WorldWideScience

Sample records for arrays zno thin

  1. Preparation of Aligned ZnO Nanorod Arrays on Sn-Doped ZnO Thin Films by Sonicated Sol-Gel Immersion Fabricated for Dye-Sensitized Solar Cell

    Directory of Open Access Journals (Sweden)

    I. Saurdi

    2014-01-01

    Full Text Available Aligned ZnO Nanorod arrays are deposited on the Sn-doped ZnO thin film via sonicated sol-gel immersion method. The structural, optical, and electrical properties of the Sn-doped ZnO thin films were investigated. Results show that the Sn-doped ZnO thin films with small grain size (~20 nm, high average transmittance (96% in visible region, and good resistivity 7.7 × 102 Ω·cm are obtained for 2 at.% Sn doping concentration. The aligned ZnO nanorod arrays with large surface area were also obtained for 2 at.% Sn-doped ZnO thin film. They were grown on sol-gel derived Sn-doped ZnO thin film, which acts as a seed layer, via sonicated sol-gel immersion method. The grown aligned ZnO nanorod arrays show high transmittance at visible region. The fabricated dye-sensitised solar cell based on the 2.0 at.% Sn-doped ZnO thin film with aligned ZnO nanorod arrays exhibits improved current density, open-circuit voltage, fill factor, and conversion efficiency compared with the undoped ZnO and 1 at.% Sn-doped ZnO thin films.

  2. Plasmonic enhancement of UV emission from ZnO thin films induced by Al nano-concave arrays

    International Nuclear Information System (INIS)

    Norek, Małgorzata; Łuka, Grzegorz; Włodarski, Maksymilian

    2016-01-01

    Highlights: • Al nano-concave arrays with different interpore distance (D c ) were prepared. • PL of ZnO thin films deposited directly on the Al nano-concaves were studied. • The effect of 10 nm Al 2 O 3 spacer on PL emission from ZnO thin films was analyzed. • Plasmonic enhancement of the PL emission was dependent on the D c and the spacer. • The highest 9-fold enhancement was obtained for the Al/ZnO sample with D c ∼333 nm. - Abstract: Surface plasmons (SPs) supported by Al nano-concave arrays with increasing interpore distance (D c ) were used to enhance the ultraviolet light emission from ZnO thin films. Two sets of samples were prepared: in the first set the thin ZnO films were deposited directly on Al nanoconcaves (the Al/ZnO samples) and in the second set a 10 nm − Al 2 O 3 spacer was placed between the textured Al and the ZnO films (the Al/Al 2 O 3 -ALD/ZnO samples). In the Al/ZnO samples the enhancement was limited by a nonradiative energy dissipation due to the Ohmic loss in the Al metal. However, for the ZnO layer deposited directly on Al nanopits synthesized at 150 V (D c = 333 ± 18 nm), the largest 9-fold enhancement was obtained by achieving the best energy fit between the near band-edge (NBE) emission from ZnO and the λ (0,1) SPP resonance mode. In the Al/Al 2 O 3 -ALD/ZnO samples the amplification of the UV emission was smaller than in the Al/ZnO samples due to a big energy mismatch between the NBE emission and the λ (0,1) plasmonic mode. The results obtained in this work indicate that better tuning of the NBE − λ (0,1) SPP resonance mode coupling is possible through a proper modification of geometrical parameters in the Al/Al 2 O 3 -ALD/ZnO system such as Al nano-concave spacing and the thickness of the corresponding layer. This approach will reduce the negative influence of the non-radiative plasmonic modes and most likely will lead to further enhancement of the SP-modulated UV emission from ZnO thin films.

  3. Plasmonic enhancement of UV emission from ZnO thin films induced by Al nano-concave arrays

    Energy Technology Data Exchange (ETDEWEB)

    Norek, Małgorzata, E-mail: mnorek@wat.edu.pl [Department of Advanced Materials and Technologies, Faculty of Advanced Technologies and Chemistry, Military University of Technology, Kaliskiego 2, 00-908 Warsaw (Poland); Łuka, Grzegorz [Institute of Physics, Polish Academy of Sciences, al. Lotników 32/46, 02-668 Warsaw (Poland); Włodarski, Maksymilian [Institute of Optoelectronics, Military University of Technology, Str. Kaliskiego 2, 00-908 Warszawa (Poland)

    2016-10-30

    Highlights: • Al nano-concave arrays with different interpore distance (D{sub c}) were prepared. • PL of ZnO thin films deposited directly on the Al nano-concaves were studied. • The effect of 10 nm Al{sub 2}O{sub 3} spacer on PL emission from ZnO thin films was analyzed. • Plasmonic enhancement of the PL emission was dependent on the D{sub c} and the spacer. • The highest 9-fold enhancement was obtained for the Al/ZnO sample with D{sub c} ∼333 nm. - Abstract: Surface plasmons (SPs) supported by Al nano-concave arrays with increasing interpore distance (D{sub c}) were used to enhance the ultraviolet light emission from ZnO thin films. Two sets of samples were prepared: in the first set the thin ZnO films were deposited directly on Al nanoconcaves (the Al/ZnO samples) and in the second set a 10 nm − Al{sub 2}O{sub 3} spacer was placed between the textured Al and the ZnO films (the Al/Al{sub 2}O{sub 3}-ALD/ZnO samples). In the Al/ZnO samples the enhancement was limited by a nonradiative energy dissipation due to the Ohmic loss in the Al metal. However, for the ZnO layer deposited directly on Al nanopits synthesized at 150 V (D{sub c} = 333 ± 18 nm), the largest 9-fold enhancement was obtained by achieving the best energy fit between the near band-edge (NBE) emission from ZnO and the λ{sub (0,1)} SPP resonance mode. In the Al/Al{sub 2}O{sub 3}-ALD/ZnO samples the amplification of the UV emission was smaller than in the Al/ZnO samples due to a big energy mismatch between the NBE emission and the λ{sub (0,1)} plasmonic mode. The results obtained in this work indicate that better tuning of the NBE − λ{sub (0,1)} SPP resonance mode coupling is possible through a proper modification of geometrical parameters in the Al/Al{sub 2}O{sub 3}-ALD/ZnO system such as Al nano-concave spacing and the thickness of the corresponding layer. This approach will reduce the negative influence of the non-radiative plasmonic modes and most likely will lead to further

  4. Identification of Tequila with an Array of ZnO Thin Films: A Simple and Cost-Effective Method

    Directory of Open Access Journals (Sweden)

    Pedro Estanislao Acuña-Avila

    2017-12-01

    Full Text Available An array of ZnO thin film sensors was obtained by thermal oxidation of physical vapor deposited thin Zn films. Different conditions of the thermal treatment (duration and temperature were applied in view of obtaining ZnO sensors with different gas sensing properties. Films having undergone a long thermal treatment exhibited high responses to low ethanol concentrations, while short thermal treatments generally led to sensors with high ethanol sensitivity. The sensor array was used to distinguish among Tequilas and Agave liquor. Linear discriminant analysis and the multilayer perceptron neural network reached 100% and 86.3% success rates in the discrimination between real Tequila and Agave liquor and in the identification of Tequila brands, respectively. These results are promising for the development of an inexpensive tool offering low complexity and cost of analysis for detecting fraud in spirits.

  5. Electrodeposition of CdSe coatings on ZnO nanowire arrays for extremely thin absorber solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Majidi, Hasti [Department of Chemical and Biological Engineering, Drexel University, 3141 Chestnut St, Philadelphia, PA 19104 (United States); Baxter, Jason B., E-mail: jbaxter@drexel.ed [Department of Chemical and Biological Engineering, Drexel University, 3141 Chestnut St, Philadelphia, PA 19104 (United States)

    2011-02-15

    We report on electrodeposition of CdSe coatings onto ZnO nanowire arrays and determine the effect of processing conditions on material properties such as morphology and microstructure. CdSe-coated ZnO nanowire arrays have potential use in extremely thin absorber (ETA) solar cells, where CdSe absorbs visible light and injects photoexcited electrons into the ZnO nanowires. We show that room-temperature electrodeposition enables growth of CdSe coatings that are highly crystalline, uniform, and conformal with precise control over thickness and microstructure. X-ray diffraction and transmission electron microscopy show nanocrystalline CdSe in both hexagonal and cubic phases with grain size {approx}5 nm. Coating morphology depends on electrodeposition current density. Uniform and conformal coatings were achieved using moderate current densities of {approx}2 mA cm{sup -2} for nanowires with roughness factor of {approx}10, while lower current densities resulted in sparse nucleation and growth of larger, isolated islands. Electrodeposition charge density controls the thickness of the CdSe coating, which was exploited to investigate the evolution of the morphology at early stages of nucleation and growth. UV-vis transmission spectroscopy and photoelectrochemical solar cell measurements demonstrate that CdSe effectively sensitizes ZnO nanowires to visible light.

  6. Electrodeposition of CdSe coatings on ZnO nanowire arrays for extremely thin absorber solar cells

    International Nuclear Information System (INIS)

    Majidi, Hasti; Baxter, Jason B.

    2011-01-01

    We report on electrodeposition of CdSe coatings onto ZnO nanowire arrays and determine the effect of processing conditions on material properties such as morphology and microstructure. CdSe-coated ZnO nanowire arrays have potential use in extremely thin absorber (ETA) solar cells, where CdSe absorbs visible light and injects photoexcited electrons into the ZnO nanowires. We show that room-temperature electrodeposition enables growth of CdSe coatings that are highly crystalline, uniform, and conformal with precise control over thickness and microstructure. X-ray diffraction and transmission electron microscopy show nanocrystalline CdSe in both hexagonal and cubic phases with grain size ∼5 nm. Coating morphology depends on electrodeposition current density. Uniform and conformal coatings were achieved using moderate current densities of ∼2 mA cm -2 for nanowires with roughness factor of ∼10, while lower current densities resulted in sparse nucleation and growth of larger, isolated islands. Electrodeposition charge density controls the thickness of the CdSe coating, which was exploited to investigate the evolution of the morphology at early stages of nucleation and growth. UV-vis transmission spectroscopy and photoelectrochemical solar cell measurements demonstrate that CdSe effectively sensitizes ZnO nanowires to visible light.

  7. ZnO Thin Film Electronics for More than Displays

    Science.gov (United States)

    Ramirez, Jose Israel

    Zinc oxide thin film transistors (TFTs) are investigated in this work for large-area electronic applications outside of display technology. A constant pressure, constant flow, showerhead, plasma-enhanced atomic layer deposition (PEALD) process has been developed to fabricate high mobility TFTs and circuits on rigid and flexible substrates at 200 °C. ZnO films and resulting devices prepared by PEALD and pulsed laser deposition (PLD) have been compared. Both PEALD and PLD ZnO films result in densely packed, polycrystalline ZnO thin films that were used to make high performance devices. PEALD ZnO TFTs deposited at 300 °C have a field-effect mobility of ˜ 40 cm2/V-s (and > 20 cm2/V-S deposited at 200 °C). PLD ZnO TFTs, annealed at 400 °C, have a field-effect mobility of > 60 cm2/V-s (and up to 100 cm2/V-s). Devices, prepared by either technique, show high gamma-ray radiation tolerance of up to 100 Mrad(SiO2) with only a small radiation-induced threshold voltage shift (VT ˜ -1.5 V). Electrical biasing during irradiation showed no enhanced radiation-induced effects. The study of the radiation effects as a function of material stack thicknesses revealed the majority of the radiation-induced charge collection happens at the semiconductor-passivation interface. A simple sheet-charge model at that interface can describe the radiation-induced charge in ZnO TFTs. By taking advantage of the substrate-agnostic process provided by PEALD, due to its low-temperature and excellent conformal coatings, ZnO electronics were monolithically integrated with thin-film complex oxides. Application-based examples where ZnO electronics provide added functionality to complex oxide-based devices are presented. In particular, the integration of arrayed lead zirconate titanate (Pb(Zr, Ti)O3 or PZT) thin films with ZnO electronics for microelectromechanical systems (MEMs) and deformable mirrors is demonstrated. ZnO switches can provide voltage to PZT capacitors with fast charging and slow

  8. Synthesis and characterization of Mn-doped ZnO column arrays

    International Nuclear Information System (INIS)

    Yang Mei; Guo Zhixing; Qiu Kehui; Long Jianping; Yin Guangfu; Guan Denggao; Liu Sutian; Zhou Shijie

    2010-01-01

    Mn-doped ZnO column arrays were successfully synthesized by conventional sol-gel process. Effect of Mn/Zn atomic ratio and reaction time were investigated, and the morphology, tropism and optical properties of Mn-doped ZnO column arrays were characterized by SEM, XRD and photoluminescence (PL) spectroscopy. The result shows that a Mn/Zn atomic ratio of 0.1 and growth time of 12 h are the optimal condition for the preparation of densely distributed ZnO column arrays. XRD analysis shows that Mn-doped ZnO column arrays are highly c-axis oriented. As for Mn-doped ZnO column arrays, obvious increase of photoluminescence intensity is observed at the wavelength of ∼395 nm and ∼413 nm, compared to pure ZnO column arrays.

  9. Highly Uniform Epitaxial ZnO Nanorod Arrays for Nanopiezotronics

    Directory of Open Access Journals (Sweden)

    Nagata T

    2009-01-01

    Full Text Available Abstract Highly uniform and c-axis-aligned ZnO nanorod arrays were fabricated in predefined patterns by a low temperature homoepitaxial aqueous chemical method. The nucleation seed patterns were realized in polymer and in metal thin films, resulting in, all-ZnO and bottom-contacted structures, respectively. Both of them show excellent geometrical uniformity: the cross-sectional uniformity according to the scanning electron micrographs across the array is lower than 2%. The diameter of the hexagonal prism-shaped nanorods can be set in the range of 90–170 nm while their typical length achievable is 0.5–2.3 μm. The effect of the surface polarity was also examined, however, no significant difference was found between the arrays grown on Zn-terminated and on O-terminated face of the ZnO single crystal. The transmission electron microscopy observation revealed the single crystalline nature of the nanorods. The current–voltage characteristics taken on an individual nanorod contacted by a Au-coated atomic force microscope tip reflected Schottky-type behavior. The geometrical uniformity, the designable pattern, and the electrical properties make the presented nanorod arrays ideal candidates to be used in ZnO-based DC nanogenerator and in next-generation integrated piezoelectric nano-electromechanical systems (NEMS.

  10. Fast light-induced reversible wettability of a zinc oxide nanorod array coated with a thin gold layer

    Science.gov (United States)

    Wei, Yuefan; Du, Hejun; Kong, Junhua; Tran, Van-Thai; Koh, Jia Kai; Zhao, Chenyang; He, Chaobin

    2017-11-01

    Zinc oxide (ZnO) has gained much attention recently due to its excellent physical and chemical properties, and has been extensively studied in energy harvesting applications such as photovoltaic and piezoelectric devices. In recent years, its reversible wettability has also attracted increasing interest. The wettability of ZnO nanostructures with various morphologies has been studied. However, to the best of our knowledge, there is still a lack of investigations on further modifications on ZnO to provide more benefits than pristine ZnO. Comprehensive studies on the reversible wettability are still needed. In this study, a ZnO nanorod array was prepared via a hydrothermal process and subsequently coated with thin gold layers with varied thickness. The morphologies and structures, optical properties and wettability were investigated. It is revealed that the ZnO-Au system possesses recoverable wettability upon switching between visible-ultraviolet light and a dark environment, which is verified by the contact angle change. The introduction of the thin gold layer to the ZnO nanorod array effectively increases the recovery rate of the wettability. The improvements are attributed to the hierarchical structures, which are formed by depositing thin gold layers onto the ZnO nanorod array, the visible light sensitivity due to the plasmonic effect of the deposited gold, as well as the fast charge-induced surface status change upon light illumination or dark storage. The improvement is beneficial to applications in environmental purification, energy harvesting, micro-lenses, and smart devices.

  11. Highly transparent and UV-resistant superhydrophobic SiO2-coated ZnO nanorod arrays

    KAUST Repository

    Gao, Yangqin; Gereige, Issam; El Labban, Abdulrahman; Cha, Dong Kyu; Isimjan, Tayirjan T.; Beaujuge, Pierre

    2014-01-01

    Highly transparent and UV-resistant superhydrophobic arrays of SiO 2-coated ZnO nanorods are prepared in a sequence of low-temperature (<150 C) steps on both glass and thin sheets of PET (2 × 2 in. 2), and the superhydrophobic nanocomposite

  12. Synthesis of ordered large-scale ZnO nanopore arrays

    International Nuclear Information System (INIS)

    Ding, G.Q.; Shen, W.Z.; Zheng, M.J.; Fan, D.H.

    2006-01-01

    An effective approach is demonstrated for growing ordered large-scale ZnO nanopore arrays through radio-frequency magnetron sputtering deposition on porous alumina membranes (PAMs). The realization of highly ordered hexagonal ZnO nanopore arrays benefits from the unique properties of ZnO (hexagonal structure, polar surfaces, and preferable growth directions) and PAMs (controllable hexagonal nanopores and localized negative charges). Further evidence has been shown through the effects of nanorod size and thermal treatment of PAMs on the yielded morphology of ZnO nanopore arrays. This approach opens the possibility of creating regular semiconducting nanopore arrays for the application of filters, sensors, and templates

  13. ZnO thin films and nanostructures for emerging optoelectronic applications

    Science.gov (United States)

    Rogers, D. J.; Teherani, F. H.; Sandana, V. E.; Razeghi, M.

    2010-02-01

    ZnO-based thin films and nanostructures grown by PLD for various emerging optoelectronic applications. AZO thin films are currently displacing ITO for many TCO applications due to recent improvements in attainable AZO conductivity combined with processing, cost and toxicity advantages. Advances in the channel mobilities and Id on/off ratios in ZnO-based TTFTs have opened up the potential for use as a replacement for a-Si in AM-OLED and AM-LCD screens. Angular-dependent specular reflection measurements of self-forming, moth-eye-like, nanostructure arrays grown by PLD were seen to have green gap in InGaN-based LEDs was combated by substituting low Ts PLD n-ZnO for MOCVD n-GaN in inverted hybrid heterojunctions. This approach maintained the integrity of the InGaN MQWs and gave LEDs with green emission at just over 510 nm. Hybrid n-ZnO/p-GaN heterojunctions were also seen to have the potential for UV (375 nm) EL, characteristic of ZnO NBE emission. This suggests that there was significant hole injection into the ZnO and that such LEDs could profit from the relatively high exciton binding energy of ZnO.

  14. Enhanced ultraviolet photo-response in Dy doped ZnO thin film

    Science.gov (United States)

    Kumar, Pawan; Singh, Ranveer; Pandey, Praveen C.

    2018-02-01

    In the present work, a Dy doped ZnO thin film deposited by the spin coating method has been studied for its potential application in a ZnO based UV detector. The investigations on the structural property and surface morphology of the thin film ensure that the prepared samples are crystalline and exhibit a hexagonal crystal structure of ZnO. A small change in crystallite size has been observed due to Dy doping in ZnO. AFM analysis ascertains the grain growth and smooth surface of the thin films. The Dy doped ZnO thin film exhibits a significant enhancement in UV region absorption as compared to the pure ZnO thin film, which suggests that Dy doped ZnO can be used as a UV detector. Under UV irradiation of wavelength 325 nm, the photocurrent value of Dy doped ZnO is 105.54 μA at 4.5 V, which is 31 times greater than that of the un-doped ZnO thin film (3.39 μA). The calculated value of responsivity is found to increase significantly due to the incorporation of Dy in the ZnO lattice. The observed higher value of photocurrent and responsivity could be attributed to the substitution of Dy in the ZnO lattice, which enhances the conductivity, electron mobility, and defects in ZnO and benefits the UV sensing property.

  15. Integrated ZnO nanotube arrays as efficient dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Xi, Y., E-mail: yxi6@cqu.edu.cn [Department of Applied Physics, Chongqing University, Chongqing 400044 (China); School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0245 (United States); Wu, W.Z.; Fang, H. [School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0245 (United States); Hu, C.G. [Department of Applied Physics, Chongqing University, Chongqing 400044 (China)

    2012-07-15

    Highlights: Black-Right-Pointing-Pointer Tuning the reaction parameters, we got the best reaction conditions on ITO glass. Black-Right-Pointing-Pointer Introduce ZnO NTs design of photoanode featuring high aspect ratio structure. Black-Right-Pointing-Pointer The design strategy integrates the optical fibers or ITO with ZnO NTs grown. - Abstract: Zinc oxide (ZnO) is a wide band gap semiconducting material and has been considered as an alternative material in dye-sensitized solar cell (DSSC) applications. A high-performance nanotube (NT) photoanode must have a large surface area for dye adsorption in order to enhance conversion efficiency. In this work, the way of hydrothermally grown ZnO NT arrays on the indium tin oxide (ITO) substrate is presented by utilizing a systematic study. By adjusting the hydrothermal reaction parameters, we attained the optimizing reaction conditions on the ITO substrate. Moreover, ZnO NT arrays are introduced as a photoanode on various substrates, such as optical fiber and ITO glass, for DSSCs applications. We took the contrast test with conversion efficiency of the DSSC based on ZnO NT arrays versus ZnO nanowire arrays on the ITO substrate, which the DSSC based on ZnO NT arrays shows significantly enhanced power conversion efficiency. Furthermore, the conversion efficiency of DSSC based on the ZnO NT arrays grown on an optical fiber substrate is enhanced up to 1.44%.

  16. Decoration of PbS nanoparticles on Al-doped ZnO nanorod array thin film with hydrogen treatment as a photoelectrode for solar water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Hsu, Chih-Hsiung; Chen, Chao-Hong [Department of Chemical Engineering and Research Center for Energy Technology and Strategy, National Cheng Kung University, Tainan 701, Taiwan, ROC (China); Chen, Dong-Hwang, E-mail: chendh@mail.ncku.edu.tw [Department of Chemical Engineering and Research Center for Energy Technology and Strategy, National Cheng Kung University, Tainan 701, Taiwan, ROC (China)

    2013-03-25

    Highlights: ► AZO nanorod array thin film is used as a photoanode for solar water splitting. ► Hydrogen treatment and sensitization by PbS nanoparticles enhance photocurrent. ► A novel ITO/FTO-free composite photoelectrode is developed. ► The pre-fabrication and use of an extra TCO thin film substrate is unnecessary. -- Abstract: Al-doped ZnO (AZO) nanorod arrays thin film with hydrogen treatment is directly used as a photoelectrode for solar water splitting without an extra transparent conducting oxide (TCO) thin film because it possesses the functions of TCO thin film and photoactive 1-dimensional nanostructured semiconductor simultaneously. To enhance the absorption in the visible region, PbS nanoparticles decorated the AZO nanorods via successive ionic layer adsorption and reaction route. The PbS nanoparticles have a face-centered cubic structure and their decoration does not destroy the 1-dimensional morphology of AZO nanorod arrays. With increasing the cycle number of PbS nanoparticles decoration, the grain size and loading of PbS nanoparticles become larger gradually which leads to lower energy bandgap and stronger absorption. A maximum photocurrent density of 1.65 mW cm{sup −2} is obtained when the cycle number is 20, which is much higher than those without PbS nanoparticles sensitization or hydrogen treatment. This demonstrates that the AZO nanorod array thin film with hydrogen treatment can be directly used as a photoelectrode without an extra TCO thin film. Because the use of expensive metals can be avoided and the pre-fabrication of TCO thin film substrate is necessary no more, the fabrication of such a composite photoelectrode becomes simple and low-cost. So, it has great potentials in solar water splitting after sensitization by quantum dots capable of visible light absorption.

  17. Controlling growth rate anisotropy for formation of continuous ZnO thin films from seeded substrates

    International Nuclear Information System (INIS)

    Zhang, R H; Slamovich, E B; Handwerker, C A

    2013-01-01

    Solution-processed zinc oxide (ZnO) thin films are promising candidates for low-temperature-processable active layers in transparent thin film electronics. In this study, control of growth rate anisotropy using ZnO nanoparticle seeds, capping ions, and pH adjustment leads to a low-temperature (90 ° C) hydrothermal process for transparent and high-density ZnO thin films. The common 1D ZnO nanorod array was grown into a 2D continuous polycrystalline film using a short-time pure solution method. Growth rate anisotropy of ZnO crystals and the film morphology were tuned by varying the chloride (Cl − ) ion concentration and the initial pH of solutions of zinc nitrate and hexamethylenetetramine (HMTA), and the competitive adsorption effects of Cl − ions and HMTA ligands on the anisotropic growth behavior of ZnO crystals were proposed. The lateral growth of nanorods constituting the film was promoted by lowering the solution pH to accelerate the hydrolysis of HMTA, thereby allowing the adsorption effects from Cl − to dominate. By optimizing the growth conditions, a dense ∼100 nm thickness film was fabricated in 15 min from a solution of [Cl − ]/[Zn 2+ ] = 1.5 and pH= 4.8 ± 0.1. This film shows >80% optical transmittance and a field-effect mobility of 2.730 cm 2 V −1 s −1 at zero back-gate bias. (paper)

  18. Direct current magnetron sputter-deposited ZnO thin films

    International Nuclear Information System (INIS)

    Hoon, Jian-Wei; Chan, Kah-Yoong; Krishnasamy, Jegenathan; Tou, Teck-Yong; Knipp, Dietmar

    2011-01-01

    Zinc oxide (ZnO) is a very promising electronic material for emerging transparent large-area electronic applications including thin-film sensors, transistors and solar cells. We fabricated ZnO thin films by employing direct current (DC) magnetron sputtering deposition technique. ZnO films with different thicknesses ranging from 150 nm to 750 nm were deposited on glass substrates. The deposition pressure and the substrate temperature were varied from 12 mTorr to 25 mTorr, and from room temperature to 450 deg. C, respectively. The influence of the film thickness, deposition pressure and the substrate temperature on structural and optical properties of the ZnO films was investigated using atomic force microscopy (AFM) and ultraviolet-visible (UV-Vis) spectrometer. The experimental results reveal that the film thickness, deposition pressure and the substrate temperature play significant role in the structural formation and the optical properties of the deposited ZnO thin films.

  19. Piezoelectric Nanogenerator Using p-Type ZnO Nanowire Arrays

    KAUST Repository

    Lu, Ming-Pei; Song, Jinhui; Lu, Ming-Yen; Chen, Min-Teng; Gao, Yifan; Chen, Lih-Juann; Wang, Zhong Lin

    2009-01-01

    Using phosphorus-doped ZnO nanowire (NW) arrays grown on silicon substrate, energy conversion using the p-type ZnO NWs has been demonstrated for the first time. The p-type ZnO NWs produce positive output voltage pulses when scanned by a conductive

  20. Nanofabrication and characterization of ZnO nanorod arrays and branched microrods by aqueous solution route and rapid thermal processing

    International Nuclear Information System (INIS)

    Lupan, Oleg; Chow, Lee; Chai, Guangyu; Roldan, Beatriz; Naitabdi, Ahmed; Schulte, Alfons; Heinrich, Helge

    2007-01-01

    This paper presents an inexpensive and fast fabrication method for one-dimensional (1D) ZnO nanorod arrays and branched two-dimensional (2D), three-dimensional (3D) - nanoarchitectures. Our synthesis technique includes the use of an aqueous solution route and post-growth rapid thermal annealing. It permits rapid and controlled growth of ZnO nanorod arrays of 1D - rods, 2D - crosses, and 3D - tetrapods without the use of templates or seeds. The obtained ZnO nanorods are uniformly distributed on the surface of Si substrates and individual or branched nano/microrods can be easily transferred to other substrates. Process parameters such as concentration, temperature and time, type of substrate and the reactor design are critical for the formation of nanorod arrays with thin diameter and transferable nanoarchitectures. X-ray diffraction, scanning electron microscopy, X-ray photoelectron spectroscopy, transmission electron microscopy and Micro-Raman spectroscopy have been used to characterize the samples

  1. Single-Crystal Mesoporous ZnO Thin Films Composed of Nanowalls

    KAUST Repository

    Wang, Xudong

    2009-02-05

    This paper presents a controlled, large scale fabrication of mesoporous ZnO thin films. The entire ZnO mesoporous film is one piece of a single crystal, while high porosity made of nanowalls is present. The growth mechanism was proposed in comparison with the growth of ZnO nanowires. The ZnO mesoporous film was successfully applied as a gas sensor. The fabrication and growth analysis of the mesoporous ZnO thin film gi ve general guidance for the controlled growth of nanostructures. It also pro vides a unique structure with a superhigh surface-to-volume ratio for surface-related applications. © 2009 American Chemical Society.

  2. Field emission properties of ZnO nanosheet arrays

    International Nuclear Information System (INIS)

    Naik, Kusha Kumar; Rout, Chandra Sekhar; Khare, Ruchita; More, Mahendra A.; Chakravarty, Disha; Late, Dattatray J.; Thapa, Ranjit

    2014-01-01

    Electron emission properties of electrodeposited ZnO nanosheet arrays grown on Indium tin oxide coated glass substrates have been studied. Influence of oxygen vacancies on electronic structures and field emission properties of ZnO nanosheets are investigated using density functional theory. The oxygen vacancies produce unshared d electrons which form an impurity energy state; this causes shifting of Fermi level towards the vacuum, and so the barrier energy for electron extraction reduces. The ZnO nanosheet arrays exhibit a low turn-on field of 2.4 V/μm at 0.1 μA/cm 2 and current density of 50.1 μA/cm 2 at an applied field of 6.4 V/μm with field enhancement factor, β = 5812 and good field emission current stability. The nanosheet arrays grown by a facile electrodeposition process have great potential as robust high performance vertical structure electron emitters for future flat panel displays and vacuum electronic device applications

  3. Laser nanostructuring of ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Nedyalkov, N., E-mail: nned@ie.bas.bg [Department of Electronics and Electrical Engineering, Keio University, 3-14-1 Hiyoshi Kohoku-ku, Yokohama-shi, Kanagawa-ken 223-8522 (Japan); Institute of Electronics, Bulgarian Academy of Sciences, Tzarigradsko shousse 72, Sofia 1784 (Bulgaria); Koleva, M.; Nikov, R.; Atanasov, P. [Institute of Electronics, Bulgarian Academy of Sciences, Tzarigradsko shousse 72, Sofia 1784 (Bulgaria); Nakajima, Y.; Takami, A.; Shibata, A.; Terakawa, M. [Department of Electronics and Electrical Engineering, Keio University, 3-14-1 Hiyoshi Kohoku-ku, Yokohama-shi, Kanagawa-ken 223-8522 (Japan)

    2016-06-30

    Highlights: • Nanosecond laser pulse nanostructuring of ZnO thin films on metal substrate is demonstrated. • Two regimes of the thin film modification are observed depending on the applied laser fluence. • At high fluence regime the ZnO film is homogeneously decomposed into nanosized particles. • The characteristic size of the formed nanostructures corresponds to the domain size of the thin film. - Abstract: In this work, results on laser processing of thin zinc oxide films deposited on metal substrate are presented. ZnO films are obtained by classical nanosecond pulsed laser deposition method in oxygen atmosphere on tantalum substrate. The produced films are then processed by nanosecond laser pulses at wavelength of 355 nm. The laser processing parameters and the film thickness are varied and their influence on the fabricated structures is estimated. The film morphology after the laser treatment is found to depend strongly on the laser fluence as two regimes are defined. It is shown that at certain conditions (high fluence regime) the laser treatment of the film leads to formation of a discrete nanostructure, composed of spherical like nanoparticles with narrow size distribution. The dynamics of the melt film on the substrate and fast cooling are found to be the main mechanisms for fabrication of the observed structures. The demonstrated method is an alternative way for direct fabrication of ZnO nanostructures on metal which can be easy implemented in applications as resistive sensor devices, electroluminescent elements, solar cell technology.

  4. Enhanced field emission of ZnO nanoneedle arrays via solution etching at room temperature

    DEFF Research Database (Denmark)

    Ma, Huanming; Qin, Zhiwei; Wang, Zaide

    2017-01-01

    ZnO nanoneedle arrays (ZnO nns) were synthesized by a facile two-step solution-phase method based on the etching of pre-synthesized ZnO nanowire arrays (ZnO nws) with flat ends at room temperature. Field emission measurement results showed that the turn-on electronic fields of ZnO nns and nws wer...

  5. Appraisal on Textured Grain Growth and Photoconductivity of ZnO Thin Film SILAR

    Directory of Open Access Journals (Sweden)

    Deepu Thomas

    2014-01-01

    Full Text Available ZnO thin films were prepared by successive ionic layer adsorption reaction (SILAR method. The textured grain growth along c-axis in pure ZnO thin films and doped with Sn was studied. The structural analysis of the thin films was done by X-ray diffraction and surface morphology by scanning electron microscopy. Textured grain growth of the samples was measured by comparing the peak intensities. Textured grain growth and photo current in ZnO thin films were found to be enhanced by doping with Sn. ZnO thin film having good crystallinity with preferential (002 orientation is a semiconductor with photonic properties of potential benefit to biophotonics. From energy dispersive X-ray analysis, it is inferred that oxygen vacancy creation is responsible for the enhanced textured grain growth in ZnO thin films.

  6. Tunable field emission characteristics of ZnO nanowires coated with varied thickness of lanthanum boride thin films

    International Nuclear Information System (INIS)

    Zhao, C.X.; Li, Y.F.; Chen, Jun; Deng, S.Z.; Xu, N.S.

    2013-01-01

    Lanthanum boride (LaB x ) thin films with various thicknesses were deposited on ZnO nanowire arrays by electron beam evaporation. Field emission characteristics of ZnO nanowires show close dependence on LaB x coating thickness. The turn-on field increases with increasing LaB x coating thickness from 10 nm to 50 nm. The observed phenomena were explained by a model that the tunneling at ZnO/LaB x interface dominates the emission process. - Highlights: ► Coating thickness dependence of field emission characteristics of ZnO nanowires was observed from LaB x coated ZnO nanowires. ► More stable field emission was observed from ZnO nanowires with LaB x coating. ► A model was proposed that the tunneling at ZnO/LaB x interface dominates the emission process

  7. Two different mechanisms on UV emission enhancement in Ag-doped ZnO thin films

    International Nuclear Information System (INIS)

    Xu, Linhua; Zheng, Gaige; Zhao, Lilong; Pei, Shixin

    2015-01-01

    Ag-doped ZnO thin films were prepared by a sol–gel method. The structural, morphological and optical properties of the samples were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), UV–vis and photoluminescence spectra. The results show that the Ag in the ZnO thin films annealed at 500 °C for 1 h substitutes for Zn and exists in the form of Ag + ion (Ag Zn ) while the Ag in the ZnO thin films without a post-annealing mainly exists in the form of simple substance (Ag 0 ). The incorporation of Ag indeed can improve the ultraviolet emission of ZnO thin films and suppress the visible emissions at the same time. However, the mechanisms on the ultraviolet emission enhancement in the annealed and unannealed Ag-doped ZnO thin films are very different. As for the post-annealed Ag-doped ZnO thin films, the UV emission enhancement maybe mainly results from more electron–hole pairs (excitons) due to Ag-doping while for the unannealed Ag-doped ZnO thin films; the UV emission enhancement is attributed to the resonant coupling between exciton emission in ZnO and localized surface plasmon in Ag nanoparticles. - Highlights: • Ag-doped ZnO thin films have been prepared by the sol–gel method. • Ag-doping can enhance ultraviolet emission of ZnO thin films and depress the visible emissions at the same time. • There are two different mechanisms on UV emission enhancement in Ag-doped ZnO thin films. • The UV emission enhancement from the resonant coupling between excitonic emissions and localized surface plasmon in Ag nanoparticle is very attractive

  8. Implanted ZnO thin films: Microstructure, electrical and electronic properties

    International Nuclear Information System (INIS)

    Lee, J.; Metson, J.; Evans, P.J.; Kinsey, R.; Bhattacharyya, D.

    2007-01-01

    Magnetron sputtered polycrystalline ZnO thin films were implanted using Al, Ag, Sn, Sb and codoped with TiN in order to improve the conductivity and to attempt to achieve p-type behaviour. Structural and electrical properties of the implanted ZnO thin films were examined with X-ray diffractometry (XRD), scanning electron microscopy (SEM), secondary ion mass spectrometry (SIMS), atomic force microscopy (AFM) and conductivity measurements. Depth profiles of the implanted elements varied with the implant species. Implantation causes a partial amorphisation of the crystalline structure and decreases the effective grain size of the films. One of the findings is the improvement, as a consequence of implantation, in the conductivity of initially poorly conductive samples. Heavy doping may help for the conversion of conduction type of ZnO thin films. Annealing in vacuum mitigated structural damage and stress caused by implantation, and improved the conductivity of the implanted ZnO thin films

  9. Piezoelectric Response Evaluation of ZnO Thin Film Prepared by RF Magnetron Sputtering

    Directory of Open Access Journals (Sweden)

    Cheng Da-Long

    2017-01-01

    Full Text Available The most important parameter of piezoelectric materials is piezoelectric coefficient (d33. In this study, the piezoelectric ZnO thin films were deposited on the SiNx/Si substrate. The 4 inches substrate is diced into 8 cm× 8 cm piece. During the deposition process, a zinc target (99.999 wt% of 2 inches diameter was used. The vertical distance between the target and the substrate holder was fixed at 5 cm. The piezoelectric response of zinc oxide (ZnO thin films were obtained by using a direct measurement system. The system adopts a mini impact tip to generate an impulsive force and read out the piezoelectric signals immediately. Experimentally, a servo motor is used to produce a fixed quantity of force, for giving an impact against to the piezoelectric film. The ZnO thin films were deposited using the reactive radio frequency (RF magnetron sputtering method. The electric charges should be generated because of the material’s extrusion. This phenomenon was investigated through the oscilloscope by one shot trigger. It was apparent that all ZnO films exhibit piezoelectric responses evaluated by our measurement system, however, its exhibit a significant discrepancy. The piezoelectric responses of ZnO thin film at various deposition positions were measured and the crystal structures of the sputtering pressure were also discussed. The crystalline characteristics of ZnO thin films are investigated through the XRD and SEM. The results show the ZnO thin film exhibits good crystalline pattern and surface morphology with controlled sputtering condition. The ZnO thin films sputtered using 2 inches target present various piezoelectric responses. With the exactly related position, a best piezoelectric response of ZnO thin film can be achieved.

  10. Crystallinity Improvement of ZnO Thin Film on Different Buffer Layers Grown by MBE

    Directory of Open Access Journals (Sweden)

    Shao-Ying Ting

    2012-01-01

    Full Text Available The material and optical properties of ZnO thin film samples grown on different buffer layers on sapphire substrates through a two-step temperature variation growth by molecular beam epitaxy were investigated. The thin buffer layer between the ZnO layer and the sapphire substrate decreased the lattice mismatch to achieve higher quality ZnO thin film growth. A GaN buffer layer slightly increased the quality of the ZnO thin film, but the threading dislocations still stretched along the c-axis of the GaN layer. The use of MgO as the buffer layer decreased the surface roughness of the ZnO thin film by 58.8% due to the suppression of surface cracks through strain transfer of the sample. From deep level emission and rocking curve measurements it was found that the threading dislocations play a more important role than oxygen vacancies for high-quality ZnO thin film growth.

  11. Nanostructured ZnO thin films prepared by sol–gel spin-coating

    Energy Technology Data Exchange (ETDEWEB)

    Heredia, E., E-mail: heredia.edu@gmail.com [UNIDEF (CONICET-MINDEF), J.B. de La Salle 4397, 1603 Villa Martelli, Pcia. de Buenos Aires (Argentina); Bojorge, C.; Casanova, J.; Cánepa, H. [UNIDEF (CONICET-MINDEF), J.B. de La Salle 4397, 1603 Villa Martelli, Pcia. de Buenos Aires (Argentina); Craievich, A. [Instituto de Física, Universidade de São Paulo, Cidade Universitária, 66318 São Paulo, SP (Brazil); Kellermann, G. [Universidade Federal do Paraná, 19044 Paraná (Brazil)

    2014-10-30

    Highlights: • ZnO films synthesized by sol–gel were deposited by spin-coating on flat substrates. • Structural features of ZnO films with several thicknesses were characterized by means of different techniques. • The thicknesses of different ZnO thin films were determined by means of FESEM and AFM. • The nanoporous structures of ZnO thin films were characterized by GISAXS using IsGISAXS software. • The average densities of ZnO thin films were derived from (i) the critical angle in 1D XR patterns, (ii) the angle of Yoneda peak in 2D GISAXS images, (iii) minimization of chi2 using IsGISAXS best fitting procedure. - Abstract: ZnO thin films deposited on silica flat plates were prepared by spin-coating and studied by applying several techniques for structural characterization. The films were prepared by depositing different numbers of layers, each deposition being followed by a thermal treatment at 200 °C to dry and consolidate the successive layers. After depositing all layers, a final thermal treatment at 450 °C during 3 h was also applied in order to eliminate organic components and to promote the crystallization of the thin films. The total thickness of the multilayered films – ranging from 40 nm up to 150 nm – was determined by AFM and FESEM. The analysis by GIXD showed that the thin films are composed of ZnO crystallites with an average diameter of 25 nm circa. XR results demonstrated that the thin films also exhibit a large volume fraction of nanoporosity, typically 30–40 vol.% in thin films having thicknesses larger than ∼70 nm. GISAXS measurements showed that the experimental scattering intensity is well described by a structural model composed of nanopores with shape of oblate spheroids, height/diameter aspect ratio within the 0.8–0.9 range and average diameter along the sample surface plane in the 5–7 nm range.

  12. A high power ZnO thin film piezoelectric generator

    Science.gov (United States)

    Qin, Weiwei; Li, Tao; Li, Yutong; Qiu, Junwen; Ma, Xianjun; Chen, Xiaoqiang; Hu, Xuefeng; Zhang, Wei

    2016-02-01

    A highly efficient and large area piezoelectric ZnO thin film nanogenerator (NG) was fabricated. The ZnO thin film was deposited onto a Si substrate by pulsed laser ablation at a substrate temperature of 500 °C. The deposited ZnO film exhibited a preferred c-axis orientation and a high piezoelectric value of 49.7 pm/V characterized using Piezoelectric Force Microscopy (PFM). Thin films of ZnO were patterned into rectangular power sources with dimensions of 0.5 × 0.5 cm2 with metallic top and bottom electrodes constructed via conventional semiconductor lithographic patterning processes. The NG units were subjected to periodic bending/unbending motions produced by mechanical impingement at a fixed frequency of 100 Hz at a pressure of 0.4 kg/cm2. The output electrical voltage, current density, and power density generated by one ZnO NG were recorded. Values of ∼95 mV, 35 μA cm-2 and 5.1 mW cm-2 were recorded. The level of power density is typical to that produced by a PZT NG on a flexible substrate. Higher energy NG sources can be easily created by adding more power units either in parallel or in series. The thin film ZnO NG technique is highly adaptable with current semiconductor processes, and as such, is easily integrated with signal collecting circuits that are compatible with mass production. A typical application would be using the power harvested from irregular human foot motions to either to operate blue LEDs directly or to drive a sensor network node in mille-power level without any external electric source and circuits.

  13. Flexible organic/inorganic hybrid solar cells based on conjugated polymer and ZnO nanorod array

    International Nuclear Information System (INIS)

    Tong, Fei; Kim, Kyusang; Martinez, Daniel; Thapa, Resham; Ahyi, Ayayi; Williams, John; Park, Minseo; Kim, Dong-Joo; Lee, Sungkoo; Lim, Eunhee; Lee, Kyeong K

    2012-01-01

    We report on the photovoltaic characteristics of organic/inorganic hybrid solar cells fabricated on ‘flexible’ transparent substrates. The solar cell device is composed of ZnO nanorod array and the bulk heterojunction structured organic layer which is the blend of poly(3-hexylthiophene) (P3HT) and (6,6)-phenyl C61 butyric acid methyl ester (PCBM). The ZnO nanorod array was grown on indium tin oxide (ITO)-coated polyethylene terephthalate (PET) substrates via a low-temperature (85 °C) aqueous solution process. The blend solution consisting of conjugated polymer P3HT and fullerene PCBM was spin coated at a low spinning rate of 400 rpm on top of the ZnO nanorod array structure and then the photoactive layer was slow dried at room temperature in air to promote its infiltration into the nanorod network. As a top electrode, silver was sputtered on top of the photoactive layer. The flexible solar cell with the structure of PET/ITO/ZnO thin film/ZnO nanorods/P3HT:PCBM/Ag exhibited a photovoltaic performance with an open circuit voltage (V OC ) of 0.52 V, a short circuit current density (J SC ) of 9.82 mA cm −2 , a fill factor (FF) of 35% and a power conversion efficiency (η) of 1.78%. All the measurements were performed under 100 mW cm −2 of illumination with an air mass 1.5 G filter. To the best of our knowledge, this is the first presentation of investigation into the fabrication and characterization of organic/inorganic hybrid solar cells based on bulk heterojunction structured conjugated polymer/fullerene photoactive layer and ZnO nanorod array constructed on flexible transparent substrates. (paper)

  14. Transient behaviors of ZnO thin films on a transparent, flexible polyethylene terephthalate substrate

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Yong Jun [Department of Nano-Physics, Gachon University, 1342 Seongnamdaero, Sujeong-gu, Seongnam-si, Gyeonggi-do 461-701 (Korea, Republic of); Lee, Ho Seok [Department of Materials Science and Engineering, Korea University, 5-1 Anam-dong, Seongbuk-gu, Seoul 136-713 (Korea, Republic of); Noh, Jin-Seo, E-mail: jinseonoh@gachon.ac.kr [Department of Nano-Physics, Gachon University, 1342 Seongnamdaero, Sujeong-gu, Seongnam-si, Gyeonggi-do 461-701 (Korea, Republic of)

    2016-03-31

    Thickness-dependent electrical, structural, and optical properties of zinc oxide (ZnO) thin films on polyethylene terephthalate (PET) substrates have been investigated in the very thin thickness range of 20 to 120 nm. In this thickness range, the electrical resistance of ZnO film increased with an increase in film thickness. This unusual transition behavior was explained in terms of structural evolution from Zn-phase-incorporating non-crystalline ZnO to hexagonal-structured ZnO. A critical thickness for the full development of hexagonal ZnO crystal was estimated at approximately 80 nm in this study. ZnO thin films on PET substrates exhibit a high optical transmittance of > 70% and good endurance to bending cycles over the measured thickness range. The results of this study indicate that a trade-off should be sought between structural, electrical, optical, and mechanical properties for practical applications of very thin ZnO films on organic substrates. - Highlights: • Very thin ZnO films were sputter-deposited on the PET substrate. • The ZnO film resistance increases with an increase in film thickness until saturation. • Hexagonal crystal structures gradually develop with increasing film thickness. • A Zn phase appears in a 20-nm-thick ZnO film. • ZnO films show high optical transmittance of > 80% and good endurance to bending.

  15. Transient behaviors of ZnO thin films on a transparent, flexible polyethylene terephthalate substrate

    International Nuclear Information System (INIS)

    Kim, Yong Jun; Lee, Ho Seok; Noh, Jin-Seo

    2016-01-01

    Thickness-dependent electrical, structural, and optical properties of zinc oxide (ZnO) thin films on polyethylene terephthalate (PET) substrates have been investigated in the very thin thickness range of 20 to 120 nm. In this thickness range, the electrical resistance of ZnO film increased with an increase in film thickness. This unusual transition behavior was explained in terms of structural evolution from Zn-phase-incorporating non-crystalline ZnO to hexagonal-structured ZnO. A critical thickness for the full development of hexagonal ZnO crystal was estimated at approximately 80 nm in this study. ZnO thin films on PET substrates exhibit a high optical transmittance of > 70% and good endurance to bending cycles over the measured thickness range. The results of this study indicate that a trade-off should be sought between structural, electrical, optical, and mechanical properties for practical applications of very thin ZnO films on organic substrates. - Highlights: • Very thin ZnO films were sputter-deposited on the PET substrate. • The ZnO film resistance increases with an increase in film thickness until saturation. • Hexagonal crystal structures gradually develop with increasing film thickness. • A Zn phase appears in a 20-nm-thick ZnO film. • ZnO films show high optical transmittance of > 80% and good endurance to bending.

  16. Growth of compact arrays of optical quality single crystalline ZnO

    Indian Academy of Sciences (India)

    We report the synthesis and optical properties of compact and aligned ZnO nanorod arrays (dia, ∼ 50–200 nm) grown on a glass substrate with varying seed particle density. The suspension of ZnO nanoparticles (size, ∼ 15 nm) of various concentrations are used as seed layer for the growth of nanorod arrays via ...

  17. Growth of Horizonatal ZnO Nanowire Arrays on Any Substrate

    KAUST Repository

    Qin, Yong

    2008-12-04

    A general method is presented for growing laterally aligned and patterned ZnO nanowire (NW) arrays on any substrate as long as it is flat. The orientation control is achieved using the combined effect from ZnO seed layer and the catalytically inactive Cr (or Sn) layer for NW growth. The growth temperature (< 100 °C) is so low that the method can be applied to a wide range of substrates that can be inorganic, organic, single crystal, polycrystal, or amorphous. The laterally aligned ZnO NW arrays can be employed for various applications, such as gas sensor, field effect transistor, nanogenerator, and flexible electronics. © 2008 American Chemical Society.

  18. Catalyst growth of single crystal aligned ZnO nanorods on ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Dongxu; Andreazza, Caroline; Andreazza, Pascal [Centre de Recherche sur la Matiere Divisee, CNRS-Universite d' Orleans, 1b rue de la Ferollerie, 45071 Orleans cedex 2 (France)

    2005-02-01

    One dimensional ZnO nanorods were successfully fabricated on Si substrates via a simple physical vapor-phase transport method at 950 C. A ZnO shell covered Au/Zn alloy is assumed as the nucleation site, then ZnO nanorods grow following a vapor-solid (VS) process. In order to guide the nanorod growth a c-axis oriented ZnO thin film and Au catalyst were first deposited on Si (100) surface. SEM images show nanorods grown on this substrate are vertical to the substrate surface. (copyright 2005 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  19. Synthesis of vertical arrays of ultra long ZnO nanowires on noncrystalline substrates

    International Nuclear Information System (INIS)

    Kwon, Bong Jun; Lee, Kyung Moon; Shin, Hae-Young; Kim, Jinwoong; Liu, Jinzhang; Yoon, Seokhyun; Lee, Soonil; Ahn, Y.H.; Park, Ji-Yong

    2012-01-01

    Highlights: ► Arrays of vertical ultra-long ZnO nanowires with lengths upto 300 μm. ► Controls of lengths and diameters of vertical arrays of ZnO nanowires on SiO 2 substrates. ► Luminescent and electrical properties of ZnO nanowires prepared with different growth conditions. - Abstract: Vertically aligned arrays of ultralong ZnO nanowires were synthesized on SiO 2 substrates with carbothermal vapor phase transport method with Au seeding layer. High density of vertically aligned ZnO nanowires with lengths from a few to ∼300 μm could be grown by controlling growth conditions. Supply of high concentration of Zn vapor and control of the ratio between Zn vapor and oxygen are found to have the most significant effects on the growth of long ZnO nanowires in the vapor–solid growth mechanism. The nanowires are of high crystalline quality as confirmed by various structural, compositional, and luminescent measurements. Luminescent and electrical properties of ZnO nanowires with different growth conditions were also investigated.

  20. Effect of Mg doping in ZnO buffer layer on ZnO thin film devices for electronic applications

    Science.gov (United States)

    Giri, Pushpa; Chakrabarti, P.

    2016-05-01

    Zinc Oxide (ZnO) thin films have been grown on p-silicon (Si) substrate using magnesium doped ZnO (Mg: ZnO) buffer layer by radio-frequency (RF) sputtering method. In this paper, we have optimized the concentration of Mg (0-5 atomic percent (at. %)) ZnO buffer layer to examine its effect on ZnO thin film based devices for electronic and optoelectronic applications. The crystalline nature, morphology and topography of the surface of the thin film have been characterized. The optical as well as electrical properties of the active ZnO film can be tailored by varying the concentration of Mg in the buffer layer. The crystallite size in the active ZnO thin film was found to increase with the Mg concentration in the buffer layer in the range of 0-3 at. % and subsequently decrease with increasing Mg atom concentration in the ZnO. The same was verified by the surface morphology and topography studies carried out with scanning electron microscope (SEM) and atomic electron microscopy (AFM) respectively. The reflectance in the visible region was measured to be less than 80% and found to decrease with increase in Mg concentration from 0 to 3 at. % in the buffer region. The optical bandgap was initially found to increase from 3.02 eV to 3.74 eV by increasing the Mg content from 0 to 3 at. % but subsequently decreases and drops down to 3.43 eV for a concentration of 5 at. %. The study of an Au:Pd/ZnO Schottky diode reveals that for optimum doping of the buffer layer the device exhibits superior rectifying behavior. The barrier height, ideality factor, rectification ratio, reverse saturation current and series resistance of the Schottky diode were extracted from the measured current voltage (I-V) characteristics.

  1. Growth of Vertically Aligned ZnO Nanowire Arrays Using Bilayered Metal Catalysts

    Science.gov (United States)

    2012-01-01

    12] J. P. Liu, C. X. Guo, C. M. Li et al., “Carbon-decorated ZnO nanowire array: a novel platform for direct electrochemistry of enzymes and...cited. Vertically aligned, high-density ZnO nanowires (NWs) were grown for the first time on c-plane sapphire using binary alloys of Ni/Au or Cu/Au as...deleterious to the ZnO NW array growth. Significant improvement of the Au adhesion on the substrate was noted, opening the potential for direct

  2. Preparation and Photoluminescence of ZnO Comb-Like Structure and Nanorod Arrays

    Science.gov (United States)

    Yin, Song; Chen, Yi-qing; Su, Yong; Zhou, Qing-tao

    2007-06-01

    A large quantity of Zinc oxide (ZnO) comb-like structure and high-density well-aligned ZnO nanorod arrays were prepared on silicon substrate via thermal evaporation process without any catalyst. The morphology, growth mechanism, and optical properties of the both structures were investigated using XRD, SEM, TEM and PL. The resulting comb-teeth, with a diameter about 20 nm, growing along the [0001] direction have a well-defined epitaxial relationship with the comb ribbon. The ZnO nanorod arrays have a diameter about 200 nm and length up to several micrometers growing approximately vertical to the Si substrate. A ZnO film was obtained before the nanorods growth. A growth model is proposed for interpreting the growth mechanism of comb-like zigzag-notch nanostructure. Room temperature photoluminescence measurements under excitation wavelength of 325 nm showed that the ZnO comb-like nanostructure has a weak UV emission at around 384 nm and a strong green emission around 491 nm, which correspond to a near band-edge transition and the singly ionized oxygen vacancy, respectively. In contrast, a strong and sharp UV peak and a weak green peak was obtained from the ZnO nanorod arrays.

  3. Growth of high-aspect ratio horizontally-aligned ZnO nanowire arrays.

    Science.gov (United States)

    Soman, Pranav; Darnell, Max; Feldman, Marc D; Chen, Shaochen

    2011-08-01

    A method of fabricating horizontally-aligned zinc-oxide (ZnO) nanowire (NW) arrays with full control over the width and length is demonstrated. SEM images reveal the hexagonal structure typical of zinc oxide NWs. Arrays of high-aspect ratio horizontal ZnO NWs are fabricated by making use of the lateral overgrowth from dot patterns created by electron beam lithography (EBL). An array of patterned wires are lifted off and transferred to a flexible PDMS substrate with possible applications in several key nanotechnology areas.

  4. ZnO nano-array-based EGFET biosensor for glucose detection

    Science.gov (United States)

    Qi, Junjie; Zhang, Huihui; Ji, Zhaoxia; Xu, Minxuan; Zhang, Yue

    2015-06-01

    Electrochemical biosensors are normally based on enzymatic catalysis of a reaction that produces or consumes electrons and the sensing membranes dominate the performance. In this work, ZnO nano-array-based EGFETs were fabricated for pH and glucose detection. The ZnO nano-arrays prepared via low-temperature hydrothermal method were well-aligned, with an average length of 2 μm and diameter of 100-150 nm, and have a typical hexagonal wurtzite structure. The sensor performed with a sensitivity of 45 mV/pH and response time of about 6-7 s from pH = 4-12. UV irradiation can improve the Vref response as a result of the formation of a depletion region at the surface of ZnO nanomaterials. Due to its high specific surface area, the ZnO nano-array EGFET sensor showed a sensitivity of -0.395 mV/μM to the glucose detection in a concentration range between 20 and 100 μM. These EGFET glucose biosensors demonstrate a low detectable concentration (20 μM) with good linearity, therefore may be used to detect glucose in saliva and tears at much lower concentrations than that in blood.

  5. Growth of Horizonatal ZnO Nanowire Arrays on Any Substrate

    KAUST Repository

    Qin, Yong; Yang, Rusen; Wang, Zhong Lin

    2008-01-01

    A general method is presented for growing laterally aligned and patterned ZnO nanowire (NW) arrays on any substrate as long as it is flat. The orientation control is achieved using the combined effect from ZnO seed layer and the catalytically

  6. Room temperature synthesis and optical properties of small diameter (5 nm) ZnO nanorod arrays.

    Science.gov (United States)

    Cho, Seungho; Jang, Ji-Wook; Lee, Jae Sung; Lee, Kun-Hong

    2010-10-01

    We report a simple wet-chemical synthesis of ∼5 nm diameter ZnO nanorod arrays at room temperature (20 °C) and normal atmospheric pressure (1 atm) and their optical properties. They were single crystalline in nature, and grew in the [001] direction. These small diameter ZnO nanorod arrays can also be synthesized at 0 °C. Control experiments were also conducted. On the basis of the results, we propose a mechanism for the spontaneous growth of the small diameter ZnO structures. The optical properties of the 5 nm diameter ZnO nanorod arrays synthesized using this method were probed by UV-Visible diffuse reflectance spectroscopy. A clear blue-shift, relative to the absorption band from 50 nm diameter ZnO nanorod arrays, was attributed to the quantum confinement effects caused by the small nanocrystal size in the 5 nm diameter ZnO nanorods.

  7. Performance improvement for solution-processed high-mobility ZnO thin-film transistors

    International Nuclear Information System (INIS)

    Li Chensha; Loutfy, Rafik O; Li Yuning; Wu Yiliang; Ong, Beng S

    2008-01-01

    The fabrication technology of stable, non-toxic, transparent, high performance zinc oxide (ZnO) thin-film semiconductors via the solution process was investigated. Two methods, which were, respectively, annealing a spin-coated precursor solution and annealing a drop-coated precursor solution, were compared. The prepared ZnO thin-film semiconductor transistors have well-controlled, preferential crystal orientation and exhibit superior field-effect performance characteristics. But the ZnO thin-film transistor (TFT) fabricated by annealing a drop-coated precursor solution has a distinctly elevated linear mobility, which further approaches the saturated mobility, compared with that fabricated by annealing a spin-coated precursor solution. The performance of the solution-processed ZnO TFT was further improved when substituting the spin-coating process by the drop-coating process

  8. Performance improvement for solution-processed high-mobility ZnO thin-film transistors

    Energy Technology Data Exchange (ETDEWEB)

    Li Chensha; Loutfy, Rafik O [Department of Chemical Engineering, McMaster University, 1280 Main Street West, Hamilton, Ontario L8S 4L7 (Canada); Li Yuning; Wu Yiliang; Ong, Beng S [Materials Design and Integration Laboratory, Xerox Research Centre of Canada, 2660 Speakman Drive, Mississauga, Ontario L5K 2L1 (Canada)], E-mail: lichnsa@163.com

    2008-06-21

    The fabrication technology of stable, non-toxic, transparent, high performance zinc oxide (ZnO) thin-film semiconductors via the solution process was investigated. Two methods, which were, respectively, annealing a spin-coated precursor solution and annealing a drop-coated precursor solution, were compared. The prepared ZnO thin-film semiconductor transistors have well-controlled, preferential crystal orientation and exhibit superior field-effect performance characteristics. But the ZnO thin-film transistor (TFT) fabricated by annealing a drop-coated precursor solution has a distinctly elevated linear mobility, which further approaches the saturated mobility, compared with that fabricated by annealing a spin-coated precursor solution. The performance of the solution-processed ZnO TFT was further improved when substituting the spin-coating process by the drop-coating process.

  9. Highly transparent and UV-resistant superhydrophobic SiO2-coated ZnO nanorod arrays

    KAUST Repository

    Gao, Yangqin

    2014-02-26

    Highly transparent and UV-resistant superhydrophobic arrays of SiO 2-coated ZnO nanorods are prepared in a sequence of low-temperature (<150 C) steps on both glass and thin sheets of PET (2 × 2 in. 2), and the superhydrophobic nanocomposite is shown to have minimal impact on solar cell device performance under AM1.5G illumination. Flexible plastics can serve as front cell and backing materials in the manufacture of flexible displays and solar cells. © 2014 American Chemical Society.

  10. Comparative study of ZnO nanorods and thin films for chemical and biosensing applications and the development of ZnO nanorods based potentiometric strontium ion sensor

    Science.gov (United States)

    Khun, K.; Ibupoto, Z. H.; Chey, C. O.; Lu, Jun.; Nur, O.; Willander, M.

    2013-03-01

    In this study, the comparative study of ZnO nanorods and ZnO thin films were performed regarding the chemical and biosensing properties and also ZnO nanorods based strontium ion sensor is proposed. ZnO nanorods were grown on gold coated glass substrates by the hydrothermal growth method and the ZnO thin films were deposited by electro deposition technique. ZnO nanorods and thin films were characterised by field emission electron microscopy [FESEM] and X-ray diffraction [XRD] techniques and this study has shown that the grown nanostructures are highly dense, uniform and exhibited good crystal quality. Moreover, transmission electron microscopy [TEM] was used to investigate the quality of ZnO thin film and we observed that ZnO thin film was comprised of nano clusters. ZnO nanorods and thin films were functionalised with selective strontium ionophore salicylaldehyde thiosemicarbazone [ST] membrane, galactose oxidase, and lactate oxidase for the detection of strontium ion, galactose and L-lactic acid, respectively. The electrochemical response of both ZnO nanorods and thin films sensor devices was measured by using the potentiometric method. The strontium ion sensor has exhibited good characteristics with a sensitivity of 28.65 ± 0.52 mV/decade, for a wide range of concentrations from 1.00 × 10-6 to 5.00 × 10-2 M, selectivity, reproducibility, stability and fast response time of 10.00 s. The proposed strontium ion sensor was used as indicator electrode in the potentiometric titration of strontium ion versus ethylenediamine tetra acetic acid [EDTA]. This comparative study has shown that ZnO nanorods possessed better performance with high sensitivity and low limit of detection due to high surface area to volume ratio as compared to the flat surface of ZnO thin films.

  11. ZnO nanorod array solid phase micro-extraction fiber coating: fabrication and extraction capability

    International Nuclear Information System (INIS)

    Wang Dan; Zhang Zhuomin; Li Tiemei; Zhang Lan; Chen Guonan; Luo Lin

    2009-01-01

    In this paper, a ZnO nanorod array has been introduced as a coating to the headspace solid phase micro-extraction (HSSPME) field. The coating shows good extraction capability for volatile organic compounds (VOCs) by use of BTEX as a standard and can be considered suitable for sampling trace and small molecular VOC targets. In comparison with the randomly oriented ZnO nanorod HSSPME coating, ZnO nanorod array HSSPME fiber coating shows better extraction capability, which is attributed to the nanorod array structure of the coating. Also, this novel nanorod array coating shows good extraction selectivity to 1-propanethiol.

  12. Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

    International Nuclear Information System (INIS)

    Melikhova, O.; Čížek, J.; Lukáč, F.; Vlček, M.; Novotný, M.; Bulíř, J.; Lančok, J.; Anwand, W.; Brauer, G.; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.

    2013-01-01

    Highlights: ► Thin ZnO films and high quality ZnO crystal were electrochemically doped with hydrogen. ► Hydrogen absorbed in ZnO causes plastic deformation both in ZnO crystal and thin films. ► In ZnO crystal a sub-surface region with very high density of defects was formed. ► Moreover, plastic deformation causes specific surface modification of ZnO crystal. ► In ZnO films hydrogen-induced plastic deformation introduced defects in the whole film. -- Abstract: ZnO films with thickness of ∼80 nm were grown by pulsed laser deposition (PLD) on MgO (1 0 0) single crystal and amorphous fused silica (FS) substrates. Structural studies of ZnO films and a high quality reference ZnO single crystal were performed by slow positron implantation spectroscopy (SPIS). It was found that ZnO films exhibit significantly higher density of defects than the reference ZnO crystal. Moreover, the ZnO film deposited on MgO substrate exhibits higher concentration of defects than the film deposited on amorphous FS substrate most probably due to a dense network of misfit dislocations. The ZnO films and the reference ZnO crystal were subsequently loaded with hydrogen by electrochemical cathodic charging. SPIS characterizations revealed that absorbed hydrogen introduces new defects into ZnO

  13. Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Melikhova, O., E-mail: oksivmel@yahoo.com [Charles University in Prague, Faculty of Mathematics and Physics, V Holesovickach 2, CZ-180 00 Praha 8 (Czech Republic); Čížek, J.; Lukáč, F.; Vlček, M. [Charles University in Prague, Faculty of Mathematics and Physics, V Holesovickach 2, CZ-180 00 Praha 8 (Czech Republic); Novotný, M.; Bulíř, J.; Lančok, J. [Institute of Physics, Academy of Sciences of the Czech Republic, Na Slovance 2, 182 21 Prague (Czech Republic); Anwand, W.; Brauer, G. [Institut für Strahlenphysik, Helmholtz-Zentrum Dresden-Rossendorf, PO Box 510 119, D-01314 Dresden (Germany); Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P. [National Centre for Plasma Science and Technology, School of Physical Sciences, Glasnevin, Dublin 9 (Ireland)

    2013-12-15

    Highlights: ► Thin ZnO films and high quality ZnO crystal were electrochemically doped with hydrogen. ► Hydrogen absorbed in ZnO causes plastic deformation both in ZnO crystal and thin films. ► In ZnO crystal a sub-surface region with very high density of defects was formed. ► Moreover, plastic deformation causes specific surface modification of ZnO crystal. ► In ZnO films hydrogen-induced plastic deformation introduced defects in the whole film. -- Abstract: ZnO films with thickness of ∼80 nm were grown by pulsed laser deposition (PLD) on MgO (1 0 0) single crystal and amorphous fused silica (FS) substrates. Structural studies of ZnO films and a high quality reference ZnO single crystal were performed by slow positron implantation spectroscopy (SPIS). It was found that ZnO films exhibit significantly higher density of defects than the reference ZnO crystal. Moreover, the ZnO film deposited on MgO substrate exhibits higher concentration of defects than the film deposited on amorphous FS substrate most probably due to a dense network of misfit dislocations. The ZnO films and the reference ZnO crystal were subsequently loaded with hydrogen by electrochemical cathodic charging. SPIS characterizations revealed that absorbed hydrogen introduces new defects into ZnO.

  14. Fabrication and Characterization of Vertically Aligned ZnO Nanorod Arrays via Inverted Monolayer Colloidal Crystals Mask

    Science.gov (United States)

    Chen, Cheng; Ding, Taotao; Qi, Zhiqiang; Zhang, Wei; Zhang, Jun; Xu, Juan; Chen, Jingwen; Dai, Jiangnan; Chen, Changqing

    2018-04-01

    The periodically ordered ZnO nanorod (NR) arrays have been successfully synthesized via a hydrothermal approach on the silicon substrates by templating of the TiO2 ring deriving from the polystyrene (PS) nanosphere monolayer colloidal crystals (MCC). With the inverted MCC mask, sol-gel-derived ZnO seeds could serve as the periodic nucleation positions for the site-specific growth of ZnO NRs. The large-scale patterned arrays of single ZnO NR with good side-orientation can be readily produced. According to the experimental results, the as-integrated ZnO NR arrays showed an excellent crystal quality and optical property, very suitable for optoelectronic applications such as stimulated emitters and ZnO photonic crystal devices.

  15. Improvement of physical properties of ZnO thin films by tellurium doping

    Energy Technology Data Exchange (ETDEWEB)

    Sönmezoğlu, Savaş, E-mail: svssonmezoglu@kmu.edu.tr; Akman, Erdi

    2014-11-01

    Highlights: • We report the synthesis of tellurium-doped zinc oxide (Te–ZnO) thin films using sol–gel method. • Highly c-axis oriented Te-doped ZnO thin films were grown on FTO glasses as substrate. • 1.5% Te-doping ratio could improve the physical properties of ZnO thin films. - Abstract: This investigation addressed the structural, optical and morphological properties of tellurium incorporated zinc oxide (Te–ZnO) thin films. The obtained results indicated that Te-doped ZnO thin films exhibit an enhancement of band gap energy and crystallinity compared with non-doped films. The optical transmission spectra revealed a shift in the absorption edge toward lower wavelengths. X-ray diffraction measurement demonstrated that the film was crystallized in the hexagonal (wurtzite) phase and presented a preferential orientation along the c-axis. The XRD obtained patterns indicate that the crystallite size of the thin films, ranging from 23.9 to 49.1 nm, changed with the Te doping level. The scanning electron microscopy and atomic force microscopy results demonstrated that the grain size and surface roughness of the thin films increased as the Te concentration increased. Most significantly, we demonstrate that it is possible to control the structural, optical and morphological properties of ZnO thin films with the isoelectronic Te-incorporation level.

  16. Single-Crystal Mesoporous ZnO Thin Films Composed of Nanowalls

    KAUST Repository

    Wang, Xudong; Ding, Yong; Li, Zhou; Song, Jinhui; Wang, Zhong Lin

    2009-01-01

    This paper presents a controlled, large scale fabrication of mesoporous ZnO thin films. The entire ZnO mesoporous film is one piece of a single crystal, while high porosity made of nanowalls is present. The growth mechanism was proposed

  17. Photoluminescence of ZnO thin films deposited at various substrate temperatures

    International Nuclear Information System (INIS)

    Kao, Kuo-Sheng; Shih, Wei-Che; Ye, Wei-Tsuen; Cheng, Da-Long

    2016-01-01

    This study investigated surface acoustic wave devices with an Al/ZnO/Si structure for use in ultraviolet sensors. ZnO thin films were fabricated using a reactive radio frequency magnetron sputtering system. The substrate temperature of ZnO thin films can be varied to obtain highly crystalline properties. The surface morphologies and c-axis preferred orientation of the ZnO thin films were determined using scanning electron microscopy and X-ray diffraction. In addition, bright-field images of ZnO crystallization were investigated using a transmission electron microscope. From photoluminescence analysis, four peaks were obtained at 377.8, 384.9, 391.4, and 403.4 nm. Interdigital transducers of an aluminum electrode were fabricated on the ZnO/Si structure by using a direct current sputtering system and photolithography, combined with the lift-off method, thereby obtaining a surface acoustic wave device. Finally, frequency responses were measured using a network analyzer, and an illuminating test was adopted for the ultraviolet sensor, using a wavelength of 355 nm from a light-emitting diode. The sensitivities of the ultraviolet sensor were also discussed. - Highlights: • The ZnO/Si SAW devices exhibit the Rayleigh and Sezawa modes. • The crystalline of ZnO affects the EHP recombination and generation. • The PL spectrum of ZnO shows Gaussian fitting distributions. • The CTD_U_V is influenced by SAW types and ZnO film characteristics.

  18. Photoluminescence of ZnO thin films deposited at various substrate temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Kao, Kuo-Sheng [Department of Computer and Communication, SHU-TE University, Kaohsiung, Taiwan (China); Shih, Wei-Che [Department of Electrical Engineering, National Sun Yat-Sen University, Kaohsiung, Taiwan (China); Ye, Wei-Tsuen [Department of Computer and Communication, SHU-TE University, Kaohsiung, Taiwan (China); Cheng, Da-Long, E-mail: dlcheng@stu.edu.tw [Department of Computer and Communication, SHU-TE University, Kaohsiung, Taiwan (China)

    2016-04-30

    This study investigated surface acoustic wave devices with an Al/ZnO/Si structure for use in ultraviolet sensors. ZnO thin films were fabricated using a reactive radio frequency magnetron sputtering system. The substrate temperature of ZnO thin films can be varied to obtain highly crystalline properties. The surface morphologies and c-axis preferred orientation of the ZnO thin films were determined using scanning electron microscopy and X-ray diffraction. In addition, bright-field images of ZnO crystallization were investigated using a transmission electron microscope. From photoluminescence analysis, four peaks were obtained at 377.8, 384.9, 391.4, and 403.4 nm. Interdigital transducers of an aluminum electrode were fabricated on the ZnO/Si structure by using a direct current sputtering system and photolithography, combined with the lift-off method, thereby obtaining a surface acoustic wave device. Finally, frequency responses were measured using a network analyzer, and an illuminating test was adopted for the ultraviolet sensor, using a wavelength of 355 nm from a light-emitting diode. The sensitivities of the ultraviolet sensor were also discussed. - Highlights: • The ZnO/Si SAW devices exhibit the Rayleigh and Sezawa modes. • The crystalline of ZnO affects the EHP recombination and generation. • The PL spectrum of ZnO shows Gaussian fitting distributions. • The CTD{sub UV} is influenced by SAW types and ZnO film characteristics.

  19. Influence of surface defects in ZnO thin films on its biosensing response characteristic

    Energy Technology Data Exchange (ETDEWEB)

    Saha, Shibu; Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)

    2011-09-15

    Highly c-axis oriented zinc oxide (ZnO) thin films deposited by rf magnetron sputtering under varying processing pressure (20-50 mT) in a reactive gas mixture of argon and oxygen were studied for biosensing application. The as-deposited ZnO thin films were in a state of compressive stress having defects related to interstitial Zn and antisite oxygen. Glucose oxidase has been chosen as the model enzyme in the present study and was immobilized on the surface of ZnO thin films deposited on indium tin oxide coated Corning Glass substrate. The studies reveal a correlation between the biosensing characteristic and the presence of defects in the ZnO films. The ZnO films deposited under high pressure (50 mT) are found to be more sensitive for biosensing application due to availability of more surface area for effective immobilization of biomolecules and exhibits a suitable microenvironment with good electron transfer characteristic. The obtained results highlight the importance of desired microstate besides availability of suitable native defects in the ZnO thin film for exhibiting enhanced biosensing response.

  20. Influence of surface defects in ZnO thin films on its biosensing response characteristic

    International Nuclear Information System (INIS)

    Saha, Shibu; Gupta, Vinay

    2011-01-01

    Highly c-axis oriented zinc oxide (ZnO) thin films deposited by rf magnetron sputtering under varying processing pressure (20-50 mT) in a reactive gas mixture of argon and oxygen were studied for biosensing application. The as-deposited ZnO thin films were in a state of compressive stress having defects related to interstitial Zn and antisite oxygen. Glucose oxidase has been chosen as the model enzyme in the present study and was immobilized on the surface of ZnO thin films deposited on indium tin oxide coated Corning Glass substrate. The studies reveal a correlation between the biosensing characteristic and the presence of defects in the ZnO films. The ZnO films deposited under high pressure (50 mT) are found to be more sensitive for biosensing application due to availability of more surface area for effective immobilization of biomolecules and exhibits a suitable microenvironment with good electron transfer characteristic. The obtained results highlight the importance of desired microstate besides availability of suitable native defects in the ZnO thin film for exhibiting enhanced biosensing response.

  1. Microwave Synthesized ZnO Nanorod Arrays for UV Sensors: A Seed Layer Annealing Temperature Study.

    Science.gov (United States)

    Pimentel, Ana; Ferreira, Sofia Henriques; Nunes, Daniela; Calmeiro, Tomas; Martins, Rodrigo; Fortunato, Elvira

    2016-04-20

    The present work reports the influence of zinc oxide (ZnO) seed layer annealing temperature on structural, optical and electrical properties of ZnO nanorod arrays, synthesized by hydrothermal method assisted by microwave radiation, to be used as UV sensors. The ZnO seed layer was produced using the spin-coating method and several annealing temperatures, ranging from 100 to 500 °C, have been tested. X-ray diffraction (XRD), scanning electron microscopy (SEM), atomic force microscopy (AFM) and spectrophotometry measurements have been used to investigate the structure, morphology, and optical properties variations of the produced ZnO nanorod arrays regarding the seed layer annealing temperatures employed. After the growth of ZnO nanorod arrays, the whole structure was tested as UV sensors, showing an increase in the sensitivity with the increase of seed layer annealing temperature. The UV sensor response of ZnO nanorod arrays produced with the seed layer annealed temperature of 500 °C was 50 times superior to the ones produced with a seed layer annealed at 100 °C.

  2. Annealing effect on the photoluminescence properties of ZnO nanorod array prepared by a PLD-assistant wet chemical method

    International Nuclear Information System (INIS)

    Wei Sufeng; Lian Jianshe; Wu Hua

    2010-01-01

    Well-aligned ZnO nanorod arrays were synthesized by a wet chemical method on the glass substrate with ZnO thin film as seed layer prepared by pulsed laser deposition. The effect of annealing temperature on the luminescence characteristics was investigated. As the annealing temperature increased, the photoluminescence properties show a general enhancing tendency. The nanorod array with high ultraviolet emission and negligible visible light emission (designated by the photoluminescence intensity ratio of ultraviolet to visible emission of 66.4) is obtained by annealing the sample at 700 deg. C for 1 h. Based on the results of X-ray photoelectron spectroscopy and photoluminescence spectra, the mechanisms of visible emission were discussed. - Research Highlights: → ZnO nanorod array with good crystallography, low defects concentration and good optical property was obtained after annealed at 700 deg. C for 1 h. → The transition from the conduction band to the O i level may be responsible for the yellow-green emission. → The yellow emission may originate from the presence of Zn(OH) 2 on the surface or the band transition from conduction band to V o Zn i level. → The transition from the Zn i level to the level should produce an orange emission or an orange-red emission.

  3. Controllable growth and characterization of highly aligned ZnO nanocolumnar thin films

    Energy Technology Data Exchange (ETDEWEB)

    Onuk, Zuhal [Department of Physics, Recep Tayyip Erdogan University, Rize, 53100 (Turkey); Department of Materials Science and Engineering, University of Delaware, Newark, DE, 19716 (United States); Rujisamphan, Nopporn [Nanoscience and Nanotechnology Graduate Program, Faculty of Science, King Mongkut’s University of Technology Thonburi, 10140, Bangkok (Thailand); Theoretical and Computational Science Center (TaCS), Faculty of Science, King Mongkut’s University of Technology Thonburi, Bangkok 10140 (Thailand); Murray, Roy [Department of Physics and Astronomy, University of Delaware, Newark, DE, 19716 (United States); Bah, Mohamed [Department of Materials Science and Engineering, University of Delaware, Newark, DE, 19716 (United States); Tomakin, Murat [Department of Physics, Recep Tayyip Erdogan University, Rize, 53100 (Turkey); Shah, S.Ismat, E-mail: ismat@udel.edu [Department of Materials Science and Engineering, University of Delaware, Newark, DE, 19716 (United States); Department of Physics and Astronomy, University of Delaware, Newark, DE, 19716 (United States)

    2017-02-28

    Graphical abstract: Scanning electron micrographs of the top view surfaces (left column) and cross sections of sputtered ZnO thin films prepared at various Ar:O{sub 2} ratios: (a) and (b) 10:0, (c) and (d) 7.5:2.5, (e) and (f) 5:5, (g) and (h) 2.5:7.5. - Highlights: • Nanocolumnar ZnO films were prepared by controlling the argon-oxygen sputtering gas ratio. • Oxygen partial pressure affects the band gap alignment of the ZnO films. • Optical transmission spectroscopy and XPS were used to study band gap shifts. - Abstract: We investigated the effects of growth conditions during magnetron sputtering on the structural, morphological, and optical properties of nanostructured ZnO thin films. Undoped ZnO thin films are deposited onto p-type Si (100) and corning 7059 glass substrates by RF magnetron sputtering using a ZnO target in combination with various Ar-O{sub 2} sputtering gas mixtures at room temperature. The effect of the partial pressure of oxygen on the morphology of ZnO thin film structure and band alignment were investigated. Thickness, and therefore the growth rate of the samples measured from the cross-sectional SEM micrographs, is found to be strongly correlated with the oxygen partial pressure in the sputtering chamber. The optical transmittance spectrometry results show that the absorption edge shifts towards the longer wavelength at higher oxygen partial pressure. X-ray photoelectron spectroscopy (XPS) used for determining the surface chemical structure and valence band offsets show that conduction band can be controlled by changing the sputtering atmosphere.

  4. Preparation and electrochemical performance of bramble-like ZnO array as anode materials for lithium-ion batteries

    International Nuclear Information System (INIS)

    Yan, Junfeng; Wang, Gang; Wang, Hui; Zhang, Zhiyong; Ruan, Xiongfei; Zhao, Wu; Yun, Jiangni; Xu, Manzhang

    2015-01-01

    A bramble-like ZnO array with a special three-dimensional (3D) nanostructure was successfully fabricated on Zn foil through a facile two-step hydrothermal process. A possible growth mechanism of the bramble-like ZnO array was proposed. In the first step of hydrothermal process, the crystal nucleus of Zn(OH) 4 2− generated by the zinc atoms and OH − ions fold together preferentially along the positive polar (0001) to form the needle-like ZnO array. In the second step of hydrothermal process, the crystal nuclei of Zn(OH) 4 2− adjust their posture to keep their c-axes vertical to the perching sites due to the sufficient environmental force and further grow preferentially along the (0001) direction so as to form bramble-like ZnO array. The electrochemical properties of the needle- and bramble-like ZnO arrays as anode materials for lithium-ion batteries were investigated and compared. The results show that the bramble-like ZnO material exhibits much better lithium storage properties than the needle-like ZnO sample. Reasons for the enhanced electrochemical performance of the bramble-like ZnO material were investigated

  5. Improved ITO thin films for photovoltaic applications with a thin ZnO layer by sputtering

    International Nuclear Information System (INIS)

    Herrero, J.; Guillen, C.

    2004-01-01

    The improvement of the optical and electrical characteristics of indium tin oxide (ITO) layers is pursued to achieve a higher efficiency in its application as frontal electrical contacts in thin film photovoltaic devices. In order to take advantage of the polycrystalline structure of ZnO films as growth support, the properties of ITO layers prepared at room temperature by sputtering onto bare and ZnO-coated substrates have been analyzed using X-ray diffraction, optical and electrical measurements. It has been found that by inserting a thin ZnO layer, the ITO film resistivity can be reduced as compared to that of a single ITO film with similar optical transmittance. The electrical quality improvement is related to ITO grain growth enhancement onto the polycrystalline ZnO underlayer

  6. Photoelectrocatalytic activity of a hydrothermally grown branched Zno nanorod-array electrode for paracetamol degradation.

    Science.gov (United States)

    Lin, Chin Jung; Liao, Shu-Jun; Kao, Li-Cheng; Liou, Sofia Ya Hsuan

    2015-06-30

    Hierarchical branched ZnO nanorod (B-ZnR) arrays as an electrode for efficient photoelectrocatalytic degradation of paracetamol were grown on fluorine-doped tin oxide substrates using a solution route. The morphologic and structural studies show the ZnO trunks are single-crystalline hexagonal wurtzite ZnO with a [0001] growth direction and are densely covered by c-axis-oriented ZnO branches. The obvious enhancement in photocurrent response of the B-ZnR electrode was obtained than that in the ZnO nanoparticle (ZnO NP) electrode. For the photoelectrocatalytic degradation of paracetamol in 20 h, the conversion fraction of the drug increased from 32% over ZnO NP electrode to 62% over B-ZnR arrays with about 3-fold increase in initial reaction rate. The light intensity-dependent photoelectrocatalytic experiment indicated that the superior performance over the B-ZnR electrode was mainly ascribed to the increased specific surface area without significantly sacrificing the charge transport and pollutant diffusion efficiencies. Two aromatic intermediate compounds were observed and eventually converted into harmless carboxylic acids and ammonia. Hierarchical tree-like ZnO arrays can be considered effective alternatives to improve photoelectro degradation rates without the need for expensive additives. Copyright © 2015 Elsevier B.V. All rights reserved.

  7. Wafer-Scale High-Throughput Ordered Growth of Vertically Aligned ZnO Nanowire Arrays

    KAUST Repository

    Wei, Yaguang; Wu, Wenzhuo; Guo, Rui; Yuan, Dajun; Das, Suman; Wang, Zhong Lin

    2010-01-01

    -synthesized morphology. The development of textured ZnO seed layers for replacing single crystalline GaN and ZnO substrates extends the large-scale fabrication of vertically aligned ZnO NW arrays on substrates of other materials, such as polymers, Si, and glass

  8. Recent advances in ZnO nanostructures and thin films for biosensor applications: Review

    International Nuclear Information System (INIS)

    Arya, Sunil K.; Saha, Shibu; Ramirez-Vick, Jaime E.; Gupta, Vinay; Bhansali, Shekhar; Singh, Surinder P.

    2012-01-01

    Graphical abstract: ZnO nanostructures have shown binding of biomolecules in desired orientation with improved conformation and high biological activity, resulting in enhanced sensing characteristics. Furthermore, their compatibility with complementary metal oxide semiconductor technology for constructing integrated circuits makes them suitable candidate for future small integrated biosensor devices. This review highlights various approaches to synthesize ZnO nanostructures and thin films, and their applications in biosensor technology. Highlights: ► This review highlights various approaches to synthesize ZnO nanostructures and thin films. ► Article highlights the importance of ZnO nanostructures as biosensor matrix. ► Article highlights the advances in various biosensors based on ZnO nanostructures. ► Article describes the potential of ZnO based biosensor for new generation healthcare devices. - Abstract: Biosensors have shown great potential for health care and environmental monitoring. The performance of biosensors depends on their components, among which the matrix material, i.e., the layer between the recognition layer of biomolecule and transducer, plays a crucial role in defining the stability, sensitivity and shelf-life of a biosensor. Recently, zinc oxide (ZnO) nanostructures and thin films have attracted much interest as materials for biosensors due to their biocompatibility, chemical stability, high isoelectric point, electrochemical activity, high electron mobility, ease of synthesis by diverse methods and high surface-to-volume ratio. ZnO nanostructures have shown the binding of biomolecules in desired orientations with improved conformation and high biological activity, resulting in enhanced sensing characteristics. Furthermore, compatibility with complementary metal oxide semiconductor technology for constructing integrated circuits makes ZnO nanostructures suitable candidate for future small integrated biosensor devices. This review

  9. Recent advances in ZnO nanostructures and thin films for biosensor applications: Review

    Energy Technology Data Exchange (ETDEWEB)

    Arya, Sunil K., E-mail: sunilarya333@gmail.com [Bioelectronics Program, Institute of Microelectronics, A-Star 11 Science Park Road, Singapore Science Park II, Singapore 117685 (Singapore); Saha, Shibu [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India); Ramirez-Vick, Jaime E. [Engineering Science and Materials Department, University of Puerto Rico, Mayaguez, PR 00681 (United States); Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi 110007 (India); Bhansali, Shekhar [Department of Electrical and Computer Engineering, Florida International University, Miami, FL (United States); Singh, Surinder P., E-mail: singh.uprm@gmail.com [National Physical Laboratory, Dr K.S. Krishnan Marg, New Delhi 110012 (India)

    2012-08-06

    Graphical abstract: ZnO nanostructures have shown binding of biomolecules in desired orientation with improved conformation and high biological activity, resulting in enhanced sensing characteristics. Furthermore, their compatibility with complementary metal oxide semiconductor technology for constructing integrated circuits makes them suitable candidate for future small integrated biosensor devices. This review highlights various approaches to synthesize ZnO nanostructures and thin films, and their applications in biosensor technology. Highlights: Black-Right-Pointing-Pointer This review highlights various approaches to synthesize ZnO nanostructures and thin films. Black-Right-Pointing-Pointer Article highlights the importance of ZnO nanostructures as biosensor matrix. Black-Right-Pointing-Pointer Article highlights the advances in various biosensors based on ZnO nanostructures. Black-Right-Pointing-Pointer Article describes the potential of ZnO based biosensor for new generation healthcare devices. - Abstract: Biosensors have shown great potential for health care and environmental monitoring. The performance of biosensors depends on their components, among which the matrix material, i.e., the layer between the recognition layer of biomolecule and transducer, plays a crucial role in defining the stability, sensitivity and shelf-life of a biosensor. Recently, zinc oxide (ZnO) nanostructures and thin films have attracted much interest as materials for biosensors due to their biocompatibility, chemical stability, high isoelectric point, electrochemical activity, high electron mobility, ease of synthesis by diverse methods and high surface-to-volume ratio. ZnO nanostructures have shown the binding of biomolecules in desired orientations with improved conformation and high biological activity, resulting in enhanced sensing characteristics. Furthermore, compatibility with complementary metal oxide semiconductor technology for constructing integrated circuits makes ZnO

  10. ZnO nanorod arrays grown under different pressures and their photoluminescence properties

    Energy Technology Data Exchange (ETDEWEB)

    Meng Xiuqing [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China); Graduate School of the Chinese Academy of Sciences (China); Zhao Dongxu [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China)]. E-mail: dxzhao2000@yahoo.com.cn; Shen Dezhen [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China); Zhang Jiying [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China); Li Binghui [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China); Wang Xiaohua [National Key Laboratory of High Power Semiconductor Laser, Changchun University of Science and technology, 7089 Weixing Road Changchun (China); Fan Xiwu [Key Laboratory of Excited State Processes, Changchun Institute of Optics, Fine Mechanics and Physics, Chinese Academy of Sciences, 16 East Nan-Hu Road, Open Economic ZoneChangchun 130033 (China)

    2007-01-15

    The ZnO nanorod arrays were synthesized via a simple vapor deposition method on Si (1 1 1) substrates at a low growth temperature of 520 deg. C. By selecting different source materials under different growth pressures, well-aligned hexagonal-shaped ZnO nanorod arrays were obtained under both conditions. X-ray diffraction (XRD) analysis confirmed the nanorods are c-axis orientated. Selected area electron diffraction (SAED) and transmission electron microscopy (TEM) analysis demonstrated the individual nanorod is single crystal. Photoluminescence (PL) analyses show the superior optical properties of the nanorod arrays.

  11. ZnO nanorod arrays grown under different pressures and their photoluminescence properties

    International Nuclear Information System (INIS)

    Meng Xiuqing; Zhao Dongxu; Shen Dezhen; Zhang Jiying; Li Binghui; Wang Xiaohua; Fan Xiwu

    2007-01-01

    The ZnO nanorod arrays were synthesized via a simple vapor deposition method on Si (1 1 1) substrates at a low growth temperature of 520 deg. C. By selecting different source materials under different growth pressures, well-aligned hexagonal-shaped ZnO nanorod arrays were obtained under both conditions. X-ray diffraction (XRD) analysis confirmed the nanorods are c-axis orientated. Selected area electron diffraction (SAED) and transmission electron microscopy (TEM) analysis demonstrated the individual nanorod is single crystal. Photoluminescence (PL) analyses show the superior optical properties of the nanorod arrays

  12. Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

    International Nuclear Information System (INIS)

    Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon; Fu, Dejun; Yoon, Hyungdo

    2011-01-01

    The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

  13. Improved electrical conduction properties in unintentionally-doped ZnO thin films treated by rapid thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Youngmin; Lee, Choeun; Shim, Eunhee; Jung, Eiwhan; Lee, Jinyong; Kim, Deukyoung; Lee, Sejoon [Dongguk University-Seoul, Seoul (Korea, Republic of); Fu, Dejun [Wuhan University, Wuhan (China); Yoon, Hyungdo [Korea Electronics Technology Institute, Seongnam (Korea, Republic of)

    2011-10-15

    The effects of thermal treatments on the electrical conduction properties for the unintentionally doped ZnO thin films were investigated. Despite the decreased carrier density in the annealed ZnO thin films, the conductivity was increased because the contribution of the effective carrier mobility to the conductivity of the unintentionally-doped ZnO thin films is greater than that of the carrier density. The resistivity exponentially decreased with increasing RTA temperature, and this result was confirmed to come from the enhanced effective carrier-mobility, which originated from the increased crystallite size in the annealed ZnO thin films.

  14. Self-assembly and optical properties of patterned ZnO nanodot arrays

    International Nuclear Information System (INIS)

    Song Yijian; Zheng Maojun; Ma Li

    2007-01-01

    Patterned ZnO nanodot (ND) arrays and a ND-cavity microstructure were realized on an anodic alumina membrane (AAM) surface through a spin-coating sol-gel process, which benefits from the morphology and localized negative charge surface of AAM as well as the optimized sol concentration. The growth mechanism is believed to be a self-assembly process. This provides a simple approach to fabricate semiconductor quantum dot (QD) arrays and a QD-cavity system with its advantage in low cost and mass production. Strong ultra-violet emission, a multi-phonon process, and its special structure-related properties were observed in the patterned ZnO ND arrays

  15. Zinc Vacancy-Induced Room-Temperature Ferromagnetism in Undoped ZnO Thin Films

    Directory of Open Access Journals (Sweden)

    Hongtao Ren

    2012-01-01

    Full Text Available Undoped ZnO thin films are prepared by polymer-assisted deposition (PAD and treated by postannealing at different temperatures in oxygen or forming gases (95%  Ar+5% H2. All the samples exhibit ferromagnetism at room temperature (RT. SQUID and positron annihilation measurements show that post-annealing treatments greatly enhance the magnetizations in undoped ZnO samples, and there is a positive correlation between the magnetization and zinc vacancies in the ZnO thin films. XPS measurements indicate that annealing also induces oxygen vacancies that have no direct relationship with ferromagnetism. Further analysis of the results suggests that the ferromagnetism in undoped ZnO is induced by Zn vacancies.

  16. Annealing impact on the structural and photoluminescence properties of ZnO thin films on Ag substrates

    International Nuclear Information System (INIS)

    Xu, Linhua; Zheng, Gaige; Lai, Min; Pei, Shixin

    2014-01-01

    Graphical abstract: The Gaussian fitting indicates that the PL spectra of the ZnO thin films include four emission peaks which are centered at 380, 520, 570 and 610 nm, respectively. The ZnO thin film deposited on an Ag substrate shows a stronger green emission and a weaker UV emission than the ZnO thin film directly deposited on a Si substrate annealed at 400 °C. With the rise of annealing temperature, the visible emission intensity and wavelength are largely changed. Highlights: • ZnO thin films have been prepared on Ag substrates by sol–gel method. • The Ag substrates have a great effect on the photoluminescence of ZnO thin films. • All the films exhibit three visible emission bands including green, yellow and red. • Annealing causes a large change of the visible emission intensity and wavelength. -- Abstract: In this work, ZnO thin films were prepared by sol–gel method on Ag substrates. The structural and optical properties of the films annealed at different temperatures were analyzed by X-ray diffraction (XRD), scanning electron microscopy (SEM) and photoluminescence, respectively. The results of XRD showed that all the ZnO thin films had a wurtzite phase and were preferentially oriented along the c-axis direction. The sample annealed at 400 °C exhibited better crystalline quality than the ZnO thin film directly deposited on a Si substrate annealed at the same temperature. The photoluminescence spectra showed that ZnO thin films had an ultraviolet emission band and three visible emission bands including green, yellow and red band. The sample annealed at 400 °C exhibited a stronger green emission and a weaker ultraviolet emission compared with the ZnO thin film deposited on a Si substrate annealed at the same temperature. The difference of the luminescence properties was thought to be originated from different substrates. As for the ZnO films on Ag substrates, the increase of annealing temperature led to different changes of visible emissions

  17. Preparation and characterization of ALD deposited ZnO thin films studied for gas sensors

    Energy Technology Data Exchange (ETDEWEB)

    Boyadjiev, S.I., E-mail: boiajiev@gmail.com [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Georgi Nadjakov Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee Blvd., 1784 Sofia (Bulgaria); Georgieva, V. [Georgi Nadjakov Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee Blvd., 1784 Sofia (Bulgaria); Yordanov, R. [Department of Microelectronics, Technical University of Sofia, 8 Kliment Ohridski Blvd., 1756 Sofia (Bulgaria); Raicheva, Z. [Georgi Nadjakov Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee Blvd., 1784 Sofia (Bulgaria); Szilágyi, I.M. [MTA-BME Technical Analytical Chemistry Research Group, Szent Gellért tér 4, Budapest, H-1111 (Hungary); Budapest University of Technology and Economics, Department of Inorganic and Analytical Chemistry, Szent Gellért tér 4, Budapest, H-1111 (Hungary)

    2016-11-30

    Highlights: • For the first time the gas sensing towards NO{sub 2} of very thin ALD ZnO films is studied. • The very thin ALD ZnO films showed excellent sensitivity to NO{sub 2} at room temperature. • These very thin film ZnO-based QCM sensors very well register even low concentrations. • The sensors have fully reversible sorption and are able to be recovered in short time. • Described fast and cost-effective ALD deposition of ZnO thin films for QCM gas sensor. - Abstract: Applying atomic layer deposition (ALD), very thin zinc oxide (ZnO) films were deposited on quartz resonators, and their gas sensing properties were studied using the quartz crystal microbalance (QCM) method. The gas sensing of the ZnO films to NO{sub 2} was tested in the concentration interval between 10 and 5000 ppm. On the basis of registered frequency change of the QCM, for each concentration the sorbed mass was calculated. Further characterization of the films was carried out by various techniques, i.e. by SEM-EDS, XRD, ellipsometry, and FTIR spectroscopy. Although being very thin, the films were gas sensitive to NO{sub 2} already at room temperature and could register very well as low concentrations as 100 ppm, while the sorption was fully reversible. Our results for very thin ALD ZnO films show that the described fast, simple and cost-effective technology could be implemented for producing gas sensors working at room temperature and being capable to detect in real time low concentrations of NO{sub 2}.

  18. Growth of ZnO nanotube arrays and nanotube based piezoelectric nanogenerators

    KAUST Repository

    Xi, Yi; Song, Jinhui; Xu, Sheng; Yang, Rusen; Gao, Zhiyuan; Hu, Chenguo; Wang, Zhong Lin

    2009-01-01

    We present a systematic study of the growth of hexagonal ZnO nanotube arrays using a solution chemical method by varying the growth temperature (<100 °C), time and solution concentration. A piezoelectric nanogenerator using the as-grown ZnO nanotube arrays has been demonstrated for the first time. The nanogenerator gives an output voltage up to 35 mV. The detailed profile of the observed electric output is understood based on the calculated piezoelectric potential in the nanotube with consideration of the Schottky contact formed between the metal tip and the nanotube; and the mechanism agrees with that proposed for nanowire based nanogenerator. Our study shows that ZnO nanotubes can also be used for harvesting mechanical energy. © 2009 The Royal Society of Chemistry.

  19. Third generation biosensing matrix based on Fe-implanted ZnO thin film

    Science.gov (United States)

    Saha, Shibu; Gupta, Vinay; Sreenivas, K.; Tan, H. H.; Jagadish, C.

    2010-09-01

    Third generation biosensor based on Fe-implanted ZnO (Fe-ZnO) thin film has been demonstrated. Implantation of Fe in rf-sputtered ZnO thin film introduces redox center along with shallow donor level and thereby enhance its electron transfer property. Glucose oxidase (GOx), chosen as model enzyme, has been immobilized on the surface of the matrix. Cyclic voltammetry and photometric assay show that the prepared bioelectrode, GOx/Fe-ZnO/ITO/Glass is sensitive to the glucose concentration with enhanced response of 0.326 μA mM-1 cm-2 and low Km of 2.76 mM. The results show promising application of Fe-implanted ZnO thin film as an attractive matrix for third generation biosensing.

  20. Third generation biosensing matrix based on Fe-implanted ZnO thin film

    International Nuclear Information System (INIS)

    Saha, Shibu; Gupta, Vinay; Sreenivas, K.; Tan, H. H.; Jagadish, C.

    2010-01-01

    Third generation biosensor based on Fe-implanted ZnO (Fe-ZnO) thin film has been demonstrated. Implantation of Fe in rf-sputtered ZnO thin film introduces redox center along with shallow donor level and thereby enhance its electron transfer property. Glucose oxidase (GOx), chosen as model enzyme, has been immobilized on the surface of the matrix. Cyclic voltammetry and photometric assay show that the prepared bioelectrode, GOx/Fe-ZnO/ITO/Glass is sensitive to the glucose concentration with enhanced response of 0.326 μA mM -1 cm -2 and low Km of 2.76 mM. The results show promising application of Fe-implanted ZnO thin film as an attractive matrix for third generation biosensing.

  1. Cu2ZnSn(S,Se)4 from CuxSnSy nanoparticle precursors on ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Kavalakkatt, Jaison; Lin, Xianzhong; Kornhuber, Kai; Kusch, Patryk; Ennaoui, Ahmed; Reich, Stephanie; Lux-Steiner, Martha Ch.

    2013-01-01

    Solar cells with Cu 2 ZnSnS 4 absorber thin films have a potential for high energy conversion efficiencies with earth-abundant and non-toxic elements. In this work the formation of CZTSSe from Cu x SnS y nanoparticles (NPs) deposited on ZnO nanorod (NR) arrays as precursors for zinc is investigated. The NPs are prepared using a chemical route and are dispersed in toluene. The ZnO NRs are grown on fluorine doped SnO 2 coated glass substrates by electro deposition method. A series of samples are annealed at different temperatures between 300 °C and 550 °C in selenium containing argon atmosphere. To investigate the products of the reaction between the precursors the series is analyzed by means of X-ray diffraction (XRD) and Raman spectroscopy. The morphology is recorded by scanning electron microscopy (SEM) images of broken cross sections. The XRD measurements and the SEM images show the disappearing of ZnO NRs with increasing annealing temperature. Simultaneously the XRD and Raman measurements show the formation of CZTSSe. The formation of secondary phases and the optimum conditions for the preparation of CZTSSe is discussed. - Highlights: ► Cu x SnS y nanoparticles are deposited on ZnO nanorod arrays. ► Samples are annealed at different temperatures (300–550 °C) in Se/Ar-atmosphere. ► Raman spectroscopy, X-ray diffraction and electron microscopy are performed. ► ZnO disappears with increasing annealing temperature. ► With increasing temperature Cu x SnS y and ZnO form Cu 2 ZnSn(S,Se) 4

  2. Piezoelectric Nanogenerator Using p-Type ZnO Nanowire Arrays

    KAUST Repository

    Lu, Ming-Pei

    2009-03-11

    Using phosphorus-doped ZnO nanowire (NW) arrays grown on silicon substrate, energy conversion using the p-type ZnO NWs has been demonstrated for the first time. The p-type ZnO NWs produce positive output voltage pulses when scanned by a conductive atomic force microscope (AFM) in contact mode. The output voltage pulse is generated when the tip contacts the stretched side (positive piezoelectric potential side) of the NW. In contrast, the n-type ZnO NW produces negative output voltage when scanned by the AFM tip, and the output voltage pulse is generated when the tip contacts the compressed side (negative potential side) of the NW. In reference to theoretical simulation, these experimentally observed phenomena have been systematically explained based on the mechanism proposed for a nanogenerator. © 2009 American Chemical Society.

  3. Effects of thermal annealing temperature and duration on hydrothermally grown ZnO nanorod arrays

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, X.Q.; Kim, C.R.; Lee, J.Y.; Shin, C.M.; Heo, J.H.; Leem, J.Y. [Department of Nano Systems Engineering, Center for Nano Manufacturing, Inje University, Obang-dong, Gimhae, Gyeongnam 621-749 (Korea, Republic of); Ryu, H. [Department of Nano Systems Engineering, Center for Nano Manufacturing, Inje University, Obang-dong, Gimhae, Gyeongnam 621-749 (Korea, Republic of)], E-mail: hhryu@inje.ac.kr; Chang, J.H. [Major of Nano Semiconductor, Korea Maritime University, 1 Dongsam-dong, Yeongdo-Ku, Busan 606-791 (Korea, Republic of); Lee, H.C. [Department of Mechatronics Engineering, Korea Maritime University, 1 Dongsam-dong, Yeongdo-Ku, Busan 606-791 (Korea, Republic of); Son, C.S. [Department of Electronic Materials Engineering, Silla University, Gwaebeop-dong, Sasang-gu, Busan 617-736 (Korea, Republic of); Shin, B.C.; Lee, W.J. [Department of Nano Engineering, Dong-Eui University, 995 Eomgwangno, Busanjin-gu, Busan 614-714 (Korea, Republic of); Jung, W.G. [School of Advanced Materials Engineering, Kookmin University, 861-1, Jeongneung-dong, Seongbuk-gu, Seoul 136-702 (Korea, Republic of); Tan, S.T. [Institute of Microelectronics, 11 Science Park Road, Science Park II, Singapore 117685 (Singapore); Zhao, J.L. [School of Electrical and Electronic Engineering, Nanyang Technological University, Nanyang Avenue, Singapore 639798 (Singapore); Sun, X.W. [Institute of Microelectronics, 11 Science Park Road, Science Park II, Singapore 117685 (Singapore); School of Electrical and Electronic Engineering, Nanyang Technological University, Nanyang Avenue, Singapore 639798 (Singapore)

    2009-03-15

    In this study, the effects of thermal annealing temperature and duration on ZnO nanorod arrays fabricated by hydrothermal method were investigated. The annealed ZnO/Si(1 1 1) substrate was used for ZnO nanorod array growth. The effects of annealing treatment on the structural and optical properties were investigated by scanning electron microscopy, X-ray diffraction, and room-temperature photoluminescence measurements. With the annealing temperature of 750 {sup o}C and the annealing duration of 10 min, both the structural and optical properties of the ZnO nanorod arrays improved significantly, as indicated in the X-ray diffraction and photoluminescence measurement.

  4. Properties of antimony doped ZnO thin films deposited by spray pyrolysis technique

    Energy Technology Data Exchange (ETDEWEB)

    Sadananda Kumar, N., E-mail: sadanthara@gmail.com; Bangera, Kasturi V.; Shivakumar, G. K. [National Institute of Technology Karnataka, Surathkal, Thin Films Laboratory, Department of Physics (India)

    2015-07-15

    Antimony (Sb) doped zinc oxide (ZnO) thin films were deposited on the glass substrate at 450°C using spray pyrolysis technique. Effect of Sb doping on surface morphology structural, optical and electrical properties were studied. X-ray diffraction (XRD) analysis showed that both the undoped and doped ZnO thin films are polycrystalline in nature with (101) preferred orientation. SEM analysis showed a change in surface morphology of Sb doped ZnO thin films. Doping results in a marked increase in conductivity without affecting the transmittance of the films. ZnO films prepared with 3 at % Sb shows the lowest resistivity of 0.185 Ohm cm with a Hall mobility of 54.05 cm{sup 2} V{sup –1} s{sup –1}, and a hole concentration of 6.25 × 10{sup 17} cm{sup –3}.

  5. Use of chemically synthesized ZnO thin film as a liquefied petroleum gas sensor

    International Nuclear Information System (INIS)

    Shinde, V.R.; Gujar, T.P.; Lokhande, C.D.; Mane, R.S.; Han, Sung-Hwan

    2007-01-01

    Liquefied petroleum gas (LPG) sensing properties of ZnO thin films consisting of sub-micron rods synthesized by chemical bath deposition (CBD) method are presented in depth. The scanning electron microscopy observation reveals that ZnO sub-micron rods are of hexagonal in phase grown perpendicular to the substrate surface. Due to large surface area, the ZnO thin films of sub-micron rods were sensitive to the explosive LPG, which was studied for different time depositions and for different operating temperatures. The maximum response of 28% at 673 K was recorded under the exposure of 10% of lower explosive level (LEL) of LPG. The ZnO thin films of sub-micron rods exhibited good sensitivity and rapid response-recovery characteristics towards LPG

  6. Quantum dots coupled ZnO nanowire-array panels and their photocatalytic activities.

    Science.gov (United States)

    Liao, Yulong; Que, Wenxiu; Zhang, Jin; Zhong, Peng; Yuan, Yuan; Qiu, Xinku; Shen, Fengyu

    2013-02-01

    Fabrication and characterization of a heterojunction structured by CdS quantum dots@ZnO nanowire-array panels were presented. Firstly, ZnO nanowire-array panels were prepared by using a chemical bath deposition approach where wurtzite ZnO nanowires with a diameter of about 100 nm and 3 microm in length grew perpendicularly to glass substrate. Secondly, CdS quantum dots were deposited onto the surface of the ZnO nanowire-arrays by using successive ion layer absorption and reaction method, and the CdS shell/ZnO core heterojunction were thus obtained. Field emission scanning electron microscopy and transmission electron microscope were employed to characterize the morphological properties of the as-obtained CdS quantum dots@ZnO nanowire-array panels. X-ray diffraction was adopted to characterize the crystalline properties of the as-obtained CdS quantum dots@ZnO nanowire-array panels. Methyl orange was taken as a model compound to confirm the photocatalytic activities of the CdS shell/ZnO core heterojunction. Results indicate that CdS with narrow band gap not only acts as a visible-light sensitizer but also is responsible for an effective charge separation.

  7. Formation of p-type ZnO thin film through co-implantation

    Science.gov (United States)

    Chuang, Yao-Teng; Liou, Jhe-Wei; Woon, Wei-Yen

    2017-01-01

    We present a study on the formation of p-type ZnO thin film through ion implantation. Group V dopants (N, P) with different ionic radii are implanted into chemical vapor deposition grown ZnO thin film on GaN/sapphire substrates prior to thermal activation. It is found that mono-doped ZnO by N+ implantation results in n-type conductivity under thermal activation. Dual-doped ZnO film with a N:P ion implantation dose ratio of 4:1 is found to be p-type under certain thermal activation conditions. Higher p-type activation levels (1019 cm-3) under a wider thermal activation range are found for the N/P dual-doped ZnO film co-implanted by additional oxygen ions. From high resolution x-ray diffraction and x-ray photoelectron spectroscopy it is concluded that the observed p-type conductivities are a result of the promoted formation of PZn-4NO complex defects via the concurrent substitution of nitrogen at oxygen sites and phosphorus at zinc sites. The enhanced solubility and stability of acceptor defects in oxygen co-implanted dual-doped ZnO film are related to the reduction of oxygen vacancy defects at the surface. Our study demonstrates the prospect of the formation of stable p-type ZnO film through co-implantation.

  8. Preparation and characterization of ZnO transparent semiconductor thin films by sol-gel method

    International Nuclear Information System (INIS)

    Tsay, Chien-Yie; Fan, Kai-Shiung; Chen, Sih-Han; Tsai, Chia-Hao

    2010-01-01

    Transparent semiconductor thin films of zinc oxide (ZnO) were deposited onto alkali-free glass substrates by the sol-gel method and spin-coating technique. In this study, authors investigate the influence of the heating rate of the preheating process (4 or 10 o C/min) on the crystallization, surface morphology, and optical properties of sol-gel derived ZnO thin films. The ZnO sol was synthesized by dissolving zinc acetate dehydrate in ethanol, and then adding monoethanolamine. The as-coated films were preheated at 300 o C for 10 min and annealed at 500 o C for 1 h in air ambiance. Experimental results indicate that the heating rate of the preheating process strongly affected the surface morphology and transparency of ZnO thin film. Specifically, a heating rate of 10 o C/min for the preheating process produces a preferred orientation along the (0 0 2) plane and a high transmittance of 92% at a wavelength of 550 nm. Furthermore, this study reports the fabrication of thin-film transistors (TFTs) with a transparent ZnO active channel layer and evaluates their electrical performance.

  9. MOF-5 decorated hierarchical ZnO nanorod arrays and its photoluminescence

    Science.gov (United States)

    Zhang, Yinmin; Lan, Ding; Wang, Yuren; Cao, He; Jiang, Heng

    2011-04-01

    The strategy to manipulate nanoscale materials into well-organized hierarchical architectures is very important to both material synthesis and nanodevice applications. Here, nanoscale MOF-5 crystallites were successfully fabricated onto ordered hierarchical ZnO arrays based on aqueous chemical synthesis and molecule self-assembly technology guided room temperature diffusion method, which has the advantages of energy saving and simple operation. The structures and morphologies of the samples were performed by X-ray powder diffraction and field emission scanning electronic microscopy. The MOF-5 crystallites have good quality and bind well to the hexagonal-patterned ZnO arrays. The photoluminescence spectrum shows that the emission of hybrid MOF-5-ZnO films displays a blue shift in green emission and intensity reduction in UV emission. This ordered hybrid semiconductor material is expected to exploit the great potentiality in sensors, micro/nanodevices, and screen displays.

  10. Solid-state dye-sensitized solar cells based on ZnO nanoparticle and nanorod array hybrid photoanodes

    Directory of Open Access Journals (Sweden)

    Sue Hung-Jue

    2011-01-01

    Full Text Available Abstract The effect of ZnO photoanode morphology on the performance of solid-state dye-sensitized solar cells (DSSCs is reported. Four different structures of dye-loaded ZnO layers have been fabricated in conjunction with poly(3-hexylthiophene. A significant improvement in device efficiency with ZnO nanorod arrays as photoanodes has been achieved by filling the interstitial voids of the nanorod arrays with ZnO nanoparticles. The overall power conversion efficiency increases from 0.13% for a nanorod-only device to 0.34% for a device with combined nanoparticles and nanorod arrays. The higher device efficiency in solid-state DSSCs with hybrid nanorod/nanoparticle photoanodes is originated from both large surface area provided by nanoparticles for dye adsorption and efficient charge transport provided by the nanorod arrays to reduce the recombinations of photogenerated carriers.

  11. Wafer-Scale High-Throughput Ordered Growth of Vertically Aligned ZnO Nanowire Arrays

    KAUST Repository

    Wei, Yaguang

    2010-09-08

    This article presents an effective approach for patterned growth of vertically aligned ZnO nanowire (NW) arrays with high throughput and low cost at wafer scale without using cleanroom technology. Periodic hole patterns are generated using laser interference lithography on substrates coated with the photoresist SU-8. ZnO NWs are selectively grown through the holes via a low-temperature hydrothermal method without using a catalyst and with a superior control over orientation, location/density, and as-synthesized morphology. The development of textured ZnO seed layers for replacing single crystalline GaN and ZnO substrates extends the large-scale fabrication of vertically aligned ZnO NW arrays on substrates of other materials, such as polymers, Si, and glass. This combined approach demonstrates a novel method of manufacturing large-scale patterned one-dimensional nanostructures on various substrates for applications in energy harvesting, sensing, optoelectronics, and electronic devices. © 2010 American Chemical Society.

  12. Superhydrophobic nanostructured ZnO thin films on aluminum alloy substrates by electrophoretic deposition process

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Ying; Sarkar, D.K., E-mail: dsarkar@uqac.ca; Chen, X-Grant

    2015-02-01

    Graphical abstract: - Highlights: • Fabrication of superhydrophobic ZnO thin films surfaces by electrophoretic deposition process on aluminum substrates. • Effect of bath temperature on the physical and superhydrophobic properties of thin films. • The water contact angle of 155° ± 3 with roll off property has been observed on the film that was grown at bath temperatures of 50 °C. • The activation energy for electrophoretic deposition of SA-functionalized ZnO nanoparticle is calculated to be 0.50 eV. - Abstract: Superhydrophobic thin films have been fabricated on aluminum alloy substrates by electrophoretic deposition (EPD) process using stearic acid (SA) functionalized zinc oxide (ZnO) nanoparticles suspension in alcohols at varying bath temperatures. The deposited thin films have been characterized using both X-ray diffraction (XRD) and infrared (IR) spectroscopy and it is found that the films contain low surface energy zinc stearate and ZnO nanoparticles. It is also observed that the atomic percentage of Zn and O, roughness and water contact angle of the thin films increase with the increase of the deposited bath temperature. Furthermore, the thin film deposited at 50 °C, having a roughness of 4.54 ± 0.23 μm, shows superhydrophobic properties providing a water contact angle of 155 ± 3° with rolling off properties. Also, the activation energy of electrophoretic deposition of stearic-acid-functionalized ZnO nanoparticles is calculated to be 0.5 eV.

  13. Synthesis and characterization of ZnO thin film by low cost modified SILAR technique

    Directory of Open Access Journals (Sweden)

    Haridas D. Dhaygude

    2016-03-01

    Full Text Available The ZnO thin film is prepared on Fluorine Tin Oxide (FTO coated glass substrate by using SILAR deposition technique containing ZnSO4.7H2O and NaOH as precursor solution with 150 deeping cycles at 70 °C temperature. Nanocrystalline diamond like ZnO thin film is characterized by different characterization techniques such as X-ray diffraction (XRD, Fourier transform (FT Raman spectrometer, Field Emission Scanning Electron Microscopy (FE-SEM with Energy dispersive X-Ray Analysis (EDAX, optical absorption, surface wettability and photoelectrochemical cell performance measurement. The X-ray diffraction analysis shows that the ZnO thin film is polycrystalline in nature having hexagonal crystal structure. The FT-Raman scattering exhibits a sharp and strong mode at 383 cm−1 which confirms hexagonal ZnO nanostructure. The surface morphology study reveals that deposited ZnO film consists of nanocrystalline diamond like morphology all over the substrate. The synthesized thin film exhibited absorption wavelength around 309 nm. Optical study predicted the direct band gap and band gap energy of this film is found to be 3.66 eV. The photoelectrochemical cell (PEC parameter measurement study shows that ZnO sample confirmed the highest values of, short circuit current (Isc - 629 mAcm−2, open circuit voltage (Voc - 878 mV, fill factor (FF - 0.48, and maximum efficiency (η - 0.89%, respectively.

  14. Oxygen vacancy-induced ferromagnetism in un-doped ZnO thin films

    Science.gov (United States)

    Zhan, Peng; Wang, Weipeng; Liu, Can; Hu, Yang; Li, Zhengcao; Zhang, Zhengjun; Zhang, Peng; Wang, Baoyi; Cao, Xingzhong

    2012-02-01

    ZnO films became ferromagnetic when defects were introduced by thermal-annealing in flowing argon. This ferromagnetism, as shown by the photoluminescence measurement and positron annihilation analysis, was induced by the singly occupied oxygen vacancy with a saturated magnetization dependent positively on the amount of this vacancy. This study clarified the origin of the ferromagnetism of un-doped ZnO thin films and provides possibly an alternative way to prepare ferromagnetic ZnO films.

  15. Photocatalytic efficiency of reusable ZnO thin films deposited by sputtering technique

    International Nuclear Information System (INIS)

    Ahumada-Lazo, R.; Torres-Martínez, L.M.; Ruíz-Gómez, M.A.; Vega-Becerra, O.E.

    2014-01-01

    Graphical abstract: - Highlights: • Decolorization of Orange G dye using highly c-axis-oriented ZnO thin films. • The flake-shaped film shows superior and stable photoactivity at a wide range of pH. • The highest photodecolorization was achieved at pH of 7. • The exposure of (101) and (100) facets enhanced the photoactivity. • ZnO thin films exhibit a promising performance as recyclable photocatalysts. - Abstract: The photocatalytic activity of ZnO thin films with different physicochemical characteristics deposited by RF magnetron sputtering on glass substrate was tested for the decolorization of orange G dye aqueous solution (OG). The crystalline phase, surface morphology, surface roughness and the optical properties of these ZnO films were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM) and UV–visible spectroscopy (UV–Vis), respectively. The dye photodecolorization process was studied at acid, neutral and basic pH media under UV irradiation of 365 nm. Results showed that ZnO films grow with an orientation along the c-axis of the substrate and exhibit a wurtzite crystal structure with a (002) preferential crystalline orientation. A clear relationship between surface morphology and photocatalytic activity was observed for ZnO films. Additionally, the recycling photocatalytic abilities of the films were also evaluated. A promising photocatalytic performance has been found with a very low variation of the decolorization degree after five consecutive cycles at a wide range of pH media

  16. Photocatalytic efficiency of reusable ZnO thin films deposited by sputtering technique

    Energy Technology Data Exchange (ETDEWEB)

    Ahumada-Lazo, R.; Torres-Martínez, L.M. [Universidad Autónoma de Nuevo León, Facultad de Ingeniería Civil, Departamento de Ecomateriales y Energía, Av. Universidad S/N Ciudad Universitaria, San Nicolás de los Garza, Nuevo León C.P. 66450, México (Mexico); Ruíz-Gómez, M.A. [Universidad Autónoma de Nuevo León, Facultad de Ingeniería Civil, Departamento de Ecomateriales y Energía, Av. Universidad S/N Ciudad Universitaria, San Nicolás de los Garza, Nuevo León C.P. 66450, México (Mexico); Departmento de Física Aplicada, CINVESTAV-IPN, Antigua Carretera a Progreso km 6, Mérida, Yucatán 97310, México (Mexico); Vega-Becerra, O.E. [Centro de Investigación en Materiales Avanzados S.C, Alianza norte 202, Parque de Investigación e Innovación Tecnológica, C.P. 66600 Apodaca Nuevo León, México (Mexico); and others

    2014-12-15

    Graphical abstract: - Highlights: • Decolorization of Orange G dye using highly c-axis-oriented ZnO thin films. • The flake-shaped film shows superior and stable photoactivity at a wide range of pH. • The highest photodecolorization was achieved at pH of 7. • The exposure of (101) and (100) facets enhanced the photoactivity. • ZnO thin films exhibit a promising performance as recyclable photocatalysts. - Abstract: The photocatalytic activity of ZnO thin films with different physicochemical characteristics deposited by RF magnetron sputtering on glass substrate was tested for the decolorization of orange G dye aqueous solution (OG). The crystalline phase, surface morphology, surface roughness and the optical properties of these ZnO films were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), atomic force microscopy (AFM) and UV–visible spectroscopy (UV–Vis), respectively. The dye photodecolorization process was studied at acid, neutral and basic pH media under UV irradiation of 365 nm. Results showed that ZnO films grow with an orientation along the c-axis of the substrate and exhibit a wurtzite crystal structure with a (002) preferential crystalline orientation. A clear relationship between surface morphology and photocatalytic activity was observed for ZnO films. Additionally, the recycling photocatalytic abilities of the films were also evaluated. A promising photocatalytic performance has been found with a very low variation of the decolorization degree after five consecutive cycles at a wide range of pH media.

  17. Influence of annealing temperature on ZnO thin films grown by dual ...

    Indian Academy of Sciences (India)

    Administrator

    In electrical characterization as well, when annealing temperature was increased .... of ZnO (002) peaks and (c) crystallite size and stress generation on ZnO thin films ... sufficient kinetic energy and surface mobility to occupy stable positions ...

  18. Optimization of processing parameters on the controlled growth of c-axis oriented ZnO nanorod arrays

    Energy Technology Data Exchange (ETDEWEB)

    Malek, M. F., E-mail: mfmalek07@gmail.com; Rusop, M., E-mail: rusop@salam.uitm.my [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor (Malaysia); NANO-SciTech Centre (NST), Institute of Science (IOS), Universiti Teknologi MARA - UiTM, 40450 Shah Alam, Selangor (Malaysia); Mamat, M. H., E-mail: hafiz-030@yahoo.com [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor (Malaysia); Musa, M. Z., E-mail: musa948@gmail.com [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM) Pulau Pinang, Jalan Permatang Pauh, 13500 Permatang Pauh, Pulau Pinang (Malaysia); Saurdi, I., E-mail: saurdy788@gmail.com; Ishak, A., E-mail: ishak@sarawak.uitm.edu.my [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM), 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA (UiTM) Sarawak, Kampus Kota Samarahan, Jalan Meranek, 94300 Kota Samarahan, Sarawak (Malaysia); Alrokayan, Salman A. H., E-mail: dr.salman@alrokayan.com; Khan, Haseeb A., E-mail: khan-haseeb@yahoo.com [Chair of Targeting and Treatment of Cancer Using Nanoparticles, Deanship of Scientific Research, King Saud University (KSU), Riyadh 11451 (Saudi Arabia)

    2016-07-06

    Optimization of the growth time parameter was conducted to synthesize high-quality c-axis ZnO nanorod arrays. The effects of the parameter on the crystal growth and properties were systematically investigated. Our studies confirmed that the growth time influence the properties of ZnO nanorods where the crystallite size of the structures was increased at higher deposition time. Field emission scanning electron microsope analysis confirmed the morphologies structure of the ZnO nanorods. The ZnO nanostructures prepared under the optimized growth conditions showed an intense XRD peak which reveal a higher c-axis oriented ZnO nanorod arrays thus demonstrating the formation of defect free structure.

  19. A comparative study of physico-chemical properties of CBD and SILAR grown ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Jambure, S.B.; Patil, S.J.; Deshpande, A.R.; Lokhande, C.D., E-mail: l_chandrakant@yahoo.com

    2014-01-01

    Graphical abstract: Schematic model indicating ZnO nanorods by CBD (Z{sub 1}) and nanograins by SILAR (Z{sub 2}). - Highlights: • Simple methods for the synthesis of ZnO thin films. • Comparative study of physico-chemical properties of ZnO thin films prepared by CBD and SILAR methods. • CBD outperforms SILAR method. - Abstract: In the present work, nanocrystalline zinc oxide (ZnO) thin films have been successfully deposited onto glass substrates by simple and economical chemical bath deposition (CBD) and successive ionic layer adsorption reaction (SILAR) methods. These films were further characterized for their structural, optical, surface morphological and wettability properties. The X-ray diffraction (XRD) patterns for both CBD and SILAR deposited ZnO thin films reveal the highly crystalline hexagonal wurtzite structure. From optical studies, band gaps obtained are 2.9 and 3.0 eV for CBD and SILAR deposited thin films, respectively. The scanning electron microscope (SEM) patterns show growth of well defined randomly oriented nanorods and nanograins on the CBD and SILAR deposited samples, respectively. The resistivity of CBD deposited films (10{sup 2} Ω cm) is lower than that of SILAR deposited films (10{sup 5} Ω cm). Surface wettability studies show hydrophobic nature for both films. From the above results it can be concluded that CBD grown ZnO thin films show better properties as compared to SILAR method.

  20. A comparative study of physico-chemical properties of CBD and SILAR grown ZnO thin films

    International Nuclear Information System (INIS)

    Jambure, S.B.; Patil, S.J.; Deshpande, A.R.; Lokhande, C.D.

    2014-01-01

    Graphical abstract: Schematic model indicating ZnO nanorods by CBD (Z 1 ) and nanograins by SILAR (Z 2 ). - Highlights: • Simple methods for the synthesis of ZnO thin films. • Comparative study of physico-chemical properties of ZnO thin films prepared by CBD and SILAR methods. • CBD outperforms SILAR method. - Abstract: In the present work, nanocrystalline zinc oxide (ZnO) thin films have been successfully deposited onto glass substrates by simple and economical chemical bath deposition (CBD) and successive ionic layer adsorption reaction (SILAR) methods. These films were further characterized for their structural, optical, surface morphological and wettability properties. The X-ray diffraction (XRD) patterns for both CBD and SILAR deposited ZnO thin films reveal the highly crystalline hexagonal wurtzite structure. From optical studies, band gaps obtained are 2.9 and 3.0 eV for CBD and SILAR deposited thin films, respectively. The scanning electron microscope (SEM) patterns show growth of well defined randomly oriented nanorods and nanograins on the CBD and SILAR deposited samples, respectively. The resistivity of CBD deposited films (10 2 Ω cm) is lower than that of SILAR deposited films (10 5 Ω cm). Surface wettability studies show hydrophobic nature for both films. From the above results it can be concluded that CBD grown ZnO thin films show better properties as compared to SILAR method

  1. Ag nanoparticles-decorated ZnO nanorod array on a mechanical flexible substrate with enhanced optical and antimicrobial properties

    Science.gov (United States)

    Chen, Yi; Tse, Wai Hei; Chen, Longyan; Zhang, Jin

    2015-03-01

    Heteronanostructured zinc oxide nanorod (ZnO NR) array are vertically grown on polydimethylsiloxane (PDMS) through a hydrothermal method followed by an in situ deposition of silver nanoparticles (Ag NPs) through a photoreduction process. The Ag-ZnO heterostructured nanorods on PDMS are measured with an average diameter of 160 nm and an average length of 2 μm. ZnO NRs measured by high-resolution transmission electron microscope (HRTEM) shows highly crystalline with a lattice fringe of 0.255 nm, which corresponds to the (0002) planes in ZnO crystal lattice. The average diameter of the Ag NPs in situ deposited on the ZnO NRs is estimated at 22 ± 2 nm. As compared to the bare ZnO NRs, the heterostructured Ag-ZnO nanorod array shows enhanced ultraviolet (UV) absorption at 440 nm, and significant emission in the visible region (λem = 542 nm). In addition, the antimicrobial efficiency of Ag-ZnO heterostructured nanorod array shows obvious improvement as compared to bare ZnO nanorod array. The cytotoxicity of ZnO nanorod array with and without Ag NPs was studied by using 3 T3 mouse fibroblast cell line. No significant toxic effect is imposed on the cells.

  2. Pulsed laser deposited Al-doped ZnO thin films for optical applications

    Directory of Open Access Journals (Sweden)

    Gurpreet Kaur

    2015-02-01

    Full Text Available Highly transparent and conducting Al-doped ZnO (Al:ZnO thin films were grown on glass substrates using pulsed laser deposition technique. The profound effect of film thickness on the structural, optical and electrical properties of Al:ZnO thin films was observed. The X-ray diffraction depicts c-axis, plane (002 oriented thin films with hexagonal wurtzite crystal structure. Al-doping in ZnO introduces a compressive stress in the films which increase with the film thickness. AFM images reveal the columnar grain formation with low surface roughness. The versatile optical properties of Al:ZnO thin films are important for applications such as transparent electromagnetic interference (EMI shielding materials and solar cells. The obtained optical band gap (3.2–3.08 eV was found to be less than pure ZnO (3.37 eV films. The lowering in the band gap in Al:ZnO thin films could be attributed to band edge bending phenomena. The photoluminescence spectra gives sharp visible emission peaks, enables Al:ZnO thin films for light emitting devices (LEDs applications. The current–voltage (I–V measurements show the ohmic behavior of the films with resistivity (ρ~10−3 Ω cm.

  3. Development of novel control system to grow ZnO thin films by reactive evaporation

    Directory of Open Access Journals (Sweden)

    Gerardo Gordillo

    2016-07-01

    Full Text Available This work describes a novel system implemented to grow ZnO thin films by plasma assisted reactive evaporation with adequate properties to be used in the fabrication of photovoltaic devices with different architectures. The innovative aspect includes both an improved design of the reactor used to activate the chemical reaction that leads to the formation of the ZnO compound as an electronic system developed using the virtual instrumentation concept. ZnO thin films with excellent opto-electrical properties were prepared in a reproducible way, controlling the deposition system through a virtual instrument (VI with facilities to control the amount of evaporated zinc involved in the process that gives rise to the formation of ZnO, by means of the incorporation of PID (proportional integral differential and PWM (pulse width modulation control algorithms. The effectiveness and reliability of the developed system was verified by obtaining with good reproducibility thin films of n+-ZnO and i-ZnO grown sequentially in situ with thicknesses and resistivities suitable for use as window layers in chalcopyrite based thin film solar cells.

  4. Polyelectrolyte-assisted preparation and characterization of nanostructured ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Jia, Shijun

    2005-05-15

    The present work focuses on the synthesis and characterization of nanostructured ZnO thin films onto silicon wafers modified by self-assembled-monolayers via chemical bath deposition. Two precursor solutions were designed and used for the film deposition, in which two different polymers were introduced respectively to control the growth of the ZnO colloidal particles in solution. ZnO films were deposited from an aqueous solution containing zinc salt and hexamethylenetetramine (HMTA) in the presence of a graft-copolymer (P (MAA{sub 0.50}-co(MAA-EO{sub 20}){sub 0.50}){sub 70}). A film-formation-diagram was established based on the results obtained by scanning electron microscopy (SEM) and atomic force microscopy (AFM), which describes the influence of the concentration of HMTA and copolymer on the ZnO film formation. According to the film morphology, film formation can be classified into three categories: (a) island-like films, (b) uniform films and (c) canyon-like films. The ZnO films annealed at temperatures of 450 C, 500 C, 600 C and 700 C were examined by X-ray diffraction (XRD) and transmission electron microscopy (TEM). After annealing, the films are polycrystalline ZnO with wurtzite structure. XRD measurements indicate that with increasing annealing temperature, the average grain size increases accordingly and the crystallinity of the films is improved. Upon heating to 600 C, the ZnO films exhibit preferred orientation with c-axis normal to substrate, whereas the films annealed at 700 C even show a more explicit texture. By annealing at temperatures above 600 C the ZnO film reacts with the substrate to form an interfacial layer of Zn{sub 2}SiO{sub 4}, which grows thicker at elevated annealing temperatures. The ZnO films annealed at 600 C and 700 C show strong UV emission. Another non-aqueous solution system for ZnO thin film deposition was established, in which 2- propanol was used as a solvent and Zn(CH3COO){sub 2}.2H{sub 2}O as well as NaOH as reactants

  5. Soft-solution route to ZnO nanowall array with low threshold power density

    Science.gov (United States)

    Jang, Eue-Soon; Chen, Xiaoyuan; Won, Jung-Hee; Chung, Jae-Hun; Jang, Du-Jeon; Kim, Young-Woon; Choy, Jin-Ho

    2010-07-01

    ZnO nanowall array (ZNWA) has been directionally grown on the buffer layer of ZnO nanoparticles dip-coated on Si-wafer under a soft solution process. Nanowalls on substrate are in most suitable shape and orientation not only as an optical trap but also as an optical waveguide due to their unique growth habit, V[011¯0]≫V[0001]≈V[0001¯]. Consequently, the stimulated emission at 384 nm through nanowalls is generated by the threshold power density of only 25 kW/cm2. Such UV lasing properties are superior to those of previously reported ZnO nanorod arrays. Moreover, there is no green (defect) emission due to the mild procedure to synthesize ZNWA.

  6. Superhydrophobic Ag decorated ZnO nanostructured thin film as effective surface enhanced Raman scattering substrates

    Science.gov (United States)

    Jayram, Naidu Dhanpal; Sonia, S.; Poongodi, S.; Kumar, P. Suresh; Masuda, Yoshitake; Mangalaraj, D.; Ponpandian, N.; Viswanathan, C.

    2015-11-01

    The present work is an attempt to overcome the challenges in the fabrication of super hydrophobic silver decorated zinc oxide (ZnO) nanostructure thin films via thermal evaporation process. The ZnO nanowire thin films are prepared without any surface modification and show super hydrophobic nature with a contact angle of 163°. Silver is further deposited onto the ZnO nanowire to obtain nanoworm morphology. Silver decorated ZnO (Ag@ZnO) thin films are used as substrates for surface enhanced Raman spectroscopy (SERS) studies. The formation of randomly arranged nanowire and silver decorated nanoworm structure is confirmed using FESEM, HR-TEM and AFM analysis. Crystallinity and existence of Ag on ZnO are confirmed using XRD and XPS studies. A detailed growth mechanism is discussed for the formation of the nanowires from nanobeads based on various deposition times. The prepared SERS substrate reveals a reproducible enhancement of 3.082 × 107 M for Rhodamine 6G dye (R6G) for 10-10 molar concentration per liter. A higher order of SERS spectra is obtained for a contact angle of 155°. Thus the obtained thin films show the superhydrophobic nature with a highly enhanced Raman spectrum and act as SERS substrates. The present nanoworm morphology shows a new pathway for the construction of semiconductor thin films for plasmonic studies and challenges the orderly arranged ZnO nanorods, wires and other nano structure substrates used in SERS studies.

  7. Characterization of n and p-type ZnO thin films grown by pulsed filtered cathodic vacuum arc system

    International Nuclear Information System (INIS)

    Kavak, H.; Erdogan, E.N.; Ozsahin, I.; Esen, R.

    2010-01-01

    Full text : Semiconductor ZnO thin films with wide band gap attract much interest due to their properties such as chemical stability in hydrogen plasma, high optical transparency in the visible and nearinfrared region. Due to these properties ZnO oxide is a promising materials for electronic or optoelectronic applications such as solar cell (as an antireflecting coating and a transparent conducting material), gas sensors, surface acoustic wave devices. The purpose of this research is to improve the properties of n and p-type ZnO thin films for device applications. Polycrystalline ZnO is naturally n-type and very difficult to dope to make p-type. Therefore nowadays hardly produced p-type ZnO attracts a lot of attention. Nitrogen considered as the best dopant for p-type ZnO thin films.The transparent, conductive and very precise thickness controlled n and p-type semiconducting nanocrystalline ZnO thin films were prepared by pulsed filtered cathodic vacuum arc deposition (PFCVAD) method. Structural, optical and electrical properties of these films were investigated. And also photoluminescence properties of these films were investigated. Transparent p-type ZnO thin films were produced by oxidation of PFCVAD deposited zinc nitride. Zinc nitride thin films were deposited with various thicknesses and under different oxygen pressures on glass substrates. Zinc nitride thin films, which were deposited at room temperatures, were amorphous and the optical transmission was below 70%. For oxidation zinc nitride, the sample was annealed in air starting from 350 degrees Celsium up to 550 degrees Celsium for one hour duration. These XRD patterns imply that zinc nitride thin films converted to zinc oxide thin films with the same hexagonal crystalline structures of ZnO. The optical measurements were made for each annealing temperature and the optical transmissions of ZnO thin films were found better than 90 percent in visible range after annealing over 350 degrees Celsium. By

  8. DFT calculations on electronic properties of ZnO thin films deposited by spray pyrolysis

    Energy Technology Data Exchange (ETDEWEB)

    Cordeiro, J.M.; Reynoso, V.C.; Azevedo, D.H.M. [Universidade Estadual Paulista Julio de Mesquita Filho (UNESP), SP (Brazil)

    2016-07-01

    Full text: Introduction - Thin films of Zinc oxide (ZnO) has a wide range of technological applications, as transparent conducting electrodes in solar cells, flat panel displays, and sensors, for example. More recently applications in optoelectronics, like light emitter diodes and laser diodes, due to its large band gap, are been explored. Studies of ZnO thin films are important for these applications. Methodology - In this study thin films of ZnO have been deposited by spray pyrolysis on glass substrate. The films were characterized by XRD and UV-VIS techniques and the electronic properties as a function of the film thickness have been investigated by DFT calculations with B3LYP hybrid potential implemented in the CRYSTAL09 code. Results - The diffractograms obtained for the ZnO thin films as a function of the thickness are shown. The films exhibit a hexagonal wurtzite structure with preferred c-axis orientation in (002) direction of ZnO crystal. A quantum mechanical approach based on the periodic Density Functional Theory (DFT), with B3LYP hybrid potential was used to investigate the electronic structure of the films as a function of the thickness. The CRYSTAL09 code has been used for the calculations on the wurtzite hexagonal structure of ZnO - spatial group P63mc. For optimizing the geometry of the pure ZnO crystal, the experimental lattice parameters were got as follows: a= 0.325 nm, b= 0.325 nm, c= 0.5207 nm with c/a= 1.602. Considering to the calculations of the band structure, it is suggested that the semiconducting properties of ZnO arises from the overlapping of the 4s orbital of the conducting band of Zn and the 2p orbital of the top of valence band of O. Conclusions - The structure of ZnO thin film deposited on glass substrate present preferential orientation in (002) direction. Variation in the optical properties as a function of the film thickness was observed. The band gap energy was determined from optical analysis to be ∼ 3.27 eV. The refractive

  9. Mechanism and Growth of Flexible ZnO Nanostructure Arrays in a Facile Controlled Way

    Directory of Open Access Journals (Sweden)

    Yangping Sheng

    2011-01-01

    Full Text Available Nanostructure arrays-based flexible devices have revolutionary impacts on the application of traditional semiconductor devices. Here, a one-step method to synthesize flexible ZnO nanostructure arrays on Zn-plated flexible substrate in Zn(NO32/NH3⋅H2O solution system at 70–90∘C was developed. We found out that the decomposition of Zn(OH2 precipitations, formed in lower NH3⋅H2O concentration, in the bulk solution facilitates the formation of flower-like structure. In higher temperature, 90∘C, ZnO nanoplate arrays were synthesized by the hydrolysis of zinc hydroxide. Highly dense ZnO nanoparticale layer formed by the reaction of NH3⋅H2O with Zn plating layer in the initial self-seed process could improve the vertical alignment of the nanowires arrays. The diameter of ZnO nanowire arrays, from 200 nm to 60 nm, could be effectively controlled by changing the stability of Zn(NH342+ complex ions by varying the ratio of Zn(NO32 to NH3⋅H2O which further influence the release rate of Zn2+ ions. This is also conformed by different amounts of the Zn vacancy as determined by different UV emissions of the PL spectra in the range of 380–403 nm.

  10. A template-free sol-gel technique for controlled growth of ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Huang, N.; Zhu, M.W.; Gao, L.J.; Gong, J.; Sun, C.; Jiang, X.

    2011-01-01

    The growth of ZnO nanorod arrays via a template-free sol-gel process was investigated. The nanorod is single-crystalline wurtzite structure with [0 0 0 1] growth direction determined by the transmission electron microscope. The aligned ZnO arrays were obtained directly on the glass substrates by adjusting the temperatures and the withdrawal speeds, without seed-layer or template assistant. A thicker oriented ZnO nanorod arrays was obtained at proper experimental conditions by adding dip-coating layers. Room temperature photoluminescence spectrum exhibits an intensive UV emission with a weak broad green emission as well as a blue double-peak emission located at 451 and 468 nm, respectively. Further investigation results show that the difference in the alignment of nanorods ascribes to the different orientations of the nanoparticles-packed film formed prior to nanorods on the substrate. Well ordered ZnO nanorods are formed from this film with good c-axis orientation. Our study is expected to pave a way for direct growth of oriented nanorods by low-cost solution approaches.

  11. Studies on nonvolatile resistance memory switching in ZnO thin films

    Indian Academy of Sciences (India)

    Six decades of research on ZnO has recently sprouted a new branch in the domain of resistive random access memories. Highly resistive and c-axis oriented ZnO thin films were grown by us using d.c. discharge assisted pulsed laser deposition on Pt/Ti/SiO2/Si substrates at room temperature. The resistive switching ...

  12. A simple route to scalable fabrication of perfectly ordered ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Liu, D F; Xiang, Y J; Liao, Q; Zhang, J P; Wu, X C; Zhang, Z X; Liu, L F; Ma, W J; Shen, J; Zhou, W Y; Xie, S S

    2007-01-01

    ZnO nanorod arrays with perfect order and uniformity were prepared using a simple, low-cost, commonly available and scalable nanosphere lithography for patterning gold catalyst particles and a successive bottom-up growth technique in a tube furnace chemical vapor deposition system. Each rod in the arrays had perfect surface facets, sharp edges and uniform size. For all of the rods, their sides were oriented the same. This bottom-up assembly method may accelerate the use of ZnO nanorods in real device applications

  13. Mechanism for wettability alteration of ZnO nanorod arrays via thermal annealing in vacuum and air

    International Nuclear Information System (INIS)

    Zhang Jun; Liu Yanru; Wei Zhiyang; Zhang Junyan

    2013-01-01

    Highlights: ► Oxygen vacancy is the key factor in accounting for the change in morphology of the ZnO nanorod arrays. ► We firstly investigated the wettability alteration of ZnO nanorod arrays annealed in vacuum at different temperature. ► The hydrophilicity of the ZnO nanorod arrays annealed in air is not related to the oxygen vacancy but ascribed to the O adatom on the nanorod surface. - Abstract: The ZnO nanorod arrays were synthesized via a simple hydrothermal process followed by annealing in vacuum and air respectively at different temperature. The wettability of samples was controlled by adjusting the annealing atmosphere and temperature. To investigate the mechanism of wettability alteration, the chemical composition and surface morphology of nanorod arrays were analyzed by X-ray photoelectron spectroscopy (XPS) and field emission scanning electron microscopy (FE-SEM), respectively. Increasing oxygen vacancy concentration by increasing annealing temperature in vacuum resulted in a great change of surface morphology, which played the major role in wettability change. Under annealing in air, oxygen vacancy concentration reduced and the surface morphology of nanorod arrays showed little change with increasing annealing temperature. The wettability alteration is ascribed to the O adatom on the nanorods surface.

  14. Regulating effect of SiO2 interlayer on optical properties of ZnO thin films

    International Nuclear Information System (INIS)

    Xu, Linhua; Zheng, Gaige; Miao, Juhong; Su, Jing; Zhang, Chengyi; Shen, Hua; Zhao, Lilong

    2013-01-01

    ZnO/SiO 2 nanocomposite films with periodic structure were prepared by electron beam evaporation technique. Regulating effect of SiO 2 interlayer with various thicknesses on the optical properties of ZnO/SiO 2 thin films was investigated deeply. The analyses of X-ray diffraction show that the ZnO layers in ZnO/SiO 2 nanocomposite films have a wurtzite structure and are preferentially oriented along the c-axis while the SiO 2 layers are amorphous. The scanning electron microscope images display that the ZnO layers are composed of columnar grains and the thicknesses of ZnO and SiO 2 layers are all very uniform. The SiO 2 interlayer presents a significant modulation effect on the optical properties of ZnO thin films, which is reflected in the following two aspects: (1) the transmittance of ZnO/SiO 2 nanocomposite films is increased; (2) the photoluminescence (PL) of ZnO/SiO 2 nanocomposite films is largely enhanced compared with that of pure ZnO thin films. The ZnO/SiO 2 nanocomposite films have potential applications in light-emitting devices and flat panel displays. -- Highlights: ► ZnO/SiO 2 nanocomposite films with periodic structure were prepared by electron beam evaporation technique. ► The SiO 2 interlayer presents a significant modulation effect on the optical properties of ZnO thin films. ► The photoluminescence of ZnO/SiO 2 nanocomposite films is largely enhanced compared with that of pure ZnO thin films. ► The ZnO/SiO 2 nanocomposite films have potential applications in light-emitting devices and flat panel displays

  15. Effect of annealing temperature on surface morphology and work function of ZnO nanorod arrays

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Hainan [School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 (China); Xue, Mingshan, E-mail: xuems04@mails.ucas.ac.cn [School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 (China); Ou, Junfei [School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 (China); Jiangsu Key Laboratory for Solar Cell Materials and Technology, Changzhou University, Changzhou 213164 (China); Wang, Fajun [School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 (China); Li, Wen, E-mail: wenl@ualberta.ca [School of Materials Science and Engineering, Nanchang Hangkong University, Nanchang 330063 (China)

    2013-07-15

    Highlights: •The 600°C and 450°C isothermal sections of the Zn-Fe-B system are determined. •The solubility of Zn in Fe{sub 2}B and FeB at 600°C is 1.8 at.% and 2.5 at.%, respectively. •The solubility of Zn in Fe{sub 2}B and FeB at 450°C is 1.7 at.% and 2.1 at.%, respectively. •All Fe-Zn compounds can be in equilibrium with Fe{sub 2}B at 450°C. •Both FeB and Fe{sub 2}B are in equilibrium with the liquid phase at 600°C. -- Abstract: A simple and effective method of fabricating nanomaterials and the understanding of their electronic structures are significant for designing novel nanodevices. In this study, ZnO nanorod arrays on ITO substrate were synthesized by electrochemical deposition, and the effect of annealing temperature on surface morphology and especially work function was investigated using various techniques. The results indicated that the formation of hexagonal ZnO nanorod arrays with (0 0 0 1) orientation was strongly associated with the annealing temperature. The work function of well-aligned ZnO nanorod arrays is 4.84 eV, which shows an obvious dependence on the arrangement of ZnO nanorod arrays. These changes in work function of ZnO nanorod arrays (e.g., used as the photoanode of dye-sensitized solar cells) are important to understand the electron transport of related nanodevices.

  16. Ionized zinc vacancy mediated ferromagnetism in copper doped ZnO thin films

    Directory of Open Access Journals (Sweden)

    Shi-Yi Zhuo

    2012-03-01

    Full Text Available This paper reports the origin of ferromagnetism in Cu-doped ZnO thin films. Room-temperature ferromagnetism is obtained in all the thin films when deposited at different oxygen partial pressure. An obviously enhanced peak corresponding to zinc vacancy is observed in the photoluminescence spectra, while the electrical spin resonance measurement implies the zinc vacancy is negative charged. After excluding the possibility of direct exchange mechanisms (via free carriers, we tentatively propose a quasi-indirect exchange model (via ionized zinc vacancy for Cu-doped ZnO system.

  17. Atomic layer deposition of Al-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Tynell, Tommi; Yamauchi, Hisao; Karppinen, Maarit; Okazaki, Ryuji; Terasaki, Ichiro [Department of Chemistry, Aalto University, FI-00076 Aalto (Finland); Department of Physics, Nagoya University, Nagoya 464-8602 (Japan)

    2013-01-15

    Atomic layer deposition has been used to fabricate thin films of aluminum-doped ZnO by depositing interspersed layers of ZnO and Al{sub 2}O{sub 3} on borosilicate glass substrates. The growth characteristics of the films have been investigated through x-ray diffraction, x-ray reflection, and x-ray fluorescence measurements, and the efficacy of the Al doping has been evaluated through optical reflectivity and Seebeck coefficient measurements. The Al doping is found to affect the carrier density of ZnO up to a nominal Al dopant content of 5 at. %. At nominal Al doping levels of 10 at. % and higher, the structure of the films is found to be strongly affected by the Al{sub 2}O{sub 3} phase and no further carrier doping of ZnO is observed.

  18. Effect of surface microstructure and wettability on plasma protein adsorption to ZnO thin films prepared at different RF powers

    Energy Technology Data Exchange (ETDEWEB)

    Huang Zhanyun; Chen Min; Chen Dihu [State Key Laboratory of Optoelectronic Materials and Technologies, Sun Yat-Sen University, Guangzhou 510275 (China); Pan Shirong, E-mail: stscdh@mail.sysu.edu.c [Artificial Heart Lab, the 1st Affiliate Hospital of Sun Yat-Sen University, Guangzhou 510080 (China)

    2010-10-01

    In this paper, the adsorption behavior of plasma proteins on the surface of ZnO thin films prepared by radio frequency (RF) sputtering under different sputtering powers was studied. The microstructures and surface properties of the ZnO thin films were investigated by x-ray diffraction (XRD), scanning electron microscopy (SEM), UV-visible optical absorption spectroscopy and contact angle techniques. The results show that the ZnO thin films have better orientation of the (0 0 2) peak with increasing RF power, especially at around 160 W, and the optical band gap of the ZnO films varies from 3.2 to 3.4 eV. The contact angle test carried out by the sessile drop technique denoted a hydrophobic surface of the ZnO films, and the surface energy and adhesive work of the ZnO thin films decreased with increasing sputtering power. The amounts of human fibrinogen (HFG) and human serum albumin (HSA) adsorbing on the ZnO films and reference samples were determined by using enzyme-linked immunosorbent assay (ELISA). The results show that fewer plasma proteins and a smaller HFG/HSA ratio adsorb on the ZnO thin films' surface.

  19. Controlled synthesis of ZnO branched nanorod arrays by hierarchical solution growth and application in dye-sensitized solar cells

    International Nuclear Information System (INIS)

    Fang Xiaoming; Peng Lihua; Shang Xiaoying; Zhang Zhengguo

    2011-01-01

    We demonstrate the controlled synthesis of ZnO branched nanorod arrays on fluorine-doped SnO 2 -coated glass substrates by the hierarchical solution growth method. In the secondary growth, the concentration of Zn(NO 3 ) 2 /hexamethylenetetramine plays an important role in controlling the morphology of the branched nanorod arrays, besides that of diaminopropane used as a structure-directing agent to induce the growth of branches. The population density and morphology of the branched nanorod arrays depend on those of the nanorod arrays obtained from the primary growth, which can be modulated though the concentration of Zn(NO 3 ) 2 /hexamethylenetetramine in the primary growth solution. The dye-sensitized ZnO branched nanorod arrays exhibit much stronger optical absorption as compared with its corresponding primary nanorod arrays, suggesting that the addition of the branches improves light harvesting. The dye-sensitized solar cell based on the optimized ZnO branched nanorod array reaches a conversion efficiency of 1.66% under the light radiation of 1000 W/m 2 . The branched nanorod arrays can also be applied in other application fields of ZnO.

  20. ZnO thin films on single carbon fibres fabricated by Pulsed Laser Deposition (PLD)

    Energy Technology Data Exchange (ETDEWEB)

    Krämer, André; Engel, Sebastian [Otto Schott Institute of Materials Research (OSIM), Friedrich Schiller University Jena, Löbdergraben 32, 07743 Jena (Germany); Sangiorgi, Nicola [Institute of Science and Technology for Ceramics – National Research Council of Italy (CNR-ISTEC), via Granarolo 64, 48018 Faenza, RA (Italy); Department of Chemical Science and Technologies, University of Rome Tor Vergata, via della Ricerca Scientifica, 00133 Rome (Italy); Sanson, Alessandra [Institute of Science and Technology for Ceramics – National Research Council of Italy (CNR-ISTEC), via Granarolo 64, 48018 Faenza, RA (Italy); Bartolomé, Jose F. [Instituto de Ciencia de Materiales de Madrid (ICMM), Consejo Superior de Investigaciones Científicas (CSIC), C/Sor Juana Inés de la Cruz 3, 28049 Madrid (Spain); Gräf, Stephan, E-mail: stephan.graef@uni-jena.de [Otto Schott Institute of Materials Research (OSIM), Friedrich Schiller University Jena, Löbdergraben 32, 07743 Jena (Germany); Müller, Frank A. [Otto Schott Institute of Materials Research (OSIM), Friedrich Schiller University Jena, Löbdergraben 32, 07743 Jena (Germany); Center for Energy and Environmental Chemistry Jena (CEEC Jena), Friedrich Schiller University Jena, Philosophenweg 7a, 07743 Jena (Germany)

    2017-03-31

    Highlights: • Carbon fibres were entirely coated with thin films consisting of aligned ZnO crystals. • A Q-switched CO2 laser was utilised as radiation source. • Suitability of ZnO thin films on carbon fibres as photo anodes for DSSC was studied. - Abstract: Single carbon fibres were 360° coated with zinc oxide (ZnO) thin films by pulsed laser deposition using a Q-switched CO{sub 2} laser with a pulse duration τ ≈ 300 ns, a wavelength λ = 10.59 μm, a repetition frequency f{sub rep} = 800 Hz and a peak power P{sub peak} = 15 kW in combination with a 3-step-deposition technique. In a first set of experiments, the deposition process was optimised by investigating the crystallinity of ZnO films on silicon and polished stainless steel substrates. Here, the influence of the substrate temperature and of the oxygen partial pressure of the background gas were characterised by scanning electron microscopy and X-ray diffraction analyses. ZnO coated carbon fibres and conductive glass sheets were used to prepare photo anodes for dye-sensitised solar cells in order to investigate their suitability for energy conversion devices. To obtain a deeper insight of the electronic behaviour at the interface between ZnO and substrate I–V measurements were performed.

  1. Sub-coherent growth of ZnO nanorod arrays on three-dimensional graphene framework as one-bulk high-performance photocatalyst

    Science.gov (United States)

    Yu, Mei; Ma, Yuxiao; Liu, Jianhua; Li, Xinjie; Li, Songmei; Liu, Shenyao

    2016-12-01

    Highly ordered ZnO nanorod arrays were grown vertically on the surface of three-dimensional graphene (3DG) framework bulk to prepare a one-bulk structure. In such structure, ZnO exhibits outstanding photocatalyst performance due to its hybridization with 3DG. The sub-coherency between ZnO and 3DG ensures the template-free growth of ZnO nanorod arrays and the exposing of its most active crystal surfaces {0001}. The hybridization prevents the agglomeration of ZnO nanoparticles, helping the formation of nanorod array morphology, enhancing the mass transfer of reactants and the separation of photogenerated holes. In the efficiency test, with tiny amount of ZnO catalyst (∼5.03 × 10-3 g), the concentration of methyl orange decreased to ∼11% of the initial value within four hours. The structure possesses high average photocatalytic efficiency of 6.56 × 10-3 h-1, much higher than that of bare ZnO nanorods.

  2. Low-Temperature Rapid Fabrication of ZnO Nanowire UV Sensor Array by Laser-Induced Local Hydrothermal Growth

    Directory of Open Access Journals (Sweden)

    Sukjoon Hong

    2013-01-01

    Full Text Available We demonstrate ZnO nanowire based UV sensor by laser-induced hydrothermal growth of ZnO nanowire. By inducing a localized temperature rise using focused laser, ZnO nanowire array at ~15 μm size consists of individual nanowires with ~8 μm length and 200~400 nm diameter is readily synthesized on gold electrode within 30 min at the desired position. The laser-induced growth process is consecutively applied on two different points to bridge the micron gap between the electrodes. The resultant photoconductive ZnO NW interconnections display 2~3 orders increase in the current upon the UV exposure at a fixed voltage bias. It is also confirmed that the amount of photocurrent can be easily adjusted by changing the number of ZnO NW array junctions. The device exhibits clear response to the repeated UV illumination, suggesting that this process can be usefully applied for the facile fabrication of low-cost UV sensor array.

  3. Ultraviolet Sensing by Al-doped ZnO Thin Films

    International Nuclear Information System (INIS)

    Rashid, A.R.A.; Menon, P.S.; Shaari, S.

    2011-01-01

    We report the fabrication and characterization of an ultraviolet photoconductive sensing by using Al-doped ZnO films. Undoped ZnO, 1 at.% and 2 at% of Al were prepared on quartz glass by sol gel method with annealing temperature of 500 degree Celsius for 1 hour. The presence of spherical shaped nanoparticles were detected for undoped ZnO by using FESEM. The absorption edge shifted to a lower wavelength by doping with Al and excitonic peak can be observed. The band gap values increased by adding Al. I-V curves reveal an improvement in electrical properties when the samples are illuminated by ultraviolet (UV) light with a wavelength of 365 nm. At 1 at.% of Al, the film have a larger increment in photocurrent response when illuminated with UV light compared to undoped ZnO and 2 at.% Al. The thin films have a longer recovery time than response time. (author)

  4. (0 0 2-oriented growth and morphologies of ZnO thin films prepared by sol-gel method

    Directory of Open Access Journals (Sweden)

    Guo Dongyun

    2016-09-01

    Full Text Available Zinc acetate was used as a starting material to prepare Zn-solutions from solvents and ligands with different boiling temperature. The ZnO thin films were prepared on Si(1 0 0 substrates by spin-coating method. The effect of baking temperature and boiling temperature of the solvents and ligands on their morphologies and orientation was investigated. The solvents and ligands with high boiling temperature were favorable for relaxation of mechanical stress to form the smooth ZnO thin films. As the solvents and ligands with low boiling temperature were used to prepare Zn-solutions, the prepared ZnO thin films showed (0 0 2 preferred orientation. As n-propanol, 2-methoxyethanol, 2-(methylaminoethanol and monoethanolamine were used to prepare Zn-solutions, highly (0 0 2-oriented ZnO thin films were formed by adjusting the baking temperature.

  5. Effect of doping concentration on the conductivity and optical properties of p-type ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Pathak, Trilok Kumar [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India); Kumar, Vinod, E-mail: vinod.phy@gmail.com [Department of Physics, University of the Free State, Bloemfontein (South Africa); Swart, H.C., E-mail: swarthc@ufs.ac.za [Department of Physics, University of the Free State, Bloemfontein (South Africa); Purohit, L.P., E-mail: proflppurohitphys@gmail.com [Semiconductor Research Lab, Department of Physics, Gurukula Kangri University, Haridwar (India)

    2016-01-01

    Nitrogen doped ZnO (NZO) thin films were synthesized on glass substrates by the sol–gel and spin coating method. Zinc acetate dihydrates and ammonium acetate were used as precursors for zinc and nitrogen, respectively. X-ray diffraction study showed that the thin films have a hexagonal wurtzite structure corresponding (002) peak for undoped and doped ZnO thin films. The transmittance of the films was above 80% and the band gap of the film varies from 3.21±0.03 eV for undoped and doped ZnO. The minimum resistivity of NZO thin films was obtained as 0.473 Ω cm for the 4 at% of nitrogen (N) doping with a mobility of 1.995 cm{sup 2}/V s. The NZO thin films showed p-type conductivity at 2 and 3 at% of N doping. The AC conductivity measurements that were carried out in the frequency range 10 kHz to 0.1 MHz showed localized conduction in the NZO thin films. These highly transparent ZnO films can be used as a possible window layer in solar cells.

  6. Investigation of sensitivity and selectivity of ZnO thin film to volatile organic compounds

    Science.gov (United States)

    Teimoori, F.; Khojier, K.; Dehnavi, N. Z.

    2017-06-01

    This research addresses a detailed study on the sensitivity and selectivity of ZnO thin film to volatile organic compound (VOC) vapors that can be used for the development of VOC sensors. The ZnO thin film of 100 nm thickness was prepared by post-annealing of e-beam evaporated Zn thin film. The sample was structurally, morphologically, and chemically characterized by X-ray diffraction and field emission scanning electron microscopy analyses. The sensitivity, selectivity, and detection limit of the sample were tested with respect to a wide range of common VOC vapors, including acetone, formaldehyde, acetic acid, formic acid, acetylene, toluene, benzene, ethanol, methanol, and isopropanol in the temperature range of 200-400 °C. The results show that the best sensitivity and detection limit of the sample are related to acetone vapor in the studied temperature range. The ZnO thin film-based acetone sensor also shows a good reproducibility and stability at the operating temperature of 280 °C.

  7. Electrosynthesis and characterization of ZnO nanoparticles as inorganic component in organic thin-film transistor active layers

    International Nuclear Information System (INIS)

    Picca, Rosaria Anna; Sportelli, Maria Chiara; Hötger, Diana; Manoli, Kyriaki; Kranz, Christine; Mizaikoff, Boris; Torsi, Luisa; Cioffi, Nicola

    2015-01-01

    Highlights: • PSS-capped ZnO NPs were synthesized via a green electrochemical-thermal method • The influence of electrochemical conditions and temperature was studied • Spectroscopic data show that PSS functionalities are retained in the annealed NPs • Nanostructured ZnO improved the performance of P3HT-based thin film transistors - Abstract: ZnO nanoparticles have been prepared via a green electrochemical synthesis method in the presence of a polymeric anionic stabilizer (poly-sodium-4-styrenesulfonate, PSS), and then applied as inorganic component in poly-3-hexyl-thiophene thin-film transistor active layers. Different parameters (i.e. current density, electrolytic media, PSS concentration, and temperature) influencing nanoparticle synthesis have been studied. The resulting nanomaterials have been investigated by transmission electron microscopy (TEM) and spectroscopic techniques (UV-Vis, infrared, and x-ray photoelectron spectroscopies), assessing the most suitable conditions for the synthesis and thermal annealing of nanostructured ZnO. The proposed ZnO nanoparticles have been successfully coupled with a poly-3-hexyl-thiophene thin-film resulting in thin-film transistors with improved performance.

  8. Correlation between structural and electrical properties of ZnO thin films

    International Nuclear Information System (INIS)

    Asadov, A.; Gao, W.; Li, Z.; Lee, J.; Hodgson, M.

    2005-01-01

    Thin ZnO films were deposited by radio frequency (r.f.) and direct current (d.c.) magnetron sputtering techniques onto glass substrates. Microstructural and electrical properties of ZnO films were studied using X-ray diffractometer (XRD), scanning electron microscope (SEM) and resistivity measurements. It was found that the size of the crystallites in the d.c. deposited films increased with increasing film thickness, while the crystallite size of r.f. deposited films remained unchanged. The d.c. deposited grains also had much stronger orientation related to the substrate than the r.f. films. XRD data indicated that the thin films with d<350 nm for r.f. and <750 nm for d.c. films have a very high degree of ZnO nonstoichiometry. This agreed well with the conductivity measurements and R(T) behaviour of the films with different resistance R. It was also found that the electrical resistivity of the samples increased exponentially with the thickness of films

  9. Combined effect of oxygen deficient point defects and Ni doping in radio frequency magnetron sputtering deposited ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Saha, B., E-mail: biswajit.physics@gmail.com [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India); Department of Physics, National Institute of Technology Agartala, Jirania 799046, Tripura (India); Das, N.S.; Chattopadhyay, K.K. [Thin Film and Nano Science Laboratory, Department of Physics, Jadavpur University, 700 032 Kolkata (India)

    2014-07-01

    Ni doped ZnO thin films with oxygen deficiency have been synthesized on glass substrates by radio frequency magnetron sputtering technique using argon plasma. The combined effect of point defects generated due to oxygen vacancies and Ni doping on the optical and electrical properties of ZnO thin films has been studied in this work. Ni doping concentrations were varied and the structural, optical and electrical properties of the films were studied as a function of doping concentrations. The films were characterized with X-ray diffractometer, UV–Vis–NIR spectrophotometer, X-ray photoelectron spectroscopy, atomic force microscopy and electrical conductivity measurements. Oxygen deficient point defects (Schottky defects) made the ZnO thin film highly conducting while incorporation of Ni dopant made it more functional regarding their electrical and optical properties. The films were found to have tunable electrical conductivity with Ni doping concentrations. - Highlights: • ZnO thin films prepared by radio frequency magnetron sputtering technique • Synthesis process was stimulated to introduce Schottky-type point defects. • Point defects and external doping of Ni made ZnO thin films more functional. • Point defect induced high electrical conductivity in ZnO thin film. • Significant shift in optical bandgap observed in ZnO with Ni doping concentrations.

  10. Interfacial passivation of CdS layer to CdSe quantum dots-sensitized electrodeposited ZnO nanowire thin films

    International Nuclear Information System (INIS)

    Zhang, Jingbo; Sun, Chuanzhen; Bai, Shouli; Luo, Ruixian; Chen, Aifan; Sun, Lina; Lin, Yuan

    2013-01-01

    ZnO porous thin films with nanowire structure were deposited by the one-step electrochemical deposition method. And a CdS layer was coated on the as-deposited ZnO nanowire thin films by successive ionic layer adsorption and reaction (SILAR) method to passivate surface states. Then the films were further sensitized by CdSe quantum dots (QDs) to serve as a photoanode for fabricating quantum dots-sensitized solar cells (QDSSCs). The effect of the CdS interfacial passivation layer on the performance of the QDSSCs was systematically investigated by varying the SILAR cycle number and heating the passivation layer. The amorphous CdS layer with an optimized thickness can effectively suppress the recombination of the injected electrons with holes on QDs and the redox electrolyte. The newly formed CdS layer on the surface of the ZnO nanowire thin film obviously prolongs the electron lifetime in the passivated ZnO nanoporous thin film because of the lower surface trap density in the ZnO nanowires after CdS deposition, which is favorable to the higher short-circuit photocurrent density (J sc ). For the CdSe QDs-sensitized ZnO nanoporous thin film with the interfacial passivation layer, the J sc and conversion efficiency can reach a maximum of 8.36 mA cm −2 and 2.36%, respectively. The conversion efficiency was improved by 83.47% compared with that of the cell based on the CdSe QDs-sensitized ZnO nanoporous thin film without CdS interfacial passivation (0.39%)

  11. Effect of R.F. Power to the Structural Properties of ZnO Thin Films Deposited by Magnetron Sputtering

    International Nuclear Information System (INIS)

    Sin, N.D.M.; Rusop, M.

    2011-01-01

    The effect of RF power variation (100 watt∼400 watt ) on the zinc oxide (ZnO) thin films electrical, optical and structural properties were examined using current voltage (I-V) measurement, UV-Vis-NIR spectrophotometer, x-ray diffraction (XRD) and atomic force microscope (AFM). ZnO thin films were prepared at room temperature in pure argon atmosphere by a RF magnetron sputtering using ZnO target. The resistivity of thin film show the lowest at 300 watt. The absorption coefficient spectra obtained from UV-Vis-NIR spectrophotometer measurement show all films have low absorbance in visible and near infrared (IR) region but have high UV absorption properties using UV-VIS spectrophotometer (JASCO 670) . Highly oriented ZnO thin films [002] direction were obtained by using Rigaku Ultima IV. (author)

  12. A Comparative Study on Structural and Optical Properties of ZnO Micro-Nanorod Arrays Grown on Seed Layers Using Chemical Bath Deposition and Spin Coating Methods

    Directory of Open Access Journals (Sweden)

    Sibel MORKOÇ KARADENİZ

    2016-11-01

    Full Text Available In this study, Zinc Oxide (ZnO seed layers were prepared on Indium Tin Oxide (ITO substrates by using Chemical Bath Deposition (CBD method and Sol-gel Spin Coating (SC method. ZnO micro-nanorod arrays were grown on ZnO seed layers by using Hydrothermal Synthesis method. Seed layer effects of structural and optical properties of ZnO arrays were characterized. X-ray diffractometer (XRD, Scanning Electron Microscopy (SEM and Ultraviolet Visible (UV-Vis Spectrometer were used for analyses. ZnO micro-nanorod arrays consisted of a single crystalline wurtzite ZnO structure for each seed layer. Besides, ZnO rod arrays were grown smoothly and vertically on SC seed layer, while ZnO rod arrays were grown randomly and flower like structures on CBD seed layer. The optical absorbance peaks found at 422 nm wavelength in the visible region for both ZnO arrays. Optical bandgap values were determined by using UV-Vis measurements at 3.12 and 3.15 eV for ZnO micro-nanorod arrays on CBD seed layer and for ZnO micro-nanorod arrays on SC-seed layer respectively.DOI: http://dx.doi.org/10.5755/j01.ms.22.4.13443

  13. Investigation of thin ZnO layers in view of laser desorption-ionization

    Energy Technology Data Exchange (ETDEWEB)

    Grechnikov, A A; Borodkov, A S [Vernadsky Institute of Geochemistry and Analytical Chemistry, Russian Academy of Sciences, 19 Kosygin Str., 119991 Moscow (Russian Federation); Georgieva, V B [Georgi Nadjakov Institute of Solid State Physics, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee, 1784 Sofia (Bulgaria); Alimpiev, S S; Nikiforov, S M; Simanovsky, Ya O [General Physics Institute, Russian Academy of Sciences, 38 Vavilov Str., 119991 Moscow (Russian Federation); Dimova-Malinovska, D; Angelov, O I, E-mail: lazarova@issp.bas.b [Laboratory for Solar Energy and New Energy Sources, Bulgarian Academy of Sciences, 72 Tzarigradsko Chaussee, 1784 Sofia (Bulgaria)

    2010-04-01

    Thin zinc oxide films (ZnO) were developed as a matrix-free platform for surface assisted laser desorption-ionization (SALDI) time-of-flight mass spectrometry. The ZnO films were deposited by RF magnetron sputtering of ZnO ceramic targets in Ar atmospheres on monocrystalline silicon. The generation under UV (355 nm) laser irradiation of positive ions of atenolol, reserpine and gramicidin S from the ZnO layers deposited was studied. All analytes tested were detected as protonated molecules with no or very structure-specific fragmentation. The mass spectra obtained showed low levels of chemical background noise. All ZnO films studied exhibited high stability and good reproducibility. The detection limits for test analytes are in the 10 femtomol range.

  14. Effects of preannealing temperature of ZnO thin films on the performance of dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Kao, M.C.; Chen, H.Z.; Young, S.L. [Hsiuping Institute of Technology, Department of Electronic Engineering, Taichung (China)

    2010-03-15

    The preferred (002) orientation zinc oxide (ZnO) nanocrystalline thin films have been deposited on FTO-coated glass substrates by sol-gel spin-coating technology and rapid thermal annealing for use in dye-sensitized solar cells (DSSC). The effects of preannealing temperature (100 and 300 C) on the microstructure, morphology and optical properties of ZnO thin films were studied. The ZnO thin films were characterized by X-ray diffraction (XRD), scanning electron microscopic (SEM) and Brunauer-Emmett-Teller (BET) analysis. The photoelectric performance of DSSC was studied by I-V curve and the incident photon-to-current conversion efficiency (IPCE), respectively. From the results, the intensities of (002) peaks of ZnO thin films increases with increasing preannealing temperature from 100 C to 300 C. The increase in pore size and surface area of ZnO films crystallized at the increased preannealing temperature contributed to the improvement on the absorption of N3 dye onto the films, the short-circuit photocurrent (J{sub sc}) and open-circuit voltage (V{sub oc}) of DSSC. The higher efficiency ({eta}) of 2.5% with J{sub sc} and V{sub oc} of 8.2 mA/cm{sup 2} and 0.64 V, respectively, was obtained by the ZnO film preannealed at 300 C. (orig.)

  15. Influence of PANI Additions on Methanol Sensing Properties of ZnO Thin Films

    International Nuclear Information System (INIS)

    Mohammad Hafizuddin Jumali; Norhashimah Ramli; Izura Izzuddin; Muhammad Yahaya; Muhamad Mat Salleh

    2011-01-01

    The influence of PANI additions on methanol sensing properties of ZnO thin films at room temperature had been investigated. Commercial poly aniline powder (PANI) was mixed into 3 mL ZnO solution in five different weight percentages namely 1.25, 2.50, 3.75, 5.00 and 6.25 % to obtain ZnO/ PANI composite solutions. These solutions were spin coated onto glass substrate to form thin films. Microstructural studies by FESEM indicated that ZnO/ PANI films showed porous structures with nano size grains. The thickness of the film increased from 55 to 256 nm, proportionate to increment of PANI. The presence of 2 adsorption peaks at ∼310 nm and ∼610 nm in UV-Vis spectrum proved that addition of PANI has modified the adsorption peak of ZnO film. Methanol vapour detection showed that addition of PANI into ZnO dramatically improved the sensing properties of the sensor. The sensors also exhibited good repeatability and reversibility. Sensor with the amount of PANI of 3.75 wt % exhibited the highest sensitivity with response and recovery time was about 10 and 80 s, respectively. The possible sensing mechanism of the sensor was also discussed in this article. (author)

  16. Effects of Post Heat Treatments on ZnO Thin-Films Grown on Zn-coated Teflon Substrates

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ikhyun; Nam, Giwoong; Lee, Cheoleon; Kim, Dongwhan; Choi, Hyonkwang; Kim, Yangsoo; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of); Kim, Jin Soo [Chonbuk National University, Jeonju (Korea, Republic of); Kim, Jong Su [Yeungnam University, Gyeongsan (Korea, Republic of); Son, Jeong-Sik [Kyungwoon University, Gumi (Korea, Republic of)

    2015-06-15

    ZnO thin films were first grown on Zn-coated Teflon substrates using a spin-coating method, with various post-heating temperatures. The structural and optical properties of the ZnO thin films were then investigated using field-effect scanning-electron microscopy, X-ray diffractometry, and photoluminescence (PL) spectroscopy. The surface morphology of these ZnO thin films exhibited dendritic structures. With increasing post-heating temperature, all samples preferentially exhibited preferential c-axis orientation and increased residual tensile stress. All of the films exhibited preferential c-axis orientation, and the residual tensile stress of those increased with increasing post-heating temperature. The near-band-edge emission (NBE) peaks were red-shifted after post-heating treatment at 400 ℃. The intensity of the deep-level emission (DLE) peaks gradually decreased with increasing post- heating temperature. Moreover, the narrowest ‘full width at half maximum’ (FWHM) and the highest intensity ratio of the NBE to the DLE for thin films, were observed after post-heating at 400 ℃. The ZnO thin films fabricated with the 400 ℃ post-heating process provided the highest crystallinity and optical properties.

  17. Formation mechanisms of metallic Zn nanodots by using ZnO thin films deposited on n-Si substrates

    International Nuclear Information System (INIS)

    Yuk, J. M.; Lee, J. Y.; Kim, Y.; No, Y. S.; Kim, T. W.; Choi, W. K.

    2010-01-01

    High-resolution transmission electron microscopy and energy dispersive x-ray spectroscopy results showed that metallic Zn nanodots (NDs) were fabricated through transformation of ZnO thin films by deposition of SiO x on ZnO/n-Si (100) heterostructures. The Zn NDs with various sizes and densities were formed due to the occurrence of the mass diffusion of atoms along the grain boundaries in the ZnO thin films. The fabrication mechanisms of metallic Zn NDs through transformation of ZnO thin films deposited on n-Si substrates are described on the basis of the experimental results.

  18. Piezoelectricity and charge trapping in ZnO and Co-doped ZnO thin films

    Directory of Open Access Journals (Sweden)

    Domenico D’Agostino

    2017-05-01

    Full Text Available Piezoelectricity and charge storage of undoped and Co-doped ZnO thin films were investigated by means of PiezoResponse Force Microscopy and Kelvin Probe Force Microscopy. We found that Co-doped ZnO exhibits a large piezoelectric response, with the mean value of piezoelectric matrix element d33 slightly lower than in the undoped sample. Moreover, we demonstrate that Co-doping affects the homogeneity of the piezoelectric response, probably as a consequence of the lower crystalline degree exhibited by the doped samples. We also investigate the nature of the interface between a metal electrode, made up of the PtIr AFM tip, and the films as well as the phenomenon of charge storage. We find Schottky contacts in both cases, with a barrier value higher in PtIr/ZnO than in PtIr/Co-doped ZnO, indicating an increase in the work function due to Co-doping.

  19. Structural, optical and magnetic properties of Mn doped ZnO thin films prepared by pulsed laser deposition

    Energy Technology Data Exchange (ETDEWEB)

    Aravind, Arun, E-mail: aruncusat@gmail.com [Nanophotonic and Optoelectronic Devices Laboratory, Department of Physics, Cochin University of Science and Technology, Kochi 682 022, Kerala (India); Jayaraj, M.K., E-mail: mkj@cusat.ac.in [Nanophotonic and Optoelectronic Devices Laboratory, Department of Physics, Cochin University of Science and Technology, Kochi 682 022, Kerala (India); Kumar, Mukesh; Chandra, Ramesh [Nano Science Laboratory, Institute Instrumentation Centre, IIT Roorkee, Roorkee 247 667, Uttarakhand (India)

    2012-08-01

    Highlights: Black-Right-Pointing-Pointer Defect induced Raman active modes in Mn doped ZnO thin films. Black-Right-Pointing-Pointer Room temperature ferromagnetism. Black-Right-Pointing-Pointer Morphological variations of ZnO thin films with Mn doping. Black-Right-Pointing-Pointer Variation of refractive index of ZnO thin films with Mn doping. - Abstract: Zn{sub 1-x}Mn{sub x}O thin films were grown by pulsed laser deposition. The phase purity and the structure were confirmed by X-ray diffraction studies. The films have a transmittance more than 80% in the visible region. The refractive index of Zn{sub 0.90}Mn{sub 0.10}O films is found to be 1.77 at 550 nm. The presence of non-polar E{sub 2}{sup high} and E{sub 2}{sup low} Raman modes in thin films indicates that 'Mn' doping does not change the wurtzite structure of ZnO. Apart from the normal modes of ZnO the Zn{sub 1-x}Mn{sub x}O ceramic targets show two additional modes at 332 cm{sup -1} (I{sub 1}) and 524 cm{sup -1} (I{sub 2}). The broad Raman peaks (340-600 cm{sup -1}) observed Zn{sub 0.90}Mn{sub 0.10}O thin films can be deconvoluted into five peaks, denoted as P{sub 1}-P{sub 5}. The possible origins of Raman peaks in Zn{sub 1-x}Mn{sub x}O films are the structural disorder and morphological change caused by the Mn dopant. The B{sub 1}{sup low}, {sup 2}B{sub 1}{sup low}, B{sub 1}{sup high} and A{sub 1}{sup LO} modes as well as the surface phonon mode have been observed in heavily Mn-doped ZnO films. Zn{sub 0.98}Mn{sub 0.02}O thin film shows room temperature ferromagnetism. The saturation magnetic moment of the Zn{sub 0.98}Mn{sub 0.02}O thin film is 0.42{mu}{sub B}/Mn atom. The undoped ZnO film prepared under the same condition shows diamagnetic nature. At higher doping concentrations the formation of Mn clusters suppress the room temperature ferromagnetism in Zn{sub 1-x}Mn{sub x}O thin films and shows paramagnetism. XPS confirms the incorporation of Mn{sup 2+} into the ZnO lattice.

  20. Characterizations of multilayer ZnO thin films deposited by sol-gel spin coating technique

    Directory of Open Access Journals (Sweden)

    M.I. Khan

    Full Text Available In this work, zinc oxide (ZnO multilayer thin films are deposited on glass substrate using sol-gel spin coating technique and the effect of these multilayer films on optical, electrical and structural properties are investigated. It is observed that these multilayer films have great impact on the properties of ZnO. X-ray Diffraction (XRD confirms that ZnO has hexagonal wurtzite structure. Scanning Electron Microscopy (SEM showed the crack-free films which have uniformly distributed grains structures. Both micro and nano particles of ZnO are present on thin films. Four point probe measured the electrical properties showed the decreasing trend between the average resistivity and the number of layers. The optical absorption spectra measured using UV–Vis. showed the average transmittance in the visible region of all films is 80% which is good for solar spectra. The performance of the multilayer as transparent conducting material is better than the single layer of ZnO. This work provides a low cost, environment friendly and well abandoned material for solar cells applications. Keywords: Multilayer films, Semiconductor, ZnO, XRD, SEM, Optoelectronic properties

  1. Homogeneous vertical ZnO nanorod arrays with high conductivity on an in situ Gd nanolayer

    KAUST Repository

    Flemban, Tahani H.; Singaravelu, Venkatesh; Devi, Assa Aravindh Sasikala; Roqan, Iman S.

    2015-01-01

    We demonstrate a novel, one-step, catalyst-free method for the production of size-controlled vertical highly conductive ZnO nanorod (NR) arrays with highly desirable characteristics by pulsed laser deposition using a Gd-doped ZnO target. Our study

  2. ALD grown nanostructured ZnO thin films: Effect of substrate temperature on thickness and energy band gap

    Directory of Open Access Journals (Sweden)

    Javed Iqbal

    2016-10-01

    Full Text Available Nanostructured ZnO thin films with high transparency have been grown on glass substrate by atomic layer deposition at various temperatures ranging from 100 °C to 300 °C. Efforts have been made to observe the effect of substrate temperature on the thickness of the deposited thin films and its consequences on the energy band gap. A remarkably high growth rate of 0.56 nm per cycle at a substrate temperature of 200 °C for ZnO thin films have been achieved. This is the maximum growth rate for ALD deposited ZnO thin films ever reported so far to the best of our knowledge. The studies of field emission scanning electron microscopy and X-ray diffractometry patterns confirm the deposition of uniform and high quality nanosturtured ZnO thin films which have a polycrystalline nature with preferential orientation along (100 plane. The thickness of the films deposited at different substrate temperatures was measured by ellipsometry and surface profiling system while the UV–visible and photoluminescence spectroscopy studies have been used to evaluate the optical properties of the respective thin films. It has been observed that the thickness of the thin film depends on the substrate temperatures which ultimately affect the optical and structural parameters of the thin films.

  3. Temperature dependent optical properties of ZnO thin film using ellipsometry and photoluminescence

    Science.gov (United States)

    Bouzourâa, M.-B.; Battie, Y.; Dalmasso, S.; Zaïbi, M.-A.; Oueslati, M.; En Naciri, A.

    2018-05-01

    We report the temperature dependence of the dielectric function, the exciton binding energy and the electronic transitions of crystallized ZnO thin film using spectroscopic ellipsometry (SE) and photoluminescence (PL). ZnO layers were prepared by sol-gel method and deposited on crystalline silicon (Si) by spin coating technique. The ZnO optical properties were determined between 300 K and 620 K. Rigorous study of optical responses was achieved in order to demonstrate the quenching exciton of ZnO as a function of temperature. Numerical technique named constrained cubic splines approximation (CCS), Tauc-Lorentz (TL) and Tanguy dispersion models were selected for the ellipsometry data modeling in order to obtain the dielectric function of ZnO. The results reveals that the exciton bound becomes widely flattening at 470 K on the one hand, and on the other that the Tanguy dispersion law is more appropriate for determining the optical responses of ZnO thin film in the temperature range of 300 K-420 K. The Tauc-Lorentz, for its part, reproduces correctly the ZnO dielectric function in 470 K-620 K temperature range. The temperature dependence of the electronic transition given by SE and PL shows that the exciton quenching was observed in 420 K-∼520 K temperature range. This quenching effect can be explained by the equilibrium between the Coulomb force of exciton and its kinetic energy in the film. The kinetic energy was found to induce three degrees of freedom of the exciton.

  4. Chemical route to synthesis of mesoporous ZnO thin films and their liquefied petroleum gas sensor performance

    International Nuclear Information System (INIS)

    Dhawale, D.S.; Lokhande, C.D.

    2011-01-01

    Highlights: → Low temperature synthesis of mesoporous ZnO thin films by CBD method with urea containing bath. → Wurtzite crystal structure of mesoporous ZnO has been confirmed from the XRD study. → SEM images reveal the formation of hydrophobic mesoporous ZnO thin films. → Maximum LPG response of 52% has been achieved with high stability. - Abstract: In the present work, we report base free chemical bath deposition (CBD) of mesoporous zinc oxide (ZnO) thin films from urea containing bath for liquefied petroleum gas (LPG) sensor application. Mesoporous morphology with average pore size ∼2 μm and wurtzite crystal structure are confirmed from scanning electron microscopy (SEM) and X-ray diffraction (XRD) analysis. The surface of ZnO is hydrophobic with water contact angle 128 ± 1 o . Optical study reveals the presence of direct bad gap with energy 3.24 eV. The gas sensing study reveals the mesoporous ZnO is highly selective towards LPG as compared with CO 2 and maximum LPG response of 52% is achieved upon the exposure of 3900 ppm LPG at 573 K as well as good reproducibility and short response/recovery times.

  5. Highly stable field emission from ZnO nanowire field emitters controlled by an amorphous indium–gallium–zinc-oxide thin film transistor

    Science.gov (United States)

    Li, Xiaojie; Wang, Ying; Zhang, Zhipeng; Ou, Hai; She, Juncong; Deng, Shaozhi; Xu, Ningsheng; Chen, Jun

    2018-04-01

    Lowering the driving voltage and improving the stability of nanowire field emitters are essential for them to be applied in devices. In this study the characteristics of zinc oxide (ZnO) nanowire field emitter arrays (FEAs) controlled by an amorphous indium–gallium–zinc-oxide thin film transistor (a-IGZO TFT) were studied. A low driving voltage along with stabilization of the field emission current were achieved. Modulation of field emission currents up to three orders of magnitude was achieved at a gate voltage of 0–32 V for a constant anode voltage. Additionally, a-IGZO TFT control can dramatically reduce the emission current fluctuation (i.e., from 46.11 to 1.79% at an emission current of ∼3.7 µA). Both the a-IGZO TFT and ZnO nanowire FEAs were prepared on glass substrates in our research, demonstrating the feasibility of realizing large area a-IGZO TFT-controlled ZnO nanowire FEAs.

  6. Annealing effect on the structural, morphological and electrical properties of TiO2/ZnO bilayer thin films

    Science.gov (United States)

    Khan, M. I.; Imran, S.; Shahnawaz; Saleem, Muhammad; Ur Rehman, Saif

    2018-03-01

    The effect of annealing temperature on the structural, morphological and electrical properties of TiO2/ZnO (TZ) thin films has been observed. Bilayer thin films of TiO2/ZnO are deposited on FTO glass substrate by spray pyrolysis method. After deposition, these films are annealed at 573 K, 723 K and 873 K. XRD shows that TiO2 is present in anatase phase only and ZnO is present in hexagonal phase. No other phases of TiO2 and ZnO are present. Also, there is no evidence of other compounds like Zn-Ti etc. It also shows that the average grain size of TiO2/ZnO films is increased by increasing annealing temperature. AFM (Atomic force microscope) showed that the average roughness of TiO2/ZnO films is decreased at temperature 573-723 K and then increased at 873 K. The calculated average sheet resistivity of thin films annealed at 573 K, 723 K and 873 K is 152.28 × 102, 75.29 × 102 and 63.34 × 102 ohm-m respectively. This decrease in sheet resistivity might be due to the increment of electron concentration with increasing thickness and the temperature of thin films.

  7. Effect of different sol concentrations on the properties of nanocrystalline ZnO thin films grown on FTO substrates by sol-gel spin-coating

    International Nuclear Information System (INIS)

    Kim, Ikhyun; Kim, Younggyu; Nam, Giwoong; Kim, Dongwan; Park, Minju; Kim, Haeun; Lee, Wookbin; Leem, Jaeyoung; Kim, Jongsu; Kim, Jin Soo

    2014-01-01

    Nanocrystalline ZnO thin films grown on fluorine-doped tinoxide (FTO) substrates were fabricated using the spin-coating method. The structural and the optical properties of the ZnO thin films prepared using different sol concentrations were investigated by using field-emission scanning electron microscopy (FE-SEM), X-ray diffractometry (XRD), photoluminescence (PL) measurements, and ultraviolet-visible (UV-vis) spectrometry. The surface morphology of the ZnO thin films, as observed in the SEM images, exhibited a mountain-chain structure. XRD results indicated that the thin films were preferentially orientated along the direction of the c-axis and that the grain size of the ZnO thin films increased with increasing sol concentration. The PL spectra showed a strong ultraviolet emission peak at 3.22 eV and a broad orange emission peak at 2.0 eV. The intensities of deep-level emission (DLE) gradually increased with increasing sol concentration from 0.4 to 1.0 M. The transmittance spectra of the ZnO thin films showed that the ZnO thin films were transparent (∼85%) in the visible region and exhibited sharp absorption edges at 375 nm. Thus, The Urbach energy of ZnO thin films decreased with increasing sol concentration.

  8. A comparative study of ultraviolet photoconductivity relaxation in zinc oxide (ZnO) thin films deposited by different techniques

    International Nuclear Information System (INIS)

    Yadav, Harish Kumar; Gupta, Vinay

    2012-01-01

    Photoresponse characteristics of ZnO thin films deposited by three different techniques namely rf diode sputtering, rf magnetron sputtering, and electrophoretic deposition has been investigated in the metal-semiconductor-metal (MSM) configuration. A significant variation in the crystallinity, surface morphology, and photoresponse characteristics of ZnO thin film with change in growth kinetics suggest that the presence of defect centers and their density govern the photodetector relaxation properties. A relatively low density of traps compared to the true quantum yield is found very crucial for the realization of practical ZnO thin film based ultraviolet (UV) photodetector.

  9. A comparative study of ultraviolet photoconductivity relaxation in zinc oxide (ZnO) thin films deposited by different techniques

    Energy Technology Data Exchange (ETDEWEB)

    Yadav, Harish Kumar; Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi 110 007 (India)

    2012-05-15

    Photoresponse characteristics of ZnO thin films deposited by three different techniques namely rf diode sputtering, rf magnetron sputtering, and electrophoretic deposition has been investigated in the metal-semiconductor-metal (MSM) configuration. A significant variation in the crystallinity, surface morphology, and photoresponse characteristics of ZnO thin film with change in growth kinetics suggest that the presence of defect centers and their density govern the photodetector relaxation properties. A relatively low density of traps compared to the true quantum yield is found very crucial for the realization of practical ZnO thin film based ultraviolet (UV) photodetector.

  10. Synergistic effect of indium and gallium co-doping on the properties of RF sputtered ZnO thin films

    Science.gov (United States)

    Shaheera, M.; Girija, K. G.; Kaur, Manmeet; Geetha, V.; Debnath, A. K.; Karri, Malvika; Thota, Manoj Kumar; Vatsa, R. K.; Muthe, K. P.; Gadkari, S. C.

    2018-04-01

    ZnO thin films were synthesized using RF magnetron sputtering, with simultaneous incorporation of Indium (In) and Gallium (Ga). The structural, optical, chemical composition and surface morphology of the pure and co-doped (IGZO) thin films were characterized by X-Ray diffraction (XRD), UV-visible spectroscopy, Field Emission Scanning Electron Microscopy (FESEM), and Raman spectroscopy. XRD revealed that these films were oriented along c-axis with hexagonal wurtzite structure. The (002) diffraction peak in the co-doped sample was observed at 33.76° with a slight shift towards lower 2θ values as compared to pure ZnO. The surface morphology of the two thin films was observed to differ. For pure ZnO films, round grains were observed and for IGZO thin films round as well as rod type grains were observed. All thin films synthesized show excellent optical properties with more than 90% transmission in the visible region and band gap of the films is observed to decrease with co-doping. The co doping of In and Ga is therefore expected to provide a broad range optical and physical properties of ZnO thin films for a variety of optoelectronic applications.

  11. Characterization of ZnO thin films grown on different p-Si substrate elaborated by solgel spin-coating method

    Energy Technology Data Exchange (ETDEWEB)

    Chebil, W., E-mail: Chbil.widad@live.fr [Laboratoire Physico-chimie des Matériaux, Unité de Service Commun de Recherche “High resolution X-ray diffractometer”, Département de Physique, Université de Monastir, Faculté des Sciences de Monastir, Avenue de l’Environnement, 5019 Monastir (Tunisia); Fouzri, A. [Laboratoire Physico-chimie des Matériaux, Unité de Service Commun de Recherche “High resolution X-ray diffractometer”, Département de Physique, Université de Monastir, Faculté des Sciences de Monastir, Avenue de l’Environnement, 5019 Monastir (Tunisia); Institut Supérieur des Sciences Appliquées et de Technologie de Sousse, Université de Sousse (Tunisia); Fargi, A. [Laboratoire de Microélectronique et Instrumentation, Faculté des Sciences de Monastir, Université de Monastir, Avenue de l’environnement, 5019 Monastir (Tunisia); Azeza, B.; Zaaboub, Z. [Laboratoire Micro-Optoélectroniques et Nanostructures, Faculté des Sciences de Monastir, Université de Monastir, Avenue de l' environnement, 5019 Monastir (Tunisia); and others

    2015-10-15

    Highlights: • High quality ZnO thin films grown on different p-Si substrates were successful obtained by sol–gel process. • PL measurement revealed that ZnO thin film grown on porous Si has the better optical quality. • I–V characteristics for all heterojunctions exhibit successful diode formation. • The diode ZnO/PSi shows a better photovoltaic effect under illumination with a maximum {sub Voc} of 0.2 V. - Abstract: In this study, ZnO thin films are deposited by sol–gel technique on p-type crystalline silicon (Si) with [100] orientation, etched silicon and porous silicon. The structural analyses showed that the obtained thin films were polycrystalline with a hexagonal wurtzite structure and preferentially oriented along the c-axis direction. Morphological study revealed the presence of rounded and facetted grains irregularly distributed on the surface of all samples. PL spectra at room temperature revealed that ZnO thin film grown on porous Si has a strong UV emission with low defects in the visible region comparing with ZnO grown on plat Si and etched Si surface. The heterojunction parameters were evaluated from the (I–V) under dark and illumination at room temperature. The ideality factor, barrier height and series resistance of heterojunction grown on different p-Si substrates are determined by using different methods. Best electrical properties are obtained for ZnO layer deposited on porous silicon.

  12. Properties of ZnO Nano rods Arrays Growth via Low Temperature Hydrothermal Reaction

    International Nuclear Information System (INIS)

    Nur Syafinaz Ridhuan; Zainovia Lockman; Azlan Abdul Aziz; Azlan Abdul Aziz; Khairunisak Abdul Razak; Khairunisak Abdul Razak

    2011-01-01

    This work describes properties of 1- D ZnO nano rods (NRs) arrays growth using low temperature hydrothermal method on seeded substrate. The properties of ZnO seed were studied by varying annealed temperature from 250-450 degree Celsius. The optimum oxidation temperature to produce seeded ZnO template was 400 degree Celsius. The formations of ZnO NRs were further studied by varying hydrothermal reaction growth time from 1 to 24 hours. I-V characteristic of ZnO NRs photodetector in dark, ambient light and UV light were also studied. The change in the photoconductivity under UV illumination was found to be 1 order higher in magnitude compared to dark current and ambient light. With an incident wavelength of 370 nm and applied bias of 3V, the responsivity of photodetector was 5.0 mA/ W, which was higher compared to other reported works. The increase of photosensitivity indicated that the produced ZnO NRs were suitable for UV photodetector applications.(author)

  13. Effects of Post- Heat Treatment of Nanocrystalline ZnO Thin Films deposited on Zn-Deposited FTO Substrates

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Ikhyun; Kim, Younggyu; Nam, Giwoong; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of)

    2015-10-15

    The effects of heat-treatment temperature on the structural and optical properties of ZnO thin films were investigated with field-effect scanning electron microscopy (SEM), X-ray diffraction analysis, and photoluminescence (PL) measurements. The ZnO thin films were grown on Zn-deposited fluorine-doped tin oxide substrates by sol-gel spin coating. The SEM images of the samples showed that their surfaces had a mountain-chain-like structure. The film annealed at 400 ℃ had the highest degree of alignment along the c-axis, and its residual stress was close to zero. The PL spectra of the ZnO thin films consisted of sharp near-band-edge emissions (NBE) and broad deep-level emissions (DLE) in the visible range. The DLE peaks exhibited a green-to-red shift with an increase in the temperature. The highest INBE/IDLE ratio was observed in the film annealed at 400 ℃. Thus, the optimal temperature for growing high-quality ZnO thin films on Zn-deposited FTO substrates is 400 ℃.

  14. Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Yadav, Harish Kumar [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Sreenivas, K [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India); Katiyar, R S [Department of Physics, University of Puerto Rico, San Juan, PR 00931-3343 (Puerto Rico); Gupta, Vinay [Department of Physics and Astrophysics, University of Delhi, Delhi-110007 (India)

    2007-10-07

    We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm{sup -1}. The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A{sub 1} (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries.

  15. Defect induced activation of Raman silent modes in rf co-sputtered Mn doped ZnO thin films

    International Nuclear Information System (INIS)

    Yadav, Harish Kumar; Sreenivas, K; Katiyar, R S; Gupta, Vinay

    2007-01-01

    We study the influence of Mn doping on the vibrational properties of rf sputtered ZnO thin films. Raman spectra of the Mn doped ZnO samples reveal two additional vibrational modes, in addition to the host phonon modes, at 252 and 524 cm -1 . The intensity of the additional modes increases continuously with Mn concentration in ZnO and can be used as an indication of Mn incorporation in ZnO. The modes are assigned to the activation of ZnO silent modes due to relaxation of Raman selection rules produced by the breakdown of the translational symmetry of the crystal lattice with the incorporation of Mn at the Zn site. Furthermore, the A 1 (LO) mode is observed with very high intensity in the Raman spectra of undoped ZnO thin film and is attributed to the built-in electric field at the grain boundaries

  16. Slow positron beam study of hydrogen ion implanted ZnO thin films

    Science.gov (United States)

    Hu, Yi; Xue, Xudong; Wu, Yichu

    2014-08-01

    The effects of hydrogen related defect on the microstructure and optical property of ZnO thin films were investigated by slow positron beam, in combination with x-ray diffraction, infrared and photoluminescence spectroscopy. The defects were introduced by 90 keV proton irradiation with doses of 1×1015 and 1×1016 ions cm-2. Zn vacancy and OH bonding (VZn+OH) defect complex were identified in hydrogen implanted ZnO film by positron annihilation and infrared spectroscopy. The formation of these complexes led to lattice disorder in hydrogen implanted ZnO film and suppressed the luminescence process.

  17. Cu{sub 2}ZnSn(S,Se){sub 4} from Cu{sub x}SnS{sub y} nanoparticle precursors on ZnO nanorod arrays

    Energy Technology Data Exchange (ETDEWEB)

    Kavalakkatt, Jaison, E-mail: jai.k@web.de [Helmholtz-Zentrum Berlin fuer Materialien und Energie, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Freie Universitaet Berlin, Berlin (Germany); Lin, Xianzhong; Kornhuber, Kai [Helmholtz-Zentrum Berlin fuer Materialien und Energie, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Kusch, Patryk [Freie Universitaet Berlin, Berlin (Germany); Ennaoui, Ahmed [Helmholtz-Zentrum Berlin fuer Materialien und Energie, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Reich, Stephanie [Freie Universitaet Berlin, Berlin (Germany); Lux-Steiner, Martha Ch. [Helmholtz-Zentrum Berlin fuer Materialien und Energie, Hahn-Meitner-Platz 1, D-14109 Berlin (Germany); Freie Universitaet Berlin, Berlin (Germany)

    2013-05-01

    Solar cells with Cu{sub 2}ZnSnS{sub 4} absorber thin films have a potential for high energy conversion efficiencies with earth-abundant and non-toxic elements. In this work the formation of CZTSSe from Cu{sub x}SnS{sub y} nanoparticles (NPs) deposited on ZnO nanorod (NR) arrays as precursors for zinc is investigated. The NPs are prepared using a chemical route and are dispersed in toluene. The ZnO NRs are grown on fluorine doped SnO{sub 2} coated glass substrates by electro deposition method. A series of samples are annealed at different temperatures between 300 °C and 550 °C in selenium containing argon atmosphere. To investigate the products of the reaction between the precursors the series is analyzed by means of X-ray diffraction (XRD) and Raman spectroscopy. The morphology is recorded by scanning electron microscopy (SEM) images of broken cross sections. The XRD measurements and the SEM images show the disappearing of ZnO NRs with increasing annealing temperature. Simultaneously the XRD and Raman measurements show the formation of CZTSSe. The formation of secondary phases and the optimum conditions for the preparation of CZTSSe is discussed. - Highlights: ► Cu{sub x}SnS{sub y} nanoparticles are deposited on ZnO nanorod arrays. ► Samples are annealed at different temperatures (300–550 °C) in Se/Ar-atmosphere. ► Raman spectroscopy, X-ray diffraction and electron microscopy are performed. ► ZnO disappears with increasing annealing temperature. ► With increasing temperature Cu{sub x}SnS{sub y} and ZnO form Cu{sub 2}ZnSn(S,Se){sub 4}.

  18. An approach to fabricating chemical sensors based on ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Park, Jae Young; Song, Dong Eon; Kim, Sang Sub

    2008-01-01

    Vertically and laterally aligned ZnO nanorod arrays were synthesized on Pt-coated Si substrates by catalyst-free metal organic chemical vapor deposition. An approach to fabricating chemical sensors based on the nanorod arrays using a coating-and-etching process with a photo-resist is reported. Tests of the devices as oxygen gas sensors have been performed. Our results demonstrate that the approach holds promise for the realization of sensitive and reliable nanorod array chemical sensors

  19. Radio-frequency magnetron sputtering and wet thermal oxidation of ZnO thin film

    International Nuclear Information System (INIS)

    Liu, H. F.; Chua, S. J.; Hu, G. X.; Gong, H.; Xiang, N.

    2007-01-01

    The authors studied the growth and wet thermal oxidation (WTO) of ZnO thin films using a radio-frequency magnetron sputtering technique. X-ray diffraction reveals a preferred orientation of [1010]ZnO(0002)//[1120]Al 2 O 3 (0002) coexisted with a small amount of ZnO (1011) and ZnO (1013) crystals on the Al 2 O 3 (0001) substrate. The ZnO (1011) and ZnO (1013) crystals, as well as the in-plane preferred orientation, are absent from the growth of ZnO on the GaAs(001) substrate. WTO at 550 deg. C improves the crystalline and the photoluminescence more significantly than annealing in air, N 2 and O 2 ambient; it also tends to convert the crystal from ZnO (1011) and ZnO (1013) to ZnO (0002). The evolution of the photoluminescence upon WTO and annealing reveals that the green and orange emissions, centered at 520 and 650 nm, are likely originated from oxygen vacancies and oxygen interstitials, respectively; while the 420 nm emission, which is very sensitive to the postgrowth thermal processing regardless of the substrate and the ambient gas, is likely originated from the surface-state related defects

  20. Defects related room temperature ferromagnetism in Cu-implanted ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Li, D.; Li, D.K.; Wu, H.Z.; Liang, F.; Xie, W.; Zou, C.W.; Shao, L.X.

    2014-01-01

    Highlights: • Room temperature ferromagnetism was observed in Cu-implanted ZnO nanorod arrays. • Cu-implanted ZnO nanorods show a saturation magnetization value of 1.82 μ B /Cu. • The origin of ferromagnetism can be explained by the defects related bound magnetic polarons. -- Abstract: Room temperature ferromagnetism (FM) was observed in Cu-implanted ZnO nanorod arrays. The implantation dose for Cu ions was 1 × 10 16 cm −2 and the implantation energy was 100 keV. The ion implantation induced defects and disorder has been observed by the XRD, PL and TEM experiments. The PL spectrum revealed a dominant luminescence peaks at 390 nm and a broad and strong green emission at 500–700 nm, which is considered to be related to the ionized oxygen vacancy. Cu-implanted ZnO nanorods annealed at 500 °C show a saturation magnetization value of 1.82 μ B /Cu and a positive coercive field of 68 Oe. The carrier concentration is not much improved after annealing and in the order of 10 16 cm −3 , which suggests that FM does not depend upon the presence of a significant carrier concentration. The origin of ferromagnetism behavior can be explained on the basis of electrons and defects that form bound magnetic polarons, which overlap to create a spin-split impurity band

  1. Temperature dependent optical properties of (002) oriented ZnO thin film using surface plasmon resonance

    Science.gov (United States)

    Saha, Shibu; Mehan, Navina; Sreenivas, K.; Gupta, Vinay

    2009-08-01

    Temperature dependent optical properties of c-axis oriented ZnO thin film were investigated using surface plasmon resonance (SPR) technique. SPR data for double layer (prism-Au-ZnO-air) and single layer (prism-Au-air) systems were taken over a temperature range (300-525 K). Dielectric constant at optical frequency and real part of refractive index of the ZnO film shows an increase with temperature. The bandgap of the oriented ZnO film was found to decrease with rise in temperature. The work indicates a promising application of the system as a temperature sensor and highlights an efficient scientific tool to study optical properties of thin film under varying ambient conditions.

  2. Synthesis and photoluminescence of a full zinc blende phase ZnO nanorod array

    International Nuclear Information System (INIS)

    Zhou Shaomin; Gong Hechun; Zhang Bin; Du Zuliang; Zhang Xingtang; Wu Sixin

    2008-01-01

    A single-crystalline ZnO nanorod array with rectangular cross-sections has been synthesized, in which the as-obtained products are a complete metastable zinc blende (ZB) phase. X-ray powder diffraction, electron microscopy, and elemental maps have been used to show that the ZB-ZnO samples have a lattice constant a = 4.580 A, and are free from contamination by hexagonal wurtzite (HW) ZnO. Based on our experimental data, the associated growth mechanism is tentatively suggested. In addition, the photoluminescence (PL) spectrum (about 400 nm (3.1 eV)) of the as-fabricated ZB-ZnO products was detected; this is the first experimental report of the optical properties of ZB-ZnO nanorod arrays

  3. Study of nanocluster-assembled ZnO thin films by nanocluster-beam deposition

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Zhiwei; Lei, Wei; Zhang, Xiaobing [School of Electronic Science and Engieering, Southeast University, Nanjing (China); Tay, Beng Kang [School of Electronical and Electronic Engineering, Nanyang Technological University, Nanyang (Singapore)

    2012-01-15

    Nanocluster-assembled ZnO thin films were obtained by nanocluster-beam deposition, in which nanoclusters were produced by a magnetron sputtering gas aggregation source. Two kinds of ZnO thin films were obtained using this method with the one grown under the on-line heating temperature of 700 C, and the other grown without on-line heating. Film microstructure and optical properties are investigated by various diagnostic techniques. It was found that both of film microstructure of ZnO thin films keep wurtzite structure as that of ZnO bulk materials. The averaged particle size for the film grown without on-line heating is around 6 nm, which is a little lower than that grown with the on-line heating. It was also found that as increasing the wavelength, both of the absorbance spectra for the films decrease sharply near ultra-visible to extend slowly to the visible and infrared wavelength range. For the film grown without on-line heating, the bandgap energy was estimated to 3.77 eV, while for the film grown with on-line heating, the bandgap energy was redshift to 3.71 eV. Similar behavior was also found for PL spectra analysis, where PL spectrum exhibited a peak centered at 3.31 eV without on-line heating, while it redshift to 3.20 eV with on-line heating. The mechanisms behind these behaviors were presented in this article. (copyright 2012 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  4. In and Ga Codoped ZnO Film as a Front Electrode for Thin Film Silicon Solar Cells

    Directory of Open Access Journals (Sweden)

    Duy Phong Pham

    2014-01-01

    Full Text Available Doped ZnO thin films have attracted much attention in the research community as front-contact transparent conducting electrodes in thin film silicon solar cells. The prerequisite in both low resistivity and high transmittance in visible and near-infrared region for hydrogenated microcrystalline or amorphous/microcrystalline tandem thin film silicon solar cells has promoted further improvements of this material. In this work, we propose the combination of major Ga and minor In impurities codoped in ZnO film (IGZO to improve the film optoelectronic properties. A wide range of Ga and In contents in sputtering targets was explored to find optimum optical and electrical properties of deposited films. The results show that an appropriate combination of In and Ga atoms in ZnO material, followed by in-air thermal annealing process, can enhance the crystallization, conductivity, and transmittance of IGZO thin films, which can be well used as front-contact electrodes in thin film silicon solar cells.

  5. Title: Using Alignment and 2D Network Simulations to Study Charge Transport Through Doped ZnO Nanowire Thin Film Electrodes

    KAUST Repository

    Phadke, Sujay

    2011-09-30

    Factors affecting charge transport through ZnO nanowire mat films were studied by aligning ZnO nanowires on substrates and coupling experimental measurements with 2D nanowire network simulations. Gallium doped ZnO nanowires were aligned on thermally oxidized silicon wafer by shearing a nanowire dispersion in ethanol. Sheet resistances of nanowire thin films that had current flowing parallel to nanowire alignment direction were compared to thin films that had current flowing perpendicular to nanowire alignment direction. Perpendicular devices showed ∼5 fold greater sheet resistance than parallel devices supporting the hypothesis that aligning nanowires would increase conductivity of ZnO nanowire electrodes. 2-D nanowire network simulations of thin films showed that the device sheet resistance was dominated by inter-wire contact resistance. For a given resistivity of ZnO nanowires, the thin film electrodes would have the lowest possible sheet resistance if the inter-wire contact resistance was one order of magnitude lower than the single nanowire resistance. Simulations suggest that the conductivity of such thin film devices could be further enhanced by using longer nanowires. Solution processed Gallium doped ZnO nanowires are aligned on substrates using an innovative shear coating technique. Nanowire alignment has shown improvement in ZnO nanowire transparent electrode conductivity. 2D network simulations in conjunction with electrical measurements have revealed different regimes of operation of nanowire thin films and provided a guideline for improving electrical performance of nanowire electrodes. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  6. Electrodeposition of hierarchical ZnO nanorod arrays on flexible stainless steel mesh for dye-sensitized solar cell

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Hui; Zhai, Xiangyang; Liu, Wenwu; Zhang, Mei; Guo, Min, E-mail: guomin@ustb.edu.cn

    2015-07-01

    Hierarchical ZnO nanorod arrays (ZNRAs) were synthesized on flexible stainless steel mesh (SSM) in large scale by a two-step facile electrodeposition method. The structure and morphology of the as-prepared samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high-resolution transmission electron microscopy (HRTEM). The growth mechanism of the ZnO hierarchical nanostructures was also discussed. Moreover, the effect of ZnO morphology on the photovoltaic performance of the flexible DSSCs based on SSM supported ZnO nanostructures was investigated in detail. It is shown that the flexible DSSCs exhibited a relatively higher power conversion efficiency of 1.11% compared with that based on primary ZNRAs. - Highlights: • Hierarchical ZnO nanorod arrays (ZNRAs) were prepared by electrodeposition method. • Flexible stainless steel mesh (SSM) supported with hierarchical ZNRAs was first used for DSSCs. • The effect of ZnO morphology on the photovoltaic performance of flexible DSSCs was investigated. • The DSSC based on 3-Hierarchical ZNRAs/ZNPs showed a relatively efficiency of 1.11%.

  7. Effect of Er3+ doping on structural, morphological and photocatalytical properties of ZnO thin films

    Science.gov (United States)

    Bouhouche, S.; Bensouici, F.; Toubane, M.; Azizi, A.; Otmani, A.; Chebout, K.; Kezzoula, F.; Tala-Ighil, R.; Bououdina, M.

    2018-05-01

    In this research work, structure, microstructure, optical and photocatalytic properties of undoped and Erbium doped nanostructured ZnO thin films prepared by sol-gel dip-coating are investigated. X-ray diffraction (XRD) analysis indicates that the deposited films crystallize within the hexagonal wurtzite-type structure with a preferential growth orientation along (002) plane. Morphological observations using scanning electron microscopy (SEM) reveal important influence of Er concentration; displaying homogeneous and dense aspect for undoped to 0.3% then grid-like morphology for 0.4 and 0.5%. UV/vis/NIR transmittance spectroscopy spectra display a transmittance over 70%, and small variation in the energy gap energy 3.263–3.278 eV. Wettability test of ZnO thin films surface ranges from hydrophilic aspect for pure ZnO to hydrophobic one for Er doped ZnO, and the contact angle is found to increase from 58.7° for pure ZnO up to 98.4° for 0.4% Er doped ZnO. The photocatalytic activity measurements evaluated using the degradation of methylene blue (MB) under UV light irradiation demonstrate that undoped ZnO film shows higher photocatalytic activity compared to Er doped ZnO films, which may be attributed to the deterioration of films’crystallinity resulting in lower transmittance.

  8. Synthesis and Characterization of Molybdenum Doped ZnO Thin Films by SILAR Deposition Method

    Science.gov (United States)

    Radha, R.; Sakthivelu, A.; Pradhabhan, D.

    2016-08-01

    Molybdenum (Mo) doped zinc oxide (ZnO) thin films were deposited on the glass substrate by Successive Ionic Layer Adsorption and Reaction (SILAR) deposition method. The effect of Mo dopant concentration of 5, 6.6 and 10 mol% on the structural, morphological, optical and electrical properties of n-type Mo doped ZnO films was studied. The X-ray diffraction (XRD) results confirmed that the Mo doped ZnO thin films were polycrystalline with wurtzite structure. The field emission scanning electron microscopy (FESEM) studies shows that the surface morphology of the films changes with Mo doping. A blue shift of the optical band gap was observed in the optical studies. Effect of Mo dopant concentration on electrical conductivity was studied and it shows comparatively high electrical conductivity at 10 mol% of Mo doping concentration.

  9. Enhanced optical band-gap of ZnO thin films by sol-gel technique

    Energy Technology Data Exchange (ETDEWEB)

    Raghu, P., E-mail: dpr3270@gmail.com; Naveen, C. S.; Shailaja, J.; Mahesh, H. M., E-mail: hm-mahesh@rediffmail.com [Thin Film and Solar Cell Laboratory, Department of Electronic Science, Bangalore University, Jnanabharathi, Bangalore -560056 (India)

    2016-05-06

    Transparent ZnO thin films were prepared using different molar concentration (0.1 M, 0.2 M & 0.8 M) of zinc acetate on soda lime glass substrates by the sol-gel spin coating technique. The optical properties revealed that the transmittance found to decrease with increase in molar concentration. Absorption edge showed that the higher concentration film has increasingly red shifted. An increased band gap energy of the thin films was found to be direct allowed transition of ∼3.9 eV exhibiting their relevance for photovoltaic applications. The extinction coefficient analysis revealed maximum transmittance with negligible absorption coefficient in the respective wavelengths. The results of ZnO thin film prepared by sol-gel technique reveal its suitability for optoelectronics and as a window layer in solar cell applications.

  10. Cu-implanted ZnO nanorods array film: An aqueous synthetic approach

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Ajaya Kumar, E-mail: ajayaksingh_au@yahoo.co.in [Department of Chemistry, Govt. VYT PG. Autonomous College Durg, Chhattisgarh (India); Thool, Gautam Sheel [Department of Chemistry, Govt. VYT PG. Autonomous College Durg, Chhattisgarh (India); Singh, R.S. [Department of Physics, Govt. D.T. College, Utai, Durg, Chhattisgarh (India); Singh, Surya Prakash, E-mail: spsingh@iict.res.in [Inorganic and Physical Chemistry Division, CSIR-Indian Institute of Chemical Technology, Uppal road, Tarnaka, Hyderabad 500007 (India)

    2015-01-05

    Highlights: • Cu doped ZnO nanorods were synthesized using low temperature aqueous solution method. • We demonstrated the capping action of TEA via theoretical simulation. • Raman analysis revealed the presence of tensile strain in Cu doped ZnO nanorods. • Growth rate was found to be high in Cu doped ZnO nanorods. - Abstract: Pure and Cu doped ZnO nanorods array are synthesized via two step chemical bath deposition method. The seed layer is prepared by successive ionic layer adsorption reaction (SILAR) method. The synthesized materials have been systematically characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive X-ray (EDAX), Raman spectroscopy, Fourier transform infrared (FTIR) spectroscopy and photoluminescence (PL) spectroscopy. SEM pictures show the existence of vertically well aligned hexagonal ZnO nanorods. EDAX spectrum confirms the presence of Cu in ZnO nanorods. High intense peak of (0 0 2) plane and E{sub 2}{sup high} mode for XRD and Raman spectrum respectively, suggest the ZnO nanorods are adopted c-axis orientation perpendicular to substrate. XRD and Raman analysis shows the presence of tensile strain in Cu doped ZnO nanorods. Effect of Cu doping on lattice constants, unit cell volume and Zn–O bond length of ZnO nanorods have also been studied. Room temperature PL measurement exhibits two luminescence bands in the spectra i.e. UV emission centered at 3.215 eV and a broad visible band. Theoretical investigation for capping action of triethanolamine is done by Hartree–Fock (HF) method with 3-21G basis set using Gaussian 09 program package.

  11. Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Byunggu; Leem, Jae-Young [Inje University, Gimhae (Korea, Republic of)

    2017-01-15

    ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

  12. Effects of Doping Concentration on the Structural and Optical Properties of Spin-Coated In-doped ZnO Thin Films Grown on Thermally Oxidized ZnO Film/ZnO Buffer Layer/Mica Substrate

    International Nuclear Information System (INIS)

    Kim, Byunggu; Leem, Jae-Young

    2017-01-01

    ZnO buffer layers were deposited on mica substrates using a sol-gel spin coating method. Then, a thin film of metallic Zn was deposited onto the ZnO buffer layer/mica substrate using a thermal evaporator, and the deposited Zn thin films were then thermally oxidized in a furnace at 500 ℃ for 2 h in air. Finally, In-doped ZnO (IZO) thin films with different In concentrations were grown on the oxidized ZnO film/ZnO buffer layer/mica substrates using the sol-gel spin-coating method. All the IZO films showed ZnO peaks with similar intensities. The full width at half maximum values of the ZnO (002) peak for the IZO thin films decreased with an increase in the In concentration to 1 at%, because the crystallinity of the films was enhanced. However, a further increase in the In concentration caused the crystal quality to degrade. This might be attributed to the fact that the higher In doping resulted in an increase in the number of ionized impurities. The Urbach energy (EU) values of the IZO thin film decreased with an increase in the In concentration to 1 at % because of the enhanced crystal quality of the films. The EU values for the IZO thin films increased with the In concentration from 1 at%to 3 at%, reflecting the broadening of localized band tail state near the conduction band edge of the films.

  13. Microwave Characterization of Ba-Substituted PZT and ZnO Thin Films.

    Science.gov (United States)

    Tierno, Davide; Dekkers, Matthijn; Wittendorp, Paul; Sun, Xiao; Bayer, Samuel C; King, Seth T; Van Elshocht, Sven; Heyns, Marc; Radu, Iuliana P; Adelmann, Christoph

    2018-05-01

    The microwave dielectric properties of (Ba 0.1 Pb 0.9 )(Zr 0.52 Ti 0.48 )O 3 (BPZT) and ZnO thin films with thicknesses below were investigated. No significant dielectric relaxation was observed for both BPZT and ZnO up to 30 GHz. The intrinsic dielectric constant of BPZT was as high as 980 at 30 GHz. The absence of strong dielectric dispersion and loss peaks in the studied frequency range can be linked to the small grain diameters in these ultrathin films.

  14. Comparative study of ZnO thin films prepared by different sol-gel route

    Directory of Open Access Journals (Sweden)

    F Esmaieli Ghodsi

    2012-03-01

    Full Text Available   Retraction Notice    The paper "Comparative study of ZnO thin films prepared by different sol-gel route" by H. Absalan and F. E. Ghodsi, which appeared in Iranian Journal of Physics Research, Vol. 11, No. 4, 423-428 (in Farsi is translation of the paper "Comparative Study of ZnO Thin Films Prepared by Different Sol-Gel Route" by F. E. Ghodsi and H. Absalan, which appeared in ACTA PHYSICA POLONICA A, Vol 118 (2010 (in English and for this reason is retracted from this journal.The corresponding author  (and also the first author is the only responsible person for this action.   

  15. ZnO-nanorod arrays for solar cells with extremely thin sulfidic absorber

    Energy Technology Data Exchange (ETDEWEB)

    Belaidi, A.; Dittrich, Th.; Kieven, D.; Tornow, J.; Schwarzburg, K.; Kunst, M.; Allsop, N.; Lux-Steiner, M.-Ch. [Hahn-Meitner-Institute, Glienicker Str. 100, D-14109 Berlin (Germany); Gavrilov, S. [Moscow Institute of Electronic Technology, 124 498 Moscow (Russian Federation)

    2009-06-15

    Solar cells with an extremely thin sulfidic absorber have been prepared by spray ion layer gas reaction (ILGAR) of In{sub 2}S{sub 3} on ZnO-nanorod arrays. As transparent hole conductor, CuSCN was deposited on the coated ZnO nanorods by impregnation. Surface photovoltage spectroscopy was applied to characterize states contributing to excess carrier generation and charge separation. The charge-selective contact is formed at the In{sub 2}S{sub 3}/CuSCN interface region the states of which also contribute significantly to the photocurrent. The influence of annealing temperature and annealing time of the In{sub 2}S{sub 3}/CuSCN contact region on the open-circuit potential (V{sub OC}), short-circuit current (I{sub SC}) and fill factor (FF) was studied in detail. For solar cells based on ZnO-nanorod arrays (rod length 1.5 {mu}m), efficiency of 2.8% is obtained at AM1.5. (author)

  16. Structural, optical and magnetic properties of nanocrystalline Co-doped ZnO thin films grown by sol-gel

    Energy Technology Data Exchange (ETDEWEB)

    Kayani, Zohra Nazir; Shah, Iqra; Zulfiqar, Bareera; Sabah, Aneeqa [Lahore College for Women Univ., Lahore (Pakistan); Riaz, Saira; Naseem, Shahzad [Univ. of the Punjab, Lahore (Pakistan). Centre of Excellence in Solid State Physics

    2018-04-01

    Cobalt-doped ZnO thin films have been deposited using a sol-gel route by changing the number of coats on the substrate from 6 to 18. This project deals with various film thicknesses by increasing the number of deposited coats. The effect of thickness on structural, magnetic, surface morphology and optical properties of Co-doped ZnO thin film was studied. The crystal structure of the Co-doped ZnO films was investigated by X-ray diffraction. The films have polycrystalline wurtzite hexagonal structures. A Co{sup 2+} ion takes the place of a Zn{sup 2+} ion in the lattice without creating any distortion in its hexagonal wurtzite structure. An examination of the optical transmission spectra showed that the energy band gap of the Co-doped ZnO films increased from 3.87 to 3.97 eV with an increase in the number of coatings on the substrate. Ferromagnetic behaviour was confirmed by measurements using a vibrating sample magnetometer. The surface morphology of thin films was assessed by scanning electron microscope. The grain size on the surface of thin films increased with an increase in the number of coats.

  17. Role of vacancy defects in Al doped ZnO thin films for optoelectronic devices

    Science.gov (United States)

    Rotella, H.; Mazel, Y.; Brochen, S.; Valla, A.; Pautrat, A.; Licitra, C.; Rochat, N.; Sabbione, C.; Rodriguez, G.; Nolot, E.

    2017-12-01

    We report on the electrical, optical and photoluminescence properties of industry-ready Al doped ZnO thin films grown by physical vapor deposition, and their evolution after annealing under vacuum. Doping ZnO with Al atoms increases the carrier density but also favors the formation of Zn vacancies, thereby inducing a saturation of the conductivity mechanism at high aluminum content. The electrical and optical properties of these thin layered materials are both improved by annealing process which creates oxygen vacancies that releases charge carriers thus improving the conductivity. This study underlines the effect of the formation of extrinsic and intrinsic defects in Al doped ZnO compound during the fabrication process. The quality and the optoelectronic response of the produced films are increased (up to 1.52 mΩ \\cdotcm and 3.73 eV) and consistent with the industrial device requirements.

  18. Application of Thin ZnO ALD Layers in Fiber-Optic Fabry-Pérot Sensing Interferometers

    Directory of Open Access Journals (Sweden)

    Daria Majchrowicz

    2016-03-01

    Full Text Available In this paper we investigated the response of a fiber-optic Fabry-Pérot sensing interferometer with thin ZnO layers deposited on the end faces of the optical fibers forming the cavity. Standard telecommunication single-mode optical fiber (SMF-28 segments were used with the thin ZnO layers deposited by Atomic Layer Deposition (ALD. Measurements were performed with the interferometer illuminated by two broadband sources operating at 1300 nm and 1550 nm. Reflected interference signal was acquired by an optical spectrum analyzer while the length of the air cavity was varied. Thickness of the ZnO layers used in the experiments was 50 nm, 100 nm, and 200 nm. Uncoated SMF-28 fiber was also used as a reference. Based on the results of measurements, the thickness of the ZnO layers and the length of the cavity were selected in order to achieve good visibility. Following, the interferometer was used to determine the refractive index of selected liquids.

  19. Red photoluminescence and band edge shift from ZnO thin films

    International Nuclear Information System (INIS)

    Marotti, Ricardo E.; Badan, Juan A.; Quagliata, Eduardo; Dalchiele, Enrique A.

    2007-01-01

    The red photoluminescence (PL) band (peaked between 610 and 640 nm) from electrochemically deposited ZnO thin films is studied. The absorption coefficient is obtained from diffuse reflectance measurements. The absorption band edge depends on deposition conditions. The PL peak follows the shift of the band edge. A similar correlation appears when cooling down to 20 K. This suggests that PL is due to a transition from an intrinsic shallow state to an intrinsic deep state. Comparing against ZnO samples showing green PL, the shallow nature of the state is confirmed

  20. Enhancement of ZnO nanorod arrays-based inverted type hybrid organic solar cell using spin-coated Eosin-Y

    International Nuclear Information System (INIS)

    Lim, Eng Liang; Yap, Chi Chin; Yahaya, Muhammad; Salleh, Muhamad Mat

    2013-01-01

    This paper reports the effect of Eosin-Y coating concentration on the performance of inverted type hybrid organic solar cell based on ZnO nanorod arrays and poly(3-hexylthiophene-2,5-diyl) (P3HT). The Eosin-Y solution with concentrations of 0.05, 0.2, 2.0 and 5.0 mM was spin-coated onto the ZnO nanorod arrays grown on the fluorine-doped tin oxide glass substrate. The P3HT film was then spin-coated onto Eosin-Y-coated ZnO nanorod arrays, followed by deposition of silver (Ag) as anode using magnetron sputtering technique. The short circuit current density increased with the Eosin-Y coating concentration up to 0.2 mM, after which it started to decrease, mainly due to the aggregation of Eosin-Y which reduced the charge extraction from P3HT to ZnO. Meanwhile, the open circuit voltage increased with the Eosin-Y coating concentration, indicating reduced back charge recombination of electron on the ZnO and hole on the P3HT, as well as reduced leakage current through the direct contact between the ZnO nanorods and the Ag metal contact. The power conversion efficiency of the device with the optimum coating concentration was approximately eight times higher than that without Eosin-Y modification. (paper)

  1. Enhancement of ZnO nanorod arrays-based inverted type hybrid organic solar cell using spin-coated Eosin-Y

    Science.gov (United States)

    Lim, Eng Liang; Yap, Chi Chin; Yahaya, Muhammad; Mat Salleh, Muhamad

    2013-04-01

    This paper reports the effect of Eosin-Y coating concentration on the performance of inverted type hybrid organic solar cell based on ZnO nanorod arrays and poly(3-hexylthiophene-2,5-diyl) (P3HT). The Eosin-Y solution with concentrations of 0.05, 0.2, 2.0 and 5.0 mM was spin-coated onto the ZnO nanorod arrays grown on the fluorine-doped tin oxide glass substrate. The P3HT film was then spin-coated onto Eosin-Y-coated ZnO nanorod arrays, followed by deposition of silver (Ag) as anode using magnetron sputtering technique. The short circuit current density increased with the Eosin-Y coating concentration up to 0.2 mM, after which it started to decrease, mainly due to the aggregation of Eosin-Y which reduced the charge extraction from P3HT to ZnO. Meanwhile, the open circuit voltage increased with the Eosin-Y coating concentration, indicating reduced back charge recombination of electron on the ZnO and hole on the P3HT, as well as reduced leakage current through the direct contact between the ZnO nanorods and the Ag metal contact. The power conversion efficiency of the device with the optimum coating concentration was approximately eight times higher than that without Eosin-Y modification.

  2. Structural, optical and electrical properties of ZnO thin films prepared ...

    Indian Academy of Sciences (India)

    Administrator

    of zinc acetate on glass substrates at 450 °C. Effect of precursor concentration on structural and optical pro- perties has ... dependence of photoresponse properties of sprayed ZnO thin films on ... randomly oriented flake-like grains. The grains ...

  3. ZnO nanorod arrays prepared by chemical bath deposition combined with rapid thermal annealing: structural, photoluminescence and field emission characteristics

    International Nuclear Information System (INIS)

    Chen, Hung-Wei; He, Hsin-Min; Lee, Yi-Mu; Yang, Hsi-Wen

    2016-01-01

    ZnO nanorod arrays were prepared by low temperature chemical bath deposition (CBD) combined with rapid thermal annealing (RTA) under different ambient conditions. The structure and morphology of the synthesized ZnO have been characterized by field-emission scanning electron microscopy (FESEM) and x-ray diffraction (XRD). The obtained ZnO samples are highly crystalline with a hexagonal wurtzite phase and also display well-aligned array structure. A pronounced effect on increased nanorod length was found for the RTA-treated ZnO as compared to the as-grown ZnO. Analysis of XRD indicates that the (0 0 2) feature peak of the as-grown ZnO was shifted towards a lower angle as compared to the peaks of RTA-treated ZnO samples due to the reduction of tensile strain along the c-axis by RTA. Photoluminescence (PL) studies reveal that the ZnO nanorod arrays receiving RTA in an O 2 environment have the sharpest UV emission band and greatest intensity ratio of near band-edge emission (NBE) to deep level emission (DLE). Additionally, the effects of RTA on the field emission properties were evaluated. The results demonstrate that RTA an O 2 environment can lower the turn-on field and improve the field enhancement factor. The stability of the field emission current was also tested for 4 h. (paper)

  4. Doping properties of ZnO thin films for photovoltaic devices grown by URT-IP (ion plating) method

    International Nuclear Information System (INIS)

    Iwata, K.; Sakemi, T.; Yamada, A.; Fons, P.; Awai, K.; Yamamoto, T.; Matsubara, M.; Tampo, H.; Sakurai, K.; Ishizuka, S.; Niki, S.

    2004-01-01

    The Uramoto-gun with Tanaka magnetic field (URT)-ion plating (IP) method is a novel ion plating technique for thin film deposition. This method offers the advantage of low-ion damage, low deposition temperatures, large area deposition and high growth rates. Ga-doped ZnO thin films were grown using the URT-IP method, and the doping properties were evaluated. The opposing goals of low Ga composition and low resistivity are required for industrial applications of transparent conductive oxide (TCO). We have carried out a comparison between the carrier concentration and Ga atomic concentration in Ga-doped ZnO thin films and found the trade-off point for optimal TCO performance. The optimum growth conditions were obtained using a 3% Ga 2 O 3 content ZnO target

  5. Selective growth of ZnO thin film nanostructures: Structure, morphology and tunable optical properties

    Energy Technology Data Exchange (ETDEWEB)

    Krishnakanth, Katturi Naga; Sunandana, C. S. [School of Physics, University of Hyderabad, Hyderabad-50046 (India); Rajesh, Desapogu, E-mail: rajesh.esapogu@gmail.com, E-mail: mperd@nus.edu.sg [School of Physics, University of Hyderabad, Hyderabad-50046 (India); Dept. of Mechanical Engineering, National University of Singapore (Singapore)

    2016-05-23

    The ZnO nanostructures (spherical, rod shape) have been successfully fabricated via a thermal evaporation followed by dip coating method. The pure, doped ZnO thin films were characterized by X-ray powder diffraction (XRD) and field emission scanning electron microscopy (FESEM) and UV-Vis spectroscopy, respectively. A possible growth mechanism of the spherical, rod shape ZnO nanostructures are discussed. XRD patterns revealed that all films consist of pure ZnO phase and were well crystallized with preferential orientation towards (002) direction. Doping by PVA, PVA+Cu has effective role in the enhancement of the crystalline quality and increases in the band gap.

  6. Electrical and optical properties of a n-type ZnO thin film deposited on a Si substrate by using a double RF Co-sputtering method

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Jonghyun; Choi, Wonjoon; Kim, Chaeok; Hong, Jinpyo; Nahm, Tschanguh [Hanyang University, Seoul (Korea, Republic of); Cheong, Hyeonsik [Sogang University, Seoul (Korea, Republic of)

    2006-09-15

    Outstanding n-type ZnO thin films were prepared on Si substrates by utilizing a double RF cosputtering method. Our unique double RF technique has many attractive merits for synthesizing ZnO thin films with excellent optoelectronic properties at various temperatures. The ZnO thin films were also post-annealed at various temperatures. The X-ray diffraction patterns and X-ray photoelectron spectroscopy indicated well-grown ZnO films with a (002) orientation and with gorgeous chemically bond states, respectively. In addition, photoluminescence measurements indicated a band-gap of 3.4 eV in the ZnO films. The scanning electron microscopy images showed that the as-grown ZnO thin film had hexagonal column shapes, such as hexagonal rods. The ZnO film exhibited an UV light response with a cut-off wavelength of {approx}370 nm at room temperature.

  7. Effect of Ag doping on the properties of ZnO thin films for UV stimulated emission

    Science.gov (United States)

    Razeen, Ahmed S.; Gadallah, A.-S.; El-Nahass, M. M.

    2018-06-01

    Ag doped ZnO thin films have been prepared using sol-gel spin coating method, with different doping concentrations. Structural and morphological properties of the films have been investigated by X-ray diffraction (XRD) and scanning electron microscopy (SEM) techniques. Thin films have been optically pumped and stimulated emission has been observed with strong peaks in the UV region. The UV stimulated emission is found to be due to exciton-exciton scattering, and Ag doping promoted this process by increasing the excitons concentrations in the ZnO lattice. Output-input intensity relation and peak emission, FWHM, and quantum efficiency relations with pump intensity have been reported. The threshold for which stimulated emission started has been evaluated to be about 18 MW/cm2 with quantum efficiency of about 58.7%. Mechanisms explaining the role of Ag in enhancement of stimulated emission from ZnO thin films have been proposed.

  8. A novel, substrate independent three-step process for the growth of uniform ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Byrne, D.; McGlynn, E.; Henry, M.O.; Kumar, K.; Hughes, G.

    2010-01-01

    We report a three-step deposition process for uniform arrays of ZnO nanorods, involving chemical bath deposition of aligned seed layers followed by nanorod nucleation sites and subsequent vapour phase transport growth of nanorods. This combines chemical bath deposition techniques, which enable substrate independent seeding and nucleation site generation with vapour phase transport growth of high crystalline and optical quality ZnO nanorod arrays. Our data indicate that the three-step process produces uniform nanorod arrays with narrow and rather monodisperse rod diameters (∼ 70 nm) across substrates of centimetre dimensions. X-ray photoelectron spectroscopy, scanning electron microscopy and X-ray diffraction were used to study the growth mechanism and characterise the nanostructures.

  9. Antibacterial and barrier properties of oriented polymer films with ZnO thin films applied with atomic layer deposition at low temperatures

    International Nuclear Information System (INIS)

    Vähä-Nissi, Mika; Pitkänen, Marja; Salo, Erkki; Kenttä, Eija; Tanskanen, Anne; Sajavaara, Timo; Putkonen, Matti; Sievänen, Jenni; Sneck, Asko; Rättö, Marjaana; Karppinen, Maarit; Harlin, Ali

    2014-01-01

    Concerns on food safety, and need for high quality and extended shelf-life of packaged foods have promoted the development of antibacterial barrier packaging materials. Few articles have been available dealing with the barrier or antimicrobial properties of zinc oxide thin films deposited at low temperature with atomic layer deposition (ALD) onto commercial polymer films typically used for packaging purposes. The purpose of this paper was to study the properties of ZnO thin films compared to those of aluminum oxide. It was also possible to deposit ZnO thin films onto oriented polylactic acid and polypropylene films at relatively low temperatures using ozone instead of water as an oxidizing precursor for diethylzinc. Replacing water with ozone changed both the structure and the chemical composition of films deposited on silicon wafers. ZnO films deposited with ozone contained large grains covered and separated probably by a more amorphous and uniform layer. These thin films were also assumed to contain zinc salts of carboxylic acids. The barrier properties of a 25 nm ZnO thin film deposited with ozone at 100 °C were quite close to those obtained earlier with ALD Al 2 O 3 of similar apparent thickness on similar polymer films. ZnO thin films deposited at low temperature indicated migration of antibacterial agent, while direct contact between ZnO and Al 2 O 3 thin films and bacteria promoted antibacterial activity. - Highlights: • Thin films were grown from diethylzinc also with ozone instead of water at 70 and 100 °C. • ZnO films deposited with diethylzinc and ozone had different structures and chemistries. • Best barrier properties obtained with zinc oxide films close to those obtained with Al 2 O 3 • Ozone as oxygen source provided better barrier properties at 100 °C than water. • Both aluminum and zinc oxide thin films showed antimicrobial activity against E. coli

  10. Antibacterial and barrier properties of oriented polymer films with ZnO thin films applied with atomic layer deposition at low temperatures

    Energy Technology Data Exchange (ETDEWEB)

    Vähä-Nissi, Mika, E-mail: mika.vaha-nissi@vtt.fi [VTT Technical Research Centre of Finland, P.O. Box 1000, FI-02044, VTT (Finland); Pitkänen, Marja; Salo, Erkki; Kenttä, Eija [VTT Technical Research Centre of Finland, P.O. Box 1000, FI-02044, VTT (Finland); Tanskanen, Anne, E-mail: Anne.Tanskanen@aalto.fi [Aalto University, School of Chemical Technology, Department of Chemistry, Laboratory of Inorganic Chemistry, P.O. Box 16100, FI-00076 Aalto (Finland); Sajavaara, Timo, E-mail: timo.sajavaara@jyu.fi [University of Jyväskylä, Department of Physics, P.O. Box 35, FI-40014 Jyväskylä (Finland); Putkonen, Matti; Sievänen, Jenni; Sneck, Asko; Rättö, Marjaana [VTT Technical Research Centre of Finland, P.O. Box 1000, FI-02044, VTT (Finland); Karppinen, Maarit, E-mail: Maarit.Karppinen@aalto.fi [Aalto University, School of Chemical Technology, Department of Chemistry, Laboratory of Inorganic Chemistry, P.O. Box 16100, FI-00076 Aalto (Finland); Harlin, Ali [VTT Technical Research Centre of Finland, P.O. Box 1000, FI-02044, VTT (Finland)

    2014-07-01

    Concerns on food safety, and need for high quality and extended shelf-life of packaged foods have promoted the development of antibacterial barrier packaging materials. Few articles have been available dealing with the barrier or antimicrobial properties of zinc oxide thin films deposited at low temperature with atomic layer deposition (ALD) onto commercial polymer films typically used for packaging purposes. The purpose of this paper was to study the properties of ZnO thin films compared to those of aluminum oxide. It was also possible to deposit ZnO thin films onto oriented polylactic acid and polypropylene films at relatively low temperatures using ozone instead of water as an oxidizing precursor for diethylzinc. Replacing water with ozone changed both the structure and the chemical composition of films deposited on silicon wafers. ZnO films deposited with ozone contained large grains covered and separated probably by a more amorphous and uniform layer. These thin films were also assumed to contain zinc salts of carboxylic acids. The barrier properties of a 25 nm ZnO thin film deposited with ozone at 100 °C were quite close to those obtained earlier with ALD Al{sub 2}O{sub 3} of similar apparent thickness on similar polymer films. ZnO thin films deposited at low temperature indicated migration of antibacterial agent, while direct contact between ZnO and Al{sub 2}O{sub 3} thin films and bacteria promoted antibacterial activity. - Highlights: • Thin films were grown from diethylzinc also with ozone instead of water at 70 and 100 °C. • ZnO films deposited with diethylzinc and ozone had different structures and chemistries. • Best barrier properties obtained with zinc oxide films close to those obtained with Al{sub 2}O{sub 3} • Ozone as oxygen source provided better barrier properties at 100 °C than water. • Both aluminum and zinc oxide thin films showed antimicrobial activity against E. coli.

  11. Laser molecular beam epitaxy of ZnO thin films and heterostructures

    International Nuclear Information System (INIS)

    Opel, Matthias; Geprägs, Stephan; Althammer, Matthias; Brenninger, Thomas; Gross, Rudolf

    2014-01-01

    We report on the growth of epitaxial ZnO thin films and ZnO-based heterostructures on sapphire substrates by laser molecular beam epitaxy (MBE). We first discuss some recent developments in laser-MBE such as flexible ultraviolet laser beam optics, infrared laser heating systems or the use of atomic oxygen and nitrogen sources, and describe the technical realization of our advanced laser-MBE system. Then we describe the optimization of the deposition parameters for ZnO films such as laser fluence and substrate temperature and the use of buffer layers. The detailed structural characterization by x-ray analysis and transmission electron microscopy shows that epitaxial ZnO thin films with high structural quality can be achieved, as demonstrated by a small out-of-plane and in-plane mosaic spread as well as the absence of rotational domains. We also demonstrate the heteroepitaxial growth of ZnO-based multilayers as a prerequisite for spin transport experiments and the realization of spintronic devices. As an example, we show that TiN/Co/ZnO/Ni/Au multilayer stacks can be grown on (0 0 0 1)-oriented sapphire with good structural quality of all layers and well defined in-plane epitaxial relations. (paper)

  12. Solving “Antenna Array Thinning Problem” Using Genetic Algorithm

    Directory of Open Access Journals (Sweden)

    Rajashree Jain

    2012-01-01

    Full Text Available Thinning involves reducing total number of active elements in an antenna array without causing major degradation in system performance. Dynamic thinning is the process of achieving this under real-time conditions. It is required to find a strategic subset of antenna elements for thinning so as to have its optimum performance. From a mathematical perspective this is a nonlinear, multidimensional problem with multiple objectives and many constraints. Solution for such problem cannot be obtained by classical analytical techniques. It will be required to employ some type of search algorithm which can lead to a practical solution in an optimal. The present paper discusses an approach of using genetic algorithm for array thinning. After discussing the basic concept involving antenna array, array thinning, dynamic thinning, and application methodology, simulation results of applying the technique to linear and planar arrays are presented.

  13. Optical and structural properties of thin films of ZnO at elevated temperature

    International Nuclear Information System (INIS)

    Kayani, Zohra N.; Afzal, Tosif; Riaz, Saira; Naseem, Shahzad

    2014-01-01

    Highlights: • Thin films of ZnO are prepared on glass substrates using dip-coating. • The X-ray diffraction showed that films are crystalline. • Optical measurements show that the film possesses high transmittance in visible region. • The transmission decreased with increased withdrawal speed. • The films has direct band gap in range 3.78-3.48 eV. - Abstract: Zinc oxide (ZnO) thin films were prepared on glass substrate by sol–gel dip-coating method. The paper presents the properties of zinc oxide thin films deposited on soda-lime-glass substrate via dip-coating technique, using zinc acetate dehydrate and ethanol as raw materials. The effect of withdrawal speed on the crystalline structure, surface morphology and optical properties of the thin films has been investigated using XRD, SEM and UV–Vis spectrophotometer. X-ray diffraction study shows that all the films have hexagonal wurtzite structure with preferred orientation in (0 0 2) direction and transmission spectra showed highly transparent films with band gap ranging from 3.78 to 3.48 eV

  14. Fabrication of nanostructured Al-doped ZnO thin film for methane sensing applications

    Energy Technology Data Exchange (ETDEWEB)

    Shafura, A. K., E-mail: shafura@ymail.com; Azhar, N. E. I.; Uzer, M.; Mamat, M. H. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Sin, N. D. Md. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA Cawangan Johor, Kampus Pasir Gudang, 81750 Masai, Johor (Malaysia); Saurdi, I. [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); Faculty of Electrical Engineering, Universiti Teknologi MARA Sarawak, Kampus Kota Samarahan Jalan Meranek, Sarawak (Malaysia); Shuhaimi, A. [Dimensional Materials Research Centre (LDMRC), Department of Physics, Faculty of Science, University ofMalaya, 50603 Kuala Lumpur (Malaysia); Alrokayan, Salman A. H.; Khan, Haseeb A. [Research Chair of Targeting and Treatment Cancer Using Nanoparticles, Department Of Biochemistry, College Of Science, King Saud University, P.O: 2454 Riyadh 11451 (Saudi Arabia); Rusop, M., E-mail: nanouitm@gmail.com [NANO-ElecTronic Centre (NET), Faculty of Electrical Engineering, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia); NANO-SciTech Centre (NST), Institute of Science, Universiti Teknologi MARA, 40450 Shah Alam, Selangor (Malaysia)

    2016-07-06

    CH{sub 4} gas sensor was fabricated using spin-coating method of the nanostructured ZnO thin film. Effect of annealing temperature on the electrical and structural properties of the film was investigated. Dense nanostructured ZnO film are obtained at higher annealing temperature. The optimal condition of annealing temperature is 500°C which has conductivity and sensitivity value of 3.3 × 10{sup −3} S/cm and 11.5%, respectively.

  15. Mechanisms involved in the hydrothermal growth of ultra-thin and high aspect ratio ZnO nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Demes, Thomas [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France); Ternon, Céline, E-mail: celine.ternon@grenoble-inp.fr [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France); Univ. Grenoble Alpes, CNRS, LTM, F-38000 Grenoble (France); Morisot, Fanny [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France); Univ. Grenoble Alpes, CNRS, Grenoble-INP" 2, IMEP-LaHC, F-38000 Grenoble (France); Riassetto, David [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France); Legallais, Maxime [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France); Univ. Grenoble Alpes, CNRS, Grenoble-INP" 2, IMEP-LaHC, F-38000 Grenoble (France); Roussel, Hervé; Langlet, Michel [Univ. Grenoble Alpes, CNRS, Grenoble-INP, LMGP, F-38000 Grenoble (France)

    2017-07-15

    Highlights: • ZnO nanowires are grown on sol-gel ZnO seed layers by hydrothermal synthesis. • Ultra-thin and high aspect ratio nanowires are obtained without using additives. • Nanowire diameter is 20–25 nm regardless of growth time and seed morphology. • A nanowire growth model is developed on the basis of thermodynamic considerations. • The nanowires are intended for integration into electrically conductive nanonets. - Abstract: Hydrothermal synthesis of ZnO nanowires (NWs) with tailored dimensions, notably high aspect ratios (AR) and small diameters, is a major concern for a wide range of applications and still represents a challenging and recurring issue. In this work, an additive-free and reproducible hydrothermal procedure has been developed to grow ultra-thin and high AR ZnO NWs on sol-gel deposited ZnO seed layers. Controlling the substrate temperature and using a low reagent concentration (1 mM) has been found to be essential for obtaining such NWs. We show that the NW diameter remains constant at about 20–25 nm with growth time contrary to the NW length that can be selectively increased leading to NWs with ARs up to 400. On the basis of investigated experimental conditions along with thermodynamic and kinetic considerations, a ZnO NW growth mechanism has been developed which involves the formation and growth of nuclei followed by NW growth when the nuclei reach a critical size of about 20–25 nm. The low reagent concentration inhibits NW lateral growth leading to ultra-thin and high AR NWs. These NWs have been assembled into electrically conductive ZnO nanowire networks, which opens attractive perspectives toward the development of highly sensitive low-cost gas- or bio-sensors.

  16. Homogeneous ZnO nanostructure arrays on GaAs substrates by two-step chemical bath synthesis

    International Nuclear Information System (INIS)

    Huang, Chun-Yuan; Wu, Tzung-Han; Cheng, Chiao-Yang; Su, Yan-Kuin

    2012-01-01

    ZnO nanostructures, including nanowires, nanorods, and nanoneedles, have been deposited on GaAs substrates by the two-step chemical bath synthesis. It was demonstrated that the O 2 -plasma treatment of GaAs substrates prior to the sol–gel deposition of seed layers was essential to conformally grow the nanostructures instead of 2D ZnO bunches and grains on the seed layers. Via adjusting the growth time and concentration of precursors, nanostructures with different average diameter (26–225 nm), length (0.98–2.29 μm), and density (1.9–15.3 × 10 9 cm −2 ) can be obtained. To the best of our knowledge, this is the first demonstration of ZnO nanostructure arrays grown on GaAs substrates by the two-step chemical bath synthesis. As an anti-reflection layer on GaAs-based solar cells, the array of ZnO nanoneedles with an average diameter of 125 nm, a moderate length of 2.29 μm, and the distribution density of 9.8 × 10 9 cm −2 has increased the power conversion efficiency from 7.3 to 12.2 %, corresponding to a 67 % improvement.

  17. Cycling behaviour of sponge-like nanostructured ZnO as thin-film Li-ion battery anodes

    International Nuclear Information System (INIS)

    Garino, Nadia; Lamberti, Andrea; Gazia, Rossana; Chiodoni, Angelica; Gerbaldi, Claudio

    2014-01-01

    Highlights: • Zn is thermally oxidized in ambient air to obtain sponge-like ZnO film. • Polycrystalline, transparent, porous thin film is obtained. • Film exhibits stabile specific capacity (∼300 mAh g −1 ) after prolonged cycling. • Sponge-like ZnO film shows promising prospects as Li-ion battery anode. - Abstract: Single phase wurtzitic porous ZnO thin films are obtained by a simple two-step method, involving the sputtering deposition of a sponge-like metallic Zn layer, followed by a moderately low temperature treatment for the complete zinc oxidation. Thanks to its 3D nanostructuration, the superimposition of small branches able to grow in length almost isotropically and forming a complex topography, sponge-like ZnO can combine the fast transport properties of one dimensional material and the high surface area usually provided by nanocrystalline electrodes. When galvanostatically tested in lithium cell, after the initial decay, it can provide an almost stable specific capacity higher than 50 μAh cm −2 after prolonged cycling at estimated 0.7 C, with very high Coulombic efficiency

  18. Cycling behaviour of sponge-like nanostructured ZnO as thin-film Li-ion battery anodes

    Energy Technology Data Exchange (ETDEWEB)

    Garino, Nadia, E-mail: nadia.garino@iit.it [Center for Space Human Robotics @Polito, Istituto Italiano di Tecnologia, Corso Trento, 21, 10129 Turin (Italy); Lamberti, Andrea; Gazia, Rossana; Chiodoni, Angelica [Center for Space Human Robotics @Polito, Istituto Italiano di Tecnologia, Corso Trento, 21, 10129 Turin (Italy); Gerbaldi, Claudio, E-mail: claudio.gerbaldi@polito.it [Center for Space Human Robotics @Polito, Istituto Italiano di Tecnologia, Corso Trento, 21, 10129 Turin (Italy); GAME Lab, Department of Applied Science and Technology – DISAT, Politecnico di Torino, C.so Duca degli Abruzzi 24, 10129 Turin (Italy)

    2014-12-05

    Highlights: • Zn is thermally oxidized in ambient air to obtain sponge-like ZnO film. • Polycrystalline, transparent, porous thin film is obtained. • Film exhibits stabile specific capacity (∼300 mAh g{sup −1}) after prolonged cycling. • Sponge-like ZnO film shows promising prospects as Li-ion battery anode. - Abstract: Single phase wurtzitic porous ZnO thin films are obtained by a simple two-step method, involving the sputtering deposition of a sponge-like metallic Zn layer, followed by a moderately low temperature treatment for the complete zinc oxidation. Thanks to its 3D nanostructuration, the superimposition of small branches able to grow in length almost isotropically and forming a complex topography, sponge-like ZnO can combine the fast transport properties of one dimensional material and the high surface area usually provided by nanocrystalline electrodes. When galvanostatically tested in lithium cell, after the initial decay, it can provide an almost stable specific capacity higher than 50 μAh cm{sup −2} after prolonged cycling at estimated 0.7 C, with very high Coulombic efficiency.

  19. Quenching of surface traps in Mn doped ZnO thin films for enhanced optical transparency

    International Nuclear Information System (INIS)

    Ilyas, Usman; Rawat, R.S.; Roshan, G.; Tan, T.L.; Lee, P.; Springham, S.V.; Zhang, Sam; Fengji Li; Chen, R.; Sun, H.D.

    2011-01-01

    The structural and photoluminescence analyses were performed on un-doped and Mn doped ZnO thin films grown on Si (1 0 0) substrate by pulsed laser deposition (PLD) and annealed at different post-deposition temperatures (500-800 deg. C). X-ray diffraction (XRD), employed to study the structural properties, showed an improved crystallinity at elevated temperatures with a consistent decrease in the lattice parameter 'c'. The peak broadening in XRD spectra and the presence of Mn 2p3/2 peak at ∼640 eV in X-ray Photoelectron Spectroscopic (XPS) spectra of the doped thin films confirmed the successful incorporation of Mn in ZnO host matrix. Extended near band edge emission (NBE) spectra indicated the reduction in the concentration of the intrinsic surface traps in comparison to the doped ones resulting in improved optical transparency. Reduced deep level emission (DLE) spectra in doped thin films with declined PL ratio validated the quenching of the intrinsic surface traps thereby improving the optical transparency and the band gap, essential for optoelectronic and spintronic applications. Furthermore, the formation and uniform distribution of nano-sized grains with improved surface features of Mn-doped ZnO thin films were observed in Field Emission Scanning Electron Microscopy (FESEM) images.

  20. Photovoltaic properties of undoped ZnO thin films prepared by the spray pyrolysis technique

    Energy Technology Data Exchange (ETDEWEB)

    Ikhmayies, S.J. [Applied Science Private Univ., Amman (Jordan). Dept. of Physics; Abu El-Haija, N.M.; Ahmad-Bitar, R.N. [Jordan Univ., Amman (Jordan). Dept. of Physics

    2009-07-01

    Zinc oxide (ZnO) can be used as a window material, transparent electrode and active layer in different types of solar cells, UV emitters, and UV sensors. In addition to being low cost, ZnO is more abundant than indium tin oxide. ZnO is non toxic and has a high chemical stability in reduction environments. When ZnO films are made without any intentional doping, they exhibit n-type conductivity. ZnO thin films can be prepared by reactive sputtering, laser ablation, chemical-vapour deposition, laser molecular-beam epitaxy, thermal evaporation, sol-gel, atomic layer deposition and spray pyrolysis, with the latter being simple, inexpensive and adaptable to large area depositions. In this work ZnCl{sub 2} was used as a source of Zn where it was dissolved in distilled water. The structural, electrical and optical properties of the films were investigated due to their important characteristic for solar cell applications. Polycrystalline ZnO thin films were deposited on glass substrate by spray pyrolysis using a home-made spraying system at substrate temperature of 450 degrees C. The films were characterized by recording and analyzing their I-V plots, their transmittance, X-ray diffraction and SEM micrographs. There resistivity was found to be about 200 ohms per cm and their bandgap energy about 3.27 eV. X-ray diffraction patterns revealed that the films have a hexagonal wurtzite structure and are highly ordered with a preferential orientation (002). SEM images revealed that the substrates are continuously covered and the surface of the film is uniform. 16 refs., 4 figs.

  1. The influence of annealing in nitrogen atmosphere on the electrical, optical and structural properties of spray- deposited ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ikhmayies, S.J. [Applied Science Private Univ., Amman (Jordan). Dept. of Physics; Abu El-Haija, N.M.; Ahmad-Bitar, R.N. [Jordan Univ., Amman (Jordan). Dept. of Physics

    2009-07-01

    Thin-film zinc oxide (ZnO) has many applications in solar cell technology and is considered to be a candidate for the substitution of indium tin oxide and tin oxide. ZnO thin films can be prepared by thermal evaporation, rf-sputtering, atomic layer deposition, chemical vapor deposition, sol-gel, laser ablation and spray pyrolysis technique. Spray pyrolysis has received much attention because of its simplicity and low cost. In this study, large area and highly uniform polycrystalline ZnO thin films were produced by spray pyrolysis using a home-made spraying system on glass substrates at 450 degrees C. The electrical, optical and structural properties of the ZnO films were enhanced by annealing the thin films in nitrogen atmosphere. X-ray diffraction revealed that the films are polycrystalline with a hexagonal wurtzite structure. The preferential orientation did not change with annealing, but XRD patterns revealed that some very weak lines had grown. There was no noticeable increase in the grain size. The transmittance of the films increased as a result of annealing. It was concluded that post-deposition annealing is essential to improve the quality of the ZnO thin films. The electrical properties improved due to a decrease in resistivity. 13 refs., 5 figs.

  2. Growth and characterization of ZnO thin films prepared by electrodeposition technique

    Energy Technology Data Exchange (ETDEWEB)

    Fahoume, M.; Maghfoul, O.; Aggour, M. [L.P.M.C., Faculte des Sciences, Universite Ibn Tofail, BP. 133-14000 Kenitra (Morocco); Hartiti, B. [L.P.M.A.E.R., Faculte des Sciences et Techniques, B.P. 146 Mohammedia (Morocco); Chraibi, F.; Ennaoui, A. [L.P.M., Faculte des Sciences, Universite Mohammed V, BP.1014 Rabat (Morocco)

    2006-06-15

    ZnO thin films were deposited on either indium tin oxide-coated glass or copper substrate by the electrodeposition process, using zinc chloride and flowing air as precursors. The effect of pH on the structural and morphological ZnO films was studied and the optimum deposition conditions have been outlined. The kinetics of the growth of the films have been investigated. We note that the rate of deposition of ZnO in an acidic solution was larger than in a basic solution. The structure of the films was studied using X-ray diffractometry (XRD) and transmission electron microscopy (TEM). The surface morphology and thickness of the films were determined using scanning electron microscopy. The X-ray diffraction analysis shows that the films are polycrystalline with hexagonal crystal structure (zincite) at pH 4. The optical transmittance of ZnO decreases with varying film thickness. The optical energy bandgap was found to be 3.26eV. (author)

  3. Investigations of rapid thermal annealing induced structural evolution of ZnO: Ge nanocomposite thin films via GISAXS

    Energy Technology Data Exchange (ETDEWEB)

    Ceylan, Abdullah, E-mail: aceylanabd@yahoo.com [Department of Physics Eng., Hacettepe University, Beytepe, 06800 Ankara (Turkey); Ozcan, Yusuf [Department of Electricity and Energy, Pamukkale University, Denizli (Turkey); Orujalipoor, Ilghar [Department of Nanotechnology and Nanomedicine, Hacettepe University, Beytepe, 06800 Ankara (Turkey); Huang, Yen-Chih; Jeng, U-Ser [National Synchrotron Radiation Research Center, 101 Hsin-Ann Road, Hsinchu Science Park, Hsinchu, Taiwan (China); Ide, Semra [Department of Physics Eng., Hacettepe University, Beytepe, 06800 Ankara (Turkey); Department of Nanotechnology and Nanomedicine, Hacettepe University, Beytepe, 06800 Ankara (Turkey)

    2016-06-07

    In this work, we present in depth structural investigations of nanocomposite ZnO: Ge thin films by utilizing a state of the art grazing incidence small angle x-ray spectroscopy (GISAXS) technique. The samples have been deposited by sequential r.f. and d.c. sputtering of ZnO and Ge thin film layers, respectively, on single crystal Si(100) substrates. Transformation of Ge layers into Ge nanoparticles (Ge-np) has been initiated by ex-situ rapid thermal annealing of asprepared thin film samples at 600 °C for 30, 60, and 90 s under forming gas atmosphere. A special attention has been paid on the effects of reactive and nonreactive growth of ZnO layers on the structural evolution of Ge-np. GISAXS analyses have been performed via cylindrical and spherical form factor calculations for different nanostructure types. Variations of the size, shape, and distributions of both ZnO and Ge nanostructures have been determined. It has been realized that GISAXS results are not only remarkably consistent with the electron microscopy observations but also provide additional information on the large scale size and shape distribution of the nanostructured components.

  4. Structure and properties of nanostructured ZnO arrays and ZnO/Ag nanocomposites fabricated by pulsed electrodeposition

    Energy Technology Data Exchange (ETDEWEB)

    Kopach, V. R.; Klepikova, K. S.; Klochko, N. P., E-mail: klochko-np@mail.ru; Khrypunov, G. S.; Korsun, V. E.; Lyubov, V. M.; Kirichenko, M. V.; Kopach, A. V. [National Technical University “Kharkiv Polytechnic Institute” (Ukraine)

    2017-03-15

    We investigate the structure, surface morphology, and optical properties of nanostructured ZnO arrays fabricated by pulsed electrodeposition, Ag nanoparticles precipitated from colloidal solutions, and a ZnO/Ag nanocomposite based on them. The electronic and electrical parameters of the ZnO arrays and ZnO/Ag nanocomposites are analyzed by studying the I–V and C–V characteristics. Optimal modes for fabricating the ZnO/Ag heterostructures with the high stability and sensitivity to ultraviolet radiation as promising materials for use in photodetectors, gas sensors, and photocatalysts are determined.

  5. Micro-patterned ZnO semiconductors for high performance thin film transistors via chemical imprinting with a PDMS stamp.

    Science.gov (United States)

    Seong, Kieun; Kim, Kyongjun; Park, Si Yun; Kim, Youn Sang

    2013-04-07

    Chemical imprinting was conducted on ZnO semiconductor films via a chemical reaction at the contact regions between a micro-patterned PDMS stamp and ZnO films. In addition, we applied the chemical imprinting on Li doped ZnO thin films for high performance TFTs fabrication. The representative micro-patterned Li doped ZnO TFTs showed a field effect mobility of 4.2 cm(2) V(-1) s(-1) after sintering at 300 °C.

  6. Fabrication and characterization of ZnO nanowires array electrodes with high photocurrent densities: Effects of the seed layer calcination time

    Energy Technology Data Exchange (ETDEWEB)

    Lu, Yi-Jing; Liu, Ching-Fang; Hu, Chi-Chang, E-mail: cchu@che.nthu.edu.tw; Kuo, Jen-Hou; Boddula, Rajender

    2017-03-01

    In this work, we demonstrate that vertically grown ZnO nanowire (NW) arrays of the wurzite phase were successfully fabricated on fluorine doped tin oxide (FTO) substrates via a hydrothermal method. The coating of a seed layer onto the FTO substrates was found to favor the growth of a uniform ZnO NWs array which shows saturation in the photocurrent density with a relatively low potential bias. Furthermore, prolonging the calcination time of the seed layer makes the ZnO NWs behave the better charge separation and improve the photo-electrochemical performance. Under the irradiation at a 75 mW cm{sup −2} from a simulated sunlight source, the ZnO NWs array electrode prepared from the seed layer with calcination at 350 °C for 5 h shows a saturated photocurrent density of 514 μA cm{sup −2} and a maximum half-cell solar-to-hydrogen (HC-STH) efficiency of 0.26% was obtained at 0.6 V versus reversible hydrogen electrode (RHE) in neutral electrolyte. - Highlights: • The seed layer annealing time strongly influences the textural and photo-activity of ZnO NWs. • The average diameter and density of ZnO NWs were controlled to 47–70 nm and 46–70 NWs μm{sup −2}, respectively. • ZnO NWs show promising application potential in solar-electrocatalytic water splitting under potential bias. • The ZnO NWs with SL annealing time = 5 h achieve the highest HC-STH efficiency of 0.26% at 0.6 V.

  7. Preparation of cadmium-doped ZnO thin films by SILAR and their ...

    Indian Academy of Sciences (India)

    Cadmium-doped zinc oxide (Cd : ZnO) thin films were deposited from sodium zincate bath .... of complex ion on the substrate followed by reaction of the .... Intensity (a.u.). 0. 500 .... trum confirmed the presence of Zn, O and Cd elements in the.

  8. Excimer laser processing of ZnO thin films prepared by the sol-gel process

    International Nuclear Information System (INIS)

    Winfield, R.J.; Koh, L.H.K.; O'Brien, Shane; Crean, Gabriel M.

    2007-01-01

    ZnO thin films were prepared on soda-lime glass from a single spin-coating deposition of a sol-gel prepared with anhydrous zinc acetate [Zn(C 2 H 3 O 2 ) 2 ], monoethanolamine [H 2 NC 2 H 4 OH] and isopropanol. The deposited films were dried at 50 and 300 deg. C. X-ray analysis showed that the films were amorphous. Laser annealing was performed using an excimer laser. The laser pulse repetition rate was 25 Hz with a pulse energy of 5.9 mJ, giving a fluence of 225 mJ cm -2 on the ZnO film. Typically, five laser pulses per unit area of the film were used. After laser processing, the hexagonal wurtzite phase of zinc oxide was observed from X-ray diffraction pattern analysis. The thin films had a transparency of greater than 70% in the visible region. The optical band-gap energy was 3.454 eV. Scanning electron microscopy and profilometry analysis highlighted the change in morphology that occurred as a result of laser processing. This comparative study shows that our sol-gel processing route differs significantly from ZnO sol-gel films prepared by conventional furnace annealing which requires temperatures above 450 deg. C for the formation of crystalline ZnO

  9. Improved damp heat stability of Ga-Doped ZnO thin film by pretreatment of the polyethylene terephthalate substrate

    Science.gov (United States)

    Kim, B. B.; Seo, S. G.; Lim, Y. S.; Choi, H.-S.; Seo, W.-S.; Park, H.-H.

    2013-09-01

    A study on the damp heat stability of transparent conducting ZnO thin film grown on a polyethylene terephthalate substrate (PET) is reported. By thermal annealing of the PET substrate at 100°C with Ar flow in a vacuum chamber prior to the sputtering growth of Ga-doped ZnO (GZO) thin film, significantly enhanced damp heat stability was achieved at 60°C with a 90% relative humidity. Electrical and structural characterizations of the GZO thin films were carried out and the effects of the pretreatment on the improved damp heat stability are discussed.

  10. Reversible p-type conductivity in H passivated nitrogen and phosphorous codoped ZnO thin films using rapid thermal annealing

    Energy Technology Data Exchange (ETDEWEB)

    Mannam, Ramanjaneyulu, E-mail: ramu.nov9@gmail.com [Department of Physics, Nano Functional Materials Technology Centre and Materials Science Research Centre, Indian Institute of Technology Madras, Chennai 600036 (India); Kumar, E. Senthil [SRM Research Institute, Department of Physics and Nanotechnology, SRM University, Kattankulathur 603203, Tamil Nadu (India); DasGupta, Nandita [Microelectronics and MEMS Laboratory, Electrical Engineering Department, Indian Institute of Technology Madras, Chennai 600036 (India); Ramachandra Rao, M.S., E-mail: msrrao@iitm.ac.in [Department of Physics, Nano Functional Materials Technology Centre and Materials Science Research Centre, Indian Institute of Technology Madras, Chennai 600036 (India)

    2017-04-01

    Highlights: • Electrical transport measurements revel that the (P, N) codoped ZnO thin films exhibited change in conductivity from p-type to n-type over a span of 120 days. • Hydrogen and carbon are found to be the main unintentional impurities in n-type (P, N) codoped ZnO thin films. • Rapid thermal annealing has been used to remove both H and C from the films. • Carbon can be removed at an annealing temperature of 600 °C, whereas, the dissociation of N−H complex takes place only at 800 °C. • The n-type (P, N) codoped ZnO thin film exhibited change in conductivity to p-type at an annealing temperature of 800 °C. - Abstract: We demonstrate reversible p-type nature of pulsed laser deposited (P, N) codoped ZnO thin films using rapid thermal annealing process. As grown thin films exhibited change in conductivity from p to n-type over a span of 120 days. Non-annealed n-type thin films contain unintentional donor impurities such as hydrogen and carbon. X-ray photoelectron spectroscopy and Raman measurements conclusively show that hydrogen passivates nitrogen acceptors by forming N−H complex. Carbon can be annealed out at 600 °C, whereas, the dissociation of N−H complex takes place at 800 °C. The films revert its p-type nature at an annealing temperature of 800 °C.

  11. Acoustoelectric Effect on the Responses of SAW Sensors Coated with Electrospun ZnO Nanostructured Thin Film

    Directory of Open Access Journals (Sweden)

    Zafer Ziya Ozturk

    2012-08-01

    Full Text Available In this study, zinc oxide (ZnO was a very good candidate for improving the sensitivity of gas sensor technology. The preparation of an electrospun ZnO nanostructured thin film on a 433 MHz Rayleigh wave based Surface Acoustic Wave (SAW sensor and the investigation of the acoustoelectric effect on the responses of the SAW sensor are reported. We prepared an electrospun ZnO nanostructured thin film on the SAW devices by using an electrospray technique. To investigate the dependency of the sensor response on the structure and the number of the ZnO nanoparticles, SAW sensors were prepared with different coating loads. The coating frequency shifts were adjusted to fall between 100 kHz and 2.4 MHz. The sensor measurements were performed against VOCs such as acetone, trichloroethylene, chloroform, ethanol, n-propanol and methanol vapor. The sensor responses of n-propanol have opposite characteristics to the other VOCs, and we attributed these characteristics to the elastic effect/acoustoelectric effect.

  12. High energy electron irradiation effects on Ga-doped ZnO thin films for optoelectronic space applications

    Science.gov (United States)

    Serrao, Felcy Jyothi; Sandeep, K. M.; Bhat, Shreesha; Dharmaprakash, S. M.

    2018-03-01

    Gallium-doped ZnO (GZO) thin films of thickness 394 nm were prepared by a simple, cost-effective sol-gel spin coating method. The effect of 8 MeV electron beam irradiation with different irradiation doses ranging from 0 to 10 kGy on the structural, optical and electrical properties was investigated. Electron irradiation influences the changes in the structural properties and surface morphology of GZO thin films. X-ray diffraction analysis showed that the polycrystalline nature of the GZO films is unaffected by the high energy electron irradiation. The grain size and the surface roughness were found maximum for the GZO film irradiated with 10 kGy electron dosage. The average transmittance of GZO thin films decreased after electron irradiation. The optical band gap of Ga-doped ZnO films was decreased with the increase in the electron dosage. The electrical resistivity of GZO films decreased from 4.83 × 10-3 to 8.725 × 10-4 Ω cm, when the electron dosage was increased from 0 to 10 kGy. The variation in the optical and electrical properties in the Ga-doped ZnO thin films due to electron beam irradiation in the present study is useful in deciding their compatibility in optoelectronic device applications in electron radiation environment.

  13. Quality improvement of ZnO thin layers overgrown on Si(100 substrates at room temperature by nitridation pretreatment

    Directory of Open Access Journals (Sweden)

    Peng Wang

    2012-06-01

    Full Text Available To improve the quality of ZnO thin film overgrown on Si(100 substrate at RT (room temperature, the Si(100 surface was pretreated with different methods. The influence of interface on the overgrown ZnO layers was investigated by atomic force microscopy, photoluminescence and X-ray diffraction. We found that the nitridation pretreatment could significantly improve the quality of RT ZnO thin film through two-fold effects: one was to buffer the big lattice mismatch and ease the stress resulted from heterojunction growth; the other was to balance the interface charge, block the symmetric inheritance from the cubic Si (100 substrate and thus restrain the formation of zincblende phase.

  14. Synthesis and characterization of porous structured ZnO thin film for dye sensitized solar cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Marimuthu, T.; Anandhan, N., E-mail: anandhan-kn@rediffmail.com; Mummoorthi, M. [School of Physics, Alagappa University, Karaikudi – 630 003 (India); Dharuman, V. [Department of Bioelectronics and Biosensors, Alagappa University, Karaikudi – 630 003 (India)

    2016-05-23

    Zinc oxide (ZnO) and zinc oxide/eosin yellow (ZnO/EY) thin films were potentiostatically deposited onto fluorine doped tin oxide (FTO) glass substrate. Effect of eosin yellow dye on structural, morphological and optical properties was studied. X-ray diffraction patterns, micro Raman spectra and photoluminescence (PL) spectra reveal hexagonal wurtzite structure with less atomic defects in 101 plane orientation of the ZnO/EY film. Scanning electron microscopy (SEM) images show flower for ZnO and porous like structure for ZnO/EY thin film, respectively. DSSC was constructed and evaluated by measuring the current density verses voltage curve.

  15. Low temperature growth and properties of ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Wu, Xiang; Zheng, Yufeng; Chen, Huibo; Gong, Lihong; Qu, Fengyu

    2011-01-01

    In this paper, well aligned ZnO nanorod arrays were synthesized by a simple hydrothermal route at a low temperature. The diameters of the as-synthesized products were 20–60 nm and the lengths were as much as several micrometers. The surfaces and tops of the nanorods were smooth. The as-grown nanorod arrays were investigated by x-ray powder diffraction (XRD), scanning electron microscope (SEM), transmission electron microscope (TEM), photoluminescence (PL) spectroscopy and contact angle (CA) analysis. The as-grown nanorods were single crystalline structures with a wurtzite phase, and grew along the [0001] direction. The PL spectrum with only one strong peak at 383 nm shows good intrinsic emission

  16. Electrical characteristics of ZnO nanorods reinforced polymer nanocomposite thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bhattacharjee, Snigdha; Roy, Asim, E-mail: 28.asim@gmail.com [Department of Physics National Institute Technology Silchar Silchar-788010, Assam (India)

    2015-05-15

    ZnO nanorods have been prepared by simple chemical method, which is used to fabricate organic bistable devices (OBDs). OBDs are fabricated by incorporating different weight percent (wt %) of chemically synthesized Zinc Oxide (ZnO) nanorods into polymethylmethacrylate (PMMA). Current-voltage (I-V) measurements of the spin coated ZnO+PMMA nanocomopsite thin film on indium tin oxide (ITO) coated glass substrate showed current hysteresis behaviour, which is an indication of memory effect. The samples exhibit two distinct resistance states, ON and OFF states, characterised by relatively low and high resistance of the OBDs, respectively. It is also observed that with change in ZnO dopant concentration the value of ON/OFF current changes. Higher ON/OFF current ratio is desired for practical applications. Current conduction mechanism of the devices has been explained invoking various existing models, and it has been found that the trapped-charge-limited conduction mechanism was dominant in our samples.

  17. PDMS-based triboelectric and transparent nanogenerators with ZnO nanorod arrays.

    Science.gov (United States)

    Ko, Yeong Hwan; Nagaraju, Goli; Lee, Soo Hyun; Yu, Jae Su

    2014-05-14

    Vertically-grown ZnO nanorod arrays (NRAs) on indium tin oxide (ITO)-coated polyethylene terephthalate (PET), as a top electrode of nanogenerators, were investigated for the antireflective property as well as an efficient contact surface in bare polydimethysiloxane (PDMS)-based triboelectric nanogenerators. Compared to conventional ITO-coated PET (i.e., ITO/PET), the ZnO NRAs considerably suppressed the reflectance from 20 to 9.7% at wavelengths of 300-1100 nm, creating a highly transparent top electrode, as demonstrated by theoretical analysis. Also, the interval time between the peaks of generated output voltage under external pushing forces was significantly decreased from 1.84 to 0.19 s because the reduced contact area of the PDMS by discrete surfaces of the ZnO NRAs on ITO/PET causes a rapid sequence for triboelectric charge generation process including rubbing and separating. Therefore, the use of this top electrode enabled to operate the transparent PDMS-based triboelectric nanogenerator at high frequency of external pushing force. Under different external forces of 0.3-10 kgf, the output voltage and current were also characterized.

  18. Mechanisms involved in the hydrothermal growth of ultra-thin and high aspect ratio ZnO nanowires

    Science.gov (United States)

    Demes, Thomas; Ternon, Céline; Morisot, Fanny; Riassetto, David; Legallais, Maxime; Roussel, Hervé; Langlet, Michel

    2017-07-01

    Hydrothermal synthesis of ZnO nanowires (NWs) with tailored dimensions, notably high aspect ratios (AR) and small diameters, is a major concern for a wide range of applications and still represents a challenging and recurring issue. In this work, an additive-free and reproducible hydrothermal procedure has been developed to grow ultra-thin and high AR ZnO NWs on sol-gel deposited ZnO seed layers. Controlling the substrate temperature and using a low reagent concentration (1 mM) has been found to be essential for obtaining such NWs. We show that the NW diameter remains constant at about 20-25 nm with growth time contrary to the NW length that can be selectively increased leading to NWs with ARs up to 400. On the basis of investigated experimental conditions along with thermodynamic and kinetic considerations, a ZnO NW growth mechanism has been developed which involves the formation and growth of nuclei followed by NW growth when the nuclei reach a critical size of about 20-25 nm. The low reagent concentration inhibits NW lateral growth leading to ultra-thin and high AR NWs. These NWs have been assembled into electrically conductive ZnO nanowire networks, which opens attractive perspectives toward the development of highly sensitive low-cost gas- or bio-sensors.

  19. Slow positron beam study of hydrogen ion implanted ZnO thin films

    International Nuclear Information System (INIS)

    Hu, Yi; Xue, Xudong; Wu, Yichu

    2014-01-01

    The effects of hydrogen related defect on the microstructure and optical property of ZnO thin films were investigated by slow positron beam, in combination with x-ray diffraction, infrared and photoluminescence spectroscopy. The defects were introduced by 90 keV proton irradiation with doses of 1×10 15 and 1×10 16 ions cm −2 . Zn vacancy and OH bonding (V Zn +OH) defect complex were identified in hydrogen implanted ZnO film by positron annihilation and infrared spectroscopy. The formation of these complexes led to lattice disorder in hydrogen implanted ZnO film and suppressed the luminescence process. - Highlights: • Hydrogen introduced by ion implantation can form hydrogen-related defect complex. • V Zn +OH defect complex is identified by positron annihilation and IR spectroscopy. • Irradiation defects suppress the luminescence process

  20. Investigation of the correlation between dielectric function, thickness and morphology of nano-granular ZnO very thin films

    Energy Technology Data Exchange (ETDEWEB)

    Gilliot, Mickaël, E-mail: mickael.gilliot@univ-reims.fr [Laboratoire d' Ingénierie et Sciences des Matériaux, Université de Reims Champagne-Ardenne (France); Hadjadj, Aomar [Laboratoire d' Ingénierie et Sciences des Matériaux, Université de Reims Champagne-Ardenne (France); Martin, Jérôme [Laboratoire de Nanotechnologie et d' Instrumentation Optique, Université de Technologie de Troyes (France)

    2015-12-31

    Thin nano-granular ZnO layers were prepared using a sol–gel synthesis and spin-coating deposition process with a thickness ranging between 20 and 120 nm. The complex dielectric function (ϵ) of the ZnO film was determined from spectroscopic ellipsometry measurements. Up to a critical thickness close to 60 nm, the magnitude of both the real and the imaginary parts of ϵ rapidly increases and then slowly tends to values closer to the bulk ZnO material. This trend suggests a drastic change in the film porosity at both sides of this critical thickness, due to the pre-heating and post-crystallization processes, as confirmed by additional characterization of the structure and the morphology of the ZnO films. - Highlights: • c-Axis oriented ZnO thin films were grown with different morphological states. • The morphology and structures are controlled by controlling the thickness. • The optical properties are correlated to morphological evolution. • Two growth behaviors and property evolutions are identified around a critical thickness.

  1. Field emission characteristics of ZnO nanoneedle array cell under ultraviolet irradiation

    International Nuclear Information System (INIS)

    Lee, Woong; Jeong, Min-Chang; Kim, Min Jun; Myoung, Jae-Min

    2007-01-01

    Field emission (FE) behaviours of ZnO nanoneedle array under ultraviolet (UV) irradiation have been investigated. UV irradiation noticeably stabilized the FE behaviours. Modifications in the tunnelling barrier height and effective aspect ratio due to the oxygen-related surface species, which can be desorbed by UV irradiation, are supposed to be responsible for these observations

  2. Synthesis of ZnO thin film by sol-gel spin coating technique for H2S gas sensing application

    Science.gov (United States)

    Nimbalkar, Amol R.; Patil, Maruti G.

    2017-12-01

    In this present work, zinc oxide (ZnO) thin film synthesized by a simple sol-gel spin coating technique. The structural, morphology, compositional, microstructural, optical, electrical and gas sensing properties of the film were studied by using XRD, FESEM, EDS, XPS, HRTEM, Raman, FTIR and UV-vis techniques. The ZnO thin film shows hexagonal wurtzite structure with a porous structured morphology. Gas sensing performance of synthesized ZnO thin film was tested initially for H2S gas at different operating temperatures as well as concentrations. The maximum gas response is achieved towards H2S gas at 300 °C operating temperature, at 100 ppm gas concentration as compared to other gases like CH3OH, Cl2, NH3, LPG, CH3COCH3, and C2H5OH with a good stability.

  3. Field electron emission improvement of ZnO nanorod arrays after Ar plasma treatment

    International Nuclear Information System (INIS)

    Li Chun; Fang Guojia; Yuan Longyan; Liu Nishuang; Li Jun; Li Dejie; Zhao Xingzhong

    2007-01-01

    Vertically well-aligned single crystal ZnO nanorod arrays were synthesized and enhanced field electron emission was achieved after radio-frequency (rf) Ar plasma treatment. With Ar plasma treatment for 30 min, flat tops of the as-grown ZnO nanorods have been etched into sharp tips without damaging ZnO nanorod geometrical morphologies and crystallinity. After the Ar ion bombardment, the emission current density increases from 2 to 20 μA cm -2 at 9.0 V μm -1 with a decrease in turn-on voltage from 7.1 to 4.8 V μm -1 at a current density of 1 μA cm -2 , which demonstrates that the field emission of the as-grown ZnO nanorods has been efficiently enhanced. The scanning electron microscopy (SEM) results, in conjunction with the results of transmission electron microscopy (TEM), Raman spectroscopy and photoluminescence observation, are used to investigate the mechanisms of the field emission enhancement. It is believed that the enhancements can be mainly attributed to the sharpening of rod tops, and the decrease of electrostatic screening effect

  4. Characteristics of hydrogen co-doped ZnO : Al thin films

    International Nuclear Information System (INIS)

    Lee, S H; Lee, T S; Lee, K S; Cheong, B; Kim, W M; Kim, Y D

    2008-01-01

    ZnO films co-doped with H and Al (HAZO) were prepared by sputtering ZnO targets containing 1 wt% Al 2 O 3 on Corning glass at a substrate temperature of 150 deg. C with Ar and H 2 /Ar gas mixtures. The effects of hydrogen addition to Al-doped ZnO (AZO) films with low Al content on the electrical, the optical and the structural properties of the as-grown films as well as the vacuum- and air-annealed films were examined. Secondary ion mass spectroscopy analysis showed that the hydrogen concentration increased with increasing H 2 in sputter gas. For the as-deposited films, the free carrier number increased with increasing H 2 . The Hall mobility increased at low hydrogen content, reaching a maximum before decreasing with a further increase of H 2 content in sputter gas. Annealing at 300 deg. C resulted in the removal of hydrogen, causing a decrease in the carrier concentration. It was shown that hydrogen might exist as single isolated interstitial hydrogen bound with oxygen, thereby acting like an anionic dopant. Also, it was shown that the addition of hydrogen to ZnO films doped with low metallic dopant concentration could yield transparent conducting films with very low absorption loss as well as with proper electrical properties, which is suitable for thin film solar cell applications

  5. Vertically aligned ZnO nanowire arrays in Rose Bengal-based dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Pradhan, Basudev; Batabyal, Sudip K.; Pal, Amlan J. [Indian Association for the Cultivation of Science, Department of Solid State Physics, Kolkata 700032 (India)

    2007-05-23

    We fabricate dye-sensitized solar cells (DSSC) using vertically oriented, high density, and crystalline array of ZnO nanowires, which can be a suitable alternative to titanium dioxide nanoparticle films. The vertical nanowires provide fast routes or channels for electron transport to the substrate electrode. As an alternative to conventional ruthenium complex, we introduce Rose Bengal dye, which acts as a photosensitizer in the dye-sensitized solar cells. The dye energetically matches the ZnO with usual KI-I{sub 2} redox couple for dye-sensitized solar cell applications. (author)

  6. Large-area fabrication of patterned ZnO-nanowire arrays using light stamping lithography.

    Science.gov (United States)

    Hwang, Jae K; Cho, Sangho; Seo, Eun K; Myoung, Jae M; Sung, Myung M

    2009-12-01

    We demonstrate selective adsorption and alignment of ZnO nanowires on patterned poly(dimethylsiloxane) (PDMS) thin layers with (aminopropyl)siloxane self-assembled monolayers (SAMs). Light stamping lithography (LSL) was used to prepare patterned PDMS thin layers as neutral passivation regions on Si substrates. (3-Aminopropyl)triethoxysilane-based SAMs were selectively formed only on regions exposing the silanol groups of the Si substrates. The patterned positively charged amino groups define and direct the selective adsorption of ZnO nanowires with negative surface charges in the protic solvent. This procedure can be adopted in automated printing machines that generate patterned ZnO-nanowire arrays on large-area substrates. To demonstrate its usefulness, the LSL method was applied to prepare ZnO-nanowire transistor arrays on 4-in. Si wafers.

  7. Effects of stabilizer ratio on photoluminescence properties of sol-gel ZnO nano-structured thin films

    International Nuclear Information System (INIS)

    Boudjouan, F.; Chelouche, A.; Touam, T.; Djouadi, D.; Khodja, S.; Tazerout, M.; Ouerdane, Y.; Hadjoub, Z.

    2015-01-01

    Nanostructured ZnO thin films with different molar ratios of MEA to zinc acetate (0.5, 1.0, 1.5 and 2.0) have been deposited on glass substrates by a sol–gel dip coating technique. X-ray diffraction, Scanning Electron Microscopy, UV–visible spectrophotometry and photoluminescence spectroscopy have been employed to investigate the effect of MEA stabilizer ratio on structural, morphological, absorbance and emission properties of the ZnO thin films. Diffraction patterns have shown that all the films are polycrystalline and exhibit a wurtzite hexagonal structure. The c axis orientation has been enhanced with increasing stabilizer ratio. SEM micrographs have revealed that the morphology of the ZnO films depend on stabilizer ratio. The UV–visible absorption spectra have demonstrated that the optical absorption is affected by stabilizer ratio. The photoluminescence spectra have indicated one ultraviolet and two visible emission bands (green and red), while band intensities are found to be dependent on stabilizer ratio. ZnO thin films deposited at MEA ratio of 1.0 show the highest UV emission while the minimum UV emission intensity is observed in thin films deposited at ratio of 0.5 and the maximum green has been recorded for films deposited at MEA ratio of 2.0. - Highlight: • c axis orientation increases with increasing MEA ratio. • The increase of MEA ration from 0.5 to 1.0 enhances greatly the UV emission. • The larger I UV /I visible is obtained for the MEA to Zn ratio of 1:1. • The MEA ratio of 0.5 favors the formation of large density of V zn . • The MEA ratio of 2.0 increases the V o density

  8. Photoelectrochemical water splitting under visible light over anti-photocorrosive In2O3-coupling ZnO nanorod arrays photoanode

    International Nuclear Information System (INIS)

    Zhang, Yan; Zhang, Jinqiu; Nie, Mengyan; Sun, Kai; Li, Chunhu; Yu, Jianqiang

    2015-01-01

    In 2 O 3 quantum dots with a high crystallinity were deposited on the surface of ZnO nanorods through a chemistry bath method. The resulting In 2 O 3 -sensitizing ZnO nanorod arrays not only exhibited enhanced photoelectrochemical activity for water splitting under visible-light irradiation, but also possessed anti-photocorrosion property. The photo-induced charge-transfer property of In 2 O 3 could be improved greatly by coupling with ZnO. This observation demonstrated that the heterojunction at the interface between In 2 O 3 and ZnO could efficiently reduce the recombination of photo-induced electron–hole pairs and increase the lifetime of charge carriers and therefore enhance the photo-to-current efficiency of the In 2 O 3 –ZnO nanocrystalline arrays. It reveals that the heterojunction construction between two different semiconductors plays a very important role in determining the dynamic properties of their photogenerated charge carriers and their photo-to-current conversion efficiency

  9. ZnO synthesized in air by fs laser irradiation on metallic Zn thin films

    Science.gov (United States)

    Esqueda-Barrón, Y.; Herrera, M.; Camacho-López, S.

    2018-05-01

    We present results on rapid femtosecond laser synthesis of nanostructured ZnO. We used metallic Zn thin films to laser scan along straight tracks, until forming nanostructured ZnO. The synthesis dependence on laser irradiation parameters such as the per pulse fluence, integrated fluence, laser scan speed, and number of scans were explored carefully. SEM characterization showed that the morphology of the obtained ZnO is dictated by the integrated fluence and the laser scan speed; micro Raman and XRD results allowed to identify optimal laser processing conditions for getting good quality ZnO; and cathodoluminescence measurements demonstrated that a single laser scan at high per pulse laser fluence, but a medium integrated laser fluence and a medium laser scan speed favors a low density of point-defects in the lattice. Electrical measurements showed a correlation between resistivity of the laser produced ZnO and point-defects created during the synthesis. Transmittance measurements showed that, the synthesized ZnO can reach down to the supporting fused silica substrate under the right laser irradiation conditions. The physical mechanism for the formation of ZnO, under ultrashort pulse laser irradiation, is discussed in view of the distinct times scales given by the laser pulse duration and the laser pulse repetition rate.

  10. Synthesis, microstructural characterization and optical properties of undoped, V and Sc doped ZnO thin films

    International Nuclear Information System (INIS)

    Amezaga-Madrid, P.; Antunez-Flores, W.; Ledezma-Sillas, J.E.; Murillo-Ramirez, J.G.; Solis-Canto, O.; Vega-Becerra, O.E.; Martinez-Sanchez, R.; Miki-Yoshida, M.

    2011-01-01

    Research highlights: → Undoped, V and Sc doped ZnO thin films by Aerosol Assisted Chemical Vapour Deposition. → Optimum substrate temperatures of 673 K and 623 K for Sc and V doped films. → Around one third of the dopants in solution were deposited into the films. → Crystallite and grain size decreased with the increase of dopant concentration. → Optical band gap increased from 3.29 to 3.32 eV for undoped to 7 Sc/Zn at. %. - Abstract: Many semiconductor oxides (ZnO, TiO 2 , SnO 2 ) when doped with a low percentage of non-magnetic (V, Sc) or magnetic 3d (Co, Mn, Ni, Fe) cation behave ferromagnetically. They have attracted a great deal of interest due to the integration of semiconducting and magnetic properties in a material. ZnO is one of the most promising materials to carry out these tasks in view of the fact that it is optically transparent and has n or p type conductivity. Here, we report the synthesis, microstructural characterization and optical properties of undoped, V and Sc doped zinc oxide thin films. ZnO based thin films with additions of V and Sc were deposited by the Aerosol Assisted Chemical Vapour Deposition method. V and Sc were incorporated separately in the precursor solution. The films were uniform, transparent and non-light scattering. The microstructure of the films was characterized by Grazing Incidence X-ray Diffraction, Scanning Electron Microscopy, and Scanning Probe Microscopy. Average grain size and surface rms roughness were estimated by the measurement of Atomic Force Microscopy. The microstructure of doped ZnO thin films depended on the type and amount of dopant material incorporated. The optical properties were determined from specular reflectance and transmittance spectra. Results were analyzed to determine the optical constant and band gap of the films. An increase in the optical band gap with the content of Sc dopant was obtained.

  11. Plasmonic Properties of Vertically Aligned Nanowire Arrays

    Directory of Open Access Journals (Sweden)

    Hua Qi

    2012-01-01

    Full Text Available Nanowires (NWs/Ag sheath composites were produced to investigate plasmonic coupling between vertically aligned NWs for surface-enhanced Raman scattering (SERS applications. In this investigation, two types of vertical NW arrays were studied; those of ZnO NWs grown on nanosphere lithography patterned sapphire substrate via vapor-liquid-solid (VLS mechanism and Si NW arrays produced by wet chemical etching. Both types of vertical NW arrays were coated with a thin layer of silver by electroless silver plating for SERS enhancement studies. The experimental results show extremely strong SERS signals due to plasmonic coupling between the NWs, which was verified by COMSOL electric field simulations. We also compared the SERS enhancement intensity of aligned and random ZnO NWs, indicating that the aligned NWs show much stronger and repeatable SERS signal than those grown in nonaligned geometries.

  12. Effect of high-energy electron beam irradiation on the transmittance of ZnO thin films on transparent substrates

    International Nuclear Information System (INIS)

    Yun, Eui-Jung; Jung, Jin-Woo; Han, Young-Hwan; Kim, Min-Wan; Lee, Byung Cheol

    2010-01-01

    We investigated in this study the effects of high-energy electron beam irradiation (HEEBI) on the optical transmittance of undoped ZnO films grown on transparent substrates, such as corning glass and polyethersulfone (PES) plastic substrates, with a radio frequency (rf) magnetron sputtering technique. The ZnO thin films were treated with HEEBI in air at RT with an electron beam energy of 1 MeV and doses of 4.7 x 10 14 - 4.7 x 10 16 electrons/cm 2 . The optical transmittance of the ZnO films was measured using an ultraviolet visible near-infrared spectrophotometer. The detailed estimation process for separating the transmittance of HEEBI-treated ZnO films from the total transmittance of ZnO films on transparent substrates treated with HEEBI is given in this paper. We concluded that HEEBI causes a slight suppression in the optical transmittance of ZnO thin films. We also concluded that HEEBI treatment with a high dose shifted the optical band gap (E g ) toward the lower energy region from 3.29 to 3.28 eV whereas that with a low dose unchanged E g at 3.25 eV. This shift suggested that HEEBI at RT at a high dose acts like an annealing treatment at high temperature.

  13. Defect studies of thin ZnO films prepared by pulsed laser deposition

    International Nuclear Information System (INIS)

    Vlček, M; Čížek, J; Procházka, I; Novotný, M; Bulíř, J; Lančok, J; Anwand, W; Brauer, G; Mosnier, J-P

    2014-01-01

    Thin ZnO films were grown by pulsed laser deposition on four different substrates: sapphire (0 0 0 1), MgO (1 0 0), fused silica and nanocrystalline synthetic diamond. Defect studies by slow positron implantation spectroscopy (SPIS) revealed significantly higher concentration of defects in the studied films when compared to a bulk ZnO single crystal. The concentration of defects in the films deposited on single crystal sapphire and MgO substrates is higher than in the films deposited on amorphous fused silica substrate and nanocrystalline synthetic diamond. Furthermore, the effect of deposition temperature on film quality was investigated in ZnO films deposited on synthetic diamond substrates. Defect studies performed by SPIS revealed that the concentration of defects firstly decreases with increasing deposition temperature, but at too high deposition temperatures it increases again. The lowest concentration of defects was found in the film deposited at 450° C.

  14. Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

    Czech Academy of Sciences Publication Activity Database

    Melikhova, O.; Čížek, J.; Lukáč, F.; Vlček, M.; Novotný, Michal; Bulíř, Jiří; Lančok, Ján; Anwand, W.; Brauer, G.; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.

    2013-01-01

    Roč. 580, suppl. 1 (2013), S40-S43 ISSN 0925-8388 R&D Projects: GA ČR(CZ) GAP108/11/0958 Institutional support: RVO:68378271 Keywords : defects * hydrogen * positron annihilation * thin films * ZnO Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.726, year: 2013

  15. ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays

    Science.gov (United States)

    Meško, Marcel; Ou, Qiongrong; Matsuda, Takafumi; Ishikawa, Tomokazu; Veis, Martin; Antoš, Roman; Ogino, Akihisa; Nagatsu, Masaaki

    2009-06-01

    We report on ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays. We observed a significant reduction of the internal multiple light scattering phenomena, which are characteristic for ZnO micropowders. The microsized grains of the commercially available ZnO:Zn (P 15) were reduced to the nanometre scale by pulsed laser ablation at an oxygen ambient pressure of 10 kPa. Our investigations show no crystalline change and no shift of the broad green emission peak at 500 nm for the ZnO nanopowder. For the application in field emission displays, we demonstrate the possibility of achieving cathodoluminescence with a fine pitch size of 100 µm of the patterned pixels without requiring additional electron beam focusing and without a black matrix. Moreover, the presented results show the feasibility of employing ZnO nanopowder as a detection material for the phosphorus screen method, which is able to localize emission sites of carbon nanotube films and arrays with an accuracy comparable to scanning anode field emission microscopy.

  16. ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays

    International Nuclear Information System (INIS)

    Mesko, Marcel; Ou Qiongrong; Matsuda, Takafumi; Ishikawa, Tomokazu; Ogino, Akihisa; Nagatsu, Masaaki; Veis, Martin; Antos, Roman

    2009-01-01

    We report on ZnO nanopowder induced light scattering for improved visualization of emission sites in carbon nanotube films and arrays. We observed a significant reduction of the internal multiple light scattering phenomena, which are characteristic for ZnO micropowders. The microsized grains of the commercially available ZnO:Zn (P 15) were reduced to the nanometre scale by pulsed laser ablation at an oxygen ambient pressure of 10 kPa. Our investigations show no crystalline change and no shift of the broad green emission peak at 500 nm for the ZnO nanopowder. For the application in field emission displays, we demonstrate the possibility of achieving cathodoluminescence with a fine pitch size of 100 μm of the patterned pixels without requiring additional electron beam focusing and without a black matrix. Moreover, the presented results show the feasibility of employing ZnO nanopowder as a detection material for the phosphorus screen method, which is able to localize emission sites of carbon nanotube films and arrays with an accuracy comparable to scanning anode field emission microscopy.

  17. 16.1% Efficient Hysteresis-Free Mesostructured Perovskite Solar Cells Based on Synergistically Improved ZnO Nanorod Arrays

    KAUST Repository

    Mahmood, Khalid

    2015-06-01

    Significant efficiency improvements are reported in mesoscopic perovskite solar cells based on the development of a low-temperature solution-processed ZnO nanorod (NR) array exhibiting higher NR aspect ratio, enhanced electron density, and substantially reduced work function than conventional ZnO NRs. These features synergistically result in hysteresis-free, scan-independent, and stabilized devices with an efficiency of 16.1%. Electron-rich, nitrogen-doped ZnO (N:ZnO) NR-based electron transporting materials (ETMs) with enhanced electron mobility produced using ammonium acetate show consistently higher efficiencies by one to three power points than undoped ZnO NRs. Additionally, the preferential electrostatic interaction between the -nonpolar facets of N:ZnO and the conjugated polyelectrolyte polyethylenimine (PEI) has been relied on to promote the hydrothermal growth of high aspect ratio NR arrays and substantially improve the infiltration of the perovskite light absorber into the ETM. Using the same interactions, a conformal PEI coating on the electron-rich high aspect ratio N:ZnO NR arrays is -successfully applied, resulting in a favorable work function shift and altogether leading to the significant boost in efficiency from <10% up to >16%. These results largely surpass the state-of-the-art PCE of ZnO-based perovskite solar cells and highlight the benefits of synergistically combining mesoscale control with doping and surface modification. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

  18. Variation of microstructural and optical properties in SILAR grown ZnO thin films by thermal treatment.

    Science.gov (United States)

    Valanarasu, S; Dhanasekaran, V; Chandramohan, R; Kulandaisamy, I; Sakthivelu, A; Mahalingam, T

    2013-08-01

    The influence of thermal treatment on the structural and morphological properties of the ZnO films deposited by double dip Successive ionic layer by adsorption reaction is presented. The effect of annealing temperature and time in air ambient is presented in detail. The deposited films were annealed from 200 to 400 degrees C in air and the structural properties were determined as a function of annealing temperature by XRD. The studies revealed that films were exhibiting preferential orientation along (002) plane. The other structural parameters like the crystallite size (D), micro strain (epsilon), dislocation density (delta) and stacking fault (alpha) of as-deposited and annealed ZnO films were evaluated and reported. The optical properties were also studied and the band gap of the ZnO thins films varied from 3.27 to 3.04 eV with the annealing temperature. SEM studies revealed that the hexagonal shaped grains with uniformly distributed morphology in annealed ZnO thin films. It has been envisaged using EDX analysis that the near stoichiometric composition of the film can be attained by thermal treatment during which microstructural changes do occur.

  19. Optoelectronic properties of doped hydrothermal ZnO thin films

    KAUST Repository

    Mughal, Asad J.

    2017-03-10

    Group III impurity doped ZnO thin films were deposited on MgAl2O3 substrates using a simple low temperature two-step deposition method involving atomic layer deposition and hydrothermal epitaxy. Films with varying concentrations of either Al, Ga, or In were evaluated for their optoelectronic properties. Inductively coupled plasma atomic emission spectroscopy was used to determine the concentration of dopants within the ZnO films. While Al and Ga-doped films showed linear incorporation rates with the addition of precursors salts in the hydrothermal growth solution, In-doped films were shown to saturate at relatively low concentrations. It was found that Ga-doped films showed the best performance in terms of electrical resistivity and optical absorbance when compared to those doped with In or Al, with a resistivity as low as 1.9 mΩ cm and an optical absorption coefficient of 441 cm−1 at 450 nm.

  20. A patterned ZnO nanorod array/gas sensor fabricated by mechanoelectrospinning-assisted selective growth.

    Science.gov (United States)

    Wang, Xiaomei; Sun, Fazhe; Huang, Yongan; Duan, Yongqing; Yin, Zhouping

    2015-02-21

    Micropatterned ZnO nanorod arrays were fabricated by the mechanoelectrospinning-assisted direct-writing process and the hydrothermal growth process, and utilized as gas sensors that exhibited excellent Ohmic behavior and sensitivity response to oxidizing gas NO2 at low concentrations (1-100 ppm).

  1. Defect-band mediated ferromagnetism in Gd-doped ZnO thin films

    KAUST Repository

    Venkatesh, S.

    2015-01-07

    Gd-doped ZnO thin films prepared by pulsed laser deposition with Gd concentrations varying from 0.02–0.45 atomic percent (at. %) showed deposition oxygen pressure controlled ferromagnetism. Thin films prepared with Gd dopant levels (

  2. Effect of nickel doping on the photocatalytic activity of ZnO thin films under UV and visible light

    International Nuclear Information System (INIS)

    Kaneva, Nina V.; Dimitrov, Dimitre T.; Dushkin, Ceco D.

    2011-01-01

    Nanostructured ZnO thin films with different concentrations of Ni 2+ doping (0, 1, 5, 10 and 15 wt.%) are prepared by the sol-gel method for the first time. The thin films are prepared from zinc acetate, 2-methoxyethanol and monoethanolamine on glass substrates by using dip coating method. The films comprise of ZnO nanocrystallites with hexagonal crystal structure, as revealed by X-ray diffraction. The film surface is with characteristic ganglia-like structure as observed by Scanning Electron Microscopy. Furthermore, the Ni-doped films are tested with respect to the photocatalysis in aqueous solutions of malachite green upon UV-light illumination, visible light and in darkness. The initial concentration of malachite green and the amount of catalyst are varied during the experiments. It is found that increasing of the amount of Ni 2+ ions with respect to ZnO generally lowers the photocatalytic activity in comparison with the pure ZnO films. Nevertheless, all films exhibit a substantial activity under both, UV and visible light and in darkness as well, which is promising for the development of new ZnO photocatalysts by the sol-gel method.

  3. ZnO nanorod array polydimethylsiloxane composite solid phase micro-extraction fiber coating: fabrication and extraction capability.

    Science.gov (United States)

    Wang, Dan; Wang, Qingtang; Zhang, Zhuomin; Chen, Guonan

    2012-01-21

    ZnO nanorod array coating is a novel kind of solid-phase microextraction (SPME) fiber coating which shows good extraction capability due to the nanostructure. To prepare the composite coating is a good way to improve the extraction capability. In this paper, the ZnO nanorod array polydimethylsiloxane (PDMS) composite SPME fiber coating has been prepared and its extraction capability for volatile organic compounds (VOCs) has been studied by headspace sampling the typical volatile mixed standard solution of benzene, toluene, ethylbenzene and xylene (BTEX). Improved detection limit and good linear ranges have been achieved for this composite SPME fiber coating. Also, it is found that the composite SPME fiber coating shows good extraction selectivity to the VOCs with alkane radicals.

  4. Ga-doped ZnO thin film surface characterization by wavelet and fractal analysis

    Energy Technology Data Exchange (ETDEWEB)

    Jing, Chenlei; Tang, Wu, E-mail: tang@uestc.edu.cn

    2016-02-28

    Graphical abstract: - Highlights: • Multi-resolution signal decomposition of wavelet transform is applied to Ga-doped ZnO thin films with various thicknesses. • Fractal properties of GZO thin films are investigated by box counting method. • Fractal dimension is not in conformity with original RMS roughness. • Fractal dimension mainly depends on the underside diameter (grain size) and distance between adjacent grains. - Abstract: The change in roughness of various thicknesses Ga-doped ZnO (GZO) thin films deposited by magnetron reactive sputtering on glass substrates at room temperature was measured by atomic force microscopy (AFM). Multi-resolution signal decomposition based on wavelet transform and fractal geometry was applied to process surface profiles, to evaluate the roughness trend of relevant frequency resolution. The results give a six-level decomposition and the results change with deposited time and surface morphology. Also, it is found that fractal dimension is closely connected to the underside diameter (grain size) and the distance between adjacent grains that affect the change rate of surface and the increase of the defects such as abrupt changes lead to a larger value of fractal dimension.

  5. Friction and wear behavior of nitrogen-doped ZnO thin films deposited via MOCVD under dry contact

    Directory of Open Access Journals (Sweden)

    U.S. Mbamara

    2016-06-01

    Full Text Available Most researches on doped ZnO thin films are tilted toward their applications in optoelectronics and semiconductor devices. Research on their tribological properties is still unfolding. In this work, nitrogen-doped ZnO thin films were deposited on 304 L stainless steel substrate from a combination of zinc acetate and ammonium acetate precursor by MOCVD technique. Compositional and structural studies of the films were done using Rutherford Backscattering Spectroscopy (RBS and X-ray Diffraction (XRD. The frictional behavior of the thin film coatings was evaluated using a ball-on-flat configuration in reciprocating sliding under dry contact condition. After friction test, the flat and ball counter-face surfaces were examined to assess the wear dimension and failure mechanism. Both friction behavior and wear (in the ball counter-face were observed to be dependent on the crystallinity and thickness of the thin film coatings.

  6. Electric-field driven insulator-metal transition and tunable magnetoresistance in ZnO thin film

    Science.gov (United States)

    Zhang, Le; Chen, Shanshan; Chen, Xiangyang; Ye, Zhizhen; Zhu, Liping

    2018-04-01

    Electrical control of the multistate phase in semiconductors offers the promise of nonvolatile functionality in the future semiconductor spintronics. Here, by applying an external electric field, we have observed a gate-induced insulator-metal transition (MIT) with the temperature dependence of resistivity in ZnO thin films. Due to a high-density carrier accumulation, we have shown the ability to inverse change magnetoresistance in ZnO by ionic liquid gating from 10% to -2.5%. The evolution of photoluminescence under gate voltage was also consistent with the MIT, which is due to the reduction of dislocation. Our in-situ gate-controlled photoluminescence, insulator-metal transition, and the conversion of magnetoresistance open up opportunities in searching for quantum materials and ZnO based photoelectric devices.

  7. Scintillation characteristic of In, Ga-doped ZnO thin films with different dopant concentrations

    International Nuclear Information System (INIS)

    Fujimoto, Yutaka; Yanagida, Takayuki; Yokota, Yuui; Chani, Valery; Yoshikawa, Akira; Sekiwa, Hideyuki

    2011-01-01

    The present study describes the first detailed evaluation of the rise and the decay time of scintillation phenomenon in In 3+ - and Ga 3+ -doped ZnO thin films with different dopant concentrations. In 3+ -(25, 55, and 141 ppm) and Ga 3+ -(33, 67, 333, and 1374 ppm) doped ZnO films were grown by the Liquid Phase Epitaxy (LPE) method. The characterization was performed using the pulse X-ray equipped streak camera system. Both the rise and the decay times were shortened considerably with increasing content of In 3+ and Ga 3+ in the films. However, the scintillation light yield under 241 Am α-ray excitation reduced when concentration of In 3+ and Ga 3+ in the ZnO films was high. (author)

  8. Hydrothermal synthesis of highly crystalline ZnO nanorod arrays: Dependence of morphology and alignment on growth conditions

    Energy Technology Data Exchange (ETDEWEB)

    Azzez, Shrook A., E-mail: shurouq44@yahoo.com [Institutes of Nano-Optoelectronic Research and Technology Laboratory (INOR), Ministry of Science and Technology, Baghdad (Iraq); Hassan, Z.; Alimanesh, M.; Rasheed, Hiba S.; Sabah, Fayroz A.; Abdulateef, Sinan A. [Institutes of Nano-Optoelectronic Research and Technology Laboratory (INOR), Ministry of Science and Technology, Baghdad (Iraq); Hassan, J. J. [Department of Physics, College of Science, University of Basrah, Basrah (Iraq)

    2016-07-06

    Highly oriented zinc oxide nanorod were successfully grown on seeded p-type silicon substrate by hydrothermal methode. The morphology and the crystallinty of ZnO c-axis (002) arrays were systematically studied using field emission scanning electron microscopy (FESEM) and X-ray diffraction (XRD) methods. The effect of seed layer pre-annealing on nanorods properties was explained according to the nucleation site of ZnO nanoparticles on silicon substrate. In addition, the variation of the equal molarity of zinc nitrate hexahydrate and hexamine concentrations in the reaction vessel play a crucial role related to the ZnO nanorods.

  9. Growth and investigation of antifungal properties of ZnO nanorod arrays on the glass

    International Nuclear Information System (INIS)

    Eskandari, M.; Haghighi, N.; Ahmadi, V.; Haghighi, F.; Mohammadi, SH.R.

    2011-01-01

    In this study, we have investigated the antifungal activity of ZnO nanorods prepared by the chemical solution method against Candida albicans. In the study, Zinc oxide nanorods have been deposited on glass substrates using the chemical solution method. The as-grown samples are characterized by scanning electron microscopy (SEM) and X-ray diffraction (XRD). X-ray diffraction (XRD) showed zinc oxide nanorods grown in (0 0 2) orientation. The antifungal results indicated that ZnO nanorod arrays exhibit stable properties after two months and play an important role in the growth inhibitory of Candida albicans.

  10. Fabrication of ZnO Nanowires Arrays by Anodization and High-Vacuum Die Casting Technique, and Their Piezoelectric Properties

    Science.gov (United States)

    Kuo, Chin-Guo; Chang, Ho; Wang, Jian-Hao

    2016-01-01

    In this investigation, anodic aluminum oxide (AAO) with arrayed and regularly arranged nanopores is used as a template in the high-vacuum die casting of molten zinc metal (Zn) into the nanopores. The proposed technique yields arrayed Zn nanowires with an aspect ratio of over 600. After annealing, arrayed zinc oxide (ZnO) nanowires are obtained. Varying the anodizing time yields AAO templates with thicknesses of approximately 50 μm, 60 μm, and 70 μm that can be used in the fabrication of nanowires of three lengths with high aspect ratios. Experimental results reveal that a longer nanowire generates a greater measured piezoelectric current. The ZnO nanowires that are fabricated using an alumina template are anodized for 7 h and produce higher piezoelectric current of up to 69 pA. PMID:27023546

  11. Fabrication of ZnO Nanowires Arrays by Anodization and High-Vacuum Die Casting Technique, and Their Piezoelectric Properties.

    Science.gov (United States)

    Kuo, Chin-Guo; Chang, Ho; Wang, Jian-Hao

    2016-03-24

    In this investigation, anodic aluminum oxide (AAO) with arrayed and regularly arranged nanopores is used as a template in the high-vacuum die casting of molten zinc metal (Zn) into the nanopores. The proposed technique yields arrayed Zn nanowires with an aspect ratio of over 600. After annealing, arrayed zinc oxide (ZnO) nanowires are obtained. Varying the anodizing time yields AAO templates with thicknesses of approximately 50 μm, 60 μm, and 70 μm that can be used in the fabrication of nanowires of three lengths with high aspect ratios. Experimental results reveal that a longer nanowire generates a greater measured piezoelectric current. The ZnO nanowires that are fabricated using an alumina template are anodized for 7 h and produce higher piezoelectric current of up to 69 pA.

  12. Ultraviolet Stimulated Emission from Sol-Gel Spin Coated ZnO Thin Films

    Directory of Open Access Journals (Sweden)

    Ahmed S. Razeen

    2017-01-01

    Full Text Available Low cost ultraviolet stimulated emission has been generated using optical excitation of ZnO thin films deposited by sol-gel spin coating on n+ As-doped 100 Si-substrate. The number of deposited layers and the heat treatment have been investigated to obtain a film that can generate stimulated emission under optical excitation. The optimum condition for preparation of the film has been presented. X-ray diffraction and scanning electron microscope have been used for structural and morphological investigations. Input-output intensity dependence and spectral width, peak emission wavelength, and the quantum efficiency versus the pump intensity have been presented. A quantum efficiency of about 24.2% has been reported, a power exponent higher than 8 has been obtained in input-output intensity dependence, and a threshold of about 23 Mw/cm2 has been evaluated for the samples. The mechanism by which stimulated emission occurs has been discussed. The results show that sol-gel spin coating is a promising method for generating ultraviolet stimulated emission from ZnO thin films.

  13. Probing magnetism and electronic structure of Fe-doped ZnO thin films

    International Nuclear Information System (INIS)

    El Amiri, A.; Moubah, R.; Lmai, F.; Abid, M.; Hassanain, N.; Hlil, E.K.; Lassri, H.

    2016-01-01

    Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

  14. Probing magnetism and electronic structure of Fe-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    El Amiri, A., E-mail: aelamiri@casablanca.ma [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Moubah, R., E-mail: reda.moubah@hotmail.fr [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Lmai, F. [LPTA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Abid, M. [LPFA, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco); Hassanain, N. [Laboratoire de Physique des Matériaux, Faculté des Sciences, BP 1014 Rabat (Morocco); Hlil, E.K. [Institut Néel, CNRS et Université Joseph Fourier, BP 166, 38042 Grenoble (France); Lassri, H. [LPMMAT, Faculté des Sciences Ain Chock, Université Hassan II, BP 5366 Mâarif, Casablanca (Morocco)

    2016-01-15

    Ab-initio calculations using Korringa–Kohn–Rostoker method combined with the coherent potential approximation were performed in order to study the magnetic properties of Fe-doped ZnO thin films with different Fe contents. The extracted parameters are compared with those determined experimentally. Based on total and partial densities of state curves, we demonstrate that there is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions, respectively. The dominant mechanism is found to be antiferromagnetic. However, with increasing Fe content the ferromagnetic contribution increases. In addition, the effect of structural defects on the magnetism of the system is reported. It is shown that both Zn and O vacancies increase ferromagnetism, which is more pronounced in case of Zn. - Highlights: • The KKR–CPA approach was used to study the magnetism of Fe-doped ZnO thin films. • There is a competition between p–d exchange and superexchange mechanisms leading to weak ferromagnetic and antiferromagnetic contributions. • Zn vacancies are more significant than the O ones for obtaining ferromagnetism.

  15. Structural and Magnetic Properties of Mn doped ZnO Thin Film Deposited by Pulsed Laser Deposition

    KAUST Repository

    Baras, Abdulaziz

    2011-07-01

    Diluted magnetic oxide (DMO) research is a growing field of interdisciplinary study like spintronic devices and medical imaging. A definite agreement among researchers concerning the origin of ferromagnetism in DMO has yet to be reached. This thesis presents a study on the structural and magnetic properties of DMO thin films. It attempts to contribute to the understanding of ferromagnetism (FM) origin in DMO. Pure ZnO and Mn doped ZnO thin films have been deposited by pulsed laser deposition (PLD) using different deposition conditions. This was conducted in order to correlate the change between structural and magnetic properties. Structural properties of the films were characterized using x-ray diffraction (XRD) and scanning electron microscopy (SEM). The superconducting quantum interference device (SQUID) was used to investigate the magnetic properties of these films. The structural characterizations showed that the quality of pure ZnO and Mn doped ZnO films increased as oxygen pressure (PO) increased during deposition. All samples were insulators. In Mn doped films, Mn concentration decreased as PO increased. The Mn doped ZnO samples were deposited at 600˚C and oxygen pressure from 50-500mTorr. All Mn doped films displayed room temperature ferromagnetism (RTFM). However, at 5 K a superparamagnetic (SPM) behavior was observed in these samples. This result was accounted for by the supposition that there were secondary phase(s) causing the superparamagnetic behavior. Our findings hope to strengthen existing research on DMO origins and suggest that secondary phases are the core components that suppress the ferromagnetism. Although RTFM and SPM at low temperature has been observed in other systems (e.g., Co doped ZnO), we are the first to report this behavior in Mn doped ZnO. Future research might extend the characterization and exploration of ferromagnetism in this system.

  16. Influence of annealing temperature on the structural, optical and mechanical properties of ALD-derived ZnO thin films

    International Nuclear Information System (INIS)

    Yen, C.-Y.; Jian, S.-R.; Chen, G.-J.; Lin, C.-M.; Lee, H.-Y.; Ke, W.-C.; Liao, Y.-Y.; Yang, P.-F.; Wang, C.-T.; Lai, Y.-S.; Jang, Jason S.-C.; Juang, J.-Y.

    2011-01-01

    ZnO thin films grown on Si(1 1 1) substrates by using atomic layer deposition (ALD) were annealed at the temperatures ranging from 300 to 500 deg. C. The X-ray diffraction (XRD) results show that the annealed ZnO thin films are highly (0 0 2)-oriented, indicating a well ordered microstructure. The film surface examined by the atomic force microscopy (AFM), however, indicated that the roughness increases with increasing annealing temperature. The photoluminescence (PL) spectrum showed that the intensity of UV emission was strongest for films annealed at 500 deg. C. The mechanical properties of the resultant ZnO thin films investigated by nanoindentation reveal that the hardness decreases from 9.2 GPa to 7.2 GPa for films annealed at 300 deg. C and 500 deg. C, respectively. On the other hand, the Young's modulus for the former is 168.6 GPa as compared to a value of 139.5 GPa for the latter. Moreover, the relationship between the hardness and film grain size appear to follow closely with the Hall-Petch equation.

  17. The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

    KAUST Repository

    Venkatesh, S.

    2016-03-24

    We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaronpercolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

  18. The magnetic ordering in high magnetoresistance Mn-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Venkatesh, S.; Baras, A.; Roqan, I. S., E-mail: Iman.roqan@kaust.edu.sa [Physical Sciences and Engineering Division, King Abdullah University of Science and Technology (KAUST), Thuwal 23955-6900 (Saudi Arabia); Lee, J.-S. [Stanford Synchrotron Radiation Lightsource, SLAC National Accelerator Laboratory, Menlo Park, California 94025 (United States)

    2016-03-15

    We studied the nature of magnetic ordering in Mn-doped ZnO thin films that exhibited ferromagnetism at 300 K and superparamagnetism at 5 K. We directly inter-related the magnetisation and magnetoresistance by invoking the polaron percolation theory and variable range of hopping conduction below the metal-to-insulator transition. By obtaining a qualitative agreement between these two models, we attribute the ferromagnetism to the s-d exchange-induced spin splitting that was indicated by large positive magnetoresistance (∼40 %). Low temperature superparamagnetism was attributed to the localization of carriers and non-interacting polaron clusters. This analysis can assist in understanding the presence or absence of ferromagnetism in doped/un-doped ZnO.

  19. Improving photoelectrochemical performance on quantum dots co-sensitized TiO_2 nanotube arrays using ZnO energy barrier by atomic layer deposition

    International Nuclear Information System (INIS)

    Zeng, Min; Zeng, Xi; Peng, Xiange; Zhu, Zhuo; Liao, Jianjun; Liu, Kai; Wang, Guizhen; Lin, Shiwei

    2016-01-01

    Graphical abstract: - Highlights: • The length of TNTAs has a balance between the charge recombination and the QDs loading. • The introduction of ZnO interlayer by ALD could improve the QDs absorption. • The optimal thickness of ZnO interlayer is 1.5 nm prepared by 10 cycles ALD. - Abstract: PbS and CdS quantum dots (QDs) have been deposited onto TiO_2 nanotube arrays (TNTAs) in turn via a sonication-assisted successive ionic layer adsorption and reaction method. This method could uniformly decorate TNTAs with QDs, avoiding QDs aggregation at the mouth of TiO_2 nanotube. The loading amounts of QDs on TNTAs could be controlled by adjusting the TNTAs length. Under one sun illumination, the QDs co-sensitized TNTAs (TNTAs/QDs) with the length of about 2.4 μm displayed the highest photocurrent of 4.32 mA cm"−"2, which is 27 times higher than that of the bare TNTAs. Introduction of a thin ZnO energy barrier by atomic layer deposition (ALD) between the TNTAs and QDs can further improve the photocurrent of TNTAs/QDs. And the TNTAs/QDs with 10 ALD cycles of ZnO interlayer exhibits the highest photocurrent of 5.24 mA cm"−"2 and best photoconversion efficiency of 4.9%, a more than 20% enhancement over the bare TNTAs/QDs. Such enhanced photoelectrochemical performance may be ascribed to the increased amounts of QDs on the TNTAs due to the introduction of ZnO interlayer. The benefits of ALD layers play a crucial role in development and optimization of high-performance photoelectrodes in the near future.

  20. Tragacanth gum biopolymer as reducing and stabilizing agent in biosonosynthesis of urchin-like ZnO nanorod arrays: A low cytotoxic photocatalyst with antibacterial and antifungal properties.

    Science.gov (United States)

    Ghayempour, Soraya; Montazer, Majid; Mahmoudi Rad, Mahnaz

    2016-01-20

    Tragacanth, a natural gum, has been used for centuries as emulsifier, thickener, stabilizer and binder in various fields such as food, medical and cosmetic industries. In this study, Tragacanth gum was used as a clean and natural reducing and stabilizing agent for preparation of urchin-like ZnO nanorod arrays at low-temperature using ultrasonic irradiation. The morphology and structure of urchin-like ZnO nanorod arrays was investigated by XRD, FESEM images, EDX, UV-vis and FT-IR spectroscopy. The hexagonal zinc oxide nanorods were synthesized with the average diameter of 55-80 nm and length of 240 nm. The peak appeared in 447 cm(-1) in FTIR spectra and the peak around 362.3 nm in UV-vis spectra of ZnO nanorods confirmed the successful synthesis of ZnO nanorods. The urchin-like ZnO nanorod arrays indicated a good photocatalytic activity through degradation of methylene blue with 92.2% efficiency and rate constant of 0.0027 min(-1) at 120 min. Finally, the synthesized urchin-like ZnO nanorod arrays indicated 100% antibacterial activity against S. aureus and E. coli and 93% antifungal activity against C. albicans with a low cytotoxicity. Copyright © 2015 Elsevier Ltd. All rights reserved.

  1. Properties of fluorine and tin co-doped ZnO thin films deposited by sol–gel method

    International Nuclear Information System (INIS)

    Pan, Zhanchang; Zhang, Pengwei; Tian, Xinlong; Cheng, Guo; Xie, Yinghao; Zhang, Huangchu; Zeng, Xiangfu; Xiao, Chumin; Hu, Guanghui; Wei, Zhigang

    2013-01-01

    Highlights: •F and Sn co-doped ZnO thin films were synthesized by sol–gel method. •The effects of different F doping concentrations were investigated. •The co-doped nanocrystals exhibit good crystal quality. •The origin of the photoluminescence emissions was discussed. •The films showed high transmittance and low resistivity. -- Abstract: Highly transparent and conducting fluorine (F) and tin (Sn) co-doped ZnO (FTZO) thin films were deposited on glass substrates by the sol–gel processing. The structure and morphology of the films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and high resolution transmission electron microscopy (HRTEM) with various F doping concentrations. SEM images showed that the hexagonal ZnO crystals were well-arranged on the glass substrates and the HRTEM images indicated that the individual nanocrystals are highly oriented and exhibited a perfect lattice structure. Owing to its high carrier concentration and mobility, as well as good crystal quality, a minimum resistivity of 1 × 10 −3 Ω cm was obtained from the FTZO thin film with 3% F doping, and the average optical transmittance in the entire visible wavelength region was higher than 90%. The X-ray photoelectron spectroscopy (XPS) study confirmed the substitution of Zn 2+ by Sn ions and Room temperature photoluminescence (PL) observed for pure and FTZO thin films suggested the films exhibit a good crystallinity with a very low defect concentration

  2. Microwave-assisted low temperature fabrication of ZnO thin film electrodes for solar energy harvesting

    Energy Technology Data Exchange (ETDEWEB)

    Nirmal Peiris, T.A.; Sagu, Jagdeep S.; Hazim Yusof, Y.; Upul Wijayantha, K.G., E-mail: U.Wijayantha@lboro.ac.uk

    2015-09-01

    Metallic Zn thin films were electrodeposited on fluorine-doped tin oxide (FTO) glass substrates and oxidized under air by conventional radiant and microwave post-annealing methods to obtain ZnO thin film electrodes. The temperature of each post-annealing method was varied systematically and the photoelectrochemical (PEC) performance of electrodes was evaluated. The best photocurrent density achieved by the conventional radiant annealing method at 425 °C for 15 min was 93 μA cm{sup −2} at 1.23 V vs. NHE and the electrode showed an incident photon-to-electron conversion efficiency (IPCE) of 28.2%. X-ray diffractogram of this electrode showed that the oxidation of Zn to ZnO was not completed during the radiant annealing process as evident by the presence of metallic Zn in the electrode. For the electrode oxidized from Zn to ZnO under microwave irradiation, a photocurrent of 130 μA cm{sup −2} at 1.23 V vs. NHE and IPCE of 35.6% was observed after annealing for just 3 min, during which the temperature reached 250 °C. The photocurrent was 40% higher for the microwave annealed sample; this increase was attributed to higher surface area by preserving the nanostructure, confirmed by SEM surface topographical analysis, and better conversion yields to crystalline ZnO. Overall, it was demonstrated that oxidation of Zn to ZnO can be accomplished by microwave annealing five times faster than that of conventional annealing, thus resulting in a ~ 75% power saving. This study shows that microwave processing of materials offers significant economic and performance advantages for industrial scale up. - Highlights: • Conversion of Zn to ZnO by microwave and radiant annealing was conducted. • Microwave conversion was 5 times faster compared to radiant annealing. • Photoelectrochemical performance of microwave annealed ZnO was 40% higher. • Microwave annealing results in a 75% energy saving.

  3. Facing-target sputtering deposition of ZnO films with Pt ultra-thin layers for gas-phase photocatalytic application

    International Nuclear Information System (INIS)

    Zhang Zhonghai; Hossain, Md. Faruk.; Arakawa, Takuya; Takahashi, Takakazu

    2010-01-01

    In this paper, various zinc oxide (ZnO) films are deposited by a versatile and effective dc-reactive facing-target sputtering method. The ratios of Ar to O 2 in the mixture gas are varied from 8:2 to 6:4 at a fixed sputtering pressure of 1.0 Pa. X-ray diffraction, spectrophotometer and scanning electron microscope are used to study the crystal structure, optical property and surface morphology of the as-deposited films. The Pt ultra-thin layer, ∼2 nm thick, is deposited on the surface of ZnO film by dc diode sputtering with a mesh mask controlling the coated area. The photocatalytic activity of ZnO films and Pt-ZnO films is evaluated by decomposition of methanol under UV-vis light irradiation. The variation of photocatalytic activity depends on the ratios of Ar to O 2 , which is mainly attributed to the different grain size and carrier mobility. Though the pure ZnO film normally shows a low gas-phase photocatalytic activity, its activity is significantly enhanced by depositing Pt ultra-thin layer.

  4. Visible and UV photo-detection in ZnO nanostructured thin films via simple tuning of solution method.

    Science.gov (United States)

    Khokhra, Richa; Bharti, Bandna; Lee, Heung-No; Kumar, Rajesh

    2017-11-08

    This study demonstrates significant visible light photo-detection capability of pristine ZnO nanostructure thin films possessing substantially high percentage of oxygen vacancies [Formula: see text] and zinc interstitials [Formula: see text], introduced by simple tuning of economical solution method. The demonstrated visible light photo-detection capability, in addition to the inherent UV light detection ability of ZnO, shows great dependency of [Formula: see text] and [Formula: see text] with the nanostructure morphology. The dependency was evaluated by analyzing the presence/percentage of [Formula: see text] and [Formula: see text] using photoluminescence (PL) and X-ray photoelectron spectroscopy (XPS) measurements. Morphologies of ZnO viz. nanoparticles (NPs), nanosheets (NSs) and nanoflowers (NFs), as a result of tuning of synthesis method contended different concentrations of defects, demonstrated different photo-detection capabilities in the form of a thin film photodetector. The photo-detection capability was investigated under different light excitations (UV; 380~420 nm, white ; λ > 420 nm and green; 490~570 nm). The as fabricated NSs photodetector possessing comparatively intermediate percentage of [Formula: see text] ~ 47.7% and [Formula: see text] ~ 13.8% exhibited superior performance than that of NPs and NFs photodetectors, and ever reported photodetectors fabricated by using pristine ZnO nanostructures in thin film architecture. The adopted low cost and simplest approach makes the pristine ZnO-NSs applicable for wide-wavelength applications in optoelectronic devices.

  5. Graphene-Tapered ZnO Nanorods Array as a Flexible Antireflection Layer

    Directory of Open Access Journals (Sweden)

    Taeseup Song

    2015-01-01

    Full Text Available Flexible solar cells have drawn a great deal of attention due to their various advantages including deformable and wearable characteristics. In the solar cells, the antireflection layer plays an important role in the improvement in the conversion efficiency by increasing the light transmission and suppressing the Fresnel refraction. For the successful implantation of the antireflection layer into the flexible solar cells, the flexible mechanical property of the antireflection layer is also necessary. However, the study on flexible antireflection layer for the flexible solar cells or optoelectronics is still lacking. In this study, we report the graphene-tapered ZnO nanorods array as a flexible antireflection layer for the application in flexible solar cells. Flexible two-dimensional graphene sheet and the tapered morphology of ZnO nanorods enable conformal coverage on the flexible substrate with curved surface and significant improvements in antireflection properties, respectively.

  6. Highly transparent and conductive Sn/F and Al co-doped ZnO thin films prepared by sol–gel method

    International Nuclear Information System (INIS)

    Pan, Zhanchang; Luo, Junming; Tian, Xinlong; Wu, Shoukun; Chen, Chun; Deng, Jianfeng; Xiao, Chumin; Hu, Guanghui; Wei, Zhigang

    2014-01-01

    Highlights: • F/Sn and Al co-doped ZnO thin films were synthesized by sol–gel method. • The co-doped nanocrystals exhibit good crystal quality. • The origin of the photoluminescence emissions was discussed. • The films showed high transmittance and low resistivity. -- Abstract: Al doped ZnO, Al–Sn co-doped ZnO and Al–F co-doped ZnO nanocrystals were successfully synthesized onto glass substrates by the sol–gel method. The structure and morphology of the films are characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and high resolution transmission electron microscopy (HRTEM). The results indicated that all the films were polycrystalline with a hexagonal wurtzite structure and exhibited a c-axis preferred orientation. The electrical and optical properties were also investigated by 4-point probe device and Uv–vis spectroscopy, room temperature photoluminescence (PL) and Raman spectrum (Raman), respectively. The PL and Raman results suggested that the co-doped films with a very low defect concentration and exhibit a better crystallinity than AZO thin films. The XPS study confirmed the incorporation of Al, Sn and F ions in the ZnO lattice

  7. Template-controlled piezoactivity of ZnO thin films grown via a bioinspired approach

    Directory of Open Access Journals (Sweden)

    Nina J. Blumenstein

    2017-01-01

    Full Text Available Biomaterials are used as model systems for the deposition of functional inorganic materials under mild reaction conditions where organic templates direct the deposition process. In this study, this principle was adapted for the formation of piezoelectric ZnO thin films. The influence of two different organic templates (namely, a carboxylate-terminated self-assembled monolayer and a sulfonate-terminated polyelectrolyte multilayer on the deposition and therefore on the piezoelectric performance was investigated. While the low negative charge of the COOH-SAM is not able to support oriented attachment of the particles, the strongly negatively charged sulfonated polyelectrolyte leads to texturing of the ZnO film. This texture enables a piezoelectric performance of the material which was measured by piezoresponse force microscopy. This study shows that it is possible to tune the piezoelectric properties of ZnO by applying templates with different functionalities.

  8. Fabrication of ZnO Nanowires Arrays by Anodization and High-Vacuum Die Casting Technique, and Their Piezoelectric Properties

    Directory of Open Access Journals (Sweden)

    Chin-Guo Kuo

    2016-03-01

    Full Text Available In this investigation, anodic aluminum oxide (AAO with arrayed and regularly arranged nanopores is used as a template in the high-vacuum die casting of molten zinc metal (Zn into the nanopores. The proposed technique yields arrayed Zn nanowires with an aspect ratio of over 600. After annealing, arrayed zinc oxide (ZnO nanowires are obtained. Varying the anodizing time yields AAO templates with thicknesses of approximately 50 μm, 60 μm, and 70 μm that can be used in the fabrication of nanowires of three lengths with high aspect ratios. Experimental results reveal that a longer nanowire generates a greater measured piezoelectric current. The ZnO nanowires that are fabricated using an alumina template are anodized for 7 h and produce higher piezoelectric current of up to 69 pA.

  9. Electrical properties of solution-deposited ZnO thin-film transistors by low-temperature annealing.

    Science.gov (United States)

    Lim, Chul; Oh, Ji Young; Koo, Jae Bon; Park, Chan Woo; Jung, Soon-Won; Na, Bock Soon; Chu, Hye Yong

    2014-11-01

    Flexible oxide thin-film transistors (Oxide-TFTs) have emerged as next generation transistors because of their applicability in electronic device. In particular, the major driving force behind solution-processed zinc oxide film research is its prospective use in printing for electronics. A low-temperature process to improve the performance of solution-processed n-channel ZnO thin-film transistors (TFTs) fabricated via spin-coating and inkjet-printing is introduced here. ZnO nanoparticles were synthesized using a facile sonochemical method that was slightly modified based on a previously reported method. The influence of the annealing atmosphere on both nanoparticle-based TFT devices fabricated via spin-coating and those created via inkjet printing was investigated. For the inkjet-printed TFTs, the characteristics were improved significantly at an annealing temperature of 150 degrees C. The field effect mobility, V(th), and the on/off current ratios were 3.03 cm2/Vs, -3.3 V, and 10(4), respectively. These results indicate that annealing at 150 degrees C 1 h is sufficient to obtain a mobility (μ(sat)) as high as 3.03 cm2/Vs. Also, the active layer of the solution-based ZnO nanoparticles allowed the production of high-performance TFTs for low-cost, large-area electronics and flexible devices.

  10. Realizing luminescent downshifting in ZnO thin films by Ce doping with enhancement of photocatalytic activity

    Science.gov (United States)

    Narayanan, Nripasree; Deepak, N. K.

    2018-04-01

    ZnO thin films doped with Ce at different concentration were deposited on glass substrates by spray pyrolysis technique. XRD analysis revealed the phase purity and polycrystalline nature of the films with hexagonal wurtzite geometry and the composition analysis confirmed the incorporation of Ce in the ZnO lattice in the case of doped films. Crystalline quality and optical transmittance diminished while electrical conductivity enhanced with Ce doping. Ce doping resulted in a red-shift of optical energy gap due to the downshift of the conduction band minimum after merging with Ce related impurity bands formed below the conduction band in the forbidden gap. In the room temperature photoluminescence spectra, UV emission intensity of the doped films decreased while the intensity of the visible emission band increased drastically implying the degradation in crystallinity as well as the incorporation of defect levels capable of luminescence downshifting. Ce doping showed improvement in photocatalytic efficiency by effectively trapping the free carriers and then transferring for dye degradation. Thus Ce doped ZnO thin films are capable of acting as luminescent downshifters as well as efficient photocatalysts.

  11. The electrical, elemental, optical, and surface properties of Si-doped ZnO thin films prepared by thermionic vacuum arc

    Science.gov (United States)

    Mohammadigharehbagh, Reza; Özen, Soner; Yudar, Hafizittin Hakan; Pat, Suat; Korkmaz, Şadan

    2017-09-01

    The purpose of this work is to study the properties of Si-doped ZnO (SZO) thin films, which were prepared using the non-reactive thermionic vacuum arc technique. The analysis of the elemental, optical, and surface properties of ZnO:Si thin films was carried out using energy dispersive x-ray spectroscopy, UV-VIS spectrophotometry, atomic force microscopy, and scanning electron microscopy, respectively. The current-voltage measurement was employed in order to study the electrical properties of the films. The effect of Si doping on the physical properties of ZnO films was investigated. The film thicknesses were measured as 55 and 35 nm for glass and PET substrates, respectively. It was clearly observed from the x-ray diffraction results that the Si and ZnO peaks were present in the coated SZO films for all samples. The morphological studies showed that the deposited surfaces are homogenous, dense, and have a uniform surface, with the existence of some cracks only on the glass substrate. The elemental composition has confirmed the existence of Zn, Si, and O elements within the prepared films. Using a UV-VIS spectrophotometer, the optical parameters such as transmittance, absorbance, refractive index, and reflectance were calculated. It should be noted that the transparency and refractive indices obtained from the measurements decrease with increasing Si concentration. The obtained optical bandgap values using transmittance spectra were determined to be 3.74 and 3.84 eV for the glass and PET substrates, respectively. An increase in the bandgap results demonstrates that the Si doping concentration is comparable to the pure ZnO thin films. The current versus voltage curves revealed the ohmic nature of the films. Subsequently, the development and fabrication of excellent transparent conducting electrodes enabled the appropriate use of Si-doped ZnO thin films.

  12. Development of transparent conductive indium and fluorine co-doped ZnO thin films: Effect of F concentration and post-annealing temperature

    Energy Technology Data Exchange (ETDEWEB)

    Hadri, A. [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco); Taibi, M. [University of Mohammed V, LPCMIN, Ecole Normale Superieure, Rabat (Morocco); Loghmarti, M.; Nassiri, C.; Slimani Tlemçani, T. [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco); Mzerd, A., E-mail: mzerd@yahoo.fr [University Mohammed V, Faculty of Sciences, Physics Department, LPM, B.P. 1014, Rabat (Morocco)

    2016-02-29

    In the present work ZnO, In doped ZnO and In-F co-doped ZnO (IFZO) films were synthesized on heated glass substrates (350 °C) by the chemical spray technique. The effect of fluorine concentration on the structural, morphological, optical and electrical properties was studied. It was observed from X-ray diffraction (XRD) that the films have a polycrystalline structure and the intensity of the peaks depend on the doping and co-doping concentration. No diffraction peak related to dopants in XRD patterns along with shift in peaks angles to ZnO proved that In and F ions were doped into ZnO thin films. The Raman spectra confirm the hexagonal structure of the as-deposited films, and demonstrated an enhancement of the surface phonon mode of doped and co-doped films as compared to undoped films. The as-deposited films showed an average transmittance above 70%, in the wavelength range of 400–800 nm. A minimum electrical resistivity, in the order of 5.2 × 10{sup −} {sup 2} Ω cm was obtained for the IFZO thin film with 5 at.% F doping. Moreover, the electrical properties of doped and co-doped films were enhanced after post-deposition annealing. It was found that post-annealed thin films at 350 °C showed a decrease of one order of magnitude of the resistivity values. Such a transparent and conducting thin film can be suitable for optical and electrical applications owing to their low resistivity combined with high transmittance in the visible range. - Highlights: • Conductive transparent ZnO, IZO, IFZO thin films were deposited by spray pyrolysis. • Doping and co-doping affect morphology and optoelectrical properties. • As deposited film with high fluorine content exhibited high carrier mobility (55 cm{sup 2} V{sup −} {sup 1} s{sup −} {sup 1}). • Correlation between intrinsic defects and carrier mobility was observed. • Post-annealing in Ar atmosphere improves conductivity.

  13. Effect of stress, strain and optical properties in vacuum and normal annealed ZnO thin films using RF magnetron sputtering

    Science.gov (United States)

    Kumar, B. Santhosh; Purvaja, K.; Harinee, N.; Venkateswaran, C.

    2018-05-01

    Zinc oxide thin films have been deposited on quartz substrate using RF magnetron sputtering. The deposited films were subjected to different annealing atmosphere at a fixed temperature of 500 °C for 5h. The X-ray diffraction (XRD) patterns reveals the shift in the peak of both normal annealed and vacuum annealed thin films when compared to as-deposited ZnO film. The crystallite size, intrinsic stress and other parameters were calculated from XRD data. The surface morphology of the obtained films were studied using Atomic force microscopy (AFM). From Uv-Visible spectroscopy, the peak at 374 nm of all the films is characteristics of ZnO. The structural, thermal stability and optical properties of the annealed ZnO films are discussed in detail.

  14. Optical and electrical properties of transparent conducting B-doped ZnO thin films prepared by various deposition methods

    International Nuclear Information System (INIS)

    Nomoto, Jun-ichi; Miyata, Toshihiro; Minami, Tadatsugu

    2011-01-01

    B-doped ZnO (BZO) thin films were prepared with various thicknesses up to about 500 nm on glass substrates at 200 deg. C by dc or rf magnetron sputtering deposition, pulsed laser deposition (PLD), and vacuum arc plasma evaporation (VAPE) methods. Resistivities of 4-6 x 10 -4 Ω cm were obtained in BZO thin films prepared with a B content [B/(B + Zn) atomic ratio] around 1 at. % by PLD and VAPE methods: Hall mobilities above 40 cm 2 /Vs and carrier concentrations on the order of 10 20 cm -3 . All 500-nm-thick-BZO thin films prepared with a resistivity on the order of 10 -3 -10 -4 Ω cm exhibited an averaged transmittance above 80% in the wavelength range of 400-1100 nm. The resistivity in BZO thin films prepared with a thickness below about 500 nm was found to increase over time with exposure to various high humidity environments. In heat-resistance tests, the resistivity stability of BZO thin films was found to be nearly equal to that of Ga-doped ZnO thin films, so these films were judged suitable for use as a transparent electrode for thin-film solar cells.

  15. Improving photoelectrochemical performance on quantum dots co-sensitized TiO{sub 2} nanotube arrays using ZnO energy barrier by atomic layer deposition

    Energy Technology Data Exchange (ETDEWEB)

    Zeng, Min [Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources, College of Materials and Chemical Engineering, Hainan University, Haikou 570228 (China); Zeng, Xi [College of Chemistry and Chemical Engineering, Yunnan Normal University, Kunming, 650500 (China); Peng, Xiange; Zhu, Zhuo; Liao, Jianjun; Liu, Kai; Wang, Guizhen [Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources, College of Materials and Chemical Engineering, Hainan University, Haikou 570228 (China); Lin, Shiwei, E-mail: linsw@hainu.edu.cn [Key Laboratory of Ministry of Education for Advanced Materials in Tropical Island Resources, College of Materials and Chemical Engineering, Hainan University, Haikou 570228 (China)

    2016-12-01

    Graphical abstract: - Highlights: • The length of TNTAs has a balance between the charge recombination and the QDs loading. • The introduction of ZnO interlayer by ALD could improve the QDs absorption. • The optimal thickness of ZnO interlayer is 1.5 nm prepared by 10 cycles ALD. - Abstract: PbS and CdS quantum dots (QDs) have been deposited onto TiO{sub 2} nanotube arrays (TNTAs) in turn via a sonication-assisted successive ionic layer adsorption and reaction method. This method could uniformly decorate TNTAs with QDs, avoiding QDs aggregation at the mouth of TiO{sub 2} nanotube. The loading amounts of QDs on TNTAs could be controlled by adjusting the TNTAs length. Under one sun illumination, the QDs co-sensitized TNTAs (TNTAs/QDs) with the length of about 2.4 μm displayed the highest photocurrent of 4.32 mA cm{sup −2}, which is 27 times higher than that of the bare TNTAs. Introduction of a thin ZnO energy barrier by atomic layer deposition (ALD) between the TNTAs and QDs can further improve the photocurrent of TNTAs/QDs. And the TNTAs/QDs with 10 ALD cycles of ZnO interlayer exhibits the highest photocurrent of 5.24 mA cm{sup −2} and best photoconversion efficiency of 4.9%, a more than 20% enhancement over the bare TNTAs/QDs. Such enhanced photoelectrochemical performance may be ascribed to the increased amounts of QDs on the TNTAs due to the introduction of ZnO interlayer. The benefits of ALD layers play a crucial role in development and optimization of high-performance photoelectrodes in the near future.

  16. Contact Resistance Reduction of ZnO Thin Film Transistors (TFTs) with Saw-Shaped Electrode

    KAUST Repository

    Park, Woojin

    2018-05-15

    We report a saw-shaped electrode architecture ZnO thin film transistor (TFT) for effectively increase channel width. Such a saw-shaped electrode has ~2 times longer contact line at the contact metal/ZnO channel junction. We experimentally observed an enhancement in the output drive current by 50% and reduction in the contact resistance by over 50%, when compared to a typical shaped electrode ZnO TFT consuming the same chip area. This performance enhancement is attributed to extension of channel width. This technique can contribute to device performance enhancement and especially reduction in the contact resistance which is a serious challenge.

  17. Mott-Schottky analysis of thin ZnO films

    International Nuclear Information System (INIS)

    Windisch, Charles F. Jr.; Exarhos, Gregory J.

    2000-01-01

    Thin ZnO films, both native and doped with secondary metal ions, have been prepared by sputter deposition and also by casting from solutions containing a range of precursor salts. The conductivity and infrared reflectivity of these films are subsequently enhanced chemically following treatment in H 2 gas at 400 degree sign C or by cathodic electrochemical treatment in a neutral (pH=7) phosphate buffer solution. While Hall-type measurements usually are used to evaluate the electrical properties of such films, the present study investigated whether a conventional Mott-Schottky analysis could be used to monitor the change in concentration of free carriers in these films before and after chemical and electrochemical reduction. The Mott-Schottky approach would be particularly appropriate for electrochemically modified films since the measurements could be made in the same electrolyte used for the post-deposition electrochemical processing. Results of studies on sputtered pure ZnO films in ferricyanide solution were promising. Mott-Schottky plots were linear and gave free carrier concentrations typical for undoped semiconductors. Film thicknesses estimated from the Mott-Schottky data were also reasonably close to thicknesses calculated from reflectance measurements. Studies on solution-deposited films were less successful. Mott-Schottky plots were nonlinear, apparently due to film porosity. A combination of dc polarization and atomic force microscopy measurements confirmed this conclusion. The results suggest that Mott-Schottky analysis would be suitable for characterizing solution-deposited ZnO films only after extensive modeling was performed to incorporate the effects of film porosity on the characteristics of the space-charge region of the semiconductor. (c) 2000 American Vacuum Society

  18. Tunable light extraction efficiency of GaN light emitting diodes by ZnO nanorod arrays

    International Nuclear Information System (INIS)

    Chao, C H; Lin, W H; Lin, C F; Chen, C H; Changjean, C H

    2009-01-01

    We report the influence of ZnO nanorod arrays (NRAs) on the light extraction efficiency of GaN light emitting diodes (LEDs). Our investigation indicates that the output light intensity of the device exhibits a periodic oscillation as a function of the rod length. The variation of light extraction efficiency is caused by the Fabry–Perot resonance of the film composed of the nanorods. The theoretical analysis shows a good agreement with the measurement results. Our study reveals a method to control the output light extraction efficiency of GaN LEDs via a simple solution-based synthesized ZnO NRAs

  19. Effect of Mg doping in the gas-sensing performance of RF-sputtered ZnO thin films

    Science.gov (United States)

    Vinoth, E.; Gowrishankar, S.; Gopalakrishnan, N.

    2018-06-01

    Thin films of Mg-free and Mg-doped (3, 10 and 20 mol%) ZnO thin films have been deposited on Si (100) substrates by RF magnetron sputtering for gas-sensing application. Preferential orientation along (002) plane with hexagonal wurtzite structure has been observed in X-ray diffraction analysis. The conductivity, resistivity, and mobility of the deposited films have been measured by Hall effect measurement. The bandgap of the films has been calculated from the UV-Vis-NIR spectroscopy. It has been found that the bandgap was increased from 3.35 to 3.91 eV with Mg content in ZnO due to the radiative recombination of excitons. The change in morphology of the grown films has been investigated by scanning electron microscope. Gas-sensing measurements have been conducted for fabricated films. The sensor response, selectivity, and stability measurement were done for the fabricated films. Though better response was found towards ethanol, methanol, and ammonia for MZ2 (Mg at 10 mol%) film and maximum gas response was observed towards ammonia. The selectivity measurement reveals maximum sensitivity about 42% for ammonia. The low response time of 123 s and recovery time of 152 s towards ammonia were observed for MZ2 (Mg at 10 mol%). Stability of the Mg-doped ZnO thin film confirmed by the continuous sensing measurements for 4 months.

  20. 16.1% Efficient Hysteresis-Free Mesostructured Perovskite Solar Cells Based on Synergistically Improved ZnO Nanorod Arrays

    KAUST Repository

    Mahmood, Khalid; Swain, Bhabani Sankar; Amassian, Aram

    2015-01-01

    Significant efficiency improvements are reported in mesoscopic perovskite solar cells based on the development of a low-temperature solution-processed ZnO nanorod (NR) array exhibiting higher NR aspect ratio, enhanced electron density

  1. Fabrication and characterization of well-aligned zinc oxide nanowire arrays and their realizations in Schottky-device applications

    Energy Technology Data Exchange (ETDEWEB)

    Wong, Kin Mun; Grote, Fabian; Sun, Hui; Lei, Yong [Institute of Materials Physics, Center for Nanotechnology, University of Muenster (Germany); Wen, Liaoyong; Fang, Yaoguo [Institute of Nanochemistry and Nanobiology, Shanghai University, Shanghai 201800 (China)

    2011-07-01

    Highly ordered arrays of vertical zinc oxide (ZnO) nanowires (NWs) or nanopores were fabricated in our group by first thermal evaporating a thin film of gold on the ultrathin alumina membrane (UTAM). The UTAM was then utilized as a substrate for the growth of the ordered arrays using a chemical vapour deposition (CVD) process. Alternatively, a modified CVD process was also used to fabricate ultra-long ZnO NWs with the length of the nanowire exceeding 100 micrometres. Subsequently, densely packed arrays of ZnO NWs Schottky diodes were synthesized by transferring the long NWs on a substrate using a dry contact printing method and the electrical contacts were made on the NWs with a photolithographic process. The interesting electrical properties of the ZnO NWs, diodes or other metal oxide NWs such as the field emission, electron transport and piezoelectric properties were characterized by current-voltage or by other appropriate measurements.

  2. Electrospray Deposition of ZnO Thin Films and Its Application to Gas Sensors

    Directory of Open Access Journals (Sweden)

    Wenwang Li

    2018-02-01

    Full Text Available Electrospray is a simple and cost-effective method to fabricate micro-structured thin films. This work investigates the electrospray process of ZnO patterns. The effects of experimental parameters on jet characteristics and electrosprayed patterns are studied. The length of stable jets increases with increasing applied voltage and flow rate, and decreases with increasing nozzle-to-substrate distance, while electrospray angles exhibit an opposite trend with respect to the stable jet lengths. The diameter of electrosprayed particles decreases with increasing applied voltage, and increases with flow rate. Furthermore, an alcohol gas sensor is presented. The ZnAc is calcined into ZnO, which reveals good repeatability and stability of response in target gas. The sensing response, defined as the resistance ratio of R0/Rg, where R0 and Rg are resistance of ZnO in air and alcohol gas, increases with the concentration of alcohol vapors and electrospray deposition time.

  3. Annealing Temperature Dependent Structural and Optical Properties of RF Sputtered ZnO Thin Films.

    Science.gov (United States)

    Sharma, Shashikant; Varma, Tarun; Asokan, K; Periasamy, C; Boolchandani, Dharmendar

    2017-01-01

    This work investigates the effect of annealing temperature on structural and optical properties of ZnO thin films grown over Si 100 and glass substrates using RF sputtering technique. Annealing temperature has been varied from 300 °C to 600 °C in steps of 100, and different microstructural parameters such as grain size, dislocation density, lattice constant, stress and strain have been evaluated. The structural and surface morphological characterization has been done using X-ray Diffraction (XRD) and Scanning Electron Microscope (SEM). XRD analysis reveals that the peak intensity of 002 crystallographic orientation increases with increased annealing temperature. Optical characterization of deposited films have been done using UV-Vis-NIR spectroscopy and photoluminescence spectrometer. An increase in optical bandgap of deposited ZnO thin films with increasing annealing temperature has been observed. The average optical transmittance was found to be more than 85% for all deposited films. Photoluminiscense spectra (PL) suggest that the crystalline quality of deposited film has increased at higher annealing temperature.

  4. Construction of 3D Arrays of Cylindrically Hierarchical Structures with ZnO Nanorods Hydrothermally Synthesized on Optical Fiber Cores

    Directory of Open Access Journals (Sweden)

    Weixuan Jing

    2014-01-01

    Full Text Available With ZnO nanorods hydrothermally synthesized on manually assembled arrays of optical fiber cores, 3D arrays of ZnO nanorod-based cylindrically hierarchical structures with nominal pitch 250 μm or 375 μm were constructed. Based on micrographs of scanning electron microscopy and image processing operators of MATLAB software, the 3D arrays of cylindrically hierarchical structures were quantitatively characterized. The values of the actual diameters, the actual pitches, and the parallelism errors suggest that the process capability of the manual assembling is sufficient and the quality of the 3D arrays of cylindrically hierarchical structures is acceptable. The values of the characteristic parameters such as roughness, skewness, kurtosis, correlation length, and power spectrum density show that the surface morphologies of the cylindrically hierarchical structures not only were affected significantly by Zn2+ concentration of the growth solution but also were anisotropic due to different curvature radii of the optical fiber core at side and front view.

  5. Influence of lithium doping on the structural and electrical characteristics of ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Johny, T. Anto [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Kumar, Viswanathan, E-mail: vkumar10@yahoo.com [Centre for Materials for Electronics Technology (C-MET), (Department of Information Technology, Scientific Society, Ministry of Communication and Information Technology, Govt. of India), Athani - PO, Thrissur, 680 581 Kerala (India); Imai, Hideyuki; Kanno, Isaku [Micro Engineering, Kyoto University, Kyoto 606-8501 (Japan)

    2012-06-30

    Thin films of undoped and lithium-doped Zinc oxide, (Zn{sub 1-x}Li{sub x})O; x = 0, 0.05, 0.10 and 0.20 were prepared by sol-gel method using spin-coating technique on silicon substrates [(111)Pt/Ti/SiO{sub 2}/Si)]. The influence of lithium doping on the structural, electrical and microstructural characteristics have been investigated by means of X-ray diffraction, leakage current, piezoelectric measurements and scanning electron microscopy. The resistivity of the ZnO film is found to increase markedly with low levels (x {<=} 0.05) of lithium doping thereby enhancing their piezoelectric applications. The transverse piezoelectric coefficient, e{sub 31}{sup Low-Asterisk} has been determined for the thin films having the composition (Zn{sub 0.95}Li{sub 0.05})O, to study their suitability for piezoelectric applications. - Highlights: Black-Right-Pointing-Pointer Preferentially c-axis oriented (Zn{sub 1-x}Li{sub x})O films were spin-coated on glass. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films exhibit dense columnar microstructure. Black-Right-Pointing-Pointer Low levels of lithium doping, increases the electrical resistivity of ZnO thin films. Black-Right-Pointing-Pointer (Zn{sub 1-x}Li{sub x})O thin films show high values of transverse piezoelectric coefficient, e{sup Low-Asterisk }{sub 31}.

  6. Roughness-based monitoring of transparency and conductivity in boron-doped ZnO thin films prepared by spray pyrolysis

    International Nuclear Information System (INIS)

    Gaikwad, Rajendra S.; Bhande, Sambhaji S.; Mane, Rajaram S.; Pawar, Bhagwat N.; Gaikwad, Sanjay L.; Han, Sung-Hwan; Joo, Oh-Shim

    2012-01-01

    Graphical abstract: Display Omitted Highlights: ► We report surface roughness dependent transparency and conductivity in ZnO films. ► The surface roughness with respected to boron doping concentrations is studied. ► Boron doped and pristine Zinc oxide thin films have showed ≥95% transmittance. ► Increased carrier concentration of 9.21 × 10 21 cm −3 revealed from Hall measurement. -- Abstract: Sprayed polycrystalline ZnO and boron-doped ZnO thin films composed of spherical grains of 25–32 nm in diameters are used in roughness measurement and further correlated with the transparency and the conductivity characteristics. The surface roughness is increased up to Zn 0.98 B 0.02 O and then declined at higher boron concentrations. The sprayed ZnO films revealed ≥95% transmittance in the visible wavelength range, 1.956 × 10 −4 Ω cm electrical resistivity, 46 cm 2 /V s Hall mobility and 9.21 × 10 21 cm −3 charge carrier concentration. The X-ray photoelectron spectroscopy study has confirmed 0.15 eV binding energy change for Zn 2p 3/2 when 2 at% boron content is mixed without altering electro-optical properties substantially. Finally, using soft modeling importance of these textured ZnO over non-textured films for enhancing the solar cells performance is explored.

  7. Synthesis of highly conductive thin-walled Al-doped ZnO single-crystal microtubes by a solid state method

    Science.gov (United States)

    Hu, Shuopeng; Wang, Yue; Wang, Qiang; Xing, Cheng; Yan, Yinzhou; Jiang, Yijian

    2018-06-01

    ZnO has attracted considerable attention in fundamental studies and practical applications for the past decade due to its outstanding performance in gas sensing, photocatalytic degradation, light harvesting, UV-light emitting/lasing, etc. The large-sized thin-walled ZnO (TW-ZnO) microtube with stable and rich VZn-related acceptors grown by optical vapor supersaturated precipitation (OVSP) is a novel multifunctional optoelectronic material. Unfortunately, the OVSP cannot achieve doping due to the vapor growth process. To obtain doped TW-ZnO microtubes, a solid state method is introduced in this work to achieve thin-walled Al-doping ZnO (TW-ZnO:Al) microtubes with high electrical conductivity. The morphology and microstructures of ZnO:Al microtubes are similar to undoped ones. The Al3+ ions are confirmed to substitute Zn2+ sites and Zn(0/-1) vacancies in the lattice of ZnO by EDS, XRD, Raman and temperature-dependent photoluminescence analyses. The Al dopant acting as a donor level offers massive free electrons to increase the carrier concentrations. The resistivity of the ZnO:Al microtube is reduced down to ∼10-3 Ω·cm, which is one order of magnitude lower than that of the undoped microtube. The present work provides a simple way to achieve doped ZnO tubular components for potential device applications in optoelectronics.

  8. High-dose V+ implantation in ZnO thin film structures

    International Nuclear Information System (INIS)

    Vyatkin, A.F.; Zinenko, V.I.; Agaphonov, Yu.A.; Pustovit, A.N.; Roshchupkin, D.V.; Reuss, F.; Kirchner, C.; Kling, R.; Waag, A.

    2005-01-01

    In the last two decades, diluted magnetic semiconductors have attracted great attention as promising materials for spintronics applications. [K. Sato, H. Katyama-Yoshida, Jpn. J. Phys., Part 2 39 (2000) L555] theoretically predicted that ZnO doped with V, Cr, Fe, Co, and Ni can be ferromagnetic. This has been recently confirmed experimentally for vanadium doped ZnO films which were grown on sapphire substrates, using laser deposition technique [H. Saeki, H.N. Tabata, T. Kawai, Solid State Commun. 120 (2001) 439]. In the present work, high-dose vanadium implantation was used to produce Zn 1-x V x O (x ∼ 0.10) thin film structures (250 nm thick) that had been epitaxially grown on sapphire substrates. Implantation with the dose 2 x 10 16 cm -2 was performed to reach a maximum vanadium concentration of 10 at%. To avoid ZnO film amorphization due to radiation damage accumulation [S.O. Kucheyev, J.S. Williams, C. Jagadish, J. Zou, C. Evans, A.J. Nelson, A.V. Hamza, Phys. Rev. B 67 (2003) 094115], all implants were done at elevated temperatures 300 and 400 deg. C and ion current density 10 μA/cm 2 . X-ray diffraction, SIMS and photoluminescence techniques were exploited to study the implanted samples. No luminescence was observed in the implanted samples after implantation procedures. However, annealing at 800 deg. C for 30 min gave rise to ZnO crystal structure improvement. This implies that healing of implantation induced defects is possible even after heavy-ion bombardment. As a result, the photoluminescence peak at 3.359 eV related to the donorbound exiton was detected

  9. Homogeneous vertical ZnO nanorod arrays with high conductivity on an in situ Gd nanolayer

    KAUST Repository

    Flemban, Tahani H.

    2015-10-30

    We demonstrate a novel, one-step, catalyst-free method for the production of size-controlled vertical highly conductive ZnO nanorod (NR) arrays with highly desirable characteristics by pulsed laser deposition using a Gd-doped ZnO target. Our study shows that an in situ transparent and conductive Gd nanolayer (with a uniform thickness of ∼1 nm) at the interface between a lattice-matched (11-20) a-sapphire substrate and ZnO is formed during the deposition. This nanolayer significantly induces a relaxation mechanism that controls the dislocation distribution along the growth direction; which consequently improves the formation of homogeneous vertically aligned ZnO NRs. We demonstrate that both the lattice orientation of the substrate and the Gd characteristics are important in enhancing the NR synthesis, and we report precise control of the NR density by changing the oxygen partial pressure. We show that these NRs possess high optical and electrical quality, with a mobility of 177 cm2 (V s)-1, which is comparable to the best-reported mobility of ZnO NRs. Therefore, this new and simple method has significant potential for improving the performance of materials used in a wide range of electronic and optoelectronic applications.

  10. OLED-based biosensing platform with ZnO nanoparticles for enzyme immobilization

    Science.gov (United States)

    Cai, Yuankun; Shinar, Ruth; Shinar, Joseph

    2009-08-01

    Organic light-emitting diode (OLED)-based sensing platforms are attractive for photoluminescence (PL)-based monitoring of a variety of analytes. Among the promising OLED attributes for sensing applications is the thin and flexible size and design of the OLED pixel array that is used for PL excitation. To generate a compact, fielddeployable sensor, other major sensor components, such as the sensing probe and the photodetector, in addition to the thin excitation source, should be compact. To this end, the OLED-based sensing platform was tested with composite thin biosensing films, where oxidase enzymes were immobilized on ZnO nanoparticles, rather than dissolved in solution, to generate a more compact device. The analytes tested, glucose, cholesterol, and lactate, were monitored by following their oxidation reactions in the presence of oxygen and their respective oxidase enzymes. During such reactions, oxygen is consumed and its residual concentration, which is determined by the initial concentration of the above-mentioned analytes, is monitored. The sensors utilized the oxygen-sensitive dye Pt octaethylporphyrin, embedded in polystyrene. The enzymes were sandwiched between two thin ZnO layers, an approach that was found to improve the stability of the sensing probes.

  11. Giant coercivity in ferromagnetic Co doped ZnO single crystal thin film

    International Nuclear Information System (INIS)

    Loukya, B.; Negi, D.S.; Dileep, K.; Kumar, N.; Ghatak, Jay; Datta, R.

    2013-01-01

    The origin of ferromagnetism in ZnO doped with transition metal impurities has been discussed extensively and appeared to be a highly controversial and challenging topic in today's solid state physics. Magnetism observed in this system is generally weak and soft. We have grown Co:ZnO up to 30 at% Co in single crystal thin film form on c-plane sapphire. A composition dependent coercivity is observed in this system which reaches peak value at 25 at% Co, the values are 860 Oe and 1149 Oe with applied field along parallel and perpendicular to the film substrate interface respectively. This giant coercivity might pave the way to exploit this material as a magnetic semiconductor with novel logic functionalities. The findings are explained based on defect band itinerant ferromagnetism and its partial interaction with localized d electrons of Co through charge transfer. Besides large coercivity, an increase in the band gap with Co concentration has also been observed along with blue emission peak with long tail confirming the formation of extended point defect levels in the host lattice band gap. - Highlights: • Co doped ZnO ferromagnetic single crystal thin film. • Giant coercivity in Co:ZnO thin film which may help to turn this material into application. • Cathodoluminescence (CL) data showing increase in band gap with Co concentrations. • A theoretical proposal is made to explain the observed giant coercivity

  12. Synthesis and characterization of DC magnetron sputtered ZnO thin films under high working pressures

    International Nuclear Information System (INIS)

    Hezam, M.; Tabet, N.; Mekki, A.

    2010-01-01

    ZnO thin films were deposited on glass substrates using direct current (dc) magnetron sputtering under high working pressures. A pure zinc target was used, and sputtering was carried out in an oxygen atmosphere. The working pressure was varied between 50 and 800 mTorr. XRD characterization showed that for a window of working pressures between 300 and 500 mTorr, the deposited films were polycrystalline, with strong preferential orientation of grains along the c-axis. The film deposited at 400 mTorr had the highest (002) peak with the largest estimated grain size. Outside this window, the crystallinity and c-orientation of grains are lost. The microstructure of the films was investigated by Atomic Force microscopy (AFM). Optical transparency of the films was about 85%. The films produced were highly resistive, which might provide new alternatives for the synthesis of ZnO thin films aimed for SAW devices.

  13. Characterization of nanostructured ZnO thin films deposited through vacuum evaporation

    Directory of Open Access Journals (Sweden)

    Jose Alberto Alvarado

    2015-04-01

    Full Text Available This work presents a novel technique to deposit ZnO thin films through a metal vacuum evaporation technique using colloidal nanoparticles (average size of 30 nm, which were synthesized by our research group, as source. These thin films had a thickness between 45 and 123 nm as measured by profilometry. XRD patterns of the deposited thin films were obtained. According to the HRSEM micrographs worm-shaped nanostructures are observed in samples annealed at 600 °C and this characteristic disappears as the annealing temperature increases. The films obtained were annealed from 25 to 1000 °C, showing a gradual increase in transmittance spectra up to 85%. The optical band gaps obtained for these films are about 3.22 eV. The PL measurement shows an emission in the red and in the violet region and there is a correlation with the annealing process.

  14. Growth of ZnO nanowire arrays directly onto Si via substrate topographical adjustments using both wet chemical and dry etching methods

    Energy Technology Data Exchange (ETDEWEB)

    Smith, Nathan A., E-mail: 523615@swansea.ac.uk [Centre for Nanohealth, Department of Physics, College of Science, University of Swansea, Singleton Park SA2 8PP United Kingdom (United Kingdom); Evans, Jon E.; Jones, Daniel R. [Multidisciplinary Nanotechnology Centre, College of Engineering, University of Swansea, Singleton Park, SA2 8PP United Kingdom (United Kingdom); Lord, Alex M. [Centre for Nanohealth, College of Engineering, University of Swansea, Singleton Park, SA2 8PP United Kingdom (United Kingdom); Wilks, S.P. [Centre for Nanohealth, Department of Physics, College of Science, University of Swansea, Singleton Park SA2 8PP United Kingdom (United Kingdom)

    2015-03-15

    Highlights: • Arrays of catalyst-free ZnO NWs have been grown by CVD without seed layers on Si. • Si surface topography was altered by substrate etching, resulting in NW growth. • XPS analysis shows growth is related to topography and not surface contamination. • Using e-beam lithography with etching, selective nanowire growth is demonstrated. • Electrical measurements on the arrays show improved conduction through the Si. - Abstract: Arrays of CVD catalyst-free ZnO nanowires have been successfully grown without the use of seed layers, using both wet chemical and dry plasma etching methods to alter surface topography. XPS analysis indicates that the NW growth cannot be attributed to a substrate surface chemistry and is therefore directly related to the substrate topography. These nanowires demonstrate structural and optical properties typical of CVD ZnO nanowires. Moreover, the NW arrays exhibit a degree of vertical alignment of less than 20° from the substrate normal. Electrical measurements suggest an improved conduction path through the substrate over seed layer grown nanowires. Furthermore, the etching technique was combined with e-beam lithography to produce high resolution selective area nanowire growth. The ability to pattern uniform nanowires using mature dry etch technology coupled with the increased charge transport through the substrate demonstrates the potential of this technique in the vertical integration of nanowire arrays.

  15. Structural, electrical, and dielectric properties of Cr doped ZnO thin films: Role of Cr concentration

    Energy Technology Data Exchange (ETDEWEB)

    Gürbüz, Osman, E-mail: osgurbuz@yildiz.edu.tr; Okutan, Mustafa

    2016-11-30

    Highlights: • Magnetic material of Cr and semiconductor material of ZnO were grown by the magnetron sputtering co-sputter technique. • Perfect single crystalline structures were grown. • DC and AC conductivity with dielectric properties as a function of frequency (f = 5Hz–13 MHz) at room temperature were measured and compared. • Cr doped ZnO can be used in microwave, sensor and optoelectronic devices as the electrical conductivity increases while dielectric constant decreases with the Cr content. - Abstract: An undoped zinc oxide (ZnO) and different concentrations of chromium (Cr) doped ZnO Cr{sub x}ZnO{sub 1−x} (x = 3.74, 5.67, 8.10, 11.88, and 15.96) thin films were prepared using a magnetron sputtering technique at room temperature. These films were characterized by X-ray diffraction (XRD), High resolution scanning electron microscope (HR-SEM), and Energy dispersive X-ray spectrometry (EDS). XRD patterns of all the films showed that the films possess crystalline structure with preferred orientation along the (100) crystal plane. The average crystallite size obtained was found to be between 95 and 83 nm which was beneficial in high intensity recording peak. Both crystal quality and crystallite sizes decrease with increasing Cr concentration. The crystal and grain sizes of the all film were investigated using SEM analysis. The surface morphology that is grain size changes with increase Cr concentration and small grains coalesce together to form larger grains for the Cr{sub 11.88}ZnO and Cr{sub 15.96}ZnO samples. Impedance spectroscopy studies were carried out in the frequencies ranging from 5 Hz to 13 MHz at room temperature. The undoped ZnO film had the highest dielectric value, while dielectric values of other films decreased as doping concentrations increased. Besides, the dielectric constants decreased whereas the loss tangents increased with increasing Cr content. This was considered to be related to the reduction of grain size as Cr content in ZnO

  16. Optical and electrical properties of transparent conducting B-doped ZnO thin films prepared by various deposition methods

    Energy Technology Data Exchange (ETDEWEB)

    Nomoto, Jun-ichi; Miyata, Toshihiro; Minami, Tadatsugu [Optoelectronic Device System R and D Center, Kanazawa Institute of Technology, 7-1 Ohgigaoka, Nonoichi, Ishikawa 921-8501 (Japan)

    2011-07-15

    B-doped ZnO (BZO) thin films were prepared with various thicknesses up to about 500 nm on glass substrates at 200 deg. C by dc or rf magnetron sputtering deposition, pulsed laser deposition (PLD), and vacuum arc plasma evaporation (VAPE) methods. Resistivities of 4-6 x 10{sup -4}{Omega} cm were obtained in BZO thin films prepared with a B content [B/(B + Zn) atomic ratio] around 1 at. % by PLD and VAPE methods: Hall mobilities above 40 cm{sup 2}/Vs and carrier concentrations on the order of 10{sup 20} cm{sup -3}. All 500-nm-thick-BZO thin films prepared with a resistivity on the order of 10{sup -3}-10{sup -4}{Omega} cm exhibited an averaged transmittance above 80% in the wavelength range of 400-1100 nm. The resistivity in BZO thin films prepared with a thickness below about 500 nm was found to increase over time with exposure to various high humidity environments. In heat-resistance tests, the resistivity stability of BZO thin films was found to be nearly equal to that of Ga-doped ZnO thin films, so these films were judged suitable for use as a transparent electrode for thin-film solar cells.

  17. Ag nanoparticles-decorated ZnO nanorod array on a mechanical flexible substrate with enhanced optical and antimicrobial properties

    OpenAIRE

    Chen, Yi; Tse, Wai Hei; Chen, Longyan; Zhang, Jin

    2015-01-01

    Heteronanostructured zinc oxide nanorod (ZnO NR) array are vertically grown on polydimethylsiloxane (PDMS) through a hydrothermal method followed by an in situ deposition of silver nanoparticles (Ag NPs) through a photoreduction process. The Ag-ZnO heterostructured nanorods on PDMS are measured with an average diameter of 160?nm and an average length of 2??m. ZnO NRs measured by high-resolution transmission electron microscope (HRTEM) shows highly crystalline with a lattice fringe of 0.255?nm...

  18. Hydrophobic ZnO nanostructured thin films on glass substrate by simple successive ionic layer absorption and reaction (SILAR) method

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, P. Suresh; Raj, A. Dhayal [Thin Film and Nanomaterials Laboratory, Department of Physics, Bharathiar University, Coimbatore-641046 (India); Mangalaraj, D., E-mail: dmraj800@yahoo.co [Department of Nanoscience and Technology, Bharathiar University, Coimbatore-641046 (India); Nataraj, D. [Thin Film and Nanomaterials Laboratory, Department of Physics, Bharathiar University, Coimbatore-641046 (India)

    2010-10-01

    In the present work, ZnO nanostructured thin films were grown on glass substrates by a simple successive ionic layer absorption and reaction method (SILAR) process at relatively low temperature for its self cleaning application. X-ray diffraction, scanning electron microscopy and Photoluminescence (PL) spectra were used to characterize the prepared ZnO nanostructured film. XRD pattern clearly reviles that the grown ZnO nanostructure film reflect (002) orientation with c-direction. SEM image clearly shows the surface morphology with cluster of spindle and flower-like nanostructured with diameter various around 350 nm. Photoluminescence (PL) spectra of ZnO nanostructures film exhibit a UV emission around 385nm and visible emission in the range around 420-500 nm. Good water repellent behavior were observed for ZnO nanostructured film without any surface modification.

  19. Hydrophobic ZnO nanostructured thin films on glass substrate by simple successive ionic layer absorption and reaction (SILAR) method

    International Nuclear Information System (INIS)

    Kumar, P. Suresh; Raj, A. Dhayal; Mangalaraj, D.; Nataraj, D.

    2010-01-01

    In the present work, ZnO nanostructured thin films were grown on glass substrates by a simple successive ionic layer absorption and reaction method (SILAR) process at relatively low temperature for its self cleaning application. X-ray diffraction, scanning electron microscopy and Photoluminescence (PL) spectra were used to characterize the prepared ZnO nanostructured film. XRD pattern clearly reviles that the grown ZnO nanostructure film reflect (002) orientation with c-direction. SEM image clearly shows the surface morphology with cluster of spindle and flower-like nanostructured with diameter various around 350 nm. Photoluminescence (PL) spectra of ZnO nanostructures film exhibit a UV emission around 385nm and visible emission in the range around 420-500 nm. Good water repellent behavior were observed for ZnO nanostructured film without any surface modification.

  20. Photoelectrochemical water splitting under visible light over anti-photocorrosive In{sub 2}O{sub 3}-coupling ZnO nanorod arrays photoanode

    Energy Technology Data Exchange (ETDEWEB)

    Zhang, Yan, E-mail: zhangyanchem@qdu.edu.cn [Oceanology University of China, College of Chemistry and Chemical Engineering (China); Zhang, Jinqiu [Qingdao University, Faculty of Chemical Science and Engineering (China); Nie, Mengyan [University of Southampton, National Centre for Advanced Tribology at Southampton, School of Engineering Sciences (United Kingdom); Sun, Kai [Qingdao University, Faculty of Chemical Science and Engineering (China); Li, Chunhu [Oceanology University of China, College of Chemistry and Chemical Engineering (China); Yu, Jianqiang [Qingdao University, Faculty of Chemical Science and Engineering (China)

    2015-07-15

    In{sub 2}O{sub 3} quantum dots with a high crystallinity were deposited on the surface of ZnO nanorods through a chemistry bath method. The resulting In{sub 2}O{sub 3}-sensitizing ZnO nanorod arrays not only exhibited enhanced photoelectrochemical activity for water splitting under visible-light irradiation, but also possessed anti-photocorrosion property. The photo-induced charge-transfer property of In{sub 2}O{sub 3} could be improved greatly by coupling with ZnO. This observation demonstrated that the heterojunction at the interface between In{sub 2}O{sub 3} and ZnO could efficiently reduce the recombination of photo-induced electron–hole pairs and increase the lifetime of charge carriers and therefore enhance the photo-to-current efficiency of the In{sub 2}O{sub 3}–ZnO nanocrystalline arrays. It reveals that the heterojunction construction between two different semiconductors plays a very important role in determining the dynamic properties of their photogenerated charge carriers and their photo-to-current conversion efficiency.

  1. ZnO Nanoparticles/Reduced Graphene Oxide Bilayer Thin Films for Improved NH3-Sensing Performances at Room Temperature

    Science.gov (United States)

    Tai, Huiling; Yuan, Zhen; Zheng, Weijian; Ye, Zongbiao; Liu, Chunhua; Du, Xiaosong

    2016-03-01

    ZnO nanoparticles and graphene oxide (GO) thin film were deposited on gold interdigital electrodes (IDEs) in sequence via simple spraying process, which was further restored to ZnO/reduced graphene oxide (rGO) bilayer thin film by the thermal reduction treatment and employed for ammonia (NH3) detection at room temperature. rGO was identified by UV-vis absorption spectra and X-ray photoelectron spectroscope (XPS) analyses, and the adhesion between ZnO nanoparticles and rGO nanosheets might also be formed. The NH3-sensing performances of pure rGO film and ZnO/rGO bilayer films with different sprayed GO amounts were compared. The results showed that ZnO/rGO film sensors exhibited enhanced response properties, and the optimal GO amount of 1.5 ml was achieved. Furthermore, the optimal ZnO/rGO film sensor showed an excellent reversibility and fast response/recovery rate within the detection range of 10-50 ppm. Meanwhile, the sensor also displayed good repeatability and selectivity to NH3. However, the interference of water molecules on the prepared sensor is non-ignorable; some techniques should be researched to eliminate the effect of moisture in the further work. The remarkably enhanced NH3-sensing characteristics were speculated to be attributed to both the supporting role of ZnO nanoparticles film and accumulation heterojunction at the interface between ZnO and rGO. Thus, the proposed ZnO/rGO bilayer thin film sensor might give a promise for high-performance NH3-sensing applications.

  2. Applying RF Magnetron sputtering to prepare ZnO thin films and their characterization

    International Nuclear Information System (INIS)

    Saad, M.; Kassis, A.

    2009-05-01

    ZnO thin films were prepared using Rf magnetron sputtering under several preparation conditions (different values of deposition pressure, Rf power, substrate temperature). The optical properties of these films were investigated by measuring their transmission in the spectral range (300-1000 nm), and the electrical properties were investigated by measuring their electrical resistance. Results have been discussed in terms of the modified Thornton model for sputtered thin metal oxide films. Preparation conditions for depositing the highly resistive transparent i-ZnO buffer layer and the highly conducting transparent n-ZnO window layer for solar cells were proposed. (author)

  3. Influence of Ag thickness of aluminum-doped ZnO/Ag/aluminum-doped ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Wu, Hung-Wei, E-mail: hwwu@mail.ksu.edu.tw [Department of Computer and Communication, Kun Shan University, No. 949, Dawan Rd., Yongkang Dist., Tainan City 710, Taiwan (China); Yang, Ru-Yuan [Graduate Institute of Materials Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China); Hsiung, Chin-Min; Chu, Chien-Hsun [Department of Mechanical Engineering, National Pingtung University of Science and Technology, 1, Shuefu Rd., Neipu, Pingtung City 912, Taiwan (China)

    2012-10-01

    Highly conducting aluminum-doped ZnO (30 nm)/Ag (5-15 nm)/aluminum-doped ZnO (30 nm) multilayer thin films were deposited on glass substrate by rf magnetron sputtering (for top/bottom aluminum-doped ZnO films) and e-beam evaporation (for Ag film). The transmittance is more than 70% for wavelengths above 400 nm with the Ag layer thickness of 10 nm. The resistivity is 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm, which can be decreased to 3.8 Multiplication-Sign 10{sup -5} {Omega}-cm with the increase of the Ag layer thickness to 15 nm. The Haacke figure of merit has been calculated for the films with the best value being 8 Multiplication-Sign 10{sup -3} {Omega}{sup -1}. It was shown that the multilayer thin films have potential for applications in optoelectronics. - Highlights: Black-Right-Pointing-Pointer High-quality Al-doped ZnO (AZO)/Ag/AZO Transparent Conducting Oxide films. Black-Right-Pointing-Pointer AZO films (30 nm) made by RF sputtering; E-beam evaporation for Ag film (5-15 nm). Black-Right-Pointing-Pointer Influence of Ag thickness on optical and electrical properties were analyzed. Black-Right-Pointing-Pointer High quality multilayer film with optimal intermediate Ag layer thickness of 10 nm. Black-Right-Pointing-Pointer 3.71 Multiplication-Sign 10{sup -4} {Omega}-cm resistivity, 91.89% transmittance at 470 nm obtained and reproducible.

  4. The role of Al, Ba, and Cd dopant elements in tailoring the properties of c-axis oriented ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Ali, Dilawar [Department of Physics GC University, Lahore 54000 (Pakistan); Center for Advanced Studies in Physics, GC University Lahore, Lahore 54000 (Pakistan); Butt, M.Z., E-mail: mzakriabutt@gmail.com [Center for Advanced Studies in Physics, GC University Lahore, Lahore 54000 (Pakistan); Arif, Bilal [Department of Physics, Faculty of Arts and Sciences, Firat University, 23169 Elazig (Turkey); Al-Ghamdi, Ahmed A. [Department of Physics, Faculty of Sciences, King Abdul Aziz University, Jeddah (Saudi Arabia); Yakuphanoglu, Fahrettin [Department of Physics, Faculty of Arts and Sciences, Firat University, 23169 Elazig (Turkey); Department of Physics, Faculty of Sciences, King Abdul Aziz University, Jeddah (Saudi Arabia)

    2017-02-01

    Highly c-axis oriented un-doped ZnO and Al-, Ba-, and Cd-doped ZnO thin films were successfully deposited on glass substrate employing sol-gel spin coating method. XRD analysis showed that all thin films possess hexagonal wurtzite structure with preferred orientation along c-axis. Field emission scanning electron microscope (FESEM) was used to study the morphology of thin films. The morphology consists of spherical and non-spherical shape grains. EDX analysis confirms the presence of O, Zn, Al, Ba, and Cd in the relevant thin films. The optical properties of thin films were studied using UV–Vis spectrometer. All thin films possess more than 85% optical transmittance in the visible region. Blue shift in optical band gap E{sub g} has been observed on doping with Al, whereas doping with Ba and Cd resulted in red shift of E{sub g}. Urbach energy E{sub u} of all doped ZnO thin films was found to have excellent correlation with their band gap energy E{sub g}. Moreover, E{sub g} increases while E{sub u} decreases on the increase in crystallite size D. Optical parameters E{sub g} and E{sub u} as well as structural parameters lattice strain and stacking fault probability also show excellent correlation with the B-factor or the mean-square amplitude of atomic vibrations of the dopant elements. Electrical conductivity measurement of the thin films was carried out using two-point probe method. The electrical conductivity was found to increase with the increase in crystallite orientation along c-axis.

  5. Photocatalytic Activity and Stability of Porous Polycrystalline ZnO Thin-Films Grown via a Two-Step Thermal Oxidation Process

    Directory of Open Access Journals (Sweden)

    James C. Moore

    2014-08-01

    Full Text Available The photocatalytic activity and stability of thin, polycrystalline ZnO films was studied. The oxidative degradation of organic compounds at the ZnO surface results from the ultraviolet (UV photo-induced creation of highly oxidizing holes and reducing electrons, which combine with surface water to form hydroxyl radicals and reactive oxygen species. Therefore, the efficiency of the electron-hole pair formation is of critical importance for self-cleaning and antimicrobial applications with these metal-oxide catalyst systems. In this study, ZnO thin films were fabricated on sapphire substrates via direct current sputter deposition of Zn-metal films followed by thermal oxidation at several annealing temperatures (300–1200 °C. Due to the ease with which they can be recovered, stabilized films are preferable to nanoparticles or colloidal suspensions for some applications. Characterization of the resulting ZnO thin films through atomic force microscopy and photoluminescence indicated that decreasing annealing temperature leads to smaller crystal grain size and increased UV excitonic emission. The photocatalytic activities were characterized by UV-visible absorption measurements of Rhodamine B dye concentrations. The films oxidized at lower annealing temperatures exhibited higher photocatalytic activity, which is attributed to the increased optical quality. Photocatalytic activity was also found to depend on film thickness, with lower activity observed for thinner films. Decreasing activity with use was found to be the result of decreasing film thickness due to surface etching.

  6. Exploration of Al-Doped ZnO in Photovoltaic Thin Films

    Science.gov (United States)

    Ciccarino, Christopher; Sahiner, M. Alper

    The electrical properties of Al doped ZnO-based thin films represent a potential advancement in the push for increasing solar cell efficiency. Doping with Aluminum will theoretically decrease resistivity of the film and therefore achieve this potential as a viable option in the P-N junction phase of photovoltaic cells. The n-type semi-conductive characteristics of the ZnO layer will theoretically be optimized with the addition of Aluminum carriers. In this study, Aluminum doping concentrations ranging from 1-3% by mass were produced, analyzed, and compared. Films were developed onto ITO coated glass using the Pulsed Laser Deposition technique. Target thickness was 250 nm and ellipsometry measurements showed uniformity and accuracy in this regard. Active dopant concentrations were determined using Hall Effect measurements. Efficiency measurements showed possible applications of this doped compound, with upwards of 7% efficiency measured, using a Keithley 2602 SourceMeter set-up. XRD scans showed highly crystalline structures, with effective Al intertwining of the hexagonal wurtzile ZnO molecular structure. This alone indicates a promising future of collaboration between these two materials.

  7. Low-temperature deposition of ZnO thin films on PET and glass substrates by DC-sputtering technique

    International Nuclear Information System (INIS)

    Banerjee, A.N.; Ghosh, C.K.; Chattopadhyay, K.K.; Minoura, Hideki; Sarkar, Ajay K.; Akiba, Atsuya; Kamiya, Atsushi; Endo, Tamio

    2006-01-01

    The structural, optical and electrical properties of ZnO thin films (260 - 490 nm thick) deposited by direct-current sputtering technique, at a relatively low-substrate temperature (363 K), onto polyethylene terephthalate and glass substrates have been investigated. X-ray diffraction patterns confirm the proper phase formation of the material. Optical transmittance data show high transparency (80% to more than 98%) of the films in the visible portion of solar radiation. Slight variation in the transparency of the films is observed with a variation in the deposition time. Electrical characterizations show the room-temperature conductivity of the films deposited onto polyethylene terephthalate substrates for 4 and 5 h around 0.05 and 0.25 S cm -1 , respectively. On the other hand, for the films deposited on glass substrates, these values are 8.5 and 9.6 S cm -1 for similar variation in the deposition time. Room-temperature conductivity of the ZnO films deposited on glass substrates is at least two orders of magnitude higher than that of ZnO films deposited onto polyethylene terephthalate substrates under identical conditions. Hall-measurements show the maximum carrier concentration of the films on PET and glass substrate around 2.8 x 10 16 and 3.1 x 10 2 cm -3 , respectively. This report will provide newer applications of ZnO thin films in flexible display technology

  8. Structural and Optical Properties of ZnO Thin Film Prepared by Oxidation of Zn Metal Powders

    International Nuclear Information System (INIS)

    Hassan, N.K.; Hashim, M.R.

    2013-01-01

    High quality ZnO nano structures have been fabricated at room temperature by a simple vacuum thermal evaporator from metallic Zn powders (99.999 % purity) on a silicon (100) substrate. The Zn thin films were then transferred into a thermal tube furnace for oxidation at 700 degree Celsius for different time durations. Time was found to be a critical factor in the synthesis. This was followed by characterization of their morphological, structural and optical properties. The morphology of the grown ZnO nano structures exhibited several large grains, which increased gradually with increasing oxidation time. The crystallinity of the grown nano structures was investigated using X-ray diffraction, revealing that the synthesized ZnO was in hexagonal wurtzite phase. The photoluminescence (PL) spectra of the fabricated ZnO nano structures showed high intensity peak in the UV region due to near-band-edge (NBE) emission in which the structures oxidized for 30 min showing highest intensity. (author)

  9. Photoluminescence studies of ZnO thin films on R-plane sapphire substrates grown by sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Kim, Min Su [Department of Nano Systems Engineering, Center for Nano Manufacturing, Inje University, Gimhae, Gyungnam 621-749 (Korea, Republic of); Nam, Giwoong; Kim, Soaram [Department of Nano Engineering, Inje University, Gimhae, Gyungnam 621-749 (Korea, Republic of); Kim, Do Yeob [Holcombe Department of Electrical and Computer Engineering, Center for Optical Materials Science and Engineering Technologies, Clemson University, Clemson, SC 29634 (United States); Lee, Dong-Yul [LED R and D team, Samsung Electronics Co. Ltd., Yongin 446-711 (Korea, Republic of); Kim, Jin Soo [Research Center of Advanced Materials Development (RCAMD), Division of Advanced Materials Engineering, Chonbuk National University, Jeonju, Chonbuk 561-756 (Korea, Republic of); Kim, Sung-O [Holcombe Department of Electrical and Computer Engineering, Center for Optical Materials Science and Engineering Technologies, Clemson University, Clemson, SC 29634 (United States); Kim, Jong Su [Department of Physics, Yeungnam University, Gyeongsan, Gyeongsangbuk-do 712-749 (Korea, Republic of); Son, Jeong-Sik [Department of Visual Optics, Kyungwoon University, Gumi, Gyeongsangbuk-do 730-850 (Korea, Republic of); Leem, Jae-Young, E-mail: jyleem@inje.ac.kr [Department of Nano Systems Engineering, Center for Nano Manufacturing, Inje University, Gimhae, Gyungnam 621-749 (Korea, Republic of)

    2012-10-15

    Zinc oxide (ZnO) thin films on R-plane sapphire substrates were grown by the sol-gel spin-coating method. The optical properties of the ZnO thin films were investigated using photoluminescence. In the UV range, the asymmetric near-band-edge emission was observed at 300 K, which consisted of two emissions at 3.338 and 3.279 eV. Eight peaks at 3.418, 3.402, 3.360, 3.288, 3.216, 3.145, 3.074, and 3.004 eV, which respectively correspond to the free exciton (FX), bound exciton, transverse optical (TO) phonon replica of FX recombination, and first-order longitudinal optical phonon replica of FX and the TO (1LO+TO), 2LO+TO, 3LO+TO, 4LO+TO, and 5LO+TO, were obtained at 12 K. From the temperature-dependent PL, it was found that the emission peaks at 3.338 and 3.279 eV corresponded to the FX and TO, respectively. The activation energy of the FX and TO emission peaks was found to be about 39.3 and 28.9 meV, respectively. The values of the fitting parameters of Varshni's empirical equation were {alpha}=4 Multiplication-Sign 10{sup -3} eV/K and {beta}=4.9 Multiplication-Sign 10{sup 3} K, and the S factor of the ZnO thin films was 0.658. With increasing temperature, the exciton radiative lifetime of the FX and TO emissions increased. The temperature-dependent variation of the exciton radiative lifetime for the TO emission was slightly higher than that for the FX emission. - Highlights: Black-Right-Pointing-Pointer ZnO thin films on R-plane sapphire substrates were grown by sol-gel method. Black-Right-Pointing-Pointer Two emission peaks at 3.338 and 3.279 eV were observed at 300 K Black-Right-Pointing-Pointer Activation energies of the two peaks were 39.3 and 28.9 meV,respectively. Black-Right-Pointing-Pointer Exciton radiative lifetime of the two peaks increased with increasing temperature.

  10. Crystalline nanostructured Cu doped ZnO thin films grown at room temperature by pulsed laser deposition technique and their characterization

    Energy Technology Data Exchange (ETDEWEB)

    Drmosh, Qasem A. [Department of Mechanical Engineering, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia); Rao, Saleem G.; Yamani, Zain H. [Laser Research Group, Department of Physics, Center of Excellence in Nanotechnology, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia); Gondal, Mohammed A., E-mail: magondal@kfupm.edu.sa [Laser Research Group, Department of Physics, Center of Excellence in Nanotechnology, King Fahd University of Petroleum and Minerals, Dhahran 31261 (Saudi Arabia)

    2013-04-01

    We report structural and optical properties of Cu doped ZnO (ZnO:Cu) thin films deposited on glass substrate at room temperature by pulsed laser deposition (PLD) method without pre and post annealing contrary to all previous reports. For preparation of (ZnO:Cu) composites pure Zn and Cu targets in special geometrical arrangements were exposed to 248 nm radiations generated by KrF exciter laser. The laser energy was 200 mJ with 10 Hz frequency and 20 ns pulse width. The effect of Cu concentration on crystal structure, morphology, and optical properties were investigated by XRD, FESEM and photoluminescence spectrometer respectively. A systematic shift in ZnO (0 0 2) peak with Cu concentration observed in XRD spectra demonstrated that Cu ion has been incorporated in ZnO lattice. Uniform film with narrow size range grains were observed in FESEM images. The photoluminescence (PL) spectra measured at room temperature revealed a systematic red shift in ZnO emission peak and decrease in the band gap with the increase in Cu concentration. These results entail that PLD technique can be realized to deposit high quality crystalline ZnO and ZnO:Cu thin films without pre and post heat treatment which is normally practiced worldwide for such structures.

  11. Luminescence of two-dimensional ordered array of the ZnO quantum nanodots, obtained by means of the synthetic opal

    International Nuclear Information System (INIS)

    Gruzintsev, A.N.; Volkov, V.T.; Emelchenko, G.A.; Karpov, I.A.; Maslov, W.M.; Michailov, G.M.; Yakimov, E.E.

    2004-01-01

    The luminescence properties of ZnO films of different thickness obtained on a synthetic opal were investigated. Several narrow peaks in the exciton emission region related to the size quantum effect of the electron wave functions were detected. Two-dimensional ordered array of ZnO quantum dots formed inside the opal pores on the second sphere layer were found by the atomic force microscopy (AFM) and angle dependence of the luminescence spectra

  12. Vertically integrated nanogenerator based on ZnO nanowire arrays

    Energy Technology Data Exchange (ETDEWEB)

    Yu, Aifang; Li, Hongyu; Tang, Haoying; Liu, Tengjiao; Jiang, Peng [National Center for Nanoscience and Technology, No.11, Beiyitiao Zhongguancun, Beijing 100190 (China); Wang, Zhong Lin [National Center for Nanoscience and Technology, No.11, Beiyitiao Zhongguancun, Beijing 100190 (China); School of Materials Science and Engineering, Georgia Institute of Technology, Atlanta, GA 30332-0245 (United States)

    2011-04-15

    We report a technique to construct a vertically integrated nanogenerator (VI-NG) based on ZnO nanowire (NW) arrays. The VI-NG consists of nine single NGs connected mixed parallel and serial by a layer-by-layer stacking. For the single layer NG, the peak output voltage and current are 0.045 V and 2.5 nA, respectively. The VI-NG produces an output power density of 2.8 nW/cm{sup 2} with a peak output voltage of 0.15 V and output current of 7.2 nA. The vertical integration of the multi-NG provides a feasible technique for effectively converting mechanical energies to electricity from environment. (copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  13. Growth of vertically aligned ZnO nanorods using textured ZnO films

    Directory of Open Access Journals (Sweden)

    Meléndrez Manuel

    2011-01-01

    Full Text Available Abstract A hydrothermal method to grow vertical-aligned ZnO nanorod arrays on ZnO films obtained by atomic layer deposition (ALD is presented. The growth of ZnO nanorods is studied as function of the crystallographic orientation of the ZnO films deposited on silicon (100 substrates. Different thicknesses of ZnO films around 40 to 180 nm were obtained and characterized before carrying out the growth process by hydrothermal methods. A textured ZnO layer with preferential direction in the normal c-axes is formed on substrates by the decomposition of diethylzinc to provide nucleation sites for vertical nanorod growth. Crystallographic orientation of the ZnO nanorods and ZnO-ALD films was determined by X-ray diffraction analysis. Composition, morphologies, length, size, and diameter of the nanorods were studied using a scanning electron microscope and energy dispersed x-ray spectroscopy analyses. In this work, it is demonstrated that crystallinity of the ZnO-ALD films plays an important role in the vertical-aligned ZnO nanorod growth. The nanorod arrays synthesized in solution had a diameter, length, density, and orientation desirable for a potential application as photosensitive materials in the manufacture of semiconductor-polymer solar cells. PACS 61.46.Hk, Nanocrystals; 61.46.Km, Structure of nanowires and nanorods; 81.07.Gf, Nanowires; 81.15.Gh, Chemical vapor deposition (including plasma-enhanced CVD, MOCVD, ALD, etc.

  14. Transparent conductive ZnO layers on polymer substrates: Thin film deposition and application in organic solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Dosmailov, M. [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Leonat, L.N. [Linz Institute for Organic Solar Cells (LIOS)/Institute of Physical Chemistry, Johannes Kepler University Linz, A-4040 Linz (Austria); Patek, J. [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Roth, D.; Bauer, P. [Institute of Experimental Physics, Johannes Kepler University Linz, A-4040 Linz (Austria); Scharber, M.C.; Sariciftci, N.S. [Linz Institute for Organic Solar Cells (LIOS)/Institute of Physical Chemistry, Johannes Kepler University Linz, A-4040 Linz (Austria); Pedarnig, J.D., E-mail: johannes.pedarnig@jku.at [Institute of Applied Physics, Johannes Kepler University Linz, A-4040 Linz (Austria)

    2015-09-30

    Aluminum doped ZnO (AZO) and pure ZnO thin films are grown on polymer substrates by pulsed-laser deposition and the optical, electrical, and structural film properties are investigated. Laser fluence, substrate temperature, and oxygen pressure are varied to obtain transparent, conductive, and stoichiometric AZO layers on polyethylene terephthalate (PET) that are free of cracks. At low fluence (1 J/cm{sup 2}) and low pressure (10{sup −3} mbar), AZO/PET samples of high optical transmission in the visible range, low electrical sheet resistance, and high figure of merit (FOM) are produced. AZO films on fluorinated ethylene propylene have low FOM. The AZO films on PET substrates are used as electron transport layer in inverted organic solar cell devices employing P3HT:PCBM as photovoltaic polymer-fullerene bulk heterojunction. - Highlights: • Aluminum doped and pure ZnO thin films are grown on polyethylene terephthalate. • Growth parameters laser fluence, temperature, and gas pressure are optimized. • AZO films on PET have high optical transmission and electrical conductance (FOM). • Organic solar cells on PET using AZO as electron transport layer are made. • Power conversion efficiency of these OSC devices is measured.

  15. The effects of ZnO buffer layers on the properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition

    International Nuclear Information System (INIS)

    Kim, K-W; Lugo, F J; Lee, J H; Norton, D P

    2012-01-01

    The properties of phosphorus doped ZnO thin films grown on sapphire by pulsed laser deposition were examined, specifically focusing on the effects of undoped ZnO buffer layers. In particular, buffer layers were grown under different conditions; the transport properties of as-deposited and rapid thermal annealed ZnO:P films were then examined. As-deposited films showed n-type conductivity. After rapid thermal annealing, the film on buffer layer grown at a low temperature showed the conversion of carrier type to p-type for specific growth conditions while the films deposited on buffer layer grown at a high temperature remained n-type regardless of growth condition. The films deposited on buffer layer grown at a low temperature showed higher resistivity and more significant change of the transport properties upon rapid thermal annealing. These results suggest that more dopants are incorporated in films with higher defect density. This is consistent with high resolution x-ray diffraction results for phosphorus doped ZnO films on different buffer layers. In addition, the microstructure of phosphorus doped ZnO films is substantially affected by the buffer layer.

  16. The effect of post-annealing on surface acoustic wave devices based on ZnO thin films prepared by magnetron sputtering

    International Nuclear Information System (INIS)

    Phan, Duy-Thach; Chung, Gwiy-Sang

    2011-01-01

    Zinc oxide (ZnO) thin films were deposited on unheated silicon substrates via radio frequency (RF) magnetron sputtering, and the post-deposition annealing of the ZnO thin films was performed at 400 deg. C, 600 deg. C, 800 deg. C, and 1000 deg. C. The characteristics of the thin films were investigated by X-ray diffractometry (XRD), scanning electron microscopy (SEM), and atomic force microscopy (AFM). The films were then used to fabricate surface acoustic wave (SAW) resonators. The effects of post-annealing on the SAW devices are discussed in this work. Resulting in the 600 deg. C is determined as optimal annealing temperature for SAW devices. At 400 deg. C, the microvoids exit between the grains yield large root mean square (RMS) surface roughness and higher insertion losses in SAW devices. The highest RMS surface roughness, crack and residual stress cause a reduction of surface velocity (about 40 m/s) and increase dramatically insertion loss at 1000 deg. C. The SAW devices response becomes very weak at this temperature, the electromechanical coupling coefficient (k 2 ) of ZnO film decrease from 3.8% at 600 deg. C to 1.49% at 1000 deg. C.

  17. Microstructure of ZnO thin films deposited by high power impulse magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Reed, A.N., E-mail: amber.reed.5@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Shamberger, P.J. [Department of Materials Science and Engineering, Texas A& M University, College Station, TX 77843 (United States); Hu, J.J. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Muratore, C. [Department of Chemical and Materials Engineering, University of Dayton, Dayton, OH 45469 (United States); Bultman, J.E. [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States); University of Dayton Research Institute, University of Dayton, Dayton, OH 45469 (United States); Voevodin, A.A., E-mail: andrey.voevodin@us.af.mil [Materials and Manufacturing Directorate, Air Force Research Laboratory, 3005 Hobson Way, Wright Patterson Air Force Base, OH 45433 (United States)

    2015-03-31

    High power impulse magnetron sputtering was used to deposit thin (~ 100 nm) zinc oxide (ZnO) films from a ceramic ZnO target onto substrates heated to 150 °C. The resulting films had strong crystallinity, highly aligned (002) texture and low surface roughness (root mean square roughness less than 10 nm), as determined by X-ray diffraction, transmission electron microscopy, scanning electron microscopy and atomic force spectroscopy measurements. Deposition pressure and target–substrate distance had the greatest effect on film microstructure. The degree of alignment in the films was strongly dependent on the gas pressure. Deposition at pressures less than 0.93 Pa resulted in a bimodal distribution of grain sizes. An initial growth layer with preferred orientations (101) and (002) parallel to the interface was observed at the film–substrate interface under all conditions examined here; the extent of that competitive region was dependent on growth conditions. Time-resolved current measurements of the target and ion energy distributions, determined using energy resolved mass spectrometry, were correlated to film microstructure in order to investigate the effect of plasma conditions on film nucleation and growth. - Highlights: • Low temperature growth of nanocrystalline zinc oxide (ZnO) films. • ZnO films had a highly (002) textured, smooth, dense microstructure. • Dominant (002) orientation of films was pressure dependent. • Interfacial (101)/(002) mixed orientation layer controlled by substrate location.

  18. A hierarchically assembled mesoporous ZnO hemisphere array and hollow microspheres for photocatalytic membrane water filtration.

    Science.gov (United States)

    Pan, Jia Hong; Zhang, Xiwang; Du, Alan J; Bai, Hongwei; Ng, Jiawei; Sun, Darren

    2012-05-28

    A mesoporous ZnO hemisphere array has been prepared via a topotactic transition of Zn(4)(OH)(6)CO(3)·H(2)O (ZCHH) by chemical bath deposition. Each hemisphere is comprised of a radially oriented nanoflake shell grown on the hemispherical interior. Reaction time-dependent SEM analysis shows that the morphological formation of ZCHH involves a deposition-growth-secondary growth-redeposition procedure. Upon calcination, ZCHH readily decomposes to nanocrystalline wurtzite-phase ZnO without significant change in morphology, and the release of CO(2) and H(2)O from ZCHH creates an additional mesoporous structure in both hemispherical interior and nanoflake shell. A similar process but without using a substrate has been developed for synthesis of mesoporous ZnO hollow microspheres in powder form. Both the elaborated superstructured photocatalysts consisting of mesoporous nanoflakes have been demonstrated to exhibit excellent performances in the photocatalytic membrane filtration.

  19. ZnO transparent conductive oxide for thin film silicon solar cells

    Science.gov (United States)

    Söderström, T.; Dominé, D.; Feltrin, A.; Despeisse, M.; Meillaud, F.; Bugnon, G.; Boccard, M.; Cuony, P.; Haug, F.-J.; Faÿ, S.; Nicolay, S.; Ballif, C.

    2010-03-01

    There is general agreement that the future production of electric energy has to be renewable and sustainable in the long term. Photovoltaic (PV) is booming with more than 7GW produced in 2008 and will therefore play an important role in the future electricity supply mix. Currently, crystalline silicon (c-Si) dominates the market with a share of about 90%. Reducing the cost per watt peak and energy pay back time of PV was the major concern of the last decade and remains the main challenge today. For that, thin film silicon solar cells has a strong potential because it allies the strength of c-Si (i.e. durability, abundancy, non toxicity) together with reduced material usage, lower temperature processes and monolithic interconnection. One of the technological key points is the transparent conductive oxide (TCO) used for front contact, barrier layer or intermediate reflector. In this paper, we report on the versatility of ZnO grown by low pressure chemical vapor deposition (ZnO LP-CVD) and its application in thin film silicon solar cells. In particular, we focus on the transparency, the morphology of the textured surface and its effects on the light in-coupling for micromorph tandem cells in both the substrate (n-i-p) and superstrate (p-i-n) configurations. The stabilized efficiencies achieved in Neuchâtel are 11.2% and 9.8% for p-i-n (without ARC) and n-i-p (plastic substrate), respectively.

  20. Effect of growth time to the properties of Al-doped ZnO nanorod arrays

    Science.gov (United States)

    Ismail, A. S.; Mamat, M. H.; Malek, M. F.; Saidi, S. A.; Yusoff, M. M.; Mohamed, R.; Sin, N. D. Md; Suriani, A. B.; Rusop, M.

    2018-05-01

    Aluminum (Al)-doped zinc oxide (ZnO) nanorod array films were successfully deposited at different growth time on zinc oxide (ZnO) seed layer coated glass substrate using sol-gel immersion method. The morphology images of the films showed that the thicknesses of the films were increased parallel with the increment of growth period. The surface topology of the films displayed an increment of roughness as the growth period increased. Optical properties of the samples exposed that the percentage of transmittances reduced at higher growth time. Besides, the Urbach energy of the films slightly increased as the immersion time increased. The current-voltage (I-V) measurement indicated that the resistance increased as the immersion time increased owing to the appearance of intrinsic layer on top of the nanorods.

  1. Atomic Layer Deposition of Nickel on ZnO Nanowire Arrays for High-Performance Supercapacitors.

    Science.gov (United States)

    Ren, Qing-Hua; Zhang, Yan; Lu, Hong-Liang; Wang, Yong-Ping; Liu, Wen-Jun; Ji, Xin-Ming; Devi, Anjana; Jiang, An-Quan; Zhang, David Wei

    2018-01-10

    A novel hybrid core-shell structure of ZnO nanowires (NWs)/Ni as a pseudocapacitor electrode was successfully fabricated by atomic layer deposition of a nickel shell, and its capacitive performance was systemically investigated. Transmission electron microscopy and X-ray photoelectron spectroscopy results indicated that the NiO was formed at the interface between ZnO and Ni where the Ni was oxidized by ZnO during the ALD of the Ni layer. Electrochemical measurement results revealed that the Ti/ZnO NWs/Ni (1500 cycles) electrode with a 30 nm thick Ni-NiO shell layer had the best supercapacitor properties including ultrahigh specific capacitance (∼2440 F g -1 ), good rate capability (80.5%) under high current charge-discharge conditions, and a relatively better cycling stability (86.7% of the initial value remained after 750 cycles at 10 A g -1 ). These attractive capacitive behaviors are mainly attributed to the unique core-shell structure and the combined effect of ZnO NW arrays as short charge transfer pathways for ion diffusion and electron transfer as well as conductive Ni serving as channel for the fast electron transport to Ti substrate. This high-performance Ti/ZnO NWs/Ni hybrid structure is expected to be one of a promising electrodes for high-performance supercapacitor applications.

  2. Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

    Science.gov (United States)

    Ning, Shuai; Zhan, Peng; Wang, Wei-Peng; Li, Zheng-Cao; Zhang, Zheng-Jun

    2014-12-01

    Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ~ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ~ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed.

  3. Thin Flexible IMM Solar Array, Phase II

    Data.gov (United States)

    National Aeronautics and Space Administration — Thin, flexible, and highly efficient solar arrays are needed that package compactly for launch and deploy into large, structurally stable high power generators....

  4. A study of Eu incorporated ZnO thin films: An application of Al/ZnO:Eu/p-Si heterojunction diode

    Energy Technology Data Exchange (ETDEWEB)

    Turgut, G. [Department of Basic Sciences, Faculty of Science, Erzurum Technical University, Erzurum, 25240 (Turkey); Duman, S., E-mail: sduman@atauni.edu.tr [Department of Physics, Faculty of Science, Ataturk University, Erzurum, 25240 (Turkey); Sonmez, E. [Department of Physics, Faculty of K.K. Education, Ataturk University, Erzurum, 25240 (Turkey); Ozcelik, F.S. [Department of Physics, Faculty of Science, Ataturk University, Erzurum, 25240 (Turkey)

    2016-04-15

    Highlights: • Eu incorporated ZnO thin films were grown by sol–gel spin coating. • The influence of Eu contribution on features of ZnO was investigated. • Al/ZnO:Eu/p-Si heterojunction diodes were also fabricated. • The diode parameters were calculated from I–V measurements. - Abstract: In present work, the pure and europium (Eu) incorporated zinc oxide (ZnO) thin films were deposited with sol-gel spin coating by using zinc acetate dehydrate and Eu (III) chloride salts. The coated films were examined by means of XRD, AFM and UV/VIS spectrophotometer. The ZnO hexagonal wurtzite nanoparticles with (002) preferential direction were observed for all films. The values of crystallite size, micro-strain and surface roughness continuously increased from 21 nm, 1.10 × 10{sup −3} and 2.43 nm to the values of 35.56 nm, 1.98 × 10{sup −3} and 28.99 nm with Eu doping, respectively. The optical band gap value of the pure ZnO initially increased from 3.296 eV to 3.328 eV with Eu doping up to 2 at.% doping level, then it started to decrease with more Eu content. The electrical features of Al/n-ZnO:Eu/p-Si heterojunction diodes were inquired by current-voltage (I–V) measurements at the room temperature.

  5. Growing vertical ZnO nanorod arrays within graphite: efficient isolation of large size and high quality single-layer graphene.

    Science.gov (United States)

    Ding, Ling; E, Yifeng; Fan, Louzhen; Yang, Shihe

    2013-07-18

    We report a unique strategy for efficiently exfoliating large size and high quality single-layer graphene directly from graphite into DMF dispersions by growing ZnO nanorod arrays between the graphene layers in graphite.

  6. Enhanced photovoltaic performance of ZnO nanorod-based dye-sensitized solar cells by using Ga doped ZnO seed layer

    Energy Technology Data Exchange (ETDEWEB)

    Dou, Yuanyao [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Wu, Fang, E-mail: fang01234@163.com [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Mao, Caiying [Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Fang, Liang, E-mail: lfang@cqu.edu.cn [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China); Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Guo, Shengchun [Department of Applied Physics, College of Physics, Chongqing University, Chongqing 401331 (China); Zhou, Miao [State Key Laboratory of Mechanical Transmission, Chongqing University, Chongqing 400044 (China)

    2015-06-05

    Highlights: • ZnO nanorods were grown on Ga-doped ZnO seed layers using hydrothermal method. • Using the ZnO nanorods as photoanodes for fabricated dye-sensitized solar cells. • The highest η of 1.23% can be achieved in a DSSC with 3 at.% Ga-doped in seeds. • The effects of ZnO seed layers on electron transport properties were investigated. • The enhancement performance of DSSCs contributed to higher dye loading and η{sub cc}. - Abstract: Zinc oxide (ZnO) nanorod arrays were grown on FTO substrates with a Ga-doped ZnO (GZO) seed layer by a hydrothermal method. GZO seed layers were obtained via sol–gel technology with Ga concentration in the range of 0–4 at.%. The dye sensitized solar cells (DSSCs) using ZnO nanorod arrays as the photoanode layers were prepared. The effect of Ga dopant concentrations in ZnO seed layer on the morphology features of ZnO nanorod arrays and the performance of DSSCs were systematically investigated. Results indicate that the average diameter and density of ZnO nanorod arrays decrease with increasing Ga concentration, but their length shows an opposite trend. The photocurrent density–voltage (J–V) characteristics reveal that the DSSCs with GZO seed layer exhibit significantly improved photovoltaic performance. In particular, the highest energy conversion efficiency (η) of 1.23% can be achieved in a DSSC with 3 at.% Ga doping, which is increased by 86.36% compared with that of the undoped DSSC. The external quantum efficiency (EQE) spectra and electrochemical impedance spectroscopy (EIS) were employed to explore the photon-to-electron conversion process in DSSCs. It is demonstrated that the performance enhancement of DSSCs based on GZO seed layer can be attributed to higher amount of dye loading, more efficient electron transportation and better electrons collection efficiency.

  7. Microstructure and optical properties of nanocrystalline ZnO and ZnO:(Li or Al) thin films

    Energy Technology Data Exchange (ETDEWEB)

    Oral, A. Yavuz [Department of Materials Science and Engineering, Gebze Institute of Technology, Gebze 41400 (Turkey)]. E-mail: aoral@gyte.edu.tr; Bahsi, Z. Banu [Department of Materials Science and Engineering, Gebze Institute of Technology, Gebze 41400 (Turkey); Aslan, M. Hasan [Department of Physics, Gebze Institute of Technology, Gebze 41400 (Turkey)

    2007-03-15

    Zinc oxide thin films (ZnO, ZnO:Li, ZnO:Al) were deposited on glass substrates by a sol-gel technique. Zinc acetate, lithium acetate, and aluminum chloride were used as metal ion sources in the precursor solutions. XRD analysis revealed that Li doped and undoped ZnO films formed single phase zincite structure in contrast to Al:ZnO films which did not fully crystallize at the annealing temperature of 550 deg. C. Crystallized films had a grain size under 50 nm and showed c-axis grain orientation. All films had a very smooth surface with RMS surface roughness values between 0.23 and 0.35 nm. Surface roughness and optical band tail values increased by Al doping. Compared to undoped ZnO films, Li doping slightly increased the optical band gap of the films.

  8. Effect of Co doping concentration on structural properties and optical parameters of Co-doped ZnO thin films by sol-gel dip-coating method.

    Science.gov (United States)

    Nam, Giwoong; Yoon, Hyunsik; Kim, Byunggu; Lee, Dong-Yul; Kim, Jong Su; Leem, Jae-Young

    2014-11-01

    The structural and optical properties of Co-doped ZnO thin films prepared by a sol-gel dip-coating method were investigated. X-ray diffraction analysis showed that the thin films were grown with a c-axis preferred orientation. The position of the (002) peak was almost the same in all samples, irrespective of the Co concentration. It is thus clear that Co doping had little effect on the position of the (002) peak. To confirm that Co2+ was substituted for Zn2+ in the wurtzite structure, optical measurements were conducted at room temperature by a UV-visible spectrometer. Three absorption peaks are apparent in the Co-doped ZnO thin films that do not appear for the undoped ZnO thin film. As the Co concentration was increased, absorption related to characteristic Co2+ transitions increased because three absorption band intensities and the area underneath the absorption wells between 500 and 700 nm increased with increasing Co concentration. The optical band gap and static dielectric constant decreased and the Urbach energy and extinction coefficient increased with increasing Co concentration.

  9. Rectifying Behavior of Aligned ZnO Nano rods on Mg0.3Zn0.7O Thin Film Template

    International Nuclear Information System (INIS)

    Salina Muhamad; Suriani Abu Bakar; Mohamad Hafiz Mamat; Rafidah Ahmad; Mohamad Rusop

    2011-01-01

    Rectifying behavior more than 3 orders of aligned zinc oxide (ZnO) nano rods grown on Mg 0.3 Zn 0.7 O thin film template using chemical bath deposition method was observed, giving a barrier height of 0.75 eV, and the ideality factor achieved was almost 6, which was analyzed using thermionic emission theory. Field emission scanning electron microscope (FESEM) images revealed that the grown ZnO was in hexagonal shape, uniformly distributed and in vertically aligned form. The crystallinity of the sample being studied using X-ray diffraction (XRD), where the highest peak was found at (002) phase, confirming that high crystallinity of ZnO was attained. The effect of metal/semiconductor junction between metal and aligned ZnO nano rods was discussed in further details. (author)

  10. Functionalized carbon nanotubes in ZnO thin films for photoinactivation of bacteria

    International Nuclear Information System (INIS)

    Akhavan, O.; Azimirad, R.; Safa, S.

    2011-01-01

    Highlights: → Unfunctionalized and functionalized MWCNT/ZnO thin films were synthesized by sol-gel method. → Zn-O-C carbonaceous bonds formed in the functionalized MWCNT/ZnO thin films. → The functionalized MWCNT/ZnO had stronger photoinactivation of the bacteria than the unfunctionalize type. → 10 wt% functionalized MWCNT content had the optimum antibacterial property. - Abstract: Two types of unfunctionalized and functionalized multi-wall carbon nanotubes (MWCNTs) were prepared to be applied in fabrication of MWCNT-ZnO nanocomposite thin films with various MWCNT contents. X-ray photoelectron spectroscopy indicated formation of functional groups on surface of the functionalized MWCNTs in the MWCNT-ZnO nanocomposite. Formation of the effective carbonaceous bonds between the ZnO and the MWCNTs was also investigated through photoinactivation of Escherichia coli bacteria on surface of the both unfunctionalized and functionalized MWCNT-ZnO nanocomposites. The functionalized MWCNT-ZnO nanocomposites showed significantly stronger photoinactivation of the bacteria than the unfunctionalized ones, for all of the various MWCNT contents (from 2 to 30 wt%). While the functionalized MWCNT-ZnO nanocomposites with the optimum MWCNT content of 10 wt% inactivated whole of the bacteria after 10 min UV-visible light irradiation, the unfunctionalized ones could inactivate only 63% of the bacteria under the same conditions. The significant enhancement of the photoinactivation of the bacteria onto the surface of the functionalized MWCNT-ZnO nanocomposites was assigned to charge transfer through Zn-O-C bands formed between the Zn atoms of the ZnO film and oxygen atoms of the carboxylic functional groups of the functionalized MWCNTs.

  11. Structural, Morphological, and LPG Sensing Properties of Al-Doped ZnO Thin Film Prepared by SILAR

    Directory of Open Access Journals (Sweden)

    Shampa Mondal

    2013-01-01

    Full Text Available Undoped and aluminum doped zinc oxide (AZO thin films were deposited on glass substrates by successive ion layer adsorption and reaction (SILAR technique from ammonium zincate complex. The thin films are characterized by X-ray diffraction (XRD and scanning electron microscopy (SEM for their structural and morphological studies. Both undoped and Al-doped film show strong preferred c-axis orientation. The texture coefficient (TC of the film along (002 direction increases due to Al incorporation. SEM micrograph shows round shaped particles for pure ZnO. However AZO films show particles with off spherical shape and compact interconnected grains. Sensitivity of the film in presence of 80% LEL (lower explosive limit of LPG increases with temperature and is maximum at 325°C. Significantly high sensitivity of 87% with reasonably fast response was observed for 1% Al-doped ZnO (AZO film in presence of 1.6 vol% LPG at 325°C.

  12. Effect of strain on the structural and optical properties of Cu-N co-doped ZnO thin films

    International Nuclear Information System (INIS)

    Zhao Yue; Zhou Mintao; Li Zhao; Lv Zhiyong; Liang Xiaoyan; Min Jiahua; Wang Linjun; Shi Weimin

    2011-01-01

    Polycrystalline ZnO thin films co-doped with Cu and N have been obtained by chemical bath deposition. Introduction of Cu and N causes the change of strained stress in ZnO films, which subsequently affects the structural and optical properties. The dependence of structural and optical properties of the ZnO films on lattice strained stress is investigated by XRD measurement, SEM, PL spectrum, optical reflection and Raman spectrum. The result of photoluminescence of Cu-N co-doped ZnO films indicates that the UV emission peaks shift slightly towards higher energy side with decrease in tensile strain and vise versa. The blue-shift of the absorption edge and up-shift of E2 (high) mode of the films can be observed in the optical reflection and Raman spectra. - Highlights: →Cu-N co-doped ZnO is first prepared by the wet chemical method. → Stress is produced by the introduction of Cu and N atoms. → Effect of stress on the structural and optical properties of ZnO film is investigated. → Cu concentration will be used to control the structural and optical properties.

  13. ZnO THIN FILMS PREPARED BY SPRAY-PYROLYSIS TECHNIQUE FROM ORGANO-METALLIC PRECURSOR

    Directory of Open Access Journals (Sweden)

    Martin Mikulics

    2012-07-01

    Full Text Available Presented experiments utilize methanolic solution of zinc acetyl-acetonate as a precursor and sapphire (001 as a substrate for deposition of thin films of ZnO. The X-ray diffraction analysis revealed polycrystalline character of prepared films with preferential growth orientation along c-axis. The roughness of prepared films was assessed by AFM microscopy and represented by roughness root mean square (RMS value in range of 1.8 - 433 nm. The surface morphology was mapped by scanning electron microscopy showing periodical structure with several local defects. The optical transmittance spectrum of ZnO films was measured in wavelength range of 200-1000 nm. Prepared films are transparent in visible range with sharp ultra-violet cut-off at approximately 370 nm. Raman spectroscopy confirmed wurtzite structure and the presence of compressive stress within its structure as well as the occurrence of oxygen vacancies. The four-point Van der Pauw method was used to study the transport prosperities. The resistivity of presented ZnO films was found 8 × 10–2 Ω cm with carrier density of 1.3 × 1018 cm–3 and electron mobility of 40 cm2 V–1 s–1.

  14. Epitaxial properties of ZnO thin films on SrTiO3 substrates grown by laser molecular beam epitaxy

    International Nuclear Information System (INIS)

    Wei, X. H.; Li, Y. R.; Zhu, J.; Huang, W.; Zhang, Y.; Luo, W. B.; Ji, H.

    2007-01-01

    Epitaxial ZnO thin films with different orientations have been grown by laser molecular beam epitaxy on (001)- (011)-, and (111)-orientated SrTiO 3 single-crystal substrates. The growth behavior was in situ monitored by reflection high-energy electron diffraction, and the epitaxial orientation relations were reconfirmed by ex situ x-ray diffraction measurements. In the case of ZnO on SrTiO 3 (001), four orthogonal domains coexisted in the ZnO epilayer, i.e., ZnO(110) parallel SrTiO 3 (001) and ZnO[-111] parallel SrTiO 3 . For (011)- and (111)-orientated substrates, single-domain epitaxy with c axial orientation was observed, in which the in-plane relationship was ZnO[110] parallel SrTiO 3 [110] irrespective of the substrate orientations. Additionally, the crystalline quality of ZnO on SrTiO 3 (111) was better than that of ZnO on SrTiO 3 (011) because of the same symmetry between the (111) substrates and (001) films. The obtained results can be attributed to the difference of the in-plane crystallographic symmetry. Furthermore, those alignments can be explained by the interface stress between the substrates and the films

  15. Post-annealing effect on the room-temperature ferromagnetism in Cu-doped ZnO thin films

    International Nuclear Information System (INIS)

    Hu, Yu-Min; Kuang, Chein-Hsiun; Han, Tai-Chun; Yu, Chin-Chung; Li, Sih-Sian

    2015-01-01

    In this work, we investigated the structural and magnetic properties of both as-deposited and post-annealed Cu-doped ZnO thin films for better understanding the possible mechanisms of room-temperature ferromagnetism (RT-FM) in ZnO-based diluted magnetic oxides. All of the films have a c-axis-oriented wurtzite structure and display RT-FM. X-ray photoelectron spectroscopy results showed that the incorporated Cu ions in as-deposited films are in 1+ valence state merely, while an additional 2+ valence state occurs in post-annealed films. The presence of Cu 2+ state in post-annealed film accompanies a higher magnetization value than that of as-deposited film and, in particular, the magnetization curves at 10 K and 300 K of the post-annealed film separate distinctly. Since Cu 1+ ion has a filled 3d band, the RT-FM in as-deposited Cu-doped ZnO thin films may stem solely from intrinsic defects, while that in post-annealed films is enhanced due to the presence of CuO crystallites

  16. Thermal activation of nitrogen acceptors in ZnO thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Dangbegnon, J.K.; Talla, K.; Botha, J.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth (South Africa)

    2010-06-15

    Nitrogen doping in ZnO is inhibited by spontaneous formation of compensating defects. Perfect control of the nitrogen doping concentration is required, since a high concentration of nitrogen could induce the formation of donor defects involving nitrogen. In this work, the effect of post-growth annealing in oxygen ambient on ZnO thin films grown by Metalorganic Chemical Vapor Deposition, using NO as both oxidant and nitrogen dopant, is studied. After annealing at 700 C and above, low-temperature photoluminescence shows the appearance of a transition at {proportional_to}3.23 eV which is interpreted as pair emission involving a nitrogen acceptor. A second transition at {proportional_to}3.15 eV is also discussed. This work suggests annealing as a potential means for p-type doping using nitrogen (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  17. Defect characterization and magnetic properties in un-doped ZnO thin film annealed in a strong magnetic field

    International Nuclear Information System (INIS)

    Ning Shuai; Zhan Peng; Wang Wei-Peng; Li Zheng-Cao; Zhang Zheng-Jun

    2014-01-01

    Highly c-axis oriented un-doped zinc oxide (ZnO) thin films, each with a thickness of ∼ 100 nm, are deposited on Si (001) substrates by pulsed electron beam deposition at a temperature of ∼ 320 °C, followed by annealing at 650 °C in argon in a strong magnetic field. X-ray photoelectron spectroscopy (XPS), positron annihilation analysis (PAS), and electron paramagnetic resonance (EPR) characterizations suggest that the major defects generated in these ZnO films are oxygen vacancies. Photoluminescence (PL) and magnetic property measurements indicate that the room-temperature ferromagnetism in the un-doped ZnO film originates from the singly ionized oxygen vacancies whose number depends on the strength of the magnetic field applied in the thermal annealing process. The effects of the magnetic field on the defect generation in the ZnO films are also discussed. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  18. Improvement of stoichiometry in (ZnO)1-x(GaN)x thin films grown by laser ablation

    International Nuclear Information System (INIS)

    Gopalakrishnan, N.; Shin, B.C.; Bhuvana, K.P.; Elanchezhiyan, J.; Balasubramanian, T.

    2008-01-01

    The fabrication of pure and GaN (1 mol%) doped ZnO thin films by KrF excimer laser have been addressed. The fabricated films on Si(1 1 1) substrates have been investigated by X-ray diffraction (XRD), photoluminescence (PL) and atomic force microscopy (AFM) in order to investigate the structural, optical and morphological properties, respectively. The XRD analysis shows that the full width at half maximum (FWHM) of ZnO film is found to be decreased as doped with GaN due to the improvement of the stoichiometery between Zn and O. The PL spectra reveal that the deep level emissions due to native donor defects in pure ZnO are suppressed upon doping with GaN. The images of AFM show that the RMS surface roughness of pure ZnO, 27 nm is reduced to18 nm while doped with 1 mol% GaN. The incorporation of nitrogen in the film is confirmed by glow discharge mass spectroscopy (GDMS). The improved structural, optical and morphological properties of ZnO by GaN dopant due to enhancement of stoichiometry have been discussed in detail

  19. Effects of intermittent atomization on the properties of Al-doped ZnO thin films deposited by aerosol-assisted chemical vapor deposition

    Energy Technology Data Exchange (ETDEWEB)

    Liu, Linjie; Wang, Lixin [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Qin, Xiujuan, E-mail: qinxj@ysu.edu.cn [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Cui, Li [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); Shao, Guangjie [Hebei Key Laboratory of Applied Chemistry, Yanshan University, Qinhuangdao 066004 (China); State Key Laboratory of Metastable Materials Science and Technology, Yanshan University, Qinhuangdao 066004 (China)

    2016-04-30

    Al-doped ZnO (AZO) thin films were prepared on glass substrates with different atomization interval times by aerosol-assisted chemical vapor deposition method. The structure, morphology, and optical and electrical properties were investigated by X-ray diffractometer, atomic force microscope, UV-vis double beam spectrophotometer and 4 point probe method. ZnO thin films exhibited strong growth orientation along the (002) plane and the crystalline was affected by the atomization interval time. All the films had high transmittance and the films with interval times of 2 min and 4 min had good haze values for the transparent conducting oxide silicon solar cell applications. The AZO thin film had the best optical and electrical properties when the atomization interval time was 4 min. This is very important for the optoelectronic device applications. The surface morphology of AZO films depended on the atomization interval time. - Highlights: • Intermittent atomization is proved to be an effective measure. • Atomization interval time has an important influence on the crystallinity of films. • The surface morphology of ZnO films depends on atomization interval time. • Different hazes can be obtained by changing the atomization interval time.

  20. Effects of intermittent atomization on the properties of Al-doped ZnO thin films deposited by aerosol-assisted chemical vapor deposition

    International Nuclear Information System (INIS)

    Liu, Linjie; Wang, Lixin; Qin, Xiujuan; Cui, Li; Shao, Guangjie

    2016-01-01

    Al-doped ZnO (AZO) thin films were prepared on glass substrates with different atomization interval times by aerosol-assisted chemical vapor deposition method. The structure, morphology, and optical and electrical properties were investigated by X-ray diffractometer, atomic force microscope, UV-vis double beam spectrophotometer and 4 point probe method. ZnO thin films exhibited strong growth orientation along the (002) plane and the crystalline was affected by the atomization interval time. All the films had high transmittance and the films with interval times of 2 min and 4 min had good haze values for the transparent conducting oxide silicon solar cell applications. The AZO thin film had the best optical and electrical properties when the atomization interval time was 4 min. This is very important for the optoelectronic device applications. The surface morphology of AZO films depended on the atomization interval time. - Highlights: • Intermittent atomization is proved to be an effective measure. • Atomization interval time has an important influence on the crystallinity of films. • The surface morphology of ZnO films depends on atomization interval time. • Different hazes can be obtained by changing the atomization interval time.

  1. Peptide modified ZnO nanoparticles as gas sensors array for volatile organic compounds (VOCs)

    Science.gov (United States)

    Mascini, Marcello; Gaggiotti, Sara; Della Pelle, Flavio; Di Natale, Corrado; Qakala, Sinazo; Iwuoha, Emmanuel; Pittia, Paola; Compagnone, Dario

    2018-04-01

    In this work a peptide based gas sensor array based of ZnO nanoparticles (ZnONPs) has been realized. Four different pentapeptides molecularly modelled for alcohols and esters having cysteine as a common spacer have been immobilized onto ZnONPs. ZnONPs have been morphologically and spectroscopically characterized. Modified nanoparticles have been then deposited onto quartz crystal microbalances (QCMs) and used as gas sensors with nitrogen as carrier gas. Analysis of the pure compounds modelled demonstrated a nice fitting of modelling with real data. The peptide based ZnONPs had very low sensitivity to water, compared to previously studied AuNPs peptide based gas sensors allowing the use of the array on samples with high water content. Real samples of fruit juices have been assayed; stability of the signal, good repeatability and discrimination ability of the array was achieved.

  2. Peptide Modified ZnO Nanoparticles as Gas Sensors Array for Volatile Organic Compounds (VOCs

    Directory of Open Access Journals (Sweden)

    Marcello Mascini

    2018-04-01

    Full Text Available In this work a peptide based gas sensor array based of ZnO nanoparticles (ZnONPs has been realized. Four different pentapeptides molecularly modeled for alcohols and esters having cysteine as a common spacer have been immobilized onto ZnONPs. ZnONPs have been morphologically and spectroscopically characterized. Modified nanoparticles have been then deposited onto quartz crystal microbalances (QCMs and used as gas sensors with nitrogen as carrier gas. Analysis of the pure compounds modeled demonstrated a nice fitting of modeling with real data. The peptide based ZnONPs had very low sensitivity to water, compared to previously studied AuNPs peptide based gas sensors allowing the use of the array on samples with high water content. Real samples of fruit juices have been assayed; stability of the signal, good repeatability, and discrimination ability of the array was achieved.

  3. Enhanced electrical properties of dual-layer channel ZnO thin film transistors prepared by atomic layer deposition

    Science.gov (United States)

    Li, Huijin; Han, Dedong; Dong, Junchen; Yu, Wen; Liang, Yi; Luo, Zhen; Zhang, Shengdong; Zhang, Xing; Wang, Yi

    2018-05-01

    The thin film transistors (TFTs) with a dual-layer channel structure combing ZnO thin layer grown at 200 °C and ZnO film grown at 120 °C by atomic layer deposition are fabricated. The dual-layer channel TFT exhibits a low leakage current of 2.8 × 10-13 A, Ion/Ioff ratio of 3.4 × 109, saturation mobility μsat of 12 cm2 V-1 s-1, subthreshold swing (SS) of 0.25 V/decade. The SS value decreases to 0.18 V/decade after the annealing treatment in O2 due to the reduction of the trap states at the channel/dielectric interface and in the bulk channel layer. The enhanced performance obtained from the dual-layer channel TFTs is due to the ability of maintaining high mobility and suppressing the increase in the off-current at the same time.

  4. Theoretical study of the multiferroic properties in M-doped (M=Co, Cr, Mg) ZnO thin films

    Energy Technology Data Exchange (ETDEWEB)

    Bahoosh, S.G. [Max Planck Institute of Microstructure Physics, Weinberg 2, 06120 Halle (Germany); Apostolov, A.T. [University of Architecture, Civil Engineering and Geodesy, Faculty of Hydrotechnics, Department of Physics, 1, Hristo Smirnenski Blvd., 1046 Sofia (Bulgaria); Apostolova, I.N. [University of Forestry, Faculty of Forest Industry, 10, Kl. Ohridsky Blvd., 1756 Sofia (Bulgaria); Trimper, S. [Institute of Physics, Martin-Luther-University, D-06099 Halle (Germany); Wesselinowa, Julia M. [University of Sofia, Department of Physics, Blvd. J. Bouchier 5, 1164 Sofia (Bulgaria)

    2015-01-01

    The origin of multiferroism is still an open problem in ZnO. We propose a microscopic model to clarify the occurrence of multiferroism in this material. Using Green's function technique we study the influence of ion doping and size effects on the magnetization and polarization of ZnO thin films. The calculations for magnetic Co- and Cr-ions are based on the s–d model, the transverse Ising model in terms of pseudo-spins and a biquadratic magnetoelectric coupling, whereas in case of nonmagnetic Mg-ions the model takes into account the Coulomb interaction and an indirect coupling between the pseudo-spins via the conduction electrons. We show that the magnetization M exhibits a maximum for a fixed concentration of the doping ions. Furthermore M increases with decreasing film thickness N. The polarization increases with increasing concentration of the dopant and decreasing N. The results are in good agreement with the experimental data. - Highlights: • The paper analyzes the multiferroic properties of doped ZnO thin films by a microscopic model. • The magnetization exhibits a maximum at a fixed doping concentration. • The polarization increases with growing dopant concentration. • The ferroelectric transition temperature is enhanced for increasing dopant concentration.

  5. Surface nanostructuring of thin film composite membranes via grafting polymerization and incorporation of ZnO nanoparticles

    Science.gov (United States)

    Isawi, Heba; El-Sayed, Magdi H.; Feng, Xianshe; Shawky, Hosam; Abdel Mottaleb, Mohamed S.

    2016-11-01

    A new approach for modification of polyamid thin film composite membrane PA(TFC) using synthesized ZnO nanoparticles (ZnO NPs) was shown to enhance the membrane performances for reverse osmosis water desalination. First, active layer of synthesis PA(TFC) membrane was activated with an aqueous solution of free radical graft polymerization of hydrophilic methacrylic acid (MAA) monomer onto the surface of the PA(TFC) membrane resulting PMAA-g-PA(TFC). Second, the PA(TFC) membrane has been developed by incorporation of ZnO NPs into the MAA grafting solution resulting the ZnO NPs modified PMAA-g-PA(TFC) membrane. The surface properties of the synthesized nanoparticles and prepared membranes were investigated using the FTIR, XRD and SEM. Morphology studies demonstrated that ZnO NPs have been successfully incorporated into the active grafting layer over PA(TFC) composite membranes. The zinc leaching from the ZnO NPs modified PMAA-g-PA(TFC) was minimal, as shown by batch tests that indicated stabilization of the ZnO NPs on the membrane surfaces. Compared with the a pure PA(TFC) and PMAA-g-PA(TFC) membranes, the ZnO NPs modified PMAA-g-PA(TFC) was more hydrophilic, with an improved water contact angle (∼50 ± 3°) over the PMAA-g-PA(TFC) (63 ± 2.5°). The ZnO NPs modified PMAA-g-PA(TFC) membrane showed salt rejection of 97% (of the total groundwater salinity), 99% of dissolved bivalent ions (Ca2+, SO42-and Mg2+), and 98% of mono valent ions constituents (Cl- and Na+). In addition, antifouling performance of the membranes was determined using E. coli as a potential foulant. This demonstrates that the ZnO NPs modified PMAA-g-PA(TFC) membrane can significantly improve the membrane performances and was favorable to enhance the selectivity, permeability, water flux, mechanical properties and the bio-antifouling properties of the membranes for water desalination.

  6. Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

    International Nuclear Information System (INIS)

    Korhonen, E; Prozheeva, V; Tuomisto, F; Bierwagen, O; Speck, J S; White, M E; Galazka, Z; Liu, H; Izyumskaya, N; Avrutin, V; Özgür, Ü; Morkoç, H

    2015-01-01

    We present positron annihilation results on Sb-doped SnO 2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO 2 the concentrations appear too low to cause significant compensation. (invited article)

  7. Cation vacancies and electrical compensation in Sb-doped thin-film SnO2 and ZnO

    Science.gov (United States)

    Korhonen, E.; Prozheeva, V.; Tuomisto, F.; Bierwagen, O.; Speck, J. S.; White, M. E.; Galazka, Z.; Liu, H.; Izyumskaya, N.; Avrutin, V.; Özgür, Ü.; Morkoç, H.

    2015-02-01

    We present positron annihilation results on Sb-doped SnO2 and ZnO thin films. The vacancy types and the effect of vacancies on the electrical properties of these intrinsically n-type transparent semiconducting oxides are studied. We find that in both materials low and moderate Sb-doping leads to formation of vacancy clusters of variable sizes. However, at high doping levels cation vacancy defects dominate the positron annihilation signal. These defects, when at sufficient concentrations, can efficiently compensate the n-type doping produced by Sb. This is the case in ZnO, but in SnO2 the concentrations appear too low to cause significant compensation.

  8. Photoelectrochemical study of nanostructured ZnO thin films for hydrogen generation from water splitting

    Energy Technology Data Exchange (ETDEWEB)

    Wolcott, Abraham; Zhang, Jin Z. [Department of Chemistry and Biochemistry, University of California, Santa Cruz 1156 High St. Santa Cruz, CA 95064 (United States); Smith, Wilson A.; Zhao, Yiping [Department of Physics and Astronomy, University of Georgia, Athens, GA 30602 (United States); Kuykendall, Tevye R. [Department of Chemistry, University of California, Berkeley Berkeley, CA 94720 (United States)

    2009-06-23

    Photoelectrochemical cells based on traditional and nanostructured ZnO thin films are investigated for hydrogen generation from water splitting. The ZnO thin films are fabricated using three different deposition geometries: normal pulsed laser deposition, pulsed laser oblique-angle deposition, and electron-beam glancing-angle deposition. The nanostructured films are characterized by scanning electron microscopy, X-ray diffraction, UV-vis spectroscopy and photoelectrochemical techniques. Normal pulsed laser deposition produces dense thin films with ca. 200 nm grain sizes, while oblique-angle deposition produces nanoplatelets with a fishscale morphology and individual features measuring ca. 900 by 450 nm on average. In contrast, glancing-angle deposition generates a highly porous, interconnected network of spherical nanoparticles of 15-40 nm diameter. Mott-Schottky plots show the flat band potential of pulsed laser deposition, oblique-angle deposition, and glancing-angle deposition samples to be -0.29, -0.28 and +0.20 V, respectively. Generation of photocurrent is observed at anodic potentials and no limiting photocurrents were observed with applied potentials up to 1.3 V for all photoelectrochemical cells. The effective photon-to-hydrogen efficiency is found to be 0.1%, 0.2% and 0.6% for pulsed laser deposition, oblique-angle deposition and glancing-angle deposition samples, respectively. The photoelectrochemical properties of the three types of films are understood to be a function of porosity, crystal defect concentration, charge transport properties and space charge layer characteristics. (Abstract Copyright [2009], Wiley Periodicals, Inc.)

  9. Preparation of Zinc Oxide (ZnO) Thin Film as Transparent Conductive Oxide (TCO) from Zinc Complex Compound on Thin Film Solar Cells: A Study of O2 Effect on Annealing Process

    Science.gov (United States)

    Muslih, E. Y.; Kim, K. H.

    2017-07-01

    Zinc oxide (ZnO) thin film as a transparent conductive oxide (TCO) for thin film solar cell application was successfully prepared through two step preparations which consisted of deposition by spin coating at 2000 rpm for 10 second and followed by annealing at 500 °C for 2 hours under O2 and ambient atmosphere. Zinc acetate dehydrate was used as a precursor which dissolved in ethanol and acetone (1:1 mol) mixture in order to make a zinc complex compound. In this work, we reported the O2 effect, reaction mechanism, structure, morphology, optical and electrical properties. ZnO thin film in this work shows a single phase of wurtzite, with n-type semiconductor and has band gap, carrier concentration, mobility, and resistivity as 3.18 eV, 1.21 × 10-19cm3, 11 cm2/Vs, 2.35 × 10-3 Ωcm respectively which is suitable for TCO at thin film solar cell.

  10. Nucleation, Growth Mechanism, and Controlled Coating of ZnO ALD onto Vertically Aligned N-Doped CNTs.

    Science.gov (United States)

    Silva, R M; Ferro, M C; Araujo, J R; Achete, C A; Clavel, G; Silva, R F; Pinna, N

    2016-07-19

    Zinc oxide thin films were deposited on vertically aligned nitrogen-doped carbon nanotubes (N-CNTs) by atomic layer deposition (ALD) from diethylzinc and water. The study demonstrates that doping CNTs with nitrogen is an effective approach for the "activation" of the CNTs surface for the ALD of metal oxides. Conformal ZnO coatings are already obtained after 50 ALD cycles, whereas at lower ALD cycles an island growth mode is observed. Moreover, the process allows for a uniform growth from the top to the bottom of the vertically aligned N-CNT arrays. X-ray photoelectron spectroscopy demonstrates that ZnO nucleation takes place at the N-containing species on the surface of the CNTs by the formation of the Zn-N bonds at the interface between the CNTs and the ZnO film.

  11. Self-compensation in ZnO thin films: An insight from X-ray photoelectron spectroscopy, Raman spectroscopy and time-of-flight secondary ion mass spectroscopy analyses

    International Nuclear Information System (INIS)

    Saw, K.G.; Ibrahim, K.; Lim, Y.T.; Chai, M.K.

    2007-01-01

    As-grown ZnO typically exhibits n-type conductivity and the difficulty of synthesizing p-type ZnO for the realization of ZnO-based optoelectronic devices is mainly due to the compensation effect of a large background n-type carrier concentration. The cause of this self-compensation effect has not been conclusively identified although oxygen vacancies, zinc interstitials and hydrogen have been suggested. In this work, typical n-type ZnO thin films were prepared by sputtering and investigated using X-ray photoelectron spectroscopy, Raman spectroscopy and time-of-flight secondary ion mass spectroscopy to gain an insight on the possible cause of the self-compensation effect. The analyses found that the native defect that most likely behaved as the donor was zinc interstitial but some contribution of n-type conductivity could also come from the electronegative carbonates or hydrogen carbonates incorporated in the ZnO thin films

  12. Fabrication of undoped ZnO thin film via photosensitive sol–gel method and its applications for an electron transport layer of organic solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Luong, Chi Hieu [Department of Materials Science and Engineering and Graduate School of Energy Science and Technology, Chungnam National University, Yuseong-gu, Daejeon 305-764 (Korea, Republic of); Kim, Sarah [Central Research Division, LG Chem., Yuseong-gu, Daejeon 305-738 (Korea, Republic of); Surabhi, Srivathsava; Vo, Thanh Son; Lee, Kyung-Min; Yoon, Soon-Gil [Department of Materials Science and Engineering and Graduate School of Energy Science and Technology, Chungnam National University, Yuseong-gu, Daejeon 305-764 (Korea, Republic of); Jeong, Jun-Ho [Nanomechanical Systems Research Division, Korea Institute of Machinery and Materials, Yuseong-gu, Daejeon 305-343 (Korea, Republic of); Choi, Jun-Hyuk, E-mail: junhyuk@kimm.re.kr [Nanomechanical Systems Research Division, Korea Institute of Machinery and Materials, Yuseong-gu, Daejeon 305-343 (Korea, Republic of); Jeong, Jong-Ryul, E-mail: jrjeong@cnu.ac.kr [Department of Materials Science and Engineering and Graduate School of Energy Science and Technology, Chungnam National University, Yuseong-gu, Daejeon 305-764 (Korea, Republic of)

    2015-10-01

    Highlights: • Investigated the effect of the interfacial ZnO for ETL synthesized by photochemical reaction using photosensitive 2-nitrobenzaldehyde on the inverted P3HT:PCBM OSC. • The abrupt increase of grain size and surface roughness was observed as increasing the annealing temperature above 350 °C. • The sheet resistance abruptly decreased with increasing the annealing temperature above 350 °C. • Increase of surface roughness caused by the high annealing temperature could be detrimental to the OSCs characteristics due to a high contact resistance and a large leakage current. - Abstract: We have investigated ZnO thin films prepared via photochemical reaction as the electron transport layer (ETL) of inverted organic solar cells (OSCs). Morphological and electrical properties of the ZnO thin films prepared by the photosensitive ZnO sol were studied according to the annealing temperature and their effects on the performance of the inverted poly(3-hexylthiophene):phenyl-C61-butyric acid methyl ester (P3HT:PCBM) OSCs was characterized. It was found that the optimal annealing temperature of the ZnO thin films was 330 °C, and that devices with the ZnO ETL annealed at this temperature exhibited the largest short-circuit current density (J{sub sc}) of 9.39 mA/cm{sup 2}, as well as the highest power conversion efficiency (PCE) of 2.31%, which can be attributed to enhanced electron transport and interfacial properties. Devices containing ZnO films formed at optimal annealing condition exhibited an open circuit voltage (V{sub oc}) of 0.60 V and a fill factor (FF) of 41.0%. However, further increase of the annealing temperature led to degradation of the device performance, despite further improvements in electrical properties. We have found that marked increase in the surface roughness of the ZnO films occurred at temperatures above 350 °C which could be detrimental to the OSCs characteristics due to a high contact resistance and a large leakage current.

  13. Characterization of piesoelectric ZnO thin films and the fabrication of piezoelectric micro-cantilevers

    Energy Technology Data Exchange (ETDEWEB)

    Johnson, Raegan Lynn [Iowa State Univ., Ames, IA (United States)

    2005-01-01

    In Atomic Force Microscopy (AFM), a microcantilever is raster scanned across the surface of a sample in order to obtain a topographical image of the sample's surface. In a traditional, optical AFM, the sample rests on a bulk piezoelectric tube and a control loop is used to control the tip-sample separation by actuating the piezo-tube. This method has several disadvantages--the most noticeable one being that response time of the piezo-tube is rather long which leads to slow imaging speeds. One possible solution aimed at improving the speed of imaging is to incorporate a thin piezoelectric film on top of the cantilever beam. This design not only improves the speed of imaging because the piezoelectric film replaces the piezo-tube as an actuator, but the film can also act as a sensor. In addition, the piezoelectric film can excite the cantilever beam near its resonance frequency. This project aims to fabricate piezoelectric microcantilevers for use in the AFM. Prior to fabricating the cantilevers and also part of this project, a systematic study was performed to examine the effects of deposition conditions on the quality of piezoelectric ZnO thin films deposited by RF sputtering. These results will be presented. The deposition parameters that produced the highest quality ZnO film were used in the fabrication of the piezoelectric cantilevers. Unfortunately, the fabricated cantilevers warped due to the intrinsic stress of the ZnO film and were therefore not usable in the AFM. The complete fabrication process will be detailed, the results will be discussed and reasons for the warping will be examined.

  14. Structural characterization of ZnO thin films grown on various substrates by pulsed laser deposition

    International Nuclear Information System (INIS)

    Novotný, M; Bulíř, J; Lančok, J; Čížek, J; Kužel, R; Connolly, J; McCarthy, E; Krishnamurthy, S; Mosnier, J-P; Anwand, W; Brauer, G

    2012-01-01

    ZnO thin films were grown by pulsed laser deposition on three different substrates: sapphire (0 0 0 1), MgO (1 0 0) and fused silica (FS). The structure and morphology of the films were characterized by x-ray diffraction and scanning electron microscopy and defect studies were carried out using slow positron implantation spectroscopy (SPIS). Films deposited on all substrates studied in this work exhibit the wurtzite ZnO structure and are characterized by an average crystallite size of 20-100 nm. However, strong differences in the microstructure of films deposited on various substrates were found. The ZnO films deposited on MgO and sapphire single-crystalline substrates exhibit local epitaxy, i.e. a well-defined relation between film crystallites and the substrate. Domains with different orientation relationships with the substrate were found in both films. On the other hand, the film deposited on the FS substrate exhibits fibre texture with random lateral orientation of crystallites. Extremely high compressive in-plane stress of σ ∼ 14 GPa was determined in the film deposited on the MgO substrate, while the film deposited on sapphire is virtually stress-free, and the film deposited on the FS substrate exhibits a tensile in-plane stress of σ ∼ 0.9 GPa. SPIS investigations revealed that the concentration of open-volume defects in the ZnO films is substantially higher than that in a bulk ZnO single crystal. Moreover, the ZnO films deposited on MgO and sapphire single-crystalline substrates exhibit a significantly higher density of defects than the film deposited on the amorphous FS substrate. (paper)

  15. Earth-Abundant Oxygen Evolution Catalysts Coupled onto ZnO Nanowire Arrays for Efficient Photoelectrochemical Water Cleavage

    Science.gov (United States)

    Jiang, Chaoran; Moniz, Savio J A; Khraisheh, Majeda; Tang, Junwang

    2014-01-01

    ZnO has long been considered as a model UV-driven photoanode for photoelectrochemical water splitting, but its performance has been limited by fast charge-carrier recombination, extremely poor stability in aqueous solution, and slow kinetics of water oxidation. These issues were addressed by applying a strategy of optimization and passivation of hydrothermally grown 1D ZnO nanowire arrays. The length and diameter of bare ZnO nanowires were optimized by varying the growth time and precursor concentration to achieve optimal photoelectrochemical performance. The addition of earth-abundant cobalt phosphate (Co-Pi) and nickel borate (Ni-B) oxygen evolution catalysts onto ZnO nanowires resulted in substantial cathodic shifts in onset potential to as low as about 0.3 V versus the reversible hydrogen electrode (RHE) for Ni-B/ZnO, for which a maximum photocurrent density of 1.1 mA cm−2 at 0.9 V (vs. RHE) with applied bias photon-to-current efficiency of 0.4 % and an unprecedented near-unity incident photon-to-current efficiency at 370 nm. In addition the potential required for saturated photocurrent was dramatically reduced from 1.6 to 0.9 V versus RHE. Furthermore, the stability of these ZnO nanowires was significantly enhanced by using Ni-B compared to Co-Pi due to its superior chemical robustness, and it thus has additional functionality as a stable protecting layer on the ZnO surface. These remarkable enhancements in both photocatalytic activity and stability directly address the current severe limitations in the use of ZnO-based photoelectrodes for water-splitting applications, and can be applied to other photoanodes for efficient solar-driven fuel synthesis. PMID:25156820

  16. Study of copper doping effects on structural, optical and electrical properties of sprayed ZnO thin films

    International Nuclear Information System (INIS)

    Mhamdi, A.; Mimouni, R.; Amlouk, A.; Amlouk, M.; Belgacem, S.

    2014-01-01

    Highlights: • The sprayed Cu-doped ZnO thin layers films were well crystallised in hexagonal wurtzite phase. • Nanoncrystallites on clusters were observed whose density decreases especially at 2% Cu content. • This parallel circuit R–C represents the contribution of the grain boundaries delineating the oriented columnar microcrystallites along c-axis. - Abstract: Copper-doped zinc oxide thin films (ZnO:Cu) at different percentages (1–3%) were deposited on glass substrates using a chemical spray technique. The effect of Cu concentration on the structural, morphology and optical properties of the ZnO:Cu thin films were investigated. XRD analysis revealed that all films consist of single phase ZnO and were well crystallised in würtzite phase with the crystallites preferentially oriented towards (0 0 2) direction parallel to c-axis. The Film surface was analyzed by contact atomic force microscopy (AFM) in order to understand the effect of the doping on the surface structure. Doping by copper resulted in a slight decrease in the optical band gap energy of the films and a noticeably change in optical constants. From the spectroscopy impedance analysis we investigated the frequency relaxation phenomenon and the circuit equivalent circuit of such thin layers. Finally, all results have been discussed in terms of the copper doping concentration

  17. Synthesis of ZnO nanowire arrays on ZnO−TiO{sub 2} mixed oxide seed layer for dye sensitized solar cell applications

    Energy Technology Data Exchange (ETDEWEB)

    Marimuthu, T. [Advanced Materials and Thin Film Physics Lab, Department of Physics, Alagappa University, Karaikudi (India); Anandhan, N., E-mail: anandhan_kn@rediffmail.com [Advanced Materials and Thin Film Physics Lab, Department of Physics, Alagappa University, Karaikudi (India); Thangamuthu, R. [Electrochemical Materials Science Division, CSIR-Central Electrochemical Research Institute, Karaikudi (India); Mummoorthi, M. [Advanced Materials and Thin Film Physics Lab, Department of Physics, Alagappa University, Karaikudi (India); Ravi, G. [Photonic Crystal Lab, Department of Physics, Alagappa University, Karaikudi (India)

    2016-08-25

    ZnO nanowire arrays (NWAs) were synthesized on ZnO−TiO{sub 2} mixed oxide seeded FTO conducting glass plate by two-step sol-gel and hydrothermal method, respectively. X-ray diffraction patterns reveal the presence of mixed and hexagonal phases in seed layer and NWAs, respectively. Scanning electron microscope images showed that the FTO glass plate is uniformly covered with grains and a few nanorods in seed layer and dense NWAs are vertically grown on the seed layer. The hexagonal structure and high crystal quality have been confirmed by micro Raman spectra. Photoluminescence spectra also present that NWAs have high crystal quality and less atomic defects. UV spectra indicate that NWAs are absorbed more dye molecules and it has the band gap equal to bulk material. The efficiency of ZnO−TiO{sub 2} mixed oxide seed layer and ZnO NWAs is found to be 0.56 and 0.84% respectively. Electrochemical impedance spectra reveal that NWAs DSSC has high charge transfer recombination resistance than the seed layer DSSC. - Highlights: • ZnO nanowire arrays were synthesized by two-step sol-gel and hydrothermal method. • The crystal structure and crystalline quality of films are confirmed by Raman spectra. • The emission properties of films are investigated by photoluminescence spectra. • ZnO nanowire arrays (NWAs) have higher charge transfer recombination resistance. • The conversion efficiency of the seed layer and NWAs is to be 0.56 and 0.84%.

  18. Al and Fe co-doped transparent conducting ZnO thin film for mediator-less biosensing application

    Directory of Open Access Journals (Sweden)

    Shibu Saha

    2011-12-01

    Full Text Available Highly c-axis oriented Al and Fe co-doped ZnO (ZAF thin film is prepared by pulsed laser deposition. Fe introduces redox centre along with shallow donor level while Al doping enhances conductivity of ZnO, thus removing the requirement of both mediator and bottom conducting layer in bioelectrode. Model enzyme (glucose oxidase, was immobilized on surface of ZAF matrix. Cyclic voltammetry and photometric assay show that prepared bio-electrode is sensitive to glucose concentration with enhanced response of 0.18 μAmM-1cm-2 and low Km ∼ 2.01 mM. The results illustrate that ZAF is an attractive matrix for realization of miniaturized mediator-less solid state biosensor.

  19. Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

    KAUST Repository

    Flemban, Tahani H.; Sequeira, M. C.; Zhang, Z.; Venkatesh, S.; Alves, E.; Lorenz, K.; Roqan, Iman S.

    2016-01-01

    Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

  20. Identifying the influence of the intrinsic defects in Gd-doped ZnO thin-films

    KAUST Repository

    Flemban, Tahani H.

    2016-02-08

    Gd-doped ZnO thin films were prepared using pulsed laser deposition at different oxygen pressures and varied Gd concentrations. The effects of oxygen deficiency-related defects on the Gd incorporation, optical and structural properties, were explored by studying the impact of oxygen pressure during deposition and post-growth thermal annealing in vacuum. Rutherford Backscattering Spectrometry revealed that the Gd concentration increases with increasing oxygen pressure for samples grown with the same Gd-doped ZnO target. Unexpectedly, the c-lattice parameter of the samples tends to decrease with increasing Gd concentration, suggesting that Gd-defect complexes play an important role in the structural properties. Using low-temperature photoluminescence(PL), Raman measurements and density functional theory calculations, we identified oxygen vacancies as the dominant intrinsic point defects. PL spectra show a defect band related to oxygen vacancies for samples grown at oxygen deficiency.

  1. Band-Gap Engineering in ZnO Thin Films: A Combined Experimental and Theoretical Study

    Science.gov (United States)

    Pawar, Vani; Jha, Pardeep K.; Panda, S. K.; Jha, Priyanka A.; Singh, Prabhakar

    2018-05-01

    Zinc oxide thin films are synthesized and characterized using x-ray diffraction, field-emission scanning electron microscopy, atomic force microscopy, and optical spectroscopy. Our results reveal that the structural, morphological, and optical properties are closely related to the stress of the sample provided that the texture of the film remains the same. The anomalous results are obtained once the texture is altered to a different orientation. We support this experimental observation by carrying out first-principles hybrid functional calculations for two different orientations of the sample and show that the effect of quantum confinement is much stronger for the (100) surface than the (001) surface of ZnO. Furthermore, our calculations provide a route to enhance the band gap of ZnO by more than 50% compared to the bulk band gap, opening up possibilities for wide-range industrial applications.

  2. Enhanced performance of ZnO microballoon arrays for a triboelectric nanogenerator

    Science.gov (United States)

    Deng, Weili; Zhang, Binbin; Jin, Long; Chen, Yueqi; Chu, Wenjun; Zhang, Haitao; Zhu, Minhao; Yang, Weiqing

    2017-03-01

    In recent years, triboelectric nanogenerators (TENGs), harvesting energy from the environment as a sustainable power source, have attracted great attention. Currently, many reports focus on the effect of surface modification on the electrical output performance of the TENG. In this work, we have fabricated vertically grown ZnO microballoon (ZnOMB) arrays on top of pyramid-featured PDMS patterned film, contacted with PTFE film to construct the TENG. The electrical output performances of the designed TENG are presented under external forces with different frequencies. The corresponding output open-circuit voltage with ZnOMBs could reach about 57 V the current density about 59 mA m-2 at 100 Hz, which was about 2.3 times higher than without any ZnO. The global maximum of the instantaneous peak power could reach 1.1 W m-2 when the external load resistance was about 2 MΩ. Furthermore, the electrical output of the fabricated device could light 30 commercial LED bulbs without any rectifier circuits or energy-storage elements. This clearly suggests that this kind of surface modification can dramatically enhance the output performance of the TENG. Moreover, the design of TENG demonstrated here can be applied to various energy harvesting applications.

  3. Physical properties and heterojunction device demonstration of aluminum-doped ZnO thin films synthesized at room ambient via sol-gel method

    Energy Technology Data Exchange (ETDEWEB)

    Karaagac, Hakan, E-mail: hkaraagac@ucdavis.edu [Department of Electrical and Computer Engineering, University of California at Davis, Davis, CA 95616 (United States); Yengel, Emre; Saif Islam, M. [Department of Electrical and Computer Engineering, University of California at Davis, Davis, CA 95616 (United States)

    2012-04-25

    Highlights: Black-Right-Pointing-Pointer Undoped and Al doped ZnO (AZO) thin films were successfully prepared using sol-gel technique. Black-Right-Pointing-Pointer Structural analysis has revealed that Al doping has a significant influence on preferential orientation. Black-Right-Pointing-Pointer It has been observed that wrinkles forms on the surface of films when annealed with a fast heat ramp up rate. Black-Right-Pointing-Pointer Optical analysis has revealed that that the band gap energy of ZnO thin film increases with increasing Al doping concentration. Black-Right-Pointing-Pointer The lowest resistivity is observed for 1% Al ZnO thin film, which is 2.2 Multiplication-Sign 10{sup -2} ({Omega} cm). - Abstract: ZnO and some of its ternary wide-bandgap alloys offer interesting opportunities for designing materials with tunable band gaps, strong piezoresistivity and controlled electrical conductance with high optical transparency. Synthesizing these materials on arbitrary substrates using low-cost and unconventional techniques can help in integrating semiconductors with different physical, electrical, and optical characteristics on a single substrate for heterogeneous integration of multifunctional devices. Here we report the successful synthesis of aluminum (Al) doped ZnO (AZO) thin films on soda-lime glass, silicon and fluorine doped tin oxide (FTO) pre-coated glass substrates by using sol-gel deposition method at ambient condition. X-ray diffraction (XRD) analysis revealed that varying degree of Al doping significantly impacts the crystal orientation, semiconductor bandgap and optical transparency of the film. Crystal structure of the film is also found to be strongly correlated to the characteristics of the substrate material. The impact of heating rate during post annealing process is studied and optimized in order to improve the surface morphology of the deposited films. Optical characterizations have revealed that bandgap energy of AZO films can be tuned

  4. Structural, optical, and LED characteristics of ZnO and Al doped ZnO thin films

    Science.gov (United States)

    Sandeep, K. M.; Bhat, Shreesha; Dharmaprakash, S. M.

    2017-05-01

    ZnO (pristine) and Al doped ZnO (AZO) films were prepared using sol-gel spin coating method. The XRD analysis showed the enhanced compressive stress in AZO film. The presence of extended states below the conduction band edge in AZO accounts for the redshift in optical bandgap. The PL spectra of AZO showed significant blue emission due to the carrier recombination from defect states. The TRPL curves showed the dominant DAP recombination in ZnO film, whereas defect related recombination in Al doped ZnO film. Color parameters viz: the dominant wavelength, color coordinates (x,y), color purity, luminous efficiency and correlated color temperature (CCT) of ZnO and AZO films are calculated using 1931 (CIE) diagram. Further, a strong blue emission with color purity more than 96% is observed in both the films. The enhanced blue emission in AZO significantly increased the luminous efficiency (22.8%) compared to ZnO film (10.8%). The prepared films may be used as blue phosphors in white light generation.

  5. Enhancement in photo-electrochemical efficiency by reducing recombination rate in branched TiO2 nanotube array on functionalizing with ZnO micro crystals

    Science.gov (United States)

    Boda, Muzaffar Ahmad; Ashraf Shah, Mohammad

    2018-06-01

    In this study, branched TiO2 nanotube array were fabricated through electrochemical anodization process at constant voltage using third generation electrolyte. On account of morphological advantage, these nanotubes shows significant enhancement in photo-electrochemical property than compact or conventional titania nanotube array. However, their photo-electrochemical efficiency intensifies on coating with ZnO micro-crystals. ZnO coated branched TiO2 nanotube array shows a photocurrent density of 27.8 mA cm‑2 which is 1.55 times the photocurrent density (17.2 mA cm‑2) shown by bare branched titania nanotubes. The significant enhancement in photocurrent density shown by the resulting ZnO/TiO2 hybrid structure is attributed to suppression in electron–hole recombination phenomenon by offering smooth pathway to photo generated excitons on account of staggered band edge positions in individual semiconductors.

  6. Surface state modulation through wet chemical treatment as a route to controlling the electrical properties of ZnO nanowire arrays investigated with XPS

    International Nuclear Information System (INIS)

    Lord, Alex M.; Maffeis, Thierry G.; Allen, Martin W.; Morgan, David; Davies, Philip R.; Jones, Daniel R.; Evans, Jonathan E.; Smith, Nathan A.; Wilks, Steve P.

    2014-01-01

    Highlights: • Direct measurement of the surface band bending exhibited by ZnO nanowires using monochromatic XPS. • Modulation of the surface depletion region using wet chemical treatment (EtOH, H 2 O 2 ). • The measured surface potential barrier agrees with electrical measurements of individual nanowires. • H 2 O 2 depletes the nanowire of charge carriers while EtOH donates electrons at the surface. • EtOH has the effect of restoring the surface potential barrier of oxidised nanowires. - Abstract: ZnO is a wide bandgap semiconductor that has many potential applications including solar cell electrodes, transparent thin film transistors and gas/biological sensors. Since the surfaces of ZnO materials have no amorphous or oxidised layers, they are very environmentally sensitive, making control of their semiconductor properties challenging. In particular, the electronic properties of ZnO nanostructures are dominated by surface effects while surface conduction layers have been observed in thin films and bulk crystals. Therefore, the ability to use the ZnO materials in a controlled way depends on the development of simple techniques to modulate their surface electronic properties. Here, we use monochromatic x-ray photoelectron spectroscopy (XPS) to investigate the use of different wet chemical treatments (EtOH, H 2 O 2 ) to control the electronic properties of ZnO nanowires by modulating the surface depletion region. The valence band and core level XPS spectra are used to explore the relationship between the surface chemistry of the nanowires and the surface band bending

  7. Photoelectrocatrocatalytic hydrolysis of starch by using sprayed ZnO thin films

    Science.gov (United States)

    Sapkal, R. T.; Shinde, S. S.; Rajpure, K. Y.; Bhosale, C. H.

    2013-05-01

    Thin films of zinc oxide have been deposited onto glass/FTO substrates at optimized 400 °C by using a chemical spray pyrolysis technique. Deposited films are character photocatalytic activity by using XRD, an SEM, a UV-vis spectrophotometer, and a PEC single-cell reactor. Films are polycrystalline and have a hexagonal (wurtzite) crystal structure with c-axis (002) orientation growth perpendicular to the substrate surface. The observed direct band gap is about 3.22 eV for typical films prepared at 400 °C. The photocatalytic activity of starch with a ZnO photocatalyst has been studied by using a novel photoelectrocatalytic process.

  8. Photoelectrocatrocatalytic hydrolysis of starch by using sprayed ZnO thin films

    International Nuclear Information System (INIS)

    Sapkal, R. T.; Shinde, S. S.; Rajpure, K.Y.; Bhosale, C. H.

    2013-01-01

    Thin films of zinc oxide have been deposited onto glass/FTO substrates at optimized 400 °C by using a chemical spray pyrolysis technique. Deposited films are character photocatalytic activity by using XRD, an SEM, a UV-vis spectrophotometer, and a PEC single-cell reactor. Films are polycrystalline and have a hexagonal (wurtzite) crystal structure with c-axis (002) orientation growth perpendicular to the substrate surface. The observed direct band gap is about 3.22 eV for typical films prepared at 400 °C. The photocatalytic activity of starch with a ZnO photocatalyst has been studied by using a novel photoelectrocatalytic process. (semiconductor materials)

  9. Research Update: Atmospheric pressure spatial atomic layer deposition of ZnO thin films: Reactors, doping, and devices

    Energy Technology Data Exchange (ETDEWEB)

    Hoye, Robert L. Z., E-mail: rlzh2@cam.ac.uk, E-mail: jld35@cam.ac.uk; MacManus-Driscoll, Judith L., E-mail: rlzh2@cam.ac.uk, E-mail: jld35@cam.ac.uk [Department of Materials Science and Metallurgy, University of Cambridge, 27 Charles Babbage Road, Cambridge CB3 0FS (United Kingdom); Muñoz-Rojas, David [LMGP, University Grenoble-Alpes, CNRS, F-3800 Grenoble (France); Nelson, Shelby F. [Kodak Research Laboratories, Eastman Kodak Company, Rochester, New York 14650 (United States); Illiberi, Andrea; Poodt, Paul [Holst Centre/TNO Thin Film Technology, Eindhoven, 5656 AE (Netherlands); Roozeboom, Fred [Holst Centre/TNO Thin Film Technology, Eindhoven, 5656 AE (Netherlands); Department of Applied Physics, Eindhoven University of Technology, P.O. Box 513, Eindhoven, 5600 MB (Netherlands)

    2015-04-01

    Atmospheric pressure spatial atomic layer deposition (AP-SALD) has recently emerged as an appealing technique for rapidly producing high quality oxides. Here, we focus on the use of AP-SALD to deposit functional ZnO thin films, particularly on the reactors used, the film properties, and the dopants that have been studied. We highlight how these films are advantageous for the performance of solar cells, organometal halide perovskite light emitting diodes, and thin-film transistors. Future AP-SALD technology will enable the commercial processing of thin films over large areas on a sheet-to-sheet and roll-to-roll basis, with new reactor designs emerging for flexible plastic and paper electronics.

  10. Zinc-oxide nanorod / copper-oxide thin-film heterojunction for a nitrogen-monoxide gas sensor

    International Nuclear Information System (INIS)

    Yoo, Hwansu; Kim, Hyojin; Kim, Dojin

    2014-01-01

    A novel p - n oxide heterojunction structure was fabricated by employing n-type zinc-oxide (ZnO) nanorods grown on an indium-tin-oxide-coated glass substrate by using the hydrothermal method and a p-type copper-oxide (CuO) thin film deposited onto the ZnO nanorod array by using the sputtering method. The crystallinities and microstructures of the heterojunction materials were examined by using X-ray diffraction and scanning electron microscopy. The observed current - voltage characteristics of the p - n oxide heterojunction showed a nonlinear diode-like rectifying behavior. The effects of an oxidizing or electron acceptor gas, such as nitrogen monoxide (NO), on the ZnO nanorod/CuO thin-film heterojunction were investigated to determine the potential applications of the fabricated material for use in gas sensors. The forward current of the p - n heterojunction was remarkably reduced when NO gas was introduced into dry air at temperatures from 100 to 250 .deg. C. The NO gas response of the oxide heterojunction reached a maximum value at an operating temperature of 180 .deg. C and linearly increased as the NO gas concentration was increased from 5 to 30 ppm. The sensitivity value was observed to be as high as 170% at 180 .deg. C when biased at 2 V in the presence of 20-ppm NO. The ZnO nanorod/CuO thin-film heterojunction also exhibited a stable and repeatable response to NO gas. The experimental results suggest that the ZnO nanorod/CuO thin-film heterojunction structure may be a novel candidate for gas sensors.

  11. Zinc-oxide nanorod / copper-oxide thin-film heterojunction for a nitrogen-monoxide gas sensor

    Energy Technology Data Exchange (ETDEWEB)

    Yoo, Hwansu; Kim, Hyojin; Kim, Dojin [Chungnam National University, Daejeon (Korea, Republic of)

    2014-11-15

    A novel p - n oxide heterojunction structure was fabricated by employing n-type zinc-oxide (ZnO) nanorods grown on an indium-tin-oxide-coated glass substrate by using the hydrothermal method and a p-type copper-oxide (CuO) thin film deposited onto the ZnO nanorod array by using the sputtering method. The crystallinities and microstructures of the heterojunction materials were examined by using X-ray diffraction and scanning electron microscopy. The observed current - voltage characteristics of the p - n oxide heterojunction showed a nonlinear diode-like rectifying behavior. The effects of an oxidizing or electron acceptor gas, such as nitrogen monoxide (NO), on the ZnO nanorod/CuO thin-film heterojunction were investigated to determine the potential applications of the fabricated material for use in gas sensors. The forward current of the p - n heterojunction was remarkably reduced when NO gas was introduced into dry air at temperatures from 100 to 250 .deg. C. The NO gas response of the oxide heterojunction reached a maximum value at an operating temperature of 180 .deg. C and linearly increased as the NO gas concentration was increased from 5 to 30 ppm. The sensitivity value was observed to be as high as 170% at 180 .deg. C when biased at 2 V in the presence of 20-ppm NO. The ZnO nanorod/CuO thin-film heterojunction also exhibited a stable and repeatable response to NO gas. The experimental results suggest that the ZnO nanorod/CuO thin-film heterojunction structure may be a novel candidate for gas sensors.

  12. Nanostructured ZnO thin films by chemical bath deposition in basic aqueous ammonia solutions for photovoltaic applications

    Energy Technology Data Exchange (ETDEWEB)

    Chu, J.B.; Huang, S.M.; Zhang, D.W.; Bian, Z.Q.; Li, X.D.; Sun, Z. [East China Normal University, Engineering Research Center for Nanophotonics and Advanced Instrument, Ministry of Education, Department of Physics, Shanghai (China); Yin, X.J. [Singapore Polytechnic, Advanced Materials Technology Center, Singapore (Singapore)

    2009-06-15

    This paper presents further insights and observations of the chemical bath deposition (CBD) of ZnS thin films using an aqueous medium involving Zn-salt, ammonium sulfate, aqueous ammonia, and thiourea. Results on physical and chemical properties of the grown layers as a function of ammonia concentration are reported. Physical and chemical properties were analyzed using scanning electron microscopy (SEM), X-ray energy dispersive (EDX), and X-ray diffraction (XRD). Rapid growth of nanostructured ZnO films on fluorine-doped SnO{sub 2} (FTO) glass substrates was developed. ZnO films crystallized in a wurtzite hexagonal structure and with a very small quantity of Zn(OH){sub 2} and ZnS phases were obtained for the ammonia concentration ranging from 0.75 to 2.0 M. Flower-like and columnar nanostructured ZnO films were deposited in two ammonia concentration ranges, respectively: one between 0.75 and 1.0 M and the other between 1.4 and 2.0 M. ZnS films were formed with a high ammonia concentration of 3.0 M. The formation mechanisms of ZnO, Zn(OH){sub 2}, and ZnS phases were discussed in the CBD process. The developed technique can be used to directly and rapidly grow nanostructured ZnO film photoanodes. Annealed ZnO nanoflower and columnar nanoparticle films on FTO substrates were used as electrodes to fabricate the dye sensitized solar cells (DSSCs). The DSSC based on ZnO-nanoflower film showed an energy conversion efficiency of 0.84%, which is higher compared to that (0.45%) of the cell being constructed using a photoanode of columnar nanoparticle ZnO film. The results have demonstrated the potential applications of CBD nanostructured ZnO films for photovoltaic cells. (orig.)

  13. Electron transport properties in ZnO nanowires/poly(3-hexylthiophene) hybrid nanostructure

    International Nuclear Information System (INIS)

    Cheng Ke; Cheng Gang; Wang Shujie; Fu Dongwei; Zou Bingsuo; Du Zuliang

    2010-01-01

    The ZnO nanowires (NWs) array/poly(3-hexylthiophene) (P3HT) hybrid prototype device was fabricated. An ultraviolet (UV) light of λ = 350 nm is used to investigate the photo-electric properties of the ZnO NWs array and hybrid structure. In this way, we can avoid the excitation of P3HT, which can give us a real electron transport ability of ZnO NWs itself. Our results demonstrated a higher and faster photo-electric response of 3 s for the hybrid structure while 9 s for the ZnO NWs array. The surface states related slow photo-electric response was also observed for them. The charge transfer mechanism and the influence of surface states were discussed. The current work provides us profound understandings on the electron transport ability of ZnO NWs array in a working hybrid polymer solar cell, which is crucial for optimizing the device performance.

  14. Thin Film growth and characterization of Ti doped ZnO by RF/DC magnetron sputtering

    KAUST Repository

    Baseer Haider, M.

    2015-01-01

    Thin film Ti doped ZnO (Ti-ZnO) film were grown on sapphire (0001) substrate by RF and DC magnetron sputtering. Films were grown at a substrate temperature of 250 °C with different Ti/Zn concentration. Surface chemical study of the samples was performed by X-ray photoelectron spectroscopy to determine the stoichiometry and Ti/Zn ratio for all samples. Surface morphology of the samples were studied by atomic force microscopy. X-ray diffraction was carried out to determine the crystallinity of the film. No secondary phases of TixOy was observed. We observed a slight increase in the lattice constant with the increase in Ti concentration in ZnO. No ferromagnetic signal was observed for any of the samples. However, some samples showed super-paramagnetic phase. © 2015 Materials Research Society.

  15. Aqueous chemical growth and application of ZnO nanorods

    Energy Technology Data Exchange (ETDEWEB)

    Postels, Bianca; Kasprzak, Anna; Mofor, Augustine C.; Wehmann, Hergo-Heinrich; Bakin, Andrey; Waag, Andreas [Institute of Semiconductor Technology, Technical University Braunschweig, Hans-Sommer-Str. 66, 38106 Braunschweig (Germany)

    2007-07-01

    A very promising fabrication process for ZnO nanostructures is the aqueous chemical growth (ACG), since it is a cost efficient and low temperature approach. Using this growth technique we generated wafer-scale ZnO nanorod arrays on Si, sapphire, ITO coated glass and even on flexible polymer substrates. ACG is found to be only weakly influenced by the substrate material and we are also able to control the dimensions of the ZnO nanorods. Another benefit of ACG is the ability to fabricate patterned arrays of ZnO nanorods by a selective growth process on structured metallised surfaces. Results of structural analysis with SEM and XRD are reported. Additionally, optical properties were investigated by PL measurements. First attempts on the preparation of dye sensitised solar cells (DSSCs) are also reported. Here, the traditional sintered TiO{sub 2} nanoparticles are replaced by a densely packed and vertically aligned array of ACG ZnO nanorods. The size and morphology of the ZnO nanorods can be controlled. The influence of the length of the nanorods on the cell properties is investigated. A vapour phase transport technique was also used as alternative growth method.

  16. Gas Sensing Studies of an n-n Hetero-Junction Array Based on SnO2 and ZnO Composites

    Directory of Open Access Journals (Sweden)

    Anupriya Naik

    2016-02-01

    Full Text Available A composite metal oxide semiconductor (MOS sensor array based on tin dioxide (SNO2 and zinc oxide (ZnO has been fabricated using a straight forward mechanical mixing method. The array was characterized using X-ray photoelectron spectroscopy, scanning electron microscopy, Raman spectroscopy and X-ray diffraction. The array was evaluated against a number of environmentally important reducing and oxidizing gases across a range of operating temperatures (300–500 °C. The highest response achieved was against 100 ppm ethanol by the 50 wt% ZnO–50 wt% SnO2 device, which exhibited a response of 109.1, a 4.5-fold increase with respect to the pure SnO2 counterpart (which displayed a response of 24.4 and a 12.3-fold enhancement with respect to the pure ZnO counterpart (which was associated with a response of 8.9, towards the same concentration of the analyte. Cross sensitivity studies were also carried out against a variety of reducing gases at an operating temperature of 300 °C. The sensors array showed selectivity towards ethanol. The enhanced behaviour of the mixed oxide materials was influenced by junction effects, composition, the packing structure and the device microstructure. The results show that it is possible to tune the sensitivity and selectivity of a composite sensor, through a simple change in the composition of the composite.

  17. Influence of Al doping on structural and optical properties of Mg–Al co-doped ZnO thin films prepared by sol–gel method

    International Nuclear Information System (INIS)

    Fang, Dongyu; Lin, Kui; Xue, Tao; Cui, Can; Chen, Xiaoping; Yao, Pei; Li, Huijun

    2014-01-01

    Highlights: • Mg–Al co-doped ZnO thin films were prepared by sol–gel spin coating method. • The effects of Al doping on structural and optical properties of AMZO thin films were investigated. • The EDS spectra confirmed presence of Mg and Al elements in AMZO thin films. • The optical band gap of AMZO thin films increased with Al doping concentration increased. • The origin of the photoluminescence emissions was discussed. -- Abstract: Mg–Al co-doped ZnO (AMZO) thin films were successfully deposited onto quartz glass substrates by sol–gel spin coating method. The structure, surface morphology, composition, optical transmittance, and photoluminescence properties of AMZO thin films were characterized through X-ray diffraction, scanning electron microscopy with energy dispersive X-ray spectroscopy (EDS), transmission electron microscopy, UV–VIS–NIR spectrophotometry, and fluorescence spectrophotometry. The results indicated that AMZO thin films exhibited preferred orientation growth along the c-axis, and the full width at half maximum of the (0 0 2) diffraction peak decreased first and subsequently increased, reaching a minimum of approximately 0.275° at 3% Al content. The calculated crystallite size increased from 30.21 nm to 40.73 nm. Al doping content increased from 1% to 3% and subsequently reached 19.33 nm for Al doping content at 5%. The change in lattice parameters was demonstrated by the c/a ratio, residual stress, bond length, and volume per unit cell. EDS analysis confirmed the presence of Mg and Al elements in ZnO thin films. The atomic percentage of Mg and Al elements was nearly equal to their nominal stoichiometry within the experimental error. In addition, the optical transmittance of AMZO thin films was over 85% in the visible region, and the optical band gap increased with increasing Al doping concentration. Room temperature photoluminescence showed ultraviolet emission peak and defect emission peak. The defect emission peak of

  18. Polycrystalline ZnO: B grown by LPCVD as TCO for thin film silicon solar cells

    International Nuclear Information System (INIS)

    Fay, Sylvie; Steinhauser, Jerome; Nicolay, Sylvain; Ballif, Christophe

    2010-01-01

    Conductive zinc oxide (ZnO) grown by low pressure chemical vapor deposition (LPCVD) technique possesses a rough surface that induces an efficient light scattering in thin film silicon (TF Si) solar cells, which makes this TCO an ideal candidate for contacting such devices. IMT-EPFL has developed an in-house LPCVD process for the deposition of nanotextured boron doped ZnO films used as rough TCO for TF Si solar cells. This paper is a general review and synthesis of the study of the electrical, optical and structural properties of the ZnO:B that has been performed at IMT-EPFL. The influence of the free carrier absorption and the grain size on the electrical and optical properties of LPCVD ZnO:B is discussed. Transport mechanisms at grain boundaries are studied. It is seen that high doping of the ZnO grains facilitates the tunnelling of the electrons through potential barriers that are located at the grain boundaries. Therefore, even if these potential barriers increase after an exposition of the film to a humid atmosphere, the heavily doped LPCVD ZnO:B layers show a remarkable stable conductivity. However, the introduction of diborane in the CVD reaction induces also a degradation of the intra-grain mobility and increases over-proportionally the optical absorption of the ZnO:B films. Hence, the necessity to finely tune the doping level of LPCVD ZnO:B films is highlighted. Finally, the next challenges to push further the optimization of LPCVD ZnO:B films for thin film silicon solar cells are discussed, as well as some remarkable record cell results achieved with LPCVD ZnO:B as front electrode.

  19. Growth of thin film containing high density ZnO nanorods with low temperature calcinated seed layer

    Science.gov (United States)

    Panda, Rudrashish; Samal, Rudranarayan; Khatua, Lizina; Das, Susanta Kumar

    2018-05-01

    In this work we demonstrate the growth of thin film containing high density ZnO nanorods by using drop casting of the seed layer calcinated at a low temperature of 132 °C. Chemical bath deposition (CBD) method is used to grow the nanorods. X-ray diffraction (XRD) analysis and Field Emission Scanning Electron Microscopy (FESEM) are performed for the structural and morphological characterizations of the nanorods. The average diameter and length of nanorods are found to be 33 nm and 270 nm respectively. The bandgap of the material is estimated to be 3.2 eV from the UV-Visible absorption spectroscopy. The reported method is much more cost-effective and can be used for growth of ZnO nanorods for various applications.

  20. Efficiency of Nb-Doped ZnO Nanoparticles Electrode for Dye-Sensitized Solar Cells Application

    Science.gov (United States)

    Anuntahirunrat, Jirapat; Sung, Youl-Moon; Pooyodying, Pattarapon

    2017-09-01

    The technological of Dye-sensitized solar cells (DSSCs) had been improved for several years. Due to its simplicity and low cost materials with belonging to the part of thin films solar cells. DSSCs have numerous advantages and benefits among the other types of solar cells. Many of the DSSC devices had use organic chemical that produce by specific method to use as thin film electrodes. The organic chemical that widely use to establish thin film electrodes are Zinc Oxide (ZnO), Titanium Dioxide (TiO2) and many other chemical substances. Zinc oxide (ZnO) nanoparticles had been used in DSSCs applications as thin film electrodes. Nanoparticles are a part of nanomaterials that are defined as a single particles 1-100 nm in diameter. From a few year ZnO widely used in DSSC applications because of its optical, electrical and many others properties. In particular, the unique properties and utility of ZnO structure. However the efficiency of ZnO nanoparticles based solar cells can be improved by doped various foreign impurity to change the structures and properties. Niobium (Nb) had been use as a dopant of metal oxide thin films. Using specification method to doped the ZnO nanoparticles thin film can improved the efficiencies of DSSCs. The efficiencies of Nb-doped ZnO can be compared by doping 0 at wt% to 5 at wt% in ZnO nanoparticles thin films that prepared by the spin coating method. The thin film electrodes doped with 3 at wt% represent a maximum efficiencies with the lowest resistivity of 8.95×10-4 Ω·cm.

  1. Analysis of optical band-gap shift in impurity doped ZnO thin films by using nonparabolic conduction band parameters

    International Nuclear Information System (INIS)

    Kim, Won Mok; Kim, Jin Soo; Jeong, Jeung-hyun; Park, Jong-Keuk; Baik, Young-Jun; Seong, Tae-Yeon

    2013-01-01

    Polycrystalline ZnO thin films both undoped and doped with various types of impurities, which covered the wide carrier concentration range of 10 16 –10 21 cm −3 , were prepared by magnetron sputtering, and their optical-band gaps were investigated. The experimentally measured optical band-gap shifts were analyzed by taking into account the carrier density dependent effective mass determined by the first-order nonparabolicity approximation. It was shown that the measured shifts in optical band-gaps in ZnO films doped with cationic dopants, which mainly perturb the conduction band, could be well represented by theoretical estimation in which the band-gap widening due to the band-filling effect and the band-gap renormalization due to the many-body effect derived for a weakly interacting electron-gas model were combined and the carrier density dependent effective mass was incorporated. - Highlights: ► Optical band-gaps of polycrystalline ZnO thin films were analyzed. ► Experimental carrier concentration range covered from 10 16 to 10 21 cm −3 . ► Nonparabolic conduction band parameters were used in theoretical analysis. ► The band-filling and the band-gap renormalization effects were considered. ► The measured optical band-gap shifts corresponded well with the calculated ones

  2. TiN/Al2O3/ZnO gate stack engineering for top-gate thin film transistors by combination of post oxidation and annealing

    Science.gov (United States)

    Kato, Kimihiko; Matsui, Hiroaki; Tabata, Hitoshi; Takenaka, Mitsuru; Takagi, Shinichi

    2018-04-01

    Control of fabrication processes for a gate stack structure with a ZnO thin channel layer and an Al2O3 gate insulator has been examined for enhancing the performance of a top-gate ZnO thin film transistor (TFT). The Al2O3/ZnO interface and the ZnO layer are defective just after the Al2O3 layer formation by atomic layer deposition. Post treatments such as plasma oxidation, annealing after the Al2O3 deposition, and gate metal formation (PMA) are promising to improve the interfacial and channel layer qualities drastically. Post-plasma oxidation effectively reduces the interfacial defect density and eliminates Fermi level pinning at the Al2O3/ZnO interface, which is essential for improving the cut-off of the drain current of TFTs. A thermal effect of post-Al2O3 deposition annealing at 350 °C can improve the crystalline quality of the ZnO layer, enhancing the mobility. On the other hand, impacts of post-Al2O3 deposition annealing and PMA need to be optimized because the annealing can also accompany the increase in the shallow-level defect density and the resulting electron concentration, in addition to the reduction in the deep-level defect density. The development of the interfacial control technique has realized the excellent TFT performance with a large ON/OFF ratio, steep subthreshold characteristics, and high field-effect mobility.

  3. Title: Using Alignment and 2D Network Simulations to Study Charge Transport Through Doped ZnO Nanowire Thin Film Electrodes

    KAUST Repository

    Phadke, Sujay; Lee, Jung-Yong; West, Jack; Peumans, Peter; Salleo, Alberto

    2011-01-01

    of magnitude lower than the single nanowire resistance. Simulations suggest that the conductivity of such thin film devices could be further enhanced by using longer nanowires. Solution processed Gallium doped ZnO nanowires are aligned on substrates using

  4. Internal stress and opto-electronic properties of ZnO thin films deposited by reactive sputtering in various oxygen partial pressures

    Science.gov (United States)

    Tuyaerts, Romain; Poncelet, Olivier; Raskin, Jean-Pierre; Proost, Joris

    2017-10-01

    In this article, we propose ZnO thin films as a suitable material for piezoresistors in transparent and flexible electronics. ZnO thin films have been deposited by DC reactive magnetron sputtering at room temperature at various oxygen partial pressures. All the films have a wurtzite structure with a strong (0002) texture measured by XRD and are almost stoichiometric as measured by inductively coupled plasma optical emission spectroscopy. The effect of oxygen concentration on grain growth has been studied by in-situ multi-beam optical stress sensor, showing internal stress going from 350 MPa to -1.1 GPa. The transition between tensile and compressive stress corresponds to the transition between metallic and oxidized mode of reactive sputtering. This transition also induces a large variation in optical properties—from absorbent to transparent, and in the resistivity—from 4 × 10 - 2 Ω .cm to insulating. Finally, the piezoresistance of the thin film has been studied and showed a gauge factor (ΔR/R)/ɛ comprised between -5.8 and -8.5.

  5. The preparation of ZnO based gas-sensing thin films by ink-jet printing method

    International Nuclear Information System (INIS)

    Shen Wenfeng; Zhao Yan; Zhang Caibei

    2005-01-01

    An ink-jet printing technique was applied to prepare ZnO based gas-sensing thin films. ZnO inks with appropriate viscosity and surface tension were prepared by sol-gel techniques, and printed onto substrates using a commercial printer. After the drying and heating treatment processes, continuous ZnO films were formed and studied by scanning electron microscopy, X-ray diffraction and by a home-made gas sensitivity measuring system. It was found that the morphology and electrical properties of the films changed significantly with the thickness of the films, which can be adjusted simply by printing on the film with increasing frequency. Highest resistance and sensitivity to acetone vapor were obtained when the film was prepared by printing only once on it. Different dopants with certain concentrations could be added into the films by printing with different dopant inks and printing frequency. All Pd, Ag, and ZrO 2 dopants increased both the resistivity and the sensitivity of the films (180 ppm acetone). This work showed that the ink-jet printing technique was a convenient and low cost method to prepare films with controlled film thickness and dopant concentration

  6. Morphological, structural and optical properties of ZnO thin films deposited by dip coating method

    Energy Technology Data Exchange (ETDEWEB)

    Marouf, Sara; Beniaiche, Abdelkrim; Guessas, Hocine, E-mail: aziziamor@yahoo.fr [Laboratoire des Systemes Photoniques et Optiques Non Lineaires, Institut d' Optique et Mecanique de Precision, Universite Ferhat Abbas-Setif 1, Setif (Algeria); Azizi, Amor [Laboratoire de Chimie, Ingenierie Moleculaire et Nanostructures, Universite Ferhat Abbas-Setif 1, Setif (Algeria)

    2017-01-15

    Zinc oxide (ZnO) thin films were deposited on glass substrate by dip coating technique. The effects of sol aging time on the deposition of ZnO films was studied by using the field emission scanning electron microscopy (FE-SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), and optical transmission techniques. The morphology of the films strongly depends on preparation route and deposition technique. It is noteworthy that films deposited from the freshly prepared solution feature indistinct characteristics; had relatively poor crystalline quality and low optical transmittance in the visible region. The increase in sol aging time resulted in a gradual improvement in crystallinity (in terms of peak sharpness and peak intensity) of the hexagonal phase for all diffraction peaks. Effect of sol aging on optical transparency is quite obvious through increased transmission with prolonged sol aging time. Interestingly, 72-168 h sol aging time was found to be optimal to achieve smooth surface morphology, good crystallinity and high optical transmittance which were attributed to an ideal stability of solution. These findings present a better-defined and more versatile procedure for production of clean ZnO sols of readily adjustable nanocrystalline size. (author)

  7. Effects of ZnS layer on the performance improvement of the photosensitive ZnO nanowire arrays solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Javed, Hafiz Muhammad Asif [Electronic Materials Research Laboratory, International Center for Dielectric Research, Key Laboratory of the Ministry of Education, Xi' an Jiaotong University, Xi' an, 710049 (China); Que, Wenxiu, E-mail: wxque@mail.xjtu.edu.cn [Electronic Materials Research Laboratory, International Center for Dielectric Research, Key Laboratory of the Ministry of Education, Xi' an Jiaotong University, Xi' an, 710049 (China); Gao, Yanping; Xing, Yonglei [Electronic Materials Research Laboratory, International Center for Dielectric Research, Key Laboratory of the Ministry of Education, Xi' an Jiaotong University, Xi' an, 710049 (China); Kong, Ling Bing, E-mail: ELBKong@ntu.edu.sg [School of Materials Science and Engineering, Nanyang Technological University, Nanyang Avenue, 639798 (Singapore)

    2016-08-01

    The impact of ZnS layer as an interface modification on the photosensitive ZnO nanowire arrays solar cells was studied. CdS, CdSe and ZnS were deposited on ZnO nanowire arrays by SILAR method. When a ZnS layer was deposited, the quantum dot barrier was indirectly become in contact with the electrolyte, which thus restrained the flow of electrons. The CdS sensitized solar cells has an efficiency of 0.55% with the deposition of the ZnS(3) layer, that is, with a deposition of three times, whereas the CdS/CdSe co-sensitized solar cells has an efficiency of 2.03% with the deposition of the ZnS(1) layer. It was also noted that as the thickness of the of ZnS layer was increased, V{sub oc}, I{sub sc} and efficiencies of both the solar cells were first increased and then decreased. In addition, the CdS/N719 solar cells has an efficiency of 0.75% with the deposition of the ZnS(2) layer. - Highlights: • The impact of ZnS layer on the photosensitive ZnO nanowire solar cells was studied. • ZnS layer restrained the flow of electrons to the electrolyte. • CdS/CdSe co-sensitized solar cells have higher efficiency than CdS solar cells. • When ZnS layer was increased, V{sub oc} and I{sub sc} firstly increased and then decreased.

  8. Fabrication and characterization of nano-gas sensor arrays

    International Nuclear Information System (INIS)

    Hassan, H. S.; Kashyout, A. B.; Morsi, I.; Nasser, A. A. A.; Raafat, A.

    2015-01-01

    A novel structures of Nanomaterials gas sensors array constructed using ZnO, and ZnO doped with Al via sol-gel technique. Two structure arrays are developed; the first one is a double sensor array based on doping with percentages of 1% and 5%. The second is a quadrature sensor array based on several doping ratios concentrations (0%, 1%, 5% and 10%). The morphological structures of prepared ZnO were revealed using scanning electron microscope (SEM). X-ray diffraction (XRD) patterns reveal a highly crystallized wurtzite structure and used for identifying phase structure and chemical state of both ZnO and ZnO doped with Al under different preparation conditions and different doping ratios. Chemical composition of Al-doped ZnO nanopowders was performed using energy dispersive x-ray (EDS) analysis. The electrical characteristics of the sensor are determined by measuring the two terminal sensor’s output resistance for O 2 , H 2 and CO 2 gases as a function of temperature

  9. Fabrication and characterization of nano-gas sensor arrays

    Energy Technology Data Exchange (ETDEWEB)

    Hassan, H. S., E-mail: hassan.shokry@gmail.com; Kashyout, A. B., E-mail: hady8@yahoo.com [Electronic Materials Researches Department, Advanced Technology and New Materials Research Institute, City of Scientific Researches and technological applications, New Borg El-Arab City, Alexandria (Egypt); Morsi, I., E-mail: drimanmorsi@yahoo.com; Nasser, A. A. A., E-mail: menem-1954@yahoo.com; Raafat, A., E-mail: abrs-218@yahoo.com [Arab Academy for Science and Technology, and Maritime Transport, Alexandria, 21936 (Egypt)

    2015-03-30

    A novel structures of Nanomaterials gas sensors array constructed using ZnO, and ZnO doped with Al via sol-gel technique. Two structure arrays are developed; the first one is a double sensor array based on doping with percentages of 1% and 5%. The second is a quadrature sensor array based on several doping ratios concentrations (0%, 1%, 5% and 10%). The morphological structures of prepared ZnO were revealed using scanning electron microscope (SEM). X-ray diffraction (XRD) patterns reveal a highly crystallized wurtzite structure and used for identifying phase structure and chemical state of both ZnO and ZnO doped with Al under different preparation conditions and different doping ratios. Chemical composition of Al-doped ZnO nanopowders was performed using energy dispersive x-ray (EDS) analysis. The electrical characteristics of the sensor are determined by measuring the two terminal sensor’s output resistance for O{sub 2}, H{sub 2} and CO{sub 2} gases as a function of temperature.

  10. Research Update: Atmospheric pressure spatial atomic layer deposition of ZnO thin films: Reactors, doping, and devices

    Directory of Open Access Journals (Sweden)

    Robert L. Z. Hoye

    2015-04-01

    Full Text Available Atmospheric pressure spatial atomic layer deposition (AP-SALD has recently emerged as an appealing technique for rapidly producing high quality oxides. Here, we focus on the use of AP-SALD to deposit functional ZnO thin films, particularly on the reactors used, the film properties, and the dopants that have been studied. We highlight how these films are advantageous for the performance of solar cells, organometal halide perovskite light emitting diodes, and thin-film transistors. Future AP-SALD technology will enable the commercial processing of thin films over large areas on a sheet-to-sheet and roll-to-roll basis, with new reactor designs emerging for flexible plastic and paper electronics.

  11. Electrochemical fabrication of nanoporous polypyrrole thin films

    Energy Technology Data Exchange (ETDEWEB)

    Li Mei [Key Laboratory of Organic Optoelectronics and Molecular Engineering (Ministry of Education), Department of Chemistry, Tsinghua University, Beijing, 100084 (China); Yuan Jinying [Key Laboratory of Organic Optoelectronics and Molecular Engineering (Ministry of Education), Department of Chemistry, Tsinghua University, Beijing, 100084 (China)], E-mail: yuanjy@mail.tsinghua.edu.cn; Shi Gaoquan [Key Laboratory of Organic Optoelectronics and Molecular Engineering (Ministry of Education), Department of Chemistry, Tsinghua University, Beijing, 100084 (China)], E-mail: gshi@mail.tsinghua.edu.cn

    2008-04-30

    Polypyrrole thin films with pores in nanometer scale were synthesized by direct electrochemical oxidation of pyrrole in a mixed electrolyte of isopropyl alcohol, boron trifluoride diethyl etherate, sodium dodecylsulfonate and poly(ethylene glycol) using well-aligned ZnO nanowires arrays as templates. The thin films exhibit high conductivity of ca. {sigma}{sub rt} {approx} 20.5 s/cm and can be driven to bend during redox processes in 1.0 M lithium perchlorate aqueous solution. The movement rate of an actuator based on this nanoporous film was measured to be over 90{sup o}/s at a driving potential of 0.8 V (vs. Ag/AgCl)

  12. Electrochemical fabrication of nanoporous polypyrrole thin films

    International Nuclear Information System (INIS)

    Li Mei; Yuan Jinying; Shi Gaoquan

    2008-01-01

    Polypyrrole thin films with pores in nanometer scale were synthesized by direct electrochemical oxidation of pyrrole in a mixed electrolyte of isopropyl alcohol, boron trifluoride diethyl etherate, sodium dodecylsulfonate and poly(ethylene glycol) using well-aligned ZnO nanowires arrays as templates. The thin films exhibit high conductivity of ca. σ rt ∼ 20.5 s/cm and can be driven to bend during redox processes in 1.0 M lithium perchlorate aqueous solution. The movement rate of an actuator based on this nanoporous film was measured to be over 90 o /s at a driving potential of 0.8 V (vs. Ag/AgCl)

  13. Three-dimensional mesoscale heterostructures of ZnO nanowire arrays epitaxially grown on CuGaO2 nanoplates as individual diodes.

    Science.gov (United States)

    Forticaux, Audrey; Hacialioglu, Salih; DeGrave, John P; Dziedzic, Rafal; Jin, Song

    2013-09-24

    We report a three-dimensional (3D) mesoscale heterostructure composed of one-dimensional (1D) nanowire (NW) arrays epitaxially grown on two-dimensional (2D) nanoplates. Specifically, three facile syntheses are developed to assemble vertical ZnO NWs on CuGaO2 (CGO) nanoplates in mild aqueous solution conditions. The key to the successful 3D mesoscale integration is the preferential nucleation and heteroepitaxial growth of ZnO NWs on the CGO nanoplates. Using transmission electron microscopy, heteroepitaxy was found between the basal planes of CGO nanoplates and ZnO NWs, which are their respective (001) crystallographic planes, by the observation of a hexagonal Moiré fringes pattern resulting from the slight mismatch between the c planes of ZnO and CGO. Careful analysis shows that this pattern can be described by a hexagonal supercell with a lattice parameter of almost exactly 11 and 12 times the a lattice constants for ZnO and CGO, respectively. The electrical properties of the individual CGO-ZnO mesoscale heterostructures were measured using a current-sensing atomic force microscopy setup to confirm the rectifying p-n diode behavior expected from the band alignment of p-type CGO and n-type ZnO wide band gap semiconductors. These 3D mesoscale heterostructures represent a new motif in nanoassembly for the integration of nanomaterials into functional devices with potential applications in electronics, photonics, and energy.

  14. Enhanced stimulated emission in ZnO thin films using microdisk top-down structuring

    Energy Technology Data Exchange (ETDEWEB)

    Nomenyo, K.; Kostcheev, S.; Lérondel, G. [Laboratoire de Nanotechnologie et d' Instrumentation Optique, Institut Charles Delaunay, CNRS UMR 6281, Université de Technologie de Troyes, 12 rue Marie Curie, CS 42060, 10004 Troyes Cedex (France); Gadallah, A.-S. [Laboratoire de Nanotechnologie et d' Instrumentation Optique, Institut Charles Delaunay, CNRS UMR 6281, Université de Technologie de Troyes, 12 rue Marie Curie, CS 42060, 10004 Troyes Cedex (France); Department of Laser Sciences and Interactions, National Institute of Laser Enhanced Sciences, Cairo University, Giza (Egypt); Rogers, D. J. [Nanovation, 8, route de Chevreuse, 78117 Châteaufort (France)

    2014-05-05

    Microdisks were fabricated in zinc oxide (ZnO) thin films using a top-down approach combining electron beam lithography and reactive ion etching. These microdisk structured thin films exhibit a stimulated surface emission between 3 and 7 times higher than that from a reference film depending on the excitation power density. Emission peak narrowing, reduction in lasing threshold and blue-shifting of the emission wavelength were observed along with enhancement in the emitted intensity. Results indicate that this enhancement is due to an increase in the internal quantum efficiency combined with an amplification of the stimulated emission. An analysis in terms of waveguiding is presented in order to explain these effects. These results demonstrate that very significant gains in emission can be obtained through conventional microstructuration without the need for more onerous top-down nanostructuration techniques.

  15. ZnO nanostructures as electron extraction layers for hybrid perovskite thin films

    Science.gov (United States)

    Nikolaidou, Katerina; Sarang, Som; Tung, Vincent; Lu, Jennifer; Ghosh, Sayantani

    Optimum interaction between light harvesting media and electron transport layers is critical for the efficient operation of photovoltaic devices. In this work, ZnO layers of different morphologies are implemented as electron extraction and transport layers for hybrid perovskite CH3NH3PbI3 thin films. These include nanowires, nanoparticles, and single crystalline film. Charge transfer at the ZnO/perovskite interface is investigated and compared through ultra-fast characterization techniques, including temperature and power dependent spectroscopy, and time-resolved photoluminescence. The nanowires cause an enhancement in perovskite emission, which may be attributed to increased scattering and grain boundary formation. However, the ZnO layers with decreasing surface roughness exhibit better electron extraction, as inferred from photoluminescence quenching, reduction in the number of bound excitons, and reduced exciton lifetime in CH3NH3PbI3 samples. This systematic study is expected to provide an understanding of the fundamental processes occurring at the ZnO-CH3NH3PbI3 interface and ultimately, provide guidelines for the ideal configuration of ZnO-based hybrid Perovskite devices. This research was supported by National Aeronautics and Space administration (NASA) Grant No: NNX15AQ01A.

  16. Negative permittivity of ZnO thin films prepared from aluminum and gallium doped ceramics via pulsed-laser deposition

    DEFF Research Database (Denmark)

    Bodea, M. A.; Sbarcea, G.; Naik, G. V.

    2013-01-01

    Aluminum and gallium doped zinc oxide thin films with negative dielectric permittivity in the near infrared spectral range are grown by pulsed laser deposition. Composite ceramics comprising ZnO and secondary phase Al2O3 or Ga2O3 are employed as targets for laser ablation. Films deposited on glass...

  17. Effect of Sn-doped on microstructural and optical properties of ZnO thin films deposited by sol-gel method

    International Nuclear Information System (INIS)

    Tsay, C.-Y.; Cheng, H.-C.; Tung, Y.-T.; Tuan, W.-H.; Lin, C.-K.

    2008-01-01

    In this study, transparent thin films of Sn-doped ZnO (ZnO:Sn) were deposited onto alkali-free glass substrates by a sol-gel method; the effect of Sn doping on crystallinity, microstructural and optical properties was investigated. The atomic percentages of dopant in ZnO-based sols were Sn/Zn = 0, 1, 2, 3, and 5 at.%. The as-deposited films were pre-heated at 300 deg. C for 10 min and then annealed in air at 500 deg. C for 1 h. The results show that Sn-doped ZnO thin films demonstrate obviously improved surface roughness, enhanced transmittance in the 400-600 nm wavelength range and reduced average crystallite size. Among all of the annealed ZnO-based films in this study, films doped with 2 at.% Sn concentration exhibited the best properties, namely an average transmittance of 90%, an RMS roughness value of 1.92 nm and a resistivity of 9.3 x 10 2 Ω-cm

  18. Fabrication of thin ZnO films with wide-range tuned optical properties by reactive magnetron sputtering

    Science.gov (United States)

    Davydova, A.; Tselikov, G.; Dilone, D.; Rao, K. V.; Kabashin, A. V.; Belova, L.

    2018-02-01

    We report the manufacturing of thin zinc oxide films by reactive magnetron sputtering at room temperature, and examine their structural and optical properties. We show that the partial oxygen pressure in DC mode can have dramatic effect on absorption and refractive index (RI) of the films in a broad spectral range. In particular, the change of the oxygen pressure from 7% to 5% can lead to either conventional crystalline ZnO films having low absorption and characteristic descending dependence of RI from 2.4-2.7 RIU in the visible to 1.8-2 RIU in the near-infrared (1600 nm) range, or to untypical films, composed of ZnO nano-crystals embedded into amorphous matrix, exhibiting unexpectedly high absorption in the visible-infrared region and ascending dependence of RI with values varying from 1.5 RIU in the visible to 4 RIU in the IR (1600 nm), respectively. Untypical optical characteristics in the second case are explained by defects in ZnO structure arising due to under-oxidation of ZnO crystals. We also show that the observed defect-related film structure remains stable even after annealing of films under relatively high temperatures (30 min under 450 °C). We assume that both types of films can be of importance for photovoltaic (as contact or active layers, respectively), as well as for chemical or biological sensing, optoelectronics etc.

  19. Laser-induced grating in ZnO

    DEFF Research Database (Denmark)

    Ravn, Jesper N.

    1992-01-01

    A simple approach for the calculation of self-diffraction in a thin combined phase and amplitude grating is presented. The third order nonlinearity, the electron-hole recombination time, and the ambipolar diffusion coefficient in a ZnO crystal are measured by means of laser-induced self-diffracti......A simple approach for the calculation of self-diffraction in a thin combined phase and amplitude grating is presented. The third order nonlinearity, the electron-hole recombination time, and the ambipolar diffusion coefficient in a ZnO crystal are measured by means of laser-induced self...

  20. Cu-Doped ZnO Thin Films Deposited by a Sol-Gel Process Using Two Copper Precursors: Gas-Sensing Performance in a Propane Atmosphere

    Directory of Open Access Journals (Sweden)

    Heberto Gómez-Pozos

    2016-01-01

    Full Text Available A study on the propane gas-sensing properties of Cu-doped ZnO thin films is presented in this work. The films were deposited on glass substrates by sol-gel and dip coating methods, using zinc acetate as a zinc precursor, copper acetate and copper chloride as precursors for doping. For higher sensitivity values, two film thickness values are controlled by the six and eight dippings, whereas for doping, three dippings were used, irrespective of the Cu precursor. The film structure was analyzed by X-ray diffractometry, and the analysis of the surface morphology and film composition was made through scanning electron microscopy (SEM and secondary ion mass spectroscopy (SIMS, respectively. The sensing properties of Cu-doped ZnO thin films were then characterized in a propane atmosphere, C3H8, at different concentration levels and different operation temperatures of 100, 200 and 300 °C. Cu-doped ZnO films doped with copper chloride presented the highest sensitivity of approximately 6 × 104, confirming a strong dependence on the dopant precursor type. The results obtained in this work show that the use of Cu as a dopant in ZnO films processed by sol-gel produces excellent catalysts for sensing C3H8 gas.

  1. ZnO nanorods arrays with Ag nanoparticles on the (002) plane derived by liquid epitaxy growth and electrodeposition process

    International Nuclear Information System (INIS)

    Yin Xingtian; Que Wenxiu; Shen Fengyu

    2011-01-01

    Well-aligned ZnO nanorods (NRs) arrays with Ag nanoparticles (NPs) on the (002) plane are obtained by combining a liquid epitaxy technique with an electrodeposition process. Cyclic voltammetry study is employed to understand the electrochemical behaviors of the electrodeposition system, and potentiostatic method is employed to deposit silver NPs on the ZnO NRs in the electrolyte with an Ag + concentration of 1 mM. X-ray diffraction analysis is used to study the crystalline properties of the as-prepared samples, and energy dispersive X-ray is adopted to confirm the composition at the surface of the deposited samples. Results indicate only a small quantity of silver can be deposited on the surface of the samples. Effect of the deposition potential and time on the morphological properties of the resultant Ag NPs/ZnO NRs are investigated in detail. Scanning electron microscopy images and transmission electron microscopy images indicate that the Ag NPs deposited on the (002) plane of the ZnO NRs with a large dispersion in diameter can be obtained by a single potentiostatic deposition process, while dense Ag NPs with a much smaller diameter dispersion on the top of the ZnO NRs, most of which locate on the conical tip of the ZnO NRs, can be obtained by a two-potentiostatic deposition process, The mechanism of this deposition process is also suggested.

  2. UV and visible photoluminescence emission intensity of undoped and In-doped ZnO thin film and photoresponsivity of ZnO:In/Si hetero-junction

    International Nuclear Information System (INIS)

    Zebbar, N.; Chabane, L.; Gabouze, N.; Kechouane, M.; Trari, M.; Aida, M.S.; Belhousse, S.; Hadj Larbi, F.

    2016-01-01

    Undoped zinc oxide (ZnO) and indium-doped (ZnO:In) thin films were grown at different temperatures (250–400 °C) on alkali-free borosilicate glass and n-Si (100) substrates by Ultrasonic Spray Pyrolysis method. The structural, compositional, optical and electrical properties of ZnO films were investigated by X-ray diffraction, Scanning Electron Microscopy, Rutherford Back Scattering Spectroscopy, Fourier Transform Infrared spectroscopy, photoluminescence (PL) and the four-point probe technique. The predominance of ultraviolet (UV) and blue emission intensities was found to be closely dependent on the resistivity of the film. The visible emission band (peaking at 432 nm) prevails for low film resistivity, ranging from 10 −2 to 1 Ω·cm. By contrast, for higher resistivity (> 1 Ω·cm), there is a predominance of the UV band (382 nm). The PL and photoresponsivity results of fabricated ZnO:In/n-Si(100) heterojunctions prepared at different temperatures are discussed. The maximum spectral response of the ZnO:8%In/Si heterojunction diode fabricated at 250 °C was about 80 mA/W at zero bias. The highlighted results are attractive for the optoelectronic applications. - Highlights: • Properties of ZnO thin films grown by Ultrasonic Spray Pyrolysis at 350 °C. • Photoluminescence emission intensity in undoped ZnO film: effect of the resistivity • Photoluminescence emission intensity of In-doped ZnO film is resistivity dependent. • The spectral response of ZnO:In/Si hetero-junction deposited in the range (250–400 °C)

  3. UV and visible photoluminescence emission intensity of undoped and In-doped ZnO thin film and photoresponsivity of ZnO:In/Si hetero-junction

    Energy Technology Data Exchange (ETDEWEB)

    Zebbar, N., E-mail: nacbar2003@yahoo.fr [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Chabane, L. [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Gabouze, N. [CRTSE, 02 Bd. Frantz Fanon, BP 140, Algiers (Algeria); Kechouane, M. [LCMS, Faculty of Physics, University of Sciences and Technology (USTHB), BP 32, El-Alia, Algiers (Algeria); Trari, M. [Laboratory of Storage and Valorization of Renewable Energies, Faculty of Chemistry (USTHB), BP 32, El-Alia, Algiers (Algeria); Aida, M.S. [LCM et Interface, Faculty of Sciences, University of Constantine, 25000 (Algeria); Belhousse, S. [CRTSE, 02 Bd. Frantz Fanon, BP 140, Algiers (Algeria); Hadj Larbi, F. [MEMS & Sensors, Division Microélectronique et Nanotechnologie, Centre de Développement des Technologies Avancées (CDTA), BP 17, Baba Hassen, Algiers (Algeria)

    2016-04-30

    Undoped zinc oxide (ZnO) and indium-doped (ZnO:In) thin films were grown at different temperatures (250–400 °C) on alkali-free borosilicate glass and n-Si (100) substrates by Ultrasonic Spray Pyrolysis method. The structural, compositional, optical and electrical properties of ZnO films were investigated by X-ray diffraction, Scanning Electron Microscopy, Rutherford Back Scattering Spectroscopy, Fourier Transform Infrared spectroscopy, photoluminescence (PL) and the four-point probe technique. The predominance of ultraviolet (UV) and blue emission intensities was found to be closely dependent on the resistivity of the film. The visible emission band (peaking at 432 nm) prevails for low film resistivity, ranging from 10{sup −2} to 1 Ω·cm. By contrast, for higher resistivity (> 1 Ω·cm), there is a predominance of the UV band (382 nm). The PL and photoresponsivity results of fabricated ZnO:In/n-Si(100) heterojunctions prepared at different temperatures are discussed. The maximum spectral response of the ZnO:8%In/Si heterojunction diode fabricated at 250 °C was about 80 mA/W at zero bias. The highlighted results are attractive for the optoelectronic applications. - Highlights: • Properties of ZnO thin films grown by Ultrasonic Spray Pyrolysis at 350 °C. • Photoluminescence emission intensity in undoped ZnO film: effect of the resistivity • Photoluminescence emission intensity of In-doped ZnO film is resistivity dependent. • The spectral response of ZnO:In/Si hetero-junction deposited in the range (250–400 °C)

  4. Three-dimensional carbon cloth-supported ZnO nanorod arrays as a binder-free anode for lithium-ion batteries

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Lanyan; Wang, Xin, E-mail: wangxin@scnu.edu.cn [South China Normal University, Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics (China); Yin, Fuxing [Synergy Innovation Institute of GDUT (China); Zhang, Chengwei [Hebei University of Technology, Research Institute for Energy Equipment Materials, Tianjin Key Laboratory of Materials Laminating Fabrication and Interface Control Technology (China); Gao, Jinwei; Liu, Junming [South China Normal University, Institute of Advanced Materials, South China Academy of Advanced Optoelectronics (China); Zhou, Guofu [South China Normal University, Institute of Electronic Paper Displays, South China Academy of Advanced Optoelectronics (China); Zhang, Yongguang, E-mail: yongguangzhang@hebut.edu.cn; Bakenov, Zhumabay [Synergy Innovation Institute of GDUT (China)

    2017-02-15

    Three-dimensional ZnO nanorod arrays on flexible high surface area carbon cloth were successfully synthesized and directly used as negative electrodes for lithium-ion batteries without using any binder additive. The structure and morphology of the as-prepared hybrid ZnO electrode were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and high-resolution transmission electron microscopy (HRTEM). When tested as anodes in a lithium cell, the hybrid electrode demonstrated a high discharge capacity along with excellent rate capability and good cycling stability, delivering a reversible capacity of 891 mAh g{sup −1} at the second cycle and retaining a capacity of 469 mAh g{sup −1} after 100 cycles.

  5. Dual role of boron in improving electrical performance and device stability of low temperature solution processed ZnO thin film transistors

    Energy Technology Data Exchange (ETDEWEB)

    Gandla, Srinivas; Gollu, Sankara Rao; Sharma, Ramakant; Sarangi, Venkateshwarlu; Gupta, Dipti, E-mail: diptig@iitb.ac.in [Plastic Electronics and Energy Laboratory (PEEL), Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay, Powai, Mumbai-400076 (India)

    2015-10-12

    In this paper, we have demonstrated the dual role of boron doping in enhancing the device performance parameters as well as the device stability in low temperatures (200 °C) sol-gel processed ZnO thin film transistors (TFTs). Our studies suggest that boron is able to act as a carrier generator and oxygen vacancy suppressor simultaneously. Boron-doped ZnO TFTs with 8 mol. % of boron concentration demonstrated field-effect mobility value of 1.2 cm{sup 2} V{sup −1} s{sup −1} and threshold voltage of 6.2 V, respectively. Further, these devices showed lower shift in threshold voltage during the hysteresis and bias stress measurements as compared to undoped ZnO TFTs.

  6. Influence of Codoping on the Optical Properties of ZnO Thin Films Synthesized on Glass Substrate by Chemical Bath Deposition Method

    Directory of Open Access Journals (Sweden)

    G. Shanmuganathan

    2014-01-01

    Full Text Available Fe and K simultaneously doped ZnO thin films Zn0.99 K0.01 (Fex O (x=1, 2, 3, and 4% were synthesized by chemical bath deposition method. The XRD investigation reveals that all the doped ZnO thin films are in hexagonal wurtzite crystal structure without impurity phases. With increase in Fe concentration, the growth of thin films along c axis is evident from the XRD which indicates the increase in intensity along (002 direction. The same is visible from the surface morphology which shows the formation of hexagonal structure for higher Fe concentration. The topography shows gradual variation with Fe incorporation. The optical energy band gap obtained from the transmittance spectrum decreases from 3.42 to 3.06 eV with increase in Fe concentration indicating the red shift and this trend is consistent with the earlier experimental results. The UV emission is centered around 3.59 eV. The optical constants such as refractive index, extinction coefficient, and absorption coefficient which are essential for the optoelectronic applications were also determined.

  7. Reliable and Damage-Free Estimation of Resistivity of ZnO Thin Films for Photovoltaic Applications Using Photoluminescence Technique

    Directory of Open Access Journals (Sweden)

    N. Poornima

    2013-01-01

    Full Text Available This work projects photoluminescence (PL as an alternative technique to estimate the order of resistivity of zinc oxide (ZnO thin films. ZnO thin films, deposited using chemical spray pyrolysis (CSP by varying the deposition parameters like solvent, spray rate, pH of precursor, and so forth, have been used for this study. Variation in the deposition conditions has tremendous impact on the luminescence properties as well as resistivity. Two emissions could be recorded for all samples—the near band edge emission (NBE at 380 nm and the deep level emission (DLE at ~500 nm which are competing in nature. It is observed that the ratio of intensities of DLE to NBE (/ can be reduced by controlling oxygen incorporation in the sample. - measurements indicate that restricting oxygen incorporation reduces resistivity considerably. Variation of / and resistivity for samples prepared under different deposition conditions is similar in nature. / was always less than resistivity by an order for all samples. Thus from PL measurements alone, the order of resistivity of the samples can be estimated.

  8. EDTA-assisted synthesis of rose-like ZnO architectures

    Energy Technology Data Exchange (ETDEWEB)

    Li, Zhen [Institute of Nanochemistry and Nanobiology, Shanghai University, Shanghai 201800 (China); Shanghai Applied Radiation Institute, Shanghai University, Shanghai 201800 (China); Fang, Yaoguo [Institute of Nanochemistry and Nanobiology, Shanghai University, Shanghai 201800 (China); Peng, Liwei; Wu, Minghong [Shanghai Applied Radiation Institute, Shanghai University, Shanghai 201800 (China); Pan, Dengyu

    2010-10-15

    Rose-like ZnO nanostructures were prepared by a low-temperature solution route with assistance of ethylenediaminetetraacetic acid disodium (EDTA-2Na). The morphology of ZnO nanostructures was found to change from nanowire arrays to rose- and tower-like architectures with increasing the molar ratio of EDTA-2Na/Zn{sup 2+}. Also, the shape evolution of ZnO nanostructures with time was observed from flat nanosheets to wrinkled nanosheets and to rose-like nanostructures. EDTA-2Na as a strong complexing agent was found to play a key role in the shape evolution. Photoluminescence spectra show that the rose-like ZnO architectures have more defects than the nanowire arrays. (copyright 2010 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim) (orig.)

  9. Structural characterization of ZnO thin films grown on various substrates by pulsed laser deposition

    Czech Academy of Sciences Publication Activity Database

    Novotný, Michal; Čížek, J.; Kužel, R.; Bulíř, Jiří; Lančok, Ján; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.; Anwand, W.; Brauer, G.

    2012-01-01

    Roč. 45, č. 22 (2012), 1-12 ISSN 0022-3727 R&D Projects: GA ČR(CZ) GAP108/11/0958; GA ČR GP202/09/P324 Institutional research plan: CEZ:AV0Z10100522 Keywords : ZnO thin film * pulsed laser deposition * x-ray diffraction positron implantation spectroscopy Subject RIV: BM - Solid Matter Physics ; Magnetism Impact factor: 2.528, year: 2012 http://dx.doi.org/10.1088/0022-3727/45/22/225101

  10. Effect of different solutions on electrochemical deposition of ZnO

    International Nuclear Information System (INIS)

    Asil, H.; Chinar, K.; Gur, E.; Tuzemen, S.

    2010-01-01

    ZnO thin films were grown by electrochemical deposition (ECD) onto indium tin oxide using different compounds such as Zn(NO 3 ) 2 , Zn(C 2 H 3 O 2 ) 2 , ZnCl 2 , Zn(ClO 4 ) 2 and different solvents such as dimethylsulfoxide (DMSO) and 18 M deionized water. Furthermore, solutions were prepared using different electrolytes and concentrations in order to determine the optimum deposition parameters of ZnO. All the grown films were characterized by X-ray diffraction, optical absorption and photoluminescence measurement techniques. It is indicated that films grown by using Zn(ClO 4 ) 2 show high crystallinity and optical quality. The X-ray diffraction analysis showed that ZnO thin films which were grown electrochemically in a non-aqueous solution (DMSO) prepared by Zn(ClO 4 ) 2 have highly c-axis preferential orientation. PL measurements showed that ZnO thin films grown in Zn(ClO 4 ) 2 indicates high quality emission characteristics compared to the thin films grown by other solutions

  11. The electrical properties of low pressure chemical vapor deposition Ga doped ZnO thin films depending on chemical bonding configuration

    Energy Technology Data Exchange (ETDEWEB)

    Jung, Hanearl [School of Electrical and Electronic Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 120-749 (Korea, Republic of); Kim, Doyoung [School of Electrical and Electronic Engineering, Ulsan College, 57 Daehak-ro, Nam-gu, Ulsan 680-749 (Korea, Republic of); Kim, Hyungjun, E-mail: hyungjun@yonsei.ac.kr [School of Electrical and Electronic Engineering, Yonsei University, 50 Yonsei-ro, Seodaemun-gu, Seoul 120-749 (Korea, Republic of)

    2014-04-01

    Highlights: • Undoped and Ga doped ZnO thin films were deposited using DEZ and TMGa. • Effects of Ga doping using TMGa in Ga doped ZnO were investigated. • Degraded properties from excessive doping were analyzed using chemical bondings. - Abstract: The electrical and chemical properties of low pressure chemical vapor deposition (LP-CVD) Ga doped ZnO (ZnO:Ga) films were systematically investigated using Hall measurement and X-ray photoemission spectroscopy (XPS). Diethylzinc (DEZ) and O{sub 2} gas were used as precursor and reactant gas, respectively, and trimethyl gallium (TMGa) was used as a Ga doping source. Initially, the electrical properties of undoped LP-CVD ZnO films depending on the partial pressure of DEZ and O{sub 2} ratio were investigated using X-ray diffraction (XRD) by changing partial pressure of DEZ from 40 to 140 mTorr and that of O{sub 2} from 40 to 80 mTorr. The resistivity was reduced by Ga doping from 7.24 × 10{sup −3} Ω cm for undoped ZnO to 2.05 × 10{sup −3} Ω cm for Ga doped ZnO at the TMG pressure of 8 mTorr. The change of electric properties of Ga doped ZnO with varying the amount of Ga dopants was systematically discussed based on the structural crystallinity and chemical bonding configuration, analyzed by XRD and XPS, respectively.

  12. An Enhanced UV-Vis-NIR an d Flexible Photodetector Based on Electrospun ZnO Nanowire Array/PbS Quantum Dots Film Heterostructure.

    Science.gov (United States)

    Zheng, Zhi; Gan, Lin; Zhang, Jianbing; Zhuge, Fuwei; Zhai, Tianyou

    2017-03-01

    ZnO nanostructure-based photodetectors have a wide applications in many aspects, however, the response range of which are mainly restricted in the UV region dictated by its bandgap. Herein, UV-vis-NIR sensitive ZnO photodetectors consisting of ZnO nanowires (NW) array/PbS quantum dots (QDs) heterostructures are fabricated through modified electrospining method and an exchanging process. Besides wider response region compared to pure ZnO NWs based photodetectors, the heterostructures based photodetectors have faster response and recovery speed in UV range. Moreover, such photodetectors demonstrate good flexibility as well, which maintain almost constant performances under extreme (up to 180°) and repeat (up to 200 cycles) bending conditions in UV-vis-NIR range. Finally, this strategy is further verified on other kinds of 1D nanowires and 0D QDs, and similar enhancement on the performance of corresponding photodetecetors can be acquired, evidencing the universality of this strategy.

  13. Simulation, fabrication and characterization of ZnO based thin film transistors grown by radio frequency magnetron sputtering.

    Science.gov (United States)

    Singh, Shaivalini; Chakrabarti, P

    2012-03-01

    We report the performance of the thin film transistors (TFTs) using ZnO as an active channel layer grown by radio frequency (RF) magnetron sputtering technique. The bottom gate type TFT, consists of a conventional thermally grown SiO2 as gate insulator onto p-type Si substrates. The X-ray diffraction patterns reveal that the ZnO films are preferentially orientated in the (002) plane, with the c-axis perpendicular to the substrate. A typical ZnO TFT fabricated by this method exhibits saturation field effect mobility of about 0.6134 cm2/V s, an on to off ratio of 102, an off current of 2.0 x 10(-7) A, and a threshold voltage of 3.1 V at room temperature. Simulation of this TFT is also carried out by using the commercial software modeling tool ATLAS from Silvaco-International. The simulated global characteristics of the device were compared and contrasted with those measured experimentally. The experimental results are in fairly good agreement with those obtained from simulation.

  14. Morphologies of Sol–Gel Derived Thin Films of ZnO Using Different Precursor Materials and their Nanostructures

    Directory of Open Access Journals (Sweden)

    Chandra Sudhir

    2007-01-01

    Full Text Available AbstractWe have shown that the morphological features of the sol–gel derived thin films of ZnO depend strongly on the choice of the precursor materials. In particular, we have used zinc nitrate and zinc acetate as the precursor materials. While the films using zinc acetate showed a smoother topography, those prepared by using zinc nitrate exhibited dendritic character. Both types of films were found to be crystalline in nature. The crystallite dimensions were confined to the nanoscale. The crystallite size of the nanograins in the zinc nitrate derived films has been found to be smaller than the films grown by using zinc acetate as the precursor material. Selected area electron diffraction patterns in the case of both the precursor material has shown the presence of different rings corresponding to different planes of hexagonal ZnO crystal structure. The results have been discussed in terms of the fundamental considerations and basic chemistry governing the growth kinetics of these sol–gel derived ZnO films with both the precursor materials.

  15. Resistive Switching Characteristics in Electrochemically Synthesized ZnO Films

    Directory of Open Access Journals (Sweden)

    Shuhan Jing

    2015-04-01

    Full Text Available The semiconductor industry has long been seeking a new kind of non-volatile memory technology with high-density, high-speed, and low-power consumption. This study demonstrated the electrochemical synthesis of ZnO films without adding any soft or hard templates. The effect of deposition temperatures on crystal structure, surface morphology and resistive switching characteristics were investigated. Our findings reveal that the crystallinity, surface morphology and resistive switching characteristics of ZnO thin films can be well tuned by controlling deposition temperature. A conducting filament based model is proposed to explain the switching mechanism in ZnO thin films.

  16. Smart chemical sensors using ZnO semiconducting thin films for freshness detection of foods and beverages

    Science.gov (United States)

    Nanto, Hidehito; Kobayashi, Toshiki; Dougami, Naganori; Habara, Masaaki; Yamamoto, Hajime; Kusano, Eiji; Kinbara, Akira; Douguchi, Yoshiteru

    1998-07-01

    The sensitivity of the chemical sensor, based on the resistance change of Al2O3-doped and SnO2-doped ZnO (ZnO:Al and ZnO:SnO2) thin film, is studied for exposure to various gases. It is found that the ZnO:Al and ZnO:Sn thin film chemical sensor has a high sensitivity and excellent selectivity for amine (TMA and DMA) gas and ethanol gas, respectively. The ZnO:Al (5.0 wt%) thin film chemical sensor which exhibit a high sensitivity for exposure to odors from rotten sea foods, such as salmon, sea bream, oyster, squid and sardine, responds to the freshness change of these sea foods. The ZnO:SnO2 (78 wt%) thin film chemical sensor which exhibit a high sensitivity for exposure to aroma from alcohols, such as wine, Japanese sake, and whisky, responds to the freshness change of these alcohols.

  17. An investigation on the In doping of ZnO thin films by spray pyrolysis

    Science.gov (United States)

    Mahesh, Devika; Kumar, M. C. Santhosh

    2018-04-01

    Indium doped zinc oxide (IGZO)thin films are gaining much interest owing to its commercial application as transparent conductive oxide thin films. In the current study thin films indium doped ZnO thin films have been deposited on glass substrates by chemical spray pyrolysis technique with an indium concentration of 1, 2.5 and 4% in Zinc source. The films show a peak shift in the X-Ray Diffraction patterns with varying indium doping concentration. The (101) peak was enhanced for the 2.5 % indium doped films and variation in grain size with the different doping levels was studied. The as-deposited films are uniform and shown high transparency (>90%) in the visible region. Average thicknesses of films are found to be 800nm, calculated using the envelope method. The film with 2.5 % of indium content was found to be highly conducting than the rest, since for the lower and higher concentrations the conductivity was possibly halted by the limit in carrier concentration and indium segregation in the grain boundaries respectively. The enhancement of mobility and carrier concentration was clearly seen in the optimum films.

  18. Resistive switching: An investigation of the bipolar–unipolar transition in Co-doped ZnO thin films

    International Nuclear Information System (INIS)

    Santos, Daniel A.A.; Zeng, Hao; Macêdo, Marcelo A.

    2015-01-01

    Highlights: • A purely bipolar behavior on a Co-doped ZnO thin film has been demonstrated. • We have shown what can happen if a unipolar test is performed in a purely bipolar device. • An explanation for how a sample can show a purely bipolar switching behavior was suggested. • An important open issue about resistive switching effect was put in debate. - Abstract: In order to investigate the resistive switching effect we built devices in a planar structure in which two Al contacts were deposited on the top of the film and separated by a small gap using a shadow mask. Therefore, two samples of 10% Co-doped ZnO thin films were sputtered on glass substrate. High resolution X-ray diffraction (HRXRD) revealed a highly c-axis oriented crystalline structure, without secondary phase. The high resolution scanning electron microscopy (HRSEM) showed a flat surface with good coverage and thickness about 300 nm. A Keithley 2425 semiconductor characterization system was used to perform the resistive switching tests in the bipolar and unipolar modes. Considering only the effect of compliance current (CC), the devices showed a purely bipolar behavior since an increase in CC did not induce a transition to unipolar behavior

  19. Sonicated sol–gel preparation of nanoparticulate ZnO thin films with various deposition speeds: The highly preferred c-axis (0 0 2) orientation enhances the final properties

    International Nuclear Information System (INIS)

    Malek, M.F.; Mamat, M.H.; Khusaimi, Z.; Sahdan, M.Z.; Musa, M.Z.; Zainun, A.R.; Suriani, A.B.; Md Sin, N.D.; Abd Hamid, S.B.; Rusop, M.

    2014-01-01

    Highlights: • Minimum stress of highly c-axis oriented ZnO was grown at suitable deposition speed. • The ZnO crystal orientation was influenced by strain/stress of the film. • Minimum stress/strain of ZnO film leads to lower defects. • Bandgap and defects were closely intertwined with strain/stress. • We report additional optical and electrical properties based on deposition speed. -- Abstract: Zinc oxide (ZnO) thin films have been deposited onto glass substrates at various deposition speeds by a sonicated sol–gel dip-coating technique. This work studies the effects of deposition speed on the crystallisation behaviour and optical and electrical properties of the resulting films. X-ray diffraction (XRD) analysis showed that thin films were preferentially oriented along the (0 0 2) c-axis direction of the crystal. The transformation sequence of strain and stress effects in ZnO thin films has also been studied. The films deposited at a low deposition speed exhibited a large compressive stress of 0.78 GPa, which decreased to 0.43 GPa as the deposition speed increased to 40 mm/min. Interestingly, the enhancement in the crystallinity of these films led to a significant reduction in compressive stress. All films exhibited an average transmittance of greater than 90% in the visible region, with absorption edges at ∼380 nm. The photoluminescence (PL) measurements indicated that the intensity of the emission peaks varied significantly with deposition speed. The optical band gap energy (E g ) was evaluated as 3.276–3.289 eV, which increased with decreasing compressive stress along the c-axis. The energy band gap of the resulting ZnO films was found to be strongly influenced by the preferred c-axis (0 0 2) orientation

  20. Improved electron injection in spin coated Alq3 incorporated ZnO thin film in the device for solution processed OLEDs

    Science.gov (United States)

    Dasi, Gnyaneshwar; Ramarajan, R.; Thangaraju, Kuppusamy

    2018-04-01

    We deposit tris-(8-hydroxyquinoline)aluminum (Alq3) incorporated zinc oxide (ZnO) thin films by spin coating method under the normal ambient. It showed the higher transmittance (90% at 550 nm) when compared to that (80% at 550 nm) of spin coated pure ZnO film. SEM studies show that the Alq3 incorporation in ZnO film also enhances the formation of small sized particles arranged in the network of wrinkles on the surface. XRD reveals the improved crystalline properties upon Alq3 inclusion. We fabricate the electron-only devices (EODs) with the structure of ITO/spin coated ZnO:Alq3 as ETL/Alq3 interlayer/LiF/Al. The device showed the higher electron current density of 2.75 mA/cm2 at 12V when compared to that (0.82 mA/cm2 at 12V) of the device using pure ZnO ETL. The device results show that it will be useful to fabricate the low-cost solution processed OLEDs for future lighting and display applications.

  1. Low temperature preparation of Ag-doped ZnO nanowire arrays for sensor and light-emitting diode applications

    Science.gov (United States)

    Lupan, O.; Viana, B.; Cretu, V.; Postica, V.; Adelung, R.; Pauporté, T.

    2016-02-01

    Transition metal doped-oxide semiconductor nanostructures are important to achieve enhanced and new properties for advanced applications. We describe the low temperature preparation of ZnO:Ag nanowire/nanorod (NW/NR) arrays by electrodeposition at 90 °C. The NWs have been characterized by SEM, EDX, transmittance and photoluminescence (PL) measurements. The integration of Ag in the crystal is shown. Single nanowire/nanorod of ZnO:Ag was integrated in a nanosensor structure leading to new and enhanced properties. The ultraviolet (UV) response of the nanosensor was investigated at room temperature. Experimental results indicate that ZnO:Ag (0.75 μM) nanosensor possesses faster response/recovery time and better response to UV light than those reported in literature. The sensor structure has been also shown to give a fast response for the hydrogen detection with improved performances compared to pristine ZnO NWs. ZnO:Ag nanowire/nanorod arrays electrochemically grown on p-type GaN single crystal layer is also shown to act as light emitter in LED structures. The emission wavelength is red-shifted compared to pristine ZnO NW array. At low Ag concentration a single UV-blue emission is found whereas at higher concentration of dopant the emission is broadened and extends up to the red wavelength range. Our study indicates that high quality ZnO:Ag NW/NR prepared at low temperature by electrodeposition can serve as building nanomaterials for new sensors and light emitting diodes (LEDs) structures with low-power consumption.

  2. Annealing Heat Treatment of ZnO Nanoparticles Grown on Porous Si Substrate Using Spin-Coating Method

    Directory of Open Access Journals (Sweden)

    K. A. Eswar

    2014-01-01

    Full Text Available ZnO nanoparticles were successfully deposited on porous silicon (PSi substrate using spin-coating method. In order to prepare PSi, electrochemical etching was employed to modify the Si surface. Zinc acetate dihydrate was used as a starting material in ZnO sol-gel solution preparation. The postannealing treatments were investigated on morphologies and photoluminescence (PL properties of the ZnO thin films. Field emission scanning electron microscopy (FESEM results indicate that the thin films composed by ZnO nanoparticles were distributed uniformly on PSi. The average sizes of ZnO nanoparticle increase with increasing annealing temperature. Atomic force microscopic (AFM analysis reveals that ZnO thin films annealed at 500°C had the smoothest surface. PL spectra show two peaks that completely correspond to nanostructured ZnO and PSi. These findings indicate that the ZnO nanostructures grown on PSi are promising for application as light emitting devices.

  3. Hydrogen absorption in thin ZnO films prepared by pulsed laser deposition

    OpenAIRE

    Meilkhova, O.; Čížek, J.; Lukáč,, F.; Vlček, M.; Novotný, M.; Bulíř, J.; Lančok, J.; Anwand, W.; Brauer, G.; Connolly, J.; McCarthy, E.; Krishnamurthy, S.; Mosnier, J.-P.

    2013-01-01

    ZnO films with thickness of ~80 nm were grown by pulsed laser deposition (PLD) on MgO (1 0 0) single crystal and amorphous fused silica (FS) substrates. Structural studies of ZnO films and a high quality reference ZnO single crystal were performed by slow positron implantation spectroscopy (SPIS). It was found that ZnO films exhibit significantly higher density of defects than the reference ZnO crystal. Moreover, the ZnO film deposited on MgO substrate exhibits higher concentration of defects...

  4. X-ray photoelectron spectroscopy study and thermoelectric properties of Al-doped ZnO thin films

    International Nuclear Information System (INIS)

    Li Li; Fang Liang; Zhou Xianju; Liu Ziyi; Zhao Liang; Jiang Sha

    2009-01-01

    In this paper, high quality Al-doped ZnO (AZO) thin films were prepared by direct current (DC) reactive magnetron sputtering using a Zn target (99.99%) containing Al of 1.5 wt.%. The films obtained were characterized by X-ray photoelectron spectroscopy (XPS) and thermoelectric measurements. The XPS results reveal that Zn and Al exist only in oxidized state, while there are dominant crystal lattice and rare adsorbed oxygen for O in the annealed AZO thin films. The studies of thermoelectric property show a striking thermoelectric effect in the AZO thin films. On the one hand, the thermoelectromotive and magnetothermoelectromotive forces increase linearly with increasing temperature difference (ΔT). On the other hand, the thermoelectric power (TEP) decreases with the electrical resistance of the sample. But the TEP increases with the increase of temperature below 300 K, and it nearly does not change around room temperature. The experimental results also demonstrate that the annealing treatment increases TEP, while the external magnetic field degrades TEP.

  5. Self-assembled ZnO agave-like nanowires and anomalous superhydrophobicity

    Energy Technology Data Exchange (ETDEWEB)

    Yang, Y H; Li, Z Y; Wang, B; Wang, C X; Chen, D H; Yang, G W [State Key Laboratory of Optoelectronic Materials and Technologies, School of Physics Science and Engineering, Zhongshan University, Guangzhou 510275 (China)

    2005-09-07

    Thin films of ZnO agave-like nanowires were prepared on amorphous carbon thin layers on silicon substrates using thermal chemical vapour transport and condensation without any metal catalysts. The unusual superhydrophobicity of the fabricated surface was measured; the water contact angle reaches 151.1 deg. On the basis of experimental and theoretical analyses, it appears likely that the biomimetic microcomposite and nanocomposite surfaces of the prepared thin films of ZnO agave-like nanowires are responsible for the excellent superhydrophobicity.

  6. Hybrid AC EL structures with thin protective ZnO film

    International Nuclear Information System (INIS)

    Tsvetkova, E; Dikov, H; Kolentsov, K; Yourukova, L; Zhechev, D; Steflekova, V

    2008-01-01

    Alternating current hybrid electroluminescent Al/SnO 2 /ZnS: Cu/ZnO/Al structures with blue emission have been prepared. In these ZnO films are used as protective layers. The optical properties of different RF magnetron sputtered ZnO films have been studied. The voltage - brightness characteristics of AC EL structures with a ZnO protective film and conventional structures with a TiO 2 protective layer are compared. The investigation shows that the brightness of the structures with a ZnO protective film is higher. The improved characteristics of these new hybrid structures could be used in preparing various systems for representation of permanent or variable light information

  7. The effect of different molarities of precursor Zn(NO3)2.6H2O to the growth of ZnO by solution-immersion deposited on ZnO seeded template

    International Nuclear Information System (INIS)

    Afaah, A N; Asib, N A M; Aadila, A; Eswar, K A; Mahmud, M R; Khusaimi, Z; Alrokayan, Salman A H; Khan, Haseeb A; Mohamed, R; Rusop, M

    2015-01-01

    ZnO films were grown on glass substrates by mist-atomization, with the growth temperature of 300 °C to form ZnO seeded template. The ZnO seeded template then undergo second deposition method, which is solution-immersion method to grow ZnO on the ZnO seeded template thin film. The thin films were immersed in different molarities of starting materials; which are zinc nitrate hexahydrate and HMTA. The molarities were varied from 0.05, 0.10, 0.20 and 0.40 M. As a control to the study, the ZnO seeded template which undergoes mist-atomization only, denoted as MA only is prepared for comparison studies to the other samples. The properties of the products were examined by photoluminescence (PL) spectrophotometer, Raman spectrophotometer, and ultraviolet-visible (UV-Vis) spectrophotometer. From the PL measurement, it shows that 0.40 M sample have highest UV emission and from Raman measurements, it was found that the sample immersed in 0.40 M precursor have high crystal quality. From UV-Vis measurements, sharp UV emission at ∼378 nm is observed and 0.40 M ZnO thin film shows a better absorption properties. (paper)

  8. Characterization of a new transparent-conducting material of ZnO doped ITO thin films

    Science.gov (United States)

    Ali, H. M.

    2005-11-01

    Thin films of indium tin oxide (ITO) doped with zinc oxide have the remarkable properties of being conductive yet still highly transparent in the visible and near-IR spectral ranges. The Electron beam deposi- tion technique is one of the simplest and least expensive ways of preparing. High-quality ITO thin films have been deposited on glass substrates by Electron beam evaporation technique. The effect of doping and substrate deposition temperature was found to have a significant effect on the structure, electrical and optical properties of ZnO doped ITO films. The average optical transmittance has been increased with in- creasing the substrate temperature. The maximum value of transmittance is greater than 84% in the visible region and 85% in the NIR region obtained for film with Zn/ITO = 0.13 at substrate temperature 200 °C. The dielectric constant, average excitation energy for electronic transitions (E o), the dispersion energy (E d), the long wavelength refractive index (n ), average oscillator wave length ( o) and oscillator strength S o for the thin films were determined and presented in this work.

  9. In-situ growth of ZnO nanowire arrays on the sensing electrode via a facile hydrothermal route for high-performance NO2 sensor

    Science.gov (United States)

    Chen, Xiangxiang; Shen, Yanbai; Zhang, Wei; Zhang, Jin; Wei, Dezhou; Lu, Rui; Zhu, Lijia; Li, Hansen; Shen, Yansong

    2018-03-01

    ZnO nanowire (ZNW) arrays were in-situ grown on the sensing electrode via a facile hydrothermal route for NO2 sensing application. ZNW arrays were prepared by a seed layer deposition on the surface of the sensing electrode using a dipping process in a Zn(CH3COO)2·2H2O ethanol solution followed by a seed growth using a hydrothermal route in the Zn(NO3)2·6H2O-HMTA (C6H12N4) system. The microstructural characterizations of the ZNW arrays by means of XRD, FESEM, TEM, FTIR and XPS showed that ZnO nanowires with the diameters of 80-90 nm and the lengths of 0.6-1 μm had a single crystal hexagonal wurtzite structure. Gas sensing properties demonstrated the response of the sensor based on the ZNW arrays was linearly proportional to the NO2 concentration in the range of 1-30 ppm with good reproducibility and selectivity. The maximum sensor response to NO2 was obtained at an operating temperature of 250 °C. The response and recovery times reduced rapidly with increasing the operating temperature. The growth mechanism and sensing mechanism of the ZNW arrays were discussed in accordance with the deposition of the seed layer and the modulation of the depletion layer, respectively.

  10. Electrodeposition of ZnO nano-wires lattices with a controlled morphology; Electrodepot de reseaux de nanofils de ZnO a morphologie controlee

    Energy Technology Data Exchange (ETDEWEB)

    Elias, J.; Tena-Zaera, R.; Katty, A.; Levy-Clement, C. [Centre National de la Recherche Scientifique (CNRS), Lab. de Chimie Metallurgique des Terres Rares, UPR 209, 94 - Thiais (France)

    2006-07-01

    In this work, it is shown that the electrodeposition is a changeable low cost method which allows, according to the synthesis conditions, to obtain not only plane thin layers of ZnO but different nano-structures too. In a first part, are presented the formation conditions of a compact thin layer of nanocrystalline ZnO electrodeposited on a conducing glass substrate. This layer plays a buffer layer role for the deposition of a lattice of ZnO nano-wires. The step of nano-wires nucleation is not only determined by the electrochemical parameters but by the properties of the buffer layer too as the grain sizes and its thickness. In this context, the use of an electrodeposition method in two steps allows to control the nano-wires length and diameter and their density. The morphology and the structural and optical properties of these nano-structures have been analyzed by different techniques as the scanning and transmission electron microscopy, the X-ray diffraction and the optical spectroscopy. These studies show that ZnO nano-structures are formed of monocrystalline ZnO nano-wires, presenting a great developed surface and a great optical transparency in the visible. These properties make ZnO a good material for the development of nano-structured photovoltaic cells as the extremely thin absorber cells (PV ETA) or those with dye (DSSC) which are generally prepared with porous polycrystalline TiO{sub 2}. Its replacement by a lattice of monocrystalline ZnO nano-wires allows to reduce considerably the number of grain boundaries and in consequence to improve the transport of the electrons. The results are then promising for the PV ETA cells with ZnO nano-wires. (O.M.)

  11. Preparation of thin hexagonal highly-ordered anodic aluminum oxide (AAO) template onto silicon substrate and growth ZnO nanorod arrays by electrodeposition

    Science.gov (United States)

    Chahrour, Khaled M.; Ahmed, Naser M.; Hashim, M. R.; Elfadill, Nezar G.; Qaeed, M. A.; Bououdina, M.

    2014-12-01

    In this study, anodic aluminum oxide (AAO) templates of Aluminum thin films onto Ti-coated silicon substrates were prepared for growth of nanostructure materials. Hexagonally highly ordered thin AAO templates were fabricated under controllable conditions by using a two-step anodization. The obtained thin AAO templates were approximately 70 nm in pore diameter and 250 nm in length with 110 nm interpore distances within an area of 3 cm2. The difference between first and second anodization was investigated in details by in situ monitoring of current-time curve. A bottom barrier layer of the AAO templates was removed during dropping the voltage in the last period of the anodization process followed by a wet etching using phosphoric acid (5 wt%) for several minutes at ambient temperature. As an application, Zn nanorod arrays embedded in anodic alumina (AAO) template were fabricated by electrodeposition. Oxygen was used to oxidize the electrodeposited Zn nanorods in the AAO template at 700 °C. The morphology, structure and photoluminescence properties of ZnO/AAO assembly were analyzed using Field-emission scanning electron microscope (FESEM), Energy dispersive X-ray spectroscopy (EDX), Atomic force microscope (AFM), X-ray diffraction (XRD) and photoluminescence (PL).

  12. Effects of array arrangements in nano-patterned thin film media

    International Nuclear Information System (INIS)

    El-Hilo, M.

    2010-01-01

    In this work, the effect of different arrays arrangements on the magnetic behaviour of patterned thin film media is simulated. The modeled films consist of 80x80 cobalt grains of uniform diameter (20 nm) distributed into two different array arrangement: hexagonal (triangular) or square arrays. In addition to that, for each array arrangement, two cases of anisotropy orientations, random and textured films are considered. For both array arrangements and media orientations, hysteresis loops at different array separation (d) were simulated. Predictions show that for closely packed films, the shearing effects on the magnetization loop are much larger for the square array arrangement than the hexagonal one. According to these predictions, the bit switching field distribution in interacting 2D systems is much narrower for the hexagonal array arrangement. This result could be very important for high-density magnetic recording where a narrow bit switching field distribution is required.

  13. Hierarchical core-shell structure of ZnO nanorod@NiO/MoO₂ composite nanosheet arrays for high-performance supercapacitors.

    Science.gov (United States)

    Hou, Sucheng; Zhang, Guanhua; Zeng, Wei; Zhu, Jian; Gong, Feilong; Li, Feng; Duan, Huigao

    2014-08-27

    A hierarchical core-shell structure of ZnO nanorod@NiO/MoO2 composite nanosheet arrays on nickel foam substrate for high-performance supercapacitors was constructed by a two-step solution-based method involving two hydrothermal processes followed by a calcination treatment. Compared to one composed of pure NiO/MoO2 composite nanosheets, the hierarchical core-shell structure electrode displays better pseudocapacitive behaviors in 2 M KOH, including high areal specific capacitance values of 1.18 F cm(-2) at 5 mA cm(-2) and 0.6 F cm(-2) at 30 mA cm(-2) as well as relatively good rate capability at high current densities. Furthermore, it also shows remarkable cycle stability, remaining at 91.7% of the initial value even after 4000 cycles at a current density of 10 mA cm(-2). The enhanced pseudocapacitive behaviors are mainly due to the unique hierarchical core-shell structure and the synergistic effect of combining ZnO nanorod arrays and NiO/MoO2 composite nanosheets. This novel hierarchical core-shell structure shows promise for use in next-generation supercapacitors.

  14. Non-vacuum, single-step conductive transparent ZnO patterning by ultra-short pulsed laser annealing of solution-deposited nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Lee, Daeho; Pan, Heng; Kim, Eunpa; Grigoropoulos, Costas P. [University of California, Department of Mechanical Engineering, Berkeley, CA (United States); Ko, Seung Hwan [Korea Advanced Institute of Science and Technology (KAIST), Department of Mechanical Engineering, Daejeon (Korea, Republic of); Park, Hee K. [AppliFlex LLC, Sunnyvale, CA (United States)

    2012-04-15

    A solution-processable, high-concentration transparent ZnO nanoparticle (NP) solution was successfully synthesized in a new process. A highly transparent ZnO thin film was fabricated by spin coating without vacuum deposition. Subsequent ultra-short-pulsed laser annealing at room temperature was performed to change the film properties without using a blanket high temperature heating process. Although the as-deposited NP thin film was not electrically conductive, laser annealing imparted a large conductivity increase and furthermore enabled selective annealing to write conductive patterns directly on the NP thin film without a photolithographic process. Conductivity enhancement could be obtained by altering the laser annealing parameters. Parametric studies including the sheet resistance and optical transmittance of the annealed ZnO NP thin film were conducted for various laser powers, scanning speeds and background gas conditions. The lowest resistivity from laser-annealed ZnO thin film was about 4.75 x 10{sup -2} {omega} cm, exhibiting a factor of 10{sup 5} higher conductivity than the previously reported furnace-annealed ZnO NP film and is even comparable to that of vacuum-deposited, impurity-doped ZnO films within a factor of 10. The process developed in this work was applied to the fabrication of a thin film transistor (TFT) device that showed enhanced performance compared with furnace-annealed devices. A ZnO TFT performance test revealed that by just changing the laser parameters, the solution-deposited ZnO thin film can also perform as a semiconductor, demonstrating that laser annealing offers tunability of ZnO thin film properties for both transparent conductors and semiconductors. (orig.)

  15. Growth of high-density ZnO nanorods on wood with enhanced photostability, flame retardancy and water repellency

    Energy Technology Data Exchange (ETDEWEB)

    Kong, Lizhuo; Tu, Kunkun; Guan, Hao [Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing 100091 (China); Wang, Xiaoqing, E-mail: wangxq@caf.ac.cn [Research Institute of Forestry New Technology, Chinese Academy of Forestry, Beijing 100091 (China); Research Institute of Wood Industry, Chinese Academy of Forestry, Beijing 100091 (China)

    2017-06-15

    Highlights: • ZnO nanorod arrays were deposited on the wood surface via a hydrothermal process. • The assembled ZnO nanorod arrays greatly enhanced the photostability of wood. • The treated wood can sustain direct exposure to flame with only minor smoldering. • The ZnO-coated wood modified with stearic acid showed a superhydrophobic surface. - Abstract: Zinc oxide (ZnO) nanorod arrays were successfully assembled on the wood surface in situ via a two-step process consisting of formation of ZnO seeds and subsequent crystal growth under hydrothermal conditions at a low temperature. The morphology and crystalline structure of the formed ZnO nanorods were studied by field-emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). Highly dense and uniform arrays of ZnO nanorods with well-defined hexagonal facets were generated on the wood surface by tuning the concentration of the ZnO growth solution during the hydrothermal treatment. Accelerated weathering tests indicated that the assembled ZnO nanorod arrays were highly protective against UV radiation and greatly enhanced the photostability of the coated wood. Meanwhile, the ZnO nanorod-coated wood can withstand continuous exposure to flame with only minor smoldering in contrast with the pristine wood catching fire easily and burning rapidly. Moreover, when further modified with low-surface-energy stearic acid, the ZnO nanorod decorated wood surface can be transformed into a superhydrophobic surface, with a water contact angle (CA) of ∼154°. Such ZnO nanorod-modified woods with enhanced photostability, flame retardancy and water repellency offer an interesting alternative to conventional wood preservation strategies, highlighting their potential applications in some novel wood products.

  16. Growth of high-density ZnO nanorods on wood with enhanced photostability, flame retardancy and water repellency

    International Nuclear Information System (INIS)

    Kong, Lizhuo; Tu, Kunkun; Guan, Hao; Wang, Xiaoqing

    2017-01-01

    Highlights: • ZnO nanorod arrays were deposited on the wood surface via a hydrothermal process. • The assembled ZnO nanorod arrays greatly enhanced the photostability of wood. • The treated wood can sustain direct exposure to flame with only minor smoldering. • The ZnO-coated wood modified with stearic acid showed a superhydrophobic surface. - Abstract: Zinc oxide (ZnO) nanorod arrays were successfully assembled on the wood surface in situ via a two-step process consisting of formation of ZnO seeds and subsequent crystal growth under hydrothermal conditions at a low temperature. The morphology and crystalline structure of the formed ZnO nanorods were studied by field-emission scanning electron microscopy (FE-SEM) and X-ray diffraction (XRD). Highly dense and uniform arrays of ZnO nanorods with well-defined hexagonal facets were generated on the wood surface by tuning the concentration of the ZnO growth solution during the hydrothermal treatment. Accelerated weathering tests indicated that the assembled ZnO nanorod arrays were highly protective against UV radiation and greatly enhanced the photostability of the coated wood. Meanwhile, the ZnO nanorod-coated wood can withstand continuous exposure to flame with only minor smoldering in contrast with the pristine wood catching fire easily and burning rapidly. Moreover, when further modified with low-surface-energy stearic acid, the ZnO nanorod decorated wood surface can be transformed into a superhydrophobic surface, with a water contact angle (CA) of ∼154°. Such ZnO nanorod-modified woods with enhanced photostability, flame retardancy and water repellency offer an interesting alternative to conventional wood preservation strategies, highlighting their potential applications in some novel wood products.

  17. Effect of growth temperature on photoluminescence and piezoelectric characteristics of ZnO nanowires

    Energy Technology Data Exchange (ETDEWEB)

    Water, Walter [Institute of Electro-Optical and Materials Science, National Formosa University, Yunlin 632, Taiwan (China); Fang, T.-H. [Institute of Electro-Optical and Materials Science, National Formosa University, Yunlin 632, Taiwan (China); Institute of Mechanical and Electromechanical Engineering, National Formosa University, Yunlin 632, Taiwan (China)], E-mail: fang.tehua@msa.hinet.net; Ji, L.-W.; Lee, C.-C. [Institute of Electro-Optical and Materials Science, National Formosa University, Yunlin 632, Taiwan (China)

    2009-02-25

    ZnO nanowire arrays were synthesized on Au-coated silicon (1 0 0) substrates by using vapour-liquid-solid process in this work. The effect of growth temperatures on the crystal structure and the surface morphology of ZnO nanowires were investigated by X-ray diffraction and scanning electron microscope. The absorption and optical characteristics of the nanowires were examined by Ultraviolet/Visible spectroscopy, and photoluminescence, respectively. The photoluminescence results exhibited ZnO nanowires had an ultraviolet and blue emission at 383 and 492 nm. Then a nanogenerator with ZnO nanowire arrays was fabricated and demonstrated Schottky-like current-voltage characteristics.

  18. Area-Selective ZnO Thin Film Deposition on Variable Microgap Electrodes and Their Impact on UV Sensing

    Directory of Open Access Journals (Sweden)

    Q. Humayun

    2013-01-01

    Full Text Available ZnO thin films were deposited on patterned gold electrodes using the sol-gel spin coating technique. Conventional photolithography process was used to obtain the variable microgaps of 30 and 43 μm in butterfly topology by using zero-gap chrome mask. The structural, morphological, and electrical properties of the deposited thin films were characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, and Keithley SourceMeter, respectively. The current-voltage (I-V characterization was performed to investigate the effect of UV light on the fabricated devices. The ZnO fabricated sensors showed a photo to dark current (Iph/Id ratios of 6.26 for 30 μm and 5.28 for 43 μm gap electrodes spacing, respectively. Dynamic responses of both fabricated sensors were observed till 1V with good reproducibility. At the applied voltage of 1 V, the response time was observed to be 4.817 s and 3.704 s while the recovery time was observed to be 0.3738 s and 0.2891 s for 30 and 43 μm gaps, respectively. The signal detection at low operating voltages suggested that the fabricated sensors could be used for miniaturized devices with low power consumption.

  19. Fabrication of the heterojunction diode from Y-doped ZnO thin films on p-Si substrates by sol-gel method

    Science.gov (United States)

    Sharma, Sanjeev K.; Singh, Satendra Pal; Kim, Deuk Young

    2018-02-01

    The heterojunction diode of yttrium-doped ZnO (YZO) thin films was fabricated on p-Si(100) substrates by sol-gel method. The post-annealing process was performed at 600 °C in vacuum for a short time (3 min) to prevent inter-diffusion of Zn, Y, and Si atoms. X-ray diffraction (XRD) pattern of as-grown and annealed (600 °C in vacuum) films showed the preferred orientation along the c-axis (002) regardless of dopant concentrations. The uniform surface microstructure and the absence of other metal/oxide peaks in XRD pattern confirmed the excellence of films. The increasing bandgap and carrier concentration of YZO thin films were interpreted by the BM shift, that is, the Fermi level moves towards the conduction band edge. The current-voltage characteristics of the heterojunction diode, In/n-ZnO/p-Si/Al, showed a rectification behavior. The turn-on voltage and ideality factor of n-ZnO/p-Si and n-YZO/p-Si were observed to be 3.47 V, 2.61 V, and 1.97, 1.89, respectively. Y-dopant in ZnO thin films provided more donor electrons caused the shifting of Fermi-energy level towards the conduction band and strengthen the interest for heterojunction diodes.

  20. Influence Al doped ZnO nanostructure on structural and optical properties

    International Nuclear Information System (INIS)

    Ramelan, Ari Handono; Wahyuningsih, Sayekti; Chasanah, Uswatul; Munawaroh, Hanik

    2016-01-01

    The preparation of Al-doped ZnO (AZO) thin films prepared by the spin-coating method was reported. Preparation of AZO was conducted by annealing treatment at a temperature of 700°C. While the spin-coating process of AZO thin films were done at 2000 and 3000 rpm respectively. The structural properties of ZnO were determined by X- ray diffraction (XRD) analysis. ZnOnanostructure was formed after annealed at atemperature of 400°C.The morphology of ZnO was determined by Scanning Electron Microscopy (SEM) showed the irregular morphology about 30-50µm in size. Al doped on ZnO influenced the optical properties of those material. Increasing Al contain on ZnO cause of shifting to the lower wavelength. The optical properties of the ZnO as well as AZO films showed that higher reflectance on the ultraviolet region so those materials were used as anti-reflecting agent.Al addition significantly enhance the optical transparency and induce the blue-shift in optical bandgap of ZnO films.

  1. Structural and optical properties of Na-doped ZnO films

    Science.gov (United States)

    Akcan, D.; Gungor, A.; Arda, L.

    2018-06-01

    Zn1-xNaxO (x = 0.0-0.05) solutions have been synthesized by the sol-gel technique using Zinc acetate dihydrate and Sodium acetate which were dissolved into solvent and chelating agent. Na-doped ZnO nanoparticles were obtained from solutions to find phase and crystal structure. Na-doped ZnO films have been deposited onto glass substrate by using sol-gel dip coating system. The effects of dopant concentration on the structure, morphology, and optical properties of Na-doped ZnO thin films deposited on glass substrate are investigated. Characterization of Zn1-xNaxO nanoparticles and thin films are examined using differential thermal analysis (DTA)/thermogravimetric analysis (TGA), Scanning electron microscope (SEM) and X-Ray diffractometer (XRD). Optical properties of Zn1-xNaxO thin films were obtained by using PG Instruments UV-Vis-NIR spectrophotometer in 190-1100 nm range. The structure, morphology, and optical properties of thin films are presented.

  2. ZnO nanostructures induced by microwave plasma

    Directory of Open Access Journals (Sweden)

    Khaled A. Elsayed

    2015-07-01

    Full Text Available Microwave induced hydrogen plasma is used to fabricate ZnO thin films at low ambient gas pressure and controlled oxygen content in the gas mixture. The emission spectra have been observed. Optical emission spectroscopy was used to identify the chemical reaction mechanism. Structural quality of the so-obtained nanoparticles was studied by X-ray diffraction (XRD and high resolution scanning electron microscopy (SEM. SEM results showed that nanorods were formed in the process, and XRD results along with nanorod dimensions obtained from SEM are consistent with the formation of single and poly-crystalline ZnO nanorods. The alignment of these nanorods with respect to the substrates depends on the lattice mismatch between ZnO and the glass substrate. The minimum crystallite grain size as obtained from the SEM measurements was ∼24 nm and the average diameter is 70 nm with a length of 1–2 μm. The deposited ZnO thin films have a wide energy band gap that equals ∼3 eV.

  3. Catalytic growth of ZnO nanostructures by r.f. magnetron sputtering

    Directory of Open Access Journals (Sweden)

    Arroyo-Hernández María

    2011-01-01

    Full Text Available Abstract The catalytic effect of gold seed particles deposited on a substrate prior to zinc oxide (ZnO thin film growth by magnetron sputtering was investigated. For this purpose, selected ultra thin gold layers, with thicknesses close to the percolation threshold, are deposited by thermal evaporation in ultra high vacuum (UHV conditions and subsequently annealed to form gold nanodroplets. The ZnO structures are subsequently deposited by r.f. magnetron sputtering in a UHV chamber, and possible morphological differences between the ZnO grown on top of the substrate and on the gold are investigated. The results indicate a moderate catalytic effect for a deposited gold underlayer of 4 nm, quite close to the gold thin film percolation thickness.

  4. Electrical properties of ZnO thin films grown by MOCVD

    Energy Technology Data Exchange (ETDEWEB)

    Pagni, O. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Somhlahlo, N.N. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Weichsel, C. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa); Leitch, A.W.R. [Department of Physics, Nelson Mandela Metropolitan University, P.O. Box 77000, Port Elizabeth 6031 (South Africa)]. E-mail: andrew.leitch@nmmu.ac.za

    2006-04-01

    We report on the electrical characterization of ZnO films grown by MOCVD on glass and sapphire substrates. After correcting our temperature variable Hall measurements by applying the standard two-layer model, which takes into account an interfacial layer, scattering mechanisms in the ZnO films were studied as well as donor activation energies determined. ZnO films grown at different oxygen partial pressures indicated the importance of growth conditions on the defect structure by means of their conductivities and conductivity activation energies.

  5. Electrical properties of ZnO thin films grown by MOCVD

    International Nuclear Information System (INIS)

    Pagni, O.; Somhlahlo, N.N.; Weichsel, C.; Leitch, A.W.R.

    2006-01-01

    We report on the electrical characterization of ZnO films grown by MOCVD on glass and sapphire substrates. After correcting our temperature variable Hall measurements by applying the standard two-layer model, which takes into account an interfacial layer, scattering mechanisms in the ZnO films were studied as well as donor activation energies determined. ZnO films grown at different oxygen partial pressures indicated the importance of growth conditions on the defect structure by means of their conductivities and conductivity activation energies

  6. 3D highly oriented nanoparticulate and microparticulate array of metal oxide materials

    International Nuclear Information System (INIS)

    Vayssieres, Lionel; Guo, Jinghua; Nordgren, Joseph

    2006-01-01

    Advanced nano and micro particulate thin films of 3d transition and post-transition metal oxides consisting of nanorods and microrods with parallel and perpendicular orientation with respect to the substrate normal, have been successfully grown onto various substrates by heteronucleation, without template and/or surfactant, from the aqueous condensation of solution of metal salts or metal complexes (aqueous chemical growth). Three-dimensional arrays of iron oxide nanorods and zinc oxide nanorods with parallel and perpendicular orientation are presented as well as the oxygen K-edge polarization dependent x-ray absorption spectroscopy (XAS) study of anisotropic perpendicularly oriented microrod array of ZnO performed at synchrotron radiation source facility

  7. Luminescence properties of ZnO layers grown on Si-on-insulator substrates

    International Nuclear Information System (INIS)

    Kumar, Bhupendra; Gong, Hao; Vicknesh, S.; Chua, S. J.; Tripathy, S.

    2006-01-01

    The authors report on the photoluminescence properties of polycrystalline ZnO thin films grown on compliant silicon-on-insulator (SOI) substrates by radio frequency magnetron sputtering. The ZnO thin films on SOI were characterized by micro-Raman and photoluminescence (PL) spectroscopy. The observation of E 2 high optical phonon mode near 438 cm -1 in the Raman spectra of the ZnO samples represents the wurtzite crystal structure. Apart from the near-band-edge free exciton (FX) transition around 3.35 eV at 77 K, the PL spectra of such ZnO films also showed a strong defect-induced violet emission peak in the range of 3.05-3.09 eV. Realization of such ZnO layers on SOI would be useful for heterointegration with SOI-based microelectronics and microelectromechanical systems

  8. Studies on acetone sensing characteristics of ZnO thin film prepared by sol–gel dip coating

    Energy Technology Data Exchange (ETDEWEB)

    Muthukrishnan, Karthika; Vanaraja, Manoj [School of Electrical & Electronics Engineering, SASTRA University, Thanjavur, 613401 (India); Boomadevi, Shanmugam [Department of Physics, National Institute of Technology, Tiruchirappalli, 620015 (India); Karn, Rakesh Kumar [School of Electrical & Electronics Engineering, SASTRA University, Thanjavur, 613401 (India); Singh, Vijay [Department of Chemical Engineering, Konkuk University, Seoul, 143-701 (Korea, Republic of); Singh, Pramod K. [Solar Energy Institute, Ege University, Bornova, 35100, Izmir (Turkey); Material Research Laboratory, School of Basic Sciences and Research, Sharda University, Greater Noida, 201310, U. P. (India); Pandiyan, Krishnamoorthy, E-mail: krishpandiyan@ece.sastra.edu [School of Electrical & Electronics Engineering, SASTRA University, Thanjavur, 613401 (India)

    2016-07-15

    Acetone sensing characteristics of Zinc Oxide thin films prepared by dip coating method are discussed in this paper. The sol for dip coating was synthesized using Zinc nitrate hexahydrate (Zn (NO{sub 3}){sub 2}. 6H{sub 2}O) and organic polymer sodium carboxy methyl cellulose (Na-CMC) as a starting material. Crystallinity and crystallite size of the prepared thin film was characterised by X-ray diffraction (XRD). Morphology was studied using field emission scanning electron microscopy (FESEM). The gas sensing characteristics was studied using chemiresistive method, by exposing the film to various concentrations of acetone at room temperature. Further, for comparative study ethanol and acetaldehyde has also been tested. Gas sensing parameters such us response, selectivity, lowest detection limit, response/recovery time of the thin film towards acetone were also reported. - Highlights: • ZnO has successfully synthesized using cheap and ease method. • Detail characterization have carried out and explained. • Sensing behaviour has been studied. • Acetone sensor has been fabricated.

  9. ZnO nanocrystals and allied materials

    CERN Document Server

    Okada, Tatsuo

    2014-01-01

    ZnO has been the central theme of research in the past decade due to its various applications in band gap engineering, and textile and biomedical industries. In nanostructured form, it offers ample opportunities to realize tunable optical and optoelectronic properties and it was also termed as a potential material to realize room temperature ferromagnetism. This book presents 17 high-quality contributory chapters on ZnO related systems written by experts in this field. These chapters will help researchers to understand and explore the varied physical properties to envisage device applications of ZnO in thin film, heterostructure and nanostructure forms.

  10. Room temperature inorganic polycondensation of oxide (Cu2O and ZnO) nanoparticles and thin films preparation by the dip-coating technique

    International Nuclear Information System (INIS)

    Salek, G.; Tenailleau, C.; Dufour, P.; Guillemet-Fritsch, S.

    2015-01-01

    Oxide thin solid films were prepared by dip-coating into colloidal dispersions of oxide nanoparticles stabilized at room temperature without the use of chelating or complex organic dispersing agents. Crystalline oxide nanoparticles were obtained by inorganic polycondensation and characterized by X-ray diffraction and field emission gun scanning electron microscopy. Water and ethanol synthesis and solution stabilization of oxide nanoparticle method was optimized to prepare two different structural and compositional materials, namely Cu 2 O and ZnO. The influence of hydrodynamic parameters over the particle shape and size is discussed. Spherical and rod shape nanoparticles were formed for Cu 2 O and ZnO, respectively. Isoelectric point values of 7.5 and 8.2 were determined for cuprous and zinc oxides, respectively, after zeta potential measurements. A shear thinning and thixotropic behavior was observed in both colloidal sols after peptization at pH ~ 6 with dilute nitric acid. Every colloidal dispersion stabilized in a low cost and environmentally friendly azeotrope solution composed of 96 vol.% of ethanol with water was used for the thin film preparation by the dip-coating technique. Optical properties of the light absorber cuprous oxide and transparent zinc oxide thin solid films were characterized by means of transmittance and reflectance measurements (300–1100 nm). - Highlights: • Room temperature inorganic polycondensation of crystalline oxides • Water and ethanol synthesis and solution stabilization of oxide nanoparticles • Low cost method for thin solid film preparation

  11. Temperature-dependent photoluminescence analysis of ZnO nanowire array annealed in air

    Science.gov (United States)

    Sun, Yanan; Gu, Xiuquan; Zhao, Yulong; Wang, Linmeng; Qiang, Yinghuai

    2018-05-01

    ZnO nanowire arrays (NWAs) were prepared on transparent conducting fluorine doped tin oxide (FTO) substrates through a facile hydrothermal method, followed by a 500 °C annealing to improve their crystalline qualities and photoelectrochemical (PEC) activities. It was found that the annealing didn't change the morphology, but resulted in a significant reduction of the donor concentration. Temperature-dependent photoluminescence (PL) was carried out for a comprehensive analysis of the effect from annealing. Noteworthy, four dominant peaks were identified from the 10 K spectrum of a 500 °C annealed sample, and they were assigned to FX, D0X, (e, D0) and (e, D0) -1LO, respectively. Of them, the FX emission was only existed below 130 K, while the room-temperature (RT) PL spectrum was dominated by the D0X emission.

  12. Epitaxial growth of Sb-doped nonpolar a-plane ZnO thin films on r-plane sapphire substrates by RF magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Chen, Hou-Guang, E-mail: houguang@isu.edu.tw [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China); Hung, Sung-Po [Department of Materials Science and Engineering, I-Shou University, Kaohsiung 840, Taiwan (China)

    2014-02-15

    Highlights: ► Sb-doped nonpolar a-plane ZnO layers were epitaxially grown on sapphire substrates. ► Crystallinity and electrical properties were studied upon growth condition and doping concentration. ► The out-of-plane lattice spacing of ZnO films reduces monotonically with increasing Sb doping level. ► The p-type conductivity of ZnO:Sb film is closely correlated with annealing condition and Sb doping level. -- Abstract: In this study, the epitaxial growth of Sb-doped nonpolar a-plane (112{sup ¯}0) ZnO thin films on r-plane (11{sup ¯}02) sapphire substrates was performed by radio-frequency magnetron sputtering. The influence of the sputter deposition conditions and Sb doping concentration on the microstructural and electrical properties of Sb-doped ZnO epitaxial films was investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and the Hall-effect measurement. The measurement of the XRD phi-scan indicated that the epitaxial relationship between the ZnO:Sb layer and sapphire substrate was (112{sup ¯}0){sub ZnO}//(11{sup ¯}02){sub Al{sub 2O{sub 3}}} and [11{sup ¯}00]{sub ZnO}//[112{sup ¯}0]{sub Al{sub 2O{sub 3}}}. The out-of-plane a-axis lattice parameter of ZnO films was reduced monotonically with the increasing Sb doping level. The cross-sectional transmission electron microscopy (XTEM) observation confirmed the absence of any significant antimony oxide phase segregation across the thickness of the Sb-doped ZnO epitaxial film. However, the epitaxial quality of the films deteriorated as the level of Sb dopant increased. The electrical properties of ZnO:Sb film are closely correlated with post-annealing conditions and Sb doping concentrations.

  13. Porous Zinc Oxide Thin Films: Synthesis Approaches and Applications

    Directory of Open Access Journals (Sweden)

    Marco Laurenti

    2018-02-01

    Full Text Available Zinc oxide (ZnO thin films have been widely investigated due to their multifunctional properties, i.e., catalytic, semiconducting and optical. They have found practical use in a wide number of application fields. However, the presence of a compact micro/nanostructure has often limited the resulting material properties. Moreover, with the advent of low-dimensional ZnO nanostructures featuring unique physical and chemical properties, the interest in studying ZnO thin films diminished more and more. Therefore, the possibility to combine at the same time the advantages of thin-film based synthesis technologies together with a high surface area and a porous structure might represent a powerful solution to prepare ZnO thin films with unprecedented physical and chemical characteristics that may find use in novel application fields. Within this scope, this review offers an overview on the most successful synthesis methods that are able to produce ZnO thin films with both framework and textural porosities. Moreover, we discuss the related applications, mainly focused on photocatalytic degradation of dyes, gas sensor fabrication and photoanodes for dye-sensitized solar cells.

  14. Structure and morphology of magnetron sputter deposited ultrathin ZnO films on confined polymeric template

    Energy Technology Data Exchange (ETDEWEB)

    Singh, Ajaib [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Schipmann, Susanne [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Mathur, Aakash; Pal, Dipayan [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Sengupta, Amartya [Department of Physics, Indian Institute of Technology Delhi, Delhi 110016 (India); Klemradt, Uwe [II. Insatitute of Physics and JARA-FIT, RWTH Aachen University, 52056 Aachen (Germany); Chattopadhyay, Sudeshna, E-mail: sudeshna@iiti.ac.in [Discipline of Metallurgy Engineering and Materials Science, Indian Institute of Technology Indore, Indore 453552 (India); Discipline of Physics, Indian Institute of Technology Indore, Indore 453552 (India); Centre for Biosciences and Biomedical Engineering, Indian Institute of Technology Indore, Indore 453552 (India)

    2017-08-31

    Highlights: • Ultra-thin ZnO films grown on confined polymeric (polystyrene, PS) template. • XRR and GISAXS explore the surface/interfaces structure and morphology of ZnO/PS. • Insights into the growth mechanism of magnetron sputtered ZnO thin film on PS template. • Nucleated disk-like cylindrical particles are the basis of the formation of ZnO layers. • Effect of ZnO film thickness on room temperature PL spectra in ZnO/PS systems. - Abstract: The structure and morphology of ultra-thin zinc oxide (ZnO) films with different film thicknesses on confined polymer template were studied through X-ray reflectivity (XRR) and grazing incidence small angle X-ray scattering (GISAXS). Using magnetron sputter deposition technique ZnO thin films with different film thicknesses (<10 nm) were grown on confined polystyrene with ∼2R{sub g} film thickness, where R{sub g} ∼ 20 nm (R{sub g} is the unperturbed radius of gyration of polystyrene, defined by R{sub g} = 0.272 √M{sub 0}, and M{sub 0} is the molecular weight of polystyrene). The detailed internal structure, along the surface/interfaces and the growth direction of the system were explored in this study, which provides insight into the growth procedure of ZnO on confined polymer and reveals that a thin layer of ZnO, with very low surface and interface roughness, can be grown by DC magnetron sputtering technique, with approximately full coverage (with bulk like electron density) even in nm order of thickness, in 2–7 nm range on confined polymer template, without disturbing the structure of the underneath template. The resulting ZnO-polystyrene hybrid systems show strong ZnO near band edge (NBE) and deep-level (DLE) emissions in their room temperature photoluminescence spectra, where the contribution of DLE gets relatively stronger with decreasing ZnO film thickness, indicating a significant enhancement of surface defects because of the greater surface to volume ratio in thinner films.

  15. Electrodeposition of Cu-doped ZnO nanowire arrays and heterojunction formation with p-GaN for color tunable light emitting diode applications

    International Nuclear Information System (INIS)

    Lupan, O.; Pauporté, T.; Viana, B.; Aschehoug, P.

    2011-01-01

    Highlights: ► High quality copper-doped zinc oxide nanowires were electrochemically grown at low temperature. ► ZnO:Cu nanowires have been epitaxially grown on Mg-doped p-GaN single-crystalline layers. ► The (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction was used to fabricate a light-emitting diode structure. ► The photo- and electroluminescence emission was red-shifted to the violet spectral region compared to pure ZnO. ► The results are of importance for band-gap engineering of ZnO and for color-tunable LED. - Abstract: Copper-doped zinc oxide (ZnO:Cu) nanowires (NWs) were electrochemically deposited at low temperature on fluor-doped tin oxide (FTO) substrates. The electrochemical behavior of the Cu–Zn system for Cu-doped ZnO electrodeposition was studied and the electrochemical reaction mechanism is discussed. The synthesized ZnO arrayed layers were investigated by using SEM, XRD, EDX, photoluminescence and Raman techniques. X-ray diffraction analysis demonstrates a decrease in the lattice parameters of Cu-doped ZnO NWs. Structural analyses show that the nanomaterial is of hexagonal structure with the Cu incorporated in ZnO NWs probably by substituting zinc in the host lattice. Photoluminescence studies on pure and Cu-doped ZnO NWs shows that the near band edge emission is red-shifted by about 5 or 12 nm depending on Cu(II) concentration in the electrolytic bath solution (3 or 6 μmol l −1 ). Cu-doped ZnO NWs have been also epitaxially grown on Mg doped p-GaN single-crystalline layers and the (ZnO:Cu NWs)/(p-GaN:Mg) heterojunction has been used to fabricate a light-emitting diode (LED) structure. The emission was red-shifted to the visible violet spectral region compared to pure ZnO. The present work demonstrates the ability of electrodeposition to produce high quality ZnO nanowires with tailored optical properties by doping. The obtained results are of great importance for further studies on bandgap engineering of ZnO, for color-tunable LED applications

  16. Highly transparent and conductive Al-doped ZnO nanoparticulate thin films using direct write processing

    International Nuclear Information System (INIS)

    Vunnam, S; Ankireddy, K; Kellar, J; Cross, W

    2014-01-01

    Solution processable Al-doped ZnO (AZO) thin films are attractive candidates for low cost transparent electrodes. We demonstrate here an optimized nanoparticulate ink for the fabrication of AZO thin films using scalable, low-cost direct write processing (ultrasonic spray deposition) in air at atmospheric pressure. The thin films were made via thermal processing of as-deposited films. AZO films deposited using the proposed nanoparticulate ink with further reducing in vacuum and rf plasma of forming gas exhibited optical transparency greater than 95% across the visible spectrum, and electrical resistivity of 0.5 Ω cm and it drops down to 7.0 × 10 −2 Ω cm after illuminating with UV light, which is comparable to commercially available tin doped indium oxide colloidal coatings. Various structural analyses were performed to investigate the influence of ink chemistry, deposition parameters, and annealing temperatures on the structural, optical, and electrical characteristics of the spray deposited AZO thin films. Optical micrographs confirmed the presence of surface defects and cracks using the AZO NPs ink without any additives. After adding N-(2-Aminoethyl)-3-aminopropylmethyldimethoxy silane to the ink, AZO films exhibited an optical transparency which was virtually identical to that of the plain glass substrate. (papers)

  17. A highly selective and wide range ammonia sensor—Nanostructured ZnO:Co thin film

    International Nuclear Information System (INIS)

    Mani, Ganesh Kumar; Rayappan, John Bosco Balaguru

    2015-01-01

    Graphical abstract: - Highlights: • Cobalt doped nanostructured ZnO thin films were spray deposited on glass substrates. • Co-doped ZnO film was highly selective towards ammonia than ethanol, methanol, etc. • The range of ammonia detection was improved significantly by doping cobalt in ZnO. - Abstract: Ammonia sensing characteristics of undoped and cobalt (Co)-doped nanostructured ZnO thin films were investigated. Polycrystalline nature with hexagonal wurtzite structure and high crystalline quality with dominant (0 0 2) plane orientation of Co-doped ZnO film were confirmed by the X-ray diffractogram. Scanning electron micrographs of the undoped film demonstrated the uniform deposition of sphere-shaped grains. But, smaller particles with no clear grain boundaries were observed for Co-doped ZnO thin film. Band gap values were found to be 3.26 eV and 3.22 eV for undoped and Co-doped ZnO thin films. Ammonia sensing characteristics of Co-doped ZnO film at room temperature were investigated in the concentration range of 15–1000 ppm. Variation in the sensing performances of Co-doped and pure ZnO thin films has been analyzed and compared

  18. Photoelectrochemical properties of hierarchical ZnO micro-nanostructure sensitized with Sb2S3 nanoparticles

    Directory of Open Access Journals (Sweden)

    Zhimin GUO

    2016-02-01

    Full Text Available By using electrochemical deposition method, and assisted with additions of PEG-400 and EDA, well-aligned ZnO nanorods and hierarchical ZnO micro-nanostructure are fabricated directly on indium doped tin oxide coated conducting glass (ITO substrate. The shell-core Sb2S3/ZnO nanorod structure and the shell-core hierarchical Sb2S3/ZnO micro-nanostructure are prepared by chemical bath deposition method. SEM, XRD, UV-Vis and photocurrent test are used to characterize the morphology, nanostructures and their photoelectrochemical properties. The studies show that the photocurrent on the array membranes with shell-core hierarchical Sb2S3/ZnO micro-nanostructure is apparently higher than that with shell-core Sb2S3/ZnO nanorods array.

  19. Enhancement of photo sensor properties of nanocrystalline ZnO thin film by swift heavy ion irradiation

    Energy Technology Data Exchange (ETDEWEB)

    Mahajan, S. V.; Upadhye, D. S.; Bagul, S. B. [Department of Nanotechnology, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad-431004 (India); Shaikh, S. U.; Birajadar, R. B.; Siddiqui, F. Y.; Huse, N. P. [Thin film and Nanotechnology Laboratory, Department of Physics, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad-431004 (India); Sharma, R. B., E-mail: ramphalsharma@yahoo.com, E-mail: rps.phy@gmail.com [Thin film and Nanotechnology Laboratory, Department of Physics, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad-431004 (India); Department of Nanotechnology, Dr. Babasaheb Ambedkar Marathwada University, Aurangabad-431004 (India)

    2015-06-24

    Nanocrystalline Zinc Oxide (ZnO) thin film prepared by Low cost Successive Ionic Layer Adsorption and Reaction (SILAR) method. This film was irradiated by 120 MeV Ni{sup 7+} ions with the fluence of 5x10{sup 12}ions/cm{sup 2}. The X-ray diffraction study was shows polycrystalline nature with wurtzite structure. The optical properties as absorbance were determined using UV-Spectrophotometer and band gap was also calculated. The Photo Sensor nature was calculated by I-V characteristics with different sources of light 40W, 60W and 100W.

  20. Structure evolution of zinc oxide thin films deposited by unbalance DC magnetron sputtering

    Energy Technology Data Exchange (ETDEWEB)

    Aryanto, Didik, E-mail: didi027@lipi.go.id [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Marwoto, Putut; Sugianto [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Materials Research Group, Physics Department, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia); Sudiro, Toto [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); Birowosuto, Muhammad D. [Research Center for Physics, Indonesian Institute of Sciences, Serpong 15314, Tangerang Selatan (Indonesia); CINTRA UMI CNRS/NTU/THALES 3288 Research Techno Plaza, 50 Nanyang Drive, Border X Block, level 6, 637553 (Singapore); Sulhadi [Physics Department, Faculty of Mathematics and Science, Universitas Negeri Semarang, Gunungpati, Semarang 50229 Jawa Tengah (Indonesia)

    2016-04-19

    Zinc oxide (ZnO) thin films are deposited on corning glass substrates using unbalanced DC magnetron sputtering. The effect of growth temperature on surface morphology and crystallographic orientation of ZnO thin film is studied using atomic force microscopy (AFM) and X-ray diffraction (XRD) techniques. The surface morphology and crystallographic orientation of ZnO thin film are transformed against the increasing of growth temperature. The mean grain size of film and the surface roughness are inversely and directly proportional towards the growth temperature from room temperature to 300 °C, respectively. The smaller grain size and finer roughness of ZnO thin film are obtained at growth temperature of 400 °C. The result of AFM analysis is in good agreement with the result of XRD analysis. ZnO thin films deposited in a series of growth temperatures have hexagonal wurtzite polycrystalline structures and they exhibit transformations in the crystallographic orientation. The results in this study reveal that the growth temperature strongly influences the surface morphology and crystallographic orientation of ZnO thin film.

  1. Room temperature inorganic polycondensation of oxide (Cu{sub 2}O and ZnO) nanoparticles and thin films preparation by the dip-coating technique

    Energy Technology Data Exchange (ETDEWEB)

    Salek, G.; Tenailleau, C., E-mail: tenailleau@chimie.ups-tlse.fr; Dufour, P.; Guillemet-Fritsch, S.

    2015-08-31

    Oxide thin solid films were prepared by dip-coating into colloidal dispersions of oxide nanoparticles stabilized at room temperature without the use of chelating or complex organic dispersing agents. Crystalline oxide nanoparticles were obtained by inorganic polycondensation and characterized by X-ray diffraction and field emission gun scanning electron microscopy. Water and ethanol synthesis and solution stabilization of oxide nanoparticle method was optimized to prepare two different structural and compositional materials, namely Cu{sub 2}O and ZnO. The influence of hydrodynamic parameters over the particle shape and size is discussed. Spherical and rod shape nanoparticles were formed for Cu{sub 2}O and ZnO, respectively. Isoelectric point values of 7.5 and 8.2 were determined for cuprous and zinc oxides, respectively, after zeta potential measurements. A shear thinning and thixotropic behavior was observed in both colloidal sols after peptization at pH ~ 6 with dilute nitric acid. Every colloidal dispersion stabilized in a low cost and environmentally friendly azeotrope solution composed of 96 vol.% of ethanol with water was used for the thin film preparation by the dip-coating technique. Optical properties of the light absorber cuprous oxide and transparent zinc oxide thin solid films were characterized by means of transmittance and reflectance measurements (300–1100 nm). - Highlights: • Room temperature inorganic polycondensation of crystalline oxides • Water and ethanol synthesis and solution stabilization of oxide nanoparticles • Low cost method for thin solid film preparation.

  2. Morphological differences in transparent conductive indium-doped zinc oxide thin films deposited by ultrasonic spray pyrolysis

    International Nuclear Information System (INIS)

    Jongthammanurak, Samerkhae; Cheawkul, Tinnaphob; Witana, Maetapa

    2014-01-01

    In-doped ZnO thin films were deposited on glass substrates by an ultrasonic spray pyrolysis technique, using indium chloride (InCl 3 ) as a dopant and zinc acetate solution as a precursor. Increasing the [at.% In]/[at.% Zn] ratio changed the crystal orientations of thin films, from the (100) preferred orientation in the undoped, to the (101) and (001) preferred orientations in the In-doped ZnO thin films with 4 at.% and 6–8 at.%, respectively. Undoped ZnO thin film shows relatively smooth surface whereas In-doped ZnO thin films with 4 at.% and 6–8 at.% show surface features of pyramidal forms and hexagonal columns, respectively. X-ray diffraction patterns of the In-doped ZnO thin films with [at.% In]/[at.% Zn] ratios of 6–8% presented an additional peak located at 2-theta of 32.95°, which possibly suggested that a metastable Zn 7 In 2 O 10 phase was present with the ZnO phase. ZnO thin films doped with 2 at.% In resulted in a sheet resistance of ∼ 645 Ω/sq, the lowest value among thin films with [at.% In]/[at.% Zn] ratio in a range of 0–8%. The precursor molarity was changed between 0.05 M and 0.20 M at an [at.% In]/[at.% Zn] ratio of 2%. Increasing the precursor molarity in a range of 0.10 M–0.20 M resulted in In-doped ZnO thin films with the (100) preferred orientation. An In-doped ZnO thin film deposited by 0.20 M precursor showed a sheet resistance of 25 Ω/sq, and an optical transmission of 75% at 550 nm wavelength. The optical band gap estimated from the transmission result was 3.292 eV. - Highlights: • Indium-doped ZnO thin films were grown on glass using ultrasonic spray pyrolysis. • Thin films' orientations depend on In doping and Zn molarity of precursor solution. • Highly c-axis or a-axis orientations were found in the In-doped ZnO thin films. • In doping of 6–8 at.% may have resulted in ZnO and a metastable Zn 7 In 2 O 10 phases. • Increasing precursor molarity reduced sheet resistance of In-doped ZnO thin films

  3. Titania nanotube arrays surface-modified with ZnO for enhanced photocatalytic applications

    Energy Technology Data Exchange (ETDEWEB)

    Nageri, Manoj; Kalarivalappil, Vijila; Vijayan, Baiju K.; Kumar, Viswanathan, E-mail: vkumar10@yahoo.co.in

    2016-05-15

    Highlights: • Heterostructures of TNA/ZnO synthesised through potentiostatic anodisation followed by hydrothermal method. • Evaluation of morphological features of the heterostructure with hydrothermal processing time. • Correlation of photocatalytic activity of the hetrostructure with its morphology and surface texture. - Abstract: Well ordered titanium dioxide nanotube arrays (TNA) of average diameter 129 nm and wall thickness of 25 nm were fabricated through potentiostatic anodisation of titanium (Ti) metal substrates. Such TNA were subsequently surface-modified with various amounts of zinc oxide (ZnO) nanopowders using hydrothermal technique to obtain heterogeneous TNA/ZnO nanostructures. The crystalline phase and surface microstructure of the heterostructures were determined by X-ray diffraction, Raman spectroscopy and scanning electron microscopy respectively. The morphology of the heterostructures strongly depended on the hydrothermal conditions employed. The photocatalytic activity of the heterostructures have also been investigated and correlated with their surface morphology and texture.

  4. Angle-sensitive and fast photovoltage of silver nanocluster embeded ZnO thin films induced by 1.064-μm pulsed laser

    International Nuclear Information System (INIS)

    Song-Qing, Zhao; Li-Min, Yang; Wen-Wei, Liu; Kun, Zhao; Yue-Liang, Zhou; Qing-Li, Zhou

    2010-01-01

    Silver nanocluster embedded ZnO composite thin film was observed to have an angle-sensitive and fast photovoltaic effect in the angle range from −90° to 90°, its peak value and the polarity varied regularly with the angle of incidence of the 1.064-μm pulsed Nd:YAG laser radiation onto the ZnO surface. Meanwhile, for each photovoltaic signal, its rising time reached ∼2 ns with an open-circuit photovoltage of ∼2 ns full width at half-maximum. This angle-sensitive fast photovoltaic effect is expected to put this composite film a candidate for angle-sensitive and fast photodetector. (condensed matter: electronic structure, electrical, magnetic, and optical properties)

  5. Synthesis of ZnO nanorods by spray pyrolysis for H2S gas sensor

    International Nuclear Information System (INIS)

    Shinde, S.D.; Patil, G.E.; Kajale, D.D.; Gaikwad, V.B.; Jain, G.H.

    2012-01-01

    Highlights: ► Hexagonal pillar shaped ZnO nanorods with different sizes have been successfully synthesized by spray pyrolysis technique. ► ZnO nanorods thin films showed much better sensitivity and stability than the conventional materials to H 2 S gas (100 ppm) at 50 °C. ► This ZnO thin film has potential in application of room temperature H 2 S gas sensing. - Abstract: Hexagonal pillar shaped ZnO nanorods with different sizes have been successfully synthesized by spray pyrolysis technique (SPT). The equal amount of methanol and water is used as a solvent to dissolve the AR grade Zinc acetate for precursor solution. This solution is sprayed on to the glass substrate heated at 350 °C. The films were characterized by ultra-violet spectroscopy (UV), X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The deposition of thin films results in a layer comprising well-shaped hexagonal ZnO nanorods with diameter of 90–120 nm and length of up to 200 nm. The gas sensing properties of these films have been investigated for various interfering gases such as CO 2 , CO, ethanol, NH 3 and H 2 S, etc. at operating temperature from 30° (room temperature) to 450 °C. The results indicate that the ZnO nanorods thin films showed much better sensitivity and stability than the conventional materials to H 2 S gas (100 ppm) at 50 °C. The hexagonal pillar shaped ZnO nanorods can improve the sensitivity and selectivity of the sensors.

  6. Wide-bandgap high-mobility ZnO thin-film transistors produced at room temperature

    International Nuclear Information System (INIS)

    Fortunato, Elvira M.C.; Barquinha, Pedro M.C.; Pimentel, Ana C.M.B.G.; Goncalves, Alexandra M.F.; Marques, Antonio J.S.; Martins, Rodrigo F.P.; Pereira, Luis M.N.

    2004-01-01

    We report high-performance ZnO thin-film transistor (ZnO-TFT) fabricated by rf magnetron sputtering at room temperature with a bottom gate configuration. The ZnO-TFT operates in the enhancement mode with a threshold voltage of 19 V, a saturation mobility of 27 cm 2 /V s, a gate voltage swing of 1.39 V/decade and an on/off ratio of 3x10 5 . The ZnO-TFT presents an average optical transmission (including the glass substrate) of 80% in the visible part of the spectrum. The combination of transparency, high mobility, and room-temperature processing makes the ZnO-TFT a very promising low-cost optoelectronic device for the next generation of invisible and flexible electronics

  7. Optical band gap of ZnO thin films deposited by electron beam evaporation

    International Nuclear Information System (INIS)

    Nadeem, M. Y.; Ali, S. L.; Wasiq, M. F.; Rana, A. M.

    2006-01-01

    Optical band gap of ZnO thin films deposited by electron beam evaporation at evaporation rates ranging 5 As/sup -1/ to 15 As /sup -1/ and thickness ranging 1000A to 3000A is presented. Deposited films were annealed at 573K for one and half hour. The variations in the optical band gap were observed and showed decreasing behavior from 3.15 eV, 3.05 eV, from 3.18 eV to 3.10 eV and from 3.19 eV to 3.18 eV for films with respective thickness 1000A, 2000 A, 3000 A on increasing the evaporation rate from 5 As/sup-1/ to As/sup -1/ by keeping thickness constant. (author)

  8. Textured ZnO thin films by RF magnetron sputtering

    CERN Document Server

    Ginting, M; Kang, K H; Kim, S K; Yoon, K H; Park, I J; Song, J S

    1999-01-01

    Textured thin films ZnO has been successfully grown by rf magnetron sputtering method using a special technique of introducing a small amount of water and methanol on the deposition chamber. The grain size of the textured surface is highly dependent on the argon pressure during the deposition. The pressure in this experiment was varied from 50 mTorr down to 5 mTorr and the highest grain size of the film is obtained at 5 mTorr. The total transmittance of the films are more than 85% in the wavelength of 400 to 800 nm, and haze ratio of about 14% is obtained at 400 nm wavelength. Beside the textured surface, these films also have very low resistivity, which is lower than 1.4x10 sup - sup 3 OMEGA centre dot cm. X-ray analysis shows that the films with textured surface have four diffraction peaks on the direction of (110), (002), (101) and (112), while the non-textured films have only (110) and (002) peaks. Due to the excellent characteristics of this film, it will make the film very good TCO alternatives for the ...

  9. Photovoltaic Properties of Co-doped ZnO Thin Film on Glass Substrate

    International Nuclear Information System (INIS)

    Sabia Aye; Zin Ma Ma; May Nwe Oo; Than Than Win; Yin Maung Maung; Ko Ko Kyaw Soe

    2011-12-01

    Cobalt (Co) 0.4 mol doped zinc oxide (ZnO) fine powder was prepared by solid state mixed oxide route. Phase formation and crystal structure of Co-doped ZnO (CZO) powder were examined by X-ray diffraction (XRD). Scanning Electron Microscopy (SEM) was used to observe the micro structure of Co doped ZnO powder. Energy Dispersive X-ray Fluorescent (EDXRF) technique gave the elemental content of cobalt and zinc. Co-doped ZnO film was formed on glass substrate by spin coating technique. Photovoltaic properties of CZO/glass cell were measured.

  10. Electrodeposition of ZnO nano-wires lattices with a controlled morphology

    International Nuclear Information System (INIS)

    Elias, J.; Tena-Zaera, R.; Katty, A.; Levy-Clement, C.

    2006-01-01

    In this work, it is shown that the electrodeposition is a changeable low cost method which allows, according to the synthesis conditions, to obtain not only plane thin layers of ZnO but different nano-structures too. In a first part, are presented the formation conditions of a compact thin layer of nanocrystalline ZnO electrodeposited on a conducing glass substrate. This layer plays a buffer layer role for the deposition of a lattice of ZnO nano-wires. The step of nano-wires nucleation is not only determined by the electrochemical parameters but by the properties of the buffer layer too as the grain sizes and its thickness. In this context, the use of an electrodeposition method in two steps allows to control the nano-wires length and diameter and their density. The morphology and the structural and optical properties of these nano-structures have been analyzed by different techniques as the scanning and transmission electron microscopy, the X-ray diffraction and the optical spectroscopy. These studies show that ZnO nano-structures are formed of monocrystalline ZnO nano-wires, presenting a great developed surface and a great optical transparency in the visible. These properties make ZnO a good material for the development of nano-structured photovoltaic cells as the extremely thin absorber cells (PV ETA) or those with dye (DSSC) which are generally prepared with porous polycrystalline TiO 2 . Its replacement by a lattice of monocrystalline ZnO nano-wires allows to reduce considerably the number of grain boundaries and in consequence to improve the transport of the electrons. The results are then promising for the PV ETA cells with ZnO nano-wires. (O.M.)

  11. Synthesis of ZnO-TiO{sub 2} core-shell long nanowire arrays and their application on dye-sensitized solar cells

    Energy Technology Data Exchange (ETDEWEB)

    Feng Yamin [Department of Physics, Institute of Nanoscience and Nanotechnology, Central China Normal University, Wuhan 430079 (China); Ji Xiaoxu [School of Physics and Electronic Engineering, Nanyang Normal University, Nanyang 473003 (China); Duan Jinxia; Zhu Jianhui; Jiang Jian; Ding Hao; Meng Gaoxiang; Ding Ruimin; Liu Jinping [Department of Physics, Institute of Nanoscience and Nanotechnology, Central China Normal University, Wuhan 430079 (China); Hu Anzheng [School of Physics and Electronic Engineering, College of Xiangfan, Xiangfan 441813 (China); Huang Xintang, E-mail: xthuang@phy.ccnu.edu.cn [Department of Physics, Institute of Nanoscience and Nanotechnology, Central China Normal University, Wuhan 430079 (China)

    2012-06-15

    Long ZnO nanowire arrays (NAs) grown on fluorine-doped tin oxide (FTO) glasses have been synthesized via a facile hydrothermal method without refreshing the reaction solution and applied as the precursor. By adjusting growth conditions, ZnO NAs with tunable lengths can be achieved. A nanocomposite made of ZnO nanowire core and TiO{sub 2} shell was further realized by a novel 'fast-dip-coating' method conducted in a Ti(OC{sub 4}H{sub 9}){sub 4}-dissolved ethanol solution. The formed ZnO-TiO{sub 2} core-shell NAs on FTO substrates were applied as electrodes for dye sensitized solar cells (DSSCs). It is found that both the TiO{sub 2} coating and NAs length play important roles in the enhancement of photoelectric conversion efficiency (PCE) of DSSCs. When the length of ZnO-TiO{sub 2} NAs reaches up to 14 {mu}m, the electrode can exhibit a maximum PCE as high as 3.80%, which is 2.6 times higher than that of pure ZnO NAs. - Graphical abstract: ZnO nanowire arrays in the length of 14 {mu}m have been successfully synthesized on the FTO substrate and coated with a thin shell of TiO{sub 2}; the ZnO-TiO{sub 2} electrodes applied in DSSCs exhibit great photoelectric conversion efficiency as high as 3.80%. Highlights: Black-Right-Pointing-Pointer Long ZnO nanowire arrays have been synthesized by using hydrothermal method. Black-Right-Pointing-Pointer A TiO{sub 2} shell outside of ZnO nanowire is introduced by a fast dip-coating method. Black-Right-Pointing-Pointer ZnO and ZnO-TiO{sub 2} core-shell nanowires are applied as the electrodes for DSSCs. Black-Right-Pointing-Pointer The maximum conversion efficiency of ZnO-TiO{sub 2} electrode reaches to 3.80%.

  12. Synthesis of Thinned Concentric Circular Antenna Arrays Using Modified TLBO Algorithm

    Directory of Open Access Journals (Sweden)

    Zailei Luo

    2015-01-01

    Full Text Available Teaching-learning-based optimization (TLBO algorithm is a new kind of stochastic metaheuristic algorithm which has been proven effective and powerful in many engineering optimization problems. This paper describes the application of a modified version of TLBO algorithm, MTLBO, for synthesis of thinned concentric circular antenna arrays (CCAAs. The MTLBO is adjusted for CCAA design according to the geometry arrangement of antenna elements. CCAAs with uniform interelement spacing fixed at half wavelength have been considered for thinning using MTLBO algorithm. For practical purpose, this paper demonstrated SLL reduction of thinned CCAAs in the whole regular and extended space other than the phi = 0° plane alone. The uniformly and nonuniformly excited CCAAs have been discussed, respectively, during the simulation process. The proposed MTLBO is very easy to be implemented and requires fewer algorithm specified parameters, which is suitable for concentric circular antenna array synthesis. Numerical results clearly show the superiority of MTLBO algorithm in finding optimum solutions compared to particle swarm optimization algorithm and firefly algorithm.

  13. ZnO and Al doped ZnO thin films deposited by Spray Plasma: Effect of the growth time and Al doping on microstructural, optical and electrical properties

    International Nuclear Information System (INIS)

    Baba, Kamal; Lazzaroni, Claudia; Nikravech, Mehrdad

    2015-01-01

    Nanostructured zinc oxide (ZnO) and Al doped ZnO (ZnO:Al) thin films are deposited on glass substrate by the Spray Plasma technique. Zinc nitrate and aluminium nitrate are used as Zn and Al precursors, respectively. The effect of the growth time on structural and optical properties of undoped films is studied by X-ray diffraction, atomic force microscopy, and UV–Vis spectroscopy. The effect of Al doping on microstructural, optical and electrical characteristics of ZnO:Al films is also investigated. The results show that the grain size and the film thickness both increase with the growth time. The band gap of the layers varies from 3.17 to 3.24 eV depending on the thickness. The increase of the Al doping results in the enlargement of the peak (002) and the shift of its position to higher 2θ values. Average optical transmittance decreases from 90 to 65% with the growth time because of the thickness increase while there is no significant influence of the aluminium doping on the transmittance which is above 80% in most of the visible and near-IR range for all ZnO:Al films. The electrical properties characterized by Hall measurements show that all the deposited films exhibit high resistivity, between 4 and 10 4 Ω cm. The carrier concentration decreases from 2.10 19 to 2.10 13 cm −3 when the concentration of Al increases from 1.5 to 5 atm%. - Highlights: • The original Spray Plasma technique is used for ZnO and ZnO:Al thin film deposition. • Investigation of the effect of growth time and Al doping on the structural and optical properties • Increase of grain size and film thickness with t