onto iron oxide nanoparticle surfaces for biomedical applications.

  10. Surface functionalization of dopamine coated iron oxide nanoparticles for various surface functionalities

    International Nuclear Information System (INIS)

    Sherwood, Jennifer; Xu, Yaolin; Lovas, Kira; Qin, Ying; Bao, Yuping

    2017-01-01

    We present effective conjugation of four small molecules (glutathione, cysteine, lysine, and Tris(hydroxymethyl)aminomethane) onto dopamine-coated iron oxide nanoparticles. Conjugation of these molecules could improve the surface functionality of nanoparticles for more neutral surface charge at physiological pH and potentially reduce non-specific adsorption of proteins to nanoparticles surfaces. The success of conjugation was evaluated with dynamic light scattering by measuring the surface charge changes and Fourier transform infrared spectroscopy for surface chemistry analysis. The stability of dopamine-coated nanoparticles and the ability of conjugated nanoparticles to reduce the formation of protein corona were evaluated by measuring the size and charge of the nanoparticles in biological medium. This facile conjugation method opens up possibilities for attaching various surface functionalities onto iron oxide nanoparticle surfaces for biomedical applications.

  11. Chitosan-coated nickel-ferrite nanoparticles as contrast agents in magnetic resonance imaging

    International Nuclear Information System (INIS)

    Ahmad, Tanveer; Bae, Hongsub; Iqbal, Yousaf; Rhee, Ilsu; Hong, Sungwook; Chang, Yongmin; Lee, Jaejun; Sohn, Derac

    2015-01-01

    We report evidence for the possible application of chitosan-coated nickel-ferrite (NiFe 2 O 4 ) nanoparticles as both T 1 and T 2 contrast agents in magnetic resonance imaging (MRI). The coating of nickel-ferrite nanoparticles with chitosan was performed simultaneously with the synthesis of the nickel-ferrite nanoparticles by a chemical co-precipitation method. The coated nanoparticles were cylindrical in shape with an average length of 17 nm and an average width of 4.4 nm. The bonding of chitosan onto the ferrite nanoparticles was confirmed by Fourier transform infrared spectroscopy. The T 1 and T 2 relaxivities were 0.858±0.04 and 1.71±0.03 mM −1 s −1 , respectively. In animal experimentation, both a 25% signal enhancement in the T 1 -weighted mage and a 71% signal loss in the T 2 -weighted image were observed. This demonstrated that chitosan-coated nickel-ferrite nanoparticles are suitable as both T 1 and T 2 contrast agents in MRI. We note that the applicability of our nanoparticles as both T 1 and T 2 contrast agents is due to their cylindrical shape, which gives rise to both inner and outer sphere processes of nanoparticles. - Highlights: • Chitosan-coated nickel-ferrite (Ni-Fe 2 O 4 ) nanoparticles were synthesized in an aqueous system by chemical co-precipitation. • The characterization of bare and chitosan-coated nanoparticles were performed using various analytical tools, such as TEM, FTIR, XRD, and VMS. • We evaluated the coated particles as potential T 1 and T 2 contrast agents for MRI by measuring T 1 and T 2 relaxation times as a function of iron concentration. • Both T 1 and T 2 effects were also observed in animal experimentation

  12. The Role of Dextran Coatings on the Cytotoxicity Properties of Ceria Nanoparticles Toward Bone Cancer Cells

    Science.gov (United States)

    Yazici, Hilal; Alpaslan, Ece; Webster, Thomas J.

    2015-04-01

    Cerium oxide nanoparticles have demonstrated great potential as antioxidant and radioprotective agents for nanomedicine applications especially for cancer therapy. The surface chemistry of nanoparticles is an important property that has a significant effect on their performance in biological applications including cancer diagnosis, cancer treatment, and bacterial infection. Recently, various nanosized cerium oxide particles with different types of polymer coatings have been developed to improve aqueous solubility and allow for surface functionalization for distinct applications. In this study, the role of ceria nanoparticles coated with dextran on the cytotoxicity properties of bone cancer cells was shown. Specifically, 0.1 M and 0.01 M dextran-coated, coated ceria nanoparticles was evaluated against osteosarcoma cells. A change in cell viability was observed when treating osteosarcoma cells with 0.1 M dextran-coated ceria nanoparticles in the 250 -1000 μg/mL concentration range. In contrast, minimal toxicity to bone cancer cells was observed for the 0.01 M dextran coating after 3 days compared with the 0.1 M dextran coating. These results indicated that surface dextran functionalization had a positive impact on the cytotoxicity of cerium oxide nanoparticles against osteosarcoma cells.

  13. Acute toxicity and pharmacokinetics of 13 nm-sized PEG-coated gold nanoparticles

    International Nuclear Information System (INIS)

    Cho, Wan-Seob; Cho, Minjung; Jeong, Jinyoung; Choi, Mina; Cho, Hea-Young; Han, Beom Seok; Kim, Sheen Hee; Kim, Hyoung Ook; Lim, Yong Taik; Chung, Bong Hyun; Jeong, Jayoung

    2009-01-01

    In general, gold nanoparticles are recognized as being as nontoxic. Still, there have been some reports on their toxicity, which has been shown to depend on the physical dimension, surface chemistry, and shape of the nanoparticles. In this study, we carry out an in vivo toxicity study using 13 nm-sized gold nanoparticles coated with PEG (MW 5000). In our findings the 13 nm sized PEG-coated gold nanoparticles were seen to induce acute inflammation and apoptosis in the liver. These nanoparticles were found to accumulate in the liver and spleen for up to 7 days after injection and to have long blood circulation times. In addition, transmission electron microscopy showed that numerous cytoplasmic vesicles and lysosomes of liver Kupffer cells and spleen macrophages contained the PEG-coated gold nanoparticles. These findings of toxicity and kinetics of PEG-coated gold nanoparticles may have important clinical implications regarding the safety issue as PEG-coated gold nanoparticles are widely used in biomedical applications

  14. Size-Controlled Dissolution of Organic-Coated Silver Nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Rui; Levard, Clément; Marinakos, Stella M.; Cheng, Yingwen; Liu, Jie; Michel, F. Marc; Brown, Jr., Gordon E.; Lowry, Gregory V. (Duke)

    2012-04-02

    The solubility of Ag NPs can affect their toxicity and persistence in the environment. We measured the solubility of organic-coated silver nanoparticles (Ag NPs) having particle diameters ranging from 5 to 80 nm that were synthesized using various methods, and with different organic polymer coatings including poly(vinylpyrrolidone) and gum arabic. The size and morphology of Ag NPs were characterized by transmission electron microscopy (TEM). X-ray absorption fine structure (XAFS) spectroscopy and synchrotron-based total X-ray scattering and pair distribution function (PDF) analysis were used to determine the local structure around Ag and evaluate changes in crystal lattice parameters and structure as a function of NP size. Ag NP solubility dispersed in 1 mM NaHCO{sub 3} at pH 8 was found to be well correlated with particle size based on the distribution of measured TEM sizes as predicted by the modified Kelvin equation. Solubility of Ag NPs was not affected by the synthesis method and coating as much as by their size. Based on the modified Kelvin equation, the surface tension of Ag NPs was found to be {approx}1 J/m{sup 2}, which is expected for bulk fcc (face centered cubic) silver. Analysis of XAFS, X-ray scattering, and PDFs confirm that the lattice parameter, {alpha}, of the fcc crystal structure of Ag NPs did not change with particle size for Ag NPs as small as 6 nm, indicating the absence of lattice strain. These results are consistent with the finding that Ag NP solubility can be estimated based on TEM-derived particle size using the modified Kelvin equation for particles in the size range of 5-40 nm in diameter.

  15. Assessing antibacterial effect of filter media coated with silver nanoparticles against Bacillus spp

    Directory of Open Access Journals (Sweden)

    Mahmood Nafisi Bahabadi

    2016-04-01

    Full Text Available Background: Nanotechnology is a field of applied science and technology covering a broad range of topics. Use of nanotechnology and especially silver nanoparticles in control of bacterial diseases and infections has been studied in the recent years. The aim of the present study was to investigate the in vitro antibacterial effect of filter media coated with silver nanoparticles against Bacillus spp. Materials and methods: In this research, first, the antibacterial effects of silver nanoparticles against mentioned bacteria were evaluated by microdilution method in Broth medium. After confidence of inhibitory effect of colloidal silver nanoparticles, antibacterial effect of filter media coated with silver nanoparticles was evaluated via in vitro microbiology tests (zone of inhibition test and test tube test. Results: Present study showed that colloidal silver nanoparticles have good antimicrobial effects against tested bacteria, so that MIC and MBC of silver nanoparticles for Bacillus spp. were calculated 3.9 and 31.25 mg/L, respectively. Also significant decrease was observed in bacterial growth after exposure to filter media coated with silver nanoparticles in test tube test and  zone of inhibition test (P≤ 5%. Conclusion: The results of this research indicate that filter media coated with silver nanoparticles have considerable antimicrobial effects; therefore they could possibly be used as excellent antibacterial water filters and would have several applications in other sectors.

  16. Synthesis and characterization of carbon coated nanoparticles produced by a continuous low-pressure plasma process

    Energy Technology Data Exchange (ETDEWEB)

    Panchal, Vineet; Neergat, Manoj [Indian Institute of Technology Bombay, Department of Energy Science and Engineering (India); Bhandarkar, Upendra, E-mail: bhandarkar@iitb.ac.in [Indian Institute of Technology Bombay, Department of Mechanical Engineering (India)

    2011-09-15

    Core-shell nanoparticles coated with carbon have been synthesized in a single chamber using a continuous and entirely low-pressure plasma-based process. Nanoparticles are formed in an argon plasma using iron pentacarbonyl Fe(CO){sub 5} as a precursor. These particles are trapped in a pure argon plasma by shutting off the precursor and then coated with carbon by passing acetylene along with argon as the main background gas. Characterization of the particles was carried out using TEM for morphology, XPS for elemental composition and PPMS for magnetic properties. Iron nanoparticles obtained were a mixture of FeO and Fe{sub 3}O{sub 4}. TEM analysis shows an average size of 7-14 nm for uncoated particles and 15-24 nm for coated particles. The effect of the carbon coating on magnetic properties of the nanoparticles is studied in detail.

  17. Efficient light extraction from GaN LEDs using gold-coated ZnO nanoparticles

    KAUST Repository

    Alhadidi, A.

    2015-11-01

    We experimentally demonstrate the effect of depositing gold-coated ZnO nanoparticles on the surface of GaN multi-quantum well LED structures. We show that this method can significantly increase the amount of extracted light.

  18. Preparation of Rhodamine B Fluorescent Poly(methacrylic acid) Coated Gelatin Nanoparticles

    OpenAIRE

    Gan, Zhenhai; Ju, Jianhui; Zhang, Ting; Wu, Daocheng

    2011-01-01

    Poly(methacrylic acid) (PMAA)-coated gelatin nanoparticles encapsulated with fluorescent dye rhodamine B were prepared by the coacervation method with the aim to retard the release of rhodamine B from the gelatin matrix. With sodium sulfate as coacervation reagent for gelatin, a kind of biopolymer with excellent biocompatibility, the formed gelatin nanoparticles were cross-linked by formaldehyde followed by the polymerization of methacrylic acid coating. The fluorescent poly(methacrylic acid)...

  19. Biocarbon-coated LiFePO4 nucleus nanoparticles enhancing electrochemical performances

    DEFF Research Database (Denmark)

    Zhang, X.G.; Zhang, X.D.; He, W.

    2012-01-01

    We report a green biomimetic method to synthesize biocarbon-coated LiFePO4 nucleus nanoparticles using yeast cells as both a structural template and a biocarbon source for high-power lithium-ion batteries.......We report a green biomimetic method to synthesize biocarbon-coated LiFePO4 nucleus nanoparticles using yeast cells as both a structural template and a biocarbon source for high-power lithium-ion batteries....

  20. Effect of surfactant coating on magnetic properties of Fe3O4 nanoparticles: ESR study

    International Nuclear Information System (INIS)

    Koeseoglu, Yueksel

    2006-01-01

    Magnetic properties of surfactant-coated and uncoated superparamagnetic iron oxide nanoparticles, Fe 3 O 4 (SPION) were investigated by electron spin resonance (ESR) technique. For all samples, a strong and broad single ESR signal has been observed at all temperatures. A strong temperature dependence of ESR linewidth and resonance field is observed. Also, there is a strong effect of surfactant coating on magnetic properties of Fe 3 O 4 nanoparticles. While the resonance field is decreasing by coating, the linewidth of the ESR spectra is increasing. These changes in resonance field and the linewidth are attributed to the decrease in effective magnetic moment due to a non-collinear spin structure originated from the pinning of the surface spins and coated surfactant at the interface of nanoparticles. Also, the changes are due to the contribution of the volume of the diamagnetic coating mass to the sample volume

  1. Moessbauer Characterization of Magnetite/Polyaniline Magnetic Nanocomposite

    International Nuclear Information System (INIS)

    Rodriguez, Anselmo F. R.; Faria, Fernando S. E. D. V.; Lopez, Jorge L.; Mesquita, Antonio G. G.; Coaquira, Jose A. H.; Oliveira, Aderbal C.; Morais, Paulo C.; Azevedo, Ricardo B.; Araujo, Ana C. V. de; Alves, Severino Jr.; Azevedo, Walter M. de

    2010-01-01

    Aniline surface coated Fe 3 O 4 nanoparticles have been successfully synthesized by UV irradiation varying the time and the acid media (HCl, HNO 3 , or H 2 SO 4 ). The synthesized material represents a promising platform for application in nerve regeneration. XRD patterns are consistent with the crystalline structure of magnetite. Nevertheless, for UV irradiation times longer than 2 h, extra XRD lines reveal the presence of goethite. The mean crystallite size of uncoated particles is estimated to be 25.4 nm, meanwhile that size is reduced to 19.9 nm for the UV irradiated sample in HCl medium for 4 h. Moessbauer spectra of uncoated nanoparticles reveal the occurrence of thermal relaxation at room temperature, while the 77 K-Moessbauer spectrum suggests the occurrence of electron localization effects similar to that expected in bulk magnetite. The Mossbauer spectra of UV irradiated sample in HCl medium during 4 h, confirms the presence of the goethite phase. For this sample, the thermal relaxation is more evident, since the room temperature spectrum shows larger spectral area for the nonmagnetic component due to the smaller crystallite size. Meanwhile, the 77 K-Moessbauer spectrum suggests the absence of the electron localization effect above 77 K.

  2. In vitro antiplasmodial activity of PDDS-coated metal oxide nanoparticles against Plasmodium falciparum

    Science.gov (United States)

    Jacob Inbaneson, Samuel; Ravikumar, Sundaram

    2013-06-01

    Malaria is the most important parasitic disease, leading to annual death of about one million people and the Plasmodium falciparum develops resistant to well-established antimalarial drugs. The newest antiplasmodial drug from metal oxide nanoparticles helps in addressing this problem. Commercial nanoparticles such as Fe3O4, MgO, ZrO2, Al2O3 and CeO2 coated with PDDS and all the coated and non-coated nanoparticles were screened for antiplasmodial activity against P. falciparum. The Al2O3 nanoparticles (71.42 ± 0.49 μg ml-1) showed minimum level of IC50 value and followed by MgO (72.33 ± 0.37 μg ml-1) and Fe3O4 nanoparticles (77.23 ± 0.42 μg ml-1). The PDDS-Fe3O4 showed minimum level of IC50 value (48.66 ± 0.45 μg ml-1), followed by PDDS-MgO (60.28 ± 0.42 μg ml-1) and PDDS-CeO2 (67.06 ± 0.61 μg ml-1). The PDDS-coated metal oxide nanoparticles showed superior antiplasmodial activity than the non-PDDS-coated metal oxide nanoparticles. Statistical analysis reveals that, significant in vitro antiplasmodial activity ( P activity and it might be used for the development of antiplasmodial drugs.

  3. Zirconia-doped nanoparticles: organic coating, polymeric entrapment and application as dual-imaging agents

    OpenAIRE

    Rebuttini, Valentina; Pucci, Andrea; Arosio, Paolo; Bai, Xue; Locatelli, Erica; Pinna, Nicola; Lascialfari, Alessandro; Franchini, Mauro Comes

    2013-01-01

    Zirconia nanoparticles doped with Eu3+, Tb3+ and Gd3+ ions have been synthesized following the benzyl alcohol route. The nanoparticles were coated with N-hydroxydodecanamide and encapsulated in PLGA-b-PEG-COOH nanomicelles. The magnetic and fluorescent properties of these hybrid nanocarriers were investigated, proving them to be potential dual-imaging contrast agents.

  4. The detection of HBV DNA with gold-coated iron oxide nanoparticle gene probes

    International Nuclear Information System (INIS)

    Xi Dong; Luo Xiaoping; Lu Qianghua; Yao Kailun; Liu Zuli; Ning Qin

    2008-01-01

    Gold-coated iron oxide nanoparticle Hepatitis B virus (HBV) DNA probes were prepared, and their application for HBV DNA measurement was studied. Gold-coated iron oxide nanoparticles were prepared by the citrate reduction of tetra-chloroauric acid in the presence of iron oxide nanoparticles which were added as seeds. With a fluorescence-based method, the maximal surface coverage of hexaethiol 30-mer oligonucleotides and the maximal percentage of hybridization strands on gold-coated iron oxide nanoparticles were (120 ± 8) oligonucleotides per nanoparticle, and (14 ± 2%), respectively, which were comparable with those of (132 ± 10) and (22 ± 3%) in Au nanoparticle groups. Large network aggregates were formed when gold-coated iron oxide nanoparticle HBV DNA gene probe was applied to detect HBV DNA molecules as evidenced by transmission electron microscopy and the high specificity was verified by blot hybridization. Our results further suggested that detecting DNA with iron oxide nanoparticles and magnetic separator was feasible and might be an alternative effective method

  5. Core–shell-typed Ag-SiO2 nanoparticles as solar selective coating materials

    International Nuclear Information System (INIS)

    Gao, Tao; Jelle, Bjørn Petter; Gustavsen, Arild

    2013-01-01

    Silver (Ag) nanoparticles with typical diameter of about 50 nm have been prepared via a polyol process. The as-prepared Ag nanoparticles are well crystallized and exhibit a characteristic surface plasmon resonance (SPR) band centered at ∼423 nm. The SPR band shows a strong dependence on the sizes of Ag nanoparticles and the types of the dielectric medium. Core–shell-typed Ag-SiO 2 nanoparticles have also been prepared by depositing a thin layer (∼25 nm) of silica on Ag nanoparticles. The core–shell-typed Ag-SiO 2 nanoparticles show similar optical behaviors (absorption, transmission, and reflection) but enhanced stability compared to those of the Ag nanoparticles, indicating that the core–shell-typed Ag-SiO 2 nanoparticles may be used as solar selective coating materials for architectural window applications.

  6. Poly-l-lysine-coated magnetic nanoparticles as intracellular actuators for neural guidance

    Directory of Open Access Journals (Sweden)

    Riggio C

    2012-06-01

    Full Text Available Cristina Riggio,1,* Maria Pilar Calatayud,2,* Clare Hoskins,3 Josephine Pinkernelle,4 Beatriz Sanz,2 Teobaldo Enrique Torres,2,5 Manuel Ricardo Ibarra,2,5 Lijun Wang,3 Gerburg Keilhoff,4 Gerardo Fabian Goya,2,5 Vittoria Raffa,1,6 Alfred Cuschieri1,3 1Institute of Life Science, Scuola Superiore Sant’Anna, Piazza Martiri della Libertà, Pisa, Italy; 2Instituto de Nanociencia de Aragón, Universidad de Zaragoza. Mariano Esquillor, Zaragoza, Spain; 3IMSaT, Institute for Medical Science and Technology, University of Dundee, Dundee, Scotland; 4Otto-von-Guericke University, Institute of Biochemistry and Cell Biology, Magdeburg, Germany; 5Departamento de Física de la Materia Condensada, Facultad de Ciencias, Universidad de Zaragoza. Cerbuna 12, Zaragoza, Spain; 6Department of Biology, Università di Pisa, Pisa, Italy*These authors contributed equally to this workPurpose: It has been proposed in the literature that Fe3O4 magnetic nanoparticles (MNPs could be exploited to enhance or accelerate nerve regeneration and to provide guidance for regenerating axons. MNPs could create mechanical tension that stimulates the growth and elongation of axons. Particles suitable for this purpose should possess (1 high saturation magnetization, (2 a negligible cytotoxic profile, and (3 a high capacity to magnetize mammalian cells. Unfortunately, the materials currently available on the market do not satisfy these criteria; therefore, this work attempts to overcome these deficiencies.Methods: Magnetite particles were synthesized by an oxidative hydrolysis method and characterized based on their external morphology and size distribution (high-resolution transmission electron microscopy [HR-TEM] as well as their colloidal (Z potential and magnetic properties (Superconducting QUantum Interference Devices [SQUID]. Cell viability was assessed via Trypan blue dye exclusion assay, cell doubling time, and MTT cell proliferation assay and reactive oxygen species production

  7. New Silica Magnetite Sorbent: The Influence of Variations of Sodium Silicate Concentrations on Silica Magnetite Character

    Science.gov (United States)

    Azmiyawati, C.; Pratiwi, P. I.; Darmawan, A.

    2018-04-01

    The adsorption capacity of an adsorbent is determined by the adsorbent and the adsorbate properties. The character of the adsorbent will play a major role in its ability to adsorb the corresponding adsorbate. Therefore, in this study we looked at the effects of variations of sodium silicate concentrations on the resulting magnetite silica adsorbent properties. The application of silica coating on the magnetite was carried out through a sol-gel process with sodium silicate and HCl precursors. Based on the characterization data obtained, it was found that the silica coating on magnetite can increase the resistance to acid leaching, increase the particle size, but decrease the magnetic properties of the magnetite. Based on Gas Sorption Analyzer (GSA) and X-ray Difraction (XRD) data it can successively be determined that increase in concentration of sodium silicate will increase the surface area and amorphous structure of the Silica Magnetie.

  8. Transport of citrate-coated silver nanoparticles in unsaturated sand

    Energy Technology Data Exchange (ETDEWEB)

    Kumahor, Samuel K., E-mail: samuel.kumahor@ufz.de [Department of Soil Physics, Helmholtz Centre for Environmental Research–UFZ, Theodor-Lieser-Strasse 4, 06120 Halle-Saale (Germany); Hron, Pavel, E-mail: pavel.hron@iwr.uni-heidelberg.de [Interdisciplinary Center for Scientific Computing, University of Heidelberg, Im Neuenheimer Feld 368, Raum 422, 69120 Heidelberg (Germany); Metreveli, George, E-mail: metreveli@uni-landau.de [Universität Koblenz-Landau, Institute for Environmental Sciences, Group of Environmental and Soil Chemistry, Fortstr. 7, D-76829 Landau (Germany); Schaumann, Gabriele E., E-mail: schaumann@uni-landau.de [Universität Koblenz-Landau, Institute for Environmental Sciences, Group of Environmental and Soil Chemistry, Fortstr. 7, D-76829 Landau (Germany); Vogel, Hans-Jörg, E-mail: hans-joerg.vogel@ufz.de [Department of Soil Physics, Helmholtz Centre for Environmental Research–UFZ, Theodor-Lieser-Strasse 4, 06120 Halle-Saale (Germany); Institute of Soil Science and Plant Nutrition, Martin-Luther-University Halle-Wittenberg, Von-Seckendorff-Platz 3, 06120 Halle-Saale (Germany)

    2015-12-01

    Chemical factors and physical constraints lead to coupled effects during particle transport in unsaturated porous media. Studies on unsaturated transport as typical for soils are currently scarce. In unsaturated porous media, particle mobility is determined by the existence of an air–water interface in addition to a solid–water interface. To this end, we measured breakthrough curves and retention profiles of citrate-coated Ag nanoparticles in unsaturated sand at two pH values (5 and 9) and three different flow rates corresponding to different water contents with 1 mM KNO{sub 3} as background electrolyte. The classical DLVO theory suggests unfavorable deposition conditions at the air–water and solid–water interfaces. The breakthrough curves indicate modification in curve shapes and retardation of nanoparticles compared to inert solute. Retention profiles show sensitivity to flow rate and pH and this ranged from almost no retention for the highest flow rate at pH = 9 to almost complete retention for the lowest flow rate at pH = 5. Modeling of the breakthrough curves, thus, required coupling two parallel processes: a kinetically controlled attachment process far from equilibrium, responsible for the shape modification, and an equilibrium sorption, responsible for particle retardation. The non-equilibrium process and equilibrium sorption are suggested to relate to the solid–water and air–water interfaces, respectively. This is supported by the DLVO model extended for hydrophobic interactions which suggests reversible attachment, characterized by a secondary minimum (depth 3–5 kT) and a repulsive barrier at the air–water interface. In contrast, the solid–water interface is characterized by a significant repulsive barrier and the absence of a secondary minimum suggesting kinetically controlled and non-equilibrium interaction. This study provides new insights into particle transport in unsaturated porous media and offers a model concept representing the

  9. Microemulsion Synthesis of Nanoparticles

    Directory of Open Access Journals (Sweden)

    Gotić, M.

    2013-11-01

    Full Text Available Nanoparticles and nanomaterials have wide applications in electronics, physics, material design, being also utilized as sensors, catalysts, and more and more in biomedicine. Microemulsions are an exceptionally suitable medium for the synthesis of nanoparticles due to their thermodynamical stability, great solubility of both polar and nonpolar components, as well as their ability to control the size, dispersity and shape of the particles. This review presents microemulsion techniques for the synthesis of inorganic nanoparticles. It takes place in water-in-oil microemulsions by mixing one microemulsion with a cationic precursor, and the other with a precipitating or reducing agent, or by direct addition of reducing agents or gas (O2, NH3 ili CO2 into microemul sion (Fig. 1. Metal nanoparticles are used as catalysts, sensors, ferrofluids etc. They are produced by reducing the metal cation with a suitable reducing agent. In a similar way, one can prepare nanoparticles of alloys from the metal salts, provided that the metals are mutually soluble. The microemulsion technique is also suitable for depositing nanoparticles onto various surfaces. Highly active catalysts made from nanoparticles of Pt, Pd, Rh and other noble metals may be obtained in this way. Metal oxides and hydroxides may be prepared by hydrolysis or precipitation in the water core of microemulsion. Precipitation can be initiated by adding the base or precipitating agent into the microemulsion with water solution of metal ions. Similarly, nanoparticles may be prepared of sulphides, halogenides, cyanides, carbonates, sulphates and other insoluble metal salts. To prevent oxidation of nanoparticles, especially Fe, the particles are coated with inert metals, oxides, various polymers etc. Coating may provide additional functionality; e.g. coating with gold allows subsequent functionalization with organic compounds containing sulphur, due to the strong Au–S bond. Polymer coatings decrease

  10. PEG-stearate coated solid lipid nanoparticles as levothyroxine carriers for oral administration

    Science.gov (United States)

    Kashanian, Soheila; Rostami, Elham

    2014-03-01

    In this study, poly ethylene glycol 100 stearate (PEG 100-S) was used to prepare coated solid lipid nanoparticles with loading levothyroxine sodium (levo-loaded PEG 100-S-coated SLNs) by microemulsification technique. Evaluation of the release kinetic of prepared colloidal carriers was conducted. The particle size and zeta potential of levo-loaded PEG 100-S-coated SLNs have been measured to be 187.5 nm and -23.0 mV, respectively, using photon correlation spectroscopy (PCS). Drug entrapment efficiency (EE) was calculated to be 99 %. Differential scanning calorimetry indicated that the majority of drug loaded in PEG 100-S-coated SLNs were in amorphous state which could be considered desirable for drug delivery. The purpose of this study was to develop a new nanoparticle system, consisting lipid nanoparticles coated with PEG 100-S. The modification procedure led to a reduction in the zeta potential values, varying from -40.0 to -23.0 mV for the uncoated and PEG-coated SLNs, respectively. Stability results of the nanoparticles in gastric and intestinal media show that the low pH of the gastric medium is responsible for the critical aggregation and degradation of the uncoated lipid nanoparticles. PEG 100-S-coated SLNs were more stable due to their polymer coating layer which prevented aggregation of SLNs. Consequently, it is possible that the PEG surrounds the particles reducing the attachment of enzymes and further degradation of the triglyceride cores. Shape and surface morphology of particles were determined by transition electron microscopy and scanning electron microscopy that revealed spherical shape of nanoparticles. In vitro drug release of PEG 100-S-coated SLNs was characterized using diffusion cell which showed a controlled release for drug.

  11. Carboxylated SiO2-coated α-Fe nanoparticles: towards a versatile platform for biomedical applications.

    Science.gov (United States)

    Kohara, Kaori; Yamamoto, Shinpei; Seinberg, Liis; Murakami, Tatsuya; Tsujimoto, Masahiko; Ogawa, Tetsuya; Kurata, Hiroki; Kageyama, Hiroshi; Takano, Mikio

    2013-03-28

    Carboxylated SiO2-coated α-Fe nanoparticles have been successfully prepared via CaH2-mediated reduction of SiO2-coated Fe3O4 nanoparticles followed by surface carboxylation. These α-Fe-based nanoparticles, which are characterized by ease of coating with additional functional groups, a large magnetization of 154 emu per g-Fe, enhanced corrosion resistivity, excellent aqueous dispersibility, and low cytotoxicity, have potential to be a versatile platform in biomedical applications.

  12. Gold-coated iron nanoparticles in transparent Si3N4 matrix thin films

    Science.gov (United States)

    Sánchez-Marcos, J.; Céspedes, E.; Jiménez-Villacorta, F.; Muñoz-Martín, A.; Prieto, C.

    2013-06-01

    A new method to prepare thin films containing gold-coated iron nanoparticles is presented. The ternary Fe-Au-Si3N4 system prepared by sequential sputtering has revealed a progressive variation of microstructures from Au/Fe/Au/Si3N4 multilayers to iron nanoparticles. Microstructural characterization by transmission electron microscopy, analysis of the magnetic properties and probing of the iron short-range order by X-ray absorption spectroscopy confirm the existence of a gold-coated iron nanoparticles of 1-2 nm typical size for a specific range of iron and gold contents per layer in the transparent silicon nitride ceramic matrix.

  13. Development and characterization of magnetic iron oxide nanoparticles with a cisplatin-bearing polymer coating for targeted drug delivery

    Directory of Open Access Journals (Sweden)

    Unterweger H

    2014-08-01

    Full Text Available Harald Unterweger,1 Rainer Tietze,1 Christina Janko,1 Jan Zaloga,1 Stefan Lyer,1 Stephan Dürr,1 Nicola Taccardi,2 Ourania-Menti Goudouri,3 Alexander Hoppe,3 Dietmar Eberbeck,4 Dirk W Schubert,5 Aldo R Boccaccini,3 Christoph Alexiou1 1ENT Department, Section of Experimental Oncology and Nanomedicine (SEON, Else Kroener-Fresenius-Stiftung-Professorship, University Hospital Erlangen, 2Chair of Chemical Engineering I (Reaction Engineering, 3Institute of Biomaterials, Department of Materials Science and Engineering, University Erlangen-Nuremberg, Erlangen, 4Physikalisch-Technische Bundesanstalt, Berlin, 5Institute of Polymer Materials, Department of Materials Science and Engineering, University Erlangen-Nuremberg, Erlangen, Germany Abstract: A highly selective and efficient cancer therapy can be achieved using magnetically directed superparamagnetic iron oxide nanoparticles (SPIONs bearing a sufficient amount of the therapeutic agent. In this project, SPIONs with a dextran and cisplatin-bearing hyaluronic acid coating were successfully synthesized as a novel cisplatin drug delivery system. Transmission electron microscopy images as well as X-ray diffraction analysis showed that the individual magnetite particles were around 4.5 nm in size and monocrystalline. The small crystallite sizes led to the superparamagnetic behavior of the particles, which was exemplified in their magnetization curves, acquired using superconducting quantum interference device measurements. Hyaluronic acid was bound to the initially dextran-coated SPIONs by esterification. The resulting amide bond linkage was verified using Fourier transform infrared spectroscopy. The additional polymer layer increased the vehicle size from 22 nm to 56 nm, with a hyaluronic acid to dextran to magnetite weight ratio of 51:29:20. A maximum payload of 330 µg cisplatin/mL nanoparticle suspension was achieved, thus the particle size was further increased to around 77 nm with a zeta

  14. Nano-sensing of the orientation of fluorescing molecules with active coated nano-particles

    DEFF Research Database (Denmark)

    Arslanagic, Samel; Ziolkowski, Richard W.

    2015-01-01

    The potential of using active coated nano-particles to determine the orientation of fluorescing molecules is reported. By treating each fluorescing molecule as an electric Hertzian dipole, single and multiple fluorescing molecules emitting coherently and incoherently in various orientations...... are considered in the presence of active coated nano-particles. It is demonstrated that in addition to offering a means to determine the orientation of a single molecule or the over-all orientation of the molecules surrounding it, the nature of the far-field response from the active coated nano...

  15. Multiple-diffusion flame synthesis of pure anatase and carbon-coated titanium dioxide nanoparticles

    KAUST Repository

    Memon, Nasir

    2013-09-01

    A multi-element diffusion flame burner (MEDB) is useful in the study of flame synthesis of nanomaterials. Here, the growth of pure anatase and carbon-coated titanium dioxide (TiO2) using an MEDB is demonstrated. Hydrogen (H2), oxygen (O2), and argon (Ar) are utilized to establish the flame, whereas titanium tetraisopropoxide is used as the precursor for TiO2. The nanoparticles are characterized using high-resolution transmission electron microscopy, with elemental mapping (of C, O, and Ti), X-ray diffraction, Raman spectroscopy, and thermogravimetric analysis. The growth of pure anatase TiO2 nanoparticles occurs when Ar and H2 are used as the precursor carrier gas, while the growth of carbon-coated nanoparticles ensues when Ar and ethylene (C2H4) are used as the precursor carrier gas. A uniform coating of 3-5nm of carbon is observed around TiO2 particles. The growth of highly crystalline TiO2 nanoparticles is dependent on the gas flow rate of the precursor carrier and amorphous particles are observed at high flow rates. Carbon coating occurs only on crystalline nanoparticles, suggesting a possible growth mechanism of carbon-coated TiO2 nanoparticles. © 2013 The Combustion Institute.

  16. Ionizing radiation effect on central venous catheters (CVC) of polyurethane coatings with silver nanoparticles

    International Nuclear Information System (INIS)

    Heilman, Sonia; Silva, Leonardo G.A.; Hewer, Thiago L.R.; Souza, Michele L.

    2015-01-01

    The present work aimed to study the use of ionizing radiation for coating of silver nanoparticles on central polyurethane catheters, providing reduction of infections associated with contamination of catheters introduced into the bloodstream. Silver nanoparticles have physical, chemical and biological properties only when compared to metal on a macroscopic scale, and have been used in the medical field because of its remarkable antimicrobial activity. Titanium dioxide nanoparticles obtained by the sol gel method were used as the coating catheters for subsequent impregnation of silver nanoparticles with ionizing radiation at doses of 25 and 50 kGy. A Raman spectrometry was used to identify the polymorph of titanium oxide, rutile. In trials with (ICP OES) were evaluated amounts of titanium and silver coated catheters in titanium oxide and silver.(author)

  17. Synchrotron radiation photoelectron spectroscopy study of dextran-coated Fe3O4 magnetic nanoparticles

    International Nuclear Information System (INIS)

    Li Shaoxia; Meng Qiang; Wang Bing; Feng Weiyue; Wang Zhuo; Kui Rexi; Qian Haijie; Wang Jia'o

    2009-01-01

    Dextran-coated Fe 3 O 4 nanoparticles were prepared by untrasonification of Fe 3 O 4 nanoparticles with dextran at 85 degree C in sodium citrate medium. The surface chemical component, structure and bond of uncoated and dextran-coated nanoparticles were measured by synchrotron radiation XPS(X-ray photoelectron spectroscopy). Qualitative and quantitative analysis of C1s and O1s of Fe 3 O 4 and dextran-Fe 3 O 4 showed that the Fe 3 O 4 nanoparticles were successively coated by sodium citrate via Fe-O-C bond, and dextrans, which can be linked with their carboxylate moiety via hydrogen bond. Sodium citrate could enhance the disperse stability of reaction system and hydrophilicity of dextran-Fe 3 O 4 . (authors)

  18. Glucose-coated gold nanoparticles transfer across human brain endothelium and enter astrocytes in vitro.

    Directory of Open Access Journals (Sweden)

    Radka Gromnicova

    Full Text Available The blood-brain barrier prevents the entry of many therapeutic agents into the brain. Various nanocarriers have been developed to help agents to cross this barrier, but they all have limitations, with regard to tissue-selectivity and their ability to cross the endothelium. This study investigated the potential for 4 nm coated gold nanoparticles to act as selective carriers across human brain endothelium and subsequently to enter astrocytes. The transfer rate of glucose-coated gold nanoparticles across primary human brain endothelium was at least three times faster than across non-brain endothelia. Movement of these nanoparticles occurred across the apical and basal plasma membranes via the cytosol with relatively little vesicular or paracellular migration; antibiotics that interfere with vesicular transport did not block migration. The transfer rate was also dependent on the surface coating of the nanoparticle and incubation temperature. Using a novel 3-dimensional co-culture system, which includes primary human astrocytes and a brain endothelial cell line hCMEC/D3, we demonstrated that the glucose-coated nanoparticles traverse the endothelium, move through the extracellular matrix and localize in astrocytes. The movement of the nanoparticles through the matrix was >10 µm/hour and they appeared in the nuclei of the astrocytes in considerable numbers. These nanoparticles have the correct properties for efficient and selective carriers of therapeutic agents across the blood-brain barrier.

  19. Preparation of Rhodamine B Fluorescent Poly(methacrylic acid Coated Gelatin Nanoparticles

    Directory of Open Access Journals (Sweden)

    Zhenhai Gan

    2011-01-01

    Full Text Available Poly(methacrylic acid (PMAA-coated gelatin nanoparticles encapsulated with fluorescent dye rhodamine B were prepared by the coacervation method with the aim to retard the release of rhodamine B from the gelatin matrix. With sodium sulfate as coacervation reagent for gelatin, a kind of biopolymer with excellent biocompatibility, the formed gelatin nanoparticles were cross-linked by formaldehyde followed by the polymerization of methacrylic acid coating. The fluorescent poly(methacrylic acid coated gelatin (FPMAAG nanoparticles had a uniform spherical shape and a size distribution of 60±5 nm. Infrared spectral analysis confirmed the formation of PMAA coating on the gelatin nanoparticles. Based on UV-Vis spectra, the loading efficiency of rhodamine B for the FPMAAG nanoparticles was 0.26 μg per mg nanoparticles. The encapsulated rhodamine B could sustain for two weeks. Favorable fluorescence property and fluorescence imaging of cells confirmed that the FPMAAG nanoparticles have promising biochemical, bioanalytical, and biomedical applications.

  20. Nanoparticle Structures with (Un-)Hydrogenated Castor Oil as Hydrophobic Paper Coating.

    Science.gov (United States)

    Samyn, Pieter; Vonck, Leo; Stanssens, Dirk; Abbeele, Henk Van den

    2018-05-01

    The encapsulation of vegetable oils within an aqueous dispersion of polymer nanoparticles provides an alternative route to create functional paper coatings from renewable resources, by combining the presentation of hydrophobic moieties together with variations in roughness at the paper surface. The effects of two selected vegetable oil types, i.e., castor oil and hydrogenated castor oil (wax), are compared in terms of nanoparticle synthesis, coating hydrophobicity and surface gloss. The nanoparticles were synthesized by adding 50 wt.-% oil during imidization of poly(styrene-co-maleic anhydride) with ammonium hydroxide. From evaluation of the thermal properties, the nanoparticles have a high glass transition temperature that is suppressed in presence of oil. The nanoparticles with hydrogenated castor oil have higher imide content and better thermal stability compared to castor oil, in parallel with lower chemical reactivity of the hydrogenated oil and less interference with the imidization reaction. After deposition as a coating on paper, the physical coating properties are discussed in parallel with the coating chemistry and morphology or roughness at different scale lengths. The nanoparticle coatings with hydrogenated oil provides a multi-scale roughness with an open, porous nanoparticles structures and presentation of some amount free oil augmenting hydrophobicity towards a water contact angle of 128° (static contact angle) or 138° (advancing contact angle). The differences in surface coverage of coated papers in terms of imide and oil contents are confirmed by chemical Raman mapping. The differences in surface roughness are confirmed by non-contact profilometry, laser interferometry and atomic force microscopy.