WorldWideScience

Sample records for barium niobate glass

  1. Optical properties of Er{sup 3+}-doped strontium barium niobate nanocrystals obtained by thermal treatment in glass

    Energy Technology Data Exchange (ETDEWEB)

    Haro-Gonzalez, P. [Dep. of Fisica Fundamental Experimental, Electronica y Sistemas, Universidad de La Laguna Avda Astrofisico Franscisco Sanchez, 38206 La Laguna, S/C de Tenerife (Spain)], E-mail: patharo@ull.es; Lahoz, F. [Dep. of Fisica Fundamental Experimental, Electronica y Sistemas, Universidad de La Laguna Avda Astrofisico Franscisco Sanchez, 38206 La Laguna, S/C de Tenerife (Spain); Gonzalez-Platas, J. [Dep. of Fisica Fundamental II, Universidad de La Laguna, 38206 La Laguna, S/C de Tenerife (Spain); Caceres, J.M. [Dep. of Edafologia y Geologia, Universidad de La Laguna, 38206 La Laguna, S/C de Tenerife (Spain); Gonzalez-Perez, S. [Dep. of Fisica Fundamental Experimental, Electronica y Sistemas, Universidad de La Laguna Avda Astrofisico Franscisco Sanchez, 38206 La Laguna, S/C de Tenerife (Spain); Marrero-Lopez, D. [Dep. of Quimica Inorganica, Universidad de La Laguna, 38206 La Laguna, S/C de Tenerife (Spain); Capuj, N. [Dep. of Fisica Basica, Universidad de La Laguna, 38206 La Laguna, S/C de Tenerife (Spain); Martin, I.R. [Dep. of Fisica Fundamental Experimental, Electronica y Sistemas, Universidad de La Laguna Avda Astrofisico Franscisco Sanchez, 38206 La Laguna, S/C de Tenerife (Spain)

    2008-05-15

    Measurements of the optical properties of Er{sup 3+} ions in strontium barium niobate glass and glass ceramics have been carried out. The glasses have been fabricated using a melt-quenching method, and the glass ceramic samples have been obtained from the glass precursor by a thermal treatment. The ceramic samples formed by a glassy phase, and a crystalline phase contains nanocrystals of Sr{sub 1-x}Ba{sub x}Nb{sub 2}O{sub 6} (SBN) doped with Er{sup 3+} ions with a mean size of {approx}50 nm, as confirmed with XRD. Green up-conversion emission has been obtained under excitation at 800 nm, and the temporal evolution of this emission has been reported with the purpose of determining the involved up-conversion mechanism. These optical measures have confirmed that the Er{sup 3+} ions have been incorporated into the SBN matrix, after a thermal treatment, which produced an increment of the up-conversion efficiency.

  2. Macroscopic polarization and thermoluminescence of barium niobate - sodium niobate

    International Nuclear Information System (INIS)

    Gorban', I.S.; Gumenyuk, A.F.; Omel'yanenko, V.A.

    1989-01-01

    Thermoluminescence (TL) of initial and thermally treated purposely undoped crystals of barium niobate - sodium has been studied within 85-400 K. The TL intensity is found to depend on the temperature to which the sample has been heated. A conclusion is drawn that nonstationarity of the TL properties is due to slowly occuring processes of compensation of pyrocharge, which depend on the temperatural prehistory of the sample. A mechanism of the traps transformation in a strong pyrofield of high-impedance crystals is discussed

  3. Optical properties of calcium barium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Heine, Urs; Betzler, Klaus [Department of Physics, University of Osnabrueck (Germany); Burianek, Manfred; Muehlberg, Manfred [Institute of Crystallography, University of Cologne (Germany)

    2010-07-01

    We report on optical measurements on the novel tungsten bronze type calcium barium niobate. [001]-oriented transparent and colorless single crystals were grown by the Czochralski method with dimensions of 12 mm in diameter and about 80 mm in length. With its relatively high Curie temperature of about 538 K for the congruently melting composition of 28.1 mole% calcium and its high nonlinear coefficients, CBN is a promising material for future applications. Recent experiments revealed, that the application of an external electric field of several kV/cm to CBN at room temperature leads to an increasing opacity of the sample. This might be a drawback considering the future usability of CBN in optical systems. We present investigations on the transmittance behaviour of CBN under external electric fields, demonstrating the erasement of the clouding without affecting the polarization. Experiments have been performed at temperatures ranging from room temperature to approximately 480 K. When heating up the sample, its colorless appearance changes to a light yellow, which can be attributed to a shift of the band edge to longer wavelengths with increasing temperature. To further investigate the transmittance properties of CBN, measurements of the band edge under various temperatures up to the ferroelectric phase transition have been performed.

  4. Macroscopic polarization and thermoluminescence of barium niobate - sodium niobate. Makroskopicheskaya polyarizatsiya i termolyuminestsentsiya niobata bariya - natriya

    Energy Technology Data Exchange (ETDEWEB)

    Gorban' , I S; Gumenyuk, A F; Omel' yanenko, V A [Kievskij Gosudarstvennyj Univ., Kiev (Ukrainian SSR)

    1989-11-01

    Thermoluminescence (TL) of initial and thermally treated purposely undoped crystals of barium niobate - sodium has been studied within 85-400 K. The TL intensity is found to depend on the temperature to which the sample has been heated. A conclusion is drawn that nonstationarity of the TL properties is due to slowly occuring processes of compensation of pyrocharge, which depend on the temperatural prehistory of the sample. A mechanism of the traps transformation in a strong pyrofield of high-impedance crystals is discussed.

  5. Electrooptic and piezoelectric measurements in photorefractive barium titanate and strontium barium niobate

    International Nuclear Information System (INIS)

    Ducharme, S.; Feinberg, J.; Neurgaonkar, R.R.

    1987-01-01

    The authors measured the low-frequency (''unclamped'') electrooptic and piezoelectric coefficients in undoped BaTiO/sub 3/ and Sr/sub x/Ba/sub 1-x/Nb/sub 2/O/sub 6/ (chi - 0.61) crystals using interferometric techniques. The contribution of the piezoelectric effect to the Pockels measurement is discussed. For an applied ac electric field in the range 0.1-200 V/cm, the electrooptic and piezoelectric effects are linear in the magnitude of of the applied field and independent of its frequency in the range of 10 Hz-100 kHz. The unclamped electrooptic coefficients of poled BaTiO/sub 3/ single crystals are r/sub 13/ = 19.5 +- 1 pm/V and r/sub 33/ = 97 +- 7 pm/V, and for strontium barium niobate are r/sub 13/ = 47 +- 5 pm/V and r/sub 33/ = 235 +- 21 pm/V, all measured at a wavelength of 514.5 nm and at T = 23 0 C. For the barium titanate samples the measured Pockels coefficient r/sub c/ identical to r/sub 33/ - (n/sub 1//n/sub 3/)/sup 3/r/sub 13/ = 79 +- 6 pm/V in good agreement with the value r/sub c/ = 76 +- 7 pm/V computed from the above values of r/sub 13/ and r/sub 33/, where n/sub 1/ and n/sub 3/ are the ordinary and extraordinary indexes of refraction, respectively. The measured piezoelectric coefficient is d/sub 23/ = +28.7 +- 2 pm/V for barium titanate, and is d/sub 23/ = +24.6 +- 2 pm/V for strontium barium niobate. They also measured the photoreflective coupling of two optical beams in the crystals, and they show that the dependence of the coupling strength on beam polarization is in fair agreement with the measured values of the Pockels coefficients

  6. Rheological properties of potassium barium borate glasses

    NARCIS (Netherlands)

    Szwejda, K.A.; Vogel, D.L.; Stevels, J.M.

    1973-01-01

    Several series of potassium barium borate glasses have been investigated as to their rheological properties. It has been found, that all these glasses show deviations from ‘Newtonian’ behaviour below temperatures corresponding to viscosities of 1010 poises. The activation energies of viscous flow

  7. Ultrashort pulse chirp measurement via transverse second-harmonic generation in strontium barium niobate crystal

    Energy Technology Data Exchange (ETDEWEB)

    Trull, J.; Wang, B.; Parra, A.; Vilaseca, R.; Cojocaru, C. [Departament de Física i Enginyeria Nuclear, Universitat Politècnica Catalunya, Terrassa 08222 (Spain); Sola, I. [Grupo de Investigación en Óptica Extrema (GIOE), Departamento de Física Aplicada, Universidad de Salamanca, Plaza de la Merced s/n, 37008 Salamanca (Spain); Krolikowski, W. [Laser Physics Centre, Research School of Physics and Engineering, Australian National University, Canberra ACT 0200 (Australia); Science Program, Texas A and M University at Qatar, Doha (Qatar); Sheng, Y. [Laser Physics Centre, Research School of Physics and Engineering, Australian National University, Canberra ACT 0200 (Australia)

    2015-06-01

    Pulse compression in dispersive strontium barium niobate crystal with a random size and distribution of the anti-parallel orientated nonlinear domains is observed via transverse second harmonic generation. The dependence of the transverse width of the second harmonic trace along the propagation direction allows for the determination of the initial chirp and duration of pulses in the femtosecond regime. This technique permits a real-time analysis of the pulse evolution and facilitates fast in-situ correction of pulse chirp acquired in the propagation through an optical system.

  8. Ultrashort pulse chirp measurement via transverse second-harmonic generation in strontium barium niobate crystal

    International Nuclear Information System (INIS)

    Trull, J.; Wang, B.; Parra, A.; Vilaseca, R.; Cojocaru, C.; Sola, I.; Krolikowski, W.; Sheng, Y.

    2015-01-01

    Pulse compression in dispersive strontium barium niobate crystal with a random size and distribution of the anti-parallel orientated nonlinear domains is observed via transverse second harmonic generation. The dependence of the transverse width of the second harmonic trace along the propagation direction allows for the determination of the initial chirp and duration of pulses in the femtosecond regime. This technique permits a real-time analysis of the pulse evolution and facilitates fast in-situ correction of pulse chirp acquired in the propagation through an optical system

  9. Conical light scattering in strontium barium niobate crystals related to an intrinsic composition inhomogeneity

    International Nuclear Information System (INIS)

    Bastwoeste, K; Sander, U; Imlau, M

    2007-01-01

    Conical light scattering is uncovered in poly- and mono-domain, nominally pure and Eu-doped strontium barium niobate (SBN) crystals over a wide temperature regime. The appearance of two scattering cones, a scattering line and a corona is observed and can be explained comprehensively within the Ewald sphere concept. Photorefraction, scattering from domain boundaries or from growth striations can be excluded from explaining the origin of the scattering. It is shown that the temperature-persistent scattering process is related to a growth-induced seeding rod, i.e. a composition inhomogeneity primarily localized at the centre of the SBN sample. The rod is directed parallel to the c axis and yields a refractive-index inhomogeneity with spatial frequencies on the micro-scale

  10. Luminescence life time and time-resolved spectroscopy of Cr3+ ions in strontium barium niobate

    International Nuclear Information System (INIS)

    Han, T.P.J.; Jaque, F.; Jaque, D.; Garcia-Sole, J.; Ivleva, L.

    2006-01-01

    This paper reports on the photo-luminescence spectroscopic results of congruent strontium-barium-niobate (SBN) crystals doped with Cr 2 O, at cryogenic temperature (20 K). The experimental results reveal the need of re-assignment of the Cr 3+ ions defect centres in this material. For first time, a broad emission band in the near infrared region centred at ca. 950 nm is reported. This emission band has micro-seconds decaytime constant and a band-width full-width at half-maximum (FWHM) larger than 1700 cm -1 and has been ascribed to the vibronically assisted 4 T 2 →4 A 2 transition. A much narrower emission band centred at ca. 764 nm with milli-seconds decaytime constant and a FWHM band-width of ca. 170 cm -1 is correlated to the 2 E →4 A 2 radiative transition (R-line)

  11. Barium-borate-flyash glasses: As radiation shielding materials

    International Nuclear Information System (INIS)

    Singh, Sukhpal; Kumar, Ashok; Singh, Devinder; Thind, Kulwant Singh; Mudahar, Gurmel S.

    2008-01-01

    The attenuation coefficients of barium-borate-flyash glasses have been measured for γ-ray photon energies of 356, 662, 1173 and 1332 keV using narrow beam transmission geometry. The photon beam was highly collimated and overall scatter acceptance angle was less than 3 o . Our results have an uncertainty of less than 3%. These coefficients were then used to obtain the values of mean free path (mfp), effective atomic number and electron density. Good agreements have been observed between experimental and theoretical values of these parameters. From the studies of the obtained results it is reported here that from the shielding point of view the barium-borate-flyash glasses are better shields to γ-radiations in comparison to the standard radiation shielding concretes and also to the ordinary barium-borate glasses

  12. Crystallization of Reduced Strontium and Barium Niobate Perovskites from Borate Fluxes.

    NARCIS (Netherlands)

    Hessen, B.; Sunshine, S.A.; Siegrist, T.; Jimenez, R.

    1991-01-01

    Single crystals of three AxNbO3 (A = Sr, Ba) reduced niobate cubic perovskites have been obtained by recrystallization of reduced ternary ceramic precursors from borate fluxes under high-vacuum. Product formation could be influenced by variation of the alkaline-earth metal oxide content of the flux,

  13. Structural and optical study of tellurite-barium glasses

    Science.gov (United States)

    Grelowska, I.; Reben, M.; Burtan, B.; Sitarz, M.; Cisowski, J.; Yousef, El Sayed; Knapik, A.; Dudek, M.

    2016-12-01

    The goal of this work was to determine the effect of barium oxide on the structural, thermal and optical properties of the TeO2-BaO-Na2O (TBN) and TeO2-BaO-WO3 (TBW) glass systems. Raman spectra allow relating the glass structure and vibration properties (i.e. vibrational frequencies and Raman intensities) with the glass composition. Raman spectra show the presence of TeO4 and TeO3+1/TeO3 units that conform with the glass matrix. Differential thermal analysis DTA, XRD measurements have been considered in term of BaO addition. The spectral dependence of ellipsometric angles of the tellurite-barium glass has been studied. The optical measurements were conducted on Woollam M2000 spectroscopic ellipsometer in spectral range of 190-1700 nm. The reflectance and transmittance measurements have been done on spectrophotometer Perkin Elmer, Lambda 900 in the range of 200-2500 nm (UV-VIS-NIR). From the transmittance spectrum, the energy gap was determined.

  14. Synthesis and characterization of barium fluoride substituted zinc tellurite glasses

    Science.gov (United States)

    Aishwarya, K.; Vinitha, G.; Varma, G. Sreevidya; Asokan, S.; Manikandan, N.

    2017-12-01

    Glasses in the TeO2-ZnO-BaF2 system were prepared by standard melt quenching technique and were characterized for their thermal, optical and structural properties. Samples were found to show good thermal stability with values ranging above 100 °C for all the compositions. Optical bandgap and refractive index values were calculated from linear optical measurements using UV-Vis spectroscopy. Infrared spectra showed the presence of hydroxyl groups in the glasses indicating that the effect of fluorine was negligible in removing the hydroxyl impurities for the experimental conditions and compositions used. Raman measurements showed the modification occurring in the glass network due to addition of barium fluoride in terms of increase in the formation of non-bridging oxygen atoms compared to strong Te-O-Te linkages in the glass matrix.

  15. Phase decomposition in niobate glasses and the electrooptical effect in materials based on them

    Energy Technology Data Exchange (ETDEWEB)

    Alekseeva, I.P.; Karapetyan, G.O.; Korolov, Y.G.; Maksimov, L.V.

    1986-10-01

    This paper studies the effect of the composition and heat treatment on the dielectric, electrooptical, and structural-physical proprties of niobium-containing glasses. The appearance and intensification of fluctuations of the niobium concentration accompanying an increase in the niobium content in the samples is characteristic for glasses in the system Na/sub 2/O-K/sub 2/O-Nb/sub 2/O/sub 5/-SiO/sub 2/. The presence of insignificant quantities of NaNbO/sub 3/ microcrystals in niobate glasses gives rise to a significant growth of the dielectric constant (by a factor of 508) and the appearance of a quadratic electrooptical effect.

  16. Synthesis and characterization of Ca{sup 2+} substituted barium niobate nanopaticles for photocatalytic and luminescence applications

    Energy Technology Data Exchange (ETDEWEB)

    Dudhe, C.M. [Department of Physics, Government Institute of science, Nagpur 440001 (India); Nagdeote, S.B. [Department of Physics, Amolakchand Mahavidhyalaya, Yavatmal 445001 (India); Palikundwar, U.A., E-mail: chandraguptadudhe@gmail.com [Department of Physics, R. T. M. Nagpur University, Nagpur 440033 (India)

    2016-09-15

    Highlights: • Nanoparticles of Ca{sup 2+} (30 mol%) substituted BaNb{sub 2}O{sub 6} were synthesized. • Ca{sup 2+} ions occupy newer 8d Wyckoff positions rather than 4c. • Self-activated photoluminescence was observed. • Excellent H{sub 2} generation tendency from pure water under UV light was also observed. - Abstract: Ca{sup 2+} substituted barium niobate i.e. Ca{sub x}Ba{sub 1-x}Nb{sub 2}O{sub 6} (x = 0.3) compound in nanoparticles form was synthesized by a simple co-precipitation method for the first time and its structural characterization has been done by using powder X-ray diffraction data. Other characterizations were done by using transmission electron microscopy, energy dispersive X-ray spectroscopy, Fourier transform infrared spectroscopy and ultraviolet-visible spectroscopy. It was found that the Ca{sub x}Ba{sub 1-x}Nb{sub 2}O{sub 6} (x = 0.3) compound stabilizes in the orthorhombic phase (Pbcn space group) with the lattice parameters a = 14.984 Å, b = 5.761 Å and c = 5.216 Å. A representative TEM image shows the irregular sphere like morphology of the synthesized particles with the size ranging from 70 to 120 nm. The optical band gap energy was found to be 3.74 eV. It was observed that the synthesized nanoparticles exhibit excellent H{sub 2} evolution tendency and self–activated photoluminescence under the excitation of UV light. These activities were assigned to the nanocrystalline nature of the synthesized material.

  17. Barium oxide, calcium oxide, magnesia, and alkali oxide free glass

    Science.gov (United States)

    Lu, Peizhen Kathy; Mahapatra, Manoj Kumar

    2013-09-24

    A glass composition consisting essentially of about 10-45 mole percent of SrO; about 35-75 mole percent SiO.sub.2; one or more compounds from the group of compounds consisting of La.sub.2O.sub.3, Al.sub.2O.sub.3, B.sub.2O.sub.3, and Ni; the La.sub.2O.sub.3 less than about 20 mole percent; the Al.sub.2O.sub.3 less than about 25 mole percent; the B.sub.2O.sub.3 less than about 15 mole percent; and the Ni less than about 5 mole percent. Preferably, the glass is substantially free of barium oxide, calcium oxide, magnesia, and alkali oxide. Preferably, the glass is used as a seal in a solid oxide fuel/electrolyzer cell (SOFC) stack. The SOFC stack comprises a plurality of SOFCs connected by one or more interconnect and manifold materials and sealed by the glass. Preferably, each SOFC comprises an anode, a cathode, and a solid electrolyte.

  18. Influence of heat treatment on structure and some physical properties of lithium boro-niobate glass

    Science.gov (United States)

    Kashif, I.; Sakr, E. M.; Soliman, A. A.; Ratep, A.

    2012-08-01

    The glass composition (90 mol% Li2B4O7-10 mol% Nb2O5) was prepared by the melt quenching technique. The quenched sample was heat treated at 480°C, 545°C and 630°C for 5 h and heat treated at 780°C with different time. The times were 5, 10, 15, 20, 28, and 36 h. The glass and glass ceramics were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and dc conductivity as a function of temperature. Lithium niobate (LiNbO3) and lithium diborate (Li2B4O7) were the main phases in glass ceramic addition to traces from LiNb3O8. Crystallite size of the main phases determined from the X-ray diffraction peaks are in the range <100 nm. The fraction of crystalline (LiNbO3) phase increases with increase the heat treatment temperature and time. The relation between physical properties and structure were studied.

  19. Glass transition and crystallization kinetics of a barium borosilicate glass by a non-isothermal method

    International Nuclear Information System (INIS)

    Lopes, Andreia A. S.; Soares, Roque S.; Lima, Maria M. A.; Monteiro, Regina C. C.

    2014-01-01

    The glass transition and crystallization kinetics of a glass with a molar composition 60BaO-30B 2 O 3 -10SiO 2 were investigated by differential scanning calorimetry (DSC) under non-isothermal conditions. DSC curves exhibited an endothermic peak associated with the glass transition and two partially overlapped exothermic peaks associated with the crystallization of the glass. The dependence of the glass transition temperature (T g ) and of the maximum crystallization temperature (T p ) on the heating rate was used to determine the activation energy associated with the glass transition (E g ), the activation energy for crystallization (E c ), and the Avrami exponent (n). X-ray diffraction (XRD) revealed that barium borate (β-BaB 2 O 4 ) was the first crystalline phase to be formed followed by the formation of barium silicate (Ba 5 Si 8 O 21 ). The variations of activation energy for crystallization and of Avrami exponent with the fraction of crystallization (χ) were also examined. When the crystallization fraction (χ) increased from 0.1 to 0.9, the value of local activation energy (E c (χ)) decreased from 554 to 458 kJ/mol for the first exothermic peak and from 1104 to 831 kJ/mol for the second exothermic peak. The value determined for the Avrami exponent was near 2 indicating a similar one-dimensional crystallization mechanism for both crystalline phases. This was confirmed by the morphological studies performed by scanning electron microscopy (SEM) on glass samples heat-treated at the first and at the second crystallization temperatures

  20. Influence of barium substitution on bioactivity, thermal and physico-mechanical properties of bioactive glass

    Energy Technology Data Exchange (ETDEWEB)

    Arepalli, Sampath Kumar, E-mail: askumar.rs.cer11@iitbhu.ac.in; Tripathi, Himanshu; Vyas, Vikash Kumar; Jain, Shubham; Suman, Shyam Kumar; Pyare, Ram; Singh, S.P., E-mail: spsinghceram@gmail.com

    2015-04-01

    Barium with low concentration in the glasses acts as a muscle stimulant and is found in human teeth. We have made a primary study by substituting barium in the bioactive glass. The chemical composition containing (46.1 − X) SiO{sub 2−}–24.3 Na{sub 2}O–26.9 CaO–2.6 P{sub 2}O{sub 5}, where X = 0, 0.4, 0.8, 1.2 and 1.6 mol% of BaO was chosen and melted in an electric furnace at 1400 ± 5 °C. The glasses were characterized to determine their use in biomedical applications. The nucleation and crystallization regimes were determined by DTA and the controlled crystallization was carried out by suitable heat treatment. The crystalline phase formed was identified by using XRD technique. Bioactivity of these glasses was assessed by immersion in simulated body fluid (SBF) for various time periods. The formation of hydroxy carbonate apatite (HCA) layer was identified by FTIR spectrometry, scanning electron microscope (SEM) and XRD which showed the presence of HCA as the main phase in all tested bioactive glass samples. Flexural strength and densities of bioactive glasses have been measured and found to increase with increasing the barium content. The human blood compatibility of the samples was evaluated and found to be pertinent. - Highlights: • In vitro bioactivity of soda-lime–baria-phospho-silicate glass was investigated. • HCA formed on surface of glasses was confirmed by XRD, SEM and FTIR spectrometry. • Mechanical properties of glasses were found to increase with barium addition. • Hemolysis showed that 1.2 mol% BaO bioactive glass exhibited better biocompatibility. • Barium substituted bioactive glasses can be used as bone implants.

  1. CuO and Ag2O effect on electrical properties of barium vanadate glasses

    International Nuclear Information System (INIS)

    Bogomolova, L.D.; Glasova, M.N.; Kalygina, V.M.; Spasibkina, S.N.; Khorikov, A.A.

    1987-01-01

    Effect of CuO on barium vanadate glass (BVG) conductivity on direct and alternating currents in the frequency range (10 2 -10 4 )Hz has been studied. Effect of Ag 2 O has been also studied for comparison, as Ag and Cu have idendical structure of external electron shells (d 10 , S 1 ). CuO introduction to binary barium vanadate glasses as a modificator results in the conductivity improvement on direct and alternating currents conditioned with reducing activation energy of small radius polaron jump, apparently, owing to exchange (ferromagnetic) interaction between V(IV) and Cu(II). Jump activation energy in barium vanadate glasses with Ag 2 O increases and conductivity drops due to the distance increase between vanadium atoms

  2. Barium halide nanocrystals in fluorozirconate based glass ceramics for scintillation application

    International Nuclear Information System (INIS)

    Selling, J.

    2007-01-01

    Europium (Eu)-activated barium halide nanocrystals in fluorozirconate based glass ceramics represent a promising class of Xray scintillators. The scintillation in these glass ceramics is mainly caused by the emission of divalent Eu incorporated in hexagonal BaCl 2 nanocrystals which are formed in the glass matrix upon appropriate annealing. Experiments with cerium (Ce)-activated fluorozironate glass ceramics showed that Ce is an interesting alternative. In order to get a better understanding of the scintillation mechanism in Eu- or Ce-activated barium halide nanocrystals, an investigation of the processes in the corresponding bulk material is essential. The objective of this thesis is the investigation of undoped, Eu-, and Ce-doped barium halides by X-ray excited luminescence (XL), pulse height, and scintillation decay spectra. That will help to figure out which of these crystals has the most promising scintillation properties and would be the best nanoparticles for the glass ceramics. Furthermore, alternative dopants like samarium (Sm) and manganese (Mn) were also investigated. Besides the above-mentioned optical investigation electron paramagnetic resonance (EPR) and Moessbauer measurements were carried out in order to complete the picture of Eu-doped barium halides. The EPR data of Eu-doped BaI 2 is anticipated to yield more information about the crystal field and crystal structure that will help to understand the charge carrier process during the scintillation process. The main focus of the Moessbauer investigations was set on the Eu-doped fluorochlorozirconate glass ceramics. The results of this investigation should help to improve the glass ceramics. The Eu 2+ /Eu 3+ ratio in the glass ceramics should be determined and optimize favor of the Eu 2+ . We also want to distinguish between Eu 2+ in the glass matrix and Eu 2+ in the nanocrystals. For a better understanding of Moessbauer spectroscopy on Eu also measurements on Eu in a CaF 2 host lattice were carried

  3. Influence of barium substitution on bioactivity, thermal and physico-mechanical properties of bioactive glass.

    Science.gov (United States)

    Arepalli, Sampath Kumar; Tripathi, Himanshu; Vyas, Vikash Kumar; Jain, Shubham; Suman, Shyam Kumar; Pyare, Ram; Singh, S P

    2015-04-01

    Barium with low concentration in the glasses acts as a muscle stimulant and is found in human teeth. We have made a primary study by substituting barium in the bioactive glass. The chemical composition containing (46.1-X) SiO2--24.3 Na2O-26.9 CaO-2.6 P2O5, where X=0, 0.4, 0.8, 1.2 and 1.6mol% of BaO was chosen and melted in an electric furnace at 1400±5°C. The glasses were characterized to determine their use in biomedical applications. The nucleation and crystallization regimes were determined by DTA and the controlled crystallization was carried out by suitable heat treatment. The crystalline phase formed was identified by using XRD technique. Bioactivity of these glasses was assessed by immersion in simulated body fluid (SBF) for various time periods. The formation of hydroxy carbonate apatite (HCA) layer was identified by FTIR spectrometry, scanning electron microscope (SEM) and XRD which showed the presence of HCA as the main phase in all tested bioactive glass samples. Flexural strength and densities of bioactive glasses have been measured and found to increase with increasing the barium content. The human blood compatibility of the samples was evaluated and found to be pertinent. Copyright © 2015 Elsevier B.V. All rights reserved.

  4. Enhancement of Dielectric Breakdown Strength and Energy Conversion Efficiency of Niobate Glass-Ceramics by Sc2O3 Doping

    Science.gov (United States)

    Xiao, Shi; Xiu, Shaomei; Yang, Ke; Shen, Bo; Zhai, Jiwei

    2018-01-01

    Niobate glass-ceramics K2O-SrO-Nb2O5-B2O3-Al2O3-SiO2 (KSN-BAS) doped with different amounts of Sc2O3 have been prepared through a melt quenching/controlled crystallization method, and the influence of the Sc2O3 content on their phase composition, microstructure, dielectric performance, and charge-discharge properties investigated. X-ray powder diffraction results showed that the peak positions of the KSr2Nb5O15 phase shifted to higher angle and the glass-ceramic microstructures were significantly improved by Sc2O3 addition. Based on these results, 0.5 mol.% Sc2O3 doping was found to achieve remarkable enhancement in energy storage density, which reached 9.63 ± 0.39 J/cm3 at dielectric breakdown strength of 1450.38 ± 29.01 kV/cm with high conversion efficiency of ˜ 92.1%. For pulsed power applications, discharge speed of 17 ns and power density of 0.48 MW/cm3 were obtained in the glass-ceramic with 0.5 mol.% Sc2O3. These results could provide a new design strategy for high-performance dielectric capacitors.

  5. Barium halide nanocrystals in fluorozirconate based glass ceramics for scintillation application

    Energy Technology Data Exchange (ETDEWEB)

    Selling, J.

    2007-07-01

    Europium (Eu)-activated barium halide nanocrystals in fluorozirconate based glass ceramics represent a promising class of Xray scintillators. The scintillation in these glass ceramics is mainly caused by the emission of divalent Eu incorporated in hexagonal BaCl{sub 2} nanocrystals which are formed in the glass matrix upon appropriate annealing. Experiments with cerium (Ce)-activated fluorozironate glass ceramics showed that Ce is an interesting alternative. In order to get a better understanding of the scintillation mechanism in Eu- or Ce-activated barium halide nanocrystals, an investigation of the processes in the corresponding bulk material is essential. The objective of this thesis is the investigation of undoped, Eu-, and Ce-doped barium halides by X-ray excited luminescence (XL), pulse height, and scintillation decay spectra. That will help to figure out which of these crystals has the most promising scintillation properties and would be the best nanoparticles for the glass ceramics. Furthermore, alternative dopants like samarium (Sm) and manganese (Mn) were also investigated. Besides the above-mentioned optical investigation electron paramagnetic resonance (EPR) and Moessbauer measurements were carried out in order to complete the picture of Eu-doped barium halides. The EPR data of Eu-doped BaI{sub 2} is anticipated to yield more information about the crystal field and crystal structure that will help to understand the charge carrier process during the scintillation process. The main focus of the Moessbauer investigations was set on the Eu-doped fluorochlorozirconate glass ceramics. The results of this investigation should help to improve the glass ceramics. The Eu{sup 2+}/Eu{sup 3+} ratio in the glass ceramics should be determined and optimize favor of the Eu{sup 2+}. We also want to distinguish between Eu{sup 2+} in the glass matrix and Eu{sup 2+} in the nanocrystals. For a better understanding of Moessbauer spectroscopy on Eu also measurements on Eu in a

  6. Effect of ThO2 concentration on thermo-physical properties of barium borosilicate glass

    International Nuclear Information System (INIS)

    Mishra, R.K.; Munshi, A.K.; Kaushik, C.P.; Raj, Kanwar; Shobha, M.; Srikhande, V.K.; Kothiyal, G.P.; Tyagi, A.K.

    2006-01-01

    An advanced heavy water reactor is being developed at Bhabha Atomic Research Centre (BARC) India with an aim of utilizing thorium for power generation. The high level radioactive liquid waste (HLW) generated from reprocessing of Th-based spent fuel is expected to contain Th as one of the main constituents other than fission products, corrosion products, actinides and added chemicals. Barium borosilicate (BBS) glass is being used for vitrification of the HLW generated at the reprocessing plant at BARC, Trombay, Mumbai

  7. Chemical compositions and lead isotope ratios of ancient lead-barium glasses found in Japan

    International Nuclear Information System (INIS)

    Yamasaki, Kazuo.

    1991-01-01

    Six lead-barium glasses found in the archaeological sites of the Yayoi period in the northern part of Kyushu, Japan were chemically analysed and their lead isotope ratios were determined. These data agreed with those of the glasses of the Pre-Han period found in China, suggesting the presence of possible trade between China in the Pre-Han Period (ca. fourth-third centuries B.C.) and Japan in the earlier Yayoi period (ca. first century B.C.). (author)

  8. Gamma ray interaction with vanadyl ions in barium metaphosphate glasses; spectroscopic and ESR studies

    Science.gov (United States)

    Abdelghany, A. M.; ElBatal, H. A.; EzzElDin, F. M.

    2017-11-01

    Optical, FTIR, ESR investigations of prepared undoped barium metaphosphate glass and other samples with the same basic composition containing varying V2O5 contents (0.5, 1, 2, 3%) were carried out before and after gamma irradiation. The undoped glass shows a strong UV optical absorption which is correlated with unavoidable contaminated trace iron impurities. The V2O5-doped samples reveal two additional strong broad visible bands centered at 450 and 680 nm. Such extra peculiar and strong two broad visible bands are related to both tetravalent and trivalent vanadium ions in measurable percent due to the reducing behavior of barium phosphate host glass. Gamma irradiation on the undoped glass results in the generation of collective induced UV and visible bands which are originating from positive hole and electron centers. Glasses containing V2O5 reveal upon gamma irradiation induced defects in the UV as the undoped sample together with distinct splitting within the first broad visible band while the second broad band remains unchanged. This behavior is related to limited photoionization upon the addition of V2O5 indicating specific shielding effect of the vanadium ions towards gamma irradiation. It was noticed that irradiation causes no distinct variations in the FTIR spectra due to the presence of 50% of heavy metal oxide (BaO) and some shielding effect of vanadium ions.

  9. Optical and physical properties of sodium lead barium borate glasses doped with praseodymium ion

    Science.gov (United States)

    Lenkennavar, Susheela K.; Madhu, A.; Eraiah, B.; Kokila, M. K.

    2018-05-01

    Praseodymium doped sodium lead barium borate glasses have been prepared using single step melt quenching technique. The XRD spectrum confirms amorphous nature of glasses. The optical absorbance studies were carried out on these glasses using PekinElemer Lambda-35 Uv-Vis spectrometer in the range of 200 -1100 nm. The optical direct band gap energies were found to be in the range of 3.62 eV to 3.69 eV and indirect band gap energies were found to be in the range of 3.57 eV to 3.62eV. The refractive indices were measured by using Abbe refractometer the values are in the range of 1.620 to 1.625.

  10. White light emission and color tunability of dysprosium doped barium silicate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Mishra, Lokesh; Sharma, Anchal; Vishwakarma, Amit K.; Jha, Kaushal [Department of Applied Physics, Delhi Technological University, Delhi 110042 (India); Jayasimhadri, M., E-mail: jayaphysics@yahoo.com [Department of Applied Physics, Delhi Technological University, Delhi 110042 (India); Ratnam, B.V.; Jang, Kiwan [Department of Physics, Changwon National University, Changwon 641-77 (Korea, Republic of); Rao, A.S.; Sinha, R.K. [Department of Applied Physics, Delhi Technological University, Delhi 110042 (India)

    2016-01-15

    The present work elucidates the synthesis of Dy{sup 3+} doped barium silicate glasses, along with the subsequent studies performed to evaluate its viability in solid state lighting applications. The synthesized photonic glasses were investigated via X-Ray Diffraction, Scanning Electron Microscopy and Fourier Transform Infrared Spectroscopy. The photoluminescence properties were examined under ultraviolet (UV)/near UV (NUV) excitation. Photoluminescence spectrum exhibited characteristic emission bands at λ{sub em}=483 nm (blue) and λ{sub em}=576 nm (yellow) which are ascribed to the {sup 4}F{sub 9/2}→{sup 6}H{sub 15/2} and {sup 4}F{sub 9/2}→{sup 6}H{sub 13/2} transitions of Dy{sup 3+} ion, respectively. The chromaticity coordinates under excitation of λ{sub ex}=348 nm are (0.31, 0.34), which lies in the white region of CIE 1931 chromaticity diagram and are in excellent proximity with the standard equal energy white illuminant (0.333, 0.333). The calculated correlated color temperature and the yellow to blue (Y/B) ratio are found to be 6602 K and 1.12, respectively for the optimized sample. The synthesized photonic glass also offered the possibility of tuning the color as exemplified through the variation in CIE coordinates, correlated color temperature and the Y/B ratio. The results confirm the possibility of color tunability from the proposed glass and may be useful for various photonic device applications. - Highlights: • Successfully synthesized Dy{sup 3+} doped barium silicate glasses. • Structural properties thoroughly discussed by using XRD and FT-IR. • Photoluminescence and colorimetry properties have been investigated. • Y/B ratio and the reason for color tunability have been successfully explained. • CIE coordinates of Dy{sup 3+}:BBS glass confirm its suitability for w-LEDs.

  11. Nanostructured sodium lithium niobate and lithium niobium tantalate solid solutions obtained by controlled crystallization of glass

    International Nuclear Information System (INIS)

    Radonjic, L.; Todorovic, M.; Miladinovic, J.

    2005-01-01

    Transparent, nanostructured glass ceramics based on ferroelectric solid solutions of the type Na 1-x Li x NbO 3 (in very narrow composition regions for x = 0.12 and 0.93) and LiNb 1-y Ta y O 3 (y = 0.5 unlimited solid solubility), can be obtained by controlled crystallization of glass. The parent glass samples were prepared by conventional melt-quenching technique. Heat-treatment of the parent glasses was performed at the various temperatures, for the same time. The glass structure evolution during the controlled crystallization was examined by FT-IR spectroscopy analysis. Crystalline phases were identified by X-ray diffraction analysis and SEM was used for microstructure characterization. Densities of the crystallized glasses were measured by Archimedean principle. The capacitance and dielectric loss tangent were measured at a frequency of 1 kHz, at the room temperature. It was found that in the all investigated systems crystallize solid solutions Na 1-x Li x NbO 3 and LiNb 1-y Ta y O 3 in the glassy matrix, have crystal size on nanoscale (less than 100 nm), which is one of requirements to get a transparent glass ceramic that could be a good ferroelectric material regarding to the measured properties

  12. Structural and luminescence behavior of Er(3+) ions doped Barium tellurofluoroborate glasses.

    Science.gov (United States)

    Annapoorani, K; Maheshvaran, K; Arunkumar, S; Suriya Murthy, N; Marimuthu, K

    2015-01-25

    Er(3+) doped Barium tellurofluoroborate glasses (BTFBxE) with the chemical composition (30-x)TeO2+30B2O3+20BaO+20BaF+xEr2O3 (where x=0.01, 0.05, 0.1, 0.5, 1.0 and 2.0 in wt%) were prepared following the melt quenching technique. The different vibrational modes of borates and tellurites in the prepared glasses were explored through FTIR and Raman spectra. The optical absorption spectra have been used to determine the ionic/covalent nature of the metal-ligand bond in the prepared glasses with the help of Nephelauxetic ratio (β) and bonding parameter (δ) studies. The optical band gap of direct and indirect allowed transitions were determined from Tauc's plot and the variations of band gap energy with structural arrangements were discussed. The Urbach energy values were determined and the relatively lower values of the Urbach's energy reveal the minimal degree of disorderness in the prepared glasses. The oscillator strengths (fexp and fcal) and Judd-Ofelt (JO) intensity parameters (Ω2, Ω4 and Ω6) were calculated with the application of JO theory and the trends of the JO intensity parameters are found to be Ω2>Ω6>Ω4 for all the prepared glasses with a minimum variation in Ω2 intensity parameter values. A bright green emission was observed from the (2)H11/2+(4)S3/2→ (4)I15/2 transition and the radiative properties such as transition probability (A), stimulated emission cross-section (σP(E)), branching ratio (βr) and radiative lifetime (τ) were calculated using the JO parameters. The suitability of the prepared glasses for the fabrication of photonic devices were also discussed and reported in the present work. Copyright © 2014 Elsevier B.V. All rights reserved.

  13. Barium borosilicate glass - a potential matrix for immobilization of sulfate bearing high-level radioactive liquid waste

    International Nuclear Information System (INIS)

    Kaushik, C.P.; Mishra, R.K.; Sengupta, P.; Kumar, Amar; Das, D.; Kale, G.B.; Raj, Kanwar

    2006-01-01

    Borosilicate glass formulations adopted worldwide for immobilization of high-level radioactive liquid waste (HLW) is not suitable for sulphate bearing HLW, because of its low solubility in such glass. A suitable glass matrix based on barium borosilicate has been developed for immobilization of sulphate bearing HLW. Various compositions based on different glass formulations were made to examine compatibility with waste oxide with around 10 wt% sulfate content. The vitrified waste product obtained from barium borosilicate glass matrix was extensively evaluated for its characteristic properties like homogeneity, chemical durability, glass transition temperature, thermal conductivity, impact strength, etc. using appropriate techniques. Process parameters like melt viscosity and pour temperature were also determined. It is found that SB-44 glass composition (SiO 2 : 30.5 wt%, B 2 O 3 : 20.0 wt%, Na 2 O: 9.5 wt% and BaO: 19.0 wt%) can be safely loaded with 21 wt% waste oxide without any phase separation. The other product qualities of SB-44 waste glass are also found to be on a par with internationally adopted waste glass matrices. This formulation has been successfully implemented in plant scale

  14. Effect of 3d-transition metal doping on the shielding behavior of barium borate glasses: a spectroscopic study.

    Science.gov (United States)

    ElBatal, H A; Abdelghany, A M; Ghoneim, N A; ElBatal, F H

    2014-12-10

    UV-visible and FT infrared spectra were measured for prepared samples before and after gamma irradiation. Base undoped barium borate glass of the basic composition (BaO 40%-B2O3 60mol.%) reveals strong charge transfer UV absorption bands which are related to unavoidable trace iron impurities (Fe(3+)) within the chemical raw materials. 3d transition metal (TM)-doped glasses exhibit extra characteristic absorption bands due to each TM in its specific valence or coordinate state. The optical spectra show that TM ions favor generally the presence in the high valence or tetrahedral coordination state in barium borate host glass. Infrared absorption bands of all prepared glasses reveal the appearance of both triangular BO3 units and tetrahedral BO4 units within their characteristic vibrational modes and the TM-ions cause minor effects because of the low doping level introduced (0.2%). Gamma irradiation of the undoped barium borate glass increases the intensity of the UV absorption together with the generation of an induced broad visible band at about 580nm. These changes are correlated with suggested photochemical reactions of trace iron impurities together with the generation of positive hole center (BHC or OHC) within the visible region through generated electrons and positive holes during the irradiation process. Copyright © 2014 Elsevier B.V. All rights reserved.

  15. Optical properties of Nd3+ doped barium lithium fluoroborate glasses for near-infrared (NIR) emission

    Science.gov (United States)

    Mariselvam, K.; Arun Kumar, R.; Suresh, K.

    2018-04-01

    The neodymium doped barium lithium fluoroborate (Nd3+: BLFB) glasses with the chemical composition (70-x) H3BO3 - 10 Li2CO3 - 10 BaCO3- 5 CaF2-5 ZnO - x Nd2O3 (where x = 0.05, 0.1, 0.25, 0.5, 1, 2 in wt %) have been prepared by the conventional melt quenching technique and characterised through optical absorption, near infrared emission and decay-time measurements. The x-ray diffraction studies confirm the amorphous nature of the prepared glasses. The optical absorption spectra and emission spectra were recorded in the wavelength ranges of 190-1100 nm. The optical band gap (Eg) and Urbach energy (ΔE) values were calculated from the absorption spectra. The Judd-Ofelt intensity parameters were determined from the systematic analysis of the absorption spectrum of neodymium ions in the prepared glasses. The emission spectra exhibited three prominent peaks at 874, 1057, 1331 nm corresponding to the 4F3/2 → 4I9/2, 11/2, 13/2 transitions levels respectively in the near infrared region. The emission intensity of the 4F3/2 → 4I11/2 transition increases with the increase in neodymium concentration up to 0.5 wt% and the concentration quenching mechanism was observed for 1 wt% and 2 wt% concentrations. The lifetime of the 4F3/2 level was found to decrease with increasing Nd3+ ion concentration. The nature of energy transfer process was a single exponential curve which was studied for all the glasses and analysed.

  16. Effect of Er{sub 2}O{sub 3} dopant on electrical and optical properties of potassium sodium niobate silicate glass-ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Yongsiri, Ploypailin [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Sirisoonthorn, Somnuk [National Metal and Materials Technology Center, Pathumthani 12120 (Thailand); Pengpat, Kamonpan, E-mail: kamonpan.p@cmu.ac.th [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai 50200 (Thailand)

    2015-09-15

    Highlights: • The KNN–SiO{sub 2} doped Er{sub 2}O{sub 3} glass-ceramics was prepared by incorporation method. • High dielectric constant (458.41 at 100 kHz) and low loss (0.0005) could be obtained. • TEM and SEM confirmed the existence of KNN crystals embedded in glass matrix. • The Er{sub 2}O{sub 3} dopant causes insignificant effect on modifying E{sub g} value. - Abstract: In this study, transparent glass-ceramics from potassium sodium niobate (KNN)-silicate glass system doped with erbium oxide (Er{sub 2}O{sub 3}) were successfully prepared by incorporation method. KNN was added in glass batches as heterogeneous nucleating agent. The KNN powder was mixed with SiO{sub 2} and Er{sub 2}O{sub 3} dopant with KNN and Er{sub 2}O{sub 3} content varied between 70–80 and 0.5–1.0 mol%, respectively. Each batch was subsequently melted at 1300 °C for 15 min in a platinum crucible using an electric furnace. The quenched glasses were then subjected to heat treatment at various temperatures for 4 h. XRD results showed that the prepared glass ceramics contained crystals of KNN solid solution. In contrary, dielectric constant (ϵ{sub r}) and dielectric loss (tan δ) were found to increase with increasing heat treatment temperature. Additionally, optical properties such as absorbance and energy band gap have been investigated.

  17. Comparative study on the change in index of refraction in ion-exchange interdiffusion in alkali-silicate glasses containing calcium, strontium, barium and titanium oxides

    International Nuclear Information System (INIS)

    Livshits, V.Ya.; Marchuk, E.A.

    1993-01-01

    Different ability to ion exchange from the salts of lithium-sodium-silicate glass melt containing calcium (or strontium, or barium) and titanium oxides in addition has been shown. CaO, SrO and BaO have negative effect, but TiO 2 -positive one on the fullness of ion exchange of lithium-sodium and on the rate of interdiffusion in alkali-silicate glass. The value of change in index of refraction of glass with TiO 2 is twice higher than glass with calcium oxide (or strontium, or barium) as the fourth component

  18. Investigating the effect of V{sub 2}O{sub 5} addition on sodium barium borosilicate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Halder, Rumu, E-mail: rumuhalder24feb@gmail.com; Sengupta, Pranesh; Dey, G. K. [Materials Science Division, Bhabha Atomic Research Centre, Mumbai-700 085 (India); Sudarsan, V. [Chemistry Division, Bhabha Atomic Research Centre, Mumbai-700 085 (India); Kaushik, C. P. [Waste Management Division, Bhabha Atomic Research Centre, Mumbai-700 085 (India)

    2016-05-23

    V{sub 2}O{sub 5} doped sodium barium borosilicate glasses were characterized by photoluminescence spectroscopy and electron probe microanalyzer (EPMA). The glass remains homogeneous for lower concentration of V{sub 2}O{sub 5} but a phase separation is observed when V{sub 2}O{sub 5} doping is increased beyond 5 mol%. Detailed microanalysis reveals that the phase separated glass consists of a phase containing V, Ba and Si and a separate Si rich phase within the glass matrix. The luminescence study demonstrated that at low concentration the vanadium mainly interacts with the structural units of B/Si while at higher concentrations, V-O-V/ V-O{sup −} Na{sup +}/Ba{sup 2+} linkages are formed.

  19. Optical properties of nanocrystalline potassium lithium niobate in the glass system (100-x) TeO2-x(1.5K2O-Li2O-2.5Nb2O5).

    Science.gov (United States)

    Ahamad, M Niyaz; Varma, K B R

    2009-08-01

    Optically clear glasses of various compositions in the system (100-x) TeO2-x(1.5K2O-Li2O-2.5Nb2O5) (2 glasses comprising potassium lithium niobate (K3Li2Nb5O15) microcrystallites on the surface and nanocrystallites within the glass were obtained by controlled heat-treatment of the as-quenched glasses just above the glass transition temperature (T(g)). The optical transmission spectra of these glasses and glass-crystal composites of various compositions were recorded in the 200-2500 nm wavelength range. Various optical parameters such as optical band gap, Urbach energy, refractive index were determined. Second order optical non-linearity was established in the heat-treated samples by employing the Maker-Fringe method.

  20. Gamma ray shielding study of barium-bismuth-borosilicate glasses as transparent shielding materials using MCNP-4C code, XCOM program, and available experimental data

    Energy Technology Data Exchange (ETDEWEB)

    Bagheri, Reza; Yousefinia, Hassan [Nuclear Fuel Cycle Research School (NFCRS), Nuclear Science and Technology Research Institute (NSTRI), Atomic Energy Organization of Iran, Tehran (Iran, Islamic Republic of); Moghaddam, Alireza Khorrami [Radiology Department, Paramedical Faculty, Mazandaran University of Medical Sciences, Sari (Iran, Islamic Republic of)

    2017-02-15

    In this work, linear and mass attenuation coefficients, effective atomic number and electron density, mean free paths, and half value layer and 10th value layer values of barium-bismuth-borosilicate glasses were obtained for 662 keV, 1,173 keV, and 1,332 keV gamma ray energies using MCNP-4C code and XCOM program. Then obtained data were compared with available experimental data. The MCNP-4C code and XCOM program results were in good agreement with the experimental data. Barium-bismuth-borosilicate glasses have good gamma ray shielding properties from the shielding point of view.

  1. Effect of donor and acceptor dopants on crystallization, microstructural and dielectric behaviors of barium strontium titanate glass ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Yadav, Avadhesh Kumar, E-mail: yadav.av11@gmail.com [Department of Physics, Dr. Bheem Rao Ambedkar Government Degree College, Anaugi, Kannauj (India); Gautam, C.R. [Department of Physics, University of Lucknow, Lucknow 226007 (India); Singh, Prabhakar [Department of Physics, Indian Institute of Technology (Banaras Hindu University), Varanasi 221005 (India)

    2016-07-05

    Bulk transparent barium strontium titanate borosilicate glasses in glass system (65-x)[(Ba{sub 0.6}Sr{sub 0.4}).TiO{sub 3}]-30[2SiO{sub 2}.B{sub 2}O{sub 3}]-5[K{sub 2}O]-x[A{sub 2}O{sub 3}], A = La, Fe (x = 2, 5 and 10) were prepared by rapid melt-quench technique and subsequently, converted into glass ceramics by regulated heat treatment process. The phase identification was carried out by X-ray powder diffraction and their surface morphology was studied by scanning electron microscopy. The dielectric properties were studied by impedance spectroscopic technique. Investigated glass samples were crystallized into major and secondary phases of Ba{sub 1.91}Sr{sub 0.09}TiO{sub 4} and Ba{sub 2}TiSi{sub 2}O{sub 8}, respectively. A very high dielectric constant having value upto 68000 was found in glass ceramic sample BST5K10F. This high value of dielectric constant was attributed to interfacial polarization, which arose due to conductivity difference among semiconducting crystalline phases, conducting grains and insulating grain boundaries. Donor dopant La{sub 2}O{sub 3} and acceptor dopant Fe{sub 2}O{sub 3} play an important role for enhancing crystallization, dielectric constant and retardation of dielectric loss in the samples. Moreover, higher value of dielectric constant and lower value of dielectric loss was found in Fe{sub 2}O{sub 3} doped samples in comparison to La{sub 2}O{sub 3} doped samples. - Highlights: • Bulk transparent barium strontium titanate glasses are successfully prepared. • A very high dielectric constant upto 68000 was found in glass ceramics. • La{sub 2}O{sub 3} and Fe{sub 2}O{sub 3} play role for enhancing value of dielectric constant. • Higher dielectric constant with low dielectric loss was found in Fe{sub 2}O{sub 3} doped sample. • Such glass ceramics may be used in making capacitors for high energy storage.

  2. Investigation of the effect of barium content on the structural and gamma-ray shielding properties of bismuth borate glasses

    International Nuclear Information System (INIS)

    Parminder Kaur; Singh, K.J.; Kulwinder Kaur; Anand, Vikas; Dogra, Mridula

    2017-01-01

    Glasses doped with heavy metal oxides have been proposed to shield the hazardous gamma rays originating from nuclear reactors as alternative to the conventional concretes. In this work, transparent glasses with composition 65Bi_2O_3-xBaO-(35-x) B_2O_3 (with x =0, 4, 8 wt %) have been prepared by using melt quenching technique in the laboratory. XRD and FTIR studies have been undertaken to explore the structural properties. The amorphous nature of the prepared samples is confirmed by XRD studies. Structural changes in the system have been explored by FTIR studies. The FTIR results reveal the conversion of (BO_3) triangular units to (BO_4) tetrahedral units with the addition of barium oxide along with the creation of non-bridging oxygen in the prepared glass system. Gamma-ray shielding properties have been explored with the help of WinXCom software developed by National Institute Standards and Technology at photon energy 662 keV. Gamma ray shielding properties in terms of mass attenuation coefficient, half value layer, tenth value layer and mean free path have been found to be superior as compared to the ordinary as well as barite concrete. Therefore, it is speculated that our prepared glass samples can serve as better gamma ray shielding materials. (author)

  3. Influence of alumina on photoluminescence and thermoluminescence characteristics of Gd{sup 3+} doped barium borophosphate glasses

    Energy Technology Data Exchange (ETDEWEB)

    Kalpana, T. [Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P. (India); Gandhi, Y. [Department of Physics, Kakani Venkata Ratnam College, Nandigama 521 185, A.P. (India); Sanyal, Bhaskar [Food Technology Division, Bhabha Atomic Research Center, Trombay, Mumbai 400 085 (India); Sudarsan, V. [Bhabha Atomic Research Centre, Chemistry Division, Mumbai 400 085 (India); Bragiel, P.; Piasecki, M. [Institute of Physics, Jan Dlugosz University, Ul. Armii Krajowej 13/15, Czestochowa 42-201 (Poland); Kumar, V. Ravi [Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P. (India); Veeraiah, N., E-mail: nvr8@rediffmail.com [Department of Physics, Acharya Nagarjuna University, Nagarjuna Nagar 522 510, A.P. (India)

    2016-11-15

    Gd{sup 3+} doped barium borophosphate glasses mixed with varying concentration of Al{sub 2}O{sub 3} are synthesized. Photoluminescence, thermoluminescence and other spectroscopic studies viz., IR and EPR spectral studies, have been carried out. IR spectral studies of these glasses indicated that there is a gradual increase in the degree of depolymerization of the glass network with increase in the concentration of Al{sub 2}O{sub 3} upto 3.0 mol%. The EPR spectral studies revealed the lowest concentration of Gd{sup 3+} ion clusters in the glass mixed with 3.0 mol% of Al{sub 2}O{sub 3}. The photoluminescence emission spectra exhibited strong ultraviolet blue emission at 311 under excitation at 273 nm due to {sup 6}P{sub 7/2}→{sup 8}S{sub 7/2} transition of Gd{sup 3+} ions. The intensity of this band is found to be enhanced four times when the glass mixed with 3.0 mol% of Al{sub 2}O{sub 3} with respect to that of alumina free glass. The enrichment of this emission is attributed to the declustering of Gd{sup 3+} ions by Al{sup 3+} ions. Thermoluminescence (TL) characteristics of these glasses have also been investigated after irradiating them with different doses of γ-rays (in the range 0–8.0 kGy). The TL emission exhibited a dosimetric peak at about 200 °C. The TL output under this glow peak is observed to increase with increase of γ-ray dose. For any fixed γ-ray dose, the TL output is increased with increasing Al{sub 2}O{sub 3} content up to 3.0 mol% and beyond this concentration quenching of TL is observed. The mechanisms responsible for TL emission and the variation in TL output with the concentration of Al{sub 2}O{sub 3} are quantitatively discussed in terms of electron and hole centers developed due to interaction of γ-rays with the glass network. The dose response of these glass samples exhibited linear behavior in the dose range 0–8.0 kGy.

  4. Standardization of a PIGE methodology for simultaneous quantification of low Z elements in barium borosilicate glass samples

    International Nuclear Information System (INIS)

    Chhillar, S.; Acharya, R.; Dasari, K.B.; Pujari, P.K.; Mishra, R.K.; Kaushik, C.P.

    2013-01-01

    In order to standardize particle induced gamma-ray emission (PIGE) methodology for simultaneous quantification of light elements, analytical sensitivities of Li, F, B, Na, Al and Si were evaluated using 4 MeV proton beam ( ∼ 10 nA current) using 3 MV Pelletron at IOP, Bhubaneswar. The PIGE method was validated by determining all six elements in a synthetic sample in graphite matrix and applied to two barium borosilicate glass (BaBSG) samples. The prompt γ-rays emitted from inelastic scattering or nuclear reactions of corresponding isotopes were measured using a 60% HPGe coupled to MCA and the current normalized count rates were used for concentration calculation. (author)

  5. Crystallization Kinetics of Barium and Strontium Aluminosilicate Glasses of Feldspar Composition

    Science.gov (United States)

    Hyatt, Mark J.; Bansal, Narottam P.

    1994-01-01

    Crystallization kinetics of BaO.Al2O3.2SiO2 (BAS) and SrO.Al2O3.2SiO2 (SAS) glasses in bulk and powder forms have been studied by non-isothermal differential scanning calorimetry (DSC). The crystal growth activation energies were evaluated to be 473 and 451 kJ/mol for bulk samples and 560 and 534 kJ/mol for powder specimens in BAS and SAS glasses, respectively. Development of crystalline phases on thermal treatments of glasses at various temperatures has been followed by powder x-ray diffraction. Powder samples crystallized at lower temperatures than the bulk and the crystallization temperature was lower for SAS glass than BAS. Crystallization in both glasses appeared to be surface nucleated. The high temperature phase hexacelsian, MAl2Si2O8 (M = Ba or Sr), crystallized first by nucleating preferentially on the glass surface. Also, monoclinic celsian does not nucleate directly in the glass, but is formed at higher temperatures from the transformation of the metastable hexagonal phase. In SAS the transformation to monoclinic celsian occurred rapidly after 1 h at 1100 C. In contrast, in BAS this transformation is sluggish and difficult and did not go to completion even after 10 h heat treatment at 1400 C. The crystal growth morphologies in the glasses have been observed by optical microscopy. Some of the physical properties of the two glasses are also reported.

  6. Barium boron silicate glass-ceramic for use as sealant in planar SOFC

    International Nuclear Information System (INIS)

    Silva, M.J.; Castanho, S.R.H. Mello; Reis, S.T.

    2012-01-01

    Glass-ceramic seals play an important role in the performance of the solid oxide fuel cell (SOFC). In this work glass-ceramic seals are discussed from the point of view of the thermal behavior of the glass and the electrochemical parameters obtained from polarization curves such as corrosion current densities (i corr ), and corrosion potential (E corr ). A seal material must have a combination of thermal-mechanical and electrochemical properties in order to seal cell components and stacks and prevent side reactions. It must be stable in oxidizing and reducing atmospheres and withstand thermal cycles between room temperature and the cell operating temperature (800 to 900°C). Glass-ceramics in the system BaO- B 2 O 3 -Al 2 O 3 -SiO 2 were investigated and compared from the point of view of sealing ability. Dilatometric analysis, thermal stability against crystallization, microstructure and electrochemical durability are discussed. (author)

  7. Short-range structure and thermal properties of barium tellurite glasses

    Science.gov (United States)

    Kaur, Amarjot; Khanna, Atul; Gonzàlez, Fernando

    2017-05-01

    BaO-TeO2 glasses containing 10 to 20 BaO mol% were prepared and characterized by X-ray diffraction, density measurements, differential scanning calorimetry and Raman spectroscopy. Glass density decreases with increase in BaO concentration from 10 to 20 mol%, due to replacement of heavier TeO2 by lighter BaO, however glass transition temperature (Tg) increases significantly from a value of 318°C to 327°C due to increase in average single bond enthalpy of the tellurite network. Raman studies found that glass short-range structure consists of TeO4 and TeO3 structural units and BaO modifies the network by producing the structural transformation: TeO4→ TeO3.

  8. Zinc chloride modified electronic transport and relaxation studies in barium-tellurite glasses

    Science.gov (United States)

    Dhankhar, Sunil; Kundu, R. S.; Rani, Sunita; Sharma, Preeti; Murugavel, S.; Punia, Rajesh; Kishore, N.

    2017-09-01

    The ac conductivity of halide based tellurium glasses having composition 70 TeO2-(30-x) BaO-x ZnCl2; x = 5, 10, 15, 20 and 25 has been investigated in the frequency range 10-1 Hz to 105Hz and in the temperature range 453 K to 553 K. The frequency and temperature dependent ac conductivity show mixed behaviour with increase in halide content and found to obey Jonscher's universal power law. The values of dc conductivity, crossover frequency and frequency exponent have been estimated from the fitting of experimental data of ac conductivity with Jonscher's universal power law. For determining the conduction mechanism in studied glass system, frequency exponent has been analyzed by various theoretical models. In presently studied glasses, the ac conduction takes place via overlapping large polaron tunneling (OLPT). The values of activation energy for dc conduction (W) and the one associated with relaxation process ( E R) are found to increase with increase in x up to glass sample with x = 15 and thereafter it decrease with increase in zinc chloride content. DC conduction takes place via variable range hopping (VRH) as proposed by Mott with some modification suggested by Punia et al. The value of real part of modulus ( M') is observed to decrease with increase in temperature. The value of stretched exponent (β) obtained from fitting of M'' reveals the presence of non-Debye type of relaxation in presently studied glass samples. Scaling spectra of ac conductivity and values of electric modulus ( M' and M'') collapse into a single master curve for all the compositions and temperatures. The values of relaxation energy ( E R) for all the studied glass compositions are almost equal to W, suggesting that polarons have to overcome same barrier while relaxing and conducting. The conduction and relaxation processes in the studied glass samples are composition and temperature independent. [Figure not available: see fulltext.

  9. Gamma-ray shielding effect of Gd3+ doped lead barium borate glasses

    Science.gov (United States)

    Kummathi, Harshitha; Naveen Kumar, P.; Vedavathi T., C.; Abhiram, J.; Rajaramakrishna, R.

    2018-05-01

    The glasses of the batch xPbO: 10BaO: (90-x)B2O3: 0.2Gd2O3 (x = 40,45,50 mol %) were prepared by melt-quench technique. The work emphasizes on gamma ray shielding effect on doped lead glasses. The role of Boron is significant as it acts as better neutron attenuator as compared with any other materials, as the thermal neutron cross-sections are high for Gadolinium, 0.2 mol% is chosen as the optimum concentration for this matrix, as higher the concentration may lead to further increase as it produces secondary γ rays due to inelastic neutron scattering. Shielding effects were studied using Sodium Iodide (NaI) - Scintillation Gamma ray spectrometer. It was found that at higher concentration of lead oxide (PbO) in the matrix, higher the attenuation which can be co-related with density. Infra-red (I.R.) spectra reveals that the conversion of Lose triangles to tight tetrahedral structure results in enhancement of shielding properties. The Differential Scanning Calorimeter (D.S.C.) study also reveals that the increase in glass forming range increases the stability which in-turn results in inter-conversion of BO3 to BO4 units such that the density of glass increases with increase in PbO content, resulting in much stable and efficient gamma ray shielding glasses.

  10. Optical and EPR studies of barium alumino borate glasses containing Cu2+ ions

    Science.gov (United States)

    Ahmed, Mohamad Raheem; Phani, A. V. Lalitha; Narsimha Chary, M.; Shareefuddin, Md.

    2018-05-01

    Glass containing Cu2+ ions in (30-x) BaO-xAl2O3-69.5B2O3-0.5CuO (0 ≤ x ≤ 15 mol %) were prepared by the conventional melt quenching technique. Peak free X-ray diffractograms confirmed the amorphous nature of the glass samples. Spectroscopic studies such as optical absorption, EPR were studied to understand the effect of modifier oxide and CuO dopant. From EPR spectra the spin-Hamiltonian parameter were evaluated. The ground state of Cu2+ is dx2-y2 (2B1g state) and the site symmetry around Cu2+ is tetragonally distorted octahedral. A broad optical absorption band was observed for all the glasses containing Cu2+ ions corresponding to the 2B1g → 2B2g transition. The optical band gap and Urbach energy values are calculated.

  11. Decay kinetics study of Ag0 in silver doped barium aluminoborate glasses

    International Nuclear Information System (INIS)

    Pontuschka, W.M.; Santos, J.T. dos; Isotani, S.; Rabbani, S.R.

    1989-12-01

    EPR measurements of 30BaO.50B 2 O 3 .20Al 2 O 3 at. % glasses containing different amounts of silver impurity, X-and γ-irradiated at room temperature, showed the presence of Ag 0 and Ag ++ centers. Decay kinetics of Ag 0 was determined for different temperatures in glass containing 0.1% of silver. We show that our model of stabilization energy of H 0 in B-O rings through van der Waals forces is not applicable to Ag 0 . Thus, we propose the model of reduction of Ag 0 to Ag + as the mechanism of the Ag 0 decay kinetics. (author) [pt

  12. Mixed conductivity studies in silver oxide based barium vanado-tellurite glasses

    International Nuclear Information System (INIS)

    Pant, Meenakshi; Kanchan, D.K.; Sharma, Poonam; Jayswal, Manish S.

    2008-01-01

    The dc conductivity and frequency dependent ac conductivity of the quaternary glass system x(BaO:1.5 Ag 2 O)-(95 - x)V 2 O 5 -5TeO 2 , are reported in the frequency range 1 Hz to 32 MHz in the temperature range from room temperature to 433 K. The dc conductivity measured in high temperature range increased with transition metal oxide content while the activation range decreased. The conductivity arises mainly from polaron hopping between V 4+ and V 5+ ions. High temperature conductivity data satisfy Mott's small polaron hopping model. It is found that a mechanism of non-adiabatic hopping is the most appropriate conduction model for these glasses. A power law behavior σ(ω) = σ dc + Aω n (with 0 < n < 1) is well exhibited by the ac conductivity data of the glasses. The activation energy calculated from both the relaxation time and dc conductivity is found to be nearly same in both the cases. A scaling of the conductivity spectra with respect to temperature and composition is attempted and it is observed that the relaxation dynamics of charge carriers in the present glasses is independent of temperature and composition

  13. Spectroscopic properties of chromium(III) in zirconium barium fluoride glass (ZBLA)

    International Nuclear Information System (INIS)

    Balda, R.; Fernandez, J.; Illarramendi, M.A.; Elejalde, M.J.

    1988-01-01

    The optical properties of trivalent chromium ions in ZBLA glass have been studied for different concentrations of Cr 3 + . Optical absorption, luminescence and lifetimes have been investigated in a wide range of temperatures. The relative quantum efficiencies of these systems have been determined from the integrated luminescence decay curves as a function of the excitation wavelength

  14. Barium and calcium borate glasses as shielding materials for x rays and gamma rays

    DEFF Research Database (Denmark)

    Singh, H.; Singh, K.; Sharma, G.

    2003-01-01

    Values of the gamma-ray, mass attenuation coefficient and the effective atomic number have been determined experimentally for xBaO.(1-x) B2O3 (x=0.24, 0.30, 0.34,0.40 and 0.44) and xCaO. (I-x)B2O3 (x=0.30 and 0.40) glasses at photon energies 356, 511, 662, 1173, and 1332 keV It is pointed out tha...... that these glasses are potential radiation shielding materials. The specific volume of the glasses has been derived from density measurements and studied as a function of composition.......Values of the gamma-ray, mass attenuation coefficient and the effective atomic number have been determined experimentally for xBaO.(1-x) B2O3 (x=0.24, 0.30, 0.34,0.40 and 0.44) and xCaO. (I-x)B2O3 (x=0.30 and 0.40) glasses at photon energies 356, 511, 662, 1173, and 1332 keV It is pointed out...

  15. Luminescence properties of erbium doped sodium barium borate glass with silver nanoparticles

    Science.gov (United States)

    Rajeshree Patwari, D.; Eraiah, B.

    2018-02-01

    Alteration in the absorption features of rare earth (RE) doped glasses with silver nanoparticles is ever-challenging in photonics. Erbium (Er3+) doped glasses with composition (60-x-y)B2O3-30Na2CO3-10BaO-xEr2O3-yAgCl where (x=0.5, 1.0 and y=1.0 mol %) are synthesized using melt-quenching method. The density is determined by Archimedes principle and molar volumes are calculated. Glass samples were characterized by XRD and UV-Visible spectroscopy. UV-Visible spectra shows eleven prominent absorption peaks centred around 366, 378, 408, 442, 452, 489, 521, 547, 652, 800 and 977 nm equivalent to the rare earth (Er3+) ion transitions. The sample without rare earth shows no peaks which specifies that rare earth ion plays a spirited role in the glass matrix. The glass samples with silver and without rare earth ion shows plasmon peak on heat treatment. The energy band gap values calculated for direct and indirect transitions are in the range of 3.126-3.440eV and 2.58-3.177eV respectively. The refractive indices and Urbach energies are also determined. Photoluminescence spectra are recorded and studied for excitation of the most intense peaks of wavelengths 378 and 521nm. The luminescence of erbium ion is enhanced by the presence of silver when the concentration of rare earth ion is less than that of silver.

  16. Structure and properties of barium tin boro-phosphate glass systems with very low photoelastic constant

    Science.gov (United States)

    Itadani, M.; Tricot, G.; Doumert, B.; Takebe, H.; Saitoh, A.

    2017-08-01

    Glasses in the BaO-SnO-P2O5-B2O3 system were prepared and evaluated in order to formulate preform glasses suitable for the fabrication of fiber cores with a very low photoelastic constant. A first glass system (I: xBaO-(60-x)SnO-40P2O5) was designed with a constant P2O5 content and various BaO contents (0-40 mol. %). Introduction of 3 mol. % of B2O3 to enhance the glass stability leads to the second glass system (II: x'BaO-(57-x')SnO-40P2O5-3B2O3) with 33-38 mol. % BaO. The structure of both systems was investigated by 1D/2D magic-angle spinning nuclear magnetic resonance, Raman, and Fourier transform infrared spectroscopic techniques. 31P NMR showed the presence of Q2 and Q1 units in the first system and correlation 11B/31P NMR indicated that boron enters into the network as B(OP)4 structural units. The photoelastic constant was determined and the stability of the best formulations as well as their refractive index dispersion was established. The drawing temperature and isothermal heating time (without crystal precipitation) parameters were also accurately measured by using experimental time-temperature-transition. Considering that the refractive indices of the core and the cladding materials must match, detailed core and cladding compositions for a fiber enabling single-mode waveguide transmission were proposed.

  17. Effect of sulfur addition and heat treatment on electrical conductivity of barium vanadate glasses containing iron

    Energy Technology Data Exchange (ETDEWEB)

    Hassaan, M.Y., E-mail: myhassaan@yahoo.com [Al-Azhar University, Faculty of Science, Physics Department, 11884 Cairo (Egypt); Ebrahim, F.M.; Mostafa, A.G. [Al-Azhar University, Faculty of Science, Physics Department, 11884 Cairo (Egypt); El-Desoky, M.M., E-mail: mmdesoky@gmail.com [Suez Canal University, Faculty of Science, Physics Department, Suez (Egypt)

    2011-09-15

    Highlights: {yields} Selected glasses of V{sub 2}O{sub 5}-BaO-5Fe{sub 2}O{sub 3} system have been transformed into nanomaterials by annealing at temperature close to crystallization temperature (T{sub c}) for 1 h. {yields} Glass ceramic nanocrystals are important because of their physical properties which are not obtainable in other classes of materials. {yields} Crystal and grain sizes are the most significant structural parameters in electronic nanocrystalline glassy phases. {yields} These phases have very high electrical conductivity, hence glass-ceramic nanocrystals are expected to be used, for example, as a gas sensor. - Abstract: Six glass samples with a composition of 75V{sub 2}O{sub 5} + 10BaO + 15Fe{sub 2}O{sub 3} mol%, with 0, 10, 15, 20, and 25 wt% of sulfur were prepared by using a quenching method. The samples were measured by XRD, DSC, TEM, Moessbauer spectrometry and D.C. conductivity. The prepared samples were heat treated at temperature close to their crystallization temperatures for 1 h, and then the previous measurements were repeated. The results showed that the treatment process caused the formation of V{sub 2}O{sub 5} and FeVO{sub 4} nanocrystals with size of 17-25 nm dispersed in the glass matrix. The addition of sulfur reduced only the vanadium ions to V{sup 4+}, while it was found that iron ions were Fe{sup 3+} only. D.C. conduction enhanced due to the small polaron or electron hopping from V{sup 4+} to V{sup 5+} ions. The heat treated samples exhibit much higher conductivity and much lower activation energy than the as-prepared glasses. The heat treated samples showed decreased thermal stability with the addition of sulfur. This considerable enhancement of electrical conductivity after nanocrystallization referred to the formation of extensive and dense network of electronic conduction paths which are situated between V{sub 2}O{sub 5} nanocrystals and their surfaces.

  18. Positron annihilation in some barium borate glasses containing transition metal oxides

    International Nuclear Information System (INIS)

    Usmar, S.G.; Rawson, H.; West, R.N.

    1982-01-01

    Results of positron lifetime and angular correlation measurements for the glass series xMsub(s)Osub(r):(1-x)(0.4BaO:0.6B 2 O 3 ) are presented (Msub(s)Osub(r) equivalent to V 2 O 5 ;Fe 2 O 3 and CuO). All glasses exhibit two or three component lifetime spectra, tau 1 approximately 200 ps; tau 2 approximately 300-400 ps and tau 3 approximately 780 ps. tau 1 is attributed to a mixture of pPs and bulk state annihilation, tau 2 to a trapped or bound state and tau 3 to oPs pick-off. Supporting evidence for these assignments is found in the angular correlation results. (Auth.)

  19. Barite (Barium)

    Science.gov (United States)

    Johnson, Craig A.; Piatak, Nadine M.; Miller, M. Michael; Schulz, Klaus J.; DeYoung,, John H.; Seal, Robert R.; Bradley, Dwight C.

    2017-12-19

    Barite (barium sulfate, BaSO4) is vital to the oil and gas industry because it is a key constituent of the mud used to drill oil and gas wells. Elemental barium is an additive in optical glass, ceramic glazes, and other products. Within the United States, barite is produced mainly from mines in Nevada. Imports in 2011 (the latest year for which complete data were available) accounted for 78 percent of domestic consumption and came mostly from China.Barite deposits can be divided into the following four main types: bedded-sedimentary; bedded-volcanic; vein, cavity-fill, and metasomatic; and residual. Bedded-sedimentary deposits, which are found in sedimentary rocks with characteristics of high biological productivity during sediment accumulation, are the major sources of barite production and account for the majority of reserves, both in the United States and worldwide. In 2013, China and India were the leading producers of barite, and they have large identified resources that position them to be significant producers for the foreseeable future. The potential for undiscovered barite resources in the United States and in many other countries is considerable, however. The expected tight supply and rising costs in the coming years will likely be met by increased production from such countries as Kazakhstan, Mexico, Morocco, and Vietnam.Barium has limited mobility in the environment and exposed barium in the vicinity of barite mines poses minimal risk to human or ecosystem health. Of greater concern is the potential for acidic metal-bearing drainage at sites where the barite ores or waste rocks contain abundant sulfide minerals. This risk is lessened naturally if the host rocks at the site are acid-neutralizing, and the risk can also be lessened by engineering measures.

  20. Short-range structure of barium tellurite glasses and its correlation with stress-optic response

    Science.gov (United States)

    Kaur, Amarjot; Khanna, Atul; Fábián, Margit

    2018-06-01

    The atomic parameters of metal ion-oxygen speciation such as bond-lengths and nearest neighbor distances for Ba-O, Te-O and O-O pairs, co-ordination numbers and bond angle distributions for O-Ba-O, O-Te-O and O-O-O linkages are determined by neutron diffraction and Reverse Monte Carlo simulations on the series of xBaO-(100-x)TeO2 glasses containing 10, 15 and 20 mol% BaO. The glass network depolymerizes and the average Te-O co-ordination number decreases from 3.60 ± 0.02 to 3.48 ± 0.02 with increase in BaO concentration. Te-O bond lengths are in the range: 1.97 ± 0.01–1.92 ± 0.01 Å. Ba2+ is mostly in octahedral coordination and the Ba-O bond lengths are in the range: 2.73 ± 0.01 to 2.76 ± 0.03 Å. Te-O co-ordination number is also determined by Raman spectroscopy and it shows good agreement with the neutron data. The short-range structural properties i.e. metal ion coordination number (Nc) and bond lengths (d) were correlated with the stress-optic response. The bonding characteristic, Br values were determined from the structural data of xBaO-(100-x)TeO2 glasses and were used to predict the stress-induced birefringence properties.

  1. The effects of sulfate content on crystalline phase, microstructure, and chemical durability of zirconolite−barium borosilicate glass-ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Lang, E-mail: lang.wu@163.com [State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China); Wang, Xin; Li, Huidong; Teng, Yuancheng [State Key Laboratory Cultivation Base for Nonmetal Composites and Functional Materials, Southwest University of Science and Technology, Mianyang 621010 (China); Peng, Long [Sichuan Province Key Laboratory of Information Materials and Devices Application, Chengdu University of Information Technology, Chengdu 610225 (China)

    2016-09-15

    The effects of sulfate content on structure and chemical durability of barium borosilicate glass-ceramics were studied. The results show that the glass-ceramics with 0–1.10 mol% SO{sub 3} possess mainly CaZrTi{sub 2}O{sub 7}-2M phase along with a small amount of CaZrTi{sub 2}O{sub 7}-3T and ZrO{sub 2} phases. The hexagonal CaZrTi{sub 2}O{sub 7}-3T crystals crystallize on the surface of glass-ceramics. For the samples with 1.24–1.55 mol% SO{sub 3}, the main crystalline phases are CaTiSiO{sub 5} and CaZrTi{sub 2}O{sub 7}-2M in the bulk, while a separate sulfate layer containing Na{sub 2}SO{sub 4} and BaSO{sub 4} is observed on the surface. X-ray fluorescence analysis indicates that about 2/3 of the SO{sub 3} originally added has been lost by volatility. The normalized mass loss (NL{sub i}) for Na, B, Ca elements remains almost unchanged (∼10{sup −2} g/m{sup 2}) after 7 days for the samples with 0–1.10 mol% SO{sub 3}. The NL{sub i} for both Na and B increases gradually after 7 days when the SO{sub 3} content is 1.24 mol%. - Highlights: • Strip-shaped CaZrTi{sub 2}O{sub 7}-2M and plate-like CaTiSiO{sub 5} crystals crystallize in the bulk. • CaZrTi{sub 2}O{sub 7}-3T crystals crystallize on the surface for samples with 0–1.10 mol% SO{sub 3}. • A separate sulfate layer crystallizes on the surface when SO{sub 3} exceeds solubility.

  2. Barium enema

    Science.gov (United States)

    ... series; Colorectal cancer - lower GI series; Colorectal cancer - barium enema; Crohn disease - lower GI series; Crohn disease - barium enema; Intestinal blockage - lower GI series; Intestinal blockage - ...

  3. Lithium niobate packaging challenges

    International Nuclear Information System (INIS)

    Murphy, E.J.; Holmes, R.J.; Jander, R.B.; Schelling, A.W.

    1988-01-01

    The use of lithium niobate integrated optic devices outside of the research laboratory is predicated on the development of a sound packaging method. The authors present a discussion of the many issues that face the development of a viable, robust packaging technology. The authors emphasize the interaction of lithium niobate's physical properties with available packaging materials and technologies. The broad range of properties (i.e. electro-optic, piezo-electric, pyro-electric, photorefractive...) that make lithium niobate an interesting material in many device applications also make it a packaging challenge. The package design, materials and packaging technologies must isolate the device from the environment so that lithium niobate's properties do not adversely affect the device performance

  4. The effects of dopants on the electrical resistivity in lead magnesium niobate multilayer ceramic capacitors

    International Nuclear Information System (INIS)

    Chang, D.D.; Ling, H.C.

    1989-01-01

    Electrical resistivity studies were performed on multilayer ceramic capacitors (MLC) based on lead magnesium niobate and containing dopants of lead titanate, lead zinc niobate, and lead cobalt niobate. The results showed that lead titanate and/or lead zinc niobate had no effect on the electrical resistivity while lead cobalt niobate decreased the resistivity. In samples without lead cobalt niobate, we observed a conduction mechanism with an activation energy of --1 eV, which is commonly observed in barium titanate based dielectrics. This is attributed to ionic conduction via the motion of oxygen vacancies. The increase in conductivity (or decrease in resistivity) resulting from the addition of lead cobalt niobate was rationalized as due to electronic conduction through charge hopping among the cations. This conduction mechanism was characterized by an activation energy of --0.5 eV. Since the activation energy associated with the long-term failure was previously determined by a matrix of temperature and voltage accelerated life tests to be -- 1 eV, they conclude that conduction through charge hopping is not affecting the long-term reliability of these devices

  5. Crystalline phase, microstructure, and aqueous stability of zirconolite-barium borosilicate glass-ceramics for immobilization of simulated sulfate bearing high-level liquid waste

    Science.gov (United States)

    Wu, Lang; Xiao, Jizong; Wang, Xin; Teng, Yuancheng; Li, Yuxiang; Liao, Qilong

    2018-01-01

    The crystalline phase, microstructure, and aqueous stability of zirconolite-barium borosilicate glass-ceramics with different content (0-30 wt %) of simulated sulfate bearing high-level liquid waste (HLLW) were evaluated. The sulfate phase segregation in vitrification process was also investigated. The results show that the glass-ceramics with 0-20 wt% of HLLW possess mainly zirconolite phase along with a small amount baddeleyite phase. The amount of perovskite crystals increases while the amount of zirconolite crystals decreases when the HLLW content increases from 20 to 30 wt%. For the samples with 20-30 wt% HLLW, yellow phase was observed during the vitrification process and it disappeared after melting at 1150 °C for 2 h. The viscosity of the sample with 16 wt% HLLW (HLLW-16) is about 27 dPa·s at 1150 °C. The addition of a certain amount (≤20 wt %) of HLLW has no significant change on the aqueous stability of glass-ceramic waste forms. After 28 days, the 90 °C PCT-type normalized leaching rates of Na, B, Si, and La of the sample HLLW-16 are 7.23 × 10-3, 1.57 × 10-3, 8.06 × 10-4, and 1.23 × 10-4 g·m-2·d-1, respectively.

  6. Influence of sintering temperature on microstructures and energy-storage properties of barium strontium titanate glass-ceramics prepared by sol-gel process

    Energy Technology Data Exchange (ETDEWEB)

    Zhu, Jia; Zhang, Yong; Song, Xiaozhen; Zhang, Qian; Yang, Dongliang; Chen, Yongzhou [Beijing Key Laboratory of Fine Ceramics, State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China)

    2015-12-15

    The sol-gel processing, microstructures, dielectric properties and energy-storage properties of barium strontium titanate glass-ceramics over the sintering temperature range of 1000-1150 C were studied. Through the X-ray diffraction result, it is revealed that the crystallinity increases as the sintering temperature increased from 1000 to 1080 C and has reached a steady-state regime above 1100 C. Scanning electron microscopy images showed that with the increase of sintering temperature, the crystal size increased. Dielectric measurements revealed that the increase in the sintering temperature resulted in a significant increase in the dielectric constant, a strong sharpness of the temperature-dependent dielectric response and a pronounced decrease of the temperature of the dielectric maximum. The correlation between charge spreading behavior and activation energies of crystal and glass was discussed by the employment of the impedance spectroscopy studies. As a result of polarization-electric field hysteresis loops, both the charged and discharged densities increased with increasing sintering temperature. And the maximum value of energy storage efficiency was found to occur at 1130 C. Finally, the dependence of released energy and power densities calculated from the discharged current-time (I-t) curves on the sintering temperature was studied. The relationship between the energy storage properties and microstructure was correlated. Polarization-electric field hysteresis loops for the BST glass-ceramics sintered at different temperatures. (copyright 2015 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  7. Correlation between nanostructural and electrical properties of barium titanate-based glass-ceramic nano-composites

    Energy Technology Data Exchange (ETDEWEB)

    Al-Assiri, M.S., E-mail: msassiri@kku.edu.sa [Department of Physics, King Khaled University, P.O. Box 9003, Abha (Saudi Arabia); El-Desoky, M.M., E-mail: mmdesoky@gmail.com [Department of Physics, King Khaled University, P.O. Box 9003, Abha (Saudi Arabia); Department of Physics, Faculty of Science, Suez Canal University, Suez (Egypt)

    2011-09-08

    Highlights: > Glasses have been transformed into nanomaterials by annealing at crystallization temperature. > Glass-ceramic nano-composites are important because of their new physical. > Grain sizes are the most significant structural parameter in electronic nanocrystalline phases. > These phases are very high electrical conductivity. > Hence, glass-ceramic nanocrystals are expected to be used, as gas sensors. - Abstract: Glasses in the system BaTiO{sub 3}-V{sub 2}O{sub 5}-Bi{sub 2}O{sub 3} have been transformed into glass-ceramic nano-composites by annealing at crystallization temperature T{sub cr} determined from DSC thermograms. After annealing they consist of small crystallites embedded in glassy matrix. The crystallization temperature T{sub cr} increases with increasing BaTiO{sub 3} content. XRD and TEM of the glass-ceramic nano-composites show that nanocrystals were embedded in the glassy matrix with an average grain size of 25 nm. The resulting materials exhibit much higher electrical conductivity than the initial glasses. It was postulated that the major role in the conductivity enhancement of these nanomaterials is played by the developed interfacial regions between crystalline and amorphous phases, in which the concentration of V{sup 4+}-V{sup 5+} pairs responsible for electron hopping, has higher than values that inside the glassy matrix. The experimental results were discussed in terms of a model proposed in this work and based on a 'core-shell' concept. From the best fits, reasonable values of various small polaron hopping (SPH) parameters were obtained. The conduction was attributed to non-adiabatic hopping of small polaron.

  8. Barium Sulfate

    Science.gov (United States)

    ... uses a computer to put together x-ray images to create cross-sectional or three dimensional pictures of the inside of the body). Barium sulfate is in a class of medications called radiopaque contrast media. It works by coating the esophagus, stomach, or ...

  9. Textured and tungsten-bronze-niobate-doped (K,Na,Li)(Nb,Ta)O3 piezoceramic materials

    International Nuclear Information System (INIS)

    Soller, Thomas; Bathelt, Robert; Benkert, Katrin; Bodinger, Hermann; Schuh, Carsten; Schlenkrich, Falko

    2010-01-01

    In this study, the effects of an alkaline-earth niobate doping in tungsten-bronze (TB) stoichiometry on the piezoelectric properties and the phase transition temperatures of lead-free (K,Na,Li)(Nb,Ta)O 3 ceramics were investigated. In particular, the TB compounds barium niobate (BN), barium sodium niobate (BNN) and strontium calcium sodium niobate (SCNN) were investigated. The TB-modified ceramics show promising piezoelectric properties with large-signal piezo coefficients, d 33 * lose to 400 pm/V, planar coupling coefficients, k p , up to 0.45 and Curie temperatures of approximately 310 .deg. C. In addition, the effect of texturing on the undoped (K,Na,Li)(Nb,Ta)O 3 base composition via templated grain growth (TGG) with microcrystalline NaNbO 3 templates was examined. Lotgering factors up to 81% and strain enhancements by a factor 1.5 with large-signal values of d 33 * up to 550 pm/V could be achieved in the textured samples.

  10. Determination of barium and strontium in Basub(x)Srsub(1-x)Nbsub(2)Osub(6) monocrystals and raw materials after their solvent ' extraction separation with 1-phenyl-3-methyl-4-benzoylpyrazolone-5

    International Nuclear Information System (INIS)

    Sizonenko, N.T.; Egorova, L.A.

    1981-01-01

    The extraction of milligram amounts of barium and strontium by 1-phenyl-3-methyl-4-benzoylpyrazolone-5 solutions in various diluents has been examined. The possibility has been shown of using the reagent for extraction separation of the elements for determining the stoichiometric composition of barium- and strontium-based compounds. Conditions have been studied for separation of barium and strontium at their different ratios by the chromate method in the presence of EDTA. A procedure has been worked out of determining barium and strontium in the estimation of stoichiometric composition of charge and single crystals of barium-strontium niobates of different composition

  11. BARIUM RECOVERY PROCESS

    Science.gov (United States)

    Blanco, R.E.

    1959-07-21

    A method of separating barium from nuclear fission products is described. In accordance with the invention, barium may be recovered from an acidic solution of neutron-irradiated fissionable material by carrying ihe barium cut of solution as a sulfate with lead as a carrier and then dissolving the barium-containing precipitate in an aqueous solution of an aliphatic diamine chelating reagent. The barium values together with certain other metallic values present in the diamine solution are then absorbed onto a cation exchange resin and the barium is selectively eluted from the resin bed with concentrated nitric acid.

  12. Barium enema (image)

    Science.gov (United States)

    A barium enema is performed to examine the walls of the colon. During the procedure, a well lubricated enema tube is inserted gently into the rectum. The barium, a radiopaque (shows up on X-ray) contrast ...

  13. Effect of rare-earth additions on the structure and dielectric energy storage properties of Ba{sub x}Sr{sub 1-x}TiO{sub 3}-based barium boronaluminosilicate glass-ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Xiu, Shaomei; Xiao, Shi; Zhang, Wenqin; Xue, Shuangxi; Shen, Bo, E-mail: shenbo@tongji.edu.cn; Zhai, Jiwei, E-mail: apzhai@tongji.edu.cn

    2016-06-15

    Ba{sub x}Sr{sub 1-x}TiO{sub 3}-based barium boroaluminosilicate (BST-BBAS) glass-ceramics added with La{sub 2}O{sub 3}, Gd{sub 2}O{sub 3} and Yb{sub 2}O{sub 3} were fabricated through the melting method followed by controlled crystallization, respectively. The X-ray diffraction and the field emission scanning electron microscopy were investigated the phase composition and microstructure for the BST-BBAS glass-ceramics added with rare-earth additions, then the temperature-dependent dielectric properties and the voltage-withstand measurements were applied to study the effect of rare-earth additions on the dielectric energy storage density. These results show that the certain content of rare-earth additions can optimize the microstructure and phase structure effectively. And with the decrease of ionic radiuses of rare-earth elements, the microstructure of the glass-ceramics become more uniform. When added with 0.5 mol% Yb{sup 3+}, the theoretical energy storage density of the BST-BBAS glass-ceramics gets the largest value of 3.5 J/cm{sup 3} which is about 1.8 times compared to the undoped one. - Highlights: • A certain content of Yb{sub 2}O{sub 3} can restrain the formation of BaSi{sub 2}O{sub 5}and SiO{sub 2} phases. • The addition of rare earth can optimize the microstructure. • With 0.5 mol% Yb{sup 3+}, the dielectric energy storage density got the largest value of 3.5 J/cm{sup 3}.

  14. Glasses

    DEFF Research Database (Denmark)

    Dyre, Jeppe

    2004-01-01

    The temperature dependence of the viscosity of most glassforming liquids is known to depart significantly from the classical Arrhenius behaviour of simple fluids. The discovery of an unexpected correlation between the extent of this departure and the Poisson ratio of the resulting glass could lead...... to new understanding of glass ageing and viscous liquid dynamics....

  15. Role of Al coordination in barium phosphate glasses on the emission features of Ho{sup 3+} ion in the visible and IR spectral ranges

    Energy Technology Data Exchange (ETDEWEB)

    Satyanarayana, T.; Kalpana, T.; Ravi Kumar, V. [Department of Physics, Acharya Nagarjuna University-Nuzvid Campus, Nuzvid-521 201, A.P. (India); Veeraiah, N., E-mail: nvr8@rediffmail.co [Department of Physics, Acharya Nagarjuna University-Nuzvid Campus, Nuzvid-521 201, A.P. (India)

    2010-03-15

    The glasses of the composition (39-x)BaO-xAl{sub 2}O{sub 3}-60P{sub 2}O{sub 5}:1.0Ho{sub 2}O{sub 3} (in mol%) with x value ranging from 1.0 to 4.0 have been synthesized. The IR spectral studies of these glasses have indicated that there is a gradual transformation of Al{sup 3+} ions from tetrahedral to octahedral with increase in the concentration of Al{sub 2}O{sub 3} up to 3.0 mol%. Optical absorption and fluorescence spectra (in the visible and NIR regions) of these glasses have been recorded at room temperature. The Judd-Ofelt theory could successfully be applied to characterize the absorption and luminescence spectra of Ho{sup 3+} ions in these glasses. From the luminescence spectra, various radiative properties like transition probability A, branching ratio beta{sub r}, the radiative lifetime tau{sub r} and emission cross-section sigma{sup E} for various emission levels of these glasses have been evaluated. The radiative lifetime of the {sup 5}S{sub 2}->{sup 5}I{sub 8} (green emission) transition has also been measured. The variations observed in these parameters have been discussed in the light of varying co-ordinations (tetrahedral and octahedral positions) of Al{sup 3+} ions in the glass network. The influence of hydroxyl groups on the luminescence efficiency of the transition {sup 5}S{sub 2}->{sup 5}I{sub 8} has also been discussed. Finally the optimum concentration of Al{sub 2}O{sub 3} for getting maximum luminescence output has also been identified and reported.

  16. Synthesis of lithium niobate and monocrystal growth by Czochralski method

    International Nuclear Information System (INIS)

    Balzuweit, K.

    1988-01-01

    The qualitative analysis of lithium niobate by x-ray analysis and optical microscopy is presented. The lithium niobate compound was obtained by synthesis using niobium oxides and lithium carbonates. The lithium niobate monocrystal growth was done by Czochralski method. (M.C.K.)

  17. Reduced Dimensionality Lithium Niobate Microsystems

    Energy Technology Data Exchange (ETDEWEB)

    Eichenfield, Matt [Sandia National Lab. (SNL-NM), Albuquerque, NM (United States)

    2017-01-01

    The following report describes work performed under the LDRD program at Sandia National Laboratories October 2014 and September 2016. The work presented demonstrates the ability of Sandia Labs to develop state-of-the-art photonic devices based on thin film lithium niobate (LiNbO3 ). Section 1 provides an introduction to integrated LiNbO3 devices and motivation for developing thin film nonlinear optical systems. Section 2 describes the design, fabrication, and photonic performance of thin film optical microdisks fabricated from bulk LiNbO3 using a bulk implantation method developed at Sandia. Sections 3 and 4 describe the development of similar thin film LiNbO3 structures fabricated from LiNbO3 on insulator (LNOI) substrates and our demonstration of optical frequency conversion with state-of-the-art efficiency. Finally, Section 5 describes similar microdisk resonators fabricated from LNOI wafers with a buried metal layer, in which we demonstrate electro-optic modulation.

  18. Morphology and orientation of β-BaB{sub 2}O{sub 4} crystals patterned by laser in the inside of samarium barium borate glass

    Energy Technology Data Exchange (ETDEWEB)

    Nishii, Akihito; Shinozaki, Kenji; Honma, Tsuyoshi; Komatsu, Takayuki, E-mail: komatsu@mst.nagaokaut.ac.jp

    2015-01-15

    Nonlinear optical β-BaB{sub 2}O{sub 4} crystal lines (β-BBO) were patterned in the inside of 8Sm{sub 2}O{sub 3}–42BaO–50B{sub 2}O{sub 3} glass by irradiations of continuous-wave Yb:YVO{sub 4} lasers with a wavelength of 1080 nm (power: P=0.8–1.0 W, scanning speed: S=0.2–2.5 μm/s), in which the laser focal position was moved gradually from the surface to the inside. The morphology, size, and orientation of β-BBO crystals were examined from polarization optical microscope and birefringence imaging observations. It was demonstrated that c-axis oriented β-BBO crystals with long lengths (e.g., 20 mm) were patterned in the inside of the glass. The morphology of β-BBO in the cross-section of lines was a rectangular shape with rounded corners, and the volume of β-BBO formed increased with increasing laser power and with decreasing laser scanning speed. The maximum depth in the inside from the surface for β-BBO patterning increased with increasing laser power, e.g., D{sub max}∼100 μm at P=0.8 W, D{sub max}∼170 μm at P=0.9 W, and D{sub max}∼200 μm at P=1 W. The present study proposes that the laser-induced crystallization opens a new door for applied engineering in glassy solids. - Graphical abstract: This figure shows the POM photographs for β-BaB{sub 2}O{sub 4} crystal lines patterned by cw Yb:YVO{sub 4} fiber laser irradiations with a laser power of P=0.8 W and a laser scanning speed S=2 μm/s in the glass. The laser focal point was moved gradually from the surface into the inside. The results shown in Fig. 1 demonstrate that it is possible to pattern highly oriented β-BaB{sub 2}O{sub 4} crystals even in the inside of glasses. - Highlights: • β-BaB{sub 2}O{sub 4} crystal lines were patterned in the inside of a glass by lasers. • Laser focal position was moved gradually from the surface to the inside. • Birefringence imaging was observed. • Morphology, size, and orientation of crystals were clarified. • Crystal lines with long lengths

  19. Optical cleaning of lithium niobate crystals

    International Nuclear Information System (INIS)

    Koesters, Michael

    2010-01-01

    An all-optical method for the removal of photoexcitable electrons from photorefractive centers to get rid of optical damage in lithium niobate crystals is presented, the so-called ''optical cleaning''. The method combines the photovoltaic drift of electrons with ionic charge compensation at sufficiently high temperatures of about 180 C. Optimum choice of the light pattern plus heat dramatically decreases the concentration of photoexcitable electrons in the exposed region leading to a suppression of optical damage. Experiments with slightly iron-doped lithium niobate crystals have shown an increase of the threshold for optical damage of more than 1000 compared to those of untreated crystals. (orig.)

  20. Aspiration of Barium Contrast

    OpenAIRE

    Fuentes Santos, Cristina; Steen, Bárbara

    2014-01-01

    The aspiration of barium contrast is a rare complication that may occur during studies of the digestive tract. Barium is an inert material that can cause anywhere from an asymptomatic mechanical obstruction to serious symptoms of respiratory distress that can result in patient death. We present the case of a 79-year-old male patient in whom we observed the presence of contrast medium residue in the lung parenchyma as an incidental finding during hospitalization. When the patient’s medical fil...

  1. Catalytic oxidation of soot over alkaline niobates

    International Nuclear Information System (INIS)

    Pecchi, G.; Cabrera, B.; Buljan, A.; Delgado, E.J.; Gordon, A.L.; Jimenez, R.

    2013-01-01

    Highlights: ► No previous reported studies about alkaline niobates as catalysts for soot oxidation. ► NaNbO 3 and KNbO 3 perovskite-type oxides show lower activation energy than other lanthanoid perovskite-type oxides. ► The alkaline niobate does not show deactivation by metal loss. - Abstract: The lack of studies in the current literature about the assessment of alkaline niobates as catalysts for soot oxidation has motivated this research. In this study, the synthesis, characterization and assessment of alkaline metal niobates as catalysts for soot combustion are reported. The solids MNbO 3 (M = Li, Na, K, Rb) are synthesized by a citrate method, calcined at 450 °C, 550 °C, 650 °C, 750 °C, and characterized by AAS, N 2 adsorption, XRD, O 2 -TPD, FTIR and SEM. All the alkaline niobates show catalytic activity for soot combustion, and the activity depends basically on the nature of the alkaline metal and the calcination temperature. The highest catalytic activity, expressed as the temperature at which combustion of carbon black occurs at the maximum rate, is shown by KNbO 3 calcined at 650 °C. At this calcination temperature, the catalytic activity follows an order dependent on the atomic number, namely: KNbO 3 > NaNbO 3 > LiNbO 3 . The RbNbO 3 solid do not follow this trend presumably due to the perovskite structure was not reached. The highest catalytic activity shown by of KNbO 3 , despite the lower apparent activation energy of NaNbO 3 , stress the importance of the metal nature and suggests the hypothesis that K + ions are the active sites for soot combustion. It must be pointed out that alkaline niobate subjected to consecutive soot combustion cycles does not show deactivation by metal loss, due to the stabilization of the alkaline metal inside the perovskite structure.

  2. Optical cleaning of lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Koesters, Michael

    2010-01-15

    An all-optical method for the removal of photoexcitable electrons from photorefractive centers to get rid of optical damage in lithium niobate crystals is presented, the so-called ''optical cleaning''. The method combines the photovoltaic drift of electrons with ionic charge compensation at sufficiently high temperatures of about 180 C. Optimum choice of the light pattern plus heat dramatically decreases the concentration of photoexcitable electrons in the exposed region leading to a suppression of optical damage. Experiments with slightly iron-doped lithium niobate crystals have shown an increase of the threshold for optical damage of more than 1000 compared to those of untreated crystals. (orig.)

  3. Micro- and nanostructuration of lithium niobate

    International Nuclear Information System (INIS)

    Hartung, Holger

    2010-01-01

    In the framework of this thesis the application of the ion-beam-enhanced-etching (IBEE) technique for the fabrication of different optical elements, among these photonic crystals, in lithium niobate, was studied. The development of a mask technology fitted to the requirements of the IBEE technique as well as a simulation of the process were performed. Hereby the limitations of the technique in view on minimal structure sizes and structure quality were analyzed. In chapter 1 first the material lithium niobate with its properties and the structuration procedures studied hitherto in the literature is presented. Chapter 2 presents the functionality of the IBEE process and describes the studies on the application of IBEE in lithium niobate performed in the framework of this thesis. In chapter 3 the experimental conditions of all applied processes of the IBEE procedure, the processes used for the mask fabrication, as well all further applied methods and technologies are summarized. Chapter 4 deals with the mask fabrication. The requirements on the masks and the developments necessary for their fulfilment are studied. In chapter 5 the performed simulation of the irradiation, annealing, and etching process is described. This simulation makes the prediciton of the geometry of the components from the process parameters and vice versa the determination of parameters for the reaching of an optimal element geometry possible. In chapter 6 the application of the technique for the fabrication of photonic-crystal membranes and their optical characterization is described. Chapter 7 shows the fabrication of different waveguide and diffractive elements in lithium niobate by means of IBEE.

  4. Barium granuloma of the rectum: case report

    International Nuclear Information System (INIS)

    Kim, Dae Jin; Kim, Se Hyung; Jeoung, Ah Young; Lee, Kyoung Ho; Choi, Byung Ihn; Han, Joon Koo

    2003-01-01

    Barium granulomas usually occur after barium enema within 8 cm of the anal verge probably due to minute laceration of rectal wall by enema tip and extravasation of barium during barium enema. We report a case of barium granuloma of rectum in a 47-year-old man, who did not have history of barium enema. In rare instance, barium granuloma can occur without a history of barium enema and careful interpretation of radiologic image is essential to make a correct diagnosis

  5. Modeling and minimization of barium sulfate scale

    Science.gov (United States)

    Alan W. Rudie; Peter W. Hart

    2006-01-01

    The majority of the barium present in the pulping process exits the digester as barium carbonate. Barium carbonate dissolves in the bleach plant when the pH drops below 7 and, if barium and sulfate concentrations are too high, begins to precipitate as barium sulfate. Barium is difficult to control because a mill cannot avoid this carbonate-to-sulfate transition using...

  6. Aspiration of Barium Contrast

    Directory of Open Access Journals (Sweden)

    Cristina Fuentes Santos

    2014-01-01

    Full Text Available The aspiration of barium contrast is a rare complication that may occur during studies of the digestive tract. Barium is an inert material that can cause anywhere from an asymptomatic mechanical obstruction to serious symptoms of respiratory distress that can result in patient death. We present the case of a 79-year-old male patient in whom we observed the presence of contrast medium residue in the lung parenchyma as an incidental finding during hospitalization. When the patient’s medical file was reviewed, images were found of a barium swallow study that the patient had undergone months earlier, and we were able to observe the exact moment of the aspiration of the contrast material. The patient had been asymptomatic since the test.

  7. Observed Barium Emission Rates

    Science.gov (United States)

    Stenbaek-Nielsen, H. C.; Wescott, E. M.; Hallinan, T. J.

    1993-01-01

    The barium releases from the CRRES satellite have provided an opportunity for verifying theoretically calculated barium ion and neutral emission rates. Spectra of the five Caribbean releases in the summer of 1991 were taken with a spectrograph on board a U.S. Air Force jet aircraft. Because the line of sight release densities are not known, only relative rates could be obtained. The observed relative rates agree well with the theoretically calculated rates and, together with other observations, confirm the earlier detailed theoretical emission rates. The calculated emission rates can thus with good accuracy be used with photometric observations. It has been postulated that charge exchange between neutral barium and oxygen ions represents a significant source for ionization. If so. it should be associated with emissions at 4957.15 A and 5013.00 A, but these emissions were not detected.

  8. Lower GI Series (Barium Enema)

    Science.gov (United States)

    ... uses x-rays and a chalky liquid called barium to view your large intestine . The barium will make your large intestine more visible on ... single-contrast lower GI series, which uses only barium a double-contrast or air-contrast lower GI ...

  9. Tunable dielectric properties of Barium Magnesium Niobate (BMN) doped Barium Strontium Titanate (BST) thin films by magnetron sputtering

    Science.gov (United States)

    Alema, Fikadu; Reinholz, Aaron; Pokhodnya, Konstantin

    2013-03-01

    We report on the tunable dielectric properties of Mg and Nb co-doped Ba0.45Sr0.55TiO3 (BST) thin film prepared by the magnetron sputtering using BST target (pure and doped with BaMg0.33Nb0.67O3 (BMN)) on Pt/TiO2/SiO2/Al2O3 4'' wafers at 700 °C under oxygen atmosphere. The electrical measurements are conducted on 2432 metal-ferroelectric-metal capacitors using Pt as the top and bottom electrode. The crystalline structure, microstructure, and surface morphology of the films are analyzed and correlated to the films dielectric properties. The BMN doped and undoped BST films have shown tunabilities of 48% and 52%; and leakage current densities of 2.2x10-6 A/cm2 and 3.7x10-5 A/cm2, respectively at 0.5 MV/cm bias field. The results indicate that the BMN doped film exhibits a lower leakage current with no significant decrease in tunability. Due to similar electronegativity and ionic radii, it was suggested that both Mg2+ (accepter-type) and Nb5+ (donor-type) dopants substitutTi4+ ion in BST. The improvement in the film dielectric losses and leakage current with insignificant loss of tunability is attributed to the adversary effects of Mg2+ and Nb5+ in BST.

  10. Isotopic exchange reaction between barium ion and tri barium phosphate

    International Nuclear Information System (INIS)

    Bilgin, G.B.; Cetin, I.

    1982-01-01

    Heterogeneous exchange reaction of tri barium phosphate in barium chloride solution has been studied using 133 Ba as a tracer. The results show that the exchange fraction increases as barium chloride concentration increases for different mole ratio of the exchange ion on the solid surface and in the solution. The phenomenon was studied with respect to the previous treatment of the precipitate leading to different crystal sizes and the effect of reaction time. (author)

  11. Lithium in the barium stars

    International Nuclear Information System (INIS)

    Pinsonneault, M.H.; Sneden, C.

    1984-01-01

    New high-resolution spectra of the lithium resonance doublet have provided lithium abundances or upper limits for 26 classical and mild barium stars. The lithium lines always are present in the classical barium stars. Lithium abundances in these stars obey a trend with stellar masses consistent with that previously derived for ordinary K giants. This supports the notion that classical barium stars are post-core-He-flash or core-He-burning stars. Lithium contents in the mild barium stars, however, often are much smaller than those of the classical barium stars sometimes only upper limits may be determined. The cause for this difference is not easily understood, but may be related to more extensive mass loss by the mild barium stars. 45 references

  12. Micromachining Lithium Niobate for Rapid Prototyping of Resonant Biosensors

    International Nuclear Information System (INIS)

    Al-Shibaany, Zeyad Yousif Abdoon; Hedley, John; Huo, Dehong; Hu, Zhongxu

    2014-01-01

    Lithium niobate material is widely used in MEMS application due to its piezoelectric properties. This paper presents the micromachining process of lithium niobate to rapid prototype a resonant biosensor design. A high precision CNC machine was used to machine a sample of lithium niobate material at 5 different spindle speeds to find out the best conditions to machine this brittle material. A qualitative visual check of the surface was performed by using scanning electron microscopy, surface roughness was quantitatively investigated using an optical surface profiler and Raman spectroscopy to check the strain of the surface. Results show that the surface quality of the lithium niobate was significantly affected by the spindle speed with optimum conditions at 70k rpm giving a strained surface with 500 nm rms roughness

  13. Host Excitation-Induced Red Emission from Pr3+ in Strontium Barium Niobate Thin Film

    National Research Council Canada - National Science Library

    Liu, H

    2004-01-01

    .... At 10K, the main emission peak splits into four components. In addition, a broadband SBN-host luminescence was identified at 560 nm in the annealed sample, associated with the charge-transfer vibronic exciton...

  14. Dielectric properties of Ga{sub 2}O{sub 3}-doped barium iron niobate ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Sanjoom, Kachaporn [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, 50200 (Thailand); Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Sri Ayutthaya Road, Bangkok, 10400 (Thailand); Pengpat, Kamonpan; Eitssayeam, Sukum; Tunkasiri, Tawee [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai, 50200 (Thailand); Rujijanagul, Gobwute [Department of Physics and Materials Science, Faculty of Science, Chiang Mai University, Chiang Mai, 50200 (Thailand); Materials Science Research Center, Faculty of Science, Chiang Mai University, Chiang Mai, 50200 (Thailand); Thailand Center of Excellence in Physics, Commission on Higher Education, 328 Sri Ayutthaya Road, Bangkok, 10400 (Thailand)

    2014-08-15

    Ga-doped BaFe{sub 0.5}Nb{sub 0.5}O{sub 3} (Ba(Fe{sub 1-x}Ga{sub x}){sub 0.5}Nb{sub 0.5}O{sub 3}) ceramics were fabricated and their properties were investigated. All ceramics showed perovskite structure with cubic symmetry and the solubility of Ga in BFN ceramics had a limit at x = 0.2. Examination of the dielectric spectra indicated that all ceramic samples presented high dielectric constants that were frequency dependent. The x = 0.2 ceramic showed a very high dielectric constant (ε{sub r} > 240 000 at 1 kHz) while the x = 0.4 sample exhibited high thermal stability of dielectric constant with low loss tangent from room temperature (RT) to 100 C with ε{sub r} > 28 000 (at 1 kHz) when compared to other samples. By using a complex impedance analysis technique, bulk grain, grain boundary, and electrode response were found to affect the dielectric behavior that could be related to the Maxwell-Wagner polarization mechanism. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  15. Dielectric properties of Ga2O3-doped barium iron niobate ceramics

    International Nuclear Information System (INIS)

    Sanjoom, Kachaporn; Pengpat, Kamonpan; Eitssayeam, Sukum; Tunkasiri, Tawee; Rujijanagul, Gobwute

    2014-01-01

    Ga-doped BaFe 0.5 Nb 0.5 O 3 (Ba(Fe 1-x Ga x ) 0.5 Nb 0.5 O 3 ) ceramics were fabricated and their properties were investigated. All ceramics showed perovskite structure with cubic symmetry and the solubility of Ga in BFN ceramics had a limit at x = 0.2. Examination of the dielectric spectra indicated that all ceramic samples presented high dielectric constants that were frequency dependent. The x = 0.2 ceramic showed a very high dielectric constant (ε r > 240 000 at 1 kHz) while the x = 0.4 sample exhibited high thermal stability of dielectric constant with low loss tangent from room temperature (RT) to 100 C with ε r > 28 000 (at 1 kHz) when compared to other samples. By using a complex impedance analysis technique, bulk grain, grain boundary, and electrode response were found to affect the dielectric behavior that could be related to the Maxwell-Wagner polarization mechanism. (copyright 2014 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

  16. Fast polarization mechanisms in the uniaxial tungsten-bronze relaxor strontium barium niobate SBN-81

    Czech Academy of Sciences Publication Activity Database

    Buixaderas, Elena; Kadlec, Christelle; Kempa, Martin; Bovtun, Viktor; Savinov, Maxim; Bednyakov, Petr; Hlinka, Jiří; Dec, J.

    2017-01-01

    Roč. 7, Dec (2017), s. 1-11, č. článku 18034. ISSN 2045-2322 R&D Projects: GA ČR GA16-09142S; GA MŠk(CZ) LD15014 Institutional support: RVO:68378271 Keywords : relaxor * tungsten-bronzes * dielectric response * phonons * broad-band spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism OBOR OECD: Condensed matter physics (including formerly solid state physics, supercond.) Impact factor: 4.259, year: 2016

  17. Barium and radium radiopolarography

    International Nuclear Information System (INIS)

    Fourest, B.

    1979-01-01

    Radiopolarography has been applied to the study of two elements (barium and radium) which is difficult by classical polarography because of their strong electropositivity. Various parameters have been considered: nature, concentration and pH of supporting electrolyte. In any case of investigated mediums, the reduction to the metallic state reaction appeared to be reversible. An important variation of the barium half-wave potential E 1/2 with the ionic strength μ of the solution, imposed by LiCl used as supporting electrolyte, has been observed. It gives the possibility to estimate, for μ = 0, E 1/2 (Ba) = - 1.916 V/S.C.E. and E 1/2(Ra) = - 1.852 V/S.C.E. The values of barium and radium half wave potentials, obtained with a good accuracy in LiCl (or LiClO 4 ) 0.1 M medium, have been used to establish the amalgamation energy Δ 2 (M) of these elements. A linear variation of Δ 2 (M) with the metallic radius of the 2a elements has been obtained. On the other hand, by making the concentration of the complex forming agent (Cit 3- ) vary in the solution, we have a shift in the half wave potential from which we can deduce the stability constant of the complexe and its composition (BaCit - ; pK 1 =2). At last, nature and concentration of the supporting electrolyte (between 5.10 -2 M and 5M) have a determining influence on the extent of the polarogram plateau. This plateau is limited by an 'hollow effect' preceding the supporting electrolyte discharge. An interpretation of this effect is suggested which is based on the Stern model [fr

  18. Barium uranyl diphosphonates

    Energy Technology Data Exchange (ETDEWEB)

    Nelson, Anna-Gay D., E-mail: nelsoa@umich.edu [Department of Civil Engineering and Geological Sciences and Department of Chemistry and Biochemistry, University of Notre Dame, Notre Dame, IN 46556 (United States); Department of Earth and Environmental Sciences, University of Michigan, Ann Arbor, MI 48109-1005 (United States); Alekseev, Evgeny V. [Institute of Energy and Climate Research (IEK-6), Forschungszentrum Juelich Wilhelm-Johnen-Strasse, Juelich 52428 (Germany); Ewing, Rodney C. [Department of Earth and Environmental Sciences, University of Michigan, Ann Arbor, MI 48109-1005 (United States); Albrecht-Schmitt, Thomas E. [Department of Civil Engineering and Geological Sciences and Department of Chemistry and Biochemistry, University of Notre Dame, Notre Dame, IN 46556 (United States)

    2012-08-15

    Three Ba{sup 2+}/UO{sub 2}{sup 2+} methylenediphosphonates have been prepared from mild hydrothermal treatment of uranium trioxide, methylendiphosphonic acid (C1P2) with barium hydroxide octahydrate, barium iodate monohydrate, and small aliquots of HF at 200 Degree-Sign C. These compounds, Ba[UO{sub 2}[CH{sub 2}(PO{sub 3}){sub 2}]{center_dot}1.4H{sub 2}O (Ba-1), Ba{sub 3}[(UO{sub 2}){sub 4}(CH{sub 2}(PO{sub 3}){sub 2}){sub 2}F{sub 6}]{center_dot}6H{sub 2}O (Ba-2), and Ba{sub 2}[(UO{sub 2}){sub 2}(CH{sub 2}(PO{sub 3}){sub 2})F{sub 4}]{center_dot}5.75H{sub 2}O (Ba-3) all adopt layered structures based upon linear uranyl groups and disphosphonate molecules. Ba-2 and Ba-3 are similar in that they both have UO{sub 5}F{sub 2} pentagonal bipyramids that are bridged and chelated by the diphosphonate moiety into a two-dimensional zigzag anionic sheet (Ba-2) and a one-dimensional ribbon anionic chain (Ba-3). Ba-1, has a single crystallographically unique uranium metal center where the C1P2 ligand solely bridges to form [UO{sub 2}[CH{sub 2}(PO{sub 3}){sub 2}]{sup 2-} sheets. The interlayer space of the structures is occupied by Ba{sup 2+}, which, along with the fluoride ion, mediates the structure formed and maintains overall charge balance. - Graphical abstract: Illustration of the stacking of the layers in Ba{sub 3}[(UO{sub 2}){sub 4}(CH{sub 2}(PO{sub 3}){sub 2}){sub 2})F{sub 6}]{center_dot}6H{sub 2}O viewed along the c-axis. The structure is constructed from UO{sub 7} pentagonal bipyramidal units, U(1)O{sub 7}=gray, U(2)O{sub 7}=yellow, barium=blue, phosphorus=magenta, fluorine=green, oxygen=red, carbon=black, and hydrogen=light peach. Highlights: Black-Right-Pointing-Pointer The polymerization of the UO{sub 2}{sup 2+} sites to form uranyl dimers leads to structural variations in compounds. Black-Right-Pointing-Pointer Barium cations stitch uranyl diphosphonate anionic layers together, and help mediate structure formation. Black-Right-Pointing-Pointer HF acts as both a

  19. Barium toxicosis in a dog.

    Science.gov (United States)

    Adam, Fiona H; Noble, Peter J M; Swift, Simon T; Higgins, Brent M; Sieniawska, Christine E

    2010-09-01

    A 2-year-old 14.9-kg (32.8-lb) neutered female Shetland Sheepdog was admitted to the University of Liverpool Small Animal Teaching Hospital for evaluation of acute collapse. At admission, the dog was tachypneic and had reduced limb reflexes and muscle tone in all limbs consistent with diffuse lower motor neuron dysfunction. The dog was severely hypokalemic (1.7 mEq/L; reference range, 3.5 to 5.8 mEq/L). Clinical status of the dog deteriorated; there was muscle twitching, flaccid paralysis, and respiratory failure, which was considered a result of respiratory muscle weakness. Ventricular arrhythmias and severe acidemia (pH, 7.18; reference range, 7.35 to 7.45) developed. Intoxication was suspected, and plasma and urine samples submitted for barium analysis had barium concentrations comparable with those reported in humans with barium toxicosis. Analysis of barium concentrations in 5 control dogs supported the diagnosis of barium toxicosis in the dog. Fluids and potassium supplementation were administered IV. The dog recovered rapidly. Electrolyte concentrations measured after recovery were consistently unremarkable. Quantification of plasma barium concentration 56 days after the presumed episode of intoxication revealed a large decrease; however, the plasma barium concentration remained elevated, compared with that in control dogs. To our knowledge, this case represented the first description of barium toxicosis in the veterinary literature. Barium toxicosis can cause life-threatening hypokalemia; however, prompt supportive treatment can yield excellent outcomes. Barium toxicosis is a rare but important differential diagnosis in animals with hypokalemia and appropriate clinical signs.

  20. On barium oxide solubility in barium-containing chloride melts

    International Nuclear Information System (INIS)

    Nikolaeva, Elena V.; Zakiryanova, Irina D.; Bovet, Andrey L.; Korzun, Iraida V.

    2016-01-01

    Oxide solubility in chloride melts depends on temperature and composition of molten solvent. The solubility of barium oxide in the solvents with barium chloride content is essentially higher than that in molten alkali chlorides. Spectral data demonstrate the existence of oxychloride ionic groupings in such melts. This work presents the results of the BaO solubility in two molten BaCl 2 -NaCl systems with different barium chloride content. The received data together with earlier published results revealed the main regularities of BaO solubility in molten BaO-BaCl 2 -MCl systems.

  1. Enhancement of Lithium Niobate nanophotonic structures via spin-coating technique for optical waveguides application

    Directory of Open Access Journals (Sweden)

    Fakhri Makram A.

    2017-01-01

    Full Text Available This work is dedicated to investigation of temperature effects in Lithium Niobate (LiNbO3 nanostructures. The LiNbO3 nanostructures were deposited on glass substrate by spin-coating technique. LiNbO3 was set down at 3000 rpm for 30 sec and annealed from 100 to 600 °C. The structures were characterized and analyzed by scanning electron microscopy (SEM and ultra-violet visible (UV-vis spectrophotometer. The measured results have showed that by increasing annealing temperatures, the structures start to be more crystallized and be more homogenized until the optimum arrangement was achieved. Once this was accomplished, it's applicable for optical waveguides development. Eventually, it starts to be less crystallization and non-homogeneous. Energy gap was recorded to be at average value of 3.9 eV.

  2. MR Colonography with fecal tagging: Barium vs. barium ferumoxsil

    DEFF Research Database (Denmark)

    Achiam, M.P.; Chabanova, E.; Logager, V.B.

    2008-01-01

    and Methods. Twenty patients referred to CC underwent dark lumen MRC prior to the colonoscopy. Two groups of patients received two different oral contrast agents (barium sulfate and barium sulfate/ferumoxsil) as a laxative-free fecal tagging prior to the MRC. After MRC, the contrast agent was rated...... qualitatively (with the standard method using contrast-to-wall ratio) and subjectively (using a visual analog scale [VAS]) by three different blinded observers. Results. Evaluated both qualitatively and subjectively, the tagging efficiency of barium sulfate/ferumoxsil was significantly better (P ... barium sulfate alone. The VAS method for evaluating the tagging efficiency of contrast agents showed a high correlation (observer 11, r = 0.91) to the standard method using contrast-to-wall ratio and also a high interclass correlation (observer 11 and III = 0.89/0.85). MRC found I of 22 (5%) polyps

  3. Stability of lithium niobate on irradiation at elevated temperature

    International Nuclear Information System (INIS)

    Primak, W.; Gavin, A.P.; Anderson, T.T.; Monahan, E.

    1977-01-01

    In contrast to results obtained for neutron irradiation in a thermal reactor near room temperature, lithium niobate plates irradiated in the Experimental Breeder Reactor II (EBR-II) did not become metamict. This is attributed to the elevated temperature of the EBR-II. Ion bombardment experiments indicate that to avoid disordering of lithium niobate on irradiation, its temperature should be maintained above 673 K. Evidence for ionic conductivity was found at 873 K, indicating that it would be inadvisable to permit the temperature to rise that high, particularly with voltage across the plate. In reactor application as a microphone transducer, it is tentatively recommended that the lithium niobate be maintained in the middle of this temperature range for a major portion of reactor operating time

  4. Barium aluminate cement: its application

    International Nuclear Information System (INIS)

    Drozdz, M.; Wolek, W.

    1975-01-01

    The technology of manufacturing barium aluminate cement from barium sulfate and alumina, using a rotary kiln for firing the clinker is described. The method of granulation of the homogenized charge was used. Conditions of using the ''to mud'' method in industry were indicated. The physical and chemical properties of barium aluminate cement are determined and the quality of several batches of cement prepared on a semi-industrial scale and their suitability for making highly refractory concretes are tested. The optimal composition of the concretes is determined as a function of the mixing water and barium aluminate cement contents. Several experimental batches of concretes were used in the linings of furnaces in the steel industry. The suitability of these cements for use in fields other than steelmaking is examined. It is established that calcium aluminate cement has certain limited applications [fr

  5. Statistical properties of barium stars

    International Nuclear Information System (INIS)

    Hakkila, J.E.

    1986-01-01

    Barium stars are G- and K-giant stars with atmospheric excesses of s-process elements, and a broadband spectral depression in the blue portion of the spectrum. The strength of the λ4554 Ball line is used as a classification parameter known as the Barium Intensity. They have a mean absolute magnitude of 1.0 and a dispersion of 1.2 magnitudes (assuming a Gaussian distribution in absolute magnitude) as measured from secular and statistical parallaxes. These stars apparently belong to a young-disk population from analyses of both the solar reflex motion and their residual velocity distribution, which implies that they have an upper mass limit of around three solar masses. There is no apparent correlation of barium intensity with either luminosity or kinematic properties. The barium stars appear to be preferentially distributed in the direction of the local spiral arm, but show no preference to associate with or avoid the direction of the galactic center. They do not appear related to either the carbon or S-stars because of these tendencies and because of the stellar population to which each type of star belongs. The distribution in absolute magnitude combined with star count analyses implies that these stars are slightly less numerous than previously believed. Barium stars show infrared excesses that correlate with their barium intensities

  6. Barium light source method and apparatus

    Science.gov (United States)

    Curry, John J. (Inventor); MacDonagh-Dumler, Jeffrey (Inventor); Anderson, Heidi M. (Inventor); Lawler, James E. (Inventor)

    2002-01-01

    Visible light emission is obtained from a plasma containing elemental barium including neutral barium atoms and barium ion species. Neutral barium provides a strong green light emission in the center of the visible spectrum with a highly efficient conversion of electrical energy into visible light. By the selective excitation of barium ionic species, emission of visible light at longer and shorter wavelengths can be obtained simultaneously with the green emission from neutral barium, effectively providing light that is visually perceived as white. A discharge vessel contains the elemental barium and a buffer gas fill therein, and a discharge inducer is utilized to induce a desired discharge temperature and barium vapor pressure therein to produce from the barium vapor a visible light emission. The discharge can be induced utilizing a glow discharge between electrodes in the discharge vessel as well as by inductively or capacitively coupling RF energy into the plasma within the discharge vessel.

  7. Barium and iron abundances in red giants

    International Nuclear Information System (INIS)

    Fernandez-Villacanas, J.L.; Rego, M.; Cornide, M.

    1990-01-01

    An intermediate-dispersion abundance analysis has been carried out on a sample of 21 barium and 14 comparison stars. The excess of barium over iron has been used as the most representative indicator of peculiarity. These excesses are higher in the peculiar stars than in the nonpeculiar stars. Particularly interesting is the case of HD 67447, included in the comparison stars, with an excess Ba/Fe abundance = 1.61, probably a new barium star. A trend indicating a possible anticorrelation between barium overabundance and metallicity favors the suggestion that the barium strong group is older than the barium weak one. 36 refs

  8. Sub-band-gap laser micromachining of lithium niobate

    DEFF Research Database (Denmark)

    Christensen, F. K.; Müllenborn, Matthias

    1995-01-01

    method is reported which enables us to do laser processing of lithium niobate using sub-band-gap photons. Using high scan speeds, moderate power densities, and sub-band-gap photon energies results in volume removal rates in excess of 106µm3/s. This enables fast micromachining of small piezoelectric...

  9. The use of one-dimensional Niobate to improve MgH{sub 2} hydrogen sorption

    Energy Technology Data Exchange (ETDEWEB)

    Brum, M.C., E-mail: mbrum@metalmat.ufrj.br; Conceição, M.O.T. da; Jardim, P.M.; Santos, D.S. dos

    2014-12-05

    Highlights: • The 1-D Niobate W and Niobate C catalysts were synthesized. • The composites MgH{sub 2} + 5 wt.% catalysts were obtained by 20 min of mechanical milling. • The synthesized wired-like material 1-D Niobate W showed to be a promising catalyst. • A desorption capacity of 6.0 wt.%. of H{sub 2} was attained in 10 min with MgH{sub 2} + 5 wt.% 1-D Niobate W. - Abstract: A study was performed on the hydrogen absorption/desorption properties of MgH{sub 2} with the addition of Niobates synthesized by hydrothermal treatment of Nb{sub 2}O{sub 5} in 10 M NaOH. Scanning Electron Microscopy (SEM) and X-ray diffraction (XRD) were used to evaluate their synthesis and show the morphological and crystallographic differences between Nb{sub 2}O{sub 5} used as a precursor and the Niobates produced, the one-dimensional wired type, 1-D Niobate W and the cuboid one, Niobate C. The ball milling of MgH{sub 2} with the Niobates was performed within only 20 min and afterwards the Differential Scanning Calorimetry (DSC) examination of MgH{sub 2} + 1-D Niobate W and MgH{sub 2} + Niobate C showed the shifting of the peaks for both composites in comparison to pure MgH{sub 2}. The influence of the two different types of Niobates and also the Nb{sub 2}O{sub 5} on the hydrogen absorption/desorption capacity was evaluated at 350 °C. The higher absorption and desorption values were attained by the MgH{sub 2} + 5 wt.% 1-D Niobate W composite, reaching, in 10 min, approximately 5.0 wt.% and 6.0 wt.%, respectively. The possible mechanism involved in such property improvement upon adding niobium based catalysts with different morphology and structure was discussed.

  10. Effect of SiO2/B2O3 Ratio on the Crystallization Behavior and Dielectric Properties of Barium Strontium Titanate Glass-Ceramics Prepared by Sol-Gel Process

    Science.gov (United States)

    Chen, Yongzhou; Zhang, Yong; Song, Xiaozhen; Shen, Ziqin; Zhang, Tianyuan

    2018-05-01

    Ferroelectric glass-ceramics, with a basic composition 90 wt.% (Ba0.65Sr0.35)TiO3-10 wt.% (B2O3-nSiO2) (n = 0.5, 1, 3, 5) were synthesized by the sol-gel method and their phase development and dielectric properties were investigated by differential thermal analysis, x-ray diffraction, field emission scanning electron microscopy, dielectric temperature curves and impedance spectroscopy. From the differential thermal analysis, glass transition and crystallization behavior can be observed. From the x-ray diffraction study, two crystalline phases (Ba,Sr)TiO3 and Ba2TiSi2O8 were formed over the entire composition range of the glass-ceramics. In addition, the main crystal phase has undergone a transformation from (Ba,Sr)TiO3 to Ba2TiSi2O8 with the increase of n. A typical structure in which the crystal phase was surrounded by a glassy matrix has been observed in the scanning electron microscope images. As a result of temperature dependent dielectric property measurements, the dielectric constant increased obviously with the increase of n from 0.5 to 1. Further increasing n led to a reduction of the dielectric constant, which is in coincidence with the variation of the intensity of (Ba,Sr)TiO3 phase with n. According to the impedance spectroscopy analysis and the activation energy calculation, the relaxation peak in both Z″ and M″ data should be attributed to the crystal-glass interface, and the change of conduction mechanism with the increase of SiO2/B2O3 ratio may be attributed to the corresponding transition of the main crystal phase.

  11. Dielectric properties and vacancy-like defects in plasma-sprayed barium titanate.

    Czech Academy of Sciences Publication Activity Database

    Ctibor, Pavel; Čížek, J.; Sedláček, J.; Lukáč, František

    2017-01-01

    Roč. 100, č. 7 (2017), s. 2972-2983 ISSN 0002-7820 Institutional support: RVO:61389021 Keywords : barium titanate * plasma spraying * vacancies Subject RIV: JH - Ceramic s, Fire-Resistant Materials and Glass OBOR OECD: Ceramic s Impact factor: 2.841, year: 2016

  12. Barium titanate nanocomposite capacitor FY09 year end report.

    Energy Technology Data Exchange (ETDEWEB)

    Stevens, Tyler E.; DiAntonio, Christopher Brian; Yang, Pin; Chavez, Tom P.; Winter, Michael R.; Monson, Todd C.; Roesler, Alexander William; Fellows, Benjamin D.

    2009-11-01

    This late start RTBF project started the development of barium titanate (BTO)/glass nanocomposite capacitors for future and emerging energy storage applications. The long term goal of this work is to decrease the size, weight, and cost of ceramic capacitors while increasing their reliability. Ceramic-based nanocomposites have the potential to yield materials with enhanced permittivity, breakdown strength (BDS), and reduced strain, which can increase the energy density of capacitors and increase their shot life. Composites of BTO in glass will limit grain growth during device fabrication (preserving nanoparticle grain size and enhanced properties), resulting in devices with improved density, permittivity, BDS, and shot life. BTO will eliminate the issues associated with Pb toxicity and volatility as well as the variation in energy storage vs. temperature of PZT based devices. During the last six months of FY09 this work focused on developing syntheses for BTO nanoparticles and firing profiles for sintering BTO/glass composite capacitors.

  13. Nonlinear optical oscillation dynamics in high-Q lithium niobate microresonators.

    Science.gov (United States)

    Sun, Xuan; Liang, Hanxiao; Luo, Rui; Jiang, Wei C; Zhang, Xi-Cheng; Lin, Qiang

    2017-06-12

    Recent advance of lithium niobate microphotonic devices enables the exploration of intriguing nonlinear optical effects. We show complex nonlinear oscillation dynamics in high-Q lithium niobate microresonators that results from unique competition between the thermo-optic nonlinearity and the photorefractive effect, distinctive to other device systems and mechanisms ever reported. The observed phenomena are well described by our theory. This exploration helps understand the nonlinear optical behavior of high-Q lithium niobate microphotonic devices which would be crucial for future application of on-chip nonlinear lithium niobate photonics.

  14. Patient dose variation investigated in four Irish hospitals for barium meal and barium enema examinations

    International Nuclear Information System (INIS)

    Carroll, E.; Brennan, P.C.

    2001-01-01

    Four hospitals have been studied, intra- and inter-hospital variations examined and the mean DAP values recorded for barium enemas and barium meals. Mean DAP values for barium meals and barium enemas at 11.4 Gy.cm 2 and 20.1 Gy.cm 2 respectively have been shown. Differences between individual examinations for barium meals varied by up to a factor of 185 and for barium enemas, up to a factor of 19, with hospital means for barium meal and enema examinations each differing by up to a factor of 3. The data provided by this study have suggested that large variations in patient dose do exist in Ireland for barium meal and barium enema examinations. Fluoroscopy time was shown to be a major contributor to the variations reported, with number of images playing a minor role. Results have demonstrated the need for standardisation of technique throughout the country for these examinations. (author)

  15. Photorefractive effect at 775 nm in doped lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Nava, G.; Minzioni, P.; Cristiani, I.; Degiorgio, V. [Department of Electrical, Computer, and Biomedical Engineering, and CNISM, University of Pavia, 27100 Pavia (Italy); Argiolas, N.; Bazzan, M.; Ciampolillo, M. V.; Pozza, G.; Sada, C. [Physics and Astronomy Departement, University of Padova, 35131 Padova (Italy)

    2013-07-15

    The photorefractive effect induced by 775-nm laser light on doped lithium niobate crystals is investigated by the direct observation in the far field of the transmitted-beam distortion as a function of time. Measurements performed at various Zr-doping concentrations and different light intensities show that the 775-nm light beam induces a steady-state photorefractive effect comparable to that of 532-nm light, but the observed build-up time of the photovoltaic field is longer by three-orders of magnitude. The 775-nm photorefractivity of lithium niobate crystals doped with 3 mol. % ZrO{sub 2} or with 5.5 mol. % MgO is found to be negligible.

  16. Optical waveguides in lithium niobate: Recent developments and applications

    Energy Technology Data Exchange (ETDEWEB)

    Bazzan, Marco, E-mail: marco.bazzan@unipd.it; Sada, Cinzia, E-mail: cinzia.sada@unipd.it [Dipartimento di Fisica e Astronomia “G. Galilei,” Università di Padova, Via Marzolo 8, 35131 Padova (Italy)

    2015-12-15

    The state of the art of optical waveguide fabrication in lithium niobate is reviewed, with particular emphasis on new technologies and recent applications. The attention is mainly devoted to recently developed fabrication methods, such as femtosecond laser writing, ion implantation, and smart cut waveguides as well as to the realization of waveguides with tailored functionalities, such as photorefractive or domain engineered structures. More exotic systems, such as reconfigurable and photorefractive soliton waveguides, are also considered. Classical techniques, such as Ti in-diffusion and proton exchange, are cited and briefly reviewed as a reference standpoint to highlight the recent developments. In all cases, the application-oriented point of view is preferred, in order to provide the reader with an up-to date panorama of the vast possibilities offered by lithium niobate to integrated photonics.

  17. Shock-induced luminescence from Z-cut lithium niobate

    International Nuclear Information System (INIS)

    Brannon, P.J.; Morris, R.W.; Asay, J.R.

    1985-01-01

    Shock-induced luminescence from lithium niobate has been studied in the stress range 1.6--21.0 GPa. Both fast-framing photography and five-channel optical pyrometry were used to observe the luminescence. The framing photography showed that the emission pattern is heterogeneous for stresses just above the dynamic yield point. A further increase of the stress resulted in a pattern which was essentially homogeneous to within the experimental spatial resolution of about 30 μm. Narrowband filters and photomultiplier tubes were used in the optical pyrometry experiments. A broadband spectrum with a peak near 700 nm was observed. A plot of the energy dissipated by the shock versus shock stress correlates very well with a plot of the 700-nm intensity versus shock stress. The mechanism for light emission in lithium niobate appears to be closely related to the dynamic yielding process

  18. Erbium ion implantation into different crystallographic cuts of lithium niobate

    Czech Academy of Sciences Publication Activity Database

    Nekvindová, P.; Švecová, B.; Cajzl, J.; Macková, Anna; Malinský, Petr; Oswald, Jiří; Kolitsch, A.; Špirková, J.

    2012-01-01

    Roč. 34, č. 4 (2012), s. 652-659 ISSN 0925-3467 R&D Projects: GA MŠk(CZ) LC06041; GA ČR GA106/09/0125; GA ČR(CZ) GAP106/10/1477 Institutional research plan: CEZ:AV0Z10480505; CEZ:AV0Z10100521 Keywords : Lithium niobate * Erbium * Ion implantation * Luminescence Subject RIV: BH - Optics, Masers, Lasers Impact factor: 1.918, year: 2012

  19. Lithium niobate ultrasonic transducer design for Enhanced Oil Recovery.

    Science.gov (United States)

    Wang, Zhenjun; Xu, Yuanming; Gu, Yuting

    2015-11-01

    Due to the strong piezoelectric effect possessed by lithium niobate, a new idea that uses lithium niobate to design high-power ultrasonic transducer for Enhanced Oil Recovery technology is proposed. The purpose of this paper is to lay the foundation for the further research and development of high-power ultrasonic oil production technique. The main contents of this paper are as follows: firstly, structure design technique and application of a new high-power ultrasonic transducer are introduced; secondly, the experiment for reducing the viscosity of super heavy oil by this transducer is done, the optimum ultrasonic parameters for reducing the viscosity of super heavy oil are given. Experimental results show that heavy large molecules in super heavy oil can be cracked into light hydrocarbon substances under strong cavitation effect caused by high-intensity ultrasonic wave. Experiment proves that it is indeed feasible to design high-power ultrasonic transducer for ultrasonic oil production technology using lithium niobate. Copyright © 2015 Elsevier B.V. All rights reserved.

  20. CT-Guided Percutaneous Transthoracic Localization of Pulmonary Nodules Prior to Video-Assisted Thoracoscopic Surgery Using Barium Suspension

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Nyoung Keun; Park, Chang Min; Kang, Chang Hyun; Jeon, Yoon Kyung; Choo, Ji Yung; Lee, Hyun Ju; Goo, Jin Mo [Seoul National University College of Medicine, Seoul (Korea, Republic of)

    2012-11-15

    To describe our initial experience with CT-guided percutaneous barium marking for the localization of small pulmonary nodules prior to video-assisted thoracoscopic surgery (VATS). From October 2010 to April 2011, 10 consecutive patients (4 men and 6 women; mean age, 60 years) underwent CT-guided percutaneous barium marking for the localization of 10 small pulmonary nodules (mean size, 7.6 mm; range, 3-14 mm): 6 pure ground-glass nodules, 3 part-solid nodules, and 1 solid nodule. A 140% barium sulfate suspension (mean amount, 0.2 mL; range, 0.15-0.25 mL) was injected around the nodules with a 21-gauge needle. The technical details, surgical findings and pathologic features associated with barium localizations were evaluated. All nodules were marked within 3 mm (mean distance, 1.1 mm; range, 0-3 mm) from the barium ball (mean diameter, 9.6 mm; range, 8-16 mm) formed by the injected barium suspension. Pneumothorax occurred in two cases, for which one needed aspiration. However, there were no other complications. All barium balls were palpable during VATS and visible on intraoperative fluoroscopy, and were completely resected. Both the whitish barium balls and target nodules were identifiable in the frozen specimens. Pathology revealed one invasive adenocarcinoma, five adenocarcinoma-in-situ, two atypical adenomatous hyperplasias, and two benign lesions. In all cases, there were acute inflammations around the barium balls which did not hamper the histological diagnosis of the nodules. CT-guided percutaneous barium marking can be an effective, convenient and safe pre-operative localization procedure prior to VATS, enabling accurate resection and diagnosis of small or faint pulmonary nodules.

  1. CT-Guided Percutaneous Transthoracic Localization of Pulmonary Nodules Prior to Video-Assisted Thoracoscopic Surgery Using Barium Suspension

    International Nuclear Information System (INIS)

    Lee, Nyoung Keun; Park, Chang Min; Kang, Chang Hyun; Jeon, Yoon Kyung; Choo, Ji Yung; Lee, Hyun Ju; Goo, Jin Mo

    2012-01-01

    To describe our initial experience with CT-guided percutaneous barium marking for the localization of small pulmonary nodules prior to video-assisted thoracoscopic surgery (VATS). From October 2010 to April 2011, 10 consecutive patients (4 men and 6 women; mean age, 60 years) underwent CT-guided percutaneous barium marking for the localization of 10 small pulmonary nodules (mean size, 7.6 mm; range, 3-14 mm): 6 pure ground-glass nodules, 3 part-solid nodules, and 1 solid nodule. A 140% barium sulfate suspension (mean amount, 0.2 mL; range, 0.15-0.25 mL) was injected around the nodules with a 21-gauge needle. The technical details, surgical findings and pathologic features associated with barium localizations were evaluated. All nodules were marked within 3 mm (mean distance, 1.1 mm; range, 0-3 mm) from the barium ball (mean diameter, 9.6 mm; range, 8-16 mm) formed by the injected barium suspension. Pneumothorax occurred in two cases, for which one needed aspiration. However, there were no other complications. All barium balls were palpable during VATS and visible on intraoperative fluoroscopy, and were completely resected. Both the whitish barium balls and target nodules were identifiable in the frozen specimens. Pathology revealed one invasive adenocarcinoma, five adenocarcinoma-in-situ, two atypical adenomatous hyperplasias, and two benign lesions. In all cases, there were acute inflammations around the barium balls which did not hamper the histological diagnosis of the nodules. CT-guided percutaneous barium marking can be an effective, convenient and safe pre-operative localization procedure prior to VATS, enabling accurate resection and diagnosis of small or faint pulmonary nodules.

  2. STRESS RELAXATION CHARACTERISTICS OF SELECTED COMMERCIALLY PRODUCED GLASSES

    Directory of Open Access Journals (Sweden)

    Chocholoušek J.

    2013-06-01

    Full Text Available This paper describes a quantitative method of stress relaxation measurement in prismatic glass samples during two different time-temperature regimes using the Sénarmont compensator. Four types of glass (Barium crystal glass, Eutal, Simax, and Container glass were subjected to observation in an assembled measuring device. Results will be used for parameterization of the Tool-Narayanaswamy-Mazurin model and consequently implemented in a finite element method code.

  3. Barium aspiration and alveolarisation of barium in an infant: A case report and review of management

    Directory of Open Access Journals (Sweden)

    Alan F. Isles

    2014-05-01

    Full Text Available We describe a case of bilateral inhalation and alveolarisation of barium in an infant following a barium swallow for investigation of dusky spells associated with feeds. A bronchoscopy subsequently revealed the presence of a mid-tracheal tracheo-oesophageal cleft. We review the literature on barium aspiration, its consequences and make recommendations for management.

  4. Label-free investigation of the effects of lithium niobate polarization on cell adhesion

    Science.gov (United States)

    Mandracchia, B.; Gennari, O.; Paturzo, M.; Grilli, S.; Ferraro, P.

    2017-06-01

    The determination of contact area is pivotal to understand how biomaterials properties influence cell adhesion. In particular, the influence of surface charges is well-known but still controversial, especially when new functional materials and methods are introduced. Here, we use for the first time Holographic Total Internal Reflection Microscopy (HoloTIRM) to study the influence of the spontaneous polarization of ferroelectric lithium niobate (LN) on the adhesion properties of fibroblast cells. The selective illumination of a very thin region directly above the substrate, achieved by Total Internal Reflection, provides high-contrast images of the contact regions. Holographic recording, on the other hand, allows for label-free quantitative phase imaging of the contact areas between cells and LN. Phase signal is more sensitive in the first 100nm and, thus more reliable in order to locate focal contacts. This work shows that cells adhering on negatively polarized LN present a significant increase of the contact area in comparison with cells adhering on the positively polarized LN substrate, as well as an intensification of contact vicinity. This confirms the potential of LN as a platform for investigating the role of charges on cellular processes. The similarity of cell adhesion behavior on negatively polarized LN and glass control also confirms the possibility to use LN as an active substrate without impairing cell behavior.

  5. Barium Depletion in Hollow Cathode Emitters

    Science.gov (United States)

    Polk, James E.; Capece, Angela M.; Mikellides, Ioannis G.; Katz, Ira

    2009-01-01

    The effect of tungsten erosion, transport and redeposition on the operation of dispenser hollow cathodes was investigated in detailed examinations of the discharge cathode inserts from an 8200 hour and a 30,352 hour ion engine wear test. Erosion and subsequent re-deposition of tungsten in the electron emission zone at the downstream end of the insert reduces the porosity of the tungsten matrix, preventing the ow of barium from the interior. This inhibits the interfacial reactions of the barium-calcium-aluminate impregnant with the tungsten in the pores. A numerical model of barium transport in the internal xenon discharge plasma shows that the barium required to reduce the work function in the emission zone can be supplied from upstream through the gas phase. Barium that flows out of the pores of the tungsten insert is rapidly ionized in the xenon discharge and pushed back to the emitter surface by the electric field and drag from the xenon ion flow. This barium ion flux is sufficient to maintain a barium surface coverage at the downstream end greater than 0.6, even if local barium production at that point is inhibited by tungsten deposits. The model also shows that the neutral barium pressure exceeds the equilibrium vapor pressure of the impregnant decomposition reaction over much of the insert length, so the reactions are suppressed. Only a small region upstream of the zone blocked by tungsten deposits is active and supplies the required barium. These results indicate that hollow cathode failure models based on barium depletion rates in vacuum dispenser cathodes are very conservative.

  6. Domain wall width of lithium niobate poled during growth

    CERN Document Server

    Brooks, R; Hole, D E; Callejo, D; Bermudez, V; Diéguez, E

    2003-01-01

    Good quality crystals of periodically poled lithium niobate can be generated directly during growth. However, the temperature gradients at the zone boundaries define the width of the regions where the polarity is reversed. Hence, the region influenced the domain transition may be a significant fraction of the overall poling period for material poled during growth. Evidence for the scale of this feature is reported both by chemical etching and by the less common method of ion beam luminescence and the 'domain wall' width approximately 1 mu m for these analyses. The influence of the reversal region may differ for alternative techniques but the relevance to device design for second harmonic generation is noted.

  7. Photoluminescence of Copper-Doped Lithium Niobate Crystals

    Science.gov (United States)

    Gorelik, V. S.; Pyatyshev, A. Yu.; Sidorov, N. V.

    2018-05-01

    The photoluminescence (PL) of copper-doped lithium niobate single crystals is studied using different UV-Vis light-emitting diodes and a pulse-periodic laser with a wavelength of 266 nm as excitation radiation sources. With the resonance excitation from a 527-nm light-emitting diode, the intensity of PL increases sharply (by two orders of magnitude). When using a 467-nm light-emitting diode for excitation, the PL spectrum is characterized by the presence of multiphonon lines in the range of 520-620 nm.

  8. Dynamical symmetry breaking in barium isotopes

    International Nuclear Information System (INIS)

    Rawat, Bir Singh; Chattopadhyay, P.K.

    1997-01-01

    The isotopes of Xe with mass numbers 124, 126, 128, 130 and the isotopes of barium with mass numbers 128, 130, 132, 134 were shown to correspond to the O(6) dynamical symmetry of IBM. In the investigation of the dynamical symmetry breaking in this region, the barium isotopes for departures from O(6) symmetry have been studied

  9. Laser cooling and trapping of barium

    NARCIS (Netherlands)

    De, Subhadeep

    2008-01-01

    Laser cooling and trapping of heavy alkaline-earth element barium have been demonstrated for the first time ever. For any possible cycling transition in barium that could provide strong cooling forces, the excited state has a very large branching probability to metastable states. Additional lasers

  10. Analysis of barium by isotope mass spectrometry

    International Nuclear Information System (INIS)

    Long Kaiming; Jia Baoting; Liu Xuemei

    2004-01-01

    The isotopic abundance ratios for barium at sub-microgram level are analyzed by thermal surface ionization mass spectrometry (TIMS). Rhenium trips used for sample preparation are firstly treated to eliminate possible barium background interference. During the preparation of barium samples phosphoric acid is added as an emitting and stabilizing reagent. The addition of phosphoric acid increases the collection efficiency and ion current strength and stability for barium. A relative standard deviation of 0.02% for the isotopic abundance ratio of 137 Ba to 138 Ba is achieved when the 138 Ba ion current is (1-3) x 10 -12 A. The experimental results also demonstrate that the isotope fractionation effect is negligibly small in the isotopic analysis of barium

  11. Absorption and reflectivity of the lithium niobate surface masked with a graphene layer

    Directory of Open Access Journals (Sweden)

    O. Salas

    2017-01-01

    Full Text Available We performed simulations of the interaction of a graphene layer with the surface of lithium niobate utilizing density functional theory and molecular dynamics at 300K and atmospheric pressure. We found that the graphene layer is physisorbed on the lithium niobate surface with an adsorption energy of -0.8205 eV/(carbon-atom. Subsequently, the energy band structure, the optical absorption and reflectivity of the new system were calculated. We found important changes in these physical properties with respect to the corresponding ones of a graphene layer and of a lithium niobate crystal.

  12. Monolithic acoustic graphene transistors based on lithium niobate thin film

    Science.gov (United States)

    Liang, J.; Liu, B.-H.; Zhang, H.-X.; Zhang, H.; Zhang, M.-L.; Zhang, D.-H.; Pang, W.

    2018-05-01

    This paper introduces an on-chip acoustic graphene transistor based on lithium niobate thin film. The graphene transistor is embedded in a microelectromechanical systems (MEMS) acoustic wave device, and surface acoustic waves generated by the resonator induce a macroscopic current in the graphene due to the acousto-electric (AE) effect. The acoustic resonator and the graphene share the lithium niobate film, and a gate voltage is applied through the back side of the silicon substrate. The AE current induced by the Rayleigh and Sezawa modes was investigated, and the transistor outputs a larger current in the Rayleigh mode because of a larger coupling to velocity ratio. The output current increases linearly with the input radiofrequency power and can be effectively modulated by the gate voltage. The acoustic graphene transistor realized a five-fold enhancement in the output current at an optimum gate voltage, outperforming its counterpart with a DC input. The acoustic graphene transistor demonstrates a paradigm for more-than-Moore technology. By combining the benefits of MEMS and graphene circuits, it opens an avenue for various system-on-chip applications.

  13. Propagation characteristics of a focused laser beam in a strontium barium niobate photorefractive crystal under reverse external electric field.

    Science.gov (United States)

    Guo, Q L; Liang, B L; Wang, Y; Deng, G Y; Jiang, Y H; Zhang, S H; Fu, G S; Simmonds, P J

    2014-10-01

    The propagation characteristics of a focused laser beam in a SBN:75 photorefractive crystal strongly depend on the signal-to-background intensity ratio (R=Is/Ib) under reverse external electric field. In the range 20>R>0.05, the laser beam shows enhanced self-defocusing behavior with increasing external electric field, while it shows self-focusing in the range 0.03>R>0.01. Spatial solitons are observed under a suitable reverse external electric field for R=0.025. A theoretical model is proposed to explain the experimental observations, which suggest a new type of soliton formation due to "enhancement" not "screening" of the external electrical field.

  14. A new double contrast barium enema

    International Nuclear Information System (INIS)

    Park, Jun Sang; Cho, Won Sik; Lee, Sung Woo; Lee, Mun Gyu; Jeon, Jeong Dong; Jaun, Woo Ki; Han, Chung Yul

    1987-01-01

    A new technic of the barium enema was proposed for the better colonic double contrast study with the average 204ml of 50w/v% barium, applied to 109 serial patients. The barium was introduced to sigmoid colon, and then pushed to a mid transverse colon by the air insufflation through an enema syringe, a new device. An advance to cecum is accomplished by the air insufflation and/or the position change of the patient. The barium transfer method was developed for the best spot film exposure, through colon, by the position change of the patient, the tilting of the x-ray table and the air insufflation with the enema syringe. The mean angle of the x-ray table tilted was -10 .deg. at the beginning the barium enema till the barium sent past the splenic flexure, -15 . deg. for the best lateral view of rectum and -18 .deg. for the bet prone PA view of rectosigmoid colon. This was a simple, better and economic double contrast barium enema for the cooperative patients

  15. High insulation foam glass material from waste cathode ray tube panel glass

    DEFF Research Database (Denmark)

    König, Jakob; Petersen, Rasmus Rosenlund; Yue, Yuanzheng

    . In general CRT consists of two types of glasses: barium/strontium containing glass (panel glass) and lead containing glass (funnel and panel glass). In this work we present the possibility to produce high performance insulation material from the recycled lead-free glass. We studied the influence of foaming...... between 750 and 850°C. We investigated the influence of milling time, particle size, foaming and oxidizing agent concentrations, temperature and time on the foaming process, foam density, foam porosity and homogeneity. Only moderate foaming was observed in carbon containing samples, while the addition...... of the oxidizing agent greatly improved the foaming quality. The results showed that the amount of oxygen available from the glass is not sufficient to combust all of the added carbon, therefore, additional oxygen was supplied via manganese reduction. In general, a minimum in the foam glass density was observed...

  16. Nb 3d and O 1s core levels and chemical bonding in niobates

    International Nuclear Information System (INIS)

    Atuchin, V.V.; Kalabin, I.E.; Kesler, V.G.; Pervukhina, N.V.

    2005-01-01

    A set of available experimental data on binding energies of Nb 3d 5/2 and O 1s core levels in niobates has been observed with using energy difference (O 1s-Nb 3d 5/2 ) as a robust parameter for compound characterization. An empirical relationship between (O 1s-Nb 3d 5/2 ) values measured with XPS for Nb 5+ -niobates and mean chemical bond length L(Nb-O) has been discussed. A range of (O 1s-Nb 3d 5/2 ) values possible in Nb 5+ -niobates has been defined. An energy gap ∼1.4-1.8 eV is found between (O 1s-Nb 3d 5/2 ) values reasonable for Nb 5+ and Nb 4+ states in niobates

  17. Nb 3d and O 1s core levels and chemical bonding in niobates

    Energy Technology Data Exchange (ETDEWEB)

    Atuchin, V.V. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation)]. E-mail: atuchin@thermo.isp.nsc.ru; Kalabin, I.E. [Laboratory of Optical Materials and Structures, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Kesler, V.G. [Technical Center, Institute of Semiconductor Physics, SB RAS, Novosibirsk 630090 (Russian Federation); Pervukhina, N.V. [Laboratory of Crystal Chemistry, Institute of Inorganic Chemistry, SB RAS, Novosibirsk 630090 (Russian Federation)

    2005-02-01

    A set of available experimental data on binding energies of Nb 3d{sub 5/2} and O 1s core levels in niobates has been observed with using energy difference (O 1s-Nb 3d{sub 5/2}) as a robust parameter for compound characterization. An empirical relationship between (O 1s-Nb 3d{sub 5/2}) values measured with XPS for Nb{sup 5+}-niobates and mean chemical bond length L(Nb-O) has been discussed. A range of (O 1s-Nb 3d{sub 5/2}) values possible in Nb{sup 5+}-niobates has been defined. An energy gap {approx}1.4-1.8 eV is found between (O 1s-Nb 3d{sub 5/2}) values reasonable for Nb{sup 5+} and Nb{sup 4+} states in niobates.

  18. Rare-Earth Tantalates and Niobates Single Crystals: Promising Scintillators and Laser Materials

    Directory of Open Access Journals (Sweden)

    Renqin Dou

    2018-01-01

    Full Text Available Rare-earth tantalates, with high density and monoclinic structure, and niobates with monoclinic structure have been paid great attention as potential optical materials. In the last decade, we focused on the crystal growth technology of rare-earth tantalates and niobates and studied their luminescence and physical properties. A series of rare-earth tantalates and niobates crystals have been grown by the Czochralski method successfully. In this work, we summarize the research results on the crystal growth, scintillation, and laser properties of them, including the absorption and emission spectra, spectral parameters, energy levels structure, and so on. Most of the tantalates and niobates exhibit excellent luminescent properties, rich physical properties, and good chemical stability, indicating that they are potential outstanding scintillators and laser materials.

  19. Ridge Waveguide Structures in Magnesium-Doped Lithium Niobate, Phase I

    Data.gov (United States)

    National Aeronautics and Space Administration — In this NASA Phase I STTR effort, the feasibility of fabricating isolated ridge waveguides in 5% magnesium-doped lithium niobate (5% MgO:LN) will be established....

  20. Design considerations for quasi-phase-matching in doubly resonant lithium niobate hexagonal microresonators

    CSIR Research Space (South Africa)

    Sono, Tleyane J

    2017-08-01

    Full Text Available Fabrication capabilities of high optical quality hexagonal superstructures by chemical etching of inverted ferroelectric domains in lithium niobate platform suggests a route for efficient implementation of compact hexagonal microcavities...

  1. Double contrast barium meal and acetylcysteine

    International Nuclear Information System (INIS)

    Kinnunen, J.; Pietilae, J.; Ahovuo, J.; Mankinen, P.; Tervahartiala, P.

    1989-01-01

    In a prospective double blind study, acetylcysteine, a local and systemic respiratory tract mucolytic agent, or a placebo, were given to 100 patients prior to a double contrast barium meal to decrease the gastric mucus viscosity and to make the mucus layer thinner, in order to permit barium to outline the furrows surrounding the areae gastricae instead of the overlying thick mucus. However, acetylcysteine failed to improve either visualization of the areae gastricae or the general quality of the double contrast barium meal. (orig.)

  2. Atomization mechanisms for barium in furnace atomic absorption spectrometry

    International Nuclear Information System (INIS)

    Styris, D.L.

    1984-01-01

    Atomic absorption spectrometry and mass spectrometry are used simultaneously in order to elucidate atomization mechanisms of barium dichloride in pyrolytic graphite, vitreous carbon, and tantalum furnaces. Gas-phase barium dicarbide is observed to appear concurrently with the free barium. Barium oxide and barium dihydroxide precursors appear with the chlorides. Surface reactions involving species that are absorbed on the various furnaces are postulated to explain the appearances of the species that are observed in the gas phase. 49 references, 4 figures, 1 table

  3. Twinning structures in near-stoichiometric lithium niobate single crystals

    International Nuclear Information System (INIS)

    Yao, Shuhua; Chen, Yanfeng

    2010-01-01

    A near-stoichiometric lithium niobate single crystal has been grown by the Czochralski method in a hanging double crucible with a continuous powder supply system. Twins were found at one of the three characteristic growth ridges of the as-grown crystal. The twin structure was observed and analyzed by transmission synchrotron topography. The image shifts ΔX and ΔY in the transmission synchrotron topograph were calculated for the 3 anti 2 anti 12 and 0 anti 222 reflections based on results from high-resolution X-ray diffractometry. It is confirmed that one of the {01 anti 1 anti 2} m planes is the composition face of the twin and matrix crystals. The formation mechanism of these twins is discussed. (orig.)

  4. Integrated optics on Lithium Niobate for sensing applications

    Science.gov (United States)

    Zaltron, A.; Bettella, G.; Pozza, G.; Zamboni, R.; Ciampolillo, M.; Argiolas, N.; Sada, C.; Kroesen, S.; Esseling, M.; Denz, C.

    2015-05-01

    In micro-analytical chemistry and biology applications, optofluidic technology holds great promise for creating efficient lab-on-chip systems where higher levels of integration of different stages on the same platform is constantly addressed. Therefore, in this work the possibility of integrating opto-microfluidic functionalities in lithium niobate (LiNbO3) crystals is presented. In particular, a T-junction droplet generator is directly engraved in a LiNbO3 substrate by means of laser ablation process and optical waveguides are realized in the same material by exploiting the Titanium in-diffusion approach. The coupling of these two stages as well as the realization of holographic gratings in the same substrate will allow creating new compact optical sensor prototypes, where the optical properties of the droplets constituents can be monitored.

  5. Study of structural differences between stoichiometric and congruent lithium niobate

    CERN Document Server

    Kling, A; Correia, J G; Da Silva, M F A; Diéguez, E; Agulló-López, F; Soares, J C

    1996-01-01

    The structural differences between stoichiometric and congruent (lithium deficient) lithium niobate single crystals were studied by RBS- and NRA-channeling as well as perturbed angular correlation (PAC) measurements. The d-PAC111Cd-PAC investigations point out that a second Li site can be detected in congruent material, while only one is present in stoichiometric. Channeling studies of different axes and the comparison of the results with computer simulations corroborated former indications that this additional lattice site can be attributed to the formation of ilmenite type stacking faults. A comparative study of the energy dependence of the dechanneling showed that a remarkable disorder is also present in the Nb sublattice of the congruent crystals and that these defects have a point-like character.

  6. Photorefractive lithium niobate crystals for applications in photonics

    International Nuclear Information System (INIS)

    Hartwig, U.

    2006-12-01

    Lithium niobate crystals (LiNbO 3 ) generally show a photorefractive response, i.e., light-induced refractive index changes. Crystals are investigated at room temperature and at elevated temperatures. As a result 'classical' photorefractive holographic volume-phase gratings, originating from space charge fields and the electro-optic effect, and 'non-classical' photorefractive volume-phase gratings, which can be traced back to strong absorption gratings, emerge. Single domain and periodically poled crystals (PPLN) are investigated. PPLN is typically used in non-linear optics for frequency conversion. The crystals also show non-linear photorefractive response during holographic recording with isotropically polarized light beams of equal intensity and, in the case of PPLN, by mixing of domain and holographic gratings. The results are important for applications combining the photorefractive and non-linear optical properties of LiNbO 3 . (orig.)

  7. Fabrication and performance of porous lithium sodium potassium niobate ceramic

    Science.gov (United States)

    Chen, Caifeng; Zhu, Yuan; Ji, Jun; Cai, Feixiang; Zhang, Youming; Zhang, Ningyi; Wang, Andong

    2018-02-01

    Porous lithium sodium potassium niobate (LNK) ceramic has excellent piezoelectric properties, chemical stability and great chemical compatibility. It has a good application potential in the field of biological bone substitute. In the paper, porous LNK ceramic was fabricated with egg albumen foaming agent by foaming method. Effects of preparation process of the porous LNK ceramic on density, phase structure, hole size and piezoelectric properties were researched and characterized. The results show that the influence factors of LNK solid content and foaming agent addition are closely relevant to properties of the porous LNK ceramic. When solid content is 65% and foaming agent addition is 30%, the porous LNK ceramic has uniform holes and the best piezoelectric properties.

  8. Sealing glasses for titanium and titanium alloys

    Science.gov (United States)

    Brow, Richard K.; McCollister, Howard L.; Phifer, Carol C.; Day, Delbert E.

    1997-01-01

    Barium lanthanoborate sealing-glass compositions are provided comprising various combinations (in terms of mole-%) of boron oxide (B.sub.2 O.sub.3), barium oxide (BaO), lanthanum oxide (La.sub.2 O.sub.3), and at least one other oxide selected from the group consisting of aluminum oxide (Al.sub.2 O.sub.3), calcium oxide (CaO), lithium oxide (Li.sub.2 O), sodium oxide (Na.sub.2 O), silicon dioxide (SiO.sub.2), or titanium dioxide (TiO.sub.2). These sealing-glass compositions are useful for forming hermetic glass-to-metal seals with titanium and titanium alloys having an improved aqueous durability and favorable sealing characteristics. Examples of the sealing-glass compositions are provided having coefficients of thermal expansion about that of titanium or titanium alloys, and with sealing temperatures less than about 900.degree. C., and generally about 700.degree.-800.degree. C. The barium lanthanoborate sealing-glass compositions are useful for components and devices requiring prolonged exposure to moisture or water, and for implanted biomedical devices (e.g. batteries, pacemakers, defibrillators, pumps).

  9. Time requirement for barium reduction in intussusception

    International Nuclear Information System (INIS)

    Hwang, Hye Eun; Kim, Seung Ho; Kang, In Young; Park, Byoung Lan; Kim, Byoung Geun

    1988-01-01

    During the period between January 1985 and December 1987, barium reduction was performed in 146 cases of intussusception who were admitted to Kwangju Christian Hospital. The results were as follows: 1. Success rate to the symptom duration is relatively constant. 2. The success rate in infants with severe dehydration was 50% but it was gradually increased in infants with moderate dehydration and in infants with mild dehydration, 83.3% and 100% respectively. 3. The success rate of 12 cases in severely dehydrated infants with positive dissection sign was 16.7%. 4. The success rate of 15 cases in moderately dehydrated infants with positive dissection sign was 66.7%. 5. The average time requirement for barium reduction was 58.3 minutes. No serious complications were noted during barium reduction, except mild vomiting. 6. With above results, it is desirable that barium reduction should be performed according to the patient's physical status and radiologic findings.

  10. Barium Isotopes in Single Presolar Grains

    Science.gov (United States)

    Pellin, M. J.; Davis, A. M.; Savina, M. R.; Kashiv, Y.; Clayton, R. N.; Lewis, R. S.; Amari, S.

    2001-01-01

    Barium isotopic compositions of single presolar grains were measured by laser ablation laser resonant ionization mass spectrometry and the implications of the data for stellar processes are discussed. Additional information is contained in the original extended abstract.

  11. Barium appendicitis after upper gastrointestinal imaging.

    Science.gov (United States)

    Novotny, Nathan M; Lillemoe, Keith D; Falimirski, Mark E

    2010-02-01

    Barium appendicitis (BA) is a rarely seen entity with fewer than 30 reports in the literature. However, it is a known complication of barium imaging. To report a case of BA in a patient whose computed tomography (CT) scan was initially read as foreign body ingestion. An 18-year-old man presented with right lower quadrant pain after upper gastrointestinal imaging 2 weeks prior. A CT scan was obtained of his abdomen and pelvis that revealed a finding that was interpreted as a foreign body at the area of the terminal ileum. A plain X-ray study of the abdomen revealed radiopaque appendicoliths. Pathology confirmed the diagnosis of barium appendicitis. BA is a rare entity and the pathogenesis is unclear. Shorter intervals between barium study and presentation with appendicitis usually correlate with fewer complications. Copyright (c) 2010 Elsevier Inc. All rights reserved.

  12. Li Storage of Calcium Niobates for Lithium Ion Batteries.

    Science.gov (United States)

    Yim, Haena; Yu, Seung-Ho; Yoo, So Yeon; Sung, Yung-Eun; Choi, Ji-Won

    2015-10-01

    New types of niobates negative electrode were studied for using in lithium-ion batteries in order to alternate metallic lithium anodes. The potassium intercalated compound KCa2Nb3O10 and proton intercalated compound HCa2Nb3O10 were studied, and the electrochemical results showed a reversible cyclic voltammetry profile with acceptable discharge capacity. The as-prepared KCa2Nb3O10 negative electrode had a low discharge capacity caused by high overpotential, but the reversible intercalation and deintercalation reaction of lithium ions was activated after exchanging H+ ions for intercalated K+ ions. The initial discharge capacity of HCa2Nb3O10 was 54.2 mAh/g with 92.1% of coulombic efficiency, compared with 10.4 mAh/g with 70.2% of coulombic efficiency for KCa2Nb3O10 at 1 C rate. The improved electrochemical performance of the HCa2Nb3O10 was related to the lower bonding energy between proton cation and perovskite layer, which facilitate Li+ ions intercalating into the cation site, unlike potassium cation and perovskite layer. Also, this negative material can be easily exfoliated to Ca2Nb3O10 layer by using cation exchange process. Then, obtained two-dimensional nanosheets layer, which recently expected to be an advanced electrode material because of its flexibility, chemical stable, and thin film fabricable, can allow Li+ ions to diffuse between the each perovskite layer. Therefore, this new type layered perovskite niobates can be used not only bulk-type lithium ion batteries but also thin film batteries as a negative material.

  13. Neutral barium cloud evolution at different altitudes

    International Nuclear Information System (INIS)

    Li Lei; Xu Ronglan

    2002-01-01

    Considering the joint effects of diffusion, collision, oxidation and photoionization, the authors study the evolution of the barium cloud at different altitudes in the space plasma active experiment. The results present the variation of the loss rate, number density distribution and brightness of the barium cloud over the range from 120 to 260 km. This can be divided into oxidation, oxidation plus photoionization and photoionization regions

  14. Bacterial Reduction Of Barium Sulphate By Sulphate-Reducing Bacteria

    Directory of Open Access Journals (Sweden)

    Luptáková Alena

    2015-12-01

    Full Text Available Acid mine drainage (AMD is a worldwide problem leading to contamination of water sources. AMD are characterized by low pH and high content of heavy metals and sulphates. The barium salts application presents one of the methods for the sulphates removing from AMD. Barium chloride, barium hydroxide and barium sulphide are used for the sulphates precipitation in the form of barium sulphate. Because of high investment costs of barium salts, barium sulphide is recycled from barium sulphate precipitates. It can be recycled by thermic or bacterial reduction of barium sulphate. The aim of our study was to verify experimentally the possibility of the bacterial transformation of BaSO4 to BaS by sulphate-reducing bacteria. Applied BaSO4 came from experiments of sulphates removal from Smolnik AMD using BaCl2.

  15. An experimental study on barium peritonitis in rats

    International Nuclear Information System (INIS)

    Kang, Heung Sik; Han, Man Chung; Kim, Chu Wan

    1985-01-01

    Barium sulfate is universally used contrast media in gastrointestinal roentgenology, and spillage of barium into peritoneal cavity can occur. The references on effect of barium sulfate in the peritoneal cavity have been scattered and the results are varied. In 80 rats, body weight of 130 gm to 150 gm, sterile pure barium, sterile commercial barium, intestinal content, and mixed pure barium and intestinal content were experimentally injected into the peritoneal cavity. Consecutive weekly laparotomy and microscopic examination were done for 4 weeks. The results are as followings: 1. Mind inflammatory reaction and mild adhesion after sterile pure barium injection. 2. Mild inflammatory reaction and moderate adhesion after sterile commercial barium injection. 3. Acute peritonitis and abscess formation after intestinal content injection. 4. High mortality due to severe acute peritonitis, and severe adhesion in survivors after injection of both pure barium and intestinal content.

  16. Foaming of CRT panel glass powder with Na2CO3

    DEFF Research Database (Denmark)

    Petersen, Rasmus Rosenlund; König, Jakob; Smedskjær, Morten Mattrup

    melt, while Na2O becomes incorporated into the glass structure. We have quantified the melt expansion through density measurements and the Na2O incorporation is indicated by the decrease of the glass transition temperature (Tg) of the final foam glass. The glass foaming quality depends on the foaming......Recycling of cathode ray tube (CRT) glass remains a challenging task. The CRT glass consists of four glass types fused together: Funnel-, neck-, frit- and panel glass. The three former glasses contain toxic lead oxide, and therefore have a low recycling potential. The latter on the other hand...... is lead-free, but since barium and strontium oxide are present, panel glass is incompatible with most common recycling methods. However, foam glass production is a promising approach for the recycling of panel glass waste, since the process parameters can be changed according to the glass waste...

  17. Sulphate removal from sodium sulphate-rich brine and recovery of barium as a barium salt mixture.

    Science.gov (United States)

    Vadapalli, Viswanath R K; Zvimba, John N; Mulopo, Jean; Motaung, Solly

    2013-01-01

    Sulphate removal from sodium sulphate-rich brine using barium hydroxide and recovery of the barium salts has been investigated. The sodium sulphate-rich brine treated with different dosages of barium hydroxide to precipitate barium sulphate showed sulphate removal from 13.5 g/L to less than 400 mg/L over 60 min using a barium to sulphate molar ratio of 1.1. The thermal conversion of precipitated barium sulphate to barium sulphide achieved a conversion yield of 85% using coal as both a reducing agent and an energy source. The recovery of a pure mixture of barium salts from barium sulphide, which involved dissolution of barium sulphide and reaction with ammonium hydroxide resulted in recovery of a mixture of barium carbonate (62%) and barium hydroxide (38%), which is a critical input raw material for barium salts based acid mine drainage (AMD) desalination technologies. Under alkaline conditions of this barium salt mixture recovery process, ammonia gas is given off, while hydrogen sulfide is retained in solution as bisulfide species, and this provides basis for ammonium hydroxide separation and recovery for reuse, with hydrogen sulfide also recoverable for further industrial applications such as sulfur production by subsequent stripping.

  18. Synthesis of barium mercaptides and application of antimony/barium mercaptides

    Institute of Scientific and Technical Information of China (English)

    瞿龙; 张露露; 舒万艮

    2001-01-01

    Mercaptoacetic acid, isooctyl thioglycolate and barium hydroxide used as start materials, barium bis (2-ethylhexyl thioglycolate) (Ba(2EHTG)2), barium thioglycolate (Ba(TG)) and barium bisthioglycolate (Ba(TG)2) were synthesized. Their optimum synthetic techniques were discussed, and some physicochemical data were reported. Infrared spectroscopy and elemental analysis methods were used to identify the structures. They were put into PVC plastic products together with antimony tris (2-ethylhexyl thioglycolate) (Sb(2EHTG)3) under the suitable compounding, and their heat stability to PVC was studied. It is shown that these barium mercaptides have remarkable synergisms with antimony mercaptides and the long-term stabilizing effect of organoantimony stabilizer can be effectively improved, reducing the amount of antimony compounds so as to avoid the decrease of its stabilizing effect.

  19. Synthesis of Barium Titanate (BT) Nano Particles via Hydrothermal Route for the Production of BT-Polymer Nanocomposite

    Science.gov (United States)

    Habib, A.; Haubner, R.; Jakopic, G.; Stelzer, N.

    2007-08-01

    Barium titanate (high-k dielectric material) nano-powders (approx. 30 nm to 60 nm) were synthesised using hydrothermal route under moderate conditions. Effect of temperature and time was studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction techniques. Obtained barium titanate nano-powders were dispersed in thermoplastic polymethyl methacrylate (PMMA) to get homogeneous dispersions. Thin layers were obtained using these dispersions to achieve BaTiO3 endorsed polymer layers by dip-coating for improved polymer insulators on various substrates e.g., glass, and Au sputtered silicon wafers. SEM and focused ion beam (FIB) techniques were used to study the dispersion of barium titanate nano-particles in PMMA. The layers obtained showed homogenous distribution of BaTiO3 nano particles with no agglomeration.

  20. Alloying in an Intercalation Host: Metal Titanium Niobates as Anodes for Rechargeable Alkali-Ion Batteries.

    Science.gov (United States)

    Das, Suman; Swain, Diptikanta; Araujo, Rafael B; Shi, Songxin; Ahuja, Rajeev; Row, Tayur N Guru; Bhattacharyya, Aninda J

    2018-02-02

    We discuss here a unique flexible non-carbonaceous layered host, namely, metal titanium niobates (M-Ti-niobate, M: Al 3+ , Pb 2+ , Sb 3+ , Ba 2+ , Mg 2+ ), which can synergistically store both lithium ions and sodium ions via a simultaneous intercalation and alloying mechanisms. M-Ti-niobate is formed by ion exchange of the K + ions, which are specifically located inside galleries between the layers formed by edge and corner sharing TiO 6 and NbO 6 octahedral units in the sol-gel synthesized potassium titanium niobate (KTiNbO 5 ). Drastic volume changes (approximately 300-400 %) typically associated with an alloying mechanism of storage are completely tackled chemically by the unique chemical composition and structure of the M-Ti-niobates. The free space between the adjustable Ti/Nb octahedral layers easily accommodates the volume changes. Due to the presence of an optimum amount of multivalent alloying metal ions (50-75 % of total K + ) in the M-Ti-niobate, an efficient alloying reaction takes place directly with ions and completely eliminates any form of mechanical degradation of the electroactive particles. The M-Ti-niobate can be cycled over a wide voltage range (as low as 0.01 V) and displays remarkably stable Li + and Na + ion cyclability (>2 Li + /Na + per formula unit) for widely varying current densities over few hundreds to thousands of successive cycles. The simultaneous intercalation and alloying storage mechanisms is also studied within the density functional theory (DFT) framework. DFT expectedly shows a very small variation in the volume of Al-titanium niobate following lithium alloying. Moreover, the theoretical investigations also conclusively support the occurrence of the alloying process of Li ions with the Al ions along with the intercalation process during discharge. The M-Ti-niobates studied here demonstrate a paradigm shift in chemical design of electrodes and will pave the way for the development of a multitude of improved electrodes

  1. High-temperature thermal conductivity of uranium chromite and uranium niobate

    International Nuclear Information System (INIS)

    Fedoseev, D.V.; Varshavskaya, I.G.; Lavrent'ev, A.V.; Oziraner, S.N.; Kuznetsova, D.G.

    1979-01-01

    The technique of determining thermal conductivity coefficient of uranium niobate and uranium chromite on heating with laser radiation is described. Determined is the coefficient of free-convective heat transfer (with provision for a conduction component) by means of a standard specimen. The thermal conductivity coefficients of uranium chromite and niobate were measured in the 1300-1700 K temperature range. The results are presented in a diagram form. It has been calculated, that the thermal conductivity coefficient for uranium niobate specimens is greater in comparison with uranium chromite specimens. The thermal conductivity coefficients of the materials mentioned depend on temperature very slightly. Thermal conductivity of the materials considerably depends on their porosity. The specimens under investigation were fabricated by the pressing method and had the following porosity: uranium chromite - 30 %, uranium niobate - 10 %. Calculation results show, that thermal conductivity of dense uranium chromite is higher than thermal conductivity of dense uranium niobate. The experimental error equals approximately 20 %, that is mainly due to the error of measuring the temperature equal to +-25 deg, with a micropyrometer

  2. New, dense, and fast scintillators based on rare-earth tantalo-niobates

    International Nuclear Information System (INIS)

    Voloshyna, O.V.; Boiaryntseva, I.A.; Baumer, V.N.; Ivanov, A.I.; Korjik, M.V.; Sidletskiy, O.Ts.

    2014-01-01

    Samples of undoped yttrium and gadolinium tantalo-niobates with common formulae RE(Nb x Ta 1−x )O 4 , where RE=Y or Gd and x=0–1, have been obtained by solid-state reaction. Systematic study of structural, luminescent, and scintillation properties of these compounds was carried out. Lattice parameters and space groups of the mixed compounds were identified. UV- and X-ray luminescence spectra, as well as relative light outputs and scintillation decay times are measured. Gadolinium tantalo-niobate with the formulae GdNb 0.2 Ta 0.8 O 4 showed the light output around 13 times larger than PbWO 4 and fast decay with time constant 12 ns without additional slow component. Gadolinium tantalo-niobates may be considered as promising materials for high energy physics due to extremely high density, substantial light output, and fast decay. -- Highlights: •Structural, optical and scintillation properties of the rare earth tantalo-niobates were studied. •Light output shows about gradual increase with Nb content in GdTa x Nb 1−x O 4 . •Light output increases by 2–7 times relatively to yttrium tantalate and niobate in YTa x Nb 1−x O 4 . •GdTa 0.8 Nb 0.2 O 4 demonstrates the most promising scintillation parameters

  3. Gold particle formation via photoenhanced deposition on lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Zaniewski, A.M., E-mail: azaniews@asu.edu; Meeks, V.; Nemanich, R.J.

    2017-05-31

    Highlights: • Gold chloride is reduced into solid gold nanoparticles at the surface of a polarized semiconductor. • Reduction processes are driven by ultraviolet light. • Gold nanoparticle and silver nanoparticle deposition patterns are compared. - Abstract: In this work, we report on a technique to reduce gold chloride into sub-micron particles and nanoparticles. We use photoelectron transfer from periodically polarized lithium niobate (PPLN) illuminated with above band gap light to drive the surface reactions required for the reduction and particle formation. The particle sizes and distributions on the PPLN surface are sensitive to the solution concentration, with inhibited nucleation and large particles (>150 nm) for both low (2E−8M to 9E−7M) and high (1E−5M to 1E−3M) concentrations of gold chloride. At midrange values of the concentration, nucleation is more frequent, resulting in smaller sized particles (<150 nm). We compare the deposition process to that for silver, which has been previously studied. We find that the reduction of gold chloride into nanoparticles is inhibited compared to silver ion reduction, due to the multi-step reaction required for gold particle formation. This also has consequences for the resulting deposition patterns: while silver deposits into nanowires along boundaries between areas with opposite signed polarizations, such patterning of the deposition is not observed for gold, for a wide range of concentrations studied (2E−8 to 1E−3M).

  4. Analysis of Waveguides on Lithium Niobate Thin Films

    Directory of Open Access Journals (Sweden)

    Yiwen Wang

    2018-04-01

    Full Text Available Waveguides formed by etching, proton-exchange (PE, and strip-loaded on single-crystal lithium niobate (LN thin film were designed and simulated by a full-vectorial finite difference method. The single-mode condition, optical power distribution, and bending loss of these kinds of waveguides were studied and compared systematically. For the PE waveguide, the optical power distributed in LN layer had negligible change with the increase of PE thickness. For the strip-loaded waveguide, the relationships between optical power distribution in LN layer and waveguide thickness were different for quasi-TE (q-TE and quasi-TM (q-TM modes. The bending loss would decrease with the increase of bending radius. There was a bending loss caused by the electromagnetic field leakage when the neff of q-TM waveguide was smaller than that of nearby TE planar waveguide. LN ridge waveguides possessed a low bending loss even at a relatively small bending radius. This study is helpful for the understanding of waveguide structures as well as for the optimization and the fabrication of high-density integrated optical components.

  5. Acoustic wave filter based on periodically poled lithium niobate.

    Science.gov (United States)

    Courjon, Emilie; Bassignot, Florent; Ulliac, Gwenn; Benchabane, Sarah; Ballandras, Sylvain

    2012-09-01

    Solutions for the development of compact RF passive transducers as an alternative to standard surface or bulk acoustic wave devices are receiving increasing interest. This article presents results on the development of an acoustic band-pass filter based on periodically poled ferroelectric domains in lithium niobate. The fabrication of periodically poled transducers (PPTs) operating in the range of 20 to 650 MHz has been achieved on 3-in (76.2-mm) 500-μm-thick wafers. This kind of transducer is able to excite elliptical as well as longitudinal modes, yielding phase velocities of about 3800 and 6500 ms(-1), respectively. A new type of acoustic band-pass filter is proposed, based on the use of PPTs instead of the SAWs excited by classical interdigital transducers. The design and the fabrication of such a filter are presented, as well as experimental measurements of its electrical response and transfer function. The feasibility of such a PPT-based filter is thereby demonstrated and the limitations of this method are discussed.

  6. Generation of ionizing radiation from lithium niobate crystals

    Science.gov (United States)

    Orlikov, L. N.; Orlikov, N. L.; Arestov, S. I.; Mambetova, K. M.; Shandarov, S. M.

    2017-01-01

    The work done experimentally explores generation of electron and x-ray radiation in the process of heating and cooling monolithic and iron-doped crystals of lithium niobate. Iron doping to the concentrations in the range of 1023 m3 was carried out by adding ferric oxide into the melt during the process of crystal growth. The research into radiation generation was performed at 1-10 Pa. The speed of heating from -10 to 1070 C was 10-20 degrees a minute. Current pulses appeared at 17, 38, 56, 94, 98, 100, 105, 106, 1070 C with the interval of 1-3 minutes. The obtained electron current increased in direct proportion to the crystal surface area. The maximum current was 3mA at the design voltage 11 kV on the crystal with 14,5x10,5x10 mm3 surface area. The article describes the possibility to control the start of generation by introducing priming pulse. The results achieved are explained by the domain repolarization while heating the crystal and the appearance of electric field local strength. Bias and overcharge currents contribute to the appearance of electric strength, which stimulates breakdown and plasma formation. X-ray radiation appears both at the stage of discharge formation and during electron deceleration on gas and target material.

  7. Effect of Ion Irradiation in Cadmium Niobate Pyrochlores

    International Nuclear Information System (INIS)

    Jiang, Weilin; Weber, William J.; Thevuthasan, Suntharampillai; Boatner, Lynn A.

    2003-01-01

    Irradiation experiments have been performed for cadmium niobate pyrochlore (CdNb2O) single crystals at both 150 and 300 K using 1.0 MeV Au ions over fluences ranging from 0.01 to 0.10 ions/nm. In-situ 3.0 MeV He Rutherford backscattering spectrometry along the -axial channeling direction (RBS/C) has been applied to study the damage states ranging from small defect concentrations to a fully amorphous state. Results show that the crystal can be readily amorphized under the irradiation conditions. Room-temperature recovery of the defects produced at 150 K has been observed, while the defects produced at 300 K are thermally stable at room temperature. Results also indicate that the RBS/C analysis used in this study induced negligible damage in the near-surface regime. In addition, irradiation at and below room temperature using He and C3 ions leads to surface exfoliation at the corresponding damage peaks

  8. Recent Achievements on Photovoltaic Optoelectronic Tweezers Based on Lithium Niobate

    Directory of Open Access Journals (Sweden)

    Angel García-Cabañes

    2018-01-01

    Full Text Available This review presents an up-dated summary of the fundamentals and applications of optoelectronic photovoltaic tweezers for trapping and manipulation of nano-objects on the surface of lithium niobate crystals. It extends the contents of previous reviews to cover new topics and developments which have emerged in recent years and are marking the trends for future research. Regarding the theoretical description of photovoltaic tweezers, detailed simulations of the electrophoretic and dielectrophoretic forces acting on different crystal configurations are discussed in relation to the structure of the obtained trapping patterns. As for the experimental work, we will pay attention to the manipulation and patterning of micro-and nanoparticles that has experimented an outstanding progress and relevant applications have been reported. An additional focus is now laid on recent work about micro-droplets, which is a central topic in microfluidics and optofluidics. New developments in biology and biomedicine also constitute a relevant part of the review. Finally, some topics partially related with photovoltaic tweezers and a discussion on future prospects and challenges are included.

  9. Synthesis and characterization of bismuth zinc niobate pyrochlore nanopowders

    Directory of Open Access Journals (Sweden)

    Sonia Maria Zanetti

    2007-09-01

    Full Text Available Bismuth zinc niobate pyrochlores Bi1.5ZnNb1.5O7 (alpha-BZN, and Bi2(Zn1/3Nb2/32O 7 (beta-BZN have been synthesized by chemical method based on the polymeric precursors. The pyrochlore phase was investigated by differential scanning calorimetry, infrared spectroscopy, and X ray diffraction. Powder and sintered pellets morphology was examined by scanning electron microscopy. The study of alpha-BZN phase formation reveals that, at 500 °C, the pyrochlore phase was already present while a single-phased nanopowder was obtained after calcination at 700 °C. The crystallization mechanism of the beta-BZN is quite different, occurring through the crystallization of alpha-BZN and BiNbO4 intermediary phases. Both compositions yielded soft agglomerated powders. alpha-BZN pellets, sintered at 800 °C for 2 hours, presented a relative density of 97.3% while those of beta-BZN, sintered at 900 °C for 2 hours, reached only 91.8%. Dielectric constant and dielectric loss, measured at 1 MHz, were 150 and 4 x/10-4 for a-BZN, and 97 and 8 x 10-4 for beta-BZN.

  10. Magnetophotorefractive effect and interference filters in lithium niobate

    International Nuclear Information System (INIS)

    Dam-Hansen, C.

    1996-03-01

    This thesis deals with the fundamental photorefractive and photovoltaic properties of iron-doped lithium niobate crystals. Experimental observations of a strong magnetic field effect on the energy coupling and grating formation in a vectorial interaction scheme are presented. To the author's knowledge these are the first reported results in the field. It is shown that an enhancement of the diffraction efficiency of 60% is possible by applying even a moderate magnetic field of 0.23 T. A new theoretical model of the magnetophotorefractive effect in the vectorial interaction scheme is presented. It describes the space-charge field formation, two-wave mixing and grating formation under the influence of an externally applied magnetic field. Good agreement with the experimental results and the first measurement of nondiagonal components of the magnetophotovoltaic tensor are reported. A theoretical model for the temperature properties of photorefractive interference filters with subangstrom bandwidths are presented and compared favourably with experimental investigations. A novel method for determining the spectral response of these filters from a combined thermal and angular response measurements is described. (au) 9 tabs., 30 ills., 84 refs

  11. Coprecipitation of iron and silver with barium fluoride

    International Nuclear Information System (INIS)

    Kopilova, N.V.; Khamidov, B.O.; Kashina, Z.A.; Ikrami, D.D.

    1986-01-01

    Distribution of trace contaminants of iron and silver at coprecipitation of barium fluoride is studied in present work. It is defined that iron almost completely coprecipitated with barium fluoride in wide range of ph 5.5-12. Silver coprecipitated with barium fluoride in ph range 4-7. The value of coprecipitation varies from 94% to 100%.

  12. 40 CFR 721.10011 - Barium calcium manganese strontium oxide.

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Barium calcium manganese strontium... Specific Chemical Substances § 721.10011 Barium calcium manganese strontium oxide. (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as barium calcium...

  13. III-nitride integration on ferroelectric materials of lithium niobate by molecular beam epitaxy

    International Nuclear Information System (INIS)

    Namkoong, Gon; Lee, Kyoung-Keun; Madison, Shannon M.; Henderson, Walter; Ralph, Stephen E.; Doolittle, W. Alan

    2005-01-01

    Integration of III-nitride electrical devices on the ferroelectric material lithium niobate (LiNbO 3 ) has been demonstrated. As a ferroelectric material, lithium niobate has a polarization which may provide excellent control of the polarity of III-nitrides. However, while high temperature, 1000 deg. C, thermal treatments produce atomically smooth surfaces, improving adhesion of GaN epitaxial layers on lithium niobate, repolarization of the substrate in local domains occurs. These effects result in multi domains of mixed polarization in LiNbO 3 , producing inversion domains in subsequent GaN epilayers. However, it is found that AlN buffer layers suppress inversion domains of III-nitrides. Therefore, two-dimensional electron gases in AlGaN/GaN heterojunction structures are obtained. Herein, the demonstration of the monolithic integration of high power devices with ferroelectric materials presents possibilities to control LiNbO 3 modulators on compact optoelectronic/electronic chips

  14. Barium ion beam. Annual progress report

    International Nuclear Information System (INIS)

    Lazar, N.; Dandl, R.; Rynn, N.; Wickham, M.

    1985-01-01

    The barium ion beam Zeeman diagnostic is an in situ nonperturbing diagnostic designed to measure both the plasma electric and magnetic fields in devices such as STM and EBT. The diagnostic satisfies the requirements of high precision, spatial resolution and nonperturbation of the plasma. The technique uses resonance absorption of light from a single moded laser in a beam of energetic barium ions to measure the Zeeman effect in the absorption spectrum (to measure changes in the magnetic field) and to observe the changes in beam velocity by the Doppler shift of the absorption lines

  15. Printed Barium Strontium Titanate capacitors on silicon

    Energy Technology Data Exchange (ETDEWEB)

    Sette, Daniele [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg); Kovacova, Veronika [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Defay, Emmanuel, E-mail: emmanuel.defay@list.lu [Univ. Grenoble Alpes, F-38000 Grenoble (France); CEA, LETI, MINATEC Campus, F-38054 Grenoble (France); Luxembourg Institute of Science and Technology LIST, Materials Research and Technology Department, L-4422 Belvaux (Luxembourg)

    2015-08-31

    In this paper, we show that Barium Strontium Titanate (BST) films can be prepared by inkjet printing of sol–gel precursors on platinized silicon substrate. Moreover, a functional variable capacitor working in the GHz range has been made without any lithography or etching steps. Finally, this technology requires 40 times less precursors than the standard sol–gel spin-coating technique. - Highlights: • Inkjet printing of Barium Strontium Titanate films • Deposition on silicon substrate • Inkjet printed silver top electrode • First ever BST films thinner than 1 μm RF functional variable capacitor that has required no lithography.

  16. Ceramic fiber-reinforced monoclinic celsian phase glass-ceramic matrix composite material

    Science.gov (United States)

    Bansal, Narottam P. (Inventor); Dicarlo, James A. (Inventor)

    1994-01-01

    A hyridopolysilazane-derived ceramic fiber reinforced monoclinic celsian phase barium aluminum silicate glass-ceramic matrix composite material is prepared by ball-milling an aqueous slurry of BAS glass powder and fine monoclinic celsian seeds. The fibers improve the mechanical strength and fracture toughness and with the matrix provide superior dielectric properties.

  17. Optimal design of DC-based polarization beam splitter in lithium niobate on insulator

    Science.gov (United States)

    Gong, Zisu; Yin, Rui; Ji, Wei; Wang, Junbao; Wu, Chonghao; Li, Xiao; Zhang, Shicheng

    2017-08-01

    We propose a DC-based polarization beam splitter (PBS) in lithium niobate on insulator (LNOI). Utilizing the high birefringence property of Lithium Niobate (LiNbO3, LN), the device is achieved by simple structure in a short length. With the use of beam propagation method (BPM), the simulation results show that the device has a good performance for the separation of TE and TM polarizations with a high extinction ratio (about 35 dB). The simulated fabrication tolerance for the variation of the waveguide width is about 100 nm and the bandwidth is about 65 nm when the extinction ratio is higher than 10 dB.

  18. Gamma radiation effects on photorefractive and photoelectric properties of lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Vartanyan, Eh.S.; Ovsepyan, R.K.; Pogosyan, A.R.; Timofeev, A.L.

    1984-08-01

    Investigations into the gamma radiation effect on the photorefractive aned photoelectric properties of lithium niobate crystals have been carried out for the first time. Gamma irradiation has been found to lead to an increase in the photorefractive sensitivity. The effect of optical decoloration has been discovered for the first time along with photorelaxation currents resulting from radiation center decay under the action of light. It has been shown that an increase of photorefractive sensitivity in gamma-irradiated lithium niobate crystals is caused by a new photorefraction mechanism - photorelaxation currents.

  19. Efficient femtosecond mid-infrared pulse generation by dispersivewave radiation in bulk lithium niobate crystal

    DEFF Research Database (Denmark)

    Zhou, Binbin; Guo, Hairun; Bache, Morten

    2014-01-01

    We experimentally demonstrate efficient mid-infrared pulse generation by dispersive wave radiation in bulk lithium niobate crystal. Femtosecond mid-IR pulses centering from 2.8–2.92 µm are generated using the single pump wavelengths from 1.25–1.45 µm.......We experimentally demonstrate efficient mid-infrared pulse generation by dispersive wave radiation in bulk lithium niobate crystal. Femtosecond mid-IR pulses centering from 2.8–2.92 µm are generated using the single pump wavelengths from 1.25–1.45 µm....

  20. Writing single-mode waveguides in lithium niobate by ultra-low intensity solitons

    International Nuclear Information System (INIS)

    Fazio, E.; Ramadan, W.; Petris, A.; Chauvet, M.; Bosco, A.; Vlad, V.I.; Bertolotti, M.

    2005-01-01

    Optical waveguides can be conveniently written in photorefractive materials by using spatial solitons. We have generated bright spatial solitons inside lithium niobate which allow single-mode light propagation. Efficient waveguides have been generated with CW light powers as high as few microwatts. According to the soliton formation, waveguides can be formed with different shapes. Due to the slow response time of the lithium niobate, both for soliton formation and relaxation, the soliton waveguide remains memorised for a long time, of the order of months

  1. Tunable dual-wavelength filter and its group delay dispersion in domain-engineered lithium niobate

    Directory of Open Access Journals (Sweden)

    Guang-hao Shao

    2016-12-01

    Full Text Available A tunable dual-wavelength filter is experimentally demonstrated in domain-engineered lithium niobate. Application of an electric field on the y-surfaces of the sample results in the optical axes rotating clockwise and anticlockwise, which makes selective polarization rotation. The quasi phase-matching wavelengths could be adjusted through suitable domain design. A unique dual valley spectrum is obtained in a periodically poled lithium niobate structure with a central defect if the sample is placed between two parallel polarizers. The expected bandwidth could be varied from ∼1 nm to ∼40 nm. Moreover, both the spectral response and group delay dispersion could be engineered.

  2. Effect of sodium bicarbonate pretreatment on barium coating of mucosa during double contrast barium meal

    International Nuclear Information System (INIS)

    Kinnunen, J.; Toetterman, S.; Kaila, R.; Pietilae, J.; Linden, H.; Tervahartiala, P.

    1983-01-01

    The radiographic pattern of the areae gastricae is produced by barium lying in the intersecting furrows of the gastric mucosal surface. However, if the mucus layer on the gastric mucosa is thick, it interferes with the barium coating of the areae gastricae during double contrast barium meal. As sodium bicarbonate decreases the viscosity of mucus and thus may make the gastric mucus layer thinner, it was evaluated as a pretreatment agent in a routine double contrast upper-gastrointestinal study to improve the visualization of the areae gastricae. In a single blind study, 53 of 106 patients took sodium bicarbonate water mixtures at bedtime the day before and on the morning of the examination. According to the results of the present study mucolysis induced by the used doses of sodium bicarbonate does not significantly affect micromucosal visualization during double-contrast barium meal. (orig.) [de

  3. Effect of sodium bicarbonate pretreatment on barium coating of mucosa during double contrast barium meal

    Energy Technology Data Exchange (ETDEWEB)

    Kinnunen, J.; Toetterman, S.; Kaila, R.; Pietilae, J.; Linden, H.; Tervahartiala, P.

    1983-08-01

    The radiographic pattern of the areae gastricae is produced by barium lying in the intersecting furrows of the gastric mucosal surface. However, if the mucus layer on the gastric mucosa is thick, it interferes with the barium coating of the areae gastricae during double contrast barium meal. As sodium bicarbonate decreases the viscosity of mucus and thus may make the gastric mucus layer thinner, it was evaluated as a pretreatment agent in a routine double contrast upper-gastrointestinal study to improve the visualization of the areae gastricae. In a single blind study, 53 of 106 patients took sodium bicarbonate water mixtures at bedtime the day before and on the morning of the examination. According to the results of the present study mucolysis induced by the used doses of sodium bicarbonate does not significantly affect micromucosal visualization during double-contrast barium meal.

  4. Enterogastroesophageal reflux during barium enema: Report of a case

    International Nuclear Information System (INIS)

    Shin, Hyoun Ja; Rhee, Hak Song

    1972-01-01

    Enterogastric reflux during barium enema examination has been ascribed to various causes including incompetence of the ilepcecal valve, shunt, fistula, excessive barium etc. Recently we have encountered a case of complete enterogastroesphageal regurgitation during barium enema examination performed for the reduction of the ileocolic intuosusception in 6 months old baby. The regurgitation occurred only in the first of two barium enema examinations conducted at one month interval for recurring intussusception. The barium-saline solution used in the present study was not more than 350 ml in quantity. No organic or physical causes of such a complete regurgitation could be determined

  5. 75 FR 19657 - Barium Chloride From China

    Science.gov (United States)

    2010-04-15

    ... China AGENCY: United States International Trade Commission. ACTION: Notice of Commission determination... China. SUMMARY: The Commission hereby gives notice that it will proceed with a full review pursuant to... antidumping duty order on barium chloride from China would be likely to lead to continuation or recurrence of...

  6. Blood pressure changes during barium enema

    International Nuclear Information System (INIS)

    Roach, S.C.; Martin, O.J.D.; Owen, A.; Martin, D.F.

    2001-01-01

    AIMS: To document blood pressure changes during barium enema examination and to determine at what point in the examination changes are likely to occur. METHODS AND RESULTS: Blood pressure measurements were taken at seven points during the course of barium enema examination in 107 consecutive patients. We found that patients over the age of 60 years had statistically significant decreases in blood pressure when they were stood up during the course of the examination. Many of these patients were asymptomatic. Patients who had symptoms (15/107, 14%) when standing up had a degree of hypotension. The duration of barium enema examination is longer in those patients who experience symptoms. CONCLUSION: During a barium enema examination hypotension occurs at the point of standing up more frequently in patients over 60 years and in those who suffer symptoms at this time. Patients who fall into one of these groups should be considered at risk of fainting at this point in the examination. A modified technique to avoid standing should be considered in at-risk patients. Roach, S.C. et al. (2001)

  7. High temperature impedance spectroscopy of barium stannate ...

    Indian Academy of Sciences (India)

    (M = Ba, Sr, Ca and Pb). ... Barium stannate (BaSnO3) is a cubic pervoskite oxide com- .... were gold-sputtered and scanned in different regions using .... de ions. Water insertion into the oxide structure can be re- presented as the process of ...

  8. 75 FR 20625 - Barium Chloride From China

    Science.gov (United States)

    2010-04-20

    ... INTERNATIONAL TRADE COMMISSION [Investigation No. 731-TA-149 (Third Review)] Barium Chloride From China AGENCY: United States International Trade Commission. ACTION: Revised schedule for the subject review. DATES: Effective Date: April 9, 2010. FOR FURTHER INFORMATION CONTACT: Amy Sherman (202-205-3289...

  9. 75 FR 33824 - Barium Chloride From China

    Science.gov (United States)

    2010-06-15

    ... China Determination On the basis of the record\\1\\ developed in the subject five-year review, the United... China would be likely to lead to continuation or recurrence of material injury to an industry in the... contained in USITC Publication 4157 (June 2010), entitled Barium Chloride from China: Investigation No. 731...

  10. Thermal decomposition of barium valerate in argon

    DEFF Research Database (Denmark)

    Torres, P.; Norby, Poul; Grivel, Jean-Claude

    2015-01-01

    The thermal decomposition of barium valerate (Ba(C4H9CO2)(2)/Ba-pentanoate) was studied in argon by means of thermogravimetry, differential thermal analysis, IR-spectroscopy, X-ray diffraction and hot-stage optical microscopy. Melting takes place in two different steps, at 200 degrees C and 280...

  11. Impurities in barium titanate posistor ceramics

    Czech Academy of Sciences Publication Activity Database

    Korniyenko, S. M.; Bykov, I. P.; Glinchuk, M. J.; Laguta, V. V.; Belous, A. G.; Jastrabík, Lubomír

    2000-01-01

    Roč. 239, - (2000), s. 1209-1218 ISSN 0015-0193 Institutional research plan: CEZ:AV0Z1010914 Keywords : barium titanate phase transition * ESR * positive temperature coefficient of resistivity Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 0.547, year: 2000

  12. Growth, defect structure, and THz application of stoichiometric lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Lengyel, K.; Péter, Á.; Kovács, L.; Corradi, G.; Dravecz, G.; Hajdara, I.; Szaller, Zs.; Polgár, K. [Wigner Research Centre for Physics, Hungarian Academy of Sciences, 1121 Budapest, Konkoly-Thege M. út 29-33 (Hungary); Pálfalvi, L.; Unferdorben, M. [Institute of Physics, University of Pécs, 7624 Pécs, Ifjúság útja 6 (Hungary); Hebling, J. [Institute of Physics, University of Pécs, 7624 Pécs, Ifjúság útja 6 (Hungary); MTA-PTE High Field Terahertz Research Group, 7624 Pécs (Hungary)

    2015-12-15

    Owing to the extraordinary richness of its physical properties, congruent lithium niobate has attracted multidecade-long interest both for fundamental science and applications. The combination of ferro-, pyro-, and piezoelectric properties with large electro-optic, acousto-optic, and photoelastic coefficients as well as the strong photorefractive and photovoltaic effects offers a great potential for applications in modern optics. To provide powerful optical components in high energy laser applications, tailoring of key material parameters, especially stoichiometry, is required. This paper reviews the state of the art of growing large stoichiometric LiNbO{sub 3} (sLN) crystals, in particular, the defect engineering of pure and doped sLN with emphasis on optical damage resistant (ODR) dopants (e.g., Mg, Zn, In, Sc, Hf, Zr, Sn). The discussion is focused on crystals grown by the high temperature top seeded solution growth (HTTSSG) technique using alkali oxide fluxing agents. Based on high-temperature phase equilibria studies of the Li{sub 2}O–Nb{sub 2}O{sub 5}–X{sub 2}O ternary systems (X = Na, K, Rb, Cs), the impact of alkali homologue additives on the stoichiometry of the lithium niobate phase will be analyzed, together with a summary of the ultraviolet, infrared, and far-infrared absorption spectroscopic methods developed to characterize the composition of the crystals. It will be shown that using HTTSSG from K{sub 2}O containing flux, crystals closest to the stoichiometric composition can be grown characterized by a UV-edge position of at about 302 nm and a single narrow hydroxyl band in the IR with a linewidth of less than 3 cm{sup −1} at 300 K. The threshold concentrations for ODR dopants depend on crystal stoichiometry and the valence of the dopants; Raman spectra, hydroxyl vibration spectra, and Z-scan measurements prove to be useful to distinguish crystals below and above the photorefractive threshold. Crystals just above the threshold are

  13. Annealing behaviour of MeV erbium implanted lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Gortmaker, P; McCallum, J C [Royal Melbourne Inst. of Tech., VIC (Australia)

    1994-12-31

    Lithium niobate (LiNbO{sub 3}) is a crystalline ceramic commonly used in the fabrication of optoelectronic devices. Recently, rare earth doping of LiNbO{sub 3} has become a topic of particular interest. The electronic configuration of rare earth elements such as Erbium (Er) and Neodymium (Nd) allows them to lase in nearly any host matrix making fabrication of a whole range of new optoelectronic devices possible. At present, the doping technique, for LiNbO{sub 3} are centred upon diffusion technology, but the diffusion profiles for the rare earths are not generally well-matched to the optical modes of the device. The aim of this research is to develop MeV implantation and annealing conditions of rare earth doped LiNbO{sub 3} that would be compatible with optoelectronic device fabrication. To determine the characteristics of the rare earth elements in the LiNbO{sub 3} host material over the depth range of interest in optoelectronic device applications, high energy Rutherford backscattering spectrometry and ion channeling (RBS-C) must be used. Presented here are the Er depth profile and lattice damage results obtained from 5 MeV RBS-C measurements on samples of LiNbO{sub 3} implanted with various doses of MeV Erbium and subsequently thermally annealed at a temperature of 1000 deg C. It was found that there is a peak implant concentration (2 x 10{sup 16} Er/cm{sup 2}) for which erbium no longer goes substitutional in the lattice, and the implantation damage is not fully removed by annealing. 8 refs., 3 figs.

  14. Synthesis and thermoluminescent characterization of lithium niobate doped with erbium

    International Nuclear Information System (INIS)

    Landavazo, M.; Brown, F.; Cubillas, F.; Munoz, I.; Cruz Z, E.

    2015-10-01

    Full text: Lithium niobate (Nl) is a synthetic dielectric and is mainly used in optical devices. There are reports on the thermoluminescent property of Nl monocrystals doped with rare earths and excited with X and gamma rays. In this study the Nl was synthesized and doped with erbium (Er) at concentrations of 1, 2 and 4 % mol and was characterized by its Tl property. The synthesis was realized by solid state reaction at 1000 degrees C for 22 hours and the formation of Nl:Er was confirmed by X-ray diffraction, scanning electron microscopy and EDS analysis, finding a new phase (ErNbO 4 ). Was studied the dose-response gamma in a range of 1-1000 Gy, the material showed linear behavior of 1-600 Gy. The brightness curves have maxima at 185 and 285 degrees C to 1% in 183 and 301 degrees C for 2%, respectively. While for the concentration of 4% a maximum in 177 degrees C accompanied by a smaller peak at higher temperature of the glow curve was observed. The Tl response of Nl:Er 4% to 450 Gy was increased 271 times compared to pure Nl. The reproducibility of the Tl signal at ten cycles of irradiation-reading, present a standard deviation of 5%. In Nl:Er 1% Tl signal fades in 21.3% after 24 hours, while in 2 and 4% an unusual fading occurs. The Tl characteristics of Nl:Er synthesized material is of interest to gamma radiation dosimetry of high doses. (Author)

  15. Ridge Waveguide Structures in Magnesium-Doped Lithium Niobate

    Science.gov (United States)

    Himmer, Phillip; Battle, Philip; Suckow, William; Switzer, Greg

    2011-01-01

    This work proposes to establish the feasibility of fabricating isolated ridge waveguides in 5% MgO:LN. Ridge waveguides in MgO:LN will significantly improve power handling and conversion efficiency, increase photonic component integration, and be well suited to spacebased applications. The key innovation in this effort is to combine recently available large, high-photorefractive-damage-threshold, z-cut 5% MgO:LN with novel ridge fabrication techniques to achieve high-optical power, low-cost, high-volume manufacturing of frequency conversion structures. The proposed ridge waveguide structure should maintain the characteristics of the periodically poled bulk substrate, allowing for the efficient frequency conversion typical of waveguides and the high optical damage threshold and long lifetimes typical of the 5% doped bulk substrate. The low cost and large area of 5% MgO:LN wafers, and the improved performance of the proposed ridge waveguide structure, will enhance existing measurement capabilities as well as reduce the resources required to achieve high-performance specifications. The purpose of the ridge waveguides in MgO:LN is to provide platform technology that will improve optical power handling and conversion efficiency compared to existing waveguide technology. The proposed ridge waveguide is produced using standard microfabrication techniques. The approach is enabled by recent advances in inductively coupled plasma etchers and chemical mechanical planarization techniques. In conjunction with wafer bonding, this fabrication methodology can be used to create arbitrarily shaped waveguides allowing complex optical circuits to be engineered in nonlinear optical materials such as magnesium doped lithium niobate. Researchers here have identified NLO (nonlinear optical) ridge waveguide structures as having suitable value to be the leading frequency conversion structures. Its value is based on having the low-cost fabrication necessary to satisfy the challenging pricing

  16. Annealing behaviour of MeV erbium implanted lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Gortmaker, P.; McCallum, J.C. [Royal Melbourne Inst. of Tech., VIC (Australia)

    1993-12-31

    Lithium niobate (LiNbO{sub 3}) is a crystalline ceramic commonly used in the fabrication of optoelectronic devices. Recently, rare earth doping of LiNbO{sub 3} has become a topic of particular interest. The electronic configuration of rare earth elements such as Erbium (Er) and Neodymium (Nd) allows them to lase in nearly any host matrix making fabrication of a whole range of new optoelectronic devices possible. At present, the doping technique, for LiNbO{sub 3} are centred upon diffusion technology, but the diffusion profiles for the rare earths are not generally well-matched to the optical modes of the device. The aim of this research is to develop MeV implantation and annealing conditions of rare earth doped LiNbO{sub 3} that would be compatible with optoelectronic device fabrication. To determine the characteristics of the rare earth elements in the LiNbO{sub 3} host material over the depth range of interest in optoelectronic device applications, high energy Rutherford backscattering spectrometry and ion channeling (RBS-C) must be used. Presented here are the Er depth profile and lattice damage results obtained from 5 MeV RBS-C measurements on samples of LiNbO{sub 3} implanted with various doses of MeV Erbium and subsequently thermally annealed at a temperature of 1000 deg C. It was found that there is a peak implant concentration (2 x 10{sup 16} Er/cm{sup 2}) for which erbium no longer goes substitutional in the lattice, and the implantation damage is not fully removed by annealing. 8 refs., 3 figs.

  17. Barium carbonate as an agent to improve the electrical properties of neodymium-barium-copper system at high temperature

    International Nuclear Information System (INIS)

    Fernandes, J.P.; Duarte, G.W.; Caldart, C.; Kniess, C.T.; Montedo, O.R.K.; Rocha, M.R.; Riella, H.G.; Fiori, M.A.

    2015-01-01

    Specialized ceramics are manufactured under special conditions and contain specific elements. They possess unique electrical and thermal properties and are frequently used by the electronics industry. Ceramics containing neodymium-barium-copper (NBC) exhibit high conductivities at low temperatures. NBC-based ceramics are typically combined with oxides, i.e., NBCo produced from neodymium oxide, barium oxide and copper oxide. This study presents NBC ceramics that were produced with barium carbonate, copper oxide and neodymium oxide (NBCa) as starting materials. These ceramics have good electrical conductivities at room temperature. Their conductivities are temperature dependent and related to the starting amount of barium carbonate (w%). - Highlights: • The new crystalline structure were obtained due presence of the barium carbonate. • The NBCa compound has excellent electrical conductivity at room temperature. • The grain crystalline morphology was modified by presence of the barium carbonate. • New Phases α and β were introduced by carbonate barium in the NBC compound

  18. Barium carbonate as an agent to improve the electrical properties of neodymium-barium-copper system at high temperature

    Energy Technology Data Exchange (ETDEWEB)

    Fernandes, J.P. [Post-Graduate Program in Chemical Engineering, Universidade Federal de Santa Catarina (UFSC), Florianópolis, SC, 88040-900 (Brazil); Duarte, G.W. [Post-Graduate Program in Chemical Engineering, Universidade Federal de Santa Catarina (UFSC), Florianópolis, SC, 88040-900 (Brazil); Research Group in Technology and Information, Centro Universitário Barriga Verde (UNIBAVE), Santa Catarina, SC (Brazil); Caldart, C. [Post-Graduate Program in Science and Materials Engineering, Universidade do Extremo Sul Catarinense (UNESC), Criciúma, SC, 88806-000 (Brazil); Kniess, C.T. [Post-Graduate Program in Professional Master in Management, Universidade Nove de Julho, São Paulo, SP (Brazil); Montedo, O.R.K.; Rocha, M.R. [Post-Graduate Program in Science and Materials Engineering, Universidade do Extremo Sul Catarinense (UNESC), Criciúma, SC, 88806-000 (Brazil); Riella, H.G. [Post-Graduate Program in Chemical Engineering, Universidade Federal de Santa Catarina (UFSC), Florianópolis, SC, 88040-900 (Brazil); Fiori, M.A., E-mail: fiori@unochapeco.edu.br [Post-Graduate Program in Environmental Science, Universidade Comunitária da Região de Chapecó (UNOCHAPECÓ), Chapecó, SC, 89809-000 (Brazil); Post-Graduate Program in Technology and Management of the Innovation, Universidade Comunitária da Região de Chapecó (UNOCHAPECÓ), Chapecó, SC, 89809-000 (Brazil)

    2015-11-15

    Specialized ceramics are manufactured under special conditions and contain specific elements. They possess unique electrical and thermal properties and are frequently used by the electronics industry. Ceramics containing neodymium-barium-copper (NBC) exhibit high conductivities at low temperatures. NBC-based ceramics are typically combined with oxides, i.e., NBCo produced from neodymium oxide, barium oxide and copper oxide. This study presents NBC ceramics that were produced with barium carbonate, copper oxide and neodymium oxide (NBCa) as starting materials. These ceramics have good electrical conductivities at room temperature. Their conductivities are temperature dependent and related to the starting amount of barium carbonate (w%). - Highlights: • The new crystalline structure were obtained due presence of the barium carbonate. • The NBCa compound has excellent electrical conductivity at room temperature. • The grain crystalline morphology was modified by presence of the barium carbonate. • New Phases α and β were introduced by carbonate barium in the NBC compound.

  19. Glass sealing

    Energy Technology Data Exchange (ETDEWEB)

    Brow, R.K.; Kovacic, L.; Chambers, R.S. [Sandia National Labs., Albuquerque, NM (United States)

    1996-04-01

    Hernetic glass sealing technologies developed for weapons component applications can be utilized for the design and manufacture of fuel cells. Design and processing of of a seal are optimized through an integrated approach based on glass composition research, finite element analysis, and sealing process definition. Glass sealing procedures are selected to accommodate the limits imposed by glass composition and predicted calculations.

  20. Electrochromic Glasses.

    Science.gov (United States)

    1980-07-31

    this glass and that dipole-dipole correlations contribute to the "ferroelectric-like" character of this amorphous system. The TeO2 -W03 glasses can only...shows the dielectric constant and Fig. I(b) glass from pure TeO2 ot pure WO. In addition, glass the tan 8 of the WO glass as a function of temperature... glasses containing WO, in various glass forming nitworks of LifO-B1O0, Na:O-BzO,, and TeO2 were prepared from reagent grade oxides at 800 C - 9SO C in

  1. Fabrication of artificial gemstones from glasses: From waste to jewelry

    Science.gov (United States)

    Srisittipokakun, N.; Ruangtaweep, Y.; Horprathum, M.; Kaewkhao, J.

    2014-09-01

    In this review, several aspects of artificial gemstones from glasses have been addressed from the advantages, the fabrication process, the coloration, their properties and finally the use of RHA as the glass former for the simulant gemstones. The silica sources for preparation of glasses were locally obtained from sand and biomass ashes in Thailand. The refractive index, density and hardness values of the glass gemstones reported in these researches had been meet the standard of EU-regulation for crystal. The glass gemstones were fabricated in a variety of colors with some special features such as color changing when exposed under different light sources. Barium was used instead of lead to increase the density and refractive index of the glasses. The developments of high refractive index lead-free glasses are also leave non-toxically impact to our environment.

  2. Chemical transport of niobium(V) oxide and of lithium niobate with sulphur

    International Nuclear Information System (INIS)

    Schaefer, H.

    1988-01-01

    Niobium(V) oxide is transported by means of sulphur (calculated for 10 bar at 1223 K) from 1273 → 1173 K. The same applies for lithium niobate. Similar experiments of lithium oxide lead to turbidity of the quartz ampoule. (author)

  3. Shape manipulation of ion irradiated Ag nanoparticles embedded in lithium niobate

    NARCIS (Netherlands)

    Wolf, S.; Rensberg, J.; Johannes, A.; Thomae, R.; Smit, F.; Neveling, R.; Moodley, M.; Bierschenk, T.; Rodriquez, M.; Afra, B.; Hasan, Shakeeb Bin; Rockstuhl, C.; Ridgway, M.; Bharuth-Ram, K.; Ronning, C.

    2016-01-01

    Spherical silver nanoparticles were prepared by means of ion beam synthesis in lithium niobate. The embedded nanoparticles were then irradiated with energetic 84Kr and 197Au ions, resulting in different electronic energy losses between 8.1 and 27.5 keV nm−1 in the top layer of the samples. Due to

  4. All-optical switching in lithium niobate directional couplers with cascaded nonlinearity

    NARCIS (Netherlands)

    Schiek, R.; Baek, Y.; Krijnen, Gijsbertus J.M.; Stegeman, G.I.; Baumann, I.; Sohler, W.

    1996-01-01

    We report on intensity-dependent switching in lithium niobate directional couplers. Large nonlinear phase shifts that are due to cascading detune the coupling between the coupler branches, which makes all-optical switching possible. Depending on the input intensity, the output could be switched

  5. Giant piezoelectricity in potassium-sodium niobate lead-free ceramics.

    Science.gov (United States)

    Wang, Xiaopeng; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Cheng, Xiaojing; Zheng, Ting; Zhang, Binyu; Lou, Xiaojie; Wang, Xiangjian

    2014-02-19

    Environment protection and human health concern is the driving force to eliminate the lead from commercial piezoelectric materials. In 2004, Saito et al. [ Saito et al., Nature , 2004 , 432 , 84 . ] developed an alkali niobate-based perovskite solid solution with a peak piezoelectric constant d33 of 416 pC/N when prepared in the textured polycrystalline form, intriguing the enthusiasm of developing high-performance lead-free piezoceramics. Although much attention has been paid on the alkali niobate-based system in the past ten years, no significant breakthrough in its d33 has yet been attained. Here, we report an alkali niobate-based lead-free piezoceramic with the largest d33 of ∼490 pC/N ever reported so far using conventional solid-state method. In addition, this material system also exhibits excellent integrated performance with d33∼390-490 pC/N and TC∼217-304 °C by optimizing the compositions. This giant d33 of the alkali niobate-based lead-free piezoceramics is ascribed to not only the construction of a new rhombohedral-tetragonal phase boundary but also enhanced dielectric and ferroelectric properties. Our finding may pave the way for "lead-free at last".

  6. Erbium medium temperature localised doping into lithium niobate and sapphire: A comparative study

    Czech Academy of Sciences Publication Activity Database

    Nekvindová, P.; Macková, Anna; Peřina, Vratislav; Červená, Jarmila; Čapek, P.; Schrofel, J.; Špirková, J.; Oswald, Jiří

    90-91, - (2003), s. 559-564 ISSN 1012-0394 Institutional research plan: CEZ:AV0Z1048901 Keywords : lithium niobate * sapphire * erbium Subject RIV: BG - Nuclear, Atomic and Molecular Physics, Colliders Impact factor: 0.687, year: 2003

  7. UV laser-assisted fabrication of ridge waveguides in lithium niobate crystals

    OpenAIRE

    Sones, C.L.; Ying, C.Y.J.; Eason, R.W.; Mailis, S.; Ganguly, P.; Soergel, E.

    2010-01-01

    We present a UV laser-assisted method for the fabrication of ridge waveguides in lithium niobate. The UV laser irradiation step provides the refractive index change required for the vertical light confinement in the waveguide and also defines the ferroelectric domain pattern which produces the ridge structures after chemical etching.

  8. Safe disposal of radioactive iodide ions from solutions by Ag2O grafted sodium niobate nanofibers.

    Science.gov (United States)

    Mu, Wanjun; Li, Xingliang; Liu, Guoping; Yu, Qianhong; Xie, Xiang; Wei, Hongyuan; Jian, Yuan

    2016-01-14

    Radioactive iodine isotopes are released into the environment by the nuclear industry and medical research institutions using radioactive materials, and have negative effects on organisms living within the ecosystem. Thus, safe disposal of radioactive iodine is necessary and crucial. For this reason, the uptake of iodide ions was investigated in Ag2O nanocrystal grafted sodium niobate nanofibers, which were prepared by forming a well-matched phase coherent interface between them. The resulting composite was applied as an efficient adsorbent for I(-) anions by forming an AgI precipitate, which also remained firmly attached to the substrates. Due to their one-dimensional morphology, the new adsorbents can be easily dispersed in liquids and readily separated after purification. This significantly enhances the adsorption efficiency and reduces the separation costs. The change in structure from the pristine sodium niobate to Ag2O anchored sodium niobate and to the used adsorbent was examined by using various characterization techniques. The effects of Ag(+) concentration, pH, equilibration time, ionic strength and competing ions on the iodide ion removal ability of the composite were studied. The Ag2O nanocrystal grafted sodium niobate adsorbent showed a high adsorption capacity and excellent selectivity for I(-) anions in basic solutions. Our results are useful for the further development of improved adsorbents for removing I(-) anions from basic wastewater.

  9. Flexible Piezoelectric Touch Sensor by Alignment of Lead-Free Alkaline Niobate Microcubes in PDMS

    NARCIS (Netherlands)

    Deutz, D.B.; Mascarenhas, N.T.; Schelen, J.B.J.; de Leeuw, D.M.; van der Zwaag, S.; Groen, W.A.

    2017-01-01

    A highly sensitive, lead-free, and flexible piezoelectric touch sensor is reported based on composite films of alkaline niobate K0.485Na0.485Li0.03NbO3 (KNLN) powders aligned in a polydimethylsiloxane (PDMS) matrix. KNLN powder is fabricated by

  10. Oesophageal motility disorders - diagnosis with a barium-rice study

    International Nuclear Information System (INIS)

    Schwickert, H.C.; Schadmand-Fischer, S.; Klose, P.; Staritz, M.; Ueberschaer, B.; Thelen, M.

    1993-01-01

    The purpose of this study was to evaluate the role of a 'barium-rice' study for diagnosis of dysphagia and oesophageal motility disorders. Material and methods: 203 patients with oesophageal motility disorders of various aetiologies were examined by both conventional barium study and a 'barium-rice' study. During the latter, oesophageal clearance of a defined mixture of barium sulfate and boiled rice was measured. Results: The conventional barium study revealed prolonged transit time in only 15.8% (32 of 203 cases), whereas barium-rice study was pathological in 50.8% (103 of 203 cases). In 71 of 171 patients (41.5%) with a normal barium study, barium-rice passage was prolonged. In 23 patients, radiological results were confirmed by manometric measurements. Conclusion: Oesophageal motility disorders are detected by a barim-rice study with high sensitivity independent of the underlying disease. The barium-rice study offers a simple diagnostic tool revealing quantitative and reliable results. The barium-rice study is a suitable method for screening and follow-up of patients with dysphagia and oesophageal motility disorders. (orig.) [de

  11. Interaction of light with impurities in lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Schwesyg, Judith Renate Marie-Luise

    2011-06-06

    Congruent lithium niobate (LiNbO{sub 3}) and 5-mol% MgO-doped LiNbO{sub 3} (MgO:LN) crystals are widely used as nonlinear-optical crystals in frequency-conversion devices due to their large nonlinear-optic coefficients. These devices usually require high optical pump powers, but absorption of photons by impurities limits their usability due to heat accumulation that leads to thermo-optic refractive index changes. These refractive index changes distort the beam shape and disturb the phase-matching condition. Furthermore pyroelectric fields can build up. In this thesis the residual optical absorption in congruent LiNbO{sub 3} (CLN) and MgO:LN crystals is studied. Absorption spectra of CLN and MgO:LN crystals between 400-2000 nm reveal a residual absorption up to 0.04 cm{sup -1}. This absorption is mainly caused by transition metal impurities. Between 2300-2800 nm unknown hydrogen absorption bands in CLN and MgO:LN are revealed on the order of 0.001 cm{sup -1}. High-temperature annealing is applied to the CLN and MgO:LN crystals, which decreases optical absorption by up to one order of magnitude. As an application, the operation of a 1550-nm pumped singly-resonant CW optical parametric oscillator, resonant around 2600 nm, using a low-loss, periodically-poled, annealed CLN crystal is demonstrated. Another issue that affects CLN is photorefractive damage (PRD), i.e. light-induced refractive index changes. In contrast, MgO:LN crystals do not suffer from PRD even at high optical intensities. However, it is shown in this thesis that PRD can occur within seconds in MgO:LN, using green laser light at light intensity levels as low as 100 mW/cm{sup 2}, if the crystal is heated by several degrees Celsius during or before illumination. Photorefractive damage does not occur in CLN crystals under the same conditions. We show that the pyroelectric effect together with an elevated photoconductivity compared to that of CLN causes this beam distortion and that this effect also

  12. Interaction of light with impurities in lithium niobate crystals

    International Nuclear Information System (INIS)

    Schwesyg, Judith Renate Marie-Luise

    2011-01-01

    Congruent lithium niobate (LiNbO 3 ) and 5-mol% MgO-doped LiNbO 3 (MgO:LN) crystals are widely used as nonlinear-optical crystals in frequency-conversion devices due to their large nonlinear-optic coefficients. These devices usually require high optical pump powers, but absorption of photons by impurities limits their usability due to heat accumulation that leads to thermo-optic refractive index changes. These refractive index changes distort the beam shape and disturb the phase-matching condition. Furthermore pyroelectric fields can build up. In this thesis the residual optical absorption in congruent LiNbO 3 (CLN) and MgO:LN crystals is studied. Absorption spectra of CLN and MgO:LN crystals between 400-2000 nm reveal a residual absorption up to 0.04 cm -1 . This absorption is mainly caused by transition metal impurities. Between 2300-2800 nm unknown hydrogen absorption bands in CLN and MgO:LN are revealed on the order of 0.001 cm -1 . High-temperature annealing is applied to the CLN and MgO:LN crystals, which decreases optical absorption by up to one order of magnitude. As an application, the operation of a 1550-nm pumped singly-resonant CW optical parametric oscillator, resonant around 2600 nm, using a low-loss, periodically-poled, annealed CLN crystal is demonstrated. Another issue that affects CLN is photorefractive damage (PRD), i.e. light-induced refractive index changes. In contrast, MgO:LN crystals do not suffer from PRD even at high optical intensities. However, it is shown in this thesis that PRD can occur within seconds in MgO:LN, using green laser light at light intensity levels as low as 100 mW/cm 2 , if the crystal is heated by several degrees Celsius during or before illumination. Photorefractive damage does not occur in CLN crystals under the same conditions. We show that the pyroelectric effect together with an elevated photoconductivity compared to that of CLN causes this beam distortion and that this effect also influences frequency conversion

  13. Radioactive Barium Ion Trap Based on Metal-Organic Framework for Efficient and Irreversible Removal of Barium from Nuclear Wastewater.

    Science.gov (United States)

    Peng, Yaguang; Huang, Hongliang; Liu, Dahuan; Zhong, Chongli

    2016-04-06

    Highly efficient and irreversible capture of radioactive barium from aqueous media remains a serious task for nuclear waste disposal and environmental protection. To address this task, here we propose a concept of barium ion trap based on metal-organic framework (MOF) with a strong barium-chelating group (sulfate and sulfonic acid group) in the pore structures of MOFs. The functionalized MOF-based ion traps can remove >90% of the barium within the first 5 min, and the removal efficiency reaches 99% after equilibrium. Remarkably, the sulfate-group-functionalized ion trap demonstrates a high barium uptake capacity of 131.1 mg g(-1), which surpasses most of the reported sorbents and can selectively capture barium from nuclear wastewater, whereas the sulfonic-acid-group-functionalized ion trap exhibits ultrafast kinetics with a kinetic rate constant k2 of 27.77 g mg(-1) min(-1), which is 1-3 orders of magnitude higher than existing sorbents. Both of the two MOF-based ion traps can capture barium irreversibly. Our work proposes a new strategy to design barium adsorbent materials and provides a new perspective for removing radioactive barium and other radionuclides from nuclear wastewater for environment remediation. Besides, the concrete mechanisms of barium-sorbent interactions are also demonstrated in this contribution.

  14. Dielectric response, functionality and energy storage in epoxy nanocomposites: Barium titanate vs exfoliated graphite nanoplatelets

    International Nuclear Information System (INIS)

    Patsidis, A.C.; Kalaitzidou, K.; Psarras, G.C.

    2012-01-01

    Barium titanate/epoxy and exfoliated graphite nanoplatelets/epoxy nanocomposites were prepared and studied varying the filler content. Morphological characteristics were examined via scanning electron microscopy, while structural changes occurring in barium titanate as a function of temperature were investigated by means of X-ray diffraction. Broadband dielectric spectroscopy was employed for determining the dielectric response of the prepared systems. Based on the conducted analysis it was found that three relaxation processes are present in the spectra of the examined materials. From the slower to the faster one, these are interfacial polarization, glass to rubber transition of the polymer matrix, and rearrangement of polar side groups of the polymer chain. Systems' functionality and energy storing efficiency were assessed in terms of dielectric reinforcing function. Finally, the energy density of all systems was evaluated. Composite systems with embedded graphite nanoplatelets exhibit higher energy storing efficiency, while thermally induced structural changes in ferroelectric particles provide functional behavior to barium titanate composites. -- Graphical abstract: Systems' functionality, electrical relaxations and energy storing efficiency were assessed in terms of dielectric permittivity, electric modulus and dielectric reinforcing function (G). Further, the energy density (U) of all systems was evaluated. Composite systems with embedded graphite nanoplatelets exhibit higher energy storing efficiency, while thermally induced structural changes in ferroelectric particles provide functional behavior to barium titanate composites. Highlights: ► Relaxation phenomena were found to be present in all studied systems. ► Two processes emanate from the polymer matrix (α-mode and β-mode). ► Systems' electrical heterogeneity gives rise to interfacial polarization. ► BaTiO 3 /epoxy composites exhibit functional behavior due to structural changes. ► x

  15. Nanoparticles of barium induce apoptosis in human phagocytes.

    Science.gov (United States)

    Mores, Luana; França, Eduardo Luzia; Silva, Núbia Andrade; Suchara, Eliane Aparecida; Honorio-França, Adenilda Cristina

    2015-01-01

    Nutrients and immunological factors of breast milk are essential for newborn growth and the development of their immune system, but this secretion can contain organic and inorganic toxins such as barium. Colostrum contamination with barium is an important issue to investigate because this naturally occurring element is also associated with human activity and industrial pollution. The study evaluated the administration of barium nanoparticles to colostrum, assessing the viability and functional activity of colostral mononuclear phagocytes. Colostrum was collected from 24 clinically healthy women (aged 18-35 years). Cell viability, superoxide release, intracellular Ca(2+) release, and phagocyte apoptosis were analyzed in the samples. Treatment with barium lowered mononuclear phagocyte viability, increased superoxide release, and reduced intracellular calcium release. In addition, barium increased cell death by apoptosis. These data suggest that nanoparticles of barium in colostrum are toxic to cells, showing the importance of avoiding exposure to this element.

  16. Barium Titanate Nanoparticles for Biomarker Applications

    International Nuclear Information System (INIS)

    Matar, O; Hondow, N S; Brydson, R M D; Milne, S J; Brown, A P; Posada, O M; Wälti, C; Saunders, M; Murray, C A

    2015-01-01

    A tetragonal crystal structure is required for barium titanate nanoparticles to exhibit the nonlinear optical effect of second harmonic light generation (SHG) for use as a biomarker when illuminated by a near-infrared source. Here we use synchrotron XRD to elucidate the tetragonal phase of commercially purchased tetragonal, cubic and hydrothermally prepared barium titanate (BaTiO 3 ) nanoparticles by peak fitting with reference patterns. The local phase of individual nanoparticles is determined by STEM electron energy loss spectroscopy (EELS), measuring the core-loss O K-edge and the Ti L 3 -edge energy separation of the t 2g , e g peaks. The results show a change in energy separation between the t 2g and e g peak from the surface and core of the particles, suggesting an intraparticle phase mixture of the barium titanate nanoparticles. HAADF-STEM and bright field TEM-EDX show cellular uptake of the hydrothermally prepared BaTiO 3 nanoparticles, highlighting the potential for application as biomarkers. (paper)

  17. Barium hexaferrite nanoparticles: Synthesis and magnetic properties

    International Nuclear Information System (INIS)

    Martirosyan, K.S.; Galstyan, E.; Hossain, S.M.; Wang Yiju; Litvinov, D.

    2011-01-01

    Carbon combustion synthesis is applied to rapid and energy efficient fabrication of crystalline barium hexaferrite nanoparticles with the average particle size of 50-100 nm. In this method, the exothermic oxidation of carbon nanoparticles with an average size of 5 nm with a surface area of 80 m 2 /g generates a self-propagating thermal wave with maximum temperatures of up to 1000 deg. C. The thermal front rapidly propagates through the mixture of solid reactants converting it to the hexagonal barium ferrite. Carbon is not incorporated in the product and is emitted from the reaction zone as a gaseous CO 2 . The activation energy for carbon combustion synthesis of BaFe 12 O 19 was estimated to be 98 kJ/mol. A complete conversion to hexagonal barium ferrite is obtained for carbon concentration exceeding 11 wt.%. The magnetic properties H c ∼3000 Oe and M s ∼50.3 emu/g of the compact sintered ferrites compare well with those produced by other synthesis methods.

  18. BARIUM REDUCTION OF INTUSSUSCEPTION IN INFANCY

    Science.gov (United States)

    Denenholz, Edward J.; Feher, George. S.

    1955-01-01

    Barium enema reduction was used as the initial routine treatment in 29 infants with intussusception. In 22 of them the intussusception was reduced by this means. In three of eight patients operated upon the intussusception was found to be reduced. Four of the remaining five patients had clinical or x-ray evidence of complications before reduction by barium enema was attempted. Twenty-one of the patients, all of whom were observed in private practice, were treated without admission to the hospital. After reduction, these patients were observed closely by the clinician. None of these patients showed clinical or x-ray signs of complications before reduction. Certain clinical and roentgen criteria must be satisfied before it can be concluded that reduction by barium enema is complete. If there are clinical signs of complications with x-ray evidence of small bowel obstruction, only a very cautious attempt at hydrostatic reduction should be made. As the time factor is generally a reliable clinical guide to reducibility, the late cases should be viewed with greater caution. Long duration of symptoms, however, is not per se a contraindication to an attempt at hydrostatic reduction. PMID:13230908

  19. Making of Magnet Barium Ferit Anisotropic

    International Nuclear Information System (INIS)

    Idayati, Novrita; Dedi

    2003-01-01

    Barium Hexa ferrite (BaFe 12 O 19 ) is ceramic and materials which usually used for making of permanent magnet. In this research Barium Hexa ferrite were made Anisotropic, and applied for loudspeaker, electro motors, dynamo, KWh metre, etc. this Magnet is commonly used due to its high Induction of Remanen (Br) and coercivity (high Hc). Besides it applies a more simple and easier process technology, cheaper raw material, and easy to find it, hence the magnetic component is much cheaper. Powder Metallurgy was used for the process technology, by reacting all materials in the powder (oxide), with a certain size distribution and a tight preparation step. The next step was mixing ferrite and Barium Carbonate (in the form of oxide), calcination, compaction, cantering and characterisation. The Anisotropic particle effects a high Induce Remanen (Br) and of koersifitas (high Hc). All the process steps will is determine physical and chemical characteristics of the magnet. The best Magnet characteristic of the magnet produced in this research is Induction of Remanen (Br) = 4,27 kg, Coercivity (Hc) = 1,745 kOe, Energy Product max (BHmaks) = 2,31 MGOe

  20. Lithium niobate bulk crystallization promoted by CO2 laser radiation

    Science.gov (United States)

    Ferreira, N. M.; Costa, F. M.; Nogueira, R. N.; Graça, M. P. F.

    2012-09-01

    The crystallization induced by laser radiation is a very promising technique to promote glass/ceramic transformation, being already used to produce crystalline patterns on glass surfaces. In this work, a SiO2-Li2O-Nb2O5 glass, prepared by the sol-gel route, was submitted to CO2 laser radiation and conventional heat-treatments in order to induce the LiNbO3 crystallization. The structure and morphology of the samples prepared by both routes was analyzed as a function of exposure time, radiation power and heat-treatment temperatures by XRD, Raman spectroscopy and SEM. The results reveal a correlation between the crystallization degree of LiNbO3 particles and glass matrix with the heat treatment type and experimental parameters. An heat-treatment at 650 °C/4 h was necessary to induce crystallization in heat treatments samples while 4 W/500 s was enough for laser radiation ones, corresponding a reduction time processing of ˜14 000 s.

  1. Glass/Ceramic Composites for Sealing Solid Oxide Fuel Cells

    Science.gov (United States)

    Bansal, Narottam P.; Choi, Sung R.

    2007-01-01

    A family of glass/ceramic composite materials has been investigated for use as sealants in planar solid oxide fuel cells. These materials are modified versions of a barium calcium aluminosilicate glass developed previously for the same purpose. The composition of the glass in mole percentages is 35BaO + 15CaO + 5Al2O3 + 10B2O3 + 35SiO2. The glass seal was found to be susceptible to cracking during thermal cycling of the fuel cells. The goal in formulating the glass/ ceramic composite materials was to (1) retain the physical and chemical advantages that led to the prior selection of the barium calcium aluminosilicate glass as the sealant while (2) increasing strength and fracture toughness so as to reduce the tendency toward cracking. Each of the composite formulations consists of the glass plus either of two ceramic reinforcements in a proportion between 0 and 30 mole percent. One of the ceramic reinforcements consists of alumina platelets; the other one consists of particles of yttria-stabilized zirconia wherein the yttria content is 3 mole percent (3YSZ). In preparation for experiments, panels of the glass/ceramic composites were hot-pressed and machined into test bars.

  2. Near-field-optical-microscopy studies of micro-modifications caused by femtosecond laser irradiation in lithium niobate crystals

    International Nuclear Information System (INIS)

    Lamela, J.; Jaque, D.; Rodenas, A.; Jaque, F.; Torchia, G.A.; Vazquez, J.R.; Mendez, C.; Roso, L.

    2008-01-01

    Near-field-optical-microscopy has been used to study the micro-modifications caused by femtosecond laser pulses focused at the surface and in the volume of lithium niobate crystals. We have found experimental evidence of the existence, close to femtosecond ablation craters, of periodic modifications in the surface reflectivity. In addition, the potential application of near-field-optical microscopy for the spatial location of permanent modifications caused by femtosecond pulses focused inside lithium niobate crystals has been also demonstrated. (orig.)

  3. Kinematic and spatial distributions of barium stars - are the barium stars and Am stars related?

    International Nuclear Information System (INIS)

    Hakkila, J.

    1989-01-01

    The possibility of an evolutionary link between Am stars and barium stars is considered, and an examination of previous data suggests that barium star precursors are main-sequence stars of intermediate mass, are most likely A and/or F dwarfs, and are intermediate-mass binaries with close to intermediate orbital separations. The possible role of mass transfer in the later development of Am systems is explored. Mass transfer and loss from systems with a range of masses and orbital separations may explain such statistical peculiarities of barium stars as the large dispersion in absolute magnitude, the large range of elemental abundances from star to star, and the small number of stars with large peculiar velocities. 93 refs

  4. Effects of Barium Concentration on Oropharyngeal Swallow Timing Measures

    OpenAIRE

    Stokely, Shauna L.; Molfenter, Sonja M.; Steele, Catriona M.

    2013-01-01

    Videofluoroscopy is commonly used for evaluating oropharyngeal swallowing but requires radiopaque contrast (typically barium). Prior studies suggest that some aspects of swallowing, including timing measures of oral and pharyngeal bolus transit, vary depending on barium concentration. The aim of our study was to identify timing differences in healthy swallowing between “thin” (40 % w/v concentration) and “ultrathin” (22 % w/v concentration) barium solutions. Twenty healthy adults (Ten women; ...

  5. Contrast characteristics of barium preparations and the timing of exposure

    OpenAIRE

    渋谷, 光一; 中桐, 義忠; 東, 義晴; 杉田, 勝彦; 小橋, 高郎; 大倉, 保彦; 丹谷, 延義; 三上, 泰隆; 平木, 祥夫

    1995-01-01

    We studied the relationship between the contrast characteristics of barium suspension and timing of exposure. We poured several kinds of barium preparations on the phantom manufactured by ourselves, and took X-ray pictures continuously by a DSA system. We analyzed each of the characteris-tics of the contrast. The time which was reguired for the contrast to reach the peak (Contrast Peak Time ; CPT) was unrelated with the kind of barium preparations used. It depended on the viscosity of the con...

  6. Barium peritonitis following upper gastrointestinal series: A case report

    Energy Technology Data Exchange (ETDEWEB)

    Ko, Su Jin; Hwang, Ji Young; Kim, Yong Jin; Hong, Seong Sook [Soonchunhyang University College of Medicine, Seoul Hospital, Seoul (Korea, Republic of)

    2017-06-15

    We report a rare case of barium peritonitis following an upper gastrointestinal (GI) series and its imaging findings in a 74-year-old female. Barium peritonitis is a rare but life-threatening complication of GI contrast investigation. Therefore, clinical awareness of barium peritonitis as a complication of GI tract contrast investigation would help to prevent such a complication and manage the patients properly.

  7. Barium peritonitis following upper gastrointestinal series: A case report

    International Nuclear Information System (INIS)

    Ko, Su Jin; Hwang, Ji Young; Kim, Yong Jin; Hong, Seong Sook

    2017-01-01

    We report a rare case of barium peritonitis following an upper gastrointestinal (GI) series and its imaging findings in a 74-year-old female. Barium peritonitis is a rare but life-threatening complication of GI contrast investigation. Therefore, clinical awareness of barium peritonitis as a complication of GI tract contrast investigation would help to prevent such a complication and manage the patients properly

  8. Damage threshold of lithium niobate crystal under single and multiple femtosecond laser pulses: theoretical and experimental study

    International Nuclear Information System (INIS)

    Meng, Qinglong; Zhang, Bin; Zhong, Sencheng; Zhu, Liguo

    2016-01-01

    The damage threshold of lithium niobate crystal under single and multiple femtosecond laser pulses has been studied theoretically and experimentally. Firstly, the model for the damage threshold prediction of crystal materials based on the improved rate equation has been proposed. Then, the experimental measure method of the damage threshold of crystal materials has been given in detail. On the basis, the variation of the damage threshold of lithium niobate crystal with the pulse duration has also been analyzed quantitatively. Finally, the damage threshold of lithium niobate crystal under multiple laser pulses has been measured and compared to the theoretical results. The results show that the transmittance of lithium niobate crystal is almost a constant when the laser pulse fluence is relative low, whereas it decreases linearly with the increase in the laser pulse fluence below the damage threshold. The damage threshold of lithium niobate crystal increases with the increase in the duration of the femtosecond laser pulse. And the damage threshold of lithium niobate crystal under multiple laser pulses is obviously lower than that irradiated by a single laser pulse. The theoretical data fall in good agreement with the experimental results. (orig.)

  9. Effects of barium concentration on oropharyngeal swallow timing measures.

    Science.gov (United States)

    Stokely, Shauna L; Molfenter, Sonja M; Steele, Catriona M

    2014-02-01

    Videofluoroscopy is commonly used for evaluating oropharyngeal swallowing but requires radiopaque contrast (typically barium). Prior studies suggest that some aspects of swallowing, including timing measures of oral and pharyngeal bolus transit, vary depending on barium concentration. The aim of our study was to identify timing differences in healthy swallowing between "thin" (40 % w/v concentration) and "ultrathin" (22 % w/v concentration) barium solutions. Twenty healthy adults (Ten women; mean age = 31 years) each performed a series of three noncued 5-ml swallows each of ultrathin and thin liquid barium solutions in videofluoroscopy. Timing measures were compared between barium concentrations using a mixed-model ANOVA. The measures of interest were stage transition duration, pharyngeal transit time, and duration of upper esophageal sphincter opening. Significant differences were observed in the timing measures of swallowing with respect to barium concentration. In all cases, longer durations were seen with the higher barium concentration. Barium concentration influences timing parameters in healthy swallowing, even between ultrathin and thin concentrations. Clinicians need to understand and control for the impact of different barium stimuli on swallowing physiology.

  10. History and challenges of barium titanate: Part I

    Directory of Open Access Journals (Sweden)

    Vijatović M.M.

    2008-01-01

    Full Text Available Barium titanate is the first ferroelectric ceramics and a good candidate for a variety of applications due to its excellent dielectric, ferroelectric and piezoelectric properties. Barium titanate is a member of a large family of compounds with the general formula ABO3 called perovskites. Barium titanate can be prepared using different methods. The synthesis method depends on the desired characteristics for the end application. The used method has a significant influence on the structure and properties of barium titanate materials. In this review paper, Part I contains a study of the BaTiO3 structure and frequently used synthesis methods.

  11. Lanthanide doped strontium-barium cesium halide scintillators

    Science.gov (United States)

    Bizarri, Gregory; Bourret-Courchesne, Edith; Derenzo, Stephen E.; Borade, Ramesh B.; Gundiah, Gautam; Yan, Zewu; Hanrahan, Stephen M.; Chaudhry, Anurag; Canning, Andrew

    2015-06-09

    The present invention provides for a composition comprising an inorganic scintillator comprising an optionally lanthanide-doped strontium-barium, optionally cesium, halide, useful for detecting nuclear material.

  12. Glass consistency and glass performance

    International Nuclear Information System (INIS)

    Plodinec, M.J.; Ramsey, W.G.

    1994-01-01

    Glass produced by the Defense Waste Processing Facility (DWPF) will have to consistently be more durable than a benchmark glass (evaluated using a short-term leach test), with high confidence. The DWPF has developed a Glass Product Control Program to comply with this specification. However, it is not clear what relevance product consistency has on long-term glass performance. In this report, the authors show that DWPF glass, produced in compliance with this specification, can be expected to effectively limit the release of soluble radionuclides to natural environments. However, the release of insoluble radionuclides to the environment will be limited by their solubility, and not glass durability

  13. Colloidal glasses

    Indian Academy of Sciences (India)

    First page Back Continue Last page Overview Graphics. Colloidal glasses. Glassy state is attained when system fails to reach equilibrium due to crowding of constituent particles. In molecular glasses, glassy state is reached by rapidly lowering the temperature. In colloidal glasses, glassy state is reached by increasing the ...

  14. Scintillation properties and X-ray irradiation hardness of Ce3+-doped Gd2O3-based scintillation glass

    International Nuclear Information System (INIS)

    Liu, Liwan; Shao, Chongyun; Zhang, Yu; Liao, Xili; Yang, Qiuhong; Hu, Lili; Chen, Danping

    2016-01-01

    Ce 3+ -doped Gd 2 O 3 -based scintillation glasses are prepared within an air or CO atmosphere. The effects of fluorine, lutetium, barium, and the melting atmosphere on the optical properties, scintillation properties and irradiation hardness are studied. Absorption spectra, luminescence spectra under UV and X-ray excitation, and the X-ray radiation-induced spectra are presented. The results show that the density can be increased by doping with fluorine, lutetium and barium. The luminescence intensity decreases after X-ray irradiation. Because of charge transfer quenching, fluorine and lutetium enhance the UV-excited and X-ray excited luminescence intensity, but barium decreases. Moreover, fluorine and lutetium are advantageous to irradiation hardness while barium is not. In addition, a non-reducing atmosphere provides a higher irradiation hardness than a reducing atmosphere. Fluorine-doped glass is promising to enhance luminescence intensity, promote irradiation hardness, and increase the density.

  15. Thermo-electric oxidization of iron in lithium niobate crystals

    International Nuclear Information System (INIS)

    Falk, Matthias

    2007-01-01

    Lithium niobate crystals (LiNbO 3 ) are a promising material for nonlinear-optical applications like frequency conversion to generate visible light, e.g., in laser displays, but their achievable output power is greatly limited by the ''optical damage'', i.e., light-induced refractive-index changes caused by excitation of electrons from iron impurities and the subsequent retrapping in unilluminated areas of the crystal. The resulting space-charge fields modify the refractive indices due to the electro-optic effect. By this ''photorefractive effect'' the phase-matching condition, i.e., the avoidance of destructive interference between light generated at different crystal positions due to the dispersion of the fundamental wave and the converted wave, is disturbed critically above a certain light intensity threshold. The influence of annealing treatments conducted in the presence of an externally applied electric field (''thermo-electric oxidization'') on the valence state of iron impurities and thereby on the optical damage is investigated. It is observed that for highly iron-doped LiNbO 3 crystals this treatment leads to a nearly complete oxidization from Fe 2+ to Fe 3+ indicated by the disappearance of the absorption caused by Fe 2+ . During the treatment an absorption front forms that moves through the crystal. The absorption in the visible as well as the electrical conductivity are decreased by up to five orders of magnitude due to this novel treatment. The ratio of the Fe 2+ concentration to the total iron concentration - a measure for the strength of the oxidization - is in the order of 10 -6 for oxidized crystals whereas it is about 10 -1 for untreated samples. Birefringence changes are observed at the absorption front that are explained by the removal of hydrogen and lithium ions from the crystal that compensate for the charges of the also removed electrons from Fe 2+ . A microscopic shock-wave model is developed that explains the observed absorption front by

  16. Binding and leakage of barium in alginate microbeads.

    Science.gov (United States)

    Mørch, Yrr A; Qi, Meirigeng; Gundersen, Per Ole M; Formo, Kjetil; Lacik, Igor; Skjåk-Braek, Gudmund; Oberholzer, Jose; Strand, Berit L

    2012-11-01

    Microbeads of alginate crosslinked with Ca(2+) and/or Ba(2+) are popular matrices in cell-based therapy. The aim of this study was to quantify the binding of barium in alginate microbeads and its leakage under in vitro and accumulation under in vivo conditions. Low concentrations of barium (1 mM) in combination with calcium (50 mM) and high concentrations of barium (20 mM) in gelling solutions were used for preparation of microbeads made of high-G and high-M alginates. High-G microbeads accumulated barium from gelling solution and contained higher concentrations of divalent ions for both low- and high-Ba exposure compared with high-G microbeads exposed to calcium solely and to high-M microbeads for all gelling conditions. Although most of the unbound divalent ions were removed during the wash and culture steps, leakage of barium was still detected during storage. Barium accumulation in blood and femur bone of mice implanted with high-G beads was found to be dose-dependent. Estimated barium leakage relevant to transplantation to diabetic patients with islets in alginate microbeads showed that the leakage was 2.5 times lower than the tolerable intake value given by WHO for high-G microbeads made using low barium concentration. The similar estimate gave 1.5 times higher than is the tolerable intake value for the high-G microbeads made using high barium concentration. To reduce the risk of barium accumulation that may be of safety concern, the microbeads made of high-G alginate gelled with a combination of calcium and low concentration of barium ions is recommended for islet transplantation. Copyright © 2012 Wiley Periodicals, Inc.

  17. Application of titanates, niobates, and tantalates to neutralized defense waste decontamination: materials properties, physical forms, and regeneration techniques. Final report

    International Nuclear Information System (INIS)

    Dosch, R.G.

    1981-01-01

    A study of the application of sodium titanate (ST) to the decontamination of neutralized defense waste has been completed. The work was directed at Sr removal from dissolved salt cake, simulated in this work with a 6.0 N NaNO 3 - 0.6 N NaOH solution. Three physical forms of the titanates were developed including powder, pellets, and titanate-loaded resin beads and all were found to be superior to conventional organic ion exchange in this application. When spent, the titanate materials can be calcined to an oxide from which is a stable waste form in itself or can be added directly to a glass melter to become part of a vitrified waste form. Radiation stability of titanate powder and resin forms was assessed in tests in which these materials were exposed to 60 Co radiation. The strontium exchange capacity of the powder remained constant through a dose of 3 x 10 7 rads and retained 50% capacity after a dose of 2 x 10 9 rads. The primary mechanism involved in loss of capacity was believed to be heating associated with the irradiation. The resin forms were unchanged through a dose of 5 x 10 8 rads and retained 30% capacity after a dose of 2 x 10 9 rads. The latter dose resulted in visible degradation of the resin matrix. Anion exchange resins loaded with sodium niobate and sodium tantalate were also prepared by similar methods and evaluated for this application. These materials had Sr sorption properties comparable to the titanate material; however, they would have to provide a significant improvement to justify their higher cost

  18. Silicate glasses

    International Nuclear Information System (INIS)

    Lutze, W.

    1988-01-01

    Vitrification of liquid high-level radioactive wastes has received the greatest attention, world-wide, compared to any other HLW solidification process. The waste form is a borosilicate-based glass. The production of phosphate-based glass has been abandoned in the western world. Only in the Soviet Union are phosphate-based glasses still being developed. Vitrification techniques, equipment and processes and their remote operation have been developed and studied for almost thirty years and have reached a high degree of technical maturity. Industrial demonstration of the vitrification process has been in progress since 1978. This chapter is a survey of world-wide research and development efforts in nuclear waste glasses and its production technology. The principal glasses considered are silicate glasses which contain boron, i.e., borosilicate glasses

  19. Annealed proton exchanged optical waveguides in lithium niobate differences between the X- and Z-cuts

    CERN Document Server

    Nekvindova, P; Cervena, J; Budnar, M; Razpet, A; Zorko, B; Pelicon, P; 10.1016/S0925-3467(01)00186-0

    2002-01-01

    Summarizes results and assessments of our systematic fabrication and characterization of proton exchanged (PE) and annealed proton exchanged (APE) waveguides in lithium niobate. This study focused on different behavior of crystallographically diverse X(1120) and Z (0001) substrate cuts during waveguide fabrication, and differences in characteristics of the resulting waveguides. Non-toxic adipic acid was used as a proton source, and the waveguides properties were defined by mode spectroscopy (waveguide characteristics) and neutron depth profiling (NDP, lithium concentration and distribution), infrared vibration spectra and elastic recoil detection analysis (ERDA, concentration and depth distribution of hydrogen). It was discovered that the X-cut structure is more permeable for moving particles (lithium and hydrogen ions), which leads to a higher effectiveness of the PE process within the X-cut. The explanation of this phenomenon is based on fitting X-cut orientation towards cleavage planes of lithium niobate c...

  20. Acoustically determined linear piezoelectric response of lithium niobate up to 1100 V

    Energy Technology Data Exchange (ETDEWEB)

    Patel, N. [Sandia National Laboratories, Albuquerque, New Mexico 87185 (United States); Department of Electrical and Computer Engineering, University of New Mexico, Albuquerque, New Mexico 87106 (United States); Branch, D. W.; Cular, S. [Sandia National Laboratories, Albuquerque, New Mexico 87185 (United States); Schamiloglu, E. [Department of Electrical and Computer Engineering, University of New Mexico, Albuquerque, New Mexico 87106 (United States)

    2014-04-21

    We present a method to measure high voltages using the piezoelectric crystal lithium niobate without using voltage dividers. A 36° Y-X cut lithium niobate crystal was coupled to two acoustic transducers, where direct current voltages were applied from 128–1100 V. The time-of-flight through the crystal was determined to be linearly dependent on the applied voltage. A model was developed to predict the time-delay in response to the applied voltage. The results show a sensitivity of 17 fs/V with a measurement error of 1 fs/V was achievable using this method. The sensitivity of this method can be increased by measuring the acoustic wave after multiple passes through the crystal. This method has many advantages over traditional techniques such as: favorable scalability for larger voltages, ease of use, cost effectiveness, and compactness.

  1. Design of multi-wavelength tunable filter based on Lithium Niobate

    Science.gov (United States)

    Zhang, Ailing; Yao, Yuan; Zhang, Yue; Song, Hongyun

    2018-05-01

    A multi-wavelength tunable filter is designed. It consists of multiple waveguides among multiple waveguide gratings. A pair of electrodes were placed on both sides of each waveguide. The tunable filter uses the electro-optic effect of Lithium Niobate to tune the phase caused by each waveguide. Consequently, the wavelength and wavelength spacing of the filter are tuned by changing external voltages added on the electrode pairs. The tunable property of the filter is analyzed by phase matching condition and transfer-matrix method. Numerical results show that not only multiple wavelengths with narrow bandwidth are tuned with nearly equal spacing by synchronously changing the voltages added on all electrode pairs, but also the number of wavelengths is determined by the number of phase shifts caused by electrode pairs. Furthermore, due to the electro-optic effect of Lithium Niobate, the tuning speed of the filter can reach the order of ns.

  2. Propagation of light in the lithium niobate crystal along directions close to an optical axis

    International Nuclear Information System (INIS)

    Volkov, V.V.; Egorova, G.A.; Lonskij, Eh.S.; Potapov, E.V.; Rakov, A.V.

    1978-01-01

    Theoretical and experimental results are given of studying some characteristics of electrooptical modulator from lithium niobate when propagating in it linear-polarized light in directions close to the optical axis, the electric field being applied along the X axis. It has been shown that an increase in an angle of deviation from the optical axis of a light beam passing in the crystal changes the value of the controlling voltage. This is accompanied by the rotation of the polarization plane and the change in the intensity of the light being passed. The methods have been proposed of increasing the modulator aperture, determining the main refraction indices and some electrooptical coefficients fo the lithium niobate crystal

  3. Shape manipulation of ion irradiated Ag nanoparticles embedded in lithium niobate

    International Nuclear Information System (INIS)

    Wolf, Steffen; Rensberg, Jura; Johannes, Andreas; Ronning, Carsten; Thomae, Rainer; Smit, Frederick; Neveling, Retief; Bharuth-Ram, Krish; Moodley, Mathew; Bierschenk, Thomas; Rodriguez, Matias; Afra, Boshra; Ridgway, Mark; Hasan, Shakeeb Bin; Rockstuhl, Carsten

    2016-01-01

    Spherical silver nanoparticles were prepared by means of ion beam synthesis in lithium niobate. The embedded nanoparticles were then irradiated with energetic "8"4Kr and "1"9"7Au ions, resulting in different electronic energy losses between 8.1 and 27.5 keV nm"−"1 in the top layer of the samples. Due to the high electronic energy losses of the irradiating ions, molten ion tracks are formed inside the lithium niobate in which the elongated Ag nanoparticles are formed. This process is strongly dependent on the initial particle size and leads to a broad aspect ratio distribution. Extinction spectra of the samples feature the extinction maximum with shoulders on either side. While the maximum is caused by numerous remaining spherical nanoparticles, the shoulders can be attributed to elongated particles. The latter could be verified by COMSOL simulations. The extinction spectra are thus a superposition of the spectra of all individual particles. (paper)

  4. Influence of UV light and heat on the ferroelectric properties of lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Steigerwald, Hendrik

    2011-08-15

    One of the most important non-linear-optical materials is lithium niobate, due to its ease of fabrication, robustness, transparency in the visible-to-infrared and excellent nonlinear properties. In this thesis the issue of tailoring ferroelectric domain structures in lithium niobate crystals is approached from two sides: interaction of defect structures inside the crystal with growing ferroelectric domains is investigated and also actual domain patterning on all crystal faces by different methods is performed. Special emphasis is given to the Mg-doped material. The fundamental understanding and the methods of domain patterning developed in this thesis are then used to obtain tailored domain structures that meet the requirements of their intended application in non-linear optics. (orig.)

  5. Properties of complex tungstates, niobates, translated with fluorite-like structure

    International Nuclear Information System (INIS)

    Vetkina, S.N.; Zolin, V.F.; Sirotinkin, V.P.; Smirnov, S.A.

    1989-01-01

    Spectra of ternary tungstates, niobates and tantalates (MeLa 2 WO 7 , La 3 TO 7 ; Me=Ba, Sr; T=Ta, Nb) related to the layered fluorite group are analyzed. The laser pumping and time resolved luminescence are used for selecting spectra of unequivalent centers. The symmetry of the first center is near to the distorted cubic one. The vibrational spectra of europium in Eu 3 NbO 7 and SrLa 2 WO 7 are due to the chain-like structure of niobates and to the net-like structure of tantalates. The stimulated emission of Nd 3+ in powders of BaLa 2 WO 7 and La 3 NbO 7 is observed at wavelengths of 1.07 and 1.063 μm, respectively

  6. Gluten content of barium sulfate suspensions used for barium swallows in patients with celiac disease.

    Science.gov (United States)

    Chiu, Jennifer G; Shin, Yoona; Patel, Priti N; Mangione, Robert A

    2014-01-01

    To determine the availability and accuracy of information provided by hospitals, imaging centers, and manufacturers regarding gluten in barium sulfate suspensions. A total of 105 facilities were contacted via telephone to determine the gluten content of the contrast media used in those facilities. Manufacturers were contacted and their Web sites reviewed to determine the gluten content of their barium products. Thirty-nine percent of the hospitals and 52% of the imaging centers were not aware of the gluten content of the contrast media they used. Twenty-nine-and-a-half percent of the respondents provided the correct gluten content. The manufacturers noted that 5 products were tested and confirmed gluten free, 1 product was not tested but described as gluten free, 1 product's gluten content depended upon its flavor, and 1 product was reported to contain gluten. Clinicians caring for patients with celiac disease or patients who choose to restrict their gluten consumption must ensure that the barium sulfate suspension ingested is gluten free. It can be difficult to determine the gluten content of barium sulfate, as a majority of radiology departments and imaging centers did not know whether the product they use is gluten free. Educating staff members and improving product labeling would benefit the quality of care provided to patients with celiac disease.

  7. Temperature dependence of the thermoelectric coeffiicients of lithium niobate and lithium tantalate

    International Nuclear Information System (INIS)

    Khachaturyan, O.A.; Gabrielyan, A.I.; Kolesnik, S.P.

    1988-01-01

    Thermoelectric Zeebeck,Thomson, Peltier coefficients for LiNbO 3 and LiTaO 3 monocrystals and their dependence on temperature in 300-1400 K range were investigated. It is shown that Zeebeck (α) coefficient changes its sign, depending on temperature change - the higher is α, the higher is material conductivity in the corresponding temperature region. Thomson and Peltier coefficients were calculated analytically for lithium niobate and tantalate

  8. Generation of tunable narrow-band surface-emitted terahertz radiation in periodically poled lithium niobate.

    Science.gov (United States)

    Weiss, C; Torosyan, G; Avetisyan, Y; Beigang, R

    2001-04-15

    Generation of tunable narrow-band terahertz (THz) radiation perpendicular to the surface of periodically poled lithium niobate by optical rectification of femtosecond pulses is reported. The generated THz radiation can be tuned by use of different poling periods and different observation angles, limited only by the available bandwidth of the pump pulse. Typical bandwidths were 50-100 GHz, depending on the collection angle and the number of periods involved.

  9. Micro- and nanostructuration of lithium niobate; Mikro- und Nanostrukturierung von Lithiumniobat

    Energy Technology Data Exchange (ETDEWEB)

    Hartung, Holger

    2010-04-13

    In the framework of this thesis the application of the ion-beam-enhanced-etching (IBEE) technique for the fabrication of different optical elements, among these photonic crystals, in lithium niobate, was studied. The development of a mask technology fitted to the requirements of the IBEE technique as well as a simulation of the process were performed. Hereby the limitations of the technique in view on minimal structure sizes and structure quality were analyzed. In chapter 1 first the material lithium niobate with its properties and the structuration procedures studied hitherto in the literature is presented. Chapter 2 presents the functionality of the IBEE process and describes the studies on the application of IBEE in lithium niobate performed in the framework of this thesis. In chapter 3 the experimental conditions of all applied processes of the IBEE procedure, the processes used for the mask fabrication, as well all further applied methods and technologies are summarized. Chapter 4 deals with the mask fabrication. The requirements on the masks and the developments necessary for their fulfilment are studied. In chapter 5 the performed simulation of the irradiation, annealing, and etching process is described. This simulation makes the prediciton of the geometry of the components from the process parameters and vice versa the determination of parameters for the reaching of an optimal element geometry possible. In chapter 6 the application of the technique for the fabrication of photonic-crystal membranes and their optical characterization is described. Chapter 7 shows the fabrication of different waveguide and diffractive elements in lithium niobate by means of IBEE.

  10. Outcome of barium enema in patients with colorectal symptoms ...

    African Journals Online (AJOL)

    Background: For many years, double contrast barium enema has been an effective way to evaluate the large bowel. With the development of the colonoscope, the role of barium enema has been questioned. However it is still useful in investigating patients with colorectal symptoms especially in the developing world where ...

  11. Synthesis and properties of barium diketonates as precursors for MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Drozdov, A.A. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Troyanov, S.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Kuzmina, N.P. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Martynenko, L.I. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Alikhanyan, A.S. (Dept. of Chemistry, Moscow State Univ. (Russian Federation)); Malkerova, I.P. (Dept. of Chemistry, Moscow State Univ. (Russian Federation))

    1993-08-01

    The structures of barium diketonates depend on the way in which they are synthesized. It is shown that there is a correlation between the volatility of these compounds and their crystal structures. A new volatile mononuclear adduct of barium dipivaloylmethanate suitable for MOCVD is suggested. (orig.).

  12. Synthesis and properties of barium diketonates as precursors for MOCVD

    International Nuclear Information System (INIS)

    Drozdov, A.A.; Troyanov, S.I.; Kuzmina, N.P.; Martynenko, L.I.; Alikhanyan, A.S.; Malkerova, I.P.

    1993-01-01

    The structures of barium diketonates depend on the way in which they are synthesized. It is shown that there is a correlation between the volatility of these compounds and their crystal structures. A new volatile mononuclear adduct of barium dipivaloylmethanate suitable for MOCVD is suggested. (orig.)

  13. Thermal reactions of some calcium, strontium, and barium chromates

    International Nuclear Information System (INIS)

    Piekarska-Piesse, B.; Gontarz, Z.; Ostrowski, A.; Kucharski, R.

    2000-01-01

    Thermal decomposition of calcium chromates and solid state reactions of barium and strontium chromates(VI) with barium and strontium hydroxides and carbonates, as well as the reduction of chromates by carbon and hydrogen, have been investigated. The mechanisms of individual stages of the thermal decomposition have been proposed on the basis of morphological classification. (author)

  14. Charge distributions of barium isotopes from muonic X-rays

    International Nuclear Information System (INIS)

    Shera, E.B.; Wohlfahrt, H.D.; Hoehn, M.V.; Tanaka, Y.

    1982-01-01

    The results of a muonic X-ray study of the charge radii of stable barium isotopes are presented and compared with optical isotope shifts. The isotope shifts Δ 2 > of a wide range of barium isotopes are found to be in good agreement with the droplet model and with IBA calculations. (orig.)

  15. Barium transport in the hot spot region of fluorescent lamps

    International Nuclear Information System (INIS)

    Sigeneger, F; Rackow, K; Uhrlandt, D; Ehlbeck, J; Lieder, G

    2010-01-01

    The transport of barium atoms and ions in the vicinity of the hot spot in fluorescent lamps operating at 25 kHz is investigated by a combined experimental and theoretical approach. By laser-induced fluorescence, the particle densities of barium atoms and ions were measured time-resolved at different distances from the spot centre. In addition, the time-dependent cathode fall voltage was measured using an improved band method. The model combines a kinetic part for the electrons with a fluid part for the barium atoms and ions. Both parts are spatially resolved in spherically symmetric geometry. The space-dependent electron Boltzmann equation yields the electron density and the ionization rate coefficient of barium as functions of the cathode fall voltage. These results are used to solve the time-dependent particle balance equations of barium atoms and ions which include the ionization of barium as gain and loss terms, respectively. Good agreement between the measured and calculated particle densities of barium atoms is obtained. A sensitive dependence of the ionization frequency and of the barium particle densities on the cathode fall voltage was found.

  16. Barium enema findings of milk allergy in infants

    International Nuclear Information System (INIS)

    Kim, Gyoung Ju; Kim, Mi Jeong; Lee, Hee Jung

    2006-01-01

    We wanted to evaluate the barium enema findings of milk allergy in infants. Retrospective evaluation of the plain abdominal radiography and barium enema findings was performed in fifteen young infants suffering with milk allergy. The presence of gaseous distension, rectal gas, paralytic ileus and mechanical obstruction was evaluated on the plain radiography. The presence of spasm, a transitional zone, a reversed rectosigmoid index and mucosal irregularity was analyzed on the barium enema; the presence of barium retention was also evaluated on 24-hour-delayed plain radiography. Paralytic ileus was the most common finding on the plain radiography (93%). On the barium enema, continuous spasm of the colon, ranging from the rectum to the descending colon, was revealed in ten infants (67%). A transitional zone was observed in one infant and a reversed rectosigmoid index was revealed in four. Mucosal irregularity was observed in two infants. Barium retention was demonstrated in 11 of fifteen cases: throughout the entire colon (n = 3), from the rectum to the descending colon (n = 7), and up to the transverse colon (n = 1). The most common barium enema finding of milk allergy in infants was spasm of the distal colon. The other findings were a transitional zone, a reversed rectosigmoid index, mucosal irregularity and barium retention

  17. INFLUENCE OF BARIUM OXIDE ADDITIONS ON PORTLAND CLINKER

    Directory of Open Access Journals (Sweden)

    Anezka Zezulova

    2016-12-01

    Full Text Available Nowadays, nuclear power plants are widespread around the world and research is of great interest. Together with nuclear research, shielding of different types of radiation is an important current topic of research aiming at their safety. Portland cement has been an elementary building material for centuries. Since barium is very efficient in shielding different types of radiation, it can be assumed that the radiation shielding capability of cement can be improved by incorporation of barium. This work deals with the influence of barium oxide, added in the form of barium carbonate and sulphate, on the formation and properties of Portland clinker. The structure of burnt clinkers and the ratio of clinker phases were studied by polarizing microscopy and by X-ray diffraction. With increasing barium content, the alite-belite ratio decreases and the content of free lime gradually increases. Moreover, sulphates induce the growth of alite crystals. The ability of barium to be a part of the clinker minerals was observed by scanning electron microscopy. Belite and clinker melt contain the highest amount of barium, but aggregates of barium oxide are formed in the clinker melt. Furthermore, the rate of alite crystallization was studied under isothermal conditions.

  18. Application of magnesium hydroxide and barium hydroxide for the ...

    African Journals Online (AJOL)

    Application of magnesium hydroxide and barium hydroxide for the removal of metals and sulphate from mine water. ... equivalent to the Ba(OH)2 dosage. During CO2-dosing, CaCO3 is precipitated to the saturation level of CaCO3. Keywords: Magnesium hydroxide; barium hydroxide; sulphate removal; water treatment ...

  19. Duodenal diverticula demonstrated by barium examination

    Energy Technology Data Exchange (ETDEWEB)

    Christiansen, T.; Thommesen, P.

    An investigation for biliary tract calculi and food-stimulated gastro-oesophageal reflux was carried out in 37 patients with duodenal diverticula demonstrated by barium examination. Sixty per cent of the diverticula were located in the descending part of the duodenum. Biliary tract calculi were demonstrated in 38 per cent and food-stimulated gastro-oesophageal reflux in 81 per cent of the patients. The detection of a duodenal diverticulum should result in a supplementary investigation for gallstones and gastrooesophageal reflux and its sequelae.

  20. Short-cavity squeezing in barium

    Science.gov (United States)

    Hope, D. M.; Bachor, H-A.; Manson, P. J.; Mcclelland, D. E.

    1992-01-01

    Broadband phase sensitive noise and squeezing were experimentally observed in a system of barium atoms interacting with a single mode of a short optical cavity. Squeezing of 13 +/- 3 percent was observed. A maximum possible squeezing of 45 +/- 8 percent could be inferred for out experimental conditions, after correction for measured loss factors. Noise reductions below the quantum limit were found over a range of detection frequencies 60-170 MHz and were best for high cavity transmission and large optical depths. The amount of squeezing observed is consistent with theoretical predictions from a full quantum statistical model of the system.

  1. Shock-wave compression of lithium niobate from 2.4 to 44 GPa

    International Nuclear Information System (INIS)

    Stanton, P.L.; Graham, R.A.

    1979-01-01

    Shock compression of lithium niobate above the Hugoniot elastic limit (about 2.5 GPa) reveals a succession of unusual features. Just above the Hugoniot elastic limit, the shock velocity is observed to be well below the bulk sound speed, indicative of a drastic reduction of shear strength. The shock velocity is observed to increase with particle velocity at an unusually large rate due to the reduction of strength in a very stiff material and an anomalously large pressure derivative of the bulk modulus. This later behavior may be due to the effects of localized shock heating resulting from heterogeneous shear deformation in ferroelectrics like lithium niobate and lithium tantalate in which increases in temperature are shown to have a strong effect on bulk modulus. A shock-induced polymorphic phase transition occurs at 13.9 GPa. Above the transition point the slope of the Hugoniot curve relating shock velocity and particle velocity is unusually low, indicative of a broad mixed phase region of undetermined extent. Limited work is reported on the isomorphous crystal, lithium tantalate, which exhibits features similar to lithium niobate with a Hugoniot elastic limit of 4 GPa and a phase transition in the vicinity of 19 GPa

  2. Evaluation of barium hydroxide treatment efficacy on a dolomitic marble.

    Science.gov (United States)

    Toniolo, L; Colombo, C; Realini, M; Peraio, A; Positano, M

    2001-01-01

    The Arch of Peace, by Luigi Cagnola, is one of the most famous neoclassical monuments in Milan. It has been subjected to conservative intervention in 1998. In the present paper the efficacy of the consolidation by means of barium hydroxide has been evaluated. The stone material showed severe degradation phenomena as: erosion, pulverisation, exfoliation. The analytical data acquired through X-ray diffraction (XRD), infrared spectrophotometry (FTIR) and scanning electron microscopy (SEM-EDX), allowed to compare the conditions of stone before and after the treatment with barium hydroxide. The presence of barium has been put in evidence mainly on the surface as barium sulphate, whereas barium is only sporadically present within the thickness of the decayed material. The treatment was judged not satisfying and its inefficacy is, most probably, due to a not suitable cleaning procedure carried out before the consolidation.

  3. Barium and radium migration in unconsolidated Canadian geological materials

    International Nuclear Information System (INIS)

    Gillham, R.W.; Sharma, H.D.; Reddy, M.R.; Cooper, E.L.; Cherry, J.A.

    1981-05-01

    This report describes the results of laboratory studies on the distribution coefficients of radium and barium in samples of unconsolidated geologic materials. Graphs of Ksub(d) versus solution concentration for the respective elements showed constant Ksub(d) values in the low concentration range suggesting that, at low concentrations, a distribution coefficient is a valid means of representing the geochemical reactions of both barium and radium. The Ksub(d) values for barium range between 60 and 3500 ml/g. The values appear to be influenced by the amount of barium occurring naturally in the soil materials and thus there is little possiblility of using barium as an analog of radium in laboratory experiments. The Ksub(d) values of radium vary from 50 to 1000 ml/g indicating that a wide range of geological materials have a substantial capacity to retard the migration of radium

  4. Barium sulfate aspiration: Severe chemical pneumonia induced by a massive reflux of contrast medium during small bowel barium enema.

    Science.gov (United States)

    Zhang, Lin; Yang, Yi; Zhang, Ji; Zhou, Xiaowei; Dong, Hongmei; Zhou, Yiwu

    2015-08-01

    Barium contrast radiography is a conventional procedure aimed at revealing lesions of the alimentary tract using barium sulfate on X-ray irradiation. Although it is widely used in clinics, adverse effects and complications are observed, such as anaphylaxis, granuloma, fecalithes, abdomen-leaking, embolism, bacterial contamination, and aspiration. We report a case of death due to a massive barium sulfate aspiration resulted from an air-barium double contrast enema radiography. A 25-year-old female patient was hospitalized with symptoms of abdominal distention, nausea, vomiting and diarrhea for three days. A progressive respiratory distress presented only 1h after a small bowel air-barium double contrast enema. The patient died 11h later. The result of autopsy revealed the cause of death to be severe chemical pneumonitis induced by gastric fluid which was aspirated into her lungs. Barium sulfate is generally recognized to be chemically inert for the respiratory system, but a mixture of barium sulfate with gastric contents is fatal. Here we intend to suggest that, when determining the potential cause of death, medical examiners should consider a patient's status quo as well as the possible adverse effects and complications caused by the barium sulfate preparation during gastrointestinal radiography. Copyright © 2015 Elsevier Ireland Ltd. All rights reserved.

  5. NANOSCALE BARIUM HYDROSILICATES: CHOOSING THE SYNTHESIS TECHNOLOGY

    Directory of Open Access Journals (Sweden)

    GRISHINA Anna Nikolaevna

    2013-08-01

    Full Text Available Cement concretes are the most used materials in modern civil engineering. Due to that such materials draw great attention both in the Russian Federation and abroad. The possibility to enhance the manufacturability and operational properties of concretes results in significant reduction of overall operating costs. Many enhancement methods have been elaborated. Among them there is one based on introduction of calcium hydrosilicates into construction composition. The authors set up a hypothesis that similarity between properties and structures of different hydrosilicates (for example, alkaline earth metals and metals of the second group will provide similar increased operational characteristics. The specialists of Research and Educational Center «Nanotechnology» are developing cement composites nanomodification methods which include introduction of nanodimensional barium hydrosilicates particles. The synthesis of barium hydrosilicates particles can be done with the use of many technologies, different by energy consumption or performing complexity. Taking into account both these factors, one can assume that low-temperature sol-gel synthesis from diluted water solutions is the proper technology. The present paper shows that this assumption is correct. The selection of certain technology is made by the means of multiobjective optimization, which is in turn is performed by the means of linear scalarization. This method, while not always giving the Pareto optimal solutions, can be easily implemented. The particle size distribution is taken into consideration during selection of objectives and weights. It is shown that selected technology allows manufacturing nanoparticles with median size about 30 nm.

  6. High resolution studies of barium Rydberg states

    International Nuclear Information System (INIS)

    Eliel, E.R.

    1982-01-01

    The subtle structure of Rydberg states of barium with orbital angular momentum 0, 1, 2 and 3 is investigated. Some aspects of atomic theory for a configuration with two valence electrons are reviewed. The Multi Channel Quantum Defect Theory (MQDT) is concisely introduced as a convenient way to describe interactions between Rydberg series. Three high-resolution UV studies are presented. The first two, presenting results on a transition in indium and europium serve as an illustration of the frequency doubling technique. The third study is of hyperfine structure and isotope shifts in low-lying p states in Sr and Ba. An extensive study of the 6snp and 6snf Rydberg states of barium is presented with particular emphasis on the 6snf states. It is shown that the level structure cannot be fully explained with the model introduced earlier. Rather an effective two-body spin-orbit interaction has to be introduced to account for the observed splittings, illustrating that high resolution studies on Rydberg states offer an unique opportunity to determine the importance of such effects. Finally, the 6sns and 6snd series are considered. The hyperfine induced isotope shift in the simple excitation spectra to 6sns 1 S 0 is discussed and attention is paid to series perturbers. It is shown that level mixing parameters can easily be extracted from the experimental data. (Auth.)

  7. Three barium diphosphonates with 3-D structures

    Science.gov (United States)

    Tuikka, Matti; Haukka, Matti; Ahlgrén, Markku

    2007-06-01

    The gel crystallization method was exploited in this work in order to study the 3-D solid state structures of barium diphosphonates. This technique proved to be an effective tool for the growth of single crystals of diphosphonates for structure analysis. By using this approach, three barium diphosphonates, Ba[HO 3P(CH 2) 2PO 3H] ( 1), Ba 2[O 3P(CH 2) 3PO 3]·3H 2O ( 2) and Ba[HO 3P(CH 2) 4PO 3H] ( 3), with different three dimensional structures, were synthesized and characterized. The structures of compounds 1 and 2 were determined by single crystal X-ray diffraction and the structure of 3 by the powder diffraction method. In the structure of 1, the diphosphonate ligand is completely surrounded by the Ba atoms, which is an unusual arrangement in a diphosphonate system. The structures of 2 and 3 are more conventional. They are organized in typical pillared layers in which the separation of the layers can be adjusted by varying the length of the hydrocarbon chain.

  8. The Novel Formation of Barium Titanate Nanodendrites

    Directory of Open Access Journals (Sweden)

    Chien-Jung Huang

    2014-01-01

    Full Text Available The barium titanate (BaTiO3 nanoparticles with novel dendrite-like structures have been successfully fabricated via a simple coprecipitation method, the so-called BaTiO3 nanodendrites (BTNDs. This method was remarkable, fast, simple, and scalable. The growth solution is prepared by barium chloride (BaCl2, titanium tetrachloride (TiCl4, and oxalic acid. The shape and size of BaTiO3 depend on the amount of added BaCl2 solvent. To investigate the influence of amount of BaCl2 on BTNDs, the amount of BaCl2 was varied in the range from 3 to 6 mL. The role of BaCl2 is found to have remarkable influence on the morphology, crystallite size, and formation of dendrite-like structures. The thickness and length of the central stem of BTND were ~300 nm and ~20 μm, respectively. The branchings were found to occur at irregular intervals along the main stem. Besides, the formation mechanism of BTND is proposed and discussed.

  9. Recycle Glass in Foam Glass Production

    DEFF Research Database (Denmark)

    Petersen, Rasmus Rosenlund; König, Jakob; Yue, Yuanzheng

    The foam glass industry turn recycle glass into heat insulating building materials. The foaming process is relative insensitive to impurities in the recycle glass. It is therefore considered to play an important role in future glass recycling. We show and discuss trends of use of recycled glasses...... in foam glass industry and the supply sources and capacity of recycle glass....

  10. Radiation doses to patients undergoing barium meal and barium enema examinations

    International Nuclear Information System (INIS)

    Delichas, M. G.; Hatziioannou, K.; Papanastassiou, E.; Albanopoulou, P.; Chatzi, E.; Sioundas, A.; Psarrakos, K.

    2004-01-01

    The radiation doses received by patients during 41 barium meal (BM) and 42 barium enema (BE) examinations in two Greek hospitals are presented. Radiation dose was measured in terms of the dose area product (DAP). The effective dose and doses to certain organs were estimated using the ODS-60 software. Mean total DAP values were found to be 25 ± 11 Gy cm 2 for BM and 60 ± 35 Gy cm 2 for BE examinations, whereas the estimated mean values of effective dose were 8.6 ± 4.0 and 24 ± 16 mSv respectively. DAP to effective dose conversion coefficients were estimated to be 0.34 mSv per Gy cm 2 for BM and 0.41 mSv per Gy cm 2 for BE. (authors)

  11. Cosmos & Glass

    DEFF Research Database (Denmark)

    Beim, Anne

    1996-01-01

    The article unfolds the architectural visions of glass by Bruno Taut. It refers to inspirations by Paul Sheerbart and litterature and the Crystal Chain, also it analyses the tectonic univers that can be found in the glass pavillion for the Werkbund exposition in Cologne....

  12. Glass Glimpsed

    DEFF Research Database (Denmark)

    Lock, Charles

    2015-01-01

    Glass in poetry as it reflects the viewer and as its power of reflection are both reduced and enhanced by technology.......Glass in poetry as it reflects the viewer and as its power of reflection are both reduced and enhanced by technology....

  13. Spin glasses

    CERN Document Server

    Bovier, Anton

    2007-01-01

    Spin glass theory is going through a stunning period of progress while finding exciting new applications in areas beyond theoretical physics, in particular in combinatorics and computer science. This collection of state-of-the-art review papers written by leading experts in the field covers the topic from a wide variety of angles. The topics covered are mean field spin glasses, including a pedagogical account of Talagrand's proof of the Parisi solution, short range spin glasses, emphasizing the open problem of the relevance of the mean-field theory for lattice models, and the dynamics of spin glasses, in particular the problem of ageing in mean field models. The book will serve as a concise introduction to the state of the art of spin glass theory, usefull to both graduate students and young researchers, as well as to anyone curious to know what is going on in this exciting area of mathematical physics.

  14. Structuring of material parameters in lithium niobate crystals with low-mass, high-energy ion radiation

    Science.gov (United States)

    Peithmann, K.; Eversheim, P.-D.; Goetze, J.; Haaks, M.; Hattermann, H.; Haubrich, S.; Hinterberger, F.; Jentjens, L.; Mader, W.; Raeth, N. L.; Schmid, H.; Zamani-Meymian, M.-R.; Maier, K.

    2011-10-01

    Ferroelectric lithium niobate crystals offer a great potential for applications in modern optics. To provide powerful optical components, tailoring of key material parameters, especially of the refractive index n and the ferroelectric domain landscape, is required. Irradiation of lithium niobate crystals with accelerated ions causes strong structured modifications in the material. The effects induced by low-mass, high-energy ions (such as 3He with 41 MeV, which are not implanted, but transmit through the entire crystal volume) are reviewed. Irradiation yields large changes of the refractive index Δn, improved domain engineering capability within the material along the ion track, and waveguiding structures. The periodic modification of Δn as well as the formation of periodically poled lithium niobate (PPLN) (supported by radiation damage) is described. Two-step knock-on displacement processes, 3He→Nb and 3He→O causing thermal spikes, are identified as origin for the material modifications.

  15. Role of elastic deformation in determining the mixed alkaline earth effect of hardness in silicate glasses

    DEFF Research Database (Denmark)

    Kjeldsen, Jonas; Smedskjær, Morten Mattrup; Potuzak, M.

    2015-01-01

    been investigated previously, but the link between the resistance to elastic deformation and hardness has not yet been studied. In this work, we investigate the link between elastic deformation during indentation and Vickers hardness in a series of mixed magnesium-barium boroaluminosilicate glasses. We...

  16. Hydrolytic enzyme activity enhanced by Barium supplementation

    Directory of Open Access Journals (Sweden)

    Camilo Muñoz

    2016-10-01

    Full Text Available Hydrolysis of polymers is a first and often limiting step during the degradation of plant residues. Plant biomass is generally a major component of waste residues and a major renewable resource to obtain a variety of secondary products including biofuels. Improving the performance of enzymatic hydrolysis of plant material with minimum costs and limiting the use of additional microbial biomass or hydrolytic enzymes directly influences competitiveness of these green biotechnological processes. In this study, we cloned and expressed a cellulase and two esterases recovered from environmental thermophilic soil bacterial communities and characterize their optimum activity conditions including the effect of several metal ions. Results showed that supplementing these hydrolytic reactions with Barium increases the activity of these extracellular hydrolytic enzymes. This observation represents a simple but major improvement to enhance the efficiency and competitiveness of this process within an increasingly important biotechnological sector.

  17. Effect of certain alkaline metals on Pr doped glasses to investigate spectroscopic studies

    Science.gov (United States)

    Lenkennavar Susheela, K.; Madhu, A.; Eraiah, B.; Kokila, M. K.

    2018-02-01

    Incorporation of different Alkaline earth metal like Barium, Calcium and strontium in sodium lead borate glass doped with Pr3+ is studied. Physical parameters such as density, molar volume, molar refractivity etc have been evaluated. Effect of different atomic size of alkaline metal using optical and physical parameters is analysed. XRD and FTIR were carried out to know the structural behaviour of the glasses. Absorption and Emission spectra are recorded at room temperature and the results were discussed.

  18. The Karlsruhe 4π barium fluoride detector

    International Nuclear Information System (INIS)

    Wisshak, K.; Guber, K.; Kaeppeler, F.; Krisch, J.; Mueller, H.; Rupp, G.; Voss, F.

    1989-12-01

    A new experimental approach has been implemented for accurate measurements of neutron capture cross sections in the energy range from 5 to 200 keV. The Karlsruhe 4π Barium Fluoride Detector consists of 42 crystals shaped as hexagonal and pentagonal truncated pyramids forming a spherical shell with 10 cm inner radius and 15 cm thickness. All crystals are supplied with reflector and photomultiplier, thus representing independent gamma-ray detectors. Each detector module covers the same solid angle with respect to a gamma-ray source located in the centre. The energy resolution of the 4π detector is 14% at 662 keV and 7% at 2.5 MeV gamma-ray energy, the overall time reslution is 500 ps and the peak efficiency 90% at 1 MeV. The detector allows to register capture cascades with 95% probability above a threshold energy of 2.5 MeV in the sum energy spectrum. Neutrons are produced via the 7 Li(p,n) 7 Be reaction using the pulsed proton beam of a Van de Graaff accelerator. The neutron spectrum can be taylored according to the experimental requirements in an energy range from 5 to 200 keV by choosing appropriate proton energies. A collimated neutron beam is passing through the detector and hits the sample in the centre. The energy of captured neutrons is determined via time of flight, the primary flight path being 77 cm. The combination of short primary flight path, a 10 cm inner radius of the spherical BaF 2 shell, and the low capture cross section of barium allows to discriminate background due to capture of sample scattered neutrons in the scintillator by time of flight, leaving part of the neutron energy range completely undisturbed. (orig./HSI) [de

  19. Solar Twins and the Barium Puzzle

    International Nuclear Information System (INIS)

    Reddy, Arumalla B. S.; Lambert, David L.

    2017-01-01

    Several abundance analyses of Galactic open clusters (OCs) have shown a tendency for Ba but not for other heavy elements (La−Sm) to increase sharply with decreasing age such that Ba was claimed to reach [Ba/Fe] ≃ +0.6 in the youngest clusters (ages < 100 Myr) rising from [Ba/Fe] = 0.00 dex in solar-age clusters. Within the formulation of the s -process, the difficulty to replicate higher Ba abundance and normal La−Sm abundances in young clusters is known as the barium puzzle. Here, we investigate the barium puzzle using extremely high-resolution and high signal-to-noise spectra of 24 solar twins and measured the heavy elements Ba, La, Ce, Nd, and Sm with a precision of 0.03 dex. We demonstrate that the enhanced Ba ii relative to La−Sm seen among solar twins, stellar associations, and OCs at young ages (<100 Myr) is unrelated to aspects of stellar nucleosynthesis but has resulted from overestimation of Ba by standard methods of LTE abundance analysis in which the microturbulence derived from the Fe lines formed deep in the photosphere is insufficient to represent the true line broadening imposed on Ba ii lines by the upper photospheric layers from where the Ba ii lines emerge. Because the young stars have relatively active photospheres, Ba overabundances most likely result from the adoption of a too low value of microturbulence in the spectrum synthesis of the strong Ba ii lines but the change of microturbulence in the upper photosphere has only a minor affect on La−Sm abundances measured from the weak lines.

  20. Solar Twins and the Barium Puzzle

    Energy Technology Data Exchange (ETDEWEB)

    Reddy, Arumalla B. S.; Lambert, David L., E-mail: bala@astro.as.utexas.edu [W.J. McDonald Observatory and Department of Astronomy, The University of Texas at Austin, Austin, TX 78712-1205 (United States)

    2017-08-20

    Several abundance analyses of Galactic open clusters (OCs) have shown a tendency for Ba but not for other heavy elements (La−Sm) to increase sharply with decreasing age such that Ba was claimed to reach [Ba/Fe] ≃ +0.6 in the youngest clusters (ages < 100 Myr) rising from [Ba/Fe] = 0.00 dex in solar-age clusters. Within the formulation of the s -process, the difficulty to replicate higher Ba abundance and normal La−Sm abundances in young clusters is known as the barium puzzle. Here, we investigate the barium puzzle using extremely high-resolution and high signal-to-noise spectra of 24 solar twins and measured the heavy elements Ba, La, Ce, Nd, and Sm with a precision of 0.03 dex. We demonstrate that the enhanced Ba ii relative to La−Sm seen among solar twins, stellar associations, and OCs at young ages (<100 Myr) is unrelated to aspects of stellar nucleosynthesis but has resulted from overestimation of Ba by standard methods of LTE abundance analysis in which the microturbulence derived from the Fe lines formed deep in the photosphere is insufficient to represent the true line broadening imposed on Ba ii lines by the upper photospheric layers from where the Ba ii lines emerge. Because the young stars have relatively active photospheres, Ba overabundances most likely result from the adoption of a too low value of microturbulence in the spectrum synthesis of the strong Ba ii lines but the change of microturbulence in the upper photosphere has only a minor affect on La−Sm abundances measured from the weak lines.

  1. Precipitation method for barium metaborate (BaB2O4) synthesis from borax solution

    International Nuclear Information System (INIS)

    Akşener, Eymen; Figen, Aysel Kantürk; Pişkin, Sabriye

    2013-01-01

    In this study, barium metaborate (BaB 2 O 4 , BMB) synthesis from the borax solution was carried out. BMB currently is used in production of ceramic glazes, luminophors, oxide cathodes as well as additives to pigments for aqueous emulsion paints and also β−BaB 2 O 4 single crystals are the best candidate for fabrication of solid-state UV lasers operating at a wavelength of 200 nm due to excellent nonlinear optical properties. In the present study, synthesis was carried out from the borax solution (Na 2 B 4 O 7⋅ 10H 2 O, BDH) and barium chloride (BaCI 2⋅ 2H 2 O, Ba) in the glass-batch reactor with stirring. The effect of, times (5-15 min), molar ratio [stoich.ration (1.0:2.0), 1.25:2.0, 1.5:2.0, 2.5:2:0, 3.0:2.0, 3.5:2.0,4.0:2.0, 5.0:2.0] and also crystallization time (2-6 hour) on the BMB yield (%) was investigated at 80 °C reaction temperature. It is found that, BMB precipitation synthesis with 90 % yield can be performed from 0.50 molar ration (BDH:Ba), under 80 °C, 15 minute, and 6 hours crystallization time. The structural properties of BMB powders were characterized by using XRD, FT-IR and DTA-TG instrumental analysis technique

  2. Precipitation method for barium metaborate (BaB2O4) synthesis from borax solution

    Science.gov (United States)

    Akşener, Eymen; Figen, Aysel Kantürk; Pişkin, Sabriye

    2013-12-01

    In this study, barium metaborate (BaB2O4, BMB) synthesis from the borax solution was carried out. BMB currently is used in production of ceramic glazes, luminophors, oxide cathodes as well as additives to pigments for aqueous emulsion paints and also β-BaB2O4 single crystals are the best candidate for fabrication of solid-state UV lasers operating at a wavelength of 200 nm due to excellent nonlinear optical properties. In the present study, synthesis was carried out from the borax solution (Na2B4O7ṡ10H2O, BDH) and barium chloride (BaCI2ṡ2H2O, Ba) in the glass-batch reactor with stirring. The effect of, times (5-15 min), molar ratio [stoich.ration (1.0:2.0), 1.25:2.0, 1.5:2.0, 2.5:2:0, 3.0:2.0, 3.5:2.0,4.0:2.0, 5.0:2.0] and also crystallization time (2-6 hour) on the BMB yield (%) was investigated at 80 °C reaction temperature. It is found that, BMB precipitation synthesis with 90 % yield can be performed from 0.50 molar ration (BDH:Ba), under 80 °C, 15 minute, and 6 hours crystallization time. The structural properties of BMB powders were characterized by using XRD, FT-IR and DTA-TG instrumental analysis technique.

  3. Elaboration of optical glass-ceramic for frequency doubling

    International Nuclear Information System (INIS)

    Vigouroux, H.

    2012-01-01

    The High power laser development required the need of materials with nonlinear properties. Glass materials can be considered as ideal materials as they can be transparent and elaborated in very large dimension. Precipitation of non-centro symmetric crystalline particles in bulk glass leads to a material with bulk nonlinear properties. This glass-ceramic should be then easily integrated in such laser facilities. In this thesis, the results concerning the precipitation of the phase LiNbO 3 in the glassy-matrix 35 Li 2 O - 25 Nb 2 O 5 - 40 SiO 2 are detailed. The crystallization mechanism of this phase is studied through thermal analysis, optical and electronic microscopy as well as in-situ analyses. These studies reveal glass-ceramics are obtained through a precipitation of the lithium niobate crystalline phase in spherulite shape. The nonlinear optical properties are investigated on this materials and an original, isotropic Second Harmonic Generation Signal (SHG) is registered in the bulk glass-ceramic. A complete study using a multi-scale approach allows the correlation between the spherulite structure and the nonlinear optical properties. A mechanism at the origin of the SHG signal is proposed. This leads to a new approach for transparent inorganic materials development for isotropic SHG conversion. (author) [fr

  4. Steering Charge Kinetics of Tin Niobate Photocatalysts: Key Roles of Phase Structure and Electronic Structure.

    Science.gov (United States)

    Huang, Shushu; Wang, Chunyan; Sun, Hao; Wang, Xiaojing; Su, Yiguo

    2018-05-23

    Tin niobate photocatalysts with the phase structures of froodite (SnNb 2 O 6 ) and pyrochlore (Sn 2 Nb 2 O 7 ) were obtained by a facile solvothermal method in order to explore the impact of phase structure and electronic structure on the charge kinetics and photocatalytic performance. By employing tin niobate as a model compound, the effects of phase structure over electronic structure, photocatalytic activity toward methyl orange solution and hydrogen evolution were systematically investigated. It is found that the variation of phase structure from SnNb 2 O 6 to Sn 2 Nb 2 O 7 accompanied with modulation of particle size and band edge potentials that has great consequences on photocatalytic performance. In combination with the electrochemical impedance spectroscopy (EIS), transient photocurrent responses, transient absorption spectroscopy (TAS), and the analysis of the charge-carrier dynamics suggested that variation of electronic structure has great impacts on the charge separation and transfer rate of tin niobate photocatalysts and the subsequent photocatalytic performance. Moreover, the results of the X-ray photoelectron spectroscopy (XPS) indicated that the existent of Sn 4+ species in Sn 2 Nb 2 O 7 could result in a decrease in photocatalytic activity. Photocatalytic test demonstrated that the SnNb 2 O 6 (froodite) catalyst possesses a higher photocatalytic activity toward MO degradation and H 2 evolution compared with the sample of Sn 2 Nb 2 O 7 (pyrochlore). On the basis of spin resonance measurement and trapping experiment, it is expected that photogenerated holes, O 2 -• , and OH • active species dominate the photodegradation of methyl orange.

  5. Barium ferrite nanoparticles prepared by self-propagating low ...

    Indian Academy of Sciences (India)

    Administrator

    Kubo et al 1982; Lucchini et al 1983), hydrothermal. (Barb et al 1986), microemulsion ... combustion route employing metal oxalate precursors. In search of a suitable ... heptahydrate/barium nitrate and oxalic acid were dis- solved in minimum ...

  6. Late changes in barium sulfate aspiration: HRCT features

    International Nuclear Information System (INIS)

    Voloudaki, A.; Ergazakis, N.; Gourtsoyiannis, N.

    2003-01-01

    Aspiration of barium sulfate occurs accidentally. Lung reaction is usually mild in the early phase due to inert character of the substance and long-term reactions or late toxicities are not expected. Little if any fibrotic response is speculated. We present a case with barium aspiration, studied by high-resolution computed tomography (HRCT) 1 year after the event, as late pulmonary sequelae studied by CT have not been described yet, to the best of our knowledge. The HRCT revealed thickened interlobular septa, subpleural lines, subpleural cysts, and centrilobular micronodules along with barium particles in a subpleural distribution. Those findings indicated that barium is capable of producing mild though silent clinically fibrosis. (orig.)

  7. Synthesis, photoluminescence and magnetic properties of barium vanadate nanoflowers

    International Nuclear Information System (INIS)

    Xu, Jing; Hu, Chenguo; Xi, Yi; Peng, Chen; Wan, Buyong; He, Xiaoshan

    2011-01-01

    Graphical abstract: The flower-shaped barium vanadate was obtained for the first time. The photoluminescence and magnetic properties of the barium vanadate nanoflowers were investigated at room temperature. Research highlights: → In the paper, the flower-shaped barium vanadate were obtained for the first time. The CHM method used here is new and simple for preparation of barium vanadate. → The photoluminescence and magnetic properties of the barium vanadate nanoflowers were investigated at room temperature. The strong bluish-green emission was observed. → The ferromagnetic behavior of the barium vanadate nanoflowers was found with saturation magnetization of about 83.50 x 10 -3 emu/g, coercivity of 18.89 Oe and remnant magnetization of 4.63 x 10 -3 emu/g. → The mechanisms of PL and magnetic property of barium vanadate nanoflowers have been discussed. -- Abstract: The flower-shaped barium vanadate has been obtained by the composite hydroxide mediated (CHM) method from V 2 O 5 and BaCl 2 at 200 o C for 13 h. XRD and XPS spectrum of the as-synthesized sample indicate it is hexagonal Ba 3 V 2 O 8 with small amount of Ba 3 VO 4.8 coexistence. Scan electron microscope and transmission electron microscope display that the flower-shaped crystals are composed of nanosheets with thickness of ∼20 nm. The UV-visible spectrum shows that the barium vanadate sample has two optical gaps (3.85 eV and 3.12 eV). Photoluminescence spectrum of the barium vanadate flowers exhibits a visible light emission centered at 492 and 525 nm which might be attributed to VO 4 tetrahedron with T d symmetry in Ba 3 V 2 O 8 . The ferromagnetic behavior of the barium vanadate nanoflowers has been found with saturation magnetization of about 83.50 x 10 -3 emu/g, coercivity of 18.89 Oe and remnant magnetization of 4.63 x 10 -3 emu/g, which is mainly due to the presence of a non-orthovanadate phase with spin S = 1/2.

  8. Barium ferrite/epoxy resin nanocomposite system: Fabrication, dielectric, magnetic and hydration studies

    Directory of Open Access Journals (Sweden)

    A. Kanapitsas

    2016-03-01

    Full Text Available Composite systems of epoxy resin and barium ferrite nanoparticles have been prepared, and studied varying the content of the inclusions. Morphology of prepared samples has been examined via scanning electron microscopy and X-ray diffraction spectra, while electrical and magnetic properties were investigated by means of broadband dielectric spectroscopy, and magnetization tests respectively. Finally, water vapor sorption measurements were conducted in order to study the water sorption dynamics of the system. Electron microscopy images revealed the successful fabrication of nanocomposites. Dielectric permittivity increases with filler content, while three relaxation processes were detected in the relative spectra. These processes are attributed to interfacial polarization, glass to rubber transition of the matrix, and re-orientation of polar side groups of the polymer’s chain. Magnetization and magnetic saturation increase with magnetic nano-powder content. Nanocomposites absorb a small amount of water, not exceeding 1.7 wt%, regardless filler content, indicating their hydrophobic character.

  9. Growth of potassium niobate micro-hexagonal tablets with monoclinic phase and its excellent piezoelectric property

    Science.gov (United States)

    Chen, Zhong; Huang, Jingyun; Wang, Ye; Yang, Yefeng; Wu, Yongjun; Ye, Zhizhen

    2012-09-01

    Potassium niobate micro-hexagonal tablets were synthesized through hydrothermal reaction with KOH, H2O and Nb2O5 as source materials by using a polycrystalline Al2O3 as substrate. X-ray diffraction, Raman spectra and selected area electron diffraction analysis results indicated that the tablets exhibit monoclinic phase structure and are highly crystallized. Meanwhile, piezoelectric property of the micro-hexagonal tablets was investigated. The as-synthesized tablets exhibit excellent piezoactivities in the experiments, and an effective piezoelectric coefficient of around 80 pm/V was obtained. The tablets have huge potential applications in micro/nano-integrated piezoelectric and optical devices.

  10. Control of coercive field in lithium niobate crystals with repeated polarization reversal

    International Nuclear Information System (INIS)

    Ro, Jung Hoon; Jeong, Doun; Park, Taeyong; Kim, Chulhan; Kwon, Soon-Bok; Cha, Myoungsik; Choi, Byeong Cheol; Yu, Nanei; Kurimura, Sunao; Jeon, Gyerok

    2005-01-01

    In this study, the amount of decrease in coercive field of congruent lithium niobate during repeated poling and back-poling was measured. The polarization is reversed in 300 ms and then back-poled during the rest period. The coercive field can be decreased around 1 kV/mm with a repeated poling interval of 5 s. As the interval prolonged, the poling field decrease became smaller, and a stretched exponential function is suggested for the experimental fitting resulting in a set of meaningful parameters. These values are essential for the design of high quality domain engineering

  11. Processing and characterization of lead-free ceramics on the base of sodium-potassium niobate

    Science.gov (United States)

    Politova, E. D.; Golubko, N. V.; Kaleva, G. M.; Mosunov, A. V.; Sadovskaya, N. V.; Stefanovich, S. Yu.; Kiselev, D. A.; Kislyuk, A. M.; Panda, P. K.

    Lead-free sodium-potassium niobate-based piezoelectric materials are most intensively studied in order to replace the widely used Pb-based ones. In this work, the effects of modification of compositions by donor and acceptor dopants in the A- and B-sites of perovskite lattice on structure, dielectric, ferroelectric, and piezoelectric properties of ceramics from Morphotropic Phase Boundary in the (1-x)(K0.5Na0.5)NbO3-xBaTiO3 system and in compositions with x=0.05 and 0.06 additionally doped by Ni3+ cations have been studied.

  12. Porosity Dependence of Piezoelectric Properties for Porous Potassium Niobate System Ceramics

    Energy Technology Data Exchange (ETDEWEB)

    Wada, S; Mase, Y; Shimizu, S; Maeda, K; Fujii, I; Nakashima, K; Pulpan, P; Miyajima, N, E-mail: swada@yamanashi.ac.jp [Interdisciplinary Graduate School of Medical and Engineering, University of Yamanashi, 4-4-37 Takeda, Kofu, Yamanashi 400-8510 (Japan)

    2011-10-29

    Porous potassium niobate (KNbO{sub 3}, KN) system ceramics were prepared by a conventional sintering method using carbon black (CB) nanoparticles. First, KN nanoparticles with a size of 100 nm was mixed with CB nanoparticles and binder using ball milling with ethanol. The mixture was dried, and pressed into pellets using uniaxial pressing. After binder burnout, these ceramics was sintered in air. Their piezoelectric properties were measured and discussed a relationship between porosity and piezoelectric properties. As the results, with increasing porosity, piezoelectric g33 constant increased significantly, which suggested that porous ceramics were effective for stress sensor application.

  13. Radiation-damage-assisted ferroelectric domain structuring in magnesium-doped lithium niobate

    Science.gov (United States)

    Jentjens, L.; Peithmann, K.; Maier, K.; Steigerwald, H.; Jungk, T.

    2009-06-01

    Irradiation of 5% magnesium-doped lithium niobate crystals (LiNbO3:Mg) with high-energy, low-mass 3He ions, which are transmitted through the crystal, changes the domain reversal properties of the material. This enables easier domain engineering compared to non-irradiated material and assists the formation of small-sized periodically poled domains in LiNbO3:Mg. Periodic domain structures exhibiting a width of ≈520 nm are obtained in radiation-damaged sections of the crystals. The ferroelectric poling behavior between irradiated and non-treated material is compared.

  14. Tuning characteristics of narrowband THz radiation generated via optical rectification in periodically poled lithium niobate.

    Science.gov (United States)

    Weiss, C; Torosyan, G; Meyn, J P; Wallenstein, R; Beigang, R; Avetisyan, Y

    2001-04-23

    The tuning properties of pulsed narrowband THz radiation generated via optical rectification in periodically poled lithium niobate have been investigated. Using a disk-shaped periodically poled crystal tuning was easily accomplished by rotating the crystal around its axis and observing the generated THz radiation in forward direction. In this way no beam deflection during tuning was observed. The total tuning range extended from 180 GHz up to 830 GHz and was limited by the poling period of 127 microm which determines the maximum THz frequency in forward direction.

  15. Continuous wave ultraviolet radiation induced frustration of etching in lithium niobate single crystals

    Energy Technology Data Exchange (ETDEWEB)

    Mailis, S.; Riziotis, C.; Smith, P.G.R.; Scott, J.G.; Eason, R.W

    2003-02-15

    Illumination of the -z face of congruent lithium niobate single crystals with continuous wave (c.w.) ultraviolet (UV) laser radiation modifies the response of the surface to subsequent acid etching. A frequency doubled Ar{sup +} laser ({lambda}=244 nm) was used to illuminate the -z crystal face making it resistive to HF etching and thus transforming the illuminated tracks into ridge structures. This process enables the fabrication of relief patterns in a photolithographic manner. Spatially resolved Raman spectroscopy indicates preservation of the good crystal quality after irradiation.

  16. Diffusion of iron in lithium niobate: a secondary ion mass spectrometry study

    Energy Technology Data Exchange (ETDEWEB)

    Ciampolillo, M.V.; Argiolas, N.; Zaltron, A.; Bazzan, M.; Sada, C. [University of Padova, Physics Department (Italy); CNISM, Padova (Italy)

    2011-10-15

    Iron-doped X-cut lithium niobate crystals were prepared by means of thermal diffusion from thin film varying in a systematic way the process parameters such as temperature and diffusion duration. Secondary Ion Mass Spectrometry was exploited to characterize the iron in-depth profiles. The evolution of the composition of the Fe thin film in the range between 600 C and 800 C was studied, and the diffusion coefficient at different temperatures in the range between 900 C and 1050 C and the activation energy of the diffusion process were estimated. (orig.)

  17. Aperture scaling effects with monolithic periodically poled lithium niobate optical parametric oscillators and generators.

    Science.gov (United States)

    Missey, M; Dominic, V; Powers, P; Schepler, K L

    2000-02-15

    We used elliptical beams to demonstrate aperture scaling effects in nanosecond single-grating and multigrating periodically poled lithium niobate (PPLN) monolithic optical parametric oscillators and generators. Increasing the cavity Fresnel number in single-grating crystals broadened both the beam divergence and the spectral bandwidth. Both effects are explained in terms of the phase-matching geometry. These effects are suppressed when a multigrating PPLN crystal is used because the individual gratings provide small effective subapertures. A flood-pumped multigrating optical parametric generator displayed a low output beam divergence and contained 19 pairs of signal and idler frequencies.

  18. Investigation of the cluster formation in lithium niobate crystals by computer modeling method

    Energy Technology Data Exchange (ETDEWEB)

    Voskresenskii, V. M.; Starodub, O. R., E-mail: ol-star@mail.ru; Sidorov, N. V.; Palatnikov, M. N. [Russian Academy of Sciences, Tananaev Institute of Chemistry and Technology of Rare Earth Elements and Mineral Raw Materials, Kola Science Centre (Russian Federation)

    2017-03-15

    The processes occurring upon the formation of energetically equilibrium oxygen-octahedral clusters in the ferroelectric phase of a stoichiometric lithium niobate (LiNbO{sub 3}) crystal have been investigated by the computer modeling method within the semiclassical atomistic model. An energetically favorable cluster size (at which a structure similar to that of a congruent crystal is organized) is shown to exist. A stoichiometric cluster cannot exist because of the electroneutrality loss. The most energetically favorable cluster is that with a Li/Nb ratio of about 0.945, a value close to the lithium-to-niobium ratio for a congruent crystal.

  19. Domain-Reversed Lithium Niobate Single-Crystal Fibers are Potentially for Efficient Terahertz Wave Generation

    Directory of Open Access Journals (Sweden)

    Yalin Lu

    2008-01-01

    Full Text Available Nonlinear frequency conversion remains one of the dominant approaches to efficiently generate THz waves. Significant material absorption in the THz range is the main factor impeding the progress towards this direction. In this research, a new multicladding nonlinear fiber design was proposed to solve this problem, and as the major experimental effort, periodic domain structure was introduced into lithium niobate single-crystal fibers by electrical poling. The introduced periodic domain structures were nondestructively revealed using a crossly polarized optical microscope and a confocal scanning optical microscope for quality assurance.

  20. Porosity Dependence of Piezoelectric Properties for Porous Potassium Niobate System Ceramics

    International Nuclear Information System (INIS)

    Wada, S; Mase, Y; Shimizu, S; Maeda, K; Fujii, I; Nakashima, K; Pulpan, P; Miyajima, N

    2011-01-01

    Porous potassium niobate (KNbO 3 , KN) system ceramics were prepared by a conventional sintering method using carbon black (CB) nanoparticles. First, KN nanoparticles with a size of 100 nm was mixed with CB nanoparticles and binder using ball milling with ethanol. The mixture was dried, and pressed into pellets using uniaxial pressing. After binder burnout, these ceramics was sintered in air. Their piezoelectric properties were measured and discussed a relationship between porosity and piezoelectric properties. As the results, with increasing porosity, piezoelectric g33 constant increased significantly, which suggested that porous ceramics were effective for stress sensor application.

  1. Preparation and photocatalytic property of potassium niobate K6Nb10.8O30

    International Nuclear Information System (INIS)

    Zhang Gaoke; Zou Xi; Gong Jie; He Fangsheng; Zhang Hao; Zhang Qiang; Liu Ying; Yang Xia; Hu Bo

    2006-01-01

    The TB-type potassium niobate K 6 Nb 10.8 O 30 was synthesized by a simple solid-state reaction method. Scanning electron microscope (SEM) and X-ray diffractometer (XRD) were used to characterize the structure of the photocatalyst. The photocatalyst K 6 Nb 10.8 O 30 shows high photocatalytic activity to photodegrade acid red G under UV irradiation. The influences of catalyst dosage, initial concentration of acid red G on the photocatalytic reaction were investigated. The kinetics of photocatalytic degradation of acid red G follows the first order kinetics

  2. Processing and characterization of lead-free ceramics on the base of sodium–potassium niobate

    Directory of Open Access Journals (Sweden)

    E. D. Politova

    2018-02-01

    Full Text Available Lead-free sodium–potassium niobate-based piezoelectric materials are most intensively studied in order to replace the widely used Pb-based ones. In this work, the effects of modification of compositions by donor and acceptor dopants in the A- and B-sites of perovskite lattice on structure, dielectric, ferroelectric, and piezoelectric properties of ceramics from Morphotropic Phase Boundary in the (1−x(K0.5Na0.5NbO3–xBaTiO3 system and in compositions with x=0.05 and 0.06 additionally doped by Ni3+ cations have been studied.

  3. GLASS BOX

    National Research Council Canada - National Science Library

    Curtis, Laura

    2008-01-01

    The goals of this effort were to develop Glass Box capabilities to allow for the capturing of analyst activities and the associated data resources, track and log the results of automated processing...

  4. Cost-effectiveness of barium enemas performed by radiographers

    International Nuclear Information System (INIS)

    Brown, Lorraine; Desai, Sharad

    2002-01-01

    AIM: To assess the cost-effectiveness of barium enemas performed by radiographers compared to those performed by consultant radiologists. METHOD: Prospective study of 200 barium enemas carried out by a senior radiographer and a consultant radiologist. The sample was a consecutive sample of adult out-patients over a 3-month period, with no exclusion. The length of time of the enema and the numbers and grades of staff involved in the procedure were recorded. This was translated into staffing costs using the appropriate pay scales. RESULTS: The barium enemas performed by the superintendent radiographer were more cost-effective than those performed by the consultant radiologist (1406 pounds for 100 radiographer-performed barium enemas compared to 1787 pounds for 100 carried out by the consultant radiologist). CONCLUSION: In terms of staffing costs, radiographers performing barium enemas not only liberates radiologist time, it is also a cost-effective method of providing an out-patient barium enema service. Brown, L. and Desai, S. (2002)

  5. Structure of TeO2 - LiNbO3 glasses

    Science.gov (United States)

    Shinde, A. B.; Krishna, P. S. R.; Rao, Rekha

    2017-05-01

    Tellurite based lithium niobate glasses with composition (100-x)TeO2-xLiNbO3 (x=0.1,0.2 & 0.3) were prepared by conventional melt quenching method. The microscopic structural investigation of these glasses is carried out by means of neutron diffraction and Raman scattering measurements. It is found that the basic structural units in these glasses are TeO4 trigonal bipyramids(TBP), TeO3 trigonal pyramids(TP) and NbO6 Octahedra depending on the composition. It is evident from Raman studies that TBPs decreases, TPs increases and NbO6 Octahedra increases with increasing x. From Neutron diffraction studies it is found that network is comprised of TBPs and TPs along with TeO3+1 structural units. Distorted NbO6 octahedral units are present and also increase with the increase in x.

  6. Gamma radiation induced changes in nuclear waste glass containing Eu

    Science.gov (United States)

    Mohapatra, M.; Kadam, R. M.; Mishra, R. K.; Kaushik, C. P.; Tomar, B. S.; Godbole, S. V.

    2011-10-01

    Gamma radiation induced changes were investigated in sodium-barium borosilicate glasses containing Eu. The glass composition was similar to that of nuclear waste glasses used for vitrifying Trombay research reactor nuclear waste at Bhabha Atomic Research Centre, India. Photoluminescence (PL) and electron paramagnetic resonance (EPR) techniques were used to study the speciation of the rare earth (RE) ion in the matrix before and after gamma irradiation. Judd-Ofelt ( J- O) analyses of the emission spectra were done before and after irradiation. The spin counting technique was employed to quantify the number of defect centres formed in the glass at the highest gamma dose studied. PL data suggested the stabilisation of the trivalent RE ion in the borosilicate glass matrix both before and after irradiation. It was also observed that, the RE ion distributes itself in two different environments in the irradiated glass. From the EPR data it was observed that, boron oxygen hole centre based radicals are the predominant defect centres produced in the glass after irradiation along with small amount of E’ centres. From the spin counting studies the concentration of defect centres in the glass was calculated to be 350 ppm at 900 kGy. This indicated the fact that bulk of the glass remained unaffected after gamma irradiation up to 900 kGy.

  7. Anastomotic stenosis of the descending colon caused by barium granuloma formation following barium peritonitis: report of a case.

    Science.gov (United States)

    Kitajima, Toshihiro; Tomizawa, Kenji; Hanaoka, Yutaka; Toda, Shigeo; Matoba, Shuichiro; Kuroyanagi, Hiroya; Oota, Yasunori

    2014-11-01

    Anastomotic stricture reportedly often recurs following barium peritonitis, regardless of whether the anastomotic diameter is initially sufficient. However, the causes of repetitive stricture have not been clarified. We report a case that suggests the pathophysiology of recurrent anastomotic strictures following barium peritonitis. The patient was a 39-year-old Japanese man with idiopathic perforation of the descending colon after undergoing an upper gastrointestinal barium contrast study. After emergency peritoneal lavage and diverting colostomy, created using the perforated region, the patient recovered uneventfully and 3 months later, the colostomy was closed and the perforated colon was resected. However, 7 months after colostomy closure, abdominal distention gradually developed, and colonoscopy revealed an anastomotic stricture. The patient was referred to our hospital where he underwent resection of the anastomotic stricture. The surgical specimen exhibited barium granulomas not only in the subserosa of the entire specimen, but also in the submucosa and lamina propria localized in the anastomotic site. These findings suggest that barium was embedded in the submucosa and lamina propria with manipulation of the stapled anastomosis and that the barium trapped in the anastomotic site caused persistent inflammation, resulting in an anastomotic stricture.

  8. Surface acoustic waves in acoustic superlattice lithium niobate coated with a waveguide layer

    Science.gov (United States)

    Yang, G. Y.; Du, J. K.; Huang, B.; Jin, Y. A.; Xu, M. H.

    2017-04-01

    The effects of the waveguide layer on the band structure of Rayleigh waves are studied in this work based on a one-dimensional acoustic superlattice lithium niobate substrate coated with a waveguide layer. The present phononic structure is formed by the periodic domain-inverted single crystal that is the Z-cut lithium niobate substrate with a waveguide layer on the upper surface. The plane wave expansion method (PWE) is adopted to determine the band gap behavior of the phononic structure and validated by the finite element method (FEM). The FEM is also used to investigate the transmission of Rayleigh waves in the phononic structure with the interdigital transducers by means of the commercial package COMSOL. The results show that, although there is a homogeneous waveguide layer on the surface, the band gap of Rayleigh waves still exist. It is also found that increasing the thickness of the waveguide layer, the band width narrows and the band structure shifts to lower frequency. The present approach can be taken as an efficient tool in designing of phononic structures with waveguide layer.

  9. Bending waveguides made in x-cut lithium niobate crystals for technological applications

    International Nuclear Information System (INIS)

    Guarepi, V; Perrone, C; Aveni, M; Videla, F; Torchia, GA

    2015-01-01

    In this paper we analyse the performance of several designs of integrated optical deviators made in x-cut lithium niobate crystals by means of femtosecond laser writing using the double line approach. Straight and bent guiding structures have been designed and implemented using this technique. Well-confined propagation modes at communication wavelengths (1.55 μm) were conducted in these structures with acceptable overall losses (less than 2 dB cm −1 ). Further, a discussion about the optical propagation losses for curved and straight deviators devices is included in this work. At a low aperture angle (less than 0.2°), as expected, low losses were determined for both structures; however, a weak output light was observed for large angles (greater than 0.2°) in the straight optical circuits. In contrast, a smooth variation of the output was measured for the bent structures. The results presented in this paper support the possibility of the technological implementation of integrated optical circuits for optical communications fabricated with ultrashort laser writing in lithium niobate crystals. In addition, some hypotheses of loss mechanisms that are normally not considered are discussed in order to explain the differences between the measured values and predictions obtained by calculating with the usual models. (paper)

  10. Irradiation-induced modification of the material parameters in magnesium-doped lithium niobate

    International Nuclear Information System (INIS)

    Jentjens, Lena

    2010-01-01

    In the framework of this thesis the material properties of lithium niobate are directedly influenced by the irradiation with 3 He ions with an energy of 40 MeV. In the first part the irradiation-induced material changes are intensively studied. Long-time stable changes of the refractive index are measured in the range of up to 6.10 -3 , which depend on the radiation dose and exhibit until now no saturation behaviour. Accompanied is this change by an also dose-dependent deformation as well as a brownish change of color of the crystals. Furthermore a by several orders of magnitude increased electrical dark- and photoconductivity, which depends on the ion dose and exhibits until now also no saturation behaviour. An effect independent on the ion dose is the reduction of the coercive field strength by about 10%. Furthermore it was stated the quantity of the effects not only depends on the absolute dose, but also on the irradiation direction in view of the crystallographic c-axis. The second part of this thesis deals with the generation of microscopic structures in lithium niobate. By an ion microbeam respectively a shiftable slit aperture the fabrication of refractive-index gratings is pursued. Grating with periodicity lengths in the range of 12-160 μm could until now be detected and promise in comparison with photorefractive gratings the advance of larger stability.

  11. Periodic domain inversion in x-cut single-crystal lithium niobate thin film

    Energy Technology Data Exchange (ETDEWEB)

    Mackwitz, P., E-mail: peterm@mail.upb.de; Rüsing, M.; Berth, G.; Zrenner, A. [Department Physik, Universität Paderborn, 33095 Paderborn (Germany); Center for Optoelectronics and Photonics Paderborn, 33095 Paderborn (Germany); Widhalm, A.; Müller, K. [Department Physik, Universität Paderborn, 33095 Paderborn (Germany)

    2016-04-11

    We report the fabrication of periodically poled domain patterns in x-cut lithium niobate thin-film. Here, thin films on insulator have drawn particular attention due to their intrinsic waveguiding properties offering high mode confinement and smaller devices compared to in-diffused waveguides in bulk material. In contrast to z-cut thin film lithium niobate, the x-cut geometry does not require back electrodes for poling. Further, the x-cut geometry grants direct access to the largest nonlinear and electro-optical tensor element, which overall promises smaller devices. The domain inversion was realized via electric field poling utilizing deposited aluminum top electrodes on a stack of LN thin film/SiO{sub 2} layer/Bulk LN, which were patterned by optical lithography. The periodic domain inversion was verified by non-invasive confocal second harmonic microscopy. Our results show domain patterns in accordance to the electrode mask layout. The second harmonic signatures can be interpreted in terms of spatially, overlapping domain filaments which start their growth on the +z side.

  12. Surface acoustic waves in acoustic superlattice lithium niobate coated with a waveguide layer

    Directory of Open Access Journals (Sweden)

    G. Y. Yang

    2017-04-01

    Full Text Available The effects of the waveguide layer on the band structure of Rayleigh waves are studied in this work based on a one-dimensional acoustic superlattice lithium niobate substrate coated with a waveguide layer. The present phononic structure is formed by the periodic domain-inverted single crystal that is the Z-cut lithium niobate substrate with a waveguide layer on the upper surface. The plane wave expansion method (PWE is adopted to determine the band gap behavior of the phononic structure and validated by the finite element method (FEM. The FEM is also used to investigate the transmission of Rayleigh waves in the phononic structure with the interdigital transducers by means of the commercial package COMSOL. The results show that, although there is a homogeneous waveguide layer on the surface, the band gap of Rayleigh waves still exist. It is also found that increasing the thickness of the waveguide layer, the band width narrows and the band structure shifts to lower frequency. The present approach can be taken as an efficient tool in designing of phononic structures with waveguide layer.

  13. Barium low concentration determination in solutions using X rays energy spectrometry

    International Nuclear Information System (INIS)

    Barbosa, Joao Batista Santos; Pereira, Jose dos Santos Jorge

    1999-01-01

    This work was proposed to establish an analytical methodology for barium determination in samples from the Waste Supervision of CDTN. Barium is the focus here because it has the same chemical behaviour as radium. Therefore, barium can replace it as an inactive tracer in contention matrix studies. The methodology is made up of two phases; physical concentration and barium determination by an Energy Dispersive Spectrometer using an Am 241 photon excitation system. A very good set of results is found when Am 241 is used in fluorescing barium atoms. This fact, in addition to the physical concentration process, allows to detect up 12 ppb of elementary barium. (author)

  14. The efficacy of steroids for postoperative persistent inflammatory reaction in a patient with barium peritonitis: A case report

    Directory of Open Access Journals (Sweden)

    Hirofumi Kojima

    2017-01-01

    Conclusion: Residual barium in the intraperitoneal cavity causes persistent inflammatory reaction in patients with barium peritonitis. The use of steroids is effective for postoperative persistent inflammation due to the residual barium.

  15. High H⁻ ionic conductivity in barium hydride.

    Science.gov (United States)

    Verbraeken, Maarten C; Cheung, Chaksum; Suard, Emmanuelle; Irvine, John T S

    2015-01-01

    With hydrogen being seen as a key renewable energy vector, the search for materials exhibiting fast hydrogen transport becomes ever more important. Not only do hydrogen storage materials require high mobility of hydrogen in the solid state, but the efficiency of electrochemical devices is also largely determined by fast ionic transport. Although the heavy alkaline-earth hydrides are of limited interest for their hydrogen storage potential, owing to low gravimetric densities, their ionic nature may prove useful in new electrochemical applications, especially as an ionically conducting electrolyte material. Here we show that barium hydride shows fast pure ionic transport of hydride ions (H(-)) in the high-temperature, high-symmetry phase. Although some conductivity studies have been reported on related materials previously, the nature of the charge carriers has not been determined. BaH2 gives rise to hydride ion conductivity of 0.2 S cm(-1) at 630 °C. This is an order of magnitude larger than that of state-of-the-art proton-conducting perovskites or oxide ion conductors at this temperature. These results suggest that the alkaline-earth hydrides form an important new family of materials, with potential use in a number of applications, such as separation membranes, electrochemical reactors and so on.

  16. Barium enema in frail elderly patients.

    Science.gov (United States)

    Segal, R; Khahil, A; Leibovitz, A; Gil, I; Annuar, M; Habot, B

    2000-01-01

    Barium enema (BE) examinations for the investigation of suspected colonic disease are often unsuccessful in elderly patients. The purpose of this study was to evaluate the success rate of BE in hospitalized frail elderly patients. Four hundred and seventy-two elderly patients hospitalized for different reasons underwent BE examinations. The medical charts and radiological reports were retrospectively reviewed. One hundred and ninety-two (41%) BE examinations were considered inadequate; mostly (32%) because of inappropriate preparation. Sixty-seven patients (14%) were not cooperative and could not retain the contrast material, and in 25 patients (5%), the examination failed due to both these reasons. The characteristics associated with unsuccessful BE examination were the mean number of medical problems (p < 0.001), the mean number of scheduled medications (p < 0.05) and in particular the long-term use of laxatives (p < 0.01) or antiparkinsonian drugs (p < 0.01). Of great significance in predicting an inadequate BE were the patient's functional status (p < 0.001) and the presence of dementia (p < 0.001). The high percentage of unsuccessful BEs in the frail elderly suggests that clinicians should carefully consider the need for that examination in these patients. We suggest that only in patients where there is a clear suspicion of a bleeding or obstructing tumor should a BE examination be performed, and even in these cases, colonoscopy or CT may be preferable as the initial examination in the frail elderly. Copyright 2000 S. Karger AG, Basel

  17. Effectiveness of therapeutic barium enema for diverticular hemorrhage.

    Science.gov (United States)

    Matsuura, Mizue; Inamori, Masahiko; Nakajima, Atsushi; Komiya, Yasuhiko; Inoh, Yumi; Kawasima, Keigo; Naitoh, Mai; Fujita, Yuji; Eduka, Akiko; Kanazawa, Noriyoshi; Uchiyama, Shiori; Tani, Rie; Kawana, Kennichi; Ohtani, Setsuya; Nagase, Hajime

    2015-05-14

    To evaluate the effectiveness of barium impaction therapy for patients with colonic diverticular bleeding. We reviewed the clinical charts of patients in whom therapeutic barium enema was performed for the control of diverticular bleeding between August 2010 and March 2012 at Yokohama Rosai Hospital. Twenty patients were included in the review, consisting of 14 men and 6 women. The median age of the patients was 73.5 years. The duration of the follow-up period ranged from 1 to 19 mo (median: 9.8 mo). Among the 20 patients were 11 patients who required the procedure for re-bleeding during hospitalization, 6 patients who required it for re-bleeding that developed after the patient left the hospital, and 3 patients who required the procedure for the prevention of re-bleeding. Barium (concentration: 150 w%/v%) was administered per the rectum, and the leading edge of the contrast medium was followed up to the cecum by fluoroscopy. After confirmation that the ascending colon and cecum were filled with barium, the enema tube was withdrawn, and the patient's position was changed every 20 min for 3 h. Twelve patients remained free of re-bleeding during the follow-up period (range: 1-19 mo) after the therapeutic barium enema, including 9 men and 3 women with a median age of 72.0 years. Re-bleeding occurred in 8 patients including 5 men and 3 women with a median age of 68.5 years: 4 developed early re-bleeding, defined as re-bleeding that occurs within one week after the procedure, and the remaining 4 developed late re-bleeding. The DFI (disease-free interval) decreased 0.4 for 12 mo. Only one patient developed a complication from therapeutic barium enema (colonic perforation). Therapeutic barium enema is effective for the control of diverticular hemorrhage in cases where the active bleeding site cannot be identified by colonoscopy.

  18. The diagnostic value of barium enema in acute appendicitis

    International Nuclear Information System (INIS)

    Kim, Yong Ga; Chung, Duck Soo; Kim, Ok Dong

    1986-01-01

    Acute appendicitis is the most common acute surgical condition of the abdomen. When the clinical presentation is atypical, barium enema has proven to be safe and useful in confirming the diagnosis and reducing the negative surgical exploration. However, the performance of barium enema in acute appendicitis has known contraindication primarily because of fear of leakage by perforation of the inflamed appendix. This study using barium enema as a diagnostic aid in acute appendicitis with atypical clinical presentation was performed to further support the previously noted efficacy and safety of this procedure. The results were as followings: 1. In case of acute appendicitis with atypical clinical presentation, the use of barium enema as a diagnostic aid increased the accuracy of diagnosis and decreased the negative surgical exploration. In women between 11 to 50 years old age, especially, it played important role differentiating appendicitis from nonsurgical acute abdomen. 2. The results of the study were 92.31% in sensitivity, 7.69% in false positive, 6.9% in false negative, and 10.26% in negative appendectomy. 3. None of case of leakage of barium by perforation of the inflamed appendix was noted, therefore, barium enema was thought to be safe as a diagnostic aid in acute appendicitis. 4. A simple partial or non filling of appendix without other associated positive finding could not exclude appendicitis, therefore, close clinical observation was necessary. 5. The positive findings of barium enema and their sensitivity were as followings: 1. Non filling of appendix: 90% 2. Partial filling of appendix: 91.7% 3. Displacement or a local impression on terminal ileum: 100%

  19. Lead isotope ratios of ancient Chinese and Japanese glasses

    International Nuclear Information System (INIS)

    Yamasaki, Kazuo; Murozumi, Masayo; Nakamura, Seiji; Yuasa, Mitsuaki; Watarai, Motohiko.

    1980-01-01

    Lead isotope ratios of 29 archaeological glass samples (5 samples excavated in China, 10 samples excavated in Japan, and 14 samples made in Japan) were determined by surface ionization mass spectrometry with a HITACHI RMU-6 spectrometer. Of these glass samples, 28 were made of high lead glass, and one, of alkali-lime glass. Glass samples were decomposed in a mixture of hydrofluoric and nitric acids, and lead was separated from other elements by extraction with dithizone-chloroform. The lead nitrate solution thus prepared (corresponding to 0.5 μg Pb) was loaded on the rhenium single filament. The coefficients of variation of the determined ratios, 207 Pb/ 206 Pb and 208 Pb/ 206 Pb, were 0.1 -- 0.3%. Among the glasses excavated in Japan, some samples of the Yayoi period (ca. 3 rd C. B.C. -- ca. 3 rd C. A.D.) contained a large amount of barium in addition to lead, and resembled closely Chinese pre-Han glasses not only in chemical compositions, but also in lead isotope ratios. This means that pre-Han glasses were brought to Japan and then re-cast into glass beads characteristic of Japan. The lead isotope ratios of the glasses were compared with those of Chinese (2 samples), Korean (2) and Japanese (17) galena orea, and it was found that 12 glass beads made in the 8th century at Nara and 2 fine glass tubes made at Saga in the 18 th -- 19 th centuries showed similar lead isotope ratios with those of the Japanese galena ores. Consequently it is considered that the Japanese galena ores were already used as one of raw materials at manufacturing of these glass beads in ancient centuries. (author)

  20. Glass compositions

    Energy Technology Data Exchange (ETDEWEB)

    France, P W

    1985-05-30

    A fluoride glass for use in the production of optical fibres has an enhanced D/H ratio, preferably such that OD:OH is at least 9:1. In the example, such a glass is prepared by treating with D/sub 2/O a melt comprising 51.53 mole per cent ZrF/sub 4/, 20.47 mole per cent BaF/sub 2/, 5.27 mole per cent LaF/sub 3/, 3.24 mole per cent AlF/sub 3/, and 19.49 mole per cent LiF.

  1. Freeze cast porous barium titanate for enhanced piezoelectric energy harvesting

    Science.gov (United States)

    Roscow, J. I.; Zhang, Y.; Kraśny, M. J.; Lewis, R. W. C.; Taylor, J.; Bowen, C. R.

    2018-06-01

    Energy harvesting is an important developing technology for a new generation of self-powered sensor networks. This paper demonstrates the significant improvement in the piezoelectric energy harvesting performance of barium titanate by forming highly aligned porosity using freeze casting. Firstly, a finite element model demonstrating the effect of pore morphology and angle with respect to poling field on the poling behaviour of porous ferroelectrics was developed. A second model was then developed to understand the influence of microstructure-property relationships on the poling behaviour of porous freeze cast ferroelectric materials and their resultant piezoelectric and energy harvesting properties. To compare with model predictions, porous barium titanate was fabricated using freeze casting to form highly aligned microstructures with excellent longitudinal piezoelectric strain coefficients, d 33. The freeze cast barium titanate with 45 vol.% porosity had a d 33  =  134.5 pC N‑1 compared to d 33  =  144.5 pC N‑1 for dense barium titanate. The d 33 coefficients of the freeze cast materials were also higher than materials with uniformly distributed spherical porosity due to improved poling of the aligned microstructures, as predicted by the models. Both model and experimental data indicated that introducing porosity provides a large reduction in the permittivity () of barium titanate, which leads to a substantial increase in energy harvesting figure of merit, , with a maximum of 3.79 pm2 N‑1 for barium titanate with 45 vol.% porosity, compared to only 1.40 pm2 N‑1 for dense barium titanate. Dense and porous barium titanate materials were then used to harvest energy from a mechanical excitation by rectification and storage of the piezoelectric charge on a capacitor. The porous barium titanate charged the capacitor to a voltage of 234 mV compared to 96 mV for the dense material, indicating a 2.4-fold increase that was similar to that

  2. Fabry-Perot measurements of barium temperature in fluorescent lamps

    International Nuclear Information System (INIS)

    Hadrath, S; Garner, R

    2010-01-01

    A scanning Fabry-Perot interferometer (FPI) is used to determine the temperature of barium atoms that are liberated from the electrodes of fluorescent lamps during their steady-state operation. Barium, a constituent of the work function lowering emitter material that is placed on the tungsten coil that forms the electrode, is liberated primarily by evaporation from the hot (∼1300 K) thermionic electrode. However, there may be situations or modes of operation in which barium is, in addition, sputtered, a condition which may lead to increased end-darkening, shortened life and increased mercury consumption in the lamp. Using the FPI diagnostic, the occurrence of sputtering is inferred when barium temperatures are much greater than the electrode temperature. The FPI diagnostic senses resonance radiation (λ = 553 nm) emitted by barium atoms excited in the low pressure discharge environment, and infers temperature from the Doppler broadened linewidth. The diagnostic has proven to be successful in a number of situations. Measurements have been made on rare gas discharges and on Hg-argon discharges for different discharge currents, gas pressures and auxiliary coil currents. Measurements are phase resolved for ac-driven discharges.

  3. Air (CO2) double-contrast barium enteroclysis.

    Science.gov (United States)

    Maglinte, Dean D T; Kohli, Marc D; Romano, Stefania; Lappas, John C

    2009-09-01

    In the 1980s and 1990s in North America and Europe, air (CO(2)) double-contrast barium enteroclysis took a back seat to biphasic methylcellulose double-contrast enteroclysis in the investigation of small-bowel diseases. The widespread application of capsule endoscopy in the 21st century has identified a number of limitations of radiologic examinations in the investigation of mucosal diseases of the small intestine. Evidence-based studies comparing barium, computed tomographic (CT), and magnetic resonance (MR) enteroclysis have shown that in spite of improvements in small-bowel examination methods using CT and MR, barium examinations remain superior in the depiction of mucosal abnormalities, particularly the apthoid lesions of early Crohn disease. Barium small-bowel examinations have been recommended in the patient with a negative CT or MR enteroclysis study where the pretest probability of Crohn disease is high. A recent prospective comparison of methylcellulose double-contrast barium enteroclysis to capsule endoscopy with review of the literature has shown that air enteroclysis depicts mucosal details better than does methylcellulose double-contrast enteroclysis because of the "washout" effect of methylcellulose on superficial mucosal features. Recent articles have shown that air enteroclysis compares favorably with wireless capsule endoscopy and double-balloon endoscopy in the diagnosis of mucosal abnormalities of the small bowel. This article describes the authors' technique of performing air double-contrast enteroclysis, its clinical indications, and its pitfalls.

  4. Creating unstable velocity-space distributions with barium injections

    International Nuclear Information System (INIS)

    Pongratz, M.B.

    1983-01-01

    Large Debye lengths relative to detector dimensions and the absence of confining walls makes space an attractive laboratory for studying fundamental theories of plasma instabilities. However, natural space plasmas are rarely found displaced from equilibrium enough to permit isolation and diagnosis of the controlling parameters and driving conditions. Furthermore, any plasma or field response to the departure from equilibrium can be masked by noise in the natural system. Active experiments provide a technique for addressing the chicken or egg dilemma. Early thermite barium releases were generally conducted at low altitudes from sounding rockets to trace electric fields passively or to study configuration-space instabilities. One can also study velocity-space instabilities with barium releases. Neutral barium vapor releases wherein a typical speed greatly exceeds the thermal speed can be used to produce barium ion velocity-space distributions that should be subject to a number of microinstabilities. We examine the ion velocity-space distributions resulting from barium injections from orbiting spacecraft and shaped-charges

  5. Barium Depletion in the NSTAR Discharge Cathode After 30,000 Hours of Operation

    Science.gov (United States)

    Polk, James E.; Capece, Angela M.; Mikellides, Ioannis G.; Katz, Ira

    2010-01-01

    Dispenser hollow cathodes rely on a consumable supply of barium released by impregnant materials in the pores of a tungsten matrix to maintain a low work function surface. Examinations of cathode inserts from long duration ion engine tests show deposits of tungsten at the downstream end that appear to block the flow of barium from the interior. In addition, a numerical model of barium transport in the insert plasma indicates that the barium partial pressure in the insert may exceed the equilibrium vapor pressure of the dominant barium-producing reaction, and it was postulated previously that this would suppress barium loss in the upstream part of the insert. New measurements of the depth of barium depletion from a cathode insert operated for 30,352 hours reveal that barium loss is confined to a narrow region near the downstream end, confirming this hypothesis.

  6. Controlling Barium Sulphate Scale Deposition Problems in an unbleached Kraft Paper Mill

    CSIR Research Space (South Africa)

    Sithole, Bruce

    2015-06-01

    Full Text Available Troubleshooting of scale deposits and defects in paper samples showed that the problem was caused by barium sulphate and calcium sulphate scales. However, it was ascertained that barium sulphate was more of a concern than calcium sulphate...

  7. Selectivity in biomineralization of barium and strontium.

    Science.gov (United States)

    Krejci, Minna R; Wasserman, Brian; Finney, Lydia; McNulty, Ian; Legnini, Daniel; Vogt, Stefan; Joester, Derk

    2011-11-01

    The desmid green alga Closterium moniliferum belongs to a small number of organisms that form barite (BaSO(4)) or celestite (SrSO(4)) biominerals. The ability to sequester Sr in the presence of an excess of Ca is of considerable interest for the remediation of (90)Sr from the environment and nuclear waste. While most cells dynamically regulate the concentration of the second messenger Ca(2+) in the cytosol and various organelles, transport proteins rarely discriminate strongly between Ca, Sr, and Ba. Herein, we investigate how these ions are trafficked in C. moniliferum and how precipitation of (Ba,Sr)SO(4) crystals occurs in the terminal vacuoles. Towards this goal, we simultaneously visualize intracellular dynamics of multiple elements using X-ray fluorescence microscopy (XFM) of cryo-fixed/freeze-dried samples. We correlate the resulting elemental maps with ultrastructural information gleaned from freeze-fracture cryo-SEM of frozen-hydrated cells and use micro X-ray absorption near edge structure (micro-XANES) to determine sulfur speciation. We find that the kinetics of Sr uptake and efflux depend on external Ca concentrations, and Sr, Ba, and Ca show similar intracellular localization. A highly ion-selective cross-membrane transport step is not evident. Based on elevated levels of sulfate detected in the terminal vacuoles, we propose a "sulfate trap" model, where the presence of dissolved barium leads to preferential precipitation of (Ba,Sr)SO(4) due to its low solubility relative to SrSO(4) and CaSO(4). Engineering the sulfate concentration in the vacuole may thus be the most direct way to increase the Sr sequestered per cell, an important consideration in using desmids for phytoremediation of (90)Sr. Copyright © 2011 Elsevier Inc. All rights reserved.

  8. Occupational doses in pediatric barium meal procedures

    International Nuclear Information System (INIS)

    Filipov, D.; Schelin, H.R.; Denyak, V.; Legnani, A.; Ledesma, J.A.; Paschuk, S.A.; Sauzen, J.; Yagui, A.; Hoff, G.; Khoury, H.J.

    2015-01-01

    Ionizing radiation has become an indispensable tool when it comes to diagnosis and therapy. However, its use should happen in a rational manner, taking into account the risks to which the staff is being exposed. Barium meal (BM), or upper gastrointestinal (GI) studies, using fluoroscopy, are widely used for gastroesophageal reflux disease diagnostic in children and professionals are required to stay inside the examination room to position and immobilize pediatric patients during the procedure. Therefore, it is very important that proffessionals strictly follow the technical standards of radiation protection. According to the ICRP and the NCRP recommendations, the annual limit equivalent doses for eyes, thyroid and hands are, espectively, 20 mSv, 150 mSv and 500 mSv. Based on those data, the aim of the current study is to estimate the annual equivalent dose for eyes, thyroid and hands of professionals who perform BM procedures in children. This was done using properly package LiF:Mg,Cu,P thermoluminescent dosimeters in 37 procedures; 2 pairs were positioned near each staff´s eye, 2 pairs on each professional´s neck (on and under the lead protector) and 2 pairs on both staff´s hands. The range of the estimative annual equivalent doses, for eyes, thyroid and hands, are, respectively: 14 – 36 mSv, 7 – 22 mSv and 14 – 58 mSv. Only the closest staff to the patient exceeded the annual equivalent doses in the eyes (around 80% higher than the limit set by ICRP). However, the results from this study, for hands and thyroid, compared to similar studies, show higher values. Therefore, the optimization implementation is necessary, so that the radiation levels can be reduced. (authors)

  9. Material modifications in lithium niobate and lithium tantalate crystals by ion irradiation

    International Nuclear Information System (INIS)

    Raeth, Niels Lennart

    2017-01-01

    The artificially produced crystals lithium niobate (LiNbO 3 ) and the closely related lithium tantalate (LiTaO 3 ) are proven starting materials for producing active and passive devices that can guide, amplify, switch and process light. For this purpose, it is often necessary to be able to influence the refractive index of the substrate targeted, which is possible in addition to other methods by irradiation of the materials with fast light ions. In this work, lithium niobate and lithium tantalate crystals are irradiated with alpha particles, 3 He ions, deuterons, and protons at projectile energies of up to 14 MeV / nucleon. Energy and crystal thickness are chosen so that the projectiles penetrate the entire sample and are not implanted. All isotopes responsible for the unwanted nuclear activation of the crystals due to the irradiation are relatively short-lived and overall the activation decreases fast enough to allow the safe handling of the irradiated samples after a storage period of a few days to a few weeks. The refractive index changes produced in lithium niobate and lithium tantalate by irradiation with the different projectiles are determined interferometrically and can also be measured by suitable choice of the sample geometry as a function of the ion penetration depth: In LiNbO 3 the ordinary refractive index decreases, the extraordinary increases equally. In LiTaO 3 , both the ordinary and the extraordinary refractive indices decrease as a result of the irradiation; the ordinary refractive index change is many times stronger than the extraordinary one. There is an enormous long-term stability at room temperature for both crystal systems: Even after eleven (LiNbO 3 ) or three (LiTaO 3 ) years, no decrease in the ion beam-induced refractive index change can be observed. The ion beam-induced refractive index changes are probably the result of atomic displacements such as vacancies, defect clusters or ''latent tracks''. An explanation for

  10. Fabrication and properties of yttrium doped barium titanate film by RF sputtering

    International Nuclear Information System (INIS)

    Igarashi, H.; Yuasa, M.; Okazaki, K.

    1985-01-01

    Semiconductive barium titanate films were fabricated by RF sputtering on fused quartz, alumina and barium titanate ceramic substrates using barium titanate ceramic with a small amount of yttria as a target. The films on the barium titanate substrates turned blue color and showed a small PTC effect by heat-treating at 1000 0 C in the air after deposition at the substrate temperature of 600 0 C

  11. TV observations of the Barium-GEOS ion jet experiment

    International Nuclear Information System (INIS)

    Hapgood, M.A.; Collin, H.L.; Rothwell, P.

    1980-01-01

    The barium jet released by the Barium-GEOS rocket was observed by low light television cameras at Skibotn, Norway and Esrange, Sweden. The release produced a single well-defined jet containing barium ions with initial velocities between 7 and 12 km s -1 systematically slower than the velocities reported in previous experiments. Accurate data on the motion of the jet has been obtained for the first two minutes after release (up to a height of 2000 km). The orientation of the jet was close to that of an IGRF1975 model field line but was significantly different from that predicted by the Barraclough and Olson field model. The motion of the jet across the field lines was southwards with a velocity of about 150 m s -1 . (Auth.)

  12. Barium titanate thick films prepared by screen printing technique

    Directory of Open Access Journals (Sweden)

    Mirjana M. Vijatović

    2010-06-01

    Full Text Available The barium titanate (BaTiO3 thick films were prepared by screen printing technique using powders obtained by soft chemical route, modified Pechini process. Three different barium titanate powders were prepared: i pure, ii doped with lanthanum and iii doped with antimony. Pastes for screen printing were prepared using previously obtained powders. The thick films were deposited onto Al2O3 substrates and fired at 850°C together with electrode material (silver/palladium in the moving belt furnace in the air atmosphere. Measurements of thickness and roughness of barium titanate thick films were performed. The electrical properties of thick films such as dielectric constant, dielectric losses, Curie temperature, hysteresis loop were reported. The influence of different factors on electrical properties values was analyzed.

  13. Diagnostic role of barium enema in carcinoma rectum

    International Nuclear Information System (INIS)

    Asghar, M.

    2003-01-01

    Objective: The main aim of this barium enema study was to evaluate its role in patients suspected to have rectal pathologies with complaints of change in bowel habit, anorexia/weight loss, bleeding per rectum and acute/sub-acute colonic obstruction. Results: barium enema study as screening test for colo-rectal carcinoma was undertaken. Contrast outlined the colonic growth in 35 cases, out of which the cases of carcinoma colon were 24 including 13 patients suffering from carcinoma rectum. The percentage of carcinoma colon to total colonic growth was 68% while, carcinoma rectum to total carcinoma colon was 54%. Conclusion: On the basis of these investigations, it is concluded that patient's compliance is important factor in the early detection of colonic neoplasia. Though results of colonoscopy are more reliable but in practice, barium enema (double contrast) is performed initially to outline the lesion and then colonoscopy for biopsy purpose. (author)

  14. Gastrointestinal tract wall visualization and distention during abdominal and pelvic multidetector CT with a neutral barium sulphate suspension: comparison with positive barium sulphate suspension and with water.

    Science.gov (United States)

    Oliva, M R; Erturk, S M; Ichikawa, T; Rocha, T; Ros, P R; Silverman, S G; Mortele, K J

    2012-01-01

    When examining patients with contrast-enhanced multidetector-row CT, we determined if the stomach and small bowel were visualized and distended better with a neutral barium sulphate suspension than with positive barium sulphate suspension or water. After obtaining approval from our institutional review board, 156 patients (women: 84; mean age: 54 yrs) with no history of gastrointestinal tract disease were randomized prospectively to receive orally either 900 ml of neutral (0.1% w/v) barium sulphate suspension (n = 53), 900 ml of positive (2.1% w/v) barium sulphate suspension (n = 53), or 900 ml of water (n = 50), prior to undergoing contrast-enhanced abdominal and pelvic multidetector-row CT. Two independent radiologists evaluated the stomach, and small bowel, for luminal distension and wall visualization, using a five point scale. Results were compared using Kruskal-Wallis and Mann-Whitney U tests. The walls of the stomach, and small bowel were visualized better in patients who were administered neutral barium sulphate suspension than those who were administered either positive barium sulphate suspension (p barium sulphate suspension, the stomach and small bowel were distended better compared to patients administered water (p barium sulphate suspension (p contrast-enhanced abdominal and pelvic multidetector-row CT, orally administered neutral barium sulphate suspension allows the gastrointestinal tract to be visualized and distended better than either positive barium sulphate suspension, or water.

  15. 21 CFR 201.304 - Tannic acid and barium enema preparations.

    Science.gov (United States)

    2010-04-01

    ... 21 Food and Drugs 4 2010-04-01 2010-04-01 false Tannic acid and barium enema preparations. 201.304... Tannic acid and barium enema preparations. (a) It has become a widespread practice for tannic acid to be added to barium enemas to improve X-ray pictures. Tannic acid is capable of causing diminished liver...

  16. 49 CFR 173.182 - Barium azide-50 percent or more water wet.

    Science.gov (United States)

    2010-10-01

    ... 49 Transportation 2 2010-10-01 2010-10-01 false Barium azide-50 percent or more water wet. 173.182 Section 173.182 Transportation Other Regulations Relating to Transportation PIPELINE AND HAZARDOUS... Class 1 and Class 7 § 173.182 Barium azide—50 percent or more water wet. Barium azide—50 percent or more...

  17. 40 CFR 721.10010 - Barium manganese oxide (BaMnO3).

    Science.gov (United States)

    2010-07-01

    ... 40 Protection of Environment 30 2010-07-01 2010-07-01 false Barium manganese oxide (BaMnO3). 721... Substances § 721.10010 Barium manganese oxide (BaMnO3). (a) Chemical substance and significant new uses subject to reporting. (1) The chemical substance identified as barium manganese oxide (BaMnO3) (PMN P-00...

  18. The diagnosis of gastro-esophageal reflux disease cannot be made with barium esophagograms

    NARCIS (Netherlands)

    Saleh, C. M. G.; Smout, A. J. P. M.; Bredenoord, A. J.

    2015-01-01

    For over 50 years, barium studies have been used to diagnose gastro-esophageal reflux disease (GERD), but the value of this test is controversial. Our study aimed to determine if barium esophagograms can be used to diagnose GERD. Barium esophagograms and pH-impedance measurement were performed in 20

  19. Barium Tagging from nEXO Using Resonance Ionization Spectroscopy

    Science.gov (United States)

    Twelker, K.; Kravitz, S.

    nEXO is a 5-ton liquid enriched-xenon time projection chamber (TPC) to search for neutrinoless double-beta decay, designed to have the sensitivity to completely probe the inverted mass hierarchy of Majorana neutrinos. The detector will accommodate-as a background reduction technique-a system to recover and identify the barium decay product. This upgrade will allow a background-free measurement of neutrinoless double-beta decay and increase the half-life sensitivity of the experiment by at least one order of magnitude. Ongoing research and development includes a system to test barium extraction from liquid xenon using surface adsorption and Resonance Ionization Spectroscopy (RIS).

  20. Electronic and chemical properties of barium and indium clusters

    International Nuclear Information System (INIS)

    Onwuagba, B.N.

    1992-11-01

    The ground state electronic and chemical properties of divalent barium and trivalent indium are investigated in a self-consistent manner using the spin-polarized local density approximation in the framework of Density Functional Theory. A jellium model is adopted in the spirit of Gunnarsson and Lundqvist exchange and correlation energies and the calculated properties primarily associated with the s-p orbitals in barium and p orbitals in indium provide deepened insight towards the understanding of the mechanisms to the magic numbers in both clusters. (author). 21 refs, 5 figs

  1. Comparison of endoscopy and barium swallow with marshmallow in dysphagia.

    Science.gov (United States)

    Somers, S; Stevenson, G W; Thompson, G

    1986-06-01

    Forty-four patients with dysphagia were examined both by endoscopy and by barium swallow with a marshmallow bolus. In these patients 36 stenoses were found: 34 by radiology and 30 by endoscopy. The radiologic criteria for stenosis included arrest of the marshmallow in a manner to support a column of barium and reproduction of the patient's symptoms at the time this occurred. Radiologic false negative findings were partly due to an inability by patients to swallow an adequate marshmallow bolus; endoscopic failures were associated with small endoscopes and mild stenoses.

  2. Esophageal intramural pseudodiverticulosis characterized by barium esophagography: a case report

    LENUS (Irish Health Repository)

    O'Connor, Owen J

    2010-05-21

    Abstract Introduction Esophageal intramural pseudodiverticulosis is a rare condition characterized by the dilatation of the submucosal glands. Case presentation We present a case of esophageal intramural pseudodiverticulosis in a 72-year-old Caucasian man who presented with dysphagia and with a background history of alcohol abuse. An upper gastrointestinal endoscopy of our patient showed an esophageal stricture with abnormal mucosal appearances, but no malignant cells were seen at biopsy. Appearances on a barium esophagram were pathognomonic for esophageal intramural pseudodiverticulosis. Conclusion We demonstrate the enduring usefulness of barium esophagography in the characterization of abnormal mucosal appearances at endoscopy.

  3. Barium atoms and N20 molecular agregates reaction

    International Nuclear Information System (INIS)

    Visticot, J.P.; Mestdagh, J.M.; Alcaraz, C.; Cuvellier, J.; Berlande, J.

    1988-06-01

    The collisions between a barium atom and N20 molecular agregates are studied, for a better understanding of the solvation part in a chemical reaction. The experiments are carried out in a crossed molecular beam device. The light coming from the collision zone is scattered, and analysed by means of a photon detector. A time-of-flight technique is applied in the investigation of the beam's polymer concentration. The results show a nearly negligible chemiluminescent effect in the reaction between barium and N20 polymer. A solvated BaO formation mechanism is proposed to justify the experimental results [fr

  4. Reaction between barium and nitrogen in liquid sodium

    International Nuclear Information System (INIS)

    Addison, C.C.; Pulham, R.J.; Trevillion, E.A.

    1975-01-01

    Nitrogen in increasing amounts has been added to separate solutions of barium in sodium of constant composition (ca.4.40 mol % Ba) at 300 0 C. After rendering each mixture homogenous using an electromagnetic pump, filtration, and nitrogen analysis, all the N 2 added has been found in solution up to a solution composition approximating to Ba 4 N (i.e. 1.1 mol % N) beyond which the quantity of dissolved N 2 decreases progressively due to precipitation of the nitride Ba 2 N. The solubilization is interpreted in terms of strong preferential solvation of the nitride ion by barium cations. (author)

  5. The Kerr nonlinearity of the beta-barium borate crystal

    DEFF Research Database (Denmark)

    Bache, Morten; Guo, Hairun; Zhou, Binbin

    2013-01-01

    A popular crystal for ultrafast cascading experiments is beta-barium-borate (β-BaB2O4, BBO). It has a decent quadratic nonlinear coefficient, and because the crystal is anisotropie it can be birefringence phase-matched for type I (oo → e) second-harmonic generation (SHG). For femtosecond experime......A popular crystal for ultrafast cascading experiments is beta-barium-borate (β-BaB2O4, BBO). It has a decent quadratic nonlinear coefficient, and because the crystal is anisotropie it can be birefringence phase-matched for type I (oo → e) second-harmonic generation (SHG). For femtosecond...

  6. Preparation and characterization of antimony barium composite oxide photocatalysts

    Science.gov (United States)

    Han, X. P.; Yao, B. H.; Pan, Q. H.; Pen, C.; Zhang, C. L.

    2018-01-01

    In this paper, two kinds of antimony barium composite oxide photocatalysts have been prepared by two methods and characterized by XRD and SEM. The photocatalytic activity was evaluated by a photocatalytic reactor and an ultraviolet spectrophotometer. The results showed that-BaSb2O5•4H2O, BaSb2O6 two kinds of antimony barium composite oxide photocatalysts were successfully prepared in this experiment and they showed good photocatalytic properties. In addition, BaSb2O6 morphology showed more regular, microstructure and better catalytic performance.

  7. The photorefractive characteristics of bismuth-oxide doped lithium niobate crystals

    International Nuclear Information System (INIS)

    Zheng, Dahuai; Yao, Jiaying; Kong, Yongfa; Liu, Shiguo; Zhang, Ling; Chen, Shaolin; Xu, Jingjun

    2015-01-01

    Bismuth-doped lithium niobate (LN:Bi) crystals were grown by Czochralski method and their optical damage resistance, photorefraction, absorption spectra, and defect energy levels were investigated. The experimental results indicate that the photorefractive properties of LN:Bi were enhanced as compared with congruent one, the photorefractive response time was greatly shortened, the photorefractive sensitivity was increased, and the diffraction efficiency of near-stoichiometric LN:Bi (SLN:Bi) reached 31.72% and 49.08% at 532 nm and 488 nm laser, respectively (light intensity of 400 mW/cm 2 ). An absorption peak at about 350 nm was observed in the absorption spectrum of LN:Bi. And the defect energy levels simulation indicates new defect levels appear in the forbidden gap of LN:Bi crystals. Therefore bismuth can act as photorefractive centers in LN crystals

  8. Lightwave Circuits in Lithium Niobate through Hybrid Waveguides with Silicon Photonics.

    Science.gov (United States)

    Weigel, Peter O; Savanier, Marc; DeRose, Christopher T; Pomerene, Andrew T; Starbuck, Andrew L; Lentine, Anthony L; Stenger, Vincent; Mookherjea, Shayan

    2016-03-01

    We demonstrate a photonic waveguide technology based on a two-material core, in which light is controllably and repeatedly transferred back and forth between sub-micron thickness crystalline layers of Si and LN bonded to one another, where the former is patterned and the latter is not. In this way, the foundry-based wafer-scale fabrication technology for silicon photonics can be leveraged to form lithium-niobate based integrated optical devices. Using two different guided modes and an adiabatic mode transition between them, we demonstrate a set of building blocks such as waveguides, bends, and couplers which can be used to route light underneath an unpatterned slab of LN, as well as outside the LN-bonded region, thus enabling complex and compact lightwave circuits in LN alongside Si photonics with fabrication ease and low cost.

  9. Thermal stability of Dion-Jacobson mixed-metal-niobate double-layered perovskites

    International Nuclear Information System (INIS)

    Hermann, Andrew T.; Wiley, John B.

    2009-01-01

    The thermal stability and decomposition pathways of six Dion-Jacobson-related double-layered perovskites, ALaNb 2 O 7 (A = H, Li, Na, Ag) and (ACl)LaNb 2 O 7 (A = Fe, Cu), are investigated. These compounds are made by low temperature ( 2 O 7 . All the compounds are low temperature phases with some of them exhibiting decomposition exotherms consistent with metastability. Decomposition temperatures and reactions pathways vary with the identity of A with most decompositions resulting in the formation of a niobate (containing A) and LaNbO 4 . Results from differential scanning calorimetry and high temperature X-ray powder diffraction studies are presented and structural parameters pertinent to compound stability discussed

  10. The photorefractive characteristics of bismuth-oxide doped lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Zheng, Dahuai; Yao, Jiaying [School of Physics, Nankai University, Tianjin 300071 (China); Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072 (China); Kong, Yongfa, E-mail: kongyf@nankai.edu.cn [School of Physics, Nankai University, Tianjin 300071 (China); MOE Key Laboratory of Weak-Light Nonlinear Photonics and TEDA Applied Physics School, Nankai University, Tianjin 300457 (China); R and D Center, Taishan Sports Industry Group, Leling 253600 (China); Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072 (China); Liu, Shiguo [School of Physics, Nankai University, Tianjin 300071 (China); Zhang, Ling; Chen, Shaolin [MOE Key Laboratory of Weak-Light Nonlinear Photonics and TEDA Applied Physics School, Nankai University, Tianjin 300457 (China); Xu, Jingjun [School of Physics, Nankai University, Tianjin 300071 (China); MOE Key Laboratory of Weak-Light Nonlinear Photonics and TEDA Applied Physics School, Nankai University, Tianjin 300457 (China); Collaborative Innovation Center of Chemical Science and Engineering (Tianjin), Tianjin 300072 (China)

    2015-01-15

    Bismuth-doped lithium niobate (LN:Bi) crystals were grown by Czochralski method and their optical damage resistance, photorefraction, absorption spectra, and defect energy levels were investigated. The experimental results indicate that the photorefractive properties of LN:Bi were enhanced as compared with congruent one, the photorefractive response time was greatly shortened, the photorefractive sensitivity was increased, and the diffraction efficiency of near-stoichiometric LN:Bi (SLN:Bi) reached 31.72% and 49.08% at 532 nm and 488 nm laser, respectively (light intensity of 400 mW/cm{sup 2}). An absorption peak at about 350 nm was observed in the absorption spectrum of LN:Bi. And the defect energy levels simulation indicates new defect levels appear in the forbidden gap of LN:Bi crystals. Therefore bismuth can act as photorefractive centers in LN crystals.

  11. Conversion of broadband thermal radiation in lithium niobate crystals of various compositions

    Science.gov (United States)

    Syuy, A. V.; Litvinova, M. N.; Goncharova, P. S.; Sidorov, N. V.; Palatnikov, M. N.; Krishtop, V. V.; Likhtin, V. V.

    2013-05-01

    The conversion of the broadband thermal radiation in stoichiometric ( R = 1) lithium niobate single crystals that are grown from melt with 58.6 mol % of LiO2, congruent ( R = Li/Nb = 0.946) melt with the K2O flux admixture (4.5 and 6.0 wt %), and congruent melt and in congruent single crystals doped with the Zn2+, Gd3+, and Er3+ cations is studied. It is demonstrated that the conversion efficiency of the stoichiometric crystal that is grown from the melt with 58.6 mol % of LiO2 is less than the conversion efficiency of congruent crystal. In addition, the stoichiometric and almost stoichiometric crystals and the doped congruent crystals exhibit the blue shift of the peak conversion intensity in comparison with a nominally pure congruent crystal. For the congruent crystals, the conversion intensities peak at 520 and 495 nm, respectively.

  12. Numerical and Experimental Study of Optoelectronic Trapping on Iron-Doped Lithium Niobate Substrate

    Directory of Open Access Journals (Sweden)

    Michela Gazzetto

    2016-09-01

    Full Text Available Optoelectronic tweezers (OET are a promising technique for the realization of reconfigurable systems suitable to trap and manipulate microparticles. In particular, dielectrophoretic (DEP forces produced by OET represent a valid alternative to micro-fabricated metal electrodes, as strong and spatially reconfigurable electrical fields can be induced in a photoconductive layer by means of light-driven phenomena. In this paper we report, and compare with the experimental data, the results obtained by analyzing the spatial configurations of the DEP-forces produced by a 532 nm laser beam, with Gaussian intensity distribution, impinging on a Fe-doped Lithium Niobate substrate. Furthermore, we also present a promising preliminary result for water-droplets trapping, which could open the way to the application of this technique to biological samples manipulation.

  13. Electronic and Optical Properties of Sodium Niobate: A Density Functional Theory Study

    Directory of Open Access Journals (Sweden)

    Daniel Fritsch

    2018-01-01

    Full Text Available In recent years, much effort has been devoted to replace the most commonly used piezoelectric ceramic lead zirconate titanate Pb[ZrxTi1−x]O3 (PZT with a suitable lead-free alternative for memory or piezoelectric applications. One possible alternative to PZT is sodium niobate as it exhibits electrical and mechanical properties that make it an interesting material for technological applications. The high-temperature simple cubic perovskite structure undergoes a series of structural phase transitions with decreasing temperature. However, particularly the phases at room temperature and below are not yet fully characterised and understood. Here, we perform density functional theory calculations for the possible phases at room temperature and below and report on the structural, electronic, and optical properties of the different phases in comparison to experimental findings.

  14. Evaluation of domain randomness in periodically poled lithium niobate by diffraction noise measurement.

    Science.gov (United States)

    Dwivedi, Prashant Povel; Choi, Hee Joo; Kim, Byoung Joo; Cha, Myoungsik

    2013-12-16

    Random duty-cycle errors (RDE) in ferroelectric quasi-phase-matching (QPM) devices not only affect the frequency conversion efficiency, but also generate non-phase-matched parasitic noise that can be detrimental to some applications. We demonstrate an accurate but simple method for measuring the RDE in periodically poled lithium niobate. Due to the equivalence between the undepleted harmonic generation spectrum and the diffraction pattern from the QPM grating, we employed linear diffraction measurement which is much simpler than tunable harmonic generation experiments [J. S. Pelc, et al., Opt. Lett.36, 864-866 (2011)]. As a result, we could relate the RDE for the QPM device to the relative noise intensity between the diffraction orders.

  15. Photorefractive lithium niobate crystals for applications in photonics; Photorefraktive Lithiumniobatkristalle fuer Anwendungen in der Photonik

    Energy Technology Data Exchange (ETDEWEB)

    Hartwig, U.

    2006-12-15

    Lithium niobate crystals (LiNbO{sub 3}) generally show a photorefractive response, i.e., light-induced refractive index changes. Crystals are investigated at room temperature and at elevated temperatures. As a result 'classical' photorefractive holographic volume-phase gratings, originating from space charge fields and the electro-optic effect, and 'non-classical' photorefractive volume-phase gratings, which can be traced back to strong absorption gratings, emerge. Single domain and periodically poled crystals (PPLN) are investigated. PPLN is typically used in non-linear optics for frequency conversion. The crystals also show non-linear photorefractive response during holographic recording with isotropically polarized light beams of equal intensity and, in the case of PPLN, by mixing of domain and holographic gratings. The results are important for applications combining the photorefractive and non-linear optical properties of LiNbO{sub 3}. (orig.)

  16. Lightwave Circuits in Lithium Niobate through Hybrid Waveguides with Silicon Photonics

    Science.gov (United States)

    Weigel, Peter O.; Savanier, Marc; DeRose, Christopher T.; Pomerene, Andrew T.; Starbuck, Andrew L.; Lentine, Anthony L.; Stenger, Vincent; Mookherjea, Shayan

    2016-01-01

    We demonstrate a photonic waveguide technology based on a two-material core, in which light is controllably and repeatedly transferred back and forth between sub-micron thickness crystalline layers of Si and LN bonded to one another, where the former is patterned and the latter is not. In this way, the foundry-based wafer-scale fabrication technology for silicon photonics can be leveraged to form lithium-niobate based integrated optical devices. Using two different guided modes and an adiabatic mode transition between them, we demonstrate a set of building blocks such as waveguides, bends, and couplers which can be used to route light underneath an unpatterned slab of LN, as well as outside the LN-bonded region, thus enabling complex and compact lightwave circuits in LN alongside Si photonics with fabrication ease and low cost. PMID:26927022

  17. Formation of 2D bright spatial solitons in lithium niobate with photovoltaic response and incoherent background

    Science.gov (United States)

    Pustozerov, A.; Shandarov, V.

    2017-12-01

    The influence of incoherent background illumination produced by light-emitting diodes (LED's) of different average wavelengths and laser diode emitting in blue region of visible on diffraction characteristics of narrow coherent light beams of He-Ne laser due to refractive index changes of Fe-doped lithium niobate sample are studied. It has been experimentally demonstrated that nonlinear diffraction of red beams with wavelength 633 nm and diameters on full width of half maximum (FWHM) near to 15 μm may be totally compensated using background light with average wavelengths 450 - 465 nm. To provide the necessary intensity of incoherent background, the combinations of spherical and cylindrical concave lenses with blue LED and laser diode module without focusing its beam have been used.

  18. Ferroelectric domain inversion and its stability in lithium niobate thin film on insulator with different thicknesses

    Energy Technology Data Exchange (ETDEWEB)

    Shao, Guang-hao; Bai, Yu-hang; Cui, Guo-xin; Li, Chen; Qiu, Xiang-biao; Wu, Di; Lu, Yan-qing, E-mail: yqlu@nju.edu.cn [National Laboratory of Solid State Microstructures, College of Engineering and Applied Sciences, and Collaborative Innovation Center of Advanced Microstructures, Nanjing University, Nanjing 210093 (China); Geng, De-qiang [Jinan Jingzheng Electronics Co., Ltd., Jinan 250100 (China)

    2016-07-15

    Ferroelectric domain inversion and its effect on the stability of lithium niobate thin films on insulator (LNOI) are experimentally characterized. Two sets of specimens with different thicknesses varying from submicron to microns are selected. For micron thick samples (∼28 μm), domain structures are achieved by pulsed electric field poling with electrodes patterned via photolithography. No domain structure deterioration has been observed for a month as inspected using polarizing optical microscopy and etching. As for submicron (540 nm) films, large-area domain inversion is realized by scanning a biased conductive tip in a piezoelectric force microscope. A graphic processing method is taken to evaluate the domain retention. A domain life time of 25.0 h is obtained and possible mechanisms are discussed. Our study gives a direct reference for domain structure-related applications of LNOI, including guiding wave nonlinear frequency conversion, nonlinear wavefront tailoring, electro-optic modulation, and piezoelectric devices.

  19. Cascading second-order nonlinear processes in a lithium niobate-on-insulator microdisk.

    Science.gov (United States)

    Liu, Shijie; Zheng, Yuanlin; Chen, Xianfeng

    2017-09-15

    Whispering-gallery-mode (WGM) microcavities are very important in both fundamental science and practical applications, among which on-chip second-order nonlinear microresonators play an important role in integrated photonic functionalities. Here we demonstrate resonant second-harmonic generation (SHG) and cascaded third-harmonic generation (THG) in a lithium niobate-on-insulator (LNOI) microdisk resonator. Efficient SHG in the visible range was obtained with only several mW input powers at telecom wavelengths. THG was also observed through a cascading process, which reveals simultaneous phase matching and strong mode coupling in the resonator. Cascading of second-order nonlinear processes gives rise to an effectively large third-order nonlinearity, which makes on-chip second-order nonlinear microresonators a promising frequency converter for integrated nonlinear photonics.

  20. Ferroelectric lead magnesium niobate-lead titanate single crystals for ultrasonic hydrophone applications

    International Nuclear Information System (INIS)

    Lau, S.T.; Lam, K.H.; Chan, H.L.W.; Choy, C.L.; Luo, H.S.; Yin, Q.R.; Yin, Z.W.

    2004-01-01

    Ferroelectric lead magnesium niobate-lead titanate (PMN-PT) single crystals with a composition around the rhombohedral-tetragonal morphotropic phase boundary (65 mol% of PMN) were used to fabricate single-element needle-type hydrophones for measuring the spatial and temporal characteristics of medical ultrasonic transducers. PMN-PT single crystal was grown by a modified Bridgman method. Discs (0.5 mm thick) with normal along the direction were cut and then poled by a dc field in the thickness direction. The single crystal has a high relative permittivity (ε r ∼4000) making it appropriate for small area hydrophone applications. Single-element needle-type hydrophones with this material as the sensing element have been fabricated and characterized. The hydrophones have flat frequency response and good receiving sensitivity over certain frequency range in the megahertz region

  1. Glass: Rotary Electric Glass Furnace

    Energy Technology Data Exchange (ETDEWEB)

    Recca, L.

    1999-01-29

    Compared to conventional gas-fired furnaces, the new rotary electric furnace will increase energy efficiency while significantly reducing air emissions, product turnaround time, and labor costs. As this informative new fact sheet explains, the thousand different types of glass optical blanks produced for the photonics industry are used for lasers, telescopes, cameras, lights, and many other products.

  2. Dielectric behaviour of (Ba,Sr)TiO3 perovskite borosilicate glass ceramics

    International Nuclear Information System (INIS)

    Yadav, Avadhesh Kumar; Gautam, C.R.

    2013-01-01

    Various perovskite (Ba,Sr)TiO 3 borosilicate glasses were prepared by rapid melt-quench technique in the glass system ((Ba 1-x Sr x ).TiO 3 )-(2SiO 2 .B 2 O 3 )-(K 2 O)-(La 2 O 3 ). On the basis of differential thermal analysis results, glasses were converted into glass ceramic samples by regulated heat treatment schedules. The dielectric behaviour of crystallized barium strontium titanate borosilicate glass ceramic samples shows diffuse phase transition. The study depicts the dielectric behaviour of glass ceramic sample BST5K1L0.2S814. The double relaxation was observed in glass ceramic samples corresponding 80/20% Ba/Sr due to change in crystal structure from orthorhombic to tetragonal and tetragonal to cubic with variation of temperature. The highest value of dielectric constant was found to be 48289 for the glass ceramic sample BST5K1L0.2S814. The high value of dielectric constant attributed to space charge polarization between the glassy phase and perovskite phase. Due to very high value of dielectric constant, such glass ceramics are used for high energy storage devices. La 2 O 3 acts as nucleating agent for crystallization of glass to glass ceramics and enhances the dielectric constant and retarded dielectric loss. Such glass ceramics can be used in high energy storage devices such as barrier layer capacitors, multilayer capacitors etc. (author)

  3. Development of a glass matrix for vitrification of sulphate bearing high level radioactive liquid waste

    International Nuclear Information System (INIS)

    Kaushik, C.P.; Mishra, R.K.; Thorat, Vidya; Ramchandran, M.; Amar Kumar; Ozarde, P.D.; Raj, Kanwar; Das, D.

    2004-07-01

    High level radioactive liquid waste (HLW) is generated during reprocessing of spent nuclear fuel. In the earlier reprocessing flow sheet ferrous sulphamate has been used for valancy adjustment of Pu from IV to III for effective separation. This has resulted in generation of HLW containing significance amount of sulphate. Internationally borosilicate glass matrix has been adopted for vitrification of HLW. The first Indian vitrification facility at Waste Immobilislition Plant (WIP), Tarapur a five component borosilicate matrix (SiO 2 :B 2 O 3 :Na 2 O : MnO : TiO 2 ) has been used for vitrification of waste. However at Trombay HLW contain significant amount of sulphate which is not compatible with standard borosilicate formulation. Extensive R and D efforts were made to develop a glass formulation which can accommodate sulphate and other constituents of HLW e.g., U, Al, Ca, etc. This report deals with development work of a glass formulations for immobilization of sulphate bearing waste. Different glass formulations were studied to evaluate the compatibility with respect to sulphate and other constituents as mentioned above. This includes sodium, lead and barium borosilicate glass matrices. Problems encountered in different glass matrices for containment of sulphate have also been addressed. A glass formulation based on barium borosilicate was found to be effective and compatible for sulphate bearing high level waste. (author)

  4. Crystallization kinetics of BaO-Al2O3-SiO2 glasses

    Science.gov (United States)

    Bansal, Narottam P.; Hyatt, Mark J.

    1989-01-01

    Barium aluminosilicate glasses are being investigated as matrix materials in high-temperature ceramic composites for structural applications. Kinetics of crystallization of two refractory glass compositions in the barium aluminosilicate system were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). From variable heating rate DTA, the crystallization activation energies for glass compositions (wt percent) 10BaO-38Al2O3-51SiO2-1MoO3 (glass A) and 39BaO-25Al2O3-35SiO2-1MoO3 (glass B) were determined to be 553 and 558 kJ/mol, respectively. On thermal treatment, the crystalline phases in glasses A and B were identified as mullite (3Al2O3-2SiO2) and hexacelsian (BaO-Al2O3-2SiO2), respectively. Hexacelsian is a high-temperature polymorph which is metastable below 1590 C. It undergoes structural transformation into the orthorhombic form at approximately 300 C accompanied by a large volume change which is undesirable for structural applications. A process needs to be developed where stable monoclinic celsian, rather than hexacelsian, precipitates out as the crystal phase in glass B.

  5. Nitrate glass

    International Nuclear Information System (INIS)

    Kirilenko, I.A.; Vinogradov, E.E.

    1977-01-01

    Experimental evidence on behaviour of nitrate glasses is reviewed in terms of relationships between the presence of water in vitrescent nitrate systems and the properties of the systems. The glasses considered belong to systems of Mg(NO 3 ) 2 - Nd(NO 3 ) 3 ; Hg(NO 3 ) 2 -Nd(NO 3 ) 3 ; NaNO 3 -Mg(NO 3 ) 2 -Nd(NO 3 ) 3 ; M-Zn(NO 3 ) 3 , where M is a mixture of 20% mass NaNO 3 and 80% mass Mg(NO 3 ) 2 , and Zn is a rare earth ion. Nitrate glass is shown to be a product of dehydration. Vitrification may be regarded as a resusl of formation of molecular complexes in the chain due to hydrogen bonds of two types, i.e. water-water, or water-nicrate group. Chain formation, along with low melting points of the nitrates, hinder crystallization of nitrate melts. Provided there is enough water, this results in vitrification

  6. Iron phosphate glasses: Bulk properties and atomic scale structure

    Energy Technology Data Exchange (ETDEWEB)

    Joseph, Kitheri; Stennett, Martin C.; Hyatt, Neil C.; Asuvathraman, R.; Dube, Charu L.; Gandy, Amy S.; Govindan Kutty, K. V.; Jolley, Kenny; Vasudeva Rao, P. R.; Smith, Roger

    2017-10-01

    Bulk properties such as glass transition temperature, density and thermal expansion of iron phosphate glass compositions, with replacement of Cs by Ba, are investigated as a surrogate for the transmutation of 137Cs to 137Ba, relevant to the immobilisation of Cs in glass. These studies are required to establish the appropriate incorporation rate of 137Cs in iron phosphate glass. Density and glass transition temperature increases with the addition of BaO indicating the shrinkage and reticulation of the iron phosphate glass network. The average thermal expansion coefficient reduces from 19.8 × 10-6 K-1 to 13.4 × 10-6 K-1, when 25 wt. % of Cs2O was replaced by 25 wt. % of BaO in caesium loaded iron phosphate glass. In addition to the above bulk properties, the role of Ba as a network modifier in the structure of iron phosphate glass is examined using various spectroscopic techniques. The FeII content and average coordination number of iron in the glass network was estimated using Mössbauer spectroscopy. The FeII content in the un-doped iron phosphate glass and barium doped iron phosphate glasses was 20, 21 and 22 ± 1% respectively and the average Fe coordination varied from 5.3 ± 0.2 to 5.7 ± 0.2 with increasing Ba content. The atomic scale structure was further probed by Fe K-edge X-ray absorption spectroscopy. The average coordination number provided by extended X-ray absorption fine structure spectroscopy and X-ray absorption near edge structure was in good agreement with that given by the Mössbauer data.

  7. Status of barium studies in the present era of oncology: Are they a history?

    Science.gov (United States)

    Mahajan, Abhishek; Desai, Subash; Sable, Nilesh Pandurang; Thakur, Meenakshi Haresh

    2016-01-01

    With the advent of the modern imaging technologies, the present era of oncology is seeing steady decline in requests for barium studies due to the many reasons. It is prudent to mention here, that, barium examinations cannot be made obsolete! Our aim to preserve the age old technique of barium studies not only to keep it going on but also for the betterment and appropriate management of the patient. Our goal is not to "save" barium studies simply to keep this technology alive, per se, but rather to preserve barium radiology for the quality in patient care.

  8. Neutron shielding properties of a borated high-density glass

    Directory of Open Access Journals (Sweden)

    Saeed Aly Abdallah

    2017-01-01

    Full Text Available The neutron shielding properties of a borated high density glass system was characterized experimentally. The total removal macroscopic cross-section of fast neutrons, slow neutrons as well as the linear attenuation coefficient of total gamma rays, primary in addition to secondary, were measured experimentally under good geometric condition to characterize the attenuation properties of (75-x B2O3-1Li2O-5MgO-5ZnO-14Na2O-xBaO glassy system. Slabs of different thicknesses from the investigated glass system were exposed to a collimated beam of neutrons emitted from 252Cf and 241Am-Be neutron sources in order to measure the attenuation properties of fast and slow neutrons as well as total gamma rays. Results confirmed that barium borate glass was suitable for practical use in the field of radiation shielding.

  9. Glass capillary optics for making x-ray beams of 0.1 to 50 microns diameter

    International Nuclear Information System (INIS)

    Bilderback, Donald H.; Fontes, Ernest

    1997-01-01

    We have fabricated a unique computerized glass puller that can make parabolic or elliptically tapered glass capillaries for microbeam x-ray experiments from hollow glass tubing. We have produced optics that work in a single-bounce imaging mode or in a multi-bounce condensing mode. The imaging-mode capillaries have been used to create 20 to 50 micron diameter x-ray beams at 12 keV that are quite useful for imaging diffraction patterns from tiny bundles of carbon and Kevlar fibers. The condensing-mode capillaries are useful for creating submicron diameter beams and show great promise in x-ray fluorescence applications with femtogram sensitivity for patterned Er and Ti dopants diffused into an optically-active lithium niobate wafer

  10. Silver niobates

    International Nuclear Information System (INIS)

    Tanirbergenov, B.; Rozhenko, S.P.

    1979-01-01

    By means of determination of residual concentrations and pH measurements investigated are the AgNO 3 -KNbO 3 -H 2 O, AgNO 3 -K 3 NbO 4 -H 2 O, AgNO 3 -K 8 Nb 16 O 19 -H 2 O systems and established is formation of meta-, ortho-and hexaniobates of silver. AgNbO 3 x H 2 O, Ag 8 Nb 6 O 19 x 6H 2 O and Ag 3 NbO 3 x 2.5H 2 O are separated from aqueous solution. Using the methods of differential-thermal, thermogravimetric and X-ray-phase analyses it is shown that silver metaniobate transforms into the crystal state at 530 deg C. Ortho- and hexaniobate of silver decompose at 500 deg C with formation of silver metaniobate and metal silver

  11. PHYSICAL AND ELECTRICAL PROPERTIES ENHANCEMENT OF RARE-EARTH DOPED-POTASSIUM SODIUM NIOBATE (KNN: A REVIEW

    Directory of Open Access Journals (Sweden)

    Akmal Mat Harttat Maziati

    2015-06-01

    Full Text Available Alkaline niobate mainly potassium sodium niobate, (KxNa1-x NbO3 (abreviated as KNN has long attracted attention as piezoelectric materials as its high Curie temperature (Tc and piezoelectric properties. The volatility of alkaline element (K, Na is, however detrimental to the stoichiometry of KNN, contributing to the failure to achieve high-density structure and lead to the formation of intrinsic defects. By partially doping of several rare-earth elements, the inherent defects could be improved significantly. Therefore, considerable attempts have been made to develop doped-KNN based ceramic materials with high electrical properties. In this paper, these research activities are reviewed, including dopants type and doping role in KNN perovskite structure.

  12. SEPARATION OF BARIUM VALUES FROM URANYL NITRATE SOLUTIONS

    Science.gov (United States)

    Tompkins, E.R.

    1959-02-24

    The separation of radioactive barium values from a uranyl nitrate solution of neutron-irradiated uranium is described. The 10 to 20% uranyl nitrate solution is passed through a flrst column of a cation exchange resin under conditions favoring the adsorption of barium and certain other cations. The loaded resin is first washed with dilute sulfuric acid to remove a portion of the other cations, and then wash with a citric acid solution at pH of 5 to 7 to recover the barium along with a lesser amount of the other cations. The PH of the resulting eluate is adjusted to about 2.3 to 3.5 and diluted prior to passing through a smaller second column of exchange resin. The loaded resin is first washed with a citric acid solution at a pH of 3 to elute undesired cations and then with citric acid solution at a pH of 6 to eluts the barium, which is substantially free of undesired cations.

  13. Characterization of Barium Borate Frameworks Using Raman Spectroscopy.

    Science.gov (United States)

    Gharavi-Naeini, Jafar; Yoo, Kyung W; Stump, Nathan A

    2018-04-01

    Systematic micro-Raman scattering investigations have been carried out on Sm +2 doped 2(BaO)-n(B 2 O 3 ) matrices for n = 4, 5, 8, and 2(BaO)-(Na 2 O)-9(B 2 O 3 ) using the 364 nm excitation of an Ar + laser. The Raman results have been compared with the known structures of barium tetraborate, barium pentaborate, barium octaborate, and barium sodium nonaborate. An excellent correlation has been found between the BO 4 /BO 3 composition ratios for each product and intensity ratios of the designated BO 4 and BO 3 Raman peaks. Furthermore, the Raman frequencies of both BO 4 and BO 3 groups undergo a systematic blueshift as n increases from four to nine. The shift results from a decrease of the B-O bond lengths for both BO 4 and BO 3 groups as the samples transition from the tetraborate to nonaborate structures. Linear relations (with negative slopes) have been determined between the measured Raman frequencies and B-O bond lengths in the frameworks.

  14. Dynamics of a barium release in the magnetospheric tail

    Science.gov (United States)

    Mende, S. B.; Swenson, G. R.; Geller, S. P.; Doolittle, J. H.; Haerendel, G.

    1989-01-01

    The late time behavior of the May 13, 1985 magnetotail barium cloud is examined. The bulk dynamics of the cloud are studied based on triangulated data and data from Fabry-Perot Doppler velocity measurements. The changes in cloud morphology in relation to the in situ measurements made by the Ion Release Module satellite are discussed.

  15. Barium titanate inverted opals-synthesis, characterization, and optical properties

    Energy Technology Data Exchange (ETDEWEB)

    Soten, I.; Miguez, H.; Yang, S.M.; Petrov, S.; Coombs, N.; Tetreault, N.; Ozin, G.A. [Toronto Univ., ON (Canada). Dept. of Chemistry; Matsuura, N.; Ruda, H.E. [Toronto Univ., ON (Canada). Dept. of Metallurgy and Materials Science

    2002-01-01

    The engineering of cubic or tetragonal polymorphs of nanocrystalline barium titanate inverted opals has been achieved by thermally induced transformations. Optical characterization demonstrated photonic crystal behavior of the opals. The tuning of the ferroelectric-paraelectric transition around the Curie temperature is shown in this paper. (orig.)

  16. Electrical transport properties of calcium and barium aluminates

    NARCIS (Netherlands)

    Metselaar, R.; Hoefsloot, A.M.

    1987-01-01

    Electrical conductivity and ionic transport numbers have been measured of barium and calcium aluminates with composition CaO·nAl2O3 (n=7/12, 1, 2, 6) and 0.82 BaO·6Al2O3. At room temperatures these compounds are insulators, but at high temperatures mixed conductivity is observed. Ionic transport

  17. ORIGINAL ARTICLE ORIG ORIG Comparison of barium and ...

    African Journals Online (AJOL)

    SA JOURNAL OF RADIOLOGY • June 2007. ORIG. Abstract. Background. Simulation of patients with carcinoma of the oesophagus using radio-opaque contrast is a standard step in treatment planning prior to delivering radiation therapy. Various contrast mediums such as barium, gastrograffin and hexabrix have been used ...

  18. Synthesis and surface properties of submicron barium sulfate particles

    International Nuclear Information System (INIS)

    Zhang Ming; Zhang Bao; Li Xinhai; Yin Zhoulan; Guo Xueyi

    2011-01-01

    Barium sulfate particles were synthesized in the presence of EDTA at room temperature. X-ray diffractometry (XRD), Fourier transform infrared resonance (FTIR) and scanning electron microscopy (SEM) were used to characterize the structure and morphology of BaSO 4 particles. The effect of the preparation parameters on the particle size distribution and morphology was investigated. The conditional formation constants of Ba-EDTA at different pH values were calculated. The results show that the size and morphology of BaSO 4 particles can be effectively controlled by adding EDTA in the precipitation process. Among all the operation conditions, the pH value has significant effect on the particle size. The obtained barium sulfate particles are spherical and well dispersed at pH = 9-10. Zeta potentials of BaSO 4 were measured at different pH. The isoelectric point (IEP) of barium sulfate colloid appears at pH 6.92. The model of the solid-solution interface at a particle of BaSO 4 was presented. The FTIR result indicates that the surface of the prepared BaSO 4 absorbs the functional groups of EDTA, which lower the IEP of the barium sulfate particles.

  19. Synthesis and surface properties of submicron barium sulfate particles

    Energy Technology Data Exchange (ETDEWEB)

    Zhang Ming, E-mail: csu.light@yahoo.com.cn [College of Chemistry and Chemical Engineering, Zhaoqing University, Zhaoqing 526061 (China); School of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China); Zhang Bao; Li Xinhai [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China); Yin Zhoulan [School of Chemistry and Chemical Engineering, Central South University, Changsha 410083 (China); Guo Xueyi [School of Metallurgical Science and Engineering, Central South University, Changsha 410083 (China)

    2011-10-15

    Barium sulfate particles were synthesized in the presence of EDTA at room temperature. X-ray diffractometry (XRD), Fourier transform infrared resonance (FTIR) and scanning electron microscopy (SEM) were used to characterize the structure and morphology of BaSO{sub 4} particles. The effect of the preparation parameters on the particle size distribution and morphology was investigated. The conditional formation constants of Ba-EDTA at different pH values were calculated. The results show that the size and morphology of BaSO{sub 4} particles can be effectively controlled by adding EDTA in the precipitation process. Among all the operation conditions, the pH value has significant effect on the particle size. The obtained barium sulfate particles are spherical and well dispersed at pH = 9-10. Zeta potentials of BaSO{sub 4} were measured at different pH. The isoelectric point (IEP) of barium sulfate colloid appears at pH 6.92. The model of the solid-solution interface at a particle of BaSO{sub 4} was presented. The FTIR result indicates that the surface of the prepared BaSO{sub 4} absorbs the functional groups of EDTA, which lower the IEP of the barium sulfate particles.

  20. Pressure-assisted sintering of high purity barium titanate

    NARCIS (Netherlands)

    van den Cruijsem, S.; Varst, van der P.G.T.; With, de G.; Bortzmeyer, D.; Boussuge, M.; Chartier, Th.; Hausonne, J.M.; Mocellin, A.; Rousset, A.; Thevenot, F.

    1997-01-01

    The dielectric behaviour of High Purity Barium titanate (HPB) ceramics is strongly dependent on the grain size and porosity. For applications, control of grain size and porosity is required. Pressure-assisted sintering techniques at relatively low temperatures meet these requirements. In this study,

  1. Iatrogen perforation of the rectum following barium enema

    International Nuclear Information System (INIS)

    Eggum, R.; Kressner, U.; Haffner, J.

    1998-01-01

    Perforation of the rectum following barium enema is relatively rare, occurring in 1 of 3,000 procedures. Colorectal perforation is a serious condition and early diagnosis is of paramount importance in order to avoid any delay in treating the patient. Direct suture of the perforation, lavage, presacral drainage and stomia are the preferred methods of primary surgical treatment. 10 refs., 1 fig

  2. Effectiveness of therapeutic barium enema for diverticular hemorrhage

    Science.gov (United States)

    Matsuura, Mizue; Inamori, Masahiko; Nakajima, Atsushi; Komiya, Yasuhiko; Inoh, Yumi; Kawasima, Keigo; Naitoh, Mai; Fujita, Yuji; Eduka, Akiko; Kanazawa, Noriyoshi; Uchiyama, Shiori; Tani, Rie; Kawana, Kennichi; Ohtani, Setsuya; Nagase, Hajime

    2015-01-01

    AIM: To evaluate the effectiveness of barium impaction therapy for patients with colonic diverticular bleeding. METHODS: We reviewed the clinical charts of patients in whom therapeutic barium enema was performed for the control of diverticular bleeding between August 2010 and March 2012 at Yokohama Rosai Hospital. Twenty patients were included in the review, consisting of 14 men and 6 women. The median age of the patients was 73.5 years. The duration of the follow-up period ranged from 1 to 19 mo (median: 9.8 mo). Among the 20 patients were 11 patients who required the procedure for re-bleeding during hospitalization, 6 patients who required it for re-bleeding that developed after the patient left the hospital, and 3 patients who required the procedure for the prevention of re-bleeding. Barium (concentration: 150 w%/v%) was administered per the rectum, and the leading edge of the contrast medium was followed up to the cecum by fluoroscopy. After confirmation that the ascending colon and cecum were filled with barium, the enema tube was withdrawn, and the patient’s position was changed every 20 min for 3 h. RESULTS: Twelve patients remained free of re-bleeding during the follow-up period (range: 1-19 mo) after the therapeutic barium enema, including 9 men and 3 women with a median age of 72.0 years. Re-bleeding occurred in 8 patients including 5 men and 3 women with a median age of 68.5 years: 4 developed early re-bleeding, defined as re-bleeding that occurs within one week after the procedure, and the remaining 4 developed late re-bleeding. The DFI (disease-free interval) decreased 0.4 for 12 mo. Only one patient developed a complication from therapeutic barium enema (colonic perforation). CONCLUSION: Therapeutic barium enema is effective for the control of diverticular hemorrhage in cases where the active bleeding site cannot be identified by colonoscopy. PMID:25987779

  3. Comparison of pressure between barium reduction and air reduction of the intussusception in children

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Kyung Hwan; Park, Sang Gyu; Park, Choong Ki; Yoon, Jong Sup [Hallym University College of Medicine, Seoul (Korea, Republic of)

    1989-08-15

    There are many method of treatment of the intussusception in children, including surgery, barium reduction, air reduction, and saline enema under ultrasonographic monitoring. Among them, barium reduction and air reduction have been used widely as nonsurgical method of treatment in radiologic department. During barium reduction, the bottle filled with barium solution must not be elevated over a 3 feet from the operating table. In air reduction, diagnostic pressure is about 60 mmHg and pressure during reduction usually is maintained between 90 mmHg and 130 mmHg. The authors have studied about pressure difference of barium solution by changing height of the bottle filled with barium solution, and have compared with pressure in air reduction. The results are as follows; 1. Pressure of 20 w/v % barium solution at the 60 cm height is 44.4 mmHg, and 69.6 mmHg at the 90 cm height. 2. Pressure of 40 w/v % barium solution at the 60 cm height is 51.4 mmHg, and 80.1 mmHg at the 90 cm height. 3. Pressure of 40 w/v % barium solution at the 90cm height is much lower than the pressure maintained during air reduction, and this difference in pressure may be one of the causes of low reduction rate in barium reduction then air reduction. 4. The pressure gradient per 10 cm height is about 8.45 mmHg in 20 w/v % barium solution, about 9.21 mmHg in 30 w/v % barium solution, and about 9.72 mmHg 40 w/v % barium solution. 5. Intraluminal pressure difference between the barium reduction and the air reduction is probably of the major causes of rapid diagnosis and high reduction rate in the air reduction.

  4. Comparison of pressure between barium reduction and air reduction of the intussusception in children

    International Nuclear Information System (INIS)

    Lee, Kyung Hwan; Park, Sang Gyu; Park, Choong Ki; Yoon, Jong Sup

    1989-01-01

    There are many method of treatment of the intussusception in children, including surgery, barium reduction, air reduction, and saline enema under ultrasonographic monitoring. Among them, barium reduction and air reduction have been used widely as nonsurgical method of treatment in radiologic department. During barium reduction, the bottle filled with barium solution must not be elevated over a 3 feet from the operating table. In air reduction, diagnostic pressure is about 60 mmHg and pressure during reduction usually is maintained between 90 mmHg and 130 mmHg. The authors have studied about pressure difference of barium solution by changing height of the bottle filled with barium solution, and have compared with pressure in air reduction. The results are as follows; 1. Pressure of 20 w/v % barium solution at the 60 cm height is 44.4 mmHg, and 69.6 mmHg at the 90 cm height. 2. Pressure of 40 w/v % barium solution at the 60 cm height is 51.4 mmHg, and 80.1 mmHg at the 90 cm height. 3. Pressure of 40 w/v % barium solution at the 90cm height is much lower than the pressure maintained during air reduction, and this difference in pressure may be one of the causes of low reduction rate in barium reduction then air reduction. 4. The pressure gradient per 10 cm height is about 8.45 mmHg in 20 w/v % barium solution, about 9.21 mmHg in 30 w/v % barium solution, and about 9.72 mmHg 40 w/v % barium solution. 5. Intraluminal pressure difference between the barium reduction and the air reduction is probably of the major causes of rapid diagnosis and high reduction rate in the air reduction

  5. Structure and chemical durability of barium borosilicate glass–ceramics containing zirconolite and titanite crystalline phases

    International Nuclear Information System (INIS)

    Li, Huidong; Wu, Lang; Xu, Dong; Wang, Xin; Teng, Yuancheng; Li, Yuxiang

    2015-01-01

    In order to increase the solubility of actinides in the glass matrix, the effects of CaO, TiO 2 , and ZrSiO 4 addition (abbreviated as CTZ, in the mole ratio of 2:2:1) on crystalline phases, microstructure, and chemical durability of barium borosilicate glass–ceramics were investigated. The results show that the samples possess both zirconolite-2M and titanite phase when the CTZ content is greater than or equal to 45 wt.%. For the glass–ceramics with 45 wt.% CTZ (CTZ-45), only zirconolite-2M phase is observed after annealing at 680–740 °C for 2 h. The CTZ-45 possess zirconolite-2M and titanite phases after annealing at 700 °C first, and then annealing at 900–1050 °C for 2 h. Furthermore, the zirconolite-2M and titanite grains show a strip and brick shape, respectively. The CTZ-45 annealing at 950 °C shows the lower normalized leaching rates of B, Na and Nd when compared to that of CTZ-0 and CTZ-55. - Highlights: • CaO, TiO 2 , ZrSiO 4 (CTZ) as nucleating agents were added to barium borosilicate glass. • The samples with 45–55 wt% CTZ possess CaZrTi 2 O 7 -2M and CaTiSiO 5 crystalline phases. • CTZ-45 (45wt% CTZ) possesses only CaZrTi 2 O 7 -2M phase after annealing at 680–740 °C. • CTZ-45 possesses CaZrTi 2 O 7 -2M and CaTiSiO 5 phases after annealing at 900–1050 °C. • CTZ-45 annealing at 950 °C shows the lower leaching rates of B, Na and Nd than CTZ-0 and CTZ-55.

  6. Identification of the man-made barium copper silicate pigments among some ancient Chinese artifacts through spectroscopic analysis.

    Science.gov (United States)

    Li, Q H; Yang, J C; Li, L; Dong, J Q; Zhao, H X; Liu, S

    2015-03-05

    This article describes the complementary application of non-invasive micro-Raman spectroscopy and energy dispersive X-ray fluorescence spectrometry to the characterization of some ancient Chinese silicate artifacts. A total of 28 samples dated from fourth century BC to third century AD were analyzed. The results of chemical analysis showed that the vitreous PbO-BaO-SiO2 material was used to sinter these silicate artifacts. The barium copper silicate pigments including BaCuSi4O10, BaCuSi2O6 and BaCu2Si2O7 were widely identified from colorful areas of the samples by Raman spectroscopy. In addition, other crystalline phases such as Fe2O3, BaSi2O5, BaSO4, PbCO3 and quartz were also identified. The present study provides very valuable information to trace the technical evolution of man-made barium copper silicate pigments and their close relationship with the making of ancient PbO-BaO-SiO2 glaze and glass. Copyright © 2014 Elsevier B.V. All rights reserved.

  7. Ion irradiation effects on lithium niobate etalons for tunable spectral filters

    Science.gov (United States)

    Garranzo, D.; Ibarmia, S.; Alvarez-Herrero, A.; Olivares, J.; Crespillo, M.; Díaz, M.

    2017-11-01

    , coupled with the HV field, could trigger a dielectric breakdown in the Lithium Niobate. In this paper we present the electro-optical results obtained when exposing a set of LN samples and a lowquality full size etalon to different radiation conditions. In a first irradiation campaign, performed at the Centre for Micro Analysis of Materials (CMAM-Madrid) facilities, we were mainly focused on the long-term degradation effects with a series of high flux (109 cm-2 s-1) proton tests at an energy of 10 MeV. In order to study the possibility of a single ion breakdown, a second campaign was carried out, at the Texas A&M University (TAMU), exposing Lithium Niobate to high LET ion species (78Kr, 40Ar, 129Xe, 197Au) accelerated to the GeV energy range to penetrate or even pass through the entire Lithium Niobate thickness.

  8. Effects of chemesthetic stimuli mixtures with barium on swallowing apnea duration.

    Science.gov (United States)

    Todd, J Tee; Butler, Susan G; Plonk, Drew P; Grace-Martin, Karen; Pelletier, Cathy A

    2012-10-01

    This study tested the hypotheses that swallowing apnea duration (SAD) will increase given barium versus water, chemesthetic stimuli (i.e., water barium, age (older > younger), and genetic taste differences (supertasters > nontasters). Prospective group design. University Medical Center. Eighty healthy women were identified as nontasters and supertasters, equally comprising two age groups: 18 to 35 years and 60+ years. The KayPentax Swallowing Signals Lab was used to acquire SAD via nasal cannula during individually randomized swallows of 5 mL barium, 2.7% w/v citric acid with barium, carbonation with barium, and 50:50 diluted ethanol with barium. Data were analyzed using path analysis, with the mediator of chemesthetic perception, adjusted for repeated measures. Significant main effects of age (P = .012) and chemesthetic stimuli (P = .014) were found, as well as a significant interaction between chemesthetic stimuli and age (P = .028). Older women had a significantly longer SAD than younger women. Post hoc analyses revealed that barium mixed with ethanol elicited a significantly longer SAD than other bolus conditions, regardless of age group. There were no significant differences in SAD between barium and water conditions, and no significant effect of chemesthetic perception (P > .05). Ethanol added to barium elicited longer SAD compared to plain barium, but not the other chemesthetic conditions. Older women had a longer SAD than younger women in all conditions. These findings may influence design of future studies examining effects of various stimuli on SAD. Copyright © 2012 The American Laryngological, Rhinological, and Otological Society, Inc.

  9. Gas thermodesorption study of barium and strontium cerates

    International Nuclear Information System (INIS)

    Aksenova, T.I.; Khromushin, I.V.; Zhotabaev, Zh.R.; Bukenov, K.D.; Medvedeva, Z.V.; Berdauletov, A.K.

    2002-01-01

    Kinetic of water, oxygen, hydrogen and carbon dioxide molecules release from doped and undoped samples of barium cerates and doped strontium cerates during vacuum heating was studied. The samples were prepared by inductive melting method. The following two kinds of preliminary samples treatments were used: annealing in air (650-750 deg. C) and wet nitrogen atmosphere (625 deg.C). Main results of thermodesorption studies of barium and strontium cerates are represented in the table. The samples of doped LaSrMnO were investigated also. It was found that the initial doped samples (without preliminary annealing) did not show any gas release in temperature range of 20-1100 deg. C. This fact indicates on high stability of compositions and strong bond of 'host' oxygen in their lattice. A significant amount of water and oxygen molecules were released from BaCe 0.9 Nd 0.1 O 3 samples whereas water and hydrogen molecules desorption from SrCe 0.95 Y 0.05 O 3 samples took place. Hydrogen molecules desorption was found for strontium cerates samples; no hydrogen molecules release was observed for doped and pure barium cerate samples.Intensive water molecules release from doped samples confirms the necessity of oxygen vacancies creation in these compounds to get properties of proton conductivity, since it was not found any water molecules release from annealed undoped samples of BaCeO 3 It is necessary to notice that oxygen molecules release from these samples took place at ∼1000 deg. C that is significantly higher then from BaCeNdO samples. Forms of high temperatures part of oxygen and low temperature part of water spectra indicate that phase transformations are responsible for oxygen and water molecules desorption in this cases. These results are in good agreement with literature data. Desorption of water molecules from barium and strontium cerates took place. Oxygen desorption took place only from barium cerates. It can be explained as the following: doped barium cerates have

  10. Exposure to low-dose barium by drinking water causes hearing loss in mice.

    Science.gov (United States)

    Ohgami, Nobutaka; Hori, Sohjiro; Ohgami, Kyoko; Tamura, Haruka; Tsuzuki, Toyonori; Ohnuma, Shoko; Kato, Masashi

    2012-10-01

    We continuously ingest barium as a general element by drinking water and foods in our daily life. Exposure to high-dose barium (>100mg/kg/day) has been shown to cause physiological impairments. Direct administration of barium to inner ears by vascular perfusion has been shown to cause physiological impairments in inner ears. However, the toxic influence of oral exposure to low-dose barium on hearing levels has not been clarified in vivo. We analyzed the toxic influence of oral exposure to low-dose barium on hearing levels and inner ears in mice. We orally administered barium at low doses of 0.14 and 1.4 mg/kg/day to wild-type ICR mice by drinking water. The doses are equivalent to and 10-fold higher than the limit level (0.7 mg/l) of WHO health-based guidelines for drinking water, respectively. After 2-week exposure, hearing levels were measured by auditory brain stem responses and inner ears were morphologically analyzed. After 2-month exposure, tissue distribution of barium was measured by inductively coupled plasma mass spectrometry. Low-dose barium in drinking water caused severe hearing loss in mice. Inner ears including inner and outer hair cells, stria vascularis and spiral ganglion neurons showed severe degeneration. The Barium-administered group showed significantly higher levels of barium in inner ears than those in the control group, while barium levels in bone did not show a significant difference between the two groups. Barium levels in other tissues including the cerebrum, cerebellum, heart, liver and kidney were undetectably low in both groups. Our results demonstrate for the first time that low-dose barium administered by drinking water specifically distributes to inner ears resulting in severe ototoxicity with degeneration of inner ears in mice. Copyright © 2012 Elsevier Inc. All rights reserved.

  11. Regeneration of barium carbonate from barium sulphide in a pilot-scale bubbling column reactor and utilization for acid mine drainage

    CSIR Research Space (South Africa)

    Mulopo, J

    2012-01-01

    Full Text Available Batch regeneration of barium carbonate (BaCO3) from barium sulphide (BaS) slurries by passing CO2 gas into a pilot-scale bubbling column reactor under ambient conditions was used to assess the technical feasibility of BaCO3 recovery in the Alkali...

  12. Mie scattering in heavy-metal fluoride glasses

    International Nuclear Information System (INIS)

    Edgar, A.

    1996-01-01

    Heavy-metal fluoride glasses comprise mixtures of heavy-cation fluorides such as those of zirconium, barium, and lanthanum together with some stabilising fluorides such as AlF 3 . For particular relative proportions, the mixtures form a glass rather than a polycrystalline material when quenched from the melt. The particularly useful features of these glasses are the wide spectral region (∼200nm-8000nm) over which they are transparent, the low minimum attenuation at the centre of the spectral window, and the ease with which optically-active rare-earth ions can be incorporated, leading to potential applications in passive and active fibre optics. The minimal attenuation, which is potentially lower than for silica fibre, is generally limited by wavelength-independent scattering by particle and gas bubble inclusions. We have observed a new wavelength-dependent scattering effect in fluoride glass of the well-known composition ZLABN20. In this paper, we report on work in progress on the optical extinction and scattering spectrum of the fluoride glasses, and discuss the spectra in terms of Mie's scattering theory. The chemical nature of the scattering centres in these nominally 'pure' glasses is at present a puzzle, and relative merits of various possible models will be compared

  13. Effect of nanosecond UV laser irradiation on luminescence and absorption in silver- and copper-containing phosphate glasses

    Science.gov (United States)

    Murashov, A. A.; Sidorov, A. I.; Stoliarchuk, M. V.

    2018-03-01

    Experimental evidence is presented that nanosecond UV laser irradiation of silver- and copper-containing barium phosphate glasses leads to luminescence quenching in the visible range. Subsequent heat treatment induces an absorption in the range 350–500 nm. These effects are due to the ionisation and fragmentation of subnanometre molecular clusters by laser radiation and subsequent (heat treatment-induced) formation of nanoparticles possessing plasmon resonance. Our numerical modelling results demonstrate the feasibility of producing stable AgnCum hybrid molecular clusters in glass. Local modification of the optical properties of glass by laser light can be used for optical information recording.

  14. CRYSTALLIZATION IN MULTICOMPONENT GLASSES

    Energy Technology Data Exchange (ETDEWEB)

    KRUGER AA; HRMA PR

    2009-10-08

    In glass processing situations involving glass crystallization, various crystalline forms nucleate, grow, and dissolve, typically in a nonuniform temperature field of molten glass subjected to convection. Nuclear waste glasses are remarkable examples of multicomponent vitrified mixtures involving partial crystallization. In the glass melter, crystals form and dissolve during batch-to-glass conversion, melter processing, and product cooling. Crystals often agglomerate and sink, and they may settle at the melter bottom. Within the body of cooling glass, multiple phases crystallize in a non-uniform time-dependent temperature field. Self-organizing periodic distribution (the Liesegnang effect) is common. Various crystallization phenomena that occur in glass making are reviewed.

  15. Crystallization In Multicomponent Glasses

    International Nuclear Information System (INIS)

    Kruger, A.A.; Hrma, P.R.

    2009-01-01

    In glass processing situations involving glass crystallization, various crystalline forms nucleate, grow, and dissolve, typically in a nonuniform temperature field of molten glass subjected to convection. Nuclear waste glasses are remarkable examples of multicomponent vitrified mixtures involving partial crystallization. In the glass melter, crystals form and dissolve during batch-to-glass conversion, melter processing, and product cooling. Crystals often agglomerate and sink, and they may settle at the melter bottom. Within the body of cooling glass, multiple phases crystallize in a non-uniform time-dependent temperature field. Self-organizing periodic distribution (the Liesegnang effect) is common. Various crystallization phenomena that occur in glass making are reviewed.

  16. Surface studies of barium and barium oxide on tungsten and its application to understanding the mechanism of operation of an impregnated tungsten cathode

    Science.gov (United States)

    Forman, R.

    1976-01-01

    Surface studies have been made of multilayer and monolayer films of barium and barium oxide on a tungsten substrate. The purpose of the investigation was to synthesize the surface conditions that exist on an activated impregnated tungsten cathode and obtain a better understanding of the mechanism of operation of such cathodes. The techniques employed in these measurements were Auger spectroscopy and work-function measurements. The results of this study show that the surface of an impregnated cathode is identical to that observed for a synthesized monolayer or partial monolayer of barium on oxidized tungsten by evaluating Auger spectra and work-function measurements. Data obtained from desorption studies of barium monolayers on a tungsten substrate in conjunction with Auger and work-function results have been interpreted to show that throughout most of its life an impreganated cathode has a partial monolayer, rather than a monolayer, of barium on its surface.

  17. Barium determination in gastric contents, blood and urine by inductively coupled plasma mass spectrometry in the case of oral barium chloride poisoning.

    Science.gov (United States)

    Łukasik-Głębocka, Magdalena; Sommerfeld, Karina; Hanć, Anetta; Grzegorowski, Adam; Barałkiewicz, Danuta; Gaca, Michał; Zielińska-Psuja, Barbara

    2014-01-01

    A serious case of barium intoxication from suicidal ingestion is reported. Oral barium chloride poisoning with hypokalemia, neuromuscular and cardiac toxicity, treated with intravenous potassium supplementation and hemodialysis, was confirmed by the determination of barium concentrations in gastric contents, blood, serum and urine using the inductively coupled plasma mass spectrometry method. Barium concentrations in the analyzed specimens were 20.45 µg/L in serum, 150 µg/L in blood, 10,500 µg/L in urine and 63,500 µg/L in gastric contents. Results were compared with barium levels obtained from a non-intoxicated person. © The Author 2014. Published by Oxford University Press. All rights reserved. For Permissions, please email: journals.permissions@oup.com.

  18. NASA/Max Planck Institute Barium Ion Cloud Project.

    Science.gov (United States)

    Brence, W. A.; Carr, R. E.; Gerlach, J. C.; Neuss, H.

    1973-01-01

    NASA and the Max Planck Institute for Extraterrestrial Physics (MPE), Munich, Germany, conducted a cooperative experiment involving the release and study of a barium cloud at 31,500 km altitude near the equatorial plane. The release was made near local magnetic midnight on Sept. 21, 1971. The MPE-built spacecraft contained a canister of 16 kg of Ba CuO mixture, a two-axis magnetometer, and other payload instrumentation. The objectives of the experiment were to investigate the interaction of the ionized barium cloud with the ambient medium and to deduce the properties of electric fields in the proximity of the release. An overview of the project is given to briefly summarize the organization, responsibilities, objectives, instrumentation, and operational aspects of the project.

  19. Attainment of barium hexaferrite nanoparticles by a Pechini Method

    International Nuclear Information System (INIS)

    Galvao, S.B.; Timoteo, Jr.J.F.; Melo, G.M.; Souto, K.K.O.; Florioto, N.T.; Paskocimas, C.A.

    2009-01-01

    The barium hexaferrites (BaFe 12 O 19 ) are used as a compound of materials applied in electronic devices, as medical devices, satellites, dada servers systems, wireless systems and others. The general properties are strongly related to the microstructure and morphology, and the particles size decrease results in advantages to the majority applications, mainly the high-tech thumbnail devices. These magnetic ceramic materials, with perovskite structure, are traditionally prepared my conventional oxide mixture synthesis. In this work was studied the nanoparticle synthesis of BaFe 12 O 19 by the precursors polymeric method (Pechini), using as precursors the barium carbonate and the iron nitrate, under different thermal treatment conditions. The samples were characterized by XRD, SEM, BET, DTA and TGA. The results presented the attainment of a monophasic powder with particles size around 100 nm. (author)

  20. Influence of Magnetron Effect on Barium Hexaferrite Thin Layers

    International Nuclear Information System (INIS)

    Hassane, H.; Chatelon, J.P.; Rousseau, J.J; Siblini, A.; Kriga, A.

    2011-01-01

    In this paper, we study the effects of a magnet, located in the cathode, on barium hexaferrite thin films deposited by RF magnetron sputtering technique. During the process, these effects can modify thickness, roughness and stress of coatings. The characteristics of the deposited layers depend on the substrate position that is located opposite of magnetron cathode. In the m agnetron area , one can observe that the high stress can produce cracks or detachment of layers and the increasing of both depositing rate and surface roughness. After sputtering elaboration, barium hexaferrite films are in a compressive stress mode. But, after the post-deposition heat treatment these films are in a tensile stress mode. To improve the quality of BaM films, the subsrtate has to be set outside the magnetron area. (author)

  1. Electromagnetic properties of carbon black and barium titanate composite materials

    International Nuclear Information System (INIS)

    Wang Guiqin; Chen Xiaodong; Duan Yuping; Liu Shunhua

    2008-01-01

    Nanocrystalline carbon black/barium titanate compound particle (CP) was synthesized by sol-gel method. The phase structure and morphology of compound particle were investigated by X-ray diffraction (XRD), transmission electron microscope (TEM) and Raman spectrum measurements, the electroconductivity was test by trielectrode arrangement and the precursor powder was followed by differential scanning calorimetric measurements (DSC) and thermal gravimetric analysis (TGA). In addition, the complex relative permittivity and permeability of compound particle were investigated by reflection method. The compound particle/epoxide resin composite (CP/EP) with different contents of CP were measured. The results show barium titanate crystal is tetragonal phase and its grain is oval shape with 80-100 nm which was coated by carbon black film. As electromagnetic (EM) complex permittivity, permeability and reflection loss (RL) shown that the compound particle is mainly a kind of electric and dielectric lossy materials and exhibits excellent microwave absorption performance in the X- and Ku-bands

  2. Attainment of barium hexa ferrite nanoparticles by a Pechini method

    International Nuclear Information System (INIS)

    Galvao, Sheila B.; Timoteo, Flavio Junior J.; Machado, Tercio G.; Souto, Kesia K.O.; Floreoto, Neide T.; Paskocimas, Carlos A.

    2009-01-01

    The barium hexa ferrites (BaFe 12 O 19 ) are used as a compound of materials applied in electronic devices, as medical devices, satellites, dada servers systems, wireless systems and others. The general properties are strongly related to the microstructure and morphology, and the particles size decrease results in advantages to the majority applications, mainly the high-tech thumbnail devices. These magnetic ceramic materials, with perovskite structure, are traditionally prepared my conventional oxide mixture synthesis. In this work was studied the nanoparticle synthesis of BaFe 12 O 19 by the precursors polymeric method (Pechini), using as precursors the barium carbonate and the iron nitrate, under different thermal treatment conditions. The samples were characterized by XRD, Raman spectroscopy, SEM, BET, DTA and TGA. The results presented the attainment of a monophasic powder with particles size around 100 nm. (author)

  3. Electromagnetic properties of photodefinable barium ferrite polymer composites

    Science.gov (United States)

    Sholiyi, Olusegun; Lee, Jaejin; Williams, John D.

    2014-07-01

    This article reports the magnetic and microwave properties of a Barium ferrite powder suspended in a polymer matrix. The sizes for Barium hexaferrite powder are 3-6 μm for coarse and 0.8-1.0 μm for the fine powder. Ratios 1:1 and 3:1 (by mass) of ferrite to SU8 samples were characterized and analyzed for predicting the necessary combinations of these powders with SU8 2000 Negative photoresist. The magnetization properties of these materials were equally determined and were analyzed using Vibrating Sample Magnetometer (VSM). The Thru, Reflect, Line (TRL) calibration technique was employed in determining complex relative permittivity and permeability of the powders and composites with SU8 between 26.5 and 40 GHz.

  4. Electromagnetic properties of photodefinable barium ferrite polymer composites

    Directory of Open Access Journals (Sweden)

    Olusegun Sholiyi

    2014-07-01

    Full Text Available This article reports the magnetic and microwave properties of a Barium ferrite powder suspended in a polymer matrix. The sizes for Barium hexaferrite powder are 3–6 μm for coarse and 0.8–1.0 μm for the fine powder. Ratios 1:1 and 3:1 (by mass of ferrite to SU8 samples were characterized and analyzed for predicting the necessary combinations of these powders with SU8 2000 Negative photoresist. The magnetization properties of these materials were equally determined and were analyzed using Vibrating Sample Magnetometer (VSM. The Thru, Reflect, Line (TRL calibration technique was employed in determining complex relative permittivity and permeability of the powders and composites with SU8 between 26.5 and 40 GHz.

  5. Recycling of Glass

    DEFF Research Database (Denmark)

    Christensen, Thomas Højlund; Damgaard, Anders

    2011-01-01

    Glass is used for many purposes, but in the waste system glass is predominantly found in terms of beverage and food containers with a relatively short lifetime before ending up in the waste. Furthermore there is a large amount of flat glass used in building materials which also ends up in the waste...... system; this glass though has a long lifetime before ending up in the waste. Altogether these product types add up to 82% of the production of the European glass industry (IPCC, 2001). Recycling of glass in terms of cleaning and refilling of bottles as well as the use of broken glass in the production...... of new glass containers is well established in the glass industry. This chapter describes briefly howglass is produced and howwaste glass is recycled in the industry. Quality requirements and use of recycled products are discussed, as are the resource and environmental issues of glass recycling....

  6. Radium and thorium with barium in micronodules of cattle thyroids

    International Nuclear Information System (INIS)

    Van Middlesworth, L.

    1980-01-01

    Radium isotopes were found concentrated in thyroid glands of cattle. The incidence of measurable radium varied from 80% to less than 0.1% in thyroids from different abattoirs. The radium was concentrated in microscopic bodies containing predominantly barium and sulfur and lying within the storage of thyroglobulin, adjacent to follicular cells. Some thyroid cells may receive biologically significant doses of alpha radiation from these sources

  7. Preparation of barium and uranium targets on thick backings

    International Nuclear Information System (INIS)

    Sletten, G.

    1982-01-01

    Targets of 135 Ba and 235 U have been prepared by the technique of heavy ion sputtering. Rolled foils of 208 Pb and 197 Au were used to support 250-500 μg/cm 2 layers of barium. Uranium films have been prepared by sputtering UO 2 onto 1 mg/cm 2 titanium foils. Uranium deposit thicknesses of 300 to 1800 μg/cm 2 have been prepared. (orig.)

  8. Barium enema and CT findings of Douglas pouch metastasis

    International Nuclear Information System (INIS)

    Miyakawa, Kunihisa; Uchiyama, Nachiko; Iinuma, Hajime; Moriyama, Noriyuki

    1999-01-01

    We retrospectively reviewed barium enema and CT findings of Douglas pouch metastasis in 170 patients. The findings were divided into three types: Anterior compression type, anterior fixed folds type, and stenosis type. Patients with gastric cancer usually showed a stenosis type, especially in those with poorly differentiated adenocarcinoma. Patients with colon and ovary cancer usually showed an anterior compression type. In patients with gastric cancer, those who showed a stenosis type had the most favorable prognosis among these three types. (author)

  9. Synthesis and characterization of barium ferrite–silica nanocomposites

    International Nuclear Information System (INIS)

    Aguilar-González, M.A.; Mendoza-Suárez, G.; Padmasree, K.P.

    2013-01-01

    In this work, we prepared barium ferrite-silica (BaM-SiO 2 ) nanocomposites of different molar ratios by high-energy ball milling, followed by heat-treatment at different temperatures. The microstructure, morphology and magnetic properties were characterized for different synthesis conditions by using X-ray diffraction (XRD), scanning electron microscopy (SEM) and vibrating sample magnetometry (VSM). The results indicate that 15 h of milling was enough to avoid the generation of hematite phase and to get a good dispersion of barium ferrite particles in the ceramic matrix. For milling periods beyond 15 h and heat treatment above 900 °C, the XRD patterns showed the presence of hematite phase caused by the decomposition of BaM. The agglomerate size observed through SEM analysis was around 150 nm with a good BaM dispersion into the SiO 2 matrix. The highest saturation magnetization (Ms) value obtained was 43 emu/g and the corresponding coercivity (Hc) value of 3.4 kOe for the composition 60BaM-40SiO 2 milled for 15 h and heat treated at 900 °C. This coercivity value is acceptable for the application in magnetic recording media. Highlights: • Barium ferrite–silica nanocomposites were prepared by high energy ball milling. • Optimal processing time is 15 h milling and heat treatment at 900 °C. • This is enough to avoid the generation of hematite phase. • Obtain good dispersion of barium ferrite particles in the ceramic matrix • Above this processing time shows the presence of increased amount of hematite

  10. Optical and luminescent properties of the lead and barium molybdates

    Energy Technology Data Exchange (ETDEWEB)

    Spassky, D.A. E-mail: dima@opts.phys.msu.ru; Ivanov, S.N.; Kolobanov, V.N.; Mikhailin, V.V.; Zemskov, V.N.; Zadneprovski, B.I.; Potkin, L.I

    2004-12-01

    Time-resolved luminescence as well as excitation and reflectivity spectra of the oriented lead and barium molybdate single crystals were studied using synchrotron radiation. Features in reflectivity spectra in the fundamental absorption region were analyzed. The contribution of electronic states of lead cation to the formation of the bandgap in PbMoO{sub 4} is supposed. The role of lead states in the intrinsic luminescence of PbMoO{sub 4} is discussed.

  11. Clinical efficacy of a new barium sulfate for abdominal CT

    International Nuclear Information System (INIS)

    Yamada, Tatuya; Kohno, Mitio; Uematsu, Sadao; Nisitani, Hiromu; Tanaka, Takao.

    1988-01-01

    Computed Tomography of the abdomen requires that the intestines are filled with contrast medium so that the gut is not misinterpreted as a pathologic process. Besides, normal structures may be difficult to delimit in patients with scanty intra-abdominal fat. In Japan, up to date, only a single contrast medium has been available for this purpose, Gastrografin and thus identical with the intravasculaly used Urografin or Angiografin. A new Barium Sulfate suspention (Fusimi Seiyaku, Kagawa) for computed tomographic use has been dilute solution (4.77 %) and with suspending agents that prevent a rapid sedimentation of the Barium Sulfate. The aim of this investigation was to compare Gastrografin with a new barium regarding patients tolerance, side effects and diagnostic information. The investigation comprised 146 patients who were reffered for abdominal CT and was carried out by 5 facilities; National Cancer Center, Kobe University, Chiba University, Kyushu University and Juntendo University. Diagnostic information was judged with respect to the filling of the stomach and intestines, the presence of imaging artifacts and finally clinical estimation. Patients tolerance was investigated as regards taste and side effects. Good filling of the stomach and intestines was obtained in this investigation. However, imaging artifacts occured in only a few cases. The imaging artifacts appeared almost exclusively to arise in the boundary layer between the bowel gas and contrast medium, and were most common in the stomach. However, the contrasting effect of this medium did not in itself appear to cause any imaging artifacts. Fushimi's new barium seems to be preffered because of its lesser tendency to arise artifacts and better tendency to make good filling of the stomach and intestines. Moreover, this investigation did not have any side effects. (J.P.N.)

  12. Structure and multiferroic properties of barium hexaferrite ceramics

    International Nuclear Information System (INIS)

    Tan, Guolong; Chen, Xiuna

    2013-01-01

    Simultaneous occurrence of large ferroelectricity and strong ferromagnetism have been observed in barium hexaferrite ceramics. Barium hexaferrite (BaFe 12 O 19 ) powders with hexagonal crystal structure were successfully synthesized in a polymer precursor method using barium acetate and ferric acetylacetonate as the precursors. The powders were pressed into pellets which were sintered into ceramics at 1200 °C and 1300 °C for 1 h. The structure and morphology of the ceramics were examined using X-ray diffraction and field emission scanning electron microscopy. Large spontaneous polarization was observed in the BaFe 12 O 19 ceramics at room temperature, revealing a clear ferroelectric hysteresis loop. The maximum remanent polarization of the BaFe 12 O 19 ceramic was estimated approximately 11.8 μC cm −2 . The FeO 6 octahedron in its perovskite-like hexagonal unit cell and the shift of Fe 3+ off the center of octahedron are suggested to be the origin of the polarization in BaFe 12 O 19 . The BaFe 12 O 19 ceramics also showed strong ferromagnetism at room temperature. - Graphical abstract: Ferroelectric hysteresis loops of BaFe 12 O 19 ceramics measured at a frequency of 120 Hz, which shows that the ceramics sintered at 1200 °C is ferroelectric with P r ∼11.8 μC/cm 2 . Highlights: ► Large ferroelectricity and strong ferromagnetism were observed in barium hexaferrite ceramics. ► The maximum remanent polarization of the BaFe 12 O 19 ceramic was estimated to be 11.8 μC cm −2 . ► The FeO 6 octahedron and off-center shift of Fe 3+ are suggested to be the origin of the polarization.

  13. X-ray absorption spectroscopy investigation of structurally modified lithium niobate crystals

    Energy Technology Data Exchange (ETDEWEB)

    Vitova, Tonya

    2008-02-15

    The type and concentration of impurity centers in different valence states are crucial for tuning the photorefractive properties of doped Lithium Niobate (LN) crystals. X-ray Absorption Spectroscopy (XAS) is an appropriate tool for studying the local structure of impurity centers. XAS combined with absorption in UV/VIS/IR and High Resolution X-ray Emission Spectroscopy (HRXES) provide information about the valence state of the dopant ions in as-grown, reduced or oxidized doped LN crystals. Cu (Cu{sup 1+} and Cu{sup 2+}) and Fe (Fe{sup 2+} and Fe{sup 3+}) atoms are found in two different valence states, whereas there are indications for a third Mn valency, in addition to Mn{sup 2+} and Mn{sup 3+} in manganese-doped LN crystals. One of the charge compensation mechanisms during reduction of copper- doped LN crystals is outgassing of oxygen atoms. Cu ions in the reduced crystals have at least two different site symmetries: twofold (Cu{sup 1+}) and sixfold (Cu{sup 2+}) coordinated by O atoms. Fe and Mn atoms are coordinated by six O atoms. Cu and Fe ions are found to occupy only Li sites, whereas Mn ions are also incorporated into Li and Nb sites. The refractive index change in LN crystals irradiated with {sup 3}He{sup 2+} ions is caused by structurally disordered centers, where Nb atoms are displaced from normal crystallographic sites and Li or/and O vacancies are present. (orig.)

  14. Synthesis, structure and electrical properties of Mg-, Ni-codoped bismuth niobates

    Directory of Open Access Journals (Sweden)

    M. S. Koroleva

    2017-12-01

    Full Text Available Mg-, Ni-codoped bismuth niobates Bi1.6Mg0.8-xNixNb1.6O7-δ (x = 0; 0.2; 0.4; 0.6; 0.8 were obtained by conventional solid-state reaction method. It was shown that the Mg atoms are distributed at the Nb sites while the Ni atoms are distributed over the Bi- and the Nb-sites, according to the results of comparison of pycnometric and X-ray density of the Bi1.6Mg0.4Ni0.4Nb1.6O7-δ pyrochlore. In this case, about 15–20% of the vacancies are formed at the Bi sites. The obtained compounds are stable up to their melting point based on the DSC analysis data. Real dielectric permittivity ε' of the Bi1.6Mg0.8-xNixNb1.6O7-δ samples decreases from 80 to 65 with the temperature decrease from 25 to 700 °C and practically does not depend on frequency in the range of 1–1000 kHz. Oxides Bi1.6Mg0.8-xNixNb1.6O7-δ behave like insulators up to 280 °C, their conductivity increases with temperature (Ea,dc ≈ 1.3 eV, dc and with the Ni content at a given temperature.

  15. Phase transition characteristics and associated piezoelectricity of potassium-sodium niobate lead-free ceramics.

    Science.gov (United States)

    Wang, Yuanyu; Hu, Liang; Zhang, Qilong; Yang, Hui

    2015-08-14

    To achieve high piezoelectric activity and a wide sintering temperature range, the ceramic system concerning (1 - x)(K(0.48)Na(0.52))(Nb(0.96)Sb(0.04))O(3)-x[Bi(0.5)(Na(0.7)Ag(0.3))(0.5)](0.90) Zn(0.10)ZrO(3) was designed, and the rhombohedral-tetragonal (R-T) phase boundary can drive a high d(33). Phase transition characteristics as well as their effects on the electrical properties were investigated systematically. The R-T coexistence phase boundary (0.04 ≤ x ≤ 0.05) can be driven via modification with BNAZZ, and has been confirmed by XRD and temperature-dependent dielectric constants as well as Raman analysis, and the ceramics possess enhanced piezoelectric properties (d(33) ∼ 425 pC N(-1) and k(p) ∼ 0.43) and a high unipolar strain (∼0.3%). In addition, a wide sintering temperature range of 1050-1080 °C can warrant a large d(33) of 400-430 pC N(-1), which can benefit practical applications. As a result, the addition of BNAZZ is an effective method to improve the electrical properties (piezoelectricity and strain) and sintering behavior of potassium-sodium niobate ceramics.

  16. Thickness, humidity, and polarization dependent ferroelectric switching and conductivity in Mg doped lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Neumayer, Sabine M.; Rodriguez, Brian J., E-mail: brian.rodriguez@ucd.ie [School of Physics, University College Dublin, Belfield, Dublin 4 (Ireland); Conway Institute of Biomolecular and Biomedical Research, University College Dublin, Belfield, Dublin 4 (Ireland); Strelcov, Evgheni; Kravchenko, Ivan I.; Kalinin, Sergei V. [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Manzo, Michele; Gallo, Katia [Department of Applied Physics, KTH - Royal Institute of Technology, Roslagstullbacken 21, 10691 Stockholm (Sweden); Kholkin, Andrei L. [Department of Physics and CICECO-Aveiro Institute of Materials, 3810-193 Aveiro, Portugal and Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation)

    2015-12-28

    Mg doped lithium niobate (Mg:LN) exhibits several advantages over undoped LN such as resistance to photorefraction, lower coercive fields, and p-type conductivity that is particularly pronounced at domain walls and opens up a range of applications, e.g., in domain wall electronics. Engineering of precise domain patterns necessitates well founded knowledge of switching kinetics, which can differ significantly from that of undoped LN. In this work, the role of humidity and sample composition in polarization reversal has been investigated under application of the same voltage waveform. Control over domain sizes has been achieved by varying the sample thickness and initial polarization as well as atmospheric conditions. In addition, local introduction of proton exchanged phases allows for inhibition of domain nucleation or destabilization, which can be utilized to modify domain patterns. Polarization dependent current flow, attributed to charged domain walls and band bending, demonstrates the rectifying ability of Mg:LN in combination with suitable metal electrodes that allow for further tailoring of conductivity.

  17. Thickness, humidity, and polarization dependent ferroelectric switching and conductivity in Mg doped lithium niobate

    International Nuclear Information System (INIS)

    Neumayer, Sabine M.; Rodriguez, Brian J.; Strelcov, Evgheni; Kravchenko, Ivan I.; Kalinin, Sergei V.; Manzo, Michele; Gallo, Katia; Kholkin, Andrei L.

    2015-01-01

    Mg doped lithium niobate (Mg:LN) exhibits several advantages over undoped LN such as resistance to photorefraction, lower coercive fields, and p-type conductivity that is particularly pronounced at domain walls and opens up a range of applications, e.g., in domain wall electronics. Engineering of precise domain patterns necessitates well founded knowledge of switching kinetics, which can differ significantly from that of undoped LN. In this work, the role of humidity and sample composition in polarization reversal has been investigated under application of the same voltage waveform. Control over domain sizes has been achieved by varying the sample thickness and initial polarization as well as atmospheric conditions. In addition, local introduction of proton exchanged phases allows for inhibition of domain nucleation or destabilization, which can be utilized to modify domain patterns. Polarization dependent current flow, attributed to charged domain walls and band bending, demonstrates the rectifying ability of Mg:LN in combination with suitable metal electrodes that allow for further tailoring of conductivity

  18. Phenomenological theory of the dielectric response of lead magnesium niobate and lead scandium tantalate

    International Nuclear Information System (INIS)

    Qian, H.; Bursill, L.A.

    1997-01-01

    The influence of the random field effects originating from charges chemical defects and non-domain textures of the formation and dynamics of polar clusters is analyzed. The spatial distribution of the local fields is not totally random but contains some correlations in direction and strength. Polar clusters are classified to be dynamic or frozen according to their dynamic characteristics in the random fields. The relaxation formula of a dipolar moment in an anisotropic double-well potential is deduced. Two percolation models are introduced, one to account for frustration effects associated with multiple orientations of polar clusters, which results in a broad diffuse dielectric response and the second to account for the case whereby there may be a phase transition to a ferroelectric state. The dielectric permittivity and dissipation factor of the typical relaxors lead magnesium niobate and lead scandium tantalate are predicted as a function of both temperature and frequency, which results are in good agreement with the experimental measurements. 30 refs., 9 figs

  19. X-ray absorption spectroscopy investigation of structurally modified lithium niobate crystals

    International Nuclear Information System (INIS)

    Vitova, Tonya

    2008-02-01

    The type and concentration of impurity centers in different valence states are crucial for tuning the photorefractive properties of doped Lithium Niobate (LN) crystals. X-ray Absorption Spectroscopy (XAS) is an appropriate tool for studying the local structure of impurity centers. XAS combined with absorption in UV/VIS/IR and High Resolution X-ray Emission Spectroscopy (HRXES) provide information about the valence state of the dopant ions in as-grown, reduced or oxidized doped LN crystals. Cu (Cu 1+ and Cu 2+ ) and Fe (Fe 2+ and Fe 3+ ) atoms are found in two different valence states, whereas there are indications for a third Mn valency, in addition to Mn 2+ and Mn 3+ in manganese-doped LN crystals. One of the charge compensation mechanisms during reduction of copper- doped LN crystals is outgassing of oxygen atoms. Cu ions in the reduced crystals have at least two different site symmetries: twofold (Cu 1+ ) and sixfold (Cu 2+ ) coordinated by O atoms. Fe and Mn atoms are coordinated by six O atoms. Cu and Fe ions are found to occupy only Li sites, whereas Mn ions are also incorporated into Li and Nb sites. The refractive index change in LN crystals irradiated with 3 He 2+ ions is caused by structurally disordered centers, where Nb atoms are displaced from normal crystallographic sites and Li or/and O vacancies are present. (orig.)

  20. Modification of both d33 and TC in a potassium-sodium niobate ternary system.

    Science.gov (United States)

    Wu, Bo; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo

    2015-12-28

    In this work, we simultaneously achieved a giant d33 and a high TC in a lead-free piezoelectric ternary system of (1-x-y)K0.48Na0.52NbO3-xBiFeO3-yBi0.5Na0.5ZrO3 {(1-x-y)KNN-xBF-yBNZ}. Owing to the rhombohedral-orthorhombic-tetragonal (R-O-T) phase coexistence and the enhanced dielectric and ferroelectric properties, the ceramics with a composition of (x = 0.006, y = 0.04) show a giant d33 of ∼428 pC N(-1) together with a TC of ∼318 °C, thereby proving that the design of ternary systems is an effective way to achieve both high d33 and high TC in KNN-based materials. In addition, a good thermal stability for piezoelectricity was also observed in these ceramics (e.g., d33 > 390 pC N(-1), T ≤ 300 °C). This is the first time such a good comprehensive performance in potassium-sodium niobate materials has been obtained. As a result, we believe that this type of material system with both giant d33 and high TC is a promising candidate for high-temperature piezoelectric devices.

  1. Investigation of pyroelectric electron emission from monodomain lithium niobate single crystals

    International Nuclear Information System (INIS)

    Bourim, El Mostafa; Moon, Chang-Wook; Lee, Seung-Woon; Kyeong Yoo, In

    2006-01-01

    The behaviors of thermally stimulated electron emission from pyroelectric monodomain lithium niobate single crystal (LiNbO 3 ) were investigated by utilizing a Si p-n junction photodiode as electron detector and a receptive electron beam resist (E-beam resist) as electron collector. In high vacuum (10 -6 Torr), the pyroelectric electron emission (PEE) was found to depend on the exposed emitting polar crystal surface (+Z face or -Z face) and was significantly influenced by the emitter-electron receiver gap distances. Thus, the PEE from +Z face was detected during heating and was activated, in small gaps ( 2 mm) the emission was simply mastered by field emission effect. Whereas, The PEE from -Z face was detected during cooling and was solely due to the field ionization effect. Therewith, for small gaps ( 2 mm) PEE was governed by field ionization generating a soft and continuous plasma ambient atmosphere. Significant decrease of electron emission current was observed from +Z face after successive thermal cycles. A fast and fully emission recovery was established after a brief exposure of crystal to a poor air vacuum of 10 -1 Torr

  2. Effect of chemical pressure on competition and cooperation between polar and antiferrodistortive distortions in sodium niobate

    Science.gov (United States)

    Jauhari, Mrinal; Mishra, S. K.; Mittal, R.; Sastry, P. U.; Chaplot, S. L.

    2017-12-01

    We present results obtained from a combination of dielectric and x-ray diffraction measurements for compositional design of (1 -x )NaNb O3-x BaTi O3(NNBT x ) , which can induce interferroelectric phase transitions. Anomalies are observed in dielectric measurements performed for various compositions at 300 K, as well as at different temperatures for NNBT03. We observed the appearance(disappearance) of the superlattice reflections along with change in the intensities of the main perovskite peaks in the powder x-ray diffraction data, which provide clear evidences for structural phase transitions with composition and temperature. We found that increasing the concentration of BaTi O3 leads to the suppression of out-of-phase rotation of octahedra and an increment in tetragonality (c /a ratio), which promotes the polar mode at room temperature. The temperature-dependent powder diffraction study shows that the ferroelectric rhombohedral phase of pure sodium niobate gets suppressed for the composition x =0.03 , and the monoclinic phase C c gets stabilized at low temperature. The monoclinic phase is believed to provide for a flexible polarization rotation and is considered to be directly linked to the high-performance piezoelectricity in materials due to presence of more easy axes for spontaneous polarizations than the rhombohedral phase.

  3. Temperature dependent dielectric relaxation and ac-conductivity of alkali niobate ceramics studied by impedance spectroscopy

    Science.gov (United States)

    Yadav, Abhinav; Mantry, Snigdha Paramita; Fahad, Mohd.; Sarun, P. M.

    2018-05-01

    Sodium niobate (NaNbO3) ceramics is prepared by conventional solid state reaction method at sintering temperature 1150 °C for 4 h. The structural information of the material has been investigated by X-ray diffraction (XRD) and Field emission scanning electron microscopy (FE-SEM). The XRD analysis of NaNbO3 ceramics shows an orthorhombic structure. The FE-SEM micrograph of NaNbO3 ceramics exhibit grains with grain sizes ranging between 1 μm to 5 μm. The surface coverage and average grain size of NaNbO3 ceramics are found to be 97.6 % and 2.5 μm, respectively. Frequency dependent electrical properties of NaNbO3 is investigated from room temperature to 500 °C in wide frequency range (100 Hz-5 MHz). Dielectric constant, ac-conductivity, impedance, modulus and Nyquist analysis are performed. The observed dielectric constant (1 kHz) at transition temperature (400 °C) are 975. From conductivity analysis, the estimated activation energy of NaNbO3 ceramics is 0.58 eV at 10 kHz. The result of Nyquist plot shows that the electrical behavior of NaNbO3 ceramics is contributed by grain and grain boundary responses. The impedance and modulus spectrum asserts that the negative temperature coefficient of resistance (NTCR) behavior and non-Debye type relaxation in NaNbO3.

  4. Effect of additives for higher removal rate in lithium niobate chemical mechanical planarization

    International Nuclear Information System (INIS)

    Jeong, Sukhoon; Lee, Hyunseop; Cho, Hanchul; Lee, Sangjik; Kim, Hyoungjae; Kim, Sungryul; Park, Jaehong; Jeong, Haedo

    2010-01-01

    High roughness and a greater number of defects were created by lithium niobate (LN; LiNbO 3 ) processes such as traditional grinding and mechanical polishing (MP), should be decreased for manufacturing LN device. Therefore, an alternative process for gaining defect-free and smooth surface is needed. Chemical mechanical planarization (CMP) is suitable method in the LN process because it uses a combination approach consisting of chemical and mechanical effects. First of all, we investigated the LN CMP process using commercial slurry by changing various process conditions such as down pressure and relative velocity. However, the LN CMP process time using commercial slurry was long to gain a smooth surface because of lower material removal rate (MRR). So, to improve the material removal rate (MRR), the effects of additives such as oxidizer (hydrogen peroxide; H 2 O 2 ) and complexing agent (citric acid; C 6 H 8 O 7 ) in a potassium hydroxide (KOH) based slurry, were investigated. The manufactured slurry consisting of H 2 O 2 -citric acid in the KOH based slurry shows that the MRR of the H 2 O 2 at 2 wt% and the citric acid at 0.06 M was higher than the MRR for other conditions.

  5. Nanotechnology in lithium niobate for integrated optic frequency conversion in the UV

    Science.gov (United States)

    Busacca, Alessandro C.; Santini, Claudia; Oliveri, Luigi; Riva-Sanseverino, Stefano; Parisi, Antonino; Cino, Alfonso C.; Assanto, Gaetano

    2017-11-01

    In the domain of Earth Explorer satellites nanoengineered nonlinear crystals can optimize UV tunable solid-state laser converters. Lightweight sources can be based on Lithium Niobate (LN) domain engineering by electric field poling and guided wave interactions. In this Communication we report the preliminary experimental results and the very first demonstration of UltraViolet second-harmonic generation by first-order quasi-phase-matching in a surface-periodically-poled proton-exchanged LN waveguide. The pump source was a Ti-Sapphire laser with a tunability range of 700- 980 nm and a 40 GHz linewidth. We have measured UV continuous-wave light at 390 nm by means of a lock-in amplifier and of a photodiode with enhanced response in the UV. Measured conversion efficiency was about 1%W-1cm-2. QPM experiments show good agreement with theory and pave the way for a future implementation of the technique in materials less prone to photorefractive damage and wider transparency in the UV, such as Lithium Tantalate.

  6. Observation and analysis of nanodomain textures in dielectric relaxor lead magnesium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Bursill, L A; Qian, Hua; Peng, Julin; Fan, X D

    1995-10-01

    High-resolution (0.2nm) images are used to locate chemical domains occurring with length scales of 1-5nm in the dielectric relaxor lead magnesium niobate (PMN). The experimental HRTEM images are analysed using computer-simulations and image matching in order to clarify and characterize the nature of the chemical ordering. Madelung electrostatic energy calculations are used to rank a set of structural models for possible ordered and disordered distributions of Nb and Mg over the B-sites of perovskite ABO{sub 3}. Next, the chemical domain textures are modelled using next-nearest-neighbour Ising (NNNI) models and Monte Carlo methods. This results in a preferred model for the B-site distribution (the extended NNN-Ising model), which is used for image simulations. Both HRTEM many-beam bright-and dark-field and single-beam dark-field TEM images are obtained and compared with the experimental images. The final result is a realistic atomic model for the Nb, Mg distribution of PMN. 42 refs., 2 tabs., 10 figs.

  7. Observation and analysis of nanodomain textures in dielectric relaxor lead magnesium niobate

    International Nuclear Information System (INIS)

    Bursill, L.A.; Qian, Hua; Peng, Julin; Fan, X.D.

    1995-01-01

    High-resolution (0.2nm) images are used to locate chemical domains occurring with length scales of 1-5nm in the dielectric relaxor lead magnesium niobate (PMN). The experimental HRTEM images are analysed using computer-simulations and image matching in order to clarify and characterize the nature of the chemical ordering. Madelung electrostatic energy calculations are used to rank a set of structural models for possible ordered and disordered distributions of Nb and Mg over the B-sites of perovskite ABO 3 . Next, the chemical domain textures are modelled using next-nearest-neighbour Ising (NNNI) models and Monte Carlo methods. This results in a preferred model for the B-site distribution (the extended NNN-Ising model), which is used for image simulations. Both HRTEM many-beam bright-and dark-field and single-beam dark-field TEM images are obtained and compared with the experimental images. The final result is a realistic atomic model for the Nb, Mg distribution of PMN. 42 refs., 2 tabs., 10 figs

  8. Microwave-assisted sintering of non-stoichiometric strontium bismuth niobate ceramic: Structural and dielectric properties

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Rajveer [Department of Physics and Astrophysics, University of Delhi, New Delhi 110007 (India); Department of Physics, Atmaram Sanatan Dharma College, University of Delhi, Dhaula Kuan, New Delhi 110021 (India); Luthra, Vandna [Department of Physics, Gargi College, University of Delhi, Siri Fort Road, New Delhi 110049 (India); Tandon, R.P., E-mail: ram_tandon@hotmail.com [Department of Physics and Astrophysics, University of Delhi, New Delhi 110007 (India)

    2016-11-01

    In recent years the microwave sintering has been utilized for the synthesis of materials in enhancement of the properties. In this paper strontium bismuth niobate (Sr{sub 0.8}Bi{sub 2.2}Nb{sub 2}O{sub 9}:SBN) bulk ceramic has been synthesized by microwave reactive sintering and conventional heating techniques. A relative density of 99.6% has been achieved for microwave sintered SBN, which is higher than that of (98.81%) conventionally sintered SBN. The phase formation of SBN synthesized by both processes has been confirmed by X-ray diffraction (XRD). The surface morphology of SBN was observed by scanning electron microscopy (SEM). The microstructure was found to be more uniform in case of SBN sintered by microwave sintering. The dielectric properties of SBN were studied as a function of frequency in the temperature range of 30–500 °C. Both the samples synthesized by two different processes were found to follow Curie–Weiss law above the transition temperature. The Curie temperature was found to be higher for microwave sintered SBN. The dielectric constant and the transition temperature were observed to be higher for SBN ceramic synthesized by microwave sintering technique. The ac and dc activation energy values were also found to be higher for microwave sintered SBN as compared to conventional sintering technique.

  9. Inscription of type I and depressed cladding waveguides in lithium niobate using a femtosecond laser.

    Science.gov (United States)

    Bhardwaj, S; Mittholiya, K; Bhatnagar, A; Bernard, R; Dharmadhikari, J A; Mathur, D; Dharmadhikari, A K

    2017-07-10

    We describe two types of waveguides (type I and depressed cladding) inscribed in lithium niobate using a variable repetition rate (200 kHz-25 MHz), 270 fs duration fiber laser. The type I modification-based waveguides have propagation losses in the range from 1.2 to 10 dB/cm at 1550 nm, depending on experimental parameters. These waveguides are not permanent; they deteriorate over time. Such deterioration of waveguides can be slowed down from 30 days to 100 days by pre-annealing the samples and by writing at a 720 kHz laser repetition rate. The propagation losses measured at 1550 nm show significant improvement for pre-annealed samples. The depressed cladding-inscribed waveguides are permanent, but the propagation loss depends on the number of damage tracks. A track separation of ∼1  μm between adjacent damage tracks yields the lowest propagation loss of 0.5 dB/cm at 1550 nm for a 40 μm diameter waveguide. We observe multimode guidance for sizes in the range of 20-80 μm in these waveguide structures at 1550 nm. Their crystalline nature is found to remain intact, as inferred from second-harmonic generation within the waveguide region.

  10. Phase transitions of sodium niobate powder and ceramics, prepared by solid state synthesis

    Science.gov (United States)

    Koruza, J.; Tellier, J.; Malič, B.; Bobnar, V.; Kosec, M.

    2010-12-01

    Phase transitions of sodium niobate, prepared by the solid state synthesis method, were examined using dielectric measurements, differential scanning calorimetry, and high temperature x-ray diffraction, in order to contribute to the clarification of its structural behavior below 400 °C. Four phase transitions were detected in the ceramic sample using dielectric measurements and differential scanning calorimetry and the obtained temperatures were in a good agreement with previous reports for the transitions of the P polymorph. The anomaly observed by dielectric measurements in the vicinity of 150 °C was frequency dependent and could be related to the dynamics of the ferroelectric nanoregions. The phase transitions of the as-synthesized NaNbO3 powder were investigated using differential scanning calorimetry and high temperature x-ray diffraction. The results show the existence of the Q polymorph at room temperature, not previously reported for the powder, which undergoes a transition to the R polymorph upon heating through a temperature region between 265 and 326.5 °C. This transition is mainly related to the displacement of Na into a more symmetric position and a minor change in the tilting system. The structures at room temperature, 250, 300, and 420 °C were refined by the Rietveld method and the evolution of the tilting system of the octahedral network and cationic displacement are reported.

  11. Phase transitions of sodium niobate powder and ceramics, prepared by solid state synthesis

    International Nuclear Information System (INIS)

    Koruza, J.; Tellier, J.; Malic, B.; Bobnar, V.; Kosec, M.

    2010-01-01

    Phase transitions of sodium niobate, prepared by the solid state synthesis method, were examined using dielectric measurements, differential scanning calorimetry, and high temperature x-ray diffraction, in order to contribute to the clarification of its structural behavior below 400 deg. C. Four phase transitions were detected in the ceramic sample using dielectric measurements and differential scanning calorimetry and the obtained temperatures were in a good agreement with previous reports for the transitions of the P polymorph. The anomaly observed by dielectric measurements in the vicinity of 150 deg. C was frequency dependent and could be related to the dynamics of the ferroelectric nanoregions. The phase transitions of the as-synthesized NaNbO 3 powder were investigated using differential scanning calorimetry and high temperature x-ray diffraction. The results show the existence of the Q polymorph at room temperature, not previously reported for the powder, which undergoes a transition to the R polymorph upon heating through a temperature region between 265 and 326.5 deg. C. This transition is mainly related to the displacement of Na into a more symmetric position and a minor change in the tilting system. The structures at room temperature, 250, 300, and 420 deg. C were refined by the Rietveld method and the evolution of the tilting system of the octahedral network and cationic displacement are reported.

  12. Iron doping of lithium niobate by thermal diffusion from thin film: study of the treatment effect

    Energy Technology Data Exchange (ETDEWEB)

    Ciampolillo, Maria Vittoria; Zaltron, Annamaria; Bazzan, Marco; Argiolas, Nicola; Sada, Cinzia [Universita di Padova (Italy); CNISM, Dipartimento di Fisica ' ' G. Galilei' ' , Padova (Italy); Mignoni, Sabrina; Fontana, Marc [Universite de Metz et Supelec, Laboratoire Materiaux Optiques, Photoniques et Systemes, UMR CNRS 7132, Metz (France)

    2011-07-15

    Thermal diffusion from thin film is one of the most widespread approaches to prepare iron doped regions in lithium niobate with limited size for photorefractive applications. In this work, we investigate the doping process with the aim of determining the best process conditions giving a doped region with the characteristics required for photorefractive applications. Six samples were prepared by changing the atmosphere employed in the diffusion treatment in order to obtain different combination of diffusion profiles and reduction degrees and also to check the effect of employing a wet atmosphere. The compositional, optical, and structural properties are then extensively characterized by combining Secondary ion Mass Spectrometry, UV, visible and IR spectrophotometry, High Resolution X-Rays Diffraction, and Micro-Raman Spectroscopy. Moreover, the sample topography was checked by Atomic Force Microscopy. An analysis of all our data shows that the best results are obtained performing a double step process, i.e. diffusion in oxidizing atmosphere and subsequent reduction at lower temperature in an hydrogen-containing atmosphere. (orig.)

  13. Phase Composition of Samarium Niobate and Tantalate Thin Films Prepared by Sol-Gel Method

    Science.gov (United States)

    Bruncková, H.; Medvecký, Ľ.; Múdra, E.; Kovalčiková, A.; Ďurišin, J.; Šebek, M.; Girman, V.

    2017-12-01

    Samarium niobate SmNbO4 (SNO) and tantalate SmTaO4 (STO) thin films ( 100 nm) were prepared by sol-gel/spin-coating process on alumina substrates with PZT interlayer and annealing at 1000°C. The precursors of films were synthesized using Nb or Ta tartrate complexes. The improvement of the crystallinity of monoclinic M'-SmTaO4 phase via heating was observed through the coexistence of small amounts of tetragonal T-SmTa7O19 phase in STO precursor at 1000°C. The XRD results of SNO and STO films confirmed monoclinic M-SmNbO4 and M'-SmTaO4 phases, respectively, with traces of orthorhombic O-SmNbO4 (in SNO). In STO film, the single monoclinic M'-SmTaO4 phase was revealed. The surface morphology and topography of thin films were investigated by SEM and AFM analysis. STO film was smoother with roughness 3.2 nm in comparison with SNO (6.3 nm). In the microstructure of SNO film, small spherical ( 50 nm) and larger cuboidal particles ( 100 nm) of the SmNbO4 phase were observed. In STO, compact clusters composed of fine spherical SmTaO4 particles ( 20-50 nm) were found. Effect of samarium can contribute to the formation different polymorphs of these films for the application to environmental electrolytic thin film devices.

  14. Anisotropic surface acoustic waves in tungsten/lithium niobate phononic crystals

    Science.gov (United States)

    Sun, Jia-Hong; Yu, Yuan-Hai

    2018-02-01

    Phononic crystals (PnC) were known for acoustic band gaps for different acoustic waves. PnCs were already applied in surface acoustic wave (SAW) devices as reflective gratings based on the band gaps. In this paper, another important property of PnCs, the anisotropic propagation, was studied. PnCs made of circular tungsten films on a lithium niobate substrate were analyzed by finite element method. Dispersion curves and equal frequency contours of surface acoustic waves in PnCs of various dimensions were calculated to study the anisotropy. The non-circular equal frequency contours and negative refraction of group velocity were observed. Then PnC was applied as an acoustic lens based on the anisotropic propagation. Trajectory of SAW passing PnC lens was calculated and transmission of SAW was optimized by selecting proper layers of lens and applying tapered PnC. The result showed that PnC lens can suppress diffraction of surface waves effectively and improve the performance of SAW devices.

  15. Complex capacitance in the representation of modulus of the lithium niobate crystals

    International Nuclear Information System (INIS)

    Alim, Mohammad A.; Batra, A.K.; Bhattacharjee, Sudip; Aggarwal, M.D.

    2011-01-01

    The lithium niobate (LiNbO 3 or LN) single crystal is grown in-house. The ac small-signal electrical characterization is conducted over a temperature range 35≤T≤150 o C as a function of measurement frequency (10≤f≤10 6 Hz). Meaningful observation is noted only in a narrow temperature range 59≤T≤73 o C. These electrical data when analyzed via complex plane formalisms revealed single semicircular relaxation both in the complex capacitance (C * ) and in the modulus (M * ) planes. The physical meaning of this kind of observation is obtained on identifying the relaxation type, and then incorporating respective equivalent circuit model. The simplistic non-blocking nature of the equivalent circuit model obtained via M * -plane is established as the lumped relaxation is identified in the C * -plane. The feature of the eventual equivalent circuit model allows non-blocking aspect for the LN crystal attributing to the presence of the operative dc conduction process. Identification of this leakage dc conduction via C * -plane is portrayed in the M * -plane where the blocking nature is removed. The interacting interpretation between these two complex planes is successfully presented.

  16. Generation and tunable enhancement of a sum-frequency signal in lithium niobate nanowires

    Science.gov (United States)

    Sergeyev, Anton; Reig Escalé, Marc; Grange, Rachel

    2017-02-01

    Recent developments in the fabrication of lithium niobate (LiNbO3) structures down to the nanoscale opens up novel applications of this versatile material in nonlinear optics. Current nonlinear optical studies in sub-micron waveguides are mainly restricted to the generation of second and third harmonics. In this work, we demonstrate the generation and waveguiding of the sum-frequency generation (SFG) signal in a single LiNbO3 nanowire with a cross-section of 517 nm  ×  654 nm. Furthermore, we enhance the guided SFG signal 17.9 times by means of modal phase matching. We also display tuning of the phase-matched wavelength by varying the nanowire cross-section and changing the polarization of the incident laser. The results prove that LiNbO3 nanowires can be successfully used for nonlinear wave-mixing applications and assisting the miniaturization of optical devices. , which features invited work from the best early-career researchers working within the scope of J Phys D. This project is part of the Journal of Physics series’ 50th anniversary celebrations in 2017. Rachel Grange was selected by the Editorial Board of J Phys D as an Emerging Leader.

  17. High-Q photonic resonators and electro-optic coupling using silicon-on-lithium-niobate

    Science.gov (United States)

    Witmer, Jeremy D.; Valery, Joseph A.; Arrangoiz-Arriola, Patricio; Sarabalis, Christopher J.; Hill, Jeff T.; Safavi-Naeini, Amir H.

    2017-04-01

    Future quantum networks, in which superconducting quantum processors are connected via optical links, will require microwave-to-optical photon converters that preserve entanglement. A doubly-resonant electro-optic modulator (EOM) is a promising platform to realize this conversion. Here, we present our progress towards building such a modulator by demonstrating the optically-resonant half of the device. We demonstrate high quality (Q) factor ring, disk and photonic crystal resonators using a hybrid silicon-on-lithium-niobate material system. Optical Q factors up to 730,000 are achieved, corresponding to propagation loss of 0.8 dB/cm. We also use the electro-optic effect to modulate the resonance frequency of a photonic crystal cavity, achieving a electro-optic modulation coefficient between 1 and 2 pm/V. In addition to quantum technology, we expect that our results will be useful both in traditional silicon photonics applications and in high-sensitivity acousto-optic devices.

  18. Effect of powder processing conditions on the electromechanical properties of lithium doped potassium sodium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Mensur-Alkoy, E.; Berksoy-Yavuz, A.

    2016-07-01

    Lithium doped potassium sodium niobate ceramics with (K0.50−x/2Na0.50−x/2Lix)NbO3 composition where x=0.04 and 0.07 were fabricated by solid state calcination and pressureless sintering methods. However, two different powder processing and calcination routes were used in this study and their effect on the structural and electrical properties were investigated and discussed. The routes were namely loose calcination and compact calcination. A general trend of decreasing grain size was observed in the sintered ceramics prepared from these powders. The most drastic effect was observed on the electromechanical properties of the samples, where the maximum strain of 7% lithium modified sample under an E-field of 50kV/cm was increased from 0.09% to 0.12% by changing processing route. Furthermore, hysteretic behavior of the strain was found to decrease. This tendency was also valid for ferroelectric hysteresis property, with remnant polarization (2Pr) increasing from 23μC/cm2 to 46μC/cm2. The improvements observed in the electrical properties were discussed on the basis of chemical homogeneity and uniform ionic distribution. (Author)

  19. Barium fluoride surface preparation, analysis and UV reflective coatings at Lawrence Livermore National Laboratory

    International Nuclear Information System (INIS)

    Wuest, C.R.

    1992-01-01

    Lawrence Livermore National Laboratory (LLNL) has begun a program of study on barium fluoride scintillating crystals for the Barium Fluoride Electromagnetic Calorimeter Collaboration. This program has resulted in a number of significant improvements in the mechanical processing, polishing and coating of barium fluoride crystals. Techniques have been developed using diamond-loaded pitch lapping that can produce 15 angstrom RMS surface finishes over large areas. These lapped surfaces have been shown to be crystalline using Rutherford Back-scattering (RBS). Also, special polishing fixtures have been designed based on mounting technology developed for the 1.1 m diameter optics used in LLNL's Nova Laser. These fixtures allow as many as five 25--50 cm long barium fluoride crystals to be polished and lapped at a time with the necessary tolerances for the 16,000 crystal Barium Fluoride Calorimeter. In addition, results will be presented on coating barium fluoride with UV reflective layers of magnesium fluoride and aluminum

  20. Early colon cancer : findings on double contrast barium enema

    International Nuclear Information System (INIS)

    Kim, Seung Kwon; Lim, Jae Hoon; Lee, Soon Jin; Lim, Hyo Keun

    1998-01-01

    The purpose of this study is to describe the radiologic findings of early colon cancer on double-contrast barium enema. We retrospectively reviewed the double-contrast barium enemas of eight patients (M:F = 6:2; mean age : 67 yrs; range : 48-77 yrs) who were pathologically proven to be early colon cancer. The location, size and gross morphology of lesions was evaluated using double-contrast barium enema, while depth of invasion, degree of differentiation, precancerous lesions and lymph node metastasis were evaluated histopathologically. Early colon cancer was found in the rectum (n=4), sigmoid colon (n=3) and ascending colon (n=1). The size of mass ranged from 2.3 ∼ 8.3 (mean, 4.6) cm. And the polypoid type was most common (n=7); this was subdivided into sessile (Is, n=5), semipedunculated (Isp, n=1) and pedunculated type (Ip, n=1). Another mass was a sessile polypoid combined with a flat depressed lesion. In eight cases, four cancers were confined to the mucosa, while the remaining four had infiltrated the submucosa. Most cancers arose from villous and villotubular adenoma. All cases were well-differentiated adenocarcinoma and no metastasis to lymph nodes had occurred. In early colon cancer, lesions were mainly polypoid and large. Most arose from villous and villotubular adenoma. (author). 19 refs., 1 tab., 3 figs

  1. Complications from radiographer-performed double contrast barium enemas

    Energy Technology Data Exchange (ETDEWEB)

    Vora, P.; Chapman, A. E-mail: anthony.chapman@leedsth.nhs.uk

    2004-04-01

    AIM: To determine the types and rates of complications encountered by radiographers when performing double contrast barium enemas (DCBE). MATERIALS AND METHODS: Seven hundred and forty-one questionnaires were posted to radiographers who had in the last 5 years attended one of the biannual barium enema training courses. RESULTS: Of 741 questionnaires posted 407 (54.9%) were returned completed. Approximately 348,000 barium enema examinations had been performed. Fifty-nine radiographers reported 89 complications, including 13 intra-peritoneal and 11 extra-peritoneal perforations. There were five deaths (mortality 1 in 70,000). Deaths resulted from two of 24 (10%) perforations, two of 45 (5%) cardiac events and one cerebrovascular accident that occurred during an examination. CONCLUSIONS: Radiographers have been regularly performing DCBEs for almost a decade. The mortality for radiographer-performed DCBE is similar to that previously reported for radiologists, although a slightly higher rate of perforation is noted and so this is an area where radiographer training should be targeted.

  2. Complications from radiographer-performed double contrast barium enemas

    International Nuclear Information System (INIS)

    Vora, P.; Chapman, A.

    2004-01-01

    AIM: To determine the types and rates of complications encountered by radiographers when performing double contrast barium enemas (DCBE). MATERIALS AND METHODS: Seven hundred and forty-one questionnaires were posted to radiographers who had in the last 5 years attended one of the biannual barium enema training courses. RESULTS: Of 741 questionnaires posted 407 (54.9%) were returned completed. Approximately 348,000 barium enema examinations had been performed. Fifty-nine radiographers reported 89 complications, including 13 intra-peritoneal and 11 extra-peritoneal perforations. There were five deaths (mortality 1 in 70,000). Deaths resulted from two of 24 (10%) perforations, two of 45 (5%) cardiac events and one cerebrovascular accident that occurred during an examination. CONCLUSIONS: Radiographers have been regularly performing DCBEs for almost a decade. The mortality for radiographer-performed DCBE is similar to that previously reported for radiologists, although a slightly higher rate of perforation is noted and so this is an area where radiographer training should be targeted

  3. Microwave-hydrothermal synthesis of barium strontium titanate nanoparticles

    International Nuclear Information System (INIS)

    Simoes, A.Z.; Moura, F.; Onofre, T.B.; Ramirez, M.A.; Varela, J.A.; Longo, E.

    2010-01-01

    Research highlights: → Barium strontium titanate nanoparticles were obtained by the Hydrothemal microwave technique (HTMW) → This is a genuine technique to obtain nanoparticles at low temperature and short times → Barium strontium titanate free of carbonates with tetragonal structure was grown at 130 o C. - Abstract: Hydrothermal-microwave method (HTMW) was used to synthesize crystalline barium strontium titanate (Ba 0.8 Sr 0.2 TiO 3 ) nanoparticles (BST) in the temperature range of 100-130 o C. The crystallization of BST with tetragonal structure was reached at all the synthesis temperatures along with the formation of BaCO 3 as a minor impurity at lower syntheses temperatures. Typical FT-IR spectra for tetragonal (BST) nanoparticles presented well defined bands, indicating a substantial short-range order in the system. TG-DTA analyses confirmed the presence of lattice OH- groups, commonly found in materials obtained by HTMW process. FE/SEM revealed that lower syntheses temperatures led to a morphology that consisted of uniform grains while higher syntheses temperature consisted of big grains isolated and embedded in a matrix of small grains. TEM has shown BST nanoparticles with diameters between 40 and 80 nm. These results show that the HTMW synthesis route is rapid, cost effective, and could serve as an alternative to obtain BST nanoparticles.

  4. Spectrophotometry of barium, CH, and R-type carbon stars

    International Nuclear Information System (INIS)

    Gow, C.E.

    1976-01-01

    Observations of 35 barium, CH, R, and hydrogen-deficient carbon stars, along with ten comparison K giants, have been made with the Indiana rapid spectrum scanner and the Indiana SIT vidicon spectrometer. The scanner observations cover a wavelength range of 3300--7000 A at 30-A resolution, while the SIT vidicon observations cover a wavelength range of 3800--5000 A at 2.5-A resolution. The data have been used to form molecular indices for a quantitative measurement of the strength of molecular features appearing in this region of the spectrum, and to compare the spectral energy distribution of carbon and oxygen stars over the entire observed wavelength range. We find the C 2 Swan index correlated strongly with both the strength of an unidentified feature centered near 4000 A, and the barium-to-hydrogen ratio. A detailed comparison of the spectral energy distribution of the barium stars with normal K giants shows that this unidentified absorption feature consists of two shallows depressions, one at 4000 A and another at 4325 A

  5. Effects of polyacrylic acid additive on barium sulfate particle morphology

    Energy Technology Data Exchange (ETDEWEB)

    Li, Jie; Liu, Dandan; Jiang, Hongkun; Wang, Jun; Jing, Xiaoyan; Chen, Rongrong [Key Laboratory of Superlight Material and Surface Technology of Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 (China); Zhu, Wenting [Department of Gastroenterology, Harbin Medical University Cancer Hospital, Harbin 150081 (China); Han, Shihui [Key Laboratory of Superlight Material and Surface Technology of Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 (China); Li, Wanyou [College of Power and Energy Engineering, Harbin Engineering University, Harbin 150001 (China); Wei, Hao, E-mail: weihao7512@126.com [Key Laboratory of Superlight Material and Surface Technology of Ministry of Education, College of Material Science and Chemical Engineering, Harbin Engineering University, Harbin 150001 (China); College of Power and Energy Engineering, Harbin Engineering University, Harbin 150001 (China)

    2016-06-01

    In this paper, polyacrylic acid (PAA) was used as a growth modifier to control micron-sized barium sulfate particles via a simple precipitation reaction between sodium sulfate and barium chloride at ambient temperature. The barium sulfate particles were exhibited various morphologies, such as monodisperse spheres, ellipsoids, rose-like aggregates, etc. To better understand the formation mechanisms of the various morphologies of these particles, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray diffraction (XRD) and thermo-gravimetric analysis (TGA) were employed. It was found that the PAA concentration, pH, and Ba{sup 2+} and SO{sub 4}{sup 2−} ions concentrations were the most important parameters controlling the morphology of the BaSO{sub 4} particles. These parameters affected the BaSO{sub 4} morphology by influencing the interactions between the PAA carboxyl groups and inorganic ions and the conformation change of the PAA molecular chains. Moreover, this work attempts to provide a preliminary understanding of the formation of the spherical BaSO{sub 4} particles with the randomly coiled conformation of the polymer. - Highlights: • Polyacrylic acid (PAA) was used as a growth modifier to control micron-sized BaSO{sub 4} particles. • The PAA/BaSO{sub 4} particles were exhibited various morphologies. • Provide a preliminary understanding of the formation mechanism of BaSO{sub 4} particles.

  6. Barium as a potential indicator of phosphorus in agricultural runoff.

    Science.gov (United States)

    Ahlgren, Joakim; Djodjic, Faruk; Wallin, Mats

    2012-01-01

    In many catchments, anthropogenic input of contaminants, and in particular phosphorus (P), into surface water is a mixture of agricultural and sewage runoff. Knowledge about the relative contribution from each of these sources is vital for mitigation of major environmental problems such as eutrophication. In this study, we investigated whether the distribution of trace elements in surface waters can be used to trace the contamination source. Water from three groups of streams was investigated: streams influenced only by agricultural runoff, streams influenced mainly by sewage runoff, and reference streams. Samples were collected at different flow regimes and times of year and analyzed for 62 elements using ICP-MS. Our results show that there are significant differences between the anthropogenic sources affecting the streams in terms of total element composition and individual elements, indicating that the method has the potential to trace anthropogenic impact on surface waters. The elements that show significant differences between sources are strontium (p barium (p barium shows the greatest potential as a tracer for an individual source of anthropogenic input to surface waters. We observed a strong relationship between barium and total P in the investigated samples (R(2) = 0.78), which could potentially be used to apportion anthropogenic sources of P and thereby facilitate targeting of mitigation practices. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

  7. Effect of the structure and mechanical properties of the near-surface layer of lithium niobate single crystals on the manufacture of integrated optic circuits

    Science.gov (United States)

    Sosunov, A. V.; Ponomarev, R. S.; Yur'ev, V. A.; Volyntsev, A. B.

    2017-01-01

    This paper shows that the near-surface layer of a lithium niobate single layer 15 μm in depth is essentially different from the rest of the volume of the material from the standpoint of composition, structure, and mechanical properties. The pointed out differences are due to the effect of cutting, polishing, and smoothing of the lithium niobate plates, which increase the density of point defects and dislocations. The increasing density of the structural defects leads to uncontrollable changes in the conditions of the formations of waveguides and the drifting of characteristics of integrated optical circuits. The results obtained are very important for the manufacture of lithium niobate based integrated optical circuits.

  8. Enhanced photoelectrochemical properties of 100 MeV Si8+ ion irradiated barium titanate thin films

    International Nuclear Information System (INIS)

    Solanki, Anjana; Choudhary, Surbhi; Satsangi, Vibha R.; Shrivastav, Rohit; Dass, Sahab

    2013-01-01

    Highlights: ► Effect of 100 MeV Si 8+ ion irradiation on photoelectrochemical (PEC) properties of BaTiO 3 thin films was studied. ► Films were deposited on Indium doped Tin Oxide (ITO) coated glass by sol–gel spin coating technique. ► Optimal irradiation fluence for best PEC response was 5 × 10 11 ion cm −2 . ► Maximum photocurrent density was observed to be 0.7 mA cm −2 at 0.4 V/SCE. ► Enhanced photo-conversion efficiency was due to maximum negative flatband potential, donor density and lowest resistivity. -- Abstract: Effects of high electronic energy deposition on the structure, surface topography, optical property and photoelectrochemical behavior of barium titanate (BaTiO 3 ) thin films were investigated by irradiating films with 100 MeV Si 8+ ions at different ion fluences in the range of 1 × 10 11 –2 × 10 13 ions cm −2 . BaTiO 3 thin films were deposited on indium tin oxide coated glass substrate by sol gel spin coating method. Irradiation induced modifications in the films were analyzed using the results from XRD, SEM, cross sectional SEM, AFM and UV–Vis spectrometry. Maximum photocurrent density of 0.7 mA cm −2 at 0.4 V/SCE and applied bias hydrogen conversion efficiency (ABPE) of 0.73% was observed for BaTiO 3 film irradiated at 5 × 10 11 ions cm −2 , which can be attributed to maximum negative value of the flatband potential and donor density and lowest resistivity

  9. Strontium-90 sorption from fresh waters in the process of barium manganite modification

    International Nuclear Information System (INIS)

    Ryzhen'kov, A.P.; Egorov, Yu.V.

    1995-01-01

    Strontium-90 extraction by barium manganite from fresh water (natural non-salty water in open ponds) may be increased adding to the solution the sulfate anion containing reagents that modify a sorbent and chemically bind a sorbate. Heterogeneous anion-exchanging reaction of barium manganite transformation into barium sulfate-manganese dioxide and simultaneous coprecipitation of strontium sulfate (microelement) occur as a result of it. 9 refs., 4 figs., 1 tab

  10. Simplified assessment of segmental gastrointestinal transit time with orally small amount of barium

    Energy Technology Data Exchange (ETDEWEB)

    Yuan, Weitang; Zhang, Zhiyong; Liu, Jinbo; Li, Zhen; Song, Junmin; Wu, Changcai [Department of Colorectal Surgery, The First Affiliated Hospital and Institute of Clinical Medicine, Zhengzhou University, 450052 Zhengzhou (China); Wang, Guixian, E-mail: guixianwang@hotmail.com [Department of Colorectal Surgery, The First Affiliated Hospital and Institute of Clinical Medicine, Zhengzhou University, 450052 Zhengzhou (China)

    2012-09-15

    Objective: To determine the effectiveness and advantage of small amount of barium in the measurement of gastrointestinal transmission function in comparison with radio-opaque pallets. Methods: Protocal 1: 8 healthy volunteers (male 6, female 2) with average age 40 ± 6.1 were subjected to the examination of radio-opaque pellets and small amount of barium with the interval of 1 week. Protocol 2: 30 healthy volunteers in group 1 (male 8, female 22) with average age 42.5 ± 8.1 and 50 patients with chronic functional constipation in group 2 (male 11, female 39) with average age 45.7 ± 7.8 were subjected to the small amount of barium examination. The small amount of barium was made by 30 g barium dissolved in 200 ml breakfast. After taking breakfast which contains barium, objectives were followed with abdominal X-ray at 4, 8, 12, 24, 48, 72, 96 h until the barium was evacuated totally. Results: Small amount of barium presented actual chyme or stool transit. The transit time of radio-opaque pallets through the whole gastrointestinal tract was significantly shorter than that of barium (37 ± 8 h vs. 47 ± 10 h, P < 0.05) in healthy people. The transit times of barium in constipation patients were markedly prolonged in colon (61.1 ± 22 vs. 37.3 ± 11, P < 0.01) and rectum (10.8 ± 3.7 vs. 2.3 ± 0.8 h, P < 0.01) compared with unconstipated volunteers. Transit times in individual gastrointestinal segments were also recorded by using small amount of barium, which allowed identifying the subtypes of constipation. Conclusion: The small amount barium examination is a convenient and low cost method to provide the most useful and reliable information on the transmission function of different gastrointestinal segments and able to classify the subtypes of slow transit constipation.

  11. A Comparative Study on Magnetostructural Properties of Barium Hexaferrite Powders Prepared by Polyethylene Glycol

    OpenAIRE

    Zehra Durmus

    2014-01-01

    Nanocrystalline particles of barium hexaferrite were synthesized by a sol-gel combustion route using nitrate-citrate gels prepared from metal nitrates and citric acid solutions with Fe/Ba molar ratio 12. The present paper aims to study the effect of addition of polyethylene glycol (PEG) solutions with different molecular weights (MW: 400, 2000, and 10.000 g/mol) on magnetostructural properties of barium hexaferrite. The formation of the barium hexaferrite was inspected using X-ray diffractio...

  12. Aspiration of barium contrast medium in an elderly man with disordered swallowing

    OpenAIRE

    Bağcı Ceyhan, B.; Çelikel, T.; Koç, M.; Ahıskalı, R.; Biren, T.; Ataizi Çelikel, Ç.

    1995-01-01

    The aspiration of contrast medium during the investigation of gastrointestinal diseases is a well recognized hazard, particularly in patients with swallowing disorders. A case is reported in which accidental aspiration of contrast barium occurred owing to disordered swallowing in an elderly man. The infiltration on chest x-ray persisted 2 years after barium contrast aspiration. Inflammatory reaction and retractile, granular material observed in lung biopsy specimens suggested barium-induced p...

  13. Simplified assessment of segmental gastrointestinal transit time with orally small amount of barium

    International Nuclear Information System (INIS)

    Yuan, Weitang; Zhang, Zhiyong; Liu, Jinbo; Li, Zhen; Song, Junmin; Wu, Changcai; Wang, Guixian

    2012-01-01

    Objective: To determine the effectiveness and advantage of small amount of barium in the measurement of gastrointestinal transmission function in comparison with radio-opaque pallets. Methods: Protocal 1: 8 healthy volunteers (male 6, female 2) with average age 40 ± 6.1 were subjected to the examination of radio-opaque pellets and small amount of barium with the interval of 1 week. Protocol 2: 30 healthy volunteers in group 1 (male 8, female 22) with average age 42.5 ± 8.1 and 50 patients with chronic functional constipation in group 2 (male 11, female 39) with average age 45.7 ± 7.8 were subjected to the small amount of barium examination. The small amount of barium was made by 30 g barium dissolved in 200 ml breakfast. After taking breakfast which contains barium, objectives were followed with abdominal X-ray at 4, 8, 12, 24, 48, 72, 96 h until the barium was evacuated totally. Results: Small amount of barium presented actual chyme or stool transit. The transit time of radio-opaque pallets through the whole gastrointestinal tract was significantly shorter than that of barium (37 ± 8 h vs. 47 ± 10 h, P < 0.05) in healthy people. The transit times of barium in constipation patients were markedly prolonged in colon (61.1 ± 22 vs. 37.3 ± 11, P < 0.01) and rectum (10.8 ± 3.7 vs. 2.3 ± 0.8 h, P < 0.01) compared with unconstipated volunteers. Transit times in individual gastrointestinal segments were also recorded by using small amount of barium, which allowed identifying the subtypes of constipation. Conclusion: The small amount barium examination is a convenient and low cost method to provide the most useful and reliable information on the transmission function of different gastrointestinal segments and able to classify the subtypes of slow transit constipation

  14. Results of a cooperative study for the evaluation of the barium meal Falibaryt HD

    International Nuclear Information System (INIS)

    Reisinger, W.; Liess, G.; Beckmann, D.; Block, H.G.; Dietze, R.; Grosche, N.; Hall, E.; Lasch, G.; Knoth, H.J.; Kroeger, W.

    1986-01-01

    The diagnostic capabilities of radiologic investigations of the stomach in double contrast can be significantly improved with high-density low-viscosity barium meals. In the GDR the barium meal Falibaryt HD with a barium sulfate content of 215 g per 100 ml suspension has been developed. In nearly 1,000 radiologic investigations of the stomach (81% in relaxation with spasmolytics, 66% without hypotony) all fine structures were well imaged and the preparation therefore is comparable with the best barium meals presently on the market. (author)

  15. Barium titanate coated with magnesium titanate via fused salt method and its dielectric property

    International Nuclear Information System (INIS)

    Chen Renzheng; Cui Aili; Wang Xiaohui; Li Longtu

    2003-01-01

    Barium titanate fine particles were coated homogeneously with magnesium titanate via the fused salt method. The thickness of the magnesium titanate film is 20 nm, as verified by TEM and XRD. The mechanism of the coating is that: when magnesium chloride is liquated in 800 deg. C, magnesium will replace barium in barium titanate, and form magnesium titanate film on the surface of barium titanate particles. Ceramics sintered from the coated particles show improved high frequency ability. The dielectric constant is about 130 at the frequency from 1 to 800 MHz

  16. Effects of powdered versus liquid barium on the viscosity of fluids used in modified swallow studies

    International Nuclear Information System (INIS)

    Baron, J.; Alexander, T.

    2003-01-01

    To determine if the viscosity of thickened juice mixtures used in modified barium swallow studies significantly changes with the addition of powdered barium. We also describe a test formulation created using liquid barium, which has a negligible effect on juice viscosity. The viscosities of water and standardized honey- and nectar-consistency juices mixed with different amounts of powdered barium were measured by timing the laminar flow of a given initial hydrostatic head of fluid under gravity though an orifice of fixed diameter. Standardized juices were then mixed with a liquid formulation of barium and with measured quantities of water to produce viscosities that more closely equated with those of the standardized juices. With the addition of powdered barium, viscosity increased in all fluids, most markedly with the nectar-consistency juice. Liquid barium formulations maintained the viscosities of the original thickened juices. Rendering juices radio-opaque with barium powder results in dramatic increases in the viscosity of the resulting mixture and compromises diagnostic accuracy. Liquid barium preparations have the advantage that they can be rapidly and accurately dispensed by syringe, and their use does not significantly increase the viscosity of the preparation. (author)

  17. Effects of powdered versus liquid barium on the viscosity of fluids used in modified swallow studies

    Energy Technology Data Exchange (ETDEWEB)

    Baron, J.; Alexander, T. [Univ. of Alberta, Dept. of Radiology, Edmonton, Alberta (Canada)

    2003-06-01

    To determine if the viscosity of thickened juice mixtures used in modified barium swallow studies significantly changes with the addition of powdered barium. We also describe a test formulation created using liquid barium, which has a negligible effect on juice viscosity. The viscosities of water and standardized honey- and nectar-consistency juices mixed with different amounts of powdered barium were measured by timing the laminar flow of a given initial hydrostatic head of fluid under gravity though an orifice of fixed diameter. Standardized juices were then mixed with a liquid formulation of barium and with measured quantities of water to produce viscosities that more closely equated with those of the standardized juices. With the addition of powdered barium, viscosity increased in all fluids, most markedly with the nectar-consistency juice. Liquid barium formulations maintained the viscosities of the original thickened juices. Rendering juices radio-opaque with barium powder results in dramatic increases in the viscosity of the resulting mixture and compromises diagnostic accuracy. Liquid barium preparations have the advantage that they can be rapidly and accurately dispensed by syringe, and their use does not significantly increase the viscosity of the preparation. (author)

  18. Barium and Tc-poor S stars: Binary masqueraders among carbon stars

    OpenAIRE

    Jorissen, A.; Van Eck, S.

    1997-01-01

    The current understanding of the origin of barium and S stars is reviewed, based on new orbital elements and binary frequencies. The following questions are addressed: (i) Is binarity a necessary condition to produce a barium star? (ii) What is the mass transfer mode (wind accretion or RLOF?) responsible for their formation? (iii) Do barium stars form as dwarfs or as giants? (iv) Do barium stars evolve into Tc-poor S stars? (v) What is the relative frequency of Tc-rich and Tc-poor S stars?

  19. Prompt striations observed in a barium thermite release at 335 km

    International Nuclear Information System (INIS)

    Simons, D.J.; Pongratz, M.B.; Smith, G.M.; Barasch, G.E.; Fitzgerald, T.J.

    1981-01-01

    Three barium clouds have been released from a single rocket at altitudes of 335, 443, and 535 km. The releases were by means of barium thermite injection. Adding the different cross-field velocity components of the rocket at each of the releases resulted in barium clouds with different kinetic velocity distributions. The barium cloud with the most peaked velocity distribution striated promptly, in good agreement with theoretical predictions based on a kinetic plasma instability. Details of the data analysis and experiment are discussed

  20. Spin glasses

    International Nuclear Information System (INIS)

    Mookerjee, Abhijit

    1976-01-01

    ''Spin glasses'', are entire class of magnetic alloys of moderate dilution, in which the magnetic atoms are far enough apart to be unlike the pure metal, but close enough so that the indirect exchange energy between them (mediated by the s-d interaction between local moments and conduction electrons) dominates all other energies. Characteristic critical phenomena displayed such as freezing of spin orientation at 'Tsub(c)' and spreading of magnetic ordering, are pointed out. Anomalous behaviour, associated with these critical phenomena, as reflected in : (i) Moessbauer spectroscopy giving hyperfine splitting at Tsub(c), (ii) maxima in susceptibility and remanent magnetism, (iii) thermopower maxima and change in slope, (iv) Characteristic cusp in susceptibility and its removal by very small magnetic fields, and (v) conductivity-resistivity measurements, are discussed. Theoretical developments aimed at explaining these phenomena, in particular, the ideas from percolation and localisation theories, and the approach based on the gellations of polymers, are discussed. Finally, a new approach based on renormalisation group in disordered systems is also briefly mentioned. (K.B.)

  1. Radiation losses in microwave K_u region by conducting pyrrole/barium titanate and barium hexaferrite based nanocomposites

    International Nuclear Information System (INIS)

    Kaur, Talwinder; Kumar, Sachin; Narang, S.B.; Srivastava, A.K.

    2016-01-01

    Nanocomposites of substituted barium hexaferrite and barium titanate embedded in a polymer were synthesized via emulsion polymerization. The study was performed by using X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, electron spin resonance spectroscopy, a vibrating sample magnetometer and a vector network analyzer. It is found that maximum radiation loss occur at 16.09 GHz (−14.23 dB) frequency owing to the combined effect of conducting polymer, suitable dielectric and magnetic material. This suggests that prepared material is suitable for radiation losses. Micro structural study reveals the presence of all the phases of the compounds comprises composite. Benzene ring absorption band (at 1183 cm"−"1) in FT-IR spectra illustrates the presence of polymer. Surface morphology reveals the presence of array of particles encapsulated by the polymer. - Highlights: • Composites having polymer, barium titanate and hexaferrite have been successfully prepared. • Effective radiation absorption and losses have been achieved. • Magnetic properties have made an impact on shielding effectiveness.

  2. Radiation losses in microwave K{sub u} region by conducting pyrrole/barium titanate and barium hexaferrite based nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Talwinder [Department of Physics, Lovely Professional University, Phagwara 144411 (India); Kumar, Sachin [Department of Chemistry, Guru Nanak Dev University, Amritsar 143005 (India); Narang, S.B. [Department of Electronics Technology, Guru Nanak Dev University, Amritsar 143005 (India); Srivastava, A.K., E-mail: srivastava_phy@yahoo.co.in [Department of Physics, Lovely Professional University, Phagwara 144411 (India)

    2016-12-15

    Nanocomposites of substituted barium hexaferrite and barium titanate embedded in a polymer were synthesized via emulsion polymerization. The study was performed by using X-ray diffraction, Fourier transform infrared spectroscopy, transmission electron microscopy, electron spin resonance spectroscopy, a vibrating sample magnetometer and a vector network analyzer. It is found that maximum radiation loss occur at 16.09 GHz (−14.23 dB) frequency owing to the combined effect of conducting polymer, suitable dielectric and magnetic material. This suggests that prepared material is suitable for radiation losses. Micro structural study reveals the presence of all the phases of the compounds comprises composite. Benzene ring absorption band (at 1183 cm{sup −1}) in FT-IR spectra illustrates the presence of polymer. Surface morphology reveals the presence of array of particles encapsulated by the polymer. - Highlights: • Composites having polymer, barium titanate and hexaferrite have been successfully prepared. • Effective radiation absorption and losses have been achieved. • Magnetic properties have made an impact on shielding effectiveness.

  3. Potassium Sodium Niobate-Based Lead-Free Piezoelectric Multilayer Ceramics Co-Fired with Nickel Electrodes

    Directory of Open Access Journals (Sweden)

    Shinichiro Kawada

    2015-11-01

    Full Text Available Although lead-free piezoelectric ceramics have been extensively studied, many problems must still be overcome before they are suitable for practical use. One of the main problems is fabricating a multilayer structure, and one solution attracting growing interest is the use of lead-free multilayer piezoelectric ceramics. The paper reviews work that has been done by the authors on lead-free alkali niobate-based multilayer piezoelectric ceramics co-fired with nickel inner electrodes. Nickel inner electrodes have many advantages, such as high electromigration resistance, high interfacial strength with ceramics, and greater cost effectiveness than silver palladium inner electrodes. However, widely used lead zirconate titanate-based ceramics cannot be co-fired with nickel inner electrodes, and silver palladium inner electrodes are usually used for lead zirconate titanate-based piezoelectric ceramics. A possible alternative is lead-free ceramics co-fired with nickel inner electrodes. We have thus been developing lead-free alkali niobate-based multilayer ceramics co-fired with nickel inner electrodes. The normalized electric-field-induced thickness strain (Smax/Emax of a representative alkali niobate-based multilayer ceramic structure with nickel inner electrodes was 360 pm/V, where Smax denotes the maximum strain and Emax denotes the maximum electric field. This value is about half that for the lead zirconate titanate-based ceramics that are widely used. However, a comparable value can be obtained by stacking more ceramic layers with smaller thicknesses. In the paper, the compositional design and process used to co-fire lead-free ceramics with nickel inner electrodes are introduced, and their piezoelectric properties and reliabilities are shown. Recent advances are introduced, and future development is discussed.

  4. Linear diffraction of light waves on periodically poled domain structures in lithium niobate crystals: collinear, isotropic, and anisotropic geometries

    International Nuclear Information System (INIS)

    Shandarov, S M; Mandel, A E; Akylbaev, T M; Borodin, M V; Savchenkov, E N; Smirnov, S V; Akhmatkhanov, A R; Shur, V Ya

    2017-01-01

    The possible variants of experimental observation of light diffraction on periodically poled domain structures (PPDS) in the lithium niobate crystal with 180-degree domain Y-walls are considered. We experimentally investigated isotropic and anisotropic diffraction of coherent light (λ = 655nm) on the PPDS with spatial period Λ = 8.79 μm produced by poling method in a LiNbO 3 : 5% MgO crystal. The central wavelength of irradiation experiencing a collinear diffraction on these PPDS is estimated as λ c = 455 nm. (paper)

  5. The compact converter of Bessel beams of zero and second orders on the basis of z-cut lithium niobate

    International Nuclear Information System (INIS)

    Paranin, V D; Karpeev, S V; Khonina, S N; Tukmakov, K N

    2016-01-01

    Transformation of zero-order Bessel beams into a second-order vortex beam in the process of propagation in a c-cut of lithium niobate LiNbO 3 crystal has been investigated experimentally. The possibility of controlling beam transformation by means of changing the curve radius of the illuminating beam is shown. The possibility of Bessel beam transforming by compact devices on the basis of thin c-cuts of uniaxial crystals with a diffraction mask formed on their surface is proved. (paper)

  6. Conversion of broadband IR radiation and structural disorder in lithium niobate single crystals with low photorefractive effect

    Science.gov (United States)

    Litvinova, Man Nen; Syuy, Alexander V.; Krishtop, Victor V.; Pogodina, Veronika A.; Ponomarchuk, Yulia V.; Sidorov, Nikolay V.; Gabain, Aleksei A.; Palatnikov, Mikhail N.; Litvinov, Vladimir A.

    2016-11-01

    The conversion of broadband IR radiation when the noncritical phase matching condition is fulfilled in lithium niobate (LiNbO3) single crystals with stoichiometric (R = Li/Nb = 1) and congruent (R = 0.946) compositions, as well as in congruent single crystals doped with zinc has been investigated. It is shown that the spectrum parameters of converted radiation, such as the conversion efficiency, spectral width and position of maximum, depend on the ordering degree of structural units of the cation sublattice along the polar axis of crystal.

  7. Heterogeneous integration of lithium niobate and silicon nitride waveguides for wafer-scale photonic integrated circuits on silicon.

    Science.gov (United States)

    Chang, Lin; Pfeiffer, Martin H P; Volet, Nicolas; Zervas, Michael; Peters, Jon D; Manganelli, Costanza L; Stanton, Eric J; Li, Yifei; Kippenberg, Tobias J; Bowers, John E

    2017-02-15

    An ideal photonic integrated circuit for nonlinear photonic applications requires high optical nonlinearities and low loss. This work demonstrates a heterogeneous platform by bonding lithium niobate (LN) thin films onto a silicon nitride (Si3N4) waveguide layer on silicon. It not only provides large second- and third-order nonlinear coefficients, but also shows low propagation loss in both the Si3N4 and the LN-Si3N4 waveguides. The tapers enable low-loss-mode transitions between these two waveguides. This platform is essential for various on-chip applications, e.g., modulators, frequency conversions, and quantum communications.

  8. X-ray analysis of phase coexistence and electric poling processing in alkaline niobate-based compositions

    International Nuclear Information System (INIS)

    Fu Jian; Zuo Ruzhong; Liu Yi

    2010-01-01

    The characteristic and origin of two-phase coexistence and the content of each phase in typical alkaline niobate-based lead-free compositions were investigated through the refinement of X-ray diffraction peaks and the measurement of dielectric constant versus temperature curves. The diffuse nature of polymorphic phase transition has resulted in the coexistence of two ferroelectric phases within a wide composition and temperature range. As a result, the optimum piezoelectric properties appear in the composition rich in tetragonal phases and there is a remarkable poling temperature effect. Discussions on the difference between morphotropic phase boundary and polymorphic phase boundary were made in combination with the variation of electrical properties.

  9. Experimental and theoretical investigation of lattice defect structures in a series of Zn, Fe-doped nonstoichiometric lithium niobate

    International Nuclear Information System (INIS)

    Guo Fengyun; Lue Qiang; Sun Liang; Li Hongtao; Zhen Xihe; Xu Yuheng; Zhao Liancheng

    2006-01-01

    A series of the double doped lithium niobate (LiNbO 3 , LN) single crystals had been grown by Czochralski method. The Curie temperatures of various concentrations doped or [Li]/[Nb] ratio LN crystals measured by differential thermal analysis (DTA) were discussed to investigate their defect structures with Safaryan et al. new approach about LN lattice defect structure using Curie temperatures calculated. Infrared transmission spectra of various concentrations doped were used to compare the investigation above. The results show that the lithium vacancy model is the more probable to describe the lattice defect structure of the doped LN single crystal

  10. A review of the health impacts of barium from natural and anthropogenic exposure.

    Science.gov (United States)

    Kravchenko, Julia; Darrah, Thomas H; Miller, Richard K; Lyerly, H Kim; Vengosh, Avner

    2014-08-01

    There is an increasing public awareness of the relatively new and expanded industrial barium uses which are potential sources of human exposure (e.g., a shale gas development that causes an increased awareness of environmental exposures to barium). However, absorption of barium in exposed humans and a full spectrum of its health effects, especially among chronically exposed to moderate and low doses of barium populations, remain unclear. We suggest a systematic literature review (from 1875 to 2014) on environmental distribution of barium, its bioaccumulation, and potential and proven health impacts (in animal models and humans) to provide the information that can be used for optimization of future experimental and epidemiological studies and developing of mitigative and preventive strategies to minimize negative health effects in exposed populations. The potential health effects of barium exposure are largely based on animal studies, while epidemiological data for humans, specifically for chronic low-level exposures, are sparse. The reported health effects include cardiovascular and kidney diseases, metabolic, neurological, and mental disorders. Age, race, dietary patterns, behavioral risks (e.g., smoking), use of medications (those that interfere with absorbed barium in human organism), and specific physiological status (e.g., pregnancy) can modify barium effects on human health. Identifying, evaluating, and predicting the health effects of chronic low-level and moderate-level barium exposures in humans is challenging: Future research is needed to develop an understanding of barium bioaccumulation in order to mitigate its potential health impacts in various exposured populations. Further, while occupationally exposed at-risk populations exist, it is also important to identify potentially vulnerable subgroups among non-occupationally exposed populations (e.g., elderly, pregnant women, children) who are at higher risk of barium exposure from drinking water and food.

  11. The diagnosis of gastro-esophageal reflux disease cannot be made with barium esophagograms.

    Science.gov (United States)

    Saleh, C M G; Smout, A J P M; Bredenoord, A J

    2015-02-01

    For over 50 years, barium studies have been used to diagnose gastro-esophageal reflux disease (GERD), but the value of this test is controversial. Our study aimed to determine if barium esophagograms can be used to diagnose GERD. Barium esophagograms and pH-impedance measurement were performed in 20 subjects with reflux symptoms. pH-impedance measurements were used as gold standard for the diagnosis of GERD. Gastro-esophageal reflux measured with the barium study was defined as a positive outcome. 50% of patients presented gastro-esophageal reflux on the barium esophagogram. No significant differences were observed in acid exposure time between subjects with (median: 7.4%; interquartile range, IQR: 8.4%) or without reflux at barium esophagography (median: 5.95%; IQR: 13.05%; p > 0.05). Nor did we find differences in median proximal extent of reflux measured with impedance monitoring between patients with a positive (median: 6.7%; IQR: 1.95%) and negative barium study (median: 7.1%; IQR: 0.68%; p > 0.05). Patients with reflux on barium esophagogram did not have a positive symptom association probability more often than those who did not have reflux at barium esophagography. Lastly, there were no differences in numbers of acid, weakly acidic or total reflux episodes between those with positive or negative barium esophagogram (p > 0.05). No correlations were found between the maximum proximal extent of gastro-esophageal reflux during esophagography and pH-impedance parameters. Presence or absence of gastro-esophageal reflux during barium esophagography does not correlate with incidence or extent of reflux observed during 24-h pH-impedance monitoring and is not of value for the diagnosis of GERD. © 2014 John Wiley & Sons Ltd.

  12. Electromechanical properties of engineered lead free potassium sodium niobate based materials =

    Science.gov (United States)

    Rafiq, Muhammad Asif

    vacancies whose concentration increases with Mn doping. Single crystals of potassium sodium niobate (KNN) were grown by a modified high temperature flux method. A boron-modified flux was used to obtain the crystals at a relatively low temperature. XRD, EDS and ICP analysis proved the chemical and crystallographic quality of the crystals. The grown KNN crystals exhibit higher dielectric permittivity (29,100) at the tetragonal-to-cubic phase transition temperature, higher remnant polarization (19.4 ?C/cm2) and piezoelectric coefficient (160 pC/N) when compared with the standard KNN ceramics. KNN single crystals domain structure was characterized for the first time by piezoforce response microscopy. It could be observed that - oriented potassium sodium niobate (KNN) single crystals reveal a long range ordered domain pattern of parallel 180° domains with zig-zag 90° domains. From the comparison of KNN Single crystals to ceramics, It is argued that the presence in KNN single crystal (and absence in KNN ceramics) of such a long range order specific domain pattern that is its fingerprint accounts for the improved properties of single crystals. These results have broad implications for the expanded use of KNN materials, by establishing a relation between the domain patterns and the dielectric and ferroelectric response of single crystals and ceramics and by indicating ways of achieving maximised properties in KNN materials. (Abstract shortened by ProQuest.).

  13. Composition-Driven Phase Boundary and Piezoelectricity in Potassium-Sodium Niobate-Based Ceramics.

    Science.gov (United States)

    Zheng, Ting; Wu, Jiagang; Xiao, Dingquan; Zhu, Jianguo; Wang, Xiangjian; Lou, Xiaojie

    2015-09-16

    The piezoelectricity of (K,Na)NbO3 ceramics strongly depends on the phase boundary types as well as the doped compositions. Here, we systematically studied the relationships between the compositions and phase boundary types in (K,Na) (Nb,Sb)O3-Bi0.5Na0.5AO3 (KNNS-BNA, A=Hf, Zr, Ti, Sn) ceramics; then their piezoelectricity can be readily modified. Their phase boundary types are determined by the doped elements. A rhombohedral-tetragonal (R-T) phase boundary can be driven in the compositions range of 0.035≤BNH≤0.040 and 0.035≤BNZ≤0.045; an orthorhombic-tetragonal (O-T) phase boundary is formed in the composition range of 0.005≤BNT≤0.02; and a pure O phase can be only observed regardless of BNS content (≤0.01). In addition, the phase boundary types strongly affect their corresponding piezoelectricities. A larger d33 (∼440-450 pC/N) and a higher d33* (∼742-834 pm/V) can be attained in KNNS-BNA (A=Zr and Hf) ceramics due to the involvement of R-T phase boundary, and unfortunately KNNS-BNA (A=Sn and Ti) ceramics possess a relatively poor piezoelectricity (d33≤200 and d33*piezoelectricity and phase boundary types were also discussed. We believe that comprehensive research can design more excellent ceramic systems concerning potassium-sodium niobate.

  14. Domain wall kinetics of lithium niobate single crystals near the hexagonal corner

    Energy Technology Data Exchange (ETDEWEB)

    Choi, Ju Won [Department of Physics and Photon Science, Gwangju Institute of Science and Technology (GIST), 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); Ko, Do-Kyeong [Department of Physics and Photon Science, Gwangju Institute of Science and Technology (GIST), 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); Advanced Photonics Research Institute, GIST, 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); Yu, Nan Ei, E-mail: neyu@gist.ac.kr, E-mail: jhro@pnu.edu [Advanced Photonics Research Institute, GIST, 1 Oryong-dong, Buk-gu, Gwangju 500-712 (Korea, Republic of); Kitamura, Kenji [National Institute for Materials Science, Tsukuba, Ibaraki 305-0044 (Japan); Ro, Jung Hoon, E-mail: neyu@gist.ac.kr, E-mail: jhro@pnu.edu [Department of Biomedical Engineering, School of Medicine, Pusan National University, Busan 602-739 (Korea, Republic of)

    2015-03-09

    A mesospheric approach based on a simple microscopic 2D Ising model in a hexagonal lattice plane is proposed to explain macroscopic “asymmetric in-out domain wall motion” observation in the (0001) plane of MgO-doped stoichiometric lithium niobate. Under application of an electric field that was higher than the conventional coercive field (E{sub c}) to the ferroelectric crystal, a natural hexagonal domain was obtained with walls that were parallel to the Y-axis of the crystal. When a fraction of the coercive field of around 0.1E{sub c} is applied in the reverse direction, this hexagonal domain is shrunk (moved inward) from the corner site into a shape with a corner angle of around 150° and 15° wall slopes to the Y-axis. A flipped electric field of 0.15E{sub c} is then applied to recover the natural hexagonal shape, and the 150° corner shape changes into a flat wall with 30° slope (moved outward). The differences in corner domain shapes between inward and outward domain motion were analyzed theoretically in terms of corner and wall site energies, which are described using the domain corner angle and wall slope with respect to the crystal Y-axis, respectively. In the inward domain wall motion case, the energy levels of the evolving 150° domain corner and 15° slope walls are most competitive, and could co-exist. In the outward case, the energy levels of corners with angles >180° are highly stable when compared with the possible domain walls; only a flat wall with 30° slope to the Y-axis is possible during outward motion.

  15. Photonic guiding structures in lithium niobate crystals produced by energetic ion beams

    Science.gov (United States)

    Chen, Feng

    2009-10-01

    A range of ion beam techniques have been used to fabricate a variety of photonic guiding structures in the well-known lithium niobate (LiNbO3 or LN) crystals that are of great importance in integrated photonics/optics. This paper reviews the up-to-date research progress of ion-beam-processed LiNbO3 photonic structures and reports on their fabrication, characterization, and applications. Ion beams are being used with this material in a wide range of techniques, as exemplified by the following examples. Ion beam milling/etching can remove the selected surface regions of LiNbO3 crystals via the sputtering effects. Ion implantation and swift ion irradiation can form optical waveguide structures by modifying the surface refractive indices of the LiNbO3 wafers. Crystal ion slicing has been used to obtain bulk-quality LiNbO3 single-crystalline thin films or membranes by exfoliating the implanted layer from the original substrate. Focused ion beams can either generate small structures of micron or submicron dimensions, to realize photonic bandgap crystals in LiNbO3, or directly write surface waveguides or other guiding devices in the crystal. Ion beam-enhanced etching has been extensively applied for micro- or nanostructuring of LiNbO3 surfaces. Methods developed to fabricate a range of photonic guiding structures in LiNbO3 are introduced. Modifications of LiNbO3 through the use of various energetic ion beams, including changes in refractive index and properties related to the photonic guiding structures as well as to the materials (i.e., electro-optic, nonlinear optic, luminescent, and photorefractive features), are overviewed in detail. The application of these LiNbO3 photonic guiding structures in both micro- and nanophotonics are briefly summarized.

  16. Interface modulated currents in periodically proton exchanged Mg doped lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Neumayer, Sabine M.; Rodriguez, Brian J., E-mail: brian.rodriguez@ucd.ie, E-mail: gallo@kth.se [School of Physics, University College Dublin, Belfield, Dublin 4 (Ireland); Conway Institute of Biomolecular and Biomedical Research, University College Dublin, Belfield, Dublin 4 (Ireland); Manzo, Michele; Gallo, Katia, E-mail: brian.rodriguez@ucd.ie, E-mail: gallo@kth.se [Department of Applied Physics, KTH-Royal Institute of Technology, Roslagstullbacken 21, 10691 Stockholm (Sweden); Kholkin, Andrei L. [Department of Physics and CICECO-Aveiro Institute of Materials, 3810-193 Aveiro, Portugal and Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation)

    2016-03-21

    Conductivity in Mg doped lithium niobate (Mg:LN) plays a key role in the reduction of photorefraction and is therefore widely exploited in optical devices. However, charge transport through Mg:LN and across interfaces such as electrodes also yields potential electronic applications in devices with switchable conductivity states. Furthermore, the introduction of proton exchanged (PE) phases in Mg:LN enhances ionic conductivity, thus providing tailorability of conduction mechanisms and functionality dependent on sample composition. To facilitate the construction and design of such multifunctional electronic devices based on periodically PE Mg:LN or similar ferroelectric semiconductors, fundamental understanding of charge transport in these materials, as well as the impact of internal and external interfaces, is essential. In order to gain insight into polarization and interface dependent conductivity due to band bending, UV illumination, and chemical reactivity, wedge shaped samples consisting of polar oriented Mg:LN and PE phases were investigated using conductive atomic force microscopy. In Mg:LN, three conductivity states (on/off/transient) were observed under UV illumination, controllable by the polarity of the sample and the externally applied electric field. Measurements of currents originating from electrochemical reactions at the metal electrode–PE phase interfaces demonstrate a memresistive and rectifying capability of the PE phase. Furthermore, internal interfaces such as domain walls and Mg:LN–PE phase boundaries were found to play a major role in the accumulation of charge carriers due to polarization gradients, which can lead to increased currents. The insight gained from these findings yield the potential for multifunctional applications such as switchable UV sensitive micro- and nanoelectronic devices and bistable memristors.

  17. Effect of excess bismuth on the dielectric and piezoelectric properties of strontium bismuth niobate ceramics

    International Nuclear Information System (INIS)

    Verma, Maya; Tanwar, Amit; Sreenivas, K.

    2013-01-01

    Excess Bismuth Strontium Bismuth Niobate (Sr 2 Bi 2 Nb 2 O 9 + x wt% Bi 2 O 3 ) ceramics were prepared using conventional solid state reaction method by varying x in the range (x=0%wt - 20%wt). X-ray diffraction studies reveal no significant shift in the peak positions as the Bi content increases from 0.0 to 5%wt. However, at a higher content of Bi beyond x = 5wt% secondary phases relating to Bi 2 O 3 are identified. The c-axis orientation is found to be minimum for SBN ceramic prepared with 5% excess bismuth whereas with further increase in excess Bi 2 O 3 addition during processing, SBN ceramics show a much stronger c-axis orientation. Room temperature dielectric constant measured at 100 KHz is found to increase from 117 to 130 with increase in Bi content from x = 0 to 10wt% suggesting Bi addition has make up for the bismuth losses at higher sintering temperature (1200℃), however with further increase in Bi content (x > 10wt%), the dielectric constant decreases, and could be due to the increased probability of segregation of Bi on the grains of SBN ceramics. The improvement in ferroelectric properties were obtained when the bismuth excess is increased from 0% to 5%. It may be observed that on increasing the excess bismuth to 5%, the transition temperature increases from 424 to 450℃, while further increasing to 10%, transition becomes slightly diffused and phase transition temperature gets decreased to 398℃, which may be due to the formation of secondary phase. 5% excess Bi is found to enhance the dielectric and ferroelectricity properties, and any further increase of Bi in excess (>10%) during processing is found to degrade the electrical and functional properties of SBN. (author)

  18. Ion-beam enhanced etching for the 3D structuration of lithium niobate

    International Nuclear Information System (INIS)

    Gischkat, Thomas

    2010-01-01

    The present thesis deals with the usage of the ion-beam enhanced etching (IBEE) for the 3D structuration of lithium niobate (LiNbO 3 ).Hereby the approach of the enhancement of the wet-chemical etching rate due to the irradiation with energetic ions is pursued. This method is very success promising for the realization of micro- and nanostructures with perpendicular structural walls as well as small roughnesses. The aim of this thesis consisted therein to form the foundations for the realization of three-dimensional micro- and nanostructures (for instance: Layer systems and photonic crystals) in LiNbO 3 with high optical quality and to demonstrate on selected examples. Conditions for the success of the IBEE structuration technique is first of all the understanding of the defect formation under ion irradiation as well as the radiation-induced structure changes in the crystal and the change of the chemical resistance connected with this. For this the defect formation was studied in dependence on th ion mass, the ion energy, and the irradiation temperature. Thermally induced influences and effects on the radiation damage, as they can occur in intermediate steps in the complex processing, must be known and were studied by means of subsequent temperature treatment. The results from the defect studies were subsequently applied for the fabrication of micro- and nanostructures in LiNbO 3 . Shown is the realization of lateral structure with nearly perpendicular structure walls as well as the realization of thin membranes and slits. The subsequent combination of lateral structuration with the fabrication of thin membranes and slits allowed the three-dimensional structuration of LiNbO 3 . This is exemplarily shown for a microresonator and for a 2D photonic crystal with below lying air slit. [de

  19. Interface and thickness dependent domain switching and stability in Mg doped lithium niobate

    Energy Technology Data Exchange (ETDEWEB)

    Neumayer, Sabine M.; Rodriguez, Brian J., E-mail: gallo@kth.se, E-mail: brian.rodriguez@ucd.ie [School of Physics, University College Dublin, Belfield, Dublin 4 (Ireland); Conway Institute of Biomolecular and Biomedical Research, University College Dublin, Belfield, Dublin 4 (Ireland); Ivanov, Ilia N. [Center for Nanophase Materials Sciences, Oak Ridge National Laboratory, Oak Ridge, Tennessee 37831 (United States); Manzo, Michele; Gallo, Katia, E-mail: gallo@kth.se, E-mail: brian.rodriguez@ucd.ie [Department of Applied Physics, KTH-Royal Institute of Technology, Roslagstullbacken 21, 10691 Stockholm (Sweden); Kholkin, Andrei L. [Department of Physics and CICECO-Aveiro Institute of Materials, 3810-193 Aveiro (Portugal); Institute of Natural Sciences, Ural Federal University, 620000 Ekaterinburg (Russian Federation)

    2015-12-14

    Controlling ferroelectric switching in Mg doped lithium niobate (Mg:LN) is of fundamental importance for optical device and domain wall electronics applications that require precise domain patterns. Stable ferroelectric switching has been previously observed in undoped LN layers above proton exchanged (PE) phases that exhibit reduced polarization, whereas PE layers have been found to inhibit lateral domain growth. Here, Mg doping, which is known to significantly alter ferroelectric switching properties including coercive field and switching currents, is shown to inhibit domain nucleation and stability in Mg:LN above buried PE phases that allow for precise ferroelectric patterning via domain growth control. Furthermore, piezoresponse force microscopy (PFM) and switching spectroscopy PFM reveal that the voltage at which polarization switches from the “up” to the “down” state increases with increasing thickness in pure Mg:LN, whereas the voltage required for stable back switching to the original “up” state does not exhibit this thickness dependence. This behavior is consistent with the presence of an internal frozen defect field. The inhibition of domain nucleation above PE interfaces, observed in this study, is a phenomenon that occurs in Mg:LN but not in undoped samples and is mainly ascribed to a remaining frozen polarization in the PE phase that opposes polarization reversal. This reduced frozen depolarization field in the PE phase also influences the depolarization field of the Mg:LN layer above due to the presence of uncompensated polarization charge at the PE-Mg:LN boundary. These alterations in internal electric fields within the sample cause long-range lattice distortions in Mg:LN via electromechanical coupling, which were corroborated with complimentary Raman measurements.

  20. Anion and cation diffusion in barium titanate and strontium titanate

    International Nuclear Information System (INIS)

    Kessel, Markus Franz

    2012-01-01

    Perovskite oxides show various interesting properties providing several technical applications. In many cases the defect chemistry is the key to understand and influence the material's properties. In this work the defect chemistry of barium titanate and strontium titanate is analysed by anion and cation diffusion experiments and subsequent time-of-flight secondary ion mass spectrometry (ToF-SIMS). The reoxidation equation for barium titanate used in multi-layer ceramic capacitors (MLCCs) is found out by a combination of different isotope exchange experiments and the analysis of the resulting tracer diffusion profiles. It is shown that the incorporation of oxygen from water vapour is faster by orders of magnitude than from molecular oxygen. Chemical analysis shows the samples contain various dopants leading to a complex defect chemistry. Dysprosium is the most important dopant, acting partially as a donor and partially as an acceptor in this effectively acceptor-doped material. TEM and EELS analysis show the inhomogeneous distribution of Dy in a core-shell microstructure. The oxygen partial pressure and temperature dependence of the oxygen tracer diffusion coefficients is analysed and explained by the complex defect chemistry of Dy-doped barium titanate. Additional fast diffusion profiles are attributed to fast diffusion along grain boundaries. In addition to the barium titanate ceramics from an important technical application, oxygen diffusion in cubic, nominally undoped BaTiO 3 single crystals has been studied by means of 18 O 2 / 16 O 2 isotope exchange annealing and subsequent determination of the isotope profiles in the solid by ToF-SIMS. It is shown that a correct description of the diffusion profiles requires the analysis of the diffusion through the surface space-charge into the material's bulk. Surface exchange coefficients, space-charge potentials and bulk diffusion coefficients are analysed as a function of oxygen partial pressure and temperature. The

  1. Thermal evolution of exchange interactions in lightly doped barium hexaferrites

    Energy Technology Data Exchange (ETDEWEB)

    Trukhanov, S.V., E-mail: truhanov@ifttp.bas-net.by [National University of Science and Technology MISiS, Leninsky Prospekt, 4, 119049 Moscow (Russian Federation); SSPA “Scientific and practical materials research centre of NAS of Belarus”, P. Brovki Str., 19, 220072 Minsk, Belorussia (Belarus); Trukhanov, A.V. [National University of Science and Technology MISiS, Leninsky Prospekt, 4, 119049 Moscow (Russian Federation); SSPA “Scientific and practical materials research centre of NAS of Belarus”, P. Brovki Str., 19, 220072 Minsk, Belorussia (Belarus); Kostishyn, V.G.; Panina, L.V. [National University of Science and Technology MISiS, Leninsky Prospekt, 4, 119049 Moscow (Russian Federation); Turchenko, V.A. [Joint Institute for Nuclear Research, Joliot-Curie Str., 141980 Dubna (Russian Federation); Donetsk Institute of Physics and Technology named after A.A. Galkin of the NAS of Ukraine, 72 R.Luxemburg Str., 83114 Donetsk (Ukraine); Kazakevich, I.S. [SSPA “Scientific and practical materials research centre of NAS of Belarus”, P. Brovki Str., 19, 220072 Minsk, Belorussia (Belarus); Trukhanov, An.V. [National University of Science and Technology MISiS, Leninsky Prospekt, 4, 119049 Moscow (Russian Federation); SSPA “Scientific and practical materials research centre of NAS of Belarus”, P. Brovki Str., 19, 220072 Minsk, Belorussia (Belarus); Trukhanova, E.L.; Natarov, V.O. [SSPA “Scientific and practical materials research centre of NAS of Belarus”, P. Brovki Str., 19, 220072 Minsk, Belorussia (Belarus); Balagurov, A.M. [Joint Institute for Nuclear Research, Joliot-Curie Str., 141980 Dubna (Russian Federation)

    2017-03-15

    The lightly doped BaFe{sub 12−x}D{sub x}O{sub 19} (D=Al{sup 3+}, In{sup 3+}; x=0.1 and 0.3) polycrystalline hexaferrite samples have been investigated by powder neutron diffractometry as well as by vibration sample magnetometry in a wide temperature range from 4 K up to 740 K and in magnetic field up to 14 T to establish the nature of Fe{sup 3+}(Al{sup 3+}, In{sup 3+}) – O{sup 2-} - Fe{sup 3+}(Al{sup 3+}, In{sup 3+}) indirect exchange interactions. The crystal structure features such as the ionic coordinates and lattice parameters have been defined and Rietveld refined. The Invar effect has been observed in low temperature range below 150 K. It was explained by the thermal oscillation anharmonicity of ions. It is established that the ferrimagnet-paramagnet phase transition is a standard second-order one. From the macroscopic magnetization measurement the Curie temperature and ordered magnetic moment per nominal iron ion are obtained. From the microscopic diffraction measurement the magnetic moments at all the nonequivalent ionic positions and total magnetic moment per iron ion have been obtained at different temperatures down to 4 K. The light diamagnetic doping mechanism and magnetic structure model are proposed. The effect of light diamagnetic doping on nature of Fe{sup 3+}(Al{sup 3+}, In{sup 3+}) – O{sup 2-} - Fe{sup 3+}(Al{sup 3+}, In{sup 3+}) indirect exchange interactions with temperature increase is discussed. - Highlights: • Crystal structure for lightly doped barium hexaferrites was investigated. • Atomic coordinates and lattice parameters were Rietveld refined. • Magnetic properties for lightly doped barium hexaferrites was investigated. • Magnetic structure for lightly doped barium hexaferrites was investigated. • Magnetic moments at different position and total moment per iron ion were defined.

  2. Multiple electrical phase transitions in Al substituted barium hexaferrite

    Science.gov (United States)

    Kumar, Sunil; Supriya, Sweety; Kar, Manoranjan

    2017-12-01

    Barium hexaferrite is known to be a very good ferromagnetic material. However, it shows very good dielectric properties, i.e., the dielectric constant is comparable to that of the ferroelectric material. However, its crystal symmetry does not allow it to be a ferroelectric material. Hence, the electrical properties have revived the considerable research interest on these materials, not only for academic interest, but also for technological applications. There are a few reports on temperature dependent dielectric behavior of these materials. However, the exact cause of dielectric as well as electrical conductivity is yet to be established. Hence, Al (very good conducting material) substituted barium hexaferrite (BaFe12-xAlxO19, x = 0.0-4.0) has been prepared by following the modified sol-gel method to understand the ac and DC electrical properties of these materials. The crystal structure and parameters have been studied by employing the XRD and FTIR techniques. There are two transition temperatures, which have been observed in the temperature dependent ac dielectric and DC resistivity measurement. The response of dielectric behaviors to temperature is similar to that of the ferroelectric material; however, the dielectric polarization is due to the polaron hopping, which is evident from the DC resistivity analysis. Hence, the present observations lead to understand the electrical properties of barium hexaferrite. The frequency dependent dielectric dispersion can be understood by the modified Debye model. More interestingly, the dielectric constant decreases and DC resistivity increases with the increase in the Al concentration, which has the correlation between bond length modifications in the crystal due to substitution.

  3. lead glass brick

    CERN Multimedia

    When you look through the glass at a picture behind, the picture appears raised up because light is slowed down in the dense glass. It is this density (4.06 gcm-3) that makes lead glass attractive to physicists. The refractive index of the glass is 1.708 at 400nm (violet light), meaning that light travels in the glass at about 58% its normal speed. At CERN, the OPAL detector uses some 12000 blocks of glass like this to measure particle energies.

  4. Influence of fuel ratios on auto combustion synthesis of barium ferrite ...

    Indian Academy of Sciences (India)

    Unknown

    Influence of fuel ratios on auto combustion synthesis of barium ferrite nano particles. D BAHADUR*, S RAJAKUMAR and ANKIT KUMAR. Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology,. Mumbai 400 076 e-mail: dhirenb@iitb.ac.in. Abstract. Single-domain barium ferrite nano ...

  5. New efficient catalyst for ammonia synthesis: barium-promoted cobalt on carbon

    DEFF Research Database (Denmark)

    Hagen, Stefan; Barfod, Rasmus; Fehrmann, Rasmus

    2002-01-01

    Barium-promoted cobalt catalysts supported on carbon exhibit higher ammonia activities at synthesis temperatures than the commercial, multipromoted iron catalyst and also a lower ammonia......Barium-promoted cobalt catalysts supported on carbon exhibit higher ammonia activities at synthesis temperatures than the commercial, multipromoted iron catalyst and also a lower ammonia...

  6. Investigation on the effects of milling atmosphere on synthesis of barium ferrite/magnetite nanocomposite

    NARCIS (Netherlands)

    Molaei, M.J.; Ataie, A.; Raygan, S.; Picken, S.J.

    2011-01-01

    In this research, barium ferrite /magnetite nanocomposites synthesized via a mechano-chemical route. Graphite was used in order to reduce hematite content of barium ferrite to magnetite to produce a magnetic nanocomposite. The effects of processing conditions on the powder characteristics were

  7. Acute respiratory failure caused by aspiration of high density barium: A case report

    International Nuclear Information System (INIS)

    Park, Ki Soon; Jung, Eun A; Yang, Ik; Lee, Yul; Chung, Soo Young

    1994-01-01

    Accidental aspiration of barium contrast medium during the upper gastrointestinal study can occur in patients with swallowing disorder, especially in the elderly patients. We experienced a case of respiratory failure followed by death within a few hours in 85 year-old patient after barium aspiration

  8. Complete sulphate removal from neutralised acidic mine drainage with barium carbonate

    CSIR Research Space (South Africa)

    Swanepoel, H

    2012-03-01

    Full Text Available -barium-calcium) Desalination process which uses barium salts to further reduce the sulphate concentration to acceptable levels with the added advantage that sulphate removal can be controlled due to the low solubility of BaSO4. This paper reports on the results...

  9. Barium strontium titanate powders prepared by spray pyrolysis

    International Nuclear Information System (INIS)

    Brankovic, G.; Brankovic, Z.; Goes, M.S.; Paiva-Santos, C.O.; Cilense, M.; Varela, J.A.; Longo, E.

    2005-01-01

    Ultasonic spray pyrolysis (SP) has been investigated for the production of the barium strontium titanate (BST) powders from the polymeric precursors. The processing parameters, such as flux of aerosol and temperature profile inside the furnace, were optimized to obtain single phase BST. The powders were characterized by the methods of X-ray diffraction analysis, SEM, EDS and TEM. The obtained powders were submicronic, consisting of spherical, polycrystalline particles, with internal nanocrystalline structure. Crystallite size of 10 nm, calculated using Rietveld refinement, is in a good agreement with results of HRTEM

  10. Radium and barium in the Amazon River system

    International Nuclear Information System (INIS)

    Moore, W.S.; Edmond, J.M.

    1984-01-01

    Data for 226 Ra and 228 Ra in the Amazon River system show that the activity of each radium isotope is strongly correlated with barium concentrations. Two trends are apparent, one for rivers which drain shield areas and another for all other rivers. These data suggest that there has been extensive fractionation of U, Th, and Ba during weathering in the Amazon basin. The 226 Ra data fit a flux model for the major ions indicating that 226 Ra behaves conservatively along the main channel of the Amazon River

  11. Regularities of radium coprecipitation with barium sulfate from salt solutions

    International Nuclear Information System (INIS)

    Kudryavskij, Yu.P.; Rakhimova, O.V.

    2007-01-01

    Coprecipitation of radium with barium sulfate from highly concentrated NaCl solutions is studied, including the effects of the initial solution composition, alkaline reagent (CaO, NaOH), supporting electrolyte (NaCl) concentration, and pH. The process is promoted by high NaCl concentration in the initial solution, which is due to structural transformation and change in the sorption activity of the BaSO 4 precipitate in salt solutions. The results obtained were applied to recovery of radium from process solutions during the development and introduction of improved procedure for disinfection and decontamination of waste yielded by chlorination of loparite concentrates [ru

  12. Recharging processes, radiation induced strain and changes of OH - bands under H + ion implantation in Ti doped lithium niobate

    Science.gov (United States)

    Kumar, P.; Moorthy Babu, S.; Bhaumik, I.; Ganesamoorthy, S.; Karnal, A. K.; Kumar, Praveen; Rodrigues, G. O.; Sulania, I.; Kanjilal, D.; Pandey, A. K.; Raman, R.

    2010-01-01

    A systematic analysis of variations in structural and optical characteristics of Z-cut plates of titanium doped congruent lithium niobate single crystals implanted with 120 keV proton beam at various fluences of 10 15, 10 16 and 10 17 protons/cm 2 is presented. Through, high resolution X-ray diffraction, atomic force microscopy, Fourier transform infrared and UV-visible-NIR analysis of congruent lithium niobate, the correlation of properties before and after implantation are discussed. HRXRD (0 0 6) reflection by Triple Crystal Mode shows that both tensile and compressive strain peak are produced by the high fluence implantation. A distinct tensile peak was observed from implanted region for a fluence of 10 16 protons/cm 2. AFM micrographs indicate mountain ridges, bumps and protrusions on target surface on implantation. UV-visible-NIR spectra reveal an increase in charge transfer between Ti 3+/Ti 4+ and ligand oxygen for implantation with 10 15 protons/cm 2, while spectra for higher fluence implanted samples show complex absorption band in the region from 380-1100 nm. Variations of OH - stretching vibration mode were observed for cLN Pure, cLNT2% virgin, and implanted samples with FTIR spectra. The concentration of OH - ion before and after implantation was calculated from integral absorption intensity. The effect of 120 keV proton implantation induced structural, surface and optical studies were correlated.

  13. Influence of Fe{sup 3+} substitution on the dielectric and ferroelectric characteristics of Lead Indium Niobate

    Energy Technology Data Exchange (ETDEWEB)

    Divya, A.S.; Kumar, V., E-mail: vkumar10@yahoo.com

    2015-07-15

    Highlights: • Prepared phase-pure Fe{sup 3+}-substituted Lead Indium Niobate, Pb[(In{sub 0.50−x}Fe{sub x})Nb{sub 0.50}]O{sub 3} by sol–gel method. • Spontaneous Relaxor (R) → Ferroelectric (FE) transition observed for the composition with x = 0.20. • Local structural rearrangement responsible for R → FE transition has been confirmed by Raman spectroscopy. - Abstract: Lead Indium Niobate, Pb(In{sub 0.50}Nb{sub 0.50})O{sub 3} (PIN) is a complex perovskite that exhibits Relaxor (R) characteristics. In this study, we report the synthesis of phase-pure compositions in the system Pb[(In{sub 0.50−x}Fe{sub x})Nb{sub 0.50}]O{sub 3} by sol–gel method and discuss the influence of isovalent substitution of Indium by Iron on the dielectric and ferroelectric characteristics. Spontaneous transition to the Ferroelectric (FE) phase has been observed for the composition having x = 0.20. Local structural rearrangements responsible for R → FE transition have also been studied by Raman spectroscopy and are discussed in detail.

  14. Evidence against barium in the mushroom Trogia venenata as a cause of sudden unexpected deaths in Yunnan, China.

    Science.gov (United States)

    Zhang, Ying; Li, Yanchun; Wu, Gang; Feng, Bang; Yoell, Shanze; Yu, Zefen; Zhang, Keqin; Xu, Jianping

    2012-12-01

    This study examined barium concentrations in the mushroom Trogia venenata, the leading culprit for sudden unexpected deaths in Yunnan, southwest China. We found that barium concentrations in T. venenata from Yunnan were low and comparable to other foods, inconsistent with barium concentrations in this mushroom as a significant contributor to these deaths.

  15. Prospective comparison of double contrast barium enema plus flexible sigmoidoscopy v colonoscopy in rectal bleeding: barium enema v colonoscopy in rectal bleeding.

    OpenAIRE

    Irvine, E J; O'Connor, J; Frost, R A; Shorvon, P; Somers, S; Stevenson, G W; Hunt, R H

    1988-01-01

    Rectal bleeding often heralds serious colonic disease. The literature suggests that colonoscopy is superior to barium enema plus sigmoidoscopy, although no good comparative studies exist. Seventy one patients with overt rectal bleeding had prospectively flexible sigmoidoscopy, double contrast barium enema and colonoscopy completed independently. Against the gold standard, the sensitivity and specificity of colonoscopy were 0.69 and 0.78 respectively for a spectrum of colonic lesions, while fo...

  16. Evaluation of gastrointestinal tract transit times using barium-impregnated polyethylene spheres and barium sulfate suspension in a domestic pigeon (Columba livia) model.

    Science.gov (United States)

    Bloch, Rebecca A; Cronin, Kimberly; Hoover, John P; Pechman, Robert D; Payton, Mark E

    2010-03-01

    Barium impregnated polyethylene spheres (BIPS) are used in small animal medicine as an alternative to barium sulfate for radiographic studies of the gastrointestinal tract. To determine the usefulness of BIPS as an alternative to barium suspension in measuring gastrointestinal (GI) transit time for avian species, ventrodorsal radiographs were used to follow the passage of BIPS and 30% barium sulfate suspension through the GI tracts of domestic pigeons (Columba livia). Gastrointestinal transit times of thirty 1.5-mm BIPS administered in moistened gelatin capsules and 30% barium sulfate suspension gavaged into the crop were compared in 6 pigeons. Although the barium suspension passed out of the GI tract of all pigeons within 24 hours, the 1.5-mm BIPS remained in the ventriculus for 368.0 +/- 176.8 hours and did not clear the GI tract for 424.0 +/- 204.6 hours. Although the times for passage of BIPS and 30% barium sulfate suspension from the crop into the ventriculus were not significantly different (P = .14), the times for passage of BIPS from the ventriculus into the large intestine-cloaca and for clearance from the GI tract of the pigeons were significantly longer (P barium sulfate suspension. From the results of this study, we conclude that BIPS are not useful for radiographically evaluating GI transit times in pigeons and are unlikely to be useful in other avian species that have a muscular ventriculus. BIPS may or may not be useful for evaluating GI transit times in species that lack a muscular ventriculus.

  17. Atomization of magnesium, strontium, barium and lead nitrates on surface of graphite atomizers

    International Nuclear Information System (INIS)

    Nagdaev, V.K.; Pupyshev, A.A.

    1982-01-01

    Modelling of the processes on graphite surface using differential-thermal analysis and graphite core with identification of decomposition products of magnesium, strontium, barium and lead nitrates by X-ray analysis has shown that carbon promotes the formation of strontium, barium and lead carbonates. The obtained temperatures of strontium and barium carbonate decomposition to oxides agree satisfactorily with calculation ones. Magnesium nitrate does not react with carbon. Formation of strontium and barium carbonates results in considerable slowing down of the process of gaseous oxide dissociation. Lead carbonate is unstable and rapidly decomposes to oxide with subsequent reduction to free metal. Formation of magnesium, strontium and barium free atoms is connected with appearance of gaseous oxides in analytical zone. Oxide and free metal lead are present on graphite surface simultaneously

  18. Barium sulfate suspension as a negative oral contrast agent for MR imaging

    International Nuclear Information System (INIS)

    Li, K.C.P.; Tart, R.P.; Fitzsimmons, J.R.; Storm, B.; Mao, J.

    1989-01-01

    Proton spectroscopy with linewidth measurements and MR imaging were performed on various commercially available barium sulfate suspensions as well as inorganic sulfates and barium salts. Approximately 500 mL of 20%, 40%, 60%, and 70% wt/wt single-contrast oral barium sulfate suspensions were administered to four normal volunteers, and MR imaging was performed with both a 1.5-T and a 0.15-T MR imager. As much as 80% of the small bowel and the entire colon were well visualized with the 60% or 70% wt/wt single-contrast barium sulfate suspensions. The authors conclude that barium sulfate suspensions are useful as oral MR contrast agents

  19. Formation of barium strontium titanate powder by solid state reaction using different calcination temperatures

    International Nuclear Information System (INIS)

    Teoh Wah Tzu; Ahmad Fauzi Mohd Noor; Zainal Arifin Ahmad

    2002-01-01

    The unique electrical properties of large permittivity in Barium Strontium Titanate have been widely used to make capacitors; it can be produced by solid state reaction. In this study, the mixture of Barium Carbonate, Strontium Carbonate and Titanium Dioxide was calcined at 500 degree C, 1000 degree C, 1100 degree C , 1150 degree C, 1200 degree C, 1250 degree C and 1300 degree C. The results of the phases change in each stage were investigated via X ay Diffraction. The results show that the formation of Barium Strontium Titanate started at 1100 degree C with the presence of other phases. The mixture is fully reacted to form Barium Strontium Titanate at 1150 degree C. Only Barium Strontium Titanate was formed as the calcination temperature was set higher. (Author)

  20. Characterization of barium titanate powder doped with sodium and potassium ions by using Rietveld refining

    International Nuclear Information System (INIS)

    Andrade, M.C.; Assis, J.T.; Pereira, F.R.

    2009-01-01

    A solid-reaction synthesis of doped barium titanate was done by employing barium carbonates, sodium, potassium and titanium oxides with classic procedures. Rietveld refining of X ray diffraction data of perovskite samples with tetragonal symmetry was applying and show good agreement. Besides, the treatment performed from 600 deg C produces nanocrystals of barium titanate with average size of 33 nm. The presence of endothermic peaks related to BaTiO 3 formation at relatively low temperatures was determined by thermal analysis. A pseudo-Voigt Thompson-Cox-Hastings function was used to fit the standard samples of barium titanate. The Rietveld method has showed be efficient to detect the influences of temperature and doping on barium titanate microstructures. (author)