  1. Thermomechanical treatment of titanium alloys

    International Nuclear Information System (INIS)

    Khorev, A.K.

    1979-01-01

    The problems of the theory and practical application of thermomechanical treatment of titanium alloys are presented. On the basis of the systematic investigations developed are the methods of thermomechanical treatment of titanium alloys, established are the optimum procedures and produced are the bases of their industrial application with an account of alloy technological peculiarities and the procedure efficiency. It is found that those strengthening methods are more efficient at which the contribution of dispersion hardening prevails over the strengthening by phase hardening

  2. Nitrogen-containing steels and thermomechanical treatment

    International Nuclear Information System (INIS)

    Kaputkina, L.; Prokoshkina, V.G.; Svyazhin, G.

    2004-01-01

    The strengthening of nitrogen-containing corrosion-resistant steels resulting from alloying and thermomechanical treatment have been investigated using X-ray diffraction analysis, light microscopy, hardness measurements and tensile testing. Combined data have been obtained for nitrogen interaction with alloying elements , peculiarities of deformed structure and short-range of nitrogen-containing steels of various structural classes. The higher nitrogen and total alloying element contents, the higher deformation strengthening. Prospects of use the steels with not high nitrogen content and methods of their thermomechanical strengthening are shown. High temperature thermomechanical treatment (HTMT) is very effective for obtaining high and thermally stable constructional strength of nitrogen-containing steels of all classes. The HTMT is most effective if used in a combination with dispersion hardening for aging steels or in the case of mechanically unstable austenitic steels. (author)

  3. Thermo-mechanical treatment of the Cr-Mo constructional steel plates with Nb, Ti and B additions

    International Nuclear Information System (INIS)

    Adamczyk, J.; Opiela, M.

    2002-01-01

    Results of investigations of the influence of parameters of thermomechanical treatment, carried out by rolling with controlled recrystallization, on the microstructure and mechanical properties of Cr-Mo constructional steel with Nb, Ti and B microadditions, destined for the manufacturing of weldable heavy plates, are presented. These plates show a yield point of over 960 MPa after heat treatment. Two variants of thermomechanical treatment were worked out, based on the obtained results of investigations, when rolling a plate 40 mm thick in several passes to a plate 15 mm thick in a temperature range from 1100 to 900 o C. It was found that the lack of complete recrystallization of the austenite in the first rolling variant, leads to localization of plastic deformation in form of shear bands. There exists a segregation of MC-type carbides and alloying elements in these bands, causing a distinctive reduction of the crack resistance of the steel, as also a disadvantageous anisotropy of plastic properties of plate after tempering. For plates rolled under the same conditions, using a retention shield, a nearly three times higher impact energy in - 40 o C was obtained, as also only a slight anisotropy of plastic properties, saving the required mechanical properties. (author)

  4. New Nomenclatures for Heat Treatments of Additively Manufactured Titanium Alloys

    Science.gov (United States)

    Baker, Andrew H.; Collins, Peter C.; Williams, James C.

    2017-07-01

    The heat-treatment designations and microstructure nomenclatures for many structural metallic alloys were established for traditional metals processing, such as casting, hot rolling or forging. These terms do not necessarily apply for additively manufactured (i.e., three-dimensionally printed or "3D printed") metallic structures. The heat-treatment terminology for titanium alloys generally implies the heat-treatment temperatures and their sequence relative to a thermomechanical processing step (e.g., forging, rolling). These designations include: β-processing, α + β-processing, β-annealing, duplex annealing and mill annealing. Owing to the absence of a thermomechanical processing step, these traditional designations can pose a problem when titanium alloys are first produced via additive manufacturing, and then heat-treated. This communication proposes new nomenclatures for heat treatments of additively manufactured titanium alloys, and uses the distinct microstructural features to provide a correlation between traditional nomenclature and the proposed nomenclature.

  5. Strengthening of stable Cr-Ni austenitic stainless steel under thermomechanical treatments

    Science.gov (United States)

    Akkuzin, S. A.; Litovchenko, I. Yu.; Tyumentsev, A. N.

    2017-12-01

    The features of microstructure and mechanical properties of stable austenitic steel after thermomechanical treatment consisted of low-temperature deformation, deformation in the temperature range T = 273-873 K, and subsequent annealing were investigated. It is shown that under such treatment direct (γ → α')- and reverse (α'→γ)-martensitic transformations occur in the steel. As a result of the thermomechanical treatment submicrocrystalline structural states with high density of micro- and nanotwins and localized deformation bands are formed. The strength of the steel in these structural states is several times higher than that in the initial state.

  6. High strength and high electrical conductivity Cu–Cr system alloys manufactured by hot rolling–quenching process and thermomechanical treatments

    International Nuclear Information System (INIS)

    Xia Chengdong; Zhang Wan; Kang Zhanyuan; Jia Yanlin; Wu Yifeng; Zhang Rui; Xu Genying; Wang Mingpu

    2012-01-01

    Highlights: ► HR–Q and thermomechanical treatments are successfully developed to manufacture Cu–Cr system alloys. ► Ordered fcc structure Cr precipitates are considered to be precursors of equilibrium bcc Cr precipitates. ► The Cr precipitates are responsible for the improvement of properties. ► Additions of Zr, Mg and Si bring about significant improvement in properties of Cu–Cr alloy. ► Good properties are ascribed to grain boundary strengthening, strain hardening and precipitation hardening. - Abstract: Cu–Cr system alloy strips were manufactured by an online hot rolling–quenching (HR–Q) process and subsequent thermomechanical treatments. The microstructure and properties of the alloys were investigated by observations of optical microscopy and transmission electron microscopy, and measurements of microhardness and electrical conductivity. The results show that the HR–Q process and thermomechanical treatments are successfully developed to manufacture Cu–Cr system alloy strips with good combinations of strength, conductivity and softening resistance. Ordered fcc structure Cr precipitates, which are decomposed from the thermomechanical treated alloys, are considered to be precursors to the formation of equilibrium bcc Cr precipitates and responsible for the improvement of properties during near peak aging. Small additions of Zr, Mg and Si effectively improve the hardness and softening resistance of Cu–Cr alloy, and slightly reduce the electrical conductivity. The achievement of high strength and high electrical conductivity in the alloys is ascribed to the interactions of grain boundary strengthening, strain hardening and precipitation hardening.

  7. Thermomechanical Treatments on High Strength Al-Zn-Mg(-Cu) Alloys

    National Research Council Canada - National Science Library

    Di Russo, E; Conserva, M; Gatto, F

    1974-01-01

    An investigation was carried out to determine the metallurgical properties of Al-Zn-Mg and Al-Zn-Mg-Cu alloy products processed according to newly developed Final Thermomechanical Treatments (FTMT) of T-AHA type...

  8. Thermomechanical treatment of welded joints of aluminum-lithium alloys modified by scandium

    Science.gov (United States)

    Malikov, A. G.

    2017-12-01

    At present, the aeronautical equipment manufacture involves up-to-date high-strength aluminum alloys of decreased density resulting from the lithium admixture. Various technologies of fusible welding of these alloys are being developed. The paper presents experimental investigations of the optimization of the laser welding of aluminum alloys with the scandium-modified welded joint after thermomechanical treatment. The effect of scandium on the micro- and macrostructure is studied along with strength characteristics of the welded joint. It is found that thermomechanical treatment allows us to obtain the strength of the welded joint 0.89 for the Al-Mg-Li system and 0.99 for the Al-Cu-Li system with the welded joint modified by scandium in comparison with the base alloy after treatment.

  9. Role of grain refinement in hardening of structural steels at preliminary thermomechanical treatment

    International Nuclear Information System (INIS)

    Bukhvalov, A.B.; Grigor'eva, E.V.; Davydova, L.S.; Degtyarev, M.V.; Levit, V.I.; Smirnova, N.A.; Smirnov, L.V.

    1981-01-01

    The hardening mechanism during preliminary thermomechanical treatment with deformation by cold rolling or hydroextrusion is studied on structural 37KhN3M1 and 38KhN3MFA steels. Specimens have been tested on static tension, impact strength and fracture toughness. It is shown that hydroextrusion application instead of rolling does not change the hardening effect of preliminary thermomechanical treatment (PTMT). It is established that the increase of preliminary deformation degree and the use of accelerated short term hardening heating provides a bett er grain refinement and the increase of PTMT hardening effect [ru

  10. Effect of low-temperature thermomechanical treatment on mechanical properties of low-alloying molybdenum alloys with carbide hardening

    International Nuclear Information System (INIS)

    Bernshtejn, L.M.; Zakharov, A.M.; Veller, M.V.

    1978-01-01

    Presented are results of testing low-temperature thermomechanical treatment of low-alloying molybdenum alloys, including quenching from 2100 deg C, 40% deformation by hydroextrusion and aging at the temperature of 1200-1400 deg C. Tensile tests at room temperature with the following processing of results have shown that low-temperature thermomechanical treatment of low-alloying molybdenum alloys of Mo-Zr-C and Mo-Zr-Nb-C systems leads to a significant increase in low-temperature mechanical properties (strength properties - by 30-35%, ductility - by 30-40%) as compared with conventional heat treatment (aging after quenching). The treatment proposed increases resistance to small, as well as large plastic deformations, and leads to a simultaneous rise of strength and plastic properties at all stages of tensile test. Alloying of the Mo-Zr-C system with niobium increases both strength and plastic characteristics as compared with alloys without niobium when testing samples, subjected to low temperature thermomechanical treatment and conventional heat treatment at room temperature

  11. Thermomechanical treatment of austempered ductile iron

    Directory of Open Access Journals (Sweden)

    A. A. Nofal

    2007-11-01

    Full Text Available The production of lightweight ferrous castings with increased strength properties became unavoidable facing the serious challenge of lighter aluminum and magnesium castings. The relatively new ferrous casting alloy ADI offers promising strength prospects, and the thermo-mechanical treatment of ductile iron may suggest a new route for production of thin-wall products. This work aims at studying the influence of thermomechanical treatment, either by ausforming just after quenching and before the onset of austempering reaction or by cold rolling after austempering. In the first part of this work, ausforming of ADI up to 25% reduction in height during a rolling operation was found to add a mechanical processing component compared to the conventional ADI heat treatment, thus increasing the rate of ausferrite formation and leading to a much finer and more homogeneous ausferrite product. The kinetics of ausferrite formation was studied using both metallographic as well as XRD-techniques. The effect of ausforming on the strength was quite dramatic (up to 70% and 50% increase in the yield and ultimate strength respectively. A mechanism involving both a refined microstructural scale and an elevated dislocation density was suggested. Nickel is added to ADI to increase hardenability of thick section castings, while ausforming to higher degrees of deformation is necessary to alleviate the deleterious effect of alloy segregation on ductility. In the second part of this work, the influence of cold rolling (CR on the mechanical properties and structural characteristics of ADI was investigated. The variation in properties was related to the amount of retained austenite (γr and its mechanically induced ransformation. In the course of tensile deformation of ADI, transformation induced plasticity (TRIP takes place, indicated by the increase of the instantaneous value of strain-hardening exponent with tensile strain. The amount of retained austenite was found to

  12. Thermo-mechanical modeling of laser treatment on titanium cold-spray coatings

    Science.gov (United States)

    Paradiso, V.; Rubino, F.; Tucci, F.; Astarita, A.; Carlone, P.

    2018-05-01

    Titanium coatings are very attractive to several industrial fields, especially aeronautics, due to the enhanced corrosion resistance and wear properties as well as improved compatibility with carbon fiber reinforced plastic (CFRP) materials. Cold sprayed titanium coatings, among the others deposition processes, are finding a widespread use in high performance applications, whereas post-deposition treatments are often used to modify the microstructure of the cold-sprayed layer. Laser treatments allow one to noticeably increase the superficial properties of titanium coatings when the process parameters are properly set. On the other hand, the high heat input required to melt titanium particles may result in excessive temperature increase even in the substrate. This paper introduces a thermo-mechanical model to simulate the laser treatment effects on a cold sprayed titanium coating as well as the aluminium substrate. The proposed thermo-mechanical finite element model considers the transient temperature field due to the laser source and applied boundary conditions using them as input loads for the subsequent stress-strain analysis. Numerical outcomes highlighted the relevance of thermal gradients and thermally induced stresses and strains in promoting the damage of the coating.

  13. Research and Progress of Thermomechanical Treatment of Al-Li Alloys

    Directory of Open Access Journals (Sweden)

    WU Xiuliang

    2016-10-01

    Full Text Available The strengthening and toughening mechanism of aluminum lithium alloy treated by thermo-mechanical processing have been summarized, and the effect on the evolution of microstructures, grain structure and precipitation, were discussed and analysed deeply. The precipitation sequence and behavior of the main precipitation phase were modified by the thermo-mechanical processing, stimulating the forming of fine dispersion combined particles of δ',θ"/θ', T1, and S"/S' phases, uniformly distributed in the matrix, which significantly improved the relationships of strength and the plastic toughness, with the inhibiting of broadening of precipitate free zones, and of the precipitation and coarsening of strengthening particles at the grain boundary.The density of solute atom and vacancies significantly raised up after solution treating, and retained as supersaturated solid solution after water quenching, which acted as the driving force for the precipitation during subsequent aging. Pre-deformation and pre-aging significantly increased the density of fine dispersion strengthening particles of δ' and G.P. zones,which uniformly nucleated in the matrix, and the combined strengthening phases of δ',θ"/θ', and T1 were obtained after high temperature second aging, controlling the size and volume fraction of these particles.Refined grain and optimal grain structure were achieved by new and typical thermo-mechanical processing, and the proportion, size, and oriented relationship of main strengthening particles of δ',θ"/θ', and T1 phases were optimized.At last, the research direction of new thermo-mechanical treatment on the large scale rolled plates and hot worked forgings is pointed out, such as age forming, to meet the need of light high performance of new aluminum lithium alloys used for the large aircrafs and heavy lift launch vehicles.

  14. Influence of thermomechanical treatment on microstructure and properties of electroslag remelted Cu–Cr–Zr alloy

    International Nuclear Information System (INIS)

    Kermajani, M.; Raygan, Sh.; Hanayi, K.; Ghaffari, H.

    2013-01-01

    Highlights: • Effect of ESR process on microstructure of Cu–Cr–Zr alloy was investigated. • The hardness, strength and electrical conductivity are sensitive to thermomechanical treatment. • The microstructure of the alloy can be optimized for obtaining the best combination of mechanical and electrical properties. - Abstract: Effect of thermomechanical treatment (TMT) on aging behavior of electroslag remelted Cu–Cr–Zr alloy was investigated. The relationship between microstructure, mechanical and electrical properties was clarified using hardness, tensile and electrical conductivity testing methods and optical and scanning electron microscopy techniques. The results showed that an appropriate processing and aging treatment may improve the properties of the alloy due to the formation of fine, dispersive and coherent precipitates within the matrix. Indeed, the optimum condition for electrical conductivity and mechanical properties was obtained after cold working of 40% followed by aging at 500 °C for 150 min

  15. Influence of thermo-mechanical treatment on the tensile properties of a modified 14Cr–15Ni stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Vijayanand, V.D., E-mail: vdvijayanand@igcar.gov.in; Laha, K.; Parameswaran, P.; Nandagopal, M.; Panneer Selvi, S.; Mathew, M.D.

    2014-10-15

    The titanium modified 14Cr–15Ni austenitic stainless steel is used as clad and wrapper material for fast breeder nuclear reactor. Thermo-mechanical treatments consisting of solution annealing at two different temperatures of 1273 and 1373 K followed by cold-work and thermal ageing have been imparted to the steel to tailor its microstructure for enhancing strength. Tensile tests have been carried out on the thermo-mechanically treated steel at nominal strain rate of 1.6 × 10{sup −4} s{sup −1} over a temperature range of 298–1073 K. The yield stress and the ultimate tensile strength of the steel increased with increase in solution treatment temperature and this has been attributed to the fine and higher density of Ti(C,N) precipitate. Tensile flow behaviour of the steel has been analysed using Ludwigson and Voce constitutive equations. The steel heat treated at higher solution temperature exhibited earlier onset of cross slip during tensile deformation. The rate of recovery at higher test temperatures was also influenced by variations in solution heat treatment temperature. In addition, dynamic recrystallization during tensile deformation at higher temperatures was profound for steel solution heat-treated at lower temperature. The differences in flow behaviour and softening mechanisms during tensile testing of the steel after different heat treated conditions have been attributed to the nature of Ti(C,N) precipitation.

  16. Influence of thermo-mechanical treatment on the tensile properties of a modified 14Cr–15Ni stainless steel

    International Nuclear Information System (INIS)

    Vijayanand, V.D.; Laha, K.; Parameswaran, P.; Nandagopal, M.; Panneer Selvi, S.; Mathew, M.D.

    2014-01-01

    The titanium modified 14Cr–15Ni austenitic stainless steel is used as clad and wrapper material for fast breeder nuclear reactor. Thermo-mechanical treatments consisting of solution annealing at two different temperatures of 1273 and 1373 K followed by cold-work and thermal ageing have been imparted to the steel to tailor its microstructure for enhancing strength. Tensile tests have been carried out on the thermo-mechanically treated steel at nominal strain rate of 1.6 × 10 −4 s −1 over a temperature range of 298–1073 K. The yield stress and the ultimate tensile strength of the steel increased with increase in solution treatment temperature and this has been attributed to the fine and higher density of Ti(C,N) precipitate. Tensile flow behaviour of the steel has been analysed using Ludwigson and Voce constitutive equations. The steel heat treated at higher solution temperature exhibited earlier onset of cross slip during tensile deformation. The rate of recovery at higher test temperatures was also influenced by variations in solution heat treatment temperature. In addition, dynamic recrystallization during tensile deformation at higher temperatures was profound for steel solution heat-treated at lower temperature. The differences in flow behaviour and softening mechanisms during tensile testing of the steel after different heat treated conditions have been attributed to the nature of Ti(C,N) precipitation

  17. Dual-phase ULCB steels thermomechanically processed

    International Nuclear Information System (INIS)

    Lis, A.K.; Lis, J.

    2001-01-01

    The design philosophy of the processing of dual-phase (D-P) ultra low carbon steels (ULCB) by thermomechanical treatment has been briefly discussed. Modelling of the structure evolution during thermomechanical rolling of ULCB steel was based upon the established empirical equations for yield flow at different conditions of: deformation temperatures, strain rates and stresses for applied amount of deformation during hot deformation compression tests. The critical amount of deformation needed for the occurrence of dynamic or static recrystallization was determined. The dependence of grain refinement of the acicular bainitic and polygonal ferrite of the accelerated cooling and amount of stored energy of deformation in steel has been evaluated. Effect of the decreasing of the finishing temperature of thermomechanical processing on the increase of the impact toughness of dual-phase microstructure consisted of the bainitie-martensite islands in the ferrite matrix has been shown. The effect of ageing process after thermomechanical rolling of heavy plates on fracture toughness values of J 0.2 for ULCB-Ni steels has been established from cod tests measurements. New low cost technology of rolling of ULCB steels dual-phase is proposed. (author)

  18. EFFECT OF THERMO-MECHANICAL TREATMENT ON PROPERTIES OF PARICA PLYWOODS (Schizolobium amazonicum Huber ex Ducke

    Directory of Open Access Journals (Sweden)

    Mírian de Almeida Costa

    Full Text Available ABSTRACT Thermo-mechanical treatment is a technique for wood modification in which samples are densified by means of heat and mechanical compression, applied perpendicularly to fibers, which under different combinations of time, temperature, and pressure increases wood density and thus improve some of its properties. This study aimed to treat thermo-mechanically parica plywood and observe the effects on its physical and mechanical properties. Specimens were submitted to two treatments, 120 and 150 ºC, remaining under pressure for seven minutes and, subsequently, under zero pressure for 15 minutes. Results showed a significant increase in specific mass from 0.48 g cm-3 to an average of 0.56 g cm-3, and a compression ratio of about 31.7% on average. Physical properties also varied significantly and results showed that treated samples swelled and absorbed more water than those untreated, leading to a greater thickness non-return rate. This indicates the proposed thermal treatments did not release the internal compressive stress generated during panel pressing, not improving its dimensional stability as a result. On the other hand, mechanical properties were positively affected, leading to an increase of 27.5% and 51.8% in modulus of rupture after treatments at 120 and 150 ºC, respectively. Modulus of elasticity and glue-line shear strength did not vary statistically and Janka hardness was 29.7% higher after treatment at 150 ºC.

  19. Effect of thermo-mechanical treatments on the microstructure and mechanical properties of an ODS ferritic steel

    International Nuclear Information System (INIS)

    Oksiuta, Z.; Mueller, P.; Spaetig, P.; Baluc, N.

    2011-01-01

    The Fe-14Cr-2W-0.3Ti-0.3Y 2 O 3 oxide dispersion strengthened (ODS) reduced activation ferritic (RAF) steel was fabricated by mechanical alloying of a pre-alloyed, gas atomised powder with yttria nano-particles, followed by hot isostatic pressing and thermo-mechanical treatments (TMTs). Two kinds of TMT were applied: (i) hot pressing, or (ii) hot rolling, both followed by annealing in vacuum at 850 deg. C. The use of a thermo-mechanical treatment was found to yield strong improvement in the microstructure and mechanical properties of the ODS RAF steel. In particular, hot pressing leads to microstructure refinement, equiaxed grains without texture, and an improvement in Charpy impact properties, especially in terms of the upper shelf energy (about 4.5 J). Hot rolling leads to elongated grains in the rolling direction, with a grain size ratio of 6:1, higher tensile strength and reasonable ductility up to 750 deg. C, and better Charpy impact properties, especially in terms of the ductile-to-brittle transition temperature (about 55 deg. C).

  20. Effect of thermo-mechanical treatments on the microstructure and mechanical properties of an ODS ferritic steel

    Energy Technology Data Exchange (ETDEWEB)

    Oksiuta, Z., E-mail: oksiuta@pb.edu.pl [Bialystok Technical University, Mechanical Department, Wiejska 45c, 15-351 Bialystok (Poland); Mueller, P.; Spaetig, P.; Baluc, N. [Ecole Polytechnique Federale de Lausanne (EPFL), Centre de Recherches en Physique des Plasmas, Association Euratom-Confederation Suisse, 5232 Villigen PSI (Switzerland)

    2011-05-15

    The Fe-14Cr-2W-0.3Ti-0.3Y{sub 2}O{sub 3} oxide dispersion strengthened (ODS) reduced activation ferritic (RAF) steel was fabricated by mechanical alloying of a pre-alloyed, gas atomised powder with yttria nano-particles, followed by hot isostatic pressing and thermo-mechanical treatments (TMTs). Two kinds of TMT were applied: (i) hot pressing, or (ii) hot rolling, both followed by annealing in vacuum at 850 deg. C. The use of a thermo-mechanical treatment was found to yield strong improvement in the microstructure and mechanical properties of the ODS RAF steel. In particular, hot pressing leads to microstructure refinement, equiaxed grains without texture, and an improvement in Charpy impact properties, especially in terms of the upper shelf energy (about 4.5 J). Hot rolling leads to elongated grains in the rolling direction, with a grain size ratio of 6:1, higher tensile strength and reasonable ductility up to 750 deg. C, and better Charpy impact properties, especially in terms of the ductile-to-brittle transition temperature (about 55 deg. C).

  1. Influence of vibrational treatment on thermomechanical response of material under conditions identical to friction stir welding

    Energy Technology Data Exchange (ETDEWEB)

    Konovalenko, Ivan S., E-mail: ivkon@ispms.tsc.ru [Institute of Strength Physics and Materials Science SB RAS, Tomsk, 634055 (Russian Federation); Konovalenko, Igor S., E-mail: igkon@ispms.tsc.ru; Kolubaev, Evgeniy A., E-mail: eak@ispms.tsc.ru [Institute of Strength Physics and Materials Science SB RAS, Tomsk, 634055 (Russian Federation); National Research Tomsk Polytechnic University, Tomsk, 634050 (Russian Federation); Dmitriev, Andrey I., E-mail: dmitr@ispms.tsc.ru [Institute of Strength Physics and Materials Science SB RAS, Tomsk, 634055 (Russian Federation); National Research Tomsk Polytechnic University, Tomsk, 634050 (Russian Federation); National Research Tomsk State University, Tomsk, 634050 (Russian Federation); Psakhie, Sergey G., E-mail: sp@ms.tsc.ru [Institute of Strength Physics and Materials Science SB RAS, Tomsk, 634055 (Russian Federation); National Research Tomsk State University, Tomsk, 634050 (Russian Federation)

    2015-10-27

    A molecular dynamics model was constructed to describe material loading on the atomic scale by the mode identical to friction stir welding. It was shown that additional vibration applied to the tool during the loading mode provides specified intensity values and continuous thermomechanical action during welding. An increase in additional vibration intensity causes an increase both in the force acting on the workpiece from the rotating tool and in temperature within the welded area.

  2. Thermo-mechanical treatment for improvement of superplasticity of SUS304; SUS304 no chososei kyodo kaizen no tame no kako netsu shori

    Energy Technology Data Exchange (ETDEWEB)

    Kato, M.; Torisaka, Y. [Mechanical Engineering Lab., Tokyo (Japan)

    1998-01-25

    Thermo-mechanical treatment was given to improve further the superplastic behavior of SUS 304 stainless steel. In the SUS 304, martensite phase produced by the processing induced transformation may be reversely transformed to the primary austenite phase by high-temperature heating. Crystal grain size is micronized to 1 {mu} m by combining this reverse transformation and recrystallization of the austenite phase. However, the straining rate at that time is as extremely low as 1 times 10 {sup -4}/s or lower, which is insufficient for an industrial material. Therefore, the SUS 304 processed as described above was given again a series of thermo-mechanical treatment of the similar forced cold processing and annealing to ultra-micronize the crystalline particles. Majority of the crystalline particles have come to have a grain size of several hundred nm. This test piece showed a total elongation of 400% or more at a test temperature of 973 K and a straining rate of 1.8 times 10 {sup -3}/s or lower. In addition, the straining rate sensitivity index `m` at that time was 0.45 or higher. The superplastic deformation of the SUS 304 has a high possibility of being governed by dynamic recrystallization. 4 refs., 7 figs., 1 tab.

  3. Effect of Thermomechanical Treatment on the Environmentally Induced Cracking Behavior of AA7075 Alloy

    Science.gov (United States)

    Ghosh, Rahul; Venugopal, A.; Sankaravelayudham, P.; Panda, Rajiv; Sharma, S. C.; George, Koshy M.; Raja, V. S.

    2015-02-01

    The influence of thermomechanical treatment on the stress corrosion cracking behavior of AA7075 aluminum alloy forgings was examined in 3.5% NaCl solution by varying the extent of thermomechanical working imparted to each of the conditions. The results show that inadequate working during billet processing resulted in inferior corrosion and mechanical properties. However, more working with intermediate pre-heating stages also led to precipitation of coarse particles resulting in lowering of mechanical properties marginally and a significant reduction in the general/pitting corrosion resistance. The results obtained in the present study indicate that optimum working with controlled pre-heating levels is needed during forging to achieve the desired properties. It is also demonstrated that AA7075 in the over aged condition does not show any environmental cracking susceptibility in spite of the microstructural variations in terms of size and volume fraction of the precipitates. However, the above microstructural variations definitely affected the pitting corrosion and mechanical properties significantly and hence a strict control over the working and pre-heating stages during billet processing is suggested.

  4. Influence of isothermal thermomechanical treatment on structure and properties of structural steels

    International Nuclear Information System (INIS)

    Smirnov, M.A.; Kaletin, A.Yu.; Schastlivthev, V.M.; Kaletina, Yu.V.

    1997-01-01

    A study is made into the structure and mechanical properties of steel 35KhGSA and 37KhN3A after isothermal hardening resulting in bainitic structure formation as well as after low-temperature thermomechanical treatment (LTTMT) combining the plastic deformation at the temperature of bainitic transformation and subsequent isothermal hardening. It is shown that LTTMT permits and essential enhancement of strength properties in steel 35KhGSA, high plasticity and impact strength being reserved. This is associated with bainitic structure refinement. In steel 37KhN3A the process of carbide formation takes place along with bainitic transformation, and LTTMT results in lesser strengthening. LTTMT is fount to not practically affect the tendency of structural steels to bainitic brittleness. This treatment promotes some shift of brittleness manifestation to lower temperatures

  5. Microstructures and Properties of 40Cu/Ag(Invar) Composites Fabricated by Powder Metallurgy and Subsequent Thermo-Mechanical Treatment

    Science.gov (United States)

    Zhang, Xin; Huang, Yingqiu; Liu, Xiangyu; Yang, Lei; Shi, Changdong; Wu, Yucheng; Tang, Wenming

    2018-03-01

    Composites of 40Cu/Ag(Invar) were prepared via pressureless sintering and subsequent thermo-mechanical treatment from raw materials of electroless Ag-plated Invar alloy powder and electrolytic Cu powder. Microstructures and properties of the prepared composites were studied to evaluate the effect of the Ag layer on blocking Cu/Invar interfacial diffusion in the composites. The electroless-plated Ag layer was dense, uniform, continuous, and bonded tightly with the Invar alloy substrate. During sintering of the composites, the Ag layer effectively prevented Cu/Invar interfacial diffusion. During cold-rolling, the Ag layer was deformed uniformly with the Invar alloy particles. The composites exhibited bi-continuous network structure and considerably improved properties. After sintering at 775 °C and subsequent thermo-mechanical treatment, the 40Cu/Ag(Invar) composites showed satisfactory comprehensive properties: relative density of 99.0 pct, hardness of HV 253, thermal conductivity of 55.7 W/(m K), and coefficient of thermal expansion of 11.2 × 10-6/K.

  6. Effect of thermo-mechanical treatments on creep and fatigue properties of 9% Cr martensitic steels

    International Nuclear Information System (INIS)

    Hollner, S.; Fournier, B.; Le Pendu, J.; Caes, C.; Tournie, I.; Pineau, A.

    2011-01-01

    In the framework of the development of Generation IV nuclear reactors and fusion nuclear reactors, materials with high mechanical properties up to 550 C are required. In service the materials will be subjected to high-temperature creep and cyclic loadings. 9-12%Cr martensitic steels are candidate materials for these applications; however, they show a pronounced cyclic softening effect under cyclic loadings. This softening effect is linked to the coarsening of the martensitic microstructure. In order to refine its microstructure and its precipitation state, the commercial P91 steel has been submitted to a thermo-mechanical treatment including warm-rolling at 600 C and a tempering stage at 700 C. Microstructural observations confirm that this thermo-mechanical treatment led to a finer martensite with smaller MX-type precipitates. This evolution has an effect on the high-temperature mechanical properties: the optimized P91 steel is 100 Hv harder than the as-received P91, and its yield strength is 430 MPa higher at 20 C and 220 MPa higher at 550 C. Its lifetime under creep (at 650 C under 120 MPa) is at least 14 times longer; and the fatigue test at 650 C under 0.7% strain shows a slightly slower cyclic softening effect for the optimized P91. (authors)

  7. Improvement of the shape memory effect of a Fe-Mn-Cr-Si-Ni by original thermomechanical treatments

    International Nuclear Information System (INIS)

    Federzoni, L.; Guenin, G.; Mantel, M.

    1993-01-01

    Among the shape memory alloys, Fe-based have real perspectives of industrial development. However, to acquire a good shape memory effect, these alloys must undergo a thermomechanical treatment. For applcation perspective this treatment must be the simpliest as possible. In this paper, two types of treatment have been performed, based of the fact that : - the formation of the martensite ε, responsible for the shape memory effect, is sensitive to the microstructure - its reversibility is the best as possible if the austenite is previously hardened by a deformation at high temperature. (orig.)

  8. Mechanical properties of thermomechanical treated hyper-eutectic Al-Si-(Fe, Mn, Cu) materials

    OpenAIRE

    Umezawa, Osamu

    2005-01-01

    Tensile and high-cycle fatigue behavior of thermomechanical treated hyper-eutectic Al-Si-(Fe, Mn, Cu) materials were studied. Through the repeated thermomechanical treatment (RTMT) which is a repeat of the multi steps cold-working followed by heat treatment, Si crystals and/or intermetallic compounds were broken into some fragments and dispersed in the aluminum matrix. Fine dispersion of the second phase particles exhibited good ductility, since early fracture was overcome. A few large Si cry...

  9. Microstructure development during thermomechanical treatment of Al-Mg-Si alloy

    Directory of Open Access Journals (Sweden)

    Martinova Z.

    2002-01-01

    Full Text Available The effect of natural aging and 95% cold deformation on the microstructure evolution and aging characteristics in commercial Al - 1 mass % Mg2Si alloy subjected to thermomechanical treatment (TMT was examined. Transmission electron microscopy observations, tensile tests and electrical conductivity measurements were carried out in order to correlate microstructural features to properties on each TMT step. It was established that pre-aging at room temperature affected the morphology of dislocation structure induced by next cold deformation. The observed transition from cellular to homogenous dislocation distribution was explained by the different stability of zones produced by pre-aging of different duration. Natural aging suppressed recovery processes during post-deformation artificial aging, especially after prolonged storage after quenching and at lower aging temperature. It influenced the morphology of precipitates produced by post deformation artificial aging also. The overall effect of TMT involving prior-deformation natural aging in the scheme, on hardness, tensile properties and electrical conductivity is discussed based on experimental microstruture observations.

  10. Thermomechanical behavior of Fe-Mn-Si-Cr-Ni shape memory alloys modified with samarium

    International Nuclear Information System (INIS)

    Shakoor, R.A.; Khalid, F. Ahmad

    2009-01-01

    The deformation and training behavior of Fe-14Mn-3Si-10Cr-5Ni (wt.%) shape memory alloys containing samarium addition has been studied in the iron-based shape memory alloys. It is noticed that thermomechanical treatment (training) has significant influence on proof stress, critical stress and shape memory behavior of the alloys. The improvement in shape memory behavior can be attributed to the decrease in the proof stress and critical stress which facilitates the formation of ε (hcp martensite). It is also observed that alloy 2 containing samarium undergoes less softening as compared to alloy 1 with training which inhibits the formation of α (bcc martensite) and thus enhances the shape memory behavior. The excessive thermomechanical treatment with increase in the training cycle has led to the formation of α (bcc martensite) along with ε (hcp martensite) in the alloy 1 which appeared to have decline in the shape memory effect. This has been demonstrated by the examination of microstructure and identification of α (bcc martensite) martensite in the alloy 1 as compared to alloy 2

  11. Hydrogen embrittlement of thermomechanically treated 18Ni Maraging steel

    International Nuclear Information System (INIS)

    Munford, J.W.; Rack, H.J.; Kass, W.J.

    1977-01-01

    The influence of thermomechanical treatments on susceptibility to cracking in 100 percent relative humidity air and low pressure (93.3 KPa) gaseous hydrogen has been investigated for 18Ni (350 ksi) Maraging steel. Two thermomechanical treatments were studied, ausforming and marforming and compared with the standard solution treated and aged material. Although little difference exists for the strength and toughness values between these treatments, a two to five-fold increase in the stress intensity threshold for cracking was found for both the ausformed and marformed material. A dramatic difference in cracking kinetics was also apparent as shown by the failure times at comparable stress intensities. Fractographic analysis showed that the primary fracture mode was 100 percent intergranular for the solution treated and aged samples while the ausform and marform failures were predominately quasi-cleavage or intergranular depending on orientation. Finally, permeation and diffusion measurements were conducted on the above materials and these results are correlated with the environmental cracking behavior

  12. Hydrogen embrittlement of thermomechanically treated 18Ni Maraging steel

    Energy Technology Data Exchange (ETDEWEB)

    Munford, J.W.; Rack, H.J.; Kass, W.J.

    1977-01-01

    The influence of thermomechanical treatments on susceptibility to cracking in 100 percent relative humidity air and low pressure (93.3 KPa) gaseous hydrogen has been investigated for 18Ni (350 ksi) Maraging steel. Two thermomechanical treatments were studied, ausforming and marforming and compared with the standard solution treated and aged material. Although little difference exists for the strength and toughness values between these treatments, a two to five-fold increase in the stress intensity threshold for cracking was found for both the ausformed and marformed material. A dramatic difference in cracking kinetics was also apparent as shown by the failure times at comparable stress intensities. Fractographic analysis showed that the primary fracture mode was 100 percent intergranular for the solution treated and aged samples while the ausform and marform failures were predominately quasi-cleavage or intergranular depending on orientation. Finally, permeation and diffusion measurements were conducted on the above materials and these results are correlated with the environmental cracking behavior.

  13. Effect of High-Temperature Thermomechanical Treatment on the Brittle Fracture of Low-Carbon Steel

    Science.gov (United States)

    Smirnov, M. A.; Pyshmintsev, I. Yu.; Varnak, O. V.; Mal'tseva, A. N.

    2018-02-01

    The effect of high-temperature thermomechanical treatment (HTMT) on the brittleness connected with deformation-induced aging and on the reversible temper brittleness of a low-carbon tube steel with a ferrite-bainite structure has been studied. When conducting an HTMT of a low-alloy steel, changes should be taken into account in the amount of ferrite in its structure and relationships between the volume fractions of the lath and the acicular bainite. It has been established that steel subjected to HTMT undergoes transcrystalline embrittlement upon deformation aging. At the same time, HTMT, which suppresses intercrystalline fracture, leads to a weakening of the development of reversible temper brittleness.

  14. Thermomechanical fatigue of shape memory alloys

    International Nuclear Information System (INIS)

    Lagoudas, D C; Kumar, P K; Miller, D A; Rong, L

    2009-01-01

    As shape memory alloys (SMAs) gain popularity as high energy density actuators, one characteristic that becomes particularly important is the thermomechanical transformation fatigue life, in addition to maximum transformation strain and stability of actuation cycles. In this paper, a novel test frame design and testing protocol are discussed, for investigating the thermally activated transformation fatigue characteristics of SMAs under various applied loads for both complete and partial phase transformation. A Ni 50 Ti 40 Cu 10 (at.%) SMA was chosen for this investigation and the effects of various heat treatments on the transformation temperatures and the transformation fatigue lives of actuators were studied. For selected heat treatments, the evolution of recoverable and irrecoverable strains up to failure under different applied stress levels was studied in detail. The influence of complete and partial transformation on the fatigue life is also presented. The irrecoverable strain accumulation as a function of the number of cycles to failure for different stress levels is presented by a relationship similar to the Manson–Coffin law for both partial and complete transformations

  15. Model of mechanical properties change of steel during rolling with use of hightemperature thermomechanical treatment

    International Nuclear Information System (INIS)

    Zhadan, V.T.; Gubenko, V.T.; Bernshtejn, M.L.; Binarskij, M.S.

    1975-01-01

    A mathematical model is proposed of changes in the mechanical properties of the steel-50KHGA in the process of rolling with application of a high-temperature thermomechanical treatment (HTTMT). The model accounts for all the main particularities of the structure formation processes during a high temperature deformation of metals and alloys. The nonmonotonic dependence of the steel mechanical properties on the deformation velocity can be presented as a result of a summary effect of three parallel processes on the formation of these properties: hot working, softening and substructural hardening. The mathematical model has been constructed by the iteration method

  16. Enhancing the ABAQUS Thermomechanics Code to Simulate Steady and Transient Fuel Rod Behavior

    International Nuclear Information System (INIS)

    Williamson, R.L.; Knoll, D.A.

    2009-01-01

    A powerful multidimensional fuels performance capability, applicable to both steady and transient fuel behavior, is developed based on enhancements to the commercially available ABAQUS general-purpose thermomechanics code. Enhanced capabilities are described, including: UO2 temperature and burnup dependent thermal properties, solid and gaseous fission product swelling, fuel densification, fission gas release, cladding thermal and irradiation creep, cladding irradiation growth, gap heat transfer, and gap/plenum gas behavior during irradiation. The various modeling capabilities are demonstrated using a 2D axisymmetric analysis of the upper section of a simplified multi-pellet fuel rod, during both steady and transient operation. Computational results demonstrate the importance of a multidimensional fully-coupled thermomechanics treatment. Interestingly, many of the inherent deficiencies in existing fuel performance codes (e.g., 1D thermomechanics, loose thermo-mechanical coupling, separate steady and transient analysis, cumbersome pre- and post-processing) are, in fact, ABAQUS strengths.

  17. Thermo-mechanical process for treatment of welds

    International Nuclear Information System (INIS)

    Malik, R.K.

    1980-03-01

    Benefits from thermo-mechanical processing (TMP) of austenitic stainless steel weldments, analogous to hot isostatic pressing (HIP) of castings, most likely result from compressive plastic deformation, enhanced diffusion, and/or increased dislocation density. TMP improves ultrasonic inspectability of austenitic stainless steel welds owing to: conversion of cast dendrites into equiaxed austenitic grains, reduction in size and number of stringers and inclusions, and reduction of delta ferrite content. TMP induces structural homogenization and healing of void-type defects and thus contributes to an increase in elongation, impact strength, and fracture toughness as well as a significant reduction in data scatter for these properties. An optimum temperature for TMP or HIP of welds is one which causes negligible grain growth and an acceptable reduction in yield strength, and permits healing of porosity

  18. Effective thermo-mechanical properties and shape memory effect of CNT/SMP composites

    Science.gov (United States)

    Yang, Qingsheng; Liu, Xia; Leng, Fangfang

    2009-07-01

    Shape memory polymer (SMP) has been applied in many fields as intelligent sensors and actuators. In order to improve the mechanical properties and recovery force of SMP, the addition of minor amounts of carbon nanotubes (CNT) into SMP has attracted wide attention. A micromechanical model and thermo-mechanical properties of CNT/SMP composites were studied in this paper. The thermo-mechanical constitutive relation of intellectual composites with isotropic and transversely isotropic CNT was obtained. Moreover, the shape memory effect of CNT/SMP composites and the effect of temperature and the volume fraction of CNT were discussed. The work shows that CNT/SMP composites exhibit excellent macroscopic thermo-mechanical properties and shape memory effect, while both of them can be affected remarkably by temperature and the microstructure parameters.

  19. Thermomechanical Modelling of Friction Stir Welding

    DEFF Research Database (Denmark)

    Hattel, Jesper Henri; Schmidt, Henrik Nikolaj Blicher; Tutum, Cem Celal

    2009-01-01

    Friction Stir Welding (FSW) is a fully coupled thermomechanical process and should in general be modelled as such. Basically, there are two major application areas of thermomechanical models in the investigation of the FSW process: i) Analysis of the thermomechanical conditions such as e.g. heat...... generation and local material deformation (often referred to as flow) during the welding process itself. ii) Prediction of the residual stresses that will be present in the joint structure post to welding. While the former in general will call for a fully-coupled thermomechanical procedure, however...... for the FSW process at hand, the heat generation must either be prescribed analytically or based on a fully coupled analysis of the welding process itself. Along this line, a recently proposed thermal-pseudo-mechanical model is presented in which the temperature dependent yield stress of the weld material...

  20. Effect of ballistic electrons on ultrafast thermomechanical responses of a thin metal film

    International Nuclear Information System (INIS)

    Xiong Qi-lin; Tian Xin

    2017-01-01

    The ultrafast thermomechanical coupling problem in a thin gold film irradiated by ultrashort laser pulses with different electron ballistic depths is investigated via the ultrafast thermoelasticity model. The solution of the problem is obtained by solving finite element governing equations. The comparison between the results of ultrafast thermomechanical coupling responses with different electron ballistic depths is made to show the ballistic electron effect. It is found that the ballistic electrons have a significant influence on the ultrafast thermomechanical coupling behaviors of the gold thin film and the best laser micromachining results can be achieved by choosing the specific laser technology (large or small ballistic range). In addition, the influence of simplification of the ultrashort laser pulse source on the results is studied, and it is found that the simplification has a great influence on the thermomechanical responses, which implies that care should be taken when the simplified form of the laser source term is applied as the Gaussian heat source. (paper)

  1. Protection of type 316 austenitic stainless steel from intergranular stress corrosion cracking by thermo-mechanical treatment

    International Nuclear Information System (INIS)

    Kiuchi, Kiyoshi; Tsuji, Hirokazu; Kondo, Tatsuo

    1980-03-01

    Thermomechanical treatment that causes carbide stabilizing aging of cold worked material followed by recrystallization heating made standard stainless steels highly resistant to intergranular corrosion and stress corrosion cracking in different test environments. After a typical thermal history of simulated welding, several IGSCC susceptibility tests were made. The results showed that the treatment was successful in type 316 steel in wide range of conditions, while type 304 was protected only to a small extent even by closely controlled treatment. Response of the materials to the sensitizing heating in terms of impurity segregation at grain boundaries was also examined by means of microchemical analysis. Advantage of method is that no special care is required in selecting heats of material, so that conventional type 316 is usable by improving the mechanical properties substantially through the treatment. In some optimized cases the mechanical property improvement was typically recognized by the yield strength by about 20% higher at room temperature, compared with the material mill annealed. (author)

  2. Heat treatments and thermomechanical cycling influences on the R-phase in Ti-Ni shape memory alloys

    Directory of Open Access Journals (Sweden)

    Cezar Henrique Gonzalez

    2010-09-01

    Full Text Available This article studies changes observed on the R-phase thermoelastic behavior in a near-equiatomic Ti-Ni shape memory alloy. Three kinds of procedures have been performed: different treatments, thermomechanical cycling under constant loading in shape memory helical springs and thermal cycling in as-treated and trained samples. Several heat treatments were carried out to investigate evolution of the R-phase by differential scanning calorimetry (DSC. A heat treatment was chosen on which R-phase is absent. Shape memory springs were produced and submitted to a training process in an apparatus by tensioning the springs under constant loading. Thermal cycling in DSC was realized in as-treated and trained samples. Several aspects of one-step (B2→B19' and two-steps (B2→R→B19' martensitic transformations and R-phase formation and their evolution during tests were observed and discussed.

  3. Improvement of high-temperature thermomechanical treatment of the rolled section made of VT3-1 alloy

    International Nuclear Information System (INIS)

    Gavze, A.L.; Korostelev, Yu.P.

    2002-01-01

    Changes in mechanical properties and structure are investigated in alloy VT3-1 rods produced with the use of high temperature thermomechanical treatment (HTMT) on their heating and deformation during straightening as well as during preliminary hot deformation of the billets on a helical rolling mill (HRM). It is stated that the straightening at 550-700 deg C with elongation of ∼ 2% results in some decrease of ultimate strength and in essential enhancement of plasticity and impact strength. In a similar manner, preliminary rolling on HRM affects the properties of rods after final heat treatment. It is shown that rod production according to the experimental processing procedure increases the quality of the rods and can be realized when manufacturing rolled products of alloy VT3-1 with the use of HTMT [ru

  4. Thermo-mechanical ratcheting in jointed rock masses

    KAUST Repository

    Pasten, C.

    2015-09-01

    Thermo-mechanical coupling takes place in jointed rock masses subjected to large thermal oscillations. Examples range from exposed surfaces under daily and seasonal thermal fluctuations to subsurface rock masses affected by engineered systems such as geothermal operations. Experimental, numerical and analytical results show that thermo-mechanical coupling can lead to wedging and ratcheting mechanisms that result in deformation accumulation when the rock mass is subjected to a biased static-force condition. Analytical and numerical models help in identifying the parameter domain where thermo-mechanical ratcheting can take place.

  5. Thermo-mechanical ratcheting in jointed rock masses

    KAUST Repository

    Pasten, C.; Garcí a, M.; Santamarina, Carlos

    2015-01-01

    Thermo-mechanical coupling takes place in jointed rock masses subjected to large thermal oscillations. Examples range from exposed surfaces under daily and seasonal thermal fluctuations to subsurface rock masses affected by engineered systems such as geothermal operations. Experimental, numerical and analytical results show that thermo-mechanical coupling can lead to wedging and ratcheting mechanisms that result in deformation accumulation when the rock mass is subjected to a biased static-force condition. Analytical and numerical models help in identifying the parameter domain where thermo-mechanical ratcheting can take place.

  6. Effects of Microstructural Variability on Thermo-Mechanical Properties of a Woven Ceramic Matrix Composite

    Science.gov (United States)

    Goldsmith, Marlana B.; Sankar, Bhavani V.; Haftka, Raphael T.; Goldberg, Robert K.

    2013-01-01

    The objectives of this paper include identifying important architectural parameters that describe the SiC/SiC five-harness satin weave composite and characterizing the statistical distributions and correlations of those parameters from photomicrographs of various cross sections. In addition, realistic artificial cross sections of a 2D representative volume element (RVE) are generated reflecting the variability found in the photomicrographs, which are used to determine the effects of architectural variability on the thermo-mechanical properties. Lastly, preliminary information is obtained on the sensitivity of thermo-mechanical properties to architectural variations. Finite element analysis is used in combination with a response surface and it is shown that the present method is effective in determining the effects of architectural variability on thermo-mechanical properties.

  7. The influence of thermomechanical treatment on the creep behaviour of DIN 1.4970 austenitic stainless steel at 973 K

    International Nuclear Information System (INIS)

    Zahra, A.A.A.; Schroeder, H.

    1981-04-01

    The creep-rupture behaviour of a Type DIN 1.4970 austenitic stainless steel has been investigated at 973 K (700 0 C) in a high vacuum for three conditions of thermomechanical treatment and a wide range of applied stresses. This type of steel is a candidate for use in the German SNR-300 Fast Breeder Reactor where it shall be used after a 13% cold-working treatment and subsequent aging at 1073 K (800 0 C) for 24 hours ( standard condition ). As an alternative, two other conditions were also investigated, namely aged at 1073 K (800 0 C) for 24 hours before the cold-working (condition 2) and cold worked only (condition 1). Because of various experimental efforts in this laboratory and elsewhere to study helium induced embrittlement effects in α-implanted foil specimens, all tests were performed using foil specimens of 105 μm thickness which were solution annealed at 1373 K (1100 0 C) before the above thermomechanical treatments were applied. The rupture lives and the minimum creep rates were found to be highly dependent on the applied stresses. The treatment of condition 1 material yielded a product as strong as the standard condition 3, while the condition 2 material was less creep resistant. Structural changes as well as fractography were followed using metallographic, transmission and scanning electron microscope techniques. Transgranular ductile fracture was clearly observed in all three conditions. TEM investigations showed that dispersive TiC precipitates were present in the matrix of condition 3 material before creep testing contrary to condition 1 and 2 material. In condition 1 the TiC dispersion was already found after short creep times, while no dispersive TiC precipitates were found in condition 2 material in every test condition. (orig.) [de

  8. Effect of thermomechanical treatments on phase distribution and microstructure evolution of a Ti-48Al-2Mn-2Nb alloy

    International Nuclear Information System (INIS)

    Morris, M.A.; Leboeuf, M.

    1995-01-01

    Titanium aluminide alloys based on TiAl offer potential benefits as intermetallics for structural applications due to their low density and attractive properties at high temperature. However, their strength and ductility are very dependent on microstructural morphologies and much research is being devoted to obtaining optimal properties. The large grain sizes and solute segregations associated with conventional castings have forced much of the work to be focused on obtaining finer microstructures, both in terms of grain sizes as well as lamellar spacings. Thermomechanical treatments have been used to produce a large variety of structural morphologies ranging from fully lamellar to duplex and equiaxed and in which the proportion of each phase is also variable. By choosing the correct temperature and strain rate parameters, it may be possible to modify the microstructure by dynamic recrystallization, if during the mechanical process the lamellae of the α 2 phase can be broken down and be used to accelerate the kinetics of nucleation of the new γ grains. The present study has been carried out in order to examine this process and the authors have compared the different refined microstructures that can be obtained by a new thermomechanical process (ELIT pack-rolling) of a Ti-48Al-2Mn-2Nb alloy with respect to those obtained by heat treatments only

  9. Pilot trials of hemicelluloses extraction prior to thermomechanical pulp production: Part 1

    Science.gov (United States)

    Carl Houtman; Eric Horn

    2011-01-01

    Pilot data indicate that wood chip pretreatment with oxalic acid reduced the specific energy required to make thermomechanical pulp. A combined oxalic acid/bisulfite treatment resulted in 21% refiner energy savings and 13% increase in brightness for aspen. A low level of oxalic acid treatment was effective for spruce. Energy savings of 30% was observed with no...

  10. PRELIMINARY STUDY OF PLYWOOD PRODUCED WITH PARICÁ (Schizolobium amazonicum Huber ex Ducke VENEERS MODIFIED BY THERMO-MECHANICAL TREATMENT

    Directory of Open Access Journals (Sweden)

    Larissa Medeiros Arruda

    2011-05-01

    Full Text Available The objective of this preliminary research was to study the effects of thermo-mechanical modification in veneers of Paricá (Schizolobium amazonicum Huber ex Ducke to improve plywood hygroscopicity and mechanical properties. The amount of 24 veneers was used with the dimensions 25 x 25 cm, that were compressed under different times (5, 10 and 15 minutes at 150°C and pressure at 1 N.mm-2, constituting three treatments and one untreated. Plywood were bonded with resorcinol-formaldehyde, glue consumption of 360 g.m-2 at ambient temperature and pressure of 1 N.mm-2 for 10 hours. The samples were evaluated by colorimetric analysis and physical and mechanical properties. Colorimetric analysis showed that there was a darkening of the wood toward the increase of treatment time. The treatment was not efficient in reducing swelling, only reducing absorption of water. The mechanical properties were not significantly affected by the treatment.

  11. Operating experience with the Harwell thermo-mechanical generators

    International Nuclear Information System (INIS)

    Cooke-Yarborough, E.H.

    1980-06-01

    The Stirling-cycle thermo-mechanical generator (TMG) provides small amounts of electrical power continuously over long periods, while requiring much less fuel than other power sources running from hydrocarbon fuel or radio-isotopes. Two of these 25-watt generators, fuelled by propane, have been used to power the UK National Buoy on two successive missions. A total of more than three years experience at sea has now been accumulated. In addition, a 60-watt version has provided the power for a major lighthouse for more than a year. An early development version of the Thermo-mechanical Generator, adapted to run from the heat of a radio-isotope source, was loaded with strontium 90 titanate in October 1974 and has run continuously in the laboratory ever since. The improvements and changes found necessary in the course of 90,000 generator-hours of running time are described, and the improvements in operational performance and reliability which have resulted are outlined. (author)

  12. Mechanical and Tribological Characteristics of the AMC, Prepared by P/M Route along with Thermo-Mechanical Treatment

    Science.gov (United States)

    Mohapatra, Sambit Kumar; Maity, Kalipada; Bhuyan, Subrat Kumar; Prasad Satpathy, Mantra

    2018-03-01

    Thermo mechanical treatments have the ameliorated impacts on the mechanical and tribological properties of powder metallurgy components. In this investigation an aluminium matrix composite (AMC) {Al (92) + Mg (5) + Gr (1) + Ti (2)} has been prepared by following powder metallurgy technique, with double axial compaction and ulterior sintering. Secondary thermo-mechanical treatment i.e. hot extrusion through mathematical contoured cosine profiled die was considered. The die causes minimum velocity relative differences across the extrusion exit cross-section, which provides smooth material flow. Comparative result analysis for the mechanical and tribological characteristics of the specimen before and after extrusion was concentrated. Extrusion engenders significant amount of improvements of the properties those are attributed to excellent bond strength and uniform density distribution due to high compressive stress. Oxidative and delaminated wear mechanisms were found predominating type. To furnish the suitable explanation scanning electron microscopies have been performed for the wear surfaces.

  13. Theoretical approach to the WWER core thermomechanical modelling

    International Nuclear Information System (INIS)

    Likhatchev, Y.; Troyanov, V.; Folomeev, V.; Demishonkov, A.

    2003-01-01

    The paper presents studies on the analysis of root causes of fuel assembly bowing under operating conditions; developing of a methodology for fuel assemblies thermomechanical simulation; developing of a calculation technique for thermomechanical modelling of the fuel assemblies bowing in operational conditions. Some examples of calculation results are given

  14. Study of cast and thermo-mechanically strengthened chromium-nickel nitrogen-containing steel

    International Nuclear Information System (INIS)

    Prokoshkina, V.G.; Kaputkina, L.M.; Svyazhin, A.G.

    2000-01-01

    The effect of nitrogen on the structure and strength of corrosion-resistant chromium-nickel steels after thermal and thermomechanical treatment is studied. The 06Kh15N7AD and 07Kh15N7DAMB steels alloying by nitrogen was accomplished through the basic composition steels remelting in the molecular nitrogen atmosphere under the pressure of 0.1-2.5 MPa. The 02Kh15N5DAF and 05Kh15N5DAM steels ingots were obtained through melting in a plasma furnace under the nitrogen pressure of 0.4MPA. The high-temperature thermomechanical treatment (HTMT) was performed by rolling with preliminary blanks heating up to 1050 deg C and the rolling end temperature not below 950 deg C. It is shown, that the HTMT of the nitrogen-containing steels makes it possible to obtain strength characteristics by 1.5 times exceeding the properties of traditionally applicable corrosion-resistant steels, whereby sufficiently high plasticity of the nitrogen-containing steel is retained [ru

  15. THERMO-MECHANICALLY PROCESSED ROLLED WIRE FOR HIGH-STRENGTH ON-BOARD WIRE

    Directory of Open Access Journals (Sweden)

    V. A. Lutsenko

    2011-01-01

    Full Text Available It is shown that at twisting of wire of diameter 1,83 mm, produced by direct wire drawing of thermomechanically processed rolled wire of diameter 5,5 mm of steel 90, metal stratification is completely eliminated at decrease of carbon, manganese and an additional alloying of chrome.

  16. Thermomechanical analysis of an electrically assisted wire drawing process

    OpenAIRE

    Sánchez Egea, Antonio José; González Rojas, Hernan Alberto; Celentano, Diego Javier; Jorba Peiró, Jordi; Cao, Jia

    2017-01-01

    Electrically-assisted wire drawing process is a hybrid manufacturing process characterized by enhancement of the formability, ductility and elongation of the wire drawn specimen. A thermomechanical model to describe the change of the mechanical response due to the thermal contribution is proposed in this work. Additionally, a numerical simulation was conducted to study the potential and limitations of this hybrid process by using two different hardening laws: a phenomenological and a dislocat...

  17. Non-destructive thermo-mechanical behavior assessment of glass-ceramics for dental applications

    Science.gov (United States)

    Kordatos, E. Z.; Abdulkadhim, Z.; Feteira, A. M.

    2017-05-01

    Every year millions of people seek dental treatment to either repair damaged, unaesthetic and dysfunctional teeth or replace missing natural teeth. Several dental materials have been developed to meet the stringent requirements in terms of mechanical properties, aesthetics and chemical durability in the oral environment. Glass-ceramics exhibit a suitable combination of these properties for dental restorations. This research is focused on the assessment of the thermomechanical behavior of bio-ceramics and particularly lithium aluminosilicate glass-ceramics (LAS glass-ceramics). Specifically, methodologies based on Infrared Thermography (IRT) have been applied in order the structure - property relationship to be evaluated. Non-crystallized, partially crystallized and fully crystallized glass-ceramic samples have been non-destructively assessed in order their thermo-mechanical behavior to be associated with their micro-structural features.

  18. Influence of initial thermomechanical treatment on high temperature properties of laves phase strengthened ferritic steels

    International Nuclear Information System (INIS)

    Talik, Michal

    2016-01-01

    The aim of this work was to design 17 wt%Cr Laves phase strengthened HiperFer (High performance Ferrite) steels and evaluate their properties. This class of steel is supposed to be used in Advanced Ultra Super Critical power plants. Such cycles exhibit higher efficiency and are environmentally friendly, but improved materials with high resistance to reside/steam oxidation and sufficient creep strength are required. The work focused on the characterization of creep properties of 17Cr2.5W0.5Nb0.25Si heat resistant steel. Small batches of steels with nominal compositions of 17Cr3W0.5Nb0.25Si and 17Cr3W0.9Nb0.25Si were used to analyze the influence of chemical composition on the precipitation behaviour in comparison to 17Cr2.5W0.5Nb0.25Si steel. Creep strength of HiperFer steels is ensured by ne dispersion of thermodynamically stable Laves phase particles, while maintaining high corrosion resistance by a relatively high chromium content. Design of HiperFer steels was accomplished by thermodynamic modeling (Thermocalc) with the main tasks of elimination of the unwelcome brittle (Fe,Cr)-σ phase and maximization of the content of the strengthening C14 Fe_2Nb type Laves phase particles. Long term annealing experiments of all HiperFer steels were performed at 650 C in order to evaluate the role of chemical composition and initial thermo-mechanical treatment state on precipitation behaviour. Laves phase particles formed quickly after few hours and the size of precipitates did not change significantly within 1,000 hours. The observed development of Laves phase particles was compared with thermodynamical calculations (TC-Prisma). The creep properties of 17Cr2.5W0.5Nb0.25Si steel in different initial thermo-mechanical treatment states were tested at 650 C. The influence of different cold rolling procedures, and heat treatments was investigated. Increased cold rolling deformation had a positive effect resulting not only from work hardening, but from the acceleration of Laves

  19. Concurrent material-fabrication optimization of metal-matrix laminates under thermo-mechanical loading

    Science.gov (United States)

    Saravanos, D. A.; Morel, M. R.; Chamis, C. C.

    1991-01-01

    A methodology is developed to tailor fabrication and material parameters of metal-matrix laminates for maximum loading capacity under thermomechanical loads. The stresses during the thermomechanical response are minimized subject to failure constrains and bounds on the laminate properties. The thermomechanical response of the laminate is simulated using nonlinear composite mechanics. Evaluations of the method on a graphite/copper symmetric cross-ply laminate were performed. The cross-ply laminate required different optimum fabrication procedures than a unidirectional composite. Also, the consideration of the thermomechanical cycle had a significant effect on the predicted optimal process.

  20. PWR fuel thermomechanics

    International Nuclear Information System (INIS)

    Traccucci, R.; Leclercq, J.

    1986-01-01

    Fuel thermo-mechanics means the studies of mechanical and thermal effects, and more generally, the studies of the behavior of the fuel assembly under stresses including thermal and mechanical loads, hydraulic effects and phenomena induced by materials irradiation. This paper describes the studies dealing with the fuel assembly behavior, first in normal operating conditions, and then in accidental conditions. 43 refs [fr

  1. Enhancement of the electrochemical behaviour and biological performance of Ti–25Ta–5Zr alloy by thermo-mechanical processing

    Energy Technology Data Exchange (ETDEWEB)

    Cimpean, Anisoara [Department of Biochemistry and Molecular Biology, University of Bucharest, Spl. Independentei, 91-95, 050095 Bucharest (Romania); Vasilescu, Ecaterina; Drob, Paula [Department of Electrochemistry and Corrosion, Institute of Physical Chemistry “Ilie Murgulescu” of Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania); Cinca, Ion, E-mail: ion_cinca@hotmail.com [Faculty of Material Science and Engineering, Politehnica University, Spl. Independentei 313, 060042 Bucharest (Romania); Vasilescu, Cora; Anastasescu, Mihai [Department of Electrochemistry and Corrosion, Institute of Physical Chemistry “Ilie Murgulescu” of Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania); Mitran, Valentina [Department of Biochemistry and Molecular Biology, University of Bucharest, Spl. Independentei, 91-95, 050095 Bucharest (Romania); Drob, Silviu Iulian [Department of Electrochemistry and Corrosion, Institute of Physical Chemistry “Ilie Murgulescu” of Romanian Academy, Spl. Independentei 202, 060021 Bucharest (Romania)

    2014-05-01

    A new Ti–25Ta–5Zr alloy based only on non-toxic and non-allergic elements was elaborated in as-cast and thermo-mechanical processed, recrystallized states (XRD and SEM) in order to be used as candidate material for implant applications. Its long-term interactions with Ringer–Brown and Ringer solutions of different pH values and its cytocompatibility were determined. The thermo-mechanically processed alloy has nobler electrochemical behaviour than as-cast alloy due to finer microstructure obtained after the applied treatment. Corrosion and ion release rates presented the lowest values for the treated alloy. Nyquist and Bode plots displayed higher impedance values and phase angles for the processed alloy, denoting a more protective passive film. SEM micrographs revealed depositions from solutions that contain calcium, phosphorous and oxygen ions (EDX analysis), namely calcium phosphate. An electric equivalent circuit with two time constants was modelled. Cell culture experiments with MC3T3-E1 pre-osteoblasts demonstrated that thermo-mechanically processed Ti–25Ta–5Zr alloy supports a better cell adhesion and spreading, and enhanced cell proliferation. Altogether, these data indicate that thermo-mechanical treatment endows the alloy with improved anticorrosion and biological performances. - Highlights: • Ti–25Ta–5Zr alloy exhibited noble electrochemical, passive behaviour in simulated biofluids. • An electric equivalent circuit with two time constants was modelled. • Corrosion rates show the lowest values for the recrystallized Ti–25Ta–5Zr alloy. • In vitro tests revealed good cytocompatibility of as-cast and processed alloy. • Recrystallized treatment endows the alloy with superior biological performances.

  2. Enhancement of the electrochemical behaviour and biological performance of Ti–25Ta–5Zr alloy by thermo-mechanical processing

    International Nuclear Information System (INIS)

    Cimpean, Anisoara; Vasilescu, Ecaterina; Drob, Paula; Cinca, Ion; Vasilescu, Cora; Anastasescu, Mihai; Mitran, Valentina; Drob, Silviu Iulian

    2014-01-01

    A new Ti–25Ta–5Zr alloy based only on non-toxic and non-allergic elements was elaborated in as-cast and thermo-mechanical processed, recrystallized states (XRD and SEM) in order to be used as candidate material for implant applications. Its long-term interactions with Ringer–Brown and Ringer solutions of different pH values and its cytocompatibility were determined. The thermo-mechanically processed alloy has nobler electrochemical behaviour than as-cast alloy due to finer microstructure obtained after the applied treatment. Corrosion and ion release rates presented the lowest values for the treated alloy. Nyquist and Bode plots displayed higher impedance values and phase angles for the processed alloy, denoting a more protective passive film. SEM micrographs revealed depositions from solutions that contain calcium, phosphorous and oxygen ions (EDX analysis), namely calcium phosphate. An electric equivalent circuit with two time constants was modelled. Cell culture experiments with MC3T3-E1 pre-osteoblasts demonstrated that thermo-mechanically processed Ti–25Ta–5Zr alloy supports a better cell adhesion and spreading, and enhanced cell proliferation. Altogether, these data indicate that thermo-mechanical treatment endows the alloy with improved anticorrosion and biological performances. - Highlights: • Ti–25Ta–5Zr alloy exhibited noble electrochemical, passive behaviour in simulated biofluids. • An electric equivalent circuit with two time constants was modelled. • Corrosion rates show the lowest values for the recrystallized Ti–25Ta–5Zr alloy. • In vitro tests revealed good cytocompatibility of as-cast and processed alloy. • Recrystallized treatment endows the alloy with superior biological performances

  3. PECULIARITIES OF FORMATION OF STRUCTURE AND PROPERTIES AT THERMO-MECHANICAL PROCESSING OF ROLLED WIRE OF NICKEL

    OpenAIRE

    V. A. Lutsenko

    2012-01-01

    There are results of researches of the mechanical properties and structure of the wire rod made of low-carbon nickel molybdenum steel after reduction to toughness thermomechanical treatment in the stream of high-speed wire mill.

  4. Effect of Nb2O5 doping on improving the thermo-mechanical stability of sealing interfaces for solid oxide fuel cells.

    Science.gov (United States)

    Zhang, Qi; Du, Xinhang; Tan, Shengwei; Tang, Dian; Chen, Kongfa; Zhang, Teng

    2017-07-13

    Nb 2 O 5 is added to a borosilicate sealing system to improve the thermo-mechanical stability of the sealing interface between the glass and Fe-Cr metallic interconnect (Crofer 22APU) in solid oxide fuel cells (SOFCs). The thermo-mechanical stability of the glass/metal interface is evaluated experimentally as well as by using a finite element analysis (FEA) method. The sealing glass doped with 4 mol.% Nb 2 O 5 shows the best thermo-mechanical stability, and the sealing couple of Crofer 22APU/glass/GDC (Gd 0.2 Ce 0.8 O 1.9 ) remains intact after 50 thermal cycles. In addition, all sealing couples show good joining after being held at 750 °C for 1000 h. Moreover, the possible mechanism on the thermo-mechanical stability of sealing interface is investigated in terms of stress-based and energy-based perspectives.

  5. PECULIARITIES OF FORMATION OF STRUCTURE AND PROPERTIES AT THERMO-MECHANICAL PROCESSING OF ROLLED WIRE OF NICKEL

    Directory of Open Access Journals (Sweden)

    V. A. Lutsenko

    2012-01-01

    Full Text Available There are results of researches of the mechanical properties and structure of the wire rod made of low-carbon nickel molybdenum steel after reduction to toughness thermomechanical treatment in the stream of high-speed wire mill.

  6. Adjoint sensitivity analysis of the thermomechanical behavior of repositories

    International Nuclear Information System (INIS)

    Wilson, J.L.; Thompson, B.M.

    1984-01-01

    The adjoint sensitivity method is applied to thermomechanical models for the first time. The method provides an efficient and inexpensive answer to the question: how sensitive are thermomechanical predictions to assumed parameters. The answer is exact, in the sense that it yields exact derivatives of response measures to parameters, and approximate, in the sense that projections of the response fo other parameter assumptions are only first order correct. The method is applied to linear finite element models of thermomechanical behavior. Extensions to more complicated models are straight-forward but often laborious. An illustration of the method with a two-dimensional repository corridor model reveals that the chosen stress response measure was most sensitive to Poisson's ratio for the rock matrix

  7. First-principles study of thermal expansion and thermomechanics of single-layer black and blue phosphorus

    International Nuclear Information System (INIS)

    Sun, Hongyi; Liu, Gang; Li, Qingfang; Wan, X.G.

    2016-01-01

    The linear thermal expansion coefficients (LTEC) and thermomechanics of single-layer black and blue phosphorus are systematically studied using first-principles based on quasiharmonic approximation. We find the thermal expansion of black phosphorus is very anisotropic. The LTEC along zigzag direction has a turning from negative to positive at around 138 K, while the LTEC along armchair direction is positive (except below 8 K) and about 2.5 times larger than that along zigzag direction at 300 K. For blue phosphorus, the LTEC is negative in the temperature range from 0 to 350 K. In addition, we find that the Young's modulus and Poisson's ratio of black phosphorus along zigzag direction are 4 to 5 times larger than those along armchair direction within considered temperature range, showing a remarkable anisotropic in-plane thermomechanics property. The mechanisms of these peculiar thermal properties are also explored. This work provides a theoretical understanding of the thermal expansion and thermomechanics of this single layer phosphorus family, which will be useful in nanodevices. - Highlights: • The thermal properties of black and blue phosphorus are studied. • Black phosphorus shows remarkable anisotropic thermal expansion and thermomechanics properties. • Blue phosphorus shows novel negative thermal expansion. • The thermal expansion properties are well analyzed by grüneisen theory.

  8. Structural mechanisms of high-temperature shape changes in titanium-nickel alloys after low-temperature thermomechanical treatment

    International Nuclear Information System (INIS)

    Prokoshkin, S.D.; Turenne, S.; Khmelevskaya, I.Yu.; Brailovski, V.; Trochu, F.

    2000-01-01

    High-Temperature Shape Memory Effect (HTSME) in Ti-Ni alloys and corresponding structural and internal stress changes were studied using dilatometry, in situ electron microscope and X-ray diffractometry. The HTSME induced by the Low Temperature Thermomechanical Treatment (LTMT) consists of two stages. The temperature range of the first stage is limited to 250 o C, while the second stage extends to 400-500 o C. The first stage is caused by the oriented reverse martensite transformation. The heterogeneous residual stress field causes a different thermal stability for the different martensite orientations. During the reverse transformation an anisotropic shift of martensite and austenite X-ray lines is observed that can be due to a relaxation of the orientated stresses and to changes in the martensite lattice. The second stage of HTSME is caused by internal stress relaxation during recovery and polygonization of austenite that are not typical shape memory mechanisms. The possible reasons for the martensite stabilization induced by LTMT will be discussed. (author)

  9. A 1D thermomechanical network transition constitutive model coupled with multiple structural relaxation for shape memory polymers

    Science.gov (United States)

    Zeng, Hao; Xie, Zhimin; Gu, Jianping; Sun, Huiyu

    2018-03-01

    A new thermomechanical network transition constitutive model is proposed in the study to describe the viscoelastic behavior of shape memory polymers (SMPs). Based on the microstructure of semi-crystalline SMPs, a new simplified transformation equation is proposed to describe the transform of transient networks. And the generalized fractional Maxwell model is introduced in the paper to estimate the temperature-dependent storage modulus. In addition, a neo-KAHR theory with multiple discrete relaxation processes is put forward to study the structural relaxation of the nonlinear thermal strain in cooling/heating processes. The evolution equations of the time- and temperature-dependent stress and strain response are developed. In the model, the thermodynamical and mechanical characteristics of SMPs in the typical thermomechanical cycle are described clearly and the irreversible deformation is studied in detail. Finally, the typical thermomechanical cycles are simulated using the present constitutive model, and the simulation results agree well with the experimental results.

  10. Thermo-mechanical properties of SOFC components investigated by a combined method

    DEFF Research Database (Denmark)

    Teocoli, Francesca; Esposito, Vincenzo; Ramousse, Severine

    , and differential thermo-mechanical behavior at each layer. The combination of such factors can have a critical effect on the final shape and microstructure, and on the mechanical integrity. Thermo-mechanical properties and sintering mechanisms of important SOFC materials (CGO, YSZ, ScYSZ) were systematically...

  11. Microstructure evolution and mechanical properties of T15 high speed steel prepared by twin-atomiser spray forming and thermo-mechanical processing

    International Nuclear Information System (INIS)

    Zhang, Guoqing; Yuan, Hua; Jiao, Dongling; Li, Zhou; Zhang, Yong; Liu, Zhongwu

    2012-01-01

    Spray formed T15 high speed steel (HSS) billets were deposited using a state-of-the-art twin-atomiser spray forming facility. The effects of post thermo-mechanical processing (hot isostatic pressing and hot forging) and heat treatment on the microstructure and mechanical properties were investigated. As-deposited billet has a density over 99.3% of the theoretical value and no measurable macro-segregation was observed. The microstructure consists of the equiaxed grains with mean size of ∼18 μm and MC- and M 6 C-type carbides non-uniformly distributed inside the grains and along the grain boundaries. After optimal thermo-mechanical processing and heat treatment, the microstructure was composed of equiaxed fine tempered martensites, and refined M 6 C and MC spherical carbides particles uniformly distributed along the grain boundaries and inside the grains. The hardness reached HRC68 after thermo-mechanical processing, and the corresponding impact toughness and bending strength reached 27 J/cm 2 and 4600 MPa respectively. Although HIP cannot increase the bending strength significantly, it can effectively improve the impact toughness through refining and globurizing carbides.

  12. Introduction to nonlinear thermomechanics of solids

    CERN Document Server

    Kleiber, Michał

    2016-01-01

    The first part of this textbook presents the mathematical background needed to precisely describe the basic problem of continuum thermomechanics. The book then concentrates on developing governing equations for the problem dealing in turn with the kinematics of material continuum, description of the state of stress, discussion of the fundamental conservation laws of underlying physics, formulation of initial-boundary value problems and presenting weak (variational) formulations. In the final part the crucial issue of developing techniques for solving specific problems of thermomechanics is addressed. To this aim the authors present a discretized formulation of the governing equations, discuss the fundamentals of the finite element method and develop some basic algorithms for solving algebraic and ordinary differential equations typical of problems on hand. Theoretical derivations are followed by carefully prepared computational exercises and solutions.

  13. Efficient thermo-mechanical generation of electricity from the heat of radioisotopes

    International Nuclear Information System (INIS)

    Cooke-Yarborough, E.H.; Yeats, F.W.

    1975-01-01

    The thermomechanical generator uses a thermomechanical oscillator to convert heat efficiently into a mechanical oscillation which in turn excites a suitable transducer to generate alternating electricity. The thermomechanical oscillator used is based on the Stirling cycle, but avoids the need for rotary motion and for sliding pistons by having a mechanically-resonant, spring-suspended displacer, and by using an oscillating metal diaphragm to provide the mechanical output. The diaphragm drives an alternator consisting of a spring-suspended permanent magnet oscillating between fixed pole pieces which carry the electrical power output windings. Because a thermomechanical generator is much more efficient than a thermo-electric generator at comparable temperatures, it is particularly suitable for use with a radioisotope heat source. The amounts of radioisotope and of shielding required are both greatly reduced. A machine heated by radioisotopes and delivering 10.7W ac at 80Hz began operating in October, 1974. Operating experience with this machine is reported, and these results, together with those obtained with higher-powered machines heated by other means, are used to calculate characteristics and performance of thermo-mechanical radioisotope generators capable of using heat sources such as the waste-management 90 Sr radioisotope sources becoming available from the US nuclear waste management programme. A design to use one of these heat sources in a 52-W underwater generator is described

  14. Thermo-mechanical response and fatigue behavior of shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Kusagawa, Masaki; Asada, Yasuhide; Nakamura, Toshiya [Tokyo Univ. (Japan). Dept. of Mechanical Engineering

    1998-11-01

    Mechanical, thermo-mechanical and fatigue behaviors of Ni-Ti-Nb shape memory alloy (SMA) have been studied to prepare material data for a design purpose. Presented are testing devices, testing procedure and test results of monotonic tensile, recovery of inelastic deformation due to post heating (thermo-mechanical recovery) and fatigue for future use of the SMA as a structural material of nuclear incore structures. (orig.)

  15. Thermo-mechanical response and fatigue behavior of shape memory alloy

    International Nuclear Information System (INIS)

    Kusagawa, Masaki; Asada, Yasuhide; Nakamura, Toshiya

    1998-01-01

    Mechanical, thermo-mechanical and fatigue behaviors of Ni-Ti-Nb shape memory alloy (SMA) have been studied to prepare material data for a design purpose. Presented are testing devices, testing procedure and test results of monotonic tensile, recovery of inelastic deformation due to post heating (thermo-mechanical recovery) and fatigue for future use of the SMA as a structural material of nuclear incore structures. (orig.)

  16. Damage mechanisms in PBT-GF30 under thermo-mechanical cyclic loading

    International Nuclear Information System (INIS)

    Schaaf, A.; De Monte, M.; Hoffmann, C.; Vormwald, M.; Quaresimin, M.

    2014-01-01

    The scope of this paper is the investigation of damage mechanisms at microscopic scale on a short glass fiber reinforced polybutylene terephthalate (PBT-GF30) under thermo-mechanical cyclic loading. In addition the principal mechanisms are verified through micro mechanical FE models. In order to investigate the fatigue behavior of the material both isothermal strain controlled fatigue (ISCF) tests at three different temperatures and thermo-mechanical fatigue (TMF) tests were conducted on plain and notched specimens, manufactured by injection molding. The goal of the work is to determine the damage mechanisms occurring under TMF conditions and to compare them with the mechanisms occurring under ISCF. For this reason fracture surfaces of TMF and ISCF samples loaded at different temperature levels were analyzed using scanning electron microscopy. Furthermore, specimens that failed under TMF were examined on microsections revealing insight into both crack initiation and crack propagation. The findings of this investigation give valuable information about the main damage mechanisms of PBT-GF30 under TMF loading and serve as basis for the development of a TMF life estimation methodology

  17. Damage behavior of SnAgCu/Cu solder joints subjected to thermomechanical cycling

    International Nuclear Information System (INIS)

    Xiao, H.; Li, X.Y.; Hu, Y.; Guo, F.; Shi, Y.W.

    2013-01-01

    Highlights: •A creep–fatigue damage model based on CDM was proposed. •Designed system includes load frame, strain measure device and damage test device. •Damage evolution of solder joints was a function of accumulated inelastic strain. •Damage of solder joints is an interaction between creep and low-cycle fatigue. -- Abstract: Thermomechanical fatigue damage is a progressive process of material degradation. The objective of this study was to investigate the damage behavior of SnAgCu/Cu solder joints under thermomechanical cycling. A damage model was proposed based on continuum damage mechanics (CDM). Based upon an analysis of displacements for flip-chip solder joints subjected to thermal cycling, a special bimetallic loading frame with single-solder joint samples was designed to simulate the service conditions of actual joints in electronic packages. The assembly, which allowed for strain measurements of an individual solder joint during temperature cycling, was used to investigate the impact of stress–strain cycling on the damage behavior of SnAgCu/Cu solder joints. The characteristic parameters of the damage model were determined through thermomechanical cycling and strain measurement tests. The damage variable D = 1 − R 0 /R was selected, and values for it were obtained using a four-probe method for the single-solder joint samples every dozen cycles during thermomechanical cycling tests to verify the model. The results showed that the predicted damage was in good agreement with the experimental results. The damage evolution law proposed here is a function of inelastic strain, and the results showed that the damage rate of SnAgCu/Cu solder joints increased as the range of the applied strain increased. In addition, the microstructure evolution of the solder joints was analyzed using scanning electron microscopy, which provided the microscopic explanation for the damage evolution law of SnAgCu/Cu solder joints

  18. Damage behavior of SnAgCu/Cu solder joints subjected to thermomechanical cycling

    Energy Technology Data Exchange (ETDEWEB)

    Xiao, H., E-mail: xiaohui2013@yahoo.com.cn; Li, X.Y.; Hu, Y.; Guo, F.; Shi, Y.W.

    2013-11-25

    Highlights: •A creep–fatigue damage model based on CDM was proposed. •Designed system includes load frame, strain measure device and damage test device. •Damage evolution of solder joints was a function of accumulated inelastic strain. •Damage of solder joints is an interaction between creep and low-cycle fatigue. -- Abstract: Thermomechanical fatigue damage is a progressive process of material degradation. The objective of this study was to investigate the damage behavior of SnAgCu/Cu solder joints under thermomechanical cycling. A damage model was proposed based on continuum damage mechanics (CDM). Based upon an analysis of displacements for flip-chip solder joints subjected to thermal cycling, a special bimetallic loading frame with single-solder joint samples was designed to simulate the service conditions of actual joints in electronic packages. The assembly, which allowed for strain measurements of an individual solder joint during temperature cycling, was used to investigate the impact of stress–strain cycling on the damage behavior of SnAgCu/Cu solder joints. The characteristic parameters of the damage model were determined through thermomechanical cycling and strain measurement tests. The damage variable D = 1 − R{sub 0}/R was selected, and values for it were obtained using a four-probe method for the single-solder joint samples every dozen cycles during thermomechanical cycling tests to verify the model. The results showed that the predicted damage was in good agreement with the experimental results. The damage evolution law proposed here is a function of inelastic strain, and the results showed that the damage rate of SnAgCu/Cu solder joints increased as the range of the applied strain increased. In addition, the microstructure evolution of the solder joints was analyzed using scanning electron microscopy, which provided the microscopic explanation for the damage evolution law of SnAgCu/Cu solder joints.

  19. Thermomechanical behavior of an Fe-based shape memory alloy: transformation conditions and hystereses

    International Nuclear Information System (INIS)

    Tanaka, K.; Nishimura, F.; Tobushi, H.; Oberaigner, E.R.; Fischer, F.D.

    1995-01-01

    Transformation/thermomechanical behavior in an Fe-9%Cr-5%Ni-14%Mn-6%Si polycrystalline shape memory alloy during thermomechanical loading is investigated. The transformation lines in the stress-temperature plane are strongly influenced by the parameters characterizing the thermomechanical loading. The transformation start condition, the martensite start stress and the austenite start temperature, is carefully measured to compare the results with the other experimental and theoretical observations. The stress-strain-temperature hysteresis loops, full and sub, are determined during cyclic loading. (orig.)

  20. Contribution of Brazil nut shell fiber and electron-beam irradiation in thermomechanical properties of HDPE

    International Nuclear Information System (INIS)

    Polato, Pamella; Lorusso, Leandro Alex; Souza, Clecia de Moura; Moura, Esperidiana Augusta Barretos de; Chinellato, Anne; Rosa, Ricardo de

    2010-01-01

    In the present work, the influence of electron-beam irradiation on thermo-mechanical properties of HDPE and HDPE/Brazil nut shell fiber composite was investigated. The materials were irradiated at radiation dose 50 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. The irradiated and non-irradiated samples were submitted to thermo-mechanical tests and the correlation between their properties was discussed. The results showed that the incorporation of Brazil nut shell fiber represented a significant gain (p < 0,05) in tensile strength at break, flexural strength, flexural module, Vicat softening temperature and heat distortion temperature (HDT) properties of the HDPE. In addition, the irradiated HDPE/Brazil nut shell fiber composite presented a significant increase (p < 0.05) in this properties compared with irradiated HDPE. (author)

  1. Thermomechanical behavior of mica layers with lenticular fissures

    Science.gov (United States)

    Yang, Michael Xinyi

    The thermomechanical behavior of natural phlogopite mica specimens from seven different origins is characterized. An initial heat treatment, to a temperature between 300°C and 400°C, is found to form fissures that stabilize in the material. Following the initial heat treatment, all the phlogopite specimens, regardless of their origin and polytype, exhibit the extraordinarily large thermal expansion (intumescence), more than 200% at 600°C, in the direction perpendicular to the basal planes. This phenomenon is strictly reproducible when tested under a range of thermal conditions including thermal shock, multiple thermal fatigue cycles, varying heating or cooling rates and isothermal heating over an extensive period of time at different temperatures up to 585°C. The hysteresis, associated with the thermal cycle, is increased when the specimen is heated or cooled at a faster rate. The maximum coefficient of linear thermal expansion, approximately 10 -2°C-1, is observed over the temperature range 100--120°C. This is due to the non-structural water, entrapped within the layer structure, which undergoes a phase transition and causes the mica layers to expand abruptly. A model of lenticular fissures is developed based on thin-plate mechanics and thermodynamics assumptions. The state of a lenticular fissure with water vapor molecules is determined to correlate the experimental parameters with the material properties. The average density of water vapor molecules within a lenticular fissure is calculated to be ˜1025 m 3 for the temperature interval between 100°C and 275°C. The concentration of non-structure water, based on the model calculation, is less than 0.1% by weight. Acoustic emission (AE) signals have been reported by Pranevicius et al. (1995) to correspond to the microstructure changes as the internal lenticular fissures develop in phlogopite. This technique has also been proven feasible to characterize the thermomechanical behavior of other layer structures

  2. Simulation of thermo-mechanical effect in bulk-silicon FinFETs

    OpenAIRE

    Burenkov, Alex; Lorenz, Jürgen

    2016-01-01

    The thermo-mechanical effect in bulk-silicon FinFETs of the 14 nm CMOS technology node is studied by means of numerical simulation. The electrical performance of such devices is significantly enhanced by the intentional introduction of mechanical stress during the device processing. The thermo-mechanical effect modifies the mechanical stress distribution in active regions of the transistors when they are heated. This can lead to a modification of the electrical performance. Numerical simulati...

  3. Optimization in Friction Stir Welding - With Emphasis on Thermo-mechanical Aspects

    DEFF Research Database (Denmark)

    Tutum, Cem Celal

    combined with classical single-objective and evolutionary multi-objective optimization algorithms (i.e. SQP and NSGA-II), to find the optimum process parameters (heat input, rotational and traverse welding speeds) that would result in favorable thermo-mechanical conditions for the process.......This book deals with the challenging multidisciplinary task of combining variant thermal and thermo-mechanical simulations for the manufacturing process of friction stir welding (FSW) with numerical optimization techniques in the search for optimal process parameters. The FSW process...... is characterized by multiphysics involving solid material flow, heat transfer, thermal softening, recrystallization and the formation of residual stresses. Initially, the thermal models were addressed since they in essence constitute the basis of all other models of FSW. Following this, several integrated thermo-mechanical...

  4. Thermal stress analysis and thermo-mechanical fatigue for gas turbine blade

    International Nuclear Information System (INIS)

    Hyun, J. S.; Kim, B. S.; Kang, M. S.; Ha, J. S.; Lee, Y. S.

    2002-01-01

    The numerical analysis for gas turbine blades were carried out under several conditions by compounding temperature field, velocity field, thermal conduction of blade, and cooling heat transfer. The three types of 1,100 deg. C class 1st-stage gas turbine blades were analyzed. The analysis results are applied to the study on evaluating the remaining life for thermo-mechanical fatigue life. The thermo-mechanical fatigue experiments under out-of-phase and in-phase have been performed. The physical-based life prediction models which considered the contribution of different damage mechanisms have been applied. These models were applied to the temperature and strain rate dependences of isothermal cycling fatigue lives, and the strain-temperature history effect on the thermo-mechanical fatigue lives

  5. A roadmap for tailoring the strength and ductility of ferritic/martensitic T91 steel via thermo-mechanical treatment

    International Nuclear Information System (INIS)

    Song, M.; Sun, C.; Fan, Z.; Chen, Y.; Zhu, R.; Yu, K.Y.; Hartwig, K.T.; Wang, H.; Zhang, X.

    2016-01-01

    Ferritic/martensitic (F/M) steels with high strength and excellent ductility are important candidate materials for the life extension of the current nuclear reactors and the design of next generation nuclear reactors. Recent studies show that equal channel angular extrusion (ECAE) was able to improve mechanical strength of ferritic T91 steels moderately. Here, we examine several strategies to further enhance the mechanical strength of T91 while maintaining its ductility. Certain thermo-mechanical treatment (TMT) processes enabled by combinations of ECAE, water quench, and tempering may lead to “ductile martensite” with exceptionally high strength in T91 steel. The evolution of microstructures and mechanical properties of T91 steel were investigated in detail, and transition carbides were identified in water quenched T91 steel. This study provides guidelines for tailoring the microstructure and mechanical properties of T91 steel via ECAE enabled TMT for an improved combination of strength and ductility.

  6. Thermomechanical Response of Self-Assembled Nanoparticle Membranes

    Energy Technology Data Exchange (ETDEWEB)

    Wang, Yifan [Department; James; Chan, Henry [Center; Narayanan, Badri [Center; McBride, Sean P. [Department; Sankaranarayanan, Subramanian K. R. S. [Center; Lin, Xiao-Min [Center; Jaeger, Heinrich M. [Department; James

    2017-07-21

    Monolayers composed of colloidal nanoparticles, with a thickness of less than 10 nm, have remarkable mechanical moduli and can suspend over micrometer-sized holes to form free-standing membranes. In this paper, we discuss experiment's and coarse-grained molecular dynamics simulations characterizing the thermomechanical properties of these self-assembled nanoparticle membranes. These membranes remain strong and resilient up to temperatures much higher than previous simulation predictions and exhibit an unexpected hysteretic behavior during the first heating cooling cycle. We show this hysteretic behavior can be explained by an asymmetric ligand configuration from the self assembly process and can be controlled by changing the ligand coverage or cross-linking the ligand molecules. Finally, we show the screening effect of water molecules on the ligand interactions can strongly affect the moduli and thermomechanical behavior.

  7. Thermomechanical properties of radiation hardened oligoesteracrylates

    International Nuclear Information System (INIS)

    Lomonosova, N.V.; Chikin, Yu.A.

    1984-01-01

    Thermomechanical properties of radiation hardened oligoesteracrylates are studied by the methods of isothermal heating and thermal mechanics. Films of dimethacrylate of ethylene glycol, triethylene glycol (TGM-3), tetraethylene glycol, tridecaethylene glycol and TGM-3 mixture with methyl methacrylate hardened by different doses (5-150 kGy) using Co 60 installation with a dose rate of 2x10 -3 kGy/s served as a subject of the research. During oligoesteracrylate hargening a space network is formed, chain sections between lattice points of which are in a stressed state. Maximum of deformation is observed at 210-220 deg C on thermomechanical curves of samples hardened by doses > 5 kGy, which form and intensity is dependent on an absorbed dose. Presence of a high-temperature maximum on diaqrams of isometric heating of spatially cross-linked oligoesteracrylates is discovered. High thermal stability of three-dimensional network of radiation hardened oligoesteracrylates provides satisfactory tensile properties (40% of initial strength) in sample testing an elevated temperatures (200-250 deg C)

  8. Effect of some thermomechanical variables on plastic flow and creep-rupture of type 304 stainless steel at 5930C

    International Nuclear Information System (INIS)

    Swindeman, R.W.

    1977-01-01

    As part of an effort to examine sources of variability in the creep-rupture behavior of type 304 stainless steel, specimens subjected to a variety of prior thermomechanical treatments were tested. Included were different reannealing temperatures, cooling rates, types of prior straining, and a 24-hr age at 816 0 C. Two product forms of a single heat (heat 9T2796) were involved, and most testing was at 593 0 C. For material with coarse grain size, reannealing temperature had no pronounced influence. However, slow cooling rates and the 816 0 C aging significantly extended the rupture life. On the other hand, cold working by an equivalent of 4% tensile strain had very little influence on rupture life. Slow cooling or aging increased rupture life as a result of greatly improved creep ductility. This finding is consistent with similar observations in the literature for this and other stainless steels, and is believed to be due to the development of coarse, beneficial carbides on grain boundaries before stressing. The creep response in the primary and secondary stages was influenced by nearly all the thermomechanical treatments, but the variability in the response at relatively high stresses was scarcely greater than the variability observed in multiple tests on specimens having a common thermomechanical history. 10 figures, 1 table

  9. PECULIARITIES OF FORMATION OF STRUCTURE AND PROPERTIES AT THERMO-MECHANICAL PROCESSING OF ROLLED WIRE OF NICKEL-MOLYBDENUM STEEL WITH WELDING FUNCTION

    OpenAIRE

    V. A. Lutsenko

    2012-01-01

    There are results of researches of the mechanical properties and structure of the wire rod made of low-carbon nickel molybdenum steel after reduction to toughness thermomechanical treatment in the stream of high-speed wire mill.

  10. Nitrogen fixation in the activated sludge treatment of thermomechanical pulping wastewater: effect of dissolved oxygen.

    Science.gov (United States)

    Slade, A H; Anderson, S M; Evans, B G

    2003-01-01

    N-ViroTech, a novel technology which selects for nitrogen-fixing bacteria as the bacteria primarily responsible for carbon removal, has been developed to treat nutrient limited wastewaters to a high quality without the addition of nitrogen, and only minimal addition of phosphorus. Selection of the operating dissolved oxygen level to maximise nitrogen fixation forms a key component of the technology. Pilot scale activated sludge treatment of a thermomechanical pulping wastewater was carried out in nitrogen-fixing mode over a 15 month period. The effect of dissolved oxygen was studied at three levels: 14% (Phase 1), 5% (Phase 2) and 30% (Phase 3). The plant was operated at an organic loading of 0.7-1.1 kg BOD5/m3/d, a solids retention time of approximately 10 d, a hydraulic retention time of 1.4 d and a F:M ratio of 0.17-0.23 mg BOD5/mg VSS/d. Treatment performance was very stable over the three dissolved oxygen operating levels. The plant achieved 94-96% BOD removal, 82-87% total COD removal, 79-87% soluble COD removal, and >99% total extractives removal. The lowest organic carbon removals were observed during operation at 30% DO but were more likely to be due to phosphorus limitation than operation at high dissolved oxygen, as there was a significant decrease in phosphorus entering the plant during Phase 3. Discharge of dissolved nitrogen, ammonium and oxidised nitrogen were consistently low (1.1-1.6 mg/L DKN, 0.1-0.2 mg/L NH4+-N and 0.0 mg/L oxidised nitrogen). Discharge of dissolved phosphorus was 2.8 mg/L, 0.1 mg/L and 0.6 mg/L DRP in Phases 1, 2 and 3 respectively. It was postulated that a population of polyphosphate accumulating bacteria developed during Phase 1. Operation at low dissolved oxygen during Phase 2 appeared to promote biological phosphorus uptake which may have been affected by raising the dissolved oxygen to 30% in Phase 3. Total nitrogen and phosphorus discharge was dependent on efficient secondary clarification, and improved over the course of

  11. PECULIARITIES OF FORMATION OF STRUCTURE AND PROPERTIES AT THERMO-MECHANICAL PROCESSING OF ROLLED WIRE OF NICKEL-MOLYBDENUM STEEL WITH WELDING FUNCTION

    Directory of Open Access Journals (Sweden)

    V. A. Lutsenko

    2012-01-01

    Full Text Available There are results of researches of the mechanical properties and structure of the wire rod made of low-carbon nickel molybdenum steel after reduction to toughness thermomechanical treatment in the stream of high-speed wire mill.

  12. Enhanced thermo-mechanical performance and strain-induced ...

    Indian Academy of Sciences (India)

    Enhanced thermo-mechanical performance and strain-induced band gap reduction of TiO2@PVC nanocomposite films ... School of Chemical Engineering, Yeungnam University, Gyeongsan 712-749, Republic of Korea; School of Mechanical Engineering, Yeungnam University, Gyeongsan 712-749, Republic of Korea ...

  13. Enhancing the ABAQUS thermomechanics code to simulate multipellet steady and transient LWR fuel rod behavior

    International Nuclear Information System (INIS)

    Williamson, R.L.

    2011-01-01

    Highlights: → The ABAQUS thermomechanics code is enhanced to enable simulation of nuclear fuel behavior. → Comparisons are made between discrete and smeared fuel pellet analysis. → Multidimensional and multipellet analysis is important for accurate prediction of PCMI. → Fully coupled thermomechanics results in very smooth prediction of fuel-clad gap closure. → A smeared-pellet approximation results in significant underprediction of clad radial displacements and plastic strain. - Abstract: A powerful multidimensional fuels performance analysis capability, applicable to both steady and transient fuel behavior, is developed based on enhancements to the commercially available ABAQUS general-purpose thermomechanics code. Enhanced capabilities are described, including: UO 2 temperature and burnup dependent thermal properties, solid and gaseous fission product swelling, fuel densification, fission gas release, cladding thermal and irradiation creep, cladding irradiation growth, gap heat transfer, and gap/plenum gas behavior during irradiation. This new capability is demonstrated using a 2D axisymmetric analysis of the upper section of a simplified multipellet fuel rod, during both steady and transient operation. Comparisons are made between discrete and smeared-pellet simulations. Computational results demonstrate the importance of a multidimensional, multipellet, fully-coupled thermomechanical approach. Interestingly, many of the inherent deficiencies in existing fuel performance codes (e.g., 1D thermomechanics, loose thermomechanical coupling, separate steady and transient analysis, cumbersome pre- and post-processing) are, in fact, ABAQUS strengths.

  14. Study of Carbide Evolution During Thermo-Mechanical Processing of AISI D2 Tool Steel

    Science.gov (United States)

    Bombac, D.; Fazarinc, M.; Podder, A. Saha; Kugler, G.

    2013-03-01

    The microstructure of a cold-worked tool steel (AISI D2) with various thermo-mechanical treatments was examined in the current study to identify the effects of these treatments on phases. X-ray diffraction was used to identify phases. Microstructural changes such as spheroidization and coarsening of carbides were studied. Thermodynamic calculations were used to verify the results of the differential thermal analysis. It was found that soaking temperature and time have a large influence on dissolution, precipitation, spheroidization, and coalescence of carbides present in the steel. This consequently influences the hot workability and final properties.

  15. Thermomechanics of composite structures under high temperatures

    CERN Document Server

    Dimitrienko, Yu I

    2016-01-01

    This pioneering book presents new models for the thermomechanical behavior of composite materials and structures taking into account internal physico-chemical transformations such as thermodecomposition, sublimation and melting at high temperatures (up to 3000 K). It is of great importance for the design of new thermostable materials and for the investigation of reliability and fire safety of composite structures. It also supports the investigation of interaction of composites with laser irradiation and the design of heat-shield systems. Structural methods are presented for calculating the effective mechanical and thermal properties of matrices, fibres and unidirectional, reinforced by dispersed particles and textile composites, in terms of properties of their constituent phases. Useful calculation methods are developed for characteristics such as the rate of thermomechanical erosion of composites under high-speed flow and the heat deformation of composites with account of chemical shrinkage. The author expan...

  16. Poly-Lactide/Exfoliated C30B Interactions and Influence on Thermo-Mechanical Properties Due to Artificial Weathering

    Directory of Open Access Journals (Sweden)

    Wendy Margarita Chávez-Montes

    2016-04-01

    Full Text Available Thermal stability as well as enhanced mechanical properties of poly-lactide (PLA can increase PLA applications for short-use products. The conjunction of adequate molecular weight (MW as well as satisfactory thermo-mechanical properties, together, can lead to the achievement of suitable properties. However, PLA is susceptible to thermal degradation and thus an undesired decay of MW and a decrease of its mechanical properties during processing. To avoid this PLA degradation, nanofiller is incorporated as reinforcement to increase its thermo-mechanical properties. There are many papers focusing on filler effects on the thermal stability and mechanical properties of PLA/nanocomposites; however, these investigations lack an explanation of polymer/filler interactions. We propose interactions between PLA and Cloisite30B (C30B as nanofiller. We also study the effects on the thermal and mechanical properties due to molecular weight decay after exposure to artificial weathering. PLA blank and nanocomposites were subjected to three time treatments (0, 176, and 360 h of exposure to artificial weathering in order to achieve comparable materials with different MW. MW was acquired by means of Gel Permeation Chromatography (GPC. Thermo-mechanical properties were investigated through Thermogravimetric Analysis (TGA, Differential Scanning Calorimetry (DSC, X-ray Diffraction (XRD, Dynamic Mechanical Thermal Analysis (DMTA and Fourier Transform Infrared Spectroscopy (FTIR.

  17. On-chip detection of gel transition temperature using a novel micro-thermomechanical method.

    Directory of Open Access Journals (Sweden)

    Tsenguun Byambadorj

    Full Text Available We present a new thermomechanical method and a platform to measure the phase transition temperature at microscale. A thin film metal sensor on a membrane simultaneously measures both temperature and mechanical strain of the sample during heating and cooling cycles. This thermomechanical principle of operation is described in detail. Physical hydrogel samples are prepared as a disc-shaped gels (200 μm thick and 1 mm diameter and placed between an on-chip heater and sensor devices. The sol-gel transition temperature of gelatin solution at various concentrations, used as a model physical hydrogel, shows less than 3% deviation from in-depth rheological results. The developed thermomechanical methodology is promising for precise characterization of phase transition temperature of thermogels at microscale.

  18. Two scale damage model and related numerical issues for thermo-mechanical high cycle fatigue

    International Nuclear Information System (INIS)

    Desmorat, R.; Kane, A.; Seyedi, M.; Sermage, J.P.

    2007-01-01

    On the idea that fatigue damage is localized at the microscopic scale, a scale smaller than the mesoscopic one of the Representative Volume Element (RVE), a three-dimensional two scale damage model has been proposed for High Cycle Fatigue applications. It is extended here to aniso-thermal cases and then to thermo-mechanical fatigue. The modeling consists in the micro-mechanics analysis of a weak micro-inclusion subjected to plasticity and damage embedded in an elastic meso-element (the RVE of continuum mechanics). The consideration of plasticity coupled with damage equations at micro-scale, altogether with Eshelby-Kroner localization law, allows to compute the value of microscopic damage up to failure for any kind of loading, 1D or 3D, cyclic or random, isothermal or aniso-thermal, mechanical, thermal or thermo-mechanical. A robust numerical scheme is proposed in order to make the computations fast. A post-processor for damage and fatigue (DAMAGE-2005) has been developed. It applies to complex thermo-mechanical loadings. Examples of the representation by the two scale damage model of physical phenomena related to High Cycle Fatigue are given such as the mean stress effect, the non-linear accumulation of damage. Examples of thermal and thermo-mechanical fatigue as well as complex applications on real size testing structure subjected to thermo-mechanical fatigue are detailed. (authors)

  19. Thermomechanical evaluation of the fuel assemblies fabricated in the ININ

    International Nuclear Information System (INIS)

    Hernandez L, H.; Ortiz V, J.

    2005-01-01

    The pilot plant of fuel production of the National Institute of Nuclear Research (ININ) provided to the Laguna Verde Nuclear Power Plant (CNLV) four fuel assemblies type GE9B. The fuel irradiation was carried out in the unit 1 of the CNLV during four operation cycles, highlighting the fact that in their third cycle the four assemblies were placed in the center of the reactor core. In the Nuclear Systems Department (DSN) of the ININ it has been carried out studies to evaluate their neutron performance and to be able to determine the exposure levels of this fuels. Its also outlines the necessity to carry out a study of the thermomechanical behavior of the fuel rods that compose the assemblies, through computational codes that simulate their performance so much thermal as mechanical. For such purpose has been developing in the DSN the FETMA code, together with the codes that compose the system Fuel Management System (FMS), which evaluates the thermomechanical performance of fuel elements. In this work were used the FETMA and FEMAXI codes (developed by JAERI) to study the thermomechanical performance of the fuel elements manufactured in the ININ. (Author)

  20. Thermomechanical Analysis of Shape-Memory Composite Tape Spring

    Science.gov (United States)

    Yang, H.; Wang, L. Y.

    2013-06-01

    Intelligent materials and structures have been extensively applied for satellite designs in order to minimize the mass and reduce the cost in the launch of the spacecraft. Elastic memory composites (EMCs) have the ability of high-strain packaging and shape-memory effect, but increase the parts and total weight due to the additional heating system. Shape-memory sandwich structures Li and Wang (J. Intell. Mater. Syst. Struct. 22(14), 1605-1612, 2011) can overcome such disadvantage by using the metal skin acting as the heating element. However, the high strain in the micro-buckled metal skin decreases the deployment efficiency. This paper aims to present an insight into the folding and deployment behaviors of shape-memory composite (SMC) tape springs. A thermomechanical process was analyzed, including the packaging deformation at an elevated temperature, shape frozen at the low temperature and shape recovery after reheating. The result shows that SMC tape springs can significantly decrease the strain concentration in the metal skin, as well as exhibiting excellent shape frozen and recovery behaviors. Additionally, possible failure modes of SMC tape springs were also analyzed.

  1. A thermomechanical crystal plasticity constitutive model for ultrasonic consolidation

    KAUST Repository

    Siddiq, Amir; El Sayed, Tamer S.

    2012-01-01

    We present a micromechanics-based thermomechanical constitutive model to simulate the ultrasonic consolidation process. Model parameters are calibrated using an inverse modeling approach. A comparison of the simulated response and experimental

  2. Atomistic modeling of thermomechanical properties of SWNT/Epoxy nanocomposites

    Science.gov (United States)

    Fasanella, Nicholas; Sundararaghavan, Veera

    2015-09-01

    Molecular dynamics simulations are performed to compute thermomechanical properties of cured epoxy resins reinforced with pristine and covalently functionalized carbon nanotubes. A DGEBA-DDS epoxy network was built using the ‘dendrimer’ growth approach where 75% of available epoxy sites were cross-linked. The epoxy model is verified through comparisons to experiments, and simulations are performed on nanotube reinforced cross-linked epoxy matrix using the CVFF force field in LAMMPS. Full stiffness matrices and linear coefficient of thermal expansion vectors are obtained for the nanocomposite. Large increases in stiffness and large decreases in thermal expansion were seen along the direction of the nanotube for both nanocomposite systems when compared to neat epoxy. The direction transverse to nanotube saw a 40% increase in stiffness due to covalent functionalization over neat epoxy at 1 K whereas the pristine nanotube system only saw a 7% increase due to van der Waals effects. The functionalized SWNT/epoxy nanocomposite showed an additional 42% decrease in thermal expansion along the nanotube direction when compared to the pristine SWNT/epoxy nanocomposite. The stiffness matrices are rotated over every possible orientation to simulate the effects of an isotropic system of randomly oriented nanotubes in the epoxy. The randomly oriented covalently functionalized SWNT/Epoxy nanocomposites showed substantial improvements over the plain epoxy in terms of higher stiffness (200% increase) and lower thermal expansion (32% reduction). Through MD simulations, we develop means to build simulation cells, perform annealing to reach correct densities, compute thermomechanical properties and compare with experiments.

  3. Atomistic modeling of thermomechanical properties of SWNT/Epoxy nanocomposites

    International Nuclear Information System (INIS)

    Fasanella, Nicholas; Sundararaghavan, Veera

    2015-01-01

    Molecular dynamics simulations are performed to compute thermomechanical properties of cured epoxy resins reinforced with pristine and covalently functionalized carbon nanotubes. A DGEBA-DDS epoxy network was built using the ‘dendrimer’ growth approach where 75% of available epoxy sites were cross-linked. The epoxy model is verified through comparisons to experiments, and simulations are performed on nanotube reinforced cross-linked epoxy matrix using the CVFF force field in LAMMPS. Full stiffness matrices and linear coefficient of thermal expansion vectors are obtained for the nanocomposite. Large increases in stiffness and large decreases in thermal expansion were seen along the direction of the nanotube for both nanocomposite systems when compared to neat epoxy. The direction transverse to nanotube saw a 40% increase in stiffness due to covalent functionalization over neat epoxy at 1 K whereas the pristine nanotube system only saw a 7% increase due to van der Waals effects. The functionalized SWNT/epoxy nanocomposite showed an additional 42% decrease in thermal expansion along the nanotube direction when compared to the pristine SWNT/epoxy nanocomposite. The stiffness matrices are rotated over every possible orientation to simulate the effects of an isotropic system of randomly oriented nanotubes in the epoxy. The randomly oriented covalently functionalized SWNT/Epoxy nanocomposites showed substantial improvements over the plain epoxy in terms of higher stiffness (200% increase) and lower thermal expansion (32% reduction). Through MD simulations, we develop means to build simulation cells, perform annealing to reach correct densities, compute thermomechanical properties and compare with experiments. (paper)

  4. Test program element II blanket and shield thermal-hydraulic and thermomechanical testing, experimental facility survey

    Energy Technology Data Exchange (ETDEWEB)

    Ware, A.G.; Longhurst, G.R.

    1981-12-01

    This report presents results of a survey conducted by EG and G Idaho to determine facilities available to conduct thermal-hydraulic and thermomechanical testing for the Department of Energy Office of Fusion Energy First Wall/Blanket/Shield Engineering Test Program. In response to EG and G queries, twelve organizations (in addition to EG and G and General Atomic) expressed interest in providing experimental facilities. A variety of methods of supplying heat is available.

  5. Test program element II blanket and shield thermal-hydraulic and thermomechanical testing, experimental facility survey

    International Nuclear Information System (INIS)

    Ware, A.G.; Longhurst, G.R.

    1981-12-01

    This report presents results of a survey conducted by EG and G Idaho to determine facilities available to conduct thermal-hydraulic and thermomechanical testing for the Department of Energy Office of Fusion Energy First Wall/Blanket/Shield Engineering Test Program. In response to EG and G queries, twelve organizations (in addition to EG and G and General Atomic) expressed interest in providing experimental facilities. A variety of methods of supplying heat is available

  6. Interfacial characteristics of hybrid nanocomposite under thermomechanical loading

    Science.gov (United States)

    Choyal, Vijay; Kundalwal, Shailesh I.

    2017-12-01

    In this work, an improved shear lag model was developed to investigate the interfacial characteristics of three-phase hybrid nanocomposite which is reinforced with microscale fibers augmented with carbon nanotubes on their circumferential surfaces. The shear lag model accounts for (i) radial and axial deformations of different transversely isotropic constituents, (ii) thermomechanical loads on the representative volume element (RVE), and (iii) staggering effect of adjacent RVEs. The results from the current newly developed shear lag model are validated with the finite element simulations and found to be in good agreement. This study reveals that the reduction in the maximum value of the axial stress in the fiber and the interfacial shear stress along its length become more pronounced in the presence of applied thermomechanical loads on the staggered RVEs. The existence of shear tractions along the RVE length plays a significant role in the interfacial characteristics and cannot be ignored.

  7. Modelling the Thermomechanical Conditions in Friction Stir Welding

    DEFF Research Database (Denmark)

    Schmidt, Henrik Nikolaj Blich

    Friction Stir Welding is a solid-state welding process invented by TWI in 1991. The FSW process is unique in the sense that joining of un-weldable alloys readily can be made. The thermomechanical conditions present in the workpiece during the welding process are of great interest since...... these control the properties of the weld. In the present work, a set of experimental, analytical and numerical analyses are carried out in order to evaluate the thermomechanical conditions descriptive for welding of aluminium, in this case AA2024-T3, under a specific set of welding parameters. Despite...... these specific data, the developed models can be applied for other alloys and welding parameters as well. A detailed experiment is carried out which constitutes the basis for the development and validation of the numerical and analytical models presented in this work. The contact condition at the tool...

  8. Coupled thermomechanical behavior of graphene using the spring-based finite element approach

    Energy Technology Data Exchange (ETDEWEB)

    Georgantzinos, S. K., E-mail: sgeor@mech.upatras.gr; Anifantis, N. K., E-mail: nanif@mech.upatras.gr [Machine Design Laboratory, Department of Mechanical Engineering and Aeronautics, University of Patras, Rio, 26500 Patras (Greece); Giannopoulos, G. I., E-mail: ggiannopoulos@teiwest.gr [Materials Science Laboratory, Department of Mechanical Engineering, Technological Educational Institute of Western Greece, 1 Megalou Alexandrou Street, 26334 Patras (Greece)

    2016-07-07

    The prediction of the thermomechanical behavior of graphene using a new coupled thermomechanical spring-based finite element approach is the aim of this work. Graphene sheets are modeled in nanoscale according to their atomistic structure. Based on molecular theory, the potential energy is defined as a function of temperature, describing the interatomic interactions in different temperature environments. The force field is approached by suitable straight spring finite elements. Springs simulate the interatomic interactions and interconnect nodes located at the atomic positions. Their stiffness matrix is expressed as a function of temperature. By using appropriate boundary conditions, various different graphene configurations are analyzed and their thermo-mechanical response is approached using conventional finite element procedures. A complete parametric study with respect to the geometric characteristics of graphene is performed, and the temperature dependency of the elastic material properties is finally predicted. Comparisons with available published works found in the literature demonstrate the accuracy of the proposed method.

  9. Thermomechanical characterization of thiol-epoxy shape memory thermosets for mechanical actuators design

    Science.gov (United States)

    Belmonte, Alberto; Fernández-Francos, Xavier; De la Flor, Silvia

    2018-02-01

    In this paper, shape-memory "thiol-epoxy" polymers are synthesized and characterized as potential thermomechanical actuators. Their thermomechanical properties are investigated through dynamo mechanical and tensile analyses and related to their network structural properties by using "thiol" and "epoxy" compounds of different functionality and structure. Their mechanical properties (resistance at break, elongation limits and strain energy) are related to their shape-memory response under free-recovery conditions and partially-constrained conditions, thus, establishing the connection between network relaxation (free-recovery) with the work output capabilities (partially-constrained). Results show high mechanical performance, achieving high elongation at break values (up to 100%) and stress at break values (up to 50 MPa). The shape-memory experiments reveal strong dependence of the programming conditions and network structure on the recovery efficiency at free-conditions, whereas under partially-constrained conditions, the controlling factors are the mechanical limits at high temperature. Moreover, some recommendations to achieve the maximum work output efficiency for a given operational design of a thermomechanical actuator are deduced.

  10. Improvement of thermo-mechanical properties of ceramic materials for nuclear applications

    International Nuclear Information System (INIS)

    Decroix, G.M.; Gosset, D.; Kryger, B.; Boussuge, M.; Burlet, H.

    1994-01-01

    In order to improve the thermo-mechanical properties of materials used as neutron absorbers in nuclear reactors, cermet or cercer have been produced with two original microstructures: micro- or macro-dispersed composites. The composites thermal shock resistance has been evaluated in an image furnace. The microstructures we obtained involve different reinforcement mechanisms, such as crack deflection, crack branching, crack bridging or microcrack toughening, and improvement of thermal conductivity. The results reveal a significant improvement of the thermo-mechanical properties of the boron base neutron absorbers whose fabrication process leads to a macro-dispersed microstructure. (authors). 8 refs., 8 figs., 2 tabs

  11. Examination of the Thermo-mechanical Properties of E-Glass/Carbon Composites

    Directory of Open Access Journals (Sweden)

    Hande Sezgin

    2017-12-01

    Full Text Available Eight-ply E-glass, carbon and E-glass/carbon fabric-reinforced polyester based hybrid composites were manufactured in this study. A vacuum infusion system was used as the production method. Dynamic mechanical analysis, thermogravimetric analysis and differential scanning calorimetry analysis were conducted to examine the thermo-mechanical properties of composite samples. The effect of reinforcement type and different stacking sequences of fabric plies on the thermo-mechanical properties of composite samples were also investigated. Results showed that the type and alignment of reinforcement material has a signifi cant effect on the dynamic mechanical properties of composite samples.

  12. Thermomechanical properties of the silanized-kenaf/polystyrene composites

    Directory of Open Access Journals (Sweden)

    2009-10-01

    Full Text Available In order to improve the poor interfacial adhesion of the kenaf fiber and polystyrene (PS in their composite material, the surface of the kenaf fiber was modified using a synthesized polymeric coupling agent to promote adhesion with PS matrix. The dynamic thermo-mechanical properties of the composite composed of modified kenaf fiber and PS were also investigated. The polymeric coupling agent treatment of the kenaf fiber increased the fiber-matrix interaction through a condensation reaction between alkoxysilane and hydroxyl groups of kenaf cellulose. DMA (Dynamic Mechanical Thermal Analysis results showed that the modified fiber composites have higher E′ and lower tanδ than those with untreated fiber indicating that a greater interfacial interaction between the matrix resin and the fiber. It was also found that the storage modulus increases in proportion with the Si/C ratio on the fiber surface.

  13. Effect of gluten, egg and soy proteins on the rheological and thermo-mechanical properties of wholegrain rice flour.

    Science.gov (United States)

    Pătraşcu, Livia; Banu, Iuliana; Vasilean, Ina; Aprodu, Iuliana

    2017-03-01

    The effect of protein addition on the rheological, thermo-mechanical and baking properties of wholegrain rice flour was investigated. Gluten, powdered eggs and soy protein concentrate were first analyzed in terms of rheological properties, alone and in admixture with rice flour. The temperature ramp tests showed clear differences in the rheological behavior of the batters supplemented with different proteins. The highest thermal stability was observed in case of soy protein samples. Frequency sweep tests indicated significant improvements of the rheological properties of rice flour supplemented with 15% gluten or soy proteins. The thermo-mechanical tests showed that, due to the high fat contents and low level of free water, the dough samples containing powdered eggs exhibited the highest stability. Addition of gluten resulted in a significant decrease of the dough development time, whereas samples with powdered eggs and soy proteins were more difficult to hydrate. The incorporation of proteins into the rice flour-based dough formulations significantly affected starch behavior by decreasing the peak consistency values. Concerning the quality of the rice flour-based breads, soy protein addition resulted in lighter crumb color and increased texture attributes, samples with gluten had better resilience and adhesiveness, whereas breads with egg protein were less brittle.

  14. Going greener: Synthesis of fully biobased unsaturated polyesters for styrene crosslinked resins with enhanced thermomechanical properties

    Directory of Open Access Journals (Sweden)

    C. S. M. F. Costa

    2017-11-01

    Full Text Available The main goal of this work was the development of fully biobased unsaturated polyesters (UPs that upon crosslinking with unsaturated monomers (UM could lead to greener unsaturated polyester resins (UPRs with similar thermomechanical properties to commercial fossil based UPR. After the successful synthesis of the biobased UPs, those were crosslinked with styrene (Sty, the most commonly used monomer, and the influence of the chemical structure of the UPs on the thermomechanical characteristics of UPRs were evaluated. The properties were compared with those of a commercial resin (Resipur 9837©. The BioUPRs presented high gel contents and contact angles that are similar to the commercial resin. The thermomechanical properties were evaluated by dynamic mechanical thermal analysis (DMTA and it was found that the UPR synthesized using propylene glycol (PG, succinic acid (SuAc and itaconic acid (ItAc presented very close thermomechanical properties compared to the commercial resin.

  15. Thermo-mechanical properties of mixed ion-electron conducting membrane materials

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Bingxin

    2011-07-01

    The thesis presents thermo-mechanical properties of La{sub 0.58}Sr{sub 0.4}Co{sub 0.2}Fe{sub 0.8}O{sub 3-{delta}} (LSCF) and Ba{sub 0.5}Sr{sub 0.5}Co{sub 0.8}Fe{sub 0.2}O{sub 3-{delta}} (BSCF) perovskite materials, which are considered as oxygen transport membranes (OTM) for gas separation units. Ring-on-ring bending test with disk-shaped samples and depth-sensitive micro-indentation have been used as macroscopic and microscopic tests, respectively. In addition, the thermo-mechanical properties of a third OTM candidate material La{sub 2}NiO{sub 4+{delta}} (LNO) were investigated. The results of the thermo-mechanical measurements with the BSCF revealed an anomaly between 200 C and 400 C. In particular, the temperature dependence of Young's modulus shows a minimum at {proportional_to} 200 C. Fracture stress and toughness exhibit a qualitatively similar behavior with a minimum between 200 C and 400 C, before recovering between 500 C and 800 C. X-ray diffraction analyses verified that BSCF remains cubic in the relevant temperature range. Hence the anomalies were assumed to be related to the transition of Co{sup 3+} spin states reported for other Co-containing perovskites. This assumption could be experimentally confirmed by magnetic susceptibility measurements. The fracture surfaces of the specimens are not affected by the mechanical anomalies at intermediate temperatures, since only a transgranular fracture mode has been observed. Complementary to the mechanical characterization of BSCF, also the temperature dependency of fracture stress and elastic behavior of LSCF have been determined. Phase compositions of LSCF have been studied by in-situ high temperature XRD. Changes in phase composition with temperature are observed. At ambient temperature the LSCF perovskite material comprises two phases: rhombohedral and cubic symmetry. The ratio of the two phases depends on both cooling rate and atmosphere. The transition of rhombohedral to cubic occurs between 700 C and

  16. Finding an Optimal Thermo-Mechanical Processing Scheme for a Gum-Type Ti-Nb-Zr-Fe-O Alloy

    Science.gov (United States)

    Nocivin, Anna; Cojocaru, Vasile Danut; Raducanu, Doina; Cinca, Ion; Angelescu, Maria Lucia; Dan, Ioan; Serban, Nicolae; Cojocaru, Mirela

    2017-09-01

    A gum-type alloy was subjected to a thermo-mechanical processing scheme to establish a suitable process for obtaining superior structural and behavioural characteristics. Three processes were proposed: a homogenization treatment, a cold-rolling process and a solution treatment with three heating temperatures: 1073 K (800 °C), 1173 K (900 °C) and 1273 K (1000 °C). Results of all three proposed processes were analyzed using x-ray diffraction and scanning electron microscopy imaging, to establish and compare the structural modifications. The behavioural status was completed with micro-hardness and tensile strength tests. The optimal results were obtained for solution treatment at 1073 K.

  17. Thermo-mechanical stress analysis of cryopreservation in cryobags and the potential benefit of nanowarming.

    Science.gov (United States)

    Solanki, Prem K; Bischof, John C; Rabin, Yoed

    2017-06-01

    Cryopreservation by vitrification is the only promising solution for long-term organ preservation which can save tens of thousands of lives across the world every year. One of the challenges in cryopreservation of large-size tissues and organs is to prevent fracture formation due to the tendency of the material to contract with temperature. The current study focuses on a pillow-like shape of a cryobag, while exploring various strategies to reduce thermo-mechanical stress during the rewarming phase of the cryopreservation protocol, where maximum stresses are typically found. It is demonstrated in this study that while the level of stress may generally increase with the increasing amount of CPA filled in the cryobag, the ratio between width and length of the cryobag play a significant role. Counterintuitively, the overall maximum stress is not found when the bag is filled to its maximum capacity (when the filled cryobag resembles a sphere). Parametric investigation suggests that reducing the initial rewarming rate between the storage temperature and the glass transition temperature may dramatically decrease the thermo-mechanical stress. Adding a temperature hold during rewarming at the glass transition temperature may reduce the thermo-mechanical stress in some cases, but may have an adverse effect in other cases. Finally, it is demonstrated that careful incorporation of volumetric heating by means on nanoparticles in an alternating magnetic field, or nanowarming, can dramatically reduce the resulting thermo-mechanical stress. These observations display the potential benefit of a thermo-mechanical design of the cryopreservation protocols in order to prevent structural damage. Copyright © 2017 Elsevier Inc. All rights reserved.

  18. Thermo-mechanical properties of polystyrene-based shape memory nanocomposites

    NARCIS (Netherlands)

    Xu, B.; Fu, Y.Q.; Ahmad, M.; Luo, J.K.; Huang, W.M.; Kraft, A.; Reuben, R.; Pei, Y.T.; Chen, Zhenguo; Hosson, J.Th.M. De

    2010-01-01

    Shape memory nanocomposites were fabricated using chemically cross-linked polystyrene (PS) copolymer as a matrix and different nanofillers (including alumina, silica and clay) as the reinforcing agents. Their thermo-mechanical properties and shape memory effects were characterized. Experimental

  19. Assessment of thermo-mechanical behavior in CLAM steel first wall structures

    International Nuclear Information System (INIS)

    Liu Fubin; Yao Man

    2012-01-01

    Highlights: ► China Low Activation Martensitic steel (CLAM) as FW the structural material. ► The thermo-mechanical behavior of the FW was analyzed under the condition of normal ITER operation combined effect of plasma heat flux and neutron heating. ► The temperature dependence of the material physical properties of CLAM is summarized. - Abstract: The temperature and strain distributions of the mockup with distinct structural material (SS316L or China Low Activation Martensitic steel (CLAM)) in two-dimensional model were calculated and analyzed, based on a high heat flux (HHF) test recently reported with heat flux of 3.2 MW/m 2 . The calculated temperature and strain results in the first wall (FW), in which SS316L is as the structural material, showed good agreement with HHF test. By substituting CLAM steel for SS316L the contrast analysis indicates that the thermo-mechanical property for CLAM steel is better than that of SS316 at the same condition. Furthermore, the thermo-mechanical behavior of the FW was analyzed under the condition of normal ITER operation combined effect of plasma heat flux and neutron heating.

  20. Assessment of thermo-mechanical behavior in CLAM steel first wall structures

    Energy Technology Data Exchange (ETDEWEB)

    Liu Fubin, E-mail: liufubin_1216@126.com [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, Liaoning (China); Yao Man, E-mail: yaoman@dlut.edu.cn [School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, Liaoning (China)

    2012-01-15

    Highlights: Black-Right-Pointing-Pointer China Low Activation Martensitic steel (CLAM) as FW the structural material. Black-Right-Pointing-Pointer The thermo-mechanical behavior of the FW was analyzed under the condition of normal ITER operation combined effect of plasma heat flux and neutron heating. Black-Right-Pointing-Pointer The temperature dependence of the material physical properties of CLAM is summarized. - Abstract: The temperature and strain distributions of the mockup with distinct structural material (SS316L or China Low Activation Martensitic steel (CLAM)) in two-dimensional model were calculated and analyzed, based on a high heat flux (HHF) test recently reported with heat flux of 3.2 MW/m{sup 2}. The calculated temperature and strain results in the first wall (FW), in which SS316L is as the structural material, showed good agreement with HHF test. By substituting CLAM steel for SS316L the contrast analysis indicates that the thermo-mechanical property for CLAM steel is better than that of SS316 at the same condition. Furthermore, the thermo-mechanical behavior of the FW was analyzed under the condition of normal ITER operation combined effect of plasma heat flux and neutron heating.

  1. Thermo-mechanical simulations of early-age concrete cracking with durability predictions

    Science.gov (United States)

    Havlásek, Petr; Šmilauer, Vít; Hájková, Karolina; Baquerizo, Luis

    2017-09-01

    Concrete performance is strongly affected by mix design, thermal boundary conditions, its evolving mechanical properties, and internal/external restraints with consequences to possible cracking with impaired durability. Thermo-mechanical simulations are able to capture those relevant phenomena and boundary conditions for predicting temperature, strains, stresses or cracking in reinforced concrete structures. In this paper, we propose a weakly coupled thermo-mechanical model for early age concrete with an affinity-based hydration model for thermal part, taking into account concrete mix design, cement type and thermal boundary conditions. The mechanical part uses B3/B4 model for concrete creep and shrinkage with isotropic damage model for cracking, able to predict a crack width. All models have been implemented in an open-source OOFEM software package. Validations of thermo-mechanical simulations will be presented on several massive concrete structures, showing excellent temperature predictions. Likewise, strain validation demonstrates good predictions on a restrained reinforced concrete wall and concrete beam. Durability predictions stem from induction time of reinforcement corrosion, caused by carbonation and/or chloride ingress influenced by crack width. Reinforcement corrosion in concrete struts of a bridge will serve for validation.

  2. Study of texture and microstructure evaluation of steel API 5L X70 under various thermomechanical cycles

    Energy Technology Data Exchange (ETDEWEB)

    Masoumi, Mohammad, E-mail: Mohammad@alu.ufc.br; Herculano, Luis Flavio Gaspar; Ferreira Gomes de Abreu, Hamilton

    2015-07-15

    This work studies the influence of different thermomechanical paths on the microstructure and crystallographic texture across the thickness of API 5L X70 pipeline steel manufactured via hot rolling using X-ray diffraction (XRD), scanning electron microscope (SEM), and electron backscattered diffraction (EBSD). The starting materials were controlled hot-rolled at 1000 °C to 44% and 67% reductions and subsequently heat treated with such processes as annealing, water quenching and quench tempering at three different temperatures to evaluate the microstructure and crystallographic texture changes across the thickness. The banded ferrite-pearlite microstructure of the initial material was changed to acicular ferrite, quasi-polygonal ferrite, granular bainite, martensite and retained austenite via different heat treatments. Moreover, different thermomechanical paths induced crystallographic texture variations across the thickness, e.g., {112}//ND, {111}//ND (γ fibre), and {011}//ND fibres dominated on the surface plane in contact with the rolls, whereas {001}//ND and particularly the (001)[1 1 0] texture component developed in the centre plane on which shear deformation has a zero value in this region. In this study, a simple interpretation of texture evolution was analyzed by comparison with the orientation changes that occurred during different rolling schedules and post-treatment processes.

  3. Thermomechanical modeling and data analysis for heating experiments at Stripa, Sweden

    International Nuclear Information System (INIS)

    Chan, T.; Littlestone, N.; Wan, O.

    1979-11-01

    Comparisons were made between predicted and measured thermomechanical displacements and stresses for in situ heating experiments at a depth of 340 m in a granite body at Stripa, Sweden. We found that taking into account the temperature dependence of the thermal expansion coefficient and the mechanical properties of the rock substantially improves the agreement between theory and experiment. In general, the displacements calculated using laboratory values of rock properties agree better with field data than in the case of stresses. This may be due to the difference between in situ and laboratory rock modulus. The significance of temperature-dependent rock properties and strength to thermomechanical failure is also discussed

  4. Thermomechanical behavior of NiTiPdPt high temperature shape memory alloy springs

    International Nuclear Information System (INIS)

    Nicholson, D E; Vaidyanathan, R; Padula II, S A; Noebe, R D; Benafan, O

    2014-01-01

    Transformation strains in high temperature shape memory alloys (HTSMAs) are generally smaller than for conventional NiTi alloys and can be purposefully limited in cases where stability and repeatability at elevated temperatures are desired. Yet such alloys can still be used in actuator applications that require large strokes when used in the form of springs. Thus there is a need to understand the thermomechanical behavior of shape memory alloy spring actuators, particularly those consisting of alternative alloys. In this work, a modular test setup was assembled with the objective of acquiring stroke, stress, temperature, and moment data in real time during joule heating and forced convective cooling of Ni 19.5 Ti 50.5 Pd 25 Pt 5 HTSMA springs. The spring actuators were subjected to both monotonic axial loading and thermomechanical cycling. The role of rotational constraints (i.e., by restricting rotation or allowing for free rotation at the ends of the springs) on stroke performance was also assessed. Finally, recognizing that evolution in the material microstructure can result in changes in HTSMA spring geometry, the effect of material microstructural evolution on spring performance was examined. This was done by taking into consideration the changes in geometry that occurred during thermomechanical cycling. This work thus provides insight into designing with HTSMA springs and predicting their thermomechanical performance. (paper)

  5. Sintering nanodisperse zirconium powders with various stabilizing additives

    Directory of Open Access Journals (Sweden)

    Antsiferov V.N.

    2011-01-01

    Full Text Available Effect of various stabilizing additives on sintering kinetics of nanodisperse powders was studied by thermomechanical analysis. Temperature ranges of the most intense shrinking, characteristic points of shrinking rate changes were established. Peaks characterizing the most intense shrinking of nanodisperse zirconium powder samples were shown to allow to arrange the stabilizing additives as follows: Y2O3→CeO2→TiO2.

  6. Experimental study of thermo-mechanical behavior of a thermosetting shape-memory polymer

    Science.gov (United States)

    Liu, Ruoxuan; Li, Yunxin; Liu, Zishun

    2018-01-01

    The thermo-mechanical behavior of shape-memory polymers (SMPs) serves for the engineering applications of SMPs. Therefore the understanding of thermo-mechanical behavior of SMPs is of great importance. This paper investigates the influence of loading rate and loading level on the thermo-mechanical behavior of a thermosetting shape-memory polymer through experimental study. A series of cyclic tension tests and shape recovery tests at different loading conditions are performed to study the strain level and strain rate effect. The results of tension tests show that the thermosetting shape-memory polymer will behave as rubber material at temperature lower than the glass transition temperature (Tg) and it can obtain a large shape fix ratio at cyclic loading condition. The shape recovery tests exhibit that loading rate and loading level have little effect on the beginning and ending of shape recovery process of the thermosetting shape-memory polymer. Compared with the material which is deformed at temperature higher than Tg, the material deformed at temperature lower than Tg behaves a bigger recovery speed.

  7. Evaluation of thermo-mechanical properties data of carbon-based plasma facing materials

    International Nuclear Information System (INIS)

    Ulrickson, M.; Barabash, V.R.; Matera, R.; Roedig, M.; Smith, J.J.; Janev, R.K.

    1991-03-01

    This Report contains the proceedings, results and conclusions of the work done and the analysis performed during the IAEA Consultants' Meeting on ''Evaluation of thermo-mechanical properties data of carbon-based plasma facing materials'', convened on December 17-21, 1990, at the IAEA Headquarters in Vienna. Although the prime objective of the meeting was to critically assess the available thermo-mechanical properties data for certain types of carbon-based fusion relevant materials, the work of the meeting went well beyond this task. The meeting participants discussed in depth the scope and structure of the IAEA material properties database, the format of data presentation, the most appropriate computerized system for data storage, retrieval, exchange and management. The existing IAEA ALADDIN system was adopted as a convenient tool for this purpose and specific ALADDIN labelling schemes and dictionaries were established for the material properties data. An ALADDIN formatted test-file for the thermo-physical and thermo-mechanical properties of pyrolytic graphite is appended to this Report for illustrative purposes. (author)

  8. Effect of Water on the Thermo-Mechanical Behavior of Carbon Cloth Phenolic

    Science.gov (United States)

    Sullivan, Roy M.; Stokes, Eric; Baker, Eric H.

    2011-01-01

    The results of thermo-mechanical experiments, which were conducted previously by one of the authors, are reviewed. The strain in the direction normal to the fabric plane was measured as a function of temperature for a variety of initial moisture contents and heating rates. In this paper, the general features of the thermo-mechanical response are discussed and the effect of heating rate and initial moisture content are highlighted. The mechanical interaction between the phenolic polymer and water trapped within its free volumes as the polymer is heated to high temperatures is discussed. An equation for the internal stresses which are generated within the polymer due to trapped water is obtained from the total stress expression for a binary mixture of polymer and water. Numerical solutions for moisture diffusion in the thermo-mechanical experiments were performed and the results of these solutions are presented. The results of the moisture diffusion solutions help to explain the effects of heating rate and moisture content on the strain behavior normal to the fabric plane.

  9. Thermomechanical controls on magma supply and volcanic deformation: application to Aira caldera, Japan

    Science.gov (United States)

    Hickey, James; Gottsmann, Joachim; Nakamichi, Haruhisa; Iguchi, Masato

    2016-01-01

    Ground deformation often precedes volcanic eruptions, and results from complex interactions between source processes and the thermomechanical behaviour of surrounding rocks. Previous models aiming to constrain source processes were unable to include realistic mechanical and thermal rock properties, and the role of thermomechanical heterogeneity in magma accumulation was unclear. Here we show how spatio-temporal deformation and magma reservoir evolution are fundamentally controlled by three-dimensional thermomechanical heterogeneity. Using the example of continued inflation at Aira caldera, Japan, we demonstrate that magma is accumulating faster than it can be erupted, and the current uplift is approaching the level inferred prior to the violent 1914 Plinian eruption. Magma storage conditions coincide with estimates for the caldera-forming reservoir ~29,000 years ago, and the inferred magma supply rate indicates a ~130-year timeframe to amass enough magma to feed a future 1914-sized eruption. These new inferences are important for eruption forecasting and risk mitigation, and have significant implications for the interpretations of volcanic deformation worldwide. PMID:27619897

  10. Thermomechanical controls on magma supply and volcanic deformation: application to Aira caldera, Japan.

    Science.gov (United States)

    Hickey, James; Gottsmann, Joachim; Nakamichi, Haruhisa; Iguchi, Masato

    2016-09-13

    Ground deformation often precedes volcanic eruptions, and results from complex interactions between source processes and the thermomechanical behaviour of surrounding rocks. Previous models aiming to constrain source processes were unable to include realistic mechanical and thermal rock properties, and the role of thermomechanical heterogeneity in magma accumulation was unclear. Here we show how spatio-temporal deformation and magma reservoir evolution are fundamentally controlled by three-dimensional thermomechanical heterogeneity. Using the example of continued inflation at Aira caldera, Japan, we demonstrate that magma is accumulating faster than it can be erupted, and the current uplift is approaching the level inferred prior to the violent 1914 Plinian eruption. Magma storage conditions coincide with estimates for the caldera-forming reservoir ~29,000 years ago, and the inferred magma supply rate indicates a ~130-year timeframe to amass enough magma to feed a future 1914-sized eruption. These new inferences are important for eruption forecasting and risk mitigation, and have significant implications for the interpretations of volcanic deformation worldwide.

  11. Thermal/thermomechanical analyses for the room region with horizontal and vertial modes of emplacement

    International Nuclear Information System (INIS)

    1988-01-01

    Extensive thermal/thermomechanical analyses of the Site Characterization Plan-Conceptual Design at the Deaf Smith county Site, Texas, have been carried out for the room region with horizontal and vertical modes of emplacement. The main purpose of this study is to make a good comparison between these two modes of emplacement in this region. Homogeneous and nonhomogeneous strata under isothermal or transient temperature conditions cases were considered in the analyses. Furthermore, various pillar widths for the vertical mode emplacement were also taken into consideration. Only spent fuel (SF) waste was considered in this study. Finite element method was used throughout the analyses. The thermal responses were evaluated using SPECTROM-41 while the thermomechanical responses were calculated using SPECTROM-32. Thermal and thermomechanical comparisons between the two modes of emplacement for various cases were presented in this paper

  12. Prediction of thermo-mechanical reliability of wafer backend processes

    NARCIS (Netherlands)

    Gonda, V.; Toonder, den J.M.J.; Beijer, J.G.J.; Zhang, G.Q.; van Driel, W.D.; Hoofman, R.J.O.M.; Ernst, L.J.

    2004-01-01

    More than 65% of IC failures are related to thermal and mechanical problems. For wafer backend processes, thermo-mechanical failure is one of the major bottlenecks. The ongoing technological trends like miniaturization, introduction of new materials, and function/product integration will increase

  13. Prediction of thermo-mechanical integrity of wafer backend processes

    NARCIS (Netherlands)

    Gonda, V.; Toonder, den J.M.J.; Beijer, J.G.J.; Zhang, G.Q.; Hoofman, R.J.O.M.; Ernst, L.J.; Ernst, L.J.

    2003-01-01

    More than 65% of IC failures are related to thermal and mechanical problems. For wafer backend processes, thermo-mechanical failure is one of the major bottlenecks. The ongoing technological trends like miniaturization, introduction of new materials, and function/product integration will increase

  14. Design of an Annular Disc Subject to Thermomechanical Loading

    Directory of Open Access Journals (Sweden)

    Sergei Alexandrov

    2012-01-01

    Full Text Available Two solutions to design a thin annular disc of variable thickness subject to thermomechanical loading are proposed. It is assumed that the thickness of the disc is everywhere sufficiently small for the stresses to be averaged through the thickness. The state of stress is plane. The initiation of plastic yielding is controlled by Mises yield criterion. The design criterion for one of the solutions proposed requires that the distribution of stresses is uniform over the entire disc. In this case there is a relation between optimal values of the loading parameters at the final stage. The specific shape of the disc corresponds to each pair of such parameters. The other solution is obtained under the additional requirement that the distribution of strains is uniform. This solution exists for the disc of constant thickness at specific values of the loading parameters.

  15. Thermal and thermo-mechanical simulation of laser assisted machining

    International Nuclear Information System (INIS)

    Germain, G.; Dal Santo, P.; Lebrun, J. L.; Bellett, D.; Robert, P.

    2007-01-01

    Laser Assisted Machining (LAM) improves the machinability of materials by locally heating the workpiece just prior to cutting. The heat input is provided by a high power laser focused several millimeters in front of the cutting tool. Experimental investigations have confirmed that the cutting force can be decreased, by as much as 40%, for various materials (tool steel, titanium alloys and nickel alloys). The laser heat input is essentially superficial and results in non-uniform temperature profiles within the depth of the workpiece. The temperature field in the cutting zone is therefore influenced by many parameters. In order to understand the effect of the laser on chip formation and on the temperature fields in the different deformation zones, thermo-mechanical simulation were undertaken. A thermo-mechanical model for chip formation with and without the laser was also undertaken for different cutting parameters. Experimental tests for the orthogonal cutting of 42CrMo4 steel were used to validate the simulation via the prediction of the cutting force with and without the laser. The thermo-mechanical model then allowed us to highlight the differences in the temperature fields in the cutting zone with and without the laser. In particular, it was shown that for LAM the auto-heating of the material in the primary shear zone is less important and that the friction between the tool and chip also generates less heat. The temperature fields allow us to explain the reduction in the cutting force and the resulting residual stress fields in the workpiece

  16. Proceedings of the first thermomechanical workshop for shale

    International Nuclear Information System (INIS)

    1986-03-01

    Chapter 2 provides a description of the three federal regulations that pertain to the development of a high-level nuclear waste repository regardless of the rock type. Chapter 3 summarizes the reference shale repository conditions selected for this workshop. A room-and-pillar configuration was considered at an extraction ratio of about 0.25. The depth was assumed to be 700 m. Chapter 4 gives a summary of several case histories that were considered to be valuable in gaining an understanding of some of the design and construction features that might be unique in creating underground openings in shale. Chapter 5 assesses the data and information needs, availability, technology for acquisition, and the research and development necessary for analytical/numerical modeling in heat transfer, fluid flow, and thermomechanics. Chapter 6 assesses data and information needs in the laboratory and considerations associated with shale rock characterization. Chapter 7 assesses the data and information needs, availability, technology for acquisition, and the research and development necessary for field/in situ testing. Chapter 8 presents the consensus of the workshop participants that there is a definite need to advance the state of knowledge concerning the thermomechanical behavior of shales and to gain experience in applying this knowledge to the design of room-and-pillar excavations. Finally, Chapter 9 provides a summary of the research and development needs in the various interacting activities of repository development, including analytical/numerical modeling, laboratory testing, and field/in situ testing. The main conclusion of the workshop was that a need exists for an aggressive program in laboratory, field, numerical modeling, and design studies to provide a thermomechanical, technological base for comparison of shale types and shale regions/areas/sites

  17. Effect of cerium and thermomechanical processing on microstructure

    Indian Academy of Sciences (India)

    The effect of cerium content and thermomechanical processing on structure and properties of Fe–10.5 wt.%Al–0.8 wt%C alloy has been investigated. Alloys were prepared by a combination of air induction melting with flux cover (AIMFC) and electroslag remelting (ESR). The ESR ingots were hot-forged and hotrolled at ...

  18. Numerical characterization of thermo-mechanical performance of breeder pebble beds

    International Nuclear Information System (INIS)

    An, Zhiyong; Ying, Alice; Abdou, Mohamed

    2007-01-01

    A numerical approach using the discrete element method (DEM) has been applied to study the thermo-mechanical properties of ceramic breeder pebble beds. This numerical scheme is able to predict the inelastic behavior observed in a loading and unloading operation. In addition, it demonstrates that the average value of contact force increases linearly with overall pressure, but at a much faster rate, about 3.4 times the overall pressure increase rate. In this paper, the thermal creep properties of two different ceramic breeder pebble materials, Li 4 SiO 4 and Li 2 O, are also examined by the current numerical code. The difference found in the properties of candidate materials is reflected numerically in the overall strain in the pebble bed when the stress magnitude becomes smaller

  19. Numerical characterization of thermo-mechanical performance of breeder pebble beds

    International Nuclear Information System (INIS)

    An, Zhiyong; Ying, Alice; Abdou, Mohamed

    2008-01-01

    A numerical approach using the discrete element method (DEM) has been applied to study the thermo-mechanical properties of ceramic breeder pebble beds. This numerical scheme is able to predict the inelastic behavior observed in a loading and unloading operation. In addition, it demonstrates that the average value of contact force increases linearly with overall pressure, but at a much faster rate, about 3.4 times the overall pressure increase rate. In this paper, the thermal creep properties of two different ceramic breeder pebble materials, Li 4 SiO 4 and Li 2 O, are also examined by the current numerical code. The difference found in the properties of candidate materials is reflected numerically in the overall strain in the pebble bed when the stress magnitude becomes smaller. (author)

  20. The thermomechanical stability of micro-solid oxide fuel cells fabricated on anodized aluminum oxide membranes

    Science.gov (United States)

    Kwon, Chang-Woo; Lee, Jae-Il; Kim, Ki-Bum; Lee, Hae-Weon; Lee, Jong-Ho; Son, Ji-Won

    2012-07-01

    The thermomechanical stability of micro-solid oxide fuel cells (micro-SOFCs) fabricated on an anodized aluminum oxide (AAO) membrane template is investigated. The full structure consists of the following layers: AAO membrane (600 nm)/Pt anode/YSZ electrolyte (900 nm)/porous Pt cathode. The utilization of a 600-nm-thick AAO membrane significantly improves the thermomechanical stability due to its well-known honeycomb-shaped nanopore structure. Moreover, the Pt anode layer deposited in between the AAO membrane and the YSZ electrolyte preserves its integrity in terms of maintaining the triple-phase boundary (TPB) and electrical conductivity during high-temperature operation. Both of these results guarantee thermomechanical stability of the micro-SOFC and extend the cell lifetime, which is one of the most critical issues in the fabrication of freestanding membrane-type micro-SOFCs.

  1. A Numerical Model for the Thermomechanical Conditions During Hydration of Early-age Concrete

    DEFF Research Database (Denmark)

    Hattel, Jesper; Thorborg, Jesper

    2003-01-01

    In the present study, a macroscopic numerical model for the thermomechanical conditions during hydration of early-age concrete is presented. The formulation is based on a semi-coupled, incremental thermomechanical model where the heat production from the hydration process is expressed in terms...... of the maturity and the thermal activation is expressed by the Arrhenius principle. The material properties are assumed to depend on the hydration process via the maturity. The discretization of the governing equations is accomplished by a control volume formulation involving a time-splitting scheme for the heat...

  2. ITER baffle module small-scale mock-ups: first wall thermo-mechanical testing results

    International Nuclear Information System (INIS)

    Severi, Y.; Giancarli, L.; Poitevin, Y.; Salavy, J.F.; Le Marois, G.; Roedig, M.; Vieider, G.

    1998-01-01

    The EU-home team is in charge of the R and D related to the ITER baffle first wall. Five small-scale mock-ups, using Be, CFC and W tiles and different armour/heat-sink material joints under development, have been fabricated and thermomechanically tested in FE200 (Le Creusot) and JUDITH (Juelich) electron beam facilities. The small-scale mock-ups have been submitted to thermo-mechanical fatigue tests (up to failure using accelerating techniques). The objective was to determine the performances of the armour material joints under high heat flux cycles. (orig.)

  3. TEM characterization on new 9% Cr advanced steels thermomechanical treated after tempering

    Science.gov (United States)

    Fernández, P.; Hoffmann, J.; Rieth, M.; Roldán, M.; Gómez-Herrero, A.

    2018-03-01

    Phase transformation on new six reduced activation ferritic/martensitic steels (RAFMs) was investigated to provide the basis for the design and development of advanced steels to maintain adequate strength and creep resistance above 500 °C. The new alloys are designed to increase the amount of fine MX precipitates and reduce coarse M23C6 carbides through alloy composition refinement and the application of thermomechanical treatments. The microstructural investigations by TEM have shown M23C6, M2X, and MX precipitation after tempering at 700 °C/2h with low dislocation recovery, while at 825 °C/2h the martensite developed to subgrain formation and growth. At this stage, only M23C6 and MX were detected. Preliminary results demonstrate that it is feasible to produce fine MX strengthened particles dispersed in the matrix with further optimization of tempering treatments.

  4. ISOTHERMAL AND THERMOMECHANICAL FATIGUE OF A NICKEL-BASE SUPERALLOY

    Directory of Open Access Journals (Sweden)

    Carlos Carvalho Engler-Pinto Júnior

    2014-06-01

    Full Text Available Thermal gradients arising during transient regimes of start-up and shutdown operations produce a complex thermal and mechanical fatigue loading which limits the life of turbine blades and other engine components operating at high temperatures. More accurate and reliable assessment under non-isothermal fatigue becomes therefore mandatory. This paper investigates the nickel base superalloy CM 247LC-DS under isothermal low cycle fatigue (LCF and thermomechanical fatigue (TMF. Test temperatures range from 600°C to 1,000°C. The behavior of the alloy is strongly affected by the temperature variation, especially in the 800°C-1,000°C range. The Ramberg-Osgood equation fits very well the observed isothermal behavior for the whole temperature range. The simplified non-isothermal stress-strain model based on linear plasticity proposed to represent the thermo-mechanical fatigue behavior was able to reproduce the observed behavior for both in-phase and out-of-phase TMF cycling.

  5. Mechanical and thermomechanical properties of polycarbonate-based polyurethane-silica nanocomposites

    Directory of Open Access Journals (Sweden)

    Rafał Poręba

    2011-09-01

    Full Text Available In this work aliphatic polycarbonate-based polyurethane-silica nanocomposites were synthesized and characterized. The influence of the type and of the concentration of nanofiller differing in average particle size (7 nm for Aerosil 380 and 40 nm for Nanosilica 999 on mechanical and thermomechanical properties was investigated. DMTA measurements showed that Nanosilica 999, irrespective of its concentration, slightly increased the value of the storage shear modulus G’ but Aerosil 380 brings about a nearly opposite effect, the shear modulus in the rubber region decreases with increasing filler content. Very high elongations at break ranging from 800% to more than 1000%, as well as high tensile strengths illustrate excellent ultimate tensile properties of the prepared samples. The best mechanical and thermomechanical properties were found for the sample filled with 0.5 wt.% of Nanosilica 999.

  6. Damage evolution of TBC system under in-phase thermo-mechanical tests

    International Nuclear Information System (INIS)

    Kitazawa, R.; Tanaka, M.; Kagawa, Y.; Liu, Y.F.

    2010-01-01

    In-phase thermo-mechanical tests (TMF) of EB-PVD Y 2 O 3 -ZrO 2 thermal barrier coating (TBC) system (8 wt% Y 2 O 3 -ZrO 2 /CoNiCrAlY/IN-738 substrate) were done under a through-the-thick-direction thermal gradient from TBC surface temperature at 1150 deg. C to substrate temperature at 1000 deg. C. Deformation and failure behaviors of the TBC system were observed at the macroscopic and microscopic scales and damage evolution of the system under in-phase thermo-mechanical test was discussed. Special attention was paid to TBC layer cracking, thermally grown oxide (TGO) layer formation and void formation in bond coat and substrate. Effect of TMF conditions on the damage evolution behaviors was also discussed.

  7. Thermo-mechanical processing of a Ti 49.5Al 1.25Ag alloy

    Energy Technology Data Exchange (ETDEWEB)

    Duarte, A.; Viana, F.; Vieira, M.F.; Santos, H.M.C. [GMM/IMAT, Dept. de Engenharia Metalurgica e de Materiais, FEUP, Porto (Portugal)

    2002-07-01

    Gamma titanium aluminide is an important candidate to several applications in the aerospace and automotive industries. The great drawback of these alloys is its low ductility at room temperature. This work is part of a study that intends to increase the ductility of gamma titanium aluminide through the addition of alloying elements. In this paper the effects of the heat treatment and the deformation processing on the microstructure of a Ti 49.5Al 1.25Ag are described. The alloy was produced by arc melting, under an argon atmosphere, using a water-cooled copper crucible. The as-cast samples were heat treated at 1300 and 1400 C. Encapsulated samples were deformed by double forging and multiple step rolling. The as-cast {gamma}-TiAl alloy presented an extended degree of segregation, have been detected three microconstituents: lamellar dendrites, interdendritic Al enriched {gamma}-phase and a number of Ag rich particles located at the dendritic/interdendritic interface. The heat treatment at 1400 C for 6 hours allowed the elimination of the as-cast microstructure and its replacement by a fully lamellar one. The thermomechanical processing produced non-homogenous microstructures of deformed lamellar grains and recrystallized gamma grains. The microstructure changes occurring during the several stages of the processing were characterized using optical and scanning electron microscopy. The modification of the chemical composition of the phases was determined using SEM-EDS facilities. (orig.)

  8. Modelling of the thermomechanical behaviour of salt rock

    International Nuclear Information System (INIS)

    Albers, G.; Graefe, V.; Korthaus, E.; Pudewillis, A.; Prij, J.

    1986-01-01

    The modelling of the thermomechanical behaviour of salt rock is examined, with respect to the disposal of radioactive waste in salt formations. The calculation methods and programmes currently available for the modelling are described. Some examples are given of calculations carried out in parallel with tests. Some results of modelling calculations for a repository are presented by way of illustration. (U.K.)

  9. Uncertainty analysis of a one-dimensional constitutive model for shape memory alloy thermomechanical description

    DEFF Research Database (Denmark)

    Oliveira, Sergio A.; Savi, Marcelo A.; Santos, Ilmar F.

    2014-01-01

    The use of shape memory alloys (SMAs) in engineering applications has increased the interest of the accuracy analysis of their thermomechanical description. This work presents an uncertainty analysis related to experimental tensile tests conducted with shape memory alloy wires. Experimental data...... are compared with numerical simulations obtained from a constitutive model with internal constraints employed to describe the thermomechanical behavior of SMAs. The idea is to evaluate if the numerical simulations are within the uncertainty range of the experimental data. Parametric analysis is also developed...

  10. Cyclic life of superalloy IN738LC under in-phase and out-of-phase thermo-mechanical fatigue loading

    International Nuclear Information System (INIS)

    Chen Hongjun; Wahi, R.P.; Wever, H.

    1995-01-01

    The cyclic life of IN738LC, a widely used nickel base superalloy for blades in stationary gas turbines, was investigated under thermo-mechanical fatigue loading using a temperature variation range of 1023 to 1223 K, with temperature variation rate in the range of 6 to 15 K/min. Simple thermo-mechanical cycles with linear sequences corresponding to in-phase (IP) and out-of-phase (OP) tests were performed. Both the IP and OP tests were carried out at different constant mechanical strain ranges varied between 0.8 to 2.0% and at a constant mechanical strain rate of 10 -5 s -1 . Thermo-mechanical fatigue lives under both test conditions were compared with each other and with those of isothermal LCF tests at a temperature of 1223 K. The results show that the life under thermo-mechanical fatigue is strongly dependent on the nature of the test, i.e. stress controlled or strain controlled. (orig.)

  11. Hybrid poly(lactic acid)/nanocellulose/nanoclay composites with synergistically enhanced barrier properties and improved thermomechanical resistance

    DEFF Research Database (Denmark)

    Trifol Guzman, Jon; Plackett, David; Sillard, Cecile

    2016-01-01

    Poly(lactic acid) (PLA)‐based hybrid nanocomposites (PLA, nanoclay and nanocellulose) were prepared by reinforcing neat PLA with commercially available nanoclay (Cloisite C30B) and nanocellulose, in the form of either partially acetylated cellulose nanofibres (CNFs) or nanocrystalline cellulose......) through a reduction of up to 90% in OTR and a further reduction in the water vapour transmission rate of up to 76%. In addition, the nanocomposite films showed improved thermomechanical resistance and improved crystallisation kinetics while maintaining high film transparency. This makes the hybrid PLA...

  12. Transformation-induced plasticity in multiphase steels subjected to thermomechanical loading

    NARCIS (Netherlands)

    Tjahjanto, D.D.; Turteltaub, S.R.; Suiker, A.S.J.; Zwaag, van der S.

    2008-01-01

    The behaviour of transformation-induced plasticity steels subjected to combined thermomechanical loading is studied at the microscale by means of numerical simulations. The microstructure is composed of an austenitic phase that may deform plastically and/or transform into martensite, and a ferritic

  13. Thermomechanical Morphology of Peas and Its Relation to Fracture Behaviour

    NARCIS (Netherlands)

    Pelgrom, P.J.M.; Schutyser, M.A.I.; Boom, R.M.

    2013-01-01

    Milling and subsequent air classification can be exploited for production of functional protein-enriched fractions from legumes and grains. Fracture behaviour is of large relevance to optimal disentanglement of protein and starch and is determined by the thermomechanical morphology of the seeds.

  14. Characterization of Irreversible Fouling after Ultrafiltration of Thermomechanical Pulp Mill Process Water

    DEFF Research Database (Denmark)

    Thuvander, Johan; Zarebska, Agata; Hélix-Nielsen, Claus

    2018-01-01

    process streams is fouling of the membranes. Fouling not only increases operating costs but also reduces the operating time of the membrane plant. When optimizing the membrane cleaning method, it is important to know which compounds cause the fouling. In this work fouling of an ultrafiltration membrane...... was studied. The fouling propensity of untreated process water and microfiltrated process water was compared. Fouled membranes were analyzed using scanning electron microscopy and attenuated total reflection Fourier transform infrared spectrometry. Acid hydrolysis of membranes exposed to untreated process......Large volumes of wastewater with dissolved wood components are treated in wastewater treatment plants at thermomechanical pulp mills. It has been shown previously that hemicelluloses in these wastewater streams can be recovered by membrane filtration. A serious obstacle when treating lignocellulose...

  15. Fracture mechanics in new designed power module under thermo-mechanical loads

    Directory of Open Access Journals (Sweden)

    Durand Camille

    2014-06-01

    Full Text Available Thermo-mechanically induced failure is a major reliability issue in the microelectronic industry. On this account, a new type of Assembly Interconnected Technology used to connect MOSFETs in power modules has been developed. The reliability is increased by using a copper clip soldered on the top side of the chip, avoiding the use of aluminium wire bonds, often responsible for the failure of the device. Thus the new designed MOSFET package does not follow the same failure mechanisms as standard modules. Thermal and power cycling tests were performed on these new packages and resulting failures were analyzed. Thermo-mechanical simulations including cracks in the aluminium metallization and intermetallics (IMC were performed using Finite Element Analysis in order to better understand crack propagation and module behaviour.

  16. Damage evolution of TBC system under in-phase thermo-mechanical tests

    Energy Technology Data Exchange (ETDEWEB)

    Kitazawa, R.; Tanaka, M.; Kagawa, Y. [Research Center for Advanced Science and Technology, University of Tokyo, 4-6-1 Komaba, Meguro-ku, Tokyo 153-8904 (Japan); Liu, Y.F., E-mail: yfliu@hyper.rcast.u-tokyo.ac.jp [Research Center for Advanced Science and Technology, University of Tokyo, 4-6-1 Komaba, Meguro-ku, Tokyo 153-8904 (Japan)

    2010-10-15

    In-phase thermo-mechanical tests (TMF) of EB-PVD Y{sub 2}O{sub 3}-ZrO{sub 2} thermal barrier coating (TBC) system (8 wt% Y{sub 2}O{sub 3}-ZrO{sub 2}/CoNiCrAlY/IN-738 substrate) were done under a through-the-thick-direction thermal gradient from TBC surface temperature at 1150 deg. C to substrate temperature at 1000 deg. C. Deformation and failure behaviors of the TBC system were observed at the macroscopic and microscopic scales and damage evolution of the system under in-phase thermo-mechanical test was discussed. Special attention was paid to TBC layer cracking, thermally grown oxide (TGO) layer formation and void formation in bond coat and substrate. Effect of TMF conditions on the damage evolution behaviors was also discussed.

  17. New three-dimensional far-field potential repository thermomechanical calculations

    International Nuclear Information System (INIS)

    Hardy, M.P.; Bai, M.; Goodrich, R.R.; Lin, M.; Carlisle, S.; Bauer, S.J.

    1993-03-01

    The thermomechanical effect on the exploratory ramps, drifts, and shafts as a result of high-level nuclear waste disposal is examined using a three-dimensional thermo-elastic model. The repository layout modeled is based on the use of mechanical mining of all excavations with equivalent waste emplacement areal power densities of 57 and 80 kW/acre. Predicted temperatures and stress changes for the north and south access drifts, east main drift, east-west exploratory drift, the north and south Calico Hills access ramps, the Calico Hills north-south exploratory drift, and the optional exploratory studies facility and man and materials shafts are presented for times 10, 35, 50, 100, 300, 500, 1000, 2000, 5000, and 10,000 years after the start of waste emplacement. The study indicates that the east-west exploratory drift at the repository horizon is subject to the highest thermomechanical impact because it is located closest the buried waste canisters. For most exploratory openings, the thermally induced temperatures and stresses tend to reach the maximum magnitudes at approximately 1000 years after waste emplacement

  18. A study of thermo-mechanical stress and its impact on through-silicon vias

    International Nuclear Information System (INIS)

    Ranganathan, N; Balasubramanian, N; Prasad, K; Pey, K L

    2008-01-01

    The BOSCH etch process, which is commonly used in microelectromechanical system fabrication, has been extensively investigated in this work for implementation in through-silicon via (TSV) technology for 3D-microsystems packaging. The present work focuses on thermo-mechanical stresses caused by thermal loading due to post-TSV processes and their impact on the electrical performance of through-silicon copper interconnects. A test vehicle with deep silicon copper-plated comb structure was designed to study and evaluate different deep silicon via etch processes and its effect on the electrical leakage characteristics under various electrical and thermal stress conditions. It has been shown that the leakage current between the comb interconnect structures increases with an increase in sidewall roughness and that it can be significantly lowered by smoothening the sidewalls. It was also shown that by tailoring a non-BOSCH etch process with the normal BOSCH process, a similar leakage current reduction can be achieved. It was also shown through thermo-mechanical simulation studies that there is a clear correlation between high leakage current behavior due to non-uniform Ta barrier deposition over the rough sidewalls and the thermo-mechanical stress induced by post-TSV processes

  19. Thermomechanical behaviour of boom clay

    International Nuclear Information System (INIS)

    Sultan, N.; Delage, P.; Cui, Y.J.

    2000-01-01

    Special attention has been recently paid on temperature effects on the behaviour of deep saturated clays, in relation with nuclear deep waste storage. However, few experimental data are presently available, and existing constitutive models need to be completed. This note is aimed at completing, both experimentally and theoretically, the understanding of the effects of the over-consolidation ration on the thermal volume changes of Boom clay (Belgium). The experimental data obtained here are in a good agreement with existing data. As a complement to existing data, they are used to develop a new elastoplastic model. The adoption of a second coupled plastic mechanism provides good simulations on a complex thermo-mechanical path. (authors)

  20. Microstructural stability and thermomechanical processing of boron modified beta titanium alloys

    Science.gov (United States)

    Cherukuri, Balakrishna

    One of the main objectives during primary processing of titanium alloys is to reduce the prior beta grain size. Producing an ingot with smaller prior beta grain size could potentially eliminate some primary processing steps and thus reduce processing cost. Trace additions of boron have been shown to decrease the as-cast grain size in alpha + beta titanium alloys. The primary focus of this dissertation is to investigate the effect of boron on microstructural stability and thermomechanical processing in beta titanium alloys. Two metastable beta titanium alloys: Ti-15Mo-2.6Nb-3Al-0.2Si (Beta21S) and Ti-5Al-5V-5Mo-3Cr (Ti5553) with 0.1 wt% B and without boron additions were used in this investigation. Significant grain refinement of the as-cast microstructure and precipitation of TiB whiskers along the grain boundaries was observed with boron additions. Beta21S and Beta21S-0.1B alloys were annealed above the beta transus temperature for different times to investigate the effect of boron on grain size stability. The TiB precipitates were very effective in restricting the beta grain boundary mobility by Zener pinning. A model has been developed to predict the maximum grain size as a function of TiB size, orientation, and volume fraction. Good agreement was obtained between model predictions and experimental results. Beta21S alloys were solution treated and aged for different times at several temperatures below the beta transus to study the kinetics of alpha precipitation. Though the TiB phase did not provide any additional nucleation sites for alpha precipitation, the grain refinement obtained by boron additions resulted in accelerated aging. An investigation of the thermomechanical processing behavior showed different deformation mechanisms above the beta transus temperature. The non-boron containing alloys showed a non-uniform and fine recrystallized necklace structure at grain boundaries whereas uniform intragranular recrystallization was observed in boron containing

  1. Thermo-mechanical behavior of retro-reflector and resulting parallelism error of laser beams for Wendelstein 7-X interferometer

    International Nuclear Information System (INIS)

    Peng, X.B.; Hirsch, M.; Köppen, M.; Fellinger, J.; Bykov, V.; Schauer, F.; Vliegenthart, W.

    2014-01-01

    Highlights: • The criterion for thermo-mechanical design of W7-X interferometer retro-reflector. • Thermo-mechanical analysis of retro-reflector with two different methods. • The most flexible part in the retro-reflector is spring washer. • Calculation of parallelism error between the incoming and reflected laser beams. • The parallelism error is much lower than the design limit 28 arcs. - Abstract: A 10 channels interferometer will be used in the Wendelstein 7-X (W7-X) for plasma density control and density profile tracking with laser beams passing through the plasma. Due to complex shape of non-planar modular coils and divertor structure, there are no large poloidally opposite ports on the plasma vessel (PV). Therefore 10 in-vessel Corner Cube Retro-reflectors (CCRs) will be used. The CCRs are integrated in the water cooled heat shield and exposed directly to thermal loads from plasma radiation. Thermo-mechanical issues are very important for the design of the CCR because deformation and flatness as well as mutual angles of the three reflecting surfaces would affect the parallelism of the laser beams and the functionality of the interferometer. Intensive work has been done to explore a suitable design for the CCR concerning thermo-mechanical behavior. Previous studies Ye et al. (2008, 2009) and Köppen et al. (2011) focused on structural optimization to decrease thermal stress in the reflecting plates under the thermal loads, and on computation and check of curvature radii of the deformed reflecting surfaces with the design criterion that the curvature radius must be bigger than 200 m. The paper presents detailed thermo-mechanical analysis of the current improved CCR under thermal loads and bolt preloads. The results of the thermo-mechanical analysis were used for the study of the resulting parallelism error of the laser beams with newly developed and more reasonable design criterion

  2. Thermo-mechanical behavior of retro-reflector and resulting parallelism error of laser beams for Wendelstein 7-X interferometer

    Energy Technology Data Exchange (ETDEWEB)

    Peng, X.B., E-mail: pengxb@ipp.ac.cn [Institute of Plasma Physics, Chinese Academy of Sciences, P.O. Box 1126, 230031 Hefei Anhui (China); Max Planck Institute for Plasma Physics, EURATOM Association, Wendelsteinstr. 1, 17491 Greifswald (Germany); Hirsch, M.; Köppen, M.; Fellinger, J.; Bykov, V.; Schauer, F. [Max Planck Institute for Plasma Physics, EURATOM Association, Wendelsteinstr. 1, 17491 Greifswald (Germany); Vliegenthart, W. [TNO, Stieltjesweg 1, P.O. Box 2600, 2628 CK Delft (Netherlands)

    2014-04-15

    Highlights: • The criterion for thermo-mechanical design of W7-X interferometer retro-reflector. • Thermo-mechanical analysis of retro-reflector with two different methods. • The most flexible part in the retro-reflector is spring washer. • Calculation of parallelism error between the incoming and reflected laser beams. • The parallelism error is much lower than the design limit 28 arcs. - Abstract: A 10 channels interferometer will be used in the Wendelstein 7-X (W7-X) for plasma density control and density profile tracking with laser beams passing through the plasma. Due to complex shape of non-planar modular coils and divertor structure, there are no large poloidally opposite ports on the plasma vessel (PV). Therefore 10 in-vessel Corner Cube Retro-reflectors (CCRs) will be used. The CCRs are integrated in the water cooled heat shield and exposed directly to thermal loads from plasma radiation. Thermo-mechanical issues are very important for the design of the CCR because deformation and flatness as well as mutual angles of the three reflecting surfaces would affect the parallelism of the laser beams and the functionality of the interferometer. Intensive work has been done to explore a suitable design for the CCR concerning thermo-mechanical behavior. Previous studies Ye et al. (2008, 2009) and Köppen et al. (2011) focused on structural optimization to decrease thermal stress in the reflecting plates under the thermal loads, and on computation and check of curvature radii of the deformed reflecting surfaces with the design criterion that the curvature radius must be bigger than 200 m. The paper presents detailed thermo-mechanical analysis of the current improved CCR under thermal loads and bolt preloads. The results of the thermo-mechanical analysis were used for the study of the resulting parallelism error of the laser beams with newly developed and more reasonable design criterion.

  3. Martensitic transformation and residual stresses after thermomechanical treatment of heat treatable steel 42CrMo4 (SAE 4140)

    Energy Technology Data Exchange (ETDEWEB)

    Weise, A. [Technische Univ. Chemnitz-Zwickau, Chemnitz (Germany). Fakultaet fuer Maschinenbau und Verfahrenstechnik; Fritsche, G. [Technische Univ. Chemnitz-Zwickau, Chemnitz (Germany). Fakultaet fuer Maschinenbau und Verfahrenstechnik

    1996-01-01

    The influence of thermomechanical deformation on the residual stresses caused by quenching in bar shaped specimens of heat treatable steel 42CrMo4 has been investigated using a mechanical method for determining the distribution of residual stresses of the first kind. The results obtained show that the residual stress distribution after quenching is affected by the strengthening and softening of the austenite as a result of deformation and recrystallization and the modified transformation behaviour in martensite stage. An attempt is made to discuss qualitatively the influence of these changes on the generation of residual stresses as compared to results obtained after conventional hardening. (orig.).

  4. Martensitic transformation and residual stresses after thermomechanical treatment of heat treatable steel 42CrMo4 (SAE 4140)

    International Nuclear Information System (INIS)

    Weise, A.; Fritsche, G.

    1996-01-01

    The influence of thermomechanical deformation on the residual stresses caused by quenching in bar shaped specimens of heat treatable steel 42CrMo4 has been investigated using a mechanical method for determining the distribution of residual stresses of the first kind. The results obtained show that the residual stress distribution after quenching is affected by the strengthening and softening of the austenite as a result of deformation and recrystallization and the modified transformation behaviour in martensite stage. An attempt is made to discuss qualitatively the influence of these changes on the generation of residual stresses as compared to results obtained after conventional hardening. (orig.)

  5. Application of an enriched FEM technique in thermo-mechanical contact problems

    Science.gov (United States)

    Khoei, A. R.; Bahmani, B.

    2018-02-01

    In this paper, an enriched FEM technique is employed for thermo-mechanical contact problem based on the extended finite element method. A fully coupled thermo-mechanical contact formulation is presented in the framework of X-FEM technique that takes into account the deformable continuum mechanics and the transient heat transfer analysis. The Coulomb frictional law is applied for the mechanical contact problem and a pressure dependent thermal contact model is employed through an explicit formulation in the weak form of X-FEM method. The equilibrium equations are discretized by the Newmark time splitting method and the final set of non-linear equations are solved based on the Newton-Raphson method using a staggered algorithm. Finally, in order to illustrate the capability of the proposed computational model several numerical examples are solved and the results are compared with those reported in literature.

  6. Thermomechanical and Environmental Durability of Environmental Barrier Coated Ceramic Matrix Composites Under Thermal Gradients

    Science.gov (United States)

    Zhu, Dongming; Bhatt, Ramakrishna T.; Harder, Bryan

    2016-01-01

    This paper presents the developments of thermo-mechanical testing approaches and durability performance of environmental barrier coatings (EBCs) and EBC coated SiCSiC ceramic matrix composites (CMCs). Critical testing aspects of the CMCs will be described, including state of the art instrumentations such as temperature, thermal gradient, and full field strain measurements; materials thermal conductivity evolutions and thermal stress resistance; NDE methods; thermo-mechanical stress and environment interactions associated damage accumulations. Examples are also given for testing ceramic matrix composite sub-elements and small airfoils to help better understand the critical and complex CMC and EBC properties in engine relevant testing environments.

  7. Blanket Manufacturing Technologies : Thermomechanical Tests on HCLL Blanket Mocks Up

    International Nuclear Information System (INIS)

    Laffont, G.; Cachon, L.; Taraud, P.; Challet, F.; Rampal, G.; Salavy, J.F.

    2006-01-01

    In the Helium Cooled Lithium Lead (HCLL) Blanket concept, the lithium lead plays the double role of breeder and multiplier material, and the helium is used as coolant. The HCCL Blanket Module are made of steel boxes reinforced by stiffening plates. These stiffening plates form cells in which the breeder is slowly flowing. The power deposited in the breeder material is recovered by the breeder cooling units constituted by 5 parallel cooling plates. All the structures such as first wall, stiffening and cooling plates are cooled by helium. Due to the complex geometry of these parts and the high level of pressure and temperature loading, thermo-mechanical phenomena expected in the '' HCLL blanket concept '' have motivated the present study. The aim of this study, carried out in the frame of EFDA Work program, is to validate the manufacturing technologies of HCLL blanket module by testing small scale mock-up under breeder blanket representative operating conditions.The first step of this experimental program is the design and manufacturing of a relevant test section in the DIADEMO facility, which was recently upgraded with an He cooling loop (pressure of 80 bar, maximum temperature of 500 o C,flow rate of 30 g/s) taking the opportunity of synergies with the gas-cooled fission reactor R-and-D program. The second step will deal with the thermo-mechanical tests. This paper focuses on the program made to support the cooling plate mock up tests which will be carried out on the DIADEMO facility (CEA) by thermo-mechanical calculations in order to define the relevant test conditions and the experimental parameters to be monitored. (author)

  8. Development of ultrafine ferritic sheaves/plates in SAE 52100 steel for enhancement of strength by controlled thermomechanical processing

    Energy Technology Data Exchange (ETDEWEB)

    Chakraborty, J. [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur, W.B. 721 302 (India); Scientific Services and Research and Development, Tata Steel, Jamshedpur 831 001, Jharkhand (India); Manna, I., E-mail: imanna@metal.iitkgp.ernet.in [Department of Metallurgical and Materials Engineering, Indian Institute of Technology, Kharagpur, W.B. 721 302 (India); Central Glass and Ceramic Research Institute (CGCRI), Council of Scientific and Industrial Research (CSIR), 196 Raja S C Mullick Road, Jadavpur, Kolkata 700032 (India)

    2012-06-30

    Highlights: Black-Right-Pointing-Pointer Ultrafine bainite + martensite duplex microstructure developed in SAE 52100 steel. Black-Right-Pointing-Pointer Thermomechanical processing modifies size + morphology of bainitic ferrite. Black-Right-Pointing-Pointer Processing involves hot deformation prior to/during/after austenitizing. Black-Right-Pointing-Pointer Significant improvement in mechanical strength achieved. Black-Right-Pointing-Pointer Similar study on high carbon, low alloy steel not reported in the literature. - Abstract: The present study attempts to tailor the size, morphology and distribution of the ferrite needles/sheaves by thermomechanical processing and develop an ultrafine ferrite + martensite duplex microstructure for enhancement of strength and toughness in SAE 52100 steel. The thermo-mechanical routine included 5% hot deformation before, during or after austenitizing at 950 Degree-Sign C for 15 min followed by austempering at 270 Degree-Sign C for 30 min and subsequent water quenching to room temperature. Optical/electron microscopy along with X-ray diffraction was used to quantitatively monitor the size, morphology and distribution of the phase or phase aggregate. Significant improvement in nanohardness, wear resistance and elastic modulus and was observed in samples subjected to thermomechanical processing, as compared to that following the same austenitizing and austempering routine without hot deformation at any stage. However, improvement in the bulk mechanical property due to the present thermo-mechanical is lower than that obtained in our earlier study comprising cold deformation prior to austenitizing and austempering.

  9. Thermomechanical cycling and two-way memory effect induced in Cu-Zn-Al

    International Nuclear Information System (INIS)

    Pons, J.

    1999-01-01

    The two-way shape memory effect (TWME) has been induced by thermomechanical cycling in Cu-Zn-Al alloys using a dedicated hydraulic mechanical testing soft machine with complete computer control of force, elongation and temperature. The results concerning single crystals (composition Cu-16.9 wt.% Zn-7.7 wt.% Al, nominal M s of 273 K) and polycrystals (Cu-15.8 wt.% Zn-8.3 wt.% Al, nominal M s of 230 K, mean grain size of 1 mm) are reported for two training protocols (sequence of one thermomechanical cycle of education followed by one stress free thermal cycle to check the TWME or twenty consecutive thermomechanical cycles followed by one or two checking thermal cycles). The capacity of the trained specimen for producing work under an antagonist compressive stress is also studied and the behaviour of the deformation of the specimen under such a condition at different temperatures is analysed in terms of a competition between the contributions of the different variants: trained variants with an intrinsic deformation in the direction of the tensile stress of the training process, trained variants with an intrinsic deformation which is not well orientated with respect to this direction (in the polycrystal) and new variants with an intrinsic deformation in the direction of the compressive stress which can replace the educated variants. (orig.)

  10. Thermomechanical fatigue and damage mechanisms in Sanicro 25 steel

    Czech Academy of Sciences Publication Activity Database

    Petráš, Roman; Škorík, Viktor; Polák, Jaroslav

    2016-01-01

    Roč. 650, JAN (2016), s. 52-62 ISSN 0921-5093 R&D Projects: GA MŠk(CZ) EE2.3.30.0063; GA ČR(CZ) GA13-23652S Institutional support: RVO:68081723 Keywords : thermomechanical fatigue * Sanicro 25 steel * damage mechanism * FIB cutting * localized oxidation-cracking Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 3.094, year: 2016

  11. Thermo-Mechanical Fatigue Crack Growth of RR1000

    OpenAIRE

    Christopher John Pretty; Mark Thomas Whitaker; Steve John Williams

    2017-01-01

    Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechan...

  12. Progress in thermomechanical control of steel plates and their commercialization

    Science.gov (United States)

    Nishioka, Kiyoshi; Ichikawa, Kazutoshi

    2012-01-01

    The water-cooled thermomechanical control process (TMCP) is a technology for improving the strength and toughness of water-cooled steel plates, while allowing control of the microstructure, phase transformation and rolling. This review describes metallurgical aspects of the microalloying of steel, such as niobium addition, and discusses advantages of TMCP, for example, in terms of weldability, which is reduced upon alloying. Other covered topics include the development of equipment, distortions in steel plates, peripheral technologies such as steel making and casting, and theoretical modeling, as well as the history of property control in steel plate production and some early TMCP technologies. We provide some of the latest examples of applications of TMCP steel in various industries such as shipbuilding, offshore structures, building construction, bridges, pipelines, penstocks and cryogenic tanks. This review also introduces high heat-affected-zone toughness technologies, wherein the microstructure of steel is improved by the addition of fine particles of magnesium-containing sulfides and magnesium- or calcium-containing oxides. We demonstrate that thanks to ongoing developments TMCP has the potential to meet the ever-increasing demands of steel plates. PMID:27877477

  13. Progress in thermomechanical control of steel plates and their commercialization

    Directory of Open Access Journals (Sweden)

    Kiyoshi Nishioka and Kazutoshi Ichikawa

    2012-01-01

    Full Text Available The water-cooled thermomechanical control process (TMCP is a technology for improving the strength and toughness of water-cooled steel plates, while allowing control of the microstructure, phase transformation and rolling. This review describes metallurgical aspects of the microalloying of steel, such as niobium addition, and discusses advantages of TMCP, for example, in terms of weldability, which is reduced upon alloying. Other covered topics include the development of equipment, distortions in steel plates, peripheral technologies such as steel making and casting, and theoretical modeling, as well as the history of property control in steel plate production and some early TMCP technologies. We provide some of the latest examples of applications of TMCP steel in various industries such as shipbuilding, offshore structures, building construction, bridges, pipelines, penstocks and cryogenic tanks. This review also introduces high heat-affected-zone toughness technologies, wherein the microstructure of steel is improved by the addition of fine particles of magnesium-containing sulfides and magnesium- or calcium-containing oxides. We demonstrate that thanks to ongoing developments TMCP has the potential to meet the ever-increasing demands of steel plates.

  14. Thermomechanical characterization of pure polycrystalline tantalum

    International Nuclear Information System (INIS)

    Rittel, D.; Bhattacharyya, A.; Poon, B.; Zhao, J.; Ravichandran, G.

    2007-01-01

    The thermomechanical behavior of pure polycrystalline tantalum has been characterized over a wide range of strain rates, using the recently developed shear compression specimen [D. Rittel, S. Lee, G. Ravichandran, Experimental Mechanics 42 (2002) 58-64]. Dynamic experiments were carried out using a split Hopkinson pressure bar, and the specimen's temperature was monitored throughout the tests using an infrared radiometer. The results of the mechanical tests confirm previous results on pure Ta. Specifically, in addition to its significant strain rate sensitivity, it was observed that pure Ta exhibits very little strain hardening at high strain rates. The measured temperature rise in the specimen's gauge was compared to theoretical predictions which assume a total conversion of the mechanical energy into heat (β = 1) [G.I. Taylor, H. Quinney, Proceedings of the Royal Society of London, vol. A, 1934, pp. 307-326], and an excellent agreement was obtained. This result confirms the previous result of Kapoor and Nemat-Nasser [R. Kapoor, S. Nemat-Nasser, Mech. Mater. 27 (1998) 1-12], while a different experimental approach was adopted here. The assumption that β = 1 is found to be justified in this specific case by the lack of dynamic strain hardening of pure Ta. However, this assumption should be limited to non-hardening materials, to reflect the fact that strain hardening implies that part of the mechanical energy is stored into the material's microstructure

  15. Thermomechanical interactions of particle bed-structural wall in a layered configuration. Pt. 1. Effect of particle bed thermal expansions

    International Nuclear Information System (INIS)

    Tehranian, F.

    1995-01-01

    Materials in the form of particle beds have been considered for shielding and tritium breeding as well as neutron multiplication in many of the conceptual reactor design studies. As the level of effort of the fusion blanket community in the area of out-of-pile and in-pile (ITER) testing of integrated test modules increases, so does the need for modelling capability for predicting the thermomechanical responses of the test modules under reactor environment.In this study, the thermomechanical responses of a particle bed-structural wall system in a layered configuration, subjected to bed temperature rise and/or external coolant pressure, were considered. Equations were derived which represent the dependence of the particle-to-particle and particle-to-wall contact forces and areas on the structural wall deformations and in turn on the thermomechanical loads. Using the derived equations, parametric analyses were performed to study the variations in the thermomechanical response quantities of a beryllium particle bed-stainless steel structural wall when subjected to thermomechanical loads. The results are presented in two parts. In Part I, presented in this paper, the derivation of the analytical equations and the effects of bed temperature rise are discussed. In Part II of this study, also presented in this symposium, the effects of external coolant pressure as well as the combined effects of bed temperature rise and coolant pressure on the thermomechanical responses are given.It is shown that, depending on the stiffness of the structural walls, uniform bed temperature rises in the range 100-400 C result in non-uniform effective thermal properties through the prticle bed and could increase the bed effective thermal conductivity by a factor of 2-5 and the bed-wall interface thermal conductance by even a larger factor. (orig.)

  16. Thermomechanical Processing of Structural Steels with Dilute Niobium Additions

    Science.gov (United States)

    Cui, Z.; Patel, J.; Palmiere, E. J.

    The recrystallisation behaviour of medium carbon steels with dilute Nb addition was investigated by means of plane strain compression tests and the observation of prior austenite microstructures during different deformation conditions. It was found that complete suppression of recrystallisation did not occur in the deformation temperature range investigated. At lower deformation temperatures, partial recrystallisation occurred in the higher Nb sample. This gives the potential to obtain a full suppression of recrystallisation at lower deformation temperatures.

  17. Thermomechanical Behavior of Monolithic SN-AG-CU Solder and Copper Fiber Reinforced Solders

    National Research Council Canada - National Science Library

    Reuse, Rolando

    2005-01-01

    .... The thermomechanical cycling in the solder causes numerous reliability challenges, mostly because of the mismatch of the coefficient of thermal expansion between the silicon chip and the substrate...

  18. Surface finishing and levelling of thermomechanically hardened rolled steel

    International Nuclear Information System (INIS)

    Grosval'd, V.G.; Bashchenko, A.P.; Grishkov, A.I.; Gutnik, M.V.; Kanevskij, B.L.; Nikozov, A.I.; Sedov, N.D.; Prosin, K.A.; Safonov, L.I.

    1975-01-01

    The finishing of high-strength merchant shapes from alloy steel was tried out under industrial conditions with the equipment of metallurgical plants. After thermomechanical hardening in the production line of the rolling mill, 30KhGSN2A and 40Kh1NVA steel rounds 32 and 31 mm in diameter were straightened on a two-roller straightening machine designed by the All-Union Scientific Research Institute for Metallurgical Machinery (VNII Metmash). This made possible subsequent turning and grinding of the rods. The conditions of straightening, turning and grinding have been worked so as to obtain thermomechanically strengthened and ground rolled products approximating the gauged and ground metal in shape geometry and surface finish. It is shown that the labour-consuming operation of turning can be eliminated by reducing the machining pass of the rolled product, and this lowers the labour required for the finishing operations by 75%. After grinding with 40- and 25-grain abrasive wheels, high strength rolled shapes were obtained with a diameter of 30-0.20 mm and a surface finish of class 6-5 satisfying the technical specifications. (author)

  19. Thermo-mechanical design of the extraction grids for RF negative ion source at HUST

    Energy Technology Data Exchange (ETDEWEB)

    Zuo, Chen; Liu, Kaifeng, E-mail: kfliuhust@hust.edu.cn; Li, Dong; Mei, Zhiyuan; Zhang, Zhe; Chen, Dezhi

    2017-01-15

    Highlights: • An extraction system with cooling channels has been designed for HUST negative ion source. • Corresponding heat loads onto three grids has been used in thermo-mechanical analysis. • The analysis results could be very useful for driving the engineering design. - Abstract: Huazhong University of Science and Technology (HUST) is developing a small radio frequency negative ion source experimental setup to promote research on neutral beam injection ion sources. The extraction system for the negative ion source is the key component to obtain the negative ions. The extraction system is composed of three grids: the plasma grid, the extraction grid and the grounded grid. Each grid is impacted by different heat loads. As the grids have to fulfil specific requirements regarding ion extraction, beam optics, and thermo-mechanical issues, grid cooling systems have been included for ensuring reliable operation. This paper focuses on the thermo-hydraulic and thermo-mechanical design of the grids. Finite element calculations have been carried out to analyse the temperature and deformation of the grids under heat loads using the fluid dynamics code CFX. Based on these results, the cooling circuit design and cooling parameters are optimised to satisfy the grid requirements.

  20. Preliminary AD-Horn Thermomechanical and Electrodynamic Simulations

    CERN Document Server

    AUTHOR|(CDS)2095747; Horvath, David; Calviani, Marco

    2016-01-01

    As part of the Antiproton Decelerator (AD) target area consolidation activities planned for LS2, it has been necessary to perform a comprehensive study of the thermo-structural behaviour of the AD magnetic horn during operation, in order to detail specific requirements for the upgrade projects and testing procedures. The present work illustrates the preliminary results of the finite element analysis carried out to evaluate the thermal and structural behaviour of the device, as well as the methodology used to model and solve the thermomechanical and electrodynamic simulations performed in the AD magnetic horn.

  1. A Thermomechanical Transport Approach and Application in Soil-Water System of Polluted Mining Areas considering the Three-Phase Coupling

    Directory of Open Access Journals (Sweden)

    Xuan Guo

    2016-01-01

    Full Text Available The thermomechanical transport approach includes the process of diffusing or the condition of being diffused, absorption/desorption, swell/shrink, equilibrium/nonequilibrium, and thermomechanical transport of contaminant in three phases of polluted mining soil which are discussed. The thermomechanical transport model of the contaminants transport in polluted soil is established, and its basic equations are given. Based on that, the distribution regularities of the contaminant seepage in water-soil system are discussed in detail and the sensitivities of parameters are analyzed. The study shows that the parameter has important influence on the contamination distribution and transportation in polluted soil-water system. The influence degree is also related to the action of seepage force directly.

  2. Thermal and thermo-mechanical behavior of butyl based rubber exposed to silicon oil at elevated temperature

    International Nuclear Information System (INIS)

    Ali, S.; Ramzan, S.; Raza, R.; Ahmed, F.; Hussain, R.; Ullah, S.; Ali, S.

    2013-01-01

    Silica reinforced rubbers are used as chemical resistant seals at high temperature. In this study the effect of alkali and silicon oil on the thermal and thermo-mechanical properties of the silica reinforced butyl rubber exposed as an interface between two liquid media at elevated temperature is investigated. Rubber bladder containing alkaline solution was immersed in silicon oil at 195+-5 degree C for multiple cycles and loss in its thermal, thermo-mechanical and mechanical properties were studied by TGA, DMA and Tinius Olsen Testing Machine supported by FTIR and Optical microscopy. It was observed that the thermal and thermo-mechanical properties of butyl rubber were negatively affected due to leaching out of silica filler embedded in an organic matrix at elevated temperature. The thermal stability of exposed rubber was decreased around 200 degree C and the loss of storage modulus was observed up to 99.5% at -59 degree C. (author)

  3. COMPARATIVE ANALYSIS OF MECHANICAL CHARACTERISTICS OF THE STEELS, APPLIED FOR PRODUCTION OF CHIPPING KNIVES, RECEIVED BY METHODS OF THERMAL AND THERMOMECHANICAL PROCESSINGS

    Directory of Open Access Journals (Sweden)

    A. V. Alifanov

    2014-01-01

    Full Text Available Results of researches of chemical composition of chipping knives of foreign and domestic producers are given in the article. Results of mechanical tests of samples with determination of temporary resistance, percentage elongation, ultimate strength at cross bending, bend from the various tool steels, subjected to heat treatment (tempering and thermomechanical processing with low tempering, are given. Recommendations on use of TO and TMO for investigated steels are given.

  4. Thermo-mechanical properties and integrity of metallic interconnects in microelectronics

    Science.gov (United States)

    Ege, Efe Sinan

    In this dissertation, combined numerical (Finite Element Method) and experimental efforts were undertaken to study thermo-mechanical behavior in microelectronic devices. Interconnects, including chip-level metallization and package-level solder joints, are used to join many of the circuit parts in modern equipment. The dissertation is structured into six independent studies after the introductory chapter. The first two studies focus on thermo-mechanical fatigue of solder joints. Thermo-mechanical fatigue, in the form of damage along a microstructurally coarsened region in tin-lead solder, is analyzed along with the effects of intermetallic morphology. Also, lap-shear testing is modeled to characterize the joint and to investigate the validity of experimental data from different solder and substrate geometries. In the third study, the effects of pre-machined holes on strain localization and overall ductility in bulk eutectic tin-lead alloy is examined. Finite element analyses, taking into account the viscoplastic response, were carried out to provide a mechanistic rationale to corroborate the experimental findings. The fourth study concerns chip-level copper interconnects. Various combinations of oxide and polymer-based low-k dielectric schemes, with and without the thin barrier layers surrounding the Cu line, are considered. Attention is devoted to the thermal stress and strain fields and their dependency on material properties, geometry, and modeling details. This study is followed by a chapter on atomistics of interface-mediated plasticity in thin metallic films. The objective is to gain fundamental insight into the underlying mechanisms affecting the mechanical response of nanoscale thin films. The final study investigates the effect of microstructural heterogeneity on indentation response, for the purpose of raising awareness of the uncertainties involved in applying indentation techniques in probing mechanical properties of miniaturized devices.

  5. Thermo-mechanical response of rigid plastic laminates for greenhouse covering

    Directory of Open Access Journals (Sweden)

    Silvana Fuina

    2016-09-01

    Full Text Available Innovation in the field of protected crops represents an argument of great applied and theoretical research attention due to constantly evolving technologies and automation for higher quality flower and vegetable production and to the corresponding environmental and economic impact. The aim of this paper is to provide an analysis of some thermomechanical properties of rigid polymeric laminates for greenhouses claddings, including innovative tests such as the thermographic ones. Four types of laminates have been analysed: two polycarbonates, a polymethylmethacrylate and a polyethylene terephthalate (PET. The tests gave interesting results on different important properties, such as radiometric properties, limit stresses, strains and ductility. Moreover, a direct comparison of infrared images and force elongation curves gave important information on the relation of the (localised or homogeneous damage evolution, with both an applicative and theoretical implication. Finally, even if to the authors knowledge at present there are no examples of using PET for covering greenhouses, the results of this paper indicates the thermomechanical and radiometric characteristics of this material make it interesting for agricultural applications.

  6. Thermo-mechanical analysis of RMP coil system for EAST tokamak

    International Nuclear Information System (INIS)

    Wang, Songke; Ji, Xiang; Song, Yuntao; Zhang, Shanwen; Wang, Zhongwei; Sun, Youwen; Qi, Minzhong; Liu, Xufeng; Wang, Shengming; Yao, Damao

    2014-01-01

    Highlights: • Thermal design requirements for EAST RMP coils are summarized. • Cooling parameters based on both theoretical and numerical solutions are determined. • Compromise between thermal design and structural design is made on number of turns. • Thermo-mechanical calculations are made to validate its structural performance. - Abstract: Resonant magnetic perturbation (RMP) has been proved to be an efficient approach on edge localized modes (ELMs) control, resistive wall mode (RWM) control, and error field correction (EFC), RMP coil system under design in EAST tokamak will realize the above-mentioned multi-functions. This paper focuses on the thermo-mechanical analysis of EAST RMP coil system on the basis of sensitivity analysis, both normal and off-normal working conditions are considered. The most characteristic set of coil system is chosen with a complete modelling by means of three-dimensional (3D) finite element method, thermo-hydraulic and thermal-structural performances are investigated adequately, both locally and globally. The compromise is made between thermal performance and structural design requirements, and the results indicate that the optimized design is feasible and reasonable

  7. Application of Laser Pulse Heating to Simulate Thermomechanical Damage at Gun Bore Surfaces

    National Research Council Canada - National Science Library

    Cote, Paul

    2003-01-01

    Laser pulse heating experiments were performed to provide insights into the thermomechanical damage effects that occur at the surface of coated and uncoated gun steel under cyclic rapid heating and cooling...

  8. Thermomechanical Impact of Polyurethane Potting on Gun Launched Electronics

    Directory of Open Access Journals (Sweden)

    A. S. Haynes

    2013-01-01

    Full Text Available Electronics packages in precision guided munitions are used in guidance and control units, mission computers, and fuze-safe-and-arm devices. They are subjected to high g-loads during gun launch, pyrotechnic shocks during flight, and high g-loads upon impact with hard targets. To enhance survivability, many electronics packages are potted after assembly. The purpose of the potting is to provide additional structural support and shock damping. Researchers at the US Army recently completed a series of dynamic mechanical tests on a urethane-based potting material to assess its behavior in an electronics assembly during gun launch and under varying thermal launch conditions. This paper will discuss the thermomechanical properties of the potting material as well as simulation efforts to determine the suitability of this potting compound for gun launched electronics. Simulation results will compare stresses and displacements for a simplified electronics package with and without full potting. An evaluation of the advantages and consequences of potting electronics in munitions systems will also be discussed.

  9. Towards thermomechanics of fractal media

    Science.gov (United States)

    Ostoja-Starzewski, Martin

    2007-11-01

    Hans Ziegler’s thermomechanics [1,2,3], established half a century ago, is extended to fractal media on the basis of a recently introduced continuum mechanics due to Tarasov [14,15]. Employing the concept of internal (kinematic) variables and internal stresses, as well as the quasiconservative and dissipative stresses, a field form of the second law of thermodynamics is derived. In contradistinction to the conventional Clausius Duhem inequality, it involves generalized rates of strain and internal variables. Upon introducing a dissipation function and postulating the thermodynamic orthogonality on any lengthscale, constitutive laws of elastic-dissipative fractal media naturally involving generalized derivatives of strain and stress can then be derived. This is illustrated on a model viscoelastic material. Also generalized to fractal bodies is the Hill condition necessary for homogenization of their constitutive responses.

  10. Effect of oxygen on the thermomechanical behavior of tantalum thin films during the β-α phase transformation

    International Nuclear Information System (INIS)

    Knepper, Robert; Stevens, Blake; Baker, Shefford P.

    2006-01-01

    Tantalum thin films were prepared in the metastable β phase, and their thermomechanical behaviors were investigated in situ in an ultrahigh vacuum environment. Controlled levels of oxygen were incorporated into the films either during deposition, by surface oxidation after deposition, or during thermomechanical testing. The transformation from the β phase to the stable α phase takes place in conjunction with a distinct increase in tensile stress. The thermomechanical behavior is strongly affected by the amount of oxygen to which the film is exposed and the method of exposure. Increasing oxygen content inhibits the phase transformation, requiring higher temperatures to reach completion. It is shown that the phase transformation takes place by a nucleation and growth process that is limited by growth. Changes in the activation energy for the phase transformation due to solute drag are estimated as a function of oxygen content and the mechanisms behind the stress evolution are elucidated

  11. The influence of thermomechanical processing on microstructural evolution of Ti600 titanium alloy

    International Nuclear Information System (INIS)

    Han Yuanfei; Zeng Weidong; Qi Yunlian; Zhao Yongqing

    2011-01-01

    Highlights: → Temperature and strain rate have great influence on the microstructure features. → The formation of sub-grain and dislocation wall is the typically microstructure features observed in the β single-phase. → The elongated lamellar α platelets kinked increasingly and break up under the α + β processing conditions. → The softening mechanisms of the Ti600 alloy hot compressed at 1000-1100 deg. C are mainly dynamic recovery. - Abstract: The influences of thermomechanical processing on microstructural evolution of Ti600 alloy were studied in the temperature range of 800-1100 deg. C, and at the strain rate of 0.001-10 s -1 . During the isothermal compression experiment, the flow stress-strain curves are examined in the β single-phase and in the α + β two-phase regions. The results show that the thermomechanical processing parameters have significant influences on the microstructure of Ti600 alloy, especially on the grain size, morphologies of α phase. Moreover, the microstructural evolution was analyzed by optical microstructure (OM) and transmission electron microscopy (TEM). It was found that typical of dynamic recovery and dynamic recrystallization phenomenon occurring in the thermomechanical processing. These results will optimize the microstructural control for hot working of Ti600 alloy and deepen the understanding of the flow softening mechanism of near-α titanium alloy.

  12. Global thermo-mechanical effects from a KBS-3 type repository

    International Nuclear Information System (INIS)

    Hakami, E.; Olofsson, Stig-Olof

    1998-01-01

    The objective of this study has been to identify the global thermo-mechanical effects in the bedrock hosting a nuclear waste repository. Numerical thermo-mechanical modeling using distinct element models was performed. The number of fracture zones, the heat intensity of the waste, the material properties of the rock mass and the boundary conditions of the models were varied. Different models for multi-level repositories were also analyzed and compared to the main single-level case. Further, the global influence from the excavation of repository tunnels and deposition holes was examined by introducing weaker rock mass material properties in the repository region of one model. The maximum compression stress obtained for the main model is 44 MPa and occurs at the repository level after about 100 years of deposition. Due to thermal expansion, the rock mass displaces upward, and the maximum heave at the ground surface after 1000 years is calculated to be 16 cm. In the area close to the ground surface the horizontal stresses reduce, causing the rock to yield in tension down to a depth of about 80 meters. The fracture zones show opening displacements at shallow depths and closing and shearing at the repository level. The maximum displacements are 0.3-2.5 cm for closing, 0.0-0.8 cm for opening and 0.2-2.2 cm for shearing. The resultant stresses and displacements depend in large part on the assumptions made concerning the heat intensity of the waste. In the main model, an initial heat intensity of 10 W/m 2 is assumed, which gives larger effects than the case with 6 W/m 2 . Another important input parameter for the analysis is the Young's modulus of the rock mass. In the main model, a value of 30 GPa is assumed. Higher values of Young's modulus give larger thermo-mechanical effects. All multi-level repository layouts give rise to higher temperatures than the single-level layout, causing the compressive stresses to increase more at the repository level. The multi

  13. Exact solution for stresses/displacements in a multilayered hollow cylinder under thermo-mechanical loading

    International Nuclear Information System (INIS)

    Yeo, W.H.; Purbolaksono, J.; Aliabadi, M.H.; Ramesh, S.; Liew, H.L.

    2017-01-01

    In this study, a new analytical solution by the recursive method for evaluating stresses/displacements in multilayered hollow cylinder under thermo-mechanical loading was developed. The results for temperature distribution, displacements and stresses obtained by using the proposed solution were shown to be in good agreement with the FEM results. The proposed analytical solution was also found to produce more accurate results than those by the analytical solution reported in literature. - Highlights: • A new analytical solution for evaluating stresses in multilayered hollow cylinder under thermo-mechanical loading. • A simple computational procedure using a recursive method. • A promising technique for evaluating the operating axial and hoop stresses in pressurized composite vessels.

  14. Manufacturing and thermomechanical testing of actively cooled all beryllium high heat flux test pieces

    International Nuclear Information System (INIS)

    Vasiliev, N.N.; Sokolov, Yu.A.; Shatalov, G.E.

    1995-01-01

    One of the problems affiliated to ITER high heat flux elements development is a problem of interface of beryllium protection with heat sink routinely made of copper alloys. To get rid of this problem all beryllium elements could be used as heat receivers in places of enhanced thermal loads. In accordance with this objectives four beryllium test pieces of two types have been manufactured in open-quotes Institute of Berylliumclose quotes for succeeding thermomechanical testing. Two of them were manufactured in accordance with JET team design; they are round open-quotes hypervapotron typeclose quotes test pieces. Another two ones are rectangular test sections with a twisted tape installed inside of the circular channel. Preliminary stress-strain analysis have been performed for both type of the test pieces. Hypervapotrons have been shipped to JET where they were tested on JET test bed. Thermomechanical testing of pieces of the type of open-quotes swirl tape inside of tubeclose quotes have been performed on Kurchatov Institute test bed. Chosen beryllium grade properties, some details of manufacturing, results of preliminary stress-strain analysis and thermomechanical testing of the test pieces open-quotes swirl tape inside of tubeclose quotes type are given in this report

  15. 39 CFR 3050.41 - Treatment of additional financial reports.

    Science.gov (United States)

    2010-07-01

    ... 39 Postal Service 1 2010-07-01 2010-07-01 false Treatment of additional financial reports. 3050.41... Treatment of additional financial reports. (a) For purposes of the reports required by § 3050.40(a)(2), the... § 3050.40(c) is fairly stated in all material respects, either in relation to the basic financial...

  16. Welding thermal cycle-triggered precipitation processes in steel S700MC subjected to the thermo-mechanical control processing

    OpenAIRE

    Górka J.

    2017-01-01

    This study presents tests concerned with welding thermal process-induced precipitation processes taking place in 10 mm thick steel S700MC subjected to the Thermo-Mechanical Control Process (TMCP) with accelerated cooling. The thermomechanical processing of steel S700MC leads to its refinement, structural defects and solutioning with hardening constituents. Tests of thin foils performed using a transmission electron microscope revealed that the hardening of steel S700MC was primarily caused by...

  17. Thermo-mechanical Densification of Populus tomentosa var. tomentosa with Low Moisture Content

    Directory of Open Access Journals (Sweden)

    Dengyun Tu

    2014-05-01

    Full Text Available This study used thermo-mechanical densification technology to compress low-moisture content (3~5% rapid-growth Populus tomentosa var. tomentosa trees to produce specimens with a low-compression ratio (small volume loss and a uniform density profile and desirable properties. Furthermore, the densified specimens were subjected to post-heat treatment at 180, 190, and 200 °C for 2, 3, and 4 h, respectively. Microscopic examination was performed to observe the changes that occurred in the wood vessels after densification. To determine the influence of post-heat treatment on the set recovery, the specimens were subjected to eight cycles of soaking and drying in 20 °C water and two cycles in boiling water. The density profile tendencies of the densified specimens were in accord with undensified specimens. Microscopic observation revealed that the deformations present in the densified wood resulted from the viscous buckling of cell walls without fracture. The volume of the void areas in the specimens decreased uniformly. Post-heat treatment can decrease compressive deformation, especially when applied at 200 °C for 4 h. After two boiling water cycles of soaking and drying, the densified wood still had a certain set recovery. Therefore, densified wood should be used sparingly in high temperature and high humidity environments.

  18. Drift-scale thermomechanical analysis for the retrievability systems study

    International Nuclear Information System (INIS)

    Tsai, F.C.

    1996-01-01

    A numerical method was used to estimate the stability of potential emplacement drifts without considering a ground support system as a part of the Thermal Loading Systems Study for the Yucca Mountain Site Characterization Project. The stability of the drift is evaluated with two variables: the level of thermal loading and the diameter of the emplacement drift. The analyses include the thermomechanical effects generated by the excavation of the drift, subsequently by the thermal loads from heat-emitting waste packages, and finally by the thermal reduction resulting from rapid cooling ventilation required for the waste retrieval if required. The Discontinuous Deformation Analysis (DDA) code was used to analyze the thermomechanical response of the rock mass of multiple blocks separated by joints. The result of this stability analysis is used to discuss the geomechanical considerations for the advanced conceptual design (ACD) with respect to retrievability. In particular, based on the rock mass strength of the host rock described in the current version of the Reference Information Base, the computed thermal stresses, generated by 111 MTU/acre thermal loads in the near field at 100 years after waste emplacement, is beyond the criterion for the rock mass strength used to predict the stability of the rock mass surrounding the emplacement drift

  19. Study of the Thermo-Mechanical Behavior of the CLIC Two-Beam Modules

    CERN Document Server

    Rossi, F; Riddone, G; Österberg, K; Kossyvakis, I; Gudkov, D; Samochkine, A

    2013-01-01

    The final luminosity target of the Compact LInear Collider (CLIC) imposes a micron-level stability requirement on the two-meter repetitive two-beam modules constituting the main linacs. Two-beam prototype modules are being assembled to extensively study their thermo-mechanical behaviour under different operation modes. The power dissipation occurring in the modules will be reproduced and the efficiency of the corresponding cooling systems validated. At the same time, the real environmental conditions present in the CLIC tunnel will be studied. Air conditioning and ventilation systems have been installed in the dedicated laboratory. The air temperature will be changed from 20 to 40°C, while the air flow rate will be varied up to 0.8 m/s. During all experimental tests, the alignment of the RF structures will be monitored to investigate the influence of power dissipation and air temperature on the overall thermo-mechanical behaviour. \

  20. Thermomechanical fatigue in single crystal superalloys

    Directory of Open Access Journals (Sweden)

    Moverare Johan J.

    2014-01-01

    Full Text Available Thermomechanical fatigue (TMF is a mechanism of deformation which is growing in importance due to the efficiency of modern cooling systems and the manner in which turbines and associated turbomachinery are now being operated. Unfortunately, at the present time, relatively little research has been carried out particularly on TMF of single crystal (SX superalloys, probably because the testing is significantly more challenging than the more standard creep and low cycle fatigue (LCF cases; the scarcity and relative expense of the material are additional factors. In this paper, the authors summarise their experiences on the TMF testing of SX superalloys, built up over several years. Emphasis is placed upon describing: (i the nature of the testing method, the challenges involved in ensuring that an given testing methodology is representative of engine conditions (ii the behaviour of a typical Re-containing second generation alloy such as CMSX-4, and its differing performance in out-of-phase/in-phase loading and crystallographic orientation and (iii the differences in behaviour displayed by the Re-containing alloys and new Re-free variants such as STAL15. It is demonstrated that the Re-containing superalloys are prone to different degradation mechanisms involving for example microtwinning, TCP precipitation and recrystallisation. The performance of STAL15 is not too inferior to alloys such as CMSX-4, suggesting that creep resistance itself does not correlate strongly with resistance to TMF. The implications for alloy design efforts are discussed.

  1. Finite elements for the thermomechanical calculation of massive structures

    International Nuclear Information System (INIS)

    Argyris, J.H.; Szimmat, J.; Willam, K.J.

    1978-01-01

    The paper examines the fine element analysis of thermal stress and deformation problems in massive structures. To this end compatible idealizations are utilized for heat conduction and static analysis in order to minimize the data transfer. For transient behaviour due to unsteady heat flow and/or inelastics material processes the two computational parts are interwoven in form of an integrated software package for finite element analysis of thermomechanical problems in space and time. (orig.) [de

  2. A simple 1D model with thermomechanical coupling for superelastic SMAs

    International Nuclear Information System (INIS)

    Zaki, W; Morin, C; Moumni, Z

    2010-01-01

    This paper presents an outline for a new uniaxial model for shape memory alloys that accounts for thermomechanical coupling. The coupling provides an explanation of the dependence of SMA behavior on the loading rate. 1D simulations are carried in Matlab using simple finite-difference discretization of the mechanical and thermal equations.

  3. Thermomechanical fatigue of Sn-37 wt.% Pb model solder joints

    International Nuclear Information System (INIS)

    Liu, X.W.; Plumbridge, W.J.

    2003-01-01

    The fatigue of Sn-37 wt.% Pb model solder joints has been investigated under thermomechanical and thermal cycling. Based upon an analysis of displacements during thermomechancial cycling, a model solder joint has been designed to simulate actual joints in electronic packages. The strain-stress relationship, characterised by hysteresis loops, was determined during cycling from 30 to 125 deg. C, and the stress-range monitored throughout. The number of cycles to failure, as defined by the fall in stress range, was correlated to strain range and strain energy. The strain hardening exponent, k, varied with the definition of failure and, when a stress-range drop of 50% was used, it was 0.46. Cracks were produced during pure thermal cycling without external strains applied. These arose due to the local strains caused by thermal expansion mismatches between the solder and Cu 6 Sn 5 intermetallic layer, between the phases of solder, and due to the anisotropy of the materials. The fatigue life under thermomechanical cycling was significantly inferior to that obtained in isothermal mechanical cycling. A factor contributing to this inferiority is the internal damage produced during temperature cycling

  4. Effect of thermomechanical treatment of the stress corrosion cracking of metastable beta III titanium

    International Nuclear Information System (INIS)

    Seats, J.H.; Condit, D.O.

    1974-01-01

    Results of studies on the relations of microstructural changes with stress corrosion of Ti--11.5 Mo--6 Zr--4.5 Sn (Beta III) alloys are presented. It was found that this alloy is virtually immune to stress corrosion cracking if no imperfections in the surface are present. Specimens that had not been cold worked showed surface deterioration, but it was not serious enough to cause any marked reduction in yield strengths. The alloy is, however, susceptible to SCC if the surface contains an imperfection such as a fatigue crack where high stresses can concentrate during testing. These high stress levels at the crack tip may cause mechanical destruction of the passivating oxide and allow a higher concentration of chloride ions near the fresh metal surfaces. However, even with precracked specimens, crack propagation is slow as evidenced by no failures within the 720 hour test period. The extreme notch sensitivity of Beta III prevented initiation of fatigue cracks in the sections of the alloy with 20 and 50 percent cold work. More research must be done to test Beta III in this condition. However, on the basis of the research conducted thus far, SCC susceptibility of Beta III titanium alloy appears to be independent of thermomechanical pretreatment. (U.S.)

  5. Development and Characterization of Improved NiTiPd High-Temperature Shape-Memory Alloys by Solid-Solution Strengthening and Thermomechanical Processing

    Science.gov (United States)

    Bigelow, Glen; Noebe, Ronald; Padula, Santo, II; Garg, Anita; Olson, David

    2006-01-01

    The need for compact, solid-state actuation systems for use in the aerospace, automotive, and other transportation industries is currently motivating research in high-temperature shape-memory alloys (HTSMA) with transformation temperatures greater than 100 C. One of the basic high-temperature alloys investigated to fill this need is Ni(19.5)Ti(50.5)Pd30. Initial testing has indicated that this alloy, while having acceptable work characteristics, suffers from significant permanent deformation (or ratcheting) during thermal cycling under load. In an effort to overcome this deficiency, various solid-solution alloying and thermomechanical processing schemes were investigated. Solid-solution strengthening was achieved by substituting 5at% gold or platinum for palladium in Ni(19.5)Ti(50.5)Pd30, the so-called baseline alloy, to strengthen the martensite and austenite phases against slip processes and improve thermomechanical behavior. Tensile properties, work behavior, and dimensional stability during repeated thermal cycling under load for the ternary and quaternary alloys were compared. The relative difference in yield strength between the martensite and austenite phases and the dimensional stability of the alloy were improved by the quaternary additions, while work output was only minimally impacted. The three alloys were also thermomechanically processed by cycling repeatedly through the transformation range under a constant stress. This so-called training process dramatically improved the dimensional stability in these samples and also recovered the slight decrease in work output caused by quaternary alloying. An added benefit of the solid-solution strengthening was maintenance of enhanced dimensional stability of the trained material to higher temperatures compared to the baseline alloy, providing a greater measure of over-temperature capability.

  6. Solvability of an unsaturated porous media flow problem with thermomechanical interaction

    Czech Academy of Sciences Publication Activity Database

    Detmann, B.; Krejčí, Pavel; Rocca, E.

    2016-01-01

    Roč. 48, č. 6 (2016), s. 4175-4201 ISSN 0036-1410 R&D Projects: GA ČR(CZ) GA15-12227S Institutional support: RVO:67985840 Keywords : porous media * hysteresis * thermomechanical interactions Subject RIV: BA - General Mathematics Impact factor: 1.648, year: 2016 http://epubs.siam.org/doi/abs/10.1137/16M1056365

  7. On behaviour of fuel elements subject to combined cyclic thermomechanical loads

    International Nuclear Information System (INIS)

    Hsu, T.R.

    1980-01-01

    This paper presents detailed finite element formulations on the kinematic hardening rule of plasticity included in an existing thermoelastoplastic stress analysis code primarily designed to predict the thermomechanical behaviour of nuclear reactor fuel elements. The kinematic hardening rule is considered to be important for structures subject to repeated (or cyclic) loads. The start-up/operation/shut-down and various power excursions in a reactor all can be classified as cyclic loadings. In addition to the shifting of material yield surfaces as usually handled by the kinematic hardening rule, the thermal effect and temperature-dependent material properties have also been included in the present work for the first time. A case study related to an in-reactor experiment on a single fuel element indicated that significantly higher cumulative sheath residual strains after two load cycles was obtained by the present scheme than those calculated by the usual isotropic hardening rule. This observation may alert fuel modellers to select proper hardening rules in their analyses. (orig.)

  8. Thermo-mechanical design of the SINGAP accelerator grids for ITER NB injectors

    Energy Technology Data Exchange (ETDEWEB)

    Agostinetti, P. [Consorzio RFX, Euratom-ENEA Association, Corso Stati Uniti 4, I35127 Padova (Italy)], E-mail: piero.agostinetti@igi.cnr.it; Dal Bello, S.; Dalla Palma, M.; Zaccaria, P. [Consorzio RFX, Euratom-ENEA Association, Corso Stati Uniti 4, I35127 Padova (Italy)

    2007-10-15

    The SINGle Aperture-SINgle GAP (SINGAP) accelerator for ITER neutral beam injector foresees four grids for the extraction and acceleration of negative ions, instead of the seven grids of the Multi-Aperture Multi-Grid (MAMuG) reference configuration. The grids have to fulfil specific requirements coming from ion extraction, beam optics and thermo-mechanical issues. This paper focuses on the thermo-hydraulic and thermo-mechanical design of the grids carried out by Consorzio RFX for the design of the first ITER NB injector and the ITER NB Test Facility. The cooling circuit design (position and shape of the channels) and the cooling parameters (water coolant temperatures, pressure and velocity) were optimized with sensitivity analyses in order to satisfy the grid functional requirements (temperatures, stresses, in plane and out of plane deformations). The design required a complete modelling of the grids and their support frames by means of 3D FE and CAD models.

  9. Thermo-mechanical design aspects of mercury bombardment ion thrusters.

    Science.gov (United States)

    Schnelker, D. E.; Kami, S.

    1972-01-01

    The mechanical design criteria are presented as background considerations for solving problems associated with the thermomechanical design of mercury ion bombardment thrusters. Various analytical procedures are used to aid in the development of thruster subassemblies and components in the fields of heat transfer, vibration, and stress analysis. Examples of these techniques which provide computer solutions to predict and control stress levels encountered during launch and operation of thruster systems are discussed. Computer models of specific examples are presented.

  10. Multiscale Modeling at Nanointerfaces: Polymer Thin Film Materials Discovery via Thermomechanically Consistent Coarse Graining

    Science.gov (United States)

    Hsu, David D.

    Due to high nanointerfacial area to volume ratio, the properties of "nanoconfined" polymer thin films, blends, and composites become highly altered compared to their bulk homopolymer analogues. Understanding the structure-property mechanisms underlying this effect is an active area of research. However, despite extensive work, a fundamental framework for predicting the local and system-averaged thermomechanical properties as a function of configuration and polymer species has yet to be established. Towards bridging this gap, here, we present a novel, systematic coarse-graining (CG) method which is able to capture quantitatively, the thermomechanical properties of real polymer systems in bulk and in nanoconfined geometries. This method, which we call thermomechanically consistent coarse-graining (TCCG), is a two-bead-per-monomer CG hybrid approach through which bonded interactions are optimized to match the atomistic structure via the Iterative Boltzmann Inversion method (IBI), and nonbonded interactions are tuned to macroscopic targets through parametric studies. We validate the TCCG method by systematically developing coarse-grain models for a group of five specialized methacrylate-based polymers including poly(methyl methacrylate) (PMMA). Good correlation with bulk all-atom (AA) simulations and experiments is found for the temperature-dependent glass transition temperature (Tg) Flory-Fox scaling relationships, self-diffusion coefficients of liquid monomers, and modulus of elasticity. We apply this TCCG method also to bulk polystyrene (PS) using a comparable coarse-grain CG bead mapping strategy. The model demonstrates chain stiffness commensurate with experiments, and we utilize a density-correction term to improve the transferability of the elastic modulus over a 500 K range. Additionally, PS and PMMA models capture the unexplained, characteristically dissimilar scaling of Tg with the thickness of free-standing films as seen in experiments. Using vibrational

  11. Self-positioning of polymer membranes driven by thermomechanically induced plastic deformation

    DEFF Research Database (Denmark)

    Häfliger, Daniel; Hansen, Ole; Boisen, Anja

    2006-01-01

    Stress in polymeric resins is tailored by a thermomechanical process. It allows for controlled self-positioning of membranes in microdevices (see Figure). The process makes specific use of plastic deformation that results from the low viscosity of the polymer. This demonstrates that polymers offer...... new approaches to microfabrication that cannot be realized for common semiconductor materials without severe difficulties....

  12. Thermo-mechanical treatment of low-cost alloy Ti-4.5Al-6.9Cr-2.3Mn and microstructure and mechanical characteristics

    Science.gov (United States)

    Chen, Guangyao; Kang, Juyun; Wang, Shusen; Wang, Shihua; Lu, Xionggang; Li, Chonghe

    2018-04-01

    In this study, the thermo-mechanical treatment process for low-cost Ti-4.5Al-6.9Cr-2.3Mn alloy were designed on the basis of assessment of Ti-Al-Cr-Mn thermodynamic system. The microstructure and mechanical properties of Ti-4.5Al-6.9Cr-2.3Mn forging and sheet were investigated by using the OM, SEM and universal tensile testing machine. The results show that both the forging and sheet were consisted of α + β phase, which is consistent with the expectation, and no element Cr and Mn existed in the grain boundaries of the sheet after quenching, and the C14 laves phase was not detected. The average ultimate tensile strength (σ b), 0.2% proof strength (σ 0.2) and elongation (EI) of alloy sheet after quenching can reach 1059 MPa, 1051 MPa and 24.6 Pct., respectively. Moreover, the average ultimate tensile strength of Ti-4.5Al-6.9Cr-2.3Mn forgings can reach 1599 MPa and the average elongation can reach 11.2 Pct., and a more excellent property of Ti-4.5Al-6.9Cr-2.3Mn forging is achieved than that of TC4 forging. It provides a theoretical support for further developing this low-cost alloy.

  13. Thermo-mechanical design of the SINGAP accelerator grids for ITER NB Injectors

    International Nuclear Information System (INIS)

    Agostinetti, P.; Dal Bello, S.; Palma, M.D.; Zaccaria, P.

    2006-01-01

    The SINGle Aperture - SINgle GAP (SINGAP) accelerator for ITER neutral beam injector foresees four grids for the extraction and acceleration of negative ions, instead of the seven grids of the Multi Aperture Multi Grid (MAMuG) reference configuration. Optimized geometry of the SINGAP grids (plasma, extraction, pre-acceleration, and grounded grid) was identified by CEA Association considering specific requirements for ions extraction and beam generation referring to experimental data and code simulations. This paper focuses on the thermo-hydraulic and thermo-mechanical design of the grids carried out by Consorzio RFX for the design of the first ITER NB Injector and the ITER NB Test Facility. The cooling circuit design (position and shape of the channels) and the cooling parameters (water coolant temperatures, pressure and velocity) were optimized with thermo-hydraulic and thermo-mechanical sensitivity analyses in order to satisfy the grid functional requirements (temperatures, in plane and out of plane deformations). A complete and detailed thermo-structural design assessment of the SINGAP grids was accomplished applying the structural design rules for ITER in-vessel components and considering both the reference load conditions and the maximum load provided by the power supplies. The design required a complete modelling of the grids and their support frames by means of 3D FE and CAD models. The grids were finally integrated with the support and cooling systems inside the beam source vessel. The main results of the thermo-hydraulic and thermo-mechanical analyses are presented. The open issues are then reported, mainly regarding the material properties characterization (static and fatigue tests) and the qualification of technologies for OFHC copper electro-deposition, brazing, and welding of heterogeneous materials. (author)

  14. Effect of ultrasonic pre-treatment of thermomechanical pulp on hydrogen peroxide bleaching

    Science.gov (United States)

    Loranger, E.; Charles, A.; Daneault, C.

    2012-12-01

    Ultrasound pre-treatments of softwood TMP had been carried to evaluate its impact on the efficiency of hydrogen peroxide bleaching. The trials were performed after a factorial design of experiment using frequency, power and time as variables. The experiments were conducted in an ultrasonic bath and then bleached with hydrogen peroxide. Measurements such as brightness, L*A*B* color system coordinate, residual hydrogen peroxide and metal content were evaluated on bleached pulp. The results indicate that the effect of ultrasonic treatment on brightness was dependent on the ultrasound frequency used; the brightness increased slightly at 68 kHz and decreased at 40 and 170 kHz. These results were correlated to the ultrasound effect on the generation of transition metals (copper, iron and manganese) which are responsible for catalytic decomposition of hydrogen peroxide. The influence of metal interference was minimized by using a chelating agent such as diethylene triamine pentaacetic acid (DTPA). With the results obtained in this study we have identified a set of option conditions, e.g. 1000 W, 40 kHz, 1.5 % consistency and 0.2% addition of DTPA prior to the bleaching stage (after ultrasonic pre-treatment) who improve brightness by 2.5 %ISO.

  15. Textile wastewater reuse after additional treatment by Fenton's reagent.

    Science.gov (United States)

    Ribeiro, Marília Cleto Meirelles; Starling, Maria Clara V M; Leão, Mônica Maria Diniz; de Amorim, Camila Costa

    2017-03-01

    This study verifies textile wastewater reuse treated by the conventional activated sludge process and subjected to further treatment by advanced oxidation processes. Three alternative processes are discussed: Fenton, photo-Fenton, and UV/H 2 O 2 . Evaluation of treatments effects was based on factorial experiment design in which the response variables were the maximum removal of COD and the minimum concentration of residual H 2 O 2 in treated wastewater. Results indicated Fenton's reagent, COD/[H 2 O 2 ]/[Fe 2+ ] mass ratio of 1:2:2, as the best alternative. The selected technique was applied to real wastewater collected from a conventional treatment plant of a textile mill. The quality of the wastewater before and after the additional treatment was monitored in terms of 16 physicochemical parameters defined as suitable for the characterization of waters subjected to industrial textile use. The degradation of the wastewater was also evaluated by determining the distribution of its molecular weight along with the organic matter fractionation by ultrafiltration, measured in terms of COD. Finally, a sample of the wastewater after additional treatment was tested for reuse at pilot scale in order to evaluate the impact on the quality of dyed fabrics. Results show partial compliance of treated wastewater with the physicochemical quality guidelines for reuse. Removal and conversion of high and medium molecular weight substances into low molecular weight substances was observed, as well as the degradation of most of the organic matter originally present in the wastewater. Reuse tests indicated positive results, confirming the applicability of wastewater reuse after the suggested additional treatment. Graphical abstract Textile wastewater samples after additional treatment by Fenton's reagent, photo-Fenton and H 2 O 2 /UV tested in different conditions.

  16. Nuclear, thermo-mechanical and tritium release analysis of ITER breeding blanket

    International Nuclear Information System (INIS)

    Kosaku, Yasuo; Kuroda, Toshimasa; Enoeda, Mikio; Hatano, Toshihisa; Sato, Satoshi; Miki, Nobuharu; Akiba, Masato

    2003-06-01

    The design of the breeding blanket in ITER applies pebble bed breeder in tube (BIT) surrounded by multiplier pebble bed. It is assumed to use the same module support mechanism and coolant manifolds and coolant system as the shielding blankets. This work focuses on the verification of the design of the breeding blanket, from the viewpoints which is especially unique to the pebble bed type breeding blanket, such as, tritium breeding performance, tritium inventory and release behavior and thermo-mechanical performance of the ITER breeding blanket. With respect to the neutronics analysis, the detailed analyses of the distribution of the nuclear heating rate and TBR have been performed in 2D model using MCNP to clarify the input data for the tritium inventory and release rate analyses and thermo-mechanical analyses. With respect to the tritium inventory and release behavior analysis, the parametric analyses for selection of purge gas flow rate were carried out from the view point of pressure drop and the tritium inventory/release performance for Li 2 TiO 3 breeder. The analysis result concluded that purge gas flow rate can be set to conventional flow rate setting (88 l/min per module) to 1/10 of that to save the purge gas flow and minimize the size of purge gas pipe. However, it is necessary to note that more tritium is transformed to HTO (chemical form of water) in case of Li 2 TiO 3 compared to other breeder materials. With respect to the thermo-mechanical analyses of the pebble bed blanket structure, the analyses have been performed by ABAQUS with 2D model derived from one of eight facets of a blanket module, based on the reference design. Analyses were performed to identify the temperature distribution incorporating the pebble bed mechanical simulation and influence of mechanical behavior to the thermal behavior. The result showed that the maximum temperature in the breeding material was 617degC in the first row of breeding rods and the minimum temperature was 328

  17. Thermo-mechanical Modelling of Pebble Beds in Fusion Blankets and its Implementation by a Return-Mapping Algorithm

    International Nuclear Information System (INIS)

    Gan, Yixiang; Kamlah, Marc

    2008-01-01

    In this investigation, a thermo-mechanical model of pebble beds is adopted and developed based on experiments by Dr. Reimann at Forschungszentrum Karlsruhe (FZK). The framework of the present material model is composed of a non-linear elastic law, the Drucker-Prager-Cap theory, and a modified creep law. Furthermore, the volumetric inelastic strain dependent thermal conductivity of beryllium pebble beds is taken into account and full thermo-mechanical coupling is considered. Investigation showed that the Drucker-Prager-Cap model implemented in ABAQUS can not fulfill the requirements of both the prediction of large creep strains and the hardening behaviour caused by creep, which are of importance with respect to the application of pebble beds in fusion blankets. Therefore, UMAT (user defined material's mechanical behaviour) and UMATHT (user defined material's thermal behaviour) routines are used to re-implement the present thermo-mechanical model in ABAQUS. An elastic predictor radial return mapping algorithm is used to solve the non-associated plasticity iteratively, and a proper tangent stiffness matrix is obtained for cost-efficiency in the calculation. An explicit creep mechanism is adopted for the prediction of time-dependent behaviour in order to represent large creep strains in high temperature. Finally, the thermo-mechanical interactions are implemented in a UMATHT routine for the coupled analysis. The oedometric compression tests and creep tests of pebble beds at different temperatures are simulated with the help of the present UMAT and UMATHT routines, and the comparison between the simulation and the experiments is made. (authors)

  18. A Multi-objective Optimization Application in Friction Stir Welding: Considering Thermo-mechanical Aspects

    DEFF Research Database (Denmark)

    Tutum, Cem Celal; Hattel, Jesper Henri

    2010-01-01

    speed and traverse welding speed have been sought in order to achieve the goals mentioned above using an evolutionary multi-objective optimization (MOO) algorithm, i.e. non-dominated sorting genetic algorithm (NSGA-II), integrated with a transient, 2-dimensional sequentially coupled thermomechanical...

  19. A treatment of expansive soil using different additives

    Directory of Open Access Journals (Sweden)

    Bestun J. Nareeman

    2010-11-01

    Full Text Available There are many factors that govern the expansion behavior of soil. The primary factors are a change in water contentand the amount and type of clay size particles in the soil. Other important factors affecting the expansion behavior include the typeof soil (natural or fill, condition of the soil in terms of dry density and moisture content, magnitude of the surcharge pressure,and amount of no expansive material such as gravel or cobble size particles.In this paper, a swelling soil from the site Hamamuk earth dam, which is located in Koya town north of Iraq, is treated by fourtypes of additives; cement, steel fibers, gasoline fuel and injection by cement grout.The treatment of the expansive soil with 5 % of cement or steel fibers or the injection with cement grout revealed a betterimprovement while 4 % of gasoline oil is sufficient to reveal the optimum treatment by this material. The angle of internal friction is notaffected by the treatment while the cohesion between particles is slightly affected by these additives due to a change in the adhesionbetween the additive and soil particles.

  20. Modelling thermomechanical conditions at the tool/matrix interface in Friction Stir Welding

    DEFF Research Database (Denmark)

    Schmidt, Henrik Nikolaj Blich; Hattel, Jesper

    2004-01-01

    is obtained. A fully coupled thermo-mechanical 3D FE model has been developed in ABAQUS/Explicit using the ALE formulation and the Johnson-Cook material law. The contact forces are modelled by Coulomb’s law of friction making the contact condition highly solution dependent. The heat is generated by both...

  1. Effect of thermo-mechanical loading histories on fatigue crack growth behavior and the threshold in SUS 316 and SCM 440 steels. For prevention of high cycle thermal fatigue failures

    International Nuclear Information System (INIS)

    Okazaki, Masakazu; Muzvidziwa, Milton; Iwasaki, Akira; Kasahara, Naoto

    2014-01-01

    High cycle thermal fatigue failure of pipes induced by fluid temperature change is one of the interdisciplinary issues to be concerned for long term structural reliability of high temperature components in energy systems. In order to explore advanced life assessment methods to prevent the failure, fatigue crack propagation tests were carried out in a low alloy steel and an austenitic stainless steel under typical thermal and thermo-mechanical histories. Special attention was paid to both the effect of thermo-mechanical loading history on the fatigue crack threshold, as well as to the applicability of continuum fracture mechanics treatment to small or short cracks. It was shown experimentally that the crack-based remaining fatigue life evaluation provided more reasonable assessment than the traditional method based on the semi-empirical law in terms of 'usage factor' for high cycle thermal fatigue failure that is employed in JSME Standard, S017. The crack propagation analysis based on continuum fracture mechanics was almost successfully applied to the small fatigue cracks of which size was comparable to a few times of material grain size. It was also shown the thermo-mechanical histories introduced unique effects to the prior fatigue crack wake, resulting in occasional change in the fatigue crack threshold. (author)

  2. Thermomechanical effect of pulse-periodic laser radiation on cartilaginous and eye tissues

    Science.gov (United States)

    Baum, O. I.; Zheltov, G. I.; Omelchenko, A. I.; Romanov, G. S.; Romanov, O. G.; Sobol, E. N.

    2013-08-01

    This paper is devoted to theoretical and experimental studies into the thermomechanical action of laser radiation on biological tissues. The thermal stresses and strains developing in biological tissues under the effect of pulse-periodic laser radiation are theoretically modeled for a wide range of laser pulse durations. The models constructed allow one to calculate the magnitude of pressures developing in cartilaginous and eye tissues exposed to laser radiation and predict the evolution of cavitation phenomena occurring therein. The calculation results agree well with experimental data on the growth of pressure and deformations, as well as the dynamics of formation of gas bubbles, in the laser-affected tissues. Experiments on the effect of laser radiation on the trabecular region of the eye in minipigs demonstrated that there existed optimal laser irradiation regimens causing a substantial increase in the hydraulic permeability of the radiation-exposed tissue, which can be used to develop a novel glaucoma treatment method.

  3. Thermomechanical effect of pulse-periodic laser radiation on cartilaginous and eye tissues

    International Nuclear Information System (INIS)

    Baum, O I; Omelchenko, A I; Sobol, E N; Zheltov, G I; Romanov, G S; Romanov, O G

    2013-01-01

    This paper is devoted to theoretical and experimental studies into the thermomechanical action of laser radiation on biological tissues. The thermal stresses and strains developing in biological tissues under the effect of pulse-periodic laser radiation are theoretically modeled for a wide range of laser pulse durations. The models constructed allow one to calculate the magnitude of pressures developing in cartilaginous and eye tissues exposed to laser radiation and predict the evolution of cavitation phenomena occurring therein. The calculation results agree well with experimental data on the growth of pressure and deformations, as well as the dynamics of formation of gas bubbles, in the laser-affected tissues. Experiments on the effect of laser radiation on the trabecular region of the eye in minipigs demonstrated that there existed optimal laser irradiation regimens causing a substantial increase in the hydraulic permeability of the radiation-exposed tissue, which can be used to develop a novel glaucoma treatment method. (paper)

  4. Thermomechanical Behavior of Rotor with Rubbing

    Directory of Open Access Journals (Sweden)

    Jerzy T. Sawicki

    2003-01-01

    Full Text Available This article presents an analytical study of the dynamics and stability of rotors subjected to rubbing due to contact with seals, taking account of associated thermal effects. The seal interaction force acting on the shaft gives rise to a friction force, which is a source of heating and can induce so-called spiral vibrations. A mathematical model that has been developed couples the heat-conduction equation with the equations for motion of the rotor. Numerical simulations have been conducted that show the thermomechanical behavior of the rotor at various operating conditions. A procedure for analyzing the stability of multibearing rotors based on the system eigenvalue analysis and the state-space approach has been proposed. Finally, the experimental data related to full annular rub have been presented.

  5. 3-D electromagnetic and thermo-mechanical simulation of a RF cavity

    CERN Document Server

    Launay, F

    2003-01-01

    A 3-D thermo-mechanical study of the edge of entrance blade of IPHI's RFQ was conducted by means of I-DEAS code. The aim is to compare the temperatures reached, the constraints, and the deformations calculated on the basis of RF power density stored on the blade obtained by means of two different electromagnetic computational codes, SOPRANO and MAFIA.

  6. Application of a new thermo-mechanical model for the study of the nuclear waste disposal in clay rocks

    International Nuclear Information System (INIS)

    Dizier, A.; Li, X.L.; Francois, B.; Collin, F.; Charlier, R.

    2012-01-01

    Document available in extended abstract form only. One of the cornerstones of the nuclear waste disposal researches concerns the evolution of the damaged zone which can offer a preferential path for migration of radionuclide through modifications of its mechanical and hydraulic properties. Even if the thermo-mechanical behaviour of clays is well documented in the literature, the development of the damaged zone induced by an excavation with temperature is not well known. To investigate this problem, a new thermo-mechanical constitutive law has been implemented in the non-linear finite element code LAGAMINE developed at ULg (Universite de Liege) and has been used to model the PRACLAY experiment (Preliminary demonstration test for clay disposal of vitrified high level radioactive waste) at Mol URL (Underground Research Laboratory). Though several models are being to reproduce the different phenomena met when a thermal loading is applied to a clay specimen, the applications of such thermo-mechanical models to simulate large scale in-situ experiment are rare. Based on the work of Sultan a new thermo-mechanical constitutive law has been implemented in combination with a Cap model in the code LAGAMINE. The Cap model is a combination of a frictional criterion, a Cam-Clay model and a traction criterion. The influence of the temperature is considered through the thermo-mechanical law developed by Cui et al. (2000). This law permits to reproduce common features of the thermo-mechanical behaviour of clay, such as the decrease of the pre-consolidation pressure with temperature, the volume change, the thermal hardening, the transition between thermal dilation and thermal contraction for over-consolidated clays. These aspects are modelled with two curves in the (p',T) plane. The first one is related to the generation of the thermal volumetric plastic strains (TY curve (Thermal Yield)). The second one reproduces the decrease of the pre-consolidation pressure with the temperature

  7. Thermomechanical Behavior of High Performance Epoxy/Organoclay Nanocomposites

    Directory of Open Access Journals (Sweden)

    Artur Soares Cavalcanti Leal

    2014-01-01

    Full Text Available Nanocomposites of epoxy resin containing bentonite clay were fabricated to evaluate the thermomechanical behavior during heating. The epoxy resin system studied was prepared using bifunctional diglycidyl ether of bisphenol A (DGEBA, crosslinking agent diaminodiphenylsulfone (DDS, and diethylenetriamine (DETA. The purified bentonite organoclay (APOC was used in all experiments. The formation of nanocomposite was confirmed by X-ray diffraction analysis. Specimens of the fabricated nanocomposites were characterized by dynamic mechanical analysis (DMA. According to the DMA results a significant increase in glass transition temperature and storage modulus was evidenced when 1 phr of clay is added to epoxy resin.

  8. Microstructure history effect during sequential thermomechanical processing

    International Nuclear Information System (INIS)

    Yassar, Reza S.; Murphy, John; Burton, Christina; Horstemeyer, Mark F.; El kadiri, Haitham; Shokuhfar, Tolou

    2008-01-01

    The key to modeling the material processing behavior is the linking of the microstructure evolution to its processing history. This paper quantifies various microstructural features of an aluminum automotive alloy that undergoes sequential thermomechanical processing which is comprised hot rolling of a 150-mm billet to a 75-mm billet, rolling to 3 mm, annealing, and then cold rolling to a 0.8-mm thickness sheet. The microstructural content was characterized by means of electron backscatter diffraction, scanning electron microscopy, and transmission electron microscopy. The results clearly demonstrate the evolution of precipitate morphologies, dislocation structures, and grain orientation distributions. These data can be used to improve material models that claim to capture the history effects of the processing materials

  9. Thermo-mechanical design and testing of a microbalance for space applications

    Science.gov (United States)

    Scaccabarozzi, Diego; Saggin, Bortolino; Tarabini, Marco; Palomba, Ernesto; Longobardo, Andrea; Zampetti, Emiliano

    2014-12-01

    This work focuses on the thermo-mechanical design of the microbalance used for the VISTA (Volatile In Situ Thermogravimetry Analyzer) sensor. VISTA has been designed to operate in situ in different space environments (asteroids, Mars, icy satellites). In this paper we focus on its application on Mars, where the expected environmental conditions are the most challenging for the thermo-mechanical design. The microbalance holding system has been designed to ensure piezoelectric crystal integrity against the high vibration levels during launch and landing and to cope with the unavoidable thermo-elastic differential displacements due to CTE and temperature differences between the microbalance elements. The crystal holding system, based on three symmetrical titanium supports, provides also the electrical connections needed for crystal actuation, microbalance heating and temperature measurement on the electrode area. On the microbalance crystal surfaces the electrodes, a micro film heater (optimized to perform thermo-gravimetric analysis up to 400 °C) and a resistive thermometer are deposited through a vacuum sputtering process. A mockup of the system has been manufactured and tested at the expected vibration levels and the thermal control effectiveness has been verified in thermo-vacuum environment.

  10. Modelling the Thermo-Mechanical Behavior of Magnesium Alloys during Indirect Extrusion

    International Nuclear Information System (INIS)

    Steglich, D.; Ertuerk, S.; Bohlen, J.; Letzig, D.; Brocks, W.

    2010-01-01

    One of the basic metal forming process for semi-finished products is extrusion. Since extrusion involves complex thermo-mechanical and multiaxial loading conditions resulting in large strains, high strain rates and an increase in temperature due to deformation, a proper yield criterion and hardening law should be used in the numerical modelling of the process. A phenomenological model based on a plastic potential has been proposed that takes strain, strain rate and temperature dependency on flow behaviour into consideration. A hybrid methodology of experiment and finite element simulation has been adopted in order to obtain necessary model parameters. The anisotropy/asymmetry in yielding was quantified by tensile and compression tests of specimens prepared from different directions. The identification of the corresponding model parameters was performed by a genetic algorithm. A fully coupled thermo-mechanical analysis has been used in extrusion simulations for calculation of the temperature field by considering heat fluxes and heat generated due to plastic deformation. The results of the approach adopted in this study appeared to be successful showing promising predictions of the experiments and thus may be extended to be applicable to other magnesium alloys or even other hcp metals.

  11. Equipment for the investigation of the thermomechanical fatigue of metallic materials

    International Nuclear Information System (INIS)

    Wolter, F.; Petersen, C.

    1992-01-01

    Within the framework of the European research program on nuclear fusion, a question is to be answered which is of great importance for the design of a fusion reactor, namely: To what extent is the 'First Wall structure' damaged by the pulsating mode of operation in this reactor type. This pulsating mode of operation leads to a thermal and mechanical cyclic stress in the metal support structure of the reactor. Thermomechanical cyclic stresses of a similar kind also occur in aircraft turbines, rocket drive units, and heat generating systems. For simulation of such stresses, a facility was developed in the Karlsruhe Nuclear Research Center which permits to produce thermomechanical cyclic stresses in uniaxial metallic materials specimens. The results of investigations with a martensitic 12%-Cr steel are explained. The stress range variations show a degressive behavior at the onset of fatigue and develop into a linear decline. The plastic strain reached a plateau after a number of cycles which was dependent on the mechanical strain (linear behavior). Relationships can be described by a simple transformation of number of cycles to failure between mechanical strain and number of stress cycles to failure. (orig./MM) [de

  12. Thermomechanics of solid materials with application to the Gurson-Tvergaard material model

    Energy Technology Data Exchange (ETDEWEB)

    Santaoja, K. [VTT Manufacturing Technology, Espoo (Finland). Materials and Structural Integrity

    1997-12-31

    The elastic-plastic material model for porous material proposed by Gurson and Tvergaard is evaluated. First a general description is given of constitutive equations for solid materials by thermomechanics with internal variables. The role and definition of internal variables are briefly discussed and the following definition is given: The independent variables present (possibly hidden) in the basic laws for thermomechanics are called controllable variables. The other independent variables are called internal variables. An internal variable is shown always to be a state variable. This work shows that if the specific dissipation function is a homogeneous function of degree one in the fluxes, a description for a time-independent process is obtained. When damage to materials is evaluated, usually a scalar-valued or tensorial variable called damage is introduced in the set of internal variables. A problem arises when determining the relationship between physically observable weakening of the material and the value for damage. Here a more feasible approach is used. Instead of damage, the void volume fraction is inserted into the set of internal variables. This allows use of an analytical equation for description of the mechanical weakening of the material. An extension to the material model proposed by Gurson and modified by Tvergaard is derived. The derivation is based on results obtained by thermomechanics and damage mechanics. The main difference between the original Gurson-Tvergaard material model and the extended one lies in the definition of the internal variable `equivalent tensile flow stress in the matrix material` denoted by {sigma}{sup M}. Using classical plasticity theory, Tvergaard elegantly derived an evolution equation for {sigma}{sup M}. This is not necessary in the present model, since damage mechanics gives an analytical equation between the stress tensor {sigma} and {sigma}M. Investigation of the Clausius-Duhem inequality shows that in compression

  13. Thermomechanics of solid materials with application to the Gurson-Tvergaard material model

    International Nuclear Information System (INIS)

    Santaoja, K.

    1997-01-01

    The elastic-plastic material model for porous material proposed by Gurson and Tvergaard is evaluated. First a general description is given of constitutive equations for solid materials by thermomechanics with internal variables. The role and definition of internal variables are briefly discussed and the following definition is given: The independent variables present (possibly hidden) in the basic laws for thermomechanics are called controllable variables. The other independent variables are called internal variables. An internal variable is shown always to be a state variable. This work shows that if the specific dissipation function is a homogeneous function of degree one in the fluxes, a description for a time-independent process is obtained. When damage to materials is evaluated, usually a scalar-valued or tensorial variable called damage is introduced in the set of internal variables. A problem arises when determining the relationship between physically observable weakening of the material and the value for damage. Here a more feasible approach is used. Instead of damage, the void volume fraction is inserted into the set of internal variables. This allows use of an analytical equation for description of the mechanical weakening of the material. An extension to the material model proposed by Gurson and modified by Tvergaard is derived. The derivation is based on results obtained by thermomechanics and damage mechanics. The main difference between the original Gurson-Tvergaard material model and the extended one lies in the definition of the internal variable 'equivalent tensile flow stress in the matrix material' denoted by σ M . Using classical plasticity theory, Tvergaard elegantly derived an evolution equation for σ M . This is not necessary in the present model, since damage mechanics gives an analytical equation between the stress tensor σ and σM. Investigation of the Clausius-Duhem inequality shows that in compression, states occur which are not

  14. Multiscale Thermo-Mechanical Design and Analysis of High Frequency and High Power Vacuum Electron Devices

    Science.gov (United States)

    Gamzina, Diana

    Diana Gamzina March 2016 Mechanical and Aerospace Engineering Multiscale Thermo-Mechanical Design and Analysis of High Frequency and High Power Vacuum Electron Devices Abstract A methodology for performing thermo-mechanical design and analysis of high frequency and high average power vacuum electron devices is presented. This methodology results in a "first-pass" engineering design directly ready for manufacturing. The methodology includes establishment of thermal and mechanical boundary conditions, evaluation of convective film heat transfer coefficients, identification of material options, evaluation of temperature and stress field distributions, assessment of microscale effects on the stress state of the material, and fatigue analysis. The feature size of vacuum electron devices operating in the high frequency regime of 100 GHz to 1 THz is comparable to the microstructure of the materials employed for their fabrication. As a result, the thermo-mechanical performance of a device is affected by the local material microstructure. Such multiscale effects on the stress state are considered in the range of scales from about 10 microns up to a few millimeters. The design and analysis methodology is demonstrated on three separate microwave devices: a 95 GHz 10 kW cw sheet beam klystron, a 263 GHz 50 W long pulse wide-bandwidth sheet beam travelling wave tube, and a 346 GHz 1 W cw backward wave oscillator.

  15. Thermal and thermomechanical effects on the Al-Ca-Zn superplastic alloy studied on the positrons annihilation

    International Nuclear Information System (INIS)

    Romero, R.; Somoza, A.; Silvetti, S.P.

    1990-01-01

    Superplastic metallic materials are characterized by the presence of an unusual plastic behaviour, within a certain temperature range, with high ductility and low flow stress. This makes them suitable for their shaping with compressed air, for instance. On the other hand they behave similarly to any other metallic alloy at room temperature. One of the main problems found in superplastic alloys during deformation is the formation of cavities that may deteriorate the properties of a piece which was manufactured with this method. As an attempt to understand the origin of the cavitation, the effect of thermal and thermo-mechanical treatments was studied on superplastic alloy Al-5%wtCa-5%wtZn using a measurement technique based on positron annihilation. (Author). 3 refs., 5 figs

  16. Influence of thermo-mechanical processing on the microstructure of Cu-based shape memory alloys produced by powder metallurgy

    International Nuclear Information System (INIS)

    Rodriguez, P.P.; Ibarra, A.; Iza-Mendia, A.; Recarte, V.; Perez-Landazabal, J.I.; San Juan, J.; No, M.L.

    2003-01-01

    Cu-Al-Ni shape memory alloys processed by powder metallurgy show very good thermo-mechanical properties, much better than those found in alloys produced by conventional casting. In this paper, we present the microstructural characterisation of these powder metallurgy alloys in order to find the microscopic mechanisms, linked to the powder metallurgy processing method, which are indeed responsible of such good thermo-mechanical behaviour. Electron microscopy studies [scanning electron microscopy (SEM), electron backscatter diffraction (EBSD) and transmission electron microscopy (TEM)] show that powder metallurgy processing creates a sub-grain structure characterised by the presence of low angle sub-boundaries. These sub-boundaries are found to be lying on {1 1 0} and {1 1 2} lattice planes and are composed by an arrangement of superdislocations. These sub-boundaries may improve ductility in two ways: acting as a sink of dislocations which promotes plastic deformation and decreasing stress concentration at grain boundaries. Moreover, since sub-boundaries act as weak obstacles for the movement of martensite plates, the improvement on ductility is accomplished by an adequate thermo-mechanical behaviour

  17. Triiodothyronine addition to paroxetine in the treatment of major depressive disorder

    NARCIS (Netherlands)

    Appelhof, Bente C.; Brouwer, Jantien P.; van Dyck, Richard; Fliers, Eric; Hoogendijk, Witte J. G.; Huyser, Jochanan; Schene, Aart H.; Tijssen, Jan G. P.; Wiersinga, Wilmar M.

    2004-01-01

    There is evidence that thyroid hormone T-3 increases serotonergic neurotransmission. Therefore, T-3 addition to antidepressants may improve treatment response in major depression. In nonrefractory depression, T-3 addition to tricyclic antidepressants indeed accelerates treatment response. Current

  18. FE-simulation of hot forging with an integrated heat treatment with the objective of residual stress prediction

    Science.gov (United States)

    Behrens, Bernd-Arno; Chugreeva, Anna; Chugreev, Alexander

    2018-05-01

    Hot forming as a coupled thermo-mechanical process comprises numerous material phenomena with a corresponding impact on the material behavior during and after the forming process as well as on the final component performance. In this context, a realistic FE-simulation requires reliable mathematical models as well as detailed thermo-mechanical material data. This paper presents experimental and numerical results focused on the FE-based simulation of a hot forging process with a subsequent heat treatment step aiming at the prediction of the final mechanical properties and residual stress state in the forged component made of low alloy CrMo-steel DIN 42CrMo4. For this purpose, hot forging experiments of connecting rod geometry with a corresponding metallographic analysis and x-ray residual stress measurements have been carried out. For the coupled thermo-mechanical-metallurgical FE-simulations, a special user-defined material model based on the additive strain decomposition method and implemented in Simufact Forming via MSC.Marc solver features has been used.

  19. Thermomechanical Analysis (TMA) and its application to polymer systems

    Energy Technology Data Exchange (ETDEWEB)

    Adams, Jillian Cathleen [Los Alamos National Lab. (LANL), Los Alamos, NM (United States)

    2016-05-25

    Thermomechanical analysis (TMA) instruments are used to measure dimensional changes as a sample is heated or cooled. Data obtained from these instruments can be used to calculate the glass transition (Tg) and the coefficient of thermal expansion (CTE). Commonly, materials expand when heated and contract when cooled; however, the rate of such changes depends largely on the type of material. In manufacturing, it is important to use components with similar CTE values to avoid product failure, leaks, or a build-up of thermal stress. Therefore, TMA is a straightforward, useful tool in research and industry.

  20. Thermo-mechanical behavior of power electronic packaging assemblies: From characterization to predictive simulation of lifetimes

    Science.gov (United States)

    Dalverny, O.; Alexis, J.

    2018-02-01

    This article deals with thermo-mechanical behavior of power electronic modules used in several transportation applications as railway, aeronautic or automotive systems. Due to a multi-layered structures, involving different materials with a large variation of coefficient of thermal expansion, temperature variations originated from active or passive cycling (respectively from die dissipation or environmental constraint) induces strain and stresses field variations, giving fatigue phenomenon of the system. The analysis of the behavior of these systems and their dimensioning require the implementation of complex modeling strategies by both the multi-physical and the multi-scale character of the power modules. In this paper we present some solutions for studying the thermomechanical behavior of brazed assemblies as well as taking into account the interfaces represented by the numerous metallizations involved in the process assembly.

  1. Preliminary thermal/thermomechanical analyses of the Site Characterization Plan's Conceptual Design for a repository containing horizontally emplaced waste packages at the Deaf Smith County site

    International Nuclear Information System (INIS)

    Ghantous, N.Y.; Raines, G.E.

    1987-10-01

    This report presents thermal/thermomechanical analyses of the Site Characterization Plan Conceptual Design for horizontal package emplacement at the Deaf Smith County site, Texas. The repository was divided into three geometric regions. Then two-dimensional finite-element models were set up to approximate the three-dimensional nature of each region. Thermal and quasistatic thermomechanical finite-element analyses were performed to evaluate the thermal/thermomechanical responses of the three regions. The exponential-time creep law was used to represent the creep behavior of salt rock. The repository design was evaluated by comparing the thermal/thermomechanical responses obtained for the three regions with interim performance constraints. The preliminary results show that all the performance constraints are met except for those of the waste package. The following factors were considered in interpreting these results: (1) the qualitative description of the analytical responses; (2) the limitations of the analyses; and (3) either the conclusions based on overall evaluation of limitations and analytical results or the conclusions based on the fact that the repository design may be evaluated only after further analyses. Furthermore, a parametric analysis was performed to estimate the effect of material parameters on the predicted thermal/thermomechanical response. 23 refs., 34 figs., 9 tabs

  2. Multiphysics model of thermomechanical and helium-induced damage of tungsten during plasma heat transients

    Energy Technology Data Exchange (ETDEWEB)

    Crosby, Tamer, E-mail: tcrosby@ucla.edu; Ghoniem, Nasr M., E-mail: ghoniem@ucla.edu

    2013-11-15

    A combination of transient heating and bombardment by helium and hydrogen atoms has been experimentally proven to lead to severe surface and sub-surface damage. We developed a computational model to determine the relationship between the thermomechanical loading conditions and the onset of damage and failure of tungsten surfaces. The model is based on a thermoelasticity fracture damage approach that was developed using the phase field method. The model simulates the distribution of helium bubbles inside the grains and on grain boundaries using space-dependent rate theory. In addition, the model is coupled with a transient heat conduction analysis for temperature distributions inside the material. The results show the effects of helium bubbles on reducing tungsten surface energy. Further, a temperature gradient in the material equals to 10 K/μm, resulted in deep cracks propagating from the tungsten surface.

  3. Rheological properties of the wheat flour supplemented with different additives

    Directory of Open Access Journals (Sweden)

    GEORGETA STOENESCU

    2011-07-01

    Full Text Available One characteristic of the Romanian wheat flour in the recent years consists of high values of the falling number. The aim of the present study was to explore the Mixolab device to characterize the thermo-mechanical behaviour of flour supplemented with different additives that contain α-amylase. Mixolab parameters C4 and C5 were found to be lower in samples with high doses of additives containing α-amylases. The increase of the α-amylase dose reduces the dough stability. The samples that contain higher doses of additives presented low values of the β slope, which gives indications about starch gelatinization. The samples with reduced α-amylases activity showed high values of the γ slope.

  4. Grain size refinement of inconel 718 thermomechanical processing

    International Nuclear Information System (INIS)

    Okimoto, P.C.

    1988-01-01

    Inconel 718 is a Ni-Fe precipitation treated superalloy. It presents good thermal fatigue properties when the material has small grain size. The aim of this work is to study the grain size refinement by thermomechanical processing, through observations of the microstructural evolution and the influence of some of the process variables in the final grain size. The results have shown that this refinement occured by static recrystallization. The presence of precipitates have influenced the final grain size if the deformations are below 60%. For greater deformations the grain size is independent of the precipitate distribution in the matrix and tends to a limit size of 5 μm. (author)

  5. Effect of partially hydrolyzed guar gum on pasting, thermo-mechanical and rheological properties of wheat dough.

    Science.gov (United States)

    Mudgil, Deepak; Barak, Sheweta; Khatkar, B S

    2016-12-01

    Partially hydrolyzed guar gum was prepared using enzymatic hydrolysis of native guar gum that can be utilized as soluble fiber source. The effect of partially hydrolyzed guar gum (PHGG) on pasting, thermo-mechanical and rheological properties of wheat flour was investigated using rapid visco-analyzer, Mixolab and Microdoughlab. Wheat flour was replaced with 1-5g PHGG per 100g of wheat flour on weight basis. PHGG addition decreased the peak, trough, breakdown, setback and final viscosity of wheat flour. Water absorption and amylase activity of wheat dough were increased whereas starch gelatinization and protein weakening of wheat dough were reduced as a result of PHGG addition to wheat flour. PHGG addition also increased the peak dough height, arrival time, dough development time, dough stability and peak energy of wheat dough system. However, dough softening was decreased after PHGG addition to wheat flour dough. Overall, it can be assumed that PHGG has influenced the properties of wheat flour dough system by decreasing the RVA viscosities and increasing the water absorption and starch gelatinization of wheat dough system. Copyright © 2016 Elsevier B.V. All rights reserved.

  6. Effect of Thermomechanical Processing on Microstructure, Texture Evolution, and Mechanical Properties of Al-Mg-Si-Cu Alloys with Different Zn Contents

    Science.gov (United States)

    Wang, X. F.; Guo, M. X.; Chen, Y.; Zhu, J.; Zhang, J. S.; Zhuang, L. Z.

    2017-07-01

    The effect of thermomechanical processing on microstructure, texture evolution, and mechanical properties of Al-Mg-Si-Cu alloys with different Zn contents was studied by mechanical properties, microstructure, and texture characterization in the present study. The results show that thermomechanical processing has a significant influence on the evolution of microstructure and texture and on the final mechanical properties, independently of Zn contents. Compared with the T4P-treated (first preaged at 353 K (80 °C) for 12 hours and then naturally aged for 14 days) sheets with high final cold rolling reduction, the T4P-treated sheets with low final cold rolling reduction possess almost identical strength and elongation and higher average r values. Compared with the intermediate annealed sheets with high final cold rolling reduction, the intermediate annealed sheets with low final cold rolling reduction contain a higher number of particles with a smaller size. After solution treatment, in contrast to the sheets with high final cold rolling reduction, the sheets with low final cold rolling reduction possess finer grain structure and tend to form a weaker recrystallization texture. The recrystallization texture may be affected by particle distribution, grain size, and final cold rolling texture. Finally, the visco-plastic self-consistent (VPSC) model was used to predict r values.

  7. Study of the thermo-mechanical performances of the IFMIF-EVEDA Lithium Test Loop target assembly

    Energy Technology Data Exchange (ETDEWEB)

    Di Maio, P.A., E-mail: dimaio@din.unipa.it [Dipartimento dell' Energia, Universita di Palermo, Viale delle Scienze, 90128 Palermo (Italy); Arena, P.; Bongiovi, G. [Dipartimento dell' Energia, Universita di Palermo, Viale delle Scienze, 90128 Palermo (Italy); Giammusso, R.; Micciche, G.; Tincani, A. [ENEA C. R. Brasimone, 40032 Camugnano, Bologna (Italy)

    2012-08-15

    Highlights: Black-Right-Pointing-Pointer IFMIF-EVEDA target assembly thermo-mechanical behavior has been investigated. Black-Right-Pointing-Pointer Finite element method has been followed and a commercial code has been used. Black-Right-Pointing-Pointer Nominal, design and pressure test steady state scenarios and start-up transient conditions have been investigated. Black-Right-Pointing-Pointer Steady state results have shown that back-plate yielding may occur only under the design scenario. Black-Right-Pointing-Pointer Transient analysis has indicated that TA start-up lasts for {approx}60 h. - Abstract: Within the framework of the IFMIF R and D program and in close cooperation with ENEA-Brasimone, at the Department of Energy of the University of Palermo a research campaign has been launched to investigate the thermo-mechanical behavior of the target assembly under both steady state and start-up transient conditions. A theoretical approach based on the finite element method (FEM) has been followed and a well-known commercial code has been adopted. A realistic 3D FEM model of the target assembly has been set-up and optimized by running a mesh independency analysis. A proper set of loads and boundary conditions, mainly concerned with radiation heat transfer between the target assembly external walls and the inner walls of its containment vessel, have been considered and the target assembly thermo-mechanical behavior under nominal, design and pressure test steady state scenarios and start-up transient conditions has been investigated. Results are herewith reported and discussed.

  8. Thermomechanical behavior modeling and experimental validation of polymer-wound composite multi-layers. Hydrogen storage application

    International Nuclear Information System (INIS)

    Gentilleau, Benoit

    2012-01-01

    The purpose of this research is to study the thermomechanical behavior of the constituent materials of a type IV hydrogen storage tank: a composite, ensuring the strength, is wound around the polyurethane liner that ensures sealing of the tank and thermal insulation; at the extremities, stainless steel parts are used to allow the process connection. In this type of tank, during filling, there is a significant increase in hydrogen temperature, resulting in a gradual heating of the structure and the presence of temperature gradients. The purpose of this study is primarily to characterize the behavior of such a structure when subjects to complex thermomechanical loading. Initially, mechanical and thermal characterization tests have been made over the service life range of temperature of the tank to obtain the necessary data for the realization of a thermomechanical numerical model. Then, a behavior law of the composite, easily transferable to a complex structure such as the whole tank and taking into account the non-linearity, the matrix damage, the progressive loss of shear modulus, and the thermo-dependence of the materials parameters, is developed. The tests on technological representative specimens have been performed to better understand the mechanisms that can appear in the tank and to validate the model. Finally, a numerical study of a tank was performed. The coupled influence of temperature and damage matrix on the behavior of this structure is analyzed. (author)

  9. Thermomechanical modelling of laser surface glazing for H13 tool steel

    Science.gov (United States)

    Kabir, I. R.; Yin, D.; Tamanna, N.; Naher, S.

    2018-03-01

    A two-dimensional thermomechanical finite element (FE) model of laser surface glazing (LSG) has been developed for H13 tool steel. The direct coupling technique of ANSYS 17.2 (APDL) has been utilised to solve the transient thermomechanical process. A H13 tool steel cylindrical cross-section has been modelled for laser power 200 W and 300 W at constant 0.2 mm beam width and 0.15 ms residence time. The model can predict temperature distribution, stress-strain increments in elastic and plastic region with time and space. The crack formation tendency also can be assumed by analysing the von Mises stress in the heat-concentrated zone. Isotropic and kinematic hardening models have been applied separately to predict the after-yield phenomena. At 200 W laser power, the peak surface temperature achieved is 1520 K which is below the melting point (1727 K) of H13 tool steel. For laser power 300 W, the peak surface temperature is 2523 K. Tensile residual stresses on surface have been found after cooling, which are in agreement with literature. Isotropic model shows higher residual stress that increases with laser power. Conversely, kinematic model gives lower residual stress which decreases with laser power. Therefore, both plasticity models could work in LSG for H13 tool steel.

  10. Thermomechanical behaviour of bolted assemblies

    International Nuclear Information System (INIS)

    Scliffet, L.

    1995-01-01

    This paper presents first results obtained in an R and D study on the thermomechanical behaviour of bolted assemblies. Thermal shocks during operating transients both severely distort such assemblies and cause variations in stud pre-loads. So during a hot shock, the thermal gradient in the flange induced over-tightening due to the differential thermal expansion involved. Over-tightening can reach 70% of the nominal value, usually after 10 to 15 mn, after which the stress relaxes as soon as the heating affects the stud. A series of hot shocks causes assembly fatigue, notably resulting in thread plasticization, making it impossible to tighten the studs. In the case of cold transients, the reverse phenomenon is observed. The hot flange contracts sharply upon contact with the cold fluid, causing stress relief in the expanded studs. The resulting loss of tensile stress, which reaches up to 50%, can then cause severe leakage, especially if the nominal tightening capacity is already impaired. The study presented is based on tests and modelling. (author). 16 figs

  11. Thermomechanical evaluation of BWR fuel elements for procedures of preconditioned with FEMAXI-V

    International Nuclear Information System (INIS)

    Hernandez L, H.; Lucatero, M.A.; Ortiz V, J.

    2006-01-01

    The limitations in the burnt of the nuclear fuel usually are fixed by the one limit in the efforts to that undergo them the components of a nuclear fuel assembly. The limits defined its provide the direction to the fuel designer to reduce to the minimum the fuel failure during the operation, and they also prevent against some thermomechanical phenomena that could happen during the evolution of transitory events. Particularly, a limit value of LHGR is fixed to consider those physical phenomena that could lead to the interaction of the pellet-shirt (Pellet Cladding Interaction, PCI). This limit value it is related directly with an PCI limit that can be fixed based on experimental tests of power ramps. This way, to avoid to violate the PCI limit, the conditioning procedures of the fuel are still required for fuel elements with and without barrier. Those simulation procedures of the power ramp are carried out for the reactor operator during the starting maneuvers or of power increase like preventive measure of possible consequences in the thermomechanical behavior of the fuel. In this work, the thermomechanical behavior of two different types of fuel rods of the boiling water reactor is analyzed during the pursuit of the procedures of fuel preconditioning. Five diverse preconditioning calculations were carried out, each one with three diverse linear ramps of power increments. The starting point of the ramps was taken of the data of the cycle 8 of the unit 1 of the Laguna Verde Nucleo electric Central. The superior limit superior of the ramps it was the threshold of the lineal power in which a fuel failure could be presented by PCI, in function of the fuel burnt. The analysis was carried out with the FEMAXI-V code. (Author)

  12. Effect of quinoa and potato flours on the thermomechanical and breadmaking properties ofwheat flour

    Directory of Open Access Journals (Sweden)

    E. Rodriguez-Sandoval

    2012-09-01

    Full Text Available The thermomechanical properties of dough and the physical characteristics of bread from quinoa-wheat and potato-wheat composite flours at 10 and 20% substitution level were evaluated. The functional properties of flours were measured by the water absorption index (WAI, water solubility index (WSI and swelling power (SP. The thermomechanical properties of wheat and composite flours were assessed using a Mixolab and the baking quality characteristics of breads were weight, height, width, and specific volume. The results showed that the higher values of WAI (4.48, WSI (7.45%, and SP (4.84 were for potato flour. The quinoa-wheat composite flour presented lower setback and cooking stability data, which are a good indicator of shelf life of bread. On the other hand, the potato-wheat composite flour showed lower stability, minimum torque and peak torque, and higher water absorption. Weight, height, width, and specific volume of wheat bread were most similar to samples of potato-wheat composite flour at 10% substitution level.

  13. Experimental investigations on the state of the friction-welded joint zone in steel hybrid components after process-relevant thermo-mechanical loadings

    Science.gov (United States)

    Behrens, B.-A.; Bouguecha, A.; Vucetic, M.; Peshekhodov, I.; Matthias, T.; Kolbasnikov, N.; Sokolov, S.; Ganin, S.

    2016-10-01

    As a part of the newly established Collaborative Research Center 1153 (SFB 1153) "Process chain for the manufacturing of hybrid high-performance components by tailored forming" at the Leibniz Universität Hannover, the Institute of Forming Technology and Machines (IFUM) examines the influence of thermo-mechanical stresses on the reduced Young's modulus as well as the hardness of hybrid (steel-steel compound) joined semi-finished products. Currently the expertise in the production of bulk metal formed parts is limited to mono-materials. For manufacturing parts of hybrid materials and also for the methods of the new process routes, practical experience has to be gained. The subproject C1 within the collaborative research center 1153 with the short title "Failure Prediction" deals with the question, if the hybrid semi-finished products fulfill the thermo-mechanical demands or if they fail at the joining zone (JZ) during forging. For this purpose, stresses similar to those in the process were imposed on hybrid semi-finished products by torsion tests by using the thermo-mechanical test system Gleeble 3800. Afterwards, the specimens were examined metallographically and by nanoindentations with the help of a TriboIndenter TI950. Thus, first knowledge on the behaviour of thermo-mechanical stresses on the reduced Young's modulus and the hardness of hybrid joined semi-finished parts was gained.

  14. Thermomechanical studies in granite at Stripa, Sweden

    International Nuclear Information System (INIS)

    Cook, N.G.W.; Myer, L.R.

    1981-01-01

    Media other than rock salt are being considered for the deep, geologic disposal of nuclear wastes. The disposal of high-level nuclear waste in a deep, underground repository will subject the rock to a thermal pulse that will induce displacements, strains, and stresses in the rock. Thermomechanical experiments, with electrical heaters simulating the thermal output of waste canisters, were carried out in granite at a depth of 340 m below surface adjacent to a defunct iron ore mine at Stripa, Sweden. Changes in temperature, displacement, and stress in the rock around these heaters were measured, and the measurements were compared with predictions calculated from the theory of linear thermoelasticity. Measured temperature changes agreed well with predictions, but measured displacements and stresses were consistently less than those predicted with constant values for the coefficient of thermal expansion and elastic properties of the rock. A laboratory test program to measure these coefficients over ranges of stress and temperature representing those in the field experiment has been initiated. Test specimens were taken from cores recovered from the instrumentation holes in the Stripa experiments. Preliminary results from laboratory tests on specimens free of joints indicate that the values of Young's modulus and Poisson's ratio increase from about 60 to 80 MPa and from 0.15 to 0.22, respectively, as the confining stress is increased from 2 to 55 MPa; these values decrease with increasing temperature, more so at 2 MPa than at 55 MPa. The linear coefficient of thermal expansion at a confining stress of 30 MPa increases from about 10 x 10 - 6 / 0 C at 40 0 C to about 14 x 10 - 6 / 0 C. The magnitudes of these changes are not sufficient to resolve the disparity between measured and predicted results. Perhaps the properties of test specimens containing joints will show greater variations in the values of the thermomechanical coefficients with temperature and pressure

  15. Thermo-mechanical actuator-based miniature tagging module for localization in capsule endoscopy

    Science.gov (United States)

    Chandrappan, Jayakrishnan; Ruiqi, Lim; Su, Nandar; Yen Yi, Germaine Hoe; Vaidyanathan, Kripesh

    2011-04-01

    Capsule endoscopy is a frontline medical diagnostic tool for the gastro intestinal tract disorders. During diagnosis, efficient localization techniques are essential to specify a pathological area that may require further diagnosis or treatment. This paper presents the development of a miniature tagging module that relies on a novel concept to label the region of interest and has the potential to integrate with a capsule endoscope. The tagging module is a compact thermo-mechanical actuator loaded with a biocompatible micro tag. A low power microheater attached to the module serves as the thermal igniter for the mechanical actuator. At optimum temperature, the actuator releases the micro tag instantly and penetrates the mucosa layer of a GI tract, region of interest. Ex vivo animal trials are conducted to verify the feasibility of the tagging module concept. X-ray imaging is used to detect the location of the micro tag embedded in the GI tract wall. The method is successful, and radiopaque micro tags can provide valuable pre-operative position information on the infected area to facilitate further clinical procedures.

  16. A Simple FEM Formulation Applied to Nonlinear Problems of Impact with Thermomechanical Coupling

    Directory of Open Access Journals (Sweden)

    João Paulo de Barros Cavalcante

    Full Text Available Abstract The thermal effects of problems involving deformable structures are essential to describe the behavior of materials in feasible terms. Verifying the transformation of mechanical energy into heat it is possible to predict the modifications of mechanical properties of materials due to its temperature changes. The current paper presents the numerical development of a finite element method suitable for nonlinear structures coupled with thermomechanical behavior; including impact problems. A simple and effective alternative formulation is presented, called FEM positional, to deal with the dynamic nonlinear systems. The developed numerical is based on the minimum potential energy written in terms of nodal positions instead of displacements. The effects of geometrical, material and thermal nonlinearities are considered. The thermodynamically consistent formulation is based on the laws of thermodynamics and the Helmholtz free-energy, used to describe the thermoelastic and the thermoplastic behaviors. The coupled thermomechanical model can result in secondary effects that cause redistributions of internal efforts, depending on the history of deformation and material properties. The numerical results of the proposed formulation are compared with examples found in the literature.

  17. Thermomechanical CSM analysis of a superheater tube in transient state

    Science.gov (United States)

    Taler, Dawid; Madejski, Paweł

    2011-12-01

    The paper presents a thermomechanical computational solid mechanics analysis (CSM) of a pipe "double omega", used in the steam superheaters in circulating fluidized bed (CFB) boilers. The complex cross-section shape of the "double omega" tubes requires more precise analysis in order to prevent from failure as a result of the excessive temperature and thermal stresses. The results have been obtained using the finite volume method for transient state of superheater. The calculation was carried out for the section of pipe made of low-alloy steel.

  18. Time limited psychodynamic group therapy: Predictors of patients seeking additional treatment

    DEFF Research Database (Denmark)

    Jensen, Hans Henrik; Mortensen, Erik Lykke; Lotz, Martin

    2010-01-01

    for psychological or psychiatric problems; the percentage was 41.6 when further treatment was defined as participating in more than 5 sessions. The majority (94.8 was treated within the public health services. Participation in additional treatment was predicted by improvement on the MCMI Antisocial personality...... disorder scale and a higher SCL-90-R Somatization end-state score. When additional treatment was defined as receiving more than 5 sessions, lack of paid work before treatment (odds ratio 8.0), lack of social network support (odds ratio 2.9), and the Antisocial pre-post difference score (odds ratio 1...

  19. Plasmonically enhanced thermomechanical detection of infrared radiation.

    Science.gov (United States)

    Yi, Fei; Zhu, Hai; Reed, Jason C; Cubukcu, Ertugrul

    2013-04-10

    Nanoplasmonics has been an attractive area of research due to its ability to localize and manipulate freely propagating radiation on the nanometer scale for strong light-matter interactions. Meanwhile, nanomechanics has set records in the sensing of mass, force, and displacement. In this work, we report efficient coupling between infrared radiation and nanomechanical resonators through nanoantenna enhanced thermoplasmonic effects. Using efficient conversion of electromagnetic energy to mechanical energy in this plasmo-thermomechanical platform with a nanoslot plasmonic absorber integrated directly on a nanobeam mechanical resonator, we demonstrate room-temperature detection of nanowatt level power fluctuations in infrared radiation. We expect our approach, which combines nanoplasmonics with nanomechanical resonators, to lead to optically controlled nanomechanical systems enabling unprecedented functionality in biomolecular and toxic gas sensing and on-chip mass spectroscopy.

  20. Advance development of a technique for characterizing the thermomechanical properties of thermally stable polymers

    Science.gov (United States)

    Gillham, J. K.; Stadnicki, S. J.; Hazony, Y.

    1974-01-01

    The torsional braid experiment has been interfaced with a centralized hierarchical computing system for data acquisition and data processing. Such a system, when matched by the appropriate upgrading of the monitoring techniques, provides high resolution thermomechanical spectra of rigidity and damping, and their derivatives with respect to temperature.

  1. Thermomechanical processing of Nb-1Zr-0.1C alloy for use in compact high temperature reactors: a first report

    International Nuclear Information System (INIS)

    Chakravartty, J.K.; Kapoor, R.; Suri, A.K.

    2011-08-01

    Nb-1Zr-0.1C is a potential material for use in high temperature nuclear reactors. Use of this alloy in components requires appropriate thermomechanical processing to break the cast microstructure and to obtain uniformly distributed fine stable precipitates so as to produce the desired mechanical properties at the high operating temperatures. This report reviews the thermomechanical processing of Nb-1Zr-0.1C alloy carried out over the years by other researchers and the high temperature creep behavior of the alloy. The hot deformation of Nb-1Zr-0.1C alloy carried out at Mechanical Metallurgy Division is also presented here. From this review it is evident that most primary hot working studies were carried out between 1500 to 1700 degC. The subsequent annealing treatments, which require holding at lower temperatures of about 1100 to 1300 degC for very long times help further transform the precipitates from coarse orthorhombic to very fine cubic. Our studies on Nb-1Zr-0.1C alloy also confirm that optimum hot working lies at temperatures beyond 1500 degC where dynamic recrystallization initiates, and optimally around 1700 degC where dynamic recrystallization transforms the microstructure. Working at temperatures lower than 1000 degC may lead to the undesirable effect of both micro as well as macro strain localization, and should be avoided. (author)

  2. Global thermo-mechanical effects from a KBS-3 type repository. Summary report

    International Nuclear Information System (INIS)

    Hakami, E.; Olofsson, Stig-Olof; Hakami, H.; Israelsson, Jan

    1998-04-01

    The objective of this study has been to identify the global thermomechanical effects in the bedrock hosting a nuclear waste repository - i.e. the effects at large distances from the repository. Numerical thermomechanical modeling was performed in several steps, beginning with elastic continuum models and followed by distinct element models (3DEC), in which fracture zones are explicitly simulated. The number of fracture zones, the heat intensity of the waste, the material properties of the rock mass and the boundary conditions of the models were varied in different simulations. The results from the numerical modeling show that the principal stresses increase near the repository. The maximum stress obtained for the main model is 44 MPa and occurs at the repository level after about 100 years of deposition. Due to thermal expansion, the rock mass displaces upward, and the maximum heave at the ground surface after 1000 years is calculated to be 16 cm. In the area close to the ground surface, above the center of the repository, the horizontal stresses reduce, causing the rock to yield in tension down to a depth of about 80 m. In correspondence with the stress changes, the fracture zones show opening normal displacements at shallow depths and closing normal displacements and shearing at the repository level. The maximum displacements of the different fracture zones are 0.3-2.5 cm for closing, 0.0-0.8 cm for opening and 0.2-2.2 cm for shearing. Another important input parameter for the analysis is the Young's modulus of the rock mass. In the main model, a value of 30 GPa is assumed. Higher values of Young's modulus give larger thermo-mechanical effects. Other changes of the properties considered give minor changes of the rock mass behavior. All multi-level repository layouts give rise to higher temperatures than the single-level layout, causing the compressive stresses to increase more at the repository level. Fracture zone displacements caused by different layouts are

  3. Effects of thermomechanical process on the microstructure and mechanical properties of a fully martensitic titanium-based biomedical alloy.

    Science.gov (United States)

    Elmay, W; Prima, F; Gloriant, T; Bolle, B; Zhong, Y; Patoor, E; Laheurte, P

    2013-02-01

    Thermomechanical treatments have been proved to be an efficient way to improve superelastic properties of metastable β type titanium alloys through several studies. In this paper, this treatment routes, already performed on superelastic alloys, are applied to the Ti-24Nb alloy (at%) consisting of a pure martensite α'' microstructure. By short-time annealing treatments performed on the heavily deformed material, an interesting combination of a large recoverable strain of about 2.5%, a low elastic modulus (35 GPa) and a high strength (900 MPa) was achieved. These properties are shown to be due to a complex microstructure consisting of the precipitation of nanoscale (α+ω) phases in ultra-fine β grains. This microstructure allows a superelastic behavior through stress-induced α'' martensitic transformation. In this study, the microstructures were characterized by X-ray diffraction and transmission electron microscopy and the evolution of the elastic modulus and the strain recovery as a function of the applied strain was investigated through loading-unloading tensile tests. Copyright © 2012 Elsevier Ltd. All rights reserved.

  4. Thermomechanical Stress in Cryopreservation Via Vitrification With Nanoparticle Heating as a Stress-Moderating Effect.

    Science.gov (United States)

    Eisenberg, David P; Bischof, John C; Rabin, Yoed

    2016-01-01

    This study focuses on thermomechanical effects in cryopreservation associated with a novel approach of volumetric heating by means on nanoparticles in an alternating electromagnetic field. This approach is studied for the application of cryopreservation by vitrification, where the crystalline phase is completely avoided-the cornerstone of cryoinjury. Vitrification can be achieved by quickly cooling the material to cryogenic storage, where ice cannot form. Vitrification can be maintained at the end of the cryogenic protocol by quickly rewarming the material back to room temperature. The magnitude of the rewarming rates necessary to maintain vitrification is much higher than the magnitude of the cooling rates that are required to achieve it in the first place. The most common approach to achieve the required cooling and rewarming rates is by exposing the specimen's surface to a temperature-controlled environment. Due to the underlying principles of heat transfer, there is a size limit in the case of surface heating beyond which crystallization cannot be prevented at the center of the specimen. Furthermore, due to the underlying principles of solid mechanics, there is a size limit beyond which thermal expansion in the specimen can lead to structural damage and fractures. Volumetric heating during the rewarming phase of the cryogenic protocol can alleviate these size limitations. This study suggests that volumetric heating can reduce thermomechanical stress, when combined with an appropriate design of the thermal protocol. Without such design, this study suggests that the level of stress may still lead to structural damage even when volumetric heating is applied. This study proposes strategies to harness nanoparticles heating in order to reduce thermomechanical stress in cryopreservation by vitrification.

  5. FY15 Report on Thermomechanical Testing

    Energy Technology Data Exchange (ETDEWEB)

    Hansen, Francis D. [Sandia National Laboratories (SNL-NM), Albuquerque, NM (United States); Buchholz, Stuart [RESPEC, Rapid City, SD (United States)

    2015-08-01

    Sandia is participating in the third phase of a United States (US)-German Joint Project that compares constitutive models and simulation procedures on the basis of model calculations of the thermomechanical behavior and healing of rock salt (Salzer et al. 2015). The first goal of the project is to evaluate the ability of numerical modeling tools to correctly describe the relevant deformation phenomena in rock salt under various influences. Among the numerical modeling tools required to address this are constitutive models that are used in computer simulations for the description of the thermal, mechanical, and hydraulic behavior of the host rock under various influences and for the long-term prediction of this behavior. Achieving this goal will lead to increased confidence in the results of numerical simulations related to the secure disposal of radioactive wastes in rock salt. Results of the Joint Project may ultimately be used to make various assertions regarding stability analysis of an underground repository in salt during the operating phase as well as long-term integrity of the geological barrier in the post-operating phase A primary evaluation of constitutive model capabilities comes by way of predicting large-scale field tests. The Joint Project partners decided to model Waste Isolation Pilot Plant (WIPP) Rooms B & D which are full-scale rooms having the same dimensions. Room D deformed under natural, ambient conditions while Room B was thermally driven by an array of waste-simulating heaters (Munson et al. 1988; 1990). Existing laboratory test data for WIPP salt were carefully scrutinized and the partners decided that additional testing would be needed to help evaluate advanced features of the constitutive models. The German partners performed over 140 laboratory tests on WIPP salt at no charge to the US Department of Energy (DOE).

  6. Inorganic fullerene-like IF-WS_2/PVB nanocomposites of improved thermo-mechanical and tribological properties

    International Nuclear Information System (INIS)

    Simić, Danica; Stojanović, Dušica B.; Kojović, Aleksandar; Dimić, Mirjana; Totovski, Ljubica; Uskoković, Petar S.; Aleksić, Radoslav

    2016-01-01

    The subject of this research is to explore the possibility of preparation of nanocomposite material of improved thermo-mechanical and tribological properties, using inorganic fullerene-like tungsten disulfide nanostructures (IF-WS_2) as reinforcement in poly(vinyl butyral) (PVB). This paper also reports investigation of the effects of using different solvents in preparation of PVB/IF-WS_2 nanocomposite on the thermo-mechanical behavior of the resulting material. PVB was dissolved in ethanol, isopropanol, n-butanol and ethyl acetate. IF-WS_2 nanoparticles were added to these PVB solutions and dispersed by different deagglomeration techniques. Samples were dried and thin films were obtained. Their microstructure and the quality of IF-WS_2 dispersion and deagglomeration in PVB matrix was analyzed by scanning electron microscope (SEM). The reinforcing effect of IF-WS_2 is examined by determining hardness, reduced modulus of elasticity and coefficient of friction, by nanoindentation and nanoscratch test, in terms of the different solvents applied in preparation of the samples, mode of stirring and different contents of IF-WS_2. The glass transition temperature (T_g) was determined for the prepared samples using differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMA). Storage modulus and mechanical loss factor were observed in a defined temperature range using DMA. - Highlights: • Poly(vinyl butyral)/tungsten disulfide nanocomposites were examined. • Different solvents and deagglomeration methods affect the properties of composites. • Nanoindentation and scratch test, PSD, SEM, DSC and DMTA were analyzed. • Thermo-mechanical and antifriction properties of composite material are improved.

  7. Parametric optimization of the MVC desalination plant with thermomechanical compressor

    Science.gov (United States)

    Blagin, E. V.; Biryuk, V. V.; Anisimov, M. Y.; Shimanov, A. A.; Gorshkalev, A. A.

    2018-03-01

    This article deals with parametric optimization of the Mechanical Vapour Compression (MVC) desalination plant with thermomechanical compressor. In this plants thermocompressor is used instead of commonly used centrifugal compressor. Influence of two main parameters was studied. These parameters are: inlet pressure and number of stages. Analysis shows that it is possible to achieve better plant performance in comparison with traditional MVC plant. But is required reducing the number of stages and utilization of low or high initial pressure with power consumption maximum at approximately 20-30 kPa.

  8. Design and verification of thermomechanical parameters of P/M Ti6Al4V alloy forging

    Energy Technology Data Exchange (ETDEWEB)

    Wojtaszek, Marek, E-mail: mwojtasz@metal.agh.edu.pl; Śleboda, Tomasz

    2014-12-05

    Highlights: • Thermomechanical parameters of P/M Ti6Al4V alloy processing were determined. • The use of the mixture of elemental powders allows reducing manufacturing costs. • Numerical modelling allowed to elaborate favourable parameters of forging. • The industrial trials of hot forging of P/M Ti6Al4V alloy were successful. - Abstract: This work is focused on the design of technology of forging high-quality Ti6Al4V alloy by means of powder metallurgy methods. A mixture of elemental powders, with the chemical composition of that of Ti6Al4V alloy, was used as a starting material for the investigation. Powder mixtures were fully densified by hot compaction under precisely controlled conditions. The mechanical properties of the obtained compacts were examined. The mechanical behaviour of the investigated alloy powder compacts was evaluated by compression test under various thermomechanical conditions using Gleeble simulator. The microstructure of powder compacts as well as P/M alloy samples deformed in compression tests was examined. All data obtained from the experimental tests were applied as boundary conditions for numerical simulation of forging of selected forgings. Basing on the results of both plastometric tests and simulations, thermomechanical parameters of the investigated alloy forging were determined. Designed parameters of forging technology were verified by forging trials performed in industrial conditions. The quality of the obtained forgings was examined by means of computed tomography.

  9. Design and verification of thermomechanical parameters of P/M Ti6Al4V alloy forging

    International Nuclear Information System (INIS)

    Wojtaszek, Marek; Śleboda, Tomasz

    2014-01-01

    Highlights: • Thermomechanical parameters of P/M Ti6Al4V alloy processing were determined. • The use of the mixture of elemental powders allows reducing manufacturing costs. • Numerical modelling allowed to elaborate favourable parameters of forging. • The industrial trials of hot forging of P/M Ti6Al4V alloy were successful. - Abstract: This work is focused on the design of technology of forging high-quality Ti6Al4V alloy by means of powder metallurgy methods. A mixture of elemental powders, with the chemical composition of that of Ti6Al4V alloy, was used as a starting material for the investigation. Powder mixtures were fully densified by hot compaction under precisely controlled conditions. The mechanical properties of the obtained compacts were examined. The mechanical behaviour of the investigated alloy powder compacts was evaluated by compression test under various thermomechanical conditions using Gleeble simulator. The microstructure of powder compacts as well as P/M alloy samples deformed in compression tests was examined. All data obtained from the experimental tests were applied as boundary conditions for numerical simulation of forging of selected forgings. Basing on the results of both plastometric tests and simulations, thermomechanical parameters of the investigated alloy forging were determined. Designed parameters of forging technology were verified by forging trials performed in industrial conditions. The quality of the obtained forgings was examined by means of computed tomography

  10. Advanced Environmental Barrier Coating and SA Tyrannohex SiC Composites Integration for Improved Thermomechanical and Environmental Durability

    Science.gov (United States)

    Zhu, Dongming; Halbig, Michael; Singh, Mrityunjay

    2018-01-01

    The development of 2700 degF capable environmental barrier coating (EBC) systems, particularly, the Rare Earth "Hafnium" Silicon bond coat systems, have significantly improved the temperature capability and environmental stability of SiC/SiC Ceramic Matrix Composite Systems. We have specifically developed the advanced 2700 degF EBC systems, integrating the EBC to the high temperature SA Tyrannohex SiC fiber composites, for comprehensive performance and durability evaluations for potential turbine engine airfoil component applications. The fundamental mechanical properties, environmental stability and thermal gradient cyclic durability performance of the EBC - SA Tyrannohex composites were investigated. The paper will particularly emphasize the high pressure combustion rig recession, cyclic thermal stress resistance and thermomechanical low cycle fatigue testing of uncoated and environmental barrier coated Tyrannohex SiC SA composites in these simulated turbine engine combustion water vapor, thermal gradients, and mechanical loading conditions. We have also investigated high heat flux and flexural fatigue degradation mechanisms, determined the upper limits of operating temperature conditions for the coated SA composite material systems in thermomechanical fatigue conditions. Recent progress has also been made by using the self-healing rare earth-silicon based EBCs, thus enhancing the SA composite hexagonal fiber columns bonding for improved thermomechanical and environmental durability in turbine engine operation environments. More advanced EBC- composite systems based on the new EBC-Fiber Interphases will also be discussed.

  11. Thermo-mechanical analysis of a user filter assembly for undulator/wiggler operations at the Advanced Photon Source

    International Nuclear Information System (INIS)

    Nian, H.L.T.; Kuzay, T.M.; Collins, J.; Shu, D.; Benson, C.; Dejus, R.

    1996-01-01

    This paper reports a thermo-mechanical study of a beamline filter (user filter) for undulator/wiggler operations. It is deployed in conjunction with the current commissioning window assembly on the APS insertion device (ID) front ends. The beamline filter at the Advanced Photon Source (APS) will eventually be used in windowless operations also. Hence survival and reasonable life expectancy of the filters under intense insertion device (ID) heat flu are crucial to the beamline operations. To accommodate various user requirements, the filter is configured to be a multi-choice type and smart to allow only those filter combinations that will be safe to operate with a given ring current and beamline insertion device gap. However, this paper addresses only the thermo-mechanical analysis of individual filter integrity and safety in all combinations possible. The current filter design is configured to have four filter frames in a cascade with each frame holding five filters. This allows a potential 625 total filter combinations. Thermal analysis for all of these combinations becomes a mammoth task considering the desired choices for filter materials (pyrolitic graphite and metallic filters), filter thicknesses, undulator gaps, and the beam currents. The paper addresses how this difficult task has been reduced to a reasonable effort and computational level. Results from thermo-mechanical analyses of the filter combinations are presented both in tabular and graphical format

  12. Rheological, thermo-mechanical, and baking properties of wheat-millet flour blends.

    Science.gov (United States)

    Aprodu, Iuliana; Banu, Iuliana

    2015-07-01

    Millet has long been known as a good source of fiber and antioxidants, but only lately started to be exploited by food scientists and food industry as a consequence of increased consumer awareness. In this study, doughs and breads were produced using millet flour in different ratios (10, 20, 30, 40, and 50%) to white, dark, and whole wheat flour. The flour blends were evaluated in terms of rheological and thermo-mechanical properties. Fundamental rheological measurements revealed that the viscosity of the flour formulations increases with wheat flour-extraction rate and decreases with the addition of millet flour. Doughs behavior during mixing, overmixing, pasting, and gelling was established using the Mixolab device. The results of this bread-making process simulation indicate that dough properties become critical for the flour blends with millet levels higher than 30%. The breads were evaluated for volume, texture, and crumb-grain characteristics. The baking test and sensory evaluation results indicated that substitution levels of up to 30% millet flour could be used in composite bread flour. High levels of millet flour (40 and 50%) negatively influenced the loaf volume, crumb texture, and taste. © The Author(s) 2014.

  13. Thermo-mechanical efficiency of the bimetallic strip heat engine at the macro-scale and micro-scale

    International Nuclear Information System (INIS)

    Arnaud, A; Boughaleb, J; Monfray, S; Boeuf, F; Skotnicki, T; Cugat, O

    2015-01-01

    Bimetallic strip heat engines are energy harvesters that exploit the thermo-mechanical properties of bistable bimetallic membranes to convert heat into mechanical energy. They thus represent a solution to transform low-grade heat into electrical energy if the bimetallic membrane is coupled with an electro-mechanical transducer. The simplicity of these devices allows us to consider their miniaturization using MEMS fabrication techniques. In order to design and optimize these devices at the macro-scale and micro-scale, this article proposes an explanation of the origin of the thermal snap-through by giving the expressions of the constitutive equations of composite beams. This allows us to evaluate the capability of bimetallic strips to convert heat into mechanical energy whatever their size is, and to give the theoretical thermo-mechanical efficiencies which can be obtained with these harvesters. (paper)

  14. Improvement of high temperature fatigue lifetime in AZ91 magnesium alloy by heat treatment

    International Nuclear Information System (INIS)

    Mokhtarishirazabad, Mehdi; Azadi, Mohammad; Hossein Farrahi, Gholam; Winter, Gerhard; Eichlseder, Wilfred

    2013-01-01

    In the present paper, an improvement in high temperature fatigue properties of the AZ91 magnesium alloy with rare earth elements has been obtained by a typical heat treatment, denoted by T6. For this objective, out-of-phase thermo-mechanical fatigue, room temperature and high temperature low cycle fatigue tests are performed to compare lifetimes. Several rare earth elements are initially added to the AZ91 alloy during a gravity casting process in permanent molds. Also, the type of the heat treatment is examined. Results of specimens with only the solution (the T4 heat treatment) and the solution with the ageing process (the T6 heat treatment) are compared under isothermal fatigue loadings. Microstructural investigations are carried out, before and after fatigue experiments to demonstrate the heat treatment effect. Results showed that both low cycle fatigue and thermo-mechanical fatigue of the alloy at high temperatures increases tremendously after the T6 heat treatment. This behavior attributes to the variation of the ductility, which was a result of microstructural changes during the heat treatment and the varying temperature in fatigue tests

  15. Improvement of high temperature fatigue lifetime in AZ91 magnesium alloy by heat treatment

    Energy Technology Data Exchange (ETDEWEB)

    Mokhtarishirazabad, Mehdi [School of Metallurgy and Materials Engineering, Iran University of Science and Technology, Tehran (Iran, Islamic Republic of); Azadi, Mohammad, E-mail: m_azadi@ip-co.com [Fatigue and Wear Workgroup, Irankhodro Powertrain Company (IPCO), Tehran (Iran, Islamic Republic of); Hossein Farrahi, Gholam [School of Mechanical Engineering, Sharif University of Technology, Tehran (Iran, Islamic Republic of); Winter, Gerhard; Eichlseder, Wilfred [Chair of Mechanical Engineering, University of Leoben, Leoben (Austria)

    2013-12-20

    In the present paper, an improvement in high temperature fatigue properties of the AZ91 magnesium alloy with rare earth elements has been obtained by a typical heat treatment, denoted by T6. For this objective, out-of-phase thermo-mechanical fatigue, room temperature and high temperature low cycle fatigue tests are performed to compare lifetimes. Several rare earth elements are initially added to the AZ91 alloy during a gravity casting process in permanent molds. Also, the type of the heat treatment is examined. Results of specimens with only the solution (the T4 heat treatment) and the solution with the ageing process (the T6 heat treatment) are compared under isothermal fatigue loadings. Microstructural investigations are carried out, before and after fatigue experiments to demonstrate the heat treatment effect. Results showed that both low cycle fatigue and thermo-mechanical fatigue of the alloy at high temperatures increases tremendously after the T6 heat treatment. This behavior attributes to the variation of the ductility, which was a result of microstructural changes during the heat treatment and the varying temperature in fatigue tests.

  16. Thermomechanical processing of In-containing β-type Ti-Nb alloys.

    Science.gov (United States)

    Pilz, Stefan; Geissler, David; Calin, Mariana; Eckert, Jürgen; Zimmermann, Martina; Freudenberger, Jens; Gebert, Annett

    2018-03-01

    In this study, the effect of thermomechanical processing on microstructure evolution of the indium-containing β-type Ti alloys (Ti-40Nb)-3.5In and (Ti-36Nb)-3.5In was examined. Both alloys show an increased β-phase stability compared to binary alloys due to In additions. This leads to a reduced α''-phase fraction in the solution treated and recrystallized state in the case of (Ti-36Nb)-3.5In and to the suppression of stress-induced α'' formation and deformation twinning for (Ti-40Nb)-3.5In. The mechanical properties of the alloys were subsequently studied by quasistatic tensile tests in the recrystallized state, revealing reduced Young's modulus values of 58GPa ((Ti-40Nb)-3.5In) and 56GPa ((Ti-36Nb)-3.5In) compared to 60GPa as determined for Ti-40Nb. For both In-containing alloys the ultimate tensile strength is in the range of 560MPa. Due to the suppressed α'' formation, (Ti-40Nb)-3.5In exhibits a linear elastic deformation behavior during tensile loading together with a low Young's modulus and is therefore promising for load-bearing implants. Copyright © 2018 Elsevier Ltd. All rights reserved.

  17. Thermomechanical analyses of conceptual repository designs for the Paradox and Permian Basins

    International Nuclear Information System (INIS)

    Loken, M.C.; Callahan, G.D.; Svalstad, D.K.; Wagner, R.A.

    1987-11-01

    The potential repositories are designed to accommodate all waste forms emplaced at various thermal loadings; specifically, commercial high-level waste (30 W/m 2 ), spent fuel (15 W/m 2 ), defense high-level waste (20 W/m 2 ), and remote-handled and contact-handled transuranic nonheat-generating waste. The study evaluates the design parameters, primarily thermal loading, based on a comparison of calculable thermomechanical parameters with prescribed performance constraints. This evaluation was accomplished by numerical simulation using finite element techniques of the canister, disposal room, and repository regions of each potential site. Important thermal and thermomechanical results were compared with their prescribed constraint or limit value. All of the performance constraints were satisfied at the Davis Canyon site in the Paradox Basin for commercial high-level waste, spent fuel, and defense high-level waste at areal thermal loadings of 20 W/m 2 , 15 W/m 2 , and 20 W/m 2 , respectively. Similarly, for the Deaf Smith County site in the Permian Basin, commercial high-level waste, spent fuel, and defense high-level waste thermal loadings of 13.5 W/m 2 , 8.5 W/m 2 , and 6.0 W/m 2 , respectively, satisfied all of the performance constraints. 89 refs., 64 figs., 22 tabs

  18. Thermomechanical damage of nucleosome by the shock wave initiated by ion passing through liquid water

    International Nuclear Information System (INIS)

    Yakubovich, Alexander V.; Surdutovich, Eugene; Solov’yov, Andrey V.

    2012-01-01

    We report on the results of full-atom molecular dynamics simulations of the heat spike in the water medium caused by the propagation of the heavy ion in the vicinity of its Bragg peak. High rate of energy transfer from an ion to the molecules of surrounding water environment leads to the rapid increase of the temperature of the molecules in the vicinity of ions trajectory. As a result of an abrupt increase of the temperature we observe the formation of the nanoscale shock wave propagating through the medium. We investigate the thermomechanical damage caused by the shock wave to the nucleosome located in the vicinity of heavy ion trajectory. We observe the substantial deformation of the DNA secondary structure. We show that the produced shock wave can lead to the thermomechanical breakage of the DNA backbone covalent bonds and present estimates for the number of such strand brakes per one cell nucleus.

  19. Computerized simulation of YAG pulse laser welding of titanium alloy (TA6V): experimental characterization and modelling of the thermomechanical aspects of this process

    International Nuclear Information System (INIS)

    Robert, Y.

    2007-09-01

    This work is a part of study which goal is to realize a computer modelling of the thermomechanical phenomena occurring during the YAG pulse laser welding of titanium alloy (TA6V). The filet welding has different heterogeneities (microstructural and mechanical). In fact, the temperature causes microstructural changes (phase transformations, precipitations) and modifies the mechanical properties. Thermomechanical modelling has thus to be established for the welding of TA6V. (author)

  20. Modelling of the thermomechanical behaviour of saturated clays: application to the radioactive wastes disposal

    International Nuclear Information System (INIS)

    Rahbaoui, A.

    1995-01-01

    During the waste disposal of containers, the clay barriers of backfill and the confining medium, which is essentially composed of clay, are submitted to heavy thermal stresses which induce volume change and can result in material failure. The clay, composed of solid skeleton, adsorbed water, and free water, is submitted to physico-chemical interactions which influence its thermomechanical behaviour, itself quits different from granular media such as sand. The principal factor responsible for this response is the effect of temperature on the clays water. Thus, the loss of special structure of adsorbed water and the increase in thickness of the diffused double-layer provoke microstructural rearrangement mechanisms of particles. Those mechanisms are strongly correlated with the mechanical state of material. When it is highly over-consolidated, an irreversible swelling occurs during thermal cycle, accompanied by a breaking up of the particles and a permanent expansion of meso-pores. The greater the OCR, the more important the thermal swelling. When the material is normally consolidated, the particles settle during heating under the external stress, which results in a denser rearrangement of the material. With a slight over-consolidated material, all the intermediate stages between the above mechanisms can be reached. However, cooling produces only a weak reversible compression characterising the thermal contraction of the components. Those microscopic phenomena have been used to elaborate a macroscopic thermomechanical model based on the Cam-Clay and the Hujeux Models. The model formulation includes a thermal softening, on one hand, by the reduction of the mechanical yield surface f c and the translation of the thermal yield surface f T (PTL), and, on the other hand, an irreversible thermal expansive volumetric strain. This approach of the problem was tested along various thermomechanical paths and especially on the laboratory tests, on the expansive and non expansive

  1. Influence of tragacanth gum in egg white based bioplastics: Thermomechanical and water uptake properties.

    Science.gov (United States)

    López-Castejón, María Luisa; Bengoechea, Carlos; García-Morales, Moisés; Martínez, Inmaculada

    2016-11-05

    This study aims to extend the range of applications of tragacanth gum by studying its incorporation into bioplastics formulation, exploring the influence that different gum contents (0-20wt.%) exert over the thermomechanical and water uptake properties of bioplastics based on egg white albumen protein (EW). The effect of plasticizer nature was also evaluated through the modification of the water/glycerol ratio within the plasticizer fraction (fixed at 40wt.%). The addition of tragacanth gum generally yielded an enhancement of the water uptake capacity, being doubled at the highest content. Conversely, presence of tragacanth gum resulted in a considerable decrease in the bioplastic mechanical properties: both tensile strength and maximum elongation were reduced up to 75% approximately when compared to the gum-free system. Ageing of selected samples was also studied, revealing an important effect of storage time when tragacanth gum is present, possibly due to its hydrophilic character. Copyright © 2016 Elsevier Ltd. All rights reserved.

  2. Finite Element Analysis of the Deformation of Functionally Graded Plates under Thermomechanical Loads

    Directory of Open Access Journals (Sweden)

    A. E. Alshorbagy

    2013-01-01

    Full Text Available The first-order shear deformation plate model, accounting for the exact neutral plane position, is exploited to investigate the uncoupled thermomechanical behavior of functionally graded (FG plates. Functionally graded materials are mainly constructed to operate in high temperature environments. Also, FG plates are used in many applications (such as mechanical, electrical, and magnetic, where an amount of heat may be generated into the FG plate whenever other forms of energy (electrical, magnetic, etc. are converted into thermal energy. Several simulations are performed to study the behavior of FG plates, subjected to thermomechanical loadings, and focus the attention on the effect of the heat source intensity. Most of the previous studies have considered the midplane neutral one, while the actual position of neutral plane for functionally graded plates is shifted and should be firstly determined. A comparative study is performed to illustrate the effect of considering the neutral plane position. The volume fraction of the two constituent materials of the FG plate is varied smoothly and continuously, as a continuous power function of the material position, along the thickness of the plate.

  3. Microstructural Characterization of Thermomechanical and Heat-Affected Zones of an Inertia Friction Welded Astroloy

    Science.gov (United States)

    Oluwasegun, K. M.; Olawale, J. O.; Ige, O. O.; Shittu, M. D.; Adeleke, A. A.; Malomo, B. O.

    2014-08-01

    The behaviour of γ' phase to thermal and mechanical effects during rapid heating of Astroloy, a powder metallurgy nickel-based superalloy has been investigated. The thermo-mechanical-affected zone (TMAZ) and heat-affected zone (HAZ) microstructures of an inertia friction welded (IFW) Astroloy were simulated using a Gleeble thermo-mechanical simulation system. Detailed microstructural examination of the simulated TMAZ and HAZ and those present in actual IFW specimens showed that γ' particles persisted during rapid heating up to a temperature where the formation of liquid is thermodynamically favored and subsequently re-solidified eutectically. The result obtained showed that forging during the thermo-mechanical simulation significantly enhanced resistance to weld liquation cracking of the alloy. This is attributable to strain-induced rapid isothermal dissolution of the constitutional liquation products within 150 μm from the center of the forged sample. This was not observed in purely thermally simulated samples. The microstructure within the TMAZ of the as-welded alloy is similar to the microstructure in the forged Gleeble specimens.

  4. Fuel element thermo-mechanical analysis during transient events using the FMS and FETMA codes

    International Nuclear Information System (INIS)

    Hernandez Lopez Hector; Hernandez Martinez Jose Luis; Ortiz Villafuerte Javier

    2005-01-01

    In the Instituto Nacional de Investigaciones Nucleares of Mexico, the Fuel Management System (FMS) software package has been used for long time to simulate the operation of a BWR nuclear power plant in steady state, as well as in transient events. To evaluate the fuel element thermo-mechanical performance during transient events, an interface between the FMS codes and our own Fuel Element Thermo Mechanical Analysis (FETMA) code is currently being developed and implemented. In this work, the results of the thermo-mechanical behavior of fuel rods in the hot channel during the simulation of transient events of a BWR nuclear power plant are shown. The transient events considered for this work are a load rejection and a feedwater control failure, which among the most important events that can occur in a BWR. The results showed that conditions leading to fuel rod failure at no time appeared for both events. Also, it is shown that a transient due load rejection is more demanding on terms of safety that the failure of a controller of the feedwater. (authors)

  5. Numerical investigation on the thermo-mechanical behavior of a quadratic cross section pile heat exchanger

    DEFF Research Database (Denmark)

    Alberdi Pagola, Maria; Madsen, Søren; Lund Jensen, Rasmus

    2017-01-01

    Pile heat exchangers are traditional foundation piles with built in heat exchangers. As such, the footing of the building both serves as a structural component and a heating/cooling supply element. The existing geotechnical design standards do not consider the nature of thermo-active foundations...... and, therefore, there is a need to develop guidelines to design them properly. This paper contributes by studying the thermo-mechanical behavior of the precast piles which are 15-meter long and have a quadratic cross section and a W-shape pipe heat exchanger. This article aims to numerically assess...... the additional changes in the pile load transfer generated by its heating and cooling. In addressing this objective, a preliminary multi-physical finite element analysis is conducted which serves as a tool for exploring: i) the thermally induced mechanical stresses within the concrete and on the pile-soil axial...

  6. Thermo-mechanical tests on W7-X current lead flanges

    International Nuclear Information System (INIS)

    Dhard, Chandra Prakash; Rummel, Thomas; Zacharias, Daniel; Bykov, Victor; Moennich, Thomas; Buscher, Klaus-Peter

    2013-01-01

    Highlights: • There are significant mechanical loads on the cryostat and radial flanges for W7-X current leads. • These are due to evacuation of W7-X cryostat, cool-down of cold mass, electro-magnetic forces and self weight of leads. • The actual mechanical loads were reduced to simplify the experimental set-up. • The tests were carried out on mock-up flanges test assembly at ambient temperature and at 77 K. • The thermo-mechanical tests on W7-X current lead flanges validate the design and joints of these flanges to the leads. -- Abstract: Fourteen pieces of high temperature superconducting current leads (CL) arranged in seven pairs, will be installed on the outer vessel of Wendelstein 7-X (W7-X) stellarator. In order to support the CL, it is provided with two glass fiber reinforce plastic (GFRP) flanges, namely, the lower cryostat flange (CF) remaining at room temperature and upper radial flange (RF) at about 5 K. Both the flanges i.e. CF and RF experience high mechanical loads with respect to the CL, due to the evacuation of W7-X cryostat, cool-down of cold mass including the CL, electro-magnetic forces due to current and plasma operations and self weight of CL. In order to check the integrity of these flanges for such mechanical loads, thermo-mechanical tests were carried out on these flanges at room temperatures and at liquid nitrogen (LN2) temperatures. The details of test set-up, results and modeling are described in the paper

  7. Thermomechanical behavior and microstructural evolution of a Ni(Pd)-rich Ni{sub 24.3}Ti{sub 49.7}Pd{sub 26} high temperature shape memory alloy

    Energy Technology Data Exchange (ETDEWEB)

    Benafan, O., E-mail: othmane.benafan@nasa.gov [NASA Glenn Research Center, Structures and Materials Division, Cleveland, OH 44135 (United States); Garg, A. [University of Toledo, Toledo, OH 43606 (United States); NASA Glenn Research Center, Structures and Materials Division, Cleveland, OH 44135 (United States); Noebe, R.D.; Bigelow, G.S.; Padula, S.A. [NASA Glenn Research Center, Structures and Materials Division, Cleveland, OH 44135 (United States); Gaydosh, D.J. [Ohio Aerospace Institute, Cleveland, OH 44142 (United States); NASA Glenn Research Center, Structures and Materials Division, Cleveland, OH 44135 (United States); Vaidyanathan, R. [Advanced Materials Processing and Analysis Center, Materials Science and Engineering Department, University of Central Florida, Orlando, FL 32816 (United States); Clausen, B.; Vogel, S.C. [Materials Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM 87545 (United States)

    2015-09-15

    Highlights: • A Ni(Pd)-rich Ni{sub 24.3}Ti{sub 49.7}Pd{sub 26} high temperature shape memory alloy was characterized. • Aging resulted in fine dispersion of nano-sized precipitates. • Thermomechanical cycling resulted in dimensional instabilities due to lattice defects. • A two-way shape memory effect strain of 2% strain was obtained after cycling. - Abstract: The effect of thermomechanical cycling on a slightly Ni(Pd)-rich Ni{sub 24.3}Ti{sub 49.7}Pd{sub 26} (near stochiometric Ni–Ti basis with Pd replacing Ni) high temperature shape memory alloy was investigated. Aged tensile specimens (400 °C/24 h/furnace cooled) were subjected to constant-stress thermal cycling in conjunction with microstructural assessment via in situ neutron diffraction and transmission electron microscopy (TEM), before and after testing. It was shown that in spite of the slightly Ni(Pd)-rich composition and heat treatment used to precipitation harden the alloy, the material exhibited dimensional instabilities with residual strain accumulation reaching 1.5% over 10 thermomechanical cycles. This was attributed to insufficient strengthening of the material (insufficient volume fraction of precipitate phase) to prevent plasticity from occurring concomitant with the martensitic transformation. In situ neutron diffraction revealed the presence of retained martensite while cycling under 300 MPa stress, which was also confirmed by transmission electron microscopy of post-cycled samples. Neutron diffraction analysis of the post-thermally-cycled samples under no-load revealed residual lattice strains in the martensite and austenite phases, remnant texture in the martensite phase, and peak broadening of the austenite phase. Texture developed in the martensite phase was composed mainly of those martensitic tensile variants observed during thermomechanical cycling. Presence of a high density of dislocations, deformation twins, and retained martensite was revealed in the austenite state via in

  8. Well-posedness of a thermo-mechanical model for shape memory alloys under tension

    Czech Academy of Sciences Publication Activity Database

    Krejčí, Pavel; Stefanelli, U.

    2010-01-01

    Roč. 44, č. 6 (2010), s. 1239-1253 ISSN 0764-583X R&D Projects: GA ČR GAP201/10/2315 Institutional research plan: CEZ:AV0Z10190503 Keywords : shape memory alloys * thermo-mechanics * well-posedness * hysteresis operator Subject RIV: BA - General Mathematics Impact factor: 1.202, year: 2010 http://journals.cambridge.org/action/displayAbstract?fromPage=online&aid=8129335

  9. Wood-plastic composites using thermomechanical pulp made from oxalic acid-pretreated red pine chips

    Science.gov (United States)

    J.E. Winandy; N.M. Stark; E. Horn

    2008-01-01

    The characteristics and properties of wood fiber is one of many factors of critical importance to the performance of wood-plastic composites. In commercial thermo-mechanical pulping (TMP) of wood chips to produce fibers, high temperatures (>100°C) are used to separate the fibers during TMP refining. These mechanical pressures and temperatures are usually modulated...

  10. Thermomechanical behavior and modeling of zircaloy cladding tubes from an unirradiated state to high burn-up

    International Nuclear Information System (INIS)

    Schaeffler-Le Pichon, I.; Geyer, P.; Bouffioux, P.

    1997-01-01

    Creep laws are nowadays commonly used to simulate the fuel rod response to the solicitations it faces during its life. These laws are sufficient for describing the base operating conditions (where only creep appears), but they have to be improved for power ramp conditions (where hardening and relaxation appear). The modification due to a neutronic irradiation of the thermomechanical behavior of stress-relieved Zircaloy 4 fuel tubes that have been analysed for five different fluences ranging from a non-irradiated material to a material for which the combustion rate was very high is presented. In the second part, a viscoplastic model able to simulate, for different isotherms, out-of-flux anisotropic mechanical behavior of the cladding tubes irradiated until high burn-up is proposed. Finally, results of numerical simulations show the ability of the model to reproduce the totality of the thermomechanical experiments. (author)

  11. Thermomechanical evaluation of the fuel assemblies fabricated in the ININ; Evaluacion termomecanica de los ensambles combustibles fabricados en el ININ

    Energy Technology Data Exchange (ETDEWEB)

    Hernandez L, H.; Ortiz V, J. [ININ, 52045 Ocoyoacac, Estado de Mexico (Mexico)

    2005-07-01

    The pilot plant of fuel production of the National Institute of Nuclear Research (ININ) provided to the Laguna Verde Nuclear Power Plant (CNLV) four fuel assemblies type GE9B. The fuel irradiation was carried out in the unit 1 of the CNLV during four operation cycles, highlighting the fact that in their third cycle the four assemblies were placed in the center of the reactor core. In the Nuclear Systems Department (DSN) of the ININ it has been carried out studies to evaluate their neutron performance and to be able to determine the exposure levels of this fuels. Its also outlines the necessity to carry out a study of the thermomechanical behavior of the fuel rods that compose the assemblies, through computational codes that simulate their performance so much thermal as mechanical. For such purpose has been developing in the DSN the FETMA code, together with the codes that compose the system Fuel Management System (FMS), which evaluates the thermomechanical performance of fuel elements. In this work were used the FETMA and FEMAXI codes (developed by JAERI) to study the thermomechanical performance of the fuel elements manufactured in the ININ. (Author)

  12. Inorganic fullerene-like IF-WS{sub 2}/PVB nanocomposites of improved thermo-mechanical and tribological properties

    Energy Technology Data Exchange (ETDEWEB)

    Simić, Danica [Military Technical Institute, Ratka Resanovića 1, 11132 Belgrade (Serbia); Stojanović, Dušica B., E-mail: duca@tmf.bg.ac.rs [University of Belgrade, Faculty of Technology and Metallurgy, 11120 Belgrade (Serbia); Kojović, Aleksandar [University of Belgrade, Faculty of Technology and Metallurgy, 11120 Belgrade (Serbia); Dimić, Mirjana; Totovski, Ljubica [Military Technical Institute, Ratka Resanovića 1, 11132 Belgrade (Serbia); Uskoković, Petar S.; Aleksić, Radoslav [University of Belgrade, Faculty of Technology and Metallurgy, 11120 Belgrade (Serbia)

    2016-12-01

    The subject of this research is to explore the possibility of preparation of nanocomposite material of improved thermo-mechanical and tribological properties, using inorganic fullerene-like tungsten disulfide nanostructures (IF-WS{sub 2}) as reinforcement in poly(vinyl butyral) (PVB). This paper also reports investigation of the effects of using different solvents in preparation of PVB/IF-WS{sub 2} nanocomposite on the thermo-mechanical behavior of the resulting material. PVB was dissolved in ethanol, isopropanol, n-butanol and ethyl acetate. IF-WS{sub 2} nanoparticles were added to these PVB solutions and dispersed by different deagglomeration techniques. Samples were dried and thin films were obtained. Their microstructure and the quality of IF-WS{sub 2} dispersion and deagglomeration in PVB matrix was analyzed by scanning electron microscope (SEM). The reinforcing effect of IF-WS{sub 2} is examined by determining hardness, reduced modulus of elasticity and coefficient of friction, by nanoindentation and nanoscratch test, in terms of the different solvents applied in preparation of the samples, mode of stirring and different contents of IF-WS{sub 2}. The glass transition temperature (T{sub g}) was determined for the prepared samples using differential scanning calorimetry (DSC) and dynamic mechanical thermal analysis (DMA). Storage modulus and mechanical loss factor were observed in a defined temperature range using DMA. - Highlights: • Poly(vinyl butyral)/tungsten disulfide nanocomposites were examined. • Different solvents and deagglomeration methods affect the properties of composites. • Nanoindentation and scratch test, PSD, SEM, DSC and DMTA were analyzed. • Thermo-mechanical and antifriction properties of composite material are improved.

  13. Instrumentation requirements for the ESF thermomechanical experiments

    International Nuclear Information System (INIS)

    Pott, J.; Brechtel, C.E.

    1992-01-01

    In situ thermomechanical experiments are planned as part of the Yucca Mountain Site Characterization Project that require instruments to measure stress and displacement at temperatures that exceed the typical specifications of existing geotechnical instruments. A high degree of instrument reliability will also be required to satisfy the objectives of the experiments, therefore a study was undertaken to identify areas where improvement in instrument performance was required. A preliminary list of instruments required for the experiments was developed, based on existing test planning and analysis. Projected temperature requirements were compared to specifications of existing instruments to identify instrumentation development needs. Different instrument technologies, not currently employed in geotechnical instrumentation, were reviewed to identify potential improvements of existing designs for the high temperature environment. Technologies with strong potentials to improve instrument performance with relatively high reliability include graphite fiber composite materials, fiber optics, and video imagery

  14. Investigation of thermomechanical effects of lighting conditions on canvas paintings by laser shearography

    Science.gov (United States)

    Meybodi, M. K.; Dobrev, I.; Klausmeyer, P.; Harrington, E. J.; Furlong, C.

    Quantitative techniques to characterize thermomechanical effects of light on canvas paintings are necessary in order to better understand the deleterious effects that light has on precious art collections in museum exhibitions. In this paper, we present advances in the development of a customized laser shearography system for temporal characterization of inplane displacements of canvas paintings when subjected to specific lighting conditions. The shearography system is synchronized with a thermal IR camera and concomitant measurements of derivatives of displacements along two orthogonal shearing directions as well as thermal fields are performed. Due to the nature of the measurements, we have developed real-time temporal phase unwrapping algorithms and high-resolution Fast Fourier Transform (FFT) methods to calibrate applied shearing levels. In addition, we are developing methods to isolate thermally-induced components from randomly-induced mechanical vibrations that occur in museum environments by application of IR imaging data. Representative examples are shown, which illustrate capabilities to measure, detect, and map crack propagation as a function of lighting conditions and time.

  15. Atomistic simulation of solid solution hardening in Mg/Al alloys: Examination of composition scaling and thermo-mechanical relationships

    International Nuclear Information System (INIS)

    Yi, Peng; Cammarata, Robert C.; Falk, Michael L.

    2016-01-01

    Dislocation mobility in a solid solution was studied using atomistic simulations of an Mg/Al system. The critical resolved shear stress (CRSS) for the dislocations on the basal plane was calculated at temperatures from 0 K to 500 K with solute concentrations from 0 to 7 at%, and with four different strain rates. Solute hardening of the CRSS is decomposed into two contributions: one scales with c 2/3 , where c is the solute concentration, and the other scales with c 1 . The former was consistent with the Labusch model for local solute obstacles, and the latter was related to the athermal plateau stress due to the long range solute effect. A thermo-mechanical model was then used to analyze the temperature and strain rate dependences of the CRSS, and it yielded self-consistent and realistic results. The scaling laws were confirmed and the thermo-mechanical model was successfully parameterized using experimental measurements of the CRSS for Mg/Al alloys under quasi-static conditions. The predicted strain rate sensitivity from the experimental measurements of the CRSS is in reasonable agreement with separate mechanical tests. The concentration scaling and the thermo-mechanical relationships provide a potential tool to analytically relate the structural and thermodynamic parameters on the microscopic level with the macroscopic mechanical properties arising from dislocation mediated deformation.

  16. Application of a unified fatigue modelling to some thermomechanical fatigue problems

    International Nuclear Information System (INIS)

    Dang, K. van; Maitournam, H.; Moumni, Z.

    2005-01-01

    Fatigue under thermomechanical loadings is an important topic for nuclear industries. For instance, thermal fatigue cracking is observed in the mixing zones of the nuclear reactor. Classical computations using existing methods based on strain amplitude or fracture mechanics are not sufficiently predictive. In this paper an alternative approach is proposed based on a multiscale modelling thanks to shakedown hypothesis. Examples of predictive results are presented. Finally an application to the RHR problem is discussed. Main ideas of the fatigue modelling: Following an idea of Professor D. Drucker who wrote in 1963 'when applied to the microstructure there is a hope that the concept of endurance limit and shakedown are related, and that fatigue failure can be related to energy dissipated in idealized material when shakedown does not occur.' we have developed a theory of fatigue based on this concept which is different from classical fatigue approaches. Many predictive applications have been already done particularly for the automotive industry. Fatigue resistance of structures undergoing thermomechanical loadings in the high cycle regime as well as in the low cycle regime are calculated using this modelling. However, this fatigue theory is until now rarely used in nuclear engineering. After recalling the main points of the theory, we shall present some relevant applications which were done in different industrial sectors. We shall apply this modelling to the prediction of thermal cracking observed in the mixing zones of RHR. (authors)

  17. Best estimate modeling of fuel thermomechanical behaviour in WWER 1000 LB LOCA

    International Nuclear Information System (INIS)

    Valach, M.; Klouzal, J.; Zymak, J.; Dostal, M.

    2009-01-01

    The paper summarizes our calculations of the performance of the WWER 1000 NPP fuel rods during postulated LB LOCA. The thermomechanical modeling was performed by FRAPTRAN using the FRACAS-I mechanical model using the boundary conditions calculated by the ATHLET code. The results and their statistical evaluation are presented, the process of the generalization of gained insight into the best-estimate thermal-hydraulic analyses (BE TM) predictions in order to define a generic BE TM methodology is outlined (authors)

  18. Thermomechanical scoping calculations for the waste package environment tests

    International Nuclear Information System (INIS)

    Butkovich, T.R.; Yow, J.L. Jr.

    1986-03-01

    During the site characterization phase of the Nevada Nuclear Waste Storage Investigation Project, tests are planned to provide field information on the hydrological and thermomechanical environment. These results are needed for assessing performance of stored waste packages emplaced at depth in excavations in a rock mass. Scoping calculations were performed to provide information on displacements and stress levels attained around excavations in the rock mass from imposing a thermal load designed to simulate the heat produced by radioactive decay. In this way, approximate levels of stresses and displacements are available for choosing instrumentation type and sensitivity as well as providing indications for optimizing instrument emplacement during the test. 7 refs., 9 figs., 1 tab

  19. A thermomechanical crystal plasticity constitutive model for ultrasonic consolidation

    KAUST Repository

    Siddiq, Amir

    2012-01-01

    We present a micromechanics-based thermomechanical constitutive model to simulate the ultrasonic consolidation process. Model parameters are calibrated using an inverse modeling approach. A comparison of the simulated response and experimental results for uniaxial tests validate and verify the appropriateness of the proposed model. Moreover, simulation results of polycrystalline aluminum using the identified crystal plasticity based material parameters are compared qualitatively with the electron back scattering diffraction (EBSD) results reported in the literature. The validated constitutive model is then used to simulate the ultrasonic consolidation process at sub-micron scale where an effort is exerted to quantify the underlying micromechanisms involved during the ultrasonic consolidation process. © 2011 Elsevier B.V. All rights reserved.

  20. On the thermomechanical deformation of silver shape memory nanowires

    International Nuclear Information System (INIS)

    Park, Harold S.; Ji, Changjiang

    2006-01-01

    We present an analysis of the uniaxial thermomechanical deformation of single-crystal silver shape memory nanowires using atomistic simulations. We first demonstrate that silver nanowires can show both shape memory and pseudoelastic behavior, then perform uniaxial tensile loading of the shape memory nanowires at various deformation temperatures, strain rates and heat transfer conditions. The simulations show that the resulting mechanical response of the shape memory nanowires depends strongly upon the temperature during deformation, and can be fundamentally different from that observed in bulk polycrystalline shape memory alloys. The energy and temperature signatures of uniaxially loaded silver shape memory nanowires are correlated to the observed nanowire deformation, and are further discussed in comparison to bulk polycrystalline shape memory alloy behavior

  1. Thermo-mechanical modeling of the obduction process based on the Oman ophiolite case

    OpenAIRE

    Duretz , Thibault; Agard , Philippe; Yamato , Philippe; Ducassou , Céline; Burov , Evgenii ,; Gerya , T. V.

    2016-01-01

    International audience; Obduction emplaces regional-scale fragments of oceanic lithosphere (ophiolites) over continental lithosphere margins of much lower density. For this reason, the mechanisms responsible for obduction remain enigmatic in the framework of plate tectonics. We present two-dimensional (2D) thermo-mechanical models of obduction and investigate possible dynamics and physical controls of this process. Model geometry and boundary conditions are based on available geological and g...

  2. A multiscale finite element method for modeling fully coupled thermomechanical problems in solids

    KAUST Repository

    Sengupta, Arkaprabha; Papadopoulos, Panayiotis; Taylor, Robert L.

    2012-01-01

    This article proposes a two-scale formulation of fully coupled continuum thermomechanics using the finite element method at both scales. A monolithic approach is adopted in the solution of the momentum and energy equations. An efficient implementation of the resulting algorithm is derived that is suitable for multicore processing. The proposed method is applied with success to a strongly coupled problem involving shape-memory alloys. © 2012 John Wiley & Sons, Ltd.

  3. A multiscale finite element method for modeling fully coupled thermomechanical problems in solids

    KAUST Repository

    Sengupta, Arkaprabha

    2012-05-18

    This article proposes a two-scale formulation of fully coupled continuum thermomechanics using the finite element method at both scales. A monolithic approach is adopted in the solution of the momentum and energy equations. An efficient implementation of the resulting algorithm is derived that is suitable for multicore processing. The proposed method is applied with success to a strongly coupled problem involving shape-memory alloys. © 2012 John Wiley & Sons, Ltd.

  4. On phase transformation models for thermo-mechanically coupled response of Nitinol

    KAUST Repository

    Sengupta, Arkaprabha

    2011-03-31

    Fully coupled thermomechanical models for Nitinol at the grain level are developed in this work to capture the inter-dependence between deformation and temperature under non-isothermal conditions. The martensite transformation equations are solved using a novel algorithm which imposes all relevant constraints on the volume fractions. The numerical implementation of the resulting models within the finite element method is effected by the monolithic solution of the momentum and energy equations. Validation of the models is achieved by means of thin-tube experiments at different strain rates. © 2011 Springer-Verlag.

  5. Methacrylate based cross-linkers for improved thermomechanical properties and retention of radiation detection response in plastic scintillators

    Science.gov (United States)

    Mahl, Adam; Lim, Allison; Latta, Joseph; Yemam, Henok A.; Greife, Uwe; Sellinger, Alan

    2018-03-01

    Pulse shape discrimination (PSD) is an important method that can efficiently sort and separate neutron and gamma radiation signals. PSD is currently achieved in plastic scintillators by over-doping poly(vinyl toluene) (PVT) matrices with fluorescent molecules. Meaningful separation of the signals requires addition of >20 wt% 2,5-diphenyloxazole (PPO) fluor in PVT. At these concentrations PPO acts as a plasticizer, negatively affecting the physical properties of the final plastic such as hardness, machinability, and thermomechanical stability. This work addresses these issues by implementing a cost-effective solution using cross-linking chemistry via commercially available bisphenol A dimethacrylate (BPA-DM), and a synthesized fluorinated analogue. Both improve the physical properties of over-doped PPO based plastic scintillators without degrading the measured light yield or PSD and Figure of Merit (FoM). In addition, the fluorinated analogue appears to enhance the hydrophobicity of the surface of the plastic scintillators, which may improve the scintillators' resistance to water diffusion and subsequent radiation response degradation. The new formulations improve the feasibility of widely deploying long lifetime PSD capable plastic scintillators in large area coverage assemblies.

  6. Analysis of the finite deformation response of shape memory polymers: I. Thermomechanical characterization

    International Nuclear Information System (INIS)

    Volk, Brent L; Lagoudas, Dimitris C; Chen, Yi-Chao; Whitley, Karen S

    2010-01-01

    This study presents the analysis of the finite deformation response of a shape memory polymer (SMP). This two-part paper addresses the thermomechanical characterization of SMPs, the derivation of material parameters for a finite deformation phenomenological model, the numerical implementation of such a model, and the predictions from the model with comparisons to experimental data. Part I of this work presents the thermomechanical characterization of the material behavior of a shape memory polymer. In this experimental investigation, the vision image correlation system, a visual–photographic apparatus, was used to measure displacements in the gauge area. A series of tensile tests, which included nominal values of the extension of 10%, 25%, 50%, and 100%, were performed on SMP specimens. The effects on the free recovery behavior of increasing the value of the applied deformation and temperature rate were considered. The stress–extension relationship was observed to be nonlinear for increasing values of the extension, and the shape recovery was observed to occur at higher temperatures upon increasing the temperature rate. The experimental results, aided by the advanced experimental apparatus, present components of the material behavior which are critical for the development and calibration of models to describe the response of SMPs

  7. Lithosphere tectonics and thermo-mechanical properties: An integrated modeling approach for enhanced geothermal systems exploration in Europe

    NARCIS (Netherlands)

    Wees, J.D. van; Cloetingh, S.; Ziegler, P.A.; Lenkey, L.; Beekman, F.; Tesauro, M.; Förster, A.; Norden, B.; Kaban, M.; Hardebol, N.; Voorde, M.T.; Willingshofer, E.; Cornu, T.; Bonté, D.

    2009-01-01

    For geothermal exploration and the development of enhanced geothermal systems (EGS) knowlegde of temperature at drillable depth is a prerequisite for site selection. Equally important is the thermo-mechanical signature of the lithosphere and crust which allow to obtain critical constraints for the

  8. On capabilities of thermomechanical treatment in increasing durability of short service life elements of mining аnd processing equipment

    Directory of Open Access Journals (Sweden)

    В. И. Болобов

    2016-11-01

    Full Text Available Hadfield steel (110G13L is the basic material for fast wornout items of mining equipment: beaters, hammers, liners, refractory plates of crushers and mills. By way of example, the effect of cold hardening was specifically analyzed on the rate of wear of mining equipment parts for various types of wear by hard (more than 1100 HV and soft rock. A unique ability of that steel to resist shock wear is noted. It is shown that this steel exhibits low resistance to abrasive rock wear. Meanwhile wear by rock of hardness lower than steel (less than 1100 HV, may be substantially increased by pre-hardening of samples (up to 10-fold. In case of wear by high hardness rocks, shock impact that should contribute to hardening of the material, fails  to increase abrasive wear resistance of Hadfield steel, and in that parameter it does not differ from the conventional medium carbon steel 45. Also, the authors of this article describe a technique they developed of high-temperature thermomechanical treatment of specimen of Hadfield steel (free forging at 1150-950ºC and subsequent quenching in water and experiments in their abrasion. The results of tests show that hardness and wear resistance of Hadfield steel to hard abrasive (corundum 25A with aggregate hardness of ~2500 HV increases with plastic deformation at HTMT. For maximum plastic deformation intensity (deformation magnitude of α = 2.25, reached in the experiments by the authors, wear resistance grew by 70% as compared to undeformed steel. The dependence is presented of wear resistance of steel on hardness, HV, achieved in the result of plastic deformation. Since a similar positive effect was obtained earlier by the authors for 35HGSA steel, also used in mining machinery, they conclude that the HTMT technique may be recommended for treating short lived parts of the mining and mineral processing equipment to increase their service life.

  9. Fluka and thermo-mechanical studies for the CLIC main dump

    CERN Document Server

    Mereghetti, Alessio; Vlachoudis, Vasilis

    2011-01-01

    In order to best cope with the challenge of absorbing the multi-MW beam, a water beam dump at the end of the CLIC post-collision line has been proposed. The design of the dump for the Conceptual Design Report (CDR) was checked against with a set of FLUKA Monte Carlo simulations, for the estimation of the peak and total power absorbed by the water and the vessel. Fluence spectra of escaping particles and activation rates of radio-nuclides were computed as well. Finally, the thermal transient behavior of the water bath and a thermo-mechanical analysis of the preliminary design of the window were done.

  10. Split double factorial with additional treatment and the post-harvest of Niagara grapes

    Directory of Open Access Journals (Sweden)

    Pórtya Piscitelli Cavalcanti

    2015-09-01

    Full Text Available ABSTRACTThis study aims to discuss and explain how to deal with the analysis of experiments conducted in completely randomized design (CRD and subdivided into double factorial with additional treatment in the plot. In addition it was illustrate the discussion by analyzing data from an experiment on post-harvest of Niagara grapes. The sums of squares for each source of variation are presented, while discussing how the additional treatment affects the whole variation. Niagara grapes were treated in the pre-harvest with three preservatives (calcium chloride, calcium nitrate and calcium lactate at 0%, 0.5%, 1% and 2% and stored for 0, 10, 20 and 30 days.All the preservatives evaluated at 0% represented the control (additional treatment.

  11. Thermo-mechanical constitutive modeling of unsaturated clays based on the critical state concepts

    OpenAIRE

    Tourchi, Saeed; Hamidi, Amir

    2015-01-01

    A thermo-mechanical constitutive model for unsaturated clays is constructed based on the existing model for saturated clays originally proposed by the authors. The saturated clays model was formulated in the framework of critical state soil mechanics and modified Cam-clay model. The existing model has been generalized to simulate the experimentally observed behavior of unsaturated clays by introducing Bishop's stress and suction as independent stress parameters and modifying the hardening rul...

  12. Thermomechanical modeling of the Spent Fuel Test-Climax

    Energy Technology Data Exchange (ETDEWEB)

    Butkovich, T.R.; Patrick, W.C.

    1986-02-01

    The Spent Fuel Test-Climax (SFT-C) was conducted to evaluate the feasibility of retrievable deep geologic storage of commercially generated spent nuclear-reactor fuel assemblies. One of the primary aspects of the test was to measure the thermomechanical response of the rock mass to the extensive heating of a large volume of rock. Instrumentation was emplaced to measure stress changes, relative motion of the rock mass, and tunnel closures during three years of heating from thermally decaying heat sources, followed by a six-month cooldown period. The calculations reported here were performed using the best available input parameters, thermal and mechanical properties, and power levels which were directly measured or inferred from measurements made during the test. This report documents the results of these calculations and compares the results with selected measurements made during heating and cooling of the SFT-C.

  13. Thermomechanical modeling of the Spent Fuel Test-Climax

    International Nuclear Information System (INIS)

    Butkovich, T.R.; Patrick, W.C.

    1986-02-01

    The Spent Fuel Test-Climax (SFT-C) was conducted to evaluate the feasibility of retrievable deep geologic storage of commercially generated spent nuclear-reactor fuel assemblies. One of the primary aspects of the test was to measure the thermomechanical response of the rock mass to the extensive heating of a large volume of rock. Instrumentation was emplaced to measure stress changes, relative motion of the rock mass, and tunnel closures during three years of heating from thermally decaying heat sources, followed by a six-month cooldown period. The calculations reported here were performed using the best available input parameters, thermal and mechanical properties, and power levels which were directly measured or inferred from measurements made during the test. This report documents the results of these calculations and compares the results with selected measurements made during heating and cooling of the SFT-C

  14. Thermomechanical properties of polymer nanocomposites: Exploring a unified relationship with planar polymer films

    Science.gov (United States)

    Bansal, Amitabh

    The thermal and mechanical response of polymers, which provide limitations to their practical use, are greatly improved by the addition of a small fraction of an inorganic nanofiller. However, the resulting changes in polymer properties are poorly understood, primarily due to the non-uniform spatial distribution of nanoparticles. This research explores the properties of polystyrene filed with silica nanoparticles and illustrates for the first time that the thermodynamic properties of "polymer nanocomposites" are quantitatively equivalent to the well-understood case of planar polymer films with a uniform thickness. These ideas are quantified by drawing a direct analogy between thin film thickness and an appropriate average ligament thickness measured using electron microscopy. The change in polymer glass transition temperatures with decreasing ligament thickness were found to be quantitatively equivalent to the corresponding thin film data. In combination with viscoelastic properties of the nanocomposites that are in quantitative agreement with data from thin films, these conclusions provide a facile means of understanding and predicting the thermomechanical properties and, potentially, the engineering properties of practically relevant polymer nanocomposites. Grafting of high molecular weight polystyrene onto the silica nanoparticles greatly improves the dispersion quality of nanofillers and also provides a means to tailor the thermo-mechanical properties in nanocomposites. It is concluded that the grafted polystyrene is akin to polymer brushes on flat surfaces. The mobility and stiffness of these grafted chains are expected to be low as compared to the free polymer. In this context a mechanism for the increase in glass transition is proposed: (1) the stiff grafted chains will tend to decrease mobility and thus increase glass transition, (2) the extent of interdigitation of the grafted polystyrene into the matrix will determine the extent to which the nanocomposite

  15. Thermomechanical Modelling of Direct-Drive Friction Welding Applying a Thermal Pseudo Mechanical Model for the Generation of Heat

    DEFF Research Database (Denmark)

    Sonne, Mads Rostgaard; Hattel, Jesper Henri

    2018-01-01

    In the present work a 2D a xisymmetric thermomechanical model of the direct-drive friction welding process is developed, taking the temperature dependent shear yield stress into account in the description of the heat generation, utilizing a recent thermal pseudo mechanical model originally...... developed for the friction stir welding (FSW) process. The model is implemented in ABAQUS/Explicit via a subroutine. The application in this case is joining of austenitic stainless steel rods with an outer diameter of 112 mm, used for manufacturing of exhaust gas valves for large two stroke marine engines....... The material properties in terms of the temperature dependent flowstress curves used both in the thermal and the mechanical constitutive description are extracted from compression tests performed between 20 °C and 1200 °C on a Gleeble 1500 thermomechanical simulator. Comparison between measured and simulated...

  16. Thermo-mechanical modelling of salt caverns due to fluctuating loading conditions.

    Science.gov (United States)

    Böttcher, N.

    2015-12-01

    This work summarizes the development and application of a numerical model for the thermo-mechanical behaviour of salt caverns during cyclic gas storage. Artificial salt caverns are used for short term energy storage, such as power-to-gas or compressed air energy storage. Those applications are characterized by highly fluctuating operation pressures due to the unsteady power levels of power plants based on renewable energy. Compression and expansion of the storage gases during loading and unloading stages lead to rapidly changing temperatures in the host rock of the caverns. This affects the material behaviour of the host rock within a zone that extends several meters into the rock mass adjacent to the cavern wall, and induces thermo-mechanical stresses and alters the creep response.The proposed model features the thermodynamic behaviour of the storage medium, conductive heat transport in the host rock, as well as temperature dependent material properties of rock salt using different thermo-viscoplastic material models. The utilized constitutive models are well known and state-of-the-art in various salt mechanics applications. The model has been implemented into the open-source software platform OpenGeoSys. Thermal and mechanical processes are solved using a finite element approach, coupled via a staggered coupling scheme. The simulation results allow the conclusion, that the cavern convergence rate (and thus the efficiency of the cavern) is highly influenced by the loading cycle frequency and the resulting gas temperatures. The model therefore allows to analyse the influence of operation modes on the cavern host rock or on neighbouring facilities.

  17. High temperature fatigue behaviour of TZM molybdenum alloy under mechanical and thermomechanical cyclic loads

    International Nuclear Information System (INIS)

    Shi, H.J.; Niu, L.S.; Korn, C.; Pluvinage, G.

    2000-01-01

    High temperature isothermal mechanical fatigue and in-phase thermomechanical fatigue (TMF) tests in load control were carried out on a molybdenum-based alloy, one of the best known of the refractory alloys, TZM. The stress-strain response and the cyclic life of the material were measured during the tests. The fatigue lives obtained in the in-phase TMF tests are lower than those obtained in the isothermal mechanical tests at the same load amplitude. It appears that an additional damage is produced by the reaction of mechanical stress cycles and temperature cycles in TMF situation. Ratcheting phenomenon occurred during the tests with an increasing creep rate and it was dependent on temperature and load amplitude. A model of lifetime prediction, based on the Woehler-Miner law, was discussed. Damage coefficients that are functions of the maximum temperature and the variation of temperature are introduced in the model so as to evaluate TMF lives in load control. With this method the lifetime prediction gives results corresponding well to experimental data

  18. Thermo-mechanical design of the Plasma Driver Plate for the MITICA ion source

    Energy Technology Data Exchange (ETDEWEB)

    Pavei, Mauro, E-mail: mauro.pavei@igi.cnr.it [Consorzio RFX, EURATOM-ENEA Association, Corso Stati Uniti 4, I-35127 Padova (Italy); Palma, Mauro Dalla; Marcuzzi, Diego [Consorzio RFX, EURATOM-ENEA Association, Corso Stati Uniti 4, I-35127 Padova (Italy)

    2010-12-15

    In the framework of the activities for the development of the Neutral Beam Injector (NBI) for ITER, the detailed design of the Radio-Frequency (RF) negative ion source has been carried out. One of the most heated components of the RF source is the rear vertical plate, named Plasma Driver Plate (PDP), where the Back-Streaming positive Ions (BSI+) generated from stripping losses in the accelerator and back scattered on the plasma source impinge on. The heat loads that result are huge and concentrated, with first estimate of the power densities up to 60 MW/m{sup 2}. The breakdowns that occur into the accelerator cause such heat loads to act cyclically, so that the PDP is thermo-mechanically fatigue loaded. Moreover, the surface of the PDP facing the plasma is functionally required to be temperature controlled and to be molybdenum or tungsten coated. The thermo-hydraulic design of the plate has been carried out considering active cooling with ultra-pure water. Different heat sink materials, hydraulic circuit layout and manufacturing processes have been considered. The heat exhaust has been optimized by changing the channels geometry, the path of the heat flux in the heat sink, the thickness of the plate and maximizing the Heat Transfer Coefficient. Such optimization has been carried out by utilizing 3D Finite Element (FE) models. Afterwards all the suitable mechanical (aging, structural monotonic and cyclic) verifications have been carried out post-processing the results of the thermo-mechanical 3D FE analyses in accordance to specific procedures for nuclear components exposed to high temperature. The effect of sputtering phenomenon due to the high energy BSI+ impinging on the plate has been considered and combined with fatigue damage for the mechanical verification of the PDP. Alternative solutions having molybdenum (or tungsten coatings) facing the plasma, aiming to reduce the sputtering rate and the consequent plasma pollution, have been evaluated and related 3D FE

  19. Effect of Different Thermomechanical Processes on the Microstructure, Texture, and Mechanical Properties of API 5L X70 Steel

    Science.gov (United States)

    Masoumi, Mohammad; Echeverri, Edwan Anderson Ariza; Silva, Cleiton Carvalho; Béreš, Miloslav; de Abreu, Hamilton Ferreira Gomes

    2018-03-01

    A commercial API 5L X70 steel plate was subjected to different thermomechanical processes to propose a novel thermomechanical rolling path to achieve improved mechanical properties. Scanning electron microscopy, electron backscatter diffraction, and x-ray texture analysis were employed for microstructural characterization. The results showed that strain-free recrystallized {001} ferrite grains that developed at higher rolling temperature could not meet the American Petroleum Institute (API) requirements. Also, refined and work-hardened grains that have formed in the intercritical region with high stored energy do not provide suitable tensile properties. However, fine martensite-austenite constituents dispersed in ferrite matrix with grains having predominantly {111} and {110} orientations parallel to the normal direction that developed under isothermal rolling at 850 °C provided an outstanding combination of tensile strength and ductility.

  20. Influence of dwell times on the thermomechanical fatigue behavior of a directionally solidified Ni-base superalloy

    Czech Academy of Sciences Publication Activity Database

    Guth, S.; Petráš, Roman; Škorík, Viktor; Kruml, Tomáš; Man, Jiří; Lang, K. H.; Polák, Jaroslav

    2015-01-01

    Roč. 80, NOV (2015), s. 426-433 ISSN 0142-1123 R&D Projects: GA MŠk(CZ) EE2.3.30.0063 Institutional support: RVO:68081723 Keywords : Nickel base superalloy * Thermomechanical fatigue * Dwell time * Lifetime behavior * Damage mechanisms Subject RIV: JL - Materials Fatigue, Friction Mechanics Impact factor: 2.162, year: 2015

  1. Thermomechanical analysis of nuclear fuel elements

    International Nuclear Information System (INIS)

    Hernandez L, H.

    1997-01-01

    This work presents development of a code to obtain the thermomechanical analysis of fuel rods in the fuel assemblies inserted in the core of BWR reactors. The code uses experimental correlations developed in several laboratories. The development of the code is divided in two parts: a) the thermal part and b) the mechanical part, extending both the fuel and the cladding materials. The thermal part consists of finding the radial distribution of temperatures in the pellet, from the fuel centerline up to the coolant, along the total active length, considering one and two phase flow in the coolant, as a result of the pressure drop in the system. The mechanical part analyzes the effects of temperature gradients, pressure and irradiation, to which the fuel rod is subjected. The strains produced by swelling, creep and thermal stress in the fuel material are analyzed. In the same way the strains in the cladding are analyzed, considering the effects produced by the pressure exerted on the cladding by pellet swelling, by the pressure caused by fission gas release toward the cavities, and by the strain produced on the cladding by the pressure changes of the system. (Author)

  2. Water-cooled lithium-lead box-shaped blanket concept for Demo: thermo-mechanical optimization and manufacturing sequence proposal

    International Nuclear Information System (INIS)

    Baraer, L.; Dinot, N.; Giancarli, L.; Proust, E.; Salavy, J.F.; Severi, Y.; Quintric-Bossy, J.

    1992-01-01

    The development of the water-cooled lithium-lead box-shaped blanket concept for DEMO has now reached the stage of thermo-mechanical optimization. In the previous design phases the preliminary dimensioning of the cooling circuit has permitted to define the water proportions required in the breeder region and to demonstrate, after a minimization of steel proportion and thicknesses, that this concept could reach tritium breeding self-sufficiency. In the present analysis the location of the coolant pipes has been optimized for the whole equatorial plane cross-section of both inboard and outboard segments in order to maintain the maximum Pb-17Li/steel interface temperature below 480 deg C and to minimize the thermal gradients along the steel structures. The consequent thermo-mechanical analysis has shown that the thermal stresses always remain below the allowable limits. Segment fabricability and removal are the next design issues to be analyzed. Within this strategy, a first manufactury sequence for the outboard segment is proposed

  3. Existence and non-existence for the full thermomechanical Souza–Auricchio model of shape memory wires

    Czech Academy of Sciences Publication Activity Database

    Krejčí, Pavel; Stefanelli, U.

    2011-01-01

    Roč. 16, č. 4 (2011), s. 349-365 ISSN 1081-2865 R&D Projects: GA ČR GAP201/10/2315 Institutional research plan: CEZ:AV0Z10190503 Keywords : shape memory alloys * thermomechanics * existence result * blowup in finite time Subject RIV: BA - General Mathematics Impact factor: 1.012, year: 2011 http://mms.sagepub.com/content/early/2011/03/11/1081286510386935.abstract

  4. Existence and non-existence for the full thermomechanical Souza–Auricchio model of shape memory wires

    Czech Academy of Sciences Publication Activity Database

    Krejčí, Pavel; Stefanelli, U.

    2011-01-01

    Roč. 16, č. 4 (2011), s. 349-365 ISSN 1081-2865 R&D Projects: GA ČR GAP201/10/2315 Institutional research plan: CEZ:AV0Z10190503 Keywords : shape memory alloys * thermomechanics * existence result * blowup in finite time Subject RIV: BA - General Mathematics Impact factor: 1.012, year: 2011 http:// mms .sagepub.com/content/early/2011/03/11/1081286510386935.abstract

  5. Additive Manufacturing of NiTiHf High Temperature Shape Memory Alloy

    Science.gov (United States)

    Benafan, Othmane; Bigelow, Glen S.; Elahinia, Mohammad; Moghaddam, Narges Shayesteh; Amerinatanzi, Amirhesam; Saedi, Soheil; Toker, Guher Pelin; Karaca, Haluk

    2017-01-01

    Additive manufacturing of a NiTi-20Hf high temperature shape memory alloy (HTSMA) was investigated. A selective laser melting (SLM) process by Phenix3D Systems was used to develop components from NiTiHf powder (of approximately 25-75 m particle fractions), and the thermomechanical response was compared to the conventionally vacuum induction skull melted counterpart. Transformation temperatures of the SLM material were found to be slightly lower due to the additional oxygen pick up from the gas atomization and melting process. The shape memory response in compression was measured for stresses up to 500 MPa, and transformation strains were found to be very comparable (Up to 1.26 for the as-extruded; up to 1.52 for SLM).

  6. Mechanical and thermo-mechanical analyses of the tapered plug for plugging of deposition tunnels. A feasibility study

    Energy Technology Data Exchange (ETDEWEB)

    Faelth, Billy (Clay Technology AB, Lund (Sweden)); Gatter, Patrik (Vattenfall Power Consultant AB, Stockholm (Sweden))

    2009-09-15

    This report presents results from a study that was carried out in order to examine the applicability of the tapered plug concept for plugging of deposition tunnels in the deep repository for spent nuclear fuel. The report presents results from mechanical and thermo-mechanical models of the tapered plug. The models were analyzed with 3DEC. The models included a portion of a deposition tunnel and its intersection with a main tunnel. In the deposition tunnel, a tapered concrete plug was installed. The plug was subjected to the combined load from the swelling backfill material and from pore pressure inside the deposition tunnel. The thermo-mechanical effects due to the heat generation in the spent fuel were also included in the analyses. Generic material parameter values for the concrete were used. The following items were studied: - Stresses and displacements in the plug. - Shear stresses and shear displacements in the rock-concrete interface. - Stress additions in the rock due to the loads. The sensitivity of the results to changes of constitutive models, to changes of the plug geometry and to pore water pressure in the rock-concrete interface was examined. The results indicate that the displacements in the plug will be within reasonable ranges but the stresses may locally be high enough that they exceed acceptable levels. However, they can be reduced by choice of advantageous plug geometry and by having a good rock-concrete bond. The results also show that the stress additions in the rock due to the thermal load may yield stresses that locally exceed the spalling strength of the rock. At most locations, however, the rock stresses will amount at lower levels. It was concluded that, with choice of an appropriate design, the tapered plug seems to be an applicable concept for plugging of deposition tunnels. It was also concluded that further studies of the tapered plug concept should use material properties parameter values for low-pH concrete. Further, they should also

  7. CIEMAT’s contribution to the phase II of the OECD-NEA RIA benchmark on thermo-mechanical fuel codes performance

    Energy Technology Data Exchange (ETDEWEB)

    Sagrado, I.C.; Vallejo, I.; Herranz, L.E.

    2015-07-01

    As a part of the international efforts devoted to validate and/or update the current fuel safety criteria, the OECD-NEA has launched a second phase of the RIA benchmark on thermomechanical fuel codes performance. CIEMAT contributes simulating the ten scenarios proposed with FRAPTRAN and SCANAIR. Both codes lead to similar predictions during the heating-up; however, during the cooling-down significant deviations may appear. They are mainly caused by the estimations of gap closure and re-opening and the clad to water heat exchange approaches. The uncertainty analysis performed for the SCANAIR estimations leads to uncertainty ranges below 15% and 28% for maximum temperatures and deformations, respectively. The corresponding sensitivity analysis shows that, in addition to the injected energy, special attention should be paid to fuel thermal expansion and clad yield stress models. (Author)

  8. Effects of silicon and thermo-mechanical process on microstructure and properties of Cu–10Ni–3Al–0.8Si alloy

    International Nuclear Information System (INIS)

    Shen, Leinuo; Li, Zhou; Zhang, Zheming; Dong, Qiyi; Xiao, Zhu; Lei, Qian; Qiu, Wenting

    2014-01-01

    Highlights: • Cu–10Ni–3Al–0.8Si alloy with ultra-high strength was designed. • The addition of silicon hindered the precipitation of large NiAl phase. • Tensile strength and electrical conductivity were 1180 MPa and 18.1% IACS. • Nano-scale Ni 2 Si and Ni 3 Al improved the strength and electrical conductivity. - Abstract: Cu–10Ni–3Al–0.8Si alloy with ultra-high strength was designed and its microstructure was studied using optical microscopy, scanning electron microscopy, transmission electron microscopy. The alloy went through a set of thermo-mechanical process: solution treated at 950 °C for 4 h, then cold-rolled by 50% and aged at 450 °C for 8 h, followed by 60% cold-rolling and aging at 450 °C for 8 h. After these treatment, the tensile strength was 1180 MPa, yield strength was 1133 MPa and electrical conductivity was 18.1% IACS, respectively. The comprehensive properties, especially the electrical conductivity of the designed alloy, were much higher than those of traditional Cu–Ni–Al alloys. The addition of silicon in the designed alloy hindered the precipitation of large-scale NiAl phase and improved the strength of the alloy. The orientation relationships between δ-Ni 2 Si, Ni 3 Al precipitates and copper matrix were: [001] Cu ‖[001] Ni 3 Al ‖[001] δ ,(110) Cu ‖(110) Ni 3 Al ‖(010) δ ,(11 ¯ 0) Cu ‖ (11 ¯ 0) Ni 3 Al ||(100) δ , respectively

  9. Crystallization and thermo-mechanical properties of Li2O-ZnO-CaOSiO2 glass-ceramics with In2O3 and Fe2O3 additives

    Directory of Open Access Journals (Sweden)

    Saad M. Salman

    2015-12-01

    Full Text Available Li2O-ZnO-CaO-SiO2 based glasses were prepared by the conventional melting technique and subsequently converted to glass-ceramics by controlled crystallization. The nucleation and crystallization temperatures were determined by differential thermal analysis (DTA. The effects of adding In2O3 and Fe2O3 addition on the crystallization behaviour and thermo-mechanical properties of the prepared glass-ceramics were investigated. A study on the microstructure, close to the internal phases of the resulting glass-ceramics, was followed by using scanning electron microscope (SEM. The dilatometric thermal expansion and Vickers’ microhardness of the crystalline products were also evaluated. The crystalline phases that can be found in the resulting glass-ceramics, identified by X-ray diffraction (XRD analysis, are α-quartz-[SiO2], lithium zinc silicate-[Li2ZnSiO4], lithium disilicate-[Li2Si2O5], wollastonite-[CaSiO3], wollastonite containing iron, ferrobustamite-[(Ca0.79Fe0.21SiO3], and lithium indium silicate of pyroxene type-[LiInSi2O6]. Average thermal expansion coefficient (in the temperature range 25–700 °C decreased from 191×10-7 1/°C to 115×10-7 1/°C and the Vickers’ microhardness increased from 3.56 to 5.44 GPa with the increase of In2O3 and Fe2O3 contents in the glass-ceramics. The changes in the obtained expansion coefficient and microhardness were due to the formation of different phases which in turn influenced the rigidity/bonding and microstructure in the resultant glass-ceramics.

  10. Thermo-mechanically induced texture evolution and micro-structural change of aluminum metallization

    DEFF Research Database (Denmark)

    Brincker, Mads; Walter, Thomas; Kristensen, Peter Kjær

    2018-01-01

    During operation of high power electronic chips the topside metallization is subjected to cyclic compressive and tensile stresses leading to unwanted thermo-mechanical fatigue of the metallization layer. The stress is caused by the difference in the thermal expansion coefficients...... are not yet fully understood. In this work, we investigate the microstructural evolution of an Al metallization on high power diode chips subjected to passive thermal cycling between 20 and 100ºC. The texture of the Al film is analyzed ex-situ by a combination of electron backscatter diffraction and X...

  11. Thermo-mechanical design of a CW sweep plate emittance scanner

    International Nuclear Information System (INIS)

    Rathke, J.; Peacock, M.; Sredniawski, J.

    1996-01-01

    A sweep plate emittance scanner for use with high power, continuous wave (CW) beams has been designed, fabricated and commissioned at Northrop Grumman. The design is capable of scanning beams of up to 20 kW beam power with a spot diameter as small as 2 cm. The scanner pod is mounted on a ball screw driven linear bearing table that is driven through the beam by a stepper motor at velocities up to 30 cm/sec. This paper presents the thermo-mechanical analysis of the pod moving through a gaussian beam and the details of the mechanical design of the pod and motion system. Analyses to determine scanner cooling schemes and structural materials are presented. (author)

  12. Near-field thermal transient and thermomechanical stress analysis of a disposal vault in crystalline hard rock

    International Nuclear Information System (INIS)

    Tsui, K.K.; Tsai, A.; Lee, C.F.

    1981-01-01

    The Canadian Nuclear Fuel Waste Management Program currently focuses on the development of a disposal vault in crystalline hard rock at a reference depth of 1 km below the surface in a suitable pluton in the Canadian Shield. As part of Ontario Hydro's technical assistance to the Atomic Energy of Canada Limited in this program, studies are being carried out to determine the effects of radiogenic heat on the near-field behaviour of a disposal vault. This paper presents the study results obtained to date. Temperature and stress fields were computed and cross-checked by several finite element codes. A comparison between vertical and horizontal borehole emplacement concepts is made. The effects of material non-linearity (temperature dependence) and three-dimensionality on the thermomechanical response are evaluated. Case histories of thermal spalling or fracturing in rock were summarized and discussed to illustrate the possible mechanisms and processes involved in thermal fracturing. An assessment of the thermomechanical stability of the rock mass around a disposal vault under a state of high horizontal in-situ stress is also presented

  13. A numerical study of water percolation through an unsaturated variable aperture fracture under coupled thermomechanical effects

    International Nuclear Information System (INIS)

    Tsang, C.F.; Noorishad, J.; Hale, F.V.

    1991-12-01

    In calculation of ground water travel times associated with performance assessment of a nuclear waste repository, the role of fractures may turn out to be very important. There are two aspects related to fracture flow that have not been fully resolved. The first is the effect of coupled thermomechanical impact on fracture apertures due to the thermal output of the nuclear waste repository. The second is the effect of the variable aperture nature of the fractures. The present paper is an exploratory study of the impact of these two effects on water percolation through unsaturated fractures. The paper is divided into two main sections. the first section describes a calculation of the thermomechanical behavior of the geologic formation around a waste repository. In this exploratory study we assume two major fractures, one vertical and one horizontal through the repository center. Temperatures and thermally induced stress fields are calculated. The second part of the paper considers the unsaturated case and describes a study of water infiltration from the land surface through the vertical fracture to the repository

  14. Standard practice for strain controlled thermomechanical fatigue testing

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2010-01-01

    1.1 This practice covers the determination of thermomechanical fatigue (TMF) properties of materials under uniaxially loaded strain-controlled conditions. A “thermomechanical” fatigue cycle is here defined as a condition where uniform temperature and strain fields over the specimen gage section are simultaneously varied and independently controlled. This practice is intended to address TMF testing performed in support of such activities as materials research and development, mechanical design, process and quality control, product performance, and failure analysis. While this practice is specific to strain-controlled testing, many sections will provide useful information for force-controlled or stress-controlled TMF testing. 1.2 This practice allows for any maximum and minimum values of temperature and mechanical strain, and temperature-mechanical strain phasing, with the restriction being that such parameters remain cyclically constant throughout the duration of the test. No restrictions are placed on en...

  15. TiNi shape memory alloys: effects of the fabrication route, the oxygen content and the zirconium or hafnium additions on the metallurgical characteristics and the thermomechanical properties

    International Nuclear Information System (INIS)

    Olier, P.

    1996-01-01

    In order to promote the development of Ti-Ni shape memory alloys, we have studied the correlation between the fabrication route, the chemical composition (O 2 content, Zr or Hf additions), the metallurgical characteristics and the thermomechanical properties. A conventional sintering does not allow to obtain a homogeneous compound of pure Ti 50 Ni 50 alloy because of the occurrence of Kirkendall porosities which act as a diffusion barrier. An original process including combustion synthesis and hot-extrusion was successfully developed. Resulting products exhibit a smaller grain size (15-20μm) and an enhanced workability in comparison with products obtained by arc-melting and subsequent hot rolling. The presence of oxygen in equiatomic Ti-Ni alloy induces the oxide precipitation of Ti 4 Ni 2 O x type (with x ≤ 1). The precipitated particle fraction is proportional to the oxygen nominal content of the alloy. We show that the decrease of the transformation temperatures is correlated with the decrease of Ti in solid solution due to Ti 4 Ni 2 O precipitation. Moreover, we find that a fine and homogenous oxide dispersion is suitable to decrease the grain size during hot rolling and to enhance to the one way shape memory properties. An increase of the typical transformation temperatures is obtained through of Zr or Hf (in substitution to Ti). But, an increase of the hardness is measured, and consequently the workability of the ternary alloys becomes reduced. However, it is worthwhile to point out that a Ti 38 Ni 50 Hf 12 product obtained by arc melting and hot extrusion is able to fully recover an apparent plastic strain of more than 4% during tensile tests performed under special loading conditions. Such as behaviour is of great interest with respect to potential applications in a temperature range higher that 100 deg. C. (author)

  16. RODSWELL: a computer code for the thermomechanical analysis of fuel rods under LOCA conditions

    International Nuclear Information System (INIS)

    Casadei, F.; Laval, H.; Donea, J.; Jones, P.M.; Colombo, A.

    1984-01-01

    The present report is the user's manual for the computer code RODSWELL developed at the JRC-Ispra for the thermomechanical analysis of LWR fuel rods under simulated loss-of-coolant accident (LOCA) conditions. The code calculates the variation in space and time of all significant fuel rod variables, including fuel, gap and cladding temperature, fuel and cladding deformation, cladding oxidation and rod internal pressure. The essential characteristics of the code are briefly outlined here. The model is particularly designed to perform a full thermal and mechanical analysis in both the azimuthal and radial directions. Thus, azimuthal temperature gradients arising from pellet eccentricity, flux tilt, arbitrary distribution of heat sources in the fuel and the cladding and azimuthal variation of coolant conditions can be treated. The code combines a transient 2-dimensional heat conduction code and a 1-dimentional mechanical model for the cladding deformation. The fuel rod is divided into a number of axial sections and a detailed thermomechanical analysis is performed within each section in radial and azimuthal directions. In the following sections, instructions are given for the definition of the data files and the semi-variable dimensions. Then follows a complete description of the input data. Finally, the restart option is described

  17. Three-Dimensional Finite Element Modeling of Thermomechanical Problems in Functionally Graded Hydroxyapatite/Titanium Plate

    Directory of Open Access Journals (Sweden)

    S. N. S. Jamaludin

    2014-01-01

    Full Text Available The composition of hydroxyapatite (HA as the ceramic phase and titanium (Ti as the metallic phase in HA/Ti functionally graded materials (FGMs shows an excellent combination of high biocompatibility and high mechanical properties in a structure. Because the gradation of these properties is one of the factors that affects the response of the functionally graded (FG plates, this paper is presented to show the domination of the grading parameter on the displacement and stress distribution of the plates. A three-dimensional (3D thermomechanical model of a 20-node brick quadratic element is used in the simulation of the thermoelastic behaviors of HA/Ti FG plates subjected to constant and functional thermal, mechanical, and thermomechanical loadings. The convergence properties of the present results are examined thoroughly in order to assess the accuracy of the theory applied and to compare them with the established research results. Instead of the grading parameter, this study reveals that the loading field distribution can be another factor that reflects the thermoelastic properties of the HA/Ti FG plates. The FG structure is found to be able to withstand the thermal stresses while preserving the high toughness properties and thus shows its ability to operate at high temperature.

  18. On the hot cracking susceptibility of a semisolid aluminium 6061 weld: Application of a coupled solidification- thermomechanical model

    International Nuclear Information System (INIS)

    Rajani, H R Zareie; Phillion, A B

    2015-01-01

    A coupled solidification-thermomechanical model is presented that investigates the hot tearing susceptibility of an aluminium 6061 semisolid weld. Two key phenomena are considered: excessive deformation of the semisolid weld, initiating a hot tear, and the ability of the semisolid weld to heal the hot tear by circulation of the molten metal. The model consists of two major modules: weld solidification and thermomechanical analysis. 1) By means of a multi-scale model of solidification, the microstructural evolution of the semisolid weld is simulated in 3D. The semisolid structure, which varies as a function of welding parameters, is composed of solidifying grains and a network of micro liquid channels. The weld solidification module is utilized to obtain the solidification shrinkage. The size of the micro liquid channels is used as an indicator to assess the healing ability of the semisolid weld. 2) Using the finite element method, the mechanical interaction between the weld pool and the base metal is simulated to capture the transient force field deforming the semisolid weld. Thermomechanical stresses and shrinkage stresses are both considered in the analysis; the solidification contractions are extracted from the weld solidification module and applied to the deformation simulation as boundary conditions. Such an analysis enables characterization of the potential for excessive deformation of the weld. The outputs of the model are used to study the effect of welding parameters including welding current and speed, and also welding constraint on the hot cracking susceptibility of an aluminium alloy 6061 semisolid weld. (paper)

  19. Thermo-mechanical interaction effects in foam cored sandwich panels-correlation between High-order models and Finite element analysis results

    DEFF Research Database (Denmark)

    Palleti, Hara Naga Krishna Teja; Santiuste, Carlos; Thomsen, Ole Thybo

    2010-01-01

    Thermo-mechanical interaction effects including thermal material degradation in polymer foam cored sandwich structures is investigated using the commercial Finite Element Analysis (FEA) package ABAQUS/Standard. Sandwich panels with different boundary conditions in the form of simply supported...

  20. Thermomechanical behavior of graphite and coating materials subjected to a high heat flux

    Energy Technology Data Exchange (ETDEWEB)

    Ioki, K.; Yamada, M.; Nishikawa, M.; Uchikawa, T.; Onozuka, M.; Yamao, H.

    1987-07-01

    This study has been performed for the development of limiter and divertor plates. Their thermal and thermomechanical behavior were examined in heat load experiments with an electron beam facility, and were compared with analysis results. Graphite was proven to have a high thermal shock resistance. Its erosion thickness and thermal contact conductance were also studied. Copper alloy with coating and graphite brazed to metal were tested, and their feasibility was demonstrated for use as limiter and divertor plates of an advanced-type concept.

  1. A thermo-mechanical benchmark calculation of an hexagonal can in the BTI accident with ABAQUS code

    International Nuclear Information System (INIS)

    Zucchini, A.

    1988-07-01

    The thermo-mechanical behaviour of an hexagonal can in a benchmark problem (simulating the conditions of a BTI accident in a fuel assembly) is examined by means of the ABAQUS code: the effects of the geometric nonlinearity are shown and the results are compared with those of a previous analysis performed with the INCA code. (author)

  2. Thermo-mechanical properties of poly ε-caprolactone/poly L-lactic acid blends: addition of nalidixic acid and polyethylene glycol additives.

    Science.gov (United States)

    Douglas, P; Albadarin, Ahmad B; Al-Muhtaseb, Ala'a H; Mangwandi, Chirangano; Walker, G M

    2015-05-01

    The search for ideal biomaterials is still on-going for tissue regeneration. In this study, blends of poly ε-caprolactone (PCL) with poly l-lactic acid (PLLA), nalidixic acid (NA) and polyethylene glycol (PEG) were prepared. Mechanical and thermal properties of the blends were investigated by tensile and flexural analysis, DSC, TGA, WXRD, MFI, BET, SEM and hot stage optical microscopy. Results showed that the loading of PLLA caused a significant decrease in tensile strength and almost total eradication of the elongation at break of PCL matrix, especially after PEG and NA addition. Increased stiffness was also noted with additional NA, PEG and PLLA, resulting in an increase in the flexural modulus of the blends. Isothermal degradation indicated that bulk PCL, PLLA and the blends were thermally stable at 200°C for the duration of 2h making extrusion of the blends at this temperature viable. Morphological study showed that increasing the PLLA content and addition of the very low viscosity PEG and powder NA decreased the Melt Flow Indexer and increased the viscosity. At the higher temperature, the PLLA begins to soften and eventually melts allowing for increased flow and, coupling this with, the natural increase in MFI caused by temperature is enhanced further. The PEG and NA addition increased dramatically the pore volume which is important for cell growth and flow transport of nutrients and metabolic waste. Copyright © 2015 Elsevier Ltd. All rights reserved.

  3. Optical nonlinearity due to thermomechanical effect in the planar and homeotropic nematic liquid crystals

    Energy Technology Data Exchange (ETDEWEB)

    Poursamad, J.B. [Physics & Optic Engineering Group, University of Bonab, Bonab (Iran, Islamic Republic of); Phirouznia, A. [Department of Physics, Azerbaijan ShahidMadani University, 53714-161 Tabriz (Iran, Islamic Republic of); Sahrai, M. [Research Institue for Applied Physics and Astronomy, Univerity of Tabriz, Tabriz (Iran, Islamic Republic of)

    2015-11-01

    Possibility of observing third thermomechanical (TM) effect in uniform nematic liquid crystals (NLC) with proper selection of boundary conditions on the cell walls is theoretically studied. Absorption of a light wave induces the needed temperature gradient for the TM effect. The molecular director reorientation due to third TM effect and the induced phase shift on the probe beam are calculated. The forth TM coefficient can be measured directly by the method proposed in this work.

  4. Inorganic Nanoparticle-Modified Poly(Phenylene Sulphide/ Carbon Fiber Laminates: Thermomechanical Behaviour

    Directory of Open Access Journals (Sweden)

    Ana M. Díez-Pascual

    2013-07-01

    Full Text Available Carbon fiber (CF-reinforced high-temperature thermoplastics such as poly(phenylene sulphide (PPS are widely used in structural composites for aerospace and automotive applications. The porosity of CF-reinforced polymers is a very important topic for practical applications since there is a direct correlation between void content and mechanical properties. In this study, inorganic fullerene-like tungsten disulphide (IF-WS2 lubricant nanoparticles were used to manufacture PPS/IF-WS2/CF laminates via melt-blending and hot-press processing, and the effect of IF-WS2 loading on the quality, thermal and mechanical behaviour of the hybrid composites was investigated. The addition of IF-WS2 improved fiber impregnation, resulting in lower degree of porosity and increased delamination resistance, compression and flexural properties; their reinforcement effect was greater at temperatures above the glass transition (Tg. IF-WS2 contents higher than 0.5 wt % increased Tg and the heat deflection temperature while reduced the coefficient of thermal expansion. The multiscale laminates exhibited higher ignition point and notably reduced peak heat release rate compared to PPS/CF. The coexistence of micro- and nano-scale fillers resulted in synergistic effects that enhanced the stiffness, strength, thermal conductivity and flame retardancy of the matrix. The results presented herein demonstrate that the IF-WS2 are very promising nanofillers to improve the thermomechanical properties of conventional thermoplastic/CF composites.

  5. Effect of the Thermomechanical Treatment on Structural and Phase Transformations in Cu-14Al-3Ni Shape Memory Alloy Subjected to High-Pressure Torsion

    Science.gov (United States)

    Lukyanov, A. V.; Pushin, V. G.; Kuranova, N. N.; Svirid, A. E.; Uksusnikov, A. N.; Ustyugov, Yu. M.; Gunderov, D. V.

    2018-04-01

    The possibilities of controlling the structure and properties of a Cu-Al-Ni shape memory alloy due to the use of different schemes of the thermomechanical treatment, including forging, homogenizing in the austenitic state and subsequent quenching, and high-pressure torsion have been found. For the first time, an ultrafine-grain structure has been produced in this alloy via severe plastic deformation using high-pressure torsion. It has been detected that high-pressure torsion using ten revolutions of the anvils leads to the formation of a nanocrystalline structure with a grain size of less than 100 nm. The subsequent short-term heating of the alloy to 800°C (10 s) in the temperature region of the existence of the homogeneous β phase made it possible to form an ultrafine-grain structure with predominant sizes of recrystallized grains of 1 and 8 μm. The quenching after heating prevented the decomposition of the solid solution. The refinement of the grain structure changed the deformation behavior of the alloy, having provided the possibility of the significant plastic deformation upon mechanical tensile tests. The coarse-grained hot-forged quenched alloy was brittle, and fracture occurred along the boundaries of former austenite grains and martensite packets. The highstrength ultrafine-grained alloy also experienced mainly the intercrystalline fracture along the high-angle boundaries of elements of the structure, the grain size of which was less by two orders than that in the initial alloy. This determined an increase in its relative elongation upon mechanical tests.

  6. Physical and mechanical properties of a thermomechanically treated NiTi wire used in the manufacture of rotary endodontic instruments.

    Science.gov (United States)

    Pereira, E S J; Peixoto, I F C; Viana, A C D; Oliveira, I I; Gonzalez, B M; Buono, V T L; Bahia, M G A

    2012-05-01

    To compare physical and mechanical properties of one conventional and one thermomechanically treated nickel-titanium (NiTi) wire used to manufacture rotary endodontic instruments. Two NiTi wires 1.0 mm in diameter were characterized; one of them, C-wire (CW), was processed in the conventional manner, and the other, termed M-Wire (MW), received an additional heat treatment according to the manufacturer. Chemical composition was determined by energy-dispersive X-ray spectroscopy, phase constitution by XRD and the transformation temperatures by DSC. Tensile loading/unloading tests and Vickers microhardness measurements were performed to assess the mechanical behaviour. Data were analysed using analysis of variance (α = 0.05). The two wires showed approximately the same chemical composition, close to the 1 : 1 atomic ratio, and the β-phase was the predominant phase present. B19' martensite and the R-phase were found in MW, in agreement with the higher transformation temperatures found in this wire compared with CW, whose transformation temperatures were below room temperature. Average Vickers microhardness values were similar for MW and CW (P = 0.91). The stress at the transformation plateau in the tensile load-unload curves was lower and more uniform in the M-Wire, which also showed the smallest stress hysteresis and apparent elastic modulus. The M-Wire had physical and mechanical properties that can render endodontic instruments more flexible and fatigue resistant than those made with conventionally processed NiTi wires. © 2011 International Endodontic Journal.

  7. The mechanical properties, deformation and thermomechanical properties of alkali treated and untreated Agave continuous fibre reinforced epoxy composites

    International Nuclear Information System (INIS)

    Mylsamy, K.; Rajendran, I.

    2011-01-01

    Research highlights: → New renewable and biodegradable Agave americana fibre. → Environmentally free materials. → Good mechanical properties of Agave fibre reinforced epoxy composite materials. → Surface modification of the fibre (Alkali treatment) imported good mechanical properties. → Future scope in light weight materials manufacture. -- Abstract: The mechanical properties such as tensile, compressive, flexural, impact strength and water absorption of the alkali treated continuous Agave fibre reinforced epoxy composite (TCEC) and untreated continuous Agave fibre reinforced epoxy composite (UTCEC) were analysed. A comparison of the surfaces of TCEC and UTCEC composites was carried out by dynamic mechanical analysis (DMA), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). The thermomechanical properties of the composite reinforced with sodium hydroxide (NaOH) treated Agave fibres were considerably good as the shrinkage of the fibre during alkali treatment had facilitated more points of fibre resin interface. The SEM micrograph and FTIR spectra of the impact fracture surfaces of TCEC clearly demonstrate the better interfacial adhesion between fibre and the matrix. In both analyses the TCEC gave good performance than UTCEC and, thus, there is a scope for its application in light weight manufacture in future.

  8. Thermomechanical behavior of graphite and coating materials subjected to a high heat flux

    International Nuclear Information System (INIS)

    Ioki, K.; Yamada, M.; Nishikawa, M.; Uchikawa, T.; Onozuka, M.; Yamao, H.

    1987-01-01

    This study has been performed for the development of limiter and divertor plates. Their thermal and thermomechanical behavior were examined in heat load experiments with an electron beam facility, and were compared with analysis results. Graphite was proven to have a high thermal shock resistance. Its erosion thickness and thermal contact conductance were also studied. Copper alloy with coating and graphite brazed to metal were tested, and their feasibility was demonstrated for use as limiter and divertor plates of an advanced-type concept. (orig.)

  9. Description of the shape memory effect of radiation-modified polymers under thermomechanical action

    International Nuclear Information System (INIS)

    Chernous, D.A.; Shil'ko, S.V.; Pleskachevskij, Yu.M.

    2004-01-01

    The 'shape memory' effect of crystallizing polymer materials is simulated. The polymer is considered to be an inhomogeneous medium with a moving boundary (temperature-dependent phase composition). Using a model based on the 'frozen strain' hypothesis, the temperature dependences of stresses under isometric heating and cooling have been obtained. On the basis of the known data on the influence of gamma-irradiation on the thermomechanical characteristics the dependences of thermorelaxation and thermoshrinkage stresses on the absorbed dose for high-density polyethylene have been found. (Authors)

  10. Analysis of the thermo-mechanical behaviour of the DEMO Water-Cooled Lithium Lead breeding blanket module under normal operation steady state conditions

    Energy Technology Data Exchange (ETDEWEB)

    Di Maio, P.A.; Arena, P. [Dipartimento di Energia, Ingegneria dell’Informazione e Modelli Matematici, Università di Palermo, Viale delle Scienze, 90128 Palermo (Italy); Aubert, J. [CEA Saclay, DEN/DANS/DM2S/SEMT, 91191 Gif sur Yvette Cedex (France); Bongiovì, G. [Dipartimento di Energia, Ingegneria dell’Informazione e Modelli Matematici, Università di Palermo, Viale delle Scienze, 90128 Palermo (Italy); Chiovaro, P., E-mail: pierluigi.chiovaro@unipa.it [Dipartimento di Energia, Ingegneria dell’Informazione e Modelli Matematici, Università di Palermo, Viale delle Scienze, 90128 Palermo (Italy); Giammusso, R. [ENEA – C.R. Brasimone, 40032 Camugnano (Italy); Li Puma, A. [CEA Saclay, DEN/DANS/DM2S/SEMT, 91191 Gif sur Yvette Cedex (France); Tincani, A. [ENEA – C.R. Brasimone, 40032 Camugnano (Italy)

    2015-10-15

    Highlights: • A DEMO WCLL blanket module thermo-mechanical behaviour has been investigated. • Two models of the WCLL blanket module have been set-up adopting a code based on FEM. • The water flow domain in the module has been considered. • A set of uncoupled steady state thermo-mechanical analyses has been carried out. • Critical temperature is not overcome. Safety verifications are generally satisfied. - Abstract: Within the framework of DEMO R&D activities, a research cooperation has been launched between ENEA, the University of Palermo and CEA to investigate the thermo-mechanical behaviour of the outboard equatorial module of the DEMO1 Water-Cooled Lithium Lead (WCLL) blanket under normal operation steady state scenario. The research campaign has been carried out following a theoretical–computational approach based on the Finite Element Method (FEM) and adopting a qualified commercial FEM code. In particular, two different 3D FEM models (Model 1 and Model 2), reproducing respectively the central and the lateral poloidal–radial slices of the WCLL blanket module, have been set up. A particular attention has been paid to the modelling of water flow domain, within both the segment box channels and the breeder zone tubes, to simulate realistically the coolant-box thermal coupling. Results obtained are herewith reported and critically discussed.

  11. Technical support for GEIS: radioactive waste isolation in geologic formations. Volume 20. Thermo-mechanical stress analysis and development of thermal loading guidelines

    International Nuclear Information System (INIS)

    1978-04-01

    This volume is one of a 23-volume series which supplements a Contribution to Draft Generic Environmental Impact Statement on Commercial Waste Management: Radioactive Waste Isolation in Geologic Formations, Y/OWI/TM-44. The series provides a more complete technical basis for the preconceptual designs, resource requirements, and environmental source terms associated with isolating commercial LWR wastes in underground repositories in salt, granite, shale and basalt. Wastes are considered from three fuel cycles: uranium and plutonium recycling, no recycling of spent fuel, and uranium-only recycling. The thermo-mechanical analysis of proposed preconceptual repositories in granite, shale and basalt have been undertaken. The analysis, was conducted on three different levels of scale (i) Very Near Field (canister scale), (ii) Near Field (excavation scale) and (iii) Far Field (regional scale) studies. Three numerical methods were used to undertake the thermo-mechanical calculations; namely, the finite element method for thermal stress analysis, the boundary element method for thermal and thermal stress analysis and the semi-analytical method also for thermal and thermal stresses analysis. From the thermo-mechanical studies with simplifying assumptions on rock mass behavior where applicable, recommendations for areal thermal loadings to assure retrievability of the canisters and long term safety of the repository are given

  12. Thermo-mechanical tests of a CFC divertor mock-up

    International Nuclear Information System (INIS)

    Cardella, A.; Akiba, M.; Duwe, R.; Di Pietro, E.; Suzuki, S.; Satoh, K.; Reheis, N.

    1994-01-01

    Thermo-mechanical tests have been performed on a divertor mock-up consisting of a metallic tube armoured with five carbon fibre composite tiles. The tube is inserted the tiles and brazed with TiCuSil braze (monoblock concept). The tube material is TZM, a molybdenum alloy, and the armour material is SEP CARB N112, a high conductivity carbon-carbon composite. Using special surface preparation consisting of laser drilling, small (≅ 500 μm) holes in the composite have been made to increase the surface wetted by the braze and the resistance. The mock-up has been tested at the JAERI 400 kW electron beam test facility JEBIS. The aim of the test was to assess the performance of the mock-up in screening and thermal fatigue tests with particular attention to the behaviour of the armour to heat sink joint. (orig.)

  13. A Study of the Effect of Interrupted Quenches on a Thermomechanically Processed High Carbon Steel.

    Science.gov (United States)

    1982-10-01

    steel . Successful martempering requires a cooling rate sufficient to avoid the nose of the C- curve and thus prevent significant bainite formation. When...STUDY OF THE EFFECT OF INTERRUPTED QUENCHES ON A THERMONECHANICALLY PROCESSED HIGH CARBON STEEL by Steven A. Barton October 1982 Thesis Advisor: T.R...unlimited. A Study of the Effect of Interrupted Quenches on a Thermomechanically Processed High Carbon Steel by Steven A. Barton Lieutenant, United

  14. Thermo-Mechanical Characterisation of In-Plane Properties for CSM E-glass Epoxy Polymer Composite Materials – Part 1

    DEFF Research Database (Denmark)

    Jakobsen, Johnny; Jensen, Martin; Andreasen, Jens H.

    2013-01-01

    The in-plane thermo-mechanical properties and residual stresses of a CSM E-glass/Epoxy material are characterised through the use of DSC and TMA. The measured data is used to generate material models which describe the mechanical behaviour as a function of conversion and temperature. The in-plane...

  15. The Numerical Nuclear Reactor for High-Fidelity Integrated Simulation of Neutronic, Thermal-Hydraulic, and Thermo-Mechanical Phenomena

    Energy Technology Data Exchange (ETDEWEB)

    Kim, K. S.; Ju, H. G.; Jeon, T. H. and others

    2005-03-15

    A comprehensive high fidelity reactor core modeling capability has been developed for detailed analysis of current and advanced reactor designs as part of a US-ROK collaborative I-NERI project. High fidelity was accomplished by integrating highly refined solution modules for the coupled neutronic, thermal-hydraulic, and thermo-mechanical phenomena. Each solution module employs methods and models that are formulated faithfully to the first-principles governing the physics, real geometry, and constituents. Specifically, the critical analysis elements that are incorporated in the coupled code capability are whole-core neutron transport solution, ultra-fine-mesh computational fluid dynamics/heat transfer solution, and finite-element-based thermo-mechanics solution, all obtained with explicit (fuel pin cell level) heterogeneous representations of the components of the core. The vast computational problem resulting from such highly refined modeling is solved on massively parallel computers, and serves as the 'numerical nuclear reactor'. Relaxation of modeling parameters were also pursued to make problems run on clusters of workstations and PCs for smaller scale applications as well.

  16. The Numerical Nuclear Reactor for High-Fidelity Integrated Simulation of Neutronic, Thermal-Hydraulic, and Thermo-Mechanical Phenomena

    International Nuclear Information System (INIS)

    Kim, K. S.; Ju, H. G.; Jeon, T. H. and others

    2005-03-01

    A comprehensive high fidelity reactor core modeling capability has been developed for detailed analysis of current and advanced reactor designs as part of a US-ROK collaborative I-NERI project. High fidelity was accomplished by integrating highly refined solution modules for the coupled neutronic, thermal-hydraulic, and thermo-mechanical phenomena. Each solution module employs methods and models that are formulated faithfully to the first-principles governing the physics, real geometry, and constituents. Specifically, the critical analysis elements that are incorporated in the coupled code capability are whole-core neutron transport solution, ultra-fine-mesh computational fluid dynamics/heat transfer solution, and finite-element-based thermo-mechanics solution, all obtained with explicit (fuel pin cell level) heterogeneous representations of the components of the core. The vast computational problem resulting from such highly refined modeling is solved on massively parallel computers, and serves as the 'numerical nuclear reactor'. Relaxation of modeling parameters were also pursued to make problems run on clusters of workstations and PCs for smaller scale applications as well

  17. On the Effects of Thermal History on the Development and Relaxation of Thermo-Mechanical Stress in Cryopreservation.

    Science.gov (United States)

    Eisenberg, David P; Steif, Paul S; Rabin, Yoed

    2014-01-01

    This study investigates the effects of the thermal protocol on the development and relaxation of thermo-mechanical stress in cryopreservation by means of glass formation, also known as vitrification. The cryopreserved medium is modeled as a homogeneous viscoelastic domain, constrained within either a stiff cylindrical container or a highly compliant bag. Annealing effects during the cooling phase of the cryopreservation protocol are analyzed. Results demonstrate that an intermediate temperature-hold period can significantly reduce the maximum tensile stress, thereby decreasing the potential for structural damage. It is also demonstrated that annealing at temperatures close to glass transition significantly weakens the dependency of thermo-mechanical stress on the cooling rate. Furthermore, a slower initial rewarming rate after cryogenic storage may drastically reduce the maximum tensile stress in the material, which supports previous experimental observations on the likelihood of fracture at this stage. This study discusses the dependency of the various stress components on the storage temperature. Finally, it is demonstrated that the stiffness of the container wall can affect the location of maximum stress, with implications on the development of cryopreservation protocols.

  18. Thermo-mechanical fatigue behavior of the intermetallic gamma-TiAl alloy TNB-V5 with different microstructures

    International Nuclear Information System (INIS)

    Roth, M; Biermann, H

    2010-01-01

    The cyclic deformation and fatigue behavior of the γ-TiAl alloy TNB-V5 is studied under thermo-mechanical load for the three technically important microstructures Fully-Lamellar (FL), Near-Gamma (NG) and Duplex (DP), respectively. Thus, thermo-mechanical fatigue (TMF) tests were carried out with different temperature-strain cycles, different temperature ranges from 400 0 C to 800 0 C and with two different strain ranges. Cyclic deformation curves, stress-strain hysteresis loops and fatigue lives are presented. The type of microstructure shows a surprisingly small influence on the cyclic deformation and fatigue behavior under TMF conditions. For a general life prediction the damage parameter of Smith, Watson and Topper P SWT is well suitable, if the testing and the application temperature ranges, respectively, include temperatures above the ductile-brittle transition temperature (approx. 750 0 C). If the maximum temperature is below that temperature, the brittle materials' behavior yields a high scatter of fatigue lives and a low slope of the fatigue life curve and therefore the damage parameter P SWT cannot be applied for the live prediction.

  19. Optimization of the heat and mechanical treatment of the Al-Zn-Mg-Li alloy

    Directory of Open Access Journals (Sweden)

    M. Stegliński

    2010-07-01

    Full Text Available In terms of high strength in relation to mass the alloys of aluminium – lithium find more and more use mainly in aircraft industry like inspacecraft. At present intensive investigations are carried out in aim of use of Al – Li in automotive industry in particular to components subject to fatigue wear. It could contribute to replace transmission’s elements made from traditional materials by aluminium - lithium alloys. However low resistance to wear due to forming of thin Al2O3 layer which is reproducing in friction contact disqualifies using aluminium alloys in friction contact. From this point of view first stage of investigation was to enhance hardness properties of the substrate by applying thermo-mechanical treatment.In this article the results of heat treatment of Al-Zn-Mg-Li alloy were presented. During investigations optimum parameters (timetemperature of the solution heat treatment were elaborated. Micro hardness on the cross-section were investigated. Phase, chemicalcomposition and morphology were determined. It was found that hardness after thermo-mechanical treatment of Al-Zn-Mg-Li is about20% higher than for AlCu4Mg1 (7075 –T6 alloy.

  20. Precipitation Strengthening by Induction Treatment in High Strength Low Carbon Microalloyed Hot-Rolled Plates

    Science.gov (United States)

    Larzabal, G.; Isasti, N.; Rodriguez-Ibabe, J. M.; Uranga, P.

    2018-03-01

    The use of microalloyed steels in the production of thick plates is expanding due to the possibility of achieving attractive combinations of strength and toughness. As market requirements for high strength plates are increasing and new applications require reduced weight and innovative designs, novel approaches to attaining cost-effective grades are being developed. The mechanism of precipitation strengthening has been widely used in thin strip products, since the optimization of the coiling strategy offers interesting combinations in terms of final properties and microalloying additions. Precipitation strengthening in thick plates, however, is less widespread due to the limitation of interphase precipitation during continuous cooling after hot rolling. With the main objective of exploring the limits of this strengthening mechanism, laboratory thermomechanical simulations that reproduced plate hot rolling mill conditions were performed using low carbon steels microalloyed with Nb, NbMo, and TiMo additions. After continuous cooling to room temperature, a set of heat treatments using fast heating rates were applied simulating the conditions of induction heat treatments. An important increase of both yield and tensile strengths was measured after induction treatment without any important impairment in toughness properties. A significant precipitation hardening is observed in Mo-containing grades under specific heat treatment parameters.

  1. Thermomechanical DART code improvements for LEU VHD dispersion and monolithic fuel element analysis

    International Nuclear Information System (INIS)

    Taboada, H.; Saliba, R.; Moscarda, M.V.; Rest, J.

    2005-01-01

    A collaboration agreement between ANL/US DOE and CNEA Argentina in the area of Low Enriched Uranium Advanced Fuels has been in place since October 16, 1997 under the Implementation Arrangement for Technical Exchange and Cooperation in the Area of Peaceful Uses of Nuclear Energy. An annex concerning DART code optimization has been operative since February 8, 1999. Previously, as a part of this annex a visual FASTDART version and also a DART THERMAL version were presented during RERTR 2000, 2002 and RERTR 2003 Meetings. During this past year the following activities were completed: Optimization of DART TM code Al diffusion parameters by testing predictions against reliable data from RERTR experiments. Improvements on the 3-D thermo-mechanical version of the code for modeling the irradiation behavior of LEU U-Mo monolithic fuel. Concerning the first point, by means of an optimization of parameters of the Al diffusion through the interaction product theoretical expression, a reasonable agreement between DART temperature calculations with reliable RERTR PIE data was reached. The 3-D thermomechanical code complex is based upon a finite element thermal-elastic code named TERMELAS, and irradiation behavior provided by the DART code. An adequate and progressive process of coupling calculations of both codes at each time step is currently developed. Compatible thermal calculation between both codes was reached. This is the first stage to benchmark and validate against RERTR PIE data the coupling process. (author)

  2. Thermo-mechanical constitutive modeling of unsaturated clays based on the critical state concepts

    Directory of Open Access Journals (Sweden)

    Saeed Tourchi

    2015-04-01

    Full Text Available A thermo-mechanical constitutive model for unsaturated clays is constructed based on the existing model for saturated clays originally proposed by the authors. The saturated clays model was formulated in the framework of critical state soil mechanics and modified Cam-clay model. The existing model has been generalized to simulate the experimentally observed behavior of unsaturated clays by introducing Bishop's stress and suction as independent stress parameters and modifying the hardening rule and yield criterion to take into account the role of suction. Also, according to previous studies, an increase in temperature causes a reduction in specific volume. A reduction in suction (wetting for a given confining stress may induce an irreversible volumetric compression (collapse. Thus an increase in suction (drying raises a specific volume i.e. the movement of normal consolidation line (NCL to higher values of void ratio. However, some experimental data confirm the assumption that this reduction is dependent on the stress level of soil element. A generalized approach considering the effect of stress level on the magnitude of clays thermal dependency in compression plane is proposed in this study. The number of modeling parameters is kept to a minimum, and they all have clear physical interpretations, to facilitate the usefulness of model for practical applications. A step-by-step procedure used for parameter calibration is also described. The model is finally evaluated using a comprehensive set of experimental data for the thermo-mechanical behavior of unsaturated soils.

  3. Thermo-mechanical analysis of FG nanobeam with attached tip mass: an exact solution

    Science.gov (United States)

    Ghadiri, Majid; Jafari, Ali

    2016-12-01

    Present disquisition proposes an analytical solution method for exploring the vibration characteristics of a cantilever functionally graded nanobeam with a concentrated mass exposed to thermal loading for the first time. Thermo-mechanical properties of FGM nanobeam are supposed to change through the thickness direction of beam based on the rule of power-law (P-FGM). The small-scale effect is taken into consideration based on nonlocal elasticity theory of Eringen. Linear temperature rise (LTR) through thickness direction is studied. Existence of centralized mass in the free end of nanobeam influences the mechanical and physical properties. Timoshenko beam theory is employed to derive the nonlocal governing equations and boundary conditions of FGM beam attached with a tip mass under temperature field via Hamilton's principle. An exact solution procedure is exploited to achieve the non-dimensional frequency of FG nanobeam exposed to temperature field with a tip mass. A parametric study is led to assess the efficacy of temperature changes, tip mass, small scale, beam thickness, power-law exponent, slenderness and thermal loading on the natural frequencies of FG cantilever nanobeam with a point mass at the free end. It is concluded that these parameters play remarkable roles on the dynamic behavior of FG nanobeam subjected to LTR with a tip mass. The results for simpler states are confirmed with known data in the literature. Presented numerical results can serve as benchmarks for future thermo-mechanical analyses of FG nanobeam with tip mass.

  4. A meshless approach to thermomechanics of DC casting of aluminium billets

    International Nuclear Information System (INIS)

    Mavrič, B; Šarler, B

    2016-01-01

    The ability to model thermomechanics in DC casting is important due to the technological challenges caused by physical phenomena such as different ingot distortions, cracking, hot tearing and residual stress. Many thermomechanical models already exist and usually take into account three contributions: elastic, thermal expansion, and viscoplastic to model the mushy zone. These models are, in a vast majority, solved by the finite element method. In the present work the elastic model that accounts for linear thermal expansion is considered. The method used for solving the model is of a novel meshless type and extends our previous meshless attempts in solving fluid mechanics problems. The solution to the problem is constructed using collocation on the overlapping subdomains, which are composed of computational nodes. Multiquadric radial basis functions, augmented by monomials, are used for the displacement interpolation. The interpolation is constructed in such a manner that it readily satisfies the boundary conditions. The discretization results in construction of a global square sparse matrix representing the system of linear equations for the displacement field. The developed method has many advantages. The system of equations can be easily constructed and efficiently solved. There is no need to perform expensive meshing of the domain and the formulation of the method is similar in two and three dimensions. Since no meshing is required, the nodes can easily be added or removed, which allows for efficient adaption of the node arrangement density. The order of convergence, estimated through an analytically solvable test, can be adjusted through the number of interpolation nodes in the subdomain, with 6 nodes being enough for the second order convergence. Simulations of axisymmetric mechanical problems, associated with low frequency electromagnetic DC casting are presented. (paper)

  5. Thermomechanical fatigue behavior of SiC/Ti-24Al-11Nb in air and argon environments

    Science.gov (United States)

    Bartolotta, Paul A.; Verrilli, Michael J.

    1992-01-01

    A series of tension-tension, load-controlled thermomechanical fatigue (TMF) tests were conducted on a titanium aluminide composite in both laboratory air and a flowing argon environment. Results from these tests show that the environment plays an increasingly important role as applied stress levels are decreased. Differences in damage mechanisms between the two environments were observed which corresponds to observed variations in TMF lives.

  6. Tungsten - rhenium alloys wire: overview of thermomechanical processing and properties data

    International Nuclear Information System (INIS)

    Bryskin, B.

    2001-01-01

    The scope of this study encompasses the compositional modifications of the tungsten-rhenium dual system (W-3/5 Re up to W-27 Re) as well as some of the tungsten-molybdenum-rhenium ternary system. The alloys of interest are considered with a specific representation of powder metallurgy route based on doped or undoped tungsten vs. vacuum melted materials. This paper constitutes an in-depth review of structural and mechanical properties and systematic compilation of challenges necessary to provide the quality consistency of severely drawn filaments. The issue of thermomechanical processing trends is addressed as an important part of W-Re fabrication technology to achieve further improvement in design properties of rod and wire. (author)

  7. Stability characteristics of compressible boundary layers over thermo-mechanically compliant walls

    Science.gov (United States)

    Dettenrieder, Fabian; Bodony, Daniel

    2017-11-01

    Transition prediction at hypersonic flight conditions continues to be a challenge and results in conservative safety factors that increase vehicle weight. The weight and thus cost reduction of the outer skin panels promises significant impact; however, fluid-structure interaction due to unsteady perturbations in the laminar boundary layer regime has not been systematically studied at conditions relevant for reusable, hypersonic flight. In this talk, we develop and apply convective and global stability analyses for compressible boundary layers over thermo-mechanically compliant panels. This compliance is shown to change the convective stability of the boundary layer modes, with both stabilization and destabilization observed. Finite panel lengths are shown to affect the global stability properties of the boundary layer.

  8. Experimental simulation of irradiation effects on thermomechanical behaviour of UO2 fuel: Impact of solid and gaseous fission products

    International Nuclear Information System (INIS)

    Balland, J.

    2007-12-01

    Predictive simulation of thermomechanical behaviour of nuclear fuel has to take into account irradiation effects. Fission Products (FP) can modify the thermomechanical behaviour of UO 2 . During this thesis, differentiation was made between fission products which create a solid solution with UO 2 and gaseous products, generating pressurized bubbles. SIMFUELS containing gadolinium oxide and pressurized argon bubbles were manufactured, respectively by conventional process and by Gas Pressure Sintering. Brittle and ductile behaviour of UO 2 was investigated, under experimental conditions representative of Pellet-Cladding Interaction (PCI), respectively with 3 points bending tests and compressive creep tests. Investigation of brittle behaviour of UO 2 showed that fracture is mainly controlled by natural defects, like porosities, acting like starting points for cracks propagation. Addition of simulates fission products increase the brittle-to-ductile transition temperature of UO 2 , up to 400-500 C regarding FP in solid solution, and up to 200 C for gaseous products. Fission products although reduce fracture stresses, by a factor between 1.5 and 4, respectively for gas bubbles and solid solutions. Decrease of fracture stress is linked to an increase of microstructural defects due the solid solution and to pressurized bubbles located at grain boundaries. Pellets were tested under compressive solicitation at high temperatures. Experimental results of creep tests are well represented by Norton laws. Creep controlling mechanisms are evidenced by microstructural analysis performed on pellets at different strains. On the basis of calculations made for fuels having the same microstructures than the SIMFUELs, a creep factor is determined. It revealed a strong hardening effect of the solid solution, due to the fact that the added elements anchor the dislocations, whereas pressurized bubbles showed a coupling between hardening and softening effects. (author)

  9. Regional-scale geomechanical impact assessment of underground coal gasification by coupled 3D thermo-mechanical modeling

    Science.gov (United States)

    Otto, Christopher; Kempka, Thomas; Kapusta, Krzysztof; Stańczyk, Krzysztof

    2016-04-01

    Underground coal gasification (UCG) has the potential to increase the world-wide coal reserves by utilization of coal deposits not mineable by conventional methods. The UCG process involves combusting coal in situ to produce a high-calorific synthesis gas, which can be applied for electricity generation or chemical feedstock production. Apart from its high economic potentials, UCG may induce site-specific environmental impacts such as fault reactivation, induced seismicity and ground subsidence, potentially inducing groundwater pollution. Changes overburden hydraulic conductivity resulting from thermo-mechanical effects may introduce migration pathways for UCG contaminants. Due to the financial efforts associated with UCG field trials, numerical modeling has been an important methodology to study coupled processes considering UCG performance. Almost all previous UCG studies applied 1D or 2D models for that purpose, that do not allow to predict the performance of a commercial-scale UCG operation. Considering our previous findings, demonstrating that far-field models can be run at a higher computational efficiency by using temperature-independent thermo-mechanical parameters, representative coupled simulations based on complex 3D regional-scale models were employed in the present study. For that purpose, a coupled thermo-mechanical 3D model has been developed to investigate the environmental impacts of UCG based on a regional-scale of the Polish Wieczorek mine located in the Upper Silesian Coal Basin. The model size is 10 km × 10 km × 5 km with ten dipping lithological layers, a double fault and 25 UCG reactors. Six different numerical simulation scenarios were investigated, considering the transpressive stress regime present in that part of the Upper Silesian Coal Basin. Our simulation results demonstrate that the minimum distance between the UCG reactors is about the six-fold of the coal seam thickness to avoid hydraulic communication between the single UCG

  10. Inline temperature compensation for dimensional metrology of polymer parts in a production environment based on 3D thermomechanical analysis

    DEFF Research Database (Denmark)

    Sonne, M. R.; Gonzalez, D.; Costa, G. Dalla

    2018-01-01

    Abstract In the present work a new method for thermal compensation in dimensional metrology of polymer parts in a production environment based on 3D thermomechanical simulations is developed. A fixture for measuring the length dimension of a classical polymer part is placed in a production enviro...

  11. Thermomechanical processing of aluminum micro-alloyed with Sc, Zr, Ti, B, and C

    Science.gov (United States)

    McNamara, Cameron T.

    Critical exploration of the minimalistic high strength low alloy aluminum (HSLA-Al) paradigm is necessary for the continued development of advanced aluminum alloys. In this study, scandium (Sc) and zirconium (Zr) are examined as the main precipitation strengthening additions, while magnesium (Mg) is added to probe the synergistic effects of solution and precipitation hardening, as well as the grain refinement during solidification afforded by a moderate growth restriction factor. Further, pathways of recrystallization are explored in several potential HSLA-Al syste =ms sans Sc. Aluminum-titanium-boron (Al-Ti-B) and aluminum-titanium-carbon (Al-Ti-C) grain refining master alloys are added to a series of Al-Zr alloys to examine both the reported Zr poisoning effect on grain size reduction and the impact on recrystallization resistance through the use of electron backscattered diffraction (EBSD) imaging. Results include an analysis of active strengthening mechanisms and advisement for both constitution and thermomechanical processing of HSLA-Al alloys for wrought or near-net shape cast components. The mechanisms of recrystallization are discussed for alloys which contain a bimodal distribution of particles, some of which act as nucleation sites for grain formation during annealing and others which restrict the growth of the newly formed grains.

  12. Ash fusion and thermo-mechanical (TMA) analyses

    Energy Technology Data Exchange (ETDEWEB)

    Creelman, R.A. [R.A. Creelman and Associates, Epping, NSW (Australia)

    1996-10-01

    Various tests and analytical techniques are used to evaluate the potential of coals to foul and slag furnace surfaces. This paper compares three thermo-mechanical analyses (TMA) techniques, the Australian Coal Industry Research Laboratories (ACIRL) `Improved Ash Fusion` test, the HRL Technologies Pty Ltd test, and the Commonwealth Scientific and Industrial Research Organisation test. The ACIRL test appears to the contender for becoming a standard test that will replace the ash fusibility temperatures test (AFT). The series of events which produce a fused mass is outlined from observations in the course of an experiment conducted by ACARP. The paper concludes that results from tests based on TMA quantify the extent of shrinkage and indicate temperatures at which rapid shrinkage occurs and which correspond to the formation of liquid phases that can be identified on ternary phase diagrams. Temperatures corresponding to particular extents of shrinkage and the existence and extent of formation of these phases, as quantified by the magnitude of `peaks` in the TMA test, provide an alternative basis for defining ash fusibility temperatures. Shrinkage procedures provide alternatives to existing AFTs, as well as techniques for trouble-shooting problems in existing plant. (author). 1 fig., 10 refs.

  13. Electrical and Thermo-Mechanical properties of Irradiated Clay Nanoparticle/SBR Composites

    International Nuclear Information System (INIS)

    Ata, M.M.E.M.

    2011-01-01

    Polymer-Composites incorporating metal, semiconductors, Carbon black, nano materials and Clay materials have been widely used and studied as multifunctional materials with inherent polymer properties. Polymer-clay nano composites show remarkable property improvement when compared to conventionally scaled composites. For designing new materials with desirable, predicted properties, a better understanding of structure-property relationships is necessary. In this work, we employ dielectric relaxation spectroscopy (DRS) to investigate molecular mobility in relation to morphology in styrene butadiene rubber-SBR (treated and untreated) nano composites. In addition to the investigation of dipolar processes, special attention is paid here to the investigation of conductivity effects and mechanical as well as thermo-mechanical properties. From the stress-strain characteristics, one found that, all the compositions showed a tensile strength higher than the virgin rubber. By increasing the filler loading, the tensile strength of the prepared composites increases. The elongation at break for treated and untreated clay filed composites increases with an increase in filer loading up to 10 p hr and then followed by a decrease up to 15 p hr. The cross linking density, υ increases with both treated and untreated clay contents and treated samples have higher increasing rate of υ values than untreated one. To elucidate the tensile behavior of the test samples. The Ht model is tested by using non-Gaussian chain statistics, which give a good fitting with the experimental data.

  14. Regularities of texture formation in alloys undergoing phase transformations during heat treatment and plastic working

    International Nuclear Information System (INIS)

    Ageev, N.V.; Babarehko, A.A.

    1983-01-01

    Peculiarities of texture formation in metals undergoing phase transformations in the temperature range of heat treatment and hot working are investigated theoretically and experimentally. A low-temperature phase after hot working is shown to inherite a high-temperature phase texture due to definite orientation conformity during phase transformation. Strengthened heat and thermomechanical treatments, as a rule, do not destroy material texture but change it

  15. Two-Scale Modelling of Effects of Microstructure and Thermomechanical Properties on Dynamic Performance of an Aluminium Alloy

    Science.gov (United States)

    2010-09-01

    Influences of microstructure and properties of an aluminium alloy on resistance to dynamic perforation are predicted using a decoupled multiscale ... simulated performance. Library parameters typical for aluminium alloys (Kohn, 1969) are used for the macroscopic equation of state of Al 2139, details of...Two-Scale Modelling of Effects of Microstructure and Thermomechanical Properties on Dynamic Performance of an Aluminium Alloy by J. D

  16. Thermal, thermo-hydraulic and thermo-mechanic analysis for fuel elements of IEA-R1 reactor at 5MW

    International Nuclear Information System (INIS)

    Teixeira e Silva, A.; Silva Macedo, L.V. da

    1989-01-01

    In connection with the on going conversion of IEA-R1 Research Reactor, operated by IPEN-CNEN/SP, from the use of highly enriched uranium (HEU) fuel to the use of low enriched uranium (LEU) fuel, steady-state thermal and thermo-hydraulic analysis of both existing HEU and proposed LEU cores under 2 MW operating conditions have been carried out. Keeping in mind the possibility of power upgrading, steady-state thermal, thermo-hydraulic and thermomechanical analysis of proposed LEU core under 5 MW operating conditions have also been carried out. The thermal and thermo-hydraulic analysis at 2 MW show that the conversion of the existing HEU core to be proposed LEU core will not change the reactor safety margins. Although the upgrading of the reactor power to 5 MW will result in safety margins lower than in case of 2MW, these will be still sufficient for optimum operation and safe behaviour. The thermomechanical analysis at 5 MW show that the thermal stresses induced in the fuel element will satisfy the design limits for mechanical strenght and elastic stability. (author) [pt

  17. Thermomechanical treatment of starch

    NARCIS (Netherlands)

    Goot, van der A.J.; Einde, van den R.M.

    2006-01-01

    Starch is used as a major component in many food and nonfood applications and determines the overall product properties to a large extent. It is therefore important to understand the effect of processing on starch. Many starch-based products are produced using a thermal as well as a mechanical

  18. The effect of boron addition on microstructure and mechanical properties of biomedical Ti35Nb6Ta alloy

    Energy Technology Data Exchange (ETDEWEB)

    Málek, Jaroslav, E-mail: malek@ujp.cz [UJP PRAHA a.s., Nad Kamínkou 1345, 156 10 Prague, Zbraslav (Czech Republic); CTU in Prague, Faculty of Mechanical Engineering, Department of Materials Engineering, Karlovo Namesti 13, 121 35 Praha 2 (Czech Republic); Hnilica, František, E-mail: hnilica@ujp.cz [UJP PRAHA a.s., Nad Kamínkou 1345, 156 10 Prague, Zbraslav (Czech Republic); Veselý, Jaroslav, E-mail: vesely@ujp.cz [UJP PRAHA a.s., Nad Kamínkou 1345, 156 10 Prague, Zbraslav (Czech Republic); Smola, Bohumil, E-mail: smola@met.mff.cuni.cz [Charles University, Faculty of Mathematics and Physics, Ke Karlovu 5, 121 16 Prague 2 (Czech Republic); Březina, Vítězslav, E-mail: brezinavita@gmail.com [Masaryk University, Faculty of Medicine, Department of Stomathology, Komenského Náměstí 220/2, 662 43 Brno (Czech Republic); Kolařík, Kamil, E-mail: kamil.kolarik@email.cz [Faculty of Mechanical Engineering, University of West Bohemia, Univerzitní 22, 306 14 Plzeň (Czech Republic)

    2014-10-15

    The beta-titanium alloys are promising materials for bioapplications but their processing via melting is difficult. Coarse grains have been observed in as-cast specimens. Subsequent thermo-mechanical processing seems to be necessary in order to obtain fine-grained microstructure with better mechanical properties. The grain size can be decreased significantly by addition of small boron amount. In this work Ti–35Nb–6Ta alloy with various B additions (0, 0.05, 0.1, 0.3 and 0.5 wt.%) has been studied. Even the smallest amount of B leads to significant grain refinement in Ti–35Nb–6Ta alloy (from 1300 to about 350 μm). Slight grain refinement has been observed also after hot forging and solution treatment. TiB particles emerged in specimens due to B addition. These particles contribute to changes in mechanical properties not only in hot forged and solution treated specimens (hardness increase from 140 to 180 HV10), but also in cold swaged specimens (hardness from 230 to 250 HV10, tensile strength from 800 to 920 MPa). The hardness values can be increased up to 370 HV10 during aging at 400 °C (specimen with 0.5 wt.% B). It has been observed that specimens with low boron addition 0.05 wt.% possess no cytotoxicity. On the other hand in specimens with 0.1 wt.% B or more slight adverse effect on cytotoxicity has been observed. - Highlights: • The influence of boron on microstructure and mechanical properties has been studied. • Beta-transus temperature has been determined. • Cytotoxicity depending on boron content has been evaluated. • Possibility of final heat treatment has been determined.

  19. Evaluation of Thermal and Thermo-mechanical Behavior of Full-scale Energy Foundations

    Science.gov (United States)

    Murphy, Kyle D.

    This study focuses on the thermo-mechanical and thermal behavior of full-scale energy foundations installed as part of two buildings recently constructed in Colorado. The soil stratigraphy at each of the sites differed, but both foundations were expected to function as primarily end-bearing elements with a tip socketed into rock. The heat exchanger configurations were also different amongst the foundations at both sites, permitting evaluation of the role of heat exchange. A common thread for both energy foundation case histories was the monitoring of the temperature and axial strain within the foundations during heat exchange operations. The first case study involves an evaluation of the long-term thermo-mechanical response of two full-scale energy foundations installed at the new Denver Housing Authority (DHA) Senior Living Facility at 1099 Osage St. in Denver, Colorado. Due to the construction schedule for this project, the thermal properties of the foundations and surrounding subsurface could not be assessed using thermal response tests. However, instrumentation was incorporated into the foundations to assess their long-term heat exchange response as well as the thermo-mechanical strains, stresses, and displacements that occurred during construction and operation of the ground-source heat pump system. The temperature changes within the foundations during heating and cooling operations over a period of approximately 600 days ranged from 9 to 32 °C, respectively. The thermal axial stresses in the foundations were calculated from the measured strains, and ranged from 3.1 MPa during heating to --1.0 MPa during cooling. These values are within reasonable limits for reinforced concrete structures. The maximum thermal axial stress was observed near the toe of both foundations, which is consistent with trends expected for end-bearing toe boundary conditions. The greatest thermal axial strains were observed near the top of the foundations (upward expansion during

  20. Enhancing the ABAQUS Thermomechanics Code to Simulate Multidimensional Steady and Transient Fuel Rod Behavior

    Energy Technology Data Exchange (ETDEWEB)

    Williamson, R.L.; Knoll, D.A. [Idaho National Laboratory, PO Box 1625, Idaho Falls, ID 83415-3855 (United States)

    2009-06-15

    convective heat transfer boundary is applied to the clad outer wall. Energy generation in the fuel is specified using a spatially uniform volumetric fission rate. The analysis includes three time periods: an initial rise to power from ambient conditions, steady operation to a burnup of approximately 47 MWd/kgU, and then a power ramp and 12 hr hold. Results are presented at various stages of burnup during steady operation and then at the end of the power-ramp and hold. The 2D axisymmetric model permits an in-depth view of the evolving temperature and stress fields at the so called 'triple point', where the ends of two adjacent pellets contact the clad. Displacement and temperature results clearly demonstrate the importance of fully-coupled thermomechanics as the gap narrows and contact occurs. The clad axial stress in this region evolves from bending, during initial contact, to full tension, as the fuel and clad are mechanically coupled via friction and fuel swelling results in axial clad displacement. A plot of the clad radial displacement along the axial length shows initial uniform clad creep-down during steady operation, the effects of initial pellet-clad contact at the pellet ends (triple points), eventual full pellet/clad contact, and significant increased displacement during power ramping. The expected 'bamboo' profile along the clad length is clearly demonstrated. An important point is that ABAQUS implicit numeric and error-based time step control permits time step sizes ranging from less than 0.1 s, during power-up, to greater than 10 days, during steady operation. The code can easily accommodate combined steady and transient reactor operations. Results from a multiple pellet simulation demonstrate the importance of a multidimensional fully coupled thermomechanics treatment. Interestingly, many of the inherent deficiencies in existing codes are, in fact, ABAQUS strengths. (authors)

  1. Additional Treatments for High-Risk Obstetric Antiphospholipid Syndrome: a Comprehensive Review.

    Science.gov (United States)

    Ruffatti, Amelia; Hoxha, Ariela; Favaro, Maria; Tonello, Marta; Colpo, Anna; Cucchini, Umberto; Banzato, Alessandra; Pengo, Vittorio

    2017-08-01

    Most investigators currently advocate prophylactic-dose heparin plus low-dose aspirin as the preferred treatment of otherwise healthy women with obstetric antiphospholipid syndrome, whilst women with a history of vascular thrombosis alone or associated with pregnancy morbidity are usually treated with therapeutic heparin doses in association with low-dose aspirin in an attempt to prevent both thrombosis and pregnancy morbidity. However, the protocols outlined above fail in about 20 % of pregnant women with antiphospholipid syndrome. Identifying risk factors associated with pregnancy failure when conventional therapies are utilized is an important step in establishing guidelines to manage these high-risk patients. Some clinical and laboratory risk factors have been found to be related to maternal-foetal complications in pregnant women on conventional therapy. However, the most efficacious treatments to administer to high-risk antiphospholipid syndrome women in addition to conventional therapy in order to avoid pregnancy complications are as yet unestablished. This is a comprehensive review on this topic and an invitation to participate in a multicentre study in order to identify the best additional treatments to be used in this subset of antiphospholipid syndrome patients.

  2. Tee-junction of LMFR secondary circuit involving thermal, thermomechanical and fracture mechanics assessment on a striping phenomenon

    International Nuclear Information System (INIS)

    Lee, H.-Y.; Kim, J.-B.; Yoo, B.

    2002-01-01

    This paper presents the thermomechanical and fracture mechanics evaluation procedure of thermal striping damage on the secondary piping of LMFR using Green's function method and standard FEM. The thermohydraulic loading conditions used in the present analysis are simplified sinusoidal thermal loads and the random type thermal loads. The thermomechanical fatigue damage was evaluated according to ASME code subsection NH. The results of fatigue analysis for the sinusoidal and random type load cases showed that fatigue failure would occur at a welded joint during 90 000 hours of operation. The assessment for the fracture behavior of the welded joint showed that the crack would be initiated at an early stage of the operation. The fatigue crack was evaluated to propagate up to 5 mm along the thickness direction during the first 940.7 and 42 698.9 hours of operation for the sinusoidal and the random loading cases, respectively. However, it was evaluated that the crack would be arrested because of the low level of the primary stresses. The fatigue and crack propagation analyses for the random type loads were performed by Green's function method. (author)

  3. Thermo-mechanical fatigue behavior of the intermetallic gamma-TiAl alloy TNB-V5 with different microstructures

    Energy Technology Data Exchange (ETDEWEB)

    Roth, M [now at IAV GmbH, Kauffahrtei 25, D-09120 Chemnitz (Germany); Biermann, H, E-mail: marcel.roth@iav.d [TU Bergakademie Freiberg, Institute for Materials Engineering, Gustav-Zeuner-Strasse 5, D-09599 Freiberg (Germany)

    2010-07-01

    The cyclic deformation and fatigue behavior of the {gamma}-TiAl alloy TNB-V5 is studied under thermo-mechanical load for the three technically important microstructures Fully-Lamellar (FL), Near-Gamma (NG) and Duplex (DP), respectively. Thus, thermo-mechanical fatigue (TMF) tests were carried out with different temperature-strain cycles, different temperature ranges from 400{sup 0}C to 800{sup 0}C and with two different strain ranges. Cyclic deformation curves, stress-strain hysteresis loops and fatigue lives are presented. The type of microstructure shows a surprisingly small influence on the cyclic deformation and fatigue behavior under TMF conditions. For a general life prediction the damage parameter of Smith, Watson and Topper P{sub SWT} is well suitable, if the testing and the application temperature ranges, respectively, include temperatures above the ductile-brittle transition temperature (approx. 750{sup 0}C). If the maximum temperature is below that temperature, the brittle materials' behavior yields a high scatter of fatigue lives and a low slope of the fatigue life curve and therefore the damage parameter P{sub SWT} cannot be applied for the live prediction.

  4. Thermomechanical theory of materials undergoing large elastic and viscoplastic deformation (AWBA development program)

    International Nuclear Information System (INIS)

    Martin, S.E.; Newman, J.B.

    1980-11-01

    A thermomechanical theory of large deformation elastic-inelastic material behavior is developed which is based on a multiplicative decomposition of the strain. Very general assumptions are made for the elastic and inelastic constitutive relations and effects such as thermally-activated creep, fast-neutron-flux-induced creep and growth, annealing, and strain recovery are compatible with the theory. Reduced forms of the constitutive equations are derived by use of the second law of thermodynamics in the form of the Clausius-Duhem inequality. Observer invariant equations are derived by use of an invariance principle which is a generalization of the principle of material frame indifference

  5. Comparative Analysis of the Effects of Severe Plastic Deformation and Thermomechanical Training on the Functional Stability of Ti50.5Ni24.5Pd25 High-Temperature Shape Memory Alloy

    Science.gov (United States)

    Atli, K. C.; Karaman, I.; Noebe, R. D.; Maier, H. J.

    2010-01-01

    We compare the effectiveness of a conventional thermomechanical training procedure and severe plastic deformation via equal channel angular extrusion to achieve improved functional stability in a Ti50.5Ni24.5Pd25 high-temperature shape memory alloy. Thermomechanical testing indicates that both methods result in enhanced shape memory characteristics, such as reduced irrecoverable strain and thermal hysteresis. The mechanisms responsible for the improvements are discussed in light of microstructural findings from transmission electron microscopy.

  6. Far-field thermomechanical response of argillaceous rock to emplacement of a nuclear-waste repository

    International Nuclear Information System (INIS)

    McVey, D.F.; Thomas, R.K.; Lappin, A.R.

    1980-08-01

    Before heat-producing wastes can be emplaced safely in any argillaceous rock, it will be necessary to understand the far-field thermal and thermomechanical response of this rock to waste emplacement. This report presents the results of a first series of calculations aimed at estimating the far-field response of argillite to waste emplacement. Because the thermal and mechanical properties of argillite are affected by its content of expandable clay, its behavior is briefly compared and contrasted with that of a shale having the same matrix thermal properties, but containing no expandable clay. Under this assumption, modeled temperatures are the same for the two rock types at equivalent power densities and reflect the large dependence of in-situ temperatures on both initial power density and waste type. Thermomechanical calculations indicate that inclusion of contraction behavior of expandable clays in the assumed argillite thermal expansion behavior results, in some cases, in generation of a large zone in and near the repository that has undergone volumetric contraction but is surrounded by uniformly compressive stresses. Information available to date indicates that this contraction would likely result in locally increased fluid permeability and decreased in-situ thermal conductivity, but might well be advantageous as regards radionuclide retention, because of the increased surface area within the contracted zone. Assumption of continuous and positive expansion behavior for the shale eliminates the near-repository contraction and tensional zones, but results in near-surface tensional zones directly above the repository

  7. Mechanical properties of Fe3Al-based alloys with addition of carbon, niobium and titanium

    International Nuclear Information System (INIS)

    Zhang Zhengrong; Liu Wenxi

    2006-01-01

    Several Fe 3 Al-based iron aluminides with the addition of alloying elements carbon, niobium and titanium were produced by vacuum induction melting (VIM) and hot spinning forging. Analytic techniques including transmission electron microscopy (TEM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used in studying the microstructure and fracture manner of these alloys. The results show that due to the addition of alloying elements, the superlattice dislocations tend towards multiple slipping, leaving behind on their slip plane ribbons of square-shaped slip-induced antiphase boundaries. The elongation of Fe 3 Al in tension at room temperature increased to about 10% by the addition of suitable alloying elements, the usage of thermo-mechanical processing that has the function of refining grains and substructures, and subsequent annealing

  8. Gamma ray induced chromophore modification of softwood thermomechanical pulp

    International Nuclear Information System (INIS)

    Robert, S.; Daneault, C.; Viel, C.; Lepine, F.

    1992-01-01

    This study focuses on bleaching a softwood (black spruce, balsam fur) thermomechanical pulp with gamma rays. Gamma rays are known for their enormous penetrating power, along with their ionizing properties. They can generate highly energetic radicals capable of oxidizing lignin chromophores. The authors studied the influence of isopropyl alcohol, sodium borohydride, oxygen, hydrogen peroxide, nitrogen dioxide and water along with gamma ray irradiation of the pulps. The authors measured the optimal dose and dose rate, along with the influence of the radical scavengers like oxygen on the bleaching effect of gamma irradiated pulps. They observe various degrees of bleaching of these pulps. Evidence relates this bleaching to the generation of perhydroxyl anions upon irradiation of water. Also, they were able to pinpoint the influence of the dose rate on the rate of formation and disappearance of these perhydroxyl anions and their influence on bleaching kinetics. Stability toward photoyellowing, and photoyellowing's kinetic of papers from these pulps was also studied

  9. Mass transport in low permeability rocks under the influence of coupled thermomechanical and hydrochemical effects - an overview

    International Nuclear Information System (INIS)

    Tsang, C.F.

    1984-10-01

    The present paper gives a general overview of mass transport in low permeability rocks under the coupled thermomechanical and hydrochemical effects associated with a nuclear waste repository. A classification of coupled processes is given. Then an ess is presented. example of a coupled process is presented. Discussions of coupled processes based on a recent LBL Panel meeting are summarized. 5 references, 3 figures, 4 tables

  10. Thermo-mechanical analysis of high level nuclear wastes in granite

    International Nuclear Information System (INIS)

    Millard, A.; Guri, G.; Raimbault, M.

    1991-01-01

    In order to appraise the safety of a storage of high level nuclear wastes in rock masses, it is necessary to assess, among other features, the thermo-mechanical behaviour of the host rock for long periods (thousands of years). In France, four different media are considered as potential host rocks: granite, shale, salt, clay. The present paper is devoted to some analysis of a generic storage configuration in granite. The case of a rock mass without any major fault has been considered. The granite is modelled by means of an elastic fracturing model (no tension type). The results obtained show that some fissures, induced by the heat generation, develop mainly above the repository. The opening of the fissures, within the frame of the adopted hypothesis, have not a strong influence on the rock mass, as a geological barrier for the radionuclides. (author)

  11. Thermomechanical simulations and experimental validation for high speed incremental forming

    Science.gov (United States)

    Ambrogio, Giuseppina; Gagliardi, Francesco; Filice, Luigino; Romero, Natalia

    2016-10-01

    Incremental sheet forming (ISF) consists in deforming only a small region of the workspace through a punch driven by a NC machine. The drawback of this process is its slowness. In this study, a high speed variant has been investigated from both numerical and experimental points of view. The aim has been the design of a FEM model able to perform the material behavior during the high speed process by defining a thermomechanical model. An experimental campaign has been performed by a CNC lathe with high speed to test process feasibility. The first results have shown how the material presents the same performance than in conventional speed ISF and, in some cases, better material behavior due to the temperature increment. An accurate numerical simulation has been performed to investigate the material behavior during the high speed process confirming substantially experimental evidence.

  12. Short vegetal-fiber reinforced HDPE—A study of electron-beam radiation treatment effects on mechanical and morphological properties

    International Nuclear Information System (INIS)

    Ferreira, Maiara S.; Sartori, Mariana N.; Oliveira, Rene R.; Guven, Olgun; Moura, Esperidiana A.B.

    2014-01-01

    Graphical abstract: - Highlights: • HDPE reinforced with short piassava fiber composites were prepared by melt-mixing processing. • Glycidyl methacrylate (GMA) was tested as a radiation cross-linking agent. • The materials were irradiated with 100 and 200 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. • The better interfacial adhesion between fiber and HDPE matrix was observed for composites with GMA addition irradiated with radiation dose of 200 kGy. - Abstract: The effects of electron-beam radiation treatment on fiber-matrix adhesion and mechanical properties of short piassava fibers reinforced high density polyethylene (HDPE) matrix were studied. Glycidyl methacrylate (GMA) was added at 2.5% and 5.0% (on piassava fiber wt) as a cross-linking agent and the effects upon the properties of the resulting composites treated by electron-beam radiation were also examined. HDPE reinforced with short piassava fiber composites was prepared by melt-mixing processing, using a twin screw extruder machine. The materials were irradiated with 100 and 200 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. Material samples were submitted to mechanical and thermo-mechanical tests and SEM analyses. Correlation between properties was discussed. The comparison of mechanical and thermo-mechanical properties of the composites showed that electron-beam radiation treatment produced a significant improvement in mechanical properties, when compared with the non-irradiated composite sample and neat HDPE. Scanning electron microscopy (SEM) studies of the composite failure surfaces indicated that there was an improved adhesion between fiber and matrix. Examination of the failure surfaces indicated dependence of the interfacial adhesion upon the radiation dose and GMA content. Better interfacial adhesion between fiber and HDPE matrix was observed for composites with 5.0% GMA addition and treated with electron

  13. Short vegetal-fiber reinforced HDPE—A study of electron-beam radiation treatment effects on mechanical and morphological properties

    Energy Technology Data Exchange (ETDEWEB)

    Ferreira, Maiara S.; Sartori, Mariana N.; Oliveira, Rene R. [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes 2242, zip code 05508-000 São Paulo, SP (Brazil); Guven, Olgun [Hacettepe University, Department of Chemistry, Polymer Chemistry Division, Beytepe, zip code 06800 Ankara (Turkey); Moura, Esperidiana A.B., E-mail: eabmoura@ipen.br [Nuclear and Energy Research Institute, IPEN-CNEN/SP, Av. Prof. Lineu Prestes 2242, zip code 05508-000 São Paulo, SP (Brazil)

    2014-08-15

    Graphical abstract: - Highlights: • HDPE reinforced with short piassava fiber composites were prepared by melt-mixing processing. • Glycidyl methacrylate (GMA) was tested as a radiation cross-linking agent. • The materials were irradiated with 100 and 200 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. • The better interfacial adhesion between fiber and HDPE matrix was observed for composites with GMA addition irradiated with radiation dose of 200 kGy. - Abstract: The effects of electron-beam radiation treatment on fiber-matrix adhesion and mechanical properties of short piassava fibers reinforced high density polyethylene (HDPE) matrix were studied. Glycidyl methacrylate (GMA) was added at 2.5% and 5.0% (on piassava fiber wt) as a cross-linking agent and the effects upon the properties of the resulting composites treated by electron-beam radiation were also examined. HDPE reinforced with short piassava fiber composites was prepared by melt-mixing processing, using a twin screw extruder machine. The materials were irradiated with 100 and 200 kGy using a 1.5 MeV electron beam accelerator, at room temperature in presence of air. Material samples were submitted to mechanical and thermo-mechanical tests and SEM analyses. Correlation between properties was discussed. The comparison of mechanical and thermo-mechanical properties of the composites showed that electron-beam radiation treatment produced a significant improvement in mechanical properties, when compared with the non-irradiated composite sample and neat HDPE. Scanning electron microscopy (SEM) studies of the composite failure surfaces indicated that there was an improved adhesion between fiber and matrix. Examination of the failure surfaces indicated dependence of the interfacial adhesion upon the radiation dose and GMA content. Better interfacial adhesion between fiber and HDPE matrix was observed for composites with 5.0% GMA addition and treated with electron

  14. Review on effect of chemical, thermal, additive treatment on mechanical properties of basalt fiber and their composites

    Science.gov (United States)

    Jain, Naman; Singh, Vinay Kumar; Chauhan, Sakshi

    2017-12-01

    Basalt fiber is emerging out the new reinforcing material for composites. To overcome some of the disadvantages of fibers such as poor bonding to polymers, low thermal stability and high moisture absorption fiber characteristics are modified with chemical, thermal and additive treatments. Chemical treatment corrosive resistance to alkali and acid were investigated which were used to clean and modify the surface of fiber for higher bonding with resins. To improve the thermal stability and reduce moisture uptake thermal treatment such as plasma and non thermal plasma were used which increased the surface roughness and change the chemical composition of surface of basalt fiber. Additive treatment is used to improve the mechanical properties of fibers, in basalt fiber additive treatment was done with SiO2 additive because of its chemical composition which contains major content of SiO2. In present investigation review on the effect of different treatment such as chemical, thermal and additive were studied. Effect of these treatment on chemical composition of the surface of basalt fiber and corrosion to acidic and alkali solution were studied with their effect on mechanical properties of basalt fiber and their composite.

  15. PIN99W, Modelling of VVER and PWR Fuel Rod Thermomechanical Behaviour

    International Nuclear Information System (INIS)

    Valach, M.; Strizhov, P.; Svoboda, R.

    2000-01-01

    1 - Description of program or function: The Code is developed to describe fuel rod thermomechanical behaviour in operational conditions. The main goal of this code is to calculate fuel temperature, gap conductivity, fission gas release and inner gas pressure. 2 - Methods: - fuel rod temperature response is solved by using one-dimensional finite element method combined with weighted residuals method; - the code involves models describing physical phenomena typical for the fuel irradiated in Light Water Power Reactors (densification, restructuring, fission gas release, swelling and relocation) ; - this code is updated and improves PIN-micro code. 3 - Restrictions on the complexity of the problem: - simplified mechanistic solution; - only steady-state solution; - no cladding failure criterion; - no model for axial fuel-cladding interaction

  16. Correlation between some thermo-mechanical and physico-chemical properties in multi-component glasses of Se-Te-Sn-Cd system

    Science.gov (United States)

    Kumar, Amit; Mehta, Neeraj

    2017-06-01

    The glass transition phenomenon is guided by the swift cooling of a melt (glass-forming liquid). Consequently, the glass as a final product consists of a considerable number of micro-voids having the size of the order of atomic and/or molecular sizes. The model of free volume fluctuation helps in describing the diverse physico-chemical properties of amorphous materials (like glasses and polymers). This theory is based on the fraction of fluctuation free frozen at the glass transition temperature and it forms a basis for determination of various significant thermo-mechanical properties. In the present work, Vickers hardness test method is employed that provides useful information concerning the mechanical behavior of brittle solids. The present work emphasizes the results of micro-indentation measurements on recently synthesized novel Se78- x Te20Sn2Cd x glassy system. Basic thermo-mechanical parameters such as micro-hardness, volume ( V h), formation energy ( E h) of micro-voids in the glassy network and modulus of elasticity ( E) have been determined and their variation with glass composition has been investigated.

  17. Correlation between some thermo-mechanical and physico-chemical properties in multi-component glasses of Se-Te-Sn-Cd system

    International Nuclear Information System (INIS)

    Kumar, Amit; Mehta, Neeraj

    2017-01-01

    The glass transition phenomenon is guided by the swift cooling of a melt (glass-forming liquid). Consequently, the glass as a final product consists of a considerable number of micro-voids having the size of the order of atomic and/or molecular sizes. The model of free volume fluctuation helps in describing the diverse physico-chemical properties of amorphous materials (like glasses and polymers). This theory is based on the fraction of fluctuation free frozen at the glass transition temperature and it forms a basis for determination of various significant thermo-mechanical properties. In the present work, Vickers hardness test method is employed that provides useful information concerning the mechanical behavior of brittle solids. The present work emphasizes the results of micro-indentation measurements on recently synthesized novel Se_7_8_-_xTe_2_0Sn_2Cd_x glassy system. Basic thermo-mechanical parameters such as micro-hardness, volume (V_h), formation energy (E_h) of micro-voids in the glassy network and modulus of elasticity (E) have been determined and their variation with glass composition has been investigated. (orig.)

  18. Thermo-mechanical properties improvement of asphalt binder by using methylmethacrylate/ethylene glycol dimethacrylate

    Directory of Open Access Journals (Sweden)

    A.A. Ragab

    2016-09-01

    Full Text Available Various polymer-modified asphalt compositions for paving and roofing applications are known since several years ago. The degree to which a polymer improves the asphalt’s properties depends on the compatibility of the polymer and the asphalt. Highly compatible polymers are more effective in providing property improvements. In this research, the influence of in situ polymerization of methylmethacrylate monomer with asphalt in presence of ethylene glycol dimethacrylate (EGDM as a crosslinker on the rheological and thermal properties of asphalt binder of type penetration grade 60/70 was studied. To achieve this aim, MMA/EGDM(MC in different ratios as 5, 10 and 15% (w/w were used to modify the thermo-mechanical properties of asphalt via forming chemical bond, and the changing in mechanical and thermal properties, of the mixes as well as the storage stability were studied. Also, the morphology (SEM, thermal characterization (TGA, dynamic mechanical analysis (DMA, bending and rheological tests were detected. The obtained experimental results revealed that the addition of MC causes both the rheological and thermal properties of the binder to improve and the prepared PMAs has high temperature susceptibility and low curing time. The improvement in the properties of the virgin asphalt will be effective in using this soft type in coating applications instead of highly expensive oxidized one.

  19. The Effect of Thermo-mechanical Processing on the Ballistic Limit Velocity of Extra Low Interstitial Titanium Alloy Ti-6AL- 4V

    National Research Council Canada - National Science Library

    Burkins, Matthew

    2000-01-01

    .... Department of Energy's Albany Research Center (ARC) performed a joint research program to evaluate the effect of thermo-mechanical processing on the ballistic limit velocity for an extra-low interstitial grade of the titanium alloy Ti-6Al-4V...

  20. Thermo-mechanical simulation and parameters optimization for beam blank continuous casting

    International Nuclear Information System (INIS)

    Chen, W.; Zhang, Y.Z.; Zhang, C.J.; Zhu, L.G.; Lu, W.G.; Wang, B.X.; Ma, J.H.

    2009-01-01

    The objective of this work is to optimize the process parameters of beam blank continuous casting in order to ensure high quality and productivity. A transient thermo-mechanical finite element model is developed to compute the temperature and stress profile in beam blank continuous casting. By comparing the calculated data with the metallurgical constraints, the key factors causing defects of beam blank can be found out. Then based on the subproblem approximation method, an optimization program is developed to search out the optimum cooling parameters. Those optimum parameters can make it possible to run the caster at its maximum productivity, minimum cost and to reduce the defects. Now, online verifying of this optimization project has been put in practice, which can prove that it is very useful to control the actual production

  1. Thermo-mechanical fatigue behavior of reduced activation ferrite/martensite stainless steels

    International Nuclear Information System (INIS)

    Petersen, C.; Rodrian, D.

    2002-01-01

    The thermo-mechanical cycling fatigue (TMCF) behavior of reduced activation ferrite/martensite stainless steels is examined. The test rig consists of a stiff load frame, which is directly heated by the digitally controlled ohmic heating device. Cylindrical specimens are used with a wall thickness of 0.4 mm. Variable strain rates are applied at TMCF test mode, due to the constant heating rate of 5.8 K/s and variable temperature changes. TMCF results of as received EUROFER 97 in the temperature range between 100 and 500-600 deg. C show a reduction in life time (a factor of 2) compared to F82H mod. and OPTIFER IV. TMCF-experiments with hold times of 100 and 1000 s show dramatic reduction in life time for all three materials

  2. Thermo-Mechanical tests for the CLIC two-beam module study

    CERN Document Server

    Xydou, A; Riddone, G; Daskalaki, E

    2014-01-01

    The luminosity goal of CLIC requires micron level precision with respect to the alignment of the components on its two-meter long modules, composing the two main linacs. The power dissipated inside the module components introduces mechanical deformations affecting their alignment and therefore the resulting machine performance. Several two-beam prototype modules must be assembled to extensively measure their thermo-mechanical behavior under different operation modes. In parallel, the real environmental conditions present in the CLIC tunnel should be studied. The air conditioning and ventilation system providing specified air temperature and flow has been installed in the dedicated laboratory. The power dissipation occurring in the modules is being reproduced by the electrical heaters inserted inside the RF structure mock-ups and the quadrupoles. The efficiency of the cooling systems is being verified and the alignment of module components is monitored. The measurement results will be compared to finite elemen...

  3. Thermo-mechanical analysis of an acceleration grid for the international thermonuclear experimental reactor-neutral beam injection system

    International Nuclear Information System (INIS)

    Fujiwara, Yukio; Hanada, Masaya; Okumura, Yoshikazu; Suzuki, Satoshi; Watanabe, Kazuhiro

    2001-01-01

    In the engineering design of a negative-ion beam source for a high-power neutral beam injection (NBI) system, one of the most important issues is thermo-mechanical design of acceleration grids for producing several tens of MW ion beams. An acceleration grid for the international thermonuclear experimental reactor-neutral beam injection (ITER-NBI) system will be subjected to the heat loading as high as 1.5 MW. In the present paper, thermo-mechanical characteristics of the acceleration grid for the ITER-NBI system were analyzed. Numerical simulation indicated that maximum aperture-axis displacement of the acceleration grid due to thermal expansion would be about 0.7 mm for the heat loading of 1.5 MW. From the thin lens theory of beam optics, beamlet deflection angle by the aperture-axis displacement was estimated to be about 2 mrad, which is within the requirement of the engineering design of the ITER-NBI system. Numerical simulation also indicated that no melting on the acceleration grid would occur for a heat loading of 1.5 MW, while local plastic deformation would happen. To avoid the plastic deformation, it is necessary to reduce the heat loading onto the acceleration grid to less than 1 MW

  4. Thermo-Mechanical Fatigue Crack Growth of RR1000.

    Science.gov (United States)

    Pretty, Christopher John; Whitaker, Mark Thomas; Williams, Steve John

    2017-01-04

    Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF) evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP) testing produces accelerated crack growth rates compared with out-of-phase (OOP) due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles.

  5. Thermo-Mechanical Fatigue Crack Growth of RR1000

    Directory of Open Access Journals (Sweden)

    Christopher John Pretty

    2017-01-01

    Full Text Available Non-isothermal conditions during flight cycles have long led to the requirement for thermo-mechanical fatigue (TMF evaluation of aerospace materials. However, the increased temperatures within the gas turbine engine have meant that the requirements for TMF testing now extend to disc alloys along with blade materials. As such, fatigue crack growth rates are required to be evaluated under non-isothermal conditions along with the development of a detailed understanding of related failure mechanisms. In the current work, a TMF crack growth testing method has been developed utilising induction heating and direct current potential drop techniques for polycrystalline nickel-based superalloys, such as RR1000. Results have shown that in-phase (IP testing produces accelerated crack growth rates compared with out-of-phase (OOP due to increased temperature at peak stress and therefore increased time dependent crack growth. The ordering of the crack growth rates is supported by detailed fractographic analysis which shows intergranular crack growth in IP test specimens, and transgranular crack growth in 90° OOP and 180° OOP tests. Isothermal tests have also been carried out for comparison of crack growth rates at the point of peak stress in the TMF cycles.

  6. A fast-track preliminary thermo-mechanical design of oil export pipelines from P-56 platform

    Energy Technology Data Exchange (ETDEWEB)

    Solano, Rafael F.; Mendonca, Salete M. de [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil); Franco, Luciano D.; Walker, Alastair; El-Gebaly, Sherif H. [INTECSEA, Rio de Janeiro, RJ (Brazil)

    2009-12-19

    The oil export pipelines of Marlim Sul field Module 3, Campus Basin, offshore Brazil, will operate in high pressure and temperature conditions, and will be laid on seabed crossing ten previously laid pipelines along the routes. In terms of thermo-mechanical design, these conditions turn out to be great challenges. In order to obtain initial results and recommendations for detail design, a preliminary thermo-mechanical design of pipelines was carried out as a fast-track design before the bid. This way, PETROBRAS can assess and emphasize the susceptibility of these lines to lateral buckling and pipeline walking behavior. Therefore, PETROBRAS can present a preliminary mitigation strategy for lateral buckling showing solutions based on displacement controlled criteria and by introducing buckle initiation along the pipeline using distribution buoyancy. Besides that, axial displacements and loads at the pipeline ends can be furnished also in order to provide a basis for the detailed design. The work reported in this paper follows the SAFEBUCK JIP methodology and recommendation, which were used to determine the allowable strain and maximum allowable VAS (Virtual Anchor Spacing) considered in the buckling mitigation strategy. The paper presents also the formation of uncontrolled buckles on the seabed and the propensity for pipeline walking in its sections between buckles. The buckling mitigation strategy established in this preliminary design confirms that the oil pipeline specifications are adequate to maintain integrity during design life. (author)

  7. A mesoscopic thermomechanically coupled model for thin-film shape-memory alloys by dimension reduction and scale transition

    Czech Academy of Sciences Publication Activity Database

    Benešová, B.; Kružík, Martin; Pathó, G.

    2014-01-01

    Roč. 26, č. 5 (2014), s. 683-713 ISSN 0935-1175 R&D Projects: GA ČR GAP201/10/0357; GA ČR(CZ) GAP201/12/0671 Grant - others:GA ČR(CZ) GAP105/11/0411 Institutional support: RVO:67985556 Keywords : Dimension reduction problems · * Parametrized measures * Thermomechanics Subject RIV: BA - General Mathematics Impact factor: 1.779, year: 2014 http://library.utia.cas.cz/separaty/2014/MTR/kruzik-0439681.pdf

  8. Shape distortion and thermo-mechanical properties of SOFC components from green tape to sintering body

    DEFF Research Database (Denmark)

    Teocoli, Francesca; Ni, De Wei; Tadesse Molla, Tesfaye

    due to binder burn out, differential shrinkage behavior and to a potential interfacial reaction between the two materials. To analyze the phenomena, shrinkage of SOFC components single layers and bilayered samples were measured insitu by optical dilatometer. The densification mismatch stress, due...... to the strain rate difference between materials, was calculated using Cai’s model. Camber (curvature) development for in situ co-firing of a bi-layer ceramic green tape has been investigated. Analysis of shape evolution from green to sintered body can be carried out by the thermo-mechanical analysis techniques....

  9. A numerical study of crack interactions under thermo-mechanical load using EFGM

    International Nuclear Information System (INIS)

    Pant, Mohit; Singh, I. V.; Mishra, B. K.

    2011-01-01

    In this work, element free Galerkin method (EFGM) has been used to obtain the solution of various edge crack problems under thermo-mechanical loads as it provides a versatile technique to model stationary as well as moving crack problems without re-meshing. Standard diffraction criterion has been modified with multiple crack weight technique to characterize the presence of various cracks in the domain of influence of a particular node. The effect of crack inclination has been studied for single as well as two edge cracks, whereas the cracks interaction has been studied for two edge cracks lying on same as well as opposite edges under plane stress conditions. The values of mode-I and mode-II stress intensity factors have been evaluated by the interaction integral approach

  10. Thermophysical and Thermomechanical Properties of Thermal Barrier Coating Systems

    Science.gov (United States)

    Zhu, Dongming; Miller, Robert A.

    2000-01-01

    Thermal barrier coatings have been developed for advanced gas turbine and diesel engine applications to improve engine reliability and fuel efficiency. However, the issue of coating durability under high temperature cyclic conditions is still of major concern. The coating failure is closely related to thermal stresses and oxidation in the coating systems. Coating shrinkage cracking resulting from ceramic sintering and creep at high temperatures can further accelerate the coating failure process. The purpose of this paper is to address critical issues such as ceramic sintering and creep, thermal fatigue and their relevance to coating life prediction. Novel test approaches have been established to obtain critical thermophysical and thermomechanical properties of the coating systems under near-realistic temperature and stress gradients encountered in advanced engine systems. Emphasis is placed on the dynamic changes of the coating thermal conductivity and elastic modulus, fatigue and creep interactions, and resulting failure mechanisms during the simulated engine tests. Detailed experimental and modeling results describing processes occurring in the thermal barrier coating systems provide a framework for developing strategies to manage ceramic coating architecture, microstructure and properties.

  11. Strain-rate dependent plasticity in thermo-mechanical transient analysis

    International Nuclear Information System (INIS)

    Rashid, Y.R.; Sharabi, M.N.

    1980-01-01

    The thermo-mechanical transient behavior of fuel element cladding and other reactor components is generally governed by the strain-rate properties of the material. Relevant constitutive modeling requires extensive material data in the form of strain-rate response as function of true-stress, temperature, time and environmental conditions, which can then be fitted within a theoretical framework of an inelastic constitutive model. In this paper, we present a constitutive formulation that deals continuously with the entire strain-rate range and has the desirable advantage of utilizing existing material data. The derivation makes use of strain-rate sensitive stress-strain curve and strain-rate dependent yield surface. By postulating a strain-rate dependent on Mises yield function and a strain-rate dependent kinematic hardening rule, we are able to derive incremental stress-strain relations that describe the strain-rate behavior in the entire deformation range spanning high strain-rate plasticity and creep. The model is sufficiently general as to apply to any materials and loading histories for which data is available. (orig.)

  12. Influence of different hydrocolloids on dough thermo-mechanical properties and in vitro starch digestibility of gluten-free steamed bread based on potato flour.

    Science.gov (United States)

    Liu, Xingli; Mu, Taihua; Sun, Hongnan; Zhang, Miao; Chen, Jingwang; Fauconnier, Marie Laure

    2018-01-15

    The effects of hydrocolloids (hydroxypropylmethylcellulose (HPMC), Carboxymethylcellulose (CMC), xanthan gum (XG), and apple pectin (AP)) at different concentrations on dough thermo-mechanical properties and in vitro starch digestibility of gluten-free potato steamed bread were investigated. Results showed that hydrocolloids addition significantly increased the gelatinization temperature (from 52.0 to 64.2°C) and water absorption (from 56.22 to 66.50%) of potato dough. Moreover, hydrocolloids may be interacted with protein and starch, the density of potato protein bands was decreased by hydrocolloids addition, the reason might be that higher molecular weight complexes might be formed between proteins-hydrocolloids or proteins-proteins, thus change the protein solubility. Furthermore, steamed breads with hydrocolloids presented higher specific volume and lower hardness, and the rapidly digestible starch and estimated glycemic index were significantly decreased from 45.51 to 20.64, from 69.54 to 55.17, respectively. In conclusion, HPMC and XG could be used as improvers in the gluten-free potato steamed bread. Copyright © 2017. Published by Elsevier Ltd.

  13. A general procedure for thermomechanical calibration of nano/micro-mechanical resonators

    International Nuclear Information System (INIS)

    Hauer, B.D.; Doolin, C.; Beach, K.S.D.; Davis, J.P.

    2013-01-01

    We describe a general procedure to calibrate the detection of a nano/micro-mechanical resonator’s displacement as it undergoes thermal Brownian motion. A brief introduction to the equations of motion for such a resonator is presented, followed by a detailed derivation of the corresponding power spectral density (PSD) function, which is identical in all situations aside from a system-dependent effective mass value. The effective masses for a number of different resonator geometries are determined using both finite element method (FEM) modeling and analytical calculations. -- Highlights: •Model micro- and nanomechanical resonators displaced by their own thermal motion. •Review the theoretical framework for describing thermomechanical systems. •Present a recipe for measurement calibration on devices of arbitrary shape. •Point out and correct inconsistencies in the existing literature. •Provide an authoritative guide and reference for practitioners in this area

  14. A general procedure for thermomechanical calibration of nano/micro-mechanical resonators

    Energy Technology Data Exchange (ETDEWEB)

    Hauer, B.D., E-mail: bhauer@ualberta.ca; Doolin, C.; Beach, K.S.D., E-mail: kbeach@ualberta.ca; Davis, J.P., E-mail: jdavis@ualberta.ca

    2013-12-15

    We describe a general procedure to calibrate the detection of a nano/micro-mechanical resonator’s displacement as it undergoes thermal Brownian motion. A brief introduction to the equations of motion for such a resonator is presented, followed by a detailed derivation of the corresponding power spectral density (PSD) function, which is identical in all situations aside from a system-dependent effective mass value. The effective masses for a number of different resonator geometries are determined using both finite element method (FEM) modeling and analytical calculations. -- Highlights: •Model micro- and nanomechanical resonators displaced by their own thermal motion. •Review the theoretical framework for describing thermomechanical systems. •Present a recipe for measurement calibration on devices of arbitrary shape. •Point out and correct inconsistencies in the existing literature. •Provide an authoritative guide and reference for practitioners in this area.

  15. Thermomechanical behavior of a two-way shape memory composite actuator

    International Nuclear Information System (INIS)

    Ge, Qi; Westbrook, Kristofer K; Dunn, Martin L; Jerry Qi, H; Mather, Patrick T

    2013-01-01

    Shape memory polymers (SMPs) are a class of smart materials that can fix a temporary shape and recover to their permanent (original) shape in response to an environmental stimulus such as heat, electricity, or irradiation, among others. Most SMPs developed in the past can only demonstrate the so-called one-way shape memory effect; i.e., one programming step can only yield one shape memory cycle. Recently, one of the authors (Mather) developed a SMP that exhibits both one-way shape memory (1W-SM) and two-way shape memory (2W-SM) effects (with the assistance of an external load). This SMP was further used to develop a free-standing composite actuator with a nonlinear reversible actuation under thermal cycling. In this paper, a theoretical model for the PCO SMP based composite actuator was developed to investigate its thermomechanical behavior and the mechanisms for the observed phenomena during the actuation cycles, and to provide insight into how to improve the design. (paper)

  16. Effect of thermo-mechanical refining pressure on the properties of wood fibers as measured by nanoindentation and atomic force microscopy

    Science.gov (United States)

    Cheng Xing; Siqun Wang; George M. Pharr; Leslie H. Groom

    2008-01-01

    Refined wood fibers of a 54-year-old loblolly pine (Pinus taeda L.) mature wood were investigated by nanoindentation and atomic force microscopy (AFM). The effect of steam pressure, in the range of 2?18 bar, during thermomechanical refining was investigated and the nanomechanical properties and nano- or micro-level damages of the cell wall were...

  17. Commercial alkaline earth boroaluminosilicate glasses for sealing solid oxide cell stacks. Part I: Development of glass-ceramic microstructure and thermomechanical properties

    DEFF Research Database (Denmark)

    Agersted, Karsten; Balic-Zunic, Tonci

    2018-01-01

    Sealing performance in solid oxide cell (SOC) stacks and the devitrification process of commercially available alkaline earth boroaluminosilicate glasses containing 48‐61 mol% SiO2, 18‐28 mol% CaO, 1‐7 mol% MgO, 7‐10 mol% Al2O3, 1‐11 mol% B2O3 plus minor amounts of Na2O, K2O, FeO, and TiO2 were...... investigated and quantified through analysis of phase assemblages as function of heat treatments above the glass transition temperatures using the electron microprobe and powder X‐ray diffraction. For two of these glasses devitrification behavior was compared to the devitrification behavior of similar glasses...... produced in the laboratory. Glasses were characterized after annealing in air at 800°C and 850°C for up to 6 weeks. Even though the glasses lie within a relatively narrow compositional range, sealing performance and the resulting microstructures differed significantly. Best thermomechanical properties...

  18. Correlation between some thermo-mechanical and physico-chemical properties in multi-component glasses of Se-Te-Sn-Cd system

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Amit; Mehta, Neeraj [Banaras Hindu University, Department of Physics, Institute of Science, Varanasi (India)

    2017-06-15

    The glass transition phenomenon is guided by the swift cooling of a melt (glass-forming liquid). Consequently, the glass as a final product consists of a considerable number of micro-voids having the size of the order of atomic and/or molecular sizes. The model of free volume fluctuation helps in describing the diverse physico-chemical properties of amorphous materials (like glasses and polymers). This theory is based on the fraction of fluctuation free frozen at the glass transition temperature and it forms a basis for determination of various significant thermo-mechanical properties. In the present work, Vickers hardness test method is employed that provides useful information concerning the mechanical behavior of brittle solids. The present work emphasizes the results of micro-indentation measurements on recently synthesized novel Se{sub 78-x}Te{sub 20}Sn{sub 2}Cd{sub x} glassy system. Basic thermo-mechanical parameters such as micro-hardness, volume (V{sub h}), formation energy (E{sub h}) of micro-voids in the glassy network and modulus of elasticity (E) have been determined and their variation with glass composition has been investigated. (orig.)

  19. Physical, structural and thermomechanical properties of oil palm nano filler/kenaf/epoxy hybrid nanocomposites

    Energy Technology Data Exchange (ETDEWEB)

    Saba, N., E-mail: naheedchem@gmail.com [Laboratory of Biocomposite Technology, Institute of Tropical Forestry and Forest Products(INTROP), Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia); Paridah, M.T. [Laboratory of Biocomposite Technology, Institute of Tropical Forestry and Forest Products(INTROP), Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia); Abdan, K. [Department of Biological and Agricultural Engineering, Faculty of Engineering, Universiti Putra Malaysia, 43400 UPM Serdang Selangor (Malaysia); Ibrahim, N.A. [Department of Chemistry, Faculty of Science, Universiti Putra Malaysia, 43400 UPM Serdang, Selangor (Malaysia)

    2016-12-01

    The present research study deals with the fabrication of kenaf/epoxy hybrid nanocomposites by the incorporation of oil palm nano filler, montmorillonite (MMT) and organically modified montmorillonite (OMMT) at 3% loading, through hand lay-up technique. Effect of adding different nano fillers on the physical (density), structural [X-ray diffraction (XRD)] and thermomechanical analysis (TMA) of kenaf/epoxy composites were carried out. Density results revealed that the incorporation of nano filler in the kenaf/epoxy composites increases the density which in turn increases the hardness of the hybrid nanocomposites. XRD analysis confirmed the presence of nano fillers in the structure of their respective fabricated hybrid nanocomposites. All hybrid nanocomposites displayed lower coefficient of thermal expansion (CTE) with respect to kenaf/epoxy composites. Overall results predicted that the properties improvement in nano OPEFB/kenaf/epoxy was quite comparable to MMT/kenaf/epoxy but relatively lesser to OMMT/kenaf/epoxy hybrid nanocomposites and higher with respect to kenaf/epoxy composites. The improvement ascribed due to improved interfacial bonding or cross linking between kenaf fibers and epoxy matrix by addition of nano filler. - Highlights: • Nano OPEFB/kenaf/epoxy hybrid nanocomposites were fabricated by hand lay-up. • Effect of nano OPEFB on density & structure of kenaf/epoxy were investigated. • Thermal expansion coefficients of kenaf/epoxy and hybrid nanocomposites evaluated. • Comparative studies were made with MMT and OMMT kenaf/epoxy hybrid nanocomposites.

  20. Physical, structural and thermomechanical properties of oil palm nano filler/kenaf/epoxy hybrid nanocomposites

    International Nuclear Information System (INIS)

    Saba, N.; Paridah, M.T.; Abdan, K.; Ibrahim, N.A.

    2016-01-01

    The present research study deals with the fabrication of kenaf/epoxy hybrid nanocomposites by the incorporation of oil palm nano filler, montmorillonite (MMT) and organically modified montmorillonite (OMMT) at 3% loading, through hand lay-up technique. Effect of adding different nano fillers on the physical (density), structural [X-ray diffraction (XRD)] and thermomechanical analysis (TMA) of kenaf/epoxy composites were carried out. Density results revealed that the incorporation of nano filler in the kenaf/epoxy composites increases the density which in turn increases the hardness of the hybrid nanocomposites. XRD analysis confirmed the presence of nano fillers in the structure of their respective fabricated hybrid nanocomposites. All hybrid nanocomposites displayed lower coefficient of thermal expansion (CTE) with respect to kenaf/epoxy composites. Overall results predicted that the properties improvement in nano OPEFB/kenaf/epoxy was quite comparable to MMT/kenaf/epoxy but relatively lesser to OMMT/kenaf/epoxy hybrid nanocomposites and higher with respect to kenaf/epoxy composites. The improvement ascribed due to improved interfacial bonding or cross linking between kenaf fibers and epoxy matrix by addition of nano filler. - Highlights: • Nano OPEFB/kenaf/epoxy hybrid nanocomposites were fabricated by hand lay-up. • Effect of nano OPEFB on density & structure of kenaf/epoxy were investigated. • Thermal expansion coefficients of kenaf/epoxy and hybrid nanocomposites evaluated. • Comparative studies were made with MMT and OMMT kenaf/epoxy hybrid nanocomposites.

  1. Stress state of main stop valve with 500 mm nominal diameter white thermomechanical loading

    International Nuclear Information System (INIS)

    Koklyuev, G.A.; Plotnikov, V.P.

    1987-01-01

    The method of finite elements was applied to calculate the stress-strain state of the main isolation valve case with 500 mm nominal diameter while thermomechanical loading. Maximum stress takes place in the zone of joining nozzles with a spherical case and it attains the value of 138 MPa at working pressure of 12.5 MPa. The stress level in the point of nozzle-case welding is essentially lower than in zones of stres concentration and when excluding water hitting the slot of the lack of fusion in the route of the weld the weld service life is attained during the calculated service life

  2. Thermo-mechanical Properties of Upper Jurassic (Malm) Carbonate Rock Under Drained Conditions

    Science.gov (United States)

    Pei, Liang; Blöcher, Guido; Milsch, Harald; Zimmermann, Günter; Sass, Ingo; Huenges, Ernst

    2018-01-01

    The present study aims to quantify the thermo-mechanical properties of Neuburger Bankkalk limestone, an outcrop analog of the Upper Jurassic carbonate formation (Germany), and to provide a reference for reservoir rock deformation within future enhanced geothermal systems located in the Southern German Molasse Basin. Experiments deriving the drained bulk compressibility C were performed by cycling confining pressure p c between 2 and 50 MPa at a constant pore pressure p p of 0.5 MPa after heating the samples to defined temperatures between 30 and 90 °C. Creep strain was then measured after each loading and unloading stage, and permeability k was obtained after each creep strain measurement. The drained bulk compressibility increased with increasing temperature and decreased with increasing differential pressure p d = p c - p p showing hysteresis between the loading and unloading stages above 30 °C. The apparent values of the indirectly calculated Biot coefficient α ind containing contributions from inelastic deformation displayed the same temperature and pressure dependencies. The permeability k increased immediately after heating and the creep rates were also temperature dependent. It is inferred that the alteration of the void space caused by temperature changes leads to the variation of rock properties measured under isothermal conditions while the load cycles applied under isothermal conditions yield additional changes in pore space microstructure. The experimental results were applied to a geothermal fluid production scenario to constrain drawdown and time-dependent effects on the reservoir, overall, to provide a reference for the hydromechanical behavior of geothermal systems in carbonate, and more specifically, in Upper Jurassic lithologies.

  3. Effect of boron and carbon on thermomechanical fatigue of IN 718 superalloy

    International Nuclear Information System (INIS)

    Xiao, L.; Chen, D.L.; Chaturvedi, M.C.

    2006-01-01

    Stress-controlled thermomechanical fatigue (TMF) behavior of IN 718 superalloy with different concentrations of boron (B) and carbon (C) was studied with temperature varying between 350 and 650 deg. C at different cyclic stress ranges and at a stress ratio of R = 0.1. Initial cyclic softening followed by a significant cyclic hardening was observed in the in-phase (IP) TMF, while continuous cyclic hardening occurred during out-of-phase (OP) TMF. Tensile cyclic creep was observed in all the TMF deformation regimes, and the creep strain increased with increasing number of cycles and stress range. B and C additions were found to retard the cyclic creep, leading to an effective improvement in the fatigue life of IP-TMF. Among the four alloys tested, the alloy with 29 ppm B and 225 ppm C exhibited the lowest creep strain and the highest IP-TMF life at the lower stress range. In the OP-TMF, the fatigue life increased with increasing B concentration at the higher stress range, and with C concentration at the lower stress range. The IP-TMF life was observed to be much shorter than that of the OP-TMF, with a crossover occurring at the higher stress range. Fractographic examinations showed that the fracture was predominantly intergranular in the IP-TMF mode, and transgranular, as characterized by typical fatigue striations, in the OP-TMF mode of deformation. The difference in the fracture mechanisms between the IP and OP-TMF mode of deformation was the primary reason for a significant influence of the loading mode on the TMF lifetime

  4. A preliminary study of thermo-mechanical stability of carbon S-phase formed in austenitic stainless steel

    Energy Technology Data Exchange (ETDEWEB)

    Li, Wei; Chiu, Yu Long; Dong, Hanshan, E-mail: wsgddf@hotmail.com [School of Metallurgy and Materials, College of Physical and Engineering Sciences, The University of Birmingham, Birmingham (United Kingdom)

    2010-07-01

    Carbon S-phase was generated in the surface of AISI316 austenitic stainless steel by plasma carburising at 500°C for 10h in a gas mixture of 1.5%CH4 and 98.5%H{sub 2}. The thermo-mechanical stability of the carbon S-phase was studied by stressing the 'dog-bone' tensile specimens in the range of 0-200MPa at temperatures ranging from 400 to 500°C for 100-150h. Post-test characterisation was conducted using XRD, SEM, TEM and micro-indentation. The experimental results demonstrate that when tested at a fix temperature the thickness of the carbon S-phase layer increased with the stress applied to the tensile specimens during the thermo-mechanical stability tests. This indicates that tensile stress promotes the diffusion of carbon in the carbon-S-phase. When stressed at 400°C the microstructure of the carbon S-phase was not affected by the stress level; however, when stressed at 450 and 500°C for 100MPa or above, the corrosion resistance of the carbon S-phase slightly deteriorated. The application of a tensile stress during annealing of S-phase layer can retard the deduction of its hardness. This is believed to be related to the early stage precipitation of carbides in the S-phase, which could be facilitated by the applied tensile stress during thermal annealing. (author)

  5. Spatially resolved quantitative mapping of thermomechanical properties and phase transition temperatures using scanning probe microscopy

    Science.gov (United States)

    Jesse, Stephen; Kalinin, Sergei V; Nikiforov, Maxim P

    2013-07-09

    An approach for the thermomechanical characterization of phase transitions in polymeric materials (polyethyleneterephthalate) by band excitation acoustic force microscopy is developed. This methodology allows the independent measurement of resonance frequency, Q factor, and oscillation amplitude of a tip-surface contact area as a function of tip temperature, from which the thermal evolution of tip-surface spring constant and mechanical dissipation can be extracted. A heating protocol maintained a constant tip-surface contact area and constant contact force, thereby allowing for reproducible measurements and quantitative extraction of material properties including temperature dependence of indentation-based elastic and loss moduli.

  6. Microstructuring of thermo-mechanically highly stressed surfaces final report of the DFG research group 576

    CERN Document Server

    Rienäcker, Adrian; Knoll, Gunter; Bach, Friedrich-Wilhelm; Maier, Hans; Reithmeier, Eduard; Dinkelacker, Friedrich

    2015-01-01

    This contributed volume presents the final research results of the DFG Research Group 576, which is a joint initiative of five different institutes of the Leibniz Universität Hannover and the Universität Kassel, Germany. The research of the DFG Research Group 576 focuses on improving the tribological behavior of thermomechanically highly stressed surfaces, particularly on cylinder liner for combustion engines. The target audience primarily comprises researchers and experts in the field but the book may also be beneficial for graduate students who want to specialize in the field.

  7. Effect of Multipass TIG and Activated TIG Welding Process on the Thermo-Mechanical Behavior of 316LN Stainless Steel Weld Joints

    Science.gov (United States)

    Ganesh, K. C.; Balasubramanian, K. R.; Vasudevan, M.; Vasantharaja, P.; Chandrasekhar, N.

    2016-04-01

    The primary objective of this work was to develop a finite element model to predict the thermo-mechanical behavior of an activated tungsten inert gas (ATIG)-welded joint. The ATIG-welded joint was fabricated using 10 mm thickness of 316LN stainless steel plates in a single pass. To distinguish the merits of ATIG welding process, it was compared with manual multipass tungsten inert gas (MPTIG)-welded joint. The ATIG-welded joint was fabricated with square butt edge configuration using an activating flux developed in-house. The MPTIG-welded joint was fabricated in thirteen passes with V-groove edge configuration. The finite element model was developed to predict the transient temperature, residual stress, and distortion of the welded joints. Also, microhardness, impact toughness, tensile strength, ferrite measurement, and microstructure were characterized. Since most of the recent publications of ATIG-welded joint was focused on the molten weld pool dynamics, this research work gives an insight on the thermo-mechanical behavior of ATIG-welded joint over MPTIG-welded joint.

  8. Impact of Age, Gender, and Addition of Probiotics on Treatment Success for Helicobacter pylori in Children

    Directory of Open Access Journals (Sweden)

    Noam Weiner MD

    2015-10-01

    Full Text Available The primary objective of this study was to evaluate the effect of age, gender, and the use of probiotics with standard treatment regimen on Helicobacter pylori eradication. Based on endoscopic findings and clinical presentation, selected patients were treated with standard triple therapy (omeprazole, clarithromycin, and amoxicillin. Those who failed were offered a repeat treatment with omeprazole, metronidazole, and amoxicillin. After the publications of the possible advantages of probiotic treatment on H pylori eradication, the probiotic agent “Probiotica Forte” was routinely added to the treatment. Eradication was noted for 94/130 patients (72% and for 128/197 patients (65% with or without probiotic agent, respectively (P = .23. For second-line treatment eradication was noted in 33/46 (72% and in 9/20 (45% with or without probiotic agent, respectively (P = .053. The addition of probiotics may improve eradication success especially in addition to second-line treatment.

  9. Energy-based fatigue model for shape memory alloys including thermomechanical coupling

    Science.gov (United States)

    Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Van Herpen, Alain; Zhang, Weihong

    2016-03-01

    This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well.

  10. Compilation of data for thermomechanical analyses of four potential salt repositories

    International Nuclear Information System (INIS)

    Tammemagi, H.Y.; Loken, M.C.; Osnes, J.D.; Wagner, R.A.

    1986-01-01

    This report includes a collection and summarization of the data which are necessary to perform thermomechanical analyses of four potential salt repository sites: Paradox Basin, Utah; Permian Basin, Texas; Richton Dome, Mississippi; and Vacherie Dome, Louisiana. Thermal, mechanical, and hydrogeological material properties are presented so that the numerical analyses can be subdivided into three geometric regions: canister, disposal room, and repository site. Data are presented for the salt formations, the surrounding geological units, and for human-made materials placed in the repository such as the nuclear waste and its protective steel liner. Wherever possible, site-specific data are used which have been determined from laboratory testing of drill core or from interpretation of geophysical logs. Although much effort has been made to obtain the most appropriate data, there are deficiencies because some of the required site-specific data are either not available or are inconsistent with anticipated values

  11. Experimental study on the thermo-mechanical behaviour of stiff clay under non-isotropic stress state

    International Nuclear Information System (INIS)

    Tang, Anh Minh; Cui, Yu-Jun; Li, Xiang-Ling

    2012-01-01

    Document available in extended abstract form only. Stiff clay is usually considered as possible host-rock for geological radioactive waste disposal due to its low permeability and its self-sealing capacity. Boom Clay, for instance, is one of the clays currently considered by the Belgian radioactive waste management agency Ondraf/Niras as a potential host for a geological repository. In order to analyse the performance of this material, it is important to understand its behaviour under the coupled thermo-hydro-mechanical solicitations. In laboratory, several studies have been performed to study the volume change of clay under coupled thermomechanical loading. The results show that heating under drained conditions can induce thermal dilation at low confining stress and thermal contraction at high confining stress. On the other hand, compression tests performed at constant temperature show that the compressibility parameters of soil can be modified by temperature change. These features are now well considered in constitutive laws based on the framework of elasto-plasticity. Under undrained conditions, heating can increase pore-water pressure and this behaviour can be simulated using the theoretical thermo-poro-elastic framework. The temperature effect on the soil behaviour under triaxial compression is also often considered. It is commonly accepted that heating decreases the shear strength of clay but this softening can be hidden by the thermal contraction that occurs during heating which can induce at the same time soil hardening. In spite of these existing works, laboratory tests considering the thermo-mechanical loading path that the soil can be subjected to are still rare. Actually, in the case of geological radioactive waste disposal, after the installation of waste canisters, the soil is expected to be heated under non-isotropic stress state. Most of the existing laboratory works show heating tests in odometer cell or triaxial cell under isotropic stress

  12. Structure of maraging steel after thermomechanical treatment at high temperature

    International Nuclear Information System (INIS)

    Prokoshkina, V.G.; Kaputkina, L.M.; Mozzhukhin, V.E.

    1981-01-01

    Developed polygonized substructure is formed in austenite of maraging Cr-Ni steels under the selected conditions of hot deformation during high temperature mechanical treatment (HTMT). Substructure of hot deformed austenite is inherited by packet martensite during cooling. Presence of developed polygonized substructure in austenite results in grinding and high uniformity of packet sizes of martensite crystals. Substructure of α-phase of the investigated steels after HTMT, as well as the one inherited from hot deformed austenite, is inherited at α→γ-transformation in the process of repetitive austenization, and it can be preserved within a limited temperature-time range of heating in γ-region [ru

  13. Microstructural modeling of fatigue fracture of shape memory alloys at thermomechanical cyclic loading

    Science.gov (United States)

    Belyaev, Fedor S.; Evard, Margarita E.; Volkov, Aleksandr E.

    2018-05-01

    A microstructural model of shape memory alloys (SMA) describing their deformation and fatigue fracture is presented. A new criterion of fracture has been developed which takes into account the effect of hydrostatic pressure, deformation defects and material damage. It is shown that the model can describe the fatigue fracture of SMA under various thermomechanical cycling regimes. Results of calculating the number of cycles to failure at thermocycling under a constant stress, at symmetric two-sided cyclic deformation, at straining-unloading cycles, at cycling in the regime of the thermodynamic cycles of a SMA working body in the hard (strain controlled) and soft (stress controlled) working cycles, is studied. Results of calculating the number of cycles to failure are presented for different parameters of these cycles.

  14. Effects of thermal aging on thermo-mechanical behavior of a glass sealant for solid oxide cell applications

    DEFF Research Database (Denmark)

    Abdoli, Hamid; Alizadeh, Parvin; Boccaccini, Dino

    2014-01-01

    Thermo-mechanical properties of a silicate based glass and its potential use for sealing application in intermediate temperature solid oxide cell (SOC) are presented in this paper. Effects of thermal aging are discussed on structural and microstructural evolution, thermal expansion, viscosity......'s modulus in which a transition between a slow softening (elastic) regime and a rapid softening one was observed. Crystallization induced by thermal aging led to higher creep resistance, but lower capability of crack healing when inspected by electron microscopy. However, potential of stress relaxation...

  15. Thermal expansion coefficient and thermomechanical properties of SiN(x) thin films prepared by plasma-enhanced chemical vapor deposition.

    Science.gov (United States)

    Tien, Chuen-Lin; Lin, Tsai-Wei

    2012-10-20

    We present a new method based on fast Fourier transform (FFT) for evaluating the thermal expansion coefficient and thermomechanical properties of thin films. The silicon nitride thin films deposited on Corning glass and Si wafers were prepared by plasma-enhanced chemical vapor deposition in this study. The anisotropic residual stress and thermomechanical properties of silicon nitride thin films were studied. Residual stresses in thin films were measured by a modified Michelson interferometer associated with the FFT method under different heating temperatures. We found that the average residual-stress value increases when the temperature increases from room temperature to 100°C. Increased substrate temperature causes the residual stress in SiN(x) film deposited on Si wafers to be more compressive, but the residual stress in SiN(x) film on Corning glass becomes more tensile. The residual-stress versus substrate-temperature relation is a linear correlation after heating. A double substrate technique is used to determine the thermal expansion coefficients of the thin films. The experimental results show that the thermal expansion coefficient of the silicon nitride thin films is 3.27×10(-6)°C(-1). The biaxial modulus is 1125 GPa for SiN(x) film.

  16. Thermomechanical effects on permeability for a 3-D model of YM rock

    International Nuclear Information System (INIS)

    Berge, P A; Blair, S C; Wang, H F

    1999-01-01

    The authors estimate how thermomechanical processes affect the spatial variability of fracture permeability for a 3-D model representing Topopah Spring tuff at the nuclear-waste repository horizon in Yucca Mountain, Nevada. Using a finite-difference code, they compute thermal stress changes. They evaluate possible permeability enhancement resulting from shear slip along various mapped fracture sets after 50 years of heating, for rock in the near-field environment of the proposed repository. The results indicate permeability enhancement of a factor of 2 for regions about 10 to 30 m above drifts, for north-south striking vertical fractures. Shear slip and permeability increases of a factor of 4 can occur in regions just above drifts, for east-west striking vertical fractures. Information on how permeability may change over the lifetime of a geologic repository is important to the prediction and evaluation of repository performance

  17. Microwave propagation and absorption and its thermo-mechanical consequences in heterogeneous rocks.

    Science.gov (United States)

    Meisels, R; Toifl, M; Hartlieb, P; Kuchar, F; Antretter, T

    2015-02-10

    A numerical analysis in a two-component model rock is presented including the propagation and absorption of a microwave beam as well as the microwave-induced temperature and stress distributions in a consistent way. The analyses are two-dimensional and consider absorbing inclusions (discs) in a non-absorbing matrix representing the model of a heterogeneous rock. The microwave analysis (finite difference time domain - FDTD) is performed with values of the dielectric permittivity typical for hard rocks. Reflections at the discs/matrix interfaces and absorption in the discs lead to diffuse scattering with up to 20% changes of the intensity in the main beam compared to a homogeneous model rock. The subsequent thermo-mechanical finite element (FE) analysis indicates that the stresses become large enough to initiate damage. The results are supported by preliminary experiments on hard rock performed at 2.45 GHz.

  18. AB INITIO Modeling of Thermomechanical Properties of Mo-Based Alloys for Fossil Energy Conversion

    Energy Technology Data Exchange (ETDEWEB)

    Ching, Wai-Yim

    2013-12-31

    In this final scientific/technical report covering the period of 3.5 years started on July 1, 2011, we report the accomplishments on the study of thermo-mechanical properties of Mo-based intermetallic compounds under NETL support. These include computational method development, physical properties investigation of Mo-based compounds and alloys. The main focus is on the mechanical and thermo mechanical properties at high temperature since these are the most crucial properties for their potential applications. In particular, recent development of applying ab initio molecular dynamic (AIMD) simulations to the T1 (Mo{sub 5}Si{sub 3}) and T2 (Mo{sub 5}SiB{sub 2}) phases are highlighted for alloy design in further improving their properties.

  19. Influence of Carbon Nano Tubes on the Thermo-Mechanical Properties of Unsaturated Polyester Nanocomposite

    International Nuclear Information System (INIS)

    Alam, A K M Moshiul; Beg, M D H; Yunus, Rosli Mohd

    2015-01-01

    To date nano fillers are renowned reinforcing agent for polymer materials. In this work, unsaturated polyester (UPR) nanocomposites were fabricated by 0.1, 0.3 and 0.5 wt% multi walled carbon nanotubes (MWCNTs) through solution dispersion and casting method. The influence of MWCNT content was investigated by thermo-mechanical properties. Dispersion of nanotubes was observed by fracture morphology. The strength of nanocomposites rose with raising the CNT content. Moreover, DSC thermograms of nanocomposites represent noticeable improvement of glass transition temperature (T g ), melting temperature (T m ) and enthalpy (ΔH m ). Micro-crystallinity of nanocomposites increased with increasing the CNT content. Moreover, the stiffness increased with increasing the CNT content. (paper)

  20. Drift scale thermomechanical analysis for thermal loading and retrievability studies

    International Nuclear Information System (INIS)

    Tsai, F.C.

    1995-01-01

    The repository portion of the Mined Geologic Disposal System for the disposal of spent nuclear fuel and high-level radioactive waste is currently in the advanced conceptual design stage. In support of systems studies, a numerical method was used to estimate the stability of emplacement drifts. Thermomechanical analyses, using the Discontinuous Deformation Analysis code, were performed using input data from Yucca Mountain documents. The analysis found that the stresses produced in the rock at thermal loads of 27.4 kilograms uranium per m2 (KgU/m2) would exceed stability criteria and could result in tunnel instability. At thermal loads between 20.5 KgU/m2, the drift is predicted to be stable and its structural integrity remains after thermal loading. In this case, the smaller diameter drift emplacement appears to have better stability. However, local rock spalling may occur. According to the numerical prediction, more rock fall may occur during the retrieval period due to the stress relaxation caused by the rapid cooling in the immediate drift area

  1. Transient Thermo-Mechanical Analysis of the TPSG4 Beam Diluter

    CERN Document Server

    Goddard, B; Herrera-Martínez, A; Kadi, Y; Marque, S

    2002-01-01

    A new extraction channel is being built in the Super Proton Synchrotron (SPS) Long Straight Section 4 (LSS4) to transfer proton beams to the Large Hadron Collider (LHC) and also to the CERN Neutrino to Gran Sasso (CNGS) target. The beam is extracted in a fast mode during a single turn. For this purpose a protection of the MSE copper septum coil, in the form of a beam diluting element placed upstream, will be required to cope with the new failure modes associated with the fast extraction operation. The present analysis focuses on the thermo-mechanical behavior of the proposed TPSG4 diluter element irradiated by a fast extracted beam (up to 4.9 x 10^13 protons per 7.2 mus pulse) from the SPS. The deposited energy densities, estimated from primary and secondary particle simulations using the high-energy particle transport code FLUKA, were converted to internal heat generation rates taken as a thermal load input for the finite-element engineering analyses code ANSYS. According to the time dependence of the extrac...

  2. Pressurized Slot Testing to Determine Thermo-Mechanical Properties of Lithophysal Tuff at Yucca Mountain Nevada.

    Energy Technology Data Exchange (ETDEWEB)

    George, James T.; Sobolik, Steven R.; Lee, Moo Y.; Park, Byoung; Costin, Laurence

    2018-05-01

    The study described in this report involves heated and unheated pressurized slot testing to determine thermo-mechanical properties of the Tptpll (Tertiary, Paintbrush, Topopah Spring Tuff Formation, crystal poor, lower lithophysal) and Tptpul (upper lithophysal) lithostratigraphic units at Yucca Mountain, Nevada. A large volume fraction of the proposed repository at Yucca Mountain may reside in the Tptpll lithostratigraphic unit. This unit is characterized by voids, or lithophysae, which range in size from centimeters to meters, making a field program an effective method of measuring bulk thermal-mechanical rock properties (thermal expansion, rock mass modulus, compressive strength, time-dependent deformation) over a range of temperature and rock conditions. The field tests outlined in this report provide data for the determination of thermo-mechanical properties of this unit. Rock-mass response data collected during this field test will reduce the uncertainty in key thermal-mechanical modeling parameters (rock-mass modulus, strength and thermal expansion) for the Tptpll lithostratigraphic unit, and provide a basis for understanding thermal-mechanical behavior of this unit. The measurements will be used to evaluate numerical models of the thermal-mechanical response of the repository. These numerical models are then used to predict pre- and post-closure repository response. ACKNOWLEDGEMENTS The authors would like to thank David Bronowski, Ronnie Taylor, Ray E. Finley, Cliff Howard, Michael Schuhen (all SNL) and Fred Homuth (LANL) for their work in the planning and implementation of the tests described in this report. This is a reprint of SAND2004-2703, which was originally printed in July 2004. At that time, it was printed for a restricted audience. It has now been approved for unlimited release.

  3. Energy-based fatigue model for shape memory alloys including thermomechanical coupling

    International Nuclear Information System (INIS)

    Zhang, Yahui; Zhu, Jihong; Moumni, Ziad; Zhang, Weihong; Van Herpen, Alain

    2016-01-01

    This paper is aimed at developing a low cycle fatigue criterion for pseudoelastic shape memory alloys to take into account thermomechanical coupling. To this end, fatigue tests are carried out at different loading rates under strain control at room temperature using NiTi wires. Temperature distribution on the specimen is measured using a high speed thermal camera. Specimens are tested to failure and fatigue lifetimes of specimens are measured. Test results show that the fatigue lifetime is greatly influenced by the loading rate: as the strain rate increases, the fatigue lifetime decreases. Furthermore, it is shown that the fatigue cracks initiate when the stored energy inside the material reaches a critical value. An energy-based fatigue criterion is thus proposed as a function of the irreversible hysteresis energy of the stabilized cycle and the loading rate. Fatigue life is calculated using the proposed model. The experimental and computational results compare well. (paper)

  4. Thermomechanical behavior of dry contacts in disc brake rotor with a grey cast iron composition

    Directory of Open Access Journals (Sweden)

    Belhocine Ali

    2013-01-01

    Full Text Available The main purpose of this study is to analysis the thermomechanical behavior of the dry contact between the brake disc and pads during the braking phase. The simulation strategy is based on the calculation code ANSYS11. The modeling of transient temperature in the disk is actually used to identify the factor of geometric design of the disk to install the ventilation system in vehicles. The thermal-structural analysis is then used coupling to determine the deformation established and the Von Mises stresses in the disk, the contact pressure distribution in pads. The results are satisfactory compared to those found in the literature.

  5. The equations of the thermomechanics of electrically conducting nonferromagnetic bodies taking account of structural transformations

    International Nuclear Information System (INIS)

    Nagirnyi, T.S.

    1993-01-01

    Studies of the coupled processes in electrically conducting nonferromagnetic viscoelastic bodies usually begin with a system of equations that accounts for the influence of rheology on the mechanical and temperature fields. In this context, rheology is understood as the course of certain internal processes in the body that are reflected when the relaxation time and the defects of thermomechanical moduli are specified. In this work, the methods of continuum mechanics are used to state a system of equations for the quantitative description of coupled mechanical, thermal, and electromagnetic processes taking account of structural transformations in the context of the model of a rheologically simple electrically conducting nonferromagnetic body

  6. Contact-Free Support Structures for Part Overhangs in Powder-Bed Metal Additive Manufacturing

    Directory of Open Access Journals (Sweden)

    Kenneth Cooper

    2017-12-01

    Full Text Available This study investigates the feasibility of a novel concept, contact-free support structures, for part overhangs in powder-bed metal additive manufacturing. The intent is to develop alternative support designs that require no or little post-processing, and yet, maintain effectiveness in minimizing overhang distortions. The idea is to build, simultaneously during part fabrications, a heat sink (called “heat support”, underneath an overhang to alter adverse thermal behaviors. Thermomechanical modeling and simulations using finite element analysis were applied to numerically research the heat support effect on overhang distortions. Experimentally, a powder-bed electron beam additive manufacturing system was utilized to fabricate heat support designs and examine their functions. The results prove the concept and demonstrate the effectiveness of contact-free heat supports. Moreover, the method was tested with different heat support parameters and applied to various overhang geometries. It is concluded that the heat support proposed has the potential to be implemented in industrial applications.

  7. Thermo-mechanical screening tests to qualify beryllium pebble beds with non-spherical pebbles

    Energy Technology Data Exchange (ETDEWEB)

    Reimann, Joerg, E-mail: joerg.reimann@partner.kit.edu [IKET, Karlsruhe Institute of Technology, Karlsruhe (Germany); Fretz, Benjamin [KBHF GmbH, Eggenstein-Leopoldshafen (Germany); Pupeschi, Simone [IAM, Karlsruhe Institute of Technology, Karlsruhe (Germany)

    2015-10-15

    Highlights: • In present ceramic breeder blankets, pebble-shaped beryllium is used as a neutron multiplier. • Spherical pebbles are considered as the candidate material, however, non-spherical particles are of economic interest. • Thermo-mechanical pebble bed data do merely exist for non-spherical beryllium grades. • Uniaxial compression tests (UCTs), combined with the Hot Wire Technique (HWT) were used to measure the stress–strain relations and the thermal conductivity. • A small experimental set-up had to be used and a detailed 3D modelling was of prime importance. • Compared to spherical pebble beds, non-spherical pebble beds are generally softer and mainly the thermal conductivity is lower. - Abstract: In present ceramic breeder blankets, pebble-shaped beryllium is used as a neutron multiplier. Fairly spherical pebbles are considered as a candidate material, however, non-spherical particles are of economic interest because production costs are much lower. Yet, thermo-mechanical pebble bed data do merely exist for these beryllium grades, and the blanket relevant potential of these grades cannot be judged. Screening experiments were performed with three different grades of non-spherical beryllium pebbles, produced by different companies, accompanied by experiments with the reference beryllium pebble beds. Uniaxial compression tests (UCTs), combined with the Hot Wire Technique (HWT), were performed to measure both the stress–strain relation and the thermal conductivity, k, at different stress levels. Because of the limited amounts of the non-spherical materials, the experimental set-ups were small and a detailed 3D modelling was of prime importance in order to prove that the used design was appropriate. Compared to the pebble beds consisting of spherical pebbles, non-spherical pebble beds are generally softer (smaller stress for a given strain), and, mainly as a consequence of this, for a given strain value, the thermal conductivity is lower. This

  8. Hydromechanical and Thermomechanical Behaviour of Elastic Fractures during Thermal Stimulation of Naturally Fractured Reservoirs

    Science.gov (United States)

    Jalali, Mohammadreza; Valley, Benoît

    2015-04-01

    During the last two decades, incentives were put in place in order to feed our societies in energy with reduced CO2 emissions. Various policies have been considered to fulfill this strategy such as replacing coal by natural gas in power plants, producing electricity using CO2 free resources, and CO2 sequestration as a remediation for large point-source emitters (e.g. oil sands facilities, coal-fired power plants, and cement kilns). Naturally fractured reservoirs (NFRs) are among those geological structures which play a crucial role in the mentioned energy revolution. The behavior of fractured reservoirs during production processes is completely different than conventional reservoirs because of the dominant effects of fractures on fluid flux, with attendant issues of fracture fabric complexity and lithological heterogeneity. The level of complexity increases when thermal effects are taking place - as during the thermal stimulation of these stress-sensitive reservoirs in order to enhance the gas production in tight shales and/or increase the local conductivity of the fractures during the development of enhanced geothermal systems - where temperature is introduced as another degree of freedom in addition to pressure and displacement (or effective stress). Study of these stress-pressure-temperature effects requires a thermo-hydro-mechanical (THM) coupling approach, which considers the simultaneous variation of effective stress, pore pressure, and temperature and their interactions. In this study, thermal, hydraulic and mechanical behavior of partially open and elastic fractures in a homogeneous, isotropic and low permeable porous rock is studied. In order to compare the hydromechanical (HM) and thermomechanical (TM) characteristics of these fractures, three different injection scenarios, i.e. constant isothermal fluid injection rate, constant cooling without any fluid injection and constant cold fluid injection, are considered. Both thermomechanical and hydromechanical

  9. Microstructure and Thermomechanical Properties of Magnesium Alloys Castings

    Directory of Open Access Journals (Sweden)

    P. Lichý

    2012-04-01

    Full Text Available Magnesium alloys thanks to their high specific strength have an extensive potential of the use in a number of industrial applications. The most important of them is the automobile industry in particular. Here it is possible to use this group of materials for great numbers of parts from elements in the car interior (steering wheels, seats, etc., through exterior parts (wheels particularly of sporting models, up to driving (engine blocks and gearbox mechanisms themselves. But the use of these alloys in the engine structure has its limitations as these parts are highly thermally stressed. But the commonly used magnesium alloys show rather fast decrease of strength properties with growing temperature of stressing them. This work is aimed at studying this properties both of alloys commonly used (of the Mg-Al-Zn, Mn type, and of that ones used in industrial manufacture in a limited extent (Mg-Al-Sr. These thermomechanical properties are further on complemented with the microstructure analysis with the aim of checking the metallurgical interventions (an effect of inoculation. From the studied materials the test castings were made from which the test bars for the tensile test were subsequently prepared. This test took place within the temperature range of 20°C – 300°C. Achieved results are summarized in the concluding part of the contribution.

  10. Microstructure and thermomechanical pretreatment effects on creep behaviour of helium-implanted DIN 1.4970 austenitic stainless steel

    International Nuclear Information System (INIS)

    Matta, M.K.; Kesternich, W.

    1990-01-01

    Microstructure investigations were carried out on unimplanted and 150 at ppm helium implanted foil specimens of DIN 1.4970 austenitic stainless steel after various thermomechanical pretreatments. Creep test were also carried out for both helium-implanted and unimplanted specimens at 700degC and 800degC. The strength, ductility and rupture time are correalted with the dislocation and precipitate distributions. Helium embrittlement can be reduced in these experiments when dispersive TiC precipitate distributions are produced by proper pretreatments or allowed to form during creep test. (author). 14 refs., 11 figs

  11. Impact of Thermomechanical Fiber Pre-Treatment Using Twin-Screw Extrusion on the Production and Properties of Renewable Binderless Coriander Fiberboards

    Science.gov (United States)

    Uitterhaegen, Evelien; Labonne, Laurent; Merah, Othmane; Talou, Thierry; Ballas, Stéphane; Véronèse, Thierry

    2017-01-01

    The aim of this study consisted of manufacturing renewable binderless fiberboards from coriander straw and a deoiled coriander press cake, thus at the same time ensuring the valorization of crop residues and process by-products. The press cake acted as a natural binder inside the boards owing to the thermoplastic behavior of its protein fraction during thermopressing. The influence of different fiber-refining methods was evaluated and it was shown that a twin-screw extrusion treatment effectively improved fiber morphology and resulted in fiberboards with enhanced performance as compared to a conventional grinding process. The best fiberboard was produced with extrusion-refined straw using a 0.4 liquid/solid (L/S) ratio and with 40% press cake addition. The water sensitivity of the boards was effectively reduced by 63% through the addition of an extrusion raw material premixing operation and thermal treatment of the panels at 200 °C, resulting in materials with good performance showing a flexural strength of 29 MPa and a thickness swelling of 24%. Produced without the use of any chemical adhesives, these fiberboards could thus present viable, sustainable alternatives for current commercial wood-based materials such as oriented strand board, particleboard and medium-density fiberboard, with high cost-effectiveness. PMID:28714928

  12. Thermomechanical analysis of Natural Rubber behaviour stressed at room temperature.

    Directory of Open Access Journals (Sweden)

    Chrysochoos A.

    2010-06-01

    Full Text Available Owing to their high molecular mobility, stressed rubber chains can easily change their conformations and get orientated. This phenomena leads to so high reversible draw ratio that this behaviour is called rubber elasticity [1-3]. The analogy with ideal gases leads to an internal energy independent of elongation, the stress being attributed to a so-called configuration entropy. However, this analysis cannot take thermal expansion into account and moreover prohibits predicting standard thermo-elastic effect noticed at small elongations and the thermoelastic inversion effects [4]. This paper aims at : observing and quantifying dissipative and coupling effects associated with deformation energy, generated when Natural Rubber is stretched. re-examine the thermomechanical behaviour model of rubberlike materials, under the generalised standard material concept. From an experimental viewpoint, energy balance is created using infrared and quantitative imaging techniques. Digital Image Correlation (DIC provides in-the-plane displacement fields and, after derivation, strain and strain-rate fields. We have used those techniques to evidence the thermoelastic inversion effect as shown on Figure 1 where different weights have been fixed to warmed specimen and we monitored the sample deformation while it recovers room temperature. But we have also used those techniques to perform energy balance : analysis of the mechanical equilibrium allows estimates of the stress pattern and computation of deformation energy rates under a plane stress hypothesis [5]. Infrared Thermography (IRT gives the surface temperature of the sample. To estimate the distribution of heat sources, image processing with a local heat equation and a minimal set of approximation functions (image filtering was used. The time courses of deformation energy and heat associated with cyclic process are plotted in Figure 2. The time derivatives of both forms of energy are approximately similar. This

  13. Thermo-mechanic and sensory properties of wheat and rye breads produced with varying concentration of the additive

    Directory of Open Access Journals (Sweden)

    Demin Mirjana A.

    2013-01-01

    Full Text Available The effects of different concentrations of the complex additive containing emulsifiers, oxido-reductive substances and enzymes, on the rheological conditions of dough, and on the sensory properties of three groups of bread were investigated. The best initial quality and the lowest degree of protein network weakening had the dough obtained from mixed wheat and rye flours. The best expected baking properties were shown by the white wheat flour due to the least damage of its starch. The use of the additive has an effect on the absorption of water and on the majority of C-values of all sorts of flour. The amount of additive had a significant effect on the sensory properties of wheat bread crumb texture. Also, storage duration significantly affected (p <0.01 the sensory properties of integral wheat bread aroma-taste and the weighted mean score. The interaction of these two factors had no significant effect on any of sensory properties of the investigated groups of bread.

  14. Is addition of sodium fluoride to cyclical etidronate beneficial in the treatment of corticosteroid induced osteoporosis?

    NARCIS (Netherlands)

    Lems, W. F.; Jacobs, J. W.; Bijlsma, J. W.; van Veen, G. J.; Houben, H. H.; Haanen, H. C.; Gerrits, M. I.; van Rijn, H. J.

    1997-01-01

    To investigate whether administration of sodium fluoride (NaF) in addition to cyclical etidronate has a positive effect on bone mineral density (BMD) in patients with established osteoporosis during continued treatment with corticosteroids. 47 patients who were receiving treatment with

  15. 78 FR 14508 - Notice of Affirmation of Addition of a Treatment Schedule for Methyl Bromide Fumigation of...

    Science.gov (United States)

    2013-03-06

    ... contacting the Animal and Plant Health Inspection Service, Plant Protection and Quarantine, Manuals Unit, 92... the Plant Protection and Quarantine Treatment Manual a treatment schedule for methyl bromide..., 2013, we are affirming the addition to the Plant Protection and Quarantine Treatment Manual of the...

  16. Thermomechanical and adhesive properties of radiation-modified polymer composites for thermosetting products

    International Nuclear Information System (INIS)

    Kalkis, V.; Maksimov, R.D.; Kalnins, M.; Zicans, J.; Bocoka, T.; Revjakin, O.

    2000-01-01

    The gamma-irradiated blends of polyethylene (PE) with ethylene / propylene / diene copolymer (Epdm) and thermotropic liquid crystalline polymer (LCP) are investigated. The radiation dose absorbed does not exceed 150 kGy (10 kGy=1 Mrad). It is shown that the even small amounts of LCP added to PE improve the mechanical and operational properties of composites and the thermosetting products made of them. The temperature dependences of the elastics modulus, tension diagrams at a temperature above the PE melting point, and recovery curves of the oriented specimens are presented. The kinetics of thermorelaxation and residual setting stresses upon isometric heating and cooling of the previously oriented composites is studied. The data on the influence of LCP on the adhesion interaction of the blend with steel are obtained. The features of thermomechanical and adhesive properties are discussed and the results of morphological and calorimetric tests are given. (author)

  17. A simple analytical thermo-mechanical model for liquid crystal elastomer bilayer structures

    Directory of Open Access Journals (Sweden)

    Yun Cui

    2018-02-01

    Full Text Available The bilayer structure consisting of thermal-responsive liquid crystal elastomers (LCEs and other polymer materials with stretchable heaters has attracted much attention in applications of soft actuators and soft robots due to its ability to generate large deformations when subjected to heat stimuli. A simple analytical thermo-mechanical model, accounting for the non-uniform feature of the temperature/strain distribution along the thickness direction, is established for this type of bilayer structure. The analytical predictions of the temperature and bending curvature radius agree well with finite element analysis and experiments. The influences of the LCE thickness and the heat generation power on the bending deformation of the bilayer structure are fully investigated. It is shown that a thinner LCE layer and a higher heat generation power could yield more bending deformation. These results may help the design of soft actuators and soft robots involving thermal responsive LCEs.

  18. Effect of TMP variables upon structure and properties in ODS alloy HDA 8077 sheet. [ThermoMechanical Processing of Oxide Dispersion Strengthened nickel alloy

    Science.gov (United States)

    Rothman, M. F.; Tawancy, H. M.

    1980-01-01

    The effects of oxide content level and variations in thermomechanical processing upon the final structure and properties of HDA 8077 sheet have been systematically examined. It was found that creep strength and formability are substantially influenced by both oxide content and TMP schedule. Variations in creep properties obtained appear to correlate with observed microstructures.

  19. Numerical modeling of the thermomechanical behavior of networks of underground galleries for the storage of the radioactive waste: approach by homogenization

    International Nuclear Information System (INIS)

    Zokimila, P.

    2005-10-01

    Deep geological disposal is one of the privileged options for the storage of High Level radioactive waste. A good knowledge of the behavior and properties of the potential geological formations as well as theirs evolution in time under the effect of the stress change induced by a possible installation of storage is required. The geological formation host will be subjected to mechanical and thermal solicitations due respectively to the excavation of the disposal tunnels and the release of heat of the canisters of radioactive waste. These thermomechanical solicitations will generate a stress relief in the host layer and disposal tunnels deformations as well as the extension of the damaged zones (EDZ) could cause local and global instabilities. This work aims to develop calculation methods to optimize numerical modeling of the thermoelastic behavior of the disposal at a large scale and to evaluate thermomechanical disturbance induced by storage on the geological formation host. Accordingly, after a presentation of the state of knowledge on the thermomechanical aspects of the rocks related to deep storage, of numerical modeling 2D and 3D of the thermoelastic behavior of individual disposal tunnel and a network of tunnels were carried out by a discrete approach. However, this classical approach is penalizing to study the global behavior of disposal storage. To mitigate that, an approach of numerical modeling, based on homogenization of periodic structures, was proposed. Formulations as numerical procedures were worked out to calculate the effective thermoelastic behavior of an equivalent heterogeneous structure. The model, obtained by this method, was validated with existing methods of homogenization such as the self-consistent model, as well as the Hashin-Shtrikman bounds. The comparison between the effective thermoelastic behavior and current thermoelastic behavior of reference showed a good coherence of the results. For an application to deep geological storage, the

  20. Reliable high-power diode lasers: thermo-mechanical fatigue aspects

    Science.gov (United States)

    Klumel, Genady; Gridish, Yaakov; Szafranek, Igor; Karni, Yoram

    2006-02-01

    High power water-cooled diode lasers are finding increasing demand in biomedical, cosmetic and industrial applications, where repetitive cw (continuous wave) and pulsed cw operation modes are required. When operating in such modes, the lasers experience numerous complete thermal cycles between "cold" heat sink temperature and the "hot" temperature typical of thermally equilibrated cw operation. It is clearly demonstrated that the main failure mechanism directly linked to repetitive cw operation is thermo-mechanical fatigue of the solder joints adjacent to the laser bars, especially when "soft" solders are used. Analyses of the bonding interfaces were carried out using scanning electron microscopy. It was observed that intermetallic compounds, formed already during the bonding process, lead to the solders fatigue both on the p- and n-side of the laser bar. Fatigue failure of solder joints in repetitive cw operation reduces useful lifetime of the stacks to hundreds hours, in comparison with more than 10,000 hours lifetime typically demonstrated in commonly adopted non-stop cw reliability testing programs. It is shown, that proper selection of package materials and solders, careful design of fatigue sensitive parts and burn-in screening in the hard pulse operation mode allow considerable increase of lifetime and reliability, without compromising the device efficiency, optical power density and compactness.

  1. Thermo-Mechanical Modeling of Laser-Mig Hybrid Welding (lmhw)

    Science.gov (United States)

    Kounde, Ludovic; Engel, Thierry; Bergheau, Jean-Michel; Boisselier, Didier

    2011-01-01

    Hybrid welding is a combination of two different technologies such as laser (Nd: YAG, CO2…) and electric arc welding (MIG, MAG / TIG …) developed to assemble thick metal sheets (over 3 mm) in order to reduce the required laser power. As a matter of fact, hybrid welding is a lso used in the welding of thin materials to benefit from process, deep penetration and gap limit. But the thermo-mechanical behaviour of thin parts assembled by LMHW technology for railway cars production is far from being controlled the modeling and simulation contribute to the assessment of the causes and effects of the thermo mechanical behaviour in the assembled parts. In order to reproduce the morphology of melted and heat-affected zones, two analytic functions were combined to model the heat source of LMHW. On one hand, we applied a so-called "diaboloïd" (DB) which is a modified hyperboloid, based on experimental parameters and the analysis of the macrographs of the welds. On the other hand, we used a so-called "double ellipsoïd" (DE) which takes the MIG only contribution including the bead into account. The comparison between experimental result and numerical result shows a good agreement.

  2. Reduced softening of EUROFER 97 under thermo-mechanical and multiaxial fatigue loading and its impact on the design rules

    International Nuclear Information System (INIS)

    Aktaa, J.; Weick, M.; Petersen, C.

    2007-01-01

    Full text of publication follows: Toward test blanket module (TBM) in ITER and DEMO fusion power plants design rules for components built from EUROFER 97 get more and more in the midpoint of interest. One of the specific characteristic of EUROFER 97 as a ferritic-martensitic steel is its cyclic softening yielding to lower stresses under strain controlled fatigue loading and thus longer lifetimes. However our thermo-mechanical and multiaxial fatigue tests showed lifetimes remarkably lower than those expected on the base of isothermal uniaxial fatigue tests. Reduced cyclic softening observed in these experiments is believed as one of the reasons of the shorter fatigue lifetimes. When applying the design rules, derived for EUROFER 97 on the base of isothermal uniaxial data considering the recommendations in the ASME and RCC-MR code, to our thermo-mechanical and multiaxial fatigue tests for verification strong loss in their conservatism has been found. The lifetimes observed in a part of the multiaxial experiments are even lower than the design lifetimes supposed to be sufficiently conservative. To overcome this problem new design rules are proposed among others on the base of damage and lifetime prediction model developed lately for EUROFER 97. In this paper the experimental findings as well as the new design approaches will be presented and discussed. (authors)

  3. Numerical simulation for the coupled thermo-mechanical performance of a lined rock cavern for underground compressed air energy storage

    Science.gov (United States)

    Zhou, Shu-Wei; Xia, Cai-Chu; Zhao, Hai-Bin; Mei, Song-Hua; Zhou, Yu

    2017-12-01

    Compressed air energy storage (CAES) is a technology that uses compressed air to store surplus electricity generated from low power consumption time for use at peak times. This paper presents a thermo-mechanical modeling for the thermodynamic and mechanical responses of a lined rock cavern used for CAES. The simulation was accomplished in COMSOL Multiphysics and comparisons of the numerical simulation and some analytical solutions validated the thermo-mechanical modeling. Air pressure and temperatures in the sealing layer and concrete lining exhibited a similar trend of ‘up-down-down-up’ in one cycle. Significant temperature fluctuation occurred only in the concrete lining and sealing layer, and no strong fluctuation was observed in the host rock. In the case of steel sealing, principal stresses in the sealing layer were larger than those in the concrete and host rock. The maximum compressive stresses of the three layers and the displacement on the cavern surface increased with the increase of cycle number. However, the maximum tensile stresses exhibited the opposite trend. Polymer sealing achieved a relatively larger air temperature and pressure compared with steel and air-tight concrete sealing. For concrete layer thicknesses of 0 and 0.1 m and an initial air pressure of 4.5 MPa, the maximum rock temperature could reach 135 °C and 123 °C respectively in a 30 day simulation.

  4. High energy flux thermo-mechanical test of 1D-carbon-carbon fibre composite prototypes for the SPIDER diagnostic calorimeter

    International Nuclear Information System (INIS)

    De Muri, M.; Pasqualotto, R.; Dalla Palma, M.; Cervaro, V.; Fasolo, D.; Franchin, L.; Tollin, M.; Serianni, G.; Cavallin, T.; Greuner, H.; Böswirth, B.

    2014-01-01

    Operation of the thermonuclear fusion experiment ITER requires additional heating via injection of neutral beams from accelerated negative ions. In the SPIDER test facility, under construction in Padova, the production of negative ions will be studied and optimised. STRIKE (Short-Time Retractable Instrumented Kalorimeter Experiment) is a diagnostic used to characterise the SPIDER beam during short pulse operation (several seconds) to verify if the beam meets the ITER requirements about the maximum allowed beam non-uniformity (below ±10%). The major components of STRIKE are 16 1D-CFC (Carbon-Carbon Fibre Composite) tiles, observed at the rear side by a thermal camera. This contribution gives an overview of some tests under high energy particle flux, aimed at verifying the thermo-mechanical behaviour of several CFC prototype tiles. The tests were performed in the GLADIS facility at IPP (Max-Plank-Institut für Plasmaphysik), Garching. Dedicated linear and nonlinear simulations were carried out to interpret the experiments and a comparison of the experimental data with the simulation results is presented. The results of some morphological and structural studies on the material after exposure to the GLADIS beam are also given

  5. Thermal and thermomechanical analyses of WIPP [Waste Isolation Pilot Plant] shaft seals: Topical report RSI-0324

    International Nuclear Information System (INIS)

    Van Sambeek, L.L.

    1987-10-01

    Thermal and thermomechanical analyses provided information on the behavior and stability of concrete seals emplaced in a circular shaft. The two types of concrete considered were an expansive salt-saturated concrete for seals located in rock salt or other rock and an expansive freshwater concrete for seals located in nonsalt rock. Thermal analyses determined the temperature rise in the concrete and surrounding rock as a result of the exothermic hydration of the cement in the concretes. The thermomechanical analyses considered time-dependent elastic modulus, thermoelastic expansion, time-dependent chemically induced expansion, and creep of the concrete; thermoelastic behavior of the nonsalt rocks; and thermoelastic and creep behavior of the rock salt. Supplementary analyses determined the effects of pressure loading on a face of the seal as might result from a static brine head or the swelling of a bentonite backfill; the influence of using a reduced elastic modulus for the rock salt; and the effect of eliminating the chemical expansivity of the concrete. Results of interest were the development of radial stress in the seal, the magnitudes of tensile and shear stresses induced in the seal and rock, and the effect of bonding or lack of bonding between the seal and the surrounding rock. The chemical expansivity of the concrete was shown to be important for the development of radial stresses in the seal and at the contact between the seal and the surrounding rock. The shear stresses induced in the seal by the swelling pressure of bentonite become a concern if the radial stresses are not developed. 20 refs., 58 figs., 3 tabs

  6. Amplitude Dependent Internal Friction in a Mg-Al-Zn Alloy Studied after Thermal and Mechanical Treatment

    Directory of Open Access Journals (Sweden)

    Zuzanka Trojanová

    2017-10-01

    Full Text Available The amplitude-dependent internal friction of continuously-cast and rolled AZ31 magnesium alloy was measured in this study. Samples were annealed and quenched step by step; immediately after the treatment, the amplitude dependence of the logarithmic decrement was measured. Changes in the microstructure due to thermomechanical treatment were reflected in changes in the damping. Internal friction is influenced by the dislocation substructure and its modification due to solute atoms migration, microplastic deformation, and twins’ formation. Internal friction in the rolled sheets is affected by the rolling texture.

  7. Numerical simulation of residual stress in laser based additive manufacturing process

    Science.gov (United States)

    Kalyan Panda, Bibhu; Sahoo, Seshadev

    2018-03-01

    Minimizing the residual stress build-up in metal-based additive manufacturing plays a pivotal role in selecting a particular material and technique for making an industrial part. In beam-based additive manufacturing, although a great deal of effort has been made to minimize the residual stresses, it is still elusive how to do so by simply optimizing the processing parameters, such as beam size, beam power, and scan speed. Amid different types of additive manufacturing processes, Direct Metal Laser Sintering (DMLS) process uses a high-power laser to melt and sinter layers of metal powder. The rapid solidification and heat transfer on powder bed endows a high cooling rate which leads to the build-up of residual stresses, that will affect the mechanical properties of the build parts. In the present work, the authors develop a numerical thermo-mechanical model for the measurement of residual stress in the AlSi10Mg build samples by using finite element method. Transient temperature distribution in the powder bed was assessed using the coupled thermal to structural model. Subsequently, the residual stresses were estimated with varying laser power. From the simulation result, it found that the melt pool dimensions increase with increasing the laser power and the magnitude of residual stresses in the built part increases.

  8. Thermo-mechanical models of obduction applied to the Oman ophiolite

    Science.gov (United States)

    Thibault, Duretz; Philippe, Agard; Philippe, Yamato; Céline, Ducassou; Taras, Gerya; Evguenii, Burov

    2015-04-01

    During obduction regional-scale fragments of oceanic lithosphere (ophiolites) are emplaced somewhat enigmatically on top of lighter continental lithosphere. We herein use two-dimensional thermo-mechanical models to investigate the feasibility and controlling parameters of obduction. The models are designed using available geological data from the Oman (Semail) ophiolite. Initial and boundary conditions are constrained by plate kinematic and geochronological data and modeling results are validated against petrological and structural observations. The reference model consists of three distinct stages: (1) initiation of oceanic subduction initiation away from Arabian margin, (2) emplacement of the Oman Ophiolite atop the Arabian margin, (2) dome-like exhumation of the subducted Arabian margin beneath the overlying ophiolite. A parametric study suggests that 350-400 km of shortening allows to best fit both the peak P-T conditions of the subducted margin (1.5-2.5 GPa / 450-600°C) and the dimensions of the ophiolite (~170 km width), in agreement with previous estimations. Our results further confirm that the locus of obduction initiation is close to the eastern edge of the Arabian margin (~100 km) and indicate that obduction is facilitated by a strong continental basement rheology.

  9. Thermomechanical analyses of phenolic foam reinforced with glass fiber mat

    International Nuclear Information System (INIS)

    Zhou, Jintang; Yao, Zhengjun; Chen, Yongxin; Wei, Dongbo; Wu, Yibing

    2013-01-01

    Highlights: • Over 10% glass fiber was used to reinforce phenolic foam in the shape of glass fiber mat. • Nucleating agents were used together with glass fiber mat and improved tensile strength of phenolic foam by 215.6%. • Nucleating agents lead to a smaller bubble size of phenolic foam. • The glass transition temperature of phenolic foam remained unchanged during the reinforcement. - Abstract: In this paper, thermomechanical analysis (TMA) and dynamic mechanical analysis were employed to study the properties of phenolic foam reinforced with glass fiber mat. Unreinforced phenolic foam was taken as the control sample. Mechanical tests and scanning electron microscopy were performed to confirm the results of TMA. The results show that glass fiber mat reinforcement improves the mechanical performance of phenolic foam, and nucleating agents improve it further. Phenolic foam reinforced with glass fiber mat has a smaller thermal expansion coefficient compared with unreinforced foam. The storage modulus of the reinforced phenolic foam is also higher than that in unreinforced foam, whereas the loss modulus of the former is lower than that of the latter. The glass transition temperature of the phenolic foam matrix remains unchanged during the reinforcement

  10. Thermomechanical Fatigue of Ductile Cast Iron and Its Life Prediction

    Science.gov (United States)

    Wu, Xijia; Quan, Guangchun; MacNeil, Ryan; Zhang, Zhong; Liu, Xiaoyang; Sloss, Clayton

    2015-06-01

    Thermomechanical fatigue (TMF) behaviors of ductile cast iron (DCI) were investigated under out-of-phase (OP), in-phase (IP), and constrained strain-control conditions with temperature hold in various temperature ranges: 573 K to 1073 K, 723 K to 1073 K, and 433 K to 873 K (300 °C to 800 °C, 450 °C to 800 °C, and 160 °C to 600 °C). The integrated creep-fatigue theory (ICFT) model was incorporated into the finite element method to simulate the hysteresis behavior and predict the TMF life of DCI under those test conditions. With the consideration of four deformation/damage mechanisms: (i) plasticity-induced fatigue, (ii) intergranular embrittlement, (iii) creep, and (iv) oxidation, as revealed from the previous study on low cycle fatigue of the material, the model delineates the contributions of these physical mechanisms in the asymmetrical hysteresis behavior and the damage accumulation process leading to final TMF failure. This study shows that the ICFT model can simulate the stress-strain response and life of DCI under complex TMF loading profiles (OP and IP, and constrained with temperature hold).

  11. Dynamic thermomechanical response of bimaterial microcantilevers to periodic heating by infrared radiation.

    Science.gov (United States)

    Kwon, Beomjin; Rosenberger, Matthew; Bhargava, Rohit; Cahill, David G; King, William P

    2012-01-01

    This paper investigates the dynamic thermomechanical response of bimaterial microcantilevers to periodic heating by an infrared laser operating at a wavelenegth of 10.35 μm. A model relates incident radiation, heat transfer, temperature distribution in the cantilever, and thermal expansion mismatch to find the cantilever displacement. Experiments were conducted on two custom-fabricated bimaterial cantilevers and two commercially available bimaterial microcantilevers. The cantilever response was measured as a function of the modulation frequency of the laser over the range of 0.01-30 kHz. The model and the method of cantilever displacement calibration can be applied for bimaterial cantilever with thick coating layer. The sensitivity and signal-to-noise of bimaterial cantilevers were evaluated in terms of either total incident power or incident flux. The custom-fabricated bimaterial cantilevers showed 9X or 190X sensitivity improvement compared to commercial cantilevers. The detection limit on incident flux is as small as 0.10 pW μm(-2) Hz(-1/2).

  12. Thermo-mechanical properties of W/Mo markers coatings deposited on bulk W

    International Nuclear Information System (INIS)

    Grigore, E; Ruset, C; Gherendi, M; Chioibasu, D; Hakola, A

    2016-01-01

    In the present paper marker structures consisting of W/Mo layers were deposited on bulk W samples by using a modified CMSII method. This technology, compared to standard CMSII, prevents the formation of nano-pore structures at interfaces. The thicknesses of the markers were in the range 20–35 μm to balance the requirements associated with the wall erosion in ITER and thermo-mechanical performances. The coatings structure and composition were evaluated by glow discharge optical emission spectrometry (GDOES), and energy dispersive x-ray spectroscopy measurements (EDX). The adhesion of the coatings to the substrate has been assessed by scratch test method. In order to evaluate their effectiveness as potential markers for fusion applications, the marker coatings have been tested in an electron beam facility at a temperature of 1000 °C and a power density of about 3 MW m −2 . A number of 300 pulses with duration of 420 s (35 testing hours) were applied on the marker coated samples. (paper)

  13. Thermo-mechanical properties of W/Mo markers coatings deposited on bulk W

    Science.gov (United States)

    Grigore, E.; Ruset, C.; Gherendi, M.; Chioibasu, D.; Hakola, A.; contributors, JET

    2016-02-01

    In the present paper marker structures consisting of W/Mo layers were deposited on bulk W samples by using a modified CMSII method. This technology, compared to standard CMSII, prevents the formation of nano-pore structures at interfaces. The thicknesses of the markers were in the range 20-35 μm to balance the requirements associated with the wall erosion in ITER and thermo-mechanical performances. The coatings structure and composition were evaluated by glow discharge optical emission spectrometry (GDOES), and energy dispersive x-ray spectroscopy measurements (EDX). The adhesion of the coatings to the substrate has been assessed by scratch test method. In order to evaluate their effectiveness as potential markers for fusion applications, the marker coatings have been tested in an electron beam facility at a temperature of 1000 °C and a power density of about 3 MW m-2. A number of 300 pulses with duration of 420 s (35 testing hours) were applied on the marker coated samples.

  14. Thermo-mechanical modelling and experimental validation of CLIC prototype module type 0

    CERN Document Server

    Kortelainen, Lauri; Koivurova, Hannu; Riddone, Germana; Österberg, Kenneth

    Micron level stability of the two-meter repetitive modules constituting the two main linacs is one of the most important requirements to achieve the luminosity goal for the Compact Linear Collider. Structural deformations due to thermal loads and related to the RF power dissipated inside the modules affect the alignment of the linacs and therefore the resulting luminosity performance. A CLIC prototype module has been assembled in a dedicated laboratory and a thermal test program has been started in order to study its thermo-mechanical behaviour. This thesis focuses on the finite elements modelling of the first CLIC prototype module 0. The aim of the modelling is to examine the temperature distributions and the resulting deformations of the module in different operating conditions defined in the thermal test program. The theoretical results have been compared to the experimental ones; the comparison shows that the results are in good agreement both for the thermal behaviour of the module and for the resulting ...

  15. Enhanced treatment of waste frying oil in an activated sludge system by addition of crude rhamnolipid solution.

    Science.gov (United States)

    Zhang, Hongzi; Xiang, Hai; Zhang, Guoliang; Cao, Xia; Meng, Qing

    2009-08-15

    The presence of high-strength oil and grease (O&G) in wastewater poses serious challenges for environment. Addition of surfactant into the activated sludge bioreactor is feasible in reducing high concentrations of O&G via enhancing its bioavailability. In this paper, an aqueous biosurfactant solution of rhamnolipid as a cell-free culture broth of Pseudomonas aeruginosa zju.um1 was added into a batch of aerobic activated sludge system for treatment of the waste frying oil. This treatment was conducted on both bench and pilot-scales, whereas the removal efficiency of frying oil was determined by analyzing the residue concentration of O&G and chemical oxygen demand (COD). In the presence of varying concentrations of rhamnolipid from 22.5 mg/L to 90 mg/L, aerobic treatment for 30 h was enough to remove over 93% of O&G while this biodegradability was only 10% in the control system with the absence of rhamnolipids. The equivalent biodegradability was similarly obtained on COD under addition of rhamnolipid. Compared with bench studies, a higher treatment efficiency with the presence of rhamnolipids was achieved on a pilot-scale of activated sludge system, in which a short time of 12h was required for removing approximately 95% of O&G while the control treatment attained a low efficiency of 17%. Finally, foaming and biodegradability of rhamnolipids in activated sludge system were further examined in the whole treatment process. It seems that the addition of rhamnolipid-containing culture broth showed great potential for treatment of oily wastewater by activated sludge.

  16. Enhanced treatment of waste frying oil in an activated sludge system by addition of crude rhamnolipid solution

    International Nuclear Information System (INIS)

    Zhang Hongzi; Xiang Hai; Zhang Guoliang; Cao Xia; Meng Qing

    2009-01-01

    The presence of high-strength oil and grease (O and G) in wastewater poses serious challenges for environment. Addition of surfactant into the activated sludge bioreactor is feasible in reducing high concentrations of O and G via enhancing its bioavailability. In this paper, an aqueous biosurfactant solution of rhamnolipid as a cell-free culture broth of Pseudomonas aeruginosa zju.um1 was added into a batch of aerobic activated sludge system for treatment of the waste frying oil. This treatment was conducted on both bench and pilot-scales, whereas the removal efficiency of frying oil was determined by analyzing the residue concentration of O and G and chemical oxygen demand (COD). In the presence of varying concentrations of rhamnolipid from 22.5 mg/L to 90 mg/L, aerobic treatment for 30 h was enough to remove over 93% of O and G while this biodegradability was only 10% in the control system with the absence of rhamnolipids. The equivalent biodegradability was similarly obtained on COD under addition of rhamnolipid. Compared with bench studies, a higher treatment efficiency with the presence of rhamnolipids was achieved on a pilot-scale of activated sludge system, in which a short time of 12 h was required for removing approximately 95% of O and G while the control treatment attained a low efficiency of 17%. Finally, foaming and biodegradability of rhamnolipids in activated sludge system were further examined in the whole treatment process. It seems that the addition of rhamnolipid-containing culture broth showed great potential for treatment of oily wastewater by activated sludge.

  17. Effects of boundary conditions on thermomechanical calculations: Spent fuel test - climax

    International Nuclear Information System (INIS)

    Butkovich, T.R.

    1982-10-01

    The effects of varying certain boundary conditions on the results of finite-element calculations were studied in relation to the Spent Fuel Test - Climax. The study employed a thermomechanical model with the ADINA structural analysis. Nodal temperature histories were generated with the compatible ADINAT heat flow codes. The boundary conditions studied included: (1) The effect of boundary loading on three progressively larger meshes. (2) Plane strain vs plane stress conditions. (3) The effect of isothermal boundaries on a small mesh and on a significantly larger mesh. The results showed that different mesh sizes had an insignificant effect on isothermal boundaries up to 5 y, while on the smallest and largest mesh, the maximum temperature difference in the mesh was 0 C. In the corresponding ADINA calculation, these different mesh sizes produce insignificant changes in the stress field and displacements in the region of interest near the heat sources and excavations. On the other hand, plane stress produces horizontal and vertical stress differences approx. 9% higher than does plane strain

  18. Validating predictions made by a thermo-mechanical model of melt segregation in sub-volcanic systems

    Science.gov (United States)

    Roele, Katarina; Jackson, Matthew; Morgan, Joanna

    2014-05-01

    consistent with the real data. This highlights improvements that could be made to the thermo-mechanical model, such as an extension into 3-D that would be capable of capturing the effects of convective instabilities. In addition, it describes how far numerical models are capable of reducing the uncertainty in the parameter space for poorly defined crustal properties. Most importantly however, it gives an improved understanding of the intrusion and development of melt zones in the continental crust that ultimately control the formation of volcanic systems. [1] Solano, J. M. S., M. D. Jackson, R. S. J. Sparks, J. D. Blundy, and C. Annen (2012). Melt segregation in deep crustal hot zones: a mechanism for chemical differentiation, crustal assimilation and the formation of evolved magmas. Journal of Petrology, 53, Number 10, Pages 1999-2026. DOI: 10.1093/petrology/egs041.

  19. Rock mechanical, thermomechanical and hydraulic behaviour of the near field for spent nuclear fuel

    International Nuclear Information System (INIS)

    Johansson, E.; Hakala, M.; Lorig, L.J.

    1991-10-01

    Teollisuuden Voima Oy (TVO) is investigating the feasibility of disposing high level nuclear waste in crystalline rock at depths of 400 to 600 meters below the ground surface. Two explicit distinct element computer codes UDEC and 3DEC were used to simulate the mechanical response associated with excavation and the thermomechanical response associated with waste emplacement. Model input data are mostly based on preliminary design of the repository and on field data from on-going site investigations in Finland. The results showed that the overall stability of the repository near-field appears to be good during the studied time period 0 - 900 years. The maximum displacements after excavation are about 2 mm on the walls of the disposal tunnel. Joint openings are only a few micrometers. The hydraulic conductivity increases by 4 to 6 times within the zone of 0,3 m around the tunnel and emplacement hole, and farther away the average increase in conductivity is 1,2 to 1,7 times. After 60 years the heating increases the stresses in the vicinity of the excavated rooms, and closes the joints decreasing the hydraulic conductivity by 93 - 99 % when assuming 10 μm in-situ hydraulic aperture. However, when assuming 50 μm in-situ hydraulic aperture the hydraulic conductivity increases 10 - 40 % because the change in dynamic viscosity of water has a larger effect than the joint aperture change. After 900 years in the cooling stage the stresses and displacements come back almost to the same level as after the excavation. Some permanent displacements remain in the joints due to the shearing. The hydraulic conductivity at 900 years is 10 - 70 % of the conductivity after the excavation. The comparisons between the 2-D and 3-D results show that the two-dimensional modeling, if sufficient cross-sections have been analyzed, is enough to describe mechanical behaviour of the near-field, whereas the three-dimensional modeling is needed in some cases to assess the thermomechanical behaviour

  20. Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

    Energy Technology Data Exchange (ETDEWEB)

    Misra, R.D.K., E-mail: dmisra@louisiana.edu [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); Jia, Z. [Center for Structural and Functional Materials, University of Louisiana at Lafayette, P.O. Box 44130, Lafayette, LA 70503 (United States); O' Malley, R. [Nucor Steel Decatur, LLC Sheet Mill, 4301, Iverson Blvd., Trinity, AL 35673 (United States); Jansto, S.J. [CBMM-Reference Metals Company, 1000 Old Pond Road, Bridgeville, PA 15017 (United States)

    2011-11-15

    Highlights: {yields} Copper does not significantly influence toughness. {yields} Copper precipitation during aging occurs at dislocations. {yields} Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of {epsilon}-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of {epsilon}-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

  1. Precipitation behavior during thin slab thermomechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength structural steels: The effect on mechanical properties

    International Nuclear Information System (INIS)

    Misra, R.D.K.; Jia, Z.; O'Malley, R.; Jansto, S.J.

    2011-01-01

    Highlights: → Copper does not significantly influence toughness. → Copper precipitation during aging occurs at dislocations. → Precipitation of copper and carbides is mutually exclusive. - Abstract: We describe here the precipitation behavior of copper and fine-scale carbides during thermo-mechanical processing and isothermal aging of copper-bearing niobium-microalloyed high strength steels. During thermo-mechanical processing, precipitation of ε-copper occurs in polygonal ferrite and at the austenite-ferrite interface. In contrast, during isothermal aging, nucleation of ε-copper precipitation occurs at dislocations. In the three different chemistries investigated, the increase in strength associated with copper during aging results only in a small decrease in impact toughness, implying that copper precipitates do not seriously impair toughness, and can be considered as a viable strengthening element in microalloyed steels. Precipitation of fine-scale niobium carbides occurs extensively at dislocations and within ferrite matrix together with vanadium carbides. In the presence of titanium, titanium carbides act as a nucleus for niobium carbide formation. Irrespective of the nature of carbides, copper precipitates and carbides are mutually exclusive.

  2. Full-scale effects of addition of sludge from water treatment stations into processes of sewage treatment by conventional activated sludge.

    Science.gov (United States)

    Luiz, Marguti André; Sidney Seckler, Ferreira Filho; Passos, Piveli Roque

    2018-06-01

    An emerging practice for water treatment plant (WTP) sludge is its disposal in wastewater treatment plants (WWTP), an alternative that does not require the installation of sludge treatment facilities in the WTP. This practice can cause both positive and negative impacts in the WWTP processes since the WTP sludge does not have the same characteristics as domestic wastewater. This issue gives plenty of information in laboratory and pilot scales, but lacks data from full-scale studies. The main purpose of this paper is to study the impact of disposing sludge from the Rio Grande conventional WTP into the ABC WWTP, an activated sludge process facility. Both plants are located in São Paulo, Brazil, and are full-scale facilities. The WTP volumetric flow rate (4.5 m³/s) is almost three times that of WWTP (1.6 m³/s). The data used in this study came from monitoring the processes at both plants. The WWTP liquid phase treatment analysis included the variables BOD, COD, TSS, VSS, ammonia, total nitrogen, phosphorus and iron, measured at the inlet, primary effluent, mixed liquor, and effluent. For the WWTP solids treatment, the parameters tested were total and volatile solids. The performance of the WWTP process was analyzed with and without sludge addition: 'without sludge' in years 2005 and 2006 and 'with sludge' from January 2007 to March 2008. During the second period, the WTP sludge addition increased the WWTP removal efficiencies for solids (93%-96%), organic matter (92%-94% for BOD) and phosphorus (52%-88%), when compared to the period 'without sludge'. These improvements can be explained by higher feed concentrations combined to same or lower effluent concentrations in the 'with sludge' period. No critical negative impacts occurred in the sludge treatment facilities, since the treatment units absorbed the extra solids load from the WTP sludge. Copyright © 2018 Elsevier Ltd. All rights reserved.

  3. Micro-thermomechanical constitutive model of transformation induced plasticity and its application on armour steel

    Energy Technology Data Exchange (ETDEWEB)

    Sun, C.Y. [School of Mechanical Engineering, University of Science and Technology Beijing, Beijing 100083 (China)], E-mail: suncy@me.ustb.edu.cn; Fang, G.; Lei, L.P.; Zeng, P. [Key Laboratory of Advanced Materials Processing Technology, Ministry of Education, Department of Mechanical Engineering, Tsinghua University, Beijing 100084 (China)

    2009-01-15

    Based on the crystallographic theory of martensitic transformation and internal variable constitutive theory, a micromechanical constitutive model of martensitic transformation induced plasticity was developed. Plastic strains of product and parent phases as well as the volume fraction of each martensitic variant were considered as internal variables describing the microstructure evolution. The plasticity flow both in austenite and martensitic variants domain is described by J{sub 2} flow theory. The thermodynamic driving force acting on these internal variables was obtained through the determination of the intrinsic dissipation due to plastic flow and the growth of martensitic domains. The evolution laws of the internal variables are derived, furthermore macroscopic response due to the change of internal variables is obtained. Thermomechanical behavior of armour steel under uniaxial loading was tested which showed a good agreement with experimental results.

  4. Micro-thermomechanical constitutive model of transformation induced plasticity and its application on armour steel

    International Nuclear Information System (INIS)

    Sun, C.Y.; Fang, G.; Lei, L.P.; Zeng, P.

    2009-01-01

    Based on the crystallographic theory of martensitic transformation and internal variable constitutive theory, a micromechanical constitutive model of martensitic transformation induced plasticity was developed. Plastic strains of product and parent phases as well as the volume fraction of each martensitic variant were considered as internal variables describing the microstructure evolution. The plasticity flow both in austenite and martensitic variants domain is described by J 2 flow theory. The thermodynamic driving force acting on these internal variables was obtained through the determination of the intrinsic dissipation due to plastic flow and the growth of martensitic domains. The evolution laws of the internal variables are derived, furthermore macroscopic response due to the change of internal variables is obtained. Thermomechanical behavior of armour steel under uniaxial loading was tested which showed a good agreement with experimental results

  5. Design of durability and lifetime assessment method under thermomechanical stress for thermal barrier coatings

    Energy Technology Data Exchange (ETDEWEB)

    Shin, Hyun Gyoo; Choi, Young Kue; Jeon, Seol; Lee, Hee Soo [Pusan National University, Busan (Korea, Republic of); Jeon, Min Seok [Korea Testing Laboratory, Seoul (Korea, Republic of)

    2014-01-15

    A durability testing method under thermo-mechanical stress for thermal barrier coatings (TBC) specimens was designed by a combination of an electric furnace and a tensile testing machine, which was done on TBCs on NIMONIC 263 substrates by an atmospheric plasma spraying (APS) deposition method. The testing conditions were chosen according to a preliminary experiment that identified the elastic deformation region of the top coating and the substrate during mechanical loading. Surface cracking and a decrease in the thickness of the top coating, which are typical degradation behaviors under conventional thermal shock testing, were observed after the designed thermal fatigue test, and delamination at the top coating-bond coating interface occurred by the mechanical load. Lifetime assessment was conducted by statistical software using life cycle data which were obtained after the thermal fatigue test.

  6. Development of antimicrobial active packaging materials based on gluten proteins.

    Science.gov (United States)

    Gómez-Heincke, Diana; Martínez, Inmaculada; Partal, Pedro; Guerrero, Antonio; Gallegos, Críspulo

    2016-08-01

    The incorporation of natural biocide agents into protein-based bioplastics, a source of biodegradable polymeric materials, manufactured by a thermo-mechanical method is a way to contribute to a sustainable food packaging industry. This study assesses the antimicrobial activity of 10 different biocides incorporated into wheat gluten-based bioplastics. The effect that formulation, processing, and further thermal treatments exert on the thermo-mechanical properties, water absorption characteristics and rheological behaviour of these materials is also studied. Bioplastics containing six of the 10 examined bioactive agents have demonstrated suitable antimicrobial activity at 37 °C after their incorporation into the bioplastic. Moreover, the essential oils are able to create an antimicrobial atmosphere within a Petri dish. Depending on the selected biocide, its addition may alter the bioplastics protein network in a different extent, which leads to materials exhibiting less water uptake and different rheological and thermo-mechanical behaviours. © 2015 Society of Chemical Industry. © 2015 Society of Chemical Industry.

  7. Mechanical Characterization and Corrosion Testing of X608 Al Alloy

    Energy Technology Data Exchange (ETDEWEB)

    Prabhakaran, Ramprashad; Choi, Jung-Pyung; Stephens, Elizabeth V.; Catalini, David; Lavender, Curt A.; Rohatgi, Aashish

    2016-02-07

    This paper describes the mechanical characterization and corrosion testing of X608 Al alloy that is being considered for A-pillar covers for heavy-duty truck applications. Recently, PNNL developed a thermo-mechanical process to stamp A-pillar covers at room temperature using this alloy, and the full-size prototype was successfully stamped by a tier-1 supplier. This study was conducted to obtain additional important information related to the newly developed forming process, and to further improve its mechanical properties. The solutionization temperature, pre-strain and paint-bake heat-treatment were found to influence the alloy’s fabricability and mechanical properties. Natural aging effect on the formability was investigated by limiting dome height (LDH) tests. Preliminary corrosion experiments showed that the employed thermo-mechanical treatments did not significantly affect the corrosion behavior of Al X608.

  8. Petri neural network model for the effect of controlled thermomechanical process parameters on the mechanical properties of HSLA steels

    Energy Technology Data Exchange (ETDEWEB)

    Datta, S.

    1999-10-01

    The effect of composition and controlled thermomechanical process parameters on the mechanical properties of HSLA steels is modelled using the Widrow-Hoff's concept of training a neural net with feed-forward topology by applying Rumelhart's back propagation type algorithm for supervised learning, using a Petri like net structure. The data used are from laboratory experiments as well as from the published literature. The results from the neural network are found to be consistent and in good agreement with the experimented results. (author)

  9. Microstructure evolution and texture development in thermomechanically processed Mg-Li-Al based alloys

    Energy Technology Data Exchange (ETDEWEB)

    Kumar, Vinod [Department of Materials Science and Engineering, IIT Kanpur (India); Govind [Vikram Sarabhai Space Center, Trivandrum (India); Shekhar, Rajiv; Balasubramaniam, R. [Department of Materials Science and Engineering, IIT Kanpur (India); Balani, Kantesh, E-mail: kbalani@iitk.ac.in [Department of Materials Science and Engineering, IIT Kanpur (India)

    2012-06-15

    Highlights: Black-Right-Pointing-Pointer Thermomechanical processing of novel LAT 971 and LATZ 9531 Mg-Al-Li based alloys. Black-Right-Pointing-Pointer Microstructural deviation from the equilibrium phase diagram. Black-Right-Pointing-Pointer Disparity in texture of these alloys after hot-rolling (recrystallization and grain growth). Black-Right-Pointing-Pointer Role of alloying and phase distribution in affecting the texture/interplaner spacing. - Abstract: In the present study, the influence of alloying and thermomechanical processing on the microstructure and texture evolution on the two Mg-Li-Al based alloys, namely Mg-9 wt% Li-7 wt% Al-1 wt% Sn (LAT971) and Mg-9 wt% Li-5 wt% Al-3 wt% Sn-1 wt% Zn (LATZ9531) has been elicited. Novel Mg-Li-Al based alloys were cast (induction melting under protective atmosphere) followed by hot rolling at {approx}573 K with a cumulative reduction of five. A contrary dual phase dendritic microstructure rich in {alpha}-Mg, instead of {beta}-Li phase predicted by equilibrium phase diagram of Mg-Li binary alloy was observed. Preferential presence of Mg-Li-Sn primary precipitates (size 4-10 {mu}m) within {alpha}-Mg phase and Mg-Li-Al secondary precipitates (<3 {mu}m) interspersed in {beta}-Li indicated their degree of dissolution during hot-rolling and homogenization in the dual phase matrix. Presence of Al, Sn and Zn alloying elements in the Mg-Li based alloy has resulted an unusual dual-phase microstructure, change in the lattice parameter, and intriguing texture evolution after hot-rolling of cast LAT 971 and LATZ9531 alloy. Strong texture was absent in the as-cast samples whereas texture development after hot-rolling revealed an increased activity of the non-basal (101{sup Macron }0) slip planes. The quantification of the grain average misorientation (less than 2 Degree-Sign ) using electron backscattered diffraction confirmed the presence of strain free grains in majority of the grains (fraction >0.75) after hot-rolling of Mg

  10. Structural and thermomechanical properties of the zinc-blende AlX (X = P, As, Sb) compounds

    Science.gov (United States)

    Ha, Vu Thi Thanh; Hung, Vu Van; Hanh, Pham Thi Minh; Nguyen, Viet Tuyen; Hieu, Ho Khac

    2017-08-01

    The structural and thermomechanical properties of zinc-blende aluminum class of III-V compounds have been studied based on the statistical moment method (SMM) in quantum statistical mechanics. Within the SMM scheme, we derived the analytical expressions of the nearest-neighbor distance, thermal expansion coefficient, atomic mean-square displacement and elastic moduli (Young’s modulus, bulk modulus and shear modulus). Numerical calculations have been performed for zinc-blende AlX (X = As, P, Sb) at ambient conditions up to the temperature of 1000 K. Our results are in good and reasonable agreements with earlier measurements and can provide useful references for future experimental and theoretical works. This research presents a systematic approach to investigate the thermodynamic and mechanical properties of materials.

  11. Effects of thermomechanical processing on microstructure and properties of bainitic work hardening steel

    Energy Technology Data Exchange (ETDEWEB)

    Cao, Jie, E-mail: caojie910@ahut.edu.cn [School of Metallurgical Engineering, Anhui University of Technology, Ma’anshan 243002 (China); Yan, Jun; Zhang, Jing [School of Metallurgical Engineering, Anhui University of Technology, Ma’anshan 243002 (China); Yu, Tongren [Technology Center, Maanshan Iron & Steel Company Limited, Ma’anshan 243000 (China)

    2015-07-15

    The thermomechanical processing (TMP) of a bainitic work hardening steel was carried out on a Gleeble3500 simulator. The microstructure of processed specimens was investigated by means of optical and electron microscopy, and tensile tests were performed in a ZwickRoell tensile tester. The deformation temperatures of austenite varied from 800 °C to 900 °C. The cooling methods include single rate cooling method and two-stage cooling method. The two-stage cooling method includes fast cooling rates ranging from 4 °C/s to 12 °C/s and slow cooling rates ranging from 1 °C/s to 2 °C/s. It is shown that, within the range of parameters tested, the obtained microstructures are granular bainite, the tensile strength of the steel can be adjusted from 897.8 MPa to 1083.2 MPa, and good plasticity can be obtained at different strength levels.

  12. The effects of short-lived radionuclides and porosity on the early thermo-mechanical evolution of planetesimals

    Science.gov (United States)

    Lichtenberg, Tim; Golabek, Gregor J.; Gerya, Taras V.; Meyer, Michael R.

    2016-08-01

    The thermal history and internal structure of chondritic planetesimals, assembled before the giant impact phase of chaotic growth, potentially yield important implications for the final composition and evolution of terrestrial planets. These parameters critically depend on the internal balance of heating versus cooling, which is mostly determined by the presence of short-lived radionuclides (SLRs), such as 26Al and 60Fe, as well as the heat conductivity of the material. The heating by SLRs depends on their initial abundances, the formation time of the planetesimal and its size. It has been argued that the cooling history is determined by the porosity of the granular material, which undergoes dramatic changes via compaction processes and tends to decrease with time. In this study we assess the influence of these parameters on the thermo-mechanical evolution of young planetesimals with both 2D and 3D simulations. Using the code family I2ELVIS/I3ELVIS we have run numerous 2D and 3D numerical finite-difference fluid dynamic models with varying planetesimal radius, formation time and initial porosity. Our results indicate that powdery materials lowered the threshold for melting and convection in planetesimals, depending on the amount of SLRs present. A subset of planetesimals retained a powdery surface layer which lowered the thermal conductivity and hindered cooling. The effect of initial porosity was small, however, compared to those of planetesimal size and formation time, which dominated the thermo-mechanical evolution and were the primary factors for the onset of melting and differentiation. We comment on the implications of this work concerning the structure and evolution of these planetesimals, as well as their behavior as possible building blocks of terrestrial planets.

  13. Thermo-mechanical characterization of ceramic pebbles for breeding blanket

    Energy Technology Data Exchange (ETDEWEB)

    Lo Frano, Rosa, E-mail: rosa.lofrano@ing.unipi.it; Aquaro, Donato; Scaletti, Luca

    2016-11-01

    Highlights: • Experimental activities to characterize the Li{sub 4}SiO{sub 4}. • Compression tests of pebbles. • Experimental evaluation of thermal conductivity of pebbles bed at different temperatures. • Experimental test with/without compression load. - Abstract: An open issue for fusion power reactor is to design a suitable breeding blanket capable to produce the necessary quantity of the tritium and to transfer the energy of the nuclear fusion reaction to the coolant. The envisaged solution called Helium-Cooled Pebble Bed (HCPB) breeding blanket foresees the use of lithium orthosilicate (Li{sub 4}SiO{sub 4}) or lithium metatitanate (Li{sub 2}TiO{sub 3}) pebble beds. The thermal mechanical properties of the candidate pebble bed materials are presently extensively investigated because they are critical for the feasibility and performances of the numerous conceptual designs which use a solid breeder. This study is aimed at the investigation of mechanical properties of the lithium orthosilicate and at the characterization of the main chemical, physical and thermo-mechanical properties taking into account the production technology. In doing that at the Department of Civil and Industrial Engineering (DICI) of the University of Pisa adequate experiments were carried out. The obtained results may contribute to characterize the material of the pebbles and to optimize the design of the envisaged fusion breeding blankets.

  14. Thermomechanical architecture of the VIS focal plane for Euclid

    International Nuclear Information System (INIS)

    Martignac, Jerome; Carty, Michael; Tourette, Thierry; Bachet, Damien; Berthe, Michel; Augueres, Jean-Louis; Amiaux, Jerome; Fontignie, Jean; Horeau, Benoit; Renaud, Diana

    2014-01-01

    One of the main challenges for current and near future space experiments is the increase of focal plane complexity in terms of amount of pixels. In the frame work of the ESA Euclid mission to be launched in 2020, the Euclid Consortium is developing an extremely large and stable focal plane for the VIS instrument. CEA has developed the thermomechanical architecture of that Focal Plane taking into account all the very stringent performance and mission related requirements. The VIS Focal Plane Assembly integrates 36 CCDs (operated at 150 K) connected to their front end electronics (operated at 280 K) as to obtain one of the largest focal plane (0.6 billion pixels) ever built for space application after the GAIA one. The CCDs are CCD273 type specially designed and provided by the e2v company under ESA contract, front end electronics is studied and provided by MSSL. In this paper we first recall the specific requirements that have driven the overall architecture of the VIS-FPA and especially the solutions proposed to cope with the scientific needs of an extremely stable focal plane, both mechanically and thermally. The mechanical structure based on SiC material used for the cold sub assembly supporting the CCDs is detailed. We describe also the modular architecture concept that we have selected taking into account AIT-AIV and programmatic constraints. (authors)

  15. Effect of Thermomechanical Processing and Crystallographic Orientation on the Corrosion Behavior of API 5L X70 Pipeline Steel

    Science.gov (United States)

    Ohaeri, Enyinnaya; Omale, Joseph; Eduok, Ubong; Szpunar, Jerzy

    2018-04-01

    This work presents the electrochemical response of X70 pipeline steel substrates thermomechanically processed at different conditions. The WE sample was hot rolled at a temperature range of 850 °C to 805 °C and cooled at a rate of 42.75 °C/s. Another sample WD was hot rolled from 880 °C to 815 °C and cooled at a faster rate of 51.5 °C/s. Corrosion tests were conducted electrochemically by potentiodynamic polarization in hydrogen-charged and non-hydrogen-charged environments. A lower corrosion rate was measured with hydrogen charging due to the rapid formation of corrosion product film on pipeline substrate, but WE specimen emerged as the most susceptible to corrosion with and without hydrogen charging. Variations in thermomechanical rolling conditions influenced grain orientation, protective film properties, corrosion, and cracking behavior on both specimens. Cracks were seen in both specimens after hydrogen charging, but specimen WE experienced a more intense deterioration of protective corrosion product film and subsequent cracking. A large part of specimen WD retained its protective corrosion product film after the polarization test, and sites where spalling occurred resulted in pitting with less cracking. Despite weak crystallographic texture noticed in both specimens, WD showed a higher intensity of corrosion-resistant 111||ND-oriented grains, while WE showed a more random distribution of 111||ND-, 011||ND-, and 001||ND-oriented grains with a lower intensity.

  16. Effect of Thermomechanical Processing and Crystallographic Orientation on the Corrosion Behavior of API 5L X70 Pipeline Steel

    Science.gov (United States)

    Ohaeri, Enyinnaya; Omale, Joseph; Eduok, Ubong; Szpunar, Jerzy

    2018-06-01

    This work presents the electrochemical response of X70 pipeline steel substrates thermomechanically processed at different conditions. The WE sample was hot rolled at a temperature range of 850 °C to 805 °C and cooled at a rate of 42.75 °C/s. Another sample WD was hot rolled from 880 °C to 815 °C and cooled at a faster rate of 51.5 °C/s. Corrosion tests were conducted electrochemically by potentiodynamic polarization in hydrogen-charged and non-hydrogen-charged environments. A lower corrosion rate was measured with hydrogen charging due to the rapid formation of corrosion product film on pipeline substrate, but WE specimen emerged as the most susceptible to corrosion with and without hydrogen charging. Variations in thermomechanical rolling conditions influenced grain orientation, protective film properties, corrosion, and cracking behavior on both specimens. Cracks were seen in both specimens after hydrogen charging, but specimen WE experienced a more intense deterioration of protective corrosion product film and subsequent cracking. A large part of specimen WD retained its protective corrosion product film after the polarization test, and sites where spalling occurred resulted in pitting with less cracking. Despite weak crystallographic texture noticed in both specimens, WD showed a higher intensity of corrosion-resistant 111|| ND-oriented grains, while WE showed a more random distribution of 111|| ND-, 011|| ND-, and 001|| ND-oriented grains with a lower intensity.

  17. Thermo-Mechanical Behavior and Shakedown of Shape Memory Alloy Cable Structures

    Science.gov (United States)

    Biggs, Daniel B.

    Shape memory alloys (SMAs) are a versatile class of smart materials that exhibit adaptive properties which have been applied to solve engineering problems in wide-ranging fields from aerospace to biomedical engineering. Yet there is a lack of understanding of the fundamental nature of SMAs in order to effectively apply them to challenging problems within these engineering fields. Stranding fine NiTi wires into a cable form satisfies the demands of many aerospace and civil engineering applications which require actuators to withstand large tensile loads. The impact of increased bending and twisting in stranded NiTi wire structures, as well as introducing contact mechanics to the unstable phase transformation is not well understood, and this work aims to fill that void. To study the scalability of NiTi cables, thermo-mechanical characterization tests are conducted on cables much larger than those previously tested. These cables are found to have good superelastic properties and repeatable cyclic behavior with minimal induced plasticity. The behavior of additional cables, which have higher transition temperatures that can be used in a shape memory mode as thermo-responsive, high force actuator elements, are explored. These cables are found to scale up the performance of straight wire by maintaining an equivalent work output. Moreover, this work investigates the degradation of the thermal actuation of SMA wires through novel stress-temperature paths, discovering several path dependent behaviors of transformation-induced plasticity. The local mechanics of NiTi cable structures are explored through experiments utilizing digital image correlation, revealing new periodic transformation instabilities. Finite element simulations are presented, which indicate that the instabilities are caused by friction and relative sliding between wires in a cable. Finally, a study of the convective heat transfer of helical wire involving a suite of wind tunnel experiments, numerical

  18. Evolution of mechanical behavior of 6XXX aluminium alloy due to the precipitation state during a thermo-mechanical process

    International Nuclear Information System (INIS)

    Bardel, Didier; Perez, Michel; Nelias, Daniel; Chaise, Thibaut; Garnier, Jerome; Bourlier, Florent

    2014-01-01

    The aim of this research is to link the microstructural state and the mechanical properties of an age hardening alloy during a fast heat treatment such as encountered during welding. A coupled model between precipitation state and mechanical properties is used to predict the yield strength and hardening behavior that can be observed experimentally. The method permits the identification of the kinematic and isotropic contributions in the hardening model. The methodology is applied to a 6061-T6 aluminium alloy which is used in the Jules Horowitz reactor vessel. The general idea of this methodology is to couple an efficient microstructural model to a mechanical one based on the dislocation theory and ad'hoc experiments. The theoretical background is based on the work of Kampmann and Wagner, known as the KWN model, to account for nucleation, growth/dissolution and coarsening of precipitates. This analysis requires transient thermo-mechanical experimental data. The efficiency of these models and their coupling are shown for a series 6XXX aluminium alloy which contains β'' and β' precipitates. Ultimately these models are coupled to a FEA model and allows to predict the distribution of precipitates within each element of the mesh, and subsequently its mechanical behavior. (authors)

  19. Comparison of Diafiltration and Size-Exclusion Chromatography to Recover Hemicelluloses From Process Water From Thermomechanical Pulping of Spruce

    Science.gov (United States)

    Andersson, Alexandra; Persson, Tobias; Zacchi, Guido; Stålbrand, Henrik; Jönsson, Ann-Sofi

    Hemicelluloses constitute one of the most abundant renewable resources on earth. To increase their utilization, the isolation of hemicelluloses from industrial biomass side-streams would be beneficial. A method was investigated to isolate hemicelluloses from process water from a thermomechanical pulp mill. The method consists of three steps: removal of solids by microfiltration, preconcentration of the hemicelluloses by ultrafiltration, and purification by either size-exclusion chromatography (SEC) or diafiltration. The purpose of the final purification step is to separate hemicelluloses from small oligosaccharides, monosaccharides, and salts. The ratio between galactose, glucose, and mannose in oligo- and polysaccharides after preconcentration was 0.8∶1∶2.8, which is similar to that found in galactoglucomannan. Continuous diafiltration was performed using a composite fluoro polymer membrane with cutoff of 1000 Da. After diafiltration with four diavolumes the purity of the hemicelluloses was 77% (gram oligo- and polysaccharides/ gram total dissolved solids) and the recovery was 87%. Purification by SEC was performed with 5, 20, and 40% sample loadings, respectively and a flow rate of 12 or 25 mL/min (9 or 19 cm/h). The purity of hemicelluloses after SEC was approx 82%, and the recovery was above 99%. The optimal sample load and flow rate were 20% and 25 mL/min, respectively. The process water from thermomechanical pulping of spruce is inexpensive. Thus, the recovery of hemicelluloses is not of main importance. If the purity of 77%, obtained with diafiltration, is sufficient for the utilization of the hemicelluloses, diafiltration probably offers a less expensive alternative in this application.

  20. Review on structural fatigue of NiTi shape memory alloys: Pure mechanical and thermo-mechanical ones

    Directory of Open Access Journals (Sweden)

    Guozheng Kang

    2015-11-01

    Full Text Available Structural fatigue of NiTi shape memory alloys is a key issue that should be solved in order to promote their engineering applications and utilize their unique shape memory effect and super-elasticity more sufficiently. In this paper, the latest progresses made in experimental and theoretical analyses for the structural fatigue features of NiTi shape memory alloys are reviewed. First, macroscopic experimental observations to the pure mechanical and thermo-mechanical fatigue features of the alloys are summarized; then the state-of-arts in the mechanism analysis of fatigue rupture are addressed; further, advances in the construction of fatigue failure models are provided; finally, summary and future topics are outlined.