Beryllium satellite thrust cone design, manufacture and test

International Nuclear Information System (INIS)

Schneiter, H.; Chandler, D.

1977-01-01

Pre-formed beryllium sheet material has been used in the design, manufacturing and test of a satellite thrust cone structure. Adhesive bonding was used for attachment of aluminium flanges and conical segment lap strips. Difficulties in beryllium structure design such as incompatibilities with aluminium and handling problems are discussed. Testing to optimize beryllium-beryllium and beryllium-aluminium adhesive bonds is described. The completed thrust cone assembly has been subjected to static load testing and the results are presented. A summary of the relative merits of the use of beryllium in satellite structures is given with recommendations for future users. (author)

BPX toroidal field coil design

International Nuclear Information System (INIS)

Heitzenvoeder, D.J.

1992-01-01

This paper reports on the toroidal field (TF) coil system of the Burning Plasma Experiment (BPX) which consists of (18) beryllium copper magnets arrayed in a wedged configuration with a major radius of 2.6 meters and a field strength capability on axis of 9.0 Tesla. The toroidal array is constructed from six (3)-coil modules to facilitate remote recovery in the event of a magnet failure after nuclear activation precludes hands-on servicing. The magnets are of a modified Bitter plate design with partial cases of type 316-LN stainless steel welded with Inconel 182 weld wire. The coil turn plates are fabricated from CDA C17510 beryllium copper with optimized mechanical, thermal, and electrical characteristics. joints within the turns and between turns are made by welding with C17200 filler wire. Cryogenic cooling is employed to reduce power dissipation and to enhance performance. The magnets are cooled between experimental pulses by pressurized liquid nitrogen flowing through channels in the edges of the coil turns. This arrangement makes possible one full-power pulse per hour. Electrical insulation consists of polyimide-glass sheets bonded in place with vacuum-pressure impregnated epoxy/glass

New audio applications of beryllium metal

International Nuclear Information System (INIS)

Sato, M.

1977-01-01

The major applications of beryllium metal in the field of audio appliances are for the vibrating cones for the two types of speakers 'TWITTER' for high range sound and 'SQUAWKER' for mid range sound, and also for beryllium cantilever tube assembled in stereo cartridge. These new applications are based on the characteristic property of beryllium having high ratio of modulus of elasticity to specific gravity. The production of these audio parts is described, and the audio response is shown. (author)

Construction and assembling of the trim coils for the Milan superconducting cyclotron

International Nuclear Information System (INIS)

Baccaglioni, G.; Cartegni, G.C.; Fusetti, M.; Gini, L.; Grilli, L.

1986-01-01

This paper presents the main characteristics of the trim coils realized for the heavy ions superconducting cyclotron under construction at the Milan University. The guidelines in the choice of the conductor size, of the insulation and cooling parameters are discussed in some details. The main operations in the coils construction, as winding, impregnation, electrical tests and assembling, are described

Transition of W7-X non-planar coils from manufacturing to assembly

Energy Technology Data Exchange (ETDEWEB)

Ehrke, G. [Max-Planck-Institut fuer Plasmaphysik (IPP), EURATOM Association, Wendelsteinstrasse 1, D-17491 Greifswald (Germany)], E-mail: gunnar.ehrke@ipp.mpg.de

2009-06-15

The main magnetic field of Wendelstein 7-X fusion experiment (W7-X) at Max-Planck-Institut fuer Plasmaphysik Greifswald, Germany will be provided by 50 non-planar coils and supported by 20 planar coils. The non-planar coils were delivered by a consortium (CON) consisting of Babcock Noell GmbH Germany (BNG) and ASG Superconductors S.p.A. Italy (ASG). The coil production ended with the delivery of the last non-planar coil in March 2008 at the manufacturing branch of BNG in Zeitz, Germany. The construction of the coils was characterised by design changes, many rework actions and resulting time delays. Due to these numerous adjustments and changes a continuous improvement process was needed. This paper will give an overview about the transition of the non-planar coils from the acceptance tests at the manufacturer site to the beginning of the assembly at IPP. Furthermore this report will highlight technical interfaces in the period of transition.

N-terminal aliphatic residues dictate the structure, stability, assembly, and small molecule binding of the coiled-coil region of cartilage oligomeric matrix protein.

Science.gov (United States)

Gunasekar, Susheel K; Asnani, Mukta; Limbad, Chandani; Haghpanah, Jennifer S; Hom, Wendy; Barra, Hanna; Nanda, Soumya; Lu, Min; Montclare, Jin Kim

2009-09-15

The coiled-coil domain of cartilage oligomeric matrix protein (COMPcc) assembles into a homopentamer that naturally recognizes the small molecule 1,25-dihydroxyvitamin D(3) (vit D). To identify the residues critical for the structure, stability, oligomerization, and binding to vit D as well as two other small molecules, all-trans-retinol (ATR) and curcumin (CCM), here we perform an alanine scanning mutagenesis study. Ten residues lining the hydrophobic pocket of COMPcc were mutated into alanine; of the mutated residues, the N-terminal aliphatic residues L37, L44, V47, and L51 are responsible for maintaining the structure and function. Furthermore, two polar residues, T40 and Q54, within the N-terminal region when converted into alanine improve the alpha-helical structure, stability, and self-assembly behavior. Helical stability, oligomerization, and binding appear to be linked in a manner in which mutations that abolish helical structure and assembly bind poorly to vit D, ATR, and CCM. These results provide not only insight into COMPcc and its functional role but also useful guidelines for the design of stable, pentameric coiled-coils capable of selectively storing and delivering various small molecules.

Regulatory coiled-coil domains promote head-to-head assemblies of AAA+ chaperones essential for tunable activity control.

Science.gov (United States)

Carroni, Marta; Franke, Kamila B; Maurer, Michael; Jäger, Jasmin; Hantke, Ingo; Gloge, Felix; Linder, Daniela; Gremer, Sebastian; Turgay, Kürşad; Bukau, Bernd; Mogk, Axel

2017-11-22

Ring-forming AAA+ chaperones exert ATP-fueled substrate unfolding by threading through a central pore. This activity is potentially harmful requiring mechanisms for tight repression and substrate-specific activation. The AAA+ chaperone ClpC with the peptidase ClpP forms a bacterial protease essential to virulence and stress resistance. The adaptor MecA activates ClpC by targeting substrates and stimulating ClpC ATPase activity. We show how ClpC is repressed in its ground state by determining ClpC cryo-EM structures with and without MecA. ClpC forms large two-helical assemblies that associate via head-to-head contacts between coiled-coil middle domains (MDs). MecA converts this resting state to an active planar ring structure by binding to MD interaction sites. Loss of ClpC repression in MD mutants causes constitutive activation and severe cellular toxicity. These findings unravel an unexpected regulatory concept executed by coiled-coil MDs to tightly control AAA+ chaperone activity.

Static stress analysis of coupling superconducting solenoid coil assembly for muon ionization cooling experiment

International Nuclear Information System (INIS)

Pan Heng; Wang Li; Wu Hong; Guo Xinglong; Xu Fengyu

2010-01-01

The stresses in the coupling superconducting solenoid coil assembly, which is applied in the Muon Ionization Cooling Experiment (MICE), are critical for the structure design and mechanical stability because of a large diameter and relative high magnetic field. This paper presents an analytical stress solution for the MICE coupling coil assembly. The stress due to winding tension is calculated by assuming the coil package as a set of combined cylinders. The thermal and electromechanical stresses are obtained by solving the partial differential equations of displacement based on the power series expansion method. The analytical stress solution is proved to be feasible by calculating stresses in a tested superconducting solenoid with 2.58 m bore at room temperature. The analytical result of the MICE coupling coil is in good agreement with that of the finite element which shows that the transverse shear stress induced by Lorentz force is principally dominant to magnet instability. (authors)

Solid state bonding of beryllium-copper for an ITER first wall application

International Nuclear Information System (INIS)

Odegard, B.C. Jr.; Cadden, C.H.

1998-02-01

Several different joint assemblies were evaluated in support of a manufacturing technology for diffusion bonding a beryllium armor tile to a copper alloy heat sink for fusion reactor applications. Because beryllium reacts with all but a few elements to form intermetallic compounds, this study considered several different surface treatments as a means of both inhibiting these reactions and promoting a good diffusion bond between the two substrates. A diffusion bonded assemblies used aluminum or an aluminum-beryllium composite (AlBeMet-150) as the interfacial material in contact with beryllium. In most cases, explosive bonding was utilized as a technique for joining the copper alloy heat sink to an aluminum or AlBeMet-150 substrate, which was subsequently diffusion bonded to an aluminum coated beryllium tile. In this approach, a 250 microm thick titanium foil was used as a diffusion barrier between the copper and aluminum to prevent the formation of Cu-Al intermetallic phases. In all cases, a hot isostatic pressing (HIP) furnace was used in conjunction with canned assemblies in order to minimize oxidation and apply sufficient pressure on the assembly for excellent metal-to-metal contact and subsequent bonding. Several different processing schedules were evaluated during the course of this study; bonded assemblies were produced that failed outside the bond area indicating a 100% joint efficiency

Solid state bonding of beryllium-copper for an ITER first wall application

Energy Technology Data Exchange (ETDEWEB)

Odegard, B.C. Jr.; Cadden, C.H. [Sandia National Labs., Livermore, CA (United States)

1998-01-01

Several different joint assemblies were evaluated in support of a manufacturing technology for diffusion bonding a beryllium armor tile to a copper alloy heat sink for fusion reactor applications. Because beryllium reacts with all but a few elements to form intermetallic compounds, this study considered several different surface treatments as a means of both inhibiting these reactions and promoting a good diffusion bond between the two substrates. All diffusion bonded assemblies used aluminum or an aluminum-beryllium composite (AlBeMet-150) as the interfacial material in contact with beryllium. In most cases, explosive bonding was utilized as a technique for joining the copper alloy heat sink to an aluminum or AlBeMet-150 substrate, which was subsequently diffusion bonded to an aluminum coated beryllium tile. In this approach, a 250 {mu}m thick titanium foil was used as a diffusion barrier between the copper and aluminum to prevent the formation of Cu-Al intermetallic phases. In all cases, a hot isostatic pressing (HIP) furnace was used in conjunction with canned assemblies in order to minimize oxidation and apply sufficient pressure on the assembly for excellent metal-to-metal contact and subsequent bonding. Several different processing schedules were evaluated during the course of this study; bonded assemblies were produced that failed outside the bond area indicating a 100% joint efficiency. (author)

Development of all-beryllium riveted structures

International Nuclear Information System (INIS)

Floyd, D.R.; Leslie, W.W.; Miley, D.V.; Nokes, R.W.

1976-01-01

Results are presented of a development program aimed at making a full-scale, all-beryllium frustrum by riveted assembly methods. Included are descriptions of the sheet-metal fabrication practices and assembly plans. Results of extensive mechanical testing of both ingot- and powder-source beryllium products that are presented include tensile, notch-tensile, bearing, and shear tests. Although the full-size structure has not been built, examples are given of several conical and cylindrical structures that were made. The largest of these is a 20-in. diameter, 15-in. long cylinder that was roll-formed from one 0.050-in. thick ingot sheet and assembled with 60 countersunk rivets. Tensile testing of riveted flat coupons is also reported as is bulge testing of riveted cylindrical shells. A cost comparison of riveted deep-drawn and powder-source cylinders is made. Results show that when strength and dimensional tolerance requirements are not severe, a riveted assembly approach is warranted. 33 figures, 8 tables

Fabrication of First 4-m Coils for the LARP MQXFA Quadrupole and Assembly in Mirror Structure

CERN Document Server

Holik, E F; Anerella, M; Bossert, R; Cavanna, E; Cheng, D; Dietderich, D R; Ferracin, P; Ghosh, A K; Izquierdo Bermudez, S; Krave, S; Nobrega, A; Perez, J C; Pong, I; Sabbi, G L; Santini, C; Schmalzle, J; Wanderer, P; Wang, X; Yu, M

2017-01-01

The US LHC Accelerator Research Program is constructing prototype interaction region quadrupoles as part of the US in-kind contribution to the Hi-Lumi LHC project. The low-beta MQXFA Q1/Q3 coils have a 4-m length and a 150 mm bore. The design is first validated on short, one meter models (MQXFS) developed as part of the longstanding Nb$_{3}$Sn quadrupole R&D; by LARP in collaboration with CERN. In parallel, facilities and tooling are being developed and refined at BNL, LBNL, and FNAL to enable long coil production, assembly, and cold testing. Long length scale-up is based on the experience from the LARP 90 mm aperture (TQ-LQ) and 120 mm aperture (HQ and Long HQ) programs. A 4-m long MQXF practice coil was fabricated, water jet cut and analyzed to verify procedures, parts, and tooling. In parallel, the first complete prototype coil (QXFP01a) was fabricated and assembled in a long magnetic mirror, MQXFPM1, to provide early feedback on coil design and fabrication following the successful experience of previo...

Quasistationary magnetic field generation with a laser-driven capacitor-coil assembly.

Science.gov (United States)

Tikhonchuk, V T; Bailly-Grandvaux, M; Santos, J J; Poyé, A

2017-08-01

Recent experiments are showing possibilities to generate strong magnetic fields on the excess of 500 T with high-energy nanosecond laser pulses in a compact setup of a capacitor connected to a single turn coil. Hot electrons ejected from the capacitor plate (cathode) are collected at the other plate (anode), thus providing the source of a current in the coil. However, the physical processes leading to generation of currents exceeding hundreds of kiloamperes in such a laser-driven diode are not sufficiently understood. Here we present a critical analysis of previous results and propose a self-consistent model for the high current generation in a laser-driven capacitor-coil assembly. It accounts for three major effects controlling the diode current: the space charge neutralization, the plasma magnetization between the capacitor plates, and the Ohmic heating of the external circuit-the coil-shaped connecting wire. The model provides the conditions necessary for transporting strongly super-Alfvenic currents through the diode on the time scale of a few nanoseconds. The model validity is confirmed by a comparison with the available experimental data.

Coil-springs used as mechanical filter. Modification of the bottom tie plate of a fuel assembly

International Nuclear Information System (INIS)

Nylund, O.

1993-01-01

Describes an improved design of the bottom tie plate of a fuel assembly. The improvement of the design is an arrangement of horizontal channels holding coil-springs and crossing the vertical channels for the cooling water. The coil-springs work as strainers for the cooling water

Beryllium

Science.gov (United States)

Foley, Nora K.; Jaskula, Brian W.; Piatak, Nadine M.; Schulte, Ruth F.; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

2017-12-19

Beryllium is a mineral commodity that is used in a variety of industries to make products that are essential for the smooth functioning of a modern society. Two minerals, bertrandite (which is supplied domestically) and beryl (which is currently supplied solely by imports), are necessary to ensure a stable supply of high-purity beryllium metal, alloys, and metal-matrix composites and beryllium oxide ceramics. Although bertrandite is the source mineral for more than 90 percent of the beryllium produced globally, industrial beryl is critical for the production of the very high purity beryllium metal needed for some strategic applications. The current sole domestic source of beryllium is bertrandite ore from the Spor Mountain deposit in Utah; beryl is imported mainly from Brazil, China, Madagascar, Mozambique, and Portugal. High-purity beryllium metal is classified as a strategic and critical material by the Strategic Materials Protection Board of the U.S. Department of Defense because it is used in products that are vital to national security. Beryllium is maintained in the U.S. stockpile of strategic materials in the form of hot-pressed beryllium metal powder.Because of its unique chemical properties, beryllium is indispensable for many important industrial products used in the aerospace, computer, defense, medical, nuclear, and telecommunications industries. For example, high-performance alloys of beryllium are used in many specialized, high-technology electronics applications, as they are energy efficient and can be used to fabricate miniaturized components. Beryllium-copper alloys are used as contacts and connectors, switches, relays, and shielding for everything from cell phones to thermostats, and beryllium-nickel alloys excel in producing wear-resistant and shape-retaining high-temperature springs. Beryllium metal composites, which combine the fabrication ability of aluminum with the thermal conductivity and highly elastic modulus of beryllium, are ideal for

A periodic table of coiled-coil protein structures.

Science.gov (United States)

Moutevelis, Efrosini; Woolfson, Derek N

2009-01-23

Coiled coils are protein structure domains with two or more alpha-helices packed together via interlacing of side chains known as knob-into-hole packing. We analysed and classified a large set of coiled-coil structures using a combination of automated and manual methods. This led to a systematic classification that we termed a "periodic table of coiled coils," which we have made available at http://coiledcoils.chm.bris.ac.uk/ccplus/search/periodic_table. In this table, coiled-coil assemblies are arranged in columns with increasing numbers of alpha-helices and in rows of increased complexity. The table provides a framework for understanding possibilities in and limits on coiled-coil structures and a basis for future prediction, engineering and design studies.

Research on neutron energy spectrum of the beryllium, iron and polyethylene shells assemblies injected by D-T neutron

International Nuclear Information System (INIS)

An, Li; Guo, Haiping; Wang, Xinhua

2009-04-01

To test a simulation code, the multi-shell assemblies were established, which were made of beryllium stainless steel and polyethylene from the interior to the outer. The symmetry axes are all in the line of the D + beam. The neutron energy spectra above 1 MeV were obtained in medium by the detector of stilbene crystal of φ18 min x 20 mm. The distance between source and the spherical surface was 30 cm and 50 cm. The measurement channels are in the angle 0 degree and 120 degree relative to D + beam direction. The measurement positions are 0 cm, 9.7 cm, 12.8 cm and 17.3 cm away from the center of the assembly in both directions. The spectrum in different positions of the multi-shell assemblies in medium were compared and analyzed. (authors)

Development of all-beryllium riveted structures. [Frustrum; cylinders; cones

Energy Technology Data Exchange (ETDEWEB)

Floyd, D. R.; Leslie, W. W.; Miley, D. V.; Nokes, R. W.

1976-04-20

Results are presented of a development program aimed at making a full-scale, all-beryllium frustrum by riveted assembly methods. Included are descriptions of the sheet-metal fabrication practices and assembly plans. Results of extensive mechanical testing of both ingot- and powder-source beryllium products that are presented include tensile, notch-tensile, bearing, and shear tests. Although the full-size structure has not been built, examples are given of several conical and cylindrical structures that were made. The largest of these is a 20-in. diameter, 15-in. long cylinder that was roll-formed from one 0.050-in. thick ingot sheet and assembled with 60 countersunk rivets. Tensile testing of riveted flat coupons is also reported as is bulge testing of riveted cylindrical shells. A cost comparison of riveted deep-drawn and powder-source cylinders is made. Results show that when strength and dimensional tolerance requirements are not severe, a riveted assembly approach is warranted. 33 figures, 8 tables. (auth)

NCSX Trim Coil Design

International Nuclear Information System (INIS)

Kalish, M.; Brooks, A.; Rushinski, J.; Upcavage, R.

2009-01-01

The National Compact Stellarator Experiment (NCSX) was being constructed at the Princeton Plasma Physics Laboratory in partnership with Oak Ridge National Laboratory before work was stopped in 2008. The objective of this experiment was to develop the stellarator concept and evaluate it's potential as a model for future fusion power plants. Stellarator design requires very precisely positioned Modular Coils of complex shape to form 3D plasmas. In the design of NCSX, Trim Coils were required to compensate for both the positioning of the coils during assembly and the fabrication tolerances of the Modular Coils. Use of the Trim Coils allowed for larger tolerances increasing ease of assembly and decreasing overall cost. A set of Trim coils was developed to suppress the toroidal flux in island regions due to misalignment, magnetic materials, and eddy currents. The requirement imposed upon the design forced the toroidal flux in island regions below 10% of the total toroidal flux in the plasma. An analysis was first performed to evaluate candidate Trim Coil configurations iterating both the size, number, and position of the coils. The design was optimized considering both performance and cost while staying within the tight restraints presented by the space limited geometry. The final design of the Trim Coils incorporated a 48 Coil top bottom symmetric set. Fabrication costs were minimized by having only two coil types and using a planar conventional design with off the shelf commercial conductor. The Trim Coil design incorporated supports made from simple structural shapes assembled together in a way which allowed for adjustment as well as accommodation for the tolerance build up on the mating surfaces. This paper will summarize the analysis that led to the optimization of the Trim Coils set, the trim coil mechanical design, thermal and stress analysis, and the design of the supporting Trim Coil structure

SPECTROGRAPHIC DETERMINATION OF BERYLLIUM IN OILFIELD WATERS USING A PLASMA ARC

Energy Technology Data Exchange (ETDEWEB)

Collins, A. G.; Pearson, C. A.

1963-10-15

Geochemical studies of the distribution of the trace, minor, and major constituents of oilfield waters aid in the exploration for petroleum and other minerals, determination of the origin and distribution of oilfield waters and petroleum, and location of casing leaks and of water pollution sources. The determination of the beryllium and related data should be useful in these studies. An emission spectrographic method utilizing a plasma arc assembly for determining beryllium in oilfield waters, with a sensitivity permitting detection of less than 1 ppb, was developed. Beryllium was extracted from synthetic and natural oilfield waters with chloroform and acetylacetone. The extracts were aspirated directly into the plasma arc, and the beryllium emission intensity was recorded on photographic plates. (auth)

Beryllium. Evaluation of beryllium hydroxide industrial processes. Pt. 3

International Nuclear Information System (INIS)

Lires, O.A.; Delfino, C.A.; Botbol, J.

1991-01-01

This work continues the 'Beryllium' series. It is a historical review of different industrial processes of beryllium hydroxide obtention from beryllium ores. Flowsheats and operative parameters of five plants are provided. These plants (Degussa, Brush Beryllium Co., Beryllium Corp., Murex Ltd., SAPPI) were selected as representative samples of diverse commercial processes in different countries. (Author) [es

Structure of bacteriophage T4 fibritin: a segmented coiled coil and the role of the C-terminal domain.

Science.gov (United States)

Tao, Y; Strelkov, S V; Mesyanzhinov, V V; Rossmann, M G

1997-06-15

Oligomeric coiled-coil motifs are found in numerous protein structures; among them is fibritin, a structural protein of bacteriophage T4, which belongs to a class of chaperones that catalyze a specific phage-assembly process. Fibritin promotes the assembly of the long tail fibers and their subsequent attachment to the tail baseplate; it is also a sensing device that controls the retraction of the long tail fibers in adverse environments and, thus, prevents infection. The structure of fibritin had been predicted from sequence and biochemical analyses to be mainly a triple-helical coiled coil. The determination of its structure at atomic resolution was expected to give insights into the assembly process and biological function of fibritin, and the properties of modified coiled-coil structures in general. The three-dimensional structure of fibritin E, a deletion mutant of wild-type fibritin, was determined to 2.2 A resolution by X-ray crystallography. Three identical subunits of 119 amino acid residues form a trimeric parallel coiled-coil domain and a small globular C-terminal domain about a crystallographic threefold axis. The coiled-coil domain is divided into three segments that are separated by insertion loops. The C-terminal domain, which consists of 30 residues from each subunit, contains a beta-propeller-like structure with a hydrophobic interior. The residues within the C-terminal domain make extensive hydrophobic and some polar intersubunit interactions. This is consistent with the C-terminal domain being important for the correct assembly of fibritin, as shown earlier by mutational studies. Tight interactions between the C-terminal residues of adjacent subunits counteract the latent instability that is suggested by the structural properties of the coiled-coil segments. Trimerization is likely to begin with the formation of the C-terminal domain which subsequently initiates the assembly of the coiled coil. The interplay between the stabilizing effect of the C

Investigation of fracture in pressurized gas metal arc welded beryllium

International Nuclear Information System (INIS)

Heiple, C.R.; Merlini, R.J.; Adams, R.O.

1976-01-01

Premature failures during proof testing of pressurized-gas-metal-arc (PGMA) welded beryllium assemblies were investigated. The failures were almost entirely within the beryllium (a forming grade, similar to HP-10 or S-240), close to and parallel to the weld interface. The aluminum-silicon weld filler metal deposit was not centered in the weld groove in the failed assemblies, and failure occurred on the side of the weld opposite the bias in the weld deposit. Tensile tests of welded samples demonstrated that the failures were unrelated to residual machining damage from cutting the weld groove, and indicated small lack-of-fusion areas near the weld start to be the most likely origin of the failures. Acoustic emission was monitored during tensile tests of the welds. The majority of acoustic emission was probably from crack propagation through the weld filler metal. Tensile bars cut from the region of the weld start behaved differently; they failed at lower loads and exhibited an acoustic emission behavior believed to be from cracking in the weld metal-beryllium interface. Improvement in the quality of these and similar beryllium welds can therefore most likely be made by centering the weld deposit and reducing the size of the weld start defect. 21 fig

(Beryllium). Internal Report No. 137, Jan. 15, 1958; Le beryllium

Energy Technology Data Exchange (ETDEWEB)

Mouret, P; Rigaud, A

1959-07-01

After a brief summary of the physical and chemical properties of beryllium, the various chemical treatments which can be applied to beryllium minerals either directly or after a physical enrichment are discussed. These various treatments give either the hydroxide or beryllium salts, from which either beryllium oxide or metallic beryllium can easily be obtained. The purification, analysis and uses of beryllium are also briefly discussed. (author)

Beryllium production using beryllium fluoride

International Nuclear Information System (INIS)

Hubler, Carlos Henrique

1993-01-01

This work presents the beryllium production by thermal decomposition of the ammonium beryllium fluoride, followed by magnesium reduction, obtained in the small pilot plant of the Brazilian National Nuclear Energy Commission - Nuclear Engineering Institute

Beryllium and copper-beryllium alloys; Beryllium und Kupfer-Beryllium-Legierungen

Energy Technology Data Exchange (ETDEWEB)

Nagel, Nikolaus [Materion Brush GmbH, Stuttgart (Germany). Operation and Quality/EH and S

2017-02-15

The light metal beryllium is a comparatively rare element, which today is primarily derived from bertrandite. It is mainly used as pure metal or in the form of copper-beryllium alloys, e.g., in automotive industry, aerospace, and electrical components. The wide range of applications is mainly attributed to the extremely high rigidity/density ratio. An overview of the history of the metal, its production, and recycling as well as the properties of CuBe alloys are given.

Method for welding beryllium

Science.gov (United States)

Dixon, R.D.; Smith, F.M.; O`Leary, R.F.

1997-04-01

A method is provided for joining beryllium pieces which comprises: depositing aluminum alloy on at least one beryllium surface; contacting that beryllium surface with at least one other beryllium surface; and welding the aluminum alloy coated beryllium surfaces together. The aluminum alloy may be deposited on the beryllium using gas metal arc welding. The aluminum alloy coated beryllium surfaces may be subjected to elevated temperatures and pressures to reduce porosity before welding the pieces together. The aluminum alloy coated beryllium surfaces may be machined into a desired welding joint configuration before welding. The beryllium may be an alloy of beryllium or a beryllium compound. The aluminum alloy may comprise aluminum and silicon. 9 figs.

Method for welding beryllium

International Nuclear Information System (INIS)

Dixon, R.D.; Smith, F.M.; O'Leary, R.F.

1997-01-01

A method is provided for joining beryllium pieces which comprises: depositing aluminum alloy on at least one beryllium surface; contacting that beryllium surface with at least one other beryllium surface; and welding the aluminum alloy coated beryllium surfaces together. The aluminum alloy may be deposited on the beryllium using gas metal arc welding. The aluminum alloy coated beryllium surfaces may be subjected to elevated temperatures and pressures to reduce porosity before welding the pieces together. The aluminum alloy coated beryllium surfaces may be machined into a desired welding joint configuration before welding. The beryllium may be an alloy of beryllium or a beryllium compound. The aluminum alloy may comprise aluminum and silicon. 9 figs

Mechanisms of hydrogen retention in metallic beryllium and beryllium oxide and properties of ion-induced beryllium nitride

International Nuclear Information System (INIS)

Oberkofler, Martin

2011-01-01

In the framework of this thesis laboratory experiments on atomically clean beryllium surfaces were performed. They aim at a basic understanding of the mechanisms occurring upon interaction of a fusion plasma with a beryllium first wall. The retention and the temperature dependent release of implanted deuterium ions are investigated. An atomistic description is developed through simulations and through the comparison with calculations based on density functional theory. The results of these investigations are compared to the behaviour of hydrogen upon implantation into thermally grown beryllium oxide layers. Furthermore, beryllium nitride is produced by implantation of nitrogen into metallic beryllium and its properties are investigated. The results are interpreted with regard to the use of beryllium in a fusion reactor. (orig.)

Beryllium and growth. II. The effect of beryllium on plant growth

Energy Technology Data Exchange (ETDEWEB)

Hoagland, M B

1952-01-01

Experiments were undertaken to determine whether beryllium could replace magnesium in a growing organism. This was stimulated by the several known growth effects of beryllium in animals and by the fact that beryllium apparently competes with magnesium for animal alkaline phosphatases. The following findings are noted: (1) beryllium can reduce the magnesium requirement of plants by some 60% within a certain range of magnesium deficiency. (2) The residual obligatory magnesium requirements is probably accounted for by chlorophyll since beryllium appears to have no primary effect on chlorophyll or chlorophyll production. (3) The pH of the nutrient solution is critical: at acid pH's, beryllium is highly toxic, and growth increase due to beryllium only appears at initial pH's above 11.2, although this initial pH rapidly falls to neutrality during the experimental period. 22 references, 4 figures, 1 table.

Plasma spraying of beryllium and beryllium-aluminum-silver alloys

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Elliott, K.E.; Jacobson, L.A.

1994-01-01

A preliminary investigation on plasma-spraying of beryllium and a beryllium-aluminum-4% silver alloy was done at the Los Alamos National Laboratory's Beryllium Atomization and Thermal Spray Facility (BATSF). Spherical Be and Be-Al-4%Ag powders, which were produced by centrifugal atomization, were used as feedstock material for plasma-spraying. The spherical morphology of the powders allowed for better feeding of fine (<38 μm) powders into the plasma-spray torch. The difference in the as-deposited densities and deposit efficiencies of the two plasma-sprayed powders will be discussed along with the effect of processing parameters on the as-deposited microstructure of the Be-Al-4%Ag. This investigation represents ongoing research to develop and characterize plasma-spraying of beryllium and beryllium-aluminum alloys for magnetic fusion and aerospace applications

Plasma spraying of beryllium and beryllium-aluminum-silver alloys

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Elliott, K.E.; Jacobson, L.A.

1993-01-01

A preliminary investigation on plasma-spraying of beryllium and a beryllium-aluminum 4% silver alloy was done at the Los Alamos National Laboratory's Beryllium Atomization and Thermal Spray Facility (BATSF). Spherical Be and Be-Al-4%Ag powders, which were produced by centrifugal atomization, were used as feedstock material for plasma-spraying. The spherical morphology of the powders allowed for better feeding of fine (<38 μm) powders into the plasma-spray torch. The difference in the as-deposited densities and deposit efficiencies of the two plasma-sprayed powders will be discussed along with the effect of processing parameters on the as-deposited microstructure of the Be-Al-4%Ag. This investigation represents ongoing research to develop and characterize plasma-spraying of beryllium and beryllium-aluminum alloys for magnetic fusion and aerospace applications

The heterotrimeric laminin coiled-coil domain exerts anti-adhesive effects and induces a pro-invasive phenotype.

Directory of Open Access Journals (Sweden)

Patricia Santos-Valle

Full Text Available Laminins are large heterotrimeric cross-shaped extracellular matrix glycoproteins with terminal globular domains and a coiled-coil region through which the three chains are assembled and covalently linked. Laminins are key components of basement membranes, and they serve as attachment sites for cell adhesion, migration and proliferation. In this work, we produced a recombinant fragment comprising the entire laminin coiled-coil of the α1-, β1-, and γ1-chains that assemble into a stable heterotrimeric coiled-coil structure independently of the rest of the molecule. This domain was biologically active and not only failed to serve as a substrate for cell attachment, spreading and focal adhesion formation but also inhibited cell adhesion to laminin when added to cells in a soluble form at the time of seeding. Furthermore, gene array expression profiling in cells cultured in the presence of the laminin coiled-coil domain revealed up-regulation of genes involved in cell motility and invasion. These findings were confirmed by real-time quantitative PCR and zymography assays. In conclusion, this study shows for the first time that the laminin coiled-coil domain displays anti-adhesive functions and has potential implications for cell migration during matrix remodeling.

Superconducting coil system and methods of assembling the same

Science.gov (United States)

Rajput-Ghoshal, Renuka; Rochford, James H.; Ghoshal, Probir K.

2016-01-19

A superconducting magnet apparatus is provided. The superconducting magnet apparatus includes a power source configured to generate a current; a first switch coupled in parallel to the power source; a second switch coupled in series to the power source; a coil coupled in parallel to the first switch and the second switch; and a passive quench protection device coupled to the coil and configured to by-pass the current around the coil and to decouple the coil from the power source when the coil experiences a quench.

Beryllium

International Nuclear Information System (INIS)

Hansen, N.B.

1980-01-01

A method for determination of beryllium in minerals and rocks is described. The method comprises microanalysis and trace analysis. Because of the toxidity of beryllium the method is designed for determination of a hitherto unknown small amount, 1-10 nanogram Be. With the optimal amount for determination, 3 ng Be, the relative error of the method is 10%. The description includes an inventory of chemicals and apparatus, also an example of application of the method on the mineral epididymite. In brief, the sample is melted with sodium carbonate and sodium tetra borate; when required the sample in advance is fumed with hydrogen fluoride and sulphuric acid to evaporate silica. The residuum is dissolved in water and hydrogen chloride, upon which the solution is made to volume. In the Ring oven interfering compounds are masked with EDTA. Beryllium is settled with chrome azurol and ammonia. Beryllium is identified and evaluated in comparison with previously produced standards. (author)

Beryllium

International Nuclear Information System (INIS)

Hansen, N.B.

1979-01-01

A method for determination of beryllium in minerals and rocks is described. The method comprises microanalysis and trace analysis. Because of the toxidity of beryllium the method is designed for determination of a hitherto unknown small amount, 1-10 nanogram Be. With the optimal amount for determination, 3 ng Be, the relative error of the method is 10%. The description includes an inventory of chemicals and apparatus, also an example of application of the method on the mineral epididymite. In brief, the sample is melted with sodium carbonate and sodium tetra borate; when required the sample in advance is fumed with hydrogen fluoride and sulphuric acid to evaporate silica. The residuum is dissolved in water and hydrogen chloride, upon which the solution is made to volume. In the Ring oven interfering compounds are masked with EDTA. Beryllium is settled with chrome azurol and ammonia. Beryllium is identified and evaluated in comparison with previously produced standards. (author)

Beryllium health effects in the era of the beryllium lymphocyte proliferation test.

Science.gov (United States)

Maier, L A

2001-05-01

The beryllium lymphocyte proliferation test (BeLPT) has revolutionized our approach to the diagnosis, screening, and surveillance of beryllium health effects. Based on the development of a beryllium-specific cell-mediated immune response, the BeLPT has allowed us to define early health effects of beryllium, including beryllium sensitization (BeS), and chronic beryllium disease (CBD) at a subclinical stage. The use of this test as a screening tool has improved our understanding of these health effects. From a number of studies it is apparent that BeS precedes CBD and develops after as little as 9 weeks of beryllium exposure. CBD occurs within 3 months and up to 30 years after initial beryllium exposure. Exposure-response variables have been associated with BeS/CBD, including work as a machinist, chemical or metallurgical operator, laboratory technician, work in ceramics or beryllium metal production, and years of beryllium exposure. Recent studies have found BeS and CBD in workplaces in which the majority of exposures were below the 2 microg/m3 OSHA time-weighted average (TWA). Ideally, the BeLPT would be used in surveillance aimed at defining other risk-related processes, determining exposure variables which predict BeS and CBD, and defining the exposure level below which beryllium health effects do not occur. Unfortunately, the BeLPT can result in false negative tests and still requires an invasive procedure, a bronchoscopy, for the definitive diagnosis of CBD. Thus, research is needed to establish new tests to be used alone or in conjunction with the BeLPT to improve our ability to detect early beryllium health effects.

Analysis of the KANT experiment on beryllium using TRIPOLI-4 Monte Carlo code

International Nuclear Information System (INIS)

Lee, Yi-Kang

2011-01-01

Beryllium is an important material in fusion technology for multiplying neutrons in blankets. However, beryllium nuclear data are differently presented in modern nuclear data evaluations. Recent investigations with the TRIPOLI-4 Monte Carlo simulation of the tritium breeding ratio (TBR) demonstrated that beryllium reaction data are the main source of the calculation uncertainties between ENDF/B-VII.0 and JEFF-3.1. To clarify the calculation uncertainties from data libraries on beryllium, in this study TRIPOLI-4 calculations of the Karlsruhe Neutron Transmission (KANT) experiment have been performed by using ENDF/B-VII.0 and new JEFF-3.1.1 data libraries. The KANT Experiment on beryllium has been used to validate neutron transport codes and nuclear data libraries. An elaborated KANT experiment benchmark has been compiled and published in the NEA/SINBAD database and it has been used as reference in the present work. The neutron multiplication in bulk beryllium assemblies was considered with a central D-T neutron source. Neutron leakage spectra through the 5, 10, and 17 cm thick spherical beryllium shells were calculated and five-group partial leakage multiplications were reported and discussed. In general, improved C/E ratios on neutron leakage multiplications have been obtained. Both ENDF/B-VII.0 and JEFF-3.1.1 beryllium data libraries of TRIPOLI-4 are acceptable now for fusion neutronics calculations.

Corrosion of beryllium

International Nuclear Information System (INIS)

Mueller, J.J.; Adolphson, D.R.

1987-01-01

The corrosion behavior of beryllium in aqueous and elevated-temperature oxidizing environments has been extensively studied for early-intended use of beryllium in nuclear reactors and in jet and rocket propulsion systems. Since that time, beryllium has been used as a structural material in les corrosive environments. Its primary applications include gyro systems, mirror and reentry vehicle structures, and aircraft brakes. Only a small amount of information has been published that is directly related to the evaluation of beryllium for service in the less severe or normal atmospheric environments associated with these applications. Despite the lack of published data on the corrosion of beryllium in atmospheric environments, much can be deduced about its corrosion behavior from studies of aqueous corrosion and the experiences of fabricators and users in applying, handling, processing, storing, and shipping beryllium components. The methods of corrosion protection implemented to resist water and high-temperature gaseous environments provide useful information on methods that can be applied to protect beryllium for service in future long-term structural applications

SOURCE AND PATHWAY DETERMINATION FOR BERYLLIUM FOUND IN BECHTEL NEVADA NORTH LAS VEGAS FACILITIES

Energy Technology Data Exchange (ETDEWEB)

BECHTEL NEVADA

2004-07-01

In response to the report ''Investigation of Beryllium Exposure Cases Discovered at the North Las Vegas Facility of the National Nuclear Security Administration'', published by the U.S. Department of Energy (DOE), National Nuclear Security Administration (NNSA) in August 2003, Bechtel Nevada (BN) President and General Manager Dr. F. A. Tarantino appointed the Beryllium Investigation & Assessment Team (BIAT) to identify both the source and pathway for the beryllium found in the North Las Vegas (NLV) B-Complex. From September 8 to December 18, 2003, the BIAT investigated the pathway for beryllium and determined that a number of locations existed at the Nevada Test Site (NTS) which could have contained sufficient quantities of beryllium to result in contamination if transported. Operations performed in the B-1 Building as a result of characterization activities at the Engine Maintenance, Assembly, and Disassembly (EMAD); Reactor Maintenance, Assembly, and Disassembly (RMAD); Test Cells A and C; and the Central Support Facility in Area 25 had the greatest opportunity for transport of beryllium. Investigative monitoring and sampling was performed at these sites with subsequent transport of sample materials, equipment, and personnel from the NTS to the B-1 Building. The timeline established by the BIAT for potential transport of the beryllium contamination into the B-1 Building was from September 1997 through November 2002. Based on results of recently completed swipe sampling, no evidence of transport of beryllium from test areas has been confirmed. Results less than the DOE beryllium action level of 0.2 ???g/100 cm2 were noted for work support facilities located in Area 25. All of the identified sites in Area 25 worked within the B-1 tenant's residency timeline have been remediated. Legacy contaminants have either been disposed of or capped with clean borrow material. As such, no current opportunity exists for release or spread of beryllium

Laser fabrication of beryllium components

International Nuclear Information System (INIS)

Hanafee, J.E.; Ramos, T.J.

1995-08-01

Working with the beryllium industry on commercial applications and using prototype parts, the authors have found that the use of lasers provides a high-speed, low-cost method of cutting beryllium metal, beryllium alloys, and beryllium-beryllium oxide composites. In addition, they have developed laser welding processes for commercial structural grades of beryllium that do not need a filler metal; i.e., autogenous welds were made in commercial structural grades of beryllium by using lasers

Sub-20 nm Stable Micelles Based on a Mixture of Coiled-Coils: A Platform for Controlled Ligand Presentation.

Science.gov (United States)

Ang, JooChuan; Ma, Dan; Jung, Benson T; Keten, Sinan; Xu, Ting

2017-11-13

Ligand-functionalized, multivalent nanoparticles have been extensively studied for biomedical applications from imaging agents to drug delivery vehicles. However, the ligand cluster size is usually heterogeneous and the local valency is ill-defined. Here, we present a mixed micelle platform hierarchically self-assembled from a mixture of two amphiphilic 3-helix and 4-helix peptide-polyethylene glycol (PEG)-lipid hybrid conjugates. We demonstrate that the local multivalent ligand cluster size on the micelle surface can be controlled based on the coiled-coil oligomeric state. The oligomeric states of mixed peptide bundles were found to be in their individual native states. Similarly, mixed micelles indicate the orthogonal self-association of coiled-coil amphiphiles. Using differential scanning calorimetry, fluorescence recovery spectroscopy, and coarse-grained molecular dynamics simulation, we studied the distribution of coiled-coil bundles within the mixed micelles and observed migration of coiled-coils into nanodomains within the sub-20 nm mixed micelle. This report provides important insights into the assembly and formation of nanophase-separated micelles with precise control over the local multivalent state of ligands on the micelle surface.

Highlights from the assembly of the helical field coils for the Advanced Toroidal Facility

International Nuclear Information System (INIS)

Benson, R.D.

1985-01-01

The helical field (HF) coils in the Advanced Toroidal Facility (ATF) device consist of a set of 24 identical segments connected to form a continuous pair of helical coils wrapped around a toroidal vacuum vessel. Each segment weighs approximately 1364 kg (3000 lb) and is composed of 14 water-cooled copper plate conductors bolted to a cast stainless steel structural support member with a T-shape cross section (known as the structural tee). The segment components are electrically insulated with Kapton adhesive tape, G-10, Tefzel, and rubber to withstand 2.5 kV. As a final insulator and structural support, the entire segment is vacuum impregnated with epoxy. This paper offers a brief overview of the processes used to assemble the component parts into a completed segment, including identification of items that required special attention. 4 figs

Beryllium and growth. III. The effect of beryllium on plant phosphatase

Energy Technology Data Exchange (ETDEWEB)

Hoagland, M B

1952-01-01

The purpose of the investigations was to correlate the apparent ability of beryllium to substitute for magnesium in plant growth with a specific biochemical effect of the metal. Through association with earlier work on beryllium inhibition of animal alkaline phosphatase, a study was made of the effect of beryllium and other metals upon the activity of a phosphatase derived from tomato leaves. Although only indirect evidence is available that this enzyme system was magnesium-activated, beryllium was found to inhibit reversibly the splitting of GP and ATP. Other metals were also found to be inhibitory but the ATP-ase inhibition - and especially the ratio of P split from GP to P split from ATP - was higher for beryllium than for any other metal studied. The significance of this finding in relation to energy metabolism, growth, and beryllium toxicity is discussed. 12 references, 5 figures, 2 tables.

Beryllium chemistry and processing

CERN Document Server

Walsh, Kenneth A

2009-01-01

This book introduces beryllium; its history, its chemical, mechanical, and physical properties including nuclear properties. The 29 chapters include the mineralogy of beryllium and the preferred global sources of ore bodies. The identification and specifics of the industrial metallurgical processes used to form oxide from the ore and then metal from the oxide are thoroughly described. The special features of beryllium chemistry are introduced, including analytical chemical practices. Beryllium compounds of industrial interest are identified and discussed. Alloying, casting, powder processing, forming, metal removal, joining and other manufacturing processes are covered. The effect of composition and process on the mechanical and physical properties of beryllium alloys assists the reader in material selection. The physical metallurgy chapter brings conformity between chemical and physical metallurgical processing of beryllium, metal, alloys, and compounds. The environmental degradation of beryllium and its all...

Progress on the RF Coupling Coil Module Design for the MICE Channel

International Nuclear Information System (INIS)

Li, D.; Green, M.A.; Virostek, S.P.; Zisman, M.S.; Lau, W.; White, A.E.; Yang, S.Q.

2005-01-01

We describe the progress on the design of the RF coupling coil (RFCC) module for the international Muon Ionization Cooling Experiment (MICE) at Rutherford Appleton Laboratory (RAL) in the UK. The MICE cooling channel design consists of one SFOFO cell that is similar to that of the US Study-II of a neutrino factory. The MICE RFCC module comprises a superconducting solenoid, mounted around four normal conducting 201.25-MHz RF cavities. Each cavity has a pair of thin curved beryllium windows to close the conventional open beam irises, which allows for independent control of the phase in each cavity and for the RF power to be fed separately. The coil package that surrounds the RF cavities is mounted on a vacuum vessel. The RF vacuum is shared between the cavities and the vacuum vessel around the cavities such that there is no differential pressure on the thin beryllium windows. This paper discusses the design progress of the RFCC module and the fabrication progress of a prototype 201.25-MHz cavity

Beryllium. Beryllium oxide, obtention and properties. Pt.4

International Nuclear Information System (INIS)

Lires, O.A.; Delfino, C.A.; Botbol, J.

1991-01-01

As a continuation of the 'Beryllium' series this work reviews several methods of high purity beryllia production. Diverse methods of obtention and purification from different beryllium compounds are described. Some chemical, mechanical and electrical properties related with beryllia obtention methods are summarized. (Author) [es

Beryllium

International Nuclear Information System (INIS)

1988-01-01

In this data sheet the occurrence, ore processing, chemical and physical properties and the uses of beryllium and its alloys is presented. The hazards involved in the use of beryllium and its compounds in the laboratory are discussed with particular reference to its toxicity, carcinogenicity, handling, storage, disposal, fire prevention and the principal health hazards. Further reading is suggested. (UK)

Mechanisms of hydrogen retention in metallic beryllium and beryllium oxide and properties of ion-induced beryllium nitride; Rueckhaltemechanismen fuer Wasserstoff in metallischem Beryllium und Berylliumoxid sowie Eigenschaften von ioneninduziertem Berylliumnitrid

Energy Technology Data Exchange (ETDEWEB)

Oberkofler, Martin

2011-09-22

In the framework of this thesis laboratory experiments on atomically clean beryllium surfaces were performed. They aim at a basic understanding of the mechanisms occurring upon interaction of a fusion plasma with a beryllium first wall. The retention and the temperature dependent release of implanted deuterium ions are investigated. An atomistic description is developed through simulations and through the comparison with calculations based on density functional theory. The results of these investigations are compared to the behaviour of hydrogen upon implantation into thermally grown beryllium oxide layers. Furthermore, beryllium nitride is produced by implantation of nitrogen into metallic beryllium and its properties are investigated. The results are interpreted with regard to the use of beryllium in a fusion reactor. (orig.)

Extractive metallurgy of the beryllium

International Nuclear Information System (INIS)

Alonso, Neusa; Capocchi, Jose Deodoro Trani

1995-01-01

A bibliographic review is performed on the beryllium extractive metallurgy. The work describes the main type of ores and processes applied to the metallic beryllium production, beryllium oxide production using fluoride, sulfide and direct chlorination. The thermodynamic consideration are made on beryllium reduction processes, discussing the viability of the beryllium oxide and hallide reduction processes. Under the technological viewpoint, the Cu-Be alloys main production processes are discussed, and the main toxicity problems related with beryllium are mentioned

The JET divertor coil

International Nuclear Information System (INIS)

Last, J.R.; Froger, C.; Sborchia, C.

1989-01-01

The divertor coil is mounted inside the Jet vacuum vessel and is able to carry 1 MA turns. It is of conventional construction - water cooled copper, epoxy glass insulation -and is contained in a thin stainless steel case. The coil has to be assembled, insulated and encased inside the Jet vacuum vessel. A description of the coil is given, together with technical information (including mechanical effects on the vacuum vessel), an outline of the manufacture process and a time schedule. (author)

Technical Basis for PNNL Beryllium Inventory

Energy Technology Data Exchange (ETDEWEB)

Johnson, Michelle Lynn

2014-07-09

The Department of Energy (DOE) issued Title 10 of the Code of Federal Regulations Part 850, “Chronic Beryllium Disease Prevention Program” (the Beryllium Rule) in 1999 and required full compliance by no later than January 7, 2002. The Beryllium Rule requires the development of a baseline beryllium inventory of the locations of beryllium operations and other locations of potential beryllium contamination at DOE facilities. The baseline beryllium inventory is also required to identify workers exposed or potentially exposed to beryllium at those locations. Prior to DOE issuing 10 CFR 850, Pacific Northwest Nuclear Laboratory (PNNL) had documented the beryllium characterization and worker exposure potential for multiple facilities in compliance with DOE’s 1997 Notice 440.1, “Interim Chronic Beryllium Disease.” After DOE’s issuance of 10 CFR 850, PNNL developed an implementation plan to be compliant by 2002. In 2014, an internal self-assessment (ITS #E-00748) of PNNL’s Chronic Beryllium Disease Prevention Program (CBDPP) identified several deficiencies. One deficiency is that the technical basis for establishing the baseline beryllium inventory when the Beryllium Rule was implemented was either not documented or not retrievable. In addition, the beryllium inventory itself had not been adequately documented and maintained since PNNL established its own CBDPP, separate from Hanford Site’s program. This document reconstructs PNNL’s baseline beryllium inventory as it would have existed when it achieved compliance with the Beryllium Rule in 2001 and provides the technical basis for the baseline beryllium inventory.

Large coil program support structure conceptual design

International Nuclear Information System (INIS)

Litherland, P.S.

1977-01-01

The purpose of the Large Coil Program (LCP) is to perform tests on both pool boiling and force cooled superconducting toroidal field coils. The tests will attempt to approximate conditions anticipated in an ignition tokamak. The test requirements resulted in a coil support design which accommodates up to six (6) test coils and is mounted to a structure capable of resisting coil interactions. The steps leading to the present LCP coil support structure design, details on selected structural components, and the basic assembly sequence are discussed

NCSX Toroidal Field Coil Design

International Nuclear Information System (INIS)

Kalish M; Rushinski J; Myatt L; Brooks A; Dahlgren F; Chrzanowski J; Reiersen W; Freudenberg K.

2005-01-01

The National Compact Stellarator Experiment (NCSX) is an experimental device whose design and construction is underway at the Department of Energy's Princeton Plasma Physics Laboratory (PPPL). The primary coil systems for the NCSX device consist of the twisted plasma-shaping Modular Coils, the Poloidal Field Coils, and the Toroidal Field (TF) Coils. The TF Coils are D-shaped coils wound from hollow copper conductor, and vacuum impregnated with a glass-epoxy resin system. There are 18 identical, equally spaced TF coils providing 1/R field at the plasma. They operate within a cryostat, and are cooled by LN2, nominally, to 80K. Wedge shaped castings are assembled to the inboard face of these coils, so that inward radial loads are reacted via the nesting of each of the coils against their adjacent partners. This paper outlines the TF Coil design methodology, reviews the analysis results, and summarizes how the design and analysis support the design requirements

Spectrographic measurement of beryllium in the atmosphere; Dosage spectrographique du beryllium dans l'atmosphere

Energy Technology Data Exchange (ETDEWEB)

Artaud, J; Cittanova, J [Commissariat a l' Energie Atomique, Service d' Analyses et Recherches Chimiques Appliquees, Saclay (France). Centre d' Etudes Nucleaires; Crehange, G; Frequelin, S [Commissariat a l' Energie Atomique, Dir. des Applications Militaires, Service Chimie, Saclay (France). Centre d' Etudes Nucleaires; Baudin, G [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

1961-07-01

We describe here a method for the spectrographic determination of beryllium on filters which is valid for amounts varying between 0,01 and 30 {mu}g of beryllium and which is independent of the nature of the beryllium compound involved. This is a flux method (graphite-lithium carbonate mixture), the excitation being by a direct current arc. (author) [French] Nous decrivons ici, une methode de dosage spectrographique de beryllium sur filtre, valable pour des teneurs comprises entre 0,01 et 30 {mu}g de beryllium et independante de la nature du compose de beryllium a doser. C'est une methode de 'flux' (melange graphite-carbonate de lithium) l'excitation etant un arc a courant continu. (auteur)

Remote maintenance of tandem mirror hybrid coils

International Nuclear Information System (INIS)

Dietz, L.P.

1983-01-01

Hybrid Coils (superconducting coils with normal conducting inserts) are being employed with increasing frequency on Tandem Mirror Devices to obtain high field strengths. The normal conducting copper inserts are short lived in comparison to their encircling superconductors. It becomes desirable, therefore, to devise design features and maintenance procedures to replace the inner normal conducting coils without simultaneously replacing the longer lived (and significantly more costly) superconducting coils. The high neutron wall loadings require that the task be accomplished by remote control. The approach is to permanently mount the coil assemblies on track mounted carriages which serve, during machine operation merely as structural supports, but during maintenance procedures as moveable transport devices. The carriages incorporate all necessary provisions to facilitate remote maintenance operations and to adjust and align the coil assemblies with respect to adjacent machine components. The vacuum vessel is severed on both sides of the hybrid coil by means of a remote cutting machine. The entire coil is transported horizontally, normal to the machine axis to a nearby repair station. Prepositioned carriage mounted repair equipment at the repair station withdraws the damaged normal coil as a single entity and inserts a preassembled spare unit. The repaired hybrid coil is reassembled to the reactor. A cost and risk effective procedure has been evolved to maintain one of the more critical components of a Tandem Mirror Machine

COMPASS magnetic field coils and structure systems

International Nuclear Information System (INIS)

Crossland, R.T.; Booth, J.A.; Hayward, R.J.; Keogh, P.; Pratt, A.P.

1987-01-01

COMPASS is a new experimental toroidal assembly of compact design and with a wide range of physics objectives. It is required to operate either as a Tokamak or as a Reversed Field Pinch with interchangeable circular and dee-section vacuum vessels. The Toroidal field is produced by 16 rectangular coils of 4 turns with tapered conductors on the inside which nest together to form a vault to resist the centering forces. The coils are designed to produce a maximum field on axis of 2.1T which requires a current of 91 kA per turn. Two central solenoids and five pairs of coils symmetrically positioned above and below the machine equator provide the poloidal field. Both coil systems are supported form a mechanical support structure which surrounds the machine. This is primarily designed to resist out-of-plane forces on the TF coils but also acts as the base support for the PF coils and vacuum vessels. An illustration of the COMPASS Load Assembly is given and shows the D-shaped vacuum vessel, the major components and the various field windings

Risk of beryllium sensitization in a low-exposed former nuclear weapons cohort from the Cold War era.

Science.gov (United States)

Mikulski, Marek A; Leonard, Stephanie A; Sanderson, Wayne T; Hartley, Patrick G; Sprince, Nancy L; Fuortes, Laurence J

2011-03-01

The nuclear weapons industry has long been known as a source of beryllium exposure. A total of 1,004 former workers from a nuclear weapons assembly site in the Midwest were screened for sensitization to beryllium (BeS). The screenings were part of the Department of Energy (DOE) Former Worker Program established in 1996. Twenty-three (2.3%) workers were found sensitized to beryllium and this prevalence was comparable to other DOE sites. Occasional, direct exposure to beryllium through machining and grinding of copper-beryllium (Cu-Be) 2% alloy tools was found to increase the risk of sensitization compared to background exposure (OR = 3.83; 95% CI: 1.04-14.03) with a statistically significant trend (P = 0.03) revealing that particular jobs are associated with sensitization. Exposure potential in this study was estimated based on job titles and not personal exposure information. These results confirm the need to screen workers using beryllium alloy tools in other industries and for consideration of altering work practices. Copyright © 2010 Wiley-Liss, Inc.

Chronic Beryllium Disease

Science.gov (United States)

... who are exposed to beryllium will not experience health effects. Studies have shown that on average, 1 – 6 percent of exposed workers develop beryllium sensitization, although the rates can be ...

Defense programs beryllium good practice guide

Energy Technology Data Exchange (ETDEWEB)

Herr, M.

1997-07-01

Within the DOE, it has recently become apparent that some contractor employees who have worked (or are currently working) with and around beryllium have developed chronic beryllium disease (CBD), an occupational granulomatous lung disorder. Respiratory exposure to aerosolized beryllium, in susceptible individuals, causes an immunological reaction that can result in granulomatous scarring of the lung parenchyma, shortness of breath, cough, fatigue, weight loss, and, ultimately, respiratory failure. Beryllium disease was originally identified in the 1940s, largely in the fluorescent light industry. In 1950, the Atomic Energy Commission (AEC) introduced strict exposure standards that generally curtailed both the acute and chronic forms of the disease. Beginning in 1984, with the identification of a CBD case in a DOE contractor worker, there was increased scrutiny of both industrial hygiene practices and individuals in this workforce. To date, over 100 additional cases of beryllium-specific sensitization and/or CBD have been identified. Thus, a disease previously thought to be largely eliminated by the adoption of permissible exposure standards 45 years ago is still a health risk in certain workforces. This good practice guide forms the basis of an acceptable program for controlling workplace exposure to beryllium. It provides (1) Guidance for minimizing worker exposure to beryllium in Defense Programs facilities during all phases of beryllium-related work, including the decontamination and decommissioning (D&D) of facilities. (2) Recommended controls to be applied to the handling of metallic beryllium and beryllium alloys, beryllium oxide, and other beryllium compounds. (3) Recommendations for medical monitoring and surveillance of workers exposed (or potentially exposed) to beryllium, based on the best current understanding of beryllium disease and medical diagnostic tests available. (4) Site-specific safety procedures for all processes of beryllium that is likely to

Reflector-moderated critical assemblies

International Nuclear Information System (INIS)

Paxton, H.C.; Jarvis, G.A.; Byers, C.C.

1975-07-01

Experiments with reflector-moderated critical assemblies were part of the Rover Program at the Los Alamos Scientific Laboratory (LASL). These assemblies were characterized by thick D 2 O or beryllium reflectors surrounding large cavities that contained highly enriched uranium at low average densities. Because interest in this type of system has been revived by LASL Plasma Cavity Assembly studies, more detailed descriptions of the early assemblies than had been available in the unclassified literature are provided. (U.S.)

Defense programs beryllium good practice guide

International Nuclear Information System (INIS)

Herr, M.

1997-07-01

Within the DOE, it has recently become apparent that some contractor employees who have worked (or are currently working) with and around beryllium have developed chronic beryllium disease (CBD), an occupational granulomatous lung disorder. Respiratory exposure to aerosolized beryllium, in susceptible individuals, causes an immunological reaction that can result in granulomatous scarring of the lung parenchyma, shortness of breath, cough, fatigue, weight loss, and, ultimately, respiratory failure. Beryllium disease was originally identified in the 1940s, largely in the fluorescent light industry. In 1950, the Atomic Energy Commission (AEC) introduced strict exposure standards that generally curtailed both the acute and chronic forms of the disease. Beginning in 1984, with the identification of a CBD case in a DOE contractor worker, there was increased scrutiny of both industrial hygiene practices and individuals in this workforce. To date, over 100 additional cases of beryllium-specific sensitization and/or CBD have been identified. Thus, a disease previously thought to be largely eliminated by the adoption of permissible exposure standards 45 years ago is still a health risk in certain workforces. This good practice guide forms the basis of an acceptable program for controlling workplace exposure to beryllium. It provides (1) Guidance for minimizing worker exposure to beryllium in Defense Programs facilities during all phases of beryllium-related work, including the decontamination and decommissioning (D ampersand D) of facilities. (2) Recommended controls to be applied to the handling of metallic beryllium and beryllium alloys, beryllium oxide, and other beryllium compounds. (3) Recommendations for medical monitoring and surveillance of workers exposed (or potentially exposed) to beryllium, based on the best current understanding of beryllium disease and medical diagnostic tests available. (4) Site-specific safety procedures for all processes of beryllium that is

Thermomechanical testing of beryllium for the JET/ISX-B beryllium limiter experiment

International Nuclear Information System (INIS)

Watson, R.D.; Smith, M.F.; Whitley, J.B.; McDonald, J.M.

1984-01-01

Materials testing of S-65-B beryllium has been conducted in support of the beryllium limiter experiment on the ISX-B tokamak. The S-65-B grade of hot-pressed beryllium was chosen over S-200-E because of its superior strength and ductility at elevated temperatures. The testing has included measurement of tensile and yield strength, ductility, Young's Modulus, thermal conductivity, and specific heat from 50 0 C to 700 0 C. Thermal fatigue testing of a 2.5 cm beryllium cube was conducted using an electron beam to apply a heat flux of 2.5 kw/cm 2 for 0.3 second pulses for 1500 cycles. Results from the tests are compared to elastic-plastic finite element stress calculations. The testing indicates that the ISX-B beryllium limiter should survive the tokamak environment without serious structural failure, although some surface cracking is expected to occur. (author)

Beryllium allergy

International Nuclear Information System (INIS)

Schoenherr, S.; Pevny, I.

1989-12-01

Beryllium is not only a high potent allergen, but also a fotoallergen and can provoke contact allergic reactions, fotoallergic reactions, granulomatous skin reactions, pulmonary granulomatous diseases and sometimes even systemic diseases. The authors present 9 own cases of a patch test positive beryllium allergy, 7 patients with relevant allergy and 5 patients with an allergic contact stomatitis. (author)

Beryllium reflectors for research reactors. Review and preliminary finite element analysis

Energy Technology Data Exchange (ETDEWEB)

Bejarano, Pablo S; Cocco, Roxana G., E-mail: rcocco@invap.com.ar [INVAP S.E., Rio Negro (Argentina)

2012-03-15

Beryllium is used in numerous research reactors to moderate neutron energy and to reflect neutrons back into the core, thus intensifying the thermal neutron flux. However, beryllium is degraded by radiation damage, as a result of both displacement and transmutation. Displacement damage leads to point defect clustering, irradiation hardening and embrittlement. Transmutation produces helium, which results in high levels of gas and swelling, even at low temperatures. A brief state-of-the-art review on the use of reflector assemblies reveals that each user has adopted a different method for overcoming problems related to swelling: strengthening, cracking and distortion. In the present work a preliminary study about the geometry influence on the reflector assembly behavior was performed by a Finite Element Analysis (FEA). A simplified study was made varying its geometry in height, thickness and width. The results showed that the most influencing parameter in avoiding distortion due to swelling is firstly the reflector's assembly height, H; secondly its thickness, L, and lastly its angle/width, {theta}. These results contribute to the understanding of distortion behavior and the stresses generated in a simple geometry Be bar subjected to radiation, which can be a useful tool for mechanical design of more complex components. (author)

High temperature technological heat exchangers and steam generators with helical coil assembly tube bundle

International Nuclear Information System (INIS)

Korotaev, O.J.; Mizonov, N.V.; Nikolaevsky, V.B.; Nazarov, E.K.

1990-01-01

Analysis of thermal hydraulics characteristics of nuclear steam generators with different tube bundle arrangements and waste heat boilers for ammonia production units was performed on the basis of operating experience results and research and development data. The present report involves the obtained information. The estimations of steam generator performances and repair-ability are given. The significant temperature profile of the primary and secondary coolant flows are attributed to all steam generator designs. The intermediate mixing is found to be an effective means of temperature profile overcoming. At present the only means to provide an effective mixing in heat exchangers of the following types: straight tubes, field tubes, platen tubes and multibank helical coil tubes (with complicated bend distribution along their length) are section arrangements in series in conjunction with forced and natural mixing in connecting lines. Development of the unificated system from mini helical coil assemblies allows to design and manufacture heat exchangers and steam generators within the wide range of operating conditions without additional expenses on the research and development work

Measurements of beryllium sputtering yields at JET

Science.gov (United States)

Jet-Efda Contributors Stamp, M. F.; Krieger, K.; Brezinsek, S.

2011-08-01

The lifetime of the beryllium first wall in ITER will depend on erosion and redeposition processes. The physical sputtering yields for beryllium (both deuterium on beryllium (Be) and Be on Be) are of crucial importance since they drive the erosion process. Literature values of experimental sputtering yields show an order of magnitude variation so predictive modelling of ITER wall lifetimes has large uncertainty. We have reviewed the old beryllium yield experiments on JET and used current beryllium atomic data to produce revised beryllium sputtering yields. These experimental measurements have been compared with a simple physical sputtering model based on TRIM.SP beryllium yield data. Fair agreement is seen for beryllium yields from a clean beryllium limiter. However the yield on a beryllium divertor tile (with C/Be co-deposits) shows poor agreement at low electron temperatures indicating that the effect of the higher sputtering threshold for beryllium carbide is important.

Large superconducting coil fabrication development

International Nuclear Information System (INIS)

Brown, R.L.; Allred, E.L.; Anderson, W.C.; Burn, P.B.; Deaderick, R.I.; Henderson, G.M.; Marguerat, E.F.

1975-01-01

Toroidal fields for some fusion devices will be produced by an array of large superconducting coils. Their size, space limitation, and field requirements dictate that they be high performance coils. Once installed, accessibility for maintenance and repairs is severely restricted; therefore, good reliability is an obvious necessity. Sufficient coil fabrication will be undertaken to develop and test methods that are reliable, fast, and economical. Industrial participation will be encouraged from the outset to insure smooth transition from development phases to production phases. Initially, practice equipment for three meter bore circular coils will be developed. Oval shape coil forms will be included in the practice facility later. Equipment that is more automated will be developed with the expectation of winding faster and obtaining good coil quality. Alternate types of coil construction, methods of winding and insulating, will be investigated. Handling and assembly problems will be studied. All technology developed must be feasible for scaling up when much larger coils are needed. Experimental power reactors may need coils having six meter or larger bores

Beryllium R&D for blanket application

Science.gov (United States)

Donne, M. Dalle; Longhurst, G. R.; Kawamura, H.; Scaffidi-Argentina, F.

1998-10-01

The paper describes the main problems and the R&D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point.

Corrosion of beryllium oxide; Corrosion de l'oxyde de beryllium

Energy Technology Data Exchange (ETDEWEB)

Elston, J; Caillat, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1958-07-01

Data are reported on the volatilization rate of beryllium oxide in moist air depending on temperature and water vapour concentration. They are concerned with powder samples or sintered shapes of various densities. For sintered samples, the volatilization rate is very low under the following conditions: - temperature: 1300 deg. C, - water vapour concentration in moist air: 25 g/m{sup 3}, - flow rate: 12 I/hour corresponding to a speed of 40 m/hour on the surface of the sample. For calcinated powders (1300 deg. C), grain growth has been observed under a stream of moist air at 1100 deg. C. For instance, grain size changes from 0,5 to at least 2 microns after 500 hours of exposure at this temperature. Furthermore, results data are reported on corrosion of sintered beryllium oxide in pressurized water. At 250 deg. C, under a pressure of 40 kg/cm{sup 2} water is very slightly corrosive; however, internal strains are revealed. Finally, some features on the corrosion in liquid sodium are exposed. (author)Fren. [French] La volatilisation de l'oxyde de beryllium dans l'air humide est etudiee en fonction de la temperature pour differentes teneurs de vapeur d'eau. Les essais decrits portent sur de l'oxyde de beryllium en poudre ou sur des echantillons d'oxyde de beryllium fritte de differentes densites. Avec un debit d'air de 12 I/h contenant 25 g de vapeur par m{sup 3} correspondant a une vitesse de 40 m/h sur la surface de l'echantillon, la volatilisation des frittes a 1300 deg. C reste tres faible. Sur de la poudre d'oxyde de beryllium calcinee initialement a 1300 deg. C, on observe un grossissement de la taille des grains sous l'influence de l'air humide a 1100 deg. C. Par exemple, elle passe de 0,5 a au moins 2 microns apres 500 heures d'exposition a cette temperature. On donne d'autre part les resultats d'une etude de la corrosion de frittes d'oxyde de beryllium par l'eau, en autoclave. A 250 deg. C, sous une pression de 40 kg/cm{sup 2}, l'action de l'eau reste tres

Thermal effects on beryllium mirrors

International Nuclear Information System (INIS)

Weinswig, S.

1989-01-01

Beryllium is probably the most frequently used material for spaceborne system scan mirrors. Beryllium's properties include lightweightedness, high Young's modulus, high stiffness value, high resonance value. As an optical surface, beryllium is usually nickel plated in order to produce a higher quality surface. This process leads to the beryllium mirror acting like a bimetallic device. The mirror's deformation due to the bimetallic property can possibly degrade the performance of the associated optical system. As large space borne systems are designed and as temperature considerations become more crucial in the instruments, the concern about temporal deformation of the scan mirrors becomes a prime consideration. Therefore, two sets of tests have been conducted in order to ascertain the thermal effects on nickel plated beryllium mirrors. These tests are categorized. The purpose of this paper is to present the values of the bimetallic effect on typical nickel plated beryllium mirrors

SSC [Superconducting Super Collider] dipole coil production tooling

International Nuclear Information System (INIS)

Carson, J.A.; Barczak, E.J.; Bossert, R.C.; Brandt, J.S.; Smith, G.A.

1989-03-01

Superconducting Super Collider dipole coils must be produced to high precision to ensure uniform prestress and even conductor distribution within the collared coil assembly. Tooling is being prepared at Fermilab for the production of high precision 1M and 16.6M SSC dipole coils suitable for mass production. The design and construction methods builds on the Tevatron tooling and production experience. Details of the design and construction methods and measured coil uniformity of 1M coils will be presented. 4 refs., 10 figs

Sintering of beryllium oxide; Frittage de l'oxyde de beryllium

Energy Technology Data Exchange (ETDEWEB)

Caillat, R; Pointud, R [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1955-07-01

This study had for origin to find a process permitting to manufacture bricks of beryllium oxide of pure nuclear grade, with a density as elevated as possible and with standardized shape. The sintering under load was the technique kept for the manufacture of the bricks. Because of the important toxicity of the beryllium oxide, the general features for the preliminary study of the sintering, have been determined while using alumina. The obtained results will be able to act as general indication for ulterior studies with sintering under load. (M.B.) [French] Cette etude a eu pour origine la recherche d'un procede permettant de fabriquer industriellement des briques d'oxyde de beryllium nucleaireraent pures, de densite aussi elevee que possible et de forme standardisee. Le frittage sous charge fut la technique retenue pour la fabrication des briques. En raison de la grande toxicite de l'oxyde de beryllium, les caracteristiques generales du frittage, pour l'etude preliminaire, ont ete determine en utilisant de l'alumine. Les resultats obtenus pourront servir d'indication generale pour des etudes ulterieurs avec frittage sous charge. (M.B.)

Fracture toughness of irradiated beryllium

International Nuclear Information System (INIS)

Beeston, J.M.

1978-01-01

The fracture toughness of nuclear grade hot-pressed beryllium upon irradiation to fluences of 3.5 to 5.0 x 10 21 n/cm 2 , E greater than 1 MeV, was determined. Procedures and data relating to a round-robin test contributing to a standard ASTM method for unirradiated beryllium are discussed in connection with the testing of irradiated specimens. A porous grade of beryllium was also irradiated and tested, thereby enabling some discrimination between the models for describing the fracture toughness behavior of porous beryllium. The fracture toughness of unirradiated 2 percent BeO nuclear grade beryllium was 12.0 MPa m/sup 1 / 2 /, which was reduced 60 percent upon irradiation at 339 K and testing at 295 K. The fracture toughness of a porous grade of beryllium was 13.1 MPa m/sup 1 / 2 /, which was reduced 68 percent upon irradiation and testing at the same conditions. Reasons for the reduction in fracture toughness upon irradiation are discussed

Assembly of the PLT device

International Nuclear Information System (INIS)

Marino, R.

1975-11-01

The assembly of the PLT device began in June 1974 with a preassembly of the mechanical structure at a remote site. The preassembly sequence incorporated final fabrication procedures with an initial staging operation. This successful staging/fabrication procedure proved to be an invaluable asset when the final assembly was started in August 1974. The assembly continued with the initial reassembly of the previously tested structural components at the final machine site. Construction was interrupted at several points to allow for toroidal field coil, vacuum vessel, and poloidal coil installation. Two phases of toroidal field coil power tests were included in the assembly sequence prior to, and just after the vacuum vessel insertion

Beryllium-stimulated neopterin as a diagnostic adjunct in chronic beryllium disease.

Science.gov (United States)

Maier, Lisa A; Kittle, Lori A; Mroz, Margaret M; Newman, Lee S

2003-06-01

The diagnosis of chronic beryllium disease (CBD) relies on the beryllium lymphocyte proliferation test (BeLPT) to demonstrate a Be specific immune response. This test has improved early diagnosis, but cannot discriminate beryllium sensitization (BeS) from CBD. We previously found high neopterin levels in CBD patients' serum and questioned whether Be-stimulated neopterin production by peripheral blood cells in vitro might be useful in the diagnosis of CBD. CBD, BeS, Be exposed workers without disease (Be-exp) normal controls and sarcoidosis subjects were enrolled. Peripheral blood mononuclear cells (PBMN) were cultured in the presence and absence of beryllium sulfate. Neopterin levels were determined from cell supernatants by enzyme linked immunosorbent assay (ELISA). Clinical evaluation of CBD subjects included chest radiography, pulmonary function testing, exercise testing, and the BeLPT. CBD patients produced higher levels of neopterin in both unstimulated and Be-stimulated conditions compared to all other subjects (P workplace screening. Copyright 2003 Wiley-Liss, Inc.

OVERVIEW OF BERYLLIUM SAMPLING AND ANALYSIS

Energy Technology Data Exchange (ETDEWEB)

Brisson, M

2009-04-01

Because of its unique properties as a lightweight metal with high tensile strength, beryllium is widely used in applications including cell phones, golf clubs, aerospace, and nuclear weapons. Beryllium is also encountered in industries such as aluminium manufacturing, and in environmental remediation projects. Workplace exposure to beryllium particulates is a growing concern, as exposure to minute quantities of anthropogenic forms of beryllium may lead to sensitization and to chronic beryllium disease, which can be fatal and for which no cure is currently known. Furthermore, there is no known exposure-response relationship with which to establish a 'safe' maximum level of beryllium exposure. As a result, the current trend is toward ever lower occupational exposure limits, which in turn make exposure assessment, both in terms of sampling and analysis, more challenging. The problems are exacerbated by difficulties in sample preparation for refractory forms of beryllium, such as beryllium oxide, and by indications that some beryllium forms may be more toxic than others. This chapter provides an overview of sources and uses of beryllium, health risks, and occupational exposure limits. It also provides a general overview of sampling, analysis, and data evaluation issues that will be explored in greater depth in the remaining chapters. The goal of this book is to provide a comprehensive resource to aid personnel in a wide variety of disciplines in selecting sampling and analysis methods that will facilitate informed decision-making in workplace and environmental settings.

Toxicokinetics of beryllium following inhalation of beryllium oxide by Beagle dogs. III

International Nuclear Information System (INIS)

Finch, G.L.; Haley, P.J.; Hoover, M.D.; Mewhinney, J.A.; Bice, D.E.; Eidson, A.F.

1988-01-01

Young adult Beagle dogs inhaled radiolabeled beryllium oxide aerosols ( 7 BeO) prepared at either 500 deg. or 1000 deg. C to achieve one of two initial lung burdens (ILBs) of BeO. After exposure, animals were monitored by whole body counting for 7 Be, and excreta, clinical, and radiographic data were collected. One group of dogs was assigned for serial sacrifice for quantitation of beryllium clearance from lung, translocation to other organs, and histopathologic analysis of lung and lymph nodes. A second group of dogs was subjected to periodic bronchopulmonary lavage for analysis of lymphocyte responsiveness to beryllium. These latter dogs were subsequently re-exposed to the high ILB level of BeO prepared t 500 deg. C. ILBs following the second exposure were higher than that after the first exposure (74 vs. 42 μg BeO/kg, respectively). Except for one dog that exhibited enhanced beryllium retention after the second exposure, patterns of whole body clearance were similar to those observed after the initial exposures to the 500 deg. C-BeO. Analysis of lymphocyte responsiveness to beryllium in the second group of dogs is continuing. (author)

Toxicokinetics of beryllium following inhalation of beryllium oxide by Beagle dogs. III

Energy Technology Data Exchange (ETDEWEB)

Finch, G L; Haley, P J; Hoover, M D; Mewhinney, J A; Bice, D E; Eidson, A F

1988-12-01

Young adult Beagle dogs inhaled radiolabeled beryllium oxide aerosols ({sup 7}BeO) prepared at either 500 deg. or 1000 deg. C to achieve one of two initial lung burdens (ILBs) of BeO. After exposure, animals were monitored by whole body counting for {sup 7}Be, and excreta, clinical, and radiographic data were collected. One group of dogs was assigned for serial sacrifice for quantitation of beryllium clearance from lung, translocation to other organs, and histopathologic analysis of lung and lymph nodes. A second group of dogs was subjected to periodic bronchopulmonary lavage for analysis of lymphocyte responsiveness to beryllium. These latter dogs were subsequently re-exposed to the high ILB level of BeO prepared t 500 deg. C. ILBs following the second exposure were higher than that after the first exposure (74 vs. 42 {mu}g BeO/kg, respectively). Except for one dog that exhibited enhanced beryllium retention after the second exposure, patterns of whole body clearance were similar to those observed after the initial exposures to the 500 deg. C-BeO. Analysis of lymphocyte responsiveness to beryllium in the second group of dogs is continuing. (author)

Optimization of beryllium for fusion blanket applications

International Nuclear Information System (INIS)

Billone, M.C.

1993-01-01

The primary function of beryllium in a fusion reactor blanket is neutron multiplication to enhance tritium breeding. However, because heat, tritium and helium will be generated in and/or transported through beryllium and because the beryllium is in contact with other blanket materials, the thermal, mechanical, tritium/helium and compatibility properties of beryllium are important in blanket design. In particular, tritium retention during normal operation and release during overheating events are safety concerns. Accommodating beryllium thermal expansion and helium-induced swelling are important issues in ensuring adequate lifetime of the structural components adjacent to the beryllium. Likewise, chemical/metallurgical interactions between beryllium and structural components need to be considered in lifetime analysis. Under accident conditions the chemical interaction between beryllium and coolant and breeding materials may also become important. The performance of beryllium in fusion blanket applications depends on fabrication variables and operational parameters. First the properties database is reviewed to determine the state of knowledge of beryllium performance as a function of these variables. Several design calculations are then performed to indicate ranges of fabrication and operation variables that lead to optimum beryllium performance. Finally, areas for database expansion and improvement are highlighted based on the properties survey and the design sensitivity studies

Reactivity test between beryllium and copper

International Nuclear Information System (INIS)

Kawamura, H.; Kato, M.

1995-01-01

Beryllium has been expected for using as plasma facing material on ITER. And, copper alloy has been proposed as heat sink material behind plasma facing components. Therefore, both materials must be joined. However, the elementary process of reaction between beryllium and copper alloy does not clear in detail. For example, other authors reported that beryllium reacted with copper at high temperature, but it was not obvious about the generation of reaction products and increasing of the reaction layer. In the present work, from this point, for clarifying the elementary process of reaction between beryllium and copper, the out-of-pile compatibility tests were conducted with diffusion couples of beryllium and copper which were inserted in the capsule filled with high purity helium gas (6N). Annealing temperatures were 300, 400, 500, 600 and 700 degrees C, and annealing periods were 100, 300 and 1000h. Beryllium specimens were hot pressed beryllium, and copper specimens were OFC (Oxygen Free Copper)

Method for fabricating beryllium structures

Science.gov (United States)

Hovis, Jr., Victor M.; Northcutt, Jr., Walter G.

1977-01-01

Thin-walled beryllium structures are prepared by plasma spraying a mixture of beryllium powder and about 2500 to 4000 ppm silicon powder onto a suitable substrate, removing the plasma-sprayed body from the substrate and placing it in a sizing die having a coefficient of thermal expansion similar to that of the beryllium, exposing the plasma-sprayed body to a moist atmosphere, outgassing the plasma-sprayed body, and then sintering the plasma-sprayed body in an inert atmosphere to form a dense, low-porosity beryllium structure of the desired thin-wall configuration. The addition of the silicon and the exposure of the plasma-sprayed body to the moist atmosphere greatly facilitate the preparation of the beryllium structure while minimizing the heretofore deleterious problems due to grain growth and grain orientation.

Beryllium technology workshop, Clearwater Beach, Florida, November 20, 1991

International Nuclear Information System (INIS)

Longhurst, G.R.

1991-12-01

This report discusses the following topics: beryllium in the ITER blanket; mechanical testing of irradiated beryllium; tritium release measurements on irradiated beryllium; beryllium needs for plasma-facing components; thermal conductivity of plasma sprayed beryllium; beryllium research at the INEL; Japanese beryllium research activities for in-pile mockup tests on ITER; a study of beryllium bonding of copper alloy; new production technologies; thermophysical properties of a new ingot metallurgy beryllium product line; implications of beryllium:steam interactions in fusion reactors; and a test program for irradiation embrittlement of beryllium at JET

Beryllium technology workshop, Clearwater Beach, Florida, November 20, 1991

Energy Technology Data Exchange (ETDEWEB)

Longhurst, G.R.

1991-12-01

This report discusses the following topics: beryllium in the ITER blanket; mechanical testing of irradiated beryllium; tritium release measurements on irradiated beryllium; beryllium needs for plasma-facing components; thermal conductivity of plasma sprayed beryllium; beryllium research at the INEL; Japanese beryllium research activities for in-pile mockup tests on ITER; a study of beryllium bonding of copper alloy; new production technologies; thermophysical properties of a new ingot metallurgy beryllium product line; implications of beryllium:steam interactions in fusion reactors; and a test program for irradiation embrittlement of beryllium at JET.

Inhalation hazards from machining beryllium metal

International Nuclear Information System (INIS)

Hoover, M.D.; Finch, G.L.; Mewhinney, J.A.; Eidson, A.F.

1987-01-01

Beryllium metal has special nuclear and structural properties that make it useful for applications in fission and fusion reactor designs. Unfortunately, concerns for its toxicity have made designers wary of using beryllium metal. The work being reported here was undertaken to characterize the aerosols produced by two very common operations performed during preparation or modification of components for use in reactor systems: sawing and milling of beryllium metal. The study also covered beryllium metal alloys to allow comparison. Information from this study is to enable better assessments of the risk of using beryllium metal in reactor designs

Proposals for cold testing of the ITER TF coils

International Nuclear Information System (INIS)

Libeyre, P.; Ciazynski, D.; Dolgetta, N.; Duchateau, J.L.; Lyraud, C.; Kircher, F.; Schild, T.; Fietz, W.H.; Zahn, G.

2005-01-01

The ITER Toroidal Field (TF) magnet system will be made of 18 coils using Nb 3 Sn as superconducting material. These coils will operate at a maximum field of 11.8 T for a nominal current of 68 kA carried by a dual channel cable-in-conduit conductor cooled by a forced flow of supercritical helium at 4.5 K. In each coil, seven 760 m conductor lengths wound in double pancakes will be connected to each other by low resistance joints. As a final step of the reception tests, it is proposed to perform cold tests of these coils at liquid helium temperature after completion of their manufacture. The testing shall include high voltage tests to check the quality of the insulation, leak tests and pressure drop measurements of the hydraulic circuits as well as measurement of the joint resistances. Testing the coils up to nominal current is a discussed option, addressing on one hand measurement of the electrical performances in self field and on the other hand the mechanical behaviour of the coils. To perform these tests, a dedicated test facility has to be built, allowing possible simultaneous testing of two coils, assembled together in a twin coil configuration, similarly to their assembly in the torus. (authors)

Proposals for cold testing of the ITER TF coils

Energy Technology Data Exchange (ETDEWEB)

Libeyre, P.; Ciazynski, D.; Dolgetta, N.; Duchateau, J.L.; Lyraud, C. [Association Euratom/CEA Cadarache, Dept. de Recherches sur la Fusion Controlee (DRFC), 13 - Saint-Paul-lez-Durance (France); Kircher, F.; Schild, T. [CEA Saclay, Dept. d' Astrophysique, de Physique des Particules, de Physique Nucleaire et de l' Instrumentation Associee, 91- Gif sur Yvette (France); Fietz, W.H.; Zahn, G. [Association Euratom-Forschungszentrum Karlsruhe, Karlsruhe (Germany)

2005-07-01

The ITER Toroidal Field (TF) magnet system will be made of 18 coils using Nb{sub 3}Sn as superconducting material. These coils will operate at a maximum field of 11.8 T for a nominal current of 68 kA carried by a dual channel cable-in-conduit conductor cooled by a forced flow of supercritical helium at 4.5 K. In each coil, seven 760 m conductor lengths wound in double pancakes will be connected to each other by low resistance joints. As a final step of the reception tests, it is proposed to perform cold tests of these coils at liquid helium temperature after completion of their manufacture. The testing shall include high voltage tests to check the quality of the insulation, leak tests and pressure drop measurements of the hydraulic circuits as well as measurement of the joint resistances. Testing the coils up to nominal current is a discussed option, addressing on one hand measurement of the electrical performances in self field and on the other hand the mechanical behaviour of the coils. To perform these tests, a dedicated test facility has to be built, allowing possible simultaneous testing of two coils, assembled together in a twin coil configuration, similarly to their assembly in the torus. (authors)

Safe waste management practices in beryllium facilities

International Nuclear Information System (INIS)

Bhat, P.N.; Soundararajan, S.; Sharma, D.N.

2012-01-01

Beryllium, an element with the atomic symbol Be, atomic number 4, has very high stiffness to weight ratio and low density. It has good electrical conductive properties with low coefficient of thermal expansion. These properties make the metal beryllium very useful in varied technological endeavours, However, beryllium is recognised as one of the most toxic metals. Revelation of toxic effects of beryllium resulted in institution of stringent health and safety practices in beryllium handling facilities. The waste generated in such facilities may contain traces of beryllium. Any such waste should be treated as toxic waste and suitable safe waste management practices should be adopted. By instituting appropriate waste management practice and through a meticulously incorporated safety measures and continuous surveillance exercised in such facilities, total safety can be ensured. This paper broadly discusses health hazards posed by beryllium and safe methods of management of beryllium bearing wastes. (author)

Beryllium R and D for blanket application

Energy Technology Data Exchange (ETDEWEB)

Dalle Donne, M.; Scaffidi-Argentina, F. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reaktortechnik; Longhurst, G.R. [Idaho National Engineering Lab., Idaho Falls (United States); Kawamura, H. [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment

1998-10-01

The paper describes the main problems and the R and D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point. (orig.) 29 refs.

Beryllium R and D for blanket application

International Nuclear Information System (INIS)

Dalle Donne, M.; Scaffidi-Argentina, F.; Kawamura, H.

1998-01-01

The paper describes the main problems and the R and D for the beryllium to be used as neutron multiplier in blankets. As the four ITER partners propose to use beryllium in the form of pebbles for their DEMO relevant blankets (only the Russians consider the porous beryllium option as an alternative) and the ITER breeding blanket will use beryllium pebbles as well, the paper is mainly based on beryllium pebbles. Also the work on the chemical reactivity of fully dense and porous beryllium in contact with water steam is described, due to the safety importance of this point. (orig.)

(Beryllium). Internal Report No. 137, Jan. 15, 1958

International Nuclear Information System (INIS)

Mouret, P.; Rigaud, A.

1959-01-01

After a brief summary of the physical and chemical properties of beryllium, the various chemical treatments which can be applied to beryllium minerals either directly or after a physical enrichment are discussed. These various treatments give either the hydroxide or beryllium salts, from which either beryllium oxide or metallic beryllium can easily be obtained. The purification, analysis and uses of beryllium are also briefly discussed. (author)

Fabrication of the KSTAR toroidal field coil structure

International Nuclear Information System (INIS)

Choi, C.H.; Sa, J.W.; Park, H.K.; Hong, K.H.; Shin, H.; Kim, H.T.; Bak, J.S.; Lee, G.S.; Kwak, J.H.; Moon, H.G.; Yoon, H.H.; Lee, J.W.; Lee, S.K.; Song, J.Y.; Nam, K.M.; Byun, S.E.; Kim, H.C.; Ha, E.T.; Ahn, H.J.; Kim, D.S.; Lee, J.S.; Park, K.H.; Hong, C.D.

2005-01-01

The KSTAR toroidal field (TF) coil structure is under fabrication upon completion of engineering design and prototype construction. The prototype TF coil structure has been fabricated within allowable tolerances. Encasing of the prototype TF coil (TF00) in the prototype structure has been carried out through major processes involving a coil encasing, an enclosing weld, a vacuum pressure impregnation, and an outer surface machining. During the enclosing weld of the TF00 coil structure, we have measured temperatures and stresses on the coil surface. Assembly test had been performed with the TF00 coil structure. We have chosen Type 316LN as material of the TF coil structure. We used the narrow-gap TIG welding method. Doosan Heavy Industries and Construction Company (DHI) will complete the fabrication of the TF coil structure in Feb. 2006. (author)

Study beryllium microplastic deformation

International Nuclear Information System (INIS)

Papirov, I.I.; Ivantsov, V.I.; Nikolaenko, A.A.; Shokurov, V.S.; Tuzov, Yu.V.

2015-01-01

Microplastic flow characteristics systematically studied for different varieties beryllium. In isostatically pressed beryllium it decreased with increasing particle size of the powder, increasing temperature and increasing the pressing metal purity. High initial values of the limit microelasticity and microflow in some cases are due a high level of internal stresses of thermal origin and over time it can relax slowly. During long-term storage of beryllium materials with high initial resistance values microplastic deformation microflow limit and microflow stress markedly reduced, due mainly to the relaxation of thermal microstrain

Preparation of beryllium hydride

International Nuclear Information System (INIS)

Lowrance, B.R.

1975-01-01

A process is described for the preparation of beryllium hydride which comprises pyrolyzing, while in solution in a solvent inert under the reaction conditions, with respect to reactants and products and at a temperature in the range of about 100 0 to about 200 0 C, sufficient to result in the formation of beryllium hydride, a di-t-alkyl beryllium etherate wherein each tertiary alkyl radical contains from 4 to 20 carbon atoms. The pyrolysis is carried out under an atmosphere inert under the reaction conditions, with respect to reactants and products. (U.S.)

MRI surface-coil pair with strong inductive coupling.

Science.gov (United States)

Mett, Richard R; Sidabras, Jason W; Hyde, James S

2016-12-01

A novel inductively coupled coil pair was used to obtain magnetic resonance phantom images. Rationale for using such a structure is described in R. R. Mett et al. [Rev. Sci. Instrum. 87, 084703 (2016)]. The original rationale was to increase the Q-value of a small diameter surface coil in order to achieve dominant loading by the sample. A significant improvement in the vector reception field (VRF) is also seen. The coil assembly consists of a 3-turn 10 mm tall meta-metallic self-resonant spiral (SRS) of inner diameter 10.4 mm and outer diameter 15.1 mm and a single-loop equalization coil of 25 mm diameter and 2 mm tall. The low-frequency parallel mode was used in which the rf currents on each coil produce magnetic fields that add constructively. The SRS coil assembly was fabricated and data were collected using a tissue-equivalent 30% polyacrylamide phantom. The large inductive coupling of the coils produces phase-coherency of the rf currents and magnetic fields. Finite-element simulations indicate that the VRF of the coil pair is about 4.4 times larger than for a single-loop coil of 15 mm diameter. The mutual coupling between coils influences the current ratio between the coils, which in turn influences the VRF and the signal-to-noise ratio (SNR). Data on a tissue-equivalent phantom at 9.4 T show a total SNR increase of 8.8 over the 15 mm loop averaged over a 25 mm depth and diameter. The experimental results are shown to be consistent with the magnetic resonance theory of the emf induced by spins in a coil, the theory of inductively coupled resonant circuits, and the superposition principle. The methods are general for magnetic resonance and other types of signal detection and can be used over a wide range of operating frequencies.

Magnetic field alignment of coil-coil diblock copolymers and blends via intrinsic chain anisotropy

Science.gov (United States)

Rokhlenko, Yekaterina; Majewski, Pawel; Larson, Steven; Yager, Kevin; Gopalan, Padma; Avgeropoulos, Apostolos; Chan, Edwin; Osuji, Chinedum

Magnetic fields can control alignment of self-assembled soft materials such as block copolymers provided there is a suitably large magnetic susceptibility anisotropy present in the system. Recent results have highlighted the existence of a non-trivial intrinsic anisotropy in coil-coil diblock copolymers, specifically in lamellar-forming PS-b-P4VP, which enables alignment at field strengths of a few tesla in systems lacking mesogenic components. Alignment is predicated on correlation in the orientation of end-end vectors implied by the localization of block junctions at the microdomain interface and is observed on cooling across the order-disorder transition in the presence of the field. For appropriate combinations of field strength and grain size, we can leverage intrinsic chain anisotropy to magnetically direct self-assembly of many non-mesogenic systems, including other coil-coil BCPs like PS-b-PDMS and PS-b-PMMA, blends of BCPs of disparate morphologies and MWs, and blends of BCPs with homopolymers. This is noteworthy as blends of PS-b-P4VP with PEO provide a route to form functional materials such as nanoporous films by dissolution of PEO, or aligned ion conduction materials. We survey these various systems using TEM and in-situ X-ray scattering to study the phase behavior and temperature-, time- and field- dependent dynamics of alignment.

From micelles to fibers: balancing self-assembling and random coiling domains in pH-responsive silk-collagen-like protein-based polymers

NARCIS (Netherlands)

Beun, L.H.; Storm, I.M.; Werten, M.W.T.; Wolf, de F.A.; Cohen Stuart, M.A.; Vries, de R.J.

2014-01-01

We study the self-assembly of genetically engineered protein-based triblock copolymers consisting of a central pH-responsive silk-like middle block (SHn, where SH is a silk-like octapeptide, (GA)3GH and n is the number of repeats) flanked by hydrophilic random coil outer blocks (C2). Our previous

Preparation of beryllium hydride

International Nuclear Information System (INIS)

Roberts, C.B.

1975-01-01

A process is described for preparing beryllium hydride by the direct reaction of beryllium borohydride and aluminum hydride trimethylamine adduct. Volatile by-products and unreacted reactants are readily removed from the product mass by sublimation and/or evaporation. (U.S.)

Modular coil design developments for the National Compact Stellarator Experiment (NCSX)

International Nuclear Information System (INIS)

Williamson, D.; Brooks, A.; Brown, T.; Chrzanowski, J.; Cole, M.; Fan, H.-M.; Freudenberg, K.; Fogarty, P.; Hargrove, T.; Heitzenroeder, P.; Lovett, G.; Miller, P.; Myatt, R.; Nelson, B.; Reiersen, W.; Strickler, D.

2005-01-01

The National Compact Stellarator Experiment (NCSX) is a quasi-axisymmetric facility that combines the high beta and good confinement features of an advanced tokamak with the low current, disruption-free characteristics of a stellarator. The experiment is based on a three field-period plasma configuration with an average major radius of 1.4 m, a minor radius of 0.3 m, and a toroidal magnetic field on axis of up to 2 T. The modular coils are one set in a complex assembly of four coil systems that surround the highly shaped plasma. There are six, each of three coil types in the assembly for a total of 18 modular coils. The coils are constructed by winding copper cable onto a cast stainless steel winding form that has been machined to high accuracy, so that the current center of the winding pack is within ±1.5 mm of its theoretical position. The modular coils operate at a temperature of 80 K and are subjected to rapid heating and stress during a pulse. At this time, the project has completed construction of several prototype components which validate the fabrication and inspection processes that are planned for the production coils. In addition, some advanced techniques for error-field compensation and assembly simulation using computer-aided design (CAD) have been developed

The INEL beryllium multiplication experiment

International Nuclear Information System (INIS)

Smith, J.R.; King, J.J.

1991-03-01

The experiment to measure the multiplication of 14-MeV neutrons in bulk beryllium has been completed. The experiment consists of determining the ratio of 56 Mn activities induced in a large manganese bath by a central 14-MeV neutron source, with and without a beryllium sample surrounding the source. In the manganese bath method a neutron source is placed at the center of a totally-absorbing aqueous solution of MnSo 4 . The capture of neutrons by Mn produces a 56 Mn activity proportional to the emission rate of the source. As applied to the measurement of the multiplication of 14- MeV neutrons in bulk beryllium, the neutron source is a tritium target placed at the end of the drift tube of a small deuteron accelerator. Surrounding the source is a sample chamber. When the sample chamber is empty, the neutrons go directly to the surrounding MnSO 4 solution, and produce a 56 Mn activity proportional to the neutron emission rate. When the chamber contains a beryllium sample, the neutrons first enter the beryllium and multiply through the (n,2n) process. Neutrons escaping from the beryllium enter the bath and produce a 56 Mn activity proportional to the neutron emission rate multiplied by the effective value of the multiplication in bulk beryllium. The ratio of the activities with and without the sample present is proportional to the multiplication value. Detailed calculations of the multiplication and all the systematic effects were made with the Monte Carlo program MCNP, utilizing both the Young and Stewart and the ENDF/B-VI evaluations for beryllium. Both data sets produce multiplication values that are in excellent agreement with the measurements for both raw and corrected values of the multiplication. We conclude that there is not real discrepancy between experimental and calculated values for the multiplication of neutrons in bulk beryllium. 12 figs., 11 tabs., 18 refs

Beryllium minerals - demand strong for miniaturisation

International Nuclear Information System (INIS)

Griffiths, J.

1985-01-01

Beryllium is an essential constituent of over 40 minerals of which two are exploited commercially. Beryl is largely produced in the USSR and China and bertrandite in the U.S.A. Phenacite, from Canada, is also under investigation. The largest extraction plant for the recovery of beryllium in the western world is in Utah, U.S.A. and the company also produces beryllium oxide used in the manufacture of ceramics widely used in the electronics industry and for refractory articles. Beryllium-copper alloys in strip, rod and tube form are produced in the U.S.A., Germany and the U.K. Beryllium ceramics are important because of their high thermal conductivity, electrical insulation, strength and rigidity. The alloys, used as electric connectors, microswitch contacts are important for their high suitability for miniaturisation. The future growth potential for the beryllium industry is in the automotive industries in Europe and Japan. (U.K.)

Invited review the coiled coil silk of bees, ants, and hornets.

Science.gov (United States)

Sutherland, Tara D; Weisman, Sarah; Walker, Andrew A; Mudie, Stephen T

2012-06-01

In this article, we review current knowledge about the silk produced by the larvae of bees, ants, and hornets [Apoidea and Vespoidea: Hymenoptera]. Different species use the silk either alone or in composites for a variety of purposes including mechanical reinforcement, thermal regulation, or humidification. The characteristic molecular structure of this silk is α-helical proteins assembled into tetrameric coiled coils. Gene sequences from seven species are available, and each species possesses a copy of each of four related silk genes that encode proteins predicted to form coiled coils. The proteins are ordered at multiple length scales within the labial gland of the final larval instar before spinning. The insects control the morphology of the silk during spinning to produce either fibers or sheets. The silk proteins are small and non repetitive and have been produced artificially at high levels by fermentation in E. coli. The artificial silk proteins can be fabricated into materials with structural and mechanical properties similar to those of native silks. Copyright © 2011 Wiley Periodicals, Inc.

Manufacture of the poloidal field conductor insert coil (PFCI)

Energy Technology Data Exchange (ETDEWEB)

Baker, W. [EFDA CSU Garching, Boltzmannstrasse 2, 85748 Garching bei Muenchen (Germany); Keefe, C. [Tesla Engineering, Storrington, Sussex (United Kingdom); Rajainmaeki, H. [EFDA CSU Garching, Boltzmannstrasse 2, 85748 Garching bei Muenchen (Germany)], E-mail: hannu.rajainmaki@tech.efda.org; Salpietro, E. [EFDA CSU Garching, Boltzmannstrasse 2, 85748 Garching bei Muenchen (Germany)

2007-10-15

Within the framework of the R and D programme for international thermonuclear experimental reactor (ITER) the European team European Fusion Development Agreement (EFDA) has been charged with the design and manufacture of the poloidal field conductor insert coil (PFCI). The purpose of the PFCI is to test and demonstrate the performance of long-length full-scale NbTi conductors in ITER-relevant conditions. The PFCI will be tested in the central solenoid model coil test facility at the JAEA, Naka, Japan. This paper details the complete manufacturing of the PFCI including development, forming machining, pre-assembly, impregnation, final assembly and testing. The PFCI is a single-layered wound solenoid of nine turns with a transition joggle in the centre section of the winding and an intermediate joint connection between the upper termination and the main coil winding. To give the required overall dimensions to fit in the testing facility, preformed and machined glass resin composite filler pieces are assembled with the winding and is finally vacuum pressure impregnated (VPI) to create a single assembly unit. The PFCI is enclosed for assembly in a support structure, which consists of an upper and lower flange, each made up of four electrically insulated machined stainless steel castings, and 12 tie rods preloading the complete assembly in the vertical direction. The upper flange is equipped with four radial restraining jacks and the lower flange is equipped with four sets of studs and shear keys to withstand the net vertical and lateral electromagnetic forces. The PFCI is equipped with inductive heaters, voltage taps, temperature transducers, strain gauges and other instrumentation as diagnostics to monitor the performance. The current status of the manufacture is that the coil has passed the final acceptance tests and it is in the support structure assembly stage.

Beryllium. Its minerals. Pt. 1

International Nuclear Information System (INIS)

Lires, O.A.; Delfino, C.A.; Botbol, J.

1990-01-01

With this work a series of reports begins, under the generic name 'Beryllium', related to several aspects of beryllium technology. The target is to update, with critical sense, current bibliographic material in order to be used in further applications. Some of the most important beryllium ores, the Argentine emplacement of their deposits and world occurrence are described. Argentine and world production, resources and reserves are indicated here as well. (Author) [es

Method for hot pressing beryllium oxide articles

Science.gov (United States)

Ballard, Ambrose H.; Godfrey, Jr., Thomas G.; Mowery, Erb H.

1988-01-01

The hot pressing of beryllium oxide powder into high density compacts with little or no density gradients is achieved by employing a homogeneous blend of beryllium oxide powder with a lithium oxide sintering agent. The lithium oxide sintering agent is uniformly dispersed throughout the beryllium oxide powder by mixing lithium hydroxide in an aqueous solution with beryllium oxide powder. The lithium hydroxide is converted in situ to lithium carbonate by contacting or flooding the beryllium oxide-lithium hydroxide blend with a stream of carbon dioxide. The lithium carbonate is converted to lithium oxide while remaining fixed to the beryllium oxide particles during the hot pressing step to assure uniform density throughout the compact.

Belgian research on fusion beryllium waste

International Nuclear Information System (INIS)

Druyts, F.; Mallants, D.; Sillen, X.; Iseghem, P. Van

2004-01-01

Future fusion power plants will generate important quantities of neutron irradiated beryllium. Although recycling is the preferred management option for this waste, this may not be technically feasible for all of the beryllium, because of its radiological characteristics. Therefore, at SCK·CEN, we initiated a research programme aimed at studying aspects of the disposal of fusion beryllium, including waste characterisation, waste acceptance criteria, conditioning methods, and performance assessment. One of the main issues to be resolved is the development of fusion-specific waste acceptance criteria for surface or deep geological disposal, in particular with regard to the tritium content. In case disposal is the only solution, critical nuclides can be immobilised by conditioning the waste. As a first approach to immobilising beryllium waste, we investigated the vitrification of beryllium. Corrosion tests were performed on both metallic and vitrified beryllium to provide source data for performance assessment. Finally, a first step in performance assessment was undertaken. (author)

Potential exposures and risks from beryllium-containing products.

Science.gov (United States)

Willis, Henry H; Florig, H Keith

2002-10-01

Beryllium is the strongest of the lightweight metals. Used primarily in military applications prior to the end of the Cold War, beryllium is finding new applications in many commercial products, including computers, telecommunication equipment, and consumer and automotive electronics. The use of beryllium in nondefense consumer applications is of concern because beryllium is toxic. Inhalation of beryllium dust or vapor causes a chronic lung disease in some individuals at concentrations as low as 0.01 microg/m3 in air. As beryllium enters wider commerce, it is prudent to ask what risks this might present to the general public and to workers downstream of the beryllium materials industry. We address this question by evaluating the potential for beryllium exposure from the manufacturing, use, recycle, and disposal of beryllium-containing products. Combining a market study with a qualitative exposure analysis, we determine which beryllium applications and life cycle phases have the largest exposure potential. Our analysis suggests that use and maintenance of the most common types of beryllium-containing products do not result in any obvious exposures of concern, and that maintenance activities result in greater exposures than product use. Product disposal has potential to present significant individual risks, but uncertainties concerning current and future routes of product disposal make it difficult to be definitive. Overall, additional exposure and dose-response data are needed to evaluate both the health significance of many exposure scenarios, and the adequacy of existing regulations to protect workers and the public. Although public exposures to beryllium and public awareness and concern regarding beryllium risks are currently low, beryllium risks have psychometric qualities that may lead to rapidly heightened public concern.

Research program on plasma core assembly

International Nuclear Information System (INIS)

Bernard, W.; Helmick, H.H.; Jarvis, G.A.; Plassmann, E.A.; White, R.H.

1975-05-01

An operating critical assembly having a 1.024-m-diam by 1.055-m-high cavity reflected by 0.48 m of beryllium has been constructed of residual beryllium reflector segments, control drums, drive motors, and control console from the solid core nuclear rocket development program. The critical mass for uranium distributed throughout the cavity is 16.9 kg U(93.2), which is high because of neutron undermoderation in the reflector due to porosity and poison contaminants in the beryllium and graphite reflector components. A flux trapping beryllium annulus, 0.546-m-i.d. by 0.89-m-o.d., centered in the cavity, reduced the critical mass to 6.7 kg U(93.2). This arrangement will permit operation with a UF 6 zone inside the flux trap driven by an outer uranium-graphite fuel zone. The fission density inside the flux trap is appreciably higher than in the outer fuel zone. (U.S.)

Structural analysis of equilibrium and ohmic heating coil assemblies for the TFTR

International Nuclear Information System (INIS)

Chattopadhyay, S.

1975-10-01

The structural adequacy of the equilibrium and ohmic heating coils and their support systems for the TFTR device has been investigated. The capability of the coils to span ribs of the support structure has been established. The support structure has been found to be effective in resisting the magnetic forces in the coils. The bands encircling the outboard coils and the band tensioning devices have been found to perform adequately. The analysis is based on October 1975 conceptual design

Irradiated Beryllium Disposal Workshop, Idaho Falls, ID, May 29-30, 2002

Energy Technology Data Exchange (ETDEWEB)

Longhurst, Glen Reed; Anderson, Gail; Mullen, Carlan K; West, William Howard

2002-07-01

In 2001, while performing routine radioactive decay heat rate calculations for beryllium reflector blocks for the Advanced Test Reactor (ATR), it became evident that there may be sufficient concentrations of transuranic isotopes to require classification of this irradiated beryllium as transuranic waste. Measurements on samples from ATR reflector blocks and further calculations confirmed that for reflector blocks and outer shim control cylinders now in the ATR canal, transuranic activities are about five times the threshold for classification. That situation implies that there is no apparent disposal pathway for this material. The problem is not unique to the ATR. The High Flux Isotope Reactor at Oak Ridge National Laboratory, the Missouri University Research Reactor at Columbia, Missouri and other reactors abroad must also deal with this issue. A workshop was held in Idaho Falls Idaho on May 29-30, 2002 to acquaint stakeholders with these findings and consider a path forward in resolving the issues attendant to disposition of irradiated material. Among the findings from this workshop were (1) there is a real potential for the US to be dependent on foreign sources for metallic beryllium within about a decade; (2) there is a need for a national policy on beryllium utilization and disposition and for a beryllium coordinating committee to be assembled to provide guidance on that policy; (3) it appears it will be difficult to dispose of this material at the Waste Isolation Pilot Plant (WIPP) near Carlsbad, New Mexico due to issues of Defense classification, facility radioactivity inventory limits, and transportation to WIPP; (4) there is a need for a funded DOE program to seek resolution of these issues including research on processing techniques that may make this waste acceptable in an existing disposal pathway or allow for its recycle.

Method of reducing multipole content in a conductor assembly during manufacture

Science.gov (United States)

Meinke, Rainer

2013-08-20

A method for manufacture of a conductor assembly. The assembly is of the type which, when conducting current, generates a magnetic field or in which, in the presence of a changing magnetic field, a voltage is induced. In an example embodiment one or more first coil rows are formed. The assembly has multiple coil rows about an axis with outer coil rows formed about inner coil rows. A determination is made of deviations from specifications associated with the formed one or more first coil rows. One or more deviations correspond to a magnitude of a multipole field component which departs from a field specification. Based on the deviations, one or more wiring patterns are generated for one or more second coil rows to be formed about the one or more first coil rows. The one or more second coil rows are formed in the assembly. The magnitude of each multipole field component that departs from the field specification is offset.

Plasmodium vivax antigen discovery based on alpha-helical coiled coil protein motif.

Directory of Open Access Journals (Sweden)

Nora Céspedes

Full Text Available Protein α-helical coiled coil structures that elicit antibody responses, which block critical functions of medically important microorganisms, represent a means for vaccine development. By using bioinformatics algorithms, a total of 50 antigens with α-helical coiled coil motifs orthologous to Plasmodium falciparum were identified in the P. vivax genome. The peptides identified in silico were chemically synthesized; circular dichroism studies indicated partial or high α-helical content. Antigenicity was evaluated using human sera samples from malaria-endemic areas of Colombia and Papua New Guinea. Eight of these fragments were selected and used to assess immunogenicity in BALB/c mice. ELISA assays indicated strong reactivity of serum samples from individuals residing in malaria-endemic regions and sera of immunized mice, with the α-helical coiled coil structures. In addition, ex vivo production of IFN-γ by murine mononuclear cells confirmed the immunogenicity of these structures and the presence of T-cell epitopes in the peptide sequences. Moreover, sera of mice immunized with four of the eight antigens recognized native proteins on blood-stage P. vivax parasites, and antigenic cross-reactivity with three of the peptides was observed when reacted with both the P. falciparum orthologous fragments and whole parasites. Results here point to the α-helical coiled coil peptides as possible P. vivax malaria vaccine candidates as were observed for P. falciparum. Fragments selected here warrant further study in humans and non-human primate models to assess their protective efficacy as single components or assembled as hybrid linear epitopes.

Evaluation of mechanical integrity for helical coil hold-down spring of PLUS7TM fuel

International Nuclear Information System (INIS)

Choi, Ki Sung; Kim, Yong Hwan; Kwon, Jung Tack; Kim, Kyu Tae

2004-01-01

Nuclear fuel assembly is subject to hydraulic forces generated by primary coolant flow during reactor operation. These forces may be sufficient to overcome the fuel assembly weight thereby allowing the fuel assembly to lift off of its support. To provide a positive hold-down margin against the upward coolant flow forces, helical coil springs or leaf springs are installed in the fuel assemblies. An advanced fuel for Korean Standard Nuclear Power Plants (KSNP), PLUS7 fuel has developed to get the thermal margin increase, failure free and high seismic resistance, etc. And the new designed helical coil hold-down spring was introduced into PLUS7 fuel assembly. The purpose of this paper is to evaluate the mechanical integrity for the helical coil hold-down spring of PLUS7 fuel assembly

Investigations of the ternary system beryllium-carbon-tungsten and analyses of beryllium on carbon surfaces; Untersuchung des ternaeren Systems Beryllium-Kohlenstoff-Wolfram und Betrachtungen von Beryllium auf Kohlenstoffoberflaechen

Energy Technology Data Exchange (ETDEWEB)

Kost, Florian

2009-05-25

Beryllium, carbon and tungsten are planned to be used as first wall materials in the future fusion reactor ITER. The aim of this work is a characterization of mixed material formation induced by thermal load. To this end, model systems (layers) were prepared and investigated, which give insight into the basic physical and chemical concepts. Before investigating ternary systems, the first step was to analyze the binary systems Be/C and Be/W (bottom-up approach), where the differences between the substrates PG (pyrolytic graphite) and HOPG (highly oriented pyrolytic graphite) were of special interest. Particularly X-ray photoelectron spectroscopy (XPS), low energy ion scattering (ISS) and Rutherford backscattering spectroscopy (RBS) were used as analysis methods. Beryllium evaporated on carbon shows an island growth mode, whereas a closed layer can be assumed for layer thicknesses above 0.7 nm. Annealing of the Be/C system induces Be{sub 2}C island formation for T{>=}770 K. At high temperatures (T{>=}1170 K), beryllium carbide dissociates, resulting in (metallic) beryllium desorption. For HOPG, carbide formation starts at higher temperatures compared to PG. Activation energies for the diffusion processes were determined by analyzing the decreasing beryllium amount versus annealing time. Surface morphologies were characterized using angle-resolved XPS (ARXPS) and atomic force microscopy (AFM). Experiments were performed to study processes in the Be/W system in the temperature range from 570 to 1270 K. Be{sub 2}W formation starts at 670 K, a complete loss of Be{sub 2}W is observed at 1170 K due to dissociation (and subsequent beryllium desorption). Regarding ternary systems, particularly Be/C/W and C/Be/W were investigated, attaching importance to layer thickness (reservoir) variations. At room temperature, Be{sub 2}C, W{sub 2}C, WC and Be{sub 2}W formation at the respective interfaces was observed. Further Be{sub 2}C is forming with increasing annealing temperatures

METHOD OF BRAZING BERYLLIUM

Science.gov (United States)

Hanks, G.S.; Keil, R.W.

1963-05-21

A process is described for brazing beryllium metal parts by coating the beryllium with silver (65- 75 wt%)-aluminum alloy using a lithium fluoride (50 wt%)-lithium chloride flux, and heating the coated joint to a temperature of about 700 un. Concent 85% C for about 10 minutes. (AEC)

Sanitary-hygienic and ecological aspects of beryllium production

Energy Technology Data Exchange (ETDEWEB)

Dvinskykh, E.M.; Savchuk, V.V.; Sidorov, V.L.; Slobodin, D.B.; Tuzov, Y.V. [Ulba Metallurgical Plant, Ust-Kamenogorsk (Kazakhstan)

1998-01-01

The Report describes An organization of sanitary-hygienic and ecological control of beryllium production at Ulba metallurgical plant. It involves: (1) the consideration of main methods for protection of beryllium production personnel from unhealthy effect of beryllium, (2) main kinds of filters, used in gas purification systems at different process areas, (3) data on beryllium monitoring in water, soil, on equipment. This Report also outlines problems connected with designing devices for a rapid analysis of beryllium in air as well as problems of beryllium production on ecological situation in the town. (author)

Beryllium for fusion application - recent results

International Nuclear Information System (INIS)

Khomutov, A.; Barabash, V.; Chakin, V.; Chernov, V.; Davydov, D.; Gorokhov, V.; Kawamura, H.; Kolbasov, B.; Kupriyanov, I.; Longhurst, G.; Scaffidi-Argentina, F.; Shestakov, V.

2002-01-01

The main issues for the application of beryllium in fusion reactors are analyzed taking into account the latest results since the ICFRM-9 (Colorado, USA, October 1999) and presented at 5th IEA Be Workshop (10-12 October 2001, Moscow Russia). Considerable progress has been made recently in understanding the problems connected with the selection of the beryllium grades for different applications, characterization of the beryllium at relevant operational conditions (irradiation effects, thermal fatigue, etc.), and development of required manufacturing technologies. The key remaining problems related to the application of beryllium as an armour in near-term fusion reactors (e.g. ITER) are discussed. The features of the application of beryllium and beryllides as a neutron multiplier in the breeder blanket for power reactors (e.g. DEMO) in pebble-bed form are described

Beryllium for fusion application - recent results

Science.gov (United States)

Khomutov, A.; Barabash, V.; Chakin, V.; Chernov, V.; Davydov, D.; Gorokhov, V.; Kawamura, H.; Kolbasov, B.; Kupriyanov, I.; Longhurst, G.; Scaffidi-Argentina, F.; Shestakov, V.

2002-12-01

The main issues for the application of beryllium in fusion reactors are analyzed taking into account the latest results since the ICFRM-9 (Colorado, USA, October 1999) and presented at 5th IEA Be Workshop (10-12 October 2001, Moscow Russia). Considerable progress has been made recently in understanding the problems connected with the selection of the beryllium grades for different applications, characterization of the beryllium at relevant operational conditions (irradiation effects, thermal fatigue, etc.), and development of required manufacturing technologies. The key remaining problems related to the application of beryllium as an armour in near-term fusion reactors (e.g. ITER) are discussed. The features of the application of beryllium and beryllides as a neutron multiplier in the breeder blanket for power reactors (e.g. DEMO) in pebble-bed form are described.

CCBuilder 2.0: Powerful and accessible coiled-coil modeling.

Science.gov (United States)

Wood, Christopher W; Woolfson, Derek N

2018-01-01

The increased availability of user-friendly and accessible computational tools for biomolecular modeling would expand the reach and application of biomolecular engineering and design. For protein modeling, one key challenge is to reduce the complexities of 3D protein folds to sets of parametric equations that nonetheless capture the salient features of these structures accurately. At present, this is possible for a subset of proteins, namely, repeat proteins. The α-helical coiled coil provides one such example, which represents ≈ 3-5% of all known protein-encoding regions of DNA. Coiled coils are bundles of α helices that can be described by a small set of structural parameters. Here we describe how this parametric description can be implemented in an easy-to-use web application, called CCBuilder 2.0, for modeling and optimizing both α-helical coiled coils and polyproline-based collagen triple helices. This has many applications from providing models to aid molecular replacement for X-ray crystallography, in silico model building and engineering of natural and designed protein assemblies, and through to the creation of completely de novo "dark matter" protein structures. CCBuilder 2.0 is available as a web-based application, the code for which is open-source and can be downloaded freely. http://coiledcoils.chm.bris.ac.uk/ccbuilder2. We have created CCBuilder 2.0, an easy to use web-based application that can model structures for a whole class of proteins, the α-helical coiled coil, which is estimated to account for 3-5% of all proteins in nature. CCBuilder 2.0 will be of use to a large number of protein scientists engaged in fundamental studies, such as protein structure determination, through to more-applied research including designing and engineering novel proteins that have potential applications in biotechnology. © 2017 The Authors Protein Science published by Wiley Periodicals, Inc. on behalf of The Protein Society.

The nature of beryllium disease

International Nuclear Information System (INIS)

Williams, W.J.

1977-01-01

The increasing use of beryllium in modern industry poses a continuing health hazard with a real risk of producing incapacitating disease and even death. Beryllium and its salts are very toxic, even in small doses and may produce lesions in any organ. The majority of cases follow inhalation and may cause either acute or chronic lung disease. Acute pulmonary disease is a form of chemical pneumonitis while the chronic disease is characterised by the production of granulomas and fibrosis. The skin may be affected with the finding of dermatitis, acute or chronic ulceration. Other organs commonly involved include the liver and kidneys. The pathology of beryllium disease is not specific and diagnosis depends on satisfying the following criteria - history of exposure, consistent clinical, radiographic and pathological finding, presence of beryllium in tissue/fluid and evidence of hypersensitivity. Recent development of 'in vitro' tests of hypersensitivity may prove of value in both diagnosis and prevention of disease. Beryllium disease responds to steroid therapy but the only sure treatment is avoidance of exposure. (author)

Beryllium electrodeposition on aluminium cathode from chloride melts

International Nuclear Information System (INIS)

Nichkov, I.F.; Novikov, E.A.; Serebryakov, G.A.; Kanashin, Yu.P.; Sardyko, G.N.

1980-01-01

Cathodic processes during beryllium deposition on liquid and solid aluminium cathodes are investigated. Mixture of sodium, potassium and beryllium chloride melts served as an lectrolyte. Beryllium ion discharge at the expense of alloy formation takes place at more positive potentials than on an indifferent cathode at low current densities ( in the case of liquid aluminium cathode). Metallographic analysis and measurements of microhardness have shown, that the cathodic product includes two phases: beryllium solid solution in aluminium and metallic beryllium. It is concluded, that aluminium-beryllium alloys with high cathodic yield by current can be obtained by the electrolytic method

Control of beryllium powder at a DOE facility

International Nuclear Information System (INIS)

Langner, G.C.; Creek, K.L.; Castro, R.G.

1997-01-01

Beryllium is contained in a number of domestic and national defense items. Although many items might contain beryllium in some manner, few people need worry about the adverse effects caused by exposure to beryllium because it is the inhalable form of beryllium that is most toxic. Chronic beryllium disease (CBD), a granulomas and fibrotic lung disease with long latency, can be developed after inhalation exposures to beryllium. It is a progressive, debilitating lung disease. Its occurrence in those exposed to beryllium has been difficult to predict because some people seem to react to low concentration exposures whereas others do not react to high concentration exposures. Onset of the disease frequently occurs between 15 to 20 years after exposure begins. Some people develop the disease after many years of low concentration exposures but others do not develop CBD even though beryllium is shown to be present in lungs and urine. Conclusions based on these experiences are that their is some immunological dependence of developing CBD in about 3--4% of the exposed population, but the exact mechanism involved has not yet been identified. Acute beryllium disease can occur after a single exposure to a concentration of greater than 0.100 mg/m3 (inhalation exposure); it is characterized by the development of chemical pneumoconiosis, a respiratory disease. The acute effect of skin contact is a dermatitis characterized by itching and reddened, elevated, or fluid-accumulated lesions which appear particularly on the exposed surfaces of the body, especially the face, neck, arms, and hands. Small particles of beryllium that enter breaks in the skin can lead to the development of granulomas and/or open sores that do not heal until the beryllium has been removed. Our interest is only airborne beryllium, which is found in areas that machine or produce beryllium

Regulated assembly of a supramolecular centrosome scaffold in vitro

DEFF Research Database (Denmark)

Woodruff, J. B.; Wueseke, O.; Viscardi, V.

2015-01-01

are not well understood. In Caenorhabditis elegans, PCM assembly requires the coiled-coil protein SPD-5. We found that recombinant SPD-5 could polymerize to form micrometer-sized porous networks in vitro. Network assembly was accelerated by two conserved regulators that control PCM assembly in vivo, Polo...

The IEA Large Coil Task

International Nuclear Information System (INIS)

Beard, D.S.; Klose, W.; Shimamoto, S.; Vecsey, G.

1988-01-01

A multinational program of cooperative research, development, demonstrations, and exchanges of information on superconducting magnets for fusion was initiated in 1977 under an IEA agreement. The first major step in the development of TF magnets was called the Large Coil Task. Participants in LCT were the U.S. DOE, EURATOM, JAERI, and the Departement Federal de l'Interieur of Switzerland. The goals of LCT were to obtain experimental data, to demonstrate reliable operation of large superconducting coils, and to prove design principles and fabrication techniques being considered for the toroidal magnets of thermonuclear reactors. These goals were to be accomplished through coordinated but largely independent design, development, and construction of six test coils, followed by collaborative testing in a compact toroidal test array at fields of 8 T and higher. Under the terms of the IEA Agreement, the United States built and operated the test facility at Oak Ridge and provided three test coils. The other participants provided one coil each. Information on design and manufacturing and all test data were shared by all. The LCT team of each participant included a government laboratory and industrial partners or contractors. The last coil was completed in 1985, and the test assembly was completed in October of that year. Over the next 23 months, the six-coil array was cooled down and extensive testing was performed. Results were gratifying, as tests achieved design-point performance and well beyond. (Each coil reached a peak field of 9 T.) Experiments elucidated coil behavior, delineated limits of operability, and demonstrated coil safety. (orig./KP)

Accomplishments in Field Period Assembly for NCSX. This is how we did it

International Nuclear Information System (INIS)

Viola, Michael; Edwards, J.; Brown, T.; Dudek, L.; Ellis, R.; Heitzenroeder, P.; Strykowsky, R.; Cole, Michael

2009-01-01

The National Compact Stellarator Experiment (NCSX) was a collaborative effort between ORNL and PPPL. PPPL provided the assembly techniques with guidance from ORNL to meet design criteria. The individual vacuum vessel segments, modular coils, trim coils, and toroidal field coils components were delivered to the Field Period Assembly (FPA) crew who then would complete the component assemblies and then assemble the final three field period assemblies, each consisting of two sets of three modular coils assembled over a 120o vacuum vessel segment with the trim coils and toroidal field coils providing the outer layer. The requirements for positioning the modular coils were found to be most demanding. The assembly tolerances required for accurate positioning of the field coil windings in order to generate sufficiently accurate magnetic fields strained state of the art techniques in metrology and alignment and required constant monitoring of assembly steps with laser trackers, measurement arms, and photogrammetry. The FPA activities were being performed concurrently while engineering challenges were being resolved. For example, it was determined that high friction electrically isolated shims were needed between the modular coil interface joints and low distortion welding was required in the nose region of those joints. This took months of analysis and development yet the assembly was not significantly impacted because other assembly tasks could be performed in parallel with ongoing assembly tasks as well as tasks such as advance tooling setup preparation for the eventual welding tasks. The crew technicians developed unique, accurate time saving techniques and tooling which provided significant cost and schedule savings. Project management displayed extraordinary foresight and every opportunity to gain advanced knowledge and develop techniques was taken advantage of. Despite many risk concerns, the cost and schedule performance index was maintained nearly 1.0 during the

Research of beryllium safety issues

International Nuclear Information System (INIS)

Longhurst, G.R.; Anderl, R.A.; Dolan, T.J.; Hankins, M.R.; Pawelko, R.J.

1993-01-01

Beryllium has been identified as a leading contender for the plasma-facing material in ITER. Its use has some obvious advantages, but there are also a number of safety concerns associated with it. The Idaho National Engineering Laboratory (INEL) has undertaken a number of studies to help resolve some of these issues. One issue is the response of beryllium to neutron irradiation. We have tested samples irradiated in the Advanced Test Reactor (ATR) and are currently preparing to make measurements of the change in mechanical properties of beryllium samples irradiated at elevated temperatures in the Fast Flux Test Facility (FFTF) and the Experimental Breeder Reactor II (EBR-II) at the INEL. Mechanical tests will be conducted at the irradiation temperatures of 375-550 C. Other experiments address permeation and retention of implanted tritium in plasma-sprayed beryllium. In one test the porosity of the material allowed 0.12% of implanted ions and 0.17% of atoms from background gas pressure to pass through the foil with essentially no delay. For comparison, similar tests on fully dense hot-rolled, vacuum melted or sintered powder foils of high purity beryllium showed only 0.001% of implanting ions to pass through the foil, and then only after a delay of several hours. None of the molecular gas appeared to permeate these latter targets. An implication is that plasma-sprayed beryllium may substantially enhance recycling of tritium to the plasma provided it is affixed to a relatively impermeable substrate. (orig.)

Offshoots from beryllium development programme

International Nuclear Information System (INIS)

Sharma, B.P.; Sinha, P.K.

1995-01-01

The paper briefly presents extraction and processing of beryllium metal as practiced in the beryllium facilities at Turbhe, New Bombay. These facilities have been set up to meet the indigenous requirements of the metal in space and nuclear science programmes. As offshoot of this beryllium development programme has been the development of a number of pyro and powder metallurgical equipment. Indigenous development of these pieces of equipment has been a professionally rewarding experience. Efforts are now on to promote these equipment for industrial use. (author). 6 refs., 6 figs., 2 tabs

Fatigue assessment of central support structure coil jacket of 4.5 MJ SMES

International Nuclear Information System (INIS)

Akhter, Javed; Bhunia, Uttam; Mondal, Bidhan Chandra; Nandi, Chinmay; Pal, Gautam; Saha, Subimal

2013-01-01

The Superconducting coil of 4.5 SMES will be of sector-toroidal type with 8 sectors. The maximum coil current will be 1200 Amperes. During its life time the SMES will be subjected to several cycles of charging and discharging. Thus the structural assessment of coil central support structure and the Liquid Helium Jacket, which comprises of the stress analysis and the fatigue life assessment, is a critical part of the design. In this paper fatigue life assessment of the 4.5 MJ SMES coil central support structure and the Liquid Helium Jacket together with the related stress analysis is presented. Coupled electromagnetic and Structural analysis using the commercial finite element analysis package ANSYS is performed. Considering the cyclic symmetry of the coil assembly, only 1/8th of the assembly is modelled. (author)

Fluorimetric method for determination of Beryllium

International Nuclear Information System (INIS)

Sparacino, N.; Sabbioneda, S.

1996-10-01

The old fluorimetric method for the determination of Beryllium, based essentially on the fluorescence of the Beryllium-Morine complex in a strongly alkaline solution, is still competitive and stands the comparison with more modern methods or at least three reasons: in the presence of solid or gaseous samples (powders), the times necessary to finalize an analytic determination are comparable since the stage of the process which lasts the longest is the mineralization of the solid particles containing Beryllium, the cost of a good fluorimeter is by far Inferior to the cost, e. g., of an Emission Spectrophotometer provided with ICP torch and magnets for exploiting the Zeeman effect and of an Atomic absorption Spectrophotometer provided with Graphite furnace; it is possible to determine, fluorimetrically, rather small Beryllium levels (about 30 ng of Beryllium/sample), this potentiality is more than sufficient to guarantee the respect of all the work safety and hygiene rules now in force. The study which is the subject of this publication is designed to the analysis procedure which allows one to reach good results in the determination of Beryllium, chiefly through the control and measurement of the interference effect due to the presence of some metals which might accompany the environmental samples of workshops and laboratories where Beryllium is handled, either at the pure state or in its alloys. The results obtained satisfactorily point out the merits and limits of this analytic procedure

Preparation of beryllium hydride

International Nuclear Information System (INIS)

Bergeron, C.R.; Baker, R.W.

1975-01-01

Beryllium hydride of high bulk density, suitable for use as a component of high-energy fuels, is prepared by the pyrolysis, in solution in an inert solvent, of a ditertiary-alkyl beryllium. An agitator introduces mechanical energy into the reaction system, during the pyrolysis, at the rate of 0.002 to 0.30 horsepower per gallon of reaction mixture. (U.S.)

High-strength beryllium block

International Nuclear Information System (INIS)

Pinto, N.P.; Keith, G.H.

1977-01-01

Beryllium billets hot isopressed using fine powder of high purity have exceptionally attractive properties; average tensile ultimate, 0.2% offset yield strength and elongation are 590 MPa, 430 MPa and 4.0% respectively. Properties are attributed to the fine grain size (about 4.0 μm average diameter) and the relatively low levels of BeO present as fine, well-dispersed particles. Dynamic properties, e.g., fracture toughness, are similar to those of standard grade, high-purity beryllium. The modulus of beryllium is retained to very high stress levels, and the microyield stress or precision elastic limit is higher than for other grades, including instrument grades. Limited data for billets made from normal-purity fine powders show similar room temperature properties. (author)

Metrology Techniques for the Assembly of NCSX

International Nuclear Information System (INIS)

Priniski, C.; Dodson, T.; Duco, M.; Raftopoulos, S.; Ellis, R.; Brooks, A.

2009-01-01

In support of the National Compact Stellerator Experiment (NCSX), stellerator assembly activities continued this past year at the Princeton Plasma Physics Laboratory (PPPL) in partnership with the Oak Ridge National Laboratory (ORNL). The construction program saw the completion of the first two Half Field-Period Assemblies (HPA), each consisting of three modular coils. The full machine includes six such sub-assemblies. A single HPA consists of three of the NCSX modular coils wound and assembled at PPPL. These geometrically-complex three dimensional coils were wound using computer-aided metrology and CAD models to tolerances within +/- 0.5mm. The assembly of these coils required similar accuracy on a larger scale with the added complexity of more individual parts and fewer degrees of freedom for correction. Several new potential positioning issues developed for which measurement and control techniques were developed. To accomplish this, CAD coordinate-based computer metrology equipment and software similar to the solutions employed for winding the modular coils was used. Given the size of the assemblies, the primary tools were both interferometer aided and Absolute Distance Measurement (ADM)-only based laser trackers. In addition, portable Coordinate Measurement Machine (CMM) arms and some novel indirect measurement techniques were employed. This paper will detail both the use of CAD coordinate-based metrology technology and the techniques developed and employed for dimensional control of NSCX subassemblies. The results achieved and possible improvements to techniques will be discussed.

The Short Model Coil (SMC) dipole: an R&D program towards Nb$_{3}$Sn accelerator magnets

CERN Document Server

Bajko, M; Canfer, S; Ellwood, G; Feuvrier, J; Guinchard, M; Karppinen, M; Kokkinos, C; Manil, P; Milanese, A; Oberli, L; Perez, J-C; Regis, F; de Rijk, G

2011-01-01

The Short Model Coil (SMC) assembly has been designed, as test bench for short racetrack coils wound with Nb$_{3}$Sn cable. The mechanical structure comprises an iron yoke surrounded by a 20 mm thick aluminium alloy shell, and includes four loading pads that transmit the required pre-compression from the outer shell into the two coils. The outer shell is pre-tensioned with mechanical keys that are inserted with the help of pressurized bladders and two 30 mm diameter aluminium alloy rods provide the axial loading to the coil ends. The outer shell, the axial rods, and the coils are instrumented with strain gauges, which allow precise monitoring of the loading conditions during the assembly and at cryogenic temperature during the magnet test. Two SMC assemblies have been completed and cold tested in the frame of a European collaboration between CEA (FR), CERN and STFC (UK) and with the technical support from LBNL (US). This paper describes the main features of the SMC assembly, the experience from the dummy asse...

The SMC (Short Model Coil) dipole: An R&D program for Nb$_{3}$Sn accelerator magnets

CERN Document Server

Perez, J C; Bordini, B; Canfer, S; Ellwood, G; Feuvrier, J; Guinchard, M; Karppinen, M; Kokkinos, C; Manil, P; Milanese, A; Oberli, L; Regis, F; de Rijk, G

2012-01-01

The Short Model Coil (SMC) assembly has been designed, as test bench for short racetrack coils wound with Nb$_{3}$Sn cable. The mechanical structure comprises an iron yoke surrounded by a 20 mm thick aluminium alloy shell, and includes four loading pads that transmit the required pre-compression from the outer shell into the two coils. The outer shell is pre-tensioned with mechanical keys that are inserted with the help of pressurized bladders and two 30 mm diameter aluminium alloy rods provide the axial loading to the coil ends. The outer shell, the axial rods, and the coils are instrumented with strain gauges, which allow precise monitoring of the loading conditions during the assembly and at cryogenic temperature during the magnet test. Two SMC assemblies have been completed and cold tested in the frame of a European collaboration between CEA (FR), CERN and STFC (UK) and with the technical support from LBNL (US). This paper describes the main features of the SMC assembly, the experience from the dummy ass...

Reaction-diffusion modeling of hydrogen in beryllium

Energy Technology Data Exchange (ETDEWEB)

Wensing, Mirko; Matveev, Dmitry; Linsmeier, Christian [Forschungszentrum Juelich GmbH, Institut fuer Energie- und Klimaforschung - Plasmaphysik (Germany)

2016-07-01

Beryllium will be used as first-wall material for the future fusion reactor ITER as well as in the breeding blanket of DEMO. In both cases it is important to understand the mechanisms of hydrogen retention in beryllium. In earlier experiments with beryllium low-energy binding states of hydrogen were observed by thermal desorption spectroscopy (TDS) which are not yet well understood. Two candidates for these states are considered: beryllium-hydride phases within the bulk and surface effects. The retention of deuterium in beryllium is studied by a reaction rate approach using a coupled reaction diffusion system (CRDS)-model relying on ab initio data from density functional theory calculations (DFT). In this contribution we try to assess the influence of surface recombination.

Recommended design correlations for S-65 beryllium

International Nuclear Information System (INIS)

Billone, M.C.

1995-01-01

The properties of tritium and helium behavior in irradiated beryllium are reviewed, along with the thermal-mechanical properties needed for ITER design analysis. Correlations are developed to describe the performance of beryllium in a fusion reactor environment. While this paper focuses on the use of beryllium as a plasma-facing component (PFC) material, the correlations presented here can also be used to describe the performance of beryllium as a neutron multiplier for a tritium breeding blanket. The performance properties for beryllium are subdivided into two categories: properties which do not change with irradiation damage to the bulk of the material; and properties which are degraded by neutron irradiation. The irradiation-independent properties described within are: thermal conductivity, specific heat capacity, thermal expansion, and elastic constants. Irradiation-dependent properties include: yield strength, ultimate tensile strength, plastic tangent modulus, uniform and total tensile elongation, thermal and irradiation-induced creep strength, He-induced swelling and tritium retention/release. The approach taken in developing properties correlations is to describe the behavior of dense, pressed S-65 beryllium -- the material chosen for ITER PFC application -- as a function of temperature. As there are essentially no data on the performance of porous and/or irradiated S-65 beryllium, the degradation of properties with as-fabricated porosity and irradiation are determined from the broad data base on S-200F, as well as other types and grades, and applied to S-65 beryllium by scaling factors. The resulting correlations can be used for Be produced by vacuum hot pressing (VHP) and cold-pressing (CP)/sintering(S)/hot-isostatic-pressing (HIP). The performance of plasma-sprayed beryllium is discussed but not quantified

Exposure and genetics increase risk of beryllium sensitisation and chronic beryllium disease in the nuclear weapons industry.

Science.gov (United States)

Van Dyke, Michael V; Martyny, John W; Mroz, Margaret M; Silveira, Lori J; Strand, Matt; Cragle, Donna L; Tankersley, William G; Wells, Susan M; Newman, Lee S; Maier, Lisa A

2011-11-01

Beryllium sensitisation (BeS) and chronic beryllium disease (CBD) are caused by exposure to beryllium with susceptibility affected by at least one well-studied genetic host factor, a glutamic acid residue at position 69 (E69) of the HLA-DPβ chain (DPβE69). However, the nature of the relationship between exposure and carriage of the DPβE69 genotype has not been well studied. The goal of this study was to determine the relationship between DPβE69 and exposure in BeS and CBD. Current and former workers (n=181) from a US nuclear weapons production facility, the Y-12 National Security Complex (Oak Ridge, Tennessee, USA), were enrolled in a case-control study including 35 individuals with BeS and 19 with CBD. HLA-DPB1 genotypes were determined by PCR-SSP. Beryllium exposures were assessed through worker interviews and industrial hygiene assessment of work tasks. After removing the confounding effect of potential beryllium exposure at another facility, multivariate models showed a sixfold (OR 6.06, 95% CI 1.96 to 18.7) increased odds for BeS and CBD combined among DPβE69 carriers and a fourfold (OR 3.98, 95% CI 1.43 to 11.0) increased odds for those exposed over an assigned lifetime-weighted average exposure of 0.1 μg/m(3). Those with both risk factors had higher increased odds (OR 24.1, 95% CI 4.77 to 122). DPβE69 carriage and high exposure to beryllium appear to contribute individually to the development of BeS and CBD. Among workers at a beryllium-using facility, the magnitude of risk associated with either elevated beryllium exposure or carriage of DPβE69 alone appears to be similar.

Some aspects of beryllium disposal in Kazakhstan

International Nuclear Information System (INIS)

Shestakov, V.; Chikhray, Y.; Shakhvorostov, Yr.

2004-01-01

Historically in Kazakhstan all disposals of used beryllium and beryllium wasted materials were stored and recycled at JSC ''Ulba Metallurgical Plant''. Since Ulba Metallurgical Plant (beside beryllium and tantalum production) is one of the world largest complex producers of fuel for nuclear power plants as well it has possibilities, technologies and experience in processing toxic and radioactive wastes related with those productions. At present time only one operating Kazakhstan research reactors (EWG1M in Kurchatov) contains beryllium made core. The results of current examination of that core allow using it without replacement long time yet (at least for next five-ten years). Nevertheless the problem how to utilize such irradiated beryllium becomes actual issue for Kazakhstan even today. Since Kazakhstan is the member of ITER/DEMO Reactors Projects and is permanently considered as possible provider of huge amount of beryllium for those reactors so that is the reason for starting studies of possibilities of large scale processing/recycling of such disposed irradiated beryllium. It is clear that the Ulba Metallurgical Plant is considered as the best site for it in Kazakhstan. The draft plan how to organize experimental studies of irradiated beryllium disposals in Kazakhstan involving National Nuclear Center, National University (Almaty), JSC ''Ulba Metallurgical Plant'' (Ust-Kamenogorsk) would be presented in this paper as well as proposals to arrange international collaboration in that field through ISTC (International Science Technology Center, Moscow). (author)

Effect of transient heating loads on beryllium

International Nuclear Information System (INIS)

Kupriyanov, Igor B.; Porezanov, Nicolay P.; Nikolaev, Georgyi N.; Kurbatova, Liudmila A.; Podkovyrov, Vyacheslav L.; Muzichenko, Anatoliy D.; Zhitlukhin, Anatoliy M.; Khimchenko, Leonid N.; Gervash, Alexander A.

2014-01-01

Highlights: • We study the effect of transient plasma loads on beryllium erosion and surface microstructure. • Beryllium targets were irradiated by plasma streams with energy of 0.5–1 MJ/m 2 at ∼250 °C. • Under plasma loads 0.5–1 MJ/m 2 cracking of beryllium surface is rather slight. • Under 0.5 MJ/m 2 the mass loss of Be is no more than 0.2 g/m 2 shot and decreasing with shots number. • Under 1 MJ/m 2 maximum mass loss of beryllium was 3.7 g/m 2 shot and decreasing with shots number. - Abstract: Beryllium will be used as a plasma facing material for ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of ITER first wall. The results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility are presented. The Be/CuCrZr mock-ups were exposed to upto 100 shots by deuterium plasma streams with pulse duration of 0.5 ms at ∼250 °C and average heat loads of 0.5 and 1 MJ/m 2 . Experiments were performed at 250 °C. The evolution of surface microstructure and cracks morphology as well as beryllium mass loss are investigated under erosion process

The Cryogenic Properties of Several Aluminum-Beryllium Alloys and a Beryllium Oxide Material

Science.gov (United States)

Gamwell, Wayne R.; McGill, Preston B.

2003-01-01

Performance related mechanical properties for two aluminum-beryllium (Al-Be) alloys and one beryllium-oxide (BeO) material were developed at cryogenic temperatures. Basic mechanical properties (Le., ultimate tensile strength, yield strength, percent elongation, and elastic modulus were obtained for the aluminum-beryllium alloy, AlBeMetl62 at cryogenic [-195.5"C (-320 F) and -252.8"C (-423"F)I temperatures. Basic mechanical properties for the Be0 material were obtained at cyrogenic [- 252.8"C (-423"F)] temperatures. Fracture properties were obtained for the investment cast alloy Beralcast 363 at cryogenic [-252.8"C (-423"F)] temperatures. The AlBeMetl62 material was extruded, the Be0 material was hot isostatic pressing (HIP) consolidated, and the Beralcast 363 material was investment cast.

The beryllium production at Ulba metallurgical plant (Ust-Kamenogrsk, Kazakhstan)

Energy Technology Data Exchange (ETDEWEB)

Dvinskykh, E.M.; Savchuk, V.V.; Tuzov, Y.V. [Ulba Metallurgical Plant (Zavod), Ust-Kamenogorsk, Abay prospect 102 (Kazakhstan)

1998-01-01

The Report includes data on beryllium production of Ulba metallurgical plant, located in Ust-Kamenogorsk (Kazakhstan). Beryllium production is showed to have extended technological opportunities in manufacturing semi-products (beryllium ingots, master alloys, metallic beryllium powders, beryllium oxide) and in production of structural beryllium and its parts. Ulba metallurgical plant owns a unique technology of beryllium vacuum distillation, which allows to produce reactor grades of beryllium with a low content of metallic impurities. At present Ulba plant does not depend on raw materials suppliers. The quantity of stored raw materials and semi-products will allow to provide a 25-years work of beryllium production at a full capacity. The plant has a satisfactory experience in solving ecological problems, which could be useful in ITER program. (author)

Beryllium poisonings; Les intoxications par le beryllium

Energy Technology Data Exchange (ETDEWEB)

Alibert, S.

1959-03-15

This note reports a bibliographical study of beryllium toxicity. Thus, this bibliographical review addresses and outlines aspects and issues like aetiology, cases of acute poisoning (cutaneous manifestations, pulmonary manifestations), chronic poisoning (cutaneous, pulmonary and bone manifestations), excretion and localisation, and prognosis.

The immunotoxicity of beryllium

International Nuclear Information System (INIS)

Reeves, A.L.

1983-01-01

In the disease berylliosis, granulomatous hypersensitivity is the specific immune response to tissue contact with a poorly soluble particle of beryllium compound, mediated through the accumulation and proliferation of reticuloendothelial cells. A review is given of the work accomplished since the 1950's and particularly since the 1970's to elucidate the nature and consequences of this response to beryllium and its compounds. (U.K.)

Investigation of beryllium/steam interaction

Energy Technology Data Exchange (ETDEWEB)

Chekhonadskikh, A.M.; Vurim, A.D.; Vasilyev, Yu.S.; Pivovarov, O.S. [Inst. of Atomic Energy National Nuclear Center of the Republic of Kazakstan Semipalatinsk (Kazakhstan); Shestakov, V.P.; Tazhibayeva, I.L.

1998-01-01

In this report program on investigations of beryllium emissivity and transient processes on overheated beryllium surface attacked by water steam to be carried out in IAE NNC RK within Task S81 TT 2096-07-16 FR. The experimental facility design is elaborated in this Report. (author)

Assessment of LANL beryllium waste management documentation

International Nuclear Information System (INIS)

Danna, J.G.; Jennrich, E.A.; Lund, D.M.; Davis, K.D.; Hoevemeyer, S.S.

1991-04-01

The objective of this report is to determine present status of the preparation and implementation of the various high priority documents required to properly manage the beryllium waste generated at the Laboratory. The documents being assessed are: Waste Acceptance Criteria, Waste Characterization Plan, Waste Certification Plan, Waste Acceptance Procedures, Waste Characterization Procedures, Waste Certification Procedures, Waste Training Procedures and Waste Recordkeeping Procedures. Beryllium is regulated (as a dust) under 40 CFR 261.33 as ''Discarded commercial chemical products, off specification species, container residues and spill residues thereof.'' Beryllium is also identified in the 3rd thirds ruling of June 1, 1990 as being restricted from land disposal (as a dust). The beryllium waste generated at the Laboratory is handled separately because beryllium has been identified as a highly toxic carcinogenic material

Chronic Beryllium Disease Prevention Program Report

Energy Technology Data Exchange (ETDEWEB)

Lee, S

2012-03-29

This document describes how Lawrence Livermore National Laboratory (LLNL) meets the requirements and management practices of federal regulation 10 CFR 850, 'Chronic Beryllium Disease Prevention Program (CBDPP).' This revision of the LLNL CBDPP incorporates clarification and editorial changes based on lessons learned from employee discussions, observations and reviews of Department of Energy (DOE) Complex and commercial industry beryllium (Be) safety programs. The information is used to strengthen beryllium safety practices at LLNL, particularly in the areas of: (1) Management of small parts and components; and (2) Communication of program status to employees. Future changes to LLNL beryllium activities and on-going operating experience will be incorporated into the program as described in Section S, 'Performance Feedback.'

Study on Pole Arrangement of the CEDM Coils

International Nuclear Information System (INIS)

Park, Jin Seok; Lee, Myoung Goo; Kim, Hyun Min; Cho, Yeon Ho; Choi, Taek Sang

2013-01-01

The coil stack assembly is important for reliable operation of the CEDM, there have been efforts to improve the design by optimizing the design parameters such as dimensions and winding turns. However, magnetic forces of the CEDM can also change by different pole arrangement even if their design parameters are the same. Since the latch coil and lift coil are installed connected to each other, they produce magnetically coupled field when they are energized at the same time. This coupling field can affect the magnetic force of the CEDM significantly. In this paper, coil pole arrangement effects are studied. Electro-magnetic analysis is performed for the different pole arrangements of the CEDM coils to calculate the magnetic forces. Pole arrangement effects on magnetic forces were studied by static analysis of the CEDM magnetic field. Magnetic forces were calculated and compared for the two different pole arrangements of the coils. The results show that the magnetic poles of the lift coil and latch coil shall be arranged to have the same magnetic pole direction to achieve higher magnetic force

Design and Fabrication of the KSTAR Poloidal Field Coil Structure

International Nuclear Information System (INIS)

Park, H. K.; Choi, C. H.; Sa, J. W.

2005-01-01

The KSTAR magnet system consists of 16 toroidal field(TF) coils. 4 pairs of central solenoid(CS) coils, and 3 pairs of outer poloidal field(PF) coils. The TF coils are encased in a structure to enhance mechanical stability. The CS coil structure is supported on top of the TF coil structure and supplies a vertical compression of 15 MN to prevent lateral movement due to a repulsive force between the CS coils. The PF coil system is vertically symmetry to the machine mid-plane and consists of 6 coils and 80 support structures(i.e, 16 for PF5, 32 for PF6 and 32 fort PF7). All PF coil structures should absorb the thermal contraction difference between TF coil structure and PF coils due to cool down and endure the vertical and radial magnetic forces due to current charging. In order to satisfy these structural requirements. the PF5 coil structure is designed base on hinges and both of PF6 and PF7 coil structures based on flexible plates. The PF coil structures are assembled on the TF coil structure with an individual basement that is welded on the TF coil structure

Manufacture of the Poloidal Field Conductor Insert Coil (PFCI)

International Nuclear Information System (INIS)

Baker, W.; Rajainmaeki, H.; Salpietro, E.; Keefe, C.

2006-01-01

Within the framework of the R(and)D programme for ITER (International Thermonuclear Experimental Reactor) the European team EFDA (European Fusion Development Agreement) have been charged with the design and manufacture of the Poloidal Field Conductor Insert Coil (PFCI). The purpose of the PFCI is to test and demonstrate the performance of long length full scale NbTi conductors in ITER relevant conditions. The PFCI will be tested in the Central Solenoid Model Coil test facility at the JAEA Naka Japan. This paper details the complete manufacturing details of the PFCI including development, forming machining, pre-assembly, impregnation, final assembly and testing. The PFCI is a single layer wound solenoid of 9 turns with a transition joggle in the centre section of the winding and an intermediate joint connection between the upper termination and the main coil winding. To give the required overall dimensions to fit in the testing facility, pre-formed and machined glass resin composite filler pieces are assembled with the winding and finally Vacuum Pressure Impregnated to create a single assembly unit. The PFCI is enclosed for assembly in a support structure which consist of an upper and lower flange that each are made up by 4 machined stainless steel castings which are electrically insulated by epoxy glass sheet material and 12 tie rods which preload the complete assembly in the vertical direction while the upper flange is equipped with 4 radial restraining jacks and the lower flange is equipped with 4 sets of studs and shear keys to withstand the net vertical and lateral electromagnetic forces. The PFCI is equipped with inductive heaters, voltage taps, temperature transducers, strain gauges and other instrumentation as diagnostics to monitor the performance. The current status of the manufacture is that the coil is in the process of final impregnation and should be completed and delivered before the summer of this year. (author)

Beryllium concentration in pharyngeal tonsils in children

Directory of Open Access Journals (Sweden)

Ewa Nogaj

2014-06-01

Full Text Available Power plant dust is believed to be the main source of the increased presence of the element beryllium in the environment which has been detected in the atmospheric air, surface waters, groundwater, soil, food, and cigarette smoke. In humans, beryllium absorption occurs mainly via the respiratory system. The pharyngeal tonsils are located on the roof of the nasopharynx and are in direct contact with dust particles in inhaled air. As a result, the concentration levels of beryllium in the pharyngeal tonsils are likely to be a good indicator of concentration levels in the air. The presented study had two primary aims: to investigate the beryllium concentration in pharyngeal tonsils in children living in southern Poland, and the appropriate reference range for this element in children’s pharyngeal tonsils. Pharyngeal tonsils were extracted from a total of 379 children (age 2–17 years, mean 6.2 ± 2.7 years living in southern Poland. Tonsil samples were mineralized in a closed cycle in a pressure mineralizer PDS 6, using 65% spectrally pure nitric acid. Beryllium concentration was determined using the ICP-AES method with a Perkin Elmer Optima 5300DVTM. The software Statistica v. 9 was used for the statistical analysis. It was found that girls had a significantly greater beryllium concentration in their pharyngeal tonsils than boys. Beryllium concentration varies greatly, mostly according to the place of residence. Based on the study results, the reference value for beryllium in pharyngeal tonsils of children is recommended to be determined at 0.02–0.04 µg/g.

ZPPR-20 phase D : a cylindrical assembly of polyethylene moderated U metal reflected by beryllium oxide and polyethylene.

Energy Technology Data Exchange (ETDEWEB)

Lell, R.; Grimm, K.; McKnight, R.; Shaefer, R.; Nuclear Engineering Division; INL

2006-09-30

The Zero Power Physics Reactor (ZPPR) fast critical facility was built at the Argonne National Laboratory-West (ANL-W) site in Idaho in 1969 to obtain neutron physics information necessary for the design of fast breeder reactors. The ZPPR-20D Benchmark Assembly was part of a series of cores built in Assembly 20 (References 1 through 3) of the ZPPR facility to provide data for developing a nuclear power source for space applications (SP-100). The assemblies were beryllium oxide reflected and had core fuel compositions containing enriched uranium fuel, niobium and rhenium. ZPPR-20 Phase C (HEU-MET-FAST-075) was built as the reference flight configuration. Two other configurations, Phases D and E, simulated accident scenarios. Phase D modeled the water immersion scenario during a launch accident, and Phase E (SUB-HEU-MET-FAST-001) modeled the earth burial scenario during a launch accident. Two configurations were recorded for the simulated water immersion accident scenario (Phase D); the critical configuration, documented here, and the subcritical configuration (SUB-HEU-MET-MIXED-001). Experiments in Assembly 20 Phases 20A through 20F were performed in 1988. The reference water immersion configuration for the ZPPR-20D assembly was obtained as reactor loading 129 on October 7, 1988 with a fissile mass of 167.477 kg and a reactivity of -4.626 {+-} 0.044{cents} (k {approx} 0.9997). The SP-100 core was to be constructed of highly enriched uranium nitride, niobium, rhenium and depleted lithium. The core design called for two enrichment zones with niobium-1% zirconium alloy fuel cladding and core structure. Rhenium was to be used as a fuel pin liner to provide shut down in the event of water immersion and flooding. The core coolant was to be depleted lithium metal ({sup 7}Li). The core was to be surrounded radially with a niobium reactor vessel and bypass which would carry the lithium coolant to the forward inlet plenum. Immediately inside the reactor vessel was a rhenium

Study on assembly techniques and procedures for ITER tokamak device

International Nuclear Information System (INIS)

Obara, Kenjiro; Kakudate, Satoshi; Shibanuma, Kiyoshi; Sago, Hiromi; Ue, Koichi; Shimizu, Katsusuke; Onozuka, Masanori

2006-06-01

The International Thermonuclear Experimental Reactor (ITER) tokamak is mainly composed of a doughnut-shaped vacuum vessel (VV), four types of superconducting coils such as toroidal field coils (TF coils) arranged around the VV, and in-vessel components, such as blanket and divertor. The dimensions and weight of the respective components are around a few ten-meters and several hundred-tons. In addition, the whole tokamak assembly, which are composed of these components, are roughly estimated, 26 m in diameter, 18 m in height and over 16,500 tons in total weight. On the other hand, as for positioning and assembly tolerances of the VV and the TF coil are required to be a high accuracy of ±3 mm in spite of large size and heavy weight. The assembly procedures and techniques of the ITER tokamak are therefore studied, taking account of the tolerance requirements as well as the configuration of the tokamak with large size and heavy weight. Based on the above backgrounds, the assembly procedures and techniques, which are able to assemble the tokamak with high accuracy, are described in the present report. The tokamak assembly operations are categorized into six work break down structures (WBS), i.e., (1) preparation for assembly operations, (2) sub-assembly of the 40deg sector composed of 40deg VV sector, two TF coils and thermal shield between VV and TF coil at the assembly hall, (3) completion of the doughnut-shaped tokamak assembly composed of nine 40deg sectors in the cryostat at the tokamak pit, (4) measurement of positioning and accuracy after the completion of the tokamak assembly, (5) installation of the ex-vessel components, and (6) installation of in-vessel components. In the present report, two assembly operations of (2) and (3) in the above six WBS, which are the most critical in the tokamak assembly, are mainly described. The report describes the following newly developed tokamak assembly procedures and techniques, jigs and tools for assembly and metrology

Measured Strain of Nb3Sn Coils During Excitation and Quench

International Nuclear Information System (INIS)

Caspi, S.; Bartlett, S.E.; Dietderich, D.R.; Ferracin, P.; Gourlay, S.A.; Hannaford, C.R.; Hafalia, A.R.; Lietzke, S.; Mattafirri, M.; Nyman, M.; Sabbi, G.

2005-01-01

The strain in a high field Nb 3 Sn coil was measured during magnet assembly, cool-down, excitation and spot heater quenches. Strain was measured with a full bridge strain gauge mounted directly over the turns and impregnated with the coil. Two such coils were placed in a ''common coil'' fashion capable of reaching 11T at 4.2K. The measured steady state strain in the coil is compared with results obtained using the FEM code ANSYS. During quenches, the transient strain (due to temperature rise) was also measured and compared with the calculated mechanical time response to a quench

Status of beryllium study for fusion in RF

International Nuclear Information System (INIS)

Khomutov, A.M.; Kupriyanov, I.B.; Markushkin, Yu.E.; Gervash, A.; Kolbasov, B.N.

2004-01-01

The main directions of research activities in the field of beryllium application science and technology carried out in Russia during 2001-2003 have been reviewed. The main results of these investigations have been highlighted. First wall and port-limier. The investigation on the actively cooled components with beryllium cladding is under progress objecting on the clarification of their ultimate thermo cycling capabilities. The study of behavior of bulk beryllium and the boundary region of the contact with the cooling structure under the intensive thermo cycling loading and neutron irradiation have been the object of consideration in particular. The works on the optimization and modification of industrial fabrication processes for commercial scaled production of beryllium tile were also under way. The influence of neutron irradiation. The new experimental data on the nuclear properties of several Russian beryllium grades has been obtained. The samples have been subjected to the high neutron dozes. The influence of low temperature (70-200degree C) neutron irradiation on the thermal conductivity has been examined in particular. The interrelations of the helium inventory and temperature of neutron irradiation with tritium release out of irradiated beryllium samples have been analyzed. The beryllium associated safety questions. The experiments on the modeling of normal working conditions and conditions imitating the plasma disruption events in ITER performance scenario have been continued. The new experimental information on the coefficient of pulverization of beryllium and the accumulation of deuterium in beryllium under the action of proton beam has been collected. The dependence of the reaction rate constant for the beryllium oxidation by the water vapor for different conditions has been analyzed. The compact, porous and powder beryllium samples have been tested at the wide range of temperature, pressure and duration of reaction with water vapor. The calculating

Research of flaw assessment methods for beryllium reflector elements

International Nuclear Information System (INIS)

Shibata, Akira; Ito, Masayasu; Takemoto, Noriyuki; Tanimoto, Masataka; Tsuchiya, Kunihiko; Nakatsuka, Masafumi; Ohara, Hiroshi; Kodama, Mitsuhiro

2012-02-01

Reflector elements made from metal beryllium is widely used as neutron reflectors to increase neutron flux in test reactors. When beryllium reflector elements are irradiated by neutron, bending of reflector elements caused by swelling occurs, and beryllium reflector elements must be replaced in several years. In this report, literature search and investigation for non-destructive inspection of Beryllium and experiments for Preliminary inspection to establish post irradiation examination method for research of characteristics of metal beryllium under neutron irradiation were reported. (author)

Coils in a fusion device and its fabrication method

International Nuclear Information System (INIS)

Maeda, Hideto; Moritani, Einoshin.

1975-01-01

Object: To provide a coil for nuclear fusion equipment, which coil has superior rigidity and strength and is separable into two sections and used for removing impurity ions from high temperature plasma such as heavy hydrogen and tritium. Structure: The coil according to the invention is manufactured by (1) a step of insulating horseshoe-shaped conductors one from another and bundling them into coil halves. (2) a step of assembling a flange on a coil case accommodating each coil half and hermetically welding a lid to each end of the coil half, (3) a step of evacuating the interior of each coil case, (4) a step of pouring a thermosetting resin into each evacuated coil case and hardening the resin, (5) a step of connecting the two coil halves with their ends not covered with resin held in abutting relation to each other, (6) a step of coupling coil case joint pieces to the joined portions and covering the joint pieces with a seal box and hermetically welding the box to the joint pieces, and (7) a step of pouring a thermosetting resin into each evacuated joint portion and hardening the resin. (Kamimura, M.)

Composite beryllium-ceramics breeder pin elements for a gas cooled solid blanket

International Nuclear Information System (INIS)

Carre, F.; Chevreau, G.; Gervaise, F.; Proust, E.

1986-06-01

Helium coolant have main advantages compared to water for solid blankets. But limitations exist too and the development of attractive helium cooled blankets based on breeder pin assemblies has been essentially made possible by the derivation from recent CEA neutronic studies of an optimized composite beryllium/ceramics breeder arrangement. Description of the proposed toroidal blanket layout for Net is made together with the analysis of its main performance. Merits of the considered composite Be/ceramics breeder elements are discussed

Beryllium R and D for fusion applications

International Nuclear Information System (INIS)

Scaffidi-Argentina, F.; Longhurst, G.R.; Shestakov, V.; Kawamura, H.

2000-01-01

Beryllium is one of the primary candidates as both plasma-facing material (PFM) and neutron multiplier in the next-step fusion reactors. Both sintered-product blocks and pebbles are considered in fusion reactor designs. Beryllium evaporated on carbon tiles has also been used in Joint European Torus (JET) and may be considered for other designs. Future efforts are directed toward the pebble form of beryllium. Research and evaluations of data are underway to determine the most attractive material processing approaches in terms of fabrication cost and quality; technical issues associated with heat transfer; thermal, mechanical and irradiation stability; safety and tritium release. Beryllium plasma-facing components will require periodic repair or replacement, therefore disposal or recycling of activated and tritiated beryllium will also be a concern. Beryllium as a component of the molten salt, Flibe is also being considered in novel approaches to the plasma-structure interface. This paper deals with the main issues related to the use of Be in a fusion reactor as both neutron multiplier and first wall material. These issues include potential reactions with steam during accidents and the health and environmental aspects of its use, reprocessing and reuse, or disposal

Beryllium R and D for fusion applications

Energy Technology Data Exchange (ETDEWEB)

Scaffidi-Argentina, F. E-mail: francesco.scaffidi@iket.fzk.de; Longhurst, G.R.; Shestakov, V.; Kawamura, H

2000-11-01

Beryllium is one of the primary candidates as both plasma-facing material (PFM) and neutron multiplier in the next-step fusion reactors. Both sintered-product blocks and pebbles are considered in fusion reactor designs. Beryllium evaporated on carbon tiles has also been used in Joint European Torus (JET) and may be considered for other designs. Future efforts are directed toward the pebble form of beryllium. Research and evaluations of data are underway to determine the most attractive material processing approaches in terms of fabrication cost and quality; technical issues associated with heat transfer; thermal, mechanical and irradiation stability; safety and tritium release. Beryllium plasma-facing components will require periodic repair or replacement, therefore disposal or recycling of activated and tritiated beryllium will also be a concern. Beryllium as a component of the molten salt, Flibe is also being considered in novel approaches to the plasma-structure interface. This paper deals with the main issues related to the use of Be in a fusion reactor as both neutron multiplier and first wall material. These issues include potential reactions with steam during accidents and the health and environmental aspects of its use, reprocessing and reuse, or disposal.

BERYLLIUM MEASUREMENT IN COMMERCIALLY AVAILABLE WET WIPES

Energy Technology Data Exchange (ETDEWEB)

Youmans-Mcdonald, L.

2011-02-18

Analysis for beryllium by fluorescence is now an established method which is used in many government-run laboratories and commercial facilities. This study investigates the use of this technique using commercially available wet wipes. The fluorescence method is widely documented and has been approved as a standard test method by ASTM International and the National Institute for Occupational Safety and Health (NIOSH). The procedure involves dissolution of samples in aqueous ammonium bifluoride solution and then adding a small aliquot to a basic hydroxybenzoquinoline sulfonate fluorescent dye (Berylliant{trademark} Inc. Detection Solution Part No. CH-2) , and measuring the fluorescence. This method is specific to beryllium. This work explores the use of three different commercial wipes spiked with beryllium, as beryllium acetate or as beryllium oxide and subsequent analysis by optical fluorescence. The effect of possible interfering metals such as Fe, Ti and Pu in the wipe medium is also examined.

Beryllium Measurement In Commercially Available Wet Wipes

International Nuclear Information System (INIS)

Youmans-Mcdonald, L.

2011-01-01

Analysis for beryllium by fluorescence is now an established method which is used in many government-run laboratories and commercial facilities. This study investigates the use of this technique using commercially available wet wipes. The fluorescence method is widely documented and has been approved as a standard test method by ASTM International and the National Institute for Occupational Safety and Health (NIOSH). The procedure involves dissolution of samples in aqueous ammonium bifluoride solution and then adding a small aliquot to a basic hydroxybenzoquinoline sulfonate fluorescent dye (Berylliant(trademark) Inc. Detection Solution Part No. CH-2) , and measuring the fluorescence. This method is specific to beryllium. This work explores the use of three different commercial wipes spiked with beryllium, as beryllium acetate or as beryllium oxide and subsequent analysis by optical fluorescence. The effect of possible interfering metals such as Fe, Ti and Pu in the wipe medium is also examined.

Beryllium dust generation resulting from plasma bombardment

International Nuclear Information System (INIS)

Doerner, R.; Mays, C.

1997-01-01

The beryllium dust resulting from erosion of beryllium samples subjected to plasma bombardment has been measured in PISCES-B. Loose surface dust was found to be uniformly distributed throughout the device and accounts for 3% of the eroded material. A size distribution measurement of the loose surface dust shows an increasing number of particles with decreasing diameter. Beryllium coatings on surfaces with a line of sight view of the target interaction region account for an additional 33% of the eroded beryllium material. Flaking of these surface layers is observed and is thought to play a significant role in dust generation inside the vacuum vessel. (orig.)

Investigations of the ternary system beryllium-carbon-tungsten and analyses of beryllium on carbon surfaces

International Nuclear Information System (INIS)

Kost, Florian

2009-01-01

Beryllium, carbon and tungsten are planned to be used as first wall materials in the future fusion reactor ITER. The aim of this work is a characterization of mixed material formation induced by thermal load. To this end, model systems (layers) were prepared and investigated, which give insight into the basic physical and chemical concepts. Before investigating ternary systems, the first step was to analyze the binary systems Be/C and Be/W (bottom-up approach), where the differences between the substrates PG (pyrolytic graphite) and HOPG (highly oriented pyrolytic graphite) were of special interest. Particularly X-ray photoelectron spectroscopy (XPS), low energy ion scattering (ISS) and Rutherford backscattering spectroscopy (RBS) were used as analysis methods. Beryllium evaporated on carbon shows an island growth mode, whereas a closed layer can be assumed for layer thicknesses above 0.7 nm. Annealing of the Be/C system induces Be 2 C island formation for T≥770 K. At high temperatures (T≥1170 K), beryllium carbide dissociates, resulting in (metallic) beryllium desorption. For HOPG, carbide formation starts at higher temperatures compared to PG. Activation energies for the diffusion processes were determined by analyzing the decreasing beryllium amount versus annealing time. Surface morphologies were characterized using angle-resolved XPS (ARXPS) and atomic force microscopy (AFM). Experiments were performed to study processes in the Be/W system in the temperature range from 570 to 1270 K. Be 2 W formation starts at 670 K, a complete loss of Be 2 W is observed at 1170 K due to dissociation (and subsequent beryllium desorption). Regarding ternary systems, particularly Be/C/W and C/Be/W were investigated, attaching importance to layer thickness (reservoir) variations. At room temperature, Be 2 C, W 2 C, WC and Be 2 W formation at the respective interfaces was observed. Further Be 2 C is forming with increasing annealing temperatures. Depending on the layer

Technical issues for beryllium use in fusion blanket applications

International Nuclear Information System (INIS)

McCarville, T.J.; Berwald, D.H.; Wolfer, W.; Fulton, F.J.; Lee, J.D.; Maninger, R.C.; Moir, R.W.; Beeston, J.M.; Miller, L.G.

1985-01-01

Beryllium is an excellent non-fissioning neutron multiplier for fusion breeder and fusion electric blanket applications. This report is a compilation of information related to the use of beryllium with primary emphasis on the fusion breeder application. Beryllium resources, production, fabrication, properties, radiation damage and activation are discussed. A new theoretical model for beryllium swelling is presented

Production of beryllium oxide of nuclear purity from beryl

Energy Technology Data Exchange (ETDEWEB)

Copat, A; Sood, S P

1984-01-01

Production of beryllium oxide from beryl by the fluoride process was optimized in this study. Optimum results were obtained using a mixture of sodium hexafluorsilicate and sodium hexafluorferrate as flux and calcinating at 740/sup 0/C for 2 hours. The beryllium concentrate produced was further purified by crystallization as beryllium sulfate to obtain nuclear grade beryllium oxide

Production of beryllium oxide of nuclear purity from beryl

International Nuclear Information System (INIS)

Copat, A.; Sood, S.P.

1983-01-01

Production of beryllium oxide from beryl by the fluoride process was optimized in this study. Optimum results were obtained using a mixture of sodium hexafluorsilicate and sodium hexafluorferrate as flux and calcinating at 740 0 C for 2 hours. The beryllium concentrate produced was further purified by crystallization as beryllium sulfate to obtain nuclear grade beryllium oxide (Author) [pt

Mechanical performance of irradiated beryllium pebbles

Energy Technology Data Exchange (ETDEWEB)

Scaffidi-Argentina, F.; Dalle-Donne, M.; Werle, H. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reaktortechnik

1998-01-01

For the Helium Cooled Pebble Bed (HCPB) Blanket, which is one of the two reference concepts studied within the European Fusion Technology Programme, the neutron multiplier consists of a mixed bed of about 2 and 0.1-0.2 mm diameter beryllium pebbles. Beryllium has no structural function in the blanket, however microstructural and mechanical properties are important, as they might influence the material behavior under neutron irradiation. The EXOTIC-7 as well as the `Beryllium` experiments carried out in the HFR reactor in Petten are considered as the most detailed and significant tests for investigating it. This paper reviews the present status of beryllium post-irradiation examinations performed at the Forschungszentrum Karlsruhe with samples from these irradiation experiments, emphasizing the effects of irradiation of essential material properties and trying to elucidate the processes controlling the property changes. The microstructure, the porosity distribution, the impurity content, the behavior under compression loads and the compatibility of the beryllium pebbles with lithium orthosilicate (Li{sub 4}SiO{sub 4}) during the in-pile irradiation are presented and critically discussed. Qualitative information on ductility and creep obtained by hardness-type measurements are also supplied. (author)

Design considerations in coiled-coil fusion constructs for the structural determination of a problematic region of the human cardiac myosin rod

Energy Technology Data Exchange (ETDEWEB)

Andreas, Michael P.; Ajay, Gautam; Gellings, Jaclyn A.; Rayment, Ivan (UW)

2017-12-01

X-ray structural determination of segments of the myosin rod has proved difficult because of the strong salt-dependent aggregation properties and repeating pattern of charges on the surface of the coiled-coil that lead to the formation of paracrystals. This problem has been resolved in part through the use of globular assembly domains that improve protein folding and prevent aggregation. The primary consideration now in designing coiled-coil fusion constructs for myosin is deciding where to truncate the coiled-coil and which amino acid residues to include from the folding domain. This is especially important for myosin that contains numerous regions of low predicted coiled-coil propensity. Here we describe the strategy adopted to determine the structure of the region that extends from Arg1677 – Leu1797 that included two areas that do not show a strong sequence signature of a conventional left-handed coiled coil or canonical heptad repeat. This demonstrates again that, with careful choice of fusion constructs, overlapping structures exhibit very similar conformations for the myosin rod fragments in the canonical regions. However, conformational variability is seen around Leu1706 which is a hot spot for cardiomyopathy mutations suggesting that this might be important for function.

Preliminary results for explosion bonding of beryllium to copper

International Nuclear Information System (INIS)

Butler, D.J.; Dombrowski, D.E.

1995-01-01

This program was undertaken to determine if explosive bonding is a viable technique for joining beryllium to copper substrates. The effort was a cursory attempt at trying to solve some of the problems associated with explosive bonding beryllium and should not be considered a comprehensive research effort. There are two issues that this program addressed. Can beryllium be explosive bonded to copper substrates and can the bonding take place without shattering the beryllium? Thirteen different explosive bonding iterations were completed using various thicknesses of beryllium that were manufactured with three different techniques

Preliminary proposal for a beryllium technology program for fusion applications

International Nuclear Information System (INIS)

1985-02-01

The program was designed to provide the answers to the critical issues of beryllium technology needed in fusion blanket designs. The four tasks are as follows: (1) Beryllium property measurements needed for fusion data base. (2) Beryllium stress relaxation and creep measurements for lifetime modelling calculations. (3) Simplified recycle technique development for irradiated beryllium. (4) Beryllium neutron multiplier measurements using manganese bath absolute calibration techniques

The status of beryllium technology for fusion

Energy Technology Data Exchange (ETDEWEB)

Scaffidi-Argentina, F.; Longhurst, G.R. E-mail: gx1@inel.gov; Shestakov, V.; Kawamura, H

2000-12-01

Beryllium was used for a number of years in the Joint European Torus (JET), and it is planned to be used extensively on the lower heat-flux surfaces of the reduced technical objective/reduced cost international thermonuclear experimental reactor (RTO/RC ITER). It has been included in various forms in a number of tritium breeding blanket designs. There are technical advantages but also a number of safety issues associated with the use of beryllium. Research in a variety of technical areas in recent years has revealed interesting issues concerning the use of beryllium in fusion. Progress in this research has been presented at a series of International Workshops on Beryllium Technology for Fusion. The most recent workshop was held in Karlsruhe, Germany on 15-17 September 1999. In this paper, a summary of findings presented there and their implications for the use of beryllium in the development of fusion reactors are presented.

The status of beryllium technology for fusion

International Nuclear Information System (INIS)

Scaffidi-Argentina, F.; Longhurst, G.R.; Shestakov, V.; Kawamura, H.

2000-01-01

Beryllium was used for a number of years in the Joint European Torus (JET), and it is planned to be used extensively on the lower heat-flux surfaces of the reduced technical objective/reduced cost international thermonuclear experimental reactor (RTO/RC ITER). It has been included in various forms in a number of tritium breeding blanket designs. There are technical advantages but also a number of safety issues associated with the use of beryllium. Research in a variety of technical areas in recent years has revealed interesting issues concerning the use of beryllium in fusion. Progress in this research has been presented at a series of International Workshops on Beryllium Technology for Fusion. The most recent workshop was held in Karlsruhe, Germany on 15-17 September 1999. In this paper, a summary of findings presented there and their implications for the use of beryllium in the development of fusion reactors are presented

Ion beam assisted deposition of metal-coatings on beryllium

International Nuclear Information System (INIS)

Tashlykov, I.S.; Tul'ev, V.V.

2015-01-01

Thin films were applied on beryllium substrates on the basis of metals (Cr, Ti, Cu and W) with method of the ion-assisted deposition in vacuum. Me/Be structures were prepared using 20 kV ions irradiation during deposition on beryllium neutral fraction generated from vacuum arc plasma. Rutherford back scattering and computer simulation RUMP code were applied to investigate the composition of the modified beryllium surface. Researches showed that the superficial structure is formed on beryllium by thickness ~ 50-60 nm. The covering composition includes atoms of the deposited metal (0.5-3.3 at. %), atoms of technological impurity carbon (0.8-1.8 at. %) and oxygen (6.3-9.9 at. %), atoms of beryllium from the substrate. Ion assisted deposition of metals on beryllium substrate is accompanied by radiation enhanced diffusion of metals, oxygen atoms in the substrate, out diffusion of beryllium, carbon atoms in the deposited coating and sputtering film-forming ions assists. (authors)

Beryllium processing technology review for applications in plasma-facing components

Energy Technology Data Exchange (ETDEWEB)

Castro, R.G.; Jacobson, L.A.; Stanek, P.W.

1993-07-01

Materials research and development activities for the International Thermonuclear Experimental Reactor (ITER), i.e., the next generation fusion reactor, are investigating beryllium as the first-wall containment material for the reactor. Important in the selection of beryllium is the ability to process, fabricate and repair beryllium first-wall components using existing technologies. Two issues that will need to be addressed during the engineering design activity will be the bonding of beryllium tiles in high-heat-flux areas of the reactor, and the in situ repair of damaged beryllium tiles. The following review summarizes the current technology associated with welding and joining of beryllium to itself and other materials, and the state-of-the-art in plasma-spray technology as an in situ repair technique for damaged beryllium tiles. In addition, a review of the current status of beryllium technology in the former Soviet Union is also included.

Beryllium processing technology review for applications in plasma-facing components

International Nuclear Information System (INIS)

Castro, R.G.; Jacobson, L.A.; Stanek, P.W.

1993-07-01

Materials research and development activities for the International Thermonuclear Experimental Reactor (ITER), i.e., the next generation fusion reactor, are investigating beryllium as the first-wall containment material for the reactor. Important in the selection of beryllium is the ability to process, fabricate and repair beryllium first-wall components using existing technologies. Two issues that will need to be addressed during the engineering design activity will be the bonding of beryllium tiles in high-heat-flux areas of the reactor, and the in situ repair of damaged beryllium tiles. The following review summarizes the current technology associated with welding and joining of beryllium to itself and other materials, and the state-of-the-art in plasma-spray technology as an in situ repair technique for damaged beryllium tiles. In addition, a review of the current status of beryllium technology in the former Soviet Union is also included

Beryllium-aluminum alloys for investment castings

International Nuclear Information System (INIS)

Nachtrab, W.T.; Levoy, N.

1997-01-01

Beryllium-aluminum alloys containing greater than 60 wt % beryllium are very favorable materials for applications requiring light weight and high stiffness. However, when produced by traditional powder metallurgical methods, these alloys are expensive and have limited applications. To reduce the cost of making beryllium-aluminum components, Nuclear Metals Inc. (NMI) and Lockheed Martin Electronics and Missiles have recently developed a family of patented beryllium-aluminum alloys that can be investment cast. Designated Beralcast, the alloys can achieve substantial weight savings because of their high specific strength and stiffness. In some cases, weight has been reduced by up to 50% over aluminum investment casting. Beralcast is now being used to make thin wall precision investment castings for several advanced aerospace applications, such as the RAH-66 Comanche helicopter and F-22 jet fighter. This article discusses alloy compositions, properties, casting method, and the effects of cobalt additions on strength

Microstructure Analysis on Beryllium Reflector Blocks of Research Reactors

Energy Technology Data Exchange (ETDEWEB)

Kang, Suk Hoon; Jang, Jin Sung; Jeong, Yong Hwan; Han, Chang Hee; Jung, Yang Il; Kim, Tae Kyu [Korea Atomic Energy Research Institute, Daejeon (Korea, Republic of); Choi, Yong Seok; Oh, Kyu Hwan [Seoul National University, Seoul (Korea, Republic of)

2012-05-15

A pure beryllium has a very low mass absorption coefficient: it has been used as the reflector element material in research reactors. The lifetime of beryllium reflector elements usually determined by the swelling: the swelling leads to dimensional change in the reflector frame, which results in bending or cracking of the parts. The mechanical interference in between parts should be avoided; the anisotropy of beryllium also needs to be considered. A beryllium has hexagonal close-pack (HCP) crystal structure, which is inherently anisotropic. It has virtually no ductility in one direction. There are two main aspects in the manufacturing of beryllium which will affect its isotropy, and those are the powder morphology and the consolidation process. Powder metallurgy permits the material to be produced in isotropic and fine-grained form, which overcomes the crystal structure problem by distributing loads in low ductility oriented grains to high ductility oriented grains. There are three representative consolidating methods to make beryllium reflector blocks. Traditionally, most powder-derived grades of beryllium have been consolidated by vacuum hot-pressing (VHP). A column of loose beryllium powder is compacted under vacuum by the pressure of the opposed upper and lower punches, bringing the billet to final density. The VHP process is directional in nature: it contributes to the anisotropy of the material properties. Another consolidating method for beryllium powder is hot isostatic pressing (HIPing), which will enhance its isotropy. During HIPing, The argon gas exerts pressure uniformly in all directions on the can containing the beryllium powder. The HIP process is effective to improve the isotropy of the resulting material as well as refinement of grain sizes. The last consolidating method is hot extrusion (HE). A roughly close packed beryllium is subjected to severe plastic defomation, the grains are refined and the tensile strength is enhanced. Since the material

Safety handling of beryllium for fusion technology R and D

International Nuclear Information System (INIS)

Yoshida, Hiroshi; Okamoto, Makoto; Terai, Takayuki; Odawara, Osamu; Ashibe, Kusuo; Ohara, Atsushi.

1992-07-01

Feasibility of beryllium use as a blanket neutron multiplier, first wall and plasma facing material has been studied for the D-T burning experiment reactors such as ITER. Various experimental work of beryllium and its compounds will be performed under the conditions of high temperature and high energy particle exposure simulating fusion reactor conditions. Beryllium is known as a hazardous substance and its handling has been carefully controlled by various health and safe guidances and/or regulations in many countries. Japanese regulations for hazardous substance provide various guidelines on beryllium for the protection of industrial workers and environment. This report was prepared for the safe handling of beryllium in a laboratory scale experiments for fusion technology R and D such as blanket development. Major items in this report are; (1) Brief review of guidances and regulations in USA, UK and Japan. (2) Safe handling and administration manuals at beryllium facilities in INEL, LANL and JET. (3) Conceptual design study of beryllium handling facility for small to mid-scale blanket R and D. (4) Data on beryllium toxicity, example of clinical diagnosis of beryllium disease, and environmental occurence of beryllium. (5) Personnel protection tools of Japanese Industrial Standard for hazardous substance. (author) 61 refs

Hydrogen transport behavior of beryllium

Energy Technology Data Exchange (ETDEWEB)

Anderl, R.A.; Hankins, M.R.; Longhurst, G.R.; Pawelko, R.J. (Idaho National Engineering Lab., EG and G Idaho, Inc., Idaho Falls, ID (United States)); Macaulay-Newcombe, R.G. (Dept. of Engineering Physics, Univ. Hamilton, ON (Canada))

1992-12-01

Beryllium is being evaluated for use as a plasma-facing material in the International Thermonuclear Experimental Reactor (ITER). One concern in the evaluation is the retention and permeation of tritium implanted into the plasma-facing surface. We performed laboratory-scale studies to investigate mechanisms that influence hydrogen transport and retention in beryllium foil specimens of rolled powder metallurgy product and rolled ingot cast beryllium. Specimen characterization was accomplished using scanning electron microscopy. Auger electron spectroscopy, and Rutherford backscattering spectrometry (RBS) techniques. Hydrogen transport was investigated using ion-beam permeation experiments and nuclear reaction analysis (NRA). Results indicate that trapping plays a significant role in permeation, re-emission, and retention, and that surface processes at both upstream and downstream surfaces are also important. (orig.).

Characterization of plasma sprayed beryllium ITER first wall mockups

Energy Technology Data Exchange (ETDEWEB)

Castro, R.G.; Vaidya, R.U.; Hollis, K.J. [Los Alamos National Lab., NM (United States). Material Science and Technology Div.

1998-01-01

ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/m{sup 2} without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface. (author)

Characterization of Plasma Sprayed Beryllium ITER First Wall Mockups

International Nuclear Information System (INIS)

Castro, Richard G.; Vaidya, Rajendra U.; Hollis, Kendall J.

1997-10-01

ITER first wall beryllium mockups, which were fabricated by vacuum plasma spraying the beryllium armor, have survived 3000 thermal fatigue cycles at 1 MW/sq m without damage during high heat flux testing at the Plasma Materials Test Facility at Sandia National Laboratory in New Mexico. The thermal and mechanical properties of the plasma sprayed beryllium armor have been characterized. Results are reported on the chemical composition of the beryllium armor in the as-deposited condition, the through thickness and normal to the through thickness thermal conductivity and thermal expansion, the four-point bend flexure strength and edge-notch fracture toughness of the beryllium armor, the bond strength between the beryllium armor and the underlying heat sink material, and ultrasonic C-scans of the Be/heat sink interface

Thermo hydraulic and quench propagation characteristics of SST-1 TF coil

Energy Technology Data Exchange (ETDEWEB)

Sharma, A.N., E-mail: ansharma@ipr.res.in [Institute for Plasma Research, Gandhinagar (India); Pradhan, S. [Institute for Plasma Research, Gandhinagar (India); Duchateau, J.L. [CEA Cadarache, 13108 St Paul lez Durance Cedex (France); Khristi, Y.; Prasad, U.; Doshi, K.; Varmora, P.; Patel, D.; Tanna, V.L. [Institute for Plasma Research, Gandhinagar (India)

2014-02-15

Highlights: • Details of SST-1 TF coils, CICC. • Details of SST-1 TF coil cold test. • Quench analysis of TF magnet. • Flow changes following quench. • Predictive analysis of assembled magnet system. - Abstract: SST-1 toroidal field (TF) magnet system is comprising of sixteen superconducting modified ‘D’ shaped TF coils. During single coil test campaigns spanning from June 10, 2010 till January 24, 2011; the electromagnetic, thermal hydraulic and mechanical performances of each TF magnet have been qualified at its respective nominal operating current of 10,000 A in either two-phase or supercritical helium cooling conditions. During the current charging experiments, few quenches have initiated either as a consequence of irrecoverable normal zones or being induced in some of the TF magnets. Quench evolution in the TF coils have been analyzed in detail in order to understand the thermal hydraulic and quench propagation characteristics of the SST-1 TF magnets. The same were also simulated using 1D code Gandalf. This paper elaborates the details of the analyses and the quench simulation results. A predictive quench propagation analysis of 16 assembled TF magnets system has also been reported in this paper.

Globally optimal superconducting magnets part II: symmetric MSE coil arrangement.

Science.gov (United States)

Tieng, Quang M; Vegh, Viktor; Brereton, Ian M

2009-01-01

A globally optimal superconducting magnet coil design procedure based on the Minimum Stored Energy (MSE) current density map is outlined. The method has the ability to arrange coils in a manner that generates a strong and homogeneous axial magnetic field over a predefined region, and ensures the stray field external to the assembly and peak magnetic field at the wires are in acceptable ranges. The outlined strategy of allocating coils within a given domain suggests that coils should be placed around the perimeter of the domain with adjacent coils possessing alternating winding directions for optimum performance. The underlying current density maps from which the coils themselves are derived are unique, and optimized to possess minimal stored energy. Therefore, the method produces magnet designs with the lowest possible overall stored energy. Optimal coil layouts are provided for unshielded and shielded short bore symmetric superconducting magnets.

Productive international collaboration in the large coil task

International Nuclear Information System (INIS)

Haubenreich, P.N.; Komarek, P.; Shimamoto, S.; Vecsey, G.

1987-01-01

The Large Coil Task (LCT), initiated in 1977, has been very productive of useful technical information about superconducting toroidal field (TF) coil design and manufacture. Moreover, it has demonstrated close international collaboration in fusion technology development, including integration of large components built in four different countries. Each of six 40-t test coils was designed and produced by a major industrial team, with government laboratory guidance, to a common set of specifications. The six were assembled into a toroidal array for testing in the International Fusion Superconducting Magnet Test Facility (IFSMTF) at Oak Ridge. Testing was done by a team of representatives of EURATOM, Japan, Switzerland, and the United States, with each participant having full access to all data. Coils were thoroughly instrumented, enabling penetrating analysis of behavior

Implanted Deuterium Retention and Release in Carbon-Coated Beryllium

Science.gov (United States)

Anderl, R. A.; Longhurst, G. R.; Pawelko, R. J.; Oates, M. A.

1997-06-01

Deuterium implantation experiments have been conducted on samples of clean and carbon-coated beryllium. These studies entailed preparation and characterization of beryllium samples coated with carbon thicknesses of 100, 500, and 1000 Å. Heat treatment of a beryllium sample coated with carbon to a thickness of approximately 100 Å revealed that exposure to a temperature of 400°C under high vacuum conditions was sufficient to cause substantial diffusion of beryllium through the carbon layer, resulting in more beryllium than carbon at the surface. Comparable concentrations of carbon and beryllium were observed in the bulk of the coating layer. Higher than expected oxygen levels were observed throughout the coating layer as well. Samples were exposed to deuterium implantation followed by thermal desorption without exposure to air. Differences were observed in deuterium retention and postimplantation release behavior in the carbon-coated samples as compared with bare samples. For comparable implantation conditions (sample temperature of 400°C and an incident deuterium flux of approximately 6 × 1019 D/m2-s), the quantity of deuterium retained in the bare sample was less than that retained in the carbon-coated samples. Further, the release of the deuterium took place at lower temperatures for the bare beryllium surfaces than for carbon-coated beryllium samples.

MEASUREMENTS OF THE PROPERTIES OF BERYLLIUM FOIL

International Nuclear Information System (INIS)

ZHAO, Y.; WANG, H.

2000-01-01

The electrical conductivity of beryllium at radio frequency (800 MHz) and liquid nitrogen temperature were investigated and measured. This summary addresses a collection of beryllium properties in the literature, an analysis of the anomalous skin effect, the test model, the experimental setup and improvements, MAFIA simulations, the measurement results and data analyses. The final results show that the conductivity of beryllium is not as good as indicated by the handbook, yet very close to copper at liquid nitrogen temperature

Low resolution crystal structure of Arenicola erythrocruorin: influence of coiled coils on the architecture of a megadalton respiratory protein.

Science.gov (United States)

Royer, William E; Omartian, Michael N; Knapp, James E

2007-01-05

Annelid erythrocruorins are extracellular respiratory complexes assembled from 180 subunits into hexagonal bilayers. Cryo-electron microscopic experiments have identified two different architectural classes. In one, designated type I, the vertices of the two hexagonal layers are partially staggered, with one hexagonal layer rotated by about 16 degrees relative to the other layer, whereas in the other class, termed type II, the vertices are essentially eclipsed. We report here the first crystal structure of a type II erythrocruorin, that from Arenicola marina, at 6.2 A resolution. The structure reveals the presence of long continuous triple-stranded coiled-coil "spokes" projecting towards the molecular center from each one-twelfth unit; interdigitation of these spokes provides the only contacts between the two hexagonal layers of the complex. This arrangement contrasts with that of a type I erythrocruorin from Lumbricus terrestris in which the spokes are broken into two triple-stranded coiled coils with a disjointed connection. The disjointed connection allows formation of a more compact structure in the type I architecture, with the two hexagonal layers closer together and additional extensive contacts between the layers. Comparison of sequences of the coiled-coil regions of various linker subunits shows that the linker subunits from type II erythrocruorins possess continuous heptad repeats, whereas a sequence gap places these repeats out of register in the type I linker subunits, consistent with a disjointed coiled-coil arrangement.

Preparation of a sinterable beryllium oxide through decomposition of beryllium hydroxide (1963)

International Nuclear Information System (INIS)

Bernier, M.

1963-01-01

In the course of the present study, we have attempted to precise the factors which among the ones effective in the course of the preparation of the beryllium hydroxide and oxide and during the sintering have an influence on the final result: the density and homogeneity of the sintered body. Of the several varieties of hydroxides precipitated from a sulfate solution the β-hydroxide only is always contaminated with beryllium sulfate and cannot be purified even by thorough washing. We noticed that those varieties of the hydroxide (gel, α, β) have different decomposition rates; this behaviour is used to identify and even to dose the different species in (α, β) mixtures. The various hydroxides transmit to the resulting oxides the shape they had when precipitated. Accordingly the history of the oxide is revealed by its behaviour during its fabrication and sintering. By comparing the results of the sintering operation with the various measurements performed on the oxide powders we are led to the conclusion that an oxide obtained from beryllium hydroxide is sinterable under vacuum if the following conditions are fulfilled: the particle size must lie between 0.1 and 0.2 μ and the BeSO 4 content of the powder must be less than 0.25 per cent wt (expressed as SO 3 /BeO). The best fitting is obtained with the oxide issued from an α-hydroxide precipitated as very small aggregates and with a low sulfur-content. We have observed that this is also the case for the oxide obtained by direct calcination of beryllium sulfate. (author) [fr

Beryllium poisonings

International Nuclear Information System (INIS)

Alibert, S.

1959-03-01

This note reports a bibliographical study of beryllium toxicity. Thus, this bibliographical review addresses and outlines aspects and issues like aetiology, cases of acute poisoning (cutaneous manifestations, pulmonary manifestations), chronic poisoning (cutaneous, pulmonary and bone manifestations), excretion and localisation, and prognosis

Thermogravimetric analysis of the beryllium/steam reaction

Energy Technology Data Exchange (ETDEWEB)

Druyts, Frank E-mail: fdruyts@sckcen.be; Iseghem, Pierre van

2000-11-01

In view of the safety assessment of new fusion reactor designs, kinetic data are needed on the beryllium/steam reaction. Therefore, thermogravimetric analysis was used to determine the reactivity of beryllium in steam as a function of temperature, irradiation history and porosity of the samples. To this purpose, reference unirradiated S-200 VHP beryllium samples were compared with specimens irradiated in the BR2 reactor up to fast neutron fluences (E>1 MeV) of respectively 1.6x10{sup 21} n cm{sup -2} (resulting in a helium content of 300 appm He and a theoretical density of 99.9%) and 4x10{sup 22} n cm{sup -2} (21000 appm He, 97.2% theoretical density). Kinetics were parabolic for all tested beryllium types at 600 deg. C. At 700 deg. C, kinetics were parabolic for the unirradiated and irradiated 99.9% dense beryllium, and accelerating/linear for the irradiated 97.2% material. At 800 deg. C, all samples showed accelerating/linear behaviour. There was no influence of porosity on the reaction rate of beryllium in steam within the limited investigated density range, except at 700 deg. C, where the measured reaction rate for the irradiated 97.2% dense samples is an order of magnitude higher than for the irradiated 99.9% dense specimens.

Tritium release from neutron irradiated beryllium pebbles

Energy Technology Data Exchange (ETDEWEB)

Scaffidi-Argentina, F.; Werle, H. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reactortechnik

1998-01-01

One of the most important open issues related to beryllium for fusion applications refers to the kinetics of the tritium release as a function of neutron fluence and temperature. The EXOTIC-7 as well as the `Beryllium` experiments carried out in the HFR reactor in Petten are considered as the most detailed and significant tests for investigating the beryllium response under neutron irradiation. This paper reviews the present status of beryllium post-irradiation examinations performed at the Forschungszentrum Karlsruhe with samples from the above mentioned irradiation experiments, trying to elucidate the tritium release controlling processes. In agreement with previous studies it has been found that release starts at about 500-550degC and achieves a maximum at about 700-750degC. The observed release at about 500-550degC is probably due to tritium escaping from chemical traps, while the maximum release at about 700-750degC is due to tritium escaping from physical traps. The consequences of a direct contact between beryllium and ceramics during irradiation, causing tritium implanting in a surface layer of beryllium up to a depth of about 40 mm and leading to an additional inventory which is usually several times larger than the neutron-produced one, are also presented and the effects on the tritium release are discussed. (author)

Mechanical behavior of the ATLAS B0 model coil

CERN Document Server

Foussat, A; Acerbi, E; Alessandria, F; Berthier, R; Broggi, F; Daël, A; Dudarev, A; Mayri, C; Miele, P; Reytier, M; Rossi, L; Sorbi, M; Sun, Z; ten Kate, H H J; Vanenkov, I; Volpini, G

2002-01-01

The ATLAS B0 model coil has been developed and constructed to verify the design parameters and the manufacture techniques of the Barrel Toroid coils (BT) that are under construction for the ATLAS Detector. Essential for successful operation is the mechanical behavior of the superconducting coil and its support structure. In the ATLAS magnet test facility, a magnetic mirror is used to reproduce in the model coil the electromagnetic forces of the BT coils when assembled in the final Barrel Toroid magnet system. The model coil is extensively equipped with mechanical instrumentation to monitor stresses and force levels as well as contraction during a cooling down and excitation up to nominal current. The installed set up of strain gauges, position sensors and capacitive force transducers is presented. Moreover the first mechanical results in terms of expected main stress, strain and deformation values are presented based on detailed mechanical analysis of the design. (7 refs).

Nanostructure of self-assembled rod-coil block copolymer films for photovoltaic applications

International Nuclear Information System (INIS)

Heiser, T.; Adamopoulos, G.; Brinkmann, M.; Giovanella, U.; Ould-Saad, S.; Brochon, C.; Wetering, K. van de; Hadziioannou, G.

2006-01-01

The nanostructures of a series of rod-coil block copolymers, designed for photovoltaic applications, are studied by atomic force microscopy and transmission electron microscopy. The copolymers are composed of a semiconducting poly-p-phenylenevinylene rod with (2'-ethyl)-hexyloxy side chains and a functionalized coil block of various length and flexibility. Both, as deposited and annealed block copolymer films were investigated. The results show that highly ordered structures are only obtained if the coil block is characterized by a glass transition temperature which is significantly lower than the melting temperature of the alkyl side chains. For this material a high molecular mobility and strong driving force for crystallization of the rigid block can be achieved simultaneously. For the smallest coil to rod length ratio, we found a lamellar morphology with perpendicularly oriented lamellae with respect to the substrate. Electron diffraction data show the presence of a periodical molecular arrangement with a characteristic distance of 0.94 nm that is attributed to the distance between conjugated chains separated by the layers of alkyl sidechains

Nanostructure of self-assembled rod-coil block copolymer films for photovoltaic applications

Energy Technology Data Exchange (ETDEWEB)

Heiser, T. [Institut d' Electronique du Solide et des Systemes (InESS), CNRS/ULP, 23, rue du Loess, F-67037 Strasbourg Cedex 2 (France)]. E-mail: Thomas.Heiser@iness.c-strasbourg.fr; Adamopoulos, G. [Laboratoire d' Ingenierie des Polymeres pour les Hautes Technologies (LIPHT), Ecole Europeenne de Chimie Polymeres et Materiaux (ECPM), 25, rue Becquerel, F-67087 Strasbourg Cedex 2 (France); Brinkmann, M. [Institut Charles Sadron (ICS), CNRS, 6, rue Boussingault, F-67083 Strasbourg Cedex (France); Giovanella, U. [Laboratoire d' Ingenierie des Polymeres pour les Hautes Technologies (LIPHT), Ecole Europeenne de Chimie Polymeres et Materiaux (ECPM), 25, rue Becquerel, F-67087 Strasbourg Cedex 2 (France); Ould-Saad, S. [Institut d' Electronique du Solide et des Systemes (InESS), CNRS/ULP, 23, rue du Loess, F-67037 Strasbourg Cedex 2 (France); Brochon, C. [Laboratoire d' Ingenierie des Polymeres pour les Hautes Technologies (LIPHT), Ecole Europeenne de Chimie Polymeres et Materiaux (ECPM), 25, rue Becquerel, F-67087 Strasbourg Cedex 2 (France); Wetering, K. van de [Laboratoire d' Ingenierie des Polymeres pour les Hautes Technologies (LIPHT), Ecole Europeenne de Chimie Polymeres et Materiaux (ECPM), 25, rue Becquerel, F-67087 Strasbourg Cedex 2 (France); Hadziioannou, G. [Laboratoire d' Ingenierie des Polymeres pour les Hautes Technologies (LIPHT), Ecole Europeenne de Chimie Polymeres et Materiaux (ECPM), 25, rue Becquerel, F-67087 Strasbourg Cedex 2 (France)

2006-07-26

The nanostructures of a series of rod-coil block copolymers, designed for photovoltaic applications, are studied by atomic force microscopy and transmission electron microscopy. The copolymers are composed of a semiconducting poly-p-phenylenevinylene rod with (2'-ethyl)-hexyloxy side chains and a functionalized coil block of various length and flexibility. Both, as deposited and annealed block copolymer films were investigated. The results show that highly ordered structures are only obtained if the coil block is characterized by a glass transition temperature which is significantly lower than the melting temperature of the alkyl side chains. For this material a high molecular mobility and strong driving force for crystallization of the rigid block can be achieved simultaneously. For the smallest coil to rod length ratio, we found a lamellar morphology with perpendicularly oriented lamellae with respect to the substrate. Electron diffraction data show the presence of a periodical molecular arrangement with a characteristic distance of 0.94 nm that is attributed to the distance between conjugated chains separated by the layers of alkyl sidechains.

Effect of machining damage on tensile properties of beryllium

International Nuclear Information System (INIS)

Hanafee, J.E.

1976-01-01

It is well established that damage introduced at the surface of beryllium during machining operations can lower its mechanical properties. Tensile tests were conducted to illustrate this on beryllium presently being used for parts in the W79 program and similar to the new powder-processed beryllium specified for production (tentative specification MEL 76-001319). The objective of this study is to quantitatively illuminate the importance of controlling machining damage in this particular grade of powder-processed beryllium

Sintering of beryllium oxide

International Nuclear Information System (INIS)

Caillat, R.; Pointud, R.

1955-01-01

This study had for origin to find a process permitting to manufacture bricks of beryllium oxide of pure nuclear grade, with a density as elevated as possible and with standardized shape. The sintering under load was the technique kept for the manufacture of the bricks. Because of the important toxicity of the beryllium oxide, the general features for the preliminary study of the sintering, have been determined while using alumina. The obtained results will be able to act as general indication for ulterior studies with sintering under load. (M.B.) [fr

Managing health effects of beryllium exposure

National Research Council Canada - National Science Library

Committee on Beryllium Alloy Exposures; Committee on Toxicology; National Research Council; Division on Earth and Life Studies; National Research Council

2008-01-01

... to its occurrence in exposed people. Despite reduced workplace exposure, chronic beryllium disease continues to occur. In addition, beryllium has been classified as a likely human carcinogen by several agencies, such as the International Agency for Research on Cancer, the National Toxicology Program, and the U.S. Environmental Protection Agency. Thos...

Implanted deuterium retention and release in carbon-coated beryllium

International Nuclear Information System (INIS)

Anderl, R.A.; Longhurst, G.R.; Pawelko, R.J.; Oates, M.A.

1997-01-01

Deuterium implantation experiments have been conducted on samples of clean and carbon-coated beryllium. These studies entailed preparation and characterization of beryllium samples coated with carbon thicknesses of 100, 500, and 1000 angstrom. Heat treatment of a beryllium sample coated with carbon to a thickness of approximately 100 angstrom revealed that exposure to a temperature of 400 degrees C under high vacuum conditions was sufficient to cause substantial diffusion of beryllium through the carbon layer, resulting in more beryllium than carbon at the surface. Comparable concentrations of carbon and beryllium were observed in the bulk of the coating layer. Higher than expected oxygen levels were observed throughout the coating layer as well. Samples were exposed to deuterium implantation followed by thermal desorption without exposure to air. Differences were observed in deuterium retention and postimplantation release behavior in the carbon-coated samples as compared with bare samples. For comparable implantation conditions (sample temperature of 400 degrees C and an incident deuterium flux of approximately 6 X 10 19 D/m 2 sec), the quantity of deuterium retained in the bare sample was less than that retained in the carbon-coated samples. Further, the release of the deuterium took place at lower temperatures for the bare beryllium surfaces than for carbon-coated beryllium samples. 4 refs., 8 figs., 1 tab

Beryllium in aircraft brakes - a summary

International Nuclear Information System (INIS)

Zenczak, S.

1977-01-01

Beryllium has been in use in aircraft brakes for ten years. During the original design phases of the several aircraft programs using beryllium a number of problems requiring solution confronted the designers. In actual service the solution to these problems performed much better than had been anticipated. A summary is presented. (author)

Galvanic corrosion of beryllium welds

International Nuclear Information System (INIS)

Hill, M.A.; Butt, D.P.; Lillard, R.S.

1997-01-01

Beryllium is difficult to weld because it is highly susceptible to cracking. The most commonly used filler metal in beryllium welds is Al-12 wt.% Si. Beryllium has been successfully welded using Al-Si filler metal with more than 30 wt.% Al. This filler creates an aluminum-rich fusion zone with a low melting point that tends to backfill cracks. Drawbacks to adding a filler metal include a reduction in service temperature, a lowering of the tensile strength of the weld, and the possibility for galvanic corrosion to occur at the weld. To evaluate the degree of interaction between Be and Al-Si in an actual weld, sections from a mock beryllium weldment were exposed to 0.1 M Cl - solution. Results indicate that the galvanic couple between Be and the Al-Si weld material results in the cathodic protection of the weld and of the anodic dissolution of the bulk Be material. While the cathodic protection of Al is generally inefficient, the high anodic dissolution rate of the bulk Be during pitting corrosion combined with the insulating properties of the Be oxide afford some protection of the Al-Si weld material. Although dissolution of the Be precipitate in the weld material does occur, no corrosion of the Al-Si matrix was observed

Status of material development for lifetime expansion of beryllium reflector

Energy Technology Data Exchange (ETDEWEB)

Dorn, C [Materion Brush Beryllium and Composites, California (United States); Tsuchiya, Kunihiko; Kawamura, Hiroshi [Japan Atomic Energy Agency, Oarai Research and Development Center, Oarai, Ibaraki (Japan); Hatano, Y [Univ. of Toyama, Toyama (Japan); Chakrov, P [INP-KNNC, Almaty (Kazakhstan); Kodama, M [Nippon Nuclear Fuel Development Co., Ltd., Oarai, Ibaraki (Japan)

2012-03-15

Beryllium has been used as the reflector element material in the reactor, specifically S-200F structural grade beryllium manufactured by Materion Brush Beryllium and Composites (former, Brush Wellman Inc.). As a part of the reactor upgrade, the Japan Atomic Energy Agency (JAEA) also has carried out the cooperation experiments to extend the operating lifetime of the beryllium reflector elements. It will first be necessary to determine which of the material's physical, mechanical and chemical properties will be the most influential on that choice. The irradiation testing plans to evaluate the various beryllium grades are also briefly considered and prepared. In this paper, material selection, irradiation test plan and PEI development for lifetime expansion of beryllium are described for material testing reactors. (author)

Experiments on tritium behavior in beryllium, (1)

International Nuclear Information System (INIS)

Kawamura, Hiroshi; Ishizuka, Etsuo; Matsumoto, Mikio; Inada, Seiji; Sezaki, Katsuji; Saito, Minoru; Kato, Mineo.

1989-06-01

In JMTR, it was observed that the tritium concentration of the primary coolant increases with the reactor operation at 50 MW. As one of the tritium generation sources, we paid attention to a neutron reflector made of beryllium because the tritium generation rate in the beryllium is bigger than other components in the reactor core. On the other hand, the irradiation test of blanket materials (i.e. tritium breeding materials and neutron multipling materials) are planned for development of the fusion reactor in JMTR and the beryllium will be also irradiated as a neutron multiplier with tritium breeding materials. Therefore, as the irradiated specimens, we used a hot-pressed beryllium disk fabricated by the same method as the neutron reflector or the neutron multiplier and conducted the irradiation tests in JMTR. The purpose of these tests are to clarify the tritium behavior in the hot-pressed beryllium. In this paper, from a viewpoint of the fabrication of capsules for neutron irradiation, the specifications of the irradiated specimens and capsules are summarized. Additionally, the results on the puncture test of the container of the irradiation specimens are described. (author)

Structure investigations of some beryllium materials

Energy Technology Data Exchange (ETDEWEB)

Faeldt, I; Lagerberg, G

1960-05-15

Metallographic structure, microhardness and texture have been studied on various types of beryllium metal including hot pressed powder, a rolled strip and an extruded tube It was found that beryllium exhibits its highest hardness in directions perpendicular to the basal plane. Good ideas of the prevailing textures were obtained with an ordinary X-ray diffractometer.

Structure investigations of some beryllium materials

International Nuclear Information System (INIS)

Faeldt, I.; Lagerberg, G.

1960-05-01

Metallographic structure, microhardness and texture have been studied on various types of beryllium metal including hot pressed powder, a rolled strip and an extruded tube It was found that beryllium exhibits its highest hardness in directions perpendicular to the basal plane. Good ideas of the prevailing textures were obtained with an ordinary X-ray diffractometer

The adhesive bonding of beryllium structural components

International Nuclear Information System (INIS)

Fullerton-Batten, R.C.

1977-01-01

Where service conditions permit, adhesive bonding is a highly recommendable, reliable means of joining beryllium structural parts. Several important programs have successfully used adhesive bonding for joining structural and non-structural beryllium components. Adhesive bonding minimizes stress concentrations associated with other joining techniques and considerably improves fatigue resistance. In addition, no degradation of base metal properties occur. In many instances, structural joints can be fabricated more cheaply by adhesive bonding or in combination with adhesive bonding than by any other method used alone. An evaluation program on structural adhesive bonding of beryllium sheet components is described. A suitable surface pretreatment for beryllium adherends prior to bonding is given. Tensile shear strength and fatigue properties of FM 1000 and FM 123-5 adhesive bonded joints are reviewed and compared with data obtained from riveted joints of similar geometry. (author)

Beryllium armour produced by evaporation-condensation technique

International Nuclear Information System (INIS)

Anisimov, A.; Frolov, V.; Moszherin, S.; Pepekin, G.; Pirogov, A.; Komarov, V.; Mazul, I.

1997-01-01

Beryllium, as armour material for ITER plasma facing components, has a limited erosion lifetime. In order to repair the surface of eroded tiles in-situ, Be-deposition technologies are under consideration. One of them uses the physical vapour deposition of beryllium on copper or beryllium substrate produced by a hot Be-target placed in the vicinity of this substrate. Three different options for using this technology for ITER Be-armour application are considered. The first option is the repair in-situ of eroded Be-tiles. The second option suggests the use of this technology to provide the joining of Be to Cu-substrate. The third option assumes the use of evaporated-condensed beryllium as a bulk tile material bonded to copper substrate by conventional joining (Brazing et al.) techniques. The first results and prospects of these approaches are presented below. (orig.)

Experiments on tritium behavior in beryllium, (2)

International Nuclear Information System (INIS)

Ishitsuka, Etsuo; Kawamura, Hiroshi; Nakata, Hirokatsu; Sugai, Hiroyuki; Tanase, Masakazu.

1990-02-01

Beryllium has been used as the neutron reflector of material testing reactor and as the neutron multiplier for the fusion reactor lately. To study the tritium behavior in beryllium, we conducted the experiments, i.e., tritium release by recoil or diffusion by using the hot-pressed beryllium which had been produced both tritium and helium by neutron irradiation. From our experiments, we found that (1) amount of tritium production per one cycle irradiation (lasting 22 days) of JMTR is 10 mCi/g, (2) amount of tritium per surface area of hot-pressed beryllium released by recoil is 4 μCi/cm 2 , (3) diffusion coefficient of tritium in a temperature range of 800 ∼1180degC can be expressed with the following equation; D = 8.7 x 10 4 exp(-2.9x10 5 /R/T) cm 2 /s. (author)

Assessment of the feasibility and advantages of beryllium recycling

International Nuclear Information System (INIS)

Druyts, F.; Braet, J.; Ooms, L.

2006-01-01

This paper proposes a generic route for the recycling of beryllium from fusion reactors, based on critical issues associated with beryllium pebbles after their service life in the HCPB breeding blanket. These critical issues are the high tritium inventory, the presence of long-lived radionuclides (among which transuranics due to traces of uranium in the base metal), and the chemical toxicity of beryllium. On the basis of the chemical and radiochemical characteristics of the neutron irradiated beryllium pebbles, we describe a possible recycling route. The first step is the detritiation of the material. This can be achieved by heating the pebbles to 800 o C under an argon flow. The argon gas avoids oxidation of the beryllium, and at the proposed temperature the tritium inventory is readily released from the pebbles. In a second step, the released tritium can be oxidised on a copper oxide bed to produce tritiated water, which is consistent with the current international strategy to convert all kinds of tritiated waste into tritiated water, which can subsequently be treated in a water detritiation plant. Removal of radionuclides from the beryllium pebbles may be achieved by several types of chloride processes. The first step is to pass chlorine gas (in an argon flow) over the pebbles, thus yielding volatile BeCl 2 . This beryllium chloride can then be purified by fractional distillation. As a small fraction of the beryllium chloride contains the long-lived 10 Be isotope, 10BeCl 2 has to be separated from 9BeCl 2 , which could be achieved by centrifugal techniques. The product can then be reduced to obtain high-purity metallic beryllium. Two candidate reduction methods were identified: fused salt electrolysis and thermal decomposition. Both these methods require laboratory parametric studies to maximise the yield and achieve a high purity metal, before either process can be upgraded to a larger scale. The eventual product of the chloride reduction process must be a high

Metallurgical viewpoints on the brittleness of beryllium

Energy Technology Data Exchange (ETDEWEB)

Lagerberg, G

1960-02-15

At present the development and use of beryllium metal for structural applications is severely hampered by its brittleness. Reasons for this lack of ductility are reviewed in discussing the deformation behaviour of beryllium in relation to other hexagonal metals. The ease of fracturing in beryllium is assumed to be a consequence of a limited number of deformation modes in combination with high deformation resistance. Models for the nucleation of fracture are suggested. The relation of ductility to elastic constants as well as to grain size, texture and alloying additions is discussed.

Metallurgical viewpoints on the brittleness of beryllium

International Nuclear Information System (INIS)

Lagerberg, G.

1960-02-01

At present the development and use of beryllium metal for structural applications is severely hampered by its brittleness. Reasons for this lack of ductility are reviewed in discussing the deformation behaviour of beryllium in relation to other hexagonal metals. The ease of fracturing in beryllium is assumed to be a consequence of a limited number of deformation modes in combination with high deformation resistance. Models for the nucleation of fracture are suggested. The relation of ductility to elastic constants as well as to grain size, texture and alloying additions is discussed

Laser welding of a beryllium/tantalum collimator

International Nuclear Information System (INIS)

Lingenfelter, A.C.; Anglin, C.D.

1985-01-01

This report describes the methods utilized in the fabrication of a collimator from 0.001 inch thick beryllium and tantalum foil. The laser welding process proved to be an acceptable method for joining the beryllium in a standing edge joint configuration

Design of an interventional magnetic resonance imaging coil for cerebral surgery

Science.gov (United States)

Xu, Yue; Wang, Wen-Tao; Wang, Wei-Min

2012-11-01

In clinical magnetic resonance imaging (MRI), the design of the radiofrequency (RF) coil is very important. For certain applications, the appropriate coil can produce an improved image quality. However, it is difficult to achieve a uniform B1 field and a high signal-to-noise ratio (SNR) simultaneously. In this article, we design an interventional transmitter-and-receiver RF coil for cerebral surgery. This coil adopts a disassembly structure that can be assembled and disassembled repeatedly on the cerebral surgery gantry to reduce the amount of interference from the MRI during surgery. The simulation results and the imaging experiments demonstrate that this coil can produce a uniform RF field, a high SNR, and a large imaging range to meet the requirements of the cerebral surgery.

Beryllium brazing considerations in CANDU fuel bundle manufacture

International Nuclear Information System (INIS)

Harmsen, J.; Pant, A.; Lewis, B.J.; Thompson, W.T.

2010-01-01

'Full text:' Appendages of CANDU fuel bundle elements are currently joined to zircaloy sheaths by vacuum beryllium brazing. Ongoing environmental and workplace concerns about beryllium combined with the continuous efforts by Cameco Fuel Manufacturing in its improvement process, initiated this study to find a substitute for pure beryllium. The presentation will review the necessary functionality of brazing alloy components and short list a series of alloys with the potential to duplicate the performance of pure beryllium. Modifications to current manufacturing processes based on in-plant testing will be discussed in relation to the use of these alloys. The presentation will conclude with a summary of the progress to date and further testing expected to be necessary.

Deuterium permeation and diffusion in high-purity beryllium

International Nuclear Information System (INIS)

Abramov, E.; Riehm, M.P.; Thompson, D.A.; Smeltzer, W.W.

1990-01-01

The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. Using multilayer permeation theory the effects of surface oxide were eliminated and the diffusion coefficients of the bulk beryllium determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 =6.7x10 -9 m 2 /s and E D =28.4 kJ/mol. For the high-grade beryllium samples (99%) the parameters are D 0 =8.0x10 -9 m 2 /s and E D =35.1 kJ/mol. (orig.)

Status of beryllium R and D in Japan

International Nuclear Information System (INIS)

Kawamura, H.; Ishida, K.

2004-01-01

Recently, several R and D program of beryllium for fusion are being promoted in Japan and community of beryllium study is growing up. In the R and D area of beryllium for solid breeding blanket, major subjects are beryllide application for prototype reactor, lifetime evaluation of neutron multiplier, impurity effect of beryllium and recycling of irradiated beryllium. Especially, the study of beryllide application has significant progress in these two years. The basic properties such as tritium inventory, oxidation behavior, steam interaction for stoichiometric Be 12 Ti fabricated by HIP (Hot Isostatic Pressing) have been studied and some advantages against beryllium were made clear. For manufacturing technology development, phase diagram and ductility improvement have been studied. And, Be 12 Ti pebbles with the improved microstructure were successfully fabricated by Rotating Electrode Process. In order to enhance the R and D activities, the R and D network consisted of industries, universities and laboratories in all Japan have been organized. Many collaboration and information exchange strongly promotes the R and D and some projects for commercial application have been launched form these activities. Also international collaborative project such as IEA and ISTC have been launched or planned. Recent result of R and D in Japan is described on this paper. (author)

Quantitative method of determining beryllium or a compound thereof in a sample

Science.gov (United States)

McCleskey, T. Mark; Ehler, Deborah S.; John, Kevin D.; Burrell, Anthony K.; Collis, Gavin E.; Minogue, Edel M.; Warner, Benjamin P.

2010-08-24

A method of determining beryllium or a beryllium compound thereof in a sample, includes providing a sample suspected of comprising beryllium or a compound thereof, extracting beryllium or a compound thereof from the sample by dissolving in a solution, adding a fluorescent indicator to the solution to thereby bind any beryllium or a compound thereof to the fluorescent indicator, and determining the presence or amount of any beryllium or a compound thereof in the sample by measuring fluorescence.

Bioenvironmental Engineering Guide to Beryllium

Science.gov (United States)

2017-07-26

Dermal contact with beryllium can result in dermatitis resembling first- or second-degree burns and skin granulomas [7]. Beryllium dust, fume...minute short-term exposure limit (STEL) of 2.0 µg/m3 [§1910.1024(c)(2) & §1926.1124(c)(2)], and added provisions to prevent skin contact [§1910.1024(b...document you want more information, contact the Environmental, Safety, and Occupational Health (ESOH) Service Center at DSN 798-3764, 1-888-232-ESOH (3764

Considerations against a force compensated coil

International Nuclear Information System (INIS)

Hassenzahl, W.

1988-08-01

The cost of structural components in a large superconducting coil may well exceed the coil and cryostat cost. As a result, the idea of constructing a system composed of two different coil types assembled in such a way that the sources balance and reduce the total structural requirement is oft proposed. A suitable geometry has never been found for the fundamental reason that there can be no force compensated solution. In this paper, the general problem is presented and an analysis of the energy stored and stresses produced in the structure are described in a fundamental way. Finally, the relation between structural mass M and stored energy E, M ≥/rho/E/σ/sub w/, that is valid for all magnetic systems is developed, where /rho/ is the density of the structure and σ/sub w/ is the working stress in the structure. 12 refs., 2 figs

Considerations against a force compensated coil

International Nuclear Information System (INIS)

Hassenzahl, W.

1988-08-01

The cost of structural components in a large superconducting coil may well exceed the coil and cryostat cost. As a result, the idea of constructing a system composed of two different coil types assembled in such a way that the forces balance and reduce the total structural requirement is oft proposed. A suitable geometry has never been found for the fundamental reason that there can be no force compensated solution. In this paper, the general problem is presented and an analysis of the energy stored and stresses produced in the structure are described in a fundamental way. Finally, the relation between structural mass M and stored energy E, M ≥ /rho/E/σ/sub w/, that is valid for all magnetic systems is developed, where /rho/ is the density of the structure and σ/sub w/ is the working stress in the structure. 8 refs., 2 figs

Preparation of a sinterable beryllium oxide through decomposition of beryllium hydroxide (1963); Preparation d'un oxyde de beryllium frittable par decomposition de l'hydiloxyde (1963)

Energy Technology Data Exchange (ETDEWEB)

Bernier, M [Commissariat a l' Energie Atomique, Saclay (France). Centre d' Etudes Nucleaires

1963-07-01

In the course of the present study, we have attempted to precise the factors which among the ones effective in the course of the preparation of the beryllium hydroxide and oxide and during the sintering have an influence on the final result: the density and homogeneity of the sintered body. Of the several varieties of hydroxides precipitated from a sulfate solution the {beta}-hydroxide only is always contaminated with beryllium sulfate and cannot be purified even by thorough washing. We noticed that those varieties of the hydroxide (gel, {alpha}, {beta}) have different decomposition rates; this behaviour is used to identify and even to dose the different species in ({alpha}, {beta}) mixtures. The various hydroxides transmit to the resulting oxides the shape they had when precipitated. Accordingly the history of the oxide is revealed by its behaviour during its fabrication and sintering. By comparing the results of the sintering operation with the various measurements performed on the oxide powders we are led to the conclusion that an oxide obtained from beryllium hydroxide is sinterable under vacuum if the following conditions are fulfilled: the particle size must lie between 0.1 and 0.2 {mu} and the BeSO{sub 4} content of the powder must be less than 0.25 per cent wt (expressed as SO{sub 3}/BeO). The best fitting is obtained with the oxide issued from an {alpha}-hydroxide precipitated as very small aggregates and with a low sulfur-content. We have observed that this is also the case for the oxide obtained by direct calcination of beryllium sulfate. (author) [French] Au cours de cette etude, nous avons cherche a preciser les facteurs qui, intervenant tout au long de la preparation de l'hydroxyde, puis de l'oxyde de beryllium et enfin du frittage, peuvent avoir une influence sur le resultat final: la densite et l'homogeneite du fritte. Parmi tous les hydroxydes precipites d'une solution de sulfate, seul l'hydroxyde {beta} est toujours fortement pollue par le sulfate

Impurities effect on the swelling of neutron irradiated beryllium

International Nuclear Information System (INIS)

Donne, M.D.; Scaffidi-Argentina, F.

1995-01-01

An important factor controlling the swelling behaviour of fast neutron irradiated beryllium is the impurity content which can strongly affect both the surface tension and the creep strength of this material. Being the volume swelling of the old beryllium (early sixties) systematically higher than that of the more modem one (end of the seventies), a sensitivity analysis with the aid of the computer code ANFIBE (ANalysis of Fusion Irradiated BEryllium) to investigate the effect of these material properties on the swelling behaviour of neutron irradiated beryllium has been performed. Two sets of experimental data have been selected: the first one named Western refers to quite recently produced Western beryllium, whilst the second one, named Russian refers to relatively old (early sixties) Russian beryllium containing a higher impurity rate than the Western one. The results obtained with the ANFIBE Code were assessed by comparison with experimental data and the used material properties were compared with the data available in the literature. Good agreement between calculated and measured values has been found

Study on neutron irradiation behavior of beryllium as neutron multiplier

Energy Technology Data Exchange (ETDEWEB)

Ishitsuka, Etsuo [Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment

1998-03-01

More than 300 tons beryllium is expected to be used as a neutron multiplier in ITER, and study on the neutron irradiation behavior of beryllium as the neutron multiplier with Japan Materials Testing Reactor (JMTR) were performed to get the engineering data for fusion blanket design. This study started as the study on the tritium behavior in beryllium neutron reflector in order to make clear the generation mechanism on tritium of JMTR primary coolant since 1985. These experiences were handed over to beryllium studies for fusion study, and overall studies such as production technology of beryllium pebbles, irradiation behavior evaluation and reprocessing technology have been started since 1990. In this presentation, study on the neutron irradiation behavior of beryllium as the neutron multiplier with JMTR was reviewed from the point of tritium release, thermal properties, mechanical properties and reprocessing technology. (author)

Modeling of hydrogen interactions with beryllium

Energy Technology Data Exchange (ETDEWEB)

Longhurst, G.R. [Lockheed Martin Idaho Technologies Co., Idaho Falls, ID (United States)

1998-01-01

In this paper, improved mathematical models are developed for hydrogen interactions with beryllium. This includes the saturation effect observed for high-flux implantation of ions from plasmas and retention of tritium produced from neutronic transmutations in beryllium. Use of the models developed is justified by showing how they can replicated experimental data using the TMAP4 tritium transport code. (author)

75 FR 80734 - Chronic Beryllium Disease Prevention Program

Science.gov (United States)

2010-12-23

... are used in nuclear weapons as nuclear reactor moderators or reflectors and as nuclear reactor fuel...), grinding, and machine tooling of parts. Inhalation of beryllium particles may cause chronic beryllium...

THE IDAHO NATIONAL LABORATORY BERYLLIUM TECHNOLOGY UPDATE

International Nuclear Information System (INIS)

Glen R. Longhurst

2007-01-01

A Beryllium Technology Update meeting was held at the Idaho National Laboratory on July 18, 2007. Participants came from the U.S., Japan, and Russia. There were two main objectives of this meeting. One was a discussion of current technologies for beryllium in fission reactors, particularly the Advanced Test Reactor and the Japan Materials Test Reactor, and prospects for material availability in the coming years. The second objective of the meeting was a discussion of a project of the International Science and Technology Center regarding treatment of irradiated beryllium for disposal. This paper highlights discussions held during that meeting and major conclusions reached

Deuterium permeation and diffusion in high purity beryllium

International Nuclear Information System (INIS)

Abramov, E.

1990-05-01

The permeation rate of deuterium through high-purity beryllium membranes was measured using the gas-driven permeation technique. The time-dependent and the steady-state deuterium flux data were analyzed and the effective diffusivities of the samples were determined. A multilayer permeation theory was used in order to eliminate the surface oxide effects and the diffusion coefficients of the bulk beryllium were determined. The diffusion parameters obtained for the extra-grade beryllium samples (99.8%) are D 0 = 6.7 x 10 -9 [m 2 /s] and E D = 28.4 [KJ/mol]; and for the high-grade beryllium samples (99%) the parameters are D 0 = 8.0 x 10 -9 [m 2 /s] and E D = 35.1 [KJ/mol

Background field coils for the High Field Test Facility

International Nuclear Information System (INIS)

Zbasnik, J.P.; Cornish, D.N.; Scanlan, R.M.; Jewell, A.M.; Leber, R.L.; Rosdahl, A.R.; Chaplin, M.R.

1980-01-01

The High Field Test Facility (HFTF), presently under construction at LLNL, is a set of superconducting coils that will be used to test 1-m-o.d. coils of prototype conductors for fusion magnets in fields up to 12 T. The facility consists of two concentric sets of coils; the outer set is a stack of Nb-Ti solenoids, and the inner set is a pair of solenoids made of cryogenically-stabilized, multifilamentary Nb 3 Sn superconductor, developed for use in mirror-fusion magnets. The HFTF system is designed to be parted along the midplane to allow high-field conductors, under development for Tokamak fusion machines, to be inserted and tested. The background field coils were wound pancake-fashion, with cold-welded joints at both the inner and outer diameters. Turn-to-turn insulation was fabricated at LLNL from epoxy-fiberglass strip. The coils were assembled and tested in our 2-m-diam cryostat to verify their operation

Design and test program of a simplified divertor dummy coil structure for the WEST project

Energy Technology Data Exchange (ETDEWEB)

Doceul, L., E-mail: louis.doceul@cea.fr [CEA, IRFM, Saint-Paul-Lez-Durance Cedex F-13108 (France); Bucalossi, J.; Dougnac, H.; Ferlay, F.; Gargiulo, L.; Keller, D.; Larroque, S.; Lipa, M.; Pilia, A. [CEA, IRFM, Saint-Paul-Lez-Durance Cedex F-13108 (France); Portafaix, C. [ITER Organization, Route de Vinon-sur-Verdon 13115, St. Paul-lez-Durance (France); Saille, A. [CEA, IRFM, Saint-Paul-Lez-Durance Cedex F-13108 (France); Salami, M. [AVANTIS Engineering Groupe, ZI de l’Aiguille 46100, Figeac (France); Samaille, F.; Soler, B.; Thouvenin, D.; Verger, J.M.; Zago, B. [CEA, IRFM, Saint-Paul-Lez-Durance Cedex F-13108 (France)

2013-12-15

Highlights: • The mechanical design and integration of the divertor structure has been performed. • The design of the casing and the winding-pack has been finalized. • The coil assembly process has been validated. • The realization of a coil mock-up scale one is in progress. -- Abstract: In order to fully validate actively cooled tungsten plasma facing components (industrial fabrication, operation with long plasma duration), the implementation of a tungsten axisymmetric divertor structure in the tokamak Tore-Supra is studied. With this major upgrade, so-called WEST (Tungsten Environment in Steady state Tokamak), Tore-Supra will be able to address the problematic of long plasma discharges with a metallic divertor target. To do so, it is planned to install two symmetric divertor coils inside the vacuum vessel. This assembly, called divertor structure, is made up of two stainless steel casings containing a copper winding pack cooled by a pressurized hot water circuit (up to 180 °C, 4 MPa) and is designed to perform steady state plasma operation (up to 1000 s). The divertor structure will be a complex assembly ring of 4 m diameter representing a total weight of around 20 tons. The technical challenge of this component will be the implementation of angular sectors inside the vacuum vessel environment (TIG welding of the coil casing, induction brazing and electrical insulation of the copper winding). Moreover, this complex assembly must sustain harsh environmental conditions in terms of ultra high vacuum conditions, electromagnetical loads and electrical isolation (13 kV ground voltage) under high temperature. In order to fully validate the assembly and the performance of this complex component, the production of a scale one dummy coil is in progress. The paper will illustrate, the technical developments performed in order to finalize the design for the call for tender for fabrication. The progress and the first results of the simplified dummy coils will be also

Design and test program of a simplified divertor dummy coil structure for the WEST project

International Nuclear Information System (INIS)

Doceul, L.; Bucalossi, J.; Dougnac, H.; Ferlay, F.; Gargiulo, L.; Keller, D.; Larroque, S.; Lipa, M.; Pilia, A.; Portafaix, C.; Saille, A.; Salami, M.; Samaille, F.; Soler, B.; Thouvenin, D.; Verger, J.M.; Zago, B.

2013-01-01

Highlights: • The mechanical design and integration of the divertor structure has been performed. • The design of the casing and the winding-pack has been finalized. • The coil assembly process has been validated. • The realization of a coil mock-up scale one is in progress. -- Abstract: In order to fully validate actively cooled tungsten plasma facing components (industrial fabrication, operation with long plasma duration), the implementation of a tungsten axisymmetric divertor structure in the tokamak Tore-Supra is studied. With this major upgrade, so-called WEST (Tungsten Environment in Steady state Tokamak), Tore-Supra will be able to address the problematic of long plasma discharges with a metallic divertor target. To do so, it is planned to install two symmetric divertor coils inside the vacuum vessel. This assembly, called divertor structure, is made up of two stainless steel casings containing a copper winding pack cooled by a pressurized hot water circuit (up to 180 °C, 4 MPa) and is designed to perform steady state plasma operation (up to 1000 s). The divertor structure will be a complex assembly ring of 4 m diameter representing a total weight of around 20 tons. The technical challenge of this component will be the implementation of angular sectors inside the vacuum vessel environment (TIG welding of the coil casing, induction brazing and electrical insulation of the copper winding). Moreover, this complex assembly must sustain harsh environmental conditions in terms of ultra high vacuum conditions, electromagnetical loads and electrical isolation (13 kV ground voltage) under high temperature. In order to fully validate the assembly and the performance of this complex component, the production of a scale one dummy coil is in progress. The paper will illustrate, the technical developments performed in order to finalize the design for the call for tender for fabrication. The progress and the first results of the simplified dummy coils will be also

Room Temperature Magnetic Determination of the Current Center Line for the ITER TF Coils

CERN Document Server

Lerch, Philippe; Buzio, Marco; Negrazus, Marco; Baynham, Elwyn; Sanfilippo, Stephane; Foussat, Arnaud

2014-01-01

The ITER tokamak includes 18 superconducting D-shaped toroidal field (IT) coils. Unavoidable shape deformations as well as assembly errors will lead to field errors, which can be modeled with the knowledge of the current center line (CCL). Accurate survey during the entire manufacturing and assembly process, including transfer of survey points, is complex. In order to increase the level of confidence, a room temperature magnetic measurement of the CCL on assembled and closed winding packs is foreseen, prior to insertion into their cold case. In this contribution, we discuss the principle of the CCL determination and present a low frequency ac measurement system under development at PSI, within an ITER framework contract. The largest current allowed to flow in the TF coil at room temperature and the precision requirements for the determination of the CCL loci of the coil are hard boundaries. Eddy currents in the radial plates, the winding pack enclosures, and possibly from iron in the reinforced concrete floor...

Formation of cellular structure in beryllium at plastic working

International Nuclear Information System (INIS)

Papirov, I.I.; Nikolaenko, A.A.; Shokurov, V.S.; Pikalov, A.I.

2013-01-01

Conditions of cellular structure formation are investigated at various kinds of deformation and heat treatment of beryllium ingots. It is shown that the cellular structure plays the important role in formation of complex of physical mechanical properties of beryllium. Influence of impurity, various conditions of deformation (temperature, squeezing degree) and heat treatments on substructure, texture and mechanical properties of metal is investigated. Optimum conditions of rolling and heat treatments of beryllium are defined. The way of sign-variable cyclic deformation of beryllium ingots is offered for reception quasi-isotropic fine-grained metal. Physical-mechanical properties of ultra fine-grained metal are studied

Preparation of copper-beryllium alloys from Indian beryl

International Nuclear Information System (INIS)

Paul, C.M.; Sharma, B.P.; Subba Rao, K.S.; Rajadhyaksha, M.G.; Sundaram, C.V.

1975-01-01

The paper presents the results of laboratory-scale investigations on the preparation of copper-beryllium and aluminium beryllium master alloys starting from Indian beryl and adopting the fluoride process. The flowsheet involves: (1) conversion of the Be-values in beryl into water soluble sodium beryllium fluoride, (2) preparation of beryllium hydroxide by alkali treatment of aqueous Na 2 BeF 4 (3) conversion of Be(OH) 2 to (NH 4 ) 2 BeF 4 by treatment with NH 4 HF 2 (4) thermal decomposition of (NH 4 ) 2 BeF 4 to BeF 2 and (5) magnesium reduction of BeF 2 (without/with) the addition of copper/aluminium to obtain beryllium metal/alloys. The method has been successfully employed for the preparation of Cu-Be master alloys containing about 8% Be and free of Mg on a 200 gm scale. A1-80% Be master alloys have also been prepared by this method. Toxicity and health hazards associated with Be are discussed and the steps taken to ensure safe handling of Be are described. (author)

10 CFR 850.20 - Baseline beryllium inventory.

Science.gov (United States)

2010-01-01

... 10 Energy 4 2010-01-01 2010-01-01 false Baseline beryllium inventory. 850.20 Section 850.20 Energy... Baseline beryllium inventory. (a) The responsible employer must develop a baseline inventory of the... inventory, the responsible employer must: (1) Review current and historical records; (2) Interview workers...

Characterization of shocked beryllium

Directory of Open Access Journals (Sweden)

Papin P.A.

2012-08-01

Full Text Available While numerous studies have investigated the low-strain-rate constitutive response of beryllium, the combined influence of high strain rate and temperature on the mechanical behavior and microstructure of beryllium has received limited attention over the last 40 years. In the current work, high strain rate tests were conducted using both explosive drive and a gas gun to accelerate the material. Prior studies have focused on tensile loading behavior, or limited conditions of dynamic strain rate and/or temperature. Two constitutive strength (plasticity models, the Preston-Tonks-Wallace (PTW and Mechanical Threshold Stress (MTS models, were calibrated using common quasi-static and Hopkinson bar data. However, simulations with the two models give noticeably different results when compared with the measured experimental wave profiles. The experimental results indicate that, even if fractured by the initial shock loading, the Be remains sufficiently intact to support a shear stress following partial release and subsequent shock re-loading. Additional “arrested” drive shots were designed and tested to minimize the reflected tensile pulse in the sample. These tests were done to both validate the model and to put large shock induced compressive loads into the beryllium sample.

SAFARI-1 research reactor beryllium reflector element replacement, management and relocation

International Nuclear Information System (INIS)

Kock, Marisa De; Vlok, Jwh; Steynberg, B.J.

2012-01-01

The beryllium (Be) reflector elements of the SAFARI-1 Research Reactor were replaced in October 2011 as part of the Ageing Management Programme of the reactor. After more than three million MWh of operation over a period of 47 years, core reloading became more difficult due to the geometric deformation of the beryllium reflector elements. During the replacement of the reflector elements, criticality and reactivity worth experiments were performed and found to compare favorably with calculated values. A Beryllium Management Programme was established at SAFARI-1 to identify and apply effective and appropriate actions and practices for managing the ageing of the new beryllium reflector elements. This will provide timely detection and mitigation of ageing mechanisms relevant to beryllium reflector elements, supporting the life extension of these elements. These actions and practices include monitoring of the tritium levels in the primary water, calculating and measuring the fluxes within the beryllium reflector positions, measuring the straightness of the elements to track geometric deformation and visually inspecting the reflector elements for crack formation. Acceptance criteria indicating the end of life of the elements were established. These criteria take into account the smallest gap that could exist between elements, sudden changes in the tritium levels and formation of cracks. All the data obtained through the Beryllium Management Programme are recorded in a database. Additional benefits gained through a Beryllium Management Programme are the availability of a complete irradiation history of the beryllium reflector elements at any point in time and the establishment of a knowledge base to assists in the understanding of the behavior of the beryllium reflector elements in an irradiation environment. Straightness baseline measurements of the new beryllium reflector elements were performed with a beryllium straightness measurement tool, designed at SAFARI-1. The

SAFARI-1 research reactor beryllium reflector element replacement, management and relocation

Energy Technology Data Exchange (ETDEWEB)

Kock, Marisa De; Vlok, Jwh; Steynberg, B J [South Africa Atomic Energy Corporation (Necsa) (South Africa)

2012-03-15

The beryllium (Be) reflector elements of the SAFARI-1 Research Reactor were replaced in October 2011 as part of the Ageing Management Programme of the reactor. After more than three million MWh of operation over a period of 47 years, core reloading became more difficult due to the geometric deformation of the beryllium reflector elements. During the replacement of the reflector elements, criticality and reactivity worth experiments were performed and found to compare favorably with calculated values. A Beryllium Management Programme was established at SAFARI-1 to identify and apply effective and appropriate actions and practices for managing the ageing of the new beryllium reflector elements. This will provide timely detection and mitigation of ageing mechanisms relevant to beryllium reflector elements, supporting the life extension of these elements. These actions and practices include monitoring of the tritium levels in the primary water, calculating and measuring the fluxes within the beryllium reflector positions, measuring the straightness of the elements to track geometric deformation and visually inspecting the reflector elements for crack formation. Acceptance criteria indicating the end of life of the elements were established. These criteria take into account the smallest gap that could exist between elements, sudden changes in the tritium levels and formation of cracks. All the data obtained through the Beryllium Management Programme are recorded in a database. Additional benefits gained through a Beryllium Management Programme are the availability of a complete irradiation history of the beryllium reflector elements at any point in time and the establishment of a knowledge base to assists in the understanding of the behavior of the beryllium reflector elements in an irradiation environment. Straightness baseline measurements of the new beryllium reflector elements were performed with a beryllium straightness measurement tool, designed at SAFARI-1. The

PDX, mechanical design update and assembly

International Nuclear Information System (INIS)

Knutson, D.; Cavalluzzo, S.; Davenport, J.; Kaminsky, E.; Perry, E.; Willard, J.

1977-01-01

Mechanical design changes and refinements have occurred since the Sixth Symposium on Engineering Problems of Fusion Research. Particular attention is focused on the area of the toroidal field coil lap joint. Preassembly of major components and final assembly and alignment of the toroidal and poloidal field coils is discussed

Occupational and non-occupational allergic contact dermatitis from beryllium

Energy Technology Data Exchange (ETDEWEB)

Vilaplana, J; Romaguera, C; Grimalt, F [Allergy Department, Dermatological Service Hospital Clinico, Barcelona (Spain)

1992-01-01

There are various references to sensitization to beryllium in the literature. Since introducing a patch testing series for patients with suspected sensitization to metals, we have found 3 cases of sensitization to beryllium. Of these 3 cases, we regard the first 2 as having relevant sensitization. Beryllium chloride (1% pet.) was positive in 3 patients and negative in 150 controls. (au).

Occupational and non-occupational allergic contact dermatitis from beryllium

International Nuclear Information System (INIS)

Vilaplana, J.; Romaguera, C.; Grimalt, F.

1992-01-01

There are various references to sensitization to beryllium in the literature. Since introducing a patch testing series for patients with suspected sensitization to metals, we have found 3 cases of sensitization to beryllium. Of these 3 cases, we regard the first 2 as having relevant sensitization. Beryllium chloride (1% pet.) was positive in 3 patients and negative in 150 controls. (au)

The structure, properties and performance of plasma-sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Elliott, K.E.

1995-01-01

Plasma-spray technology is under investigation as a method for producing high thermal conductivity beryllium coatings for use in magnetic fusion applications. Recent investigations have focused on optimizing the plasma-spray process for depositing beryllium coatings on damaged beryllium surfaces. Of particular interest has been optimizing the processing parameters to maximize the through-thickness thermal conductivity of the beryllium coatings. Experimental results will be reported on the use of secondary H 2 gas additions to improve the melting of the beryllium powder and transferred-arc cleaning to improve the bonding between the beryllium coatings and the underlying surface. Information will also be presented on thermal fatigue tests which were done on beryllium coated ISX-B beryllium limiter tiles using 10 sec cycle times with 60 sec cooldowns and an International Thermonuclear Experimental Reactor (ITER) relevant divertor heat flux slightly in excess of 5 MW/m 2

Deuterium/hydrogen isotope exchange on beryllium and beryllium nitride; Deuterium/Wasserstoff-Isotopenaustausch an Beryllium und Berylliumnitrid

Energy Technology Data Exchange (ETDEWEB)

Dollase, Petra; Eichler, Michael; Koeppen, Martin; Dittmar, Timo; Linsmeier, Christian [Forschungszentrum Juelich GmbH, Institut fuer Energie- und Klimaforschung - Plasmaphysik (Germany)

2016-07-01

In the fusion experiments JET and ITER, the first wall is made up of beryllium. The use of nitrogen is discussed for radiative cooling in the divertor. This can react with the surface of the first wall to form beryllium nitride (Be{sub 3}N{sub 2}). The hydrogen isotopes deuterium and tritium, which react in the fusion reaction to helium and a neutron, are used as fuel. Since the magnetic confinement of the plasma is not perfect, deuterium and tritium ions are also found on the beryllium wall and can accumulate there. This should be avoided due to the radioactivity of tritium. Therefore the isotope exchange with deuterium is investigated to regenerate the first wall. We investigate the isotopic exchange of deuterium and protium in order to have not to work with radioactive tritium. The ion bombardment is simulated with an ion source. With voltages up to a maximum of 5 kV, deuterium and protic hydrogen ions are implanted in polycrystalline Be and Be{sub 3}N{sub 2}. The samples are then analyzed in situ using X-ray photoelectron spectroscopy (XPS) and thermal desorption spectroscopy (TDS). Subsequently, samples prepared under the same conditions are characterized ex-situ by means of nuclear reaction analysis (NRA). [German] In den Fusionsexperimenten JET und ITER besteht die erste Wand im Hauptraum aus Beryllium (Be). Zur Strahlungskuehlung im Divertor wird der Einsatz von Stickstoff diskutiert. Dieser kann mit der Oberflaeche der ersten Wand zu Berylliumnitrid (Be{sub 3}N{sub 2}) reagieren. Als Brennstoff werden die Wasserstoffisotope Deuterium und Tritium eingesetzt, die in der Fusionsreaktion zu Helium und einem Neutron reagieren. Da der magnetische Einschluss des Plasmas nicht perfekt ist, treffen auch Deuterium- und Tritiumionen auf die Berylliumwand auf und koennen sich dort anreichern. Das soll aufgrund der Radioaktivitaet von Tritium unbedingt vermieden werden. Daher wird zur Regenerierung der ersten Wand der Isotopenaustausch mit Deuterium untersucht. Wir

The Rocky Flats Environmental Technology Site beryllium characterization project

International Nuclear Information System (INIS)

Morrell, D.M.; Miller, J.R.; Allen, D.F.

1999-01-01

A site beryllium characterization project was completed at the Rocky Flats Environmental Technology Site (RFETS) in 1997. Information from historical reviews, previous sampling surveys, and a new sampling survey were used to establish a more comprehensive understanding of the locations and levels of beryllium contamination in 35 buildings. A feature of the sampling strategy was to test if process knowledge was a good predictor of where beryllium contamination could be found. Results revealed that this technique was effective at identifying where surface contamination levels might exceed the RFETS smear control level but that it was not effective in identifying where low concentrations of beryllium might be found

Phosphorus-containing azo compounds as analytical reagents for beryllium

International Nuclear Information System (INIS)

Lisenko, N.F.; Dolzhnikova, E.N.; Petrova, G.S.; Tsvetkov, E.N.; Vsesoyuznyj Nauchno-Issledovatel'skij Inst. Khimicheskikh Reaktivov i Osobo Chistykh Veshchestv, Moscow; AN SSSR, Moscow. Inst. Ehlementoorganicheskikh Soedinenij)

1979-01-01

The interaction of beryllium with six new azocompounds based on chromotropic or R-acids and o-aminophenyl-phenylphosphonic acids is studied. A sharp difference in the detection limit for beryllium by the two groups of compounds is found. Azoderivatives based on chromotropic acid are promising agent for beryllium due to sufficiently high selectivity. The introduction of the methyl-group into the o-position of the phosphorus-containing group improves the analytical properties of agents. Techniques are developed for the determination of beryllium in bronze, sewage water and in an artificial mixture using a sodium salt of 1.8-dioxi-2 [2' - (oxi- (o-methylphenyl)-phosphenyl)-phenilazo]-naphtalene-3.6-disulfoacid

Progress of the ITER Correction Coils in China

CERN Document Server

Wei, J; Han, S; Yu, X; Du, S; Li, C; Fang, C; Wang, L; Zheng, W; Liu, L; Wen, J; Li, H; Libeyre, P; Dolgetta, N; Cormany, C; Sgobba, S

2014-01-01

The ITER Correction Coils (CC) include three sets of six coils each, distributed symmetrically around the tokamak to correct error fields. Each pair of coils, located on opposite sides of the tokamak, is series connected with polarity to produce asymmetric fields. The manufacturing of these superconducting coils is undergoing qualification of the main fabrication processes: winding into multiple pancakes, welding helium inlet/outlet on the conductor jacket, turn and ground insulation, vacuum pressure impregnation, inserting into an austenitic stainless steel case, enclosure welding, and assembling the terminal service box. It has been proceeding by an intense phase of R\\&D, trials tests, and final adjustment of the tooling. This paper mainly describes the progress in ASIPP for the CC manufacturing process before and on qualification phase and the status of corresponding equipment which are ordered or designed for each process. Some test results for the key component and procedure are also presented.

Influence of physicochemical properties of beryllium particles on cultured cell toxicity

International Nuclear Information System (INIS)

Finch, G.L.; Brooks, A.L.; Hoover, M.D.; Cuddihy, R.G.

1988-01-01

The toxicity of beryllium oxide (BeO)), beryllium metal, and beryllium sulfate (BeSO 4 ) was studied in two cell lines, Chinese hamster ovary cells (CHO) and lung epithelial cells (LEC). Beryllium oxide particles were prepared at either 500 or 1000 deg. C, and two different particle sizes of beryllium metal were used. Following a 20-h exposure to beryllium compounds, cells were grown in culture to quantitate cloning ability relative to controls as a measure of cell killing, The LEC cultures were more sensitive to beryllium cytotoxicity than the CHO cells. When expressed on the basis of the mass of material added to the cultures, the order of toxicity was BeSO 4 ≥ 500 deg. C -BeO > 1000 deg. C -BeO > Be metal (small) Be metal (large). When cytotoxic effects were expressed on the basis of particulate surface rather than mass, the relative differences in toxicity between compounds was decreased. The order of toxicity was Be metal (small) ∼ Be metal (large) ∼ 500 deg. C-BeO ∼ 1000 deg. C-BeO. These data indicate that solubility influences beryllium toxicity to short-term cell cultures. (author)

Beryllium and zirconium

International Nuclear Information System (INIS)

Salesse, Marc

1959-01-01

Pure beryllium and zirconium, both isolated at about the same date but more than a century ago remained practically unused for eighty years. Fifteen years ago they were released from this state of inactivity by atomic energy, which made them into current metal a with an annual production which runs into tens of tons for the one and thousands for the other. The reasons for this promotion promise well for the future of the two metals, which moreover will probably find additional uses in other branches of industry. The attraction of beryllium and zirconium for atomic energy is easily explained. The curve of figure 1 gives the price per gram of uranium-235 as a function of enrichment: this price increases by about a factor of 3 on passing from natural uranium (0, 7 percent 235 U) to almost pure uranium-235. Because of their tow capture cross-section beryllium and zirconium make it possible, or at least easier, to use natural uranium and they thus enjoy an advantage the extent of which must be calculated for each reactor or fuel element project, but which is generally considerable. It will be seen later that this advantage should be based on figures which are even more favourable that would appear from the simple ratio 3 of the price of pure uranium- 235 contained in natural uranium. Reprint of a paper published in 'Industries Atomiques' - n. 1-2, 1959

Validation of cleaning method for various parts fabricated at a Beryllium facility

Energy Technology Data Exchange (ETDEWEB)

Davis, Cynthia M. [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

2015-12-15

This study evaluated and documented a cleaning process that is used to clean parts that are fabricated at a beryllium facility at Los Alamos National Laboratory. The purpose of evaluating this cleaning process was to validate and approve it for future use to assure beryllium surface levels are below the Department of Energy’s release limits without the need to sample all parts leaving the facility. Inhaling or coming in contact with beryllium can cause an immune response that can result in an individual becoming sensitized to beryllium, which can then lead to a disease of the lungs called chronic beryllium disease, and possibly lung cancer. Thirty aluminum and thirty stainless steel parts were fabricated on a lathe in the beryllium facility, as well as thirty-two beryllium parts, for the purpose of testing a parts cleaning method that involved the use of ultrasonic cleaners. A cleaning method was created, documented, validated, and approved, to reduce beryllium contamination.

Extraction of beryllium sulfate by a long chain amine; Extraction du sulfate de beryllium par une amine a longue chaine

Energy Technology Data Exchange (ETDEWEB)

Etaix, E.S. [Commissariat a l' Energie Atomique, Fontenay-Aux-Roses (France). Centre d' Etudes Nucleaires

1968-06-01

The extraction of sulfuric acid in aqueous solution by a primary amine in benzene solution, 3-9 (diethyl) - 6-amino tri-decane (D.E.T. ) - i.e., with American nomenclature 1-3 (ethyl-pentyl) - 4-ethyl-octyl amine (E.P.O.) - has made it possible to calculate the formation constants of alkyl-ammonium sulfate and acid sulfate. The formula of the beryllium and alkyl-ammonium sulfate complex formed in benzene has next been determined, for various initial acidity of the aqueous solution. Lastly, evidence has been given of negatively charged complexes of beryllium and sulfate in aqueous solution, through the dependence of the aqueous sulfate ions concentration upon beryllium extraction. The formation constant of these anionic complexes has been evaluated. (author) [French] L'etude de l'extraction de l'acide sulfurique en solution aqueuse par une amine primaire en solution dans le benzene, le diethyl-3,9 amino-6 tridecane (D.E.T.) - autre nom americain 1-3 (ethylpentyl) - 4-ethyloctylamine (E.P.O.) a permis de calculer les constantes de formation du sulfate et de l'hydrogenosulfate d'alkyl-ammonium. La formule du complexe de sulfate de beryllium et d'alkyl-ammonium forme en solution benzenique a ete ensuite determinee pour diverses acidites initiales de la solution aqueuse. Enfin, l'influence de la concentration des ions sulfate de la phase aqueuse sur l'extraction du beryllium a mis en evidence la formation en solution aqueuse de complexes anioniques de sulfate et de beryllium dont la constante de formation a ete evaluee. (auteur)

Extraction of beryllium sulfate by a long chain amine; Extraction du sulfate de beryllium par une amine a longue chaine

Energy Technology Data Exchange (ETDEWEB)

Etaix, E S [Commissariat a l' Energie Atomique, Fontenay-Aux-Roses (France). Centre d' Etudes Nucleaires

1968-06-01

The extraction of sulfuric acid in aqueous solution by a primary amine in benzene solution, 3-9 (diethyl) - 6-amino tri-decane (D.E.T. ) - i.e., with American nomenclature 1-3 (ethyl-pentyl) - 4-ethyl-octyl amine (E.P.O.) - has made it possible to calculate the formation constants of alkyl-ammonium sulfate and acid sulfate. The formula of the beryllium and alkyl-ammonium sulfate complex formed in benzene has next been determined, for various initial acidity of the aqueous solution. Lastly, evidence has been given of negatively charged complexes of beryllium and sulfate in aqueous solution, through the dependence of the aqueous sulfate ions concentration upon beryllium extraction. The formation constant of these anionic complexes has been evaluated. (author) [French] L'etude de l'extraction de l'acide sulfurique en solution aqueuse par une amine primaire en solution dans le benzene, le diethyl-3,9 amino-6 tridecane (D.E.T.) - autre nom americain 1-3 (ethylpentyl) - 4-ethyloctylamine (E.P.O.) a permis de calculer les constantes de formation du sulfate et de l'hydrogenosulfate d'alkyl-ammonium. La formule du complexe de sulfate de beryllium et d'alkyl-ammonium forme en solution benzenique a ete ensuite determinee pour diverses acidites initiales de la solution aqueuse. Enfin, l'influence de la concentration des ions sulfate de la phase aqueuse sur l'extraction du beryllium a mis en evidence la formation en solution aqueuse de complexes anioniques de sulfate et de beryllium dont la constante de formation a ete evaluee. (auteur)

Preparation of copper-beryllium alloys from Indian beryl

International Nuclear Information System (INIS)

Paul, C.M.; Sharma, B.P.; Subba Rao, K.S.; Rajadhyaksha, M.G.; Sundaram, C.V.

1975-01-01

The report presents the results of laboratory scale investigations on the preparation of copper-beryllium and aluminium-beryllium master alloys starting from Indian beryl and adopting the fluoride process. The flow-sheet involves : (1) conversion of the Be-values in beryl into water soluble sodium beryllium fluoride (2) preparation of beryllium hydroxide by alkali treatment of aqueous Na 2 BeF 4 (3) conversion of Be(OH) 2 to (NH 4 ) 2 BeF 4 by treatment with NH 4 HF 2 (4) thermal decomposition of (NH 4 ) 2 BeF 4 to BeF 2 and (5) magnesium reduction of BeF 2 (with the addition of copper/aluminium) to obtain beryllium alloys. The method has been successfully employed for the preparation of Cu-Be master alloys containing about 8% Be and free of Mg on a 200 gm scale. An overall Be-recovery of about 80% has been achieved. Al-8% Be master alloys have also been prepared by this method. Toxicity and health hazards associated with Be are discussed and the steps taken to ensure safe handling of Be are described. (author)

Erosion of beryllium under ITER - Relevant transient plasma loads

Science.gov (United States)

Kupriyanov, I. B.; Nikolaev, G. N.; Kurbatova, L. A.; Porezanov, N. P.; Podkovyrov, V. L.; Muzichenko, A. D.; Zhitlukhin, A. M.; Gervash, A. A.; Safronov, V. M.

2015-08-01

Beryllium will be used as a armor material for the ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of the ITER first wall. This paper presents the results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility. The Be/CuCrZr mock-ups were exposed to up to 100 shots by deuterium plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat loads range of 0.2-0.5 MJ/m2 at different temperature of beryllium tiles. The temperature of Be tiles has been maintained about 250 and 500 °C during the experiments. After 10, 40 and 100 shots, the beryllium mass loss/gain under erosion process were investigated as well as evolution of surface microstructure and cracks morphology.

Coil Tolerance Impact on Plasma Surface Quality for NCSX

International Nuclear Information System (INIS)

Brooks, Art; Reiersen, Wayne

2003-01-01

The successful operation of the National Compact Stellarator Experiment (NCSX) machine will require producing plasma configurations with good flux surfaces, with a minimum volume of the plasma lost to magnetic islands or stochastic regions. The project goal is to achieve good flux surfaces over 90% of the plasma volume. NCSX is a three period device designed to be operated with iota ranging from ∼0.4 on axis to ∼0.7 at the edge. The field errors of most concern are those that are resonant with 3/5 and 3/6 modes (for symmetry preserving field errors) and the 1/2 and 2/3 modes (for symmetry breaking field errors). In addition to losses inherent in the physics configuration itself, there will be losses from field errors arising from coil construction and assembly errors. Some of these losses can be recovered through the use of trim coils or correction coils. The impact of coil tolerances on plasma surface quality is evaluated herein for the NCSX design. The methods used in this evaluation are discussed. The ability of the NCSX trim coils to correct for field errors is also examined. The results are used to set coils tolerances for the various coil systems

Status of beryllium development for fusion applications

International Nuclear Information System (INIS)

Billone, M.C.; Donne, M.D.; Macaulay-Newcombe, R.G.

1994-05-01

Beryllium is a leading candidate material for the neutron multiplier of tritium breeding blankets and the plasma facing component of first wall and divertor systems. Depending on the application, the fabrication methods proposed include hot-pressing, hot-isostatic-pressing, cold isostatic pressing/sintering, rotary electrode processing and plasma spraying. Product forms include blocks, tubes, pebbles, tiles and coatings. While, in general, beryllium is not a leading structural material candidate, its mechanical performance, as well its performance with regard to sputtering, heat transport, tritium retention/release, helium-induced swelling and chemical compatibility, is an important consideration in first-wall/blanket design. Differential expansion within the beryllium causes internal stresses which may result in cracking, thereby affecting the heat transport and barrier performance of the material. Overall deformation can result in loading of neighboring structural material. Thus, in assessing the performance of beryllium for fusion applications, it is important to have a good database in all of these performance areas, as well as a set of properties correlations and models for the purpose of interpolation/extrapolation

Critical parameters controlling irradiation swelling in beryllium

International Nuclear Information System (INIS)

Dubinko, V.I.

1995-01-01

Radiation effects in beryllium can hardly be explained within a framework of the conventional theory based on the bias concept due to elastic interaction difference (EID) between vacancies and self-interstitial atoms (SIAs) since beryllium belongs to hexagonal close-packed metals where diffusion has been shown to be anisotropic. Diffusional anisotropy difference (DAD) between point defects changes the cavity bias for their absorption and leads to dependence of the dislocation bias on the distribution of dislocations over crystallographic directions. On the other hand, the elastic interaction between point defects and cavities gives rise to the size and gas pressure dependencies of the cavity bias, resulting in new critical quantities for bubble-void transition effects at low temperature irradiation. In the present paper, we develop the concept of the critical parameters controlling irradiation swelling with account of both DAD and EID, and take care of thermal effects as well since they are of major importance for beryllium which has an anomalously low self-diffusion activation energy. Experimental data on beryllium swelling are analyzed on the basis of the present theory. (orig.)

Design features of the KSTAR in-vessel control coils

Energy Technology Data Exchange (ETDEWEB)

Kim, H.K. [National Fusion Research Institute (NFRI), 52 Yeoeun-dong, Yusung-ku, Daejeon, 305-333 (Korea, Republic of)], E-mail: hkkim@nfri.re.kr; Yang, H.L.; Kim, G.H.; Kim, Jin-Yong; Jhang, Hogun; Bak, J.S.; Lee, G.S. [National Fusion Research Institute (NFRI), 52 Yeoeun-dong, Yusung-ku, Daejeon, 305-333 (Korea, Republic of)

2009-06-15

In-vessel control coils (IVCCs) are to be used for the fast plasma position control, field error correction (FEC), and resistive wall mode (RWM) stabilization for the Korea Superconducting Tokamak Advanced Research (KSTAR) device. The IVCC system comprises 16 segments to be unified into a single set to achieve following remarkable engineering advantages; (1) enhancement of the coil system reliability with no welding or brazing works inside the vacuum vessel, (2) simplification in fabrication and installation owing to coils being fabricated outside the vacuum vessel and installed after device assembly, and (3) easy repair and maintenance of the coil system. Each segment is designed in 8 turns coil of 32 mm x 15 mm rectangular oxygen free high conductive copper with a 7 mm diameter internal coolant hole. The conductors are enclosed in 2 mm thick Inconel 625 rectangular welded vacuum jacket with epoxy/glass insulation. Structural analyses were implemented to evaluate structural safety against electromagnetic loads acting on the IVCC for the various operation scenarios using finite element analysis. This paper describes the design features and structural analysis results of the KSTAR in-vessel control coils.

Beryllium. Health hazards and their control. Pt. 2

International Nuclear Information System (INIS)

Lires, O.A.; Delfino, C.A.; Botbol, J.

1991-01-01

In this work (continuation of 'Beryllium' series) health hazards, toxic effects, limits of permissible atmospheric contamination and safe exposure to beryllium are described. Guidelines to the design, control operations and hygienic precautions of the working facilities are given. (Author) [es

Beryllium phonon spectrum from cold neutron measurements

International Nuclear Information System (INIS)

Bulat, I.A.

1979-01-01

The inelastic coherent scattering of neutrons with the initial energy E 0 =4.65 MeV on the spectrometer according to the time of flight is studied in polycrystalline beryllium. The measurements are made for the scattering angles THETA=15, 30, 45, 60, 75 and 90 deg at 293 K. The phonon spectrum of beryllium, i-e. g(w) is reestablished from the experimental data. The data obtained are compared with the data of model calculations. It is pointed out that the phonon spectrum of beryllium has a bit excessive state density in the energy range from 10 to 30 MeV. It is caused by the insufficient statistical accuracy of the experiment at low energy transfer

Theoretical and computational studies of entangled rod-coil block copolymer diffusion

Science.gov (United States)

Wang, Muzhou; Alexander-Katz, Alfredo; Olsen, B. D.

2012-02-01

Despite continued interest in the thermodynamics of rod-coil block copolymers for functional nanostructured materials in organic electronics and biomaterials, relatively few studies have investigated the dynamics of these systems which are important for understanding diffusion, mechanics, and self-assembly kinetics. Here, the diffusion of coil-rod-coil block copolymers through entangled melts is simulated using the Kremer-Grest molecular dynamics model, demonstrating that the mismatch between the curvature of the rod and coil blocks results in dramatically slower reptation through the entanglement tube. For rod lengths near the tube diameter, this hindered diffusion is explained by a local curvature-dependent free energy penalty produced by the curvature mismatch, resulting in a rough energy surface as the rod moves along the tube contour. Compared to coil homopolymers which reptate freely along the tube, rod-coil block copolymers undergo an activated diffusion process which is considerably slower as the rod length increases. For large rods, diffusion of the rod through the tube only occurs when the coil blocks occupy straight entanglement tubes, which requires ``arm retraction'' as the dominant relaxation mechanism.

Making an Inexpensive Electromagnetic Wiggler Using Sheet Materials for the Coils

CERN Document Server

Herman-Biallas, George; Hiatt, Thomas; Neil, George; Snyder, Michael

2004-01-01

An inexpensive electromagnetic wiggler, made with twenty-eight, 4 cm periods with a K of 1 and gap of 2.6 cm was made within 10 weeks after receipt of order by an industrial machine shop. The coil design used sheet and plate materials cut to shapes using water jet cutting and was assembled in a simple stack design. The coil design extends the serpentine conductor design of the Duke OK4 to more and smaller conductors. The coils are conduction cooled to imbedded cooling plates. The wiggler features graded end pole fields, trim coil compensation for end field errors and mirror plates on the ends to avoid three dimensional end field effects. Details of the methods used in construction and the wiggler performance are presented.

Lessons Learned During the Manufacture of the NCSX Modular Coils

International Nuclear Information System (INIS)

Chrzanowski, James H.; Meighan, Thomas G.; Raftopoulos, Steven; Dudek, Lawrence; Fogarty, Paul J.

2009-01-01

The National Compact Stellarator Experiment's (NCSX) modular coils presented a number of engineering and manufacturing challenges due to their complex shapes, requirements for high dimensional accuracy and high current density requirements due to space constraints. Being the first of their kind, these coils required the implementation of many new manufacturing and measuring techniques and procedures. This was the first time that these manufacturing techniques and methods were applied in the production of coils at the laboratory. This resulted in a steep learning curve for the first several coils. Through the effective use of procedures, tooling modifications, involvement and ownership by the manufacturing workforce, and an emphasis on safety, the assembly team was able to reduce the manufacturing times and improve upon the manufacturing methods. This paper will discuss the learning curve and steps that were taken to improve the manufacturing efficiency and reduce the manufacturing times for the modular coils without forfeiting quality

ICT diagnostic method of beryllium welding quality

International Nuclear Information System (INIS)

Sun Lingxia; Wei Kentang; Ye Yunchang

2002-01-01

To avoid the interference of high density material for the quality assay of beryllium welding line, a slice by slice scanning method was proposed based upon the research results of the Industrial Computerized Tomography (ICT) diagnostics for weld penetration, weld width, off-centered deviation and weld defects of beryllium-ring welding seam with high density material inside

European Fusion Programme. ITER task T23: Beryllium characterisation. Progress report. Tensile tests on neutron irradiated and reference beryllium

International Nuclear Information System (INIS)

Moons, F.

1996-02-01

As part of the European Technology Fusion Programme, the irradiation embrittlement characteristics of the more ductile and isotopic grades of beryllium manufactured by Brush Wellman has been investigated using modern powder production and consolidation techniques . This study was initiated in support of the development and evaluation of beryllium as a neutron multiplier for the solid breeder blanket design concepts proposed for a DEMO fusion power reactor. Four different species of beryllium: S-200 F (vacuum hot pressed, 1.2 wt% BeO), S-200FH (hot isostatic pressed, 0.9 wt% BeO), S-65 (vacuum hot pressed, 0.6 wt% BeO), S-65H (hot isostatic pressed, 0.5 wt% BeO) have been compared. Three batches of the beryllium have been investigated, a neutron batch, a thermal control batch and a reference batch. Neutron irradiation has been performed at temperatures between 175 and 605 degrees Celsius up to a neutron fluence of 2.1 10 25 n.m -2 (E> 1 MeV) or 750 appm He. The results of the tensile tests are summarized

Molecular basis of coiled-coil oligomerization-state specificity.

Science.gov (United States)

Ciani, Barbara; Bjelic, Saša; Honnappa, Srinivas; Jawhari, Hatim; Jaussi, Rolf; Payapilly, Aishwarya; Jowitt, Thomas; Steinmetz, Michel O; Kammerer, Richard A

2010-11-16

Coiled coils are extensively and successfully used nowadays to rationally design multistranded structures for applications, including basic research, biotechnology, nanotechnology, materials science, and medicine. The wide range of applications as well as the important functions these structures play in almost all biological processes highlight the need for a detailed understanding of the factors that control coiled-coil folding and oligomerization. Here, we address the important and unresolved question why the presence of particular oligomerization-state determinants within a coiled coil does frequently not correlate with its topology. We found an unexpected, general link between coiled-coil oligomerization-state specificity and trigger sequences, elements that are indispensable for coiled-coil formation. By using the archetype coiled-coil domain of the yeast transcriptional activator GCN4 as a model system, we show that well-established trimer-specific oligomerization-state determinants switch the peptide's topology from a dimer to a trimer only when inserted into the trigger sequence. We successfully confirmed our results in two other, unrelated coiled-coil dimers, ATF1 and cortexillin-1. We furthermore show that multiple topology determinants can coexist in the same trigger sequence, revealing a delicate balance of the resulting oligomerization state by position-dependent forces. Our experimental results should significantly improve the prediction of the oligomerization state of coiled coils. They therefore should have major implications for the rational design of coiled coils and consequently many applications using these popular oligomerization domains.

5. IEA International workshop on beryllium technology for fusion. Book of abstracts

Energy Technology Data Exchange (ETDEWEB)

NONE

2001-07-01

The collection includes the abstracts of reports presented to the 5-th IEA international workshop on beryllium technology for fusion. The themes of reports are as follows: status of beryllium technology for fusion in Russia; manufacturing and testing of Be armoured first wall mock-up for ITER; development of the process of diffusion welding of metals stainless steel-copper-beryllium into a single composite; some features of beryllium-laser beam interaction; the effect of irradiation dose on tritium and helium release from neutron irradiated beryllium; thermal properties of neutron irradiated Be{sub 12}Ti. The results of investigating the mechanical properties variation and swelling of beryllium under high temperature neutron irradiation are presented.

5. IEA International workshop on beryllium technology for fusion. Book of abstracts

International Nuclear Information System (INIS)

2001-01-01

The collection includes the abstracts of reports presented to the 5-th IEA international workshop on beryllium technology for fusion. The themes of reports are as follows: status of beryllium technology for fusion in Russia; manufacturing and testing of Be armoured first wall mock-up for ITER; development of the process of diffusion welding of metals stainless steel-copper-beryllium into a single composite; some features of beryllium-laser beam interaction; the effect of irradiation dose on tritium and helium release from neutron irradiated beryllium; thermal properties of neutron irradiated Be 12 Ti. The results of investigating the mechanical properties variation and swelling of beryllium under high temperature neutron irradiation are presented [ru

Tritium behavior in ITER beryllium

International Nuclear Information System (INIS)

Longhurst, G.R.

1990-10-01

The beryllium neutron multiplier in the ITER breeding blanket will generate tritium through transmutations. That tritium constitutes a safety hazard. Experiments evaluating tritium storage and release mechanisms have shown that most of the tritium comes out in a burst during thermal ramping. A small fraction of retained tritium is released by thermally activated processes. Analysis of recent experimental data shows that most of the tritium resides in helium bubbles. That tritium is released when the bubbles undergo swelling sufficient to develop porosity that connects with the surface. That appears to occur when swelling reaches about 10--15%. Other tritium appears to be stored chemically at oxide inclusions, probably as Be(OT) 2 . That component is released by thermal activation. There is considerable variation in published values for tritium diffusion through the beryllium and solubility in it. Data from experiments using highly irradiated beryllium from the Idaho National Engineering Laboratory showed diffusivity generally in line with the most commonly accepted values for fully dense material. Lower density material, planned for use in the ITER blanket may have very short diffusion times because of the open structure. The beryllium multiplier of the ITER breeding blanket was analyzed for tritium release characteristics using temperature and helium production figures at the midplane generated in support of the ITER Summer Workshop, 1990 in Garching. Ordinary operation, either in Physics or Technology phases, should not result in the release of tritium trapped in the helium bubbles. Temperature excursions above 600 degree C result in large-scale release of that tritium. 29 refs., 10 figs., 3 tabs

Design of Nb3Sn Coils for LARP Long Magnets

International Nuclear Information System (INIS)

Ferracin, Paolo; Ambrosio, G.; Andreev, N.; Anerella, M.; Barzi, E.; Bossert, R.; Ferracin, P.; Caspi, S.; Lietzke, A. F.

2007-01-01

The LHC Accelerator Research Program (LARP) has a primary goal to develop, assemble, and test full size Nb 3 Sn quadrupole magnet models for a luminosity upgrade of the Large Hadron Collider (LHC). A major milestone in this development is to assemble and test, by the end of 2009, two 4 m-long quadrupole cold masses, which will be the first Nb 3 Sn accelerator magnet models approaching the length of real accelerator magnets. The design is based on the LARP Technological Quadrupoles (TQ), under development at FNAL and LBNL, with gradient higher than 200 T/m and aperture of 90 mm. The mechanical design will be chosen between two designs presently explored for the TQs: traditional collars and Al-shell based design (preloaded by bladders and keys). The fabrication of the first long quadrupole model is expected to start in the last quarter of 2007. Meanwhile the fabrication of 4 m-long racetrack coils started this year at BNL. These coils will be tested in an Al-shell based supporting structure developed at LBNL. Several challenges have to be addressed for the successful fabrication of long Nb 3 Sn coils. This paper presents these challenges with comments and solutions adopted or under study for these magnets. The coil design of these magnets, including conductor and insulation features, and quench protection studies are also presented

Design of Nb3Sn coils for LARP long magnets

International Nuclear Information System (INIS)

Ambrosio, G.; Andreev, N.; Anerella, M.; Barzi, E.; Bossert, R.; Dietderich, D.; Feher, S.; Ferracin, P.; Ghosh, A.; Gourlay, S.; Kashikhin, V.V.; Lietzke, A.; McInturff, A.; Muratore, J.; Nobrega, F.; Sabbi, G.L.; Schmalzle, J.; Wanderer, P.; Zlobin, A.V.; Fermilab; Brookhaven; LBL, Berkeley; Texas A-M

2006-01-01

The LHC Accelerator Research Program (LARP) has a primary goal to develop, assemble, and test full size Nb 3 Sn quadrupole magnet models for a luminosity upgrade of the Large Hadron Collider (LHC). A major milestone in this development is to assemble and test, by the end of 2009, two 4m-long quadrupole cold masses, which will be the first Nb3Sn accelerator magnet models approaching the length of real accelerator magnets. The design is based on the LARP Technological Quadrupoles (TQ), under development at FNAL and LBNL, with gradient higher than 200 T/m and aperture of 90 mm. The mechanical design will be chosen between two designs presently explored for the TQs: traditional collars and Al-shell based design (preloaded by bladders and keys). The fabrication of the first long quadrupole model is expected to start in the last quarter of 2007. Meanwhile the fabrication of 4m-long racetrack coils started this year at BNL. These coils will be tested in an Al-shell based supporting structure developed at LBNL. Several challenges have to be addressed for the successful fabrication of long Nb 3 Sn coils. This paper presents these challenges with comments and solutions adopted or under study for these magnets. The coil design of these magnets, including conductor and insulation features, and quench protection studies are also presented

Novel plasma source for safe beryllium spectral line studies in the presence of beryllium dust

Science.gov (United States)

Stankov, B. D.; Vinić, M.; Gavrilović Božović, M. R.; Ivković, M.

2018-05-01

Plasma source for beryllium spectral line studies in the presence of beryllium dust particles was realised. The guideline during construction was to prevent exposure to formed dust, considering the toxicity of beryllium. Plasma source characterization through determination of optimal working conditions is described. The necessary conditions for Be spectral line appearance and optimal conditions for line shape measurements are found. It is proven experimentally that under these conditions dust appears coincidently with the second current maximum. The electron density measured after discharge current maximum is determined from the peak separation of the hydrogen Balmer beta spectral line, and the electron temperature is determined from the ratios of the relative intensities of Be spectral lines emitted from successive ionized stages of atoms. Maximum values of electron density and temperature are measured to be 9.3 × 1022 m-3 and 16 800 K, respectively. Construction details and testing of the BeO discharge tube in comparison with SiO2 and Al2O3 discharge tubes are also presented in this paper.

Hydrodynamic instabilities in beryllium targets for the National Ignition Facility

Energy Technology Data Exchange (ETDEWEB)

Yi, S. A., E-mail: austinyi@lanl.gov; Simakov, A. N.; Wilson, D. C.; Olson, R. E.; Kline, J. L.; Batha, S. H. [Los Alamos National Laboratory, P.O. Box 1663, Los Alamos, New Mexico 87545 (United States); Clark, D. S.; Hammel, B. A.; Milovich, J. L.; Salmonson, J. D.; Kozioziemski, B. J. [Lawrence Livermore National Laboratory, P.O. Box 808, Livermore, California 94551 (United States)

2014-09-15

Beryllium ablators offer higher ablation velocity, rate, and pressure than their carbon-based counterparts, with the potential to increase the probability of achieving ignition at the National Ignition Facility (NIF) [E. I. Moses et al., Phys. Plasmas 16, 041006 (2009)]. We present here a detailed hydrodynamic stability analysis of low (NIF Revision 6.1) and high adiabat NIF beryllium target designs. Our targets are optimized to fully utilize the advantages of beryllium in order to suppress the growth of hydrodynamic instabilities. This results in an implosion that resists breakup of the capsule, and simultaneously minimizes the amount of ablator material mixed into the fuel. We quantify the improvement in stability of beryllium targets relative to plastic ones, and show that a low adiabat beryllium capsule can be at least as stable at the ablation front as a high adiabat plastic target.

Fabrication of the new poloidal field coils for DIII-D

International Nuclear Information System (INIS)

Heiberger, M.; Bott, R.J.; Gallix, R.; Street, R.W.

1986-01-01

The six new poloidal field coil assemblies manufactured by GA Technologies (GA) for DIII-D range in diameter from 3.4-5.3 m. Two of them are 55-turn field shaping coils. Each of the other four combines one turn of the ohmic heating coil and a 55-turn field shaping coil into a single unit encased in a stainless steel box beam. These four box beams, which provide support for the coils inside, are part of the overall coil and vacuum vessel support structure. They also serve as molds for vacuum impregnating the coils with epoxy. All coils are made of hollow, water-cooled copper conductor. The larger field shaping coils are designed for 20 kA, 3 sec rectangular current pulses with 40 0 C temperature rise. The ohmic heating coil turns are capable of currents of up to 110 kA. The conductor is wrapped with Kapton and fiberglass tape; Kapton provides 1000 V/turn and 28 kV coil-to-ground insulation. The fiberglass acts as wick and reinforcement for the vacuum impregnated epoxy resin which bonds the coil together. The fabrication process is described in detail and illustrated. Tools and setups used for special operations such as induction brazing, conductor winding, conductor bending, and vacuum impregnation are presented. The quality control procedures followed to guarantee sound brazed joints are explained. The electrical tests performed at several stages of fabrication, especially the 1000 V/turn impulse tests conducted before potting to facilitate fault detection and repair, are described

Characterization of Chiral Carbonaceous Nanotubes Prepared from Four Coiled Tubular 4,4'-biphenylene-silica Nanoribbons

Directory of Open Access Journals (Sweden)

Shuwei Lin

2014-04-01

Full Text Available Four dipeptides derived from phenylalanine were synthesized, which can self-assemble into twisted nanoribbon in deionized water. The handedness of the organic self-assemblies was controlled by the chirality of the phenylalanine at the terminals. Coiled 4,4'-biphenylene bridged polybissilsesquioxane tubular nanoribbons were prepared using the organic self-assemblies as the templates. The circular dichroism spectra indicated that the biphenylene rings preferred to twist in one-handedness within the walls of the samples. After carbonization and removal of silica, single-handed coiled carbonaceous tubular nanoribbons were obtained. The Raman spectra indicated that the carbon was amorphous. The diffuse reflectance circular dichroism spectra indicated the tubular carbonaceous nanoribbons exhibited optical activity.

Interaction of hydrogen and its isotopes with irradiated beryllium

International Nuclear Information System (INIS)

Tazhibaeva, I.L.; Shestakov, V.P.; Klepikov, A.Kh.; Pomanenko, O.G.; Chikhraj, E.V.; Kenzhin, E.A.; Zverev, V.V.; Kolbanenkov, A.N.

2000-01-01

In the article the results of experiments on hydrogen and its isotopes accumulation and gas-release from irradiated beryllium are presented. The irradiation was conducted at different media and temperatures in the RA and IVG.1M reactors. The measurements were carried out by thermal desorption method. Hydrogen release from beryllium samples saturated at different conditions were calculated. Dependence of hydrogen confinement character in beryllium from grain orientation in the sample, temperature and irradiation rate was revealed

Compatibility of stainless steels and lithiated ceramics with beryllium

Science.gov (United States)

Flament, T.; Fauvet, P.; Sannier, J.

1988-07-01

The introduction of beryllium as a neutron multiplier in ceramic blankets of thermonuclear fusion reactors may give rise to the following compatibility problems: (i) oxidation of Be by ceramics (lithium aluminate and silicates) or by water vapour; (ii) interaction between beryllium and austenitic and martensitic steels. The studies were done in contact tests under vacuum and in tests under wet sweeping helium. The contact tests under vacuum have revealed that the interaction of beryllium with ceramics seems to be low up to 700°C, the interaction of beryllium with steels is significant and is characterized by the formation of a diffusion layer and of a brittle Be-Fe-Ni compound. With type 316 L austenitic steel, this interaction appears quite large at 600°C whereas it is noticeable only at 700°C with martensitic steels. The experiments carried out with sweeping wet helium at 600°C have evidenced a slight oxidation of beryllium due to water vapour which can be enhanced in the front of uncompletely dehydrated ceramics.

Structure/property relationships in multipass GMA welding of beryllium.

Energy Technology Data Exchange (ETDEWEB)

Hochanadel, P. W. (Patrick W.); Hults, W. L. (William L.); Thoma, D. J. (Dan J.); Dave, V. R. (Vivek R.); Kelly, A. M. (Anna Marie); Pappin, P. A. (Pallas A.); Cola, M. J. (Mark J.); Burgardt, P. (Paul)

2001-01-01

Beryllium is an interesting metal that has a strength to weight ratio six times that of steel. Because of its unique mechanical properties, beryllium is used in aerospace applications such as satellites. In addition, beryllium is also used in x-ray windows because it is nearly transparent to x-rays. Joining of beryllium has been studied for decades (Ref.l). Typically joining processes include braze-welding (either with gas tungsten arc or gas metal arc), soldering, brazing, and electron beam welding. Cracking which resulted from electron beam welding was recently studied to provide structure/property relationships in autogenous welds (Ref. 2). Braze-welding utilizes a welding arc to melt filler, and only a small amount of base metal is melted and incorporated into the weld pool. Very little has been done to characterize the braze-weld in terms of the structure/property relationships, especially with reference to multipass welding. Thus, this investigation was undertaken to evaluate the effects of multiple passes on microstructure, weld metal composition, and resulting material properties for beryllium welded with aluminum-silicon filler metal.

The results of medical surveillance of beryllium production personnel

International Nuclear Information System (INIS)

Koviazin, A.; Urikh, A.; Kovianzina, L.

2004-01-01

The report presents results of surveillance of 1836 workers of beryllium production of Ulba Metallurgical Plant JSC with the acute and chronic forms of occupation diseases for 52 years of its operation. The dependence of acute and chronic occupation lesions on the protection degree is shown. It has been found out that, the risk of getting an occupation disease increases sharply at the moments of experimental works and at the time of reconstruction and some other extreme conditions in the production, that is supported by fixed lesions of eye mucous coat, skin and lung lesions. In this case, the readiness of people for their work in deleterious conditions and their personal responsibility for following the regulations of safety occupational standards plays a definite role. Therefore, the issues of protection are of paramount importance in prophylaxis both of acute and chronic exposure to beryllium. An influence of duration of service and occupation on chronic beryllium diseases is shown. A parallel between the lung beryllium disease and skin lesions by insoluble beryllium compounds is drawn for the first time. (author)

Spectrographic determination of impurities in beryllium oxide

International Nuclear Information System (INIS)

Paula Reino, L.C. de; Lordello, A.R.; Pereira, A.S.A.

1986-03-01

A method for the spectrographic determination of Al, B, Cd, Co, Cu, Cr, Fe, Mg, NaNi, Si and Zn in nuclear grade beryllium oxide has been developed. The determination of Co, Al, Na and Zn is besed upon a carrier distillation technique. Better results were obtained with 2% Ga 2 O 3 as carrier in beryllium oxide. For the elements B, Cd, Cu, Fe, Cr, Mg, Ni and Si the sample is loaded in a Scribner-Mullin shallow cup electrode, covered with graphite powder and excited in DC arc. The relative standard deviation values for different elements are in the range of 10 to 20%. The method fulfills requirements of precision and sensitivity for specification analysis of nuclear grade beryllium oxide.(Author) [pt

Progress report of preliminary studies of beryllium toxicity

Energy Technology Data Exchange (ETDEWEB)

Hodge, H.C.

1947-09-01

This document was prepared in connection with a symposium of beryllium poisoning held at the Saranac Laboratories and describes progress made and a research program aimed at characterizing the toxicity of beryllium. Seven individual papers in this document are separately indexed and cataloged for the database.

The effect of processing parameters on plasma sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Jacobson, L.A.; Cowgill, D.F.; Snead, L.L.

1993-01-01

Plasma spraying is being investigated as a potential coating technique for applying thin (0.1--5mm) layers of beryllium on plasma facing surfaces of blanket modules in ITER and also as an in-situ repair technique for repairing eroded beryllium surfaces in high heat flux divertor regions. High density spray deposits (>98% of theoretical density) of beryllium will be required in order to maximize the thermal conductivity of the beryllium coatings. A preliminary investigation was done to determine the effect of various processing parameters (particle size, particle morphology, secondary gas additions and reduced chamber pressure) on the as-deposited density of beryllium. The deposits were made using spherical beryllium feedstock powder which was produced by centrifugal atomization at Los Alamos National Laboratory (LANL). Improvements in the as-deposited densities and deposit efficiencies of the beryllium spray deposits will be discussed along with the corresponding thermal conductivity and outgassing behavior of these deposits

The effect of processing parameters on plasma sprayed beryllium for fusion applications

International Nuclear Information System (INIS)

Castro, R.G.; Stanek, P.W.; Jacobson, L.W.; Cowgill, D.F.

1993-01-01

Plasma spraying is being investigated as a potential coating technique for applying thin (0.1-5mm) layers of beryllium on plasma facing surfaces of blanket modules in ITER and also as an in-situ repair technique for repairing eroded beryllium surfaces in high heat flux divertor regions. High density spray deposits (>98% of theoretical density) of beryllium will be required in order to maximize the thermal conductivity of the beryllium coatings. A preliminary investigation was done to determine the effect of various processing parameters (particle size, particle morphology, secondary gas additions and reduced chamber pressure) on the as-deposited density of beryllium. The deposits were made using spherical beryllium feedstock powder which was produced by centrifugal atomization at Los Alamos National Laboratory (LANL). Improvements in the as-deposited densities and deposit efficiencies of the beryllium spray deposits will be discussed along with the corresponding thermal conductivity and outgassing behavior of these deposits. (orig.)

Beryllium coating produced by evaporation-condensation method and some their properties

Energy Technology Data Exchange (ETDEWEB)

Pepekin, G.I.; Anisimov, A.B.; Chernikov, A.S.; Mozherinn, S.I.; Pirogov, A.A. [SRI SIA Lutch., Podolsk (Russian Federation)

1998-01-01

The method of vacuum evaporation-condensation for deposition of beryllium coatings on metal substrates, considered in the paper, side by side with a plasma-spray method is attractive fon ITER application. In particular this technique may be useful for repair the surface of eroded tiles which is operated in a strong magnetic field. The possibility of deposition of beryllium coatings with the rate of layer growth 0.1-0.2 mm/h is shown. The compatibility of beryllium coating with copper or stainless steel substrate is provided due to intermediate barrier. The results of examination of microstructure, microhardness, porosity, thermal and physical properties and stability under thermal cycling of beryllium materials are presented. The value of thermal expansion coefficient and thermal conductivity of condensed beryllium are approximately the same as for industrial grade material produced by powder mettalurgy technique. However, the condensed beryllium has higher purity (up to 99.9-99.99 % wt.). (author)

Technical aspects of the joint JET-ISX-B beryllium limiter experiment

International Nuclear Information System (INIS)

Edmonds, P.H.; Dietz, K.J.; Mioduszewski, P.K.; Watson, R.D.; Emerson, L.C.; Gabbard, W.A.; Goodall, D.; Simpkins, J.E.; Yarber, J.L.

1985-01-01

An experiment has been performed on the Impurity Study Experiment (ISX-B) tokamak to test beryllium as a limiter material. Beryllium is an attractive candidate for a limiter and has been proposed for use in the Joint European Torus (JET) experiment. A temperature-controlled, segmented, beryllium top-rail limiter was located inside the plasma radius described by the existing titanium limiters. An extended set of diagnostics was added for measurement of scrapeoff and limiter parameters. These included visible and infrared monitoring systems, probes, and surface analysis experiments. Tokamak experiments included parameter surveys of both Ohmically heated and neutral-beam-heated plasmas and an extended fluence test of the limiter. The most significant effect of operation with a beryllium limiter was the reduction in low-Z impurities caused by gettering action of beryllium deposited on the liner walls. The experiment required the design and implementation of contamination control apparatus and work procedures to prevent the accidental dispersion of beryllium dust

Beryllium mock-ups development and ultrasonic testing for ITER divertor conditions

International Nuclear Information System (INIS)

Barabash, V.R.; Bykov, V.A.; Giniyatulin, R.N.; Gervash, A.A.; Gurieva, T.M.; Egorov, K.E.; Komarov, V.L.; Korolkov, M.D.; Mazul, I.V.; Gitarsky, L.S.; Strulia, I.L.; Sizenev, V.S.; Pronyakin, V.T.

1995-01-01

At the present time beryllium is considered as the most suitable armour material for the ITER divertor application. Different types of Be-divertor mock-up construction are compared in the report. Two different technologies of beryllium tiles joining to a heat sink body are analysed: high temperature brazing and thermodiffusion bonding. The comparative analysis of different constructions has been performed on the basis of 2-D finite element calculation for temperatures and stresses. The main parameters and diagnostic capabilities of electron beam facility for HHF testing of beryllium mock-ups are described. The first results of HHF tests of ''beryllium-copper saddle-MAGT tube'' and ''beryllium-copper plate-SS body'' mock-ups are presented. The reasons of the damages during the HHF are analysed. The technique of ultrasonic testing of the thermodifussion bonding and brazing quality for beryllium-copper joints is presented. The recorded results are prepared in the form of ultrasound grams. The testing results are compared with the metallographic analysis. (orig.)

Preparation and characterization of beryllium doped organic plasma polymer coatings

International Nuclear Information System (INIS)

Brusasco, R.; Letts, S.; Miller, P.; Saculla, M.; Cook, R.

1995-01-01

We report the formation of beryllium doped plasma polymerized coatings derived from a helical resonator deposition apparatus, using diethylberyllium as the organometaric source. These coatings had an appearance not unlike plain plasma polymer and were relatively stable to ambient exposure. The coatings were characterized by Inductively Coupled Plasma Mass Spectrometry and X-Ray Photoelectron Spectroscopy. Coating rates approaching 0.7 μm hr -1 were obtained with a beryllium-to-carbon ratio of 1:1.3. There is also a significant oxygen presence in the coating as well which is attributed to oxidation upon exposure of the coating to air. The XPS data show only one peak for beryllium with the preponderance of the XPS data suggesting that the beryllium exists as BeO. Diethylberyllium was found to be inadequate as a source for beryllium doped plasma polymer, due to thermal decomposition and low vapor recovery rates

Mechanical behavior of the mirror fusion test Facility superconducting magnet coils

International Nuclear Information System (INIS)

Horvath, J.A.

1980-01-01

The mechanical response to winding and electromagnetic loads of the Mirror Fusion Test Facility (MFTF) superconducting coil pack is presented. The 375-ton (3300 N) MFTF Yin-Yang magnet, presently the world's largest superconducting magnet, is scheduled for acceptance cold-testing in May of 1981. The assembly is made up of two identical coils which together contain over 15 miles (24 km) of superconductor wound in 58 consecutive layers of 24 turns each. Topics associated with mechanical behavior include physical properties of the coil pack and its components, winding pre-load effects, finite element analysis, magnetic load redistribution, and the design impact of predicted conductor motion

Neutron irradiation behavior of ITER candidate beryllium grades

Energy Technology Data Exchange (ETDEWEB)

Kupriyanov, I.B.; Gorokhov, V.A.; Nikolaev, G.N. [A.A.Bochvar All-Russia Scientific Research Inst. of Inorganic Materials (VNIINM), Moscow (Russian Federation); Melder, R.R.; Ostrovsky, Z.E.

1998-01-01

Beryllium is one of the main candidate materials both for the neutron multiplier in a solid breeding blanket and for the plasma facing components. That is why its behaviour under the typical for fusion reactor loading, in particular, under the neutron irradiation is of a great importance. This paper presents mechanical properties, swelling and microstructure of six beryllium grades (DshG-200, TR-30, TshG-56, TRR, TE-30, TIP-30) fabricated by VNIINM, Russia and also one - (S-65) fabricated by Brush Wellman, USA. The average grain size of the beryllium grades varied from 8 to 25 {mu}m, beryllium oxide content was 0.8-3.2 wt. %, initial tensile strength was 250-680 MPa. All the samples were irradiated in active zone of SM-3 reactor up to the fast neutron fluence (5.5-6.2) {center_dot} 10{sup 21} cm{sup -2} (2.7-3.0 dpa, helium content up to 1150 appm), E > 0.1 MeV at two temperature ranges: T{sub 1} = 130-180degC and T{sub 2} = 650-700degC. After irradiation at 130-180degC no changes in samples dimensions were revealed. After irradiation at 650-700degC swelling of the materials was found to be in the range 0.1-2.1 %. Beryllium grades TR-30 and TRR, having the smallest grain size and highest beryllium oxide content, demonstrated minimal swelling, which was no more than 0.1 % at 650-700degC and fluence 5.5 {center_dot} 10{sup 21} cm{sup -2}. Tensile and compression test results and microstructure parameters measured before and after irradiation are also presented. (author)

Erosion of beryllium under ITER – Relevant transient plasma loads

International Nuclear Information System (INIS)

Kupriyanov, I.B.; Nikolaev, G.N.; Kurbatova, L.A.; Porezanov, N.P.; Podkovyrov, V.L.; Muzichenko, A.D.; Zhitlukhin, A.M.; Gervash, A.A.; Safronov, V.M.

2015-01-01

Highlights: • We study the erosion, mass loss/gain and surface structure evolution of Be/CuCrZr mock-ups, armored with beryllium of TGP-56FW grade after irradiation by deuterium plasma heat load of 0.5 MJ/m 2 at 250 °C and 500 °C. • Beryllium mass loss/erosion under plasma heat load at 250 °C is rather small (no more than 0.2 g/m 2 shot and 0.11 μm/shot, correspondingly, after 40 shots) and tends to decrease with increasing number of shots. • Beryllium mass loss/erosion under plasma heat load at 500 °C is much higher (∼2.3 g/m 2 shot and 1.2 μm/shot, correspondingly, after 10 shot) and tends to decrease with increasing the number of shots (∼0.26 g/m 2 pulse and 0.14 μm/shot, correspondingly, after 100 shot). • Beryllium erosion value derived from the measurements of profile of irradiated surface is much higher than erosion value derived from mass loss data. - Abstract: Beryllium will be used as a armor material for the ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of the ITER first wall. This paper presents the results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility. The Be/CuCrZr mock-ups were exposed to up to 100 shots by deuterium plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat loads range of 0.2–0.5 MJ/m 2 at different temperature of beryllium tiles. The temperature of Be tiles has been maintained about 250 and 500 °C during the experiments. After 10, 40 and 100 shots, the beryllium mass loss/gain under erosion process were investigated as well as evolution of surface microstructure and cracks morphology

Erosion of beryllium under ITER – Relevant transient plasma loads

Energy Technology Data Exchange (ETDEWEB)

Kupriyanov, I.B., E-mail: igkupr@gmail.com [A.A. Bochvar High Technology Research Institute of Inorganic Materials, Rogova St. 5a, 123060 Moscow (Russian Federation); Nikolaev, G.N.; Kurbatova, L.A.; Porezanov, N.P. [A.A. Bochvar High Technology Research Institute of Inorganic Materials, Rogova St. 5a, 123060 Moscow (Russian Federation); Podkovyrov, V.L.; Muzichenko, A.D.; Zhitlukhin, A.M. [TRINITI, Troitsk, Moscow reg. (Russian Federation); Gervash, A.A. [Efremov Research Institute, S-Peterburg (Russian Federation); Safronov, V.M. [Project Center of ITER, Moscow (Russian Federation)

2015-08-15

Highlights: • We study the erosion, mass loss/gain and surface structure evolution of Be/CuCrZr mock-ups, armored with beryllium of TGP-56FW grade after irradiation by deuterium plasma heat load of 0.5 MJ/m{sup 2} at 250 °C and 500 °C. • Beryllium mass loss/erosion under plasma heat load at 250 °C is rather small (no more than 0.2 g/m{sup 2} shot and 0.11 μm/shot, correspondingly, after 40 shots) and tends to decrease with increasing number of shots. • Beryllium mass loss/erosion under plasma heat load at 500 °C is much higher (∼2.3 g/m{sup 2} shot and 1.2 μm/shot, correspondingly, after 10 shot) and tends to decrease with increasing the number of shots (∼0.26 g/m{sup 2} pulse and 0.14 μm/shot, correspondingly, after 100 shot). • Beryllium erosion value derived from the measurements of profile of irradiated surface is much higher than erosion value derived from mass loss data. - Abstract: Beryllium will be used as a armor material for the ITER first wall. It is expected that erosion of beryllium under transient plasma loads such as the edge-localized modes (ELMs) and disruptions will mainly determine a lifetime of the ITER first wall. This paper presents the results of recent experiments with the Russian beryllium of TGP-56FW ITER grade on QSPA-Be plasma gun facility. The Be/CuCrZr mock-ups were exposed to up to 100 shots by deuterium plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat loads range of 0.2–0.5 MJ/m{sup 2} at different temperature of beryllium tiles. The temperature of Be tiles has been maintained about 250 and 500 °C during the experiments. After 10, 40 and 100 shots, the beryllium mass loss/gain under erosion process were investigated as well as evolution of surface microstructure and cracks morphology.

Testing of beryllium marker coatings in PISCES-B for the JET ITER-like wall

International Nuclear Information System (INIS)

Widdowson, A.; Baldwin, M.J.; Coad, J.P.; Doerner, R.P.; Hanna, J.; Hole, D.E.; Matthews, G.F.; Rubel, M.; Seraydarian, R.; Xu, H.

2009-01-01

Beryllium has been chosen as the first wall material for ITER. In order to understand the issues of material migration and tritium retention associated with the use of beryllium, a largely beryllium first wall will be installed in JET. As part of the JET ITER-like wall, beryllium tiles with marker coatings are proposed as a diagnostic tool for studying the erosion and deposition of beryllium around the vessel. The nominal structure for these coatings is a ∼10 μm beryllium surface layer separated from the beryllium tile by a 2-3 μm metallic inter-layer. Two types of coatings are tested here; one with a nickel inter-layer and one with a copper/beryllium mixed inter-layer. The coating samples were deposited by DC magnetron sputtering at General Atomics and were exposed to deuterium plasma in PISCES-B. The results of this testing show that the beryllium/nickel marker coating would be suitable for installation in JET.

Large coil task and results of testing US coils

International Nuclear Information System (INIS)

Haubenreich, P.N.

1986-01-01

The United States, EURATOM, Japan, and Switzerland have collaborated since 1978 in development of superconducting toroidal field coils for fusion reactor applications. The United States provided a test facility nd three coils; the other participants, one coil each. All coils have the same interface dimensions and performance requirements (stable at 8 T), but internal design was decided by each team. Two US coil teams chose bath-cooled NbTi, 10-kA conductors. One developed a Nb 3 Sn conductor, cooled by internal flow, rated at 18 kA. All US coils have diagnostic instrumentation and imbedded heaters that enable stability tests and simulated nuclear heating experiments. In single-coil tests, each coil operated at full current in self-field (6.4 T). In six-coil tests that began in July 1986, one US coil and the Japanese coil hve been successfully operated at full current at 8 T. The other coils have operated as background coils while awaiting their turn as test coil. Coil tests have been informative and results gratifying. The facility has capably supported coil testing and its operation has provided information that will be useful in designing future fusion systems. Coil capabilities beyond nominal design points will be determined

Experimental studies and modeling of processes of hydrogen isotopes interaction with beryllium

Energy Technology Data Exchange (ETDEWEB)

Tazhibaeva, I.L.; Chikhray, Y.V.; Romanenko, O.G.; Klepikov, A.Kh.; Shestakov, V.P.; Kulsartov, T.V. [Science Research Inst. of Experimental and Theoretical Physics of Kazakh State Univ., Almaty (Kazakhstan); Kenzhin, E.A.

1998-01-01

The objective of this work was to clarify the surface beryllium oxide influence on hydrogen-beryllium interaction characteristics. Analysis of experimental data and modeling of processes of hydrogen isotopes accumulation, diffusion and release from neutron irradiated beryllium was used to achieve this purpose as well as the investigations of the changes of beryllium surface element composition being treated by H{sup +} and Ar{sup +} plasma glowing discharge. (author)

Protection of air in premises and environment against beryllium aerosols

Energy Technology Data Exchange (ETDEWEB)

Bitkolov, N.Z.; Vishnevsky, E.P.; Krupkin, A.V. [Research Inst. of Industrial and Marine Medicine, St. Petersburg (Russian Federation)

1998-01-01

First and foremost, the danger of beryllium aerosols concerns a possibility of their inhalation. The situation is aggravated with high biological activity of the beryllium in a human lung. The small allowable beryllium aerosols` concentration in air poses a rather complex and expensive problem of the pollution prevention and clearing up of air. The delivery and transportation of beryllium aerosols from sites of their formation are defined by the circuit of ventilation, that forms aerodynamics of air flows in premises, and aerodynamic links between premises. The causes of aerosols release in air of premises from hoods, isolated and hermetically sealed vessels can be vibrations, as well as pulses of temperature and pressure. Furthermore, it is possible the redispersion of aerosols from dirty surfaces. The effective protection of air against beryllium aerosols at industrial plants is provided by a complex of hygienic measures: from individual means of breath protection up to collective means of the prevention of air pollution. (J.P.N.)

Cause of pitting in beryllium

International Nuclear Information System (INIS)

Kershaw, R.P.

1982-01-01

Light microscopy, bare-film radiography, secondary ion mass spectroscopy, electron microprobe and physical testing were used to examine beryllium specimens exhibiting a stratified, pitted, pattern after chemical milling. The objective was to find the cause of this pattern. Specimens were found to have voids in excess of density specification allowances. These voids are attributed, at least in part, to the sublimation of beryllium fluoride during the vacuum hot pressing operation. The origin of the pattern is attributed to these voids and etching out of fines and associated impurities. Hot isostatic pressing with a subsequent heat treatment close residual porosity and dispersed impurities enough to correct the problem

Thermal conductivity of beryllium under low temperature high dose neutron irradiation

International Nuclear Information System (INIS)

Chakin, V.P.; Latypov, R.N.; Suslov, D.N.; Kupriyanov, I.B.

2004-01-01

Thermal conductivity of compact beryllium of several Russian grades such as TE-400, TE-56, TE-30, TIP and DIP differing in the production technology, grain size and impurity content has been investigated. The thermal diffusivity of beryllium was measured on the disks in the initial and irradiated conditions using the pulse method in the range from room temperature to 200degC. The thermal conductivity was calculated using the table values for the beryllium thermal capacity. The specimens and beryllium neutron source fragments were irradiation in the SM reactor at 70degC and 200degC to a neutron fluence of (0.5-11.4)·10 22 cm -2 (E>0.1 MeV) and in the BOR-60 reactor at 400degC to 16·10 22 cm -2 (E>0.1MeV), respectively. The low-temperature irradiation leads to the drop decrease of the beryllium thermal conductivity and the effect depends on the irradiation parameters. The paper analyses the effect of irradiation parameters (temperature, neutron fluence), measurement temperature and structural factors on beryllium conductivity. The experiments have revealed that the short time post-irradiation annealing at high temperature results in partial reduction of the thermal conductivity of irradiated beryllium. (author)

Proton irradiation effects on beryllium – A macroscopic assessment

Energy Technology Data Exchange (ETDEWEB)

Simos, Nikolaos, E-mail: simos@bnl.gov [Nuclear Sciences & Technology Department, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Elbakhshwan, Mohamed [Nuclear Sciences & Technology Department, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Zhong, Zhong [Photon Sciences, NSLS II, Brookhaven National Laboratory, Upton, NY, 11973 (United States); Camino, Fernando [Center for Functional Nanomaterials, Brookhaven National Laboratory, Upton, NY, 11973 (United States)

2016-10-15

Beryllium, due to its excellent neutron multiplication and moderation properties, in conjunction with its good thermal properties, is under consideration for use as plasma facing material in fusion reactors and as a very effective neutron reflector in fission reactors. While it is characterized by unique combination of structural, chemical, atomic number, and neutron absorption cross section it suffers, however, from irradiation generated transmutation gases such as helium and tritium which exhibit low solubility leading to supersaturation of the Be matrix and tend to precipitate into bubbles that coalesce and induce swelling and embrittlement thus degrading the metal and limiting its lifetime. Utilization of beryllium as a pion production low-Z target in high power proton accelerators has been sought both for its low Z and good thermal properties in an effort to mitigate thermos-mechanical shock that is expected to be induced under the multi-MW power demand. To assess irradiation-induced changes in the thermal and mechanical properties of Beryllium, a study focusing on proton irradiation damage effects has been undertaken using 200 MeV protons from the Brookhaven National Laboratory Linac and followed by a multi-faceted post-irradiation analysis that included the thermal and volumetric stability of irradiated beryllium, the stress-strain behavior and its ductility loss as a function of proton fluence and the effects of proton irradiation on the microstructure using synchrotron X-ray diffraction. The mimicking of high temperature irradiation of Beryllium via high temperature annealing schemes has been conducted as part of the post-irradiation study. This paper focuses on the thermal stability and mechanical property changes of the proton irradiated beryllium and presents results of the macroscopic property changes of Beryllium deduced from thermal and mechanical tests.

Design and fabrication of the active feedback control coils for EAST

Energy Technology Data Exchange (ETDEWEB)

Du Shijun [Institute of Plasma Physics, Chinese Academy of Sciences, P.O. Box 1126, Hefei, Anhui 230031 (China)], E-mail: dsj@ipp.ac.cn; Liu Xufeng [Institute of Plasma Physics, Chinese Academy of Sciences, P.O. Box 1126, Hefei, Anhui 230031 (China)

2008-10-15

As the active feedback control coils are located inside vacuum vessel, a reasonable design is important not only for safe operation of the coils but also for reliable operation of EAST (Experimental Advanced Superconducting Tokamak). There are some different characteristics from other coils in the design and fabrication of the coils, such as the insulation structure bearing the high baking temperature, the insulation joint with special flexible structure and the brazing method of the large size conductor inside vacuum vessel. All joints of coils are located outside the vacuum vessel for providing more connection. The conductors of the coils are designed inside the stainless steel tube and actively water cooled to prevent overheating. The ceramic rings with fiberglass tapes are used to separate the conductors and the steel tube. This insulation structure adopted in the coils can bear the high baking temperature of the vacuum vessel and its details are given in the paper. For protecting the hermetic and insulating property of the insulation joint, the small bellows is located on insulation joints to eliminate the forces on the insulator. In the fabrication, the coils are built in sections and then assembled together to form whole coils inside the vacuum vessel. The 8 kHz frequency induction heater is used to braze the conductors for cutting short brazing time and reducing heating area. The electromagnetic loads acting on the current leaders, the electrical parameters of the coil and the coil temperature are also analyzed in this paper.

Design and fabrication of the active feedback control coils for EAST

International Nuclear Information System (INIS)

Du Shijun; Liu Xufeng

2008-01-01

As the active feedback control coils are located inside vacuum vessel, a reasonable design is important not only for safe operation of the coils but also for reliable operation of EAST (Experimental Advanced Superconducting Tokamak). There are some different characteristics from other coils in the design and fabrication of the coils, such as the insulation structure bearing the high baking temperature, the insulation joint with special flexible structure and the brazing method of the large size conductor inside vacuum vessel. All joints of coils are located outside the vacuum vessel for providing more connection. The conductors of the coils are designed inside the stainless steel tube and actively water cooled to prevent overheating. The ceramic rings with fiberglass tapes are used to separate the conductors and the steel tube. This insulation structure adopted in the coils can bear the high baking temperature of the vacuum vessel and its details are given in the paper. For protecting the hermetic and insulating property of the insulation joint, the small bellows is located on insulation joints to eliminate the forces on the insulator. In the fabrication, the coils are built in sections and then assembled together to form whole coils inside the vacuum vessel. The 8 kHz frequency induction heater is used to braze the conductors for cutting short brazing time and reducing heating area. The electromagnetic loads acting on the current leaders, the electrical parameters of the coil and the coil temperature are also analyzed in this paper.

Technical issues and solutions on ITER first wall beryllium application. Industrial viewpoint

International Nuclear Information System (INIS)

Iwadachi, T.; Uda, M.; Ito, M.; Miyakawa, M.; Ibuki, M.

2004-01-01

Beryllium is selected as reference armor material of ITER primary first wall and is joined to the copper alloy heat sink such as CuCrZr or Dispersion Strengthened Copper (DSCu) Various joining technologies have been successfully developed and the manufacturing possibilities of large size first wall panels with beryllium armor has been demonstrated. Based on such results, further technical improvement is needed to reduce manufacturing cost and ensure the reliability of joining in actual size first wall. The technical issues to optimize the fabrication process of beryllium attachment were shown in this paper from an industrial point of view. Determination of the optimum size and the surface qualities of beryllium tiles are important issues in term of the material specification to ensure joining reliability and to reduce cost. The consolidation method and the finish machining methods of beryllium tiles are also critical in terms of material cost. These items should be determined by paying concern to the accommodation of the joining methods. The selections of slitting methods for attached beryllium have a great influence on fabrication cost. In the actual fabrication of beryllium attachment, safety provisions for exposure to beryllium in working environment and the recycling of the waste from the fabrication processes will be concerned sufficiently. (author)

Magnetic Field Alignment of PS-P4VP: a Non-Liquid Crystalline Coil-Coil Block Copolymer

Science.gov (United States)

Rokhlenko, Yekaterina; Zhang, Kai; Larson, Steven; Gopalan, Padma; O'Hern, Corey; Osuji, Chinedum

2015-03-01

Magnetic fields provide the ability to control alignment of self-assembled soft materials such as block copolymers. Most prior work in this area has relied on the presence of ordered assemblies of anisotropic liquid crystalline species to ensure sufficient magnetic anisotropy to drive alignment. Recent experiments with poly(styrene-b-4-vinylpyridine), a non-liquid crystalline BCP, however, show field-induced alignment of a lamellar microstructure during cooling across the order-disorder transition. Using in situ x-ray scattering, we examine the roles of field strength and cooling rate on the alignment response of this low MW coil-coil BCP. Alignment is first observed at field strengths as low as 1 Tesla and improves markedly with both increasing field strength and slower cooling. We present a geometric argument to illustrate the origin of a finite, non-trivial magnetic susceptibility anisotropy for highly stretched surface-tethered polymer chains and corroborate this using coarse-grained molecular dynamics simulations. We rationalize the magnetic field response of the system in terms of the mobility afforded by the absence of entanglements, the intrinsic anisotropy resulting from the stretched polymer chains and sterically constrained conjugated rings, and the large grain size in these low molecular weight materials.

Flow-induced vibration of helical coil compression springs

International Nuclear Information System (INIS)

Stokes, F.E.; King, R.A.

1983-01-01

Helical coil compression springs are used in some nuclear fuel assembly designs to maintain holddown and to accommodate thermal expansion. In the reactor environment, the springs are exposed to flowing water, elevated temperatures and pressures, and irradiation. Flow parallel to the longitudinal axis of the spring may excite the spring coils and cause vibration. The purpose of this investigation was to determine the flow-induced vibration (FIV) response characteristics of the helical coil compression springs. Experimental tests indicate that a helical coil spring responds like a single circular cylinder in cross-flow. Two FIV excitation mechanisms control spring vibration. Namely: 1) Turbulent Buffeting causes small amplitude vibration which increases as a function of velocity squared. 2) Vortex Shedding causes large amplitude vibration when the spring natural frequency and Strouhal frequency coincide. Several methods can be used to reduce or to prevent vortex shedding large amplitude vibrations. One method is compressing the spring to a coil pitch-to-diameter ratio of 2 thereby suppressing the vibration amplitude. Another involves modifying the spring geometry to alter its stiffness and frequency characteristics. These changes result in separation of the natural and Strouhal frequencies. With an understanding of how springs respond in the flowing water environment, the spring physical parameters can be designed to avoid large amplitude vibration. (orig.)

Analysis of surface contaminants on beryllium and aluminum windows

International Nuclear Information System (INIS)

Gmur, N.F.

1987-06-01

An effort has been made to document the types of contamination which form on beryllium window surfaces due to interaction with a synchrotron radiation beam. Beryllium windows contaminated in a variety of ways (exposure to water and air) exhibited surface powders, gels, crystals and liquid droplets. These contaminants were analyzed by electron diffraction, electron energy loss spectroscopy, energy dispersive x-ray spectroscopy and wet chemical methods. Materials found on window surfaces include beryllium oxide, amorphous carbon, cuprous oxide, metallic copper and nitric acid. Aluminum window surface contaminants were also examined

Abbreviated machining schedule for fabricating beryllium parts free of surface damage

International Nuclear Information System (INIS)

Beitscher, S.; Capes, J.F.; Leslie, W.W.; Luckow, J.R.; Riegel, R.L.

1979-01-01

This study was performed to develop a more economical method of machining damage-free beryllium components at Rocky Flats. The present method involves a 9-pass schedule of lathe turning followed by a chemical etch. Prototype beryllium hemispherical shell parts and cylindrical tensile specimens machined to simulate the parts were utilized in this study. The main investigative methods used to evaluate the amount of machining damage were metallography and tensile tests. It was found that damage-free parts could be produced by carefully controlled machining if the number of machining passes was reduced to 4 or even 3, if followed by the standard etching treatment. These findings were made on Select S-65 grade beryllium, and probably apply to other common grades of powder source beryllium but not necessarily to ingot-source beryllium. It is recommended that the 4-pass schedule becomes the standard method to produce damage-free beryllium derived from powder. Significant savings in time, labor, and equipment can be realized by this change in method without decreasing the quality of the product

Status of beryllium development for fusion applications

International Nuclear Information System (INIS)

Billone, M.C.; Macaulay-Newcombe, R.G.

1995-01-01

Beryllium is a leading candidate material for the neutron multiplier of tritium breeding blankets and the plasma-facing component of first-wall and divertor systems. Depending on the application, the fabrication methods proposed include hot-pressing, hot-isostatic-pressing, cold-isostatic-pressing/sintering, rotary electrode processing and plasma spraying. Product forms include blocks, tubes, pebbles, tiles and coatings. While, in general, beryllium is not a leading structural material candidate, its mechanical performance, as well as its performance with regard to sputtering, heat transport, tritium retention/release, helium-induced swelling and chemical compatibility, is an important consideration in first-wall/blanket design. Differential expansion within the beryllium causes internal stresses which may result in cracking, thereby affecting the heat transport and barrier performance of the material. Overall deformation can result in loading of neighboring structural material. Thus, in assessing the performance of beryllium for fusion applications, it is important to have a good database in all of these performance areas, as well as a set of properties correlations and models for the purpose of interpolation/extrapolation.In this current work, the range of anticipated fusion operating conditions is reviewed. The thermal, mechanical, chemical compatibility, tritium retention/release, and helium retention/swelling databases are then reviewed for fabrication methods and fusion operating conditions of interest. Properties correlations and uncertainty ranges are also discussed. In the case of the more complex phenomena of tritium retention/release and helium-induced swelling, fundamental mechanisms and models are reviewed in more detail. Areas in which additional data are needed are highlighted, along with some trends which suggest ways of optimizing the performance of beryllium for fusion applications. (orig.)

Construction and Test Results of Coils 2 and 3 of a 3-Nested-Coil 800-MHz REBCO Insert for the MIT 1.3-GHz LTS/HTS NMR Magnet.

Science.gov (United States)

Park, Dongkeun; Bascuñán, Juan; Michael, Philip C; Lee, Jiho; Hahn, Seungyong; Iwasa, Yukikazu

2018-04-01

We present construction and test results of Coils 2 and 3 of a 3-coil 800-MHz REBCO insert (H800) for the MIT 1.3 GHz LTS/HTS NMR magnet currently under construction. Each of three H800 coils (Coils 1-3) is a stack of no-insulation REBCO double pancakes (DPs). The innermost 8.67-T Coil 1 (26 DPs) was completed in 2016; the middle 5.64-T Coil 2 (32 DPs) has been wound, assembled, and tested; and for the outermost 4.44-T Coil 3, its 38 DPs have been wound and preliminary tests were performed to characterize each DP at 77 K. Included for Coil 2 are: 1) 77-K data of critical current, index, and turn-to-turn characteristic resistivity of each DP; 2) stacking order of the 32 DPs optimized to maximize the Coil 2 current margin and minimize its Joule dissipation in the pancake-to-pancake joints; 3) procedure to experimentally determine and apply a room-temperature preload to the DP stack; 4) 77-K and 4.2-K test results after each of 64 pancakes was over-banded with 75-μm-thick stainless steel tape for a radial thickness of 5 mm. Presented for each DP in Coil 3 are 77-K dada of critical current, index, and turn-to-turn characteristic resistivity.

Sme4 coiled-coil protein mediates synaptonemal complex assembly, recombinosome relocalization, and spindle pole body morphogenesis.

Science.gov (United States)

Espagne, Eric; Vasnier, Christelle; Storlazzi, Aurora; Kleckner, Nancy E; Silar, Philippe; Zickler, Denise; Malagnac, Fabienne

2011-06-28

We identify a large coiled-coil protein, Sme4/PaMe4, that is highly conserved among the large group of Sordariales and plays central roles in two temporally and functionally distinct aspects of the fungal sexual cycle: first as a component of the meiotic synaptonemal complex (SC) and then, after disappearing and reappearing, as a component of the spindle pole body (SPB). In both cases, the protein mediates spatial juxtaposition of two major structures: linkage of homolog axes through the SC and a change in the SPB from a planar to a bent conformation. Corresponding mutants exhibit defects, respectively, in SC and SPB morphogenesis, with downstream consequences for recombination and astral-microtubule nucleation plus postmeiotic nuclear migration. Sme4 is also required for reorganization of recombination complexes in which Rad51, Mer3, and Msh4 foci relocalize from an on-axis position to a between-axis (on-SC) position concomitant with SC installation. Because involved recombinosome foci represent total recombinational interactions, these dynamics are irrespective of their designation for maturation into cross-overs or noncross-overs. The defined dual roles for Sme4 in two different structures that function at distinct phases of the sexual cycle also provide more functional links and evolutionary dynamics among the nuclear envelope, SPB, and SC.

Identification of an abnormal beryllium lymphocyte proliferation test

International Nuclear Information System (INIS)

Frome, Edward L.; Newman, Lee S.; Cragle, Donna L.; Colyer, Shirley P.; Wambach, Paul F.

2003-01-01

The potential hazards from exposure to beryllium or beryllium compounds in the workplace were first reported in the 1930s. The tritiated thymidine beryllium lymphocyte proliferation test (BeLPT) is an in vitro blood test that is widely used to screen beryllium exposed workers in the nuclear industry for sensitivity to beryllium. The clinical significance of the BeLPT was described and a standard protocol was developed in the late 1980s. Cell proliferation is measured by the incorporation of tritiated thymidine into dividing cells on two culture dates and using three concentrations of beryllium sulfate. Results are expressed as a 'stimulation index' (SI) which is the ratio of the amount of tritiated thymidine (measured by beta counts) in the simulated cells divided by the counts for the unstimulated cells on the same culture day. Several statistical methods for use in the routine analysis of the BeLPT were proposed in the early 1990s. The least absolute values (LAV) method was recommended for routine analysis of the BeLPT. This report further evaluates the LAV method using new data, and proposes a new method for identification of an abnormal or borderline test. This new statistical-biological positive (SBP) method reflects the clinical judgment that: (i) at least two SIs show a 'positive' response to beryllium; and (ii) that the maximum of the six SIs must exceed a cut-point that is determined from a reference data set of normal individuals whose blood has been tested by the same method in the same serum. The new data is from the Y-12 National Security Complex in Oak Ridge (Y-12) and consists of 1080 workers and 33 non-exposed control BeLPTs (all tested in the same serum). Graphical results are presented to explain the statistical method, and the new SBP method is applied to the Y-12 group. The true positive rate and specificity of the new method were estimated to be 86% and 97%, respectively. An electronic notebook that is accessible via the Internet was used in

Beryllium data base for in-pile mockup test on blanket of fusion reactor, (1)

Energy Technology Data Exchange (ETDEWEB)

Kawamura, Hiroshi; Ishitsuka, Etsuo (Japan Atomic Energy Research Inst., Oarai, Ibaraki (Japan). Oarai Research Establishment); Sakamoto, Naoki; Kato, Masakazu; Takatsu, Hideyuki.

1992-11-01

Beryllium has been used in the fusion blanket designs with ceramic breeder as a neutron multiplier to increase the net tritium breeding ratio (TBR). The properties of beryllium, that is physical properties, chemical properties, thermal properties, mechanical properties, nuclear properties, radiation effects, etc. are necessary for the fusion blanket design. However, the properties of beryllium have not been arranged for the fusion blanket design. Therefore, it is indispensable to check and examine the material data of beryllium reported previously. This paper is the first one of the series of papers on beryllium data base, which summarizes the reported material data of beryllium. (author).

Spectrochemical determination of beryllium and lithium in stream sediments

International Nuclear Information System (INIS)

Gallimore, D.L.; Hues, A.D.; Palmer, B.A.; Cox, L.E.; Simi, O.R.; Bieniewski, T.M.; Steinhaus, D.W.

1979-11-01

A spectrochemical method was developed to analyze 200 or more samples of stream sediments per day for beryllium and lithium. One part of ground stream sediment is mixed with two parts graphite-SiO 2 buffer, packed into a graphite electrode, and excited in a direct-current arc. The resulting emission goes to a 3.4-m, direct-reading, Ebert spectrograph. A desk-top computer system is used to record and process the signals, and to report the beryllium and lithium concentrations. The limits of detection are 0.2 μg/g for beryllium and 0.5 μg/g for lithium. For analyses of prepared reference materials, the relative standard deviations were 16% for determining 0.2 to 100 μg/g of beryllium and 15% for determining 0.5 to 500 μg/g of lithium. A correction is made for vanadium interference

New facility for post irradiation examination of neutron irradiated beryllium

International Nuclear Information System (INIS)

Ishitsuka, Etsuo; Kawamura, Hiroshi

1995-01-01

Beryllium is expected as a neutron multiplier and plasma facing materials in the fusion reactor, and the neutron irradiation data on properties of beryllium up to 800 degrees C need for the engineering design. The acquisition of data on the tritium behavior, swelling, thermal and mechanical properties are first priority in ITER design. Facility for the post irradiation examination of neutron irradiated beryllium was constructed in the hot laboratory of Japan Materials Testing Reactor to get the engineering design data mentioned above. This facility consist of the four glove boxes, dry air supplier, tritium monitoring and removal system, storage box of neutron irradiated samples. Beryllium handling are restricted by the amount of tritium;7.4 GBq/day and 60 Co;7.4 MBq/day

Microplasticity in hot-pressed beryllium

International Nuclear Information System (INIS)

Plane, D.C.; Bonfield, W.

1977-01-01

Closed hysteresis loops measured in the microstrain region of hot pressed, commercially pure, polycrystalline beryllium are correlated with a dislocation - impurity atom, energy dissipating mechanism. (author)

Movement of liquid beryllium during melt events in JET with ITER-like wall

International Nuclear Information System (INIS)

Sergienko, G; Huber, A; Brezinsek, S; Coenen, J W; Mertens, Ph; Philipps, V; Samm, U; Arnoux, G; Matthews, G F; Nunes, I; Riccardo, V; Sirinelli, A; Devaux, S

2014-01-01

The ITER-like wall recently installed in JET comprises solid beryllium limiters and a combination of bulk tungsten and tungsten-coated carbon fibre composite divertor tiles without active cooling. During a beryllium power handling qualification experiment performed in limiter configuration with 5 MW neutral beam injection input power, accidental beryllium melt events, melt layer motion and splashing were observed locally on a few beryllium limiters in the plasma contact areas. The Lorentz force is responsible for the observed melt layer movement. To move liquid beryllium against the gravity force, the current flowing from the plasma perpendicularly to the limiter surface must be higher than 6 kA m −2 . The thermo-emission current at the melting point of beryllium is much lower. The upward motion of the liquid beryllium against gravity can be due to a combination of the Lorentz force from the secondary electron emission and plasma pressure force. (paper)

Peptide-oligonucleotide conjugates as nanoscale building blocks for assembly of an artificial three-helix protein mimic

DEFF Research Database (Denmark)

Lou, Chenguang; Martos-Maldonado, Manuel C.; Madsen, Charlotte Stahl

2016-01-01

Peptide-based structures can be designed to yield artificial proteins with specific folding patterns and functions. Template-based assembly of peptide units is one design option, but the use of two orthogonal self-assembly principles, oligonucleotide triple helix and a coiled coil protein domain ...

About kinetics of paramagnetic radiation malformations in beryllium ceramics

International Nuclear Information System (INIS)

Polyakov, A.I.; Ryabinkin, Yu.A.; Zashkvara, O.V.; Bitenbaev, M.I.; Petukhov, Yu.V.

1999-01-01

This paper [1] specifies that γ-radiation of the beryllium-oxide-based ceramics results in development of paramagnetic radiation malformations emerging the ESR spectrum in form of doublet with the splitting rate of oestrasid Δ∼1.6 and g-factor of 2.008. This report presents evaluation outcomes of dependence of paramagnetic radiation malformations concentration in beryllium ceramics on gamma-radiation dose ( 60 Co) within the range of 0-100 Mrad. Total paramagnetic parameters of beryllium ceramics in the range 0-100 Mrad of gamma-radiation dose varied slightly, and were specified by the first type of paramagnetic radiation malformations

Reducing the cost of S-65C grade beryllium for ITER first wall applications

International Nuclear Information System (INIS)

Kaczynski, D.; Sato, K.; Savchuk, V.V.; Shestakov, V.P.

2004-01-01

Beryllium is the current material of choice for plasma-facing components in ITER. The present design is for 10 mm thick beryllium tiles bonded to an actively cooled copper substrate. Brush Wellman grade S65C beryllium is preferred grade off beryllium for these tiles. S65C has the best resistance to low-cycle thermal fatigue than any other beryllium grad in the world. S65C grade beryllium has been successfully deployed in fusion reactors for more than two decades, most recently in the JET reactor. This paper will detail a supply chain to produce the most cost-effective S65C plasma facing components for ITER. This paper will also propose some future work too demonstrate the best technology for bonding beryllium to copper. (author)

A Correlation Study between Geometry of Collared Coils and Normal Quadrupole Multipole in the Main LHC Dipoles

CERN Document Server

Bertinelli, F; Berthollon-Vitte, S; Glaude, D; Vanenkov, I

2006-01-01

The quality control implemented at all LHC dipole assemblers includes precise mechanical measurements of the geometry of collared coils. A cross-analysis performed between mechanical and magnetic measurements data shows a correlation between collared coils outer dimensions and the normal quadrupole multipole (b2) for one dipole assembler. The profile geometry of the single collars - as determined from 3D measurements at the collar suppliers and CERN - could not account alone for the significant left – right aperture asymmetry observed. This triggered a deeper investigation on different elements of the geometry of single collars. The results of this work show that the relative positioning of the collaring holes, allowing a small bending deformation of collars under the effect of coil pre-stress, is an important effect that generates a b2 multipole at the limit of specification. The study has deepened the understanding of the factors affecting collared coil geometry and field quality. The precision of 3D m...

Controlling Beryllium Contaminated Material And Equipment For The Building 9201-5 Legacy Material Disposition Project

International Nuclear Information System (INIS)

Reynolds, T.D.; Easterling, S.D.

2010-01-01

This position paper addresses the management of beryllium contamination on legacy waste. The goal of the beryllium management program is to protect human health and the environment by preventing the release of beryllium through controlling surface contamination. Studies have shown by controlling beryllium surface contamination, potential airborne contamination is reduced or eliminated. Although there are areas in Building 9201-5 that are contaminated with radioactive materials and mercury, only beryllium contamination is addressed in this management plan. The overall goal of this initiative is the compliant packaging and disposal of beryllium waste from the 9201-5 Legacy Material Removal (LMR) Project to ensure that beryllium surface contamination and any potential airborne release of beryllium is controlled to levels as low as practicable in accordance with 10 CFR 850.25.

Atlas of hot isostatic beryllium powder pressing diagrams

International Nuclear Information System (INIS)

Stoev, P.I.; Papirov, I.I.; Tikhinskij, G.F.; Vasil'ev, A.A.

1995-01-01

Diagrams of hot isotopic pressing (HIP) of beryllium powder with different grain size in a wide range of pressing parameters are built by mathematical modeling methods. The HIP diagrams presented are divided into 3 groups: parametric dependencies D=f(P,T); technological HIP diagrams; compacting mechanisms. The created data bank permits to optimise beryllium powder HIP with changing parameters. 4 refs., 23 figs

A study on mechanical properties and flow-induced vibrations of coil-shaped holddown spring

International Nuclear Information System (INIS)

Kim, Kyu-Tae

2010-01-01

The fuel assemblies used in the OPR1000s in Korea employ four coil-shaped hold-down springs to exert compressive load at the top of fuel assembly so that the assemblies may not be damaged by preventing its hydraulic-induced lifting-off from its lower seating surface. However, the coolant flow generates the flow-induced vibration at the coil-shaped hold-down springs which may cause wear on the spring surfaces. A hold-own spring may be fractured if torsional stress acting on its worn area exceeds a stress limit, resulting in the loss of hold-down spring force of the fuel assembly. In this paper, flow-induced vibration tests were performed for standard and improved coil type hold-down springs to investigate the effects of these two hold-down spring designs on flow-induced vibration wear. In parallel, a wide spectrum of mechanical tests was performed to obtain vibration-related characteristics of these two hold-down springs, which can be used as input data for the fuel assembly static and dynamic analysis. It is found that the improved hold-down spring design is better against flow-induced vibration wear than the standard one. With the use of the three-dimensional Solidwork model, the stress-related design lifetime of the improved hold-down spring was estimated by extrapolating its wear data measured from the flow-induced vibration tests, which indicates that the improved HD spring design will maintain integrity during the fuel design lifetime in OPR1000s in Korea.

Corrosion of beryllium exposed to celotex and water

International Nuclear Information System (INIS)

Hill, M.A.; Butt, D.P.; Lillard, R.S.

1997-01-01

Celotex is a commercial rigid cellulose fiberboard product primarily used in the building construction industry. Currently celotex is being used as a packing material in AL-R8 containers. Ion chromatography of celotex packing material at Lawrence Livermore National Laboratory (LLNL) has indicated that this material contains aggressive anions, including chloride, which may accelerate corrosion. It is well known that beryllium is susceptible to pitting corrosion when exposed to chloride containing environments. Levy noted pitting in beryllium at the open circuit potential when exposed to 0.1 M NaCl solution. This investigation attempts to evaluate the potential risk of accelerated beryllium corrosion from celotex and water which may occur naturally when celotex dust comes into contact with moisture from the atmosphere

A diethylhydroxylaminate based mixed lithium/beryllium aggregate

Energy Technology Data Exchange (ETDEWEB)

Berger, Raphael J.F. [Paris-Lodron Universitaet Salzburg (Austria). Fachbereich fuer Materialwissenschaften und Physik; Jana, Surajit [Asansol Girls College, West-Bengal (India). Dept. of Chemistry; Froehlich, Roland [Muenster Univ. (Germany). Organisch-Chemisches Inst.; Mitzel, Norbert W. [Bielefeld Univ. (Germany). Anorganische Chemie und Strukturchemie

2015-07-01

A mixed lithium/beryllium diethylhydroxylaminate compound containing {sup n}butyl beryllium units of total molecular composition {sup n}Be(ONEt{sub 2}){sub 2} [(LiONEt{sub 2}){sup 2} {sup n}BuBeONEt{sub 2}]{sub 2} (1) was isolated from a reaction mixture of {sup n}butyl lithium, N,N-diethylhydroxylamine and BeCl{sub 2} in diethylether/thf. The crystal structure of 1 has been determined by X-ray diffraction. The aggregate is composed of two ladder-type subunits connected in a beryllium-centered distorted tetrahedron of four oxygen atoms. Only the lithium atoms are engaged in coordination with the nitrogen donor atoms. The DFT calculations support the positional occupation determined for Li and Be in the crystal structure. The DFT and the solid-state structure are in excellent agreement, indicating only weak intermolecular interactions in the solid state. Structural details of metal atom coordination are discussed.

Feasibility demonstration of consolidating porous beryllium/carbon structures. Final report

International Nuclear Information System (INIS)

Browning, M.J.; Hoover, G.E.; Mueller, J.J.; Hanes, H.D.

1977-01-01

A preliminary feasibility study was initiated to determine if porous beryllium structures could be fabricated by consolidating beryllium-coated microballoons into a rigid structure. The target specifications were to coat nominally 1-mm diameter microspheres with 0.5-mil beryllium coatings and then bond into a structure. Because of the very short time period, it was agreeable to use existing or quickly-available materials. The general approach was to apply coatings to carbon or quartz microspheres. Physical vapor deposition and ''snow-balling'' of fine beryllium powder were the two methods investigated. Once the particles were coated, HIP (pressure bonding) and pressureless sintering were to be investigated as methods for consolidating the microballoons. A low level of effort was to be spent to look at means of fabricating an all-carbon structure

Proceedings of the third IEA international workshop on beryllium technology for fusion

International Nuclear Information System (INIS)

Kawamura, Hiroshi; Okamoto, Makoto

1998-01-01

This report is the Proceedings of the Third International Energy Agency International Workshop on Beryllium Technology for Fusion. The workshop was held on October 22-24, 1997, at the Sangyou Kaikan in Mito City with 68 participants who attended from the Europe, the Russian Federation, the Kazakstan, the United States and Japan. The topics for papers were arranged into 9 sessions; beryllium applications for ITER, production and characterization, chemical compatibility and corrosion, forming and joining, plasma/tritium interactions, beryllium coating, first wall applications, neutron irradiation effects, health and safety. To utilize beryllium in the pebble type blanket, a series of discussions were intensified in multiple view points such as the swelling, He/T release from beryllium pebble irradiated up to high He content, effective thermal conductivity, tritium permeation and coating, and fabrication cost, and so on. As the plasma facing material, life time of beryllium and coated beryllium, dust and particle production, joining, waste treatment, mechanical properties and deformation by swelling were discussed as important issues. Especially, it was recognized throughout the discussions that the comparative study by the different researchers should be carried out to establish the reliability of the data reported in the workshop and in others. To enhance the comparative study, the world wide collaboration for the relative evaluation of the beryllium was proposed by the International Organization Committee and the proposal was approved by all of the participants. The 45 of the presented papers are indexed individually. (J.P.N.)

High heat flux tests on beryllium and beryllium-copper joints

International Nuclear Information System (INIS)

Roedig, M.; Duwe, R.; Linke, J.; Schuster, A.

1997-01-01

A large test program has been set up to evaluate the performance of beryllium as a plasma facing material for the divertor in thermonuclear fusion devices. Simulation of steady state heat loads of 5 MWm -2 and above on actively cooled divertor modules, and off-normal plasma conditions with energy densities in the range 1-7 MJm -2 , have been investigated. Thermal shock tests were carried out with the ITER reference grade S65-C and several Russian grades of beryllium. At incident energies up to 7 MJm -2 the best erosion behaviour is observed for S65-C and for TGP-56. Steady state heating tests with actively cooled Be/Cu mock-ups were performed at incident powers of up to 5.8 MWm -2 . All samples investigated in these tests did not show any indications of failure. A Be/Cu mock-ups with Incusil braze was loaded in thermal fatigue up to 500 cycles at an incident power of 4.8 MWm -2 . Up to the end of the experiment no temperature increase of the surface and no indication of failure was observed. (orig.)

Method of beryllium implantation in germanium substrate

International Nuclear Information System (INIS)

Kagawa, S.; Baba, Y.; Kaneda, T.; Shirai, T.

1983-01-01

A semiconductor device is disclosed, as well as a method for manufacturing it in which ions of beryllium are implanted into a germanium substrate to form a layer containing p-type impurity material. There after the substrate is heated at a temperature in the range of 400 0 C. to 700 0 C. to diffuse the beryllium ions into the substrate so that the concentration of beryllium at the surface of the impurity layer is in the order of 10 17 cm- 3 or more. In one embodiment, a p-type channel stopper is formed locally in a p-type germanium substrate and an n-type active layer is formed in a region surrounded by, and isolated from, the channel stopper region. In another embodiment, a relatively shallow p-type active layer is formed at one part of an n-type germanium substrate and p-type guard ring regions are formed surrounding, and partly overlapping said p-type active layer. In a further embodiment, a p-type island region is formed at one part of an n-type germanium substrate, and an n-type region is formed within said p-type region. In these embodiments, the p-type channel stopper region, p-type guard ring regions and the p-type island region are all formed by implanting ions of beryllium into the germanium substrate

TEM study of impurity segregations in beryllium pebbles

Energy Technology Data Exchange (ETDEWEB)

Klimenkov, M., E-mail: michael.klimenkov@kit.edu [Institute for Applied Materials – Applied Materials Physics, Karlsruhe Institute of Technology, Hermann-von-Helmholz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Chakin, V.; Moeslang, A. [Institute for Applied Materials – Applied Materials Physics, Karlsruhe Institute of Technology, Hermann-von-Helmholz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Rolli, R. [Institute for Applied Materials – Materials and Biomechanics, Karlsruhe Institute of Technology, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany)

2014-12-15

Beryllium is planned to be used as a neutron multiplier in the Helium-cooled Pebble Bed European concept of a breeding blanket of demonstration power reactor DEMO. In order to evaluate the irradiation performance, individual pebbles and constrained pebble beds were neutron-irradiated at temperatures typical of fusion blankets. Beryllium pebbles 1 mm in diameter produced by the rotating electrode method were subjected to a TEM study before and after irradiation at High Flux Reactor, Petten, Netherlands at 861 K. The grain size varied in a wide range from sub-micron size up to several tens of micrometers, which indicated formation bimodal grain size distribution. Based on the application of combined electron energy loss spectroscopy and energy dispersive X-ray spectroscopy methods, we suggest that impurity precipitates play an important role in controlling the mechanical properties of beryllium. The impurity elements were present in beryllium at a sub-percent concentration form beryllide particles of a complex (Fe/Al/Mn/Cr)B composition. These particles are often ordered along dislocations lines, forming several micron-long chains. It can be suggested that fracture surfaces often extended along these chains in irradiated material.

Development of a single-layer Nb3Sn common coil dipole model

Energy Technology Data Exchange (ETDEWEB)

Igor Novitski et al.

2002-12-13

A high-field dipole magnet based on the common coil design was developed at Fermilab for a future Very Large Hadron Collider. A short model of this magnet with a design field of 11 T in two 40-mm apertures is being fabricated using the react-and-wind technique. In order to study and optimize the magnet design two 165-mm long mechanical models were assembled and tested. A technological model consisting of magnet straight section and ends was also fabricated in order to check the tooling and the winding and assembly procedures. This paper describes the design and technology of the common coil dipole magnet and summarizes the status of short model fabrication.The results of the mechanical model tests and comparison with FE mechanical analysis are also presented.

The development of beryllium plasma spray technology for the International Thermonuclear Experimental Reactor (ITER)

International Nuclear Information System (INIS)

Castro, R.G.; Elliott, K.E.; Hollis, K.J.; Watson, R.D.

1999-01-01

Over the past five years, four international parties, which include the European Communities, Japan, the Russian Federation and the United States, have been collaborating on the design and development of the International Thermonuclear Experimental Reactor (ITER), the next generation magnetic fusion energy device. During the ITER Engineering Design Activity (EDA), beryllium plasma spray technology was investigated by Los Alamos National Laboratory as a method for fabricating and repairing and the beryllium first wall surface of the ITER tokamak. Significant progress has been made in developing beryllium plasma spraying technology for this application. Information will be presented on the research performed to improve the thermal properties of plasma sprayed beryllium coatings and a method that was developed for cleaning and preparing the surface of beryllium prior to depositing plasma sprayed beryllium coatings. Results of high heat flux testing of the beryllium coatings using electron beam simulated ITER conditions will also be presented

Reactivity effect of poisoned beryllium block shuffling in the MARIA reactor

International Nuclear Information System (INIS)

Andrzejewski, K.; Kulikowska, T.

2000-01-01

The paper is a continuation of the analysis of beryllium blocks poisoning by Li-6 and He-3 in the MARIA reactor, presented at the 22 RERTR Meeting in Budapest. A new computational tool, the REBUS-3 code, has been used for predicting the amount of poison. The code has been put into operation on a HP computer and the beryllium transmutation chains have been activated with assistance of the ANL RERTR staff. The horizontal and vertical poison distribution within beryllium blocks has been studied. A simple shuffling of beryllium blocks has been simulated to check the effect of exchanging a block with high poison concentration, adjacent to fuel elements, with a peripheral one with a low poison concentration

Uncoupling PIP2-calmodulin regulation of Kv7.2 channels by an assembly destabilizing epileptogenic mutation.

Science.gov (United States)

Alberdi, Araitz; Gomis-Perez, Carolina; Bernardo-Seisdedos, Ganeko; Alaimo, Alessandro; Malo, Covadonga; Aldaregia, Juncal; Lopez-Robles, Carlos; Areso, Pilar; Butz, Elisabeth; Wahl-Schott, Christian; Villarroel, Alvaro

2015-11-01

We show that the combination of an intracellular bi-partite calmodulin (CaM)-binding site and a distant assembly region affect how an ion channel is regulated by a membrane lipid. Our data reveal that regulation by phosphatidylinositol(4,5)bisphosphate (PIP2) and stabilization of assembled Kv7.2 subunits by intracellular coiled-coil regions far from the membrane are coupled molecular processes. Live-cell fluorescence energy transfer measurements and direct binding studies indicate that remote coiled-coil formation creates conditions for different CaM interaction modes, each conferring different PIP2 dependency to Kv7.2 channels. Disruption of coiled-coil formation by epilepsy-causing mutation decreases apparent CaM-binding affinity and interrupts CaM influence on PIP2 sensitivity. © 2015. Published by The Company of Biologists Ltd.

Assembly, Loading, and Cool‐down of the FRESCA2 Support Structure

CERN Document Server

Muñoz Garcia, J E; Ziemianski, D T; Rondeaux, F; de Rijk, G; Bajas, H; Rifflet, J M; Perez, J C; Durante, M; Charrondiere, M; Bajko, M; Devaux, M; Guinchard, M; Ferracin, P; Fessia, P; Manil, P

2014-01-01

This paper reports on the assembly process and cool-down to cryogenic temperature of the support structure of FRESCA2, which is a dipole magnet for upgrading the actual CERN cable test facility FRESCA. The structure of the FRESCA2 magnet is designed to provide the adequate pre-stress, through the use of keys, bladders, and an Al alloy shrinking cylinder. In order to qualify the assembly and loading procedures, the structure was assembled with Al blocks (dummy coils) that replaced the brittle Nb$_{3}$Sn coils, and then cooled-down to 77 K with liquid nitrogen. The evolution of the mechanical behaviour was monitored via strain gauges located on different components of the structure (shell, rods, yokes and dummy coils). We focus on the expected stresses within the structure after assembly, loading and cool-down. The expected stresses were determined from the 3D finite element model of the structure. A comparison of the 3D model stress predictions with the strain gauge data measurements is made. The coherence bet...

Development and experimental study of beryllium window for ITER radial X-ray camera

Energy Technology Data Exchange (ETDEWEB)

Chen, Zhaoxi [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei 230031 (China); Jin, Guangxu [Materion Brush (United States); Chen, Kaiyun; Chen, Yebin; Song, Yuntao [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei 230031 (China); Hu, Liqun, E-mail: lqhu@ipp.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei 230031 (China); Niu, Luying; Sheng, Xiuli; Cheng, Yong; Lu, Kun [Institute of Plasma Physics, Chinese Academy of Sciences, Hefei 230031 (China)

2013-12-15

Highlights: • The thickness of the beryllium foil is chosen as 80 μm to guarantee its safety under high pressure differential in accident events. • Using low purity of beryllium as the transition material, the effect of thermal stress caused by diffusion bonding process can be reduced. • Sealing ring and honeycomb-like supports are designed and used in the mechanical clamped beryllium window to enhance its sealing and safety performance. • The beryllium windows have good performance under severe working conditions like high temperature baking, vibration or impact load. -- Abstract: Radial X-ray camera (RXC) is a diagnostic device planned to be installed in the ITER Equatorial Port no. 12. Beryllium window will be installed between the inner and outer camera of RXC, which severs as the transmission photocathode substrate and also the vacuum isolation component. In this paper the design and manufacture process of two types of beryllium windows were introduced. Although 50 μm thickness of beryllium foil is the best choice, the 80 μm one with X-ray threshold of 1.34 keV was selected for safety consideration. Using the intermediate layer (low purity of beryllium) between the beryllium foil and the stainless steel base flange is an effective strategy to limit the welding thermal deformation and thermal stress of the thin foil caused by bonding between different materials. By using ANSYS software, the feasibility of the aperture design was analyzed and validated. Metal sealing ring was applied in the mechanical clamped beryllium window for its good stability under high temperature and neutron radiation. Although both of the hollow metal sealing ring with 0.03 mm silver coating and the pure silver sealing ring can satisfy the sealing requirement, the later one was chosen to produce the final product. Two hours 240 °C high temperature baking test, two hours 3.3 Hz vibration test and fatigue test were performed on the two types of beryllium windows. Based on the

Mechanical properties of ISABELLE superconducting coils

International Nuclear Information System (INIS)

Thompson, P.; Bertsche, A.; Fuhrmann, J.; Greene, A.; Grove, E.; Repeta, L.; Short, F.; Tannenbaum, M.; Wanderer, P.

1981-01-01

As a part of the manufacturing processes, several mechanical measurements are made on ISABELLE dipoles. These are done both to control the process and to provide information for the evaluation of the behavior of the completed magnets. This paper discusses the Young's Modulus (E = 1-3 x 10 6 psi), the thermal contraction of the coil assembly (ΔL/L = 290 +- 17 x 10 -5 at 77 0 K), and the loss of applied prestress with time

Assembly and Test of HD2, a 36 mm bore high field Nb3Sn Dipole Magnet

International Nuclear Information System (INIS)

Ferracin, P.; Bingham, B.; Caspi, S.; Cheng, D.W.; Dietderich, D.R.; Felice, H.; Godeke, A.; Hafalia, A.R.; Hannaford, C.R.; Joseph, J.; Lietzke, A.F.; Lizarazo, J.; Sabbi, G.; Trillaud, F.; Wang, X.

2008-01-01

We report on the fabrication, assembly, and test of the Nb 3 Sn dipole magnet HD2. The magnet, aimed at demonstrating the application of Nb 3 Sn superconductor in high field accelerator-type dipoles, features a 36 mm clear bore surrounded by block-type coils with tilted ends. The coil design is optimized to minimize geometric harmonics in the aperture and the magnetic peak field on the conductor in the coil ends. The target bore field of 15 T at 4.3 K is consistent with critical current measurements of extracted strands. The coils are horizontally pre-stressed during assembly using an external aluminum shell pre-tensioned with water-pressurized bladders. Axial pre-loading of the coil ends is accomplished through two end plates and four aluminum tension rods. The strain in coil, shell, and rods is monitored with strain gauges during assembly, cool-down and magnet excitation, and compared with 3D finite element computations. Magnet's training performance, quench locations, and ramp-rate dependence are then analyzed and discussed.

A design for a high voltage magnet coil ringer test set

International Nuclear Information System (INIS)

Koska, W.; Sims, R.E.

1992-04-01

By discharging a bank of charged capacitors through a high power SCR switch into an SSC dipole magnet assembly, it is possible to ''ring'' the coil and develop a voltage stress of greater than 50 volts turn-to-turn, thereby verifying the insulation integrity. We will present an overview of the test set design for a 2 kV isolated SCR firing circuit, including safety features, selectable capacitor banks, and digital waveform storage system. Results from testing typical coils and magnets will be included. Possible upgrades are also discussed

Toroid field coil shear key installation study, DOE task No. 22

International Nuclear Information System (INIS)

Jones, C.E.; Meier, R.W.; Yuen, J.L.

1995-01-01

Concepts for fitting and installation of the scissor keys, triangular keys, and truss keys in the ITER Toroidal Field (TF) Coil Assembly were developed and evaluated. In addition, the process of remote removal and replacement of a failed TF coil was considered. Two concepts were addressed: central solenoid installed last (Naka Option 1) and central solenoid installed first (Naka Option 2). In addition, a third concept was developed which utilized the favorable features of both concepts. A time line for installation was estimated for the Naka Option 1 concept

Method of crude ore defluoridation in hydrometallurgy of beryllium, affording fluorosilicic acid

International Nuclear Information System (INIS)

Samojlov, V.I.; Borsuk, A.N.; Zherin, I.I.

2006-01-01

Results of laboratory and industrial tests conducted at Ul'ba Metallurgical Plant on leaching bertrandite - phenacite - fluorite flotation concentrate containing ∼4 wt. % beryllium in a rotary furnace using sulfuric acid are presented. The technology is shown to provide a 7.8% reduction in the net cost of beryllium production (1 kg) in the form of technical-grade Be(OH) 2 by obviating the need of smelting beryllium concentrates and alkali fluxes. Besides, the technology permits concomitant production of H 2 SiF 6 , its commercial sales promoting a 17.6% reduction in beryllium production net cost [ru

Thermal Properties of Beryllium Metal

International Nuclear Information System (INIS)

Cho, Tae Won; Baek, Je Kyun; Jeong, Gwan Yoon; Kim, Ji Hyeon; Sohn, Dong Seong

2013-01-01

It is known that the presence of as-fabricated porosity largely affect thermal conductivity of beryllium. Therefore, in this paper we will suggest a new thermal conductivity equation which consider volume fraction and discuss how this can be applied to irradiation induced degradation of thermal conductivity later. This study was performed to develop a new correlation of thermal conductivity of Beryllium. Although there are many factors like BeO contents, impurity level, grain size, and porosity, we assumed porosity will be the dominant factor for thermal conductivity. Therefore, a new correlation which consider volume fraction by applying Maxwell-Eucken equation is developed and this is consistent to some degrees. However, increasing impurity level and decreasing grain size will decrease thermal conductivity. Therefore, we need to consider their effects although we assume BeO contents, impurity, and grain size do not make noticeable effects in the future. Furthermore, thermal conductivity degradation by neutron irradiation should be considered afterward. There are two main factors for the thermal conductivity degradation: the one is defects formed by neutron collisions and the other is helium generated by transmutation of Be. It is known that they make a considerable degradation of conductivity. Beryllium is known there are considerable volume increases by helium accumulation. Therefore, we anticipate our suggested model can be applicable if it has been developed furthermore considering irradiation induced swelling

HEINBE; the calculation program for helium production in beryllium under neutron irradiation

International Nuclear Information System (INIS)

Shimakawa, Satoshi; Ishitsuka, Etsuo; Sato, Minoru

1992-11-01

HEINBE is a program on personal computer for calculating helium production in beryllium under neutron irradiation. The program can also calculate the tritium production in beryllium. Considering many nuclear reactions and their multi-step reactions, helium and tritium productions in beryllium materials irradiated at fusion reactor or fission reactor may be calculated with high accuracy. The calculation method, user's manual, calculated examples and comparison with experimental data were described. This report also describes a neutronics simulation method to generate additional data on swelling of beryllium, 3,000-15,000 appm helium range, for end-of-life of the proposed design for fusion blanket of the ITER. The calculation results indicate that helium production for beryllium sample doped lithium by 50 days irradiation in the fission reactor, such as the JMTR, could be achieved to 2,000-8,000 appm. (author)

Behavior of beryllium pebbles under irradiation

Energy Technology Data Exchange (ETDEWEB)

Dalle-Donne, M.; Scaffidi-Argentina, F. [Forschungszentrum Karlsruhe GmbH Technik und Umwelt (Germany). Inst. fuer Neutronenphysik und Reactortechnik; Baldwin, D.L.; Gelles, D.S.; Greenwood, L.R.; Kawamura, H.; Oliver, B.M.

1998-01-01

Beryllium pebbles are being considered in fusion reactor blanket designs as neutron multiplier. An example is the European `Helium Cooled Pebble Bed Blanket.` Several forms of beryllium pebbles are commercially available but little is known about these forms in response to fast neutron irradiation. Commercially available beryllium pebbles have been irradiated to approximately 1.3 x 10{sup 22} n/cm{sup 2} (E>1 MeV) at 390degC. Pebbles 1-mm in diameter manufactured by Brush Wellman, USA and by Nippon Gaishi Company, Japan, and 3-mm pebbles manufactured by Brush Wellman were included. All were irradiated in the below-core area of the Experimental Breeder Reactor-II in Idaho Falls, USA, in molybdenum alloy capsules containing helium. Post-irradiation results are presented on density change measurements, tritium release by assay, stepped-temperature anneal, and thermal ramp desorption tests, and helium release by assay and stepped-temperature anneal measurements, for Be pebbles from two manufacturing methods, and with two specimen diameters. The experimental results on density change and tritium and helium release are compared with the predictions of the code ANFIBE. (author)

New and Emerging Technologies for Real-Time Air and Surface Beryllium Monitoring

Energy Technology Data Exchange (ETDEWEB)

Phifer, B.E. Jr.; Churnetski, E.L.; Cooke, L.E.; Reed, J.J.; Howell, M.L.; Smith, V.D.

2001-09-01

In this study, five emerging technologies were identified for real-time monitoring of airborne beryllium: Microwave-Induced Plasma Spectroscopy (MIPS), Aerosol Beam-Focused Laser-Induced Plasma Spectroscopy (ABFLIPS), Laser-Induced Breakdown Spectroscopy (LIBS), Surfaced-Enhanced Raman Scattering (SERS) Spectroscopy, and Micro-Calorimetric Spectroscopy (CalSpec). Desired features of real-time air beryllium monitoring instrumentation were developed from the Y-12 CBDPP. These features were used as guidelines for the identification of potential technologies as well as their unique demonstrated capability to provide real-time monitoring of similar materials. However, best available technologies were considered, regardless of their ability to comply with the desired features. None of the five technologies have the capability to measure the particle size of airborne beryllium. Although reducing the total concentration of airborne beryllium is important, current literature suggests that reducing or eliminating the concentration of respirable beryllium is critical for worker health protection. Eight emerging technologies were identified for surface monitoring of beryllium. CalSpec, MIPS, SERS, LIBS, Laser Ablation, Absorptive Stripping Voltametry (ASV), Modified Inductively Coupled Plasma (ICP) Spectroscopy, and Gamma BeAST. Desired features of real-time surface beryllium monitoring were developed from the Y-12 CBDPP. These features were used as guidelines for the identification of potential technologies. However, the best available technologies were considered regardless of their ability to comply with the desired features.

Retrospective beryllium exposure assessment at the Rocky Flats Environmental Technology site

International Nuclear Information System (INIS)

Barnard, A.E.; Torma-Krajewski, J.; Viet, S.M.

1997-01-01

Since the 1960's, beryllium machining was performed to make nuclear weapon components at the Department of Energy (DOE) Rocky Flats Plant. Beryllium exposure was assessed via fixed airhead (FAH) sampling in which the filter cassette was affixed to the machine, generally within a few feet of the worker's breathing zone. Approximately 500,000 FAH samples were collected for beryllium over three decades. From 1984 to 1987, personal breathing zone (PBZ) samples were also collected as part of the evaluation of a new high velocity/low volume local exhaust ventilation (HV/LV LEV) system. The purpose of this study was to determine how the two types of sampling data could be used for an exposure assessment in the beryllium shop

JET-ISX-B beryllium limiter experiment safety analysis report and operational safety requirements

International Nuclear Information System (INIS)

Edmonds, P.H.

1985-09-01

An experiment to evaluate the suitability of beryllium as a limiter material has been completed on the ISX-B tokamak. The experiment consisted of two phases: (1) the initial operation and characterization in the ISX experiment, and a period of continued operation to the specified surface fluence (10 22 atoms/cm 2 ) of hydrogen ions; and (2) the disassembly, decontamination, or disposal of the ISX facility. During these two phases of the project, the possibility existed for beryllium and/or beryllium oxide powder to be produced inside the vacuum vessel. Beryllium dust is a highly toxic material, and extensive precautions are required to prevent the release of the beryllium into the experimental work area and to prevent the contamination of personnel working on the device. Details of the health hazards associated with beryllium and the appropriate precautions are presented. Also described in appendixes to this report are the various operational safety requirements for the project

Modeling tritium processes in plasma-facing beryllium

International Nuclear Information System (INIS)

Longhurst, G.R.; Anderl, R.A.; Dolan, T.J.; Mulock, M.J.

1995-01-01

In this paper we present techniques and recommended parameters for modeling tritium implantation, trapping and release, and permeation, in beryllium-clad structures adjacent to the plasma. Among the features that should be considered are the effects of surface films, the mobility of beryllium through those films, damage caused by ion implantation, especially in regions where pitting may be expected, and bubble formation. Tritium transport parameters recommended are based on fits with experimental data and available theory. Estimates of inventories in ITER using these parameters are also given. 31 refs., 2 figs., 1 tab

Nuclear magnetic resonance apparatus having semitoroidal RF coil for use in topical NMR and NMR imaging

International Nuclear Information System (INIS)

Fukushima, E.; Assink, R.A.; Roeder, S.B.W.; Gibson, A.A.V.

1984-01-01

An improved nuclear magnetic resonance (NMR) apparatus for use in topical magnetic resonance (TMR) spectroscopy and other remote sensing NMR applications includes a semitoroidal radio frequency (rf) coil. The semitoroidal rf coil produces an effective alternating magnetic field at a distance from the poles of the coil, to enable NMR measurements to be taken from selected regions inside an object, particularly human and other living subjects. The semitoroidal rf coil is relatively insensitive to magnetic interference from metallic objects located behind the coil, thereby rendering the coil particularly suited for use in both conventional and superconducting NMR magnets. The semitoroidal NMR coil can be constructed so that it emits little or no excess rf electric field associated with the rf magnetic field, thus avoiding adverse effects due to dielectric heating of the sample or to any other electric field interactions. The coil may be combined with a like orthogonal coil and suitably driven to provide a circularly polarised field; or it may be used in conjunction with a concentrically nested smaller semitoroidal coil to move the maximum field further from the coil assembly. (author)

The status of beryllium research for fusion in the United States

International Nuclear Information System (INIS)

Longhurst, G.R.; Snead, L.L.; Abou-Sena, A.A.

2004-01-01

Use of beryllium in fusion reactor has been considered for neutron multiplication in breeding blankets an as an oxygen getter for plasma - facing surface. Previous beryllium research for fusion in the United States included issues of interest to fission (swelling an changes in mechanical and thermal properties) as well as interactions with plasmas and hydrogen isotopes and methods of fabrication. When the United States formally withdrew its participation in the International Experimental Reactor (ITER) program, much of this effort was terminated. The focus in the U.S. has been mainly on toxic effects of beryllium and on industrial hygiene and health-related issues. Work continued at the INEEL (Idaho National Engineering and Environmental Laboratory) and elsewhere on beryllium-containing molten salts. This activity is part of the JUPITER II Agreement. Plasma spray of ITER first wall samples at Los Alamos National Laboratory has been performed under the European Fusion Development Agreement. Effects of irradiation on beryllium structure are being studied at Oak Ridge National Laboratory. Numerical and phenomenological models are being developed and applied at the University of California Los Angels to investigate thermo-mechanical characteristics of beryllium pebble beds, similar to research being carried out at Forschungszentrum Karlsruhe and elsewhere. Additional work, not funded by the fusion program, has dealt with issues of disposal, and recycling. (author)

The Status of Beryllium Research for Fusion in the United States

International Nuclear Information System (INIS)

Glen R. Longhurst

2003-01-01

Use of beryllium in fusion reactors has been considered for neutron multiplication in breeding blankets and as an oxygen getter for plasma-facing surfaces. Previous beryllium research for fusion in the United States included issues of interest to fission (swelling and changes in mechanical and thermal properties) as well as interactions with plasmas and hydrogen isotopes and methods of fabrication. When the United States formally withdrew its participation in the International Thermonuclear Experimental Reactor (ITER) program, much of this effort was terminated. The focus in the U.S. has been mainly on toxic effects of beryllium and on industrial hygiene and health-related issues. Work continued at the INEEL and elsewhere on beryllium-containing molten salts. This activity is part of the JUPITER II Agreement. Plasma spray of ITER first wall samples at Los Alamos National Laboratory has been performed under the European Fusion Development Agreement. Effects of irradiation on beryllium structure are being studied at Oak Ridge National Laboratory. Numerical and phenomenological models are being developed and applied to better understand important processes and to assist with design. Presently, studies are underway at the University of California Los Angeles to investigate thermo-mechanical characteristics of beryllium pebble beds, similar to research being carried out at Forschungszentrum Karlsruhe and elsewhere. Additional work, not funded by the fusion program, has dealt with issues of disposal, and recycling

Dynamic Models of Heating and Cooling Coils with One—Dimensional Air Distribution

Institute of Scientific and Technical Information of China (English)

WangZijie; G.Krauss

1993-01-01

This paper presents the simulation models of the plate-fin,air-to-water(or water vapour) heat exchangers used as air-heating or air-cooling and dehumidifying colis in the HVAC(Heating,Ventilation and AIr-Conditioning)systems.The thermal models are used to calculate the heat exchange between distributing air and coil pipes and outlet temperatures of air and heat or chilled fluid.The aerodynamic models are used to account for the pressure drop of the air crossing the coil tubes,They can also be used to optimize the structres of such coils.The models are based on principal laws of teat and mass conservation and fluid mechanics.They are transparent and easy to use.In our work,a coil is considered as an assembly of numbers of basic elements in which all the state variables are unique.Therefore we can conveniently simulate the coils with different structures and different geometric parameters.Two modular programs TRNSYS(Transient System Simulation)and ESACAP are utilized as supporting softwares which make the programming and simulation greatly simplified.The coil elements and a real coil were simulated.The results were compared with the data offered by the manufacturer(company SOFICA) and also with those obtained using critical methods such as NTU method ,etc.and good agreement is attained.

Fabrication and replacement work of beryllium frame and gamma-ray shield

International Nuclear Information System (INIS)

Watahiki, Shunsuke; Hanawa, Yoshio; Asano, Norikazu; Hiyama, Kazuhisa; Ito, Sachito; Tsuboi, Kazuaki; Fukasaku, Akitomi

2012-03-01

This replacement work was carried out under refurbishment plan of JMTR for beryllium distortion draw to acceptable limit. And gamma-ray shield refurbishment was carried out the view point of prevention maintenance in consideration of operation plan. Fabrication of beryllium frame and gamma-ray shield was spent for two years it was finished in February, 2010. It took five months to replacement work from January 2010. In this report is presented fabrication and replacement work of beryllium frame and gamma-ray shield. (author)

Modular coils: a promising toroidal-reactor-coil system

International Nuclear Information System (INIS)

Chu, T.K.; Furth, H.P.; Johnson, J.L.; Ludescher, C.; Weimer, K.E.

1981-04-01

The concept of modular coils originated from a need to find reactor-relevant stellarator windings, but its usefulness can be extended to provide an externally applied, additional rotational transform in tokamaks. Considerations of (1) basic principles of modular coils, (2) types of coils, (3) types of configurations (general, helically symmetric, helically asymmetric, with magnetic well, with magnetic hill), (4) types of rotational transform profile, and (5) structure and origin of ripples are given. These results show that modular coils can offer a wide range of vacuum magnetic field configurations, some of which cannot be obtained with the classical stellarator or torsatron coil configuration

R&D for a single-layer Nb$_{3}$Sn common coil dipole using the react-and-wind fabrication technique

CERN Document Server

Ambrosio, G; Barzi, E; Bauer, P; Chichili, D R; Ewald, K D; Fehér, S; Imbasciati, L; Kashikhin, V V; Limon, P J; Litvinenko, L; Novitski, I; Rey, J M; Scanlan, R M; Yadav, S; Yamada, R; Zlobin, A V

2002-01-01

A dipole magnet based on the common coil design, using prereacted Nb /sub 3/Sn superconductor, is under development at Fermilab, for a future Very Large Hadron Collider. This magnet has some innovative design and technological features such as single layer coils, a 22 mm wide 60-strand Rutherford type cable and stainless steel collars reinforced by horizontal bridges inserted between coil blocks. Both left and right coils are wound simultaneously into the collar structure and then impregnated with epoxy. In order to optimize the design and fabrication techniques an R&D program is underway. The production of cables with the required characteristics was shown possible. Collar laminations were produced, assembled and tested in order to check the effectiveness of the bridges and the validity of the mechanical design. A mechanical model consisting in a 165 mm long section of the magnet straight section was assembled and tested. This paper summarizes the status of the program, and reports the results of fabrica...

Optimization of the JET Beryllium tile profile for power handling

International Nuclear Information System (INIS)

Nunes, I.; Vries, P. de; Lomas, P.J.; Loarte, A.

2006-01-01

The primary objective of the ITER-like wall project is to install a beryllium main wall and a tungsten divertor. From the point of view of plasma operations, the power handling properties of the new Be tiles may affect the operational space. The tiles design has to be such that it allows routine plasma operation for ITER relevant scenarios, i.e., 3-5 MA ELMy H-modes with high power input (P in > 30 MW) for lengths of time of ∼ 10 s. Due to the constrains imposed by heat conductivity, eddy current and stress torques on a Be tile, a single Be tile must be an assembly of castellated slices [Thompson V. et al, this conference]. From the point of view of plasma operations, the power handling properties of the new Be tiles can restrict the operational space of JET, if considerable melting of the tiles is to be avoided. This paper describes the power handling studies for the beryllium wall tiles and the optimisation of their design to achieve the operation goal described above. The melting temperature for Be is 1289 o C, corresponding to a energy limit of 60 MJ/m 2 for 10 s [Thompson V. et al, this conference]. For low field line angles, the power density on the toroidally facing surfaces is several times higher than the power density on the tile face requiring these to be shadowed. Furthermore the poloidally facing surfaces also have to be shadowed from assembly to assembly due to the large gap between assemblies. The tiles have been designed taking into account these limits and with a geometrical design such as to avoid exposed surfaces at high angles to the magnetic field being melted due to the expected loads. This has been achieved after detailed studies of the power handling of the various limiters and protections, including the effect of the curvature of the flux surfaces, shadowing and tolerance to misalignment. The surface of the tiles is defined such that, when possible, there is an even distribution of power density over the entire tile surface, and that

Codeposition of deuterium ions with beryllium oxide at elevated temperatures

CERN Document Server

Markin, A V; Gorodetsky, A E; Negodaev, M A; Rozhanskii, N V; Scaffidi-Argentina, F; Werle, H; Wu, C H; Zalavutdinov, R K; Zakharov, A P

2000-01-01

Deuterium-loaded BeO films were produced by sputtering the beryllium target with 10 keV Ne ions in D sub 2 gas at a pressure of approximately 1 Pa. The sputtered beryllium reacts - on the substrate surface - with the residual oxygen, thus forming a beryllium oxide layer. Biasing the substrate negatively with respect to the target provides the simultaneous bombardment of the growing film surface with D ions formed by Ne-D sub 2 collisions. Substrate potential governs the maximum energy of ions striking the growing film surface while its size governs the flux density. According to X-ray photoelectron spectroscopy (XPS), electron probe microanalysis (EPMA) and reflection high energy electron diffraction (RHEED) data, the beryllium is deposited in the form of polycrystalline hcp-BeO layers with negligible (about 1 at.%) carbon and neon retention. Thermal desorption spectroscopy (TDS) data shows a strong deuterium bonding, with a desorption peak at 950 K, in the films deposited at -50 and -400 V substrate potentia...

Hanford Site Beryllium Program: Past, Present, and Future - 12428

Energy Technology Data Exchange (ETDEWEB)

Fisher, Mark [CH2M Hill Plateau Remediation Company, Richland, Washington 99354 (United States); Garcia, Pete [U.S. Department of Energy - Richland Office, Richland, Washington 99352 (United States); Goeckner, Julie [U.S. Department of Energy - HQ, EMCBC, Cincinnati, Ohio 45202 (United States); Millikin, Emily [Washington Closure Hanford, Richland, Washington 99354 (United States); Stoner, Mike [Mission Support Alliance, Richland, Washington 99354 (United States)

2012-07-01

The U.S. Department of Energy (DOE) has a long history of beryllium use because of the element's broad application to many nuclear operations and processes. At the Hanford Site beryllium alloy was used to fabricate parts for reactors, including fuel rods for the N-Reactor during plutonium production. Because of continued confirmed cases of chronic beryllium disease (CBD), and data suggesting CBD occurs at exposures to low-level concentrations, the DOE decided to issue a rule to further protect federal and contractor workers from hazards associated with exposure to beryllium. When the beryllium rule was issued in 1999, each of the Hanford Site contractors developed a Chronic Beryllium Disease Prevention Program (CBDPP) and initial site wide beryllium inventories. A new site-wide CBDPP, applicable to all Hanford contractors, was issued in May, 2009. In the spring of 2010 the DOE Headquarters Office of Health, Safety, and Security (HSS) conducted an independent inspection to evaluate the status of implementation of the Hanford Site Chronic Beryllium Disease Prevention Program (CBDPP). The report identified four Findings and 12 cross-cutting Opportunities for Improvement (OFIs). A corrective action plan (CAP) was developed to address the Findings and crosscutting OFIs. The DOE directed affected site contractors to identify dedicated resources to participate in development of the CAP, along with involving stakeholders. The CAP included general and contractor-specific recommendations. Following initiation of actions to implement the approved CAP, it became apparent that additional definition of product deliverables was necessary to assure that expectations were adequately addressed and CAP actions could be closed. Consequently, a supplement to the original CAP was prepared and transmitted to DOE-HQ for approval. Development of the supplemental CAP was an eight month effort. From the onset a core group of CAP development members were identified to develop a mechanism

The analysis of beryllium-copper diffusion joint after HHF test

International Nuclear Information System (INIS)

Guiniatouline, R.N.; Mazul, I.V.; Rubkin, S.Y.

1995-01-01

The development of beryllium-copper joints which can withstand to relevant ITER divertor conditions is one of the important tasks at present time. One of the main problem for beryllium-copperjoints, is the inter-metallic layers, the strength and life time of joints significantly depends from the width and contents of the intermetallic layers. The objective of this work is to study the diffusion joint of TGP-56 beryllium to OFHC copper after thermal response and thermocyclic tests with beryllium-copper mockup. The BEY test were performed at e-beam facility (EBTS, SNLA). The following methods were used for analyses: the roentgenographic analysis; X-ray spectrum analysis; the fracture graphic analysis. During the investigation the followed studies were done: the analysis of diffusion boundary Be-Cu, which was obtained at the crossection of one of the tiles, the analysis of the debonded surfaces of a few beryllium tiles and corresponding copper parts; the analysis of upper surface of one of the tiles after HHF tests. The results of this work have showed that: the joint roentgenographic and elements analyses indicated the following phases in the diffusion zone: Cu 2 Be (∼170 μm), CuBe (∼30μm), CuBe 2 (∼1 μm) and solid solution of copper in beryllium. The phases Cu 2 Be, CuBe and solid solution of copper in beryllium were indicated using quantitative microanalysis and phases CuBe, CuBe 2 , Cu, Be - by roentgenographic analysis; the source of fracture (initial crack) is located in the central part of the tiles, the crack caused by the influence of residual stresses during cooling of a mock-up after fabrication and developed under the conditions of slow elastic-plastic growing during the process of thermal fatigue testing. The analysis gives the important data about joint's quality and also may be used for any type of joints and its comparison for ITER applications

Reactivity effects due to beryllium poisoning of BR2

International Nuclear Information System (INIS)

Kalcheva, S.; Ponsard, B.; Koonen, E.

2004-01-01

This paper illustrates the impact of the poisoning of the beryllium reflector on reactivity variations of the Belgian MTR BR2 in SCK.CEN. Detailed calculations by MCNP-4C of reactivity effects caused by strong neutron absorbers 3 He and 6 Li during reactor operation history are presented. The importance of beryllium poisoning for the accuracy of reactivity predictions is discussed. (authors)

Joining of beryllium by braze welding technique: preliminary results

Energy Technology Data Exchange (ETDEWEB)

Banaim, P.; Abramov, E. [Ben-Gurion Univ. of the Negev, Beersheba (Israel); Zalkind, S.; Eden, S.

1998-01-01

Within the framework of some applications, there is a need to join beryllium parts to each other. Gas Tungsten Arc Braze Welds were made in beryllium using 0.3 mm commercially Aluminum (1100) shim preplaced at the joint. The welds exhibited a tendency to form microcracks in the Fusion Zone and Heat Affected Zone. All the microcracks were backfilled with Aluminum. (author)

Extraction of beryllium sulfate by a long chain amine

International Nuclear Information System (INIS)

Etaix, E.S.

1968-01-01

The extraction of sulfuric acid in aqueous solution by a primary amine in benzene solution, 3-9 (diethyl) - 6-amino tri-decane (D.E.T. ) - i.e., with American nomenclature 1-3 (ethyl-pentyl) - 4-ethyl-octyl amine (E.P.O.) - has made it possible to calculate the formation constants of alkyl-ammonium sulfate and acid sulfate. The formula of the beryllium and alkyl-ammonium sulfate complex formed in benzene has next been determined, for various initial acidity of the aqueous solution. Lastly, evidence has been given of negatively charged complexes of beryllium and sulfate in aqueous solution, through the dependence of the aqueous sulfate ions concentration upon beryllium extraction. The formation constant of these anionic complexes has been evaluated. (author) [fr

Investigation of the beryllium ion-surface interaction

Energy Technology Data Exchange (ETDEWEB)

Guseva, M.I. [Kurchatov Inst., Moscow (Russian Federation); Birukov, A.Yu. [Kurchatov Inst., Moscow (Russian Federation); Gureev, V.M. [Kurchatov Inst., Moscow (Russian Federation); Daneljan, L.S. [Kurchatov Inst., Moscow (Russian Federation); Korshunov, S.N. [Kurchatov Inst., Moscow (Russian Federation); Martynenko, Yu.V. [Kurchatov Inst., Moscow (Russian Federation); Moskovkin, P.S. [Kurchatov Inst., Moscow (Russian Federation); Sokolov, Yu.A. [Kurchatov Inst., Moscow (Russian Federation); Stoljarova, V.G. [Kurchatov Inst., Moscow (Russian Federation); Kulikauskas, V.S. [M.V. Lomonosov University, Moscow (Russian Federation); Zatekin, V.V. [M.V. Lomonosov University, Moscow (Russian Federation)

1996-10-01

The energy and temperature dependence of self-sputtering yields of beryllium were measured. The energy dependence of the beryllium self-sputtering yield agrees well with that calculated by Eckstein et al. Below 770 K the self-sputtering yields are temperature independent; at T{sub irr.}>870 K the yield increases steeply. Beryllium samples were implanted at 370 K with monoenergetic 5 keV hydrogen ions and with a stationary hydrogen plasma power flux of about 5 MW/m{sup 2}. In the fluence range of 5 x 10{sup 22}-1.5 x 10{sup 25} m{sup -2} the depth profile is shifted towards the surface with increasing fluence and the concentration of trapped hydrogen atoms is reduced from 3.3 x 10{sup 21} to 7.4 x 10{sup 20} m{sup -2}. About 95% of the trapped hydrogen is located within bubbles and only {proportional_to}5% is trapped as atoms. With increasing implantation fluence the bubbles coalesce, producing channels through which hydrogen escapes. (orig.).

Beryllium thin films for resistor applications

Science.gov (United States)

Fiet, O.

1972-01-01

Beryllium thin films have a protective oxidation resistant property at high temperature and high recrystallization temperature. However, the experimental film has very low temperature coefficient of resistance.

Experience of beryllium blocks operation in the SM and MIR nuclear reactors useful for fusion

International Nuclear Information System (INIS)

Chakin, V.P.; Melder, R.R.; Belozerov, S.V.

2004-01-01

The results are presented concerning the examinations of state of beryllium blocks after the completion of their operation in the SM and MIR reactors. Both cracks and more significant mechanical damages are revealed in the irradiated beryllium blocks. Under neutron irradiation of beryllium radiation degradation of its physical and mechanical properties occurs. It shows itself in embrittlement, decrease of brittle strength level as well in worsening of thermal conductivity that leads to increase of thermal stresses into beryllium block. Under irradiation it takes place damage of beryllium microstructure, in particular, formation of radiation defects occurs in the form of dislocation loops and great amount of helium atoms. Optimization of beryllium radioactive waste storage is related to their preliminary surface and volumetric decontamination. (author)

Zone-refining of beryllium(II) acetylacetonate

International Nuclear Information System (INIS)

Yoshida, Isao; Kobayashi, Hiroshi; Ueno, Keihei

1975-01-01

Zone melting was applied to bis (acetylacetonato) beryllium(II), Be(AA) 2 , to remove trace metal constiutents. The effective distribution coefficient, k, of a minor component measured in a binary mixture with the majority of Be(AA) 2 , fell in the range of 0.4 to 0.8, while the value obtained in a multiple component mixture fell in the range of 0.8 to 0.9 except Zn(II)- and Ni(II) chelates. Cr(AA) 3 was concentrated upward in the direction of the zone travelling, and similar results were obtained with Cu(II)-, Co(III)- Fe(III)- and Al(III) acetylacetonates, while Zn(II)-, Ni(II)- and Mn(III) chelates were fractionated in the both ends of the column. On the other hand, when the zone was moved downward, the minor components were concentrated in the lower end of a column. Efficiency in zone refining was compared to each other between the upward- and downward zone travelling modes on the crude beryllium acetylacetonates obtained from a commercial reagent of beryllium nitrate, and the latter mode was found more effective in the concentration of trace components. Discussion was given on possible mechanisms resulting in the difference in the refining efficiency. (author)

CCHMM_PROF: a HMM-based coiled-coil predictor with evolutionary information

DEFF Research Database (Denmark)

Bartoli, Lisa; Fariselli, Piero; Krogh, Anders

2009-01-01

tools are available for predicting coiled-coil domains in protein sequences, including those based on position-specific score matrices and machine learning methods. RESULTS: In this article, we introduce a hidden Markov model (CCHMM_PROF) that exploits the information contained in multiple sequence...... alignments (profiles) to predict coiled-coil regions. The new method discriminates coiled-coil sequences with an accuracy of 97% and achieves a true positive rate of 79% with only 1% of false positives. Furthermore, when predicting the location of coiled-coil segments in protein sequences, the method reaches...

Real-time monitoring of airborne beryllium, at OSHA limit levels, by time-resolved laser-induced breakdown spectroscopy

International Nuclear Information System (INIS)

Radziemski, L.J.; Loree, T.R.; Cremers, D.A.

1982-01-01

Real-time detection of beryllium particulate is being investigated by the new technique of laser-induced breakdown spectroscopy. For beryllium detection we monitor the 313.1-nm feature of once ionized beryllium (Be II). Numerous publications describe the technique, our beryllium results, and other applications. Here we summarize the important points and describe our experiments with beryllium

Influence of impurities in Beryllium on tritium breeding ratio

International Nuclear Information System (INIS)

Yamauchi, M.; Ochiai, K.; Verzilov, Y.; Ito, M.; Wada, M.; Nishitani, T.

2004-01-01

Several neutronics experiments simulating fusion blankets have been conducted with 14 MeV neutron source to assess the reliability of nuclear analysis codes. However, the analyses have not always presented good agreements so far between calculated and measured tritium production rates. One of the reasons was considered as impurities in beryllium which has negligibly small neutron absorption cross section in low energy range. Chemical compositions of beryllium were analyzed by Inductively Coupled Plasma (ICP) method, and a pulsed neutron decay experiment discovered that the macroscopic neutron absorption cross section for beryllium medium may be about 30% larger than the value calculated by the data specified by manufacturing company. The influence of the impurities on the calculations was studied on the basis of the fusion DEMO-reactor blanket design. As a result of the study, it was made clear that the impurities affect the local tritium production rates when the size of beryllium medium is more than 20-30 mean free paths (30-40 cm) in thickness. In case of some blanket designs that meet the above condition, the effect on tritium breeding ratio may become as large as about 4%. (author)

Influence of impurities in Beryllium on tritium breeding ratio

Energy Technology Data Exchange (ETDEWEB)

Yamauchi, M; Ochiai, K; Verzilov, Y; Ito, M; Wada, M; Nishitani, T [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

2004-03-01

Several neutronics experiments simulating fusion blankets have been conducted with 14 MeV neutron source to assess the reliability of nuclear analysis codes. However, the analyses have not always presented good agreements so far between calculated and measured tritium production rates. One of the reasons was considered as impurities in beryllium which has negligibly small neutron absorption cross section in low energy range. Chemical compositions of beryllium were analyzed by Inductively Coupled Plasma (ICP) method, and a pulsed neutron decay experiment discovered that the macroscopic neutron absorption cross section for beryllium medium may be about 30% larger than the value calculated by the data specified by manufacturing company. The influence of the impurities on the calculations was studied on the basis of the fusion DEMO-reactor blanket design. As a result of the study, it was made clear that the impurities affect the local tritium production rates when the size of beryllium medium is more than 20-30 mean free paths (30-40 cm) in thickness. In case of some blanket designs that meet the above condition, the effect on tritium breeding ratio may become as large as about 4%. (author)

Evaluation of the hazard associated with fabricating beryllium copper alloys

International Nuclear Information System (INIS)

Senn, T.J.

1977-01-01

Beryllium-copper alloys should be considered toxic materials and proper controls must be used when they are machined, heated, or otherwise fabricated. Air samples should be taken for each type of fabrication to determine the worker's exposure and the effectiveness of the controls in use. It has been shown that aerosols containing beryllium are generated during the four methods of fabrication tested, and that these aerosols can be reduced through local exhaust to undetectable levels. Considering the acute, chronic and possibly carcinogenic effects of exposure to beryllium, effective controls should be required because they are feasible both technologically and economically. The health hazards and control measures are reviewed

Historical perspectives on the uses and health risks of beryllium

International Nuclear Information System (INIS)

Preuss, O.P.

1985-01-01

Unawareness of the health risks of beryllium resulted in a decade of unmitigated exposure of several thousand workers and numerous cases of beryllium disease in employees and nearby residents. Subsequent adoption of exposure limits and their implementation with effective technical controls reduced the occurrence of new cases, which were mainly due to accidental exposures, to a minimum. The fact that continuously growing production and consumption did not alter this trend demonstrates the effectiveness of the present threshold limit value. It shows that the potential health hazard can be well contained and that beryllium can be produced and fabricated without undue risk to employees or the general public

Operational experience with the JET beryllium evaporators in the J1W test bed

International Nuclear Information System (INIS)

Peacock, A.T.; Dietz, K.J.; Israel, G.; Jensen, H.S.; Johnson, A.; Pick, M.A.; Saibene, G.; Sartori, R.

1989-01-01

Four beryllium evaporators were fitted onto the JET vessel during March 1989. These evaporators are planned to give the first introduction of beryllium into the JET machine to study the effect of using beryllium as a first wall material. Over 200 hours operational experience with such an evaporator had been gained on a test bed facility in which the evaporation rate, radial evaporant distribution and head operating temperature had been determined. The results obtained on this facility with two different heat materials, sintered S-65B and vacuum cast beryllium are described. The test vessel has also been used to conduct beryllium wall pumping experiments using the ''Langmuir effect''. The initial results of these experiments will be described. (author)

TFTR Inner Support Structure final assembly and installation

International Nuclear Information System (INIS)

Rocco, R.E.; Brown, G.; Carglia, G.; Heitzenroeder, P.; Koenig, F.; Mookerjee, S.; Raugh, J.

1983-01-01

The Inner Support Structure (ISS) of the TFTR provides a specific level of restraint to the net centering force and overturning moment produced by the Toroidal Field (TF) coils and to the vertical forces produced by the Inner Poloidal Field (PF) coils. This is accomplished consistent with the need for four radial dielectric breaks running the entire length of the ISS to prevent eddy current loops. A brief description of the major components, method of manufacture and material selection of the ISS and PF coils is presented. Particular attention is given to the integration of the PF coils and the ISS components into the total assembly and the installation of strain gauges and crack monitors on the ISS. The requirements of no gaps at the interfaces of the ISS teeth at all three horizontal planes is discussed. The problem encountered with achieving the no gap requirement and the successful resolution of this problem, including its impact on installation of the ISS, is also discussed. The installation of the ISS, including setting in position, preloading with TF coil clips, and final tensioning of the tension bars is discussed. A brief description of the lower and upper lead stem splicing operation is presented. Subsequent to the final assembly, electrical tests were performed prior to and after installation on the TFTR machine. An overview of the tests and their results is presented

Report of a technical evaluation panel on the use of beryllium for ITER plasma facing material and blanket breeder material

Energy Technology Data Exchange (ETDEWEB)

Ulrickson, M.A. [ed.] [Sandia National Labs., Albuquerque, NM (United States); Manly, W.D. [Oak Ridge National Lab., TN (United States); Dombrowski, D.E. [Brush Wellman, Inc., Cleveland, OH (United States)] [and others

1995-08-01

Beryllium because of its low atomic number and high thermal conductivity, is a candidate for both ITER first wall and divertor surfaces. This study addresses the following: why beryllium; design requirements for the ITER divertor; beryllium supply and unirradiated physical/mechanical property database; effects of irradiation on beryllium properties; tritium issues; beryllium health and safety; beryllium-coolant interactions and safety; thermal and mechanical tests; plasma erosion of beryllium; recommended beryllium grades for ITER plasma facing components; proposed manufacturing methods to produce beryllium parts for ITER; emerging beryllium materials; proposed inspection and maintenance techniques for beryllium components and coatings; time table and costs; and the importance of integrating materials and manufacturing personnel with designers.

Report of a technical evaluation panel on the use of beryllium for ITER plasma facing material and blanket breeder material

International Nuclear Information System (INIS)

Ulrickson, M.A.; Manly, W.D.; Dombrowski, D.E.

1995-08-01

Beryllium because of its low atomic number and high thermal conductivity, is a candidate for both ITER first wall and divertor surfaces. This study addresses the following: why beryllium; design requirements for the ITER divertor; beryllium supply and unirradiated physical/mechanical property database; effects of irradiation on beryllium properties; tritium issues; beryllium health and safety; beryllium-coolant interactions and safety; thermal and mechanical tests; plasma erosion of beryllium; recommended beryllium grades for ITER plasma facing components; proposed manufacturing methods to produce beryllium parts for ITER; emerging beryllium materials; proposed inspection and maintenance techniques for beryllium components and coatings; time table and costs; and the importance of integrating materials and manufacturing personnel with designers

DETERMINING BERYLLIUM IN DRINKING WATER BY GRAPHITE FURNACE ATOMIC ABSORPTION SPECTROSCOPY

Science.gov (United States)

A direct graphite furnace atomic absorption spectroscopy method for the analysis of beryllium in drinking water has been derived from a method for determining beryllium in urine. Ammonium phosphomolybdate and ascorbic acid were employed as matrix modifiers. The matrix modifiers s...

Novel Coiled-Coil Cell Division Factor ZapB Stimulates Z Ring Assembly and Cell Division

DEFF Research Database (Denmark)

Ebersbach, Gitte; Galli, Elizabeth; Møller-Jensen, Jakob

2008-01-01

Formation of the Z ring is the first known event in bacterial cell division. However, it is not yet known how the assembly and contraction of the Z ring is regulated. Here, we identify a novel cell division factor ZapB in Escherichia coli that simultaneously stimulates Z ring assembly and cell...... division. Deletion of zapB resulted in delayed cell division and the formation of ectopic Z rings and spirals whereas overexpression of ZapB resulted in nucleoid condensation and aberrant cell divisions. Localization of ZapB to the divisome depended on FtsZ but not FtsA, ZipA or FtsI and ZapB interacted...... with FtsZ in a bacterial two-hybrid analysis. The simultaneous inactivation of FtsA and ZipA prevented Z ring assembly and ZapB localization. Time lapse microscopy showed that ZapB-GFP is present at mid-cell in a pattern very similar to that of FtsZ. Cells carrying a zapB deletion and the ftsZ84ts allele...

Thermal fatigue of beryllium

International Nuclear Information System (INIS)

Deksnis, E.; Ciric, D.; Falter, H.

1995-01-01

Thermal fatigue life of S65c beryllium castellated to a geometry 6 x 6 x (8-10)mm deep has been tested for steady heat fluxes of 3 MW/m 2 to 5 MW/m 2 and under pulsed heat fluxes (10-20 MW/m 2 ) for which the time averaged heat flux is 5 MW/m 2 . These tests were carried out in the JET neutral beam test facility A test sequence with peak surface temperatures ≤ 600 degrees C produced no visible fatigue cracks. In the second series of tests, with T max ≤ 750 degrees C evidence for fatigue appeared after a minimum of 1350 stress cycles. These fatigue data are discussed in view of the observed lack of thermal fatigue in JET plasma operations with beryllium PFC. JET experience with S65b and S65c is reviewed; recent operations with Φ = 25 MW/m 2 and sustained melting/resolidification are also presented. The need for a failure criterion for finite element analyses of Be PFC lifetimes is discussed

Corrosion of beryllium oxide

International Nuclear Information System (INIS)

Elston, J.; Caillat, R.

1958-01-01

Data are reported on the volatilization rate of beryllium oxide in moist air depending on temperature and water vapour concentration. They are concerned with powder samples or sintered shapes of various densities. For sintered samples, the volatilization rate is very low under the following conditions: - temperature: 1300 deg. C, - water vapour concentration in moist air: 25 g/m 3 , - flow rate: 12 I/hour corresponding to a speed of 40 m/hour on the surface of the sample. For calcinated powders (1300 deg. C), grain growth has been observed under a stream of moist air at 1100 deg. C. For instance, grain size changes from 0,5 to at least 2 microns after 500 hours of exposure at this temperature. Furthermore, results data are reported on corrosion of sintered beryllium oxide in pressurized water. At 250 deg. C, under a pressure of 40 kg/cm 2 water is very slightly corrosive; however, internal strains are revealed. Finally, some features on the corrosion in liquid sodium are exposed. (author) [fr

2-d and 1-d Nanomaterials Construction through Peptide Computational Design and Solution Assembly

Science.gov (United States)

Pochan, Darrin

Self-assembly of molecules is an attractive materials construction strategy due to its simplicity in application. By considering peptidic molecules in the bottom-up materials self-assembly design process, one can take advantage of inherently biomolecular attributes; intramolecular folding events, secondary structure, and electrostatic/H-bonding/hydrophobic interactions to define hierarchical material structure and consequent properties. Importantly, while biomimicry has been a successful strategy for the design of new peptide molecules for intermolecular assembly, computational tools have been developed to de novo design peptide molecules required for construction of pre-determined, desired nanostructures and materials. A new system comprised of coiled coil bundle motifs theoretically designed to assemble into designed, one and two-dimensional nanostructures will be introduced. The strategy provides the opportunity for arbitrary nanostructure formation, i.e. structures not observed in nature, with peptide molecules. Importantly, the desired nanostructure was chosen first while the peptides needed for coiled coil formation and subsequent nanomaterial formation were determined computationally. Different interbundle, two-dimensional nanostructures are stabilized by differences in amino acid composition exposed on the exterior of the coiled coil bundles. Computation was able to determine molecules required for different interbundle symmetries within two-dimensional sheets stabilized by subtle differences in amino acid composition of the inherent peptides. Finally, polymers were also created through covalent interactions between bundles that allowed formation of architectures spanning flexible network forming chains to ultra-stiff polymers, all with the same building block peptides. The success of the computational design strategy is manifested in the nanomaterial results as characterized by electron microscopy, scattering methods, and biophysical techniques. Support

Leachability characteristics of beryllium in redmud waste and its stabilization in cement

International Nuclear Information System (INIS)

Saradhi, I.V.; Mahadevan, T.N.; Krishnamoorthy, T.M.

1999-01-01

More than 70% of the beryl ore processed by the Beryllium Metal Plant at the BARC Vashi Complex ends up as redmud waste. The presence of significant quantities (0.4 to 0.8%) of beryllium in the redmud qualifies it as hazardous requiring safe handling, storage and disposal. The waste also contains 0.09% of water soluble fluoride. The various standard protocol of procedures were employed to estimate the leachability of beryllium from redmud for both short term and long term periods. Nearly 50% of beryllium present in redmud is leachable in water. We have tried the stabilization of redmud using portland cement. The proportion of redmud to cement was in the ratio of 1:1, 1:2 and 1:4. The blocks were cast, cured and used in the leachability experiments using standard protocols as above. The results of the TCLP test gave the levels of beryllium well below the standard limits in the TCLP extract of cement stabilized waste indicating the suitability of stabilization of redmud with cement whereas that of raw waste (redmud) are much higher than the prescribed limits. The total leach percent of beryllium in 1:2 block is 0.05% over period of 164 days whereas 1:1 and 1:4 gave a leach percent of 0.26 and 0.15% respectively. The DLT results indicate, diffusion controlled release of beryllium from the cement stabilized redmud blocks. The effective diffusion coefficient of beryllium obtained from the modelling study is 10 orders of magnitude less than the molecular diffusion coefficient of beryllium indicating the effectiveness of cement stabilization. From the detailed experiments performed, it is felt that 1:2 proportion of redmud and cement will be the best suited option for stabilization of redmud waste. The 1:1 proportion of redmud to cement mixture which could not be cast into compact cement blocks also exhibited very low leachability characteristics similar to 1:2 and 1:4 and can be be favourably considered for stabilization in case of space constraints at storage sites. The

Sensitive quench detection of the HTS coil using a co-winding coil

International Nuclear Information System (INIS)

Takagi, Tomohiro; Ariyama, Takahiro; Takao, Tomoaki; Tsukamoto, Osami

2017-01-01

The authors have studied the co-winding coil method (CW method) using the co-wound coil electrically insulated from the HTS coil. In this method, the quench is detected by the voltage difference between the coil of the HTS tape (HTS coil) and the coil of the normal conductor (CW coil). The voltage induced in the CW coil caused by the change of the magnetic field is almost the same as that in the HTS coil because the coils are magnetically coupled close to each other. Therefore, it is expected that the induced voltage will be canceled with high accuracy and that the resistive voltage in the HTS coil will be detected with greater sensitivity compared to the bridge balance method, which is used commonly. In this study, quench detection applying the CW method is demonstrated using an experimental double-pancake coil. A tape with the copper layer deposited on the polymer substrate was used as the insulated conductor wire to form the CW coil. An additional pancake coil was used to expose the experimental double-pancake coil to the external magnetic field asymmetrically. It was shown that the CW method can detect the resistive voltage with greater sensitivity even when the HTS coil was exposed to the changing asymmetric external magnetic field. (author)

Physicochemical characteristics of aerosol particles generated during the milling of beryllium silicate ores: implications for risk assessment.

Science.gov (United States)

Stefaniak, Aleksandr B; Chipera, Steve J; Day, Gregory A; Sabey, Phil; Dickerson, Robert M; Sbarra, Deborah C; Duling, Mathew G; Lawrence, Robert B; Stanton, Marcia L; Scripsick, Ronald C

2008-01-01

Inhalation of beryllium dusts generated during milling of ores and cutting of beryl-containing gemstones is associated with development of beryllium sensitization and low prevalence of chronic beryllium disease (CBD). Inhalation of beryllium aerosols generated during primary beryllium production and machining of the metal, alloys, and ceramics are associated with sensitization and high rates of CBD, despite similar airborne beryllium mass concentrations among these industries. Understanding the physicochemical properties of exposure aerosols may help to understand the differential immunopathologic mechanisms of sensitization and CBD and lead to more biologically relevant exposure standards. Properties of aerosols generated during the industrial milling of bertrandite and beryl ores were evaluated. Airborne beryllium mass concentrations among work areas ranged from 0.001 microg/m(3) (beryl ore grinding) to 2.1 microg/m(3) (beryl ore crushing). Respirable mass fractions of airborne beryllium-containing particles were 80% in high-energy input areas (beryl melting, beryl grinding). Particle specific surface area decreased with processing from feedstock ores to drumming final product beryllium hydroxide. Among work areas, beryllium was identified in three crystalline forms: beryl, poorly crystalline beryllium oxide, and beryllium hydroxide. In comparison to aerosols generated by high-CBD risk primary production processes, aerosol particles encountered during milling had similar mass concentrations, generally lower number concentrations and surface area, and contained no identifiable highly crystalline beryllium oxide. One possible explanation for the apparent low prevalence of CBD among workers exposed to beryllium mineral dusts may be that characteristics of the exposure material do not contribute to the development of lung burdens sufficient for progression from sensitization to CBD. In comparison to high-CBD risk exposures where the chemical nature of aerosol

Assessment of the beryllium lymphocyte proliferation test using statistical process control.

Science.gov (United States)

Cher, Daniel J; Deubner, David C; Kelsh, Michael A; Chapman, Pamela S; Ray, Rose M

2006-10-01

Despite more than 20 years of surveillance and epidemiologic studies using the beryllium blood lymphocyte proliferation test (BeBLPT) as a measure of beryllium sensitization (BeS) and as an aid for diagnosing subclinical chronic beryllium disease (CBD), improvements in specific understanding of the inhalation toxicology of CBD have been limited. Although epidemiologic data suggest that BeS and CBD risks vary by process/work activity, it has proven difficult to reach specific conclusions regarding the dose-response relationship between workplace beryllium exposure and BeS or subclinical CBD. One possible reason for this uncertainty could be misclassification of BeS resulting from variation in BeBLPT testing performance. The reliability of the BeBLPT, a biological assay that measures beryllium sensitization, is unknown. To assess the performance of four laboratories that conducted this test, we used data from a medical surveillance program that offered testing for beryllium sensitization with the BeBLPT. The study population was workers exposed to beryllium at various facilities over a 10-year period (1992-2001). Workers with abnormal results were offered diagnostic workups for CBD. Our analyses used a standard statistical technique, statistical process control (SPC), to evaluate test reliability. The study design involved a repeated measures analysis of BeBLPT results generated from the company-wide, longitudinal testing. Analytical methods included use of (1) statistical process control charts that examined temporal patterns of variation for the stimulation index, a measure of cell reactivity to beryllium; (2) correlation analysis that compared prior perceptions of BeBLPT instability to the statistical measures of test variation; and (3) assessment of the variation in the proportion of missing test results and how time periods with more missing data influenced SPC findings. During the period of this study, all laboratories displayed variation in test results that

Analysis of a beryllium-copper diffusion joint after HHF test

International Nuclear Information System (INIS)

Guiniatouline, R.N.; Mazul, I.V.; Gorodetsky, A.E.; Zalavutdinov, R.Kh.; Rybakov, S.Yu.; Savenko, V.I.

1996-01-01

The development of beryllium-copper joints which can withstand relevant ITER divertor conditions is one of the important tasks at the present time. One of the main problems associated with these joints is the intermetallic layers. The strength and life of these joints significantly depend on the width and contents of the intermetallic layers. The objective of this work is to study the diffusion joint of TGP-56 beryllium to OFHC copper after thermal response and thermocyclic tests with a beryllium-copper mock-up. The HHF test was performed on the e-beam facility (EBTS, SNLA). The following methods were used for analysis: roentgenographic analysis, X-ray spectrum analysis and fracture analysis. During the investigation the following studies were undertaken: the analysis of the diffusion boundary layer, which was obtained at the cross-section of one of the tiles, the analysis of the debonded surfaces of several beryllium tiles and corresponding copper parts and the analysis of the upper surface of one of the tiles after HHF tests. The joint roentgenographic and element analyses revealed the following phases in the diffusion zone: Cu 2 Be (∝170 μm), CuBe (∝30 μm), CuBe 2 (∝1 μm) and a solid solution of copper in beryllium. The phases Cu 2 Be, CuBe and the solid solution of copper in beryllium were detected by the quantitative microanalysis and the phases CuBe, CuBe 2 and CuBe, by the roentgenographic analysis. The fracture (origin) is located in the central part of the tiles. This crack was caused by residual stresses and thermal fatigue testing. This analysis provides important data on the joint quality and may be used for all types of joints used for ITER applications. (orig.)

Worker Environment Beryllium Characterization Study

International Nuclear Information System (INIS)

2009-01-01

This report summarizes the conclusion of regular monitoring of occupied buildings at the Nevada Test Site and North Las Vegas facility to determine the extent of beryllium (Be) contamination in accordance with Judgment of Needs 6 of the August 14, 2003, 'Minnema Report.'

Conductor fabrication for ITER Model Coils. Status of the EU cabling and jacketing activities

International Nuclear Information System (INIS)

Corte, A. della; Ricci, M.V.; Spadoni, M.; Bessette, D.; Duchateau, J.L.; Salpietro, E.; Garre, R.; Rossi, S.; Penco, R.; Laurenti, A.

1994-01-01

The conductors for the ITER magnets are being defined according to the operating requirements of the machine. To demonstrate the technological feasibility of the main features of the magnets, two model coils (central solenoid and toroidal field), with bores in the range 2-3 m, will be manufactured. This is the first significant industrial production of full-size conductor (a total of about 6.5 km for these coils). One cabling and one jacketing line have been assembled in Europe. The former can cable up to 1100 m (6 tons) unit lengths; the latter, which can also handle 1000 m conductor lengths, has been assembled in a shorter version (320 m). A description of the lines is reported, together with the results of the trials performed up to now. (author) 2 figs

Design and fabrication of a beryllium limiter for ISX-B

International Nuclear Information System (INIS)

Edmonds, P.H.; Watson, R.D.; Smith, M.F.

1984-01-01

A movable, temperature-controlled, beryllium rail limiter has been used in the Impurity Study Experiment (ISX-B) tokamak at the Oak Ridge National Laboratory (ORNL). The purpose of the experiment was to evaluate the suitability of the material for installation on the Joint European Torus (JET) experiment. The limiter was designed for a surface temperature rise of 600 0 C for each tokamak shot. This rise corresponds to a heat flux to the limiter surface of approximately 2.1 to 2.4 kW/cm 2 for 0.3 s. The experimental test was expected to require a lifetime of approximately 3000 neutral beam-heated plasma discharges to meet the planned surface fluence of 10 22 hydrogen ions per cm 2 . A temperature control system was used to maintain the base-plate temperature of the limiter at about 200 0 C. Normal plasma radius was 24 cm. The experimental results indicate that the beryllium limiter functions normally unless brought to melting point, when evaporated beryllium covers the liner walls, gettering the discharge. Under these conditions beryllium was the dominant impurity

Long-term follow-up of beryllium sensitized workers from a single employer

Directory of Open Access Journals (Sweden)

Curtis Anne M

2010-01-01

Full Text Available Abstract Background Up to 12% of beryllium-exposed American workers would test positive on beryllium lymphocyte proliferation test (BeLPT screening, but the implications of sensitization remain uncertain. Methods Seventy two current and former employees of a beryllium manufacturer, including 22 with pathologic changes of chronic beryllium disease (CBD, and 50 without, with a confirmed positive test were followed-up for 7.4 +/-3.1 years. Results Beyond predicted effects of aging, flow rates and lung volumes changed little from baseline, while DLCO dropped 17.4% of predicted on average. Despite this group decline, only 8 subjects (11.1% demonstrated physiologic or radiologic abnormalities typical of CBD. Other than baseline status, no clinical or laboratory feature distinguished those who clinically manifested CBD at follow-up from those who did not. Conclusions The clinical outlook remains favorable for beryllium-sensitized individuals over the first 5-12 years. However, declines in DLCO may presage further and more serious clinical manifestations in the future. These conclusions are tempered by the possibility of selection bias and other study limitations.

Characterization of beryllium foil produced by hot rolling

International Nuclear Information System (INIS)

Wittenauer, J.; Nieh, T.G.; Waychunas, G.

1992-01-01

Beryllium foil is important for a number of aerospace applications including honeycomb structures and metal-matrix composites. In this study, a method of producing beryllium foil directly from powder or flake is demonstrated. A variety of foils were produced in the thickness range 90-300 μm, free from defects such as pinholes and excessive surface roughness, and exhibiting sufficient formability for honeycomb manufacture. Foil produced directly from powder or flake exhibits crystallographic texture, microstructure, and formability equivalent to foil produced from more massive precursors. (Author)

Mechanical compression tests of beryllium pebbles after neutron irradiation up to 3000 appm helium production

Energy Technology Data Exchange (ETDEWEB)

Chakin, V., E-mail: vladimir.chakin@kit.edu [Karlsruhe Institute of Technology, Institite for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Rolli, R.; Moeslang, A. [Karlsruhe Institute of Technology, Institite for Applied Materials, Hermann-von-Helmholtz-Platz 1, 76344 Eggenstein-Leopoldshafen (Germany); Zmitko, M. [The European Joint Undertaking for ITER and the Development of Fusion Energy, c/Josep Pla, no. 2, Torres Diagonal Litoral, Edificio B3, 08019 Barcelona (Spain)

2015-04-15

Highlights: • Compression tests of highly neutron irradiated beryllium pebbles have been performed. • Irradiation hardening of beryllium pebbles decreases the steady-state strain-rates. • The steady-state strain-rates of irradiated beryllium pebbles exceed their swelling rates. - Abstract: Results: of mechanical compression tests of irradiated and non-irradiated beryllium pebbles with diameters of 1 and 2 mm are presented. The neutron irradiation was performed in the HFR in Petten, The Netherlands at 686–968 K up to 1890–2950 appm helium production. The irradiation at 686 and 753 K cause irradiation hardening due to the gas bubble formation in beryllium. The irradiation-induced hardening leads to decrease of steady-state strain-rates of irradiated beryllium pebbles compared to non-irradiated ones. In contrary, after irradiation at higher temperatures of 861 and 968 K, the steady-state strain-rates of the pebbles increase because annealing of irradiation defects and softening of the material take place. It was shown that the steady-state strain-rates of irradiated beryllium pebbles always exceed their swelling rates.

Comparison of the induced fields using different coil configurations during deep transcranial magnetic stimulation.

Directory of Open Access Journals (Sweden)

Mai Lu

Full Text Available Stimulation of deeper brain structures by transcranial magnetic stimulation (TMS plays a role in the study of reward and motivation mechanisms, which may be beneficial in the treatment of several neurological and psychiatric disorders. However, electric field distributions induced in the brain by deep transcranial magnetic stimulation (dTMS are still unknown. In this paper, the double cone coil, H-coil and Halo-circular assembly (HCA coil which have been proposed for dTMS have been numerically designed. The distributions of magnetic flux density, induced electric field in an anatomically based realistic head model by applying the dTMS coils were numerically calculated by the impedance method. Results were compared with that of standard figure-of-eight (Fo8 coil. Simulation results show that double cone, H- and HCA coils have significantly deep field penetration compared to the conventional Fo8 coil, at the expense of induced higher and wider spread electrical fields in superficial cortical regions. Double cone and HCA coils have better ability to stimulate deep brain subregions compared to that of the H-coil. In the mean time, both double cone and HCA coils increase risk for optical nerve excitation. Our results suggest although the dTMS coils offer new tool with potential for both research and clinical applications for psychiatric and neurological disorders associated with dysfunctions of deep brain regions, the selection of the most suitable coil settings for a specific clinical application should be based on a balanced evaluation between stimulation depth and focality.

Monitoring beryllium during site cleanup and closure using a real-time analyzer

Energy Technology Data Exchange (ETDEWEB)

Schlager, R.J.; Sappey, A.D.; French, P.D. [ADA Technologies, Inc., Englewood, CO (United States)

1998-12-31

Beryllium metal has a number of unique properties that have been exploited for use in commercial and government applications. Airborne beryllium particles can represent a significant human health hazard if deposited in the lungs. These particles can cause immunologically-mediated chronic granulomatous lung disease (chronic beryllium disease). Traditional methods of monitoring airborne beryllium involve collecting samples of air within the work area using a filter. The filter then undergoes chemical analysis to determine the amount of beryllium collected during the sampling period. These methods are time-consuming and results are known only after a potential exposure has occurred. The need for monitoring exposures in real time has prompted government and commercial companies to develop instrumentation that will allow for the real time assessment of short-term exposures so that adequate protection for workers in contaminated environments can be provided. Such an analyzer provides a tool that will allow government and commercial sites to be cleaned up in a more safe and effective manner since exposure assessments can be made instantaneously. This paper describes the development and initial testing of an analyzer for monitoring airborne beryllium using a technique known as Laser-Induced Breakdown Spectroscopy (LIBS). Energy from a focused, pulsed laser is used to vaporize a sample and create an intense plasma. The light emitted from the plasma is analyzed to determine the quantity of beryllium in the sampled air. A commercial prototype analyzer has been fabricated and tested in a program conducted by Lawrence Livermore National Laboratory, Los Alamos National Laboratory, Lovelace Respiratory Research Institute, and ADA Technologies, Inc. Design features of the analyzer and preliminary test results are presented.

A Hold-down Margin Assessment using Statistical Method for the PWR Fuel Assembly

International Nuclear Information System (INIS)

Jeon, S. Y.; Park, N. K.; Lee, K. S.; Kim, H. K.

2007-01-01

The hold-down springs provide an acceptable hold down force against hydraulic uplift force absorbing the length change of the fuel assembly relative to the space between the upper and lower core plates in PWR. These length changes are mainly due to the thermal expansion, irradiation growth and creep down of the fuel assemblies. There are two kinds of hold-down springs depending on the different design concept of the reactor internals of the PWR in Korea, one is a leaf-type hold down spring for Westinghouse type plants and the other is a coil-type hold-down spring for OPR1000 (Optimized Power Reactor 1000). There are four sets of hold-down springs in each fuel assembly for leaf type hold-down spring and each set of the hold-down springs consists of multiple tapered leaves to form a cantilever leaf spring set. The length, width and thickness of the spring leaves are selected to provide the desired spring constant, deflection range, and hold down force. There are four coil springs in each fuel assembly for coil-type hold-down spring. In this study, the hold-down forces and margins were calculated for the leaf-type and coil-type hold-down springs considering geometrical data of the fuel assembly and its components, length changes of the fuel assembly due to thermal expansion, irradiation growth, creep, and irradiation relaxation. The hold-down spring forces were calculated deterministically and statistically to investigate the benefit of the statistical calculation method in view of hold-down margin. The Monte-Carlo simulation method was used for the statistical hold down force calculation

Optimization of Coil Element Configurations for a Matrix Gradient Coil.

Science.gov (United States)

Kroboth, Stefan; Layton, Kelvin J; Jia, Feng; Littin, Sebastian; Yu, Huijun; Hennig, Jurgen; Zaitsev, Maxim

2018-01-01

Recently, matrix gradient coils (also termed multi-coils or multi-coil arrays) were introduced for imaging and B 0 shimming with 24, 48, and even 84 coil elements. However, in imaging applications, providing one amplifier per coil element is not always feasible due to high cost and technical complexity. In this simulation study, we show that an 84-channel matrix gradient coil (head insert for brain imaging) is able to create a wide variety of field shapes even if the number of amplifiers is reduced. An optimization algorithm was implemented that obtains groups of coil elements, such that a desired target field can be created by driving each group with an amplifier. This limits the number of amplifiers to the number of coil element groups. Simulated annealing is used due to the NP-hard combinatorial nature of the given problem. A spherical harmonic basis set up to the full third order within a sphere of 20-cm diameter in the center of the coil was investigated as target fields. We show that the median normalized least squares error for all target fields is below approximately 5% for 12 or more amplifiers. At the same time, the dissipated power stays within reasonable limits. With a relatively small set of amplifiers, switches can be used to sequentially generate spherical harmonics up to third order. The costs associated with a matrix gradient coil can be lowered, which increases the practical utility of matrix gradient coils.

Permeation behavior of deuterium implanted into beryllium

Energy Technology Data Exchange (ETDEWEB)

Nakamura, Hirofumi; Hayashi, Takumi; O' hira, Shigeru; Nishi, Masataka [Japan Atomic Energy Research Inst., Tokai, Ibaraki (Japan). Tokai Research Establishment

2001-09-01

Study on Implantation Driven Permeation (IDP) behavior of deuterium through pure beryllium was investigated as a part of the research to predict the tritium permeation through the first wall components ITER (International Thermonuclear Experimental Reactor). The permeation experiments were carried out with two beryllium specimens, one was an unannealed specimen and the other was that annealed at 1173 K. The permeation flux was measured as a function of specimen temperature and incident ion flux. Surface analysis of specimen was also carried out after the permeation experiment. Permeation was observed only with the annealed specimen and no significant permeation was observed with unannealed specimen under the present experimental condition (maximum temperature: 685 K, detection limit: 1x10{sup 13} D atoms/m{sup 2}s). It could be attributed that the intrinsic lattice defects, which act as diffusion preventing site, decreased with the specimen annealing. Based on the result of steady and transient permeation behavior and surface analysis, it was estimated that the deuterium permeation implanted into annealed beryllium was controlled by surface recombination due to the oxide layer on the surface of the permeated side. (author)

Quantifying design trade-offs of beryllium targets on NIF

Science.gov (United States)

Yi, S. A.; Zylstra, A. B.; Kline, J. L.; Loomis, E. N.; Kyrala, G. A.; Shah, R. C.; Perry, T. S.; Kanzleiter, R. J.; Batha, S. H.; MacLaren, S. A.; Ralph, J. E.; Masse, L. P.; Salmonson, J. D.; Tipton, R. E.; Callahan, D. A.; Hurricane, O. A.

2017-10-01

An important determinant of target performance is implosion kinetic energy, which scales with the capsule size. The maximum achievable performance for a given laser is thus related to the largest capsule that can be imploded symmetrically, constrained by drive uniformity. A limiting factor for symmetric radiation drive is the ratio of hohlraum to capsule radii, or case-to-capsule ratio (CCR). For a fixed laser energy, a larger hohlraum allows for driving bigger capsules symmetrically at the cost of reduced peak radiation temperature (Tr). Beryllium ablators may thus allow for unique target design trade-offs due to their higher ablation efficiency at lower Tr. By utilizing larger hohlraum sizes than most modern NIF designs, beryllium capsules thus have the potential to operate in unique regions of the target design parameter space. We present design simulations of beryllium targets with a large CCR = 4.3 3.7 . These are scaled surrogates of large hohlraum low Tr beryllium targets, with the goal of quantifying symmetry tunability as a function of CCR. This work performed under the auspices of the U.S. DOE by LANL under contract DE-AC52- 06NA25396, and by LLNL under Contract DE-AC52-07NA27344.

Semi-solid metal forming of beryllium-reinforced aluminum alloys

International Nuclear Information System (INIS)

Haws, W.; Lane, L.; Marder, J.; Nicholas, N.

1995-01-01

A Powder Metallurgy (PM) based, Semi-Solid Metal (SSM) forming process has been developed to produce low cost near-net shapes of beryllium-reinforced aluminum alloys. Beryllium acts as a reinforcing additive to the aluminum, in which there is nearly no mutual solid solubility. The modulus of elasticity of the alloy dramatically increases, while the density and thermal expansion coefficient decrease with increasing beryllium content. The material is suitable for complex thermal management and vibration resistance applications, as well as for airborne components which are density and stiffness sensitive. The forming process involves heating a blank of the material to a temperature at which the aluminum is semi-solid and the beryllium is solid. The semi-solid blank is then injected without turbulence into a permanent mold. High quality, near net shape components can be produced which are functionally superior to those produced by other permanent mold processes. Dimensional accuracy is equivalent to or better than that obtained in high pressure die casting. Cost effectiveness is the primary advantage of this technique compared to other forming processes. The advantages and limitations of the process are described. Physical and mechanical property data are presented, as well as directions for future investigation

Worker Environment Beryllium Characterization Study

Energy Technology Data Exchange (ETDEWEB)

NSTec Environment, Safety, Health & Quality

2009-12-28

This report summarizes the conclusion of regular monitoring of occupied buildings at the Nevada Test Site and North Las Vegas facility to determine the extent of beryllium (Be) contamination in accordance with Judgment of Needs 6 of the August 14, 2003, “Minnema Report.”

Mechanical properties of ISABELLE superconducting coils

Energy Technology Data Exchange (ETDEWEB)

Thompson, P.; Bertsche, A.; Fuhrmann, J.; Greene, A.; Grove, E.; Repeta, L.; Short, F.; Tannenbaum, M.; Wanderer, P.

1981-01-01

As a part of the manufacturing processes, several mechanical measurements are made on ISABELLE dipoles. These are done both to control the process and to provide information for the evaluation of the behavior of the completed magnets. This paper discusses the Young's Modulus (E = 1-3 x 10/sup 6/ psi), the thermal contraction of the coil assembly (..delta..L/L = 290 +- 17 x 10/sup -5/ at 77/sup 0/K), and the loss of applied prestress with time (approx. 20% for times 20 days).

The uses and adverse effects of beryllium on health

DEFF Research Database (Denmark)

Cooper, Ross G.; Harrison, Adrian Paul

2009-01-01

published in sources unobtainable through requests at the British Library, and some had no impact factor and were excluded. Conclusion: Beryllium has some useful but undoubtedly harmful effects on health and well-being. Measures needed to be taken to prevent hazardous exposure to this element, making its......Context: This review describes the health effects of beryllium exposure in the workplace and the environment. Aim: To collate information on the consequences of occupational and environmental exposure to beryllium on physiological function and well being. Materials and Methods: The criteria used...... tabulated. Years 2001-10 gave the greatest match (45.9%) for methodological parameters, followed by 27.71% for 1991-2000. Years 1971-80 and 1981-90 were not significantly different in the information published and available whereas years 1951-1960 showed a lack of suitable articles. Some articles were...

Lawrence Livermore Laboratory's beryllium control program for high-explosive test firing bunkers and tables

International Nuclear Information System (INIS)

Johnson, J.S.

1980-01-01

This report on the control program to minimize beryllium levels in Laboratory workplaces includes an outline of beryllium surface, soil, and air levels and an 11-y summary of sampling results from two high-use, high-explosive test firing bunkers. These sampling data and other studies demonstrate that the beryllium control program is functioning effectively

Routine phasing of coiled-coil protein crystal structures with AMPLE

Directory of Open Access Journals (Sweden)

Jens M. H. Thomas

2015-03-01

Full Text Available Coiled-coil protein folds are among the most abundant in nature. These folds consist of long wound α-helices and are architecturally simple, but paradoxically their crystallographic structures are notoriously difficult to solve with molecular-replacement techniques. The program AMPLE can solve crystal structures by molecular replacement using ab initio search models in the absence of an existent homologous protein structure. AMPLE has been benchmarked on a large and diverse test set of coiled-coil crystal structures and has been found to solve 80% of all cases. Successes included structures with chain lengths of up to 253 residues and resolutions down to 2.9 Å, considerably extending the limits on size and resolution that are typically tractable by ab initio methodologies. The structures of two macromolecular complexes, one including DNA, were also successfully solved using their coiled-coil components. It is demonstrated that both the ab initio modelling and the use of ensemble search models contribute to the success of AMPLE by comparison with phasing attempts using single structures or ideal polyalanine helices. These successes suggest that molecular replacement with AMPLE should be the method of choice for the crystallographic elucidation of a coiled-coil structure. Furthermore, AMPLE may be able to exploit the presence of a coiled coil in a complex to provide a convenient route for phasing.

Application of powder metallurgy beryllium in Beijing spectrometer III beam pipe

International Nuclear Information System (INIS)

Zheng Lifang; Li Xunfeng; Wang Li; Ji Quan; Liu Jianping

2008-01-01

According to the requirements of Beijing Spectrometer III (BESIII) beam pipe, the physical properties of several materials were compared and powder metallurgy beryllium was chosen as the material for the central pipe of the BES III beam pipe. Weight-loss method was used to study the corrosion of powder metallurgy beryllium in No. 1 oil for electron discharge machining (EDM-1). The result shows that the anticorrosive property of powder metallurgy beryllium in EDM-1 is high. The corrosion rate, 4.18 x 10 -7 kg· m -2 ·h -1 in initial stage, becomes small with the lapse of the time and stabilizes at 1.54 x 10 -7 kg·m -2 ·h -1 at last. It can be estimated that the powder metallurgy beryllium will be corroded 19.9 μm in the depth in 10 years and it accounts for 3.32% of the smallest thickness of the central pipe, which satisfies the requirements of the BESIII. (authors)

Detection of beryllium in oxides and silicates by electron-probe microanalysis

Directory of Open Access Journals (Sweden)

V. V. Khiller

2017-12-01

Full Text Available The author developed the technique of electron-probe microanalysis for quantitative determination of beryllium content, providing the example of studying natural minerals (aluminosilicates and oxides. This technique allowed to obtain a quantitative content of beryllium (in combination with other elements in the emeralds of the Mariinsky beryllium deposit and in zonal mariinskite-chrysoberyl from the chromitites of the Bazhenov ophiolite complex. All analyzes of minerals were performed on a CAMECA SX 100 electron probe microanalyzer with five wave spectrometers (IGG UB RAS. The pressure in the sample chamber was 2 × 10–4 Pa, in the electron gun region – 4 × 10–6 Pa, in wave spectrometers – 7 Pa. Accelerating voltage was 10 kV, the current of absorbed electrons on the Faraday cylinder (beam current was 100–150 nA. Diameter of the electron beam focused on the sample was 2 μm, the angle of x-ray extraction was 40°. The spectra were obtained on wave spectrometers with TAP crystal analyzers (2d = 25.745 Å, LPET (2d = 8.75 Å, LiF (2d = 4.0226 Å, and PC3 (2d = 211.4 Å, a specialized crystal for determining the content of beryllium and boron; the author carried out all the elements measurements along the Kα-lines. To determine position of the analytical peak and the background from two sides with the minimum possible spectral overlap, the author preliminarily recorded spectra on wave spectrometers. The obtained microprobe analyzes of minerals with quantitative determination of beryllium converge well with the available theoretical compositions of beryl and chrysoberyl, which indicates the high efficiency of the developed technique. By using this technique, we can relatively quickly and reliably determine the quantitative content of beryllium in natural silicates and oxides, which is an acute need for geological researchers studying the mineralogy of beryllium deposits.

Design and tests of a simplified divertor dummy coil structure for the WEST project

International Nuclear Information System (INIS)

Doceul, L.; Bucalossi, J.; Dougnac, H.; Ferlay, F.; Gargiulo, L.; Keller, D.; Larroque, S.; Lipa, M.; Pilia, A.; Saille, A.; Samaille, F.; Soler, B.; Thouvenin, D.; Verger, J.M.; Zago, B.; Portafaix, C.; Salami, M.

2015-01-01

Full text of publication follows. In order to fully validate actively cooled tungsten plasma facing components (industrial fabrication, operation with long plasma duration), the implementation of a tungsten axisymmetric divertor structure in the tokamak Tore-Supra is studied. With this major upgrade, so called WEST (Tungsten Environment in Steady state Tokamak), Tore-Supra will be able to address the problematic of long plasma discharges with a metallic divertor target. To do so, it is planned to install two symmetric divertor coils inside the vacuum vessel. This assembly, called divertor structure, is made up of two stainless steel casings containing a copper winding pack cooled by a pressurized hot water circuit (up to 200 Celsius degrees, 4 MPa) and is designed to perform steady state plasma operation (up to 1000 s). The divertor structure will be a complex assembly of 4 meter diameter and 4 meter height representing a total weight of around 20 tonnes. The technical challenge of this component will be the implementation of angular sectors inside the vacuum vessel environment (TIG welding of the coil casing, induction brazing and electrical insulation of the copper winding). Moreover, this complex assembly must sustain harsh environmental conditions in terms of ultra high vacuum conditions, mechanical loads (induced by disruptions) and electrical isolation (13 kV test) under high temperature. In order to fully validate the feasibility, the mounting and the performance of this complex component, the production of a scale one dummy coil is in progress. The paper will illustrate, the technical developments performed during 2012 in order to finalise the design for the call for tender phase. The progress and the first results of the simplified dummy coils will be also addressed. (authors)

Lawrence Livermore Laboratory's beryllium control program for high-explosive test firing bunkers and tables

International Nuclear Information System (INIS)

Johnson, J.S.

1978-01-01

This detailed report on Lawrence Livermore Laboratory's control program to minimize beryllium levels in Laboratory workplaces includes an outline of beryllium surface, soil, and air levels and an 11-y summary of sampling results from two high-use, high-explosive test firing bunkers. These sampling data and other studies demonstrate that the beryllium control program is funcioning effectively

Introduction to beryllium: uses, regulatory history, and disease.

Science.gov (United States)

Kolanz, M E

2001-05-01

Beryllium is an ubiquitous element in the environment, and it has many commercial applications. Because of its strength, electrical and thermal conductivity, corrosion resistance, and nuclear properties, beryllium products are used in the aerospace, automotive, energy, medical, and electronics industries. What eventually came to be known as chronic beryllium disease (CBD) was first identified in the 1940s, when a cluster of cases was observed in workers from the fluorescent light industry. The U.S. Atomic Energy Commission recommended the first 8-hour occupational exposure limit (OEL) for beryllium of 2.0 microg/m3 in 1949, which was later reviewed and accepted by the American Conference of Governmental Industrial Hygienists (ACGIH), the American Industrial Hygiene Association (AIHA), the American National Standards Institute (ANSI), the Occupational Safety and Health Administration (OSHA), and the vast majority of countries and standard-setting bodies worldwide. The 2.0 microg/m3 standard has been in use by the beryllium industry for more than 50 years and has been considered adequate to protect workers against clinical CBD. Recently, improved diagnostic techniques, including immunological testing and safer bronchoscopy, have enhanced our ability to identify subclinical CBD cases that would have formerly remained unidentified. Some recent epidemiological studies have suggested that some workers may develop CBD at exposures less than 2.0 microg/m3. ACGIH is currently reevaluating the adequacy of the current 2.0 microg/m3 guideline, and a plethora of research initiatives are under way to provide a better understanding of the cause of CBD. The research is focusing on the risk factors and exposure metrics that could be associated with CBD, as well as on efforts to better characterize the natural history of CBD. There is growing evidence that particle size and chemical form may be important factors that influence the risk of developing CBD. These research efforts are

Triple Halo Coil: Development and Comparison with Other TMS Coils

Science.gov (United States)

Rastogi, Priyam; Hadimani, Ravi; Jiles, David

Transcranial Magnetic Stimulation (TMS) is a non-invasive stimulation technique that can be used for the treatment of various neurological disorders such as Parkinson's Disease, PTSD, TBI and anxiety by regulating synaptic activity. TMS is FDA approved for the treatment of major depressive disorder. There is a critical need to develop deep TMS coils that can stimulate deeper regions of the brain without excessively stimulating the cortex in order to provide an alternative to surgical methods. We have developed a novel multi-coil configuration called ``Triple Halo Coil'' (THC) that can stimulate deep brain regions. Investigation of induced electric and magnetic field in these regions have been achieved by computer modelling. Comparison of the results due to THC configuration have been conducted with other TMS coils such as ``Halo Coil'', circular coil and ``Figure of Eight'' coil. There was an improvement of more than 15 times in the strength of magnetic field, induced by THC configuration at 10 cm below the vertex of the head when compared with the ``Figure of Eight'' coil alone. Carver Charitable Trust.

Preparation and physical characteristics of a lithium-beryllium-substituted fluorapatite

International Nuclear Information System (INIS)

Lexa, D.

1999-01-01

A lithium-beryllium-substituted fluorapatite, Li 0.50 Be 0.25 Ca 4.50 (PO 4 ) 3 F, has been prepared by means of a high-temperature reaction between lithium beryllium fluoride, Li 2 BeF 4 , and tricalcium phosphate, Ca 3 (PO 4 ) 2 . This material has potential application as a waste form for radioactive and toxic fluoride salts. Monitoring of the reaction progress by differential scanning calorimetry indicated that the reaction was initiated by melting of the fluoride salt and that it was fast and complete. While reactive sintering of lithium beryllium fluoride with tricalcium phosphate led to a rather porous product, melting of the reactants with subsequent solidification readily produced a substituted fluorapatite with a near-theoretical bulk density

Mechanical properties of irradiated beryllium

International Nuclear Information System (INIS)

Beeston, J.M.; Longhurst, G.R.; Wallace, R.S.

1992-01-01

Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 x 10 25 n/m 2 (E > MeV) at an irradiation temperature of 75deg C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium. (orig.)

Mechanical properties of irradiated beryllium

Energy Technology Data Exchange (ETDEWEB)

Beeston, J.M.; Longhurst, G.R.; Wallace, R.S. (EG and G Idaho, Inc., Idaho Falls, ID (United States). Idaho National Engineering Lab.); Abeln, S.P. (EG and G Rocky Flats, Inc., Golden, CO (United States))

1992-10-01

Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 x 10[sup 25] n/m[sup 2] (E > MeV) at an irradiation temperature of 75deg C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium. (orig.).

Mechanical properties of irradiated beryllium

Science.gov (United States)

Beeston, J. M.; Longhurst, G. R.; Wallace, R. S.; Abeln, S. P.

1992-10-01

Beryllium is planned for use as a neutron multiplier in the tritium breeding blanket of the International Thermonuclear Experimental Reactor (ITER). After fabricating samples of beryllium at densities varying from 80 to 100% of the theoretical density, we conducted a series of experiments to measure the effect of neutron irradiation on mechanical properties, especially strength and ductility. Samples were irradiated in the Advanced Test Reactor (ATR) to a neutron fluence of 2.6 × 10 25 n/m 2 ( E > 1 MeV) at an irradiation temperature of 75°C. These samples were subsequently compression-tested at room temperature, and the results were compared with similar tests on unirradiated specimens. We found that the irradiation increased the strength by approximately four times and reduced the ductility to approximately one fourth. Failure was generally ductile, but the 80% dense irradiated samples failed in brittle fracture with significant generation of fine particles and release of small quantities of tritium.

Investigation of the mechanism of interaction of Lithium 6 ions on Beryllium 9

International Nuclear Information System (INIS)

Coste, Mireille

1962-01-01

The objective of this research on the interaction of Lithium 6 and Beryllium 9 ions is to obtain new indications on the mode of interaction of these heavy ions, and on the configuration of target nuclei and projectile nuclei. In a first part, the author presents and describes the experimental conditions which comprise a Van de Graaff accelerator, a source, a stripper, and a target. He reports the study of α particles emitted by the reaction between the Lithium and Beryllium ions: description of the experimental installation (irradiation chamber and method), presentation and interpretation of experimental results. In the next part, he reports the study of Lithium 7 and Beryllium 10 nuclides emitted by disintegration of Beryllium 11: description of experimental conditions, variations of cross sections, variation of the cross section rate, and interpretation. The author then addresses the study of the intervention of the mode of interaction by 15 N compound nucleus in the reactions between lithium and beryllium ions: study of intensities of the different spectrum lines, measurement of the Doppler effect produced of the 479 keV line, interpretation of results. In conclusion, the author analyses the mechanism of interaction between lithium and beryllium ions, and discusses different theories: the Newns and Glendenning theories, and the Leigh theory

Encapsulation of gold nanoparticles into self-assembling protein nanoparticles

Directory of Open Access Journals (Sweden)

Yang Yongkun

2012-10-01

Full Text Available Abstract Background Gold nanoparticles are useful tools for biological applications due to their attractive physical and chemical properties. Their applications can be further expanded when they are functionalized with biological molecules. The biological molecules not only provide the interfaces for interactions between nanoparticles and biological environment, but also contribute their biological functions to the nanoparticles. Therefore, we used self-assembling protein nanoparticles (SAPNs to encapsulate gold nanoparticles. The protein nanoparticles are formed upon self-assembly of a protein chain that is composed of a pentameric coiled-coil domain at the N-terminus and trimeric coiled-coil domain at the C-terminus. The self-assembling protein nanoparticles form a central cavity of about 10 nm in size, which is ideal for the encapsulation of gold nanoparticles with similar sizes. Results We have used SAPNs to encapsulate several commercially available gold nanoparticles. The hydrodynamic size and the surface coating of gold nanoparticles are two important factors influencing successful encapsulation by the SAPNs. Gold nanoparticles with a hydrodynamic size of less than 15 nm can successfully be encapsulated. Gold nanoparticles with citrate coating appear to have stronger interactions with the proteins, which can interfere with the formation of regular protein nanoparticles. Upon encapsulation gold nanoparticles with polymer coating interfere less strongly with the ability of the SAPNs to assemble into nanoparticles. Although the central cavity of the SAPNs carries an overall charge, the electrostatic interaction appears to be less critical for the efficient encapsulation of gold nanoparticles into the protein nanoparticles. Conclusions The SAPNs can be used to encapsulate gold nanoparticles. The SAPNs can be further functionalized by engineering functional peptides or proteins to either their N- or C-termini. Therefore encapsulation of gold

In-pile thermocycling testing and post-test analysis of beryllium divertor mockups

Energy Technology Data Exchange (ETDEWEB)

Giniatulin, R.; Mazul, I. [Efremov Inst., St. Petersburg (Russian Federation); Melder, R.; Pokrovsky, A.; Sandakov, V.; Shiuchkin, A.

1998-01-01

The main damaging factors which impact the ITER divertor components are neutron irradiation, cyclic surface heat loads and hydrogen environment. One of the important questions in divertor mockups development is the reliability of beryllium/copper joints and the beryllium resistance under neutron irradiation and thermal cycling. This work presents the experiment, where neutron irradiation and thermocyclic heat loads were applied simultaneously for two beryllium/copper divertor mockups in a nuclear reactor channel to simulate divertor operational conditions. Two mockups with different beryllium grades were mounted facing each other with the tantalum heater placed between them. This device was installed in the active zone of the nuclear reactor SM-2 (Dimitrovgrad, Russia) and the tantalum block was heated by neutron irradiation up to a high temperature. The main part of the heat flux from the tantalum surface was transported to the beryllium surface through hydrogen, as a result the heat flux loaded two mockups simultaneously. The mockups were cooled by reactor water. The device was lowered to the active zone so as to obtain the heating regime and to provide cooling lifted. This experiment was performed under the following conditions: tantalum heater temperature - 1950degC; hydrogen environment -1000 Pa; surface heat flux density -3.2 MW/m{sup 2}; number of thermal cycles (lowering and lifting) -101; load time in each cycle - 200-5000 s; dwell time (no heat flux, no neutrons) - 300-2000 s; cooling water parameters: v - 1 m/s, Tin - 50degC, Pin - 5 MPa; neutron fluence -2.5 x 10{sup 20} cm{sup -2} ({approx}8 years of ITER divertor operation from the start up). The metallographic analysis was performed after experiment to investigate the beryllium and beryllium/copper joint structures, the results are presented in the paper. (author)

Comparative thermal cyclic test of different beryllium grades previously subjected to simulated disruption loads

International Nuclear Information System (INIS)

Gervash, A.; Giniyatulin, R.; Mazul, I.

1999-01-01

Considering beryllium as plasma facing armour this paper presents recent results obtained in Russia. A special process of joining beryllium to a Cu-alloy material structure is described and recent results of thermal cycling tests of such joints are presented. Summarizing the results, the authors show that a Cu-alloy heat sink structure armoured with beryllium can survive high heat fluxes (≥10 MW/m 2 ) during 1000 heating/cooling cycles without serious damage to the armour material and its joint. The principal feasibility of thermal cycling of beryllium grades and their joints directly in the core of a nuclear reactor is demonstrated and the main results of this test are presented. The paper also describes the thermal cycling of different beryllium grades having cracks initiated by previously applied high heat loads simulating plasma disruptions. (orig.)

Status of construction and assembly of Wendelstein 7-X

International Nuclear Information System (INIS)

Hartmann, D.A.

2005-01-01

Wendelstein 7-X (W7-X) is a low-shear stellarator with an optimized quasi-isodynamic configuration and five-fold symmetry that is presently under construction in Greifswald, Germany. The goal of the device is to investigate the fusion reactor capability of stellarators. Therefore the magnetic field will be generated using superconducting coils and all relevant components (10 MW ECR heating system, divertor and wall protection elements) are designed for 30 min. operation, which is equivalent to steady-state. The basic parameters of the device are: magnetic field up to 3 T on axis, major radius 5.5 m, average minor radius 0.55m. The device consists of 50 non-planar and 20 planar coils, the coil support structure, 10 plasma vessel half modules, 10 outer vessel half shells and 299 ports. Presently of the non- planar coils 38 winding packs have been produced, of which 25 have been embedded. Two of the coils have been successfully tested for their cryogenic and superconducting properties at the test site at CEA Saclay and were delivered. Of the planar coils all 20 winding packs have been produced, 5 have been embedded. 6 of the plasma vessel half modules and about 180 of the ports have been delivered. The first module of the coil support structure is being machined and will be delivered in fall 2005. The assembly of the device started last fall: diagnostic Mirnov coils were attached to the outside of the plasma vessel, sections of the super-insulation were added, the first coil was threaded onto a section of a plasma vessel half module and a second section was welded onto the first catching the threaded coil in between. Presently the further progress of assembly is slowed down by the required reworking of several coils. The inside of the plasma vessel will be fully lined by water cooled structures: divertor modules consisting of CFC elements brazed onto CuCrZr substructures for areas with convective losses up to 10 MW/m 2 and double-walled stainless steel panels for

Beryllium and lithium resource requirements for solid blanket designs for fusion reactors

International Nuclear Information System (INIS)

Powell, J.R.

1975-01-01

The lithium and beryllium requirements are analyzed for an economy of 10 6 MW(e) CTR 3 capacity using solid blanket fusion reactors. The total lithium inventory in fusion reactors is only approximately 0.2 percent of projected U. S. resources. The lithium inventory in the fusion reactors is almost entirely 6 Li, which must be extracted from natural lithium. Approximately 5 percent of natural lithium can be extracted as 6 Li. Thus the total feed of natural lithium required is approximately 20 times that actually used in fusion reactors, or approximately 4 percent of U. S. resources. Almost all of this feed is returned to the U. S. resource base after 6 Li is extracted, however. The beryllium requirements are on the order of 10 percent of projected U. S. resources. Further, the present cost of lithium and the cost of beryllium extraction could both be increased tenfold with only minor effects on CTR capital cost. Such an increase should substantially multiply the economically recoverable resources of lithium and beryllium. It is concluded that there are no lithium or beryllium resource limitations preventing large-scale implementation of solid blanket fusion reactors. (U.S.)

Biomaterials Made from Coiled-Coil Peptides.

Science.gov (United States)

Conticello, Vincent; Hughes, Spencer; Modlin, Charles

The development of biomaterials designed for specific applications is an important objective in personalized medicine. While the breadth and prominence of biomaterials have increased exponentially over the past decades, critical challenges remain to be addressed, particularly in the development of biomaterials that exhibit highly specific functions. These functional properties are often encoded within the molecular structure of the component molecules. Proteins, as a consequence of their structural specificity, represent useful substrates for the construction of functional biomaterials through rational design. This chapter provides an in-depth survey of biomaterials constructed from coiled-coils, one of the best-understood protein structural motifs. We discuss the utility of this structurally diverse and functionally tunable class of proteins for the creation of novel biomaterials. This discussion illustrates the progress that has been made in the development of coiled-coil biomaterials by showcasing studies that bridge the gap between the academic science and potential technological impact.

Technical aspects of the joint JET-ISX-B beryllium limiter experiment

International Nuclear Information System (INIS)

Edmonds, P.H.; Dietz, K.J.; Mioduszewski, P.K.; Watson, R.D.; Emerson, L.C.; Gabbard, W.A.; Goodall, D.; Simpkins, J.E.; Yarber, J.L.

1984-01-01

An experiment has been performed on the Impurity Study Experiment (ISX-B) tokamak to test beryllium as a limiter material. Beryllium is an attractive candidate for a limiter and has been proposed for use in the Joint European Torus (JET) experiment. A temperature-controlled, segmented, beryllium top-rail limiter was located inside the plasma radius described by the existing titanium limiters. An extended set of diagnostics was added for measurement of scrapeoff and limiter parameters. These included visible and infrared monitoring systems, probes, and surface analysis experiments. Tokamak experiments included parameter surveys of both ohmically heated and neutral-beam-heated plasmas and an extended fluence test of the limiter

Experimental Simulation of Beryllium Armour Damage Under ITER-like Intense Transient Plasma Loads

Energy Technology Data Exchange (ETDEWEB)

Kupriyanov, I.; Basaleev, E.; Nikolaev, G.; Kurbatova, L., E-mail: igkupr@gmail.com [A.A. Bochvar High Technology Research Institute of Inorganic Material, Moscow (Russian Federation); Podkovyrov, V.; Zhitlukhin, A. [SRC RF TRINITI, Troitsk (Russian Federation); Khimchenko, L. L. [Project Centre of ITER, Moscow (Russian Federation)

2012-09-15

Full text: Beryllium will be used as a plasma facing material in the next generation of tokamaks such as ITER. During plasma operation in ITER, the plasma facing materials and components will be suffered by different kinds of loading which may affect their surface or their joint to the heat sink. In addition to quasi-stationary loadings which are caused by the normal cycling operation, the plasma facing components and materials may also be exposed to the intense short transient loads like disruptions, ELMs. All these events may lead to beryllium surface melting, cracking, evaporation and erosion. It is expected that the erosion of beryllium under transient plasma loads such as ELMs and disruptions will mainly determine a lifetime of ITER first wall. To obtain the experimental data for the evaluation of the beryllium armor lifetime and dust production under ITER-relevant transient loads, the advanced plasma gun QSPA-Be facility has been constructed in Bochvar Institute. This paper presents recent results of the experiments with Russian beryllium of TGP-56FW ITER grade. The mock-ups of a special design armored with two beryllium targets (80 x 80 x 10 mm{sup 3}) were tested by hydrogen plasma streams (5 cm in diameter) with pulse duration of 0.5 ms and heat load of 0.5 and 1.0 MJ/m{sup 2}. Experiments were performed at RT temperature. The evolution of surface microstructure and profile, cracks morphology and mass loss/gain under erosion process on the beryllium surface exposed to up to 250 shots will be presented and discussed. (author)

The fourth international energy agency international workshop on beryllium technology for fusion

International Nuclear Information System (INIS)

Scaffidi-Argentina, F.; Longhurst, G.R.

2000-01-01

The main objective of the workshop was to support the advancement of the international development of fusion power through communication and dissemination of information on progress made in beryllium technology. This has been accomplished through presentation of original research on issues of current interest to the fusion beryllium community. The workshop was divided into ten technical sessions that addressed the following general topics: production and characterization, health and safety, forming and joining, chemical compatibility, thermal-mechanical properties, pebble bed behavior, high-heat-flux performance, irradiation effects, plasma-tritium interaction, and molten beryllium-bearing salts

The fourth international energy agency international workshop on beryllium technology for fusion

Energy Technology Data Exchange (ETDEWEB)

Scaffidi-Argentina, F.; Longhurst, G.R.

2000-05-01

The main objective of the workshop was to support the advancement of the international development of fusion power through communication and dissemination of information on progress made in beryllium technology. This has been accomplished through presentation of original research on issues of current interest to the fusion beryllium community. The workshop was divided into ten technical sessions that addressed the following general topics: production and characterization, health and safety, forming and joining, chemical compatibility, thermal-mechanical properties, pebble bed behavior, high-heat-flux performance, irradiation effects, plasma-tritium interaction, and molten beryllium-bearing salts.