Room Temperature Imprint Using Crack-Free Monolithic SiO2-PVA Nanocomposite for Fabricating Microhole Array on Silica Glass

Directory of Open Access Journals (Sweden)

Shigeru Fujino

2015-01-01

Full Text Available This paper aims to fabricate microhole arrays onto a silica glass via a room temperature imprint and subsequent sintering by using a monolithic SiO2-poly(vinyl alcohol (PVA nanocomposite as the silica glass precursor. The SiO2-PVA suspension was prepared from fumed silica particles and PVA, followed by drying to obtain tailored SiO2-PVA nanocomposites. The dependence of particle size of the fumed silica particles on pore size of the nanocomposite was examined. Nanocomposites prepared from 7 nm silica particles possessed suitable mesopores, whereas the corresponding nanocomposites prepared from 30 nm silica particles hardly possessed mesopores. The pore size of the nanocomposites increased as a function of decreasing pH of the SiO2-PVA suspension. As a consequence, the crack-free monolithic SiO2-PVA nanocomposite was obtained using 7 nm silica particles via the suspension at pH 3. Micropatterns were imprinted on the monolithic SiO2-PVA nanocomposite at room temperature. The imprinted nanocomposite was sintered to a transparent silica glass at 1200°C in air. The fabricated sintered glass possessed the microhole array on their surface with aspect ratios identical to the mold.

Efficiency enhancement in dye sensitized solar cells using dual function mesoporous silica as scatterer and back recombination inhibitor

Science.gov (United States)

Tanvi; Mahajan, Aman; Bedi, R. K.; Kumar, Subodh; Saxena, Vibha; Aswal, D. K.

2016-08-01

In the present work, we report the usage of mesoporous silica for improving light harvesting as well as for suppression of back recombination without affecting the extent of dye loading on TiO2 films. Synthesized mesoporous SiO2 was characterized by X-ray photoelectron spectroscopy, X-ray diffraction, Brunauer Emmett and Teller measurement, Scanning electron microscopy and Transmission electron microscopy. DSSCs were fabricated by incorporating different wt% of mesoporous SiO2 in TiO2 paste. An improvement of 50% was observed for devices fabricated using 0.75 wt% of mesoporous SiO2. The mechanism behind the improvement was investigated using electrochemical impedance spectroscopy and UV-Vis spectroscopy.

Dual functional porous anti-reflective coatings with a photocatalytic effect based on a single layer system

Science.gov (United States)

Jilavi, M. H.; Mousavi, S. H.; Müller, T. S.; de Oliveira, P. W.

2018-05-01

Anti-reflection and photocatalytic properties are desirable for improving the optical properties of electronic devices. We describe a method of fabrication a single-layer, anti-reflective (AR) thin film with an additional photocatalytic property. The layer is deposited on glass substrates by means of a low-cost dip-coating method using a SiO2-TiO2 solution. A comparative study was undertaken to investigate the effects of TiO2 concentrations on the photocatalytic properties of the film and to determine the optimal balance between transmittance and photocatalysis. The average transmittance increases from T = 90.51% to T = 95.46 ± 0.07% for the wavelengths between 380 and 1200 nm. The structural characterization indicated the formation of thin, porous SiO2-TiO2 films with a roughness of less than 7.5 nm. The quality of the samples was evaluated by a complete test program of the mechanical, chemical and accelerated weathering stability. This results open up new possibilities for cost-effective AR coatings for the glass and solar cell industries.

Photo-Electrical Characterization of Silicon Micropillar Arrays with Radial p/n Junctions Containing Passivation and Anti-Reflection Coatings

NARCIS (Netherlands)

Vijselaar, Wouter; Elbersen, R.; Tiggelaar, Roald M.; Gardeniers, Han; Huskens, Jurriaan

2017-01-01

In order to assess the contributions of anti-reflective and passivation effects in microstructured silicon-based solar light harvesting devices, thin layers of aluminum oxide (Al2O3), silicon dioxide (SiO2), silicon-rich silicon nitride (SiNx), and indium tin oxide (ITO), with a thickness ranging

Selective dry etching of silicon containing anti-reflective coating

Science.gov (United States)

Sridhar, Shyam; Nolan, Andrew; Wang, Li; Karakas, Erdinc; Voronin, Sergey; Biolsi, Peter; Ranjan, Alok

2018-03-01

Multi-layer patterning schemes involve the use of Silicon containing Anti-Reflective Coating (SiARC) films for their anti-reflective properties. Patterning transfer completion requires complete and selective removal of SiARC which is very difficult due to its high silicon content (>40%). Typically, SiARC removal is accomplished through a non-selective etch during the pattern transfer process using fluorine containing plasmas, or an ex-situ wet etch process using hydrofluoric acid is employed to remove the residual SiARC, post pattern transfer. Using a non-selective etch may result in profile distortion or wiggling, due to distortion of the underlying organic layer. The drawbacks of using wet etch process for SiARC removal are increased overall processing time and the need for additional equipment. Many applications may involve patterning of active structures in a poly-Si layer with an underlying oxide stopping layer. In such applications, SiARC removal selective to oxide using a wet process may prove futile. Removing SiARC selectively to SiO2 using a dry etch process is also challenging, due to similarity in the nature of chemical bonds (Si - O) in the two materials. In this work, we present highly selective etching of SiARC, in a plasma driven by a surface wave radial line slot antenna. The first step in the process involves an in-situ modification of the SiARC layer in O2 plasma followed by selective etching in a NF3/H2 plasma. Surface treatment in O2 plasma resulted in enhanced etching of the SiARC layer. For the right processing conditions, in-situ NF3/H2 dry etch process demonstrated selectivity values greater than 15:1 with respect to SiO2. The etching chemistry, however, was sensitive to NF3:H2 gas ratio. For dilute NF3 in H2, no SiARC etching was observed. Presumably, this is due to the deposition of ammonium fluorosilicate layer that occurs for dilute NF3/H2 plasmas. Additionally, challenges involved in selective SiARC removal (selective to SiO2, organic

Optical properties of the Al2O3/SiO2 and Al2O3/HfO2/SiO2 antireflective coatings

Science.gov (United States)

Marszałek, Konstanty; Winkowski, Paweł; Jaglarz, Janusz

2014-01-01

Investigations of bilayer and trilayer Al2O3/SiO2 and Al2O3/HfO2/SiO2 antireflective coatings are presented in this paper. The oxide films were deposited on a heated quartz glass by e-gun evaporation in a vacuum of 5 × 10-3 [Pa] in the presence of oxygen. Depositions were performed at three different temperatures of the substrates: 100 °C, 200 °C and 300 °C. The coatings were deposited onto optical quartz glass (Corning HPFS). The thickness and deposition rate were controlled with Inficon XTC/2 thickness measuring system. Deposition rate was equal to 0.6 nm/s for Al2O3, 0.6 nm - 0.8 nm/s for HfO2 and 0.6 nm/s for SiO2. Simulations leading to optimization of the thin film thickness and the experimental results of optical measurements, which were carried out during and after the deposition process, have been presented. The optical thickness values, obtained from the measurements performed during the deposition process were as follows: 78 nm/78 nm for Al2O3/SiO2 and 78 nm/156 nm/78 nm for Al2O3/HfO2/SiO2. The results were then checked by ellipsometric technique. Reflectance of the films depended on the substrate temperature during the deposition process. Starting from 240 nm to the beginning of visible region, the average reflectance of the trilayer system was below 1 % and for the bilayer, minima of the reflectance were equal to 1.6 %, 1.15 % and 0.8 % for deposition temperatures of 100 °C, 200 °C and 300 °C, respectively.

Structurally stabilized organosilane-templated thermostable mesoporous titania.

Science.gov (United States)

Amoli, Vipin; Tiwari, Rashmi; Dutta, Arghya; Bhaumik, Asim; Sinha, Anil Kumar

2014-01-13

Structurally thermostable mesoporous anatase TiO2 (m-TiO2) nanoparticles, uniquely decorated with atomically dispersed SiO2, is reported for the first time. The inorganic Si portion of the novel organosilane template, used as a mesopores-directing agent, is found to be incorporated in the pore walls of the titania aggregates, mainly as isolated sites. This is evident by transmission electron microscopy and high-angle annular dark field scanning transmission electron microscopy, combined with electron dispersive X-ray spectroscopy. This type of unique structure provides exceptional stability to this new material against thermal collapse of the mesoporous structure, which is reflected in its high surface area (the highest known for anatase titania), even after high-temperature (550 °C) calcination. Control of crystallite size, pore diameter, and surface area is achieved by varying the molar ratios of the titanium precursor and the template during synthesis. These mesoporous materials retain their porosity and high surface area after template removal and further NaOH/HCl treatment to remove silica. We investigate their performance for dye-sensitized solar cells (DSSCs) with bilayer TiO2 electrodes, which are prepared by applying a coating of m-TiO2 onto a commercial titania (P25) film. The high surface area of the upper mesoporous layer in the P25-m-TiO2 DSSC significantly increases the dye loading ability of the photoanode. The photocurrent and fill factor for the DSSC with the bilayer TiO2 electrode are greatly improved. The large increase in photocurrent current (ca. 56%) in the P25-m-TiO2 DSSC is believed to play a significant role in achieving a remarkable increase in the photovoltaic efficiency (60%) of the device, compared to DSSCs with a monolayer of P25 as the electrode. Copyright © 2014 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Microwave electromagnetic and absorption properties of SiO2/C core/shell composites plated with metal cobalt

Science.gov (United States)

Shen, Guozhu; Fang, Xumin; Wu, Hongyan; Wei, Hongyu; Li, Jingfa; Li, Kaipeng; Mei, Buqing; Xu, Yewen

2017-04-01

A facile method has been developed to fabricate magnetic core/shell SiO2/C/Co sub-microspheres via the pyrolysis of SiO2/PANI (polyaniline) and electroless plating method. The electromagnetic parameters of these SiO2/C and SiO2/C/Co composites were measured and the microwave reflection loss properties were evaluated in the frequency range of 2-18 GHz. The results show that the dielectric loss of SiO2/C composite increases with the increase of carbonization temperature and the magnetic loss enhances due to the deposition of cobalt on the SiO2/C sub-microspheres. The reflection loss results exhibit that the microwave absorption properties of the SiO2/C/Co composites are more excellent than those of SiO2/C composites for each thickness. The maximum effective absorption bandwidth (reflection loss ≤ -10 dB) arrives at 5.0 GHz (13.0-18 GHz) for SiO2/C/Co composite with 1.5 mm of thickness and the minimum reflection loss value is -24.0 dB at 5.0 GHz with 4.0 mm of thickness. The microwave loss mechanism of the SiO2/C/Co composites was also discussed in this paper.

Core-shelled mesoporous CoFe2O4-SiO2 material with good adsorption and high-temperature magnetic recycling capabilities

Science.gov (United States)

Li, Zhi'ang; Wang, Jianlin; Liu, Min; Chen, Tong; Chen, Jifang; Ge, Wen; Fu, Zhengping; Peng, Ranran; Zhai, Xiaofang; Lu, Yalin

2018-04-01

Residues of organic dye in industrial effluents cause severe water system pollution. Although several methods, such as biodegradation and activated carbon adsorption, are available for treating these effluents before their discharge into waterbodies, secondary pollution by adsorbents and degrading products remains an issue. Therefore, new materials should be identified to solve this problem. In this work, CoFe2O4-SiO2 core-shell structures were synthesized using an improved Stöber method by coating mesoporous silica onto CoFe2O4 nanoparticles. The specific surface areas of the synthesized particles range from 30 m2/g to 150 m2/g and vary according to the dosage amount of tetraethoxysilane. Such core-shelled nanoparticles have the following advantages for treating industrial effluents mixed with dye: good adsorption capability, above-room-temperature magnetic recycling capability, and heat-enduring stability. Through adsorption of methylene blue, a typical dyeing material, the core-shell-structured particles show a good adsorption capability of approximately 33 mg/L. The particles are easily and completely collected by magnets, which is possible due to the magnetic property of core CoFe2O4. Heat treatment can burn out the adsorbed dyes and good adsorption performance is sustained even after several heat-treating loops. This property overcomes the common problem of particles with Fe3O4 as a core, by which Fe3O4 is oxidized to nonmagnetic α-Fe2O3 at the burning temperature. We also designed a miniature of effluent-treating pipeline, which demonstrates the potential of the application.

Sustainable synthesis of magnetically separable SiO2/Co@Fe2O4 nanocomposite and its catalytic applications for the benzimidazole synthesis

Science.gov (United States)

Jithendra Kumara, K. S.; Krishnamurthy, G.; Sunil Kumar, N.; Naik, Nagaraja; Praveen, T. M.

2018-04-01

The Co(II) and Fe(III) centres magnetically separable two new mesoporous nanocatalyst were synthesised via chemical synthesis method. The transmission electron microscopic studies (TEM) show that, the particles are spherical shape with mean size of 20 nm. The Raman spectroscopy and X-ray photoelectron spectroscopy (XPS) reveals that SiO2 is coating on the surface of the cobalt ferrate nanoparticle (CoFe2O4). The SiO2 coating is efficiently preventing the aggregated collision of nanoparticles. Magnetic measurements show that diamagnetic character of the SiO2 is unaffected to the coercivity of SiO2 coated CoFe2O4 particles. In addition, these nanoparticles are used as nanocatalyst for high yielding, facile and expeditious synthesis of various functionalized 2-arylbenzimidazoles via one-pot condensation. The cascade including imine formation, cyclization, condensation, and aromatization occurs, without addition of any reducing or oxidizing agents. In all situations, the desired product was synthesised with excellent yield. The shorter reaction time, mild reaction condition, simplicity, non-toxicity, safe reaction and easy workup are the impotent merits of this protocol.

Space Weathering of Silicates Simulated by Successive Laser Irradiation: In Situ Reflectance Measurements of Fo90, Fo99+, and Sio2

Science.gov (United States)

Loeffler, M. J.; Dukes, C. A.; Christoffersen, R.; Baragiola, R. A.

2016-01-01

Pulsed-laser irradiation causes the visible-near-infrared spectral slope of olivine (Fo90 and Fo99+) and SiO2 to increase (redden), while the olivine samples darken and the SiO2 samples brighten slightly. XPS analysis shows that irradiation of Fo90 produces metallic Fe. Analytical SEM and TEM measurements confirm that reddening in the Fo90 olivine samples correlates with the production of nanophase metallic Fe (npFe0) grains, 2050 nm in size. The reddening observed in the SiO2 sample is consistent with the formation of SiO or other SiOx species that absorb in the visible. The weak spectral brightening induced by laser irradiation of SiO2 is consistent with a change in surface topography of the sample. The darkening observed in the olivine samples is likely caused by the formation of larger npFe0 particles, such as the 100400 nm diameter npFe0 identified during our TEM analysis of Fo90 samples. The Fo90 reflectance spectra are qualitatively similar to those in previous experiments suggesting that in all cases formation of npFe0 is causing the spectral alteration. Finally, we find that the accumulation of successive laserpulses cause continued sample darkening in the Vis-NIR, which suggests that repeated surface impacts are an efficient way to darken airless body surfaces.

Facile synthesis of highly biocompatible folic acid-functionalised SiO2 nanoparticles encapsulating rare-earth metal complexes, and their application in targeted drug delivery.

Science.gov (United States)

Xu, Xiuling; Hu, Fan; Shuai, Qi

2017-11-14

Mesoporous silica core-shell nanospheres encapsulating a rare-earth metal complex (RC) were first synthesised through a facile W/O (water in oil) inverse microemulsion method. In order to achieve targeted complex delivery, folic acid (FA) was used as the targeting component due to its high affinity for over-expressed folate receptors (FRs) in cancer cells. The RC 2 @SiO 2 -FA nanospheres were characterised via ultraviolet-visible light absorption spectroscopy (UV-vis spectroscopy), dynamic light scattering (DLS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). A microwave method was used to synthesise five RC cores based on 4-chlorophenoxyacetic acid, and their crystal structures were further confirmed using X-ray diffraction. The five RC cores have the following chemical formulae: [Er 2 (p-CPA) 6 (H 2 O) 6 ] RC 1 , [Ho 2 (p-CPA) 6 (H 2 O) 6 ] RC 2 , [Sm(p-CPA) 3 (H 2 O)] RC 3 , [Pr(p-CPA) 3 (H 2 O)]·3H 2 O RC 4 and [Ce(p-CPA) 3 (H 2 O) 2 ]·2H 2 O RC 5 . The carboxyl groups showed two kinds of coordination modes, namely μ 2 -η 1 :η 1 and μ 2 -η 1 :η 2 , among RC 1 -RC 5 . The flexible -OCH 2 COO- spacer group, which can undergo rotation of its C-O and C-C bonds, offered great potential for structural diversity. In vivo experiments revealed that the nanospheres exhibited no obvious cytotoxicity on HepG2 cells and 293 T cells, even at concentrations of up to 80 μg mL -1 . Nevertheless, all of the RC cores showed a certain degree of anti-tumour efficacy; in particular, RC 2 showed the strongest cytotoxicity against HepG2 cells. Interestingly, the cytotoxicity of all of the RC 2 @SiO 2 -FA nanospheres was higher than that of lone RC 2 . These types of FA-targeted mesoporous silica nanocarriers can be used for the delivery of anti-tumour RC, and provide a basis for the further study of affordable non-platinum-based complexes.

Enhanced Photocatalytic Activity of ZrO2-SiO2 Nanoparticles by Platinum Doping

Directory of Open Access Journals (Sweden)

Mohammad W. Kadi

2013-01-01

Full Text Available ZrO2-SiO2 mixed oxides were prepared via the sol-gel method. Photo-assisted deposition was utilized for doping the prepared mixed oxide with 0.1, 0.2, 0.3, and 0.4 wt% of Pt. XRD spectra showed that doping did not result in the incorporation of Pt within the crystal structure of the material. UV-reflectance spectrometry showed that the band gap of ZrO2-SiO2 decreased from 3.04 eV to 2.48 eV with 0.4 wt% Pt doping. The results show a specific surface area increase of 20%. Enhanced photocatalysis of Pt/ZrO2-SiO2 was successfully tested on photo degradation of cyanide under illumination of visible light. 100% conversion was achieved within 20 min with 0.3 wt% of Pt doped ZrO2-SiO2.

Preparation, characterization and photocatalytic applications of amine-functionalized mesoporous silica impregnated with transition-metal-monosubstituted polyoxometalates

International Nuclear Information System (INIS)

Li Li; Liu, Chunming; Geng Aifang; Jiang Chunjie; Guo Yihang; Hu Changwen

2006-01-01

Amine-functionalized mesoporous silica materials impregnated with transition-metal-monosubstituted polyoxometalates, K 5 [M(H 2 O)PW 11 O 39 ]-(EtO) 3 SiCH 2 CH 2 CH 2 NH 2 -MCM-48 (M = Co/Ni), were prepared by coordination of nickel/cobalt centers in the clusters with the amine surface groups in amine-functionalized mesoporous silica supports. The materials obtained were characterized by powder X-ray diffraction (XRD), UV-vis diffuse reflectance spectra (UV-vis-DR), infrared (IR) spectra, magic-angle spinning 31 P MAS NMR, transmission electron microscopy (TEM) and nitrogen adsorption measurements, indicating that the primary Keggin structures remained intact in as-prepared composites, and the composites possessed mesoporous structures. The composites exhibited UV-photocatalytic activity to degrade dye rhodamine B (RB), and the pesticides including hexachlorobenzene (HCB) and methylparathion (MPT). Leakage of K 5 [M(H 2 O)PW 11 O 39 ] from the support was hardly observed during the photocatalytic tests, attributed to strong coordination interactions between the Keggin units and the amine-functionalized silica surface. -- Graphical abstract: The K 5 [M(H 2 O)PW 11 O 39 ]-(EtO) 3 SiCH 2 CH 2 CH 2 NH 2 -SiO 2 composites were prepared by coordination of M centers in the Keggin units with the amine surface groups in amine-functionalized mesoporous silica supports, and the composites exhibited photocatalytic activity to degrade aqueous rhodamine B, hexachlorobenzene and methyl parathion

High-temperature synthesis of highly hydrothermal stable mesoporous silica and Fe-SiO2 using ionic liquid as a template

International Nuclear Information System (INIS)

Liu, Hong; Wang, Mengyang; Hu, Hongjiu; Liang, Yuguang; Wang, Yong; Cao, Weiran; Wang, Xiaohong

2011-01-01

Mesoporous silicas and Fe-SiO 2 with worm-like structures have been synthesized using a room temperature ionic liquid, 1-hexadecane-3-methylimidazolium bromide, as a template at a high aging temperature (150-190 o C) with the assistance of NaF. The hydrothermal stability of mesoporous silica was effectively improved by increasing the aging temperature and adding NaF to the synthesis gel. High hydrothermally stable mesoporous silica was obtained after being aged at 190 o C in the presence of NaF, which endured the hydrothermal treatment in boiling water at least for 10 d or steam treatment at 600 o C for 6 h. The ultra hydrothermal stability could be attributed to its high degree of polymerization of silicate. Furthermore, highly hydrothermal stable mesoporous Fe-SiO 2 has been synthesized, which still remained its mesostructure after being hydrothermally treated at 100 o C for 12 d or steam-treated at 600 o C for 6 h. -- Graphical abstract: Worm-like mesoporous silica and Fe-SiO 2 with high hydrothermal stability have been synthesized using ionic liquid 1-hexadecane-3-methylimidazolium bromide as a template under the assistance of NaF at high temperature. Display Omitted Research highlights: → Increasing aging temperature improved the hydrothermal stability of materials. →Addition of NaF enhanced the polymerization degree of silicates. → Mesoporous SiO 2 and Fe-SiO 2 obtained have remarkable hydrothermal stability.

Synthesis and photocatalytic activity of mesoporous – (001) facets TiO_2 single crystals

International Nuclear Information System (INIS)

Dong, Yeshuo; Fei, Xuening; Zhou, Yongzhu

2017-01-01

Highlights: • The (001) facets of TiO_2 single crystals with mesoporous structure. • The (010) and (100) facets of TiO_2 single crystals were covered by the flower – shaped TiO_2 crystals. • This special structure could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. - Abstract: In this work, the mesoporous – (001) facets TiO_2 single crystals have been successfully synthesized through a two-step solvothermal route without any template. Their structure and morphology were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), ultraviolet-visible (UV–vis) diffuse reflectance spectroscopy and energy dispersive X-ray spectrometer (EDX). Based on the different characteristics and atomic arrangements on each facet of anatase TiO_2 single crystals, we synthesized these mesoporous – (001) facets TiO_2 single crystals by controlling the interaction characteristics of hydrofluoric acid (HF) and isopropanol (i-PrOH) on the crystal facets. It can been seen that the (001) facets of these as-synthesized TiO_2 single crystals have a clear mesoporous structure through the SEM images and BET methods. Moreover, the other four facets were covered by the flower – shaped TiO_2 crystals with the generation of the mesoporous – (001) facets. This special and interesting morphology could promote charge separation and provide more active sites, which will lead to a substantial increase in photocatalytic activity. Moreover, it is more intuitive to reflect that the different crystal facets possess the different properties due to their atomic arrangement. Besides, according to the different synthetic routes, we proposed and discussed a plausible synthesis mechanism of these mesoporous – (001) facets TiO_2 single crystals.

Photoemission study on electrical dipole at SiO_2/Si and HfO_2/SiO_2 interfaces

International Nuclear Information System (INIS)

Fujimura, Nobuyuki; Ohta, Akio; Ikeda, Mitsuhisa; Makihara, Katsunori; Miyazaki, Seiichi

2017-01-01

Electrical dipole at SiO_2/Si and HfO_2/SiO_2 interfaces have been investigated by X-ray photoelectron spectroscopy (XPS) under monochromatized Al Kα radiation. From the analysis of the cut-off energy for secondary photoelectrons measured at each thinning step of a dielectric layer by wet-chemical etching, an abrupt potential change caused by electrical dipole at SiO_2/Si and HfO_2/SiO_2 interfaces has been clearly detected. Al-gate MOS capacitors with thermally-grown SiO_2 and a HfO_2/SiO_2 dielectric stack were fabricated to evaluate the Al work function from the flat band voltage shift of capacitance-voltage (C-V) characteristics. Comparing the results of XPS and C-V measurements, we have verified that electrical dipole formed at the interface can be directly measured by photoemission measurements. (author)

Phenol-formaldehyde carbon with ordered/disordered bimodal mesoporous structure as high-performance electrode materials for supercapacitors

Science.gov (United States)

Cai, Tingwei; Zhou, Min; Han, Guangshuai; Guan, Shiyou

2013-11-01

A novel phenol-formaldehyde carbon with ordered/disordered bimodal mesoporous structure is synthesized by the facile evaporation induced self-assembly strategy under a basic aqueous condition with SiO2 particles as template. The prepared bimodal mesoporous carbons (BMCs) are composed of ordered mesoporous and disordered mesoporous with diameter of about 3.5 nm and 7.0 nm, respectively. They can be employed as supercapacitor electrodes in H2SO4 aqueous electrolyte after the simple acid-treatment. BMC exhibits an exceptional specific capacitance of 344 F g-1 at the current density of 0.1 A g-1, although it has a relatively low surface area of 722 m2 g-1. And the BMC electrode displays an excellent cycling stability over 10,000 cycles.

Effect of SiO2 coating in bolometric Ge light detectors for rare event searches

International Nuclear Information System (INIS)

Beeman, J.W.; Gentils, A.; Giuliani, A.; Mancuso, M.; Pessina, G.; Plantevin, O.; Rusconi, C.

2013-01-01

In germanium-based light detectors for scintillating bolometers, a SiO 2 anti-reflective coating is often applied on the side of the germanium wafer exposed to light with the aim to improve its light collection efficiency. In this paper, we report about a measurement, performed in the temperature range 25–35 mK, of the light-collection increase obtained thanks to this method, which resulted to be of the order of 20%. The procedure followed has been carefully selected in order to minimize systematic effects. The employed light sources have the same spectral features (peaking at ∼630nm wavelength) that will characterize future neutrinoless double beta decay experiments on the isotope 82 Se and based on ZnSe crystals, such as LUCIFER. The coupling between source and light detector reproduces the configuration used in scintillating bolometers. The present measurement clarifies the role of SiO 2 coating and describes a method and a set-up that can be extended to the study of other types of coatings and luminescent materials

Effect of SiO2 coating in bolometric Ge light detectors for rare event searches

Science.gov (United States)

Beeman, J. W.; Gentils, A.; Giuliani, A.; Mancuso, M.; Pessina, G.; Plantevin, O.; Rusconi, C.

2013-05-01

In germanium-based light detectors for scintillating bolometers, a SiO2 anti-reflective coating is often applied on the side of the germanium wafer exposed to light with the aim to improve its light collection efficiency. In this paper, we report about a measurement, performed in the temperature range 25-35 mK, of the light-collection increase obtained thanks to this method, which resulted to be of the order of 20%. The procedure followed has been carefully selected in order to minimize systematic effects. The employed light sources have the same spectral features (peaking at ˜630 nm wavelength) that will characterize future neutrinoless double beta decay experiments on the isotope 82Se and based on ZnSe crystals, such as LUCIFER. The coupling between source and light detector reproduces the configuration used in scintillating bolometers. The present measurement clarifies the role of SiO2 coating and describes a method and a set-up that can be extended to the study of other types of coatings and luminescent materials.

The Role of SiO2 Gas in the Operation of Anti-Corrosion Coating Produced by PVD

Directory of Open Access Journals (Sweden)

Meysam Zarchi

2015-09-01

Full Text Available This study examined theSiO2 gas present in the coatings used in corrosion industry.These layers have been created by physical vapor deposition (PVD, with an appropriate performance. Sublimation of SiO2is used to protect PVD aluminum flakes from water corrosionand to generate highly porous SiO2 flakes with holes in the nanometer range. SiOx/Al/SiOx sandwiches were made as well as Ag loaded porous SiO2 as antimicrobial filler.

Synthesis and Luminescence Properties of Yellow-emitting SiO2/Zn2SiO4: Mn Nanocomposite

Directory of Open Access Journals (Sweden)

Karim OMRI

2014-05-01

Full Text Available Yellow light emitting Mn2+-doped b-Zn2SiO4 phosphor nanoparticles embedded in SiO2 host matrix, were prepared by a simple solid-phase reaction under natural atmosphere at 1500 °C for 2 hours after the incorporation of manganese doped zinc oxide nanoparticles in silica using sol-gel method. The SiO2/Zn2SiO4:Mn nanocomposite was characterized by X-ray diffraction (XRD, transmission electron microscopy (TEM, scanning electron microscopy (SEM and photoluminescence (PL. The nanopowder was crystallized in triclinic b-Zn2SiO4 phase with a particles size varies between 70 nm and 84 nm. The SiO2/b-Zn2SiO4:Mn nanocomposite exhibited a broad yellow emission band at 575 nm under UV excitation light. The dependence of the intensity and energy position of the obtained PL band on measurement temperature and power excitation will be discussed.

Inorganic Nanocrystals Functionalized Mesoporous Silica Nanoparticles: Fabrication and Enhanced Bio-applications

Directory of Open Access Journals (Sweden)

Tiancong Zhao

2017-12-01

Full Text Available Mesoporous SiO2 nanoparticles (MSNs are one of the most promising materials for bio-related applications due to advantages such as good biocompatibility, tunable mesopores, and large pore volume. However, unlike the inorganic nanocrystals with abundant physical properties, MSNs alone lack functional features. Thus, they are not sufficiently suitable for bio-applications that require special functions. Consequently, MSNs are often functionalized by incorporating inorganic nanocrystals, which provide a wide range of intriguing properties. This review focuses on inorganic nanocrystals functionalized MSNs, both their fabrication and bio-applications. Some of the most utilized methods for coating mesoporous silica (mSiO2 on nanoparticles were summarized. Magnetic, fluorescence and photothermal inorganic nanocrystals functionalized MSNs were taken as examples to demonstrate the bio-applications. Furthermore, asymmetry of MSNs and their effects on functions were also highlighted.

Preparation of Organized Mesoporous Silica from Sodium Metasilicate Solutions in Alkaline Medium using Nonionic Surfactants

Czech Academy of Sciences Publication Activity Database

Zukalová, Markéta; Rathouský, Jiří; Zukal, Arnošt

2003-01-01

Roč. 68, č. 10 (2003), s. 2019-2031 ISSN 0010-0765 Institutional research plan: CEZ:AV0Z4040901 Keywords : mesoporous SiO2 * sodium metasilicate * nonionic surfactants Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 1.041, year: 2003

The Correlation of Pore Size and Bioactivity of Spray-Pyrolyzed Mesoporous Bioactive Glasses

Directory of Open Access Journals (Sweden)

Yu-Jen Chou

2017-05-01

Full Text Available SiO2–CaO–P2O5-based mesoporous bioactive glasses (MBGs were synthesized by spray pyrolysis in this study. Three commonly used non-ionic tri-block copolymers (L121, P123, and F127 with various lengths of hydrophilic chains were applied as structural templates to achieve different pore sizes. A mesoporous structure was observed in each as-prepared specimen, and the results showed that the L121-treated MBG had the largest pore size. The results of bioactivity tests indicated that the growth of hydroxyapatite is related to the pore size of the materials.

Synthesis and Characterization of Ti-Phenyl at SiO2 Core-Shell Nanoparticles Catalyst

International Nuclear Information System (INIS)

Syamsi Aini; Jon Efendi; Syamsi Aini; Jon Efendi

2012-01-01

This study highlights the potential use of Ti-Phenyl at SiO 2 core-shell nanoparticles as heterogeneous catalysis in oxidation reaction. The Ti-Phenyl at SiO 2 was synthesized by reduction of TiCl 4 and diazonium salt with sodium borohydride to produce phenyl titanium nanoparticles (Ti-Phenyl), followed by the silica shell coating using tetraethyl orthosilicate (TEOS). The Ti-Phenyl at SiO 2 nanoparticles were characterized by Fourier transform infrared (FTIR) spectrometer, diffuse reflectance (DR) UV-visible spectrometer, thermogravimetric analyzer (TGA), X-ray diffraction (XRD) spectrometer, field emission scanning electron microscope (FESEM) and transmission electron microscope (TEM). The core-shell size of Ti-Phenyl at SiO 2 was in the range of 40 to 100 nm with its core composed with an agglomeration of Ti-Phenyl. The Ti-Phenyl at SiO 2 was active as a catalyst in the liquid phase epoxidation of 1-octene with aqueous hydrogen peroxide as an oxidant. (author)

The ceramic SiO2 and SiO2-TiO2 coatings on biomedical Ti6Al4VELI titanium alloy

International Nuclear Information System (INIS)

Surowska, B.; Walczak, M.; Bienias, J.

2004-01-01

The paper presents the study of intermediate SiO 2 and SiO 2 -TiO 2 sol-gel coatings and dental porcelain coatings on Ti6Al4VELI titanium alloy. Surface microstructures and wear behaviour by pin-on-disc method of the ceramic coatings were investigated. The analysis revealed: (1) a compact, homogeneous SiO 2 and SiO 2 -TiO 2 coating and (2) that intermediate coatings may provide a durable joint between metal and porcelain, and (3) that dental porcelain on SiO 2 and TiO 2 coatings shows high wear resistance. (author)

Moessbauer studies of magnetic Fe2O3/SiO2 nanocomposite

International Nuclear Information System (INIS)

Lancok, A.; Zaveta, K.; Savii, C.; Barcova, K.

2006-01-01

Fe 2 O 3 /SiO 2 magnetic nanocomposites rich in Fe 2 O 3 have been obtained by annealing at 1000 grad C the xerogel samples, prepared under various conditions. The target concentrations of iron oxide in inert matrix were 20% and 30%. As mesoporous matrices both silica and polyvinyl alcohol - silica hybrid ones were used. The xerogel nanocomposite samples were obtained in situ and by impregnation under ultrasonic activation. All obtained samples were annealed under moderate oxidation conditions (air) and inert atmosphere such as vacuum or nitrogen. Moessbauer spectra were obtained using a conventional Moessbauer spectrometer with a 57 Co/Rh source and constant acceleration. Velocity calibration was done using α-iron, and the Moessbauer parameters are given relative to this standard at room temperature. The Moessbauer spectra contained the sextets of ε-Fe 2 O 3 , hematite, and superparamagnetic component. The content of various phases in the samples depends on the conditions of preparation. In one of the samples also magnetite was present. The ranges of the ε-Fe 2 O 3 area of the samples are 39-76%. The hematite phase is only residual, after transformation due to heat treatment. (authors)

Metalloporphyrins immobilized in Fe3O4@SiO2 mesoporous submicrospheres: Reusable biomimetic catalysts for hydrocarbon oxidation.

Science.gov (United States)

Barbosa, Isaltino A; de Sousa Filho, Paulo C; da Silva, Douglas L; Zanardi, Fabrício B; Zanatta, Lucas D; de Oliveira, Adilson J A; Serra, Osvaldo A; Iamamoto, Yassuko

2016-05-01

We successfully immobilized metalloporphyrins (MeP) in mesoporous silica coating magnetite spheres. In this sense, we prepared two different classes of core@shell supports, which comprise aligned (Fe3O4-AM-MeP, MeP=FeP or MnP) and non-aligned (Fe3O4-NM-MeP, MeP=FeP or MnP) mesoporous magnetic structures. X-ray diffractometry and energy dispersive X-ray spectroscopy confirmed the mesoporous nature of the silica shell of the materials. Magnetization measurements, scanning and transmission electron microscopies (SEM/TEM), electrophoretic mobility (ζ-potential), and infrared spectroscopy (FTIR) also confirm the composition and structure of the materials. The catalysts maintained their catalytic activity during nine reaction cycles toward hydrocarbon oxidation processes without detectable catalyst leaching. The catalysis results revealed a biomimetic pattern of cytochrome P450-type enzymes, thus confirming that the prepared materials are can effectively mimic the activity of such groups. Copyright © 2016 Elsevier Inc. All rights reserved.

Enhanced visible light photocatalytic performance of polyaniline modified mesoporous single crystal TiO{sub 2} microsphere

Energy Technology Data Exchange (ETDEWEB)

Deng, Yaocheng [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Tang, Lin, E-mail: tanglin@hnu.edu.cn [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Zeng, Guangming, E-mail: zgming@hnu.edu.cn [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Dong, Haoran; Yan, Ming; Wang, Jingjing [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China); Hu, Wei [College of Physics and Microelectronics Science, Hunan University, Changsha, 410082 (China); Wang, Jiajia; Zhou, Yaoyu; Tang, Jing [College of Environmental Science and Engineering, Hunan University, Changsha, 410082 (China); Key Laboratory of Environmental Biology and Pollution Control, Hunan University, Ministry of Education, Changsha 410082 (China)

2016-11-30

Highlights: • The mesoporous single crystal microsphere of PANI/MS-TiO{sub 2} improved the light absorption. • The mesoporous structure of MS-TiO{sub 2} can increase the loading amount of PANI. • The synergistic effect between PANI and MS-TiO{sub 2} promoted the separation of charges. • Improved photocatalysis was achieved via PANI modified mesoporous single crystal TiO{sub 2} microsphere. - Abstract: Polyaniline (PANI) modified mesoporous single crystal TiO{sub 2} microsphere (PANI/MS-TiO{sub 2}) with excellent photocatalytic activity was successfully prepared by a simple method of solution evaporation and chemisorption. The X-ray diffraction characterization demonstrated that the whole MS-TiO{sub 2} kept the crystal type of anatase. The nitrogen adsorption-desorption characterization coupled with scanning electron microscopy indicated that the MS-TiO{sub 2} possessed a unique mesoporous structure with high specific surface area, which resulted in the increased load of PANI on the surface of MS-TiO{sub 2} and multiple light reflection in the photocatalyst. The UV–vis diffuse reflectance spectra confirmed that PANI/MS-TiO{sub 2} presented more absorption ability in the visible light range than that of the pristine MS-TiO{sub 2}. The transient photocurrent responses and electrochemical impedance spectroscopy (EIS) indicated the high photo responses and fast photogenerated charge separation efficiency of PANI/MS-TiO{sub 2}. The photocatalytic activity of the PANI/MS-TiO{sub 2} was evaluated by the photodegradation of RhB and MB under visible light irradiation. MS-TiO{sub 2} photocatalyst with different molar ration of PANI had been prepared, and the results showed that the optimal photocatalyst (PANI/MS-TiO{sub 2} (1:40)) exhibited the highest photocatalytic efficiency which is nearly three times as great as that of pristine MS-TiO{sub 2} for the degradation of the RhB and MB under visible light irradiation. The remarkable performance of the PANI

Photocatalytic degradation of Acephate, Omethoate, and Methyl parathion by Fe_3O_4@SiO_2@mTiO_2 nanomicrospheres

International Nuclear Information System (INIS)

Zheng, Lingling; Pi, Fuwei; Wang, Yifan; Xu, Hui; Zhang, Yinzhi; Sun, Xiulan

2016-01-01

Highlights: • An efficient photocatalyst Fe_3O_4@SiO_2@mTiO_2 with high magnetic response and large specific surface area was synthesized. • Photocatalytic efficiency of Fe_3O_4@SiO_2@mTiO_2 on Acephate, Omethoate, and Methyl Parathion was higher than TiO_2 P-25. • Possible photocatalytic degradation mechanisms for the Acephate, Omethoate, and Methyl Parathion were proposed. - Abstract: A novel magnetic mesoporous nanomicrospheres Fe_3O_4@SiO_2@mTiO_2 were synthetized and characterized by a series of techniques including FE-TEM, EDS, FE-SEM, PXRD, XPS, BET, TGA as well as VSM, and subsequently tested as a photocatalyst for the degradation of Acephate, Omethoate, and Methyl parathion under UV irradiation. The well-designed nanomicrospheres exhibit a pure and highly crystalline anatase TiO_2 layer, large specific surface area, and high-magnetic-response. Photocatalytic degradation of the three organophosphorus pesticides (OPPs) and the formation intermediates were identified using HPLC, TOC-V_c_p_n, IC, pH meter and GC–MS. Acephate, Omethoate, and Methyl parathion disappeared after 45 min, 45 min, and 80 min UV illumination, respectively. At the end of the treatment, the total organic carbon (TOC) of the OPPs was reduced 80–85%. The main mineralization products were SO_4"2"−, NO_3"− and PO_4"3"− and Omethoate additionally formed NO_2"−. Based on the results, we proposed the photocatalytic degradation pathways for Acephate, Omethoate, and Methyl parathion.

New intelligent multifunctional SiO2/VO2 composite films with enhanced infrared light regulation performance, solar modulation capability, and superhydrophobicity.

Science.gov (United States)

Wang, Chao; Zhao, Li; Liang, Zihui; Dong, Binghai; Wan, Li; Wang, Shimin

2017-01-01

Highly transparent, energy-saving, and superhydrophobic nanostructured SiO 2 /VO 2 composite films have been fabricated using a sol-gel method. These composite films are composed of an underlying infrared (IR)-regulating VO 2 layer and a top protective layer that consists of SiO 2 nanoparticles. Experimental results showed that the composite structure could enhance the IR light regulation performance, solar modulation capability, and hydrophobicity of the pristine VO 2 layer. The transmittance of the composite films in visible region ( T lum ) was higher than 60%, which was sufficient to meet the requirements of glass lighting. Compared with pristine VO 2 films and tungsten-doped VO 2 film, the near IR control capability of the composite films was enhanced by 13.9% and 22.1%, respectively, whereas their solar modulation capability was enhanced by 10.9% and 22.9%, respectively. The water contact angles of the SiO 2 /VO 2 composite films were over 150°, indicating superhydrophobicity. The transparent superhydrophobic surface exhibited a high stability toward illumination as all the films retained their initial superhydrophobicity even after exposure to 365 nm light with an intensity of 160 mW . cm -2 for 10 h. In addition, the films possessed anti-oxidation and anti-acid properties. These characteristics are highly advantageous for intelligent windows or solar cell applications, given that they can provide surfaces with anti-fogging, rainproofing, and self-cleaning effects. Our technique offers a simple and low-cost solution to the development of stable and visible light transparent superhydrophobic surfaces for industrial applications.

Catalytic hydrodeoxygenation of 2-methoxy phenol and dibenzofuran over Pt/mesoporous zeolites

International Nuclear Information System (INIS)

Lee, Hyung Won; Jun, Bo Ram; Kim, Hannah; Kim, Do Heui; Jeon, Jong-Ki; Park, Sung Hoon; Ko, Chang Hyun; Kim, Tae-Wan; Park, Young-Kwon

2015-01-01

The hydrodeoxygenation of 2-methoxy phenol and dibenzofuran, which are representative model compounds of bio-oil, was performed using two different Pt/mesoporous zeolite catalysts, Pt/mesoporous Y and Pt/mesoporous MFI. The reforming of 2-methoxy phenol and dibenzofuran via catalytic hydrodeoxygenation was investigated using a batch reactor at 40 bar and 250 °C. The characteristics of the catalysts were analyzed by N 2 adsorption-desorption, X-ray diffraction, and NH 3 temperature programmed desorption. Pt/mesoporous zeolite catalysts containing both strong acid sites and mesopores showed the higher conversion of 2-methoxy phenol than Pt/SiO 2 and Pt/Si-MCM-48 with no acid sites, Pt/γ-Al 2 O 3 , and a mixture of mesoporous Y and Pt/SiO 2 , indicating the importance of both Pt and strong acid sites for high catalytic activity. Among the two Pt/mesoporous zeolite catalysts tested, the conversion of 2-methoxy phenol to cyclohexane over Pt/mesoporous Y was much higher than that over the Pt/mesoporous MFI. This was attributed to the better textural properties, such as surface area, pore volume and micropore size, compared to those of Pt/mesoporous MFI. The catalytic conversions of dibenzofuran obtained using two Pt/mesoporous zeolite catalysts were similar and the main products were 1,1′-bicyclohexyl, cyclopentylmethyl-cyclohexane and cyclohexane. In addition, the reaction mechanisms of 2-methoxy phenol and dibenzofuran over Pt/mesoporous zeolite were suggested. - Highlights: • HDO of 2-methoxy phenol and dibenzofuran was performed over Pt/mesoporous zeolites. • Pt/mesoporous zeolites have mesopores and strong acid sites. • Main product of HDO of 2-methoxy phenol was cyclohexane. • Main products of HDO of dibenzofuran were bicyclohexyl (BCH), i-BCH, and cyclohexane

Association behaviour of 241Am(III) on SiO2(amorphous) and SiO2(quartz) colloids

International Nuclear Information System (INIS)

Degueldre, C.; Wernli, B.

1993-01-01

SiO 2 colloids have been identified as a potential vector for enhancing radionuclide transport in granitic groundwater and in concrete pore water. The sorption behaviour of 241 Am(III) on SiO 2 colloids was studied as a function of americium concentration pH (5-12), colloid concentration, ionic strength, temperature and SiO 2 allotropic species. The Am(III) sorption mechanism on amorphous silica is different from that on quartz. For SiO 2(amorphous) solution, the variation of log K p (ml g -1 ) with pH is linear (pH=5-9) with a slope of +1 indicating a one proton exchange mechanism. The colloid concentration (ppm) affects the sorption and log K p 3.7-0.67 log [SiO 2 ] (pH = 6). K p increases insignificantly when the ionic strength decreases. It shows no significant variation, however, with the Am concentration. On amorphous silica, the Am(III) sorption is driven by proton exchange from the silanol groups. For SiO 2 (quartz), log K p is constant over a large range of quartz concentration in suspension and the variation of log K p with pH is about linear (pH = 5-12), with a slope of 0.28, indicating a more complex exchange mechanism. Reactions taking into account the interaction of positive Am(OH) w (3-w)+ species on to the negatively charged quartz surface are suggested. (author)

SiO2 Antireflection Coatings Fabricated by Electron-Beam Evaporation for Black Monocrystalline Silicon Solar Cells

Directory of Open Access Journals (Sweden)

Minghua Li

2014-01-01

Full Text Available In this work we prepared double-layer antireflection coatings (DARC by using the SiO2/SiNx:H heterostructure design. SiO2 thin films were deposited by electron-beam evaporation on the conventional solar cell with SiNx:H single-layer antireflection coatings (SARC, while to avoid the coverage of SiO2 on the front side busbars, a steel mask was utilized as the shelter. The thickness of the SiNx:H as bottom layer was fixed at 80 nm, and the varied thicknesses of the SiO2 as top layer were 105 nm and 122 nm. The results show that the SiO2/SiNx:H DARC have a much lower reflectance and higher external quantum efficiency (EQE in short wavelengths compared with the SiNx:H SARC. A higher energy conversion efficiency of 17.80% was obtained for solar cells with SiO2 (105 nm/SiNx:H (80 nm DARC, an absolute conversion efficiency increase of 0.32% compared with the conventional single SiNx:H-coated cells.

Functionalized Mesoporous Silica Membranes for CO2 Separation Applications

Directory of Open Access Journals (Sweden)

Hyung-Ju Kim

2015-01-01

Full Text Available Mesoporous silica molecular sieves are emerging candidates for a number of potential applications involving adsorption and molecular transport due to their large surface areas, high pore volumes, and tunable pore sizes. Recently, several research groups have investigated the potential of functionalized mesoporous silica molecular sieves as advanced materials in separation devices, such as membranes. In particular, mesoporous silica with a two- or three-dimensional pore structure is one of the most promising types of molecular sieve materials for gas separation membranes. However, several important challenges must first be addressed regarding the successful fabrication of mesoporous silica membranes. First, a novel, high throughput process for the fabrication of continuous and defect-free mesoporous silica membranes is required. Second, functionalization of mesopores on membranes is desirable in order to impart selective properties. Finally, the separation characteristics and performance of functionalized mesoporous silica membranes must be further investigated. Herein, the synthesis, characterization, and applications of mesoporous silica membranes and functionalized mesoporous silica membranes are reviewed with a focus on CO2 separation.

Volatile Organic Compounds Sensing Using Optical Fibre Long Period Grating with Mesoporous Nano-Scale Coating

Directory of Open Access Journals (Sweden)

Jiri Hromadka

2017-02-01

Full Text Available A long period grating (LPG modified with a mesoporous film infused with a calixarene as a functional compound was employed for the detection of individual volatile organic compounds (VOCs and their mixtures. The mesoporous film consisted of an inorganic part, SiO2 nanoparticles (NPs, along with an organic moiety of poly(allylamine hydrochloride polycation PAH, which was finally infused with the functional compound, p-sulphanato calix[4]arene (CA[4] or p-sulphanato calix[8]arene (CA[8]. The LPG sensor was designed to operate at the phase matching turning point to provide the highest sensitivity. The sensing mechanism is based on the measurement of the refractive index (RI change induced by a complex of the VOCs with calixarene. The LPG, modified with a coating of 5 cycles of (SiO2 NPs/PAH and infused with CA[4] or CA[8], was exposed to chloroform, benzene, toluene and acetone vapours. The British Standards test of the VOCs emissions from material (BS EN ISO 16000-9:2006 was used to test the LPG sensor performance.

Fabrication of hierarchical graphene@Fe3O4@SiO2@polyaniline quaternary composite and its improved electrochemical performance

International Nuclear Information System (INIS)

Wang, Lei; Zhu, Jianfeng; Yang, Haibo; Wang, Fen; Qin, Yi; Zhao, Ting; Zhang, Pei

2015-01-01

Highlights: • Graphene@Fe 3 O 4 @SiO 2 @polyaniline hierarchical structures have been fabricated. • The reflection loss of the composites is below −10 dB in 10.5–16.3 GHz. • The maximum absorption of the composites is −40.7 dB at 12.5 GHz. - Abstract: Hierarchical graphene@Fe 3 O 4 @SiO 2 @polyaniline quaternary composite is fabricated subtly. Their microwave absorption properties are also investigated in the 2–18 GHz frequency range. Transmission electron microscopy (TEM) and scanning electron microscope (SEM) reveal that Fe 3 O 4 @SiO 2 @polyaniline core@shell@shell heteronanostructures are densely covered on the surfaces of graphene, and form hierarchical structures. Compared with two-dimensional binary nanocomposites of graphene@Fe 3 O 4 , the hierarchical structure exhibits enhanced EM absorption in terms of both the maximum reflection loss value and the absorption bandwidth. The maximum reflection loss value can reach −40.7 dB at 12.5 GHz with a thickness of 2.5 mm and the bandwidth corresponding to the reflection loss below −10 dB is 5.8 GHz (from 10.5 to 16.3 GHz)

Do SiO 2 and carbon-doped SiO 2 nanoparticles melt? Insights from QM/MD simulations and ramifications regarding carbon nanotube growth

Science.gov (United States)

Page, Alister J.; Chandrakumar, K. R. S.; Irle, Stephan; Morokuma, Keiji

2011-05-01

Quantum chemical molecular dynamics (QM/MD) simulations of pristine and carbon-doped SiO 2 nanoparticles have been performed between 1000 and 3000 K. At temperatures above 1600 K, pristine nanoparticle SiO 2 decomposes rapidly, primarily forming SiO. Similarly, carbon-doped nanoparticle SiO 2 decomposes at temperatures above 2000 K, primarily forming SiO and CO. Analysis of the physical states of these pristine and carbon-doped SiO 2 nanoparticles indicate that they remain in the solid phase throughout decomposition. This process is therefore one of sublimation, as the liquid phase is never entered. Ramifications of these observations with respect to presently debated mechanisms of carbon nanotube growth on SiO 2 nanoparticles will be discussed.

Effect of oxide charge trapping on x-ray photoelectron spectroscopy of HfO2/SiO2/Si structures

International Nuclear Information System (INIS)

Abe, Yasuhiro; Miyata, Noriyuki; Suzuki, Haruhiko; Kitamura, Koji; Igarashi, Satoru; Nohira, Hiroshi; Ikenaga, Eiji

2009-01-01

We examined the effects of interfacial SiO 2 layers and a surface metal layer on the photoelectron spectra of HfO 2 /SiO 2 /Si structures by hard X-ray photoemission spectroscopy with synchrotron radiation as well as conventional X-ray photoelectron spectroscopy (XPS). The Hf 4f and Hf 3d photoelectron peaks broadened and shifted toward a higher binding energy with increasing thickness of the interfacial SiO 2 layer, even though photoelectrons may have been emitted from the HfO 2 layer with the same chemical composition. Thinning the interfacial Si oxide layer to approximately one monolayer and depositing a metal layer on the HfO 2 surface suppressed these phenomena. The O 1s photoelectron spectra revealed marked differences between the metal- and nonmetal-deposited HfO 2 /SiO 2 /Si structures; HfO 2 and SiO 2 components in the O 1s photoelectron spectra for the metal-deposited structures were observed at reasonably separated binding energies, but those for the nonmetal-deposited structures were not separated clearly. From this behavior concerning the effects of interfacial SiO 2 and surface metal layers, we concluded that the Hf 4f, Hf 3d, and O 1s spectra measured from the HfO 2 /SiO 2 /Si structures did not reflect actual chemical bonding states. We consider that potential variations in the HfO 2 film owing to charge trapping strongly affect the measured photoelectron spectra. On the basis of angle-resolved XPS measurements, we propose that positive charges are trapped at the HfO 2 surface and negative charges are trapped inside the HfO 2 layer. (author)

Influence of radiation-damages on parameters of lattice oscillations in crystalline and vitreous SiO2

International Nuclear Information System (INIS)

Abdukadyrova, I.Kh.

2008-01-01

Using IR reflection spectroscopy, the influence of radiation-induced disturbances on a number of parameters of lattice oscillations in two SiO 2 modifications was investigated. Radiation kinetics of changes in spectral characteristics of fundamental oscillations in SiO 2 crystalline and glassy states was determined. Dose dependences of both reflectivity and degenerate mode vibrational frequency were found to show minima whose locations were governed by a type of a sample. Under higher doses of neutron radiation (10 21 cm -2 ), certain characteristics of bands were observed to be of the same values for the both materials modified. The features of radiation kinetics were found for dynamic parameters of the samples. It was deduced that specific character of radiation-induced changes observed in spectral and dynamic parameters of oscillations in the region of degenerate modes was due to both the accumulation of radiation damages and a change in the force field surrounding bridge-type bonds which was related with the change in the SiO 2 structure. (authors)

SiO2 Nanopillars on Microscale Roughened Surface of GaN-Based Light-Emitting Diodes by SILAR-Based Method

Directory of Open Access Journals (Sweden)

X. F. Zeng

2013-01-01

Full Text Available We reported the SiO2 nanopillars on microscale roughened surface on GaN-based LED to enhance light-extraction efficiency. ZnO nanoparticles were deposited on SiO2 as an etching mask before ICP etching SiO2 by successive ionic layer adsorption and reaction method (SILAR, and the different heights of SiO2 nanopillars on microroughened ITO/GaN were obtained after etching. Compared to a regular (flat surface GaN-based LED, the light output power for a LED with microroughening was increased by 33%. Furthermore, the proposed LEDs with SiO2 nanopillars on microroughened surface show the enhancement in light output power by 42.7%–49.1% at 20 mA. The increase in light output power is mostly attributed to reduction in Fresnel reflection by rough surface. The height of SiO2 nanopillars was increasing cause resulting in more rough on the microscale surface of GaN-based LEDs.

Preliminary study in development of glass-ceramic based on SiO2-LiO2 system, starting of different SiO2 starting powders

International Nuclear Information System (INIS)

Daguano, J.K.M.F.; Santos, F.A.; Santos, C.; Marton, L.F.M.; Conte, R.A.; Rodrigues Junior, D.; Melo, F.C.L.

2009-01-01

In this work, lithium disilicate glass-ceramics were developed starting of the rice ash- SiO 2 and Li 2 CO 3 powders. The results were compared with glass ceramics based on the lithium disilicate obtained by commercial SiO 2 powders. Glass were melted at 1580 deg C, and annealed at 850 deg C. X-Ray diffraction and scanning electron microscopy were used for characterization of the materials, and hardness and fracture toughness were evaluated using Vickers indentation method. Glasses with amorphous structure were obtained in both materials. After annealing, 'rice-ash' samples presented Li 2 SiO 3 and residual SiO 2 as crystalline phases. On the other side, commercial SiO 2 - Samples presented only Li 2 Si 2 O 5 as crystalline phases and the better results of hardness and fracture toughness. (author)

Total Ionizing Dose Effects of Si Vertical Diffused MOSFET with SiO2 and Si3N4/SiO2 Gate Dielectrics

Directory of Open Access Journals (Sweden)

Jiongjiong Mo

2017-01-01

Full Text Available The total ionizing dose irradiation effects are investigated in Si vertical diffused MOSFETs (VDMOSs with different gate dielectrics including single SiO2 layer and double Si3N4/SiO2 layer. Radiation-induced holes trapping is greater for single SiO2 layer than for double Si3N4/SiO2 layer. Dielectric oxidation temperature dependent TID effects are also studied. Holes trapping induced negative threshold voltage shift is smaller for SiO2 at lower oxidation temperature. Gate bias during irradiation leads to different VTH shift for different gate dielectrics. Single SiO2 layer shows the worst negative VTH at VG=0 V, while double Si3N4/SiO2 shows negative VTH shift at VG=-5 V, positive VTH shift at VG=10 V, and negligible VTH shift at VG=0 V.

Thermodynamics of Bi2O3-SiO2 system

Directory of Open Access Journals (Sweden)

Onderka B.

2017-01-01

Full Text Available Thermodynamic properties of the liquid Bi2O3-SiO2 solutions were determined from the results of the electrochemical measurements by use of the solid oxide galvanic cells with YSZ (Yttria-Stabilized-Zirconia electrolyte. Activities of Bi2O3 in the solutions were determined for 0.2, 0.3, 0.4, and 0.5 SiO2 mole fractions in the temperature range 1073-1293 K from measured electromotive force (e.m.f of the solid electrolyte galvanic cell: Bi, Bi2O3-SiO2 | YSZ | air (pO2 = 0.213 bar Additionally, heat capacity data obtained for two solid phases 6Bi2O3•SiO2 and 2Bi2O3•3SiO2 were included into optimization of thermodynamic properties of the system. Optimization procedure was supported by differential thermal analysis (DTA data obtained in this work as well as those accepted from the literature. Using the data obtained in this work, and the information about phase equilibria found in the literature, binary system Bi2O3-SiO2 was assessed with the ThermoCalc software.

Enhanced Visible Transmittance of Thermochromic VO2 Thin Films by SiO2 Passivation Layer and Their Optical Characterization

Directory of Open Access Journals (Sweden)

Jung-Hoon Yu

2016-07-01

Full Text Available This paper presents the preparation of high-quality vanadium dioxide (VO2 thermochromic thin films with enhanced visible transmittance (Tvis via radio frequency (RF sputtering and plasma enhanced chemical vapor deposition (PECVD. VO2 thin films with high Tvis and excellent optical switching efficiency (Eos were successfully prepared by employing SiO2 as a passivation layer. After SiO2 deposition, the roughness of the films was decreased 2-fold and a denser structure was formed. These morphological changes corresponded to the results of optical characterization including the haze, reflectance and absorption spectra. In spite of SiO2 coating, the phase transition temperature (Tc of the prepared films was not affected. Compared with pristine VO2, the total layer thickness after SiO2 coating was 160 nm, which is an increase of 80 nm. Despite the thickness change, the VO2 thin films showed a higher Tvis value (λ 650 nm, 58% compared with the pristine samples (λ 650 nm, 43%. This enhancement of Tvis while maintaining high Eos is meaningful for VO2-based smart window applications.

Kinetic and catalytic analysis of mesoporous metal oxides on the oxidation of Rhodamine B

Science.gov (United States)

Xaba, Morena S.; Noh, Ji-Hyang; Mokgadi, Keabetswe; Meijboom, Reinout

2018-05-01

In this study, we demonstrate the synthesis and catalytic activity of different mesoporous transition metal oxides, silica (SiO2), copper oxide (CuO), chromium oxide (Cr2O3), iron oxide (Fe2O3) cobalt oxide (Co3O4), cerium oxide (CeO2) and nickel oxide (NiO), on the oxidation of a pollutant dye, Rhodamine B (RhB). These metal oxides were synthesized by inverse micelle formation method and characterized by transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray diffraction (XRD), adsorption-desorption isotherms (BET) and H2-temperature programmed reduction (TPR). UV-vis spectrophotometry was used to monitor the time-resolved absorbance of RhB at λmax = 554 nm. Mesoporous copper oxide was calcined at different final heating temperatures of 250, 350, 450 and 550 °C, and each mesoporous copper oxide catalyst showed unique physical properties and catalytic behavior. Mesoporous CuO-550 with the smallest characteristic path length δ, proved to be the catalyst of choice for the oxidation of RhB in aqueous media. We observed that the oxidation of RhB in aqueous media is dependent on the crystallite size and characteristic path length of the mesoporous metal oxide. The Langmuir-Hinshelwood model was used to fit the experimental data and to prove that the reaction occurs on the surface of the mesoporous CuO. The thermodynamic parameters, EA, ΔH#, ΔS# and ΔG# were calculated and catalyst recycling and reusability were demonstrated.

Efficient photodecomposition of herbicide imazapyr over mesoporous Ga2O3-TiO2 nanocomposites.

Science.gov (United States)

Ismail, Adel A; Abdelfattah, Ibrahim; Faisal, M; Helal, Ahmed

2018-01-15

The unabated release of herbicide imazapyr into the soil and groundwater led to crop destruction and several pollution-related concerns. In this contribution, heterogeneous photocatalytic technique was employed utilizing mesoporous Ga 2 O 3 -TiO 2 nanocomposites for degrading imazapyr herbicide as a model pollutant molecule. Mesoporous Ga 2 O 3 -TiO 2 nanocomposites with varied Ga 2 O 3 contents (0-5wt%) were synthesized through sol-gel process. XRD and Raman spectra exhibited extremely crystalline anatase TiO 2 phase at low Ga 2 O 3 content which gradually reduced with the increase of Ga 2 O 3 content. TEM images display uniform TiO 2 particles (10±2nm) with mesoporous structure. The mesoporous TiO 2 exhibits large surface areas of 167m 2 g -1 , diminished to 108m 2 g -1 upon 5% Ga 2 O 3 incorporation, with tunable mesopore diameter in the range of 3-9nm. The photocatalytic efficiency of synthesized Ga 2 O 3 -TiO 2 nanocomposites was assessed by degrading imazapyr herbicide and comparing with commercial photocatalyst UV-100 and mesoporous Ga 2 O 3 under UV illumination. 0.1% Ga 2 O 3 -TiO 2 nanocomposite is considered the optimum photocatalyst, which degrades 98% of imazapyr herbicide within 180min. Also, the photodegradation rate of imazapyr using 0.1% Ga 2 O 3 -TiO 2 nanocomposite is nearly 10 and 3-fold higher than that of mesoporous Ga 2 O 3 and UV-100, respectively. The high photonic efficiency and long-term stability of the mesoporous Ga 2 O 3 -TiO 2 nanocomposites are ascribed to its stronger oxidative capability in comparison with either mesoporous TiO 2 , Ga 2 O 3 or commercial UV-100. Copyright © 2017 Elsevier B.V. All rights reserved.

Preparation and Characterization of Fluorescent SiO2 Microspheres

Science.gov (United States)

Xu, Cui; Zhang, Hao; Guan, Ruifang

2018-01-01

Fluorescent compound without typical fluorophores was synthesized with citric acid (CA) and aminopropyltriethoxysilane (APTS) firstly, and then it was grafted to the surface of the prepared SiO2 microspheres by chemical reaction. The fluorescent SiO2 microspheres with good fluorescent properties were obtained by optimizing the reaction conditions. And the morphology and structure of the fluorescent SiO2 microspheres have been characterized by scanning electron microscopy (SEM) and fourier transform infrared (FTIR) spectroscopy. The results showed that the preparation of fluorescent SiO2 microspheres have good monodispersity and narrow particle size distribution. Moreover, the fluorescent SiO2 microspheres can be applied to detect Fe3+ in aqueous solution, prepare fluorescent SiO2 rubber, and have potential to be applied in the fluorescent labeling and fingerprint appearing technique fields.

Photoluminescence analysis of Ce3+:Zn2SiO4 & Li++ Ce3+:Zn2SiO4: phosphors by a sol-gel method

Science.gov (United States)

Babu, B. Chandra; Vandana, C. Sai; Guravamma, J.; Rudramadevi, B. Hemalatha; Buddhudu, S.

2015-06-01

Here, we report on the development and photoluminescence analysis of Zn2SiO4, Ce3+:Zn2SiO4 & Li+ + Ce3+: Zn2SiO4 novel powder phosphors prepared by a sol-gel technique. The total amount of Ce3+ ions was kept constant in this experiment at 0.05 mol% total doping. The excitation and emission spectra of undoped (Zn2SiO4) and Ce3+ doped Zn2SiO4 and 0.05 mol% Li+ co-doped samples have been investigated. Cerium doped Zn2SiO4 powder phosphors had broad blue emission corresponding to the 2D3/2→2FJ transition at 443nm. Stable green-yellow-red emission has been observed from Zn2SiO4 host matrix and also we have been observed the enhanced luminescence of Li+ co-doped Zn2SiO4:Ce3+. Excitation and emission spectra of these blue luminescent phosphors have been analyzed in evaluating their potential as luminescent screen coating phosphors.

Investigating the Trimethylaluminium/Water ALD Process on Mesoporous Silica by In Situ Gravimetric Monitoring

Directory of Open Access Journals (Sweden)

Verena E. Strempel

2018-05-01

Full Text Available A low amount of AlOx was successfully deposited on an unordered, mesoporous SiO2 powder using 1–3 ALD (Atomic Layer Deposition cycles of trimethylaluminium and water. The process was realized in a self-built ALD setup featuring a microbalanceand a fixed particle bed. The reactor temperature was varied between 75, 120, and 200 °C. The self-limiting nature of the deposition was verified by in situ gravimetric monitoring for all temperatures. The coated material was further analyzed by nitrogen sorption, inductively coupled plasma-optical emission spectroscopy, powder X-ray diffraction, high-resolution transmission electron microscopy, attenuated total reflection Fourier transformed infrared spectroscopy, and elemental analysis. The obtained mass gains correspond to average growth between 0.81–1.10 Å/cycle depending on substrate temperature. In addition, the different mass gains during the half-cycles in combination with the analyzed aluminum content after one, two, and three cycles indicate a change in the preferred surface reaction of the trimethylaluminium molecule from a predominately two-ligand exchange with hydroxyl groups to more single-ligand exchange with increasing cycle number. Nitrogen sorption isotherms demonstrate (1 homogeneously coated mesopores, (2 a decrease in surface area, and (3 a reduction of the pore size. The experiment is successfully repeated in a scale-up using a ten times higher substrate batch size.

Ionic conductivity of sodium silicate glasses grown within confined volume of mesoporous silica template

Science.gov (United States)

Chatterjee, Soumi; Saha, Shyamal Kumar; Chakravorty, Dipankar

2018-04-01

Nanodimensional sodium silicate glasses of composition 30Na2O.70SiO2 has been prepared within the pores of 5.5 nm of mesoporous silica as a template using the surfactant P123. The nanocomposite was characterized by X-ray diffraction, transmission electron microscope, and X-ray photoelectron spectroscopy. Electrical conductivity of the sample was studied by ac impedance spectroscopy. The activation energy for ionic conduction was found to be 0.13 eV with dc conductivity at room temperature of 10-6 S-cm-1. This is attributed to the creation of oxygen ion vacancies at the interface of mesoporous silica and nanoglass arising out of the presence of Si2+ species in the system. These nanocomposites are expected to be useful for applications in sodiumion battery for storage of renewable energy.

Synthesis and characterization of nanoparticulate MnS within the pores of mesoporous silica

International Nuclear Information System (INIS)

Barry, Louse; Copley, Mark; Holmes, Justin D.; Otway, David J.; Kazakova, Olga; Morris, Michael A.

2007-01-01

Mesoporous silica was loaded with nanoparticulate MnS via a simple post-synthesis treatment. The mesoporous material that still contained surfactant was passivated to prevent MnS formation at the surface. The surfactant was extracted and a novel manganese ethylxanthate was used to impregnate the pore network. This precursor thermally decomposes to yield MnS particles that are smaller or equal to the pore size. The particles exhibit all three common polymorphs. The passivation treatment is most effective at lower loadings because at the highest loadings (SiO 2 :MnS molar ratio of 6:1) large particles (>50 nm) form at the exterior of the mesoporous particles. The integrity of the mesoporous network is maintained through the preparation and high order is maintained. The MnS particles exhibit unexpected ferromagnetism at low temperatures. Strong luminescence of these samples is observed and this suggests that they may have a range of important application areas. - Graphical abstract: A novel manganese ethylxanthate precursor was used to impregnate the pore network of mesoporous silica and was decomposed to yield MnS particles smaller or equal to the pore size. The particles exhibit all three common polymorphs, demonstrate unexpected ferromagnetism at low temperatures and display a strong luminescence

Effective surface modification of MnFe2O4@SiO2@PMIDA magnetic nanoparticles for rapid and high-density antibody immobilization

Science.gov (United States)

Rashid, Zahra; Soleimani, Masoud; Ghahremanzadeh, Ramin; Vossoughi, Manouchehr; Esmaeili, Elaheh

2017-12-01

The present study is aimed at the synthesis of MnFe2O4@SiO2@PMIDA in terms of highly efficient sensing platform for anti-prostate specific membrane antigen (PSMA) immobilization. Superparamagnetic manganese ferrite nanoparticles were synthesized following co-precipitation method and then SiO2 shell was coated on the magnetic core with tetraethyl orthosilicate (TEOS) through a silanization reaction to prevent oxidation, agglomeration and, increase the density of OH groups on the surface of MnFe2O4. Subsequently, MnFe2O4@SiO2@PMIDA obtained as a result of the reaction between N-(phosphonomethyl)iminodiacetic acid (PMIDA) and MnFe2O4@SiO2. The reactive carboxyl groups on the surface of magnetic nanoparticles can efficiently conjugate to a monoclonal antibody, specific to PSMA, which was confirmed by enzyme-linked immune sorbent assay (ELISA). Thus, this kind of functionalized magnetic nanoparticles is promising to be utilized in the improvement of ELISA-based biosensors and also will be effective in a variety of biomedical applications such as cell separation, diagnosis, and monitoring of human diseases.

Synthesis and characterization of silica mesoporous material produced by hydrothermal continues pH adjusting path way

Directory of Open Access Journals (Sweden)

A. Salemi Golezani

2016-08-01

Full Text Available Mesoporous silica molecular sieves MCM-41 were synthesized under hydrothermal conditions. For this purpose, a solution with a molar coefficient of water, cetyltri-methyl ammonium bromide surfactants as template and sodium silicate as the source of SiO2 are used. Phase formation, morphology and gas absorption properties were investigated by XRD and BET analysis, respectively. The results showed that silica mesoporous material has been successfully synthesized. A favorable special surface and porosity volume together with regular arrangement of nano metric-hexagonal porosities were obtained from this synthesis. Thickness of the wall and average diameter of the pores are 0.8 nm and 4 nm, respectively.

Synthesis of Ordered Mesoporous CuO/CeO2 Composite Frameworks as Anode Catalysts for Water Oxidation

Directory of Open Access Journals (Sweden)

Vassiliki Markoulaki Ι

2015-11-01

Full Text Available Cerium-rich metal oxide materials have recently emerged as promising candidates for the photocatalytic oxygen evolution reaction (OER. In this article, we report the synthesis of ordered mesoporous CuO/CeO2 composite frameworks with different contents of copper(II oxide and demonstrate their activity for photocatalytic O2 production via UV-Vis light-driven oxidation of water. Mesoporous CuO/CeO2 materials have been successfully prepared by a nanocasting route, using mesoporous silica as a rigid template. X-ray diffraction, electron transmission microscopy and N2 porosimetry characterization of the as-prepared products reveal a mesoporous structure composed of parallel arranged nanorods, with a large surface area and a narrow pore size distribution. The molecular structure and optical properties of the composite materials were investigated with Raman and UV-Vis/NIR diffuse reflectance spectroscopy. Catalytic results indicated that incorporation of CuO clusters in the CeO2 lattice improved the photochemical properties. As a result, the CuO/CeO2 composite catalyst containing ~38 wt % CuO reaches a high O2 evolution rate of ~19.6 µmol·h−1 (or 392 µmol·h−1·g−1 with an apparent quantum efficiency of 17.6% at λ = 365 ± 10 nm. This OER activity compares favorably with that obtained from the non-porous CuO/CeO2 counterpart (~1.3 µmol·h−1 and pure mesoporous CeO2 (~1 µmol·h−1.

Photocatalytic Removal of Phenol under Natural Sunlight over N-TiO2-SiO2 Catalyst: The Effect of Nitrogen Composition in TiO2-SiO2

Directory of Open Access Journals (Sweden)

Viet-Cuong Nguyen

2009-01-01

Full Text Available In this present work, high specific surface area and strong visible light absorption nitrogen doped TiO2-SiO2 photocatalyst was synthesized by using sol-gel coupled with hydrothermal treatment method. Nitrogen was found to improve the specific surface area while it also distorted the crystal phase of the resulting N-TiO2-SiO2 catalyst. As the N/ (TiO2-SiO2 molar ratio was more than 10%, the derived catalyst presented the superior specific surface area up to 260 m2/g. Nevertheless, its photoactivity towards phenol removal was observed to significantly decrease, which could results from the too low crystallinity. The nitrogen content in N-TiO2-SiO2 catalyst was therefore necessary to be optimized in terms of phenol removal efficiency and found at ca. 5%. Under UVA light and natural sunlight irradiation of 80 min, N(5%-TiO2-SiO2 catalyst presented the phenol decomposition efficiencies of 68 and 100%, respectively. It was also interestingly found in this study that the reaction rate was successfully expressed using a Langmuir-Hinshelwood (L-H model, indicating the L-H nature of photocatalytic phenol decomposition reaction on the N-TiO2-SiO2 catalyst.

THE THERMODYNAMIC PROPERTIES OF MELTS OF DOUBLE SYSTEM MgO – Al2O3, MgO – SiO2, MgO – CaF2, Al2O3 – SiO2, Al2O3 – CaF2, SiO2 – CaF2

Directory of Open Access Journals (Sweden)

В. Судавцова

2012-04-01

Full Text Available Methodology of prognostication of thermodynamics properties of melts is presented from the coordinatesof liquidus of diagram of the state in area of equilibria a hard component is solution, on which energies ofmixing of Gibbs are expected in the double border systems of MgO – Al2O3, MgO – SiO2, MgO – CaF2,Al2O3 – SiO2, Al2O3 - CaF2, SiO2 - CaF2. For the areas of equilibrium there is quasibinary connection(MgAl2O4, Mg2SiO4, Al6Si2O13 – a grout at calculations was used equalization of Hauffe-Wagner. Theobtained data comport with literary

Self-Assembly of TiO2/CdS Mesoporous Microspheres with Enhanced Photocatalytic Activity via Hydrothermal Method

Directory of Open Access Journals (Sweden)

Sujing Yu

2014-01-01

Full Text Available Self assembly of TiO2/CdS mesoporous microspheres was synthesized via hydrothermal method. The samples were characterized by X-ray powder diffraction (XRD, ultraviolet-visible diffuse reflectance spectroscopy (DRS, transmission electron microscopy (TEM, energy-dispersive spectroscopy analysis (EDS, high-resolution transmission electron microscopy (HRTEM, Brunauer-Emmett-Teller (BET, X-ray photoelectron spectroscopy (XPS, and photoluminescence spectra (PL. The as-synthesized TiO2/CdS mesoporous microspheres showed superior photocatalytic activity for the degradation of RhB under either visible light or simulated sunlight irradiation; the 10 wt% TiO2/CdS sample showed the best performance. Moreover, this catalyst showed improved stability, and the activity did not decrease significantly after four recycles. The heterojunction between TiO2 and CdS may be favorable for the transport of photoinduced electrons from CdS to TiO2. In addition, the mesoporous structure could increase the utilization of light energy and facilitate the diffusion of reactants and products during the photocatalytic reaction.

The effect of rare earth dopants on the structure, surface texture and photocatalytic properties of TiO2-SiO2 prepared by sol-gel method

International Nuclear Information System (INIS)

Mohamed, R.M.; Mkhalid, I.A.

2010-01-01

The sol-gel method was successfully used to prepare a series of TiO 2 -SiO 2 and rare earth (RE) (La 3+ , Nd 3+ , Sm 3+ , Gd 3+ )-doped TiO 2 -SiO 2 nanoparticles at a doping level of 3 atomic percent. The structural features of parent TiO 2 -SiO 2 and RE-TiO 2 -SiO 2 fired at 550 o C have been investigated by XRD, UV-diffuse reflection, SEM and nitrogen adsorption measurements at -196 o C. XRD data verified the formation of typical characteristic anatase form in all the prepared RE-doped TiO 2 -SiO 2 samples. In comparison with the pure TiO 2 -SiO 2 samples (ca. 35 nm in diameter), the RE-TiO 2 -SiO 2 samples have relatively small particle size indicating that the doping with RE metal ions can improve the particle morphology, and retard the grain growth of TiO 2 -SiO 2 during heat treatment. The results indicated that Gd 3+ doped TiO 2 -SiO 2 has the lowest bandgap and particle size compared with pure TiO 2 -SiO 2 and other nanoparticles of RE-doped TiO 2 -SiO 2 . The highest surface area (S BET ) and pore volume (V p ) values were recorded for Gd-TiO 2 -SiO 2 as well. The effect of doping on the photoactivity was evaluated by the photocatalytic degradation of EDTA as a probe reaction. Among all the pure and RE-doped TiO 2 -SiO 2 , Gd 3+ -TiO 2 -SiO 2 performed the highest catalytic activity towards the tested reaction. That might be due to its special characteristics of particle size, surface texture and bandgap properties. Details of the synthesis procedure and results of the characterization studies of the produced RE-TiO 2 -SiO 2 are presented in this paper.

Synthesis and in vitro bioactivity of mesoporous bioactive glass scaffolds

International Nuclear Information System (INIS)

Shih, C.J.; Chen, H.T.; Huang, L.F.; Lu, P.S.; Chang, H.F.; Chang, I.L.

2010-01-01

The main objective of the present study was to determine the effect of thermal treatment procedures (calcination temperature, heating rate and duration time) on the synthesis of SiO 2 -CaO-P 2 O 5 mesoporous bioactive glass scaffolds. This is accomplished by thermogravimetric analyses, Fourier transform infrared (FTIR) absorption spectra, X-ray diffraction (XRD) and by analysis of nitrogen adsorption/desorption isotherms. In vitro bioactivity can also be assessed by the cytotoxic effect of the glasses on the NIH-3T3 cell line, and by characterization of MC-3T3-E1 cell attachment.

CO2/N2开关型脒基表面活性剂软模板制备介孔二氧化硅%Synthesis of mesoporous silica using CO2/N2switchable surfactant as soft templates

Institute of Scientific and Technical Information of China (English)

代利; 郑饶君; 马宇萱; 蒋建中; 崔正刚

2015-01-01

模板法是制备介孔 SiO2的常用方法之一,而模板法通常需要脱除模板后才能得到介孔结构.以传统表面活性剂为模板合成介孔二氧化硅,除模板方法还有高温焙烧、溶剂萃取等,但这些方法均存在一定的缺点,如导致结构坍塌、消耗大量溶剂等.本文采用开关型表面活性剂N'-十二烷基-N,N-二甲基乙基脒碳酸氢盐为模板剂,以正硅酸四乙酯(TEOS)为硅源在碱性条件下合成SiO2.与常规除模板法不同,本实验在反应结束后加热并通入N2使表面活性剂分解失去表面活性,用水和丙酮洗涤后得到了形貌规整、孔道有序、具有较高比表面积和孔容的介孔 SiO2.同时还研究了有机盐乙二胺四乙酸二钠(Na2EDTA)对介孔有序度、所得介孔材料比表面积、孔容孔径和模板残留量的影响.%Template method is used widely to synthesize mesoporous silica. However,the mesoporous structure can be obtained only after the templates are removed. Calcination,solvent extraction etc. are frequently used to remove conventional surfactant templates. However,these template removal methods could bring problems such as resulting structure collapse or massive consumption of solvent. In this paper,we synthesized silica using switchable surfactant of N'-dodecyl-N,N-dimethylacetamidinium bicarbonate as templates and tetraethoxysilane (TEOS) as silicon source in alkaline solution. Compared to conventional template removal method,the switchable surfactants decomposed and lost its surface activity by heating the mixture together with N2 injection when the reaction was completed. Mesoporous silica with uniform morphology,ordered mesopore,large specific surface area and pore volume was then obtained after washed with water and acetone. The effect of Na2EDTA on the order of mesopore,specific surface area,pore volume,size of pore and templates residue was discussed.

Preparation, characterization and catalytic behavior of hierachically porous CuO/α-Fe2O3/SiO2 composite material for CO and o-DCB oxidation

Institute of Scientific and Technical Information of China (English)

Xiaodong Ma; Xi Feng; Xuan He; Hongwen Guo; Lu Lü

2011-01-01

Hierachically porous (HP) CuO/α-Fe2O3/SiO2 composite material was fabricated by sol-gel method and multi-hydrothermal processes using HP-SiO2 as support.The resulting material was characterized by N2 adsorption-desorption,X-ray diffraction and scanning electron microscopy.The as-prepared CuO/Fe2O3/HP-SiO2 sample,with α-Fe2O3 and CuO nanocrystals,possessed a co-continuous skeleton,through-macroporous and mesoporous structure.Its catalytic behavior for CO and o-DCB oxidation was investigated.The result showed that CuO/Fe2O3/HP-SiO2 catalyst exhibited high catalytic activity for both CO and o-DCB oxidation,indicating its potential application in combined abatement of CO and chlorinated volatile organic compounds.

Potential energy landscape of an interstitial O2 molecule in a SiO2 film near the SiO2/Si(001) interface

Science.gov (United States)

Ohta, Hiromichi; Watanabe, Takanobu; Ohdomari, Iwao

2008-10-01

Potential energy distribution of interstitial O2 molecule in the vicinity of SiO2/Si(001) interface is investigated by means of classical molecular simulation. A 4-nm-thick SiO2 film model is built by oxidizing a Si(001) substrate, and the potential energy of an O2 molecule is calculated at Cartesian grid points with an interval of 0.05 nm in the SiO2 film region. The result shows that the potential energy of the interstitial site gradually rises with approaching the interface. The potential gradient is localized in the region within about 1 nm from the interface, which coincides with the experimental thickness of the interfacial strained layer. The potential energy is increased by about 0.62 eV at the SiO2/Si interface. The result agrees with a recently proposed kinetic model for dry oxidation of silicon [Phys. Rev. Lett. 96, 196102 (2006)], which argues that the oxidation rate is fully limited by the oxidant diffusion.

Preparation and Characterization of WS2@SiO2 and WS2@PANI Core-Shell Nanocomposites

Directory of Open Access Journals (Sweden)

Hagit Sade

2018-03-01

Full Text Available Two tungsten disulfide (WS2-based core-shell nanocomposites were fabricated using readily available reagents and simple procedures. The surface was pre-treated with a surfactant couple in a layer-by-layer approach, enabling good dispersion of the WS2 nanostructures in aqueous media and providing a template for the polymerization of a silica (SiO2 shell. After a Stöber-like reaction, a conformal silica coating was achieved. Inspired by the resulting nanocomposite, a second one was prepared by reacting the surfactant-modified WS2 nanostructures with aniline and an oxidizing agent in an aqueous medium. Here too, a conformal coating of polyaniline (PANI was obtained, giving a WS2@PANI nanocomposite. Both nanocomposites were analyzed by electron microscopy, energy dispersive X-ray spectroscopy (EDS and FTIR, verifying the core-shell structure and the character of shells. The silica shell was amorphous and mesoporous and the surface area of the composite increases with shell thickness. Polyaniline shells slightly differ in their morphologies dependent on the acid used in the polymerization process and are amorphous like the silica shell. Electron paramagnetic resonance (EPR spectroscopy of the WS2@PANI nanocomposite showed variation between bulk PANI and the PANI shell. These two nanocomposites have great potential to expand the use of transition metals dichalcogenides (TMDCs for new applications in different fields.

Immobilization induced molecular compression of ionic liquid in ordered mesoporous matrix

Science.gov (United States)

Tripathi, Alok Kumar; Singh, Rajendra Kumar

2018-02-01

In this work, ionic liquid (IL) 1-ethyl-3-methylimidazolium bis(fluorosulfonyl)imide ([EMIM][FSI]) has been immobilized into ordered mesoporous silica MCM-41 by a physical imbibition process. Transmission electron microscopy confirms the filling of mesopores of MCM-41. The effect of IL content in MCM-41 was probed in terms of thermal stability, chemical interactions, and dielectric properties. N2-sorption results indicate the compression of the IL in the nanopores of MCM-41, which contributes to an increase of the melting point probed by differential scanning calorimetry. The quantum chemical calculations confirmed that the ion-ion interaction in ion-pairs of IL were preferred over the hydrogen bonding interaction in the presence of SiO2 molecules, and these interactions probably compress the molecular size in the nanopores of MCM-41. Strong interactions between IL and porous MCM-41 were suggested as the mechanism of this immobilization, which was characterized by FTIR and dielectric spectroscopy.

Silver effect on the structure of SiO2-CaO-P2O5 ternary system

International Nuclear Information System (INIS)

Vulpoi, Adriana; Baia, Lucian; Simon, Simion; Simon, Viorica

2012-01-01

In this study are reported results obtained from the structural, morphological and textural investigations of 56SiO 2 ∙(40-x)CaO·4P 2 O 5 ·xAg 2 O system, where 0 ≤ x ≤ 10 mol%. The samples obtained by sol–gel method were annealed and then characterized by X-ray diffraction (XRD), differential thermal analysis (DTA), thermal gravimetric analysis (TGA), vibrational spectroscopy (Raman, FTIR), N 2 -adsorption measurements, and transmission electron microscopy (TEM). XRD patterns of the investigated samples exhibit tricalcium phosphate (TCP) nanostructured phase and show the existence of metallic silver as dispersed phase. The presence of apatite-like phase is underlined by the recorded Raman and especially FT-IR spectra. TEM pictures indicate the presence of silver nanoparticles of almost spherical shapes and various sizes inside the matrix, depending on the Ag 2 O content. Regarding the textural properties, it was observed both a decrease of the specific surface area as well as a progressive change of the mesoporous characteristics with the silver addition, the latter behavior recommending the potential use of these samples for applications, where the morphology control is required.

Optical properties of ZrO2, SiO2 and TiO2-SiO2 xerogels and coatings doped with Eu3+ and Eu2+

Directory of Open Access Journals (Sweden)

Gonçalves Rogéria R.

1999-01-01

Full Text Available Eu3+ doped bulk monoliths and thin films were obtained by sol-gel methods in the ZrO2, SiO2 and SiO2-TiO2 systems. Eu3+ 5D0 ® 7FJ emission and decay time characteristics were measured during the entire experimental preparation route from the initial sol to the final xerogels. The crystalline phases identified were tetragonal ZrO2 and mixtures of rutile and anatase TiO2 at high temperature treatments in bulk samples. Good quality thin films were obtained for all systems by dip-coating optical glasses (Schott BK270. The same spectroscopic features were observed either for the bulk monoliths or the films. By appropriate heat treatments under H2 atmosphere Eu2+ containing samples could be obtained in the SiO2-TiO2 system.

Band alignment of atomic layer deposited SiO2 and HfSiO4 with (\\bar{2}01) β-Ga2O3

Science.gov (United States)

Carey, Patrick H., IV; Ren, Fan; Hays, David C.; Gila, Brent P.; Pearton, Stephen J.; Jang, Soohwan; Kuramata, Akito

2017-07-01

The valence band offset at both SiO2/β-Ga2O3 and HfSiO4/β-Ga2O3 heterointerfaces was measured using X-ray photoelectron spectroscopy. Both dielectrics were deposited by atomic layer deposition (ALD) onto single-crystal β-Ga2O3. The bandgaps of the materials were determined by reflection electron energy loss spectroscopy as 4.6 eV for Ga2O3, 8.7 eV for Al2O3 and 7.0 eV for HfSiO4. The valence band offset was determined to be 1.23 ± 0.20 eV (straddling gap, type I alignment) for ALD SiO2 on β-Ga2O3 and 0.02 ± 0.003 eV (also type I alignment) for HfSiO4. The respective conduction band offsets were 2.87 ± 0.70 eV for ALD SiO2 and 2.38 ± 0.50 eV for HfSiO4, respectively.

Electrodeposition of gold nanoparticles on mesoporous TiO{sub 2} photoelectrode to enhance visible region photocurrent

Energy Technology Data Exchange (ETDEWEB)

Supriyono,; Krisnandi, Yuni Krisyuningsih; Gunlazuardi, Jarnuzi, E-mail: jarnuzi@ui.ac.id [Department of Chemistry, FMIPA, Universitas Indonesia, Kampus UI Depok (Indonesia)

2016-04-19

Electrodeposition of gold nanoparticles (Au NPs) on the mesoporous TiO{sub 2} photoelectrode to enchance visible region photocurrent have been investigated. Mesoporous TiO{sub 2} was prepared by a sol gel method and immobilized to the fluorine doped tin oxide (FTO) substrate by dip coating technique. Gold nanoparticles were electrodeposited on the TiO{sub 2} surface and the result FTO/TiO{sub 2}/Au was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), energy dispersive spectroscopy (EDS), UV-Vis diffuse reflectance spectroscopy (DRS), and X-ray diffraction (XRD). The generated photocurrent was evaluated with an electrochemical workstation (e-DAQ/e-recorder 401) using 60 W wolfram lamp as visible light source. The photoelectrochemical evaluation indicated that the presence of gold nanoparticles on TiO{sub 2} photoelectrode shall enhance the photocurrent up to 50%.

Preparation, structural characterization, and in vitro cell studies of three-dimensional SiO2-CaO binary glass scaffolds built ofultra-small nanofibers.

Science.gov (United States)

Luo, Honglin; Li, Wei; Ao, Haiyong; Li, Gen; Tu, Junpin; Xiong, Guangyao; Zhu, Yong; Wan, Yizao

2017-07-01

Three-dimensional (3D) nanofibrous scaffolds hold great promises in tissue engineering and regenerative medicine. In this work, for the first time, 3D SiO 2 -CaO binary glass nanofibrous scaffolds have been fabricated via a combined method of template-assisted sol-gel and calcination by using bacterial cellulose as the template. SEM with EDS, TEM, and AFM confirm that the molar ratio of Ca to Si and fiber diameter of the resultant SiO 2 -CaO nanofibers can be controlled by immersion time in the solution of tetraethyl orthosilicate and ethanol. The optimal immersion time was 6h which produced the SiO 2 -CaO binary glass containing 60at.% Si and 40at.% Ca (named 60S40C). The fiber diameter of 60S40C scaffold is as small as 29nm. In addition, the scaffold has highly porous 3D nanostructure with dominant mesopores at 10.6nm and macropores at 20μm as well as a large BET surface area (240.9m 2 g -1 ), which endow the 60S40C scaffold excellent biocompatibility and high ALP activity as revealed by cell studies using osteoblast cells. These results suggest that the 60S40C scaffold has great potential in bone tissue regeneration. Copyright © 2017 Elsevier B.V. All rights reserved.

Realization of Colored Multicrystalline Silicon Solar Cells with SiO2/SiNx:H Double Layer Antireflection Coatings

Directory of Open Access Journals (Sweden)

Minghua Li

2013-01-01

Full Text Available We presented a method to use SiO2/SiNx:H double layer antireflection coatings (DARC on acid textures to fabricate colored multicrystalline silicon (mc-Si solar cells. Firstly, we modeled the perceived colors and short-circuit current density (Jsc as a function of SiNx:H thickness for single layer SiNx:H, and as a function of SiO2 thickness for the case of SiO2/SiNx:H (DARC with fixed SiNx:H (refractive index n=2.1 at 633 nm, and thickness = 80 nm. The simulation results show that it is possible to achieve various colors by adjusting the thickness of SiO2 to avoid significant optical losses. Therefore, we carried out the experiments by using electron beam (e-beam evaporation to deposit a layer of SiO2 over the standard SiNx:H for 156×156 mm2 mc-Si solar cells which were fabricated by a conventional process. Semisphere reflectivity over 300 nm to 1100 nm and I-V measurements were performed for grey yellow, purple, deep blue, and green cells. The efficiency of colored SiO2/SiNx:H DARC cells is comparable to that of standard SiNx:H light blue cells, which shows the potential of colored cells in industrial applications.

Stability analysis of SiO2/SiC multilayer coatings

International Nuclear Information System (INIS)

Fu Zhiqiang; Jean-Charles, R.

2006-01-01

The stability behaviours of SiC coatings and SiO 2 /SiC coatings in helium with little impurities are studied by HSC Chemistry 4.1, the software for analysis of Chemical reaction and equilibrium in multi-component complex system. It is found that in helium with a low partial pressure of oxidative impurities under different total pressure, the key influence factor controlling T cp of SiC depends is the partial pressure of oxidative impurities; T cp of SiC increases with the partial pressure of oxidative impurities. In helium with a low partial pressure of different impurities, the key influence factor of T cs of SiO 2 are both the partial pressure of impurities and the amount of impurities for l mol SiO 2 ; T cs of SiO 2 increases with the partial pressure of oxidative impurities at the same amount of the impurities for 1 mol SiO 2 while it decreases with the amount of the impurities for 1 mm SiO 2 at the same partial pressure of the impurities. The influence of other impurities on T cp of SiC in He-O 2 is studied and it is found that CO 2 , H 2 O and N-2 increase T cp of SiC in He-O 2 while H 2 , CO and CH 4 decrease T cp of SiC He-O 2 . When there exist both oxidative impurities and reductive impurities, their effect on T cs of SiO 2 can be suppressed by the other. In HTR-10 operation atmosphere, SiO 2 /SiC coatings can keep stable status at higher temperature than SiC coatings, so SiO 2 /SiC coatings is more suitable to improve the oxidation resistance of graphite in HTR-10 operation atmosphere compared with SiC coatings. (authors)

Effect of Commercial SiO2 and SiO2 from rice husk ash loading on biodegradation of Poly (lactic acid) and crosslinked Poly (lactic acid)

Science.gov (United States)

Prapruddivongs, C.; Apichartsitporn, M.; Wongpreedee, T.

2017-09-01

In this work, biodegradation behavior of poly (lactic acid) (PLA) and crosslinked PLA filled with two types of SiO2, precipitated SiO2 (commercial SiO2) and SiO2 from rice husk ash, were studied. Rice husks were first treated with 2 molar hydrochloric acid (HCl) to produce high purity SiO2, before burnt in a furnace at 800°C for 6 hours. All components were melted bending by an internal mixer then hot pressed using compression molder to form tested specimens. FTIR spectra of SiO2 and PLA samples were investigated. The results showed the lack of silanol group (Si-OH) of rice husk ash after steric acid surface modification, while the addition of particles can affect the crosslinking of the PLA. For biodegradation test by evaluating total amount of carbon dioxide (CO2) evolved during 60 days incubation at a controlled temperature of 58±2°C, the results showed that the biodegradation of crosslinked PLA occurred slower than the neat PLA. However, SiO2 incorporation enhanced the degree of biodegradation In particular, introducing commercial SiO2 in PLA and crosslinked PLA tended to clearly increase the degree of biodegradation as a consequence of the more accelerated hydrolysis degradation.

SiO2@TiO2 Coating: Synthesis, Physical Characterization and Photocatalytic Evaluation

Directory of Open Access Journals (Sweden)

A. Rosales

2018-03-01

Full Text Available Use of silicon dioxide (SiO2 and titanium dioxide (TiO2 have been widely investigated individually in coatings technology, but their combined properties promote compatibility for different innovative applications. For example, the photocatalytic properties of TiO2 coatings, when exposed to UV light, have interesting environmental applications, such as air purification, self-cleaning and antibacterial properties. However, as reported in different pilot projects, serious durability problems, associated with the adhesion between the substrate and TiO2, have been evidenced. Thus, the aim of this work is to synthesize SiO2 together with TiO2 to increase the durability of the photocatalytic coating without affecting its photocatalytic potential. Therefore, synthesis using sonochemistry, synthesis without sonochemistry, physical characterization, photocatalytic evaluation, and durability of the SiO2, SiO2@TiO2 and TiO2 coatings are presented. Results indicate that using SiO2 improved the durability of the TiO2 coating without affecting its photocatalytic properties. Thus, this novel SiO2@TiO2 coating shows potential for developing long-lasting, self-cleaning and air-purifying construction materials.

Dependence of Photocatalytic Activity of TiO2-SiO2 Nanopowders

Directory of Open Access Journals (Sweden)

M. Riazian

2014-10-01

Full Text Available Structural properties and chemical composition change the photocatalytic activity in TiO2-SiO2 nanopowder composite. The SiO2-TiO2 nanostructure is synthesized based on sol–gel method. The nanoparticles are characterized by x-ray fluorescents (XRF, x- ray diffraction (XRD, tunneling electron microscopy (TEM, field emission scanning electron microscopy (FE-SEM, UV-vis. Spectrophotometer and furrier transmission create infrared absorption (FTIR techniques. The rate constant k for the degradation of methylen blue in its aqueous solution under UV irradiation is determined as a measure of photocatalytic activity. Dependence between photocatalytic activity and SiO2 content in the composite is determined. Rate constant k is found dependent on the content of SiO2 in the composite that calcined at 900 oC. The addition of low composition SiO2 to the TiO2 matrix (lower than 45% enhances the photocatalytic activity due to thermal stability and increasing in the surface area. The effects of chemical compositions on the surface topography and the crystallization of phases are studied.

Optical Fibre NO2 Sensor Based on Lutetium Bisphthalocyanine in a Mesoporous Silica Matrix

Directory of Open Access Journals (Sweden)

Marc Debliquy

2018-03-01

Full Text Available In this article, we describe a NO2 sensor consisting of a coating based on lutetium bisphthalocyanine (LuPc2 in mesoporous silica. The sensor exploits the absorption spectrum change of this material which strongly and reversibly decreases in contact with NO2. NO2 is measured by following the amplitude change in the reflected spectrum of the coating deposited on the tip of a silica fibre. As diffusion of NO2 in LuPc2 is slow, the response time could be slow. To reduce it, the active molecules are dispersed in a mesoporous silica matrix deposited by a sol-gel process (Evaporation Induced Self Assembly avoiding the formation of large crystals. Doing so, the response is fairly fast. As the recovery is slow at room temperature, the recovery time is reduced by exposure to UV light at 365 nm. This UV light is directly introduced in the fibre yielding a practical sensor sensitive to NO2 in the ppm range suitable for pollution monitoring.

Magnetic SiO2/Fe3O4 colloidal crystals

International Nuclear Information System (INIS)

Huang, C-K; Hou, C-H; Chen, C-C; Tsai, Y-L; Chang, L-M; Wei, H-S; Hsieh, K-H; Chan, C-H

2008-01-01

We proposed a novel technique to fabricate colloidal crystals by using monodisperse SiO 2 coated magnetic Fe 3 O 4 (SiO 2 /Fe 3 O 4 ) microspheres. The magnetic SiO 2 /Fe 3 O 4 microspheres with a diameter of 700 nm were synthesized in the basic condition with ferric sulfate, ferrous sulfate, tartaric acid and tetraethyl orthosilicate (TEOS) in the reaction system. Monodisperse SiO 2 /Fe 3 O 4 superparamagnetic microspheres have been successfully used to fabricate colloidal crystals under the existing magnetic field

Precipitation of amorphous SiO2 particles and their properties

Directory of Open Access Journals (Sweden)

S. Musić

2011-03-01

Full Text Available The experimental conditions were optimized for the synthesis of amorphous SiO2 particles by the reaction of neutralization of sodium silicate solution with H2SO4 solution. Amorphous SiO2 particles were characterized by XRD, FT-IR, FE-SEM, EDS and microelectrophoresis. The amorphous peak was located at 2θ = 21.8º in the XRD pattern. Primary SiO2 particles were ~ 15 to ~ 30 nm in size and they aggregated into bigger particles. Amorphous SiO2 particles showed a specific surface area up to 130 m²g-1, dependent on the parameters of the precipitation process. The EDS spectrum of amorphous SiO2 particles did not show contamination with sulfate or other ions, which cannot be excluded in traces. pHzpc =1.7 was obtained by microelectrophoresis.

Surface spins disorder in uncoated and SiO2 coated maghemite nanoparticles

International Nuclear Information System (INIS)

Zeb, F.; Nadeem, K.; Shah, S. Kamran Ali; Kamran, M.; Gul, I. Hussain; Ali, L.

2017-01-01

We studied the surface spins disorder in uncoated and silica (SiO 2 ) coated maghemite (γ-Fe 2 O 3 ) nanoparticles using temperature and time dependent magnetization. The average crystallite size for SiO 2 coated and uncoated nanoparticles was about 12 and 29 nm, respectively. Scanning electron microscopy (SEM) showed that the nanoparticles are spherical in shape and well separated. Temperature scans of zero field cooled (ZFC)/field cooled (FC) magnetization measurements showed lower average blocking temperature (T B ) for SiO 2 coated maghemite nanoparticles as compared to uncoated nanoparticles. The saturation magnetization (M s ) of SiO 2 coated maghemite nanoparticles was also lower than the uncoated nanoparticles and is attributed to smaller average crystallite size of SiO 2 coated nanoparticles. For saturation magnetization vs. temperature data, Bloch's law (M(T)= M(0).(1− BT b )) was fitted well for both uncoated and SiO 2 coated nanoparticles and yields: B =3×10 −7 K -b , b=2.22 and B=0.0127 K -b , b=0.57 for uncoated and SiO 2 coated nanoparticles, respectively. Higher value of B for SiO 2 coated nanoparticles depicts decrease in exchange coupling due to enhanced surface spins disorder (broken surface bonds) as compared to uncoated nanoparticles. The Bloch's exponent b was decreased for SiO 2 coated nanoparticles which is due to their smaller average crystallite size or finite size effects. Furthermore, a sharp increase of coercivity at low temperatures (<25 K) was observed for SiO 2 coated nanoparticles which is also due to contribution of increased surface anisotropy or frozen surface spins in these smaller nanoparticles. The FC magnetic relaxation data was fitted to stretched exponential law which revealed slower magnetic relaxation for SiO 2 coated nanoparticles. All these measurements revealed smaller average crystallite size and enhanced surface spins disorder in SiO 2 coated nanoparticles than in uncoated γ-Fe 2 O 3 nanoparticles

PECVD SiO2 dielectric for niobium Josephson IC process

International Nuclear Information System (INIS)

Lee, S.Y.; Nandakumar, V.; Murdock, B.; Hebert, D.

1991-01-01

PECVD SiO 2 dielectric has been evaluated as an insulator for a Nb-based, all-refractory Josephson integrated circuit process. First, the properties of PECVD SiO 2 films were measured and compared with those of evaporated SiO films. Second, the PECVD SiO 2 dielectric film was used in our Nb-based Josephson integrated circuit process. The main problem was found to be the deterioration of the critical temperature of the superconducting niobium adjacent to the SiO 2 . The cause and a solution of the problem were investigated. Finally, a Josephson integrated sampler circuit was fabricated and tested. This paper shows acceptable junction I-V characteristics and a measured time resolution of a 4.9 ps pulse in liquid helium

PAC study in the HfO2-SiO2 system

International Nuclear Information System (INIS)

Chain, C.Y.; Damonte, L.C.; Ferrari, S.; Munoz, E.; Torres, C. Rodriguez; Pasquevich, A.F.

2010-01-01

A high-k HfO 2 /SiO 2 gate stack is taking the place of SiO 2 as a gate dielectric in field effect transistors. This fact makes the study of the solid-state reaction between these oxides very important. Nanostructure characterization of a high-energy ball milled and post-annealed equimolar HfO 2 and amorphous SiO 2 powder mixture has been carried out by perturbed angular correlations (PAC) technique. The study was complemented with X-ray diffraction and positron annihilation lifetime spectroscopy (PALS). The experimental results revealed that the ball milling of equimolar mixtures increases the defects concentration in hafnium oxide. No solid-state reaction occurred even after 8 h of milling. The formation of HfSiO 4 (hafnon) was observed in the milled blends annealed at high temperatures.The PAC results of the milled samples are compared with those obtained for pure m-ZrO 2 subjected to high-energy ball milling and with reported microstructure data for the system ZrO 2 -SiO 2 .

Preparation and characterization of Fe3O4/SiO2/Bi2MoO6 composite as magnetically separable photocatalyst

International Nuclear Information System (INIS)

Hou, Xuemei; Tian, Yanlong; Zhang, Xiang; Dou, Shuliang; Pan, Lei; Wang, Wenjia; Li, Yao; Zhao, Jiupeng

2015-01-01

Highlights: • Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite was prepared by a hydrothermal method. • The composite has an enhanced visible absorption compared with pure Bi 2 MoO 6 . • The magnetic photocatalyst displayed excellent stability and reusability. • O 2 ·− and · OH play a major role during the photocatalytic process. - Abstract: In this paper, Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres were prepared by a facile hydrothermal method. The scanning electron microscope (SEM) results revealed that flower-like three dimensional (3D) Bi 2 MoO 6 microspheres were decorated with Fe 3 O 4 /SiO 2 magnetic nanoparticles. The UV–vis diffuse reflection spectra showed extended absorption within the visible light range compared with pure Bi 2 MoO 6 . We evaluated the photocatalytic activities of Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 microspheres on the degradation of Rhodamine B (RhB) under visible light irradiation and found that the obtained composite exhibited higher photocatalytic activity than pure Bi 2 MoO 6 and P25. Moreover, the Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 composite also displayed excellent stability and their photocatalytic activity decreased slightly after reusing 5 cycles. Meanwhile, the composite could be easily separated by applying an external magnetic field. The trapping experiment results suggest that superoxide radical species O 2 ·− and hydroxyl radicals · OH play a major role in Fe 3 O 4 /SiO 2 /Bi 2 MoO 6 system under visible light irradiation. The combination of flower-like three dimensional (3D) Bi 2 MoO 6 microspheres and Fe 3 O 4 /SiO 2 magnetic nanospheres provides a useful strategy for designing multifunctional nanostructure materials with enhanced photocatalytic activities in the potential applications of water purification

Coupling between Ge-nanocrystals and defects in SiO2

International Nuclear Information System (INIS)

Skov Jensen, J.; Franzo, G.; Leervad Petersen, T.P.; Pereira, R.; Chevallier, J.; Christian Petersen, M.; Bech Nielsen, B.; Nylandsted Larsen, A.

2006-01-01

Room temperature photoluminescence (PL) at around 600 nm from magnetron-sputtered SiO 2 films co-doped with Ge is reported. The PL signal is observed in pure SiO 2 , however, its intensity increases significantly in the presence of Ge-nanocrystals (Ge-nc). The PL intensity has been optimized by varying the temperature of heat treatment, type of gas during heat treatment, concentration of Ge in the SiO 2 films, and gas pressure during deposition. Maximum intensity occurs when Ge-nc of around 3.5 nm are present in large concentration in SiO 2 layers deposited at fairly high gas pressure. Based on time resolved PL, and PL measurements after α-particle irradiation or H passivation, we attribute the origin of the PL to a defect in SiO 2 (probably an O deficiency) that is excited through an energy transfer from Ge-nc. There is no direct PL from the Ge-nc; however, there is a strong coupling between excitons created in the Ge-nc and the SiO 2 defect

Gradient SiNO anti-reflective layers in solar selective coatings

Science.gov (United States)

Ren, Zhifeng; Cao, Feng; Sun, Tianyi; Chen, Gang

2017-08-01

A solar selective coating includes a substrate, a cermet layer having nanoparticles therein deposited on the substrate, and an anti-reflection layer deposited on the cermet layer. The cermet layer and the anti-reflection layer may each be formed of intermediate layers. A method for constructing a solar-selective coating is disclosed and includes preparing a substrate, depositing a cermet layer on the substrate, and depositing an anti-reflection layer on the cermet layer.

A novel fabrication of a high performance SiO(2)-graphene oxide (GO) nanohybrids: Characterization of thermal properties of epoxy nanocomposites filled with SiO(2)-GO nanohybrids.

Science.gov (United States)

Haeri, S Z; Ramezanzadeh, B; Asghari, M

2017-05-01

In this study it has been aimed to enhance the thermal resistance of epoxy coating through incorporation of SiO 2 -GO nanohybrids. SiO 2 -GO nanohybrids were synthesized through one-step sol-gel route using a mixture of Tetraethylorthosilane (TEOS) and 3-Aminopropyl triethoxysilane (APTES) silanes. The SiO 2 -GO nanohybrids were prepared at various hydrolysis times of 24, 48 and 72h. Then 0.2wt.% of GO and SiO 2 -GO nanohybrids were separately incorporated into the epoxy coating. Results revealed that amino functionalized SiO 2 nanoparticles with particle size around 20-30nm successfully synthesized on the basal plane of GO. Results showed significant improvement of dispersion and interfacial interactions between nanohybrids and epoxy composite arising from covalent bonding between the SiO 2 -GO and the epoxy matrix. It was found that the thermal resistance of SiO 2 -GO nanohybrids and SiO 2 -GO/Epoxy nanocomposite was noticeably higher than GO and epoxy matrix, respectively. Copyright © 2017 Elsevier Inc. All rights reserved.

Preparation of Mesoporous SnO2 by Electrostatic Self-Assembly

Directory of Open Access Journals (Sweden)

Yang Jing

2014-01-01

Full Text Available We report a simple and scalable strategy to synthesize mesoporous SnO2 with tin dioxide nanoparticles of 5-6 nm crystalline walls and 3-4 nm pore diameter with the assistance of Mo7O246- as templating agent at room temperature. The samples were characterized by XRD, TEM, UV-DRS, XPS, and BET. The product has a moderately high surface area of 132 m2 g−1 and a narrow mesoporous structure with an average pore diameter of 3.5 nm. The photocatalytic activities of the mesoporous SnO2 were evaluated by the degradation of methyl orange (MO in aqueous solution under UV light irradiation.

Regulating effect of SiO2 interlayer on optical properties of ZnO thin films

International Nuclear Information System (INIS)

Xu, Linhua; Zheng, Gaige; Miao, Juhong; Su, Jing; Zhang, Chengyi; Shen, Hua; Zhao, Lilong

2013-01-01

ZnO/SiO 2 nanocomposite films with periodic structure were prepared by electron beam evaporation technique. Regulating effect of SiO 2 interlayer with various thicknesses on the optical properties of ZnO/SiO 2 thin films was investigated deeply. The analyses of X-ray diffraction show that the ZnO layers in ZnO/SiO 2 nanocomposite films have a wurtzite structure and are preferentially oriented along the c-axis while the SiO 2 layers are amorphous. The scanning electron microscope images display that the ZnO layers are composed of columnar grains and the thicknesses of ZnO and SiO 2 layers are all very uniform. The SiO 2 interlayer presents a significant modulation effect on the optical properties of ZnO thin films, which is reflected in the following two aspects: (1) the transmittance of ZnO/SiO 2 nanocomposite films is increased; (2) the photoluminescence (PL) of ZnO/SiO 2 nanocomposite films is largely enhanced compared with that of pure ZnO thin films. The ZnO/SiO 2 nanocomposite films have potential applications in light-emitting devices and flat panel displays. -- Highlights: ► ZnO/SiO 2 nanocomposite films with periodic structure were prepared by electron beam evaporation technique. ► The SiO 2 interlayer presents a significant modulation effect on the optical properties of ZnO thin films. ► The photoluminescence of ZnO/SiO 2 nanocomposite films is largely enhanced compared with that of pure ZnO thin films. ► The ZnO/SiO 2 nanocomposite films have potential applications in light-emitting devices and flat panel displays

Anti-inflammation performance of curcumin-loaded mesoporous calcium silicate cement.

Science.gov (United States)

Chen, Yuan-Chien; Shie, Ming-You; Wu, Yuan-Haw Andrew; Lee, Kai-Xing Alvin; Wei, Li-Ju; Shen, Yu-Fang

2017-09-01

Calcium silicate (CS) cements have excellent bioactivity and can induce the bone-like apatite formation. They are good biomaterials for bone tissue engineering and bone regenerative medicine. However, they have degradability and the dissolved CS can cause the inflammatory response at the early post-implantation stage. The purpose of this study was to design and prepare the curcumin-loaded mesoporous CS (MesoCS/curcumin) cements as a strategy to reduce the inflammatory reaction after implantation. The MesoCS/curcumin cements were designed and prepared. The characteristics of MesoCS/curcumin specimens were examined by transmission electron microscopy (TEM), X-ray diffraction (XRD) and scanning electron microscopy (SEM). Their physical properties, biocompatibility, and anti-inflammatory ability were also evaluated. The MesoCS/curcumin cements displayed excellent biocompatibility and physical properties. Their crystalline characterizations were very similar with MesoCS cements. After soaking in simulated body fluid, the bone-like apatite layer of the MesoCS/curcumin cements could be formed. In addition, it could inhibit the expression of tumor necrosis factor-α (TNF-α) and interleukin-1 (IL-1) after inflammation reaction induced by lipopolysaccharides and had good anti-inflammatory ability. Adding curcumin in MesoCS cements can reduce the inflammatory reaction, but does not affect the original biological activity and properties of MesoCS cements. It can provide a good strategy to inhibit the inflammatory reaction after implantation for bone tissue engineering and bone regenerative medicine. Copyright © 2017. Published by Elsevier B.V.

Biomedical bandpass filter for fluorescence microscopy imaging based on TiO2/SiO2 and TiO2/MgF2 dielectric multilayers

International Nuclear Information System (INIS)

Butt, M A; Fomchenkov, S A; Verma, P; Khonina, S N; Ullah, A

2016-01-01

We report a design for creating a multilayer dielectric optical filters based on TiO 2 and SiO 2 /MgF 2 alternating layers. We have selected Titanium dioxide (TiO 2 ) for high refractive index (2.5), Silicon dioxide (SiO 2 ) and Magnesium fluoride (MgF 2 ) as a low refractive index layer (1.45 and 1.37) respectively. Miniaturized visible spectrometers are useful for quick and mobile characterization of biological samples. Such devices can be fabricated by using Fabry-Perot (FP) filters consisting of two highly reflecting mirrors with a central cavity in between. Distributed Bragg Reflectors (DBRs) consisting of alternating high and low refractive index material pairs are the most commonly used mirrors in FP filters, due to their high reflectivity. However, DBRs have high reflectivity for a selected range of wavelengths known as the stopband of the DBR. This range is usually much smaller than the sensitivity range of the spectrometer range. Therefore a bandpass filters are required to restrict wavelength outside the stopband of the FP DBRs. The proposed filter shows a high quality with average transmission of 97.4% within the passbands and the transmission outside the passband is around 4%. Special attention has been given to keep the thickness of the filters within the economic limits. It can be suggested that these filters are exceptional choice for florescence imaging and Endoscope narrow band imaging. (paper)

Adsorption of vitamin E on mesoporous titania nanocrystals

International Nuclear Information System (INIS)

Shih, C.J.; Lin, C.T.; Wu, S.M.

2010-01-01

Tri-block nonionic surfactant and titanium chloride were used as starting materials for the synthesis of mesoporous titania nanocrystallite powders. The main objective of the present study was to examine the synthesis of mesoporous titania nanocrystals and the adsorption of vitamin E on those nanocrystals using X-ray diffraction (XRD), transmission electron microscopy, and nitrogen adsorption and desorption isotherms. When the calcination temperature was increased to 300 o C, the reflection peaks in the XRD pattern indicated the presence of an anatase phase. The crystallinity of the nanocrystallites increased from 80% to 98.6% with increasing calcination temperature from 465 o C to 500 o C. The N 2 adsorption data and XRD data taken after vitamin E adsorption revealed that the vitamin E molecules were adsorbed in the mesopores of the titania nanocrystals.

Comparisons between TiO2- and SiO2-flux assisted TIG welding processes.

Science.gov (United States)

Tseng, Kuang-Hung; Chen, Kuan-Lung

2012-08-01

This study investigates the effects of flux compounds on the weld shape, ferrite content, and hardness profile in the tungsten inert gas (TIG) welding of 6 mm-thick austenitic 316 L stainless steel plates, using TiO2 and SiO2 powders as the activated fluxes. The metallurgical characterizations of weld metal produced with the oxide powders were evaluated using ferritoscope, optical microscopy, and Vickers microhardness test. Under the same welding parameters, the penetration capability of TIG welding with TiO2 and SiO2 fluxes was approximately 240% and 292%, respectively. A plasma column made with SiO2 flux exhibited greater constriction than that made with TiO2 flux. In addition, an anode root made with SiO2 flux exhibited more condensation than that made with TiO2 flux. Results indicate that energy density of SiO2-flux assisted TIG welding is higher than that of TiO2-flux assisted TIG welding.

SiO2 Glass Density to Lower-Mantle Pressures

DEFF Research Database (Denmark)

Petitgirard, Sylvain; Malfait, Wim J.; Journaux, Baptiste

2017-01-01

and present Earth. SiO2 is the main constituent of Earth's mantle and is the reference model system for the behavior of silicate melts at high pressure. Here, we apply our recently developed x-ray absorption technique to the density of SiO2 glass up to 110 GPa, doubling the pressure range...... for such measurements. Our density data validate recent molecular dynamics simulations and are in good agreement with previous experimental studies conducted at lower pressure. Silica glass rapidly densifies up to 40 GPa, but the density trend then flattens to become asymptotic to the density of SiO2 minerals above 60...... GPa. The density data present two discontinuities at similar to 17 and similar to 60 GPa that can be related to a silicon coordination increase from 4 to a mixed 5/6 coordination and from 5/6 to sixfold, respectively. SiO2 glass becomes denser than MgSiO3 glass at similar to 40 GPa, and its density...

Concentration effect of Tm3+ on cathodoluminescence properties of SiO2: Tm3+ and SiO2:Ho3+, Tm3+ systems

CSIR Research Space (South Africa)

Dhlamini, MS

2012-05-01

Full Text Available .physb.2011.09.091 Concentration effect of Tm3+ on cathodoluminescence properties of SiO2: Tm 3+ and SiO2:Ho 3+, Tm3+ systems M.S. Dhlamini, G.H. Mhlongo, H.C. Swart, O.M. Ntwaeaborwa, K.T. Hillie ABSTRACT: Cathodoluminescence (CL) properties of Si...O2 powders activated with thulium (Tm3+) and holmium (Ho3+) ions prepared by a sol–gel process were investigated. Different molar concentrations of Tm3+ co-doped with Ho3+ were studied. The 460 nm peak was monitored and the influence of the beam...

Epoxy-based broadband anti-reflection coating for millimeter-wave optics

OpenAIRE

Rosen, Darin; Suzuki, Aritoki; Keating, Brian; Krantz, William; Lee, Adrian T.; Quealy, Erin; Richards, Paul L.; Siritanasak, Praween; Walker, William

2013-01-01

We have developed epoxy-based, broadband anti-reflection coatings for millimeter-wave astrophysics experiments with cryogenic optics. By using multiple-layer coatings where each layer steps in dielectric constant, we achieved low reflection over a wide bandwidth. We suppressed the reflection from an alumina disk to 10% over fractional bandwidths of 92% and 104% using two-layer and three-layer coatings, respectively. The dielectric constants of epoxies were tuned between 2.06 and 7.44 by mixin...

Materiais SiO2-TiO2 para a degradação fotocatalítica de diuron

Directory of Open Access Journals (Sweden)

Arthur Alaím Bernardes

2011-01-01

Full Text Available SiO2-TiO2 materials prepared by sol-gel method were evaluated in the photocatalytic degradation of diuron. The materials were prepared with and without surfactant cetyltrimethylammonium chloride at different temperatures (25, 50 and 100 ºC. The samples were characterized by N2 adsorption-desorption measurements, scanning electron microscopy, X-ray diffraction, ultraviolet-visible diffuse reflectance spectroscopy and infrared diffuse reflectance spectroscopy. The results showed that the materials synthesized with the surfactant had higher surface areas and band-gap values similar to anatase. All materials were more active than the commercial catalyst P-25 and better performance was achieved using the surfactant in the material synthesis.

Adsorption of vitamin E on mesoporous titania nanocrystals

Energy Technology Data Exchange (ETDEWEB)

Shih, C.J., E-mail: cjshih@kmu.edu.tw [Department of Fragrance and Cosmetic Science, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China); Lin, C.T.; Wu, S.M. [School of Pharmacy, College of Pharmacy, Kaohsiung Medical University, Kaohsiung 807, Taiwan (China)

2010-07-15

Tri-block nonionic surfactant and titanium chloride were used as starting materials for the synthesis of mesoporous titania nanocrystallite powders. The main objective of the present study was to examine the synthesis of mesoporous titania nanocrystals and the adsorption of vitamin E on those nanocrystals using X-ray diffraction (XRD), transmission electron microscopy, and nitrogen adsorption and desorption isotherms. When the calcination temperature was increased to 300 {sup o}C, the reflection peaks in the XRD pattern indicated the presence of an anatase phase. The crystallinity of the nanocrystallites increased from 80% to 98.6% with increasing calcination temperature from 465 {sup o}C to 500 {sup o}C. The N{sub 2} adsorption data and XRD data taken after vitamin E adsorption revealed that the vitamin E molecules were adsorbed in the mesopores of the titania nanocrystals.

Ordered mesoporous silica (OMS) as an adsorbent and membrane for separation of carbon dioxide (CO2).

Science.gov (United States)

Chew, Thiam-Leng; Ahmad, Abdul L; Bhatia, Subhash

2010-01-15

Separation of carbon dioxide (CO(2)) from gaseous mixture is an important issue for the removal of CO(2) in natural gas processing and power plants. The ordered mesoporous silicas (OMS) with uniform pore structure and high density of silanol groups, have attracted the interest of researchers for separation of carbon dioxide (CO(2)) using adsorption process. These mesoporous silicas after functionalization with amino groups have been studied for the removal of CO(2). The potential of functionalized ordered mesoporous silica membrane for separation of CO(2) is also recognized. The present paper reviews the synthesis of mesoporous silicas and important issues related to the development of mesoporous silicas. Recent studies on the CO(2) separation using ordered mesoporous silicas (OMS) as adsorbent and membrane are highlighted. The future prospectives of mesoporous silica membrane for CO(2) adsorption and separation are also presented and discussed. Copyright 2009 Elsevier B.V. All rights reserved.

Metasurface-based anti-reflection coatings at optical frequencies

Science.gov (United States)

Monti, Alessio; Alù, Andrea; Toscano, Alessandro; Bilotti, Filiberto

2018-05-01

In this manuscript, we propose a metasurface approach for the reduction of electromagnetic reflection from an arbitrary air‑dielectric interface. The proposed technique exploits the exotic optical response of plasmonic nanoparticles to achieve complete cancellation of the field reflected by a dielectric substrate by means of destructive interference. Differently from other, earlier anti-reflection approaches based on nanoparticles, our design scheme is supported by a simple transmission-line formulation that allows a closed-form characterization of the anti-reflection performance of a nanoparticle array. Furthermore, since the working principle of the proposed devices relies on an average effect that does not critically depend on the array geometry, our approach enables low-cost production and easy scalability to large sizes. Our theoretical considerations are supported by full-wave simulations confirming the effectiveness of this design principle.

More accurate definition of liquation dome in Na2O-B2O3-SiO2 system

International Nuclear Information System (INIS)

Alekseeva, Z.D.; Mazurin, O.V.; Aver'yanov, V.I.; Galakhov, F.Ya.

1977-01-01

The liquation region in the system Na 2 O-B 2 O 3 -SiO 2 was investigated. The liquation temperatures were determined by the boundary of disappearance of opalescence in specimens with pre-induced opalescence. Extrapolation of the concentration dependences of the liquation temperature along sections with a constant SiO 2 content to a point indicates that with a SiO 2 content of 20-40% the liquation boundary in the system B 2 O 3 -SiO 2 hardly lies above 450 deg C

Adsorption of cationic dye on a biohybrid SiO2-alginate

International Nuclear Information System (INIS)

Barrón Zambrano, J A; Ávila Ortega, A; Muñoz Rodríguez, D; Carrera Figueiras, C; López-Pérez, A J

2013-01-01

In this work, a biohybrid material based on SiO 2 -alginate was obtained and its properties of adsorption evaluated using methylene blue as a model dye. The experimental results showed that the biohybrid SiO 2 -alginate has a higher adsorption ability compared to their base compounds (SiO 2 and alginate). Methylene blue adsorption is pH dependent, resulting in a maximum adsorption at pH = 8. The sorption kinetics rate is similar to SiO 2 . Kinetic data were fitted to a model of pseudosecond order. The experimental isotherms fit well the Langmuir model.

Physical and Electrical Properties of SiO2 Layer Synthesized by Eco-Friendly Method

Science.gov (United States)

Kim, Jong-Woong; Kim, Young-Seok; Hong, Sung-Jei; Hong, Tae-Hwan; Han, Jeong-In

2010-05-01

SiO2 thin film has a wide range of applications, including insulation layers in microelectronic devices, such as semiconductors and flat panel displays, due to its advantageous characteristics. Herein, we developed a new eco-friendly method for manufacturing SiO2 nanoparticles and, thereby, SiO2 paste to be used in the digital printing process for the fabrication of SiO2 film. By excluding harmful Cl- and NO3- elements from the SiO2 nanoparticle synthetic process, we were able to lower the heat treatment temperature for the SiO2 precursor from 600 to 300 °C and the diameter of the final SiO2 nanoparticles to about 14 nm. The synthesized SiO2 nanoparticles were dispersed in an organic solvent with additives to make a SiO2 paste for feasibility testing. The SiO2 paste was printed onto a glass substrate to test the feasibility of using it for digital printing. The insulation resistance of the printed film was high enough for it to be used as an insulation layer for passivation.

UV-VUV laser induced phenomena in SiO2 glass

International Nuclear Information System (INIS)

Kajihara, Koichi; Ikuta, Yoshiaki; Oto, Masanori; Hirano, Masahiro; Skuja, Linards; Hosono, Hideo

2004-01-01

Creation and annihilation of point defects were studied for SiO 2 glass exposed to ultraviolet (UV) and vacuum UV (VUV) lights to improve transparency and radiation toughness of SiO 2 glass to UV-VUV laser light. Topologically disordered structure of SiO 2 glass featured by the distribution of Si-O-Si angle is a critical factor degrading transmittance near the fundamental absorption edge. Doping with terminal functional groups enhances the structural relaxation and reduces the number of strained Si-O-Si bonds by breaking up the glass network without creating the color centers. Transmittance and laser toughness of SiO 2 glass for F 2 laser is greatly improved in fluorine-doped SiO 2 glass, often referred as 'modified silica glass'. Interstitial hydrogenous species are mobile and reactive at ambient temperature, and play an important role in photochemical reactions induced by exposure to UV-VUV laser light. They terminate the dangling-bond type color centers, while enhancing the formation of the oxygen vacancies. These findings are utilized to develop a deep-UV optical fiber transmitting ArF laser photons with low radiation damage

Novel hydrophobic PDVB/R-SiO2 for adsorption of volatile organic compounds from highly humid gas stream.

Science.gov (United States)

Lu, Han-feng; Cao, Jie-jing; Zhou, Ying; Zhan, De-li; Chen, Yin-fei

2013-11-15

A novel organic-inorganic hydrophobic polydivinylbenzene-silica adsorbent (PDVB/R-SiO2) was successfully prepared by introducing a specific amount of divinylbenzene and solvent (i.e., tetrahydrofuran) to SiO2pores and initiating polymerization under solvothermal conditions. New smaller structures and surface areas were formed in the SiO2 pores. The PDVB/R-SiO2-0.5 samples exhibited a bimodal pore size distribution with both SiO2 micropores/mesopores (0.5-2.0 nm) and mesopores (2.0-5.0 nm). The surface areas increased from 116 m(2)/g (SiO2) to 246 m(2)/g. The breakthrough curves of toluene adsorption indicated that the amount adsorbed on PDVB/R-SiO2-0.5 was 12 times higher than that on SiO2. The highly humid environment exhibited no effect on adsorption because the surface of PDVB was functionalized. The adsorbed toluene was easily desorbed in hot N2 stream at 100 °C. After 10 adsorption-desorption cycles, PDVB/R-SiO2-0.5 continued exhibiting excellent adsorption, indicating superior structural and regeneration abilities. Copyright © 2013 Elsevier B.V. All rights reserved.

A simple large-scale synthesis of mesoporous In_2O_3 for gas sensing applications

International Nuclear Information System (INIS)

Zhang, Su; Song, Peng; Yan, Huihui; Yang, Zhongxi; Wang, Qi

2016-01-01

Graphical abstract: Large-scale mesoporous In_2O_3 nanostructures for gas-sensing applications were successfully fabricated via a facile Lewis acid catalytic the furfural alcohol resin template route. - Highlights: • Mesoporous In_2O_3 nanostructures with high-yield have been successfully fabricated via a facile strategy. • The microstructure and formation mechanism of mesoporous In_2O_3 nanostructures were discussed based on the experimental results. • The as-prepared In_2O_3 samples exhibited high response, short response-recovery times and good selectivity to ethanol gas. - Abstract: In this paper, large-scale mesoporous In_2O_3 nanostructures were synthesized by a facile Lewis acid catalytic the furfural alcohol resin (FAR) template route for the high-yield. Their morphology and structure were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), differential thermal and thermogravimetry analysis (DSC-TG) and the Brunauer-Emmett-Teller (BET) approach. The as-obtained mesoporous In_2O_3 nanostructures possess excellent mesoporous and network structure, which increases the contact area with the gases, it is conducive for adsorption-desorption of gas on the surface of In_2O_3. The In_2O_3 particles and pores were both about 15 nm and very uniform. In gas-sensing measurements with target gases, the gas sensor based on mesoporous In_2O_3 nanostructures showed a good response, short response-recovery time, good selectivity and stability to ethanol. These properties are due to the large specific surface area of mesoporous structure. This synthetic method could use as a new design concept for functional mesoporous nanomaterials and for mass production.

Study on sodium water glass-based anti-reflective film and its application in dye-sensitized solar cells

Energy Technology Data Exchange (ETDEWEB)

Huang, Q.Z. [Key Laboratory of Renewable Energy, Guangdong Key Laboratory of New and Renewable Energy Research and Development, Guangzhou Institute of Energy Conversion, Chinese Academy of Sciences, Guangzhou 510000 (China); University of Chinese Academy of Sciences, Beijing 100049 (China); Shi, J.F., E-mail: shijf@ms.giec.ac.cn [Key Laboratory of Renewable Energy, Guangdong Key Laboratory of New and Renewable Energy Research and Development, Guangzhou Institute of Energy Conversion, Chinese Academy of Sciences, Guangzhou 510000 (China); Wang, L.L.; Li, Y.J.; Zhong, L.W. [Key Laboratory of Renewable Energy, Guangdong Key Laboratory of New and Renewable Energy Research and Development, Guangzhou Institute of Energy Conversion, Chinese Academy of Sciences, Guangzhou 510000 (China); Xu, G., E-mail: xugang@ms.giec.ac.cn [Key Laboratory of Renewable Energy, Guangdong Key Laboratory of New and Renewable Energy Research and Development, Guangzhou Institute of Energy Conversion, Chinese Academy of Sciences, Guangzhou 510000 (China)

2016-07-01

In this paper, anti-reflective (AR) films are prepared from sodium water glass with a simple dip-coating method. The effects of SiO{sub 2}/Na{sub 2}O molar ratio, concentration of water glass, and withdrawal speed on the anti-reflection performance of the AR films are systematically studied. The optimized AR film is further applied in dye-sensitized solar cells (DSCs). The optical properties and surface morphology of AR films are analyzed by ultraviolet-visible spectrophotometer, scanning electron microscope, and atomic force microscope. Transmittance of the glass coated with sodium water glass-based AR film is increased by 3.2% when the SiO{sub 2}/Na{sub 2}O molar ratio, concentration, and withdrawal speed equal to 3.8, 5 wt%, and 80 mm/min, respectively. Under this condition, the thickness of the AR film is 127 nm and the AR film has obvious porous structure. In addition, the power conversion efficiency of DSC coated by AR film is increased from 7.92% to 8.24%, compared with the DSC without AR film. - Highlights: • Anti-reflective films are prepared from sodium water glass. • Transmittance of anti-reflective film is increased by 3.2%. • Efficiency of dye-sensitized cell is improved by anti-reflective film.

Liquidus Temperature of SrO-Al2O3-SiO2 Glass-Forming Compositions

DEFF Research Database (Denmark)

Abel, Brett M.; Morgan, James M.; Mauro, John C.

2013-01-01

. In the composition range of interest for industrial glasses, Tliq tends to decrease with increasing strontium-to-alumina ratio. We find that cristobalite, mullite, and slawsonite are the dominant devitrification phases for the compositions with high SiO2, SiO2+Al2O3, and SrO contents, respectively. By comparison...... with the phase diagrams for CaO-Al2O3-SiO2 and MgO-Al2O3-SiO2 systems, we have found that for the highest [RO]/[Al2O3] ratios, Tliq exhibits a minimum value for R = Ca. Based on the phase diagram established here, the composition of glass materials, for example, for liquid crystal display substrates, belonging...... to the SrO-Al2O3-SiO2 family may be designed with a more exact control of the glass-forming ability by avoiding the regions of high liquidus temperature....

Fabrication and properties of highly luminescent materials from Tb(OH)3-SiO2 and Tb(OH)3-SiO2:Eu3+ nanotubes

International Nuclear Information System (INIS)

Tran Thu Huong; Tran Kim Anh; Le Quoc Minh

2009-01-01

Luminescent nanomaterials with one-dimensional (1D) structures have attracted much attention due to their unique properties and potential applications in nanophotonics and nanobiophotonics. In this paper, we report a synthesis of terbium - hydroxide - at - silica Tb(OH) 3 -SiO 2 and Tb(OH) 3 -SiO 2 :Eu 3+ nanotubes. Terbium - hydroxide tubes were synthesized by soft template method. The size of the tubes can be controlled precisely and have outer diameters ranging from 80 to 120 nm, wall thickness of about 30 nm, and lengths ranging from 300 to 800 nm. To fabricate core/shell materials, the seed growth method is used. FESEM, X-ray diffraction, Raman spectra of Tb(OH) 3 and Tb(OH) 3 -SiO 2 nanotubes were investigated. The photoluminescence (PL) spectrum of Tb(OH) 3 under 325 nm excitation consists of four main peaks at 488, 542, 582, and 618 nm. Furthermore, a preliminary suggestion for the mechanism of growth of the Tb(OH) 3 nanotubes using the soft - template synthesis technique has been proposed. The PL intensity from Tb(OH) 3 -SiO 2 or Tb(OH) 3 -SiO 2 :Eu 3+ nanotubes is much stronger than that of Tb(OH) 3 .

Long lasting yellow phosphorescence and photostimulated luminescence in Sr3SiO5 : Eu2+ and Sr3SiO5 : Eu2+, Dy3+ phosphors

International Nuclear Information System (INIS)

Sun Xiaoyuan; Zhang Jiahua; Zhang Xia; Luo Yongshi; Wang Xiaojun

2008-01-01

We report the observation of long lasting yellow phosphorescence and photostimulated luminescence (PSL) in Sr 3 SiO 5 : Eu 2+ and Sr 3 SiO 5 : Eu 2+ , Dy 3+ phosphors. The decay patterns of phosphorescence and thermoluminescence curves demonstrate that introduction of Dy 3+ into Sr 3 SiO 5 : Eu 2+ can generate a large number of shallow traps and deep traps. The generated deep traps prolong the phosphorescence up to 6 h after UV irradiation. The PSL is studied under 808 nm excitation. Slow rising and falling edges of the emission in Sr 3 SiO 5 : Eu 2+ , Dy 3+ are observed, showing a retrapping process by the generated shallow traps due to co-doping Dy 3+ .

In-situ functionalization of mesoporous hexagonal ZnO synthesized in task specific ionic liquid as a photocatalyst for elimination of SO2, NOx, and CO

Science.gov (United States)

Kowsari, Elaheh; Abdpour, Soheil

2017-12-01

A novel mesoporous structure of zinc oxide was synthesized in hydrothermal autocalve in the presence of a functional ionic liquid (FIL) {[CH2CH2] O2 (mm)2}. This FIL with ether groups was used simultaneously as a designer templating agent and a source of the hydroxyl radical. The presence of this ionic liquid led to producing ethylene glycol in the reaction media, which adsorb on the surface of mesoporous hexagonal ZnO plates. These mesoporous structures can adsorb pollutant gases and increase photocatalytic oxidation of pollutant gases in compare with commercial ZnO nanoparticles and agglomerated nanoparticles synthesized in this work. XPS data confirmed ethylene glycol production by the ionic liquid, which could prove a role for ionic liquids as designers. The estimated BET surface area values of ZnO hexagonal mesoporous plates and agglomerated particles were 84 m2/g and 12 m2/g respectively. Optical properties of the mesoporous structures were analyzed by photoluminescence spectroscopy and diffuse reflectance UV-visible spectroscopy. The performance of these structures as efficient photocatalysts was further demonstrated by their removal of NOx, SO2, and CO under UV irradiation. The removal of NOx, SO2, and CO under UV irradiation was 56%, 81%, and 35% respectively, after 40 min of irradiation time. Reusability of the photocatalyst was determined; the results show no significant decrease of activity of photocatalyst. after five cycles.

Effect of magnesia on the degradability and bioactivity of sol-gel derived SiO2-CaO-MgO-P2O5 system glasses.

Science.gov (United States)

Ma, J; Chen, C Z; Wang, D G; Jiao, Y; Shi, J Z

2010-11-01

Mesoporous 58SiO(2)-(38-x)CaO-xMgO-4P(2)O(5) glasses (where x=0, 5, 10 and 20 mol%) have been prepared by the sol-gel synthesis route. The effects of the substitution of MgO for CaO on glass degradation and bioactivity were studied in tris-(hydroxymethyl)-aminomethane and hydrochloric acid buffer solution (Tris-HCl) and simulated body fluid (SBF), respectively. It is observed that the synthesized glasses with various MgO contents possess the similar textural properties. The studies of in vitro degradability and bioactivity show that the rate of glass degradation gradually decreases with the increase of MgO and the formation of apatite layer on glass surface is retarded. The influences of the composition upon glass properties are explained in terms of their internal structures. Copyright (c) 2010 Elsevier B.V. All rights reserved.

The Effects of Doping Copper and Mesoporous Structure on Photocatalytic Properties of TiO2

Directory of Open Access Journals (Sweden)

Yang Wang

2014-01-01

Full Text Available This paper describes a system for the synthesis of Cu-doped mesoporous TiO2 nanoparticles by a hydrothermal method at relatively low temperatures. The technique used is to dope the as-prepared mesoporous TiO2 system with copper. In this method, the copper species with the form of Cu1+, which was attributed to the reduction effect of dehydroxylation and evidenced by X-ray photoelectron spectroscopy (XPS and X-ray diffraction (XRD, was well dispersed in the optimal concentration 1 wt.% Cu-doped mesoporous TiO2. In this as-prepared mesoporous TiO2 system, original particles with a size of approximately 20 nm are aggregated together to shapes of approximately 1100 nm, which resulted in the porous aggregate structure. More importantly, the enhancement of the photocatalytic activity was discussed as effects due to the formation of stable Cu(I and the mesoporous structure in the Cu-doped mesoporous TiO2. Among them, Cu-doped mesoporous TiO2 shows the highest degradation rate of methyl orange (MO. In addition, the effects of initial solution pH on degradation of MO had also been investigated. As a result, the optimum values of initial solution pH were found to be 3.

Near zero reflection by nanostructured anti-reflection coating design for Si substrates

Science.gov (United States)

Al-Fandi, Mohamed; Makableh, Yahia F.; Khasawneh, Mohammad; Rabady, Rabi

2018-05-01

The nanostructure design of near zero reflection coating for Si substrates by using ZnO Nanoneedles (ZnONN) is performed and optimized for the visible spectral range. The design investigates the ZnONN tip to body ratio effect on the anti-reflection coating properties. Different tip to body ratios are used on Si substrates. Around zero reflection is achieved by the Nanoneedles structure design presented in this work, leading to minimal reflection losses from the Si surface. The current design evolves a solution to optical losses and surface contamination effects associated with Si solar cells.

[In situ diffuse reflectance FTIR spectroscopy study of CO adsorption on Ni2P/mesoporous molecule sieve catalysts].

Science.gov (United States)

Liu, Qian-qian; Ji, Sheng-fu; Wu, Ping-yi; Hu, Lin-hua; Huang, Xiao-fan; Zhu, Ji-qin; Li, Cheng-yue

2009-05-01

Abstract The supported nickel phosphate precursors were prepared by incipient wetness impregnation using nickel nitrate as nickel source, diammonium hydrogen phosphate as phosphorus source, and MCM-41, MCM-48, SBA-15 and SBA-16 as supports, respectively. Then, the supported Ni2 P catalysts were prepared by temperature-programmed reduction in flowing Hz from their nickel phosphate precursors. The in situ diffuse reflectance FTIR spectroscopy (DRIFTS) analysis with the probe molecule CO was carried out to characterize the surface properties. The results indicated that there were significant differences in the spectral features of the samples. The upsilon(CO) absorbances observed for adsorbed CO on mesoporous molecule sieve was attributed to weak physical adsorption. There are four different kinds of upsilon(CO) absorbances observed for adsorbed CO on Ni2 P/MCM-41 catalyst with the following assignments: (1) the formation of Ni(CO)4 at 2055 cm(-1). (2) CO terminally bonded to cus Ni(delta+) (02P/MCM-48, Ni2P/ SBA-15 and Ni2P/SBA-16 catalysts. The absorbance observed at 2051-2055 cm(-1) for CO adsorption on Ni2P/MCM-48, Ni2P/SBA-15 and Ni2P/SBA-16 catalysts is due to the formation of Ni(CO)4 species. The other upsilon absorbances observed at 2093-2096 cm(-1) was attributed to CO terminally bonded to cus Ni(delta+) (0

Effect of surfactant concentration on characteristics of mesoporous bioactive glass prepared by evaporation induced self-assembly process

International Nuclear Information System (INIS)

Shih, Chi-Chung; Chien, Chi-Sheng; Kung, Jung-Chang; Chen, Jian-Chih; Chang, Shy-Shin; Lu, Pei-Shan; Shih, Chi-Jen

2013-01-01

Highlights: ► All the unwanted organic contents were removed completely at temperatures above 600 °C. ► Specific surface area and pore volume of Mesoporous bioactive glasses reached maximum at the critical surfactant concentration. ► SAED pattern suggests that some glassy structures in the Bioactive Glasses became crystalline due to the heat treatment. ► The MBGs can induce the formation of an apatite-like layer on their surface in SBF, even after short soaking periods. - Abstract: Mesoporous bioactive glasses were prepared by the evaporation-induced self-assembly method. The main objective of the present study is to determine the effect of surfactant concentration on the synthesis of SiO 2 –CaO–P 2 O 5 mesoporous bioactive glasses; the characterization techniques used include X-ray diffraction, scanning electron microscopy and nitrogen adsorption and desorption isotherms. The results show that the specific surface area initially increased with increasing surfactant concentrations in the range of 2.1–9.1 wt% and significantly decreased from 328.7 to 204.0 m 2 /g in the concentration range of 9.1–12.5 wt%. For texture evaluation, the selected area electron diffraction patterns of the mesoporous bioactive glass precursor gels (9.1 wt% F127) calcined at different temperatures were analyzed; these patterns support the notion that some glassy structures in bioactive glasses become crystalline following heat treatment. The scanning electron microscopy images and X-ray diffraction patterns obtained agree with the inductively coupled plasma with atomic emission spectroscopy results as the mesoporous bioactive glasses can induce the formation of an apatite-like layer on their surface in SBF, even after short soaking periods.

3-D Printed Anti-Reflection Structures for the Terahertz Region

Science.gov (United States)

Bomba, Jarosław; Suszek, Jarosław; Makowski, Michał; Sobczyk, Artur; Sypek, Maciej

2018-01-01

Terahertz radiation has a growing number of applications in material characterization, where spectral fingerprinting and diffractive effects are the carriers of information. On the other hand, electromagnetic waves in the range of millimeters exhibit strong unwanted specular reflections, resulting in uncontrolled interferences. This problem is especially disturbing in the goniometric time-domain spectroscopy (TDS) configuration, where angular distribution of the field modified by the sample is altered by unwanted reflections. For this reason, low-cost anti-reflection layers are desired. Here, we present a simple way of designing and manufacturing one-sided and two-sided anti-reflection polyamide layers for the THz range. The structures were fabricated using 3-D printers based on selective laser sintering. We demonstrate experimentally in the goniometric time-domain spectroscopy the significant reduction of wavelength-dependent oscillations in Fabry-Perot configuration in the range between 0.1 and 0.3 THz. We also examine the influence of the anti-reflection layers on the distribution of THz energy in reflected, transmitted, and diffracted fields.

Broadband anti-reflective and water-repellent coatings on glass substrates for self-cleaning photovoltaic cells

International Nuclear Information System (INIS)

Li, Xiaoyu; He, Junhui; Liu, Weiyi

2013-01-01

Graphical abstract: High performance broadband antireflective and water-repellent coatings were fabricated on glass substrates, which can improve the short-circuit current of solar cells as much as 6.6% in comparison with glass substrates without the coatings. - Highlights: • Broadband anti-reflective and water-repellent coatings were fabricated. • Transmittance increased to 99.0%, significantly higher than that of commercial solar glasses. • The performance of standard solar cells with the AR coating was enhanced as much as 6.6%. - Abstract: High performance broadband antireflective (AR) and water-repellent coatings were fabricated on glass substrates by assembly of silica nanoparticles and polyelectrolytes via the layer-by-layer (LbL) assembly technique, followed by calcination and hydrophobic modification. A porous poly(diallyladimethylammonium chloride) (PDDA)/20 nm SiO 2 nanoparticles (S-20) multilayer coating with AR property was prepared first. The maximum transmittance is as high as 99.0%, while that of the glass substrate is only 91.3%. After calcination and hydrophobic modification, the coating became water-repellent while maintaining the good AR property. Such water-repellent AR coatings can improve the short-circuit current of solar cells as much as 6.6% in comparison with glass substrates without the coatings. Scanning electron microscopy (SEM) was used to observe the morphology and thickness of coatings. Transmission spectra and reflection spectra were characterized by UV–vis spectrophotometer. The surface wettability was studied by a contact angle/interface system

Effects of ordered mesoporous structure and La-doping on the microwave absorbing properties of CoFe2O4

Science.gov (United States)

Shang, Tao; Lu, Qingshan; Chao, Luomeng; Qin, Yanli; Yun, Yuehou; Yun, Guohong

2018-03-01

Low-density ordered mesoporous CoFe2O4 (Osbnd CFO) and CoLa0.12Fe1.88O4 (Osbnd CLFO) are prepared by nanocasting method using mesoporous silica SBA-15 as a hard-template. The crystal structure, surface chemical state, magnetic properties and electromagnetic parameters are characterized by X-ray diffraction, transmission electron microscopy, N2 adsorption-desorption measurement, X-ray photoelectron spectroscopy, physical property measurement system and vector network analyzer. The results show that all the samples formed a single phase with cubic spinel structure. Meanwhile Osbnd CFO and Osbnd CLFO possess a highly ordered mesostructure. Comparing with particle CoFe2O4 (P-CFO), Osbnd CFO with high specific surface area exhibits lower magnetic saturation (Ms), higher imaginary part of complex permittivity (ε‧‧) and imaginary part of the complex permeability (μ‧‧). The minimum reflection loss (RL) of Osbnd CFO reaches -27.36 dB with a matching thickness of 3.0 mm. The enhancement of the microwave absorbing performances of Osbnd CFO can be mainly attributed to the good impedance matching, high electromagnetic wave attenuation and multiple reflections of electromagnetic wave originated from the ordered mesoporous structure. The Ms of Osbnd CLFO decreases after La3+ doping, while the specific surface area, coercivity value, ε‧‧ and μ‧‧ of Osbnd CLFO increase. The minimum RL of Osbnd CLFO reaches -46.47 dB with a thickness of 3.0 mm, and the effective absorption frequency bandwidth reaches 4.9 GHz.

A simple large-scale synthesis of mesoporous In2O3 for gas sensing applications

Science.gov (United States)

Zhang, Su; Song, Peng; Yan, Huihui; Yang, Zhongxi; Wang, Qi

2016-08-01

In this paper, large-scale mesoporous In2O3 nanostructures were synthesized by a facile Lewis acid catalytic the furfural alcohol resin (FAR) template route for the high-yield. Their morphology and structure were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), differential thermal and thermogravimetry analysis (DSC-TG) and the Brunauer-Emmett-Teller (BET) approach. The as-obtained mesoporous In2O3 nanostructures possess excellent mesoporous and network structure, which increases the contact area with the gases, it is conducive for adsorption-desorption of gas on the surface of In2O3. The In2O3 particles and pores were both about 15 nm and very uniform. In gas-sensing measurements with target gases, the gas sensor based on mesoporous In2O3 nanostructures showed a good response, short response-recovery time, good selectivity and stability to ethanol. These properties are due to the large specific surface area of mesoporous structure. This synthetic method could use as a new design concept for functional mesoporous nanomaterials and for mass production.

Mesoporous PtSnO2/C Catalyst with Enhanced Catalytic Activity for Ethanol Electro-oxidation

Directory of Open Access Journals (Sweden)

Siyu Chen

2018-01-01

Full Text Available In this paper, we report the synthesis, characterization, and electrochemical evaluation of a mesoporous PtSnO2/C catalyst, called PtSnO2(M/C, with a nominal Pt : Sn ratio of 3 : 1. Brunauer–Emmett–Teller and transmission electron microscopy characterizations showed the obvious mesoporous structure of SnO2 in PtSnO2(M/C catalyst. X-ray photoelectron spectroscopy analysis exhibited the interaction between Pt and mesoporous SnO2. Compared with Pt/C and commercial PtSnO2/C catalysts, PtSnO2(M/C catalyst has a lower active site, but higher catalytic activity for ethanol electro-oxidation reaction (EOR. The enhanced activity could be attributed to Pt nanoparticles deposited on mesoporous SnO2 that could decrease the amount of poisonous intermediates produced during EOR by the interaction between Pt and mesoporous SnO2.

Facile preparation of polyethylenimine-tannins coated SiO2 hybrid materials for Cu2+ removal

Science.gov (United States)

Huang, Qiang; Liu, Meiying; Zhao, Jiao; Chen, Junyu; Zeng, Guangjian; Huang, Hongye; Tian, Jianwen; Wen, Yuanqing; Zhang, Xiaoyong; Wei, Yen

2018-01-01

Polyethylenimine-tannins coated SiO2 (SiO2@PEI-TA) hybrid materials have been prepared via a single-step multifunctional coating with polyethylenimine (PEI) and tannins (TA), and characterized by transmission electron microscope (TEM), Fourier transform infrared spectroscopy (FT-IR), thermogravimetric analysis (TGA), and X-ray photoelectron spectroscopy (XPS). The as-prepared SiO2@PEI-TA composites were examined as adsorbents to remove the Cu2+ from aqueous solution. The effects of contact time, initial Cu2+ concentration, solution pH and temperature, on Cu2+ adsorption have been investigated. The results show that the adsorption of Cu2+ onto SiO2@PEI-TA is dependent on the contact time, Cu2+ concentration, pH and temperature. The SiO2@PEI-TA composites show a 2.4-fold increase in adsorption capacity, implying that the introduction of PEI-TA coating is in favor of the Cu2+ adsorption. Based on the analysis of kinetic data, the kinetics of Cu2+ adsorption is more accurately described by the pseudo-second-order model. The equilibrium data are analyzed by Langmuir and Freundlich isotherms. Results of isotherms show that the better agreement is Freundlich isotherm model with correlation coefficient of 0.9914, which suggests that the adsorption of Cu2+ onto SiO2@PEI-TA is mainly a heterogeneous adsorption process. Thermodynamic analyses show that the adsorption interaction is actually a spontaneous and endothermic chemical process, which might involve the chemical chelation between Cu2+ and functional groups (amine and carboxyl groups) on the surface of SiO2@PEI-TA. In addition, the Cu2+ ions could desorb from SiO2@PEI-TA by using acid solution and the adsorption efficiency remains at high level after five adsorption-desorption recycles. These results provide potential applications of these novel adsorbents for the removal of heavy metal Cu2+ from aqueous solution and also provide strong evidence to support the adsorption mechanism proposed in the study.

Synthesis of mesoporous TiO2 in aqueous alcoholic medium and evaluation of its photocatalytic activity

International Nuclear Information System (INIS)

Kumaresan, L.; Prabhu, A.; Palanichamy, M.; Murugesan, V.

2011-01-01

Research highlights: → Mesoporous TiO 2 synthesized using P123 as soft template in sol-gel method. → Nanoparticle aggregates are better for photocatalytic activity than free nanoparticles. → Particle to particle transport of electrons in the conduction band of aggregates are important factor. - Abstract: Mesoporous TiO 2 was synthesized using triblock copolymer as the structure directing template in ethanol/water, isopropanol/water or 1-butanol/water medium by sol-gel method. The presence of intense peak at low angle in the XRD patterns confirmed the orderly arrangement of mesopores in the material. Among the three different alcohols, ethanol had influenced better in controlling the particle size than others. The enhanced specific surface area also revealed the formation of mesopores. Aggregates of particles were clearly seen in the TEM images and the size of the particles was approximately 10 nm. The photocatalytic activity of mesoporous TiO 2 was evaluated using aqueous alachlor as a model pollutant. The activity of mesoporous TiO 2 synthesized in ethanol/water mole ratio of 50 was higher than other mesoporous TiO 2 and commercial TiO 2 (Degussa P-25). The transport of excited electrons from one particle to its neighboring nanoparticles of mesoporous TiO 2 is suggested to be the cause for enhanced photocatalytic activity.

Preparation and Characterization of SiO2/SiCN Core-shell Ceramic Microspheres

Directory of Open Access Journals (Sweden)

ZHANG Hai-yuan

2017-05-01

Full Text Available The SiO2/PSN core-shell microspheres were prepared via an emulsion reaction combined with the polymer-derived ceramics (PDCs method using polysilazane (PSN in situ polymerization on the surface of SiO2 modified by silane coupling agents MPS, followed by pyrolysis process to obtain SiO2/SiCN core-shell ceramic microspheres. The effects of raw mass ratio, curing time and pyrolysis temperature on the formation and the morphology of core-shell microspheres were studied. The morphology, chemical composition and phase transformation were characterized by SEM, EDS, TEM, FT-IR and XRD. The results show that after reaction for 4h at 200℃, SiO2 completely coated PSN forms a core-shell microsphere with rough surface when the mass ratio of SiO2 and PSN is 1:4; when pyrolysis temperature is at 800-1200℃, amorphous SiO2/SiCN core-shell ceramic microspheres are prepared; at 1400℃, the amorphous phase partially crystallizes to produce SiO2, SiC and Si3N4 phase.

High gain durable anti-reflective coating

Energy Technology Data Exchange (ETDEWEB)

Maghsoodi, Sina; Brophy, Brenor L.; Colson, Thomas E.; Gonsalves, Peter R.; Abrams, Ze' ev R.

2017-06-27

Disclosed herein are polysilsesquioxane-based anti-reflective coating (ARC) compositions, methods of preparation, and methods of deposition on a substrate. In one embodiment, the polysilsesquioxane of this disclosure is prepared in a two-step process of acid catalyzed hydrolysis of organoalkoxysilane followed by addition of tetralkoxysilane that generates silicone polymers with >40 mol % silanol based on Si-NMR. These high silanol siloxane polymers are stable and have a long shelf-life in polar organic solvents at room temperature. Also disclosed are low refractive index ARC made from these compositions with and without additives such as porogens, templates, thermal radical initiator, photo radical initiators, crosslinkers, Si--OH condensation catalyst and nano-fillers. Also disclosed are methods and apparatus for applying coatings to flat substrates including substrate pre-treatment processes, coating processes and coating curing processes including skin-curing using hot-air knives. Also disclosed are coating compositions and formulations for highly tunable, durable, highly abrasion-resistant functionalized anti-reflective coatings.

CoFe2O4-SiO2 Composites: Preparation and Magnetodielectric Properties

Directory of Open Access Journals (Sweden)

T. Ramesh

2016-01-01

Full Text Available Cobalt ferrite (CoFe2O4 and silica (SiO2 nanopowders have been prepared by the microwave hydrothermal (M-H method using metal nitrates as precursors of CoFe2O4 and tetraethyl orthosilicate as a precursor of SiO2. The synthesized powders were characterized by XRD and FESEM. The (100-x (CoFe2O4 + xSiO2 (where x = 0%, 10%, 20%, and 30% composites with different weight percentages have been prepared using ball mill method. The composite samples were sintered at 800°C/60 min using the microwave sintering method and then their structural and morphological studies were investigated using X-ray diffraction (XRD, Fourier transformation infrared (FTIR spectra, and scanning electron microscopy (SEM, respectively. The effect of SiO2 content on the magnetic and electrical properties of CoFe2O4/SiO2 nanocomposites has been studied via the magnetic hysteresis loops, complex permeability, permittivity spectra, and DC resistivity measurements. The synthesized nanocomposites with adjustable grain sizes and controllable magnetic properties make the applicability of cobalt ferrite even more versatile.

Design of multi-layer anti-reflection coating for terrestrial solar panel ...

Indian Academy of Sciences (India)

2National Centre for Photovoltaic Research & Education, Department of Electrical Engineering,. Indian Institute of Technology, Bombay 400 076, India. MS received 14 .... improve the anti-reflective property, a low refractive index material like ...

Synthesis of TiO2-doped SiO2 composite films and its applications

Indian Academy of Sciences (India)

Wintec

structure of the titanium oxide species in the TiO2-doped SiO2 composite films and the photocatalytic reactiv- ity in order to ... gaku D-max γA diffractometer with graphite mono- chromized ... FT–IR absorption spectra of TiO2-doped SiO2 com-.

Mesoporous Carbon Produced from Tri-constituent Mesoporous Carbon-silica Composite for Water Purification

KAUST Repository

Yu, Yanjie

2012-01-01

Highly ordered mesoporous carbon-silica nanocomposites with interpenetrating carbon and silica networks were synthesized by the evaporation-induced tri-constituent co- assembly approach. The removal of silica by concentrated NaOH solution produced mesoporous carbons, which contained not only the primary large pores, but also the secondary mesopores in the carbon walls. The thus synthesized mesoporous carbon was further activated by using ZnCl2. The activated mesoporous carbon showed an improved surface area and pore volume. The synthesized mesoporous carbon was tested for diuron removal from water and the results showed that the carbon gave a fast diuron adsorption kinetics and a high diuron removal capacity, which was attributable to the primary mesopore channels being the highway for mass transfer, which led to short diffusion path length and easy accessibility of the interpenetrated secondary mesopores. The optimal adsorption capacity of the porous carbon was determined to be 390 mg/g, the highest values ever reported for diuron adsorption on carbon-based materials.

Mesoporous Carbon Produced from Tri-constituent Mesoporous Carbon-silica Composite for Water Purification

KAUST Repository

Yu, Yanjie

2012-05-01

Highly ordered mesoporous carbon-silica nanocomposites with interpenetrating carbon and silica networks were synthesized by the evaporation-induced tri-constituent co- assembly approach. The removal of silica by concentrated NaOH solution produced mesoporous carbons, which contained not only the primary large pores, but also the secondary mesopores in the carbon walls. The thus synthesized mesoporous carbon was further activated by using ZnCl2. The activated mesoporous carbon showed an improved surface area and pore volume. The synthesized mesoporous carbon was tested for diuron removal from water and the results showed that the carbon gave a fast diuron adsorption kinetics and a high diuron removal capacity, which was attributable to the primary mesopore channels being the highway for mass transfer, which led to short diffusion path length and easy accessibility of the interpenetrated secondary mesopores. The optimal adsorption capacity of the porous carbon was determined to be 390 mg/g, the highest values ever reported for diuron adsorption on carbon-based materials.

Physico-Chemical and Catalytic Properties of Mesoporous CuO-ZrO2 Catalysts

Directory of Open Access Journals (Sweden)

Sulaiman N. Basahel

2016-04-01

Full Text Available Mesoporous CuO-ZrO2 catalysts were prepared and calcined at 500 °C. The performance of the synthesized catalysts for benzylation of benzene using benzyl chloride was studied. The bare support (macroporous ZrO2 offered 45% benzyl chloride conversion after reaction time of 10 h at 75 °C. Significant increase in benzyl chloride conversion (98% was observed after CuO loading (10 wt. % on porous ZrO2 support. The conversion was decreased to 80% with increase of CuO loading to 20 wt. %. Different characterization techniques (XRD, Raman, diffuse reflectance UV-vis, N2-physisorption, H2-TPR, XPS and acidity measurements were used to evaluate physico-chemical properties of CuO-ZrO2 catalysts; the results showed that the surface and structural characteristics of the ZrO2 phase as well as the interaction between CuO-ZrO2 species depend strongly on the CuO content. The results also indicated that ZrO2 support was comprised of monoclinic and tetragonal phases with macropores. An increase of the volume of monoclinic ZrO2 phase was observed after impregnation of 10 wt. % of CuO; however, stabilization of tetragonal ZrO2 phase was noticed after loading of 20 wt. % CuO. The presence of low-angle XRD peaks indicates that mesoscopic order is preserved in the calcined CuO-ZrO2 catalysts. XRD reflections due to CuO phase were not observed in case of 10 wt. % CuO supported ZrO2 sample; in contrast, the presence of crystalline CuO phase was observed in 20 wt. % CuO supported ZrO2 sample. The mesoporous 10 wt. % CuO supported ZrO2 catalyst showed stable catalytic activity for several reaction cycles. The observed high catalytic activity of this catalyst could be attributed to the presence of a higher number of dispersed interactive CuO (Cu2+-O-Zr4+ species, easy reducibility, and greater degree of accessible surface Lewis acid sites.

Cube-like Fe3O4@SiO2@Au@Ag magnetic nanoparticles: a highly efficient SERS substrate for pesticide detection

Science.gov (United States)

Sun, Mei; Zhao, Aiwu; Wang, Dapeng; Wang, Jin; Chen, Ping; Sun, Henghui

2018-04-01

As a novel surface-enhanced Raman spectroscopic (SERS) nanocomposite, cube-like Fe3O4@SiO2@Au@Ag magnetic nanoparticles (NPs) were synthesized for the first time. Cube-like α-Fe2O3 NPs with uniform size were achieved by optimizing reaction temperature and time. Firstly, the cube-like Fe3O4@SiO2 with good dispersity was achieved by calcining α-Fe2O3@SiO2 NPs in hydrogen atmosphere at 360 °C for 2.5 h, followed by self-assembling a PEI shell via sonication. Furthermore, the Au@Ag particles were densely assembled on the Fe3O4@SiO2 NPs to form the Fe3O4@SiO2@Au@Ag composite structure via strong Ag-N interaction. The obtained nanocomposites exhibited an excellent SERS behavior, reflected by the low detection of limit (p-ATP) at the 5 × 10-14 M level. Moreover, these nanocubes were used for the detection of thiram, and the detection limit can reach 5 × 10-11 M. Meanwhile, the U.S. Environmental Protection Agency specifies that the residue in fruit must be lower than 7 ppm. Hence, the resulting substrate with high SERS activity has great practical potential applications in the rapid detection of chemical, biological, and environment pollutants with a simple portable Raman instrument at trace level.

Synthesis of Hollow Nanotubes of Zn2SiO4 or SiO2: Mechanistic Understanding and Uranium Adsorption Behavior.

Science.gov (United States)

Tripathi, Shalini; Bose, Roopa; Roy, Ahin; Nair, Sajitha; Ravishankar, N

2015-12-09

We report a facile synthesis of Zn2SiO4 nanotubes using a two-step process consisting of a wet-chemical synthesis of core-shell ZnO@SiO2 nanorods followed by thermal annealing. While annealing in air leads to the formation of hollow Zn2SiO4, annealing under reducing atmosphere leads to the formation of SiO2 nanotubes. We rationalize the formation of the silicate phase at temperatures much lower than the temperatures reported in the literature based on the porous nature of the silica shell on the ZnO nanorods. We present results from in situ transmission electron microscopy experiments to clearly show void nucleation at the interface between ZnO and the silica shell and the growth of the silicate phase by the Kirkendall effect. The porous nature of the silica shell is also responsible for the etching of the ZnO leading to the formation of silica nanotubes under reducing conditions. Both the hollow silica and silicate nanotubes exhibit good uranium sorption at different ranges of pH making them possible candidates for nuclear waste management.

Controllable Fabrication of Ordered Mesoporous Bi2WO6 and Its High Photocatalytic Activity under Visible Light

Directory of Open Access Journals (Sweden)

Xueming Dang

2014-01-01

Full Text Available Ordered mesoporous Bi2WO6 was fabricated by nanocasting technique using SBA-15 as the template. The effect of the dosage of SBA-15 on the formation of the ordered structure and the photocatalytic ability of mesoporous Bi2WO6 was discussed. It was confirmed that the ordered mesoporous structure was obtained as the dosage of SBA-15 was 0.3 g. It was found that, compared to Bi2WO6, the RhB degradation rate with ordered mesoporous Bi2WO6 was enhanced under visible light (λ>400 nm by the photocatalytic measurements. The enhanced photocatalytic performance of ordered mesoporous Bi2WO6 was attributed to its particular ordered mesoporous structure which could increase the light-harvesting efficiency, reduce the recombination of the photogenerated charge carriers, and promote the surface reaction.

SIMULTANEOUS OBSERVATIONS OF SiO AND H2O MASERS TOWARD SYMBIOTIC STARS

International Nuclear Information System (INIS)

Cho, Se-Hyung; Kim, Jaeheon

2010-01-01

We present the results of simultaneous observations of SiO v = 1, 2, J = 1-0, 29 SiO v = 0, J = 1-0, and H 2 O 6 16 -5 23 maser lines performed with the KVN Yonsei 21 m radio telescope from 2009 November to 2010 January. We searched for these masers in 47 symbiotic stars and detected maser emission from 21 stars, giving the first time detection from 19 stars. Both SiO and H 2 O masers were detected from seven stars of which six were D-type symbiotic stars and one was an S-type star, WRAY 15-1470. In the SiO maser emission, the 28 SiO v = 1 maser was detected from 10 stars, while the v = 2 maser was detected from 15 stars. In particular, the 28 SiO v = 2 maser emission without the v = 1 maser detection was detected from nine stars with a detection rate of 60%, which is much higher than that of isolated Miras/red giants. The 29 SiO v = 0 maser emission was also detected from two stars, H 2-38 and BF Cyg, together with the 28 SiO v = 2 maser. We conclude that these different observational results between isolated Miras/red giants and symbiotic stars may be related with the presence of hot companions in a symbiotic binary system.

Super-hydrophobic self-cleaning bead-like SiO2@PTFE nanofiber membranes for waterproof-breathable applications

Science.gov (United States)

Liang, Yueyao; Ju, Jingge; Deng, Nanping; Zhou, Xinghai; Yan, Jing; Kang, Weimin; Cheng, Bowen

2018-06-01

Superhydrophobic waterproof-breathable membranes, which possess a huge superiority in multi-functional applications including self-cleaning, anti-icing, anticorrosion and protective clothing, have aroused considerable attention owing to their excellent performance. Herein, the robust superhydrophobic microporous fibrous membranes were efficiently prepared via a facile and environmental-friendly electro-blown spinning (EBS) technique followed by calcination. Compared with hydrophobic pure PTFE fibrous membranes, the bead-like SiO2@PTFE nanofiber membranes (BLNFMs) exhibited superhydrophobic surface with the advancing water angle (θadv) and the water contact angle (WCA) up to 161° and 155°, respectively. The SiO2 nanoparticles were introduced as fillers which can alter the pore structure and form the multilevel rough surface. The BLNFMs could maintain superhydrophobic surface even after abrasion for 30 times or exposing to a strong corrosive solution with PH from 0 to 12 for 24 h. Besides, the BLNFMs were endowed with the modest vapor permeability (9.7 kg·m-2·d-1) and air permeability (7.2 mm·s-1) when the concentration of SiO2 nanoparticles reached to 7.3 wt%. In addition, a potential relationship among θadv, maximum pore size (dmax) and breathability (effective breathing area) was proposed in order to design the waterproof-breathable membranes with excellent properties. Furthermore, the superhydrophobic membranes with durable self-cleaning property provided the advantages of potential applications in the fields of membrane distillation, versatile protective clothing, etc.

Crystallization kinetics of BaO-Al2O3-SiO2 glasses

Science.gov (United States)

Bansal, Narottam P.; Hyatt, Mark J.

1989-01-01

Barium aluminosilicate glasses are being investigated as matrix materials in high-temperature ceramic composites for structural applications. Kinetics of crystallization of two refractory glass compositions in the barium aluminosilicate system were studied by differential thermal analysis (DTA), X-ray diffraction (XRD), and scanning electron microscopy (SEM). From variable heating rate DTA, the crystallization activation energies for glass compositions (wt percent) 10BaO-38Al2O3-51SiO2-1MoO3 (glass A) and 39BaO-25Al2O3-35SiO2-1MoO3 (glass B) were determined to be 553 and 558 kJ/mol, respectively. On thermal treatment, the crystalline phases in glasses A and B were identified as mullite (3Al2O3-2SiO2) and hexacelsian (BaO-Al2O3-2SiO2), respectively. Hexacelsian is a high-temperature polymorph which is metastable below 1590 C. It undergoes structural transformation into the orthorhombic form at approximately 300 C accompanied by a large volume change which is undesirable for structural applications. A process needs to be developed where stable monoclinic celsian, rather than hexacelsian, precipitates out as the crystal phase in glass B.

The influence of SiO2 Addition on 2MgO-Al2O3-3.3P2O5 Glass

DEFF Research Database (Denmark)

Larsen, P.H.; Poulsen, F.W.; Berg, Rolf W.

1999-01-01

2MgO-Al2O3-3.3P2O5 glasses with increasing amounts of SiO2 are considered for sealing applications in Solid Oxide Fuel Cells (SOFC). The change in chemical durability under SOFC anode conditions and the linear thermal expansion is measured as functions of the SiO2 concentration. Raman spectroscopy...... analysis of the glasses reveals no sign of important changes in the glass structure upon SiO2 addition. Some increase in glass durability with SiO2 concentration is reported and its cause is discussed....

Diffusive charge transport in graphene on SiO 2

Science.gov (United States)

Chen, J.-H.; Jang, C.; Ishigami, M.; Xiao, S.; Cullen, W. G.; Williams, E. D.; Fuhrer, M. S.

2009-07-01

We review our recent work on the physical mechanisms limiting the mobility of graphene on SiO 2. We have used intentional addition of charged scattering impurities and systematic variation of the dielectric environment to differentiate the effects of charged impurities and short-range scatterers. The results show that charged impurities indeed lead to a conductivity linear in density ( σ(n)∝n) in graphene, with a scattering magnitude that agrees quantitatively with theoretical estimates; increased dielectric screening reduces the scattering from charged impurities, but increases the scattering from short-range scatterers. We evaluate the effects of the corrugations (ripples) of graphene on SiO 2 on transport by measuring the height-height correlation function. The results show that the corrugations cannot mimic long-range (charged impurity) scattering effects, and have too small an amplitude-to-wavelength ratio to significantly affect the observed mobility via short-range scattering. Temperature-dependent measurements show that longitudinal acoustic phonons in graphene produce a resistivity that is linear in temperature and independent of carrier density; at higher temperatures, polar optical phonons of the SiO 2 substrate give rise to an activated, carrier density-dependent resistivity. Together the results paint a complete picture of charge carrier transport in graphene on SiO 2 in the diffusive regime.

Microwave synthesis and electrochemical characterization of mesoporous carbon@Bi{sub 2}O{sub 3} composites

Energy Technology Data Exchange (ETDEWEB)

Xia, Nannan [Department of Chemistry and Institute of Nanochemistry, Jinan University, Guangzhou 510632 (China); Yuan, Dingsheng, E-mail: tydsh@jnu.edu.cn [Department of Chemistry and Institute of Nanochemistry, Jinan University, Guangzhou 510632 (China); Zhou, Tianxiang; Chen, Jingxing; Mo, Shanshan; Liu, Yingliang [Department of Chemistry and Institute of Nanochemistry, Jinan University, Guangzhou 510632 (China)

2011-05-15

Graphical abstract: An efficient and quick microwave method has been employed to prepare worm-like mesoporous carbon@Bi{sub 2}O{sub 3} composites for the first time. The electrochemical measurement shows the worm-like mesoporous carbon@Bi{sub 2}O{sub 3} composites exhibits excellent capacitance performance and the maximum specific capacitance is up to 386 F g{sup -1}. Research highlights: {yields} An efficient and quick microwave method has been employed. {yields} A worm-like mesoporous carbon@Bi{sub 2}O{sub 3} composites have been successfully prepared. {yields} This composite exhibits excellent capacitance performance. {yields} This composite could be a potential electrode material for the supercapacitors. -- Abstract: An efficient and quick microwave method has been employed to prepare worm-like mesoporous carbon@Bi{sub 2}O{sub 3} composites for the first time. As-prepared products have been characterized by X-ray diffraction, N{sub 2} adsorption-desorption, scanning electron microscopy, transmission electron microscopy and inductive coupled plasma atomic emission spectroscopy. The electrochemical measurement shows the worm-like mesoporous carbon@Bi{sub 2}O{sub 3} composites exhibits excellent capacitance performance and the maximum specific capacitance reaches 386 F g{sup -1}, three times more than the pure worm-like mesoporous carbon.

Design of multi-layer anti-reflection coating for terrestrial solar panel ...

Indian Academy of Sciences (India)

To date, there is no ideal anti-reflection (AR) coating available on solar glass which can effectively transmit the incident light within the visible wavelength range. However, there is a need to develop multifunctional coatingwith superior anti-reflection properties and self-cleaning ability meant to be used for solar glass panels.

A rational repeating template method for synthesis of 2D hexagonally ordered mesoporous precious metals.

Science.gov (United States)

Takai, Azusa; Doi, Yoji; Yamauchi, Yusuke; Kuroda, Kazuyuki

2011-03-01

A repeating template method is presented for the synthesis of mesoporous metals with 2D hexagonal mesostructures. First, a silica replica (i.e., silica nanorods arranged periodically) is prepared by using 2D hexagonally ordered mesoporous carbon as the template. After that, the obtained silica replica is used as the second template for the preparation of mesoporous ruthenium. After the ruthenium species are introduced into the silica replica, the ruthenium species are then reduced by a vapor-infiltration method by using the reducing agent dimethylamine borane. After the ruthenium deposition, the silica is chemically removed. Analysis by transmission and scanning electron microscopies, a nitrogen-adsorption-desorption isotherm, and small-angle X-ray scattering revealed that the mesoporous ruthenium had a 2D hexagonal mesostructure, although the mesostructural ordering is decreased compared to that of the original mesoporous carbon template. This method is widely applicable to other metal systems. By changing the metal species introduced into the silica replica, several mesoporous metals (palladium and platinum) can be synthesized. Ordered mesoporous ruthenium and palladium, which are not easily attainable by the soft-templating methods, can be prepared. This study has overcome the composition variation limitations of the soft-templating method. Copyright © 2011 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Research on the biological activity and doxorubicin release behavior in vitro of mesoporous bioactive SiO2-CaO-P2O5 glass nanospheres

Science.gov (United States)

Wang, Xiang; Wang, Gen; Zhang, Ying

2017-10-01

Mesoporous bioactive glass (MBG) nanospheres have been synthesized by a facile method of sacrificing template using cetyl trimethyl ammonium bromide (CTAB) as surfactant. The prepared MBG nanospheres possess high specific surface area (632 m2 g-1) as well as uniform size (∼100 nm). In addition, MBG nanospheres exhibited a quick in vitro bioactive response in simulated body fluids (SBF) and excellent bioactivity of inducing hydroxyapatite (HA) forming on the surface of MBG nanospheres. Furthermore, MBG nanospheres can sustain release of doxorubicin (DOX) with a higher encapsulation efficiency (63.6%) and show distinct degradation in PBS by releasing Si and Ca ions. The encapsulation efficiency and DOX release of MBG nanospheres could be controlled by mesoporous structure and local pH environment. The greater surface area and pore volumes of prepared MBG nanospheres are conducive to bioactive response and drug release in vitro. The amino groups in DOX can be easily protonated at acidic medium to become positively charged NH+3, which allow these drug molecules to be desorbed from the surface of MBG nanospheres via electrostatic effect. Therefore, the synthesized MBG nanospheres have a pH-sensitive drug release capability. In addition, the cytotoxicity of MBG nanospheres was assessed using a cell counting kit-8 (CCK-8), and results showed that the synthesized MBG nanospheres had no significant cytotoxicity to MC3T3 cells. These all indicated that as-prepared MBG nanospheres are promising candidates for bone tissue engineering.

Selective adsorption of thiophenic compounds from fuel over TiO2/SiO2 under UV-irradiation.

Science.gov (United States)

Miao, Guang; Ye, Feiyan; Wu, Luoming; Ren, Xiaoling; Xiao, Jing; Li, Zhong; Wang, Haihui

2015-12-30

This study investigates selective adsorption of thiophenic compounds from fuel over TiO2/SiO2 under UV-irradiation. The TiO2/SiO2 adsorbents were prepared and then characterized by N2 adsorption, X-ray diffraction and X-ray photoelectron spectroscopy. Adsorption isotherms, selectivity and kinetics of TiO2/SiO2 were measured in a UV built-in batch reactor. It was concluded that (a) with the employment of UV-irradiation, high organosulfur uptake of 5.12 mg/g was achieved on the optimized 0.3TiO2/0.7SiO2 adsorbent at low sulfur concentration of 15 ppmw-S, and its adsorption selectivity over naphthalene was up to 325.5; (b) highly dispersed TiO2 served as the photocatalytic sites for DBT oxidation, while SiO2 acted as the selective adsorption sites for the corresponding oxidized DBT using TiO2 as a promoter, the two types of active sites worked cooperatively to achieve the high adsorption selectivity of TiO2/SiO2; (c) The kinetic rate-determining step for the UV photocatalysis-assisted adsorptive desulfurization (PADS) over TiO2/SiO2 was DBT oxidation; (d) consecutive adsorption-regeneration cycles suggested that the 0.3TiO2/0.7SiO2 adsorbent can be regenerated by acetonitrile washing followed with oxidative air treatment. This work demonstrated an effective PADS approach to greatly enhance adsorption capacity and selectivity of thiophenic compounds at low concentrations for deep desulfurization under ambient conditions. Copyright © 2015 Elsevier B.V. All rights reserved.

Preparation of a Si/SiO2 -Ordered-Mesoporous-Carbon Nanocomposite as an Anode for High-Performance Lithium-Ion and Sodium-Ion Batteries.

Science.gov (United States)

Zeng, Lingxing; Liu, Renpin; Han, Lei; Luo, Fenqiang; Chen, Xi; Wang, Jianbiao; Qian, Qingrong; Chen, Qinghua; Wei, Mingdeng

2018-04-03

In this work, an Si/SiO 2 -ordered-mesoporous carbon (Si/SiO 2 -OMC) nanocomposite was initially fabricated through a magnesiothermic reduction strategy by using a two-dimensional bicontinuous mesochannel of SiO 2 -OMC as a precursor, combined with an NaOH etching process, in which crystal Si/amorphous SiO 2 nanoparticles were encapsulated into the OMC matrix. Not only can such unique porous crystal Si/amorphous SiO 2 nanoparticles uniformly dispersed in the OMC matrix mitigate the volume change of active materials during the cycling process, but they can also improve electrical conductivity of Si/SiO 2 and facilitate the Li + /Na + diffusion. When applied as an anode for lithium-ion batteries (LIBs), the Si/SiO 2 -OMC composite displayed superior reversible capacity (958 mA h g -1 at 0.2 A g -1 after 100 cycles) and good cycling life (retaining a capacity of 459 mA h g -1 at 2 A g -1 after 1000 cycles). For sodium-ion batteries (SIBs), the composite maintained a high capacity of 423 mA h g -1 after 100 cycles at 0.05 A g -1 and an extremely stable reversible capacity of 190 mA h g -1 was retained even after 500 cycles at 1 A g -1 . This performance is one of the best long-term cycling properties of Si-based SIB anode materials. The Si/SiO 2 -OMC composites exhibited great potential as an alternative material for both lithium- and sodium-ion battery anodes. © 2018 Wiley-VCH Verlag GmbH & Co. KGaA, Weinheim.

Luminescence properties of Ca2 Ga2 SiO7 :RE phosphors for UV white-light-emitting diodes.

Science.gov (United States)

Jiao, Mengmeng; Lv, Wenzhen; Lü, Wei; Zhao, Qi; Shao, Baiqi; You, Hongpeng

2015-03-16

A series of Eu(2+) -, Ce(3+) -, and Tb(3+) -doped Ca2 Ga2 SiO7 phosphors is synthesized by using a high-temperature solid-state reaction. The powder X-ray diffraction and structure refinement data indicate that our prepared phosphors are single phased and the phosphor crystalizes in a tetrahedral system with the ${P\\bar 42m}$ (113) space group. The Eu(2+) - and Ce(3+) -doped phosphors both have broad excitation bands, which match well with the UV light-emitting diodes chips. Under irradiation of λ=350 nm, Ca2 Ga2 SiO7 :Eu(2+) and Ca2 Ga2 SiO7 :Ce(3+) , Li(+) have green and blue emissions, respectively. Luminescence of Ca2 Ga2 SiO7 :Tb(3+) , Li(+) phosphor varies with the different Tb(3+) contents. The thermal stability and energy-migration mechanism of Ca2 Ga2 SiO7 :Eu(2+) are also studied. The investigation results indicate that the prepared Ca2 Ga2 SiO7 :Eu(2+) and Ca2 Ga2 SiO7 :Ce(3+) , Li(+) samples show potential as green and blue phosphors, respectively, for UV-excited white-light-emitting diodes. © 2015 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Processing of SiO2 protective layer using HMDS precursor by combustion CVD.

Science.gov (United States)

Park, Kyoung-Soo; Kim, Youngman

2011-08-01

Hexamethyldisilazane (HMDS, [(CH3)3Si]2NH) was used as a precursor to form SiO2 protective coatings on IN738LC alloys by combustion chemical vapor deposition (CCVD). SEM and XPS showed that the processed coatings were composed mainly of SiO2. The amount of HMDS had the largest effect on the size of the SiO2 agglomerates and the thickness of the deposited coatings. The specimens coated with SiO2 using the 0.05 mol/l HMDS solution showed a significantly higher temperature oxidation resistance than those deposited under other conditions.

Pt Catalyst Supported within TiO2 Mesoporous Films for Oxygen Reduction Reaction

International Nuclear Information System (INIS)

Huang, Dekang; Zhang, Bingyan; Bai, Jie; Zhang, Yibo; Wittstock, Gunther; Wang, Mingkui; Shen, Yan

2014-01-01

In this study, dispersed Pt nanoparticles into mesoporous TiO 2 thin films are fabricated by a facile electrochemical deposition method as electro-catalysts for oxygen reduction reaction. The mesoporous TiO 2 thin films coated on the fluorine-doped tin oxide glass by screen printing allow a facile transport of reactants and products. The structural properties of the resulted Pt/TiO 2 electrode are evaluated by field emission scanning electron microscopy, energy dispersive X-ray spectrometry, X-ray diffraction, and X-ray photoelectron spectroscopy. Cyclic voltammetry measurements are performed to study the electrochemical properties of the Pt/TiO 2 electrode. Further study demonstrates the stability of the Pt catalyst supported within TiO 2 mesoporous films for the oxygen reduction reaction

Study on spectroscopic properties and effects of tungsten ions in 2Bi2O3-3GeO2/SiO2 glasses.

Science.gov (United States)

Yu, Pingsheng; Su, Liangbi; Cheng, Junhua; Zhang, Xia; Xu, Jun

2017-04-01

The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass samples have been prepared by the conventional melt quenching technique. XRD patterns, absorption spectra, excitation-emission spectra and Raman measurements were utilized to characterize the synthesized glasses. When substitute SiO 2 for GeO 2 , the 0.4Bi 2 O 3 -(0.4-0.1)GeO 2 -(0.2-0.5)SiO 2 glasses exhibit strong emission centered at about 475nm (under 300nm excitation), and the decay constants are within the scope of 20-40ns. W doping into 2Bi 2 O 3 -3SiO 2 glass could increase the emission intensity of 470nm, and the W-doped 2Bi 2 O 3 -3SiO 2 glass has shown another emission at about 433nm with much shorter decay time (near 10ns). The 2Bi 2 O 3 -3GeO 2 /SiO 2 glass system could be the possible candidate for scintillator in high energy physics applications. Copyright © 2017 Elsevier Ltd. All rights reserved.

Transverse mode control in proton-implanted and oxide-confined VCSELs via patterned dielectric anti-phase filters

Science.gov (United States)

Kesler, Benjamin; O'Brien, Thomas; Dallesasse, John M.

2017-02-01

A novel method for controlling the transverse lasing modes in both proton implanted and oxide-confined vertical- cavity surface-emitting lasers (VCSELs) with a multi-layer, patterned, dielectric anti-phase (DAP) filter is pre- sented. Using a simple photolithographic liftoff process, dielectric layers are deposited and patterned on individual VCSELs to modify (increase or decrease) the mirror reflectivity across the emission aperture via anti-phase reflections, creating spatially-dependent threshold material gain. The shape of the dielectric pattern can be tailored to overlap with specific transverse VCSEL modes or subsets of transverse modes to either facilitate or inhibit lasing by decreasing or increasing, respectively, the threshold modal gain. A silicon dioxide (SiO2) and titanium dioxide (TiO2) anti-phase filter is used to achieve a single-fundamental-mode, continuous-wave output power greater than 4.0 mW in an oxide-confined VCSEL at a lasing wavelength of 850 nm. A filter consisting of SiO2 and TiO2 is used to facilitate injection-current-insensitive fundamental mode and lower order mode lasing in proton implanted VCSELs at a lasing wavelength of 850 nm. Higher refractive index dielectric materials such as amorphous silicon (a-Si) can be used to increase the effectiveness of the anti-phase filter on proton implanted devices by reducing the threshold modal gain of any spatially overlapping modes. This additive, non-destructive method allows for mode selection at any lasing wavelength and for any VCSEL layer structure without the need for semiconductor etching or epitaxial regrowth. It also offers the capability of designing a filter based upon available optical coating materials.

Cd2SiO4/Graphene nanocomposite: Ultrasonic assisted synthesis, characterization and electrochemical hydrogen storage application.

Science.gov (United States)

Masjedi-Arani, Maryam; Salavati-Niasari, Masoud

2018-05-01

For the first time, a simple and rapid sonochemical technique for preparing of pure Cd 2 SiO 4 nanostructures has been developed in presence of various surfactants of SDS, CTAB and PVP. Uniform and fine Cd 2 SiO 4 nanoparticle was synthesized using of polymeric PVP surfactant and ultrasonic irradiation. The optimized cadmium silicate nanostructures added to graphene sheets and Cd 2 SiO 4 /Graphene nanocomposite synthesized through pre-graphenization. Hydrogen storage capacity performances of Cd 2 SiO 4 nanoparticle and Cd 2 SiO 4 /Graphene nanocomposite were compared. Obtained results represent that Cd 2 SiO 4 /Graphene nanocomposites have higher hydrogen storage capacity than Cd 2 SiO 4 nanoparticles. Cd 2 SiO 4 /Graphene nanocomposites and Cd 2 SiO 4 nanoparticles show hydrogen storage capacity of 3300 and 1300 mAh/g, respectively. Copyright © 2018 Elsevier B.V. All rights reserved.

Spectroscopy of photonic band gaps in mesoporous one-dimensional photonic crystals based on aluminum oxide

International Nuclear Information System (INIS)

Gorelik, V.S.; Voinov, Yu.P.; Shchavlev, V.V.; Bi, Dongxue; Shang, Guo Liang; Fei, Guang Tao

2017-01-01

Mesoporous one-dimensional photonic crystals based on aluminum oxide have been synthesized by electrochemical etching method. Reflection spectra of the obtained mesoporous samples in a wide spectral range that covers several band gaps are presented. Microscopic parameters of photonic crystals are calculated and corresponding reflection spectra for the first six band gaps are presented.

Enhanced the hydrophobic surface and the photo-activity of TiO2-SiO2 composites

Science.gov (United States)

Wahyuni, S.; Prasetya, A. T.

2017-02-01

The aim of this research is to develop nanomaterials for coating applications. This research studied the effect of various TiO2-SiO2 composites in acrylic paint to enhance the hydrophobic properties of the substrate. Titanium dioxide containing silica in the range 20-35 mol% has been synthesized using sol-gel route. The XRD’s spectra show that increasing SiO2 content in the composite, decreasing its crystalline properties but increasing the surface area. TiO2-SiO2 composite was dispersed in acrylic paint in 2% composition by weight. The largest contact angle was 70, which produced by the substrate coated with TS-35-modified acrylic paint. This study also investigated the enhanced photo-activity of TiO2-SiO2 modified with poly-aniline. The XRD spectra show that the treatment does not change the crystal structure of TiO2. The photo-activity of the composite was evaluated by degradation of Rhodamine-B with visible light. The best performance of the degradation process was handled by the composite treated with 0.1mL anilines per gram of TiO2-SiO2 composite (TSP-A). On the other side, the contact angle 70 has not shown an excellent hydrophobic activity. However, the AFM spectra showed that nanoroughness has started to form on the surface of acrylic paint modified with TiO2-SiO2 than acrylic alone.

SiO2-induced release of sVEGFRs from pulmonary macrophages.

Science.gov (United States)

Chao, Jie; Lv, Yan; Chen, Jin; Wang, Jing; Yao, Honghong

2018-01-01

The inhalation of silicon dioxide (SiO 2 ) particles causes silicosis, a stubborn pulmonary disease that is characterized by alveolar inflammation during the early stage. Soluble cytokine receptors (SCRs) play important roles in regulating inflammation by either attenuating or promoting cytokine signaling. However, the role of SCRs in silicosis remains unknown. Luminex assays revealed increased soluble vascular endothelial growth factor receptor (sVEGFR) family levels in the plasma of silicosis patients. In an enzyme-linked immunosorbent assay (ELISA), cells from the differentiated human monocytic cell line U937 released sVEGFR family proteins after exposure to SiO 2 (50μg/cm 2 ). Further Western blot experiments revealed that VEGFR expression was also elevated in U937 cells. In contrast, levels of sVEGFR family members did not change in the supernatants of human umbilical vein endothelial cells (HUVECs) after exposure to SiO 2 (50μg/cm 2 ). Interestingly, VEGFR expression in HUVECs decreased after SiO 2 treatment. In a scratch assay, HUVECs exhibited cell migration ability, indicating the acquisition of mesenchymal properties. Our findings highlight the important role of sVEGFRs in both inflammation and fibrosis induced by SiO 2 , suggesting a possible mechanism for the fibrogenic effects observed in pulmonary diseases associated with fibrosis. Copyright © 2017 Elsevier B.V. All rights reserved.

Highly efficient transparent Zn2SiO4:Mn2+ phosphor film on quartz glass

International Nuclear Information System (INIS)

Seo, K.I.; Park, J.H.; Kim, J.S.; Kim, G.C.; Yoo, J.H.

2009-01-01

Highly efficient transparent Zn 2 SiO 4 :Mn 2+ film phosphors on quartz substrates were deposited by the thermal diffusion of sputtered ZnO:Mn film. They show a textured structure with some preferred orientations. Our film phosphor shows, for the best photoluminescence (PL) brightness, a green PL brightness of about 20% of a commercial Zn 2 SiO 4 :Mn 2+ powder phosphor screen. The film shows a high transmittance of more than 10% at the red-color region. The excellence in PL brightness and transmittance can be explained in terms of the textured crystal growth with a continuous gradient of Zn 2 SiO 4 : Mn 2+ crystals.

A simple large-scale synthesis of mesoporous In{sub 2}O{sub 3} for gas sensing applications

Energy Technology Data Exchange (ETDEWEB)

Zhang, Su; Song, Peng, E-mail: mse_songp@ujn.edu.cn; Yan, Huihui; Yang, Zhongxi; Wang, Qi, E-mail: mse_wangq@ujn.edu.cn

2016-08-15

Graphical abstract: Large-scale mesoporous In{sub 2}O{sub 3} nanostructures for gas-sensing applications were successfully fabricated via a facile Lewis acid catalytic the furfural alcohol resin template route. - Highlights: • Mesoporous In{sub 2}O{sub 3} nanostructures with high-yield have been successfully fabricated via a facile strategy. • The microstructure and formation mechanism of mesoporous In{sub 2}O{sub 3} nanostructures were discussed based on the experimental results. • The as-prepared In{sub 2}O{sub 3} samples exhibited high response, short response-recovery times and good selectivity to ethanol gas. - Abstract: In this paper, large-scale mesoporous In{sub 2}O{sub 3} nanostructures were synthesized by a facile Lewis acid catalytic the furfural alcohol resin (FAR) template route for the high-yield. Their morphology and structure were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), differential thermal and thermogravimetry analysis (DSC-TG) and the Brunauer-Emmett-Teller (BET) approach. The as-obtained mesoporous In{sub 2}O{sub 3} nanostructures possess excellent mesoporous and network structure, which increases the contact area with the gases, it is conducive for adsorption-desorption of gas on the surface of In{sub 2}O{sub 3}. The In{sub 2}O{sub 3} particles and pores were both about 15 nm and very uniform. In gas-sensing measurements with target gases, the gas sensor based on mesoporous In{sub 2}O{sub 3} nanostructures showed a good response, short response-recovery time, good selectivity and stability to ethanol. These properties are due to the large specific surface area of mesoporous structure. This synthetic method could use as a new design concept for functional mesoporous nanomaterials and for mass production.

Enhanced thermal properties of novel shape-stabilized PEG composite phase change materials with radial mesoporous silica sphere for thermal energy storage

OpenAIRE

Min, Xin; Fang, Minghao; Huang, Zhaohui; Liu, Yan?gai; Huang, Yaoting; Wen, Ruilong; Qian, Tingting; Wu, Xiaowen

2015-01-01

Radial mesoporous silica (RMS) sphere was tailor-made for further applications in producing shape-stabilized composite phase change materials (ss-CPCMs) through a facile self-assembly process using CTAB as the main template and TEOS as SiO2 precursor. Novel ss-CPCMs composed of polyethylene glycol (PEG) and RMS were prepared through vacuum impregnating method. Various techniques were employed to characterize the structural and thermal properties of the ss-CPCMs. The DSC results indicated that...

Photocatalytic application of TiO2/SiO2-based magnetic nanocomposite (Fe3O4@SiO2/TiO2 for reusing of textile wastewater

Directory of Open Access Journals (Sweden)

Laleh Enayati Ahangar

2016-01-01

Full Text Available In this research we have developed a treatment method for textile wastewater by TiO2/SiO2-based magnetic nanocomposite. Textile wastewater includes a large variety of dyes and chemicals and needs treatments. This manuscript presents a facile method for removing dyes from the textile wastewater by using TiO2/SiO2-based nanocomposite (Fe3O4@SiO2/TiO2 under UV irradiation. This magnetic nanocomposite, as photocatalytically active composite, is synthesized via solution method in mild conditions. A large range of cationic, anionic and neutral dyes including: methyl orange, methylene blue, neutral red, bromocresol green and methyl red are used for treatment investigations. Neutral red and bromocresol green have good results in reusing treatment. The high surface area of nanocomposites improve the kinetic of wastewater treatment. In this method, by using the magnetic properties of Fe3O4 nanoparticles, TiO2-based photocatalyst could be separated and reused for 3 times. The efficiency of this method is respectively 100% and 65% for low concentration (10 ppm and high concentration (50 ppm of neutral red and bromocrosol green after 3 h treatment. The efficiency of treatment using the second used nanocomposite was 90% for 10 ppm of the same dyes.

Efficient photocatalytic activity with carbon-doped SiO2 nanoparticles

KAUST Repository

Zhang, Dongen

2013-01-01

Photocatalysis provides a \\'green\\' approach to completely eliminate various kinds of contaminants that are fatal for current environmental and energy issues. Semiconductors are one of the most frequently used photocatalysts as they can absorb light over a wide spectral range. However, it is also well known that naked SiO2 is not an efficient photocatalyst due to its relatively large band gap, which could only absorb shortwave ultraviolet light. In this report, nanoscale particles of carbon-doped silicon dioxide (C-doped SiO2) for use in photocatalysis were successfully prepared by a facile one-pot thermal process using tetraethylorthosilicate (TEOS) as the source of both silicon and carbon. These particles were subsequently characterized by thermogravimetric analysis, X-ray diffraction, standard and high resolution transmission electron microscopy and X-ray photoelectron spectroscopy. The C-doped SiO2 displayed outstanding photocatalytic properties, as evidenced by its catalysis of Rhodamine B degradation under near-UV irradiation. We propose that carbon doping of the SiO2 lattice creates new energy states between the bottom of the conduction band and the top of the valence band, which narrows the band gap of the material. As a result, the C-doped SiO2 nanoparticles exhibit excellent photocatalytic activities in a neutral environment. The novel synthesis reported herein for this material is both energy efficient and environmentally friendly and as such shows promise as a technique for low-cost, readily scalable industrial production. © 2013 The Royal Society of Chemistry.

Luminescence and origin of lead-related centers in single crystalline films of Y2SiO5 and Lu2SiO5

International Nuclear Information System (INIS)

Babin, V.; Gorbenko, V.; Krasnikov, A.; Mihokova, E.; Nikl, M.; Zazubovich, S.; Zorenko, Yu.

2013-01-01

In the temperature range 4.2–350 K, the steady-state and time-resolved emission and excitation spectra and luminescence decay kinetics are studied for the undoped Y 2 SiO 5 and Lu 2 SiO 5 single crystalline films grown by liquid phase epitaxy method from the PbO-based flux and, owing to that, containing lead ions substituting for Y 3+ or Lu 3+ ions. Luminescence characteristics of Pb-related centers of different types are identified. On the basis of the results obtained, we suggest that the ultraviolet emission of Pb-related centers arises from the Pb 2+ ions substituting for Y 3+ or Lu 3+ ions in the Y1 and Lu1 lattice sites of the X 2 structure. Possible hypotheses on the origin of the intense complex lead-related blue emission are discussed. We propose phenomenological models describing the excited-state dynamics of the studied luminescence centers. We also determine characteristic parameters of the corresponding relaxed excited states, in particular, the energy separations between the excited states and the rates of the radiative and non-radiative transitions from these states. -- Highlights: •Emission of lead centers in Y 2 SiO 5 and Lu 2 SiO 5 single crystalline films is studied. •The ultraviolet emission arises from Pb 2+ ions located in Y1 or Lu1 lattice sites. •Possible hypotheses on the origin of the blue emission are proposed and discussed. •The relaxed excited states parameters of various Pb-related centers are determined

Semiconductor nanocrystals formed in SiO2 by ion implantation

International Nuclear Information System (INIS)

Zhu, J.G.; White, C.W.; Budai, J.D.; Withrow, S.P.; Chen, Y.

1994-11-01

Nanocrystals of group IV (Si, Ge and SiGe), III-V (GaAs), and II-VI (CdSe) semiconductor materials have been fabricated inside SiO 2 by ion implantation and subsequent thermal annealing. The microstructure of these nanocrystalline semiconductor materials has been studied by transmission electron microscopy (TEM). The nanocrystals form in near-spherical shape with random crystal orientations in amorphous SiO 2 . Extensive studies on the nanocrystal size distributions have been carried out for the Ge nanocrystals by changing the implantation doses and the annealing temperatures. Remarkable roughening of the nanocrystals occurs when the annealing temperature is raised over the melting temperature of the implanted semiconductor material. Strong red photoluminescence peaked around 1.67 eV has been achieved in samples with Si nanocrystals in SiO 2

Effect of SiO2 addition and gamma irradiation on the lithium borate glasses

Science.gov (United States)

Raut, A. P.; Deshpande, V. K.

2018-01-01

The physical properties like density, glass transition temperature (Tg), and ionic conductivity of lithium borate (LB) glasses with SiO2 addition were measured before and after gamma irradiation. Remarkable changes in properties have been obtained in the physical properties of LB glasses with SiO2 addition and after gamma irradiation. The increase in density and glass transition temperature of LB glasses with SiO2 addition has been explained with the help of increase in density of cross linking due to SiO4 tetrahedra formation. The increase in ionic conductivity with SiO2 addition was explained with the help of ‘mixed glass former effect’. The increase in density and Tg of LB glasses with SiO2 addition after gamma irradiation has been attributed to fragmentation of bigger ring structure into smaller rings, which increases the density of cross linking and hence compaction. The exposure of gamma irradiation has lead to decrease in ionic conductivity of LB glasses with SiO2 addition. The atomic displacement caused by gamma irradiation resulted in filling of interstices and decrease in trapping sites. This explains the obtained decrease in ionic conductivity after gamma irradiation of glasses. The obtained results of effect of SiO2 addition and gamma irradiation on the density, Tg and ionic conductivity has been supported by FTIR results.

Soft-Template Synthesis of Mesoporous Anatase TiO2 Nanospheres and Its Enhanced Photoactivity

Directory of Open Access Journals (Sweden)

Xiaojia Li

2017-11-01

Full Text Available Highly crystalline mesoporous anatase TiO2 nanospheres with high surface area (higher than P25 and anatase TiO2 are prepared by a soft-template method. Despite the high specific surface area, these samples have three times lower equilibrium adsorption (<2% than Degussa P25. The rate constant of the mesoporous anatase TiO2 (0.024 min−1 reported here is 364% higher than that of P25 (0.0066 min−1, for the same catalytic loading. The results of oxidation-extraction photometry using several reactive oxygen species (ROS scavengers indicated that mesoporous anatase TiO2 generates more ROS than P25 under UV-light irradiation. This significant improvement in the photocatalytic performance of mesoporous spherical TiO2 arises from the following synergistic effects in the reported sample: (i high surface area; (ii improved crystallinity; (iii narrow pore wall thicknesses (ensuring the rapid migration of photogenerated carriers to the surface of the material; and (iv greater ROS generation under UV-light.

Characterization of remote O2-plasma-enhanced CVD SiO2/GaN(0001) structure using photoemission measurements

Science.gov (United States)

Truyen, Nguyen Xuan; Ohta, Akio; Makihara, Katsunori; Ikeda, Mitsuhisa; Miyazaki, Seiichi

2018-01-01

The control of chemical composition and bonding features at a SiO2/GaN interface is a key to realizing high-performance GaN power devices. In this study, an ∼5.2-nm-thick SiO2 film has been deposited on an epitaxial GaN(0001) surface by remote O2-plasma-enhanced chemical vapor deposition (O2-RPCVD) using SiH4 and Ar/O2 mixture gases at a substrate temperature of 500 °C. The depth profile of chemical structures and electronic defects of the O2-RPCVD SiO2/GaN structures has been evaluated from a combination of SiO2 thinning examined by X-ray photoelectron spectroscopy (XPS) and the total photoelectron yield spectroscopy (PYS) measurements. As a highlight, we found that O2-RPCVD is effective for fabricating an abrupt SiO2/GaN interface.

Self-Ordered Voids Formation in SiO2 Matrix by Ge Outdiffusion

OpenAIRE

B. Pivac; P. Dubček; J. Dasović; H. Zorc; S. Bernstorff; J. Zavašnik; B. Vlahovic

2018-01-01

The annealing behavior of very thin SiO2/Ge multilayers deposited on Si substrate by e-gun deposition in high vacuum was explored. It is shown that, after annealing at moderate temperatures (800°C) in inert atmosphere, Ge is completely outdiffused from the SiO2 matrix leaving small (about 3 nm) spherical voids embedded in the SiO2 matrix. These voids are very well correlated and formed at distances governed by the preexisting multilayer structure (in vertical direction) and self-organization ...

Use of MnO2 and MnO2 SiO2 for sorbing of Sr-90 from liquid rad waste

International Nuclear Information System (INIS)

Subiarto; Las, Thamzil; Aan BH, Martin; Utomo, Cahyo Hari

1998-01-01

The synthesis of MnO 2 adsorbent and MnO 2 -SiO 2 composite has been done. MnO 2 synthesis is done by the reaction of KMnO 4 , Mn(NO 3 ) 2 .4H 2 O and Na 2 S 2 O 4 ( MnO 2 -A, MnO 2 -B, and MnO 2 -T ). MnO 2 . SiO 2 is made from KMnO 4 , Na 2 SiO 3 , and H 2 O 2 . The result obtained show the best Sr-90 sorption by MnO 2 -A with Kd = 2085.63 ml/g, by MnO 2 -L with Kd = 755.09 ml/g, and by MnO 2 - SiO 2 composite with Kd = 1466.51 ml/g. From this result, we can conclude that MnO 2 -SiO 2 can be expanded for Sr-90 sorption from liquid radioactive waste. (author)

Ionic Liquid Confined in Mesoporous Polymer Membrane with Improved Stability for CO2/N2 Separation

Directory of Open Access Journals (Sweden)

Ming Tan

2017-09-01

Full Text Available Supported ionic liquid membranes (SILMs have a promising prospect of application in flue gas separation, owing to its high permeability and selectivity of CO2. However, existing SILMs have the disadvantage of poor stability due to the loss of ionic liquid from the large pores of the macroporous support. In this study, a novel SILM with high stability was developed by confining ionic liquid in a mesoporous polymer membrane. First, a mesoporous polymer membrane derived from a soluble, low-molecular-weight phenolic resin precursor was deposited on a porous Al2O3 support, and then 1-ethyl-3-methylimidazolium tetrafluoroborate ([emim][BF4] was immobilized inside mesopores of phenolic resin, forming the SILM under vacuum. Effects of trans-membrane pressure difference on the SILM separation performance were investigated by measuring the permeances of CO2 and N2. The SILM exhibits a high ideal CO2/N2 selectivity of 40, and an actual selectivity of approximately 25 in a mixed gas (50% CO2 and 50% N2 at a trans-membrane pressure difference of 2.5 bar. Compared to [emim][BF4] supported by polyethersulfone membrane with a pore size of around 0.45 μm, the [emim][BF4] confined in a mesoporous polymer membrane exhibits an improved stability, and its separation performance remained stable for 40 h under a trans-membrane pressure difference of 1.5 bar in a mixed gas before the measurement was intentionally stopped.

Thermally tunable VO2-SiO2 nanocomposite thin-film capacitors

Science.gov (United States)

Sun, Yifei; Narayanachari, K. V. L. V.; Wan, Chenghao; Sun, Xing; Wang, Haiyan; Cooley, Kayla A.; Mohney, Suzanne E.; White, Doug; Duwel, Amy; Kats, Mikhail A.; Ramanathan, Shriram

2018-03-01

We present a study of co-sputtered VO2-SiO2 nanocomposite dielectric thin-film media possessing continuous temperature tunability of the dielectric constant. The smooth thermal tunability is a result of the insulator-metal transition in the VO2 inclusions dispersed within an insulating matrix. We present a detailed comparison of the dielectric characteristics of this nanocomposite with those of a VO2 control layer and of VO2/SiO2 laminate multilayers of comparable overall thickness. We demonstrated a nanocomposite capacitor that has a thermal capacitance tunability of ˜60% between 25 °C and 100 °C at 1 MHz, with low leakage current. Such thermally tunable capacitors could find potential use in applications such as sensing, thermal cloaks, and phase-change energy storage devices.

Cytotoxicity and effect on GJIC of SiO2 nanoparticles in HL-7702 cells

International Nuclear Information System (INIS)

Pan Tao; Jin Minghua; Liu Xiaomei; Du Zhongjun; Zhou Xianqing; Huang Peili; Sun Zhiwei

2013-01-01

Objective: To study the cytotoxicity and effect on gap junction intracellular communication (GJIC) of SiO 2 nanoparticles in HL-7702 cells, and to provide experimental basis for toxicity assessment and the security applications of SiO 2 nanoparticles. Methods: Transmission electron microscope (TEM) was used to characterize two kinds of SiO 2 nanoparticles, verifying their size, dispersion and shape; dynamic light scattering (DLS) method was used to analyze the water dispersion and culture medium dispersion of the SiO 2 nanoparticles; MTT assay was carried out to examine the cytotoxicities of the two sizes SiO 2 nanoparticles on the cells; lactate dehydrogenase (LDH) release assay was performed to examine the integrity nano of the cell membrane; Scrape-loading and dye transfer assay was performed to examine the effect of SiO 2 nanoparticles on GJIC. Results: Based on the result of TEM, two kinds of SiO 2 nanoparticles were spherically shaped, uniformly sized and sporadically dispersed; the statistical analysis results showed the diameters of the two nanoparticles were (447.60±20.78) nm and (67.42±5.69) nm, respectively, thus they could be categorized as submicron scale and nano scale. The DLS method results manifested that the hydration nanoparticle sizes of the two SiO 2 nanoparticles were (684.37±18.76) nm, (128.31±7.64) nm in high purity water and (697.02±19.57) nm, (133.74±8.97) nm in RPMI-1640 solution, all the two nanoparticles were well dispersed without aggregation. MTT assay indicated that 24 h after treatment of SiO 2 nanoparticles, the cell viabilities were affected by both the size and the dose of the SiO 2 nanoparticles; the higher the dose was, the less viability the cells exhibited. Moreover, the nano scale particles inflicted more damage to the cells. LDH release assay indicated that the SiO 2 particles could also damage the cell membrane in a dose-dependent and size-dependent way. Scrape-loading and dye transfer assay indicated that the nano

The Effect of SiO2 Shell on the Suppression of Photocatalytic Activity of TiO2 and ZnO Nanoparticles

International Nuclear Information System (INIS)

Lee, Min Hee; Lee, Choon Soo; Patil, Umakant Mahadev; Kochuveedu, Saji Thomas

2012-01-01

In this study, we investigate the potential use of TiO 2 SiO 2 and ZnO SiO 2 core/shell nanoparticles (NPs) as effective UV shielding agent. In the typical synthesis, SiO 2 was coated over different types of TiO 2 (anatase and rutile) and ZnO by sol-gel method. The synthesized TiO 2 SiO 2 and ZnO SiO 2 Nps were characterized by UV-Vis, XRD, Sem and TEM. The UV-vis absorbance and transmittance spectra of core shell NPs showed an efficient blocking effect in the UV region and more than 90% transmittance in the visible region. XRD and SAED studies confirmed the formation of amorphous SiO 2 coated over the TiO 2 and ZnO NPs. The FESEM and TEM images shows that coating of SiO 2 over the surface of anatase, rutile TiO 2 and ZnO NPs resulted in the increase in particle size by ∼30 nm. In order to study the UV light shielding capability of the samples, photocatalytic degradation of methylene blue dye on TiO 2 SiO 2 and ZnO SiO 2 NPs was performed. Photocatalytic activity for both types of TiO 2 NPs was partially suppressed. In comparison, the photocatalytic activity of ZnO almost vanished after the SiO 2 coating

Passivation of pigment-grade TiO2 particles by nanothick atomic layer deposited SiO2 films

International Nuclear Information System (INIS)

King, David M; Liang Xinhua; Weimer, Alan W; Burton, Beau B; Akhtar, M Kamal

2008-01-01

Pigment-grade TiO 2 particles were passivated using nanothick insulating films fabricated by atomic layer deposition (ALD). Conformal SiO 2 and Al 2 O 3 layers were coated onto anatase and rutile powders in a fluidized bed reactor. SiO 2 films were deposited using tris-dimethylaminosilane (TDMAS) and H 2 O 2 at 500 deg. C. Trimethylaluminum and water were used as precursors for Al 2 O 3 ALD at 177 deg. C. The photocatalytic activity of anatase pigment-grade TiO 2 was decreased by 98% after the deposition of 2 nm SiO 2 films. H 2 SO 4 digest tests were performed to exhibit the pinhole-free nature of the coatings and the TiO 2 digest rate was 40 times faster for uncoated TiO 2 than SiO 2 coated over a 24 h period. Mass spectrometry was used to monitor reaction progress and allowed for dosing time optimization. These results demonstrate that the TDMAS-H 2 O 2 chemistry can deposit high quality, fully dense SiO 2 films on high radius of curvature substrates. Particle ALD is a viable passivation method for pigment-grade TiO 2 particles

Effect of interfacial SiO2- y layer and defect in HfO2- x film on flat-band voltage of HfO2- x /SiO2- y stacks for backside-illuminated CMOS image sensors

Science.gov (United States)

Na, Heedo; Lee, Jimin; Jeong, Juyoung; Kim, Taeho; Sohn, Hyunchul

2018-03-01

In this study, the effect of oxygen gas fraction during deposition of a hafnium oxide (HfO2- x ) film and the influence of the quality of the SiO2- y interlayer on the nature of flat-band voltage ( V fb) in TiN/HfO/SiO2- y /p-Si structures were investigated. X-ray photoemission spectroscopy analysis showed that the non-lattice oxygen peak, indicating an existing oxygen vacancy, increased as the oxygen gas fraction decreased during sputtering. From C- V and J- E analyses, the V fb behavior was significantly affected by the characteristics of the SiO2- y interlayer and the non-lattice oxygen fraction in the HfO2- x films. The HfO2- x /native SiO2- y stack presented a V fb of - 1.01 V for HfO2- x films with an oxygen gas fraction of 5% during sputtering. Additionally, the V fb of the HfO2- x /native SiO2- y stack could be controlled from - 1.01 to - 0.56 V by changing the deposition conditions of the HfO2- x film with the native SiO2- y interlayer. The findings of this study can be useful to fabricate charge-accumulating layers for backside-illuminated image sensor devices.

Irradiation-induced hardening/softening in SiO2 studied with instrumented indentation

International Nuclear Information System (INIS)

Nakano, Shinsuke; Muto, Shunsuke; Tanabe, Tetsuo

2005-01-01

To understand the plastic deformation mechanism of SiO 2 polytypes, we measured the mechanical parameters of He + -irradiated crystalline SiO 2 (α-quartz, c-SiO 2 ) and vitreous SiO 2 (silica glass, v-SiO 2 ) as functions of the irradiation dose, by using the instrumented indentation method combined with a finite-element analysis. We extracted the effects of local rotation and bending of the SiO 4 framework (the degree of local structural freedom), which play key roles in the plastic deformation, and expressed the hardness change with a simple formula. For v-SiO 2 , the changes in the density and the number of broken bonds correlated well with the change in the degree of freedom. In contrast, for c-SiO 2 the present formulation was insufficient to fully express the hardness change in the structural disordering regime. The structure change by irradiation peculiar to this material is discussed, based on the theoretical formulation

Analysis of an anti-reflecting nanowire transparent electrode for solar cells

Science.gov (United States)

Zhao, Zhexin; Wang, Ken Xingze; Fan, Shanhui

2017-03-01

Transparent electrodes are an important component in many optoelectronic devices, especially solar cells. In this paper, we investigate a nanowire transparent electrode that also functions as an anti-reflection coating for silicon solar cells, taking into account the practical constraints that the electrode is typically encapsulated and needs to be in electric contact with the semiconductor. Numerical simulations show that the electrode can provide near-perfect broadband anti-reflection over much of the frequency range above the silicon band gap for both polarizations while keeping the sheet resistance sufficiently low. To provide insights into the physics mechanism of this broadband anti-reflection, we introduce a generalized Fabry-Perot model, which captures the effects of the higher order diffraction channels as well as the modification of the reflection coefficient of the interface introduced by the nanowires. This model is validated using frequency-domain electromagnetic simulations. Our work here provides design guidelines for nanowire transparent electrode in a device configuration that is relevant for solar cell applications.

Engineering of mesoporous silica nanoparticles for release of ginsenoside CK and Rh2 to enhance their anticancer and anti-inflammatory efficacy: in vitro studies

Science.gov (United States)

Singh, Priyanka; Singh, Hina; Castro-Aceituno, Verónica; Ahn, Sungeun; Kim, Yeon Ju; Farh, Mohamed El-Agamy; Yang, Deok Chun

2017-07-01

The current study highlights the fabrication of drug delivery system by utilizing 200 nm mesoporous silica nanoparticles (MSNPs) with 4-nm pore size, as a carrier system for delivery ginsenoside compound K (CK) and Rh2 to enhance their efficacy. The two pharmacologically imperative ginsenosides, CK and Rh2, were loaded to the MSNPs to prepare MSNPs-CK and MSNPs-Rh2, respectively. A fluorescein isothiocyanate (FITC) fluorescent dye was combined in the MSNPs carrier system, in order to trace the cellular uptake of ginsenoside-loaded nanoparticles for in vitro studies. Following purification, the so-prepared MSNPs-CK-FITC and MSNPs-Rh2-FITC were characterized by several analytical techniques, which includes, high-pressure liquid chromatography (HPLC), 1H NMR, field emission transmission electron microscopy (FE-TEM), Fourier transform infrared spectroscopy (FT-IR), x-ray diffraction (XRD), thermogravimetric analysis (TGA), and dynamic light scattering (DLS). In vitro cytotoxicity assay in HaCaT skin cells, A549 lung cancer cells, HepG2 liver carcinoma cells, and HT-29 colon cancer cell lines were tested for MSNPs-CK-FITC and MSNPs-Rh2-FITC. The results demonstrate the excellent biocompatibility of nanoparticles in normal cell lines (HaCaT skin cells) and anticancer efficacy in all the tested cancer cell lines at 10-μM concentration. Additionally, the in vitro anti-inflammatory behavior of MSNPs-CK-FITC and MSNPs-Rh2-FITC were checked in RAW264.7 (murine macrophage) cell lines. The outcomes showed higher anti-inflammatory efficacy of MSNPs-CK-FITC and MSNPs-Rh2-FITC as compared to standard ginsenosides CK and Rh2 in RAW264.7 cell lines. Thus, with 200 nm MSNPs carrier system for the delivery ginsenosides CK and Rh2, a high amount of loading and increasing in vitro pharmacological efficacies of ginsenosides were realized. This study may provide useful insights for designing and improving the applicability of MSNPs for ginsenoside delivery.

Influence of SiO2 Addition on Properties of PTFE/TiO2 Microwave Composites

Science.gov (United States)

Yuan, Ying; Wang, Jie; Yao, Minghao; Tang, Bin; Li, Enzhu; Zhang, Shuren

2018-01-01

Composite substrates for microwave circuit applications have been fabricated by filling polytetrafluoroethylene (PTFE) polymer matrix with ceramic powder consisting of rutile TiO2 ( D 50 ≈ 5 μm) partially substituted with fused amorphous SiO2 ( D 50 ≈ 8 μm) with composition x vol.% SiO2 + (50 - x) vol.% TiO2 ( x = 0, 3, 6, 9, 12), and the effects of SiO2 addition on characteristics such as the density, moisture absorption, microwave dielectric properties, and thermal properties systematically investigated. The results show that the filler was well distributed throughout the matrix. High dielectric constant ( ɛ r > 7.19) and extremely low moisture absorption (ceramic particles served as barriers and improved the thermal stability of the PTFE polymer, retarding its decomposition. The temperature coefficient of dielectric constant ( τ ɛ ) of the composites shifted toward the positive direction (from - 309 ppm/°C to - 179 ppm/°C) as the SiO2 content was increased, while the coefficient of thermal expansion remained almost unchanged (˜ 35 ppm/°C).

Enhancement of reactivity in Li4SiO4-based sorbents from the nano-sized rice husk ash for high-temperature CO2 capture

International Nuclear Information System (INIS)

Wang, Ke; Zhao, Pengfei; Guo, Xin; Li, Yimin; Han, Dongtai; Chao, Yang

2014-01-01

achieved porous agglomerates of submicron particles resulting from a high anti-sintering character of its calcined CRHA. This more favorable structure of CRHA-Li 4 SiO 4 could lead to the higher CO 2 adsorption capacity of 30.5 wt% (6.92 mmol/g Li 4 SiO 4 , corresponding to 83.1% efficiency), faster kinetic behavior and better regenerability (its adsorption capacity only decreased 2.1 wt% from the first cycle to the 15th cycle), which was illustrated by the thermogravimetric analyses and fix bed results

Bioactivity of gel-glass powders in the CaO-SiO2 system: a comparison with ternary (CaO-P2O5-SiO2) and quaternary glasses (SiO2-CaO-P2O5-Na2O).

Science.gov (United States)

Saravanapavan, Priya; Jones, Julian R; Pryce, Russell S; Hench, Larry L

2003-07-01

Bioactive glasses react chemically with body fluids in a manner that is compatible with the repair processes of the tissues. This results in the formation of an interfacial bond between the glasses and living tissue. Bioactive glasses also stimulate bone-cell proliferation. This behavior is dependent on the chemical composition as well as the surface texture of the glasses. It has been recently reported that gel-derived monolith specimens in the binary SiO2 - CaO are bioactive over a similar molar range of SiO2 content as the previously studied ternary CaO-P2O5-SiO2 system. In this report, the preparation and bioactivity of the binary gel-glass powder with 70 mol % SiO2 is discussed and its bioactivity is compared with the melt-derived 45S5 (quaternary) Bioglass and sol-gel-derived 58S (ternary) bioactive gel-glass compositions. Dissolution kinetic parameters K(1) and K(2) were also computed based on the silicon release for all glass powders. It was shown that the simple two-component SiO2-CaO gel-glass powder is bioactive with comparable dissolution rates as the clinically used melt-derived 45S5 Bioglass powder and extensively studied sol-gel-derived 58S gel-glass powder. Copyright 2003 Wiley Periodicals, Inc.

Structural colors of the SiO2/polyethyleneimine thin films on poly(ethylene terephthalate) substrates

International Nuclear Information System (INIS)

Jia, Yanrong; Zhang, Yun; Zhou, Qiubao; Fan, Qinguo; Shao, Jianzhong

2014-01-01

The SiO 2 /polyethyleneimine (PEI) films with structural colors on poly(ethylene terephthalate) (PET) substrates were fabricated by an electrostatic self-assembly method. The morphology of the films was characterized by Scanning Electron Microscopy. The results showed that there was no distinguishable multilayered structure found of SiO 2 /PEI films. The optical behaviors of the films were investigated through the color photos captured by a digital camera and the color measurement by a multi-angle spectrophotometer. Different hue and brightness were observed at various viewing angles. The structural colors were dependent on the SiO 2 particle size and the number of assembly cycles. The mechanism of the structural colors generated from the assembled films was elucidated. The morphological structures and the optical properties proved that the SiO 2 /PEI film fabricated on PET substrate formed a homogeneous inorganic/organic SiO 2 /PEI composite layer, and the structural colors were originated from single thin film interference. - Highlights: • SiO 2 /PEI thin films were electrostatic self-assembled on PET substrates. • The surface morphology and optical behavior of the film were investigated. • The structural colors varied with various SiO 2 particle sizes and assembly cycles. • Different hue and lightness of SiO 2 /PEI film were observed at various viewing angles. • Structural color of the SiO 2 /PEI film originated from single thin film interference

PENGUJIAN AKTIVITAS KOMPOSIT Fe2O3-SiO2 SEBAGAI FOTOKATALIS PADA FOTODEGRADASI 4-KLOROFENOL (The Activity Test of Fe2O3-SiO2 Composite As Photocatalyst on 4-Chlorophenol Photodegradation

Directory of Open Access Journals (Sweden)

Eko Sri Kunarti

2009-03-01

Full Text Available ABSTRAK  Pada penelitian ini telah dilakukan pengujian aktivitas komposit Fe2O3-SiO2 sebagai fotokatalis pada fotodegradasi 4-klorofenol. Penelitian diawali dengan preparasi dan karakterisasi fotokatalis Fe2O3-SiO2. Preparasi dilakukan dengan metode sol-gel pada temperatur kamar menggunakan tetraetil ortosilikat (TEOS dan besi (III nitrat sebagai prekursor diikuti dengan perlakuan termal pada temperature 500 oC. Karakterisasi dilakukan dengan metode spektrometri inframerah, difraksi sinar-X dan spektrometri fluoresensi sinar-X. Uji aktivitas komposit untuk fotodegradasi 4-klorofenol dilakukan dalam reaktor tertutup yang dilengkapi dengan lampu UV. Pada uji ini telah dipelajari pengaruh waktu penyinaran dan pH larutan terhadap efektivitas fotodegradasi 4-klorofenol. Hasil penelitian menunjukkan bahwa komposit Fe2O3-SiO2 dapat dipreparasi dengan metode sol-gel pada temperatur kamar diikuti perlakuan termal. Komposit Fe2O3-SiO2 dapat meningkatkan efektivitas fotodegradasi 4-klorofenol dari 11,86 % menjadi 55,38 %. Efektivitas fotodegradasi 4- klorofenol dipengaruhi waktu penyinaran dan pH larutan yang semakin lama waktu penyinaran efektifitas fotodegradasi semakin tinggi, namun waktu penyinaran yang lebih lama dari 4 jam dapat menurunkan efektivitasnya. pH larutan memberikan pengaruh yang berbeda-beda pada efektivitas fotodegradasi 4-klorofenol.   ABSTRACT The activity test of Fe2O3-SiO2 composite as photocatalyst on 4-chlorophenol photodegradation has been studied. The research was initiated by preparation of Fe2O3-SiO2 photocatalyst and followed by characterization. The preparation was conducted by sol-gel method at room temperature using tetraethylorthosilicate (TEOS and iron (III nitrate as precursors followed by thermal treatment at a temperature of 500oC. The characterizations were performed by X-ray Diffraction (XRD, Infrared and X-ray Fluorescence Spectrophotometry. The photocatalytic activity test of composites for 4 chlorophenol

Analysis of SiO2 nanoparticles binding proteins in rat blood and brain homogenate

Directory of Open Access Journals (Sweden)

Shim KH

2014-12-01

Full Text Available Kyu Hwan Shim,1 John Hulme,1 Eun Ho Maeng,2 Meyoung-Kon Kim,3 Seong Soo A An1 1Department of Bionano Technology, Gachon Medical Research Institute, Gachon University, Sungnam-si, 2Department of Analysis, KTR, Kimpo, Gyeonggi-do, 3Department of Biochemistry and Molecular Biology, Korea University Medical School and College, Seoul, South Korea Abstract: A multitude of nanoparticles, such as titanium oxide (TiO2, zinc oxide, aluminum oxide, gold oxide, silver oxide, iron oxide, and silica oxide, are found in many chemical, cosmetic, pharmaceutical, and electronic products. Recently, SiO2 nanoparticles were shown to have an inert toxicity profile and no association with an irreversible toxicological change in animal models. Hence, exposure to SiO2 nanoparticles is on the increase. SiO2 nanoparticles are routinely used in numerous materials, from strengthening filler for concrete and other construction composites, to nontoxic platforms for biomedical application, such as drug delivery and theragnostics. On the other hand, recent in vitro experiments indicated that SiO2 nanoparticles were cytotoxic. Therefore, we investigated these nanoparticles to identify potentially toxic pathways by analyzing the adsorbed protein corona on the surface of SiO2 nanoparticles in the blood and brain of the rat. Four types of SiO2 nanoparticles were chosen for investigation, and the protein corona of each type was analyzed using liquid chromatography-tandem mass spectrometry technology. In total, 115 and 48 plasma proteins from the rat were identified as being bound to negatively charged 20 nm and 100 nm SiO2 nanoparticles, respectively, and 50 and 36 proteins were found for 20 nm and 100 nm arginine-coated SiO2 nanoparticles, respectively. Higher numbers of proteins were adsorbed onto the 20 nm sized SiO2 nanoparticles than onto the 100 nm sized nanoparticles regardless of charge. When proteins were compared between the two charges, higher numbers of proteins were

Preparation of mesoporous CdS-containing TiO{sub 2} film and enhanced visible light photocatalytic property

Energy Technology Data Exchange (ETDEWEB)

Zhu, Yanmei; Wang, Renliang, E-mail: rlwang@tsmc.edu.cn; Zhang, Wenping; Ge, Haiyan; Wang, Xiaopeng; Li, Li

2015-01-15

Highlights: • Well-dispersed distribution of CdS nanoparticles inside of TiO{sub 2} mesoporous structures was fabricated. • The sensitization of CdS nanoparticles significantly extends the response of TiO{sub 2} mesoporous film in the visible region. • An improved visible light photocatalytic activity was observed by the CdS–MTF. - Abstract: Mesoporous TiO{sub 2} films containing CdS nanocrystals were successfully fabricated by a two-step process of successive ionic layer adsorption and reaction (SILAR) technique and a solvothermal method followed by annealing. The distribution of CdS nanoparticles in the inner structures of the TiO{sub 2} mesoporous films is confirmed by field emission scanning electron microscope. The CdS modification of the mesoporous films results in an increase in the visible light adsorption, and exhibits more excellent photocatalytic degradation of methyl orange (MO) under visible light irradiation.

Incorporation of Znq2 complexes into mesoporous silica and their transparent polymer luminescent nanocomposites

International Nuclear Information System (INIS)

Du Yaying; Fu Yuqin; Shi Yongli; Lue Xiaodan; Lue Changli; Su Zhongmin

2009-01-01

Znq 2 -functionalized colloidal mesoporous silicas (Znq 2 -CMS)/polymer transparent nanocomposites were prepared by in situ bulk polymerization. CMS nanoparticles or nanorods with hydroxyl-, mercapto- and sulfonic-functionalized interiors were obtained by different synthetic routes in the nanosize dimensions between 50 and 500 nm. The luminescent Znq 2 complex was successfully introduced in the pores of different mesoporous silicas by chemical adsorption as the driving force. The different internal circumstances of mesoporous silicas had an obvious effect on the luminescence and lifetime of Znq 2 complex. The transparent fluorescent nanocomposites were fabricated from different Znq 2 -CMS and suitable monomers. The Znq 2 -CMS were uniformly dispersed in the polymer matrix without evident aggregation. The photoluminescence properties of Znq 2 -CMS in the transparent matrix exhibited a dependence on the inner surrounding of CMS due to the interaction between Znq 2 -CMS and polymers. The maximum emission peak of the nanocomposites had a red-shift of 28 nm as compared to pure Znq 2 -CMS. - Graphical abstract: Znq 2 -functionalized colloidal mesoporous silicas (Znq 2 -CMS)/polymer transparent fluorescent nanocomposites were prepared by in situ bulk polymerization. The figure shows the synthetic scheme for the Znq 2 -CMS and their transparent bulk nanocomposites.

Screen-Printed Photochromic Textiles through New Inks Based on SiO2@naphthopyran Nanoparticles.

Science.gov (United States)

Pinto, Tânia V; Costa, Paula; Sousa, Céu M; Sousa, Carlos A D; Pereira, Clara; Silva, Carla J S M; Pereira, Manuel Fernando R; Coelho, Paulo J; Freire, Cristina

2016-10-26

Photochromic silica nanoparticles (SiO 2 @NPT), fabricated through the covalent immobilization of silylated naphthopyrans (NPTs) based on 2H-naphtho[1,2-b]pyran (S1, S2) and 3H-naphtho[2,1-b]pyran (S3, S4) or through the direct adsorption of the parent naphthopyrans (1, 3) onto silica nanoparticles (SiO 2 NPs), were successfully incorporated onto cotton fabrics by a screen-printing process. Two aqueous acrylic- (AC-) and polyurethane- (PU-) based inks were used as dispersing media. All textiles exhibited reversible photochromism under UV and solar irradiation, developing fast responses and intense coloration. The fabrics coated with SiO 2 @S1 and SiO 2 @S2 showed rapid color changes and high contrasts (ΔE* ab = 39-52), despite presenting slower bleaching kinetics (2-3 h to fade to the original color), whereas the textiles coated with SiO 2 @S3 and SiO 2 @S4 exhibited excellent engagement between coloration and decoloration rates (coloration and fading times of 1 and 2 min, respectively; ΔE* ab = 27-53). The PU-based fabrics showed excellent results during the washing fastness tests, whereas the AC-based textiles evidenced good results only when a protective transfer film was applied over the printed design.

Densification of ∼5 nm-thick SiO_2 layers by nitric acid oxidation

International Nuclear Information System (INIS)

Choi, Jaeyoung; Joo, Soyeong; Park, Tae Joo; Kim, Woo-Byoung

2017-01-01

Highlights: • Leakage current density of the commercial PECVD grown ∼5 nm SiO_2 layer has been decreased about three orders of magnitude by densification. • The densification of SiO_2 layer is achieved by high oxidation ability of O·. • Densities of suboxide, fixed charge (N_f) and defect state (N_d) in SiO_2/Si interface are decreased by NAOS and PMA. • Tunneling barrier height (Φ_t) is increased because of the increase of atomic density in SiO_2 layer. - Abstract: Low-temperature nitric acid (HNO_3) oxidation of Si (NAOS) has been used to improve the interface and electrical properties of ∼5 nm-thick SiO_2/Si layers produced by plasma-enhanced chemical vapor deposition (PECVD). Investigations of the physical properties and electrical characteristics of these thin films revealed that although their thickness is not changed by NAOS, the leakage current density at a gate bias voltage of −1 V decreases by about two orders of magnitude from 1.868 × 10"−"5 A/cm"2. This leakage current density was further reduced by post-metallization annealing (PMA) at 250 °C for 10 min in a 5 vol.% hydrogen atmosphere, eventually reaching a level (5.2 × 10"−"8 A/cm"2) approximately three orders of magnitude less than the as-grown SiO_2 layer. This improvement is attributed to a decrease in the concentration of suboxide species (Si"1"+, Si"2"+ and Si"3"+) in the SiO_2/Si interface, as well as a decrease in the equilibrium density of defect sites (N_d) and fixed charge density (N_f). The barrier height (Φ_t) generated by a Poole-Frenkel mechanism also increased from 0.205 to 0.371 eV after NAOS and PMA. The decrease in leakage current density is therefore attributed to a densification of the SiO_2 layer in combination with the removal of OH species and increase in interfacial properties at the SiO_2/Si interface.

Anti-reflective polymer-nanocomposite coatings fabricated by RIR-MAPLE

Science.gov (United States)

Singaravalu, S.; Mayo, D. C.; Park, H. K.; Schriver, K. E.; Haglund, R. F.

2013-02-01

There is increasing demand for functional polymeric optical coatings for plastic substrates. In the case of anti-reflective (AR) coatings, this is challenging because polymers exhibit a relatively narrow range of refractive indices. We synthesized a four-layer AR stack using hybrid polymer:nanoparticle materials deposited by resonant infrared matrixassisted pulsed laser evaporation (RIR-MAPLE). An Er:YAG laser ablated frozen solutions of a high-index composite containing TiO2 nanoparticles and PMMA, alternating with a low-index solution of PMMA. The optimized AR coatings, with thicknesses calculated using commercial software, yielded a coating for polycarbonate with relative transmission over 94%, scattering less than 5% and a reflection coefficient below 0.8% across the visible range.

Ion assisted deposition of SiO2 film from silicon

Science.gov (United States)

Pham, Tuan. H.; Dang, Cu. X.

2005-09-01

Silicon dioxide, SiO2, is one of the preferred low index materials for optical thin film technology. It is often deposited by electron beam evaporation source with less porosity and scattering, relatively durable and can have a good laser damage threshold. Beside these advantages the deposition of critical optical thin film stacks with silicon dioxide from an E-gun was severely limited by the stability of the evaporation pattern or angular distribution of the material. The even surface of SiO2 granules in crucible will tend to develop into groove and become deeper with the evaporation process. As the results, angular distribution of the evaporation vapor changes in non-predicted manner. This report presents our experiments to apply Ion Assisted Deposition process to evaporate silicon in a molten liquid form. By choosing appropriate process parameters we can get SiO2 film with good and stable property.

Electrochemical synthesis of mesoporous Pt-Au binary alloys with tunable compositions for enhancement of electrochemical performance.

Science.gov (United States)

Yamauchi, Yusuke; Tonegawa, Akihisa; Komatsu, Masaki; Wang, Hongjing; Wang, Liang; Nemoto, Yoshihiro; Suzuki, Norihiro; Kuroda, Kazuyuki

2012-03-21

Mesoporous Pt-Au binary alloys were electrochemically synthesized from lyotropic liquid crystals (LLCs) containing corresponding metal species. Two-dimensional exagonally ordered LLC templates were prepared on conductive substrates from diluted surfactant solutions including water, a nonionic surfactant, ethanol, and metal species by drop-coating. Electrochemical synthesis using such LLC templates enabled the preparation of ordered mesoporous Pt-Au binary alloys without phase segregation. The framework composition in the mesoporous Pt-Au alloy was controlled simply by changing the compositional ratios in the precursor solution. Mesoporous Pt-Au alloys with low Au content exhibited well-ordered 2D hexagonal mesostructures, reflecting those of the original templates. With increasing Au content, however, the mesostructural order gradually decreased, thereby reducing the electrochemically active surface area. Wide-angle X-ray diffraction profiles, X-ray photoelectron spectra, and elemental mapping showed that both Pt and Au were atomically distributed in the frameworks. The electrochemical stability of mesoporous Pt-Au alloys toward methanol oxidation was highly improved relative to that of nonporous Pt and mesoporous Pt films, suggesting that mesoporous Pt-Au alloy films are potentially applicable as electrocatalysts for direct methanol fuel cells. Also, mesoporous Pt-Au alloy electrodes showed a highly sensitive amperometric response for glucose molecules, which will be useful in next-generation enzyme-free glucose sensors.

Efficient capture of CO2 over ordered micro-mesoporous hybrid carbon nanosphere

Science.gov (United States)

Chen, Changwei; Yu, Yanke; He, Chi; Wang, Li; Huang, Huang; Albilali, Reem; Cheng, Jie; Hao, Zhengping

2018-05-01

Four kinds of carbon-based adsorbents (micro-mesoporous hybrid carbon nanosphere and N-doped hollow carbon sphere with single-, double- or ruga-shell morphology) with different structural and textural properties were prepared and systematically studied in CO2 capture. All synthesized samples possess high specific surface area (828-910 m2 g-1), large pore volume (0.71-1.81 cm3 g-1), and different micropore contents varied from 2.1% to 46.4%. Amongst, the ordered micro-mesoporous carbon nanosphere (OM-CNS) exhibits the best adsorption performance with CO2 uptake as high as 3.01 mmol g-1 under conditions of 298 K and 1.0 bar, better than most of the reported CO2 adsorbents. The excellent CO2 adsorption capacity of OM-CNS can be reasonably attributed to the synergistic effect of ordered mesopore channels and abundant structural micropores which are beneficial for the diffusion and trapping of CO2 adsorbate. Moreover, the OM-CNS shows excellent CO2 trapping selectivity and superior stability and recyclability, which endow the OM-CNS as a promising and environmental-friendly adsorbent for CO2 capture and separation under practical conditions.

SIMULTANEOUS OBSERVATIONS OF SiO AND H{sub 2}O MASERS TOWARD KNOWN STELLAR H{sub 2}O MASER SOURCES

Energy Technology Data Exchange (ETDEWEB)

Kim, Jaeheon [Yonsei University Observatory, Seongsan-ro 262, Seodaemun, Seoul 120-749 (Korea, Republic of); Cho, Se-Hyung [Korean VLBI Network Yonsei Radio Astronomy Observatory, Yonsei University, Seongsan-ro 262, Seodaemun, Seoul 120-749 (Korea, Republic of); Kim, Sang Joon, E-mail: jhkim@kasi.re.kr, E-mail: cho@kasi.re.kr, E-mail: sjkim1@khu.ac.kr [Department of Astronomy and Space Science, Kyung Hee University, Seocheon-Dong, Giheung-Gu, Yongin, Gyeonggi-Do 446-701 (Korea, Republic of)

2013-01-01

We present the results of simultaneous observations of SiO v = 1, 2, {sup 29}SiO v = 0, J = 1-0, and H{sub 2}O 6{sub 16}-5{sub 23} maser lines toward 152 known stellar H{sub 2}O maser sources using the Yonsei 21 m radio telescope of the Korean VLBI Network from 2009 June to 2011 January. Both SiO and H{sub 2}O masers were detected from 62 sources with a detection rate of 40.8%. The SiO-only maser emission without H{sub 2}O maser detection was detected from 27 sources, while the H{sub 2}O-only maser without SiO maser detection was detected from 22 sources. Therefore, the overall SiO maser emission was detected from 89 sources, resulting in a detection rate of 58.6%. We have identified 70 new detections of the SiO maser emission. For both H{sub 2}O and SiO maser detected sources, the peak and integrated antenna temperatures of SiO masers are stronger than those of H{sub 2}O masers in both Mira variables and OH/IR stars and the relative intensity ratios of H{sub 2}O to SiO masers in OH/IR stars are larger than those in Mira variables. In addition, distributions of 152 observed sources were investigated in the IRAS two-color diagram.

Crack-resistant Al2O3-SiO2 glasses.

Science.gov (United States)

Rosales-Sosa, Gustavo A; Masuno, Atsunobu; Higo, Yuji; Inoue, Hiroyuki

2016-04-07

Obtaining "hard" and "crack-resistant" glasses have always been of great important in glass science and glass technology. However, in most commercial glasses both properties are not compatible. In this work, colorless and transparent xAl2O3-(100-x)SiO2 glasses (30 ≤ x ≤ 60) were fabricated by the aerodynamic levitation technique. The elastic moduli and Vickers hardness monotonically increased with an increase in the atomic packing density as the Al2O3 content increased. Although a higher atomic packing density generally enhances crack formation in conventional oxide glasses, the indentation cracking resistance increased by approximately seven times with an increase in atomic packing density in binary Al2O3-SiO2 glasses. In particular, the composition of 60Al2O3 • 40SiO2 glass, which is identical to that of mullite, has extraordinary high cracking resistance with high elastic moduli and Vickers hardness. The results indicate that there exist aluminosilicate compositions that can produce hard and damage-tolerant glasses.

Preparation of mesoporous alumina particles by spray pyrolysis and application to double bond migration of 2-butene.

Science.gov (United States)

Song, Ki Chang; Kim, Joo Hyun; Kim, Jin Han; Jung, Kyeong Youl; Park, Young-Kwon; Jeon, Jong-Ki

2011-07-01

The objective of the present study is to investigate the catalytic performance of mesoporous alumina that were prepared via spray pyrolysis for double bond migration from 2-butene to 1-butene. The mesoporous alumina particles were prepared via spray pyrolysis by changing the types of organic surfactants and Al precursors. The texture and acidic properties of mesoporous alumina were analyzed through N2 adsorption, SEM, ammonia-temperature programmed desorption, and FT-IR of adsorbed pyridine. The morphologies and texture properties of the mesoporous alumina were found to have been strongly influenced by the combination of the Al precursor and the structure-directing agents. The mesoporous alumina samples had two kinds of acidic sites: a Lewis acid site and a H-bonded weak acid site. 1-Butene was produced selectively through double bond migration of 2-butene over all of the mesoporous alumina catalysts. The catalyst prepared by using a chloride compound as an aluminium precursor and CTAC as a structure-directing agent showed the highest activity in the double bond migration of 2-butene, which was attributed to its large surface area and an overall high amount of acid sites.

Preparation of Carbon Nanotube/TiO2 Mesoporous Hybrid Photoanode with Iron Pyrite (FeS2) Thin Films Counter Electrodes for Dye-Sensitized Solar Cell

OpenAIRE

Bayram Kilic; Sunay Turkdogan; Aykut Astam; Oguz Can Ozer; Mansur Asgin; Hulya Cebeci; Deniz Urk; Selin Pravadili Mucur

2016-01-01

Multi-walled carbon nanotube (MWCNT)/TiO2 mesoporous networks can be employed as a new alternative photoanode in dye-sensitized solar cells (DSSCs). By using the MWCNT/TiO2 mesoporous as photoanodes in DSSC, we demonstrate that the MWCNT/TiO2 mesoporous photoanode is promising alternative to standard FTO/TiO2 mesoporous based DSSC due to larger specific surface area and high electrochemical activity. We also show that iron pyrite (FeS2) thin films can be used as an efficient counter electrode...

Enhanced antioxidation and microwave absorbing properties of SiO2-coated flaky carbonyl iron particles

Science.gov (United States)

Zhou, Yingying; Xie, Hui; Zhou, Wancheng; Ren, Zhaowen

2018-01-01

SiO2 was successfully coated on the surface of flaky carbonyl iron particles using a chemical bath deposition method in the presence of 3-aminopropyl triethoxysilane (APTES). The morphologies, composition, valence states of elements, as well as antioxidation and electromagnetic properties of the samples were characterized by scanning electron microscope (SEM), energy dispersive spectrometer (EDS), X-ray photoelectron spectroscopy (XPS), thermogravimetric (TG) and microwave network analyzer. TG curve shows the obvious weight gain of carbonyl iron was deferred to 360 °C after SiO2-coated, which can be ascribed to the exits of SiO2 overlayer. Compared with the raw carbonyl iron, SiO2-coated sample shows good wave absorption performance due to its impedance matching. The electromagnetic properties of raw and SiO2-coated carbonyl iron particles were characterized in X band before and after heat treatment at 250 °C for 10 h. It was established that SiO2-coated carbonyl iron demonstrate good thermal stability, indicating SiO2-coating is useful in the usage of microwave absorbers operating at temperature up to 250 °C.

Facile route for synthesis of mesoporous Cr2O3 sheet as anode materials for Li-ion batteries

International Nuclear Information System (INIS)

Cao, Zhiqin; Qin, Mingli; Jia, Baorui; Zhang, Lin; Wan, Qi; Wang, Mingshan; Volinsky, Alex A.; Qu, Xuanhui

2014-01-01

Mesoporous Cr 2 O 3 with a high specific surface area of 162 m 2 g −1 is prepared by the solution combustion method. The mesoporous Cr 2 O 3 has a sheet structure, which consists of nanoparticles with an average size of 20 nm. As an anode electrode material for rechargeable lithium-ion batteries, the mesoporous Cr 2 O 3 nanoparticles display enhanced electrochemical performance. Stable and reversible capacity of 480 mA h g −1 after 55 cycles is demonstrated. The enhanced electrochemical performance of the Cr 2 O 3 can be attributed to the high surface area and morphological characteristics of mesoporous materials

Surface properties of SiO2 with and without H2O2 treatment as gate dielectrics for pentacene thin-film transistor applications

Science.gov (United States)

Hung, Cheng-Chun; Lin, Yow-Jon

2018-01-01

The effect of H2O2 treatment on the surface properties of SiO2 is studied. H2O2 treatment leads to the formation of Si(sbnd OH)x at the SiO2 surface that serves to reduce the number of trap states, inducing the shift of the Fermi level toward the conduction band minimum. H2O2 treatment also leads to a noticeable reduction in the value of the SiO2 capacitance per unit area. The effect of SiO2 layers with H2O2 treatment on the behavior of carrier transports for the pentacene/SiO2-based organic thin-film transistor (OTFT) is also studied. Experimental identification confirms that the shift of the threshold voltage towards negative gate-source voltages is due to the reduced number of trap states in SiO2 near the pentacene/SiO2 interface. The existence of a hydrogenated layer between pentacene and SiO2 leads to a change in the pentacene-SiO2 interaction, increasing the value of the carrier mobility.

Scalable 2D Mesoporous Silicon Nanosheets for High-Performance Lithium-Ion Battery Anode.

Science.gov (United States)

Chen, Song; Chen, Zhuo; Xu, Xingyan; Cao, Chuanbao; Xia, Min; Luo, Yunjun

2018-03-01

Constructing unique mesoporous 2D Si nanostructures to shorten the lithium-ion diffusion pathway, facilitate interfacial charge transfer, and enlarge the electrode-electrolyte interface offers exciting opportunities in future high-performance lithium-ion batteries. However, simultaneous realization of 2D and mesoporous structures for Si material is quite difficult due to its non-van der Waals structure. Here, the coexistence of both mesoporous and 2D ultrathin nanosheets in the Si anodes and considerably high surface area (381.6 m 2 g -1 ) are successfully achieved by a scalable and cost-efficient method. After being encapsulated with the homogeneous carbon layer, the Si/C nanocomposite anodes achieve outstanding reversible capacity, high cycle stability, and excellent rate capability. In particular, the reversible capacity reaches 1072.2 mA h g -1 at 4 A g -1 even after 500 cycles. The obvious enhancements can be attributed to the synergistic effect between the unique 2D mesoporous nanostructure and carbon capsulation. Furthermore, full-cell evaluations indicate that the unique Si/C nanostructures have a great potential in the next-generation lithium-ion battery. These findings not only greatly improve the electrochemical performances of Si anode, but also shine some light on designing the unique nanomaterials for various energy devices. © 2018 WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.

Development of nano SiO2 incorporated nano zinc phosphate coatings on mild steel

International Nuclear Information System (INIS)

Tamilselvi, M.; Kamaraj, P.; Arthanareeswari, M.; Devikala, S.; Selvi, J. Arockia

2015-01-01

Highlights: • Nano SiO 2 incorporated nano zinc phosphate coating on mild steel was developed. • Coatings showed enhanced corrosion resistance. • The nano SiO 2 is adsorbed on mild steel surface and become nucleation sites. • The nano SiO 2 accelerates the phosphating process. - Abstract: This paper reports the development of nano SiO 2 incorporated nano zinc phosphate coatings on mild steel at low temperature for achieving better corrosion protection. A new formulation of phosphating bath at low temperature with nano SiO 2 was attempted to explore the possibilities of development of nano zinc phosphate coatings on mild steel with improved corrosion resistance. The coatings developed were studied by Scanning Electron Microscopy (SEM), Energy-Dispersive X-ray Spectroscopy (EDX), X-ray Diffraction (XRD), Transmission Electron Microscopy (TEM) and Electrochemical measurements. Significant variation in the coating weight, morphology and corrosion resistance was observed as nano SiO 2 concentrations varied from 0.5–4 g/L. The results showed that, the nano SiO 2 in the phosphating solution changed the initial potential of the interface between mild steel substrate and phosphating solution and reduce the activation energy of the phosphating process, increase the nucleation sites and yielded zinc phosphate coatings of higher coating weight, greater surface coverage and enhanced corrosion resistance. Better corrosion resistance was observed for coatings derived from phosphating bath containing 1.5 g/L nano SiO 2 . The new formulation reported in the present study was free from Ni or Mn salts and had very low concentration of sodium nitrite (0.4 g/L) as accelerator

Thermal Annealing Effect on Optical Properties of Binary TiO2-SiO2 Sol-Gel Coatings

Directory of Open Access Journals (Sweden)

Xiaodong Wang

2012-12-01

Full Text Available TiO2-SiO2 binary coatings were deposited by a sol-gel dip-coating method using tetrabutyl titanate and tetraethyl orthosilicate as precursors. The structure and chemical composition of the coatings annealed at different temperatures were analyzed by Raman spectroscopy and Fourier Transform Infrared (FTIR spectroscopy. The refractive indices of the coatings were calculated from the measured transmittance and reflectance spectra. An increase in refractive index with the high temperature thermal annealing process was observed. The Raman and FTIR results indicate that the refractive index variation is due to changes in the removal of the organic component, phase separation and the crystal structure of the binary coatings.

Design of flexible PANI-coated CuO-TiO2-SiO2 heterostructure nanofibers with high ammonia sensing response values

Science.gov (United States)

Pang, Zengyuan; Nie, Qingxin; Lv, Pengfei; Yu, Jian; Huang, Fenglin; Wei, Qufu

2017-06-01

We report a room-temperature ammonia sensor with extra high response values and ideal flexibility, including polyaniline (PANI)-coated titanium dioxide-silicon dioxide (TiO2-SiO2) or copper oxide-titanium dioxide-silicon dioxide (CuO-TiO2-SiO2) composite nanofibers. Such flexible inorganic TiO2-SiO2 and CuO-TiO2-SiO2 composite nanofibers were prepared by electrospinning, followed by calcination. Then, in situ polymerization of aniline monomers was carried out with inorganic TiO2-SiO2 and CuO-TiO2-SiO2 composite nanofibers as templates. Gas sensing tests at room temperature indicated that the obtained CuO-TiO2-SiO2/PANI composite nanofibers had much higher response values to ammonia gas (ca. 45.67-100 ppm) than most of those reported before as well as the prepared TiO2-SiO2/PANI composite nanofibers here. These excellent sensing properties may be due to the P-N, P-P heterojunctions and a structure similar to field-effect transistors formed on the interfaces between PANI, TiO2, and CuO, which is p-type, n-type, and p-type semiconductor, respectively. In addition, the prepared free-standing CuO-TiO2-SiO2/PANI composite nanofiber membrane was easy to handle and possessed ideal flexibility, which is promising for potential applications in wearable sensors in the future.

Facile synthesis of microporous SiO2/triangular Ag composite nanostructures for photocatalysis

Science.gov (United States)

Sirohi, Sidhharth; Singh, Anandpreet; Dagar, Chakit; Saini, Gajender; Pani, Balaram; Nain, Ratyakshi

2017-11-01

In this article, we present a novel fabrication of microporous SiO2/triangular Ag nanoparticles for dye (methylene blue) adsorption and plasmon-mediated degradation. Microporous SiO2 nanoparticles with pore size aminopropyl) trimethoxysilane) to introduce amine groups. Amine-functionalized microporous silica was used for adsorption of triangular silver (Ag) nanoparticles. The synthesized microporous SiO2 nanostructures were investigated for adsorption of different dyes including methylene blue, congo red, direct green 26 and curcumin crystalline. Amine-functionalized microporous SiO2/triangular Ag nanostructures were used for plasmon-mediated photocatalysis of methylene blue. The experimental results revealed that the large surface area of microporous silica facilitated adsorption of dye. Triangular Ag nanoparticles, due to their better charge carrier generation and enhanced surface plasmon resonance, further enhanced the photocatalysis performance.

Composition and crystallization kinetics of R2O-Al2O3-SiO2 glass-ceramics

International Nuclear Information System (INIS)

Xiong, Dehua; Cheng, Jinshu; Li, Hong

2010-01-01

The crystallization behavior and microstructure of R 2 O-Al 2 O 3 -SiO 2 (R means K, Na and Li) glass were investigated by means of differential scanning calorimeter (DSC), X-ray diffraction (XRD) and scanning electron microscopy (SEM). The crystallization kinetic parameters including the crystallization apparent activation energy (E a ), the Avrami parameter (n), glass transition temperature (T g ) and the activity energy of glass transition (E t ) were also measured with different methods. The results have shown that: the DSC traces of composition A parent glass have two different precipitation crystallization peaks corresponding to E a1 (A) = 151.4 kJ/mol (Li 2 SiO 3 ) and E a2 (A) = 623.1 kJ/mol (Li 2 Si 2 O 5 ), the average value of n = 1.70 (Li 2 Si 2 O 5 ) for the surface crystallization and E t (A) = 202.8 kJ/mol. And E a (B) = 50.7 kJ/mol (Li 2 SiO 3 ), the average value of n = 3.89 (Li 2 SiO 3 ) for the bulk crystallization and E t (B) = 220.4 kJ/mol for the composition B parent glass. Because of the content of R 2 O is bigger than composition A, composition B parent glass has a lower E a , T g and a larger n, E t .

Electron dynamics in films made of transition metal nanograins embedded in SiO[sub 2]: Infrared reflectivity and nanoplasma infrared resonance

KAUST Repository

Massa, Néstor E.

2009-06-04

We report on near normal infrared reflectivityspectra of ∼550 nm thick films made of cosputtered transition metal nanograins and SiO2 in a wide range of metal fractions. Co0.85(SiO2)0.15,with conductivity well above the percolation threshold has a frequency and temperature behavior according to what it is find in conductingmetal oxides. The electron scattering rate displays a unique relaxation time characteristic of single type of carriers experiencing strong electron-phonon interactions. Using small polaron fits we identify those phonons as glass vibrational modes. Ni0.61(SiO2)0.39, with a metal fraction closer to the percolation threshold, undergoes a metal-nonmetal transition at ∼77 K. Here, as it is suggested by the scattering rate nearly quadratic dependence, we broadly identify two relaxation times (two carrier contributions) associated to a Drude mode and a midinfrared overdamped band, respectively. Disorder induced, the midinfrared contribution drives the phase transition by thermal electron localization. Co0.51(SiO2)0.49 has the reflectivity of an insulator with a distinctive band at ∼1450 cm−1 originating in electron promotion, localization, and defect induced polaron formation. Angle dependent oblique reflectivity of globally insulating Co0.38(SiO2)0.62, Fe0.34(SiO2)0.66, and Ni0.28(SiO2)0.72, reveals a remarkable resonance at that band threshold. We understand this as due to the excitation by normal to the film electric fields of defect localized electrons in the metallic nanoparticles. At higher oblique angles, this localized nanoplasma couples to SiO2 longitudinal optical Berreman phonons resulting in band peak softening reminiscent to the phonon behavior undergoing strong electron-phonon interactions. Singular to a globally insulating phase, we believe that this resonance might be a useful tool for tracking metal-insulator phase transitions in inhomogeneous materials.

Mesoporous carbon materials

Science.gov (United States)

Dai, Sheng; Fulvio, Pasquale Fernando; Mayes, Richard T.; Wang, Xiqing; Sun, Xiao-Guang; Guo, Bingkun

2014-09-09

A conductive mesoporous carbon composite comprising conductive carbon nanoparticles contained within a mesoporous carbon matrix, wherein the conductive mesoporous carbon composite possesses at least a portion of mesopores having a pore size of at least 10 nm and up to 50 nm, and wherein the mesopores are either within the mesoporous carbon matrix, or are spacings delineated by surfaces of said conductive carbon nanoparticles when said conductive carbon nanoparticles are fused with each other, or both. Methods for producing the above-described composite, devices incorporating them (e.g., lithium batteries), and methods of using them, are also described.

Excellent Brightness with Shortening Lifetime of Textured Zn2SiO4:Mn2+ Phosphor Films on Quartz Glass

Science.gov (United States)

Park, Jehong; Park, Kwangwon; Lee, Jaebum; Kim, Jongsu; Kim, Seongsin Margaret; Kung, Patrick

2010-04-01

Green-emissive textured Zn2SiO4:Mn2+ phosphor films were fabricated by the thermal diffusion of ZnO:Mn on quartz glass. The Zn2SiO4:Mn2+ phosphor films became textured along several hexagonal directions and their chemical composition was continuously graded at the interface. The decay time of Mn2+ was as short as 4.4 ms, and the optical transition probability of the films defined as the inverse of decay time showed a strong correlation with film texture degree as a function of annealing temperature. The brightest Zn2SiO4:Mn2+ film showed a photoluminescent brightness as high as 65% compared with a commercial Zn2SiO4:Mn2+ phosphor powder screen and a maximum absolute transparency of 70%. These excellent optical properties are explained by the combination of the unique textured structure and continuous grading of the Zn2SiO4:Mn2+ chemical composition at the interface.

Potentiodynamical deposition of nanostructured MnO2 film at the assist of electrodeposited SiO2 as template

International Nuclear Information System (INIS)

Wu, Lian-Kui; Xia, Jie; Hou, Guang-Ya; Cao, Hua-Zhen; Tang, Yi-Ping; Zheng, Guo-Qu

2016-01-01

Highlights: • MnO 2 -SiO 2 composite film is prepared by potentiodynamical deposition. • Hierarchical porous MnO 2 films is obtained after the etching of SiO 2 . • The obtained MnO 2 film electrode exhibit high specific capacitance. - Abstract: We report a novel silica co-electrodeposition route to prepare nanostructured MnO 2 films. Firstly, MnO 2 -SiO 2 composite film was fabricated on a stainless steel substrate by potentiodynamical deposition, i.e. cyclic deposition, and then the SiO 2 template was removed by simple immersion in concentrated alkaline solution, leading to the formation of a porous MnO 2 (po-MnO 2 ) matrix. The structure and morphology of the obtained films were characterized using Fourier transform infrared spectroscopy (FTIR), X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The electrochemical properties of the po-MnO 2 film were evaluated by cyclic voltammetry (CV), galvanostatic charge–discharge (GCD) and electrochemical impedance spectroscopy (EIS). Results showed that this porous MnO 2 derived from the MnO 2 -SiO 2 composite film exhibits good electrochemical performance for potential use as a supercapacitor material.

Magnetic ordered mesoporous Fe3O4/CeO2 composites with synergy of adsorption and Fenton catalysis

Science.gov (United States)

Li, Keyan; Zhao, Yongqin; Song, Chunshan; Guo, Xinwen

2017-12-01

Magnetic Fe3O4/CeO2 composites with highly ordered mesoporous structure and large surface area were synthesized by impregnation-calcination method, and the mesoporous CeO2 as support was synthesized via the hard template approach. The composition, morphology and physicochemical properties of the materials were characterized by XRD, SEM, TEM, XPS, Raman spectra and N2 adsorption/desorption analysis. The mesoporous Fe3O4/CeO2 composite played a dual-function role as both adsorbent and Fenton-like catalyst for removal of organic dye. The methylene blue (MB) removal efficiency of mesoporous Fe3O4/CeO2 was much higher than that of irregular porous Fe3O4/CeO2. The superior adsorption ability of mesoporous materials was attributed to the abundant oxygen vacancies on the surface of CeO2, high surface area and ordered mesoporous channels. The good oxidative degradation resulted from high Ce3+ content and the synergistic effect between Fe and Ce. The mesoporous Fe3O4/CeO2 composite presented low metal leaching (iron 0.22 mg L-1 and cerium 0.63 mg L-1), which could be ascribed to the strong metal-support interactions for dispersion and stabilization of Fe species. In addition, the composite can be easily separated from reaction solution with an external magnetic field due to its magnetic property, which is important to its practical applications.

Preparation of mesoporous Ag-containing TiO{sub 2} heterojunction film and its photocatalytic property

Energy Technology Data Exchange (ETDEWEB)

Wang, Q. Y., E-mail: wangqingyao0532@163.com [Ludong University, School of Chemistry and Materials Science (China); Qiao, J. L. [Jilin Agricultural University, College of Horticulture (China); Cui, X. Y. [Mudanjiang Medical University, School of Public Health (China); Zhong, J. S. [Hangzhou Dianzi University, College of Materials and Environmental Engineering (China); Xu, Y. B.; Zhang, S. H.; Zhang, Q. H.; Chang, P.; Li, M.; Zhang, C.; Gao, S. M., E-mail: gaosm@ustc.edu [Ludong University, School of Chemistry and Materials Science (China)

2015-03-15

Mesoporous Ag/TiO{sub 2} heterojunction films (Ag-MTHF) with enhanced photocatalytic activity were synthesized by a three-step approach including an electrochemical anodization technique followed by successive ionic layer adsorption and reaction (SILAR) and solvothermal methods. The distribution of Ag nanoparticles on the inner structure of the mesoporous TiO{sub 2} film was confirmed by field emission scanning electron (FE-SEM) and transmission electron microscopes (TEM). The formation progress of the novel mesoporous Ag/TiO{sub 2} nanojunction film with Ag average diameter of 17 nm was illuminated. The formed nanojunction between Ag and TiO{sub 2} nanoparticles largely enhanced the photocatalytic degradation of methyl orangey (MO), and the corresponding mechanism was proposed.

Synthesis of metallic nanoparticles in SiO2 matrices

International Nuclear Information System (INIS)

Gutierrez W, C.; Mondragon G, G.; Perez H, R.; Mendoza A, D.

2004-01-01

Metallic nanoparticles was synthesized in SiO 2 matrices by means of a process of two stages. The first one proceeded via sol-gel, incorporating the metallic precursors to the reaction system before the solidification of the matrix. Later on, the samples underwent a thermal treatment in atmosphere of H 2 , carrying out the reduction of the metals that finally formed to the nanoparticles. Then it was detected the presence of smaller nanoparticles than 20 nm, dispersed and with the property of being liberated easily of the matrix, conserving a free surface, chemically reactive and with response to external electromagnetic radiation. The system SiO 2 -Pd showed an important thermoluminescent response. (Author)

Preparation and CO{sub 2} adsorption properties of aminopropyl-functionalized mesoporous silica microspheres

Energy Technology Data Exchange (ETDEWEB)

Araki, S.; Doi, H.; Sano, Y.; Tanaka, S.; Miyake, Y. [Hitachi Zosen Corp., Osaka (Japan). Technical Research Institute

2009-11-15

Aminopropyl-functionalized mesoporous silica microspheres (AF-MSM) were synthesized by a simple one-step modified Stober method. Dodecylamine (DDA) was used as the catalyst for the hydrolysis and condensation of the silica source and as the molecular template to prepare the ordered mesopores. The mesoporous silica surfaces were modified to aminopropyl groups by the co-condensation of tetraethoxysilane (TEOS) with 3-aminopropyltriethoxysilane (APTES), up to a maximum of 20 mol.% APTES content in the silica source. The particle size, Brunauer-Emmet-Teller (BET) specific surface area, and mesoporous regularity decreased with increasing APTES content. It is believed that this result is caused by a decreasing amount of DDA incorporated into AF-MSM with increasing APTES content. It was also confirmed that the spherical shape and the mesostructure were maintained even if 20 mol.% of APTES was added to the silica source. Moreover, AF-MSM was applied to the CO{sub 2} adsorbent. The breakthrough time of the CO{sub 2} and CO{sub 2} adsorption capacities increased with increasing APTES content. The adsorption capacity of CO{sub 2} for AF-MSM, prepared at 20 mol.% APTES, was 0.54 mmol g{sup -1}. Carbon dioxide adsorbed onto AF-MSM was completely desorbed by heating in a N{sub 2} purge at 423 K for 30 min.

Structural aspects of B2O3-substituted (PbO)0.5(SiO2)0.5 glasses

International Nuclear Information System (INIS)

Sudarsan, V.; Kulshreshtha, S.K.; Shrikhande, V.K.; Kothiyal, G.P.

2002-01-01

Lead borosilicate glasses having general formulae (PbO) 0.5-x (SiO 2 ) 0.5 (B 2 O 3 ) x with 0.0≤x≤0.4 and (PbO) 0.5 (SiO 2 ) 0.5-y (B 2 O 3 ) y with 0.0≤y≤0.5 have been prepared by a conventional melt-quench method and characterized by 29 Si, 11 B magic angle spinning (MAS) NMR techniques and infrared spectroscopy, as regards their structural features. From 29 Si NMR results, it has been inferred that with increasing concentration of boron oxide, (PbO) 0.5-x (SiO 2 ) 0.5 (B 2 O 3 )x glasses exhibit a systematic increase in the number of Q 4 structural units of Si at the expense of Q 2 structural units, along with the formation of Si-O-B linkages. On the other hand, for (PbO) 0.5 (SiO 2 ) 0.5-y (B 2 O 3 ) y glasses, there is no direct interaction between SiO 2 and B 2 O 3 in the glass network, as revealed by the 29 Si MAS NMR studies. Boron exists in both trigonal and tetrahedral configurations for these two series of glasses and for the (PbO) 0.5 (SiO 2 ) 0.5-y (B 2 O 3 ) y series of glasses; the relative concentration of these two structural units remains almost constant with increasing B 2 O 3 concentration. In contrast, for (PbO) 0.5-x (SiO 2 ) 0.5 (B 2 O 3 ) x glasses, there is a slight increase in the number of BO 3 structural units above x = 0.2, as there is a competition between SiO 2 and B 2 O 3 for interaction with Pb 2+ , thereby leading to the formation of BO 3 structural units. For both series of glasses, the thermal expansion coefficient is found to decrease with increasing B 2 O 3 concentration, the effect being more pronounced for the (PbO) 0.5-x (SiO 2 ) 0.5 (B 2 O 3 ) x series of glasses due to the increased concentration of Q 4 structural units of silicon and better cross-linking as a result of the formation of Si-O-B-type linkages. (author)

Structurally stabilized mesoporous TiO2 nanofibres for efficient dye-sensitized solar cells

Directory of Open Access Journals (Sweden)

Fargol Hasani Bijarbooneh

2013-09-01

Full Text Available One-dimensional (1D TiO2 nanostructures are very desirable for providing fascinating properties and features, such as high electron mobility, quantum confinement effects, and high specific surface area. Herein, 1D mesoporous TiO2 nanofibres were prepared using the electrospinning method to verify their potential for use as the photoelectrode of dye-sensitized solar cells (DSSCs. The 1D mesoporous nanofibres, 300 nm in diameter and 10-20 μm in length, were aggregated from anatase nanoparticles 20-30 nm in size. The employment of these novel 1D mesoporous nanofibres significantly improved dye loading and light scattering of the DSSC photoanode, and resulted in conversion cell efficiency of 8.14%, corresponding to an ∼35% enhancement over the Degussa P25 reference photoanode.

Formation of radiative centers in SiO2 by tin high-dose implantation

International Nuclear Information System (INIS)

Komarov, F.F.; Parkhomenko, I.N.; Vlasukova, L.A.; Mil'chanin, O.V.; Mokhovikov, M.A.; Wendler, E.; Wesch, W.

2013-01-01

The structural transformations in SiO 2 layers implanted with high fluence of Sn ions have been investigated. It has been found that post-implantation annealing results in the β-Sn precipitation as well as the formation of SnO 2 -enriched regions in SiO 2 :Sn matrix. The intensive emission in the range of photon energies 1.5 – 3.5 eV is registered for the implanted and annealed samples. We attribute it to the oxygen deficiency centers created in the SiO 2 :Sn matrix and at the 'nanocluster/SiO 2 ' interfaces. (authors)

Structure and crystallization of SiO2 and B2O3 doped lithium disilicate glasses from theory and experiment.

Science.gov (United States)

Erlebach, Andreas; Thieme, Katrin; Sierka, Marek; Rüssel, Christian

2017-09-27

Solid solutions of SiO 2 and B 2 O 3 in Li 2 O·2SiO 2 are synthesized and characterized for the first time. Their structure and crystallization mechanisms are investigated employing a combination of simulations at the density functional theory level and experiments on the crystallization of SiO 2 and B 2 O 3 doped lithium disilicate glasses. The remarkable agreement of calculated and experimentally determined cell parameters reveals the preferential, kinetically controlled incorporation of [SiO 4 ] and [BO 4 ] at the Li + lattice sites of the Li 2 O·2SiO 2 crystal structure. While the addition of SiO 2 increases the glass viscosity resulting in lower crystal growth velocities, glasses containing B 2 O 3 show a reduction of both viscosities and crystal growth velocities. These observations could be rationalized by a change of the chemical composition of the glass matrix surrounding the precipitated crystal phase during the course of crystallization, which leads to a deceleration of the attachment of building units required for further crystal growth at the liquid-crystal interface.

High efficiency nanocomposite sorbents for CO2 capture based on amine-functionalized mesoporous capsules

KAUST Repository

Qi, Genggeng; Wang, Yanbing; Estevez, Luis; Duan, Xiaonan; Anako, Nkechi; Park, Ah-Hyung Alissa; Li, Wen; Jones, Christopher W.; Giannelis, Emmanuel P.

2011-01-01

A novel high efficiency nanocomposite sorbent for CO2 capture has been developed based on oligomeric amine (polyethylenimine, PEI, and tetraethylenepentamine, TEPA) functionalized mesoporous silica capsules. The newly synthesized sorbents exhibit extraordinary capture capacity up to 7.9 mmol g-1 under simulated flue gas conditions (pre-humidified 10% CO 2). The CO2 capture kinetics were found to be fast and reached 90% of the total capacities within the first few minutes. The effects of the mesoporous capsule features such as particle size and shell thickness on CO2 capture capacity were investigated. Larger particle size, higher interior void volume and thinner mesoporous shell thickness all improved the CO2 capacity of the sorbents. PEI impregnated sorbents showed good reversibility and stability during cyclic adsorption-regeneration tests (50 cycles). © 2011 The Royal Society of Chemistry.

Beyond sixfold coordinated Si in SiO2 glass at ultrahigh pressures.

Science.gov (United States)

Prescher, Clemens; Prakapenka, Vitali B; Stefanski, Johannes; Jahn, Sandro; Skinner, Lawrie B; Wang, Yanbin

2017-09-19

We investigated the structure of SiO 2 glass up to 172 GPa using high-energy X-ray diffraction. The combination of a multichannel collimator with diamond anvil cells enabled the measurement of structural changes in silica glass with total X-ray diffraction to previously unachievable pressures. We show that SiO 2 first undergoes a change in Si-O coordination number from fourfold to sixfold between 15 and 50 GPa, in agreement with previous investigations. Above 50 GPa, the estimated coordination number continuously increases from 6 to 6.8 at 172 GPa. Si-O bond length shows first an increase due to the fourfold to sixfold coordination change and then a smaller linear decrease up to 172 GPa. We reconcile the changes in relation to the oxygen-packing fraction, showing that oxygen packing decreases at ultrahigh pressures to accommodate the higher than sixfold Si-O coordination. These results give experimental insight into the structural changes of silicate glasses as analogue materials for silicate melts at ultrahigh pressures.

Cotton fabric finishing with TiO2/SiO2 composite hydrosol based on ionic cross-linking method

International Nuclear Information System (INIS)

Xu, Z.J.; Tian, Y.L.; Liu, H.L.; Du, Z.Q.

2015-01-01

Highlights: • We studied the cotton finishing with TiO 2 /SiO 2 based on ionic cross-linking method. • The samples treated with CHTAC had lower value of whiteness. • The samples treated with BTCA achieved higher crease recovery angle and lower tensile strength. • The ionic cross-linking treatment (CHTAC + BTCA + TiO 2 /SiO 2 ) was better than with TiO 2 /SiO 2 sol alone. - Abstract: Cotton fabric was successfully modified by 3-chloro-2-hydroxypropyl trimethyl ammonium chloride (CHTAC), 1,2,3,4-butanetetracarboxylic acid (BTCA) and TiO 2 /SiO 2 sol. Self-cleaning characteristic was investigated using a Color Measuring and Matching System with 6 h sunlight irradiation. And the stability of TiO 2 /SiO 2 coatings was explored by measuring the washing fastness and wrinkle resistance of treated cotton samples. In addition, whiteness index, crease recovery angle and tensile strength retention (%) of treated samples were evaluated. Moreover, the morphology, structure change and crystallinity of samples were observed by scanning electron microscopy (SEM), Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD), respectively. The results revealed that the samples treated with CHTAC had lower value of whiteness index as compared with original cotton fabric. It was also found that samples treated with BTCA achieved higher crease recovery angle and lower tensile strength. Moreover, the treatment of CHTAC and BTCA had adverse effect on the crystallinity of cotton samples, as treated samples had lower crystallinity in comparison with raw cotton fabrics. Nevertheless, the stability of self-cleaning coatings was better for samples treated with ionic cross-linking treatment (CHTAC + BTCA + TiO 2 /SiO 2 ) than samples treated with TiO 2 /SiO 2 sol alone. Furthermore, compared with original samples the UV-blocking property of ionic cross-linking treated samples was obviously enhanced

Urinary matrix metalloproteinases reflect renal damage in anti-neutrophil cytoplasm autoantibody-associated vasculitis

NARCIS (Netherlands)

Sanders, J.S.F.; Huitema, M.G.; Hanemaaijer, R.; Goor, H. van; Kallenberg, C.G.M.; Stegeman, C.A.

2007-01-01

Renal expression of MMP-2, -9, and tissue inhibitor of MMP-1 (TIMP-1) correlates with histological disease activity in anti-neutrophil cytoplasm autoantibody (ANCA)-associated vasculitis (AAV). We studied whether urinary and plasma levels of MMP-2, -9, and TIMP-1 reflect renal expression of these

Ca2 Al2 SiO7 :Ce3+ phosphors for mechanoluminescence dosimetry.

Science.gov (United States)

Tiwari, Geetanjali; Brahme, Nameeta; Sharma, Ravi; Bisen, D P; Sao, Sanjay Kumar; Sahu, Ishwar Prasad

2016-12-01

A series of Ce 3+ ion single-doped Ca 2 Al 2 SiO 7 phosphors was synthesized by a combustion-assisted method at an initiating temperature of 600 °C. The samples were annealed at 1100 °C for 3 h and their X-ray diffraction patterns confirmed a tetragonal structure. The phase structure, particle size, surface morphology and elemental analysis were analyzed using X-ray diffraction (XRD), transmission electron microscope (TEM), scanning electron microscopy (SEM) and energy dispersive X-ray (EDX) spectroscopy techniques. Thermoluminescence (TL) intensity increased with increase in ultraviolet (UV) light exposure time up to 15 min. With further increase in the UV irradiation time the TL intensity decreases. The increase in TL intensity indicates that trap concentration increased with UV exposure time. A broad peak at 121 °C suggested the existence of a trapping level. The peak of mechanoluminescence (ML) intensity versus time curve increased linearly with increasing impact velocity of the moving piston. Mechanoluminescence intensity increased with increase in UV irradiation time up to 15 min. Under UV-irradiation excitation, the TL and ML emission spectra of Ca 2 Al 2 SiO 7 :Ce 3+ phosphor showed the characteristic emission of Ce 3+ peaking at 400 nm (UV-violet) and originating from the Ce 3+ transitions of 5d-4f ( 2 F 5/2 and 2 F 7/2 ). The photoluminescence (PL) emission spectra for Ca 2 Al 2 SiO 7 :Ce 3+ were similar to the ML/TL emission spectra. The mechanism of ML excitation and the suitability of the Ca 2 Al 2 SiO 7 :Ce 3+ phosphor for radiation dosimetry are discussed. Copyright © 2016 John Wiley & Sons, Ltd. Copyright © 2016 John Wiley & Sons, Ltd.

Preparation of mesoporous MnO2/C catalyst for n-hexyl acetate synthesis

International Nuclear Information System (INIS)

Yang Zeheng; Pan Yanmei; Mei Zhousheng; Zhang Weixin

2012-01-01

A mesoporous MnO 2 /C composite was prepared by impregnating self-made porous carbon spheres with manganese nitrate aqueous solution and subsequently reacting with KMnO 4 aqueous solution. It was characterized with X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM), field emission scanning electron microscopy (FESEM), the Brunauer-Emmett-Teller (BET) surface area and the Barrett-Joyner-Halenda (BJH) pore size distribution. The as-prepared mesoporous MnO 2 /C composite was used as catalyst for the synthesis of n-hexyl acetate, and the effects of MnO 2 loading and esterification reaction parameters on the esterification rate were investigated. The results prove that MnO 2 loading has a significant effect on the catalytic activity and that the mesoporous MnO 2 /C composite exhibits high catalytic activity with an esterification rate of 96.42% under the conditions below: MnO 2 loading (73.09 wt%), catalyst dosage (0.1% in total weight), acetic acid/n-hexanol molar ratio (2:1), reaction temperature (130 °C) and reaction time (5 h).

Raman and optical absorption spectroscopic investigation of Yb-Er codoped phosphate glasses containing SiO2

Institute of Scientific and Technical Information of China (English)

Youkuo Chen; Lei Wen; Lili Hu; Wei Chen; Y. Guyot; G. Boulon

2009-01-01

Yb-Er codoped Na2O-Al2O3-P2Os-xSiO2 glasses containing 0 鈥? 20 mol% SiO2 were prepared successfully. The addition of SiO2 to the phosphate glass not only lengthens the bond between P5+ and non-bridging oxygen but also reduces the number of P=O bond. In contrast with silicate glass in which there is only four-fold coordinated Si4+, most probably there coexist [SiO4] tetrahedron and [SiO6] octahedron in our glasses. Within the range of 0 鈥? 20 mol% SiO2 addition, the stimulated emission cross-section of Er3+ ion only decreases no more than 10%. The Judd-Ofelt intensity parameters of Er3+, 惟.2 does not change greatly, but 惟74 and 惟6 decrease obviously with increasing SiO2 addition, because the bond between Er + and O2- is more strongly covalently bonded.

SiO2 stabilized Pt/C cathode catalyst for proton exchange membrane fuel cells

International Nuclear Information System (INIS)

Zhu Tong; Du Chunyu; Liu Chuntao; Yin Geping; Shi Pengfei

2011-01-01

This paper describes the preparation of SiO 2 stabilized Pt/C catalyst (SiO 2 /Pt/C) by the hydrolysis of alkoxysilane, and examines the possibility that the SiO 2 /Pt/C is used as a durable cathode catalyst for proton exchange membrane fuel cells (PEMFCs). TEM and XRD results revealed that the hydrolysis of alkoxysilane did not significantly change the morphology and crystalline structure of Pt particles. The SiO 2 /Pt/C catalyst exhibited higher durability than the Pt/C one, due to the facts that the silica layers covered were beneficial for reducing the Pt aggregation and dissolution as well as increasing the corrosion resistance of supports, although the benefit of silica covering was lower than the case of Pt/CNT catalyst. Also, it was observed that the activity of the SiO 2 /Pt/C catalyst for the oxygen reduction reaction was somewhat reduced compared to the Pt/C one after the silica covering. This reduction was partially due to the low oxygen kinetics as revealed by the rotating-disk-electrode measurement. Silica covering by hydrolysis of only 3-aminopropyl trimethoxysilane is able to achieve a good balance between the durability and activity, leading to SiO 2 /Pt/C as a promising cathode catalyst for PEMFCs.

Characterization of the implantation damage in SiO2 with x-ray photoelectron spectroscopy

International Nuclear Information System (INIS)

Ajioka, T.; Ushio, S.

1986-01-01

X-ray photoelectron spectroscopy (XPS) has been applied to characterize the damage introduced into SiO 2 by ion implantation. By measuring the peak width of Si/sub 2p/ from SiO 2 which corresponds to perturbation of the SiO 2 network, good depth profiles of the damage have been obtained for implanted samples and subsequently annealed samples. The results show that the damage distributed more widely than that calculated from energy deposition and that the perturbation of the network is caused not only by radiation damage but also by the existence of impurities in the network. It has been found that the XPS method is effective to understand the atomic structure, and thus, electrical properties of SiO 2

Adsorption of uranyl in SiO2 porous glass

International Nuclear Information System (INIS)

Benedetto, F. E.; Prado, M. O.

2013-01-01

Vitreous SiO 2 porous matrices can be used in many applications involving the uptake of chemical species on its solid surface. In this work, vitreous silica sponges were prepared from a sodium borosilicate glass manufactured in our laboratory. The product obtained was then separated into phases with subsequent leaching of the soluble phase rich in B and Na. The resulting porous matrices have a specific surface of 35 m2/gr. Adsorption of uranyl ions onto the SiO 2 porous surface was studied to evaluate the use of this material as a filter for treatment of uranium containing water. The effects of contact time, adsorbent mass and equilibrium concentration of solution were studied. The porous adsorbent exhibits a pseudo-second-order kinetic behavior. The sponges with adsorbed uranium were thermally sealed as a way of U immobilization. Retention of uranium was confirmed during the matrix sealing by TGA. Uranium concentration before and after adsorption tests were made by means of ICP-OES. For uranium concentration of 800 ppm, 72 hours contact time and pH of 3.5, the amount of uranium adsorbed was 21.06 ± 0.02 mg U per gram of vitreous porous SiO 2 . (author)

Synthesis, characterizations and photocatalytic studies of mesoporous titania prepared by using four plant skins as templates

Energy Technology Data Exchange (ETDEWEB)

Miao Yingchun [Department of Applied Chemistry, Key Laboratory of Medicinal Chemistry for Natural Resource, Ministry of Education, Yunnan University, Kunming 650091 (China); Faculty of Chemical and Life Sciences, Qujing Normal University, Qujing 655000 (China); Zhai Zhongbiao [Department of Applied Chemistry, Key Laboratory of Medicinal Chemistry for Natural Resource, Ministry of Education, Yunnan University, Kunming 650091 (China); Kunming Metallurgy Research Institute, Kunming 650031 (China); He Jiao; Li Bin; Li Junjie [Department of Applied Chemistry, Key Laboratory of Medicinal Chemistry for Natural Resource, Ministry of Education, Yunnan University, Kunming 650091 (China); Wang Jiaqiang, E-mail: jqwang@ynu.edu.cn [Department of Applied Chemistry, Key Laboratory of Medicinal Chemistry for Natural Resource, Ministry of Education, Yunnan University, Kunming 650091 (China)

2010-07-20

Anatase mesoporous titania with novel morphologies were synthesized by using the skins of tomatoes, bulb onions, grapes, and garlic bulbs, respectively, as templates and used for the photodegradation of Gentian violet, methyl violet, xylenol orange, and Rhodamine B under UV light. The samples were characterized by a combination of various physicochemical techniques, such as X-ray diffraction, SEM, HRTEM, N{sub 2} adsorption/desorption, diffuse reflectance UV-Vis, and FT-IR. It was found that all of the synthesized mesoporous titania samples exhibited similar morphologies to those of the original templates. The photoactivity of P25 TiO{sub 2} for the four dyes is nearly the same while the mesoporous titania samples synthesized by using the four skins as templates exhibited varied photoactivities for the four dyes.

Effects of four step sintering on Y2O3: SiO2 nanocomposite

International Nuclear Information System (INIS)

Ahlawat, Rachna

2015-01-01

Need for high performance materials for advanced applications have led to the development of new concepts in materials design processing and their fabrication. The development of nanocrystalline materials with improved and novel properties is an important turning point in materials research. In present work, we report synthesis and structural characterization of Y 2 O 3 : SiO 2 nanocomposite. Sol-gel technique is being used to prepare-Y 2 O 3 SiO 2 nanocomposite due to its effectiveness in preparing samples with good mixing of starting materials and at relatively low reaction temperature. We have used Y(NO 3 ) 3 .4H 2 O and TEOS as precursors and followed usual approach of sol-gel technique, the final product of Y 2 O 3 : SiO 2 nanocomposite is obtained in the form of powder. The powder samples were sintered at different temperature for different time durations in programmable muffle furnace. The samples were characterized by complementary techniques as X-Ray Diffraction (XRD), Fourier Transforms Infrared Spectroscopy (FTIR) and Transmission Electron Microscopy (TEM). (author)

Gyroidal mesoporous carbon materials and methods thereof

Energy Technology Data Exchange (ETDEWEB)

Wiesner, Ulrich B.; Werner, Joerg G.

2017-07-25

The present invention relates to, inter alia, gyroidal mesoporous carbon materials and methods of use and manufacture thereof. In one embodiment, the present invention relates to a mesoporous carbon composition comprising a gyroidal mesoporous carbon having an ordered gyroidal structure and mesopores having a pore size of greater than 2 nanometers (nm) in diameter, and more particularly greater than 11 nm in diameter.

Functionalized mesoporous silica nanoparticles for oral delivery of budesonide

Energy Technology Data Exchange (ETDEWEB)

Yoncheva, K., E-mail: krassi.yoncheva@gmail.com [Department of Pharmaceutical Technology, Faculty of Pharmacy, Medical University of Sofia, 2 Dunav Str., 1000 Sofia (Bulgaria); Popova, M. [Institute of Organic Chemistry with Centre of Phytochemistry, Bulgarian Academy of Sciences, Sofia (Bulgaria); Szegedi, A.; Mihaly, J. [Institute of Nanochemistry and Catalysis, Chemical Research Center, Hungarian Academy of Sciences, Pusztaszeri út. 59-67, 1025 Budapest (Hungary); Tzankov, B.; Lambov, N.; Konstantinov, S.; Tzankova, V. [Department of Pharmaceutical Technology, Faculty of Pharmacy, Medical University of Sofia, 2 Dunav Str., 1000 Sofia (Bulgaria); Pessina, F.; Valoti, M. [Dipartimento di Scienze della Vita, Universita di Siena, via Aldo Moro 2, Siena (Italy)

2014-03-15

Non-functionalized and amino-functionalized mesoporous silica nanoparticle were loaded with anti-inflammatory drug budesonide and additionally post-coated with bioadhesive polymer (carbopol). TEM images showed spherical shape of the nanoparticles and slightly higher polydispersity after coating with carbopol. Nitrogen physisorption and thermogravimetic analysis revealed that more efficient loading and incorporation into the pores of nanoparticles was achieved with the amino-functionalized silica carrier. Infrared spectra indicated that the post-coating of these nanoparticles with carbopol led to the formation of bond between amino groups of the functionalized carrier and carboxyl groups of carbopol. The combination of amino-functionalization of the carrier with the post-coating of the nanoparticles sustained budesonide release. Further, an in vitro model of inflammatory bowel disease showed that the cytoprotective effect of budesonide loaded in the post-coated silica nanoparticles on damaged HT-29 cells was more pronounced compared to the cytoprotection obtained with pure budesonide. -- Graphical abstract: Silica mesoporous MCM-41 particles were amino-functionalized, loaded with budesonide and post-coated with bioadhesive polymer (carbopol) in order to achieve prolonged residence of anti-inflammatory drug in GIT. Highlights: • Higher drug loading in amino-functionalized mesoporous silica. • Amino-functionalization and post-coating of the nanoparticles sustained drug release. • Achievement of higher cytoprotective effect with drug loaded into the nanoparticles.

The electrorheological properties of nano-sized SiO2 particle materials doped with rare earths

International Nuclear Information System (INIS)

Liu Yang; Liao Fuhui; Li Junran; Zhang Shaohua; Chen Shumei; Wei Chenguan; Gao Song

2006-01-01

Electrorheological (ER) materials of pure SiO 2 and SiO 2 doped with rare earths (RE = Ce, Gd, Y) (non-metallic glasses (silicates)) were prepared using Na 2 SiO 3 and RECl 3 as starting materials. The electrorheological properties are not enhanced by all rare earth additions. The material doped with Ce exhibits the best ER performance

Preparation of mesoporous zirconia microspheres as inert matrix

Energy Technology Data Exchange (ETDEWEB)

Guo, Ting [State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China); Wang, Chen; Lv, Jinlong [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China); Liang, Tongxiang, E-mail: txliang@tsinghua.edu.cn [State Key Laboratory of New Ceramics and Fine Processing, Institute of Nuclear and New Energy Technology, Tsinghua University, Beijing, 100084 (China)

2016-12-01

Mesoporous zirconia microspheres, with a diameter of 900 μm, were prepared as an inert accelerator driven system (ADS) transmutation element matrix by the sol-gel method. The purpose of mesopores is to improve the adsorption capacity of inert matrix fuel (IMF) for minor actinides. The study indicated that the mesoporous zirconia performance was improved after the microspheres were hydrothermally treated at 150 °C, the specific surface area increased from 28.29 m{sup 2}/g to 61.28 m{sup 2}/g, and hydrothermal treatment avoided the cracking of the microspheres. Pre-decomposition of the organics during the hydrothermal process stabilized the mesoporous structure. The average pore diameter of mesoporous microsphere was 14.3 nm. - Highlights: • Mesoporous zirconia microspheres with a diameter of 900 μm were prepared as ADS transmutation element inert matrix. • The mesoporous performance was improved after the microspheres were hydrothermally treated at 150 °C. • The specific surface area increased from 28.29 m{sup 2}/g to 61.28 m{sup 2}/g. • The hydrothermal treatment could avoid the cracking of the microspheres. • The specific surface area of mesoporous microsphere was 61.28 m{sup 2}/g and the average pore diameter was 14.3 nm.

A facile approach to fabricate Au nanoparticles loaded SiO2 microspheres for catalytic reduction of 4-nitrophenol

International Nuclear Information System (INIS)

Tang, Mingyi; Huang, Guanbo; Li, Xianxian; Pang, Xiaobo; Qiu, Haixia

2015-01-01

Hydrophilic and biocompatible macromolecules were used to improve and simplify the process for the fabrication of core/shell SiO 2 @Au composite particles. The influence of polymers on the morphology of SiO 2 @Au particles with different size of SiO 2 cores was analyzed by transmission electron microscopy and scanning electron microscopy. The optical property of the SiO 2 @Au particles was studied with UV–Vis spectroscopy. The results indicate that the structure and composition of macromolecules affect the morphology of Au layers on SiO 2 microspheres. The SiO 2 @Au particles prepared in the presence of polyvinyl alcohol (PVA) or polyvinylpyrrolidone (PVP) have thin and complete Au nanoshells owing to their inducing act in preferential growth of Au nanoparticles along the surface of SiO 2 microspheres. SiO 2 @Au particles can be also prepared from SiO 2 microspheres modified with 3-aminopropyltrimethoxysilane in the presence of PVA or PVP. This offers a simple way to fabricate a Au layer on SiO 2 or other microspheres. The SiO 2 @Au particles demonstrated high catalytic activity in the reduction of 4-nitrophenol. - Highlights: • Facile direct deposition method for Au nanoparticles on silica microspheres. • Influence of different types of macromolecule on the formation of Au shell. • High catalytic performance of Au nanoparticles on silica microspheres

Electronic states of SiO2-MxOy (MxOy=P205, TiO2 and ZrO2) glasses

Energy Technology Data Exchange (ETDEWEB)

Kowada, Y [Hyogo Univ. of Teacher Education, Hyogo (Japan); Adachi, H [Kyoto Univ. (Japan). Faculty of Engineering; Minami, T [Univ. of Osaka Prefecture, Osaka (Japan). Faculty of Engineering

1993-12-01

Using the sol-gel method the surface of metal and glass substrates can be modified. For example, stainless steel sheets coated with the SiO2-ZrO2 glass films have higher resistance to corrosion and oxidation. The coating films contain high concentration of alkali ions diffusing from the glass substrates. It suggests that the sodium ions are trapped strongly within the coating films and are blocked to further diffuse to the surface. This behavior must be associated with the chemical bonding around the sodium ions in the SiO2-TiO2 and SiO2-ZrO2 films. For better understanding of the chemical bonding in the glasses, the electronic states of the SiO2-MxOy glasses were calculated by means of the DV-Xa cluster method. In this paper, the calculation method is explained, the results are discussed and the conclusion is stated. 17 refs., 6 figs.

Luminescence characteristics of Mg2SiO4:Nd

International Nuclear Information System (INIS)

Indira, P.; Subrahmanyam, R.V.; Murthy, K.V.R.

2011-01-01

Thermoluminescence (TL) properties of Magnesium Ortho silicate (2:1) Mg 2 SiO 4 doped with various concentrations of rare earth (Nd) have been studied. The phosphor material were prepared using standard solid state reaction technique and heated specimens at 1100 ± 20 deg C for two hours. 4% Ammonium chloride was used as flux. The received material was grinded in an agate mortar and pestle. The TL exhibited by the Mg 2 SiO 4 with varying concentration of Nd is interesting in nature. It is interesting to note but as the concentration of Nd increases the peak around 125 deg C TL peak intensity increases. But the hump around 200 deg C resolved as TL peak at 253 deg C with high intensity. (author)

Composite hydrogel based on surface modified mesoporous silica and poly[(2-acryloyloxy)ethyl trimethylammonium chloride

International Nuclear Information System (INIS)

Torres, Cecilia C.; Urbano, Bruno F.; Campos, Cristian H.; Rivas, Bernabé L.; Reyes, Patricio

2015-01-01

This work focused on the synthesis, characterization and water absorbency of a composite hydrogel based on poly[(2-acryloyloxy)ethyl trimethylammonium chloride] and mesoporous silica, MCM-41. The MCM-41 was synthesized and later surface functionalized with triethoxyvinylsilane (VTES) and 3-trimethoxysilylpropylmethacrylate (TMSPM) by a post-grafting procedure. The composite hydrogels were obtained by in-situ polymerization using a mixture of monomer, crosslinker and initiator in the presence of functionalized MCM-41. Diverse characterization techniques were used at the different stages of synthesis, namely, FT-IR, TEM, SEM, DRX, 29 Si and 13 C solid state NMR, and N 2 adsorption isotherms at 77 K. Finally, the water uptake performance of the composites was tested as a function of time, mesoporous silica loading and coupling agent used at the functionalization. The composites using non-functionalized MCM-41 reached the highest water uptake, whereas those composite with MCM-41 TMSPM exhibited the lowest sorption. - Highlights: • Hydrophilic crosslinked polymer-mesoporous silica was obtained. • Mesoporous silica MCM-41 was synthesized and functionalized with organosilane. • Functionalization of MCM-41 affects the water uptake of composite. • Mesoporous silica is covalently bound to the polymer acting as crosslinked point

Visible Light Excited Catalysis and Reusability Performances of TiO2@Pr:Y2SiO5 Upconversion Materials

Directory of Open Access Journals (Sweden)

Yan Jiao

2017-01-01

Full Text Available To get high efficiency photodegradation on pollutants under visible light, Pr(III doped Y2SiO5 upconversion materials and anatase TiO2 nanofilm coated Pr:Y2SiO5 composite have been prepared by using a sol-gel method. XRD and SEM test results indicated that TiO2 nanofilm was well coated on Pr:Y2SiO5 to form TiO2@Pr:Y2SiO5 composite particles with the sizes of 0.5–1.0 μm. To avoid secondary pollution resulting from incomplete recovery of catalyst particles, TiO2@Pr:Y2SiO5 was loaded on the glass fiber filters by using a dip-coating method. It is found that the catalyst particles were embedded into the carrier firmly, even after having been reused for 6 times. The luminescence intensities of TiO2@Pr:Y2SiO5 were getting down sharply with the coating contents of TiO2 increased, which was attributed to the adsorption of the luminescence by the TiO2 film in situ. As a result, TiO2@Pr:Y2SiO5 with 4% TiO2, which presented lowest luminescence intensity, showed the highest efficiency on the photodegradation of nitrobenzene wastewater. The catalysts loaded on glass fiber filters showed excellent reusability on the photodegradation of nitrobenzene and presented a photodegradation rate of 95% at the first time and up to 75.9% even after 6 times of reusing by the treatment time of 12 h.

Tunable graphene doping by modulating the nanopore geometry on a SiO2/Si substrate

KAUST Repository

Lim, Namsoo

2018-02-28

A tunable graphene doping method utilizing a SiO2/Si substrate with nanopores (NP) was introduced. Laser interference lithography (LIL) using a He–Cd laser (λ = 325 nm) was used to prepare pore size- and pitch-controllable NP SiO2/Si substrates. Then, bottom-contact graphene field effect transistors (G-FETs) were fabricated on the NP SiO2/Si substrate to measure the transfer curves. The graphene transferred onto the NP SiO2/Si substrate showed relatively n-doped behavior compared to the graphene transferred onto a flat SiO2/Si substrate, as evidenced by the blue-shift of the 2D peak position (∼2700 cm−1) in the Raman spectra due to contact doping. As the porosity increased within the substrate, the Dirac voltage shifted to a more positive or negative value, depending on the initial doping type (p- or n-type, respectively) of the contact doping. The Dirac voltage shifts with porosity were ascribed mainly to the compensation for the reduced capacitance owing to the SiO2–air hetero-structured dielectric layer within the periodically aligned nanopores capped by the suspended graphene (electrostatic doping). The hysteresis (Dirac voltage difference during the forward and backward scans) was reduced when utilizing an NP SiO2/Si substrate with smaller pores and/or a low porosity because fewer H2O or O2 molecules could be trapped inside the smaller pores.

Fourier transform infrared spectroscopic study of gamma irradiated SiO2 nanoparticles

Science.gov (United States)

Huseynov, Elchin; Garibov, Adil; Mehdiyeva, Ravan; Huseynova, Efsane

2018-03-01

In the present work, nano SiO2 particles are investigated before and after gamma irradiation (25, 50, 75, 100 and 200 kGy) using Fourier transform infrared (FTIR) spectroscopy method for the wavenumber between 400-4000 cm-1. It is found that as a result of spectroscopic analysis, five new peaks have appeared after gamma radiation. Two of new obtained peaks (which are located at 687 cm-1 and 2357 cm-1 of wavenumber) were formed as a result of gamma radiation interaction with Si-O bonds. Another three new peaks (peaks appropriate to 941, 2052 and 2357 cm-1 values of wavenumber) appear as a result of interaction of water with nano SiO2 particles after gamma irradiation. It has been defined as asymmetrical bending vibration, symmetrical bending vibration, symmetrical stretching vibration and asymmetrical stretching vibration of Si-O bonds appropriate to peaks.

Effect of Ni/Al2O3-SiO2 and Ni/Al2O3-SiO2 with K2O Promoter Catalysts on H2, CO and CH4 Concentration by CO2 Gasification of Rosa Multiflora Biomass

Directory of Open Access Journals (Sweden)

Tursunov Obid

2017-11-01

Full Text Available The thermal behaviour of the Rosa mutiflora biomass by thermogravimetric analysis was studied at heating rate 3 K min−1 from ambient temperature to 950 °C. TGA tests were performed in high purity carbon dioxide (99 998% with a flow rate 200 ml/min and 100 mg of sample, milled and sieved to a particle size below 250 µm. Moreover, yields of gasification products such as hydrogen (H2, carbon monoxide (CO and methane (CH4 were determined based on the thermovolumetric measurements of catalytic (Ni/Al2O3-SiO2 and Ni/Al2O3-SiO2 with K2O promoter catalysts and non-catalytic gasification of the Rosa multiflora biomass. Additionally, carbon conversion degrees are presented. Calculations were made of the kinetic parameters of carbon monoxide and hydrogen formation reaction in the catalytic and non-catalytic CO2 gasification processes. A high temperature of 950 °C along with Ni/Al2O3-SiO2and Ni/Al2O3-SiO2 with K2O promoter catalysts resulted in a higher conversion of Rosa multiflora biomass into gaseous yield production with greatly increasing of H2 and CO contents. Consequently, H2 and CO are the key factors to produce renewable energy and bio-gases (synthesis gas. The parameters obtained during the experimental examinations enable a tentative assessment of plant biomasses for the process of large-scale gasification in industrial sectors.

Hazards of TiO2 and amorphous SiO2 nanoparticles

NARCIS (Netherlands)

Reijnders, L.; Kahn, H.A.; Arif, I.A.

2012-01-01

TiO2 and amorphous SiO2 nanoparticles have been described as ‘safe’, ‘non-toxic’ and ‘environment friendly’ in scientific literature. However, though toxicity data are far from complete, there is evidence that these nanoparticles are hazardous. TiO2 nanoparticles have been found hazardous to humans

Silicon electrodeposition from chloride-fluoride melts containing K2SiF6 and SiO2

Directory of Open Access Journals (Sweden)

Zhuk Sergey I.

2017-01-01

Full Text Available Silicon electrodeposition on glassy carbon from the KF-KCl-K2SiF6, KF-KCl-K2SiF6-KOH and KF-KCl-K2SiF6-SiO2 melts was studied by the cyclic voltammetry. Тhe electroreduction of Si(IV to metallic Si was observed as a single 4-electron wave under all considered conditions. The reactions of cathode reduction of silicon from fluoride and oxyfluoride complexes were suggested. It was shown that the process can be controlled by the preliminary transformation of SiO44- to SiF62- and SiOxFyz-. The influence of the current density on structure and morphology of silicon deposits obtained during galvanostatic electrolysis of the KF-KCl-K2SiF6-SiO2 melt was studied.

Synthesis of 2D Nitrogen-Doped Mesoporous Carbon Catalyst for Oxygen Reduction Reaction

Directory of Open Access Journals (Sweden)

Zhipeng Yu

2017-02-01

Full Text Available 2D nitrogen-doped mesoporous carbon (NMC is synthesized by using a mesoporous silica film as hard template, which is then investigated as a non-precious metal catalyst for the oxygen reduction reaction (ORR. The effect of the synthesis conditions on the silica template and carbon is extensively investigated. In this work, we employ dual templates—viz. graphene oxide and triblock copolymer F127—to control the textural features of a 2D silica film. The silica is then used as a template to direct the synthesis of a 2D nitrogen-doped mesoporous carbon. The resultant nitrogen-doped mesoporous carbon is characterized by transmission electron microscopy (TEM, nitrogen ad/desorption isotherms, X-ray photoelectron spectroscopy (XPS, cyclic voltammetry (CV, and rotating disk electrode measurements (RDE. The electrochemical test reveals that the obtained 2D-film carbon catalyst yields a highly electrochemically active surface area and superior electrocatalytic activity for the ORR compared to the 3D-particle. The superior activity can be firstly attributed to the difference in the specific surface area of the two catalysts. More importantly, the 2D-film morphology makes more active sites accessible to the reactive species, resulting in a much higher utilization efficiency and consequently better activity. Finally, it is noted that all the carbon catalysts exhibit a higher ORR activity than a commercial Pt catalyst, and are promising for use in fuel cells.

Co-electrospinning fabrication and photocatalytic performance of TiO2/SiO2 core/sheath nanofibers with tunable sheath thickness

International Nuclear Information System (INIS)

Cao, Houbao; Du, Pingfan; Song, Lixin; Xiong, Jie; Yang, Junjie; Xing, Tonghai; Liu, Xin; Wu, Rongrong; Wang, Minchao; Shao, Xiaoli

2013-01-01

Graphical abstract: - Highlights: • The core–sheath TiO 2 /SiO 2 nanofibers were fabricated by co-electrospinning technique. • The catalytic property of nanofibers with different sheath thickness was studied. • The potential methods of improving catalytic efficiency are suggested. - Abstract: In this paper, core/sheath TiO 2 /SiO 2 nanofibers with tunable sheath thickness were directly fabricated via a facile co-electrospinning technique with subsequent calcination at 500 °C. The morphologies and structures of core/sheath TiO 2 /SiO 2 nanofibers were characterized by TGA, FESEM, TEM, FTIR, XPS and BET. It was found that the 1D core/sheath nanofibers are made up of anatase–rutile TiO 2 core and amorphous SiO 2 sheath. The influences of SiO 2 sheath and its thickness on the photoreactivity were evaluated by observing photo-degradation of methylene blue aqueous solution under the irradiation of UV light. Compared with pure TiO 2 nanofibers, the core/sheath TiO 2 /SiO 2 nanofibers performed a better catalytic performance. That was attributed to not only efficient separation of hole–electron pairs resulting from the formation of heterojunction but also larger surface area and surface silanol group which will be useful to provide higher capacity for oxygen adsorption to generate more hydroxyl radicals. And the optimized core/sheath TiO 2 /SiO 2 nanofibers with a sheath thickness of 37 nm exhibited the best photocatalytic performance

Tumor vascular-targeted co-delivery of anti-angiogenesis and chemotherapeutic agents by mesoporous silica nanoparticle-based drug delivery system for synergetic therapy of tumor

Directory of Open Access Journals (Sweden)

Li X

2015-12-01

Full Text Available Xiaoyu Li, Meiying Wu, Limin Pan, Jianlin Shi State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai, People’s Republic of China Abstract: To overcome the drawback of drug non-selectivity in traditional chemotherapy, the construction of multifunctional targeting drug delivery systems is one of the most effective and prevailing approaches. The intratumoral anti-angiogenesis and the tumor cell-killing are two basic approaches in fighting tumors. Herein we report a novel tumor vascular-targeting multidrug delivery system using mesoporous silica nanoparticles as carrier to co-load an antiangiogenic agent (combretastatin A4 and a chemotherapeutic drug (doxorubicin and conjugate with targeting molecules (iRGD peptide for combined anti-angiogenesis and chemotherapy. Such a dual-loaded drug delivery system is capable of delivering the two agents at tumor vasculature and then within tumors through a differentiated drug release strategy, which consequently results in greatly improved antitumor efficacy at a very low doxorubicin dose of 1.5 mg/kg. The fast release of the antiangiogenic agent at tumor vasculatures led to the disruption of vascular structure and had a synergetic effect with the chemotherapeutic drug slowly released in the following delivery of chemotherapeutic drug into tumors. Keywords: mesoporous silica nanoparticles, drug delivery, tumor vasculatures targeting, antiangiogenic agent

Mesoporous TiO2 Micro-Nanometer Composite Structure: Synthesis, Optoelectric Properties, and Photocatalytic Selectivity

Directory of Open Access Journals (Sweden)

Kun Liu

2012-01-01

Full Text Available Mesoporous anatase TiO2 micro-nanometer composite structure was synthesized by solvothermal method at 180°C, followed by calcination at 400°C for 2 h. The as-prepared TiO2 was characterized by X-ray diffraction (XRD, scanning electron microscope (SEM, transmission electron microscope (TEM, and Fourier transform infrared spectrum (FT-IR. The specific surface area and pore size distribution were obtained from N2 adsorption-desorption isotherm, and the optoelectric property of the mesoporous TiO2 was studied by UV-Vis absorption spectrum and surface photovoltage spectra (SPS. The photocatalytic activity was evaluated by photodegradation of sole rhodamine B (RhB and sole phenol aqueous solutions under simulated sunlight irradiation and compared with that of Degussa P-25 (P25 under the same conditions. The photodegradation preference of this mesoporous TiO2 was also investigated for an RhB-phenol mixed solution. The results show that the TiO2 composite structure consists of microspheres (∼0.5–2 μm in diameter and irregular aggregates (several hundred nanometers with rough surfaces and the average primary particle size is 10.2 nm. The photodegradation activities of this mesoporous TiO2 on both RhB and phenol solutions are higher than those of P25. Moreover, this as-prepared TiO2 exhibits photodegradation preference on RhB in the RhB-phenol mixture solution.

Nanoscale silver-assisted wet etching of crystalline silicon for anti-reflection surface textures.

Science.gov (United States)

Li, Rui; Wang, Shuling; Chuwongin, Santhad; Zhou, Weidong

2013-01-01

We report here an electro-less metal-assisted chemical etching (MacEtch) process as light management surface-texturing technique for single crystalline Si photovoltaics. Random Silver nanostructures were formed on top of the Si surface based on the thin film evaporation and annealing process. Significant reflection reduction was obtained from the fabricated Si sample, with approximately 2% reflection over a wide spectra range (300 to 1050 nm). The work demonstrates the potential of MacEtch process for anti-reflection surface texture fabrication of large area, high efficiency, and low cost thin film solar cell.

Stability of trapped electrons in SiO2

International Nuclear Information System (INIS)

Fleetwood, D.M.; Winokur, P.S.; Flament, O.; Leray, J.L.

1998-01-01

Electron trapping near the Si/SiO 2 interface plays a crucial role in mitigating the response of MOS devices to ionizing radiation or high-field stress. These electrons offset positive charge due to trapped holes, and can be present at densities exceeding 10 12 cm -2 in the presence of a similar density of trapped positive charge. The nature of the defects that serve as hosts for trapped electrons in the near-interfacial SiO 2 is presently unknown, although there is compelling evidence that these defects are often intimately associated with trapped holes. This association is depicted most directly in the model of Lelis et al., which suggests that trapped electrons and holes occupy opposite sides of a compensated E center in SiO 2 . Charge exchange between electron traps and the Si can occur over a wide range of time scales, depending on the trap depth and location relative to the Si/SiO 2 interface. Here the authors report a detailed study of the stability of electron traps associated with trapped holes near the Si/SiO 2 interface

Theory of Al2O3 incorporation in SiO2

DEFF Research Database (Denmark)

Lægsgaard, Jesper

2002-01-01

Different possible forms of Al2O3 units in a SiO2 network are studied theoretically within the framework of density-functional theory. Total-energy differences between the various configurations are obtained, and simple thermodynamical arguments are used to provide an estimate of their relative...

Controlled synthesis of mesoporous β-Ni(OH)2 and NiO nanospheres with enhanced electrochemical performance

International Nuclear Information System (INIS)

Xing, Shengtao; Wang, Qian; Ma, Zichuan; Wu, Yinsu; Gao, Yuanzhe

2012-01-01

Highlights: ► Uniform mesoporous β-Ni(OH) 2 and NiO nanospheres with hierarchical structures were synthesized by a simple complexation–precipitation method. ► Both ammonia and citrate played an important role for the formation of mesoporous nanospheres. ► β-Ni(OH) 2 and NiO nanospheres showed excellent capacitive properties due to their mesoporous structures and larger surface areas. -- Abstract: Uniform mesoporous β-Ni(OH) 2 and NiO nanospheres with hierarchical structures were synthesized by a facile complexation–precipitation method. The effects of ammonia and citrate on the structure and morphology of the products were thoroughly investigated by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy and nitrogen adsorption–desorption measurements. The results indicated that ammonia played an important role for the formation of flowerlike spheres assembled from nanosheets. The addition of citrate could remarkably reduce the particle sizes and increase the specific surface areas of flowerlike spheres. A possible formation mechanism based on the experimental results was proposed to understand their growing procedures. β-Ni(OH) 2 and NiO nanospheres prepared with the addition of citrate showed excellent capacitive properties due to their mesoporous structures and large surface areas, suggesting the importance of controlled synthesis of hierarchical nanostructures for their applications.

Positron annihilation in SiO 2-Si studied by a pulsed slow positron beam

Science.gov (United States)

Suzuki, R.; Ohdaira, T.; Uedono, A.; Kobayashi, Y.

2002-06-01

Positron and positronium (Ps) behavior in SiO 2-Si have been studied by means of positron annihilation lifetime spectroscopy (PALS) and age-momentum correlation (AMOC) spectroscopy with a pulsed slow positron beam. The PALS study of SiO 2-Si samples, which were prepared by a dry-oxygen thermal process, revealed that the positrons implanted in the Si substrate and diffused back to the interface do not contribute to the ortho-Ps long-lived component, and the lifetime spectrum of the interface has at least two components. From the AMOC study, the momentum distribution of the ortho-Ps pick-off annihilation in SiO 2, which shows broader momentum distribution than that of crystalline Si, was found to be almost the same as that of free positron annihilation in SiO 2. A varied interface model was proposed to interpret the results of the metal-oxide-semiconductor (MOS) experiments. The narrow momentum distribution found in the n-type MOS with a negative gate bias voltage could be attributed to Ps formation and rapid spin exchange in the SiO 2-Si interface. We have developed a two-dimensional positron lifetime technique, which measures annihilation time and pulse height of the scintillation gamma-ray detector for each event. Using this technique, the positronium behavior in a porous SiO 2 film, grown by a sputtering method, has been studied.

Effect of SiO2 passivation overlayers on hillock formation in Al thin films

International Nuclear Information System (INIS)

Kim, Deok-kee

2012-01-01

Hillock formation in Al thin films with varying thicknesses of SiO 2 as a passivation layer was investigated during thermal cycling. Based on the stress measurements and the number of hillocks, 250 nm thick SiO 2 was thick enough to suppress the hillock formation and the suppression of hillock at 250 nm passivation and the lack of suppression at thinner passivation is related to the presence/absence of protection against the diffusive flow of atoms from the surrounding area to the surface due to the biaxial compressive stresses present in the film through the weak spots in the passivation layer. The stress state of Al films measured during annealing (the driving force for hillock formation) did not vary much with SiO 2 thickness. A small number of hillocks formed during the plasma enhanced chemical vapor deposition of SiO 2 overlayers at 300 °C. - Highlights: ► We examined the effect of SiO 2 overlayers on hillock formation in Al thin films. ► Thin overlayers were not effective in suppressing diffusive flow to the surface. ► A thick overlayer suppressed the diffusive flow from the interior to the surface. ► The stress state of Al films did not vary much with SiO 2 passivation thickness. ► High mechanical strength provided a large driving force for the large grain growth.

Crystallization and chemical durability of glasses in the system Bi2O3-SiO2

International Nuclear Information System (INIS)

Fredericci, C.

2011-01-01

The crystallization of the Bi 2 O 3 -SiO 2 -TiO 2 -Al 2 O 3 -Na 2 O-K 2 O and Bi 2 O 3 -SiO 2 -ZnO-Al 2 O 3 -B 2 O 3 -Na 2 O glasses was studied using glass samples prepared by traditional melt-quench method. Differential thermal analysis (DTA) curves suggested that surface crystallization played a major role in the crystallization of the glass samples. X-ray diffraction (XRD) analysis revealed the crystallization of bismuth silicate for both glasses and bismuth silicate and zinc silicate for the glass containing ZnO. Through scanning electron microscopy (MEV) and energy dispersive spectroscopy (EDS), it was possible to observe that the crystals of zinc silicate (Zn 2 SiO 4 ) were readily attacked by hot 0,1 N sulfuric acid, whereas bismuth silicate crystals were more resistant to acidic attack etching. (author)

Preparation of Carbon Nanotube/TiO2 Mesoporous Hybrid Photoanode with Iron Pyrite (FeS2) Thin Films Counter Electrodes for Dye-Sensitized Solar Cell

Science.gov (United States)

Kilic, Bayram; Turkdogan, Sunay; Astam, Aykut; Ozer, Oguz Can; Asgin, Mansur; Cebeci, Hulya; Urk, Deniz; Mucur, Selin Pravadili

2016-05-01

Multi-walled carbon nanotube (MWCNT)/TiO2 mesoporous networks can be employed as a new alternative photoanode in dye-sensitized solar cells (DSSCs). By using the MWCNT/TiO2 mesoporous as photoanodes in DSSC, we demonstrate that the MWCNT/TiO2 mesoporous photoanode is promising alternative to standard FTO/TiO2 mesoporous based DSSC due to larger specific surface area and high electrochemical activity. We also show that iron pyrite (FeS2) thin films can be used as an efficient counter electrode (CE), an alternative to the conventional high cost Pt based CE. We are able to synthesis FeS2 nanostructures utilizing a very cheap and easy hydrothermal growth route. MWCNT/TiO2 mesoporous based DSSCs with FeS2 CE achieved a high solar conversion efficiency of 7.27% under 100 mW cm-2 (AM 1.5G 1-Sun) simulated solar irradiance which is considerably (slightly) higher than that of A-CNT/TiO2 mesoporous based DSSCs with Pt CE. Outstanding performance of the FeS2 CE makes it a very promising choice among the various CE materials used in the conventional DSSC and it is expected to be used more often to achieve higher photon-to-electron conversion efficiencies.

Compositional and optical properties of SiO x films and (SiO x /SiO y ) junctions deposited by HFCVD

Science.gov (United States)

2014-01-01

In this work, non-stoichiometric silicon oxide (SiO x ) films and (SiO x /SiO y ) junctions, as-grown and after further annealing, are characterized by different techniques. The SiO x films and (SiO x /SiO y ) junctions are obtained by hot filament chemical vapor deposition technique in the range of temperatures from 900°C to 1,150°C. Transmittance spectra of the SiO x films showed a wavelength shift of the absorption edge thus indicating an increase in the optical energy band gap, when the growth temperature decreases; a similar behavior is observed in the (SiO x /SiO y ) structures, which in turn indicates a decrease in the Si excess, as Fourier transform infrared spectroscopy (FTIR) reveals, so that, the film and junction composition changes with the growth temperature. The analysis of the photoluminescence (PL) results using the quantum confinement model suggests the presence of silicon nanocrystal (Si-nc) embedded in a SiO x matrix. For the case of the as-grown SiO x films, the absorption and emission properties are correlated with quantum effects in Si-nc and defects. For the case of the as-grown (SiO x /SiO y ) junctions, only the emission mechanism related to some kinds of defects was considered, but silicon nanocrystal embedded in a SiO x matrix is present. After thermal annealing, a phase separation into Si and SiO2 occurs, as the FTIR spectra illustrates, which has repercussions in the absorption and emission properties of the films and junctions, as shown by the change in the A and B band positions on the PL spectra. These results lead to good possibilities for proposed novel applications in optoelectronic devices. PACS 61.05.-a; 68.37.Og; 61.05.cp; 78.55.-m; 68.37.Ps; 81.15.Gh PMID:25342935

Self-Ordered Voids Formation in SiO2 Matrix by Ge Outdiffusion

Directory of Open Access Journals (Sweden)

B. Pivac

2018-01-01

Full Text Available The annealing behavior of very thin SiO2/Ge multilayers deposited on Si substrate by e-gun deposition in high vacuum was explored. It is shown that, after annealing at moderate temperatures (800°C in inert atmosphere, Ge is completely outdiffused from the SiO2 matrix leaving small (about 3 nm spherical voids embedded in the SiO2 matrix. These voids are very well correlated and formed at distances governed by the preexisting multilayer structure (in vertical direction and self-organization (in horizontal direction. The formed films produce intensive photoluminescence (PL with a peak at 500 nm. The explored dynamics of the PL decay show the existence of a very rapid process similar to the one found at Ge/SiO2 defected interface layers.

Si nanocrystals embedded in SiO2: Optical studies in the vacuum ultraviolet range

DEFF Research Database (Denmark)

Pankratov, V.; Osinniy, Viktor; Kotlov, A.

2011-01-01

done. It is demonstrated that the experimentally determined blueshift of the photoluminescence excitation and absorption spectra is larger than the theoretical predictions. The influence of point defects in the SiO2 matrix on the optical and luminescence properties of the embedded Si nanocrystals...... is discussed. Moreover, it is demonstrated that no energy transfer takes place between the SiO2 and Si nanocrystals when the excitation energy is higher than the band-to-band transition energy in SiO2....

B2O3/SiO2 substitution effect on structure and properties of Na2O-CaO-SrO-P2O5-SiO2 bioactive glasses from molecular dynamics simulations.

Science.gov (United States)

Ren, Mengguo; Lu, Xiaonan; Deng, Lu; Kuo, Po-Hsuen; Du, Jincheng

2018-05-23

The effect of B2O3/SiO2 substitution in SrO-containing 55S4.3 bioactive glasses on glass structure and properties, such as ionic diffusion and glass transition temperature, was investigated by combining experiments and molecular dynamics simulations with newly developed potentials. Both short-range (such as bond length and bond angle) and medium-range (such as polyhedral connection and ring size distribution) structures were determined as a function of glass composition. The simulation results were used to explain the experimental results for glass properties such as glass transition temperature and bioactivity. The fraction of bridging oxygen increased linearly with increasing B2O3 content, resulting in an increase in overall glass network connectivity. Ion diffusion behavior was found to be sensitive to changes in glass composition and the trend of the change with the level of substitution is also temperature dependent. The differential scanning calorimetry (DSC) results show a decrease in glass transition temperature (Tg) with increasing B2O3 content. This is explained by the increase in ion diffusion coefficient and decrease in ion diffusion energy barrier in glass melts, as suggested by high-temperature range (above Tg) ion diffusion calculations as B2O3/SiO2 substitution increases. In the low-temperature range (below Tg), the Ea for modifier ions increased with B2O3/SiO2 substitution, which can be explained by the increase in glass network connectivity. Vibrational density of states (VDOS) were calculated and show spectral feature changes as a result of the substitution. The change in bioactivity with B2O3/SiO2 substitution is discussed with the change in pH value and release of boric acid into the solution.

Carbon-coated mesoporous SnO2 nanospheres as anode material for lithium ion batteries

International Nuclear Information System (INIS)

Wang, Fei; Song, Xiaoping; Yao, Gang; Zhao, Mingshu; Liu, Rui; Xu, Minwei; Sun, Zhanbo

2012-01-01

In this paper mesoporous SnO 2 nanospheres with an average diameter of about 83 nm, composed of many tiny primary particles (∼10 nm) and holes, are synthesized on a large scale by a simple hydrothermal route. The as-prepared mesoporous SnO 2 nanospheres were uniformly coated with carbon by a further hydrothermal treatment in glucose aqueous solution. As anode materials for lithium-ion batteries, the core–shell SnO 2 /C nanocomposites exhibit a markedly improved cycling performance.

Fluorescein isothiocyanate and rhodamine B dye encapsulated mesoporous SiO2 for applications of blue LED excited white LED

Science.gov (United States)

Das, Sourav; Manam, J.

2018-05-01

In this work, the fluorescein isothiocyanate (FITC) and rhodamine B (RhB) dyes were encapsulated in mesoporous silica nanoparticles (MSNp). The MSNp-FITC-RhB nanohybrids phosphor showed a dichromatic PL emission at green region and orange region when excited at 460 nm. A Forster Resonance Energy Transfer (FRET) was observed from FITC to RhB. The materials were further characterized by XRD, FTIR, TEM, and temperature dependent photoluminescence. The CIE coordinates were tuned from greenish yellow to the orange region and quantum yield was reached 52.04% based on FRET. So by combining the MSNp-FITC-RhB nanohybrids phosphor with the blue LED chip, the white light emission with flexible Color Correlated Temperature and improved Color Rendering Index can be obtained.

Ultralow-density SiO2 aerogels prepared by a two-step sol-gel process

International Nuclear Information System (INIS)

Wang Jue; Li Qing; Shen Jun; Zhou Bin; Chen Lingyan; Jiang; Weiyang

1996-01-01

Low density SiO 2 gels are prepared by a two-step sol-gel process from TEOS. The influence of various solution ratios on the gelation process is investigated. The comparative characterization of gels using different solvent, such as ethanol, acetone and methyl cyanide, is also given. The ultralow-density SiO 2 aerogels with density less than 10 kg/m 3 are prepared by CO 2 supercritical drying technique. The structure difference between SiO 2 aerogels prepared by conventional single-step process and the two-step process is also presented

Structure-Dependent Spectroscopic Properties of Yb3+-Doped Phosphosilicate Glasses Modified by SiO2

Directory of Open Access Journals (Sweden)

Ling Wang

2017-02-01

Full Text Available Yb3+-doped phosphate glasses containing different amounts of SiO2 were successfully synthesized by the conventional melt-quenching method. The influence mechanism of SiO2 on the structural and spectroscopic properties was investigated systematically using the micro-Raman technique. It was worth noting that the glass with 26.7 mol % SiO2 possessed the longest fluorescence lifetime (1.51 ms, the highest gain coefficient (1.10 ms·pm2, the maximum Stark splitting manifold of 2F7/2 level (781 cm−1, and the largest scalar crystal-field NJ and Yb3+ asymmetry degree. Micro-Raman spectra revealed that introducing SiO2 promoted the formation of P=O linkages, but broke the P=O linkages when the SiO2 content was greater than 26.7 mol %. Based on the previous 29Si MAS NMR experimental results, these findings further demonstrated that the formation of [SiO6] may significantly affect the formation of P=O linkages, and thus influences the spectroscopic properties of the glass. These results indicate that phosphosilicate glasses may have potential applications as a Yb3+-doped gain medium for solid-state lasers and optical fiber amplifiers.

Structure-Dependent Spectroscopic Properties of Yb3+-Doped Phosphosilicate Glasses Modified by SiO2

Science.gov (United States)

Wang, Ling; Zeng, Huidan; Yang, Bin; Ye, Feng; Chen, Jianding; Chen, Guorong; Smith, Andew T.; Sun, Luyi

2017-01-01

Yb3+-doped phosphate glasses containing different amounts of SiO2 were successfully synthesized by the conventional melt-quenching method. The influence mechanism of SiO2 on the structural and spectroscopic properties was investigated systematically using the micro-Raman technique. It was worth noting that the glass with 26.7 mol % SiO2 possessed the longest fluorescence lifetime (1.51 ms), the highest gain coefficient (1.10 ms·pm2), the maximum Stark splitting manifold of 2F7/2 level (781 cm−1), and the largest scalar crystal-field NJ and Yb3+ asymmetry degree. Micro-Raman spectra revealed that introducing SiO2 promoted the formation of P=O linkages, but broke the P=O linkages when the SiO2 content was greater than 26.7 mol %. Based on the previous 29Si MAS NMR experimental results, these findings further demonstrated that the formation of [SiO6] may significantly affect the formation of P=O linkages, and thus influences the spectroscopic properties of the glass. These results indicate that phosphosilicate glasses may have potential applications as a Yb3+-doped gain medium for solid-state lasers and optical fiber amplifiers. PMID:28772601

Effect of sol aging time on the anti-reflective properties of silica coatings templated with phosphoric acid

Directory of Open Access Journals (Sweden)

Wen Wen

Full Text Available Silica anti-reflective coatings have been prepared by a sol–gel dip-coating process using the sol containing phosphoric acid as a pore-forming template. The effect of the aging time of the sol on the anti-reflective properties has been investigated. The surface topography of the silica AR coatings has been characterized. With increasing sol aging time, more over-sized pores larger than 100 nm are formed in the silica coatings. These could act as scattering centers, scattering visible light and thereby lowering transmittance. The optimal aging time was identified as 1 day, and the corresponding silica coatings showed a maximum transmittance of 99.2%, representing an 8% increase compared to the bare glass substrate. Keywords: Thin films, Anti-reflective coatings, Aging, Dip-coating, Sol–gel preparation

Enhancement of photocatalytic properties of TiO2 nanoparticles doped with CeO2 and supported on SiO2 for phenol degradation

International Nuclear Information System (INIS)

Hao, Chunjing; Li, Jing; Zhang, Zailei; Ji, Yongjun; Zhan, Hanhui; Xiao, Fangxing; Wang, Dan; Liu, Bin; Su, Fabing

2015-01-01

Highlights: • CeO 2 -TiO 2 /SiO 2 composites were prepared via a facile co-precipitation method. • Introduction of SiO 2 support increases the dispersion of CeO 2 -TiO 2 . • CeO 2 -TiO 2 /SiO 2 exhibits an enhanced photocatalytic efficiency for phenol degradation. • Ce 3+ /Ce 4+ pair coexisting in CeO 2 improves electron–hole pairs separation efficiency. - Abstract: A series of CeO 2 -TiO 2 and CeO 2 -TiO 2 /SiO 2 composites were prepared with TiCl 4 and Ce (NO 3 ) 3 ·6H 2 O as precursors via a facile co-precipitation method. The obtained samples were characterized by various techniques such as X-ray diffraction (XRD), nitrogen adsorption (N 2 -BET), Fourier transformation infrared spectrum (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM), and UV–Vis spectroscopy measurements. The results indicated that TiO 2 doped with CeO 2 and supported on SiO 2 could reduce the crystallite size, inhibit the phase transformation, enhance the thermal stability, and effectively extend the spectral response from UV to visible range. When applied to the phenol photodegradation on a homemade batch reactor with an external cooling jacket, the CeO 2 -TiO 2 /SiO 2 catalysts exhibited significantly enhanced photodegradation efficiency in comparison with commercial Degussa P25 and CeO 2 -TiO 2 . The unique catalytic properties of CeO 2 -TiO 2 /SiO 2 were ascribed to improved electron–hole pairs separation efficiency and formation of more reactive oxygen species owing to the presence of Ce 3+ /Ce 4+ , as well as high dispersion of active component of CeO 2 -TiO 2 as a result of the introduction of SiO 2 support. Furthermore, the catalysts can be easily recovered from the reaction solution by centrifugation and reused for four cycles without significant loss of activity

Synthesis of MgO nanoparticle loaded mesoporous Al2O3 and its defluoridation study

International Nuclear Information System (INIS)

Dayananda, Desagani; Sarva, Venkateswara R.; Prasad, Sivankutty V.; Arunachalam, Jayaraman; Parameswaran, Padmanabhan; Ghosh, Narendra N.

2015-01-01

Highlights: • Simple and cost effective preparation of MgO nanoparticles loaded mesoporous Al 2 O 3 . • Adsorbents possess high surface area and mesoporous structure. • Higher fluoride removal capacity of MgO loaded Al 2 O 3 than that of pure Al 2 O 3 . • Faster fluoride adsorption kinetics of MgO loaded Al 2 O 3 from water. - Abstract: MgO nanoparticle loaded mesoporous alumina has been synthesized using a simple aqueous solution based cost effective method for removal of fluoride from water. Wide angle powder X-ray diffraction, nitrogen adsorption desorption analysis, transmission electron microscopy techniques and energy dispersive X-ray spectroscopy were used to characterize the synthesized adsorbents. Synthesized adsorbents possess high surface area with mesoporous structure. The adsorbents have been thoroughly investigated for the adsorption of F − using batch adsorption method. MgO nanoparticle loading on mesoporous Al 2 O 3 enhances the F − adsorption capacity of Al 2 O 3 from 56% to 90% (initial F − concentration = 10 mg L −1 ). Kinetic study revealed that adsorption kinetics follows the pseudo-second order model, suggesting the chemisorption mechanism. The F − adsorption isotherm data was explained by both Langmuir and Freundlich model. The maximum adsorption capacity of 40MgO@Al 2 O 3 was 37.35 mg g −1 . It was also observed that, when the solutions having F − concentration of 5 mg L −1 and 10 mg L −1 was treated with 40MgO@Al 2 O 3 , the F − concentration in treated water became <1 mg L −1 , which is well below the recommendation of WHO

Fiber-optic thermometer application of thermal radiation from rare-earth end-doped SiO2 fiber

International Nuclear Information System (INIS)

Katsumata, Toru; Morita, Kentaro; Komuro, Shuji; Aizawa, Hiroaki

2014-01-01

Visible light thermal radiation from SiO 2 glass doped with Y, La, Ce, Pr, Nd, Eu, Tb, Dy, Ho, Er, Tm, Yb, and Lu were studied for the fiber-optic thermometer application based on the temperature dependence of thermal radiation. Thermal radiations according to Planck's law of radiation are observed from the SiO 2 fibers doped with Y, La, Ce, Pr, Eu, Tb, and Lu at the temperature above 1100 K. Thermal radiations due to f-f transitions of rare-earth ions are observed from the SiO 2 fibers doped with Nd, Dy, Ho, Er, Tm, and Yb at the temperature above 900 K. Peak intensities of thermal radiations from rare-earth doped SiO 2 fibers increase sensitively with temperature. Thermal activation energies of thermal radiations by f-f transitions seen in Nd, Dy, Ho, Er, Tm, and Yb doped SiO 2 fibers are smaller than those from SiO 2 fibers doped with Y, La, Ce, Pr, Eu, Tb, and Lu. Thermal radiation due to highly efficient f-f transitions in Nd, Dy, Ho, Er, Tm, and Yb ions emits more easily than usual thermal radiation process. Thermal radiations from rare-earth doped SiO 2 are potentially applicable for the fiber-optic thermometry above 900 K

Preparation of Raspberry-like Superhydrophobic SiO2 Particles by Sol-gel Method and Its Potential Applications

Directory of Open Access Journals (Sweden)

Xu Gui-Long

2011-12-01

Full Text Available Raspberry‐like SiO2 particles with a nano‐micro‐binary structure were prepared by a simple sol‐gel method using tetraethoxysilane (TEOS and methyltriethoxysilane (MTES as precursors. The chemical components and morphology of the SiO2 particles were characterized by Fourier transform infrared spectroscopy (FT‐IR and a Transmission electron microscope (TEM. The surface topography and wetting behaviour of the raspberry‐like SiO2 surface were observed with a Scanning electron microscope (SEM and studied by the water/oil contact angle (CA, respectively. The thermal stability of the prepared SiO2 particles was characterized by TGA analysis. The results show that the highly dispersed SiO2 particles initially prepared by the sol‐gel method turn into raspberry‐like particles with during the aging process. The raspberry‐like SiO2 particles show superhydrophobicity and superoleophilicity across a wide range of pH values. The SiO2 particles were thermally stable up to 475°C, while above this temperature the hydrophobicity decreases and finally becomes superhydrophobic when the temperature reaches 600°C. The raspberry‐like SiO2 particles which were prepared have potential applications in the fields of superhydrophobic surfaces, water‐oil separation, anti‐corrosion and fluid transportation.

Super-bright and short-lived photoluminescence of textured Zn2SiO4:Mn2+ phosphor film on quartz glass

Science.gov (United States)

Park, Jehong; Park, Kwangwon; Lee, Jaebum; Kim, Jongsu; Seo, Kwangil; Kwon, Kevin; Kung, Patrick; Kim, Seongsin M.

2010-02-01

Green-emissive textured Zn2SiO4:Mn2+ phosphor film was fabricated by a thermal diffusion of ZnO:Mn on quartz glass. The characterization has been performed in terms of Mn2+ ions concentration (Mn/Zn=1~9 mol %). As an increase of Mn2+ ions concentration in the Zn2SiO4:Mn2+ phosphor film, the emission peak was red shifted from 519 nm to 526 nm, and the decay time to 10% of the maximum intensity was shorter from 20 ms to 0.5 ms. All annealed Zn2SiO4:Mn2+ phosphor films became textured along some hexagonal directions on the amorphous quartz glass. The brightest Zn2SiO4:Mn2+ film at optimal Mn2+ concentration of 5 % showed the photoluminescence brightness of 65 % and the shortened decay time of 4.4 ms in comparison with a commercially Zn2SiO4: Mn2+ powder phosphor screen. The excellencies can be attributed to a unique textured structure.

Composite hydrogel based on surface modified mesoporous silica and poly[(2-acryloyloxy)ethyl trimethylammonium chloride

Energy Technology Data Exchange (ETDEWEB)

Torres, Cecilia C. [Department of Organic Chemistry, Faculty of Chemical Science, University of Concepción (Chile); Urbano, Bruno F., E-mail: burbano@udec.cl [Department of Polymer Chemistry, Faculty of Chemical Science, University of Concepción (Chile); Campos, Cristian H. [Department of Organic Chemistry, Faculty of Chemical Science, University of Concepción (Chile); Rivas, Bernabé L. [Department of Polymer Chemistry, Faculty of Chemical Science, University of Concepción (Chile); Reyes, Patricio [Department of Physical Chemistry, Faculty of Chemical Science, University of Concepción (Chile)

2015-02-15

This work focused on the synthesis, characterization and water absorbency of a composite hydrogel based on poly[(2-acryloyloxy)ethyl trimethylammonium chloride] and mesoporous silica, MCM-41. The MCM-41 was synthesized and later surface functionalized with triethoxyvinylsilane (VTES) and 3-trimethoxysilylpropylmethacrylate (TMSPM) by a post-grafting procedure. The composite hydrogels were obtained by in-situ polymerization using a mixture of monomer, crosslinker and initiator in the presence of functionalized MCM-41. Diverse characterization techniques were used at the different stages of synthesis, namely, FT-IR, TEM, SEM, DRX, {sup 29}Si and {sup 13}C solid state NMR, and N{sub 2} adsorption isotherms at 77 K. Finally, the water uptake performance of the composites was tested as a function of time, mesoporous silica loading and coupling agent used at the functionalization. The composites using non-functionalized MCM-41 reached the highest water uptake, whereas those composite with MCM-41 TMSPM exhibited the lowest sorption. - Highlights: • Hydrophilic crosslinked polymer-mesoporous silica was obtained. • Mesoporous silica MCM-41 was synthesized and functionalized with organosilane. • Functionalization of MCM-41 affects the water uptake of composite. • Mesoporous silica is covalently bound to the polymer acting as crosslinked point.

In-situ synthesis of SiO2@MOF composites for high-efficiency removal of aniline from aqueous solution

Science.gov (United States)

Han, Tongtong; Li, Caifeng; Guo, Xiangyu; Huang, Hongliang; Liu, Dahuan; Zhong, Chongli

2016-12-01

A series of SiO2@aluminum-MOF(MIL-68) composites with different SiO2 loadings have been synthesized by a simple and mild compositing strategy for high-efficiency removal of aniline. As evidenced from SEM and TEM images as well as the particle size distribution, the incorporation of SiO2 can improve the dispersity of MIL-68(Al) in composites, and result in the smaller particle size than that of pristine MIL-68(Al). Besides, the adsorption of aniline over SiO2, MIL-68(Al), the physical mixture of these two materials, and SiO2@MIL-68(Al) composites was investigated comparatively, demonstrating a relatively high adsorption capacity (531.9 mg g-1) of 7% SiO2@MIL-68(Al) towards aniline. Combining the ultrafast adsorption dynamics (reaching equilibrium within 40 s) and great reusability, 7% SiO2@MIL-68(Al) shows excellent adsorption performance. This indicates that the SiO2@MIL-68(Al) composites possess great potential applications as a kind of fascinating adsorbent in water pollution protection.

Assembly of Fe3O4 nanoparticles on SiO2 monodisperse spheres

Indian Academy of Sciences (India)

Assembly of Fe3O4 nanoparticles on SiO2 monodisperse spheres. K C BARICK and D BAHADUR*. Department of Metallurgical Engineering and Materials Science, Indian Institute of Technology Bombay,. Mumbai 400 076, India. Abstract. The assembly of superparamagnetic Fe3O4 nanoparticles on submicroscopic SiO2 ...

Identification and quality assessment of beverages using a long period grating fibre-optic sensor modified with a mesoporous thin film

Directory of Open Access Journals (Sweden)

Sergiy Korposh

2014-08-01

Full Text Available In this study, an optical fibre long period grating (LPG sensor functionalised with a mesoporous thin film was employed for the identification and quality assessment of beverages. The principle of the discrimination of beverages using an LPG sensor is based on the measurement of the change in refractive index of a sensitive film, induced by the binding of the chemical compounds present in the beverage. The sensitive film deposited onto the LPG consisted of poly(allylamine hydrochloride (PAH and silica nanospheres (SiO2 NPs with diameters ranging from 40 nm to 50 nm. PAH imparts selectivity, while the SiO2 NPs endow the film with high porosity and enhanced sensitivity. In this study, five different types of beverages, red and white wines, brandy, nihonshyu (sake, a Japanese rice wine, and shochu (a Japanese distilled beverage, prepared via distillation and fermentation, were used to assess the capability of the sensor to identify the origin of the beverages. In addition, a selection of red wines was used to evaluate the use of the sensor in the assessment of the quality of beverages. The results obtained were benchmarked against those obtained using gas chromatography–mass spectrometry for the determination of volatile compounds contributing to the flavours of a set of red wines. Principal component analysis (PCA was employed for data analysis. This approach enabled both quality assessment of beverages and identification of the methods and materials used for their preparation. Keywords: Long period grating, Mesoporous thin film, Layer-by-layer, Quality assessment, Beverages

A study of the anti-reflection efficiency of natural nano-arrays of varying sizes

International Nuclear Information System (INIS)

Sun Mingxia; Liang Aiping; Zheng Yongmei; Watson, Gregory S; Watson, Jolanta A

2011-01-01

The dependence of optical reflectivity and wettability on the surface topography of 32 species of cicada wing membranes has been investigated using UV-visible spectrophotometry, contact angle measurements and environmental scanning electron microscopy. The nanoscale hexagonally close packed protrusions have been shown to exhibit an anti-reflection and in some cases an anti-wetting function. The parameters of the structures were measured to be 77-148 nm in diameter, 44-117 nm in spacing and 159-481 nm in height. The transmittance spectrum and static contact angles were measured. At a wavelength range of 500-2500 nm, only minor differences in the anti-reflection performance were observed for each cicada species ascribed to the mechanism of impedance matching between cuticle and air. The transmittance properties of cicada wings were altered successfully through the scanning probe microscope-based manipulation by reducing the protrusion height via the contact mode. A near linear dependence was found between a decrease in protuberance height and a resulting increase in reflectance intensity. A diversity of wettability was observed with contact angles varying from 56.5 0 to 146.0 0 . Both effects of anti-reflection and wettability are dependent on the height of protrusions. The anti-reflection is insensitive when the wavelength is larger than the lateral feature size of the nanostructure. The stronger hydrophobic properties are generally associated with a larger diameter, closer spacing and greater height of protrusions when the wing membrane is intact.

Origin of the n -type and p -type conductivity of MoS 2 monolayers on a SiO 2 substrate

KAUST Repository

Dolui, Kapildeb

2013-04-02

Ab initio density functional theory calculations are performed to study the electronic properties of a MoS2 monolayer deposited over a SiO 2 substrate in the presence of interface impurities and defects. When MoS2 is placed on a defect-free substrate, the oxide plays an insignificant role since the conduction band top and the valence band minimum of MoS2 are located approximately in the middle of the SiO2 band gap. However, if Na impurities and O dangling bonds are introduced at the SiO2 surface, these lead to localized states, which modulate the conductivity of the MoS2 monolayer from n- to p-type. Our results show that the conductive properties of MoS2 deposited on SiO 2 are mainly determined by the detailed structure of the MoS 2/SiO2 interface, and suggest that doping the substrate can represent a viable strategy for engineering MoS2-based devices. © 2013 American Physical Society.

Synthesis and electrochemical performance of mesoporous SiO{sub 2}–carbon nanofibers composite as anode materials for lithium secondary batteries

Energy Technology Data Exchange (ETDEWEB)

Hyun, Yura; Choi, Jin-Yeong [Department of Chemistry, Keimyung University (Korea, Republic of); Park, Heai-Ku [Department of Chemical Engineering, Keimyung University (Korea, Republic of); Bae, Jae Young [Department of Chemistry, Keimyung University (Korea, Republic of); Lee, Chang-Seop, E-mail: surfkm@kmu.ac.kr [Department of Chemistry, Keimyung University (Korea, Republic of)

2016-10-15

Highlights: • Mesoporous SiO{sub 2}–carbon nanofibers composite synthesized on Ni foam without any binder. • This composite was directly applied as anode material of Li secondary batteries. • Showed the highest initial (2420 mAh/g) and discharging (2092 mAh/g) capacity. • This material achieved a retention rate of 86.4% after 30 cycles. - Abstract: In this study, carbon nanofibers (CNFs) and mesoporous SiO{sub 2}–carbon nanofibers composite were synthesized and applied as the anode materials in lithium secondary batteries. CNFs and mesoporous SiO{sub 2}–CNFs composite were grown via chemical vapor deposition method with iron-copper catalysts. Mesoporous SiO{sub 2} materials were prepared by sol–gel method using tetraethylorthosilicate as the silica source and cetyltrimethylammoniumchloride as the template. Ethylene was used as the carbon source and passes into a quartz reactor of a tube furnace heated to 600 °C, and the temperature was maintained at 600 °C for 10 min to synthesize CNFs and mesoporous SiO{sub 2}–CNFs composite. The electrochemical characteristics of the as-prepared CNFs and mesoporous SiO{sub 2}–CNFs composite as the anode of lithium secondary batteries were investigated using a three-electrode cell. In particular, the mesoporous SiO{sub 2}–CNFs composites synthesized without binder after depositing mesoporous SiO{sub 2} on Ni foam showed the highest charging and discharging capacity and retention rate. The initial capacity (2420 mAh/g) of mesoporous SiO{sub 2}–CNFs composites decreased to 2092 mAh/g after 30 cycles at a retention rate of 86.4%.

Synthesis of Mesoporous Single Crystal Co(OH)2 Nanoplate and Its Topotactic Conversion to Dual-Pore Mesoporous Single Crystal Co3O4.

Science.gov (United States)

Jia, Bao-Rui; Qin, Ming-Li; Li, Shu-Mei; Zhang, Zi-Li; Lu, Hui-Feng; Chen, Peng-Qi; Wu, Hao-Yang; Lu, Xin; Zhang, Lin; Qu, Xuan-Hui

2016-06-22

A new class of mesoporous single crystalline (MSC) material, Co(OH)2 nanoplates, is synthesized by a soft template method, and it is topotactically converted to dual-pore MSC Co3O4. Most mesoporous materials derived from the soft template method are reported to be amorphous or polycrystallined; however, in our synthesis, Co(OH)2 seeds grow to form single crystals, with amphiphilic block copolymer F127 colloids as the pore producer. The single-crystalline nature of material can be kept during the conversion from Co(OH)2 to Co3O4, and special dual-pore MSC Co3O4 nanoplates can be obtained. As the anode of lithium-ion batteries, such dual-pore MSC Co3O4 nanoplates possess exceedingly high capacity as well as long cyclic performance (730 mAh g(-1) at 1 A g(-1) after the 350th cycle). The superior performance is because of the unique hierarchical mesoporous structure, which could significantly improve Li(+) diffusion kinetics, and the exposed highly active (111) crystal planes are in favor of the conversion reaction in the charge/discharge cycles.

UV Light-Driven Photodegradation of Methylene Blue by Using Mn0.5Zn0.5Fe2O4/SiO2 Nanocomposites

Science.gov (United States)

Indrayana, I. P. T.; Julian, T.; Suharyadi, E.

2018-04-01

The photodegradation activity of nanocomposites for 20 ppm methylene blue solution has been investigated in this work. Nanocomposites Mn0.5Zn0.5Fe2O4/SiO2 have been synthesized using coprecipitation method. The X-ray diffraction (XRD) pattern confirmed the formation of three phases in sample Mn0.5Zn0.5Fe2O4/SiO2 i.e., Mn0.5Zn0.5Fe2O4, Zn(OH)2, and SiO2. The appearance of SiO2 phase showed that the encapsulation process has been carried out. The calculated particles size of Mn0.5Zn0.5Fe2O4/SiO2 is greater than Mn0.5Zn0.5Fe2O4. Bonding analysis via vibrational spectra for Mn0.5Zn0.5Fe2O4/SiO2 confirmed the formation of bonds Me-O-Si stretching (2854.65 cm-1) and Si-O-Si asymmetric stretching (1026.13 cm-1). The optical gap energy of Mn0.5Zn0.5Fe2O4/SiO2 was smaller (2.70 eV) than Mn0.5Zn0.5Fe2O4 (3.04 eV) due to smaller lattice dislocation and microstrain that affect their electronic structure. The Mn0.5Zn0.5Fe2O4/SiO2 showed high photodegradation ability due to smaller optical gap energy and the appearance of SiO2 ligand that can easily attract dye molecules. The Mn0.5Zn0.5Fe2O4/SiO2 also showed high degradation activity even without UV light radiation. The result showed that photodegradation reaction doesn’t follow pseudo-first order kinetics.

Mesoporous amine-bridged polysilsesquioxane for CO2 capture

KAUST Repository

Qi, Genggeng

2011-01-01

A novel class of amine-supported sorbents based on amine-bridged mesoporous polysilsesquioxane was developed via a simple one-pot sol-gel process. The new sorbent allows the incorporation of a large amount of active groups without sacrificing surface area or pore volume available for CO2 capture, leading to a CO2 capture capacity of 3.2 mmol g−1 under simulated flue gas conditions. The sorbent is readily regenerated at 100°C and exhibits good stability over repetitive adsorption-desorption cycling.

Pd-Pt Catalysts on Mesoporous SiO2-Al2O3 with Superior Activity for HDS of 4,6-Dimethyldibenzothiophene: Effect of Metal Loading and Support Composition

Czech Academy of Sciences Publication Activity Database

Vít, Zdeněk; Gulková, Daniela; Kaluža, Luděk; Kupčík, Jaroslav

2015-01-01

Roč. 179, DEC 2015 (2015), s. 44-53 ISSN 0926-3373 R&D Projects: GA ČR GAP106/11/0902 Institutional support: RVO:67985858 ; RVO:61388980 Keywords : Pd-Pt catalyst * mesoporous silica-alumina * 4,6-DMDBT Subject RIV: CF - Physical ; Theoretical Chemistry ; CA - Inorganic Chemistry (UACH-T) Impact factor: 8.328, year: 2015

3D-Printed Broadband Dielectric Tube Terahertz Waveguide with Anti-Reflection Structure

Science.gov (United States)

Vogt, Dominik Walter; Leonhardt, Rainer

2016-11-01

We demonstrate broadband, low loss, and close-to-zero dispersion guidance of terahertz (THz) radiation in a dielectric tube with an anti-reflection structure (AR-tube waveguide) in the frequency range from 0.2 to 1.0 THz. The anti-reflection structure (ARS) consists of close-packed cones in a hexagonal lattice arranged on the outer surface of the tube cladding. The feature size of the ARS is in the order of the wavelength between 0.2 and 1.0 THz. The waveguides are fabricated with the versatile and cost efficient 3D-printing method. Terahertz time-domain spectroscopy (THz-TDS) measurements as well as 3D finite-difference time-domain simulations (FDTD) are performed to extensively characterize the AR-tube waveguides. Spectrograms, attenuation spectra, effective phase refractive indices, and the group-velocity dispersion parameters β 2 of the AR-tube waveguides are presented. Both the experimental and numerical results confirm the extended bandwidth and smaller group-velocity dispersion of the AR-tube waveguide compared to a low loss plain dielectric tube THz waveguide. The AR-tube waveguide prototypes show an attenuation spectrum close to the theoretical limit given by the infinite cladding tube waveguide.

Preparation of TiO2-SiO2 composite photocatalysts for environmental applications

Czech Academy of Sciences Publication Activity Database

Paušová, Š.; Krýsa, J.; Jirkovský, Jaromír; Prevot, V.; Mailhot, G.

2014-01-01

Roč. 89, č. 8 (2014), s. 1129-1135 ISSN 0268-2575 Institutional support: RVO:61388955 Keywords : photocatalysis * TiO2/SiO2 * composite Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 2.349, year: 2014

Transfer free graphene growth on SiO2 substrate at 250 °C

Science.gov (United States)

Vishwakarma, Riteshkumar; Rosmi, Mohamad Saufi; Takahashi, Kazunari; Wakamatsu, Yuji; Yaakob, Yazid; Araby, Mona Ibrahim; Kalita, Golap; Kitazawa, Masashi; Tanemura, Masaki

2017-03-01

Low-temperature growth, as well as the transfer free growth on substrates, is the major concern of graphene research for its practical applications. Here we propose a simple method to achieve the transfer free graphene growth on SiO2 covered Si (SiO2/Si) substrate at 250 °C based on a solid-liquid-solid reaction. The key to this approach is the catalyst metal, which is not popular for graphene growth by chemical vapor deposition. A catalyst metal film of 500 nm thick was deposited onto an amorphous C (50 nm thick) coated SiO2/Si substrate. The sample was then annealed at 250 °C under vacuum condition. Raman spectra measured after the removal of the catalyst by chemical etching showed intense G and 2D peaks together with a small D and intense SiO2 related peaks, confirming the transfer free growth of multilayer graphene on SiO2/Si. The domain size of the graphene confirmed by optical microscope and atomic force microscope was about 5 μm in an average. Thus, this approach will open up a new route for transfer free graphene growth at low temperatures.

Integrated nanophotonic hubs based on ZnO-Tb(OH3/SiO2 nanocomposites

Directory of Open Access Journals (Sweden)

Lin Yu

2011-01-01

Full Text Available Abstract Optical integration is essential for practical application, but it remains unexplored for nanoscale devices. A newly designed nanocomposite based on ZnO semiconductor nanowires and Tb(OH3/SiO2 core/shell nanospheres has been synthesized and studied. The unique sea urchin-type morphology, bright and sharply visible emission bands of lanthanide, and large aspect ratio of ZnO crystalline nanotips make this novel composite an excellent signal receiver, waveguide, and emitter. The multifunctional composite of ZnO nanotips and Tb(OH3/SiO2 nanoparticles therefore can serve as an integrated nanophotonics hub. Moreover, the composite of ZnO nanotips deposited on a Tb(OH3/SiO2 photonic crystal can act as a directional light fountain, in which the confined radiation from Tb ions inside the photonic crystal can be well guided and escape through the ZnO nanotips. Therefore, the output emission arising from Tb ions is truly directional, and its intensity can be greatly enhanced. With highly enhanced lasing emissions in ZnO-Tb(OH3/SiO2 as well as SnO2-Tb(OH3/SiO2 nanocomposites, we demonstrate that our approach is extremely beneficial for the creation of low threshold and high-power nanolaser.

Fabrication and characterization of mesoporous TiO2/polypyrrole-based nanocomposite for electrorheological fluid

International Nuclear Information System (INIS)

Wei Chuan; Zhu Yihua; Jin Yi; Yang Xiaoling; Li Chunzhong

2008-01-01

Mesoporous TiO 2 /polypyrrole (PPy)-based nanocomposite for electrorheological fluid was synthesized through one-pot method. By exploiting the combination conductivity of PPy and high dielectric constant of TiO 2 , the ER fluid exhibited an enhanced effect. The shear stress was 3.3 times as high as that of mesoporous TiO 2 . Powder X-ray diffraction (XRD), TEM and Fourier transform infrared (FT-IR) spectroscopy were employed to characterize the as-made samples. Using a modified rotational viscometer, the electrorheological effect was measured. Dielectric spectra were also given to explain the mechanism

Ordered mesoporous crystalline gamma-Al2O3 with variable architecture and porosity from a single hard template.

Science.gov (United States)

Wu, Zhangxiong; Li, Qiang; Feng, Dan; Webley, Paul A; Zhao, Dongyuan

2010-09-01

In this paper, an efficient route is developed for controllable synthesis of ordered mesoporous alumina (OMA) materials with variable pore architectures and high mesoporosity, as well as crystalline framework. The route is based on the nanocasting pathway with bimodal mesoporous carbon as the hard template. In contrast to conventional reports, we first realize the possibility of creating two ordered mesopore architectures by using a single carbon hard template obtained from organic-organic self-assembly, which is also the first time such carbon materials are adopted to replicate ordered mesoporous materials. The mesopore architecture and surface property of the carbon template are rationally designed in order to obtain ordered alumina mesostructures. We found that the key factors rely on the unique bimodal mesopore architecture and surface functionalization of the carbon hard template. Namely, the bimodal mesopores (2.3 and 5.9 nm) and the surface functionalities make it possible to selectively load alumina into the small mesopores dominantly and/or with a layer of alumina coated on the inner surface of the large primary mesopores with different thicknesses until full loading is achieved. Thus, OMA materials with variable pore architectures (similar and reverse mesostructures relative to the carbon template) and controllable mesoporosity in a wide range are achieved. Meanwhile, in situ ammonia hydrolysis for conversion of the metal precursor to its hydroxide is helpful for easy crystallization (as low as approximately 500 degrees C). Well-crystallized alumina frameworks composed of gamma-Al(2)O(3) nanocrystals with sizes of 6-7 nm are obtained after burning out the carbon template at 600 degrees C, which is advantageous over soft-templated aluminas. The effects of synthesis factors are demonstrated and discussed relative to control experiments. Furthermore, our method is versatile enough to be used for general synthesis of other important but difficult

Refractories in the Al2O3-ZrO2-SiO2 system

International Nuclear Information System (INIS)

Banerjee, S.P.; Bhadra, A.K.; Sircar, N.R.

1978-01-01

The effect of addition of ZrO 2 in different proportions in the refractories of the Al 2 O 3 -SiO 2 system was studied. The investigation was confined to two broad ranges of compositions incorporating zirconia (15-30 percent and 80-85 percent) in the Al 2 O 3 -ZrO 2 -SiO 2 system. The overall attainment of properties is dependent upon the mode of fabrication and firing, and bears a relationship with the phase assemblages and the relative proportion thereof. Of the different characteristics, the trend of dissociation of zircon has been found to be specially significant vis-a-vis the temperature of firing and thermal shock resistance. Reassociation of the dissociated products has been ascribed to bring forth improved resistance to thermal spalling. The different products developed during this investigation are considered to be very promising which find useful applications in view of the properties attained by them. (auth.)

Bulk properties and near-critical behaviour of SiO2 fluid

Science.gov (United States)

Green, Eleanor C. R.; Artacho, Emilio; Connolly, James A. D.

2018-06-01

Rocky planets and satellites form through impact and accretion processes that often involve silicate fluids at extreme temperatures. First-principles molecular dynamics (FPMD) simulations have been used to investigate the bulk thermodynamic properties of SiO2 fluid at high temperatures (4000-6000 K) and low densities (500-2240 kg m-3), conditions which are relevant to protoplanetary disc condensation. Liquid SiO2 is highly networked at the upper end of this density range, but depolymerises with increasing temperature and volume, in a process characterised by the formation of oxygen-oxygen (Odbnd O) pairs. The onset of vaporisation is closely associated with the depolymerisation process, and is likely to be non-stoichiometric at high temperature, initiated via the exsolution of O2 molecules to leave a Si-enriched fluid. By 6000 K the simulated fluid is supercritical. A large anomaly in the constant-volume heat capacity occurs near the critical temperature. We present tabulated thermodynamic properties for silica fluid that reconcile observations from FPMD simulations with current knowledge of the SiO2 melting curve and experimental Hugoniot curves.

Microstructural dependence on relevant physical-mechanical properties on SiO2-Na2O-CaO-P2O5 biological glasses.

Science.gov (United States)

Rajendran, V; Begum, A Nishara; Azooz, M A; el Batal, F H

2002-11-01

Bioactive glasses of the system SiO2-Na2O-CaO-P2O5 have been prepared by the normal melting and annealing technique. The elastic moduli, attenuation, Vickers hardness, fracture toughness and fracture surface energy have been obtained using the known method at room temperature. The temperature dependence of elastic moduli and attenuation measurements have been extended over a wide range of temperature from 150 to 500 K. The SiO2 content dependence of velocities, attenuation, elastic moduli, and other parameters show an interesting observation at 45 wt% of SiO2 by exhibiting an anomalous behaviour. A linear relation is developed for Tg, which explores the influence of Na2O on SiO2-Na2O-CaO-P2O5 bioactive glasses. The measured hardness, fracture toughness and fracture surface energy show a linear relation with Young's modulus. It is also interesting to note that the observed results are functions of polymerisation and the number of non-bridging oxygens (NBO) prevailing in the network with change in SiO2 content. The temperature dependence of velocities, attenuation and elastic moduli show the existence of softening in the glass network structure as temperature increases.

Controlled synthesis of mesoporous β-Ni(OH){sub 2} and NiO nanospheres with enhanced electrochemical performance

Energy Technology Data Exchange (ETDEWEB)

Xing, Shengtao; Wang, Qian [College of Chemistry and Material Sciences, Hebei Normal University, Shijiazhuang 050016 (China); Ma, Zichuan, E-mail: mazc@vip.163.com [College of Chemistry and Material Sciences, Hebei Normal University, Shijiazhuang 050016 (China); Wu, Yinsu; Gao, Yuanzhe [College of Chemistry and Material Sciences, Hebei Normal University, Shijiazhuang 050016 (China)

2012-09-15

Highlights: ► Uniform mesoporous β-Ni(OH){sub 2} and NiO nanospheres with hierarchical structures were synthesized by a simple complexation–precipitation method. ► Both ammonia and citrate played an important role for the formation of mesoporous nanospheres. ► β-Ni(OH){sub 2} and NiO nanospheres showed excellent capacitive properties due to their mesoporous structures and larger surface areas. -- Abstract: Uniform mesoporous β-Ni(OH){sub 2} and NiO nanospheres with hierarchical structures were synthesized by a facile complexation–precipitation method. The effects of ammonia and citrate on the structure and morphology of the products were thoroughly investigated by X-ray powder diffraction, scanning electron microscopy, transmission electron microscopy and nitrogen adsorption–desorption measurements. The results indicated that ammonia played an important role for the formation of flowerlike spheres assembled from nanosheets. The addition of citrate could remarkably reduce the particle sizes and increase the specific surface areas of flowerlike spheres. A possible formation mechanism based on the experimental results was proposed to understand their growing procedures. β-Ni(OH){sub 2} and NiO nanospheres prepared with the addition of citrate showed excellent capacitive properties due to their mesoporous structures and large surface areas, suggesting the importance of controlled synthesis of hierarchical nanostructures for their applications.

Enhancement of the CIGS solar cell's efficiency by anti-reflection coating with teflon AF

Energy Technology Data Exchange (ETDEWEB)

Bae, Hong-Sub; Kim, Chan; Rhee, Il-Su [Kyungpook National University, Daegu (Korea, Republic of); Jo, Hyun-Jun; Kim, Dae-Hwan [Daegu Gyeongbuk Institute of Science and Technology, Daegu (Korea, Republic of); Hong, Sung-Wook [Daegu University, Gyeongsan (Korea, Republic of)

2014-11-15

An anti-reflection (AR) layer of Teflon AF was deposited on the front surface of a Cu(In,Ga)Se{sub 2} (CIGS) solar cell with a structure of grid/TCO/ZnO/CdS/Cu(In,Ga)Se{sub 2}/Mo/glass by using the spin coating method. This AR layer reduced the front-surface reflection, which resulted in high efficiency for the CIGS solar cell. The thickness of the Teflon AF layer was varied to determine the thickness that gave the highest transmittance of incident light into the active absorber of the CIGS solar cell. The optimum thickness of the Teflon AF layer was found to be 105 nm. CIGS solar cells with a Teflon AF layer of 105 nm were constructed, and their efficiencies were compared with those of solar cells without a Teflon AF layer. The average increase in the relative efficiency of the solar cells was 2.63% due to the inclusion of an anti-reflection layer of Teflon AF.

Effect of hydrothermal treatment on catalytic activity of amorphous mesoporous Cr2O3–ZrO2 nanomaterials for ethanol oxidation

International Nuclear Information System (INIS)

Mahmoud, Hala R.

2015-01-01

Mesoporous 0.25Cr 2 O 3 –0.75ZrO 2 binary oxide catalysts (CZ-H) with high specific surface areas were successfully synthesized by hydrothermal treatment. The effect of synthesis conditions, such as hydrothermal temperature and time of CZ-H nanomaterials were investigated by X-ray diffraction (XRD), high-resolution transmission electron microscopy (HR-TEM), energy dispersive spectroscopic (EDS), UV–vis diffuse reflectance spectroscopy (DRS) and N 2 adsorption–desorption measurements (BET). The XRD analysis indicated the formation of amorphous materials of binary oxides. The results showed that hydrothermal temperature and time of CZ-H nanomaterials had great influence on the average particle diameter and surface area. Under the optimum synthesis conditions, the best CZ-H nanomaterial synthesized at 210 °C for 3 h (i.e., CZ-H213), presented spherical structure with smallest average particle diameter found to be 1.5 nm and possessed highest surface area of 526.6 m 2 /g. Optical studies by UV–vis spectroscopy for the different CZ-H nanomaterials exhibit slightly blue shift from 3.20 to 3.33 eV due to quantum confined exciton absorption. Moreover, hydrothermal synthesis leads to catalysts with higher surface area and with better acid–base properties than conventional co-precipitation method. Compared to the other nanomaterials, the CZ-H213 catalyst appears to be the best candidate for further application in acid–base catalysis and reusability. - Graphical abstract: Display Omitted - Highlights: • Mesoporous 25%Cr 2 O 3 –75%ZrO 2 catalysts (CZ-H) were prepared by hydrothermal method. • The hydrothermal temperature and time modified the properties of CZ-H nanomaterials. • The best CZ-H nanomaterial synthesized at 210 °C for 3 h (i.e., CZ-H213). • A CZ-H213 nanomaterial had the highest S BET and smallest average particle diameter. • A mesoporous CZ-H213 used as a reusable active catalyst in the ethanol conversion

Alkali passivation mechanism of sol-gel derived TiO2-SiO2 films coated on soda-lime-silica glass substrates

Energy Technology Data Exchange (ETDEWEB)

Matsuda, A; Matsuno, Y; Katayama, S; Tsuno, T [Nippon Steel Glass Co. Ltd., Tokyo (Japan); Toge, N; Minami, T [University of Osaka Prefecture, Osaka (Japan). College of Engineering

1992-09-01

TiO2-SiO2 films prepared by the sol-gel method serves as an effective alkali passivation layer on a soda-lime-silica glass substrate and the film is superior to a sol-gel derived pure SiO2 film from the view point of weathering resistance improvement. To clarify the reason, alkali passivation mechanism of sol-gel derived TiO2-SiO2 glass films with different TiO2 contents coated on a soda-lime-silica glass substrate was studied by SIMS (secondary ion mass spectroscopy) and XPS (X-ray photoelectron spectroscopy) analyses, and compared with the results of a sol-gel derived pure SiO2 film. As a result, the following conclusions were obtained: An increase in TiO2 content in the TiO2 SiO2 film increases the sodium concentration in the film, which was induced by sodium migration from the glass substrate during the heat-treatment. Because of the presence of sodium the TiO2 -SiO2 films serve not as a barrier but as an effective getter of alkali ions and thereby effectively improve the weathering resistance Of the glass substrate. 10 refs., 6 figs.

Water droplet behavior on superhydrophobic SiO2 nanocomposite films during icing/deicing cycles

NARCIS (Netherlands)

Lazauskas, A.; Guobiene, A.; Prosycevas, I.; Baltrusaitis, V.; Grigaliunas, V.; Narmontas, P.; Baltrusaitis, Jonas

2013-01-01

This work investigates water droplet behavior on superhydrophobic (water contact angle value of 162 ± 1°) SiO2 nanocomposite films subjected to repetitive icing/deicing treatments, changes in SiO2 nanocomposite film surface morphology and their non-wetting characteristics. During the experiment,

The improvement of SiO2 nanotubes electrochemical behavior by hydrogen atmosphere thermal treatment

Science.gov (United States)

Spataru, Nicolae; Anastasescu, Crina; Radu, Mihai Marian; Balint, Ioan; Negrila, Catalin; Spataru, Tanta; Fujishima, Akira

2018-06-01

Highly defected SiO2 nanotubes (SiO2-NT) were obtained by a simple sol-gel procedure followed by calcination. Boron-doped diamond (BDD) polycrystalline films coated with SiO2-NT were used as working electrodes and, unexpectedly, cyclic voltammetric experiments have shown that the concentration of both positive and negative defects at the surface is high enough to enable redox processes involving positively charged Ru(bpy)32+/3+ to occur. Conversely, no electrochemical activity was put into evidence for Fe(CN)63-/4- species, most likely as a result of the strong electrostatic repulsion exerted by the negatively charged SiO2 surface. The concentration of surface defects was further increased by a subsequent thermal treatment in a hydrogen atmosphere which, as EIS measurements have shown, significantly promotes Ru(bpy)32+ anodic oxidation. Digital simulation of the voltammetric responses demonstrated that this treatment does not lead to a similar increase of the number of electron-donor sites. It was also found that methanol anodic oxidation at hydrogenated SiO2-NT-supported platinum results in Tafel slopes of 116-220 mV decade-1, comparable to those reported for both conventional PtRu and Pt-oxide catalysts.