WorldWideScience

Sample records for cement paste mortar

  1. Chloride ingress in cement paste and mortar

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede; Hansen, Per Freiesleben; Coats, Alison M.

    1999-01-01

    In this paper chloride ingress in cement paste and mortar is followed by electron probe microanalysis. The influence of several paste and exposure parameters on chloride ingress are examined (e.g., water-cement ratio, silica fume addition, exposure time, and temperature), The measurements...

  2. Cement Pastes and Mortars Containing Nitrogen-Doped and Oxygen-Functionalized Multiwalled Carbon Nanotubes

    Directory of Open Access Journals (Sweden)

    Mauricio Martínez-Alanis

    2016-01-01

    Full Text Available Cement pastes and mortars based on ordinary Portland cement containing nitrogen-doped multiwalled carbon nanotubes (MWCNT-Nx or oxygen-functionalized multiwalled carbon nanotubes (MWCNT-Ox are investigated. To incorporate MWCNTs into the cementitious matrix, the as-produced carpets are dispersed over periods of 1 and 2 hours in distilled water at pH levels of 1 and 7. The cement pastes are prepared by adding 0.1 wt% of MWCNTs to cement powder, followed by characterization with SEM and X-ray diffraction (XRD at an early age (first hours of hydration. The mortars are mechanically characterized during the hydration process for a period of 28 days. SEM characterization of cement pastes revealed that the carbon nanotubes are well incorporated in the cementitious matrix, with the hydrated cement grains interconnected by long carbon nanotubes. XRD characterizations demonstrated that, during the hydration of cement pastes, different peaks emerged that were associated with ettringite, hydrated calcium silicate, and calcium hydroxide, among other structures. Results of the compressive strength measurements for mortars simultaneously mixed with MWCNT-Nx and MWCNT-Ox reached an increment of approximately 30% in compressive strength. In addition, density functional theory calculations were performed in nitrogen-doped and oxygen-functionalized carbon nanotubes interacting with a cement grain.

  3. Investigating the Influence of Waste Basalt Powder on Selected Properties of Cement Paste and Mortar

    Science.gov (United States)

    Dobiszewska, Magdalena; Beycioğlu, Ahmet

    2017-10-01

    Concrete is the most widely used man-made construction material in civil engineering applications. The consumption of cement and thus concrete, increases day by day along with the growth of urbanization and industrialization and due to new developments in construction technologies, population growing, increasing of living standard. Concrete production consumes much energy and large amounts of natural resources. It causes environmental, energy and economic losses. The most important material in concrete production is cement. Cement industry contributes to production of about 7% of all CO2 generated in the world. Every ton of cement production releases nearly one ton of CO2 to atmosphere. Thus the concrete and cement industry changes the environment appearance and influences it very much. Therefore, it has become very important for construction industry to focus on minimizing the environmental impact, reducing energy consumption and limiting CO2 emission. The need to meet these challenges has spurred an interest in the development of a blended Portland cement in which the amount of clinker is reduced and partially replaced with mineral additives - supplementary cementitious materials (SCMs). Many researchers have studied the possibility of using another mineral powder in mortar and concrete production. The addition of marble dust, basalt powder, granite or limestone powder positively affects some properties of cement mortar and concrete. This paper presents an experimental study on the properties of cement paste and mortar containing basalt powder. The basalt powder is a waste emerged from the preparation of aggregate used in asphalt mixture production. Previous studies have shown that analysed waste used as a fine aggregate replacement, has a beneficial effect on some properties of mortar and concrete, i.e. compressive strength, flexural strength and freeze resistance also. The present study shows the results of the research concerning the modification of cement

  4. Influence of citric acid as setting retarder in CPV portland cement pastes and mortars

    International Nuclear Information System (INIS)

    Mendes, B.C.; Lopes, M.M.S.; Alvarenga, R.C.S.S.; Fassoni, D.P.; Pedroti, L.G.; Azevedo, A.R.G. de

    2016-01-01

    This work aims to study the availability of using and the influence of citric acid in the properties of pastes and mortars made with Portland cement CPV ARI both in fresh and hardened form. The citric acid dosages were 0, 0.4%, and 0.8% relative to the cement mass. The produced cement pastes were tested to determine normal consistency water and initial and final setting times. Mortars were tested to determine the consistency index, specific gravity, air entrained content in the fresh stage, hardened bulk density, compressive strength at ages 7, 14, and 28 days, and analysis by XRD technique. The results show that citric acid, besides improve the mortar workability, contribute to an increase in mechanical strength in older than 14 days. (author)

  5. Microstructure engineering of Portland cement pastes and mortars through addition of ultrafine layer silicates

    DEFF Research Database (Denmark)

    Lindgreen, Holger; Geiker, Mette; Krøyer, Hanne

    2008-01-01

    Pozzolanic submicron-sized silica fume and the non-pozzolanic micron- and nano-sized layer silicates (clay minerals) kaolinite, smectite and palygorskite have been used as additives in Portland cement pastes and mortars. These layer silicates have different particle shape (needles and plates......), surface charge, and size (micron and nano). The structure of the resulting cement pastes and mortars has been investigated by atomic force microscopy (AFM), helium porosimetry, nitrogen adsorption (specific surface area and porosity), low-temperature calorimetry (LTC) and thermal analysis. The main result...... is that the cement paste structure and porosity can be engineered by addition of selected layer silicates having specific particle shapes and surface properties (e.g., charge and specific surface area). This seems to be due to the growth of calcium-silicate hydrates (C-S-H) on the clay particle surfaces...

  6. The shrinkage of hardening cement paste and mortar

    NARCIS (Netherlands)

    Haas, de G.D.; Kreijger, P.C.; Niël, E.M.M.G.; Slagter, J.C.; Stein, H.N.; Theissing, E.M.; Wallendael, van M.

    1975-01-01

    This paper is an abstract from the report of the commission B10: "The influence of the shrinkage of cement on the shrink-age of concrete", of the Netherlands Committee for Concrete Research. Measurements of pulse velocity, volume shrinkage and heat of hydration on hardening portland cement support

  7. Effects of Blended-Cement Paste Chemical Composition Changes on Some Strength Gains of Blended-Mortars

    Science.gov (United States)

    Kirgiz, Mehmet Serkan

    2014-01-01

    Effects of chemical compositions changes of blended-cement pastes (BCPCCC) on some strength gains of blended cement mortars (BCMSG) were monitored in order to gain a better understanding for developments of hydration and strength of blended cements. Blended cements (BC) were prepared by blending of 5% gypsum and 6%, 20%, 21%, and 35% marble powder (MP) or 6%, 20%, 21%, and 35% brick powder (BP) for CEMI42.5N cement clinker and grinding these portions in ball mill at 30 (min). Pastes and mortars, containing the MP-BC and the BP-BC and the reference cement (RC) and tap water and standard mortar sand, were also mixed and they were cured within water until testing. Experiments included chemical compositions of pastes and compressive strengths (CS) and flexural strengths (FS) of mortars were determined at 7th-day, 28th-day, and 90th-day according to TS EN 196-2 and TS EN 196-1 present standards. Experimental results indicated that ups and downs of silica oxide (SiO2), sodium oxide (Na2O), and alkali at MP-BCPCC and continuously rising movement of silica oxide (SiO2) at BP-BCPCC positively influenced CS and FS of blended cement mortars (BCM) in comparison with reference mortars (RM) at whole cure days as MP up to 6% or BP up to 35% was blended for cement. PMID:24587737

  8. Effects of Blended-Cement Paste Chemical Composition Changes on Some Strength Gains of Blended-Mortars

    Directory of Open Access Journals (Sweden)

    Mehmet Serkan Kirgiz

    2014-01-01

    Full Text Available Effects of chemical compositions changes of blended-cement pastes (BCPCCC on some strength gains of blended cement mortars (BCMSG were monitored in order to gain a better understanding for developments of hydration and strength of blended cements. Blended cements (BC were prepared by blending of 5% gypsum and 6%, 20%, 21%, and 35% marble powder (MP or 6%, 20%, 21%, and 35% brick powder (BP for CEMI42.5N cement clinker and grinding these portions in ball mill at 30 (min. Pastes and mortars, containing the MP-BC and the BP-BC and the reference cement (RC and tap water and standard mortar sand, were also mixed and they were cured within water until testing. Experiments included chemical compositions of pastes and compressive strengths (CS and flexural strengths (FS of mortars were determined at 7th-day, 28th-day, and 90th-day according to TS EN 196-2 and TS EN 196-1 present standards. Experimental results indicated that ups and downs of silica oxide (SiO2, sodium oxide (Na2O, and alkali at MP-BCPCC and continuously rising movement of silica oxide (SiO2 at BP-BCPCC positively influenced CS and FS of blended cement mortars (BCM in comparison with reference mortars (RM at whole cure days as MP up to 6% or BP up to 35% was blended for cement.

  9. Moisture migration and drying properties of hardened cement paste and mortar

    International Nuclear Information System (INIS)

    Numao, T.; Fukuzawa, K.; Mihashi, H.

    1993-01-01

    Moisture content and movement have a significant influence on mechanical properties of concrete. Therefore, many studies have been done on the migration or loss of water in concrete mostly without any external loads. Concrete in actual structures, however, is usually under stresses. As the microstructure of concrete is changed by the load, the observed moisture movement phenomena may be changed. Hence it is necessary to study the moisture migration in concrete under compressive stress in order to estimate rationally the mechanical behavior such as creep and shrinkage in actual concrete structures. In this paper, the influence of compressive stress on moisture migration and water loss of hardened cement paste were studied experimentally and analytically. Furthermore, comparing them with the results of mortar specimens, the influence of containing aggregates was also discussed

  10. Microstructural Properties of Cement Paste and Mortar Modified by Low Cost Nanoplatelets Sourced from Natural Materials

    Directory of Open Access Journals (Sweden)

    Piao Huang

    2018-05-01

    Full Text Available Nanomaterials have been widely used in cement-based materials. Graphene has excellent properties for improving the durability of cement-based materials. Given its high production budget, it has limited its wide potential for application in the field of engineering. Hence, it is very meaningful to obtain low cost nanoplatelets from natural materials that can replace graphene nanoplatelets (GNPs The purpose of this paper is to improve the resistance to chloride ion penetration by optimizing the pore structure of cement-based materials, and another point is to reduce investment costs. The results illustrated that low cost CaCO3 nanoplatelets (CCNPs were successfully obtained under alkali treatment of seashell powder, and the chloride ion permeability of cement-based materials significantly decreased by 15.7% compared to that of the control samples when CCNPs were incorporated. Furthermore, the compressive strength of cement pastes at the age of 28 days increased by 37.9% than that of the plain sample. Improvement of performance of cement-based materials can be partly attributed to the refinement of the pore structure. In addition, AFM was employed to characterize the nanoplatelet thickness of CCNPs and the pore structures of the cement-based composites were analyzed by MIP, respectively. CCNPs composite cement best performance could lay the foundation for further study of the durability of cement-based materials and the application of decontaminated seashells.

  11. Microstructure engineering of Portland cement pastes and mortars through addition of ultrafine layer silicates

    DEFF Research Database (Denmark)

    Lindgreen, Holger; Geiker, Mette Rica; Krøyer, Hanne

    2008-01-01

    , in comparison to the pure cement pasta and the paste containing kaolinite, a more open pore structure consisting of fine pores. Silica fume paste contains a significant amount of closed pores. As a secondary result, it is demonstrated that both the degree and duration of sample drying strongly modifies...

  12. Incorporation mode effect of Nano-silica on the rheological and mechanical properties of cementitious pastes and cement mortars

    Science.gov (United States)

    Safi, B.; Aknouche, H.; Mechakra, H.; Aboutaleb, D.; Bouali, K.

    2018-04-01

    Previous research indicates that the inclusion of nanosilica (NS) modifies the properties of the fresh and hardened state, compared to the traditional mineral additions. NS decreases the setting times of the cement mortar compared to silica fume (SF) and reduce of required water while improving the cohesion of the mixtures in the fresh state. Some authors estimate that the appropriate percentage of Nano-silica should be small (1 to 5% by weight) because of difficulties caused by agglomeration to particles during mixing, while others indicate that 10% by weight, if adjustments are made to the formulation to avoid an excess of self-drying and micro cracks that could impede strength. For this purpose, the present work aim to see the effect of the introduction mode of the nanosilica on the rheological and physic mechanical properties of cement mortars. In this study, NS was used either powdered with cement or in solution with the superplasticizer (Superplasticizer doped in nanosilica). Results show that the use of nanosilica powder (replacing cement on the one hand) has a negative influence on the rheological parameters and the rheological behavior of cementitious pastes. However, the introduction of nanosilica in solution in the superplasticizer (SP) was significantly improved the rheological parameters and the rheological behavior of cementitious pastes. Indeed, more the dosage of NS-doped SP increases more the shear stress and viscosities of the cementitious pastes become more fluid and manageable. A significant reduction of shear stress and plastic viscosity were observed that due to the increase in superplasticizer. A dosage of 1.5% NS-doped SP gave adequate fluidity and the shear rate was lower.

  13. Evaluation of the properties of bitumen and cement pastes and mortars used in the immobilization of waste radioactive

    International Nuclear Information System (INIS)

    Vieira, Vanessa Mota; de Tello, Cledola Cassia Oliveira

    2013-01-01

    The Project RBMN was launched in November 2008 and aims to establish, manage and execute all tasks for implementing the Brazilian Repository, from its conception to its construction. The concept to be adopted will be a near-surface repository. The inventory includes wastes from the operation of nuclear power plants, fuel cycle facilities and from the use of radionuclides in medicine, industry and activities research and development. The implementation of the national repository is an important technical requirement, and a legal requirement for the entry into operation of the nuclear power plant Angra 3. In Brazil, for the immobilization and solidification of radioactive waste of low and intermediate level of radiation from NPPs are used cement, in Angra 1, and bitumen, in Angra 2. Studies indicate serious concerns about the risks associated with bituminization radioactive waste, much related to the process as the product. There are two major problems due to the presence of products bituminization in repositories, swelling of the waste products and their degradation in the long term. To accommodate the swelling, filling the drums must be limited to 70 - 90% of its volume, which reduces the structural stability of the repository and the optimization of deposition. This study aims to evaluate of the properties of bitumen and cement pastes and mortars used in the immobilization of waste radioactive. (author)

  14. Influence of microstructure on the diffusive transport in pastes, mortars and concretes made with cement Portland and silica fume

    International Nuclear Information System (INIS)

    Bajja, Zineb

    2016-01-01

    Thanks to its high mechanical strength and its potential containment capacity conferred by a compact microstructure, concrete is considered as the most suitable material to compose the engineered barrier of some radioactive waste storage structure. Knowledge of diffusion properties and microstructure of these cementitious materials is then essential to study their long-term durability. In a more specific context of low and intermediate waste management, the use of formulations containing silica fume (SF) appears of great importance. The experimental approach consists in selecting many formulations of pastes and mortars to test by the HTO through-out diffusion test. Their initial compositions (water to binder ratio, SF content, sand content and particle size) were varied in order to browse different microstructures and diffusion properties, and to see the influence of each parameter (water, SF, content and grain size of sand) on the evolution of diffusivity within these materials. The microstructure was investigated to interpret the obtained values of diffusion coefficients. Different complementary techniques have been used to characterize the porous structure (water and mercury intrusion porosimetry, nitrogen adsorption), to verify SF reactivity (TGA, SEM associated to EDS) or to determine the profile porosity at ITZ (SEM combined with image analysis).The relationship between microstructure and diffusion coefficients (DeHTO) was then discussed. The ultimate goal was to find a link between microstructure properties and transport parameters to estimate from a simple characterization, the DeHTO of concrete, difficult to get from HTO diffusion cells test. Other attempts have also been made to try to assess the concrete diffusion coefficient, such as the multi-scale modeling approach (the scale of hydrates 3D model), or the diffusion of other elements ( like oxygen or nitrogen). This study shows that silica fume agglomerates (slurry) observed in cement paste and mortar

  15. The effect of pozzolan additions on the shrinkage of cement pastes and mortars during their first hours of age

    Directory of Open Access Journals (Sweden)

    Ossa, M. Mauricio

    1992-03-01

    Full Text Available The traditional favour enjoyed by cement including additions and by their diverse uses in Chile calls for an extense investigation of their behaviour in order that the results may justify their utilization in specific projects. This works studies volume changes occurring in cement pastes and mortars containing pozzolan additions during their first hours of age. This investigation used cements made in the laboratory from raw materials supplied by chilean manufacturers. Two types of clinkers were used, namely; a gypsum type and a natural pozzolan type, added in proportions ranging from 0 to 30%.Tests were conducted to ascertain the shrinkage of cement pastes and mortars since the first moments following their mixing operation, employing there for moulds fitted with a special device designed and implemented at the laboratory of the IDIEM Department of Agglomerants. The results thus gathered corroborated the fact that independently of cement characteristics, in general the deformation of pastes and mortars exhibits successive periods of first shrinkage swelling, and second shrinkage. The first shrinkage is affected by the ambient conditions of humidity, temperature, and wind (evaporation, but also in a preponderant way by cement specific surface, which allows higher velocity in the chemical reactions occurring during that period. Moreover the compactation degree is also affecting shrinkage, here. On the other hand, it was confirmed that with cements of like fineness, those having higher C3A contents exhibit an overall shrinkage larger than that of cements having low contents. At last it was possible to ascertain that an increase in pozzolan contents does not affect shrinkage directly, but that its presence may eventually modify the gypsum/clinker ratio and thus give rise to changes, specially in the two States of swelling and second shrinkage.

    La tradicional aceptación en Chile de los cementos con adición y su diversidad

  16. Nondestructive exploratory tests of corrosion of steels embedded in cement-paste and mortar by the use of γ-ray

    International Nuclear Information System (INIS)

    Sekine, Isao; Yuasa, Makoto; Hotta, Akihiko

    1992-01-01

    Nondestructive exploratory test of corrosion of steels embedded in cement paste and mortar was carried out by the method based on γ-ray back-scattering. The possibility of such test was investigated with the theoretical calculation. From these results of the test, the difference (ΔD) of back-scattering dose rate of corroded and uncorroded specimens of bare-steels or cement paste- and mortar-embedded-steels was found and increased with angle (ω) of Compton scattering. A relationship between ΔD and ω was observed. The relation of ΔD with ω by the test corresponded to that by the theoretical calculation. For the steels embedded in cement paste and mortar, the value of ΔD decreased and became irregular depending upon i) the thickness and component of cover and ii) the shape of steel. The subject in future will be the investigation for a method of the exploratory test by γ-ray back-scattering by consideration of above environmental conditions. (author)

  17. Shrinkage-reducing admixtures and early-age desiccation in cement pastes and mortars

    DEFF Research Database (Denmark)

    Bentz, D. P.; Geiker, Mette Rica; Hansen, Kurt Kielsgaard

    2001-01-01

    Fundamental studies of the early-age desiccation of cement-based materials with and without a shrinkage-reducing admixture (SRA) have been performed. Studies have been conducted under both sealed and drying conditions. Physical measurements include mass loss, surface tension, X-ray absorption to ...... to low w/c ratio concretes undergoing self-desiccation, in addition to their normal usage to reduce drying shrinkage.......Fundamental studies of the early-age desiccation of cement-based materials with and without a shrinkage-reducing admixture (SRA) have been performed. Studies have been conducted under both sealed and drying conditions. Physical measurements include mass loss, surface tension, X-ray absorption...

  18. Cement-latex grouting mortar for cementing boreholes

    Energy Technology Data Exchange (ETDEWEB)

    Kateev, I S; Golyshkina, L A; Gorbunova, I V; Kurochkin, B M; Vakula, Ya V

    1980-01-01

    The need for the development of cement-latex grouting mortar for the purpose of separating strata when reinforcing boreholes at deposits in the Tatar Associated SSR is evaluated. Results of studies of the physical and mechanical properties of cement-latex grouting mortar systems (mortar plus brick) are presented. Formulas for preparing cement-latex grouting mortor are evaluated and results of industrial tests of such mortars shown.

  19. The effect of bond characteristics between steel slag fine aggregate and cement paste on mechanical properties of concrete and mortar

    International Nuclear Information System (INIS)

    Yuji, W.

    1988-01-01

    The ordinary fine aggregate in concrete has been replaced by ground and sieved steel slag fine aggregate, treated and exposed to air for three months. Compared with concrete made from natural sand, properties such as compressive strength, flexural strength, elastic modules, permeability and abrasion resistance are considerably improved. The improvement increases with a decrease in w/c ratio, an increase in curing time and an increase in the replacement weight of sand. These results are due to the fact that the steel slag contains some active minerals such as C/sub 3/S, C/sub 2/S, C/sub 4/AF, etc., and shows favorable surface physical characteristics that improve the bond between steel slag particles and cement paste. The results of XRD, SEM and EPM microhardness showed that there are heavier concentration of ions, with finer crystals and a lower degree of CH orientation at the interfacial zone between steel slag particles and cement paste. The study also found small cementitious and fibrous C-S-H crystals growing from the fine aggregate, which are linked with hydrated products form cement paste making the bond and structural characteristic more favorable with cement. The steel slag fine aggregate is an active mineral similar to cement. The bond between the aggregate and cement paste is strengthened both physically and chemically

  20. Hospital waste ashes in Portland cement mortars

    International Nuclear Information System (INIS)

    Genazzini, C.; Zerbino, R.; Ronco, A.; Batic, O.; Giaccio, G.

    2003-01-01

    Nowadays, most concretes incorporate mineral additions such as pozzolans, fly ash, silica fume, blast furnace slag, and calcareous filler among others. Although the technological and economical benefits were the main reasons for the use of mineral additions, the prevention of environmental contamination by means of proper waste disposal becomes a priority. The chance of incorporating hospital waste ashes in Portland cement-based materials is presented here. Ash characterization was performed by chemical analysis, X-ray diffraction, radioactive material detection, and fineness and density tests. Conduction calorimetry and setting time tests were developed on pastes including ash contents from 0% to 100%. Mortars were prepared including ash contents up to 50% of cement. The results of setting time, temperature development, flexural and compressive strengths, water absorption, density, and leachability are analyzed. Results indicate that Portland cement systems could become an alternative for the disposal of this type of ashes

  1. Influence of citric acid as setting retarder in CPV portland cement pastes and mortars; Influencia do acido citrico como retardador de pega em pastas e argamassas de cimento portland CPV ARI

    Energy Technology Data Exchange (ETDEWEB)

    Mendes, B.C.; Lopes, M.M.S.; Alvarenga, R.C.S.S.; Fassoni, D.P.; Pedroti, L.G. [Universidade Federal de Vicosa (UFV), MG (Brazil); Azevedo, A.R.G. de, E-mail: afonso.garcez91@gmail.com [Universidade Estadual do Norte Fluminense Darcy Ribeiro (UENF), Campos dos Goytacazes, RJ (Brazil)

    2016-07-01

    This work aims to study the availability of using and the influence of citric acid in the properties of pastes and mortars made with Portland cement CPV ARI both in fresh and hardened form. The citric acid dosages were 0, 0.4%, and 0.8% relative to the cement mass. The produced cement pastes were tested to determine normal consistency water and initial and final setting times. Mortars were tested to determine the consistency index, specific gravity, air entrained content in the fresh stage, hardened bulk density, compressive strength at ages 7, 14, and 28 days, and analysis by XRD technique. The results show that citric acid, besides improve the mortar workability, contribute to an increase in mechanical strength in older than 14 days. (author)

  2. Mechanical characterization of sisal reinforced cement mortar

    OpenAIRE

    R. Fujiyama; F. Darwish; M.V. Pereira

    2014-01-01

    This work aims at evaluating the mechanical behavior of sisal fiber reinforced cement mortar. The composite material was produced from a mixture of sand, cement, and water. Sisal fibers were added to the mixture in different lengths. Mechanical characterization of both the composite and the plain mortar was carried out using three point bend, compression, and impact tests. Specimens containing notches of different root radii were loaded in three point bending in an effort to determine the eff...

  3. Preliminary investigation of the effect of air-pollution-control residue from waste incineration on the properties of cement paste and mortar

    DEFF Research Database (Denmark)

    Geiker, Mette Rica; Kjeldsen, Ane Mette; Galluci, Emmanuel

    2006-01-01

    For preliminary assessment of the engineering properties of concrete with air-pollution-control residue from waste incineration (APC) the possible reactivity of APC and the effect of APC on cement hydration were investigated by isothermal calorimetry, chemical shrinkage (pychnometry), thermal...... analysis (TG), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Furthermore, compressive strength development was measured and impregnated plane sections were prepared. The APC was from a Danish wet process plant. Although the APC contained high amounts of chloride (approx. 10%) and heavy......% and 20% APC showed a major retarding effect of APC on the development of hydration. The APC was found to be pozzolanic. Chemical shrinkage measurements indicated early expansive reactions of pastes with the APC including evolution of air. Crack formation was observed in mortars with APC, and strength...

  4. Mechanical characterization of sisal reinforced cement mortar

    Directory of Open Access Journals (Sweden)

    R. Fujiyama

    2014-01-01

    Full Text Available This work aims at evaluating the mechanical behavior of sisal fiber reinforced cement mortar. The composite material was produced from a mixture of sand, cement, and water. Sisal fibers were added to the mixture in different lengths. Mechanical characterization of both the composite and the plain mortar was carried out using three point bend, compression, and impact tests. Specimens containing notches of different root radii were loaded in three point bending in an effort to determine the effect of the fibers on the fracture toughness of the material. The results obtained indicate that, while fiber reinforcement leads to a decrease in compressive strength, J-integral calculations at maximum load for the different notch root radii have indicated, particularly for the case of long fibers, a significant superiority of the reinforced material in comparison with the plain cement mortar, in consistence with the impact test data.

  5. Strength and Drying Shrinkage of Alkali-Activated Slag Paste and Mortar

    Directory of Open Access Journals (Sweden)

    Mao-chieh Chi

    2012-01-01

    Full Text Available The aim of this study is to investigate the strengths and drying shrinkage of alkali-activated slag paste and mortar. Compressive strength, tensile strength, and drying shrinkage of alkali-activated slag paste and mortar were measured with various liquid/slag ratios, sand/slag ratios, curing ages, and curing temperatures. Experimental results show that the higher compressive strength and tensile strength have been observed in the higher curing temperature. At the age of 56 days, AAS mortars show higher compressive strength than Portland cement mortars and AAS mortars with liquid/slag ratio of 0.54 have the highest tensile strength in all AAS mortars. In addition, AAS pastes of the drying shrinkage are higher than AAS mortars. Meanwhile, higher drying shrinkage was observed in AAS mortars than that observed comparable Portland cement mortars.

  6. Studies on diffusion of 137Cs in cement mortar

    International Nuclear Information System (INIS)

    Takebe, Shinichi; Shimooka, Kenji; Wadachi, Yoshiki; Kuramoto, Yuzuru.

    1989-12-01

    Penetration experiment of 137 Cs into the impermeable cement mortar which has been treated by the impermeable reagent (XYPEX reagent) was carried out in order to advance the performance of engineered barrier for Low Level Radioactive Waste. The result showed that the radioactive concentration at deeper region in the impermeable cement mortar specimen was decreased about 1 order of magnitude below that in the untreated specimen. Diffusion coefficient calculated from the radioactive concentration of 137 Cs in the cement mortar specimen was 9.1 x 10 -5 cm 2 /day for untreated cement mortar specimen and 4.0 x 10 -5 cm 2 /day for the impermeable cement mortar specimen, respectively. Treatment of cement mortar by the impermeable reagent was found to be effective to reduce the value of appearent diffusion coefficient for 137 Cs in the cement mortar. (author)

  7. Compressive and flexural strength of cement mortar stabilized with ...

    African Journals Online (AJOL)

    Mortar is a material with wide range of applications in the construction industry. However, plain mortar matrices are usually brittle and often cracks and fails more suddenly than reinforced mortars. In this study, the compressive and flexural strengths of cement mortar stabilized with Raffia Palm Fruit Peel (RPFP) as fibre were ...

  8. Experimental Investigation of Multi-mode Fiber Laser Cutting of Cement Mortar

    Science.gov (United States)

    2018-01-01

    This study successfully applied multi-mode laser cutting with the variation of the laser cutting speed to cement mortar for the first time. The effects of the amount of silica sand in the cement mortar on laser cutting are tested and analyzed. The kerf width and penetration depth of the specimens after laser cutting are investigated. As the laser cutting speed increases, the penetration depth decreases for both cement paste and cement mortar, whereas the kerf width becomes saturated and increases, respectively, for cement paste and cement mortar. Cross sections of the specimens are compared with illustrations. Top-view images of the cement mortar with indicators of the physical characteristics, such as re-solidification, burning, and cracks are examined, and the possible causes of these characteristics are explained. The optical absorption rates of cement-based materials are quantified at wide ranges of wavelength to compare the absorption rates in accordance with the materials compositions. The chemical composition variation before and after laser cutting is also compared by EDX (Energy Dispersive X-Ray) analysis. In addition to these observations, material removal mechanisms for cement mortar are proposed. PMID:29439431

  9. Experimental Investigation of Multi-mode Fiber Laser Cutting of Cement Mortar.

    Science.gov (United States)

    Lee, Dongkyoung; Pyo, Sukhoon

    2018-02-10

    This study successfully applied multi-mode laser cutting with the variation of the laser cutting speed to cement mortar for the first time. The effects of the amount of silica sand in the cement mortar on laser cutting are tested and analyzed. The kerf width and penetration depth of the specimens after laser cutting are investigated. As the laser cutting speed increases, the penetration depth decreases for both cement paste and cement mortar, whereas the kerf width becomes saturated and increases, respectively, for cement paste and cement mortar. Cross sections of the specimens are compared with illustrations. Top-view images of the cement mortar with indicators of the physical characteristics, such as re-solidification, burning, and cracks are examined, and the possible causes of these characteristics are explained. The optical absorption rates of cement-based materials are quantified at wide ranges of wavelength to compare the absorption rates in accordance with the materials compositions. The chemical composition variation before and after laser cutting is also compared by EDX (Energy Dispersive X-Ray) analysis. In addition to these observations, material removal mechanisms for cement mortar are proposed.

  10. Sulfate resistance of nanosilica contained Portland cement mortars

    Science.gov (United States)

    Batilov, Iani B.

    Soils, sea water and ground water high in sulfates are commonly encountered hostile environments that can attack the structure of concrete via chemical and physical mechanisms which can lead to costly repairs or replacement. Sulfate attack is a slow acting deteriorative phenomenon that can result in cracking, spalling, expansion, increased permeability, paste-to-aggregate bond loss, paste softening, strength loss, and ultimately, progressive failure of concrete. In the presented research study, Portland cement (PC) mortars containing 1.5% to 6.0% nanosilica (nS) cement replacement by weight were tested for sulfate resistance through full submersion in sodium sulfate to simulate external sulfate attack. Mortars with comparable levels of cement replacement were also prepared with microsilica (mS). Three cement types were chosen to explore nS' effectiveness to reduce sulfate expansion, when paired with cements of varying tricalcium aluminate (C3A) content and Blaine fineness, and compare it to that of mS. Mortars were also made with combined cement replacement of equal parts nS and mS to identify if they were mutually compatible and beneficial towards sulfate resistance. Besides sulfate attack expansion of mortar bars, the testing program included investigations into transport and microstructure properties via water absorption, sulfate ion permeability, porosimetry, SEM with EDS, laser diffraction, compressive strength, and heat of hydration. Expansion measurements indicated that mS replacement mortars outperformed both powder form nS, and nS/mS combined replacement mixtures. A negative effect of the dry nS powder replacement attributed to agglomeration of its nanoparticles during mixing negated the expected superior filler, paste densification, and pozzolanic activity of the nanomaterial. Agglomerated nS was identified as the root cause behind poor performance of nS in comparison to mS for all cement types, and the control when paired with a low C3A sulfate resistant

  11. Physico Mechanical Properties of Irradiated Waste Rubber Cement Mortar

    International Nuclear Information System (INIS)

    Younes, M.M.

    2010-01-01

    In the present study a partial replacement of aggregate with two different ratios of waste rubber (5%, 10%) with the addition of a constant ratio of rice husk ash (RHA), 5% was carried out. The hardened cement mortar used the optimum water of consistency. The specimens were molded into 1 inch cubic moulds .The specimens were first cured for 24 hours, at 100% relative humidity and then cured under tap water for 3, 7 and 28 days followed by irradiation at different doses of gamma irradiation namely 5 and 10 kGy. The physico-chemical and mechanical properties such as compressive strength, total porosity and bulk density were studied for the three types of specimens. The results showed that the values of the compressive strength, bulk density and chemically combined water of the blended cement mortar paste (OPC-RHA) increase ,while blended cement mortar paste with 5% RHA and 5, 10% waste rubber decrease. The results were confirmed by scanning electron microscopy and thermal behavior of the specimens. Also, it was observed that the irradiated sample was thermally more stable than the unirradiated one

  12. Radiation chemical treatment of cement mortar - polymer composites

    International Nuclear Information System (INIS)

    Younes, M.M.

    1994-01-01

    The development of the hardened cement pastes,mortars and concretes which contain polymers has progressed rapidly in years. Developmental work has identified a number of applications where the high strength and excellent durability of the composite materials will provide definite advantages over conventional mortars and concretes. The first investigations of polymer - impregnated concrete tried mainly to increase the quantity of absorbed and polymerised monomer because this gave a greater decrease in the original of concrete and a subsequent improvement in physico - mechanical properties. However, the production costs which is due mainly to the organic polymer, becomes the most important item. In this respect recent research showed the possibility of obtaining with a very compact concrete, of relative low porosity, a compound material with high performances after impregnation 26 tabs.,28 figs.,109 refs

  13. The effect of two types of modified Mg-Al hydrotalcites on reinforcement corrosion in cement mortar

    NARCIS (Netherlands)

    Yang, Z.; Polder, R.; Mol, J.M.C.; Andrade, C.

    2017-01-01

    Two modified Mg-Al hydrotalcites (MHTs), (MHT-pAB and MHT-NO2) were incorporated into mortar (with different w/c ratios) in two different ways: (1) as one of the mixing components in bulk mortar; (2) as part of cement paste coating of the reinforcing steel. Accelerated chloride migration, cyclic

  14. Effect of brief heat-curing on microstructure and mechanical properties in fresh cement based mortars

    International Nuclear Information System (INIS)

    Ballester, P.; Hidalgo, A.; Marmol, I.; Morales, J.; Sanchez, L.

    2009-01-01

    The effect of temperature on fresh mortar and cement paste was evaluated by simulating the curing conditions of external buildings plastering applied under extremely hot weather. The specimens were heated at controlled temperatures in the 40-80 o C range by exposure to IR radiation over short periods. The effect of soaking for a short time was also examined. The results of compressive strength tests, scanning electron microscopy, infrared spectroscopy and mercury porosimetry helped to characterize the mechanical and physico-chemical properties of the studied sample. Early age behaviour (28 days) in neat cement was barely affected by the temperature. By contrast, exposure to high temperatures caused significant microstructural changes in the mortar. However, successive soaking over short periods was found to reactivate the mechanism of curing and restore the expected mechanical properties. Based on the results, application of cement based mortar at high temperatures is effective when followed by a short, specific soaking process.

  15. Use of red mud as addition for portland cement mortars

    International Nuclear Information System (INIS)

    Ribeiro, D.V.; Morelli, M.R.

    2011-01-01

    The aim of the present research work was to investigate the possibility of adding red mud, an alkaline leaching waste that is obtained from bauxite during the Bayer process for alumina production, in the raw meal of Portland cement mortars. The red mud is classified as dangerous, according to NBR 10004/2004, and world while generation reached over 117 million tons/year. This huge production requires high consuming products to be used as incorporation matrix and we studied the influence of red mud addition on the characteristics of cement mortars and concrete. In this paper the properties of Portland cement mortars incorporating high amounts of red mud was evaluated: pH variation, fresh (setting time, workability or normal consistency and water retention), and hardened state (mechanical strength, capillary water absorption, density and apparent porosity). Results seem promising for red mud additions up to 20 wt%. (author)

  16. Determination of the chloride diffusion coefficient in blended cement mortars

    NARCIS (Netherlands)

    Elfmarkova, V.; Spiesz, P.R.; Brouwers, H.J.H.; Bilek, V.; Kersner, Z.

    2014-01-01

    Literature shows that the RCM test development and experience concerns only Ordinary Portland cement. Therefore, a validation of this test method is needed for other types of binders. This study analyzes the application of RCM test for mortars prepared with different binders: Ordinary Portland

  17. Effect of Gum Arabic Karroo as a water-reducing admixture in cement mortar

    Directory of Open Access Journals (Sweden)

    Rose Mbugua

    2016-12-01

    Full Text Available The aim of this study was to develop Gum Acacia Karroo (GAK as set retarding-water reducing admixture in cement mortars. Retarding admixtures are used to counter effect the accelerated hydration of cement at elevated temperatures by slowing down the retarding process especially during the day when concreting work is done. However most retarding admixtures available in the market are expensive, thereby making them out of reach for small consumers of concrete in Africa are expensive and not readily available. GAK, which contains soluble sugars, was investigated as a set-retarding water reducing-admixture. Setting time was measured in cement pastes with different dosages of GAK and a commercial retarding agent (Tard CE. Compressive strength, bleeding and flow test were investigated on cement mortars with the control being cement mortar without admixture. GAK was found to increase final setting time by 6 h above control. Compressive strength increased when water cement ratio was reduced from 0.5 to 0.4. Thermogravimetric analysis revealed increased dosage of GAK reduced hydration rate.

  18. Adsorption of cesium on cement mortar from aqueous solutions

    Energy Technology Data Exchange (ETDEWEB)

    Volchek, Konstantin, E-mail: konstantin.volchek@ec.gc.ca [Emergencies Science and Technology Section, Environment Canada, 335 River Road, Ottawa, Ontario, Canada K1A 0H3 (Canada); Miah, Muhammed Yusuf [Emergencies Science and Technology Section, Environment Canada, 335 River Road, Ottawa, Ontario, Canada K1A 0H3 (Canada); Department of Applied Chemistry and Chemical Technology, Noakhali Science and Technology University (Bangladesh); Kuang, Wenxing; DeMaleki, Zack [Emergencies Science and Technology Section, Environment Canada, 335 River Road, Ottawa, Ontario, Canada K1A 0H3 (Canada); Tezel, F. Handan [Department of Chemical and Biological Engineering, University of Ottawa, 161 Louis-Pasteur, Ottawa, Ontario, Canada K1N 6N5 (Canada)

    2011-10-30

    Highlights: {yields} The adsorption of cesium on cement mortar was investigated in a range of temperatures and cesium concentrations. {yields} The pseudo-second order kinetic model produced a good fit with the experimental kinetic data. {yields} Equilibrium test results correlated well with the Freundlich isotherm adsorption model. {yields} The interaction between cesium ions and cement mortar was dominated by chemical adsorption. - Abstract: The adsorption of cesium on cement mortar from aqueous solutions was studied in series of bench-scale tests. The effects of cesium concentration, temperature and contact time on process kinetics and equilibrium were evaluated. Experiments were carried out in a range of initial cesium concentrations from 0.0103 to 10.88 mg L{sup -1} and temperatures from 278 to 313 K using coupons of cement mortar immersed in the solutions. Non-radioactive cesium chloride was used as a surrogate of the radioactive {sup 137}Cs. Solution samples were taken after set periods of time and analyzed by inductively coupled plasma mass spectroscopy. Depending on the initial cesium concentration, its equilibrium concentration in solution ranged from 0.0069 to 8.837 mg L{sup -1} while the respective surface concentration on coupons varied from 0.0395 to 22.34 {mu}g cm{sup -2}. Equilibrium test results correlated well with the Freundlich isotherm model for the entire test duration. Test results revealed that an increase in temperature resulted in an increase in adsorption rate and a decrease in equilibrium cesium surface concentration. Among several kinetic models considered, the pseudo-second order reaction model was found to be the best to describe the kinetic test results in the studied range of concentrations. The adsorption activation energy determined from Arrhenius equation was found to be approximately 55.9 kJ mol{sup -1} suggesting that chemisorption was the prevalent mechanism of interaction between cesium ions and cement mortar.

  19. 3D Simulation of micromechanical behavior of cement paste

    NARCIS (Netherlands)

    Qian, Z.; Ye, G.; Schlangen, H.E.J.G.; Van Breugel, K.

    2010-01-01

    Numerical modeling of fracture processes of brittle materials, such as cement paste, mortar, concrete and rocks, started in the late 1960s when the discrete and smeared cracking models were introduced. In the 1990s, Schlangen and van Mier proposed another numerical model to compensate the drawbacks

  20. MODIFICATION OF FOAMED CEMENT-CLAY MORTARS BY STABILIZERS

    Directory of Open Access Journals (Sweden)

    Panfilova Marina Ivanovna

    2012-10-01

    by-product generated in the course of combustion of crossties, and reduction of the cement consumption rate. The authors have identified that ash added into the injection does not cause any deterioration of the mortar strength; rather, it assures its structural stability and prevents any leaching of heavy metals that it contains. The authors have identified that adding 20 to 26 % of flue ash into the injection reduces the mortar hardening time by 30 %, while the strength of the mortar that has 20 % of ash is almost equal to the one of the benchmark sample. However, any higher ash content causes deterioration of the hardening strength of the mortar. Therefore, the authors have discovered that 20 % of the cement may be replaced by the ash generated in the course of combustion of waste crossties. This replacement is to be performed in the course of preparation of mortars, and it is aimed at the strengthening of the soil. This operation is to be performed in the incinerator to preserve the solution properties. This technology reduces the amount of hazardous by-products through their recycling.

  1. Optimization of superplasticizer in portland pozzolana cement mortar and concrete

    Science.gov (United States)

    Sathyan, Dhanya; Anand, K. B.; Mini, K. M.; Aparna, S.

    2018-02-01

    Chemical Admixtures are added to concrete at the time of mixing of its constituents to impart workability. The requirement of right workability is the essence of good concrete. It has been found that the use of optimum use of admixtures is very important since low dosage may result in loss of fluidity and over dosage could lead to segregation, bleeding, excessive air entrainment etc in concrete. Hence it is essential to find optimum dosage of superplasticizer for getting good strength and workability. But large number of trial tests are required in the field to find the saturation dosage of superplasticizer in concrete which requires more materials and consume more time. The paper deals with developing a co-relation between the quantity requirements of superplasticiser in mortar to that of cement concrete to get good workability. In this work for preparing mortar and concrete 4 brands of locally available Portland pozzolana cement (PPC) and superplasticizer (SP) belonging to 4 different families namely Polycarboxylate Ether (PCE), Lignosulphate (LS), Sulfonated Naphthalene Formaldehyde (SNF) and Sulfonated Melamine Formaldehyde (SMF) are used. Two different brands of SP’s are taken from each family. Workability study on the superplasticized mortar with cement to sand ratio 1:1.5 and water cement ratio of 0.4 was performed using marsh cone and flow table test and workability study on the concrete with same cement/sand ratio and water cement ratio was done using slump cone and flow table test. Saturation dosage of superplasticizer in mortar and concrete determined experimentally was compared to study the correlation between two. Compressive strength study on concrete cubes were done on concrete mixes with a superplasticizer dosage corresponding to the saturation dosage and a comparative study were done to analyse the improvement in the compressive strength with addition of superplasticizer from different family.

  2. Compressive Strength and Physical Properties Behavior of Cement Mortars with addition of Cement Klin Dust

    Directory of Open Access Journals (Sweden)

    Auday A Mehatlaf

    2017-12-01

    Full Text Available Cement Klin Dust (CKD was the waste of almost cement industry factories, so that in this paper utilization of CKD as filler in cement and/or concrete was the main objective. CKD from the Karbala cement factory had been used and analysis to know the chemical composition of the oxides was done. In this paper cement mortars with different weight percentages of CKD (0,5,10,20,30,40 had been prepared. Physical properties such as density and porosity were done in different age curing (3, 7, 28 day. In addition, mechanical properties included the coefficient of thermal conductivity and compressive strength had also observed with different age (3,7, and 28 for all prepared specimens. From the obtained the experimental results and their discussion, it was clear that the addition (20% of CKD had the good results in cement mortars.  

  3. Compressive Strength and Physical Properties Behavior of Cement Mortars with addition of Cement Klin Dust

    OpenAIRE

    Auday A Mehatlaf

    2017-01-01

    Cement Klin Dust (CKD) was the waste of almost cement industry factories, so that in this paper utilization of CKD as filler in cement and/or concrete was the main objective. CKD from the Karbala cement factory had been used and analysis to know the chemical composition of the oxides was done. In this paper cement mortars with different weight percentages of CKD (0,5,10,20,30,40) had been prepared. Physical properties such as density and porosity were done in different age curing (3, 7, 28) d...

  4. Experimental study of chloride diffusivity in unsaturated ordinary Portland cement mortar

    NARCIS (Netherlands)

    Zhang, Y.; Ye, G.; Santhanam, M.

    2017-01-01

    Experiments are carried out to investigate the chloride diffusivity in partially saturated ordinary Portland cement mortars with water-to-cement (w/c) ratios of 0.4, 0.5 and 0.6. Based on resistivity measurement and Nernst-Einstein equation, the chloride diffusivities of cement mortars at various

  5. Characteristic of Polymer-Impregnated Cement Mortar: Composites: Bulk Density and Microstructure

    International Nuclear Information System (INIS)

    Younes, M.M.; Abo-El-Enein, S.A.; El-Saft, M.M.; Sadek, M.A.; Zohdy, K.M.

    2010-01-01

    The effect of radiation initiated polymerization of some monomers on the physical properties of polymer-incorporated mortar was studied. The monomers used were: castor oil (C.O.), 4, 4'-diphenylmethane diisocyanate (MDI) and methyl methacrylate (MMA). Polymerization was carried out by subjecting the monomer-impregnated mortar specimens to different doses of gamma radiation. Where polyurethane (pu) and polyurethane -methyl methacrylate copolymers were formed within the pore system. The influence of polymer impregnation on the various physico-mechanical characteristics of the resulting composites was studied with respect to bulk density and polymer loading. Scanning electron microscopy (SEM) was employed to study the micro-structural characteristics of the neat hardened Ordinary Portland Cement (OPC) mortar pastes and their polymer-impregnated composites

  6. Acidic Attack Resistance of Cement Mortar Treated with Alkaline

    Directory of Open Access Journals (Sweden)

    Nadia Nazhat Sabeeh

    2017-12-01

    Full Text Available The negative effect of acidic attack on the properties of concrete and cement mortar is a topic of increasing significance in the recent years. Many attempts has occurred to mitigate this negative impact by improving the properties of concrete and increase resistance to acids by using additives. The present study includes treatment of sand by alkaline material and examine the effect of treatment on cement mortar resistance towards hydrochloric and sulfuric acid. Results show that sand treatment by alkaline material significantly enhance mortar ability to resist acids. In terms of loss weight, the maximum weight rate gain was 25.54% for specimens immersed in Hydrochloric acid with water cement ratio 40%. For specimens immersed in HCl, the average gain in compressive strength is (20.15-19.433% for w/c (40-45% respectively. The average gain in modulus of rupture toward the influence of H2SO4 is (18.37–17.99% for w/c (40-45%, respectively.

  7. Protection of Steel Rebar in Salt-Contaminated Cement Mortar Using Epoxy Nanocomposite Coatings

    Directory of Open Access Journals (Sweden)

    The Huu Nguyen

    2018-01-01

    Full Text Available Epoxy reinforced with two kinds of nanoparticles dealing with nano-SiO2 and nano-Fe2O3 was coated on steel rebar embedded in a chloride contaminated cement mortar. NaCl was added to the fresh Portland cement paste (at 0.3% and 0.5% by weight of cement to simulate the chloride contamination at the critical level. The effect of incorporating nanoparticles on the corrosion resistance of epoxy-coated steel rebar was investigated by linear potentiodynamic polarization and electrochemical impedance spectroscopy. For the 0.3 wt.% chloride mortars, the electrochemical monitoring of the coated steel rebars during immersion for 56 days in 0.1 M NaOH solutions suggested the beneficial role of nano-Fe2O3 particles in significantly improving the corrosion resistance of the epoxy-coated rebar. After 56 days of immersion, the nano-Fe2O3 reduced the corrosion current of epoxy-coated rebar by a factor of 7.9. When the chloride concentration in the cement mortar was 0.5 wt.%, the incorporation of nanoparticles into the epoxy matrix did not enhance the corrosion resistance of epoxy coating for the rebar. At this critical level, chloride ions initiated rebar corrosion through nanoparticles at the epoxy/rebar interface.

  8. Effect of olive waste (Husk on behavior of cement paste

    Directory of Open Access Journals (Sweden)

    Sharaf Alkheder

    2016-12-01

    Full Text Available Jordan is a famous country in terms of olive trees agriculture that resulted in a mass production of olive oil products. The huge amounts of olive waste (husk that resulted from olives processing to produce olive oil represent an environmental challenge in the country. The idea in this paper comes to use olive waste as a partial replacement for Portland cement in cement paste to conserve the environment, reduce cement consumption and increase cost efficiency. The wastes were burned properly in an oven and maintained for 6 h until it was fully transformed into ashes. Then, the oven was turned off and ashes were allowed to cool. After cooling, the material passed sieve #200 were used. The sieved ashes were used in the cement mix as a partial cement replacement for making the mortar and cement paste. Normal consistency and setting time were determined as well as soundness, compressive strength. Results indicated that normal consistency of the cement pastes containing different percentage of olive waste is somehow lower than that of the ordinary cement paste and slightly decreases with increasing the percentage. The results also indicated that the compressive strength of hardened blended cement paste containing different percentages of olive waste slightly decrease with olive waste content at 3, 7, and 28 days.

  9. Assessment of Pb-slag, MSWI bottom ash and boiler and fly ash for using as a fine aggregate in cement mortar.

    Science.gov (United States)

    Saikia, Nabajyoti; Cornelis, Geert; Mertens, Gilles; Elsen, Jan; Van Balen, Koenraad; Van Gerven, Tom; Vandecasteele, Carlo

    2008-06-15

    Three types of wastes, metallurgical slag from Pb production (SLG), the sand-sized (0.1-2 mm) fraction of MSWI bottom ash from a grate furnace (SF), and boiler and fly ash from a fluidised bed incinerator (BFA), were characterized and used to replace the fine aggregate during preparation of cement mortar. The chemical and mineralogical behaviour of these wastes along with the reactivities of the wastes with lime and the hydration behaviour of ordinary Portland cement paste with and without these wastes added were evaluated by various chemical and instrumental techniques. The compressive strengths of the cement mortars containing waste as a partial substitution of fine aggregates were also assessed. Finally, leaching studies of the wastes and waste containing cement mortars were conducted. SLG addition does not show any adverse affect during the hydration of cement, or on the compressive strengths behaviours of mortars. Formation of expansive products like ettringite, aluminium hydroxide and H2 gas due to the reaction of some constituents of BFA and SF with alkali creates some cracks in the paste as well as in the cement mortars, which lower the compressive strength of the cement mortars. However, utilization of all materials in cement-based application significantly improves the leaching behaviour of the majority of the toxic elements compared to the waste as such.

  10. The long term effect on cement mortar by admixture of spray drying absorption products

    International Nuclear Information System (INIS)

    Jeppesen, K.G.

    1988-01-01

    Preliminary investigations have shown that the substitutions of up to 10% fly ash (FA), with spray drying absorption products (SDA), in cement mortars (cement: 80% rapid portland cement (RPC), 10-20% FA, 0-10% SDA) results in low early strength of the same magnitude as in mortar with 80% RPC + 20% FA. Use of the modified instructions for preparation of mortar prisms containing SDA resulted in satisfactory early strengths. A series of mortar prisms with increasing content of SDA (x% RPC, (100-x)% SDA in cements; 0 80% cannot be stored wet. The effects on mortars of the individual constituents of the SDA-products are studied by XRD, development in strength and density. Fragments of 2 year old SDA containing cement mortars and SDA containing concrete from a parking place have been studied

  11. Chemical composition influence of cement based mortars on algal biofouling

    Science.gov (United States)

    Estelle, Dalod; Alexandre, Govin; Philippe, Grosseau; Christine, Lors; René, Guyonnet; Denis, Damidot

    2013-04-01

    The main cause of building-facade biodegradation is the growth of microorganisms. This phenomenon depends on several parameters such as the geographical situation, the environmental conditions and the surface state of the substrate. Several researches have been devoted to the study of the effect of porosity and roughness on the biofouling of stones and mortars. However, none of them have addressed the influence of the mortar chemistry on the microorganism growth kinetic. The main objective of this study is to highlight the influence of the mortar chemistry in relationship with its physical properties on biological weathering. Earlier work showed a good resistance of Calcium Aluminate Cements to biodeterioration by acidogenic bacteria (Thiobacillus) and fungi (Alternaria alternata, Aspergillus Niger and Coniosporium uncinatum). In order to characterize the influence of the mortar chemistry on biofouling, two Portland cements and two alumina cements are used. Among micro-organisms able to grow, green algae are most involved in the aesthetic deterioration of facades. Indeed, they can colonize any type of media and can be a source of nutrients for other micro-organisms such as fungi. The green algae Klebsormidium flaccidum is chosen because of its representativeness. It is indeed the species the most frequently identified and isolated from samples taken on sites. The biofouling kinetic is followed on samples exposed outdoor and on samples tested in a laboratory bench which consists in spraying an algae culture on mortar specimens. The results obtained by in situ trials are compared with the results obtained on the laboratory bench. The microorganism growth kinetic is measured by image analysis. To improve the detection of algae on the surface of the cementitious samples, the raw image is converted in the YIQ color space. Y, I and Q correspond respectively to luminance, in-phase, and quadrature. On the Q channel, the areas covered by algae and the areas of clean mortar

  12. Comparative study on strength properties of cement mortar by partial replacement of cement with ceramic powder and silica fume

    Science.gov (United States)

    Himabindu, Ch.; Geethasri, Ch.; Hari, N.

    2018-05-01

    Cement mortar is a mixture of cement and sand. Usage of high amount of cement increases the consumption of natural resources and electric power. To overcome this problem we need to replace cement with some other material. Cement is replaced with many other materials like ceramic powder, silica fume, fly ash, granulated blast furnace slag, metakaolin etc.. In this research cement is replaced with ceramic powder and silica fume. Different combinations of ceramic powder and silica fume in cement were replaced. Cement mortar cubes of 1:3 grade were prepared. These cubes were cured under normal water for 7 days, 14days and 28 days. Compressive strength test was conducted for all mixes of cement mortar cubes.

  13. Evaluation of red mud as pozzolanic material in replacement of cement for production of mortars

    International Nuclear Information System (INIS)

    Manfroi, E.P.; Cheriaf, M.; Rocha, J.C.

    2010-01-01

    Red mud is a by-product of the alkaline extraction of aluminum from the bauxite and represents a renewed environmental problem due the significant annual throughput by the plants. In the present work, the pozzolanic properties of Brazilian red mud fired at 600, 700, 800 and 900 deg C were investigated by monitoring lime consumption using DTA analysis and Brazilian standard methodology NBR 5772 (1992). Products and kinetics of hydration were determined in cement pastes produced with 5 and 15% red mud using x-ray diffraction and DTA analysis. Compressive strength and capillary absorption tests were realized on mortars constituted by 5, 10 and 15% red mud in replacement of cement. When calcined at 600 deg C, the red mud develops good pozzolanic properties, and the compressive strength of mortars produced with this waste meet values in accordance with regulatory standard. These results shown than red mud can be used, in partial replacement of cement, as new construction material to produce sustainable mortars with low environmental impact. (author)

  14. Resistance to acid attack of portland cement mortars produced with red mud as a pozzolanic additive

    International Nuclear Information System (INIS)

    Balbino, Thiago Gabriel Ferreira; Fortes, Gustavo Mattos; Lourenco, Rafaela Roberta; Rodrigues, Jose de Anchieta

    2011-01-01

    Portland cement structures are usually exposed to aggressive environments, which requires the knowledge of the performance of these materials under deleterious conditions. In this study, it was evaluated the resistance to acid attack of mortars that contain ordinary (CPI) and compost (CPII-Z) Portland cements, adding to the first red mud (RB) as a pozzolanic additive in different conditions: without calcination, calcined at 400 ° C and at 600 ° C. The specimens were subjected to HCl and H 2 SO 4 solutions, both with concentration of 1.0 Mol L -1 for 28 days, monitoring the weight loss and leached material nature by atomic emission inductively coupled plasma (ICP). The hydration products were studied by thermogravimetric analysis (TGA) and X-ray diffraction (XRD) of the hydrated cement pastes. It was observed a reduction of portlandite amount in the RB containing cement pastes, indicating a possible pozzolanic activity of the red mud. The mortars prepared with RB were more resistant to HCl, while that ones with calcined RB present a better performance in H 2 SO 4 attack. (author)

  15. The Effect of Graphene Oxide on Cement Mortar

    Science.gov (United States)

    Kjaernsmo, Henrik; Kakay, Samdar; Fossa, Kjell T.; Gronli, John

    2018-05-01

    This paper investigates the effect of water dispersed- and powder Graphene oxide (GO) nanoparticle on fresh cement mortar, microstructure and mechanical strength after 3,7, and 28 days of curing. These properties were studied by treating the cement mortar with 0.03 wt%, 0.05 wt%, and 0.2 wt% GO of the cement weight combined with 0.8wt % polycarboxylate superplasticizer. The results show that the workability decreases as increasing the content of water dispersed GO. The heat of hydration is increased for both types of GO systems. The percent air content in 0.03 wt% and 0.05 wt% GO is almost constant, but increased from 3.2 % to 4.9 % in 0.2 wt% water dispersed GO. The increased air content has effect on poor compaction and workability. GO has the potential of accelerating the hydration process and enhance the early mechanical strength (3 and 7 days), but the workability seems to diminish the mechanical strength after 28 days of curing, particularly for the highest content of water dispersed GO. No distinct influence of GO on the microstructure. The overall results showed that the impact of water dispersed GO was found out to be higher than the powder GO.

  16. Polymer-Cement Mortar with Quarry Waste as Sand Replacement

    Directory of Open Access Journals (Sweden)

    D. N. Gómez-Balbuena

    2018-01-01

    Full Text Available The activities of carved Quarry extraction generate problems of landscape pollution such is the case of solid waste discharged into open land dumps in central Mexico. This article presents the technological application of this solid waste in a new polymeric material with properties similar to those of a traditional mortar. It is concluded that the polymeric material uses low amounts of cement with respect to the traditional mortar, and it is elaborated with the recycled quarry as they are presented in its granulometry. The polymer used favored a low water/cement ratio (0.3 which did not allow to decrease resistance due to the fine nature of the materials (residues and cement in addition to maintaining the workability of the material. The quarry residue was classified as silt with low plasticity and was characterized by X-ray diffraction and Fluorescence to identify 76% of SiO2, which is why it was used as a stone aggregate even though the fines content was approximately 93%. The maximum compression resistance obtained at 28 days were 8 Mpa with the polymer/solid ratios of 0.10, water/solids of 0.30, and quarry/solids of 0.67. Linear equations were analyzed for more representative values with R squared adjustment.

  17. Evaluation of electric properties of cement mortars containing pozzolans

    Directory of Open Access Journals (Sweden)

    Cruz, J. M.

    2011-03-01

    Full Text Available In this paper the evolution of the microstructure of Portland cement mortar is analyzed, by using electrical impedance measurements. Cement mortars are compared without and with two pozzolanic substitutions: spent fluid catalytic cracking catalyst (FCC and metakaolin (MK. The measurement method is described and the model for analyzing the electrical impedance spectra is developed. Three electrical parameters are defined: electrical resistivity, capacitance exponent, and capacitive factor. The results show a significant increase in resistivity of the mortars with pozzolans after 7 days of curing, especially in mortars with MK. This increase is correlated with lime-fixing by the pozzolans. The capacitive properties evolve differently at early age, but reach the same values after 148 days. The electrical and mineralogical data show that the evolution of the microstructure in the mortar with MK starts before it does in the mortars with FCC and that the final microstructure becomes different.

    En este trabajo se analiza la microestructura de morteros de cemento Portland, mediante medidas de impedancia eléctrica. Se comparan morteros de cemento sin y con dos sustituciones puzolánicas: residuo de catalizador de craqueo catalítico (FCC y metacaolín (MK. Se describe el método de medida y se desarrolla el modelo de análisis de los espectros de impedancia eléctrica. Se definen tres parámetros eléctricos: resistividad eléctrica, exponente capacitivo, y factor capacitivo. Se observa un aumento importante de la resistividad de los morteros con puzolana a partir de los 7 días de curado, sobre todo en morteros con MK. Este aumento está correlacionado con la fijación de cal de las puzolanas. Las propiedades capacitivas son diferentes a edad temprana, pero se igualan a los 148 días. Los resultados eléctricos y mineralógicos muestran que la evolución microestructural comienza antes en los morteros con MK que con FCC y que la microestructura

  18. Influence of moisture condition on chloride diffusion in partially saturated ordinary Portland cement mortar

    NARCIS (Netherlands)

    Zhang, Y.; Zhang, M.; Ye, G.

    2018-01-01

    Experiments have been carried out to study the influence of moisture condition, including moisture content and its distribution, on the chloride diffusion in partially saturated ordinary Portland cement mortar. The mortar samples with water-to-cement (w/c) ratios of 0.4, 0.5 and 0.6, cured for 1

  19. Natural radioactivity levels and danger ratio in cements, concretes and mortars used in construction

    International Nuclear Information System (INIS)

    Meneses, J.; Pacheco, C.; Avila, J. M.; Miro, C.

    2010-01-01

    We have determined the natural radiation level in three types of adhesive cements, five types of concrete and two types of mortars of different strength normally used in the construction field. Of these materials, both concrete and mortars were prepared in our laboratories, cements the contrary were of a commercial nature.

  20. Inhibition of Cracks on the Surface of Cement Mortar Using Estabragh Fibers

    Directory of Open Access Journals (Sweden)

    Tahereh Soleimani

    2013-01-01

    Full Text Available The influence of adding Estabragh fibers into the cement composites of mortar on surface cracks and mechanical properties of mortar has been studied at various fiber proportions of 0.25%, 0.5%, and 0.75%. The mortar shrinkage was evaluated by counting the number of cracks and measuring the width of cracks on the surface of mortar specimens. Although the Estabragh fibers loss their strength in an alkali environment of cement composites, the ability of Estabragh fibers to bridge on the microcracks in the mortar matrix causes a decrease in the number of cracks and in their width on the surface of the mortar samples in comparison with the plain mortar. However, considering the mechanical properties of specimens such as bending strength and compressive strength, among all fiber proportions, only the specimens with 0.25% of Estabragh fiber performed better in all respects compared to the physical and mechanical properties of reinforced cement composite of mortar. Consequently, by adding 0.25% of Estabragh fibers to the cement mortar, a remarkable inhibition in crack generation on fiber-containing cement composite of mortar is achieved.

  1. The effects of cement-based and cement-ash-based mortar slabs on indoor air quality

    DEFF Research Database (Denmark)

    Krejcirikova, Barbora; Kolarik, Jakub; Wargocki, Pawel

    2018-01-01

    The effects of emissions from cement-based and cement-ash-based mortar slabs were studied. In the latter, 30% of the cement content had been replaced by sewage sludge ash. They were tested singly and together with either carpet or linoleum. The air exhausted from the chambers was assessed by means...... of odour intensity and chemical characterization of emissions. Odour intensity increased with the increased exposed area of the slabs. It did not differ significantly between cement-based or cement-ash-based mortar and neither did the chemical composition of the exhaust air. A significant sink effect...

  2. Physical and mechanical properties of cement mortar made with brick waste

    Directory of Open Access Journals (Sweden)

    Mohamed Guendouz

    2018-01-01

    Full Text Available The development of new building materials is a current problem where researchers are trying to find the right materials for each region and returning cheapest countries. Recycling and recovery of waste are now considered as a promising solution to meet the deficit between production and consumption and protecting the environment. This work focused on the study of the effect of brick waste in the production of cement mortar with substitution rates ranging from 5-30% by weight of cement and to compare its performance with fresh and hardened state with ordinary mortar considered as control mortar. Compressive and tensile strengths up to 28 days of age were compared with those of controlled mortar. Water absorption was also measured at 28 days of age. The test results indicate the beneficial effect of brick waste powder on performance of cement mortar with an optimum of 15% of cement weight substitution.

  3. Effect of amorphous silica ash used as a partial replacement for cement on the compressive and flexural strengths cement mortar.

    Science.gov (United States)

    Usman, Aliyu; Ibrahim, Muhammad B.; Bala, Nura

    2018-04-01

    This research is aimed at investigating the effect of using amorphous silica ash (ASA) obtained from rice husk as a partial replacement of ordinary Portland cement (OPC) on the compressive and flexural strength of mortar. ASA was used in partial replacement of ordinary Portland cement in the following percentages 2.5 percent, 5 percent, 7.5 percent and 10 percent. These partial replacements were used to produce Cement-ASA mortar. ASA was found to contain all major chemical compounds found in cement with the exception of alumina, which are SiO2 (91.5%), CaO (2.84%), Fe2O3 (1.96%), and loss on ignition (LOI) was found to be 9.18%. It also contains other minor oxides found in cement. The test on hardened mortar were destructive in nature which include flexural strength test on prismatic beam (40mm x 40mm x 160mm) and compressive strength test on the cube size (40mm x 40mm, by using the auxiliary steel plates) at 2,7,14 and 28 days curing. The Cement-ASA mortar flexural and compressive strengths were found to be increasing with curing time and decreases with cement replacement by ASA. It was observed that 5 percent replacement of cement with ASA attained the highest strength for all the curing ages and all the percentage replacements attained the targeted compressive strength of 6N/mm2 for 28 days for the cement mortar

  4. Influence of relationship water/cement upon the processing of cements with pozzolana in standard mortar

    Directory of Open Access Journals (Sweden)

    Gener Rizo, M.

    2002-03-01

    Full Text Available The processing of standard mortar is completed following different methods in accordance with the country, but they exist two fundamental tendecies, the ISO and the ASTM. The cuban norm for mechanic-physic tests is based in ISO, and so they use a constant relationship water/cement in the processing of standard mortar a great problem concerning the cement users when they tested those mixed with puzzolanes, because they don't take care of the bigger water needs of those materials. In this work we present an study of the behaviour of Pozzolanic Portland cements (PP-250 elaborates with a fix and changeable relationship water/cement, obtained starting from the fluidity of the pure Portland cement. (P-350 The results obtained shows that the mechanical resistance decreased in cement mortars PP-250 realised with changeable relationship water/cement. So we recommend the adoption of an optional procedure to elaborate a quality mortar with pozzolana cements.

    La elaboración del mortero normalizado se realiza internacionalmente por diferentes métodos, pero existen dos tendencias fundamentales, la enunciada por ISO y por ASTM. La norma cubana de ensayos físico-mecánicos de cemento se basa en la norma ISO, por lo que para la elaboración del mortero normalizado se utiliza una relación agua/cemento constante. Esto ha provocado discrepancias con los usuarios del cemento, especialmente cuando se ensayan los cementos que contienen puzolanas, ya que se plantea que no se tiene en cuenta la mayor demanda de agua de estos materiales. En el presente trabajo se presenta un estudio del comportamiento de cementos Portland Puzolánicos (PP-250 elaborados con una relación agua/ cemento fija y variable, lograda a partir de la fluidez de la pasta de cemento Portland puro (P-350. Los resultados obtenidos indican que se producen disminuciones en la resistencia mecánica en los morteros de cemento PP-250 elaborados con agua/ cemento variable y recomienda la

  5. Highly permeable, cement-bounded backfilling mortars for SMA repositories

    International Nuclear Information System (INIS)

    Jacobs, F.; Mayer, G.; Wittmann, F.H.

    1994-03-01

    In low- and intermediate-level waste repositories, gas is produced due e.g. to corrosion. This gas must be able to escape from the repository in order to prevent damage to the repository structure. A cement-based backfill should take over this function. For this purpose, the composition of cement-based materials was varied to study their influence on porosity and permeability. In parallel to this study the behaviour of fresh concrete, the liberation of the heat of hydration and the hardened concrete properties were investigated. To characterize the permeability of cement-based materials the following parameters are important: 1) composition of the material (pore fabric), 2) storage conditions (degree of saturation), 3) degree of hydration (age), 4) measuring fluid. A change in the composition of cement-based materials can vary the permeability by ten orders of magnitude. It is shown that, by using dense aggregates, the transport of the fluid takes place through the matrix and along the aggregate/matrix interface. By using porous aggregates the permeability can be increased by two orders of magnitude. In the case of a dense matrix, porous aggregates do not alter the permeability. Increasing the matrix content or interface content increases permeability. Hence light weight mortars are an obvious choice. Like-grained mixes showed higher permeabilities in combination with better mechanical properties but, in comparison to normal mixes, they showed worse flow properties. With the composition cement-: water-: aggregate content 1:0.4:5.33 the likegrained mix with aggregates ranging from 2 to 3 mm proved to be a suitable material. With a low compaction after 28 days this mix reaches a permeability of 4.10 -12 m 2 and an uniaxial cylinder compressive strength of 16 N/mm 2 . (author) 58 figs., 23 tabs., refs

  6. Determining the water-cement ratio, cement content, water content and degree of hydration of hardened cement paste: Method development and validation on paste samples

    International Nuclear Information System (INIS)

    Wong, H.S.; Buenfeld, N.R.

    2009-01-01

    We propose a new method to estimate the initial cement content, water content and free water/cement ratio (w/c) of hardened cement-based materials made with Portland cements that have unknown mixture proportions and degree of hydration. This method first quantifies the composition of the hardened cement paste, i.e. the volumetric fractions of capillary pores, hydration products and unreacted cement, using high-resolution field emission scanning electron microscopy (FE-SEM) in the backscattered electron (BSE) mode and image analysis. From the obtained data and the volumetric increase of solids during cement hydration, we compute the initial free water content and cement content, hence the free w/c ratio. The same method can also be used to calculate the degree of hydration. The proposed method has the advantage that it is quantitative and does not require comparison with calibration graphs or reference samples made with the same materials and cured to the same degree of hydration as the tested sample. This paper reports the development, assumptions and limitations of the proposed method, and preliminary results from Portland cement pastes with a range of w/c ratios (0.25-0.50) and curing ages (3-90 days). We also discuss the extension of the technique to mortars and concretes, and samples made with blended cements.

  7. Effect of water curing duration on strength behaviour of portland composite cement (PCC) mortar

    Science.gov (United States)

    Caronge, M. A.; Tjaronge, M. W.; Hamada, H.; Irmawaty, R.

    2017-11-01

    Cement manufacturing of Indonesia has been introduced Portland Composite Cement (PCC) to minimize the rising production cost of cement which contains 80% clinker and 20% mineral admixture. A proper curing is very important when the cement contains mineral admixture materials. This paper reports the results of an experimental study conducted to evaluate the effect of water curing duration on strength behaviour of PCC mortar. Mortar specimens with water to cement ratio of (W/C) 0.5 were casted. Compressive strength, flexural strength and concrete resistance were tested at 7, 28 and 91 days cured water. The results indicated that water curing duration is essential to continue the pozzolanic reaction in mortar which contributes to the development of strength of mortar made with PCC.

  8. Statistical approach to predict compressive strength of high workability slag-cement mortars

    International Nuclear Information System (INIS)

    Memon, N.A.; Memon, N.A.; Sumadi, S.R.

    2009-01-01

    This paper reports an attempt made to develop empirical expressions to estimate/ predict the compressive strength of high workability slag-cement mortars. Experimental data of 54 mix mortars were used. The mortars were prepared with slag as cement replacement of the order of 0, 50 and 60%. The flow (workability) was maintained at 136+-3%. The numerical and statistical analysis was performed by using database computer software Microsoft Office Excel 2003. Three empirical mathematical models were developed to estimate/predict 28 days compressive strength of high workability slag cement-mortars with 0, 50 and 60% slag which predict the values accurate between 97 and 98%. Finally a generalized empirical mathematical model was proposed which can predict 28 days compressive strength of high workability mortars up to degree of accuracy 95%. (author)

  9. The transformation of waste Bakelite to replace natural fine aggregate in cement mortar

    Directory of Open Access Journals (Sweden)

    Nopagon Usahanunth

    2017-06-01

    Full Text Available Bakelite material has been used to produce the various components for cars and consumer goods industry in Thailand. The growth of Bakelite consumption increases Bakelite waste. Bakelite waste is prohibited from disposing of direct landfilling and open burning because of the improper disposal and emission reasons. A large amount of this waste needs the large safe space of warehouse area for keeping which becomes a waste management problem. Size reduction by milling machine is helpful for waste handling and storing, however, the post-milling waste Bakelite plastic utilization shall be studied to maintain the waste storing capacity. There are some studies of the milling machine used for waste plastic size reduction. However, the particular study of milling machine application for waste size reduction and its milling waste utilization is still insufficient in Thailand. The purpose of this research is the use of waste Bakelite aggregate milling machine for Bakelite waste size reduction and use of the post-milling waste Bakelite as a fine aggregate to replace natural sand material in cement mortar. The waste Bakelite fine aggregate (WBFA was mixed in cement mortar mixture with the proportion 0% 20% 40% 60% 80% and 100% by volume for cement mortar sample preparation. The mortar sample was tested for compressive strength follow ASTM standard. The compressive test result of mortar samples will be compared between conventional mortar (0% WBFA and waste Bakelite mortar (WBM as well as comparing with the mortar standard. From an analysis of the sample test data found that the WBFA content in cement mortar mixture can predict the strength of WBM. The compressive strength of WBM at 28 days age with the fraction of WBFA is not exceeded 11.03%, and 23.08% respectively can be met the mortar standard according to the equation. The utilization of WBM to develop mortar non-structural mortar product can be usable from a technical point of view.

  10. Effect of cement fineness and polycarboxylate dosage on the rheological and mechanical behavior of a mortar

    Directory of Open Access Journals (Sweden)

    Zahia Didouche

    2018-01-01

    Full Text Available The use of certain organic additives in the production of mortar and concrete influences the workability and the hydration kinetic of mortar. This results in a modification of some properties, namely rheological behavior and mechanical strength. The objective of this work is to evaluate the rheological and mechanical behavior of a mortar by varying the fineness of the cement and using the superplasticizer Polycarboxylate.

  11. Effect of nylon fiber on mechanical properties of cement based mortar

    Science.gov (United States)

    Hanif, I. M.; Syuhaili, M. R. Noor; Hasmori, M. F.; Shahmi, S. M.

    2017-11-01

    An investigation has been carried out to study the effect of nylon fiber on the mechanical properties of cement based mortar after receiving large quantities of nylon waste. Subsequently, this research was conducted to compare the compressive, tensile and flexural strength of normal cement based mortar with nylon fiber cement based mortar. All samples using constant water-cement ratio of 0.63 and three different percentages of nylon fiber were added in the mixture during the samples preparation period which consists of 0.5%, 1.5% and 2.5% by total weight of cement based mortar. The results obtained with different nylon percentage marked an increases in compressive strength (up to 17%), tensile strength (up to 21%) and flexural strength (up to 13%) when compared with control cement based mortar samples. Therefore, the results obtained from this study shows that by using nylon fiber as additive material can improve the mechanical properties of the cement based mortar and at the same time produce a good sustainable product that can protects and conserve the marine environment.

  12. Valorisation of waste plastic bags in cement-mortar composites as ...

    African Journals Online (AJOL)

    2015-01-07

    Jan 7, 2015 ... Keywords: Waste plastic bags, cement-plastic-mortar composite, aggregates coating ..... and closely attached to the aggregate by physical bonds and ... transformation steps, known as fusing material behaviour. In fact,.

  13. Influence of polymer fibers on rheological properties of cement mortars

    Directory of Open Access Journals (Sweden)

    Malaszkiewicz Dorota

    2017-10-01

    Full Text Available The reinforcing effect of fibers in cement composites often results in the improvement of the brittle nature of cementitious materials. But the decrease in the workability of fresh concrete is often the disadvantage of fibers addition. Conventional single-point workability tests cannot characterize workability of concrete in terms of fundamental rheological parameters. To this end, this paper describes an investigation of the influence of synthetic fiber additions (fiber length in the range 12–50 mm and volume fraction in the range 0–4% on the rheological properties of fiber reinforced fresh mortar (FRFM and development of these properties over time. The rheometer Viskomat XL was used in this study. Within the limitations of the instrument and testing procedure it is shown that FRFMs conform to the Bingham model. Natural postglacial sand 0/4 mm was used as a fine aggregate and cement CEMI 42.5 R was used as a binder. Three commercial synthetic fibers were selected for these examinations. Rheological properties were expressed in terms of Bingham model parameters g (yield value and h (plastic viscosity. Based on the test results it was found out that the fiber type and volume fraction affected both the yield stress and plastic viscosity.

  14. Influence of polymer fibers on rheological properties of cement mortars

    Science.gov (United States)

    Malaszkiewicz, Dorota

    2017-10-01

    The reinforcing effect of fibers in cement composites often results in the improvement of the brittle nature of cementitious materials. But the decrease in the workability of fresh concrete is often the disadvantage of fibers addition. Conventional single-point workability tests cannot characterize workability of concrete in terms of fundamental rheological parameters. To this end, this paper describes an investigation of the influence of synthetic fiber additions (fiber length in the range 12-50 mm and volume fraction in the range 0-4%) on the rheological properties of fiber reinforced fresh mortar (FRFM) and development of these properties over time. The rheometer Viskomat XL was used in this study. Within the limitations of the instrument and testing procedure it is shown that FRFMs conform to the Bingham model. Natural postglacial sand 0/4 mm was used as a fine aggregate and cement CEMI 42.5 R was used as a binder. Three commercial synthetic fibers were selected for these examinations. Rheological properties were expressed in terms of Bingham model parameters g (yield value ) and h (plastic viscosity). Based on the test results it was found out that the fiber type and volume fraction affected both the yield stress and plastic viscosity.

  15. Use of waste brick as a partial replacement of cement in mortar.

    Science.gov (United States)

    Naceri, Abdelghani; Hamina, Makhloufi Chikouche

    2009-08-01

    The aim of this study is to investigate the use of waste brick as a partial replacement for cement in the production of cement mortar. Clinker was replaced by waste brick in different proportions (0%, 5%, 10%, 15% and 20%) by weight for cement. The physico-chemical properties of cement at anhydrous state and the hydrated state, thus the mechanical strengths (flexural and compressive strengths after 7, 28 and 90 days) for the mortar were studied. The microstructure of the mortar was investigated using scanning electron microscopy (SEM), the mineralogical composition (mineral phases) of the artificial pozzolan was investigated by the X-ray diffraction (XRD) and the particle size distributions was obtained from laser granulometry (LG) of cements powders used in this study. The results obtained show that the addition of artificial pozzolan improves the grinding time and setting times of the cement, thus the mechanical characteristics of mortar. A substitution of cement by 10% of waste brick increased mechanical strengths of mortar. The results of the investigation confirmed the potential use of this waste material to produce pozzolanic cement.

  16. Use of waste brick as a partial replacement of cement in mortar

    International Nuclear Information System (INIS)

    Naceri, Abdelghani; Hamina, Makhloufi Chikouche

    2009-01-01

    The aim of this study is to investigate the use of waste brick as a partial replacement for cement in the production of cement mortar. Clinker was replaced by waste brick in different proportions (0%, 5%, 10%, 15% and 20%) by weight for cement. The physico-chemical properties of cement at anhydrous state and the hydrated state, thus the mechanical strengths (flexural and compressive strengths after 7, 28 and 90 days) for the mortar were studied. The microstructure of the mortar was investigated using scanning electron microscopy (SEM), the mineralogical composition (mineral phases) of the artificial pozzolan was investigated by the X-ray diffraction (XRD) and the particle size distributions was obtained from laser granulometry (LG) of cements powders used in this study. The results obtained show that the addition of artificial pozzolan improves the grinding time and setting times of the cement, thus the mechanical characteristics of mortar. A substitution of cement by 10% of waste brick increased mechanical strengths of mortar. The results of the investigation confirmed the potential use of this waste material to produce pozzolanic cement.

  17. physico-chemical studies on polymer impregnated blending cement mortar composite

    International Nuclear Information System (INIS)

    Abdel-Rahman, H.A.

    2001-01-01

    as the increasing of the demand on a specific performance characteristics in concrete such as improved strength, low heat, sulfate resistance, improved impermeability and certain other applications. some of the industrial waste materials such as the blast-furnace slag, silica fume and fly ash were mixed with the cement clinker to produce blended cement . the use of these materials modifies the strength, pore structure and permeability of hardened cement mortar or concrete. the incorporation of blast furnace slag and silica fume in the hardened blended cement mortar or concrete is a common practice recently due to technological, economical and environmental benefits

  18. R7T7 glass alteration in the presence of mortar: effect of the cement grade

    International Nuclear Information System (INIS)

    Andriambololona, Z.; Godon, N.; Vernaz, E.

    1991-01-01

    R7T7 glass alteration was investigated in the presence of four mortars prepared from four different cement grades: 'CPA' Portland cement (mortar M1), CPA with pozzolana additive (M2), CPA with amorphous silica additive (M3) and 'CLK' blast furnace slag cement (M4). Glass specimens were also altered in Volvic mineral water and in a cement effluent. Glass corrosion in the cement media was greater than in Volvic water, but well below what could be expected from the high pH (approx 12.5). The relatively low alteration was probably related to the protective action of the calcium-enriched gel layer that formed at the glass surface. The glass corrosion rate was 2 to 3 times lower with cement containing pozzolana or silica gel additives or with CLK cement than with CPA cement alone. 8 refs., 8 figs

  19. Effect of Gamma Irradiation on Polymer Modified White Sand Cement Mortar Composites

    International Nuclear Information System (INIS)

    Khattab, M.M.

    2012-01-01

    This study focuses on the substitution effect of standard sand of conventional cement mortar made from ordinary Portland cement (OPC) and standard sand (SS) OPC/SS 1:3; by different ratios of white sand (WS) powder to prepare three types of white sand cement mortar designated as 1OPC:2SS:1WS, 1OPC:1SS:2WS and 1OPC:0SS:3WS. The prepared samples were first cured under tap water for different time intervals namely 3, 7, 28 and 90 days. The effect of addition of 10% styrene-acrylic ester (SAE) as well as the effect of different doses of gamma rays (10, 20, 30 and 50 kGy) on the physicomechanical properties of polymer modified white sand cement mortar specimens also discussed. Compression strength test, total porosity and water absorption percentages were measured according to standard specifications. The obtained data indicated that, the cement mortar samples containing different ratios of white sand have lower values of compressive strength as compared to the conventional cement mortar while, the percentages of total porosity and water absorption increased. On the other hand, the polymer modified mortar specimens showed a noticeably enhancement in the physico-mechanical properties under the effect of gamma-radiation than those of untreated samples. These results were confirmed by scanning electron microscopy (SEM), and thermogravimetric analysis (TGA) studies

  20. Utilization of recycled glass derived from cathode ray tube glass as fine aggregate in cement mortar

    International Nuclear Information System (INIS)

    Ling, Tung-Chai; Poon, Chi-Sun

    2011-01-01

    Graphical abstract: Display Omitted Highlights: → A recycling/treatment process to remove lead on funnel glass surface is described. → Utilizing recycled funnel glass in mortar can reduce hazardous CRT glass wastes. → Effects of CRT glass content on the properties of cement mortar are studied. → Fly ash can effectively mitigate ASR expansion of mortar even at 100% glass content. → Alkaline medium in cement matrix successfully prevented the leaching of lead. - Abstract: Rapid advances in the electronic industry led to an excessive amount of early disposal of older electronic devices such as computer monitors and old televisions (TV) before the end of their useful life. The management of cathode ray tubes (CRT), which have been a key component in computer monitors and TV sets, has become a major environmental problem worldwide. Therefore, there is a pressing need to develop sustainable alternative methods to manage hazardous CRT glass waste. This study assesses the feasibility of utilizing CRT glass as a substitute for natural aggregates in cement mortar. The CRT glass investigated was an acid-washed funnel glass of dismantled CRT from computer monitors and old TV sets. The mechanical properties of mortar mixes containing 0%, 25%, 50%, 75% and 100% of CRT glass were investigated. The potential of the alkali-silica reaction (ASR) and leachability of lead were also evaluated. The results confirmed that the properties of the mortar mixes prepared with CRT glass was similar to that of the control mortar using sand as fine aggregate, and displayed innocuous behaviour in the ASR expansion test. Incorporating CRT glass in cement mortar successfully prevented the leaching of lead. We conclude that it is feasible to utilize CRT glass in cement mortar production.

  1. Investigation of a Hardened Cement Paste Grout

    DEFF Research Database (Denmark)

    Esteves, Luis Pedro; Sørensen, Eigil Verner

    This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S.......This report documents a series of tests performed on a hardened cement paste grout delivered by the client, Det Norske Veritas A/S....

  2. The effect of modified hydrotalcites on mechanical properties and chloride penetration resistance in cement mortar

    NARCIS (Netherlands)

    Yang, Z.; Fischer, H.; Polder, R.B.

    2015-01-01

    In this paper, two types of modified hydrotalcites (MHT) were incorporated into cement mortars with two dosage levels (replacing 5% and 10% cement by mass). Designated testing programme including strength test, porosity test, and rapid chloride migration and diffusion test were employed to

  3. Characteristics of shock propagation in high-strength cement mortar

    Science.gov (United States)

    Wang, Zhanjiang; Li, Xiaolan; Zhang, Ruoqi

    2001-06-01

    Planar impact experiments have been performed on high-strength cement mortar to determine characteristics of shock propagation.The experiments were conducted on a light-gas gun,and permanent-magnet particle velocity gages were used to obtain the sand of 0.5 3.5mm size.A bulk density of 2.31g/cm^3,and a compressive and tensile strength of 82MPa and 7.8MPa,respectively,were determined.Three kinds of experimental techniques were used,including the reverse ballistic configuration.These techniques effectively averaged the measured dynamic compression state over a sensibly large volume of the test sample.The impact velocities were controlled over a range of approximately 80m/s to 0.83km/s.Hugoniot equation of state data were obtained for the material over a pressure range of approximately 0.2 2.0GPa,and its nonlinear constitutive relation were analyzed.The experiment results show that,in higher pressure range provided in the experiment,the shock wave in the material splits into two components of an elastic and a plastic,with the Hugoniot elastic limit 0.4 0.5GPa and the precursor velocity about 4.7km/s,and the material presents a very strong nonlinear dynamic response,and its shock amplitude will greatly decrease in propagation.

  4. Strength and Mechanical Properties of High Strength Cement Mortar with Silica Fume

    OpenAIRE

    川上, 英男; 谷, 康博

    1993-01-01

    Two series of tests were carried out to clarify the effects of silica fume on the strength and mechanical properties of cement mortar. The test specimens of cement mortar were prepared within the flow values between 180 mm and 240 mm which qualifies better workability of the concrete. The fiow values were attained by using superplasticizer. The specimens were tested at the age of 4 weeks. Main results of the experiments are as follows. 1. At a given cement water ratio,the larger volume of sil...

  5. Cement content influence in rebar corrosion in carbonated mortars

    Directory of Open Access Journals (Sweden)

    Américo, P. O.

    2003-12-01

    Full Text Available The cement hydration products protect the concrete rebars of the reinforced concrete due to the production of Ca(OH2, NaOH, and KOH that, upon dissolving in the concrete s aqueous phase, generate a pH above 12.5. However, reinforced concrete structures are exposed to pollutant gases, such as, CO2 which upon penetrating the concrete, reacts with the alkaline components, consequently reducing the pH of the aqueous phase causing the loss of passivity by the rebar and as a consequence its corrosion when there is the presence of humidity and oxygen. The objective of the current paper is the analysis of the alkaline reserve influence, measured by the cement content, in the corrosion of rebars employing the polarization resistance technique for determining the corrosion intensity. Results for corrosion intensity of rebars embedded in prismatic mortar test specimens are produced with three cement content levels, with equal water/cement ratio. Cylindrical test specimens were also used for verification of the capillary absorption and the porosity by means of mercury porosymetry The results show that the initiation period is shorter and the corrosion intensity of the rebars is higher when the cement content is lower However, there is also an alteration in the microstructure upon altering the cement content, and far this reason one cannot conclude that the alkaline reserve alone is responsible for these results.

    Los productos de hidratación del cemento protegen las armaduras embebidas en el hormigón debido a la gran cantidad de Ca(OH2, NaOH y KOH disueltos en la fase acuosa del hormigón que proporcionan un pH mayor que 12,5. Sin embargo, las estructuras de hormigón armado están expuestas a los gases contaminantes como el CO2, que al penetrar en el hormigón reacciona con los compuestos alcalinos, se reduce el pH de la fase acuosa y provocan la despasivación de la armadura. Posteriormente, si hay

  6. Using dehydrated cement paste as new type of cement additive

    NARCIS (Netherlands)

    Yu, R.; Shui, Z.H.; Dong, J

    2013-01-01

    This paper presents an experimental study, including evaluation and modification, on using dehydrated cement paste (DCP) as a new type of cement additive. After a series of processes, normal DCP (N-DCP) was produced as before and a modified form of DCP (M-DCP) was produced as well. The cementitious

  7. Quantitative sensing of corroded steel rebar embedded in cement mortar specimens using ultrasonic testing

    Science.gov (United States)

    Owusu Twumasi, Jones; Le, Viet; Tang, Qixiang; Yu, Tzuyang

    2016-04-01

    Corrosion of steel reinforcing bars (rebars) is the primary cause for the deterioration of reinforced concrete structures. Traditional corrosion monitoring methods such as half-cell potential and linear polarization resistance can only detect the presence of corrosion but cannot quantify it. This study presents an experimental investigation of quantifying degree of corrosion of steel rebar inside cement mortar specimens using ultrasonic testing (UT). A UT device with two 54 kHz transducers was used to measure ultrasonic pulse velocity (UPV) of cement mortar, uncorroded and corroded reinforced cement mortar specimens, utilizing the direct transmission method. The results obtained from the study show that UPV decreases linearly with increase in degree of corrosion and corrosion-induced cracks (surface cracks). With respect to quantifying the degree of corrosion, a model was developed by simultaneously fitting UPV and surface crack width measurements to a two-parameter linear model. The proposed model can be used for predicting the degree of corrosion of steel rebar embedded in cement mortar under similar conditions used in this study up to 3.03%. Furthermore, the modeling approach can be applied to corroded reinforced concrete specimens with additional modification. The findings from this study show that UT has the potential of quantifying the degree of corrosion inside reinforced cement mortar specimens.

  8. The influence of hardening conditions on the properties of masonry cement mortar prisms made in brick moulds

    NARCIS (Netherlands)

    Bertram, G.; Lourenco, P.B.; Hasseltine, B.A.; Vasconseles, G.

    2014-01-01

    One aspect of our investigation into the spacing of movement joints involved the short and long term deformation of mortar embedded in masonry. In this research the influence of hardening conditions on the physical and mechanical properties of masonry cement mortar [M5] were studied. Mortar prisms

  9. THE USE OF NATURAL TRASS FROM SAYUTAN MAGETAN AND LIME FROM NGAMPEL BLORA AS THE MATERIAL OF CEMENT SUBSTITUTION FOR MORTAR MIXTURE

    Directory of Open Access Journals (Sweden)

    Muhammad Nurzain

    2015-05-01

    Full Text Available Construction works in the Regency of Magetan, as well as in the mountain area far from capital cities and remote from transportation facilities, require large amount of material. In order to cope with the need of sand, people uses natural trass which are plenty to be found in the area. Test and research on its characteristic and strength with its potentials to be used as cement substitution have never been carried out. Lime was taken from Ngampel village, Blora as it is commonly sold in the area. The planned mixture of lime-trass paste was in the effort to obtain the best composition. The weight ratios used were 100%:0%, 80%:20%, 60%:40%, 40%:60%, 20%:80 and 0%:100%. The mortar mixture with cement substitution was 100%, 80%, 60%, 40%, 20% and 0%.The compressive strength of the lime-trash mixture was between 0.000 MPa and 2.545 MPa. The mortar compressive strength achieved was 0.373 MPa - 26.585 MPa. The test results of mortar compressive strength showed that the more cement substitution amount used, the less the compressive strength would be. The mortar compressive strength increased in line to the age of the mortar. The mortar tensile strength obtained was 0.000 MPa - 2.169 MPa. The block compressive strength obtained was 3.336 MPa - 3.403 MPa. Water absorbency of the block was 15.831% -16.056%.

  10. Axial compression behavior of concrete masonry wallettes strengthened with cement mortar overlays

    Directory of Open Access Journals (Sweden)

    F. L. De Oliveira

    Full Text Available This paper presents the results of a series of axial compression tests on concrete block wallettes coated with cement mortar overlays. Different types of mortars and combinations with steel welded meshes and fibers were tested. The experimental results were discussed based on different theoretical approaches: analytical and Finite Element Method models. The main conclusions are: a the application of mortar overlays increases the wall strength, but not in a uniform manner; b the strengthening efficiency of wallettes loaded in axial compression is not proportional to the overlay mortar strength because it can be affected by the failure mechanisms of the wall; c steel mesh reinforced overlays in combination with high strength mortar show better efficiency, because the steel mesh mitigates the damage effects in the block wall and in the overlays themselves; d simplified theoretical methods of analysis as described in this paper can give satisfactory predictions of masonry wall behavior up to a certain level.

  11. Chloride Ion Adsorption Capacity of Anion Exchange Resin in Cement Mortar

    Directory of Open Access Journals (Sweden)

    Yunsu Lee

    2018-04-01

    Full Text Available This paper presents the effect of anion exchange resin (AER on the adsorption of chloride ions in cement mortar. The kinetic and equilibrium behaviors of AER were investigated in distilled water and Ca(OH2 saturated solutions, and then the adsorption of chloride ions by the AER in the mortar specimen was determined. The AER was used as a partial replacement for sand in the mortar specimen. The mortar specimen was coated with epoxy, except for an exposed surface, and then immersed in a NaCl solution for 140 days. The chloride content in the mortar specimen was characterized by energy dispersive X-ray fluorescence analysis and electron probe microanalysis. The results showed that the AER could adsorb the chloride ions from the solution rapidly but had a relatively low performance when the pH of its surrounding environment increased. When the AER was mixed in the cement mortar, its chloride content was higher than that of the cement matrix around it, which confirms the chloride ion adsorption capacity of the AER.

  12. Partial replacement of Portland cement by red ceramic waste in mortars: study of pozzolanic activity

    International Nuclear Information System (INIS)

    Silva, A.R. da; Cabral, K.C.; Pinto, E.N. de M.G.l.

    2016-01-01

    The objective of this study is to analyze the pozzolanic activity of red ceramic residue on the partial replacement of Portland cement in mortars. The mortars were prepared by substituting 25% of the Portland cement for ground of ceramic residue with water cement’s factor of 0.48. The concrete used to construct the reference mortars and those with addiction was CPII-Z-32 (compound of Portland pozzolana cement). The chemical analysis and physical ceramic waste showed that this meets the requirements of NBR12653 (2014) for use as pozzolanic material. The pozzolanic activity index (IAP) obtained for the ceramic waste to twenty-eight days cure rate was 80.28%. (author)

  13. NANOFIBRILLATED CELLULOSE (NFC AS A POTENTIAL REINFORCEMENT FOR HIGH PERFORMANCE CEMENT MORTAR COMPOSITES

    Directory of Open Access Journals (Sweden)

    Mònica Ardanuy,

    2012-07-01

    Full Text Available In this work, nanofibrillated cellulose (NFC has been evaluated as a potential reinforcement for cement mortar composites. Two types of vegetable fibres with different composition and properties (cellulose content and microfibrillar angle, sisal, and cotton linters pulps, were initially characterised in order to assess their reinforcing capability. Sisal pulp was found to be most suitable as reinforcement for the brittle cementitious matrix. Nanofibrillated cellulose was produced by the application of a high intensity refining process of the sisal pulp. It was found that 6 hours of refining time was required to obtain the desired nanofibrillation of the fibers. Cement mortar composites reinforced with both the sisal fibres and the nanofibrillated cellulose were prepared, and the mechanical properties were determined under flexural tests. The cement mortar composites reinforced with the nanofibrillated cellulose exhibited enhanced flexural properties, but lower values of fracture energy, than the ones reinforced with the conventional sisal fibres.

  14. Influence of fly ash fineness on water requirement and shrinkage of blended cement mortars

    Directory of Open Access Journals (Sweden)

    Vanissorn Vimonsatit

    2015-12-01

    Full Text Available In this paper, the influence of fly ash fineness on water requirement and shrinkage of blended cement mortar was studied. The results indicate that the water requirement and shrinkage characteristic of the blended cement mortar are dependent on fly ash fineness and replacement level. The use of coarse fly ash slightly reduces the water requirement but greatly reduced the drying and the autogenous shrinkage of the blended cement mortars and the reduction is more with an increase in the fly ash replacement level. The finer fly ashes further reduce the water requirement, but increase the drying and the autogenous shrinkages as compared with coarser fly ash. The incorporation of superplasticizer drastically reduces the water requirement, but the effect on the drying and autogenous shrinkages of the normal Portland cement mortar is small. However, for the fly ash mortar, the use of superplasticizer results in a decrease in drying shrinkage and in a substantial increase in the autogenous shrinkage particularly for the fine fly ash at a high replacement level.

  15. Evaluation of sulfate resistance of cement mortars containing black rice husk ash.

    Science.gov (United States)

    Chatveera, B; Lertwattanaruk, P

    2009-03-01

    In this paper, black rice husk ashes (BRHAs), which are agrowastes from an electricity generating power plant and a rice mill, were ground and used as a partial cement replacement. The durability of mortars under sulfate attack including expansion and compressive strength loss were investigated. For parametric study, BRHA were used as a Portland cement Type 1 replacement at the levels of 0%, 10%, 30%, and 50% by weight of binder. The water-to-binder ratios were 0.55 and 0.65. For the durability of mortar exposed to sulfate attack, 5% sodium sulfate (Na2SO4) and magnesium sulfate (MgSO4) solutions were used. As a result, when increasing the percentage replacement of BRHA, the expansion and compressive strength loss of mortar decreased. At the replacement levels of 30% and 50% of BRHA, the expansion of the mortars was less than those mixed with sulfate-resistant cement. However, the expansion of the mortars exposed to Na2SO4 was more than those exposed to MgSO4. Increasing the replacement level of BRHA tends to reduce the compressive strength loss of mortars exposed to Na2SO4 attack. In contrary, under MgSO4 attack, when increasing the replacement level of BRHA, the compressive strength loss increases from 0% to 50% in comparison to Portland cement mortar. Results show that ground BRHA can be applied as a pozzolanic material to concrete and also improve resistance to sodium sulfate attack, but it can impair resistance to magnesium sulfate attack.

  16. Characterization of Mechanical and Bactericidal Properties of Cement Mortars Containing Waste Glass Aggregate and Nanomaterials

    Directory of Open Access Journals (Sweden)

    Pawel Sikora

    2016-08-01

    Full Text Available The recycling of waste glass is a major problem for municipalities worldwide. The problem concerns especially colored waste glass which, due to its low recycling rate as result of high level of impurity, has mostly been dumped into landfills. In recent years, a new use was found for it: instead of creating waste, it can be recycled as an additive in building materials. The aim of the study was to evaluate the possibility of manufacturing sustainable and self-cleaning cement mortars with use of commercially available nanomaterials and brown soda-lime waste glass. Mechanical and bactericidal properties of cement mortars containing brown soda-lime waste glass and commercially available nanomaterials (amorphous nanosilica and cement containing nanocrystalline titanium dioxide were analyzed in terms of waste glass content and the effectiveness of nanomaterials. Quartz sand is replaced with brown waste glass at ratios of 25%, 50%, 75% and 100% by weight. Study has shown that waste glass can act as a successful replacement for sand (up to 100% to produce cement mortars while nanosilica is incorporated. Additionally, a positive effect of waste glass aggregate for bactericidal properties of cement mortars was observed.

  17. Characterization of Mechanical and Bactericidal Properties of Cement Mortars Containing Waste Glass Aggregate and Nanomaterials

    Science.gov (United States)

    Sikora, Pawel; Augustyniak, Adrian; Cendrowski, Krzysztof; Horszczaruk, Elzbieta; Rucinska, Teresa; Nawrotek, Pawel; Mijowska, Ewa

    2016-01-01

    The recycling of waste glass is a major problem for municipalities worldwide. The problem concerns especially colored waste glass which, due to its low recycling rate as result of high level of impurity, has mostly been dumped into landfills. In recent years, a new use was found for it: instead of creating waste, it can be recycled as an additive in building materials. The aim of the study was to evaluate the possibility of manufacturing sustainable and self-cleaning cement mortars with use of commercially available nanomaterials and brown soda-lime waste glass. Mechanical and bactericidal properties of cement mortars containing brown soda-lime waste glass and commercially available nanomaterials (amorphous nanosilica and cement containing nanocrystalline titanium dioxide) were analyzed in terms of waste glass content and the effectiveness of nanomaterials. Quartz sand is replaced with brown waste glass at ratios of 25%, 50%, 75% and 100% by weight. Study has shown that waste glass can act as a successful replacement for sand (up to 100%) to produce cement mortars while nanosilica is incorporated. Additionally, a positive effect of waste glass aggregate for bactericidal properties of cement mortars was observed. PMID:28773823

  18. compressive and flexural strength of cement mortar stabilized with ...

    African Journals Online (AJOL)

    PROF. BARTH EKWEME

    concrete. However, plain mortar materials are usually brittle and often crack more easily and fail more suddenly than ... impact strength, higher elastic modulus, better sound proofness ..... in Concrete. Unpublished Ph.D. Thesis, Department.

  19. Pore structure in blended cement pastes

    DEFF Research Database (Denmark)

    Canut, Mariana Moreira Cavalcanti

    Supplementary cementitious materials (SCMs), such as slag and fly ash, are increasingly used as a substitute for Portland cement in the interests of improvement of engineering properties and sustainability of concrete. According to studies improvement of engineering properties can be explained by...... on assumptions of degree of reaction and product densities gave for plain cement pastes results comparable to MIP data.......Supplementary cementitious materials (SCMs), such as slag and fly ash, are increasingly used as a substitute for Portland cement in the interests of improvement of engineering properties and sustainability of concrete. According to studies improvement of engineering properties can be explained...... supplement each other. Cement pastes (w/b=0.4) with and without slag and fly ash cured at two moisture (sealed and saturated) and temperature (20 and 55ºC) conditions were used to investigate the combined impact of SCMs addition and curing on the pore structure of pastes cured up to two years. Also...

  20. PERFORMANCE OF CEMENT MORTARS REPLACED BY GROUND WASTE BRICK IN DIFFERENT AGGRESSIVE CONDITIONS

    Directory of Open Access Journals (Sweden)

    ILHAMI DEMIR

    2011-09-01

    Full Text Available This article investigates the sulphate resistance of cement mortars when subjected to different exposure conditions. Cement mortars were prepared using ground waste brick (GWB as a pozzolanic partial replacement for cement at replacement levels of 0%, 2.5%, 5%, 7.5, 10%, 12.5 and 15%. Mortar specimens were stored under three different conditions: continuous curing in lime-saturated tab water (TW, continuous exposure to 5% sodium sulphate solution (SS, and continuous exposure to 5% ammonium nitrate solution (AN, at a temperature of 20 ± 3 ºC, for 7, 28, 90, and 180 days. Prisms with dimensions of 25×25×285 mm, to determine the expansions of the mortar samples; and another set of prisms with dimensions of 40×40×160 mm, were prepared to calculate the compressive strength of the samples. It was determined that the GWB replacement ratios between 2.5% and 10% decreased the 180 days expansion values. The highest compressive strength values were found for the samples with 10% replacement ratio in the TW, SS, and AN conditions for 180 days. The microstructure of the mortars were investigated using scanning electron microscopy (SEM and the Energy dispersive X-ray (EDX.

  1. Coupling between mechanical behaviour and drying of cementing materials: experimental study on mortars

    International Nuclear Information System (INIS)

    Yurtdas, I.

    2003-10-01

    The aim of this work is to understand the desiccation effects on the mechanical behaviour of cement materials. Two mortars of ratio E/C=0.5 and 0.8 have been tested. All the tests have been implemented after a six months maturing in water. The experimental study has been carried out as follows: 1)tests characterizing the differed behaviour and the transport properties have been carried out 2)tests characterizing the short term multiaxial mechanical behaviour have been carried out. The desiccation shrinkage in terms of the weight loss presents three characteristic phases. The permeability measurement on the mortar 05 shows that the permeability of the specimens dried and crept is greater than those of the specimens dried before being crept, and the permeability of the specimens submitted to a desiccation creep and then dried is sensibly the same as the last one in spite of a very important differed deformation. The influence of the desiccation on the uniaxial and deviatoric compressions resistance depends of the binding agent: for a cement paste of good quality (E/C=0.5), the resistances increase with the desiccation because of the capillary depression and of the hydric gradients. For a cement paste of low quality (E/C=0.8), there is a competitive effect between the increase of the microcracks induced and the specimen rigidification; the microcracking becomes then the parameter controlling the rupture process. The elasto-plastic behaviour becomes a damageable elasto-plastic behaviour during desiccation which induces, as the decrease of the E/C ratio, a translation of the elastic limit surfaces and ruptures towards higher stresses. In parallel, the elastic properties and the incompressibility modulus are damaged and the volume deformations increase after the drying. At last, the decrease of the Young modulus and the passage to the third shrinkage phase in terms of the weight loss coincide. This can be attributed to the induced microcracking: this decrease of the

  2. Influence of superplasticizer on the rheology of fresh cement asphalt paste

    Directory of Open Access Journals (Sweden)

    Jianwei Peng

    2015-12-01

    Full Text Available Cement asphalt (CA paste is an organic–inorganic composite material of cement and asphalt emulsion. Its complicated rheological behavior affects its site application in high speed railway. Superplasticizers (SPs are usually used to improve the construction properties of fresh CA mortar. However, the principle of SPs acting on the rheology of CA paste is seldom studied. In this paper, the effects of polycarboxylate (PCA and naphthalenesulfonate (PNS on the rheological properties of CA pastes, asphalt emulsions (both anionic and cationic and cement pastes were studied, respectively from the viewpoint of adsorption and zeta potential. Centrifugation method was used to determine the adsorption of asphalt onto cement particle, electroacoustic method was employed to study the zeta potential of cement particles of concentrated paste, and optical microscopy was used to observe the dispersion of particles. The results suggest that both PCA and PNS can decrease the yield stress and apparent viscosity of CA pastes. The effect of SPs on the rheology of CA paste can be explained by two reasons. First, PNS can adsorb on both asphalt and cement surface, change the zeta potential and then decrease their yield stress and viscosity, while PCA only adsorb on cement surface. Second, the competitive adsorption of SPs and asphalt prevents asphalt from adsorbing on cement surface and then more asphalt droplets are released into aqueous solution, thereby enhancing the particle dispersion.

  3. Electrodialytically treated MSWI APC residue as substitute for cement in mortar

    DEFF Research Database (Denmark)

    Kirkelund, Gunvor Marie; Geiker, Mette Rica; Jensen, Pernille Erland

    2014-01-01

    Air pollution control (APC) residues from municipal solid waste incineration (MSWI) are considered hazardous waste and need pretreatment prior to possible reuse. Here, two MSWI APC residues, from which the most mobile fraction of heavy metals and salts has been removed by carbonation and/or elect......Air pollution control (APC) residues from municipal solid waste incineration (MSWI) are considered hazardous waste and need pretreatment prior to possible reuse. Here, two MSWI APC residues, from which the most mobile fraction of heavy metals and salts has been removed by carbonation and....../or electrodialytic remediation, were used in Portland cement mortar. Mortar bars with 15 % weight replacement of cement by APC residues showed compressive strengths up to 40 MPa after 28/32 days. Heavy metal and salt leaching from both crushed and monolithic mortars with APC residues was generally similar...

  4. Performance Characteristics of Waste Glass Powder Substituting Portland Cement in Mortar Mixtures

    Science.gov (United States)

    Kara, P.; Csetényi, L. J.; Borosnyói, A.

    2016-04-01

    In the present work, soda-lime glass cullet (flint, amber, green) and special glass cullet (soda-alkaline earth-silicate glass coming from low pressure mercury-discharge lamp cullet and incandescent light bulb borosilicate glass waste cullet) were ground into fine powders in a laboratory planetary ball mill for 30 minutes. CEM I 42.5N Portland cement was applied in mortar mixtures, substituted with waste glass powder at levels of 20% and 30%. Characterisation and testing of waste glass powders included fineness by laser diffraction particle size analysis, specific surface area by nitrogen adsorption technique, particle density by pycnometry and chemical analysis by X-ray fluorescence spectrophotometry. Compressive strength, early age shrinkage cracking and drying shrinkage tests, heat of hydration of mortars, temperature of hydration, X-ray diffraction analysis and volume stability tests were performed to observe the influence of waste glass powder substitution for Portland cement on physical and engineering properties of mortar mixtures.

  5. Wood ash used as partly sand and/or cement replacement in mortar

    DEFF Research Database (Denmark)

    Ottosen, Lisbeth M.; Hansen, Esben Østergaard; Jensen, Pernille Erland

    2016-01-01

    , and the present work reports a characterization of three different WAs. Properties of mortar samples with the WAs used as partly cement and/or sand replacement are reported. Compressive strength development and porosity are the mortar properties in focus. The overall aim of the work is to evaluate the influence...... of the ashes were dry and sampled just after the incineration, whereas one ash had a water content of 15%, because the ash was sprayed with water to avoid dust during ash handling at the incineration plant. Regardless of replacing cement or sand with WAs, the compressive strength decreased compared...... to a reference without ash, however, the decrease was small for two of the ashes. Using the ash with the high LoI resulted in significantly lower compressive strength compared to the other two ashes. The mortar samples with two of the ashes (with low LoI) had qualities, which were very encouraging in order...

  6. The application of modified hydrotalcites as chloride scavengers and inhibitor release agents in cement mortars

    NARCIS (Netherlands)

    Yang, Z.; Fischer, H.; Polder, R.B.

    2014-01-01

    Owing to the unique molecular structure and high ion exchange capacity, hydrotalcites are believed to have a potential to be modified and tailor-made as an active component of concrete. In this paper, two types of modified hydrotalcites (MHT-pAB and MHT-NO2) were incorporated into cement mortars

  7. Determination of isothermal unsaturated capillary flow in high performance cement mortars by NMR imaging

    NARCIS (Netherlands)

    Hazrati, K.; Pel, L.; Marchand, J.; Kopinga, K.; Pigeon, M.

    2002-01-01

    The time-dependent liquid water distribution in cement mortar mixtures during water absorption was determined using a proton nuclear magnetic resonance imaging (NMRI) technique. The variation of the material water diffusion coefficient with the water content was established on the basis of these

  8. INFLUENCE OF SILICEOUS AND CALCAREOUS FLY-ASHES ON PROPERTIES OF CEMENT MORTARS

    Directory of Open Access Journals (Sweden)

    Gabriela Monika Rutkowska

    2016-09-01

    Full Text Available Care of the environment in accordance with the principles of sustainable development introduces the possibility and need for waste recycling. Construction and building industries have the greatest potential for reuse of waste. The article presents the results of investigations of cement mortars – tests of compressive and tensile strength after 28 and 56 days of curing – for normative mortars and mortars containing fly ashes – calcareous and siliceous ash – in their composition. To make the samples, the Portland cement CEM I 32,5 R, 42,5R and natural aggregate with graining of 0–2 mm were used. Concrete with siliceous and calcareous admixtures was made in six lots where the ash was added in the quantity of 2%, 5%, 10% of the cement mass or the 2%, 5%, 10% of cement was replaced by ashes. After the tests, it was stated that the siliceous fly-ash admixture increases the compressive and bending strength in comparison to the mortars with the calcareous ash admixtures.

  9. Determination of Chlorinated Solvent Sorption by Porous Material-Application to Trichloroethene Vapor on Cement Mortar.

    Science.gov (United States)

    Musielak, Marion; Brusseau, Mark L; Marcoux, Manuel; Morrison, Candice; Quintard, Michel

    2014-08-01

    Experiments have been performed to investigate the sorption of trichloroethene (TCE) vapor by concrete material or, more specifically, the cement mortar component. Gas-flow experiments were conducted using columns packed with small pieces of cement mortar obtained from the grinding of typical concrete material. Transport and retardation of TCE at high vapor concentrations (500 mg L -1 ) was compared to that of a non-reactive gas tracer (Sulfur Hexafluoride, SF6). The results show a large magnitude of retardation (retardation factor = 23) and sorption (sorption coefficient = 10.6 cm 3 g -1 ) for TCE, compared to negligible sorption for SF6. This magnitude of sorption obtained with pollutant vapor is much bigger than the one obtained for aqueous-flow experiments conducted for water-saturated systems. The considerable sorption exhibited for TCE under vapor-flow conditions is attributed to some combination of accumulation at the air-water interface and vapor-phase adsorption, both of which are anticipated to be significant for this system given the large surface area associated with the cement mortar. Transport of both SF6 and TCE was simulated successfully with a two-region physical non-equilibrium model, consistent with the dual-medium structure of the crushed cement mortar. This work emphasizes the importance of taking into account sorption phenomena when modeling transport of volatile organic compounds through concrete material, especially in regard to assessing vapor intrusion.

  10. ALKALI-ACTIVATED CEMENT MORTARS CONTAINING RECYCLED CLAY-BASED CONSTRUCTION AND DEMOLITION WASTE

    Directory of Open Access Journals (Sweden)

    F. Puertas

    2015-09-01

    Full Text Available The use of clay-based waste as an aggregate for concrete production is an amply studied procedure. Nonetheless, research on the use of this recycled aggregate to prepare alkaline cement mortars and concretes has yet to be forthcoming. The present study aimed to determine: the behaviour of this waste as a pozzolan in OPC systems, the mechanical strength in OPC, alkali-activated slag (AAS and fly ash (AAFA mortars and the effect of partial replacement of the slag and ash themselves with ground fractions of the waste. The pozzolanic behaviour of clay-based waste was confirmed. Replacing up to 20 % of siliceous aggregate with waste aggregate in OPC mortars induced a decline in 7 day strength (around 23 wt. %. The behaviour of waste aggregate in AAMs mortars, in turn, was observed to depend on the nature of the aluminosilicate and the replacement ratio used. When 20 % of siliceous aggregate was replaced by waste aggregate in AAS mortars, the 7 day strength values remained the same (40 MPa. In AAFA mortars, waste was found to effectively replace both the fly ash and the aggregate. The highest strength for AAFA mortars was observed when they were prepared with both a 50 % replacement ratio for the ash and a 20 % ratio for the aggregate.

  11. Fine natural aggregate replacement for sandy residue from itabirite exploitation in Portland cement mortar

    International Nuclear Information System (INIS)

    Melo, V.A.R.; Freire, C.B.; Pereira Junior, S.S.; Lameiras, F.S.; Tello, C.C.O.

    2011-01-01

    The fine natural aggregates are a material largely used by the civil construction for mortar and concrete production. Due to tightening legal restrictions imposed on their extraction, alternative materials are being considered. The use of sandy residue from BIF (banded iron formations) exploitation was investigated. It requires their grinding and flotation to concentrate iron oxides. Large amounts of sandy residue composed of quartz and iron oxides are generated in this process. The sandy residue was characterized relative to mineralogical composition, particle size distribution, presence of organic impurities, and particle shape. Mortar formulations were prepared by varying the type of cement, the cement to aggregate proportion and the water/cement ratio (a/c). The results of viscosity and density of fresh mortar, setting time, and compressive strength are presented. Compressive strength up to 19.5 MPa at 28 days were achieved with the use of cement CPV, a/c ratio of 0.80 and cement:aggregate proportion of 1:2. The results demonstrate the technical feasibility of using sandy residue as fine aggregate. (author)

  12. Correlating cement characteristics with rheology of paste

    International Nuclear Information System (INIS)

    Vikan, H.; Justnes, H.; Winnefeld, F.; Figi, R.

    2007-01-01

    The influence of cement characteristics such as cement fineness and clinker composition on the 'flow resistance' measured as the area under the shear stress-shear rate flow curve has been investigated. Three different types of plasticizers namely naphthalene sulphonate-formaldehyde condensate, polyether grafted polyacrylate, and lignosulphonate have been tested in this context on 6 different cements. The flow resistance correlated well with the cement characteristic (Blaine.{d.cC 3 A + [1 - d].C 3 S}) where the factor d represents relative reactivity of cubic C 3 A and C 3 S while cC 3 A and C 3 S represent the content of these minerals. It was found to be either a linear or exponential function of the combined cement characteristic depending on plasticizer type and dosage. The correlation was valid for a mix of pure cement and cement with fly ash, limestone filler (4%), as well as pastes with constant silica fume dosage, when the mineral contents were determined by Rietveld analysis of X-ray diffractograms

  13. Estimation and measurement of porosity change in cement paste

    International Nuclear Information System (INIS)

    Lee, Eunyong; Jung, Haeryong; Kwon, Ki-jung; Kim, Do-Gyeum

    2011-01-01

    Laboratory-scale experiments were performed to understand the porosity change of cement pastes. The cement pastes were prepared using commercially available Type-I ordinary Portland cement (OPC). As the cement pastes were exposed in water, the porosity of the cement pastes sharply increased; however, the slow decrease of porosity was observed as the dissolution period was extended more than 50 days. As expected, the dissolution reaction was significantly influenced by w/c ratio and the ionic strength of solution. A thermodynamic model was applied to simulate the porosity change of the cement pastes. It was highly influenced by the depth of the cement pastes. There was porosity increase on the surface of the cement pastes due to dissolution of hydration products, such as portlandite, ettringite, and CSH. However, the decrease of porosity was estimated inside the cement pastes due to the precipitation of cement minerals. (author)

  14. Effect of Copolymer Latexes on Physicomechanical Properties of Mortar Containing High Volume Fly Ash as a Replacement Material of Cement

    Directory of Open Access Journals (Sweden)

    El-Sayed Negim

    2014-01-01

    Full Text Available This paper investigates the physicomechanical properties of mortar containing high volume of fly ash (FA as partial replacement of cement in presence of copolymer latexes. Portland cement (PC was partially replaced with 0, 10, 20, 30 50, and 60% FA. Copolymer latexes were used based on 2-hydroxyethyl acrylate (2-HEA and 2-hydroxymethylacrylate (2-HEMA. Testing included workability, setting time, absorption, chemically combined water content, compressive strength, and scanning electron microscopy (SEM. The addition of FA to mortar as replacement of PC affected the physicomechanical properties of mortar. As the content of FA in the concrete increased, the setting times (initial and final were elongated. The results obtained at 28 days of curing indicate that the maximum properties of mortar occur at around 30% FA. Beyond 30% FA the properties of mortar reduce and at 60% FA the properties of mortar are lower than those of the reference mortar without FA. However, the addition of polymer latexes into mortar containing FA improved most of the physicomechanical properties of mortar at all curing times. Compressive strength, combined water, and workability of mortar containing FA premixed with latexes are higher than those of mortar containing FA without latexes.

  15. Effect of copolymer latexes on physicomechanical properties of mortar containing high volume fly ash as a replacement material of cement.

    Science.gov (United States)

    Negim, El-Sayed; Kozhamzharova, Latipa; Gulzhakhan, Yeligbayeva; Khatib, Jamal; Bekbayeva, Lyazzat; Williams, Craig

    2014-01-01

    This paper investigates the physicomechanical properties of mortar containing high volume of fly ash (FA) as partial replacement of cement in presence of copolymer latexes. Portland cement (PC) was partially replaced with 0, 10, 20, 30 50, and 60% FA. Copolymer latexes were used based on 2-hydroxyethyl acrylate (2-HEA) and 2-hydroxymethylacrylate (2-HEMA). Testing included workability, setting time, absorption, chemically combined water content, compressive strength, and scanning electron microscopy (SEM). The addition of FA to mortar as replacement of PC affected the physicomechanical properties of mortar. As the content of FA in the concrete increased, the setting times (initial and final) were elongated. The results obtained at 28 days of curing indicate that the maximum properties of mortar occur at around 30% FA. Beyond 30% FA the properties of mortar reduce and at 60% FA the properties of mortar are lower than those of the reference mortar without FA. However, the addition of polymer latexes into mortar containing FA improved most of the physicomechanical properties of mortar at all curing times. Compressive strength, combined water, and workability of mortar containing FA premixed with latexes are higher than those of mortar containing FA without latexes.

  16. Physico-Chemical studies on irradiated polymer-reinforcement cement mortar composites

    International Nuclear Information System (INIS)

    Younes, M.M.

    2001-01-01

    The reinforced concrete suffers from corrosion by several salts, acids or alkalies and physico-mechanical properties are greatly affected. This leads to reduce the life of reinforced concrete structure. The present investigation deals with a comparison of corrosion presentation efficiency and passivity retention of reinforcement steel coated with methylethyl and propyl inhibitors which are prepared by using γ radiation and non-coated steel embedded in γ -induced polyester cement mortar composites. From the results of these studies several conclusions could be derived and these are summarized as follows: 1- The time required to reach passivation for coated steel embedded in the mortar after soaking in tap water for 28 days lies within the range 5-15 minutes; whereas, the time required to reach passivation for steel embedded in the polyester cement mortar composites is very short (1 minute). This result is related to the presence of copolymerized polyester in the pore system of the specimens. 2- The time required to reach passivation for steel coated by inhibitors in the mortar specimens after curing in tap water for 6 months is lower than that of non -coated steel embedded in the mortar specimens cured at the same conditions. 3- A relatively high degree of corrosion inhibition was obtained for the steel embedded in polyester-cement mortar composites after curing in sea water for 28 days, the time required to reach passivation is considered as moderate in the case of methyl and ethyl inhibitors the time to passivation (T.T.P.) = 9 minutes and the degree of inhibition of steel coated with the propyl inhibitor is comparatively low (T.T.P.=21 minutes)

  17. Effect of Polysiloxanes on Roughness and Durability of Basalt Fibres–Reinforced Cement Mortar

    Directory of Open Access Journals (Sweden)

    Danuta Barnat-Hunek

    2018-04-01

    Full Text Available The influence of roughness and the way it affects the adhesion properties and surface free energy (SFE of polysiloxanes hydrophobised basalt fibres–reinforced cement mortars were determined in this article. The physical properties of mortars were investigated in the experimental part, which also explored the impact of hydrophobisation and basalt fibres (BF addition on SFE, frost resistance, contact angle (CA, and roughness. A device capable of calculating all parameters was used to indicate the surface roughness and 3D topography. Prior to and after conducting surface and weight hydrophobisation, the contact angle of mortars was specified. Subsequently, it was used for carrying out SFE calculation by means of Neumann’s method, enabling us to characterize the adhesion properties and wettability of mortars. The research indicated that the surface roughness was substantially decreased, in turn raising the frost resistance. The corrosion resistance drops when the surface roughness, water absorption, and number of fibres in the mortar increase. The SEM images presenting the structure of polysiloxane coating and mortars were provided.

  18. Elementary characterization of samples of Portland cement, natural gypsum and phosphogypsum mortars from Brazil

    Energy Technology Data Exchange (ETDEWEB)

    Narloch, Danielle Cristine; Paschuk, Sergei Anatolyevich; Corrêa, Janine Nicolosi; Torres, Catarina Alzira Peddis; Mazer, Wellington; Macioski, Gustavo [Universidade Tecnologica Federal do Parana (UTFPR), PR (Brazil); Lara, Alessandro [Universidade de Sao Paulo (USP), SP (Brazil). Departamento de Fisica; Casali, Juliana Machado, E-mail: janine_nicolosi@hotmail.com, E-mail: alellara@hotmail.com, E-mail: jucasali@gmail.com [Instituto Federal de Santa Catarina (IFSC), Florianópolis, SC (Brazil)

    2017-07-01

    Portland cement, the basic ingredient of concrete and is manufactured by crushing, milling and proportioning limestone, sand, clay, iron ore and secondary materials such as shells, chalk or marl combined with shale slate or blast furnace slag, fly ash, gypsum, phosphogypsum, and some others. Evaluating the physical and mineralogical characteristics of the cement and its chemical composition is essential to establish the quality of the product. Therefore, the objective of this work was to characterize and quantify the most common chemical elements in the samples of Brazilian Portland cement, natural gypsum, and phosphogypsum mortars by means of X-ray dispersive energy spectroscopy (EDXRF), as well as to evaluate the strength of these mortars. For analysis of the compressive strength, initially prepared samples were submitted to a destructive mechanical test. Subsequently samples were milled and compacted to form thin tablets, which were submitted to the EDXRF analysis. The qualitative and quantitative analyzes showed that for phosphogypsum mortar the largest mass fractions were found of 49.8±2.5% (Si), 24.66±0.96% (S) and 22.10±0.42% (Ca). For gypsum mortar those values were found of 43.41±0.45% (Ca), 33.8 ± 0.8% (S) and 18.9±1.2% (Si), respectively; and for Portland cement mortar, the predominant elements in those samples have the mass fractions of 64.20±0.52% (Ca) and 27.3±1.5% (Si). The results showed that obtained values of mass fraction of the elements Si, S, K, Ca, Ti, Fe are in rather good agreement with quantities indicated for manufacture. Besides, gypsum and phosphogypsum presented almost the same composition and compressive strength. (author)

  19. Elementary characterization of samples of Portland cement, natural gypsum and phosphogypsum mortars from Brazil

    International Nuclear Information System (INIS)

    Narloch, Danielle Cristine; Paschuk, Sergei Anatolyevich; Corrêa, Janine Nicolosi; Torres, Catarina Alzira Peddis; Mazer, Wellington; Macioski, Gustavo; Lara, Alessandro

    2017-01-01

    Portland cement, the basic ingredient of concrete and is manufactured by crushing, milling and proportioning limestone, sand, clay, iron ore and secondary materials such as shells, chalk or marl combined with shale slate or blast furnace slag, fly ash, gypsum, phosphogypsum, and some others. Evaluating the physical and mineralogical characteristics of the cement and its chemical composition is essential to establish the quality of the product. Therefore, the objective of this work was to characterize and quantify the most common chemical elements in the samples of Brazilian Portland cement, natural gypsum, and phosphogypsum mortars by means of X-ray dispersive energy spectroscopy (EDXRF), as well as to evaluate the strength of these mortars. For analysis of the compressive strength, initially prepared samples were submitted to a destructive mechanical test. Subsequently samples were milled and compacted to form thin tablets, which were submitted to the EDXRF analysis. The qualitative and quantitative analyzes showed that for phosphogypsum mortar the largest mass fractions were found of 49.8±2.5% (Si), 24.66±0.96% (S) and 22.10±0.42% (Ca). For gypsum mortar those values were found of 43.41±0.45% (Ca), 33.8 ± 0.8% (S) and 18.9±1.2% (Si), respectively; and for Portland cement mortar, the predominant elements in those samples have the mass fractions of 64.20±0.52% (Ca) and 27.3±1.5% (Si). The results showed that obtained values of mass fraction of the elements Si, S, K, Ca, Ti, Fe are in rather good agreement with quantities indicated for manufacture. Besides, gypsum and phosphogypsum presented almost the same composition and compressive strength. (author)

  20. The comparison of properties and cost of material use of natural rubber and sand in manufacturing cement mortar for construction sub-base layer

    Science.gov (United States)

    Rahman, R.; Nemmang, M. S.; Hazurina, Nor; Shahidan, S.; Khairul Tajuddin Jemain, Raden; Abdullah, M. E.; Hassan, M. F.

    2017-11-01

    The main issue related to this research was to examine the feasibility of natural rubber SMR 20 in the manufacturing of cement mortar for sub-base layer construction. Subbase layers have certain functions that need to be fulfilled in order to assure strong and adequate permeability of pavement performance. In a pavement structure, sub-base is below the base and serves as the foundation for the overall pavement structure, transmitting traffic loads to the sub-grade and providing drainage. Based on this research, the natural rubber, SMR 20 was with the percentages of 0%, 5%, 10% and 15% to mix with sand in the manufacture of the cement mortar. This research describes some of the properties and cost of the materials for the natural rubber and sand in cement mortar manufacturing by laboratory testing. Effects of the natural rubber replacement on mechanical properties of mortar were investigated by laboratory testing such as compressive strength test and density. This study obtained the 5% of natural rubber replaced in sand can achieved the strength of normal mortar after 7 days and 28 days. The strength of cement mortar depends on the density of cement mortar. According to the cost of both materials, sand shows the lower cost in material for the cement mortar manufacturing than the uses of natural rubber. Thus, the convectional cement mortar which used sand need lower cost than the modified rubber cement mortar and the most economical to apply in industrial. As conclusion, the percentage of 5% natural rubber in the cement mortar would have the same with normal cement mortar in terms of the strength. However, in terms of the cost of the construction, it will increase higher than cost of normal cement mortar production. So that, this modified cement mortar is not economical for the road sub-base construction.

  1. Alkali binding in hydrated Portland cement paste

    NARCIS (Netherlands)

    Chen, Wei; Brouwers, Jos

    2010-01-01

    The alkali-binding capacity of C–S–H in hydrated Portland cement pastes is addressed in this study. The amount of bound alkalis in C–S–H is computed based on the alkali partition theories firstly proposed by Taylor (1987) and later further developed by Brouwers and Van Eijk (2003). Experimental data

  2. Basic study of water-cement ratio evaluation for fresh mortar using an ultrasonic measurement technique

    International Nuclear Information System (INIS)

    Hamza Haffies Ismail; Murata, Yorinobu

    2009-01-01

    The objective of this research is for the basic study of ultrasonic evaluation method for the determination of the water-cement-ratio (W/C) in fresh concrete at the early age of hardening. Water-cement ratio is a important parameter to evaluate the strength of concrete for concrete construction. Using an ultrasonic pulse measurement technique, wave velocity and frequency variations depend on the age of concrete during hardening process could be evaluated. As a sample test, fresh mortar of water-cement ratio of 40 %, 50% and 60 % was poured into cylindrical plastic mould form (φ100 mm x 50 mm). For an ultrasonic pulse wave transmission technique, two wide band ultrasonic transducers were set on the top and bottom surface of mortar, and start measuring from 10 minutes after pouring water until 60 minutes of 5 minutes of intervals. As a result, it was confirmed that wave velocity and center frequency were changed with the age of mortar depends on the water-cement ratio. (author)

  3. Porosity and liquid absorption of cement paste

    DEFF Research Database (Denmark)

    Krus, M.; Hansen, Kurt Kielsgaard; Kunzel, H. M.

    1997-01-01

    be a slowing-down effect which is related to water because the absorption of organic liquids, such as hexane, is quite normal. Measurements of the porosity of hardened cement paste determined by helium pycnometry and water saturation show that water molecules can enter spaces in the microstructure which...... are not accessible to the smaller helium atoms. Considering the results of dilatation tests both before and after water and hexane saturation, it seems possible that a contraction of capillary pores due to moisture-related swelling of the cement gel leads to the non-linear water absorption over the square root...

  4. Composite cement mortars based on marine sediments and oyster shell powder

    Directory of Open Access Journals (Sweden)

    Ez-zaki, H.

    2016-03-01

    Full Text Available Additions of dredged marine sediments and oyster shell powder (OS as cement substitute materials in mortars are examined by several techniques. The sediments have high water and chloride contents and calcite, quartz, illite and kaolinite as principal minerals. The OS powders are entirely composed of calcium carbonate and traces of other impurities. Four mixtures of treated sediments and OS powders at 650 °C and 850 °C are added to Portland cement at 8%, 16% and 33% by weight. The hydration of composite pastes is followed by calorimetric tests, the porosity accessible to water, the bulk density, the permeability to gas, the compressive strength and the accelerated carbonation resistance are measured. In general, the increase of addition amounts reduced the performance of mortars. However, a reduction of gas permeability was observed when the addition was up to 33%. Around 16% of addition, the compressive strength and carbonation resistance were improved.En este trabajo se ha valorado la sustitución de cemento en morteros por sedimentos marinos dragados y polvo de concha de ostra (OS. Los sedimentos tienen altos contenidos de agua, cloruros, calcita, cuarzo, illita y caolinita como minerales principales. Los polvos OS están compuestos de carbonato cálcico y trazas de otras impurezas. Se añadieron a un cemento Portland, cuatro mezclas de los sedimentos y polvos de OS tratados a 650 °C y 850 °C en proporciones del 8%, 16% y 33% en peso. La hidratación de pastas se estudió a través de calorimetría. Se estudió además la porosidad accesible al agua, densidad aparente, permeabilidad al gas, resistencia a compresión y carbonatación acelerada. En general, un aumento en la adición produjo una reducción del rendimiento de los morteros. Se observó, sin embargo, una reducción de la permeabilidad a los gases con porcentajes de adición de hasta el 33%. Con valores del 16% de sustitución, mejoraron las resistencias mecánicas y la

  5. Effect of Chlorides on Conductivity and Dielectric Constant in Hardened Cement Mortar: NDT for Durability Evaluation

    Directory of Open Access Journals (Sweden)

    Sunkook Kim

    2016-01-01

    Full Text Available Dielectric constant and conductivity, the so-called EM properties (electromagnetic, are widely adopted for NDT (Nondestructive Technique in order to detect damage or evaluate performance of concrete without damage to existing RC (reinforced concrete. Among deteriorating agents, chloride ion is considered as one of the most critical threats due to rapid penetration and direct effect on steel corrosion. In the work, cement mortar samples with 3 w/c (water-to-cement ratios and 4 levels of chloride addition are considered. Conductivity and dielectric constant are measured in the normal frequency range. They increase with strength of mortar and more chloride ions due to denser pore formation. Furthermore, the behaviors of measured EM property are investigated with carbonation velocity and strength, which shows an attempt of application to durability evaluation through EM measurement.

  6. Effect of Modified Rubber Particles Mixing Amount on Properties of Cement Mortar

    Directory of Open Access Journals (Sweden)

    Gang Xue

    2017-01-01

    Full Text Available The crumb rubber cement mortar is prepared by the crumb rubber aggregates in 60 mesh which are modified by 1% polyvinyl alcohol (PVA solution. Some mechanical properties of cement mortar with different crumb rubber aggregate amounts are researched including compressive strength, flexural strength, the ratio of compressive strength to flexural strength, impact resistance, and dry contraction percentage. In our tests, we consider six kinds of the rubber contents, 0%, 7.5%, 15%, 19%, 22.5%, and 30%, respectively. The optimal mixing amount of crumb rubber is determined by measuring three indices, the ratio of compressive strength to flexural strength, impact resistance, and dry contraction percentage. It is shown by test that the ratio of compressive strength to flexural strength is the smallest when the mixing amount of rubber is 19%; meanwhile high impact resistance and rational drying shrinkage are observed. The optimal mixing amount of the rubber particles is 19% determined by this test.

  7. Characterization and modeling of major constituent equilibrium chemistry of a blended cement mortar

    International Nuclear Information System (INIS)

    Arnold, J.; Kosson, D. S.; Brown, K. G.; Garrabrants, A. C.; Meeussen, J. C. L.; Van Der Sloot, H. A.

    2013-01-01

    Cementitious materials containing ground granulated iron blast furnace slag and coal combustion fly ash as admixtures are being used extensively for nuclear waste containment applications. Whereas the solid phases of ordinary Portland cement (OPC) have been studied in great detail, the chemistry of cement, fly ash and slag blends has received relatively less study. Given that OPC is generally more reactive than slag and fly ash, the mineralogy of OPC provides a logical starting point for describing the major constituent chemistry of blended cement mortars. To this end, a blended cement mortar containing Portland cement, granulated blast furnace slag, fly ash and quartz sand was modeled using a set of solid phases known to form in hydrated OPC with the geochemical speciation solver LeachXS/ORCHESTRA. Comparison of modeling results to the experimentally determined pH-dependent batch leaching concentrations (USEPA Method 1313) indicates that major constituent concentrations are described reasonably well with the Portland cement mineral set; however, modeled and measured aluminum concentrations differ greatly. Scanning electron microscopic analysis of the mortar reveals the presence of Al-rich phyllosilicate minerals heretofore unreported in similar cementitious blends: kaolinite and potassic phyllosilicates similar in composition to illite and muscovite. Whereas the potassic phyllosilicates are present in the quartz sand aggregate, the formation of kaolinite appears to be authigenic. The inclusion of kaolinite in speciation modeling provides a substantially improved description of the release of Al and therefore, suggests that the behavior of phyllosilicate phases may be important for predicting long-term physico-chemical behavior of such systems. (authors)

  8. Nanofibrillated cellulose (NFC) as a potential reinforcement for high performance cement mortar composites

    OpenAIRE

    Ardanuy Raso, Mònica; Claramunt Blanes, Josep; Arévalo Peces, Raquel; Parés Sabatés, Ferran; Aracri, Elisabetta; Vidal Lluciá, Teresa

    2012-01-01

    In this work, nanofibrillated cellulose (NFC) has been evaluated as a potential reinforcement for cement mortar composites. Two types of vegetable fibres with different composition and properties (cellulose content and microfibrillar angle), sisal, and cotton linters pulps, were initially characterized in order to assess their reinforcement capability. Sisal pulp was found to be most suitable as reinforcement for their brittle cementitious matrix. Nanofibrillated cellulose was produced by th...

  9. Industrial Wastes as Alternative Mineral Addition in Portland Cement and as Aggregate in Coating Mortars

    OpenAIRE

    Oliveira, Kamilla Almeida; Nazário, Bruna Inácio; Oliveira, Antonio Pedro Novaes de; Hotza, Dachamir; Raupp-Pereira, Fabiano

    2017-01-01

    This paper presents an evaluation study of wastes from pulp and paper as well as construction and demolition industries for application in cement-based materials. The alternative raw materials were used as a source of calcium carbonate (CaCO3) and as pozzolanic material (water-reactive SiO2) in partial replacement of Portland cement. In addition to the hydraulic binder, coating mortars were composed by combining the pulp and paper fluidized bed sand residue with construction and demolition wa...

  10. Effect of colloidal nano-silica on the mechanical and physical behaviour of waste-glass cement mortar

    International Nuclear Information System (INIS)

    Aly, M.; Hashmi, M.S.J.; Olabi, A.G.; Messeiry, M.; Abadir, E.F.; Hussain, A.I.

    2012-01-01

    Highlights: → Glass powder (GP) and nano-silica (CS) were used as a partial cement replacement in cement mortar (CM). → No damaging effect can be detected due to the reaction between GP and CM with particle size up to 75 μm. → Hybrid combination of GP/CS greatly improved mechanical properties and microstructure of CM. -- Abstract: This paper presents a laboratory study of the properties of colloidal nano-silica (CS)/waste glass cement composites. The microstructure, alkali-silica reaction (ASR), and the mechanical properties of cement mortars containing waste glass powder (WG) as a cement replacement with and without CS are investigated and compared with plain mortar. In addition, the hydration of cement compounds was followed by differential thermal analysis (DTA), thermogravimetric analysis (TGA), and X-ray diffraction (XRD). The results show that incorporation of WG has a positive effect on the mechanical properties of cement mortars especially when CS is presented. In addition, the DTA/TGA results and XRD analysis show a reduction in the calcium hydroxide (CH) content in mortars with both WG and a hybrid combination of WG and CS. This confirms the improvement of mechanical properties and the occurrence of the pozzolanic reaction after 28 days of hydration.

  11. Changes in water absorptivity of slag based cement mortars exposed to sulphur-oxidising A. thiooxidans bacteria

    Science.gov (United States)

    Estokova, A.; Smolakova, M.; Luptakova, A.; Strigac, J.

    2017-10-01

    Water absorptivity is heavily influenced by the volume and connectivity of pores in the pore network of cement composites and has been used as an important parameter for quantifying their durability. To improve the durability and permeability of mortars, various mineral admixtures such as furnace slag, silica fume or fly ash are added into the mortar and concrete mixtures. These admixtures provide numerous important advantages such as corrosion control, improvement of mechanical and physical properties and better workability. This study investigated the changes in absorptivity of cement mortars with different amounts of mineral admixture, represented by granulated blast furnace slag, under aggressive bacterial influence. The water absorptivity of mortars specimens exposed to sulphur-oxidising bacteria A. thiooxidans for the period of 3 and 6 months has changed due to bio-corrosion-based degradation process. The differences in water absorptivity in dependence on the mortars composition have been observed.

  12. Comparison of creep of the cement pastes included fly ash

    Directory of Open Access Journals (Sweden)

    Padevět Pavel

    2017-01-01

    Full Text Available The paper is devoted to comparison of creep of cement pastes containing fly ash admixture. The size of creep in time depends on the amount of components of the cement paste. Attention is paid to the content of classical fly ash in cement paste and its impact on the size of creep. The moisture of cement pastes is distinguished because it significantly affects the rheological properties of the material.

  13. Determination of the chloride diffusion coefficient in blended cement mortars

    NARCIS (Netherlands)

    Elfmarkova, V.; Spiesz, P.R.; Brouwers, H.J.H.

    2015-01-01

    The rapid chloride migration test (RCM) is a commonly used accelerated test for the determination of the chloride diffusion coefficient in concrete. Nevertheless, the initial development and further experience with the RCM test concern mainly the ordinary Portland cement system. Therefore, the

  14. Studies on potential of Portland cement mortar for binding of ...

    Indian Academy of Sciences (India)

    Paramalinggam Thanalechumi

    10%, and basic (pH [ 7) curing solution was found to be better than water for curing purposes. It is concluded ... regulations on waste management by the Department of. Environment [8]. .... cement, sand and sediment [16, 17]. The major ...

  15. Evaluation of nitric and acetic acid resistance of cement mortars containing high-volume black rice husk ash.

    Science.gov (United States)

    Chatveera, B; Lertwattanaruk, P

    2014-01-15

    This paper presents the performance of cement mortar containing black rice husk ash (BRHA) under nitric and acetic acid attacks. The BRHA, collected from an electrical generating power plant that uses rice husk as fuel, was ground using a grinding machine. The compressive strength loss, weight loss, and expansion of mortars under nitric and acetic acid attack were investigated. The test results of BRHA properties in accordance with the ASTM C 618 standard found that the optimal grinding time was 4 h as this achieved a Blaine fineness of 5370 cm(2)/g. For parametric study, BRHA were used as a Portland cement Type 1 replacement at the levels of 0%, 10%, 20%, 30%, 40%, and 50% by weight of binder. The water-to-binder ratios were 0.55, 0.60, and 0.65. From test results, when the percentage replacements of BRHA in cement increased, it was observed that the strength loss and weight loss of mortars containing BRHA under acetic acid attack were higher than those of the mortars against nitric acid attack. It was found that, of the various BHRA mortars, the strength loss and weight loss due to nitric and acetic acid attacks were the lowest in the mortar with 10% BRHA replacement. For 10%, 20% and 30% BRHA replacements, the rate of expansion of the BRHA mortar decreased when compared with the control mortar. For the mortars with other percentage replacements of BRHA, the rate of expansion increased. Furthermore, the effective water-to-binder ratios of control and BRHA mortars were the primary factor for determining the durability of mortar mixed with BRHA. Copyright © 2013 Elsevier Ltd. All rights reserved.

  16. Rheology of Carbon Fibre Reinforced Cement-Based Mortar

    International Nuclear Information System (INIS)

    Banfill, Phillip F. G.; Starrs, Gerry; McCarter, W. John

    2008-01-01

    Carbon fibre reinforced cement based materials (CFRCs) offer the possibility of fabricating 'smart' electrically conductive materials. Rheology of the fresh mix is crucial to satisfactory moulding and fresh CFRC conforms to the Bingham model with slight structural breakdown. Both yield stress and plastic viscosity increase with increasing fibre length and volume concentration. Using a modified Viskomat NT, the concentration dependence of CFRC rheology up to 1.5% fibre volume is reported

  17. Rheology of Carbon Fibre Reinforced Cement-Based Mortar

    Science.gov (United States)

    Banfill, Phillip F. G.; Starrs, Gerry; McCarter, W. John

    2008-07-01

    Carbon fibre reinforced cement based materials (CFRCs) offer the possibility of fabricating "smart" electrically conductive materials. Rheology of the fresh mix is crucial to satisfactory moulding and fresh CFRC conforms to the Bingham model with slight structural breakdown. Both yield stress and plastic viscosity increase with increasing fibre length and volume concentration. Using a modified Viskomat NT, the concentration dependence of CFRC rheology up to 1.5% fibre volume is reported.

  18. Estimating the chloride transport in cement paste

    Directory of Open Access Journals (Sweden)

    Princigallo, A.

    2012-06-01

    Full Text Available A method was developed to measure the diffusion coefficient of chloride ions in cement paste based on an analytical solution to Fick’s 2nd law in a cylindrical coordinate system. This natural method yielded diffusivity results within as little as a month. Testing time was reduced by exploiting the three-dimensional inward flux in the specimen. In an attempt to determine the saturation concentration, dense portland cement pastes were exposed to a concentrated chloride solution. The method proved to be useful for exploring cement hydration-induced changes in the diffusion coefficient of cement paste.

    Se ha desarrollado un método para medir el coeficiente de difusión de los iones cloruro en la pasta de cemento, partiendo de una aplicación analítica de la segunda ley de Fick en un sistema de coordinadas cilíndrico. Este método, que es natural, demostró ser capaz de producir resultados de difusividad en tan solo un mes. Se consiguió reducir el tiempo de ensayo mediante el aprovechamiento de la tridimensionalidad del flujo desde el exterior al interior de la probeta. A fin de determinar la concentración de saturación, se sometieron las pastas de cemento Portland a una disolución de cloruros concentrada. Este método resultó ser útil en el estudio de los cambios del coeficiente de difusión de la pasta de cemento provocados por las reacciones de hidratación que tienen lugar en esta.

  19. Rheological study of self-compacting mortars based on ternary cements

    Directory of Open Access Journals (Sweden)

    Elhadja Dada

    2018-01-01

    Full Text Available Self-compacting concrete (SCC is able to provide the ability to be easily implemented without vibration and to achieve spectacular structures, by its high fluidity and its rheological stability. By against its formulation requires a large volume of cement, which is necessary to allow its flow. The current environmental considerations lead to reduce the production of clinker however, it is essential to use cementitious additions to replace cement, because of their high availability and their moderate price. Furthermore, their use contributes in a simple and economical way to solve the problems related to the environment. The objective of our work is to study the effects of the incorporation of mineral additions such as: blast furnace slag of El-Hadjar (BFS, and marble powder (MP on the rheological parameters of selfcompacting mortars developed in different combinations in ternary system with a substitution rate ranging from 20% to 60%. According to this study, it been found that the substitution of cement by blast furnace slag and marble powder has negatively affected the rheological behavior of the mixtures. In addition, a considerable decrease in the rheological parameters has been achieved with a substitution rate of 20% of slag and 30% of marble powder. As well as an improvement of workability has been proven to self-compacting mortars and this is due to the increase of ternary cement replacement rate by marble powder from 20% to 30%.

  20. The effect of different surfactants/plastisizers on the electrical behavior of CNT nano-modified cement mortars

    Science.gov (United States)

    Dalla, P. T.; Alafogianni, P.; Tragazikis, I. K.; Exarchos, D. A.; Dassios, K.; Barkoula, N.-M.; Matikas, T. E.

    2015-03-01

    Cement-based materials have in general low electrical conductivity. Electrical conductivity is the measure of the ability of the material to resist the passage of electrical current. The addition of a conductive admixture such as Multi-Walled Carbon Nanotubes (MWCNTs) in a cement-based material increases the conductivity of the structure. This research aims to characterize nano-modified cement mortars with MWCNT reinforcements. Such nano-composites would possess smartness and multi-functionality. Multifunctional properties include electrical, thermal and piezo-electric characteristics. One of these properties, the electrical conductivity, was measured using a custom made apparatus that allows application of known D.C. voltage on the nano-composite. In this study, the influence of different surfactants/plasticizers on CNT nano-modified cement mortar specimens with various concentrations of CNTs (0.2% wt. cement CNTs - 0.8% wt. cement CNTs) on the electrical conductivity is assessed.

  1. Study of Experiment on Rock-like Material Consist of fly-ash, Cement and Mortar

    Science.gov (United States)

    Nan, Qin; Hongwei, Wang; Yongyan, Wang

    2018-03-01

    Study the uniaxial compression test of rock-like material consist of coal ash, cement and mortar by changing the sand cement ratio, replace of fine coal, grain diameter, water-binder ratio and height-diameter ratio. We get the law of four factors above to rock-like material’s uniaxial compression characteristics and the quantitative relation. The effect law can be sum up as below: sample’s uniaxial compressive strength and elasticity modulus tend to decrease with the increase of sand cement ratio, replace of fine coal and water-binder ratio, and it satisfies with power function relation. With high ratio increases gradually, the uniaxial compressive strength and elastic modulus is lower, and presents the inverse function curve; Specimen tensile strength decreases gradually with the increase of fly ash. By contrast, uniaxial compression failure phenomenon is consistent with the real rock common failure pattern.

  2. THE INFLUENCE OF JOINT GRINDING OF CEMENT AND COOPER SLAG ON MORTAR PROPERTIES

    Directory of Open Access Journals (Sweden)

    Kravtsov Aleksey Vladimirovich

    2016-08-01

    Full Text Available The problem of applying copper manufacturing waste locating in the Chelyabinsk region as a component of mixed is considered in this article. Application of mixed binder with superplasticizers, based on esters with carboxyl groups, have not sufficiently been studied by the present time due to the diversity of species and complexity of the chemical structure. This trend is current for today’s science because of the growing rates and scales of building production, in particular, of concrete works. Copper slag dumps located in the Ural Federal district haven’t been widely used in building production or in other industrial production by the present time. Efficient utilization of copper production waste materials will help to solve ecological problems in many regions of Russia. Structure formation period of cement stone based on mixed binder made of Portland cement and granulated cooper slag with application of superplasticizer is studied in the article. The authors present a thermal variation diagram of mortar based on mixed binder made of Portland cement and granulated cooper slag in the process of 21 hours of hardening under normal conditions and the results of ultrasound investigation of concrete structure formation period during 5 hours of hardening. The strength development process diagram of mortar based on mixed binder made of Portland cement and granulated cooper slag for 28 days of hardening under normal conditions and the research results of the compressive strength of concrete samples are shown in this article. The obtained characteristics don’t confirm the prospects of applying joint grinding for mortar with the observed kind of non-ferrous metallurgy waste. Also, the obtained results allow us to make a conclusion about little advantages of using this method of binder production. Copper slag can be more effectively used as a component of complex organic and mineral admixture for building production with different purposes and fields

  3. Microstructural characterization of phases and interfaces of Portland cement mortar using high resolution microscopy

    International Nuclear Information System (INIS)

    Barreto, M.F.O.; Brandao, P.R.G.

    2014-01-01

    In Portland cement mortars it is of paramount importance to investigate the bond strength between mortar and masonry by means of the study of interfaces and surfaces that make up the system mortar/ceramic block. In this work the aim was to characterize the chemical compositions, microstructures, surfaces and interfaces of mortars applied on ceramic blocks. Therefore, two important characterization tools were used: field-effect gun (FEG) scanning electron microscope (SEM) - FEI Quanta 200 with energy-dispersive (X-ray) spectrometer (EDS) and SEM system with EGF Nanofabrication FIB - FEI Quanta 3D FEG also with an EDS coupled. To date the results obtained from the research show that the characterization of cementitious materials with high resolution SEM is an important tool in the detection and differentiation of hydrated calcium silicates (CSH), calcium hydroxide (Ca(OH)2), ettringite and calcium carbonate by means of morphological, topographical and chemical data, thus providing extremely reliable as well as qualitative data from the structure of cementitious materials. (author)

  4. Microstructural characterization of phases and interfaces of Portland cement mortar using high resolution microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Barreto, M.F.O.; Brandao, P.R.G., E-mail: matheusfob@yahoo.com.br, E-mail: pbrandao@demin.ufmg.br [Universidade Federal de Minas Gerais (UFMG), MG (Brazil)

    2014-07-01

    In Portland cement mortars it is of paramount importance to investigate the bond strength between mortar and masonry by means of the study of interfaces and surfaces that make up the system mortar/ceramic block. In this work the aim was to characterize the chemical compositions, microstructures, surfaces and interfaces of mortars applied on ceramic blocks. Therefore, two important characterization tools were used: field-effect gun (FEG) scanning electron microscope (SEM) - FEI Quanta 200 with energy-dispersive (X-ray) spectrometer (EDS) and SEM system with EGF Nanofabrication FIB - FEI Quanta 3D FEG also with an EDS coupled. To date the results obtained from the research show that the characterization of cementitious materials with high resolution SEM is an important tool in the detection and differentiation of hydrated calcium silicates (CSH), calcium hydroxide (Ca(OH)2), ettringite and calcium carbonate by means of morphological, topographical and chemical data, thus providing extremely reliable as well as qualitative data from the structure of cementitious materials. (author)

  5. The Use of Fly Ash and Lime Sludge as Partial Replacement of Cement in Mortar

    Directory of Open Access Journals (Sweden)

    Vaishali Sahu

    2014-01-01

    Full Text Available The increased demand of drinking water and power has led huge generation of water treatment plant residue i.e. sludge and the thermal power plant by-product such as fly ash. Large quantities of sludge and fly ash are produced in India and disposed off by landfilling or dumping in and around sites. In this study fly ash and water softening sludge (lime sludge has been utilized in mortar. Two types of mortar (type I and II with four binder combinations have been tried. Binder I consists of 70% fly ash (FA and 30% lime sludge (LS , 0 % gypsum (G, binder II is 70% FA, 30% LS and 1% G, binder III is 50% FA, 30% LS and 20% cement and the binder IV is 40% FA, 40% LS with 20% cement. The effect of various combinations on strength has been discussed here. This paper outlines the composition of the composite material, method of preparation of mortar specimen, testing procedure and salient results thereof.

  6. Cement-base bearing pads mortar for connections in the precast concrete: study of surface roughness

    Directory of Open Access Journals (Sweden)

    M. K. El Debs

    Full Text Available Bearing pads are used in precast concrete connections to avoid concentrated stresses in the contact area between the precast elements. In the present research, the bearing pads are Portland cement mortar with styrene-butadiene latex (SB, lightweight aggregate (expanded vermiculite-term and short fibers (polypropylene, glass and PVA, in order to obtain a material with low modulus of elasticity and high tenacity, compared with normal Portland cement mortar. The objective of this paper is to analyze the influence of surface roughness on the pads and test other types of polypropylene fibers. Tests were carried out to characterize the composite and test on bearing pads. Characterization tests show compressive strength of 41MPa and modulus of elasticity of 12.8GPa. The bearing pads tests present 30% reduction of stiffness in relation to a reference mortar. The bearing pads with roughness on both sides present a reduction up to 30% in stiffness and an increase in accumulated deformation of more than 120%, regarding bearing pads with both sides smooth.

  7. Effect of high temperature and type of cooling on some mechanical properties of cement mortar

    Directory of Open Access Journals (Sweden)

    Abdulhussei Faisal

    2018-01-01

    Full Text Available Mortar of cement as construction materials subjected sometimes to high temperature. Some of properties of this mortar being studied after this effect. The effect of high temperature 100, 200, 400 and 700°C (exposed for two hrs. on some mechanical properties (compressive and flexural strength of two groups of cement mortar samples (with and without the addition of crushed bricks and superplasticizer as modifying materials has been studied. Two methods of cooling samples by air and by water for 1/2 hr. was used, then tested after 3, 7 and 28 days. The results showed that the compressive and flexural strength for reference mix exposed to 700°C and water cooling decreased by 65.3 % and 64.7%, respectively, compared with their reference mix tested at 20°C in 28 days. While mixes containing 100% of crushed brick as an additive and air cooling decreases by 12.3% and 9% of their compressive and flexural strength, respectively compared with the mixes tested at 20°C in 28 days. Also showed that the decreases in flexural strength for no sand mixes containing 100% of crushed brick and 4% of superplasticizer exposed to 700°C and then water cooling was 28.2% compared to those for reference mixes tested at 20°C.

  8. Properties and durability of metakaolin blended cements: mortar and concrete

    Directory of Open Access Journals (Sweden)

    Abbas, Rafik

    2010-12-01

    Full Text Available This article explores the effect of metakaolin, a pozzolan, on concrete performance. Compressive and splitting tensile strength were found for specimens cured for up to 360 and 90 days, respectively. Changes were recorded in the compressive strength of specimens exposed to salt (chloride and sulfatechloride solutions, and chloride penetration and binding capacity were measured. The findings were compared to the results for concrete prepared with ordinary Portland (OPC and moderate heat of hydration (Type II cement. MK was found to have a very positive effect on 28-day concrete strength, due to microstructure improvement of the hydrated cement. Replacing cement with metakaolin effectively raised concrete resistance to chloride attack. Concrete containing metakaolin proved to be substantially more durable in sulfate-chloride environment.

    En este trabajo se estudia el efecto del metacaolín sobre las prestaciones del hormigón. Las probetas curadas a 360 y 90 días se sometieron a ensayos de resistencia a compresión y de tracción indirecta respectivamente. Se hizo un seguimiento de la resistencia a la compresión de los materiales ante el ataque de sales (soluciones de cloruro y de sulfato-cloruro y, se midió la penetración de cloruros y la capacidad de los hormigones de inmovilizar estos iones. Los resultados se compararon con los obtenidos con hormigones elaborados con cemento pórtland ordinario (OPC y, con cemento de calor de hidratación moderado (tipo II. El MK resultó influir muy positivamente en la resistencia del hormigón a 28 días debido a la mejora de la microestructura del cemento hidratado. La sustitución de cemento por metacaolín aumentó la resistencia del hormigón al ataque de cloruros. El hormigón con metacaolín demostró ser más duradero en entornos de sulfato-cloruro que los hormigones elaborados con OPC o con cemento de tipo II. Los perfiles de concentración de cloruros a distintas profundidades y la

  9. Micro and nanostructural characterization of surfaces and interfaces of Portland cement mortars using atomic force microscopy

    International Nuclear Information System (INIS)

    Barreto, M.F.O.; Brandao, P.R.G.

    2014-01-01

    The characterization of Portland cement mortars is very important in the study the interfaces and surfaces that make up the system grout/ceramic block. In this sense, scanning electron microscopy and energy-dispersive (X-ray) spectrometer are important tools in investigating the morphology and chemical aspects. However, more detailed topographic information can be necessary in the characterization process. In this work, the aim was to characterize topographically surfaces and interfaces of mortars applied onto ceramic blocks. This has been accomplished by using the atomic force microscope (AFM) - MFP-3D-SA Asylum Research. To date, the results obtained from this research show that the characterization of cementitious materials with the help of AFM has an important contribution in the investigation and differentiation of hydrated calcium silicates (CSH), calcium hydroxide (Ca(OH)2, ettringite and calcium carbonate by providing morphological and micro topographical data, which are extremely important and reliable for the understanding of cementitious materials. (author)

  10. Effect of W/C Ratio on Durability and Porosity in Cement Mortar with Constant Cement Amount

    Directory of Open Access Journals (Sweden)

    Yun-Yong Kim

    2014-01-01

    Full Text Available Water is often added to concrete placing for easy workability and finishability in construction site. The additional mixing water can help easy mixing and workability but causes increased porosity, which yields degradation of durability and structural performances. In this paper, cement mortar samples with 0.45 of W/C (water to cement ratio are prepared for control case and durability performances are evaluated with additional water from 0.45 to 0.60 of W/C. Several durability tests including strength, chloride diffusion, air permeability, saturation, and moisture diffusion are performed, and they are analyzed with changed porosity. The changing ratios and patterns of durability performance are evaluated considering pore size distribution, total porosity, and additional water content.

  11. Improved cement mortars by addition of carbonated fly ash from solid waste incinerators

    Directory of Open Access Journals (Sweden)

    López-Zaldívar, O.

    2015-09-01

    Full Text Available This article presents the results of a research developing high performance cement mortars with the addition of municipal solid waste incineration fly ash (MSWIFA stabilized as insoluble carbonates. The encapsulation of hazardous wastes in mortar matrixes has also been achieved. The ashes present high concentrations of chlorides, Zn and Pb. A stabilization process with NaHCO3 has been developed reducing 99% the content of chlorides. Developed mortars replace 10% per weight of the aggregates by treated MSWIFA. Physical/mechanical properties of these mortars have been studied. Presence of Zn, Pb, Cu and Cd has been also analyzed confirming that leaching of these heavy metal ions is mitigated. Conclusions prove better behavior of CAC and CSA mortars than those of CEM-I and CEM-II cement. Results are remarkable for the CAC mortars, improving reference strengths in more than 25%, which make them a fast-curing product suitable for the repair of structures or industrial pavements.Este artículo presenta los resultados del desarrollo de morteros mejorados con la incorporación de cenizas volantes de residuos sólidos urbanos inertizadas en forma de carbonatos. Además se consigue la encapsulación de un residuo peligroso. Las cenizas presentan una alta concentración de cloruros, Zn y Pb. Se ha desarrollado un proceso de estabilización con NaHCO3 reduciendo en un 99% el contenido de cloruros. Los morteros reemplazan un 10% en peso del árido por cenizas tratadas. Se han analizado sus propiedades físico/mecánicas y la presencia de Zn, Pb, Cu y Cd. Se demuestra un mejor comportamiento de los morteros de CAC y CSA que los de CEM-I y CEM-II y se mitiga el lixiviado de metales pesados. Los resultados son significativos en los morteros CAC al mejorar las resistencias de los de referencia en un 25%. Los morteros desarrollados son de curado rápido adecuados para la reparación de estructuras o soleras industriales.

  12. Effect of Addition of A Marble Dust on Drying Shrinkage Cracks of Cement Mortar Reinforced with Various Fibers

    Directory of Open Access Journals (Sweden)

    Basim Thabit Al-Khafaji

    2017-05-01

    Full Text Available This investigation is conducted to study the effect of addition of marble powder (marble dust and different fibers on drying shrinkage cracks and some properties of fibers reinforcment cement mortar. Steel molds having a trapezoidal section, and the end restrained at square shape with( 2.7 meter at length are used to study restrained drying shrinkage of cement mortar. Specimens of ( compressive .flextural. splitting strength were cast. The admixture (marble dust was used to replacie weight of cement with three levels of (4%, 8% and 16% and the fiber hemp and sisal fiber were added for all mixes with proportion by volum of cement . All specimens were cured for (14 days. Average of three results was taken for any test of compressive, tensil and flextural strength. The experimental results showed that the adding of this admixture(marble dust cause adelay in a formation of cracks predicted from a drying shrinkage ,decreases of its width , and hence increases of (compressive, splitting tensil and flextural strength at levels of (4%, and 8%. Thus there is a the positive effect when fiberes added for all mixes of cement mortar with addition of (marble dust. All The admixtures (marble dust and fibers have the obvious visible effect in the delay of the information of shrinkage cracks and the decrease of its width as Compared to the cement mortar mixes when marble dust added a alone.

  13. The Effect of Sodium Hydroxide Molarity on Strength Development of Non-Cement Class C Fly Ash Geopolymer Mortar

    Science.gov (United States)

    Wardhono, A.

    2018-01-01

    The use of fly ash as cement replacement material can overcome the environmental issues, especially the global warming problem caused by the greenhouse effect. This is attributed to the CO2 gas produced during the cement manufacturing process, which 1 ton of cement is equivalent to 1 ton CO2. However, the major problem of fly ash is the requirement of activators to activate the polymer reactions. The most common activator used in non-cement or geopolymer material is the combination of sodium hydroxide (NaOH) and sodium silicate. This study aims to identify the effect of NaOH molarity as activator on strength development of non-cement class C fly ash geopolymer mortar. The molarity variations of NaOH were 6 Molar (M), 8M, 10M, 12M, 14M and 15M. The compressive strength test was performed at the age of 3, 7 and 28 days in accordance with ASTM standard, and the specimens were cured at room temperature. The results show that the highest compressive strength was achieved by geopolymer mortar with a molarity of 12M. It exhibits a higher strength to that normal mortar at 28 days. However, the use of NaOH molarity more than 12M tends to decrease the strength of non-cement geopolymer mortar specimens.

  14. Effect of Nanosilica Particle Size on the Water Permeability, Abrasion Resistance, Drying Shrinkage, and Repair Work Properties of Cement Mortar Containing Nano-SiO2

    Directory of Open Access Journals (Sweden)

    Sattawat Haruehansapong

    2017-01-01

    Full Text Available This work presents the effect of nanosilica particle sizes on durability properties and repair work properties of cement mortar containing nanosilica (NS. Three different NS particle sizes of 12, 20, and 40 nm were used and compared with those of cement mortar without NS and cement mortar with silica fume (SF. Interesting results were obtained in which the particle size of NS affected directly the abrasion resistance and water permeability. NS with particle size of 40 nm is the optimum size and gave the highest abrasion resistance and water permeability. For repair work properties, cement mortars containing NS (12 and 20 nm and SF experienced higher drying shrinkage than that of cement mortar without NS and then presented cracking behavior and debonding between the cement mortars and concrete substrate. Cement mortar containing 40 nm of NS gave the lowest drying shrinkage, the lowest crack number, and the highest adhesive strength. These results indicate that the particle size of NS affected not only the durability properties but also the repair work properties of cement mortar.

  15. Effect of nano clay particles on mechanical, thermal and physical behaviours of waste-glass cement mortars

    International Nuclear Information System (INIS)

    Aly, M.; Hashmi, M.S.J.; Olabi, A.G.; Messeiry, M.; Hussain, A.I.

    2011-01-01

    Highlights: → Glass powder (GP) and nano clay (NC) were used as a partial cement replacement in cement mortar (CM). → No damaging effect can be detected due to the reaction between GP and CM with particle size up to 75 μm. → Hybrid combination of GP/NC greatly improved mechanical properties and microstructure of CM. - Abstract: Worldwide, around 2.6 billion tons of cement is produced annually. This huge size of production consumes large amounts of energy and is one of the largest contributors to carbon dioxide (CO 2 ) release. Accordingly, there is a pressing demand to minimise the quantity of cement used in the concrete industry. The main challenge to this is to get durable concrete with less cement and within reasonable cost. The economic, environmental and engineering benefits of reusing ground waste-glass powder (WGP) as a partial cement replacement has been established, but low glass reactivity and the possible alkali-silica reaction (ASR) are a drawback. Recent advances in nano-technology have revealed that nano-sized particles such as nano clay (NC) have a high surface area to volume ratio that provides the potential for tremendous chemical reactivity, accelerating pozzolanic activity and hindering ASR. This paper presents a laboratory study of the properties of NC/WGP cement composites. The microstructure, ASR, fracture energy, compressive and flexural properties of cement mortars containing WGP as a cement replacement with and without NC are investigated and compared with plain matrix. In addition, the hydration of cement compounds was followed by differential thermal analysis (DTA), thermogravimetric analysis (TGA), and also X-ray diffraction (XRD). The results showed that incorporation of glass powder has a positive effect on the mechanical properties of cement mortars after 28 days of hydration. Also, the results revealed that the mechanical properties of the cement mortars with a hybrid combination of glass powder and NC were all higher than

  16. Effects of coal fly ash on the rheological characteristics of concrete paste and mortar; Zum Einfluss von Steinkohlenflugaschen auf das rheologische Verhalten von Zementleimen und -moerteln

    Energy Technology Data Exchange (ETDEWEB)

    Freimann, T.

    2002-07-01

    For the placement of concrete at a building site the workability of the fresh concrete is one of the most important influence parameters. The workability is depending on the internal forces within the suspension and interactions between the solid particles. Particularly the paste and mortar phase and thus the sort and composition of fine constituents influence decisively the flowability of the fresh concrete. In addition to cement often fly ashes (FA) are used as fine components in concrete. Not only the properties of the hardened concrete are changed by the addition of FA but also the rheological properties of the fresh mortar and paste. In this study the most important parameters of the basic ingredients regarding the flowability were determined on the basis of experiments with cement/FA-pastes and mortars with a maximum particle size of 2 mm. General statements about the effect, respectively the application of FA were formulated. At the main part experiments were performed using the rotational viscometer (Viskomat) in order to determine the yield value and plastic viscosity according to the Bingham model. For cement/FA-suspensions the influence of the FA on the internal forces is presented and compared between pastes and mortars. The addition of FA influences the yield value as well as the plastic viscosity of the suspension. With the aid of multiple linear regression analysis the material parameters were determined which are most important for the rheological properties. Several numerical equations were derived permitting an estimation of yield value and viscosity of various cement/FA-suspensions. For practical use a nomogram was developed which allows a rapid estimation of the rheological behaviour for different fly ashes. The results of the investigation showed that an appropriate parameter to describe FA-influence on the flowability is the water demand determined by EN 196 with the same procedure as for cement (required amount of water in Vol.-% for normal

  17. Enhancement of thermal neutron shielding of cement mortar by using borosilicate glass powder.

    Science.gov (United States)

    Jang, Bo-Kil; Lee, Jun-Cheol; Kim, Ji-Hyun; Chung, Chul-Woo

    2017-05-01

    Concrete has been used as a traditional biological shielding material. High hydrogen content in concrete also effectively attenuates high-energy fast neutrons. However, concrete does not have strong protection against thermal neutrons because of the lack of boron compound. In this research, boron was added in the form of borosilicate glass powder to increase the neutron shielding property of cement mortar. Borosilicate glass powder was chosen in order to have beneficial pozzolanic activity and to avoid deleterious expansion caused by an alkali-silica reaction. According to the experimental results, borosilicate glass powder with an average particle size of 13µm showed pozzolanic activity. The replacement of borosilicate glass powder with cement caused a slight increase in the 28-day compressive strength. However, the incorporation of borosilicate glass powder resulted in higher thermal neutron shielding capability. Thus, borosilicate glass powder can be used as a good mineral additive for various radiation shielding purposes. Copyright © 2017 Elsevier Ltd. All rights reserved.

  18. Influence of Titanium Dioxide Nanoparticles on the Sulfate Attack upon Ordinary Portland Cement and Slag-Blended Mortars

    Directory of Open Access Journals (Sweden)

    Atta-ur-Rehman

    2018-02-01

    Full Text Available In this study, the effects of titanium dioxide (TiO2 nanoparticles on the sulfate attack resistance of ordinary Portland cement (OPC and slag-blended mortars were investigated. OPC and slag-blended mortars (OPC:Slag = 50:50 were made with water to binder ratio of 0.4 and a binder to sand ratio of 1:3. TiO2 was added as an admixture as 0%, 3%, 6%, 9% and 12% of the binder weight. Mortar specimens were exposed to an accelerated sulfate attack environment. Expansion, changes in mass and surface microhardness were measured. Scanning Electron Microscopy (SEM, Energy Dispersive Spectroscopy (EDS, X-ray Diffraction (XRD, Thermogravimetry Analysis (TGA and Differential Scanning Calorimetry (DSC tests were conducted. The formation of ettringite and gypsum crystals after the sulfate attack were detected. Both these products had caused crystallization pressure in the microstructure of mortars and deteriorated the mortars. Our results show that the addition of nano-TiO2 accelerated expansion, variation in mass, loss of surface microhardness and widened cracks in OPC and slag-blended mortars. Nano-TiO2 containing slag-blended mortars were more resistant to sulfate attack than nano-TiO2 containing OPC mortars. Because nano-TiO2 reduced the size of coarse pores, so it increased crystallization pressure due to the formation of ettringite and gypsum thus led to more damage under sulfate attack.

  19. Application of microbial biocementation to improve the physico-mechanical properties of cement mortar

    Directory of Open Access Journals (Sweden)

    S.A. Abo-El-Enein

    2013-04-01

    Full Text Available Calcite is one of the most common and wide spread mineral on Earth constituting 4 wt% of the Earth’s crust. It is naturally found in extensive sedimentary rock masses, as lime stone marble and calcareous sandstone in marine, fresh water and terrestrial environments. Calcium carbonate is one of the most well known mineral that bacteria deposit by the phenomenon called biocementation or microbiologically induced calcite precipitation (MICP. Such deposits have recently emerged as promising binders for protecting and consolidating various building materials. Microbially enhanced calcite precipitation on concrete or mortar has become an important area of research regarding construction materials. This study describes a method of strength and water absorption improvement of cement–sand mortar by the microbiologically induced calcium carbonate precipitation. A moderately alkalophilic aerobic Sporosarcina pasteurii was incorporated at different cell concentrations with the mixing water. The study showed that a 33% increase in 28 days compressive strength of cement mortar was achieved with the addition of about one optical density (1 OD of bacterial cells with mixing water. The strength and water absorption improvement are due to the growth of calcite crystals within the pores of the cement–sand matrix as indicated from the microstructure obtained from scanning electron microscopy (SEM examination.

  20. Measuring techniques for autogenous strain of cement paste

    DEFF Research Database (Denmark)

    Lura, Pietro; Jensen, Ole Mejlhede

    2007-01-01

    Volumetric measurement of autogenous strain is frequently performed by placing the fresh cement paste in a rubber membrane submerged in water. The volume change of the cement paste is measured by the amount of water displaced by the submerged sample. Volumetric and linear measurements of autogenous...... of the volumetric method. Water absorption is driven by a lowering of the water activity in the cement paste due to dissolved salts in the pore fluid and to self-desiccation. From the moment of casting, significant water uptake was registered in all experiments. This water uptake influenced the volumetric...... on the same cement pastes....

  1. Lime mud from cellulose industry as raw material in cement mortars

    Directory of Open Access Journals (Sweden)

    Modolo, R. C.E.

    2014-12-01

    Full Text Available This study reports the use of lime mud (LM in cement-based-mortars. Lime mud is a waste generated in the production of cellulose by the kraft mill process. It is mainly composed of CaCO3, a small amount of magnesium carbonate and other trace minerals. Mortars were prepared by adding different amounts of LM (10, 20 and 30% by weight of cement in dry weight. The mortar compositions were evaluated through rheology and flow table measurements, assuring that all the samples exhibited adequate conditions for testing in both equipments. The hardened state properties were also evaluated through mechanical strengths at 7, 28 and 90 days of curing. Following a waste management solution perspective, this work intend to provide a general evaluation of LM application in cement based mortars, looking at both fresh and hardened properties in order to guarantee that the final application requirements are not hindered.Este estudio revela el uso de lodo de carbonato (LM en morteros de cemento. El LM es un residuo compuesto principalmente por CaCO3 generado en la producción de pasta de papel por el método Kraft. Los morteros se prepararon a partir de la adición de diferentes niveles de LM (10, 20 y 30% en peso de cemento en peso seco. Las composiciones de los morteros fueron caracterizadas através de mediciones de reología de mesa y de flujo, asegurando que las muestras exhibían condiciones adecuadas para su caracterización en ambos equipamientos. Las propiedades en estado endurecido también se evaluaron através de resistencias mecánicas a los 7, 28 y 90 días de cura. Con objeto de gestión de residuos, este trabajo tiene la intención de proporcionar una visión general de la aplicación de LM en los morteros, haciendo hincapié en las propiedades con el fin de garantizar que los requisitos para su aplicación final no se vean obstaculizados.

  2. Study of Tritium Behavior in Cement Paste

    International Nuclear Information System (INIS)

    Takata, H.; Motoshima, T.; Satake, S.; Nishikawa, M.

    2005-01-01

    The concrete materials are used as the partition wall of the tritium handling facilities. It is important to grasp the tritium behavior in the concrete wall for radiation safety. It is considered in this study that the surface water on the concrete materials consists of physically adsorbed water, chemically adsorbed water and structural water as in the case of porous adsorption materials. The adsorption capacity due to physically and chemically adsorption isotherms observed in this study shows that the amount of water adsorption on the cement paste is a quarter of the amount adsorbed onto the surface of activated alumina or molecular sieves 5A (MS-5A). It shows that concrete is easily contaminated with tritiated water

  3. Influence of Waste Glass Powder Addition on the Pore Structure and Service Properties of Cement Mortars

    Directory of Open Access Journals (Sweden)

    José Marcos Ortega

    2018-03-01

    Full Text Available At present, reusing waste constitutes an important challenge in order to reach a more sustainable environment. The cement industry is an important pollutant industrial sector. Therefore, the reduction of its CO2 emissions is now a popular topic of study. One way to lessen those emissions is partially replacing clinker with other materials. In this regard, the reuse of waste glass powder as a clinker replacement could be possible. This is a non-biodegradable residue that permanently occupies a large amount of space in dumping sites. The aim of this work is to study the long-term effects (400 days of the addition of waste glass powder on the microstructure and service properties of mortars that incorporate up to 20% of this addition as clinker replacement. The microstructure has been characterised using the non-destructive impedance spectroscopy technique and mercury intrusion porosimetry. Furthermore, differential thermal analysis was also performed. Compressive strength and both steady-state and non-steady-state chloride diffusion coefficients have also been determined. Considering the obtained results, mortars with 10% and 20% waste glass powder showed good service properties until 400 days, similar to or even better than those made with ordinary Portland cement without additions, with the added value of contributing to sustainability.

  4. Study on cement mortar and concrete made with sewage sludge ash.

    Science.gov (United States)

    Chang, F C; Lin, J D; Tsai, C C; Wang, K S

    2010-01-01

    This study investigated the feasibility of reusing wastewater sludge ash in construction materials to replace partial materials. Wastewater sludge sampled from thermal power plant was burned into sludge ash at 800°C in the laboratory. The sludge incineration ash has low heavy metal including Pb, Cd, Cr and Cu, so it belongs to general enterprise waste. The chemical composition of sludge incineration ash was summed up in SiO₂, CaO, Fe₂O₃ and MgO. Then the wastewater sludge ash is also found to be a porous material with irregular surface. When the sludge ash was used to replace mortar or concrete cement, its water-adsorption capability will result in the reduction of mortar workability and compressive strength. Cement is being substituted for sludge ash, and 10 percent of sludge ash is more appropriate. Sludge ash is reused to take the place of construction materials and satisfies the requests of standard specification except for higher water absorption.

  5. Influence of Portland Cement Class on the Corrosion Rate of Steel Reinforcement in Cement Mortar Caused by Penetrating Chloride and Sulfate from the Environment

    Directory of Open Access Journals (Sweden)

    Bikić, F.

    2013-01-01

    Full Text Available The influence of portland cement class on the corrosion rate of steel reinforcement in cement mortar caused by penetrating chloride or sulfate from the environment in already hardened cement mortar is investigated in this paper. Three classes of portland cement have been used for the tests, PC 35, PC 45 and PC 55. Cylindrical samples of cement mortar with steel reinfor- cement in the middle were treated 6 months at room temperature in the following solutions: w(SO42- = 2.1 % and w(Cl- = 5 %. Two techniques have been used for testing corrosion rate of steel reinforcement in cement mortar: Tafel extrapolation technique and potentiodynamic polarization technique. Investigations were conducted by potentiostat/galvanostat Princeton Applied Research 263A-2 with the software PowerCORR®. The results of both techniques indi-cate the most active corrosion of steel reinforcement in the samples prepared from cement PC 35 in both treated solutions, while the lowest corrosion of the steel reinforcement was observed in cement samples prepared from cement PC 55. This conclusion was drawn by analyzing the results shown in Figs. 1–4. Comparing corrosion current density of samples, working electrodes, Figs. 1 and 2, Table 2, the results show the most stable corrosion of steel reinforcement in samples prepared from cement PC 55, and the most active corrosion in samples prepared from ce- ment PC 35. The most active corrosion in samples prepared from cement PC 35 is evident from the positions of the open circuit potentials whose values are less for samples prepared from cement PC 35 in both the treated solution, Figs. 1 and 2, Table 2. Comparison of the anodic polarization curves of the working electrodes in both the treated solutions, Figs. 3 and 4, also shows that the intensity of corrosion is the largest for the working electrodes prepared from cement PC 35 and the smallest for the working electrodes prepared from cement PC 55. Investigation results should be

  6. Utilization of recycled cathode ray tubes glass in cement mortar for X-ray radiation-shielding applications.

    Science.gov (United States)

    Ling, Tung-Chai; Poon, Chi-Sun; Lam, Wai-Shung; Chan, Tai-Po; Fung, Karl Ka-Lok

    2012-01-15

    Recycled glass derived from cathode ray tubes (CRT) glass with a specific gravity of approximately 3.0 g/cm(3) can be potentially suitable to be used as fine aggregate for preparing cement mortars for X-ray radiation-shielding applications. In this work, the effects of using crushed glass derived from crushed CRT funnel glass (both acid washed and unwashed) and crushed ordinary beverage container glass at different replacement levels (0%, 25%, 50%, 75% and 100% by volume) of sand on the mechanical properties (strength and density) and radiation-shielding performance of the cement-sand mortars were studied. The results show that all the prepared mortars had compressive strength values greater than 30 MPa which are suitable for most building applications based on ASTM C 270. The density and shielding performance of the mortar prepared with ordinary crushed (lead-free) glass was similar to the control mortar. However, a significant enhancement of radiation-shielding was achieved when the CRT glasses were used due to the presence of lead in the glass. In addition, the radiation shielding contribution of CRT glasses was more pronounced when the mortar was subject to a higher level of X-ray energy. Copyright © 2011 Elsevier B.V. All rights reserved.

  7. Potential Use Of Carbide Lime Waste As An Alternative Material To Conventional Hydrated Lime Of Cement-Lime Mortars

    OpenAIRE

    Al Khaja, Waheeb A.

    1992-01-01

    The present study aimed at the possibility of using the carbide lime waste as an alternative material to the conventional lime used for cement-lime mortar. The waste is a by-product obtained in the generation of acetylene from calcium carbide. Physical and chemical properties of the wastes were studied. Two cement-lime-sand mix proportions containing carbide lime waste were compared with the same mix proportions containing conventional lime along with a control mix without lime. Specimens wer...

  8. Utilization of recycled cathode ray tubes glass in cement mortar for X-ray radiation-shielding applications

    International Nuclear Information System (INIS)

    Ling, Tung-Chai; Poon, Chi-Sun; Lam, Wai-Shung; Chan, Tai-Po; Fung, Karl Ka-Lok

    2012-01-01

    Highlights: ► It is feasible to use recycled CRT glass in mortar as shield against X-ray radiation. ► Shielding properties of CRT mortar is strongly depended on CRT content. ► Linear attenuation coefficient was reduced by 142% upon 100% CRT glass in mortar. ► Effect of mortar thickness and irradiation energies on shielding was investigated. - Abstract: Recycled glass derived from cathode ray tubes (CRT) glass with a specific gravity of approximately 3.0 g/cm 3 can be potentially suitable to be used as fine aggregate for preparing cement mortars for X-ray radiation-shielding applications. In this work, the effects of using crushed glass derived from crushed CRT funnel glass (both acid washed and unwashed) and crushed ordinary beverage container glass at different replacement levels (0%, 25%, 50%, 75% and 100% by volume) of sand on the mechanical properties (strength and density) and radiation-shielding performance of the cement–sand mortars were studied. The results show that all the prepared mortars had compressive strength values greater than 30 MPa which are suitable for most building applications based on ASTM C 270. The density and shielding performance of the mortar prepared with ordinary crushed (lead-free) glass was similar to the control mortar. However, a significant enhancement of radiation-shielding was achieved when the CRT glasses were used due to the presence of lead in the glass. In addition, the radiation shielding contribution of CRT glasses was more pronounced when the mortar was subject to a higher level of X-ray energy.

  9. A positron annihilation study on the hydration of cement pastes

    International Nuclear Information System (INIS)

    Consolati, G.; Quasso, F.

    2007-01-01

    Positron annihilation lifetime spectroscopy experiments were carried out in various ordinary Portland cement pastes, in an attempt to monitor the porosity of the pastes. It is found that positronium intensity is well correlated to the time evolution of the total porosity and it is influenced by the water-to-cement ratio. This parameter is also sensitive to the delayed hydration process induced by adding methanol to the water-cement mixture

  10. Reuse of By-Products from Ready-Mixed Concrete Plants for the Production of Cement Mortars

    Directory of Open Access Journals (Sweden)

    Monika Zervaki

    2013-06-01

    Full Text Available This study was motivated by the necessity to recycle sludge water resulting from washing out concrete mixing trucks - a problem of both environmental and economic importance for the ready-mixed concrete industry. Sludge water from ready-mixed concrete plants as well as dry sludge, which is derived from the settling of the water, are hazardous for disposal due to their high pH value (pH>11.5. In this work, cement mortars were composed using either sludge water after various treatment, or dry sludge in several ratios. The cement mortars were tested for their workability and strength development. The purpose of this experimental design was to prove that sludge water, as well as sludge in a wet or dry form, can be used in the production of mortars without degrading any of their properties.

  11. Mechanical characterization of Portland cement mortars containing petroleum or coal tar

    Directory of Open Access Journals (Sweden)

    Garcés, P.

    2007-08-01

    Full Text Available This article discusses experimental data on the flexural and compressive strength of Portland cement mortars containing additions or cement replacements consisting in petroleum or coal tar, by-products of the oil and coal industries. The materials studied were two coal (BACA and BACB and two petroleum (BPP and BPT tars. The results show that it is feasible to use such materials as a partial replacement for cement in mortar manufacture. This should lead to the design of a new sustainable product that will contribute to lowering the environmental impact of construction materials while at the same time opening up an avenue for the re-use of this type of industrial by-products.En este artículo se presentan datos experimentales de resistencia a flexión y a compresión de morteros de cemento Portland con adición y sustitución de breas de petróleo y de alquitrán de carbón, que son subproductos de la industria del carbón o del petróleo. Los materiales estudiados son breas de alquitrán de carbón A (BACA y B (BACB, y dos breas de petróleo (BPP y (BPT. Los datos demuestran la viabilidad del uso de estas breas en la fabricación de morteros con menores contenidos de cemento, permitiendo diseñar un nuevo material sostenible con el medio ambiente y que contribuya a reducir el impacto ambiental de los materiales de construcción, hecho que permite abrir una nueva vía de valorización de estos subproductos.

  12. Dry and wet "deposition" studies of the degradation of cement mortars

    Directory of Open Access Journals (Sweden)

    Martínez-Ramírez, S.

    1998-06-01

    Full Text Available The reaction of portland cement mortars with SO2 gaseous pollutant and artificial 'acid rain' solution has been examined using laboratory exposure chambers, with realistic presentation rates of pollutants. The mortar were previously carbonated to produce superficial carbonation. Two mortars with different w/c ratio and hence specific surface were prepared and exposed into the chambers. For dry deposition of SO2 pollutant gas, the important roles of water and water plus oxidant in increasing chemical reaction are readily revealed. Further, accessible porosity also increases reaction through increased times of reaction of pollutant with the mortars. Interestingly, in the absence of deliberate surface wetting, the presence of oxidant, ozone, leads to a reduction in the already limited extent of reaction. Wet deposition studies using artificial 'acid rain' solution result in gypsum formation, which is more extensive for mortars of increased w/c ratios.

    Se han realizado ensayos de laboratorio de simulación de los procesos ambientales de "deposición" seca y húmeda sobre morteros de cemento portland, estudiándose las reacciones que se producen con el contaminante SO2 ("deposición" seca y la disolución de 'lluvia acida' ("deposición" húmeda. Los morteros de cemento se carbonataron para favorecer la carbonatación superficial de los mismos. Se prepararon morteros con dos relaciones a/c con el fin de estudiar la influencia que la variable superficie específica tenía en el proceso de deterioro de dichos materiales. En los estudios de deposición seca con SO2 como gas agresivo se ha visto la importancia que el agua y el agua junto a un oxidante tienen en la reacción del contaminante con los componentes del mortero. La superficie específica Juega un papel importante, ya que al aumentar, aumenta la reacción con el contaminante. La reacción en presencia de oxidante, (SO2+O3

  13. Hydration rate and strength development of low-heat type portland cement mortar mixed with pozzolanic materials

    International Nuclear Information System (INIS)

    Matsui, Jun

    1998-01-01

    Recently, low-heat type Portland cement was specified in Japan Industrial Standards (JIS). Its hydration proceeds slowly. The results of the research so far obtained indicate that slow hydration of cement and mixing of pozzolanic materials with cement make micro-structure of harded cement paste dense and durable. In this study, a blended cement using low-heat type Portland cement and some of pozzolanic materials has been newly developed and its strength property and hydration ratio were checked. The followings are conclusion. (1) Hydration rate of cement paste varies with the replacement ratio of pozzolanic materials. (2) A good liner relationship between strength and total hydration rate of cement paste was observed. (3) A proper replacement ratio of both base-cement and pozzolanic material for manufacturing a blended cement is 50%. (author)

  14. Evaluation Some Properties of NanoMetakaolin or Rice Husk Ash Cement Mortar and its Resistance to Elevated Temperature

    Directory of Open Access Journals (Sweden)

    Jassim Atiya Alwan

    2016-12-01

    Full Text Available The objective of this research is to find the optimum value of some properties like compressive, flexural strength of blended cement mortar by nanometakaolin ( NMK or rice husk ash (RHA and to evaluate the effect of high temperature on these properties. The ordinary Portland cement(OPC of mortar was partially substituted by NMK or RHA of 5,10,15 and 20% by weight of cement. (108 control and blended specimens were casted and tested at ambient temperature (33 ºC for compressive and flexural strength for 28 and 90 days. Another (270 of the control and blended specimens were casted and cured for 90 days and exposed to elevated temperature of a gradual increase in temperature up to 200 ºC,300 ºC, 400 ºC,600 ºC and 800 ºC for two hours in an electrical furnace and they were under the same previous tests. The test results at ambient temperature indicate that the optimum compressive and flexural strength was with ratio of 15% NMK cement replacement in mortar for 28 and 90 days but for RHA was ratio of 10% for 28 days and 15% of cement weight in mortar for 90 days compared to control specimens. The results of exposing control and blended specimens of (90 days to elevated temperature showed that the optimum strength for control and the best MK replacement ratio were found at 200 ºC, and the best RHA replacement ratio specimens was found at 300 ºC. It is also found that exposing the mortar to more than these temperatures destroyed its strength and it was detrimental to its properties.

  15. Physico-chemical studies of gamma-irradiated polyester. Impregnated cement mortar composite

    International Nuclear Information System (INIS)

    Ismail, M.R.; Afifi, M.S.

    1998-01-01

    The effect of impregnation time on the physico-chemical and mechanical properties of polyester-cement mortar composite has been investigated. The samples were soaked in unsaturated polyester resin containing 40% styrene monomer at impregnation times ranging from 1-15 hours and then exposed to 50 kGy of γ-irradiation. The effects on polymer loading, compressive strength, apparent porosity, and water absorption in addition to IR spectra and TGA of the samples were studied. It was found that, the polymer loading and compressive strength increase with the increased of soaking time up to 4 hours and there is no significant improvement of the polymer loading and strength. Whereas, the apparent porosity and water absorption behave in an opposite direction. These are attributed to the presence of polymer in the pores of the samples. IR spectra showed that, new bands appeared as result of the reaction between polyester and set cement. TGA showed that, the polyester cement composite has higher thermal stability as a compared to irradiated polyester. (author)

  16. The influence of cement type and temperature on chloride binding in cement paste

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede; Korzen, Migge Sofie Hoffmann; Skibsted, Jørgen

    1998-01-01

    This paper describes effects of cement type and temperature on chloride binding in cement paste, which is an important subject in relation to life-time modelling of reinforced concrete structures. The influence of cement type on chloride binding is investigated by substituting cement with pure...... cement clinker. Both theoretical considerations and experimental data for chloride binding in cement pastes are presented. A physico-chemically based model to describe the influence of temperature on physical binding of chloride is presented. Solid-state 27Al and 29Si magic-angle spinning (MAS) nuclear...... magnetic resonance (NMR) spectroscopy has been used for quantification of the anhydrous and hydrated aluminate and silicate phases in the chloride exposed cement pastes. The 27Al isotropic chemical shift and nuclear quadrupole coupling is reported for a synthetic sample of Friedel's salt, Ca2Al(OH)6Cl×2H2O....

  17. Low porosity portland cement pastes based on furan polymers

    International Nuclear Information System (INIS)

    Darweesh, H.H.M.

    2005-01-01

    The effect of three different types of Furan polymers on the porosity, mechanical properties, mechanism of hydration and microstructure of Ordinary Portland cement (OPC) pastes was investigated. The results showed that mixing the OPC with Furan polymers, the standard water of consistency of the different cement pastes decreases and therefore the setting times (initial and final) are shortened. The total porosity of the hardened cement pastes decreased, while the mechanical properties improved and enhanced at all curing ages of hydration compared with those of the pure OPC pastes. The hydration process with Furan polymers proceeded according to the following decreasing order: F.ac. > F.ph. > F.alc. > OPC

  18. Hydration characteristics and structure formation of cement pastes containing metakaolin

    Directory of Open Access Journals (Sweden)

    Dvorkin Leonid

    2018-01-01

    Full Text Available Metakaolin (MK is one of the most effective mineral admixtures for cement-based composites. The deposits of kaolin clays are wide-spread in the world. Metakaolin is comparable to silica fume as an active mineral admixture for cement-based composites. In this paper, the rheological and mechanical properties of cement paste containing metakaolin are investigated. The effect of MK is more evident at “tight” hydration conditions within mixtures with low water-cement ratio, provided by application of superplasticizers. The cement is replaced with 0 to 15% metakaolin, and superplasticizer content ranged from 0 to 1.5% by weight of cementitious materials (i.e. cement and metakaolin. An equation is derived to describe the relationship between the metakaolin and superplasticizer content and consistency of pastes. There is a linear dependence between metakalolin content and water demand. Second-degree polynomial describe the influence of superplasticizer content. The application of SP and MK may produce cement-water suspensions with water-retaining capacity at 50-70% higher than control suspensions. The investigation of initial structure forming of cement pastes with SP-MK composite admixture indicates the extension of coagulation structure forming phase comparing to the pastes without additives. Crystallization stage was characterized by more intensive strengthening of the paste with SP-MK admixture comparing to the paste without admixtures and paste with SP. Results on the porosity parameters for hardened cement paste indicate a decrease in the average diameter of pores and refinement of pore structure in the presence of metakaolin. A finer pore structure associated with an increase in strength. X-ray analysis data reveal a growing number of small-crystalline low-alkaline calcium hydrosilicates and reducing portlandite content, when MK dosage increases. Scanning electron microscopy (SEM data confirm, that hardened cement paste containing MK has

  19. Carbonation of calcium aluminate cement pastes

    Directory of Open Access Journals (Sweden)

    Fernández-Carrasco, L.

    2001-12-01

    Full Text Available This work discusses the results from accelerated tests intended to investigate the ways the different curing methods affect the carbonation of calcium aluminate cements pastes (CAC. The research was focused on the mineralogical composition of hydrated and carbonated samples. The compressive strengths and the porosity of the samples have been determined. Results point out that vaterite and aragonite are formed as a result of carbonation of both cubic and hexagonal calcium aluminate hydrates. The polymorph of calcium carbonate formed does not depend on the curing process. Carbonation rates is higher in hexagonal than in cubic hydrates. Results obtained through this study evidence that, as a consequence of the carbonation process of CAC pastes, in test conditions, an increase of the mechanical strengths occurs.

    En el presente trabajo se discuten los resultados obtenidos en los ensayos acelerados llevados a cabo para investigar los efectos de diferentes métodos de curado sobre la carbonatacion de pastas del cemento de aluminato de calcio (CAC. Se estudió la composición mineralógica de las muestras hidratadas y carbonatadas. Además, se determinaron las resistencias mecánicas a compresión y la porosidad de las probetas. Los resultados indican que la vaterita y el aragonito son las polimorfías del CaCO3 que se forman al carbonatar los aluminatos cálcicos hidratos, tanto los de naturaleza hexagonal como cúbica. El polimorfo del carbonato cálcico formado no depende del proceso de curado. La velocidad de carbonatación de los hidratos hexagonales es mayor que la de los cúbicos. Los resultados obtenidos en el presente trabajo han evidenciado que como consecuencia del proceso de carbonatación sobre pastas de CAC, en las condiciones realizadas, se produce un incremento en las resistencias mecánicas.

  20. Using Neutron Radiography to Quantify Water Transport and the Degree of Saturation in Entrained Air Cement Based Mortar

    Science.gov (United States)

    Lucero, Catherine L.; Bentz, Dale P.; Hussey, Daniel S.; Jacobson, David L.; Weiss, W. Jason

    Air entrainment is commonly added to concrete to help in reducing the potential for freeze thaw damage. It is hypothesized that the entrained air voids remain unsaturated or partially saturated long after the smaller pores fill with water. Small gel and capillary pores in the cement matrix fill quickly on exposure to water, but larger pores (entrapped and entrained air voids) require longer times or other methods to achieve saturation. As such, it is important to quantitatively determine the water content and degree of saturation in air entrained cementitious materials. In order to further investigate properties of cement-based mortar, a model based on Beer's Law has been developed to interpret neutron radiographs. This model is a powerful tool for analyzing images acquired from neutron radiography. A mortar with a known volume of aggregate, water to cement ratio and degree of hydration can be imaged and the degree of saturation can be estimated.

  1. Radiation use in measurement and control of cement and fine aggregate segregation in mortar

    International Nuclear Information System (INIS)

    Veado, Maria Adelaide Rabelo Vasconcelos.

    1991-09-01

    Segregation of solid particles in a mortar for structural purposes was measured by a nuclear method in which the grains were marked by neutron activation. The influence of vibration time on segregation was studied, and the method was capable of detecting a segregation trend, that is a higher concentration of cement and finer aggregate particles in the upper longer of the specimens. Results were more significant when the finer grains were marked rather than. The coarser ones, due to statistical constraints imposed by the smaller quantities of the latter. The Segregation increased with increasing vibration times. The validity of the proposed nuclear method for segregation measurements has been confirmed. (author). 15 refs., 5 figs., 19 tabs

  2. Synthesis of dextrin-stabilized colloidal silver nanoparticles and their application as modifiers of cement mortar.

    Science.gov (United States)

    Konował, Emilia; Sybis, Marta; Modrzejewska-Sikorska, Anna; Milczarek, Grzegorz

    2017-11-01

    Various commercial dextrins were used as reducing and stabilizing agents for a novel one-step synthesis of silver nanoparticles from ammonia complexes of silver ions. As a result, stable colloids of silver were formed during the reaction with the particle size being the function of the dextrin type. The obtained colloids were characterized by UV-vis spectrophotometry, size distribution (using Non-Invasive Backscatter optics) and transmission electron microscopy (TEM). The achieved results clearly indicate the possibility of low-cost production of large quantities of colloidal silver nanoparticles using materials derived from renewable sources. The resulting silver colloids can be used for different purposes, e.g. as bactericidal agents. Combination of the aforementioned properties of nanosilver particles with plasticizing properties of dextrin enables to obtain cement mortars with increased workability and enhanced compressive strength. Moreover, the obtained material is also characterized by increased immunity to adverse impact of microorganisms. Copyright © 2017 Elsevier B.V. All rights reserved.

  3. Leaching behaviour of tritium from a hardened cement paste

    International Nuclear Information System (INIS)

    Matsuzuru, H.; Moriyama, N.; Ito, A.

    1979-01-01

    Leaching of tritium from a hardened cement paste into an aqueous phase has been studied to assess the safety of solidification of the tritiated liquid waste with cement. Leaching tests were carried out in accordance with the method recommended by the International Atomic Energy Agency. The leaching fraction was measured as functions of the waste-cement wt ratio (Wa/C), temperature of leachant and curing time. the tritium leachability of cements follows the order: alumina cement > Portland cement > slag cement. The fraction of tritium leached increases with increasing Wa/C and temperature and decreasing curing period. A deionized water as a leachant gives a slightly higher leachability than the synthetic sea water. The coating of the specimen surface with bitumen reduces the leachability to about 5% of its value for the specimen without coating. (author)

  4. Small angle neutron scattering from hydrated cement pastes

    International Nuclear Information System (INIS)

    Sabine, T.M.; Bertram, W.K.; Aldridge, L.P.

    1996-01-01

    Small angle neutron scattering (SANS) was used to study the microstructure of hydrating cement made with, and without silica fume. Some significant differences were found between the SANS spectra of pastes made from OPC (ordinary Portland cement) and DSP (made with silica fume and superplasticiser). The SANS spectra are interpreted in terms of scattering from simple particles. Particle growth was monitored during hydration and it was found that the growth correlated with the heat of hydration of the cement

  5. Simple method of dynamic Young’s modulus determination in lime and cement mortars

    Directory of Open Access Journals (Sweden)

    Rosell, J. R.

    2011-03-01

    Full Text Available The present work explains a simple method to determine the dynamic Young module (MOE by inducing a set of small mechanical perturbation to samples of lime and cement mortars and correlating the results obtained with results determined using other techniques and methods. The procedure described herein follows the instructions stated in the UNE-EN ISO 12680-1 standard for refractory products although in this study the instructions are applied to standardized RILEM 4x4x16 cm test samples made of lime and cement mortars. In addition, MOE determinations are obtained by using ultrasonic impulse velocity while static Young's modulus determinations are obtained by performing conventional bending tests. The ability of this procedure to correlate with results from other techniques, along with its simplicity, suggests that it can be widely adapted to determine the deformability of mortars under load using standardized samples.

    El presente trabajo muestra un método simple para determinar el módulo de Young dinámico (MOE a partir de pequeñas perturbaciones mecánicas producidas a probetas de mortero de cal y de cemento, correlacionando los resultados obtenidos con las correspondientes mediciones realizadas con otras técnicas. El procedimiento sigue básicamente las instrucciones fijadas en la norma UNE-EN ISO 12680-1 de productos refractarios, pero aplicándolo a probetas normalizadas RILEM 4x4x16 de morteros confeccionados con cal y cemento. Paralelamente se realizan determinaciones del MOE a partir de la velocidad de paso de impulsos ultrasónicos y determinaciones del módulo de Young estático a partir de ensayos de flexión convencionales. La simplicidad del método aplicado y la correlación de los resultados obtenidos con las variables medidas permiten concluir que esta metodología es de aplicación directa para determinar la deformabilidad bajo carga de los morteros a partir de probetas normalizadas.

  6. Durability of Gamma Irradiated Polymer Impregnated Blended Cement Pastes

    International Nuclear Information System (INIS)

    Khattab, M.M.; Abdel-Rahman, H.A.; Younes, M.M.

    2010-01-01

    This study is focusing on durability and performance of the neat blended cement paste as well as those of the polymer-impregnated paste towards seawater and various concentrations of magnesium sulfate solutions up to 6 months of curing. The neat blended cement paste is prepared by a partial substitution of ordinary Portland cement with 5% of active rice husk ash (RHA). These samples were cured under tap water for 7 days. Similar samples were impregnated with unsaturated polyester resin (UPE) and subjected to various doses of gamma rays ranging from 10 to 50 kGy. The results showed that the irradiated impregnated specimens gave higher values of compressive strength than the neat blended cement paste specimens. On immersing the neat blended cement specimens and polymer impregnated specimens especially that irradiated at 30 kGy in seawater and different concentrations of magnesium sulfate solutions up to 6 months of curing, the results showed that the polymer impregnated blended cement (OPC-RHA-UPE) paste have a good resistance towards aggressive media as compared to the neat blended cement (OPC-RHA) paste. The results also indicated that the sea water has a greater corrosive effect than the magnesium sulfate solutions. These results were confirmed by scanning electron microscopy (SEM) and mercury intrusion porosimetry (MIP)

  7. Cement paste prior to setting: A rheological approach

    Energy Technology Data Exchange (ETDEWEB)

    Bellotto, Maurizio, E-mail: maurizio.bellotto@bozzetto.it

    2013-10-15

    The evolution of cement paste during the dormant period is analyzed via small amplitude oscillation rheological measurements. Cement paste, from the very first moments after mixing cement and water, shows the formation of an elastic gel whose strength is rapidly increasing over time. Up to the onset of Portlandite precipitation G′(t) increases by more than 2 orders of magnitude and in the acceleratory period G′(t) continues steadily to increase. A microstructural modification is likely to occur between the dormant and the acceleratory period. At low deformations in the linearity domain the storage modulus G′(ω) exhibits a negligible frequency dependence. At higher deformations cement paste shows a yield stress which increases on increasing paste concentration. The presence of superplasticizers decreases the yield stress and increases the gelation threshold of the paste. Above the gelation threshold the evolution of cement paste with superplasticizers follows similar trends to the neat paste. -- Highlights: •The gelation of cement paste during the dormant period is analyzed via rheometry. •The observed evolution is proposed to be related to the pore structure refinement. •Similarities are observed with colloidal gels and colloidal glasses.

  8. Quantifying the distribution of paste-void spacing of hardened cement paste using X-ray computed tomography

    Energy Technology Data Exchange (ETDEWEB)

    Yun, Tae Sup, E-mail: taesup@yonsei.ac.kr [School of Civil and Environmental Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul, 120-749 (Korea, Republic of); Kim, Kwang Yeom, E-mail: kimky@kict.re.kr [Korea Institute of Construction Technology, 283 Goyangdae-ro, Ilsanseo-gu, Goyang, 411-712 (Korea, Republic of); Choo, Jinhyun, E-mail: jinhyun@stanford.edu [Department of Civil and Environmental Engineering, Stanford University, Stanford, CA 94305 (United States); Kang, Dong Hun, E-mail: timeriver@naver.com [School of Civil and Environmental Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul, 120-749 (Korea, Republic of)

    2012-11-15

    The distribution of paste-void spacing in cement-based materials is an important feature related to the freeze-thaw durability of these materials, but its reliable estimation remains an unresolved problem. Herein, we evaluate the capability of X-ray computed tomography (CT) for reliable quantification of the distribution of paste-void spacing. Using X-ray CT images of three mortar specimens having different air-entrainment characteristics, we calculate the distributions of paste-void spacing of the specimens by applying previously suggested methods for deriving the exact spacing of air-void systems. This methodology is assessed by comparing the 95th percentile of the cumulative distribution function of the paste-void spacing with spacing factors computed by applying the linear-traverse method to 3D air-void system and reconstructing equivalent air-void distribution in 3D. Results show that the distributions of equivalent void diameter and paste-void spacing follow lognormal and normal distributions, respectively, and the ratios between the 95th percentile paste-void spacing value and the spacing factors reside within the ranges reported by previous numerical studies. This experimental finding indicates that the distribution of paste-void spacing quantified using X-ray CT has the potential to be the basis for a statistical assessment of the freeze-thaw durability of cement-based materials. - Highlights: Black-Right-Pointing-Pointer The paste-void spacing in 3D can be quantified by X-ray CT. Black-Right-Pointing-Pointer The distribution of the paste-void spacing follows normal distribution. Black-Right-Pointing-Pointer The spacing factor and 95th percentile of CDF of paste-void spacing are correlated.

  9. Potentiometric Determination of Free Chloride in Cement Paste – an ...

    African Journals Online (AJOL)

    ... cement paste.16 The accuracy and reliability of this analytical technique has been checked against a certified reference material, Merck sodium chloride solution. Confidence levels (CL0.95), of 0.03 and relative standard deviations of 0.2 % for chloride were determined for ordinary Portland cement (OPC) chloride binding ...

  10. Altered cement hydration and subsequently modified porosity, permeability and compressive strength of mortar specimens due to the influence of electrical current

    NARCIS (Netherlands)

    Susanto, A.; Koleva, D.A.; Van Breugel, K.

    2014-01-01

    This paper reports on the influence of stray current flow on microstructural prop-erties, i.e. pore connectivity and permeability of mortar specimens, and link these to the observed alterations in mechanical properties and cement hydration. Mortar specimens were partly submerged in water and calcium

  11. Impedance Spectroscopy Study of the Effect of Environmental Conditions on the Microstructure Development of Sustainable Fly Ash Cement Mortars.

    Science.gov (United States)

    Ortega, José Marcos; Sánchez, Isidro; Climent, Miguel Ángel

    2017-09-25

    Today, the characterisation of the microstructure of cement-based materials using non-destructive techniques has become an important topic of study, and among them, the impedance spectroscopy has recently experienced great progress. In this research, mortars with two different contents of fly ash were exposed to four different constant temperature and relative humidity environments during a 180-day period. The evolution of their microstructure was studied using impedance spectroscopy, whose results were contrasted with mercury intrusion porosimetry. The hardening environment has an influence on the microstructure of fly ash cement mortars. On one hand, the impedance resistances R₁ and R₂ are more influenced by the drying of the materials than by microstructure development, so they are not suitable for following the evolution of the porous network under non-optimum conditions. On the other hand, the impedance spectroscopy capacitances C₁ and C₂ allow studying the microstructure development of fly ash cement mortars exposed to those conditions, and their results are in accordance with mercury intrusion porosimetry ones. Finally, it has been observed that the combined analysis of the abovementioned capacitances could be very useful for studying shrinkage processes in cement-based materials kept in low relative humidity environments.

  12. Effects of the super plasticizers and the water/cement ratio on the mini-slump of Portland cement pastes

    International Nuclear Information System (INIS)

    Meirelles, J.R.; Morelli, A.C.; Baldo, J.B.

    1998-01-01

    The rheology of Portland cement concrete is dominated by the cement paste rheology. In general the rheological behavior of cement pastes is evaluated by means of the mini-slump test. In the present paper it was investigated the effect of the water/cement ratio was as of two types of superplasticizers (melamine and naftalen based) on the mini-slump of pastes of common cement pastes. (author)

  13. Experimental studies on effect of Date Seed Ash (DSA) on strength properties of cement sand mortar

    Science.gov (United States)

    Gunarani, G. I.; Chakkravarthy, S. P.

    2017-07-01

    The need for alternative material for the cement is arising and being compromised by many engineering researchers. However, the growing demand and surging prices of raw materials challenges the constructional field. India, being one of the largest agricultural economy, produces a quantitative volume of agro-waste that is being dumped. In the conventional concrete production, coarse aggregate (CA) plays an important filler material. The initial study on date seed as a replacement for CA was not successful. This study primarily focuses on Date seed ash as a replacement material for ordinary Portland cement. OPC was replaced by Date Palm Seed Ash (DPSA) in the ratio up to 10% in terms of 2% interval. The main objective of this paper was to study the variation of strength properties of mortar by DPSA in specified ratio along with curing period of 3,7,14 and 28 days. The stress strain behavior has indicated a significant improvement. The overall results indicated the increase in replacing ratio, decreases the strength properties. However the physical, chemical and mechanical properties increased gradually in strength in minimal ratio.

  14. Mechanical and chemical properties of polyvinyl alcohol modified cement mortar with silica fume used as matrix including radioactive waste

    International Nuclear Information System (INIS)

    Dakroury, A. M.

    2007-01-01

    This paper discussed the mechanical and chemical properties of polyvinyl alcohol - modified cement mortar with silica fume to assess the safety for disposal of radioactive waste. The modified cement mortars containing polyvinyl alcohol (PVA) in the presence of 10 % silica fume (SF) .The chemical reaction between polymer and cement - hydrated product were investigated by the Infrared Spectral Technology, Differential Thermal Analysis and X-ray diffraction. The leaching of 137Cs from a waste composite into a surrounding fluid has been studied .The results shown that PVA increases the strength and decreases the porosity. The increase in strength duo to the interaction of PVA with cement , may be forming some new compound that fill the pores or improve the bond between the cement . The pozzolanic reaction of the SF increases the calcium silicate hydrates in the hardening matrix composites. There is distinct change in the refinement of the pore structure in cement composites giving fewer capillary pores and more of the finer gel pores

  15. Numerical simulation of heat and mass transport during hydration of Portland cement mortar in semi-adiabatic and steam curing conditions

    OpenAIRE

    Hernandez-Bautista, E.; Bentz, D. P.; Sandoval-Torres, S.; de Cano-Barrita, P. F. J.

    2016-01-01

    A model that describes hydration and heat-mass transport in Portland cement mortar during steam curing was developed. The hydration reactions are described by a maturity function that uses the equivalent age concept, coupled to a heat and mass balance. The thermal conductivity and specific heat of mortar with water-to-cement mass ratio of 0.30 was measured during hydration, using the Transient Plane Source method. The parameters for the maturity equation and the activation energy were obtaine...

  16. Prediction of chloride ingress and binding in cement paste

    DEFF Research Database (Denmark)

    Geiker, Mette Rica; Nielsen, Erik Pram; Herforth, Duncan

    2007-01-01

    This paper summarizes recent work on an analytical model for predicting the ingress rate of chlorides in cement-based materials. An integral part of this is a thermodynamic model for predicting the phase equilibria in hydrated Portland cement. The model’s ability to predict chloride binding...... in Portland cement pastes at any content of chloride, alkalis, sulfates and carbonate was verified experimentally and found to be equally valid when applied to other data in the literature. The thermodynamic model for predicting the phase equilibria in hydrated Portland cement was introduced into an existing...... Finite Difference Model for the ingress of chlorides into concrete which takes into account its multi-component nature. The “composite theory” was then used to predict the diffusivity of each ion based on the phase assemblage present in the hydrated Portland cement paste. Agreement was found between...

  17. Ternary Blends of High Aluminate Cement, Fly ash and Blast-furnace slag for Sewerage Lining Mortar

    Science.gov (United States)

    Chao, L. C.; Kuo, C. P.

    2018-01-01

    High aluminate cement (HAC), fly ash (FA) and blast-furnace slag (BFS) have been treated sustainable materials for the use of cement products for wastewater infrastructure due to their capabilities of corrosion resistance. The purpose of this study is to optimize a ternary blend of above mentioned materials for a special type of mortar for sewerage lining. By the using of Taguchi method, four control parameters including water/cementitious material ratio, mix water content, fly ash content and blast-furnace slag content were considered in nine trial mix designs in this study. By evaluating target properties including (1) maximization of compressive strength, (2) maximization of electricity resistance and (3) minimization of water absorption rate, the best possible levels for each control parameter were determined and the optimal mix proportions were verified. Through the implementation of the study, a practical and completed idea for designing corrosion resistive mortar comprising HAC, FA and BSF is provided.

  18. The applicability of alkaline-resistant glass fiber in cement mortar of road pavement: Corrosion mechanism and performance analysis

    Directory of Open Access Journals (Sweden)

    Qin Xiaochun

    2017-11-01

    Full Text Available The main technical requirements of road pavement concrete are high flexural strength and fatigue durability. Adding glass fiber into concrete could greatly increase flexural strength and wearing resistance of concrete. However, glass fiber has the great potential of corrosion during the cement hydration, which will directly affect the long-term performance and strength stability. In this paper, accelerated corrosion experiments have been done to find out the corrosion mechanism and property of alkali-resistant glass fiber in cement mortar. The applicability and practicability of alkaline-resistant glass fiber in road concrete have been illustrated in the analysis of flexural strength changing trend of cement mortar mixed with different proportions of activated additives to protect the corrosion of glass fiber by cement mortar. The results have shown that a 30% addition of fly ash or 10% addition of silica fume to cement matrix could effectively improve the corrosion resistance of alkali-resistant glass fiber. The optimal mixing amount of alkali-resistant glass fiber should be about 1.0 kg/m3 in consideration of ensuring the compressive strength of reinforced concrete in road pavement. The closest-packing method has been adopted in the mixture ratio design of alkali-resistant glass fiber reinforced concrete, not only to reduce the alkalinity of the cement matrix through large amount addition of activated additives but also to greatly enhance the flexural performance of concrete with the split pressure ratio improvement of 12.5–16.7%. The results suggested a prosperous application prospect for alkaline-resistant glass fiber reinforced concrete in road pavement.

  19. Hydration of fly ash cement and microstructure of fly ash cement pastes

    Energy Technology Data Exchange (ETDEWEB)

    Shiyuan, H.

    1981-01-01

    The strength development and hydration of fly ash cement and the influence of addition of gypsum on those were studied at normal and elevated temperatures. It was found that an addition of a proper amount of gypsum to fly ash cement could accelerate the pozzolanic reaction between CH and fly ash, and as a result, increase the strength of fly ash cement pastes after 28 days.

  20. The degree of hydration assessment of blended cement pastes by differential thermal and thermogravimetric analysis. Morphological evolution of the solid phases

    International Nuclear Information System (INIS)

    Monteagudo, S.M.; Moragues, A.; Gálvez, J.C.; Casati, M.J.; Reyes, E.

    2014-01-01

    Highlights: • A proposal of hydration degree calculation for blended cement pastes is presented. • The method is based both on the contributions of various authors and on DTA–TG results. • Paste and mortar specimens with BFS, FA and SF mineral admixtures were used. • The evaluation of CH gives information on hydration and pozzolanic reactions. • The assessment of α provides an insight into future strength evolution. - Abstract: The degree of hydration assessment of cement paste from differential thermal and thermogravimetric analysis data has been performed by several authors that have offered a number of proposals for technical application to blended cements. In this paper, two calculation methods are studied in detail. Then, a proposal of the degree of hydration calculation for blended cements, based on the analysis of experimental results of DTA–TG, is presented. The proposed method combines the contributions of the authors and allows straightforward calculation of the degree of hydration from the experimental results. Validation of the methodology was performed by macroscopic and microstructural tests through paste and mortar specimens with blast furnace slag, flying ash and silica fume mineral admixtures bei(g)ng used. Tests of scanning electron microscopy with an energy dispersive analyser on paste specimens, and of mechanical strength on mortar specimens with the same percentages of substitution, were performed. They showed good agreement with the information derived from the differential thermal and thermogravimetric analysis data

  1. Damage identification in cement paste amended with carbon nanotubes

    Science.gov (United States)

    Soltangharaei, Vafa; Anay, Rafal; Assi, Lateef; Ziehl, Paul; Matta, Fabio

    2018-04-01

    Cement-based composites have been used as reliable materials in building and civil engineering infrastructure for many decades. Although there are several advantages, some drawbacks such as premature cracking may be problematic for sensitive applications such as those found in nuclear power plants or associated waste storage facilities. In this study, acoustic emission monitoring was employed to detect stress waves associated with damage progression during uniaxial compressive loading. Acoustic emission data resulting from loading of plain cement paste prisms and cement paste prisms amended with carbon nanotubes are compared. Unsupervised pattern recognition is employed to categorize the data. Results indicate that increased acoustic emission activity was recorded for the plain cement paste prisms when compared to prisms amended with carbon nanotubes.

  2. Influence of recycled polystyrene beads on cement paste properties

    Directory of Open Access Journals (Sweden)

    Maaroufi Maroua

    2018-01-01

    Full Text Available In order to keep up with the requirements of sustainable development, there is a growing interest towards reducing the energy consumption in the construction and rehabilitation of buildings and the promotion of recycling waste in building materials. The use of recycled polystyrene beads in cement-based materials composition constitutes a solution to improve the insulation in buildings. This allows also limiting landfill by reusing the polystyrene waste. The aim of this study is to compare some properties and performances of a cement paste containing polystyrene beads to a reference paste designed with only the same cement. An experimental campaign was conducted and the obtained results showed that adding recycled polystyrene beads to a cement paste improves its hygro-thermal properties. Further studies are however necessary to better understand the real role of the polystyrene beads in the heat and mass transfers.

  3. Cement mortar-degraded spinney waste composite as a matrix for immobilizing some low and intermediate level radioactive wastes: Consistency under frost attack

    International Nuclear Information System (INIS)

    Eskander, S.B.; Saleh, H.M.

    2012-01-01

    Highlights: ► Spinney fiber is one of the wastes generated from spinning of cotton raw materials. ► Cement mortar composite was hydrated by using the degraded slurry of spinney wastes. ► Frost resistance was assessed for the mortar-degraded spinney waste composite specimens. ► SEM image, FT-IR and XRD patterns were performed for samples subjected to frost attack. - Abstract: The increasing amounts of spinning waste fibers generated from cotton fabrication are problematic subject. Simultaneous shortage in the landfill disposal space is also the most problem associated with dumping of these wastes. Cement mortar composite was developed by hydrating mortar components using the waste slurry obtained from wet oxidative degradation of these spinney wastes. The consistency of obtained composite was determined under freeze–thaw events. Frost resistance was assessed for the mortar composite specimens by evaluating its compressive strength, apparent porosity and mass loss at the end of each period of freeze–thaw up to 45 cycles. Scanning electron microscopy, infrared spectroscopy and X-ray diffraction analyses were performed for samples subjected to frost attack aiming at evaluating the cement mortar in the presence of degraded spinney waste. The cement mortar composite exhibits acceptable resistance and durability against the freeze–thaw treatment that could be chosen in radioactive waste management as immobilizing agent for some low and intermediate level radioactive wastes.

  4. Microstructure of hydrated cement pastes as determined by SANS

    International Nuclear Information System (INIS)

    Sabine, T.; Bertram, W.; Aldridge, L.

    1999-01-01

    Full text: Technologists have known how to make concrete for over 2000 years but despite painstaking research no one has been able to show how and why concrete sets. Part of the problem is that the calcium silicate hydrate (the gel produced by hydrating cement) is amorphous and cannot be characterised by x-ray crystallographic techniques. Small angle neutron scattering on instrument V12a at BENSC was used to characterise the hydration reactions and show the growth of the calcium silicate hydrates during initial hydration and the substantial differences in the rate of growth and structure as different additives are used. SANS spectra were measured as a function of the hydration from three different types of cement paste: 1) Ordinary Portland Cement made with a water to cement ratio of about 0.4; 2) A blend of Ordinary Portland Cement(25%) and Ground Granulated Blast Furnace Slag (75%) with a water to cement ration of about 0.4; 3) A dense paste made from silica fume(24%), Ordinary Portland Cement (76%) at a water to powder ratio of 0.18. The differences in the spectra are interpreted in terms of differences between the microstructure of the pastes

  5. Effect of the leaching of calcium hydroxide from cement paste on mechanical and physical properties

    International Nuclear Information System (INIS)

    Carde, C.; Francois, R.

    1997-01-01

    This paper deals with the effect of the leaching process of cement based materials on their mechanical and physical properties. In order to characterize this effect, the authors have performed experiments on cement paste samples. The leaching process was achieved by the use of a 50% concentrate solution of ammonium nitrate. Both compression tests and water porosity tests were conducted on micro-cylinder samples (10, 12, 14 and 20 mm of diameter) because of the slow kinetics of degradation due to the leaching. The deterioration of the cement paste and the mortar exposed to the action of the ammonium nitrate was manifested by a peripheral zone of less resistance. This process induces mainly a total leaching of Ca(OH) 2 and a progressive decalcification of C-S-H which leads to a gradient of C/S ratio in the leaching zone. Both mechanical tests and water porosity tests show that there is a linear variation of the loss of strength and the increase in porosity in relation to the ratio of degraded area over total area of the sample A d /A t . It means that both compressive resistance and water porosity of the leaching zone are constant whatever the size of the degraded zone and then whatever the time of exposure to the chemical attack. So the authors could venture the hypothesis that the dissolution of calcium hydroxide is the essential parameter governing both decrease in strength and increase in porosity

  6. Irreversible dilation of NaCl contaminated lime-cement mortar due to crystallization cycles

    International Nuclear Information System (INIS)

    Lubelli, B.; Hees, R.P.J. van; Huinink, H.P.; Groot, C.J.W.P.

    2006-01-01

    The mechanism of damage occurring in NaCl contaminated materials has not been clarified yet. Apart from crystallization pressure, other hypotheses have been proposed to explain the cause of decay. Irreversible dilation has been observed in a few cases but has never been studied in a more systematic way. The aim of the research is to contribute to the modeling of this phenomenon. In the present paper the effect of NaCl on the hydric and hygric behavior of a lime-cement mortar is extensively studied. The results indicate that NaCl influences the hydric and hygric dilation behavior of the material. The material contaminated with NaCl shrinks during dissolution and dilates during crystallization of the salt. This dilation is irreversible and sufficient to damage the material after few dissolution/crystallization cycles. This behavior is not restricted to NaCl, but is observed in the presence of other salts as well (NaNO 3 and KCl). Outcomes of electron microscopy studies suggest that salts causing irreversible dilation tend to crystallize as layers on the pore wall

  7. The refilling of pores in cement mortars treated by chemicals and desiccation at different temperatures

    Directory of Open Access Journals (Sweden)

    Menéndez Pazos, Ignacio

    1992-09-01

    Full Text Available Bases under the law of solubility product, the pores of the cement mortar are refilled by impregnation with two salts that form another insoluble salt. The number of treatments to be underdone and the drying temperatures more suitable in each case. The calcium salts like impregnants and urea sodium oxalate and sugar like precipitates are employed, obtained in each case the corresponding pores are occupied, which depends generally on the number of treatments and in particular the drier temperature.

    Basados en los principios del producto de solubilidad, se rellenan los poros de las probetas de mortero de cemento por impregnación con dos sales que forman otra insoluble. Se determina el número de tratamientos a realizar y las temperaturas de secado más idóneas en cada caso. Se emplean sales cálcicas como impregnantes, y urea, oxalato sódico y azúcar como precipitantes, obteniéndose en cada caso las correspondientes ocupaciones de poros que dependen, por lo general, del número de tratamientos y, en particular, de la temperatura de secado.

  8. Spectroscopic investigation of Ni speciation in hardened cement paste.

    Science.gov (United States)

    Vespa, M; Dähn, R; Grolimund, D; Wieland, E; Scheidegger, A M

    2006-04-01

    Cement-based materials play an important role in multi-barrier concepts developed worldwide for the safe disposal of hazardous and radioactive wastes. Cement is used to condition and stabilize the waste materials and to construct the engineered barrier systems (container, backfill, and liner materials) of repositories for radioactive waste. In this study, Ni uptake by hardened cement paste has been investigated with the aim of improving our understanding of the immobilization process of heavy metals in cement on the molecular level. X-ray absorption spectroscopy (XAS) coupled with diffuse reflectance spectroscopy (DRS) techniques were used to determine the local environment of Ni in cement systems. The Ni-doped samples were prepared at two different water/cement ratios (0.4, 1.3) and different hydration times (1 hour to 1 year) using a sulfate-resisting Portland cement. The metal loadings and the metal salts added to the system were varied (50 up to 5000 mg/kg; NO3(-), SO4(2-), Cl-). The XAS study showed that for all investigated systems Ni(ll) is predominantly immobilized in a layered double hydroxide (LDH) phase, which was corroborated by DRS measurements. Only a minor extent of Ni(ll) precipitates as Ni-hydroxides (alpha-Ni(OH)2 and beta-Ni(OH)2). This finding suggests that Ni-Al LDH, rather than Ni-hydroxides, is the solubility-limiting phase in the Ni-doped cement system.

  9. Re-use of drinking water treatment plant (DWTP) sludge: Characterization and technological behaviour of cement mortars with atomized sludge additions

    International Nuclear Information System (INIS)

    Husillos Rodriguez, N.; Martinez Ramirez, S.; Blanco Varela, M.T.; Guillem, M.; Puig, J.; Larrotcha, E.; Flores, J.

    2010-01-01

    This paper aims to characterize spray-dried DWTP sludge and evaluate its possible use as an addition for the cement industry. It describes the physical, chemical and micro-structural characterization of the sludge as well as the effect of its addition to Portland cements on the hydration, water demand, setting and mechanical strength of standardized mortars. Spray drying DWTP sludge generates a readily handled powdery material whose particle size is similar to those of Portland cement. The atomized sludge contains 12-14% organic matter (mainly fatty acids), while its main mineral constituents are muscovite, quartz, calcite, dolomite and seraphinite (or clinoclor). Its amorphous material content is 35%. The mortars were made with type CEM I Portland cement mixed with 10 to 30% atomized sludge exhibited lower mechanical strength than the control cement and a decline in slump. Setting was also altered in the blended cements with respect to the control.

  10. Green and early age compressive strength of extruded cement mortar monitored with compression tests and ultrasonic techniques

    International Nuclear Information System (INIS)

    Voigt, Thomas; Malonn, Tim; Shah, Surendra P.

    2006-01-01

    Knowledge about the early age compressive strength development of cementitious materials is an important factor for the progress and safety of many construction projects. This paper uses cylindrical mortar specimens produced with a ram extruder to investigate the transition of the mortar from plastic and deformable to hardened state. In addition, wave transmission and reflection measurements with P- and S-waves were conducted to obtain further information about the microstructural changes during the setting and hardening process. The experiments have shown that uniaxial compression tests conducted on extruded mortar cylinders are a useful tool to evaluate the green strength as well as the initiation and further development of the compressive strength of the tested material. The propagation of P-waves was found to be indicative of the internal structure of the tested mortars as influenced, for example, by the addition of fine clay particles. S-waves used in transmission and reflection mode proved to be sensitive to the inter-particle bonding caused by the cement hydration and expressed by an increase in compressive strength

  11. Changes in Properties of Cement and Lime Mortars When Incorporating Fibers from End-of-Life Tires

    Directory of Open Access Journals (Sweden)

    Lluís Gil

    2016-02-01

    Full Text Available This paper studies the addition of fibers from end-of-life tires to commercial mortar mixtures. Two different types of mortar, one lime-plastic and other cement-fluid, are mixed with different percentage of fibers ranging from 0% to 1%. The changes in bulk density, consistency, compressive and flexural strength, dynamic Young modulus and water absorption are studied. According to the results, consistency is the property that shows more relevant changes for an addition of 0.25% fibers. Consistency is related to workability and affects the water absorption and the Young modulus values. On the contrary, bulk density and mechanical properties did not change with the addition of fibers. The results prove that this fiber, considered a waste from recycling of end-of-life tires, can be used in commercial mixtures without losing strength. On the other hand, mortar workability limits the amount of fibers that can be included in the mixture and this parameter determines the performance of the mortar.

  12. Thermal analysis of cement pastes with superabsorbent polymers

    DEFF Research Database (Denmark)

    Esteves, Luis Pedro; Jensen, Ole Mejlhede; Lukosiute, Irena

    2013-01-01

    Thermal analysis of cement systems is very helpful in the understanding of many different properties of cementitious compounds, both for the original reacting compounds, and also for the resulting hydration products. Superabsorbent polymers can be added to cement systems with many different reasons......, so it is relevant that fundamental knowledge of this new compound on the development of hydration is well understood [1-3]. This paper reports research on thermal analysis of cement pastes with superabsorbent polymers. We have studied several parameters: the concentration of SAP in the system......, the effect of particle size distribution, and their influence on the hydration process with focus on cement-silica systems. This is done at different thermodynamic conditions, so the energy of activation in the different systems can be accessed. This paper provides information relevant to hydration modelling...

  13. Effect of various Portland cement paste compositions on early-age strain

    Science.gov (United States)

    Guzzetta, Alana G.

    Early-age strain in paste, mortar, and concrete mixtures was investigated using a new method where the specimen shape was a cone frustum. Strain of the specimen from both the horizontal and vertical directions was captured by height change measurement. The volumetric strain was then calculated as a function of the height change and was plotted versus time. A correlation was found between the slopes of the volumetric strain curve resulting from this test method and the initial setting time of the tested material. An initial evaluation of the repeatability of this innovative test method was conducted. The early-age strain effects of aggregate volume, shrinkage reducing admixture, water-cementitious ratio (w/cm), and partial cement replacement with supplementary cementitious materials were tested and individually compared. From these comparisons, it was observed that ambient temperature, bleed water development, and rheological properties had a significant impact on the volumetric strain results. Data showed increased strain as aggregate volume was reduced and as the w/cm was changed from 0.25 up to 0.50. The addition of shrinkage reducing admixture generally caused an increase in the 36-hour volumetric strain value. In most of the mixtures, cement replacement with 20% fly ash or 10% metakaolin reduced the measured volumetric strain when the w/cm was 0.30. Replacement of cement with 10% silica fume caused an insignificant change in volumetric strain results.

  14. Influence of clinker grinding-aids on the intrinsic characteristics of cements and on the behaviour of mortars

    Directory of Open Access Journals (Sweden)

    Fernández Luco, L.

    2003-12-01

    Full Text Available In the production of portland cement, grinding aids are used to improve the grinding stage and reduce the energy required to achieve the required fineness. These additives remain in the final product and they might influence the characteristics and properties of the cement, and thus, mortar and concrete. This paper presents an evaluation of two grinding-aid additives used in the production of portland cement ground in a ball mill at a laboratory stage, with suitable proportions of portland cement clinker and gypsum. A control cement mix was also produced without using any admixture and the results are shown on a comparative basis. Conclusions indicate that grinding-aids additives have some influence on the characteristics of portland cement produced, increasing their specific surface and modifying microstructure and its packing ability. Mortars and concretes made with cements ground with the addition of gringing-aids exhibit higher strength at any age and a reduced water demand. Special attention should be taken to consider any interaction with water-reducing admixture in concretes and mortars.

    En la fabricación de cemento portland es una práctica creciente la utilización de aditivos para optimizar el proceso de molienda; éstos quedan incorporados en el producto final y pueden influir sobre las características y propiedades del cemento, morteros y hormigones. En este trabajo se presenta la evaluación de dos aditivos comerciales en la molienda conjunta de clínker de cemento portland y yeso comercial, tratados en un molino a bolas a escala de laboratorio, en forma comparativa con un cemento sin aditivo producido en forma equivalente. Las conclusiones indican que los aditivos de molienda tienen influencia en las características del cemento resultante, incrementando su superficie y modificando su microestructura y estado de agregación; los morteros mejoran sus prestaciones mecánicas a todas las edades y se reduce la demanda de agua

  15. Evaluation of red mud as pozzolanic material in replacement of cement for production of mortars; Avaliacao da lama vermelha como material pozolanico em substituicao ao cimento para producao de argamassas

    Energy Technology Data Exchange (ETDEWEB)

    Manfroi, E.P.; Cheriaf, M.; Rocha, J.C., E-mail: elizmanfroi@yahoo.com.b, E-mail: malik@valores.ufsc.b [Universidade Federal de Santa Catarina (UFSC), Florianopolis, SC (Brazil). Dept. de Engenharia Civil

    2010-07-01

    Red mud is a by-product of the alkaline extraction of aluminum from the bauxite and represents a renewed environmental problem due the significant annual throughput by the plants. In the present work, the pozzolanic properties of Brazilian red mud fired at 600, 700, 800 and 900 deg C were investigated by monitoring lime consumption using DTA analysis and Brazilian standard methodology NBR 5772 (1992). Products and kinetics of hydration were determined in cement pastes produced with 5 and 15% red mud using x-ray diffraction and DTA analysis. Compressive strength and capillary absorption tests were realized on mortars constituted by 5, 10 and 15% red mud in replacement of cement. When calcined at 600 deg C, the red mud develops good pozzolanic properties, and the compressive strength of mortars produced with this waste meet values in accordance with regulatory standard. These results shown than red mud can be used, in partial replacement of cement, as new construction material to produce sustainable mortars with low environmental impact. (author)

  16. Heat of hydration measurements on cemented radioactive wastes. Part 1: cement-water pastes

    International Nuclear Information System (INIS)

    Lee, D.J.

    1983-12-01

    This report describes the hydration of cement pastes in terms of chemical and kinetic models. A calorimetric technique was used to measure the heat of hydration to develop these models. The effects of temperature, water/cement ratio and cement replacements, ground granulated blast furnace slag (BFS) and pulverised fuel ash (PFA) on the hydration of ordinary Portland cement (OPC) is reported. The incorporation of BFS or PFA has a marked effect on the hydration reaction. The effect of temperature is also important but changing the water/cement ratio has little effect. Results from cement pastes containing only water and cement yield total heats of reaction of 400, 200 and 100 kJ/kg for OPC, BFS and PFA respectively. Using the results from the models which have been developed, the effect of major salts present in radioactive waste streams can be assessed. Values of the total heat of reaction, the time to complete 50 percent reaction, and the energy of activation, can be compared for different waste systems. (U.K.)

  17. Engineering properties of cement mortar with pond ash in South Korea as construction materials: from waste to concrete

    Science.gov (United States)

    Jung, Sang Hwa; Kwon, Seung-Jun

    2013-09-01

    Among the wastes from coal combustion product, only fly ash is widely used for mineral mixture in concrete for its various advantages. However the other wastes including bottom ash, so called PA (pond ash) are limitedly reused for reclamation. In this paper, the engineering properties of domestic pond ash which has been used for reclamation are experimentally studied. For this, two reclamation sites (DH and TA) in South Korea are selected, and two domestic PAs are obtained. Cement mortar with two different w/c (water to cement) ratios and 3 different replacement ratios (0%, 30%, and 60%) of sand are prepared for the tests. For workability and physical properties of PA cement mortar, several tests like flow, setting time, and compressive strength are evaluated. Several durability tests including porosity measuring, freezing and thawing, chloride migration, and accelerated carbonation are also performed. Through the tests, PA (especially from DH area) in surface saturated condition is evaluated to have internal curing action which leads to reasonable strength development and durability performances. The results show a potential applicability of PA to concrete aggregate, which can reduce consuming natural resources and lead to active reutilization of coal product waste.

  18. Influence of supplementary cementitious materials on water transport kinetics and mechanical properties of hydrated lime and cement mortars

    Directory of Open Access Journals (Sweden)

    Ince, C.

    2015-06-01

    Full Text Available The purpose of this paper is an investigation of the possible role of supplementary cementitious materials (SCMs on water transport kinetics and mechanical properties of hydrated lime (CL90 and Portland cement (PC mortars. The properties of hydrated lime are significantly different from those of cement and therefore modifying fresh and hardened properties of these mortars are vital for mortar/substrate optimisation in masonry construction. The parameters investigated in this paper often are the main barriers to the use of hydrated lime in construction practice. The results show that transfer sorptivity and time to dewater freshly-mixed hydrated lime mortars can be modified when binder is partially replaced with SCMs. Compressive strength of CL90 mortars is increased systematically with the increased replacement levels of SCMs and the results are supported with the microstructural images. The ability to modify the water transport kinetics and mechanical properties allows compatibility between the mortar and the substrate unit in masonry construction.El objetivo de este artículo es investigar el papel de los materiales cementantes suplementarios (SCMs en la cinética de transporte del agua y en las propiedades mecánicas de los morteros de cal hidratada (CL90 y cemento Portland. Las propiedades de la cal hidratada son significativamente diferentes a las del cemento y por lo tanto el control de las propiedades de los morteros frescos y endurecidos es fundamental en la optimización mortero/substrato en albañilería. Los parámetros estudiados en este trabajo son a menudo las principales barreras para el uso de la cal hidratada en la práctica de la construcción. Los resultados indican que la absortividad y el tiempo necesario para deshidratar morteros de cal hidratada recién mezclados pueden ser controlados cuando el conglomerante es parcialmente remplazado por SCMs. La resistencia a compresión de los morteros CL90 aumenta sistem

  19. Predicting the drying shrinkage behavior of high strength portland cement mortar under the combined influence of fine aggregate and steel micro fiber

    International Nuclear Information System (INIS)

    Li, Zhengqi

    2017-01-01

    The workability, 28-day compressive strength and free drying shrinkage of a very high strength (121-142 MPa) steel micro fiber reinforced portland cement mortar were studied under a combined influence of fine aggregate content and fiber content. The test results showed that an increase in the fine aggregate content resulted in decreases in the workability, 28-day compressive strength and drying shrinkage of mortar at a fixed fiber content. An increase in the fiber content resulted in decreases in the workability and drying shrinkage of mortar, but an increase in the 28-day compressive strength of mortar at a fixed fine aggregate content. The modified Gardner model most accurately predicted the drying shrinkage development of the high strength mortars, followed by the Ross model and the ACI 209R-92 model. The Gardner model gave the least accurate prediction for it was developed based on a database of normal strength concrete. [es

  20. Predicting the drying shrinkage behavior of high strength portland cement mortar under the combined influence of fine aggregate and steel micro fiber

    Directory of Open Access Journals (Sweden)

    Zhengqi Li

    2017-03-01

    Full Text Available The workability, 28-day compressive strength and free drying shrinkage of a very high strength (121-142 MPa steel micro fiber reinforced portland cement mortar were studied under a combined influence of fine aggregate content and fiber content. The test results showed that an increase in the fine aggregate content resulted in decreases in the workability, 28-day compressive strength and drying shrinkage of mortar at a fixed fiber content. An increase in the fiber content resulted in decreases in the workability and drying shrinkage of mortar, but an increase in the 28-day compressive strength of mortar at a fixed fine aggregate content. The modified Gardner model most accurately predicted the drying shrinkage development of the high strength mortars, followed by the Ross model and the ACI 209R-92 model. The Gardner model gave the least accurate prediction for it was developed based on a database of normal strength concrete.

  1. Characterization of cement paste as engineered barrier of borehole repository

    International Nuclear Information System (INIS)

    Ferreira, Eduardo G.A.; Isiki, Vera L. K.; Miyamoto, Hissae; Marumo, Julio T.; Vicente, Roberto

    2009-01-01

    Results of axial rupture by compression of cylindrical cement paste samples are presented. This is part of a research on cement paste behavior aiming at investigating the durability of cementitious materials in the environment of repositories for radioactive waste. Portland cement paste is intended to be used as a backfill in a deep borehole for disposal of sealed radiation sources which concept is under development. The service life of the engineered barrier materials plays an important role in the long term safety of such facilities. Accelerated tests in laboratory are being used to evaluate the performance of cement paste under the temperature expected at some hundred meters below grade, under exposure to the radiation emitted by the sources, and under the attack of aggressive chemicals dissolved in the groundwater, during the millennia necessary for the decay of the most active and long-lived radionuclides present in the waste. The large variability in results of mechanical strength as measured by axial compression of cylindrical samples is the subject of this short communication. (author)

  2. Natural radioactivity levels and danger ratio in cements, concretes and mortars used in construction; Determinacion de niveles radiactivos naturales e indices de peligrosidad en cementos, hormigones y morteros utilizados en construccion

    Energy Technology Data Exchange (ETDEWEB)

    Meneses, J.; Pacheco, C.; Avila, J. M.; Miro, C.

    2010-07-01

    We have determined the natural radiation level in three types of adhesive cements, five types of concrete and two types of mortars of different strength normally used in the construction field. Of these materials, both concrete and mortars were prepared in our laboratories, cements the contrary were of a commercial nature.

  3. Evaluation of compatible mortars to repair 19th century natural cement cast stone from the French Rhône-Alpes region

    Directory of Open Access Journals (Sweden)

    Myriam Bouichou

    2008-01-01

    Full Text Available In France, natural cements were extensively produced in the middle of the 19th century. In the French Alps, due to their ochre color, these cements were massively used, notably to produce cast stone, to simulate natural freestone. A preliminary survey revealed an overall good state of preservation of the buildings of this period. Two kinds of decays mechanisms were however identified : erosion affecting the surface of the majority of the buildings, inducing a gradual disappearance of the initial "fake-stone aspect", and a spalling phenomenon often combined with salts crystallization, observed only on a few buildings. Today, due to a lack of appropriate repair materials, the rehabilitation of these buildings mainly consists in the use of gray Portland-cement-based-mortars combined with a painting finishing, which is not satisfactory considering the conservation deontology, as the original appearance is lost. Therefore, the aim of this project was to develop and to test compatible repair materials to restore the culture heritage of this region. Based on the preliminary characterization of a set of representative ancient buildings, combined to a literature review, specifications concerning the composition and the main properties of repair materials, which could assure a compatibility with the ancient concrete of the region were established. Then, three Prompt-cement and one Portland-cement based mortars were selected, two of them being specifically formulated. Firstly, the appearance, the workability and the mechanical and physical properties of those mortars were characterized. Secondly, to evaluate the compatibility of the selected mortars with ancient concrete, Prompt-cement-based slabs were cast using a 19th century concrete formula, and were artificially eroded. After applying the 4 mortars on the slabs, visual observations and pull-out tests will be carried out before and after artificial aging. Finally, the repair mortar presenting the best

  4. Resonant frequency and elastic modulus measurements on hardened cement pastes

    International Nuclear Information System (INIS)

    Lee, D.J.

    1982-12-01

    A new technique for measuring resonant frequency and elastic modulus is described. This has been used on specimens of hardened cement paste containing water with no simulated waste, and the results compared with measurements of ultrasonic pulse velocity, dimensional movements and compressive strength made on the same formulations. In addition, measurements were made on a specimen containing simulated waste which demonstrated the applicability of the new technique for following the development of the mechanical properties of cemented simulant radioactive waste in the laboratory. (U.K.)

  5. Modifications induced by adding natural zeolitic pozzolans to cement paste

    Directory of Open Access Journals (Sweden)

    Blanco-Varela, M. T.

    2005-12-01

    Full Text Available Volcanic pozzolans owe their pozzolanic activity chiefly to the presence of vitreous or zeolitic material rich in SiO2, and Al20y compounds that react with the portlandite produced during cement hydration to generate amorphous gels with cementitious properties. The present study analyzes the modifications taking place in the composition, structure and micro structure of the hydra ted cement paste when 20% of the cement by weight is replaced by two finely ground zeolitic rocks from Cuban deposits. Hydrated cement pastes were prepared with a CEM I35 cement, as well as with mixes of the cement and two Cuban zeolitic rocks (20% by weight. After eight months of hydration, the pastes were characterized -mineralogically, chemically and microstructurally- with XRD, FTIR, 29Si and 27Al MAS NMR, DTA/TG, back scattered electron microscopy and mercury porosimetry techniques. The replacement of 20% by weight of the cement with two finely ground zeolitic rocks significantly modified the composition, structure, quantity and microstructure of the hydrated cement paste reaction product. The C-S-H gel formed in these pastes differed in quantity, which was larger, and composition from the original cement gel. Moreover, the gel formed in addition-free cement had a higher Ca and a lower Al content and shorter silicate chains than the C-S-H product formed in the pastes made with zeolitic rocks. Finally, the pastes with pozzolan additions had fewer and smaller pores.

    La actividad de las puzolanas de origen volcánico procede fundamentalmente de la presencia de material vitreo o zeolítico rico en SiO2 y Al2Oy que son los que reaccionan con la portlandita producida en la hidratación del cemento generando geles amorfos con propiedades cementantes. El objetivo del presente trabajo es estudiar las modificaciones que produce la sustitución del 20% en peso de cemento por dos

  6. Porosity study on free mineral addition cement paste

    International Nuclear Information System (INIS)

    Salgueiro, W.; Somoza, A.; Cabrera, O.; Consolati, G.

    2004-01-01

    A study of the hydration process and the porosity evolution in a cement paste is presented. The analysis of porosity was made in samples with water to cement ratios (w/c) of 0.24, 0.40 and 0.60 at age of 3, 7, 28 and 365 days, respectively. Information on the evolution of total porosity and on the strength of the paste were obtained using positron annihilation lifetime spectroscopy (PALS), scanning electron microscopy (SEM), X-ray diffraction (XRD), mechanical tests (compression and flexion) and water absorption techniques. Specifically, positron lifetime technique allowed us to analyze the evolution of gel and capillary porosity during the hydration process. Using a simple function proposed, reasonable fits to the experimental data of the porosity evolution as a function of the compression strength were obtained

  7. Coupling between mechanical behaviour and drying of cementing materials: experimental study on mortars; Couplage comportement mecanique et dessiccation des materiaux a matrice cimentaire: etude experimentale sur mortiers

    Energy Technology Data Exchange (ETDEWEB)

    Yurtdas, I

    2003-10-15

    The aim of this work is to understand the desiccation effects on the mechanical behaviour of cement materials. Two mortars of ratio E/C=0.5 and 0.8 have been tested. All the tests have been implemented after a six months maturing in water. The experimental study has been carried out as follows: 1)tests characterizing the differed behaviour and the transport properties have been carried out 2)tests characterizing the short term multiaxial mechanical behaviour have been carried out. The desiccation shrinkage in terms of the weight loss presents three characteristic phases. The permeability measurement on the mortar 05 shows that the permeability of the specimens dried and crept is greater than those of the specimens dried before being crept, and the permeability of the specimens submitted to a desiccation creep and then dried is sensibly the same as the last one in spite of a very important differed deformation. The influence of the desiccation on the uniaxial and deviatoric compressions resistance depends of the binding agent: for a cement paste of good quality (E/C=0.5), the resistances increase with the desiccation because of the capillary depression and of the hydric gradients. For a cement paste of low quality (E/C=0.8), there is a competitive effect between the increase of the microcracks induced and the specimen rigidification; the microcracking becomes then the parameter controlling the rupture process. The elasto-plastic behaviour becomes a damageable elasto-plastic behaviour during desiccation which induces, as the decrease of the E/C ratio, a translation of the elastic limit surfaces and ruptures towards higher stresses. In parallel, the elastic properties and the incompressibility modulus are damaged and the volume deformations increase after the drying. At last, the decrease of the Young modulus and the passage to the third shrinkage phase in terms of the weight loss coincide. This can be attributed to the induced microcracking: this decrease of the

  8. Behavior of cement paste as backfill in waste disposal boreholes

    International Nuclear Information System (INIS)

    Ferreira, Eduardo G.A.; Isiki, Vera L.K.; Miyamoto, Hissae; Marumo, Julio T.; Vicente, Roberto

    2011-01-01

    The Radioactive Waste Management Laboratory (GRR) at the Nuclear and Energy Research Institute (IPEN) in Sao Paulo, Brazil, is developing the concept a repository for disposition of disused sealed radioactive sources in a deep borehole, aiming at providing a feasible and inexpensive alternative for final disposal. A relevant fraction of the Brazilian inventory of sources has long half-life which prevents them to be disposed of in shallow ground disposal facilities. In the concept of repository under study, Portland cement paste is intended to be used as a backfill between the steel casing and the geological formation around the borehole. Cement paste will function as structural, an additional barrier against the migration of radionuclides outside the repository, and as a blockage against the transport of water between the different strata of the geological setting. The durability of cementitious materials under the conditions prevailing at the depth of disposal is as yet unknown. The objective of this research is to investigate the behavior of the cement paste and to estimate its service life. In this paper we present the results of mechanical strength measurements and chemical and mineralogical analysis of samples to detect the changes caused by radiation, temperature and aggressive chemicals present in ground water. Techniques of analysis included Inductively Coupled Plasma Atomic Emission Spectroscopy, Ion Chromatography, X-Ray Diffraction, and Thermo-Gravimetric Analysis. (author)

  9. On estimating the effective diffusive properties of hardened cement pastes

    International Nuclear Information System (INIS)

    Stora, E.; Bary, B.; Stora, E.; He, Qi-Chang

    2008-01-01

    The effective diffusion coefficients of hardened cement pastes can vary between a few orders of magnitude. The paper aims at building a homogenization model to estimate these macroscopic diffusivities and capture such strong variations. For this purpose, a three-scale description of the paste is proposed, relying mainly on the fact that the initial cement grains hydrate forming a complex microstructure with a multi-scale pore structure. In particular, porosity is found to be well connected at a fine scale. However, only a few homogenization schemes are shown to be adequate to account for such connectivity. Among them, the mixed composite spheres assemblage estimate (Stora, E., He, Q.-C., Bary, B.: J. Appl. Phys. 100(8), 084910, 2006a) seems to be the only one that always complies with rigorous bounds and is consequently employed to predict the effects of this fine porosity on the material effective diffusivities. The model proposed provides predictions in good agreement with experimental results and is consistent with the numerous measurements of critical pore diameters issued from mercury intrusion porosimetry tests. The evolution of the effective diffusivities of cement pastes subjected to leaching is also assessed by adopting a simplified scenario of the decalcification process. (authors)

  10. [Microbial settlement of paint- and building-materials in the sphere of drinking water. 9. Communication: experimental examination of cement mortar for the lining with tiles (author's transl)].

    Science.gov (United States)

    Schoenen, D; Thofern, E

    1981-12-01

    The observation of a microbial growth in form of macrocolonies upon the joints of a tiled drinking water reservoir caused the microbiological testing of different pure mineral and some plastic containing cement mortar. Besides the conditions allowing the growth of macrocolonies on tiled plates with a construction like in a reservoir were examined.

  11. Corrosion rate of steel embedded in blended Portland and fluid catalytic cracking catalyst residue (FC3R cement mortars

    Directory of Open Access Journals (Sweden)

    Payá, J.

    2008-12-01

    Full Text Available This paper reports on a study of the corrosion levels in steel bars embedded in mortars made with a blend of Portland cement and (0-20% spent fluid catalytic cracking catalyst residue (FC3R, with a variable (0.3-0.7 water/binder (w/b ratio. The specimens were stored in the following conditions: relative humidity of 40, 80 or 100% and CO2 concentrations of 5 and 100%. The steel corrosion rate was measured with polarization resistance techniques. In the absence of aggressive agents, the steel was found to remain duly passivated in mortars with an FC3R content of up to 15% under all the conditions of relative humidity tested. The reinforcement corrosion level in mortars with a w/b ratio of 0.3 and 15% FC3R subjected to accelerated carbonation was similar to the level observed in the unblended Portland cement control mortar.En este trabajo se ha estudiado el nivel de corrosión de barras de acero embebidas en morteros de cemento Portland con relación agua/material cementante (a/mc variable (0,3-0,7, en los que parte del cemento (0-20% se sustituyó por catalizador de craqueo usado (FC3R. Las condiciones de conservación de las probetas elaboradas fueron las siguientes: distintas humedades relativas (40, 80 y 100% y dos concentraciones de CO2 (5 y 100%. La velocidad de corrosión de los aceros se midió mediante la técnica de resistencia de polarización. Se ha podido determinar que, bajo las distintas condiciones de humedad relativa y ausencia de agresivo, los aceros se mantuvieron correctamente pasivados en los morteros con contenidos de FC3R de hasta el 15%. El nivel de corrosión que presenta el refuerzo embebidos en morteros con sustitución de un 15% de cemento por FC3R y relación a/mc 0,3, al ser sometidos a un proceso de carbonatación acelerada, era muy similar al mostrado por el mortero patrón, sin FC3R.

  12. Effect of sewage sludge ash (SSA on the mechanical performance and corrosion levels of reinforced Portland cement mortars

    Directory of Open Access Journals (Sweden)

    Andión, L. G.ª

    2006-06-01

    Full Text Available The article describes a study conducted to determinecorrosion in reinforcement embedded in Portland cement(PC mortars with different percentages of sewage sludgeash (SSA admixtures. The polarization resistancetechnique was used to determine the steel corrosion rate(Icorr in the test specimens. The samples were subjectedto different environmental conditions and aggressiveagents: 100% relative humidity (RH, accelerated carbonationat 70% RH and seawater immersion. Portlandcement was partially substituted for SSA in the mixes atrates of 0, 10, 20, 30 and 60% (by mass to make thedifferent mortars. The results show that where cementwas replaced by SSA at rates of up to 10% by mass,mortar corrosion performance was comparable to thebehaviour observed in SSA-free mortars (control mortar:0% SSA. Data for higher rates are also shown. From themechanical standpoint, SSA exhibited moderate pozzolanicactivity and the best performance when SSA wasadded at a rate of 10% to mixes with a water/(binder:PC + SSA (w/b ratio of 0.5.Se ha estudiado el nivel de corrosion que presentan lasarmaduras embebidas en morteros fabricados con cementoPortland (CP con diferentes porcentajes de sustitucion deceniza de lodo de depuradora (CLD. Se ha utilizado la tecnicade la Resistencia a la Polarizacion para determinar lavelocidad de corrosion del acero embebido en las muestrasestudiadas. Las muestras se han sometido a diferentes condicionesambientales y agentes agresivos: 100% de humedadrelativa (HR, carbonatacion acelerada al 70% HR einmersion en agua de mar. Para la fabricacion de los distintosmorteros, el cemento Portland ha sido parcialmente sustituidopor CLD en los siguientes porcentajes en masa: 0,10, 20, 30 y 60%. Los resultados muestran que sustitucionesde cemento por CLD de hasta el 10% en masa no alteranel comportamiento frente a la corrosion de los morterosal compararlos con los morteros libres de CLD (morteroscontrol: 0% de sustitucion de cemento por CLD. Se

  13. Manufacturing of mortars and concretes non-traditionals, by Portland cement, metakaoline and gypsum (15.05%

    Directory of Open Access Journals (Sweden)

    Talero, R.

    1999-12-01

    Full Text Available In a thorough previous research (1, it appeared that creation, evolution and development of the values of compressive mechanical strength (CS and flexural strength (FS, measured in specimens 1x1x6cm of mortar type ASTM C 452-68 (2, manufactured by ordinary Portland cement P-1 (14.11% C3A or PY-6 (0.00% C3A, metakaolin and gypsum (CaSO4∙2H2O -or ternary cements, CT-, were similar to the ones commonly developed in mortars and concretes of OPC. This paper sets up the experimental results obtained from non-traditional mortars and concretes prepared with such ternary cements -TC-, being the portland cement/metakaolin mass ratio, as follows: 80/20, 70/30 and 60/40. Finally, the behaviour of these cements against gypsum attack, has been also determined, using the following parameters: increase in length (ΔL%, compressive, CS, and flexural, FS, strengths, and ultrasound energy, UE. Experimental results obtained from these non-traditional mortars and concretes, show an increase in length (ΔL, in CS and FS, and in UE values, when there is addition of metakaolin.

    En una exhaustiva investigación anterior (1, se pudo comprobar que la creación, evolución y desarrollo de los valores de resistencias mecánicas a compresión, RMC, y flexotracción, RMF, proporcionados por probetas de 1x1x6 cm, de mortero 1:2,75, selenitoso tipo ASTM C 452-68 (2 -que habían sido preparadas con arena de Ottawa, cemento portland, P-1 (14,11% C3A o PY- 6 (0,00% C3A, metacaolín y yeso (CaSO4∙2H2O-, fue semejante a la que, comúnmente, desarrollan los morteros y hormigones tradicionales de cemento portland. En el presente trabajo se exponen los resultados experimentales obtenidos de morteros y hormigones no tradicionales, preparados con dichos cementos ternarios, CT, siendo las proporciones porcentuales en masa ensayadas, cemento portland/metacaolín, las siguientes: 80/20, 70

  14. ThE EFFECT OF METAKOLIN, MICROSILICA AND NANOSILICA ON THE MECHANICAL PROPERTIES AND MICROSTRUCTURE OF CEMENT MORTAR

    Directory of Open Access Journals (Sweden)

    H. R. Sobhani Kavkani

    2016-06-01

    Full Text Available Different mineral admixtures of Indian metakaolin, Iranian silica fume and nanosilica were used to produce high performance mortars. Two different sands types with grain size of 0.015-4mm were mixed with type II Portland cement, polycarboxylate superplasticizer,mineral admixture with 650kg/m3 cement content and water/cement ratio of 0.35. Different amount of cement was replaced by metakaolin or silica fume (5-15wt% or nanosilica (0.8-5wt%. After mixing, moulding and curing, compressive strength, electrical resistivity and abrasion resistance were studied. The maximum compressive strength of 28 days samples were 76MPa, 79MPa and 75MPa for 15wt% substitution of cement with metakaolin, silica fume and 5wt% with nanosilica. The compressive strength of these samples showed 28%, 33% and 26% increment in comparison with reference sample, respectively. X-ray patterns showed that replacing silica fume leads to reduction of Portlandite (Ca(OH2 phase. This can be attributed to the pozzolanic reaction and formation of new hydrated calcium silicate phase (CSH that caused improvement of strength of admixtures containing samples. The microstructure of silica fume containing sample also showed better bond between sand and matrix. The electrical resistivity of samples with 15wt% metakaolin or silica fume and 5wt% nanosilica reach to 21kΩ.cm, 15 kΩ.cm and 10kΩ.cm, respectively. These samples showed high durability and corrosion resistance relative to reference samples (3.4 kΩ.cm. The abrasion resistance of different admixtures, specially silica fume containing samples were improved.

  15. PROPERTIES AND MICROSTRUCTURE OF CEMENT PASTE INCLUDING RECYCLED CONCRETE POWDER

    Directory of Open Access Journals (Sweden)

    Jaroslav Topič

    2017-02-01

    Full Text Available The disposal and further recycling of concrete is being investigated worldwide, because the issue of complete recycling has not yet been fully resolved. A fundamental difficulty faced by researchers is the reuse of the recycled concrete fines which are very small (< 1 mm. Currently, full recycling of such waste fine fractions is highly energy intensive and resulting in production of CO2. Because of this, the only recycling methods that can be considered as sustainable and environmentally friendly are those which involve recycled concrete powder (RCP in its raw form. This article investigates the performance of RCP with the grain size < 0.25 mm as a potential binder replacement, and also as a microfiller in cement-based composites. Here, the RCP properties are assessed, including how mechanical properties and the microstructure are influenced by increasing the amount of the RCP in a cement paste (≤ 25 wt%.

  16. Study of the effect of Kaolin in the mortar of cement matrices by confinement of ion exchange resins

    Directory of Open Access Journals (Sweden)

    Labied S.

    2018-01-01

    Full Text Available Radioactive waste arising as a result of nuclear activities should be safely managed from its generation to final disposal in an appropriate conditioned form to reduce the risk of radiation exposure of technical personnel and of the public and to limit contamination of the environment. The immobilization of low and intermediate level radioactive wastes in cementitious matrices is the most commonly used technique to produce inexpensive waste matrix that complies with regulatory requirements in order to protect humans and the environment against nuisance caused by ionizing radiation. Cement based materials are used in radioactive waste management to produce stable waste forms. This matrix constitutes the first build engineering barrier in disposal facilities. In this work, the kaolin is used to enhance the mechanical performance of the matrix of confinement of ion exchange resins by gradually replacing the sand in mortar with kaolin clay. The Kaolin clay sample was a special pure product, sourced from a foreign country. The maximum quantity of resins that can be incorporated into the mortar formulation without the packages losing their strength is 13.915% which results in a better mechanical strength at 6.7686 MPA compression with kaolin.

  17. The influence of cellulose nanocrystal additions on the performance of cement paste

    Science.gov (United States)

    Yizheng Cao; Pablo Zavaterri; Jeff Youngblood; Robert Moon; Jason Weiss

    2015-01-01

    The influence of cellulose nanocrystals (CNCs) addition on the performance of cement paste was investigated. Our mechanical tests show an increase in the flexural strength of approximately 30% with only 0.2% volume of CNCs with respect to cement. Isothermal calorimetry (IC) and thermogravimetric analysis (TGA) show that the degree of hydration (DOH) of the cement paste...

  18. Cracking in cement paste induced by autogenous shrinkage

    DEFF Research Database (Denmark)

    Lura, Pietro; Jensen, Ole Mejlhede; Weiss, Jason

    2009-01-01

    technique allows identification of microcracks while avoiding artefacts induced by unwanted restraint, drying, or temperature variations during sample preparation. Small cylindrical samples of cement paste are cast with steel rods of different diameters in their centre. The rods restrain the autogenous......, and creep as a function of hydration time were used as inputs in the analysis. The experimental results and the numerical analysis showed that samples with larger steel rods had the highest probability of developing microcracks. In addition, the pattern and the width of the observed microcracks showed good...

  19. Measuring techniques for autogenous strain of cement paste

    DEFF Research Database (Denmark)

    Lura, Pietro; Jensen, Ole Mejlhede

    2006-01-01

    of the volumetric method. Water absorption is driven by a lowering of the water activity in the cement paste due to dissolved salts in the pore fluid and to self-desiccation. From the moment of casting, significant water uptake was registered in all experiments. This water uptake influenced the volumetric...... measurements by the same order of magnitude as the autogenous strain itself. By performing the measurements in a paraffin oil bath instead of a water bath, this artefact was eliminated. Furthermore, volumetric measurements performed in paraffin oil gave almost identical results as linear measurements performed...

  20. Study of cement pastes rheological behavior using dynamic shear rheometer

    Directory of Open Access Journals (Sweden)

    J. E. S. L. Teixeira

    Full Text Available Concrete, in its fresh state, has flow characteristics that are crucial to its proper launch and densification. These characteristics are usually measured through empirical testing as the slump test, but this test does not quantify completely the material behavior. Since this material is characterized as a Bingham fluid, it is essential the study of its rheological behavior to verify its properties even in fresh state. The use of classical rheology has been employed by the scientific community to obtain rheological parameters determinants to characterize this material, such as yield stress, plastic viscosity and evolution of shear stress to shear rate. Thus, this present study aims to determine the rheological behavior of different cement pastes produced with cement CP III 40 RS, varying between them the hydration periods (20 and 60 min, the water-cement ratio (0.40, 0.45 and 0.50 and the use or not of additive. Samples were assayed by flow test to determine the rheological parameters showing the effect of the variables mentioned above in these parameters.

  1. Effect of natural fibers on mechanical properties of green cement mortar

    Science.gov (United States)

    AL-Zubaidi, Aseel B.

    2018-05-01

    Natural fibers of banana, reed, palm and coconut were used to reinforce cement composite. Optical microscopy showed that the prepared fibers are different in size and morphology. Nearly equiaxed, ribbon-like and nearly cylindrical morphologies were observed. Each of the utilized natural fibers was incorporated in the cement matrix at 0, 0.25, 0.5, 0.75 and 1.0 wt% and cured for 28 days. The scanning electron micrographs for the 1.0 wt% -reinforced composite showed differences in porosity, grain size and shape. Each of the utilized fibers has different effect on the microstructure of the cement composite that depends on the fiber size and morphology. Water absorption, thermal conductivity, bending strength, hardness and compression strengths were measured for the reinforced cement composite. It is found that the final physical and mechanical properties of the set cement composite depend on the fiber content and fiber type through the differences in their sizes and morphologies.

  2. Phase distribution and microstructural changes of self-compacting cement paste at elevated temperature

    International Nuclear Information System (INIS)

    Ye, G.; Liu, X.; De Schutter, G.; Taerwe, L.; Vandevelde, P.

    2007-01-01

    Self-compacting concrete, as a new smart building material with various advanced properties, has been used for a wide range of structures and infrastructures. However little investigation have been reported on the properties of Self-compacting when it is exposed to elevated temperatures. Previous experiments on fire test have shown the differences between high performance concrete and traditional concrete at elevated temperature. This difference is largely depending on the microstructural properties of concrete matrix, i.e. the cement paste, especially on the porosity, pore size distribution and the connectivity of pores in cement pastes. In this contribution, the investigations are focused on the cement paste. The phase distribution and microstructural changes of self-compacting cement paste at elevated temperatures are examined by mercury intrusion porosimetry and scanning electron microscopy. The chemical decomposition of self-compacting cement paste at different temperatures is determined by thermogravimetric analysis. The experimental results of self-compacting cement paste are compared with those of high performance cement paste and traditional cement paste. It was found that self-compacting cement paste shows a higher change of the total porosity in comparison with high performance cement paste. When the temperature is higher than 700 deg. C, a dramatic loss of mass was observed in the self-compacting cement paste samples with addition of limestone filler. This implies that the SCC made by this type of self-compacting cement paste will probably show larger damage once exposed to fire. Investigation has shown that 0.5 kg/m 3 of Polypropylene fibers in the self-compacting cement paste can avoid the damage efficiently

  3. Leaching of both calcium hydroxide and C-S-H from cement paste: Modeling the mechanical behavior

    International Nuclear Information System (INIS)

    Carde, C.; Torrenti, J.M.; Francois, R.

    1996-01-01

    This paper deals with the effect of the leaching process of cement based materials on their mechanical properties. This process induces mainly a total leaching of Ca(OH) 2 and a progressive decalcification of C-S-H which leads to a gradient of C/S ratio in the leaching zone. In a previous work, the authors venture the hypothesis that the dissolution of calcium hydroxide was the essential parameter governing both decrease in strength and increase in porosity in the case of a paste sample made with an OPC cement which leads to a 20% content of calcium. In order to quantify the effect of the decrease of C/S ratio in C-S-H, the authors have performed experiments on paste samples with the admixture of silica fume to reduce the content of calcium hydroxide and thus emphasize the effect of C/S ratio decrease of the C-S-H. The leaching process was achieved by the use of a 50% concentrate solution of ammonium nitrate. Compression tests were conducted on micro-cylinder samples (10, 12, 14, 20 and 30 mm of diameter) because of the slow kinetics of degradation due to the leaching. The deterioration of the cement paste and the mortar exposed to the action of the ammonium nitrate was indicated by a peripheral zone of less resistance. The experimental results allow the modeling of the mechanical behavior of cement pastes in relation to the ratio of degraded area over total area of the sample A d /A t . The model thus defined allows separation of the effect of calcium hydroxide leaching and C-S-H leaching, and shows the importance of the first one. The current research program tries to characterize the deterioration of the mechanical properties of the concrete surrounding radioactive wastes, due to the water flow during storage

  4. Mortars for 3D printing

    Directory of Open Access Journals (Sweden)

    Demyanenko Olga

    2018-01-01

    Full Text Available The paper is aimed at developing scientifically proven compositions of mortars for 3D printing modified by a peat-based admixture with improved operational characteristics. The paper outlines the results of experimental research on hardened cement paste and concrete mixture with the use of modifying admixture MT-600 (thermally modified peat. It is found that strength of hardened cement paste increases at early age when using finely dispersed admixtures, which is the key factor for formation of construction and technical specifications of concrete for 3D printing technologies. The composition of new formations of hardened cement paste modified by MT-600 admixture were obtained, which enabled to suggest the possibility of their physico-chemical interaction while hardening.

  5. Effect of polycarboxylate admixture structure on cement paste rheology

    Directory of Open Access Journals (Sweden)

    Aranda, M. A. G.

    2007-06-01

    Full Text Available The purpose of the present study was to analyze the effect of the structural differences in four polycarboxylate and polyether admixtures on the rheological properties of cement pastes with different chemical and mineralogical compositions and different active additions (CEM I 42.5 R, CEM I 52.5 R, CEM I 52.5 N/SR, CEM II/AV 42.5R, CEM II/B-L 32.5 R, CEM III/B 32.5R, BL I 52.5R and CAC – European standard EN 197-1:2000. The results of the minislump test concurred with the variations observed in the values of the rheological parameters (shear stress and plastic viscosity. The structural characteristic of the admixtures found to play the most prominent role in their fluidizing effect was the proportion of carboxylate (CG and polyether (EG group components. In cements characteristics such as fineness and the C3A/calcium sulphate and C3S/C3A ratios were also observed to be essential to admixture effectiveness. In this regard, the rheological parameters varied most widely in CEM I 52.5N/SR pastes and least in BL I 52.5R cement pastes. Of the additioned cements, the CEM III/B 32.5R pastes, which contained granulated blast furnace slag, showed the highest rises in flowability. Finally, the fluidizing effect of polycarboxylate superplasticizers was much more intense in calcium aluminate cements, although flowability declined rapidly in this material.El objetivo de este trabajo ha sido estudiar el efecto de las diferencias estructurales de cuatro aditivos basados en policarboxilatos y poliéteres sobre las propiedades reológicas de pastas de cemento con diferente composición química, mineralógica y con distintas adiciones activas (CEM I 42,5 R, CEM I 52,5 R, CEM I 52,5 N/SR, CEM II/AV 42,5R, CEM II/ B-L 32,5 R, CEM III/B 32,5R, BL I 52,5R y CAC - Norma EN 197-1:2000. Los resultados obtenidos sobre la fluidez de la pasta en el ensayo del “Minislump” coinciden con la evolución de los valores de los parámetros reológicos (esfuerzo de

  6. Early age volume changes in concrete due to chemical shrinkage of cement paste

    Directory of Open Access Journals (Sweden)

    Ebensperger, L.

    1991-12-01

    Full Text Available Unrestrained early age volume changes due to chemical shrinkage in cement pastes, mortars and concretes have been determined. The measurements were performed on sealed and unsealed samples which were stored under water. The chemical shrinkage of unsealed specimens represents the amount of absorbed water due to the chemical reaction of the cement It depends only on the cement content of the sample and does not lead to changes of the external dimensions. However the chemical shrinkage of sealed specimens is connected with a real volume change due to self-desiccation and the effect of internal pressures. The shrinkage depends in this case on the restraining effect of coarse aggregates as well as the cement content. The chemical shrinkage measured on sealed concretes was much higher than the one expected to ocurr on concretes, because normally an equalization of pressure takes place to some extent in the interior of the concrete. The use of expansive additives showed that they may compensate the chemical shrinkage, but its dosage is very sensitive and should be defined exactly for each case particularly.

    Se han determinado los cambios volumétricos que ocurren en pastas de cemento, morteros y hormigones a edad temprana debido al efecto de la retracción química. Las mediciones se realizaron en probetas selladas y no selladas sumergidas bajo agua. La retracción química en probetas no selladas representa la cantidad de agua absorbida debido a la reacción química del cemento. Depende solamente del contenido de cemento de la probeta y no produce ningún cambio en las dimensiones de la probeta. Por el contrario, la retracción química en probetas selladas está relacionada con un cambio volumétrico real debido al efecto de la autodesecación y presiones internas. La retracción en este caso depende tanto de la restricción que imponen los áridos, como del contenido de cemento. La retracción química medida en hormigones sellados

  7. Local porosity analysis of pore structure in cement paste

    International Nuclear Information System (INIS)

    Hu Jing; Stroeven, Piet

    2005-01-01

    Three-dimensional (3-D) local porosity theory (LPT) was originally proposed by Hilfer and recently used for the analysis of pore space geometry in model sandstone. LPT pursues to define the probability density functions of porosity and porosity connectivity. In doing so, heterogeneity differences in various sandstone samples were assessed. However, fundamental issues as to the stochastic concept of geometric heterogeneity are ignored in Hilfer's LPT theory. This paper focuses on proper sampling procedures that should be based on stochastic approaches to multistage sampling and geometric heterogeneity. Standard LPT analysis provides a 3-D microscopic modeling approach to materials. Traditional experimental techniques yield two-dimensional (2-D) section images, however. Therefore, this paper replaces the method for assessing material data in standard LPT theory to a more practical one, based on stereological, 3-D interpretation of quantitative image analysis data. The developed methodology is used to characterize the pore structure in hardened cement paste with various water/cement ratios (w/c) at different hydration stages

  8. Research of Cemented Paste Backfill in Offshore Environments

    Science.gov (United States)

    Wang, Kun; Yang, Peng; Lyu, Wensheng; Lin, Zhixiang

    2018-01-01

    To promote comprehensive utilization of mine waste tailings and control ground pressure, filling mine stopes with cement paste backfill (CPB) is becoming the most widely used and applicable method in contemporary underground mining. However, many urgent new problems have arisen during the exploitation in offshore mines owing to the complex geohydrology conditions. A series of rheological, settling and mechanical tests were carried out to study the influences of bittern ions on CPB properties in offshore mining. The results showed that: (1) the bittern ion compositions and concentrations of backfill water sampled in mine filling station were similar to seawater. Backfill water mixed CPB slurry with its higher viscosity coefficient was adverse to pipeline gravity transporting; (2) Bleeding rate of backfill water mixed slurry was lower than that prepared with tap water at each cement-tailings ratio; (3) The UCS values of backfill water mixed samples were higher at early curing ages (3d, 7d) and then became lower after longer curing time at 14d and 28d. Therefore, for mine production practice, the offshore environments can have adverse effects on the pipeline gravity transporting and have positive effects on stope dewatering process and early-age strength growth.

  9. About influence of some superplasticizers on hydration and the structure of hardened cement paste

    Directory of Open Access Journals (Sweden)

    Koryanova Yulia

    2017-01-01

    Full Text Available Current construction can not be imagined without the use of high-quality mortars and concretes obtained by using high-tech and workable mixtures with lower water content. Obtaining such mixtures in current conditions is impossible without the use of superplasticizers. The use of superplasticizers in concrete technology requires an answer to the question of the influence of superplasticizers on the deformation-strength properties of cement stone. There is a well-known dependence “composition-technology-structure-properties”, from which it follows that the strength and deformation properties of cement stone directly depend on the hydration of cement stone in the early stages and structure formation. The influence of some types of superplasticizers on the hydration and structure of cement stone, namely, total, open and conditionally-closed porosity, total contraction, autogenous shrinkage, contraction porosity and hydration heat is considered in the article.

  10. Evaluation of pulp and mortar to pack bitumen radioactive waste

    International Nuclear Information System (INIS)

    Gregorio, Marina da S.; Vieira, Vanessa M.; Tello, Cledola C.O.

    2013-01-01

    According to international experience, for the deposition of cement in surface repository, is necessary the use of cement mortar pastes to immobilize the product. Determining the most efficient folder or for the packed mortar, as well as its ideal formulation, is the goal of this study. To do various experiments with samples of cement paste and mortar, with presence of fluxing and / or clay were performed. Viscosity, density, setting time and compressive strength were evaluated. This study will be presented only the results found in testing of compressive strength to be an essential parameter in the transport, storage and disposal of the product. From the results found will be selected the best formulations for use in packed bitumen tailings from the National Radioactive Waste Repository

  11. Combined effect of nano-SiO2 and nano-Fe2O3 on compressive strength, flexural strength, porosity and electrical resistivity in cement mortars

    International Nuclear Information System (INIS)

    Sanjuán, M.A.; Argiz, C.; Gálvez, J.C.; Reyes, E.

    2018-01-01

    The compressive strength, flexural strength, porosity and electrical resistivity properties of cement mortars with nano-Fe2O3 and nano-SiO2 are studied. Amorphous silica is the main component of pozzolanic materials due to its reaction with calcium hydroxide formed from calcium silicate (C3S and C2S) hydration. The pozzolanic reaction rate is not only proportional to the amount of amorphous silica but also to the surface area available for reaction. Subsequently, fine nano-Fe2O3 and nano-SiO2 particles in mortars are expected to improve mortar performance. The experimental results showed that the compressive strength of mortars with nano-Fe2O3 and nano-SiO2 particles were lower than those obtained with the reference mortar at seven and 28 days. It was shown that the nano-particles were not able to enhance mechanical strength on every occasion. The continuous microstructural progress monitored by mercury intrusion porosimetry (MIP) measurements, pore-size distribution (PSD), total porosity and critical pore diameter also confirmed such results. [es

  12. Combined effect of nano-SiO2 and nano-Fe2O3 on compressive strength, flexural strength, porosity and electrical resistivity in cement mortars

    Directory of Open Access Journals (Sweden)

    M. A. Sanjuán

    2018-03-01

    Full Text Available The compressive strength, flexural strength, porosity and electrical resistivity properties of cement mortars with nano-Fe2O3 and nano-SiO2 are studied. Amorphous silica is the main component of pozzolanic materials due to its reaction with calcium hydroxide formed from calcium silicate (C3S and C2S hydration. The pozzolanic reaction rate is not only proportional to the amount of amorphous silica but also to the surface area available for reaction. Subsequently, fine nano-Fe2O3 and nano-SiO2 particles in mortars are expected to improve mortar performance. The experimental results showed that the compressive strength of mortars with nano-Fe2O3 and nano-SiO2 particles were lower than those obtained with the reference mortar at seven and 28 days. It was shown that the nano-particles were not able to enhance mechanical strength on every occasion. The continuous microstructural progress monitored by mercury intrusion porosimetry (MIP measurements, pore-size distribution (PSD, total porosity and critical pore diameter also confirmed such results.

  13. The C-S-H gel of Portland cement mortars: Part I. The interpretation of energy-dispersive X-ray microanalyses from scanning electron microscopy, with some observations on C-S-H, AFm and AFt phase compositions

    International Nuclear Information System (INIS)

    Famy, C.; Brough, A.R.; Taylor, H.F.W.

    2003-01-01

    Scanning electron microscopy (SEM) microanalyses of the calcium-silicate-hydrate (C-S-H) gel in Portland cement pastes rarely represent single phases. Essential experimental requirements are summarised and new procedures for interpreting the data are described. These include, notably, plots of Si/Ca against other atom ratios, 3D plots to allow three such ratios to be correlated and solution of linear simultaneous equations to test and quantify hypotheses regarding the phases contributing to individual microanalyses. Application of these methods to the C-S-H gel of a 1-day-old mortar identified a phase with Al/Ca=0.67 and S/Ca=0.33, which we consider to be a highly substituted ettringite of probable composition C 6 A 2 S-bar 2 H 34 or {Ca 6 [Al(OH) 6 ] 2 ·24H 2 O}(SO 4 ) 2 [Al(OH) 4 ] 2 . If this is true for Portland cements in general, it might explain observed discrepancies between observed and calculated aluminate concentrations in the pore solution. The C-S-H gel of a similar mortar aged 600 days contained unsubstituted ettringite and an AFm phase with S/Ca=0.125

  14. Positron annihilation probing for the hydratation rate of cement paste

    International Nuclear Information System (INIS)

    Myllylae, R.; Karras, M.

    1975-01-01

    Positron annihilation has been found to be a possible probe for the exponential hydratation of cement paste. Both lifetime and Doppler line broadening measurements revealed the hydratation rate. With the aid of increased stability in the lifetime spectrometer it has been possible to extend the measuring sensitivity over a period of several weeks. Two main lifetimes, tau 1 = 480 +- 20 psec and tau 2 = 2.1 +- 0.1 nsec, were observed to be constant during the hydratation. The intensity of the 2.1 nsec component changed from 4 to 8% after 47 days, and simultaneously the annihilation line narrowed from 2.6 to 2.4 keV. This behaviour has been interpreted as an increase in positronium formation. The possible practical applications of positron annihilation radiation as a hydratation probe has been evaluated for use in a concrete laboratory and even for regular construction work. (orig.) [de

  15. The effect of fly ash and coconut fibre ash as cement replacement materials on cement paste strength

    Science.gov (United States)

    Bayuaji, R.; Kurniawan, R. W.; Yasin, A. K.; Fatoni, H. AT; Lutfi, F. M. A.

    2016-04-01

    Concrete is the backbone material in the construction field. The main concept of the concrete material is composed of a binder and filler. Cement, concrete main binder highlighted by environmentalists as one of the industry are not environmentally friendly because of the burning of cement raw materials in the kiln requires energy up to a temperature of 1450° C and the output air waste CO2. On the other hand, the compound content of cement that can be utilized in innovation is Calcium Hydroxide (CaOH), this compound will react with pozzolan material and produces additional strength and durability of concrete, Calcium Silicate Hydrates (CSH). The objective of this research is to explore coconut fibers ash and fly ash. This material was used as cement replacement materials on cement paste. Experimental method was used in this study. SNI-03-1974-1990 is standard used to clarify the compressive strength of cement paste at the age of 7 days. The result of this study that the optimum composition of coconut fiber ash and fly ash to substitute 30% of cement with 25% and 5% for coconut fibers ash and fly ash with similar strength if to be compared normal cement paste.

  16. Revealing the influence of water-cement ratio on the pore size distribution in hydrated cement paste by using cyclohexane

    Science.gov (United States)

    Bede, Andrea; Ardelean, Ioan

    2017-12-01

    Varying the amount of water in a concrete mix will influence its final properties considerably due to the changes in the capillary porosity. That is why a non-destructive technique is necessary for revealing the capillary pore distribution inside hydrated cement based materials and linking the capillary porosity with the macroscopic properties of these materials. In the present work, we demonstrate a simple approach for revealing the differences in capillary pore size distributions introduced by the preparation of cement paste with different water-to-cement ratios. The approach relies on monitoring the nuclear magnetic resonance transverse relaxation distribution of cyclohexane molecules confined inside the cement paste pores. The technique reveals the whole spectrum of pores inside the hydrated cement pastes, allowing a qualitative and quantitative analysis of different pore sizes. The cement pastes with higher water-to-cement ratios show an increase in capillary porosity, while for all the samples the intra-C-S-H and inter-C-S-H pores (also known as gel pores) remain unchanged. The technique can be applied to various porous materials with internal mineral surfaces.

  17. HYDRATION PROCESS AND MECHANICAL PROPERTIES OF CEMENT PASTE WITH RECYCLED CONCRETE POWDER AND SILICA SAND POWDER

    Directory of Open Access Journals (Sweden)

    Jaroslav Topič

    2017-11-01

    Full Text Available Recycled concrete powder (RCP mostly consisting of cement paste could be reused as partial cement replacement. The aim of this paper is to compare hydration and mechanical properties of RCP and two types of silica sand powder (SSP. Comparison of those materials combined with cement can highlight the binder properties of recycled concrete powder. Using of two types of SSP also show an influence of their fines on hydration process and mechanical properties. Particle size analysis and calorimetric measurement were carried out and mechanical properties such as bulk density, dynamic Young’s modulus and compression strength were examine. Calorimetric measurement proves the presence of exposed non-hydrated particles in RCP that can react again. However lower density of old cement paste in RCP overweight the mentioned potential of RCP and mechanical properties are decreasing compared with reference cement paste and cement paste SSP.

  18. Description of the structural evolution of a hydrating portland cement paste by SANS

    International Nuclear Information System (INIS)

    Haeussler, F.; Eichhorn, F.; Baumbach, H.

    1994-01-01

    On the spectrometer MURN at the pulsed reactor IBR-2 dry Portland cement, silica fume, and a hydrating Portland cement paste were studied by small-angle neutron scattering (SANS). By using the TOF-method a momentum transfer from 0.07 nm -1 to 7 nm -1 is detectable. Every component (dry cement powder, clinker minerals, hydrating cement pastes) shows a different scattering behaviour. In the measured Q-region the hardening cement paste does not show a Porod-like behaviour of SANS-curves. In contrast the Porod's potential law holds for dry powder samples of clinker minerals and silica fume. In experiments carried out to observe the hydration progress within the first 321 days the characteristics of the scattering curves (potential behaviour, the radius of gyration, and the macroscopic scattering cross section at Q = 0 nm -1 were measured. Some evolution of the inner structure of the hardened cement paste was noted. (orig.)

  19. Literature survey on phase composition of hardened cement paste containing fly ash

    International Nuclear Information System (INIS)

    Otsuka, Taku; Yamamoto, Takeshi

    2015-01-01

    The purpose of this literature survey is to collect the knowledge on the effect of fly ash in hardened cement paste and the information about evaluation of physicochemical performance based on phase composition of hardened cement paste. The performance of hardened cement paste containing fly ash is affected by the property of fly ash, hydration of cement and pozzolanic reaction of fly ash. Some properties of fly ash such as density and chemical composition are reflected in phase composition, showing the progress of cement hydration and pozzolanic reaction. Therefore clarification of the relationship of phase composition and performance will lead to appropriate evaluation of the property of fly ash. The amount of pore, chemical shrinkage, pore solution, compressive strength, Young modulus and alkali silica reaction have relations to the phase composition of hardened cement paste. It is considered as future subject to clarify the relationship of phase composition and performance for various properties of fly ash. (author)

  20. E-modulus evolution and its relation to solids formation of pastes from commercial cements

    DEFF Research Database (Denmark)

    Maia, Lino; Azenha, Miguel; Geiker, Mette

    2012-01-01

    Models for early age E-modulus evolution of cement pastes are available in the literature, but their validation is limited. This paper provides correlated measurements of early age evolution of E-modulus and hydration of pastes from five commercial cements differing in limestone content. A recently...

  1. Determination of unfixed ammonium in cement and cement mortar used for lining drinking water pipes. Zur Bestimmung des nicht fixierten Ammoniums in Zement und Zementmoertel fuer die Innenauskleidung von Trinkwasserrohren

    Energy Technology Data Exchange (ETDEWEB)

    Bruins, J; Maurer, W [Siegen Univ. (Gesamthochschule) (Germany, F.R.). Inst. fuer Analytische Chemie

    1989-09-01

    The reinfection of cement-lined drinking water pipes after heavy chlorine treatment may be caused by the ammonium content of the cement mortar used; the ammonia reduces the amount of chlorine available for disinfection. The chlorine depletion should therefore be reduced by using a mortar which is low in, or free from, ammonia. This article investigates the trace analysis required for determining the ammonium content. The samples were prepared by separating the ammonia from the complex matrix by an excess of alkali combined with distillation. The ammonium content was determined by ion chromatography followed by conductivity detection, or by a post-column reaction with Nesslers reagent followed by photometric detection at=425 nm. Both methods show good reproducibility (S{sub rel} approx. 2%) and recovery (approx. 96%). The results agree well with the other methods which were used in an interlaboratory test. (orig.).

  2. Effects of Static Magnetic Fields on the Physical, Mechanical, and Microstructural Properties of Cement Pastes

    Directory of Open Access Journals (Sweden)

    Juan J. Soto-Bernal

    2015-01-01

    Full Text Available This paper presents the results of an experimental study carried out to comprehend the physical, mechanical, and microstructural behavior of cement pastes subjected to static magnetic fields while hydrating and setting. The experimental methodology consisted in exposing fresh cement pastes to static magnetic fields at three different magnetic induction strengths: 19.07, 22.22, and 25.37 Gauss. The microstructural characterization makes evident that there are differences in relation to amount and morphology of CSH gel; the amount of CSH is larger and its morphology becomes denser and less porous with higher magnetostatic induction strengths; it also shows the evidence of changes in the mineralogical composition of the hydrated cement pastes. The temperature increasing has no negative effects over the cement paste compressive strength since the magnetostatic field affects the process of hydration through a molecular restructuring process, which makes cement pastes improve microstructurally, with a reduced porosity and a higher mechanical strength.

  3. Pore structure and carbonation in blended lime-cement pastes

    Directory of Open Access Journals (Sweden)

    Álvarez, J. I.

    2006-06-01

    Full Text Available The present study aims to gain a fuller understandingof the curing process in lime pastes (100, 90, 80, 70,60, 50 and 40% lime blended with cement by analyzingcarbonation in these materials. A hydrated, airslaked lime powder and CEM II A/L 32.5 Portlandcement were used for the blends. These materialswere singled out for research primarily because theymay be used in the restoration of heritage monuments.Variation in weight was used as an indicator for carbonation.A new parameter, A, was found to vary inverselywith the percentage of the cement because of theprevalence of Knudsen diffusion in the paste, in turndue to the characteristics of the pore structure, whichwas studied by mercury intrusion porosimetry (MIP.The hygroscopic study conducted on the different pastesprovided information on water content at a givenhumidity and its location, i.e., adsorbed on the surfaceof the pores or condensed inside them, obstructing thediffusion of CO2. The conclusion drawn from this studyof the curing process was that neither drying nor C3Shydration retarded lime carbonation.En este trabajo se estudia el proceso de carbonatacionen pastas mixtas de cal y cemento (100, 90, 80, 70, 60,50 y 40% de cal con el objeto de obtener un mejorconocimiento del proceso de curado en estos materiales.Para ello se ha empleado una cal aerea hidratada en polvoy un cemento Portland del tipo CEM II A/L 32,5. Enparticular, este estudio investiga estos materiales ya quepueden ser utilizados en la restauracion del PatrimonioCultural. Se ha utilizado la variacion de peso como indicadordel proceso de carbonatacion. Se ha establecidoun nuevo parametro, A, que varia inversamente con elporcentaje de cemento en la pasta, debido al predominiode la difusion de Knudsen como consecuencia de laestructura porosa, que ha sido estudiada por medio deporosimetria de intrusion de mercurio (PIM. El estudiohigroscopico realizado sobre las diversas pastas permiteconocer el contenido en agua a una

  4. Method of producing grouting mortar

    Energy Technology Data Exchange (ETDEWEB)

    Shelomov, I K; Alchina, S I; Dizer, E I; Gruzdeva, G A; Nikitinskii, V I; Sabirzyanov, A K

    1980-10-07

    A method of producing grouting mortar by mixing the cement with an aqueous salt solution is proposed. So as to increase the quality of the mortar through an acceleration of the time for hardening, the mixture is prepared in two stages, in the first of which 20-30% of the entire cement batch hardens, and in the second of which the remainder of the cement hardens; 1-3-% of an aqueous salt solution is used in quantities of 0.5/1 wt.-% of weight of the cement. The use of this method of producing grouting mortar helps to increase the flexural strength of the cement brick up to 50% after two days ageing by comparison with the strength of cement brick produced from grouting mortar by ordinary methods utilizing identical quantities of the initial components (cement, water, chloride).

  5. Color agreement between nanofluorapatite ceramic discs associated with try-in pastes and with resin cements

    Directory of Open Access Journals (Sweden)

    Paulo Rigoni

    2012-12-01

    Full Text Available The aim of this study was to evaluate the in vitro color agreement between nanofluorapatite ceramic discs (e.max Ceram / Ivoclar Vivadent / A2 associated with try-in pastes and those bonded with resin cements (Vitique / DMG/ try-in shade A2½ and cement shade A2½, Variolink II / Ivoclar Vivadent / try-in shade A1 and cement shade A1, and Choice 2 / Bisco / try-in shade A2 and cement shade A2, and to evaluate the shade stability of the discs bonded with resin cements. The shades of composite resin discs (Lliss / FGM / A2 and nanofluorapatite ceramic discs with try-in pastes or cements were evaluated according to the Vita Classical shade guide by a digital spectrophotometer (Micro EspectroShade, MHT immediately after placing the try-in pastes or resin cements between composite resin discs and ceramic discs. Other evaluations were performed at 2, 5, and 6 day intervals after cementation with the resin cements. All ceramic discs that received try-in pastes presented an A2 shade. There was no statistical difference in the shade of the ceramic specimens fixed with different cements at the different intervals, as evaluated by the Friedman test (p > 0.05. Two try-in pastes presented shade compatibility with those recommended by the manufacturers. There was no similarity of shades between the ceramic discs with try-in pastes and those with the respective resin cements. Shade stability was observed in ceramic discs with resin cements within the intervals evaluated.

  6. INFLUENCE OF SUBSTITUTION OF ORDINARY PORTLAND CEMENT BY SILICA FUME ON THE HYDRATION OF SLAG-PORTLAND CEMENT PASTES

    Directory of Open Access Journals (Sweden)

    E.A. El-Alfi

    2011-06-01

    Full Text Available Effect of gradual substitution of ordinary Portland cement by a few percent of silica fume (0.0, 2.5, 5.0 and 7.5 wt.% on the hydration properties of slag-Portland cement pastes up to 12 months was investigated. The results show that the composite cement pastes containing silica fume give the higher physico-mechanical properties than that of the slag-Portland cement. Also, the XRD results reveal that the peak of Ca(OH2 shows higher intensity in the sample without silica fume and completely disappears in the sample containing 7.5 wt.% silica fume content. Also, the intensity peaks of C4AH13 sharply increase with silica fume content.

  7. The Assessment of Cement Mortars after Thermal Degradation by Acoustic Non-destructive Methods

    Science.gov (United States)

    Topolář, L.; Štefková, D.; Hoduláková, M.

    2017-10-01

    Thanks, the terrorist attacks on the worldwide interest in the design of structures for fire greatly increased. One of the advantages of concrete over other building materials is its inherent fire-resistive properties. The concrete structural components still must be able to withstand dead and live loads without collapse even though the rise in temperature causes a decrease in the strength and modulus of elasticity for concrete and steel reinforcement. In addition, fully developed fires cause expansion of structural components and the resulting stresses and strains must be resisted. This paper reports the results of measurements by Impact-echo method and measurement by ultrasound. Both methods are based on the acoustic properties of the material which are dependent on its condition. These acoustic methods allow identifying defects and are thus suitable for monitoring the building structure condition. The results are obtained in the laboratory during the degradation of composite materials based on cement by high-temperature.

  8. Evaluation of structural behaviour and corrosion resistant of austenitic AISI 304 and duplex AISI 2304 stainless steel reinforcements embedded in ordinary Portland cement mortars

    International Nuclear Information System (INIS)

    Medina, E.; Cobo, A.; Bastidas, D. M.

    2012-01-01

    The mechanical and structural behaviour of two stainless steels reinforcements, with grades austenitic EN 1.4301 (AISI 304) and duplex EN 1.4362 (AISI 2304) have been studied, and compared with the conventional carbon steel B500SD rebar. The study was conducted at three levels: at rebar level, at section level and at structural element level. The different mechanical properties of stainless steel directly influence the behaviour at section level and structural element level. The study of the corrosion behaviour of the two stainless steels has been performed by electrochemical measurements, monitoring the corrosion potential and the lineal polarization resistance (LPR), of reinforcements embedded in ordinary Portland cement (OPC) mortar specimens contaminated with different amount of chloride over one year time exposure. Both stainless steels specimens embedded in OPC mortar remain in the passive state for all the chloride concentration range studied after one year exposure. (Author) 26 refs.

  9. Damage evolution analysis in mortar, during compressive loading using acoustic emission and X-ray tomography: Effects of the sand/cement ratio

    International Nuclear Information System (INIS)

    Elaqra, H.; Godin, N.; Peix, G.; R'Mili, M.; Fantozzi, G.

    2007-01-01

    This paper explores the use of acoustic emission (AE) and X-ray tomography to identify the mechanisms of damage and the fracture process during compressive loading on concrete specimens. Three-dimensional (3D) X-ray tomography image analysis was used to observe defects of virgin mortar specimen under different compressive loads. Cumulative AE events were used to evaluate damage process in real time according to the sand/cement ratio. This work shows that AE and X-ray tomography are complementary nondestructive methods to measure, characterise and locate damage sites in mortar. The effect of the sand proportion on damage and fracture behaviour is studied, in relation with the microstructure of the material

  10. An innovative approach to achieve re-centering and ductility of cement mortar beams through randomly distributed pseudo-elastic shape memory alloy fibers

    Science.gov (United States)

    Shajil, N.; Srinivasan, S. M.; Santhanam, M.

    2012-04-01

    Fibers can play a major role in post cracking behavior of concrete members, because of their ability to bridge cracks and distribute the stress across the crack. Addition of steel fibers in mortar and concrete can improve toughness of the structural member and impart significant energy dissipation through slow pull out. However, steel fibers undergo plastic deformation at low strain levels, and cannot regain their shape upon unloading. This is a major disadvantage in strong cyclic loading conditions, such as those caused by earthquakes, where self-centering ability of the fibers is a desired characteristic in addition to ductility of the reinforced cement concrete. Fibers made from an alternative material such as shape memory alloy (SMA) could offer a scope for re-centering, thus improving performance especially after a severe loading has occurred. In this study, the load-deformation characteristics of SMA fiber reinforced cement mortar beams under cyclic loading conditions were investigated to assess the re-centering performance. This study involved experiments on prismatic members, and related analysis for the assessment and prediction of re-centering. The performances of NiTi fiber reinforced mortars are compared with mortars with same volume fraction of steel fibers. Since re-entrant corners and beam columns joints are prone to failure during a strong ground motion, a study was conducted to determine the behavior of these reinforced with NiTi fiber. Comparison is made with the results of steel fiber reinforced cases. NiTi fibers showed significantly improved re-centering and energy dissipation characteristics compared to the steel fibers.

  11. Dosification of a cement-talc-chamotte refractory mortar subjected to thermal shock

    Directory of Open Access Journals (Sweden)

    Kittl, P.

    1992-03-01

    Full Text Available A cement-talc-chamotte refractory mixture was dosified by subjecting the same to thermal shock. To this end, specimens compacted to 350 Kg/cm2 through compression as well as specimens compacted manually were prepared. All the specimens were submitted to an initial working temperature of 1000ºC and then left to cool down to room temperature. The thermal shock was originated by heating the specimens in an oven till reaching a certain temperature T¡ and then quenching the same through immersion in water at 20ºC; temperature T¡ was varied between 170ºC and 970ºC by means of 100ºC increments. The optimum dosification amounting to 90 % cement-talc and 10 % chamotte was obtained by studying mean stress at compression fracture of five cement-talc-chamote mixtures as a function of thermal shock. In addition, thermal fatigue exhibited by the optimum dosification was studied through the determination of mean loss in compressive strength, which amounted to 52% after 7 cycles with ΔT = 500ºC.

    Se dosificó una mezcla refractaria cemento-talco-chamota sometiéndola a un choque térmico. Con este objeto se fabricaron probetas compactadas a 350 kg/cm2 mediante compresión y probetas compactadas manualmente. Se aplicó a todas ellas una temperatura inicial de trabajo a 1.000 ºC, luego se las dejó enfriar hasta que alcanzaran la temperatura de sala del laboratorio. El choque térmico se originó calentando las probetas en un horno hasta una temperatura T¡ y luego se las enfrió súbitamente sumergiéndolas en agua a 20 ºC; la temperatura T¡ varió entre 170 ºC y 970 ºC con incrementos de 100 ºC. La dosificación óptima, 90% cemento-talco y 10% chamota, se obtuvo estudiando la tensión media de fractura a la compresión de cinco mezclas de cemento-talco-chamota en función del choque térmico. Se estudió además la fatiga térmica de la dosificación óptima determinando la

  12. Wet versus dry cement pastes and concretes: a mathematical approach to their strength and fracture properties

    International Nuclear Information System (INIS)

    Suarez Antola, R.

    2006-12-01

    The fracture process of a continuous matrix in a porous medium under the combined effect of filtration and external mechanical loads is considered. Taking into account the differences between the failure mechanisms of cement paste under tension and its failure mechanisms under compression, an analytical approach to the relation between water flow and fracture in saturated porous Portland cement pastes is developed. The well known differences in behaviour between the flexural and compressive strengths of wet and dry Portland cement pastes is explained. The extension of the obtained results to the flexural and compressive strength of normal concrete is briefly discussed, including suggestions for further experimental and digital simulation work

  13. Hydration and leaching characteristics of cement pastes made from electroplating sludge.

    Science.gov (United States)

    Chen, Ying-Liang; Ko, Ming-Sheng; Lai, Yi-Chieh; Chang, Juu-En

    2011-06-01

    The purpose of this study was to investigate the hydration and leaching characteristics of the pastes of belite-rich cements made from electroplating sludge. The compressive strength of the pastes cured for 1, 3, 7, 28, and 90 days was determined, and the condensation of silicate anions in hydrates was examined with the (29)Si nuclear magnetic resonance (NMR) technology. The leachabilities of the electroplating sludge and the hardened pastes were studied with the multiple toxicity characteristic leaching procedure (MTCLP) and the tank leaching test (NEN 7345), respectively. The results showed that the electroplating sludge continued to leach heavy metals, including nickel, copper, and zinc, and posed a serious threat to the environment. The belite-rich cement made from the electroplating sludge was abundant in hydraulic β-dicalcium silicate, and it performed well with regard to compressive-strength development when properly blended with ordinary Portland cements. The blended cement containing up to 40% the belite-rich cement can still satisfy the compressive-strength requirements of ASTM standards, and the pastes cured for 90 days had comparable compressive strength to an ordinary Portland cement paste. It was also found that the later hydration reaction of the blended cements was relatively more active, and high fractions of belite-rich cement increased the chain length of silicate hydrates. In addition, by converting the sludge into belite-rich cements, the heavy metals became stable in the hardened cement pastes. This study thus indicates a viable alternative approach to dealing with heavy metal bearing wastes, and the resulting products show good compressive strength and heavy-metal stability. Copyright © 2011 Elsevier Ltd. All rights reserved.

  14. Partial replacement of Portland cement by red ceramic waste in mortars: study of pozzolanic activity; Substituicao parcial do cimento Portland por residuo de ceramica vermelha em argamassas: estudo da atividade pozolonica

    Energy Technology Data Exchange (ETDEWEB)

    Silva, A.R. da; Cabral, K.C.; Pinto, E.N. de M.G.l., E-mail: kleber.cabral@ufersa.edu.br [Universidade Federal Rural do Semi-Arido (UFERSA), Mossoro, RN (Brazil)

    2016-07-01

    The objective of this study is to analyze the pozzolanic activity of red ceramic residue on the partial replacement of Portland cement in mortars. The mortars were prepared by substituting 25% of the Portland cement for ground of ceramic residue with water cement’s factor of 0.48. The concrete used to construct the reference mortars and those with addiction was CPII-Z-32 (compound of Portland pozzolana cement). The chemical analysis and physical ceramic waste showed that this meets the requirements of NBR12653 (2014) for use as pozzolanic material. The pozzolanic activity index (IAP) obtained for the ceramic waste to twenty-eight days cure rate was 80.28%. (author)

  15. Acoustic emissions and electric signal recordings, when cement mortar beams are subjected to three-point bending under various loading protocols

    Directory of Open Access Journals (Sweden)

    A. Kyriazopoulos

    2017-04-01

    Full Text Available Two experimental techniques are used study the response of cement mortar beams subjected to three-point bending under various load¬ing protocols. The techniques used are the detection of weak electric current emissions known as Pressure Stimulated Currents and the Acoustic Emissions (in particular, the cumulative AE energy and the b-value analysis. Patterns are detected that can be used to predict upcoming fracture, regard¬less of the adopted loading protocol in each experiment. The expe¬rimental results of the AE and PSC techniques lead to the conclusion that when the calculated Ib values decrease, the PSC starts increasing strongly.

  16. Efeito do tempo de cura na rigidez de argamassas produzidas com cimento Portland Effect of the curing time on the stiffness of mortars produced with Portland cement

    Directory of Open Access Journals (Sweden)

    G. C. R. Garcia

    2011-03-01

    Full Text Available O concreto de cimento Portland é um dos materiais mais usados no mundo inteiro, entretanto, devido a sua estrutura ser muito complexa, torna-se imprescindível estudar suas propriedades com bastante profundidade. O concreto é produzido a partir de uma argamassa, de areia e cimento, com adição de agregados graúdos, sendo que suas propriedades estão basicamente suportadas nessa argamassa de constituição. O objetivo deste trabalho foi estudar a variação da rigidez de duas argamassas de composições com razão cimento:areia de 1:2 e 1:3 em função do tempo de cura, tendo como parâmetro a variação do módulo de Young. Os resultados mostraram que o módulo de Young cresce até atingir o valor máximo no oitavo dia, sendo que nos três primeiros dias esse crescimento é mais acentuado. A análise dos resultados indica que grande parte do processo de hidratação do cimento, com formação das ligações químicas responsáveis pela rigidez da argamassa, acontece nos primeiros dias de cura.Concrete produced with Portland cement is one of building materials most widely used worldwide. However, due to its highly complex structure, its properties require in-depth studies. Concrete is a mortar consisting of a mixture of cement, sand and coarse aggregates, and its properties are represented basically by the mortar base. The aim of this work was to study the change in stiffness of two mortar compositions cured at 25 ºC with a cement-to-sand ratio of 1:2 and 1:3, as a function of curing time using the variation of Young modulus as the measuring parameter. The results showed that Young modulus increases up to a maximum value on the 8th day, and that this increase is more pronounced during the first three days. An analysis of the results indicates that a large part of the cement hydration process, involving the formation of chemical bonds that are responsible for the mortar stiffness, takes place in the early days of curing.

  17. Creep and fatigue behavior of a novel 2-component paste-like formulation of acrylic bone cements.

    Science.gov (United States)

    Köster, Ulrike; Jaeger, Raimund; Bardts, Mareike; Wahnes, Christian; Büchner, Hubert; Kühn, Klaus-Dieter; Vogt, Sebastian

    2013-06-01

    The fatigue and creep performance of two novel acrylic bone cement formulations (one bone cement without antibiotics, one with antibiotics) was compared to the performance of clinically used bone cements (Osteopal V, Palacos R, Simplex P, SmartSet GHV, Palacos R+G and CMW1 with Gentamicin). The preparation of the novel bone cement formulations involves the mixing of two paste-like substances in a static mixer integrated into the cartridge which is used to apply the bone cement. The fatigue performance of the two novel bone cement formulations is comparable to the performance of the reference bone cements. The creep compliance of the bone cements is significantly influenced by the effects of physical ageing. The model parameters of Struik's creep law are used to compare the creep behavior of different bone cements. The novel 2-component paste-like bone cement formulations are in the group of bone cements which exhibit a higher creep resistance.

  18. Structure investigations on Portland cement paste by small angle neutron scattering

    International Nuclear Information System (INIS)

    Dragolici, C.A.; Lin, A.

    2004-01-01

    Hydrated Portland cement is a very complex material. Cement paste consists of many crystalline and non-crystalline phases in various ranges of sizes (μm and nm scale). The crystalline phases are embedded in amorphous phases of hydration products. We investigated the structural changes of hydrating phases in a time interval up to 18 days, at Budapest Neutron Center's SANS spectrometer. The small angle neutron scattering of Portland cements prepared with a various water-to-cement ratios, gave us information about the microstructure changes in the material. Fractals were a suitable way for structure modelling. Some comments regarding the opportunity of using the most common models are pointed out. (authors)

  19. Influence of spraying on the early hydration of accelerated cement pastes

    International Nuclear Information System (INIS)

    Salvador, Renan P.; Cavalaro, Sergio H.P.; Cano, Miguel; Figueiredo, Antonio D.

    2016-01-01

    In practice, most of the studies about the interaction between cement and accelerators is performed with hand-mixed pastes. However, in many applications mixing occurs through spraying, which may affect accelerators reactivity and the microstructure of the hardened paste. The objective of this study is to analyze how the mixing process influences the early hydration of accelerated cement pastes. Isothermal calorimetry, X-ray diffraction, thermogravimetry and SEM imaging were performed on cement pastes produced by hand-mixing and by spraying, using equivalent doses of an alkali-free and an alkaline accelerator and two types of cement. Results showed a great influence of the spraying process on the reactivity of accelerators and on the morphology of the precipitated hydrates. Variations in hydration kinetics caused by the mixing method are explained and the results obtained might have a significant repercussion on how future research on the behavior of accelerated mixes will be performed.

  20. The effect of blast furnace slag on the microstructure of the cement paste/steel interface

    International Nuclear Information System (INIS)

    Onabolu, O.A.; Pratt, P.L.

    1988-01-01

    The microstructures of steel reinforced ordinary Portland cement mortar samples, and those containing 40% and 70% slag as cement replacement, have been studied by electron optical techniques, after exposure to stagnant sea-water at 23 0 C for 320 days. Fracture surfaces along the interface with steel were examined using secondary electron imaging in the SEM. This revealed differences between the OPC and slag specimens as regards the morphology of the phases and the amounts of calcium hydroxide present. The microstructure at the interface with steel was studied by means of back scattered electron imaging combined with quantitative image analysis. Chloride concentrations at sections around the interface were determined by means of an EDXA facility linked to the SEM. Even after 320 days immersion in sea-water, there was some calcium hydroxide present in the interfacial zone

  1. Effects of Static Magnetic Fields on the Physical, Mechanical, and Microstructural Properties of Cement Pastes

    OpenAIRE

    Soto-Bernal, Juan J.; Gonzalez-Mota, Rosario; Rosales-Candelas, Iliana; Ortiz-Lozano, Jose A.

    2015-01-01

    This paper presents the results of an experimental study carried out to comprehend the physical, mechanical, and microstructural behavior of cement pastes subjected to static magnetic fields while hydrating and setting. The experimental methodology consisted in exposing fresh cement pastes to static magnetic fields at three different magnetic induction strengths: 19.07, 22.22, and 25.37 Gauss. The microstructural characterization makes evident that there are differences in relation to amount ...

  2. Experimental drying shrinkage of hardened cement pastes as a function of relative humidity

    DEFF Research Database (Denmark)

    Hansen, Kurt Kielsgaard; Baroghel, V.B.

    1996-01-01

    The results of an experimental study concerning drying shrinkage measured as a function of relative humidity on thin specimens of mature hardened cement pastes are presented. The results obtained at two laboratories are compared.......The results of an experimental study concerning drying shrinkage measured as a function of relative humidity on thin specimens of mature hardened cement pastes are presented. The results obtained at two laboratories are compared....

  3. Evolution of porosity in a Portland cement paste studied through positron annihilation lifetime spectroscopy

    International Nuclear Information System (INIS)

    Consolati, G.; Quasso, F.

    2003-01-01

    Positron annihilation lifetime spectroscopy experiments were carried out in an ordinary Portland cement paste characterized by a water-to-cement ratio w/c=0.8, in order to monitor the porosity of the paste. It was found that ortho-positronium intensity is a suitable quantity to this purpose, being sensitive to the amount of water contained in the pores. The experimental data show good agreement with the porosity calculated according to the Powers' thin filmsodel

  4. Strength and Deformability of Fiber Reinforced Cement Paste on the Basis of Basalt Fiber

    Directory of Open Access Journals (Sweden)

    Yury Barabanshchikov

    2016-01-01

    Full Text Available The research object of the paper is cement paste with the particulate reinforcement of basalt fiber. Regardless of fibers’ length at the same fiber cement mix workability and cement consumption equality compressive solidity of the specimens is reduced with increasing fiber content. This is due to the necessity to increase the water-cement ratio to obtain a given workability. The flexural stability of the specimens with increasing fiber content increments in the same conditions. There is an optimum value of the fibers’ dosage. That is why stability has a maximum when crooking. The basaltic fiber particulate reinforcement usage can abruptly increase the cement paste level limiting extensibility, which is extremely important in terms of crack resistance.

  5. Effect of addition of Sikament-R superplasticizer on the hydration characteristics of portland cement pastes

    Directory of Open Access Journals (Sweden)

    Safaa.M. El Gamal

    2012-08-01

    Full Text Available The effect of addition of Sikament-R superplasticizer (modified lignosulphonate base on the hydration characteristics of hardened Portland cement pastes were studied at different curing conditions. Four mixtures were prepared using 0, 0.2, 0.4 and 0.6 wt% addition of Sikament-R superplasticizer (SR of cement. These pastes were hydrated under two different conditions; (i normal curing at room temperature; 25 °C up to 90 days periods and (ii hydrothermal curing at a pressure of 8 atm. of saturated steam up to 24 h. The compressive strength, combined water content, free lime content, gel/space ratio and microstructure of hardened cement pastes were studied. The results revealed that addition of SR superplasticizer promote the dispersion of cement particles and interacts with Ca(OH2. The addition of SR superplasticizer exhibits Portland cement better workability during the preparation of pastes. In addition, amore compact structure were obtained leading to higher values of compressive strength for all the hardened hydrated pastes under both normal and hydrothermal curing. The results indicated that the addition of SR superplasticizer to Portland cement does not alter the types of hydration products formed during normal or hydrothermal conditions; only it caused a decrease in the degree of the porosity of the formed pastes.

  6. Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage

    Directory of Open Access Journals (Sweden)

    Hongzhi Cui

    2014-12-01

    Full Text Available In this research, structural-functional integrated cement-based materials were prepared by employing cement paste and a microencapsulated phase change material (MPCM manufactured using urea-formaldehyde resin as the shell and paraffin as the core material. The encapsulation ratio of the MPCM could reach up to 91.21 wt%. Thermal energy storage cement pastes (TESCPs incorporated with different MPCM contents (5%, 10%, 15%, 20% and 25% by weight of cement were developed, and their thermal and mechanical properties were studied. The results showed that the total energy storage capacity of the hardened cement specimens with MPCM increased by up to 3.9-times compared with that of the control cement paste. The thermal conductivity at different temperature levels (35–36 °C, 55–56 °C and 72–74 °C decreased with the increase of MPCM content, and the decrease was the highest when the temperature level was 55–56 °C. Moreover, the compressive strength, flexural strength and density of hardened cement paste decreased with the increase in MPCM content linearly. Among the evaluated properties, the compressive strength of TESCPs had a larger and faster degradation with the increase of MPCM content.

  7. Thermophysical and Mechanical Properties of Hardened Cement Paste with Microencapsulated Phase Change Materials for Energy Storage.

    Science.gov (United States)

    Cui, Hongzhi; Liao, Wenyu; Memon, Shazim Ali; Dong, Biqin; Tang, Waiching

    2014-12-16

    In this research, structural-functional integrated cement-based materials were prepared by employing cement paste and a microencapsulated phase change material (MPCM) manufactured using urea-formaldehyde resin as the shell and paraffin as the core material. The encapsulation ratio of the MPCM could reach up to 91.21 wt%. Thermal energy storage cement pastes (TESCPs) incorporated with different MPCM contents (5%, 10%, 15%, 20% and 25% by weight of cement) were developed, and their thermal and mechanical properties were studied. The results showed that the total energy storage capacity of the hardened cement specimens with MPCM increased by up to 3.9-times compared with that of the control cement paste. The thermal conductivity at different temperature levels (35-36 °C, 55-56 °C and 72-74 °C) decreased with the increase of MPCM content, and the decrease was the highest when the temperature level was 55-56 °C. Moreover, the compressive strength, flexural strength and density of hardened cement paste decreased with the increase in MPCM content linearly. Among the evaluated properties, the compressive strength of TESCPs had a larger and faster degradation with the increase of MPCM content.

  8. Strontium binding to cement paste cured at different temperature

    International Nuclear Information System (INIS)

    Peterson, V.K.; Ray, A.

    1999-01-01

    Concentration - depth profiles were measured using Proton Induced X-ray Emission (PIXE). These results were used as a measure of the Sr 2+ retention abilities of each matrix. Ordinary Portland cement (OPC) and cemented clinoptilolite samples were cured at 25 deg C, 60 deg C and 150 deg C. As expected, the Sr 2+ penetration depth increased with increasing OPC cure temperature, caused by an increase in sample permeability. Surprisingly, the penetration depths of Sr 2+ increased with the addition of clinoptilolite to the OPC, also thought to be caused by an increase in sample permeability. However, the increase in penetration depth was reduced in samples cured at higher temperatures

  9. Mechanical Properties and Durability of CNT Cement Composites

    Directory of Open Access Journals (Sweden)

    María del Carmen Camacho

    2014-02-01

    Full Text Available In the present paper, changes in mechanical properties of Portland cement-based mortars due to the addition of carbon nanotubes (CNT and corrosion of embedded steel rebars in CNT cement pastes are reported. Bending strength, compression strength, porosity and density of mortars were determined and related to the CNT dosages. CNT cement paste specimens were exposed to carbonation and chloride attacks, and results on steel corrosion rate tests were related to CNT dosages. The increase in CNT content implies no significant variations of mechanical properties but higher steel corrosion intensities were observed.

  10. Behaviour of corroded steel in a Ca(OH2-saturated solution and in cement mortar. Possibility of rehabilitation

    Directory of Open Access Journals (Sweden)

    Hernández, L. S.

    2007-03-01

    Full Text Available The present study compared the response of rust-free and corroded steel electrodes in Ca(OH2-saturated solutions and in cement mortar, essentially defined in terms of polarization resistance as measured with gravimetric, metallographic and electrochemical methods. Answers were sought for the following questions, which persist despite the use of reinforced concrete (RC in building for over a century: At what corrosion rate is RC durability seriously compromised? Does restoration of the initial conditions in properly manufactured concrete guarantee repassivation of corroded steel? Does the use of inhibitors enhance repassivation? Does the nature of the corrosion products have any significant effect on the response of corroded steel reinforcement? The results obtained in indicated that the effectiveness of preventive methods is much more closely related to the degree of existing corrosion than to the nature of the corrosion products.En el presente trabajo se analizan las respuestas de electrodos de acero, limpios y precorroídos, en soluciones saturadas de Ca(OH2 y en mortero de cemento, recurriendo para ello a técnicas gravimétricas, metalográficas y electroquímicas, esencialmente a medidas de resistencia de polarización. Se intenta encontrar respuesta a las siguientes dudas persistentes después de más de un siglo de utilización de las estructuras de hormigón armado (EHA: ¿qué velocidades de corrosión comprometen seriamente la durabilidad de las EHA? ¿La restauración de las condiciones iniciales de un hormigón correctamente fabricado garantiza la recuperación del estado pasivo en los refuerzos ya corroídos? ¿La utilización de inhibidores facilita la repasivación de los refuerzos? ¿Cambia la naturaleza de los productos de corrosión sustancialmente la respuesta de las armaduras ya corroídas? Los resultados obtenidos indican que la eficacia de las medidas preventivas resulta mucho más condicionada por el grado de

  11. Influence of chemical composition of civil construction waste in the cement paste

    International Nuclear Information System (INIS)

    Cunha, G.A.; Andrade, A.C.D.; Souza, J.M.M.; Evangelista, A.C.J.; Almeida, V.C.

    2009-01-01

    The construction and demolition waste when disposed inappropriately might cause serious public health problems. Its reutilization focusing on the development of new products using simple production techniques, assuring a new product life cycle and not damaging the environment is inserted in sustainable concept. The aim of this work was identifying the characteristics of types of waste generated in a residential reform (glassy ceramic and fill dirt leftovers) verifying separately its influence on cement pastes mechanical behavior. Cement pastes + wastes were prepared in 25% and 50% proportions with an approximately 0,35 water/cement relation and, glue time determination, water absorption, resistance to compression and X-ray fluorescence assays were taken. The results indicate that the chemical composition of the waste causes changes in the behavior of cement pastes, reflecting on their resistance to compression. (author)

  12. Influence of time addition of superplasticizers on the rheological properties of fresh cement pastes

    International Nuclear Information System (INIS)

    Aiad, Ismail

    2003-01-01

    It is well known that the fluidity and the fluidity loss of fresh cement pastes are affected by the kind and the time of addition of organic admixtures. The influence of the time addition of two chemical admixtures, namely, melamine formaldehyde sulfonate (MFS) and naphthalene formaldehyde sulfonate (NFS), on the rheological properties of ordinary Portland and sulfate-resisting cement pastes through the first 120 min of hydration was investigated. The admixture addition was delayed by 0, 5, 10, 15, 20, and 25 min. Shear stress and apparent viscosity of the cement pastes were determined at different shear rates (3-146 s -1 ) and hydration times of 30, 60, 90, and 120 min. The concentration of Ca 2+ and the combined water content of the cement pastes were determined after 120 min. Yield stress and plastic viscosity values were also determined by using the Bingham model. The results show that an increase in the addition time of the admixture reduces the shear stress, the yield stress, and the plastic viscosity of the cement pastes at the early ages (15 min) as well as at later early ages (120 min). The optimum delaying time of admixture addition is found to be 10-15 min. This time does not depend on the cement and superplasticizer type

  13. Early-age acoustic emission measurements in hydrating cement paste: Evidence for cavitation during solidification due to self-desiccation

    DEFF Research Database (Denmark)

    Lura, Pietro; Couch, J.; Jensen, Ole Mejlhede

    2009-01-01

    . According to these experimental results, the acoustic emission measured around setting time was attributed to cavitation events occurring in the pores of the cement paste due to self-desiccation. This paper shows how acoustic emission might be used to indicate the time when the fluid–solid transition occurs......In this study, the acoustic emission activity of cement pastes was investigated during the first day of hydration. Deaired, fresh cement pastes were cast in sealed sample holders designed to minimize friction and restraint. The majority of acoustic emission events occurred in lower water to cement...... ratio pastes, while cement pastes with higher water to cement ratios showed significantly less acoustic activity. These acoustic events occurred around the time of setting. A layer of water on the surface of the cement pastes substantially reduced acoustic emission activity at the time of setting...

  14. Influence of increasing amount of recycled concrete powder on mechanical properties of cement paste

    Science.gov (United States)

    Topič, Jaroslav; Prošek, Zdeněk; Plachý, Tomáš

    2017-09-01

    This paper deals with using fine recycled concrete powder in cement composites as micro-filler and partial cement replacement. Binder properties of recycled concrete powder are given by exposed non-hydrated cement grains, which can hydrate again and in small amount replace cement or improve some mechanical properties. Concrete powder used in the experiments was obtained from old railway sleepers. Infrastructure offer more sources of old concrete and they can be recycled directly on building site and used again. Experimental part of this paper focuses on influence of increasing amount of concrete powder on mechanical properties of cement paste. Bulk density, shrinkage, dynamic Young’s modulus, compression and flexural strength are observed during research. This will help to determine limiting amount of concrete powder when decrease of mechanical properties outweighs the benefits of cement replacement. The shrinkage, dynamic Young’s modulus and flexural strength of samples with 20 to 30 wt. % of concrete powder are comparable with reference cement paste or even better. Negative effect of concrete powder mainly influenced the compression strength. Only a 10 % cement replacement reduced compression strength by about 25 % and further decrease was almost linear.

  15. Chloride ingress in cement paste and mortar measured by Electron Probe Micro Analysis

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede

    1998-01-01

    is an important basis for designing the durability of concrete structures. As an example the Danish Great Belt link is designed to have 100 years durability based on calculation of chloride ingress.During the last 15 years the types of concrete used in practice have changed substantially. Due to plasticizers......Chloride ingress is a common cause of deterioration of reinforced concrete structures. Concrete may be exposed to chloride by sea water or deicing salts. The chloride initiates corrosion of the reinforcement which through expansion disrupts the concrete. Modelling the chloride ingress...... and mineral additives concretes with higher strengths and reduced permeability are produced. Recently it has become clear that traditional chloride ingress models do not apply to modern concretes. Actually, the life time model used for the Danish Great Belt link has shown up to be based on wrong assumptions...

  16. Sustainable Blended Cements-Influences of Packing Density on Cement Paste Chemical Efficiency.

    Science.gov (United States)

    Knop, Yaniv; Peled, Alva

    2018-04-18

    This paper addresses the development of blended cements with reduced clinker amount by partial replacement of the clinker with more environmentally-friendly material (e.g., limestone powders). This development can lead to more sustainable cements with reduced greenhouse gas emission and energy consumption during their production. The reduced clicker content was based on improved particle packing density and surface area of the cement powder by using three different limestone particle diameters: smaller (7 µm, 3 µm) or larger (70 µm, 53 µm) than the clinker particles, or having a similar size (23 µm). The effects of the different limestone particle sizes on the chemical reactivity of the blended cement were studied by X-ray diffraction (XRD), thermogravimetry and differential thermogravimetry (TG/DTG), loss on ignition (LOI), isothermal calorimetry, and the water demand for reaching normal consistency. It was found that by blending the original cement with limestone, the hydration process and the reactivity of the limestone itself were increased by the increased surface area of the limestone particles. However, the carbonation reaction was decreased with the increased packing density of the blended cement with limestone, having various sizes.

  17. Effect of Fly Ash and Silica Fume on the Mechanical Properties of Cement Paste at Different Stages of Hydration

    Science.gov (United States)

    2015-08-10

    All materials were placed in a clean, labeled stainless steel mixing bowl and weighed to the nearest ten thousandth of a pound. The cement and fly...on the Mechanical Properties of Cement Paste at Different Stages of Hydration This thesis investigates the effect of fly ash and silica fume on... cement paste hydration. Percentages of each additive will replace the cement by volume to be studied at five ages. These percentages will be compared

  18. Investigation of Rheological Properties of Blended Cement Pastes Using Rotational Viscometer and Dynamic Shear Rheometer

    Directory of Open Access Journals (Sweden)

    Yoo Jae Kim

    2018-01-01

    Full Text Available To successfully process concrete, it is necessary to predict and control its flow behavior. However, the workability of concrete is not completely measured or specified by current standard tests. Furthermore, it is only with a clear picture of cement hydration and setting that full prediction and control of concrete performance can be generalized. In order to investigate the rheological properties of blended cement pastes, a rotational viscometer (RV was used to determine the flow characteristics of ordinary and blended pastes to provide assurance that it can be pumped and handled. Additionally, a dynamic shear rheometer (DSR was used to characterize both the viscous and elastic components of pastes. Ordinary Portland cement paste and blended pastes (slag, fly ash, and silica fume were investigated in this study. The stress and strain of the blended specimens were measured by the DSR, which characterizes both viscous and elastic behaviors by measuring the complex shear modulus (the ratio of total shear stress to total shear strain and phase angle (an indicator of the relative amounts of recoverable and nonrecoverable deformation of materials. Cement pastes generally exhibit different rheological behaviors with respect to age, mineral admixture type, and cement replacement level.

  19. Reuse of ground waste glass as aggregate for mortars.

    Science.gov (United States)

    Corinaldesi, V; Gnappi, G; Moriconi, G; Montenero, A

    2005-01-01

    This work was aimed at studying the possibility of reusing waste glass from crushed containers and building demolition as aggregate for preparing mortars and concrete. At present, this kind of reuse is still not common due to the risk of alkali-silica reaction between the alkalis of cement and silica of the waste glass. This expansive reaction can cause great problems of cracking and, consequently, it can be extremely deleterious for the durability of mortar and concrete. However, data reported in the literature show that if the waste glass is finely ground, under 75mum, this effect does not occur and mortar durability is guaranteed. Therefore, in this work the possible reactivity of waste glass with the cement paste in mortars was verified, by varying the particle size of the finely ground waste glass. No reaction has been detected with particle size up to 100mum thus indicating the feasibility of the waste glass reuse as fine aggregate in mortars and concrete. In addition, waste glass seems to positively contribute to the mortar micro-structural properties resulting in an evident improvement of its mechanical performance.

  20. Influence of various amount of diatomaceous earth used as cement substitute on mechanical properties of cement paste

    Science.gov (United States)

    Pokorný, Jaroslav; Pavlíková, Milena; Medved, Igor; Pavlík, Zbyšek; Zahálková, Jana; Rovnaníková, Pavla; Černý, Robert

    2016-06-01

    Active silica containing materials in the sub-micrometer size range are commonly used for modification of strength parameters and durability of cement based composites. In addition, these materials also assist to accelerate cement hydration. In this paper, two types of diatomaceous earths are used as partial cement replacement in composition of cement paste mixtures. For raw binders, basic physical and chemical properties are studied. The chemical composition of tested materials is determined using classical chemical analysis combined with XRD method that allowed assessment of SiO2 amorphous phase content. For all tested mixtures, initial and final setting times are measured. Basic physical and mechanical properties are measured on hardened paste samples cured 28 days in water. Here, bulk density, matrix density, total open porosity, compressive and flexural strength, are measured. Relationship between compressive strength and total open porosity is studied using several empirical models. The obtained results give evidence of high pozzolanic activity of tested diatomite earths. Their application leads to the increase of both initial and final setting times, decrease of compressive strength, and increase of flexural strength.

  1. E-modulus evolution and its relation to solids formation of pastes from commercial cements

    International Nuclear Information System (INIS)

    Maia, Lino; Azenha, Miguel; Geiker, Mette; Figueiras, Joaquim

    2012-01-01

    Models for early age E-modulus evolution of cement pastes are available in the literature, but their validation is limited. This paper provides correlated measurements of early age evolution of E-modulus and hydration of pastes from five commercial cements differing in limestone content. A recently developed methodology allowed continuous monitoring of E-modulus from the time of casting. The methodology is a variant of classic resonant frequency methods, which are based on determination of the first resonant frequency of a composite beam containing the material. The hydration kinetics — and thus the rate of formation of solids — was determined using chemical shrinkage measurements. For the cements studied similar relationships between E-modulus and chemical shrinkage were observed for comparable water-to-binder ratio. For commercial cements it is suggested to model the E-modulus evolution based on the amount of binder reacted, instead of the degree of hydration.

  2. Using Mortar Mixing Pump for Magnesia Mortars Preparing and Transporting

    Science.gov (United States)

    Kiyanets, A. V.

    2017-11-01

    The article is devoted to the problem of preparation and transportation of magnesia mortars with the help of screw mortar mixing pumps. The urgency of the wide use of mortars on magnesia binders (Sorel’s cement) in construction is substantiated due to their high characteristics: strength, hardening speed, wear resistance, possibility of using organic and mineral aggregates, ecological purity and economic efficiency. The necessity for the development of a technique for calculating the main parameters of a mortar mixing pump for its application in the technology of preparation and transportation of magnesia mortars is demonstrated. The analysis of various types of modern mortar mixing pumps is given. The conclusions are drawn about the advantages and disadvantages of standard schemes. The description of the experiment for determination of the productivity of a mortar mixing pump is described depending on the plasticity (mobility) of the used magnesia mortar. The graph and description of the mathematical dependency of the productivity of the mortar mixing pump on the magnesia mortar plasticity are given. On the basis of the obtained dependency, as well as the already known formulas given in the article, a new method is proposed for calculating the main parameters of the screw mortar mixing pump in preparation and transportation of magnesia mortar: productivity, feed range, supply pressure, drive power.

  3. The influence of cellulose nanocrystals on the microstructure of cement paste

    Science.gov (United States)

    Yizheng Cao; Nannan Tian; David Bahr; Pablo D. Zavattieri; Jeffrey Youngblood; Robert J. Moon; Jason Weiss

    2016-01-01

    This paper reports the influence of raw and sonicated cellulose nanocrystals (CNCs) on the micro-structure of cement paste. A novel centrifugation method is designed to measure the concentrations of the adsorbed CNCs (aCNCs) on the cement surface, and the free CNCs (fCNCs) which are mobile in water. It is found that, the majority of the CNCs (>94%) are aCNCs....

  4. Preliminary observations of water movement in cement pastes during curing using X-ray absorption

    DEFF Research Database (Denmark)

    Bentz, D. P.; Hansen, Kurt Kielsgaard

    2000-01-01

    X-ray absorption and concurrent mass measurements are used in quantifying water movement in 4 to 5 mm thick cement paste specimens with their top surface exposed to drying. Experimental variables examined in this preliminary study include water-to-cement (wic) ratio and open vs. capped samples....... The implications of these experimental observations for curing of concrete and application of repair materials are discussed....

  5. Chloride diffusivity in hardened cement paste from microscale analyses and accounting for binding effects

    OpenAIRE

    Carrara, P; De Lorenzis, L; Bentz, D P

    2016-01-01

    The diffusion of chloride ions in hardened cement paste (HCP) under steady-state conditions and accounting for the highly heterogeneous nature of the material is investigated. The HCP microstructures are obtained through segmentation of X-ray images of real samples as well as from simulations using the cement hydration model CEMHYD3D. Moreover, the physical and chemical interactions between chloride ions and HCP phases (binding), along with their effects on the diffusive process, are explicit...

  6. Rheological Properties of Very High-Strength Portland Cement Pastes: Influence of Very Effective Superplasticizers

    Directory of Open Access Journals (Sweden)

    Adriano Papo

    2010-01-01

    Full Text Available The influence of the addition of very effective superplasticizers, that are commercially available, employed for maximising the solid loading of very high-strength Portland cement pastes, has been investigated. Cement pastes were prepared from deionized water and a commercially manufactured Portland cement (Ultracem 52.5 R. Cement and water were mixed with a vane stirrer according to ASTM Standard C305. The 0.38 to 0.44 water/cement ratio range was investigated. Three commercial superplasticizing agents produced by Ruredil S.p.a. were used. They are based on a melamine resin (Fluiment 33 M, on a modified lignosulphonate (Concretan 200 L, and on a modified polyacrylate (Ergomix 1000. Rheological tests were performed at 25°C by using the rate controlled coaxial cylinder viscometer Rotovisko-Haake 20, system M5-osc., measuring device MV2P with serrated surfaces. The tests were carried out under continuous flow conditions. The results of this study were compared with those obtained in a previous article for an ordinary Portland cement paste.

  7. Mechano-Physical Properties and Microstructure of Carbon Nanotube Reinforced Cement Paste after Thermal Load.

    Science.gov (United States)

    Szeląg, Maciej

    2017-09-11

    The article presents the results obtained in the course of a study on the use of carbon nanotubes (CNTs) for the modification of a cement matrix. Carbon nanotubes were introduced into a cement paste in the form of an aqueous dispersion in the presence of a surfactant (SDS-sodium dodecyl sulfate), which was sonicated. The selected physical and mechanical parameters were examined, and the correlations between these parameters were determined. An analysis of the local microstructure of the modified cement pastes has been carried out using scanning electron microscope (SEM) and X-ray microanalysis (EDS). In addition, the effect of carbon nanotubes on the change in characteristics of the cementitious material exposed to the sudden, short-term thermal load, was determined. The obtained material was characterized by a much lower density than a traditional cement matrix because the phenomenon of foaming occurred. The material was also characterized by reduced durability, higher shrinkage, and higher resistance to the effect of elevated temperature. Further research on the carbon nanotube reinforced cement paste, with SDS, may contribute to the development of a modified cement binder for the production of a lightweight or an aerated concrete.

  8. Mechano-Physical Properties and Microstructure of Carbon Nanotube Reinforced Cement Paste after Thermal Load

    Science.gov (United States)

    2017-01-01

    The article presents the results obtained in the course of a study on the use of carbon nanotubes (CNTs) for the modification of a cement matrix. Carbon nanotubes were introduced into a cement paste in the form of an aqueous dispersion in the presence of a surfactant (SDS—sodium dodecyl sulfate), which was sonicated. The selected physical and mechanical parameters were examined, and the correlations between these parameters were determined. An analysis of the local microstructure of the modified cement pastes has been carried out using scanning electron microscope (SEM) and X-ray microanalysis (EDS). In addition, the effect of carbon nanotubes on the change in characteristics of the cementitious material exposed to the sudden, short-term thermal load, was determined. The obtained material was characterized by a much lower density than a traditional cement matrix because the phenomenon of foaming occurred. The material was also characterized by reduced durability, higher shrinkage, and higher resistance to the effect of elevated temperature. Further research on the carbon nanotube reinforced cement paste, with SDS, may contribute to the development of a modified cement binder for the production of a lightweight or an aerated concrete. PMID:28891976

  9. Hydration kinetics of cements by Time-Domain Nuclear Magnetic Resonance: Application to Portland-cement-derived endodontic pastes

    International Nuclear Information System (INIS)

    Bortolotti, Villiam; Fantazzini, Paola; Mongiorgi, Romano; Sauro, Salvatore; Zanna, Silvano

    2012-01-01

    Time-Domain Nuclear Magnetic Resonance (TD-NMR) of 1 H nuclei is used to monitor the maturation up to 30 days of three different endodontic cement pastes. The “Solid–liquid” separation of the NMR signals and quasi-continuous distributions of relaxation times allow one to follow the formation of chemical compounds and the build-up of the nano- and subnano-structured C–S–H gel. 1 H populations, distinguished by their different mobilities, can be identified and assigned to water confined within the pores of the C–S–H gel, to crystallization water and Portlandite, and to hydroxyl groups. Changes of the TD-NMR parameters during hydration are in agreement with the expected effects of the different additives, which, as it is known, can substantially modify the rate of reactions and the properties of cementitious pastes. Endodontic cements are suitable systems to check the ability of this non-destructive technique to give insight into the complex hydration process of real cement pastes.

  10. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Kwang Yeom, E-mail: kimky@kict.re.kr [Korea Institute of Construction Technology, 283 Goyangdae-ro, Ilsanseo-gu, Goyang 411-712 (Korea, Republic of); Yun, Tae Sup, E-mail: taesup@yonsei.ac.kr [School of Civil and Environmental Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 120-749 (Korea, Republic of); Park, Kwang Pil, E-mail: bamtol97@kict.re.kr [Korea Institute of Construction Technology, 283 Goyangdae-ro, Ilsanseo-gu, Goyang 411-712 (Korea, Republic of)

    2013-08-15

    When cement-based materials are exposed to the high temperatures induced by fire, which can rapidly cause temperatures of over 1000 °C, the changes in pore structure and density prevail. In the present study, mortar specimens were subjected to a series of increasing temperatures to explore the temperature-dependent evolution of internal pore structure. High-performance X-ray computed tomography (CT) was used to observe the evolution of temperature-induced discontinuities at the sub-millimeter level. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed to investigate the cause of physical changes in the heated mortar specimens. Results exhibit the changes in pore structure caused by elevated temperatures, and thermally induced fractures. We discuss the progressive formation of thermally induced fracture networks, which is a prerequisite for spalling failure of cement-based materials by fire, based on visual observations of the 3D internal structures revealed by X-ray CT.

  11. Evaluation of pore structures and cracking in cement paste exposed to elevated temperatures by X-ray computed tomography

    International Nuclear Information System (INIS)

    Kim, Kwang Yeom; Yun, Tae Sup; Park, Kwang Pil

    2013-01-01

    When cement-based materials are exposed to the high temperatures induced by fire, which can rapidly cause temperatures of over 1000 °C, the changes in pore structure and density prevail. In the present study, mortar specimens were subjected to a series of increasing temperatures to explore the temperature-dependent evolution of internal pore structure. High-performance X-ray computed tomography (CT) was used to observe the evolution of temperature-induced discontinuities at the sub-millimeter level. X-ray diffraction (XRD) and scanning electron microscopy (SEM) were employed to investigate the cause of physical changes in the heated mortar specimens. Results exhibit the changes in pore structure caused by elevated temperatures, and thermally induced fractures. We discuss the progressive formation of thermally induced fracture networks, which is a prerequisite for spalling failure of cement-based materials by fire, based on visual observations of the 3D internal structures revealed by X-ray CT

  12. Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste

    International Nuclear Information System (INIS)

    Yoon, Seyoon; Moon, Juhyuk; Bae, Sungchul; Duan, Xiaonan; Giannelis, Emmanuel P.; Monteiro, Paulo M.

    2014-01-01

    This study investigated the feasibility of using calcined layered double hydroxides (CLDHs) to prevent chloride-induced deterioration in reinforced concrete. CLDHs not only adsorbed chloride ions in aqueous solution with a memory effect but also had a much higher binding capacity than the original layered double hydroxides (LDHs) in the cement matrix. We investigated this adsorption in hardened cement paste in batch cultures to determine adsorption isotherms. The measured and theoretical binding capacities (153 mg g −1 and 257 mg g −1 , respectively) of the CLDHs were comparable to the theoretical capacity of Friedel's salt (2 mol mol −1 or 121 mg g −1 ), which belongs to the LDH family among cementitious phases. We simulated chloride adsorption by CLDHs through the cement matrix using the Fickian model and compared the simulation result to the X-ray fluorescence (XRF) chlorine map. Based on our results, it is proposed that the adsorption process is governed by the chloride transport through the cement matrix; this process differs from that in an aqueous solution. X-ray diffraction (XRD) analysis showed that the CLDH rebuilds the layered structure in a cementitious environment, thereby demonstrating the feasibility of applying CLDHs to the cement and concrete industries. - Highlights: • We examine the adsorption equilibrium and kinetics of CLDH in the hydrated cement. • CLDH capacity to bind chloride ions in the hydrated cement paste is determined. • We model chloride adsorption by CLDH through the cement matrix. • CLDH reforms the layered structure with ion adsorption in the cement matrix

  13. Deterioration of limestone aggregate mortars by liquid sodium in fast breeder reactor environment

    Energy Technology Data Exchange (ETDEWEB)

    Mohammed Haneefa, K., E-mail: mhkolakkadan@gmail.com [Department of Civil Engineering, IIT Madras, Chennai (India); Santhanam, Manu [Department of Civil Engineering, IIT Madras, Chennai (India); Parida, F.C. [Radiological Safety Division, Indira Gandhi Centre for Atomic Research, Kalpakkam (India)

    2014-08-15

    Highlights: • Limestone mortars were exposed to liquid sodium exposure at 550 °C. • Micro-analytical techniques were used to characterize the exposed specimens. • The performance of limestone mortar was greatly influenced by w/c. • The fundamental degradation mechanisms of limestone mortars were identified. - Abstract: Hot liquid sodium at 550 °C can interact with concrete in the scenario of an accidental spillage of sodium in liquid metal cooled fast breeder reactors. To protect the structural concrete from thermo-chemical degradation, a sacrificial layer of limestone aggregate concrete is provided over it. This study investigates the fundamental mechanisms of thermo-chemical interaction between the hot liquid sodium and limestone mortars at 550 °C for a duration of 30 min in open air. The investigation involves four different types of cement with variation of water-to-cement ratios (w/c) from 0.4 to 0.6. Comprehensive analysis of experimental results reveals that the degree of damage experienced by limestone mortars displayed an upward trend with increase in w/c ratios for a given type of cement. Performance of fly ash based Portland pozzolana cement was superior to other types of cements for a w/c of 0.55. The fundamental degradation mechanisms of limestone mortars during hot liquid sodium interactions include alterations in cement paste phase, formation of sodium compounds from the interaction between solid phases of cement paste and aggregate, modifications of interfacial transition zone (ITZ), decomposition of CaCO{sub 3}, widening and etching of rhombohedral cleavages, and subsequent breaking through the weakest rhombohedral cleavage planes of calcite, staining, ferric oxidation in grain boundaries and disintegration of impurity minerals in limestone.

  14. Deterioration of limestone aggregate mortars by liquid sodium in fast breeder reactor environment

    International Nuclear Information System (INIS)

    Mohammed Haneefa, K.; Santhanam, Manu; Parida, F.C.

    2014-01-01

    Highlights: • Limestone mortars were exposed to liquid sodium exposure at 550 °C. • Micro-analytical techniques were used to characterize the exposed specimens. • The performance of limestone mortar was greatly influenced by w/c. • The fundamental degradation mechanisms of limestone mortars were identified. - Abstract: Hot liquid sodium at 550 °C can interact with concrete in the scenario of an accidental spillage of sodium in liquid metal cooled fast breeder reactors. To protect the structural concrete from thermo-chemical degradation, a sacrificial layer of limestone aggregate concrete is provided over it. This study investigates the fundamental mechanisms of thermo-chemical interaction between the hot liquid sodium and limestone mortars at 550 °C for a duration of 30 min in open air. The investigation involves four different types of cement with variation of water-to-cement ratios (w/c) from 0.4 to 0.6. Comprehensive analysis of experimental results reveals that the degree of damage experienced by limestone mortars displayed an upward trend with increase in w/c ratios for a given type of cement. Performance of fly ash based Portland pozzolana cement was superior to other types of cements for a w/c of 0.55. The fundamental degradation mechanisms of limestone mortars during hot liquid sodium interactions include alterations in cement paste phase, formation of sodium compounds from the interaction between solid phases of cement paste and aggregate, modifications of interfacial transition zone (ITZ), decomposition of CaCO 3 , widening and etching of rhombohedral cleavages, and subsequent breaking through the weakest rhombohedral cleavage planes of calcite, staining, ferric oxidation in grain boundaries and disintegration of impurity minerals in limestone

  15. Characterization of different types of ceramic waste and its incorporation to the cement paste

    International Nuclear Information System (INIS)

    Cunha, G.A.; Evangelista, A.C.J.; Almeida, V.C. de

    2009-01-01

    The porcelain tike is a product resulting from the technological development of ceramic plating industry. Its large acceptation by the consumer market is probably linked with certain properties, such as low porosity, high mechanical resistance, facility in maintenance, besides being a material of modern and versatile characteristics. The aim of this work was characterizing the different ceramic wastes (enameled and porcelain tike) and evaluating its influence on the mechanical behavior in cement pastes. The wastes were characterized through the determination of its chemical composition, size particle distribution and X-ray diffraction. Cement pastes + wastes were prepared in 25% and 50% proportions and glue time determination, water absorption and resistance to compression assays were taken. The results indicate that although the wastes don't show any variation in the elementary chemical composition, changes in the cement paste behavior related to the values of resistance to compression were observed. (author)

  16. Rehydration and microstructure of cement paste after heating at temperatures up to 300 deg. C

    International Nuclear Information System (INIS)

    Farage, M.C.R.; Sercombe, J.; Galle, C.

    2003-01-01

    This paper is concerned with the evolution of the microstructure of cementitious materials subjected to high temperatures and subsequent resaturation in the particular context of long-term storage of radioactive wastes, where diffusive and convective properties are of primary importance. Experimental results obtained by mercury intrusion porosimetry (MIP) are presented concerning the evolution of the pore network of ordinary portland cement (OPC) paste heated at temperatures varying between 80 and 300 deg. C. The consequences of heating on the macroscopic properties of cement paste are evaluated by measures of the residual gas permeabilities, elastic moduli and Poisson's ratio, obtained by nondestructive methods. Resaturation by direct water absorption and water vapour sorption are used to estimate the reversibility of dehydration. The results provide some evidence of the self-healing capacity of resaturated cement paste after heating at temperatures up to 300 deg. C

  17. Effects of densified silica fume on microstructure and compressive strength of blended cement pastes

    International Nuclear Information System (INIS)

    Ji Yajun; Cahyadi, Jong Herman

    2003-01-01

    Some experimental investigations on the microstructure and compressive strength development of silica fume blended cement pastes are presented in this paper. The silica fume replacement varies from 0% to 20% by weight and the water/binder ratio (w/b) is 0.4. The pore structure by mercury intrusion porosimetry (MIP), the micromorphology by scanning electron microscopy (SEM) and the compressive strength at 3, 7, 14, 28, 56 and 90 days have been studied. The test results indicate that the improvements on both microstructure and mechanical properties of hardened cement pastes by silica fume replacement are not effective due to the agglomeration of silica fume particles. The unreacted silica fume remained in cement pastes, the threshold diameter was not reduced and the increase in compressive strength was insignificant up to 28 days. It is suggested that the proper measures should be taken to disperse silica fume agglomeration to make it more effective on improving the properties of materials

  18. FRP confined smart concrete/mortar

    Science.gov (United States)

    Xiao, Y.; Zhu, P. S.; Choi, K. G.; Wu, Y. T.; Huang, Z. Y.; Shan, B.

    2006-03-01

    In this study, fiber reinforced polymer (FRP) confined smart concrete/mortar sensors were invented and validated for significantly improved measurement range. Several trial mixes were made using cement mortar and micron-phase graphite powders at different mix proportions. Compressive loading tests were conducted on smart mortar cylinder specimens with or without FRP confinement. Two-probe method was used to detect the electrical resistance of the smart cement mortar specimens. Strong correlation was recognized between the stress and electric resistance of the smart mortar. The test results indicated that the FRP wrapping could significantly enlarge the range of such self-sensing property as a consequence of confinement.

  19. Evaluation of water behavior between aggregate and cement paste matrix by neutron radiography

    International Nuclear Information System (INIS)

    Maruyama, Ippei; Kanematsu, Manabu; Teramoto, Atsushi; Hayano, Hiroyuki; Iikura, Hiroshi; Noguchi, Takafumi

    2009-01-01

    The purpose of this study is to evaluate a water-supplied area from the saturated lightweight aggregate in high strength concrete. For this objective, phenomena of water transfer between cement paste, whose water to cement ratio is 0.25, and aggregates is visualized by neutron radiography technique. The parameter of this test was the type of aggregates, namely saturated lightweight aggregate, air dried lightweight aggregate, and ordinary sandstone. Additionally the steel is also tested for understanding the 'wall-effect'. Experimental results show that water supply from saturated lightweight aggregate continued upto more than 14days, and the water supplied area of cement paste was ranged within 4mm from the aggregate surface, and air dried lightweight aggregate suck the water from cement paste upto 12 hours and that water was released after 24 hours. Reduction of water content in cement paste, which was seen in both the test with steel and ordinary sandstone, was ranged within 1.2 mm from the surface. (author)

  20. Influence of MWCNT/surfactant dispersions on the mechanical properties of Portland cement pastes

    Science.gov (United States)

    Rodríguez, B.; Quintero, J. H.; Arias, Y. P.; Mendoza-Reales, O. A.; Ochoa-Botero, J. C.; Toledo-Filho, R. D.

    2017-12-01

    This work studies the reinforcing effect of Multi Walled Carbon Nanotubes (MWCNT) on cement pastes. A 0.35% solid concentration of MWCNT in powder was dispersed in deionized water with sodium dodecyl sulfate (cationic surfactant), cetylpyridinium chloride (anionic surfactant) and triton X-100 (amphoteric surfactant) using an ultrasonic tip processor. Three concentrations of each surfactant (1mM, 10mM and 100mM) were tested, and all samples were sonicated until an adequate dispersion degree was obtained. Cement pastes with additions of carbon nanotubes of 0.15% by mass of cement were produced in two steps; first the dispersions of MWCNT were combined with the mixing water using an ultrasonic tip processor to guarantee homogeneity, and then cement was added and mixed until a homogeneous paste was obtained. Direct tensile strength, apparent density and open porosity of the pastes were measured after 7 days of curing. It was found that the MWCNT/surfactants dispersions decrease the mechanical properties of the cement based matrix due to an increased porosity caused by the presence of surfactants.

  1. Laboratory investigation of the influence of two types of modified hydrotalcites on chloride ingress into cement mortar

    NARCIS (Netherlands)

    Yang, Z.; Fischer, H.; Polder, R.

    2015-01-01

    Owing to the unique molecular structure and high ion exchange capacity, hydrotalcites are believed to have a potential to be modified and tailor-made as an active component of mortar and/or concrete. In this paper, two types of modified hydrotalcites (MHT-pAB and MHT-NO2) were incorporated into

  2. Friedel's salt profiles from thermogravimetric analysis and thermodynamic modelling of Portland cement-based mortars exposed to sodium chloride solution

    DEFF Research Database (Denmark)

    Shi, Zhenguo; Geiker, Mette Rica; Lothenbach, Barbara

    2017-01-01

    Thermogravimetric analysis (TGA), powder X-ray diffraction (XRD) and thermodynamic modelling have been used to obtain Friedel's salt profiles for saturated mortar cylinders exposed to a 2.8 M NaCl solution. Comparison of the measured Friedel's salt profiles with the total chloride profiles...

  3. The effect of temperature rise on microstructural properties of cement-based materials : Correlation of experimental data and a simulation approach

    NARCIS (Netherlands)

    Susanto, A.; Koleva, D.A.; Van Breugel, K.

    2015-01-01

    This work reports on the influence of stray current flow on temperature rise in hardening cement-based materials and consequently altered cement hydration. To simulate stray current, different levels of electrical current were applied to cement paste and mortar specimens immediately after casting.

  4. Autogenous Deformation and Change of the Relative Humidity in Silica Fume-Modified Cement Paste

    DEFF Research Database (Denmark)

    Jensen, Ole mejlhede; Hansen, Per Freiesleben

    1996-01-01

    Even during sealed curing and at a constant temperature a hardening cement paste will deform and the relative humidity within its pores will lower. This autogenous deformation and autogenous relative humidity change may be so significant that the cement paste cracks if the deformation is restrained....... This article focuses on the influence of silica fume addition on autogenous deformation and autogenous relative humidity change. Continuous measurement of autogenous deformation and autogenous relative humidity change for more than 1 year and 1« years, respectively, was performed. The investigations show...... thatsilica fume addition markedly increases the autogenous shrinkage as well as the autogenous relative humidity change....

  5. Water dynamics in hardened ordinary Portland cement paste or concrete: from quasielastic neutron scattering.

    Science.gov (United States)

    Bordallo, Heloisa N; Aldridge, Laurence P; Desmedt, Arnaud

    2006-09-14

    Portland cement reacts with water to form an amorphous paste through a chemical reaction called hydration. In concrete the formation of pastes causes the mix to harden and gain strength to form a rock-like mass. Within this process lies the key to a remarkable peculiarity of concrete: it is plastic and soft when newly mixed, strong and durable when hardened. These qualities explain why one material, concrete, can build skyscrapers, bridges, sidewalks and superhighways, houses, and dams. The character of the concrete is determined by the quality of the paste. Creep and shrinkage of concrete specimens occur during the loss and gain of water from cement paste. To better understand the role of water in mature concrete, a series of quasielastic neutron scattering (QENS) experiments were carried out on cement pastes with water/cement ratio varying between 0.32 and 0.6. The samples were cured for about 28 days in sealed containers so that the initial water content would not change. These experiments were carried out with an actual sample of Portland cement rather than with the components of cement studied by other workers. The QENS spectra differentiated between three different water interactions: water that was chemically bound into the cement paste, the physically bound or "glassy water" that interacted with the surface of the gel pores in the paste, and unbound water molecules that are confined within the larger capillary pores of cement paste. The dynamics of the "glassy" and "unboud" water in an extended time scale, from a hundred picoseconds to a few nanoseconds, could be clearly differentiated from the data. While the observed motions on the picosecond time scale are mainly stochastic reorientations of the water molecules, the dynamics observed on the nanosecond range can be attributed to long-range diffusion. Diffusive motion was characterized by diffusion constants in the range of (0.6-2) 10(-9) m(2)/s, with significant reduction compared to the rate of diffusion

  6. On the effect of mixing on property development of cement pastes

    DEFF Research Database (Denmark)

    Geiker, Mette Rica; Bøhm, Anja; Kjeldsen, Ane Mette

    2006-01-01

    by hand and in a high-speed mixer. Chemical shrinkage was measured to illustrate the effect of mixing on development of hydration. Chloride migration was measured on 28 days old pastes to illustrate the effect of mixing on the hydrated pastes. The present investigation of pastes of white Portland cement...... showed an effect of mixing on the development of chemical shrinkage, i.e. hydration, of pastes with superplasticizer, but without silica fume. Silica fume agglomerates were observed in thin sections of pastes with silica fume and mixed by hand; however no effect on the development of hydration...

  7. THE EFFECT OF PLASTICIZER ON MECHANICAL PROPERTIES OF THE CEMENT PASTE WITH FINE GROUND RECYCLED CONCRETE

    Directory of Open Access Journals (Sweden)

    Jaromír Hrůza

    2017-11-01

    Full Text Available This article deals with the usage of recycled concrete, which arises from the demolition of concrete structures. The work is focused on the development of mechanical properties (Young's modulus, compressive and flexural strength depending amount of plasticizer in the mixture. In the experiment were prepared three sets of samples with different amounts of plasticizer (0, 0.5 and 1.0 wt. % of cement. Each pair always contained reference samples (only cement and 35 wt. % of fine ground recycled concrete. One of the main reasons for the use of finely ground recycled concrete was a certain substitution of cement in the mixture, which is the most expensive component. Development of Young's modulus was measured by the nondestructive method. The aim of the experiment was to determine the effect of plasticizer on the resulting physical and mechanical properties of cement pastes with fine ground recycled concrete.

  8. Structure investigations on Portland cement paste by small angle neutron scattering

    International Nuclear Information System (INIS)

    Dragolici, C. A.; Len, A.

    2003-01-01

    Portland cement pastes consist of many crystalline and non-crystalline phases in various ranges of sizes (nm and mm scale). The crystalline phases are embedded in amorphous phases of the hydration products. We investigated the structural changes of hydrating phases in the time interval of 1-30 days at Budapest Neutron Center's SANS diffractometer. The small angle neutron scattering of Portland cements prepared with a water-to-cement ratio from 0,3 to 0,8 gave us information about the microstructure changes in the material. Fractals were a suitable way for structure modelling. The variation of fractals size depending on the preparation-to-measurement time interval and water-to-cement ratio could be observed. (authors)

  9. Individual and combined effects of chloride, sulfate, and magnesium ions on hydrated Portland-cement paste

    International Nuclear Information System (INIS)

    Poole, T.S.; Wakeley, L.D.; Young, C.L.

    1994-03-01

    Ground water with a high concentration of magnesium ion is known to cause deterioration to portland cement concretes. A proposed mechanism for this deterioration process published previously involves an approximate 1:1 replacement of Ca ions by Mg ions in the crystalline phases of hydrated cement. The current study was undertaken to determine which ions, among magnesium, chloride, and sulfate, cause deterioration; whether their deleterious action is individual or interdependent; and to relate this mechanism of deterioration to the outlook for a 100-yr service life of concretes used in mass placements at the Waste Isolation Pilot Plant. Loss of Ca ion by cement pastes was found to be strongly related to the concentration of Mg ion in simulated ground-water solutions in which the paste samples were aged. This was true of both salt- containing and conventional cement pastes. No other ion in the solutions exerted a strong effect on Ca loss. Ca ion left first from calcium hydroxide in the pastes, depleting all calcium hydroxide by 60 days. Some calcium silicate hydrate remained even after 90 days in the solutions with the highest concentration of Mg ion, while the paste samples deteriorated noticeably. The results indicated a mechanism that involves dissolution of Ca phases and transport of Ca ions to the surface of the sample, followed by formation of Mg-bearing phases at this reaction surface rather than directly by substitution within the microstructure of hydrated cement. Given that calcium hydroxide and calcium silicate hydrate are the principal strength-giving phases of hydrated cement, this mechanism indicates the likelihood of significant loss of integrity of a concrete exposed to Mg-bearing ground water at the WIPP. The rate of deterioration ultimately will depend on Mg-ion concentration, the microstructure materials of the concrete exposed to that groundwater, and the availability of brine

  10. Flow properties of MK-based geopolymer pastes. A comparative study with standard Portland cement pastes.

    Science.gov (United States)

    Favier, Aurélie; Hot, Julie; Habert, Guillaume; Roussel, Nicolas; d'Espinose de Lacaillerie, Jean-Baptiste

    2014-02-28

    Geopolymers are presented in many studies as alternatives to ordinary Portland cement. Previous studies have focused on their chemical and mechanical properties, their microstructures and their potential applications, but very few have focussed on their rheological behaviour. Our work highlights the fundamental differences in the flow properties, which exist between geopolymers made from metakaolin and Ordinary Portland Cement (OPC). We show that colloidal interactions between metakaolin particles are negligible and that hydrodynamic effects control the rheological behaviour. Metakaolin-based geopolymers can then be described as Newtonian fluids with the viscosity controlled mainly by the high viscosity of the suspending alkaline silicate solution and not by the contribution of direct contacts between metakaolin grains. This fundamental difference between geopolymers and OPC implies that developments made in cement technology to improve rheological behaviour such as plasticizers will not be efficient for geopolymers and that new research directions need to be explored.

  11. The durability of mortar: consideration of interfacial transition zones to characterize and to model the physicals and chemicals mechanisms involved in mortar corrosion

    International Nuclear Information System (INIS)

    Bourdette, B.

    1994-01-01

    In the framework of a study program aiming at anticipating the lifetime of concrete containers used for radioactive waste surface storage, the aim of this work is to model the physical and chemical processes of leaching of the mortars (cement paste + sand) by low ionized water at pH=8.5. This step is indispensable before the predicting of concrete durability (cement paste + sand + gravels) in which it can exist an initial microcrack. The mortar can be described as a three-phase system: the aggregates, the transition aureoles (aggregates-cement paste interfaces) and the cement matrix. The evolution of the very particular characteristics of the transition aureoles in terms of the degradation have been studied. The study has shown that the thickness of the degraded zone in the transition aureole is identical to those of the cement matrix. It has been shown too that the diffusion coefficient in the degraded transition aureole is similar to the diffusion coefficient in the degraded cement matrix. These observations can eventually be explained by a recombination of the texture and of the structure of the transition aureole during the degradation. This reorganization could lead to a decrease of the textural and structural differences which exist between the transition aureole and the cement matrix. As it has been supposed that the characteristics of the degraded zone govern the degradation kinetics, the thickness degraded in the transition aureole is then similar to those of the cement matrix. Mortar can then be considered as a two-phase system towards the degradation: the cement paste is assimilated to a pure paste but with different characteristics due to the presence of transition aureoles. In order to model the degradation of the mortar, the model used has been developed and validated by Adenot for pure cement pastes. At 300 years, the model anticipates that the thickness of the degraded zone in the mortar is of 2.9 cm, which is lightly higher than for the pure paste

  12. Mineralogy and chemistry of cement paste in borehole radioactive waste repository

    International Nuclear Information System (INIS)

    Ferreira, Eduardo G.A.; Isiki, Vera L.K.; Miyamoto, Hissae; Marumo, Julio T.; Vicente, Roberto

    2009-01-01

    Results of chemical characterization of cement paste samples after irradiation and immersion in salt solutions are presented. This is part of a research on cement paste behavior aiming at investigating the durability of cementitious materials in the environment of repositories for radioactive waste. Portland cement paste is intended to be used as a backfill in a deep borehole for disposal of sealed radiation sources which concept is under development. The service life of the engineered barrier materials plays an important role in the long term safety of such facilities. Accelerated tests in laboratory are being used to evaluate the performance of cement paste under the temperature expected at some hundred meters below grade, under exposure to the radiation emitted by the sources, and under the attack of aggressive chemicals dissolved in the groundwater, during the millennia necessary for the decay of the most active and long-lived radionuclides present in the waste. ICP-OES, Ion chromatography, X-ray diffraction, SEM and TGA are some techniques being employed in this research project. (author)

  13. Influence of temperature on autogenous deformation and relative humidity change in hardening cement paste

    DEFF Research Database (Denmark)

    Jensen, Ole Mejlhede; Hansen, Per Freiesleben

    1999-01-01

    This paper deals with autogenous deformation and autogenous relative humidity change (RH change) in hardening cement paste. Theoretical considerations and experimental data are presented, which elucidate the influence of temperature on these properties. This is an important subject in the control...

  14. Cement paste surface roughness analysis using coherence scanning interferometry and confocal microscopy

    International Nuclear Information System (INIS)

    Apedo, K.L.; Munzer, C.; He, H.; Montgomery, P.; Serres, N.; Fond, C.; Feugeas, F.

    2015-01-01

    Scanning electron microscopy and scanning probe microscopy have been used for several decades to better understand the microstructure of cementitious materials. Very limited work has been performed to date to study the roughness of cementitious materials by optical microscopy such as coherence scanning interferometry (CSI) and chromatic confocal sensing (CCS). The objective of this paper is to better understand how CSI can be used as a tool to analyze surface roughness and topography of cement pastes. Observations from a series of images acquired using this technique on both polished and unpolished samples are described. The results from CSI are compared with those from a STIL confocal microscopy technique (SCM). Comparison between both optical techniques demonstrates the ability of CSI to measure both polished and unpolished cement pastes. - Highlights: • Coherence scanning interferometry (CSI) was used to analyze cement paste surfaces. • The results from the CSI were compared with those from a confocal microscopy. • 3D roughness parameters were obtained using the window resizing method. • Polished and unpolished cement pastes were studied

  15. Cement paste surface roughness analysis using coherence scanning interferometry and confocal microscopy

    Energy Technology Data Exchange (ETDEWEB)

    Apedo, K.L., E-mail: apedo@unistra.fr [ICube, Université de Strasbourg, CNRS, 2 rue Boussingault, 67000 Strasbourg (France); Munzer, C.; He, H. [ICube, INSA de Strasbourg, CNRS, 24 Bld de la Victoire, 67084 Strasbourg (France); Montgomery, P. [ICube, Université de Strasbourg, CNRS, 23 rue du Loess, 67037 Strasbourg (France); Serres, N. [ICube, INSA de Strasbourg, CNRS, 24 Bld de la Victoire, 67084 Strasbourg (France); Fond, C. [ICube, Université de Strasbourg, CNRS, 2 rue Boussingault, 67000 Strasbourg (France); Feugeas, F. [ICube, INSA de Strasbourg, CNRS, 24 Bld de la Victoire, 67084 Strasbourg (France)

    2015-02-15

    Scanning electron microscopy and scanning probe microscopy have been used for several decades to better understand the microstructure of cementitious materials. Very limited work has been performed to date to study the roughness of cementitious materials by optical microscopy such as coherence scanning interferometry (CSI) and chromatic confocal sensing (CCS). The objective of this paper is to better understand how CSI can be used as a tool to analyze surface roughness and topography of cement pastes. Observations from a series of images acquired using this technique on both polished and unpolished samples are described. The results from CSI are compared with those from a STIL confocal microscopy technique (SCM). Comparison between both optical techniques demonstrates the ability of CSI to measure both polished and unpolished cement pastes. - Highlights: • Coherence scanning interferometry (CSI) was used to analyze cement paste surfaces. • The results from the CSI were compared with those from a confocal microscopy. • 3D roughness parameters were obtained using the window resizing method. • Polished and unpolished cement pastes were studied.

  16. Application of water vapor sorption measurements for porosity characterization of hardened cement pastes

    DEFF Research Database (Denmark)

    Wu, Min; Johannesson, Björn; Geiker, Mette Rica

    2014-01-01

    data were reviewed. Water vapor sorption measurements were then applied to two hardened cement pastes and one model porous material MCM-41. The specific surface area was calculated based on different equations accounting for multilayer adsorption and the PSD was analyzed from both the absorption...

  17. Measurement of water transport from saturated pumice aggregates to hardening cement paste

    DEFF Research Database (Denmark)

    Lura, Pietro; Bentz, Dale; Lange, David A.

    2006-01-01

    In internal water curing of High Performance Concrete, it is fundamental to know how and when the water contained in the internal curing agent is released into the hydrating cement paste. In this study, X-ray absorption measurements showed that considerable transport of water from saturated pumice...... the crucial factor to avoid self-desiccation shrinkage at early-age....

  18. Water demand of amorphous nano silica and their impact on the workability of cement paste

    NARCIS (Netherlands)

    Quercia Bianchi, G.; Hüsken, G.; Brouwers, H.J.H.

    2012-01-01

    This paper addresses the characterization of six different amorphous silica samples with respect to their application in cement paste. Different mixes are compared and analyzed using the mini spread-flow test method. Also the granular properties, different void fraction states of packing and

  19. Experimental and numerical study on cement paste degradation under external sulfate attack

    NARCIS (Netherlands)

    Ma, X.; Copuroglu, O.; Schlangen, H.E.J.G.; Han, N; Xing, F; Saouma, V.; Bolander, J.; Landis, E.

    2016-01-01

    External sulfate attack is one of the situations that may cause gradual but severe damage in cementitious materials, which may lead to cracking, increased permeability and strength loss. In this paper, thin-walled hollow cement paste cylinders with a wall thickness of 2.5mm were made considering the

  20. POF based smart sensor for studying the setting dynamics of cement paste

    International Nuclear Information System (INIS)

    Rajesh, M; Sheeba, M; Nampoori, V P N

    2007-01-01

    Fiber optic smart sensors are used to monitor the civil structures. One of the important parameters in civil engineering is the setting characteristics of concrete made of cement. The paper discusses how a simple polymer optical fiber can be used to characterise the setting dynamics of various grades of cement. The results explain the comparative performance of polymer fiber over silica fiber. The basic principle underlying the sensor is that as the cement sets, it exerts a stress on the sensing fiber, which is laid within the cement paste. This stress induces strain on the optical fiber, which can be thought of as a series of aperiodic microbends on the surface of the fiber. This in turn changes the characteristics of the light signal transmitted through the fiber and can be viewed as stress induced modulation of light in the fiber. By monitoring the intensity variation of transmitted light signal with time we can determine the cement setting rate. This can be used as an effective tool for quality testing of commercially available cements of different grades

  1. Effect of Limestone Powder on Acid Attack Characteristics of Cement Pastes

    Directory of Open Access Journals (Sweden)

    Shuhua LIU

    2014-12-01

    Full Text Available The acid resistance of cement pastes containing limestone powder with two different water-binder (w/b ratios exposed to acetic (pH = 4 and sulfuric acid (pH = 2 solutions respectively were investigated in this paper. Limestone powder, fly ash and silica fume were also added to the cement paste mixture at different proportions. Static and flowing aqueous environments were set in this experiment. Strength and microstructure of the pastes after acid attack were investigated by using strength test, X-ray diffractometer (XRD and scanning electron microscopy (SEM. The experimental results show that the erosion degree depends not only on pH value of the solution and w/b ratio of the pastes, but also on the content of limestone powder. Acetic acid reacts with calcium hydroxide and carbonate thus dissolving the pastes, while sulfuric acid consumed calcium hydroxide, and generated gypsum and ettringite. The consumption of calcium hydroxide in the flowing solution group is higher than that in the static solution because the flowing sulfuric acid solution has negative effect upon the gypsum crystallization. Fly ash and silica fume are beneficial to limestone cement paste because of the less calcium hydroxide formation, which is among the hydrates vulnerable to acid erosion. DOI: http://dx.doi.org/10.5755/j01.ms.20.4.6231

  2. Addition of Silica Fume to Improve Strength of Cement Paste

    Science.gov (United States)

    Chen, Jiajian; Chen, Hongniao; Li, Gu

    2018-03-01

    This study measured the packing densities of 0 to 30% silica fume (SF) added cementitious materials and strength of the cementitious pastes with various water content. The results revealed that addition of silica fume up to a certain level has great effects on packing density and strength. In-depth analysis illustrated that a lower W/CM ratio would not always result in a higher cube strength, and the range between 0.05 and 0.07 µm would be the amount of water film thickness (WFT) for muximum strength.

  3. A thermal comparator sensor for measuring autogenous deformation in hardening Portland cement paste

    DEFF Research Database (Denmark)

    Østergaard, Thomas; Jensen, Ole Mejlhede

    2003-01-01

    This paper describes a simple and accurate experimental device specially developed to measure autogenous deformation in hardening cement-based materials. The measuring system consists of a so-called thermal comparator sensor and a modular thermostatically controlled system. The operating principle...... of the thermal comparator is based on thermal expansion of aluminium. A particular characteristic of the measuring system is the fixation of the thermal comparator sensor to the deforming specimen. The modular system ensures effective thermostatic control of the hydrating cement paste samples. The technique...... allows continuous measurement with high accuracy of the linear deformation as well as determination of the activation energy of autogenous deformation....

  4. Radon exhalation of cementitious materials made with coal fly ash: Part 2 - testing hardened cement-fly ash pastes

    International Nuclear Information System (INIS)

    Kovler, K.; Perevalov, A.; Levit, A.; Steiner, V.; Metzger, L.A.

    2005-01-01

    Increased interest in measuring radionuclides and radon concentrations in fly ash (FA), cement and other components of building products is due to the concern about health hazards of naturally occurring radioactive materials (NORM). The paper focuses on studying the influence of FA on radon exhalation rate (radon flux) from cementitious materials. In the previous part of the paper the state of the art was presented, and the experiments for testing raw materials, Portland cement and coal fly ash, were described. Since the cement and FA have the most critical role in the radon release process relative to other concrete constituents (sand and gravel), and their contribution is dominant in the overall radium content of concrete, tests were carried out on cement paste specimens with different FA contents, 0-60% by weight of the binder (cement+FA). It is found that the dosage of FA in cement paste has a limited influence on radon exhalation rate, if the hardened material is relatively dense. The radon flux of cement-FA pastes is lower than that of pure cement paste: it is about ∼3 mBq m -2 s -1 for cement-FA pastes with FA content as high as 960 kg m -3

  5. Estimation of the degree of hydration of blended cement pastes by a scanning electron microscope point-counting procedure

    International Nuclear Information System (INIS)

    Feng, X.; Garboczi, E.J.; Bentz, D.P.; Stutzman, P.E.; Mason, T.O.

    2004-01-01

    A scanning electron microscope (SEM) point-counting technique was employed to study the hydration of plain portland and blended cement pastes containing fly ash or slag. For plain portland cement pastes, the results for the degree of cement hydration obtained by the SEM point-counting technique were consistent with the results from the traditional loss-on-ignition (LOI) of nonevaporable water-content measurements; agreement was within ±10%. The standard deviation in the determination of the degree of cement hydration via point counting ranged from ±1.5% to ±1.8% (one operator, one sample). For the blended cement pastes, it is the first time that the degree of hydration of cement in blended systems has been studied directly. The standard deviation for the degree of hydration of cement in the blended cement pastes ranged from ±1.4% to ±2.2%. Additionally, the degrees of reaction of the mineral admixtures (MAs) were also measured. The standard deviation for the degree of fly ash reaction was ±4.6% to ±5.0% and ±3.6% to ±4.3% for slag. All of the analyses suggest that the SEM point-counting technique can be a reliable and effective analysis tool for use in studies of the hydration of blended cement pastes

  6. Creep and fatigue behavior of a novel 2-component paste-like formulation of acrylic bone cements

    OpenAIRE

    Köster, U.; Jaeger, R.; Bardts, M.; Wahnes, C.; Büchner, H.; Kühn, K.-D.; Vogt, S.

    2013-01-01

    The fatigue and creep performance of two novel acrylic bone cement formulations (one bone cement without antibiotics, one with antibiotics) was compared to the performance of clinically used bone cements (Osteopal V, Palacos R, Simplex P, SmartSet GHV, Palacos R+G and CMW1 with Gentamicin). The preparation of the novel bone cement formulations involves the mixing of two paste-like substances in a static mixer integrated into the cartridge which is used to apply the bone cement. The fatigue pe...

  7. Experimental and modeling study of Portland cement paste degradation in boric acid

    International Nuclear Information System (INIS)

    Benakli, A.; Chomat, L.; Le Bescop, P.; Wall, J.

    2015-01-01

    In the framework of Spent Fuel Pools (SFP) lifetime studies, an investigation of the Portland cement degradation in boric acid has been requested by the Electric Power Research Institute. The main goal of this study is to identify the physico-chemical degradation mechanisms involved in boric acid media. Both experimental and modeling approaches are considered. Concerning degradation experiments, sample of cement paste are immersed during three and nine months in a boric acid solution at 2400 ppm that is periodically renewed. Boric acid concentration has been chosen to be representative of SFP solution. Results will be confronted with reactive transport numerical calculations performed by the reactive transport code HYTEC associated with a dedicated extended database called Thermoddem. The analysis of degradation solution revealed a main ions release mechanism driven by diffusion especially for calcium, nitrate, sodium and sulfate. Leaching behavior of magnesium seems to be more complex. Decalcification is the major degradation process involved, even if a non-negligible contribution of further cations (Mg 2+ , Na + ) and anions (SO 4 2- ) has been noticed. Analysis of degradation soution also revealed that kinetic of Portland cement paste degradation in boric acid is higher than in pure water, regarding the degraded depths measured and calcium leaching rate. This observation has been confirmed by solid characterization. Microstructure analysis of degraded Portland cement paste showed a global porosity increase in the degraded zone that might be mainly attributed to Portlandite dissolution. An Ettringite reprecipitation in the degraded zone has been suspected but could also be Ettringite-like phases containing boron. The analysis techniques used did not allow us to differentiate it, and no others specific mineral phases containing boron has been identified. Profile pattern by XRD analysis allowed us to identify four zones composing the degraded Portland cement paste

  8. Effect of Admixtures on the Yield Stresses of Cement Pastes under High Hydrostatic Pressures.

    Science.gov (United States)

    Yim, Hong Jae; Kim, Jae Hong; Kwon, Seung Hee

    2016-03-02

    When cement-based materials are transported at a construction site, they undergo high pressures during the pumping process. The rheological properties of the materials under such high pressures are unknown, and estimating the workability of the materials after pumping is a complex problem. Among various influential factors on the rheology of concrete, this study investigated the effect of mineral and chemical admixtures on the high-pressure rheology. A rheometer was fabricated that could measure the rheological properties while maintaining a high pressure to simulate the pumping process. The effects of superplasticizer, silica fume, nanoclay, fly ash, or ground granulated blast furnace slag were investigated when mixed with two control cement pastes. The water-to-cement ratios were 0.35 and 0.50.

  9. Corrosivity of cement pastes with addition of sludge generated in water treatment plant

    International Nuclear Information System (INIS)

    Rodrigues, R.A.; Martins, B.E.D.B.S.; Couto, V.M.P.; Carvalho, L.J.; Almeida, V.C.

    2011-01-01

    The amount of sludge produced in a water treatment plant (WTP) is an important economic factor in the context of waste treatment. The present article has the objective of study the corrosion of cement pastes produced with blended sludge. Aqueous extracts were produced from the milling of masses containing 5%, 10% and 30% of sludge in relation to cement after 28 days of healing. These extracts were used for polarization assays in order to determine the corrosiveness of the folders when in contact with the used fittings. Moreover, other chemical analysis tests were carried out for sludge characterization: X-ray fluorescence and X-ray diffraction. The obtained results point to the possibility of use of the studied cement masses in the development of construction materials promoting the economic reuse of WTP sludge before discarded in landfills. (author)

  10. Effect of Admixtures on the Yield Stresses of Cement Pastes under High Hydrostatic Pressures

    Directory of Open Access Journals (Sweden)

    Hong Jae Yim

    2016-03-01

    Full Text Available When cement-based materials are transported at a construction site, they undergo high pressures during the pumping process. The rheological properties of the materials under such high pressures are unknown, and estimating the workability of the materials after pumping is a complex problem. Among various influential factors on the rheology of concrete, this study investigated the effect of mineral and chemical admixtures on the high-pressure rheology. A rheometer was fabricated that could measure the rheological properties while maintaining a high pressure to simulate the pumping process. The effects of superplasticizer, silica fume, nanoclay, fly ash, or ground granulated blast furnace slag were investigated when mixed with two control cement pastes. The water-to-cement ratios were 0.35 and 0.50.

  11. Crack-closing of cement mortar beams using NiTi cold-drawn SMA short fibers

    Science.gov (United States)

    Choi, Eunsoo; Kim, Dong Joo; Chung, Young-Soo; Kim, Hee Sun; Jung, Chungsung

    2015-01-01

    In this study, crack-closing tests of mortar beams reinforced by shape memory alloy (SMA) short fibers were performed. For this purpose, NiTi SMA fibers with a diameter of 0.965 mm and a length of 30 mm were made from SMA wires of 1.0 mm diameter by cold drawing. Four types of SMA fibers were prepared, namely, straight and dog-bone-shaped fiber and the two types of fibers with paper wrapping in the middle of the fibers. The paper provides an unbonded length of 15 mm. For bending tests, six types of mortar beams with the dimensions of 40 mm × 40 mm × 160 mm (B×H×L) were prepared. The SMA fibers were placed at the bottom center of the beams along with an artificial crack of 10 mm depth and 1 mm thickness. This study investigated the influence of SMA fibers on the flexural strength of the beams from the measured force- deflection curves. After cracking, the beams were heated at the bottom by fire to activate the SMA fibers. Then, the beams recovered the deflection, and the cracks were closed. This study evaluated crack-closing capacity using the degree of crack recovery and deflection-recovery factor. The first factor is estimated from the crack-width before and after crack-closing, and the second one is obtained from the downward deflection due to loading and the upward deflection due to the closing force of the SMA fibers.

  12. Farklı Puzolanik Katkıların Çimento Harçlarının Mekanik Özelikleri Üzerine Etkisi = The Effect of Different Puzzolanic Additives on Mechanical Properties of Cement Mortars

    Directory of Open Access Journals (Sweden)

    H. Aygül YEPREM

    2004-06-01

    Full Text Available In this study, cement mortar samples containing fly ash obtained from Soma Power Plant, two different types of natural pozzolan supplied from Yenişehir and Bilecik and silica fume from Antalya Ferrocrom Industry partial replacement of cement clinker. The strength of the mortars prepared by these mixtures were investigated. The mixtures were prepared by using 10% fly ash and 5% silica fume and the trass contents varied as 30%, 35%, and 40%. Chemical analyses of these mixtures were carried out and Blaine specific surface area values were measured. In performed tests, the highest strength values were noticed in mortars containing natural puzzolan from Bilecik which has high fineness.

  13. Chloride adsorption by calcined layered double hydroxides in hardened Portland cement paste

    KAUST Repository

    Yoon, Seyoon

    2014-06-01

    This study investigated the feasibility of using calcined layered double hydroxides (CLDHs) to prevent chloride-induced deterioration in reinforced concrete. CLDHs not only adsorbed chloride ions in aqueous solution with a memory effect but also had a much higher binding capacity than the original layered double hydroxides (LDHs) in the cement matrix. We investigated this adsorption in hardened cement paste in batch cultures to determine adsorption isotherms. The measured and theoretical binding capacities (153 mg g -1 and 257 mg g-1, respectively) of the CLDHs were comparable to the theoretical capacity of Friedel\\'s salt (2 mol mol-1 or 121 mg g-1), which belongs to the LDH family among cementitious phases. We simulated chloride adsorption by CLDHs through the cement matrix using the Fickian model and compared the simulation result to the X-ray fluorescence (XRF) chlorine map. Based on our results, it is proposed that the adsorption process is governed by the chloride transport through the cement matrix; this process differs from that in an aqueous solution. X-ray diffraction (XRD) analysis showed that the CLDH rebuilds the layered structure in a cementitious environment, thereby demonstrating the feasibility of applying CLDHs to the cement and concrete industries. © 2014 Published by Elsevier B.V. All rights reserved.

  14. Investigation on the Rheological Behavior of Fly Ash Cement Composites at Paste and Concrete Level

    Science.gov (United States)

    Thiyagarajan, Hemalatha; Mapa, Maitri; Kushwaha, Rakhi

    2018-06-01

    Towards developing sustainable concrete, nowadays, high volume replacement of cement with fly ash (FA) is more common. Though the replacement of fly ash at 20-30% is widely accepted due to its advantages at both fresh and hardened states, applicability and acceptability of high volume fly ash (HVFA) is not so popular due to some adverse effects on concrete properties. Nowadays to suit various applications, flowing concretes such as self compacting concrete is often used. In such cases, implications of usage of HVFA on fresh properties are required to be investigated. Further, when FA replacement is beyond 40% in cement, it results in the reduction of strength and in order to overcome this drawback, additions such as nano calcium carbonate (CC), lime sludge (LS), carbon nano tubes (CNT) etc. are often incorporated to HVFA concrete. Hence, in this study, firstly, the influence of replacement level of 20-80% FA on rheological property is studied for both cement and concrete. Secondly, the influence of additions such as LS, CC and CNT on rheological parameters are discussed. It is found that the increased FA content improved the flowability in paste as well as in concrete. In paste, the physical properties such as size and shape of fly ash is the reason for increased flowability whereas in concrete, the paste volume contributes dominantly for the flowability rather than the effect due to individual FA particle. Reduced density of FA increases the paste volume in FA concrete thus reducing the interparticle friction by completely coating the coarse aggregate.

  15. The Retentive Strength of Cemented Zirconium Oxide Crowns after Dentin Pretreatment with Desensitizing Paste Containing 8% Arginine and Calcium Carbonate

    Science.gov (United States)

    Pilo, Raphael; Harel, Noga; Nissan, Joseph; Levartovsky, Shifra

    2016-01-01

    The effect of dentin pretreatment with Desensitizing Paste containing 8% arginine and calcium carbonate on the retention of zirconium oxide (Y-TZP) crowns was tested. Forty molar teeth were mounted and prepared using a standardized protocol. Y-TZP crowns were produced using computer-aided design and computer-aided manufacturing (CAD-CAM) technology. The 40 prepared teeth were either pretreated with Desensitizing Paste or not pretreated. After two weeks, each group was subdivided into two groups, cemented with either Resin Modified Glass Ionomer Cement (RMGIC) or Self Adhesive Resin Cement (SARC)). Prior to cementation, the surface areas of the prepared teeth were measured. After aging, the cemented crown-tooth assemblies were tested for retentive strength using a universal testing machine. The debonded surfaces of the teeth and crowns were examined microscopically at 10× magnification. Pretreating the dentin surfaces with Desensitizing Paste prior to cementation did not affect the retention of the Y-TZP crowns. The retentive values for RMGIC (3.04 ± 0.77 MPa) were significantly higher than those for SARC (2.28 ± 0.58 MPa). The predominant failure modes for the RMGIC and SARC were adhesive cement-dentin and adhesive cement-crown, respectively. An 8.0% arginine and calcium carbonate in-office desensitizing paste can be safely used to reduce post-cementation sensitivity without reducing the retentive strength of Y-TZP crowns. PMID:27023532

  16. The Retentive Strength of Cemented Zirconium Oxide Crowns after Dentin Pretreatment with Desensitizing Paste Containing 8% Arginine and Calcium Carbonate

    Directory of Open Access Journals (Sweden)

    Raphael Pilo

    2016-03-01

    Full Text Available The effect of dentin pretreatment with Desensitizing Paste containing 8% arginine and calcium carbonate on the retention of zirconium oxide (Y-TZP crowns was tested. Forty molar teeth were mounted and prepared using a standardized protocol. Y-TZP crowns were produced using computer-aided design and computer-aided manufacturing (CAD-CAM technology. The 40 prepared teeth were either pretreated with Desensitizing Paste or not pretreated. After two weeks, each group was subdivided into two groups, cemented with either Resin Modified Glass Ionomer Cement (RMGIC or Self Adhesive Resin Cement (SARC. Prior to cementation, the surface areas of the prepared teeth were measured. After aging, the cemented crown-tooth assemblies were tested for retentive strength using a universal testing machine. The debonded surfaces of the teeth and crowns were examined microscopically at 10× magnification. Pretreating the dentin surfaces with Desensitizing Paste prior to cementation did not affect the retention of the Y-TZP crowns. The retentive values for RMGIC (3.04 ± 0.77 MPa were significantly higher than those for SARC (2.28 ± 0.58 MPa. The predominant failure modes for the RMGIC and SARC were adhesive cement-dentin and adhesive cement-crown, respectively. An 8.0% arginine and calcium carbonate in-office desensitizing paste can be safely used to reduce post-cementation sensitivity without reducing the retentive strength of Y-TZP crowns.

  17. Assessment of aggregates- cement paste border in concretes containing silica fume and fly ash

    Directory of Open Access Journals (Sweden)

    Ali Sademomtazi

    2017-12-01

    Full Text Available The bond between aggregate and cement paste, called the interfacial transition zone (ITZ is an important parameter that effect on the mechanical properties and durability of concrete. Transition zone microstructure and porosity (pores of cement paste or concrete are affected by the type and properties of materials used which evaluated in this research. On the other hand, the use of efficient, low-cost and reliable method is particularly important for evaluating of concrete performance against the chloride ion penetration and its relationships with transition zone as a suitable index to assess the durability. So far, various methods to approach the electrical Indices are presented. In this research, the effect of pozzolanic materials fly ash (10%, 20% and 30% and silica fume (5% and 10% as substitute of cement by weight in binary and ternary mixtures on the fresh and hardened concrete properties were investigated. To determine mechanical properties, the compressive strength, splitting tensile strength and modulus of elasticity tests were performed. Also, water penetration depth, porosity, water sorptivity, specific electrical resistivity, rapid chloride penetration test (RCPT and rapid chloride migration test (RCMT tests were applied to evaluate concrete durability. To examine the border of aggregate and cement paste morphology of concrete specimens, scanning electron microscope images (SEM was used. The fresh concrete results showed that the presence of silica fume in binary and ternary mixtures reduced workability and air content but fly ash increased them. Adding silica fume to mixtures of containing flay ash while increasing mechanical strength reduced the porosity and pores to 18%. The presence of pozzolanic materials in addition to increasing bond quality and uniformity of aggregate-cement matrix border a considerably positive effect on the transport properties of concrete.

  18. Evaluation of water transfer from saturated lightweight aggregate to cement paste matrix by neutron radiography

    International Nuclear Information System (INIS)

    Maruyama, I.; Kanematsu, M.; Noguchi, T.; Iikura, H.; Teramoto, A.; Hayano, H.

    2009-01-01

    In high-strength concrete with low water-cement ratio, self-desiccation occurs due to cement hydration and causes shrinkage and an increased risk of cracking. While high-strength concrete has a denser matrix than normal-strength concrete, resulting in lower permeability, early-age cracks would cancel out this advantage. For the mitigation of this self-desiccation and resultant shrinkage, water-saturated porous aggregate, such as artificial lightweight aggregate, may be used in high-strength concrete. In this contribution, for the purpose of clarification of the volume change of high-strength concrete containing water-saturated lightweight aggregate, water transfer from the lightweight aggregate to cement paste matrix is visualized by neutron radiography. As a result, it is clear that water was supplied to the cement paste matrix in the range 3-8 mm from the surface of the aggregate, and the osmotic forces may yield water transfer around lightweight aggregate in a few hours after mixing.

  19. Development of carbon nanotube modified cement paste with microencapsulated phase-change material for structural-functional integrated application.

    Science.gov (United States)

    Cui, Hongzhi; Yang, Shuqing; Memon, Shazim Ali

    2015-04-10

    Microencapsulated phase-change materials (MPCM) can be used to develop a structural-functional integrated cement paste having high heat storage efficiency and suitable mechanical strength. However, the incorporation of MPCM has been found to degrade the mechanical properties of cement based composites. Therefore, in this research, the effect of carbon nanotubes (CNTs) on the properties of MPCM cement paste was evaluated. Test results showed that the incorporation of CNTs in MPCM cement paste accelerated the cement hydration reaction. SEM micrograph showed that CNTs were tightly attached to the cement hydration products. At the age of 28 days, the percentage increase in flexural and compressive strength with different dosage of CNTs was found to be up to 41% and 5% respectively. The optimum dosage of CNTs incorporated in MPCM cement paste was found to be 0.5 wt %. From the thermal performance test, it was found that the cement paste panels incorporated with different percentages of MPCM reduced the temperature measured at the center of the room by up to 4.6 °C. Inverse relationship was found between maximum temperature measured at the center of the room and the dosage of MPCM.

  20. Development of Carbon Nanotube Modified Cement Paste with Microencapsulated Phase-Change Material for Structural–Functional Integrated Application

    Directory of Open Access Journals (Sweden)

    Hongzhi Cui

    2015-04-01

    Full Text Available Microencapsulated phase-change materials (MPCM can be used to develop a structural–functional integrated cement paste having high heat storage efficiency and suitable mechanical strength. However, the incorporation of MPCM has been found to degrade the mechanical properties of cement based composites. Therefore, in this research, the effect of carbon nanotubes (CNTs on the properties of MPCM cement paste was evaluated. Test results showed that the incorporation of CNTs in MPCM cement paste accelerated the cement hydration reaction. SEM micrograph showed that CNTs were tightly attached to the cement hydration products. At the age of 28 days, the percentage increase in flexural and compressive strength with different dosage of CNTs was found to be up to 41% and 5% respectively. The optimum dosage of CNTs incorporated in MPCM cement paste was found to be 0.5 wt %. From the thermal performance test, it was found that the cement paste panels incorporated with different percentages of MPCM reduced the temperature measured at the center of the room by up to 4.6 °C. Inverse relationship was found between maximum temperature measured at the center of the room and the dosage of MPCM.

  1. Thermogravimetric analyses and mineralogical study of polymer modified mortar with silica fume

    Directory of Open Access Journals (Sweden)

    Alessandra Etuko Feuzicana de Souza Almeida

    2006-09-01

    Full Text Available Mineral and organic additions are often used in mortars to improve their properties. Microstructural investigation concerning the effects of styrene acrylic polymer and silica fume on the mineralogical composition of high-early-strength portland cement pastes after 28 days of hydration are presented in this paper. Thermogravimetry and derivative thermogravimetry were used to study the interaction between polymers and cement, as well as the extent of pozzolanic reaction of the mortars with silica fume. Differential scanning calorimetry and X ray diffraction were used to investigate the cement hydration and the effect of the additions. The results showed that the addition of silica fume and polymer reduces the portlandite formation due to delaying of Portland cement hydration and pozzolanic reaction.

  2. Autogenous shrinkage in high-performance cement paste: An evaluation of basic mechanisms

    DEFF Research Database (Denmark)

    Lura, Pietro; Jensen, Ole Mejlhede; van Breugel, Klaas

    2003-01-01

    In this paper, various mechanisms Suggested to cause autogenous shrinkage are presented. The mechanisms are evaluated from the point of view of their soundness and applicability to quantitative modeling of autogenous shrinkage. The capillary tension approach is advantageous, because it has a sound...... mechanical and thermodynamical basis. Furthermore, this mechanism is easily applicable in a numerical model when dealing with a continuously changing microstructure. In order to test the numerical model, autogenous deformation and internal relative humidity (RH) of a Portland cement paste were measured...... on the capillary tension approach. Because a part of the RH drop in the cement paste is due to dissolved salts in the pore solution, a method is suggested to separate this effect from self-desiccation and to calculate the actual stress in the pore fluid associated with menisci formation....

  3. The mechanical properties and hydration characteristics of cement pastes containing added-calcium coal gangue

    Energy Technology Data Exchange (ETDEWEB)

    Dongxu Li; Xuyan Song [Nanjing University of Technology, Nanjing (China). College of Material Science and Engineering

    2008-04-15

    The mechanical properties of several kinds of coal gangue calcined with limestone were researched so as to find the optimum way of calcinations with limestone. The microstructure and property of hydration process of cement pastes containing added-calcium coal gangue were analyzed by means of scanning electron microscope (SEM) and the method of mercury in trusion poremeasurement. When the proper amounst of gypsum and fluorite were taken as mineralizers in the course of calcinations of added-calcium coal gangue, the activity of coal gangue can be effectively improved. The results of mechanical property and structural characteristics such as hydration, hydration products and microstructure etc. of cement pastes containing added-calcium coal gangue are consistent.

  4. Pore size distribution, strength, and microstructure of portland cement paste containing metal hydroxide waste

    Energy Technology Data Exchange (ETDEWEB)

    Majid, Z.A.; Mahmud, H.; Shaaban, M.G.

    1996-12-31

    Stabilization/solidification of hazardous wastes is used to convert hazardous metal hydroxide waste sludge into a solid mass with better handling properties. This study investigated the pore size development of ordinary portland cement pastes containing metal hydroxide waste sludge and rice husk ash using mercury intrusion porosimetry. The effects of acre and the addition of rice husk ash on pore size development and strength were studied. It was found that the pore structures of mixes changed significantly with curing acre. The pore size shifted from 1,204 to 324 {angstrom} for 3-day old cement paste, and from 956 to 263 {angstrom} for a 7-day old sample. A reduction in pore size distribution for different curing ages was also observed in the other mixtures. From this limited study, no conclusion could be made as to any correlation between strength development and porosity. 10 refs., 6 figs., 3 tabs.

  5. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    KAUST Repository

    Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

    2014-01-01

    In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

  6. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    KAUST Repository

    Itty, Pierre-Adrien

    2014-06-01

    In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover. © 2014 Elsevier Ltd.

  7. High-efficiency cogeneration boiler bagasse-ash geochemistry and mineralogical change effects on the potential reuse in synthetic zeolites, geopolymers, cements, mortars, and concretes.

    Science.gov (United States)

    Clark, Malcolm W; Despland, Laure M; Lake, Neal J; Yee, Lachlan H; Anstoetz, Manuela; Arif, Elisabeth; Parr, Jeffery F; Doumit, Philip

    2017-04-01

    Sugarcane bagasse ash re-utilisation has been advocated as a silica-rich feed for zeolites, pozzolans in cements and concretes, and geopolymers. However, many papers report variable success with the incorporation of such materials in these products as the ash can be inconsistent in nature. Therefore, understanding what variables affect the ash quality in real mills and understanding the processes to characterise ashes is critical in predicting successful ash waste utilisation. This paper investigated sugarcane bagasse ash from three sugar mills (Northern NSW, Australia) where two are used for the co-generation of electricity. Data shows that the burn temperatures of the bagasse in the high-efficiency co-generation boilers are much higher than those reported at the temperature measuring points. Silica polymorph transitions indicate the high burn temperatures of ≈1550 °C, produces ash dominated α -quartz rather than expected α-cristobilite and amorphous silica; although α-cristobilite, and amorphous silica are present. Furthermore, burn temperatures must be ≤1700 °C, because of the absence of lechatelierite where silica fusing and globulisation dominates. Consequently, silica-mineralogy changes deactivate the bagasse ash by reducing silica solubility, thus making bagasse ash utilisation in synthetic zeolites, geopolymers, or a pozzolanic material in mortars and concretes more difficult. For the ashes investigated, use as a filler material in cements and concrete has the greatest potential. Reported mill boiler temperatures discrepancies and the physical characteristics of the ash, highlight the importance of accurate temperature monitoring at the combustion seat if bagasse ash quality is to be prioritised to ensure a usable final ash product.

  8. High-efficiency cogeneration boiler bagasse-ash geochemistry and mineralogical change effects on the potential reuse in synthetic zeolites, geopolymers, cements, mortars, and concretes

    Directory of Open Access Journals (Sweden)

    Malcolm W. Clark

    2017-04-01

    Full Text Available Sugarcane bagasse ash re-utilisation has been advocated as a silica-rich feed for zeolites, pozzolans in cements and concretes, and geopolymers. However, many papers report variable success with the incorporation of such materials in these products as the ash can be inconsistent in nature. Therefore, understanding what variables affect the ash quality in real mills and understanding the processes to characterise ashes is critical in predicting successful ash waste utilisation. This paper investigated sugarcane bagasse ash from three sugar mills (Northern NSW, Australia where two are used for the co-generation of electricity. Data shows that the burn temperatures of the bagasse in the high-efficiency co-generation boilers are much higher than those reported at the temperature measuring points. Silica polymorph transitions indicate the high burn temperatures of ≈1550 °C, produces ash dominated α −quartz rather than expected α-cristobilite and amorphous silica; although α-cristobilite, and amorphous silica are present. Furthermore, burn temperatures must be ≤1700 °C, because of the absence of lechatelierite where silica fusing and globulisation dominates. Consequently, silica-mineralogy changes deactivate the bagasse ash by reducing silica solubility, thus making bagasse ash utilisation in synthetic zeolites, geopolymers, or a pozzolanic material in mortars and concretes more difficult. For the ashes investigated, use as a filler material in cements and concrete has the greatest potential. Reported mill boiler temperatures discrepancies and the physical characteristics of the ash, highlight the importance of accurate temperature monitoring at the combustion seat if bagasse ash quality is to be prioritised to ensure a usable final ash product. Keywords: Materials Science, Civil Engineering

  9. In Vivo Osteogenic Potential of Biomimetic Hydroxyapatite/Collagen Microspheres: Comparison with Injectable Cement Pastes

    Science.gov (United States)

    Manzanares, Maria-Cristina; Ginebra, Maria-Pau; Franch, Jordi

    2015-01-01

    The osteogenic capacity of biomimetic calcium deficient hydroxyapatite microspheres with and without collagen obtained by emulsification of a calcium phosphate cement paste has been evaluated in an in vivo model, and compared with an injectable calcium phosphate cement with the same composition. The materials were implanted into a 5 mm defect in the femur condyle of rabbits, and bone formation was assessed after 1 and 3 months. The histological analysis revealed that the cements presented cellular activity only in the margins of the material, whereas each one of the individual microspheres was covered with osteogenic cells. Consequently, bone ingrowth was enhanced by the microspheres, with a tenfold increase compared to the cement, which was associated to the higher accessibility for the cells provided by the macroporous network between the microspheres, and the larger surface area available for osteoconduction. No significant differences were found in terms of bone formation associated with the presence of collagen in the materials, although a more extensive erosion of the collagen-containing microspheres was observed. PMID:26132468

  10. Mercury release from fly ashes and hydrated fly ash cement pastes

    Science.gov (United States)

    Du, Wen; Zhang, Chao-yang; Kong, Xiang-ming; Zhuo, Yu-qun; Zhu, Zhen-wu

    2018-04-01

    The large-scale usage of fly ash in cement and concrete introduces mercury (Hg) into concrete structures and a risk of secondary emission of Hg from the structures during long-term service was evaluated. Three fly ashes were collected from coal-fired power plants and three blend cements were prepared by mixing Ordinary Portland cement (OPC) with the same amount of fly ash. The releasing behaviors of Hg0 from the fly ash and the powdered hydrated cement pastes (HCP) were measured by a self-developed Hg measurement system, where an air-blowing part and Hg collection part were involved. The Hg release of fly ashes at room temperature varied from 25.84 to 39.69 ng/g fly ash during 90-days period of air-blowing experiment. In contrast, the Hg release of the HCPs were in a range of 8.51-18.48 ng/g HCP. It is found that the Hg release ratios of HCPs were almost the same as those of the pure fly ashes, suggesting that the hydration products of the HCP have little immobilization effect on Hg0. Increasing temperature and moisture content markedly promote the Hg release.

  11. In Vivo Osteogenic Potential of Biomimetic Hydroxyapatite/Collagen Microspheres: Comparison with Injectable Cement Pastes.

    Directory of Open Access Journals (Sweden)

    Erika Cuzmar

    Full Text Available The osteogenic capacity of biomimetic calcium deficient hydroxyapatite microspheres with and without collagen obtained by emulsification of a calcium phosphate cement paste has been evaluated in an in vivo model, and compared with an injectable calcium phosphate cement with the same composition. The materials were implanted into a 5 mm defect in the femur condyle of rabbits, and bone formation was assessed after 1 and 3 months. The histological analysis revealed that the cements presented cellular activity only in the margins of the material, whereas each one of the individual microspheres was covered with osteogenic cells. Consequently, bone ingrowth was enhanced by the microspheres, with a tenfold increase compared to the cement, which was associated to the higher accessibility for the cells provided by the macroporous network between the microspheres, and the larger surface area available for osteoconduction. No significant differences were found in terms of bone formation associated with the presence of collagen in the materials, although a more extensive erosion of the collagen-containing microspheres was observed.

  12. In situ 3D monitoring of corrosion on carbon steel and ferritic stainless steel embedded in cement paste

    International Nuclear Information System (INIS)

    Itty, Pierre-Adrien; Serdar, Marijana; Meral, Cagla; Parkinson, Dula; MacDowell, Alastair A.; Bjegović, Dubravka; Monteiro, Paulo J.M.

    2014-01-01

    Highlights: • The morphology of the corrosion of steel in cement paste was studied in situ. • During galvanostatic corrosion, carbon steel reinforcement corroded homogeneously. • On ferritic stainless steel, deep corrosion pits formed and caused wider cracks. • The measured rate of steel loss correlated well with Faraday’s law of electrolysis. - Abstract: In a X-ray microcomputed tomography study, active corrosion was induced by galvanostatically corroding steel embedded in cement paste. The results give insight into corrosion product build up, crack formation, leaching of products into the cracks and voids, and differences in morphology of corrosion attack in the case of carbon steel or stainless steel reinforcement. Carbon steel was homogeneously etched away with a homogeneous layer of corrosion products forming at the steel/cement paste interface. For ferritic stainless steel, pits were forming, concentrating the corrosion products locally, which led to more extensive damage on the cement paste cover

  13. Evaluation of pulp and mortar to pack bitumen radioactive waste; Avaliacao de pastas e argamassas para o embalado de rejeitos radioativos betuminizados

    Energy Technology Data Exchange (ETDEWEB)

    Gregorio, Marina da S.; Vieira, Vanessa M.; Tello, Cledola C.O., E-mail: msg@cdtn.br, E-mail: vanessamotavieira@gmail.com, E-mail: tellocc@cdtn.br [Centro de Desenvolvimento da Tecnologia Nuclear (CDTN/CNEN-MG), Belo Horizonte, MG (Brazil)

    2013-07-01

    According to international experience, for the deposition of cement in surface repository, is necessary the use of cement mortar pastes to immobilize the product. Determining the most efficient folder or for the packed mortar, as well as its ideal formulation, is the goal of this study. To do various experiments with samples of cement paste and mortar, with presence of fluxing and / or clay were performed. Viscosity, density, setting time and compressive strength were evaluated. This study will be presented only the results found in testing of compressive strength to be an essential parameter in the transport, storage and disposal of the product. From the results found will be selected the best formulations for use in packed bitumen tailings from the National Radioactive Waste Repository.

  14. The influence of calcium lignosulphonate - sodium bicarbonate on the status of ettringite crystallization in fly ash cement paste

    Energy Technology Data Exchange (ETDEWEB)

    Yang, K.; Zhang, C.; Liu, Z. [Hebei Institute of Technology, Tang Shan (China)

    2002-01-01

    Calcium lignosulphonate (CL) - sodium bicarbonate (SB) (a total of 0.7% by weight of cement and CL to SB ratio of 1:1.8) will cause the fluidity of fly ash cement paste to decrease rapidly. It is the variation of the status of ettringite crystallization that causes this phenomenon. Experimental results show that CL-SB affects the liquid-phase composition of fly ash cement paste remarkably. As a result, ettringite crystallizes out in the shape of needles from the solution. These needle-like crystal particles are distributed in the solution at a certain distance from the surface of clinker particles. At the initial hydration stage, the crystallization of ettringite is stronger in fly ash cement with calcined gypsum than in fly ash cement with gypsum. 5 refs., 10 figs., 2 tabs.

  15. Utilization of Foaming Technology in Cemented Paste Backfill of High-Mud Superfine Unclassified Tailings

    Directory of Open Access Journals (Sweden)

    Jian-wen Zhao

    2017-01-01

    Full Text Available Due to high-mud content in superfine unclassified tailings (SUT, the viscosity of cemented paste backfill (CPB is high and its pipeline transportation properties are poor. Foaming technology was introduced to prepare a new three-phase flow backfill (TFB using a foaming machine. Then the rheological parameters of TFB with different bubble ratio were measured and their pipeline transportation properties were simulated by Fluent. Besides, the simulation results were further verified by a semi-industrial loop test. The results indicate that the optimum ratio of TFB is a cement-sand ratio of 1 : 8, mass concentration of 70%, and bubble ratio of 20%. Compared with CPB, the decrease of bleeding rate, viscosity, and resistance loss of TFB is 27%, 25%, and 30%, respectively. Therefore, foaming technology is an innovative and feasible solution for high-mud CPB in reducing viscosity, decreasing resistance loss, and improving pipeline transporting efficiency.

  16. Modeling the degradation of Portland cement pastes by biogenic organic acids

    International Nuclear Information System (INIS)

    De Windt, Laurent; Devillers, Philippe

    2010-01-01

    Reactive transport models can be used to assess the long-term performance of cement-based materials subjected to biodegradation. A bioleaching test (with Aspergillus niger fungi) applied to ordinary Portland cement pastes during 15 months is modeled with HYTEC. Modeling indicates that the biogenic organic acids (acetic, butyric, lactic and oxalic) strongly accelerate hydrate dissolution by acidic hydrolysis whilst their complexation of aluminum has an effect on the secondary gel stability only. The deepest degradation front corresponds to portlandite dissolution and decalcification of calcium silicate hydrates. A complex pattern of sulfate phases dissolution and precipitation takes place in an intermediate zone. The outermost degraded zone consists of alumina and silica gels. The modeling accurateness of calcium leaching, pH evolution and degradation thickness is consistently enhanced whilst considering increase of diffusivity in the degraded zones. Precipitation of calcium oxalate is predicted by modeling but was hindered in the bioleaching reactor.

  17. Calcium Sulfoaluminate, Geopolymeric, and Cementitious Mortars for Structural Applications

    Directory of Open Access Journals (Sweden)

    Alessandra Mobili

    2017-09-01

    Full Text Available This paper deals with the study of calcium sulfoaluminate (CSA and geopolymeric (GEO binders as alternatives to ordinary Portland cement (OPC for the production of more environmentally-friendly construction materials. For this reason, three types of mortar with the same mechanical strength class (R3 ≥ 25 MPa, according to EN 1504-3 were tested and compared; they were based on CSA cement, an alkaline activated coal fly ash, and OPC. Firstly, binder pastes were prepared and their hydration was studied by means of X-ray diffraction (XRD and differential thermal-thermogravimetric (DT-TG analyses. Afterwards, mortars were compared in terms of workability, dynamic modulus of elasticity, adhesion to red clay bricks, free and restrained drying shrinkage, water vapor permeability, capillary water absorption, and resistance to sulfate attack. DT-TG and XRD analyses evidenced the main reactive phases of the investigated binders involved in the hydration reactions. Moreover, the sulfoaluminate mortar showed the smallest free shrinkage and the highest restrained shrinkage, mainly due to its high dynamic modulus of elasticity. The pore size distribution of geopolymeric mortar was responsible for the lowest capillary water absorption at short times and for the highest permeability to water vapor and the greatest resistance to sulfate attack.

  18. On the Utilization of Pozzolanic Wastes as an Alternative Resource of Cement

    Directory of Open Access Journals (Sweden)

    Md. Rezaul Karim

    2014-12-01

    Full Text Available Recently, as a supplement of cement, the utilization of pozzolanic materials in cement and concrete manufacturing has increased significantly. This study investigates the scope to use pozzolanic wastes (slag, palm oil fuel ash and rice husk ash as an alkali activated binder (AAB that can be used as an alternative to cement. To activate these materials, sodium hydroxide solution was used at 1.0, 2.5 and 5.0 molar concentration added into the mortar, separately. The required solution was used to maintain the flow of mortar at 110% ± 5%. The consistency and setting time of the AAB-paste were determined. Mortar was tested for its flow, compressive strength, porosity, water absorption and thermal resistance (heating at 700 °C and investigated by scanning electron microscopy. The experimental results reveal that AAB-mortar exhibits less flow than that of ordinary Portland cement (OPC. Surprisingly, AAB-mortars (with 2.5 molar solution achieved a compressive strength of 34.3 MPa at 28 days, while OPC shows that of 43.9 MPa under the same conditions. Although water absorption and porosity of the AAB-mortar are slightly high, it shows excellent thermal resistance compared to OPC. Therefore, based on the test results, it can be concluded that in the presence of a chemical activator, the aforementioned pozzolans can be used as an alternative material for cement.

  19. NMR relaxometry study of plaster mortar with polymer additives

    Energy Technology Data Exchange (ETDEWEB)

    Jumate, E.; Manea, D. [Technical University of Cluj-Napoca, Faculty of Civil Engineering. 15 C Daicoviciu Str., 400020, Cluj-Napoca (Romania); Moldovan, D.; Fechete, R. [Technical University of Cluj-Napoca, Department of Physics and Chemistry, 25 G. Baritiu Str., 400027, Cluj-Napoca (Romania)

    2013-11-13

    The cement mixed with water forms a plastic paste or slurry which stiffness in time and finally hardens into a resistant stone. The addition of sand aggregates, polymers (Walocel) and/or calcium carbonate will modify dramatically the final mortar mechanic and thermal properties. The hydration processes can be observed using the 1D NMR measurements of transverse T{sub 2} relaxation times distributions analysed by a Laplace inversion algorithm. These distributions were obtained for mortar pasta measured at 2 hours after preparation then at 3, 7 and 28 days after preparation. Multiple components are identified in the T{sub 2} distributions. These can be associated with the proton bounded chemical or physical to the mortar minerals characterized by a short T{sub 2} relaxation time and to water protons in pores with three different pore sizes as observed from SEM images. The evaporation process is faster in the first hours after preparation, while the mortar hydration (bonding of water molecules to mortar minerals) can be still observed after days or months from preparation. Finally, the mechanic resistance was correlated with the transverse T{sub 2} relaxation rates corresponding to the bound water.

  20. NMR relaxometry study of plaster mortar with polymer additives

    Science.gov (United States)

    Jumate, E.; Moldovan, D.; Fechete, R.; Manea, D.

    2013-11-01

    The cement mixed with water forms a plastic paste or slurry which stiffness in time and finally hardens into a resistant stone. The addition of sand aggregates, polymers (Walocel) and/or calcium carbonate will modify dramatically the final mortar mechanic and thermal properties. The hydration processes can be observed using the 1D NMR measurements of transverse T2 relaxation times distributions analysed by a Laplace inversion algorithm. These distributions were obtained for mortar pasta measured at 2 hours after preparation then at 3, 7 and 28 days after preparation. Multiple components are identified in the T2 distributions. These can be associated with the proton bounded chemical or physical to the mortar minerals characterized by a short T2 relaxation time and to water protons in pores with three different pore sizes as observed from SEM images. The evaporation process is faster in the first hours after preparation, while the mortar hydration (bonding of water molecules to mortar minerals) can be still observed after days or months from preparation. Finally, the mechanic resistance was correlated with the transverse T2 relaxation rates corresponding to the bound water.

  1. NMR relaxometry study of plaster mortar with polymer additives

    International Nuclear Information System (INIS)

    Jumate, E.; Manea, D.; Moldovan, D.; Fechete, R.

    2013-01-01

    The cement mixed with water forms a plastic paste or slurry which stiffness in time and finally hardens into a resistant stone. The addition of sand aggregates, polymers (Walocel) and/or calcium carbonate will modify dramatically the final mortar mechanic and thermal properties. The hydration processes can be observed using the 1D NMR measurements of transverse T 2 relaxation times distributions analysed by a Laplace inversion algorithm. These distributions were obtained for mortar pasta measured at 2 hours after preparation then at 3, 7 and 28 days after preparation. Multiple components are identified in the T 2 distributions. These can be associated with the proton bounded chemical or physical to the mortar minerals characterized by a short T 2 relaxation time and to water protons in pores with three different pore sizes as observed from SEM images. The evaporation process is faster in the first hours after preparation, while the mortar hydration (bonding of water molecules to mortar minerals) can be still observed after days or months from preparation. Finally, the mechanic resistance was correlated with the transverse T 2 relaxation rates corresponding to the bound water

  2. Nuclear magnetic resonance study of diffusion and relaxation in hydrating white cement pastes of different water content

    International Nuclear Information System (INIS)

    Nestle, Nikolaus; Galvosas, Petrik; Geier, Oliver; Zimmermann, Christian; Dakkouri, Marwan; Karger, Jorg

    2001-01-01

    While the nuclear spin relaxation time changes in hydrating cement materials have been widely studied by various groups during the last 20 years, data on the self-diffusion behavior of the pore water during hydration of a cement paste are much scarcer. Taking advantage of improved spectrometer hardware for pulsed field gradient diffusometry and a specialized pulse sequence which is designed to compensate the detrimental effects of inner magnetic field gradients in the sample we have studied the water self-diffusion behavior in pastes prepared from white cement at various water/cement ratios. For the same mixtures, studies of the transverse spin relaxation behavior were also conducted. A comparison of the results from both techniques shows that the diffusion coefficient starts to decrease only much later than the relaxation times for all pastes studied. [copyright] 2001 American Institute of Physics

  3. A multi-technique investigation of the nanoporosity of cement paste

    International Nuclear Information System (INIS)

    Jennings, Hamlin M.; Thomas, Jeffrey J.; Gevrenov, Julia S.; Constantinides, Georgios; Ulm, Franz-Josef

    2007-01-01

    The nanometer-scale structure of cement paste, which is dominated by the colloidal-scale porosity within the C-S-H gel phase, has a controlling effect on concrete properties but is difficult to study due to its delicate structure and lack of long-range order. Here we present results from three experimental techniques that are particularly suited to analyzing disordered nanoporous materials: small-angle neutron scattering (SANS), weight and length changes during equilibrium drying, and nanoindentation. Particular attention is paid to differences between pastes of different ages and cured at different temperatures. The SANS and equilibrium drying results indicate that hydration of cement paste at 20 deg. C forms a low-density (LD) C-S-H gel structure with a range of gel pore sizes and a relatively low packing fraction of solid particles. This fine structure may persist indefinitely under saturated conditions. However, if the paste is dried or is cured at elevated temperatures (60 deg. C or greater) the structure collapses toward a denser (less porous) and more stable configuration with fewer large gel pores, resulting in a greater amount of capillary porosity. Nanoindentation measurements of pastes cured at different temperatures demonstrate in all cases the existence of two C-S-H structures with different characteristic values of the indentation modulus. The average value of the modulus of the LD C-S-H is the same for all pastes tested to date, and a micromechanical analysis indicates that this value corresponds to the denser and more stable configuration of LD C-S-H. The experimental results presented here are interpreted in terms of a previously proposed quantitative 'colloid' model of C-S-H gel, resulting in an improved understanding of the microstructural changes associated with drying and heat curing

  4. Formation of magnesium silicate hydrate (M-S-H) cement pastes using sodium hexametaphosphate

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Tingting [Faculty of Infrastructure Engineering, Dalian University of Technology, Dalian 116024 (China); Department of Materials, Centre for Advanced Structural Ceramics, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Department of Civil and Environmental Engineering, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Vandeperre, Luc J. [Department of Materials, Centre for Advanced Structural Ceramics, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom); Cheeseman, Christopher R., E-mail: c.cheeseman@imperial.ac.uk [Department of Civil and Environmental Engineering, Imperial College London, South Kensington Campus, London SW7 2AZ (United Kingdom)

    2014-11-15

    Magnesium silicate hydrate (M-S-H) gel is formed by the reaction of brucite with amorphous silica during sulphate attack in concrete and M-S-H is therefore regarded as having limited cementing properties. The aim of this work was to form M-S-H pastes, characterise the hydration reactions and assess the resulting properties. It is shown that M-S-H pastes can be prepared by reacting magnesium oxide (MgO) and silica fume (SF) at low water to solid ratio using sodium hexametaphosphate (NaHMP) as a dispersant. Characterisation of the hydration reactions by x-ray diffraction and thermogravimetric analysis shows that brucite and M-S-H gel are formed and that for samples containing 60 wt.% SF and 40 wt.% MgO all of the brucites react with SF to form M-S-H gel. These M-S-H cement pastes were found to have compressive strengths in excess of 70 MPa.

  5. Influence of superplasticizers on the long-term properties of cement pastes and possible impact on radionuclide uptake in a cement-based repository for radioactive waste

    International Nuclear Information System (INIS)

    Wieland, E.; Lothenbach, B.; Glaus, M.A.; Thoenen, T.; Schwyn, B.

    2014-01-01

    Highlights: • We investigate the hydration of different cement mixes containing concrete admixtures. • The concentration of concrete admixtures decreases with time due to sorption on cement phases. • We observe no influence on the phase composition of cement paste and the ion composition of pore fluids. • Uptake of 63 Ni, 152 Eu and 228 Th by cement paste is not affected by the concrete admixtures. - Abstract: Cementitious materials will be used for the construction of the engineered barrier of the planned repositories for radioactive waste in Switzerland. Superplasticizers (SPs) are commonly used to improve the workability of concretes and, along with a set accelerator (Acc), to produce shotcrete. In this study the influence of a polycarboxylate- (PCE) and a polynaphthalene-sulphonate-based (PNS) SP on the hydration process, mineral composition and the sorption behaviour of metal cations has been investigated using an ordinary Portland cement (OPC), a low-alkali cement mix (LAC) consisting of CEM III-type cement and nanosilica, and a shotcrete-type cement mix (ESDRED) consisting of a CEM I-type cement and silica fume prepared in the presence of an alkali-free set accelerator. Both the PCE and PNS SP do not significantly influence the amount and quantity of hydrates formed during hydration. The concentration of both SPs decreased rapidly in the early stage of the hydration process for all cements due to sorption onto cement phases. After 28 days of hydration and longer, the concentration of the PNS SP in the pore fluids of all cements was generally lower than that of the PCE SP, indicating stronger uptake of the PNS SP. The formate present in the Acc sorbs only weakly onto the cement phases, which led to higher aqueous concentration of organics in the ESDRED cement than in OPC and LAC. Sorption experiments with 63 Ni, 152 Eu and 228 Th on a cation exchange resin indicate that, at concentrations above 0.1 g L −1 , the two SPs could reduce sorption of metal

  6. Microwave detection of delaminations between fiber reinforced polymer (FRP) composite and hardened cement paste

    Science.gov (United States)

    Hughes, D.; Kazemi, M.; Marler, K.; Zoughi, R.; Myers, J.; Nanni, A.

    2002-05-01

    Fiber reinforced polymer (FRP) composites are increasingly being used for the rehabilitation of concrete structures. Detection and characterization of delaminations between an FRP composite and a concrete surface are of paramount importance. Consequently, the development of a one sided, non-contact, real time and rapid nondestructive testing (NDT) technique for this purpose is of great interest. Near-field microwave NDT techniques, using open-ended rectangular waveguide probes, have shown great potential for detecting delaminations in layered composite structures such as these. The results of some theoretical and experimental investigations on a specially prepared cement paste specimen are presented here.

  7. Application of experimental plans method to formulate a self compacting cement paste

    Directory of Open Access Journals (Sweden)

    Mebrouki, A.

    2010-06-01

    Full Text Available The self-compacting concrete formulation means to elaborate a self-compacting cement paste to which will be injected aggregates. The purpose of this work is to find the composition of this cement paste containing local materials (pozzolanic cement, limestone fillers, superplasticizer and water having self-compacting properties. The use of the experimental plans method shows that it is possible to delimit an experimental field bounded by the volumetric proportions of materials composing the paste. The field was transformed in equations form conditioned by implicit constraints, defining zones of minimal shearing threshold and maximum viscosity; numerical resolution submitted to the optimization criteria permitted to define the volumetric proportions of each mixing parameter contributing to the preparation of an optimal paste. After experimental checking to validate obtained results, conclusions are that, from results given by ternary diagrams and desirability’s functions, a composition of an optimal self-compacting cement pas was obtained.

    En este trabajo se estudia la constitución de una pasta autocompactante a base de materiales locales argelinos (cemento binario de base puzolánica natural de Beni Saf y filler calizo de cantera. La reología de la pasta se estudia en función de las dosificaciones de cemento, caliza, superplastificante y agua. La fluidez de las pastas así formadas se deducen de los ensayos de escurrimiento del mini cono y del tiempo de flujo en el cono de Marsh. Utilizando el diseño estadístico de mezclas, el número de ensayos se ha visto considerablemente reducido, el problema se transformó en ecuaciones y después se resolvió numéricamente. A partir de las curvas de los diagramas ternarios, uniendo las respuestas de escurrimiento y el tiempo de flujo de las pastas en función de las dosificaciones en constituyentes y estudiando las funciones de conveniencia para cada respuesta, se terminará por deducir una

  8. Evaluation method of radiation stability of hardened cement paste with chemical additives

    Energy Technology Data Exchange (ETDEWEB)

    Medvedev, Vyacheslav; Pustovgar, Andrey [National Research Univ. ' Moscow State Univ. of Civil Engineering' (MSUCE), Moscow (Russian Federation); National Research Univ. ' Moscow State Univ. of Civil Engineering' (MSUCE), Moscow (Russian Federation). Scientific Research Inst. of Constructional Materials and Technologies; Denisov, Alexander; Soloviev, Vitaly [National Research Univ. ' Moscow State Univ. of Civil Engineering' (MSUCE), Moscow (Russian Federation)

    2013-07-01

    The influence of additives on the radiation resistance of the concrete will occur through the influence of radiation changes of hardened cement paste on radiation changes of concrete and can be quite significant. The test sequence was produced according to the modified method. The samples were prepared in the form of prisms with the following dimensions: 10 mm x 10 mm, 30 mm long. Measurement series were produced after each heating and cooling sequence. Then the difference between the values before and after heating was calculated. (orig.)

  9. Effect of AlF3 Production Waste on the Properties of Hardened Cement Paste

    Directory of Open Access Journals (Sweden)

    Danutė VAIČIUKYNIENĖ

    2012-06-01

    Full Text Available The possibility to use by-product SiO2·nH2O (often called AlF3 production waste in cement casting has been attracting the interest of researchers for many years, although high content of fluorine makes the use of amorphous SiO2 problematic. Finding the way of utilizing waste products is a very important research topic at the moment. In this study AlF3 production waste was investigated as the basic ingredient of a new pozzolanic material. The goal of this study is to investigate the possibilities of using AlF3 production waste, washed in ammonia solution, in cement stone specimens. Chemically treated silica gel additive was proved to reduce the amount of Ca(OH2 and CaCO3 in hardened cement paste samples. Experimental research has revealed that the density in hydrated samples reduces from 2220 kg/m3 to 2030 kg/m3 with the increase of silica gel content from 0 % to 35 %. The compressive strength of samples containing 10 % of silica gel additive increased by 8.04 % compared to the samples without the additive. SiO2 additive used at 10 % and 20 % increased the maximum hydration temperature. In this case, the additive modifies the hydration kinetics.DOI: http://dx.doi.org/10.5755/j01.ms.18.2.1925

  10. Assessment of hydration process and mechanical properties of cemented paste backfill by electrical resistivity measurement

    Science.gov (United States)

    Xu, Wenbin; Tian, Xichun; Cao, Peiwang

    2018-04-01

    Cemented paste backfill (CPB) is an emerging mine backfill technique that allows environmentally hazardous tailings to return to the underground openings or stopes, thereby maximising the safety, efficiency and productivity of operation. Uniaxial compressive strength (UCS) is one of the most commonly used parameters for evaluating the mechanical performance of CPB; the prediction of the UCS of CPB structures from early to advanced ages is of great practical importance. This study aims to investigate the predictability of the UCS of CPB during the hydration process based on electrical resistivity (ER) measurement. For this purpose, the samples prepared at different cement-to-tailing ratios and solid contents were subjected to the ER test during the whole hydration process and UCS tests at 3, 7, 28 days of curing periods. The effect of cement-to-tailing ratio and solid content on the ER and UCS of CPB samples was obtained; the UCS values were correlated with the corresponding ER data. Microstructural analysis was also performed on CPB samples to understand the effect of microstructure on the ER data. The result shows that the ER of CPB decreases first and then increases with the speed which is faster in the previous part than the latter. The ER and UCS of CPB samples increased with increasing cement-to-tailing ratio and solid content and curing periods. A logarithmic relationship is established for each mixture in order to predict the UCS of CPB based on ER. Scanning electron microscope analyses have revealed that the microstructure of the CPB changes with the age from the initial floc to honeycomb, and eventually to the compact clumps. The ER properties of CPB samples were highly associated with their respective microstructural properties. The major output of this study is that ER test is effectively capable for a preliminary prediction of the UCS of CPB.

  11. Development of methodology for evaluation of long-term safety aspects of organic cement paste components

    International Nuclear Information System (INIS)

    Andersson, M.; Holgersson, S.; Ervanne, H.

    2008-12-01

    Long-term safety aspects of superplasticizers (SP) and other cement paste components were studied in this joint Nagra - NUMO - SKB - Posiva project with aim to develop a methodology for the evaluation of the long-term safety aspects of superplasticizers (SP) and other organic components of cement pastes. The study also evaluated the effects of SPs and other cement paste components that have already been used or that are most likely to be used in the construction of the high-level nuclear waste repositories in Sweden, Switzerland, Finland and Japan. The main long-term safety issue of concern is whether the superplasticizers and/or other organic components of cement pastes might affect the transport properties of radionuclides. A full evaluation of whether the superplasticizers can be used in a high-level nuclear waste repository cannot be answered based on the studies but a classification of the superplasticizers based on their impact on sorption of radionuclides has been done. The basic methodology for testing, leaching and analyzing of leachants and solid samples of different types was developed at CRIEPI. Two different methodologies for studying the impact of SPs on the sorption of Eu on crushed rock were tested and developed by Helsinki University (HU) and Chalmers University of Technology (CTH). Methods for analyzing organics leaching from grouts were successfully tested by CRIEPI and CTH (Chalmers University of Technology). At CRIEPI the total organic content (TOC) of the leachants was analyzed by Infrared absorption spectrometry (IR) followed by Gel Permeation Chromatography (GPC) for the identification of the organic compounds. At CTH several different analytical methods were tested (e.g. IR, UV spectroscopy, NMR, MALDI-TOF), but these methods still require improvement. In addition to SPs, organics are present in several components of cement pastes, for example in cement grinding aid (CGA) and micro silica slurry. The results suggests that the main high

  12. Diffusion of He in OPC paste and low-heat Portland cement paste containing fly-ash in contact with aqueous phase

    International Nuclear Information System (INIS)

    Sato, Fuminori; Miwata, Chikanori; Noda, Natsuko; Sato, Seichi; Kozaki, Tamotsu; Higashihara, Tomohiro; Hironaga, Michihiko; Kawanishi, Motoi

    2008-01-01

    As a part of gas migration studies in concrete package for nuclear waste surrounded by water-saturated rock, the helium diffusion in ordinary Portland cement paste (OPC) was studied using disk form specimen at various water-to-cement (w/c) ratios. The helium diffusion in low-heat Portland cement paste containing fly-ash (LPF) was also studied. Apparent diffusion coefficients of helium in OPC paste were ∼1 x 10 -10 m 2 s -1 at 0.4 w/c ratio, independent of increase of w/c ratio. It is likely that the materials formation such as C-S-H and CH in capillary pores in OPC plays an important role on the helium diffusion rather than porosity increase. Apparent diffusion coefficient of helium in LPF was two orders of magnitude smaller than that in OPC. It is quite possible that the addition of fly-ash contributes to the formation of hydration products which markedly enhance discontinuity of capillary pore. The results of the present study on the two kinds of cement pastes give us valuable information about alternatives to release gas from cement package. (author)

  13. Effect of sodium monofluorophosphate treatment on microstructure and frost salt scaling durability of slag cement paste

    International Nuclear Information System (INIS)

    Copuroglu, O.; Fraaij, A.L.A.; Bijen, J.M.J.M.

    2006-01-01

    Sodium-monofluorophosphate (Na-MFP) is currently in use as a surface applied corrosion inhibitor in the concrete industry. Its basic mechanism is to protect the passive layer of the reinforcement steel against disruption due to carbonation. Carbonation is known as the most detrimental environmental effect on blast furnace slag cement (BFSC) concrete with respect to frost salt scaling. In this paper the effect of Na-MFP on the microstructure and frost salt scaling resistance of carbonated BFSC paste is presented. The results of electron microscopy, mercury intrusion porosimetry (MIP) and X-ray diffraction (XRD) are discussed. It is found that the treatment modifies the microstructure and improves the resistance of carbonated BFSC paste against frost salt attack

  14. A comparative study of the pore structures and surfaces of hardened cement pastes of potential use in radioactive waste repositories

    International Nuclear Information System (INIS)

    Rowan, S.M.; Donaldson, L.; White, S.

    1988-02-01

    Measurements of water vapour adsorption at 20 0 C and mercury intrusion have been used to compare the surfaces and pore structures of hardened cement pastes made from ordinary portland cement (OPC) and the additives blast furnace slag (BFS) and pulverised fuel ash (PFA). The results suggest that each additive, after taking part in the hydration reaction with OPC, produces a paste whose gel pore structure is similar to that derived from OPC alone. The BET adsorption surface area of the cement pastes, in the form of half inch diameter coupons was ca. 55 m 2 g -1 and was not influenced by the presence of the additives. However the pastes containing the additives have a larger and better interconnected meso and macropore structure than OPC which may account for larger diffusion coefficients reported elsewhere for caesium ions passing through concrete containing BFS in comparison with a concrete containing OPC alone. (author)

  15. Influence of triethanolamine on the hydration product of portlandite in cement paste and the mechanism

    International Nuclear Information System (INIS)

    Yan-Rong, Zhang; Xiang-Ming, Kong; Zi-Chen, Lu; Zhen-Bao, Lu; Qing, Zhang; Bi-Qin, Dong; Feng, Xing

    2016-01-01

    The influences of triethanolamine (TEA) on the portlandite in hardened cement pastes (HCPs) were systematically investigated. Results show that the addition of TEA in cement pastes leads to a visible reduction of Ca(OH) 2 (CH) content and considerably alters the morphology of CH crystals from large and parallel-stacked lamellar shape to smaller and distorted actinomorphic one. For the first time, the CH micro-crystals and even non-crystalline CH in HCPs were observed in the presence of TEA. Due to integration of CH micro-crystals in C–S–H phase, remarkable higher Ca/Si ratio of C–S–H phase was found. The formation of TEA-Ca 2+ complex via the interaction between Ca 2+ and the oxygen atoms in TEA molecule was evidenced by the results of NMR and UV. It is believed that TEA can be introduced into the crystallization process of portlandite and thus significantly alters the morphology of CH crystals and even the content of the crystalline CH phase.

  16. Autogenous shrinkage in high-performance cement paste: An evaluation of basic mechanisms

    International Nuclear Information System (INIS)

    Lura, Pietro; Jensen, Ole Mejlhede; Breugel, Klaas van

    2003-01-01

    In this paper, various mechanisms suggested to cause autogenous shrinkage are presented. The mechanisms are evaluated from the point of view of their soundness and applicability to quantitative modeling of autogenous shrinkage. The capillary tension approach is advantageous, because it has a sound mechanical and thermodynamical basis. Furthermore, this mechanism is easily applicable in a numerical model when dealing with a continuously changing microstructure. In order to test the numerical model, autogenous deformation and internal relative humidity (RH) of a Portland cement paste were measured during the first week of hardening. The isothermal heat evolution was also recorded to monitor the progress of hydration and the elastic modulus in compression was measured. RH change, degree of hydration and elastic modulus were used as input data for the calculation of autogenous deformation based on the capillary tension approach. Because a part of the RH drop in the cement paste is due to dissolved salts in the pore solution, a method is suggested to separate this effect from self-desiccation and to calculate the actual stress in the pore fluid associated with menisci formation

  17. Cemented Backfilling Technology of Paste-Like Based on Aeolian Sand and Tailings

    Directory of Open Access Journals (Sweden)

    Qinli Zhang

    2016-12-01

    Full Text Available Aeolian sand, tailings, and #32.5 Portland cement were used to produce backfilling aggregate, and physicochemical evaluations and proportioning tests were conducted. It is revealed that a mixture of aeolian sand and tailings can be used as a backfilling aggregate for the complementarities of their physicochemical properties; e.g., high Al2O3 content in the aeolian sand and CaO content in the tailings, coarse particles of aeolian sand and fine particles of tailings, etc. In addition, the optimal backfilling aggregate was shown to have a mass fraction of 72%–74%, a cement–sand ratio of 1:8, and an aeolian sand proportion of 25%. Furthermore, viscometer tests were used to analyze the rheological characteristics, and the slurry in these optimized proportions exhibited shear thinning phenomena with an initial yield stress, which belongs to paste-like—a cemented backfilling slurry with a higher mass fraction than a two-phase flow and better flowability than a paste slurry. Finally, the application of this backfilling technology shows that it can not only realize safe mining, but also bring huge economic benefits, and has some constructive guidance for environmental protection.

  18. Detecting the Water-soluble Chloride Distribution of Cement Paste in a High-precision Way.

    Science.gov (United States)

    Chang, Honglei; Mu, Song

    2017-11-21

    To improve the accuracy of the chloride distribution along the depth of cement paste under cyclic wet-dry conditions, a new method is proposed to obtain a high-precision chloride profile. Firstly, paste specimens are molded, cured, and exposed to cyclic wet-dry conditions. Then, powder samples at different specimen depths are grinded when the exposure age is reached. Finally, the water-soluble chloride content is detected using a silver nitrate titration method, and chloride profiles are plotted. The key to improving the accuracy of the chloride distribution along the depth is to exclude the error in the powderization, which is the most critical step for testing the distribution of chloride. Based on the above concept, the grinding method in this protocol can be used to grind powder samples automatically layer by layer from the surface inward, and it should be noted that a very thin grinding thickness (less than 0.5 mm) with a minimum error less than 0.04 mm can be obtained. The chloride profile obtained by this method better reflects the chloride distribution in specimens, which helps researchers to capture the distribution features that are often overlooked. Furthermore, this method can be applied to studies in the field of cement-based materials, which require high chloride distribution accuracy.

  19. The impact of sulphate and magnesium on chloride binding in Portland cement paste

    Energy Technology Data Exchange (ETDEWEB)

    De Weerdt, K., E-mail: klaartje.d.weerdt@ntnu.no [Department of Structural Engineering, Norwegian University of science and Technology, Trondheim (Norway); SINTEF Building and Infrastructure, Trondheim (Norway); Orsáková, D. [Department of Civil Engineering, Technical University of Brno, Brno (Czech Republic); Geiker, M.R. [Department of Structural Engineering, Norwegian University of science and Technology, Trondheim (Norway)

    2014-11-15

    The effect of magnesium and sulphate present in sea water on chloride binding in Portland cement paste was investigated. Ground well hydrated cement paste was exposed to MgCl{sub 2}, NaCl, NaCl + MgCl{sub 2}, MgSO{sub 4} + MgCl{sub 2} and artificial sea water solutions with a range of concentrations at 20 °C. Chloride binding isotherms are determined and pH of the solutions were measured. A selection of samples was examined by SEM-EDS to identify phase changes upon exposure. The experimental data were compared with calculations of a thermodynamic model. Chloride binding from sea water was similar to chloride binding for NaCl solutions. The magnesium content in the sea water lead to a slight decrease in pH, but this did not result in a notable increase in chloride binding. The sulphate present in sea water reduces both chloride binding in C–S–H and AFm phases, as the C–S–H incorporates more sulphates instead of chlorides, and part of the AFm phases converts to ettringite.

  20. Influence of Microencapsulated Phase Change Material (PCM) Addition on (Micro) Mechanical Properties of Cement Paste

    Science.gov (United States)

    Schlangen, Erik

    2017-01-01

    Excessive cracking can be a serious durability problem for reinforced concrete structures. In recent years, addition of microencapsulated phase change materials (PCMs) to concrete has been proposed as a possible solution to crack formation related to temperature gradients. However, the addition of PCM microcapsules to cementitious materials can have some drawbacks, mainly related to strength reduction. In this work, a range of experimental techniques has been used to characterize the microcapsules and their effect on properties of composite cement pastes. On the capsule level, it was shown that they are spherical, enabling good distribution in the material during the mixing process. Force needed to break the microcapsules was shown to depend on the capsule diameter and the temperature, i.e., whether it is below or above the phase change temperature. On the cement paste level, a marked drop of compressive strength with increasing PCM inclusion level was observed. The indentation modulus has also shown to decrease, probably due to the capsules themselves, and to a lesser extent due to changes in porosity caused by their inclusion. Finally, a novel micro-cube splitting technique was used to characterize the tensile strength of the material on the micro-meter length scale. It was shown that the strength decreases with increasing PCM inclusion percentage, but this is accompanied by a decrease in measurement variability. This study will contribute to future developments of cementitious composites incorporating phase change materials for a variety of applications. PMID:28773225

  1. Evaluation of dynamic elasticity module in samples of Portland (type 1) cement paste exposed to neutronic irradiation

    International Nuclear Information System (INIS)

    Rosa Junior, A.A.; Lucki, G.

    1986-01-01

    The fast neutron radiation effects and temperature on Portland cement are studied. The Dynamic Elasticity Module (Ed) in samples of Portland cement paste was evaluated. Ultrassonic technics were applied (resonance frequency and pulse velocity). The samples were irradiated with fast neutrons to fluence of 7,2 x 10 18 n/cm 2 (E approx. 1 MeV), at temperature of 120 + - 5 0 C, due to gamma heating. This temperature was simulated in laboratory in a microwave oven. (Author) [pt

  2. Solid state NMR and LVSEM studies on the hardening of latex modified tile mortar systems

    International Nuclear Information System (INIS)

    Rottstegge, J.; Arnold, M.; Herschke, L.; Glasser, G.; Wilhelm, M.; Spiess, H.W.; Hergeth, W.D.

    2005-01-01

    Construction mortars contain a broad variety of both inorganic and organic additives beside the cement powder. Here we present a study of tile mortar systems based on portland cement, quartz, methyl cellulose and different latex additives. As known, the methyl cellulose stabilizes the freshly prepared cement paste, the latex additive enhances final hydrophobicity, flexibility and adhesion. Measurements were performed by solid state nuclear magnetic resonance (NMR) and low voltage scanning electron microscopy (LVSEM) to probe the influence of the latex additives on the hydration, hardening and the final tile mortar properties. While solid state NMR enables monitoring of the bulk composition, scanning electron microscopy affords visualization of particles and textures with respect to their shape and the distribution of the different phases. Within the alkaline cement paste, the poly(vinyl acetate) (VAc)-based latex dispersions stabilized by poly(vinyl alcohol) (PVA) were found to be relatively stable against hydrolysis. The influence of the combined organic additives methyl cellulose, poly(vinyl alcohol) and latexes stabilized by poly(vinyl alcohol) on the final silicate structure of the cement hydration products is small. But even small amounts of additives result in an increased ratio of ettringite to monosulfate within the final hydrated tile mortar as monitored by 27 Al NMR. The latex was found to be adsorbed to the inorganic surfaces, acting as glue to the inorganic components. For similar latex water interfaces built up by poly(vinyl alcohol), a variation in the latex polymer composition results in modified organic textures. In addition to the networks of the inorganic cement and of the latex, there is a weak network build up by thin polymer fibers, most probably originating from poly(vinyl alcohol). Besides the weak network, polymer fibers form well-ordered textures covering inorganic crystals such as portlandite

  3. Macroscopic and spectroscopic investigations on the immobilization of radionuclides by hardened cement paste

    International Nuclear Information System (INIS)

    Wieland, E.; Bonhoure, I.; Tits, J.; Scheidegger, A.M.; Bradbury, M.H.

    2002-01-01

    The uptake of safety-relevant radionuclides was studied using a combination of macroscopic (wet chemistry) and spectroscopic (X-ray absorption fine structure (XAFS) spectroscopy) techniques with the aim of gaining a mechanistic understanding of the uptake processes on hardened cement paste (HCP) and deducing robust sets of sorption values. HCP contains impurities of metal cations in the ppb to ppm concentration range. As a consequence, the inventories of stable isotopes are expected to be significant in a cementitious near-field and may even exceed the radionuclide inventories of the waste matrix for many safety-relevant radioelements. In view of the significant inventories of stable isotopes, it is suggested that isotopic exchange - replacement of stable isotopes by their radioactive counterparts in the cement matrix - is an important immobilisation process in HCP. However, it is not a priori known what proportion of each elemental inventory is available for isotopic exchange. Wet chemistry studies with Cs and Sr show that the total inventory of these elements is reversibly bound and that their partitioning between HCP and pore water can be modelled using the distribution values deduced from studies of the corresponding tracers ( 137 Cs and 85 Sr). This finding corroborates the relevance of isotopic exchange in cementitious systems. Wet chemistry investigations need to be complemented by spectroscopic techniques, e.g., XAFS, in order to gain a mechanistic understanding of the chemical processes by which waste ions become immobilised in cement-based matrices. XAFS can be used to obtain information at the atomic/molecular level, i.e., the type, number and distance of neighbouring atoms. XAFS studies on cementitious systems are still rather rare, and therefore information on the potential and limitations of this technique is sparse. Mechanistic aspects of the immobilisation processes are discussed for some safety-relevant radionuclides (e.g. Ni and Sr) using the

  4. Usability of cement paste containing carbon nanofibres as an anode in electrochemical chloride extraction from concrete

    Directory of Open Access Journals (Sweden)

    Moral, B. del

    2013-03-01

    Full Text Available In the application of the electrochemical chloride extraction (ECE technique, traditionally, the Ti-RuO2 wire netting has been used as the external anode. This article provides the results of the research based on the use of conductive cement paste with addition of carbon nanofibers (CNF as anodes and its application in ECE. The tests were developed in concrete specimens previously contaminated with chloride. The efficiencies achieved were compared with those obtained using a traditional anode (Ti-RuO2 and cement pastes with the addition of other carbonaceous materials. The results show the feasibility of using conductive cement paste with CNF as the anode in the electrochemical extraction of chlorides in concrete, finding similar efficiencies to those obtained with traditional Ti-RuO2 wire netting but with the added advantage that it can be adapted to complex structural geometries as it can be applied as a paste.

    En la aplicación de la técnica de extracción electroquímica de cloruros (EEC, tradicionalmente se ha venido empleando como ánodo externo una malla de Ti-RuO2. En este artículo se aportan los resultados de investigaciones basadas en la utilización de ánodos formados por pasta de cemento conductora con adición de nanofibras de carbono (NFC y su aplicación en EEC. Las experiencias se desarrollaron en probetas de hormigón contaminado previamente con cloruro. Las eficiencias alcanzadas se compararon con las obtenidas empleando un ánodo tradicional (Ti-RuO2 así como pastas de cemento con adición de otros materiales carbonosos. Los resultados muestran la viabilidad en la utilización de la pasta de cemento conductora con NFC como ánodo en la aplicación en EEC en hormigón, encontrándose eficiencias similares a las obtenidas con la tradicional malla de Ti-RuO2 pero teniendo la ventaja añadida sobre ésta de que es posible adaptarla a geometrías estructurales complejas al ser aplicada en forma de pasta.

  5. Effect of MXene (Nano-Ti3C2 on Early-Age Hydration of Cement Paste

    Directory of Open Access Journals (Sweden)

    Haibin Yin

    2015-01-01

    Full Text Available As a new two-dimensional material, MXene (nano-Ti3C2 has been widely applied in many fields, especially for reinforced composite materials. In this paper, mechanical testing, X-ray diffraction (XRD, hydration heat, scanning electron microscope (SEM, and EDS analysis were used to analyze the impact of MXene on cement hydration properties. The obtained results revealed that (a MXene could greatly improve the early compressive strength of cement paste with 0.04 wt% concentration, (b the phase type of early-age hydration products has not been changed after the addition of MXene, (c hydration exothermic rate within 72 h has small difference at different amount of MXene, and (d morphologies of hydration products were varied with the dosage of MXene, a lot of tufted ettringites appeared in 3 d hydration products when the content of MXene was 0.04 wt%, which will have a positive effect on improving the early mechanical properties of cement paste. MXene has inhibited the Portland cement hydration process; the main role of MXene in the cement hydration process is to promote the messy ettringite becoming regular distribution at a node and form network connection structure in the crystals growth process, making the mechanics performance of cement paste significantly improved.

  6. Sorption kinetics of superabsorbent polymers (SAPs) in fresh Portland cement-based pastes visualized and quantified by neutron radiography and correlated to the progress of cement hydration

    Energy Technology Data Exchange (ETDEWEB)

    Schroefl, Christof, E-mail: christof.schroefl@tu-dresden.de [Technische Universität Dresden, Fakultät Bauingenieurwesen, Institut für Baustoffe, DE-01062 Dresden (Germany); Mechtcherine, Viktor [Technische Universität Dresden, Fakultät Bauingenieurwesen, Institut für Baustoffe, DE-01062 Dresden (Germany); Vontobel, Peter; Hovind, Jan; Lehmann, Eberhard [Paul Scherrer Institut, Laboratory for Neutron Scattering and Imaging, CH-5232 Villigen/AG (Switzerland)

    2015-09-15

    Water sorption of two superabsorbent polymers in cement-based pastes has been characterized by neutron radiography. Cement pastes with W/C of 0.25 and 0.50 and one additionally containing silica fume (W/C = 0.42) were investigated. The SAPs differed in their inherent sorption kinetics in extracted cement pore solution (SAP 1: self-releasing; SAP 2: retentive). Desorption from SAP 1 started very early after paste preparation. Hence, its individual non-retentiveness governs its behavior only. SAP 2 released water into all matrices, but its kinetics were different. In the paste with the highest W/C, some moderate water release was recorded from the beginning. In the other two pastes, SAP 2 retained its stored liquid during the dormant period, i.e., up to the percolation threshold. Intense desorption then set in and continued throughout the acceleration period. These findings explain the pronouncedly higher efficiency of SAP 2 as internal curing admixture as compared to SAP 1.

  7. Sorption kinetics of superabsorbent polymers (SAPs) in fresh Portland cement-based pastes visualized and quantified by neutron radiography and correlated to the progress of cement hydration

    International Nuclear Information System (INIS)

    Schroefl, Christof; Mechtcherine, Viktor; Vontobel, Peter; Hovind, Jan; Lehmann, Eberhard

    2015-01-01

    Water sorption of two superabsorbent polymers in cement-based pastes has been characterized by neutron radiography. Cement pastes with W/C of 0.25 and 0.50 and one additionally containing silica fume (W/C = 0.42) were investigated. The SAPs differed in their inherent sorption kinetics in extracted cement pore solution (SAP 1: self-releasing; SAP 2: retentive). Desorption from SAP 1 started very early after paste preparation. Hence, its individual non-retentiveness governs its behavior only. SAP 2 released water into all matrices, but its kinetics were different. In the paste with the highest W/C, some moderate water release was recorded from the beginning. In the other two pastes, SAP 2 retained its stored liquid during the dormant period, i.e., up to the percolation threshold. Intense desorption then set in and continued throughout the acceleration period. These findings explain the pronouncedly higher efficiency of SAP 2 as internal curing admixture as compared to SAP 1

  8. Carbonation around near aggregate regions of old hardened concrete cement paste

    International Nuclear Information System (INIS)

    Tam, Vivian W.Y.; Gao, X.F.; Tam, C.M.

    2005-01-01

    Analogous with most modern cities, waste disposal is a pressing issue due to limited landfill and public filling (land reclamation) areas in Hong Kong in which construction and demolition (C and D) waste forms the major source. Concrete, apportioning the largest portion of C and D waste, has the greatest potential for recycling. However, the knowledge on micro-structural behavior of concrete waste is immature to give adequate details on the macro-behavior of concrete waste. This paper attempts to examine the problems of recycling old concrete by investigating the microstructure and phase transformation of the concrete samples collected from buildings with 46 and 37 years of services. From the results of Fourier transform infrared spectroscopy (FT-IR) and scanning electron microscopy (SEM) examination, it is found that there are a lot of pores at the near layers of aggregate where carbonation of the hardened cement paste (HCP) is high. The pores may be generated as a result of poor workmanship such as insufficient concrete mixing time, trapping of air voids beneath coarse aggregate, inappropriate water to cement ratio, and the microclimate conditions such as humidity that affects the demand on water from the aggregate during mixing

  9. Effects of calcium leaching on diffusion properties of hardened and altered cement pastes

    Science.gov (United States)

    Kurumisawa, Kiyofumi; Haga, Kazuko; Hayashi, Daisuke; Owada, Hitoshi

    2017-06-01

    It is very important to predict alterations in the concrete used for fabricating disposal containers for radioactive waste. Therefore, it is necessary to understand the alteration of cementitious materials caused by calcium leaching when they are in contact with ground water in the long term. To evaluate the long-term transport characteristics of cementitious materials, the microstructural behavior of these materials should be considered. However, many predictive models of transport characteristics focus on the pore structure, while only few such models consider both, the spatial distribution of calcium silicate hydrate (C-S-H), portlandite, and the pore spaces. This study focused on the spatial distribution of these cement phases. The auto-correlation function of each phase of cementitious materials was calculated from two-dimensional backscattered electron imaging, and the three-dimensional spatial image of the cementitious material was produced using these auto-correlation functions. An attempt was made to estimate the diffusion coefficient of chloride from the three-dimensional spatial image. The estimated diffusion coefficient of the altered sample from the three-dimensional spatial image was found to be comparable to the measured value. This demonstrated that it is possible to predict the diffusion coefficient of the altered cement paste by using the proposed model.

  10. Viability Study of a Safe Method for Health to Prepare Cement Pastes with Simultaneous Nanometric Functional Additions

    Directory of Open Access Journals (Sweden)

    M. A. de la Rubia

    2018-01-01

    Full Text Available The use of a mixing method based on a novel dry dispersion procedure that enables a proper mixing of simultaneous nanometric functional additions while avoiding the health risks derived from the exposure to nanoparticles is reported and compared with a common manual mixing in this work. Such a dry dispersion method allows a greater workability by avoiding problems associated with the dispersion of the particles. The two mixing methods have been used to prepare Portland cement CEM I 52.5R pastes with additions of nano-ZnO with bactericide properties and micro- or nanopozzolanic SiO2. The hydration process performed by both mixing methods is compared in order to determine the efficiency of using the method. The hydration analysis of these cement pastes is carried out at different ages (from one to twenty-eight days by means of differential thermal analysis and thermogravimetry (DTA-TG, X-ray diffraction (XRD, scanning electron microscopy (SEM, and Fourier transform infrared spectroscopy (FTIR analyses. Regardless of composition, all the mixtures of cement pastes obtained by the novel dispersion method showed a higher retardation of cement hydration at intermediate ages which did not occur at higher ages. In agreement with the resulting hydration behaviour, the use of this new dispersion method makes it possible to prepare homogeneous cement pastes with simultaneous functional nanoparticles which are physically supported on the larger particles of cement, avoiding exposure to the nanoparticles and therefore minimizing health risks. Manual mixing of cement-based materials with simultaneous nanometric functional nanoparticles on a large scale would make it difficult to obtain a homogenous material together with the health risks derived from the handling of nanoparticles.

  11. The influence of superabsorbent polymers on the autogenous shrinkage properties of cement pastes with supplementary cementitious materials

    DEFF Research Database (Denmark)

    Snoeck, D.; Jensen, Ole Mejlhede; De Belie, N.

    2015-01-01

    Fly ash and blast-furnace slag containing binders are frequently used in the construction industry and it is important to know the extent of autogenous shrinkage and its (ideal) mitigation by superabsorbent polymers in these systems as a function of their age. In this paper, the autogenous...... shrinkage was determined by manual and automated shrinkage measurements. Autogenous shrinkage was reduced in cement pastes with the supplementary cementitious materials versus Portland cement pastes. At later ages, the rate of autogenous shrinkage is higher due to the pozzolanic activity. Internal curing...

  12. Observation of the failure mechanism of brick masonry doublets with cement and lime mortars by microfocus X-ray computed tomography

    OpenAIRE

    Hendrickx, Roel; Bruyninckx, Katrien; Schueremans, Luc; Kerckhofs, Greet; Verstrynge, Els; Wevers, Martine; Van Balen, Koenraad

    2010-01-01

    The nature of the failure mechanism of masonry under compression depends on the properties of the brick and mortar. It is well-known that the ratio of stiffness of both materials has an important effect. Furthermore the pattern of crack development and propagation and the occurrence of local compaction of soft mortars have been the subject of some study, but remained difficult to observe. This study aims at the visualisation of these phenomena by using a hydraulic press inside a microfocus X-...

  13. Prediction of water vapour sorption isotherms and microstructure of hardened Portland cement pastes

    International Nuclear Information System (INIS)

    Burgh, James M. de; Foster, Stephen J.; Valipour, Hamid R.

    2016-01-01

    Water vapour sorption isotherms of cementitious materials reflect the multi-scale physical microstructure through its interaction with moisture. Our ability to understand and predict adsorption and desorption behaviour is essential in the application of modern performance-based approaches to durability analysis, along with many other areas of hygro-mechanical and hygro-chemo-mechanical behaviour. In this paper, a new physically based model for predicting water vapour sorption isotherms of arbitrary hardened Portland cement pastes is presented. Established thermodynamic principles, applied to a microstructure model that develops with hydration, provide a rational basis for predictions. Closed-form differentiable equations, along with a rational consideration of hysteresis and scanning phenomena, makes the model suitable for use in numerical moisture simulations. The microstructure model is reconciled with recently published 1 H NMR and mercury intrusion porosimetry results.

  14. Microstructural and bulk property changes in hardened cement paste during the first drying process

    Energy Technology Data Exchange (ETDEWEB)

    Maruyama, Ippei, E-mail: ippei@dali.nuac.nagoya-u.ac.jp [Graduate School of Environmental Studies, Nagoya University, ES Building, No. 546, Furo-cho, Chikusa-ku, Nagoya 464–8603 (Japan); Nishioka, Yukiko; Igarashi, Go [Graduate School of Environmental Studies, Nagoya University, ES Building, No. 539, Furo-cho, Chikusa-ku, Nagoya 464–8603 (Japan); Matsui, Kunio [Products and Marketing Development Dept. Asahi-KASEI Construction Materials Corporation, 106 Someya, Sakai-machi, Sashima-gun, Ibaraki, 306–0493 (Japan)

    2014-04-01

    This paper reports the microstructural changes and resultant bulk physical property changes in hardened cement paste (hcp) during the first desorption process. The microstructural changes and solid-phase changes were evaluated by water vapor sorption, nitrogen sorption, ultrasonic velocity, and {sup 29}Si and {sup 27}Al nuclear magnetic resonance. Strength, Young's modulus, and drying shrinkage were also examined. The first drying process increased the volume of macropores and decreased the volume of mesopores and interlayer spaces. Furthermore, in the first drying process globule clusters were interconnected. During the first desorption, the strength increased for samples cured at 100% to 90% RH, decreased for 90% to 40% RH, and increased again for 40% to 11% RH. This behavior is explained by both microstructural changes in hcp and C–S–H globule densification. The drying shrinkage strains during rapid drying and slow drying were compared and the effects of the microstructural changes and evaporation were separated.

  15. Standard Test Method for Bond Strength of Ceramic Tile to Portland Cement Paste

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2002-01-01

    1.1 This test method covers the determination of the ability of glazed ceramic wall tile, ceramic mosaic tile, quarry tile, and pavers to be bonded to portland cement paste. This test method includes both face-mounted and back-mounted tile. 1.2 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.

  16. Microstructure in hardened cement pastes measured by mercury intrusion porosimetry and low temperature microcalorimetry

    DEFF Research Database (Denmark)

    Hansen, Kurt Kielsgaard; Baroghel, V.B.; Künzel, H.M.

    1996-01-01

    The present paper is presenting some of the results on microstructure from the CEC-Science Project CT91-0737 "Characterization of microstructure as a tool for prediction of moisture transfer in porous media". In the Project the microstructure for the porous media is studied by absorption isotherms......, image analysis, mercury intrusion porosimetry and low temperature microcalorimetry.The present paper is dealing with cumulated pore size distributions measured by mercury intrusion porosimetry (MIP) from two laboratories (LCPC, IBP) and low temperature microcalorimetry (CAL) from one laboratory (BKM......). The materials are five different hardened cement pastes. The materials, the preparation procedure for the samples, the experiments and the experimental results are described. Finally, the results are compared and discussed....

  17. Influence of the pore network on hydrogen diffusion through blended cement pastes

    International Nuclear Information System (INIS)

    Boher, Cedric; Frizon, Fabien; Bart, Florence; Lorente, Sylvie

    2013-01-01

    This article presents a study on the influence of the pore size distribution on gas diffusion through CEM V cement pastes, for different water saturation degrees. The numerical results are compared to the experimental hydrogen diffusion coefficients obtained with water saturation levels ranging from 20% to 95%. The model developed in our research group accounts for the various types of transfer through the pore network: Knudsen diffusion or molecular diffusion depending on the pore size, together with hydrogen diffusion through water. The virtual pore network is created from mercury porosimetry data as a result of the combination of different sizes pore families. By testing different combinations, we could propose pore arrangements leading to diffusion coefficients corresponding to the experimental ones, and show how the combinations of the biggest pore family contribute to control the gas diffusion process. (authors)

  18. Influence of CO2 Laser Radiation on the Mechanical Properties of Portland Cement Pastes

    Directory of Open Access Journals (Sweden)

    González-Mota, R.

    2011-03-01

    Full Text Available This article presents the results of the treatment of fresh cement pastes with CO2 laser radiation (10.6μm, in order to improve its mechanical properties in addition to obtaining lower setting times than those of a natural setting (without radiation . It was observed that the CO2 laser radiation has a positive influence on the mechanical properties of cement paste, not due to the heat produced during irradiation, but due to the effect of electric field propagation on water molecules, whose are arranged around functional groups of the binder and by the effect of ration, causes a micro vibration effect, resulting in a more compact and less porous paste which has better mechanical properties compared to natural setting paste. The internal and surface temperature of the samples, the evolution of setting, Young's modulus (using ultrasonic pulse velocity and compressive strength were registered.En este artículo se presentan los resultados correspondientes al tratamiento de pastas frescas de cemento con radiación láser de CO2 (10.6µm, con el propósito de mejorar sus propiedades mecánicas además de obtener tiempos de fraguado menores a los del fraguado en forma natural (sin radiación. Se demostró que la radiación con láser de CO2 influye positivamente en las propiedades mecánicas de la pasta de cemento, no por el calentamiento producido durante la irradiación, sino por el efecto de la propagación del campo eléctrico sobre las moléculas de agua que están dispuestas alrededor de los grupos funcionales del aglutinante y que al rotar producen un efecto equivalente a micro vibraciones, dando como resultado un material más compacto, con menos poros y mejores propiedades mecánicas respecto al fraguado natural. Se registró la temperatura interna y superficial de las muestras, la evolución del fraguado, el módulo de Young y la resistencia a compresión.

  19. Properties of mortars made by uncalcined FGD gypsum-fly ash-ground granulated blast furnace slag composite binder

    International Nuclear Information System (INIS)

    Zhong Shiyun; Ni Kun; Li Jinmei

    2012-01-01

    Highlights: ► The mortar with uncalcined FGD gypsum has suitable workability. ► The strength of mortar with uncalcined FGD gypsum is higher than that of mortar without uncalcined FGD gypsum. ► The dry shrinkage of mortar with uncalcined FGD gypsum is lower than that of mortar without uncalcined FGD gypsum. ► The leaching of sulfate ion of mortar is studied. - Abstract: A series of novel mortars were developed from composite binder of uncalcined FGD gypsum, fly ash (FA) and ground granulated blast furnace slag (GGBFS) for the good utilization of flue gas desulphurization (FGD) gypsum. At a fixed ratio (20%) of GGBFS to the composite binder, keeping consistency of the mortar between 9.5 and 10.0 cm, the properties of the composite mortar were studied. The results show that higher water/binder (W/B) is required to keep the consistency when increasing the percentage of FGD gypsum. No obvious influences of the W/B and content of FGD gypsum on the bleeding of paste were observed which keeps lower than 2% under all experimental conditions tried. The highest compressive and flexural strengths (ratio is 20% FGD gypsum, 20% GGBFS and 60% FA) are 22.6 and 4.3 MPa at 28 days, respectively. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) results indicate that massive ettringite crystals and C–S–H gels exist in the hydration products. At 90 days the mortars with FGD gypsum is dramatically smaller drying shrinkage (563–938 micro strain) than that without FGD gypsum (about 2250 micro strain). The release of the SO 4 2- from the mortar was analyzed, indicating that the dissolution of sulfate increases with FGD gypsum. The concentration of SO 4 2- releasing from the mortar with 10% FGD gypsum is almost equal to that obtained from the mortar without FGD gypsum. The release of SO 4 2- from the mortar with 20% FGD gypsum is 9200 mg·m −2 , which is lower than that from the mortar with 95% cement clinker and 5% FGD gypsum.

  20. Casting granular ion exchange resins with medium-active waste in cement

    International Nuclear Information System (INIS)

    Beijer, O.

    1980-01-01

    Medium active waste from nuclear power stations in Sweden is trapped in granular ion exchange resins. The resin is mixed with cement paste and cast in a concrete shell which is cubic and has an edge dimension of 1.2 m. In some cases the ion exchange cement mortar has cracked. The report presents laboratory sutdies of the properties of the ion exchange resin and the mortar. Also the leaching of the moulds has been investigated. It was shown that a mixture with a water cement ratio higher than about 0.5 swells considerably during the first weeks after casting. The diffusion constant for cesium 137 has been determined at 3.10 -4 cm 2 /24-hour period in conjunction with exposure of the mould and mortar to sea water. The Swedish language report has 400 pages with 90 figures and 30 tables. (author)

  1. Potencialidades de um caulim calcinado como material de substituição parcial do cimento portland em argamassas Potentialities of a calcined kaolin as material of partial replacement of portland cement in mortars

    Directory of Open Access Journals (Sweden)

    Marilia P. de Oliveira

    2006-06-01

    Full Text Available A utilização de argilas calcinadas na forma de metacaulinita, como material pozolânico para argamassas e concretos, tem recebido atenção considerável nos últimos anos. Este trabalho objetivou avaliar o desempenho mecânico de argamassas, nas quais foi utilizado um caulim calcinado proveniente do Estado da Paraíba, como material de substituição parcial do cimento Portland. Utilizaram-se duas finuras do caulim: passando nas peneiras ABNT 200 (0,074 mm e 325 (0,044 mm e calcinados nas temperaturas de 700, 800 e 900 ºC pelo tempo de 2 h. As amostras foram caracterizadas através de análise química, análise térmica diferencial, difração de raios-X e área específica. Obteve-se o índice de atividade pozolânica com a cal e o cimento Portland. O percentual de substituição adotado foi de 0, 10, 20, 30 e 40%. A relação aglomerante: areia foi de 1:1,5 e a relação água/aglomerante fixada igual 0,4. O efeito da substituição parcial do cimento na argamassa foi avaliado através da resistência à compressão simples, nas idades de 7, 28 e 90 dias. As argamassas estudadas apresentaram resistência superior em relação à da referência, até o nível de 30% de substituição.The use of burnt clays, in the metakaolin form, as pozzolanic material for mortars and concretes has received a remarkable attention in the last years. This paper aimed to evaluate the mechanical property of mortars, in which a calcined kaolin originating from the State of Paraiba, was used as partial cement replacement material. Two finess of the kaolin were used: ABNT 200 (0.074 mm and 325 (0.044 mm and burnt at temperatures of 700, 800 and 900 ºC for a period of 2 h. Both materials were characterized by chemical analysis, differential thermal analysis, X-ray diffraction, specific area tests. The pozolanic activity index was obtanied using lime and cement Portland. The amounts of replacement were 10, 20, 30 and 40%, besides the reference mortar. The binder

  2. Carbonation-Induced Mineralogical Changes in Coal Mining Waste Blended Cement Pastes and Their Influence on Mechanical and Microporosity Properties

    Directory of Open Access Journals (Sweden)

    Moisés Frías

    2018-04-01

    Full Text Available The worldwide pursuit of new eco-efficient pozzolans is ongoing. Kaolinite-based waste is an eco-friendly source of recycled metakaolinite, a highly pozzolanic product. In this study, a blended cement paste containing 20% activated coal waste (ACW was exposed to a 100% CO2 atmosphere at 65% RH for 7 days. The variations in its phase composition and strength were studied and compared to an OPC control. Both pastes were cured for 28 days prior to the carbonation test. Reaction kinetics were assessed using XRD, SEM/EDX, TG/DTG, FT-IR, Micro-Raman spectroscopy, pore solution pH and the cumulative carbonated fraction. The blended cement carbonated 68% faster than the control. While portlandite carbonation was the main reaction in both cements, decalcification was also observed (more intensely in the 20% ACW paste in other hydraulic calcium phases (C-S-H gel, monocarboaluminate (C4AcH12, ettringite and tetracalcium aluminate (C4AH13. The end product of this reaction was calcium carbonate, mainly in the form of calcite, although traces of aragonite and amorphous carbonate were also detected. Compressive strength values rose with accelerated carbonation time and pore size reduction in both cement pastes.

  3. Effect of Ground Waste Concrete Powder on Cement Properties

    Directory of Open Access Journals (Sweden)

    Xianwei Ma

    2013-01-01

    Full Text Available The paste/mortar attached to the recycled aggregate decreases the quality of the aggregate and needs to be stripped. The stripped paste/mortar is roughly 20% to 50% in waste concrete, but relevant research is very limited. In this paper, the effects of ground waste concrete (GWC powder, coming from the attached paste/mortar, on water demand for normal consistency, setting time, fluidity, and compressive strength of cement were analyzed. The results show that the 20% of GWC powder (by the mass of binder has little effect on the above properties and can prepare C20 concrete; when the sand made by waste red clay brick (WRB replaces 20% of river sand, the strength of the concrete is increased by 17% compared with that without WRB sand.

  4. Nanostructural Deformation Analysis of Calcium Silicate Hydrate in Portland Cement Paste by Atomic Pair Distribution Function

    Directory of Open Access Journals (Sweden)

    Hiroshi Suzuki

    2016-01-01

    Full Text Available The deformation of nanostructure of calcium silicate hydrate (C-S-H in Portland cement (PC paste under compression was characterized by the atomic pair distribution function (PDF, measured using synchrotron X-ray diffraction. The PDF of the PC paste exhibited a unique deformation behavior for a short-range order below 2.0 nm, close to the size of the C-S-H globule, while the deformation for a long-range order was similar to that of a calcium hydroxide phase measured by Bragg peak shift. The compressive deformation of the C-S-H nanostructure was comprised of three stages with different interactions between globules. This behavior would originate from the granular nature of C-S-H, which deforms with increasing packing density by slipping the interfaces between globules, rearranging the overall C-S-H nanostructure. This new approach will lead to increasing applications of the PDF technique to understand the deformation mechanism of C-S-H in PC-based materials.

  5. Critical aspects of nano-indentation technique in application to hardened cement paste

    International Nuclear Information System (INIS)

    Davydov, D.; Jirasek, M.; Kopecky, L.

    2011-01-01

    Several open questions related to the experimental protocol and processing of data acquired by the nano-indentation (NI) technique are investigated. The volume fractions of mechanically different phases obtained from statistical NI (SNI) analysis are shown to be different from those obtained by back-scattered electron (BSE) image analysis and X-ray diffraction (XRD) method on the same paste. Judging from transmission electron microscope (TEM) images, the representative volume element of low-density calcium-silicate hydrates (C-S-H) can be considered to be around 500 nm, whereas for high-density C-S-H it is about 100 nm. This raises the question how the appropriate penetration depth for NI experiments should be selected. Changing the maximum load from 1 mN to 5 mN, the effect of penetration depth on the experimental results is studied. As an alternative to the SNI method, a 'manual' indentation method is proposed, which combines information from BSE and atomic-force microscopy (AFM), coupled to the NI machine. The AFM allows to precisely indent a high-density C-S-H rim around unhydrated clinkers in cement paste. Yet the results from that technique still show a big scatter.

  6. Impact of the associated cation on chloride binding of Portland cement paste

    International Nuclear Information System (INIS)

    De Weerdt, K.; Colombo, A.; Coppola, L.; Justnes, H.; Geiker, M.R.

    2015-01-01

    Well hydrated cement paste was exposed to MgCl 2 , CaCl 2 and NaCl solutions at 20 °C. The chloride binding isotherms for free chloride concentrations ranging up to 1.5 mol/l were determined experimentally. More chlorides were found to be bound when the associated cation was Mg 2 + or Ca 2 + compared to Na + . The chloride binding capacity of the paste appeared to be related to the pH of the exposure solution. In order to explain the cation dependency of the chloride binding a selection of samples was investigated in detail using experimental techniques such as TG, XRD and SEM–EDS to identify the phases binding the chlorides. The experimentally obtained data were compared with the calculations of a thermodynamic model, GEMS. It was concluded that the measured change in chloride binding depending on the cation was mainly governed by the pH of the exposure solution and thereby the binding capacity of the C-S-H

  7. Preparation and Characterization of New Geopolymer-Epoxy Resin Hybrid Mortars

    Directory of Open Access Journals (Sweden)

    Raffaele Cioffi

    2013-07-01

    Full Text Available The preparation and characterization of metakaolin-based geopolymer mortars containing an organic epoxy resin are presented here for the first time. The specimens have been prepared by means of an innovative in situ co-reticulation process, in mild conditions, of commercial epoxy based organic resins and geopolymeric slurry. In this way, geopolymer based hybrid mortars characterized by a different content of normalized sand (up to 66% in weight and by a homogeneous dispersion of the organic resin have been obtained. Once hardened, these new materials show improved compressive strength and toughness in respect to both the neat geopolymer and the hybrid pastes since the organic polymer provides a more cohesive microstructure, with a reduced amount of microcracks. The microstructural characterization allows to point out the presence of an Interfacial Transition Zone similar to that observed in cement based mortars and concretes. A correlation between microstructural features and mechanical properties has been studied too.

  8. Properties of Foamed Mortar Prepared with Granulated Blast-Furnace Slag

    OpenAIRE

    Zhao, Xiao; Lim, Siong-Kang; Tan, Cher-Siang; Li, Bo; Ling, Tung-Chai; Huang, Runqiu; Wang, Qingyuan

    2015-01-01

    Foamed mortar with a density of 1300 kg/m3 was prepared. In the initial laboratory trials, water-to-cement (w/c) ratios ranging from 0.54 to 0.64 were tested to determine the optimal value for foamed mortar corresponding to the highest compressive strength without compromising its fresh state properties. With the obtained optimal w/c ratio of 0.56, two types of foamed mortar were prepared, namely cement-foamed mortar (CFM) and slag-foamed mortar (SFM, 50% cement was replaced by slag weight). ...

  9. Formulating a low-alkalinity cement for radioactive waste repositories

    International Nuclear Information System (INIS)

    Coumes, C. Cau Dit; Courtois, S.; Leclercq, S.; Bourbon, X.

    2004-01-01

    A multi-annual research program has been launched in January 2003 by CEA, EDF and ANDRA in order to formulate and characterize low-alkalinity and low-heat cements which would be compatible with an underground waste repository environment. Four types of bindings have been investigated: binary blends of Portland cement and silica fume or metakaolin, as well as ternary blends of Portland cement, fly ash and silica fume or metakaolin. Promising results have been obtained with a mixture comprising 37.5% Portland cement, 32.5% silica fume, and 30% fly ash: pH of water in equilibrium with fully hydrated cement is below 11. Moreover, silica fume compensates for the low reactivity of fly ash, while fly ash allows to reduce water demand, heat release, and dimensional variations of cement pastes and mortars. (authors)

  10. Formulating a low-alkalinity cement for radioactive waste repositories

    Energy Technology Data Exchange (ETDEWEB)

    Coumes, C. Cau Dit; Courtois, S.; Leclercq, S.; Bourbon, X

    2004-07-01

    A multi-annual research program has been launched in January 2003 by CEA, EDF and ANDRA in order to formulate and characterize low-alkalinity and low-heat cements which would be compatible with an underground waste repository environment. Four types of bindings have been investigated: binary blends of Portland cement and silica fume or metakaolin, as well as ternary blends of Portland cement, fly ash and silica fume or metakaolin. Promising results have been obtained with a mixture comprising 37.5% Portland cement, 32.5% silica fume, and 30% fly ash: pH of water in equilibrium with fully hydrated cement is below 11. Moreover, silica fume compensates for the low reactivity of fly ash, while fly ash allows to reduce water demand, heat release, and dimensional variations of cement pastes and mortars. (authors)

  11. THE USE OF SISAL FIBRE AS REINFORCEMENT IN CEMENT BASED COMPOSITES

    OpenAIRE

    Tolêdo Filho,Romildo Dias; Joseph,Kuruvilla; Ghavami,Khosrow; England,George Leslie

    1999-01-01

    ABSTRACT The inclusion of fibre reinforcement in concrete, mortar and cement paste can enhance many of the engineering properties of the basic materials, such as fracture toughness, flexural strength and resistance to fatigue, impact, thermal shock and spalling. In recent years, a great deal of interest has been created worldwide on the potential applications of natural fibre reinforced, cement based composites. Investigations have been carried out in many countries on various mechanical prop...

  12. Parameters of Alumina Cement and Portland Cement with Addition of Chalcedonite Meal

    Science.gov (United States)

    Kotwa, Anna

    2017-10-01

    Aluminous cement is a quick binder with special properties. It is used primarily to make non-standard monolithic components exposed to high temperatures, + 1300°C. It is also a component of adhesives and mortars. It has a very short setting time. It is characterized by rapid increase in mechanical strength and resistance to aggressive sulphates. It can be used in reinforced concrete structures. Laying of concrete, construction mortar made of alumina cement can be carried out even at temperatures of -10°C. This article discusses a comparison of the parameters of hardened mortar made of alumina cement GÓRKAL 40 and Portland cement CEM I 42.5R. The mortars contain an addition of chalcedonite meal with pozzolanic properties, with particle size of less than 0.063μm. The meal was added in amounts of 5% and 20% of cement weight. Chalcedonite meal used in the laboratory research is waste material, resulting from chalcedonite aggregate mining. It has the same properties as the rock from which it originates. We have compared the parameters of hardened mortar i.e. compressive strength, water absorption and capillarity. The addition of 20% chalcedonite meal to mortars made from aluminous cement will decrease durability by 6.1% relative to aluminous cement mortar without addition of meal. Considering the results obtained during the absorbency tests, it can be stated that the addition of chalcedonite meal reduces weight gains in mortars made with cement CEM I 42.5 R and alumina cement. Use of alumina cement without addition of meal in mortars causes an increase of mass by 248% compared to Portland cement mortars without additions, in the absorption tests. The addition of chalcedonite meal did not cause increased weight gain in the capillary action tests. For the alumina cement mortars, a lesser weight gains of 24.7% was reported, compared to the Portland cement mortar after 28 days of maturing.

  13. Temperature dependence of autogenous shrinkage of silica fume cement pastes with a very low water–binder ratio

    Energy Technology Data Exchange (ETDEWEB)

    Maruyama, I., E-mail: ippei@dali.nuac.nagoya-u.ac.jp [Graduate School of Environmental Studies, Nagoya University, ES Building, No. 539, Furo-cho, Chikusa-ku, Nagoya 464-8603 (Japan); Teramoto, A. [Graduate School of Environmental Studies, Nagoya University, Faculty of Engineering, ES Building, No. 546, Furo-cho, Chikusa-ku, Nagoya 464-8603 (Japan)

    2013-08-15

    Ultra-high-strength concrete with a large unit cement content undergoes considerable temperature increase inside members due to hydration heat, leading to a higher risk of internal cracking. Hence, the temperature dependence of autogenous shrinkage of cement pastes made with silica fume premixed cement with a water–binder ratio of 0.15 was studied extensively. Development of autogenous shrinkage showed different behaviors before and after the inflection point, and dependence on the temperature after mixing and subsequent temperature histories. The difference in autogenous shrinkage behavior poses problems for winter construction because autogenous shrinkage may increase with decrease in temperature after mixing before the inflection point and with increase in temperature inside concrete members with large cross sections.

  14. Temperature dependence of autogenous shrinkage of silica fume cement pastes with a very low water–binder ratio

    International Nuclear Information System (INIS)

    Maruyama, I.; Teramoto, A.

    2013-01-01

    Ultra-high-strength concrete with a large unit cement content undergoes considerable temperature increase inside members due to hydration heat, leading to a higher risk of internal cracking. Hence, the temperature dependence of autogenous shrinkage of cement pastes made with silica fume premixed cement with a water–binder ratio of 0.15 was studied extensively. Development of autogenous shrinkage showed different behaviors before and after the inflection point, and dependence on the temperature after mixing and subsequent temperature histories. The difference in autogenous shrinkage behavior poses problems for winter construction because autogenous shrinkage may increase with decrease in temperature after mixing before the inflection point and with increase in temperature inside concrete members with large cross sections

  15. A study on the effect of nano silica on compressive strength of high volume fly ash mortars and concretes

    International Nuclear Information System (INIS)

    Shaikh, F.U.A.; Supit, S.W.M.; Sarker, P.K.

    2014-01-01

    Highlights: • The addition of NS compensates low early age compressive strength of HVFA system. • NS also contributes to later age compressive strength gain of HVFA system. • The XRD results confirm the reduction of CH in HVFA paste due to addition of NS. - Abstract: This paper presents the effect of nano silica (NS) on the compressive strength of mortars and concretes containing different high volume fly ash (HVFA) contents ranging from 40% to 70% (by weight) as partial replacement of cement. The compressive strength of mortars is measured at 7 and 28 days and that for concretes is measured at 3, 7, 28, 56 and 90 days. The effects of NS in microstructure development and pozzolanic reaction of pastes containing above HVFA contents are also studied through backscattered electron (BSE) image and X-ray diffraction (XRD) analysis. Results show that among different NS contents ranging from 1% to 6%, cement mortar containing 2% NS exhibited highest 7 and 28 days compressive strength. This NS content (2%) is then added to the HVFA mortars and concretes and the results show that the addition of 2% NS improved the early age (7 days) compressive strength of mortars containing 40% and 50% fly ash by 5% and 7%, respectively. However, this improvement is not observed at high fly ash contents beyond 50%. On the other hand, all HVFA mortars exhibited improvement in 28 days compressive strength due to addition of 2% NS and the most significant improvement is noticed in mortars containing more than 50% fly ash. In HVFA concretes, the improvement of early age (3 days) compressive strength is also noticed due to addition of 2% NS. The BSE and XRD analysis results also support the above findings

  16. Properties of calcium depleted hydrated cement paste: mineralogical characterization and cesium adsorption

    International Nuclear Information System (INIS)

    Babaahmadi, A.; Tang, L.; Zareen, A.

    2015-01-01

    Understanding the changes in adsorption properties of cementitious barriers and the effect on the release of radio-nuclides to the environment during the service life of the repository is of high importance. A major degradation scenario within safety assessment analysis of nuclear waste repositories is decalcification of cementitious materials due to long-term contact with groundwater. In order to decrease the uncertainty in the simulation of this process due to extrapolating short term data sets based on short term experimental analysis, acceleration methods enhancing the decalcification process can be used. However it is not yet completely proved that how different the properties of the aged samples through accelerated leaching is compared to the samples aged in natural ageing process. In this study the changes in cesium adsorption of the hydrated cement paste due to calcium depletion is taken in to consideration. The aged samples are prepared with application of an accelerating electro-chemical migration method. The mineralogical properties of decalcified specimens are characterized to demonstrate their comparability with naturally leached samples. The gradual effect of migration function on cementitious materials indicates a relatively homogenous leaching in cementitious specimens and a considerable increase in specific surface area due to the leaching of calcium. It is concluded that the aged samples having a larger surface area and less calcium and alkalis ions compared to pristine materials, exhibit a higher binding potential for Cs ions

  17. Moisture migration and shrinkage of hardened cement paste at elevated temperatures

    International Nuclear Information System (INIS)

    Numao, Tatsuya; Mihashi, Hirozo.

    1991-01-01

    The drying shrinkage of concrete is caused by the loss of water in the concrete. The moisture diffusion behavior influences the mechanical properties of concrete. When concrete is exposed to high temperature, the rate of moisture migration becomes fast, and moisture gradient is formed. This gradient causes cracks on the concrete surface. Accordingly, it is important to study on the relation between the drying shrinkage and the water diffusion in concrete when its mechanical properties at elevated temperature are discussed. In this paper, the results of the experiment which was carried out by using thin-walled cylinder specimens kept at different temperature and stress are reported. The specimens, the drying shrinkage of concrete and acoustic emission (AE), the thermal expansion of hardened cement paste, the influence that temperature change exerted to the drying shrinkage, and the influence that compressive stress and temperature exerted to water migration are described. The thin-walled cylinder specimens were useful for these experimental studies. (K.I.)

  18. Swine deep bedding ashes as a mineral additive for cement based mortar Cinzas de cama sobreposta de suínos como adição mineral em argamassas de cimento

    Directory of Open Access Journals (Sweden)

    Melissa Selaysim Di Campos

    2008-04-01

    Full Text Available The sustainability of intensive swine production demands alternative destinations for the generated residues. Ashes from swine rice husk-based deep bedding were tested as a mineral addition for cement mortars. The ashes were obtained at 400 to 600ºC, ground and sieved through a 325 mesh sieve (# 0.045 mm. The characterization of the ashes included the determination of the index of pozzolanic activity with lime. The ashes were also tested as partial substitutes of Portland cement. The mortars were prepared using a cement:sand proportion of 1:1.5, and with water/cement ratio of 0.4. Three percentages of mass substitution of the cement were tested: 10, 20 and 30%. Mortar performances were assessed at 7 and 28 days determining their compressive strength. The chosen condition for calcinations at the laboratory scale was related to the maximum temperature of 600ºC since the resulting ashes contained vitreous materials and presented satisfactory values for the pozzolanic index under analysis. The pozzolanic activity indicated promising results for ashes produced at 600ºC as a replacement of up to 30% in cement masses.A sustentabilidade das regiões de produção intensiva de suínos requer destinos alternativos para os resíduos gerados. Cinzas de cama sobreposta de suínos à base casca de arroz, foram testadas como adição mineral em substituição ao cimento. As cinzas foram obtidas nas temperaturas de 400 a 600ºC, moídas e passadas por peneira ABNT 325 (# 0,045 mm. A caracterização de cinzas incluiu a determinação do índice de atividade pozolânica com a cal. As cinzas também foram testadas como substitutos parciais de cimento Portland. As argamassas foram preparadas na proporção cimento:areia de 1:1,5 e com fator água-cimento de 0,4. Três porcentagens de substituição do cimento comercial foram usadas: 10, 20 e 30% em massa. O desempenho das argamassas foi avaliado aos 7 e aos 28 dias com a determinação da resistência

  19. Basalt waste added to Portland cement

    Directory of Open Access Journals (Sweden)

    Thiago Melanda Mendes

    2016-08-01

    Full Text Available Portland cement is widely used as a building material and more than 4.3 billion tons were produced in 2014, with increasing environmental impacts by this industry, mainly through CO2 emissions and consumption of non-removable raw materials. Several by-products have been used as raw materials or fuels to reduce environmental impacts. Basaltic waste collected by filters was employed as a mineral mixture to Portland cement and two fractions were tested. The compression strength of mortars was measured after 7 days and Scanning Electron Microscopy (SEM and Electron Diffraction Scattering (EDS were carried out on Portland cement paste with the basaltic residue. Gains in compression strength were observed for mixtures containing 2.5 wt.% of basaltic residue. Hydration products observed on surface of basaltic particles show the nucleation effect of mineral mixtures. Clinker substitution by mineral mixtures reduces CO2 emission per ton of Portland cement.

  20. Analysis of Cement-Based Pastes Mixed with Waste Tire Rubber

    Science.gov (United States)

    Sola, O. C.; Ozyazgan, C.; Sayin, B.

    2017-03-01

    Using the methods of thermal gravimetry, differential thermal analysis, Furier transform infrared analysis, and capillary absorption, the properties of a cement composite produced by introducing waste tyre rubber into a cement mixture were investigated. It was found that the composite filled with the rubber had a much lower water absorption ability than the unfilled one.

  1. Properties of mortars made by uncalcined FGD gypsum-fly ash-ground granulated blast furnace slag composite binder.

    Science.gov (United States)

    Zhong, Shiyun; Ni, Kun; Li, Jinmei

    2012-07-01

    A series of novel mortars were developed from composite binder of uncalcined FGD gypsum, fly ash (FA) and ground granulated blast furnace slag (GGBFS) for the good utilization of flue gas desulphurization (FGD) gypsum. At a fixed ratio (20%) of GGBFS to the composite binder, keeping consistency of the mortar between 9.5 and 10.0 cm, the properties of the composite mortar were studied. The results show that higher water/binder (W/B) is required to keep the consistency when increasing the percentage of FGD gypsum. No obvious influences of the W/B and content of FGD gypsum on the bleeding of paste were observed which keeps lower than 2% under all experimental conditions tried. The highest compressive and flexural strengths (ratio is 20% FGD gypsum, 20% GGBFS and 60% FA) are 22.6 and 4.3 MPa at 28 days, respectively. Scanning electron microscopy (SEM) and X-ray diffraction (XRD) results indicate that massive ettringite crystals and C-S-H gels exist in the hydration products. At 90 days the mortars with FGD gypsum is dramatically smaller drying shrinkage (563-938 micro strain) than that without FGD gypsum (about 2250 micro strain). The release of the SO(4)(2-) from the mortar was analyzed, indicating that the dissolution of sulfate increases with FGD gypsum. The concentration of SO(4)(2-) releasing from the mortar with 10% FGD gypsum is almost equal to that obtained from the mortar without FGD gypsum. The release of SO(4)(2-) from the mortar with 20% FGD gypsum is 9200 mg·m(-2), which is lower than that from the mortar with 95% cement clinker and 5% FGD gypsum. Copyright © 2012 Elsevier Ltd. All rights reserved.

  2. Electromagnetic interference shielding with Portland cement paste containing carbon materials and processed fly ash

    Directory of Open Access Journals (Sweden)

    Zornoza, E.

    2010-12-01

    Full Text Available The study described in this article explored the effect of adding different types of carbon materials (graphite powder and three types of carbon fibre, fly ash (with 5.6%, 15.9% and 24.3% Fe2O3, and a mix of both on electromagnetic interference (EMI shielding in Portland cement pastes. The parameters studied included the type and aspect ratio of the carbonic material, composite material thickness, the frequency of the incident electromagnetic radiation and the percentage of the magnetic fraction in the fly ash. The findings showed that the polyacrylonitrile-based carbon fibres, which had the highest aspect ratio, provided more effective shielding than any of the other carbon materials studied. Shielding was more effective in thicker specimens and at higher radiation frequencies. Raising the magnetic fraction of the fly ash, in turn, also enhanced paste shielding performance. Finally, adding both carbon fibre and fly ash to the paste resulted in the most effective EMI shielding as a result of the synergies generated.

    En el presente trabajo se investiga la influencia de la adición de diferentes tipos de materiales carbonosos (polvo de grafito y 3 tipos de fibra de carbono, de una ceniza volante con diferentes contenidos de fase magnética (5,6%, 15,9% y 24,3% de Fe2O3 y de una mezcla de ambos, sobre la capacidad de apantallar interferencias electromagnéticas de pastas de cemento Pórtland. Entre los parámetros estudiados se encuentra: el tipo de material carbonoso, la relación de aspecto del material carbonoso, el espesor del material compuesto, la frecuencia de la radiación electromagnética incidente y el porcentaje de fracción magnética en la ceniza volante. Los resultados obtenidos indican que entre los materiales carbonosos estudiados son las fibras de carbono basadas en poliacrilonitrilo con una mayor relación de aspecto las que dan mejores resultados de apantallamiento. Al aumentar

  3. Concrete Durability Properties and Microstructural Analysis of Cement Pastes with Nopal Cactus Mucilage as a Natural Additive

    Directory of Open Access Journals (Sweden)

    Ramírez-Arellanes, S.

    2012-09-01

    Full Text Available The present study evaluated the addition of a 3% nopal cactus mucilage solution to cement pastes, in its effects on setting times, flow, hydration, and microstructure, as well as on capillary water absorption and chloride diffusion in concrete. Hydration was characterized through XRD and microstructure was characterized with SEM. The mucilage solution/cement and water/cement ratios tested were 0.30, 0.45, and 0.60. The results in cement pastes indicate that the addition of mucilage increases setting times, reduces flow, slows cement hydration, and inhibits the formation of calcium hydroxide crystals in comparison with the control. Capillary absorption was significantly reduced in concrete containing mucilage, and chloride diffusion coefficients dropped up to 20% in the mixture with a mucilage/cement ratio = 0.30. The mixture with a mucilage/cement ratio = 0.45 displayed marginal reduction, and the mixture with mucilage/cement ratio = 0.60 exhibited a diffusion coefficient that was greater than the control for the specimens without moist curing.En esta investigación se evaluó el efecto de una solución de mucílago de nopal al 3% en los tiempos de fraguado, fluidez, hidratación y microestructura de pastas de cemento, y absorción capilar de agua y difusión de cloruros en concreto. La hidratación fue caracterizada por XRD y la microestructura por medio de SEM. Las relaciones solución de mucílago/cemento y agua/cemento fueron 0,30; 0,45 y 0,60. Los resultados en las pastas de cemento indican que el mucílago retarda los tiempos de fraguado, reduce la fluidez, retarda la hidratación del cemento, e inhibe la formación de cristales de hidróxido de calcio, comparados con los controles. La absorción capilar en concreto conteniendo mucílago se redujo significativamente y los coeficientes de difusión de cloruros disminuyeron hasta 20% en la mezcla mucílago/cemento = 0.30. En la relación mucílago/cemento = 0.45 la reducción fue marginal y

  4. Mortar modified with sulfonated polystyrene produced from waste plastic cups

    OpenAIRE

    MOTTA,L. A. C.; VIEIRA,J. G.; OMENA,T. H.; FARIA,F. A. C.; RODRIGUES FILHO,G.; ASSUNÇÃO,R. M. N.

    2016-01-01

    Abstract In this work, we studied the addition of sulfonated polystyrene produced from waste plastic cups as an admixture for mortars. Mortars were analyzed with polystyrene content of 0.0; 0.2; 0.6; 1.0 and 1.4% in relation to the cement mass. The influence of polystyrene on the mortars' properties was evaluated by the consistency index, water retention, water absorption, porosity, elasticity modulus, compressive strength, flexural strength, bond tensile strength and microscopy. The increase...

  5. Aggregate-cement paste transition zone properties affecting the salt-frost damage of high-performance concretes

    International Nuclear Information System (INIS)

    Cwirzen, Andrzej; Penttala, Vesa

    2005-01-01

    The influence of the cement paste-aggregate interfacial transition zone (ITZ) on the frost durability of high-performance silica fume concrete (HPSFC) has been studied. Investigation was carried out on eight non-air-entrained concretes having water-to-binder (W/B) ratios of 0.3, 0.35 and 0.42 and different additions of condensed silica fume. Studies on the microstructure and composition of the cement paste have been made by means of environmental scanning electron microscope (ESEM)-BSE, ESEM-EDX and mercury intrusion porosimetry (MIP) analysis. The results showed that the transition zone initiates and accelerates damaging mechanisms by enhancing movement of the pore solution within the concrete during freezing and thawing cycles. Cracks filled with ettringite were primarily formed in the ITZ. The test concretes having good frost-deicing salt durability featured a narrow transition zone and a decreased Ca/Si atomic ratio in the transition zone compared to the bulk cement paste. Moderate additions of silica fume seemed to densify the microstructure of the ITZ

  6. Effect of thermally activated paper sludge on the mechanical properties and porosity of cement pastes

    Directory of Open Access Journals (Sweden)

    García, R.

    2009-06-01

    Full Text Available The present article discusses the effect of paper sludge additions, calcined at 700 ºC for two hours, on cement paste pore structure and mechanical strength. Both total and capillary porosity were observed to depend on the percentage of calcined sludge added to the cementitious matrix. While a 10% addition induced values for both slightly higher than the control, adding 20% prompted the opposite result, reducing porosity values with respect to the control. Substantial refinement was observed, with a rise in pores smaller than 0.01 μm (gel pores when the calcined sludge was added. Such refinement was greater at the higher percentage of sludge. After approximately 15 days, strength was lower in both the additioned pastes compared to the control. A high correlation (R2≥0.939 was found between total porosity and compressive strength for both percentages studied.El presente trabajo muestra el resultado de una investigación llevada a cabo en pastas de cemento que contienen un 10 y un 20% de lodo de papel calcinado a 700 ºC, durante 2h. Se estudia cómo afecta esta adición activa en la estructura porosa y las resistencias mecánicas. Se demuestra que tanto la porosidad total como la capilar dependen del porcentaje de lodo calcinado añadido a la matriz cementante. Así, un 10% de adición muestra para ambas porosidades valores ligeramente superiores al de la pasta de referencia, sin embargo la incorporación de un 20% produce un resultado contrario, disminuyendo ambas porosidades con respecto a la pasta control. Para el caso de poros de tamaño inferior a 0,01 μm (poros de gel se detecta un importante proceso de refinamiento con la incorporación del lodo calcinado, este refinamiento es tanto mayor cuanto mayor es el porcentaje añadido. En cuanto a los valores de resistencia, para los dos porcentajes de adición se produce una disminución a partir de aproximadamente 15 días, respecto a la pasta patrón. Se muestra una buena correlaci

  7. A study of the water vapor sorption isotherms of hardened cement pastes: Possible pore structure changes at low relative humidity and the impact of temperature on isotherms

    DEFF Research Database (Denmark)

    Wu, Min; Johannesson, Björn; Geiker, Mette Rica

    2014-01-01

    cement paste samples and a model material MCM-41. The pronounced impact of temperature on desorption isotherms of cement based materials as reported in literature was not found in this investigation. The results suggest that the differences between the sorption isotherms measured at different...

  8. A Study of Array Direction HDPE Fiber Reinforced Mortar

    Science.gov (United States)

    Kamsuwan, Trithos

    2018-02-01

    This paper presents the effect of array direction HDPE fiber using as the reinforced material in cement mortar. The experimental data were created reference to the efficiency of using HDPE fiber reinforced on the tensile properties of cement mortar with different high drawn ratio of HDPE fibers. The fiber with the different drawn ratio 25x (d25 with E xx), and 35x (d35 with E xx) fiber volume fraction (0%, 1.0%, 1.5%) and fiber length 20 mm. were used to compare between random direction and array direction of HDPE fibers and the stress - strain displacement relationship behavior of HDPE short fiber reinforced cement mortar were investigated. It was found that the array direction with HDPE fibers show more improved in tensile strength and toughness when reinforced in cement mortar.

  9. Mortar modified with sulfonated polystyrene produced from waste plastic cups

    Directory of Open Access Journals (Sweden)

    L. A. C. MOTTA

    Full Text Available Abstract In this work, we studied the addition of sulfonated polystyrene produced from waste plastic cups as an admixture for mortars. Mortars were analyzed with polystyrene content of 0.0; 0.2; 0.6; 1.0 and 1.4% in relation to the cement mass. The influence of polystyrene on the mortars' properties was evaluated by the consistency index, water retention, water absorption, porosity, elasticity modulus, compressive strength, flexural strength, bond tensile strength and microscopy. The increase in the sulfonated polystyrene content decreased the elasticity modulus of the mortar and, despite higher porosity, there was a reduction of water absorption by capillarity. In relation to mortar without admixture, the modified mortar showed an increase in water retention and consistency index, and a large increase in flexural strength and bond tensile strength. The significant increase of bond tensile strength (214% with admixture 1% highlights the potential of the produced material as an adhesive mortar.

  10. Self healing phenomena in concretes and masonry mortars: A microscopic study

    NARCIS (Netherlands)

    Nijland, T.G.; Larbi, J.A.; Hees, R.P.J. van; Lubelli, B.A.; Rooij, M.R. de

    2007-01-01

    A microscopic survey of over 1000 of samples of concrete and masonry mortars from structures in the Netherlands shows that, in practice, self healing occurs in historic lime and lime – puzzolana mortars, in contrast to modern cement bound concretes and mortars. Self healing may be effected by the

  11. Water extraction out of mortar during brick laying. An NMR study

    NARCIS (Netherlands)

    Brocken, H.J.P.

    1996-01-01

    The water extraction out of mortar during brick laying was studied by nuclear magnetic resonance. The water extraction is an important parameter that determines, e.g., the stiffness of the mortar due to compaction of the cement particles and the bond strength of the cured-mortar interfaces but allo

  12. Properties of Chemically Combusted Calcium Carbide Residue and Its Influence on Cement Properties

    Directory of Open Access Journals (Sweden)

    Hongfang Sun

    2015-02-01

    Full Text Available Calcium carbide residue (CCR is a waste by-product from acetylene gas production. The main component of CCR is Ca(OH2, which can react with siliceous materials through pozzolanic reactions, resulting in a product similar to those obtained from the cement hydration process. Thus, it is possible to use CCR as a substitute for Portland cement in concrete. In this research, we synthesized CCR and silica fume through a chemical combustion technique to produce a new reactive cementitious powder (RCP. The properties of paste and mortar in fresh and hardened states (setting time, shrinkage, and compressive strength with 5% cement replacement by RCP were evaluated. The hydration of RCP and OPC (Ordinary Portland Cement pastes was also examined through SEM (scanning electron microscope. Test results showed that in comparison to control OPC mix, the hydration products for the RCP mix took longer to formulate. The initial and final setting times were prolonged, while the drying shrinkage was significantly reduced. The compressive strength at the age of 45 days for RCP mortar mix was found to be higher than that of OPC mortar and OPC mortar with silica fume mix by 10% and 8%, respectively. Therefore, the synthesized RCP was proved to be a sustainable active cementitious powder for the strength enhanced of building materials, which will result in the diversion of significant quantities of this by-product from landfills.

  13. Properties of Chemically Combusted Calcium Carbide Residue and Its Influence on Cement Properties.

    Science.gov (United States)

    Sun, Hongfang; Li, Zishanshan; Bai, Jing; Memon, Shazim Ali; Dong, Biqin; Fang, Yuan; Xu, Weiting; Xing, Feng

    2015-02-13

    Calcium carbide residue (CCR) is a waste by-product from acetylene gas production. The main component of CCR is Ca(OH)₂, which can react with siliceous materials through pozzolanic reactions, resulting in a product similar to those obtained from the cement hydration process. Thus, it is possible to use CCR as a substitute for Portland cement in concrete. In this research, we synthesized CCR and silica fume through a chemical combustion technique to produce a new reactive cementitious powder (RCP). The properties of paste and mortar in fresh and hardened states (setting time, shrinkage, and compressive strength) with 5% cement replacement by RCP were evaluated. The hydration of RCP and OPC (Ordinary Portland Cement) pastes was also examined through SEM (scanning electron microscope). Test results showed that in comparison to control OPC mix, the hydration products for the RCP mix took longer to formulate. The initial and final setting times were prolonged, while the drying shrinkage was significantly reduced. The compressive strength at the age of 45 days for RCP mortar mix was found to be higher than that of OPC mortar and OPC mortar with silica fume mix by 10% and 8%, respectively. Therefore, the synthesized RCP was proved to be a sustainable active cementitious powder for the strength enhanced of building materials, which will result in the diversion of significant quantities of this by-product from landfills.

  14. Temperature dependence, 0 to 40 deg. C, of the mineralogy of Portland cement paste in the presence of calcium carbonate

    International Nuclear Information System (INIS)

    Matschei, Thomas; Glasser, Fredrik P.

    2010-01-01

    Thermodynamic calculations disclose that significant changes of the AFm and AFt phases and amount of Ca(OH) 2 occur between 0 and 40 deg. C; the changes are affected by added calcite. Hydrogarnet, C 3 AH 6 , is destabilised at low carbonate contents and/or low temperatures 3 -ettringite. A nomenclature scheme is proposed and AFm-AFt phase relations are presented in isothermal sections at 5, 25 and 40 deg. C. The AFt and AFm phase relations are depicted in terms of competition between OH, CO 3 and SO 4 for anion sites. Diagrams are presented showing how changing temperatures affect the volume of the solid phases with implications for space filling by the paste. Specimen calculations are related to regimes likely to occur in commercial cements and suggestions are made for testing thermal impacts on cement properties by defining four regimes. It is concluded that calculation provides a rapid and effective tool for exploring the response of cement systems to changing composition and temperature and to optimise cement performance.

  15. Natural cement and stone restoration of Bourges Cathedral (France

    Directory of Open Access Journals (Sweden)

    C. Gosselin

    2008-01-01

    Full Text Available Natural cement, also called "Roman cement", was invented at the end of the 18th Century and played an important role in the development of civil engineering works until the 1860s. More surprisingly, it was also used to restore historic buildings, such as gothic cathedrals. This paper deals with the mineralogy and the durability of natural cement, in the particular case of the Bourges Cathedral in France. This study illustrates the interest of this material particularly adapted in stone repair or substitution. Contrary to traditional mortars, the present samples are made of neat cement paste, revealed by the absence of mineral additions as quartz or carbonate sand. Several combined techniques (SEM-EDS, TGA, XRD were carried out to determine the composition of the hydraulic binder rich in calcium aluminate hydrates. The raw marl at the origin of the cement production contains oxidized pyrites which consist in a potential source of sulphate pollution of the surrounding limestone. The exposition of the cement in urban environment leads to some weathering features as atmospheric sulphation. Finally a petrophysical approach, based on water porosity, capillary sorption and compressive strength, has been performed to demonstrate the durability and the compatibility of roman cement applied as a restoration mortar of historical building.

  16. Self-Shrinkage Behaviors of Waste Paper Fiber Reinforced Cement Paste considering Its Self-Curing Effect at Early-Ages

    Directory of Open Access Journals (Sweden)

    Zhengwu Jiang

    2016-01-01

    Full Text Available The aim of this paper was to study how the early-age self-shrinkage behavior of cement paste is affected by the addition of the waste paper fibers under sealed conditions. Although the primary focus was to determine whether the waste paper fibers are suitable to mitigate self-shrinkage as an internal curing agent under different adding ways, evaluating their strength, pore structure, and hydration properties provided further insight into the self-cured behavior of cement paste. Under the wet mixing condition, the waste paper fibers could mitigate the self-shrinkage of cement paste and, at additions of 0.2% by mass of cement, the waste paper fibers were found to show significant self-shrinkage cracking control while providing some internal curing. In addition, the self-curing efficiency results were analyzed based on the strength and the self-shrinkage behaviors of cement paste. Results indicated that, under a low water cement ratio, an optimal dosage and adding ways of the waste paper fibers could enhance the self-curing efficiency of cement paste.

  17. Assessment the potential of using Carbon nanotubes reinforcements for improving the tensile/flexural strength and fracture toughness of Portland cement paste for damage resistant concrete transportation infrastructures.

    Science.gov (United States)

    2010-09-01

    The focus of this study was on exploring the use of nanotechnology-based nano-filaments, such as carbon : nanotubes (CNTs) and nanofibers (CNFs), as reinforcement in improving the mechanical properties of Portland : cement paste as a construction mat...

  18. Effect of Pigment Colouring on Physico-mechanical Properties of Hardened Cement Paste and Response of Colour Intensity to UV Radiation

    International Nuclear Information System (INIS)

    Khattab, M.M.; Abdel-Rahman, H.A.; Hassan, M.S.

    2010-01-01

    In this work, different ratios of pigment colour was mixed with cement paste during mixing. The pigment colour used was Phthalocyanine Green. The effect of pigment colouring on hardened cement paste (HCP) was characterized in terms of compressive strength, IR spectroscopic analysis and X-ray diffraction. In addition, the effect of UV radiation on the colour strength of hardened cement paste/pigment colour composites was investigated. The results indicated that the increase in the ratio of pigment colour was accompanied with a slight decrease in the values of compressive strength. The exposure of the coloured hardened cement paste to UV radiation for long lengths of time causes a little effect on the colour intensity

  19. Sulfate and acid resistant concrete and mortar

    Science.gov (United States)

    Liskowitz, John W.; Wecharatana, Methi; Jaturapitakkul, Chai; Cerkanowicz, deceased, Anthony E.

    1998-01-01

    The present invention relates to concrete, mortar and other hardenable mixtures comprising cement and fly ash for use in construction and other applications, which hardenable mixtures demonstrate significant levels of acid and sulfate resistance while maintaining acceptable compressive strength properties. The acid and sulfate hardenable mixtures of the invention containing fly ash comprise cementitious materials and a fine aggregate. The cementitous materials may comprise fly ash as well as cement. The fine aggregate may comprise fly ash as well as sand. The total amount of fly ash in the hardenable mixture ranges from about 60% to about 120% of the total amount of cement, by weight, whether the fly ash is included as a cementious material, fine aggregate, or an additive, or any combination of the foregoing. In specific examples, mortar containing 50% fly ash and 50% cement in cementitious materials demonstrated superior properties of corrosion resistance.

  20. A numerical-statistical approach to determining the representative elementary volume (REV of cement paste for measuring diffusivity

    Directory of Open Access Journals (Sweden)

    Zhang, M. Z.

    2010-12-01

    Full Text Available Concrete diffusivity is a function of its microstructure on many scales, ranging from nanometres to millimetres. Multi-scale techniques are therefore needed to model this parameter. Representative elementary volume (REV, in conjunction with the homogenization principle, is one of the most common multi-scale approaches. This study aimed to establish a procedure for establishing the REV required to determine cement paste diffusivity based on a three-step, numerical-statistical approach. First, several series of 3D cement paste microstructures were generated with HYMOSTRUC3D, a cement hydration and microstructure model, for different volumes of cement paste and w/c ratios ranging from 0.30 to 0.60. Second, the finite element method was used to simulate the diffusion of tritiated water through these microstructures. Effective cement paste diffusivity values for different REVs were obtained by applying Fick’s law. Finally, statistical analysis was used to find the fluctuation in effective diffusivity with cement paste volume, from which the REV was then determined. The conclusion drawn was that the REV for measuring diffusivity in cement paste is 100x100x100 μm3.

    La difusividad del hormigón depende de su microestructura a numerosas escalas, desde nanómetros hasta milímetros, por lo que se precisa de técnicas multiescala para representar este parámetro. Junto con el principio de homogeneización, uno de los métodos multiescala más habituales es el volumen elemental representativo (VER. El objeto de este estudio era establecer un procedimiento que permitiera determinar el VER necesario para calcular la difusividad de la pasta de cemento, basándose en un método numéricoestadístico que consta de tres etapas. Primero, se crearon varias series de microestructuras de pasta de cemento en 3D con HYMOSTRUC3D, un programa que permite crear un modelo de la hidratación y microestructura del cemento. Luego se empleó el método de

  1. On the mechanism of polypropylene fibres in preventing fire spalling in self-compacting and high-performance cement paste

    International Nuclear Information System (INIS)

    Liu, X.; Ye, G.; De Schutter, G.; Yuan, Y.; Taerwe, L.

    2008-01-01

    With the increasing application of self-compacting concrete (SCC) in construction and infrastructure, the fire spalling behavior of SCC has been attracting due attention. In high performance concrete (HPC), addition of polypropylene fibers (PP fibers) is widely used as an effective method to prevent explosive spalling. Hence, it would be useful to investigate whether the PP fibers are also efficient in SCC to avoid explosive spalling. However, no universal agreement exists concerning the fundamental mechanism of reducing the spalling risk by adding PP fiber. For SCC, the reduction of flowability should be considered when adding a significant amount of fibres. In this investigation, both the micro-level and macro-level properties of pastes with different fiber contents were studied in order to investigate the role of PP fiber at elevated temperature in self-compacting cement paste samples. The micro properties were studied by backscattering electron microscopy (BSE) and mercury intrusion porosimetry (MIP) tests. The modification of the pore structure at elevated temperature was investigated as well as the morphology of the PP fibers. Some macro properties were measured, such as the gas permeability of self-compacting cement paste after heating at different temperatures. The factors influencing gas permeability were analyzed. It is shown that with the melting of PP fiber, no significant increase in total pore volume is obtained. However, the connectivity of isolated pores increases, leading to an increase of gas permeability. With the increase of temperature, the addition of PP fibers reduces the damage of cement pastes, as seen from the total pore volume and the threshold pore diameter changes. From this investigation, it is concluded that the connectivity of pores as well as the creation of micro cracks are the major factors which determine the gas permeability after exposure to high temperatures. Furthermore, the connectivity of the pores acts as a dominant factor

  2. Mortar fights acid corrosion

    Energy Technology Data Exchange (ETDEWEB)

    1982-05-14

    The burning of coal or oil to produce heat required to operate a power boiler also generates a severe corrosion problem within the interior of the duct and stacks used to emit the flue gas into the atmosphere. How can concrete and steel be protected from the effects of acid attack, when the acids are carried in a gas form, or come into direct contact with the steel or concrete from spillage or immersion conditions. Industry in North America has found that the solution to this problem is to build an outside concrete column, in this case of Portland cement, and inside that column, build a totally independent brick liner bonded with Sauereisen mortar.

  3. Steel corrosion resistance in model solutions and reinforced mortar containing wastes

    NARCIS (Netherlands)

    Koleva, D.A.; Van Breugel, K.

    2012-01-01

    This work reports on the corrosion resistance of steel in alkaline model solutions and in cement-based materials (mortar). The model solutions and the mortar specimens were Ordinary Portland Cement (OPC) based. Further, hereby discussed is the implementation of an eco-friendly approach of waste

  4. Physical and chemical characterization of pastes of bone cements with ZrO2

    International Nuclear Information System (INIS)

    Quinto H, A.; Pina B, M.C.

    2003-01-01

    Setting times and temperature of sixteen calcium phosphate cements added with ZrO 2 were evaluated. Their behaviors were analysed to be used like injectable formulations in surgery of bone. Two cements of calcium phosphates enriched with ZrO 2 with the best characteristics in setting times and temperature, were mechanically tested after 1 and 7 days of prepared. Density was determined using a pycnometer, chemical composition was determined by X-ray diffraction and the molecular structure was determined by infrared spectroscopy. (Author)

  5. The Impact of Additive on the Properties of Fresh and Hardened Mortar

    Directory of Open Access Journals (Sweden)

    Jurga Šeputytė

    2012-11-01

    Full Text Available This paper considers the impact of additives on the properties of mortar. For investigation purposes, two types of Portland cement (CEM II/A-LL 42.5 N and CEM I N (MA, fine aggregate sand, lime, water and air-entraining and stabilizing additives were used. To determine the effects of additives on the mortar mix, the analysis of cone penetration into the mix, mortar mobility, water extraction out of mortar, density and flexural and compressive testing were conducted. When put into mortar, air-entraining and stabilizing additives changed structure. In this case, density and flexural and compressive strength of mortar are reduced.

  6. The Aesthetical quality of SSA-containing mortar and concrete

    DEFF Research Database (Denmark)

    Kappel, Annemette; Kirkelund, Gunvor Marie; Ottosen, Lisbeth M.

    2014-01-01

    that gives a characteristic red colour. The process of grinding SSA has shown to improve the compressive strength of SSA- containing mortar (Donatello et al. 2010). Thus, in this study SSA was grinded in 6 different intervals ranging from 0 – 10 min, and then added to the mortar mix replacing 20% of cement....... The experiment revealed that the colour of the SSA-containing mortar intensified as the time interval of the grinding process increased. Each of the 6 steps within the time interval provided an additional colour tone and generated a colour scale consisting of mortar samples ranging from greyish to a more...

  7. Influence of chemical composition of civil construction waste in the cement paste; Influencia da composicao quimica dos residuos da construcao civil a pasta de cimento

    Energy Technology Data Exchange (ETDEWEB)

    Cunha, G.A.; Andrade, A.C.D.; Souza, J.M.M.; Evangelista, A.C.J.; Almeida, V.C., E-mail: valeria@eq.ufrj.b [Universidade Federal do Rio de Janeiro (EQ/UFRJ), RJ (Brazil). Escola de Quimica

    2009-07-01

    The construction and demolition waste when disposed inappropriately might cause serious public health problems. Its reutilization focusing on the development of new products using simple production techniques, assuring a new product life cycle and not damaging the environment is inserted in sustainable concept. The aim of this work was identifying the characteristics of types of waste generated in a residential reform (glassy ceramic and fill dirt leftovers) verifying separately its influence on cement pastes mechanical behavior. Cement pastes + wastes were prepared in 25% and 50% proportions with an approximately 0,35 water/cement relation and, glue time determination, water absorption, resistance to compression and X-ray fluorescence assays were taken. The results indicate that the chemical composition of the waste causes changes in the behavior of cement pastes, reflecting on their resistance to compression. (author)

  8. Revealing the dark side of Portlandite Clusters in cement paste by circular polarization microscopy

    NARCIS (Netherlands)

    Copuroglu, O.

    2016-01-01

    Plane and crossed polarization are the two standard light modes in polarized light microscopy that are widely used to characterize crystalline and amorphous phases in cement-based materials. However, the use of the crossed polarized light mode has been found to be restrictive for studying

  9. Tensile strength of hydrated cement paste phases assessed by microbending tests and nanoindentation

    Czech Academy of Sciences Publication Activity Database

    Němeček, J.; Králík, V.; Šmilauer, V.; Polívka, Leoš; Jäger, Aleš

    2016-01-01

    Roč. 73, Oct (2016), 164-173 ISSN 0958-9465 R&D Projects: GA ČR GBP108/12/G043 Institutional support: RVO:68378271 Keywords : cement * hydration products * micro-beam * tensile strength * fracture energy * nanoindentation * focused ion beam Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 4.265, year: 2016

  10. Drilling mortar

    Energy Technology Data Exchange (ETDEWEB)

    Theodorescu, V; Ditulescu, E

    1979-01-30

    A method is proposed for producing stable drilling mortar from drilled rock which makes it possible to stabilize the walls of the borehole and to maintain producing horizons of oil and gas wells in an undisturbed state. The proposed drilling mortar includes 5-12 wt.-% dry modified calcium lignosulfonate in the form of a solution containing about 30% dry matter with the addition of 0.1 wt.-% anti-foaming agent consisting of C/sub 19/-C/sub 20/ alcohol dissolved in a light petroleum product; cream of milk with about 10 wt.-% Ca(OH)/sub 2/ in a quantity sufficient for reducing the pH value of the ions down to 10.5; sodium chloride in amounts from 5 mg to 100 ml (aqueous phase); ordinarily used agents for ensuring the necessary density, viscosity, and filterability. For example, the preparation of the drilling fluid begins with the processing under laboratory conditions of lignosulfonic pulp obtained in the production of yeast fodder with the following characteristics: specific density, 1.15 kgf/dm/sup 3/; water content, 67% (according to the Dean and Stark method); pH 4.0. In the vessel is placed 1000 cm/sup 3/ lignosulfonic pulp containing 33% dry matter, and the pulp is heated to 90-95/sup 0/C by means of a water bath. To the heated pulp 33 cm/sup 3/ formic acid at a 40-% concentration is added by mixing. The specific temperature of the pulp is maintained in the constant mixing process for two hours. Then the cream of milk containing 10 wt.-% Ca(OH)/sub 2/ is added to raise the pH to 10.5. The cooled product is calcium lignosulfonate. To produce a stable form of the drilling mortar, 750 g clay and 10 g trass gel are added to a vessel containing 1500 cm/sup 3/ fresh water by means of mixing. The resulting dispersed mass remains at rest for 12 hours for purposes of hydration. Then 2 g of an anti-foaming agent dissolved in 6 cm/sup 3/ benzene is introduced to 1000 cm/sup 3/ modified calcium lignosulfonate produced by the above method.

  11. MORTAR WITH UNSERVICEABLE TIRE RESIDUES

    Directory of Open Access Journals (Sweden)

    J. A. Canova

    2009-01-01

    Full Text Available This study analyzes the effects of unserviceable tire residues on rendering mortar using lime and washed sand at a volumetric proportion of 1:6. The ripened composite was dried in an oven and combined with both cement at a volumetric proportion of 1:1.5:9 and rubber powder in proportional aggregate volumes of 6, 8, 10, and 12%. Water exudation was evaluated in the plastic state. Water absorption by capillarity, fresh shrinkage and mass loss, restrained shrinkage and mass loss, void content, flexural strength, and deformation energy under compression were evaluated in the hardened state. There was an improvement in the water exudation and water absorption by capillarity and drying shrinkage, as well as a reduction of the void content and flexural strength. The product studied significantly aided the water exudation from mortar and, capillary elevation in rendering.

  12. MORTAR WITH UNSERVICEABLE TIRE RESIDUES

    Directory of Open Access Journals (Sweden)

    José Aparecido Canova

    2009-12-01

    Full Text Available This study analyzes the effects of unserviceable tire residues on rendering mortar using lime and washed sand at a volumetric proportion of 1:6. The ripened composite was dried in an oven and combined with both cement at a volumetric proportion of 1:1.5:9 and rubber powder in proportional aggregate volumes of 6, 8, 10, and 12%. Water exudation was evaluated in the plastic state. Water absorption by capillarity, fresh shrinkage and mass loss, restrained shrinkage and mass loss, void content, flexural strength, and deformation energy under compression were evaluated in the hardened state. There was an improvement in the water exudation and water absorption by capillarity and drying shrinkage, as well as a reduction of the void content and flexural strength. The product studied significantly aided the water exudation from mortar and, capillary elevation in rendering.

  13. Development of low weight self-levelling mortars

    International Nuclear Information System (INIS)

    Padilla, A; Panama, I; Toledo, A; Flores, A

    2015-01-01

    This work shows the development of self levelling mortars, using micro bubbles based on aluminium silicate with a density of 0.25 g/cm 3 . Mortars formulations are composed by 8 different components in order to achieve properties balance between fresh and solid state. The mean objective is development light weight mortars with high fluidity and compression strength using micro bubbles and some additives. Formulations were designed employing Taguchi DOE of 8 variables and 3 states. Result analysis according to Taguchi method lets indentify the preponderant effect of each variable on the cited properties. Several formulations reached fluidity higher than 250%, with compression strength around 100 kg/cm 2 and a low volumetric weigh. Obtained volumetric weights are 20% less than commercial self levelling mortars weight. Finally some relations are presented such: as relation water/cement with fluidity, and micro bubble content versus mortars volumetric weight, and finally compression strength versus the volumetric weight of mortars

  14. Quantitative study on the effect of high-temperature curing at an early age on strength development of concrete. Experiment with mortar using moderate-heat portland cement

    International Nuclear Information System (INIS)

    Sugiyama, Hisashi; Chino, Shigeo

    1999-01-01

    The effect of high-temperature curing at an early age on the strength development of concrete using moderate-heat portland cement was quantitatively studied. High-temperature curing conditions were set so as to give systematic variations in the temperature-time factors. As a result, the integrated value of curing temperature during the period having a significant effect on the strength development was proposed as a parameter that expressed the degree of high-temperature curing. The effect of high-temperature curing on the strength development of concrete using moderate-heat portland cement could be exactly predicted with the integrated value of curing temperature during the period from 0 to 3 days. (author)

  15. Properties of backfilling material for solidifying miscellaneous waste using recycled cement from waste concrete

    International Nuclear Information System (INIS)

    Matsuda, Atsuo; Yamamoto, Kazuo; Konishi, Masao; Iwamoto, Yoshiaki; Yoshikane, Toru; Koie, Toshio; Nakashima, Yoshio.

    1997-01-01

    A large reduction of total radioactive waste is expected, if recycled cement from the waste concrete of decommissioned nuclear power plants would be able to be used the material for backfilling mortar among the miscellaneous waste. In this paper, we discuss the hydration, strength and consistency of recycled cement compared with normal portland cement. The strength of recycled cement mortar is lower than that of normal portland cement mortar on the same water to cement ratio. It is possible to obtain the required strength to reduce the water to cement ratio by using of high range water-reducing AE agent. According to reducing of water to cement ratio, the P-type funnel time of mortar increase with the increase of its viscosity. However, in new method of self-compactability for backfilling mortar, it became evident that there was no difference between the recycled cement and normal portland cement on the self-compactability. (author)

  16. The macro- and micro properties of cement pastes with silica-rich materials cured by wet-mixed steaming injection

    International Nuclear Information System (INIS)

    Wu, D.S.; Peng, Y.N.

    2003-01-01

    This research used cement pastes with a low water/blaine ratio (W/b=0.27). Rice husk ashes (RHA) burned at 700 and 850 deg. C, silica fume, silica sand (Ottawa standard sand), etc., were the added ingredients. Wet-mixed steam injection (WMSI) was at five different temperatures: 65, 80, 120, 150 and 180 deg. C. We investigated cement pastes with added silica-rich materials. For different WMSI temperatures and times, we explored the relations between compressive strength, hydration products, and pozzolanic reaction mechanism. From scanning electron microscopy (SEM) and EDS, we know that hydration products become very complicated, depending on the WMSI temperatures and times. It is difficult to determine the direct effects on the strength based on changes in the products. Experimental results, however, clearly showed that the compressive strength was worst for 80 deg. C and best for 180 deg. C. High-temperature WMSI is best with 4-h presteaming period and 8-h retention time. Curing in saturated limewater for 28 days did not increase the strength. The three types of silica-rich materials used in this research all participated in the reaction during high-temperature WMSI; they helped to increase the strength. Addition of Ottawa standard sand resulted in the best strength, followed by addition of RHA, while addition of silica fume was worse than the others. Specimens treated with high-temperature WMSI would swell slightly if they were placed in air. This was different from normal-temperature curing

  17. Recycle of fired phosphogypsum waste product as a cement replacement and its role on the hydration and strength development of pastes

    International Nuclear Information System (INIS)

    Tantawi, S.H.

    2005-01-01

    The effect of Partially up to fully substituted of treated phosphogypsum x(PG) for natural gypsum on the physico- mechanical as well as kinetic of hydration of ordinary Portland cement has been discussed . The results show that by increasing PG % the water to cement ratio decreased while the initial and final setting times increased So PG acts as a retarder and water reducer . The retardation effect may be attributed to formation of ettringite layer which formed on the surface of C3A of cement pastes . The chemically combined water, free lime content and bulk density increased with curing time and with PG content for all cement pastes up to 90 days due to increasing of the rate of hydration. The compressive strength increased by increasing of PG % due to formation of anhydrite , changes in major oxides content and reduction of impurities . X-Ray Diffraction, SEM and DTA of some samples have been studied

  18. Mortar and concrete based on calcium sulphate binders

    NARCIS (Netherlands)

    Bakker, J.J.F.; Brouwers, H.J.H.; Fischer, H.B

    2006-01-01

    In this study both hemi-hydrate and anhydrite are tested as calcium sulphate binders for structural mortar and concrete. The advantage of using calcium sulphates instead of cement as a binder is the fact that the production of calcium sulphate is more environmental friendly than that of cement. For

  19. Pore solution in alkali-activated slag cement pastes. Relation to the composition and structure of calcium silicate hydrate

    International Nuclear Information System (INIS)

    Puertas, F.; Fernandez-Jimenez, A.; Blanco-Varela, M.T.

    2004-01-01

    In this work, the relationship between the composition of pore solution in alkali-activated slag cement (AAS) pastes activated with different alkaline activator, and the composition and structure of the main reaction products, has been studied. Pore solution was extracted from hardened AAS pastes. The analysis of the liquids was performed through different techniques: Na, Mg and Al by atomic absorption (AA), Ca ions by ionic chromatography (IC) and Si by colorimetry; pH was also determined. The solid phases were analysed by XRD, FTIR, solid-state 29 Si and 27 Al NMR and BSE/EDX. The most significant changes in the ionic composition of the pore solution of the AAS pastes activated with waterglass take place between 3 and 24 h of reaction. These changes are due to the decrease of the Na content and mainly to the Si content. Results of 29 Si MAS NMR and FTIR confirm that the activation process takes place with more intensity after 3 h (although at this age, Q 2 units already exist). The pore solution of the AAS pastes activated with NaOH shows a different evolution to this of pastes activated with waterglass. The decrease of Na and Si contents progresses with time. The nature of the alkaline activator influences the structure and composition of the calcium silicate hydrate formed as a consequence of the alkaline activation of the slag. The characteristic of calcium silicate hydrate in AAS pastes activated with waterglass is characterised by a low structural order with a low Ca/Si ratio. Besides, in this paste, Q 3 units are detected. The calcium silicate hydrate formed in the pastes activated with NaOH has a higher structural order (higher crystallinity) and contains more Al in its structure and a higher Ca/Si ratio than those obtained with waterglass

  20. Immobilization of IFR salt wastes in mortar

    International Nuclear Information System (INIS)

    Fischer, D.F.; Johnson, T.R.

    1988-01-01

    Portland cement-base mortars are being considered for immobilizing chloride salt wastes produced by the fuel cycles of Integral Fast Reactors (IFR). The IFR is a sodium-cooled fast reactor with metal alloy fuels. It has a close-coupled fuel cycle in which fission products are separated from the actinides in an electrochemical cell operating at 500/degree/C. This cell has a liquid cadmium anode in which the fuels are dissolved and a liquid salt electrolyte. The salt will be a mixture of either lithium, potassium, and sodium chlorides or lithium, calcium, barium, and sodium chlorides. One method being considered for immobilizing the treated nontransuranic salt waste is to disperse the salt in a portland cement-base mortar that will be sealed in corrosion-resistant containers. For this application, the grout must be sufficiently fluid that it can be pumped into canister-molds where it will solidify into a strong, leach-resistant material. The set times must be longer than a few hours to allow sufficient time for processing, and the mortar must reach a reasonable compressive strength (/approximately/7 MPa) within three days to permit handling. Because fission product heating will be high, about 0.6 W/kg for a mortar containing 10% waste salt, the effects of elevated temperatures during curing and storage on mortar properties must be considered

  1. A preliminary study of the influence of ions in the pore solution of hardened cement pastes on the porosity determination by low temperature calorimetry

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Min, E-mail: miwu@byg.dtu.dk [Department of Civil Engineering, Technical University of Denmark, Building 118, 2800 Lyngby (Denmark); Johannesson, Björn [Department of Civil Engineering, Technical University of Denmark, Building 118, 2800 Lyngby (Denmark); Geiker, Mette [Department of Structural Engineering, Norwegian University of Science and Technology, Trondheim (Norway)

    2014-08-10

    Highlights: • Ionic concentrations in cement pore solution at freezing temperatures were simulated. • Effects of ions in determining pore sizes by low temperature calorimetry were studied. • Ions in cement pore solution affect the pore size determination to a limited extent. - Abstract: Thermodynamic modeling was used to predict the ionic concentrations in the pore solution of cement pastes at different temperatures during a freezing and melting measurement in low temperature calorimetry (LTC) studies. By using the predicted ionic concentrations, the temperature depressions caused by the ions presented in the pore solution were determined. The influence of the freezing/melting point depression caused by the ions on the determined pore size distribution by LTC was demonstrated. Thermodynamic modeling using the program PHREEQC was performed on the cylinder and powder samples of cement pastes prepared by two types of cements, i.e., CEM I 32.5 R and CEM III/B 42.5 N. Using the modeled ionic concentrations, the calculated differential pore size distributions for the studied samples with and without considering the temperature depression caused by the ions in the pore solution were compared. The results indicate that for the studied cement paste samples, the influence of the temperature depression caused by the presence of the ions in the pore solution on the determination of the pore size distribution by LTC is limited.

  2. A preliminary study of the influence of ions in the pore solution of hardened cement pastes on the porosity determination by low temperature calorimetry

    International Nuclear Information System (INIS)

    Wu, Min; Johannesson, Björn; Geiker, Mette

    2014-01-01

    Highlights: • Ionic concentrations in cement pore solution at freezing temperatures were simulated. • Effects of ions in determining pore sizes by low temperature calorimetry were studied. • Ions in cement pore solution affect the pore size determination to a limited extent. - Abstract: Thermodynamic modeling was used to predict the ionic concentrations in the pore solution of cement pastes at different temperatures during a freezing and melting measurement in low temperature calorimetry (LTC) studies. By using the predicted ionic concentrations, the temperature depressions caused by the ions presented in the pore solution were determined. The influence of the freezing/melting point depression caused by the ions on the determined pore size distribution by LTC was demonstrated. Thermodynamic modeling using the program PHREEQC was performed on the cylinder and powder samples of cement pastes prepared by two types of cements, i.e., CEM I 32.5 R and CEM III/B 42.5 N. Using the modeled ionic concentrations, the calculated differential pore size distributions for the studied samples with and without considering the temperature depression caused by the ions in the pore solution were compared. The results indicate that for the studied cement paste samples, the influence of the temperature depression caused by the presence of the ions in the pore solution on the determination of the pore size distribution by LTC is limited

  3. Diffusion behavior of anion in hardened low-heat portland cement paste containing fly ash. Dependence of effective diffusion coefficient on pore structure

    International Nuclear Information System (INIS)

    Chida, Taiji; Yoshida, Takahiro

    2012-01-01

    In the sub-surface disposal system, the closely packed concrete layer is expected the low diffusivity to retard the migration of radionuclides. Low-heat portland cement containing 30 wt% fly ash (FAC) is a candidate cement material for the construction of sub-surface repository because of its high dense structure and its resistance to cracking. Previously, we reported that FAC has lower diffusivity than Ordinary Portland Cement (OPC) for acetic acid and iodine. However, the mechanism for low diffusivity of FAC was not clear. In this study, the diffusion of multiple trace ions (chlorine, bromine and iodine) in hardened cement pastes was examined by through-diffusion experiments. The effective diffusion coefficients, D e , of the trace ions for hardened OPC cement pastes were on the order of 10 -12 m 2 s -1 for trace ions, and D e for hardened FAC cement pastes were on the order of 10 -13 m 2 s -1 for chlorine, 10 -14 m 2 s -1 for bromine and 10 -15 m 2 s -1 for iodine. Additionally, the pore size distribution and porosity of FAC changed to more closely packed structure for 13 months by the pozzolanic reaction, and the pore size distribution of FAC (mainly 3-10 nm) were an order of magnitude smaller than that of OPC. These results suggest that the low diffusivity of FAC is based on the continuous change in the pore structure and the nano-scale pore size retarding the migration of trace ions. (author)

  4. Rheology and zeta potential of cement pastes containing calcined silt and ground granulated blast-furnace slag

    Directory of Open Access Journals (Sweden)

    Safi, B.

    2011-09-01

    Full Text Available This study aimed to analyse the re-use of dam silt as a supplementary binder for self-compacting concrete (SCC. When burnt, silt becomes more reactive because the kaolin it contains is converted into metakaolin. Portland cement, calcined or burnt silt and ground granulated blast furnace slag were used in this research. Cement pastes were prepared with blends containing two or three of these materials. The replacement ratio for burnt silt in both cases was 10 % and 20 % by cement weight and the ratio for the slag was a constant 30 % by weight of the blend. Rheological and zeta potential tests were conducted to evaluate paste electrokinetics and rheological behaviour. The findings showed that burnt silt is apt for use as an addition to cement for SCC manufacture.

    En el presente trabajo se ha analizado la posibilidad de utilizar los lodos procedentes de embalses como adición en la fabricación del hormigón autocompactante (HAC. Con la calcinación, estos materiales se vuelven más reactivos debido a la transformación en metacaolín, del caolín que forma parte de su composición. Las materias primas empleadas en esta investigación son: cemento Pórtland, lodos de embalse calcinados y escorias granuladas de horno alto. Se prepararon pastas de cemento con mezclas que contenían dos o tres de estos materiales. El porcentaje de reemplazo de los lodos calcinados osciló entre el 10 y el 20 % en peso del cemento, mientras que el de la escoria fue del 30 % en peso de la mezcla. Se llevaron a cabo ensayos reológicos y de potencial zeta para evaluar el comportamiento electrocinético y reológico de las distintas pastas. De acuerdo con los resultados obtenidos, una vez calcinados, los lodos de embalse son aprovechables como adición al cemento con destino a la preparación de HAC.

  5. Ultrafine portland cement performance

    Directory of Open Access Journals (Sweden)

    C. Argiz

    2018-04-01

    Full Text Available By mixing several binder materials and additions with different degrees of fineness, the packing density of the final product may be improved. In this work, ultrafine cement and silica fume mixes were studied to optimize the properties of cement-based materials. This research was performed in mortars made of two types of cement (ultrafine Portland cement and common Portland cement and two types of silica fume with different particle-size distributions. Two Portland cement replacement ratios of 4% and 10% of silica fume were selected and added by means of a mechanical blending method. The results revealed that the effect of the finer silica fume mixed with the coarse cement enhances the mechanical properties and pore structure refinement at a later age. This improvement is somewhat lower in the case of ultrafine cement with silica fume.

  6. Mineral resource of the month: hydraulic cement

    Science.gov (United States)

    van Oss, Hendrik G.

    2012-01-01

    Hydraulic cements are the binders in concrete and most mortars and stuccos. Concrete, particularly the reinforced variety, is the most versatile of all construction materials, and most of the hydraulic cement produced worldwide is portland cement or similar cements that have portland cement as a basis, such as blended cements and masonry cements. Cement typically makes up less than 15 percent of the concrete mix; most of the rest is aggregates. Not counting the weight of reinforcing media, 1 ton of cement will typically yield about 8 tons of concrete.

  7. A pulsed field gradient and NMR imaging investigations of the water retention mechanism by cellulose ethers in mortars

    International Nuclear Information System (INIS)

    Patural, Laetitia; Porion, Patrice; Van Damme, Henri; Govin, Alexandre; Grosseau, Philippe; Ruot, Bertrand; Deves, Olivier

    2010-01-01

    The study presented in this paper is devoted to improve the knowledge on the influence of cellulose ethers (CE) on the freshly-mixed mortars water retention. Indeed, this crucial property is the most important imparted by these polysaccharides. One of the assumptions proposed to explain this phenomenon is that CE acts as diffusion barrier to the water. To test this hypothesis, the CE effect on the self-diffusion coefficient of water in solution and on the water mobility between two fresh cement pastes was studied by Nuclear Magnetic Resonance. CE does not significantly modify the water self-diffusion coefficient in CE solution or in admixed cement pastes. Moreover the interdiffusion imaging experiments demonstrated that the water diffusion at the paste/paste interface is not affected by the presence of cellulosic admixture.

  8. Interactions between hydrated cement paste and organic acids: Thermodynamic data and speciation modeling

    Energy Technology Data Exchange (ETDEWEB)

    De Windt, Laurent, E-mail: laurent.dewindt@mines-paristech.fr [MINES ParisTech, PSL Research University, Centre de Géosciences, 35 Rue St-Honoré, 77305 Fontainebleau Cedex (France); Bertron, Alexandra; Larreur-Cayol, Steeves; Escadeillas, Gilles [University of Toulouse, UPS/INSA/LMDC, 135 Av. de Rangueil, 31077 Toulouse Cedex 04 (France)

    2015-03-15

    Interactions of short-chain organic acids with hydrated cement phases affect structure durability in the agro-food and nuclear waste industries but can also be used to modify cement properties. Most previous studies have been experimental, performed at fixed concentrations and pH, without quantitatively discriminating among polyacidity effects, or complexation and salt precipitation processes. This paper addresses such issues by thermodynamic equilibrium calculations for acetic, citric, oxalic, succinic acids and a simplified hydrated CEM-I. The thermodynamic constants collected from the literature allow the speciation to be modeled over a wide range of pH and concentrations. Citric and oxalic had a stronger chelating effect than acetic acid, while succinic acid was intermediate. Similarly, Ca-citrate and Ca-oxalate salts were more insoluble than Ca-acetate and Ca-succinate salts. Regarding aluminium complexation, hydroxyls, sulfates, and acid competition was highlighted. The exploration of acid mixtures showed the preponderant effect of oxalate and citrate over acetate and succinate.

  9. Leaching Behavior of Heavy Metals from Cement Pastes Using a Modified Toxicity Characteristic Leaching Procedure (TCLP).

    Science.gov (United States)

    Huang, Minrui; Feng, Huajun; Shen, Dongsheng; Li, Na; Chen, Yingqiang; Shentu, Jiali

    2016-03-01

    As the standard toxicity characteristic leaching procedure (TCLP) can not exhaust the acid neutralizing capacity of the cement rotary kiln co-processing solid wastes products which is particularly important for the assessment of the leaching concentrations of heavy metals. A modified TCLP was proposed. The extent of leaching of heavy metals is low using the TCLP and the leaching performance of the different metals can not be differentiated. Using the modified TCLP, however, Zn leaching was negligible during the first 180 h and then sharply increased (2.86 ± 0.18 to 3.54 ± 0.26 mg/L) as the acidity increased (pH leaching is enhanced using the modified TCLP. While Pb leached readily during the first 126 h and then leachate concentrations decreased to below the analytical detection limit. To conclude, this modified TCLP is a more suitable method for these cement rotary kiln co-processing products.

  10. Recycled sand in lime-based mortars.

    Science.gov (United States)

    Stefanidou, M; Anastasiou, E; Georgiadis Filikas, K

    2014-12-01

    The increasing awareness of the society about safe guarding heritage buildings and at the same time protecting the environment promotes strategies of combining principles of restoration with environmentally friendly materials and techniques. Along these lines, an experimental program was carried out in order to investigate the possibility of producing repair, lime-based mortars used in historic buildings incorporating secondary materials. The alternative material tested was recycled fine aggregates originating from mixed construction and demolition waste. Extensive tests on the raw materials have been performed and mortar mixtures were produced using different binding systems with natural, standard and recycled sand in order to compare their mechanical, physical and microstructure properties. The study reveals the improved behavior of lime mortars, even at early ages, due to the reaction of lime with the Al and Si constituents of the fine recycled sand. The role of the recycled sand was more beneficial in lime mortars rather than the lime-pozzolan or lime-pozzolan-cement mortars as a decrease in their performance was recorded in the latter cases due to the mortars' structure. Copyright © 2014 Elsevier Ltd. All rights reserved.

  11. Effect of temperature on structural quality of the cement paste and high-strength concrete with silica fume

    International Nuclear Information System (INIS)

    Janotka, Ivan; Nuernbergerova, Terezia

    2005-01-01

    Experimental investigation conducted to study the thermo-mechanical properties of concrete at Temelin (Czech Republic), Mochovce (Slovakia), and Penly (France) nuclear power plants reveals structural integrity degradation between 100 and 200 deg C due to both a loss of water bound in hydrated cement minerals and subsequently air void formation. Test results indicate changes in strength, average pore radius and calculated permeability coefficients for Mochovce specimens exposed to temperatures up to 400 deg C. It demonstrates that the permeability coefficient measured on the basis of pore sizes using mercury intrusion porosimetry is suitable technique for the evaluation of concrete quality. It confirms that strength and permeability coefficient are equivalent structural quality variables of concrete. At 400 deg C gel-like hydration products are decomposed, at 600 deg C Ca(OH) 2 is dehydroxylated, and CaCO 3 dissociation to CaO and CO 2 accompanied with the re-crystallisation of non-binding phases from hydrated cement under re-combustion are dominant processes between 600 and 800 deg C. This stage of concrete is characterised by the collapse of its structural integrity, revealing residual compressive strength. This paper reports high-strength concrete behaviour subjected to temperatures up to 200 deg C. In accordance with previous results, research studies of structure-property relation show the changes in strength, dynamic modulus of elasticity, strain-stress behaviour, and shrinkage-induced deformations influenced by a hydrate phase decomposition. Volume reduction of the hydrate phase due to the loss of bound water mass is the cause of air void formation, and pore structure coarsening. The main attention is herein devoted to the evaluation of utility property decrease of high-strength concrete and microstructure degradation of the cement paste with the same composition than that in concrete when attacked by elevated temperatures

  12. Characterization of different types of ceramic waste and its incorporation to the cement paste; Caracterizaco de diferentes tipos de residuos ceramicos e sua incorporacao a pasta de cimento

    Energy Technology Data Exchange (ETDEWEB)

    Cunha, G.A.; Evangelista, A.C.J.; Almeida, V.C. de, E-mail: valeria@eq.ufrj.b [Universidade Federal do Rio de Janeiro (EQ/UFRJ), RJ (Brazil). Escola de Quimica

    2009-07-01

    The porcelain tike is a product resulting from the technological development of ceramic plating industry. Its large acceptation by the consumer market is probably linked with certain properties, such as low porosity, high mechanical resistance, facility in maintenance, besides being a material of modern and versatile characteristics. The aim of this work was characterizing the different ceramic wastes (enameled and porcelain tike) and evaluating its influence on the mechanical behavior in cement pastes. The wastes were characterized through the determination of its chemical composition, size particle distribution and X-ray diffraction. Cement pastes + wastes were prepared in 25% and 50% proportions and glue time determination, water absorption and resistance to compression assays were taken. The results indicate that although the wastes don't show any variation in the elementary chemical composition, changes in the cement paste behavior related to the values of resistance to compression were observed. (author)

  13. Effect of uniaxially pressing ordinary Portland cement pastes containing metal hydroxides on porosity, density, and leaching

    International Nuclear Information System (INIS)

    Cheeseman, C.R.; Asavapisit, S.; Knight, J.

    1998-01-01

    Synthetic metal hydroxide wastes containing Zn and Pb have been mixed with partially hydrated cement and uniaxially pressed. The effect on porosity, pore size distribution, and bulk and skeletal densities has been characterized using mercury intrusion porosimetry. Ca(OH) 2 formation has been determined using differential thermal analysis and metal leaching has been assessed in a series of static leach tests completed on monolithic samples. Pressed solidified materials have increased density, reduced porosity, and reduced Ca(OH) 2 . They exhibit increased resistance to acid attack in terms of sample weight loss during leaching due to reduced release of alkalis. Leaching of Zn and Pb is primarily determined by pH. A peak observed in Zn leaching from pressed samples is due to the effect of changing leachate pH on the dominant Zn species present

  14. Diffusion and sorption on hardened cement pastes - experiments and modelling results

    Energy Technology Data Exchange (ETDEWEB)

    Jakob, A.; Sarott, F.-A.; Spieler, P.

    1999-08-01

    Large parts of repositories for low and intermediate level radioactive waste consist of cementitious materials. Radionuclides are transported by diffusion in the cement matrix or, in case of fractured or highly permeable cement, by advection and dispersion. In this work we aim at a mechanistic understanding of diffusion processes of some reactive tracers. On the laboratory scale, ten through-diffusion experiments were performed to study these processes for Cl{sup -}, I{sup -}, Cs{sup +} and Ni{sup 2+} ions in a Sulphate Resisting Portland Cement (SRPC) equilibrated with an artificial pore water. Some of the experiments continued up to nearly three years with daily measurements. In all the experiments, a cement disk initially saturated with an artificial pore water was exposed on one side to a highly diluted solution containing the species of interest. On the second side, a near-zero concentration boundary was maintained to drive through-diffusion of the tracer. The changes of concentrations on both sides of the samples were monitored, allowing careful mass balances. From these data, values of the diffusive flux and the mass of tracer taken up by the cementitious material were determined as a function of time. In the subsequent modelling, the time histories of these tracer breakthroughs were fitted using five different models. The simplest model neglects all retarding mechanisms except pure diffusion. More complex models either account for instantaneous equilibrium sorption in form of linear or non-linear (Freundlich) sorption or for first-order sorption kinetics where the forward reaction may be linear or non-linear according to the Freundlich isotherm, while the back-reaction is linear. Hence, the analysis allows the extraction of the diffusion coefficient and parameter values for the sorption isotherm or rate-constants for sorption and desorption. The fits to the experimental data were carried out by an automated Marquardt-Levenberg procedure yielding error

  15. Microstructure: Surface and cross-sectional studies of hydroxyapatite formation on the surface of white Portland cement paste in vitro

    International Nuclear Information System (INIS)

    Chaipanich, Arnon; Torkittikul, Pincha

    2011-01-01

    The formation of hydroxyapatite was investigated at the surface and at the cross-section of white Portland cement paste samples before and after immersion in simulated body fluid. Scanning electron microscope images showed that hydroxyapatite were found at the surface of white Portland cement after immersion in simulated body fluid. Hydroxyapatite grains of mostly ∼1 μm size with some grain size of ∼2-3 μm were seen after 4 days immersion period. More estabilshed hydroxyapatite grain size of ∼3 μm grains were observed at longer period of immersion at 7 and 10 days. The cross-section of the samples was investigated using line scanning technique and was used to determine the hydroxyapatite layer. A strong spectrum of phosphorus is detected up to 6-8 μm depth for samples after 4, 7 and 10 days immersion in simulated body fluid when compared to weak spectrum detected before immersion. The increase in the phosphorus spectrum corresponds to the hydroxyapatite formation on the surface of the samples after the samples were placed in simulated body fluid.

  16. Mortar alteration: experimental study and ancient analogues

    International Nuclear Information System (INIS)

    Rassineux, Francois

    1987-01-01

    As the durability of cemented matrices is a matter of great importance in numerous domains, notably for the long term reliability of surface storages of radioactive wastes, the objective of this research thesis is to define mechanisms of evolution of cemented matrices when in contact with diluted aqueous solutions. The author notably studied the influence of the lixiviation mode on the evolution of two mortars having different compositions (pH, CO 2 pressure, system containment, and cement mineralogical nature appear to be the main governing parameters), the alteration (dissolution is the prevailing process in the interaction between cemented matrices and a diluted solution such as rain water), and ancient binders (archaeological binders containing mineral phases such as hydrated calcium silicates or hydro-grossulars). The obtained results lead to the definition of alteration mechanisms in modern cements, and highlight factors governing the durability of these materials when submitted to meteoric alteration [fr

  17. The mechanism of cesium immobilization in densified silica-fume blended cement pastes

    International Nuclear Information System (INIS)

    Bar-Nes, G.; Katz, A.; Peled, Y.; Zeiri, Y.

    2008-01-01

    The role of silica-fume agglomerates, found in densified silica-fume (DSF) pastes, in the immobilization mechanism of Cs ions was studied. Samples of cementitious pastes containing two different forms of silica fume - DSF and raw silica fume (RSF) - were prepared. Leaching experiments showed that both additives reduced the leachability of the metal ion, but the effect of the DSF paste was much stronger. Scanning Electron Microscopy, together with Differential Thermal Analysis, proved that no agglomerated particles were present in the RSF pastes and that the extent of pozzolanic reactivity was higher. We therefore believe that unreacted silica within the DSF agglomerates adsorbs Cs ions and consequently increases their immobilization. Furthermore, this work suggests that during the pozzolanic reaction, a hydrated rim develops around the agglomerate that acts as an additional diffusion barrier for the Cs ions, resulting in an increased efficiency of Cs immobilization

  18. Durability of API class B cement pastes exposed to aqueous solutions containing chloride, sulphate and magnesium ions

    Directory of Open Access Journals (Sweden)

    Hernández, M. E.

    2008-12-01

    Full Text Available This paper discusses a durability study conducted on API class B cement, the type used in shallow oil wells, when exposed to aggressive formation water. Its resistance to the major ions, namely –SO4=, Mg+2 and Cl-–, is related both to its capacity to assimilate the aggressive action of each harmful agent and to the changes in the chemical reactivity of some of its components. The methodology used consisted in preparing and immersing cement specimens in neutral solutions containing variable concentrations of these ions to monitor the chemical reactions taking place. These solutions were analyzed and XRD studies were conducted for over a year to identify mineralogical variations. The purposes of the study were to determine the effects of joint ionic attack on this kind of cement and to monitor the variations in the calcium concentration