WorldWideScience

Sample records for cathode containment materials

  1. Cathode materials review

    Energy Technology Data Exchange (ETDEWEB)

    Daniel, Claus, E-mail: danielc@ornl.gov; Mohanty, Debasish, E-mail: danielc@ornl.gov; Li, Jianlin, E-mail: danielc@ornl.gov; Wood, David L., E-mail: danielc@ornl.gov [Oak Ridge National Laboratory, 1 Bethel Valley Road, MS6472 Oak Ridge, TN 37831-6472 (United States)

    2014-06-16

    The electrochemical potential of cathode materials defines the positive side of the terminal voltage of a battery. Traditionally, cathode materials are the energy-limiting or voltage-limiting electrode. One of the first electrochemical batteries, the voltaic pile invented by Alessandro Volta in 1800 (Phil. Trans. Roy. Soc. 90, 403-431) had a copper-zinc galvanic element with a terminal voltage of 0.76 V. Since then, the research community has increased capacity and voltage for primary (nonrechargeable) batteries and round-trip efficiency for secondary (rechargeable) batteries. Successful secondary batteries have been the lead-acid with a lead oxide cathode and a terminal voltage of 2.1 V and later the NiCd with a nickel(III) oxide-hydroxide cathode and a 1.2 V terminal voltage. The relatively low voltage of those aqueous systems and the low round-trip efficiency due to activation energies in the conversion reactions limited their use. In 1976, Wittingham (J. Electrochem. Soc., 123, 315) and Besenhard (J. Power Sources 1(3), 267) finally enabled highly reversible redox reactions by intercalation of lithium ions instead of by chemical conversion. In 1980, Goodenough and Mizushima (Mater. Res. Bull. 15, 783-789) demonstrated a high-energy and high-power LiCoO{sub 2} cathode, allowing for an increase of terminal voltage far beyond 3 V. Over the past four decades, the international research community has further developed cathode materials of many varieties. Current state-of-the-art cathodes demonstrate voltages beyond any known electrolyte stability window, bringing electrolyte research once again to the forefront of battery research.

  2. Cathode materials review

    International Nuclear Information System (INIS)

    Daniel, Claus; Mohanty, Debasish; Li, Jianlin; Wood, David L.

    2014-01-01

    The electrochemical potential of cathode materials defines the positive side of the terminal voltage of a battery. Traditionally, cathode materials are the energy-limiting or voltage-limiting electrode. One of the first electrochemical batteries, the voltaic pile invented by Alessandro Volta in 1800 (Phil. Trans. Roy. Soc. 90, 403-431) had a copper-zinc galvanic element with a terminal voltage of 0.76 V. Since then, the research community has increased capacity and voltage for primary (nonrechargeable) batteries and round-trip efficiency for secondary (rechargeable) batteries. Successful secondary batteries have been the lead-acid with a lead oxide cathode and a terminal voltage of 2.1 V and later the NiCd with a nickel(III) oxide-hydroxide cathode and a 1.2 V terminal voltage. The relatively low voltage of those aqueous systems and the low round-trip efficiency due to activation energies in the conversion reactions limited their use. In 1976, Wittingham (J. Electrochem. Soc., 123, 315) and Besenhard (J. Power Sources 1(3), 267) finally enabled highly reversible redox reactions by intercalation of lithium ions instead of by chemical conversion. In 1980, Goodenough and Mizushima (Mater. Res. Bull. 15, 783-789) demonstrated a high-energy and high-power LiCoO 2 cathode, allowing for an increase of terminal voltage far beyond 3 V. Over the past four decades, the international research community has further developed cathode materials of many varieties. Current state-of-the-art cathodes demonstrate voltages beyond any known electrolyte stability window, bringing electrolyte research once again to the forefront of battery research

  3. Cathode materials review

    Science.gov (United States)

    Daniel, Claus; Mohanty, Debasish; Li, Jianlin; Wood, David L.

    2014-06-01

    The electrochemical potential of cathode materials defines the positive side of the terminal voltage of a battery. Traditionally, cathode materials are the energy-limiting or voltage-limiting electrode. One of the first electrochemical batteries, the voltaic pile invented by Alessandro Volta in 1800 (Phil. Trans. Roy. Soc. 90, 403-431) had a copper-zinc galvanic element with a terminal voltage of 0.76 V. Since then, the research community has increased capacity and voltage for primary (nonrechargeable) batteries and round-trip efficiency for secondary (rechargeable) batteries. Successful secondary batteries have been the lead-acid with a lead oxide cathode and a terminal voltage of 2.1 V and later the NiCd with a nickel(III) oxide-hydroxide cathode and a 1.2 V terminal voltage. The relatively low voltage of those aqueous systems and the low round-trip efficiency due to activation energies in the conversion reactions limited their use. In 1976, Wittingham (J. Electrochem. Soc., 123, 315) and Besenhard (J. Power Sources 1(3), 267) finally enabled highly reversible redox reactions by intercalation of lithium ions instead of by chemical conversion. In 1980, Goodenough and Mizushima (Mater. Res. Bull. 15, 783-789) demonstrated a high-energy and high-power LiCoO2 cathode, allowing for an increase of terminal voltage far beyond 3 V. Over the past four decades, the international research community has further developed cathode materials of many varieties. Current state-of-the-art cathodes demonstrate voltages beyond any known electrolyte stability window, bringing electrolyte research once again to the forefront of battery research.

  4. Cathode material for lithium batteries

    Science.gov (United States)

    Park, Sang-Ho; Amine, Khalil

    2013-07-23

    A method of manufacture an article of a cathode (positive electrode) material for lithium batteries. The cathode material is a lithium molybdenum composite transition metal oxide material and is prepared by mixing in a solid state an intermediate molybdenum composite transition metal oxide and a lithium source. The mixture is thermally treated to obtain the lithium molybdenum composite transition metal oxide cathode material.

  5. Lithium containing manganese dioxide (composite dimensional manganese oxide-CDMO) as a cathod active material for lithium secondary batteries

    Energy Technology Data Exchange (ETDEWEB)

    Furukawa, Nobuhiro; Noma, Toshiyuki; Teraji, Kazuo; Nakane, Ikuo; Yamamoto, Yuji; Saito, Toshihiko (Sanyo Electric Co., Ltd., Osaka, Japan)

    1989-06-05

    Manganese dioxide containing lithium ions in a solid matrix was investigated in the lithium nonaqueous cell. Li/sub x/MnO/sub 2+{delta}/ material prepared, with the thermal treatment, by the solid state reaction of manganese dioxide and lithium hydroxide, 7 to 3 in molar ratio, at the temperature of 375{sup 0}C in air for 20 hours, exhibited the rechargeability in the lithium nonaqueous cell. A discharging and changing cycle test, 0.14 or 0.26e/Mn in each of both the discharge and charge, was also made, with the use of a flat type cell, to demonstrate it in performance. Synthetic Li/sub x/MnO/sub 2+{delta}/ was discussed, in advantageous use for the secondary lithium cell, based on the discharging and charging characteristics. As a conclusion of the foregoing, composite dimensional manganese oxide is expected to be good as active material of positive electrode for the secondary lithium cell use. 11 refs., 11 figs., 3 tabs.

  6. Cathode materials: A personal perspective

    Energy Technology Data Exchange (ETDEWEB)

    Goodenough, John B. [Texas Materials Institute, University of Texas at Austin, ETC 9.102, 1 University Station, Austin, TX 78712-1063 (United States)

    2007-12-06

    A thermodynamically stable rechargeable battery has a voltage limited by the window of the electrolyte. An aqueous electrolyte has a window of 1.2 eV, which prevents achieving the high energy density desired for many applications. A non-aqueous electrolyte with a window of 5 eV requires Li{sup +} rather than H{sup +} as the working ion. Early experiments with Li{sub x}TiS{sub 2} cathodes showed competitive capacity and rate capability, but problems with a lithium anode made the voltage of a safe cell based on a sulfide cathode too low to be competitive with a nickel/metal-hydride battery. Transition-metal oxides can give voltages of 4.5 V versus Li{sup +}/Li{sup 0}. However, the challenge with oxides has been to obtain a competitive capacity and rate capability while retaining a high voltage with low-cost, environmentally friendly cathode materials. Comparisons will be made between layered Li{sub 1-x}MO{sub 2}, spinels Li{sub 1-x}[M{sub 2}]O{sub 4}, and olivines Li{sub 1-x}MPO{sub 4} having 0 < x < 1. Although higher capacities can be obtained with layered Li{sub 1-x}MO{sub 2} compounds, which have enabled the wireless revolution, their metastability makes them unlikely to be used in power applications. The spinel and olivine framework structures have been shown to be capable of charge/discharge rates of over 10C with a suitable temperature range for plug-in hybrid vehicles. (author)

  7. Hydrothermal synthesis of cathode materials

    Science.gov (United States)

    Chen, Jiajun; Wang, Shijun; Whittingham, M. Stanley

    A number of cathodes are being considered for the next generation of lithium ion batteries to replace the expensive LiCoO 2 presently used. Besides the layered oxides, such as LiNi yMn yCo 1-2 yO 2, a leading candidate is lithium iron phosphate with the olivine structure. Although this material is inherently low cost, a manufacturing process that produces electrochemically active LiFePO 4 at a low cost is also required. Hydrothermal reactions are one such possibility. A number of pure phosphates have been prepared using this technique, including LiFePO 4, LiMnPO 4 and LiCoPO 4; this method has also successfully produced mixed metal phosphates, such as LiFe 0.33Mn 0.33Co 0.33PO 4. Ascorbic acid was found to be better than hydrazine or sugar at preventing the formation of ferric ions in aqueous media. When conductive carbons are added to the reaction medium excellent electrochemical behavior is observed.

  8. Synthesis and properties of novel TEMPO-contained polypyrrole derivatives as the cathode material of organic radical battery

    International Nuclear Information System (INIS)

    Xu, Lihuan; Yang, Fang; Su, Chang; Ji, Lvlv; Zhang, Cheng

    2014-01-01

    Two 2,2,6,6-tetramethylpiperidinyl-N-oxy (TEMPO) contained polypyrrole (PPy) derivatives with the different side-chain length were synthesized by esterification of 4-hydroxy-2,2,6,6-tetramethylpiperidine-1-oxyl free radial with pyrrole butyric acid and pyrrole caproic acid. Then the homopolymers of 4-(3-(Pyrrol-1-yl)butyryloxy)-2,2,6,6-tetramethylpiperidin-1-yloxy (PPy-B-TEMPO) and 4-(3-(Pyrrol-1-yl)hexanoyloxy)-2,2,6,6-tetramethylpiperidin-1-yloxy (PPy-C-TEMPO) were prepared by chemical oxidative polymerization. The structure, morphology, electrochemical properties of prepared polymers were characterized by fourier transform infrared spectroscopy (FTIR), ultraviolet visible spectroscopy (UV-vis), scanning electron microscopy (SEM), cyclic voltammograms (CV) and electrochemical impedance spectra (EIS), respectively. Also, the charge-discharge properties of the prepared polymers were studied by galvanostatic charge-discharge testing. The results demonstrated that the as-synthesized nitroxide radical polymers showed a reversible two-electron redox reaction process in the potential limits of 2.5–3.0 V and 3.4–3.8 V vs Li/Li + , respectively. Under our experimental conditions, PPy only presented the discharge capacity of 16.5 mAh·g −1 at 20 mA·g −1 between 2.5 and 4.2 V, while PPy-B-TEMPO with the short side-chain linked to TEMPO groups exhibited an initial discharge capacity of up to 86.5 mAh·g −1 with two well-defined plateaus. Furthermore, the PPy-C-TEMPO with the longer linking side-chain even displayed a discharge capacity of 115 mAh·g −1 . These superior electrochemical performances were ascribed to the flexible linking side-chain and the introduction of stable conductive PPy main chain, which benefits the improvement of charge carrier transportation in the aggregated polymer bulk

  9. A study on the recovery of TRU elements by a container-aided solid cathode

    International Nuclear Information System (INIS)

    Kwon, S.W.; Lee, J.H.; Woo, M.S.; Shim, J.B.; Kim, E.H.; Yoo, J.H.; Park, S.W.; Park, H.S.

    2005-01-01

    Pyroprocessing is a very prominent way for the recovery of the long-lived elements from the spent nuclear fuel. Electrorefining is a key technology of pyroprocessing and generally composed of two recovery steps - deposit of uranium onto a solid cathode and the recovery of TRU (TRansUranic) elements by a liquid cadmium cathode. The liquid cadmium cathode has some problems such as a cadmium volatilization problem, a low separation factor, and a complicates structure. In this study, CASC (Container-Aided Solid Cathode) was proposed as a candidate for replacing a liquid cadmium cathode and the deposition behavior of the cathode was examined during the electrorefining experiments. The CASC is a solid cathode surrounded with a porous ceramic container, where the container is used to capture the dripped deposit from the cathode. In the electrorefining experiment, the uranium used as a surrogate for the TRU elements, was effectively separated from cerium. The anode material and surface area were also investigated during electrolysis experiments for the more efficient electrorefining system. From the results of this study, it is concluded that the container-aided solid cathode can be a potential candidate for replacing a liquid cadmium cathode and the cathode should be developed further for the better electrolysis operation. (author)

  10. S-containing copolymer as cathode material in poly(ethylene oxide)-based all-solid-state Li-S batteries

    Science.gov (United States)

    Gracia, Ismael; Ben Youcef, Hicham; Judez, Xabier; Oteo, Uxue; Zhang, Heng; Li, Chunmei; Rodriguez-Martinez, Lide M.; Armand, Michel

    2018-06-01

    Inverse vulcanization copolymers (p(S-DVB)) from the radical polymerization of elemental sulfur and divinylbenzene (DVB) have been studied as cathode active materials in poly(ethylene oxide) (PEO)-based all-solid-state Li-S cells. The Li-S cell comprising the optimized p(S-DVB) cathode (80:20 w/w S/DVB ratio) and lithium bis(fluorosulfonyl)imide/PEO (LiFSI/PEO) electrolyte shows high specific capacity (ca. 800 mAh g-1) and high Coulombic efficiency for 50 cycles. Most importantly, polysulfide (PS) shuttle is highly mitigated due to the strong interactions of PS species with polymer backbone in p(S-DVB). This is demonstrated by the stable cycling of the p(S-DVB)-based cell using lithium bis(trifluoromethanesulfonyl)imide (LiTFSI)/PEO electrolyte, where successful charging cannot be achieved even at the first cycle with plain elemental S-based cathode material due to the severe PS shuttle phenomenon. These results suggest that inverse vulcanization copolymers are promising alternatives to elemental sulfur for enhancing the electrochemical performance of PEO-based all-solid-state Li-S cells.

  11. 2013 Estorm - Invited Paper - Cathode Materials Review

    Energy Technology Data Exchange (ETDEWEB)

    Daniel, Claus [ORNL; Mohanty, Debasish [ORNL; Li, Jianlin [ORNL; Wood III, David L [ORNL

    2014-01-01

    The electrochemical potential of cathode materials defines the positive side of the terminal voltage of a battery. Traditionally, cathode materials are the energy-limiting or voltage-limiting electrode. One of the first electrochemical batteries, the voltaic pile invented by Alessandro Volta in 1800 (Phil. Trans. Roy. Soc. 90, 403 431) had a copper-zinc galvanic element with a terminal voltage of 0.76 V. Since then, the research community has increased capacity and voltage for primary (nonrechargeable) batteries and round-trip efficiency for secondary (rechargeable) batteries. Successful secondary batteries have been the lead acid with a lead oxide cathode and a terminal voltage of 2.1 V and later the NiCd with a nickel(III) oxide hydroxide cathode and a 1.2 V terminal voltage. The relatively low voltage of those aqueous systems and the low round-trip efficiency due to activation energies in the conversion reactions limited their use. In 1976, Wittingham (J. Electrochem. Soc., 123, 315) and Besenhard (J Power Sources 1(3), 267) finally enabled highly reversible redox reactions by intercalation of lithium ions instead of by chemical conversion. In 1980, Goodenough and Mizushima (Mater. Res. Bull. 15, 783 789) demonstrated a high-energy and high-power LiCoO2 cathode, allowing for an increase of terminal voltage far beyond 3 V. Over the past four decades, the international research community has further developed cathode materials of many varieties. Current state-of-the-art cathodes demonstrate voltages beyond any known electrolyte stability window, bringing electrolyte research once again to the forefront of battery research.

  12. Material and Energy Flows in the Production of Cathode and Anode Materials for Lithium Ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Dunn, Jennifer B. [Argonne National Lab. (ANL), Argonne, IL (United States); James, Christine [Michigan State Univ., East Lansing, MI (United States); Gaines, Linda [Argonne National Lab. (ANL), Argonne, IL (United States); Gallagher, Kevin [Argonne National Lab. (ANL), Argonne, IL (United States); Dai, Qiang [Argonne National Lab. (ANL), Argonne, IL (United States); Kelly, Jarod C. [Argonne National Lab. (ANL), Argonne, IL (United States)

    2015-09-01

    The Greenhouse gases, Regulated Emissions and Energy use in Transportation (GREET) model has been expanded to include four new cathode materials that can be used in the analysis of battery-powered vehicles: lithium nickel cobalt manganese oxide (LiNi0.4Co0.2Mn0.4O2 [NMC]), lithium iron phosphate (LiFePO4 [LFP]), lithium cobalt oxide (LiCoO2 [LCO]), and an advanced lithium cathode (0.5Li2MnO3∙0.5LiNi0.44Co0.25Mn0.31O2 [LMR-NMC]). In GREET, these cathode materials are incorporated into batteries with graphite anodes. In the case of the LMR-NMC cathode, the anode is either graphite or a graphite-silicon blend. Lithium metal is also an emerging anode material. This report documents the material and energy flows of producing each of these cathode and anode materials from raw material extraction through the preparation stage. For some cathode materials, we considered solid state and hydrothermal preparation methods. Further, we used Argonne National Laboratory’s Battery Performance and Cost (BatPaC) model to determine battery composition (e.g., masses of cathode, anode, electrolyte, housing materials) when different cathode materials were used in the battery. Our analysis concluded that cobalt- and nickel-containing compounds are the most energy intensive to produce.

  13. Material and Energy Flows in the Production of Cathode and Anode Materials for Lithium Ion Batteries

    Energy Technology Data Exchange (ETDEWEB)

    Dunn, Jennifer B. [Argonne National Lab. (ANL), Argonne, IL (United States). Energy Systems Division; James, Christine [Michigan State Univ., East Lansing, MI (United States). Chemical Engineering and Materials Science Dept.; Gaines, Linda G. [Argonne National Lab. (ANL), Argonne, IL (United States). Energy Systems Division; Gallagher, Kevin [Argonne National Lab. (ANL), Argonne, IL (United States). Chemical Sciences and Engineering Division

    2014-09-30

    The Greenhouse gases, Regulated Emissions and Energy use in Transportation (GREET) model has been expanded to include four new cathode materials that can be used in the analysis of battery-powered vehicles: lithium nickel cobalt manganese oxide (LiNi0.4Co0.2Mn0.4O2 [NMC]), lithium iron phosphate (LiFePO4 [LFP]), lithium cobalt oxide (LiCoO2 [LCO]), and an advanced lithium cathode (0.5Li2MnO3∙0.5LiNi0.44Co0.25Mn0.31O2 [LMR-NMC]). In GREET, these cathode materials are incorporated into batteries with graphite anodes. In the case of the LMR-NMC cathode, the anode is either graphite or a graphite-silicon blend. This report documents the material and energy flows of producing each of these cathode and anode materials from raw material extraction through the preparation stage. For some cathode materials, we considered solid state and hydrothermal preparation methods. Further, we used Argonne National Laboratory’s Battery Performance and Cost (BatPaC) model to determine battery composition (e.g., masses of cathode, anode, electrolyte, housing materials) when different cathode materials were used in the battery. Our analysis concluded that cobalt- and nickel-containing compounds are the most energy intensive to produce.

  14. Li- and Mn-Rich Cathode Materials: Challenges to Commercialization

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming [Energy and Environmental Directorate, Pacific Northwest National Laboratory, 902 Battelle Boulevard Richland WA 99354 USA; Myeong, Seungjun [School of Energy and Chemical Engineering, Green Energy Materials Development Center, Ulsan National Institute of Science and Technology (UNIST), Korea 689-798; Cho, Woongrae [School of Energy and Chemical Engineering, Green Energy Materials Development Center, Ulsan National Institute of Science and Technology (UNIST), Korea 689-798; Yan, Pengfei [Environmental Molecular Sciences Laboratory, Pacific Northwest National Laboratory, 902 Battelle Boulevard Richland WA 99354 USA; Xiao, Jie [Energy and Environmental Directorate, Pacific Northwest National Laboratory, 902 Battelle Boulevard Richland WA 99354 USA; Wang, Chongmin [Environmental Molecular Sciences Laboratory, Pacific Northwest National Laboratory, 902 Battelle Boulevard Richland WA 99354 USA; Cho, Jaephil [School of Energy and Chemical Engineering, Green Energy Materials Development Center, Ulsan National Institute of Science and Technology (UNIST), Korea 689-798; Zhang, Ji-Guang [Energy and Environmental Directorate, Pacific Northwest National Laboratory, 902 Battelle Boulevard Richland WA 99354 USA

    2016-12-14

    The lithium- and manganese-rich (LMR) layered structure cathode exhibit one of the highest specific energy (~900 Wh kg-1) among all the cathode materials. However, the practical applications of LMR cathodes are still hindered by several significant challenges including voltage fade, large initial capacity loss, poor rate capability and limited cycle life. Herein, we review the recent progresses and understandings on the application of LMR cathode materials from practical point of view. Several key parameters of LMR cathodes that affect the LMR/graphite full cell operation are systematically analysed. These factors include the first cycle capacity loss, voltage fade, powder tap density, electrode density of LMR based cathode etc. New approaches to minimize the detrimental effect of these factors are highlighted in this work. We also provided the perspectives for the future research on LMR cathode materials, focusing on addressing the fundamental problems of LMR cathodes while always keeping practical considerations in mind.

  15. Properties of cathode materials in alkaline cells

    International Nuclear Information System (INIS)

    Salkind, A.J.; McBreen, J.; Freeman, R.; Parkhurst, W.A.

    1985-01-01

    Conventional and new cathode materials in primary and secondary alkaline cells were investigated for stability, structure, electrochemical reversibility and efficiency. Included were various forms of AgO for reserve-type silver-zinc batteries, a new material - AgNiO/sub 2/ - and several nickel electrodes for nickel-cadmium and nickel-hydrogen cells for aerospace applications. A comparative study was made of the stability of electroformed and chemically prepared AgO. Stability was correlated with impurities detected by XPS and SAM. After the first discharge AgNiO/sub 2/ can be recharged to the monovalent level. The discharge product is predominantly silver. Plastic-bonded nickel electrodes display a second plateau on discharge. Additions of Co(OH)/sub 2/ largely eliminate this

  16. Thermodynamic evaluation of liquid Cd cathode containing U and Pu

    International Nuclear Information System (INIS)

    Kurata, Masaki; Uozumi, Koichi; Kato, Tetsuya; Iizuka, Masatoshi

    2009-01-01

    In our previous study, a mixture of U and Pu was recovered in liquid Cd cathode from molten salt under various conditions of the U:Pu ratio. Two important things were observed. The first was that three kinds of precipitated phase had been detected in the saturated liquid Cd cathode, such as a U metal and two kinds of U-Pu-Cd compound. The compositions of the compounds were roughly (U+Pu):Cd=1:11 and (U+Pu):Cd=1:6. The second was that the U metal had selectively precipitated in the saturated liquid Cd cathode under the condition that the U:Pu ratio is higher than about 0.8 in the liquid Cd phase. In the present study, phase diagrams were evaluated by the CALPHAD method on the liquid Cd cathode containing U and Pu. The U-Pu-Cd compounds were modeled as MCd 11 -type and MCd 6 -type, respectively, based on the reported binary phase diagrams of U-Cd and Pu-Cd. The calculated result reasonably agreed with the experimental observations. The variations in the U and Pu activities were estimated along with the U:Pu ratio, which is related to the precipitation of various phases in the liquid Cd cathode. (author)

  17. Development of cathode material for lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    Rustam Mukhtaruly Turganaly

    2014-08-01

    Full Text Available The electrochemical characteristics of the cathode material coated with carbon layer has been developed. Various carbon coating methods. There  has been carried out a comparative electrochemical analysis of the coated and uncoated with carbon cathode material

  18. Iron phosphate materials as cathodes for lithium batteries

    CERN Document Server

    Prosini, Pier Paolo

    2011-01-01

    ""Iron Phosphate Materials as Cathodes for Lithium Batteries"" describes the synthesis and the chemical-physical characteristics of iron phosphates, and presents methods of making LiFePO4 a suitable cathode material for lithium-ion batteries. The author studies carbon's ability to increase conductivity and to decrease material grain size, as well as investigating the electrochemical behaviour of the materials obtained. ""Iron Phosphate Materials as Cathodes for Lithium Batteries"" also proposes a model to explain lithium insertion/extraction in LiFePO4 and to predict voltage profiles at variou

  19. Radioactive Material Containment Bags

    National Research Council Canada - National Science Library

    2000-01-01

    The audit was requested by Senator Joseph I. Lieberman based on allegations made by a contractor, Defense Apparel Services, about the Navy's actions on three contracts for radioactive material containment bags...

  20. A Novel Cathode Material for Cathodic Dehalogenation of 1,1-Dibromo Cyclopropane Derivatives.

    Science.gov (United States)

    Gütz, Christoph; Selt, Maximilian; Bänziger, Markus; Bucher, Christoph; Römelt, Christina; Hecken, Nadine; Gallou, Fabrice; Galvão, Tomás R; Waldvogel, Siegfried R

    2015-09-28

    Leaded bronze turned out to be an excellent cathode material for the dehalogenation reaction of cyclopropanes without affecting the strained molecular entity. With this particular alloy, beneficial properties of lead cathodes are conserved, whereas the corrosion of cathode is efficiently suppressed. The solvent in the electrolyte determines whether a complete debromination reaction is achieved or if the process can be selectively stopped at the monobromo cyclopropane intermediate. The electroorganic conversion tolerates a variety of functional groups and can be conducted at rather complex substrates like cyclosporine A. This approach allows the sustainable preparation of cyclopropane derivatives. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  1. Battery designs with high capacity anode materials and cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Masarapu, Charan; Anguchamy, Yogesh Kumar; Han, Yongbong; Deng, Haixia; Kumar, Sujeet; Lopez, Herman A.

    2017-10-03

    Improved high energy capacity designs for lithium ion batteries are described that take advantage of the properties of high specific capacity anode active compositions and high specific capacity cathode active compositions. In particular, specific electrode designs provide for achieving very high energy densities. Furthermore, the complex behavior of the active materials is used advantageously in a radical electrode balancing design that significantly reduced wasted electrode capacity in either electrode when cycling under realistic conditions of moderate to high discharge rates and/or over a reduced depth of discharge.

  2. Impregnated cathode coated with tungsten thin film containing Sc2O3

    International Nuclear Information System (INIS)

    Yamamoto, S.; Taguchi, S.; Watanabe, I.; Kawase, S.

    1987-01-01

    An impregnated cathode of a novel structure is proposed, fabricated, and evaluated. A thin tungsten film 100--400 nm in thickness containing various amounts of Sc 2 O 3 is coated on a standard impregnated cathode composed of a porous tungsten body in which electron emissive materials are impregnated. The electron emission property measured with a diode configuration is found to be dependent on Sc 2 O 3 content and surface atom distribution. Surface atom distribution is depicted by means of Auger electron spectroscopy. For high electron emission enhancement it is necessary for Sc 2 O 3 content to be 2.5--6.5 wt. % and for a layer of the order of a monolayer in thickness composed of Ba, Sc, and O to develop on the cathode surface

  3. The cathode material for a plasma-arc heater

    Science.gov (United States)

    Yelyutin, A. V.; Berlin, I. K.; Averyanov, V. V.; Kadyshevskii, V. S.; Savchenko, A. A.; Putintseva, R. G.

    1983-11-01

    The cathode of a plasma arc heater experiences a large thermal load. The temperature of its working surface, which is in contact with the plasma, reaches high values, as a result of which the electrode material is subject to erosion. Refractory metals are usually employed for the cathode material, but because of the severe erosion do not usually have a long working life. The most important electrophysical characteristic of the electrode is the electron work function. The use of materials with a low electron work function allows a decrease in the heat flow to the cathode, and this leads to an increase in its erosion resistance and working life. The electroerosion of certain materials employed for the cathode in an electric arc plasma generator in the process of reduction smelting of refractory metals was studied.

  4. Container for radioactive materials

    International Nuclear Information System (INIS)

    Housholder, W.R.; Greer, N.L.

    1976-01-01

    The improvement of the construction of containers for the transport of nuclear fuels is proposed where above all, the insulating mass suggested is important as it acts as a safeguard in case of an accident. The container consists of a metal casing in which there is a pressure boiler and a gamma-shielding device, spacers between the metal casing and the shielding device as well as an insulation filling the space between them. The insulating material is a water-in-resin emulsion which is hardened or cross-linked by peroxide and which can furthermore contain up to 50 wt.% solid silicious material such as vermuculite or chopped glass fibre. The construction and variations of the insulating mass composition are described in great detail. (HR) [de

  5. Chromium (V) compounds as cathode material in electrochemical power sources

    Science.gov (United States)

    Delnick, F.M.; Guidotti, R.A.; McCarthy, D.K.

    A cathode for use in a thermal battery, comprising a chromium (V) compound. The preferred materials for this use are Ca/sub 5/(CrO/sub 4/)/sub 3/Cl, Ca/sub 5/(CrO/sub 4/)OH, and Cr/sub 2/O/sub 5/. The chromium (V) compound can be employed as a cathode material in ambient temperature batteries when blended with a suitably conductive filler, preferably carbon black.

  6. Material containment enclosure

    International Nuclear Information System (INIS)

    Carlson, D.O.

    1993-01-01

    An isolation enclosure and a group of isolation enclosures are described which are useful when a relatively large containment area is required. The enclosure is in the form of a ring having a section removed so that a technician may enter the center area of the ring. In a preferred embodiment, an access zone is located in the transparent wall of the enclosure and extends around the inner perimeter of the ring so that a technician can insert his hands into the enclosure to reach any point within. The inventive enclosures provide more containment area per unit area of floor space than conventional material isolation enclosures. 3 figures

  7. Surface Modification Technique of Cathode Materials for LI-ION Battery

    Science.gov (United States)

    Jia, Yongzhong; Han, Jinduo; Jing, Yan; Jin, Shan; Qi, Taiyuan

    Cathode materials for Li-ion battery LiMn2O4 and LiCo0.1Mn1.9O4 were prepared by soft chemical method. Carbon, which was made by decomposing organic compounds, was used as modifying agent. Cathode material matrix was mixed with water solution that had contained organic compound such as cane sugar, soluble amylum, levulose et al. These mixture were reacted at 150 200 °C for 0.5 4 h in a Teflon-lined autoclave to get a series of homogeneously C-coated cathode materials. The new products were analyzed by X-ray diffraction (XRD) and infrared (IR). Morphology of cathode materials was characterized by scanning electron microscope (SEM) and transition electron microscope (TEM). The new homogeneously C-coated products that were used as cathode materials of lithium-ion battery had good electrochemical stability and cycle performance. This technique has free-pollution, low cost, simpleness and easiness to realize the industrialization of the cathode materials for Li-ion battery.

  8. Consumer Products Containing Radioactive Materials

    Science.gov (United States)

    Fact Sheet Adopted: February 2010 Health Physics Society Specialists in Radiation Safety Consumer Products Containing Radioactive Materials Everything we encounter in our daily lives contains some radioactive material, ...

  9. Durability and performance optimization of cathode materials for fuel cells

    Science.gov (United States)

    Colon-Mercado, Hector Rafael

    The primary objective of this dissertation is to develop an accelerated durability test (ADT) for the evaluation of cathode materials for fuel cells. The work has been divided in two main categories, namely high temperature fuel cells with emphasis on the Molten Carbonate Fuel Cell (MCFC) cathode current collector corrosion problems and low temperature fuel cells in particular Polymer Electrolyte Fuel Cell (PEMFC) cathode catalyst corrosion. The high operating temperature of MCFC has given it benefits over other fuel cells. These include higher efficiencies (>50%), faster electrode kinetics, etc. At 650°C, the theoretical open circuit voltage is established, providing low electrode overpotentials without requiring any noble metal catalysts and permitting high electrochemical efficiency. The waste heat is generated at sufficiently high temperatures to make it useful as a co-product. However, in order to commercialize the MCFC, a lifetime of 40,000 hours of operation must be achieved. The major limiting factor in the MCFC is the corrosion of cathode materials, which include cathode electrode and cathode current collector. In the first part of this dissertation the corrosion characteristics of bare, heat-treated and cobalt coated titanium alloys were studied using an ADT and compared with that of state of the art current collector material, SS 316. PEMFCs are the best choice for a wide range of portable, stationary and automotive applications because of their high power density and relatively low-temperature operation. However, a major impediment in the commercialization of the fuel cell technology is the cost involved due to the large amount of platinum electrocatalyst used in the cathode catalyst. In an effort to increase the power and decrease the cathode cost in polymer electrolyte fuel cell (PEMFC) systems, Pt-alloy catalysts were developed to increase its activity and stability. Extensive research has been conducted in the area of new alloy development and

  10. Materials characterization of impregnated W and W–Ir cathodes after oxygen poisoning

    International Nuclear Information System (INIS)

    Polk, James E.; Capece, Angela M.

    2015-01-01

    Highlights: • Impregnated W and W–Ir cathodes were operated with 100 ppm of oxygen in Xe gas. • High concentrations of oxygen accelerated the formation of tungstate layers. • The W–Ir emitter exhibited less erosion and redeposition at the upstream end. • Tungsten was preferentially transported in the insert plasma of the W–Ir cathode. - Abstract: Electric thrusters use hollow cathodes as the electron source for generating the plasma discharge and for beam neutralization. These cathodes contain porous tungsten emitters impregnated with BaO material to achieve a lower surface work function and are operated with xenon propellant. Oxygen contaminants in the xenon plasma can poison the emitter surface, resulting in a higher work function and increased operating temperature. This could lead directly to cathode failure by preventing discharge ignition or could accelerate evaporation of the BaO material. Exposures over hundreds of hours to very high levels of oxygen can result in increased temperatures, oxidation of the tungsten substrate, and the formation of surface layers of barium tungstates. In this work, we present results of a cathode test in which impregnated tungsten and tungsten–iridium emitters were operated with 100 ppm of oxygen in the xenon plasma for several hundred hours. The chemical and morphological changes were studied using scanning electron microscopy, energy dispersive spectroscopy, and laser profilometry. The results provide strong evidence that high concentrations of oxygen accelerate the formation of tungstate layers in both types of emitters, a phenomenon not inherent to normal cathode operation. Deposits of pure tungsten were observed on the W–Ir emitter, indicating that tungsten is preferentially removed from the surface and transported in the insert plasma. A W–Ir cathode surface will therefore evolve to a pure W composition, eliminating the work function benefit of W–Ir. However, the W–Ir emitter exhibited less erosion

  11. Radioactive material transporting container

    International Nuclear Information System (INIS)

    Watabe, Yukio.

    1990-01-01

    As a supporting member of a sealing container for containing spent fuels, etc., a straight pipe or a cylinder has been used. However, upon dropping test, the supporting member is buckled toward the central axis of a transporting container and a shock absorber is crushed in the axial direction to prevent its pushing force to the outer side, which may possibly hinder normal shock moderating function. Then, at least more than one-half of the supporting member is protruded radially to the outer side of the sealing container beyond the fixed portion with the sealed container, so that the member has a portion extended in the radial outside of the transporting container with an angle greater than the angle formed between a line connecting the outer circumference at the bottom of an outer cylinder with the gravitational center of the transporting container and the central axis of the transporting container. As a result, buckling of the supporting member toward the central axis of the transporting container upon dropping test can be prevented and the deformation of the shock absorber is neither not prevented to exhibit normal shock absorbing effect. This can improve the reliability and reduce the amount of shock absorbers. (N.H.)

  12. Sulfur-carbon nanocomposites and their application as cathode materials in lithium-sulfur batteries

    Energy Technology Data Exchange (ETDEWEB)

    Liang, Chengdu; Dudney, Nancy J.; Howe, Jane Y.

    2017-08-01

    The invention is directed in a first aspect to a sulfur-carbon composite material comprising: (i) a bimodal porous carbon component containing therein a first mode of pores which are mesopores, and a second mode of pores which are micropores; and (ii) elemental sulfur contained in at least a portion of said micropores. The invention is also directed to the aforesaid sulfur-carbon composite as a layer on a current collector material; a lithium ion battery containing the sulfur-carbon composite in a cathode therein; as well as a method for preparing the sulfur-composite material.

  13. High-Capacity, High-Voltage Composite Oxide Cathode Materials

    Science.gov (United States)

    Hagh, Nader M.

    2015-01-01

    This SBIR project integrates theoretical and experimental work to enable a new generation of high-capacity, high-voltage cathode materials that will lead to high-performance, robust energy storage systems. At low operating temperatures, commercially available electrode materials for lithium-ion (Li-ion) batteries do not meet energy and power requirements for NASA's planned exploration activities. NEI Corporation, in partnership with the University of California, San Diego, has developed layered composite cathode materials that increase power and energy densities at temperatures as low as 0 degC and considerably reduce the overall volume and weight of battery packs. In Phase I of the project, through innovations in the structure and morphology of composite electrode particles, the partners successfully demonstrated an energy density exceeding 1,000 Wh/kg at 4 V at room temperature. In Phase II, the team enhanced the kinetics of Li-ion transport and electronic conductivity at 0 degC. An important feature of the composite cathode is that it has at least two components that are structurally integrated. The layered material is electrochemically inactive; however, upon structural integration with a spinel material, the layered material can be electrochemically activated and deliver a large amount of energy with stable cycling.

  14. Innovative application of ionic liquid to separate Al and cathode materials from spent high-power lithium-ion batteries.

    Science.gov (United States)

    Zeng, Xianlai; Li, Jinhui

    2014-04-30

    Because of the increasing number of electric vehicles, there is an urgent need for effective recycling technologies to recapture the significant amount of valuable metals contained in spent lithium-ion batteries (LiBs). Previous studies have indicated, however, that Al and cathode materials were quite difficult to separate due to the strong binding force supplied by the polyvinylidene fluoride (PVDF), which was employed to bind cathode materials and Al foil. This research devoted to seek a new method of melting the PVDF binder with heated ionic liquid (IL) to separate Al foil and cathode materials from the spent high-power LiBs. Theoretical analysis based on Fourier's law was adopted to determine the heat transfer mechanism of cathode material and to examine the relationship between heating temperature and retention time. All the experimental and theoretic results show that peel-off rate of cathode materials from Al foil could reach 99% when major process parameters were controlled at 180°C heating temperature, 300 rpm agitator rotation, and 25 min retention time. The results further imply that the application of IL for recycling Al foil and cathode materials from spent high-power LiBs is highly efficient, regardless of the application source of the LiBs or the types of cathode material. This study endeavors to make a contribution to an environmentally sound and economically viable solution to the challenge of spent LiB recycling. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. Oxyphosphorus-containing polymers as binders for battery cathodes

    Science.gov (United States)

    Pratt, Russell Clayton; Mullin, Scott Allen; Eitouni, Hany Basam

    2018-05-29

    A class of polymeric phosphorous esters can be used as binders for battery cathodes. Metal salts can be added to the polymers to provide ionic conductivity. The polymeric phosphorous esters can be formulated with other polymers either as mixtures or as copolymers to provide additional desirable properties. Examples of such properties include even higher ionic conductivity and improved mechanical properties. Furthermore, cathodes that include the polymeric phosphorous esters can be assembled with a polymeric electrolyte separator and an anode to form a complete battery.

  16. Materials designed for containments

    International Nuclear Information System (INIS)

    Piehl, K.H.

    1976-01-01

    The present article points out that high-tensile fine-grained steels have been used successfully in the construction of reactor containments, spherical gasometers, and pressure vessels. It has been confirmed that their use requires safety measures concerning lay out and production. Viscosity properties of high-tensile, fine-grained steels can be improved significantly by means of electroslag remelting. The extent to which this improvement influences the heat-affected zone is being examined. (orig./RW) [de

  17. Carbonization kinetics of La2O3-Mo cathode materials

    International Nuclear Information System (INIS)

    Jinshu, W.; Meiling, Z.; Tieyong, Z.; Jiuxing, Z.; Zuoren, N.

    2001-01-01

    The carbonization kinetics of La 2 O 3 -Mo cathode materials has been studied by thermal analysis method. Three-stage model of the carbonization has been presented in this paper. The carbonization rate is initially controlled by chemical reaction, then controlled by chemical reaction mixed with diffusion, finally controlled by diffusion. After the initial experimental data are processed according to this model, the correlation coefficients of the kinetic curves are satisfactory. The apparent activation energy of carbonization of La 2 O 3 -Mo cathode materials has been obtained. At the same time, we have deduced the empirical expressions of the amount of weight increased per unit area after carbonization, temperature and time in the temperature range 1393 K - 1493 K. (author)

  18. Cathode Lens Mode of the SEM in Materials Science Applications

    Czech Academy of Sciences Publication Activity Database

    Frank, Luděk; Müllerová, Ilona; Matsuda, K.; Ikeno, S.

    2007-01-01

    Roč. 48, č. 5 (2007), s. 944-948 ISSN 1345-9678 R&D Projects: GA ČR GA102/05/2327; GA ČR GA202/04/0281 Institutional research plan: CEZ:AV0Z20650511 Keywords : electron microscopy of materials * scanning electron microscopy * low energy electron microscopy * cathode lens Subject RIV: JA - Electronics ; Optoelectronics, Electrical Engineering Impact factor: 1.018, year: 2007

  19. Comparison of Nonprecious Metal Cathode Materials for Methane Production by Electromethanogenesis.

    KAUST Repository

    Siegert, Michael; Yates, Matthew D; Call, Douglas F; Zhu, Xiuping; Spormann, Alfred; Logan, Bruce E

    2014-01-01

    In methanogenic microbial electrolysis cells (MMCs), CO2 is reduced to methane using a methanogenic biofilm on the cathode by either direct electron transfer or evolved hydrogen. To optimize methane generation, we examined several cathode materials

  20. Reactivity between carbon cathode materials and electrolyte based on industrial and laboratory data

    CSIR Research Space (South Africa)

    Chauke, L

    2013-07-01

    Full Text Available Interaction between electrolyte and carbon cathodes during the electrolytic production of aluminium decreases cell life. This paper describes the interaction between carbon cathode materials and electrolyte, based on industrial and laboratory data...

  1. Cobalt and cerium coated Ni powder as a new candidate cathode material for MCFC

    International Nuclear Information System (INIS)

    Kim, Min Hyuk; Hong, Ming Zi; Kim, Young-Suk; Park, Eunjoo; Lee, Hyunsuk; Ha, Hyung-Wook; Kim, Keon

    2006-01-01

    The dissolution of nickel oxide cathode in the electrolyte is one of the major technical obstacles to the commercialization of molten carbonate fuel cell (MCFC). To improve the MCFC cathode stability, the alternative cathode material for MCFC was prepared, which was made of Co/Ce-coated on the surface of Ni powder using a polymeric precursor based on the Pechini method. X-ray diffraction (XRD) and scanning electron microscopy (SEM) with energy dispersive X-ray analysis (EDAX) were employed in characterization of the alternative cathode materials. The Co/Ce-coated Ni cathode prepared by the tape-casting technique. The solubility of the Co/Ce-coated Ni cathode was about 80% lower when compare to that of pure Ni cathode under CO 2 :O 2 (66.7:33.3%) atmosphere at 650 deg. C. Consequently, the fine Co/Ce-coated Ni powder could be confirmed as a new alternative cathode material for MCFC

  2. Container Materials, Fabrication And Robustness

    International Nuclear Information System (INIS)

    Dunn, K.; Louthan, M.; Rawls, G.; Sindelar, R.; Zapp, P.; Mcclard, J.

    2009-01-01

    The multi-barrier 3013 container used to package plutonium-bearing materials is robust and thereby highly resistant to identified degradation modes that might cause failure. The only viable degradation mechanisms identified by a panel of technical experts were pressurization within and corrosion of the containers. Evaluations of the container materials and the fabrication processes and resulting residual stresses suggest that the multi-layered containers will mitigate the potential for degradation of the outer container and prevent the release of the container contents to the environment. Additionally, the ongoing surveillance programs and laboratory studies should detect any incipient degradation of containers in the 3013 storage inventory before an outer container is compromised.

  3. Innovative application of ionic liquid to separate Al and cathode materials from spent high-power lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Xianlai; Li, Jinhui, E-mail: jinhui@tsinghua.edu.cn

    2014-04-01

    Highlights: • Manual dismantling is superior in spent high-power LiBs recycling. • Heated ionic liquid can effectively separate Al and cathode materials. • Fourier’s law was adopted to determine the heat transfer mechanism. • The process of spent LiBs recycling with heated ionic liquid dismantling was proposed. - Abstract: Because of the increasing number of electric vehicles, there is an urgent need for effective recycling technologies to recapture the significant amount of valuable metals contained in spent lithium-ion batteries (LiBs). Previous studies have indicated, however, that Al and cathode materials were quite difficult to separate due to the strong binding force supplied by the polyvinylidene fluoride (PVDF), which was employed to bind cathode materials and Al foil. This research devoted to seek a new method of melting the PVDF binder with heated ionic liquid (IL) to separate Al foil and cathode materials from the spent high-power LiBs. Theoretical analysis based on Fourier’s law was adopted to determine the heat transfer mechanism of cathode material and to examine the relationship between heating temperature and retention time. All the experimental and theoretic results show that peel-off rate of cathode materials from Al foil could reach 99% when major process parameters were controlled at 180 °C heating temperature, 300 rpm agitator rotation, and 25 min retention time. The results further imply that the application of IL for recycling Al foil and cathode materials from spent high-power LiBs is highly efficient, regardless of the application source of the LiBs or the types of cathode material. This study endeavors to make a contribution to an environmentally sound and economically viable solution to the challenge of spent LiB recycling.

  4. Triple-conducting layered perovskites as cathode materials for proton-conducting solid oxide fuel cells.

    Science.gov (United States)

    Kim, Junyoung; Sengodan, Sivaprakash; Kwon, Goeun; Ding, Dong; Shin, Jeeyoung; Liu, Meilin; Kim, Guntae

    2014-10-01

    We report on an excellent anode-supported H(+) -SOFC material system using a triple conducting (H(+) /O(2-) /e(-) ) oxide (TCO) as a cathode material for H(+) -SOFCs. Generally, mixed ionic (O(2-) ) and electronic conductors (MIECs) have been selected as the cathode material of H(+) -SOFCs. In an H(+) -SOFC system, however, MIEC cathodes limit the electrochemically active sites to the interface between the proton conducting electrolyte and the cathode. New approaches to the tailoring of cathode materials for H(+) -SOFCs should therefore be considered. TCOs can effectively extend the electrochemically active sites from the interface between the cathode and the electrolyte to the entire surface of the cathode. The electrochemical performance of NBSCF/BZCYYb/BZCYYb-NiO shows excellent long term stability for 500 h at 1023 K with high power density of 1.61 W cm(-2) . © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  5. Cathodic electrodeposition of ceramic and organoceramic materials. Fundamental aspects.

    Science.gov (United States)

    Zhitomirsky, I

    2002-03-29

    Electrodeposition of ceramic materials can be performed by electrophoretic (EPD) or electrolytic (ELD) deposition. Electrophoretic deposition is achieved via motion of charged particles towards an electrode under an applied electric field. Electrolytic deposition produces colloidal particles in cathodic reactions for subsequent deposition. Various electrochemical strategies and deposition mechanisms have been developed for electrodeposition of ceramic and organoceramic films, and are discussed in the present article. Electrode-position of ceramic and organoceramic materials includes mass transport, accumulation of particles near the electrode and their coagulation to form a cathodic deposit. Various types of interparticle forces that govern colloidal stability in the absence and presence of processing additives are discussed. Novel theoretical contributions towards an interpretation of particle coagulation near the electrode surface are reviewed. Background information is given on the methods of particle charging, stabilization of colloids in aqueous and non-aqueous media, electrophoretic mobility of ceramic particles and polyelectrolytes, and electrode reactions. This review also covers recent developments in the electrodeposition of ceramic and organoceramic materials.

  6. Container for shipping dangerous material

    International Nuclear Information System (INIS)

    Blum, P.T.

    1987-01-01

    This container for shipping dangerous material is made by a cylindrical casing of austenitic stainless steel with rounded ends and walls of uniform thickness with welded joins, a tubular metal shock absorber fixed over each end of the casing, removable lugs fixed to the casing, optionally retainers for the material within the casing [fr

  7. Fundamental degradation mechanisms of layered oxide Li-ion battery cathode materials: Methodology, insights and novel approaches

    International Nuclear Information System (INIS)

    Hausbrand, R.; Cherkashinin, G.; Ehrenberg, H.; Gröting, M.; Albe, K.; Hess, C.; Jaegermann, W.

    2015-01-01

    Graphical abstract: - Highlights: • Description of recent in operando and in situ analysis methodology. • Surface science approach using photoemission for analysis of cathode surfaces and interfaces. • Ageing and fatigue of layered oxide Li-ion battery cathode materials from the atomistic point of view. • Defect formation and electronic structure evolution as causes for cathode degradation. • Significance of interfacial energy alignment and contact potential for side reactions. - Abstract: This overview addresses the atomistic aspects of degradation of layered LiMO 2 (M = Ni, Co, Mn) oxide Li-ion battery cathode materials, aiming to shed light on the fundamental degradation mechanisms especially inside active cathode materials and at their interfaces. It includes recent results obtained by novel in situ/in operando diffraction methods, modelling, and quasi in situ surface science analysis. Degradation of the active cathode material occurs upon overcharge, resulting from a positive potential shift of the anode. Oxygen loss and eventual phase transformation resulting in dead regions are ascribed to changes in electronic structure and defect formation. The anode potential shift results from loss of free lithium due to side reactions occurring at electrode/electrolyte interfaces. Such side reactions are caused by electron transfer, and depend on the electron energy level alignment at the interface. Side reactions at electrode/electrolyte interfaces and capacity fade may be overcome by the use of suitable solid-state electrolytes and Li-containing anodes

  8. Developments in the Material Fabrication and Performance of LiMn2O4 dCld Cathode Material

    Science.gov (United States)

    2016-06-13

    manganese oxide spinel materials exhibit promising electrochemical performance and good thermodynamic and kinetic stability when used as a cathode in... oxide spinel (LiMn2O4) is a potential viable active cathode material for use in these versatile applications due to its low toxicity, good capacity...Developments in the Material Fabrication and Performance of LiMn2O4-dCld Cathode Material Paula C Latorre, Ashley L Ruth, and Terrill B Atwater

  9. Copper sulfates as cathode materials for Li batteries

    Energy Technology Data Exchange (ETDEWEB)

    Schwieger, Jonathan N.; Kraytsberg, Alexander; Ein-Eli, Yair [Technion Israel Institute of Technology, Department of Materials Engineering, Technion City, Haifa 32000 (Israel)

    2011-02-01

    As lithium battery technology sets out to bridge the gap between portable electronics and the electrical automotive industry, cathode materials still stand as the bottleneck regarding performances. In the realm of highly attractive polyanion-type structures as high-voltage cathode materials, the sulfate group (SO{sub 4}){sup 2-} possesses an acknowledged superiority over other contenders in terms of open circuit voltage arising from the inductive effect of strong covalent S-O bonds. In parallel, novel lithium insertion mechanisms are providing alternatives to traditional intercalation, enabling reversible multi-electron processes securing high capacities. Combining both of these advantageous features, we report here the successful electrochemical reactivity of copper sulfate pentahydrate (CuSO{sub 4}.5H{sub 2}O) with respect to lithium insertion via a two-electron displacement reaction entailing the extrusion of metallic copper at a dual voltage of 3.2 V and 2.7 V followed by its reversible insertion at 3.5 V and 3.8 V. At this stage, cyclability was still shown to be limited due to the irreversible degradation to a monohydrate structure owing to constitutional water loss. (author)

  10. Copper sulfates as cathode materials for Li batteries

    Science.gov (United States)

    Schwieger, Jonathan N.; Kraytsberg, Alexander; Ein-Eli, Yair

    As lithium battery technology sets out to bridge the gap between portable electronics and the electrical automotive industry, cathode materials still stand as the bottleneck regarding performances. In the realm of highly attractive polyanion-type structures as high-voltage cathode materials, the sulfate group (SO 4) 2- possesses an acknowledged superiority over other contenders in terms of open circuit voltage arising from the inductive effect of strong covalent S-O bonds. In parallel, novel lithium insertion mechanisms are providing alternatives to traditional intercalation, enabling reversible multi-electron processes securing high capacities. Combining both of these advantageous features, we report here the successful electrochemical reactivity of copper sulfate pentahydrate (CuSO 4·5H 2O) with respect to lithium insertion via a two-electron displacement reaction entailing the extrusion of metallic copper at a dual voltage of 3.2 V and 2.7 V followed by its reversible insertion at 3.5 V and 3.8 V. At this stage, cyclability was still shown to be limited due to the irreversible degradation to a monohydrate structure owing to constitutional water loss.

  11. Sulfur containing nanoporous materials, nanoparticles, methods and applications

    Science.gov (United States)

    Archer, Lynden A.; Navaneedhakrishnan, Jayaprakash

    2018-01-30

    Sulfur containing nanoparticles that may be used within cathode electrodes within lithium ion batteries include in a first instance porous carbon shape materials (i.e., either nanoparticle shapes or "bulk" shapes that are subsequently ground to nanoparticle shapes) that are infused with a sulfur material. A synthetic route to these carbon and sulfur containing nanoparticles may use a template nanoparticle to form a hollow carbon shape shell, and subsequent dissolution of the template nanoparticle prior to infusion of the hollow carbon shape shell with a sulfur material. Sulfur infusion into other porous carbon shapes that are not hollow is also contemplated. A second type of sulfur containing nanoparticle includes a metal oxide material core upon which is located a shell layer that includes a vulcanized polymultiene polymer material and ion conducting polymer material. The foregoing sulfur containing nanoparticle materials provide the electrodes and lithium ion batteries with enhanced performance.

  12. Co-free, iron perovskites as cathode materials for intermediate-temperature solid oxide fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Hou, Shu-en [Engineering Research Center of Nano-Geo Materials of Ministry of Education, China University of Geosciences, Wuhan, 430074 (China); Texas Materials Institute, ETC 9.102, The University of Texas at Austin, Austin, TX 78712 (United States); Alonso, Jose Antonio [Instituto de Ciencia de Materiales de Madrid, CSIC, Cantoblanco, E-28049 Madrid (Spain); Texas Materials Institute, ETC 9.102, The University of Texas at Austin, Austin, TX 78712 (United States); Goodenough, John B. [Texas Materials Institute, ETC 9.102, The University of Texas at Austin, Austin, TX 78712 (United States)

    2010-01-01

    We have developed a Co-free solid oxide fuel cell (SOFC) based upon Fe mixed oxides that gives an extraordinary performance in test-cells with H{sub 2} as fuel. As cathode material, the perovskite Sr{sub 0.9}K{sub 0.1}FeO{sub 3-{delta}} (SKFO) has been selected since it has an excellent ionic and electronic conductivity and long-term stability under oxidizing conditions; the characterization of this material included X-ray diffraction (XRD), thermal analysis, scanning microscopy and conductivity measurements. The electrodes were supported on a 300-{mu}m thick pellet of the electrolyte La{sub 0.8}Sr{sub 0.2}Ga{sub 0.83}Mg{sub 0.17}O{sub 3-{delta}} (LSGM) with Sr{sub 2}MgMoO{sub 6} as the anode and SKFO as the cathode. The test cells gave a maximum power density of 680 mW cm{sup -2} at 800 C and 850 mW cm{sup -2} at 850 C, with pure H{sub 2} as fuel. The electronic conductivity shows a change of regime at T {approx} 350 C that could correspond to the phase transition from tetragonal to cubic symmetry. The high-temperature regime is characterized by a metallic-like behavior. At 800 C the crystal structure contains 0.20(1) oxygen vacancies per formula unit randomly distributed over the oxygen sites (if a cubic symmetry is assumed). The presence of disordered vacancies could account, by itself, for the oxide-ion conductivity that is required for the mass transport across the cathode. The result is a competitive cathode material containing no cobalt that meets the target for the intermediate-temperature SOFC. (author)

  13. Comparison of Nonprecious Metal Cathode Materials for Methane Production by Electromethanogenesis.

    KAUST Repository

    Siegert, Michael

    2014-02-18

    In methanogenic microbial electrolysis cells (MMCs), CO2 is reduced to methane using a methanogenic biofilm on the cathode by either direct electron transfer or evolved hydrogen. To optimize methane generation, we examined several cathode materials: plain graphite blocks, graphite blocks coated with carbon black or carbon black containing metals (platinum, stainless steel or nickel) or insoluble minerals (ferrihydrite, magnetite, iron sulfide, or molybdenum disulfide), and carbon fiber brushes. Assuming a stoichiometric ratio of hydrogen (abiotic):methane (biotic) of 4:1, methane production with platinum could be explained solely by hydrogen production. For most other materials, however, abiotic hydrogen production rates were insufficient to explain methane production. At -600 mV, platinum on carbon black had the highest abiotic hydrogen gas formation rate (1600 ± 200 nmol cm(-3) d(-1)) and the highest biotic methane production rate (250 ± 90 nmol cm(-3) d(-1)). At -550 mV, plain graphite (76 nmol cm(-3) d(-1)) performed similarly to platinum (73 nmol cm(-3) d(-1)). Coulombic recoveries, based on the measured current and evolved gas, were initially greater than 100% for all materials except platinum, suggesting that cathodic corrosion also contributed to electromethanogenic gas production.

  14. Preparation and electrochemical performance of sulfur-alumina cathode material for lithium-sulfur batteries

    Energy Technology Data Exchange (ETDEWEB)

    Dong, Kang [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China); Wang, Shengping, E-mail: spwang@cug.edu.cn [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China); Zhang, Hanyu; Wu, Jinping [Faculty of Material Science and Chemistry, China University of Geosciences, 388 Lumo Road, 430074 Wuhan (China)

    2013-06-01

    Highlights: ► Micron-sized alumina was synthesized as adsorbent for lithium-sulfur batteries. ► Sulfur-alumina material was synthesized via crystallizing nucleation. ► The Al{sub 2}O{sub 3} can provide surface area for the deposition of Li{sub 2}S and Li{sub 2}S{sub 2}. ► The discharge capacity of the battery is improved during the first several cycles. - Abstract: Nano-sized sulfur particles exhibiting good adhesion with conducting acetylene black and alumina composite materials were synthesized by means of an evaporated solvent and a concentrated crystallization method for use as the cathodes of lithium-sulfur batteries. The composites were characterized and examined by X-ray diffraction, environmental scanning electron microscopy and electrochemical methods, such as cyclic voltammetry, electrical impedance spectroscopy and charge–discharge tests. Micron-sized flaky alumina was employed as an adsorbent for the cathode material. The initial discharge capacity of the cathode with the added alumina was 1171 mAh g{sup −1}, and the remaining capacity was 585 mAh g{sup −1} after 50 cycles at 0.25 mA cm{sup −2}. Compared with bare sulfur electrodes, the electrodes containing alumina showed an obviously superior cycle performance, confirming that alumina can contribute to reducing the dissolution of polysulfides into electrolytes during the sulfur charge–discharge process.

  15. Preparation and electrochemical performance of sulfur-alumina cathode material for lithium-sulfur batteries

    International Nuclear Information System (INIS)

    Dong, Kang; Wang, Shengping; Zhang, Hanyu; Wu, Jinping

    2013-01-01

    Highlights: ► Micron-sized alumina was synthesized as adsorbent for lithium-sulfur batteries. ► Sulfur-alumina material was synthesized via crystallizing nucleation. ► The Al 2 O 3 can provide surface area for the deposition of Li 2 S and Li 2 S 2 . ► The discharge capacity of the battery is improved during the first several cycles. - Abstract: Nano-sized sulfur particles exhibiting good adhesion with conducting acetylene black and alumina composite materials were synthesized by means of an evaporated solvent and a concentrated crystallization method for use as the cathodes of lithium-sulfur batteries. The composites were characterized and examined by X-ray diffraction, environmental scanning electron microscopy and electrochemical methods, such as cyclic voltammetry, electrical impedance spectroscopy and charge–discharge tests. Micron-sized flaky alumina was employed as an adsorbent for the cathode material. The initial discharge capacity of the cathode with the added alumina was 1171 mAh g −1 , and the remaining capacity was 585 mAh g −1 after 50 cycles at 0.25 mA cm −2 . Compared with bare sulfur electrodes, the electrodes containing alumina showed an obviously superior cycle performance, confirming that alumina can contribute to reducing the dissolution of polysulfides into electrolytes during the sulfur charge–discharge process

  16. The explosive cathode on the base of carbon-fibrous plastic material

    International Nuclear Information System (INIS)

    Korenev, S.A.; Baranov, A.M.; Kostyuchenko, S.V.; Chernenko, N.M.

    1988-01-01

    Production process of exploseve cathodes on the base of carbon-fibrous plastic material of any geometric form and size is discussed. Experimental study of current take-off from cathodes with diameter 2 cm of 10 kV and 150-250 kV voltage are given. It is shown that ignition voltage of cathode plasma is 2 kV with 5 mm gap electrode of diode and 5 ·10 -5 Tor pressure of residual gas. It is shown that carbon-fibrous cathode, made by this technology, provides more stable current take-off electron beam (withoud oscillations) in comparison with other cathodes

  17. Transport containers for radioactive material

    International Nuclear Information System (INIS)

    Doroszlai, P.; Ferroni, F.

    1984-01-01

    A cylindrical container for the transportation of radioactive reactor elements includes a top end, a bottom end and a pair of removable outwardly curved shock absorbers, each including a double-shelled construction having an internal shell with a convex intrados configuration and an external shell with a convex extrados configuration, the shock absorbers being filled with a low density energy-absorbing material and mounted at the top end and the bottom end of the container, respectively, and each of the shock absorbers having a toroidal configuration, and deformable tubes disposed within the shock absorbers and extending in the axial direction of the container

  18. New Cathode Materials for Intermediate Temperature Solid Oxide Fuel Cells

    Energy Technology Data Exchange (ETDEWEB)

    Allan J. Jacobson

    2006-09-30

    Operation of SOFCs at intermediate temperatures (500-800 C) requires new combinations of electrolyte and electrode materials that will provide both rapid ion transport across the electrolyte and electrode-electrolyte interfaces and efficient electrocatalysis of the oxygen reduction and fuel oxidation reactions. This project concentrates on materials and issues associated with cathode performance that are known to become limiting factors as the operating temperature is reduced. The specific objectives of the proposed research are to develop cathode materials that meet the electrode performance targets of 1.0 W/cm{sup 2} at 0.7 V in combination with YSZ at 700 C and with GDC, LSGM or bismuth oxide based electrolytes at 600 C. The performance targets imply an area specific resistance of {approx}0.5 {Omega}cm{sup 2} for the total cell. The research strategy is to investigate both established classes of materials and new candidates as cathodes, to determine fundamental performance parameters such as bulk diffusion, surface reactivity and interfacial transfer, and to couple these parameters to performance in single cell tests. The initial choices for study were perovskite oxides based on substituted LaFeO{sub 3} (P1 compositions), where significant data in single cell tests exist at PNNL for example, for La{sub 0.8}Sr{sub 0.2}FeO{sub 3} cathodes on both YSZ and CSO/YSZ. The materials selection was then extended to La{sub 2}NiO{sub 4} compositions (K1 compositions), and then in a longer range task we evaluated the possibility of completely unexplored group of materials that are also perovskite related, the ABM{sub 2}O{sub 5+{delta}}. A key component of the research strategy was to evaluate for each cathode material composition, the key performance parameters, including ionic and electronic conductivity, surface exchange rates, stability with respect to the specific electrolyte choice, and thermal expansion coefficients. In the initial phase, we did this in parallel with

  19. Preparation of cathode materials for Li-ion cells by acid dissolution

    International Nuclear Information System (INIS)

    Oh, Si Hyoung; Jeong, Woon Tae; Cho, Won Il; Cho, Byung Won; Woo, Kyoungja

    2005-01-01

    New synthesis route called acid dissolution method, preparing the high-performance cathode materials for the lithium-ion cells, was successfully developed. In this method, insoluble starting materials such as metal carbonates or metal hydroxides are dissolved in strong organic acidic solution which contains a chelating agent. And then, the solvent of the solution containing starting materials is eliminated to obtain the xerogel of the initial solution whose chemical form is expressed as Li[MA 3 ], where M is a transition metal atom and A is the anion of the organic acid. The xerogel is then calcined at the high temperature to obtain polycrystalline cathode materials. In this work, the applicability of this method was demonstrated synthesizing a polycrystalline single-phase LiCoO 2 using lithium carbonate, cobalt hydroxide as the insoluble starting materials and the acrylic acid as a chelating agent. The synthesized powders calcined at 800 deg. C showed a good electrochemical performance in the half-cell test

  20. Molten material-containing vessel

    International Nuclear Information System (INIS)

    Akagawa, Katsuhiko

    1998-01-01

    The molten material-containing vessel of the present invention comprises a vessel main body having an entrance opened at the upper end, a lid for closing the entrance, an outer tube having an upper end disposed at the lower surface of the lid, extended downwardly and having an closed lower end and an inner tube disposed coaxially with the outer tube. When a molten material is charged from the entrance to the inside of the vessel main body of the molten material-containing vessel and the entrance is closed by the lid, the outer tube and the inner tube are buried in the molten material in the vessel main body, accordingly, a fluid having its temperature elevated by absorption of the heat of the molten material rises along the inner circumferential surface of the outer tube, abuts against the lower surface of the lid and cooled by exchanging heat with the lid and forms a circulating flow. Since the heat in the molten material is continuously absorbed by the fluid, transferred to the lid and released from the lid to the atmospheric air, heat releasing efficiency can be improved compared with conventional cases. (N.H.)

  1. Direct regeneration of recycled cathode material mixture from scrapped LiFePO4 batteries

    Science.gov (United States)

    Li, Xuelei; Zhang, Jin; Song, Dawei; Song, Jishun; Zhang, Lianqi

    2017-03-01

    A new green recycling process (named as direct regeneration process) of cathode material mixture from scrapped LiFePO4 batteries is designed for the first time. Through this direct regeneration process, high purity cathode material mixture (LiFePO4 + acetylene black), anode material mixture (graphite + acetylene black) and other by-products (shell, Al foil, Cu foil and electrolyte solvent, etc.) are recycled from scrapped LiFePO4 batteries with high yield. Subsequently, recycled cathode material mixture without acid leaching is further directly regenerated with Li2CO3. Direct regeneration procedure of recycled cathode material mixture from 600 to 800 °C is investigated in detail. Cathode material mixture regenerated at 650 °C display excellent physical, chemical and electrochemical performances, which meet the reuse requirement for middle-end Li-ion batteries. The results indicate the green direct regeneration process with low-cost and high added-value is feasible.

  2. Computational Screening for Design of Optimal Coating Materials to Suppress Gas Evolution in Li-Ion Battery Cathodes.

    Science.gov (United States)

    Min, Kyoungmin; Seo, Seung-Woo; Choi, Byungjin; Park, Kwangjin; Cho, Eunseog

    2017-05-31

    Ni-rich layered oxides are attractive materials owing to their potentially high capacity for cathode applications. However, when used as cathodes in Li-ion batteries, they contain a large amount of Li residues, which degrade the electrochemical properties because they are the source of gas generation inside the battery. Here, we propose a computational approach to designing optimal coating materials that prevent gas evolution by removing residual Li from the surface of the battery cathode. To discover promising coating materials, the reactions of 16 metal phosphates (MPs) and 45 metal oxides (MOs) with the Li residues, LiOH, and Li 2 CO 3 are examined within a thermodynamic framework. A materials database is constructed according to density functional theory using a hybrid functional, and the reaction products are obtained according to the phases in thermodynamic equilibrium in the phase diagram. In addition, the gravimetric efficiency is calculated to identify coating materials that can eliminate Li residues with a minimal weight of the coating material. Overall, more MP and MO materials react with LiOH than with Li 2 CO 3 . Specifically, MPs exhibit better reactivity to both Li residues, whereas MOs react more with LiOH. The reaction products, such as Li-containing phosphates or oxides, are also obtained to identify the phases on the surface of a cathode after coating. On the basis of the Pareto-front analysis, P 2 O 5 could be an optimal material for the reaction with both Li residuals. Finally, the reactivity of the coating materials containing 3d/4d transition metal elements is better than that of materials containing other types of elements.

  3. A new high power thermal battery cathode material

    International Nuclear Information System (INIS)

    Faul, I.

    1986-01-01

    Smaller and lighter thermal batteries are major aims of the battery research programme at RAE Farnborough. Modern designs of thermal batteries, for use as power supplies in weapon systems, almost invariably use the Li:molten salt:FeS/sub 2/ system because of the significant increase in energy density achieved in comparison with the earlier Ca/CaCrO/sub 4/ couple. The disadvantage of the FeS/sub 2/ system is that the working cell voltage, between 1.5 and 2.0 V, is significantly lower so leading to more cells per battery than the earlier system. Further work at RAE and MSA (Britain) Ltd showed that the poor thermal stability of TiS/sub 2/ limited its use in thermal batteries, whilst the more stable V/sub 6/O/sub 13/ oxidised the electrolyte, giving poor efficiencies. However, the resulting reduced vanadium oxide material, subsequently called lithiated vanadium oxide (LVO), was found to be an excellent high voltage thermal battery cathode, being the subject of both UK and US patents. In this study both V/sub 6/O/sub 13/ made by the direct stoichiometric reaction of V/sub 2/O/sub 5/ and V and also by thermal decomposition of NH/sub 4/VO/sub 3/ under argon, have been used with equal success as the starting material for the preparation of LVO

  4. Metalized, three-dimensional structured oxygen cathode materials for lithium/air batteries and method for making and using the same

    Energy Technology Data Exchange (ETDEWEB)

    Xing, Weibing; Buettner-Garrett, Josh

    2017-04-18

    This disclosure relates generally to cathode materials for electrochemical energy cells, more particularly to metal/air electrochemical energy cell cathode materials containing silver vanadium oxide and methods of making and using the same. The metal/air electrochemical energy cell can be a lithium/air electrochemical energy cell. Moreover the silver vanadium oxide can be a catalyst for one or more of oxidation and reduction processes of the electrochemical energy cell.

  5. Oxide Fiber Cathode Materials for Rechargeable Lithium Cells

    Science.gov (United States)

    Rice, Catherine E.; Welker, Mark F.

    2008-01-01

    LiCoO2 and LiNiO2 fibers have been investigated as alternatives to LiCoO2 and LiNiO2 powders used as lithium-intercalation compounds in cathodes of rechargeable lithium-ion electrochemical cells. In making such a cathode, LiCoO2 or LiNiO2 powder is mixed with a binder [e.g., poly(vinylidene fluoride)] and an electrically conductive additive (usually carbon) and the mixture is pressed to form a disk. The binder and conductive additive contribute weight and volume, reducing the specific energy and energy density, respectively. In contrast, LiCoO2 or LiNiO2 fibers can be pressed and sintered to form a cathode, without need for a binder or a conductive additive. The inter-grain contacts of the fibers are stronger and have fewer defects than do those of powder particles. These characteristics translate to increased flexibility and greater resilience on cycling and, consequently, to reduced loss of capacity from cycle to cycle. Moreover, in comparison with a powder-based cathode, a fiber-based cathode is expected to exhibit significantly greater ionic and electronic conduction along the axes of the fibers. Results of preliminary charge/discharge-cycling tests suggest that energy densities of LiCoO2- and LiNiO2-fiber cathodes are approximately double those of the corresponding powder-based cathodes.

  6. Advanced cathode materials for high-power applications

    Science.gov (United States)

    Amine, K.; Liu, J.; Belharouak, I.; Kang, S.-H.; Bloom, I.; Vissers, D.; Henriksen, G.

    In our efforts to develop low cost high-power Li-ion batteries with excellent safety, as well as long cycle and calendar life, lithium manganese oxide spinel and layered lithium nickel cobalt manganese oxide cathode materials were investigated. Our studies with the graphite/LiPF 6/spinel cells indicated a very significant degradation of capacity with cycling at 55 °C. This degradation was caused by the reduction of manganese ions on the graphite surface which resulted in a significant increase of the charge-transfer impedance at the anode/electrolyte interface. To improve the stability of the spinel, we investigated an alternative salt that would not generate HF acid that may attack the spinel. The alternative salt we selected for this work was lithium bisoxalatoborate, LiB(C 2O 4) 2 ("LiBoB"). In this case, the graphite/LiBoB/spinel Li-ion cells exhibited much improved cycle/calendar life at 55 °C and better abuse tolerance, as well as excellent power. A second system based on LiNi 1/3Co 1/3Mn 1/3O 2 layered material was also investigated and its performance was compared to commercial LiNi 0.8Co 0.15Al 0.05O 2. Cells based on LiNi 1/3Co 1/3Mn 1/3O 2 showed lower power fade and better thermal safety than the LiNi 0.8Co 0.15Al 0.05O 2-based commercial cells under similar test conditions. Li-ion cells based on the material with excess lithium (Li 1.1Ni 1/3Co 1/3Mn 1/3O 2) exhibited excellent power performance that exceeded the FreedomCAR requirements.

  7. Optimization of Layered Cathode Materials for Lithium-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Christian Julien

    2016-07-01

    Full Text Available This review presents a survey of the literature on recent progress in lithium-ion batteries, with the active sub-micron-sized particles of the positive electrode chosen in the family of lamellar compounds LiMO2, where M stands for a mixture of Ni, Mn, Co elements, and in the family of yLi2MnO3•(1 − yLiNi½Mn½O2 layered-layered integrated materials. The structural, physical, and chemical properties of these cathode elements are reported and discussed as a function of all the synthesis parameters, which include the choice of the precursors and of the chelating agent, and as a function of the relative concentrations of the M cations and composition y. Their electrochemical properties are also reported and discussed to determine the optimum compositions in order to obtain the best electrochemical performance while maintaining the structural integrity of the electrode lattice during cycling.

  8. Particle size effect of Ni-rich cathode materials on lithium ion battery performance

    International Nuclear Information System (INIS)

    Hwang, Ilkyu; Lee, Chul Wee; Kim, Jae Chang; Yoon, Songhun

    2012-01-01

    Graphical abstract: The preparation condition of Ni-rich cathode materials was investigated. When the retention time was short, a poor cathode performance was observed. For long retention time condition, cathode performance displayed a best result at pH 12. Highlights: ► Ni-rich cathode materials (LiNi 0.8 Co 0.15 Al 0.05 O 2 ) were prepared by co-precipitation method using separate addition of Al salt. ► Particle size of Ni-rich cathode materials became larger with increase of retention time and solution pH. ► Cathode performance was poor for low retention time. ► Optimal pH for co-precipitation was 12. -- Abstract: Herein, Ni-rich cathode materials (LiNi 0.8 Co 0.15 Al 0.05 O 2 ) in lithium ion batteries are prepared by a separate addition of Ni/Co salt and Al sol solution using a continuously stirred tank reactor. Retention time and solution pH were controlled in order to obtain high performance cathode material. Particle size increase was observed with a higher retention time of the reactants. Also, primary and secondary particles became smaller according to an increase of solution pH, which was probably due to a decrease of growth rate. From the cathode application, a high discharge capacity (175 mAh g −1 ), a high initial efficiency (90%) and a good cycleability were observed in the cathode material prepared under pH 12 condition, which was attributed to its well-developed layered property and the optimal particle size. However, rate capability was inversely proportional to the particle size, which was clarified by a decrease of charge-transfer resistance measured in the electrochemical impedance spectroscopy.

  9. Polycarbonyl(quinonyl) organic compounds as cathode materials for sustainable lithium ion batteries

    International Nuclear Information System (INIS)

    Zeng, Ronghua; Xing, Lidan; Qiu, Yongcai; Wang, Yating; Huang, Wenna; Li, Weishan; Yang, Shihe

    2014-01-01

    Highlights: • Quinonyl compounds containing –OH groups are reported as cathode of sustainable Li-ion battery. • Lithiation potential of these compounds is positively correlated to -OH group number on them. • These compounds exhibit a discharge plateau of 3 V and deliver a capacity of over 180 mAh g -1 at 20 mA g -1 . - Abstract: Suitably designed organic compounds are promising renewable electrode materials for lithium ion batteries (LIBs) with minimal environmental impacts and no CO 2 release. Herein we report a series of polycarbonyl organic compounds with different number of hydroxyl groups, which can be obtained from renewable plants, as cathode materials for LIBs. Density functional theory (DFT) calculations based on the natural bond orbital (NBO) reveal a positive correlation between the reduction potentials and the number of hydroxyl groups, which is borne out experimentally. Anthraquinone (AQ) with three or four -OH groups has the structural advantages for improving the discharge plateaus. Mechanistic studies show that AQ containing neighbouring carbonyl groups and hydroxyl groups facilitates the formation of six or five-membered rings with lithium ion. Charge/discharge tests show that AQ, 1,5-DHAQ, 1,2,7-THAQ, and 1,2,5,8-THAQ can achieve initial discharge capacities of 215, 190, 186 and 180 mAh g -1 at a current density of 20 mA g -1 , corresponding to 84%, 85%, 89% and 91% of their theoretical capacities, respectively

  10. High-Current Cold Cathode Employing Diamond and Related Materials

    Energy Technology Data Exchange (ETDEWEB)

    Hirshfield, Jay L. [Omega-P, Inc., New Haven, CT (United States)

    2014-10-22

    The essence of this project was for diamond films to be deposited on cold cathodes to improve their emission properties. Films with varying morphology, composition, and size of the crystals were deposited and the emission properties of the cathodes that utilize such films were studied. The prototype cathodes fabricated by the methods developed during Phase I were tested and evaluated in an actual high-power RF device during Phase II. These high-power tests used the novel active RF pulse compression system and the X-band magnicon test facility at US Naval Research Laboratory. In earlier tests, plasma switches were employed, while tests under this project utilized electron-beam switching. The intense electron beams required in the switches were supplied from cold cathodes embodying diamond films with varying morphology, including uncoated molybdenum cathodes in the preliminary tests. Tests with uncoated molybdenum cathodes produced compressed X-band RF pulses with a peak power of 91 MW, and a maximum power gain of 16.5:1. Tests were also carried out with switches employing diamond coated cathodes. The pulse compressor was based on use of switches employing electron beam triggering to effect mode conversion. In experimental tests, the compressor produced 165 MW in a ~ 20 ns pulse at ~18× power gain and ~ 140 MW at ~ 16× power gain in a 16 ns pulse with a ~ 7 ns flat-top. In these tests, molybdenum blade cathodes with thin diamond coatings demonstrated good reproducible emission uniformity with a 100 kV, 100 ns high voltage pulse. The new compressor does not have the limitations of earlier types of active pulse compressors and can operate at significantly higher electric fields without breakdown.

  11. Effect of Metal (Mn, Ti) Doping on NCA Cathode Materials for Lithium Ion Batteries

    OpenAIRE

    Wan, Dao Yong; Fan, Zhi Yu; Dong, Yong Xiang; Baasanjav, Erdenebayar; Jun, Hang-Bae; Jin, Bo; Jin, En Mei; Jeong, Sang Mun

    2018-01-01

    NCA (LiNi0.85Co0.10Al0.05-x MxO2, M=Mn or Ti, x < 0.01) cathode materials are prepared by a hydrothermal reaction at 170°C and doped with Mn and Ti to improve their electrochemical properties. The crystalline phases and morphologies of various NCA cathode materials are characterized by XRD, FE-SEM, and particle size distribution analysis. The CV, EIS, and galvanostatic charge/discharge test are employed to determine the electrochemical properties of the cathode materials. Mn and Ti doping res...

  12. Effect of Cobalt Content on the Electrochemical Properties and Structural Stability of NCA Type Cathode Materials

    OpenAIRE

    Ghatak, Kamalika; Basu, Swastik; Das, Tridip; Kumar, Hemant; Datta, Dibakar

    2018-01-01

    At present, the most common type of cathode materials, NCA [Li_(1-x)Ni_(0.80)Co_(0.15)Al_(0.05)O_(2), x = 0 to 1], have a very high concentration of cobalt. Since cobalt is toxic and expensive, the existing design of cathode materials is neither cost-effective nor environmentally benign. We have performed density functional theory (DFT) calculations to investigate electrochemical, electronic, and structural properties of four types of NCA cathode materials with the simultaneous decrease in Co...

  13. Li2C2, a High-Capacity Cathode Material for Lithium Ion Batteries.

    Science.gov (United States)

    Tian, Na; Gao, Yurui; Li, Yurong; Wang, Zhaoxiang; Song, Xiaoyan; Chen, Liquan

    2016-01-11

    As a typical alkaline earth metal carbide, lithium carbide (Li2C2) has the highest theoretical specific capacity (1400 mA h g(-1)) among all the reported lithium-containing cathode materials for lithium ion batteries. Herein, the feasibility of using Li2C2 as a cathode material was studied. The results show that at least half of the lithium can be extracted from Li2C2 and the reversible specific capacity reaches 700 mA h g(-1). The C≡C bond tends to rotate to form C4 (C≡C⋅⋅⋅C≡C) chains during lithium extraction, as indicated with the first-principles molecular dynamics (FPMD) simulation. The low electronic and ionic conductivity are believed to be responsible for the potential gap between charge and discharge, as is supported with density functional theory (DFT) calculations and Arrhenius fitting results. These findings illustrate the feasibility to use the alkali and alkaline earth metal carbides as high-capacity electrode materials for secondary batteries. © 2016 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  14. Electrochemical Treatment of Wastewater Containing Mixed Reactive Dyes Using Carbon Nanotube Modified Cathode Electrodes

    Directory of Open Access Journals (Sweden)

    Nader Djafarzadeh

    2016-11-01

    Full Text Available Nowadays, advanced electrochemical oxidation processes are promising methods for the treatment of wastewaters containing organic dyes. One of these methods is the Electro-Fenton (EF technique in which an electrical current is applied to the cathode and anode electrodes to promote electrochemical reactions that generate hydroxyl radicals which mineralize organic pollutants and remove them from wastewater. To carry out the Electro-Fenton process iIn this work, the carbon paper (CP electrode was initially modified with carbon nanotubes (CNT to produce the CP-CNT electrode which was used as the cathode to remove a mixture of organic dyestuff (containing Reactive Blue 69, Reactive Red 195, and Reactive Yellow 84 from wastewaters. Comparison of the two types of cathode electrodes (i.e., CNT and the modified CP-CNT showed that the CP-CNT outperformed the CP electrode. The EF process was employed to treat 500 ml of a mixture of dyes (50 mg/L of each dye containing sodium soulfate and Fe+3 ions. The results revealed that the highest color removal efficiency was achieved when a current of 300 mA was applied for 210 min. COD measurments were used to calculate the effective current and power consumption. It was found that the 300 mA current applied over a period of 210 min yielded the highest effective current and the lowest power consumption. The amount of dyes mineralized by the EF process in the dye solution indicated that 78% of the initial COD had been removed under the above conditions. It may be concluded that the Electro-Fenton process can be successfully used for the treatment of wastewaters containing mixtures of dye pollutants. Cathode electrode type, electrical current, and electrolysis duration were identified as the parameters affecting the process.

  15. Quantifying the environmental impact of a Li-rich high-capacity cathode material in electric vehicles via life cycle assessment.

    Science.gov (United States)

    Wang, Yuqi; Yu, Yajuan; Huang, Kai; Chen, Bo; Deng, Wensheng; Yao, Ying

    2017-01-01

    A promising Li-rich high-capacity cathode material (xLi 2 MnO 3 ·(1-x)LiMn 0.5 Ni 0.5 O 2 ) has received much attention with regard to improving the performance of lithium-ion batteries in electric vehicles. This study presents an environmental impact evaluation of a lithium-ion battery with Li-rich materials used in an electric vehicle throughout the life cycle of the battery. A comparison between this cathode material and a Li-ion cathode material containing cobalt was compiled in this study. The battery use stage was found to play a large role in the total environmental impact and high greenhouse gas emissions. During battery production, cathode material manufacturing has the highest environmental impact due to its complex processing and variety of raw materials. Compared to the cathode with cobalt, the Li-rich material generates fewer impacts in terms of human health and ecosystem quality. Through the life cycle assessment (LCA) results and sensitivity analysis, we found that the electricity mix and energy efficiency significantly influence the environmental impacts of both battery production and battery use. This paper also provides a detailed life cycle inventory, including firsthand data on lithium-ion batteries with Li-rich cathode materials.

  16. Defect thiospinels: a new class of reversible cathode material

    Science.gov (United States)

    James, A. C. W. P.; Goodenough, J. B.

    1989-05-01

    The defect thiospinel Cu 0.07[Ti 2]S 4 was prepared by low-temperature oxidative extraction of copper from Cu[Ti 2]S 4. Up to two equivalents of lithium can be inserted into Cu 0.07[Ti 2]S 4 reversibly with fast electrochemical kinetics at room temperature; the defect thiospinel is, therefore, a highly promising alternative to layered TiS 2 as a cathode material for lithium secondary batteries. Samples of Cu 1- x [Ti 2]S 4 (0⩽ x ⩽ 0.93) and Li xCu 0.07[Ti 2]S 4 (0 < x < 2) were prepared and characterised by 65Cu and 7Li solid-state NMR, neutron powder diffraction, and electrochemical measurements. Cu 0.07[Ti 2]S 4 is a semimetal with the residual copper located on the normal spinel A-cation sites. The lithium in Li xCu 0.07[Ti 2]S 4 is located only in the 16c octahedral sites of the spinel framework at all lithium compositions. The open-circuit voltage of Li xCu 0.07[Ti 2]S 4versus lithium metal is nearly identical to that of layered Li xTiS 2 over the whole lithium-composition range. The chemical diffusion constant of lithium in Li xCu 0.07[Ti 2]S 4 (0.5 ⩽ x⩽ 1.5) was found to be 1 × 10 -9 cm 2 s -1, which is comparable with that in layered Li xTiS 2.

  17. Advanced Cathode Material For High Energy Density Lithium-Batteries, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — Advanced cathode materials having high red-ox potential and high specific capacity offer great promise to the development of high energy density lithium-based...

  18. Factors Affecting the Battery Performance of Anthraquinone-based Organic Cathode Materials

    Energy Technology Data Exchange (ETDEWEB)

    Xu, Wu; Read, Adam L.; Koech, Phillip K.; Hu, Dehong; Wang, Chong M.; Xiao, Jie; Padmaperuma, Asanga B.; Graff, Gordon L.; Liu, Jun; Zhang, Jiguang

    2012-02-01

    Two organic cathode materials based on poly(anthraquinonyl sulfide) structure with different substitution positions were synthesized and their electrochemical behavior and battery performances were investigated. The substitution positions on the anthraquinone structure, binders for electrode preparation and electrolyte formulations have been found to have significant effects on the battery performances of such organic cathode materials. The substitution position with less steric stress has higher capacity, longer cycle life and better high-rate capability. Polyvinylidene fluoride binder and ether-based electrolytes are favorable for the high capacity and long cycle life of the quinonyl organic cathodes.

  19. Synthesis of Co-Al-Cl LDH by cathodic material reprocessing from cellular phone batteries

    Energy Technology Data Exchange (ETDEWEB)

    Amaral, Fabio Augusto do; Machado, Erica Oliveira; Freitas, Leonardo Luis de; Santana, Laiane Kalita; Canobre, Sheila Cristina, E-mail: fabioamaral@yahoo.com.br, E-mail: fabioamaral@iqufu.ufu.br [Universidade Federal de Uberlandia (UFU/LAETE), (Brazil). Inst. de Quimica. Lab. de Armazenamento de Energia e Tratamento de Efluente

    2014-08-15

    The aim of this paper was the recovering of the cathodic material from discarded lithium ion batteries for obtainment of the lamellar double hydroxides (LDHs) by the co-precipitation method at variable pH in HCl and H{sub 2}O{sub 2} 1:1 (v/v) acid solution containing Co and Al (extracted from cathodic material composed of LiCoO{sub 2} and aluminum foil). These metals were precipitated in LiOH at pH 9 or 11, or NH{sub 4}OH at pH 9 and submitted to the hydrothermal treatment (HT) to improve the structural organization of the LDHs lamellae. After precipitation, the resulting solids were structurally characterized by XRD for phase identification and calculation of the unit cell parameter, thermally by TGA for the identification of the mass loss and morphologically by SEM. The sample obtained by precipitation with LiOH at pH 11 / hydrothermal treatment showed diffraction peaks similar to hydrotalcite, morphological and thermal characteristics similar to the pattern Co-Al-Cl LDH obtained by co-precipitation at constant pH 8. (author)

  20. Graphene-Based Composites as Cathode Materials for Lithium Ion Batteries

    Directory of Open Access Journals (Sweden)

    Libao Chen

    2013-01-01

    Full Text Available Owing to the superior mechanical, thermal, and electrical properties, graphene was a perfect candidate to improve the performance of lithium ion batteries. Herein, we review the recent advances in graphene-based composites and their application as cathode materials for lithium ion batteries. We focus on the synthesis methods of graphene-based composites and the superior electrochemical performance of graphene-based composites as cathode materials for lithium ion batteries.

  1. High-resolution TEM microscopy study of the creep behaviour of carbon-based cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Wei, E-mail: wwlyzwkj@126.com [College of Materials Science and Engineering, Henan University of Science and Technology, Luoyang 471023 (China); Collaborative Innovation Center of Nonferrous Metals Henan Province, Luoyang 471023 (China); Chen, Weijie [College of Materials Science and Engineering, Henan University of Science and Technology, Luoyang 471023 (China); Collaborative Innovation Center of Nonferrous Metals Henan Province, Luoyang 471023 (China); Gu, Wanduo [Collaborative Innovation Center of Nonferrous Metals Henan Province, Luoyang 471023 (China)

    2017-02-27

    Creep is in close relationship with the materials deterioration and deformation of the cathodes in aluminum reduction cells. The purpose of this work is to obtain the creep mechanism of the carbon cathode for aluminum electrolysis. A modified Rapoport equipment was used for measuring the creep strain of the semi-graphitic cathodes during aluminum electrolysis with CR=2.5 and at temperature of 945 ℃. The arrangement of carbon atom has been studied after hexagonal graphite converting into rhombohedral graphite during aluminum electrolysis by XRD and high-resolution transmission electron microscopy (HRTEM). The creep deformation of the carbon cathode has a close relationship with the mobile dislocation walls. These results will be helpful in controlling the cathode quality and its performance in aluminum reduction cells.

  2. Synthesis and Electrochemical Performance of LixMn2-yCoyO4-dCld Cathode Material

    Science.gov (United States)

    2016-06-13

    Synthesis and Electrochemical Performance of LixMn2-yCoyO4-dCld Cathode Material Terrill B. Atwater, Paula C. Latorre, and Ashley L. Ruth U.S...low toxicity, comparable capacity, and low cost. However, this spinel suffers from capacity fading due to fracturing of the cell structure...dopants of interest include compounds containing Group VIII Row 4 (Fe, Co, and Ni) elements, cobalt in particular. In addition to fabrication method

  3. Preparation of cathode materials for solid oxide solid fuel (SOFC) using gelatin

    International Nuclear Information System (INIS)

    Silva, R.M.; Aquino, F. de M.; Macedo, D.A. de; Sa, A.M.; Galvao, G.O.

    2016-01-01

    Fuel cells are electrochemical devices that convert chemical energy into electrical energy. These devices are basically divided into interconnectors, electrolyte, anode, and cathode. Recently, studies of improvements in microstructural and morphological properties of calcium cobaltate (Ca_3Co_4O_9, C349) has been made regarding its potential use as SOFC cathode for intermediate temperature. Gelatin has proven to be effective as a polymerizing agent in the synthesis of nanocrystalline materials. This work reports the synthesis and characterization of the C349 cathode using commercial gelatin. The structural properties of the material were determined by X-ray diffraction (XRD). Morphological characterization was performed by scanning electron microscopy (SEM). The results showed the formation of the crystalline phase at 900 °C, indicating the effectiveness of the gelatin in the preparation of cathodes for SOFC. (author)

  4. The Impact of Strong Cathodic Polarization on SOC Electrolyte Materials

    DEFF Research Database (Denmark)

    Kreka, Kosova; Hansen, Karin Vels; Jacobsen, Torben

    2016-01-01

    One of the most promising reversible energy conversion/storage technologies is that of Solid Oxide Fuel/Electrolysis Cells (SOFC/SOEC, collectively termed SOC). Long term durability is typically required for such devises to become economically feasible, hence considerable amount of work has...... of impurities at the grain boundaries, electrode poisoning, delamination or cracks of the electrolyte etc., have been observed in cells operated at such conditions, lowering the lifetime of the cell1,2. High polarizations are observed at the electrolyte/cathode interface of an electrolysis cell operated at high...... current density. In case of a cell voltage above 1.6 V, p-type and n-type electronic conductivity are often observed at the anode and cathode respectively3. Hence, a considerable part of the current is lost as leakage through the electrolyte, thus lowering the efficiency of the cell considerably....

  5. Packet D: Fuel containing materials

    International Nuclear Information System (INIS)

    Tokarevskij, V.V.

    1999-01-01

    The tasks of the project 'D' are: increase of nuclear safety by fuel containing mass (FCM) characterisation, and development of a preliminary plan for FCM management which should be accomplished by FCM extraction

  6. Transport containers for radioactive material

    International Nuclear Information System (INIS)

    Bibby, D.

    1978-01-01

    A transport container for transporting irradiated nuclear fuel is described comprising a steel flask with detachable cover and having external heat exchange fins. The flask contains a solid annular shield comprised of discrete bodies of Pb or Fe bonded together by a solid matrix, for attenuating gamma rays and neutron emission. This may comprise lead shot bonded together by concrete or polyethylene, or alternatively iron shot bonded by concrete. (UK)

  7. Dry containment of radioactive materials

    International Nuclear Information System (INIS)

    Williams, C.E.

    1980-01-01

    A cask for the dry containment of radioactive fuel elements is described. The cask has a cover which contains valved drain and purge passageways. These passageways are sealed by after purge cover seals which are clamped over them and to the outer surface of the cover. The cover seals are tested by providing them with a pair of concentric ring seal elements squeezed between the cover seal and the outer surface of the cover and by forcing a gas under pressure into the annular region between the seal element

  8. Effect of Metal (Mn, Ti Doping on NCA Cathode Materials for Lithium Ion Batteries

    Directory of Open Access Journals (Sweden)

    Dao Yong Wan

    2018-01-01

    Full Text Available NCA (LiNi0.85Co0.10Al0.05-x MxO2, M=Mn or Ti, x < 0.01 cathode materials are prepared by a hydrothermal reaction at 170°C and doped with Mn and Ti to improve their electrochemical properties. The crystalline phases and morphologies of various NCA cathode materials are characterized by XRD, FE-SEM, and particle size distribution analysis. The CV, EIS, and galvanostatic charge/discharge test are employed to determine the electrochemical properties of the cathode materials. Mn and Ti doping resulted in cell volume expansion. This larger volume also improved the electrochemical properties of the cathode materials because Mn4+ and Ti4+ were introduced into the octahedral lattice space occupied by the Li-ions to expand the Li layer spacing and, thereby, improved the lithium diffusion kinetics. As a result, the NCA-Ti electrode exhibited superior performance with a high discharge capacity of 179.6 mAh g−1 after the first cycle, almost 23 mAh g−1 higher than that obtained with the undoped NCA electrode, and 166.7 mAh g−1 after 30 cycles. A good coulombic efficiency of 88.6% for the NCA-Ti electrode is observed based on calculations in the first charge and discharge capacities. In addition, the NCA-Ti cathode material exhibited the best cycling stability of 93% up to 30 cycles.

  9. Preparation and Characterization of Cathode Materials for Lithium-Oxygen Batteries

    DEFF Research Database (Denmark)

    Storm, Mie Møller

    A possible future battery type is the Li-air battery which theoretically has the potential of reaching gravimetric energy densities close to those of gasoline. The Li-airbattery is discharged by the reaction of Li-ions and oxygen, drawn from the air, reacting at the battery cathode to form Li2O2....... The type of cathode material affects the battery discharge capacity and charging potential and with a carbon based cathode many questions are still unanswered. The focus of this Ph.D. project has been the synthesis of reduced graphene oxide as well as the investigation of the effect of reduced graphene...... the discharge capacity of the battery as well as the charging potential. In situ X-ray diffraction studies on carbon black cathodes in a capillary battery showed the formation of crystalline Li2O2 on the first discharge cycle, the intensity of Li2O2 on the second discharge cycle was however diminished...

  10. Materials for high-level waste containment

    International Nuclear Information System (INIS)

    Marsh, G.P.

    1982-01-01

    The function of the high-level radioactive waste container in storage and of a container/overpack combination in disposal is considered. The consequent properties required from potential fabrication materials are discussed. The strategy adopted in selecting containment materials and the experimental programme underway to evaluate them are described. (U.K.)

  11. Statistical analysis on hollow and core-shell structured vanadium oxide microspheres as cathode materials for Lithium ion batteries

    Directory of Open Access Journals (Sweden)

    Xing Liang

    2018-06-01

    Full Text Available In this data, the statistical analyses of vanadium oxide microspheres cathode materials are presented for the research article entitled “Statistical analyses on hollow and core-shell structured vanadium oxides microspheres as cathode materials for Lithium ion batteries” (Liang et al., 2017 [1]. This article shows the statistical analyses on N2 adsorption-desorption isotherm and morphology vanadium oxide microspheres as cathode materials for LIBs. Keywords: Adsorption-desorption isotherm, Pore size distribution, SEM images, TEM images

  12. Storage containers for radioactive material

    International Nuclear Information System (INIS)

    Cassidy, D.A.; Dates, L.R.; Groh, E.F.

    1981-01-01

    A radioactive material storage system is disclosed for use in the laboratory. This system is composed of the following: a flat base plate with a groove in one surface thereof and a hollow pedestal extending perpendicularly away from the other surface thereof; a sealing gasket in the groove, a cover having a filter therein and an outwardly extending flange which fits over the plate; the groove and the gasket, and a clamp for maintaining the cover and the plate are sealed together, whereby the plate and the cover and the clamp cooperate to provide a storage area for radioactive material readily accessible for use or inventory. Wall mounts are provided to prevent accidental formation of critical masses during storage

  13. Cathode and electrolyte materials for solid oxide fuel cells and ion transport membranes

    Science.gov (United States)

    Jacobson, Allan J; Wang, Shuangyan; Kim, Gun Tae

    2014-01-28

    Novel cathode, electrolyte and oxygen separation materials are disclosed that operate at intermediate temperatures for use in solid oxide fuel cells and ion transport membranes based on oxides with perovskite related structures and an ordered arrangement of A site cations. The materials have significantly faster oxygen kinetics than in corresponding disordered perovskites.

  14. Cathode material for lithium ion accumulators prepared by screen printing for Smart Textile applications

    Science.gov (United States)

    Syrový, T.; Kazda, T.; Syrová, L.; Vondrák, J.; Kubáč, L.; Sedlaříková, M.

    2016-03-01

    The presented study is focused on the development of LiFePO4 based cathode for thin and flexible screen printed secondary lithium based accumulators. An ink formulation was developed for the screen printing technique, which enabled mass production of accumulator's cathode for Smart Label and Smart Textile applications. The screen printed cathode was compared with an electrode prepared by the bar coating technique using an ink formulation based on the standard approach of ink composition. Obtained LiFePO4 cathode layers were characterized by scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and galvanostatic charge/discharge measurements at different loads. The discharge capacity, capacity retention and stability at a high C rate of the LiFePO4 cathode were improved when Super P and PVDF were replaced by conductive polymers PEDOT:PSS. The achieved capacity during cycling at various C rates was approximately the same at the beginning and at the end, and it was about 151 mAh/g for cycling under 1C. The obtained results of this novelty electrode layer exceed the parameters of several electrode layers based on LiFePO4 published in literature in terms of capacity, cycling stability and overcomes them in terms of simplicity/industrial process ability of cathode layer fabrication and electrode material preparation.

  15. Radiation Shielding Materials and Containers Incorporating Same

    Energy Technology Data Exchange (ETDEWEB)

    Mirsky, Steven M.; Krill, Stephen J.; and Murray, Alexander P.

    2005-11-01

    An improved radiation shielding material and storage systems for radioactive materials incorporating the same. The PYRolytic Uranium Compound (''PYRUC'') shielding material is preferably formed by heat and/or pressure treatment of a precursor material comprising microspheres of a uranium compound, such as uranium dioxide or uranium carbide, and a suitable binder. The PYRUC shielding material provides improved radiation shielding, thermal characteristic, cost and ease of use in comparison with other shielding materials. The shielding material can be used to form containment systems, container vessels, shielding structures, and containment storage areas, all of which can be used to house radioactive waste. The preferred shielding system is in the form of a container for storage, transportation, and disposal of radioactive waste. In addition, improved methods for preparing uranium dioxide and uranium carbide microspheres for use in the radiation shielding materials are also provided.

  16. 78 FR 16709 - Certain Cold Cathode Fluorescent Lamp (“CCFL”) Inverter Circuits and Products Containing Same...

    Science.gov (United States)

    2013-03-18

    ... INTERNATIONAL TRADE COMMISSION [Investigation No. 337-TA-666 (Modification Proceeding)] Certain Cold Cathode Fluorescent Lamp (``CCFL'') Inverter Circuits and Products Containing Same; Commission's... inverter circuits and products containing the same by reason of infringement of various U.S. patents. The...

  17. Radioactive materials transporting container and vehicles

    International Nuclear Information System (INIS)

    Reese, S.L.

    1980-01-01

    A container and vehicle therefor for transporting radioactive materials is provided. The container utilizes a removable system of heat conducting fins made of a light weight highly heat conductive metal, such as aluminum or aluminum alloys. This permits a substantial reduction in the weight of the container during transport, increases the heat dissipation capability of the container and substantially reduces the scrubbing operation after loading and before unloading the radioactive material from the container. The vehicle utilizes only a pair of horizontal side beams interconnecting a pair of yoke members to support the container and provide the necessary strength and safety with a minimum of weight

  18. Li-rich layer-structured cathode materials for high energy Li-ion batteries

    Science.gov (United States)

    Li, Liu; Lee, Kim Seng; Lu, Li

    2014-08-01

    Li-rich layer-structured xLi2MnO3 ṡ (1 - x)LiMO2 (M = Mn, Ni, Co, etc.) materials have attracted much attention due to their extraordinarily high reversible capacity as the cathode material in Li-ion batteries. To better understand the nature of this type of materials, this paper reviews history of development of the Li-rich cathode materials, and provides in-depth study on complicated crystal structures and reaction mechanisms during electrochemical charge/discharge cycling. Despite the fabulous capability at low rate, several drawbacks still gap this type of high-capacity cathode materials from practical applications, for instance the large irreversible capacity loss at first cycle, poor rate capability, severe voltage decay and capacity fade during electrochemical charge/discharge cycling. This review will also address mechanisms for these inferior properties and propose various possible solutions to solve above issues for future utilization of these cathode materials in commercial Li-ion batteries.

  19. High-energy cathode material for long-life and safe lithium batteries

    Science.gov (United States)

    Sun, Yang-Kook; Myung, Seung-Taek; Park, Byung-Chun; Prakash, Jai; Belharouak, Ilias; Amine, Khalil

    2009-04-01

    Layered lithium nickel-rich oxides, Li[Ni1-xMx]O2 (M=metal), have attracted significant interest as the cathode material for rechargeable lithium batteries owing to their high capacity, excellent rate capability and low cost. However, their low thermal-abuse tolerance and poor cycle life, especially at elevated temperature, prohibit their use in practical batteries. Here, we report on a concentration-gradient cathode material for rechargeable lithium batteries based on a layered lithium nickel cobalt manganese oxide. In this material, each particle has a central bulk that is rich in Ni and a Mn-rich outer layer with decreasing Ni concentration and increasing Mn and Co concentrations as the surface is approached. The former provides high capacity, whereas the latter improves the thermal stability. A half cell using our concentration-gradient cathode material achieved a high capacity of 209mAhg-1 and retained 96% of this capacity after 50 charge-discharge cycles under an aggressive test profile (55∘C between 3.0 and 4.4V). Our concentration-gradient material also showed superior performance in thermal-abuse tests compared with the bulk composition Li[Ni0.8Co0.1Mn0.1]O2 used as reference. These results suggest that our cathode material could enable production of batteries that meet the demanding performance and safety requirements of plug-in hybrid electric vehicles.

  20. Monitoring local redox processes in LiNi0.5Mn1.5O4 battery cathode material by in operando EPR spectroscopy

    Science.gov (United States)

    Niemöller, Arvid; Jakes, Peter; Eurich, Svitlana; Paulus, Anja; Kungl, Hans; Eichel, Rüdiger-A.; Granwehr, Josef

    2018-01-01

    Despite the multitude of analytical methods available to characterize battery cathode materials, identifying the factors responsible for material aging is still challenging. We present the first investigation of transient redox processes in a spinel cathode during electrochemical cycling of a lithium ion battery by in operando electron paramagnetic resonance (EPR). The battery contains a LiNi0.5Mn1.5O4 (LNMO) spinel cathode, which is a material whose magnetic interactions are well understood. The evolution of the EPR signal in combination with electrochemical measurements shows the impact of Mn3+ on the Li+ motion inside the spinel. Moreover, state of charge dependent linewidth variations confirm the formation of a solid solution for slow cycling, which is taken over by mixed models of solid solution and two-phase formation for fast cycling due to kinetic restrictions and overpotentials. Long-term measurements for 480 h showed the stability of the investigated LNMO, but also small amounts of cathode degradation products became visible. The results point out how local, exchange mediated magnetic interactions in cathode materials are linked with battery performance and can be used for material characterization.

  1. Synthesis of lithium nickel cobalt manganese oxide cathode materials by infrared induction heating

    Science.gov (United States)

    Hsieh, Chien-Te; Chen, Yu-Fu; Pai, Chun-Ting; Mo, Chung-Yu

    2014-12-01

    This study adopts an in-situ infrared (IR) sintering incorporated with carbonization technique to synthesize carbon-coated LiNi1/3Co1/3Mn1/3O2 (LNCM) cathode materials for Li-ion batteries. Compared with electric resistance heating, the in-situ IR sintering is capable of rapidly producing highly-crystalline LNCM powders at 900 °C within a short period, i.e., 3 h in this case. Glucose additive is employed to serve a carbon precursor, which is carbonized and coated over the surface of LNCM crystals during the IR sintering process. The electrochemical performance of LNCM cathodes is well examined by charge-discharge cycling at 0.1-5C. An appropriate carbon coating is capable of raising discharge capacity (i.e., 181.5 mAh g-1 at 0.1C), rate capability (i.e., 75.0 mAh g-1 at 5C), and cycling stability (i.e., capacity retention: 94.2% at 1C after 50 cycles) of LNCM cathodes. This enhanced performance can be ascribed to the carbon coating onto the external surface of LNCM powders, creating an outer circuit of charge-transfer pathway and preventing cathode corrosion from direct contact to the electrolyte. Accordingly, the in-situ IR sintering technique offers a potential feasibility for synthesizing cathode materials commercially in large scale.

  2. Microwave synthesis of copper network onto lithium iron phosphate cathode materials for improved electrochemical performance

    Energy Technology Data Exchange (ETDEWEB)

    Hsieh, Chien-Te, E-mail: cthsieh@saturn.yzu.edu.tw [Department of Chemical Engineering and Materials Science, Yuan Ze University, Taoyuan 320, Taiwan (China); Liu, Juan-Ru [Department of Chemical Engineering and Materials Science, Yuan Ze University, Taoyuan 320, Taiwan (China); Juang, Ruey-Shin [Department of Chemical and Materials Engineering, Chang Gung University, Taoyuan 333, Taiwan (China); Lee, Cheng-En; Chen, Yu-Fu [Department of Chemical Engineering and Materials Science, Yuan Ze University, Taoyuan 320, Taiwan (China)

    2015-03-01

    Herein reported is an efficient microwave-assisted (MA) approach for growing Cu network onto LiFePO{sub 4} (LFP) powders as cathode materials for high-performance Li-ion batteries. The MA approach is capable of depositing highly-porous Cu network, fully covered the LFP powders. The electrochemical performance of Cu-coated LFP cathodes are well characterized by charge/discharge cycling and electrochemical impedance spectroscopy (EIS). The Cu network acts as the key role in improving the specific capacity, rate capability, electrode polarization, as compared to fresh LFP cathode without the Cu coating. The EIS incorporated with equivalent circuit reveals that the completed Cu network obviously suppresses the charge transfer resistance. This result can be attributed to the fact that the Cu network ensures the LFP crystals to get electron easily, alleviating the electrode polarization in view of one-dimensional Li{sup +} ion mobility in the olivine crystals. Based on the analysis of Randles plots, the relatively higher Li{sup +} diffusion coefficient reflects the more efficient Li{sup +} pathway in the LFP powders through the aid of porous Cu network. - Highlights: • An efficient route was used to prepare Cu/LiFePO{sub 4} (LFP) hybrid as cathode material. • The Cu/LFP cathodes exhibit an improved performance as compared to fresh LFP one. • The microwave approach can deposit Cu network, fully covered the LFP powders. • The Cu network ensures LFP to get electrons, alleviating electrode polarization.

  3. Microwave synthesis of copper network onto lithium iron phosphate cathode materials for improved electrochemical performance

    International Nuclear Information System (INIS)

    Hsieh, Chien-Te; Liu, Juan-Ru; Juang, Ruey-Shin; Lee, Cheng-En; Chen, Yu-Fu

    2015-01-01

    Herein reported is an efficient microwave-assisted (MA) approach for growing Cu network onto LiFePO 4 (LFP) powders as cathode materials for high-performance Li-ion batteries. The MA approach is capable of depositing highly-porous Cu network, fully covered the LFP powders. The electrochemical performance of Cu-coated LFP cathodes are well characterized by charge/discharge cycling and electrochemical impedance spectroscopy (EIS). The Cu network acts as the key role in improving the specific capacity, rate capability, electrode polarization, as compared to fresh LFP cathode without the Cu coating. The EIS incorporated with equivalent circuit reveals that the completed Cu network obviously suppresses the charge transfer resistance. This result can be attributed to the fact that the Cu network ensures the LFP crystals to get electron easily, alleviating the electrode polarization in view of one-dimensional Li + ion mobility in the olivine crystals. Based on the analysis of Randles plots, the relatively higher Li + diffusion coefficient reflects the more efficient Li + pathway in the LFP powders through the aid of porous Cu network. - Highlights: • An efficient route was used to prepare Cu/LiFePO 4 (LFP) hybrid as cathode material. • The Cu/LFP cathodes exhibit an improved performance as compared to fresh LFP one. • The microwave approach can deposit Cu network, fully covered the LFP powders. • The Cu network ensures LFP to get electrons, alleviating electrode polarization

  4. Is alpha-V2O5 a cathode material for Mg insertion batteries?

    Energy Technology Data Exchange (ETDEWEB)

    Sa, Niya; Wang, Hao; Proffit, Danielle L.; Lipson, Albert L.; Key, Baris; Liu, Miao; Feng, Zhenxing; Fister, Timothy T.; Ren, Yang; Sun, Cheng-Jun; Vaughey, John T.; Fenter, Paul A.; Persson, Kristin A.; Burrell, Anthony K.

    2016-08-01

    When designing a high energy density battery, one of the critical features is a high voltage, high capacity cathode material. In the development of Mg batteries, oxide cathodes that can reversibly intercalate Mg, while at the same time being compatible with an electrolyte that can deposit Mg reversibly are rare. Herein, we report the compatibility of Mg anodes with a-V2O5 by employing magnesium bis(trifluoromethane sulfonyl)imide in diglyme electrolytes at very low water levels. Electrolytes that contain a high water level do not reversibly deposit Mg, but interestingly these electrolytes appear to enable much higher capacities for an a-V2O5 cathode. Solid state NMR indicates that the major source of the higher capacity in high water content electrolytes originates from reversible proton insertion. In contrast, we found that lowering the water level of the magnesium bis(trifluoromethane sulfonyl)imide in diglyme electrolyte is critical to achieve reversible Mg deposition and direct evidence for reversible Mg intercalation is shown. Findings we report here elucidate the role of proton intercalation in water-containing electrolytes and clarify numerous conflicting reports of Mg insertion into a-V2O5.

  5. Fe-N-C catalyst modified graphene sponge as a cathode material for lithium-oxygen battery

    International Nuclear Information System (INIS)

    Yu, Ling; Shen, Yue; Huang, Yunhui

    2014-01-01

    Highlights: • Hydrothermally-synthesized graphene sponge is excellent skeleton of Li-O 2 cathode. • Fe-N-C catalyst loaded on GS was attained via pyrolysis of FePc and GS composites. • High capacity and good cyclability were achieved with Fe-N-GS air electrode. • The synergy of porous structure and catalytic activity leads to the high performance. - Abstract: The cathode of a lithium-oxygen battery needs the synergism of a porous conducting material and a catalyst to facilitate the formation and decomposition of lithium peroxide. Here we introduce a graphene sponge (GS) modified with Fe-N-C catalyst for the oxygen reduction reaction (ORR) and the oxygen evolution reaction (OER). The porous, 3-dimensional conductive and free standing nature of the graphene sponge makes it become excellent skeleton of cathode for lithium-oxygen battery. The Fe-N-C catalyst nanoparticles dispersed uniformly on the graphene sheets show excellent catalytic reactivity in both discharge and charge processes. This kind of composite material greatly improves the capacity and cyclability of the lithium-oxygen battery. With dimethyl sulphoxide as electrolyte, the capacity reaches 6762 mAh g −1 which is twice of the pure graphene sponge. In addition, the cell containing Fe-N-GS air electrode exhibits stable cyclic performance and effective reduction of charge potential plateau, indicating that Fe-N-GS is promising as an OER catalyst in rechargeable lithium-air batteries

  6. Experimental Investigations into U/TRU Recovery using a Liquid Cadmium Cathode and Salt Containing High Rare Earth Concentrations

    Energy Technology Data Exchange (ETDEWEB)

    Shelly X. Li; Steven D. Herrmann; Michael F. Simpson

    2009-09-01

    Experimental Investigations into U/TRU Recovery using a Liquid Cadmium Cathode and Salt Containing High Rare Earth Concentrations Shelly X. Li, Steven D. Herrmann, and Michael F. Simpson Pyroprocessing Technology Department Idaho National Laboratory P.O. Box 1625, Idaho Falls, ID 83415 USA Abstract - A series of six bench-scale liquid cadmium cathode (LCC) tests was performed to obtain basic separation data with focus on the behavior of rare earth elements. The electrolyte used for the tests was a mixed salt from the Mk-IV and Mk-V electrorefiners, in which spent metal fuels from Experimental Breeder Reactor-II (EBR-II) had been processed. Rare earth (RE) chlorides, such as NdCl3, CeCl3, LaCl3, PrCl3, SmCl3, and YCl3, were spiked into the salt prior to the first test to create an extreme case for investigating rare earth contamination of the actinides collected by a LCC. For the first two LCC tests, an alloy with the nominal composition of 41U-30Pu-5Am-3Np-20Zr-1RE was loaded into the anode baskets as the feed material. The anode feed material for Runs 3 to 6 was spent ternary fuel (U-19Pu-10Zr). The Pu/U ratio in the salt varied from 0.6 to 1.3. Chemical and radiochemical analytical results confirmed that U and transuranics can be collected into the LCC as a group under the given run conditions. The RE contamination level in the LCC product was up to 6.7 wt% of the total metal collected. The detailed data for partitioning of actinides and REs in the salt and Cd phases are reported in the paper.

  7. Study of bismuth oxide compounds as cathodic materials in lithium accumulators

    International Nuclear Information System (INIS)

    Apostolova, R.D.; Shembel', E.M.

    1999-01-01

    Two groups of bismuth oxide base compounds: rare earth bismuthides - SmBiO 3 and EuBiO 3 , as well as the Aurivillius phase - Bi 4 V 2 O 11 , were synthesized and electrochemically studied as novel cathodic materials for high-energy lithium current sources [ru

  8. Comparison of gap frame designs and materials for precision cathode strip chambers

    International Nuclear Information System (INIS)

    Horvath, J.A.; Pratuch, S.M.; Belser, F.C.

    1993-01-01

    Precision cathode strip chamber perimeter designs that incorporate either continuous or discrete-post gap frames are analyzed. The effects of ten design and material combinations on gravity sag, mass, stress, and deflected shape are evaluated. Procedures are recommended for minimizing mass in the chamber perimeter region while retaining structural integrity and electrical design latitude

  9. Nickel Hexacyanoferrate Nanoparticles as a Low Cost Cathode Material for Lithium-Ion Batteries

    International Nuclear Information System (INIS)

    Omarova, Marzhana; Koishybay, Aibolat; Yesibolati, Nulati; Mentbayeva, Almagul; Umirov, Nurzhan; Ismailov, Kairat; Adair, Desmond; Babaa, Moulay-Rachid; Kurmanbayeva, Indira; Bakenov, Zhumabay

    2015-01-01

    Potassium nickel hexacyanoferrate KNi[Fe(CN) 6 ] (NiHCF) was synthesized by a simple co-precipitation method and investigated as a cathode material for lithium-ion batteries. The X-ray diffraction and transmission electron microscopy studies revealed the formation of pure phase of agglomerated NiHCF nanoparticles of about 20–50 nm in size. The material exhibited stable cycling performance as a cathode in a lithium half-cell within a wide range of current densities, and a working potential around 3.3 V vs. Li + /Li. The lithium ion diffusion coefficient in this system was determined to be in a range of 10 −9 to 10 −8 cm 2 s −1 , which is within the values for the cathode materials for lithium-ion batteries with high rate capability. Considering promising electrochemical performance and attractive lithium-ion diffusion properties of this material along with its economical benefits and simplified preparation, NiHCF could be considered as a very promising cathode for large scale lithium-ion batteries.

  10. One-Pot Synthesis of Lithium-Rich Cathode Material with Hierarchical Morphology.

    Science.gov (United States)

    Luo, Kun; Roberts, Matthew R; Hao, Rong; Guerrini, Niccoló; Liberti, Emanuela; Allen, Christopher S; Kirkland, Angus I; Bruce, Peter G

    2016-12-14

    Lithium-rich transition metal oxides, Li 1+x TM 1-x O 2 (TM, transition metal), have attracted much attention as potential candidate cathode materials for next generation lithium ion batteries because their high theoretical capacity. Here we present the synthesis of Li[Li 0.2 Ni 0.2 Mn 0.6 ]O 2 using a facile one-pot resorcinol-formaldehyde method. Structural characterization indicates that the material adopts a hierarchical porous morphology consisting of uniformly distributed small pores and disordered large pore structures. The material exhibits excellent electrochemical cycling stability and a good retention of capacity at high rates. The material has been shown to be both advantageous in terms of gravimetric and volumetric capacities over state of the art commercial cathode materials.

  11. Building up an electrocatalytic activity scale of cathode materials for organic halide reductions

    International Nuclear Information System (INIS)

    Bellomunno, C.; Bonanomi, D.; Falciola, L.; Longhi, M.; Mussini, P.R.; Doubova, L.M.; Di Silvestro, G.

    2005-01-01

    A wide investigation on the electrochemical activity of four model organic bromides has been carried out in acetonitrile on nine cathodes of widely different affinity for halide anions (Pt, Zn, Hg, Sn, Bi, Pb, Au, Cu, Ag), and the electrocatalytic activities of the latter have been evaluated with respect to three possible inert reference cathode materials, i.e. glassy carbon, boron-doped diamond, and fluorinated boron-doped diamond. A general electrocatalytic activity scale for the process is proposed, with a discussion on its modulation by the configuration of the reacting molecule, and its connection with thermodynamic parameters accounting for halide adsorption

  12. Cathodes for lithium ion batteries: the benefits of using nanostructured materials

    International Nuclear Information System (INIS)

    Bazito, Fernanda F.C.; Torresi, Roberto M.

    2006-01-01

    Commercially available lithium ion cells, which are the most advanced among rechargeable batteries available so far, employ microcrystalline transition metal oxides as cathodes, which function as Li insertion hosts. In search for better electrochemical performance the use of nanomaterials in place of these conventional ones has emerged as excellent alternative. In this review we present a brief introduction about the motivations to use nanostructured materials as cathodes in lithium ion batteries. To illustrate such advantages we present some examples of research directed toward preparations and electrochemical data of the most used cathodes in nanoscale, such as LiCoO 2 , LiMn 2 O 4 , LiMnO 2 , LiV 2 O 5 e LiFePO 4 . (author)

  13. Highly Graphitic Carbon Nanofibers Web as a Cathode Material for Lithium Oxygen Batteries

    Directory of Open Access Journals (Sweden)

    Hyungkyu Han

    2018-01-01

    Full Text Available The lithium oxygen battery is a promising energy storage system due to its high theoretical energy density and ability to use oxygen from air as a “fuel”. Although various carbonaceous materials have been widely used as a cathode material due to their high electronic conductivity and facial processability, previous studies mainly focused on the electrochemical properties associated with the materials (such as graphene and carbon nanotubes and the electrode configuration. Recent reports demonstrated that the polarization associated with cycling could be significantly increased by lithium carbonates generated from the reaction between the carbon cathode and an electrolyte, which indicates that the physicochemical properties of the carbon cathode could play an important role on the electrochemical performances. However, there is no systematic study to understand these phenomena. Here, we systematically explore the electrochemical properties of carbon nanofibers (CNF webs with different graphitization degree as a cathode for Li oxygen batteries. The physicochemical properties and electrochemical properties of CNF webs were carefully monitored before and after cycling. CNF webs are prepared at 1000, 1200 and 1400 °C. CNF web pyrolyzed at 1400 °C shows lowered polarization and improved cycle retention compared to those of CNF webs pyrolyzed at 1000 and 1200 °C.

  14. Recent advances on Fe- and Mn-based cathode materials for lithium and sodium ion batteries

    Science.gov (United States)

    Zhu, Xiaobo; Lin, Tongen; Manning, Eric; Zhang, Yuancheng; Yu, Mengmeng; Zuo, Bin; Wang, Lianzhou

    2018-06-01

    The ever-growing market of electrochemical energy storage impels the advances on cost-effective and environmentally friendly battery chemistries. Lithium-ion batteries (LIBs) are currently the most critical energy storage devices for a variety of applications, while sodium-ion batteries (SIBs) are expected to complement LIBs in large-scale applications. In respect to their constituent components, the cathode part is the most significant sector regarding weight fraction and cost. Therefore, the development of cathode materials based on Earth's abundant elements (Fe and Mn) largely determines the prospects of the batteries. Herein, we offer a comprehensive review of the up-to-date advances on Fe- and Mn-based cathode materials for LIBs and SIBs, highlighting some promising candidates, such as Li- and Mn-rich layered oxides, LiNi0.5Mn1.5O4, LiFe1-xMnxPO4, NaxFeyMn1-yO2, Na4MnFe2(PO4)(P2O7), and Prussian blue analogs. Also, challenges and prospects are discussed to direct the possible development of cost-effective and high-performance cathode materials for future rechargeable batteries.

  15. Activated graphene as a cathode material for Li-ion hybrid supercapacitors.

    Science.gov (United States)

    Stoller, Meryl D; Murali, Shanthi; Quarles, Neil; Zhu, Yanwu; Potts, Jeffrey R; Zhu, Xianjun; Ha, Hyung-Wook; Ruoff, Rodney S

    2012-03-14

    Chemically activated graphene ('activated microwave expanded graphite oxide', a-MEGO) was used as a cathode material for Li-ion hybrid supercapacitors. The performance of a-MEGO was first verified with Li-ion electrolyte in a symmetrical supercapacitor cell. Hybrid supercapacitors were then constructed with a-MEGO as the cathode and with either graphite or Li(4)Ti(5)O(12) (LTO) for the anode materials. The results show that the activated graphene material works well in a symmetrical cell with the Li-ion electrolyte with specific capacitances as high as 182 F g(-1). In a full a-MEGO/graphite hybrid cell, specific capacitances as high as 266 F g(-1) for the active materials at operating potentials of 4 V yielded gravimetric energy densities for a packaged cell of 53.2 W h kg(-1).

  16. Asbestos-Containing Materials (ACM) and Demolition

    Science.gov (United States)

    There are specific federal regulatory requirements that require the identification of asbestos-containing materials (ACM) in many of the residential buildings that are being demolished or renovated by a municipality.

  17. Storage vessel for containing radiation contaminated material

    International Nuclear Information System (INIS)

    Ogawa, Kazuya.

    1995-01-01

    A container pipe and an outer pipe are coaxially assembled integrally in a state where securing spacers are disposed between the container pipe and the outer pipe, and an annular flow channel is formed around the container pipe. Radiation contaminated material-containing body (glass solidified package) is contained in the container pipe. The container pipe and the outer pipe in an integrated state are suspended from a ceiling plug of a cell chamber of a storage vessel, and supporting devices are assembled between the pipes and a support structure. A shear/lug mechanism is used for the supporting devices. The combination of the shear/lug allows radial and vertical movement but restrict horizontal movement of the outer tube. The supporting devices are assembled while visually recognizing the state of the shear/lug mechanism between the outer pipe and the support mechanism. Accordingly, operationability upon assembling the container pipe and the outer pipe is improved. (I.N.)

  18. Use of limestone powder during incorporation of Pb-containing cathode ray tube waste in self-compacting concrete.

    Science.gov (United States)

    Sua-iam, Gritsada; Makul, Natt

    2013-10-15

    For several decades, cathode ray tubes (CRTs) were the primary display component of televisions and computers. The CRT glass envelope contains sufficient levels of lead oxide (PbO) to be considered hazardous, and there is a need for effective methods of permanently encapsulating this material during waste disposal. We examined the effect of adding limestone powder (LS) on the fresh and cured properties of self-compacting concrete (SCC) mixtures containing waste CRT glass. The SCC mixtures were prepared using Type 1 Portland cement at a constant cement content of 600 kg/m(3) and a water-to-cement ratio (w/c) of 0.38. CRT glass waste cullet was blended with river sand in proportions of 20 or 40% by weight. To suppress potential viscosity effects limestone powder was added at levels of 5, 10, or 15% by weight. The slump flow time, slump flow diameter, V-funnel flow time, Marsh cone flow time, and setting time of the fresh concrete were tested, as well as the compressive strength and ultrasonic pulse velocity of the hardened concrete. Addition of limestone powder improved the fresh and hardened properties. Pb leaching levels from the cured concrete were within US EPA allowable limits. Copyright © 2013 Elsevier Ltd. All rights reserved.

  19. Structural and Chemical Evolution of Li- and Mn-rich Layered Cathode Material

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming; Xu, Pinghong; Gu, Meng; Xiao, Jie; Browning, Nigel D.; Yan, Pengfei; Wang, Chong M.; Zhang, Jiguang

    2015-02-24

    Lithium (Li)- and manganese-rich (LMR) layered-structure materials are very promising cathodes for high energy density lithium-ion batteries. However, their voltage fading mechanism and its relationships with fundamental structural changes are far from being sufficiently understood. Here we report the detailed phase transformation pathway in the LMR cathode (Li[Li0.2Ni0.2Mn0.6]O2) during cycling for the samples prepared by hydro-thermal assistant method. It is found the transformation pathway of LMR cathode is closely correlated to its initial structure and preparation conditions. The results reveal that LMR cathode prepared by HA approach experiences a phase transformation from the layered structure to a LT-LiCoO2 type defect spinel-like structure (Fd-3m space group) and then to a disordered rock-salt structure (Fm-3m space group). The voltage fade can be well correlated with the Li ion insertion into octahedral sites, rather than tetrahedral sites, in both defect spinel-like structure and disordered rock-salt structure. The reversible Li insertion/removal into/from the disordered rock-salt structure is ascribed to the Li excess environment that can satisfy the Li percolating in the disordered rock-salt structure despite the increased kinetic barrier. Meanwhile, because of the presence of a great amount of oxygen vacancies, a significant decrease of Mn valence is detected in the cycled particle, which is below that anticipated for a potentially damaging Jahn-Teller distortion (+3.5). Clarification of the phase transformation pathway, cation redistribution, oxygen vacancy and Mn valence change undoubtedly provides insights into a profound understanding on the voltage fade, and capacity degradation of LMR cathode. The results also inspire us to further enhance the reversibility of LMR cathode via improving its surface structural stability.

  20. Composite cathode materials development for intermediate temperature solid oxide fuel cell systems

    Science.gov (United States)

    Qin, Ya

    Solid oxide fuel cell (SOFC) systems are of particular interest as electrochemical power systems that can operate on various hydrocarbon fuels with high fuel-to-electrical energy conversion efficiency. Within the SOFC stack, La0.8Sr 0.2Ga0.8Mg0.115Co0.085O3-delta (LSGMC) has been reported as an optimized composition of lanthanum gallate based electrolytes to achieve higher oxygen ionic conductivity at intermediate temperatures, i.e., 500-700°C. The electrocatalytic properties of interfaces between LSGMC electrolytes and various candidate intermediate-temperature SOFC cathodes have been investigated. Sm0.5Sr0.5CoO 3-delta (SSC), and La0.6Sr0.4Co0.2Fe 0.8O3-delta (LSCF), in both pure and composite forms with LSGMC, were investigated with regards to both oxygen reduction and evolution, A range of composite cathode compositions, having ratios of SSC (in wt.%) with LSGMC (wt.%) spanning the compositions 9:1, 8:2, 7:3, 6:4 and 5:5, were investigated to determine the optimal cathode-electrolyte interface performance at intermediate temperatures. All LSGMC electrolyte and cathode powders were synthesized using the glycine-nitrate process (GNP). Symmetrical electrochemical cells were investigated with three-electrode linear dc polarization and ac impedance spectroscopy to characterize the kinetics of the interfacial reactions in detail. Composite cathodes were found to perform better than the single phase cathodes due to significantly reduced polarization resistances. Among those composite SSC-LSGMC cathodes, the 7:3 composition has demonstrated the highest current density at the equivalent overpotential values, indicating that 7:3 is an optimal mixing ratio of the composite cathode materials to achieve the best performance. For the composite SC-LSGMC cathode/LSGMC interface, the cathodic overpotential under 1 A/cm2 current density was as low as 0.085 V at 700°C, 0.062V at 750°C and 0.051V at 800°C in air. Composite LSCF-LSGMC cathode/LSGMC interfaces were found to have

  1. Vanadium oxide nanotubes as cathode material for Mg-ion batteries

    DEFF Research Database (Denmark)

    Christensen, Christian Kolle; Sørensen, Daniel Risskov; Bøjesen, Espen Drath

    Vanadium oxide compounds as cathode material for secondary Li-ion batteries gained interest in the 1970’s due to high specific capacity (>250mAh/g), but showed substantial capacity fading.1 Developments in the control of nanostructured morphologies have led to more advanced materials, and recently...... vanadium oxide nanotubes (VOx-NT) were shown to perform well as a cathode material for Mg-ion batteries.2 The VOx-NTs are easily prepared via a hydrothermal process to form multiwalled scrolls of VO layer with primary amines interlayer spacer molecules.3 The tunable and relative large layer spacing 1-3 nm...... synchrotron powder X-ray diffraction measured during battery operation. These results indicate Mg-intercalation in the multiwalled VOx-NTs occurs within the space between the individual vanadium oxide layers while the underlying VOx frameworks constructing the walls are affected only to a minor degree...

  2. Four-electron transfer tandem tetracyanoquinodimethane for cathode-active material in lithium secondary battery

    Science.gov (United States)

    Kurimoto, Naoya; Omoda, Ryo; Mizumo, Tomonobu; Ito, Seitaro; Aihara, Yuichi; Itoh, Takahito

    2018-02-01

    Quinoid compounds are important candidates of organic active materials for lithium-ion batteries. However, its high solubility to organic electrolyte solutions and low redox potential are known as their major drawbacks. To circumvent these issues, we have designed and synthesized a tandem-tetracyanoquinonedimethane type cathode-active material, 11,11,12,12,13,13,14,14-octacyano-1,4,5,8-anthradiquinotetramethane (OCNAQ), that has four redox sites per molecule, high redox potential and suppressed solubility to electrolyte solution. Synthesized OCNAQ has been found to have two-step redox reactions by cyclic voltammetry, and each step consists of two-electron reactions. During charge-discharge tests using selected organic cathode-active materials with a lithium metal anode, the cell voltages obtained from OCNAQ are higher than those for 11,11-dicyanoanthraquinone methide (AQM) as expected, due to the strong electron-withdrawing effect of the cyano groups. Unfortunately, even with the use of the organic active material, the issue of dissolution to the electrolyte solution cannot be suppressed completely; however, appropriate choice of the electrolyte solutions, glyme-based electrolyte solutions in this study, give considerable improvement of the cycle retention (98% and 56% at 10 and 100 cycles at 0.5C, respectively). The specific capacity and energy density obtained in this study are 206 mAh g-1 and 554 mWh g-1 with respect to the cathode active material.

  3. Containing and discarding method for radiation contaminated materials and radiation contaminated material containing composite member

    International Nuclear Information System (INIS)

    Akagawa, Katsuhiko.

    1995-01-01

    A container for high level radiation contaminated materials is loaded in an outer container in a state of forming a gap between the outer container and a container wall, low level radiation contaminated materials are filled to the gap between the container of the radiation contaminated materials and the container wall, and then the outer container is sealed. In addition, the thickness of the layer of the low level radiation contaminated materials is made substantially uniform. Then, since radiation rays from the container of the radiation contaminated materials are decayed by the layer of the low level radiation contaminated materials at the periphery of the container and the level of the radiation rays emitted from the outer container is extremely reduced than in a case where the entire amount of high level radiation contaminated materials are filled, the level is suppressed to an extent somewhat higher than the level in the case where the entire amount of the low level radiation contaminated materials are filled. Accordingly, the management corresponds to that for the low level radiation contaminated materials, and the steps for the management and the entire volume thereof are reduced than in a case where the high level radiation contaminated materials and the low level radiation contaminated materials are sealed separately. (N.H.)

  4. Synthesis and investigation of novel cathode materials for sodium ion batteries

    Science.gov (United States)

    Sawicki, Monica

    Environmental pollution and eventual depletion of fossil fuels and lithium has increased the need for research towards alternative electrical energy storage systems. In this context, research in sodium ion batteries (NIBs) has become more prevalent since the price in lithium has increased due to its demand and reserve location. Sodium is an abundant resource that is low cost, and safe; plus its chemical properties are similar to that of Li which makes the transition into using Na chemistry for ion battery systems feasible. In this study, we report the effects of processing conditions on the electrochemical properties of Na-ion batteries made of the NaCrO2 cathode. NaCrO2 is synthesized via solid state reactions. The as-synthesized powder is then subjected to high-energy ball milling under different conditions which reduces particle size drastically and causes significant degradation of the specific capacity for NaCrO2. X-ray diffraction reveals that lattice distortion has taken place during high-energy ball milling and in turn affects the electrochemical performance of the cathode material. This study shows that a balance between reducing particle size and maintaining the layered structure is essential to obtain high specific capacity for the NaCrO2 cathode. In light of the requirements for grid scale energy storage: ultra-long cycle life (> 20,000 cycles and calendar life of 15 to 20 years), high round trip efficiency (> 90%), low cost, sufficient power capability, and safety; the need for a suitable cathode materials with excellent capacity retention such as Na2MnFe(CN)6 and K2MnFe(CN)6 will be investigated. Prussian blue (A[FeIIIFeII (CN)6]•xH2O, A=Na+ or K+ ) and its analogues have been investigated as an alkali ion host for use as a cathode material. Their structure (FCC) provides large ionic channels along the direction enabling facile insertion and extraction of alkali ions. This material is also capable of more than one Na ion insertion per unit formula

  5. Comparative Issues of Cathode Materials for Li-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Christian M. Julien

    2014-03-01

    Full Text Available After an introduction to lithium insertion compounds and the principles of Li-ion cells, we present a comparative study of the physical and electrochemical properties of positive electrodes used in lithium-ion batteries (LIBs. Electrode materials include three different classes of lattices according to the dimensionality of the Li+ ion motion in them: olivine, layered transition-metal oxides and spinel frameworks. Their advantages and disadvantages are compared with emphasis on synthesis difficulties, electrochemical stability, faradaic performance and security issues.

  6. Buried waste containment system materials. Final Report

    International Nuclear Information System (INIS)

    Weidner, J.R.; Shaw, P.G.

    1997-10-01

    This report describes the results of a test program to validate the application of a latex-modified cement formulation for use with the Buried Waste Containment System (BWCS) process during a proof of principle (POP) demonstration. The test program included three objectives. One objective was to validate the barrier material mix formulation to be used with the BWCS equipment. A basic mix formula for initial trials was supplied by the cement and latex vendors. The suitability of the material for BWCS application was verified by laboratory testing at the Idaho National Engineering and Environmental Laboratory (INEEL). A second objective was to determine if the POP BWCS material emplacement process adversely affected the barrier material properties. This objective was met by measuring and comparing properties of material prepared in the INEEL Materials Testing Laboratory (MTL) with identical properties of material produced by the BWCS field tests. These measurements included hydraulic conductivity to determine if the material met the US Environmental Protection Agency (EPA) requirements for barriers used for hazardous waste sites, petrographic analysis to allow an assessment of barrier material separation and segregation during emplacement, and a set of mechanical property tests typical of concrete characterization. The third objective was to measure the hydraulic properties of barrier material containing a stop-start joint to determine if such a feature would meet the EPA requirements for hazardous waste site barriers

  7. In Situ X-ray Diffraction Studies of Cathode Materials in Lithium Batteries

    International Nuclear Information System (INIS)

    Yang, X. Q.; Sun, X.; McBreen, J.; Mukerjee, S.; Gao, Yuan; Yakovleva, M. V.; Xing, X. K.; Daroux, M. L.

    1998-01-01

    There is an increasing interest in lithiated transition metal oxides because of their use as cathodes in lithium batteries. LiCoO 2 , LiNiO 2 and LiMn 2 O 4 are the three most widely used and studied materials, At present, although it is relative expensive and toxic, LiCoO 2 is the material of choice in commercial lithium ion batteries because of its ease of manufacture, better thermal stability and cycle life. However, the potential use of lithium ion batteries with larger capacity for power tools and electric vehicles in the future will demand new cathode materials with higher energy density, lower cost and better thermal stability. LiNiO 2 is isostructural with LiCoO 2 . It offers lower cost and high energy density than LiCoO 2 . However, it has much poorer thermal stability than LiCoO 2 , in the charged (delithiated) state. Co, Al, and other elements have been used to partially replace Ni in LiNiO 2 system in order to increase the thermal stability. LiMn 2 O 4 has the highest thermal stability and lowest cost and toxicity. However, the low energy density and poor cycle life at elevated temperature are the major obstacles for this material. In order to develop safer, cheaper, and better performance cathode materials, the in-depth understanding of the relationships between the thermal stability and structure, performance and structure are very important. The performance here includes energy density and cycle life of the cathode materials. X-ray diffraction (XRD) is one of the most powerful tools to study these relationships. The pioneer ex situ XRD work on cathode materials for lithium batteries was done by Ohzuku. His XRD studies on LiMn 2 O 4 , LiCoO 2 , LiNiO 2 , LiNi 0.5 Co 0.5 O 2 , and LiAl x Ni 1-x O 2 cathodes at different states of charge have provided important guidelines for the development of these new materials. However, the kinetic nature of the battery system definitely requires an in situ XRD technique to study the detail structural changes of the

  8. Secondary cell with orthorhombic alkali metal/manganese oxide phase active cathode material

    Science.gov (United States)

    Doeff, Marca M.; Peng, Marcus Y.; Ma, Yanping; Visco, Steven J.; DeJonghe, Lutgard C.

    1996-01-01

    An alkali metal manganese oxide secondary cell is disclosed which can provide a high rate of discharge, good cycling capabilities, good stability of the cathode material, high specific energy (energy per unit of weight) and high energy density (energy per unit volume). The active material in the anode is an alkali metal and the active material in the cathode comprises an orthorhombic alkali metal manganese oxide which undergoes intercalation and deintercalation without a change in phase, resulting in a substantially linear change in voltage with change in the state of charge of the cell. The active material in the cathode is an orthorhombic structure having the formula M.sub.x Z.sub.y Mn.sub.(1-y) O.sub.2, where M is an alkali metal; Z is a metal capable of substituting for manganese in the orthorhombic structure such as iron, cobalt or titanium; x ranges from about 0.2 in the fully charged state to about 0.75 in the fully discharged state, and y ranges from 0 to 60 atomic %. Preferably, the cell is constructed with a solid electrolyte, but a liquid or gelatinous electrolyte may also be used in the cell.

  9. Cathode Materials for High Energy Density Lithium Batteries

    Directory of Open Access Journals (Sweden)

    Lefèvre G.

    2017-01-01

    Li2MnSiO4 has a large theoretical specific capacity (333 mAh/g through exchange of 2 lithium ions per formula unit. The thermal stability due to strong Si-O bonds makes LiMnSiO a very promising material for future energy storage in space applications. Preparation in inert atmosphere showed beneficial improvements of LMSO’s electrochemical properties. Nano-sizing and carbon coating have been effective ways to improve electronic conductivity and therefore electrochemical performance. Up to 1.66 Li per formula unit can be re-inserted in the 1st cycle. XRD analysis showed complete amorphization of Li2MnSiO4 after the 1st charge at 4.8 V with complete modification of the charge/discharge curves in the next cycles. Increasing the carbon coating ratio limits capacity loss during cycling but did not avoid amorphization. Finally influence of voltage window on structure stability was investigated. Careful choice of upper limit voltage has been showed to stabilize Li2MnSiO4 structure but for now is still limited to low Li+ insertion/extraction from the host material.

  10. Sulfurized carbon: a class of cathode materials for high performance lithium/sulfur batteries

    Directory of Open Access Journals (Sweden)

    Sheng S. Zhang

    2013-12-01

    Full Text Available Liquid electrolyte lithium/sulfur (Li/S batteries cannot come into practical applications because of many problems such as low energy efficiency, short cycle life, and fast self-discharge. All these problems are related to the dissolution of lithium polysulfide, a series of sulfur reduction intermediates, in the liquid electrolyte, and resulting parasitic reactions with the Li anode. Covalently binding sulfur onto carbon surface is a solution to completely eliminate the dissolution of lithium polysulfide and make the Li/S battery viable for practical applications. This can be achieved by replacing elemental sulfur with sulfurized carbon as the cathode material. This article reviews the current efforts on this subject and discusses the syntheses, electrochemical properties, and prospects of the sulfurized carbon as a cathode material in the rechargeable Li/S batteries.

  11. Mechanism of chromium poisoning the conventional cathode material for solid oxide fuel cells

    Science.gov (United States)

    Zhang, Xiaoqiang; Yu, Guangsen; Zeng, Shumao; Parbey, Joseph; Xiao, Shuhao; Li, Baihai; Li, Tingshuai; Andersson, Martin

    2018-03-01

    Chromium poisoning the La0.875Sr0.125MnO3 (LSM) cathode for solid oxide fuel cells is a critical issue that can strongly affect the stability. In this study, we evaluate the temperature distribution in a SOFC based on a 3D model and then combine conductivity test and material computation to reveal the effects of chromium in SUS430 stainless steels on LSM conductivities. The starch concentration in LSM pellets and the applied pressure on the contact with interconnect materials show close relationships with the chromium poisoning behavior. The density functional theory (DFT) computing results indicate that chromium atoms preferably adsorb on the MnO2-terminated and La (Sr)-O-terminated (001) surfaces. The resulting conclusions are expected to deeply understand mechanism of chromium deactivating conventional cathodes at some typical operational conditions, and offer crucial information to optimize the structure to avoid the poisoning effect.

  12. Electrocoagulation of whey acids: anode and cathode materials, electroactive area and polarization curves

    Directory of Open Access Journals (Sweden)

    Francisco Prieto Garcia

    2017-06-01

    Full Text Available Anode (Al and Fe and cathode (graphite and Ti/RuO2 materials have been tested for electrocoagulation (EC and purification of the acid whey. The electroactive areas (EA of electrodes were calculated by the double layer capacitance method. Experiments were performed by cyclic voltammetry, chronoamperometry and polarization experiments. Among cathodic materials, the Ti/RuO2 electrode showed higher EA (2167 cm2 than graphite (1560 cm2. The Fe anode was found more stable than Al with greater charge transfer carried out in less time. Correlation of these results with those obtained during preliminary tests confirmed high removals (79 % in 8 h. For the Al electrode, 24 h were required to achieve efficiency of 49 %.

  13. Transition-metal chlorides as conversion cathode materials for Li-ion batteries

    International Nuclear Information System (INIS)

    Li Ting; Chen, Zhong X.; Cao, Yu L.; Ai, Xin P.; Yang, Han X.

    2012-01-01

    Insoluble AgCl and soluble CuCl 2 were selected and investigated as model compounds of transition-metal chlorides for electrochemical conversion cathode materials. The experimental results demonstrated that the AgCl nanocrystals can convert reversibly to metallic Ag with nearly full utilization of its one-electron redox capacity (187 mAh g −1 ). Similarly, the CuCl 2 -filled mesoporous carbon can realize a reversible two-electron transfer reaction, giving a very high reversible capacity of 466 mAh g −1 after 20 cycles. These data imply that the metal chlorides can undergo complete electrochemical conversion utilizing their full oxidation states for electrical energy storage as previously reported metal fluorides, possibly being used as high capacity cathode materials for Li-ion batteries.

  14. Graphene Modified LiFePO4 Cathode Materials for High Power Lithium ion Batteries

    International Nuclear Information System (INIS)

    Zhou, X.; Wang, F.; Zhu, Y.; Liu, Z.

    2011-01-01

    Graphene-modified LiFePO 4 composite has been developed as a Li-ion battery cathode material with excellent high-rate capability and cycling stability. The composite was prepared with LiFePO 4 nanoparticles and graphene oxide nanosheets by spray-drying and annealing processes. The LiFePO 4 primary nanoparticles embedded in micro-sized spherical secondary particles were wrapped homogeneously and loosely with a graphene 3D network. Such a special nanostructure facilitated electron migration throughout the secondary particles, while the presence of abundant voids between the LiFePO 4 nanoparticles and graphene sheets was beneficial for Li + diffusion. The composite cathode material could deliver a capacity of 70 mAh g -1 at 60C discharge rate and showed a capacity decay rate of <15% when cycled under 10C charging and 20C discharging for 1000 times.

  15. Mesoporous nitrogen-rich carbon materials as cathode catalysts in microbial fuel cells

    KAUST Repository

    Ahn, Yongtae

    2014-12-01

    The high cost of the catalyst material used for the oxygen reduction reaction in microbial fuel cell (MFC) cathodes is one of the factors limiting practical applications of this technology. Mesoporous nitrogen-rich carbon (MNC), prepared at different temperatures, was examined as an oxygen reduction catalyst, and compared in performance to Pt in MFCs and electrochemical cells. MNC calcined at 800 °C produced a maximum power density of 979 ± 131 mW m-2 in MFCs, which was 37% higher than that produced using MNC calined at 600 °C (715 ± 152 mW m-2), and only 14% lower than that obtained with Pt (1143 ± 54 mW m-2). The extent of COD removal and coulombic efficiencies were the same for all cathode materials. These results show that MNC could be used as an alternative to Pt in MFCs. © 2014 Elsevier B.V. All rights reserved.

  16. Electron-deficient anthraquinone derivatives as cathodic material for lithium ion batteries

    Science.gov (United States)

    Takeda, Takashi; Taniki, Ryosuke; Masuda, Asuna; Honma, Itaru; Akutagawa, Tomoyuki

    2016-10-01

    We studied the electronic and structural properties of electron-deficient anthraquinone (AQ) derivatives, Me4N4AQ and TCNAQ, and investigated their charge-discharge properties in lithium ion batteries along with those of AQ. Cyclic voltammogram, X-ray structure analysis and theoretical calculations revealed that these three acceptors have different features, such as different electron-accepting properties with different reduction processes and lithium coordination abilities, and different packing arrangements with different intermolecular interactions. These differences greatly affect the charge-discharge properties of lithium ion batteries that use these compounds as cathode materials. Among these compounds, Me4N4AQ showed a high charge/discharge voltage (2.9-2.5 V) with high cyclability (>65% of the theoretical capacity after 30 cycles; no decrease after 15 cycles). These results provide insight into more in-depth design principles for lithium ion batteries using AQ derivatives as cathodic materials.

  17. Investigation and optimisation of a plasma cathode electron beam gun for material processing applications

    OpenAIRE

    Del Pozo Rodriguez, Sofia

    2016-01-01

    This thesis was submitted for the degree of Doctor of Philosophy and awarded by Brunel University London. This thesis describes design, development and testing work on a plasma cathode electron beam gun as well as plasma diagnosis experiments and Electron Beam (EB) current measurements carried out with the aim of maximising the power of the EB extracted and optimising the electron beam gun system for material processing applications. The elements which influence EB gun design are described...

  18. Treating agent for urea containing radioactive materials

    International Nuclear Information System (INIS)

    Ogawa, Hiroshi; Maki, Kentaro.

    1973-01-01

    Object: To add a coagulant into urea containing radioactive material to precipitate and remove the radioactive material in the urea. Structure: Iodosalt is added into urea and next, a mixed reagent in which silver ion or silver acetic ion and iron hydroxide precipitation or ferrite ion coexist is added therein. The urea is treated to have a sufficient alkaline, after which it is introduced into a basket type centrifuge formed with a filter layer in combination of an upper glass fiber layer and a lower active carbon layer. The treating agent can uniformly remove radioactive ion and radioactive chelate within urea containing inorganic salt and various metabolites. (Nakamura, S.)

  19. Atmospheric Plasma Spraying Low-Temperature Cathode Materials for Solid Oxide Fuel Cells

    Science.gov (United States)

    Harris, J.; Kesler, O.

    2010-01-01

    Atmospheric plasma spraying (APS) is attractive for manufacturing solid oxide fuel cells (SOFCs) because it allows functional layers to be built rapidly with controlled microstructures. The technique allows SOFCs that operate at low temperatures (500-700 °C) to be fabricated by spraying directly onto robust and inexpensive metallic supports. However, standard cathode materials used in commercial SOFCs exhibit high polarization resistances at low operating temperatures. Therefore, alternative cathode materials with high performance at low temperatures are essential to facilitate the use of metallic supports. Coatings of lanthanum strontium cobalt ferrite (LSCF) were fabricated on steel substrates using axial-injection APS. The thickness and microstructure of the coating layers were evaluated, and x-ray diffraction analysis was performed on the coatings to detect material decomposition and the formation of undesired phases in the plasma. These results determined the envelope of plasma spray parameters in which coatings of LSCF can be manufactured, and the range of conditions in which composite cathode coatings could potentially be manufactured.

  20. Theoretical evaluation of high-energy lithium metal phosphate cathode materials in Li-ion batteries

    Science.gov (United States)

    Howard, Wilmont F.; Spotnitz, Robert M.

    Lithium metal phosphates (olivines) are emerging as long-lived, safe cathode materials in Li-ion batteries. Nano-LiFePO 4 already appears in high-power applications, and LiMnPO 4 development is underway. Current and emerging Fe- and Mn-based intercalants, however, are low-energy producers compared to Ni and Co compounds. LiNiPO 4, a high voltage olivine, has the potential for superior energy output (>10.7 Wh in 18650 batteries), compared with commercial Li(Co,Ni)O 2 derivatives (up to 9.9 Wh). Speculative Co and Ni olivine cathode materials charged to above 4.5 V will require significant advances in electrolyte compositions and nanotechnology before commercialization. The major drivers toward 5 V battery chemistries are the inherent abuse tolerance of phosphates and the economic benefit of LiNiPO 4: it can produce 34% greater energy per dollar of cell material cost than LiAl 0.05Co 0.15Ni 0.8O 2, today's "standard" cathode intercalant in Li-ion batteries.

  1. Mineralogical conversion of asbestos containing materials

    International Nuclear Information System (INIS)

    Pulsford, S.K.; Foltz, A.D.; Ek, R.B.

    1996-01-01

    The principal objective of the Technical Task Plan (TTP) is to demonstrate a thermal-chemical mineralogical asbestos conversion unit at the Hanford Site, which converts non-radiological asbestos containing materials (ACMs) into an asbestos-free material. The permanent thermal-chemical mineralogical conversion of ACMs to a non-toxic, non-hazardous, potentially marketable end product should not only significantly reduce the waste stream volumes but terminate the open-quotes cradle to graveclose quotes ownership liabilities

  2. Investigation of the removing process of cathode material in micro-EDM using an atomistic-continuum model

    International Nuclear Information System (INIS)

    Guo, Jianwen; Zhang, Guojun; Huang, Yu; Ming, Wuyi; Liu, Min; Huang, Hao

    2014-01-01

    Highlights: • An atomistic-continuum computational simulation model for single-discharge micro-EDM process of Cu cathode is constructed. • Cathode material is removed mainly in the form of single atoms or small clusters in micro-EDM. • Electric action leads to the formation of peaks on the surface of crater. • Removing process of cathode material under the hybrid action combining the thermal action and the electric action is studied, and the strength of either action needed for material to remove is much reduced. - Abstract: In micro-electrical discharge machining (micro-EDM), the discharge duration is ultra-short, and both the electric action and the thermal action by the discharge channel play important roles in the removing process of cathode material. However, in most researches on the machining mechanism of micro-EDM, only the thermal action is concerned. In this article, a combined atomistic-continuum modeling method in which the two-temperature model and the molecular dynamics simulation model are integrated is used to construct the simulation model for cathode in single-discharge micro-EDM process. With this simulation model, removing processes of Cu cathode material in micro-EDM under pure thermal action, pure electric action and the combination of them are investigated in a simulative way. By analyzing evolutions of temperature, stress and micro-structure of material as well as the dynamical behaviors of material in the removing process, mechanisms of the cathode material removal and crater formation are revealed. In addition, the removing process of cathode material under the combination of pure thermal action and pure electric action is compared with those under the two pure actions respectively to analyze the interactive effect between the thermal action and the electric action

  3. Evaluation of materials for bipolar plates in simulated PEM fuel-cell cathodic environments

    Energy Technology Data Exchange (ETDEWEB)

    Rivas, S.V.; Belmonte, M.R.; Moron, L.E.; Torres, J.; Orozco, G. [Centro de Investigacion y Desarrollo Technologico en Electroquimica S.C. Parcque Sanfandila, Queretaro (Mexico); Perez-Quiroz, J.T. [Mexican Transport Inst., Queretaro (Mexico); Cortes, M. A. [Mexican Petroleum Inst., Mexico City (Mexico)

    2008-04-15

    The bipolar plates in proton exchange membrane fuel cells (PEMFC) are exposed to an oxidizing environment on the cathodic side, and therefore are susceptible to corrosion. Corrosion resistant materials are needed for the bipolar plates in order to improve the lifespan of fuel cells. This article described a study in which a molybdenum (Mo) coating was deposited over austenitic stainless steel 316 and carbon steel as substrates in order to evaluate the resulting surfaces with respect to their corrosion resistance in simulated anodic and cathodic PEMFC environments. The molybdenum oxide films were characterized by scanning electron microscopy (SEM) and Raman spectroscopy. The article presented the experiment and discussed the results of the corrosion behaviour of coated stainless steel. In general, the electrochemical characterization of bare materials and coated steel consisted of slow potentiodynamic polarization curves followed by a constant potential polarization test. The test medium was 0.5M sulfuric acid with additional introduction of oxygen to simulate the cathodic environment. All tests were performed at ambient temperature and at 50 degrees Celsius. The potentiostat used was a Gamry instrument. It was concluded that it is possible to deposit Mo-oxides on steel without using another alloying metal. The preferred substrate for corrosion prevention was found to be an alloy with high chromium content. 24 refs., 4 figs.

  4. Arcjet cathode phenomena

    Science.gov (United States)

    Curran, Francis M.; Haag, Thomas W.; Raquet, John F.

    1989-01-01

    Cathode tips made from a number of different materials were tested in a modular arcjet thruster in order to examine cathode phenomena. Periodic disassembly and examination, along with the data collected during testing, indicated that all of the tungsten-based materials behaved similarly despite the fact that in one of these samples the percentage of thorium oxide was doubled and another was 25 percent rhenium. The mass loss rate from a 2 percent thoriated rhenium cathode was found to be an order of magnitude greater than that observed using 2 percent thoriated tungsten. Detailed analysis of one of these cathode tips showed that the molten crater contained pure tungsten to a depth of about 150 microns. Problems with thermal stress cracking were encountered in the testing of a hafnium carbide tip. Post test analysis showed that the active area of the tip had chemically reacted with the propellant. A 100 hour continuous test was run at about 1 kW. Post test analysis revealed no dendrite formation, such as observed in a 30 kW arcjet lifetest, near the cathode crater. The cathodes from both this test and a previously run 1000 hour cycled test displayed nearly identical arc craters. Data and calculations indicate that the mass losses observed in testing can be explained by evaporation.

  5. New polyanion-based cathode materials for alkali-ion batteries

    Science.gov (United States)

    Yaghoobnejad Asl, Hooman

    A number of new materials have been discovered through exploratory synthesis with the aim to be studied as the positive electrode (cathode) in Li-ion and Na-ion batteries. The focus has been set on the ease of synthesis, cost and availability of active ingredients in the battery, and decent cycle-life performance through a combination of iron and several polyanionic ligands. An emphasis has been placed also on phosphite (HPO32-) as a polyanionic ligand, mainly due to the fact that it has not been studied seriously before as a polyanion for cathode materials. The concept of mixed polyanions, for example, boro-phosphate and phosphate-nitrates were also explored. In each case the material was first made and purified via different synthetic strategies, and the crystal structure, which dominantly controls the performance of the materials, has been extensively studied through Single-Crystal X-ray Diffraction (SCXRD) or synchrotron-based Powder X-ray Diffraction (PXRD). This investigation yielded four new compositions, namely Li3Fe 2(HPO3)3Cl, LiFe(HPO3)2, Li0.8Fe(H2O)2B[P2O8]•H 2O and AFePO4NO3 (A = NH4/Li, K). Furthermore, for each material the electrochemical performance for insertion of Li+ ion has been studied by means of various electrochemical techniques to reveal the nature of alkali ion insertion. In addition Na-ion intercalation has been studied for boro-phosphate and AFePO4NO3. Additionally a novel synthesis procedure has been reported for tavorite LiFePO4F 1-x(OH)x, where 0 ≤ x ≤ 1, an important class of cathode materials. The results obtained clearly demonstrate the importance of crystal structure on the cathode performance through structural and compositional effects. Moreover these findings may contribute to the energy storage community by providing insight into the solid-state science of electrode material synthesis and proposing new alternative compositions based on sustainable materials.

  6. Controlling the reaction between boron-containing sealing glass and a lanthanum-containing cathode by adding Nb2O5

    Science.gov (United States)

    Zhao, Dandan; Fang, Lihua; Tang, Dian; Zhang, Teng

    2016-09-01

    In solid oxide fuel cell (SOFC) stacks, the volatile boron species present in the sealing glass often react with the lanthanum-containing cathode, degrading the activity of the cathode (this phenomenon is known as boron poisoning). In this work, we report that this detrimental reaction can be effectively reduced by doping bismuth-containing borosilicate sealing glass-ceramic with a niobium dopant. The addition of Nb2O5 not only condenses the [SiO4] structural units in the glass network, but also promotes the conversion of [BO3] to [BO4]. Moreover, the Nb2O5 dopant enhances the formation of boron-containing phases (Ca3B2O6 and CaB2Si2O8), which significantly reduces the volatility of boron compounds in the sealing glass, suppressing the formation of LaBO3 in the reaction couple between the glass and the cathode. The reported results provide a new approach to solve the problem of boron poisoning.

  7. Container for storage of environmental incompatible materials

    International Nuclear Information System (INIS)

    Ruggenthaler, P.T.

    1984-01-01

    The container consists of a cuboid chamber, closed to five sides, just as the cover made of concrete. Iron mountings for use with lifting gears are coupled with the armouring of the container. The cover is made in such a way that mountings are hidden by the recesses at its borders. Therefore it is possible to stick these boxes. Concrete employed for is enriched with sealing materials of synthetics, the box is painted too. Sensors on the outside ensure telemetering of closeness of the boxes. (J.K.) [de

  8. SULPHUR DIOXIDE LEACHING OF URANIUM CONTAINING MATERIAL

    Science.gov (United States)

    Thunaes, A.; Rabbits, F.T.; Hester, K.D.; Smith, H.W.

    1958-12-01

    A process is described for extracting uranlum from uranium containing material, such as a low grade pitchblende ore, or mill taillngs, where at least part of the uraniunn is in the +4 oxidation state. After comminuting and magnetically removing any entrained lron particles the general material is made up as an aqueous slurry containing added ferric and manganese salts and treated with sulfur dioxide and aeration to an extent sufficient to form a proportion of oxysulfur acids to give a pH of about 1 to 2 but insufficient to cause excessive removal of the sulfur dioxide gas. After separating from the solids, the leach solution is adjusted to a pH of about 1.25, then treated with metallic iron in the presence of a precipitant such as a soluble phosphate, arsonate, or fluoride.

  9. Chemical behavior of lanthanides-tungsten composite materials used in thermo-emissive cathodes

    International Nuclear Information System (INIS)

    Cadoret, K.; Cachard, J. de; Martinez, L.; Millot, F.; Hennet, L.; Douy, A.; Licheron, M.

    2001-01-01

    This work presents the crystallography and chemistry of new lanthanides-tungsten composite materials developed to manufacture thermionic cathodes for power grid tubes, based on the same principle than thorium-free cathodes. By mean of x-Ray diffraction at high temperature and under vacuum with synchrotron radiation facilities, we followed in real time the different phases and phase transitions that can occur during the heating process and the carburization at 1550 o C of such tungstates deposits on thin tungsten ribbons. Melting points for composition between 9 La 2 O 3 - 1 WO 3 and 2 La 2 O 3 - 9 WO 3 were specified under the pressure of 1x10 -6 mbar. After interpretation of x-ray diffraction results, phase diagram of n La 2 O 3 - m WO 3 system under vacuum in equilibrium with metallic tungsten have been deduced. Moreover we underline by these works the fact that using a lanthanum-rich tungstate involves better stability and chemical homogeneity of the cathodes surfaces with temperature. (author)

  10. High-Capacity Cathode Material with High Voltage for Li-Ion Batteries.

    Science.gov (United States)

    Shi, Ji-Lei; Xiao, Dong-Dong; Ge, Mingyuan; Yu, Xiqian; Chu, Yong; Huang, Xiaojing; Zhang, Xu-Dong; Yin, Ya-Xia; Yang, Xiao-Qing; Guo, Yu-Guo; Gu, Lin; Wan, Li-Jun

    2018-03-01

    Electrochemical energy storage devices with a high energy density are an important technology in modern society, especially for electric vehicles. The most effective approach to improve the energy density of batteries is to search for high-capacity electrode materials. According to the concept of energy quality, a high-voltage battery delivers a highly useful energy, thus providing a new insight to improve energy density. Based on this concept, a novel and successful strategy to increase the energy density and energy quality by increasing the discharge voltage of cathode materials and preserving high capacity is proposed. The proposal is realized in high-capacity Li-rich cathode materials. The average discharge voltage is increased from 3.5 to 3.8 V by increasing the nickel content and applying a simple after-treatment, and the specific energy is improved from 912 to 1033 Wh kg -1 . The current work provides an insightful universal principle for developing, designing, and screening electrode materials for high energy density and energy quality. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  11. Dynamic behaviour of interphases and its implication on high-energy-density cathode materials in lithium-ion batteries

    Science.gov (United States)

    Li, Wangda; Dolocan, Andrei; Oh, Pilgun; Celio, Hugo; Park, Suhyeon; Cho, Jaephil; Manthiram, Arumugam

    2017-01-01

    Undesired electrode–electrolyte interactions prevent the use of many high-energy-density cathode materials in practical lithium-ion batteries. Efforts to address their limited service life have predominantly focused on the active electrode materials and electrolytes. Here an advanced three-dimensional chemical and imaging analysis on a model material, the nickel-rich layered lithium transition-metal oxide, reveals the dynamic behaviour of cathode interphases driven by conductive carbon additives (carbon black) in a common nonaqueous electrolyte. Region-of-interest sensitive secondary-ion mass spectrometry shows that a cathode-electrolyte interphase, initially formed on carbon black with no electrochemical bias applied, readily passivates the cathode particles through mutual exchange of surface species. By tuning the interphase thickness, we demonstrate its robustness in suppressing the deterioration of the electrode/electrolyte interface during high-voltage cell operation. Our results provide insights on the formation and evolution of cathode interphases, facilitating development of in situ surface protection on high-energy-density cathode materials in lithium-based batteries. PMID:28443608

  12. Recycling of spent lithium-ion battery cathode materials by ammoniacal leaching

    International Nuclear Information System (INIS)

    Ku, Heesuk; Jung, Yeojin; Jo, Minsang; Park, Sanghyuk; Kim, Sookyung; Yang, Donghyo; Rhee, Kangin; An, Eung-Mo; Sohn, Jeongsoo; Kwon, Kyungjung

    2016-01-01

    Highlights: • Ammoniacal leaching is used to recover spent Li-ion battery cathode materials. • Leaching agents consist of ammonia, ammonium sulfite and ammonium carbonate. • Ammonium sulfite is a reductant and ammonium carbonate acts as pH buffer. • Co and Cu can be fully leached while Mn and Al are not leached. • Co recovery via ammoniacal leaching is economical compared to acid leaching. - Abstract: As the production and consumption of lithium ion batteries (LIBs) increase, the recycling of spent LIBs appears inevitable from an environmental, economic and health viewpoint. The leaching behavior of Ni, Mn, Co, Al and Cu from treated cathode active materials, which are separated from a commercial LIB pack in hybrid electric vehicles, is investigated with ammoniacal leaching agents based on ammonia, ammonium carbonate and ammonium sulfite. Ammonium sulfite as a reductant is necessary to enhance leaching kinetics particularly in the ammoniacal leaching of Ni and Co. Ammonium carbonate can act as a pH buffer so that the pH of leaching solution changes little during leaching. Co and Cu can be fully leached out whereas Mn and Al are hardly leached and Ni shows a moderate leaching efficiency. It is confirmed that the cathode active materials are a composite of LiMn_2O_4, LiCo_xMn_yNi_zO_2_, Al_2O_3 and C while the leach residue is composed of LiNi_xMn_yCo_zO_2, LiMn_2O_4, Al_2O_3, MnCO_3 and Mn oxides. Co recovery via the ammoniacal leaching is believed to gain a competitive edge on convenitonal acid leaching both by reducing the sodium hydroxide expense for increasing the pH of leaching solution and by removing the separation steps of Mn and Al.

  13. Freeze drying synthesis of LiNi0.5Mn0.5O2 cathode materials

    International Nuclear Information System (INIS)

    Shlyakhtin, O.A.; Yoon, Young Soo; Choi, Sun Hee; Oh, Young-Jei

    2004-01-01

    The influence of several processing conditions on the phase formation and electrochemical performance of LiNi 0.5 Mn 0.5 O 2 powders, obtained by freeze drying method, is studied. Thermal processing in pellets at maximum heating rate promotes better crystallographic ordering of hexagonal LiNi 0.5 Mn 0.5 O 2 and maximum capacity values irrespectively of chemical composition of the precursor. Instead, intense mechanical processing of precursors exerts considerable negative effect on the electrochemical performance. Cathode materials containing superstoichiometric amount of lithium (Li 1.3 Mn 0.5 Ni 0.5 O 2+δ ) demonstrate reversible capacity values up to 190 mAh/g between 2.5 and 4.6 V

  14. Crystallite Size and Microstrain Measurement of Cathode Material after Mechanical Milling using Neutron Diffraction Technique

    Directory of Open Access Journals (Sweden)

    A. Fajar

    2010-12-01

    Full Text Available The measurements of neutron diffraction patterns of commercially product and 10 hour mechanically milled cathode material lithium cobaltites (LiCoO2 have been performed. Rietveld analysis using FullProf does not show the change of crystal structure due to milling process, but the diffraction pattern has a lower intensity and the diffraction-line was broadening. The results of line-broadening study on milled sample using Rietveld methods detected that the microstrain was occurred in the sample with value 0.127080(35 % and the average crystallite size was 424.78(20 Å.

  15. Reuse of Material Containing Natural Radionuclides - 12444

    Energy Technology Data Exchange (ETDEWEB)

    Metlyaev, E.G.; Novikova, N.J. [Burnasyan Federal Medical Biophysical Centre, Moscow (Russian Federation)

    2012-07-01

    Disposal of and use of wastes containing natural radioactive material (NORM) or technologically enhanced natural radioactive material (TENORM) with excessive natural background as a building material is very important in the supervision body activity. At the present time, the residents of Octyabrsky village are under resettlement. This village is located just near the Priargunsky mining and chemical combine (Ltd. 'PPGHO'), one of the oldest uranium mines in our country. The vacated wooden houses in the village are demolished and partly used as a building material. To address the issue of potential radiation hazard of the wooden beams originating from demolition of houses in Octyabrsky village, the contents of the natural radionuclides (K-40, Th-232, Ra-226, U- 238) are being determined in samples of the wooden beams of houses. The NORM contents in the wooden house samples are higher, on average, than their content in the reference sample of the fresh wood shavings, but the range of values is rather large. According to the classification of waste containing the natural radionuclides, its evaluation is based on the effective specific activity. At the effective specific activity lower 1.5 kBq/kg and gamma dose rate lower 70 μR/h, the material is not considered as waste and can be used in building by 1 - 3 classes depending upon A{sub eff} value. At 1.5 kBq/kg < A{sub eff} ≤ 4 kBq/kg (4 class), the wooden beams might be used for the purpose of the industrial building, if sum of ratios between the radionuclide specific activity and its specific activity of minimum significance is lower than unit. The material classified as the waste containing the natural radionuclides has A{sub eff} higher 1.5 kBq /kg, and its usage for the purpose of house-building and road construction is forbidden. As for the ash classification and its future usage, such usage is unreasonable, because, according to the provided material, more than 50% of ash samples are considered as

  16. Effect of calcination temperature on microstructure and electrochemical performance of lithium-rich layered oxide cathode materials

    International Nuclear Information System (INIS)

    Ma, Quanxin; Peng, Fangwei; Li, Ruhong; Yin, Shibo; Dai, Changsong

    2016-01-01

    Highlights: • A series of Li-rich layered oxide cathode materials (Li_1_._2Mn_0_._5_6Ni_0_._1_6Co_0_._0_8O_2) were successfully synthesized via a two-step synthesis method. • The effects of calcination temperature on the cathode materials were researched in detail. • A well-crystallized layered structure was obtained as the calcination temperature increased. • The samples calcined in a range of 850–900 °C exhibited excellent electrochemical performance. - Abstract: Lithium-rich layered oxide cathode materials (Li_1_._2Mn_0_._5_6Ni_0_._1_6Co_0_._0_8O_2 (LLMO)) were synthesized via a two-step synthesis method involving co-precipitation and high-temperature calcination. The effects of calcination temperature on the cathode materials were studied in detail. Structural and morphological characterizations revealed that a well-crystallized layered structure was obtained at a higher calcination temperature. Electrochemical performance evaluation revealed that a cathode material obtained at a calcination temperature of 850 °C delivered a high initial discharge capacity of 266.8 mAh g"−"1 at a 0.1 C rate and a capacity retention rate of 95.8% after 100 cycles as well as excellent rate capability. Another sample calcinated at 900 °C exhibited good cycling stability. It is concluded that the structural stability and electrochemical performance of Li-rich layered oxide cathode materials were strongly dependent on calcination temperatures. The results suggest that a calcination temperature in a range of 850–900 °C could promote electrochemical performance of this type of cathode materials.

  17. Effect of calcination temperature on microstructure and electrochemical performance of lithium-rich layered oxide cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Ma, Quanxin; Peng, Fangwei; Li, Ruhong; Yin, Shibo; Dai, Changsong, E-mail: changsd@hit.edu.cn

    2016-11-15

    Highlights: • A series of Li-rich layered oxide cathode materials (Li{sub 1.2}Mn{sub 0.56}Ni{sub 0.16}Co{sub 0.08}O{sub 2}) were successfully synthesized via a two-step synthesis method. • The effects of calcination temperature on the cathode materials were researched in detail. • A well-crystallized layered structure was obtained as the calcination temperature increased. • The samples calcined in a range of 850–900 °C exhibited excellent electrochemical performance. - Abstract: Lithium-rich layered oxide cathode materials (Li{sub 1.2}Mn{sub 0.56}Ni{sub 0.16}Co{sub 0.08}O{sub 2} (LLMO)) were synthesized via a two-step synthesis method involving co-precipitation and high-temperature calcination. The effects of calcination temperature on the cathode materials were studied in detail. Structural and morphological characterizations revealed that a well-crystallized layered structure was obtained at a higher calcination temperature. Electrochemical performance evaluation revealed that a cathode material obtained at a calcination temperature of 850 °C delivered a high initial discharge capacity of 266.8 mAh g{sup −1} at a 0.1 C rate and a capacity retention rate of 95.8% after 100 cycles as well as excellent rate capability. Another sample calcinated at 900 °C exhibited good cycling stability. It is concluded that the structural stability and electrochemical performance of Li-rich layered oxide cathode materials were strongly dependent on calcination temperatures. The results suggest that a calcination temperature in a range of 850–900 °C could promote electrochemical performance of this type of cathode materials.

  18. Manganese Sesquioxide as Cathode Material for Multivalent Zinc Ion Battery with High Capacity and Long Cycle Life

    International Nuclear Information System (INIS)

    Jiang, Baozheng; Xu, Chengjun; Wu, Changle; Dong, Liubing; Li, Jia; Kang, Feiyu

    2017-01-01

    Highlights: • Manganese oxides with Mn(III) state is firstly reported to store zinc ion. • Zinc ion battery with α-Mn 2 O 3 cathode is assembled. • Storage mechanism of zinc ion in α-Mn 2 O 3 is investigated. - Abstract: Rechargeable zinc ion battery is considered as one of the most potential energy storage devices for large-scale energy storage system due to its safety, low-cost, high capacity and nontoxicity. However, only a few cathode materials have been studied for rechargeable zinc ion batteries. Here, we firstly report manganese sesquioxide (Mn 2 O 3 ) with Mn(III) state as cathode material for rechargeable zinc ion battery. The α-Mn 2 O 3 cathode displays a reversible capacity of 148 mAh g −1 , which is relatively high among all the reported cathode materials for ZIB. The cathode also exhibits good rate capability and excellent cycling stability with a long cycle life up to 2000 times. The ion storage mechanism of α-Mn 2 O 3 in zinc ion battery was also revealed. The pristine α-Mn 2 O 3 undergoes a reversible phase transition from bixbyite structure to layered-type zinc birnessite during the electrochemical zinc ion insertion and extraction. The results not only benefit for the practical application of rechargeable zinc ion battery, but also broaden the horizons of understanding the electrochemical behavior and mechanism of rechargeable zinc ion batteries.

  19. Synthesis and characterization of cathode, anode and electrolyte materials for rechargeable lithium batteries

    Science.gov (United States)

    Yang, Shoufeng

    Two new classes of cathode materials were studied: iron phosphate/sulfate materials and layered manganese oxides, both of which are low cost and had shown some potential. The first class of materials have poor conductivity and cyclability. I studied a number of methods for increasing the conductivity, and determined that grinding the material with carbon black was as effective as special in-situ coatings. The optimum carbon loading was determined to be between 6 and 15 wt%. Too much carbon reduces the volumetric energy density, whereas too little significantly increased cell polarization (reduced the rate of reaction). The kinetic and thermodynamic stability of LiFePO 4 was also studied and it was determined that over discharge protection will be needed as irreversible Li3PO4 can be formed at low potentials. A novel hydrothermal synthesis method was developed, but the significant level of Fe on the Li site reduces the reaction rate too much. In the case of the layered manganese oxide, cation substitution with Co and Ni is found to be effective in avoiding Jahn-Teller effects and improving electrochemistry. A wide range of tin compounds have been suggested as lithium storage media for advanced anode materials, as tin can store over 4 Li per Sn atom. Lithium hexafluorophosphate, LiPF6, is presently the salt of choice for LiCoO2 batteries, but it is expensive and dissolves some manganese compounds. The lithium bis(oxolato)borate (BOB) salt was recently reported, and I made a study of its use in cells with the LiFePO4 cathode and the tin anode. During its synthesis, it became clear that LiBOB is very reactive with many solvents, and these complexes were characterized to better understand this new material. In LiBOB the lithium is five coordinated, an unstable configuration for the lithium ion so that water and many other solvents rapidly react to make a six coordination. Only in the case of ethylene carbonate was the lithium found to be four coordinated. The Li

  20. The use and optimization of stainless steel mesh cathodes in microbial electrolysis cells

    KAUST Repository

    Zhang, Yimin; Merrill, Matthew D.; Logan, Bruce E.

    2010-01-01

    , and cathodes made of this material with high specific surface areas can achieve performance similar to carbon cathodes containing a platinum catalyst in MECs. SS mesh cathodes were examined here as a method to provide a higher surface area material than flat

  1. Manufacturing method for radioactive material containing vessel

    International Nuclear Information System (INIS)

    Kamino, Yoshikazu; Nishioka, Eiji; Toyota, Michinori.

    1997-01-01

    A containing vessel for radioactive materials (for example, spent fuels) comprises an inner cylinder made of stainless steel having a space for containing radioactive materials at the inside and an outer cylinder made of stainless steel disposed at the outer side of the inner cylinder. Lead homogenization is applied to a space between the inner and the outer cylinders to deposit a lead layer. Then, molten lead heated to a predetermined temperature is cast into the space between the inner and the outer cylinders. A valve is opened to discharge the molten lead in the space from a molten lead discharge pipe, and heated molten lead is injected from a molten lead supply pipe. Then, the discharge of the molten lead and the injection of the molten lead are stopped, and the lead in the space is coagulated. With such procedures, gaps are not formed between the lead of the homogenized portion and the lead of cast portion even when the thickness of the inner and the outer cylinders is great. (I.N.)

  2. Recycling of spent lithium-ion battery cathode materials by ammoniacal leaching.

    Science.gov (United States)

    Ku, Heesuk; Jung, Yeojin; Jo, Minsang; Park, Sanghyuk; Kim, Sookyung; Yang, Donghyo; Rhee, Kangin; An, Eung-Mo; Sohn, Jeongsoo; Kwon, Kyungjung

    2016-08-05

    As the production and consumption of lithium ion batteries (LIBs) increase, the recycling of spent LIBs appears inevitable from an environmental, economic and health viewpoint. The leaching behavior of Ni, Mn, Co, Al and Cu from treated cathode active materials, which are separated from a commercial LIB pack in hybrid electric vehicles, is investigated with ammoniacal leaching agents based on ammonia, ammonium carbonate and ammonium sulfite. Ammonium sulfite as a reductant is necessary to enhance leaching kinetics particularly in the ammoniacal leaching of Ni and Co. Ammonium carbonate can act as a pH buffer so that the pH of leaching solution changes little during leaching. Co and Cu can be fully leached out whereas Mn and Al are hardly leached and Ni shows a moderate leaching efficiency. It is confirmed that the cathode active materials are a composite of LiMn2O4, LiCoxMnyNizO2, Al2O3 and C while the leach residue is composed of LiNixMnyCozO2, LiMn2O4, Al2O3, MnCO3 and Mn oxides. Co recovery via the ammoniacal leaching is believed to gain a competitive edge on convenitonal acid leaching both by reducing the sodium hydroxide expense for increasing the pH of leaching solution and by removing the separation steps of Mn and Al. Copyright © 2016 Elsevier B.V. All rights reserved.

  3. Comprehensive Enhancement of Nanostructured Lithium-Ion Battery Cathode Materials via Conformal Graphene Dispersion.

    Science.gov (United States)

    Chen, Kan-Sheng; Xu, Rui; Luu, Norman S; Secor, Ethan B; Hamamoto, Koichi; Li, Qianqian; Kim, Soo; Sangwan, Vinod K; Balla, Itamar; Guiney, Linda M; Seo, Jung-Woo T; Yu, Xiankai; Liu, Weiwei; Wu, Jinsong; Wolverton, Chris; Dravid, Vinayak P; Barnett, Scott A; Lu, Jun; Amine, Khalil; Hersam, Mark C

    2017-04-12

    Efficient energy storage systems based on lithium-ion batteries represent a critical technology across many sectors including consumer electronics, electrified transportation, and a smart grid accommodating intermittent renewable energy sources. Nanostructured electrode materials present compelling opportunities for high-performance lithium-ion batteries, but inherent problems related to the high surface area to volume ratios at the nanometer-scale have impeded their adoption for commercial applications. Here, we demonstrate a materials and processing platform that realizes high-performance nanostructured lithium manganese oxide (nano-LMO) spinel cathodes with conformal graphene coatings as a conductive additive. The resulting nanostructured composite cathodes concurrently resolve multiple problems that have plagued nanoparticle-based lithium-ion battery electrodes including low packing density, high additive content, and poor cycling stability. Moreover, this strategy enhances the intrinsic advantages of nano-LMO, resulting in extraordinary rate capability and low temperature performance. With 75% capacity retention at a 20C cycling rate at room temperature and nearly full capacity retention at -20 °C, this work advances lithium-ion battery technology into unprecedented regimes of operation.

  4. Investigating the stability of cathode materials for rechargeable lithium ion batteries

    Science.gov (United States)

    Huang, Yiqing

    Lithium ion batteries are widely used in portable electronic devices and electric vehicles. However, safety is one of the most important issues for the Li-ion batteries' use. Some cathode materials, such as LiCoO 2, are thermally unstable in the charged state. Upon decomposition these cathode materials release O2, which could react with organic electrolyte, leading to a thermal runaway. Thus understanding the stability of the cathode materials is critical to the safety of lithium ion batteries. Olivine-type LiMnPO4 is a promising cathode material for lithium ion batteries because of its high energy density. We have revealed the critical role of carbon in the stability and thermal behaviour of olivine MnPO 4 obtained by chemical delithiation of LiMnPO4. (Li)MnPO 4 samples with various particle sizes and carbon contents were studied. Carbon-free LiMnPO4 obtained by solid state synthesis in O 2 becomes amorphous upon delithiation. Small amounts of carbon (0.3 wt.%) help to stabilize the olivine structure, so that completely delithiated crystalline olivine MnPO4 can be obtained. Larger amount of carbon (2 wt.%) prevents full delithiation. Heating in air, O2, or N 2 results in structural disorder (cathode materials and the electrolyte. The thermal stability of electrochemically delithiated Li0.1N 0.8C0.15Al0.05O2 (NCA), FePO4 (FP), Mn0.8Fe0.2PO4 (MFP), hydrothermally synthesized VOPO4, LiVOPO4 and electrochemically lithiated Li2VOPO4 is investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis, coupled with mass spectrometry (TGA-MS). The thermal stability is found in the order: NCA< VOPO4< MFP< FP=LiVOPO4=Li2VOPO4. Sealed capsule high pressure experiments show a phase transformation of VOPO4 → HVOPO4 → H2VOPO4 when VOPO4 reacts with electrolyte (1 M LiPF6 in EC: DMC=1:1) between 200 and 300 °C. Finally, we characterize the lithium storage and release mechanism of V2O5 aerogels by x-ray photoelectron spectroscopy (XPS). We study the

  5. High Energy Density Li-ion Cells for EV’s Based on Novel, High Voltage Cathode Material Systems

    Energy Technology Data Exchange (ETDEWEB)

    Kepler, Keith [Farasis Energy Inc; Slater, Michael [Farasis Energy Inc

    2018-03-14

    This Li-ion cell technology development project had three objectives: to develop advanced electrode materials and cell components to enable stable high-voltage operation; to design and demonstrate a Li-ion cell using these materials that meets the PHEV40 performance targets; and to design and demonstrate a Li-ion cell using these materials that meets the EV performance targets. The major challenge to creating stable high energy cells with long cycle life is system integration. Although materials that can give high energy cells are known, stabilizing them towards long-term cycling in the presence of other novel cell components is a major challenge. The major technical barriers addressed by this work include low cathode specific energy, poor electrolyte stability during high voltage operation, and insufficient capacity retention during deep discharge for Si-containing anodes. Through the course of this project, Farasis was able to improve capacity retention of NCM materials for 4.4+ V operation, through both surface treatment and bulk-doping approaches. Other material advances include increased rate capability and of HE-NCM materials through novel synthesis approach, doubling the relative capacity at 1C over materials synthesized using standard methods. Silicon active materials proved challenging throughout the project and ultimately were the limiting factor in the energy density vs. cycle life trade off. By avoiding silicon anodes for the lower energy PHEV design, we manufactured cells with intermediate energy density and long cycle life under high voltage operation for PHEV applications. Cells with high energy density for EV applications were manufactured targeting a 300 Wh/kg design and were able to achieve > 200 cycles.

  6. Novel copper redox-based cathode materials for room-temperature sodium-ion batteries

    Science.gov (United States)

    Xu, Shu-Yin; Wu, Xiao-Yan; Li, Yun-Ming; Hu, Yong-Sheng; Chen, Li-Quan

    2014-11-01

    Layered oxides of P2-type Na0.68Cu0.34Mn0.66O2, P2-type Na0.68Cu0.34Mn0.50Ti0.16O2, and O'3-type NaCu0.67Sb0.33O2 were synthesized and evaluated as cathode materials for room-temperature sodium-ion batteries. The first two materials can deliver a capacity of around 70 mAh/g. The Cu2+ is oxidized to Cu3+ during charging, and the Cu3+ goes back to Cu2+ upon discharging. This is the first demonstration of the highly reversible change of the redox couple of Cu2+/Cu3+ with high storage potential in secondary batteries.

  7. Synthesis of V2O5 microspheres by spray pyrolysis as cathode material for supercapacitors

    Science.gov (United States)

    Yin, Zhendong; Xu, Jie; Ge, Yali; Jiang, Qiaoya; Zhang, Yaling; Yang, Yawei; Sun, Yuping; Hou, Siyu; Shang, Yuanyuan; Zhang, Yingjiu

    2018-03-01

    Vanadium oxide (V2O5) microspheres have attracted considerable attention in the energy field due to their unique properties such as high stability and electrochemical activity. Here, massive V2O5 microspheres with smooth surface, hollow cavity and uniform particle sizes (0.4–1.5 μm), were synthesized by a facile spray pyrolysis process. Post-treatment at predefined temperatures effectively turned the microsphere shell into stacked nanorods with widths of 100 nm and lengths of 500 nm when processed at 500 °C for 3 h under nitrogen atmosphere, with enhanced crystallinity. When applied as cathode materials for supercapacitors, the post-treated V2O5 microspheres at 500 °C exhibited improved specific capacitance and longer discharge time. This is an effective method to manufacture massive V2O5 microspheres with tailored structure and potential applications in high-performance energy storage materials.

  8. Metal Nanoparticles and Carbon-Based Nanostructures as Advanced Materials for Cathode Application in Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Pietro Calandra

    2010-01-01

    Full Text Available We review the most advanced methods for the fabrication of cathodes for dye-sensitized solar cells employing nanostructured materials. The attention is focused on metal nanoparticles and nanostructured carbon, among which nanotubes and graphene, whose good catalytic properties make them ideal for the development of counter electrode substrates, transparent conducting oxide, and advanced catalyst materials.

  9. Methods for using novel cathode and electrolyte materials for solid oxide fuel cells and ion transport membranes

    Science.gov (United States)

    Jacobson, Allan J.; Wang, Shuangyan; Kim, Gun Tae

    2016-01-12

    Methods using novel cathode, electrolyte and oxygen separation materials operating at intermediate temperatures for use in solid oxide fuel cells and ion transport membranes include oxides with perovskite related structures and an ordered arrangement of A site cations. The materials have significantly faster oxygen kinetics than in corresponding disordered perovskites.

  10. Energy storage in hybrid organic-inorganic materials hexacyanoferrate-doped polypyrrole as cathode in reversible lithium cells

    DEFF Research Database (Denmark)

    Torres-Gomez, G,; Skaarup, Steen; West, Keld

    2000-01-01

    A study of the hybrid oganic-inorganic hexacyanoferrate-polypyrrole material as a cathode in rechargeable lithium cells is reported as part of a series of functional hybrid materials that represent a new concept in energy storage. The effect of synthesis temperatures of the hybrid in the specific...

  11. Investigating local degradation and thermal stability of charged nickel-based cathode materials through real-time electron microscopy.

    Science.gov (United States)

    Hwang, Sooyeon; Kim, Seung Min; Bak, Seong-Min; Cho, Byung-Won; Chung, Kyung Yoon; Lee, Jeong Yong; Chang, Wonyoung; Stach, Eric A

    2014-09-10

    In this work, we take advantage of in situ transmission electron microscopy (TEM) to investigate thermally induced decomposition of the surface of Li(x)Ni(0.8)Co(0.15)Al(0.05)O2 (NCA) cathode materials that have been subjected to different states of charge (SOC). While uncharged NCA is stable up to 400 °C, significant changes occur in charged NCA with increasing temperature. These include the development of surface porosity and changes in the oxygen K-edge electron energy loss spectra, with pre-edge peaks shifting to higher energy losses. These changes are closely related to O2 gas released from the structure, as well as to phase changes of NCA from the layered structure to the disordered spinel structure, and finally to the rock-salt structure. Although the temperatures where these changes initiate depend strongly on the state of charge, there also exist significant variations among particles with the same state of charge. Notably, when NCA is charged to x = 0.33 (the charge state that is the practical upper limit voltage in most applications), the surfaces of some particles undergo morphological and oxygen K-edge changes even at temperatures below 100 °C, a temperature that electronic devices containing lithium ion batteries (LIB) can possibly see during normal operation. Those particles that experience these changes are likely to be extremely unstable and may trigger thermal runaway at much lower temperatures than would be usually expected. These results demonstrate that in situ heating experiments are a unique tool not only to study the general thermal behavior of cathode materials but also to explore particle-to-particle variations, which are sometimes of critical importance in understanding the performance of the overall system.

  12. Study of LiFePO{sub 4} cathode materials coated with high surface area carbon

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Cheng-Zhang; Fey, George Ting-Kuo [Department of Chemical and Materials Engineering, National Central University, Chung-Li 32054 (China); Kao, Hsien-Ming [Department of Chemistry, National Central University, Chung-Li 32054 (China)

    2009-04-01

    LiFePO{sub 4} is a potential cathode material for 4 V lithium-ion batteries. Carbon-coated lithium iron phosphates were prepared using a high surface area carbon to react precursors through a solid-state process, during which LiFePO{sub 4} particles were embedded in amorphous carbon. The carbonaceous materials were synthesized by the pyrolysis of peanut shells under argon, where they were carbonized in a two-step process that occurred between 573 and 873 K. The shells were also treated with a proprietary porogenic agent with the goal of altering the pore structure and surface area of the pyrolysis products. The electrochemical properties of the as-prepared LiFePO{sub 4}/C composite cathode materials were systematically characterized by X-ray diffraction, scanning electron microscope, element mapping, energy dispersive spectroscopy, Raman spectroscopy, and total organic carbon (TOC) analysis. In LiFePO{sub 4}/C composites, the carbon not only increases rate capability, but also stabilizes capacity. In fact, the capacity of the composites increased with the specific surface area of carbon. The best result was observed with a composite made of 8.0 wt.% with a specific surface area of 2099 m{sup 2} g{sup -1}. When high surface area carbon was used as a carbon source to produce LiFePO{sub 4}, overall conductivity increased from 10{sup -8} to 10{sup -4} S cm{sup -1}, because the inhibition of particle growth during the final sintering process led to greater specific capacity, improved cycling properties and better rate capability compared to a pure olivine LiFePO{sub 4} material. (author)

  13. Strategies to curb structural changes of lithium/transition metal oxide cathode materials & the changes’ effects on thermal & cycling stability

    Science.gov (United States)

    Xiqian, Yu; Enyuan, Hu; Seongmin, Bak; Yong-Ning, Zhou; Xiao-Qing, Yang

    2016-01-01

    Structural transformation behaviors of several typical oxide cathode materials during a heating process are reviewed in detail to provide in-depth understanding of the key factors governing the thermal stability of these materials. We also discuss applying the information about heat induced structural evolution in the study of electrochemically induced structural changes. All these discussions are expected to provide valuable insights for designing oxide cathode materials with significantly improved structural stability for safe, long-life lithium ion batteries, as the safety of lithium-ion batteries is a critical issue; it is widely accepted that the thermal instability of the cathodes is one of the most critical factors in thermal runaway and related safety problems. Project supported by the U.S. Department of Energy, the Assistant Secretary for Energy Efficiency and Renewable Energy, Office of Vehicle Technologies (Grant No. DE-SC0012704).

  14. Closure for casks containing radioactive materials

    International Nuclear Information System (INIS)

    Hall, G.V.B.; Mallory, C.W.

    1990-01-01

    This patent describes an improved closure for covering and sealing an opening in a single cask for containing radioactive material, wherein the opening is characterized by a ledge. It comprises: an inner lid receivable within the opening and having a gasket means that is seatable over the ledge; an outer lid which is likewise receivable into the opening and securable therearound when the outer lid is rotated relative to the opening. The inner lid remaining stationary relative to the cask opening when the outer lid is rotated and having no torque applied thereto by the outer lid when the outer lid is rotated, and bolt means threadedly mounted through the outer lid for applying a compressive force between the inner and outer lids after the outer lid has been secured to the opening in order to depress the gasket means of the inner lid into sealing engagement with the ledge while avoiding the application of torsion between the gasket means and the ledge

  15. Containers for the transport of radioactive materials

    International Nuclear Information System (INIS)

    Bochard, C.

    1975-01-01

    The container for heat evolving radioactive materials has a metallic outer casing formed with outwardly projecting heat dissipating or cooling members, such as pins or fins, while each of its ends is formed with a flat flange which extends radially beyond the outer ends of the cooling members. A perforated wall extends between the flanges to define with same and with the periphery of the outer casing an annular space within which the cooling members are enclosed. This perforated wall is adapted to support a flexible covering sleeve the ends of which are clamped by inflatable seals between the periphery of the flanges and outer rings removably secured to the latter. Spraying means are provided within the aforesaid space to permit of projecting an uncontaminated liquid on the cooling members to cool the container before and/or while the latter is immersed in a loading and unloading pond with the sleeve mounted in position. The lower flange is provided with liquid collecting and evacuating means and compressed air may be injected into the said space to force the collected liquid outwardly. (auth)

  16. Novel Carbon Materials in the Cathode Formulation for High Rate Rechargeable Hybrid Aqueous Batteries

    Directory of Open Access Journals (Sweden)

    Xiao Zhu

    2017-11-01

    Full Text Available Novel carbon materials, carbon nanotubes (CNTs and porous graphene (PG, were exploited and used as conductive additives to improve the rate performance of LiMn2O4 cathode for the rechargeable aqueous Zn/LiMn2O4 battery, namely the rechargeable hybrid aqueous battery (ReHAB. Thanks to the long-range conductivity and stable conductive network provided by CNTs, the rate and cycling performances of LiMn2O4 cathode in ReHAB are highly improved—up to about 100 mAh·g−1 capacity is observed at 10 C (1 C = 120 mAh·g−1. Except for CNTs, porous graphene (PG with a high surface area, an abundant porous structure, and an excellent electrical conductivity facilitates the transportation of Li ions and electrons, which can also obviously enhance the rate capability of the ReHAB. This is important because the ReHAB could be charged/discharged in a few minutes, and this leads to potential application of the ReHAB in automobile industry.

  17. Graphitized Carbon: A Promising Stable Cathode Catalyst Support Material for Long Term PEMFC Applications.

    Science.gov (United States)

    Mohanta, Paritosh Kumar; Regnet, Fabian; Jörissen, Ludwig

    2018-05-28

    Stability of cathode catalyst support material is one of the big challenges of polymer electrolyte membrane fuel cells (PEMFC) for long term applications. Traditional carbon black (CB) supports are not stable enough to prevent oxidation to CO₂ under fuel cell operating conditions. The feasibility of a graphitized carbon (GC) as a cathode catalyst support for low temperature PEMFC is investigated herein. GC and CB supported Pt electrocatalysts were prepared via an already developed polyol process. The physical characterization of the prepared catalysts was performed using transmission electron microscope (TEM), X-ray Powder Diffraction (XRD) and inductively coupled plasma optical emission spectrometry (ICP-OES) analysis, and their electrochemical characterizations were conducted via cyclic voltammetry(CV), rotating disk electrode (RDE) and potential cycling, and eventually, the catalysts were processed using membrane electrode assemblies (MEA) for single cell performance tests. Electrochemical impedance spectroscopy (EIS) and scanning electrochemical microscopy (SEM) have been used as MEA diagonostic tools. GC showed superior stability over CB in acid electrolyte under potential conditions. Single cell MEA performance of the GC-supported catalyst is comparable with the CB-supported catalyst. A correlation of MEA performance of the supported catalysts of different Brunauer⁻Emmett⁻Teller (BET) surface areas with the ionomer content was also established. GC was identified as a promising candidate for catalyst support in terms of both of the stability and the performance of fuel cell.

  18. New Redox Polymers that Exhibit Reversible Cleavage of Sulfur Bonds as Cathode Materials.

    Science.gov (United States)

    Baloch, Marya; Ben Youcef, Hicham; Li, Chunmei; Garcia-Calvo, Oihane; Rodriguez, Lide M; Shanmukaraj, Devaraj; Rojo, Teofilo; Armand, Michel

    2016-11-23

    Two new cathode materials based on redox organosulfur polymers were synthesized and investigated for rechargeable lithium batteries as a proof-of-concept study. These cathodes offered good cycling performance owing to the absence of polysulfide solubility, which plagues Li/S systems. Herein, an aliphatic polyamine or a conjugated polyazomethine was used as the base to tether the redox-active species. The activity comes from the cleavage and formation of S-S or N-S bonds, which is made possible by the rigid conjugated backbone. The synthesized polymers were characterized through FTIR spectroscopy and thermogravimetric analysis (TGA). Galvanostatic measurements were performed to evaluate the discharge/charge cycles and characterize the performance of the lithium-based cells, which displayed initial discharge capacities of approximately 300 mA h g -1 at C/5 over 100 cycles with approximately 98 % Coulombic efficiency. © 2016 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  19. Liquid filter for liquids containing radioactive materials

    International Nuclear Information System (INIS)

    Rohleder, N.; Schwarz, F.

    1986-01-01

    A device for filtering radioactive liquids loaded with solids is described, which has a pressure-resistant housing with a lid and an incomer for the turbid liquid and a collecting space and drain for the filtrate at the bottom of the housing. A filter cartridge is present in this housing. Such a filtering device must be suitable for use in nuclear plants, must be easy to replace by remote control and must minimise the carrying over of radioactive particles. This problem should be solved by the filter cartridge consisting of a large number of horizontal filter plates stacked above one another, which carry a deep layer filter material acting in the sub-micron range. The turbid liquid runs into the centre of the stack of filter plates via a vertical central duct. The intermediate spaces between the filter places are connected to this central duct via the layer of filter material. The filter plates are sealed against one another on the outer circumference and have radial drain openings for the filtrate on the outside. The central duct is sealed at the lower end by a plate. When the filter cartridge is replaced, the radioactive waste in the filter cartridge remains safely enclosed and can be conditioned in suitable containers. (orig.) [de

  20. Cathodic processes in high-temperature molten salts for the development of new materials processing methods

    International Nuclear Information System (INIS)

    Schwandt, Carsten

    2017-01-01

    Molten salts play an important role in the processing of a range of commodity materials. This includes the large-scale production of iron, aluminium, magnesium and alkali metals as well as the refining of nuclear fuel materials. This presentation focuses on two more recent concepts in which the cathodic reactions in molten salt electrolytic cells are used to prepare high-value-added materials. Both were developed and advanced at the Department of Materials Science and Metallurgy at the University of Cambridge and are still actively being pursued. One concept is now generally known as the FFC-Cambridge process. The presentation will highlight the optimisation of the process towards high selectivities for tubes or particles depict a modification of the method to synthesize tin-filled carbon nanomaterial, and illustrate the implementation of a novel type of process control to enable the preparation of gramme quantities of material within a few hours with simple laboratory equipment. Also discussed will be the testing of these materials in lithium ion batteries

  1. Recycling of spent lithium-ion battery cathode materials by ammoniacal leaching

    Energy Technology Data Exchange (ETDEWEB)

    Ku, Heesuk; Jung, Yeojin; Jo, Minsang; Park, Sanghyuk [Department of Energy & Mineral Resources Engineering, Sejong University, Seoul 05006 (Korea, Republic of); Kim, Sookyung [Urban Mine Department, Korea Institute of Geoscience and Mineral Resources, 124 Gwahang-no, Yuseong-gu, Daejeon (Korea, Republic of); Yang, Donghyo, E-mail: ydh@kigam.re.kr [Urban Mine Department, Korea Institute of Geoscience and Mineral Resources, 124 Gwahang-no, Yuseong-gu, Daejeon (Korea, Republic of); Rhee, Kangin; An, Eung-Mo; Sohn, Jeongsoo [Urban Mine Department, Korea Institute of Geoscience and Mineral Resources, 124 Gwahang-no, Yuseong-gu, Daejeon (Korea, Republic of); Kwon, Kyungjung, E-mail: kfromberk@gmail.com [Department of Energy & Mineral Resources Engineering, Sejong University, Seoul 05006 (Korea, Republic of)

    2016-08-05

    Highlights: • Ammoniacal leaching is used to recover spent Li-ion battery cathode materials. • Leaching agents consist of ammonia, ammonium sulfite and ammonium carbonate. • Ammonium sulfite is a reductant and ammonium carbonate acts as pH buffer. • Co and Cu can be fully leached while Mn and Al are not leached. • Co recovery via ammoniacal leaching is economical compared to acid leaching. - Abstract: As the production and consumption of lithium ion batteries (LIBs) increase, the recycling of spent LIBs appears inevitable from an environmental, economic and health viewpoint. The leaching behavior of Ni, Mn, Co, Al and Cu from treated cathode active materials, which are separated from a commercial LIB pack in hybrid electric vehicles, is investigated with ammoniacal leaching agents based on ammonia, ammonium carbonate and ammonium sulfite. Ammonium sulfite as a reductant is necessary to enhance leaching kinetics particularly in the ammoniacal leaching of Ni and Co. Ammonium carbonate can act as a pH buffer so that the pH of leaching solution changes little during leaching. Co and Cu can be fully leached out whereas Mn and Al are hardly leached and Ni shows a moderate leaching efficiency. It is confirmed that the cathode active materials are a composite of LiMn{sub 2}O{sub 4}, LiCo{sub x}Mn{sub y}Ni{sub z}O{sub 2,} Al{sub 2}O{sub 3} and C while the leach residue is composed of LiNi{sub x}Mn{sub y}Co{sub z}O{sub 2}, LiMn{sub 2}O{sub 4}, Al{sub 2}O{sub 3}, MnCO{sub 3} and Mn oxides. Co recovery via the ammoniacal leaching is believed to gain a competitive edge on convenitonal acid leaching both by reducing the sodium hydroxide expense for increasing the pH of leaching solution and by removing the separation steps of Mn and Al.

  2. Free energy for protonation reaction in lithium-ion battery cathode materials

    International Nuclear Information System (INIS)

    Benedek, R.; Thackeray, M. M.; van de Walle, A.

    2008-01-01

    Calculations are performed of free energies for proton-for-lithium-ion exchange reactions in lithium-ion battery cathode materials. First-principles calculations are employed for the solid phases and tabulated ionization potential and hydration energy data for aqueous ions. Layered structures, spinel LiMn 2 O 4 , and olivine LiFePO 4 are considered. Protonation is most favorable energetically in layered systems, such as Li 2 MnO 3 and LiCoO 2 . Less favorable are ion-exchange in spinel LiMn 2 O 4 and LiV 3 O 8 . Unfavorable is the substitution of protons for Li in olivine LiFePO 4 , because of the large distortion of the Fe and P coordination polyhedra. The reaction free energy scales roughly linearly with the volume change in the reaction

  3. Thermal Stability and Reactivity of Cathode Materials for Li-Ion Batteries.

    Science.gov (United States)

    Huang, Yiqing; Lin, Yuh-Chieh; Jenkins, David M; Chernova, Natasha A; Chung, Youngmin; Radhakrishnan, Balachandran; Chu, Iek-Heng; Fang, Jin; Wang, Qi; Omenya, Fredrick; Ong, Shyue Ping; Whittingham, M Stanley

    2016-03-23

    The thermal stability of electrochemically delithiated Li0.1Ni0.8Co0.15Al0.05O2 (NCA), FePO4 (FP), Mn0.8Fe0.2PO4 (MFP), hydrothermally synthesized VOPO4, LiVOPO4, and electrochemically lithiated Li2VOPO4 is investigated by differential scanning calorimetry (DSC) and thermogravimetric analysis, coupled with mass spectrometry (TGA-MS). The thermal stability of the delithiated materials is found to be in the order of NCA cathode is indeed predicted to be marginally less stable than FP but significantly more stable than NCA in the absence of electrolyte. An analysis of the reaction equilibria between VOPO4 and EC using a multicomponent phase diagram approach yields products and reaction enthalpies that are highly consistent with the experiment results.

  4. Effect of CeO2-coating on the electrochemical performances of LiFePO4/C cathode material

    International Nuclear Information System (INIS)

    Yao Jingwen; Wu Feng; Qiu Xinping; Li Ning; Su Yuefeng

    2011-01-01

    Highlights: → The first study the effect of CeO 2 coating on LiFePO 4 /C at low temperature. → Coated cathode shows improved capacities at high rates and low temperature. → CeO 2 -coating decreases electrode polarization and increases charge-transfer reaction activity. - Abstract: The effect of CeO 2 coating on LiFePO 4 /C cathode material has been investigated. The crystalline structure and morphology of the synthesized powders have been characterized by XRD, SEM, TEM and their electrochemical performances both at room temperature and low temperature are evaluated by CV, EIS and galvanostatic charge/discharge tests. It is found that, nano-CeO 2 particles distribute on the surface of LiFePO 4 without destroying the crystal structure of the bulk material. The CeO 2 -coated LiFePO 4 /C cathode material shows improved lithium insertion/extraction capacity and electrode kinetics, especially at high rates and low temperature. At -20 deg. C, the CeO 2 -coated material delivers discharge capacity of 99.7 mAh/g at 0.1C rate and the capacity retention of 98.6% is obtained after 30 cycles at various charge/discharge rates. The results indicate that the surface treatment should be an effective way to improve the comprehensive properties of the cathode materials for lithium ion batteries.

  5. Structural and Electrical Properties of Lithium-Ion Rechargeable Battery Using the LiFePO4/Carbon Cathode Material.

    Science.gov (United States)

    Kim, Young-Sung; Jeoung, Tae-Hoon; Nam, Sung-Pill; Lee, Seung-Hwan; Kim, Jea-Chul; Lee, Sung-Gap

    2015-03-01

    LiFePO4/C composite powder as cathode material and graphite powder as anode material for Li-ion batteries were synthesized by using the sol-gel method. An electrochemical improvement of LiFePO4 materials has been achieved by adding polyvinyl alcohol as a carbon source into as-prepared materials. The samples were characterized by elemental analysis (EA), X-ray diffraction (XRD), and field emission scanning electron microscopy (FE-EM). The chemical composition of LiFePO4/C powders was in a good agreement with that of the starting solution. The capacity loss after 500 cycles of LiFePO4/C cell is 11.1% in room temperature. These superior electrochemical properties show that LiFePO4/C composite materials are promising candidates as cathode materials.

  6. Manufacturing method for radioactive material containing vessel

    International Nuclear Information System (INIS)

    Nishioka, Hideharu; Matsushita, Kazuo; Toyota, Michinori.

    1997-01-01

    Lead homogenization is applied on the inner surface of a space formed between an inner cylinder and an outer cylinder, and a molten lead heated to about 400 to 500degC is cast into a space formed between the inner cylinder and the outer cylinder in a state where the inner and the outer cylinders are heated to from 200 to 300degC. The space formed between the inner cylinder and the outer cylinder is heated to and kept at 330degC or higher for at least 2minutes after the casting of the molten lead, and then it is cooled. Thus, lowering of density of the molten lead due to excess elevation of temperature or dropping of the lead at the homogenization portion by heating the inner and the outer cylinders to an excessively high temperature are not caused. In addition, formation of gaps in the boundary between the inner cylinder and the outer cylinder or between the lead of the homogenized portion and that of the cast portion due to the melting of the lead of the homogenized portion in the space is prevented reliably thereby capable of forming a satisfactory shielding member. Then, even when the thickness of the inner cylinder and the outer cylinder is large, radioactive material containing vessel excellent in heat releasing property and radiation shielding property can be manufactured. (N.H.)

  7. Advanced carbon materials/olivine LiFePO4 composites cathode for lithium ion batteries

    Science.gov (United States)

    Gong, Chunli; Xue, Zhigang; Wen, Sheng; Ye, Yunsheng; Xie, Xiaolin

    2016-06-01

    In the past two decades, LiFePO4 has undoubtly become a competitive candidate for the cathode material of the next-generation LIBs due to its abundant resources, low toxicity and excellent thermal stability, etc. However, the poor electronic conductivity as well as low lithium ion diffusion rate are the two major drawbacks for the commercial applications of LiFePO4 especially in the power energy field. The introduction of highly graphitized advanced carbon materials, which also possess high electronic conductivity, superior specific surface area and excellent structural stability, into LiFePO4 offers a better way to resolve the issue of limited rate performance caused by the two obstacles when compared with traditional carbon materials. In this review, we focus on advanced carbon materials such as one-dimensional (1D) carbon (carbon nanotubes and carbon fibers), two-dimensional (2D) carbon (graphene, graphene oxide and reduced graphene oxide) and three-dimensional (3D) carbon (carbon nanotubes array and 3D graphene skeleton), modified LiFePO4 for high power lithium ion batteries. The preparation strategies, structure, and electrochemical performance of advanced carbon/LiFePO4 composite are summarized and discussed in detail. The problems encountered in its application and the future development of this composite are also discussed.

  8. Studies of selected synthesis procedures of the conducting LiFePO{sub 4}-based composite cathode materials for Li-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Ojczyk, W.; Marzec, J.; Swierczek, K.; Zajac, W.; Molenda, J. [Faculty of Materials Science and Ceramics, AGH University of Science and Technology, Al. Mickiewicza 30, 30-059 Krakow (Poland); Molenda, M.; Dziembaj, R. [Faculty of Chemistry, Jagiellonian University, ul. R. Ingardena 3, 30-060 Krakow (Poland)

    2007-11-15

    In this paper technological aspects of a synthesis of phospho-olivine LiFePO{sub 4} based composite cathode materials for lithium batteries are presented. An effective synthesis route yielding a highly conductive composite cathode material was developed. The structural, electrical and electrochemical properties of these materials were investigated. It was shown that the enhanced conductivity of the cathode material is due to the presence of a thin layer of the reduced material which has metallic properties, which is formed on the grain surfaces of the phospho-olivine. We propose a synthesis route yielding LiFePO{sub 4}/Fe{sub 2}P composite material. (author)

  9. About the Compatibility between High Voltage Spinel Cathode Materials and Solid Oxide Electrolytes as a Function of Temperature.

    Science.gov (United States)

    Miara, Lincoln; Windmüller, Anna; Tsai, Chih-Long; Richards, William D; Ma, Qianli; Uhlenbruck, Sven; Guillon, Olivier; Ceder, Gerbrand

    2016-10-12

    The reactivity of mixtures of high voltage spinel cathode materials Li 2 NiMn 3 O 8 , Li 2 FeMn 3 O 8 , and LiCoMnO 4 cosintered with Li 1.5 Al 0.5 Ti 1.5 (PO 4 ) 3 and Li 6.6 La 3 Zr 1.6 Ta 0.4 O 12 electrolytes is studied by thermal analysis using X-ray-diffraction and differential thermoanalysis and thermogravimetry coupled with mass spectrometry. The results are compared with predicted decomposition reactions from first-principles calculations. Decomposition of the mixtures begins at 600 °C, significantly lower than the decomposition temperature of any component, especially the electrolytes. For the cathode + Li 6.6 La 3 Zr 1.6 Ta 0.4 O 12 mixtures, lithium and oxygen from the electrolyte react with the cathodes to form highly stable Li 2 MnO 3 and then decompose to form stable and often insulating phases such as La 2 Zr 2 O 7 , La 2 O 3 , La 3 TaO 7 , TiO 2 , and LaMnO 3 which are likely to increase the interfacial impedance of a cathode composite. The decomposition reactions are identified with high fidelity by first-principles calculations. For the cathode + Li 1.5 Al 0.5 Ti 1.5 (PO 4 ) 3 mixtures, the Mn tends to oxidize to MnO 2 or Mn 2 O 3 , supplying lithium to the electrolyte for the formation of Li 3 PO 4 and metal phosphates such as AlPO 4 and LiMPO 4 (M = Mn, Ni). The results indicate that high temperature cosintering to form dense cathode composites between spinel cathodes and oxide electrolytes will produce high impedance interfacial products, complicating solid state battery manufacturing.

  10. Evidence of the Current Collector Effect: Study of the SOFC Cathode Material Ca3Co4O9+d

    NARCIS (Netherlands)

    Rolle, A.; Thoréton, V.; Rozier, P.; Capoen, E.; Mentré, O.; Boukamp, Bernard A.; Daviero-Minaud, S.

    2012-01-01

    In the study of the performance of solid oxide fuel cell (SOFC) electrodes, the possible influence of the applied current collector is often not mentioned or recognized. In this article, as part of an optimization study of the potentially attractive Ca3Co4O9+δ cathode material (Ca349), special

  11. Electrochemical performance of NCM/LFP/Al composite cathode materials for lithium-ion batteries

    Science.gov (United States)

    Allahyari, Ehsan; Ghorbanzadeh, Milad; Riahifar, Reza; Hadavi, S. M. M.

    2018-05-01

    The LiNi0.5Mn0.3Co0.2O2 (NCM) was synthesized via conventional solution combustion synthesis method. Different amounts of LiFePO4 (10, 20 and 30 wt%) were added to NCM via the ball milling technique to improve electrochemical performance including discharge capacity, cycle stability, and rate capability. The LiNi0.5Mn0.3Co0.2O2/LiFePO4 containing 20 wt% LiFePO4 was considered as the optimum composition according to the electrochemical results and SEM images. The Al powder was added to optimum LiNi0.5Mn0.3Co0.2/LiFePO4-0.2 composite through planetary ball mill to enhance the conductivity of LiNi0.5Mn0.3Co0.2O2/LiFePO4-0.2. The LiNi0.5Mn0.3Co0.2O2/LiFePO4-0.2/Al composite cathodes provide better electrochemical performance compared to pure LiNi0.5Mn0.3Co0.2O2 cathodes. The results indicate that by addition of 20 wt% of LiFePO4, the internal resistance of the electrode as well as the charge transfer resistance are reduced. Due to the strong P–O bond of the PO4 in LiFePO4, side reactions between the active electrode and electrolyte is prevented. In addition, according to weakness of the Ionic conductivity in solid electrolyte, in this paper aluminum powders added to the electrode for resolving this problem.

  12. Cathode materials produced by spray flame synthesis for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Hamid, NoorAshrina Binti A.

    2013-07-03

    Lithium ion batteries are one of the most enthralling rechargeable energy storage systems for portable application due to their high energy density. Nevertheless, with respect to electromobility innovation towards better electrochemical properties such as higher energy and power density is required. Altering the cathode material used in Li-ion batteries is favorable since the mass- and volume performance is closely related to the cathode electrode mass. Instead of using LiCoO{sub 2} as cathode electrode, LiFePO{sub 4} has gained serious attention as this material owns a high theoretical capacity of 170 mAh g{sup -1}. It is non-toxic, cheap and consists of abundant materials but suffers from low electronic and ionic conductivity. Utilization of nanotechnology methods in combination with composite formation is known to cure this problem effectively. In this work, a new combination of techniques using highly scalable gas-phase synthesis namely spray-flame synthesis and subsequent solid-state reaction has been used to synthesize nanocomposite LiFePO{sub 4}/C. At first this work deals with the formation and characterization of nanosize FePO{sub 4} from a solution of iron(III)acetylacetonate and tributyl phosphate in toluene using spray-flame synthesis. It was shown that a subsequent solid state reaction with Li{sub 2}CO{sub 3} and glucose yielded a LiFePO{sub 4}/C nanocomposite with very promising electrochemical properties. Based on these initial findings the influence of two synthesis parameter - carbon content and annealing temperature - was investigated towards the physicochemical properties of LiFePO{sub 4}/C. It was shown that an annealing temperature of 700 C leads to high purity composite materials consisting of crystalline LiFePO{sub 4} with crystallite sizes well below 100 nm and amorphous carbon consisting of disordered and graphite-like carbon. Variation of glucose amount between 10 and 30 wt% resulted in carbon contents between 2.1 and 7.3 wt%. In parallel

  13. Cathode materials produced by spray flame synthesis for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Hamid, NoorAshrina Binti A.

    2013-07-03

    Lithium ion batteries are one of the most enthralling rechargeable energy storage systems for portable application due to their high energy density. Nevertheless, with respect to electromobility innovation towards better electrochemical properties such as higher energy and power density is required. Altering the cathode material used in Li-ion batteries is favorable since the mass- and volume performance is closely related to the cathode electrode mass. Instead of using LiCoO{sub 2} as cathode electrode, LiFePO{sub 4} has gained serious attention as this material owns a high theoretical capacity of 170 mAh g{sup -1}. It is non-toxic, cheap and consists of abundant materials but suffers from low electronic and ionic conductivity. Utilization of nanotechnology methods in combination with composite formation is known to cure this problem effectively. In this work, a new combination of techniques using highly scalable gas-phase synthesis namely spray-flame synthesis and subsequent solid-state reaction has been used to synthesize nanocomposite LiFePO{sub 4}/C. At first this work deals with the formation and characterization of nanosize FePO{sub 4} from a solution of iron(III)acetylacetonate and tributyl phosphate in toluene using spray-flame synthesis. It was shown that a subsequent solid state reaction with Li{sub 2}CO{sub 3} and glucose yielded a LiFePO{sub 4}/C nanocomposite with very promising electrochemical properties. Based on these initial findings the influence of two synthesis parameter - carbon content and annealing temperature - was investigated towards the physicochemical properties of LiFePO{sub 4}/C. It was shown that an annealing temperature of 700 C leads to high purity composite materials consisting of crystalline LiFePO{sub 4} with crystallite sizes well below 100 nm and amorphous carbon consisting of disordered and graphite-like carbon. Variation of glucose amount between 10 and 30 wt% resulted in carbon contents between 2.1 and 7.3 wt%. In parallel

  14. Charging material into a container and closing the container

    International Nuclear Information System (INIS)

    Critchley, R.J.; Oldham, S.R.

    1989-01-01

    Radioactive waste material is passed from a cell through a port into a storage drum which has a mouth with a removable lid. A port door includes an electromagnet to hold the lid to the door and both are moved into the cell by a pneumatic cylinder to allow loading of the drum and after re-closure of door and lid swaging tools operate to deform the lid to form one or more lips which engage under the margin around mouth to resist separation of the lid from the drum. Seals are provided. The swaging tools, or a single swaging tool, can be rotatably mounted on the port door. (author)

  15. Preparation of iron-deposited graphite surface for application as cathode material during electrochemical vat-dyeing process

    International Nuclear Information System (INIS)

    Anbu Kulandainathan, M.; Kiruthika, K.; Christopher, G.; Babu, K. Firoz; Muthukumaran, A.; Noel, M.

    2008-01-01

    Iron-deposited graphite surfaces were prepared, characterized and employed as cathode materials for electrochemical vat-dyeing process containing very low concentration of sodium dithionite. The electrodeposition, in presence of ammonium thiocyanate and gelatin or animal glue as binding additives, were found to give finer iron deposits for improved electrochemical dyeing application. The electrodeposits were characterized using scanning electron microscopy, electron-dispersive X-ray spectroscopy and X-ray diffraction methods, before and after electrochemical dyeing process. The electrochemical activity of the iron-deposited graphite electrodes always stored in water seems to depend on the surface-bound Fe 3+ /Fe 2+ redox species. Vat dyes like C.I. Vat Violet 1, C.I. Vat Green 1 and C.I. Vat Blue 4 could be efficiently dyed employing these above electrode materials. The colour intensity and washing fastness of the dyed fabrics were found to be equal with conventionally dyed fabrics. The electrodes could also be reused for the dyeing process

  16. Separation factor dependence upon cathode material for tritium separation from heavy water by electrolysis

    International Nuclear Information System (INIS)

    Ogata, Y.; Sakuma, Y.; Ohtani, N.; Kotaka, M.

    2002-01-01

    Using three cathode materials, i.e. carbon (C), stainless steel (SUS), and nickel (Ni), tritium was separated from heavy water by electrolysis, and the separation factors were compared. To separate hydrogen isotopes, heavy water was electrolyzed by an electrolysis device with a solid polymer electrode (SPE), which needed no electrolyte additives for electrolysis. The anode was made of 3 mm thickness of a sintered porous titanium plate covered with iridium oxide. The cathode was made of the same thickness of a sintered porous carbon, stainless steel, or nickel plate. Heavy water or light water spiked with tritiated water was electrolyzed 20 A x 60 min with the electrolysis cell temperature at 10, 20 or 30degC, and 15 A x 80 min at 5degC. The produced hydrogen and oxygen gases were recombined using a palladium catalyst with nitrogen gas as a carrier. The activities of the water in the electrolysis cell and of the recombined water were analyzed using a liquid scintillation counter. The apparent D-T separation factor (SF D/T ) and H-T separation factor (SF H/T ) were calculated as quotient the specific activity of the water in the cell divided by that of the recombined water. The electrolysis potential to keep the current 20 A was 2-3 V. The average yields of the recombined water were 95%. At the cell temperature of 20degC, SF D/T (C), SF D/T (SUS), and SF D/T (Ni) were 2.42, 2.17, and 2.05, respectively. At the same temperature, SF H/T (C), SF H/T (SUS), and SF H/T (Ni) were 12.5, 10.8, and 11.8, respectively. The SFs were in agreement with the results in other works. The SFs were changed with the cell temperature. (author)

  17. Mo-containing tetrahedral amorphous carbon deposited by dual filtered cathodic vacuum arc with selective pulsed bias voltage

    International Nuclear Information System (INIS)

    Pasaja, Nitisak; Sansongsiri, Sakon; Intarasiri, Saweat; Vilaithong, Thiraphat; Anders, Andre

    2007-01-01

    Metal-containing tetrahedral amorphous carbon films were produced by dual filtered cathodic vacuum arc plasma sources operated in sequentially pulsed mode. Negatively pulsed bias was applied to the substrate when carbon plasma was generated, whereas it was absent when the molybdenum plasma was presented. Film thickness was measured after deposition by profilometry. Glass slides with silver pads were used as substrates for the measurement of the sheet resistance. The microstructure and composition of the films were characterized by Raman spectroscopy and Rutherford backscattering, respectively. It was found that the electrical resistivity decreases with an increase of the Mo content, which can be ascribed to an increase of the sp 2 content and an increase of the sp 2 cluster size

  18. 30 CFR 56.16004 - Containers for hazardous materials.

    Science.gov (United States)

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Containers for hazardous materials. 56.16004 Section 56.16004 Mineral Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND... Storage and Handling § 56.16004 Containers for hazardous materials. Containers holding hazardous materials...

  19. 30 CFR 57.16004 - Containers for hazardous materials.

    Science.gov (United States)

    2010-07-01

    ... 30 Mineral Resources 1 2010-07-01 2010-07-01 false Containers for hazardous materials. 57.16004 Section 57.16004 Mineral Resources MINE SAFETY AND HEALTH ADMINISTRATION, DEPARTMENT OF LABOR METAL AND... Storage and Handling § 57.16004 Containers for hazardous materials. Containers holding hazardous materials...

  20. Preparation of mesohollow and microporous carbon nanofiber and its application in cathode material for lithium–sulfur batteries

    International Nuclear Information System (INIS)

    Wu, Yuanhe; Gao, Mingxia; Li, Xiang; Liu, Yongfeng; Pan, Hongge

    2014-01-01

    Highlights: • Mesohollow and microporous carbon fibers were prepared via electrospinning and carbonization. • Sulfur (S) incorporated into the porous fibers by thermal heating in 60 wt.%, forming composite. • S fills fully in the micropores and partially in the mesohollows of the carbon fibers. • The composite shows high capacity and capacity retention as cathode material for Li–S batteries. • Mesohollow and microporous structure is effective in improving the property of S cathode. - Abstract: Mesohollow and microporous carbon nanofibers (MhMpCFs) were prepared by a coaxial electrospinning with polyacrylonitrile (PAN) and polymethylmethacrylate (PMMA) as outer and inner spinning solutions followed by a carbonization. The carbon fibers were thermal treated with sublimed sulfur to form S/MhMpCFs composite, which was used as cathode material for lithium–sulfur batteries. Electrochemical study shows that the S/MhMpCFs cathode material provides a maximum capacity of 815 mA h/g after several cycles of activation, and the capacity retains 715 mA h/g after 70 cycles, corresponding to a retention of 88%. The electrochemical property of the S/MhMpCFs composite is much superior than the S-incorporated solid carbon fibers prepared from electrospinning of single PAN. The mechanism of the enhanced electrochemical property of the S/MhMpCFs composite is discussed

  1. High-Thermal- and Air-Stability Cathode Material with Concentration-Gradient Buffer for Li-Ion Batteries.

    Science.gov (United States)

    Shi, Ji-Lei; Qi, Ran; Zhang, Xu-Dong; Wang, Peng-Fei; Fu, Wei-Gui; Yin, Ya-Xia; Xu, Jian; Wan, Li-Jun; Guo, Yu-Guo

    2017-12-13

    Delivery of high capacity with high thermal and air stability is a great challenge in the development of Ni-rich layered cathodes for commercialized Li-ion batteries (LIBs). Herein we present a surface concentration-gradient spherical particle with varying elemental composition from the outer end LiNi 1/3 Co 1/3 Mn 1/3 O 2 (NCM) to the inner end LiNi 0.8 Co 0.15 Al 0.05 O 2 (NCA). This cathode material with the merit of NCM concentration-gradient protective buffer and the inner NCA core shows high capacity retention of 99.8% after 200 cycles at 0.5 C. Furthermore, this cathode material exhibits much improved thermal and air stability compared with bare NCA. These results provide new insights into the structural design of high-performance cathodes with high energy density, long life span, and storage stability materials for LIBs in the future.

  2. Rechargeable lithium/polymer cathode batteries

    Science.gov (United States)

    Osaka, Tetsuya; Nakajima, Toshiki; Shiota, Koh; Owens, Boone B.

    1989-06-01

    Polypyrrole (PPy) and polyaniline (PAn) were investigated for cathode materials of rechargeable lithium batteries. PPy films prepared with PF6(-) anion and/or platinum substrate precoated with nitrile butadiene rubber (NBR) were excellent cathode materials because of rough and/or highly oriented film structure. PAn films were successfully prepared from non-aqueous propylene carbonate solution containing aniline, CF3COOH and lithium perchlorate. Its acidity strongly affects the anion doping-undoping behavior. The PAn cathode prepared in high acidic solution (e.g., 4:1 ratio of acid:aniline) gives the excellent battery performance.

  3. Intercalation of Mg-ions in layered V2O5 cathode materials for rechargeable Mg-ion batteries

    DEFF Research Database (Denmark)

    Sørensen, Daniel Risskov; Johannesen, Pætur; Christensen, Christian Kolle

    The development of functioning rechargeable Mg-ion batteries is still in its early stage, and a coarse screening of suitable cathode materials is still on-going. Within the intercalation-type cathodes, layered crystalline materials are of high interest as they are known to perform well in Li-ion...... intercalation batteries and are also increasingly being explored for Na-ion batteries. Here, we present an investigation of the layered material orthorhombic V2O5, which is a classical candidate for an ion-intercalation material having a high theoretical capacity1. We present discharge-curves for the insertion...... discharge. This indicates that the degradation is highly associated with formation of ion-blocking layers on the anode....

  4. Depression cathode structure for cathode ray tubes having surface smoothness and method for producing same

    International Nuclear Information System (INIS)

    Rychlewski, T.V.

    1984-01-01

    Depression cathode structures for cathode ray tubes are produced by dispensing liquid cathode material into the depression of a metallic supporting substrate, removing excess cathode material by passing a doctor blade across the substrate surface and over the depression, and drying the cathode layer to a substantially immobile state. The cathode layer may optionally be further shaped prior to substantially complete drying thereof

  5. Characterization and electrochemical performances of MoO2 modified LiFePO4/C cathode materials synthesized by in situ synthesis method

    International Nuclear Information System (INIS)

    He, Jichuan; Wang, Haibin; Gu, Chunlei; Liu, Shuxin

    2014-01-01

    Graphical abstract: The MoO 2 modified LiFePO 4 /C cathode materials were synthesized by in situ synthesis method. MoO 2 can sufficiently coat on the LiFePO 4 /C particles surface and does not alter LiFePO 4 crystal structure, and the adding of MoO 2 decreases the particles size and increases the tap density of cathode materials. The existence of MoO 2 improves electrochemical performance of LiFePO 4 cathode materials in specific capability and lithium ion diffusion and charge transfer resistance of cathode materials. - Highlights: • The MoO 2 modified LiFePO 4 /C cathode materials were synthesized by in situ synthesis method. • The existence of MoO 2 decreases the particles size and increases the tap density of cathode materials. • MoO 2 can sufficiently coat on the surface of LiFePO 4 /C cathode materials. • The existence of MoO 2 enhanced electrochemical performance of LiFePO 4 /C cathode materials. - Abstract: The MoO 2 modified LiFePO 4 /C cathode materials were synthesized by in situ synthesis method. Phase compositions and microstructures of the products were characterized by X-ray powder diffraction (XRD), SEM, TEM and EDS. Results indicate that MoO 2 can sufficiently coat on the LiFePO 4 surface and does not alter LiFePO 4 crystal structure, the existence of MoO 2 decreases the particles size and increases the tap density of cathode materials. The electrochemical behavior of cathode materials was analyzed using galvanostatic measurement, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The results show that the existence of MoO 2 improves electrochemical performance of LiFePO 4 cathode materials in specific capability and lithium ion diffusion and charge transfer resistance. The initial charge–discharge specific capacity and apparent lithium ion diffusion coefficient increase, the charge transfer resistance decreases with MoO 2 content and maximizes around the MoO 2 content is 5 wt%. It has been had further proved that

  6. Reduced Graphene Oxide Decorated Na3V2(PO43 Microspheres as Cathode Material With Advanced Sodium Storage Performance

    Directory of Open Access Journals (Sweden)

    Hezhang Chen

    2018-05-01

    Full Text Available Reduced graphene oxide (rGO sheet decorated Na3V2(PO43 (NVP microspheres were successfully synthesized by spray-drying method. The NVP microspheres were embedded by rGO sheets, and the surface of the particles were coated by rGO sheets and amorphous carbon. Thus, the carbon conductive network consisted of rGO sheets and amorphous carbon generated in the cathode material. NVP microspheres decorated with different content of rGO (about 0, 4, 8, and 12 wt% were investigated in this study. The electrochemical performance of NVP exhibited a significant enhancement after rGO introduction. The electrode containing about 8 wt% rGO (NVP/G8 showed the best rate and cycle performance. NVP/G8 electrode exhibited the discharge capacity of 64.0 mAh g−1 at 70°C, and achieved high capacity retention of 95.5% after cycling at 10°C for 100 cycles. The polarization of the electrode was inhibited by the introduction of rGO sheets. Meanwhile, compared with the pristine NVP electrode, NVP/G8 electrode exhibited small resistance and high diffusion coefficient of sodium ions.

  7. Photo-assisted electrochemical abatement of trifluralin using a cathode containing a C60-carbon nanotubes composite.

    Science.gov (United States)

    Hasanzadeh, Aliyeh; Khataee, Alireza; Zarei, Mahmoud; Joo, Sang Woo

    2018-05-01

    This work reports the potential application of modified gas-diffusion electrode (GDE) with C 60 -CNT composite, as a stable and efficient cathode material for degradation of trifluralin (TRL) pesticide by photo-assisted electrochemical (PE) process. C 60 -CNT composite was prepared and characterized. Subsequently, a novel C 60 -CNT composite modified GDE cathode was developed and the electrochemical and physical characteristics of the modified GDEs were studied. C 60 -CNT composite/GDE showed great efficiencies for electro-generating H 2 O 2 , owing to huge surface area and high conductivity. Afterwards, a comparative study of TRL oxidation via photolysis, anodic oxidation (AO) and PE processes using C 60 -CNT composite/GDE revealed the degradation percentages of 42.2, 48.5 and 93.4%, respectively, after 180 min of treatment. The TRL degradation followed a pseudo-first-order kinetics, being faster in the order: photolysis composite/GDE exhibited great performance for the degradation of TRL (20 mg L -1 ) under its original pH, Na 2 SO 4 electrolyte concentration of 0.05 mol L -1 , applied current intensity of 300 mA, and flow rate of 12.5 L h -1 . TOC results displayed that 92.8% of TRL was mineralized after 8 h of PE process. In addition, a plausible pathway for mineralization of TRL was proposed according to the identified by-products detected by means of gas chromatography-mass spectroscopy (GC-MS), High-performance liquid chromatography (HPLC) and ion chromatography analyses. Copyright © 2018 Elsevier Ltd. All rights reserved.

  8. Determination of the mechanism and extent of surface degradation in Ni-based cathode materials after repeated electrochemical cycling

    Directory of Open Access Journals (Sweden)

    Sooyeon Hwang

    2016-09-01

    Full Text Available We take advantage of scanning transmission electron microscopy and electron energy loss spectroscopy to investigate the changes in near-surface electronic structure and quantify the degree of local degradation of Ni-based cathode materials with the layered structure (LiNi0.8Mn0.1Co0.1O2 and LiNi0.4Mn0.3Co0.3O2 after 20 cycles of delithiation and lithiation. Reduction of transition metals occurs in the near-surface region of cathode materials: Mn is the major element to be reduced in the case of relatively Mn-rich composition, while reduction of Ni ions is dominant in Ni-rich materials. The valences of Ni and Mn ions are complementary, i.e., when one is reduced, the other is oxidized in order to maintain charge neutrality. The depth of degradation zone is found to be much deeper in Ni-rich materials. This comparative analysis provides important insights needed for the devising of new cathode materials with high capacity as well as long lifetime.

  9. Defect physics vis-à-vis electrochemical performance in layered mixed-metal oxide cathode materials

    Science.gov (United States)

    Hoang, Khang; Johannes, Michelle

    Layered mixed-metal oxides with different compositions of (Ni,Co,Mn) [NCM] or (Ni,Co,Al) [NCA] have been used in commercial lithium-ion batteries. Yet their defect physics and chemistry is still not well understood, despite having important implications for the electrochemical performance. In this presentation, we report a hybrid density functional study of intrinsic point defects in the compositions LiNi1/3Co1/3Mn1/3O2 (NCM1/3) and LiNi1/3Co1/3Al1/3O2 (NCA1/3) which can also be regarded as model compounds for NCM and NCA. We will discuss defect landscapes in NCM1/3 and NCA1/3 under relevant synthesis conditions with a focus on the formation of metal antisite defects and its implications on the electrochemical properties and ultimately the design of NCM and NCA cathode materials.

  10. High Oxygen Reduction Reaction Performances of Cathode Materials Combining Polyoxometalates, Coordination Complexes, and Carboneous Supports.

    Science.gov (United States)

    Zhang, Shuangshuang; Oms, Olivier; Hao, Long; Liu, Rongji; Wang, Meng; Zhang, Yaqin; He, Hong-Yan; Dolbecq, Anne; Marrot, Jérôme; Keita, Bineta; Zhi, Linjie; Mialane, Pierre; Li, Bin; Zhang, Guangjin

    2017-11-08

    A series of carbonaceous-supported precious-metal-free polyoxometalate (POM)-based composites which can be easily synthesized on a large scale was shown to act as efficient cathode materials for the oxygen reduction reaction (ORR) in neutral or basic media via a four-electron mechanism with high durability. Moreover, exploiting the versatility of the considered system, its activity was optimized by the judicious choice of the 3d metals incorporated in the {(PW 9 ) 2 M 7 } (M = Co, Ni) POM core, the POM counterions and the support (thermalized triazine-based frameworks (TTFs), fluorine-doped TTF (TTF-F), reduced graphene oxide, or carbon Vulcan XC-72. In particular, for {(PW 9 ) 2 Ni 7 }/{Cu(ethylenediamine) 2 }/TTF-F, the overpotential required to drive the ORR compared well with those of Pt/C. This outstanding ORR electrocatalytic activity is linked with two synergistic effects due to the binary combination of the Cu and Ni centers and the strong interaction between the POM molecules and the porous and highly conducting TTF-F framework. To our knowledge, {(PW 9 ) 2 Ni 7 }/{Cu(ethylenediamine) 2 }/TTF-F represents the first example of POM-based noble-metal-free ORR electrocatalyst possessing both comparable ORR electrocatalytic activity and much higher stability than that of Pt/C in neutral medium.

  11. Cathodic Polarization Coats Titanium Based Implant Materials with Enamel Matrix Derivate (EMD

    Directory of Open Access Journals (Sweden)

    Matthias J. Frank

    2014-03-01

    Full Text Available The idea of a bioactive surface coating that enhances bone healing and bone growth is a strong focus of on-going research for bone implant materials. Enamel matrix derivate (EMD is well documented to support bone regeneration and activates growth of mesenchymal tissues. Thus, it is a prime candidate for coating of existing implant surfaces. The aim of this study was to show that cathodic polarization can be used for coating commercially available implant surfaces with an immobilized but functional and bio-available surface layer of EMD. After coating, XPS revealed EMD-related bindings on the surface while SIMS showed incorporation of EMD into the surface. The hydride layer of the original surface could be activated for coating in an integrated one-step process that did not require any pre-treatment of the surface. SEM images showed nano-spheres and nano-rods on coated surfaces that were EMD-related. Moreover, the surface roughness remained unchanged after coating, as it was shown by optical profilometry. The mass peaks observed in the matrix-assisted laser desorption/ionization time-of-flight mass spectroscopy (MALDI-TOF MS analysis confirmed the integrity of EMD after coating. Assessment of the bioavailability suggested that the modified surfaces were active for osteoblast like MC3M3-E1 cells in showing enhanced Coll-1 gene expression and ALP activity.

  12. Storage chamber for container of radiation-contaminated material

    International Nuclear Information System (INIS)

    Takakura, Masahide.

    1996-01-01

    The present invention concerns a storage chamber for containing radiation-contaminated materials in containing tubes and having cooling fluids circulated at the outer side of the containing tubes. The storage chamber comprises a gas supply means connected to the inside of the container tube for supplying a highly heat-conductive gas and a gas exhaustion means for discharging the gas present in the container tube. When containing vessels for radiation-contaminated materials are contained in the container tube, the gases present inside of the container tube is exhausted by means of the gas exhaustion means, and highly heat conductive gases are filled from the gas supply means to the space between the container tube and the containing vessels for the radiation-contaminated materials. When the temperature of the highly heat conductive gas is elevated due to the heat generation of the radiation-contaminated materials, the container tube is heated, and then cooled by the cooling fluid at the outer side of the container tube. In this case, the heat of the radiation-contaminated material-containing vessels is removed by the heat conduction by the highly heat conductive gas to reduce temperature gradient between the containing vessels and the containing tube. This can enhance the cooling effect. (T.M.)

  13. Transport and storage container for radioactive materials

    International Nuclear Information System (INIS)

    Engelstaedter, R.; Henning, E.; Storch, S.

    1987-01-01

    The container consists of a reinforced concrete wall, which is lined on the outsinde with a steel sheet and on the inside by a steel sheet several times thicker than this steel sheet. A front container opening can be closed by a reinforced concrete lid, which consists of a concrete core. This is surrounded by a lining, a covering and a lost shell. The cover projects beyond the reinforced concrete lid, so that bolts can be introduced in holes equally distributed over the extent of the cover, which can be turned in the threaded holes of threaded anchors, which are fixed on the steel sheet on the side towards the reinforced conrete wall. (orig./HP) [de

  14. Cathodic behaviour of nonstoichiometric (la,Sr){sub 1-x}(Co,Mn)O{sub 3} materials

    Energy Technology Data Exchange (ETDEWEB)

    Abrantes, J.C.C.; Rodrigues, C.M.S. [ESTG, Inst. Politecnico Viana do Castelo (Portugal); Labrincha, J.A.; Frade, J.R.; Marques, F.M.B. [Aveiro Univ. (Portugal). Dept. de Engenharia de Ceramica e do Vidro

    1996-10-01

    Solid oxide fuel cells (SOFCs) are expected to become competitive devices for electrical power generation, but successful application might be dependent on decreasing working temperatures to 800{sup o}C or lower, without detrimental effects on electrode processes and ohmic losses. This requires alternative electrode and electrolyte materials. The high electronic and oxygen ion conductivities of (La,Sr)CoO{sub 3} are promising for oxygen reduction, but high temperature reaction with yttria-stabilised zirconia (YSZ) electrolytes and excessive thermal expansion mismatch have prevented the current application of these cathode materials. Expected ways to try to minimise the reactivity of cobaltates involve A-site deficiency, and partial Mn for Co substitution. The latter is also expected to contribute to lower the thermal expansion mismatch. In this work (La,Sr){sub 1-x}(Co,Mn)O{sub 3} materials were prepared by solid state reaction and characterised by X-ray diffraction, thermal expansion and electrical conductivity measurements. The reactivity between these electrode materials and YSZ was also evaluated by XRD and SEM. Electrode layers were screen-printed on YSZ substrates and cathodic polarisation was measured at temperatures up to 1000{sup o}C. A-site substoichiometry and Co for Mn substitution affect the cathodic polarisation, but this also depends on some morphological features of screen-printed electrode layers. (author)

  15. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    International Nuclear Information System (INIS)

    Yang, Fan; Wang, Jinshu; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-01

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y 2 O 3 distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y 2 O 3 improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y 2 O 3 content in the samples. The maximum secondary emission yield δ max of the cathode with 15% amount of Y 2 O 3 can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J 0 of 4.18A/cm 2 has reached at 1050 °C b for this kind of cathode after being activated at 1200 °C b , which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work

  16. Studies on the pressed yttrium oxide-tungsten matrix as a possible dispenser cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Fan; Wang, Jinshu, E-mail: wangjsh@bjut.edu.cn; Liu, Wei; Liu, Xiang; Zhou, Meiling

    2015-01-15

    Yttrium oxide was chosen as the secondary emission substance based on calculation results through first principle theory method. A new kind of pressed yttrium oxide-tungsten matrix dispenser cathodes are prepared by a sol–gel method combined with high temperature sintering in dry hydrogen atmosphere. The results show that the growth of the grains is hampered by the pinning effect of Y{sub 2}O{sub 3} distributing uniformly between the tungsten particles, resulting in the formation of small grain size. It is found that Y{sub 2}O{sub 3} improves the secondary electron emission property, i.e., the secondary emission yield increases with the increase of Y{sub 2}O{sub 3} content in the samples. The maximum secondary emission yield δ{sub max} of the cathode with 15% amount of Y{sub 2}O{sub 3} can reach 2.92. Furthermore, the cathode shows a certain thermionic emission performance. The zero field emission current density J{sub 0} of 4.18A/cm{sup 2} has reached at 1050 °C{sub b} for this kind of cathode after being activated at 1200 °C{sub b}, which are much higher than that of rare earth oxide doped molybdenum (REO-Mo) cathode reported in the previous work. - Highlights: • Yttrium oxide was chosen as the secondary emission substance based on first principle calculation result. • A new kind of cathode has been successfully obtained. • Pressed yttrium oxide-tungsten matrix dispenser cathode exhibits good emission properties. • The improvement of the cathode emission can be well explained by the surface analysis results presented in this work.

  17. Carbon black as an alternative cathode material for electrical energy recovery and transfer in a microbial battery.

    Science.gov (United States)

    Zhang, Xueqin; Guo, Kun; Shen, Dongsheng; Feng, Huajun; Wang, Meizhen; Zhou, Yuyang; Jia, Yufeng; Liang, Yuxiang; Zhou, Mengjiao

    2017-08-01

    Rather than the conventional concept of viewing conductive carbon black (CB) to be chemically inert in microbial electrochemical cells (MECs), here we confirmed the redox activity of CB for its feasibility as an electron sink in the microbial battery (MB). Acting as the cathode of a MB, the solid-state CB electrode showed the highest electron capacity equivalent of 18.58 ± 0.46 C/g for the unsintered one and the lowest capacity of 2.29 ± 0.48 C/g for the one sintered under 100% N 2 atmosphere. The capacity vibrations of CBs were strongly in coincidence with the abundances of C=O moiety caused by different pretreatments and it implied one plausible mechanism based on CB's surface functionality for its electron capturing. Once subjected to electron saturation, CB could be completely regenerated by different strategies in terms of electrochemical discharging or donating electrons to biologically-catalyzed nitrate reduction. Surface characterization also revealed that CB's regeneration fully depended on the reversible shift of C=O moiety, further confirming the functionality-based mechanism for CB's feasibility as the role of MB's cathode. Moreover, resilience tests demonstrated that CB cathode was robust for the multi-cycles charging-discharging operations. These results imply that CB is a promising alternative material for the solid-state cathode in MBs.

  18. Marine microbial fuel cell: Use of stainless steel electrodes as anode and cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Dumas, C.; Basseguy, R.; Etcheverry, L.; Bergel, A. [Laboratoire de Genie Chimique, CNRS-INPT, Toulouse Cedex (France); Mollica, A. [CNR-ISMAR, Genoa (Italy); Feron, D. [SCCME, CEA Saclay, Gif-sur-Yvette (France)

    2007-12-01

    Numerous biocorrosion studies have stated that biofilms formed in aerobic seawater induce an efficient catalysis of the oxygen reduction on stainless steels. This property was implemented here for the first time in a marine microbial fuel cell (MFC). A prototype was designed with a stainless steel anode embedded in marine sediments coupled to a stainless steel cathode in the overlying seawater. Recording current/potential curves during the progress of the experiment confirmed that the cathode progressively acquired effective catalytic properties. The maximal power density produced of 4 mW m{sup -2} was lower than those reported previously with marine MFC using graphite electrodes. Decoupling anode and cathode showed that the cathode suffered practical problems related to implementation in the sea, which may found easy technical solutions. A laboratory fuel cell based on the same principle demonstrated that the biofilm-covered stainless steel cathode was able to supply current density up to 140 mA m{sup -2} at +0.05 V versus Ag/AgCl. The power density of 23 mW m{sup -2} was in this case limited by the anode. These first tests presented the biofilm-covered stainless steel cathodes as very promising candidates to be implemented in marine MFC. The suitability of stainless steel as anode has to be further investigated. (author)

  19. Comparative study on experiments and simulation of blended cathode active materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Appiah, Williams Agyei; Park, Joonam; Van Khue, Luu; Lee, Yunju; Choi, Jaecheol; Ryou, Myung-Hyun; Lee, Yong Min

    2016-01-01

    We simulate the electrochemical properties of Li-ion cells consisting of a blended cathode composed of LiMn 2 O 4 and LiNi 0.6 Co 0.2 Mn 0.2 O 2 and an artificial graphite anode using the Li-ion battery model available in COMSOL MULTIPHYSICS 4.4 along with a capacity fade model. The discharge profiles of the pure and blended cathodes at various current rates obtained through simulations and experimental results are well matched. By combining two capacity fade models available in literature, namely the solid electrolyte interphase (SEI) growth model and the Mn 2+ dissolution model, the cycling performance of the pure LiMn 2 O 4 cells at 25 °C are successfully simulated and found to be in a good agreement with the experimental results. The blended cathode exhibits better capacity retention than the pure LiMn 2 O 4 during cycling. We also observed that at high powers, the gravimetric energy density of the LiMn 2 O 4 cathode exceeds that of the LiNi 0.6 Co 0.2 Mn 0.2 O 2 cathode; the reverse effect is seen at low powers. Further, we were able to easily modulate the energy and power densities of the blended cathode system by changing the blend ratio in our simulation model.

  20. The impact of new cathode materials relative to baseline performance of microbial fuel cells all with the same architecture and solution chemistry

    KAUST Repository

    Yang, Wulin

    2017-04-21

    Differences in microbial fuel cell (MFC) architectures, materials, and solution chemistries, have previously hindered direct comparisons of improvements in power production due to new cathode materials. However, one common reactor design has now been used in many different laboratories around the world under similar operating conditions based on using: a graphite fiber brush anode, a platinum cathode catalyst, a single-chamber cube-shaped (4-cm) MFC with a 3-cm diameter anolyte chamber, 50 mM phosphate buffer, and an acetate fuel. Analysis of several publications over 10 years from a single laboratory showed that even under such identical operational conditions, maximum power densities varied by 15%, with an average of 1.36 ± 0.20 W m–2 (n=24), normalized to cathode projected area (34 W m–3 liquid volume). In other laboratories, maximum power was significantly less, with an average of 1.03 ± 0.46 W m–2 (n=11), despite identical conditions. One likely reason for the differences in power is cathode age. Power production with Pt catalyst cathodes significantly declined after one month of operation or more to 0.87 ± 0.31 W m–2 (n=18) based on studies where cathode aging was examined, while in many studies the age of the cathode was not reported. Using these studies as a performance baseline, we review the claims of improvements in power generation due to new anode or cathode materials, or changes in solution conductivities and substrates.

  1. Synthesis and characterization of LiFePO4/C cathode materials by sol-gel method.

    Science.gov (United States)

    Liu, Shuxin; Yin, Hengbo; Wang, Haibin; Wang, Hong

    2014-09-01

    The carbon coated LiFePO4 cathode materials (LiFePO4/C) were successfully synthesized by sol-gel method with glucose, citric acid and PEG-4000 as dispersant and carbon source, respectively. The microstructure and grain size of LiFePO4/C composite were characterized by X-ray diffraction, Raman spectroscopy, transmission electron microscopy. The results showed that the carbon source and calcination temperature had important effect on the graphitization degree of carbon; the carbon decomposed by citric acid had higher graphitization degree; with calcination temperature rising, the graphitization degree of carbon increased and the particles size increased. The graphitization degree and grain size were very important for improving the electrochemical performance of LiFePO4 cathode materials, according to the experimental results, the sample LFP-700 (LFP-C) which was synthesized with citric acid as dispersant at 700 degree C had lower polarization and larger discharge capacity.

  2. Preparation and characterization of SnO2 and Carbon Co-coated LiFePO4 cathode materials.

    Science.gov (United States)

    Wang, Haibin; Liu, Shuxin; Huang, Yongmao

    2014-04-01

    The SnO2 and carbon co-coated LiFePO4 cathode materials were successfully synthesized by solid state method. The microstructure and morphology of LiFePO4 composites were characterized by X-ray diffraction, Raman spectroscopy, scanning electron microscopy and transmission electron microscope. The results showed that the SnO2 and carbon co-coated LiFePO4 cathode materials exhibited more uniform particle size distribution. Compared with the uncoated LiFePO4/C, the structure of LiFePO4 with SnO2 and carbon coating had no change. The existence of SnO2 and carbon coating layer effectively enhanced the initial discharge capacity. Among the investigated samples, the one with DBTDL:LiFePO4 molar ratios of 7:100 exhibited the best electrochemical performance.

  3. Absorbent material for type a radioactive materials packaging containing liquids

    International Nuclear Information System (INIS)

    Saunders, G.A.

    1989-11-01

    The application of absorbent materials to the packaging and transport of liquid radioactive materials in Type A packages has not been reported in the literature. However, a significant body of research exists on absorbent materials for personal hygiene products such as diapers. Absorption capacity is dependent on both the absorbent material and the liquid being absorbed. Theoretical principles for capillary absorption in both the horizontal and the vertical plane indicate that small contact angle between the absorbent fibre and the liquid, and a small inter-fibre pore size are important. Some fluid parameters such as viscosity affect the rate of absorption but not the final absorption capacity. There appears to be little comparability between results obtained for the same absorbent and fluid using different test procedures. Test samples of materials from several classes of potential absorbents have been evaluated in this study, and shown to have a wide range of absorbent capacities. Foams, natural fibres, artificial fibres and granular materials are all potentially useful absorbents, with capacities ranging from as little as 0.86 to as much as 40.6 grams of distilled water per gram of absorbent. Two experimental procedures for evaluating the absorbent capacity of these materials have been detailed in this report, and found suitable for evaluating granular, fibrous or foam materials. Compression of the absorbent material reduces its capacity, but parameters such as relative humidity, pH, temperature, and viscosity appear to have little significant influence on capacity. When the materials were loaded to 50% of their one-minute absorbency, subsequent loss of the absorbed liquid was generally minimal. All of the absorbent materials rapidly lost their absorbed water through evaporation within twenty-four hours in still air at 21 degrees C and 50% relative humidity

  4. A versatile single molecular precursor for the synthesis of layered oxide cathode materials for Li-ion batteries.

    Science.gov (United States)

    Li, Maofan; Liu, Jiajie; Liu, Tongchao; Zhang, Mingjian; Pan, Feng

    2018-02-01

    A carbonyl-bridged single molecular precursor LiTM(acac) 3 [transition metal (TM) = cobalt/manganese/nickel (Co/Mn/Ni), acac = acetylacetone], featuring a one-dimensional chain structure, was designed and applied to achieve the layered oxide cathode materials: LiTMO 2 (TM = Ni/Mn/Co, NMC). As examples, layered oxides, primary LiCoO 2 , binary LiNi 0.8 Co 0.2 O 2 and ternary LiNi 0.5 Mn 0.3 Co 0.2 O 2 were successfully prepared to be used as cathode materials. When they are applied to lithium-ion batteries (LIBs), all exhibit good electrochemical performance because of their unique morphology and great uniformity of element distribution. This versatile precursor is predicted to accommodate many other metal cations, such as aluminum (Al 3+ ), iron (Fe 2+ ), and sodium (Na + ), because of the flexibility of organic ligand, which not only facilitates the doping-modification of the NMC system, but also enables synthesis of Na-ion layered oxides. This opens a new direction of research for the synthesis of high-performance layered oxide cathode materials for LIBs.

  5. Cathode material and pulsed plasma treatment influence on the microstructure and microhardness of high-chromium cast iron surface

    Directory of Open Access Journals (Sweden)

    Юлія Геннадіївна Чабак

    2016-11-01

    Full Text Available The article presents an analysis of the cathode material and the pulse plasma treatment mode influence on the surface microstructure and microhardness of high chrome (15% Cr cast iron. The methods of metallographic analysis and microhardness measurements were used. It has been shown that pulsed plasma treatment at 4 kV voltage with the use of the electro-axial thermal accelerator results in surface modification with high microhardness 950-1050 HV50, and in the formation of the coating due to the transfer of the electrodes material. The specific features of using different cathode materials have been systematized. It has been found that graphite electrodes are not recommended to be used due to their low strength and fracture under plasma pulses. In case of using tungsten cathode a coating of small thickness (20-30 microns and having cracks has been formed on the specimen surface. The most expedient is to apply the electrodes with low melting point (such as killed St.3, which provides a high-quality state of treated surface and formation the protective crack-free coating of 80-100 microns thick. It has been found that as a result of the plasma pulsed treatment the enrichment of coating with carbon is likely to occur that results in microhardness increase. The prospects of this technology as well as its shortcomings have been described

  6. Reaction mechanism and thermal stability study on cathode materials for rechargeable lithium ion batteries

    Science.gov (United States)

    Fang, Jin

    Olivine-type lithium iron phosphate has been a very promising cathode material since it was proposed by Padhi in 1997, low-cost, environmental friendly and stable structure ensure the commercialization of LiFePO 4. In LiFePO4, during charge and discharge process, Li ions are transferred between two phases, Li-poor LialphaFePO 4 and Li-rich Li1-betaFePO4, which implies a significant energy barrier for the new phase nucleation and interface growth, contrary to the fast reaction kinetics experimentally observed. The understanding of the lithiation and delithiation mechanism of this material has spurred a lot of research interests. Many theory models have been proposed to explain the reaction mechanism of LiFePO4, among them, the single phase model claims that the reaction goes through a metastable single phase, and the over potential required to form this single phase is about 30mV, so we studied the driving force to transport lithium ions between Lialpha FePO4 and Li1-betaFePO4 phases and compared the particle sizes effect. Experiment results shows that, the nano-sized (30nm) LiFePO4 has wider solid solution range, lower solid solution formation temperature and faster kinetics than normal LiFePO4 (150nm). Also a 20mV over potential was observed in both samples, either after relaxing the FePO4/LiFePO4 system to equilibrium or transport lithium from one side to the other side, the experiment result is corresponding to theoretical calculation; indicates the reaction might go through single-phase reaction mechanism. The energy and power density of lithium ion battery largely depend on cathode materials. Mn substituted LiFePO4 has a higher voltage than LiFePO4, which results a higher theoretical energy density. Safety issue is one of the most important criterions for batteries, since cathode materials need to maintain stable structure during hundreds of charge and discharge cycles and ranges of application conditions. We have reported that iron-rich compound o-Fe1-yMnyPO4

  7. High-Capacity Micrometer-Sized Li 2 S Particles as Cathode Materials for Advanced Rechargeable Lithium-Ion Batteries

    KAUST Repository

    Yang, Yuan

    2012-09-19

    Li 2S is a high-capacity cathode material for lithium metal-free rechargeable batteries. It has a theoretical capacity of 1166 mAh/g, which is nearly 1 order of magnitude higher than traditional metal oxides/phosphates cathodes. However, Li 2S is usually considered to be electrochemically inactive due to its high electronic resistivity and low lithium-ion diffusivity. In this paper, we discover that a large potential barrier (∼1 V) exists at the beginning of charging for Li 2S. By applying a higher voltage cutoff, this barrier can be overcome and Li 2S becomes active. Moreover, this barrier does not appear again in the following cycling. Subsequent cycling shows that the material behaves similar to common sulfur cathodes with high energy efficiency. The initial discharge capacity is greater than 800 mAh/g for even 10 μm Li 2S particles. Moreover, after 10 cycles, the capacity is stabilized around 500-550 mAh/g with a capacity decay rate of only ∼0.25% per cycle. The origin of the initial barrier is found to be the phase nucleation of polysulfides, but the amplitude of barrier is mainly due to two factors: (a) charge transfer directly between Li 2S and electrolyte without polysulfide and (b) lithium-ion diffusion in Li 2S. These results demonstrate a simple and scalable approach to utilizing Li 2S as the cathode material for rechargeable lithium-ion batteries with high specific energy. © 2012 American Chemical Society.

  8. Development of Graphene-based novel cathode material in MES system

    DEFF Research Database (Denmark)

    Chen, Leifeng; Aryal, Nabin; Ammam, Fariza

    2014-01-01

    Sporomusa ovata (S.O) typically have a negative outer-surface charge. The graphene oxide (GO) is the acceptor of the electron. If the GO accept electrons from the Sporomusa ovata and the GO can be reduced to graphene. This will lead to in situ construction of a bacteria/graphene network in the cathode......It has been reported that physical contact between unique nanostructures of electrode and bacteria isimportant for microbial electrosynthesis. The higher specific surface area of cathode can increase contact interface area with bacteria and enhance electron-exchange at the electrode surface...... and RamanSpectrum to character the GO and R-GO. The density of the Sporomusa ovate on the R-GO cathode can becharactered by the confocal laser-scanning fuorescence microscopyer. Acetate is measured via high performance liquid chromatography (HPLC). The images of R-GO/Sporomusa ovate can be characterizedand...

  9. Binder materials for the cathodes applied to self-stratifying membraneless microbial fuel cell.

    Science.gov (United States)

    Walter, Xavier Alexis; Greenman, John; Ieropoulos, Ioannis

    2018-04-19

    The recently developed self-stratifying membraneless microbial fuel cell (SSM-MFC) has been shown as a promising concept for urine treatment. The first prototypes employed cathodes made of activated carbon (AC) and polytetrafluoroethylene (PTFE) mixture. Here, we explored the possibility to substitute PTFE with either polyvinyl-alcohol (PVA) or PlastiDip (CPD; i.e. synthetic rubber) as binder for AC-based cathode in SSM-MFC. Sintered activated carbon (SAC) was also tested due to its ease of manufacturing and the fact that no stainless steel collector is needed. Results indicate that the SSM-MFC having PTFE cathodes were the most powerful measuring 1617 μW (11 W·m -3 or 101 mW·m -2 ). SSM-MFC with PVA and CPD as binders were producing on average the same level of power (1226 ± 90 μW), which was 24% less than the SSM-MFC having PTFE-based cathodes. When balancing the power by the cost and environmental impact, results clearly show that PVA was the best alternative. Power wise, the SAC cathodes were shown being the less performing (≈1070 μW). Nonetheless, the lower power of SAC was balanced by its inexpensiveness. Overall results indicate that (i) PTFE is yet the best binder to employ, and (ii) SAC and PVA-based cathodes are promising alternatives that would benefit from further improvements. Copyright © 2018 The Authors. Published by Elsevier B.V. All rights reserved.

  10. Self-closing shielded container for use with radioactive materials

    Science.gov (United States)

    Smith, J.E.

    A container for storage of radioactive material comprises a container body and a closure member. The closure member is coupled to the container body to enable the closure body to move automatically from a first position (e.g., closed) to a second position (open).

  11. Lithium-Excess Research of Cathode Material Li2MnTiO4 for Lithium-Ion Batteries

    OpenAIRE

    Zhang, Xinyi; Yang, Le; Hao, Feng; Chen, Haosen; Yang, Meng; Fang, Daining

    2015-01-01

    Lithium-excess and nano-sized Li2+xMn1−x/2TiO4 (x = 0, 0.2, 0.4) cathode materials were synthesized via a sol-gel method. The X-ray diffraction (XRD) experiments indicate that the obtained main phases of Li2.0MnTiO4 and the lithium-excess materials are monoclinic and cubic, respectively. The scanning electron microscope (SEM) images show that the as-prepared particles are well distributed and the primary particles have an average size of about 20–30 nm. The further electrochemical tests revea...

  12. Effects of titanium incorporation on phase and electrochemical performance in LiFePO4 cathode material

    International Nuclear Information System (INIS)

    Wang Zhaohui; Pang Quanquan; Deng Kejian; Yuan Lixia; Huang Fei; Peng Yunlong; Huang Yunhui

    2012-01-01

    Highlights: ► Nominal LiFe 1−x Ti x PO 4 cathode materials were synthesized via solid-state reaction. ► A clear feature of Ti-doped LiFePO 4 has been clarified. ► The formation of impurity phases strongly depends on Ti doping level. ► Appropriate amount of Ti in LiFePO 4 can enhance the electrochemical performance. - Abstract: Ti-incorporated LiFe 1−x Ti x PO 4 (0 ≤ x ≤ 0.2) samples have been prepared via a two-step solid-state reaction route. The samples have systematically been investigated with X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, scanning electron microscope (SEM), transmission electron microscope (TEM), cyclic voltammetry (CV) and charge/discharge measurements. The incorporation of Ti in LiFePO 4 significantly enhances the electrochemical performance; the carbon-coated LiFe 0.9 Ti 0.1 PO 4 sample shows the best performance. It is confirmed that LiFe 1−x Ti x PO 4 with x ≤ 0.05 are of single phase while those with 0.07 ≤ x ≤ 0.2 contain impurity phases: LiTi 2 (PO 4 ) 3 and TiP 2 O 7 . The impurities influence not only the electronic conductivity, but also the total specific capacity. Appropriate amount of titanium incorporation is favorable for the improvement in electrochemical performance.

  13. Device for separating, purifying and recovering nuclear fuel material, impurities and materials from impurity-containing nuclear fuel materials or nuclear fuel containing material

    International Nuclear Information System (INIS)

    Sato, Ryuichi; Kamei, Yoshinobu; Watanabe, Tsuneo; Tanaka, Shigeru.

    1988-01-01

    Purpose: To separate, purify and recover nuclear fuel materials, impurities and materials with no formation of liquid wastes. Constitution: Oxidizing atmosphere gases are introduced from both ends of a heating furnace. Vessels containing impurity-containing nuclear fuel substances or nuclear fuel substance-containing material are continuously disposed movably from one end to the other of the heating furnace. Then, impurity oxides or material oxides selectively evaporated from the impurity-containing nuclear fuel substances or nuclear fuel substance-containing materials are entrained in the oxidizing atmosphere gas and the gases are led out externally from a discharge port opened at the intermediate portion of the heating furnace, filters are disposed to the exit to solidify and capture the nuclear fuel substances and traps are disposed behind the filters to solidify and capture the oxides by spontaneous air cooling or water cooling. (Sekiya, K.)

  14. High insulation foam glass material from waste cathode ray tube panel glass

    DEFF Research Database (Denmark)

    König, Jakob; Petersen, Rasmus Rosenlund; Yue, Yuanzheng

    . In general CRT consists of two types of glasses: barium/strontium containing glass (panel glass) and lead containing glass (funnel and panel glass). In this work we present the possibility to produce high performance insulation material from the recycled lead-free glass. We studied the influence of foaming...... between 750 and 850°C. We investigated the influence of milling time, particle size, foaming and oxidizing agent concentrations, temperature and time on the foaming process, foam density, foam porosity and homogeneity. Only moderate foaming was observed in carbon containing samples, while the addition...... of the oxidizing agent greatly improved the foaming quality. The results showed that the amount of oxygen available from the glass is not sufficient to combust all of the added carbon, therefore, additional oxygen was supplied via manganese reduction. In general, a minimum in the foam glass density was observed...

  15. Microstructure control of SOFC cathode material: The role of dispersing agent

    Science.gov (United States)

    Ismail, Ismariza; Jani, Abdul Mutalib Md; Osman, Nafisah

    2017-09-01

    In the present works, La0.6Sr0.4Co0.2Fe0.8O3-δ (LSCF) cathode powders were synthesized by a sol-gel method with the aid of ethylene glycol which served as the dispersing agent. The phase formation and morphology of the powders were examined by X-Ray diffractometer (XRD) and field emission scanning electron microscopy (FESEM), respectively. The electrochemical properties of the synthesized cathode were obtained using an electrochemical impedance spectroscopy (EIS). The characteristic peaks for LSCF phase appears in the X-ray diffractogram after calcined at 500 °C and complete formation of LSCF single phase was attained at 700 °C. FESEM micrographs showed the presence of spherical particles of the powders with approximate particle size between 10 to 60 nm along with agglomerate morphologies. Well dispersed particles and fewer aggregates were observed for samples prepared with addition of ethylene glycol as the synthesizing aid. The surface area obtained for powder sample prepared with the aid of dispersing agent is 12.0 m2g-1. The EIS measurement results depicts a lower area specific resistance (ASR) obtained for sample prepared with addition of the ethylene glycol as compared to the pristine sample. The present results encourage the optimization of the cathode particle design in order to further improve the cathode performance.

  16. Sea urchin-like mesoporous carbon material grown with carbon nanotubes as a cathode catalyst support for fuel cells

    Energy Technology Data Exchange (ETDEWEB)

    Kuo, Ping-Lin; Hsu, Chun-Han; Li, Wan-Ting; Jhan, Jing-Yi; Chen, Wei-Fu [Department of Chemical Engineering, National Cheng Kung University, Tainan 70101 (China)

    2010-12-15

    A sea urchin-like carbon (UC) material with high surface area (416 m{sup 2} g{sup -1}), adequate electrical conductivity (59.6 S cm{sup -1}) and good chemical stability was prepared by growing carbon nanotubes onto mesoporous carbon hollow spheres. A uniform dispersion of Pt nanoparticles was then anchored on the UC, where the Pt nanoparticles were prepared using benzylamine as the stabilizer. For this Pt loaded carbon, cyclic voltammogram measurements showed an exceptionally high electrochemically active surface area (EAS) (114.8 m{sup 2} g{sup -1}) compared to the commonly used commercial E-TEK catalyst (65.2 m{sup 2} g{sup -1}). The durability test demonstrates that the carbon used as a support exhibited minor loss in EAS of Pt. Compared to the E-TEK (20 wt%) cathode catalyst, this Pt loaded UC catalyst has greatly enhanced catalytic activity toward the oxygen reduction reaction, less cathode flooding and considerably improved performance, resulting in an enhancement of ca. 37% in power density compared with that of E-TEK. Based on the results obtained, the UC is an excellent support for Pt nanoparticles used as cathode catalysts in proton exchange membrane fuel cells. (author)

  17. Complex-wide representation of material packaged in 3013 containers

    Energy Technology Data Exchange (ETDEWEB)

    Narlesky, Joshua E.; Peppers, Larry G.; Friday, Gary P.

    2009-06-01

    The DOE sites packaging plutonium oxide materials packaged according to Department of Energy 3013 Standard (DOE-STD-3013) are responsible for ensuring that the materials are represented by one or more samples in the Materials Identification and Surveillance (MIS) program. The sites categorized most of the materials into process groups, and the remaining materials were characterized, based on the prompt gamma analysis results. The sites issued documents to identify the relationships between the materials packaged in 3013 containers and representative materials in the MIS program. These “Represented” documents were then reviewed and concurred with by the MIS Working Group. However, these documents were developed uniquely at each site and were issued before completion of sample characterization, small-scale experiments, and prompt gamma analysis, which provided more detailed information about the chemical impurities and the behavior of the material in storage. Therefore, based on the most recent data, relationships between the materials packaged in 3013 containers and representative materials in the MIS program been revised. With the prompt gamma analysis completed for Hanford, Rocky Flats, and Savannah River Site 3013 containers, MIS items have been assigned to the 3013 containers for which representation is based on the prompt gamma analysis results. With the revised relationships and the prompt gamma analysis results, a Master “Represented” table has been compiled to document the linkages between each 3013 container packaged to date and its representative MIS items. This table provides an important link between the Integrated Surveillance Program database, which contains information about each 3013 container to the MIS items database, which contains the characterization, prompt gamma data, and storage behavior data from shelf-life experiments for the representative MIS items.

  18. Complex-wide representation of material packaged in 3013 containers

    International Nuclear Information System (INIS)

    Narlesky, Joshua E.; Peppers, Larry G.; Friday, Gary P.

    2009-01-01

    The DOE sites packaging plutonium oxide materials packaged according to Department of Energy 3013 Standard (DOE-STD-3013) are responsible for ensuring that the materials are represented by one or more samples in the Materials Identification and Surveillance (MIS) program. The sites categorized most of the materials into process groups, and the remaining materials were characterized, based on the prompt gamma analysis results. The sites issued documents to identify the relationships between the materials packaged in 3013 containers and representative materials in the MIS program. These 'Represented' documents were then reviewed and concurred with by the MIS Working Group. However, these documents were developed uniquely at each site and were issued before completion of sample characterization, small-scale experiments, and prompt gamma analysis, which provided more detailed information about the chemical impurities and the behavior of the material in storage. Therefore, based on the most recent data, relationships between the materials packaged in 3013 containers and representative materials in the MIS program have been revised. With the prompt gamma analysis completed for Hanford, Rocky Flats, and Savannah River Site 3013 containers, MIS items have been assigned to the 3013 containers for which representation is based on the prompt gamma analysis results. With the revised relationships and the prompt gamma analysis results, a Master 'Represented' table has been compiled to document the linkages between each 3013 container packaged to date and its representative MIS items. This table provides an important link between the Integrated Surveillance Program database, which contains information about each 3013 container to the MIS items database, which contains the characterization, prompt gamma data, and storage behavior data from shelf-life experiments for the representative MIS items

  19. CdTe/TiO{sub 2} nanocomposite material for photogenerated cathodic protection of 304 stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Xiu-tong, E-mail: xiutongwang@gmail.com [Institutes of Oceanology, Chinese Academy of Sciences, Qingdao 266071 China (China); Wei, Qin-yi, E-mail: weiqiny200@163.com [Institutes of Oceanology, Chinese Academy of Sciences, Qingdao 266071 China (China); University of Chinese Academy of Sciences, 19 (Jia) Yuquan Road, Beijing 100049 (China); Zhang, Liang, E-mail: zzll20081988@126.com [CNOOC Information Technology co., Ltd. Beijing Branch, Beijing 100029 China (China); Sun, Hao-fen, E-mail: fyqfyx@163.com [School of Environmental and Municipal Engineering Qingdao, Qingdao Technological University, Qingdao 266033 China (China); Li, Hong, E-mail: lhqdio1987@163.com [Institutes of Oceanology, Chinese Academy of Sciences, Qingdao 266071 China (China); Zhang, Qiao-xia, E-mail: qiaoxiazhang1989@163.com [Institutes of Oceanology, Chinese Academy of Sciences, Qingdao 266071 China (China)

    2016-06-15

    Graphical abstract: - Highlights: • The photoelectric properties of TiO{sub 2} could greatly improve by doping with CdTe. • The cathodic protection property of the CdTe/TiO{sub 2} was superior to that of pure TiO{sub 2}. • The protective action of the CdTe/TiO{sub 2} for 304SS could be maintained in the dark. - Abstract: TiO{sub 2} nanotubes were fabricated by the anodization method, and CdTe was deposited on them via electrochemical deposition method. The optimal performance of the CdTe/TiO{sub 2} composites was achieved via changing the acidity of the electrolyte. Scanning electron microscopy, energy dispersive spectroscopy and X-ray diffraction were used to investigate the surface morphology, elemental analysis and phase characteristics of the composite materials. Some electrochemical tests, such as open-circuit potential, current variation versus time were carried out to investigate the photogenerated cathodic protection of 304 stainless steel by CdTe/TiO{sub 2}. The results indicated that the cathodic protection performance of the CdTe/TiO{sub 2} composite was superior to that of pure TiO{sub 2} in the wavelength of visible light. The CdTe/TiO{sub 2} composite exhibited optimal photogenerated cathodic protection properties under visible light for the corrosion potential of 304 stainless steel shifted negatively to −850 mV when the concentration of HCl in the deposition electrolyte was 1 mol/L.

  20. Effect of microstructure on low temperature electrochemical properties of LiFePO4/C cathode material

    International Nuclear Information System (INIS)

    Zhao, Nannan; Zhi, Xiaoke; Wang, Li; Liu, Yanhui; Liang, Guangchuan

    2015-01-01

    Graphical abstract: The low temperature performance of Li-ion batteries and LiFePO 4 /C composites was discussed. A conclusion that cathode material is the main limitation for the low temperature performance was come up, by comparing the low temperature performance of 18650 Li-ion batteries with LiMn 2 O 4 , LiNi 1/3 Co 1/3 Mn 1/3 O 2 and LiFePO 4 /C as cathode materials. The low temperature performance results indicate the LiFePO 4 /C microstructure is the main factor influencing the low temperature performance of LiFePO 4 . A new LiFePO 4 /C with pomegranate-like spherical structure was proposed in this paper, which shows superior low temperature performance, which can be attributed to its uniform fine primary particles and smaller primary particles. - Highlights: • Low temperature performance of Li-ion battery and LiFePO 4 /C composite was discussed. • Cathode material mainly decided the low temperature performance of Li-ion battery. • LiFePO 4 /C microstructure mainly affects its low temperature performance. • Pomegranate-like spherical structure LiFePO 4 /C has good low temperature performance. - Abstract: The low-temperature electrochemical performance of Li-ion batteries is mainly determined by the choice of cathode material, as evident from a comparison of the low-temperature electrochemical performance of the 18650 batteries with the LiMn 2 O 4 , LiNi 1/3 Co 1/3 Mn 1/3 O 2 , and LiFePO 4 /C as the cathode, respectively, at −20 °C. LiFePO 4 /C materials with different morphologies and microstructures were prepared by different methods. The samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), galvanostatic charge–discharge measurements and EIS. The low-temperature performance of the samples and those of the coin cells utilizing the materials as cathodes were measured. The results indicate that the microstructure of LiFePO 4 /C is a key factor determining the low

  1. Effect of controlled potential on SCC of nuclear waste package container materials

    International Nuclear Information System (INIS)

    Lum, B. Y.; Roy, A. K.; Spragge, M. K.

    1999-01-01

    The slow-strain-rate (SSR) test technique was used to evaluate the susceptibility of Titanium (Ti) Gr-7 (UNS R52400) and Ti Gr-12 (UNS R53400) to stress corrosion cracking (SCC). Ti Gr-7 and Ti Gr-12 are two candidate container materials for the multi-barrier package for nuclear waste. The tests were done in a deaerated 90 C acidic brine (pH ∼ 2.7) containing 5 weight percent (wt%) sodium chloride (NaCl) using a strain rate of 3.3 x 10 -6 sec -1 . Before being tested in the acidic brine, specimens of each alloy were pulled inside the test chamber in the dry condition at ambient temperature. Then while in the test solution, specimens were strained under different cathodic (negative) controlled electrochemical potentials. These controlled potentials were selected based on the corrosion potential measured in the test solution before the specimens were strained. Results indicate that the times to failure (TTF) for Ti Gr-12 were much shorter than those for Ti Gr-7. Furthermore, as the applied potential became more cathodic, Ti Gr-12 showed reduced ductility in terms of percent reduction in area (%RA) and true fracture stress (σ f ). In addition, TTF and percent elongation (%El) reached the minimum values when Ti Gr-12 was tested under an impressed potential of -1162 mV. However, for Ti Gr-7, all these ductility parameters were not significantly influenced by the changes in applied potential. In general, the results of hydrogen analysis by secondary ion mass spectrometry (SIMS) showed increased hydrogen concentration at more cathodic controlled potentials. Optical microscopy and scanning electron microscopy (SEM) were used to evaluate the morphology of cracking both at the primary fracture face and the secondary cracks along the gage section of the broken tensile specimen. Transgranular secondary cracks were observed in both alloys possibly resulting from the formation of brittle titanium hydrides due to cathodic charging. The primary fracture face was characterized

  2. A study of emission property and microstructure of rare earth oxide-molybdenum cermet cathode materials made by spark plasma sintering

    International Nuclear Information System (INIS)

    Wang Jinshu; Li Hongyi; Yang Sa; Cui Ying; Zhou Meiling

    2004-01-01

    A fast sintering method, spark plasma sintering (SPS) was used for the synthesis of rare earth oxide-molybdenum cathode material. The secondary emission property, microstructure, and phase constitution of materials have been studied in this paper. The experimental results show that the maximum secondary emission coefficient of this material can be high to 3.84, much higher than that of rare earth oxide-molybdenum cathode made by traditional sintering method. The grain size is less than 1 μm and rare earth distributed evenly in the material. After the material was activated at 1600 deg. C, a 4 μm layer of rare earth oxide which leads to the high secondary emission coefficient of the material, is formed on the surface of the cathode

  3. Highly conductive cathode materials for Li-ion batteries prepared by thermal nanocrystallization of selected oxide glasses

    Energy Technology Data Exchange (ETDEWEB)

    Pietrzak, T.K.; Wasiucionek, M.; Michalski, P.P.; Kaleta, A.; Garbarczyk, J.E., E-mail: garbar@if.pw.edu.pl

    2016-11-15

    Glassy analogs of two important cathode materials for Li-ion cells: V{sub 2}O{sub 5} and phosphoolivine LiFePO{sub 4} were heat-treated in order to prepare nanocrystallized materials with high electronic conductivity of up to 7 × 10{sup −2} S cm{sup −1} and ca 7 × 10{sup −3} S cm{sup −1} at 25 °C, respectively. There is a clear correlation between the crystallization phenomena and the increase in the electrical conductivity for both groups of glasses. Electrochemical tests of heat-treated glasses of the V{sub 2}O{sub 5}–P{sub 2}O{sub 5} system, used as cathodes in lithium cells confirm their good gravimetric capacity and reversibility. Heat-treatment of glasses of the Li{sub 2}O–FeO–V{sub 2}O{sub 5}–P{sub 2}O{sub 5} system also leads to a high increase in the conductivity and to formation of nanocrystalline grains in the glassy matrix, evidenced by HR-TEM images. The temperature dependence of the conductivity of these materials follows the Arrhenius formula. The presented results indicate that the overall increase in conductivity in nanocrystallized materials is due to good charge transport properties of their interfacial regions.

  4. Synthesis of Cation and Water Free Cryptomelane Type OMS-2 Cathode Materials: The Impact of Tunnel Water on Electrochemistry

    Energy Technology Data Exchange (ETDEWEB)

    Poyraz, Altug S.; Huang, Jianping; Zhang, Bingjie; Marschilok, Amy C.; Takeuchi, Kenneth J.; Takeuchi, Esther S.

    2017-01-01

    Cryptomelane type manganese dioxides (α-MnO2, OMS-2) are interesting potential cathode materials due to the ability of their one dimensional (1D) tunnels to reversibly host various cations including Li+and an accessible stable 3+/4+ redox couple. Here, we synthesized metal cation free OMS-2 materials where the tunnels were occupied by only water and hydronium ions. Water was subsequently removed from the tunnels. Cation free OMS-2 and Dry-OMS-2 were used as cathodes in Li based batteries to investigate the role of tunnel water on their electrochemistry. The initial discharge capacity was higher for Dry-OMS-2 (252 mAh/g) compared to OMS-2 (194 mAh/g), however, after 100 cycles Dry-OMS-2 and OMS-2 delivered 137 mAh/g and 134 mAh/g, respectively. Li+ion diffusion was more facile for Dry-OMS as evidenced by rate capability, at 400 mA/g. Dry-OMS-2 delivered 135mAh/g whereas OMS-2 delivered ~115 mAh/g. This first report of the impact of tunnel water on the electrochemistry of OMS-2 type materials demonstrates that the presence of tunnel water in OMS-2 type materials negatively impacts the electrochemistry.

  5. Construction of tubular polypyrrole-wrapped biomass-derived carbon nanospheres as cathode materials for lithium–sulfur batteries

    International Nuclear Information System (INIS)

    Yu, Qiuhong; Lu, Yang; Peng, Tao; Hou, Xiaoyi; Luo, Rongjie; Wang, Yange; Yan, Hailong; Luo, Yongsong; Liu, Xianming; Kim, Jang-Kyo

    2017-01-01

    A promising hybrid material composed of tubular polypyrrole (T-PPy)-wrapped monodisperse biomass-derived carbon nanospheres (BCSs) was first synthesized successfully via a simple hydrothermal approach by using watermelon juice as the carbon source, and further used as an anchoring object for sulfur (S) of lithium–sulfur (Li–S) batteries. The use of BCSs with hydrophilic nature as a framework could provide large interface areas between the active materials and electrolyte, and improve the dispersion of T-PPy, which could help in the active material utilization. As a result, BCS@T-PPy/S as a cathode material exhibited a high capacity of 1143.6 mA h g −1 and delivered a stable capacity up to 685.8 mA h g −1 after 500 cycles at 0.5 C, demonstrating its promising application for rechargeable Li–S batteries. (paper)

  6. Solvothermal synthesis and electrochemical performance of Li2MnSiO4/C cathode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Wang, Yan-Chao; Zhao, Shi-Xi; Zhai, Peng-Yuan; Li, Fang; Nan, Ce-Wen

    2014-01-01

    Highlights: • Li 2 MnSiO 4 /C nanocomposite has been synthesized by the solvothermal method. • The particles of Li 2 MnSiO 4 /C are much smaller and more uniform. • The presence of Ni improves discharge capacity of Li 2 MnSiO 4 /C cathode material. • The initial discharge capacity of Ni-modified Li 2 MnSiO 4 /C is 274.5 mAh g −1 at 25 °C. - Abstract: Orthorhombic structure Li 2 MnSiO 4 /C with Pmn2 1 space group is synthesized by the solvothermal method. Carbon coating and Ni 2+ doping are used to improve the electronic conductivity and the cycling performance of Li 2 MnSiO 4 cathode material, respectively. The particles of Li 2 MnSiO 4 /C are much smaller and more uniform than those of Li 2 MnSiO 4 due to the carbon coating. It is shown that Ni 2+ has been reduced into metal Ni during the synthesis process. The synthesized Ni-modified Li 2 MnSiO 4 /C (denoted as (LMS@Ni)/C) cathode material exhibits better electrochemical performance in comparison with Li 2 MnSiO 4 /C, attributing to higher lithium ion diffusion coefficient as well as electronic conductivity. The initial discharge capacity of (LMS@Ni)/C is 274.5 mA h g −1 and the reversible capacity after 20 cycles is 119.8 mA h g −1 at 25 °C

  7. Candidate container materials for Yucca Mountain waste package designs

    International Nuclear Information System (INIS)

    McCright, R.D.; Halsey, W.G.; Gdowski, G.E.; Clarke, W.L.

    1991-09-01

    Materials considered as candidates for fabricating nuclear waste containers are reviewed in the context of the Conceptual Design phase of a potential repository located at Yucca Mountain. A selection criteria has been written for evaluation of candidate materials for the next phase -- Advanced Conceptual Design. The selection criteria is based on the conceptual design of a thin-walled container fabricated from a single metal or alloy; the criteria consider the performance requirements on the container and the service environment in which the containers will be emplaced. A long list of candidate materials is evaluated against the criteria, and a short list of materials is proposed for advanced characterization in the next design phase

  8. Characterization of plutonium-containing materials and storage canisters

    International Nuclear Information System (INIS)

    Mason, R.E.

    1997-01-01

    Throughout the weapons complex, plutonium materials are stored in various containers. Some plutonium has been stored for 20 yr or more. The physical and chemical properties of the plutonium material and the containers that hold it are often not well characterized. The U.S. Department of Energy (DOE) 3013 standard sets criteria to which stored material must conform. The 3013 standard regulates materials that hold 50% or greater plutonium, and the other 50% is not specified and is usually unknown. The Materials Identification and Surveillance project is tasked to characterize representative materials and begin to characterize the other 50% and to show that materials can be brought into 3013 criteria conformance through thermal treatments

  9. Polymorphs of LiFeSO4F as cathode materials for lithium ion batteries - a first principle computational study.

    Science.gov (United States)

    Chung, Sai Cheong; Barpanda, Prabeer; Nishimura, Shin-Ichi; Yamada, Yuki; Yamada, Atsuo

    2012-06-28

    We have investigated polymorphs of LiFeSO4F, tavorite and triplite, which have been reported as cathode materials for lithium ion batteries. The predicted voltages are 3.64 and 3.90 V for tavorite and triplite, respectively, which agreed excellently with experimental data. It is found that the lithiated states (LiFeSO4F) of the polymorphs are almost degenerate in energy. The difference in voltage is mainly due to the difference in the stabilities of the delithiated states (FeSO4F). This is rationalized by the Fe(3+)-Fe(3+) repulsion in the edge sharing geometry of the triplite structure.

  10. Studies on bare and Mg-doped LiCoO2 as a cathode material for lithium ion batteries

    CSIR Research Space (South Africa)

    Reddy, MV

    2014-05-01

    Full Text Available at ScienceDirect Electrochimica Acta jo ur nal ho me p age: www.elsev ier .com/ locate /e lec tac ta Graphical Abstract Electrochimica Acta xxx (2013) xxx–xxx Studies on Bare and Mg-doped LiCoO2 as a cathode material for Lithium ion Batteries M.V. Reddy... for Lithium ion Batteries M.V. Reddy∗, Thor Wei Jie, Charl J. Jafta, Kenneth I. Ozoemena, Mkhulu K. Mathe, A. Sree Kumaran Nair, Soo Soon Peng, M. Sobri Idris, Geetha Balakrishna, Fabian I. Ezema, B.V.R. Chowdari • Layered compounds, Li...

  11. NMR study on the Li diffusion in a cathode material of amorphous vanadium pentoxide-5 mol% phosphorus pentoxide

    International Nuclear Information System (INIS)

    Asai, T.; Sugimoto, S.; Kawai, S.

    1989-01-01

    Diffusion properties of Li ion in a cathode material of amorphous Li chi V 2 O 5 with 5 mol% P 2 O 5 (chi=0.2-2) studied by means of Li NMR. From the relaxation time, the diffusion coefficient at 25 0 C is obtained. From the second moment, Li + ions seemed to occupy sites approximately 2.9 A apart in a large cavity similar to that in the crystalline V 2 O 5 . It is suggested that there are three kinds of sites for the Li + ion in the cavity, and that the ion changes the site of one kind to the others at chi≅0.6

  12. Synthesis of Nanoscale Lithium-Ion Battery Cathode Materials Using a Porous Polymer Precursor Method

    KAUST Repository

    Deshazer, H.D.

    2011-01-01

    Fine particles of metal oxides with carefully controlled compositions can be easily prepared by the thermal decomposition of porous polymers, such as cellulose, into which solutions containing salts of the desired cations have been dissolved. This is a simple and versatile method that can be used to produce a wide variety of materials with a range of particle sizes and carefully controlled chemical compositions. Examples of the use of this method to produce fine particles of LiCoO2 and Li(NiMnCo)1/3O2, which are used in the positive electrodes of lithium-ion batteries, are shown. Experiments have demonstrated that materials made using this method can have electrochemical properties comparable to those typically produced by more elaborate procedures. © 2011 The Electrochemical Society.

  13. Properties of Copper Doped Neodymium Nickelate Oxide as Cathode Material for Solid Oxide Fuel Cells

    Directory of Open Access Journals (Sweden)

    Lee Kyoung-Jin

    2016-06-01

    Full Text Available Mixed ionic and electronic conducting K2NiF4-type oxide, Nd2Ni1-xCuxO4+δ (x=0~1 powders were synthesized by solid state reaction technique and solid oxide fuel cells consisting of a Nd2Ni1-xCuxO4+δ cathode, a Ni-YSZ anode and ScSZ as an electrolyte were fabricated. The effect of copper substitution for nickel on the electrical and electrochemical properties was examined. Small amount of copper doping (x=0.2 resulted in the increased electrical conductivity and decreased polarization resistance. It appears that this phenomenon was associated with the high mean valence of nickel and copper and the resulting excess oxygen (δ. It was found that power densities of the cell with the Nd2Ni1-xCuxO4+δ (x=0.1 and 0.2 cathode were higher than that of the cell with the Nd2NiO4+δ cathode.

  14. Strategies toward High-Performance Cathode Materials for Lithium-Oxygen Batteries.

    Science.gov (United States)

    Wang, Kai-Xue; Zhu, Qian-Cheng; Chen, Jie-Sheng

    2018-05-11

    Rechargeable aprotic lithium (Li)-O 2 batteries with high theoretical energy densities are regarded as promising next-generation energy storage devices and have attracted considerable interest recently. However, these batteries still suffer from many critical issues, such as low capacity, poor cycle life, and low round-trip efficiency, rendering the practical application of these batteries rather sluggish. Cathode catalysts with high oxygen reduction reaction (ORR) and evolution reaction activities are of particular importance for addressing these issues and consequently promoting the application of Li-O 2 batteries. Thus, the rational design and preparation of the catalysts with high ORR activity, good electronic conductivity, and decent chemical/electrochemical stability are still challenging. In this Review, the strategies are outlined including the rational selection of catalytic species, the introduction of a 3D porous structure, the formation of functional composites, and the heteroatom doping which succeeded in the design of high-performance cathode catalysts for stable Li-O 2 batteries. Perspectives on enhancing the overall electrochemical performance of Li-O 2 batteries based on the optimization of the properties and reliability of each part of the battery are also made. This Review sheds some new light on the design of highly active cathode catalysts and the development of high-performance lithium-O 2 batteries. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  15. LiCaFeF6: A zero-strain cathode material for use in Li-ion batteries

    Science.gov (United States)

    de Biasi, Lea; Lieser, Georg; Dräger, Christoph; Indris, Sylvio; Rana, Jatinkumar; Schumacher, Gerhard; Mönig, Reiner; Ehrenberg, Helmut; Binder, Joachim R.; Geßwein, Holger

    2017-09-01

    A new zero-strain LiCaFeF6 cathode material for reversible insertion and extraction of lithium ions is presented. LiCaFeF6 is synthesized by a solid-state reaction and processed to a conductive electrode composite via high-energy ball-milling. In the first cycle, a discharge capacity of 112 mAh g-1 is achieved in the voltage range from 2.0 V to 4.5 V. The electrochemically active redox couple is Fe3+/Fe2+ as confirmed by Mössbauer spectroscopy and X-ray absorption spectroscopy. The compound has a trigonal colquiriite-type crystal structure (space group P 3 bar 1 c). By means of in situ and ex situ XRD as well as X-ray absorption fine structure spectroscopy a reversible response to Li uptake/release is found. For an uptake of 0.8 mol Li per formula unit only minimal changes occur in the lattice parameters causing a total change in unit cell volume of less than 0.5%. The spatial distribution of cations in the crystal structure as well as the linkage between their corresponding fluorine octahedra is responsible for this very small structural response. With its zero-strain behaviour this material is expected to exhibit only negligible mechanical degradation. It may be used as a cathode material in future lithium-ion batteries with strongly improved safety and cycle life.

  16. 19 CFR 10.461 - Retail packaging materials and containers.

    Science.gov (United States)

    2010-04-01

    ... Free Trade Agreement Rules of Origin § 10.461 Retail packaging materials and containers. Packaging... classification set out in General Note 26(n), HTSUS. If the good is subject to a regional value content... non-originating materials, as the case may be, in calculating the regional value content of the good...

  17. Naphthalene Diimide Based n-Type Conjugated Polymers as Efficient Cathode Interfacial Materials for Polymer and Perovskite Solar Cells.

    Science.gov (United States)

    Jia, Tao; Sun, Chen; Xu, Rongguo; Chen, Zhiming; Yin, Qingwu; Jin, Yaocheng; Yip, Hin-Lap; Huang, Fei; Cao, Yong

    2017-10-18

    A series of naphthalene diimide (NDI) based n-type conjugated polymers with amino-functionalized side groups and backbones were synthesized and used as cathode interlayers (CILs) in polymer and perovskite solar cells. Because of controllable amine side groups, all the resulting polymers exhibited distinct electronic properties such as oxidation potential of side chains, charge carrier mobilities, self-doping behaviors, and interfacial dipoles. The influences of the chemical variation of amine groups on the cathode interfacial effects were further investigated in both polymer and perovskite solar cells. We found that the decreased electron-donating property and enhanced steric hindrance of amine side groups substantially weaken the capacities of altering the work function of the cathode and trap passivation of the perovskite film, which induced ineffective interfacial modifications and declining device performance. Moreover, with further improvement of the backbone design through the incorporation of a rigid acetylene spacer, the resulting polymers substantially exhibited an enhanced electron-transporting property. Upon use as CILs, high power conversion efficiencies (PCEs) of 10.1% and 15.2% were, respectively, achieved in polymer and perovskite solar cells. Importantly, these newly developed n-type polymers were allowed to be processed over a broad thickness range of CILs in photovoltaic devices, and a prominent PCE of over 8% for polymer solar cells and 13.5% for perovskite solar cells can be achieved with the thick interlayers over 100 nm, which is beneficial for roll-to-roll coating processes. Our findings contribute toward a better understanding of the structure-performance relationship between CIL material design and solar cell performance, and provide important insights and guidelines for the design of high-performance n-type CIL materials for organic and perovskite optoelectronic devices.

  18. Preparation and enhanced electrochemical properties of nano-sulfur/poly(pyrrole-co-aniline) cathode material for lithium/sulfur batteries

    International Nuclear Information System (INIS)

    Qiu Linlin; Zhang Shichao; Zhang Lan; Sun, Mingming; Wang Weikun

    2010-01-01

    Poly(pyrrole-co-aniline) (PPyA) copolymer nanofibers were prepared by chemical oxidation method with cetyltrimethyl ammonium chloride (CTAC) as template, and the nano-sulfur/poly(pyrrole-co-aniline) (S/PPyA) composite material in lithium batteries was achieved via co-heating the mixture of PPyA and sublimed sulfur at 160 deg. C for 24 h. The component and structure of the materials were characterized by FTIR, Raman, XRD, and SEM. PPyA with nanofiber network structure was employed as a conductive matrix, adsorbing agent and firm reaction chamber for the sulfur cathode materials. The nano-dispersed composite exhibited a specific capacity up to 1285 mAh g -1 in the initial cycle and remained 866 mAh g -1 after 40 cycles.

  19. Test plan for buried waste containment system materials

    International Nuclear Information System (INIS)

    Weidner, J.; Shaw, P.

    1997-03-01

    The objectives of the FY 1997 barrier material work at the Idaho National Engineering and Environmental Laboratory are to (1) select a waste barrier material and verify that it is compatible with the Buried Waste Containment System Process, and (2) determine if, and how, the Buried Waste Containment System emplacement process affects the material properties and performance (on proof of principle scale). This test plan describes a set of measurements and procedures used to validate a waste barrier material for the Buried Waste Containment System. A latex modified proprietary cement manufactured by CTS Cement Manufacturing Company will be tested. Emplacement properties required for the Buried Waste Containment System process are: slump between 8 and 10 in., set time between 15 and 30 minutes, compressive strength at set of 20 psi minimum, and set temperature less than 100 degrees C. Durability properties include resistance to degradation from carbonate, sulfate, and waste-site soil leachates. A set of baseline barrier material properties will be determined to provide a data base for comparison with the barrier materials when tested in the field. The measurements include permeability, petrographic analysis to determine separation and/or segregation of mix components, and a set of mechanical properties. The measurements will be repeated on specimens from the field test material. The data will be used to determine if the Buried Waste Containment System equipment changes the material. The emplacement properties will be determined using standard laboratory procedures and instruments. Durability of the barrier material will be evaluated by determining the effect of carbonate, sulfate, and waste-site soil leachates on the compressive strength of the barrier material. The baseline properties will be determined using standard ASTM procedures. 9 refs., 1 fig., 2 tabs

  20. Process for recycling mixed-cathode materials from spent lithium-ion batteries and kinetics of leaching.

    Science.gov (United States)

    Li, Li; Bian, Yifan; Zhang, Xiaoxiao; Guan, Yibiao; Fan, Ersha; Wu, Feng; Chen, Renjie

    2018-01-01

    A "grave-to-cradle" process for the recycling of spent mixed-cathode materials (LiCoO 2 , LiCo 1/3 Ni 1/3 Mn 1/3 O 2 , and LiMn 2 O 4 ) has been proposed. The process comprises an acid leaching followed by the resynthesis of a cathode material from the resulting leachate. Spent cathode materials were leached in citric acid (C 6 H 8 O 7 ) and hydrogen peroxide (H 2 O 2 ). Optimal leaching conditions were obtained at a leaching temperature of 90 °C, a H 2 O 2 concentration of 1.5 vol%, a leaching time of 60 min, a pulp density of 20 g L -1 , and a citric acid concentration of 0.5 M. The leaching efficiencies of Li, Co, Ni, and Mn exceeded 95%. The leachate was used to resynthesize new LiCo 1/3 Ni 1/3 Mn 1/3 O 2 material by using a sol-gel method. A comparison of the electrochemical properties of the resynthesized material (NCM-spent) with that synthesized directly from original chemicals (NCM-syn) indicated that the initial discharge capacity of NCM-spent at 0.2 C was 152.8 mA h g -1 , which was higher than the 149.8 mA h g -1 of NCM-syn. After 160 cycles, the discharge capacities of the NCM-spent and NCM-syn were 140.7 mA h g -1 and 121.2 mA h g -1 , respectively. After discharge at 1 C for 300 cycles, the NCM-spent material remained a higher capacity of 113.2 mA h g -1 than the NCM-syn (78.4 mA h g -1 ). The better performance of the NCM-spent resulted from trace Al doping. A new formulation based on the shrinking-core model was proposed to explain the kinetics of the leaching process. The activation energies of the Li, Co, Ni, and Mn leaching were calculated to be 66.86, 86.57, 49.46, and 45.23 kJ mol -1 , respectively, which indicates that the leaching was a chemical reaction-controlled process. Copyright © 2017 Elsevier Ltd. All rights reserved.

  1. 49 CFR 176.76 - Transport vehicles, freight containers, and portable tanks containing hazardous materials.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 2 2010-10-01 2010-10-01 false Transport vehicles, freight containers, and... TRANSPORTATION HAZARDOUS MATERIALS REGULATIONS CARRIAGE BY VESSEL General Handling and Stowage § 176.76 Transport... paragraphs (b) through (f) of this section, hazardous materials authorized to be transported by vessel may be...

  2. Simple synthesis of amorphous NiWO4 nanostructure and its application as a novel cathode material for asymmetric supercapacitors.

    Science.gov (United States)

    Niu, Lengyuan; Li, Zhangpeng; Xu, Ye; Sun, Jinfeng; Hong, Wei; Liu, Xiaohong; Wang, Jinqing; Yang, Shengrong

    2013-08-28

    This study reports a simple synthesis of amorphous nickel tungstate (NiWO4) nanostructure and its application as a novel cathode material for supercapacitors. The effect of reaction temperature on the electrochemical properties of the NiWO4 electrode was studied, and results demonstrate that the material synthesized at 70 °C (NiW-70) has shown the highest specific capacitance of 586.2 F g(-1) at 0.5 A g(-1) in a three-electrode system. To achieve a high energy density, a NiW-70//activated carbon asymmetric supercapacitor is successfully assembled by use of NiW-70 and activated carbon as the cathode and anode, respectively, and then, its electrochemical performance is characterized by cyclic voltammetry and galvanostatic charge-discharge measurements. The results show that the assembled asymmetric supercapacitor can be cycled reversibly between 0 and 1.6 V with a high specific capacitance of 71.1 F g(-1) at 0.25 A g(-1), which can deliver a maximum energy density of 25.3 Wh kg(-1) at a power density of 200 W kg(-1). Furthermore, this asymmetric supercapacitor also presented an excellent, long cycle life along with 91.4% specific capacitance being retained after 5000 consecutive times of cycling.

  3. Advanced cathode materials for polymer electrolyte fuel cells based on pt/ metal oxides: from model electrodes to catalyst systems.

    Science.gov (United States)

    Fabbri, Emiliana; Pătru, Alexandra; Rabis, Annett; Kötz, Rüdiger; Schmidt, Thomas J

    2014-01-01

    The development of stable catalyst systems for application at the cathode side of polymer electrolyte fuel cells (PEFCs) requires the substitution of the state-of-the-art carbon supports with materials showing high corrosion resistance in a strongly oxidizing environment. Metal oxides in their highest oxidation state can represent viable support materials for the next generation PEFC cathodes. In the present work a multilevel approach has been adopted to investigate the kinetics and the activity of Pt nanoparticles supported on SnO2-based metal oxides. Particularly, model electrodes made of SnO2 thin films supporting Pt nanoparticles, and porous catalyst systems made of Pt nanoparticles supported on Sb-doped SnO2 high surface area powders have been investigated. The present results indicate that SnO2-based supports do not modify the oxygen reduction reaction mechanism on the Pt nanoparticle surface, but rather lead to catalysts with enhanced specific activity compared to Pt/carbon systems. Different reasons for the enhancement in the specific activity are considered and discussed.

  4. Understanding local degradation of cycled Ni-rich cathode materials at high operating temperature for Li-ion batteries

    International Nuclear Information System (INIS)

    Hwang, Sooyeon; Kim, Dong Hyun; Chung, Kyung Yoon; Chang, Wonyoung

    2014-01-01

    We utilize transmission electron microscopy in conjunction with electron energy loss spectroscopy to investigate local degradation that occurs in Li x Ni 0.8 Co 0.15 Al 0.05 O 2 cathode materials (NCA) after 30 cycles with cutoff voltages of 4.3 V and 4.8 V at 55 °C. NCA has a homogeneous crystallographic structure before electrochemical reactions; however, we observed that 30 cycles of charge/discharge reactions induced inhomogeneity in the crystallographic and electronic structures and also introduced porosity particularly at surface area. These changes were more noticeable in samples cycled with higher cutoff voltage of 4.8 V. Effect of operating temperature was further examined by comparing electronic structures of oxygen of the NCA particles cycled at both room temperature and 55 °C. The working temperature has a greater impact on the NCA cathode materials at a cutoff voltage of 4.3 V that is the practical the upper limit voltage in most applications, while a cutoff voltage of 4.8 V is high enough to cause surface degradation even at room temperature.

  5. Understanding local degradation of cycled Ni-rich cathode materials at high operating temperature for Li-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Hwang, Sooyeon; Kim, Dong Hyun; Chung, Kyung Yoon; Chang, Wonyoung, E-mail: cwy@kist.re.kr [Center for Energy Convergence, Korea Institute of Science and Technology, Seoul 136-791 (Korea, Republic of)

    2014-09-08

    We utilize transmission electron microscopy in conjunction with electron energy loss spectroscopy to investigate local degradation that occurs in Li{sub x}Ni{sub 0.8}Co{sub 0.15}Al{sub 0.05}O{sub 2} cathode materials (NCA) after 30 cycles with cutoff voltages of 4.3 V and 4.8 V at 55 °C. NCA has a homogeneous crystallographic structure before electrochemical reactions; however, we observed that 30 cycles of charge/discharge reactions induced inhomogeneity in the crystallographic and electronic structures and also introduced porosity particularly at surface area. These changes were more noticeable in samples cycled with higher cutoff voltage of 4.8 V. Effect of operating temperature was further examined by comparing electronic structures of oxygen of the NCA particles cycled at both room temperature and 55 °C. The working temperature has a greater impact on the NCA cathode materials at a cutoff voltage of 4.3 V that is the practical the upper limit voltage in most applications, while a cutoff voltage of 4.8 V is high enough to cause surface degradation even at room temperature.

  6. Understanding local degradation of cycled Ni-rich cathode materials at high operating temperature for Li-ion batteries

    Science.gov (United States)

    Hwang, Sooyeon; Kim, Dong Hyun; Chung, Kyung Yoon; Chang, Wonyoung

    2014-09-01

    We utilize transmission electron microscopy in conjunction with electron energy loss spectroscopy to investigate local degradation that occurs in LixNi0.8Co0.15Al0.05O2 cathode materials (NCA) after 30 cycles with cutoff voltages of 4.3 V and 4.8 V at 55 °C. NCA has a homogeneous crystallographic structure before electrochemical reactions; however, we observed that 30 cycles of charge/discharge reactions induced inhomogeneity in the crystallographic and electronic structures and also introduced porosity particularly at surface area. These changes were more noticeable in samples cycled with higher cutoff voltage of 4.8 V. Effect of operating temperature was further examined by comparing electronic structures of oxygen of the NCA particles cycled at both room temperature and 55 °C. The working temperature has a greater impact on the NCA cathode materials at a cutoff voltage of 4.3 V that is the practical the upper limit voltage in most applications, while a cutoff voltage of 4.8 V is high enough to cause surface degradation even at room temperature.

  7. Mesoporous LiMnPO4/C nanoparticles as high performance cathode material for lithium ion batteries

    International Nuclear Information System (INIS)

    Wen, Fang; Shu, Hongbo; Zhang, Yuanyuan; Wan, Jiajia; Huang, Weihua; Yang, Xiukang; Yu, Ruizhi; Liu, Li; Wang, Xianyou

    2016-01-01

    LiMnPO 4 has been considered as one of the most promising high voltage cathode materials for next-generation lithium ion batteries. However, LiMnPO 4 suffers from intrinsic drawbacks of extremely low electronic conductivity and ionic diffusivity between LiMnPO 4 /MnPO 4 . In this paper, mesoporous LiMnPO 4 nanoparticles are synthesized successfully via a facile glycine-assisted solvothermal rout. The as-prepared mesoporous LiMnPO 4 /C nanoparticles present well-defined abundant mesoporous structure (diameter of 3 ∼ 10 nm), uniform carbon layer (thickness of 3 ∼ 4 nm), high specific surface area (90.1 m 2 /g). As a result, the mesoporous LiMnPO 4 /C nanoparticles achieve excellent electrochemical performance as cathode materials for lithium ion batteries. It demonstrates a high discharge capacity of 167.7, 161.6, 156.4, 148.4 and 128.7 mAh/g at 0.1, 0.5, 1, 2 and 5C, and maintains a discharge capacity of 130.0 mAh/g after 100 cycles at 1C. The good electrochemical performance is attributed to its special interpenetrating mesoporous structure in LiMnPO 4 nanoparticles, which significantly enhances the ionic and electronic transport and additional capacitive behavior to compensate the sluggish kinetics.

  8. Enhancement of discharge performance of Li/CF x cell by thermal treatment of CF x cathode material

    Science.gov (United States)

    Zhang, Sheng S.; Foster, Donald; Read, Jeffrey

    In this work we demonstrate that the thermal treatment of CF x cathode material just below the decomposition temperature can enhance discharge performance of Li/CF x cells. The performance enhancement becomes more effective when heating a mixture of CF x and citric acid (CA) since CA serves as an extra carbon source. Discharge experiments show that the thermal treatment not only reduces initial voltage delay, but also raises discharge voltage. Whereas the measurement of powder impedance indicates the thermal treatment does not increase electronic conductivity of CF x material. Based on these facts, we propose that the thermal treatment results in a limited decomposition of CF x, which yields a subfluorinated carbon (CF x- δ), instead of a highly conductive carbon. In the case of CF x/AC mixture, the AC provides extra carbon that reacts with F 2 and fluorocarbon radicals generated by the thermal decomposition of CF x to form subfluorinated carbon. The process of thermal treatment is studied by thermogravimetric analysis and X-ray diffraction, and the effect of treatment conditions such as heating temperature, heating time and CF x/CA ratio on the discharge performance of CF x cathode is discussed. As an example, a Li/CF x cell using CF x treated with CA at 500 °C under nitrogen for 2 h achieved theretical specific capacity when being discharged at C/5. Impedance analysis indicates that the enhanced performance is attributed to a significant reduction in the cell reaction resistance.

  9. Super high energy density of Li3V2(PO4)3 as cathode materials for lithium ion batteries

    Science.gov (United States)

    Noerochim, Lukman; Amin, Mochammad Karim Al; Susanti, Diah; Triwibowo, Joko

    2018-04-01

    Lithium ion batteries have many advantages such as high energy density, no memory effect, long time cycleability and friendly environment. One type of cathode material that can be developed is Li3V2(PO4)3. In this study has been carried out the synthesis of Li3V2(PO4)3 with a hydrothermal temperature variation of 140, 160 and 180 °C and calcination temperature at 800 °C. SEM images show that the morphology of Li3V2(PO4)3 has irregular flakes with a size between 1-10 µm. CV results show redox reaction occurs in the range between 3 V to 4.8 V with the highest specific discharge capacity of 136 mAh/g for specimen with temperature hydrothermal and calcination are 180 °C and 800 °C. This result demonstrates that Li3V2(PO4)3 has a great potential as cathode material for lithium ion battery.

  10. The preparation and electrochemical performances of LiFePO4-multiwalled nanotubes composite cathode materials for lithium ion batteries

    International Nuclear Information System (INIS)

    Feng Yan

    2010-01-01

    LiFePO 4 -MWCNTs (multi-walled carbon nanotubes) composite cathode materials were prepared by mixing LiFePO 4 and MWCNTs in ethanol followed by heat-treatment at 500 deg. C for 5 h. The structural, morphology and electrochemical performances of LiFePO 4 -MWCNTs composite materials were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), galvanostatic charge-discharge cycle tests, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). The results indicated that MWCNTs adding improved the electronic conductivity, the discharge capacity, cycle stability and lithium ion diffusion kinetics of LiFePO 4 , but MWCNTs adding did not charge the orthorhombic olivine-type structure of LiFePO 4 . In all these prepared LiFePO 4 with x wt.% MWCNTs (x = 4, 7, 10) composites, 7 wt.% MWCNTs adding composite cathode shows the best electrochemical performance, which gets an initial discharge capacity of 152.7 mAh g -1 at 0.18 C discharge rates with capacity retention ratio of 97.77% after 100 cycles.

  11. Atomic-scale understanding of non-stoichiometry effects on the electrochemical performance of Ni-rich cathode materials

    Science.gov (United States)

    Kong, Fantai; Liang, Chaoping; Longo, Roberto C.; Zheng, Yongping; Cho, Kyeongjae

    2018-02-01

    As the next-generation high energy capacity cathode materials for Li-ion batteries, Ni-rich oxides face the problem of obtaining near-stoichiometric phases due to excessive Ni occupying Li sites. These extra-Ni-defects drastically affect the electrochemical performance. Despite of its importance, the fundamental correlation between such defects and the key electrochemical properties is still poorly understood. In this work, using density-functional-theory, we report a comprehensive study on the effects of non-stoichiometric phases on properties of Ni-rich layered oxides. For instance, extra-Ni-defects trigger charge disproportionation reaction within the system, alleviating the Jahn-Teller distortion of Ni3+ ions, which constitutes an important reason for their low formation energies. Kinetic studies of these defects reveal their immobile nature, creating a "pillar effect" that increases the structural stability. Ab initio molecular dynamics revealed Li depletion regions surrounding extra-Ni-defects, which are ultimate responsible for the arduous Li diffusion and re-intercalation, resulting in poor rate performance and initial capacity loss. Finally, the method with combination of high valence cation doping and ion-exchange synthesis is regarded as the most promising way to obtain stoichiometric oxides. Overall, this work not only deepens our understanding of non-stoichiometric Ni-rich layered oxides, but also enables further optimizations of high energy density cathode materials.

  12. The influence of reduced graphene oxide on electrical conductivity of LiFePO4-based composite as cathode material

    International Nuclear Information System (INIS)

    Arifin, Muhammad; Aimon, Akfiny Hasdi; Winata, Toto; Abdullah, Mikrajuddin; Iskandar, Ferry

    2016-01-01

    LiFePO 4 is fascinating cathode active materials for Li-ion batteries application because of their high electrochemical performance such as a stable voltage at 3.45 V and high specific capacity at 170 mAh.g −1 . However, their low intrinsic electronic conductivity and low ionic diffusion are still the hindrance for their further application on Li-ion batteries. Therefore, the efforts to improve their conductivity are very important to elevate their prospecting application as cathode materials. Herein, we reported preparation of additional of reduced Graphene Oxide (rGO) into LiFePO 4 -based composite via hydrothermal method and the influence of rGO on electrical conductivity of LiFePO 4 −based composite by varying mass of rGO in composition. Vibration of LiFePO 4 -based composite was detected on Fourier Transform Infrared Spectroscopy (FTIR) spectra, while single phase of LiFePO 4 nanocrystal was observed on X-Ray Diffraction (XRD) pattern, it furthermore, Scanning Electron Microscopy (SEM) images showed that rGO was distributed around LiFePO4-based composite. Finally, the 4-point probe measurement result confirmed that the optimum electrical conductivity is in additional 2 wt% rGO for range 1 to 2 wt% rGO

  13. Effect of Decreasing Cobalt Content on the Electrochemical Properties and Structural Stability of Li_(1-x)Ni_(y)Co_(z)Al_(0.05)O_(2) Type Cathode Materials

    OpenAIRE

    Ghatak, Kamalika; Kumar, Hemant; Nadimpalli, Siva; Datta, Dibakar

    2017-01-01

    In Lithium ion batteries (LIBs), proper design of cathode materials influences its intercalation behavior, overall cost, structural stability, and its impact on environment. At present, the most common type of cathode materials, NCA , has very high cobalt concentration. Since cobalt is toxic and expensive, the existing design of cathode materials is not cost-effective, and environmentally benign. However, these immensely important issues have not yet been properly addressed. Therefore, we hav...

  14. Ti substrate coated with composite Cr–MoO2 coatings as highly selective cathode materials in hypochlorite production

    International Nuclear Information System (INIS)

    Lačnjevac, U.Č.; Jović, B.M.; Gajić-Krstajić, Lj.M.; Kovač, J.; Jović, V.D.; Krstajić, N.V.

    2013-01-01

    Highlights: ► Composite Cr–MoO 2 coatings were prepared by electrodeposition onto mild steel and Ti substrates. ► Ti/Cr–MoO 2 electrodes were investigated as cathode materials for the hypochlorite production. ► Selectivity of electrodes increased with the increase of the content of MoO 2 in the coating. ► The current efficiency for the HER exceeded 97% at the best cathode. ► The suppression of hypochlorite reduction is caused by the presence of Cr 2 O 3 at the surface. -- Abstract: The aim of this work was to investigate the possibility of preparation of the composite Cr–MoO 2 coatings onto steel and titanium substrates as cathode materials with high selective properties which imply the suppression of hypochlorite reduction as a side reaction during hypochlorite commercial production. The electrodes were prepared by simultaneous deposition of chromium and suspended MoO 2 particles on titanium substrate from acid chromium (VI) bath. The current efficiency for electrodeposition of the composite coatings did not vary significantly with the concentration of suspended MoO 2 particles. The content of molybdenum in the deposits was relatively low (0.2–1.5 at.%) and increased with increasing the concentration of suspended MoO 2 particles in the bath, in the range from 0 to 10 g dm −3 . With further increase in the concentration of MoO 2 , the content of molybdenum in the coating varied insignificantly. X-ray photoelectron spectroscopy-XPS and EDS analysis were applied to analyze elemental composition and chemical bonding of elements on the surface and in the sub-surface region of obtained coatings. When the concentration of MoO 2 particles in the bath was raised above 5 g dm −3 , the appearance of the coating changed from the typical pure chromium deposit to needle-like deposit with the appearance of black inclusions on the surface. XPS analysis and corresponding Cr 2p spectra showed the presence of chromium oxide, probably Cr 2 O 3 with Cr(3

  15. Corrosion aspects of steel radioactive waste containers in cementitious materials

    International Nuclear Information System (INIS)

    Smart, Nick

    2012-01-01

    Nick Smart from Serco, UK, gave an overview of the effects of cementitious materials on the corrosion of steel during storage and disposal of various low- and intermediate-level radioactive wastes. Steel containers are often used as an overpack for the containment of radioactive wastes and are routinely stored in an open atmosphere. Since this is an aerobic and typically humid environment, the steel containers can start to corrode whilst in storage. Steel containers often come into contact with cementitious materials (e.g. grout encapsulants, backfill). An extensive account of different steel container designs and of steel corrosion mechanisms was provided. Steel corrosion rates under conditions buffered by cementitious materials have been evaluated experimentally. The main conclusion was that the cementitious environment generally facilitates the passivation of steel materials. Several general and localised corrosion mechanisms need to be considered when evaluating the performance of steel containers in cementitious environments, and environmental thresholds can be defined and used with this aim. In addition, the consequences of the generation of gaseous hydrogen by the corrosion of carbon steel under anoxic conditions must be taken into account. Discussion of the paper included: Is crevice corrosion really significant in cementitious systems? Crevice corrosion is unlikely in the cementitious backfill considered because it will tend to neutralise any acidic conditions in the crevice. What is the role of microbially-induced corrosion (MIC) in cementitious systems? Microbes are likely to be present in a disposal facility but their effect on corrosion is uncertain

  16. Assessment of materials for nuclear fuel immobilization containers

    Energy Technology Data Exchange (ETDEWEB)

    Nuttall, K; Urbanic, V F

    1981-09-01

    A wide range of engineering metals and alloys has been assessed for their suitability as container materials for irradiated nuclear fuel intended for permanent disposal in a deep, underground hard-rock vault. The expected range of service conditions in the disposal vault are discussed, as well as the material properties required for this application. An important requirement is that the container last at least 500 years without being breached. The assessment is treated in two parts. Part I concentrates on the physical and mechanical metallurgy, with special reference to strength, weldability, potential embrittlement mechanisms and some economic aspects. Part II discusses possible mechanisms of metallic corrosion for the various engineering alloys and the expected range of environmental conditions in the vault. Localized corrosion and delayed fracture processes are identified as being most likely to limit container lifetime. Hence an essential requirement is that such processes either be absent or proceed at an insignificant rate. Three groups of alloys are recommended for further consideration as possible container materials: AISI 300 series austenitic stainless steels, high nickel-base alloys and very dilute titanium-base alloys. Specific alloys from each group are indicated as having the optimum combination of required properties, including cost. For container designs where the outer container shell does not independently support the service loads, copper should also be considered. The final material selection will depend primarily on the enviromental conditions in the vault. 42 figures, 31 tables.

  17. Transport of bundles and equipment which contain radioactive material

    International Nuclear Information System (INIS)

    1987-01-01

    This norm settles down: 1) The requirements that should be completed in relation to safety precautions and protection against ionizing radiations during the transport radioactive material and/or equipment containing it, in order to avoid risks to the collective and the environment. 2) The basic information on procedures that will be completed in the event of happening accidents during the transport or the transit storage of radioactive material and/or equipment that contain it. 3) The measures of security and physical protection during the transport of radioactive material and/or equipment containing it. This norm is applied: 1) To all the ways of transport (by air, by ground and by ship, fluvial and marine) of radioactive material and/or equipment that contain it. 2) To all natural or legal, public or private person, devoted to install, produce, trade, market, import or export radioactive materials and/or equipment containing it, and that needs to transport them as main or secondary activity [es

  18. Nondestructive Examination Of Plutonium-Bearing Material Containers

    International Nuclear Information System (INIS)

    Yerger, L.; Mcclard, J.; Traver, L.; Grim, T.

    2010-01-01

    The first nondestructive examination (NDE) of 3013-type containers as part of the Department of Energy's (DOE's) Integrated Surveillance Program (ISP) was performed in February, 2005. Since that date 280 NDE surveillances on 255 containers have been conducted. These containers were packaged with plutonium-bearing materials at multiple DOE sites. The NDE surveillances were conducted at Hanford, Lawrence Livermore National Laboratory (LLNL), and Savannah River Site (SRS). These NDEs consisted of visual inspection, mass verification, radiological surveys, prompt gamma analysis, and radiography. The primary purpose of performing NDE surveillances is to determine if there has been a significant pressure buildup inside the inner 3013 container. This is done by measuring the lid deflection of the inner 3013 container using radiography images. These lid deflection measurements are converted to pressure measurements to determine if a container has a pressure of a 100 psig or greater. Making this determination is required by Surveillance and Monitoring Plan (S and MP). All 3013 containers are designed to withstand at least 699 psig as specified by DOE-STD-3013. To date, all containers evaluated have pressures under 50 psig. In addition, the radiography is useful in evaluating the contents of the 3013 container as well as determining the condition of the walls of the inner 3013 container and the convenience containers. The radiography has shown no signs of degradation of any container, but has revealed two packaging anomalies. Quantitative pressure measurements based on lid deflections, which give more information than the 'less than or greater than 100 psig' (pass/fail) data are also available for many containers. Statistical analyses of the pass/fail data combined with analysis of the quantitative data show that it is extremely unlikely that any container in the population of 3013 containers considered in this study (e.g., containers packaged according to the DOE-STD-3013

  19. Electrochemical performance of La2O3/Li2O/TiO2 nano-particle coated cathode material LiFePO4.

    Science.gov (United States)

    Wang, Hong; Yang, Chi; Liu, Shu-Xin

    2014-09-01

    Cathode material, LiFePO4 was modified by coating with a thin layer of La2O3/Li2O/TiO2 nano-particles for improving its performance for lithium ion batteries. The morphology and structure of the modified cathode material were characterized by powder X-ray diffraction, scanning electron microcopy and AES. The performance of the battery with the modified cathode material, including cycling stability, C-rate discharge was examined. The results show that the battery composed of the coated cathode materials can discharge at a large current density and show stable cycling performance in the range from 2.5 to 4.0 V. The rate of Li ion diffusion increases in the battery with the La2O3/Li2O/TiO2-coated LiFePO4 as a cathode and the coating layer may acts as a faster ion conductor (La(2/3-x)Li(3x)TiO3).

  20. Effect of preparation methods of LiNi1-xCoxO2 cathode materials on their chemical structure and electrode performance

    International Nuclear Information System (INIS)

    Cho, J.; Kim, G.; Lim, H.S.

    1999-01-01

    The authors have studied effects of different starting materials on preparation of LiNi 1-x Co x O 2 cathode material for a Li-ion cell where x = 0.1, 0.2, and 0.3, and the electrochemical properties of resulting compounds from two different preparation methods. A preparation method (method B) which uses spherical powder of Ni 1-x Co x (OH) 2 as one of the starting material produced a much superior cathode material than the other method (method A) which uses Ni(OH) 2 and Co(OH) 2 . Method A produced compounds with relatively high degrees of cation mixing which reduces electrochemical utilization (discharge capacity), increases irreversible capacity, and reduces stability on cycling of the cathode material. Method B, in contrast, produced cathode material with a much reduced degree of cation-mixing, thus improving the electrochemical properties. The spherical particle of material prepared by method B has the additional advantage of improved packing density of the electrode with improved volumetric energy density. The ratio of c/a was increased and the electrochemical stability on cycling of the material was improved as the content of Co (value of x) is increased

  1. Application of electron irradiation to food containers and packaging materials

    International Nuclear Information System (INIS)

    Ueno, Koji

    2010-01-01

    Problems caused by microbial contamination and hazardous chemicals have attracted much attention in the food industry. The number of systems such as hygienic management systems and Hazard Analysis Critical Control Point (HACCP) systems adopted in the manufacturing process is increasing. As manufacturing process control has become stricter, stricter control is also required for microbial control for containers and packaging materials (from disinfection to sterilization). Since safe and reliable methods for sterilizing food containers and packaging materials that leave no residue are required, electron beam sterilization used for medical equipment has attracted attention from the food industry. This paper describes an electron irradiation facility, methods for applying electron beams to food containers and packaging materials, and products irradiated with electron beams. (author)

  2. Surveillance of sealed containers with plutonium oxide materials (ms163)

    Science.gov (United States)

    Worl, Laura; Berg, John; Ford, Doris; Martinez, Max; McFarlan, Jim; Morris, John; Padilla, Dennis; Rau, Karen; Smith, Coleman; Veirs, Kirk; Hill, Dallas; Prenger, Coyne

    2000-07-01

    DOE is embarking upon a program to store large quantities of plutonium-bearing materials for up to fifty years. Materials destined for long-term storage include metals and oxides that are stabilized and packaged according to the DOE storage standard, where the packaging consists of two nested, welded, stainless steel containers. We have designed instrumented storage containers that mimic the inner storage can specified in the 3013 standard at both full- and small-scale capacities (2.4 liter and 0.005 liter, respectively), Figures 1 and 2. The containers are designed to maintain the volume to material mass ratio while allowing the gas composition and pressure to be monitored over time.

  3. Storage and transport containers for radioactive medical materials

    International Nuclear Information System (INIS)

    Suthanthiran, K.

    1989-01-01

    This patent describes a storage and transport container for small-diameter ribbon-like lengths of material including radioactive substances for use in medical treatments, comprising: an exterior shell for radiation shielding metal having top and bottom members of radiation shielding metal integral therewith; radiation shielding metal extending downward from the top of the container and forming a central cavity, the central cavity being separate from the exterior shell material of the container and extending downwardly a distance less than the height of the container; a plurality of small diameter carrier tubes located within the interior of the container and having one end of each tube opening through one side of the container and the other end of such tube opening through the opposite lateral side of the container with the central portion of each tube passing under the central cavity; and a plug of radiation shielding metal removably located in the top the central cavity for shielding the radiation from radiation sources located within the container

  4. Strategies to curb structural changes of lithium/transition metal oxide cathode materials and the changes’ effects on thermal and cycling stability

    International Nuclear Information System (INIS)

    Yu Xiqian; Hu Enyuan; Bak, Seongmin; Zhou Yong-Ning; Yang Xiao-Qing

    2016-01-01

    Structural transformation behaviors of several typical oxide cathode materials during a heating process are reviewed in detail to provide in-depth understanding of the key factors governing the thermal stability of these materials. We also discuss applying the information about heat induced structural evolution in the study of electrochemically induced structural changes. All these discussions are expected to provide valuable insights for designing oxide cathode materials with significantly improved structural stability for safe, long-life lithium ion batteries, as the safety of lithium-ion batteries is a critical issue; it is widely accepted that the thermal instability of the cathodes is one of the most critical factors in thermal runaway and related safety problems. (topical review)

  5. Electrochemical Characteristics of Layered Transition Metal Oxide Cathode Materials for Lithium Ion Batteries: Surface, Bulk Behavior, and Thermal Properties.

    Science.gov (United States)

    Tian, Chixia; Lin, Feng; Doeff, Marca M

    2018-01-16

    Layered lithium transition metal oxides, in particular, NMCs (LiNi x Co y Mn z O 2 ) represent a family of prominent lithium ion battery cathode materials with the potential to increase energy densities and lifetime, reduce costs, and improve safety for electric vehicles and grid storage. Our work has focused on various strategies to improve performance and to understand the limitations to these strategies, which include altering compositions, utilizing cation substitutions, and charging to higher than usual potentials in cells. Understanding the effects of these strategies on surface and bulk behavior and correlating structure-performance relationships advance our understanding of NMC materials. This also provides information relevant to the efficacy of various approaches toward ensuring reliable operation of these materials in batteries intended for demanding traction and grid storage applications. In this Account, we start by comparing NMCs to the isostructural LiCoO 2 cathode, which is widely used in consumer batteries. Effects of changing the metal content (Ni, Mn, Co) upon structure and performance of NMCs are briefly discussed. Our early work on the effects of partial substitution of Al, Fe, and Ti for Co on the electrochemical and bulk structural properties is then covered. The original aim of this work was to reduce the Co content (and thus the raw materials cost) and to determine the effect of the substitutions on the electrochemical and bulk structural properties. More recently, we have turned to the application of synchrotron and advanced microscopy techniques to understand both bulk and surface characteristics of the NMCs. Via nanoscale-to-macroscale spectroscopy and atomically resolved imaging techniques, we were able to determine that the surfaces of NMC undergo heterogeneous reconstruction from a layered structure to rock salt under a variety of conditions. Interestingly, formation of rock salt also occurs under abuse conditions. The surface

  6. An annotated history of container candidate material selection

    International Nuclear Information System (INIS)

    McCright, R.D.

    1988-07-01

    This paper documents events in the Nevada Nuclear Waste Storage Investigations (NNWSI) Project that have influenced the selection of metals and alloys proposed for fabrication of waste package containers for permanent disposal of high-level nuclear waste in a repository at Yucca Mountain, Nevada. The time period from 1981 to 1988 is covered in this annotated history. The history traces the candidate materials that have been considered at different stages of site characterization planning activities. At present, six candidate materials are considered and described in the 1988 Consultation Draft of the NNWSI Site Characterization Plan (SCP). The six materials are grouped into two alloy families, copper-base materials and iron to nickel-base materials with an austenitic structure. The three austenitic candidates resulted from a 1983 survey of a longer list of candidate materials; the other three candidates resulted from a special request from DOE in 1984 to evaluate copper and copper-base alloys. 24 refs., 2 tabs

  7. Synthesis and electrochemical characterization of nano-CeO2-coated nanostructure LiMn2O4 cathode materials for rechargeable lithium batteries

    International Nuclear Information System (INIS)

    Arumugam, D.; Kalaignan, G. Paruthimal

    2010-01-01

    LiMn 2 O 4 spinel cathode materials were coated with 0.5, 1.0, and 1.5 wt.% CeO 2 by a polymeric process, followed by calcination at 850 o C for 6 h in air. The surface-coated LiMn 2 O 4 cathode materials were physically characterized using X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron microscopy (XPS). XRD patterns of CeO 2 -coated LiMn 2 O 4 revealed that the coating did not affect the crystal structure or the Fd3m space group of the cathode materials compared to uncoated LiMn 2 O 4 . The surface morphology and particle agglomeration were investigated using SEM, TEM image showed a compact coating layer on the surface of the core materials that had average thickness of about 20 nm. The XPS data illustrated that the CeO 2 completely coated the surface of the LiMn 2 O 4 core cathode materials. The galvanostatic charge and discharge of the uncoated and CeO 2 -coated LiMn 2 O 4 cathode materials were measured in the potential range of 3.0-4.5 V (0.5 C rate) at 30 o C and 60 o C. Among them, the 1.0 wt.% of CeO 2 -coated spinel LiMn 2 O 4 cathode satisfies the structural stability, high reversible capacity and excellent electrochemical performances of rechargeable lithium batteries.

  8. Nitrate remediation in a novel upflow bio-electrochemical reactor (UBER) using palm shell activated carbon as cathode material

    International Nuclear Information System (INIS)

    Ghafari, Shahin; Hasan, Masitah; Aroua, Mohamed Kheireddine

    2009-01-01

    This study investigated the biological denitrification method which is a treatment method able to reduce inorganic nitrate compounds to harmless nitrogen gas. Autohydrogenotrophic denitrifying bacteria were used in this study to prevent any problematic outcomes associated with heterotrophic microorganisms. An upflow bio-electrochemical reactor (UBER) was used to accommodate hydrogenotrophic denitrifying bacteria employing palm shell granular activated carbon (GAC) as the biocarrier and cathode material. Bicarbonate as the external inorganic carbon source was fed to the reactor and hydrogen as the electron donor was generated in situ through electrolysis of water. Central composite design (CCD) and response surface methodology (RSM) were applied to investigate the effects of two operating parameters, namely electric current (I) and hydraulic retention time (HRT), on performance of the UBER. Electric current range of 0-20 mA and HRT range of 6-36 h were examined and results showed that nitrate can be entirely reduced within application of a wide operational range of electric current (10-16 mA) as well as HRT (13.5-30 h). However, increase of pH at cathode zone up to 10.5 inhibited nitrite reduction, and it was not reduced to the satisfactory level.

  9. Crystallography and Growth of Epitaxial Oxide Films for Fundamental Studies of Cathode Materials Used in Advanced Li-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Leonid A. Bendersky

    2017-05-01

    Full Text Available Li-ion battery systems, synthesized as epitaxial thin films, can provide powerful insights into their electrochemical processes. Crystallographic analysis shows that many important cathode oxides have an underlying similarity: their structures can be considered as different ordering schemes of Li and transition metal ions within a pseudo-cubic sublattice of oxygen anions arranged in a face-center cubic (FCC fashion. This oxygen sublattice is compatible with SrTiO3 and similar perovskite oxides, thus perovskites can be used as supporting substrates for growing epitaxial cathode films. The predicted epitaxial growth and crystallographic relations were experimentally verified for different oxide films deposited by pulsed laser deposition (PLD on SrTiO3 or SrRuO3/SrTiO3 of different orientations. The results based on cross-sectional high-resolution TEM of the following films are presented in the paper: (a trigonal LiCoO2; (b orthorhombic LiMnO2; (c monoclinic Li2MnO3; (d compositionally-complex monoclinic Li1.2Mn0.55Ni0.15Co0.1O2. All results demonstrated the feasibility of epitaxial growth for these materials, with the growth following the predicted cube-on-cube orientation relationship between the cubic and pseudo-cubic oxygen sublattices of a substrate and a film, respectively.

  10. System for indicating the level of material in a container

    International Nuclear Information System (INIS)

    Erb, T.L.

    1980-01-01

    In a radiation detecting system for controlling the level of material in a container, the first counter accumulates pulses generated by a geiger tube at a rate related to the level of material and a second counter accumulates clock pulses. A race condition is established between a NAND circuit indicating that the first counter has reached a predetermined total, and a NAND circuit indicating that the second counter has reached a second predetermined total representing a fixed counting interval. The first NAND circuit to respond to its predetermined total actuates a circuit to reset both counters and, if indicative of the material level being below a predetermined minimum, actuates an alarm or operates a control circuit to add material to the container. In the example shown, an additional NAND circuit responds to a different count in the first counter which count in the same time interval corresponds to a higher level, and when material is being added to the container, the race condition is between two NAND circuits. The effect of this is to provide a hysteresis effect preventing the circuit from 'hunting' around one level of material. (author)

  11. Corrosion-Resistant Container for Molten-Material Processing

    Science.gov (United States)

    Stern, Theodore G.; McNaul, Eric

    2010-01-01

    In a carbothermal process, gaseous methane is passed over molten regolith, which is heated past its melting point to a temperature in excess of 1,625 C. At this temperature, materials in contact with the molten regolith (or regolith simulant) corrode and lose their structural properties. As a result, fabricating a crucible to hold the molten material and providing a method of contact heating have been problematic. Alternative containment approaches use a large crucible and limit the heat zone of the material being processed, which is inefficient because of volume and mass constraints. Alternative heating approaches use non-contact heating, such as by laser or concentrated solar energy, which can be inefficient in transferring heat and thus require higher power heat sources to accomplish processing. The innovation is a combination of materials, with a substrate material having high structural strength and stiffness and high-temperature capability, and a coating material with a high corrosion resistance and high-temperature capability. The material developed is a molybdenum substrate with an iridium coating. Creating the containment crucible or heater jacket using this material combination requires only that the molybdenum, which is easily processed by conventional methods such as milling, electric discharge machining, or forming and brazing, be fabricated into an appropriate shape, and that the iridium coating be applied to any surfaces that may come in contact with the corrosive molten material. In one engineering application, the molybdenum was fashioned into a container for a heat pipe. Since only the end of the heat pipe is used to heat the regolith, the container has a narrowing end with a nipple in which the heat pipe is snugly fit, and the external area of this nipple, which contacts the regolith to transfer heat into it, is coated with iridium. At the time of this reporting, no single material has been found that can perform the functions of this combination

  12. SmBaCoCuO5+x as cathode material based on GDC electrolyte for intermediate-temperature solid oxide fuel cells

    International Nuclear Information System (INIS)

    Lue Shiquan; Long, Guohui; Ji Yuan; Meng Xiangwei; Zhao Hongyuan; Sun Cuicui

    2011-01-01

    Research highlights: → We synthesize a new kind of layered perovskite SmBaCoCuO 5+x (SBCCO) as a cathode material of a solid oxide fuel cell. → There are some reports on the performance of cathodes in proton-conducting SOFCs based on BaCe 0.8 Sm 0.2 O 3-δ electrolyte. → However, to the best of our knowledge, the performance of SBCCO cathodes in oxygen-ion conducting SOFCs has not been reported to date. → In this work, the ceramic powder SBCCO is examined as a cathode for IT-SOFCs based on Ce 0.9 Gd 0.1 O 1.95 (GDC) electrolyte. - Abstract: The performance of SmBaCoCuO 5+x (SBCCO) cathode has been investigated for their potential utilization in intermediate-temperature solid oxide fuel cells (IT-SOFCs). The powder X-ray diffraction (XRD), thermal expansion and electrochemical performance on Ce 0.9 Gd 0.1 O 1.95 (GDC) electrolyte are evaluated. XRD results show that there is no chemical reaction between SBCCO cathode and GDC electrolyte when the temperature is below 950 o C. The thermal expansion coefficient (TEC) value of SBCCO is 15.53 x 10 -6 K -1 , which is ∼23% lower than the TEC of the SmBaCo 2 O 5+x (SBCO) sample. The electrochemical impedance spectra reveals that SBCCO symmetrical half-cells by sintering at 950 deg. C has the best electrochemical performance and the area specific resistance (ASR) of SBCCO cathode is as low as 0.086 Ω cm 2 at 800 o C. An electrolyte-supported fuel cell generates good performance with the maximum power density of 517 mW cm -2 at 800 deg. C in H 2 . Preliminary results indicate that SBCCO is promising as a cathode for IT-SOFCs.

  13. Electrochemical properties of LiMn2O4 cathode material doped with an actinide

    International Nuclear Information System (INIS)

    Eftekhari, Ali; Moghaddam, Abdolmajid Bayandori; Solati-Hashjin, Mehran

    2006-01-01

    Metal substation as an efficient approach for improvement of battery performance of LiMn 2 O 4 was performed by an actinide dopant. Uranium as the last natural element and most common actinide was employed for this purpose. Cyclic voltammetric studies revealed that incorporation of uranium into LiMn 2 O 4 spinel significantly improves electrochemical performance. It also strengthens the spinel stability to exhibit better cycleability. Surprisingly, the capacity increases upon cycling of LiU 0.01 Mn 1.99 O 4 cathode. This inverse behavior is attributed to uniform distribution of dopant during insertion/extraction process. In other words, this is an electrochemical refinement of the nanostructure which is not detectable in microscale morphology, as rearrangement of dopant in nanoscale occurs and this is an unexceptional nanostructural ordering. In addition, uranium doping strengthens the Li diffusion, particularly at redox potentials

  14. A closed-loop process for recycling LiNixCoyMn(1−x−yO2 from mixed cathode materials of lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    Rujuan Zheng

    2017-01-01

    Full Text Available With the rapid development of consumer electronics and electric vehicles (EV, a large number of spent lithium-ion batteries (LIBs have been generated worldwide. Thus, effective recycling technologies to recapture a significant amount of valuable metals contained in spent LIBs are highly desirable to prevent the environmental pollution and resource depletion. In this work, a novel recycling technology to regenerate a LiNi1/3Co1/3Mn1/3O2 cathode material from spent LIBs with different cathode chemistries has been developed. By dismantling, crushing, leaching and impurity removing, the LiNi1/3Co1/3Mn1/3O2 (selected as an example of LiNixCoyMn(1−x−yO2 powder can be directly prepared from the purified leaching solution via co-precipitation followed by solid-state synthesis. For comparison purposes, a fresh-synthesized sample with the same composition has also been prepared using the commercial raw materials via the same method. X-ray diffraction (XRD, scanning electron microscopy (SEM and electrochemical measurements have been carried out to characterize these samples. The electrochemical test result suggests that the re-synthesized sample delivers cycle performance and low rate capability which are comparable to those of the fresh-synthesized sample. This novel recycling technique can be of great value to the regeneration of a pure and marketable LiNixCoyMn(1−x−yO2 cathode material with low secondary pollution. Keywords: Spent lithium-ion battery, Cathode material recycling, Acid leaching, Purification, Co-precipitation

  15. Synthesis and characterization of Co-doped lanthanum nickelate perovskites for solid oxide fuel cell cathode material

    International Nuclear Information System (INIS)

    Chavez G, L.; Hinojosa R, M.; Medina L, B.; Ringuede, A.; Cassir, M.; Vannier, R. N.

    2017-01-01

    In the perovskite structures widely investigated and used as solid oxide fuel cells cathodes, oxygen reduction is mainly limited to the triple phase boundary (TPB), where oxygen (air), electrode and electrolyte are in contact. It is possible via the sol-gel modified Pechini method to: 1) control the material grain size, which can increase TPBs, 2) produce a homogenous material and 3) obtain a cathode material in a faster way compared with the solid state route. LaNi_xCo_1_-_xO_3 (x = 0.3, 0.5, 0.7) were synthesized by the modified Pechini method. The perovskite phase formation began at 350 degrees Celsius and the presence of pure LaNi_0_._7Co_0_._3O_3, LaNi_0_._5Co_0_._5O_3 and LaNi_0_._3Co_0_._7O_3 structures was evidenced by high temperature X-ray diffraction (Ht-XRD) measurements. Scanning electron microscopy (Sem) micrographs showed that the microstructure evolves with the amount of cobalt from a coalesced to an open structure. Electrochemical impedance spectroscopy (EIS) on symmetrical cells LaNi_xCo_1_-_xO_3/YSZ (Yttria-stabilized zirconia)/LaNi_xCo_1_-_xO_3 showed that the highest ASR (area specific resistance) is obtained with x = 0.3, whereas ASR values are similar for x = 0.5 and 0.7 at temperatures higher than 600 degrees Celsius. At temperatures lower than 600 degrees Celsius, ASR is the lowest for LaNi_0_._5Co_0_._5O_3, showing that this composition with intermediate porosity appears as a good choice for and intermediate-temperature solid oxid fuel cell. (Author)

  16. Enhanced electrochemical properties of LiNiO{sub 2}-based cathode materials by nanoscale manganese carbonate treatment

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Junkai; Wang, Zhixing, E-mail: zxwang.csu@hotmail.com; Guo, Huajun; Li, Xinhai

    2017-05-01

    Highlights: • Li residuals are consumed during the process of modification. • MnO{sub 2} coating layer can protect bulk material from the erosion of electrolyte. • The electrochemical performance is enhanced by the nanosacle MnCO{sub 3} treatment. • The enhancement of coating can be strengthened by the removal of lithium impurities. - Abstract: LiNiO{sub 2}-based layered oxides are of great importance as cathode materials for rechargeable batteries. In this paper, illustrating LiNi{sub 0.8}Co{sub 0.15}Al{sub 0.05}O{sub 2} as an example, the effect of nanoscale MnCO{sub 3} treatment on LiNiO{sub 2}-based materials is investigated for the first time. The structures of materials and the properties about the object surface are characterized by XRD, SEM, TEM, EDAX and XPS. The results demonstrate that a part of MnCO{sub 3} is able to react with lithium impurities to form nonstoichiometric Li{sub x}Mn{sub y}O{sub 4} and the rest of MnCO{sub 3} is converted to MnO{sub 2} coating on the surface of the material in situ. After 100 repeated cycles at 1C, the modified material exhibits a capacity retention rate of 91.2%, while the bare material only remains 84.8%. And the modified material exhibits more significantly improved cycling stability when cycling at 60 °C, maintaining 85.7% of its initial capacity at 1C after 100th cycles. The consumption of Li impurities can decelerate the decomposition of electrolyte during cycling, thus result in less resistive byproducts. Moreover, the obtained MnO{sub 2} coating layer acts as an isolating layer to suppress the drastic reaction between active material and electrolyte. This synergistic effect is responsible for the excellent properties of MnCO{sub 3}-modified material.

  17. Radiation exposure by man-modified materials containing natural radionuclides

    Energy Technology Data Exchange (ETDEWEB)

    Becker, D.E. [Technical Inspection Agency of Bavaria, Munich (Germany); Eder, E. [Government of Bavaria, Ministry for State Development and Environmental Affairs Development, Munich (Germany); Reichelt, A. [Technical Inspection Agency of Bavaria, Munich (Germany)

    1992-07-01

    More than one hundred materials, containing natural radioactive nuclides, are being investigated due to radiation exposure to people. This paper deals with thoriated gas mantles and shows that the radiation exposure by inhalation of radionuclides released while burning and exchange is not negligible. (author)

  18. 19 CFR 10.539 - Retail packaging materials and containers.

    Science.gov (United States)

    2010-04-01

    ...-Singapore Free Trade Agreement Rules of Origin § 10.539 Retail packaging materials and containers. Packaging... requirement. The United States importer of good C decides to use the build-down method, RVC=((AV−VNM)/AV... content requirement. In applying this method, the non-originating blister packages are taken into account...

  19. Ensuring the 50 year life of a fissile material container

    International Nuclear Information System (INIS)

    Glass, R.E.; Towne, T.L.

    1997-12-01

    Sandia was presented with an opportunity in 1993 to design containers for the long term storage and transport of fissile material. This program was undertaken at the direction of the US Department of Energy and in cooperation with Lawrence Livermore National Laboratory and Los Alamos National Laboratory which were tasked with developing the internal fixturing for the contents. The hardware is being supplied by Allied Signal Federal Manufacturing and Technologies, and the packaging will occur at Mason and Hangar Corporation's Pantex Plant. The unique challenge was to design a container that could be sealed with the fissile material contents; and, anytime during the next 50 years, the container could be transported with only the need for the pre-shipment leak test. This required not only a rigorous design capable of meeting the long term storage and transportation requirements, but also resulted in development of a surveillance program to ensure that the container continues to perform as designed over the 50-year life. This paper addresses the design of the container, the testing that was undertaken to demonstrate compliance with US radioactive materials transport regulations, and the surveillance program that has been initiated to ensure the 50-year performance

  20. An assessment of materials for nuclear fuel immobilization containers

    International Nuclear Information System (INIS)

    Nuttall, K.; Urbanic, V.F.

    1981-09-01

    A wide range of engineering metals and alloys was assessed for their suitability as container materials for irradiated nuclear fuel intended for permanent disposal in a deep, underground hard-rock vault. The container must last at least 500 years without being breached. Materials were assessed for their physical and mechanical metallurgy, weldability, potential embrittlement mechanisms, and economics. A study of the possible mechanisms of metallic corrosion for the various engineering alloys and the expected range of environmental conditons in the vault showed that localized corrosion and delayed fracture processes are the most likely to limit container lifetime. Thus such processes either must be absent or proceed at an insignificant rate. Three groups of alloys are recommended for further study: AISI 300 series austenitic stainless steels, high nickel-base alloys and very dilute titanium-base alloys. Specific alloys from each group are indicated as having the optimum combination of required properties, including cost. For container designs where the outer container shell does not independently support the service loads, copper should also be considered. The final material selection will depend primarily on the environmental conditions in the vault

  1. Turning Waste Chemicals into Wealth-A New Approach To Synthesize Efficient Cathode Material for an Li-O2 Battery.

    Science.gov (United States)

    Yao, Ying; Wu, Feng

    2017-09-20

    An Li-O 2 battery requires the oxygen-breathing cathode to be highly electronically conductive, rapidly oxygen diffusive, structurally stable, and often times electrocatalytically active. Catalyst-decorated porous carbonaceous materials are the chosen air cathode in this regard. Alternatively, biomass-derived carbonaceous materials possess great ability to remove heavy and toxic metal ions from waste, forming a metal-adsorbed porous carbonaceous material. The similar structure between the air cathode and the metal-adsorbed biomass-derived carbon nicely bridges these two irrelevant areas. In this study, we investigated the electrochemical activity of a biochar material Ag-ESB directly synthesized from ethanol sludge residue in a rechargeable aprotic Li-O 2 battery. Ag ions were adsorbed from sewage and became Ag nanoparticles with uniform coverage on the biochar surface. The as-prepared material exhibits good electrochemical behavior in battery testing, especially toward the battery efficiency and cyclability. This study provides the possibility of synthetically efficient cathode material by reusing "waste" such as biofuel sludge residue. It is an economically and environmentally friendly approach both for an energy-storage system and for waste recycling.

  2. Building Honeycomb-Like Hollow Microsphere Architecture in a Bubble Template Reaction for High-Performance Lithium-Rich Layered Oxide Cathode Materials.

    Science.gov (United States)

    Chen, Zhaoyong; Yan, Xiaoyan; Xu, Ming; Cao, Kaifeng; Zhu, Huali; Li, Lingjun; Duan, Junfei

    2017-09-13

    In the family of high-performance cathode materials for lithium-ion batteries, lithium-rich layered oxides come out in front because of a high reversible capacity exceeding 250 mAh g -1 . However, the long-term energy retention and high energy densities for lithium-rich layered oxide cathode materials require a stable structure with large surface areas. Here we propose a "bubble template" reaction to build "honeycomb-like" hollow microsphere architecture for a Li 1.2 Mn 0.52 Ni 0.2 Co 0.08 O 2 cathode material. Our material is designed with ca. 8-μm-sized secondary particles with hollow and highly exposed porous structures that promise a large flexible volume to achieve superior structure stability and high rate capability. Our preliminary electrochemical experiments show a high capacity of 287 mAh g -1 at 0.1 C and a capacity retention of 96% after 100 cycles at 1.0 C. Furthermore, the rate capability is superior without any other modifications, reaching 197 mAh g -1 at 3.0 C with a capacity retention of 94% after 100 cycles. This approach may shed light on a new material engineering for high-performance cathode materials.

  3. Turning Waste Chemicals into Wealth—A New Approach To Synthesize Efficient Cathode Material for an Li–O 2 Battery

    Energy Technology Data Exchange (ETDEWEB)

    Yao, Ying; Wu, Feng (Beijing Inst. Tech.)

    2017-03-20

    An Li–O2 battery requires the oxygen-breathing cathode to be highly electronically conductive, rapidly oxygen diffusive, structurally stable, and often times electrocatalytically active. Catalyst-decorated porous carbonaceous materials are the chosen air cathode in this regard. Alternatively, biomass-derived carbonaceous materials possess great ability to remove heavy and toxic metal ions from waste, forming a metal-adsorbed porous carbonaceous material. The similar structure between the air cathode and the metal-adsorbed biomass-derived carbon nicely bridges these two irrelevant areas. In this study, we investigated the electrochemical activity of a biochar material Ag-ESB directly synthesized from ethanol sludge residue in a rechargeable aprotic Li–O2 battery. Ag ions were adsorbed from sewage and became Ag nanoparticles with uniform coverage on the biochar surface. The as-prepared material exhibits good electrochemical behavior in battery testing, especially toward the battery efficiency and cyclability. This study provides the possibility of synthetically efficient cathode material by reusing “waste” such as biofuel sludge residue. It is an economically and environmentally friendly approach both for an energy-storage system and for waste recycling.

  4. Targeted partial surface modification with nano-SiO2@Li2CoPO4F as high-voltage cathode material for LIBs

    Science.gov (United States)

    Chang, Caiyun; Huang, Zhipeng; Tian, Runsai; Jiang, Xinyu; Li, Chunsheng; Feng, Jijun

    2017-10-01

    Tuning whole/partial surface modification on cathode material with oxide material is a sought-after method to enhance the electrochemical performance in power storage field. Herein, nano-SiO2 targeted partial surface modified high voltage cathode material Li2CoPO4F has been successfully fabricated via a facile self-assembly process in silica dispersion at ambient temperature. With the aid of polar -OH groups attracted on the surface of SiO2 micelles, the nano-SiO2 preferentially nestle up along the borders and boundaries of Li2CoPO4F particles, where protection should be deployed with emphasis against the undesirable interactions between materials and electrolytes. Compared with pristine Li2CoPO4F, the SiO2 selectively modified Li2CoPO4F cathode materials, especially LCPF-3S, exhibit desirable electrochemical performances with higher discharge capacity, more outstanding cycle stability and favorable rate capability without any additional carbon involved. The greatly enhanced electrochemical properties can be attributed to the improved lithium-ion diffusion kinetics and structure tolerance during repeated lithiation/delithiation process. Such findings reveal a great potential of nano-SiO2 modified Li2CoPO4F as high energy cathode material for lithium ion batteries.

  5. Hearth furnace for distilling powdered materials containing hydrocarbons

    Energy Technology Data Exchange (ETDEWEB)

    1937-06-21

    The present invention has for its object a hearth furnace particularly intended for the distillation of powdered material containing hydrocarbons. It consists of a fixed circular hearth above which are placed the moving scrapers intended to displace the material from the center toward the periphery. The material is poured by a central vertical pipe at the base of which is arranged a rotating ring for distributing the material on the hearth; this ring, which is fastened on the vertical axis of the drive, carries the radial arms to which are attached the scrapers arranged obliquely by the support on the arms and intended to displace the material on the hearth. The hearth is heated from below by means of forced circulation of gases produced in a fire-box and maintained at a convenient temperature by mixing with a part of the cold gases.

  6. Materials performance in off-gas systems containing iodine

    International Nuclear Information System (INIS)

    Beavers, J.A.; Berry, W.E.; Griess, J.C.

    1981-11-01

    During the reprocessing of spent reactor fuel elements, iodine is released to gas streams from which it is ultimately removed by conversion to nonvolatile iodic acid. Under some conditions iodine can produce severe corrosion in off-gas lines; in this study these conditions were established. Iron- and nickel-based alloys containing more than 6% molybdenum, such as Hastelloy G (7%), Inconel 625 (9%), and Hastelloy C-276 (16%), as well as titanium and zirconium, remained free of attack under all conditions tested. When the other materials, notably the austenitic stainless steels, were exposed to gas streams containing even only low concentrations of iodine and water vapors at 25 and 40 0 C, a highly corrosive, brownish-green liquid formed on their surfaces. In the complete absence of water vapor, the iodine-containing liquid did not form and all materials remained unaffected. The liquid that formed had a low pH (usually 2 inhibited attack

  7. Functioning mechanism of AlF3 coating on the Li- and Mn-rich cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming; Gu, Meng; Xiao, Jie; Polzin, Bryant; Yan, Pengfei; Chen, Xilin; Wang, Chong M.; Zhang, Jiguang

    2014-11-25

    Li- and Mn-rich (LMR) material is a very promising cathode for lithium ion batteries because of their high theoretical energy density (~900 Wh kg-1) and low cost. However, their poor long-term cycling stability, voltage fade, and low rate capability are significant barriers hindered their practical applications. Surface coating, e.g. AlF3 coating, can significantly improve the capacity retention and enhance the rate capability. However, the fundamental mechanism of this improvement and the microstructural evolution related to the surface coating is still not well understood. Here, we report systematic studies of the microstructural changes of uncoated and AlF3-coated materials before and after cycling using aberration-corrected scanning/transmission electron microscopy and electron energy loss spectroscopy. The results reveal that surface coating can reduce the oxidation of electrolyte at high voltage, thus suppressing the accumulation of SEI layer on electrode particle surface. Surface coating also enhances structural stability of the surface region (especially the electrochemically transformed spinel-like phase), and protects the electrode from severe etching/corrosion by the acidic species in the electrolyte, therefore limiting the degradation of the material. Moreover, surface coating can alleviate the undesirable voltage fade by minimize layered-spinel phase transformation in the bulk region of the materials. These fundamental findings may also be widely applied to explain the functioning mechanism of other surface coatings used in a broad range of electrode materials.

  8. Mitigating Voltage Decay of Li-Rich Cathode Material via Increasing Ni Content for Lithium-Ion Batteries.

    Science.gov (United States)

    Shi, Ji-Lei; Zhang, Jie-Nan; He, Min; Zhang, Xu-Dong; Yin, Ya-Xia; Li, Hong; Guo, Yu-Guo; Gu, Lin; Wan, Li-Jun

    2016-08-10

    Li-rich layered materials have been considered as the most promising cathode materials for future high-energy-density lithium-ion batteries. However, they suffer from severe voltage decay upon cycling, which hinders their further commercialization. Here, we report a Li-rich layered material 0.5Li2MnO3·0.5LiNi0.8Co0.1Mn0.1O2 with high nickel content, which exhibits much slower voltage decay during long-term cycling compared to conventional Li-rich materials. The voltage decay after 200 cycles is 201 mV. Combining in situ X-ray diffraction (XRD), ex situ XRD, ex situ X-ray photoelectron spectroscopy, and scanning transmission electron microscopy, we demonstrate that nickel ions act as stabilizing ions to inhibit the Jahn-Teller effect of active Mn(3+) ions, improving d-p hybridization and supporting the layered structure as a pillar. In addition, nickel ions can migrate between the transition-metal layer and the interlayer, thus avoiding the formation of spinel-like structures and consequently mitigating the voltage decay. Our results provide a simple and effective avenue for developing Li-rich layered materials with mitigated voltage decay and a long lifespan, thereby promoting their further application in lithium-ion batteries with high energy density.

  9. Development of Latent Heat Storage Phase Change Material Containing Plaster

    Directory of Open Access Journals (Sweden)

    Diana BAJARE

    2016-05-01

    Full Text Available This paper reviews the development of latent heat storage Phase Change Material (PCM containing plaster as in passive application. Due to the phase change, these materials can store higher amounts of thermal energy than traditional building materials and can be used to add thermal inertia to lightweight constructions. It was shown that the use of PCMs have advantages stabilizing the room temperature variations during summer days, provided sufficient night ventilation is allowed. Another advantage of PCM usage is stabilized indoor temperature on the heating season. The goal of this study is to develop cement and lime based plaster containing microencapsulated PCM. The plaster is expected to be used for passive indoor applications and enhance the thermal properties of building envelope. The plaster was investigated under Scanning Electron Microscope and the mechanical, physical and thermal properties of created plaster samples were determined.

  10. Container materials for isolation of radioactive waste in salt

    International Nuclear Information System (INIS)

    Streicher, M.A.; Andrews, A.

    1987-10-01

    The workshop reviewed the extensive data on the corrosion resistance of low-carbon steel in simulated salt repository environments, determined whether these data were sufficient to recommend low-carbon steel for fabrication of the container, and assessed the suitability of other materials under consideration in the SRP. The panelists determined the need for testing and research programs, recommended experimental approaches, and recommended materials based on existing technology. On the first day of the workshop, presentations were made on waste package requirements; the expected corrosion environment; degradation processes, including a review of data from corrosion tests on carbon steel; and rationales for container design and materials, modeling studies, and planned future work. The second day was devoted to a panel caucus, presentation of workshop findings, and open discussion. 76 refs., 2 figs., 3 tabs

  11. Recycling of LiCo0.59Mn0.26Ni0.15O2 cathodic material from spent Li-ion batteries by the method of the citrate gel combustion

    Directory of Open Access Journals (Sweden)

    Senćanski Jelena V.

    2017-01-01

    Full Text Available The Li-ion batteries are the main power source for the high technology devices, such as mobile phones and electric vehicles. Because of that, the number of spent Li-ion batteries significantly increases. Today, the number of active mobile phones crossed 7.19 billion. It is estimated that the mass of the spent lithium ion batteries in China will exceed 500,000 t by 2020. The trouble is in the ingredients of these batteries. They contain Li, Co, Mn, Ni, Cu, Al and toxic and flammable electrolytes which have a harmful affection to the environment. Because of that, the recycling procedure attracts raising attention of researches. Several commercial spent Li-ion batteries were recycled by the relatively fast, economic and simple procedure. The three ways of separating the cathode material from Al collector were examined after the manual dismantling of the components of batteries with the Li(Co–Mn–NiO2 as cathode material. These were: 1. dissolution of the Al collector in the alkali medium, 2. peeling off with N-methylpyrrolidone and 3. thermal decomposition of the adhesive at 700°C. The procedure with the highest yield was the one with the dissolution in alkali medium. The chemical analysis of the single batteries'' components (the crust, Al/Cu collector, cathode material were done by the atomic absorption spectrometry. The components, before the analysis, were dissolved. The re-synthesis of the cathode material by the method of the citrate gel combustion was done after the separating the cathode material and dissolving it in the nitric acid. The obtained product was, after annealing, characterized by the methods of X-ray diffraction and Raman spectroscopy. The recycled product was LiCo0.59Mn0.26Ni0.15O2 stoichiometry, with the hexagonal layered structure α-NaFeO2 type. The functionalization of the resynthesized material was examined in the 1 M solution LiClO4 in the propylene carbonate, by galvanostatic charging, with the current density of 0

  12. Synthesis and characterization of gadolinia-doped ceria-silver cermet cathode material for solid oxide fuel cells

    International Nuclear Information System (INIS)

    Datta, Pradyot; Majewski, Peter; Aldinger, Fritz

    2008-01-01

    A series of Ce 0.9 Gd 0.1 O 2-δ -Ag cermets with different Ag contents were prepared by conventional sintering process aiming at assessing the suitability of using them as cathode material for solid oxide fuel cell (SOFC) with Gadolinia-doped ceria electrolyte. The chemical compatibility between Ce 0.9 Gd 0.1 O 2-δ (CGO) and Ag was investigated by X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy. Thermal expansion coefficients of the cermets were measured as a function of Ag content and were found to increase with metallic content. Although oxygen adsorption at the surface of the cermets could be detected, no reaction or solid solubility between CGO and Ag was found

  13. Na2MnSiO4 as an attractive high capacity cathode material for sodium-ion battery

    Science.gov (United States)

    Law, Markas; Ramar, Vishwanathan; Balaya, Palani

    2017-08-01

    Here we report a polyanion-based cathode material for sodium-ion batteries, Na2MnSiO4, registering impressive sodium storage performances with discharge capacity of 210 mAh g-1 at an average voltage of 3 V at 0.1 C, along with excellent long-term cycling stability (500 cycles at 1 C). Insertion/extraction of ∼1.5 mol of sodium ion per formula unit of the silicate-based compound is reported and the utilisation of Mn2+ ⇋ Mn4+ redox couple is also demonstrated by ex-situ XPS. Besides, this study involves a systematic investigation of influence of the electrolyte additive (with different content) on the sodium storage performance of Na2MnSiO4. The electrolyte additive forms an optimum protective passivation film on the electrode surface, successfully reducing manganese dissolution.

  14. Electrochemical characterization of nano-sized Pd-based catalysts as cathode materials in direct methanol fuel cells.

    Science.gov (United States)

    Choi, M; Han, C; Kim, I T; An, J C; Lee, J J; Lee, H K; Shim, J

    2011-01-01

    To improve the catalytic activity of palladium (Pd) as a cathode catalyst in direct methanol fuel cells (DMFCs), we prepared palladium-titanium oxide (Pd-TiO2) catalysts which the Pd and TiO2 nanoparticles were simultaneously impregnated on carbon. We selected Pd and TiO2 as catalytic materials because of their electrochemical stability in acid solution. The crystal structure and the loading amount of Pd and TiO2 on carbon were characterized by X-ray diffraction (XRD) and energy dispersive X-ray microanalysis (EDX). The electrochemical characterization of Pd-TiO2/C catalysts for the oxygen reduction reaction was carried out in half and single cell systems. The catalytic activities of the Pd-TiO2 catalysts were strongly influenced by the TiO2 content. In the single cell test, the Pd-TiO2 catalysts showed very comparable performance to the Pt catalyst.

  15. Effect of microstructure on low temperature electrochemical properties of LiFePO{sub 4}/C cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Nannan; Zhi, Xiaoke; Wang, Li; Liu, Yanhui; Liang, Guangchuan, E-mail: liangguangchuan@hebut.edu.cn

    2015-10-05

    Graphical abstract: The low temperature performance of Li-ion batteries and LiFePO{sub 4}/C composites was discussed. A conclusion that cathode material is the main limitation for the low temperature performance was come up, by comparing the low temperature performance of 18650 Li-ion batteries with LiMn{sub 2}O{sub 4}, LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2} and LiFePO{sub 4}/C as cathode materials. The low temperature performance results indicate the LiFePO{sub 4}/C microstructure is the main factor influencing the low temperature performance of LiFePO{sub 4}. A new LiFePO{sub 4}/C with pomegranate-like spherical structure was proposed in this paper, which shows superior low temperature performance, which can be attributed to its uniform fine primary particles and smaller primary particles. - Highlights: • Low temperature performance of Li-ion battery and LiFePO{sub 4}/C composite was discussed. • Cathode material mainly decided the low temperature performance of Li-ion battery. • LiFePO{sub 4}/C microstructure mainly affects its low temperature performance. • Pomegranate-like spherical structure LiFePO{sub 4}/C has good low temperature performance. - Abstract: The low-temperature electrochemical performance of Li-ion batteries is mainly determined by the choice of cathode material, as evident from a comparison of the low-temperature electrochemical performance of the 18650 batteries with the LiMn{sub 2}O{sub 4}, LiNi{sub 1/3}Co{sub 1/3}Mn{sub 1/3}O{sub 2}, and LiFePO{sub 4}/C as the cathode, respectively, at −20 °C. LiFePO{sub 4}/C materials with different morphologies and microstructures were prepared by different methods. The samples were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), galvanostatic charge–discharge measurements and EIS. The low-temperature performance of the samples and those of the coin cells utilizing the materials as cathodes were measured. The results

  16. Atomic-Resolution Visualization of Distinctive Chemical Mixing Behavior of Ni, Co and Mn with Li in Layered Lithium Transition-Metal Oxide Cathode Materials

    Energy Technology Data Exchange (ETDEWEB)

    Yan, Pengfei; Zheng, Jianming; Lv, Dongping; Wei, Yi; Zheng, Jiaxin; Wang, Zhiguo; Kuppan, Saravanan; Yu, Jianguo; Luo, Langli; Edwards, Danny J.; Olszta, Matthew J.; Amine, Khalil; Liu, Jun; Xiao, Jie; Pan, Feng; Chen, Guoying; Zhang, Jiguang; Wang, Chong M.

    2015-07-06

    Capacity and voltage fading of layer structured cathode based on lithium transition metal oxide is closely related to the lattice position and migration behavior of the transition metal ions. However, it is scarcely clear about the behavior of each of these transition metal ions. We report direct atomic resolution visualization of interatomic layer mixing of transition metal (Ni, Co, Mn) and lithium ions in layer structured oxide cathodes for lithium ion batteries. Using chemical imaging with aberration corrected scanning transmission electron microscope (STEM) and DFT calculations, we discovered that in the layered cathodes, Mn and Co tend to reside almost exclusively at the lattice site of transition metal (TM) layer in the structure or little interlayer mixing with Li. In contrast, Ni shows high degree of interlayer mixing with Li. The fraction of Ni ions reside in the Li layer followed a near linear dependence on total Ni concentration before reaching saturation. The observed distinctively different behavior of Ni with respect to Co and Mn provides new insights on both capacity and voltage fade in this class of cathode materials based on lithium and TM oxides, therefore providing scientific basis for selective tailoring of oxide cathode materials for enhanced performance.

  17. Study of Poly (3,4-ethylenedioxythiophene)/MnO2 as Composite Cathode Materials for Aluminum-Air Battery

    International Nuclear Information System (INIS)

    Kuo, Yu-Lin; Wu, Ching-Chen; Chang, Wen-Sheng; Yang, Ching-Ru; Chou, Hung-Lung

    2015-01-01

    Highlights: • Open-tunnel structure of MnO 2 catalysts were prepared by the hydrothermal method. • PEDOT was deposited on MnO 2 /carbon paper by oxidative chemical vapor deposition. • PEDOT/α-MnO 2 /10AA composite cathode shows the highest discharge performance. • The enhancement on discharge performance was due to the clear charge transfer. - Abstract: This study focuses on the development of the composite electrode materials for an aluminum-air battery and improving the oxygen reduction reaction (ORR) of the air electrode by matching alpha- and beta- manganese dioxide (MnO 2 ) with poly-(3,4-ethylenedioxythiophene) (PEDOT) conducting polymer. The catalyst powders of α-MnO 2 and β-MnO 2 are prepared by hydrothermal method with different precursors, while PEDOT conducting polymer is subsequently deposited on the screen-printed electrodes (MnO 2 /carbon paper) by oxidative chemical vapor deposition (oCVD). Material characteristics of prepared MnO 2 powder and PEDOT layer are investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Raman scattering spectroscopy. The half-cell polarization curve test is found to be strongly depended on the crystalline phases of MnO 2 . From experimental observations and a density functional theory (DFT) study, the conductivity of PEDOT/α-MnO 2 is found to be higher than PEDOT/β-MnO 2 contributed to structural effect mediated improvements in charge transfer. As a result, integrating the deposition of PEDOT on α-MnO 2 /carbon paper as composite cathode is suitable for the use in aluminum-air battery

  18. Vanadium Oxyfluoride/Few-Layer Graphene Composite as a High-Performance Cathode Material for Lithium Batteries.

    Science.gov (United States)

    Cambaz, Musa Ali; Vinayan, B P; Clemens, Oliver; Munnangi, Anji Reddy; Chakravadhanula, Venkata Sai Kiran; Kübel, Christian; Fichtner, Maximilian

    2016-04-18

    Metal oxyfluoride compounds are gathering significant interest as cathode materials for lithium ion batteries at the moment because of their high theoretical capacity and resulting high energy density. In this regard, a new and direct approach is presented to synthesize phase-pure vanadium oxyfluoride (VO2F). The structure of VO2F was identified by Rietveld refinement of the powder X-ray diffraction (XRD) pattern. It crystallizes in a perovskite-type structure with disorder of the oxide and fluoride ions. The as-synthesized VO2F was tested as a cathode material for lithium ion batteries after being surface-coated with few-layer graphene. The VO2F delivered a first discharge capacity of 254 mA h g(-1) and a reversible capacity of 208 mA h g(-1) at a rate of C/20 for the first 20 cycles with an average discharge voltage of 2.84 V, yielding an energy density of 591 W h kg(-1). Improved rate capability that outperforms the previous report has been achieved, showing a discharge capacity of 150 mA h g(-1) for 1 C. The structural changes during lithium insertion and extraction were monitored by ex-situ XRD analysis of the electrodes discharged and charged to various stages. Lithium insertion results in an irreversible structural change of the anion lattice from (3)/4 cubic close packing to hexagonal close packing to accommodate the inserted lithium ions while keeping the overall space-group symmetry. For the first time we have revealed a structural change for the ReO3-type structure of as-prepared VO2F to the RhF3 structure after lithiation/delithiation, with structural changes that have not been observed in previous reports. Furthermore, the new synthetic approach described here would be a platform for the synthesis of new oxyfluoride compounds.

  19. Deposition and characterization of thin films of materials with application in cathodes for lithium rechargeable micro batteries

    International Nuclear Information System (INIS)

    Lopez I, J.

    2007-01-01

    In this thesis work is reported the deposition and characterization of thin films of materials of the type LiMO 2 , with M=Co and Ni, which have application in cathodes for micro-batteries of lithium ions. In the last years some investigators have reported that the electrochemical operation of the lithium ions batteries it can improve recovering the cathode, in bundle form, with some metal oxides as the Al 2 O 3 ; for that the study of the formation of thin films in bilayer form LiMO 2 /AI 2 O 3 is of interest in the development of lithium ions micro batteries. The thin films were deposited using the laser ablation technique studying the effect of some deposit parameters in the properties of the one formed material, as: laser fluence, substrate temperature and working atmosphere, with the purpose of optimizing it. In the case of the LiCoO 2 it was found that to use an inert atmosphere of argon allows to obtain the material with the correct composition. Additionally, with the use of a temperature in the substrate of 150 C is possible to obtain to the material with certain crystallinity grade that to the subjected being to a post-deposit thermal treatment at 300 C for three hours, it gives as result a totally crystalline material. In the case of the thin films of LiNiO 2 , it was necessary to synthesize the oxide starting from a reaction of solid state among nickel oxide (NiO) and lithium oxide (Li 2 O) obtaining stoichiometric LiNiO 2 . For the formation of the thin films of LiNiO 2 it was used an argon atmosphere and the laser fluence was varied, the deposits were carried out to two different substrates temperatures, atmosphere and 160 C. In both cases the material it was recovered with an alumina layer, found that this layer didn't modify the structural properties of the base oxide (LiCoO 2 and LiNiO 2 ). (Author)

  20. Defect Chemistry, Electrical Properties, and Evaluation of New Oxides Sr2 CoNb1-x Tix O6-δ (0≤x≤1) as Cathode Materials for Solid Oxide Fuel Cells.

    Science.gov (United States)

    Azcondo, María Teresa; Yuste, Mercedes; Pérez-Flores, Juan Carlos; Muñoz-Gil, Daniel; García-Martín, Susana; Muñoz-Noval, Alvaro; Orench, Inés Puente; García-Alvarado, Flaviano; Amador, Ulises

    2017-07-21

    The perovskite series Sr 2 CoNb 1-x Ti x O 6-δ (0≤x≤1) was investigated in the full compositional range to assess its potential as cathode material for solid oxide fuel cell (SOFC). The variation of transport properties and thus, the area specific resistances (ASR) are explained by a detailed investigation of the defect chemistry. Increasing the titanium content from x=0-1 produces both oxidation of Co 3+ to Co 4+ (from 0 up to 40 %) and oxygen vacancies (from 6.0 to 5.7 oxygen atom/formula unit), although each charge compensation mechanism predominates in different compositional ranges. Neutron diffraction reveals that samples with high Ti-contents lose a significant amount of oxygen upon heating above 600 K. Oxygen is partially recovered upon cooling as the oxygen release and uptake show noticeably different kinetics. The complex defect chemistry of these compounds, together with the compositional changes upon heating/cooling cycles and atmospheres, produce a complicated behavior of electrical conductivity. Cathodes containing Sr 2 CoTiO 6-δ display low ASR values, 0,13 Ω cm 2 at 973 K, comparable to those of the best compounds reported so far, being a very promising cathode material for SOFC. © 2017 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  1. Electrochemical performance of a rechargeable lithium battery containing a Li Mn{sub 2} O{sub 4} cathode; Desempenho eletroquimico de uma bateria recarregavel de litio com catodo de LiMn{sub 2}O{sub 4}

    Energy Technology Data Exchange (ETDEWEB)

    Amaral, Fabio A.; Ferracin, Luiz C.; Brazuna, Priscila R.; Bocchi, Nerilso [Sao Carlos Univ., SP (Brazil). Dept. de Quimica. Lab. de Pesquisas em Eletroquimica

    1999-07-01

    This paper reports the evaluation of a rechargeable lithium battery, containing a Li Mn{sub 2} O{sub 4} cathode obtained from the {epsilon}-Mn O{sub 2}, through measurements of galvanostatic charge and discharge. The cathode presented a satisfactory electrochemical performance with charge capacity of approximately 110 m A h g{sup -1}. The Teflon electrochemical cell presented satisfactory results only for the initial charge and discharge cycles.

  2. Layered P2-Na 2/3 Co 1/2 Ti 1/2 O 2 as a high-performance cathode material for sodium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Sabi, Noha; Doubaji, Siham; Hashimoto, Kazuki; Komaba, Shinichi; Amine, Khalil; Solhy, Abderrahim; Manoun, Bouchaib; Bilal, Essaid; Saadoune, Ismael

    2017-02-01

    Layered oxides are regarded as promising cathode materials for sodium-ion batteries. We present Na2/3Co1/2Ti1/2O2 as a potential new cathode material for sodium-ion batteries. The crystal features and morphology of the pristine powder were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The cathode material is evaluated in galvanostatic charge-discharge and galvanostatic intermittent titration tests, as well as ex-situ X-ray diffraction analysis. Synthesized by a high-temperature solid state reaction, Na2/3Co1/2Ti1/2O2 crystallizes in P2-type structure with P6(3)/mmc space group. The material presents reversible electrochemical behavior and delivers a specific discharge capacity of 100 mAh g(-1) when tested in Na half cells between 2.0 and 4.2 V (vs. Na+/Na), with capacity retention of 98% after 50 cycles. Furthermore, the electrochemical cycling of this titanium-containing material evidenced a reduction of the potential jumps recorded in the NaxCoO2 parent phase, revealing a positive impact of Ti substitution for Co. The ex-situ XRD measurements confirmed the reversibility and stability of the material. No structural changes were observed in the XRD patterns, and the P2-type structure was stable during the charge/discharge process between 2.0 and 4.2 V vs. Na+/Na. These outcomes will contribute to the progress of developing low cost electrode materials for sodium-ion batteries. (C) 2017 Elsevier B.V. All rights reserved.

  3. Glucose from a cellulose-containing raw material

    Energy Technology Data Exchange (ETDEWEB)

    Feniksova, R V

    1977-01-01

    Glucose was produced by mixing the raw material with an enzyme and water, enzymic hydrolysis of raw material, and separation of the hydrolyzate. To increase the yield of glucose, the hydrolysis took place in 2 stages: at the 1st stage, the hydrolysis was continued until the mixture of glucose and oligosaccharides was obtained under the influence of an active enzyme (1 to 20 units/g of cellulose present in the raw material); at the 2nd stage, cellulase immobilized on an insoluble carrier (by covalent bonds) was used for the hydrolysis of oligosaccharides. The hydromodulus of the suspension of cellulose-containing raw material was maintained 5 to 30. A carrier nonhydrolyzable by cellulase, for instance a homogenious macroporous Aerosil gel, a porous glass, or porous ceramics, was used.

  4. Metallurgically prepared NiCu alloys as cathode materials for hydrogen evolution reaction

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Kunchan; Xia, Ming [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Xiao, Tao [2nd Xiangya Hospital, Central South University, Changsha 410011 (China); Lei, Ting, E-mail: tlei@mail.csu.edu.cn [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China); Yan, Weishan [State Key Laboratory of Powder Metallurgy, Central South University, Changsha 410083 (China)

    2017-01-15

    Ni−Cu bimetallic alloys with Cu content of 5, 10, 20, 30 and 50 wt% are prepared by powder metallurgy method, which consisted of powder mixing, pressing and sintering processes. The X-ray diffraction (XRD) measurement confirms that all the five Ni−Cu alloys possess the f.c.c. structure. The hydrogen evolution reaction (HER) activity of the prepared Ni−Cu alloy electrodes was studied in 6 M KOH solution by cathodic current-potential curves and electrochemical impedance spectroscopy (EIS) techniques. It was found that the electrocatalytic activity for the HER depended on the composition of Ni−Cu alloys, where Ni−10Cu alloy exhibited considerably higher HER activity than Ni plate and other Ni−Cu alloys, indicative of its chemical composition related intrinsic activity. - Highlights: • Ni−Cu alloys with various Cu contents were prepared by powder metallurgy method. • Ni−Cu alloy exhibits chemical composition related synergistic effect for HER activity. • Ni−10Cu alloy electrode presents a most efficient activity for HER. • Two time constants are observed in Nyquist curve and both of them related to the kinetics of HER.

  5. Metallurgically prepared NiCu alloys as cathode materials for hydrogen evolution reaction

    International Nuclear Information System (INIS)

    Wang, Kunchan; Xia, Ming; Xiao, Tao; Lei, Ting; Yan, Weishan

    2017-01-01

    Ni−Cu bimetallic alloys with Cu content of 5, 10, 20, 30 and 50 wt% are prepared by powder metallurgy method, which consisted of powder mixing, pressing and sintering processes. The X-ray diffraction (XRD) measurement confirms that all the five Ni−Cu alloys possess the f.c.c. structure. The hydrogen evolution reaction (HER) activity of the prepared Ni−Cu alloy electrodes was studied in 6 M KOH solution by cathodic current-potential curves and electrochemical impedance spectroscopy (EIS) techniques. It was found that the electrocatalytic activity for the HER depended on the composition of Ni−Cu alloys, where Ni−10Cu alloy exhibited considerably higher HER activity than Ni plate and other Ni−Cu alloys, indicative of its chemical composition related intrinsic activity. - Highlights: • Ni−Cu alloys with various Cu contents were prepared by powder metallurgy method. • Ni−Cu alloy exhibits chemical composition related synergistic effect for HER activity. • Ni−10Cu alloy electrode presents a most efficient activity for HER. • Two time constants are observed in Nyquist curve and both of them related to the kinetics of HER.

  6. Photometric determination of yttrium in zirconium-containing materials

    International Nuclear Information System (INIS)

    Barbina, T.M.; Polezhaev, Yu.M.

    1984-01-01

    Comparative evaluation of the effect of different ways of eliminating the zirconium interfering effect on the results of yttrium photometric determination with arsenazo 2 in artificial mixtures of Y 2 O 3 and ZrO 2 , containing 5 and 10 mol.% Y 2 O 3 , has been carried out. The effect of Zr is eliminated by means of its precipitation by ammonium solution in the form of hydroxide and using camouflaging with 25% sulfosalicylic acid. Both ways do not provide a correct enough result. The use of non-reagent thermohydrolytic Zr precipitation during the analysis of zirconium-containing materials permits to obtain correct and well-reproducible results

  7. Probing the Complexities of Structural Changes in Layered Oxide Cathode Materials for Li-Ion Batteries during Fast Charge-Discharge Cycling and Heating.

    Science.gov (United States)

    Hu, Enyuan; Wang, Xuelong; Yu, Xiqian; Yang, Xiao-Qing

    2018-02-20

    The rechargeable lithium-ion battery (LIB) is the most promising energy storage system to power electric vehicles with high energy density and long cycling life. However, in order to meet customers' demands for fast charging, the power performances of current LIBs need to be improved. From the cathode aspect, layer-structured cathode materials are widely used in today's market and will continue to play important roles in the near future. The high rate capability of layered cathode materials during charging and discharging is critical to the power performance of the whole cell and the thermal stability is closely related to the safety issues. Therefore, the in-depth understanding of structural changes of layered cathode materials during high rate charging/discharging and the thermal stability during heating are essential in developing new materials and improving current materials. Since structural changes take place from the atomic level to the whole electrode level, combination of characterization techniques covering multilength scales is quite important. In many cases, this means using comprehensive tools involving diffraction, spectroscopy, and imaging to differentiate the surface from the bulk and to obtain structural/chemical information with different levels of spatial resolution. For example, hard X-ray spectroscopy can yield the bulk information and soft X-ray spectroscopy can give the surface information; X-ray based imaging techniques can obtain spatial resolution of tens of nanometers, and electron-based microcopy can go to angstroms. In addition to challenges associated with different spatial resolution, the dynamic nature of structural changes during high rate cycling and heating requires characterization tools to have the capability of collecting high quality data in a time-resolved fashion. Thanks to the advancement in synchrotron based techniques and high-resolution electron microscopy, high temporal and spatial resolutions can now be achieved. In

  8. Solution-combustion synthesized aluminium-doped spinel (LiAl(subx)Mn(sub2-x)O(sub4) as a high-performance lithium-ion battery cathode material

    CSIR Research Space (South Africa)

    Kebede, MA

    2015-06-01

    Full Text Available High-performing (LiAl(subx)Mn(sub2-x)O(sub4) (x = 0, 0.125, 0.25, 0.375, and 0.5) spinel cathode materials for lithium-ion battery were developed using a solution combustion method. The as-synthesized cathode materials have spinel cubic structure...

  9. Molten salt-directed synthesis method for LiMn2O4 nanorods as a cathode material for a lithium-ion battery with superior cyclability

    CSIR Research Space (South Africa)

    Kebede, Mesfin A

    2017-02-01

    Full Text Available A molten salt synthesis technique has been used to prepare nanorods of Mn2O3 and single-crystal LiMn2O4 nanorods cathode material with superior capacity retention. The molten salt-directed synthesis involved the use of NaCl as the eutectic melt...

  10. Solid state cathode materials for secondary magnesium-ion batteries that are compatible with magnesium metal anodes in water-free electrolyte

    International Nuclear Information System (INIS)

    Crowe, Adam J.; Bartlett, Bart M.

    2016-01-01

    With high elemental abundance, large volumetric capacity, and dendrite-free metal deposition, magnesium metal anodes offer promise in beyond-lithium-ion batteries. However, the increased charge density associated with the divalent magnesium-ion (Mg 2+ ), relative to lithium-ion (Li + ) hinders the ion-insertion and extraction processes within many materials and structures known for lithium-ion cathodes. As a result, many recent investigations incorporate known amounts of water within the electrolyte to provide temporary solvation of the Mg 2+ , improving diffusion kinetics. Unfortunately with the addition of water, compatibility with magnesium metal anodes disappears due to forming an ion-insulating passivating layer. In this short review, recent advances in solid state cathode materials for rechargeable magnesium-ion batteries are highlighted, with a focus on cathode materials that do not require water contaminated electrolyte solutions for ion insertion and extraction processes. - Graphical abstract: In this short review, we present candidate materials for reversible Mg-battery cathodes that are compatible with magnesium metal in water-free electrolytes. The data suggest that soft, polarizable anions are required for reversible cycling.

  11. Preparation and characterization of electronically conducting polypyrrole-montmorillonite nanocomposite and its potential application as a cathode material for oxygen reduction

    International Nuclear Information System (INIS)

    Rajapakse, R.M.G.; Murakami, Kenji; Bandara, H.M.N.; Rajapakse, R.M.M.Y.; Velauthamurti, K.; Wijeratne, S.

    2010-01-01

    Simple wet chemical processes were deployed to prepare low-cost conducting nanocomposites based on natural clays with 2:1 layered structures such as sodium montmorillonite (MMT). Ce(IV) modified MMT was used for the spontaneous polymerization of pyrrole within clay interlayers. The resulted clay-conducting polypyrrole nanocomposites containing the reduced form of the oxidising agent, have been extensively characterized by X-ray diffraction (XRD) technique for interlayer spacing variations and by Fourier transform infra red (FT-IR) spectroscopy to study the interactions between the clay and polymer functional groups. DC polarization technique with both blocking and non-blocking electrodes was used to distinguish between the ionic and electronic transport numbers and to recognize the type of mobile ionic species. AC impedance analysis further resolved the electrical conduction of these materials. Bulk conductivity analysis implied that the polypyrrole (PPY) formed within Ce(IV) modified MMT posses dominant electronic conductivity. The low-cost, light-weight and stable polymer-clay nanocomposite prepared by Ce(IV) intercalated MMT, [Ce(III)-PPY-MMT], seems to be a promising cathode material for oxygen reduction and hence may find applications in fuel cell industries.

  12. Freeze drying synthesis of Li{sub 3}MnO{sub 4} cathode material for Li-ion batteries: A physico-electrochemical study

    Energy Technology Data Exchange (ETDEWEB)

    Surace, Yuri; Simões, Mário; Karvonen, Lassi; Yoon, Songhak; Pokrant, Simone [Laboratory Materials for Energy Conversion, EMPA – Swiss Federal Laboratories for Materials Science and Technology, Überlandstrasse 129, CH-8600 Dübendorf (Switzerland); Weidenkaff, Anke, E-mail: weidenkaff@imw.uni-stuttgart.de [Materials Chemistry, Institute for Materials Science, University of Stuttgart, Heisenbergstrasse 3, DE-70569 Stuttgart (Germany)

    2015-09-25

    Highlights: • Facilitated synthesis of Li{sub 3}MnO{sub 4} with a smaller thermal budget via freeze drying. • Electrochemical activity enhanced by micro- and nanostructure modifications. • Capacity increase of 30% at 1st discharge versus standard synthesis process. - Abstract: Li{sub 3}MnO{sub 4}, a lithium rich phase containing manganese (V), is a promising cathode material for Li-ion batteries due to its very high theoretical capacity (698 A h kg{sup −1}). Li{sub 3}MnO{sub 4} was synthesized from freeze dried precursors at 398 K. Combined structural, morphological and chemical characterization by XRD, TGA, SEM, TEM and XPS revealed improvements in the micro- and nanostructure in comparison to the material synthesized by a standard solid state chemistry route. The average particle size decreased from 10 μm to 3.5 μm and the average crystallite size from close to 100 nm to around 30 nm. These modifications enhanced the capacity (23% at 10 A kg{sup −1} and up to 31% at 50 A kg{sup −1} with a maximum discharge capacity of 290 A h kg{sup −1}) and the rate capability.

  13. POLYMER COMPOSITES MODIFIED BY WASTE MATERIALS CONTAINING WOOD FIBRES

    Directory of Open Access Journals (Sweden)

    Bernardeta Dębska

    2016-11-01

    Full Text Available In recent years, the idea of sustainable development has become one of the most important require-ments of civilization. Development of sustainable construction involves the need for the introduction of innovative technologies and solutions that will combine beneficial economic effects with taking care of the health and comfort of users, reducing the negative impact of the materials on the environment. Composites obtained from the use of waste materials are part of these assumptions. These include modified epoxy mortar containing waste wood fibres, described in this article. The modification consists in the substitution of sand by crushed waste boards, previously used as underlays for panels, in quantities of 0%, 10%, 20%, 35% and 50% by weight, respectively. Composites containing up to 20% of the modifier which were characterized by low water absorption, and good mechanical properties, also retained them after the process of cyclic freezing and thawing.

  14. Disposal containers for radioactive waste materials and separation systems for radioactive waste materials

    International Nuclear Information System (INIS)

    Rubin, L.S.

    1986-01-01

    A separation system for dewatering radioactive waste materials includes a disposal container, drive structure for receiving the container, and means for releasably attaching the container to the drive structure. The separation structure disposed in the container adjacent the inner surface of the side wall structure retains solids while allowing passage of liquids. The inlet port structure in the container top wall is normally closed by first valve structure that is centrifugally actuated to open the inlet port and the discharge port structure at the container periphery receives liquid that passes through the separation structure and is normally closed by a second valve structure that is centrifugally actuated to open the discharge ports. The container also includes a coupling structure for releasable engagement with the centrifugal drive structure. The centrifugal force produced when the container is driven in rotation by the drive structure opens the valve structures, and radioactive waste material introduced into the container through the open inlet port is dewatered, and the waste is compacted. The ports are automatically closed by the valves when the container drum is not subjected to centrifugal force such that containment effectiveness is enhanced and exposure of personnel to radioactive materials is minimized. (author)

  15. Gamma motes for detection of radioactive materials in shipping containers

    International Nuclear Information System (INIS)

    Harold McHugh; William Quam; Stephan Weeks; Brendan Sever

    2007-01-01

    Shipping containers can be effectively monitored for radiological materials using gamma (and neutron) motes in distributed mesh networks. The mote platform is ideal for collecting data for integration into operational management systems required for efficiently and transparently monitoring international trade. Significant reductions in size and power requirements have been achieved for room-temperature cadmium zinc telluride (CZT) gamma detectors. Miniaturization of radio modules and microcontroller units are paving the way for low-power, deeply-embedded, wireless sensor distributed mesh networks

  16. ERG review of waste package container materials selection and corrosion

    International Nuclear Information System (INIS)

    Moak, D.P.; Perrin, J.S.

    1986-07-01

    The Engineering Review Group (ERG) was established by the Office of Nuclear Waste Isolation (ONWI) to help evaluate engineering-related issues in the US Department of Energy's nuclear waste repository program. The October 1984 meeting of the ERG reviewed the waste package container materials selection and corrosion. This report documents the ERG's comments and recommendations on these subjects and the ONWI response to the specific points raised by the ERG

  17. Functioning Mechanism of AlF 3 Coating on the Li- and Mn-Rich Cathode Materials

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Jianming; Gu, Meng; Xiao, Jie; Polzin, Bryant J.; Yan, Pengfei; Chen, Xilin; Wang, Chongmin; Zhang, Ji-Guang

    2014-11-25

    We report systematic studies of the microstructural changes of uncoated and AlF3-coated Li-rich Mn-rich (LMR) cathode materials (Li1.2Ni0.15Co0.10Mn0.55O2) before and after cycling using a combination of aberration-corrected scanning/transmission electron microscopy (S/TEM) and electron energy loss spectroscopy (EELS). TEM coupled with EELS provides detailed information about the crystallographic and electronic structure changes that occur after cycling, thus revealing the fundamental improvement mechanism of surface coating. The results demonstrate that the surface coating reduces oxidation of the electrolyte at high voltage, suppressing the accumulation of a thick solid electrolyte interface (SEI) layer on electrode particle surface. Surface coating significantly enhances the stability of the surface structure and protects the electrode from severe etching/corrosion by the acidic species in the electrolyte, reducing the formation of etched surfaces and corrosion pits. Moreover, surface coating alleviates the undesirable voltage fade by mitigating layered to spinel-like phase transformation in the bulk region of the material. These fundamental findings may also be widely applied to explain the functioning mechanisms of other surface coatings used in a broad range of electrode materials.

  18. Binder-free cobalt phosphate one-dimensional nanograsses as ultrahigh-performance cathode material for hybrid supercapacitor applications

    Science.gov (United States)

    Sankar, K. Vijaya; Lee, S. C.; Seo, Y.; Ray, C.; Liu, S.; Kundu, A.; Jun, S. C.

    2018-01-01

    One-dimensional (1D) nanostructure exhibits excellent electrochemical performance because of their unique physico-chemical properties like fast electron transfer, good rate capability, and cyclic stability. In the present study, Co3(PO4)2 1D nanograsses are grown on Ni foam using a simple and eco-friendly hydrothermal technique with different reaction times. The open space with uniform nanograsses displays a high areal capacitance, rate capability, energy density, and cyclic stability due to the nanostructure enhancing fast ion and material interactions. Ex-situ microscope images confirm the dependence of structural stability on the reaction time, and the nanograsses promoted ion interaction through material. Further, the reproducibility of the electrochemical performance confirms the binder-free Co3(PO4)2 1D nanograsses to be a suitable high-performance cathode material for application to hybrid supercapacitor. Finally, the assembled hybrid supercapacitor exhibits a high energy density (26.66 Wh kg-1 at 750 W kg-1) and longer lifetimes (80% retained capacitance after 6000 cycles). Our results suggests that the Co3(PO4)2 1D nanograss design have a great promise for application to hybrid supercapacitor.

  19. Lithium-Excess Research of Cathode Material Li2MnTiO4 for Lithium-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Xinyi Zhang

    2015-11-01

    Full Text Available Lithium-excess and nano-sized Li2+xMn1−x/2TiO4 (x = 0, 0.2, 0.4 cathode materials were synthesized via a sol-gel method. The X-ray diffraction (XRD experiments indicate that the obtained main phases of Li2.0MnTiO4 and the lithium-excess materials are monoclinic and cubic, respectively. The scanning electron microscope (SEM images show that the as-prepared particles are well distributed and the primary particles have an average size of about 20–30 nm. The further electrochemical tests reveal that the charge-discharge performance of the material improves remarkably with the lithium content increasing. Particularly, the first discharging capacity at the current of 30 mA g−1 increases from 112.2 mAh g−1 of Li2.0MnTiO4 to 187.5 mAh g−1 of Li2.4Mn0.8TiO4. In addition, the ex situ XRD experiments indicate that the monoclinic Li2MnTiO4 tends to transform to an amorphous state with the extraction of lithium ions, while the cubic Li2MnTiO4 phase shows better structural reversibility and stability.

  20. Carbon Quantum Dot Surface-Engineered VO2 Interwoven Nanowires: A Flexible Cathode Material for Lithium and Sodium Ion Batteries.

    Science.gov (United States)

    Balogun, Muhammad-Sadeeq; Luo, Yang; Lyu, Feiyi; Wang, Fuxin; Yang, Hao; Li, Haibo; Liang, Chaolun; Huang, Miao; Huang, Yongchao; Tong, Yexiang

    2016-04-20

    The use of electrode materials in their powdery form requires binders and conductive additives for the fabrication of the cells, which leads to unsatisfactory energy storage performance. Recently, a new strategy to design flexible, binder-, and additive-free three-dimensional electrodes with nanoscale surface engineering has been exploited in boosting the storage performance of electrode materials. In this paper, we design a new type of free-standing carbon quantum dot coated VO2 interwoven nanowires through a simple fabrication process and demonstrate its potential to be used as cathode material for lithium and sodium ion batteries. The versatile carbon quantum dots that are vastly flexible for surface engineering serve the function of protecting the nanowire surface and play an important role in the diffusion of electrons. Also, the three-dimensional carbon cloth coated with VO2 interwoven nanowires assisted in the diffusion of ions through the inner and the outer surface. With this unique architecture, the carbon quantum dot nanosurface engineered VO2 electrode exhibited capacities of 420 and 328 mAh g(-1) at current density rate of 0.3 C for lithium and sodium storage, respectively. This work serves as a milestone for the potential replacement of lithium ion batteries and next generation postbatteries.

  1. Lithium-Excess Research of Cathode Material Li₂MnTiO₄ for Lithium-Ion Batteries.

    Science.gov (United States)

    Zhang, Xinyi; Yang, Le; Hao, Feng; Chen, Haosen; Yang, Meng; Fang, Daining

    2015-11-20

    Lithium-excess and nano-sized Li 2+x Mn₁ - x /2 TiO₄ ( x = 0, 0.2, 0.4) cathode materials were synthesized via a sol-gel method. The X-ray diffraction (XRD) experiments indicate that the obtained main phases of Li 2.0 MnTiO₄ and the lithium-excess materials are monoclinic and cubic, respectively. The scanning electron microscope (SEM) images show that the as-prepared particles are well distributed and the primary particles have an average size of about 20-30 nm. The further electrochemical tests reveal that the charge-discharge performance of the material improves remarkably with the lithium content increasing. Particularly, the first discharging capacity at the current of 30 mA g -1 increases from 112.2 mAh g -1 of Li 2.0 MnTiO₄ to 187.5 mAh g -1 of Li 2.4 Mn 0.8 TiO₄. In addition, the ex situ XRD experiments indicate that the monoclinic Li₂MnTiO₄ tends to transform to an amorphous state with the extraction of lithium ions, while the cubic Li₂MnTiO₄ phase shows better structural reversibility and stability.

  2. Stowing of packages containing radioactive materials on conveyances

    International Nuclear Information System (INIS)

    Draulans, J.; Lafontaine, I.; Chevalier, G.; Gilles, P.; Jolys, J.C.; Pouard, M.

    1986-04-01

    The Commission of the European Communities has financed some research work carried out jointly by the ''Commissariat a l'Energie Atomique'' and the belgian company ''TRANSNUBEL'', in the field of stowing containers for radioactive materials on trucks. 2 reference type accidents are selected: . a front-end collision against a rigid barrier at an impact speed of 50 km/h . a side-on collision of an impacting vehicle at a speed of 25-35 km/h against a truck loaded with a container. A mathematical model has been developed by means of the CEA Trico code to compute a frontal impact in which the container (1.3 t weight), is stowed by means of 4 tie-down members, each for a nominal load of 2 t. Results indicate the stowing being insufficient and the attachment points too weak to keep the container on the platform. Real tests have been performed to verify these results. Tie-down members and chocks have been defined on the basis of static- and dynamic tests for being used in 8 crash tests. Different containers (low- and high center of gravity) and different ways of stowing have been tried out. An attempt is made to work a code of good practice for stowing, by means of tie-down members and chocks, packages on a truck platform. 19 refs

  3. Synthesis and characterization of Co-doped lanthanum nickelate perovskites for solid oxide fuel cell cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Chavez G, L.; Hinojosa R, M. [Universidad Autonoma de Nuevo Leon, Ciudad Universitaria, San Nicolas de los Garza, 66450 Nuevo Leon (Mexico); Medina L, B.; Ringuede, A.; Cassir, M. [Institut de Recherche de Chimie Paris, CNRS-Chimie ParisTech, 11 rue Pierre et Marie Curie, 75005 Paris (France); Vannier, R. N., E-mail: leonardo.chavezgr@uanl.edu.mx [Unite de Catalyse et de Chimie du Solide, UMR 8181 CNRS, 59655, Villeneuve d Ascq Cedex (France)

    2017-11-01

    In the perovskite structures widely investigated and used as solid oxide fuel cells cathodes, oxygen reduction is mainly limited to the triple phase boundary (TPB), where oxygen (air), electrode and electrolyte are in contact. It is possible via the sol-gel modified Pechini method to: 1) control the material grain size, which can increase TPBs, 2) produce a homogenous material and 3) obtain a cathode material in a faster way compared with the solid state route. LaNi{sub x}Co{sub 1-x}O{sub 3} (x = 0.3, 0.5, 0.7) were synthesized by the modified Pechini method. The perovskite phase formation began at 350 degrees Celsius and the presence of pure LaNi{sub 0.7}Co{sub 0.3}O{sub 3}, LaNi{sub 0.5}Co{sub 0.5}O{sub 3} and LaNi{sub 0.3}Co{sub 0.7}O{sub 3} structures was evidenced by high temperature X-ray diffraction (Ht-XRD) measurements. Scanning electron microscopy (Sem) micrographs showed that the microstructure evolves with the amount of cobalt from a coalesced to an open structure. Electrochemical impedance spectroscopy (EIS) on symmetrical cells LaNi{sub x}Co{sub 1-x}O{sub 3}/YSZ (Yttria-stabilized zirconia)/LaNi{sub x}Co{sub 1-x}O{sub 3} showed that the highest ASR (area specific resistance) is obtained with x = 0.3, whereas ASR values are similar for x = 0.5 and 0.7 at temperatures higher than 600 degrees Celsius. At temperatures lower than 600 degrees Celsius, ASR is the lowest for LaNi{sub 0.5}Co{sub 0.5}O{sub 3}, showing that this composition with intermediate porosity appears as a good choice for and intermediate-temperature solid oxid fuel cell. (Author)

  4. Corrosion of container and infrastructure materials under clay repository conditions

    International Nuclear Information System (INIS)

    Debruyn, W.; Dresselaers, J.; Vermeiren, P.; Kelchtermans, J.; Tas, H.

    1991-01-01

    With regard to the disposal of high-level radioactive waste, it was recommended in a IAEA Technical Committee meeting to perform tests in realistic environments corresponding with normal and accidental conditions, to qualify and apply corrosion monitoring techniques for corrosion evaluation under real repository conditions and to develop corrosion and near-field evolution models. The actual Belgian experimental programme for the qualification of a container for long-term HLW storage in clay formations complies with these recommendations. The emphasis in the programme is indeed on in situ corrosion testing and monitoring and on in situ control of the near-field chemistry. Initial field experiments were performed in a near-surface clay quarry at Terhaegen. Based on a broad laboratory material screening programme and in agreement with the Commission of the European Communities, three reference materials were chosen for extensive in situ overpack testing. Ti/0.2 Pd and Hastelloy C-4 were chosen as reference corrosion resistant materials and a low-carbon steel as corrosion allowance reference material. This report summarizes progress made in the material qualification programme since the CEC contract of 1983-84. 57 Figs.; 15 Tabs.; 18 Refs

  5. Electrochemical characterization of a LiV3O8-polypyrrole composite as a cathode material for lithium ion batteries

    International Nuclear Information System (INIS)

    Tian Fanghua; Liu Li; Yang Zhenhua; Wang Xingyan; Chen Quanqi; Wang Xianyou

    2011-01-01

    Research highlights: → LiV 3 O 8 -PPy composite has been synthesized successfully. → LiV 3 O 8 -PPy composite shows better cycling behavior and rate capability than LiV 3 O 8 . → LiV 3 O 8 -PPy composite shows lower electrochemical resistance than LiV 3 O 8 . - Abstract: LiV 3 O 8 -Polypyrrole (LiV 3 O 8 -PPy) composite has been chemically synthesized by an oxidative polymerization of pyrrole monomer on the surface of LiV 3 O 8 using ferric chloride as oxidizing agent. The electrochemical properties of LiV 3 O 8 -PPy composite were systematically investigated using a variety of electrochemical methods. The LiV 3 O 8 -PPy composite electrode exhibited better cycling behavior and superior rate capability as compared with the bare LiV 3 O 8 electrode. Cyclic voltammetry corroborated the galvanostatic cycling tests, with the composite cathode material showing better reversibility than bare material. Finally, fitting the impedance results to an equivalent circuit indicated that the enhanced electrochemical performances of LiV 3 O 8 -PPy composite resulted from a facilitated kinetics of interfacial charge transfer in the presence of PPy.

  6. A high-capacity, low-cost layered sodium manganese oxide material as cathode for sodium-ion batteries.

    Science.gov (United States)

    Guo, Shaohua; Yu, Haijun; Jian, Zelang; Liu, Pan; Zhu, Yanbei; Guo, Xianwei; Chen, Mingwei; Ishida, Masayoshi; Zhou, Haoshen

    2014-08-01

    A layered sodium manganese oxide material (NaMn3 O5 ) is introduced as a novel cathode materials for sodium-ion batteries. Structural characterizations reveal a typical Birnessite structure with lamellar stacking of the synthetic nanosheets. Electrochemical tests reveal a particularly large discharge capacity of 219 mAh g(-1) in the voltage rang of 1.5-4.7 V vs. Na/Na(+) . With an average potential of 2.75 V versus sodium metal, layered NaMn3 O5 exhibits a high energy density of 602 Wh kg(-1) , and also presents good rate capability. Furthermore, the diffusion coefficient of sodium ions in the layered NaMn3 O5 electrode is investigated by using the galvanostatic intermittent titration technique. The results greatly contribute to the development of room-temperature sodium-ion batteries based on earth-abundant elements. © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  7. Synthesis of novel high-voltage cathode material LiCoPO4 via rheological phase method

    International Nuclear Information System (INIS)

    Tan, Long; Luo, Zhimei; Liu, Haowen; Yu, Ying

    2010-01-01

    For the first time, rheological phase method, a simple and effective route, is applied to synthesize novel cathode material LiCoPO 4 . X-ray diffraction spectrometer (XRD), X-ray photoelectron spectrometer (XPS), transmission electron microscope (TEM) and electrochemical impedance spectroscopy (EIS) are taken to investigate this material, respectively. XRD figure shows that the rheological sample is better crystallized than the solid-state one. XPS result of the rheological sample exhibits that the valence of Co is 2+. TEM images show that better dispersed particles with smaller size can be formed by rheological method comparing to the solid-state route. Charge-discharge test is carried out in the range of 3.0-5.0 V at 0.2 mA cm -2 . The initial discharge capacity for rheological phase and solid-state powder is 71.5 and 30.9 mAh g -1 , respectively. The better electrochemical property should be ascribed to the better crystallized rheological phase production with better dispersed and smaller particles, which can greatly facilitate the diffusion of Li + .

  8. Long-term cyclability of LiFePO4/carbon composite cathode material for lithium-ion battery applications

    International Nuclear Information System (INIS)

    Liu Jing; Wang Jiawei; Yan Xuedong; Zhang Xianfa; Yang Guiling; Jalbout, Abraham F.; Wang Rongshun

    2009-01-01

    A simple high-energy ball milling combined with spray-drying method has been developed to synthesize LiFePO 4 /carbon composite. This material delivers an improved tap density of 1.3 g/cm 3 and a high electronic conductivity of 10 -2 to 10 -3 S/cm. The electrochemical performance, which is especially notable for its high-rate performance, is excellent. The discharge capacities are as high as 109 mAh/g at the current density of 1100 mA/g (about 6.5C rate) and 94 mAh/g at the current density of 1900 mA/g (about 11C rate). At the high current density of 1700 mA/g (10C rate), it exhibits a long-term cyclability, retaining over 92% of its original discharge capacity beyond 2400 cycles. Therefore, the as-prepared LiFePO 4 /carbon composite cathode material is capable of such large-scale applications as hybrid and plug-in hybrid electric vehicles.

  9. A porous C/LiFePO4/multiwalled carbon nanotubes cathode material for Lithium ion batteries

    International Nuclear Information System (INIS)

    Qin, Guohui; Ma, Qianqian; Wang, Chengyang

    2014-01-01

    Highlights: •C/LiFePO 4 /MWCNT was synthesized by a incorporation of sol-gel approach and an electro-polymerization progress with a subsequent carbonization progress. •The prepared C/LiFePO 4 /MWCNTs electrode presents high-rate ability, cyclic stability, and a relative volume density. •Such cathode material is an alternative candidate for high power lithium ion batteries. -- Abstract: Three dimensional (3D) porous C/LiFePO 4 /MWCNTs was synthesized by a hybrid of in situ sol gel strategy and a facile electro-polymerization polyaniline technique and a simultaneous sintering progress. In combined with the 3D hierarchical pore topologies and high electronic conduction facilitating the kinetics of both electron transport and lithium ion diffusion within the particles, the optimized electrodes exhibit an ultrahigh rate capacity, stable charge/discharge cycle ability, and a comparative volume capacity. The synthesized LiFePO 4 composite offers a discharge capacity of 169.6mAhg −1 (nearly to its the theoretical capability 170mAhg −1 ) at the C/10 rate and delivers a good rate performance with a capacity of 141.9mAh g −1 at a high rate of 20 C, and stable charge/discharge cycle ability (>95% capacity retention after 200 charge/discharge cycles).This non-organic facile synthesize avenue can be high desirable to prepare high-power electrode materials

  10. Li{sub 2}MnSiO{sub 4} as a potential Li-battery cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Dominko, R.; Bele, M.; Gaberscek, M.; Jamnik, J. [National Institute of Chemistry, P.O.B. 660, SI-1001 Ljubljana (Slovenia); Kokalj, A. [Institute Jozef Stefan, Jamova 39, SI-1000 Ljubljana (Slovenia)

    2007-12-06

    Recently we synthesized and preliminary characterized a new material for potential use in Li-battery cathodes: Li{sub 2}MnSiO{sub 4}. Although its theoretical capacity is about 330 mAh g{sup -1}, the actual measurements showed a much smaller value (about 120 mAh g{sup -1}). One of the reasons for the poor performance could be the poor electronic conductivity (<10{sup -14} S cm{sup -1} at RT) causing a huge polarization during charge-discharge. However, in the present paper we show that reducing the particle size down to the range of 20-50 nm and additional particle embedment into a carbon phase does not significantly improve the electrochemistry of Li{sub 2}MnSiO{sub 4}. Observations of structural changes during the first charge shows a complete loss of peaks when reaching the nominal composition of ca. Li{sub 1}MnSiO{sub 4}. The peaks are not recovered during subsequent cycling. It is supposed that extraction of Li causes significant structural changes so that the resulting material is only able to reversibly exchange a limited amount of Li. (author)

  11. Ca3Co4O9+δ, a growing potential SOFC cathode material: impact of the layer composition and thickness on the electrochemical properties

    NARCIS (Netherlands)

    Rolle, A.; Abbas, H.A.A.; Huo, D.; Capoen, E.; Mentré, O.; Vannier, R.N.; Daviero-Minaud, S.; Boukamp, Bernard A.

    2016-01-01

    The thermoelectric material Ca3Co4O9 + δ (CCO), with an electronic conductivity of σe = 240 S·cm− 1 at 650 °C and a good chemical and mechanical compatibility with the standard Ce0.9Gd0.1O1.95 electrolyte (CGO, TEC: 9–10 · 10− 6 K− 1), was recently identified as a potential cathode material for

  12. Electrochemical performance of co-doped Li1.2Mn0.6Ni0.2O2 cathode materials

    CSIR Research Space (South Africa)

    David, K

    2013-04-01

    Full Text Available The composite material has a xLi2MnO3·(1-x)LiMO2 (M = Mn, Co, Ni) structure has been considered as one of the most promising cathode materials for advanced lithium-ion batteries due to their low-cost and high capacity (> 200 mAh g−1) between 4.8 V...

  13. Corrosion of candidate container materials by Yucca Mountain bacteria

    International Nuclear Information System (INIS)

    Horn, J; Jones, D; Lian, T; Martin, S; Rivera, A

    1999-01-01

    Several candidate container materials have been studied in modified Yucca Mountain (YM) ground water in the presence or absence of YM bacteria. YM bacteria increased corrosion rates by 5-6 fold in UNS G10200 carbon steel, and nearly 100-fold in UNS NO4400 Ni-Cu alloy. YM bacteria caused microbiologically influenced corrosion (MIC) through de-alloying or Ni-depletion of Ni-Cu alloy as evidenced by scanning electronic microscopy (SEM) and inductively coupled plasma spectroscopy (ICP) analysis. MIC rates of more corrosion-resistant alloys such as UNS NO6022 Ni-Cr- MO-W alloy, UN's NO6625 Ni-Cr-Mo alloy, and UNS S30400 stainless steel were measured below 0.05 umyr, however YM bacteria affected depletion of Cr and Fe relative to Ni in these materials. The chemical change on the metal surface caused by depletion was characterized in anodic polarization behavior. The anodic polarization behavior of depleted Ni-based alloys was similar to that of pure Ni. Key words: MIC, container materials, YM bacteria, de-alloying, Ni-depletion, Cr-depletion, polarization resistance, anodic polarization,

  14. Container materials in environments of corroded spent nuclear fuel

    Science.gov (United States)

    Huang, F. H.

    1996-07-01

    Efforts to remove corroded uranium metal fuel from the K Basins wet storage to long-term dry storage are underway. The multi-canister overpack (MCO) is used to load spent nuclear fuel for vacuum drying, staging, and hot conditioning; it will be used for interim dry storage until final disposition options are developed. Drying and conditioning of the corroded fuel will minimize the possibility of gas pressurization and runaway oxidation. During all phases of operations the MCO is subjected to radiation, temperature and pressure excursions, hydrogen, potential pyrophoric hazard, and corrosive environments. Material selection for the MCO applications is clearly vital for safe and efficient long-term interim storage. Austenitic stainless steels (SS) such as 304L SS or 316L SS appear to be suitable for the MCO. Of the two, Type 304L SS is recommended because it possesses good resistance to chemical corrosion, hydrogen embrittlement, and radiation-induced corrosive species. In addition, the material has adequate strength and ductility to withstand pressure and impact loading so that the containment boundary of the container is maintained under accident conditions without releasing radioactive materials.

  15. Processing Uranium-Bearing Materials Containing Coal and Loam

    Energy Technology Data Exchange (ETDEWEB)

    Civin, V; Prochazka, J [Research and Development Laboratory No. 3 of the Uranium Industry, Prague, Czechoslovakia (Czech Republic)

    1967-06-15

    Among the ores which are classified as low-grade in the CSSR are mixtures of coal and bentonitic loam of tertiary origin, containing approximately 0.1% U and with a moisture content at times well above 20-30%. The uranium is held mainly by the carbonaceous component. Conventional processing of these materials presents various difficulties which are not easily overcome. During leaching the pulp thickens and frequently becomes pasty, due to the presence of montmorillonites. Further complications arise from the high sorption capacity of the materials (again primarily due to montmorillonites) and poor sedimentation of the viscous pulps. In addition, the materials are highly refractory to the leaching agents. The paper presents experience gained in solving the problems of processing these ores. The following basic routes were explored: (1) separation of the carbonaceous and loamy components: The organic component appears to be the main activity carrier. Processing the concentrated material upon separation of the inactive or less active loam may not only remove the thixotropic behaviour but also substantially reduce the cost of the ore treatment; (2) 'liquifying' the pulps or preventing the thickening of the pulp by addition of suitable agents; (3) joint acid or carbonate processing of the materials in question with current ore types; (4) removal or suppression of thixotropic behaviour by thermal pretreatment of the material; and (5) application of the 'acid cure' method. The first method appears to be the most effective, but it presents considerable difficulties due to the extreme dispersion of the carbonaceous phase and further research is being carried out. Methods 2 and 3 proved to be unacceptable. Method 4, which includes roasting at 300-400{sup o}C, is now being operated on an industrial scale. The final method has also shown definite advantages for particular deposits of high montmorillonite content material. (author)

  16. Reversible multi-electron redox chemistry of π-conjugated N-containing heteroaromatic molecule-based organic cathodes

    Science.gov (United States)

    Peng, Chengxin; Ning, Guo-Hong; Su, Jie; Zhong, Guiming; Tang, Wei; Tian, Bingbing; Su, Chenliang; Yu, Dingyi; Zu, Lianhai; Yang, Jinhu; Ng, Man-Fai; Hu, Yong-Sheng; Yang, Yong; Armand, Michel; Loh, Kian Ping

    2017-07-01

    Even though organic molecules with well-designed functional groups can be programmed to have high electron density per unit mass, their poor electrical conductivity and low cycle stability limit their applications in batteries. Here we report a facile synthesis of π-conjugated quinoxaline-based heteroaromatic molecules (3Q) by condensation of cyclic carbonyl molecules with o-phenylenediamine. 3Q features a number of electron-deficient pyrazine sites, where multiple redox reactions take place. When hybridized with graphene and coupled with an ether-based electrolyte, an organic cathode based on 3Q molecules displays a discharge capacity of 395 mAh g-1 at 400 mA g-1 (1C) in the voltage range of 1.2-3.9 V and a nearly 70% capacity retention after 10,000 cycles at 8 A g-1. It also exhibits a capacity of 222 mAh g-1 at 20C, which corresponds to 60% of the initial specific capacity. Our results offer evidence that heteroaromatic molecules with multiple redox sites are promising in developing high-energy-density, long-cycle-life organic rechargeable batteries.

  17. Contained scanning electron microscope facility for examining radioactive materials

    International Nuclear Information System (INIS)

    Hsu, C.W.

    1986-03-01

    At the Savannah River Laboratory (SRL) radioactive solids are characterized with a scanning electron microscope (SEM) contained in a glove box. The system includes a research-grade Cambridge S-250 SEM, a Tracor Northern TN-5500 x-ray and image analyzer, and a Microspec wavelength-dispersive x-ray analyzer. The containment facility has a glove box train for mounting and coating samples, and for housing the SEM column, x-ray detectors, and vacuum pumps. The control consoles of the instruments are located outside the glove boxes. This facility has been actively used since October 1983 for high alpha-activity materials such as plutonium metal and plutonium oxide powders. Radioactive defense waste glasses and contaminated equipment have also been examined. During this period the facility had no safety-related incidents, and personnel radiation exposures were maintained at less than 100 mrems

  18. Band structure analysis on olivine LiMPO4 and delithiated MPO4 (M = Fe, Mn) cathode materials

    International Nuclear Information System (INIS)

    Yi, Ting-Feng; Fang, Zi-Kui; Xie, Ying; Zhu, Yan-Rong; Dai, Changsong

    2014-01-01

    Highlights: • The conductivity of Li x MPO 4 were discussed relying on first principles technique. • Relationship between structure properties and microscopic bonding was addressed. • A mechanism responsible for the structural instability of MnPO 4 was proposed. - Abstract: Olivine compounds, i.e. Li x MPO 4 (M = Fe, Mn), are now regarded as the most competitive positive-electrode materials for future applications of large-scale rechargeable lithium batteries. There are significant interests in their electronic structures, because the microscopic information is very important for elucidating the structural stability, electrochemical performance, and electronic conductivity issues of batteries for high-rate applications. The structure stabilities of LiMPO 4 and MPO 4 (M = Fe, Mn) cathode materials are analyzed according to first principles calculations. The result shows that LiMPO 4 (M = Fe, Mn) materials exhibit good structure stability, which is mainly contributed to the extremely strong P-O covalent bonds. Furthermore, the introduction of P ions is also helpful for the chemical potential decrease of the materials. The band structure analysis reveals that the electronic conductance of LiFePO 4 , LiMnPO 4 , and FePO 4 is poor, while MnPO 4 possesses half metallic property. According to the electron distribution, it can be confirmed that Mn-O(II) bonds are weakened after Li + extractions, which is different from the variation trend of Fe-O(II) bonds. The decrease of Mn-O(II) bond strength is thus favorable for the phase transformation observed in experiments

  19. Vanadyl phosphates as high energy density cathode materials for rechargeable sodium battery

    Science.gov (United States)

    Zhang, Ruigang; Mizuno, Fuminori; Ling, Chen; Whittingham, Stanley M.; Zhang, Ruibo; Chen, Zehua

    2017-08-01

    A positive electrode comprising .epsilon.-VOPO.sub.4 and/or Na.sub.x(.epsilon.-VOPO.sub.4) wherein x is a value from 0.1 to 1.0 as an active ingredient, wherein the electrode is capable of insertion and release of sodium ions and a reversible sodium battery containing the positive electrode are provided.

  20. Shipping container for a bottle of radioactive material

    International Nuclear Information System (INIS)

    Soldan, D.W.

    1975-01-01

    A shipping container for a bottle of radioactive material comprises a can having a cavity therein for receiving the bottle, a screw cap for the can and the cavity, and an annular bottle retainer extending downwardly in the cavity from its upper end having an outwardly extending flange at its upper end clamped between the cap and the upper end of the cavity and an inwardly extending flange at its lower end receiving the neck of the bottle. The cap carries a sponge to absorb spillage from the bottle. (U.S.)

  1. Towards deriving Ni-rich cathode and oxide-based anode materials from hydroxides by sharing a facile co-precipitation method.

    Science.gov (United States)

    Qiu, Haifa; Du, Tengfei; Wu, Junfeng; Wang, Yonglong; Liu, Jian; Ye, Shihai; Liu, Sheng

    2018-05-22

    Although intensive studies have been conducted on layered transition metal oxide(TMO)-based cathode materials and metal oxide-based anode materials for Li-ion batteries, their precursors generally follow different or even complex synthesis routes. To share one route for preparing precursors of the cathode and anode materials, herein, we demonstrate a facile co-precipitation method to fabricate Ni-rich hydroxide precursors of Ni0.8Co0.1Mn0.1(OH)2. Ni-rich layered oxide of LiNi0.8Co0.1Mn0.1O2 is obtained by lithiation of the precursor in air. An NiO-based anode material is prepared by calcining the precursor or multi-walled carbon nanotubes (MWCNTs) incorporated precursors. The pre-addition of ammonia solution can simplify the co-precipitation procedures and the use of an air atmosphere can also make the heat treatment facile. LiNi0.8Co0.1Mn0.1O2 as the cathode material delivers a reversible capacity of 194 mA h g-1 at 40 mA g-1 and a notable cycling retention of 88.8% after 100 cycles at 200 mA g-1. This noticeable performance of the cathode arises from a decent particle morphology and high crystallinity of the layered oxides. As the anode material, the MWCNTs-incorporated oxides deliver a much higher reversible capacity of 811.1 mA h g-1 after 200 cycles compared to the pristine oxides without MWCNTs. The improvement on electrochemical performance can be attributed to synergistic effects from MWCNTs incorporation, including reinforced electronic conductivity, rich meso-pores and an alleviated volume effect. This facile and sharing method may offer an integrated and economical approach for commercial production of Ni-rich electrode materials for Li-ion batteries.

  2. Radioactive material dry-storage facility and radioactive material containing method

    International Nuclear Information System (INIS)

    Kanai, Hidetoshi; Kumagaya, Naomi; Ganda, Takao.

    1997-01-01

    The present invention provides a radioactive material dry storage facility which can unify the cooling efficiency of a containing tube and lower the pressure loss in a storage chamber. Namely, a cylindrical body surrounds a first containing tube situated on the side of an air discharge portion among a plurality of containing tubes and forms an annular channel extending axially between the cylindrical body and the first containing tube. An air flow channel partitioning member is disposed below a second containing tube situated closer to an air charging portion than the first containing tube. A first air flow channel is formed below the air channel partitioning member extending from the air charging portion to the annular channel. The second air channel is formed above the air channel partitioning member and extends from the air charging portion to the air discharge portion by way of a portion between the second containing tubes and the portion between the cylindrical body and the first containing tube. Then, low temperature air can be led from the air charging portion to the periphery of the first containing tube. The effect of cooling the first containing tube can be enhanced. The difference between the cooling efficiency between the second containing tube and the first containing tube is decreased. (I.S.)

  3. Characterization and electrochemical properties of high tap-density LiFePO4/C cathode materials by a combination of carbothermal reduction and molten salt methods

    International Nuclear Information System (INIS)

    Fey, George Ting-Kuo; Lin, Yi-Chuan; Kao, Hsien-Ming

    2012-01-01

    Olivine-structured LiFePO 4 cathode materials were prepared via a combination of carbothermal reduction (CR) and molten salt (MS) methods. To enhance the powder's tap density, the LiFePO 4 /C composite was pressed into pellets and then sintered for at least 1 h at 1028 K in the reaction environment of KCl molten salts. The use of molten salt can effectively influence unit cell volume, morphology and tap density of particles, and consequently change the electrochemical performance of LiFePO 4 /C. The composites were characterized in detail by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), dynamic light scattering (DLS), Raman spectroscopy and tap density testing. The final product with high tap density of 1.50 g cm −3 contains 4.58 wt% carbon and exhibits good discharge capacity of 141 mAh g −1 at a 0.2 C-rate in the potential range of 2.8–4.0 V.

  4. Modification of clay-based waste containment materials

    International Nuclear Information System (INIS)

    Adu-Wusu, K.; Whang, J.M.; McDevitt, M.F.

    1997-01-01

    Bentonite clays are used extensively for waste containment barriers to help impede the flow of water in the subsurface because of their low permeability characteristics. However, they do little to prevent diffusion of contaminants, which is the major transport mechanism at low water flows. A more effective way of minimizing contaminant migration in the subsurface is to modify the bentonite clay with highly sorptive materials. Batch sorption studies were conducted to evaluate the sorptive capabilities of organo-clays and humic- and iron-based materials. These materials proved to be effective sorbents for the organic contaminants 1,2,4-trichlorobenzene, nitrobenzene, and aniline in water, humic acid, and methanol solution media. The sorption capacities were several orders of magnitude greater than that of unmodified bentonite clay. Modeling results indicate that with small amounts of these materials used as additives in clay barriers, contaminant flux through walls could be kept very small for 100 years or more. The cost of such levels of additives can be small compared to overall construction costs

  5. Performance of Cement Containing Laterite as Supplementary Cementing Material

    Directory of Open Access Journals (Sweden)

    Abbas Bukhari, Z. S.

    2013-03-01

    Full Text Available The utilization of different industrial waste, by-products or other materials such as ground granulated blast furnace slag, silica fume, fly ash, limestone, and kiln dust, etc. as supplemen- tary cementing materials has received considerable attention in recent years. A study has been conducted to look into the performance of laterite as Supplementary Cementing Materials (SCM. The study focuses on compressive strength performance of blended cement containing different percentage of laterite. The cement is replaced accordingly with percentage of 2 %, 5 %, 7 % and 10 % by weight. In addition, the effect of use of three chemically different laterites have been studied on physical performance of cement as in setting time, Le-Chatlier expansion, loss on ignition, insoluble residue, free lime and specifically compressive strength of cement cubes tested at the age of 3, 7, and 28 days. The results show that the strength of cement blended with laterite as SCM is enhanced. Key words: Portland cement, supplementary cementing materials (SCM, laterite, compressive strength KUI – 6/2013 Received January 4, 2012 Accepted February 11, 2013

  6. Synthesis of Nanoscale Lithium-Ion Battery Cathode Materials Using a Porous Polymer Precursor Method

    KAUST Repository

    Deshazer, H.D.; Mantia, F. La; Wessells, C.; Huggins, R.A.; Cui, Y.

    2011-01-01

    (NiMnCo)1/3O2, which are used in the positive electrodes of lithium-ion batteries, are shown. Experiments have demonstrated that materials made using this method can have electrochemical properties comparable to those typically produced by more elaborate

  7. Silver-coated LiVPO4F composite with improved electrochemical performance as cathode material for lithium-ion batteries

    Science.gov (United States)

    Yang, Bo; Yang, Lin

    2015-12-01

    Nano-structured LiVPO4F/Ag composite cathode material has been successfully synthesized via a sol-gel route. The structural and physical properties, as well as the electrochemical performance of the material are compared with those of the pristine LiVPO4F. X-ray diffraction (XRD) and scanning electron microscopy (SEM) reveal that Ag particles are uniformly dispersed on the surface of LiVPO4F without destroying the crystal structure of the bulk material. An analysis of the electrochemical measurements show that the Ag-modified LiVPO4F material exhibits high discharge capacity, good cycle performance (108.5 mAh g-1 after 50th cycles at 0.1 C, 93% of initial discharge capacity) and excellent rate behavior (81.8 mAh g-1 for initial discharge capacity at 5 C). The electrochemical impedance spectroscopy (EIS) results reveal that the adding of Ag decreases the charge-transfer resistance (Rct) of LiVPO4F cathode. This study demonstrates that Ag-coating is a promising way to improve the electrochemical performance of the pristine LiVPO4F for lithium-ion batteries cathode material.

  8. Enhanced electrochemical performance of Ti substituted P2-Na2/3Ni1/4Mn3/4O2 cathode material for sodium ion batteries

    International Nuclear Information System (INIS)

    Zhao, Wenwen; Tanaka, Akinobu; Momosaki, Kyoko; Yamamoto, Shinji; Zhang, Fabi; Guo, Qixin; Noguchi, Hideyuki

    2015-01-01

    Highlights: • Ti substituted P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 cathode was synthesized. • Structural and electrochemical properties of Na 2/3 Ni 1/4 Ti x Mn 3/4-x O 2 were studied. • Ti substituted cathodes exhibit enhanced cycleability and rate performance. • Ti substitution has impact on stabilizing the P2 structure during cycling. -- Abstract: Ti substituted P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 cathode material with the composition of Na 2/3 Ni 1/4 Ti x Mn 3/4-x O 2 has been synthesized by solid state method. The influence of Ti substitution for Mn on the structure, morphology and electrochemical performances of P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 has been investigated. X-ray diffraction (XRD) results of Ti substituted sample show that they exhibit same diffraction patterns as those of pristine P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 . Progressive change in the lattice parameters of Ti substituted samples suggests that Mn was successfully substituted by Ti. In contrast to P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 which shows step-type voltage profiles, Ti substituted samples show sloping voltage profiles. Drastic capacity fade occurred for P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 cathode, while Ti substituted cathodes still show high capacity retention over 92% after 25 cycles at the voltage range of 2.0-4.3 V. Even cycled at high upper cut-off voltage of 4.5 V, Ti=0.20 sample can deliver a reversible capacity of 140 mAhg −1 with the capacity retention over 92% after 25 cycles. Furthermore, Ti substituted cathodes exhibit enhanced rate capability over pristine P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 cathode. Comparison of the Ex-situ XRD results of the cycled P2-Na 2/3 Ni 1/4 Mn 3/4 O 2 and its substituted samples provides evidence that the improved electrochemical performance of Ti substituted cathodes would be attributed to the stabilization of the structure with Ti substitution

  9. Recent Development of Graphene-Based Cathode Materials for Dye-Sensitized Solar Cells

    Directory of Open Access Journals (Sweden)

    Man-Ning Lu

    2016-01-01

    Full Text Available Dye-sensitized solar cells (DSSCs have attracted extensive attention for serving as potential low-cost alternatives to silicon-based solar cells. As a vital role of a typical DSSC, the counter electrode (CE is generally employed to collect electrons via the external circuit and speed up the reduction reaction of I3- to I- in the redox electrolyte. The noble Pt is usually deposited on a conductive glass substrate as CE material due to its excellent electrical conductivity, electrocatalytic activity, and electrochemical stability. To achieve cost-efficient DSSCs, reasonable efforts have been made to explore Pt-free alternatives. Recently, the graphene-based CEs have been intensively investigated to replace the high-cost noble Pt CE. In this paper, we provided an overview of studies on the electrochemical and photovoltaic characteristics of graphene-based CEs, including graphene, graphene/Pt, graphene/carbon materials, graphene/conducting polymers, and graphene/inorganic compounds. We also summarize the design and advantages of each graphene-based material and provide the possible directions for designing new graphene-based catalysts in future research for high-performance and low-cost DSSCs.

  10. Three-dimensional interconnected cobalt oxide-carbon hollow spheres arrays as cathode materials for hybrid batteries

    Directory of Open Access Journals (Sweden)

    Jiye Zhan

    2016-06-01

    Full Text Available Hierarchical porous metal oxides arrays is critical for development of advanced energy storage devices. Herein, we report a facile template-assisted electro-deposition plus glucose decomposition method for synthesis of multilayer CoO/C hollow spheres arrays. The CoO/C arrays consist of multilayer interconnected hollow composite spheres with diameters of ∼350 nm as well as thin walls of ∼20 nm. Hierarchical hollow spheres architecture with 3D porous networks are achieved. As cathode of high-rate hybrid batteries, the multilayer CoO/C hollow sphere arrays exhibit impressive enhanced performances with a high capacity (73.5 mAh g−1 at 2 A g−1, and stable high-rate cycling life (70 mAh g−1 after 12,500 cycles at 2 A g−1. The improved electrochemical performance is owing to the composite hollow-sphere architecture with high contact area between the active materials and electrolyte as well as fast ion/electron transportation path.

  11. Vanadium Pentoxide-Based Composite Synthesized Using Microwave Water Plasma for Cathode Material in Rechargeable Magnesium Batteries

    Directory of Open Access Journals (Sweden)

    Tatsuhiko Yajima

    2013-10-01

    Full Text Available Multivalent cation rechargeable batteries are expected to perform well as high-capacity storage devices. Rechargeable magnesium batteries have an advantage in terms of resource utilization and safety. Here, we report on sulfur-doped vanadium pentoxide (S-V2O5 as a potential material for the cathodes of such a battery; S-V2O5 showed a specific capacity of 300 mAh·g−1. S-V2O5 was prepared by a method using a low-temperature plasma generated by carbon felt and a 2.45 GHz microwave generator. This study investigates the ability of S-V2O5 to achieve high capacity when added to metal oxide. The highest recorded capacity (420 mAh·g−1 was reached with MnO2 added to composite SMn-V2O5, which has a higher proportion of included sulfur than found in S-V2O5. Results from transmission electron microscopy, energy-dispersive X-ray spectroscopy, Micro-Raman spectroscopy, and X-ray photoelectron spectroscopy show that the bulk of the SMn-V2O5 was the orthorhombic V2O5 structure; the surface was a xerogel-like V2O5 and a solid solution of MnO2 and sulfur.

  12. Synthesis and Electrochemical Properties of Fe-doped V6O13 as Cathode Material for Lithium-ion Battery

    Directory of Open Access Journals (Sweden)

    YUAN Qi

    2018-01-01

    Full Text Available Fe-doped V6O13 was synthesized via a facile hydrothermal method after preparing precursor in order to improve the discharge capacity and cycle performance of V6O13 cathode material at high-lithium state. XRD, SEM and XPS were employed to characterize the phase, morphology and valence of the Fe-doped V6O13. Meanwhile, the electrochemical performance was analyzed and researched. Different morphologies and electrochemical performances of Fe-doped V6O13 were obtained via doping different contents of Fe3+ ion. The sample 0.02 presented the largest thickness of nanosheets (the thickness of 600-900nm and clearance between layers. The Fe-doped V6O13 has a better electrochemical performance than that of pure V6O13. The sample 0.02 exhibits the best electrochemical performance, the initial discharge specific capacity is 433mAh·g-1 and the capacity retention is 47.1% after 100 cycles.

  13. Synthesis and characterization of LiFePo4/C cathode material by freeze drying method with PVP

    Directory of Open Access Journals (Sweden)

    Kuzmanović Maja D.

    2014-01-01

    Full Text Available Lithium iron phosphate is a promising cathode material for lithium ion battery application thanks to its good characteristics. Here is presented the freeze drying method for the preparation of carbon coated LiFePO4, where PVP is used as a carbon source. The main advantage of this method is mixing at the atomic level and introducing the carbon source into the precursor solution. The synthesis process can be divided into three stages: freezing of a precursor solution, drying under vacuum until water evaporates and calicination of as-dried powder at slightly reductive atmosphere. Powder X-ray diffraction measurement demonstrated single phase LiFePO4 with crystallite size of 45.8 nm. Morphology and particle size was revealed with scanning electron microscopy and particle size analyzer. Galvanostatic cycling from 2.3 to 4.1 V vs. Li/Li+, shows typical LiFePO4 redox behavior with plateau at 3.4 V. The discharge capacity value obtained at C/10 rate was 154 mAh- 1, with decrease on greater C-rates.

  14. Three-dimensional graphene/LiFePO4 nanostructures as cathode materials for flexible lithium-ion batteries

    International Nuclear Information System (INIS)

    Ding, Y.H.; Ren, H.M.; Huang, Y.Y.; Chang, F.H.; Zhang, P.

    2013-01-01

    Graphical abstract: Graphene/LiFePO 4 composites as a high-performance cathode material for flexible lithium-ion batteries have been prepared by using a co-precipitation method to synthesize graphene/LiFePO4 powders as precursors and then followed by a solvent evaporation process. - Highlights: • Flexible LiFePO 4 /graphene films were prepared first time by a solvent evaporation process. • The flexible electrode exhibited a high discharge capacity without conductive additives. • Graphene network offers the electrode adequate strength to withstand repeated flexing. - Abstract: Three-dimensional graphene/LiFePO 4 nanostructures for flexible lithium-ion batteries were successfully prepared by solvent evaporation method. Structural characteristics of flexible electrodes were investigated by X-ray diffraction (XRD), atomic force microscopy (AFM) and scanning electron microscopy (SEM). Electrochemical performance of graphene/LiFePO 4 was examined by a variety of electrochemical testing techniques. The graphene/LiFePO 4 nanostructures showed high electrochemical properties and significant flexibility. The composites with low graphene content exhibited a high capacity of 163.7 mAh g −1 at 0.1 C and 114 mAh g −1 at 5 C without further incorporation of conductive agents

  15. Detecting nuclear materials smuggling: performance evaluation of container inspection policies.

    Science.gov (United States)

    Gaukler, Gary M; Li, Chenhua; Ding, Yu; Chirayath, Sunil S

    2012-03-01

    In recent years, the United States, along with many other countries, has significantly increased its detection and defense mechanisms against terrorist attacks. A potential attack with a nuclear weapon, using nuclear materials smuggled into the country, has been identified as a particularly grave threat. The system for detecting illicit nuclear materials that is currently in place at U.S. ports of entry relies heavily on passive radiation detectors and a risk-scoring approach using the automated targeting system (ATS). In this article we analyze this existing inspection system and demonstrate its performance for several smuggling scenarios. We provide evidence that the current inspection system is inherently incapable of reliably detecting sophisticated smuggling attempts that use small quantities of well-shielded nuclear material. To counter the weaknesses of the current ATS-based inspection system, we propose two new inspection systems: the hardness control system (HCS) and the hybrid inspection system (HYB). The HCS uses radiography information to classify incoming containers based on their cargo content into "hard" or "soft" containers, which then go through different inspection treatment. The HYB combines the radiography information with the intelligence information from the ATS. We compare and contrast the relative performance of these two new inspection systems with the existing ATS-based system. Our studies indicate that the HCS and HYB policies outperform the ATS-based policy for a wide range of realistic smuggling scenarios. We also examine the impact of changes in adversary behavior on the new inspection systems and find that they effectively preclude strategic gaming behavior of the adversary. © 2011 Society for Risk Analysis.

  16. Copper-substituted, lithium rich iron phosphate as cathode material for lithium secondary batteries

    International Nuclear Information System (INIS)

    Lee, S.B.; Cho, S.H.; Heo, J.B.; Aravindan, V.; Kim, H.S.; Lee, Y.S.

    2009-01-01

    Carbon-free, copper-doped, lithium rich iron phosphates, Li 1+x Fe 1-y Cu y PO 4 (0 ≤ x ≤ 0.15, 0 ≤ y ≤ 0.005), have been synthesized by a solid-state reaction method. From the optimization, the Li 1.05 Fe 0.997 Cu 0.003 PO 4 phase showed superior performances in terms of phase purity and high discharge capacity. The structural, morphological, and electrochemical properties were studied and compared to LiFePO 4 , Li 1.05 FePO 4 , LiFe 0.997 Cu 0.003 PO 4 , and materials. X-ray photoelectron spectroscopy (XPS) was conducted to ensure copper doping. Only smooth surface morphologies were observed for lithium rich iron phosphates, namely Li 1.05 FePO 4 and Li 1.05 Fe 0.997 Cu 0.003 PO 4 . The Li/Li 1.05 Fe 0.997 Cu 0.003 PO 4 cell delivered an initial discharge capacity of 145 mAh/g and was 18 mAh/g higher than the Li/LiFePO 4 cell without any carbon coating effect. Cyclic voltammetry revealed excellent reversibility of the Li 1.05 Fe 0.997 Cu 0.003 PO 4 material. High rate capability studies were also performed and showed a capacity retention over 95% during the cycling. We concluded that substituted Li and Cu ions play an important role in enhancing battery performance of the LiFePO 4 material through improving the kinetics of the lithium insertion/extraction reaction on the electrode.

  17. Evaluation of low cost cathode materials for treatment of industrial and food processing wastewater using microbial electrolysis cells

    KAUST Repository

    Tenca, Alberto; Cusick, Roland D.; Schievano, Andrea; Oberti, Roberto; Logan, Bruce E.

    2013-01-01

    Microbial electrolysis cells (MECs) can be used to treat wastewater and produce hydrogen gas, but low cost cathode catalysts are needed to make this approach economical. Molybdenum disulfide (MoS2) and stainless steel (SS) were evaluated

  18. Lithium recycling and cathode material regeneration from acid leach liquor of spent lithium-ion battery via facile co-extraction and co-precipitation processes.

    Science.gov (United States)

    Yang, Yue; Xu, Shengming; He, Yinghe

    2017-06-01

    A novel process for extracting transition metals, recovering lithium and regenerating cathode materials based on facile co-extraction and co-precipitation processes has been developed. 100% manganese, 99% cobalt and 85% nickel are co-extracted and separated from lithium by D2EHPA in kerosene. Then, Li is recovered from the raffinate as Li 2 CO 3 with the purity of 99.2% by precipitation method. Finally, organic load phase is stripped with 0.5M H 2 SO 4 , and the cathode material LiNi 1/3 Co 1/3 Mn 1/3 O 2 is directly regenerated from stripping liquor without separating metal individually by co-precipitation method. The regenerative cathode material LiNi 1/3 Co 1/3 Mn 1/3 O 2 is miro spherical morphology without any impurities, which can meet with LiNi 1/3 Co 1/3 Mn 1/3 O 2 production standard of China and exhibits good electrochemical performance. Moreover, a waste battery management model is introduced to guarantee the material supply for spent battery recycling. Copyright © 2017 Elsevier Ltd. All rights reserved.

  19. A Practical Anodic and Cathodic Curve Intersection Model to Understand Multiple Corrosion Potentials of Fe-Based Glassy Alloys in OH- Contained Solutions.

    Science.gov (United States)

    Li, Y J; Wang, Y G; An, B; Xu, H; Liu, Y; Zhang, L C; Ma, H Y; Wang, W M

    2016-01-01

    A practical anodic and cathodic curve intersection model, which consisted of an apparent anodic curve and an imaginary cathodic line, was proposed to explain multiple corrosion potentials occurred in potentiodynamic polarization curves of Fe-based glassy alloys in alkaline solution. The apparent anodic curve was selected from the measured anodic curves. The imaginary cathodic line was obtained by linearly fitting the differences of anodic curves and can be moved evenly or rotated to predict the number and value of corrosion potentials.

  20. Octahedral magnesium manganese oxide molecular sieves as the cathode material of aqueous rechargeable magnesium-ion battery

    International Nuclear Information System (INIS)

    Zhang, Hongyu; Ye, Ke; Shao, Shuangxi; Wang, Xin; Cheng, Kui; Xiao, Xue; Wang, Guiling; Cao, Dianxue

    2017-01-01

    Highlights: • The mico-sheet Mg-OMS-1 is synthesized by a simple hydrothermal method. • The mechanism of Mg 2+ insertion/deinsertion from Mg-OMS-1 is explored. • The electrode exhibits a good electrochemical performance in MgCl 2 electrolyte. - Abstract: Aqueous magnesium-ion batteries have shown the desired properties of high safety characteristics, similar electrochemical properties to lithium and low cost for energy storage applications. The micro-sheet morphology of todorokite-type magnesium manganese oxide molecular sieve (Mg-OMS-1) material, which applies as a novel cathode material for magnesium-ion battery, is obtained by the simple hydrothermal method. The structure and morphology of the particles are confirmed by X-ray power diffraction, X-ray photoelectron spectroscopy, inductively coupled plasma, scanning and transmission electron microscopy. The electrochemical performance of Mg-OMS-1 is researched by cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and constant current charge-discharge measurement. Mg-OMS-1 shows a good battery behavior for Mg 2+ insertion and deinsertion in the aqueous electrolyte. When discharging at 10 mA g −1 in 0.2 mol dm −3 MgCl 2 aqueous electrolyte, the initial discharge capacity reaches 300 mAh g −1 . The specific capacity retention rate is 83.7% after cycling 300 times at 100 mA g −1 in 0.5 mol dm −3 MgCl 2 electrolyte with a columbic efficiency of nearly 100%.

  1. Synthesis of LiFePO4/C cathode material from ferric oxide and organic lithium salts

    International Nuclear Information System (INIS)

    Shi Zhongqi; Huang Ming; Huai Yongjian; Lin Ziji; Yang Kerun; Hu Xuebu; Deng Zhenghua

    2011-01-01

    Research highlights: → LiFePO 4 can be synthesized from Fe 2 O 3 by a sequence of free-radical reactions. → Organic lithium salts can avoid the composition segregation of the precursor. → Low cost ferric oxide and environmentally friendly distilled water are used. - Abstract: LiFePO 4 /C cathode material has been simply synthesized via a modified in situ solid-state reaction route using the raw materials of Fe 2 O 3 , NH 4 H 2 PO 4 , Li 2 C 2 O 4 and lithium polyacrylate (PAALi). The sintering temperature of LiFePO 4 /C precursor is studied by thermo-gravimetric (TG)/differential thermal analysis (DTA). The physical properties of LiFePO 4 /C are then investigated through analysis using by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM) and the electrochemical properties are investigated by electrochemical impedance spectra (EIS), cyclic voltammogram (CV) and constant current charge/discharge test. The LiFePO 4 /C composite with the particle size of ∼200 nm shows better discharge capacity (156.4 mAh g -1 ) than bare LiFePO 4 (52.3 mAh g -1 ) at 0.2 C due to the improved electronic conductivity which is demonstrated by EIS. The as-prepared LiFePO 4 /C through this method also shows excellent high-rate characteristic and cycle performance. The initial discharge capacity of the sample is 120.5 mAh g -1 and the capacity retention rate is 100.6% after 50 cycles at 5 C rate. The results prove that the using of organic lithium salts can obtain a high performance LiFePO 4 /C composite.

  2. The effect of cathode surface impurities on gap closure

    International Nuclear Information System (INIS)

    Hinshelwood, D.D.

    1983-01-01

    Gap closure due to cathode (or anode) plasma motion is often the principal limitation on the pulse length of intense beam diodes and magnetically insulated transmission lines. Since the plasma expansion velocity is typically on the order of the sound speed, a high atomic number plasma is desirable. In recent experiments performed on a Sandia Nereus accelerator (240kV, 50kA, 3-30kA/cm 2 , 70ns) with a parallel plate diode, the cathode plasma was seen to be composed of both the cathode substrate material and constituents (hydrogen and carbon) of surface contaminants such as pump oils. The plasma expansion velocities, inferred from impedance measurements, were 1.5-2 cm/μs and were the same for carbon, aluminum and stainless steel cathodes. This similarity, combined with the temperature estimates of 2-3eV obtained from spectroscopy, implied that the expansion was due to protons from surface contaminants. Similar results were reported from studies of ablatively driven plasmas. In a continuation of the work, the results of time and spatially resolved spectroscopic studies of plasma formed on aluminum cathodes, yielding measurements of the expansion velocities of different components of the cathode plasma, are presented. We have heated stainless steel cathodes in situ to 700 0 C. The Hα line emission was seen to decrease by more than an order of magnitude (becoming lost in the background) when the cathodes were heated but no change in the impedance behavior was observed. Evidently the heating was insufficient to remove the last monolayer, which should contain more than enough hydrogen to close the gap. Preliminary experiments with gold-plated cathodes (which should be more resistant to chemisorption) yielded similar results. Further measurements of plasma formed on heated cathodes are presented

  3. Radiation levels on empty cylinders containing heel material

    Energy Technology Data Exchange (ETDEWEB)

    Shockley, C.W. [Martin Marietta Energy Systems, Inc., Paducah, KY (United States)

    1991-12-31

    Empty UF{sub 6} cylinders containing heel material were found to emit radiation levels in excess of 200 mr/hr, the maximum amount stated in ORO-651. The radiation levels were as high as 335 mr/hr for thick wall (48X and 48Y) cylinders and 1050 mr/hr for thin wall (48G and 48H) cylinders. The high readings were found only on the bottom of the cylinders. These radiation levels exceeded the maximum levels established in DOT 49 CFR, Part 173.441 for shipment of cylinders. Holding periods of four weeks for thick-wall cylinders and ten weeks for thin-wall cylinders were established to allow the radiation levels to decay prior to shipment.

  4. High performance Li3V2(PO4)3/C composite cathode material for lithium ion batteries studied in pilot scale test

    International Nuclear Information System (INIS)

    Chen Zhenyu; Dai Changsong; Wu Gang; Nelson, Mark; Hu Xinguo; Zhang Ruoxin; Liu Jiansheng; Xia Jicai

    2010-01-01

    Li 3 V 2 (PO 4 ) 3 /C composite cathode material was synthesized via carbothermal reduction process in a pilot scale production test using battery grade raw materials with the aim of studying the feasibility for their practical applications. XRD, FT-IR, XPS, CV, EIS and battery charge-discharge tests were used to characterize the as-prepared material. The XRD and FT-IR data suggested that the as-prepared Li 3 V 2 (PO 4 ) 3 /C material exhibits an orderly monoclinic structure based on the connectivity of PO 4 tetrahedra and VO 6 octahedra. Half cell tests indicated that an excellent high-rate cyclic performance was achieved on the Li 3 V 2 (PO 4 ) 3 /C cathodes in the voltage range of 3.0-4.3 V, retaining a capacity of 95% (96 mAh/g) after 100 cycles at 20C discharge rate. The low-temperature performance of the cathode was further evaluated, showing 0.5C discharge capacity of 122 and 119 mAh/g at -25 and -40 o C, respectively. The discharge capacity of graphite//Li 3 V 2 (PO 4 ) 3 batteries with a designed battery capacity of 14 Ah is as high as 109 mAh/g with a capacity retention of 92% after 224 cycles at 2C discharge rates. The promising high-rate and low-temperature performance observed in this work suggests that Li 3 V 2 (PO 4 ) 3 /C is a very strong candidate to be a cathode in a next-generation Li-ion battery for electric vehicle applications.

  5. Bismuth-doped La1.75Sr0.25NiO4+: δ as a novel cathode material for solid oxide fuel cells

    NARCIS (Netherlands)

    Zhu, Zhesheng; Li, Mei; Xia, Changrong; Bouwmeester, Henny J.M.

    2017-01-01

    Bismuth has been doped into mixed ionic-electronic conducting La1.75Sr0.25NiO4+δ (LSN) with the 2D K2NiF4-type structure to evaluate its influence on various properties of the host material, which include its potential use as a SOFC cathode. X-ray powder diffraction indicates that LSN retains its

  6. Novel sodium intercalated (NH4)2V6O16 platelets: High performance cathode materials for lithium-ion battery.

    Science.gov (United States)

    Fei, Hailong; Wu, Xiaomin; Li, Huan; Wei, Mingdeng

    2014-02-01

    A simple and versatile method for preparation of novel sodium intercalated (NH4)2V6O16 is developed via a simple hydrothermal route. It is found that ammonium sodium vanadium bronze displays higher discharge capacity and better rate cyclic stability than ammonium vanadium bronze as lithium-ion battery cathode material because of smaller charge transfer resistance, which would favor superior discharge capacity and rate performance. Crown Copyright © 2013. Published by Elsevier Inc. All rights reserved.

  7. Analysis of wallboard containing a phase change material

    Science.gov (United States)

    Tomlinson, J. J.; Heberle, D. P.

    Phase change materials (PCMs) used on the interior of buildings hold the promise for improved thermal performance by reducing the energy requirements for space conditioning and by improving thermal comfort by reducing temperature swings inside the building. Efforts are underway to develop a gypsum wallboard containing a hydrocarbon PCM. With a phase change temperature in the room temperature range, the PCM wallboard adds substantially to the thermal mass of the building while serving the same architectural function as conventional wallboard. To determine the thermal and economic performance of this PCM wallboard, the Transient Systems Simulation Program (TRNSYS) was modified to accommodate walls that are covered with PCM plasterboard, and to apportion the direct beam solar radiation to interior surfaces of a building. The modified code was used to simulate the performance of conventional and direct-gain passive solar residential-sized buildings with and without PCM wallboard. Space heating energy savings were determined as a function of PCM wallboard characteristics. Thermal comfort improvements in buildings containing the PCM were qualified in terms of energy savings. The report concludes with a present worth economic analysis of these energy savings and arrives at system costs and economic payback based on current costs of PCMs under study for the wallboard application.

  8. Evaluation of calculational and material models for concrete containment structures

    International Nuclear Information System (INIS)

    Dunham, R.S.; Rashid, Y.R.; Yuan, K.A.

    1984-01-01

    A computer code utilizing an appropriate finite element, material and constitutive model has been under development as a part of a comprehensive effort by the Electric Power Research Institute (EPRI) to develop and validate a realistic methodology for the ultimate load analysis of concrete containment structures. A preliminary evaluation of the reinforced and prestressed concrete modeling capabilities recently implemented in the ABAQUS-EPGEN code has been completed. This effort focuses on using a state-of-the-art calculational model to predict the behavior of large-scale reinforced concrete slabs tested under uniaxial and biaxial tension to simulate the wall of a typical concrete containment structure under internal pressure. This paper gives comparisons between calculations and experimental measurements for a uniaxially-loaded specimen. The calculated strains compare well with the measured strains in the reinforcing steel; however, the calculations gave diffused cracking patterns that do not agree with the discrete cracking observed in the experiments. Recommendations for improvement of the calculational models are given. (orig.)

  9. Electrochemical impedance spectroscopy characterization of LiFePO4 cathode material with carboxymethylcellulose and poly-3,4-ethylendioxythiophene/polystyrene sulfonate

    International Nuclear Information System (INIS)

    Eliseeva, S.N.; Apraksin, R.V.; Tolstopjatova, E.G.; Kondratiev, V.V.

    2017-01-01

    Highlights: • New composition of perspective LiFePO 4 /PEDOT:PSS/CMC cathode material are explored. • Conducting polymer binder markedly reduce an interfacial resistance. • High rate performance due to enhanced ionic and electronic conductivity. • Comparison of kinetic parameters obtained from fitting of EIS data was performed. - Abstract: Novel cathode material compositions based on lithium iron phosphate (LFP) were prepared using conducting polymer dispersion poly-3,4-ethylenedioxythiopene/polystyrene sulfonate (PEDOT:PSS) and water-based carboxymethylcellulose (РЎРњРЎ) as a binder solely and in mixture PEDOT:PSS/РЎРњРЎ. The electrochemical properties of materials in lithium-ion batteries were investigated by galvanostatic charge-discharge curves and by electrochemical impedance spectroscopy and the results were compared with conventional PVDF-bound material. Our best materials consisting of 92 wt% of C-LiFePO 4 , 4 wt% of carbon black and 4 wt% of conducting polymer binder exhibited excellent rate capability with discharge capacity 148 mAh g −1 (at 0.2C, normalized by the electrode mass), 143 mAh g −1 at 1C and 128 mAh g −1 at 5C as well as good cycling stability at 1C (less than 1% decay after 100 cycles). Impedance spectra of batteries with different compositions were measured and analyzed. Comparison of kinetic parameters obtained for different electrodes revealed main factors responsible for significant improvement of electrochemical performance of LFP-based cathode materials modified with conducting polymer in comparison with conventional electrode. The transition from conventional PVDF-bound LFP-based cathode composition to modified by conducting polymer PEDOT:PSS/CMC was found very effective. The electrode with optimal composition showed substantial decrease of interfacial charge transfer resistance for 30 times, and decrease of Warburg diffusion resistance. The mechanism of positive influence of

  10. The interaction of iodine with organic material in containment

    International Nuclear Information System (INIS)

    Wren, J.C.; Ball, J.M.; Glown, G.A.; Portmann, R.; Sanipelli, G.G.

    1996-01-01

    Organic impurities in containment water, originating from various painted structural surfaces and organic containment materials, could have a significant impact on iodine volatility following an accident. A research program at the Whiteshell Laboratories of AECL has been designed to determine the impact of organic impurities on iodine volatility under accident conditions. The program consists of experimental, literature and modelling studies on the radiolysis or organic compounds in the aqueous phase, thermal and radiolytic formation and decomposition of organic iodides, dissolution of organic solvents from various painted surfaces into the aqueous phase, and iodine deposition on painted surfaces. The experimental studies consist of bench-scale 'separate effects' tests as well as intermediate-scale 'integrated effects' in the Radioiodine Test facility. The studies have shown that organic impurities will be found in containment water, arising from the dissolution of organic compounds from various surface paints and that these compounds can potentially have a significant impact on iodine volatility following an accident. The main impact of surface paints will occur through aqueous-phase reactions of the organic compounds that they release to the aqueous phase. Under the radiation conditions expected during an accident, these compounds will react to reduce the pH and dissolved oxygen concentration, consequently increasing the formation of I 2 from I - that is present in the sump. It appears that the rates of these processes may be controlled by the dissolution kinetics of the organic compounds from the surface coatings. Moreover, the organic compounds may also react thermally and radiolytically with I 2 to form organic iodides in the aqueous phase. Our studies have shown that the formation of organic iodides from soluble organics such as ketones, alcohols and phenols may have more impact on the total iodine volatility than the formation of CH 3 I. (author) 13 figs., 2

  11. The interaction of iodine with organic material in containment

    Energy Technology Data Exchange (ETDEWEB)

    Wren, J C; Ball, J M; Glown, G A; Portmann, R; Sanipelli, G G [Atomic Energy of Canada Ltd., Pinawa, MB (Canada). Whiteshell Labs.

    1996-12-01

    Organic impurities in containment water, originating from various painted structural surfaces and organic containment materials, could have a significant impact on iodine volatility following an accident. A research program has been designed to determine the impact of organic impurities on iodine volatility under accident conditions. The program consists of experimental, literature and modelling studies on the radiolysis or organic compounds in the aqueous phase, thermal and radiolytic formation and decomposition of organic iodides, dissolution of organic solvents from various painted surfaces into the aqueous phase, and iodine deposition on painted surfaces. The experimental studies consist of bench-scale `separate effects` tests as well as intermediate-scale `integrated effects` in the Radioiodine Test facility. The studies have shown that organic impurities will be found in containment water, arising from the dissolution of organic compounds from various surface paints and that these compounds can potentially have a significant impact on iodine volatility following an accident. The main impact of surface paints will occur through aqueous-phase reactions of the organic compounds that they release to the aqueous phase. Under the radiation conditions expected during an accident, these compounds will react to reduce the pH and dissolved oxygen concentration, consequently increasing the formation of I{sub 2} from I{sup -} that is present in the sump. It appears that the rates of these processes may be controlled by the dissolution kinetics of the organic compounds from the surface coatings. Moreover, the organic compounds may also react thermally and radiolytically with I{sub 2} to form organic iodides in the aqueous phase. Our studies have shown that the formation of organic iodides from soluble organics such as ketones, alcohols and phenols may have more impact on the total iodine volatility than the formation of CH{sub 3}I. (author) 13 figs., 2 tabs., 19 refs.

  12. Fabricating Composite-Material Structures Containing SMA Ribbons

    Science.gov (United States)

    Turner, Travis L.; Cano, Roberto J.; Lach, Cynthia L.

    2003-01-01

    An improved method of designing and fabricating laminated composite-material (matrix/fiber) structures containing embedded shape-memory-alloy (SMA) actuators has been devised. Structures made by this method have repeatable, predictable properties, and fabrication processes can readily be automated. Such structures, denoted as shape-memory-alloy hybrid composite (SMAHC) structures, have been investigated for their potential to satisfy requirements to control the shapes or thermoelastic responses of themselves or of other structures into which they might be incorporated, or to control noise and vibrations. Much of the prior work on SMAHC structures has involved the use SMA wires embedded within matrices or within sleeves through parent structures. The disadvantages of using SMA wires as the embedded actuators include (1) complexity of fabrication procedures because of the relatively large numbers of actuators usually needed; (2) sensitivity to actuator/ matrix interface flaws because voids can be of significant size, relative to wires; (3) relatively high rates of breakage of actuators during curing of matrix materials because of sensitivity to stress concentrations at mechanical restraints; and (4) difficulty of achieving desirable overall volume fractions of SMA wires when trying to optimize the integration of the wires by placing them in selected layers only.

  13. Inelastic analysis acceptance criteria for radioactive material transportation containers

    International Nuclear Information System (INIS)

    Ammerman, D.J.; Ludwigsen, J.S.

    1993-01-01

    The design criteria currently used in the design of radioactive material (RAM) transportation containers are taken from the ASME Boiler and Pressure Vessel Code (ASME, 1992). These load-based criteria are ideally suited for pressure vessels where the loading is quasistatic and all stresses are in equilibrium with externally applied loads. For impact events, the use of load-based criteria is less supportable. Impact events tend to be energy controlled, and thus, energy-based acceptance criteria would appear to be more appropriate. Determination of an ideal design criteria depends on what behavior is desired. Currently there is not a design criteria for inelastic analysis for RAM nation packages that is accepted by the regulatory agencies. This lack of acceptance criteria is one of the major factors in limiting the use of inelastic analysis. In this paper inelastic analysis acceptance criteria based on stress and strain-energy density will be compared for two stainless steel test units subjected to impacts onto an unyielding target. Two different material models are considered for the inelastic analysis, a bilinear fit of the stress-strain curve and a power law hardening model that very closely follows the stress-strain curve. It is the purpose of this paper to stimulate discussion and research into the area of strain-energy density based inelastic analysis acceptance criteria

  14. Nature of the Electrochemical Properties of Sulphur Substituted LiMn2O4 Spinel Cathode Material Studied by Electrochemical Impedance Spectroscopy

    Directory of Open Access Journals (Sweden)

    Monika Bakierska

    2016-08-01

    Full Text Available In this work, nanostructured LiMn2O4 (LMO and LiMn2O3.99S0.01 (LMOS1 spinel cathode materials were comprehensively investigated in terms of electrochemical properties. For this purpose, electrochemical impedance spectroscopy (EIS measurements as a function of state of charge (SOC were conducted on a representative charge and discharge cycle. The changes in the electrochemical performance of the stoichiometric and sulphur-substituted lithium manganese oxide spinels were examined, and suggested explanations for the observed dependencies were given. A strong influence of sulphur introduction into the spinel structure on the chemical stability and electrochemical characteristic was observed. It was demonstrated that the significant improvement in coulombic efficiency and capacity retention of lithium cell with LMOS1 active material arises from a more stable solid electrolyte interphase (SEI layer. Based on EIS studies, the Li ion diffusion coefficients in the cathodes were estimated, and the influence of sulphur on Li+ diffusivity in the spinel structure was established. The obtained results support the assumption that sulphur substitution is an effective way to promote chemical stability and the electrochemical performance of LiMn2O4 cathode material.

  15. Stress corrosion cracking of candidate materials for nuclear waste containers

    International Nuclear Information System (INIS)

    Maiya, P.S.; Shack, W.J.; Kassner, T.F.

    1989-09-01

    Types 304L and 316L stainless steel (SS), Incoloy 825, Cu, Cu-30%Ni, and Cu-7%Al have been selected as candidate materials for the containment of high-level nuclear waste at the proposed Yucca Mountain Site in Nevada. The susceptibility of these materials to stress corrosion cracking has been investigated by slow-strain-rate tests (SSRTs) in water which simulates that from well J-13 (J-13 water) and is representative of the groundwater present at the Yucca Mountain site. The SSRTs were performed on specimens exposed to simulated J-13 water at 93 degree C and at a strain rate 10 -7 s -1 under crevice conditions and at a strain rate of 10 -8 s -1 under both crevice and noncrevice conditions. All the tests were interrupted after nominal elongation strains of 1--4%. Examination by scanning electron microscopy showed some crack initiation in virtually all specimens. Optical microscopy of metallographically prepared transverse sections of Type 304L SS suggests that the crack depths are small (<10 μm). Preliminary results suggest that a lower strain rate increases the severity of cracking of Types 304L and 316L SS, Incoloy 825, and Cu but has virtually no effect on Cu-30%Ni and Cu-7%Al. Differences in susceptibility to cracking were evaluated in terms of a stress ratio, which is defined as the ratio of the increase in stress after local yielding in the environment to the corresponding stress increase in an identical test in air, both computed at the same strain. On the basis of this stress ratio, the ranking of materials in order of increasing resistance to cracking is: Types 304L SS < 316L SS < Incoloy 825 congruent Cu-30%Ni < Cu congruent Cu-7%Al. 9 refs., 12 figs., 7 tabs

  16. Detection of nuclear material by photon activation inside cargo containers

    Science.gov (United States)

    Gmar, Mehdi; Berthoumieux, Eric; Boyer, Sébastien; Carrel, Frédérick; Doré, Diane; Giacri, Marie-Laure; Lainé, Frédéric; Poumarède, Bénédicte; Ridikas, Danas; Van Lauwe, Aymeric

    2006-05-01

    Photons with energies above 6 MeV can be used to detect small amounts of nuclear material inside large cargo containers. The method consists in using an intense beam of high-energy photons (bremsstrahlung radiation) in order to induce reactions of photofission on actinides. The measurement of delayed neutrons and delayed gammas emitted by fission products brings specific information on localization and quantification of the nuclear material. A simultaneous measurement of both of these delayed signals can overcome some important limitations due to matrix effects like heavy shielding and/or the presence of light elements as hydrogen. We have a long experience in the field of nuclear waste package characterization by photon interrogation and we have demonstrated that presently the detection limit can be less than one gram of actinide per ton of package. Recently we tried to extend our knowledge to assess the performance of this method for the detection of special nuclear materials in sea and air freights. This paper presents our first results based on experimental measurements carried out in the SAPHIR facility, which houses a linear electron accelerator with the energy range from 15 MeV to 30 MeV. Our experiments were also modeled using the full scale Monte Carlo techniques. In addition, and in a more general frame, due to the lack of consistent data on photonuclear reactions, we have been working on the development of a new photonuclear activation file (PAF), which includes cross sections for more than 600 isotopes including photofission fragment distributions and delayed neutron tables for actinides. Therefore, this work includes also some experimental results obtained at the ELSA electron accelerator, which is more adapted for precise basic nuclear data measurements.

  17. Control of electrochemical properties of nickel-rich layered cathode materials for lithium ion batteries by variation of the manganese to cobalt ratio

    Science.gov (United States)

    Sun, Ho-Hyun; Choi, Wonchang; Lee, Joong Kee; Oh, In-Hwan; Jung, Hun-Gi

    2015-02-01

    Various Ni-rich layered oxide cathodes (above 0.80 Ni content), such as LiNi1-y-zCoyAlzO2 (NCA), are used in electric vehicles (EVs) due to their high capacity (∼200 mAh g-1 for NCA). However, to improve cycle performance and thermal stability and to ensure longer and safer usage, numerous studies have investigated surface modification, coating, and doping of cathode materials. In this study, we have investigated the characteristics of Li[Ni0.85CoxMn0.15-x]O2 with various Mn to Co ratios (x = 0-0.15) synthesized by a coprecipitation method. The discharge capacities of the Li[Ni0.85CoxMn0.15-x]O2 cathodes are similar at around 206 mAh g-1 at room temperature and 213.8 mAh g-1 at 55 °C between 2.7 and 4.3 V at a 0.2C rate, while the cyclability, thermal stability, and rate capability of all samples differ according to the Mn and Co ratio. The Li[Ni0.85Co0.05Mn0.10]O2 cathode shows the most promising electrochemical properties under different conditions among the various cathodes evaluated; it displays a high rate capacity (approximately 163 mAh g-1 at 5C rate) at 25 °C and good thermal stability (main exothermic temperature of 233.7 °C and relatively low heat evolution of 857.3 J g-1).

  18. Sufficient Utilization of Zirconium Ions to Improve the Structure and Surface properties of Nickel-Rich Cathode Materials for Lithium-Ion Batteries.

    Science.gov (United States)

    He, Tao; Lu, Yun; Su, Yuefeng; Bao, Liying; Tan, Jing; Chen, Lai; Zhang, Qiyu; Li, Weikang; Chen, Shi; Wu, Feng

    2018-02-19

    We doped Zr 4+ ions in the outer layer of Ni 0.8 Co 0.1 Mn 0.1 (OH) 2 by coprecipitation. The distribution of Zr 4+ in the final cathode materials showed a gradient distribution because of ion migration during the thermal treatment. The doped layer was confirmed by using various analysis methods (energy-dispersive X-ray spectroscopy, XRD, X-ray photoelectron spectroscopy, and TEM), which implies that Zr 4+ can not only occupy both the transition metal slabs and Li slabs but also form a Li 2 ZrO 3 layer on the surface as a highly ion-conductive layer. The doped Zr 4+ in the transition metal slabs can stabilize the crystal structure because of the strong Zr-O bond energy, and the doped Zr 4+ in the Li slabs can act as pillar ions to improve the structural stability and reduce cation mixing. The gradient doping can take advantage of the "pillar effect" and restrain the "blocking effect" of the pillar ions, which reduces irreversible capacity loss and improves the cycling and rate performance of the Ni-rich cathode materials. The capacity retention of the modified sample reached 83.2 % after 200 cycles at 1C (200 mA g -1 ) at 2.8-4.5 V, and the discharge capacity was up to 164.7 mAh g -1 at 10C. This effective strategy can improve the structure stability of the cathode material while reducing the amount of non-electrochemical active dopant because of the gradient distribution of the dopant. In addition, the highly ion-conductive layer of Li 2 ZrO 3 on the surface can improve the rate performance of the cathode. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

  19. Cathodes and electrolytes for rechargeable magnesium batteries and methods of manufacture

    Energy Technology Data Exchange (ETDEWEB)

    Kumta, Prashant N.; Saha, Partha; Datta, Moni Kanchan; Manivannan, Ayyakkannu

    2018-04-17

    The invention relates to Chevrel-phase materials and methods of preparing these materials utilizing a precursor approach. The Chevrel-phase materials are useful in assembling electrodes, e.g., cathodes, for use in electrochemical cells, such as rechargeable batteries. The Chevrel-phase materials have a general formula of Mo6Z8 and the precursors have a general formula of MxMo6Z8. The cathode containing the Chevrel-phase material in accordance with the invention can be combined with a magnesium-containing anode and an electrolyte.

  20. Cathodes and electrolytes for rechargeable magnesium batteries and methods of manufacture

    Science.gov (United States)

    Kumta, Prashant N.; Saha, Partha; Datta, Moni Kanchan; Manivannan, Ayyakkannu

    2018-04-17

    The invention relates to Chevrel-phase materials and methods of preparing these materials utilizing a precursor approach. The Chevrel-phase materials are useful in assembling electrodes, e.g., cathodes, for use in electrochemical cells, such as rechargeable batteries. The Chevrel-phase materials have a general formula of Mo6Z8 and the precursors have a general formula of MxMo6Z8. The cathode containing the Chevrel-phase material in accordance with the invention can be combined with a magnesium-containing anode and an electrolyte.

  1. Layered SmBaCuCoO5+δ and SmBaCuFeO5+δ perovskite oxides as cathode materials for proton-conducting SOFCs

    International Nuclear Information System (INIS)

    Nian Qiong; Zhao Ling; He Beibei; Lin Bin; Peng Ranran; Meng Guangyao; Liu Xingqin

    2010-01-01

    A dense BaCe 0.8 Sm 0.2 O 5+δ (BCS) electrolyte was fabricated on a porous anode by in situ drop-coating to develop a simple and cost-effective route to fabricate proton-conducting solid oxide fuel cells (SOFCs). Layered perovskite-structure oxides SmBaCuCoO 5+δ (SBCC) and SmBaCuFeO 5+δ (SBCF) were prepared and the electrical conductivity, the thermal expansion coefficient and electrochemical performance were investigated as potential cathode materials for proton-conducting SOFCs. Thermal expansion coefficients of SBCC and SBCF were suitable for BCS electrolyte and the electrical conductivity of the SBCC is higher than that of the SBCF. The maximum power density of 449 mW cm 2 and 333 mW cm 2 at 700 o C were obtained for the SBCC/BCS/NiO-BCS and SBCF/BCS/NiO-BCS cells, respectively. The interfacial polarization resistances for SBCC and SBCF cathode are as low as 0.137 Ω cm -2 and 0.196 Ω cm -2 at 700 o C, respectively. The results indicate that the SBCC and SBCF are promising cathode materials for proton-conducting SOFCs.

  2. Superior lithium-ion insertion/extraction properties of a novel LiFePO4/C/graphene material used as a cathode in aqueous solution.

    Science.gov (United States)

    Duan, Wenyuan; Zhao, Mingshu; Shen, Junfang; Zhao, Suixin; Song, Xiaoping

    2017-09-28

    Herein, olivine LiFePO 4 covered with graphene and carbon layers is prepared via a sol-gel method, followed by calcination, and the resultant composite is used as a cathode material in aqueous rechargeable lithium-ion batteries (ARLBs). The phase structure and morphology of the composite are characterized via X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HRTEM) and specific surface area analysis (BET). The ARLB system is fabricated using LiFePO 4 /C/graphene as the cathode and a zinc anode in 1 mol L -1 ZnSO 4 ·7H 2 O and saturated LiNO 3 aqueous solution without dissolved oxygen, which delivers a capacity of 153 mA h g -1 at 0.5C rate. Even at a 50C rate, it maintains a capacity of 95 mA h g -1 after 200 cycles. The excellent rate capabilities show that this cathode material exhibits good electrochemical performance and this novel ARLB has great potential in the fields of energy storage and high power sources.

  3. Fe/Fe3C decorated 3-D porous nitrogen-doped graphene as a cathode material for rechargeable Li–O2 batteries

    International Nuclear Information System (INIS)

    Lai, Yanqing; Chen, Wei; Zhang, Zhian; Qu, Yaohui; Gan, Yongqing; Li, Jie

    2016-01-01

    Graphical abstract: Fe/Fe 3 C decorated 3-D porous N-doped graphene are prepaed by a one-step carbonization process, with MOF as the structure-directing agent. The method provides a simple and scalable route for preparing 3-D porous graphene materials.The as-prepared material possesses an excellent bi-functional electrocatalytic activity. While applied as the cathode materials of Li–O 2 batteries, the cell exihibits high capacity and considerable rate capability. - Highlights: • A facile simple strategy is employed to in-situ fabricate Fe/Fe 3 C decorated 3-D porous nitrogen-doped graphene. • MIL-100(Fe), a kind of metal-organic framework, is proved playing a structure-directing role in this advanced synthesis route. • This material possesses excellent bi-functional electro-catalytic activity for ORR and OER and shows good electrochemical performance while used as cathode material for Li–O 2 batteries. • The MOF-assisted synthesis method would be a promising new strategy for the synthesis of 3-D porous graphene materials. - Abstract: Fe/Fe 3 C decorated 3-D porous N-doped graphene (F-PNG) is designed and synthesized via a one-step carbonization route. During the process, MIL-100(Fe), a kind of metal organic frameworks (MOFs) plays a structure-directing role. It is found that F-PNG with 3-D porous structure is constituted by N-doped graphene and extremely small Fe/Fe 3 C particles uniformly distribute on the surface of graphene. This rationally designed F-PNG possesses excellent oxygen reduction reaction and oxygen evolution reaction bifunctional electrocatalytic activity. While the material is explored as a cathode of Li–O 2 batteries, it exhibits excellent electrochemical performances, delivering a discharge voltage platform of ∼2.91 V and a charge voltage platform of ∼3.52 V at 0.1 mA cm −2 , showing a good cycle performance and having a discharge capacity of ∼7150 mAh g −1 carbon+catalyst at 0.1 mA cm −2 . The excellent performance of

  4. Synthesis of Li2MnSiO4-graphene composite and its electrochemical performances as a cathode material for lithium ion batteries.

    Science.gov (United States)

    Kim, Jeonghyun; Song, Taeseup; Park, Hyunjung; Yuh, Junhan; Paik, Ungyu

    2014-10-01

    The Li2MnSiO4 is a promising candidate as a cathode for lithium ion batteries due to its large theoretical capacity of 330 mA h g(-1) and high thermal stability. However, the problems related to low electronic conductivity and large irreversible capacity at the first cycle limits its practical use as a Li-ion cathode material. We have developed a carbon coated Li2MnSiO4-graphene composite electrode to overcome these problems. Our designed electrode exhibits high reversible capacity of 301 mA h g(-1), with a high initial coulombic efficiency, and a discharge capacity at current rate of 0.5 C, that is double value of carbon coated Li2MnSiO4-carbon black composite electrode. These significant improvements are attributed to fast electron transport along the graphene sheet.

  5. Nanotube cathodes.

    Energy Technology Data Exchange (ETDEWEB)

    Overmyer, Donald L.; Lockner, Thomas Ramsbeck; Siegal, Michael P.; Miller, Paul Albert

    2006-11-01

    Carbon nanotubes have shown promise for applications in many diverse areas of technology. In this report we describe our efforts to develop high-current cathodes from a variety of nanotubes deposited under a variety of conditions. Our goal was to develop a one-inch-diameter cathode capable of emitting 10 amperes of electron current for one second with an applied potential of 50 kV. This combination of current and pulse duration significantly exceeds previously reported nanotube-cathode performance. This project was planned for two years duration. In the first year, we tested the electron-emission characteristics of nanotube arrays fabricated under a variety of conditions. In the second year, we planned to select the best processing conditions, to fabricate larger cathode samples, and to test them on a high-power relativistic electron beam generator. In the first year, much effort was made to control nanotube arrays in terms of nanotube diameter and average spacing apart. When the project began, we believed that nanotubes approximately 10 nm in diameter would yield sufficient electron emission properties, based on the work of others in the field. Therefore, much of our focus was placed on measured field emission from such nanotubes grown on a variety of metallized surfaces and with varying average spacing between individual nanotubes. We easily reproduced the field emission properties typically measured by others from multi-wall carbon nanotube arrays. Interestingly, we did this without having the helpful vertical alignment to enhance emission; our nanotubes were randomly oriented. The good emission was most likely possible due to the improved crystallinity, and therefore, electrical conductivity, of our nanotubes compared to those in the literature. However, toward the end of the project, we learned that while these 10-nm-diameter CNTs had superior crystalline structure to the work of others studying field emission from multi-wall CNT arrays, these nanotubes still

  6. Nanotube cathodes

    International Nuclear Information System (INIS)

    Overmyer, Donald L.; Lockner, Thomas Ramsbeck; Siegal, Michael P.; Miller, Paul Albert

    2006-01-01

    Carbon nanotubes have shown promise for applications in many diverse areas of technology. In this report we describe our efforts to develop high-current cathodes from a variety of nanotubes deposited under a variety of conditions. Our goal was to develop a one-inch-diameter cathode capable of emitting 10 amperes of electron current for one second with an applied potential of 50 kV. This combination of current and pulse duration significantly exceeds previously reported nanotube-cathode performance. This project was planned for two years duration. In the first year, we tested the electron-emission characteristics of nanotube arrays fabricated under a variety of conditions. In the second year, we planned to select the best processing conditions, to fabricate larger cathode samples, and to test them on a high-power relativistic electron beam generator. In the first year, much effort was made to control nanotube arrays in terms of nanotube diameter and average spacing apart. When the project began, we believed that nanotubes approximately 10 nm in diameter would yield sufficient electron emission properties, based on the work of others in the field. Therefore, much of our focus was placed on measured field emission from such nanotubes grown on a variety of metallized surfaces and with varying average spacing between individual nanotubes. We easily reproduced the field emission properties typically measured by others from multi-wall carbon nanotube arrays. Interestingly, we did this without having the helpful vertical alignment to enhance emission; our nanotubes were randomly oriented. The good emission was most likely possible due to the improved crystallinity, and therefore, electrical conductivity, of our nanotubes compared to those in the literature. However, toward the end of the project, we learned that while these 10-nm-diameter CNTs had superior crystalline structure to the work of others studying field emission from multi-wall CNT arrays, these nanotubes still

  7. Fuel salt and container material studies for MOSART transforming system

    Energy Technology Data Exchange (ETDEWEB)

    Ignatiev, V.; Feynberg, O.; Merzlyakov, A.; Surenkov, A.; Zagnitko, A. [National Research Center, Kurchatov Institute, Moscow (Russian Federation); Afonichkin, V.; Bovet, A.; Khokhlov, V. [Institute of High Temperature Electrochemisty, Ekaterinburg (Russian Federation); Subbotin, V.; Gordeev, M.; Panov, A.; Toropov, A. [Institute of Technical Physics, Snezhinsk (Russian Federation)

    2013-07-01

    A study is under progress to examine the feasibility of single stream Molten Salt Actinide Recycling and Transmuting system without and with Th support (MOSART) fuelled with different compositions of actinide tri-fluorides (AnF{sub 3}) from used LWR fuel. New fast-spectrum design options with homogeneous core and fuel salts with high enough solubility for AnF{sub 3} are being examined because of new goals. The flexibility of single fluid MOSART concept with Th support is underlined, particularly, possibility of its operation in self-sustainable mode (Conversion Ratio: CR=1) using different loadings and make up. The paper summarizes the most current status of fuel salt and container material data for the MOSART concept received within ISTC-3749 and ROSATOM-MARS projects. Key physical and chemical properties of various fluoride fuel salts are reported. The issues like salt purification, the electroreduction of U(IV) to U(III) in LiF-ThF{sub 4} and the electroreduction of Yb(III) to Yb(II) in LiF-NaF are detailed.

  8. Assessment of four different cathode materials at different initial pHs using unbuffered catholytes in microbial electrolysis cells

    KAUST Repository

    Ribot-Llobet, Edgar; Nam, Joo-Youn; Tokash, Justin C.; Guisasola, Albert; Logan, Bruce E.

    2013-01-01

    Nickel foam (NF), stainless steel wool (SSW), platinum coated stainless steel mesh (Pt), and molybdenum disulfide coated stainless steel mesh (MoS 2) electrodes have been proposed as catalysts for hydrogen gas production, but previous tests have primarily examined their performance in well buffered solutions. These materials were compared using two-chamber microbial electrolysis cells (MECs), and linear sweep voltammetry (LSV) in unbuffered saline solutions at two different initial pHs (7 and 12). There was generally no appreciable effect of initial pH on production rates or total gas production. NF produced hydrogen gas at a rate of 1.1 m3 H2/m 3·d, which was only slightly less than that using Pt (1.4 m3 H2/m3·d), but larger than that obtained with SSW (0.52 m3 H2/m3·d) or MoS2 (0.67 m3 H2/m3·d). Overall hydrogen gas recoveries with SSW (29.7 ± 0.5 mL), MoS2 (28.6 ± 1.3 mL) and NF (32.4 ± 2 mL) were only slightly less than that of Pt (37.9 ± 0.5 mL). Total energy recoveries, based on the gas produced versus electrical energy input, ranged from 0.75 ± 0.02 for Pt, to 0.55 ± 0.02 for SSW. An LSV analysis showed no effect of pH for NF and Pt, but overpotentials were reduced for MoS2 and SSW by using an initial lower pH. At cathode potentials more negative than -0.85 V (vs Ag/AgCl), NF had lower overpotentials than the MoS2. These results provide the first assessment of these materials under practical conditions of high pH in unbuffered saline catholytes, and position NF as the most promising inexpensive alternative to Pt.

  9. Synthesis of LiFePO{sub 4}/C cathode material from ferric oxide and organic lithium salts

    Energy Technology Data Exchange (ETDEWEB)

    Shi Zhongqi; Huang Ming [Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu, Sichuan 610041 (China); Graduate School of Chinese Academy of Sciences, Beijing, 100039 (China); Huai Yongjian [Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu, Sichuan 610041 (China); Graduate School of Chinese Academy of Sciences, Beijing, 100039 (China); China Aviation Lithium Battery Co., Ltd, Luoyang, Henan 471003 (China); Lin Ziji; Yang Kerun [Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu, Sichuan 610041 (China); Graduate School of Chinese Academy of Sciences, Beijing, 100039 (China); Hu Xuebu [Department of Chemistry and Materials, Sichuan Normal University, Chengdu, Sichuan 610068 (China); Zhongke Laifang Power Science and Technology Co., Ltd., Chengdu, Sichuan 610041 (China); Deng Zhenghua, E-mail: zhdeng@cioc.ac.c [Chengdu Institute of Organic Chemistry, Chinese Academy of Sciences, Chengdu, Sichuan 610041 (China); Graduate School of Chinese Academy of Sciences, Beijing, 100039 (China); Zhongke Laifang Power Science and Technology Co., Ltd., Chengdu, Sichuan 610041 (China)

    2011-04-15

    Research highlights: {yields} LiFePO{sub 4} can be synthesized from Fe{sub 2}O{sub 3} by a sequence of free-radical reactions. {yields} Organic lithium salts can avoid the composition segregation of the precursor. {yields} Low cost ferric oxide and environmentally friendly distilled water are used. - Abstract: LiFePO{sub 4}/C cathode material has been simply synthesized via a modified in situ solid-state reaction route using the raw materials of Fe{sub 2}O{sub 3}, NH{sub 4}H{sub 2}PO{sub 4}, Li{sub 2}C{sub 2}O{sub 4} and lithium polyacrylate (PAALi). The sintering temperature of LiFePO{sub 4}/C precursor is studied by thermo-gravimetric (TG)/differential thermal analysis (DTA). The physical properties of LiFePO{sub 4}/C are then investigated through analysis using by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscope (TEM) and the electrochemical properties are investigated by electrochemical impedance spectra (EIS), cyclic voltammogram (CV) and constant current charge/discharge test. The LiFePO{sub 4}/C composite with the particle size of {approx}200 nm shows better discharge capacity (156.4 mAh g{sup -1}) than bare LiFePO{sub 4} (52.3 mAh g{sup -1}) at 0.2 C due to the improved electronic conductivity which is demonstrated by EIS. The as-prepared LiFePO{sub 4}/C through this method also shows excellent high-rate characteristic and cycle performance. The initial discharge capacity of the sample is 120.5 mAh g{sup -1} and the capacity retention rate is 100.6% after 50 cycles at 5 C rate. The results prove that the using of organic lithium salts can obtain a high performance LiFePO{sub 4}/C composite.

  10. Assessment of four different cathode materials at different initial pHs using unbuffered catholytes in microbial electrolysis cells

    KAUST Repository

    Ribot-Llobet, Edgar

    2013-03-01

    Nickel foam (NF), stainless steel wool (SSW), platinum coated stainless steel mesh (Pt), and molybdenum disulfide coated stainless steel mesh (MoS 2) electrodes have been proposed as catalysts for hydrogen gas production, but previous tests have primarily examined their performance in well buffered solutions. These materials were compared using two-chamber microbial electrolysis cells (MECs), and linear sweep voltammetry (LSV) in unbuffered saline solutions at two different initial pHs (7 and 12). There was generally no appreciable effect of initial pH on production rates or total gas production. NF produced hydrogen gas at a rate of 1.1 m3 H2/m 3·d, which was only slightly less than that using Pt (1.4 m3 H2/m3·d), but larger than that obtained with SSW (0.52 m3 H2/m3·d) or MoS2 (0.67 m3 H2/m3·d). Overall hydrogen gas recoveries with SSW (29.7 ± 0.5 mL), MoS2 (28.6 ± 1.3 mL) and NF (32.4 ± 2 mL) were only slightly less than that of Pt (37.9 ± 0.5 mL). Total energy recoveries, based on the gas produced versus electrical energy input, ranged from 0.75 ± 0.02 for Pt, to 0.55 ± 0.02 for SSW. An LSV analysis showed no effect of pH for NF and Pt, but overpotentials were reduced for MoS2 and SSW by using an initial lower pH. At cathode potentials more negative than -0.85 V (vs Ag/AgCl), NF had lower overpotentials than the MoS2. These results provide the first assessment of these materials under practical conditions of high pH in unbuffered saline catholytes, and position NF as the most promising inexpensive alternative to Pt.

  11. Vanadium oxide based cpd. useful as a cathode active material - is used in lithium or alkali metal batteries to prolong life cycles

    DEFF Research Database (Denmark)

    1997-01-01

    A mixt. of metallic iron particles and vanadium pentoxide contg. V in its pentavalent state in a liq. is reacted to convert at least some of the pentavalent V to its tetravalent state and form a gel. The liq. phase is then sepd. from the oxide based gel to obtain a solid material(I) comprising Fe......, V and oxygen where at least some of the V is in the tetravalent state. USE-(I) is a cathode active material in electric current producing storage cells. ADVANTAGE-Use of (I) in Li or alkali metal batteries gives prolonged life cycles.Storage cells using (I) have improved capacity during charge...

  12. AB/sub 5/-catalyzed hydrogen evolution cathodes

    Energy Technology Data Exchange (ETDEWEB)

    Hall, D E; Sawada, T; Shepard, V R; Tsujikawa, Y

    1984-01-01

    The AB/sub 5/ metal compounds are highly efficient hydrogen evolution electrocatalysts in alkaline electrolyte. Three types of AB/sub 5/-catalyzed cathode structures were made, using the hydride-forming AB/sub 5/ compounds in particulate form. Plastic-bonded cathodes containing >90 w/o AB/sub 5/ (finished-weight basis) were the most efficient, giving hydrogen evolution overpotentials (/eta/ /SUB H2/ ) of about 0.05 V at 200 mA cm/sup -2/. However, they tended to swell and shed material during electrolysis. Pressed, sintered cathodes containing 40-70 w/o catalyst in a nickel binder gave /eta/ /SUB H2/ about0.08 V; catalyst retention was excellent. Porous, sintered cathode coatings were made with 30-70 w/o AB/sub 5/ catalyst loadings. Their overpotentials were similar to those of the pressed, sintered cathodes. However, at catalyst loadings below about 40 w/o, high overpotentials characteristic of the nickel binder were observed. The structural and electrochemical properties of the three AB/sub 5/-catalyzed cathodes are discussed.

  13. LaCoO3: Promising cathode material for protonic ceramic fuel cells based on a BaCe0.2Zr0.7Y0.1O3−δ electrolyte

    DEFF Research Database (Denmark)

    Ricote, Sandrine; Bonanos, Nikolaos; Lenrick, Filip

    2012-01-01

    Symmetric cells (cathode/electrolyte/cathode) were prepared using BaCe0.2Zr0.7Y0.1O3−δ (BCZY27) as proton conducting electrolyte and LaCoO3 (LC) infiltrated into a porous BCZY27 backbone as cathode. Single phased LC was formed after annealing in air at 600 °C for 2 h. Scanning electron micrograph...... that the presence of oxide ion conduction in the cathode material is not necessary for good performance.......Symmetric cells (cathode/electrolyte/cathode) were prepared using BaCe0.2Zr0.7Y0.1O3−δ (BCZY27) as proton conducting electrolyte and LaCoO3 (LC) infiltrated into a porous BCZY27 backbone as cathode. Single phased LC was formed after annealing in air at 600 °C for 2 h. Scanning electron micrographs...... showed the presence of the infiltrated LC in the full cathode depth. Transmission electron micrographs revealed LC grains (60–80 nm) covering partly the BCZY27 grains (200 nm–1 μm). Impedance spectra were recorded at 500 °C and 600 °C, varying the oxygen partial pressure and the water vapour pressure...

  14. Synthesis and characterization of a novel Gd0.9Ba0.1CoO3-δ SOFC cathode material

    International Nuclear Information System (INIS)

    Lenka, R.K.; Mahata, T.; Sinha, P.K.; Tyagi, A.K.

    2012-01-01

    Perovskite materials with general formula ABO 3 (A = La and other rare earth metals, Ca, Sr, Ba etc.; B = Mn, Fe, Co, Ni etc.) are widely used as cathode materials in SOFCs. Doped cobaltites are reported to have better electro-catalytic activities for oxygen reduction reaction as well as higher electronic conductivities than other electrode materials. However, thermal expansion coefficient values of many cobaltites are significantly higher than that of commonly used oxygen ion conducting electrolyte materials. Among the different rare earth metals that form lanthanide cobaltite perovskites the thermal expansion coefficients (TEC) of the cobaltites decrease in the order of La, Pr, Nd, Sm and Gd. TEC can be tailored by substituting 'A' sites or Co sites with suitable elements. In general, substitution of Co site decreases catalytic activity and electronic conductivity. Increase in ionic conductivity has been reported with substitution in the 'A' site. In the present investigation 10 mol% Ba substituted GdCoO 3 has been studied as a SOFC cathode material

  15. Combustion of crude oil sludge containing naturally occurring radioactive material

    International Nuclear Information System (INIS)

    Mohamad Puad Abu; Muhd Noor Muhd Yunus; Shamsuddin, A.H.; Sopian, K.

    2000-01-01

    The characteristics of crude oil sludge fi-om the crude oil terminal are very unique because it contains both heavy metals and also Naturally Occurring Radioactive Material (NORM). As a result, the Department of Environmental (DOE) and the Atomic Energy Licensing Board (AELB) considered it as Scheduled Wastes and Low Level Radioactive Waste (LLRW) respectively. As a Scheduled Wastes, there is no problem in dealing with the disposal of it since there already exist a National Center in Bukit Nanas to deal with this type of waste. However, the Center could not manage this waste due to the presence of NORM by which the policy regarding the disposal of this kind of waste has not been well established. This situation is unclear to certain parties, especially with respect to the relevant authorities having final jurisdiction over the issue as well as the best practical method of disposal of this kind of waste. Existing methods of treatment viewed both from literature and current practice include that of land farming, storing in plastic drum, re-injection into abandoned oil well, recovery, etc., found some problems. Due to its organic nature, very low level in radioactivity and the existence of a Scheduled Waste incineration facility in Bukit Nanas, there is a potential to treat this sludge by using thermal treatment technology. However, prior to having this suggestion to be put into practice, there are issues that need to be addressed. This paper attempts to discuss the potentials and the related issues of combusting crude oil sludge based on existing experimental data as well as mathematical modeling

  16. Evaluation of low cost cathode materials for treatment of industrial and food processing wastewater using microbial electrolysis cells

    KAUST Repository

    Tenca, Alberto

    2013-02-01

    Microbial electrolysis cells (MECs) can be used to treat wastewater and produce hydrogen gas, but low cost cathode catalysts are needed to make this approach economical. Molybdenum disulfide (MoS2) and stainless steel (SS) were evaluated as alternative cathode catalysts to platinum (Pt) in terms of treatment efficiency and energy recovery using actual wastewaters. Two different types of wastewaters were examined, a methanol-rich industrial (IN) wastewater and a food processing (FP) wastewater. The use of the MoS2 catalyst generally resulted in better performance than the SS cathodes for both wastewaters, although the use of the Pt catalyst provided the best performance in terms of biogas production, current density, and TCOD removal. Overall, the wastewater composition was more of a factor than catalyst type for accomplishing overall treatment. The IN wastewater had higher biogas production rates (0.8-1.8 m3/m3-d), and COD removal rates (1.8-2.8 kg-COD/m3-d) than the FP wastewater. The overall energy recoveries were positive for the IN wastewater (3.1-3.8 kWh/kg-COD removed), while the FP wastewater required a net energy input of -0.7 - 1.2 kWh/kg-COD using MoS 2 or Pt cathodes, and -3.1 kWh/kg-COD with SS. These results suggest that MoS2 is the most suitable alternative to Pt as a cathode catalyst for wastewater treatment using MECs, but that net energy recovery will be highly dependent on the specific wastewater. © 2012, Hydrogen Energy Publications, LLC. Published by Elsevier Ltd. All rights reserved.

  17. Development of Separation Materials Containing Palladium for Hydrogen Isotopes Separation

    International Nuclear Information System (INIS)

    Deng Xiaojun; Luo Deli; Qian Xiaojing

    2010-01-01

    Displacement chromatography (DC) is a ascendant technique for hydrogen isotopes separation. The performance of separation materials is a key factor to determine the separation effect of DC. At present,kinds of materials are researched, including palladium materials and non-palladium materials. It is hardly replaceable because of its excellent separation performance, although palladium is expensive. The theory of hydrogen isotopes separation using DC was introduced at a brief manner, while several palladium separation materials were expatiated in detail(Pd/K, Pd-Al 2 O 3 , Pd-Pt alloy). Development direction of separation materials for DC was forecasted elementarily. (authors)

  18. Structural changes and thermal stability of charged LiNixMnyCozO₂ cathode materials studied by combined in situ time-resolved XRD and mass spectroscopy.

    Science.gov (United States)

    Bak, Seong-Min; Hu, Enyuan; Zhou, Yongning; Yu, Xiqian; Senanayake, Sanjaya D; Cho, Sung-Jin; Kim, Kwang-Bum; Chung, Kyung Yoon; Yang, Xiao-Qing; Nam, Kyung-Wan

    2014-12-24

    Thermal stability of charged LiNixMnyCozO2 (NMC, with x + y + z = 1, x:y:z = 4:3:3 (NMC433), 5:3:2 (NMC532), 6:2:2 (NMC622), and 8:1:1 (NMC811)) cathode materials is systematically studied using combined in situ time-resolved X-ray diffraction and mass spectroscopy (TR-XRD/MS) techniques upon heating up to 600 °C. The TR-XRD/MS results indicate that the content of Ni, Co, and Mn significantly affects both the structural changes and the oxygen release features during heating: the more Ni and less Co and Mn, the lower the onset temperature of the phase transition (i.e., thermal decomposition) and the larger amount of oxygen release. Interestingly, the NMC532 seems to be the optimized composition to maintain a reasonably good thermal stability, comparable to the low-nickel-content materials (e.g., NMC333 and NMC433), while having a high capacity close to the high-nickel-content materials (e.g., NMC811 and NMC622). The origin of the thermal decomposition of NMC cathode materials was elucidated by the changes in the oxidation states of each transition metal (TM) cations (i.e., Ni, Co, and Mn) and their site preferences during thermal decomposition. It is revealed that Mn ions mainly occupy the 3a octahedral sites of a layered structure (R3̅m) but Co ions prefer to migrate to the 8a tetrahedral sites of a spinel structure (Fd3̅m) during the thermal decomposition. Such element-dependent cation migration plays a very important role in the thermal stability of NMC cathode materials. The reasonably good thermal stability and high capacity characteristics of the NMC532 composition is originated from the well-balanced ratio of nickel content to manganese and cobalt contents. This systematic study provides insight into the rational design of NMC-based cathode materials with a desired balance between thermal stability and high energy density.

  19. H1259 Container Foams: Performance Data on Aged Materials

    International Nuclear Information System (INIS)

    Linda Domeier

    2002-01-01

    Samples of the three cushioning foams used in the H1259 weapon storage container were obtained in 1997, 1998, 2000 and 2001 and tested for density, compression set and compressive strength using the same procedures specified for acceptance testing. Foams from six containers, all about 30 years old and located at Pantex, were evaluated. The bottom cushioning foam is a General Plastics polyurethane foam and the two side pads are rebonded polyurethane foams. All the tests were carried out at room temperature. When compared to the original acceptance requirements the foams were generally in-spec for density and compressive strength at 10% strain and were generally out-of-spec for compression set and compressive strength at 50% strain. Significant variability was noted in the performance of each foam sample and even more in the container-to-container foam performance. The container-to-container variability remains the major unknown in predicting the long-term suitability of these containers for continued use. The performance of the critical bottom cushion foams was generally more uniform and closer to the specified performance than that of the rebonded foams. It was judged that all the foams were adequate for continued use as storage container foams (not shipping) under controlled conditions to mitigate temperature extremes or high impact. This archived information is important in evaluations of the continued suitability for weapon storage use of the H1259 containers and other containers using the same foam cushions

  20. Recovery of valuable metals from waste cathode materials of spent lithium-ion batteries using mild phosphoric acid

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Xiangping, E-mail: chenxiangping101@163.com [School of Environmental Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China); Ma, Hongrui, E-mail: mahr@sust.edu.cn [School of Environmental Science and Engineering, Shaanxi University of Science & Technology, Xi’an 710021 (China); Luo, Chuanbao; Zhou, Tao [College of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China)

    2017-03-15

    Graphical abstract: Cobalt can be directly recovered as Co{sub 3}(PO{sub 4}){sub 2} from waste LiCoO{sub 2} using H{sub 3}PO{sub 4} as leaching and precipitating agent. - Highlights: • Phosphoric acid was innovatively used as leaching and precipitating agent. • Over 99% Co and Li can be separated and recovered in a single leaching step. • Co and Li can be separated under mild conditions of 40 °C and 0.7 M H{sub 3}PO{sub 4}. • Activation energy values for Co and Li are 7.3 and 10.168 kJ/mol. • Cobalt phosphate (97.1% in purity) can be obtained as the leaching product. - Abstract: Sustainable recycling of valuable metals from spent lithium-ion batteries (LIBs) may be necessary to alleviate the depletion of strategic metal resources and potential risk of environmental pollution. Herein a hydrometallurgical process was proposed to explore the possibility for the recovery of valuable metals from the cathode materials (LiCoO{sub 2}) of spent LIBs using phosphoric acid as both leaching and precipitating agent under mild leaching conditions. According to the leaching results, over 99% Co can be separated and recovered as Co{sub 3}(PO{sub 4}){sub 2} in a short-cut process involved merely with leaching and filtrating, under the optimized leaching conditions of 40 °C (T), 60 min (t), 4 vol.% H{sub 2}O{sub 2}, 20 mL g{sup −1} (L/S) and 0.7 mol/L H{sub 3}PO{sub 4}. Then leaching kinetics was investigated based on the logarithmic rate kinetics model and the obtained results indicate that the leaching of Co and Li fits well with this model and the activation energies (Ea) for Co and Li are 7.3 and 10.2 kJ/mol, respectively. Finally, it can be discovered from characterization results that the obtained product is 97.1% pure cobalt phosphate (Co{sub 3}(PO{sub 4}){sub 2}).

  1. Towards highly stable storage of sodium ions: a porous Na(3)V(2)(PO(4))(3)/C cathode material for sodium-ion batteries.

    Science.gov (United States)

    Shen, Wei; Wang, Cong; Liu, Haimei; Yang, Wensheng

    2013-10-18

    A porous Na3 V2 (PO4 )3 cathode material coated uniformly with a layer of approximately 6 nm carbon has been synthesized by the sol-gel method combined with a freeze-drying process. The special porous morphology and structure significantly increases the specific surface area of the material, which greatly enlarges the contact area between the electrode and electrolyte, and consequently supplies more active sites for sodium ions. When employed as a cathode material of sodium-ion batteries, this porous Na3 V2 (PO4 )3 /C exhibits excellent rate performance and cycling stability; for instance, it shows quite a flat potential plateau at 3.4 V in the potential window of 2.7-4.0 V versus Na(+) /Na and delivers an initial capacity as high as 118.9 and 98.0 mA h g(-1) at current rates of 0.05 and 0.5 C, respectively, and after 50 cycles, a good capacity retention of 92.7 and 93.6 % are maintained. Moreover, even when the discharge current density is increased to 5 C (590 mA g(-1) ), an initial capacity of 97.6 mA h g(-1) can still be achieved, and an exciting capacity retention of 88.6 % is obtained after 100 cycles. The good cycle performance, excellent rate capability, and moreover, the low cost of Na3 V2 (PO4 )3 /C suggest that this material is a promising cathode for large-scale sodium-ion rechargeable batteries. Copyright © 2013 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  2. Filtered cathodic arc source

    International Nuclear Information System (INIS)

    Falabella, S.; Sanders, D.M.

    1994-01-01

    A continuous, cathodic arc ion source coupled to a macro-particle filter capable of separation or elimination of macro-particles from the ion flux produced by cathodic arc discharge is described. The ion source employs an axial magnetic field on a cathode (target) having tapered sides to confine the arc, thereby providing high target material utilization. A bent magnetic field is used to guide the metal ions from the target to the part to be coated. The macro-particle filter consists of two straight solenoids, end to end, but placed at 45 degree to one another, which prevents line-of-sight from the arc spot on the target to the parts to be coated, yet provides a path for ions and electrons to flow, and includes a series of baffles for trapping the macro-particles. 3 figures

  3. Nanowire Na0.35MnO2 from a hydrothermal method as a cathode material for aqueous asymmetric supercapacitors

    Science.gov (United States)

    Zhang, B. H.; Liu, Y.; Chang, Z.; Yang, Y. Q.; Wen, Z. B.; Wu, Y. P.; Holze, R.

    2014-05-01

    Nanowire Na0.35MnO2 was prepared by a simple and low energy consumption hydrothermal method; its electrochemical performance as a cathode material for aqueous asymmetric supercapacitors in Na2SO4 solution was investigated. Due to the nanowire structure its capacitance (157 F g-1) is much higher than that of the rod-like Na0.95MnO2 (92 F g-1) from solid phase reaction although its sodium content is lower. When it is assembled into an asymmetric aqueous supercapacitor using activated carbon as the counter electrode and aqueous 0.5 mol L-1 Na2SO4 electrolyte solution, the nanowire Na0.35MnO2 shows an energy density of 42.6 Wh kg-1 at a power density of 129.8 W kg-1 based on the total weight of the two electrode material, higher than those for the rod-like Na0.95MnO2, with an energy density of 27.3 Wh kg-1 at a power density of 74.8 W kg-1, and that of LiMn2O4. The new material presents excellent cycling behavior even when dissolved oxygen is not removed from the electrolyte solution. The results hold great promise for practical applications of this cathode material since sodium is much cheaper than lithium and its natural resources are rich.

  4. In situ study of Li-ions diffusion and deformation in Li-rich cathode materials by using scanning probe microscopy techniques

    Science.gov (United States)

    Zeng, Kaiyang; Li, Tao; Tian, Tian

    2017-08-01

    In this paper, the scanning probe microscopy (SPM) based techniques, namely, conductive-AFM, electrochemical strain microscopy (ESM) and AM-FM (amplitude modulation-frequency modulation) techniques, are used to in situ characterize the changes in topography, conductivity and elastic properties of Li-rich layered oxide cathode (Li1.2Mn0.54Ni0.13Co0.13O2) materials, in the form of nanoparticles, when subject to the external electric field. Nanoparticles are the basic building blocks for composite cathode in a Li-ion rechargeable battery. Characterization of the structure and electrochemical properties of the nanoparticles is very important to understand the performance and reliability of the battery materials and devices. In this study, the conductivity, deformation and mechanical properties of the Li-rich oxide nanoparticles under different polarities of biases are studied using the above-mentioned SPM techniques. This information can be correlated with the Li+-ion diffusion and migration in the particles under external electrical field. The results also confirm that the SPM techniques are ideal tools to study the changes in various properties of electrode materials at nano- to micro-scales during or after the ‘simulated’ battery operation conditions. These techniques can also be used to in situ characterize the electrochemical performances of other energy storage materials, especially in the form of the nanoparticles.

  5. Hydrothermal synthesis and rate capacity studies of Li3V2(PO4)3 nanorods as cathode material for lithium-ion batteries

    International Nuclear Information System (INIS)

    Liu Haowen; Cheng Cuixia; Huang Xintang; Li Jinlin

    2010-01-01

    It is an effective method by synthesizing one-dimensional nanostructure to improve the rate performances of cathode materials for Li-ion batteries. In this paper, Li 3 V 2 (PO 4 ) 3 nanorods were successfully prepared by hydrothermal reaction method. The structure, composition and shape of the prepared were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scan electron microscope (SEM) and transmission electron microscope (TEM), respectively. The data indicate the as-synthesis powders are defect-rich nanorods and the sizes are the length of several hundreds of nanometers to 1 μm and the diameter of about 60 nm. The preferential growth direction of the prepared material was the [1 2 0]. The electrodes consisting of the Li 3 V 2 (PO 4 ) 3 nanorods show the better discharge capacities at high rates over a potential range of 3.0-4.6 V. These results can be attributed to the shorter distance of electron transport and the fact that ion diffusion in the electrode material is limited by the nanorod radius. All these results indicate that the resulting Li 3 V 2 (PO 4 ) 3 nanorods are promising cathode materials in lithium-ion batteries.

  6. Preparation of cathode materials for solid oxide solid fuel (SOFC) using gelatin; Preparacao de materiais catodicos para celulas a combustivel de oxido solido (SOFC) atraves do uso de gelatina

    Energy Technology Data Exchange (ETDEWEB)

    Silva, R.M.; Aquino, F. de M.; Macedo, D.A. de; Sa, A.M.; Galvao, G.O., E-mail: rinaldo_mendesa@hotmail.com [Universidade Federal da Paraiba (UFPB), Joao Pessoa, PB (Brazil)

    2016-07-01

    Fuel cells are electrochemical devices that convert chemical energy into electrical energy. These devices are basically divided into interconnectors, electrolyte, anode, and cathode. Recently, studies of improvements in microstructural and morphological properties of calcium cobaltate (Ca{sub 3}Co{sub 4}O{sub 9}, C349) has been made regarding its potential use as SOFC cathode for intermediate temperature. Gelatin has proven to be effective as a polymerizing agent in the synthesis of nanocrystalline materials. This work reports the synthesis and characterization of the C349 cathode using commercial gelatin. The structural properties of the material were determined by X-ray diffraction (XRD). Morphological characterization was performed by scanning electron microscopy (SEM). The results showed the formation of the crystalline phase at 900 °C, indicating the effectiveness of the gelatin in the preparation of cathodes for SOFC. (author)

  7. The preparation and graphene surface coating NaTi_2(PO_4)_3 as cathode material for lithium ion batteries

    International Nuclear Information System (INIS)

    Li, Na; Wang, Yanping; Rao, Richuan; Dong, Xiongzi; Zhang, Xianwen; Zhu, Sane

    2017-01-01

    Graphical abstract: The NaTi_2(PO_4)_3/graphene composite is used directly as cathode electrode material for lithium-ion battery by using metal lithium as an anode electrode. Meanwhile, the electrochemical properties of the composite in this system is firstly studied in detail. The NaTi_2(PO_4)_3/graphene composite exhibits the better rate and cyclic performance than NaTi_2(PO_4)_3, which is ascribed to its stable 3-D framework and the enhanced electronic conduction resulting from the graphene sheets surface modification. - Highlights: • The graphene coated NaTi_2(PO_4)_3 was prepared by a simple sol-gel method followed by calcination. • The electrochemical properties of the NaTi_2(PO_4)_3/graphene composite was firstly studied in detail when used as cathode electrode material for lithium-ion batteries. • The electrochemical reaction mechanism of NaTi_2(PO_4)_3/graphene composite was investigated by ex situ XRD. - Abstract: The graphene coated NaTi_2(PO_4)_3 has been fabricated via a simple sol-gel process followed by calcination. The NaTi_2(PO_4)_3/graphene (NTP/G) composite is used directly as cathode electrode material for lithium-ion battery and the electrochemical properties of the composite in this system is firstly studied in detail. In the charge-discharge process, two Li"+ can occupy octahedral M (2) site and be reversibly intercalated into the 3D framework of NTP through the ion conduction channel where almost all of Na"+ are immobilized to sustain the framework. At 5C rate, the capacity retention of the NTP/G composite after 800 cycles is still up to 82.7%. The superior electrochemical properties of NTP/G is ascribed to its stable 3-D framework and the enhanced electronic conduction resulting from the graphene sheets surface modification.

  8. Electrical conductivity and reaction with lithium of LiFe{sub 1-y}Mn{sub y}PO{sub 4} olivine-type cathode materials

    Energy Technology Data Exchange (ETDEWEB)

    Molenda, J.; Ojczyk, W.; Marzec, J. [Faculty of Materials Science and Ceramics, AGH University of Science and Technology, al. Mickiewicza 30, 30-059 Krakow (Poland)

    2007-12-06

    Structural, electrical and electrochemical properties of Mn-substituted phospho-olivines LiFe{sub 1-y}Mn{sub y}PO{sub 4} were investigated and compared to those of LiFePO{sub 4}. Rietvield refined XRD patterns taken in the course of delithiation process showed apparent difference between phase compositions of these cathode materials upon lithium extraction. Contrary to the LiFePO{sub 4} and LiMnPO{sub 4} compositions for which a two-phase mechanism of electrochemical lithium extraction/insertion is observed, in case of Mn-substituted LiFe{sub 1-y}Mn{sub y}PO{sub 4} samples a single-phase mechanism of deintercalation was observed in the studied range of lithium concentration. Electrochemical characterization of the cathode materials were performed in Li/Li{sup +}/Li{sub x}Fe{sub 1-y}Mn{sub y}PO{sub 4}-type cells for y = 0.0, 0.25, 0.55, 0.75 and 1.0 compositions. Voltammery studies showed low reversibility of the lithium extraction process in the high-voltage ''manganese'' range, while in the ''iron'' range the reversibility of lithium extraction is high. Impedance measurements of the LiFe{sub 1-y}Mn{sub y}PO{sub 4} cathode materials, which enabled separation of the ionic and electronic components of their entire electrical conductivity, showed distinct influence of Mn content on the electronic part of conductivity. EIS measurements performed at different states of cell charge revealed that the charge-transfer impedance in Li{sub x}Fe{sub 1-y}Mn{sub y}PO{sub 4} is much lower than that of Li{sub x}FePO{sub 4}. (author)

  9. Effect of Mg-doping on the degradation of LiNiO2-based cathode materials by combined spectroscopic methods

    OpenAIRE

    Muto, Shunsuke; Tatsumi, Kazuyoshi; Kojima, Yuji; Oka, Hideaki; Kondo, Hiroki; Horibuchi, Kayo; Ukyo, Yoshio

    2012-01-01

    The performance of a LiNiO2-based cell has been shown to be significantly improved by Mg-doping of LiNi0.8Co0.15Al0.05O2 (Mg-doped NCA) cathode materials. In the present study, the effects of Mg-doping were examined by electrochemical impedance spectroscopy (EIS) and scanning transmission electron microscopy-electron energy loss spectroscopy. EIS analysis revealed that the activation energy of Mg-doped NCA for the charge-transfer reaction was larger than that of undoped NCA by a factor of ∼10...

  10. Designing new lithium-excess cathode materials from percolation theory: nanohighways in Li(x)Ni(2-4x/3)Sb(x/3)O2.

    Science.gov (United States)

    Twu, Nancy; Li, Xin; Urban, Alexander; Balasubramanian, Mahalingam; Lee, Jinhyuk; Liu, Lei; Ceder, Gerbrand

    2015-01-14

    Increasing lithium content is shown to be a successful strategy for designing new cathode materials. In layered Li(x)Ni(2-4x/3)Sb(x/3)O2 (x = 1.00-1.15), lithium excess improves both discharge capacity and capacity retention at 1C. Structural studies reveal a complex nanostructure pattern of Li-Sb and Ni-Sb ordering where the interface between these domains forms the correct local configuration for good lithium mobility. The <1 nm Li-Sb stripe domains and their interfaces thereby effectively act as nanohighways for lithium diffusion.

  11. 19 CFR 10.601 - Retail packaging materials and containers.

    Science.gov (United States)

    2010-04-01

    ...-Central America-United States Free Trade Agreement Rules of Origin § 10.601 Retail packaging materials and...), HTSUS. (b) Effect on regional value content calculation. If the good is subject to a regional value... originating or non-originating materials, as the case may be, in calculating the regional value content of the...

  12. Development of neutron shielding concrete containing iron content materials

    Science.gov (United States)

    Sariyer, Demet; Küçer, Rahmi

    2018-02-01

    Concrete is one of the most important construction materials which widely used as a neutron shielding. Neutron shield is obtained of interaction with matter depends on neutron energy and the density of the shielding material. Shielding properties of concrete could be improved by changing its composition and density. High density materials such as iron or high atomic number elements are added to concrete to increase the radiation resistance property. In this study, shielding properties of concrete were investigated by adding iron, FeB, Fe2B, stainless - steel at different ratios into concrete. Neutron dose distributions and shield design was obtained by using FLUKA Monte Carlo code. The determined shield thicknesses vary depending on the densities of the mixture formed by the additional material and ratio. It is seen that a combination of iron rich materials is enhanced the neutron shielding of capabilities of concrete. Also, the thicknesses of shield are reduced.

  13. Synthesis and characterization of high-density LiFePO4/C composites as cathode materials for lithium-ion batteries

    International Nuclear Information System (INIS)

    Chang Zhaorong; Lv Haojie; Tang Hongwei; Li Huaji; Yuan Xiaozi; Wang Haijiang

    2009-01-01

    To achieve a high-energy-density lithium electrode, high-density LiFePO 4 /C composite cathode material for a lithium-ion battery was synthesized using self-produced high-density FePO 4 as a precursor, glucose as a C source, and Li 2 CO 3 as a Li source, in a pipe furnace under an atmosphere of 5% H 2 -95% N 2 . The structure of the synthesized material was analyzed and characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The electrochemical properties of the synthesized LiFePO 4 /carbon composite were investigated by cyclic voltammetry (CV) and the charge/discharge process. The tap-density of the synthesized LiFePO 4 /carbon composite powder with a carbon content of 7% reached 1.80 g m -3 . The charge/discharge tests show that the cathode material has initial charge/discharge capacities of 190.5 and 167.0 mAh g -1 , respectively, with a volume capacity of 300.6 mAh cm -3 , at a 0.1C rate. At a rate of 5C, the LiFePO 4 /carbon composite shows a high discharge capacity of 98.3 mAh g -1 and a volume capacity of 176.94 mAh cm -3 .

  14. One-step facile synthesis of Ni2P/C as cathode material for Ni/Zn aqueous secondary battery

    Science.gov (United States)

    Li, JiLan; Chen, ChangGuo

    2018-01-01

    Nickel phosphides/carbon(Ni2P/C) composites have been successfully synthesized via a simple one-pot hydrothermal method using glucose as carbon source for the first time. By contrast, the pure Ni2P was prepared under the same conditions without glucose. The results show that glucose not only provide the carbon source, but also prevent the aggregation of Ni2P particles. The as-obtained Ni2P/C composites and pure Ni2P were used as cathode material for alkaline Ni/Zn battery. Owing to unique Ni2P/C composites and loose, Ultra thin flower-like shape the synthesized Ni2P/C material delivers high capacity of 176 mAh g-1 at 1 A g-1 and 82 mAh g-1 at 5 A g-1 current density in Ni2P/C-Zn battery. Moreover, it shows a good cycling life that capacity fading only about 6.2% after 1500 cycles. All of these indicate that the prepared Ni2P/C composites may be a new promising cathode material for Ni-Zn rechargeable battery.

  15. Room temperature large-scale synthesis of layered frameworks as low-cost 4 V cathode materials for lithium ion batteries

    Science.gov (United States)

    Hameed, A. Shahul; Reddy, M. V.; Nagarathinam, M.; Runčevski, Tomče; Dinnebier, Robert E; Adams, Stefan; Chowdari, B. V. R.; Vittal, Jagadese J.

    2015-01-01

    Li-ion batteries (LIBs) are considered as the best available technology to push forward the production of eco-friendly electric vehicles (EVs) and for the efficient utilization of renewable energy sources. Transformation from conventional vehicles to EVs are hindered by the high upfront price of the EVs and are mainly due to the high cost of LIBs. Hence, cost reduction of LIBs is one of the major strategies to bring forth the EVs to compete in the market with their gasoline counterparts. In our attempt to produce cheaper high-performance cathode materials for LIBs, an rGO/MOPOF (reduced graphene oxide/Metal-Organic Phosphate Open Framework) nanocomposite with ~4 V of operation has been developed by a cost effective room temperature synthesis that eliminates any expensive post-synthetic treatments at high temperature under Ar/Ar-H2. Firstly, an hydrated nanocomposite, rGO/K2[(VO)2(HPO4)2(C2O4)]·4.5H2O has been prepared by simple magnetic stirring at room temperature which releases water to form the anhydrous cathode material while drying at 90 °C during routine electrode fabrication procedure. The pristine MOPOF material undergoes highly reversible lithium storage, however with capacity fading. Enhanced lithium cycling has been witnessed with rGO/MOPOF nanocomposite which exhibits minimal capacity fading thanks to increased electronic conductivity and enhanced Li diffusivity. PMID:26593096

  16. Synthesis and electrochemical characterization of mesoporous Li2FeSiO4/C composite cathode material for Li-ion batteries

    Science.gov (United States)

    Kumar, Ajay; Jayakumar, O. D.; Bazzi, Khadije; Nazri, Gholam-Abbas; Naik, Vaman M.; Naik, Ratna

    2015-03-01

    Lithium iron silicate (Li2FeSiO4) has the potential as cathode for Li ion batteries due to its high theoretical capacity (~ 330 mAh/g) and improved safety. The application of Li2FeSiO4 as cathode material has been challenged by its poor electronic conductivity and slow lithium ion diffusion in the solid phase. In order to solve these problems, we have synthesized mesoporous Li2FeSiO4/C composites by sol-gel method using the tri-block copolymer (P123) as carbon source. The phase purity and morphology of the composite materials were characterized by x-ray diffraction, SEM and TEM. The XRD pattern confirmed the formation of ~ 12 nm size Li2FeSiO4 crystallites in composites annealed at 600 °C for 6 h under argon atmosphere. The electrochemical properties are measured using the composite material as positive electrode in a standard coin cell configuration with lithium as the active anode and the cells were tested using AC impedance spectroscopy, cyclic voltammetry, and galvanostatic charge/discharge cycling. The Li2FeSiO4/C composites showed a discharge capacity of ~ 240 mAh/g at a rate of C/30 at room temperature. The effect of different annealing temperature and synthesis time on the electrochemical performance of Li2FeSiO4/C will be presented.

  17. Room temperature large-scale synthesis of layered frameworks as low-cost 4 V cathode materials for lithium ion batteries

    Science.gov (United States)

    Hameed, A. Shahul; Reddy, M. V.; Nagarathinam, M.; Runčevski, Tomče; Dinnebier, Robert E.; Adams, Stefan; Chowdari, B. V. R.; Vittal, Jagadese J.

    2015-11-01

    Li-ion batteries (LIBs) are considered as the best available technology to push forward the production of eco-friendly electric vehicles (EVs) and for the efficient utilization of renewable energy sources. Transformation from conventional vehicles to EVs are hindered by the high upfront price of the EVs and are mainly due to the high cost of LIBs. Hence, cost reduction of LIBs is one of the major strategies to bring forth the EVs to compete in the market with their gasoline counterparts. In our attempt to produce cheaper high-performance cathode materials for LIBs, an rGO/MOPOF (reduced graphene oxide/Metal-Organic Phosphate Open Framework) nanocomposite with ~4 V of operation has been developed by a cost effective room temperature synthesis that eliminates any expensive post-synthetic treatments at high temperature under Ar/Ar-H2. Firstly, an hydrated nanocomposite, rGO/K2[(VO)2(HPO4)2(C2O4)]·4.5H2O has been prepared by simple magnetic stirring at room temperature which releases water to form the anhydrous cathode material while drying at 90 °C during routine electrode fabrication procedure. The pristine MOPOF material undergoes highly reversible lithium storage, however with capacity fading. Enhanced lithium cycling has been witnessed with rGO/MOPOF nanocomposite which exhibits minimal capacity fading thanks to increased electronic conductivity and enhanced Li diffusivity.

  18. Cathodic protection for the bottoms of above ground storage tanks

    Energy Technology Data Exchange (ETDEWEB)

    Mohr, John P. [Tyco Adhesives, Norwood, MA (United States)

    2004-07-01

    Impressed Current Cathodic Protection has been used for many years to protect the external bottoms of above ground storage tanks. The use of a vertical deep ground bed often treated several bare steel tank bottoms by broadcasting current over a wide area. Environmental concerns and, in some countries, government regulations, have introduced the use of dielectric secondary containment liners. The dielectric liner does not allow the protective cathodic protection current to pass and causes corrosion to continue on the newly placed tank bottom. In existing tank bottoms where inadequate protection has been provided, leaks can develop. In one method of remediation, an old bottom is covered with sand and a double bottom is welded above the leaking bottom. The new bottom is welded very close to the old bottom, thus shielding the traditional cathodic protection from protecting the new bottom. These double bottoms often employ the use of dielectric liner as well. Both the liner and the double bottom often minimize the distance from the external tank bottom. The minimized space between the liner, or double bottom, and the bottom to be protected places a challenge in providing current distribution in cathodic protection systems. This study examines the practical concerns for application of impressed current cathodic protection and the types of anode materials used in these specific applications. One unique approach for an economical treatment using a conductive polymer cathodic protection method is presented. (author)

  19. Impacts of cathodic protection on waste package performance

    International Nuclear Information System (INIS)

    Atkins, J.E.; Lee, J.H.; Andrews, R.W.

    1996-01-01

    The current design concept for a multi-barrier waste container for the potential repository at Yucca Mountain, Nevada, calls for an outer barrier of 100 mm thick corrosion-allowance material (CAM) (carbon steel) and an inner barrier of 20 mm thick corrosion-resistant material (CRM) (Alloy 825). Fulfillment of the NRC subsystem requirements (10 CFR 60.113) of substantially complete containment and controlled release of radionuclides from the engineered barrier system (EBS) will rely mostly upon the robust waste container design, among other EBS components. In the current waste container design, some degree of cathodic protection of CRM will be provided by CAM. This paper discusses a sensitivity case study for the impacts of cathodic protection of the inner barrier by the outer barrier on the performance of waste package

  20. Microscopical characterization of carbon materials derived from coal and petroleum and their interaction phenomena in making steel electrodes, anodes and cathode blocks for the Microscopy of Carbon Materials Working Group of the ICCP

    Science.gov (United States)

    Predeanu, G.; Panaitescu, C.; Bălănescu, M.; Bieg, G.; Borrego, A.G.; Diez, M. A.; Hackley, Paul C.; Kwiecińska, B.; Marques, M.; Mastalerz, Maria; Misz-Kennan, M.; Pusz, S.; Suarez-Ruiz, I.; Rodrigues, S.; Singh, A. K.; Varma, A. K.; Zdravkov, A.; Zivotić, D.

    2015-01-01

    This paper describes the evaluation of petrographic textures representing the structural organization of the organic matter derived from coal and petroleum and their interaction phenomena in the making of steel electrodes, anodes and cathode blocks.This work represents the results of the Microscopy of Carbon Materials Working Group in Commission III of the International Committee for Coal and Organic Petrology between the years 2009 and 2013. The round robin exercises were run on photomicrograph samples. For textural characterization of carbon materials the existing ASTM classification system for metallurgical coke was applied.These round robin exercises involved 15 active participants from 12 laboratories who were asked to assess the coal and petroleum based carbons and to identify the morphological differences, as optical texture (isotropic/anisotropic), optical type (punctiform, mosaic, fibre, ribbon, domain), and size. Four sets of digital black and white microphotographs comprising 151 photos containing 372 fields of different types of organic matter were examined. Based on the unique ability of carbon to form a wide range of textures, the results showed an increased number of carbon occurrences which have crucial role in the chosen industrial applications.The statistical method used to evaluate the results was based on the “raw agreement indices”. It gave a new and original view on the analysts' opinion by not only counting the correct answers, but also all of the knowledge and experience of the participants. Comparative analyses of the average values of the level of overall agreement performed by each analyst in the exercises during 2009–2013 showed a great homogeneity in the results, the mean value being 90.36%, with a minimum value of 83% and a maximum value of 95%.

  1. Characterization of Concrete Mixes Containing Phase Change Materials

    Science.gov (United States)

    Paksoy, H.; Kardas, G.; Konuklu, Y.; Cellat, K.; Tezcan, F.

    2017-10-01

    Phase change materials (PCM) can be used in passive building applications to achieve near zero energy building goals. For this purpose PCM can be added in building structures and materials in different forms. Direct incorporation, form stabilization and microencapsulation are different forms used for PCM integration in building materials. In addition to thermal properties of PCM itself, there are several other criteria that need to be fulfilled for the PCM enhanced building materials. Mechanical properties, corrosive effects, morphology and thermal buffering have to be determined for reliable and long-term applications in buildings. This paper aims to give an overview of characterization methods used to determine these properties in PCM added fresh concrete mixes. Thermal, compressive strength, corrosion, and microscopic test results for concrete mixes with PCM are discussed.

  2. Evaluation of Ca3(Co,M2O6 (M=Co, Fe, Mn, Ni as new cathode materials for solid-oxide fuel cells

    Directory of Open Access Journals (Sweden)

    Fushao Li

    2015-10-01

    Full Text Available Series compounds Ca3(Co0.9M0.12O6 (M=Co, Fe, Mn, Ni with hexagonal crystal structure were prepared by sol–gel route as the cathode materials for solid oxide fuel cells (SOFCs. Effects of the varied atomic compositions on the structure, electrical conductivity, thermal expansion and electrochemical performance were systematically evaluated. Experimental results showed that the lattice parameters of Ca3(Co0.9Fe0.12O6 and Ca3(Co0.9Mn0.12O6 were both expanded to certain degree. Electron-doping and hole-doping effects were expected in Ca3(Co0.9Mn0.12O6 and Ca3(Co0.9Ni0.12O6 respectively according to the chemical states of constituent elements and thermal-activated behavior of electrical conductivity. Thermal expansion coefficients (TEC of Ca3(Co0.9M0.12O6 were measured to be distributed around 16×10−6 K−1, and compositional elements of Fe, Mn, and Ni were especially beneficial for alleviation of the thermal expansion problem of cathode materials. By using Ca3(Co0.9M0.12O6 as the cathodes operated at 800 °C, the interfacial area-specific resistance varied in the order of M=Cocathode materials for SOFCs.

  3. Improve electrochemical performance of CeO2 surface modification LiNi0.80Co0.15Al0.05O2 cathode material

    Science.gov (United States)

    Xia, Shubiao; Zhang, Yingjie; Dong, Peng; Zhang, Yannan

    2014-06-01

    Lithium ion battery cathode material LiNi0.8Co0.15Al0.05O2 cathode has successfully prepared by co-precipitation. CeO2 surface modification has improved LiNi0.80Co0.15Al0.05O2 electrochemical performance use sol-gel method and subsequent heat treatment at 600 °C for 5 h. Different to other conventional coating material, CeO2 coating layer can not only inhibit the reaction of the electrode and the electrolyte, but also can reduce the impedance of electron transfer due to its high conductivity, and inhibit the production of Ni2+ because of its high oxidation. The surface-modified and pristine LiNi0.80Co0.15Al0.05O2 powders are characterized by XRD, SEM, TEM, XPS, CV and DSC. When CeO2 coating is 0.02% (mole ratio), contrast to pristine NCA, the CeO2-coated NCA cathode exhibits no decrease in its initial specific capacity of 184 mAh g -1 (at 0.2 C) and excellent capacity retention (86% of its initial capacity at 1 C) between 2.75 and 4.3 V after 100 cycles. The results indicate that the CeO2 surface treatment should be an effective way to improve cycle properties due to CeO2 inhibit the electrodes and the electrolyte side effects.

  4. A facile method of preparing LiMnPO4/reduced graphene oxide aerogel as cathodic material for aqueous lithium-ion hybrid supercapacitors

    Science.gov (United States)

    Xu, Lin; Wang, Senlin; Zhang, Xiao; He, Taobin; Lu, Fengxia; Li, Huichang; Ye, Junhui

    2018-01-01

    A facile method of preparing LiMnPO4/reduced graphene oxide aerogel (LMP/rGO) as cathodic material was reported here. LiMnPO4 nano-particles were prepared using a facile polyvinyl pyrrolidone-assisted solvothermal route. Then LMP/rGO aerogel was prepared using the accessible restacking method. The influence of the cathodic electrode composition (ratio of rGO to LiMnPO4) on the performance of the LMP/rGO was evaluated by constant-current discharge tests. When compared with 217C g-1 for the pristine LMP, the best LMP/rGO (the content of rGO is 27.3 wt%) exhibits a higher capacity of 464.5C g-1 (at 0.5 A g-1), which presenting the capacity enhance of 114%. Moreover, a lithium-ion hybrid supercapacitor (LIHS) was successfully assembled by using LMP/rGO aerogel as the cathodic electrode and rGO aerogel as the anodic electrode. The LMP/rGO//rGO device achieves excellent specific energy of 16.46 W h kg-1 at a power density of 0.38 kW kg-1, even under the higher specific power of 4.52 kW kg-1, there still holds the specific energy of 11.79 W h kg-1. The LMP/rGO//rGO device maintains 91.2% of the initial capacity after 10,000 cycles (at 2 A g-1), which displays high rate performance and long cycle life. The 3D LMP/rGO aerogel could be a promising candidate material for the lithium-ion hybrid supercapacitors.

  5. Polyaniline/multi-walled carbon nanotubes composite with core-shell structures as a cathode material for rechargeable lithium-polymer cells

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Pan [School of Marine Science and Technology, Harbin Institute of Technology, Weihai 264209 (China); Han, Jia-Jun, E-mail: hanjiajunhitweihai@163.com [School of Marine Science and Technology, Harbin Institute of Technology, Weihai 264209 (China); Jiang, Li-Feng [Dalian Chemical Institute of Chinese Academy of Sciences, Dalian 116011 (China); Li, Zhao-Yu; Cheng, Jin-Ning [School of Marine Science and Technology, Harbin Institute of Technology, Weihai 264209 (China)

    2017-04-01

    Highlights: • The polyaniline multi-walled carbon nanotubes composite with core-shell structures was synthetized via in situ chemical oxidative polymerization, and the materials were characterized by physical and chemical methods. • The PANI/WMCNTs was synthetized via in situ chemical oxidative polymerization with core-shell structures. • The WMCNTs highly enhanced the conductivity of composites. • The comopsites were more conducive to the intercalation and deintercalation of anions and cations. • The much better performance as the cathode for lithium-ion cells was acquired for the composites. • The composites are low cost and eco-friendly which have a good prospect in future. - Abstract: The aniline was polymerized onto functionalized multi-walled carbon nanotubes in order to obtain a cathode material with core-shell structures for lithium batteries. The structure and morphology of the samples were investigated by Fourier transform infrared spectroscopy analysis, scanning electron microscope, transmission electron microscope and X-ray diffraction. The electrochemical properties of the composite were characterized by the cyclic voltammetry, the charge/discharge property, coulombic efficiency, and ac impedance spectroscopy in detail. At a constant current density of 0.2 C, the first specific discharge capacity of the reduced and oxidized PANI/WMCNTs were 181.8 mAh/g and 135.1 mAh/g separately, and the capacity retention rates were corresponding to 76.75% and 86.04% for 100 cycles with 99% coulombic efficiency. It was confirmed that the CNTs obviously enhanced the conductivity and electrochemical performance of polyaniline, and compared with the pure PANI, the reduced composite possessed a quite good performance for the cathode of lithium batteries.

  6. Experimental analysis of plastic materials containing radionuclides for decontamination viability

    International Nuclear Information System (INIS)

    Tazaki, Kazue; Nakano, Mikio; Takehara, Teruaki; Ishigaki, Yasuhito; Nakagawa, Hideaki

    2015-01-01

    After the Fukushima Daiichi Nuclear Power Plant (FDNPP) accident on 11 March, 2011, the high radioactive dosage was found in polluted water for agriculture use at Baba, Haramachi, Minami-Soma, Fukushima Prefecture, Japan. Field experiment for decontamination of water had been studied by using commercial plastic materials. The agricultural water comes from Tetsuzan dam is full of radioactive-contaminated water. Experimental analysis showed that the plastic materials can take up radioactive elements for several months soaked in the polluted agricultural water. The quantitative analyses using X-ray fluorescence analysis, Ge semiconductor and scanning electron microscopy equipped with energy dispersive X-ray spectrometer (SEM-EDS), revealed the detection of the radionuclides on the plastic materials with diatom and clays. The results suggest the adsorption of radionuclides on the surface of plastic materials due to FDNPP accident. The plastic materials associated with clays and diatoms could be stronger carriers of radionuclides in the polluted water. Adherence of diatoms to the plastic fiber in the water for 7 months suggested that some plastic materials were taking up heavy metals (Zn, Ba, Pb, Sb) with radioactive elements (Cs etc.). Mechanisms by which radioactive pollutants and microorganisms are adsorbed onto and desorbed from clays at aqueous interface can be understood by combining chemical analysis with electron microscopy observation. (author)

  7. Lithium nickel cobalt manganese oxide synthesized using alkali chloride flux: morphology and performance as a cathode material for lithium ion batteries.

    Science.gov (United States)

    Kim, Yongseon

    2012-05-01

    Li(Ni(0.8)Co(0.1)Mn(0.1))O(2) (NCM811) was synthesized using alkali chlorides as a flux and the performance as a cathode material for lithium ion batteries was examined. Primary particles of the powder were segregated and grown separately in the presence of liquid state fluxes, which induced each particle to be composed of one primary particle with well-developed facet planes, not the shape of agglomerates as appears with commercial NCMs. The new NCM showed far less gas emission during high temperature storage at charged states, and higher volumetric capacity thanks to its high bulk density. The material is expected to provide optimal performances for pouch type lithium ion batteries, which require high volumetric capacity and are vulnerable to deformation caused by gas generation from the electrode materials.

  8. New CSA guideline for the exemption or clearance from regulatory control of materials that contain, or potentially contain, nuclear substances

    International Nuclear Information System (INIS)

    Rhodes, M.; Kwong, A.

    2011-01-01

    The Canadian Standards Association (CSA) guideline N292.5, Guideline for the exemption or clearance from regulatory control of materials that contain, or potentially contain, nuclear substances, was recently developed to address a need for guidance on approaches for clearance of materials from facilities licensed by the Canadian Nuclear Safety Commission (CNSC) consistent with Canadian and international recommendations. This guideline is also applicable to determining if an activity associated with materials that contain nuclear substances is exempt from requiring a CNSC licence. The guideline summarizes the regulatory requirements associated with the exemption and clearance of materials and provides a graded approach to designing a survey based on the risk of residual contamination being present. (author)

  9. Polymers Containing 1, 3, 4-Oxadiazole Rings for Advanced Materials

    Directory of Open Access Journals (Sweden)

    Mariana-Dana Damaceanu

    2011-10-01

    Full Text Available This paper presents the synthesis, properties and potential applications of new polymers containing 1, 3, 4-oxadiazole rings, tacking into account the requirements of the modern technologies. Two classes of polymers containing oxadiazole rings were approached: polyamides and polyimides. All the polymers were characterized with respect to the identification of their chemical structure, solubility, molecular weights, film forming ability, thermal, dielectric and optical properties, and the behaviour of polyoxadiazole films upon irradiation with pulsed KrF laser. All the properties were discussed in correlation with their chemical structure and compared with those of related polymers.

  10. Synthesis and properties of Li{sub 2}MnO{sub 3}-based cathode materials for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Xue, Leigang; Zhang, Shu; Li, Shuli; Lu, Yao; Toprakci, Ozan [Fiber and Polymer Science Program, Department of Textile Engineering, Chemistry and Science, North Carolina State University, Raleigh, NC 27695-8301 (United States); Xia, Xin [Fiber and Polymer Science Program, Department of Textile Engineering, Chemistry and Science, North Carolina State University, Raleigh, NC 27695-8301 (United States); College of Textile and Clothing, Xinjiang University, Xinjiang, Urumchi 830046 (China); Chen, Chen [College of Textile and Clothing, Xinjiang University, Xinjiang, Urumchi 830046 (China); Hu, Yi [Fiber and Polymer Science Program, Department of Textile Engineering, Chemistry and Science, North Carolina State University, Raleigh, NC 27695-8301 (United States); Engineering Research Center for Eco-Dyeing and Finishing of Textiles, Zhejiang Sci-Tech University, Hangzhou, Zhejiang 310018 (China); Zhang, Xiangwu, E-mail: xiangwu_zhang@ncsu.edu [Fiber and Polymer Science Program, Department of Textile Engineering, Chemistry and Science, North Carolina State University, Raleigh, NC 27695-8301 (United States)

    2013-11-15

    Highlights: •0.3Li{sub 2}MnO{sub 3}·0.5LiMn{sub 0.5}Ni{sub 0.5}O{sub 2}·0.2LiCoO{sub 2} was synthesized by a co-precipitation method. •The preparation method is simple and this material is inexpensive due to the high contents of Mn and Ni. •The material could be charged to a high potential to extract more lithium without structural damage. •A relatively high capacity of 178 mAh g{sup −1} is delivered between 2.0 and 4.6 V with excellent cycling performance. -- Abstract: Lithium-ion batteries have been wildly used in various portable electronic devices and the application targets are currently moving from small-sized mobile devices to large-scale electric vehicles and grid energy storage. Therefore, lithium-ion batteries with higher energy densities are in urgent need. For high-energy cathodes, Li{sub 2}MnO{sub 3}–LiMO{sub 2} layered–layered (M = Mn, Co, Ni) materials are of significant interest due to their high specific capacities over wide operating potential windows. Here, three Li{sub 2}MnO{sub 3}-based cathode materials with α-NaFeO{sub 2} structure were prepared by a facile co-precipitation method and subsequent heat treatment. Among these three materials, 0.3Li{sub 2}MnO{sub 3}·0.5LiMn{sub 0.5}Ni{sub 0.5}O{sub 2}·0.2LiCoO{sub 2} shows the best lithium storage capability. This cathode material is composed of uniform nanosized particles with diameters ranging from 100 to 200 nm, and it could be charged to a high cutoff potential to extract more lithium, resulting in a high capacity of 178 mAh g{sup −1} between 2.0 and 4.6 V with almost no capacity loss over 100 cycles.

  11. The influence of reduced graphene oxide on electrical conductivity of LiFePO{sub 4}-based composite as cathode material

    Energy Technology Data Exchange (ETDEWEB)

    Arifin, Muhammad; Aimon, Akfiny Hasdi; Winata, Toto; Abdullah, Mikrajuddin [Physics of Electronic Materials Research Division, Department of Physics, Institut Teknologi Bandung, Bandung 40132 Indonesia (Indonesia); Iskandar, Ferry, E-mail: ferry@fi.itb.ac.id [Physics of Electronic Materials Research Division, Department of Physics, Institut Teknologi Bandung, Bandung 40132 Indonesia (Indonesia); Research Center for Nanoscience and Nanotechnology Institut Teknologi Bandung, Bandung 40132 Indonesia (Indonesia)

    2016-02-08

    LiFePO{sub 4} is fascinating cathode active materials for Li-ion batteries application because of their high electrochemical performance such as a stable voltage at 3.45 V and high specific capacity at 170 mAh.g{sup −1}. However, their low intrinsic electronic conductivity and low ionic diffusion are still the hindrance for their further application on Li-ion batteries. Therefore, the efforts to improve their conductivity are very important to elevate their prospecting application as cathode materials. Herein, we reported preparation of additional of reduced Graphene Oxide (rGO) into LiFePO{sub 4}-based composite via hydrothermal method and the influence of rGO on electrical conductivity of LiFePO{sub 4}−based composite by varying mass of rGO in composition. Vibration of LiFePO{sub 4}-based composite was detected on Fourier Transform Infrared Spectroscopy (FTIR) spectra, while single phase of LiFePO{sub 4} nanocrystal was observed on X-Ray Diffraction (XRD) pattern, it furthermore, Scanning Electron Microscopy (SEM) images showed that rGO was distributed around LiFePO4-based composite. Finally, the 4-point probe measurement result confirmed that the optimum electrical conductivity is in additional 2 wt% rGO for range 1 to 2 wt% rGO.

  12. Synthesis of three-dimensionally interconnected sulfur-rich polymers for cathode materials of high-rate lithium-sulfur batteries

    Science.gov (United States)

    Kim, Hoon; Lee, Joungphil; Ahn, Hyungmin; Kim, Onnuri; Park, Moon Jeong

    2015-06-01

    Elemental sulfur is one of the most attractive cathode active materials in lithium batteries because of its high theoretical specific capacity. Despite the positive aspect, lithium-sulfur batteries have suffered from severe capacity fading and limited rate capability. Here we report facile large-scale synthesis of a class of organosulfur compounds that could open a new chapter in designing cathode materials to advance lithium-sulfur battery technologies. Porous trithiocyanuric acid crystals are synthesized for use as a soft template, where the ring-opening polymerization of elemental sulfur takes place along the thiol surfaces to create three-dimensionally interconnected sulfur-rich phases. Our lithium-sulfur cells display discharge capacity of 945 mAh g-1 after 100 cycles at 0.2 C with high-capacity retention of 92%, as well as lifetimes of 450 cycles. Particularly, the organized amine groups in the crystals increase Li+-ion transfer rate, affording a rate performance of 1210, mAh g-1 at 0.1 C and 730 mAh g-1 at 5 C.

  13. Synthesis of three-dimensionally interconnected sulfur-rich polymers for cathode materials of high-rate lithium–sulfur batteries

    Science.gov (United States)

    Kim, Hoon; Lee, Joungphil; Ahn, Hyungmin; Kim, Onnuri; Park, Moon Jeong

    2015-01-01

    Elemental sulfur is one of the most attractive cathode active materials in lithium batteries because of its high theoretical specific capacity. Despite the positive aspect, lithium–sulfur batteries have suffered from severe capacity fading and limited rate capability. Here we report facile large-scale synthesis of a class of organosulfur compounds that could open a new chapter in designing cathode materials to advance lithium–sulfur battery technologies. Porous trithiocyanuric acid crystals are synthesized for use as a soft template, where the ring-opening polymerization of elemental sulfur takes place along the thiol surfaces to create three-dimensionally interconnected sulfur-rich phases. Our lithium–sulfur cells display discharge capacity of 945 mAh g−1 after 100 cycles at 0.2 C with high-capacity retention of 92%, as well as lifetimes of 450 cycles. Particularly, the organized amine groups in the crystals increase Li+-ion transfer rate, affording a rate performance of 1210, mAh g−1 at 0.1 C and 730 mAh g−1 at 5 C. PMID:26065407

  14. Synthesis of LiFePO4/Graphene Nano composite and Its Electrochemical Properties as Cathode Material for Li-Ion Batteries

    International Nuclear Information System (INIS)

    Ma, X.; Chen, G.; Liu, Q.; Zeng, G.; Wu, T.

    2014-01-01

    LiFePO 4 /graphene nano composite was successfully synthesized by rheological phase method and its electrochemical properties as the cathode materials for lithium ion batteries were measured. As the iron source in the synthesis, FeOOH nano rods anchored on graphene were first synthesized. The FeOOH nano rods precursors and the final LiFePO 4 /graphene nano composite products were characterized by XRD, SEM, and TEM. While the FeOOH precursors were nano rods with 5-10 nm in diameter and 10-50 nm in length, the LiFePO 4 were nanoparticles with 20-100 nm in size. Compared with the electrochemical properties of LiFePO 4 particles without graphene nano sheets, it is clear that the graphene nano sheets can improve the performances of LiFePO 4 as the cathode material for lithium ion batteries. The as-synthesized LiFePO 4 /graphene nano composite showed high capacities and good cyclabilities. When measured at room temperature and at the rate of 0.1 C (1 C = 170 mA g -1 ), the composite showed a discharge capacity of 156 mA h g -1 in the first cycle and a capacity retention of 96% after 15 cycles. The improved performances of the composite are believed to be the result of the three-dimensional conducting network formed by the flexible and planar graphene nano sheets.

  15. Evaluation of GdBaCo{sub 2}O{sub 5+{delta}} as cathode material for doped lanthanum gallate electrolyte IT-SOFCs

    Energy Technology Data Exchange (ETDEWEB)

    Tarancon, A. [Department of Inorganic Chemistry, University of La Laguna, La Laguna, Tenerife (Spain); EME/XaRMAE/IN, Department of Electronics, University of Barcelona (Spain); Marrero-Lopez, D.; Ruiz-Morales, J.C.; Nunez, P. [Department of Inorganic Chemistry, University of La Laguna, La Laguna, Tenerife (Spain); Pena-Martinez, J.

    2008-10-15

    The layered perovskite GdBaCo{sub 2}O{sub 5+{delta}} (GBCO), recently proposed for intermediate temperature solid oxide fuel cell applications, was investigated and compared with Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-{delta}} (BSCF) cathode material using La{sub 0.9}A{sub 0.1}Ga{sub 0.8}Mg{sub 0.2}O{sub 2.85} (A=Sr,Ba) as electrolytes. Area-specific resistance was measured by impendance spectroscopy in symmetrical cells. The cobaltites were prepared by a modified citrate sol-gel route and tested as cathode materials for doped lanthanum gallate-based cells using dry H{sub 2} as fuel and air as oxidant, rendering power density values of 180 and 240 mW cm {sup -2} at 1,073 K (1 mm thick pellets) for GBCO and BSCF fuel cells, respectively. (Abstract Copyright [2008], Wiley Periodicals, Inc.)

  16. Influence of thermal-decomposition temperatures on structures and properties of V2O5 as cathode materials for lithium ion battery

    Directory of Open Access Journals (Sweden)

    Yu Chen

    2015-02-01

    Full Text Available Submicron spherical V2O5 particles with a uniform size and a lower crystallinity were successfully synthesized by a chemical precipitation-thermal decomposition technique using the commercial V2O5 powders as starting material. The crystal structure and grain morphology of samples were characterized by X-ray diffraction (XRD and scanning electron microscopy (SEM, respectively. Electrochemical testing such as discharge–charge cycling (CD and cyclic voltammetry (CV were employed in evaluating their electrochemical properties as cathode materials for lithium ion battery. Results reveal that the crystallinity and crystalline size of V2O5 particles increased when the thermal-decomposition temperature increased from 400 °C to 500 °C, and their adhesiveness was also synchronously increased. This indicate that the thermal-decomposition temperature palyed a significant influence on electrochemical properties of V2O5 cathodes. The V2O5 sample obtained at 400 °C delivered not only a high initial discharge capacity of 330 mA h g−1 and also the good cycle stability during 50 cycles due to its higher values of α in crystal structure and better dispersity in grain morphology.

  17. Fabrication and characterization of Cu/YSZ cermet high temperature electrolysis cathode material prepared by high-energy ball-milling method

    International Nuclear Information System (INIS)

    Lee, Sungkyu; Kim, Jong-Min; Hong, Hyun Seon; Woo, Sang-Kook

    2009-01-01

    Cu/YSZ cermet (40 and 60 vol.% Cu powder with balance YSZ) is a more economical cathode material than the conventional Ni/YSZ cermet for high temperature electrolysis (HTE) of water vapor and it was successfully fabricated by high-energy ball-milling of Cu and YSZ powders, pressing into pellets (o 13 mm x 2 mm) and subsequent sintering process at 700 deg. C under flowing 5%-H 2 /Ar gas. The Cu/YSZ composite material thus fabricated was characterized using various analytical tools such as XRD, SEM, and laser diffraction and scattering method. Electrical conductivity of sintered Cu/YSZ cermet pellets thus fabricated was measured by using 4-probe technique for comparison with that of conventional Ni/YSZ cermets. The effect of composite composition on the electrical conductivity was investigated and a marked increase in electrical conductivity for copper contents greater than 40 vol.% in the composite was explained by percolation threshold. Also, Cu/YSZ cermet was selected as a candidate for HTE cathode of self-supporting planar unit cell and its electrochemical performance was investigated, paving the way for preliminary correlation of high-energy ball-milling parameters with observed physical and electrochemical performance of Cu/YSZ cermets

  18. Fabrication and characterization of Cu/YSZ cermet high-temperature electrolysis cathode material prepared by high-energy ball-milling method

    International Nuclear Information System (INIS)

    Lee, Sungkyu; Kang, Kyoung-Hoon; Kim, Jong-Min; Hong, Hyun Seon; Yun, Yongseung; Woo, Sang-Kook

    2008-01-01

    Cu/YSZ composites (40 and 60 vol.% Cu powder with balance YSZ) was successfully fabricated by high-energy ball-milling of Cu and YSZ powders at 400 rpm for 24 h, pressing into pellets (O 13 mm x 2 mm) and subsequent sintering process at 900 deg. C under flowing 5%-H 2 /Ar gas for use as cermet cathode material of high-temperature electrolysis (HTE) of water vapor in a more economical way compared with conventional Ni/YSZ cermet cathode material. The Cu/YSZ composite powders thus synthesized and sintered were characterized using various analytical tools such as XRD, SEM, and laser diffraction and scattering method. Electrical conductivity of sintered Cu/YSZ cermet pellets thus fabricated was measured using 4-probe technique and compared with that of Ni/YSZ cermets. The effect of composites composition on the electrical conductivity was investigated and marked increase in electrical conductivity for copper contents greater than 40 vol.% in the composite was explained by percolation threshold

  19. Synthesis of LiFePO4/Graphene Nanocomposite and Its Electrochemical Properties as Cathode Material for Li-Ion Batteries

    Directory of Open Access Journals (Sweden)

    Xiaoling Ma

    2015-01-01

    Full Text Available LiFePO4/graphene nanocomposite was successfully synthesized by rheological phase method and its electrochemical properties as the cathode materials for lithium ion batteries were measured. As the iron source in the synthesis, FeOOH nanorods anchored on graphene were first synthesized. The FeOOH nanorods precursors and the final LiFePO4/graphene nanocomposite products were characterized by XRD, SEM, and TEM. While the FeOOH precursors were nanorods with 5–10 nm in diameter and 10–50 nm in length, the LiFePO4 were nanoparticles with 20–100 nm in size. Compared with the electrochemical properties of LiFePO4 particles without graphene nanosheets, it is clear that the graphene nanosheets can improve the performances of LiFePO4 as the cathode material for lithium ion batteries. The as-synthesized LiFePO4/graphene nanocomposite showed high capacities and good cyclabilities. When measured at room temperature and at the rate of 0.1C (1C = 170 mA g−1, the composite showed a discharge capacity of 156 mA h g−1 in the first cycle and a capacity retention of 96% after 15 cycles. The improved performances of the composite are believed to be the result of the three-dimensional conducting network formed by the flexible and planar graphene nanosheets.

  20. Guidelines for Assessment and Abatement of Asbestos-Containing Materials in Buildings.

    Science.gov (United States)

    Pielert, James H.; Mathey, Robert G.

    This report presents guidelines, based on available information, for the assessment and abatement of asbestos-containing materials in buildings. Section 1 provides background information on the history and use of asbestos-containing products in buildings, the characteristics of asbestos fibers, products and materials containing asbestos, and…

  1. Processing fissile material mixtures containing zirconium and/or carbon

    Science.gov (United States)

    Johnson, Michael Ernest; Maloney, Martin David

    2013-07-02

    A method of processing spent TRIZO-coated nuclear fuel may include adding fluoride to complex zirconium present in a dissolved TRIZO-coated fuel. Complexing the zirconium with fluoride may reduce or eliminate the potential for zirconium to interfere with the extraction of uranium and/or transuranics from fission materials in the spent nuclear fuel.

  2. Method of processing liquid wastes containing radioactive materials

    International Nuclear Information System (INIS)

    Matsumoto, Kaname; Shirai, Takamori; Nemoto, Kuniyoshi; Yoshikawa, Jun; Matsuda, Takeshi.

    1983-01-01

    Purpose: To reduce the number of solidification products by removing, particularly, Co-60 that is difficult to remove in a radioactive liquid wastes containing a water-soluble chelating agent, by adsorbing Co-60 to a specific chelating agent. Method: Liquid wastes containing radioactive cobalt and water-soluble chelating agent are passed through the layer of less water-soluble chelating agent that forms a complex compound with cobalt in an acidic pH region. Thus, the chelating compound of radioactive cobalt (particularly Co-60) is eliminated by adsorbing the same on a specific chelating agent layer. The chelating agent having Co-60 adsorbed thereon is discarded as it is through the cement- or asphalt-solidification process, whereby the number of solidification products to be generated can significantly be suppressed. (Moriyama, K.)

  3. Study of improving the thermal response of a construction material containing a phase change material

    Science.gov (United States)

    Laaouatni, A.; Martaj, N.; Bennacer, R.; Elomari, M.; El Ganaoui, M.

    2016-09-01

    The use of phase change materials (PCMs) for improving the thermal comfort in buildings has become an attractive application. This solution contributes to increasing the thermal inertia of the building envelope and reducing power consumption. A building element filled with a PCM and equipped with ventilation tubes is proposed, both for increasing inertia and contributing to refreshing building envelope. A numerical simulation is conducted by the finite element method in COMSOL Multiphysics, which aims to test the thermal behaviour of the developed solution. An experimental study is carried out on a concrete block containing a PCM with ventilation tubes. The objective is to see the effect of PCM coupled with ventilation on increasing the inertia of the block. The results show the ability of this new solution to ensure an important thermal inertia of a building.

  4. Carbon nanotube: nanodiamond Li-ion battery cathodes with increased thermal conductivity

    Science.gov (United States)

    Salgado, Ruben; Lee, Eungiee; Shevchenko, Elena V.; Balandin, Alexander A.

    2016-10-01

    Prevention of excess heat accumulation within the Li-ion battery cells is a critical design consideration for electronic and photonic device applications. Many existing approaches for heat removal from batteries increase substantially the complexity and overall weight of the battery. Some of us have previously shown a possibility of effective passive thermal management of Li-ion batteries via improvement of thermal conductivity of cathode and anode material1. In this presentation, we report the results of our investigation of the thermal conductivity of various Li-ion cathodes with incorporated carbon nanotubes and nanodiamonds in different layered structures. The cathodes were synthesized using the filtration method, which can be utilized for synthesis of commercial electrode-active materials. The thermal measurements were conducted with the "laser flash" technique. It has been established that the cathode with the carbon nanotubes-LiCo2 and carbon nanotube layered structure possesses the highest in-plane thermal conductivity of 206 W/mK at room temperature. The cathode containing nanodiamonds on carbon nanotubes structure revealed one of the highest cross-plane thermal conductivity values. The in-plane thermal conductivity is up to two orders-of-magnitude greater than that in conventional cathodes based on amorphous carbon. The obtained results demonstrate a potential of carbon nanotube incorporation in cathode materials for the effective thermal management of Li-ion high-powered density batteries.

  5. Containment system of contamination in irradiated materials handling laboratories

    International Nuclear Information System (INIS)

    Lobao, A.S.T.; Araujo, J.A. de; Camilo, R.L.

    1988-01-01

    A study to prevent radiactivity release in lab scale is presented. As a basis for the design all the limits established by the IAEA for ventilation systems were observed. An evaluation of the different parameters involved in the design have been made, resulting in the specification of the working areas, ducts and filtering systems in order to get the best conditions for the safe handling of irradiated materials. (author) [pt

  6. Comparative study of biogenic and abiotic iron-containing materials

    Energy Technology Data Exchange (ETDEWEB)

    Cherkezova-Zheleva, Z., E-mail: zzhel@ic.bas.bg; Shopska, M., E-mail: shopska@ic.bas.bg; Paneva, D. [Bulgarian Academy of Sciences, Institute of Catalysis (Bulgaria); Kovacheva, D. [Bulgarian Academy of Sciences, Institute of General and Inorganic Chemistry (Bulgaria); Kadinov, G.; Mitov, I. [Bulgarian Academy of Sciences, Institute of Catalysis (Bulgaria)

    2016-12-15

    Series of iron-based biogenic materials prepared by cultivation of Leptothrix group of bacteria in different feeding media (Sphaerotilus-Leptothrix group of bacteria isolation medium, Adler, Lieske and silicon-iron-glucose-peptone) were studied. Control samples were obtained in the same conditions and procedures but the nutrition media were not infected with bacteria, i.e. they were sterile. Room and low temperature Mössbauer spectroscopy, powder X-ray diffraction (XRD), and infrared spectroscopy (IRS) were used to reveal the composition and physicochemical properties of biomass and respective control samples. Comparative analysis showed differences in their composition and dispersity of present phases. Sample composition included different ratio of nanodimensional iron oxyhydroxide and oxide phases. Relaxation phenomena such as superparamagnetism or collective magnetic excitation behaviour were registered for some of them. The experimental data showed that the biogenic materials were enriched in oxyhydroxides of high dispersion. Catalytic behaviour of a selected biomass and abiotic material were studied in the reaction of CO oxidation. In situ diffuse-reflectance (DR) IRS was used to monitor the phase transformations in the biomass and CO conversion.

  7. Nanoporous LiMn2O4 spinel prepared at low temperature as cathode material for aqueous supercapacitors

    Science.gov (United States)

    Wang, F. X.; Xiao, S. Y.; Gao, X. W.; Zhu, Y. S.; Zhang, H. P.; Wu, Y. P.; Holze, R.

    2013-11-01

    LiMn2O4 spinel was prepared by a hydrothermal method using α-MnO2 nanotubes as precursor at 180 °C, a temperature much lower than that in previously reported methods. It is nanoporous with a pore size of about 40-50 nm and a BET surface area of 9.76 m2 g-1. It exhibits a high specific capacitance of 189 F g-1 at 0.3 A g-1 as a cathode for an aqueous supercapacitor. Even at 12 A g-1, it still has a capacitance of 166 F g-1. After 1500 cycles, there is no evident capacity fading. The LiMn2O4 cathode can deliver an energy density of 31.9 Wh kg-1 at 3480 W kg-1 and even maintain 19.4 Wh kg-1 at about 5100 W kg-1 based on the mass of LiMn2O4.

  8. Pulsed Electron Source with Grid Plasma Cathode and Longitudinal Magnetic Field for Modification of Material and Product Surfaces

    Science.gov (United States)

    Devyatkov, V. N.; Koval, N. N.

    2018-01-01

    The description and the main characteristics of the pulsed electron source "SOLO" developed on the basis of the plasma cathode with grid stabilization of the emission plasma boundary are presented. The emission plasma is generated by a low-pressure arc discharge, and that allows to form the dense low-energy electron beam with a wide range of independently adjustable parameters of beam current pulses (pulse duration of 20-250 μs, pulse repetition rate of 1-10 s-1, amplitude of beam current pulses of 20-300 A, and energy of beam electrons of 5-25 keV). The special features of generation of emission plasma by constricted low-pressure arc discharge in the grid plasma cathode partially dipped into a non-uniform magnetic field and of formation and transportation of the electron beam in a longitudinal magnetic field are considered. The application area of the electron source and technologies realized with its help are specified.

  9. Irradiation studies of mallard duck eggs material containing Mirex

    International Nuclear Information System (INIS)

    Lane, R.H.; Grodner, R.M.; Graves, J.L.

    1976-01-01

    Eggs containing Mirex (dodecachloropentacyclo[5.3.0.0 2 , 6 .0 3 , 9 .0 4 , 8 ]decane) from mallard ducks (Anas platyrhychos l.), fed diets with the insecticide incorporated at levels of 1 and 100 ppM for 25 weeks, were subjected to ultraviolet (uv) and γ irradiation. Seven derivatives were obtained on photolysis and eight derivatives were obtained from γ irradiation. Irradiation products appeared to be mono and dihydro derivatives of Mirex. Structural assignments for two monohydro derivatives and three dihydro derivatives were made on the basis of retention time and mass spectral data

  10. Electrochromic device containing metal oxide nanoparticles and ultraviolet blocking material

    Science.gov (United States)

    Garcia, Guillermo; Koo, Bonil; Gregoratto, Ivano; Basu, Sourav; Rosen, Evelyn; Holt, Jason; Thomsen, Scott

    2017-10-17

    An electrochromic device includes a nanostructured transition metal oxide bronze layer that includes one or more transition metal oxide and one or more dopant. The electrochromic device also includes nanoparticles containing one or more transparent conducting oxide (TCO), a solid state electrolyte, a counter electrode, and at least one protective layer to prevent degradation of the one or more nanostructured transition metal oxide bronze. The nanostructured transition metal oxide bronze selectively modulates transmittance of near-infrared (NIR) and visible radiation as a function of an applied voltage to the device.

  11. Method of forming capsules containing a precise amount of material

    Science.gov (United States)

    Grossman, M.W.; George, W.A.; Maya, J.

    1986-06-24

    A method of forming a sealed capsule containing a submilligram quantity of mercury or the like, the capsule being constructed from a hollow glass tube, by placing a globule or droplet of the mercury in the tube. The tube is then evacuated and sealed and is subsequently heated so as to vaporize the mercury and fill the tube therewith. The tube is then separated into separate sealed capsules by heating spaced locations along the tube with a coiled heating wire means to cause collapse spaced locations there along and thus enable separation of the tube into said capsules. 7 figs.

  12. Recent Progress in the Design of Advanced Cathode Materials and Battery Models for High-Performance Lithium-X (X = O2 , S, Se, Te, I2 , Br2 ) Batteries.

    Science.gov (United States)

    Xu, Jiantie; Ma, Jianmin; Fan, Qinghua; Guo, Shaojun; Dou, Shixue

    2017-07-01

    Recent advances and achievements in emerging Li-X (X = O 2 , S, Se, Te, I 2 , Br 2 ) batteries with promising cathode materials open up new opportunities for the development of high-performance lithium-ion battery alternatives. In this review, we focus on an overview of recent important progress in the design of advanced cathode materials and battery models for developing high-performance Li-X (X = O 2 , S, Se, Te, I 2 , Br 2 ) batteries. We start with a brief introduction to explain why Li-X batteries are important for future renewable energy devices. Then, we summarize the existing drawbacks, major progress and emerging challenges in the development of cathode materials for Li-O 2 (S) batteries. In terms of the emerging Li-X (Se, Te, I 2 , Br 2 ) batteries, we systematically summarize their advantages/disadvantages and recent progress. Specifically, we review the electrochemical performance of Li-Se (Te) batteries using carbonate-/ether-based electrolytes, made with different electrode fabrication techniques, and of Li-I 2 (Br 2 ) batteries with various cell designs (e.g., dual electrolyte, all-organic electrolyte, with/without cathode-flow mode, and fuel cell/solar cell integration). Finally, the perspective on and challenges for the development of cathode materials for the promising Li-X (X = O 2 , S, Se, Te, I 2 , Br 2 ) batteries is presented. © 2017 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  13. Outstanding Li-storage performance of LiFePO4@MWCNTs cathode material with 3D network structure for lithium-ion batteries

    Science.gov (United States)

    Sun, Xiaodong; Zhang, Le

    2018-05-01

    In this work, the MWCNTs-decorated LiFePO4 microspheres (LiFePO4@MWCNTs) with a 3D network structure have been synthesized by a facile and efficient spray-drying approach followed by solid-state reaction in a reduction atmosphere. In the as-prepared composite, the MWCNTs around LiFePO4 nanoparticles can provide 3D conductive networks which greatly facilitate the transport of Li+-ion and electron during the electrochemical reaction. Compared to the pure LiFePO4 material, the LiFePO4@MWCNTs composite as cathode for lithium-ion batteries exhibits significantly improved Li-storage performance in terms of rate capability and cyclic stability. Therefore, we can speculate that the spray-drying approach is a promising route to prepare the high-performance electrode materials with 3D network structure for electrochemical energy storage.

  14. Synopsis of Cathode No.4 Activation

    International Nuclear Information System (INIS)

    Kwan, Joe; Ekdahl, C.; Harrison, J.; Kwan, J.; Leitner, M.; McCruistian, T.; Mitchell, R.; Prichard, B.; Roy, P.

    2006-01-01

    The purpose of this report is to describe the activation of the fourth cathode installed in the DARHT-II Injector. Appendices have been used so that an extensive amount of data could be included without danger of obscuring important information contained in the body of the report. The cathode was a 612 M type cathode purchased from Spectra-Mat. Section II describes the handling and installation of the cathode. Section III is a narrative of the activation based on information located in the Control Room Log Book supplemented with time plots of pertinent operating parameters. Activation of the cathode was performed in accordance with the procedure listed in Appendix A. The following sections provide more details on the total pressure and constituent partial pressures in the vacuum vessel, cathode heater power/filament current, and cathode temperature

  15. The impact of new cathode materials relative to baseline performance of microbial fuel cells all with the same architecture and solution chemistry

    KAUST Repository

    Yang, Wulin; Kim, Kyoung-Yeol; Saikaly, Pascal; Logan, Bruce E

    2017-01-01

    age. Power production with Pt catalyst cathodes significantly declined after one month of operation or more to 0.87 ± 0.31 W m–2 (n=18) based on studies where cathode aging was examined, while in many studies the age of the cathode was not reported

  16. Thermal Characteristics of Conversion-Type FeOF Cathode in Li-ion Batteries

    Directory of Open Access Journals (Sweden)

    Liwei Zhao

    2017-10-01

    Full Text Available Rutile FeOF was used as a conversion-type cathode material for Li-ion batteries. In the present study, 0.6Li, 1.4Li, and 2.7Li per mole lithiation reactions were carried out by changing the electrochemical discharge reaction depth. The thermal characteristics of the FeOF cathode were investigated by thermogravimetric mass spectrometric (TG-MS and differential scanning calorimeter (DSC systems. No remarkable HF release was detected, even up to 700 °C, which indicated a low toxic risk for the FeOF cathode. Changes in the thermal properties of the FeOF cathode via different conversion reaction depths in the associated electrolyte were studied by changing the cathode/electrolyte ratio in the mixture. LiFeOF was found to exothermically react with the electrolyte at about 210 °C. Similar exothermic reactions were found with charged FeOF cathodes because of the irreversible Li ions. Among the products of the conversion reaction of FeOF, Li2O was found to exothermically react with the electrolyte at about 120 °C, which induced the main thermal risk of the FeOF cathode. It suggests that the oxygen-containing conversion-type cathodes have a higher thermal risk than the oxygen-free ones, but controlling the cathode/electrolyte ratio in cells successfully reduced the thermal risk. Finally, the thermal stability of the FeOF cathode was evaluated in comparison with FeF3 and LiFePO4 cathodes.

  17. EFFECT OF CURRENT, TIME, FEED AND CATHODE TYPE ON ELECTROPLATING PROCESS OF URANIUM SOLUTION

    Directory of Open Access Journals (Sweden)

    Sigit Sigit

    2017-02-01

    Full Text Available ABSTRACT   EFFECT OF CURRENT, TIME, FEED AND CATHODE TYPE ON ELECTROPLATING PROCESS OF URANIUM SOLUTION. Electroplating process of uranyl nitrate and effluent process has been carried out in order to collect uranium contained therein using electrode Pt / Pt and Pt / SS at various currents and times. Material used for electrode were Pt (platinum and SS (Stainlees Steel. Feed solution of 250 mL was entered into a beaker glass equipped with Pt anode - Pt cathode or Pt anode - SS cathode, then fogged direct current from DC power supply with specific current and time so that precipitation of uranium sticking to the cathode. After the processes completed, the cathode was removed and weighed to determine weight of precipitates, while the solution was analyzed to determine the uranium concentration decreasing after and before electroplating process. The experiments showed that a relatively good time to acquire uranium deposits at the cathode was 1 hour by current 7 ampere, uranyl nitrate as feed, and Pt (platinum as cathode. In these conditions, uranium deposits attached to the cathode amounted to 74.96% of the original weight of uranium oxide in the feed or 206.5 mg weight. The use of Pt cathode for  uranyl nitrate, SS and Pt cathode for effluent process feed gave uranium specific weight at the cathode of 12.99 mg/cm2, 2.4 mg/cm2 and 5.37 mg/cm2 respectively for current 7 ampere and electroplating time 1 hour. Keywords: Electroplating, uranyl nitrate, effluent process, Pt/Pt electrode, Pt/SS electrode

  18. Orbital-Specific observation of O2p and Ni3d electrons in LiNi0.5Mn0.5O2, a cathode material for lithium-ion batteries

    Directory of Open Access Journals (Sweden)

    Yoshinori Satou

    2017-09-01

    Full Text Available Cathode materials for lithium-ion batteries containing Ni2+ have attracted much interest because of their high theoretical capacity. However, the precise electronic structures of these cathode materials have not yet been clearly observed, especially the energy positions of the O2p and Ni3d orbitals and the shape of the density of states. The aim of this study was to investigate the relative energy positions and shape of the density of states of O2p and Ni3d for LiNi0.5Mn0.5O2 experimentally. We cleaved a LiNi0.5Mn0.5O2 pellet in an Ar-filled glove box and performed synchrotron ultraviolet photoelectron spectroscopy for different photon energies, which enabled us to investigate the relative cross-section intensity of O2p and Ni3d. As a result, the valence-band structure was determined. We found that O2p electrons are itinerant and exist in the vicinity of the Fermi energy more than Ni3d electrons. Ni3d electrons are more localized and spread mainly from 1.2–1.5 eV below the Fermi energy. To validate the electronic structure, we measured the synchrotron O K-edge X-ray absorption fine structure of electrochemically lithium-extracted LiNi0.5Mn0.5O2. The electronic structure demonstrated that ligand holes in the oxygen atoms form below the Fermi level during the initial stage of Li extraction and that the formation rate of the holes decreases with Li extraction.

  19. Orbital-Specific observation of O2p and Ni3d electrons in LiNi0.5Mn0.5O2, a cathode material for lithium-ion batteries

    Science.gov (United States)

    Satou, Yoshinori; Komine, Shigeki; Shimizu, Sumera

    2017-09-01

    Cathode materials for lithium-ion batteries containing Ni2+ have attracted much interest because of their high theoretical capacity. However, the precise electronic structures of these cathode materials have not yet been clearly observed, especially the energy positions of the O2p and Ni3d orbitals and the shape of the density of states. The aim of this study was to investigate the relative energy positions and shape of the density of states of O2p and Ni3d for LiNi0.5Mn0.5O2 experimentally. We cleaved a LiNi0.5Mn0.5O2 pellet in an Ar-filled glove box and performed synchrotron ultraviolet photoelectron spectroscopy for different photon energies, which enabled us to investigate the relative cross-section intensity of O2p and Ni3d. As a result, the valence-band structure was determined. We found that O2p electrons are itinerant and exist in the vicinity of the Fermi energy more than Ni3d electrons. Ni3d electrons are more localized and spread mainly from 1.2-1.5 eV below the Fermi energy. To validate the electronic structure, we measured the synchrotron O K-edge X-ray absorption fine structure of electrochemically lithium-extracted LiNi0.5Mn0.5O2. The electronic structure demonstrated that ligand holes in the oxygen atoms form below the Fermi level during the initial stage of Li extraction and that the formation rate of the holes decreases with Li extraction.

  20. Structural characterization of layered Na0.5Co0.5Mn0.5O2 material as a promising cathode for sodium-ion batteries

    Science.gov (United States)

    Manikandan, Palanisamy; Heo, Seongwoo; Kim, Hyun Woo; Jeong, Hu Young; Lee, Eungje; Kim, Youngsik

    2017-09-01

    Layered Na0.5Co0.5Mn0.5O2 material is synthesized through a facile mixed hydroxy-carbonate route using (Co0.5Mn0.5)2(OH)2CO3 precursor and well characterized as a hexagonal layered structure under P63/mmc space group. The lattice parameters and unit cell volume (a = 2.8363 Å, c = 11.3152 Å and V = 78.83 Å3) are calculated by Rietveld refinement analysis. A flaky-bundle morphology is obtained to the layered Na0.5Co0.5Mn0.5O2 material with the hexagonal flake size ∼30 nm. Advanced transmission electron microscopic images are revealed the local structure of the layered Na0.5Co0.5Mn0.5O2 material with contrasting bright dots and faint dark dots corresponding to the Co/Mn and Na atoms. Two oxidation and reduction peaks are occurred in a cyclic voltammetric analysis corresponding to Co3+/Co4+ and Mn3+/Mn4+ redox processes. These reversible processes are attributed to the intercalation/de-intercalation of Na+ ions into the host structure of layered Na0.5Co0.5Mn0.5O2 material. Accordingly, the sodium cell is delivered the initial charge-discharge capacity 53/144 mAh g-1 at 0.5 C, which cycling studies are extended to rate capability test at 1 C, 3 C and 5C. Eventually, the Na-ion full-cell is yielded cathode charge-discharge capacity 55/52 mAh g-1 at 0.212 mA and exhibited as a high voltage cathode for Na-ion batteries.

  1. Atomistic Insights into FeF3 Nanosheet: An Ultrahigh-Rate and Long-Life Cathode Material for Li-Ion Batteries.

    Science.gov (United States)

    Yang, Zhenhua; Zhao, Shu; Pan, Yanjun; Wang, Xianyou; Liu, Hanghui; Wang, Qun; Zhang, Zhijuan; Deng, Bei; Guo, Chunsheng; Shi, Xingqiang

    2018-01-24

    Iron fluoride with high operating voltage and theoretical energy density has been proposed as a high-performance cathode material for Li-ion batteries. However, the inertness of pristine bulk FeF 3 results in poor Li kinetics and cycling life. Developing nanosheet-based electrode materials is a feasible strategy to solve these problems. Herein, on the basis of first-principles calculations, first the stability of FeF 3 (012) nanosheet with different atomic terminations under different environmental conditions was systematically studied, then the Li-ion adsorption and diffusion kinetics were thoroughly probed, and finally the voltages for different Li concentrations were given. We found that F-terminated nanosheet is energetically favorable in a wide range of chemical potential, which provide a vehicle for lithium ion diffusion. Our Li-ion adsorption and diffusion kinetics study revealed that (1) the formation of Li dimer is the most preferred, (2) the Li diffusion energy barrier of Li dimer is lower than isolated Li atom (0.17 eV for Li dimer vs 0.22 eV for Li atom), and (3) the diffusion coefficient of Li is 1.06 × 10 -6 cm 2 ·s -1 , which is orders of magnitude greater than that of Li diffusion in bulk FeF 3 (10 -13 -10 -11 cm 2 ·s -1 ). Thus, FeF 3 nanosheet can act as an ultrahigh-rate cathode material for Li-ion batteries. More importantly, the calculated voltage and specific capacity of Li on the FeF 3 (012) nanosheet demonstrate that it has a much more stable voltage profile than bulk FeF 3 for a wide range of Li concentration. So, few layers FeF 3 nanosheet provides the desired long-life energy density in Li-ion batteries. These above findings in the current study shed new light on the design of ultrahigh-rate and long-life FeF 3 cathode material for Li-ion batteries.

  2. Remote automated material handling of radioactive waste containers

    International Nuclear Information System (INIS)

    Greager, T.M.

    1994-09-01

    To enhance personnel safety, improve productivity, and reduce costs, the design team incorporated a remote, automated stacker/retriever, automatic inspection, and automated guidance vehicle for material handling at the Enhanced Radioactive and Mixed Waste Storage Facility - Phase V (Phase V Storage Facility) on the Hanford Site in south-central Washington State. The Phase V Storage Facility, scheduled to begin operation in mid-1997, is the first low-cost facility of its kind to use this technology for handling drums. Since 1970, the Hanford Site's suspect transuranic (TRU) wastes and, more recently, mixed wastes (both low-level and TRU) have been accumulating in storage awaiting treatment and disposal. Currently, the Hanford Site is only capable of onsite disposal of radioactive low-level waste (LLW). Nonradioactive hazardous wastes must be shipped off site for treatment. The Waste Receiving and Processing (WRAP) facilities will provide the primary treatment capability for solid-waste storage at the Hanford Site. The Phase V Storage Facility, which accommodates 27,000 drum equivalents of contact-handled waste, will provide the following critical functions for the efficient operation of the WRAP facilities: (1) Shipping/Receiving; (2) Head Space Gas Sampling; (3) Inventory Control; (4) Storage; (5) Automated/Manual Material Handling

  3. Cathode ray tube screens

    International Nuclear Information System (INIS)

    Cockayne, B.; Robbins, D.J.; Glasper, J.L.

    1982-01-01

    An improved cathode ray tube screen is described which consists of a single- or a poly-crystalline slice of a material such as yttrium aluminium garnet in which dopants such as Tb 3 + , Eu 3 + , Ce 3 + or Tm 3 + are ion implanted to different depths or in different areas of the screen. Annealing the screen removes lattice damage caused by the ion implanting and assists the diffusion of the dopant into the crystal. (U.K.)

  4. Effects of materials containing antimicrobial compounds on food hygiene.

    Science.gov (United States)

    Møretrø, Trond; Langsrud, Solveig

    2011-07-01

    Surfaces with microorganisms may transfer unwanted microorganisms to food through cross-contamination during processing and preparation. A high hygienic status of surfaces that come in contact with food is important in order to reduce the risk of cross-contamination. During the last decade, products containing antimicrobial compounds, such as cutting boards, knives, countertops, kitchen utensils, refrigerators, and conveyor belts, have been introduced to the market, claiming hygienic effects. Such products are often referred to as "treated articles." Here we review various aspects related to treated articles intended for use during preparation and processing of food. Regulatory issues and methods to assess antibacterial effects are covered. Different concepts for treated articles as well as their antibacterial activity are reviewed. The effects of products with antimicrobials on food hygiene and safety are discussed. Copyright ©, International Association for Food Protection

  5. Cyclodextrin-Containing Polymers: Versatile Platforms of Drug Delivery Materials

    Directory of Open Access Journals (Sweden)

    Jeremy D. Heidel

    2012-01-01

    Full Text Available Nanoparticles are being widely explored as potential therapeutics for numerous applications in medicine and have been shown to significantly improve the circulation, biodistribution, efficacy, and safety profiles of multiple classes of drugs. One leading class of nanoparticles involves the use of linear, cyclodextrin-containing polymers (CDPs. As is discussed in this paper, CDPs can incorporate therapeutic payloads into nanoparticles via covalent attachment of prodrug/drug molecules to the polymer (the basis of the Cyclosert platform or by noncovalent inclusion of cationic CDPs to anionic, nucleic acid payloads (the basis of the RONDEL platform. For each of these two approaches, we review the relevant molecular architecture and its rationale, discuss the physicochemical and biological properties of these nanoparticles, and detail the progress of leading drug candidates for each that have achieved clinical evaluation. Finally, we look ahead to potential future directions of investigation and product candidates based upon this technology.

  6. On material and energy sources of formation of fuel-containing materials during Chernobyl NPP UNIT 4 accident

    Directory of Open Access Journals (Sweden)

    O. V. Mikhailov

    2016-12-01

    Full Text Available Results of detailed analysis of material substance of lava-like fuel-containing materials sources (FCM and clusters with high uranium concentration were presented. Material and energy balance are aggregated in a process model for optimal composition of sacrificial materials and FCM. Quantitative estimate is given for spent nuclear fuel’ afterheat in a number of other heat energy sources in reactor vault. Conclusion was made that upon condition of 50 % heat loss, remained amount of “useful” heat would be sufficient for proceeding of blast furnace version of fuel-containing materials.

  7. Packaging material and flexible medical tubing containing thermally exfoliated graphite oxide

    Science.gov (United States)

    Prud'homme, Robert K. (Inventor); Aksay, Ilhan A. (Inventor)

    2011-01-01

    A packaging material or flexible medical tubing containing a modified graphite oxide material, which is a thermally exfoliated graphite oxide with a surface area of from about 300 m.sup.2/g to 2600 m.sup.2/g.

  8. Detection of tiny amounts of fissile materials in large-sized containers with radioactive waste

    Science.gov (United States)

    Batyaev, V. F.; Skliarov, S. V.

    2018-01-01

    The paper is devoted to non-destructive control of tiny amounts of fissile materials in large-sized containers filled with radioactive waste (RAW). The aim of this work is to model an active neutron interrogation facility for detection of fissile ma-terials inside NZK type containers with RAW and determine the minimal detectable mass of U-235 as a function of various param-eters: matrix type, nonuniformity of container filling, neutron gen-erator parameters (flux, pulse frequency, pulse duration), meas-urement time. As a result the dependence of minimal detectable mass on fissile materials location inside container is shown. Nonu-niformity of the thermal neutron flux inside a container is the main reason of the space-heterogeneity of minimal detectable mass in-side a large-sized container. Our experiments with tiny amounts of uranium-235 (<1 g) confirm the detection of fissile materials in NZK containers by using active neutron interrogation technique.

  9. The preparation and graphene surface coating NaTi{sub 2}(PO{sub 4}){sub 3} as cathode material for lithium ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Li, Na; Wang, Yanping; Rao, Richuan; Dong, Xiongzi [Department of Chemical and Chemical Engineering, Hefei normal University, Hefei, Anhui 230601 (China); Zhang, Xianwen, E-mail: 18326056237@163.com [Institute of Advanced Energy Technology & Equipment, Hefei University of Technology, 193 Tunxi Road, Hefei, Anhui 230009 (China); Zhu, Sane, E-mail: sdjnlina@163.com [Department of Chemistry and Materials Engineering, Hefei University, Hefei, Anhui 230601 (China)

    2017-03-31

    Graphical abstract: The NaTi{sub 2}(PO{sub 4}){sub 3}/graphene composite is used directly as cathode electrode material for lithium-ion battery by using metal lithium as an anode electrode. Meanwhile, the electrochemical properties of the composite in this system is firstly studied in detail. The NaTi{sub 2}(PO{sub 4}){sub 3}/graphene composite exhibits the better rate and cyclic performance than NaTi{sub 2}(PO{sub 4}){sub 3}, which is ascribed to its stable 3-D framework and the enhanced electronic conduction resulting from the graphene sheets surface modification. - Highlights: • The graphene coated NaTi{sub 2}(PO{sub 4}){sub 3} was prepared by a simple sol-gel method followed by calcination. • The electrochemical properties of the NaTi{sub 2}(PO{sub 4}){sub 3}/graphene composite was firstly studied in detail when used as cathode electrode material for lithium-ion batteries. • The electrochemical reaction mechanism of NaTi{sub 2}(PO{sub 4}){sub 3}/graphene composite was investigated by ex situ XRD. - Abstract: The graphene coated NaTi{sub 2}(PO{sub 4}){sub 3} has been fabricated via a simple sol-gel process followed by calcination. The NaTi{sub 2}(PO{sub 4}){sub 3}/graphene (NTP/G) composite is used directly as cathode electrode material for lithium-ion battery and the electrochemical properties of the composite in this system is firstly studied in detail. In the charge-discharge process, two Li{sup +} can occupy octahedral M (2) site and be reversibly intercalated into the 3D framework of NTP through the ion conduction channel where almost all of Na{sup +} are immobilized to sustain the framework. At 5C rate, the capacity retention of the NTP/G composite after 800 cycles is still up to 82.7%. The superior electrochemical properties of NTP/G is ascribed to its stable 3-D framework and the enhanced electronic conduction resulting from the graphene sheets surface modification.

  10. Development of thin film cathodes for lithium-ion batteries in the material system Li–Mn–O by r.f. magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Fischer, J., E-mail: julian.fischer@kit.edu [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Applied Materials Physics (IAM-AWP), Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Adelhelm, C.; Bergfeldt, T. [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Applied Materials Physics (IAM-AWP), Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Chang, K. [RWTH Aachen University, Materials Chemistry, Kopernikusstrasse 10, 46 52074 Aachen (Germany); Ziebert, C.; Leiste, H.; Stüber, M.; Ulrich, S. [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Applied Materials Physics (IAM-AWP), Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Music, D.; Hallstedt, B. [RWTH Aachen University, Materials Chemistry, Kopernikusstrasse 10, 46 52074 Aachen (Germany); Seifert, H.J. [Karlsruhe Institute of Technology (KIT), Institute for Applied Materials, Applied Materials Physics (IAM-AWP), Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

    2013-01-01

    Today most commercially available lithium ion batteries are still based on the toxic and expensive LiCoO{sub 2} as a standard cathode material. However, lithium manganese based cathode materials are cheaper and environmentally friendlier. In this work cubic-LiMn{sub 2}O{sub 4} spinel, monoclinic-Li{sub 2}MnO{sub 3} and orthorhombic-LiMnO{sub 2} thin films have been synthesized by non-reactive r.f. magnetron sputtering from two ceramic targets (LiMn{sub 2}O{sub 4}, LiMnO{sub 2}) in a pure argon discharge. The deposition parameters, namely target power and working gas pressure, were optimized in a combination with a post deposition heat treatment with respect to microstructure and electrochemical behavior. The chemical composition was determined using inductively coupled plasma optical emission spectroscopy and carrier gas hot extraction. The films' crystal structure, phase evolution and morphology were investigated by X-ray diffraction, micro Raman spectroscopy and scanning electron microscopy. Due to the fact that these thin films consist of the pure active material without any impurities, such as binders or conductive additives like carbon black, they are particularly well suited for measurements of the intrinsic physical properties, which is essential for fundamental understanding. The electrochemical behavior of the cubic and the orthorhombic films was investigated by galvanostatic cycling in half cells against metallic lithium. The cubic spinel films exhibit a maximum specific capacity of ∼ 82 mAh/g, while a specific capacity of nearly 150 mAh/g can be reached for the orthorhombic counterparts. These films are promising candidates for future all solid state battery applications. - Highlights: ► Synthesis of 3 Li–Mn–O structures by one up-scalable thin film deposition method ► Formation of o-LiMnO{sub 2} by r.f. magnetron sputtering in combination with post-annealing ► Discharge capacity with o-LiMnO{sub 2} cathodes twice as high as for c

  11. Development of thin film cathodes for lithium-ion batteries in the material system Li–Mn–O by r.f. magnetron sputtering

    International Nuclear Information System (INIS)

    Fischer, J.; Adelhelm, C.; Bergfeldt, T.; Chang, K.; Ziebert, C.; Leiste, H.; Stüber, M.; Ulrich, S.; Music, D.; Hallstedt, B.; Seifert, H.J.

    2013-01-01

    Today most commercially available lithium ion batteries are still based on the toxic and expensive LiCoO 2 as a standard cathode material. However, lithium manganese based cathode materials are cheaper and environmentally friendlier. In this work cubic-LiMn 2 O 4 spinel, monoclinic-Li 2 MnO 3 and orthorhombic-LiMnO 2 thin films have been synthesized by non-reactive r.f. magnetron sputtering from two ceramic targets (LiMn 2 O 4 , LiMnO 2 ) in a pure argon discharge. The deposition parameters, namely target power and working gas pressure, were optimized in a combination with a post deposition heat treatment with respect to microstructure and electrochemical behavior. The chemical composition was determined using inductively coupled plasma optical emission spectroscopy and carrier gas hot extraction. The films' crystal structure, phase evolution and morphology were investigated by X-ray diffraction, micro Raman spectroscopy and scanning electron microscopy. Due to the fact that these thin films consist of the pure active material without any impurities, such as binders or conductive additives like carbon black, they are particularly well suited for measurements of the intrinsic physical properties, which is essential for fundamental understanding. The electrochemical behavior of the cubic and the orthorhombic films was investigated by galvanostatic cycling in half cells against metallic lithium. The cubic spinel films exhibit a maximum specific capacity of ∼ 82 mAh/g, while a specific capacity of nearly 150 mAh/g can be reached for the orthorhombic counterparts. These films are promising candidates for future all solid state battery applications. - Highlights: ► Synthesis of 3 Li–Mn–O structures by one up-scalable thin film deposition method ► Formation of o-LiMnO 2 by r.f. magnetron sputtering in combination with post-annealing ► Discharge capacity with o-LiMnO 2 cathodes twice as high as for c-LiMn 2 O 4 ► Thin film deposition of m-Li 2 MnO 3 and

  12. Synthesis and structural stability of Cr-doped Li2MnSiO4/C cathode materials by solid-state method

    Science.gov (United States)

    Cheng, Hong-Mei; Zhao, Shi-Xi; Wu, Xia; Zhao, Jian-Wei; Wei, Lei; Nan, Ce-Wen

    2018-03-01

    The crystal structure of the Li2MnSiO4 cathode material would collapse during the charge and discharge process because of that the Mn-O coordination polyhedron changed from [MnO4] into [MnO6] in the process of Mn+2 to Mn+4, but the Cr element could remain [CrO4] crystal ligand from Cr+2 to Cr+4, so Cr element substitution was used to improve the structural stability of the Li2MnSiO4 cathode material. In this work, Li2Mn1-xCrxSiO4/C nanocomposites were synthesized by solid-state method. XRD, SEM and TEM observations show that the as-prepared Li2Mn1-xCrxSiO4/C materials presents an orthorhombic crystal structure (S.G. Pmn21), the particle size of Li2Mn1-xCrxSiO4/C powder ranges from 50 to 100 nm. The XRD and XPS results indicate that Cr+2 is successfully doped into Li2MnSiO4 lattice and has well compatibility with Li2MnSiO4. The electrochemical results display that Li2Mn92.5%Cr7.5%SiO4/C exhibits significantly enhanced cycle stability and discharge capability. The initial discharge capacity of the Li2Mn92.5%Cr7.5%SiO4/C sample is 255 mAh g-1, and the discharge capacity was still about 60 mAh g-1 after 50 cycles. Furthermore, the XRD patterns, TEM images and Raman analysis reveal that the Cr doping enhances the structural stability of Li2Mn1-xCrxSiO4/C and improves the electrochemical activity of the cathode. Thus, the Li2Mn92.5%Cr7.5%SiO4/C have shown potential applications for lithium ion batteries.

  13. Synthesis and characterization of high-density LiFePO{sub 4}/C composites as cathode materials for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Chang Zhaorong [College of Chemistry and Environmental Science, Henan Normal University, Xinxiang 453007 (China)], E-mail: czr_56@163.com; Lv Haojie; Tang Hongwei; Li Huaji [College of Chemistry and Environmental Science, Henan Normal University, Xinxiang 453007 (China); Yuan Xiaozi; Wang Haijiang [Institute for Fuel Cell Innovation, National Research Council of Canada, Vancouver, BC, V6T 1W5 (Canada)

    2009-08-01

    To achieve a high-energy-density lithium electrode, high-density LiFePO{sub 4}/C composite cathode material for a lithium-ion battery was synthesized using self-produced high-density FePO{sub 4} as a precursor, glucose as a C source, and Li{sub 2}CO{sub 3} as a Li source, in a pipe furnace under an atmosphere of 5% H{sub 2}-95% N{sub 2}. The structure of the synthesized material was analyzed and characterized by X-ray diffraction (XRD) and scanning electron microscope (SEM). The electrochemical properties of the synthesized LiFePO{sub 4}/carbon composite were investigated by cyclic voltammetry (CV) and the charge/discharge process. The tap-density of the synthesized LiFePO{sub 4}/carbon composite powder with a carbon content of 7% reached 1.80 g m{sup -3}. The charge/discharge tests show that the cathode material has initial charge/discharge capacities of 190.5 and 167.0 mAh g{sup -1}, respectively, with a volume capacity of 300.6 mAh cm{sup -3}, at a 0.1C rate. At a rate of 5C, the LiFePO{sub 4}/carbon composite shows a high discharge capacity of 98.3 mAh g{sup -1} and a volume capacity of 176.94 mAh cm{sup -3}.

  14. Oxygen reduction kinetics and transport properties of (Ba,Sr)(Co,Fe)O3-δ solid oxide fuel cell cathode materials

    International Nuclear Information System (INIS)

    Wang, Lei; Merkle, Rotraut; Baumann, Frank S.; Maier, Joachim; Fleig, Juergen

    2007-01-01

    Full text: The oxygen reduction at the surface of cathode materials is crucial for the performance of solid oxide fuel cells (SOFC), but a detailed understanding of the mechanism is not available yet. (Ba x Sr 1-x )(Co 1-y Fe y )O 3-δ shows strongly improved oxygen reduction rates compared to previously applied perovskite cathode materials. In this work, surface rate constants as well as bulk transport properties are studied. (Ba x Sr 1-x )(Co 1-y Fe y )O 3-δ with 0≤x≤0.5, 0.2≤y≤1 was synthesized by the Pechini method. Oxygen stoichoimetry was obtained from thermo-gravimetric analysis, confirming that Ba 0.5 Sr 0.5 Co 0.8 Fe 0.2 O 3-δ has an exceptionally low oxygen content which is generally smaller than 2.5. Dense thin films were grown by pulsed laser deposition (PLD) and patterned into circular microelectrodes by photolithography. The surface resistance R s , which dominate the overall electrode resistance, were measured by impedance spectroscopy on individual microelectrodes at different T, pO 2 and applied electrical bias. PLD technique greatly helps to study the oxygen reduction kinetics since only measurements on dense thin films allow to record absolute R s values without interference from morphology effects. These R s values were found to be much lower than those for (La,Sr)(Co,Fe)O 3-δ . The variation of the surface reaction rates with A-site and B-site composition was studied and correlations with bulk materials properties such as oxygen nonstoichiometry, ionic mobility or oxidation enthalpy were examined. Plausible reaction mechanisms as well as possible reasons for the high absolute surface reaction rates will be discussed

  15. Technique of stowing packages containing radioactive materials during maritime transportation

    International Nuclear Information System (INIS)

    Ringot, G.; Chevalier, G.; Tomachevsky, E.; Draulans, J.; Lafontaine, I.

    1989-01-01

    The Mont Louis accident (August 25, 1984 - North Sea), in which uraniumhexafluoride packages were involved, alarmed a large number of European competent authorities, including the Commission of European Communities. The latter sponsored in 1986-1987 a bibliographic data collection to obtain a first view on the problem. (C.E.C contracts n degree 86-B-7015-11-004-17 and 86-B-7015-11-005-17). The collected data supply the necessary basis for further work, aiming to increase the safety of transporting radioactive material by ship. The study collected the different deceleration values, used by the transport companies and defined the accident conditions to be considered. This work can serve as a basis for later research to end with the proposal of a code of good practice for stowing. The research-work has been carried out jointly by C.E.A.-France, I.P.S.N. at Fontenay-aux-Roses and by Transnubel S.A. Brussels Belgium. The preliminary research included two main tasks: a statistical analysis, a bibliographic study of ship accidents

  16. Impact of container material on the development of Aedes aegypti larvae at different temperatures.

    Science.gov (United States)

    Kumar, Gaurav; Singh, R K; Pande, Veena; Dhiman, R C

    2016-01-01

    Aedes aegypti, the primary vector of dengue generally breeds in intradomestic and peridomestic containers made up of different materials, i.e. plastic, iron, rubber, earthen material etc. The material of container is likely to affect the temperature of water in container with variation in environmental temperature. The present study was aimed to determine the effect of different container materials on larval development of Ae. aegypti at different temperatures. Newly hatched I instar larvae (2-4 h old) were used in the study and experiments were conducted using three different containers made up of plastic, iron and earthen material. Three replicates for each type of container at 22, 26, 30, 34, 38, 40, and 42°C were placed in environmental chamber for the development of larvae. At temperatures >22°C, 50% pupation was completed in earthen pot within 4.3±0.6 to 6.3±0.6 days followed by plastic containers (5±0 to 8±0 days) and iron containers (6±0 to 9±0 days). Developmental time for 50% pupation in the three containers differed significantly (p containers (p containers resulted in significant variations in the developmental period of larvae. More than 35°C temperature of water was found inimical for pupal development. The results revealed the variation in temperature of water in different types of containers depending on the material of container, affecting duration of larval development. As the larval development was faster in earthen pot as compared to plastic and iron containers, community should be discouraged for storing the water in earthen pots. However, in view of containers of different materials used by the community in different temperature zones in the country, further studies are required for devising area-specific preventive measures for Aedes breeding.

  17. A soft chemical route to multicomponent lithium transition metal oxide nanowires as promising cathode materials for lithium secondary batteries

    International Nuclear Information System (INIS)

    Park, Dae-Hoon; Lim, Seung-Tae; Hwang, Seong-Ju

    2006-01-01

    We have synthesized 1D nanowires of lithium nickel manganese oxides with two different crystal structures through the chemical oxidation reaction of solid-state precursor LiMn 0.5 Ni 0.5 O 2 under hydrothermal condition. According to X-ray diffraction and elemental analyses, the nanowires obtained by persulfate treatments at 65 and 120 deg. C crystallize with a hexagonal layered and an α-MnO 2 -type structure, respectively, in which nickel and manganese ion