  1. Effect of pulp density and particle size on indirect bioleaching of Pomalaa nickel laterite using metabolic citric acid

    Science.gov (United States)

    Petrus, H. B. T. M.; Wanta, K. C.; Setiawan, H.; Perdana, I.; Astuti, W.

    2018-01-01

    Nickel laterite ore contains oxide of iron, aluminum or both with nickel, cobalt and chromium which can be leached out using hydrometallurgical process. For the purpose of meeting the world’s increasing demand of nickel, there is a need to invent environmentally friendly process to efficiently leach nickel. This experiment used nickel laterite ore obtained from Pomalaa, South Sulawesi. The leaching agent is metabolic citric acid produced by Aspergillus niger under optimum condition. Leaching process was done in three-necked flask in atmospheric temperature and constant stirring speed of 200 rpm. The variable examined in the experiment was pulp density and particle size of nickel laterite ore. Samples were taken at 3, 7, 10, 14, and 17 minutes and then filtered and diluted to be analyzed using ICP-AES. The result of the experiment showed the maximum recovery of metals increase with the decrease of the pulp density. The maximum recovery for varying pulp density were at 5% solid/liquid ratio and the recovery were Ni at 1.63%, Al at 0.47%, Fe at 0.23% and Mg at 1.09%. The effect of particle size on leaching process showed that the leaching process follows the shrinking core model. The maximum recovery of metals at particle size were at 100-120 mesh with Ni at 1.37%, Fe at 0.10%, Al at 0.72% and Mg at 0.62%.

  2. Processing of low- grade nickel bearing laterites

    OpenAIRE

    Krstev, Boris; Ilic, Ilija

    1999-01-01

    A combination of current trends and developments may undermine the sulphides supremacy and might tip the balance in favour of laterites for new investigations or projects. A list of current laterite operations or laterites processing today is following: Ferronickel smelting, Matte smelting, Reduction roasting-ammonia leaching and High pressure sulphuric acid leaching.Apart from the above mentioned process routes, there have been many attempts to develop processes know as alternative processes...

  3. Synthesis and characterization of Co3O4 prepared from atmospheric pressure acid leach liquors of nickel laterite ores

    Science.gov (United States)

    Meng, Long; Guo, Zhan-cheng; Qu, Jing-kui; Qi, Tao; Guo, Qiang; Hou, Gui-hua; Dong, Peng-yu; Xi, Xin-guo

    2018-01-01

    A chemical precipitation-thermal decomposition method was developed to synthesize Co3O4 nanoparticles using cobalt liquor obtained from the atmospheric pressure acid leaching process of nickel laterite ores. The effects of the precursor reaction temperature, the concentration of Co2+, and the calcination temperature on the specific surface area, morphology, and the electrochemical behavior of the obtained Co3O4 particles were investigated. The precursor basic cobaltous carbonate and cobaltosic oxide products were characterized and analyzed by Fourier transform infrared spectroscopy, thermogravimetric differential thermal analysis, X-ray diffraction, field-emission scanning electron microscopy, specific surface area analysis, and electrochemical analysis. The results indicate that the specific surface area of the Co3O4 particles with a diameter of 30 nm, which were obtained under the optimum conditions of a precursor reaction temperature of 30°C, 0.25 mol/L Co2+, and a calcination temperature of 350°C, was 48.89 m2/g. Electrodes fabricated using Co3O4 nanoparticles exhibited good electrochemical properties, with a specific capacitance of 216.3 F/g at a scan rate of 100 mV/s.

  4. Extraction of nickel from Ramu laterite by sulphation roasting-water leaching

    Science.gov (United States)

    Wang, Weiwei; Du, Shangchao; Liu, Guo; Tang, Jianwen; Lu, Yeda; Lv, Dong

    2017-08-01

    Recovery of nickel from a PNG nickel laterite with high content of iron by a sulphation roasting-water leaching has been studied. The influences of sulfuric acid/ore ratio, temperature of roasting and water on recovery efficiency were investigated. The effective separation of nickel over the co-existed elements including iron was achieved by the process with mixing, curing, roasting and leaching stages. Near 100% of nickel was leached from the roasted laterite by water at 80°C in an atmospheric air, while co-leaching of about 2% of iron, under the optimal pre-treatment conditions with the ratio of acid: ore around 0.45:1 and the roasting temperature about 650°C. The advantages and disadvantages of sulphation atmospheric leaching are compared with pressure acid leaching with engineering consideration.

  5. Satellite Remote Sensing For Aluminum And Nickel Laterites

    Science.gov (United States)

    Henderson, Frederick B.; Penfield, Glen T.; Grubbs, Donald K.

    1984-08-01

    The new LANDSAT-4,-5/Thematic Mapper (TM) land observational satellite remote sensing systems are providing dramatically new and important short wave infrared (SWIR) data, which combined with Landsat's Multi-Spectral Scanner (MSS) visible (VIS), very near infrared (VNIR), and thermal infrared (TI) data greatly improves regional geological mapping on a global scale. The TM will significantly improve clay, iron oxide, aluminum, and nickel laterite mapping capabilities over large areas of the world. It will also improve the ability to discriminate vegetation stress and species distribution associated with lateritic environments. Nickel laterites on Gag Island, Indonesia are defined by MSS imagery. Satellite imagery of the Cape Bougainville and the Darling Range, Australia bauxite deposits show the potential use of MSS data for exploration and mining applications. Examples of satellite syn-thetic aperture radar (SAR) for Jamaica document the use of this method for bauxite exploration. Thematic Mapper data will be combined with the French SPOT satellite's high spatial resolution and stereoscopic digital data, and U.S., Japanese, European, and Canadian Synthetic Aperture Radar (SAR) data to assist with logistics, mine development, and environ-mental concerns associated with aluminum and nickel lateritic deposits worldwide.

  6. laterite

    Indian Academy of Sciences (India)

    In the Deccan region of western India ferricrete duricrusts, usually described as laterites, cap some basalt summits east of the Western Ghats escarpment, basalts of the low-lying Konkan. Plain to its west, as well as some sizeable isolated basalt plateaus rising from the Plain. The duricrusts are iron-cemented saprolite with ...

  7. Advances in microbial leaching processes for nickel extraction from lateritic minerals - A review

    International Nuclear Information System (INIS)

    Behra, Sunil Kumar; Mulaba-Bafubiandi, Antoine Floribert

    2015-01-01

    Lateritic nickel minerals constitute about 80% of nickel reserves in the world, but their contribution for nickel production is about 40%. The obstacles in extraction of nickel from lateritic minerals are attributed to their very complex mineralogy and low nickel content. Hence, the existing metallurgical techniques are not techno-economically feasible and environmentally sustainable for processing of such complex deposits. At this juncture, microbial mineral processing could be a benevolent approach for processing of lateritic minerals in favor of nickel extraction. The microbial mineral processing route offers many advantages over conventional metallurgical methods as the process is operated under ambient conditions and requires low energy input; thus these processes are relatively simple and environment friendly. Microbial processing of the lateritic deposits still needs improvement to make it industrially viable. Microorganisms play the pivotal role in mineral bio-processing as they catalyze the extraction of metals from minerals. So it is inevitable to explore the physiological and bio-molecular mechanisms involved in this microbe-mineral interaction. The present article offers comprehensive information about the advances in microbial processes for extraction of nickel from laterites.

  8. Advances in microbial leaching processes for nickel extraction from lateritic minerals - A review

    Energy Technology Data Exchange (ETDEWEB)

    Behra, Sunil Kumar; Mulaba-Bafubiandi, Antoine Floribert [Faculty of Engineering and the Built Environment, University of Johannesburg, (South Africa)

    2015-08-15

    Lateritic nickel minerals constitute about 80% of nickel reserves in the world, but their contribution for nickel production is about 40%. The obstacles in extraction of nickel from lateritic minerals are attributed to their very complex mineralogy and low nickel content. Hence, the existing metallurgical techniques are not techno-economically feasible and environmentally sustainable for processing of such complex deposits. At this juncture, microbial mineral processing could be a benevolent approach for processing of lateritic minerals in favor of nickel extraction. The microbial mineral processing route offers many advantages over conventional metallurgical methods as the process is operated under ambient conditions and requires low energy input; thus these processes are relatively simple and environment friendly. Microbial processing of the lateritic deposits still needs improvement to make it industrially viable. Microorganisms play the pivotal role in mineral bio-processing as they catalyze the extraction of metals from minerals. So it is inevitable to explore the physiological and bio-molecular mechanisms involved in this microbe-mineral interaction. The present article offers comprehensive information about the advances in microbial processes for extraction of nickel from laterites.

  9. Bioleaching of nickel by Aspergillus humicola SKP102 isolated from Indian lateritic overburden

    Directory of Open Access Journals (Sweden)

    Suchhanda Ghosh

    2016-01-01

    Full Text Available The lateritic deposits spread over the Eastern Ghats of Sukinda Valley, Odisha, India, produce a huge amount of overburden annually as a byproduct of chromite mining. This chromite mining overburden contains nickel, the only source of the metal in the country. During this study Aspergillus humicola SKP102, an indigenous fungus isolated from the mining overburden was employed for the leaching of nickel. About 53.89% of the nickel could be leached by the fungus when grown in batch mode using a Czapek dox medium containing 2% (w/v of the mining overburden. The parameters affecting bioleaching were optimized in order to grow the fungus and leach the metal. Of the different options of cheap carbon sources, straw infusion and molasses emerged as viable options for the growth of the fungus and the leaching of nickel. Two-step and indirect techniques were also used for this purpose, and they resulted in 53.09% and 65.04% Ni leaching respectively. Adding diluted sulfuric acid to the leaching medium resulted in 97.05% nickel recovery from the overburden pulp. A. humicola SKP102 could be a potential tool for leaching nickel from the mining overburden.

  10. 3D modeling of the laterites on top of the Koniambo Massif, New Caledonia: refinement of the per descensum lateritic model for nickel mineralization

    Science.gov (United States)

    Quesnel, Benoît; de Veslud, Christian Le Carlier; Boulvais, Philippe; Gautier, Pierre; Cathelineau, Michel; Drouillet, Maxime

    2017-10-01

    Resulting from the weathering of the Peridotite Nappe, laterites are abundant in New Caledonia and host one of the largest nickel deposits worldwide. This work presents a 3D model of the Koniambo nickel laterite ore deposit. It shows that the laterites are located along the ridges of the massif and organized as hectometric-sized patches obliquely cut by the topography and distributed at various elevations. Three kinds of geometry were observed: (i) a thick laterite cover (between 20 and 40 m) overlying saprolite and mainly localized on topographic highs, (ii) a thin laterite cover (from a few meters to 20 m) mainly localized on areas with gentle slopes, and (iii) exposure of saprolite without laterite cover. Our data show that Ni-rich and Ni-poor areas are organized as hectometric-sized patches which broadly correlate with the distribution of the laterite thickness. The highest Ni areas are localized on slopes where laterite cover is thin or absent. The areas with lowest Ni are located in topographic highs under the thickest laterite cover. The vertical Ni mass balance for each borehole shows that, in areas with thick laterite cover, Ni is sub-equilibrated to slightly depleted whereas in areas with thin laterite cover, Ni is enriched. This suggests the existence of lateral infiltration of water rich in dissolved Ni, from areas such as topographic highs to downstream slope areas, in a process leading to enrichment of saprolite in Ni in slope areas. Mechanical transport and leaching of laterite material on slopes, including Ni-bearing material, could also contribute to local enrichment of Ni in the saprolite.

  11. Biocatalytic and chemical leaching of a low-grade nickel laterite ore

    Science.gov (United States)

    Ciftci, Hasan; Atik, Suleyman; Gurbuz, Fatma

    2018-04-01

    Nickel and cobalt recovery from a low-grade nickel laterite ore, supplied from Çaldağ deposit (Manisa, Turkey) were investigated by bio and chemical leaching processes. The fungus, Aspergillus niger was used for biocatalytic leaching experiments. The effects of parameters (solid ratio and sucrose concentration) on the biocatalytic leaching of the ore were initially tested in flasks to obtain the optimum conditions for the A. niger. Then chemical leaching was applied as a comparison to bioleaching, using organic acids (citric, oxalic, acetic and gluconic acids) as well as a mixture of acids. According the results, the maximum dissolution yield of nickel, cobalt and iron were detected respectively as 95.3%, 74.3% and 50.0% by biocatalytic processes which containing 25% (w/v) sucrose and 1% (w/v) solids. The increase in the solid ratio adversely influenced the biocatalytic activity of A. niger. Finally, further tests in reactors (v = 1 and 10 L) were performed using the optimum conditions from the flask tests. The difference in metals recovery between biocatalytic and chemical leaching was significantly important. Bioleaching produced higher Ni and Co extractions (34.3-75.6%) than chemical process.

  12. Carbothermic Reduction of Nickeliferous Laterite Ores for Nickel Pig Iron Production in China: A Review

    Science.gov (United States)

    Rao, Mingjun; Li, Guanghui; Jiang, Tao; Luo, Jun; Zhang, Yuanbo; Fan, Xiaohui

    2013-11-01

    Both the consumption and production of crude stainless steel in China rank first in the world. In 2011, the nickel production in China amounted to 446 kilotons, with the proportion of electrolytic nickel and nickel pig iron (NPI) registering 41.5% and 56.5%, respectively. NPI is a low-cost feedstock for stainless steel production when used as a substitute for electrolytic nickel. The existing commercial NPI production processes such as blast furnace smelting, rotary kiln-electric furnace smelting, and Krupp-Renn (Nipon Yakin Oheyama) processes are discussed. As low-temperature (below 1300°C) reduction of nickeliferous laterite ores followed by magnetic separation could provide an alternative avenue without smelting at high temperature (~1500°C) for producing ferronickel with low cost, the fundamentals and recent developments of the low-temperature reduction of nickeliferous laterite ores are reviewed.

  13. Thermodynamic analysis of the reduction process of Colombian lateritic nickel ore

    International Nuclear Information System (INIS)

    Diaz, S. C.; Garces, A.; Restrepo, O. J.; Lara, M. A.; Camporredondo, J. E.

    2015-01-01

    The Colombian nickeliferous laterites are minerals used for the nickel extraction by hydrometallurgical and pyrometallurgical processes. In this work the thermodynamic behaviour of three Colombian lateritic mineral samples are described, with contents of 1.42%, 1.78% y 2.04% of nickel, when they are subjected to the calcination and reduction processes. The mineral was characterized using X Rays Diffraction and X Rays Fluorescence, giving evidence of the presence of mineralogical species such as nepouite (Ni 3 Si 2 O 5 (OH) 4 ), goethite (Fe 2 O 3 .H 2 O), silica (SiO 2 ), antigorite (Mg 3 Si 2 O 5 (OH) 4 ) and fosferite (Mg 2 SiO 4 ). The thermodynamic analysis was conducted using the software HSC Chemistry for Windows 5.1 and was focused in the quantitative determination of the chemical evolution of the mixture of these minerals with variable quantities of coal, in function of temperature. The results produced by the program showed, in the equilibrium, the feasibility of complete reduction of the nickel, and additionally, a considerable high percentage of reduction of iron oxides (up to 99%) using ratio C/O .1 at temperatures close to 1100 degree centigrade. (Author)

  14. ERT and Well Data Tie for Nickel Laterite Characterization

    Science.gov (United States)

    Aswad, Sabrianto; Mamela Mais, Difar; Syamsuddin; Wanni

    2018-03-01

    The need of ERT method in nickel latentes exploration can’t be deny. This method have capability to make exploration more effective and efficient. In reality this method still remain ambiguity in its application, especially for geologist and mining expert. These ambiguity related with layer zone determination (limonite, saprolite and bedrock), the same resistivity values in the different zones and determination of bedrock. This paper try to expose interesting fact to overcome this ambiguity by using ERT data and drill data tie. This tie will show characteristic of nickel lateric based on resisitivity value and the contribution of chemistry element for resistivity value. Data ERT was collected by using gradient configuration and well data consist of mayor element and minor element. Tie result showed difference resistivity value in limonite layer influence by Fe, H2O and Ni, where resistivity value from saprolite layer influenced by Fe, H2O, Si02, MgO, Al, Cr, and Ni in certain accumulation. In bedrock layer, almost all drill data did not reach bedrock but only reached the boulder alone, it is supported by the value of the resistivity of rock unserpentinized peridotite which should show a relatively large resistivity value

  15. The effect of smelting time and composition of palm kernel shell charcoal reductant toward extractive Pomalaa nickel laterite ore in mini electric arc furnace

    Science.gov (United States)

    Sihotang, Iqbal Huda; Supriyatna, Yayat Iman; Ismail, Ika; Sulistijono

    2018-04-01

    Indonesia is a country that is rich in natural resources. Being a third country which has a nickel laterite ore in the world after New Caledonia and Philippines. However, the processing of nickel laterite ore to increase its levels in Indonesia is still lacking. In the processing of nickel laterite ore into metal, it can be processed by pyrometallurgy method that typically use coal as a reductant. However, coal is a non-renewable energy and have high enough levels of pollution. One potentially replace is the biomass, that is a renewable energy. Palm kernel shell are biomass that can be used as a reductant because it has a fairly high fix carbon content. This research aims to make nickel laterite ores become metal using palm kernel shell charcoal as reductant in mini electric arc furnace. The result show that the best smelting time of this research is 60 minutes with the best composition of the reductant is 2,000 gram.

  16. Co-reduction of Copper Smelting Slag and Nickel Laterite to Prepare Fe-Ni-Cu Alloy for Weathering Steel

    Science.gov (United States)

    Guo, Zhengqi; Pan, Jian; Zhu, Deqing; Zhang, Feng

    2018-02-01

    In this study, a new technique was proposed for the economical and environmentally friendly recovery of valuable metals from copper smelting slag while simultaneously upgrading nickel laterite through a co-reduction followed by wet magnetic separation process. Copper slag with a high FeO content can decrease the liquidus temperature of the SiO2-Al2O3-CaO-MgO system and facilitate formation of liquid phase in a co-reduction process with nickel laterite, which is beneficial for metallic particle growth. As a result, the recovery of Ni, Cu, and Fe was notably increased. A crude Fe-Ni-Cu alloy with 2.5% Ni, 1.1% Cu, and 87.9% Fe was produced, which can replace part of scrap steel, electrolytic copper, and nickel as the burden in the production of weathering steel by an electric arc furnace. The study further found that an appropriate proportion of copper slag and nickel laterite in the mixture is essential to enhance the reduction, acquire appropriate amounts of the liquid phase, and improve the growth of the metallic alloy grains. As a result, the liberation of alloy particles in the grinding process was effectively promoted and the metal recovery was increased significantly in the subsequent magnetic separation process.

  17. Nickel distribution and isotopic fractionation in a Brazilian lateritic regolith: Coupling Ni isotopes and Ni K-edge XANES

    Science.gov (United States)

    Ratié, G.; Garnier, J.; Calmels, D.; Vantelon, D.; Guimarães, E.; Monvoisin, G.; Nouet, J.; Ponzevera, E.; Quantin, C.

    2018-06-01

    Ultramafic (UM) rocks are known to be nickel (Ni) rich and to weather quickly, which makes them a good candidate to look at the Ni isotope systematics during weathering processes at the Earth's surface. The present study aims at identifying the Ni solid speciation and discussing the weathering processes that produce Ni isotope fractionation in two deep laterite profiles under tropical conditions (Barro Alto, Goiás State, Brazil). While phyllosilicates and to a lower extent goethite are the main Ni-bearing phases in the saprolitic part of the profile, iron (Fe) oxides dominate the Ni budget in the lateritic unit. Nickel isotopic composition (δ60Ni values) has been measured in each unit of the regolith, i.e., rock, saprock, saprolite and laterite (n = 52). δ60Ni varies widely within the two laterite profiles, from -0.10 ± 0.05‰ to 1.43 ± 0.05‰, showing that significant Ni isotope fractionation occurs during the weathering of UM rocks. Overall, our results show that during weathering, the solid phase is depleted in heavy Ni isotopes due to the preferential sorption and incorporation of light Ni isotopes into Fe oxides; the same mechanisms likely apply to the incorporation of Ni into phyllosilicates (type 2:1). However, an isotopically heavy Ni pool is observed in the solid phase at the bottom of the saprolitic unit. This feature can be explained by two hypotheses that are not mutually exclusive: (i) a depletion in light Ni isotopes during the first stage of weathering due to the preferential dissolution of light Ni-containing minerals, and (ii) the sorption or incorporation of isotopically heavy Ni carried by percolating waters (groundwater samples have δ60Ni of 2.20 and 2.27‰), that were enriched in heavy Ni isotopes due to successive weathering processes in the overlying soil and laterite units.

  18. Effects of reduction temperature to Ni and Fe content and the morphology of agglomerate of reduced laterite limonitic nickel ore by coal-bed method

    Science.gov (United States)

    Abdul, Fakhreza; Pintowantoro, Sungging; Kawigraha, Adji; Nursidiq, Ahlidin

    2018-04-01

    As the current drop of nickel sulfide ore on earth, the attention to nickel laterite ore processing was inscreased in order to fulfill the future nickel demand needs. This research aims to optimized the process of nickel laterite ore extraction using coal bed method. This research was conducted by reducing low grade nickel laterite ore (limonitic) with nickel content of 1.25 %. The reduction process was carried out using CO gas which formed by the reaction of coal and dolomite. The Briquette of nickel ore, coal, Na2SO4 mixtures incorporated in the crucible with bed, then reduced for 6 hours at the temperature of 1200 °C. 1400 °C, and 1400 °C. The result of the research shown that the highest increase of Ni content and Ni recovery value was in the reduction temperature of 1400 °C with the increase of 3.44 %, and the recovery value of Ni equal to 86.75 %. While the highest increase of Fe content and Fe recovery value, respectively, was in the reduction temperature of 1300 °C with the increase of 22.67 % and 1200 °C with Fe recovery value of 89.41 %.

  19. Analysis of holding time variations to Ni and Fe content and morphology in nickel laterite limonitic reduction process by using coal-dolomite bed

    Science.gov (United States)

    Abdul, Fakhreza; Pintowantoro, Sungging; Yuwandono, Ridwan Bagus

    2018-04-01

    With the depletion of nickel sulfide ore resources, the nickel laterit processing become an attention to fulfill nickel world demans. Reducing laterite nickel by using a low cost carbonaceous reductan has proved produces high grade ferronickel alloy. In this research, reduction was carried out to low grade laterite nickel (limonite) with 1.25% nikel content by using CO gas reductant formed by reaction between coal and dolomite. Reduction process preceded by forming brickets mixture from limonit ore, coal, and Na2SO4, then the brickets placed inside crucible bed together with dolomit and reduced at temperature 1400 °C with holding time variations 4, 6, and 8 hours. EDX, XRD, and SEM test were carried out to find out the Ni and nickel grade after reduced, the phases that formed, and the morphology brickets after reduced. The reduction results shows that the highest increase on nickel grade was obtained by 8 hours holding time increasing 5.84 % from initial grade, and the highest recovery was obtained by 6 hours holding time with recovery 88.51 %. While the higest increase on Fe grade was obtained by 4 hours holding time, and the highest recovery Fe was obtained by 4 hours holding time with recovery 85.41%.

  20. Fluoride adsorption onto an acid treated lateritic mineral from Kenya ...

    African Journals Online (AJOL)

    1) from Kenya was studied by batch experiments. The effect of acid-treatment of adsorbent and change in temperature, mass of LM-1, pH and selected competing ions was evaluated. The adsorption process was strongly influenced by ...

  1. Effects of simulated acid rain on microbial characteristics in a lateritic red soil.

    Science.gov (United States)

    Xu, Hua-qin; Zhang, Jia-en; Ouyang, Ying; Lin, Ling; Quan, Guo-ming; Zhao, Ben-liang; Yu, Jia-yu

    2015-11-01

    A laboratory experiment was performed to examine the impact of simulated acid rain (SAR) on nutrient leaching, microbial biomass, and microbial activities in a lateritic red soil in South China. The soil column leaching experiment was conducted over a 60-day period with the following six SAR pH treatments (levels): 2.5, 3.0, 3.5, 4.0, 4.5, and 5.0 and one control treatment (pH = 7). Compared with the control treatment, the concentrations of soil organic matter, total nitrogen, total phosphorus, total potassium, soil microbial biomass carbon (MBC), soil microbial biomass nitrogen (MBN), and average well color density (AWCD) in the Ecoplates were all significantly decreased by leaching with SAR at different pH levels. The decrease in MBC and MBN indicated that acid rain reduced the soil microbial population, while the decrease in AWCD revealed that acid rain had a negative effect on soil bacterial metabolic function. Soil basal respiration increased gradually from pH 4.0 to 7.0 but decreased dramatically from pH 2.5 to 3.0. The decrease in soil nutrient was the major reason for the change of soil microbial functions. A principal component analysis showed that the major carbon sources used by the bacteria were carbohydrates and carboxylic acids.

  2. Inorganic polymers from laterite using activation with phosphoric acid and alkaline sodium silicate solution: Mechanical and microstructural properties

    International Nuclear Information System (INIS)

    Enzo Ferrari, Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy))" data-affiliation=" (Dipartimento di Ingegneria Enzo Ferrari, Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy))" >Lassinantti Gualtieri, Magdalena; Enzo Ferrari, Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy))" data-affiliation=" (Dipartimento di Ingegneria Enzo Ferrari, Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy))" >Romagnoli, Marcello; Pollastri, Simone; Gualtieri, Alessandro F.

    2015-01-01

    Geopolymers from laterite, an iron-rich soil available in developing countries, have great potential as building materials. In this work, laterite from Togo (Africa) was used to prepare geopolymers using both phosphoric acid and alkaline sodium silicate solution. Microstructural properties were investigated by scanning electron microscopy, X-ray powder diffraction and mercury porosimetry, whereas thermal properties were evaluated by thermal analyses. The local environment of iron was studied by X-ray Absorption Spectroscopy (XANES region). The mechanical properties were determined. Modulus of Rupture and Young's modulus fell in the ranges 3.3–4.5 MPa and 12–33 GPa, respectively, rendering the materials good candidates for construction purposes. Heating above 900 °C results in weight-gain, presumably due to iron redox reactions. X-ray Absorption Spectroscopy data evidence changes in the chemical and structural environments of iron following thermal treatment of geopolymers. These changes indicate interaction between the geopolymer structure and iron during heating, possibly leading to redox properties. -- Highlights: •Geopolymerization of laterite is promising for fabrication of building materials. •Both phosphoric acid and alkaline sodium silicate solution can be used for activation. •Thermally activated redox properties of the inorganic polymers were observed

  3. Inorganic polymers from laterite using activation with phosphoric acid and alkaline sodium silicate solution: Mechanical and microstructural properties

    Energy Technology Data Exchange (ETDEWEB)

    Lassinantti Gualtieri, Magdalena, E-mail: magdalena.gualtieri@unimore.it [Dipartimento di Ingegneria " Enzo Ferrari" , Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy); Romagnoli, Marcello [Dipartimento di Ingegneria " Enzo Ferrari" , Università degli studi di Modena e Reggio Emilia, Via Vignolese 905/a, I-41125 Modena (Italy); Pollastri, Simone; Gualtieri, Alessandro F. [Dipartimento di Scienze Chimiche e Geologiche, Università degli studi di Modena e Reggio Emilia, Via S. Eufemia 19I, I-41121 Modena (Italy)

    2015-01-15

    Geopolymers from laterite, an iron-rich soil available in developing countries, have great potential as building materials. In this work, laterite from Togo (Africa) was used to prepare geopolymers using both phosphoric acid and alkaline sodium silicate solution. Microstructural properties were investigated by scanning electron microscopy, X-ray powder diffraction and mercury porosimetry, whereas thermal properties were evaluated by thermal analyses. The local environment of iron was studied by X-ray Absorption Spectroscopy (XANES region). The mechanical properties were determined. Modulus of Rupture and Young's modulus fell in the ranges 3.3–4.5 MPa and 12–33 GPa, respectively, rendering the materials good candidates for construction purposes. Heating above 900 °C results in weight-gain, presumably due to iron redox reactions. X-ray Absorption Spectroscopy data evidence changes in the chemical and structural environments of iron following thermal treatment of geopolymers. These changes indicate interaction between the geopolymer structure and iron during heating, possibly leading to redox properties. -- Highlights: •Geopolymerization of laterite is promising for fabrication of building materials. •Both phosphoric acid and alkaline sodium silicate solution can be used for activation. •Thermally activated redox properties of the inorganic polymers were observed.

  4. Nickel Inhibits Mitochondrial Fatty Acid Oxidation

    Science.gov (United States)

    Uppala, Radha; McKinney, Richard W.; Brant, Kelly A.; Fabisiak, James P.; Goetzman, Eric S.

    2015-01-01

    Nickel exposure is associated with changes in cellular energy metabolism which may contribute to its carcinogenic properties. Here, we demonstrate that nickel strongly represses mitochondrial fatty acid oxidation—the pathway by which fatty acids are catabolized for energy—in both primary human lung fibroblasts and mouse embryonic fibroblasts. At the concentrations used, nickel suppresses fatty acid oxidation without globally suppressing mitochondrial function as evidenced by increased glucose oxidation to CO2. Pre-treatment with L-carnitine, previously shown to prevent nickel-induced mitochondrial dysfunction in neuroblastoma cells, did not prevent the inhibition of fatty acid oxidation. The effect of nickel on fatty acid oxidation occurred only with prolonged exposure (>5 hr), suggesting that direct inhibition of the active sites of metabolic enzymes is not the mechanism of action. Nickel is a known hypoxia-mimetic that activates hypoxia inducible factor-1α (HIF1α). Nickel-induced inhibition of fatty acid oxidation was blunted in HIF1α knockout fibroblasts, implicating HIF1α as one contributor to the mechanism. Additionally, nickel down-regulated the protein levels of the key fatty acid oxidation enzyme very long-chain acyl-CoA dehydrogenase (VLCAD) in a dose-dependent fashion. In conclusion, inhibition of fatty acid oxidation by nickel, concurrent with increased glucose metabolism, represents a form of metabolic reprogramming that may contribute to nickel-induced carcinogenesis. PMID:26051273

  5. Development and application of an instrument for analysis of iron in laterite ore with the characteristics needed for use in nickel production. Part of a coordinated programme on on-line X-ray and neutron techniques for industrial process control

    International Nuclear Information System (INIS)

    Vizoso, J.R.

    1980-06-01

    This document describes the performance testing of an instrument for the analysis of iron laterite ore used in the production of nickel. It proved to give satisfactory results with an error less or equal to 1% under working conditions (20 0 C - 40 0 C, 80% - 85% relative humidity)

  6. stabilized lateritic soil

    African Journals Online (AJOL)

    user

    this work to optimize the amount of bagasse ash content in cement-stabilized lateritic soil. Geometric .... can handle or consider all the properties involved at the same time to ...... Bearig Ratio of Used oil contaminated Lateritic soils” Nigerian ...

  7. Concentration and Separation of Scandium from Ni Laterite Ore Processing Streams

    Directory of Open Access Journals (Sweden)

    Şerif Kaya

    2017-12-01

    Full Text Available The presence of a considerable amount of scandium in lateritic nickel-cobalt ores necessitates the investigation of possible processing alternatives to recover scandium as a byproduct during nickel and cobalt production. Therefore, in this study, rather than interfering with the main nickel-cobalt production circuit, the precipitation-separation behavior of scandium during a pH-controlled precipitation process from a synthetically prepared solution was investigated to adopt the Sc recovery circuit into an already existing hydrometallurgical nickel-cobalt hydroxide processing plant. The composition of the synthetic solution was determined according to the hydrometallurgical nickel laterite ore processing streams obtained from a HPAL (high-pressure sulphuric acid leaching process. In order to selectively precipitate and concentrate scandium with minimum nickel and cobalt co-precipitation, the pH of the solution was adjusted by CaCO3, MgO, Na2CO3, and NaOH. It was found that precipitation with MgO or Na2CO3 is more advantageous to obtain a precipitate containing higher amounts of scandium with minimum mass when compared to the CaCO3 route, which makes further processing more viable. As a result of this study, it is proposed that by a simple pH-controlled precipitation process, scandium can be separated from the nickel and cobalt containing process solutions as a byproduct without affecting the conventional nickel-cobalt hydroxide production. By further processing this scandium-enriched residue by means of leaching, SX (solvent extraction, and precipitation, an intermediate (NH42NaScF6 product can be obtained.

  8. Thermodynamic Analysis of the Selective Reduction of a Nickeliferous Limonitic Laterite Ore by Hydrogen

    Science.gov (United States)

    Elliott, R.; Pickles, C. A.

    2017-09-01

    Nickeliferous limonitic laterite ores are becoming increasingly attractive as a source of metallic nickel as the costs associated with recovering nickel from the sulphide ores increase. Unlike the sulphide ores, however, the laterite ores are not amenable to concentration by conventional mineral processing techniques such as froth flotation. One potential concentrating method would be the pyrometallurgical solid state reduction of the nickeliferous limonitic ores at relatively low temperatures, followed by beneficiation via magnetic separation. A number of reductants can be utilized in the reduction step, and in this research, a thermodynamic model has been developed to investigate the reduction of a nickeliferous limonitic laterite by hydrogen. The nickel recovery to the ferronickel phase was predicted to be greater than 95 % at temperatures of 673-873 K. Reductant additions above the stoichiometric requirement resulted in high recoveries over a wider temperature range, but the nickel grade of the ferronickel decreased.

  9. Potential for cobalt recovery from lateritic ores in Europe

    Science.gov (United States)

    Herrington, R.

    2012-04-01

    Cobalt is one of the 'critical metals' identified under the EU Raw Materials Initiative. Annually the global mine production of cobalt is around 55,000 tonnes,with Europe's industries consuming around 30% of that figure. Currently Europe produces around 27 tonnes of cobalt from mines in Finland although new capacity is planned. Co-bearing nickel laterite ores being mined in Greece, Macedonia and Kosovo where the cobalt is currently not being recovered (ores have typical analyses of 0.055% Co and >1% Ni,). These ores are currently treated directly in pyrometallurgical plants to recover the contained nickel and this process means there is no separate cobalt product produced. Hydrometallurgical treatment of mineralogically suitable laterite ores can recover the cobalt; for example Cuba recovers 3,500 tonnes of cobalt from its laterite mining operations, which are of a similar scale to the current European operations. Implementation of hydrometallurgical techniques is in its infancy in Europe with one deposit in Turkey planning to use atmospheric heap leaching to recover nickel and copper from oxide-dominated ores. More widespread implementation of these methods to mineralogically suitable ore types could unlock the highly significant undeveloped resources (with metal contents >0.04% Co and >1% Ni), which have been defined throughout the Balkans eastwards into Turkey. At a conservative estimate, this region has the potential to supply up to 30% of the EU cobalt requirements.

  10. Solubility of nickel-cadmium ferrite in acids

    International Nuclear Information System (INIS)

    Vol'ski, V.; Vol'ska, Eh.; Politan'ska, U.

    1977-01-01

    The solubility of a solid solution of nickel-cadmium ferrite containing an excess of ferric oxide, (CdO)sub(0.5), (NiO)sub(0.5) and (Fe 2 O 3 )sub(1.5), in hydrochloric and nitric acids at 20, 40 and 60 deg C, was determined colorimetrically and chelatometrically, as well as by studying the x-ray diffraction patterns of the preparations prior to dissolution and their residues after dissolution. It is shown that cadmium passes into the solution faster than iron and nickel; after 800 hours, the solution contains 40% of iron ions and more than 80% of cadmium ions. The kinetics of ferrite dissolution is studied

  11. Comparative study of electroless nickel film on different organic acids modified cuprammonium fabric (CF)

    Science.gov (United States)

    Zhao, Hang; Lu, Yinxiang

    2016-01-01

    Nickel films were grown on citric acid (CA), malic acid (MA) and oxalic acid (OA) modified cuprammonium fabric (CF) substrates via electroless nickel deposition. The nickel films were examined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). Their individual deposition rate and electromagnetic interference (EMI) shielding effectiveness (SE) were also investigated to compare the properties of electroless nickel films. SEM images illustrated that the nickel film on MA modified CF substrate was smooth and uniform, and the density of nickel nuclei was much higher. Compared with that of CA modified CF, the coverage of nickel nuclei on OA and MA modified CF substrate was very limited and the nickel particles size was too big. XRD analysis showed that the nickel films deposited on the different modified CF substrates had a structure with Ni (1 1 1) preferred orientation. All the nickel coatings via different acid modification were firmly adhered to the CF substrates, as demonstrated by an ultrasonic washing test. The result of tensile test indicated that the electroless nickel plating on CF has ability to strengthen the CF substrate while causes limited effect on tensile elongation. Moreover, the nickel film deposited on MA modified CF substrate showed more predominant in EMI SE than that deposited on CA or OA modified CF.

  12. Separation and Precipitation of Nickel from Acidic Sulfate Leaching Solution of Molybdenum-Nickel Black Shale by Potassium Nickel Sulfate Hexahydrate Crystallization

    Science.gov (United States)

    Deng, Zhigan; Wei, Chang; Fan, Gang; Li, Xingbin; Li, Minting; Li, Cunxiong

    2018-02-01

    Nickel was separated and precipitated with potassium nickel sulfate hexahydrate [K2Ni(SO4)2·6H2O] from acidic sulfate solution, a leach solution from molybdenum-nickel black shale. The effects of the potassium sulfate (K2SO4) concentration, crystallization temperature, solution pH, and crystallization time on nickel(II) recovery and iron(III) precipitation were investigated, revealing that nickel and iron were separated effectively. The optimum parameters were K2SO4 concentration of 200 g/L, crystallization temperature of 10°C, solution pH of 0.5, and crystallization time of 24 h. Under these conditions, 97.6% nickel(II) was recovered as K2Ni(SO4)2·6H2O crystals while only 2.0% of the total iron(III) was precipitated. After recrystallization, 98.4% pure K2Ni(SO4)2·6H2O crystals were obtained in the solids. The mother liquor was purified by hydrolysis-precipitation followed by cooling, and more than 99.0% K2SO4 could be crystallized. A process flowsheet was developed to separate iron(III) and nickel(II) from acidic-sulfate solution.

  13. Comparative study of electroless nickel film on different organic acids modified cuprammonium fabric (CF)

    Energy Technology Data Exchange (ETDEWEB)

    Zhao, Hang; Lu, Yinxiang, E-mail: yxlu@fudan.edu.cn

    2016-01-30

    Graphical abstract: - Highlights: • An etchant-free and moderate surface pre-treatment process was studied. • Citric acid, malic acid and oxalic acid were selected as modification agents. • High adhesive nickel coating on cuprammonium fabric was obtained. • The electromagnetic parameters were evaluated from the experimental data. - Abstract: Nickel films were grown on citric acid (CA), malic acid (MA) and oxalic acid (OA) modified cuprammonium fabric (CF) substrates via electroless nickel deposition. The nickel films were examined using scanning electron microscopy (SEM) and X-ray diffraction (XRD). Their individual deposition rate and electromagnetic interference (EMI) shielding effectiveness (SE) were also investigated to compare the properties of electroless nickel films. SEM images illustrated that the nickel film on MA modified CF substrate was smooth and uniform, and the density of nickel nuclei was much higher. Compared with that of CA modified CF, the coverage of nickel nuclei on OA and MA modified CF substrate was very limited and the nickel particles size was too big. XRD analysis showed that the nickel films deposited on the different modified CF substrates had a structure with Ni (1 1 1) preferred orientation. All the nickel coatings via different acid modification were firmly adhered to the CF substrates, as demonstrated by an ultrasonic washing test. The result of tensile test indicated that the electroless nickel plating on CF has ability to strengthen the CF substrate while causes limited effect on tensile elongation. Moreover, the nickel film deposited on MA modified CF substrate showed more predominant in EMI SE than that deposited on CA or OA modified CF.

  14. Improvement of acid and base resistance of nickel phosphate pigment by the addition of lanthanum cation

    International Nuclear Information System (INIS)

    Onoda, Hiroaki; Matsui, Hironori; Tanaka, Isao

    2007-01-01

    Transition metal phosphates are used as inorganic pigments, however these materials had a weak point for acid and base resistance. Because lanthanum phosphate is insoluble in acidic and basic solution, the addition of lanthanum cation was tried for the improvement of the acid and base resistance of nickel phosphate pigment. The lanthanum-doped nickel phosphates were prepared from phosphoric acid, nickel nitrate, and lanthanum nitrate solution. The additional effects of lanthanum cation were studied on the chemical composition, particle shape and size distribution, specific surface area, color, acid and base resistance of the precipitations and their thermal products

  15. Ferronickel Preparation from Nickeliferous Laterite by Rotary Kiln-Electric Furnace Process

    Science.gov (United States)

    Li, Guanghui; Jia, Hao; Luo, Jun; Peng, Zhiwei; Zhang, Yuanbo; Jiang, Tao

    Nickel is an important strategic metal, which is mainly used for stainless steel production. In the recent years, ferronickel has been used as a substitute for electrolytic nickel for alleviating the cost of stainless steel production. Rotary kiln-electric furnace (RKEF) smelting is currently the world-wide mainstreaming process for ferronickel production from nickeliferous laterite ore, in spite of the high power consumption. In this study, aiming to provide some meaningful guidance for ferronickel production of RKEF smelting, reductive roasting followed by smelting process was carried out. The conditions including reducing parameters (roasting temperature and time) and smelting parameters (coke dosage, CaO dosage, melting temperature and time) were ascertained. The metal recovery ratios, as well as Ni, Fe, S and P content of ferronickel were considered. The results showed that a ferronickel containing 10. 32 wt. % Ni was obtained from a laterite with 1. 85 wt. % Ni, the nickel recovery ratio was about 99%.

  16. Mechanistic and Kinetic Analysis of Na2SO4-Modified Laterite Decomposition by Thermogravimetry Coupled with Mass Spectrometry.

    Directory of Open Access Journals (Sweden)

    Song Yang

    Full Text Available Nickel laterites cannot be effectively used in physical methods because of their poor crystallinity and fine grain size. Na2SO4 is the most efficient additive for grade enrichment and Ni recovery. However, how Na2SO4 affects the selective reduction of laterite ores has not been clearly investigated. This study investigated the decomposition of laterite with and without the addition of Na2SO4 in an argon atmosphere using thermogravimetry coupled with mass spectrometry (TG-MS. Approximately 25 mg of samples with 20 wt% Na2SO4 was pyrolyzed under a 100 ml/min Ar flow at a heating rate of 10°C/min from room temperature to 1300°C. The kinetic study was based on derivative thermogravimetric (DTG curves. The evolution of the pyrolysis gas composition was detected by mass spectrometry, and the decomposition products were analyzed by X-ray diffraction (XRD. The decomposition behavior of laterite with the addition of Na2SO4 was similar to that of pure laterite below 800°C during the first three stages. However, in the fourth stage, the dolomite decomposed at 897°C, which is approximately 200°C lower than the decomposition of pure laterite. In the last stage, the laterite decomposed and emitted SO2 in the presence of Na2SO4 with an activation energy of 91.37 kJ/mol. The decomposition of laterite with and without the addition of Na2SO4 can be described by one first-order reaction. Moreover, the use of Na2SO4 as the modification agent can reduce the activation energy of laterite decomposition; thus, the reaction rate can be accelerated, and the reaction temperature can be markedly reduced.

  17. 2-Mercaptobenzimidazole, 2-Mercaptobenzothiazole, and Thioglycolic Acid in an Electroless Nickel-Plating Bath

    Directory of Open Access Journals (Sweden)

    Ahmet Ozan Gezerman

    2015-01-01

    Full Text Available The use of three different materials, 2-mercaptobenzimidazole, 2-mercaptobenzothiazole, and thioglycolic acid, was investigated to improve the performance of electroless nickel-plating baths. By changing the concentrations of these materials, sample plates were coated. Optical microscope images were obtained by selecting representative coated plates. From the results of the investigations, the effects of these materials on electroless nickel plating were observed, and the most appropriate amounts of these materials for nickel plating were determined. Moreover, the nickel plating speed observed with the bath solution containing 2-mercaptobenzimidazole, 2-mercaptobenzothiazole, and thioglycolic acid is higher than that in the case of traditional electroless plating baths, but the nickel consumption amount in the former case is lower. In order to minimize the waste water generated from electroless nickel-plating baths, we determined the lowest amounts of the chemicals that can be used for the concentrations reported in the literature.

  18. Zinc-Nickel Codeposition in Sulfate Solution Combined Effect of Cadmium and Boric Acid

    Directory of Open Access Journals (Sweden)

    Y. Addi

    2011-01-01

    Full Text Available The combined effect of cadmium and boric acid on the electrodeposition of zinc-nickel from a sulfate has been investigated. The presence of cadmium ion decreases zinc in the deposit. In solution, cadmium inhibits the zinc ion deposition and suppresses it when deposition potential value is more negative than −1.2 V. Low concentration of CdSO4 reduces the anomalous nature of Zn-Ni deposit. Boric acid decreases current density and shifts potential discharge of nickel and hydrogen to more negative potential. The combination of boric acid and cadmium increases the percentage of nickel in the deposit. Boric acid and cadmium.

  19. Nickel production in Serbia-technological and environmental aspects

    Directory of Open Access Journals (Sweden)

    Željko Kamberović

    2014-12-01

    Full Text Available Demand for nickel is constantly growing due to the versatility of its application, at the first place for stainless steel production. Ore reserves and possibility of nickel production of today’s Serbia and in neighboring countries were thoroughly investigated, and presented work is part of a wider project of sublimation of scientific and professional experience in the field of nickel extractive metallurgy on domestic raw materials. Presented research explores the possibility of high pressure sulfuric acid leaching of Serbian lateritic ores from localities Rudjinci, Ba and Lipovac. All three investigated ore deposits behaved differently both during preparation and during hydrometallurgical treatment. As optimal method for ore preparation proved to be crushing-milling-sieving route, but without possibility of concentrate production. Only for Rudjinci ore deposit achieved leaching efficiency reached satisfactory level of 95%. Within presented paper flow-sheet is proposed for processing high-magnesium laterite ores, with iron and magnesium oxide Both could be recirculated and used again in technological process; MgO for iron precipitation and SO2 for production of leaching agent, sulfuric acid. Final decision on the sustainability of the process will be made according to techno-economic and environmental evaluation. Estimated overall impact of the project implementation on the environment is negative.

  20. Nickel extraction from nickel matte

    Science.gov (United States)

    Subagja, R.

    2018-01-01

    In present work, the results of research activities to make nickel metal from nickel matte are presented. The research activities were covering a) nickel matte characterization using Inductively Couple plasma (ICP), Electron Probe Micro Analyzer (EPMA) and X-Ray Diffraction (XRD), b) nickel matte dissolution process to dissolve nickel from nickel matte into the spent electrolyte solutions that contains hydrochloric acid, c) purification of nickel chloride leach solution by copper cementation process to remove copper using nickel matte, selective precipitation process to remove iron, solvent extraction using Tri normal octyl amine to separate cobalt from nickel chloride solutions and d) Nickel electro winning process to precipitate nickel into the cathode surface from purified nickel chloride solution by using direct current. The research activities created 99, 72 % pure nickel metal as the final product of the process.

  1. Geotechnical, mechanical and geological characterization of lateritic ...

    African Journals Online (AJOL)

    The rock sample powder and lateritic gravels mineralogy were determined using optical microscopy and X-rays diffraction on the total fractions and the fine ones. The overall chemical compositions of major elements of lateritic gravels were determined by the use of X-fluorescence and titrimetry. The results obtained show ...

  2. Requerimientos tecnológicos del transportador de laterita hacia el molino de bolas, de la Empresa Productora de Níquel Comandante Ernesto Guevara; Technological Requirements of the Conveyor Belt which Carries Laterite to the Balls Mill in Nickel Producer

    Directory of Open Access Journals (Sweden)

    Javier Muñoz Álvarez

    2011-02-01

    Full Text Available Se describe el flujo productivo existente en la Empresa Productora del Níquel Comandante Ernesto Guevara,hasta la etapa de la molienda seca, con énfasis en los detalles técnicos de mayor relevancia en el proceso.Se analiza la influencia de la cantidad de mineral en el sistema sobre el comportamiento energético de lamolienda. Finalmente se determinan los requerimientos tecnológicos impuestos por el transportador delaterita 215 - TR - 201 al accionamiento eléctrico, en función de las características y las necesidades delproceso. In the paper, the productive flow existing in the nickel producer enterprise Commandant Ernesto Guevarawas described until the stage of dry milling, with an emphasis on the technical details of greater relevancy inthe process. There was analyzed the influence of the amount of mineral in the system over the energyconsumption performance of the milling. Finally it were identified the technological requirements imposed bythe 215 - TR - 201 laterite carrier to the electric drive, according to the characteristics and needs of theprocess.

  3. Corrosion resistance of nickel alloys with chromium and silicon to the red fuming nitric acid

    International Nuclear Information System (INIS)

    Gurvich, L.Ya.; Zhirnov, A.D.

    1994-01-01

    Corrosion and electrochemical behaviour of binary Ni-Cr, Ni-Si nickel and ternary Ni-Cr-Si alloys in the red fuming nitric acid (RFNA) (8-% of HNO 3 +20% of N 2 O 4 ) is studied. It is shown that nickel alloying with chromium improves its corrosion resistance to the red fuming nitric acid. Nickel alloying with silicon in quantities of up to 5 % reduces, and up to 10%-increases abruptly the corrosion resistance with subsequent decrease of the latter after the further increase of concentration. Ni-15% of Cr alloy alloying with silicon increases monotonously the corrosion resistance. 10 refs., 7 figs., 3 tabs

  4. Leaching behavior of lanthanum, nickel and iron from spent catalyst using inorganic acids

    Science.gov (United States)

    Astuti, W.; Prilitasari, N. M.; Iskandar, Y.; Bratakusuma, D.; Petrus, H. T. B. M.

    2018-01-01

    Highly technological applications of rare earth metals (REs) and scarcity of supply have become an incentive torecover the REs from various resources, which include high grade and low grade ores, as well as recycledwaste materials. Spent hydrocracking catalyst contain lanthanum and a variety of valuable metals such as nickel and iron. This study investigated the recovery of lanthanum, nickel and iron from spent hydrocracking catalyst by leaching using various inorganic acid (sulfuric acid, hydrochloric acid, and nitric acid). The effect of acid concentration, type of acid and leaching temperature was conducted to study the leaching behavior of each valuable metal from spent-catalyst. It has been shown that it is possible to recover more than 90% of lanthanum, however the leaching efficiency of nickel and iron in this process was very low. It can be concluded that the leaching process is selective for lanthanum recovery from hydrocracking spent-catalyst.

  5. Bio-extraction of metal ions from laterite ore by Penicillium ...

    African Journals Online (AJOL)

    Administrator

    2011-09-19

    Sep 19, 2011 ... prolonged weathering, laterite soil is produced. Plentiful oxygen .... to wet digestion process by using nitric acid and hydrogen peroxide as described by ... between 1.9 and 3.1, oxalic acid pH ranges from 1.2 to. 2.9, tartaric ...

  6. 2-Mercaptobenzimidazole, 2-Mercaptobenzothiazole, and Thioglycolic Acid in an Electroless Nickel-Plating Bath

    OpenAIRE

    Ahmet Ozan Gezerman; Burcu Didem Çorbacıoğlu

    2015-01-01

    The use of three different materials, 2-mercaptobenzimidazole, 2-mercaptobenzothiazole, and thioglycolic acid, was investigated to improve the performance of electroless nickel-plating baths. By changing the concentrations of these materials, sample plates were coated. Optical microscope images were obtained by selecting representative coated plates. From the results of the investigations, the effects of these materials on electroless nickel plating were observed, and the most appropriate amo...

  7. Effect of L-ascorbic acid on nickel-induced alterations in serum lipid profiles and liver histopathology in rats.

    Science.gov (United States)

    Das, Kusal K; Gupta, Amrita Das; Dhundasi, Salim A; Patil, Ashok M; Das, Swastika N; Ambekar, Jeevan G

    2006-01-01

    Nickel exposure greatly depletes intracellular ascorbate and alters ascorbate-cholesterol metabolism. We studied the effect of the simultaneous oral treatment with L-ascorbic acid (50 mg/100 g body weight (BW) and nickel sulfate (2.0 mg/100 g BW, i.p) on nickelinduced changes in serum lipid profiles and liver histopathology. Nickel-treated rats showed a significant increase in serum low-density lipoprotein-cholesterol, total cholesterol, triglycerides, and a significant decrease in serum high-density lipoprotein-cholesterol. In the liver, nickel sulfate caused a loss of normal architecture, fatty changes, extensive vacuolization in hepatocytes, eccentric nuclei, and Kupffer cell hypertrophy. Simultaneous administration of L-ascorbic acid with nickel sulfate improved both the lipid profile and liver impairments when compared with rats receiving nickel sulfate only. The results indicate that L-ascorbic acid is beneficial in preventing nickel-induced lipid alterations and hepatocellular damage.

  8. Time-dependent uptake and toxicity of nickel to Enchytraeus crypticus in the presence of humic acid and fulvic acid

    NARCIS (Netherlands)

    He, Erkai; Qiu, Hao; Qiu, Rongliang; Rentenaar, Charlotte; Devresse, Quentin; Van Gestel, Cornelis A.M.

    2017-01-01

    The present study aimed to investigate the influence of different fractions of dissolved organic carbon (DOC) on the uptake and toxicity of nickel (Ni) in the soil invertebrate Enchytraeus crypticus after different exposure times. The addition of DOC as humic acid or fulvic acid significantly

  9. Nickel deficiency disrupts metabolism of ureides, amino acids, and organic acids of young pecan foliage.

    Science.gov (United States)

    Bai, Cheng; Reilly, Charles C; Wood, Bruce W

    2006-02-01

    The existence of nickel (Ni) deficiency is becoming increasingly apparent in crops, especially for ureide-transporting woody perennials, but its physiological role is poorly understood. We evaluated the concentrations of ureides, amino acids, and organic acids in photosynthetic foliar tissue from Ni-sufficient (Ni-S) versus Ni-deficient (Ni-D) pecan (Carya illinoinensis [Wangenh.] K. Koch). Foliage of Ni-D pecan seedlings exhibited metabolic disruption of nitrogen metabolism via ureide catabolism, amino acid metabolism, and ornithine cycle intermediates. Disruption of ureide catabolism in Ni-D foliage resulted in accumulation of xanthine, allantoic acid, ureidoglycolate, and citrulline, but total ureides, urea concentration, and urease activity were reduced. Disruption of amino acid metabolism in Ni-D foliage resulted in accumulation of glycine, valine, isoleucine, tyrosine, tryptophan, arginine, and total free amino acids, and lower concentrations of histidine and glutamic acid. Ni deficiency also disrupted the citric acid cycle, the second stage of respiration, where Ni-D foliage contained very low levels of citrate compared to Ni-S foliage. Disruption of carbon metabolism was also via accumulation of lactic and oxalic acids. The results indicate that mouse-ear, a key morphological symptom, is likely linked to the toxic accumulation of oxalic and lactic acids in the rapidly growing tips and margins of leaflets. Our results support the role of Ni as an essential plant nutrient element. The magnitude of metabolic disruption exhibited in Ni-D pecan is evidence of the existence of unidentified physiological roles for Ni in pecan.

  10. [Nickel exposure to A549 cell damage and L-ascorbic acid interference effect].

    Science.gov (United States)

    Fu, Yao; Wang, Yue; Dan, Han; Zhang, Lin; Ma, Wenhan; Pan, Yulin; Wu, Yonghui

    2015-05-01

    Studying different concentrations of nickel smelting smoke subjects of human lung adenocarcinoma cells (A549) carcinogenic effects, discusses the influence of L-ascorbic acid protection. The A549 cells were divided into experimental and L-ascorbic acid in the intervention group. Plus exposure group concentration of nickel refining dusts were formulated 0.00, 6.25, 12.50, 25.00, 50.00, 100.00 µg/ml suspension, the intervention group on the basis of the added exposure group containing L-ascorbic acid (100 mmol/L), contact 24 h. Detection of cell viability by MTT assay. When the test substance concentration select 0.00, 25.00, 50.00, 100.00 µg/ml experiment for internal Flou-3 fluorescent probe to detect cell Ca²⁺ concentration, within DCFH-DA detect intracellular reactive oxygen (ROS) content, real-time quantitative PCR (real time, in the RT-PCR) was used to detect cell HIF-1α gene expression. With the increase of concentration, subjects increased cell growth inhibition rate, intracellular Ca²⁺ concentration increases, ROS content increased, HIF-1α gene expression increased, differences were statistically significant (P nickel exposure damage to cells. With subjects following exposure to nickel concentration increased, its effect on A549 cell damage increases, L-ascorbic acid cell damage caused by nickel has certain protective effect.

  11. Some physiological and biochemical responses to nickel in salicylic acid applied chickpea (Cicer arietinum L.) seedlings.

    Science.gov (United States)

    Canakci, Songül; Dursun, Bahar

    2011-09-01

    The present study examined the effects of salicylic acid pre-application on the responses of seven-day-old chickpea (Cicer arietinum L.) seedlings to nickel. For this purpose, the plants were treated with 1 mM salicylic acid solution for 6 and 10 hours and then treated with 0.75, 1.5 and 3 mM nickel solutions for 48 hours hydroponically. Following the treatment, changes in seedling length, seedling fresh weight and leaf dry weight (after 10 hours), as well as MDA, proline, protein and pigment contents (after 6 and 10 hours) were examined. Salicylic acid pre-application was found to significantly alleviate the typical harmful effects caused by nickel and 3 mM nickel concentration in particular, on the parameters associated with toxic stress. However, pre-application of salicylic acid for 6 and 10 hours without nickel treatment did not produce any stimulatory or inhibitory effect on the seedlings as compared to the controls.

  12. Geological interpretation of Eastern Cuba Laterites from an airborne magnetic and radioactive isotope survey

    Energy Technology Data Exchange (ETDEWEB)

    Batista, J.A; Blanco, J [Departamento de Geologia, Instituto Superior Minero Metalurgico de Moa, (Cuba); Perez-Flores, M.A [Centro de Investigacion Cientifica y Educacion Superior de Ensenada, Baja California (Mexico)

    2008-04-15

    In eastern Cuba area several geophysical techniques have been applied to distinguish the main geological characteristics of the laterites which are of economical importance for the extraction of iron, nickel and chrome. The geophysical measurements include an aeromagnetic survey and thorium (eTh), potassium (K) and uranium (eU) isotope measurements. The results of gamma spectrometer measurements make a distinction between laterite reservoirs. The application of the magnetic and isotope methods allowed the determination of the distribution and development of the laterite crust, as well as the determination of hydrothermal alterations affecting the laterites, which is very useful for mining exploration and exploitation. Such alterations indicate the presence of silicates, which have negative effects on the metallurgic process. It is known that laterite crust has a high content of eU and eTh. [Spanish] Se han utilizado varias tecnicas geofisicas en la region oriental de Cuba para distinguir las principales caracteristicas geologicas de las lateritas, que poseen importancia economica para la extraccion de hierro, niquel y cobalto. Las mediciones geofisicas incluyen un estudio aeromagnetico y mediciones de isotopos de torio (eTh), potasio (K) y uranio (eU). Los resultados de las mediciones espectrometricas establecen diferencias entre los yacimientos de lateritas. De la aplicacion del metodo magnetico e isotopico se determino la distribucion y desarrollo de las cortezas lateriticas, asi como la ubicacion de alteraciones hidrotermales que afectan a las lateritas, lo cual es muy util durante la exploracion y explotacion minera. Esas alteraciones indican la presencia de silicatos, que tienen un efecto negativo en el proceso metalurgico. Se conoce que las cortezas lateriticas tienen altos contenidos de eU y eTh. De los contenidos de eU y eTh se infiere que las lateritas de la region de Moa se formaron antes que las de Mayari. De estas mediciones fue posible inferir el

  13. Silicate bonded ceramics of laterites

    International Nuclear Information System (INIS)

    Wagh, A.S.; Douse, V.

    1989-05-01

    Sodium silicate is vacuum impregnated in bauxite waste (red mud) at room temperature to develop ceramics of mechanical properties comparable to the sintered ceramics. For a concentration up to 10% the fracture toughness increases from 0.12 MNm -3/2 to 0.9 MNm -3/2 , and the compressive strength from 7 MNm -2 to 30 MNm -2 . The mechanical properties do not deteriorate, when soaked in water for an entire week. The viscosity and the concentration of the silicate solution are crucial, both for the success of the fabrication and the economics of the process. Similar successful results have been obtained for bauxite and lime stone, even though the latter has poor weathering properties. With scanning electron microscopy and energy dispersive analysis, an attempt is made to identify the crystals formed in the composite, which are responsible for the strength. The process is an economic alternative to the sintered ceramics in the construction industry in the tropical countries, rich in lateritic soils and poor in energy. Also the process has all the potential for further development in arid regions abundant in limestone. (author). 6 refs, 20 figs, 3 tabs

  14. Thermoluminescence of laterites: applicability in dating

    International Nuclear Information System (INIS)

    Sankaran, A.V.; Nambi, K.S.V.; Sunta, C.M.

    1985-01-01

    The northward drift of the Indian subcontinent during the past geological periods brought it under the spell of humid tropical climate in post-mesozoic times which initiated chemical weathering processes (lateritization) of the ancient crustal rocks leading to neomineralization. In the present study, thermoluminescence (TL) of these 'later-formed minerals' has been used to date laterites from a number of localities in India. While the TL emission of most of the laterite samples was poor, three from Kerala, Tamil Nadu and Karnataka states, each derived from mineralogically dissimilar parent rock, yielded measurable TL and provided dates in the range of 2 to 3.6 x 10 5 yr. It is suggested that TL dating can be a promising tool for such samples, and especially those with low alpha activity (U, Th at sub-ppm levels). (author)

  15. Thermoluminescence of laterites: applicability in dating

    Energy Technology Data Exchange (ETDEWEB)

    Sankaran, A V; Nambi, K S.V.; Sunta, C M

    1985-01-01

    The northward drift of the Indian subcontinent during the past geological periods brought it under the spell of humid tropical climate in post-mesozoic times which initiated chemical weathering processes (lateritization) of the ancient crustal rocks leading to neomineralization. In the present study, thermoluminescence (TL) of these 'later-formed minerals' has been used to date laterites from a number of localities in India. While the TL emission of most of the laterite samples was poor, three from Kerala, Tamil Nadu and Karnataka states, each derived from mineralogically dissimilar parent rock, yielded measurable TL and provided dates in the range of 2 to 3.6 x 10/sup 5/ yr. It is suggested that TL dating can be a promising tool for such samples, and especially those with low alpha activity (U, Th at sub-ppm levels).

  16. Combinatorial Optimization for Energy Saving in Nickel Industry Non-Newtonian Fluid Pumping System

    International Nuclear Information System (INIS)

    Hernández Ramírez, Gabriel; Legra Lobaina, Aristides; Columbié Navarro, Angel; Marcos Aníbal León Segovia

    2017-01-01

    In the present work a study of the influence of the rheological parameters of the lateritic hydromixtures with the energetic ones of the pumping systems that guarantee the productivity of nickel company 'Commander Pedro Sotto Alba' is carried out. From an experimental study and through an estimator, the rheological parameters are modeled as a function of the factors: temperature, solids content, chemical and granulometric composition. From an appropriate discretization of the model of the lateritic hydrometer pumping system and the application of a Discrete Combination Optimization Double Sequencing procedure, the operating parameters of this system were obtained, in order to guarantee a flow rate of 1600 m3 / h and one Adequate solids concentration. It is concluded that the use of a mathematical model that relates the rheological parameters of the lateritic pulp and the energy parameters of the pumping system, guarantee the metallurgical and energy efficiency in the acid leaching process with an average increase in production between 1000-1500 T Ni + Co / y and an energy saving of 30 MWh /year. (author)

  17. Hydrogenation of Levulinic Acid over Nickel Catalysts Supported on Aluminum Oxide to Prepare γ-Valerolactone

    Directory of Open Access Journals (Sweden)

    Jie Fu

    2015-12-01

    Full Text Available Four types of nickel catalysts supported on aluminum oxide (Ni/Al2O3 with different nickel loadings were synthesized using the co-precipitation method and were used for the hydrogenation of levulinic acid (LA to prepare γ-valerolactone (GVL. The synthesized Ni/Al2O3 catalysts exhibited excellent catalytic activity in dioxane, and the activity of the catalysts was excellent even after being used four times in dioxane. The catalytic activity in dioxane as a solvent was found to be superior to the activity in water. Nitrogen physisorption, X-ray diffraction, and transmission electron microscopy were employed to characterize the fresh and used catalysts. The effects of the nickel loading, temperature, hydrogen pressure, and substrate/catalyst ratio on the catalytic activity were investigated.

  18. The effect of laterite density on radon diffusion behavior.

    Science.gov (United States)

    Li, Yongmei; Tan, Wanyu; Tan, Kaixuan; Liu, Zehua; Fang, Qi; Lv, Junwen; Duan, Xianzhe; Liu, Zhenzhong; Guo, Yueyue

    2018-02-01

    Radon generated in porous media such as soils and rocks migrates into indoor and outdoor air mainly by diffusion, possessing significant hazards to human health. In order to reduce these hazards of radon, it is of great importance to study the diffusion behavior of radon. In this study, we systematically measured the radon diffusion coefficient of laterite with the density ranging from 0.917gcm -3 to 2.238gcm -3 , and studied the effect of laterite density on the radon diffusion. The results show that the radon diffusion coefficient of the laterite generally decreases with the increasing laterite density. In addition, three possible relationships between the radon diffusion coefficient and the laterite density are found out as follows: (1) the linear correlation with a slope of -4.48 × 10 -6 for laterite with density ranging from 0.917 to 1.095gcm -3 , (2) the exponential correlation for laterite with density from 1.095 to 1.63gcm -3 , (3) linear correlation with a slope of -3.1 × 10 -7 for laterite with density from 1.63 to 2.238gcm -3 . The complex relationship between the radon diffusion coefficient and density is caused by the change of porosity and tortuosity of the laterite. Therefore, we suggest that a suitable density should be adopted while using the laterite to effectively cover uranium tailings or economically produce building materials that can curb the radon exhalation. Copyright © 2017 Elsevier Ltd. All rights reserved.

  19. Electrochemical activity of iron in acid treated bentonite and influence of added nickel

    Energy Technology Data Exchange (ETDEWEB)

    Mudrinić, T., E-mail: tihana@nanosys.ihtm.bg.ac.rs [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Mojović, Z.; Milutinović-Nikolić, A. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Mojović, M. [University of Belgrade, Faculty of Physical Chemistry, Studenski trg 12-16, 11000 Belgrade (Serbia); Žunić, M. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia); Vukelić, N. [University of Belgrade, Faculty of Physical Chemistry, Studenski trg 12-16, 11000 Belgrade (Serbia); Jovanović, D. [University of Belgrade-Institute of Chemistry, Technology and Metallurgy, Center for Catalysis and Chemical Engineering, Njegoševa 12, 11000 Belgrade (Serbia)

    2015-10-30

    Highlights: • Mild acid treatment followed by incorporation of nickel was performed on bentonite. • Modified bentonites based electrodes were tested in H{sub 2}SO{sub 4} by cyclic voltammetry. • Acid treatment increased current response of electroactive iron within smectite. • Incorporation of Ni improved reversibility of Fe{sup 2+}/Fe{sup 3+} oxidation/reduction process. - Abstract: Bentonite originated from Mečji Do, Serbia, was submitted to acid treatment at 70 °C for 30 min, while only the concentration of applied HCl varied. The obtained acid treated samples were used to modify glassy carbon (GC) electrode. The effect of applied acid treatment on the electrochemical behavior of GC electrodes modified with these materials was investigated. Furthermore, the effect of the introduction of nickel into acid treated samples was studied. The incorporation of nickel into acid treated bentonite was achieved by either ion exchange or impregnation/decomposition method. The obtained samples were characterized using the following methods: inductively coupled plasma (ICP), X-ray diffraction (XRD), Fourier transform infrared (FTIR) spectroscopy and electron spin resonance (ESR) spectroscopy. The electrochemical behavior of these samples was tested by cyclic voltammetry in 0.1 mol dm{sup −3} H{sub 2}SO{sub 4} solution. The ICP, FTIR and ESR results exhibited a slight decrease of iron content in the acid treated samples. XRD and FTIR results confirmed that the conditions applied for the acid treatment were mild enough for the smectite structure to be preserved. The electrocatalytic test showed that the current response of Fe{sup 2+}/Fe{sup 3+} oxidation/reduction process increased on the GC electrodes separately modified with each of the acid treated samples in comparison with current obtained on the GC electrode modified with untreated sample. These results indicated that applied acid treatment probably increased the accessibility of the electroactive iron within

  20. Comments on the paper: 'Optical reflectance, optical refractive index and optical conductivity measurements of nonlinear optics for L-aspartic acid nickel chloride single crystal'

    Science.gov (United States)

    Srinivasan, Bikshandarkoil R.; Naik, Suvidha G.; Dhavskar, Kiran T.

    2016-02-01

    We argue that the 'L-aspartic acid nickel chloride' crystal reported by the authors of the title paper (Optics Communications, 291 (2013) 304-308) is actually the well-known diaqua(L-aspartato)nickel(II) hydrate crystal.

  1. Hydrometallurgical processing of nickel lateritic ores / Гидрометаллургическая обработка латеритных руд никеля / Hidrometalurško tretiranje lateritnih ruda nikla

    Directory of Open Access Journals (Sweden)

    Srećko R. Stopić

    2016-10-01

    Full Text Available Nickel production is a very important activity for the European Union because nickel is a unique constituent of stainless steel. Europe has lateritic (oxidic ore deposits along a very well-known belt starting from the Alps and ending to the Himalayas. The lateritic belt passes through western Balkans and Greece and continues through Turkey to Asia. The known lateritic deposits in Serbia are located in three different areas called: Zapadna Morava (Rudjinci, Veluce, Ba, Sumadija (Lipovac, Kolarevici, Bucje and Mokra Gora, which have many natural resources such as forests, rivers, etc. Therefore, it is very important to understand and show hydrometallurgical treatments of lateritic ores via mining and metallurgy in different parts of the world. In this paper, several exploitation scenarios for hydrometallurgical treatment and benefication of lateritic ores will be shown: Direct Nickel Process, Ravensthorpe and Murrin Murrin in Australia and Meta Cobalt Nickel in Turkey. / Производство никеля представляет важную отрасль промышленности в Евросоюзе, так как никель является составляющим элементом в производстве нержавеющей стали. Европа обладает ресурсами оксидных руд, находящихся на большой территории от Альп до Гималаев, охватывая западную часть Балкан и Грецию, простилаясь через Турцию до Азии. Известные резервы латеритных руд находятся в Сербии, располагаясь в трех зонах: Западная Морава (Руждинцы, Велуце, Ба, Шумадия (Липовац, Коларевичи, Бучье и Мокра Гора, представляющих собой природные ресурсы,

  2. 3-D periodic mesoporous nickel oxide for nonenzymatic uric acid sensors with improved sensitivity

    Science.gov (United States)

    Huang, Wei; Cao, Yang; Chen, Yong; Zhou, Yang; Huang, Qingyou

    2015-12-01

    3-D periodic mesoporous nickel oxide (NiO) particles with crystalline walls have been synthesized through the microwave-assisted hard template route toward the KIT-6 silica. It was investigated as a nonenzymatic amperometric sensor for the detection of uric acid. 3-D periodic nickel oxide matrix has been obtained by the hard template route from the KIT-6 silica template. The crystalline nickel oxide belonged to the Ia3d space group, and its structure was characterized by X-ray diffraction (XRD), N2 adsorption-desorption, and transmission electron microscopy (TEM). The analysis results showed that the microwave-assisted mesoporous NiO materials were more appropriate to be electrochemical sensors than the traditional mesoporous NiO. Cyclic voltammetry (CV) revealed that 3-D periodic NiO exhibited a direct electrocatalytic activity for the oxidation of uric acid in sodium hydroxide solution. The enzyme-less amperometric sensor used in the detection of uric acid with detection limit of 0.005 μM (S/N = 3) over wide linear detection ranges up to 0.374 mM and with a high sensitivity of 756.26 μA mM-1 cm-2, and a possible mechanism was also given in the paper.

  3. Mathematical models to predict rheological parameters of lateritic hydromixtures

    OpenAIRE

    Gabriel Hernández-Ramírez; Arístides A. Legrá-Lobaina; Beatriz Ramírez-Serrano; Liudmila Pérez-García

    2017-01-01

    The present work had as objective to establish mathematical models that allow the prognosis of the rheological parameters of the lateritic pulp at concentrations of solids from 35% to 48%, temperature of the preheated hydromixture superior to 82 ° C and number of mineral between 3 and 16. Four samples of lateritic pulp were used in the study at different process locations. The results allowed defining that the plastic properties of the lateritic pulp in the conditions of this study conform to...

  4. Ultrasound augmented leaching of nickel sulfate in sulfuric acid and hydrogen peroxide media.

    Science.gov (United States)

    Li, Haoyu; Li, Shiwei; Peng, Jinhui; Srinivasakannan, Chandrasekar; Zhang, Libo; Yin, Shaohua

    2018-01-01

    A new method of preparation high purity nickel sulfate assisted by ultrasonic was studied. The process mechanism was analyzed by Inductively Coupled Plasma (ICP), X-ray diffraction (XRD), Scanning electron microscopy (SEM), and Energy dispersive X-ray spectrometry (EDS).The reaction mechanisms of oxidizing leaching and ultrasonic leaching were explored, respectively. Results showed that ultrasonic treatment peel off the oxide film on the surface of nickel. The leachate under strongly agitated, the yield rate of nickel sulfate was accelerate. And the reaction area was increased by the cavitation effect, the liquid-solid reaction was promoted, and the activation energy was reduced. The leaching rate of nickel reached 46.29% by conventional leaching, which takes about 5h. Under the same conditions, the ultrasonic leaching rate reached 40%, only half of the conventional leaching time. Concentration of leaching agent, reaction temperature, ultrasonic power, leaching time had significant effect on the enhancement of the leaching reaction with ultrasonic radiation. The leaching rate of 60.41% under the optimum experiment conditions as follows: sulfuric acid concentration 30%, hydrogen peroxide 10%, leaching temperature 333K, ultrasonic power 200W and leaching time 4h. The kinetic study of the system was investigated, and the reaction rates of conventional leaching and ultrasonic leaching were controlled by diffusion, and the apparent activation energies were 16.2kJ/mol and 11.83kJ/mol. Copyright © 2017. Published by Elsevier B.V.

  5. Influence of Surface Pretreatment on the Corrosion Resistance of Cold-Sprayed Nickel Coatings in Acidic Chloride Solution

    Science.gov (United States)

    Scendo, Mieczyslaw; Zorawski, Wojciech; Staszewska-Samson, Katarzyna; Makrenek, Medard; Goral, Anna

    2018-03-01

    Corrosion resistance of the cold-sprayed nickel coatings deposited on the Ni surface (substrate) without and with abrasive grit-blasting treatment of the substrate was investigated. The corundum powder with different grain sizes was used. The corrosive environment contained an acidic chloride solution. The mechanism of the corrosion of nickel was suggested and discussed. Corrosion electrochemical parameters were determined by electrochemical methods. The corrosion effect of a nickel coating depends on the grain size used to prepare the substrate. The nickel coating after the medium grit-blasting treatment of the substrate was found to be the most corrosion resistant. However, the smallest resistance on the corrosion effect should be attributed to the nickel coating on the substrate after the coarse grit-blasting treatment.

  6. Nickel-cadmium batteries: effect of electrode phase composition on acid leaching process.

    Science.gov (United States)

    Nogueira, C A; Margarido, F

    2012-01-01

    At the end of their life, Ni-Cd batteries cause a number of environmental problems because of the heavy metals they contain. Because of this, recycling of Ni-Cd batteries has been carried out by dedicated companies using, normally, pyrometallurgical technologies. As an alternative, hydrometallurgical processes have been developed based on leaching operations using several types of leachants. The effect of factors like temperature, acid concentration, reaction time, stirring speed and grinding of material on the leaching yields of metals contained in anodic and cathodic materials (nickel, cadmium and cobalt) using sulphuric acid, is herein explained based on the structural composition of the electrode materials. The nickel, cobalt and cadmium hydroxide phases, even with a small reaction time (less than 15 minutes) and low temperature (50 degrees C) and acid concentration (1.1 M H2SO4), were efficiently leached. However, leaching of the nickel metallic phase was more difficult, requiring higher values of temperature, acid concentration and reaction time (e.g. 85 degrees C, 1.1 M H2SO4 and 5 h, respectively) in order to obtain a good leaching efficiency for anodic and cathodic materials (70% and 93% respectively). The stirring speed was not significant, whereas the grinding of electrode materials seems to promote the compaction of particles, which appears to be critical in the leaching of Ni degrees. These results allowed the identification and understanding of the relationship between the structural composition of electrode materials and the most important factors that affect the H2SO4 leaching of spent Ni-Cd battery electrodes, in order to obtain better metal-recovery efficiency.

  7. Stabilization of Ikpayongo laterite with cement and calcium carbide ...

    African Journals Online (AJOL)

    Laterite obtained from Ikpayongo was stabilized with 2-10 % cement and 2-10 % Calcium Carbide waste, for use as pavement material. Atterberg's limits test, California bearing ratio (CBR) and unconfined compressive strength (UCS) tests were conducted on the natural laterite and the treated soil specimens. The plasticity ...

  8. 3-D periodic mesoporous nickel oxide for nonenzymatic uric acid sensors with improved sensitivity

    International Nuclear Information System (INIS)

    Huang, Wei; Cao, Yang; Chen, Yong; Zhou, Yang; Huang, Qingyou

    2015-01-01

    Graphical abstract: The enzyme-less amperometric sensor based on 3-D periodic mesoporous NiO nanomaterials used in the detection of uric acid with detection limit of 0.005 μM (S/N = 3) over wide linear detection ranges up to 0.374 mM and with a high sensitivity of 756.26 μA mM"−"1 cm"−"2. - Highlights: • Microwave-assisted method was used to fabricate the 3-D periodic mesoporous NiO particles. • The mesoporous nickel oxide was applied to nonenzymatic uric acid biosensor. • The detection limit is 0.005 μM over wide linear detection ranges up to 0.374 mM. • The sensitivity is 756.26 μA mM"−"1 cm"−"2. - Abstract: 3-D periodic mesoporous nickel oxide (NiO) particles with crystalline walls have been synthesized through the microwave-assisted hard template route toward the KIT-6 silica. It was investigated as a nonenzymatic amperometric sensor for the detection of uric acid. 3-D periodic nickel oxide matrix has been obtained by the hard template route from the KIT-6 silica template. The crystalline nickel oxide belonged to the Ia3d space group, and its structure was characterized by X-ray diffraction (XRD), N_2 adsorption–desorption, and transmission electron microscopy (TEM). The analysis results showed that the microwave-assisted mesoporous NiO materials were more appropriate to be electrochemical sensors than the traditional mesoporous NiO. Cyclic voltammetry (CV) revealed that 3-D periodic NiO exhibited a direct electrocatalytic activity for the oxidation of uric acid in sodium hydroxide solution. The enzyme-less amperometric sensor used in the detection of uric acid with detection limit of 0.005 μM (S/N = 3) over wide linear detection ranges up to 0.374 mM and with a high sensitivity of 756.26 μA mM"−"1 cm"−"2, and a possible mechanism was also given in the paper.

  9. 3-D periodic mesoporous nickel oxide for nonenzymatic uric acid sensors with improved sensitivity

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Wei; Cao, Yang, E-mail: caowang507@163.com; Chen, Yong; Zhou, Yang; Huang, Qingyou

    2015-12-30

    Graphical abstract: The enzyme-less amperometric sensor based on 3-D periodic mesoporous NiO nanomaterials used in the detection of uric acid with detection limit of 0.005 μM (S/N = 3) over wide linear detection ranges up to 0.374 mM and with a high sensitivity of 756.26 μA mM{sup −1} cm{sup −2}. - Highlights: • Microwave-assisted method was used to fabricate the 3-D periodic mesoporous NiO particles. • The mesoporous nickel oxide was applied to nonenzymatic uric acid biosensor. • The detection limit is 0.005 μM over wide linear detection ranges up to 0.374 mM. • The sensitivity is 756.26 μA mM{sup −1} cm{sup −2}. - Abstract: 3-D periodic mesoporous nickel oxide (NiO) particles with crystalline walls have been synthesized through the microwave-assisted hard template route toward the KIT-6 silica. It was investigated as a nonenzymatic amperometric sensor for the detection of uric acid. 3-D periodic nickel oxide matrix has been obtained by the hard template route from the KIT-6 silica template. The crystalline nickel oxide belonged to the Ia3d space group, and its structure was characterized by X-ray diffraction (XRD), N{sub 2} adsorption–desorption, and transmission electron microscopy (TEM). The analysis results showed that the microwave-assisted mesoporous NiO materials were more appropriate to be electrochemical sensors than the traditional mesoporous NiO. Cyclic voltammetry (CV) revealed that 3-D periodic NiO exhibited a direct electrocatalytic activity for the oxidation of uric acid in sodium hydroxide solution. The enzyme-less amperometric sensor used in the detection of uric acid with detection limit of 0.005 μM (S/N = 3) over wide linear detection ranges up to 0.374 mM and with a high sensitivity of 756.26 μA mM{sup −1} cm{sup −2}, and a possible mechanism was also given in the paper.

  10. Assessment of corrosion resistance of cast cobalt- and nickel-chromium dental alloys in acidic environments.

    Science.gov (United States)

    Mercieca, Sven; Caligari Conti, Malcolm; Buhagiar, Joseph; Camilleri, Josette

    2018-01-01

    The aim of this study was to compare the degradation resistance of nickel-chromium (Ni-Cr) and cobalt-chromium (Co-Cr) alloys used as a base material for partial dentures in contact with saliva. Wiron® 99 and Wironit Extra-Hard® were selected as representative casting alloys for Ni-Cr and Co-Cr alloys, respectively. The alloys were tested in contact with deionized water, artificial saliva and acidified artificial saliva. Material characterization was performed by X-ray diffractometry (XRD) and microhardness and nanohardness testing. The corrosion properties of the materials were then analyzed using open circuit potential analysis and potentiodynamic analysis. Alloy leaching in solution was assessed by inductively coupled plasma mass spectrometry techniques. Co-Cr alloy was more stable than the Ni-Cr alloy in all solutions tested. Leaching of nickel and corrosion attack was higher in Ni-Cr alloy in artificial saliva compared with the acidified saliva. The corrosion resistance of the Co-Cr alloy was seen to be superior to that of the Ni-Cr alloy, with the former exhibiting a lower corrosion current in all test solutions. Microstructural topographical changes were observed for Ni-Cr alloy in contact with artificial saliva. The Ni-Cr alloy exhibited microstructural changes and lower corrosion resistance in artificial saliva. The acidic changes did not enhance the alloy degradation. Ni-Cr alloys are unstable in solution and leach nickel. Co-Cr alloys should be preferred for clinical use.

  11. Synthesis and characterization of Mono-Aqua-Pentakis (Isoni-Cotinic Acid) Nickel (II) Sulfate Trihydrate

    Science.gov (United States)

    Syaima, H.; Rahardjo, S. B.; Amanati, N.

    2018-05-01

    A complex of nickel (II) with isonicotinic acid (asint) was successfully obtained. The complex was synthesized in 1:2 mole ratio of metal to the ligand in methanol. The percentage of nickel was 6.91% determined by Atomic Absorption Spectroscopy (AAS). Therefore, the predicted formula was Ni(asint)5SO4(H2O)4. The molar conductivity of the complex was measured by conductivity meter corresponding to 1:1 electrolyte. The thermal analysis of the formed complex was determined by Differential Thermal Analysis (DTA) indicating that the complex contains four water molecules as ligand and hydrates. The magnetic susceptibility measurement showed that the complex was paramagnetic with μeff= 3.30 B.M. Electronic spectra of the formed complex appeared at two transition peaks on λ= 394 nm and 659 nm. The infrared spectra of the complex showed a shift of tertiary N-group absorption in 1234 and 1338 cm-1 compared to isonicotinic acid at 1149 and 1331 cm-1. In addition, the shift also appeared in the -OH group absorption which was to the lower wavenumber at 3371 cm-1 from 3425 cm-1 (isonicotinic acid). This fact indicated that the functional groups were coordinated to the central metal ion. The possibility formula of the complex was [Ni(asint)5(H2O)]SO4·3H2O with octahedral structure.

  12. Mobility of gamma-emitting fission products in typical black and laterite soils

    International Nuclear Information System (INIS)

    D'Souza, T.J.; Mistry, K.B.

    1981-01-01

    Studies on the movement of the gamma-emitting fission products 106 Ru, 125 Sb, 137 Cs and 144 Ce, surface deposited on columns of the black and laterite soils revealed that the mobility of these nuclides in the two soils depended mainly on the ionic form of the nuclide, soil reaction and predominant clay mineral type in the soil. Results showed a rapid breakthrough of 106 Ru in the black soil and considerable migration to the lower layers in the laterite soil on leaching with rain water, or moderately high calcium or sodium irrigation waters. While near complete fixation of 144 Ce and 137 Cs in the top contaminated layer of both soils was observed, a slight movement of 125 Sb only in the black soil was noticed. Incorporation of organic matter had no effects on the movement of fission products in both soil types, whereas ethylenediaminetraacetic acid (EDTA) induced variable movement of the different radionuclides in the two soil types. (author)

  13. The Corrosion Behavior of Nickel and Inconel 600 in Sodium Hydroxide and Hydrochloric Acid Solution at 280 .deg. C

    International Nuclear Information System (INIS)

    Lee, Ihh Chong; Suk, Tae Won

    1980-01-01

    The corrosion behavior of nickel and Inconel 600 has been investigated by the weight change measurement method at pH ranges 3∼13 of the solution. The specimens were exposed to aqueous solutions in a static autoclave at 280 .deg. C for 210 hours. The pH of the solutions was adjusted by hydrochloric acid and sodium hydroxide and the dissolved oxygen concentration was fixed as 10 ppb by using pure nitrogen gas. Weight loss of Inconel 600 was much less than that of nickel over the tested pH ranges. At pH 9.5, nickel and Inconel 600 showed the minimum weight loss phenomenon and the values of weight loss were 1.5mg/dm 2 and 0.9mg/dm 2 , respectively. Microscopic examination showed that nickel surface was attacked uniformly, whereas Inconel 600 surface was not greatly

  14. Straining electrode behavior and corrosion resistance of nickel base alloys in high temperature acidic solution

    International Nuclear Information System (INIS)

    Yamanaka, Kazuo

    1992-01-01

    Repassivation behavior and IGA resistance of nickel base alloys containing 0∼30 wt% chromium was investigated in high temperature acid sulfate solution. (1) The repassivation rate was increased with increasing chromium content. And so the amounts of charge caused by the metal dissolution were decreased with increasing chromium content. (2) Mill-annealed Alloy 600 suffered IGA at low pH environment below about 3.5 at the fixed potentials above the corrosion potential in 10%Na 2 SO 4 +H 2 SO 4 solution at 598K. On the other hand, thermally-treated Alloy 690 was hard to occur IGA at low pH environments which mill-annealed Alloy 600 occurred IGA. (3) It was considered that the reason, why nickel base alloys containing high chromium content such as Alloy 690 (60%Ni-30%Cr-10%Fe) had high IGA/SCC resistance in high temperature acidic solution containing sulfate ion, is due to both the promotion of the repassivation and the suppression of the film dissolution by the formation of the dense chromium oxide film

  15. Corrosion of stainless steels and nickel-base alloys in solutions of nitric acid and hydrofluoric acid

    International Nuclear Information System (INIS)

    Horn, E.M.; Renner, M.

    1992-01-01

    Reactions involving nitric acid may always result in the contamination of this acid with fluorides. In highly concentrted nitric acid, the presence of small amounts of HF will substantially reduce the corrosion of metallic materials. Mixtures consisting of hydrofluoric acid and hypo-azeotropic nitric acid on the other hand will strongly attack: the metal loss will markedly increase with increasing HNO 3 and HF concentrations as well as with rising temperatures. The investigation covered 12 stainless steel grades and nickel-base alloys. With constant HNO 3 content, corrosion rates will rise linearly when increasing the HF concentration. With constant HF concentration (0,25 M), corrosion rates will increase rapidly with increasing nitric acid concentration (from 0.3 M to 14.8 M). This can best be described by superimposing a linear function and a hyperbolic function that is reflecting the change in the HNO 3 content. Alloys containing as much chromium as possible (up to 46 wt.%) will exhibit the best corrosion resistance. Alloy NiCr30FeMo (Hastelloy alloy G-30) proved to be well suitable in this investigation. (orig.) [de

  16. Nickel Deficiency Disrupts Metabolism of Ureides, Amino Acids, and Organic Acids of Young Pecan Foliage[OA

    Science.gov (United States)

    Bai, Cheng; Reilly, Charles C.; Wood, Bruce W.

    2006-01-01

    The existence of nickel (Ni) deficiency is becoming increasingly apparent in crops, especially for ureide-transporting woody perennials, but its physiological role is poorly understood. We evaluated the concentrations of ureides, amino acids, and organic acids in photosynthetic foliar tissue from Ni-sufficient (Ni-S) versus Ni-deficient (Ni-D) pecan (Carya illinoinensis [Wangenh.] K. Koch). Foliage of Ni-D pecan seedlings exhibited metabolic disruption of nitrogen metabolism via ureide catabolism, amino acid metabolism, and ornithine cycle intermediates. Disruption of ureide catabolism in Ni-D foliage resulted in accumulation of xanthine, allantoic acid, ureidoglycolate, and citrulline, but total ureides, urea concentration, and urease activity were reduced. Disruption of amino acid metabolism in Ni-D foliage resulted in accumulation of glycine, valine, isoleucine, tyrosine, tryptophan, arginine, and total free amino acids, and lower concentrations of histidine and glutamic acid. Ni deficiency also disrupted the citric acid cycle, the second stage of respiration, where Ni-D foliage contained very low levels of citrate compared to Ni-S foliage. Disruption of carbon metabolism was also via accumulation of lactic and oxalic acids. The results indicate that mouse-ear, a key morphological symptom, is likely linked to the toxic accumulation of oxalic and lactic acids in the rapidly growing tips and margins of leaflets. Our results support the role of Ni as an essential plant nutrient element. The magnitude of metabolic disruption exhibited in Ni-D pecan is evidence of the existence of unidentified physiological roles for Ni in pecan. PMID:16415214

  17. Summary of a Situation from Laboratory Investigation of Yugoslav Nickel Bearing Ores by Segregation-Flotation-Magnetic Separation

    OpenAIRE

    Krstev, Boris; Ilic, Ilija

    1988-01-01

    A huge list of current laterite operations or laterites processing is following: Fe - ni smelting, Matte smelting, Reduction roasting-ammonia leaching and HPA leaching. Apart from the above mentioned process routes, there have been many attempts to develop processes know as alternative processes, which have included: Sulphuric, Nitric acid leaching, Chlorine leaching, Acid pugging and sulphating roast, especially Segregation Process etc.

  18. Column leaching of chromium and nickel from a contaminated soil using EDTA and citric acid

    International Nuclear Information System (INIS)

    Jean-Soro, Liliane; Bordas, François; Bollinger, Jean-Claude

    2012-01-01

    This study investigates the column leaching of a soil contaminated mainly with Cr and Ni by using two chelants: citric acid (biodegradable) and EDTA (non-biodegradable) followed with water rinse. The chelants lead to Cr and Ni leaching, in addition to major elements (Ca, Fe, Mg, Al, Mn and Zn) showing the dissolution of soil mineral constituents. EDTA leaches more major elements and Ni than citric acid related to the respective stability of metal–chelant complexes; citric acid leaches more Cr than EDTA, certainly because of a substitution reaction with Cr(VI). In the case of alternating chelant/water applications, leaching occurs during the chelant applications, but also during water applications. In the case of chelant/water applications followed by continuous water application, both Cr and Ni leach over time. This increased mobility could be due to the residual chelant present in soil as well as to the dissolution/mobilization of mineral or organic soil fractions. - Highlights: ► Column leaching of an industrial soil contaminated with chromium and nickel. ► Citric acid or EDTA were used alternatively or followed with water rinse. ► Chelants lead to Cr and Ni leaching and the dissolution of soil mineral constituents. ► Leaching of these two metals proceeds continuously during water rinse. ► Chelants deeply impacted Cr and Ni mobility. - Citric acid or EDTA application deeply impact Cr and Ni mobility during column leaching of a contaminated soil.

  19. Mineralogical and geochemical aspects of nickeliferous laterite of Vermelho region, Serra dos Carajas (State of Para)

    International Nuclear Information System (INIS)

    Almeida Correa, S.L. de.

    1982-01-01

    Mineralogical and geochemical studies were carried out on the nickeliferous laterite of Vermelho region (Serra of Carajas, state of Para). A total of 64 samples were analysed by X-ray fluorescence analysis and atomic absorption, spectrophotometry, including bed-rock specimens. The laterite is derived from ultramafic rocks (serpentinites) and there horizons were recognized towards the top: saprolitic horizon with a thickness of more than 4 meters, clay horizon 6,1 meters thick and limonitic horizon with a thickness of 8,3 meters. The process of weathering affected both major and trace elements which were bleached, transported and reprecipitated. This caused variations in the concentration of the elements with depth, except for magnesium which was extensively bleached. Nickel concentrations in the clay horizon probably was a result of ion exchange between smectite and Ni-bearing solutions, the source of this Ni being goethite. Cobalt and zinc were also strongly enriched during the process of laterization, although maximum concentrations of these elements are found in different horizons. (author)

  20. chemical and mineralogical characterization of lateritic iron ore

    African Journals Online (AJOL)

    DJFLEX

    2010-04-22

    Apr 22, 2010 ... The laterite iron ore deposit at Auchi, Edo State, Nigeria was studied chemically and mineralogically. The results of the chemical ... SAMPLE PREPARATION. The samples .... 2µm) and were subjected to X-ray diffraction using.

  1. geometric models for lateritic soil stabilized with cement

    African Journals Online (AJOL)

    user

    stabilized lateritic soil and also to develop geometric models. The compaction, California .... on how effective limited field data are put to use in decision-making. ..... silicates was described as the most important phase of cement and the ...

  2. stabilization of ikpayongo laterite with cement and calcium carbide

    African Journals Online (AJOL)

    PROF EKWUEME

    Laterite obtained from Ikpayongo was stabilized with 2-10 % cement and 2-10 % Calcium Carbide waste, for use .... or open dumping which have effect on surface and ... Table 1: Chemical Composition of Calcium Carbide Waste and Cement.

  3. Effect of citric acid and EDTA on chromium and nickel uptake and translocation by Datura innoxia

    International Nuclear Information System (INIS)

    Jean, Liliane; Bordas, Francois; Gautier-Moussard, Cecile; Vernay, Philippe; Hitmi, Adnane; Bollinger, Jean-Claude

    2008-01-01

    EDTA and citric acid were tested to solubilize metals and enhance their uptake by Datura innoxia, chosen because of its ability to accumulate and tolerate metals. Two application modes were used on an industrial soil contaminated mainly by Cr and Ni. The results showed that citric acid was the most effective at increasing the uptake of Cr and EDTA for Ni. These results are consistent with the effectiveness of both chelants in solubilizing metals from the soil. The translocation factor (TF) of Ni was 1.6- and 6.7-fold higher than the control, respectively, for one and two applications of 1 mmol kg -1 EDTA. After two applications of 5 and 10 mmol kg -1 citric acid, the TF of Cr increased 2- and 3.5-fold relative to the control. Whatever the concentration, the application of EDTA modified the plant physiology significantly. For citric acid this was only observed with the highest dose (10 mmol kg -1 ). - Chelant effectiveness in increasing chromium and nickel uptake by Datura innoxia is the result of the increase in translocation versus negative effect on plant physiology

  4. Electroless nickel plating on abs plastics from nickel chloride and nickel sulfate baths

    International Nuclear Information System (INIS)

    Inam-ul-haque; Ahmad, S.; Khan, A.

    2005-01-01

    Aqueous acid nickel chloride and alkaline nickel sulphate bath were studied for electroless nickel planting on acrylonitrile-butadiene-styrene (ABS) plastic. Before electroless nickel plating, specimens were etched, sensitized and activated. Effects of sodium hypophosphite and sodium citrate concentration on the electroless nickel plating thickness were discussed. Aqueous acid nickel chloride bath comprising, nickel chloride 10 g/L, sodium hypophosphite 40 g/L, sodium citrate 40g/L at pH 5.5, temperature 85 deg. C and density of 1 Be/ for thirty minutes gave best coating thickness in micrometer. It was found that acid nickel chloride bath had a greater stability, wide operating range and better coating thickness results than alkaline nickel sulphate bath. Acid nickel chloride bath gave better coating thickness than alkaline nickel sulfate bath

  5. Could humic acid relieve the biochemical toxicities and DNA damage caused by nickel and deltamethrin in earthworms (Eisenia foetida)?

    Science.gov (United States)

    Shen, Chen-Chao; Shen, Dong-Sheng; Shentu, Jia-Li; Wang, Mei-Zhen; Wan, Ming-Yang

    2015-12-01

    The aim of the study was to determine whether humic acid (HA) prevented gene and biochemical toxic effects in earthworms (Eisenia foetida) exposed to nickel and deltamethrin (at 100 and 1 mg kg(-1), respectively) in soil. Cellular- and molecular-level toxic effects of nickel and deltamethrin in earthworms were evaluated by measuring damage to lipid membranes and DNA and the production of protein carbonyls over 42 days of exposure. Nickel and deltamethrin induced significant levels of oxidative stress in earthworms, increasing the production of peroxidation products (malondialdehyde and protein carbonyls) and increasing the comet assay tail DNA% (determined by single-cell gel electrophoresis). DNA damage was the most sensitive of the three indices because it gave a higher sample/control ratio than did the other indices. The presence of HA alleviated (in decreasing order of effectiveness) damage to DNA, proteins, and lipid membranes caused by nickel and deltamethrin. A low HA dose (0.5-1% HA in soil) prevented a great deal of lipid membrane damage, but the highest HA dose (3% HA in soil) prevented still more DNA damage. However, the malondialdehyde concentrations in earthworms were higher at the highest HA dose than at the lower HA doses. The amounts of protein carbonyls produced at different HA doses were not significantly different. The toxic effects to earthworms caused by increased oxidizable nickel concentrations could be relieved by adding HA.

  6. Effect of the application of ultrasonic waves on the leaching of nickel ore

    International Nuclear Information System (INIS)

    Reyes Padilla, Osniel; Castellanos Suarez, Jose; Hernandez Martinez, A. Naida; Cortes Miranda, Maritza; Abraham Islas, Osvel; Cardenas Merella, Rodnie; Trujillo, Maria Elena; Nicot, Yarisleydis; Calzada, Lidia; Sanabria de la Torre, Antonio; Echaide Hernandez, Marcos Julio

    2016-01-01

    The use of the ultrasonic waves (OU) he/she has been successful in some fields like: the medicine, in catalysts, treatments of foods and in the chemical procedures of laboratory. The applications of OU in the mining are not very well-known and it is not reported in detail in the literature. In the CIPIMM they have been carried out some test in the laboratory with positive results, for what the studies of this technique are continued. The objective of this work was to evaluate in a preliminary phase the application of ultrasonic waves in the process of lixiviation of nickel minerals. The prepared pulps with the mineral were treated in an ultrasonic bathroom at laboratory level. In the process of atmospheric lixiviation with H 2 SO 4 , the application of OU produced an increment in the nickel breakup between a 2 and 5%. The kinetics of breakup of Co was quicker than that of the nickel. The use of OU doesn't increase in a significant way the breakup of the iron, making that the process is selective. It was observed that the treatment with OU of 60 minutes during the lixiviation of the pulp of mineral lateritic (Serpentine of Nicaro) it was enough. The reported maximum recovery of Neither and Co was: 69% neither and 33% Co. The acid consumption (which represents 70% of the costs of industrial process) was between 11 to 20 t of acid per ton of nickel leached, being lower than the average reported consumption (26 ton acid / ton nickel) in the industrial plant acid pressure leaching in Moa. (Author)

  7. Human exposure to nickel

    Energy Technology Data Exchange (ETDEWEB)

    Grandjean, P

    1984-01-01

    In order of abundance in the earth's crust, nickel ranks as the 24th element and has been detected in different media in all parts of the biosphere. Thus, humans are constantly exposed to this ubiquitous element, though in variable amounts. Occupational exposures may lead to the retention of 100 micrograms of nickel per day. Environmental nickel levels depend particularly on natural sources, pollution from nickel-manufacturing industries and airborne particles from combustion of fossil fuels. Absorption from atmospheric nickel pollution is of minor concern. Vegetables usually contain more nickel than do other food items. Certain products, such as baking powder and cocoa powder, have been found to contain excessive amounts of nickel, perhaps related to nickel leaching during the manufacturing process. Soft drinking-water and acid beverages may dissolve nickel from pipes and containers. Scattered studies indicate a highly variable dietary intake of nickel, but most averages are about 200-300 micrograms/day. In addition, skin contact to a multitude of metal objects may be of significance to the large number of individuals suffering from contact dermatitis and nickel allergy. Finally, nickel alloys are often used in nails and prostheses for orthopaedic surgery, and various sources may contaminate intravenous fluids. Thus, human nickel exposure originates from a variety of sources and is highly variable. Occupational nickel exposure is of major significance, and leaching of nickel may add to dietary intakes and to cutaneous exposures. 79 references.

  8. High temperature dissolution of chromium substituted nickel ferrite in nitrilotriacetic acid medium

    Energy Technology Data Exchange (ETDEWEB)

    Sathyaseelan, V.S.; Chandramohan, P.; Velmurugan, S., E-mail: svelu@igcar.gov.in

    2016-12-01

    High temperature (HT) dissolution of chromium substituted nickel ferrite was carried out with relevance to the decontamination of nuclear reactors by way of chemical dissolution of contaminated corrosion product oxides present on stainless steel coolant circuit surfaces. Chromium substituted nickel ferrites of composition, NiFe{sub (2−x)}Cr{sub x}O{sub 4} (x ≤ 1), was synthetically prepared and characterized. HT dissolution of these oxides was carried out in nitrilotriacetic acid medium at 160 °C. Dissolution was remarkably increased at 160 °C when compared to at 85 °C in a reducing decontamination formulation. Complete dissolution could be achieved for the oxides with chromium content 0 and 0.2. Increasing the chromium content brought about a marked reduction in the dissolution rate. About 40 fold decrease in rate of dissolution was observed when chromium was increased from 0 to 1. The rate of dissolution was not very significantly reduced in the presence of N{sub 2}H{sub 4}. Dissolution of oxide was found to be stoichiometric. - Highlights: • Dissolution of NiFe{sub (2−x)}Cr{sub x}O{sub 4} was remarkably increased at 160 °C in NTA medium. • The dissolution was significantly decreasing with the increase in Cr content in the oxide. • Dissolution rate is dependent on the lability of metal-oxo bonds. • The rate of dissolution was not significantly reduced in the presence of N{sub 2}H{sub 4.} • NTA at high temperature is effective for decontamination of stainless steel surfaces.

  9. Brucella abortus ure2 region contains an acid-activated urea transporter and a nickel transport system

    Directory of Open Access Journals (Sweden)

    García-Lobo Juan M

    2010-04-01

    Full Text Available Abstract Background Urease is a virulence factor that plays a role in the resistance of Brucella to low pH conditions, both in vivo and in vitro. Brucella contains two separate urease gene clusters, ure1 and ure2. Although only ure1 codes for an active urease, ure2 is also transcribed, but its contribution to Brucella biology is unknown. Results Re-examination of the ure2 locus showed that the operon includes five genes downstream of ureABCEFGDT that are orthologs to a nikKMLQO cluster encoding an ECF-type transport system for nickel. ureT and nikO mutants were constructed and analyzed for urease activity and acid resistance. A non-polar ureT mutant was unaffected in urease activity at neutral pH but showed a significantly decreased activity at acidic pH. It also showed a decreased survival rate to pH 2 at low concentration of urea when compared to the wild type. The nikO mutant had decreased urease activity and acid resistance at all urea concentrations tested, and this phenotype could be reverted by the addition of nickel to the growth medium. Conclusions Based on these results, we concluded that the operon ure2 codes for an acid-activated urea transporter and a nickel transporter necessary for the maximal activity of the urease whose structural subunits are encoded exclusively by the genes in the ure1 operon.

  10. Dissolution of nickel ferrite and rare earths containing magnetites in citric acid - EDTA - gallic acid (CEG) formulation

    International Nuclear Information System (INIS)

    Kumbhar, A.G.; Kishore, K.; Venkateswaran, G.; Balaji, V.

    2002-01-01

    It has been shown by us earlier that gallic acid can be used as a reductant in dilute chemical decontaminant formulations containing EDTA as chelant. The results on the dissolution of magnetite in such a formulation were quite promising. Moreover, the superior radiation stability of gallic acid vis-a-vis other reductants such as ascorbic acid or oxalic acid is another plus point for this formulation. Besides having an inherent stability against radiation degradation, it is able to protect even EDTA against radiation induced decomposition to a great extent unlike the case of ascorbic acid. In an extension of that work, dissolution experiments have now been carried out on nickel ferrite and magnetites containing rare earths like La, Ce and Zr This is to simulate the presence of fission product oxides in magnetite resulting from a possible phase of operation with leaky fuel. The rate constants have been determined using the inverse cubic rate law. In the case of nickel ferrite, although there is an initial induction period, the rate constants for the dissolution were determined to be at 1.6 x 10 -2 and 3.6 x 10 -3 min -1 at 353 K and 333 K respectively. Presence of Ce in particular either alone or in combination with Zr/La at a level of 1 at.% equivalent each in magnetite is seen to increase the surface area of the oxide. The rate constants for the dissolution at 353 K in a 11:44:4 mM CEG formulation taken with magnetite and rare earth containing magnetites equivalent to yielding 22 mM Fe upon complete dissolution are as follows: 5.09 x 10 -2 min -1 (magnetite), 7.06 x 10 -2 min -1 (Ce 2 O 3 containing magnetite), 6.33 x 10 -2 min -1 (Ce 2 O 3 , ZrO 2 containing magnetite), 1 x 10 -1 min -1 (Ce 2 O 3 , ZrO 2 , La 2 O 3 containing magnetite). The presence of Ce, Zr and La at 1 at.% level each has not resulted in any turbidity in solution at the end of magnetite dissolution suggesting chemical dissolution of these rare earth oxides in the formulation. Simple magnetite

  11. Dissolution of nickel ferrite and rare earths containing magnetites in citric acid - EDTA - gallic acid (CEG) formulation

    Energy Technology Data Exchange (ETDEWEB)

    Kumbhar, A.G.; Kishore, K.; Venkateswaran, G.; Balaji, V. [Applied Chemistry Div., Bhabha Atomic Research Centre, Mumbai (India)

    2002-07-01

    It has been shown by us earlier that gallic acid can be used as a reductant in dilute chemical decontaminant formulations containing EDTA as chelant. The results on the dissolution of magnetite in such a formulation were quite promising. Moreover, the superior radiation stability of gallic acid vis-a-vis other reductants such as ascorbic acid or oxalic acid is another plus point for this formulation. Besides having an inherent stability against radiation degradation, it is able to protect even EDTA against radiation induced decomposition to a great extent unlike the case of ascorbic acid. In an extension of that work, dissolution experiments have now been carried out on nickel ferrite and magnetites containing rare earths like La, Ce and Zr This is to simulate the presence of fission product oxides in magnetite resulting from a possible phase of operation with leaky fuel. The rate constants have been determined using the inverse cubic rate law. In the case of nickel ferrite, although there is an initial induction period, the rate constants for the dissolution were determined to be at 1.6 x 10{sup -2} and 3.6 x 10{sup -3} min{sup -1} at 353 K and 333 K respectively. Presence of Ce in particular either alone or in combination with Zr/La at a level of 1 at.% equivalent each in magnetite is seen to increase the surface area of the oxide. The rate constants for the dissolution at 353 K in a 11:44:4 mM CEG formulation taken with magnetite and rare earth containing magnetites equivalent to yielding 22 mM Fe upon complete dissolution are as follows: 5.09 x 10{sup -2} min{sup -1} (magnetite), 7.06 x 10{sup -2} min{sup -1} (Ce{sub 2}O{sub 3} containing magnetite), 6.33 x 10{sup -2} min{sup -1} (Ce{sub 2}O{sub 3}, ZrO{sub 2} containing magnetite), 1 x 10{sup -1} min{sup -1} (Ce{sub 2}O{sub 3}, ZrO{sub 2}, La{sub 2}O{sub 3} containing magnetite). The presence of Ce, Zr and La at 1 at.% level each has not resulted in any turbidity in solution at the end of magnetite dissolution

  12. Performance of Cement Containing Laterite as Supplementary Cementing Material

    Directory of Open Access Journals (Sweden)

    Abbas Bukhari, Z. S.

    2013-03-01

    Full Text Available The utilization of different industrial waste, by-products or other materials such as ground granulated blast furnace slag, silica fume, fly ash, limestone, and kiln dust, etc. as supplemen- tary cementing materials has received considerable attention in recent years. A study has been conducted to look into the performance of laterite as Supplementary Cementing Materials (SCM. The study focuses on compressive strength performance of blended cement containing different percentage of laterite. The cement is replaced accordingly with percentage of 2 %, 5 %, 7 % and 10 % by weight. In addition, the effect of use of three chemically different laterites have been studied on physical performance of cement as in setting time, Le-Chatlier expansion, loss on ignition, insoluble residue, free lime and specifically compressive strength of cement cubes tested at the age of 3, 7, and 28 days. The results show that the strength of cement blended with laterite as SCM is enhanced. Key words: Portland cement, supplementary cementing materials (SCM, laterite, compressive strength KUI – 6/2013 Received January 4, 2012 Accepted February 11, 2013

  13. Interfacial reactions between humic-like substances and lateritic clay: application to the preparation of "geomimetic" materials.

    Science.gov (United States)

    Goure-Doubi, Herve; Martias, Céline; Lecomte-Nana, Gisèle Laure; Nait-Ali, Benoît; Smith, Agnès; Thune, Elsa; Villandier, Nicolas; Gloaguen, Vincent; Soubrand, Marilyne; Konan, Léon koffi

    2014-11-15

    The aim of this study was to understand the mechanisms responsible for the strengthening of "geomimetic" materials, especially the chemical bonding between clay and humic substances. The mineral matter is lateritic clay which mainly consists in kaolinite, goethite, hematite and quartz. The other starting products are fulvic acid (FA) and lime. The preparation of these geomimetic materials is inspired from the natural stabilization of soils by humic substances occurring over thousands of years. The present process involves acidic and alkaline reactions followed by a curing period of 18days at 60°C under a water saturated atmosphere. The acceleration of the strengthening process usually observed in soils makes this an original process for treatment of soils. The consolidation of the "geomimetic" materials could result from two major phenomena: (i) chemical bonding at the interface between the clay particles and iron compounds and the functional groups of the fulvic acid, (ii) a partial dissolution of the clay grains followed by the precipitation of the cementitious phases, namely calcium silicate hydrates, calcium aluminate hydrates and mixed calcium silicum and aluminum hydrates. Indeed, the decrease of the BET specific area of the lateritic clay after 24 h of reaction with FA added to the structural reorganization observed between 900 and 1000°C in the "geomimetic" material, and to the results of adsorption measurements, confirm the formation of organo-ferric complexes. The presence of iron oxides in clay, in the form of goethite, appears to be another parameter in favor of a ligand exchange process and the creation of binding bridges between FA and the mineral matter. Indeed all faces of goethite are likely to be involved in complexation reactions whereas in lateritic clay only lateral faces could be involved. The results of the adsorption experiments realized at a local scale will improve our understandings about the process of adsorption of FA on lateritic

  14. Direct formation of reduced graphene oxide and 3D lightweight nickel network composite foam by hydrohalic acids and its application for high-performance supercapacitors.

    Science.gov (United States)

    Huang, Haifu; Tang, Yanmei; Xu, Lianqiang; Tang, Shaolong; Du, Youwei

    2014-07-09

    Here, a novel graphene composite foam with 3D lightweight continuous and interconnected nickel network was successfully synthesized by hydroiodic (HI) acid using nickel foam as substrate template. The graphene had closely coated on the backbone of the 3D nickel conductive network to form nickel network supported composite foam without any polymeric binder during the HI reduction of GO process, and the nickel conductive network can be maintained even in only a small amount of nickel with 1.1 mg/cm(2) and had replaced the traditional current collector nickel foam (35 mg/cm(2)). In the electrochemical measurement, a supercapacitor device based on the 3D nickel network and graphene composite foam exhibited high rate capability of 100 F/g at 0.5 A/g and 86.7 F/g at 62.5 A/g, good cycle stability with capacitance retention of 95% after 2000 cycles, low internal resistance (1.68 Ω), and excellent flexible properties. Furthermore, the gravimetric capacitance (calculated using the total mass of the electrode) was high up to 40.9 F/g. Our work not only demonstrates high-quality graphene/nickel composite foam, but also provides a universal route for the rational design of high performance of supercapacitors.

  15. Mathematical models to predict rheological parameters of lateritic hydromixtures

    Directory of Open Access Journals (Sweden)

    Gabriel Hernández-Ramírez

    2017-10-01

    Full Text Available The present work had as objective to establish mathematical models that allow the prognosis of the rheological parameters of the lateritic pulp at concentrations of solids from 35% to 48%, temperature of the preheated hydromixture superior to 82 ° C and number of mineral between 3 and 16. Four samples of lateritic pulp were used in the study at different process locations. The results allowed defining that the plastic properties of the lateritic pulp in the conditions of this study conform to the Herschel-Bulkley model for real plastics. In addition, they show that for current operating conditions, even for new situations, UPD mathematical models have a greater ability to predict rheological parameters than least squares mathematical models.

  16. Transpassive dissolution of alloy 625, chromium, nickel, and molybdenum in high-temperature solutions containing hydrochloric acid and oxygen

    International Nuclear Information System (INIS)

    Kritzer, P.; Boukis, N.; Dinjus, E.

    2000-01-01

    Coupons of nickel, molybdenum, chromium, and the nickel-based Alloy 625 (UNS 06625) were corroded in strongly oxidizing hydrochloric acid (HCl) solutions at 350 C and a pressure (p) of 24 MPa, with reaction times between 0.75 h and 50 h. For Alloy 625, the effect of surface roughness also was investigated. Nickel and molybdenum showed strong material loss after only 5 h of reaction as a result of the instability of the solid oxides formed under experimental conditions. The attack on chromium started at the grain boundaries. At longer reaction times, thick, spalling oxide layers formed on the surface. The attack on Alloy 625 also started at the grain boundaries and at inclusions leading to the formation of small pits. On polished surfaces, the growth of these pits occurred faster than on nonpolished surfaces, but fewer pits grew. Corrosion products formed at the surface consisted of oxygen and chromium. On isolated spots, nickel- and chlorine-containing products also were found

  17. Ethylenediamine disuccinic acid enhanced phytoextraction of nickel from contaminated soils using Coronopus didymus (L.) Sm.

    Science.gov (United States)

    Sidhu, Gagan Preet Singh; Bali, Aditi Shreeya; Singh, Harminder Pal; Batish, Daizy R; Kohli, Ravinder Kumar

    2018-04-18

    In a screenhouse, the applicability of biodegradable chelant ethylenediamine disuccinic acid (EDDS) to enhance Ni-phytoextraction by Coronopus didymus was tested for the first time. This study assayed the hypothesis based upon the role of EDDS on physiological and biochemical alterations and ameliorating phytoextraction capacity of C. didymus under nickel (Ni) stress. Pot experiments were conducted for 6 weeks and C. didymus plants were cultivated in soil artificially contaminated with 30, 50, and 70 mg kg -1 Ni treatments. Soil was amended with EDDS (2 mmol kg -1 ). Plants were harvested, 1 week after EDDS application. At 70 mg kg -1 Ni level, EDDS application dramatically enhanced the root and shoot Ni concentration from 665 and 644 to 1339 and 1338 mg kg -1 , respectively. Combination of Ni + EDDS induced alterations in biochemical parameters of plants. EDDS addition posed pessimistic effects on growth, biomass, photosynthetic activity and protein content of the plants. Besides, application of EDDS stimulated the generation of superoxide anion, H 2 O 2 content and MDA level. However, EDDS assisted mount in antioxidant activities (superoxide dismutase, catalase and glutathione peroxidase) considerably neutralised the toxicity induced by reactive oxygen species in plant tissues. The results revealed EDDS efficacy to ameliorate the performance of antioxidant enzymes and improved Ni translocation in plant tissues, thus strongly marked its affinity to be used together with C. didymus for Ni-phytoextraction. Copyright © 2018 Elsevier Ltd. All rights reserved.

  18. Nickel Dermatitis - Nickel Excretion

    DEFF Research Database (Denmark)

    Menné, T.; Thorboe, A.

    1976-01-01

    Nickel excretion in urine in four females -sensitive to nickel with an intermittent dyshidrotic eruption was measured with flameless atomic absorption. Excretion of nickel was found to be increased in association with outbreaks of vesicles. The results support the idea that the chronic condition ...

  19. SAND-LATERITE MIXTURES FOR ROAD CONSTRUCTION (A ...

    African Journals Online (AJOL)

    Dr Obe

    costs in the construction of roads carrying medium density traffic and in the ... East Asia (1) but for reasons given later, their results ... that laterites are good materials for road and air-field ... countries like South Africa, this method of soil-.

  20. Multivariate erosion risk assessment of lateritic badlands of Birbhum

    Indian Academy of Sciences (India)

    Each geomorphic hazard involves a degree of risk which incorporates quantification of the probability that a hazard will be harmful. At present, the categorization of sub-watersheds into erosion risk is considered as the fundamental step to conserve the soil loss. Development of badlands over the laterites of Birbhum district ...

  1. Mineralogical and geochemical trends in lateritic weathering profiles ...

    African Journals Online (AJOL)

    The absence of bauxite minerals like gibbsite and diaspora in the profiles shows that the trend of weathering is towards iron enrichment (ferralitization) and not aluminum accumulation (bauxitization). The CIA values of the lateritic layers shows that the weathering process is matured and has reached advanced stage.

  2. effect of compactive effort on strength indices of laterite treated

    African Journals Online (AJOL)

    PROF. BARTH EKWEME

    Atterberg's limits test, compaction test, California bearing ratio (CBR) and unconfined ... size, highclay content, and the degree to which the soils have been ... in the stabilization of Ikpayongo laterite with cement. However lime which seems to be the conventional ... as soil modification or stabilization, depending on treatment ...

  3. estimation of shear strength parameters of lateritic soils using

    African Journals Online (AJOL)

    user

    ... a tool to estimate the. Nigerian Journal of Technology (NIJOTECH). Vol. ... modeling tools for the prediction of shear strength parameters for lateritic ... 2.2 Geotechnical Analysis of the Soils ... The back propagation learning algorithm is the most popular and ..... [10] Alsaleh, M. I., Numerical modeling for strain localization in ...

  4. Improvement of strength characteristics of lateritic sub-grade soil ...

    African Journals Online (AJOL)

    Journal of Applied Sciences and Environmental Management ... Abstract. This paper presents the results of investigation of the behavior of pavement subgrade soil stabilized with shredded polyethylene waste. ... Keywords: Lateritic soil, High density polyethylene (HDPE) waste, Pavement thickness, Sub-grade soil ...

  5. stabilization of ikpayongo laterite with cement and calcium carbide

    African Journals Online (AJOL)

    PROF EKWUEME

    the stabilization of soil will ensure economy in road construction, while providing an effective way of disposing calcium carbide waste. KEYWORDS: Cement, Calcium carbide waste, Stabilization, Ikpayongo laterite, Pavement material. INTRODUCTION. Road building in the developing nations has been a major challenge to ...

  6. Preparation and characterization of alumina supported nickel-oxalate catalyst for the hydrodeoxygenation of oleic acid into normal and iso-octadecane biofuel

    International Nuclear Information System (INIS)

    Ayodele, O.B.; Togunwa, Olayinka S.; Abbas, Hazzim F.; Daud, Wan Mohd Ashri Wan

    2014-01-01

    Highlights: • Preparation of nickel oxalate complex as catalyst precursor. • Incorporation of nickel oxalate complex into alumina support. • Characterization of the alumina supported nickel oxalate catalyst. • Hydrodeoxygenation of oleic acid with nickel oxalate catalyst. • Nickel oxalate catalyst reusability studies. - Abstract: In this study, nickel II oxalate complex (NiOx) was prepared by functionalization of nickel with oxalic acid (OxA) and incorporated into Al 2 O 3 to synthesize alumina supported nickel oxalate (NiOx/Al 2 O 3 ) catalyst for the hydrodeoxygenation (HDO) of oleic acid (OA) into biofuel. The synthesized NiOx/Al 2 O 3 was characterized and the X-ray fluorescence and elemental dispersive X-ray results showed that NiOx was successfully incorporated into the structure of Al 2 O 3 . The X-ray diffraction and Raman spectroscopy results confirmed that highly dispersed Ni species are present in the NiOx/Al 2 O 3 due to the functionalization with OxA. The catalytic activity of the NiOx/Al 2 O 3 on the HDO of OA produced a mixture of 21% iso-C18 and 72% n-C18 at a 360 °C, 20 bar, 30 mg NiOx/Al 2 O 3 loading pressure and gas flow rate of 100 mL/min. The presence of i-C 18 was ascribed to the OxA functionalization which increased the acidity of NiOx/Al 2 O 3 . The NiOx/Al 2 O 3 reusability study showed consistent HDO ability after 5 runs. These results are promising for further research into biofuel production for commercialization

  7. Assessing the 2D Models of Geo-technological Variables in a Block of a Cuban Laterite Ore Body. Part IV Local Polynomial Method

    Directory of Open Access Journals (Sweden)

    Arístides Alejandro Legrá-Lobaina

    2016-10-01

    Full Text Available The local polynomial method is based on assuming that is possible to estimate the value of a U variable in any of the P coordinate through local polynomials estimated based on approximate data. This investigation analyzes the probability of modeling in two dimensions the thickness and nickel, iron and cobalt concentrations in a block of Cuban laterite ores by using the mentioned method. It was also analyzed if the results of modeling these variables depend on the estimation method that is used.

  8. Influence of Bath Composition at Acidic pH on Electrodeposition of Nickel-Layered Silicate Nanocomposites for Corrosion Protection

    Directory of Open Access Journals (Sweden)

    Jeerapan Tientong

    2013-01-01

    Full Text Available Nickel-layered silicates were electrochemically deposited from acidic bath solutions. Citrate was used as a ligand to stabilize nickel (II ions in the plating solution. The silicate, montmorillonite, was exfoliated by stirring in aqueous solution over 24 hours. The plating solutions were analyzed for zeta-potential, particle size, viscosity, and conductivity to investigate the effects of the composition at various pHs. The solution particles at pH 2.5 (−22.2 mV and pH 3.0 (−21.9 mV were more stable than at pH 1.6 (−10.1 mV as shown by zeta-potential analysis of the nickel-citrate-montmorillonite plating solution. Ecorr for the films ranged from −0.32 to −0.39 V with varying pH from 1.6 to 3.0. The films were immersed in 3.5% NaCl and the open circuit potential monitored for one month. The coatings deposited at pH 3.0 were stable 13 days longer in the salt solution than the other coatings. X-ray diffraction showed a change in the (111/(200 ratio for the coatings at the various pHs. The scanning electron microscopy and hardness results also support that the electrodeposition of nickel-montmorillonite at pH 3.0 (234 GPa had improved hardness and morphology compared to pH 2.5 (174 GPa and pH 1.6 (147 GPa.

  9. Synthesis of Nickel (Ni) Doped HKUST-1 Using Solvotermal Method with Addition of Acetic Acid as Modulator

    OpenAIRE

    Safii, Farhan Fikri; Ediati, Ratna

    2015-01-01

    Hong Kong University of Science and Technology-1 (HKUST-1) is metal organic framework (MOF) that composed from ligand BTC (1,3,5-benzene tricarboxylic) and copper ions. The method used in this study is solvotermal with variations nickel ion doping and additions acetic acid as modulator. The purpose of this study is to increase the hydrogen storage capacity. The results obtained were characterized by XRD showed that the HKUST-1 and Ni-HKUST-1 has formed, showed by peaks at 2 theta = 6.7, 9.5, ...

  10. A glassy carbon electrode modified with a nickel(II) norcorrole complex and carbon nanotubes for simultaneous or individual determination of ascorbic acid, dopamine, and uric acid

    International Nuclear Information System (INIS)

    Deng, Keqin; Li, Xiaofang; Huang, Haowen

    2016-01-01

    The authors report on the synthesis of a hybrid material consisting of the porphyrinoid metal complex nickel(II) norcorrole that was noncovalently bound to carbon nanotubes (CNT-NiNC). The hybrid was characterized by UV–vis, FTIR spectroscopy, and thermogravimetric analysis. The CNT-NiNC hybrid possesses high catalytic activity and selectivity toward the oxidation of ascorbic acid, dopamine, and uric acid. It was used to modify a glassy carbon electrode which then is shown to enable simultaneous or individual determination of ascorbic acid (AA), dopamine (DA), and uric acid (UA) at pH 6.5 and typical working potentials of −70, 200 and 380 mV (vs. SCE). The detection limits (at an SNR of 3) are 2.0 μM for AA, 0.1 μM for DA, and 0.4 μM for UA. (author)

  11. Nickel recovery from electric arc furnace slag by magnetic separation

    Directory of Open Access Journals (Sweden)

    Sakaroglou Marianna

    2017-01-01

    Full Text Available During the pyrometallurgical treatment of the nickel-bearing laterite in the plant of G.M.M. S.A. LARCO, slag is produced after treatment in electric-arc furnace (EAF that contains 0.10 to 0.20 % Ni. Taking into account the great quantity of slag produced per year, the recovery of nickel from the EAF slag will add benefits to the entire process. The target of the current work is to investigate the possibility of nickel recovery from EAF slag by magnetic separation. To meet the target, the effect of the following parameters was studied: grain size, magnetic field intensity, thickness of slag layer, moisture content, and re-grinding of the coarser slag particles. The results show that it is possible to obtain a magnetic product with nickel grade close to that of the primary raw material or even better, with sufficient nickel recovery.

  12. Effects of corn cob ash on lime stabilized lateritic soil

    Science.gov (United States)

    Nnochiri, Emeka Segun

    2018-03-01

    This study assesses the effects of Corn Cob Ash (CCA) on lime-stabilized lateritic soil. Preliminary tests were carried out on the natural soil sample for purpose of identification and classification. Lime being the main stabilizing material was thoroughly mixed with the soil sample to determine the optimum lime requirement of the sample as a basis for evaluating the effects of the CCA. The optimum lime requirement was 10%. The CCA was thereafter added to the lime stabilized soil in varying proportions of 2, 4, 6, 8 and 10%. Unsoaked CBR increased from 83% at 0% CCA to highest value of 94% at 4% CCA. Unconfined Compressive Strength (UCS) values increased from 1123kN/m2 at 0% CCA to highest value of 1180kN/m2 at 4% CCA. It was therefore concluded that CCA can serve as a good complement for lime stabilization in lateritic soil.

  13. Effect of Rice Husk Ash on Cement Stabilized Laterite

    Directory of Open Access Journals (Sweden)

    Musa ALHASSAN

    2007-09-01

    Full Text Available Laterite soil collected from Maikunkele area of Minna, classified as an A-7-6 on AASHTO classification, was stabilized with 2-8% cement by weight of the dry soil. Using British Standard Light (BSL compaction energy, the effect of Rice Husk Ash (RHA on the soil was investigated with respect to compaction characteristics, California Bearing Ratio (CBR and Unconfined Compressive Strength (UCS tests. Results obtained, indicate a general decrease in Maximum Dry Density (MDD and increase in Optimum Moisture Content (OMC, all with increase in RHA Content (2-8% at specified cement contents. There was also a tremendous improvement in the CBR and UCS with increase in the RHA content at specified cement contents to their peak values at between 4-6% RHA. The UCS values also improved with curing age. This indicates the potentials of using 4-6% RHA admixed with less cement contents for laterite soil stabilization.

  14. Lateritinga project: a geochemical orientation study for Amazon lateritic

    International Nuclear Information System (INIS)

    Costa, M.L. da

    1990-01-01

    The aim of this project is the development of systematic geochemical orientation survey in lateritic weathered terrain, like those form Amazon Region. The main selected targets (sheets) are: Turiacu, Cajuapara and Serra dos Carajas, with 690 samples collected (soils and lateritic rocks). For the Aurizona-Serra do Pirocaua target (Turiacu sheet), within the purpose of this work, 49 samples were collected in a 100x 200m regular grid. From all samples the fraction minor than 200 mesh was taken to analyses (by XRF, AA, OES, ICP and fire assay) for SiO sub(2), Fe sub(2) O sub(3), TiO sub(2), P sub(2) O sub(5), Sr, Ba, Y, Nb, Zr, Ga, Sc, Ni, Co, Cr, Cu, Mn, V, As, Bi, Pt, Pd, Th, Au and REE, as well for their mineralogy by XRD. The chemical results were submitted to statistical treatment with the Geoquant-software for IBM-compatible microcomputer. (author)

  15. Perilaku Kuat Tekan Tanah Laterit dengan Stabilisasi Kapur dan Semen

    OpenAIRE

    febriani, fitri

    2017-01-01

    Laterite soil is a soil that looks like rust color because it contains high iron oxidation. This is not good for infrastructure development, so it needs an innovation as a method of land improvement, that is stabilization. The reinforcement of soil is generally used in a construction to increase the bearing capacity, so it can hold the construction load. The method that frequently used is soil stabilization by the addition of limestone and cement. In this research, the stabilization of clay i...

  16. Effect of Rice Husk Ash on Cement Stabilized Laterite

    OpenAIRE

    Musa ALHASSAN; Alhaji Mohammed MUSTAPHA

    2007-01-01

    Laterite soil collected from Maikunkele area of Minna, classified as an A-7-6 on AASHTO classification, was stabilized with 2-8% cement by weight of the dry soil. Using British Standard Light (BSL) compaction energy, the effect of Rice Husk Ash (RHA) on the soil was investigated with respect to compaction characteristics, California Bearing Ratio (CBR) and Unconfined Compressive Strength (UCS) tests. Results obtained, indicate a general decrease in Maximum Dry Density (MDD) and increase in Op...

  17. Modeling of heat and mass transfer in lateritic building envelopes

    International Nuclear Information System (INIS)

    Meukam, Pierre

    2004-10-01

    The aim of the present work is to investigate the behavior of building envelopes made of local lateritic soil bricks subjected to different climatic conditions. The analysis is developed for the prediction of the temperature, relative humidity and water content behavior within the walls. The building envelopes studied in this work consist of lateritic soil bricks with incorporation of natural pozzolan or sawdust in order to obtain small thermal conductivity and low-density materials, and limit the heat transfer between the atmospheric climate and the inside environment. In order to describe coupled heat and moisture transfer in wet porous materials, the coupled equations were solved by the introduction of diffusion coefficients. A numerical model HMtrans, developed for prediction of beat and moisture transfer in multi-layered building components, was used to simulate the temperature, water content and relative humidity profiles within the building envelopes. The results allow the prediction of the duration of the exposed building walls to the local weather conditions. They show that for any of three climatic conditions considered, relative humidity and water content do not exceed 87% and 5% respectively. There is therefore minimum possibility of water condensation in the materials studied. The durability of building envelopes made of lateritic soil bricks with incorporation of natural pozzolan or sawdust is not strongly affected by the climatic conditions in tropical and equatorial regions. (author)

  18. Understanding the residence of Co in ore minerals - towards the development of novel Co extraction strategies for laterite deposits

    Science.gov (United States)

    Dybowska, Agnieszka; Norman, Rachel; Schofield, Paul; Herrington, Richard

    2017-04-01

    Cobalt has unique properties highly valued for many applications essential to the green economy. It has been classified as a critical raw material due to the particularly high risk of supply shortage and its importance for the value chain. Despite low crustal abundance (25ppm), Co is concentrated by various geological processes to concentrations suitable for mining, however the majority of Co is recovered as a by-product of Cu and Ni processing in three principal geological settings: hydrothermal, magmatic and lateritic. Cobalt-rich laterites, which provide 20% of the world's Co, are mainly processed using energy-inefficient pyrometallurgical techniques or high-pressure acid leaching technologies often optimised for extraction of other elements, which can leave between 50 and 80% of the Co unrecovered. In order to develop more efficient Co extraction strategies, understanding the residence of Co in ore minerals is essential. To this end, we are undertaking a detailed mineralogical, chemical and atomistic-scale characterization of Co in samples from a range of laterite deposits. Bulk samples representative of the average ore material were sourced from a variety of undeveloped laterite deposits: Shevchenko (Kazakhstan), Acoje (Philippines), Nkamouna (Cameroon) and Piauí (Brazil). Bulk chemical and mineralogical characterisation was undertaken with ICP-OES/MS and XRD, followed by spatially resolved chemical and mineralogical imaging at the micron scale using µXRD, EPMA, SEM and synchrotron-based µXRF. The chemical state and local environment of Co were determined using X ray spectroscopy (μXANES and μEXAFS). The total concentrations of Co ranged from 630 to 2780 mg/kg. The ore mineral assemblage in the various samples includes goethite, maghemite, hematite, quartz, talc, serpentines, chlorites, smectites, kaolinite and chromites. Manganese oxide minerals are present but, due to their poor crystallinity and low concentration, are not routinely detectable with bulk

  19. Effects of some factors on electro-osmotic dewatering of Laterite ...

    African Journals Online (AJOL)

    ... effect on the EO process. The general effects were same for the two soil samples, but the rate of the effect varied, which implied that EO dewatering was site dependent. It was concluded that EO dewatering was a viable option for dewatering of tropical laterite. Keywords: Electro-osmosis, Soil Dewatering, Tropical Laterite, ...

  20. The High Deccan duricrusts of India and their significance for the `laterite' issue

    Science.gov (United States)

    Ollier, Cliff D.; Sheth, Hetu C.

    2008-10-01

    In the Deccan region of western India ferricrete duricrusts, usually described as laterites, cap some basalt summits east of the Western Ghats escarpment, basalts of the low-lying Konkan Plain to its west, as well as some sizeable isolated basalt plateaus rising from the Plain. The duricrusts are iron-cemented saprolite with vermiform hollows, but apart from that have little in common with the common descriptions of laterite. The classical laterite profile is not present. In particular there are no pisolitic concretions, no or minimal development of concretionary crust, and the pallid zone, commonly assumed to be typical of laterites, is absent. A relatively thin, non-indurated saprolite usually lies between the duricrust and fresh basalt. The duricrust resembles the classical laterite of Angadippuram in Kerala (southwestern India), but is much harder. The High Deccan duricrusts capping the basalt summits in the Western Ghats have been interpreted as residuals from a continuous (but now largely destroyed) laterite blanket that represents in situ transformation of the uppermost lavas, and thereby as marking the original top of the lava pile. But the unusual pattern of the duricrusts on the map and other evidence suggest instead that the duricrusts formed along a palaeoriver system, and are now in inverted relief. The two interpretations lead to different tectonic histories. Duricrust formation involved lateral material input besides vertical elemental exchange. We may have reached the stage when the very concepts of laterite and lateritization are hindering progress in regolith research.

  1. An Investigation Into The Effect Of Mixtures Of Lateritic-Cement And ...

    African Journals Online (AJOL)

    The behaviour of the laterite-cement, shale, and limedust when mixed in proportions to mould bricks under natural conditions and the improvement of structural properties of laterite for wider and more economical usage as construction material were investigated. Shale was found to be a very poor soil stabilizer because it ...

  2. Microhyla laterite sp. nov., A New Species of Microhyla Tschudi, 1838 (Amphibia: Anura: Microhylidae from a Laterite Rock Formation in South West India.

    Directory of Open Access Journals (Sweden)

    K S Seshadri

    Full Text Available In recent times, several new species of amphibians have been described from India. Many of these discoveries are from biodiversity hotspots or from within protected areas. We undertook amphibian surveys in human dominated landscapes outside of protected areas in south western region of India between years 2013-2015. We encountered a new species of Microhyla which is described here as Microhyla laterite sp. nov. It was delimited using molecular, morphometric and bioacoustics comparisons. Microhyla laterite sp. nov. appears to be restricted to areas of the West coast of India dominated by laterite rock formations. The laterite rock formations date as far back as the Cretaceous-Tertiary boundary and are considered to be wastelands in-spite of their intriguing geological history. We identify knowledge gaps in our understanding of the genus Microhyla from the Indian subcontinent and suggest ways to bridge them.

  3. 1 Molar concentration hydrofluoric acid effect at 400 C in the corrosion resistance of alloys containing nickel

    International Nuclear Information System (INIS)

    Contreras P, H.

    1992-01-01

    Corrosion rate for pure nickel, Inconel 600 and Monel alloys in a 1 Molar hydrofluoric acid solution at a 40 0 C temperature were determined. For contrasting purposes both SAE 304 SS and SAE 316 SS were included. As expected these Stainless Steels do not show good corrosion performance in the solution used. Several expressions correlating the weight and thickness loss v/s time were obtained. In the particular case of Monel, up to 2.021 hours, two expressions for the weight loss and three expressions for the thickness loss were obtained with a close to 1,0 correlation coefficient value. The Monel showed the best overall corrosion performance among the tested alloys. (author)

  4. Uranium laterite from Ipora/Amorinopolis region- Goias, Brazil

    International Nuclear Information System (INIS)

    Fernandes, S.M.

    1983-01-01

    The present study gives an account of the uranium bearing laterite in the district of Amorinopolis, GO. Emphasis is given in the study of its mineralogy and of the mineralization controls. The uranium mineralization is chiefly found within the arkosic sandstones at the base of the Devonian Ponta Grossa Formation. The ore is tabular and concordant with the bedding, the controls being simultaneously litho-stratigraphic and biochemical. Narrow permeable horizons of arkosic sandstone lie between impermeable shale an siltstone layers. Within the permeable horizon fossil remains (probably brachiopods) are replaced by uranium minerals. The oxidized iron minerals may have acted to insulate and preserve the secondary soluble uranium minerals. (author)

  5. Fluoride adsorption onto an acid treated lateritic mineral from Kenya ...

    African Journals Online (AJOL)

    Wambu

    adsorption on commercial activated carbons and alumina. (Chaturvedi et al., 1990), ion-exchange ... chemical composition showed that the adsorbent had a ..... fixed bed packed with granular calcite Water Res., 33: 3395–3402. Onyango MS ...

  6. Toxicity of nickel and silver to Nostoc muscorum: interaction with ascorbic acid, glutathione, and sulfur-containing amino acids.

    Science.gov (United States)

    Rai, L C; Raizada, M

    1987-08-01

    Exposure of Nostoc muscorum to different concentrations of Ni and Ag brought about reduction in growth, carbon fixation, heterocyst production, and nitrogenase activity and increase in the loss of ions (K+, Na+). In an attempt to ameliorate the toxicity of test metals by ascorbic acid, glutathione, and sulfur-containing amino acids (L-cysteine and L-methionine), it was found that the level of protection by ascorbic acid and glutathione was more for Ag than Ni. However, metal-induced inhibition of growth and carbon fixation was equally ameliorated by methionine. But the level of protection by cysteine was quite different, i.e., 27% for Ni and 22% for Ag. Protection of metal toxicity in N. muscorum by amino acids lends further support to self-detoxifying ability of cyanobacteria because they are known to synthesize all essential amino acids.

  7. Nickel and its alloys as perspective materials for intermediate temperature steam electrolysers operating on proton conducting solid acids as electrolyte

    DEFF Research Database (Denmark)

    Nikiforov, Aleksey; Petrushina, Irina; Jensen, Jens Oluf

    2012-01-01

    Several stainless steels, nickel-based alloys, Ta-coated stainless steel, niobium, nickel, platinum and gold were evaluated as possible materials for use in the intermediate temperature water electrolysers. The corrosion resistance was measured in molten KH2PO4 as simulated conditions corresponding...

  8. Dual Mode Fluorophore-Doped Nickel Nitrilotriacetic Acid-Modified Silica Nanoparticles Combine Histidine-Tagged Protein Purification with Site-Specific Fluorophore Labeling

    OpenAIRE

    Kim, Sung Hoon; Jeyakumar, M.; Katzenellenbogen, John A.

    2007-01-01

    We present the first example of a fluorophore-doped nickel chelate surface- modified silica nanoparticle that functions in a dual mode, combining histidine-tagged protein purification with site-specific fluorophore labeling. Tetramethylrhodamine (TMR)-doped silica nanoparticles, estimated to contain 700–900 TMRs per ca. 23-nm particle, were surface modified with nitrilotriacetic acid (NTA), producing TMR-SiO2-NTA-Ni+2. Silica-embedded TMR retains very high quantum yield, is resistant to quenc...

  9. A Study of Compressive Strength Characteristics of Laterite Sand Hollow Blocks

    Directory of Open Access Journals (Sweden)

    Abiodun Olanipekun

    2007-01-01

    Full Text Available This paper presents the results of experimental investigations carried out on partial replacement of sand with laterite as it affects the compressive strength of sandcrete hollow blocks. Two mix proportions (1:6 and 1:8 were used with laterite content varying between 0 and 50% at 10% intervals. Hand and machine compaction methods were used. Curing was done by sprinkling water on the specimens. The results showed that for each mix proportion and compaction method, the compressive strength decreases with increase in laterite content. Machine compacted hollow sandcrete blocks made from mix ratio 1:6 and with up to 10% laterite content is found suitable and hence recommended for building construction having attained a 28-day compressive strength of 2.07N/mm2 as required by the Nigerian Standards.

  10. The lateritic profile of Balkouin, Burkina Faso: Geochemistry, mineralogy and genesis

    Science.gov (United States)

    Giorgis, Ilaria; Bonetto, Sabrina; Giustetto, Roberto; Lawane, Abdou; Pantet, Anne; Rossetti, Piergiorgio; Thomassin, Jean-Hugues; Vinai, Raffaele

    2014-02-01

    This study reports on the geochemical and mineralogical characterization of a lateritic profile cropping out in the Balkouin area, Central Burkina Faso, aimed at obtaining a better understanding of the processes responsible for the formation of the laterite itself and the constraints to its development. The lateritic profile rests on a Paleoproterozoic basement mostly composed of granodioritic rocks related to the Eburnean magmatic cycle passing upwards to saprolite and consists of four main composite horizons (bottom to top): kaolinite and clay-rich horizons, mottled laterite and iron-rich duricrust. In order to achieve such a goal, a multi-disciplinary analytical approach was adopted, which includes inductively coupled plasma (ICP) atomic emission and mass spectrometries (ICP-AES and ICP-MS respectively), X-ray powder diffraction (XRPD), scanning electron microscopy with energy dispersive spectrometry (SEM-EDS) and micro-Raman spectroscopy.

  11. Contribution from coastal laterites to the nearshore placers of central west coast of India

    Digital Repository Service at National Institute of Oceanography (India)

    Gujar, A.R.; Srinivas, K.

    and basalts. The pebbles show genetic relation with the coastal laterites and Deccan trap basalts indicating their derivation from them before the last Holocene transgression. The petrography, mineralogical and geochemical analyses suggest that the minerals...

  12. Effects of Periwinkle Shell Ash on Lime-Stabilized Lateritic Soil ...

    African Journals Online (AJOL)

    ADOWIE PERE

    Keywords: atterberg limits, lateritic soil, lime stabilization, periwinkle shell ash .... specimen were prepared by carefully and completely ..... Fourth Edition. Canada: CENGAGE Learning. Holtz, RD; Kovacs, WD (1981). ... Potentials of Sugar cane.

  13. Effect of rice husk ash on some geotechnical properties of lateritic

    African Journals Online (AJOL)

    hp

    Keywords: Rice Husk Ash (RHA), Lateritic soil, Sub-grade, Maximum Dry ... stabilizing agent (cement or lime) included ... soil and then with distilled water. The clay mineral identification was done using ... California Bearing Ratio (CBR). 22.05.

  14. Facile Synthesis of Nickel Chromite Nanostructures by Hydrothermal Route for Photocatalytic Degradation of Acid Black 1 under Visible Light

    Directory of Open Access Journals (Sweden)

    F. Beshkar

    2015-01-01

    Full Text Available NiCr2O4 normal spinel nanostructures were prepared via hydrothermal treatment at 180 °C for 12 h in the presence of cetyltrimethylammonium bromide (CTAB, sodium dodecyl sulphate (SDS and poly vinylpyrrolidone-25000 (PVP-25000 as capping agents and subsequent calcination process at 500 °C for 3 h . In this method, [Ni(en2(H2O2](NO32 and [Cr(en3]Cl3.3H2O used as precursors and not utilized any alkaline or precipitating agent. Detailed characterization of  the as-prepared nanostructures were carried out by Fourier transform infrared (FTIR, X-ray diffraction (XRD, field emission scanning electron microscopy (FESEM, UV-Vis diffuse reflectance spectroscopy (DRS. XRD revealed the formation of pure nickel chromite spinel phase and SEM showed the formation of uniform sphere-like nanoparticles. Furthermore, the photocatalytic degradation of acid black 1 as diazo dye used in textile and dyeing water pollutants was Investigated.

  15. Compositional and structural characterisation of Ni-phyllosilicates in hydrous silicate type Ni-laterite deposits

    OpenAIRE

    Villanova de Benavent, Cristina

    2015-01-01

    Ni-bearing Mg-phyllosilicates (commonly known as garnierites) are significant ore minerals in many Ni-laterite deposits worldwide. However, the characterisation of these mineral phases is complex, as well as their classification and nomenclature, due to their fine-grained nature, low crystallinity and frequent occurrence as mixtures. The aim of this study is to shed some light to the nature of the Ni-bearing Mg-phyllosilicates occurring at the Falcondo Ni-laterite. In this deposit, these ...

  16. Analysis of ASTER data for mapping bauxite rich pockets within high altitude lateritic bauxite, Jharkhand, India

    Science.gov (United States)

    Guha, Arindam; Singh, Vivek Kr.; Parveen, Reshma; Kumar, K. Vinod; Jeyaseelan, A. T.; Dhanamjaya Rao, E. N.

    2013-04-01

    Bauxite deposits of Jharkhand in India are resulted from the lateritization process and therefore are often associated with the laterites. In the present study, ASTER (Advanced Space borne Thermal Emission and Reflection Radiometer) image is processed to delineate bauxite rich pockets within the laterites. In this regard, spectral signatures of lateritic bauxite samples are analyzed in the laboratory with reference to the spectral features of gibbsite (main mineral constituent of bauxite) and goethite (main mineral constituent of laterite) in VNIR-SWIR (visible-near infrared and short wave infrared) electromagnetic domain. The analysis of spectral signatures of lateritic bauxite samples helps in understanding the differences in the spectral features of bauxites and laterites. Based on these differences; ASTER data based relative band depth and simple ratio images are derived for spatial mapping of the bauxites developed within the lateritic province. In order to integrate the complementary information of different index image, an index based principal component (IPC) image is derived to incorporate the correlative information of these indices to delineate bauxite rich pockets. The occurrences of bauxite rich pockets derived from density sliced IPC image are further delimited by the topographic controls as it has been observed that the major bauxite occurrences of the area are controlled by slope and altitude. In addition to above, IPC image is draped over the digital elevation model (DEM) to illustrate how bauxite rich pockets are distributed with reference to the topographic variability of the terrain. Bauxite rich pockets delineated in the IPC image are also validated based on the known mine occurrences and existing geological map of the bauxite. It is also conceptually validated based on the spectral similarity of the bauxite pixels delineated in the IPC image with the ASTER convolved laboratory spectra of bauxite samples.

  17. The distribution pattern of main and trace elements in phosphatic laterites from Pirocaua Plateau (MA)

    International Nuclear Information System (INIS)

    Siqueira, N.V.M. de.

    1982-01-01

    The phosphate-laterite of Pirocaua (state of Maranhao) was studied with basis on several lines of evidence, namely, structure of the deposit, mineral distribution, variations in chemical composition and chemistry of ground waters in the region. The distribution of elements during the formation of the deposit is interpreted and the conditioning factors analysed. Air and water samples were studied respectively by X-ray diffraction and atomic absorption spectroscopy. The results show that fluctuations of the hydrostatic level were important during the formation of the phosphate horizon. When the deposit was formed there was also a decrease of the activity of the silicic acid and a parallel increase of acidity towards the top of the cross-section studied. In these conditions, Fe sup(2+) migrated towards the top of the deposit and was precipitated as Fe sup(3+) in the oxidizing zone. Migration of phosphate was in part due to its affinities to clay minerals, in which mechanism ground water played a major role. Mass balance calculations indicate that of the parent-rock is a phyllite, it is necessary an extreme enrichment in P and Sr to give the composition of the phosphate horizon. With basis on these observations we conclude that: 1) the parent-rock must have contents of P and Sr higher than the average for phyllites; or 2) the phosphate has some other source. (author)

  18. In situ neutron moisture meter calibration in lateritic soils

    International Nuclear Information System (INIS)

    Ruprecht, J.K.; Schofield, N.J.

    1990-01-01

    An in situ calibration procedure for complex lateritic soils of the jarrah forest of Western Australia is described. The calibration is based on non-destructive sampling of each access tube and on a regression of change in water content on change in neutron count ratio at 'wet' and 'dry' times of the year. Calibration equations with adequate precision were produced. However, there were high residual errors in the calibration equations which were due to a number of factors including soil water variability, the presence of a duricrust layer, soil sampling of gravelly soils and the variability of the cement slurry annulus surrounding each access tube. The calibration equations derived did not compare well with those from other studies in south-west Western Australia, but there was reasonable agreement with the general equations obtained by the Institute of Hydrology, U.K. 15 refs., 6 figs., 2 tabs

  19. Macrofungi in the lateritic scrub jungles of southwestern India

    Directory of Open Access Journals (Sweden)

    A. A. Greeshma

    2015-09-01

    Full Text Available A pilot study on macrofungi in scrub jungles (with and without fire-impact in lateritic region of southwestern coast of India was carried out.  Out of 11 species in 10 genera recovered, six and five species were confined to scrub jungle and fire-impacted scrub jungle, respectively.  An ectomycorrhizal Amanita sp. was the most frequent in scrub jungle associated with exotic (Acacia auriculiformis and A. mangium and plantation (Anacardium occidentale trees.  Based on traditional knowledge, it is a highly edible and nutritional delicacy in the coastal regions.  Astraeus odoratus was another common ectomycorrhizal fungus in native trees Hopea ponga, which was recovered from the fire-impacted scrub jungle and is possibly edible.  Edible termite mound mushroom Termitomyces striatus was also common in the fire-impacted scrub jungle.  Chlorophyllum molybdites was the most frequent mushroom in the fire-impacted scrub jungle.  

  20. Thermo physical properties of lateritic soil bricks: Influence of water content

    International Nuclear Information System (INIS)

    Meukam, P.; Noumowe, A.; Kofane, T.C.

    2002-11-01

    This paper presents an experimental study carried out in order to determine the properties of local materials used as construction materials. Cement stabilized compressed bricks were tested. The thermal properties of lateritic soil based materials were determined. The objectives of work reported in this paper are to determine the effect of addition of pozzolan or sawdust in lateritic soil brick on the thermal properties. It was shown that the effect of the incorporation of pozzolan or sawdust is the decreasing of the thermal conductivity and density. The moisture content of these materials can modify their thermal performance. Thus a study of the influence of the water content on the thermal conductivity k and the thermal diffusivity a is presented. The thermal conductivity, as a function of water content, increases rapidly between O% and 12% for lateritic soil. The thermal diffusivity curve presents a maximum for values of water content of 15% for lateritic soil and 8% for lateritic soil-pozzolan or lateritic soil- sawdust. (author)

  1. Nature and Properties of Lateritic Soils Derived from Different Parent Materials in Taiwan

    Directory of Open Access Journals (Sweden)

    Tzu-Hsing Ko

    2014-01-01

    Full Text Available The objective of this study was to investigate the physical, chemical, and mineralogical composition of lateritic soils in order to use these soils as potential commercial products for industrial application in the future. Five lateritic soils derived from various parent materials in Taiwan, including andesite, diluvium, shale stone, basalt, and Pleistocene deposit, were collected from the Bt1 level of soil samples. Based on the analyses, the Tungwei soil is an alfisol, whereas other lateritic soils are ultisol. Higher pH value of Tungwei is attributed to the large amounts of Ca2+ and Mg2+. Loupi and Pingchen soils would be the older lateritic soils because of the lower active iron ratio. For the iron minerals, the magnetic iron oxides such as major amounts of magnetite and maghemite were found for Tamshui and Tungwei lateritic soils, respectively. Lepidocrocite was only found in Soka soil and intermediate amounts of goethite were detected for Loupi and Pingchen soils. After Mg-saturated and K-saturated processes, major amounts of mixed layer were observed in Loupi and Soka soils, whereas the montmorillonite was only detected in Tungwei soil. The investigation results revealed that the parent materials would play an important role during soil weathering process and physical, chemical, and mineralogy compositions strongly affect the formation of lateritic soils.

  2. Nature and Properties of Lateritic Soils Derived from Different Parent Materials in Taiwan

    Science.gov (United States)

    2014-01-01

    The objective of this study was to investigate the physical, chemical, and mineralogical composition of lateritic soils in order to use these soils as potential commercial products for industrial application in the future. Five lateritic soils derived from various parent materials in Taiwan, including andesite, diluvium, shale stone, basalt, and Pleistocene deposit, were collected from the Bt1 level of soil samples. Based on the analyses, the Tungwei soil is an alfisol, whereas other lateritic soils are ultisol. Higher pH value of Tungwei is attributed to the large amounts of Ca2+ and Mg2+. Loupi and Pingchen soils would be the older lateritic soils because of the lower active iron ratio. For the iron minerals, the magnetic iron oxides such as major amounts of magnetite and maghemite were found for Tamshui and Tungwei lateritic soils, respectively. Lepidocrocite was only found in Soka soil and intermediate amounts of goethite were detected for Loupi and Pingchen soils. After Mg-saturated and K-saturated processes, major amounts of mixed layer were observed in Loupi and Soka soils, whereas the montmorillonite was only detected in Tungwei soil. The investigation results revealed that the parent materials would play an important role during soil weathering process and physical, chemical, and mineralogy compositions strongly affect the formation of lateritic soils. PMID:24883366

  3. Influence of the Trojan Nickel Mine on surface water quality, Mazowe valley, Zimbabwe: Runoff chemistry and acid generation potential of waste rock

    Science.gov (United States)

    Lupankwa, Keretia; Love, David; Mapani, Benjamin; Mseka, Stephen; Meck, Maideyi

    The impacts of mining on the environment depend on the nature of the ore body, the type of mining and the size of operation. The focus of this study is on Trojan Nickel Mine which is located 90 km north of Harare, Zimbabwe. It produces nickel from iron, iron-nickel and copper-nickel sulphides and disposes of waste rock in a rock dump. Surface water samples were taken at 11 points selected from a stream which drains the rock dump, a stream carrying underground water and the river into which these streams discharge. Samples were analysed for metals using atomic absorption spectrometry, for sulphates by gravitation and for carbonates and bicarbonates by back titration. Ninteen rock samples were collected from the dump and static tests were performed using the Sobek acid base accounting method. The results show that near neutral runoff (pH 7.0-8.5) with high concentrations of sulphate (over 100 mg/L) and some metals (Pb > 1.0 mg/L and Ni > 0.2 mg/L) emanates from the dump. This suggests that acid mine drainage is buffered in the dump (probably by carbonates). This is supported by the static tests, which show that the fine fraction of dump material neutralises acid. Runoff from the dump flows into a pond. Concentrations of sulphates and metals decrease after the dump runoff enters the pond, but sufficient remains to increase levels of calcium, sulphate, bicarbonate, iron and lead in the Pote River. The drop in concentrations at the pond indicates that the settling process has a positive effect on water quality. This could be enhanced by treating the pond water to raise pH, thus precipitating out metals and decreasing their concentrations in water draining from the pond.

  4. Biosorption of nickel with barley straw.

    Science.gov (United States)

    Thevannan, Ayyasamy; Mungroo, Rubeena; Niu, Catherine Hui

    2010-03-01

    Wastewater containing nickel sulphate generated from a nickel plating industry is of great concern. In the present work, biosorption of nickel by barley straw from nickel sulphate solution was investigated. Nickel uptake at room temperature (23+/-0.5 degrees C) was very sensitive to solution pH, showing a better uptake value at a pH of 4.85+/-0.10 among the tested values. The nickel biosorption isotherm fitted well the Langmuir equation. When the ionic strength (IS) of the solution was increased from less than 0.02-0.6M, nickel uptake was reduced to 12% of that obtained at IS of less than 0.02 M. Barley straw showed a higher nickel uptake (0.61 mmol/g) than acid washed crab shells (0.04 mmol/g), demonstrating its potential as an adsorbent for removal of nickel. Copyright (c) 2009 Elsevier Ltd. All rights reserved.

  5. Improved nickel plating of Inconel X-750

    Science.gov (United States)

    Farmer, M. E.; Feeney, J. E.; Kuster, C. A.

    1969-01-01

    Electroplating technique with acid pickling provides a method of applying nickel plating on Inconel X-750 tubing to serve as a wetting agent during brazing. Low-stress nickel-plating bath contains no organic wetting agents that cause the nickel to blister at high temperatures.

  6. Efficient and ultraviolet durable planar perovskite solar cells via a ferrocenecarboxylic acid modified nickel oxide hole transport layer.

    Science.gov (United States)

    Zhang, Jiankai; Luo, Hui; Xie, Weijia; Lin, Xuanhuai; Hou, Xian; Zhou, Jianping; Huang, Sumei; Ou-Yang, Wei; Sun, Zhuo; Chen, Xiaohong

    2018-03-28

    Planar perovskite solar cells (PSCs) that use nickel oxide (NiO x ) as a hole transport layer have recently attracted tremendous attention because of their excellent photovoltaic efficiencies and simple fabrication. However, the electrical conductivity of NiO x and the interface contact properties of the NiO x /perovskite layer are always limited for the NiO x layer fabricated at a relatively low annealing temperature. Ferrocenedicarboxylic acid (FDA) was firstly introduced to modify a p-type NiO x hole transport layer in PSCs, which obviously improves the crystallization of the perovskite layer and hole transport and collection abilities and reduces carrier recombination. PSCs with a FDA modified NiO x layer reached a PCE of 18.20%, which is much higher than the PCE (15.13%) of reference PSCs. Furthermore, PSCs with a FDA interfacial modification layer show better UV durability and a hysteresis-free effect and still maintain the original PCE value of 49.8%after being exposed to UV for 24 h. The enhanced performance of the PSCs is attributed to better crystallization of the perovskite layer, the passivation effect of FDA, superior interface contact at the NiO x /perovskite layers and enhancement of the electrical conductivity of the FDA modified NiO x layer. In addition, PSCs with FDA inserted at the interface of the perovskite/PCBM layers can also improve the PCE to 16.62%, indicating that FDA have dual functions to modify p-type and n-type carrier transporting layers.

  7. Growing Eremanthus erythropappus in crushed laterite: A promising alternative to topsoil for bauxite-mine revegetation.

    Science.gov (United States)

    Machado, Naiara Amaral de Miranda; Leite, Mariangela Garcia Praça; Figueiredo, Maurílio Assis; Kozovits, Alessandra Rodrigues

    2013-11-15

    Topsoil is the preferred substrate for areas requiring rehabilitation after bauxite mining. However, topsoil is sometimes lacking and so there is a need to test the suitability of other, locally available substrates. In an abandoned bauxite mine in Southeastern Brazil, small patches of native vegetation spontaneously established in shallow depressions over weathered laterite, suggesting that granulometric reduction may have facilitated the establishment of plants. To test this hypothesis, blocks of laterite collected in the area were crushed to simulate texture observed in the vegetation patches. Topsoil collected in a preserved ferruginous field near to the extraction area was also used as a substrate in which Eremanthus erythropappus seedlings, a native woody species, were grown. Seedlings were cultivated without fertilizers in these two substrates and also directly over the exposed and uncrushed laterite. The species proved to be very promising for the revegetation, showing a high survival rate in all substrates. Higher annual growth rates and higher final biomass values were observed in topsoil, but the granulometric reduction of laterite doubled plant growth rate in comparison to the exposed laterite. This result was likely due to the increased availability of essential nutrients to plants and to the improvement in physical conditions for root growth and functioning. Moreover, seedling allometry was not altered by the type of substrate, suggesting that the species was highly tolerant to the new substrate conditions, a fundamental characteristic for success of revegetation of bauxite extraction degraded areas. Copyright © 2013 Elsevier Ltd. All rights reserved.

  8. Effect on physical properties of laterite soil with difference percentage of sodium bentonite

    Science.gov (United States)

    Kasim, Nur Aisyah; Azmi, Nor Azizah Che; Mukri, Mazidah; Noor, Siti Nur Aishah Mohd

    2017-08-01

    This research was carried out in an attempt to know the physical properties of laterite soil with the appearance of difference percentage of sodium bentonite. Lateritic soils usually develop in tropical and other regions with similar hot and humid climate, where heavy rainfall, warm temperature and well drainage lead to the formation of thick horizons of reddish lateritic soil profiles rich in iron and aluminium. When sodium predominates, a large amount of water can be absorbed in the interlayer, resulting in the remarkable swelling properties observed with hydrating sodium bentonite. There are some basic physical properties test conducted in this research which are Specific Gravity Test, pH Test, Sieve Analysis, Hydrometer Test, Shrinkage Limit and Atterberg Limit. The test will be conducted with 0%, 5%, 10%, 15% and 20% of sodium bentonite. Each test will be repeated three times for the accuracy of the result. From the physical properties test the soil properties characteristic react with the sodium bentonite can be determine. Therefore the best percentage of sodium bentonite admixture can be determined for laterite soil. The outcomes of this study give positive results due to the potential of sodium bentonite to improve the laterite soil particle.

  9. Microwave acid-digestion method for determination of nickel, pro-oxidants and other heavy metals in different brands of banaspati ghee

    International Nuclear Information System (INIS)

    Latif, A.; Khan, F.; Noor, S.; Amin-ur-Rehman

    2009-01-01

    Samples of different brands of banaspati ghee (Hydrogenated vegetable oil) were procured from local market in Peshawar. Nickel, Pro-oxidants and other heavy metals in these samples were determined by microwave acid digestion method and were analyzed by atomic absorption spectrometry to evaluate the value of different brands of banaspati ghee found in the local Peshawar market. Microwave acid digestion program was developed to give reliable estimates for metals in small sample (0.5g) of banaspati ghee. It reduced the external contamination and required small quantities of acid, improving the detection-limits and overall accuracy of the analytical method. Iron and copper concentrations were found in ranges of (0.44-4.64 ppm), (0.072 - 0.38 ppm), respectively. Nickel ranged (0.098 - 0.24 ppm), while the concentrations of chromium, cadmium, lead, manganese and zinc ranged (0. 035 - 0. 15ppm), (0.022 - 0. 16ppm), (0.025 - 0.095ppm), (0.029 - 0.12 ppm) and (0.019 - 0.13 ppm), respectively.(author)

  10. Jasmonic acid Modulates the Physio-Biochemical Attributes, Antioxidant Enzyme Activity and Gene Expression in Glycine max under Nickel Toxicity

    Directory of Open Access Journals (Sweden)

    Geetika eSirhindi

    2016-05-01

    Full Text Available In present study, we evaluated the effects of Jasmonic acid (JA on physio-biochemical attributes, antioxidant enzyme activity and gene expression in soybean (Glycine max L. plants subjected to nickel (Ni stress. Ni stress decreases the shoot and root length and chlorophyll content by 37.23%, 38.31% and 39.21% respectively over the control. However, application of JA was found to improve the chlorophyll content and growth of Ni-stressed seedlings in terms of root and shoot length. Plants supplemented with Jasmonate restores the chlorophyll fluorescence, which was disturbed by Ni stress. The present study demonstrated increase in proline, glycinebetaine, total protein and total soluble sugar (TSS by 33.09%, 51.26%, 22.58% and 49.15% respectively under Ni toxicity as compared to control. Supplementation of JA to Ni stressed plants further enhanced the above parameters. Ni stress increases hydrogen peroxide (H2O2 by 68.49%, lipid peroxidation (MDA by 50.57% and NADPH oxidase by 50.92% over the control. Supplementation of JA minimizes the accumulation of H2O2, MDA and NADPH oxidase, which helps in stabilization of biomolecules. The activities of superoxide dismutase (SOD, peroxidase (POD, catalase (CAT and ascorbate peroxidase (APX increases by 40.04%, 28.22%, 48.53% and 56.79% respectively over the control in Ni treated seedlings and further enhancement in the antioxidant activity was observed by the application of JA. Ni treated soybean seedlings showed increase in expression of Fe-SOD by 77.62%, CAT by 15.25%, POD by 58.33% and APX by 80.58% over the control. Nevertheless, application of JA further enhanced the expression of the above genes in the present study. Our results signified that Ni stress caused negative impacts on soybean seedlings, but, co-application of JA facilitate the seedlings to combat the detrimental effects of Ni through enhanced osmolytes and osmoprotectants, antioxidant enzyme activity and gene expression.

  11. Effects of fines content on hydraulic conductivity and morphology of laterite soil as hydraulic barrier

    Science.gov (United States)

    Bello Yamusa, Yamusa; Yunus, Nor Zurairahetty Mohd; Ahmad, Kamarudin; Rahman, Norhan Abd; Sa'ari, Radzuan

    2018-03-01

    Laterite soil was investigated to find out the effects of fines content and to identify the micro-structural and molecular characteristics to evaluate its potentiality as a compacted soil landfill liner material. Tests were carried out on natural soil and reconstituted soil by dry weight of soil samples to determine the physical and engineering properties of the soil. All tests were carried out on the samples by adopting the British Standard 1377:1990. The possible mechanisms that contributed to the clay mineralogy were analyzed using spectroscopic and microscopic techniques such as field emission scanning electron microscopy (FESEM), energy-dispersive X-ray (EDX) and X-ray diffractometry (XRD). The laterite soil was found to contain kaolinite as the major clay minerals. A minimum of 50% fines content of laterite soil met the required result for hydraulic barriers in waste containment facilities.

  12. Zinc and nickel removal in limestone based treatment of acid mine drainage: The relative role of adsorption and co-precipitation

    International Nuclear Information System (INIS)

    Miller, Andrew; Wildeman, Thomas; Figueroa, Linda

    2013-01-01

    Highlights: • Limestone treatment of mining impacted water was simulated in batch reactors. • Zinc and nickel removals were quantified/characterized with a sequential extraction. • Removals were described with a surface complexation and a surface precipitation model. • Extraction/modeling results imply mechanisms beyond adsorption dominate metal removal. - Abstract: Mining influenced water may contain high metal and sulfate loads, and have low pH (acid mine drainage). Removal of these metals prior to environmental discharge is critical to maintain ecosystem vitality. Limestone based passive treatment systems are commonly used for pH neutralization. The same conditions that lead to pH neutralization may also remove a substantial amount of metals from solution, but the connection between treatment conditions and metal removal are not well understood. In this study, zinc and nickel removals are quantified in batch reactor simulated limestone treatment of acid mine drainage. The resulting solid phase is characterized with a sequential extraction procedure, and the removals are interpreted using surface complexation and surface precipitation models. Zinc and nickel removals are closely linked to the initial iron concentration in the mine water, but are also affected by pH, alkalinity, calcium and sulfate concentrations. The surface complexation model was based on literature descriptions of hydrous ferric oxide. In order to obtain a sufficient fit to the data, the surface site density was increased to an unrealistically high value. Uptake data was also fit to an existing surface precipitation model. The values used are similar to those found in previous studies. Both models indicate that adsorption is not the dominant removal process in the treatment system. Using adsorption only models will generally underpredict metal removals within limestone based treatment systems

  13. Effect of clay minerals on the stabilization of black cotton and lateritic soils

    International Nuclear Information System (INIS)

    Nyambok, I.O.

    1986-01-01

    The problem associated with black cotton and lateritic soils because of the swelling-shrinkage property of their constituent clay minerals were investigated. Samples of black cotton lateritic soils were collected from different parts of Kenya. The samples were analysed for their mineral compositions and later treated with hydrated lime in order to eliminate the swelling shrinkage behaviour. The samples were subsequently tested for their engineering properties in a soil mechanics laboratory using shear box and Casagrande apparatus. It was found that the chemical treatment of the soils with hydrated lime removes their plastic property and improves their shear strength. (author)

  14. A uric acid sensor based on electrodeposition of nickel hexacyanoferrate nanoparticles on an electrode modified with multi-walled carbon nanotubes

    International Nuclear Information System (INIS)

    Fang, B.; Feng, Y.; Wang, G.; Zhang, C.; Gu, A.; Liu, M.

    2011-01-01

    An electrode sensitive to uric acid was prepared by electrodeposition of nickel(II) hexacyanoferrate(III) on the surface of a glassy carbon electrode modified with multi-walled carbon nanotubes. The morphology of the material was characterized by scanning electron microscopy and Fourier transform infrared spectrometry. The modified electrode were characterized via cyclic voltammetry and amperometry (i - t). It exhibited efficient electron transfer ability and a strong and fast (< 3 s) response towards uric acid which is linear in the range from 0.1 μM to 18 μM, with a lower detection limit of 50 nM (at an S/N ratio of 3). In addition, the electrode exhibited good reproducibility and long-term stability. (author)

  15. Electroactivity of cobalt and nickel glyoximes with regard to the electro-reduction of protons into molecular hydrogen in acidic media

    Energy Technology Data Exchange (ETDEWEB)

    Pantani, O.; Anxolabehere-Mallart, E.; Aukauloo, A. [Equipe de Chimie Inorganique, Institut de Chimie Moleculaire et des Materiaux d' Orsay, UMR 8182, Universite Paris Sud, bat 420, 91405 Orsay Cedex (France); Millet, P. [Equipe de Physico-Chimie de l' Etat Solide, Institut de Chimie Moleculaire et des Materiaux d' Orsay, UMR 8182, Universite Paris Sud, bat 420, 91405 Orsay Cedex (France)

    2007-01-15

    Water electrolysis is a key technological process for the production of hydrogen and the storage of intermittent and renewable energy sources. For domestic applications, the proton exchange membrane (PEM) process provides a safe and efficient way to split water into molecular hydrogen and oxygen but this technology, which requires platinum family electro-catalysts, remains too expensive. Molecular chemistry offers new opportunities for synthesizing alternative low-cost compounds, sufficiently stable in strong acidic media. In this paper, results obtained with different nickel and cobalt glyoximes are presented. They have been chemically (using UV-visible spectroscopy) and electrochemically (using cyclic voltammetry and spectro-electrochemistry) characterized. Their ability to electroreduce protons into molecular hydrogen from aqueous acidic solutions is discussed, the compounds being either dissolved in solution or immobilized at the surface of a solid electrode using recast Nafion{sup (R)} films in view of PEM applications. (author)

  16. Synthesis, characterization and crystal structure of new nickel ...

    Indian Academy of Sciences (India)

    Abstract. A novel nickel molybdenum complex with the 2,6-pyridine dicarboxylic acid ligand was success- ... made for preparing nanoparticles with controllable size and shape. 2. ... Formula weight ..... talline nickel molybdates J. Alloys Compd.

  17. evaluation of lateritic soil using 2-d electrical resistivity methods at ...

    African Journals Online (AJOL)

    Global Journal

    The purpose of this study is to search for laterite which is of immense economic ... African and South American lithospheric plates (Burke,. 1971). It is bounded on the ... a number of boreholes (Omatsola and Adegoke 1980,. 1981). During the ...

  18. The contribution of lateritization processes to the formation of the kaolin deposits from eastern Amazon

    Science.gov (United States)

    da Costa, Marcondes Lima; Sousa, Daniel José Lima; Angélica, Rômulo Simões

    The eastern region of the Amazon is home to the most important kaolin bauxite producing district in Brazil, referred to as the Paragominas-Capim kaolin bauxite district, which has a reserve of at least 1.0 billion tons of high-quality kaolin used in the paper coating industry. The kaolin deposits are closely related to sedimentary rocks of the Parnaíba basin and their lateritic cover. Two large deposits are already being mined: IRCC (Ipixuna) and PPSA (Paragominas). The geology of the IRCC mine is comprised of the kaolin-bearing lower unit (truncated mature laterite succession derived from the Ipixuna/Itapecuru formation) and the upper unit (immature lateritized Barreiras formation). The lower kaolin unit is characterized by a sandy facies at the bottom and a soft (ore) with flint facies at the top. It is formed by kaolinite, quartz, some iron oxi-hydroxides, mica and several accessories and heavy minerals. The mangrove covering; and immature lateritization - partial kaolin ferruginization during the Pleistocene.

  19. Critical metals (REE, Sc, PGE) in Ni laterites from Cuba and the Dominican Republic

    Czech Academy of Sciences Publication Activity Database

    Aiglsperger, T.; Proenza, J. A.; Lewis, J. F.; Labrador, M.; Svojtka, Martin; Rojas-Purón, A.; Longo, F.; Ďurišová, Jana

    2016-01-01

    Roč. 73, March 01 (2016), s. 127-147 ISSN 0169-1368 Institutional support: RVO:67985831 Keywords : Caribbean * Cuba * Dominican Republic * Falcondo mining area * Moa Bay mining area * Ni laterite * Platinum Group Elements * Rare Earth Elements * Scandium Subject RIV: DB - Geology ; Mineralogy Impact factor: 3.095, year: 2016

  20. Flotation-separation and ICP-AES determination of ultra trace amounts of copper, cadmium, nickel and cobalt using 2-aminocyclopentene-1-dithiocarboxylic acid.

    Science.gov (United States)

    Shamsipur, Mojtaba; Hashemi, Omid Reza; Safavi, Afsaneh

    2005-09-01

    A rapid flotation method for separation and enrichment of ultra trace amounts of copper(II), cadmium(II), nickel(II) and cobalt(II) ions from water samples is established. At pH 6.5 and with sodium dodecylsulfate used as a foaming reagent, Cu2+, Cd2+, Ni2+ and Co2+ were separated simultaneously with 2-aminocyclopentene-1-dithiocarboxylic acid (ACDA) added to 1 l of aqueous solution. The proposed procedure of preconcentration is applied prior to the determination of these four analytes using inductivity coupled plasma-atomic emission spectrometry (ICP-AES). The effects of pH, concentration of ACDA, applicability of different surfactants and foreign ions on the separation efficiency were investigated. The preconcentration factor of the method is 1000 and the detection limits of copper(II), cadmium(II), nickel(II) and cobalt(II) ions are 0.078, 0.075, 0.072 and 0.080 ng ml(-1), respectively.

  1. Arsenic adsorption of lateritic soil, limestone powder, lime and fly ash on arsenic-contaminated soil

    Directory of Open Access Journals (Sweden)

    Wuthiphun, L.

    2007-05-01

    Full Text Available Arsenic adsorption efficiency of soil covering materials (lateritic soil, limestone powder, lime and fly ash on arsenic-contaminated soil obtained from Ronpiboon District, Nakhon Sri Thammarat Province tosolve arsenic air pollution problem was investigated using batch experiments. The four types of the aforementioned soil covering materials were examined to determine their arsenic adsorption efficiency, equilibriumtime as well as adsorption isotherms.The results revealed that among soil covering materials mixed with arsenic-contaminated soil at 10% w/w, the efficiency of arsenic adsorption of fly ash, lateritic soil, lime and limestone powder were 84, 60,38 and 1% respectively. The equilibrium time for lateritic soil at pH 4 was achieved within 4 hrs, whereas pH 7 and 12, the equilibrium time was 6 hrs. For fly ash, 2 hrs were required to reach the equilibrium at pH 12, while the equilibrium time was attained within 6 hrs at pH 4 and 7. Furthermore, lateritic soil possessedhigh arsenic adsorption efficiency at pH 7 and 4 and best fit with the Langmuir isotherm. The fly ash showing high arsenic adsorption efficiency at pH 12 and 7 fit the Freundlich isotherm at pH 12 and Langmuirisotherm at pH 7.This indicated that lateritic soil was suitable for arsenic adsorption at low pH, whilst at high pH,arsenic was well adsorbed by fly ash. The Freundlich and Langmuir isotherm could be used to determine quantities of soil covering materials for arsenic adsorption to prevent arsenic air pollution from arseniccontaminated soils.

  2. Nickel allergy

    DEFF Research Database (Denmark)

    Fischer, L A; Johansen, J D; Menné, T

    2007-01-01

    BACKGROUND: The frequency of nickel allergy varies between different population groups. Exposure regulation has proven effective in decreasing the frequency. Experimental studies with other allergens have shown a significant relation between patch test reactivity and repeated open application test...... in a patch test and a dilution series of three concentrations in a ROAT, with duration of up to 21 days. Eighteen persons with no nickel allergy were included as control group for the ROAT. RESULTS: The predicted dose which will elicit a reaction in 10% of allergic individuals was calculated to be 0......-response; indeed, there was no statistically significant difference. CONCLUSIONS: For elicitation of nickel allergy the elicitation threshold for the patch test is higher than the elicitation threshold (per application) for the ROAT, but is approximately the same as the accumulated elicitation threshold...

  3. Influence of Stockpile Angle in Natural Drying of Laterite Ore

    Directory of Open Access Journals (Sweden)

    Yoalbys Retirado-Mediaceja

    2016-10-01

    Full Text Available Natural drying is performed at Cuban nickel plants by depositing bulk ore in the open. The ore is currently being stockpiled without much consideration for the impact of the drying surface angle on the process power behavior. Simulations were carried out in this investigation, which prove that an increased triangular stockpile angle considerably reduces natural drying efficiency. A 45 sexagesimal degree angle to the horizontal plane results in exposure of a large volume of ore to natural drying and guarantees adequate energy performance.

  4. Selective extraction by dissolvable (nitriloacetic acid-nickel)-layered double hydroxide coupled with reaction with potassium thiocyanate for sensitive detection of iron(III).

    Science.gov (United States)

    Tang, Sheng; Chang, Yuepeng; Shen, Wei; Lee, Hian Kee

    2016-07-01

    A highly selective method has been proposed for the determination of iron cation (Fe(3+)). (Nitriloacetic acid-nickel)-layered double hydroxide ((NTA-Ni)-LDH) was successfully synthesized and used as dissolvable sorbent in dispersive solid-phase extraction to pre-concentrate and separate Fe(3+) from aqueous phase. Since Fe(3+) has a larger formation constant with NTA compared to Ni(2+), subsequently ion exchange occurred when (NTA-Ni)-LDH was added to the sample solution. The resultant (NTA-Fe)-LDH sol was isolated and transferred in an acidic medium containing potassium thiocyanate (KSCN). Since (NTA-Fe)-LDH could be dissolved in acidic conditions, Fe(3+)was released and reacted with SCN(-) to form an Fe-SCN complex. The resulting product was measured by ultraviolet-visible spectrometry for quantitative detection of Fe(3+). Extraction factors, including sample pH, reaction pH, extraction temperature, extraction time, reaction time and concentration of KSCN were optimized. This method achieved a low limit of detection of 15.2nM and a good linear range from 0.05 to 50μM (r(2)=0.9937). A nearly 18-fold enhancement of signal intensity was achieved after selective extraction. The optimized conditions were validated by applying the method to determine Fe(3+) in seawater samples. Copyright © 2016 Elsevier B.V. All rights reserved.

  5. Investigation of the Effects of Solution Temperature on the Corrosion Behavior of Austenitic Low-Nickel Stainless Steels in Citric Acid using Impedance and Polarization Measurements

    Directory of Open Access Journals (Sweden)

    Mulimbayan Francis M.

    2015-01-01

    Full Text Available Stainless steels may be classified according to alloy microstructure – ferritic, austenitic, martensitic, duplex, and precipitation hardening grades. Among these, austenitic grade has the largest contribution to market due to the alloy’s numerous industrial and domestic applications. In this study, the corrosion behavior of low-Nickel stainless steel in citric acid was investigated using potentiodynamic polarization techniques and Electrochemical Impedance Spectroscopy (EIS. The corrosion current density which is directly related to corrosion rate was extracted from the generated anodic polarization curve. Increasing the temperature of the citric acid resulted to increased corrosion current densities indicating higher corrosion rates at initial corrosion condition. EIS was performed to generate Nyquist plots whose shape and size depicts the corrosion mechanism and corrosion resistance of the alloy in citric acid, respectively. All the generated Nyquist plots have depressed semi-circle shapes implying that corrosion process takes place with charge-transfer as the rate-determining step. Based from the extracted values of polarization resistance (Rp, the temperature of the solution has negative correlation with the corrosion resistance of the studied alloy.

  6. Analysis of nickel industrial wastes by nuclear techniques and its pollution assessment

    International Nuclear Information System (INIS)

    Diaz Rizo, O.; Coto Hernandez, I.; Lopez Pino, N.; D'Alessandro Rodriguez, K.; Arado Lopez, J.O.; Diaz Arado, O.; Reyes Perez, H.

    2011-01-01

    The concentration of some heavy metal (Mn, Fe, Co, Ni, Cu and Zn) in nickel industrial wastes from Moa, northeastern Cuba, is determined. The analysis was performed by External Standard method of ED-XRF, using 238 Pu (1.11 GBq) excitation source and laterite certified reference material as standards. The capability of INAA using neutrons from a Pu-Be (10 7 n/s) source and Low-Background Gamma Spectrometer (LBGS) at InSTEC is studied. The determined concentration values for Ni, Co, Cu and Zn shows a different pollution degree according to Dutch regulations and US NOAA guidelines. (Author)

  7. Does airborne nickel exposure induce nickel sensitization?

    Science.gov (United States)

    Mann, Eugen; Ranft, Ulrich; Eberwein, Georg; Gladtke, Dieter; Sugiri, Dorothee; Behrendt, Heidrun; Ring, Johannes; Schäfer, Torsten; Begerow, Jutta; Wittsiepe, Jürgen; Krämer, Ursula; Wilhelm, Michael

    2010-06-01

    Nickel is one of the most prevalent causes of contact allergy in the general population. This study focuses on human exposure to airborne nickel and its potential to induce allergic sensitization. The study group consisted of 309 children at school-starter age living in the West of Germany in the vicinity of two industrial sources and in a rural town without nearby point sources of nickel. An exposure assessment of nickel in ambient air was available for children in the Ruhr district using routinely monitored ambient air quality data and dispersion modelling. Internal nickel exposure was assessed by nickel concentrations in morning urine samples of the children. The observed nickel sensitization prevalence rates varied between 12.6% and 30.7%. Statistically significant associations were showed between exposure to nickel in ambient air and urinary nickel concentration as well as between urinary nickel concentration and nickel sensitization. Furthermore, an elevated prevalence of nickel sensitization was associated with exposure to increased nickel concentrations in ambient air. The observed associations support the assumption that inhaled nickel in ambient air might be a risk factor for nickel sensitization; further studies in larger collectives are necessary.

  8. Microwave irradiation and citric acid assisted seed germination and phytoextraction of nickel (Ni) by Brassica napus L.: morpho-physiological and biochemical alterations under Ni stress.

    Science.gov (United States)

    Farid, Mujahid; Ali, Shafaqat; Rizwan, Muhammad; Saeed, Rashid; Tauqeer, Hafiz Muhammad; Sallah-Ud-Din, Rasham; Azam, Ahmed; Raza, Nighat

    2017-09-01

    The complex bio-geochemistry of soil allows pollutant to persist for a longer period of time which further decreased the fertility and natural composition of land. Nickel, an inorganic pollutant, coming from a wide range of industrial and manufacturing units possesses serious threat to soil degradation and crop productivity around the world. The present study was carried to evaluate the combined role of microwave irradiation (MR) and citric acid (CA) on the phytoextraction potential of Brassica napus L. under Ni stress. An initial seed germination test was conducted to select effective time scale of MR exposure. Highest seed germination was observed at exposure of 2.45 GHz frequency for 30 s. Healthy seeds of B. napus L. genotype Faisal Canola (RBN-03060) treated with MR at 2.45 GHz for 30 s were sown in plastic pots filled with 5 kg of soil. Nickel and CA applied exogenously in solution form with different combinations to both MR-treated and untreated B. napus plants. The MR-treated plants showed higher growth, biomass, photosynthetic pigments (Chl a, b, total, and carotenoids) and activities of antioxidant enzymes (SOD, POD, APX, CAT) as compared to untreated plants who showed higher reactive oxygen species (MDA, H 2 O 2 ) and electrolyte leakage. Increasing Ni concentration significantly decreased the physiological and biochemical attributes of B. napus both in MR-treated and untreated plants. The addition of CA alleviated Ni-induced toxic effects in both MR-treated and untreated plants by improving antioxidant defense system. The degree of Ni stress mitigation was higher in MR-treated plants. The Ni concentration was higher in root, stem, and leaves of MR-treated plants under CA application as compared to untreated plants. The present study concluded that seeds treated with MR before sowing showed higher accumulation and concentration of Ni from soil, and this phenomenon boosted with the application of CA.

  9. COMPARATIVE ASSESSMENT OF RICE HUSK ASH, POWDERED GLASS AND CEMENT AS LATERITIC SOIL STABILIZERS

    Directory of Open Access Journals (Sweden)

    Adebisi Ridwan

    2016-10-01

    Full Text Available This paper compares the stabilizing effects of three different materials, namely: rice husk ash, powdered glass, and cement on the properties of lateritic soil. The basic properties of the lateritic soil were first obtained through colour, moisture content determination, specific gravity, particle size distribution and Atterberg limits tests. Each of the stabilizing materials was then mixed with the lateritic soil in varying percentages of 2.5%, 5%, 7.5%, 10%, 12.5% and 15% by weight of the soil. Thereafter, compaction and California bearing ratio (CBR tests were carried out on the sample mixes to determine the effects of the materials on the lateritic soil. Chemical tests were also carried out on the samples to determine their percentage oxides composition. The compaction test showed that the highest maximum dry densities (MDD obtained for the mixed samples were 2.32 g/cm3 (at 2.5% cement addition, 2.28g/cm3 (at 5% powdered glass (PG addition and 2.18 g/cm3 (at 5% rice husk ash (RHA addition with corresponding optimum moisture contents (OMC of 10.06%, 14.3% and 12.31% respectively. The CBR tests showed that the CBR values increased in all cases as the materials were added with those of the cement and powdered glass giving the highest values and showing close semblance under unsoaked conditions. The chemical test showed that the significant oxides present in the cement, powdered glass and rice husk ash were CaO (53.60%, SiO2 (68.45% and SiO2 (89.84% respectively.

  10. Evaluation of Changes in Index Properties of Lateritic Soil Stabilized with Fly Ash

    Directory of Open Access Journals (Sweden)

    Agapitus AMADI

    2010-12-01

    Full Text Available For soils to be suitable in civil engineering projects, they must meet existing local requirements for index properties in addition to certain strength criteria. Typically, specifications limit these properties to some threshold values which in most cases are project specific. Some lateritic soils in their natural state need some treatment/modification to meet these specification requirements. The objective of this study was to evaluate changes in the index properties (i.e., particle size distribution, Atterberg limits and compaction characteristics of a residually derived lateritic soil following fly ash application. Lateritic soil – fly ash mixtures with up to 20% fly ash by dry weight of soil were tested and specimens for compaction characteristics were prepared at different compaction states (optimum, dry and wet of optimum moisture content and compacted using British Standard Light (BSL compactive effort. While soil – fly ash mixtures containing up to 15% fly ash classify as CL according to USCS classification system and plotted above A-line in the plasticity chart, it was observed that changes in the gradation characteristics of soil sample treated with 20% fly ash resulted in the alteration of its classification to ML as well as the crossing of the A- line to the silty region. The liquid limit (LL varied from 42.2 to 29.53% representing 70% reduction while the plasticity index (PI of specimen treated with 20% fly ash was 16% lower than that of natural soil. The optimum moisture content (OMC ranged from 17.36% for the natural soil to 18.34% for soil mixtures containing 20% fly ash which yielded dry unit weight of 17.2kN/m3 for the natural soil and 16.1kN/m3 for samples treated with 20% fly ash. From the study, useful data were obtained showing substantial and desirable changes in the properties of lateritic soil as a civil engineering material on application of fly ash.

  11. Effect of Lime Stabilization on Vertical Deformation of Laterite Halmahera Soil

    Science.gov (United States)

    Saing, Zubair; Djainal, Herry

    2018-04-01

    In this paper, the study was conducted to determine the lime effect on vertical deformation of road base physical model of laterite Halmahera soil. The samples of laterite soil were obtained from Halmahera Island, North Maluku Province, Indonesia. Soil characteristics were obtained from laboratory testing, according to American Standard for Testing and Materials (ASTM), consists of physical, mechanical, minerals, and chemical. The base layer of physical model testing with the dimension; 2m of length, 2m of width, and 1.5m of height. The addition of lime with variations of 3, 5, 7, an 10%, based on maximum dry density of standard Proctor test results and cured for 28 days. The model of lime treated laterite Halmahera soil with 0,1m thickness placed on subgrade layer with 1,5m thickness. Furthermore, the physical model was given static vertical loading. Some dial gauge is placed on the lime treated soil surface with distance interval 20cm, to read the vertical deformation that occurs during loading. The experimentals data was analyzed and validated with numerical analysis using finite element method. The results showed that the vertical deformation reduced significantly on 10% lime content (three times less than untreated soil), and qualify for maximum deflection (standard requirement L/240) on 7-10% lime content.

  12. ESR dating of laterite from Ban Tha Ta Suea, Kanchanaburi, Thailand

    International Nuclear Information System (INIS)

    Limsuwan, S.; Vichaidid, T.; Limsuwan, P.

    2011-01-01

    Electron spin resonance (ESR) dating was carried out on laterite samples collected from Ban Tha Ta Suea, the original deposit of the laterite used in the construction of Muang Sing Historical Park. Ban Tha Ta Suea is about 6 km east of Muang Sing Historical Park in Kanchanaburi province (181 km far from Bangkok). The dose response of the g=2.0028 ESR signal was found to be suitable for age determination. An exponential saturation function was fitted to the ESR signal growth on additional γ-irradiation. Extrapolation of this function resulted in the accumulated dose 144±5 Gy. Gamma spectroscopy and neutron activation analysis (NAA) were used to determine concentrations of 238 U, 232 Th and 40 K in the samples from which the annual dose rate 16±2 mGy was calculated. In addition, the dose rate of cosmic rays was taken into account. The ESR age of laterite samples was found to be 9.0±0.9 ka. This age falls within the Holocene epoch of the Quaternary on the geological time scale. Samples from Muang Sing Historical Park were assigned to the same epoch. Both results agree with the geological map.

  13. GEOTECHNICAL CHARACTERISTICS OF LATERITIC SOIL STABILIZED WITH SAWDUST ASH-LIME MIXTURES

    Directory of Open Access Journals (Sweden)

    Emeka Segun Nnochiri

    2017-04-01

    Full Text Available This study assesses the geotechnical characteristics of lateritic soil and sawdust ash lime (SDAL mixtures. Preliminary tests were carried out on the natural soil sample for identification and classification purposes. The sawdust was mixed with lime for stabilization in the ratio 2:1. This mixture was thereafter added to the lateritic soil in varying proportions of 2, 4, 6, 8 and 10% by weight of soil. Addition of SDAL increased values of Optimum Moisture Content (OMC from 17.0% at 0% SDAL to 26.5% at 10% SDAL by weight of soil, also, values of Maximum Dry Density (MDD decreased from 2040 kg/m3 at 0% SDAL to 1415 kg/m3 at 10% SDAL. Values of Unconfined Compressive Strength (UCS increased from 38.58 kN/m2 at 0% SDAL to highest value of 129.63 kN/m2 at 6% SDAL. The values of liquid limits and plasticity index of the soil were effectively reduced with the addition of the SDAL, from 54.0% at 0% SDAL to 49.0% at 10% SDAL and from 13.7% at 0% SDAL to 12.5% at 10% SDAL respectively. It was therefore concluded that the sawdust ash lime (SDAL mixture can serve as a cheap soil stabilizing agent for poor lateritic soil.

  14. Dating Amazonian laterites through the novel geochronometers kaolinite and iron oxides

    Science.gov (United States)

    Allard, Thierry; Bressan Riffel, Silvana; Gautheron, Cécile; Fernandes Soares, Bruna; Pinna-Jamme, Rosella; Morin, Guillaume

    2016-04-01

    Soils on Earth's surface are in constant interaction with climate. As a matter of fact, soils cannot only produce greenhouse effect gases, such as NO2 and CH4, but also behave as sinks for CO2, especially by silicate weathering. Major processes of silicate weathering are known and exhibit climatic zonation at the global scale. Laterites are particularly relevant because they are ancient and deeply weathered soils of major significance. They occupy 30 % of the continental surface and can keep records of past climates and landscape modifications (paleosurface) through specific mineral markers. These formations reach several tens of meters and are mainly composed of kaolinite, iron and aluminium oxides as well as relicts of parent minerals such as quartz and ancillary minerals. Once the major processes of laterite formation are known, their age will allow a growth of researches, owing to the implementation of various chronometers. Moreover, it is fundamental to date laterites in order to improve our understanding of soil formation related to paleoclimates, and to build predictive models of their evolution. In this study, we focus on comparing kaolinite ages with the still unknown ages of lateritic duricrusts from the central Amazon region (Brazil), where strong weathering processes were developed from the early Tertiary, after the Andean uplift. The central Amazon region displays flat areas and dissected plateaus (100-180 m a.s.l.) sustained by weathered clastic sedimentary rocks and latosols. The region contains horizons of duricrusts, relatively continuous layers of Fe-cuirasses, stratified lateritic profiles, and kaolin deposits. Here we employed two methods to date ubiquitous secondary minerals of laterite, which are consistent with geological time-scale. The corresponding geochronometers are the following: (i) radiation-induced defects in kaolinite (trapped in duricrusts) analysed by electron paramagnetic resonance spectroscopy (EPR) (Balan et al., 2005), and (ii

  15. Synthesis and Characterization of Cu(II), Co(II) and Ni(II) Complexes of Trithiocyanuric Acid: The Structure of {N,N'-Bis(3-Aminopropyl)-1,3-Propanediamine}-(Trithiocyanurato)Nickel(II)

    Czech Academy of Sciences Publication Activity Database

    Kopel, P.; Trávníček, Zdeněk; Kvítek, L.; Černošek, Z.; Wrzeszcz, G.; Marek, J.

    2003-01-01

    Roč. 56, č. 1 (2003), s. 1-11 ISSN 0095-8972 R&D Projects: GA ČR GA203/00/0152; GA AV ČR IBS5038351 Institutional research plan: CEZ:AV0Z5038910 Keywords : Copper(II) * cobalt(II) and nickel(II) complexes * Trithiocyanuric acid Subject RIV: CE - Biochemistry Impact factor: 0.841, year: 2003

  16. Bioavailability of nickel in man: effects of foods and chemically-defined dietary constituents on the absorption of inorganic nickel.

    Science.gov (United States)

    Solomons, N W; Viteri, F; Shuler, T R; Nielsen, F H

    1982-01-01

    By serial determination of the change in plasma nickel concentration following a standard dose of 22.4 mg of nickel sulfate hexahydrate containing 5 mg of elemental nickel, the bioavailability of nickel was estimated in human subjects. Plasma nickel concentration was stable in the fasting state and after an unlabeled test meal, but after the standard dose of nickel in water was elevated 48.8, 73.0, 80.0, and 53.3 microgram/1, respectively, at hours 1, 2, 3, and 4. Plasma nickel did not rise above fasting levels when 5 mg of nickel was added to two standard meals: a typical Guatemalan meal and a North American breakfast. When 5 mg of nickel was added to five beverages-whole cow milk, coffee, tea, orange juice, and Coca Cola-the rise in plasma nickel was significantly suppressed with all but Coca Cola. Response to nickel also was suppressed in the presence of 1 g of ascorbic acid. Phytic acid in a 2:1 molar ratio with nickel, however, did not affect the rise in plasma nickel. The chelate of iron and ethylenediaminetetraacetate, NaFeEDTA, an iron-fortifying agent suggested for application in Central America, slightly but not significantly depressed plasma nickel rise at 2 hours, whereas disodium EDTA depressed plasma nickel levels significantly below the fasting nickel curve at 3 and 4 hours postdose. These studies suggest that the differential responses of inorganic nickel to distinct foods, beverages, and chemically-defined dietary constituents could be important to human nutrition.

  17. Standard practice for determining the susceptibility of stainless steels and related Nickel-Chromium-Iron Alloys to stress-corrosion cracking in polythionic acids

    CERN Document Server

    American Society for Testing and Materials. Philadelphia

    2010-01-01

    1.1 This practice covers procedures for preparing and conducting the polythionic acid test at room temperature, 22 to 25°C (72 to 77°F), to determine the relative susceptibility of stainless steels or other related materials (nickel-chromiumiron alloys) to intergranular stress corrosion cracking. 1.2 This practice can be used to evaluate stainless steels or other materials in the “as received” condition or after being subjected to high-temperature service, 482 to 815°C (900 to 1500°F), for prolonged periods of time. 1.3 This practice can be applied to wrought products, castings, and weld metal of stainless steels or other related materials to be used in environments containing sulfur or sulfides. Other materials capable of being sensitized can also be tested in accordance with this test. 1.4 This practice may be used with a variety of stress corrosion test specimens, surface finishes, and methods of applying stress. 1.5 This standard does not purport to address all of the safety concerns, if any, ...

  18. Dual-mode fluorophore-doped nickel nitrilotriacetic acid-modified silica nanoparticles combine histidine-tagged protein purification with site-specific fluorophore labeling.

    Science.gov (United States)

    Kim, Sung Hoon; Jeyakumar, M; Katzenellenbogen, John A

    2007-10-31

    We present the first example of a fluorophore-doped nickel chelate surface-modified silica nanoparticle that functions in a dual mode, combining histidine-tagged protein purification with site-specific fluorophore labeling. Tetramethylrhodamine (TMR)-doped silica nanoparticles, estimated to contain 700-900 TMRs per ca. 23 nm particle, were surface modified with nitrilotriacetic acid (NTA), producing TMR-SiO2-NTA-Ni2+. Silica-embedded TMR retains very high quantum yield, is resistant to quenching by buffer components, and is modestly quenched and only to a certain depth (ca. 2 nm) by surface-attached Ni2+. When exposed to a bacterial lysate containing estrogen receptor alpha ligand binding domain (ERalpha) as a minor component, these beads showed very high specificity binding, enabling protein purification in one step. The capacity and specificity of these beads for binding a his-tagged protein were characterized by electrophoresis, radiometric counting, and MALDI-TOF MS. ERalpha, bound to TMR-SiO2-NTA-Ni++ beads in a site-specific manner, exhibited good activity for ligand binding and for ligand-induced binding to coactivators in solution FRET experiments and protein microarray fluorometric and FRET assays. This dual-mode type TMR-SiO2-NTA-Ni2+ system represents a powerful combination of one-step histidine-tagged protein purification and site-specific labeling with multiple fluorophore species.

  19. Acid extraction of molybdenum, nickel and cobalt from mineral sludge generated by rainfall water at a metal recycling plant.

    Science.gov (United States)

    Vemic, M; Bordas, F; Guibaud, G; Comte, S; Joussein, E; Lens, P N L; Van Hullebusch, E D

    2016-01-01

    This study investigated the leaching yields of Mo, Ni and Co from a mineral sludge of a metal recycling plant generated by rainfalls. The investigated mineral sludge had a complex heterogeneous composition, consisting of particles of settled soil combined with metal-bearing particles (produced by catalysts, metallic oxides and battery recycling). The leaching potential of different leaching reagents (stand-alone strong acids (HNO3 (68%), H2SO4 (98%) and HCl (36%)) and acid mixtures (aqua regia (nitric + hydrochloric (1:3)), nitric + sulphuric (1:1) and nitric + sulphuric + hydrochloric (2:1:1)) was investigated at changing operational parameters (solid-liquid (S/L) ratio, leaching time and temperature), in order to select the leaching reagent which achieves the highest metal leaching yields. Sulphuric acid (98% H2SO4) was found to be the leachant with the highest metal leaching potential. The optimal leaching conditions were a three-stage successive leaching at 80 °C with a leaching time of 2 h and S/L ratio of 0.25 g L(-1). Under these conditions, the achieved mineral sludge sample leaching yields were 85.5%, 40.5% and 93.8% for Mo, Ni and Co, respectively. The higher metal leaching potential of H2SO4 in comparison with the other strong acids/acid mixtures is attributed to the fact that H2SO4 is a diacidic compound, thus it has more H(+) ions, resulting in its stronger oxidizing power and corrosiveness.

  20. Alleviation of nickel toxicity in finger millet (Eleusine coracana L. germinating seedlings by exogenous application of salicylic acid and nitric oxide

    Directory of Open Access Journals (Sweden)

    Kasi Viswanath Kotapati

    2017-06-01

    Full Text Available This study investigated the effect of salicylic acid (SA and sodium nitroprusside (SNP; NO donor on nickel (Ni toxicity in germinating finger millet seedlings. Fourteen-day-old finger millet plants were subjected to 0.5 mmol L−1 Ni overload and treated with 0.2 mmol L−1 salicylic acid and 0.2 mmol L−1 sodium nitroprusside to lessen the toxic effect of Ni. The Ni overload led to high accumulation in the roots of growing plants compared to shoots, causing oxidative stress. It further reduced root and shoot length, dry mass, total chlorophyll, and mineral content. Exogenous addition of either 0.2 mmol L−1 SA or 0.2 mmol L−1 SNP reduced the toxic effect of Ni, and supplementation with both SA and SNP significantly reduced the toxic effect of Ni and increased root and shoot length, chlorophyll content, dry mass, and mineral concentration in Ni-treated plants. The results show that oxidative stress can be triggered in finger millet plants by Ni stress by induction of lipoxygenase activity, increase in levels of proline, O2•− radical, MDA, and H2O2, and reduction in the activity of antioxidant enzymes such as CAT, SOD, and APX in shoots and roots. Exogenous application of SA or SNP, specifically the combination of SA + SNP, protects finger millet plants from oxidative stress observed under Ni treatment.

  1. Biological role of nickel

    Energy Technology Data Exchange (ETDEWEB)

    Thauer, R K; Diekert, G; Schoenheit, P

    1980-01-01

    Several enzymes and one cofactor have recently been shown to contain nickel. For example, urease of jack beans has been found to be a nickel protein and factor F/sub 430/ from methanogenic bacteria to be a nickel tetrapyrrole. The biological role of nickel in several organisms is discussed.

  2. Coordination compounds of cobalt(II), nickel(II), copper(II), and zinc(II) with pantothenic acid

    Energy Technology Data Exchange (ETDEWEB)

    Shabilalov, A.A.; Yunuskhodzhaev, A.N.; Khodzhaev, O.F.; Azizov, M.A.

    1986-11-01

    The compounds Ni(PANA - H)/sub 2/ x 4H/sub 2/O (PANA stands for pantothenic acid, and - H indicates a deprotonated ligand), Cu(PANA - H)/sub 2/ x 2H/sub 2/O, Zn(PANA - H)/sub 2/ x H/sub 2/O, Co(PANA - H)Cl x H/sub 2/O, and Ni(PANA - H)Cl x 3H/sub 2/O have been synthesized on the basis of pantothenic acid and Co(II), Ni(II), Cu(II), and Zn(II) salts in aqueous media. The compounds have been identified by elemental and x-ray diffraction analysis. Some physicochemical properties (solubility, melting point, molar conductivity) of the compounds obtained have been studied. The structure of the compounds isolated has been established on the basis of an analysis of their IR, ESR, and electronic spectra, as well as derivatograms.

  3. Process for forming a nickel foil with controlled and predetermined permeability to hydrogen

    Science.gov (United States)

    Engelhaupt, Darell E.

    1981-09-22

    The present invention provides a novel process for forming a nickel foil having a controlled and predetermined hydrogen permeability. This process includes the steps of passing a nickel plating bath through a suitable cation exchange resin to provide a purified nickel plating bath free of copper and gold cations, immersing a nickel anode and a suitable cathode in the purified nickel plating bath containing a selected concentration of an organic sulfonic acid such as a napthalene-trisulfonic acid, electrodepositing a nickel layer having the thickness of a foil onto the cathode, and separating the nickel layer from the cathode to provide a nickel foil. The anode is a readily-corrodible nickel anode. The present invention also provides a novel nickel foil having a greater hydrogen permeability than palladium at room temperature.

  4. Process for forming a nickel foil with controlled and predetermined permeability to hydrogen

    International Nuclear Information System (INIS)

    Engelhaupt, D. E.

    1981-01-01

    The present invention provides a novel process for forming a nickel foil having a controlled and predetermined hydrogen permeability. This process includes the steps of passing a nickel plating bath through a suitable cation exchange resin to provide a purified nickel plating bath free of copper and gold cations, immersing a nickel anode and a suitable cathode in the purified nickel plating bath containing a selected concentration of an organic sulfonic acid such as a napthalene-trisulfonic acid, electrodepositing a nickel layer having the thickness of a foil onto the cathode, and separating the nickel layer from the cathode to provide a nickel foil. The anode is a readilycorrodible nickel anode. The present invention also provides a novel nickel foil having a greater hydrogen permeability than palladium at room temperature

  5. Elementary and isotopic geochemistry of vein goethite in laterite-gossanic crusts from the Igarape Bahia gold mine (Carajas, Brazil)

    International Nuclear Information System (INIS)

    Costa, Marcondes Lima da; Schumann, Thomas; Poellmann, Herbert

    1996-01-01

    The lateritic crusts of the gold mine from the Igarape Bahia, in Carajas, situated at Para state, Brazil, present themselves frequently sectioned by the goethite sub-vertical veins. The veins have the following measures: until 10 cm of thickness and more than 6 m of length. This work aims to characterize the textural, mineralogical and chemical aspects of these veins, in order to understand its evolution, mainly the relation with the laterites and its geological importance, including the aspects referents to the mineral prospecting. (author)

  6. Lewis Acid Assisted Nickel-Catalyzed Cross-Coupling of Aryl Methyl Ethers by C−O Bond-Cleaving Alkylation: Prevention of Undesired β-Hydride Elimination

    KAUST Repository

    Liu, Xiangqian; Hsiao, Chien-Chi; Kalvet, Indrek; Leiendecker, Matthias; Guo, Lin; Schoenebeck, Franziska; Rueping, Magnus

    2016-01-01

    In the presence of trialkylaluminum reagents, diverse aryl methyl ethers can be transformed into valuable products by C-O bond-cleaving alkylation, for the first time without the limiting β-hydride elimination. This new nickel

  7. Occurrence model for magmatic sulfide-rich nickel-copper-(platinum-group element) deposits related to mafic and ultramafic dike-sill complexes: Chapter I in Mineral deposit models for resource assessment

    Science.gov (United States)

    Schulz, Klaus J.; Woodruff, Laurel G.; Nicholson, Suzanne W.; Seal, Robert R.; Piatak, Nadine M.; Chandler, Val W.; Mars, John L.

    2014-01-01

    Magmatic sulfide deposits containing nickel (Ni) and copper (Cu), with or without (±) platinum-group elements (PGE), account for approximately 60 percent of the world’s nickel production. Most of the remainder of the Ni production is derived from lateritic deposits, which form by weathering of ultramafic rocks in humid tropical conditions. Magmatic Ni-Cu±PGE sulfide deposits are spatially and genetically related to bodies of mafic and/or ultramafic rocks. The sulfide deposits form when the mantle-derived mafic and/or ultramafic magmas become sulfide-saturated and segregate immiscible sulfide liquid, commonly following interaction with continental crustal rocks.

  8. Morphology and composition of gold in a lateritic profile, Fazenda Pison “Garimpo”, Amazon, Brazil

    Science.gov (United States)

    Larizzatti, J. H.; Oliveira, S. M. B.; Butt, C. R. M.

    2008-05-01

    This study describes the morphological evolution of gold grains in a lateritic weathering profile in an equatorial rainforest climate. Primary sources of gold are quartz veins associated with shallow granophyric intrusion. Gold grains were found in fresh ore, saprolite, transition zones, ferruginous duricrust, red latosol, and yellow latosol. Irregularly shaped grains predominate, with smaller proportions of dendritic and prismatic forms. Gold grains are weathered in the uppermost 10 m of the regolith. Mean gold grain size is maximum in the duricrust (>125 μm) and decreases progressively upward into the yellow latosol (duricrust formation may preserve some grains as large aggregates, but subsequent transformation into latosol further modifies them.

  9. Effect of hydrated lime on compressive strength mortar of fly ash laterite soil geopolymer mortar

    Science.gov (United States)

    Wangsa, F. A.; Tjaronge, M. W.; Djamaluddin, A. R.; Muhiddin, A. B.

    2017-11-01

    This paper explored the suitability of fly ash, hydrated lime, and laterite soil with several activator (sodium hydroxide and sodium tiosulfate) to produce geopolymer mortar. Furthermore, the heat that released by hydrated lime was used instead of oven curing. In order to produce geopolymer mortar without oven curing, three variations of curing condition has been applied. Based on the result, all the curing condition showed that the hardener mortar can be produced and exhibited the increasing of compressive strength of geopolymer mortar from 3 days to 7 days without oven curing.

  10. Improved removal of iodine-125 from effluents by the soil column method using a laterite soil

    Energy Technology Data Exchange (ETDEWEB)

    Sakuma, S H [Malaysian Inst. for Nuclear Technology Research, Bangi, Selangor (Malaysia)

    1997-02-01

    The soil column experiments were conducted to treat the liquid wastes from hospitals containing {sup 125}I. Three sorbent samples of laterite clay materials with different content of iron oxides (geothite, {alpha}-FeOOH) and hydroxides were used to sorb anionic iodate. Post-treatment of the liquid wastes with sodium hypochlorite (redox reagent) oxidized the iodide to the desirable iodate ion. pH after treatment ranges between 4.8 to 5.8 that is not very much different from the initial value pH4.5. The results show that 90 to 97% sorption of iodine with the decontamination factor between 10-32 could be obtained after the first two hours of experiments. The concentration has decreased from an initial value of 10 Bq{center_dot}mL{sup -1} to the concentration ranges 0.3 to 0.9 Bq{center_dot}mL{sup -1}. For the soil at pH between 4.5 to 6.0, positive charges predominated on the kaolinite, geothite and aluminum hydroxides. The negative {sup 125}I anions were electrostatically held by the positive charges on the mineral components of the laterite clay materials. The treated effluents could be released to the environment safely after further dilution and decay. The storage period will decrease tremendously providing better management for the disposal of the wastes by generators. The batch experiments conducted using different sorbent masses of soils, show that there was a drop in sorption where the mass of soils falls below approximately between 0 to 0.25 g. The sorption remains constant with the soil mass above 0.25 g. Another batch experiment using different concentration, shows that adsorption capacity of the laterite soil was 1.1 {mu}Ci/g. The adsorption is about 96% with a distribution coefficient of 1170. The experiments conducted show that anionic iodate in the liquid wastes can be removed by the laterite soil material. The column treatment method was more effective, easy to handle, and has low a capital and maintenance cost. (author). 9 refs, 10 figs, 2 tabs.

  11. Uranium isotope composition of a laterite profile during extreme weathering of basalt in Guangdong, South China

    Science.gov (United States)

    Huang, J.; Zhou, Z.; Gong, Y.; Lundstrom, C.; Huang, F.

    2015-12-01

    Rock weathering and soil formation in the critical zone are important for material cycle from the solid Earth to superficial system. Laterite is a major type of soil in South China forming at hot-humid climate, which has strong effect on the global uranium cycle. Uranium is closely related to the environmental redox condition because U is stable at U(Ⅳ) in anoxic condition and U(Ⅵ) as soluble uranyl ion (UO22+) under oxic circumstance. In order to understand the behavior of U isotopes during crust weathering, here we report uranium isotopic compositions of soil and base rock samples from a laterite profile originated from extreme weathering of basalt in Guangdong, South China. The uranium isotopic data were measured on a Nu Plasma MC-ICP-MS at the University of Illinois at Urbana-Champaign using the double spike method. The δ238U of BCR-1 is -0.29±0.03‰ (relative to the international standard CRM-112A), corresponding to a 238U/235U ratio of 137.911±0.004. Our result of BCR-1 agrees with previous analyses (e.g., -0.28‰ in Weyer et al. 2008) [1]. U contents of the laterite profile decrease from 1.9 ppm to 0.9 ppm with depth, and peak at 160 - 170 cm (2.3 ppm), much higher than the U content of base rocks (~0.5 ppm). In contrary, U/Th of laterites is lower than that of base rock (0.27) except the peak at the depth of 160-170 cm (0.38), indicating significant U loss during weathering. Notably, U isotope compositions of soils show a small variation from -0.38 to -0.28‰, consistent with the base rock within analytical error (0.05‰ to 0.08‰, 2sd). Such small variation can be explained by a "rind effect" (Wang et al., 2015) [2], by which U(Ⅳ) can be completely oxidized to U(VI) layer by layer during basalt weathering by dissolved oxygen. Therefore, our study indicates that U loss during basalt weathering at the hot-humid climate does not change U isotope composition of superficial water system. [1] Weyer S. et al. (2008) Natural fractionation of 238U/235

  12. Preparation of nickel and Ni_3Sn nanoparticles via extension of conventional citric acid and ethylene diamine tetraacetic acid mediated sol–gel method

    International Nuclear Information System (INIS)

    Li, Pingyun; Deng, Guodong; Guo, Xiaode; Liu, Hongying; Jiang, Wei; Li, Fengsheng

    2016-01-01

    This work aims to extend the application field of sol–gel process from conventional oxides, carbides, sulfides to metallic nanocrystalline materials. Metallic ions were coordinated with chelating agents of citric acid (CA) and ethylene diamine tetraacetic acid (EDTA) in aqueous solution. Then the solutions were dried at 383 K, resulting in the formation of sol and gel. Heating treatments of dried gels were then carried out with protection of N_2 atmosphere. Ni and Ni_3Sn alloy nanoparticles were obtained by this sol–gel method in the range of 623–823 K. The as-prepared Ni and Ni_3Sn alloy nanoparticles have average grain sizes of 15 and 30 nm, and have face-centred-cubic (fcc) crystalline phase. Our results provide new insight into the application of conventional sol–gel method. - Graphical abstract: Sol–gel method is conventionally applied to prepare oxides, carbides, and sulfides. In this work, the application field of sol–gel method is extended to metallic nanoparticles. By using citric acid (CA) and ethylene diamine tetraacetic acid (EDTA) mediated sol–gel method, metallic Ni (a and c) and Ni_3Sn (b and d) alloy nanoparticles can be prepared when the heating treatments are performed under N_2 protecting atmosphere. The Ni and Ni_3Sn nanoparticles have face-centered-cubic (fcc) crystalline phase and ultrafine grain sizes. Diffraction peaks of (110) superstructure reflection plane of Ni_3Sn nanoparticles can also be observed in Figure b, which can be considered as direct evidence of formation of alloy crystalline phase by performing this sol–gel method. - Highlights: • Ni and Ni_3Sn alloy nanoparticles have been prepared by sol–gel processes. • Citric acid and ethylene diamine tetraacetic acid were applied as chelating agent. • Diffraction peak of superstructure reflection plane of Ni_3Sn was detected by XRD. • A novel strategy for preparation of alloy nanoparticles has been presented.

  13. Gold nanoparticle/nickel oxide/poly(pyrrole-N-propionic acid hybrid multilayer film: Electrochemical study and its application in biosensing

    Directory of Open Access Journals (Sweden)

    T. Karazehir

    2017-06-01

    Full Text Available The present study describes the fabrication of Indium Tin Oxide /gold nanoparticles/nickel oxide/poly(Pyrrole-N-propionic acid (ITO/GNPs/NiO/poly(PPA multilayered film, and its modification with Tyrosinase (Ty. The ITO/GNPs/NiO/poly(PPA electrode was fabricated by sequential electrochemical assembly onto ITO substrate which electrochemical deposition provides a facile, inexpensive technique for synthesis of multilayered film within the adherent morphology with controllable film thickness. Cyclic voltammetry (CV, Fourier transform infrared spectroscopy-attenuated total reflectance (FTIR-ATR, scanning electron microcopy (SEM, and atomic force microcopy (AFM were used to characterize the film assembly processes. The properties of a semiconductor/electrolyte interface were investigated based on the Mott–Schottky (M-S approach for the modified electrodes, with the flat band potential (EFB according to the potential intercept and the carrier density (ND according to the linear slopes. The ND and EFB of ITO/GNPs/NiO/poly(PPA were obtained as 2.48·1021 cm–3 and 0.26 V, respectively. Tyrosinase was immobilized using carbodiimide coupling reaction. The bioelectrode was characterized by FTIR-ATR, SEM, AFM, electrochemical impedance spectroscopy (EIS. A Randles equivalent circuit was introduced for modeling the performance of impedimetric biosensing for the detection of the dopamine (DP and the interface of bioelectrode/electrolyte. The EIS of the ITO/GNPs/NiO/poly(PPA-Ty exhibited significant changes in the charge transfer resistance (RCT value toward the detection of dopamine over a linear range of 80 µM to 0.2 mM with a limit of detection (LOD of 5.46 µM.

  14. NICKEL PLATING PROCESS

    Science.gov (United States)

    Hoover, T.B.; Zava, T.E.

    1959-05-12

    A simplified process is presented for plating nickel by the vapor decomposition of nickel carbonyl. In a preferred form of the invention a solid surface is nickel plated by subjecting the surface to contact with a mixture containing by volume approximately 20% nickel carbonyl vapor, 2% hydrogen sulfide and .l% water vapor or 1% oxygen and the remainder carbon dioxide at room temperature until the desired thickness of nickel is obtained. The advantage of this composition over others is that the normally explosive nickel carbonyl is greatly stabilized.

  15. EFFECTS OF COMPACTIVE EFFORTS ON GEOTECHNICAL PROPERTIES OF SPENT ENGINE OIL CONTAMINATED LATERITE SOIL

    Directory of Open Access Journals (Sweden)

    OLUREMI, J. ROTIMI

    2017-03-01

    Full Text Available Investigation of the effects of compactive efforts and spent engine oil (SEO contamination on the geotechnical properties of lateritic soils was made. Contaminated specimens were prepared by mixing lateritic soil with up to 10 % SEO by dry weight of the soil in step concentration of 2 % and subjected to geotechnical tests. Results indicated a decrease in the fine content, decrease in liquid limit, maximum dry density (MDD and unconfined compressive strength (UCS with up to 10 % SEO content. No general trend was observed in the optimum moisture content (OMC with increasing SEO content. The MDD, OMC and UCS values increased with increase in the compactive effort. Regression analysis of the results showed that optimum moisture content, fine content and compactive effort significantly influence the soils UCS values. Analysis of variance showed that SEO and compactive effort has significant effect on the parameters with the exception in one case. The results of laboratory tests showed that geotechnical properties of the SEO contaminated soil were immensely impaired.

  16. Effects of Palm Kernel Shell Ash on Lime-Stabilized Lateritic Soil

    Science.gov (United States)

    Nnochiri, Emeka Segun; Ogundipe, Olumide M.; Oluwatuyi, Opeyemi E.

    2017-09-01

    The research investigated the effects of palm kernel shell ash (PKSA) on lime-stabilized lateritic soil. Preliminary tests were performed on three soil samples, i.e., L1, L2 and L3 for identification; the results showed that L1 was A-7-6, L2 was A-7-6, and L3 was A-7-6. The optimum amount of lime for each of the soil samples was achieved. The optimum amount for L1 was 10%, for L2, 8% and for L3, 10%; at these values they recorded the lowest plasticity indexes. The further addition of PKSA was performed by varying the amount of PKSA and lime added to each of the soil samples. The addition of 4% PKSA+ 6% lime, the addition of 4% PKSA + 4% lime, and the addition of 4% PKSA + 6% lime increased the California Bearing Ratio (CBR) to the highest values for L1, L2 and L3 from 8.20%. It was concluded that PKSA can be a suitable complement for lime stabilization in lateritic soil.

  17. Effects of Density and Moisture Variation on Dynamic Deformation Properties of Compacted Lateritic Soil

    Directory of Open Access Journals (Sweden)

    Weizheng Liu

    2016-01-01

    Full Text Available A series of repeated load triaxial tests were conducted in this study to investigate the influences of compaction density and postcompaction moisture variation on the dynamic elastic modulus (Ed and plastic permanent strain (PPS of compacted lateritic soil. Specimens were compacted at optimum moisture content (OMC and three degrees of compaction (90%, 93%, and 96%. Then the specimens were dried or wetted to different moisture contents (OMC, OMC±3%, OMC±6%, and OMC+9% prior to testing for Ed and PPS. Results show that moisture content has greater influence on the Ed and PSS than compaction degree, and the increase in moisture content leads to a decrease of Ed and an increase of PPS. Furthermore, an empirical relationship between Ed and applied cyclic stress (σd is developed that incorporates density and moisture variations. Three different evolution types of PPS with number of load cycles, plastic stable, plastic creep, and incremental collapse, are identified as the increase of moisture content. In addition, the critical dynamic stress (σdc separating stable and unstable deformation is determined based on the shakedown concept. The envelope curves of σdc-moisture of lateritic soil with different degrees of compaction are also determined to provide reference for the pavement design.

  18. Strength Performance Based on Flexibility from Laterite Soil Using Tire Powder and Micro Silica

    Directory of Open Access Journals (Sweden)

    Behrouz Gordan

    2015-01-01

    Full Text Available In terms of environmental issues and human health, one of the advisable techniques to improve soil behavior is the use of scrap tires for soil structures. According to the literature, Tire-Derived Aggregates (TDA are one of the valuable materials in different field of Geotechnical that can be used. TDA properties correspond to some important factors such as high level of flexible, lightweight, high permeability and economic material comparing with sand. Strength performance based on increasing flexibility from laterite soil is the main goal of this study. For this purpose, tropical laterite soil was mixed using TDA and micro silica (MS. As a research method, unconfined tests were carried for thirteen samples based on different percentage of the additives. As a result, the significant reduction for elasticity modulus and strength was observed when soil mixed just using TDA. In addition, the rate of strain at the peak of the curve was dramatically increased. The best performance was found using 6% additives when the ratio was 3% MS and 3% TDA. In fact, the effect of MS was more to increase strength. To recommend, the seepage controlling will investigate at next.

  19. The removal of fluoride from aqueous solution by a lateritic soil adsorption: Kinetic and equilibrium studies.

    Science.gov (United States)

    Iriel, Analia; Bruneel, Stijn P; Schenone, Nahuel; Cirelli, Alicia Fernández

    2018-03-01

    The use of natural sorbents to remove fluoride from drinking water is a promising alternative because of its low-cost and easy implementation. In this article, fluoride adsorption on a latosol soil from Misiones province (Argentina) was studied regarding kinetic and equilibrium aspects. Experiments were conducted in batch at room temperature under controlled conditions of pH 4-8) and ionic strength (1-10mM KNO 3 ). Experimental data indicated that adsorption processes followed a PSO kinetic where initial rates have showed to be influenced by pH solution. The necessary time to reach an equilibrium state had resulted approximately 30min. Equilibrium adsorption studies were performed at pH 8 which is similar to the natural groundwater. For that, fluoride adsorption data were successfully adjusted to Dubinin-Ataskhov model determining that the fluoride adsorption onto soil particles mainly followed a physical mechanism with a removal capacity of 0.48mgg -1 . Finally, a natural groundwater was tested with laterite obtaining a reduction close to 30% from initial concentration and without changing significantly the physicochemical properties of the natural water. Therefore, it was concluded that the use of lateritic soils for fluoride removal is very promising on a domestic scale. Copyright © 2017 Elsevier Inc. All rights reserved.

  20. Acidic leaching of potentially toxic metals cadmium, cobalt, chromium, copper, nickel, lead, and zinc from two Zn smelting slag materials incubated in an acidic soil.

    Science.gov (United States)

    Liu, Taoze; Li, Feili; Jin, Zhisheng; Yang, Yuangen

    2018-07-01

    A column leaching study, coupled with acid deposition simulation, was conducted to investigate the leaching of potentially toxic metals (PTM) from zinc smelting slag materials (SSM) after being incubated in an acid Alfisol for 120 days at room temperature. Two SSMs (SSM-A: acidic, 10 yrs exposure with moderate high PTM concentrations versus SSM-B: alkaline, 2 yrs exposure with extremely high PTM concentrations), were used for the incubation at 0.5, 1, 2.5, 5 wt% amendment ratios in triplicate. Five leaching events were conducted at day 1, 3, 7, 14, and 28, and the leaching of PTMs mainly occurred in the first three leaching events, with the highest PTM concentrations in leachate measured from 5 wt% SSM amendments. After leaching, 2.5, 12, 5.5, 14, 11, and 9 wt% of M3 extractable Pb, Zn, Cd, Co, Cr, and Ni could be released from 5 wt% SSM-A amended soils, being respectively 25, 12, 4, 2, 2, and 2 times more than those from 5 wt% SSM-B amended soils. In the leachates, the concentrations of PTMs were mostly affected by leachant pH and were closely correlated to the concentrations of Fe, Al, Ca, Mg and P with Cd, Pb, and Zn showing the most environmental concern. Visual MINTEQ 3.1 modeling suggested metallic ions and sulfate forms as the common chemical species of PTMs in the leachates; whereas, organic bound species showed importance for Cd, Pb, Cu, and Ni, and CdCl + was observed for Cd. Aluminum hydroxy, phosphate, and sulfate minerals prevailed as the saturated minerals, followed by chloropyromorphite (Pb 5 (PO 4 ) 3 Cl) and plumbogummite (PbAl 3 (PO 4 ) 2 (OH) 5 ·H 2 O) in the leachates. This study suggested that incubation of SSMs in acidic soil for a long term can enhance the release of PTMs as the forms of metallic ions and sulfate when subjected to acid deposition leaching. Copyright © 2018 Elsevier Ltd. All rights reserved.

  1. Urine nickel concentrations in nickel-exposed workers.

    Science.gov (United States)

    Bernacki, E J; Parsons, G E; Roy, B R; Mikac-Devic, M; Kennedy, C D; Sunderman, F W

    1978-01-01

    Electrothermal atomic absorption spectrometry was employed for analyses of nickel concentrations in urine samples from nickel-exposed workers in 10 occupational groups and from non-exposed workers in two control groups. Mean concentrations of nickel in urine were greatest in workers who were exposed to inhalation of aerosols of soluble nickel salts (e.g., workers in nickel plating operations and in an electrolytic nickel refinery). Less marked increases in urine nickel concentrations were found in groups of metal sprayers, nickel battery workers, bench mechanics and are welders. No significant increases in mean concentrations of nickel were found in urine samples from workers who performed grinding, buffing and polishing of nickel-containing alloys or workers in a coal gasification plant who employed Raney nickel as a hydrogenation catalyst. Measurements of nickel concentrations in urine are more sensitive and practical than measurements of serum nickel concentrations for evaluation of nickel exposures in industrial workers.

  2. A 2D nickel-based energetic MOFs incorporating 3,5-diamino-1,2,4-triazole and malonic acid: Synthesis, crystal structure and thermochemical study

    International Nuclear Information System (INIS)

    Yang, Qi; Song, Xiaxia; Ge, Jing; Zhao, Guowei; Zhang, Wendou; Xie, Gang; Chen, Sanping; Gao, Shengli

    2016-01-01

    Highlights: • An energetic MOFs with dinuclear nickel unit has been synthesized and characterized. • The Arrhenius equation, derived from kinetics analysis, is ln k = 55.89 − 332.01 × 10 3 /RT. • The standard molar enthalpy of formation of the compound is determined by a thermochemical cycle. • The molar heat capacity at T = 298.15 K is determined to be 1.42 ± 0.11 J · K −1 · g −1 . - Abstract: A new energetic MOFs, {[Ni 2 (C 2 H 5 N 5 ) 2 (C 3 H 2 O 4 ) 2 (H 2 O)]·3H 2 O} n (Hdatrz (C 2 H 5 N 5 ) = 3,5-diamino-1,2,4-triazole, H 2 mal (C 3 H 4 O 4 ) = malonic acid), has been synthesized and characterized by element analysis, chemical analysis, IR spectroscopy, single-crystal X-ray diffraction and thermal analysis. X-ray diffraction analysis confirmed that the compound featured a 2D layer structure with dinuclear Ni(II) unit. Thermal analysis demonstrated that the compound after dehydration have good thermostability with decomposition temperature up to 633 K. The non-isothermal kinetics for the compound was studied by Kissinger’s and Ozawa’s methods. The Arrhenius equation of initial thermal decomposition process of compound can be expressed as ln k = 55.89 − 332.01 × 10 3 /RT. Furthermore, a reasonable thermochemical cycle was designed based on the preparation reaction of the compound, and standard molar enthalpy of dissolution of reactants and products were measured by RD496-2000 calorimeter. Finally, the standard molar enthalpy of formation of the compound was determined to be −(2766.3 ± 2.3) kJ · mol −1 in accordance with Hess’s law. In addition, the specific heat capacity of the compound at T = 298.15 K was determined to be 1.42 ± 0.11 J · K −1 · g −1 by RD496-2000 calorimeter.

  3. Strontium isotopes reveal weathering processes in lateritic covers in southern China with implications for paleogeographic reconstructions

    Science.gov (United States)

    Wei, Xiao; Wang, Shijie; Ji, Hongbing; Shi, Zhenhua

    2018-01-01

    The isotope ratios of Sr are useful tracers for studying parent material sources, weathering processes, and biogeochemical cycling. Mineralogical and geochemical investigations of two lateritic weathering covers, in an area close to the Tropic of Cancer (Guangxi Province, southern China), were undertaken to study the regional weathering processes and Sr isotopic sources. We found that weathering and decomposition of Rb- and Sr-bearing minerals change the Sr isotopic composition in weathering products (lateritic soils). Weathering of illite lowered the 87Sr/86Sr ratio whereas dissolving and leaching of carbonate minerals increased the 87Sr/86Sr ratio. An Fe nodular horizon is widely developed on the top of the weathering covers in the studied area and it differs from the lateritic soil horizon in mineral composition, construction, and elemental concentration. Furthermore, both Fe2O3 and P2O5 (concentrations) are negatively correlated with the 87Sr/86Sr ratios, suggesting fixation of apatite by Fe oxides is a controlling factor of the Sr isotopic composition in the Fe nodular horizon. The 87Sr/86Sr and Nb/Sr ratios imply the contents and proportions of Fe nodules and clay are critical in controlling the changes of Sr isotopic composition in the Fe nodular horizon. The two stages of the weathering process of carbonate rocks are revealed by the87Sr/86Sr versus Nb/Sr diagram. The 87Sr/86Sr and Rb/Sr ratios suggest that Sr isotopes in the weathering covers within the studied area are derived mainly from parent rock weathering and that the contributions from allothogenic Sr isotopes are limited. A comparison of Sr isotopic composition signatures in the weathering covers of the studied area and Guizhou Province provided insight into the Sr isotopic source and paleogeographic evolution of southern China. From the Permian to the Triassic, the continental fragment sources of the South China sedimentary basin changed significantly. In the Permian, Southern China presented the

  4. Clay mineral facies and lateritization in basalts of the southeastern Parana Basin, Brazil

    International Nuclear Information System (INIS)

    Oliveira, M.T.G. de; Formoso, M.L.L.; Trescases, J.J.; Meunier, A.

    1998-01-01

    Seventeen samples from two lateritic profiles, each with five facies, were studied. These profiles occur on the old planation surface of the plateau basalts of the southern part of ParanáBasin, Brazil. Optical microscopy, X-ray diffraction, electron microprobe, Mössbauer spectroscopy and Fourier Transform Infrared Spectra were used to obtain information about the nature and chemical composition of each weathering facies. In addition, scanning electron microscopy and analyses of clay minerals were performed to detect microcrystalline environmental changes. Both profiles have two major parts: a loose red-clay latosol separated from an underlying mottled clay and an alterite facies; a stone line may or may not be present between the latosol and the underlying units. In both profiles the latosol consists principally of kaolinite, hematite and goethite. Two alterite facies, shaped by differential weathering, are also present in the lower profile: a halloysite–nontronite clayey matrix with a well developed fissure system occurs in the argillaceous alterite and a network of Al–goethite aggregates is typical of the highly porous cortex of the boulder alterite that is found in the stone line and below it. Gibbsite has crystallized in the large pores of porphyritic boulder alterite but is absent in the small pores of the subaphyric boulder alterite. Clay minerals observed in fissures include halloysite associated with goethite and manganese oxides. The basalt has hydrothermal green-clays (mixed layers and trioctahedral smectites) that formed between primary plagioclase, pyroxene and Ti–magnetite crystals while fresh corestones of the boulder alterite have cryptocrystalline iron-rich material. The study of these profiles shows one principal evolutionary trend for clay minerals. This trend is from smectite and mixed layers that form green clays in altered bedrock at the base of the profile to an intermediate association of nontronite and halloysite in the argillaceous

  5. Strontium isotopes reveal weathering processes in lateritic covers in southern China with implications for paleogeographic reconstructions.

    Directory of Open Access Journals (Sweden)

    Xiao Wei

    Full Text Available The isotope ratios of Sr are useful tracers for studying parent material sources, weathering processes, and biogeochemical cycling. Mineralogical and geochemical investigations of two lateritic weathering covers, in an area close to the Tropic of Cancer (Guangxi Province, southern China, were undertaken to study the regional weathering processes and Sr isotopic sources. We found that weathering and decomposition of Rb- and Sr-bearing minerals change the Sr isotopic composition in weathering products (lateritic soils. Weathering of illite lowered the 87Sr/86Sr ratio whereas dissolving and leaching of carbonate minerals increased the 87Sr/86Sr ratio. An Fe nodular horizon is widely developed on the top of the weathering covers in the studied area and it differs from the lateritic soil horizon in mineral composition, construction, and elemental concentration. Furthermore, both Fe2O3 and P2O5 (concentrations are negatively correlated with the 87Sr/86Sr ratios, suggesting fixation of apatite by Fe oxides is a controlling factor of the Sr isotopic composition in the Fe nodular horizon. The 87Sr/86Sr and Nb/Sr ratios imply the contents and proportions of Fe nodules and clay are critical in controlling the changes of Sr isotopic composition in the Fe nodular horizon. The two stages of the weathering process of carbonate rocks are revealed by the87Sr/86Sr versus Nb/Sr diagram. The 87Sr/86Sr and Rb/Sr ratios suggest that Sr isotopes in the weathering covers within the studied area are derived mainly from parent rock weathering and that the contributions from allothogenic Sr isotopes are limited. A comparison of Sr isotopic composition signatures in the weathering covers of the studied area and Guizhou Province provided insight into the Sr isotopic source and paleogeographic evolution of southern China. From the Permian to the Triassic, the continental fragment sources of the South China sedimentary basin changed significantly. In the Permian, Southern

  6. Partition of rare-earths in phosphates laterites from Maicuru, Brazil - PA

    International Nuclear Information System (INIS)

    Lemos, V.P.; Costa, M.L. da.

    1987-01-01

    The phosphatic laterites of Maicuru-Para are formed of aluminium phosphates, mainly of the crandallite group, followed by wardite, augellite and senegallite. The crandallite group is represented in the form of the solid solution goyazite-florencite-crandallite, in variable proportions. In three samples, the florencite occurs as the predominant member, while in the others crandallite is the main mineral. The unit-cell dimension of florencites, in two samples, measured are the same as those of the florencites from other deposits. The rare earths occur mainly in this mineral group with predominance of the light rare earth elements. This is well observed in the condrite normalized REE patterns. These enrichments are not regular. The geochemical characteristics of the rare earth distribution in the crandallites of Maicuru, leads tho suggest this mineral was formed from distinct lithologies. (author) [pt

  7. Effects of Rice Husk Ash on Some Geotechnical Properties of Lateritic Soil

    Directory of Open Access Journals (Sweden)

    Fidelis O. OKAFOR

    2009-12-01

    Full Text Available The study is an investigation into the effect of RHA on some geotechnical properties of a lateritic soil classified as A-2-6 (0 or SW for sub-grade purposes. The investigation includes evaluation of properties such as compaction, consistency limits and strength of the soil with RHA content of 5%, 7.5%, 10% and 12.5% by weight of the dry soil. The results obtained show that the increase in RHA content increased the OMC but decreased the MDD. It was also discovered that increase in RHA content, reduced plasticity and increased volume stability as well as the strength of the soil. 10% RHA content was also observed to be the optimum content.

  8. Existing Versus Added Soil Organic Matter in Relation to Phosphorus Availability on Lateritic Soils

    Directory of Open Access Journals (Sweden)

    Fadly Hairannoor Yusran

    2008-01-01

    Full Text Available Lateritic soils (Ultisols and Oxisols are commonly characterised by high phosphate sorbing capacity due to the type of clay and present high content of aluminium (Al and iron (Fe oxides. Addition of fresh organic matter (OM may contribute to management of these soils by releasing more bicarbonate-extractable phosphorus (BP through organic phosphorus (OP transformation, or by the soluble component of OM additions desorbing phosphate by ligand exchange. It is not known, however, whether BP results solely from addition of new OM (by either mineralisation or desorption or from transformation of inherent or pre-existing in soil. We considered that removing the existing soil OM and replacing it with an equivalent amount of new OM may help to resolve this issue, especially with respect to P transformation after OM additions. Three lateritic soils of Western Australia (including a deep regolith material with very low inherent soil OM (SOM were used, and sub-samples of the three soils were combusted (450° C to obtain soils effectively free from existing OM. A further sub-sample of the soils was not combusted. Both soil groups, receiving the same amount of organic carbon (OC, from 80 ton ha-1 biomass + soil OM or biomass equal to soil OM from peat, wheat straw (Triticum aestivum L. and lucerne hay (Medicago sativa L., were incubated for nine months. Soil bicarbonate-extractable P as well as non-extractable P (NP, measured as Total-P (TP-BP increased due to new OM application in the order lucerne hay>peat>wheat straw. The correlation between BP with soil organic carbon (SOC became more positive over time. Microbial biomass phosphorus (MBP was not well correlated with the increase of NP content and phosphatase was not related to the increase in BP. Overall, freshly applied (new OM not only contributed to the increased level of P compared with the existing OM treatment.

  9. Modeling thermal performance of exterior walls retrofitted from insulation and modified laterite based bricks materials

    Science.gov (United States)

    Wati, Elvis; Meukam, Pierre; Damfeu, Jean Claude

    2017-12-01

    Uninsulated concrete block walls commonly found in tropical region have to be retrofitted to save energy. The thickness of insulation layer used can be reduced with the help of modified laterite based bricks layer (with the considerably lower thermal conductivity than that of concrete block layer) during the retrofit building fabrics. The aim of this study is to determine the optimum location and distribution of different materials. The investigation is carried out under steady periodic conditions under the climatic conditions of Garoua in Cameroon using a Simulink model constructed from H-Tools (the library of Simulink models). Results showed that for the continuous air-conditioned space, the best wall configuration from the maximum time lag, minimum decrement factor and peak cooling transmission load perspective, is dividing the insulation layer into two layers and placing one at the exterior surface and the other layer between the two different massive layers with the modified laterite based bricks layer at the interior surface. For intermittent cooling space, the best wall configuration from the minimum energy consumption depends on total insulation thickness. For the total insulation thickness less than 8 cm approximately, the best wall configuration is placing the half layer of insulation material at the interior surface and the other half between the two different massive layers with the modified earthen material at the exterior surface. Results also showed that, the optimum insulation thickness calculated from the yearly cooling transmission (estimated only during the occupied period) and some economic considerations slightly depends on the location of that insulation.

  10. Hydrogeologic and hydraulic characterization of aquifer and nonaquifer layers in a lateritic terrain (West Bengal, India)

    Science.gov (United States)

    Biswal, Sabinaya; Jha, Madan K.; Sharma, Shashi P.

    2018-02-01

    The hydrogeologic and hydraulic characteristics of a lateritic terrain in West Bengal, India, were investigated. Test drilling was conducted at ten sites and grain-size distribution curves (GSDCs) were prepared for 275 geologic samples. Performance evaluation of eight grain-size-analysis (GSA) methods was carried out to estimate the hydraulic conductivity (K) of subsurface formations. Finally, the GSA results were validated against pumping-test data. The GSDCs indicated that shallow aquifer layers are coarser than the deeper aquifer layers (uniformity coefficient 0.19-11.4). Stratigraphy analysis revealed that both shallow and deep aquifers of varying thickness exist at depths 9-40 and 40-79 m, respectively. The mean K estimates by the GSA methods are 3.62-292.86 m/day for shallow aquifer layers and 0.97-209.93 m/day for the deeper aquifer layers, suggesting significant aquifer heterogeneity. Pumping-test data indicated that the deeper aquifers are leaky confined with transmissivity 122.69-693.79 m2/day, storage coefficient 1.01 × 10-7-2.13 × 10-4 and leakance 2.01 × 10-7-34.56 × 10-2 day-1. Although the K values yielded by the GSA methods are generally larger than those obtained from the pumping tests, the Slichter, Harleman and US Bureau Reclamation (USBR) GSA methods yielded reasonable values at most of the sites (1-3 times higher than K estimates by the pumping-test method). In conclusion, more reliable aquifers exist at deeper depths that can be tapped for dependable water supply. GSA methods such as Slichter, Harleman and USBR can be used for the preliminary assessment of K in lateritic terrains in the absence of reliable field methods.

  11. II. Electrodeposition/removal of nickel in a spouted electrochemical reactor.

    Science.gov (United States)

    Grimshaw, Pengpeng; Calo, Joseph M; Shirvanian, Pezhman A; Hradil, George

    2011-08-17

    An investigation is presented of nickel electrodeposition from acidic solutions in a cylindrical spouted electrochemical reactor. The effects of solution pH, temperature, and applied current on nickel removal/recovery rate, current efficiency, and corrosion rate of deposited nickel on the cathodic particles were explored under galvanostatic operation. Nitrogen sparging was used to decrease the dissolved oxygen concentration in the electrolyte in order to reduce the nickel corrosion rate, thereby increasing the nickel electrowinning rate and current efficiency. A numerical model of electrodeposition, including corrosion and mass transfer in the particulate cathode moving bed, is presented that describes the behavior of the experimental net nickel electrodeposition data quite well.

  12. Dissolution studies on Nickel ferrite in dilute chemical decontamination formulations

    Energy Technology Data Exchange (ETDEWEB)

    Ranganathan, S. [New Brunswick Univ., Fredericton, NB (Canada). Dept. of Chemical Engineering; Srinivasan, M.P. [Bhabha Atomic Research Centre (BARC) (India). Water and Steam Chemistry Laboratory; Raghavan, P.S. [Madras Christian College, Chennai (India); Narasimhan, S.V. [Bhabha Atomic Research Centre, Bombay (India); Gopalan, R. [Madras Christian College, Chennai (India). Department of Chemistry

    2004-09-01

    Nickel ferrite is one of the important corrosion products in the pipeline surfaces of water-cooled nuclear reactors. The dissolution of the nickel ferrite by chelating agents is very sensitive to the nature of the chelant, the nature of the reductant used in the formulation and the temperature at which the dissolution studies are performed. The dissolution is mainly controlled by the reductive dissolution of the ferrite particles, but complexing agents also play a significant role in the dissolution process. This study deals with the leaching of iron and nickel from nickel ferrite prepared by the solid-state method. The dissolution studies are performed in pyridine-2,6-dicarboxylic acid (PDCA), nitrilotriacetic acid (NTA), and ethylenediaminetetraacetic acid (EDTA) formulations containing organic reductants like ascorbic acid and low oxidation state transition metal ion reductants like Fe(II)-L (where L = PDCA, NTA, EDTA) at 85 C. The dissolution of nickel ferrite in PDCA, NTA and EDTA formulations is influenced by the presence of reductants in the formulations. The addition of Fe(II)-L in the formulation greatly enhances the dissolution of nickel ferrite. The preferential leaching of nickel over iron during the dissolution of nickel ferrite was observed in all the formulations. (orig.)

  13. Dissolution studies on Nickel ferrite in dilute chemical decontamination formulations

    International Nuclear Information System (INIS)

    Ranganathan, S.; Narasimhan, S.V.; Gopalan, R.

    2004-01-01

    Nickel ferrite is one of the important corrosion products in the pipeline surfaces of water-cooled nuclear reactors. The dissolution of the nickel ferrite by chelating agents is very sensitive to the nature of the chelant, the nature of the reductant used in the formulation and the temperature at which the dissolution studies are performed. The dissolution is mainly controlled by the reductive dissolution of the ferrite particles, but complexing agents also play a significant role in the dissolution process. This study deals with the leaching of iron and nickel from nickel ferrite prepared by the solid-state method. The dissolution studies are performed in pyridine-2,6-dicarboxylic acid (PDCA), nitrilotriacetic acid (NTA), and ethylenediaminetetraacetic acid (EDTA) formulations containing organic reductants like ascorbic acid and low oxidation state transition metal ion reductants like Fe(II)-L (where L = PDCA, NTA, EDTA) at 85 C. The dissolution of nickel ferrite in PDCA, NTA and EDTA formulations is influenced by the presence of reductants in the formulations. The addition of Fe(II)-L in the formulation greatly enhances the dissolution of nickel ferrite. The preferential leaching of nickel over iron during the dissolution of nickel ferrite was observed in all the formulations. (orig.)

  14. Kinetics of oxidation of nickel(II) aza macrocycles by ...

    Indian Academy of Sciences (India)

    The kinetics of the oxidation of nickel (II) hexaaza and nickel (II) pentaaza macrocycles by the peroxydisulphate anion, S2O8 2-, were studied in aqueous media. Effect of H on reaction rate was also studied. The rate increases with increase of S2OO8 2- concentration. Rates are almost independent of acid between H 4 ...

  15. II. Electrodeposition/removal of nickel in a spouted electrochemical reactor

    OpenAIRE

    Grimshaw, Pengpeng; Calo, Joseph M.; Shirvanian, Pezhman A.; Hradil, George

    2011-01-01

    An investigation is presented of nickel electrodeposition from acidic solutions in a cylindrical spouted electrochemical reactor. The effects of solution pH, temperature, and applied current on nickel removal/recovery rate, current efficiency, and corrosion rate of deposited nickel on the cathodic particles were explored under galvanostatic operation. Nitrogen sparging was used to decrease the dissolved oxygen concentration in the electrolyte in order to reduce the nickel corrosion rate, ther...

  16. Chemoorganotrophic Bioleaching of Olivine for Nickel Recovery

    Directory of Open Access Journals (Sweden)

    Yi Wai Chiang

    2014-06-01

    Full Text Available Bioleaching of olivine, a natural nickel-containing magnesium-iron-silicate, was conducted by applying chemoorganotrophic bacteria and fungi. The tested fungus, Aspergillus niger, leached substantially more nickel from olivine than the tested bacterium, Paenibacillus mucilaginosus. Aspergillus niger also outperformed two other fungal species: Humicola grisae and Penicillium chrysogenum. Contrary to traditional acid leaching, the microorganisms leached nickel preferentially over magnesium and iron. An average selectivity factor of 2.2 was achieved for nickel compared to iron. The impact of ultrasonic conditioning on bioleaching was also tested, and it was found to substantially increase nickel extraction by A. niger. This is credited to an enhancement in the fungal growth rate, to the promotion of particle degradation, and to the detachment of the stagnant biofilm around the particles. Furthermore, ultrasonic conditioning enhanced the selectivity of A. niger for nickel over iron to a value of 3.5. Pre-carbonating the olivine mineral, to enhance mineral liberation and change metal speciation, was also attempted, but did not result in improvement as a consequence of the mild pH of chemoorganotrophic bioleaching.

  17. Contaminated nickel scrap processing

    International Nuclear Information System (INIS)

    Compere, A.L.; Griffith, W.L.; Hayden, H.W.; Johnson, J.S. Jr.; Wilson, D.F.

    1994-12-01

    The DOE will soon choose between treating contaminated nickel scrap as a legacy waste and developing high-volume nickel decontamination processes. In addition to reducing the volume of legacy wastes, a decontamination process could make 200,000 tons of this strategic metal available for domestic use. Contaminants in DOE nickel scrap include 234 Th, 234 Pa, 137 Cs, 239 Pu (trace), 60 Co, U, 99 Tc, and 237 Np (trace). This report reviews several industrial-scale processes -- electrorefining, electrowinning, vapormetallurgy, and leaching -- used for the purification of nickel. Conventional nickel electrolysis processes are particularly attractive because they use side-stream purification of process solutions to improve the purity of nickel metal. Additionally, nickel purification by electrolysis is effective in a variety of electrolyte systems, including sulfate, chloride, and nitrate. Conventional electrorefining processes typically use a mixed electrolyte which includes sulfate, chloride, and borate. The use of an electrorefining or electrowinning system for scrap nickel recovery could be combined effectively with a variety of processes, including cementation, solvent extraction, ion exchange, complex-formation, and surface sorption, developed for uranium and transuranic purification. Selected processes were reviewed and evaluated for use in nickel side-stream purification. 80 refs

  18. Contaminated nickel scrap processing

    Energy Technology Data Exchange (ETDEWEB)

    Compere, A.L.; Griffith, W.L.; Hayden, H.W.; Johnson, J.S. Jr.; Wilson, D.F.

    1994-12-01

    The DOE will soon choose between treating contaminated nickel scrap as a legacy waste and developing high-volume nickel decontamination processes. In addition to reducing the volume of legacy wastes, a decontamination process could make 200,000 tons of this strategic metal available for domestic use. Contaminants in DOE nickel scrap include {sup 234}Th, {sup 234}Pa, {sup 137}Cs, {sup 239}Pu (trace), {sup 60}Co, U, {sup 99}Tc, and {sup 237}Np (trace). This report reviews several industrial-scale processes -- electrorefining, electrowinning, vapormetallurgy, and leaching -- used for the purification of nickel. Conventional nickel electrolysis processes are particularly attractive because they use side-stream purification of process solutions to improve the purity of nickel metal. Additionally, nickel purification by electrolysis is effective in a variety of electrolyte systems, including sulfate, chloride, and nitrate. Conventional electrorefining processes typically use a mixed electrolyte which includes sulfate, chloride, and borate. The use of an electrorefining or electrowinning system for scrap nickel recovery could be combined effectively with a variety of processes, including cementation, solvent extraction, ion exchange, complex-formation, and surface sorption, developed for uranium and transuranic purification. Selected processes were reviewed and evaluated for use in nickel side-stream purification. 80 refs.

  19. Evaluation of Digital Classification of Polarimetric SAR Data for Iron-Mineralized Laterites Mapping in the Amazon Region

    Directory of Open Access Journals (Sweden)

    Cleber G. Oliveira

    2013-06-01

    Full Text Available This study evaluates the potential of C- and L-band polarimetric SAR data for the discrimination of iron-mineralized laterites in the Brazilian Amazon region. The study area is the N1 plateau located on the northern border of the Carajás Mineral Province, the most important Brazilian mineral province which has numerous mineral deposits, particularly the world’s largest iron deposits. The plateau is covered by low-density savanna-type vegetation (campus rupestres which contrasts visibly with the dense equatorial forest. The laterites are subdivided into three units: chemical crust, iron-ore duricrust, and hematite, of which only the latter two are of economic interest. Full polarimetric data from the airborne R99B sensor of the SIVAM/CENSIPAM (L-band system and the RADARSAT-2 satellite (C-band were evaluated. The study focused on an assessment of distinct schemes for digital classification based on decomposition theory and hybrid approach, which incorporates statistical analysis as input data derived from the target decomposition modeling. The results indicated that the polarimetric classifications presented a poor performance, with global Kappa values below 0.20. The accuracy for the identification of units of economic interest varied from 55% to 89%, albeit with high commission error values. In addition, the results using L-band were considered superior compared to C-band, which suggest that the roughness scale for laterite discrimination in the area is nearer to L than to C-band.

  20. Method for regeneration of electroless nickel plating solution

    Science.gov (United States)

    Eisenmann, E.T.

    1997-03-11

    An electroless nickel(EN)/hypophosphite plating bath is provided employing acetic acid/acetate as a buffer and which is, as a result, capable of perpetual regeneration while avoiding the production of hazardous waste. A regeneration process is provided to process the spent EN plating bath solution. A concentrated starter and replenishment solution is provided for ease of operation of the plating bath. The regeneration process employs a chelating ion exchange system to remove nickel cations from spent EN plating solution. Phosphites are then removed from the solution by precipitation. The nickel cations are removed from the ion exchange system by elution with hypophosphorus acid and the nickel concentration of the eluate adjusted by addition of nickel salt. The treated solution and adjusted eluate are combined, stabilizer added, and the volume of resulting solution reduced by evaporation to form the bath starter and replenishing solution. 1 fig.

  1. Method for regeneration of electroless nickel plating solution

    Science.gov (United States)

    Eisenmann, Erhard T.

    1997-01-01

    An electroless nickel(EN)/hypophosphite plating bath is provided employing acetic acid/acetate as a buffer and which is, as a result, capable of perpetual regeneration while avoiding the production of hazardous waste. A regeneration process is provided to process the spent EN plating bath solution. A concentrated starter and replenishment solution is provided for ease of operation of the plating bath. The regeneration process employs a chelating ion exchange system to remove nickel cations from spent EN plating solution. Phosphites are then removed from the solution by precipitation. The nickel cations are removed from the ion exchange system by elution with hypophosphorous acid and the nickel concentration of the eluate adjusted by addition of nickel salt. The treated solution and adjusted eluate are combined, stabilizer added, and the volume of resulting solution reduced by evaporation to form the bath starter and replenishing solution.

  2. Chromium, Nickel and Zinc Induced Histopathological Alterations in ...

    African Journals Online (AJOL)

    Michael Horsfall

    fish, Labeo rohita to chlorides of chromium, nickel and zinc for 30 days. However ... toxicants such as salts of heavy metals, acids, organic matter ... nutritional supply becomes excessive. ... action), petrochemicals, and fertilizers and in steam.

  3. Lewis Acid Assisted Nickel-Catalyzed Cross-Coupling of Aryl Methyl Ethers by C−O Bond-Cleaving Alkylation: Prevention of Undesired β-Hydride Elimination

    KAUST Repository

    Liu, Xiangqian

    2016-04-10

    In the presence of trialkylaluminum reagents, diverse aryl methyl ethers can be transformed into valuable products by C-O bond-cleaving alkylation, for the first time without the limiting β-hydride elimination. This new nickel-catalyzed dealkoxylative alkylation method enables powerful orthogonal synthetic strategies for the transformation of a variety of naturally occurring and easily accessible anisole derivatives. The directing and/or activating properties of aromatic methoxy groups are utilized first, before they are replaced by alkyl chains in a subsequent coupling process.

  4. Lead-nickel electrochemical batteries

    CERN Document Server

    Glaize, Christian

    2012-01-01

    The lead-acid accumulator was introduced in the middle of the 19th Century, the diverse variants of nickel accumulators between the beginning and the end of the 20th Century. Although old, these technologies are always very present on numerous markets. Unfortunately they are still not used in optimal conditions, often because of the misunderstanding of the internal electrochemical phenomena.This book will show that batteries are complex systems, made commercially available thanks to considerable amounts of scientific research, empiricism and practical knowledge. However, the design of

  5. Chemical-mineralogical study of the ferrosialitic lateritic profiles in the Teneme, Farallones and Cayo Guam sectors in north east Cuba

    International Nuclear Information System (INIS)

    Njila, Tendai; Diaz Martinez, Roberto

    2016-01-01

    The results of a chemical-mineralogical study on the ferrosialitic lateritic weathering profile are presented. Analysis was done using x Ray Fluorescence and Diffraction. The chemical composition of these profile reflects a typical pattern normally observed within such weathering crusts. The sesquioxides of aluminium, iron are concentrated in the upper parts of the profiles as a result of the leaching of alkalis, alkaline-earth elements, and to a lesser extent, silica. Ferrosialitic lateritic profiles formed on Cretaceous and Paleogene islands arcs consist of secondary minerals such as gibbsite, kaolinite, goethite, hematite and montmorillonite, while those associated with basic and volcanogenic-sedimentary rocks of ophiolitic affinity in Cayo Guam are composed of gibbsite and iron oxides. Brings new chemical-mineralogical information on the ferrosialitic lateritic profiles associated with rocks of oceanic nature in north-eastern Cuba, which will help in the exploration for industrial minerals and rocks and their application in industry. (author) [es

  6. Syntheses and study on nickel(II) complexes with thiodiglycolic acid and nitrogen-donor ligands. X-ray structures of [Ni(bpy)(tdga)(H2O)] . 4H2O and [(en)Ni(µ-tdga)2Ni(en)] . 4H2O (tdgaH2=thiodiglycolic acid)

    Czech Academy of Sciences Publication Activity Database

    Kopel, P.; Trávníček, Zdeněk; Marek, J.; Mrozinski, J.

    2004-01-01

    Roč. 23, č. 9 (2004), s. 1573-1578 ISSN 0277-5387 R&D Projects: GA ČR(CZ) GA203/02/0436 Grant - others:GA MŠk1(CZ) MSM 153100007; GA MŠK1(CZ) MSM 143100008; Polish State Committee for Scientific Research(PL) 4T09A 11523 Institutional research plan: CEZ:AV0Z5038910 Keywords : nickel(II) * thiodiglycolic acid complexes * X-ray structures Subject RIV: CF - Physical ; Theoretical Chemistry Impact factor: 1.586, year: 2004

  7. NICKEL – ENVIRONMENTAL ALLERGEN

    Directory of Open Access Journals (Sweden)

    Henryka Langauer-Lewowicka

    2010-06-01

    Full Text Available Nickel (Ni is ubiquitus in our biosphere because of its emission from natural and anthropogenic sources. Its toxic and carcinogenic properties are well recognised only in workers exposed to high Ni concentrations. Nickel allergy is the most common form of cutaneus hypersensitivity in general population and also in occupationally exposed groups. As sensitizing agent Ni has a high prevalence of allergic contact dermatitis. The most important known risk factor associated with nickel allergy is ear piercing and use of other jewelry in females. In general population 17 % adults and 8 % children have Ni allergy symptoms. Permanently growing Ni allergy is regarded as serious risk for public health.

  8. Bacterial bioleaching of low grade nickel limonite and saprolite ores by mixotrophic bacteria

    Directory of Open Access Journals (Sweden)

    Chaerun Siti Khodijah

    2016-01-01

    Full Text Available Utilization of indigenous bacteria should be considered to establish a successful biohydrometallurgical process. In this study, mixrotrophic iron-oxidizing bacterial consortia consisting of Comamonas testosteroni, Alicyclobacillus ferrooxydans and Pantoea septic which were isolated from Indonesian mineral ores were examined to determine their abilities to recover nickel from limonite and saprolite ores in the bioleaching experiments using stirred tank reactors. The nickel bioleaching experiments inoculated with the bacterial consortia were carried out using coarse limonite ores and weathered saprolite ores with pulp density of 10% w/v. Abiotic controls were also carried out replacing the inocula by the sterile medium. The bioleaching processes were monitored by measuring Ni and Fe contents and pH of the leaching solution as well as the total bacterial enzymatic activity measured as FDA hydrolytic activity. The effect of leaching on the mineralogy of laterite ores was investigated by the scanning electron microscope equipped with energy-dispersive spectroscopy (SEM-EDS and X-ray powder diffraction (XRD. After 28 days of incubation, the FDA hydrolytic activity was observed in both bioleaching experiments containing limonite (17.2 μg fluorescein/mL and saprolite ores (16.9 μg fluorescein/mL. The leached Ni and Fe in the bioleaching experiments containing limonite ores (30% Ni and 5.6% Fe was greater than that in abiotic controls (1% Ni and 0.1% Fe with the pH range of 2.5 to 3.5. However, the bacterial consortia were less capable of bioleaching of Ni (2.5% with the similar leached Fe (6% from the saprolite ores. In abiotic controls, the medium pH remained relatively constant (pH 6. It was concluded that these bacterial isolated as the consortium were capable of nickel bioleaching (precious metal more effectively than iron (gangue metal, thus being applicable to the commercial processing of the difficult-to-process low-grade nickel laterite ores

  9. Occupational hand eczema caused by nickel and evaluated by quantitative exposure assessment

    DEFF Research Database (Denmark)

    Jensen, Peter; Thyssen, Jacob Pontoppidan; Johansen, Jeanne D

    2011-01-01

    Background. EU legislation has reduced the epidemic of nickel contact allergy affecting the consumer, and shifted the focus towards occupational exposure. The acid wipe sampling technique was developed to quantitatively determine skin exposure to metals. Objectives. To assess the clinical...... dilution series were performed. Results. Nickel was detected in all samples from the hands. In all patients, the nickel content on the hands was higher than on the non-exposed control area. Conclusions. Occupational exposure to nickel-releasing items raised the nickel content on exposed skin as compared...

  10. Ni, Co recovery study and Fe by acid leaching in columns; Estudio de la extraccion de Ni, Co y Fe en lateritas por medio de lixiviacion acida en columnas

    Energy Technology Data Exchange (ETDEWEB)

    Yorio, C. di; Betancourt, E.; Vivas, R.; Rus, J.

    2006-07-01

    In the following work the possibility of the mic kel recovery by hydrometallurgy extraction for nickeliferous laterite is studied. The work looks for to study the technical viability of the extraction of nickel and cobalt by means of the application of heap leaching. The ore is chemically and physically characterized with the purpose of analyzes its composition and mineral phase, by means of x-rays diffraction, quantitative chemical analysis and elementary chemical analysis by electronic microscopy. One the ore is characterized, it is mixed with sulfuric acid to relations 0.05; 0.1 and 0.2 g acid/g to agglomerated pellets and paste, with the aim to improve the percolation in column, due to the argillaceous nature of the ore leaching rate ranged from 0.305 to 1.06 x 10 l/h m''2 and in the agglomerate condition of the percolation l/h m''2 improves at interval 3.05 to 6.11 x 100 l/h m''2. (Author)

  11. Reactive transport model of the formation of oxide-type Ni-laterite profiles (Punta Gorda, Moa Bay, Cuba)

    Science.gov (United States)

    Domènech, Cristina; Galí, Salvador; Villanova-de-Benavent, Cristina; Soler, Josep M.; Proenza, Joaquín A.

    2017-10-01

    Oxide-type Ni-laterite deposits are characterized by a dominant limonite zone with goethite as the economically most important Ni ore mineral and a thin zone of hydrous Mg silicate-rich saprolite beneath the magnesium discontinuity. Fe, less soluble, is mainly retained forming goethite, while Ni is redeposited at greater depth in a Fe(III) and Ni-rich serpentine (serpentine II) or in goethite, where it adsorbs or substitutes for Fe in the mineral structure. Here, a 1D reactive transport model, using CrunchFlow, of Punta Gorda oxide-type Ni-laterite deposit (Moa Bay, Cuba) formation is presented. The model reproduces the formation of the different laterite horizons in the profile from an initial, partially serpentinized peridotite, in 106 years, validating the conceptual model of the formation of this kind of deposits in which a narrow saprolite horizon rich in Ni-bearing serpentine is formed above peridotite parent rock and a thick limonite horizon is formed over saprolite. Results also confirm that sorption of Ni onto goethite can explain the weight percent of Ni found in the Moa goethite. Sensitivity analyses accounting for the effect of key parameters (composition, dissolution rate, carbonate concentration, quartz precipitation) on the model results are also presented. It is found that aqueous carbonate concentration and quartz precipitation significantly affects the laterization process rate, while the effect of the composition of secondary serpentine or of mineral dissolution rates is minor. The results of this reactive transport modeling have proven useful to validate the conceptual models derived from field observations.

  12. Nickel in tap water

    Energy Technology Data Exchange (ETDEWEB)

    Andersen, K E; Nielsen, G D; Flyvholm, M A; Fregert, S; Gruvberge, B

    1983-03-01

    Nickel analyses of tap water from several sources in Copenhagen gave up to 490 X 10(-6) g X 1(-1) in the first 250 ml portions. Hot water gave higher values than cold water. After flushing for 5 min, low values were found. Considerable variation from time to time and from tap to tap was found. Drinking of only the first portion in the morning might have an influence on nickel hand eczema.

  13. Genesis of a mottled horizon by Fe-depletion within a laterite cover in the Amazon Basin.

    OpenAIRE

    Rosolen , Vania; Lamotte , Mathieu; Boulet , René; Trichet , Jean; Rouer , Olivier; José Melfi , Adolpho

    2002-01-01

    A mottled horizon in a laterite cover (without any duricrust) was studied by microscopy and quantitative chemical microanalysis. Apart from the voids, light red spots consisting of Fe-rich particles (≈2 μm) are set in clayey plasma. Dark red spots consisted of concentrations of Fe-rich particles. These patterns are inherited. On the border of structural or biological voids, where Fe-depletion features are systematic, gray or yellow spots result from dissolution of the Fe-rich particles and im...

  14. Effect of the use nickeliferous laterite and pumice as additives in the performance and durability of the Portland cement

    OpenAIRE

    Rueda-Gualdrón, María Carolina; Vega-Nuñez, Karen Milena; Ríos-Reyes, Carlos Alberto

    2016-01-01

    This work evaluated the pozzolanic behavior of the niqueliferous laterite of Cerromatoso (Córdoba) and the pumice of Cemex (Boyacá), based on the NTC standards for fine aggregates. The mortars were prepared with additions of 2.5%, 5% and 10% as substitutes of type I Portland cement, which tested to extreme environments (high temperatures and chemical attacks with H2SO4 y MgSO4). Results demonstrates how these alternative materials increase or decrease their puzolanic degree, as well as the ef...

  15. Moessbauer study of the evolution of a laterite iron mineral based catalyst: effect of the activation treatment

    International Nuclear Information System (INIS)

    Cubeiro, M.L.; Goldwasser, M.R.; Perez Zurita, M.J.; Franco, C.; Gonzalez-Jimenez, F.; Jaimes, E.

    1994-01-01

    The syngas reaction has been studied using a laterite iron mineral, promoted with K and Mn. In situ activation under syngas, as well as pre-treatment with H 2 followed by CO under mild and more severe conditions were tested. These activation procedures led to different iron phase compositions and to different catalytic selectivities. The C 2 -C 4 /CH 4 ratio was significantly lower for those catalysts which after reaction showed the presence of hexagonal carbide and magnetite compared to the solid, which showed the highest proportion of Haegg carbide. (orig.)

  16. Rare earth element mineralogy and geochemistry in a laterite profile from Madagascar

    International Nuclear Information System (INIS)

    Berger, Alfons; Janots, Emilie; Gnos, Edwin; Frei, Robert; Bernier, Felix

    2014-01-01

    Highlights: • Secondary REE-mineralogy depend on redox conditions inside a laterite. • Detailed mineralogy in different layers of a laterite is given. • A Gd-sulfate is described. • Change in bulk rock chemistry control REE mineralogy. - Abstract: In this study, rare earth element (REE) distribution has been investigated in a weathering profile from central Madagascar. Combination of bulk rock geochemical data (elements and isotopes) with mineral characterization reveals a remarkable evolution of the REE abundances and REE-minerals in the vertical weathering profile. In the fresh tonalite (bedrock), REE + Y concentrations are typical of granitoids (299–363 ppm) and the main REE-minerals are allanite and chevkinite. In the C-horizon (saprolite), primary REE-minerals disappear and REEs are transported via fluid to precipitate rhabdophane group minerals in cracks and pores. The presence of sulfate ligands, produced by sulfide oxidation, may be responsible for the REE speciation, as suggested by the composition of the secondary REE-minerals. Rhabdophane group minerals contain up to 9 wt% SO 3 and 7 wt% CaO, indicating a mixture between rhabdophane sensu stricto, (REE)PO 4 ·H 2 O, and tristamite, (Ca,U,Fe (III) )(PO 4 ,SO 4 )·2H 2 O. Due to intense Ca-leaching, rhabdophane disappears and Al-phosphates (alunite–jarosite group) are found in the soil. Cerianite (Ce (IV) O 2 ) also precipitates in the B-horizon of the soil. Mass transfer calculations based on immobile Ti indicate significant REE leaching in A-horizon with preferential leaching of the heavy REE. REEs accumulate partly in the B-horizon. The uniform Nd isotope compositions and the constant proportion of immobile elements do not reveal external input. In the B-horizon, total REE + Y reach 2194 ppm with high Ce concentrations (1638 ppm; 9 * Ce bedrock ) compared to other REE (3–4 * REE bedrock ). Tetravalent Ce state is dominant in the B-horizon and requires oxidizing conditions that likely

  17. Phosphorus runoff from sewage sludge applied to different slopes of lateritic soil.

    Science.gov (United States)

    Chen, Yan Hui; Wang, Ming Kuang; Wang, Guo; Chen, Ming Hua; Luo, Dan; Ding, Feng Hua; Li, Rong

    2011-01-01

    Sewage sludge (SS) applied to sloping fields at rates that exceed annual forest nutrient requirements can be a source of phosphorus (P) in runoff. This study investigates the effects of different slopes (18, 27, 36, and 45%) on P in runoff from plots amended with SS (120 Mg ha). Lateritic soil (pH 5.2) was exposed to five simulated rainfalls (90 mm h) on outdoor plots. When sludge was broadcast and mixed with surface soils, the concentrations and loss in runoff of total P in the mixed sample (MTP), total P in the settled sample (STP), total particulate P (TPP), total suspended P (TSP), and total dissolved P (TDP) were highest at 1 or 18 d after application. Initially, pollution risks to surface waters generally increased to different degrees with steeper slopes, and then diminished gradually with dwindling differences between the slopes. The runoff losses coefficient of MTP increased in the order 36 > 45 > 27 > 18%. The initial event (1 and 18 d) accounted for 67.0 to 83.6% of total runoff P losses. Particulate fraction were dominant carriers for P losses, while with the lower slopes there was higher content of P per unit particulate fraction in runoff. Phosphorus losses were greatly affected by the interaction of sludge-soil-runoff and the modification of soil properties induced by sludge amendment. It is recommended to choose lower slopes (soils should be studied further in the field under a wider diversity of conditions. Copyright © by the American Society of Agronomy, Crop Science Society of America, and Soil Science Society of America, Inc.

  18. Specification and prediction of nickel mobilization using artificial intelligence methods

    Science.gov (United States)

    Gholami, Raoof; Ziaii, Mansour; Ardejani, Faramarz Doulati; Maleki, Shahoo

    2011-12-01

    Groundwater and soil pollution from pyrite oxidation, acid mine drainage generation, and release and transport of toxic metals are common environmental problems associated with the mining industry. Nickel is one toxic metal considered to be a key pollutant in some mining setting; to date, its formation mechanism has not yet been fully evaluated. The goals of this study are 1) to describe the process of nickel mobilization in waste dumps by introducing a novel conceptual model, and 2) to predict nickel concentration using two algorithms, namely the support vector machine (SVM) and the general regression neural network (GRNN). The results obtained from this study have shown that considerable amount of nickel concentration can be arrived into the water flow system during the oxidation of pyrite and subsequent Acid Drainage (AMD) generation. It was concluded that pyrite, water, and oxygen are the most important factors for nickel pollution generation while pH condition, SO4, HCO3, TDS, EC, Mg, Fe, Zn, and Cu are measured quantities playing significant role in nickel mobilization. SVM and GRNN have predicted nickel concentration with a high degree of accuracy. Hence, SVM and GRNN can be considered as appropriate tools for environmental risk assessment.

  19. Improvement of solvents for chemical decontamination: nickel ferrites removal

    International Nuclear Information System (INIS)

    Figueroa, Carlos A.; Morando, Pedro J.; Blesa, Miguel A.

    1999-01-01

    Carboxylic acids are usually included in commercial solvents for the chemical cleaning and decontamination of metal surfaces from the oxide layers grown and/or deposited from high temperature water by corrosive process. In particular oxalic acid is included in second path of AP-Citrox method. However, in some cases, their use shows low efficiency. This fact is attributed to the special passivity of the mixed oxides as nickel ferrites. This work reports a kinetic study of dissolution of a synthetic nickel ferrite (NiFe 2 O 4 ) confronted with simple oxides (NiO and Fe 2 O 3 ) in mineral acids and oxalic acid. The dissolution factor and reaction rate were determined in several conditions (reactive concentrations, pH and added ferrous ions). Experimental data of dissolution (with and without Fe(II) added) show a congruent kinetic regime. Pure nickel oxide (NiO) is rather resistant to the attack by oxalic acid solutions, and ferrous ions do not accelerate dissolution. In fact, nickel oxide dissolves better by oxidative attack that takes advantage of the higher lability of Ni 3+ . It may be concluded that oxalic acid operates to dissolve iron, and the ensuing disruption of the solid framework accelerates the release of nickel. Our results point to use more reactive solvents in iron from mixed oxides and to the possibility of using one stage decontamination method. (author)

  20. Validity of using modified capillary column with larger diameter to study the Cs diffusion in local Taiwan laterite

    International Nuclear Information System (INIS)

    Tsing-Hai Wang; National Tsing Hua University, Hsinchu, Taiwan; Wen-Chun Yeh; Shih-Chin Tsai; Yi-Lin Jan; Shi-Ping Teng

    2008-01-01

    We have examined the working diameter of capillary columns with diameter of 5, 7, 10 and 20 mm. These modified capillary columns were carefully filled with local Taiwan laterite (LTL). The porosity and density of these packed columns was 0.51±0.02 g/g and 1.27±0.05 g/cm 3 , respectively. The diffusion experiments were then carried out in synthetic groundwater with Cs loading of 0.1mM at room temperature. Experimental results have shown that the diffusion profiles of modified capillary columns fit Fick's second law very well. This result revealed that the working diameter of a capillary column can be expanded to at least to 20 mm without affecting the validity of the derived diffusion coefficients. Among these columns, the ones with 5 mm diameter show the most consistent results of the derived K d , apparent and effective diffusion coefficients. Although the derived distribution and effective diffusion coefficients slightly decrease as the diameter of these columns increases due to the increase of the solid/liquid ratio. These values are still informative of the Cs diffusion in local Taiwan laterite. Moreover, our results clearly demonstrate the potential of using 'modified capillary method' to study the diffusion behaviors of concerned radionuclide because columns with large diameter enable the filling with more versatile geological substances. (author)

  1. Geochemical behaviour of U3O8, Mo, Y, Ga, V and Zr in laterite - bauxitic sequence of the ''Croanta-Paragominas''

    International Nuclear Information System (INIS)

    Ferraioli, R.N.M.; Ferreira, Z.C.A.

    1987-10-01

    Fifteen samples are studied, analyzed for U 3 O 8 (delayed neutrons), ThO 2 (X-ray fluorescence spectrometry) and Mo, Y, Ga, V and Zr (optical emission spectrography) in laterite - bauxitic sequence of the Paragominas, Brazil. Generical datas about the arrangements of thorium, uranium and zirconium are also presented. (C.G.C.) [pt

  2. Occupational hand eczema caused by nickel and evaluated by quantitative exposure assessment.

    Science.gov (United States)

    Jensen, Peter; Thyssen, Jacob P; Johansen, Jeanne D; Skare, Lizbet; Menné, Torkil; Lidén, Carola

    2011-01-01

    EU legislation has reduced the epidemic of nickel contact allergy affecting the consumer, and shifted the focus towards occupational exposure. The acid wipe sampling technique was developed to quantitatively determine skin exposure to metals. To assess the clinical usefulness of the acid wipe sampling technique as part of the diagnostic investigation for occupational nickel allergy-associated hand dermatitis. Six patients with vesicular dermatitis on the hands were included. Acid wipe sampling of skin and patch testing with a nickel sulfate dilution series were performed. Nickel was detected in all samples from the hands. In all patients, the nickel content on the hands was higher than on the non-exposed control area. Occupational exposure to nickel-releasing items raised the nickel content on exposed skin as compared with a non-exposed control site. Nickel-reducing measures led to complete symptom relief in all cases. In cases of a positive nickel patch test reaction and hand eczema, patients should perform the dimethylglyoxime (DMG) test on metallic items at home and at work. The acid wipe sampling technique is useful for the diagnosis of occupational hand eczema following screening with the inexpensive DMG test. © 2010 John Wiley & Sons A/S.

  3. Hydrometallurgical separation of rare earth elements, cobalt and nickel from spent nickel-metal-hydride batteries

    Science.gov (United States)

    Rodrigues, Luiz Eduardo Oliveira Carmo; Mansur, Marcelo Borges

    The separation of rare earth elements, cobalt and nickel from NiMH battery residues is evaluated in this paper. Analysis of the internal content of the NiMH batteries shows that nickel is the main metal present in the residue (around 50% in weight), as well as potassium (2.2-10.9%), cobalt (5.1-5.5%), rare earth elements (15.3-29.0%) and cadmium (2.8%). The presence of cadmium reveals that some Ni-Cd batteries are possibly labeled as NiMH ones. The leaching of nickel and cobalt from the NiMH battery powder with sulfuric acid is efficient; operating variables temperature and concentration of H 2O 2 has no significant effect for the conditions studied. A mixture of rare earth elements is separated by precipitation with NaOH. Finally, solvent extraction with D2EHPA (di-2-ethylhexyl phosphoric acid) followed by Cyanex 272 (bis-2,4,4-trimethylpentyl phosphinic acid) can separate cadmium, cobalt and nickel from the leach liquor. The effect of the main operating variables of both leaching and solvent extraction steps are discussed aiming to maximize metal separation for recycling purposes.

  4. The GENIALL process for generation of nickel-iron alloys from nickel ores or mattes

    International Nuclear Information System (INIS)

    Diaz, G.; Frias, C.; Palma, J.

    2001-01-01

    A new process, called GENIALL (acronym of Generation of Nickel Alloys), for nickel recovery as ferronickel alloys from ores or mattes without previous smelting is presented in this paper. Its core technology is a new electrolytic concept, the ROSEL cell, for electrowinning of nickel-iron alloys from concentrated chloride solutions. In the GENIALL Process the substitution of iron-based solid wastes as jarosite, goethite or hematite, by saleable ferronickel plates provides both economic and environmental attractiveness. Another advantage is that no associated sulfuric acid plant is required. The process starts with leaching of the raw material (ores or mattes) with a solution of ferric chloride. The leachate liquor is purified by conventional methods like cementation or solvent extraction, to remove impurities or separate by-products like copper and cobalt. The purified solution, that contains a mixture of ferrous and nickel chlorides is fed to the cathodic compartment of the electrowinning cell, where nickel and ferrous ions are reduced together to form an alloy. Simultaneously, ferrous chloride is oxidized to ferric chloride in the anodic compartment, from where it is recycled to the leaching stage. The new electrolytic equipment has been developed and scaled up from laboratory to pilot prototypes with commercial size electrodes of 1 m 2 . Process operating conditions have been established in continuous runs at bench and pilot plant scale. The technology has shown a remarkable capacity to produce nickel-iron alloys of a wide range of compositions, from 10% to 80% nickel, just by adjusting the operating parameters. This emerging technology could be implemented in many processes in which iron and other non-ferrous metals are harmful impurities to be removed, or valuable metals to be recovered as a marketable iron alloy. Other potential applications of this technology are regeneration of spent etching liquors, and iron removal from aqueous effluents. (author)

  5. Determination of nickel-63

    International Nuclear Information System (INIS)

    Poletiko, C.

    1988-01-01

    The research of activation products in the environment is often centered on cobalt-60 or other gamma emitters, since pure beta emitters require time consuming separations to be counted. However, some beta emitters must be checked because they have a build up in the environment, leading to potential hazards. Among these nuclides, there is nickel-63 which is a pure, soft beta emitter (67 keV) with a long half-life (100 years). A chemical separation, providing good results, was developed. Such a separation is based upon nickel carrier addition in the sample than DMG complex formation and isolation; after elimination of solvent. DMG complex is destroyed. Chemical yield is determined by flame atomic absorption measurement and nickel-63 counted by liquid scintillation. The described procedure allows the determination of low-level activities in different samples (soils, effluents, etc.). Detection limits are close to 0.1 Bq per sample

  6. Combination of acid-resistor and -scavenger improves the SEI stability and cycling ability of tin–nickel battery anodes in LiPF6-containing electrolyte

    International Nuclear Information System (INIS)

    Choo, Myeong-Ho; Nguyen, Cao Cuong; Hong, Sukhyun; Kwon, Yo Han; Woo, Sang-Wook; Kim, Je Young; Song, Seung-Wan

    2013-01-01

    Control of electrode–electrolyte interfacial reactivity and the formation of the solid electrolyte interphase (SEI) layer is a key technology for high performance rechargeable lithium batteries. Here we present the first report on a promising interfacial approach for Sn–Ni electrode that the use of acid-resisting and -scavenging fluorine-dopant on Sn combined with acid-scavenging trimethyl phosphite electrolyte additive to LiPF 6 -contiaing carbonate-based organic electrolyte improves the interfacial stability of Sn to acidic electrolyte species. As a result, a stable SEI layer consisting of a plenty of carbonate decomposition products forms and cycling ability significantly improves, in contrast to less efficient SEI formation and rapid performance fade for the electrodes without fluorine-dopant or trimethyl phosphite additive

  7. Nanoparticles of nickel hexacyanoferrate

    International Nuclear Information System (INIS)

    Bicalho, U.O.; Santos, D.C.; Silvestrini, D.R.; Trama, B.; Carmo, D.R. do

    2014-01-01

    Nanoparticles of nickel hexacyanoferrate (NHNi) were prepared in three medium (aqueous, formamide and aqueous/formamide). The materials were characterized by infrared spectroscopy (FT-IR), X-ray diffraction (XRD), electronica spectroscopy in the ultraviolet-visible (UV-Vis) region and also by cyclic voltammetry (CV). By spectroscopic analysis of X-ray diffraction was possible to estimate the size of the particles obtained by the Scherrer equation. The graphite paste electrodes containing nanoparticles of nickel hexacyanoferrate means formamide was sensitive to different concentrations of Dipyrone. (author)

  8. A critical overview of definitions and determination techniques of the internal resistance using lithium-ion, lead-acid, nickel metal-hydride batteries and electrochemical double-layer capacitors as examples

    Science.gov (United States)

    Piłatowicz, Grzegorz; Marongiu, Andrea; Drillkens, Julia; Sinhuber, Philipp; Sauer, Dirk Uwe

    2015-11-01

    The internal resistance (Ri) is one of the key parameters that determine the current state of electrochemical storage systems (ESS). It is crucial for estimating cranking capability in conventional cars, available power in modern hybrid and electric vehicles and for determining commonly used factors such as state-of-health (SoH) and state-of-function (SoF). However, ESS are complex and non-linear systems. Their Ri depends on many parameters such as current rate, temperature, SoH and state-of-charge (SoC). It is also a fact that no standardized methodologies exist and many different definitions and ways of Ri determination are being used. Nevertheless, in many cases authors are not aware of the consequences that occur when different Ri definitions are being used, such as possible misinterpretations, doubtful comparisons and false figures of merit. This paper focuses on an application-oriented separation between various Ri definitions and highlights the differences between them. The investigation was based on the following technologies: lead-acid, lithium-ion and nickel metal-hydride batteries as well as electrochemical double-layer capacitors. It is not the target of this paper to provide a standardized definition of Ri but to give researchers, engineers and manufacturers a possibility to understand what the term Ri means in their own work.

  9. Codeposition of either molybdenum or tungsten with the metals of iron group 8. The citric acid influence on codeposition of nickel and tungsten from sulphamic electrolytes

    International Nuclear Information System (INIS)

    Bernotas, A.; Kadziauskiene, V.; Jasulaitiene, V.

    1995-01-01

    The influence of citric acid on codeposition of Ni and W from sulphamic electrolytes was investigated by measuring the hydrogen content in electro deposits and determining the current efficiency and the alloy composition by chemical analysis and X-ray spectroscopy. The reduction of W(VI) to W(0) in the electrolyte with and without citric acid was found to proceed through the formation of tungsten compounds of intermediate oxidation state. It is supposed that an increased amount of tungsten in the alloys with the increase of citric acid concentration in the electrolyte (to 0.042 mol/l) is caused by a large amount of W(IV) at the cathodic surface. The further increase of the concentration of citric acid in the electrolyte causes a decrease of tungsten amount in the alloy, because the blocking of the metallic surface of Ni and W by W compounds of intermediate oxidation state makes the reduction of W(VI) to W(0) more difficult. (author). 8 refs., 3 figs., 1 tab

  10. Synthesis of α-Amino Acids via Asymmetric Phase Transfer-Catalyzed Alkylation of Achiral Nickel(II) Complexes of Glycine-Derived Schiff Bases

    NARCIS (Netherlands)

    Belokon, Yuri N.; Bespalova, Natalia B.; Churkina, Tatiana D.; Císařová, Ivana; Ezernitskaya, Marina G.; Harutyunyan, Syuzanna R.; Hrdina, Radim; Kagan, Henri B.; Kočovský, Pavel; Kochetkov, Konstantin A.; Larionov, Oleg V.; Lyssenko, Konstantin A.; North, Michael; Polášek, Miroslav; Peregudov, Alexander S.; Prisyazhnyuk, Vladimir V.; Vyskočil, Štěpán

    2003-01-01

    Achiral, diamagnetic Ni(II) complexes 1 and 3 have been synthesized from Ni(II) salts and the Schiff bases, generated from glycine and PBP and PBA, respectively, in MeONa/MeOH solutions. The requisite carbonyl-derivatizing agents pyridine-2-carboxylic acid(2-benzoyl-phenyl)-amide (PBP) and

  11. Nickel silicide formation in silicon implanted nickel

    Science.gov (United States)

    Rao, Z.; Williams, J. S.; Pogany, A. P.; Sood, D. K.; Collins, G. A.

    1995-04-01

    Nickel silicide formation during the annealing of very high dose (≥4.5×1017 ions/cm2) Si implanted Ni has been investigated, using ion beam analytical techniques, electron microscopy, and x-ray diffraction analysis. An initial amorphous Si-Ni alloy, formed as a result of high dose ion implantation, first crystallized to Ni2Si upon annealing in the temperature region of 200-300 °C. This was followed by the formation of Ni5Si2 in the temperature region of 300-400 °C and then by Ni3Si at 400-600 °C. The Ni3Si layer was found to have an epitaxial relationship with the substrate Ni, which was determined as Ni3Si∥Ni and Ni3Si∥Ni for Ni(100) samples. The minimum channeling yield in the 2 MeV He Rutherford backscattering and channeling spectra of this epitaxial layer improved with higher annealing temperatures up to 600 °C, and reached a best value measured at about 8%. However, the epitaxial Ni3Si dissolved after long time annealing at 600 °C or annealing at higher temperatures to liberate soluble Si into the Ni substrate. The epitaxy is attributed to the excellent lattice match between the Ni3Si and the Ni. The annealing behavior follows the predictions of the Ni-Si phase diagram for this nickel-rich binary system.

  12. The cost of nickel allergy

    DEFF Research Database (Denmark)

    Hamann, Carsten R; Hamann, Dathan; Hamann, Curtis

    2013-01-01

    %), followed by aluminium-bronze (62, 17%). In total, 239 denominations released nickel (28%). Coins from Bolivia, Brazil and Costa Rica did not release nickel. Fewer than one-third of the denominations or issues from China, India, the euro area and Indonesia released nickel. In the United States, the Russian...... Federation, Japan, and Mexico, one-third or more of the denominations released nickel. Conclusions. This worldwide selection of circulating coins covered countries with 75% of the world population, and shows that the majority of the world population lives in countries where coins release nickel. Pertinently...

  13. A review of nickel toxicity to marine and estuarine tropical biota with particular reference to the South East Asian and Melanesian region.

    Science.gov (United States)

    Gissi, Francesca; Stauber, Jennifer L; Binet, Monique T; Golding, Lisa A; Adams, Merrin S; Schlekat, Christian E; Garman, Emily R; Jolley, Dianne F

    2016-11-01

    The South East Asian Melanesian (SEAM) region contains the world's largest deposits of nickel lateritic ores. Environmental impacts may occur if mining operations are not adequately managed. Effects data for tropical ecosystems are required to assess risks of contaminant exposure and to derive water quality guidelines (WQG) to manage these risks. Currently, risk assessment tools and WQGs for the tropics are limited due to the sparse research on how contaminants impact tropical biota. As part of a larger project to develop appropriate risk assessment tools to ensure sustainable nickel production in SEAM, nickel effects data were required. The aim of this review was to compile data on the effects of nickel on tropical marine, estuarine, pelagic and benthic species, with a particular focus on SEAM. There were limited high quality chronic nickel toxicity data for tropical marine species, and even fewer for those relevant to SEAM. Of the data available, the most sensitive SEAM species to nickel were a sea urchin, copepod and anemone. There is a significant lack of high quality chronic data for several ecologically important taxonomic groups including cnidarians, molluscs, crustaceans, echinoderms, macroalgae and fish. No high quality chronic nickel toxicity data were available for estuarine waters or marine and estuarine sediments. The very sparse toxicity data for tropical species limits our ability to conduct robust ecological risk assessment and may require additional data generation or read-across from similar species in other databases (e.g. temperate) to fill data gaps. Recommendations on testing priorities to fill these data gaps are presented. Copyright © 2016 Elsevier Ltd. All rights reserved.

  14. Degradação das paisagens de solos lateríticos e uso da terra no distrito de Birbhum, Bengala Ocidental, Índia / Degraded lateritic soils cape and land uses in Birbhum District, West Bengal, India

    Directory of Open Access Journals (Sweden)

    V. C. Jha

    2011-12-01

    Full Text Available Degradation of lateritic environment as found in the south western and eastern Birbhum district can be considered as irresistible. Inherently poor physical and chemical status of existing lateritic soil profileand radical conversion of land uses as observed at cadastral level are the key factors of land degradation.Lateritic soilscapes are mostly affected by water erosion induced, vegetal and anthropogenic degradation attaining severe and very severe degradation status. Degraded lands in sample mouzas like Ballabhpur, Shyambati, Chawpahari Jungle, Bodakuri and Pachami account for 60.33%, 71.42%, 72.99%, 87.31% and 79.66% respectively out of their total lateritic exposures. In other words about 36.98%, 71.42%, 61.73%, 56.70% and 76.02% out of their total village areas and mostly non agricultural land use areaffected by it. Four degraded villages get the higher priority for friendly landscape conservation actions.

  15. Nickel in tap water

    DEFF Research Database (Denmark)

    Andersen, Klaus Ejner; Nielsen, G D; Flyvholm, Morten

    1983-01-01

    Nickel analyses of tap water from several sources in Copenhagen gave up to 490 X 10(-6) g X 1(-1) in the first 250 ml portions. Hot water gave higher values than cold water. After flushing for 5 min, low values were found. Considerable variation from time to time and from tap to tap was found...

  16. cobalt (ii), nickel (ii)

    African Journals Online (AJOL)

    DR. AMINU

    Department of Chemistry Bayero University, P. M. B. 3011, Kano, Nigeria. E-mail: hnuhu2000@yahoo.com. ABSTRACT. The manganese (II), cobalt (II), nickel (II) and .... water and common organic solvents, but are readily soluble in acetone. The molar conductance measurement [Table 3] of the complex compounds in.

  17. EPIDEMIOLOGICAL AND PATHOGENETIC ASPECTS OF NICKEL POISONING

    OpenAIRE

    Vladmila Bojanic; Vladimir Ilic; Biljana Jovic

    2007-01-01

    Nickel is widely distributed in the environment. High consumption of nickel containing products inevitably leads to environmental pollution by nickel and its derivatives at all stages of production, utilization, and disposal.Human exposure to nickel occurs primarily via inhalation and ingestion and is particularly high among nickel metallurgy workers. In addition, implantation of nickel-containing endoprostheses and iatrogenic administration of nickel-contaminated medica-tions leads to signif...

  18. Electro-deposition of nickel, on reactor seal discs

    International Nuclear Information System (INIS)

    Vernekar, R.B.; Bhide, G.K.

    1977-01-01

    The effect of plating variables, acidity, current density and temperature on hardness of nickel deposited from purified nickel sulfamate bath has been investigated and optimum conditions for electrodeposition of nickel plating of hardness 160-170 VHN on reactor seal discs are established. Sodium lauryl sulfate was added as a wetting agent to the bath to overcome pitting tendency of the deposit. Factors affecting hydrogen absorption by electrodeposited nickel are also discussed. It is observed that : (1) at a pH 3.5 - 4.0 the decomposition rate of sulfamate salt is almost negligible and is the best value for bath operation, (2) at 15 A/dm 2 the hardness value is consistently around 160-170 VHN, (3) the temperatures less than 50 0 C give harder deposits and the bath is best operated at temperature 50-60 0 C and (4) annealing of the plated discs substantially reduces the hardness. (M.G.B.)

  19. Fe-Ni-bearing serpentines from the saprolite horizon of Caribbean Ni-laterite deposits: new insights from thermodynamic calculations

    Science.gov (United States)

    Villanova-de-Benavent, Cristina; Domènech, Cristina; Tauler, Esperança; Galí, Salvador; Tassara, Santiago; Proenza, Joaquín A.

    2017-10-01

    Fe-Ni-bearing serpentine from the saprolite horizon is the main Ni ores in hydrous silicate-type Ni laterites and formed by chemical weathering of partially serpentinized ultramafic rocks under tropical conditions. During lateritization, Mg, Si, and Ni are leached from the surface and transported downwards. Fe2+ is oxidized to Fe3+ and fixed as insoluble Fe-oxyhydroxides (mostly goethite) that incorporate Ni. This Ni is later leached from goethite and incorporated in secondary serpentine and garnierite. As a result, a serpentine-dominated saprolite horizon forms over the ultramafic protolith, overlapped by a Fe-oxyhydroxide-dominated limonite horizon. The serpentine from the protolith (serpentine I) is of hydrothermal origin and yields similar Ni (0.10-0.62 wt.% NiO) and lower Fe (mostly 1.37-5.81 wt.% FeO) concentrations than the primary olivine. In contrast, Fe-Ni-bearing serpentine from the saprolite (serpentine II) shows significantly higher and variable Fe and Ni contents, typically ranging from 2.23 to 15.59 wt.% Fe2O3 and from 1.30 to 7.67 wt.% NiO, suggesting that serpentine get enriched in Fe and Ni under supergene conditions. This study presents detailed mineralogical, textural, and chemical data on this serpentine II, as well as new insights by thermodynamic calculations assuming ideal solution between Fe-, Ni- and Mg-pure serpentines. The aim is to assess if at atmospheric pressure and temperature Fe-Ni-bearing serpentine can be formed by precipitation. Results indicate that the formation of serpentine II under atmospheric pressure and temperature is thermodynamically supported, and pH, Eh, and the equilibrium constant of the reaction are the parameters that affect the results more significantly.

  20. Effect of nonwoven jute agrotextile mulch on soil health and productivity of broccoli (Brassica oleracea L.) in lateritic soil.

    Science.gov (United States)

    Manna, Koushik; Kundu, Manik Chandra; Saha, Biplab; Ghosh, Goutam Kumar

    2018-01-16

    A field experiment was conducted in winter season of 2015-2016 in the dry lateritic soil of Eastern India to study the effect of different thicknesses of nonwoven jute agrotextile mulches (NJATM) along with other mulches on soil health, growth and productivity of broccoli (Brassica oleracea L.). The experiment was conducted in randomized block design with six treatments viz., T 1 (control, i.e. no mulching), T 2 (300 gsm NJATM), T 3 (350 gsm NJATM), T 4 (400 gsm NJATM), T 5 (rice straw) and T 6 (black polythene mulch), each of which was replicated four times. The highest average curd weight (355.25 g) and yield (8.53 t ha -1 ) of broccoli were recorded in T 3 treatment. The lowest density of broad leaved weed, sedges and grasses were recorded in T 6 treatment which was statistically at par with T 4 . All the treatments composing of NJATM increased the population of all the soil microbes except bacteria in the root rhizosphere of broccoli from their initial population. On average, the highest population of fungi (54.0 × 10 3  cfu per g) and actinomycetes (134.75 × 10 3  cfu per g) was recorded with T 3 and T 4 treatments respectively in the post-harvest soil. The soil moisture was conserved in all treatments compared to control showing highest moisture content in T 4 treatment. Organic carbon and available N, P and K contents of soil were increased in all mulch treated plots compared to control, and their initial value and their highest value were recorded in T 3 . The NJATM of 350 gsm thickness was very effective compared to other mulches in increasing the growth and productivity of broccoli by suppressing weeds, increasing moisture, microbial population and nutrient content of the lateritic soil.

  1. Carbon deposition on nickel ferrites and nickel-magnetite surfaces

    International Nuclear Information System (INIS)

    Allen, G.C.; Jutson, J.A.

    1988-06-01

    Carbon deposition on Commercial Advanced Gas-Cooled Reactor (CAGR) fuel cladding and heat exchanger surfaces lowers heat transfer efficiency and increases fuel pin temperatures. Several types of deposit have been identified including both thin dense layers and also low density columnar deposits with filamentary or convoluted laminar structure. The low-density types are often associated with particles containing iron, nickel or manganese. To identify the role of nickel in the deposition process surfaces composed of nickel-iron spinels or metallic nickel/magnetite mixtures have been exposed to γ radiation in a gas environment simulating that in the reactor. Examination of these surfaces by Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM) have shown that while metallic nickel (Ni(O)) catalyses the formation of filamentary low density carbon deposits, the presence of divalent nickel (Ni(II)) sites in spinel type oxides is associated only with dense deposits. (author)

  2. Polarized Neutron Reflectometry of Nickel Corrosion Inhibitors.

    Science.gov (United States)

    Wood, Mary H; Welbourn, Rebecca J L; Zarbakhsh, Ali; Gutfreund, Philipp; Clarke, Stuart M

    2015-06-30

    Polarized neutron reflectometry has been used to investigate the detailed adsorption behavior and corrosion inhibition mechanism of two surfactants on a nickel surface under acidic conditions. Both the corrosion of the nickel surface and the structure of the adsorbed surfactant layer could be monitored in situ by the use of different solvent contrasts. Layer thicknesses and roughnesses were evaluated over a range of pH values, showing distinctly the superior corrosion inhibition of one negatively charged surfactant (sodium dodecyl sulfate) compared to a positively charged example (dodecyl trimethylammonium bromide) due to its stronger binding interaction with the surface. It was found that adequate corrosion inhibition occurs at significantly less than full surface coverage.

  3. Nickel hydrogen/nickel cadmium battery trade studies

    Science.gov (United States)

    Stadnick, S. J.

    1983-01-01

    Nickel Hydrogen cell and battery technology has matured to the point where a real choice exists between Nickel Hydrogen and Nickel Cadmium batteries for each new spacecraft application. During the past few years, a number of spacecraft programs have been evaluated at Hughes with respect to this choice, with the results being split about fifty-fifty. The following paragraphs contain criteria which were used in making the battery selection.

  4. Nickel ferrule applicators: a source of nickel exposure in children.

    Science.gov (United States)

    Jacob, Sharon E; Silverberg, Jonathan I; Rizk, Christopher; Silverberg, Nanette

    2015-01-01

    Eye makeup has been investigated for nickel content and found to have no direct association with nickel allergy and cosmetic dermatitis. However, the tools used (e.g., eyelash curlers, hairdressing scissors, hair curlers, and eye shadow and makeup applicators) may be sources. Nickel is ubiquitous and a wide range of sources have been reported, and makeup applicators (ferrules) now join the list. © 2015 Wiley Periodicals, Inc.

  5. Corrosion resistance of stainless steel, nickel-titanium, titanium molybdenum alloy, and ion-implanted titanium molybdenum alloy archwires in acidic fluoride-containing artificial saliva: An in vitro study

    Directory of Open Access Journals (Sweden)

    Venith Jojee Pulikkottil

    2016-01-01

    Full Text Available Objective: (1 To evaluate the corrosion resistance of four different orthodontic archwires and to determine the effect of 0.5% NaF (simulating high fluoride-containing toothpaste of about 2250 ppm on corrosion resistance of these archwires. (2 To assess whether surface roughness (Ra is the primary factor influencing the corrosion resistance of these archwires. Materials and Methods: Four different archwires (stainless steel [SS], nickel-titanium [NiTi], titanium molybdenum alloy [TMA], and ion-implanted TMA were considered for this study. Surface characteristics were analyzed using scanning electron microscopy, atomic force microscopy (AFM, and energy dispersive spectroscopy. Linear polarization test, a fast electrochemical technique, was used to evaluate the corrosion resistance, in terms of polarization resistance of four different archwires in artificial saliva with NaF concentrations of 0% and 0.5%. Statistical analysis was performed by one-way analysis of variance. Results: The potentiostatic study reveals that the corrosion resistance of low-friction TMA (L-TMA > TMA > NiTi > SS. AFM analysis showed the surface Ra of TMA > NiTi > L-TMA > SS. This indicates that the chemical composition of the wire is the primary influential factor to have high corrosion resistance and surface Ra is only secondary. The corrosion resistance of all wires had reduced significantly in 0.5% acidic fluoride-containing artificial saliva due to formation of fluoride complex compound. Conclusion: The presence of 0.5% NaF in artificial saliva was detrimental to the corrosion resistance of the orthodontic archwires. Therefore, complete removal of residual high-fluorinated toothpastes from the crevice between archwire and bracket during tooth brushing is mandatory.

  6. Comparison of galvanic corrosion potential of metal injection molded brackets to that of conventional metal brackets with nickel-titanium and copper nickel-titanium archwire combinations.

    Science.gov (United States)

    Varma, D Praveen Kumar; Chidambaram, S; Reddy, K Baburam; Vijay, M; Ravindranath, D; Prasad, M Rajendra

    2013-05-01

    The aim of the study is to investigate the galvanic corrosion potential of metal injection molding (MIM) brackets to that of conventional brackets under similar in vitro conditions with nickel-titanium and copper nickel-titanium archwires. Twenty-five maxillary premolar MIM stainless steel brackets and 25 conventional stainless steel brackets and archwires, 0.16 inch, each 10 mm length, 25 nickeltitanium wires, 25 copper nickel-titanium wires were used. They were divided into four groups which had five samples each. Combination of MIM bracket with copper nickel-titanium wire, MIM bracket with nickel-titanium wire and conventional stainless steel brackets with copper nickel-titanium wire and conventional stainless steel brackets with nickel-titanium wires which later were suspended in 350 ml of 1 M lactic acid solution media. Galvanic corrosion potential of four groups were analyzed under similar in vitro conditions. Precorrosion and postcorrosion elemental composition of MIM and conventional stainless steel bracket by scanning electron microscope (SEM) with energy dispersive spectroscope (EDS) was done. MIM bracket showed decreased corrosion susceptibility than conventional bracket with copper nickeltitanium wire. Both MIM and conventional bracket showed similar corrosion resistance potential in association with nickel-titanium archwires. It seems that both brackets are more compatible with copper nickel-titanium archwires regarding the decrease in the consequences of galvanic reaction. The EDS analysis showed that the MIM brackets with copper nickel-titanium wires released less metal ions than conventional bracket with copper nickeltitanium wires. MIM brackets showed decreased corrosion susceptibility, copper nickel-titanium archwires are compatible with both the brackets than nickel-titanium archwires. Clinically MIM and conventional brackets behaved more or less similarly in terms of corrosion resistance. In order to decrease the corrosion potential of MIM

  7. Nickel base alloys

    International Nuclear Information System (INIS)

    Gibson, R.C.; Korenko, M.K.

    1980-01-01

    Nickel based alloy, the characteristic of which is that it mainly includes in percentages by weight: 57-63 Ni, 7-18 Cr, 10-20 Fe, 4-6 Mo, 1-2 Nb, 0.2-0.8 Si, 0.01-0.05 Zr, 1.0-2.5 Ti, 1.0-2.5 Al, 0.02-0.06 C and 0.002-0.015 B. The aim is to create new nickel-chromium alloys, hardened in a solid solution and by precipitation, that are stable, exhibit reduced swelling and resistant to plastic deformation inside the reactor. These alloys of the gamma prime type have improved mechanical strengthm swelling resistance, structural stability and welding properties compared with Inconel 625 [fr

  8. Nickel accumulation by Hybanthus floribundus

    Energy Technology Data Exchange (ETDEWEB)

    Severne, B C

    1974-04-26

    Several ecotypes of Hybanthus floribundus are found across the southern part of Australia. However, the three nickel accumulating ecotypes are restricted to a broad belt in Western Australia. Nickel concentrations in this shrub were observed to decrease southwards (from 8000 to 1000 p.p.m.) as the annual rainfall increased from 7 inches to more than 30 inches. Studies have shown that nickel concentrations increase from the roots through the rootstock, into the stems and reach maximum towards the leaf tips. High nickel concentrations are also seen in seed capsules (1500 p.p.m.), seeds (2000 p.p.m.) and flowers. The maximum nickel concentration recorded is 1.6% (26% nickel in ash) in mature leaf tissue. 16 references, 2 tables.

  9. Nickel deposited on the skin-visualization by DMG test.

    Science.gov (United States)

    Julander, Anneli; Skare, Lizbet; Vahter, Marie; Lidén, Carola

    2011-03-01

    Nickel is the most common cause of contact allergy and an important risk factor for hand eczema. Visualization techniques may be powerful in showing exposures. The dimethylglyoxime (DMG) test might be used to establish skin exposure to nickel. To develop and evaluate methods for visualization of nickel on the skin by the DMG test and hand imprints. Nickel solutions at different concentrations were applied in duplicate on the hands in healthy subjects (n = 5). The DMG test and acid wipe sampling for quantification were then performed. Hand imprints were taken after manipulation of nickel-releasing tools (n = 1), and in workers performing their normal tasks (n = 7). The imprints were developed by the DMG test. The DMG test on hands gave positive results in all subjects. The lowest concentration giving rise to a colour change was set to 0.13 µg/cm(2) for DMG testing on skin. DMG test-developed imprints worked well except when hands were heavily contaminated by other particles/dust. The DMG test may be used as a simple and powerful tool for visualization of nickel on skin. DMG test-developed hand imprints may, in the future, be used for semi-quantitative or quantitative exposure assessment. © 2011 John Wiley & Sons A/S.

  10. Nickel: makes stainless steel strong

    Science.gov (United States)

    Boland, Maeve A.

    2012-01-01

    Nickel is a silvery-white metal that is used mainly to make stainless steel and other alloys stronger and better able to withstand extreme temperatures and corrosive environments. Nickel was first identified as a unique element in 1751 by Baron Axel Fredrik Cronstedt, a Swedish mineralogist and chemist. He originally called the element kupfernickel because it was found in rock that looked like copper (kupfer) ore and because miners thought that "bad spirits" (nickel) in the rock were making it difficult for them to extract copper from it. Approximately 80 percent of the primary (not recycled) nickel consumed in the United States in 2011 was used in alloys, such as stainless steel and superalloys. Because nickel increases an alloy's resistance to corrosion and its ability to withstand extreme temperatures, equipment and parts made of nickel-bearing alloys are often used in harsh environments, such as those in chemical plants, petroleum refineries, jet engines, power generation facilities, and offshore installations. Medical equipment, cookware, and cutlery are often made of stainless steel because it is easy to clean and sterilize. All U.S. circulating coins except the penny are made of alloys that contain nickel. Nickel alloys are increasingly being used in making rechargeable batteries for portable computers, power tools, and hybrid and electric vehicles. Nickel is also plated onto such items as bathroom fixtures to reduce corrosion and provide an attractive finish.

  11. The accumulation of nickel in human lungs.

    OpenAIRE

    Edelman, D A; Roggli, V L

    1989-01-01

    Using data from published studies, lung concentrations of nickel were compare for persons with and without occupational exposure to nickel. As expected, the concentrations were much higher for persons with occupational exposure. To estimate the effects of nickel-containing tobacco smoke and nickel in the ambient air on the amount of nickel accumulated in lungs over time, a model was derived that took into account various variables related to the deposition of nickel in lungs. The model predic...

  12. Nickel speciation in cement-stabilized/solidified metal treatment filtercakes

    Energy Technology Data Exchange (ETDEWEB)

    Roy, Amitava, E-mail: reroy@lsu.edu [J. Bennett Johnston, Sr., Center for Advanced Microstructures and Devices, Louisiana State University, Baton Rouge, LA 70806, USA (United States); Stegemann, Julia A., E-mail: j.stegemann@ucl.ac.uk [Centre for Resource Efficiency & the Environment, Department of Civil, Environmental & Geomatic Engineering, University College London, Chadwick Building, Gower Street, London WC1E 6BT, UK (United Kingdom)

    2017-01-05

    Highlights: • XAS shows the same Ni speciation in untreated and stabilized/solidified filtercake. • Ni solubility is the same for untreated and stabilized/solidified filtercake. • Leaching is controlled by pH and physical encapsulation for all binders. - Abstract: Cement-based stabilization/solidification (S/S) is used to decrease environmental leaching of contaminants from industrial wastes. In this study, two industrial metal treatment filtercakes were characterized by X-ray diffractometry (XRD), thermogravimetric and differential thermogravimetric analysis (TG/DTG) and Fourier transform infrared (FTIR); speciation of nickel was examined by X-ray absorption (XAS) spectroscopy. Although the degree of carbonation and crystallinity of the two untreated filtercakes differed, α-nickel hydroxide was identified as the primary nickel-containing phase by XRD and nickel K edge XAS. XAS showed that the speciation of nickel in the filtercake was unaltered by treatment with any of five different S/S binder systems. Nickel leaching from the untreated filtercakes and all their stabilized/solidified products, as a function of pH in the acid neutralization capacity test, was essentially complete below pH ∼5, but was 3–4 orders of magnitude lower at pH 8–12. S/S does not respeciate nickel from metal treatment filtercakes and any reduction of nickel leaching by S/S is attributable to pH control and physical mechanisms only. pH-dependent leaching of Cr, Cu and Ni is similar for the wastes and s/s products, except that availability of Cr, Cu and Zn at decreased pH is reduced in matrices containing ground granulated blast furnace slag.

  13. Initial deposition mechanism of electroless nickel plating on AZ91D magnesium alloys

    International Nuclear Information System (INIS)

    Song, Y.; Shan, D.; Han, E.

    2006-01-01

    The pretreatment processes and initial deposition mechanism of electroless nickel plating on AZ91D magnesium alloy were investigated by scanning electron microscopy (SEM) and energy dispersive X-ray (EDX). The results showed that alkaline cleaning could remove the greases and oils from the substrate surface. Acid etching could wipe off the metal chippings and oxides. The hydrofluoric acid activating process which could improve the adhesion of coating to substrate played a key role in the subsequent process of electroless nickel plating. The nickel coating was deposited preferentially on the primary α phase and then spread to the eutectic α phase and β phase. The nickel initially nucleated on the primary α phase by a replacement reaction, then grew depending on the autocatalysis function of nickel. The coating on the β phase displayed better adhesion than that on the α phase due to the nails fixing effect. (author)

  14. Electrolytic Recovery of Nickel from Spent Electroless Nickel Bath Solution

    Directory of Open Access Journals (Sweden)

    R. Idhayachander

    2010-01-01

    Full Text Available Plating industry is one of the largest polluting small scale industries and nickel plating is among the important surface finishing process in this industry. The waste generated during this operation contains toxic nickel. Nickel removal and recovery is of great interest from spent bath for environmental and economic reasons. Spent electroless nickel solution from a reed relay switch manufacturing industry situated in Chennai was taken for electrolytic recovery of nickel. Electrolytic experiment was carried out with mild steel and gold coated mild steel as cathode and the different parameters such as current density, time, mixing and pH of the solution were varied and recovery and current efficiency was studied. It was noticed that there was an increase in current efficiency up to 5 A/dm2 and after that it declines. There is no significant improvement with mixing but with modified cathode there was some improvement. Removal of nickel from the spent electroless nickel bath was 81.81% at 5 A/dm2 and pH 4.23. Under this condition, the content of nickel was reduced to 0.94 g/L from 5.16 g/L. with 62.97% current efficiency.

  15. Template-Assisted Synthesis and Characterization of Passivated Nickel Nanoparticles

    Directory of Open Access Journals (Sweden)

    Al-Omari IA

    2010-01-01

    Full Text Available Abstract Potential applications of nickel nanoparticles demand the synthesis of self-protected nickel nanoparticles by different synthesis techniques. A novel and simple technique for the synthesis of self-protected nickel nanoparticles is realized by the inter-matrix synthesis of nickel nanoparticles by cation exchange reduction in two types of resins. Two different polymer templates namely strongly acidic cation exchange resins and weakly acidic cation exchange resins provided with cation exchange sites which can anchor metal cations by the ion exchange process are used. The nickel ions which are held at the cation exchange sites by ion fixation can be subsequently reduced to metal nanoparticles by using sodium borohydride as the reducing agent. The composites are cycled repeating the loading reduction cycle involved in the synthesis procedure. X-Ray Diffraction, Scanning Electron Microscopy, Transmission Electron microscopy, Energy Dispersive Spectrum, and Inductively Coupled Plasma Analysis are effectively utilized to investigate the different structural characteristics of the nanocomposites. The hysteresis loop parameters namely saturation magnetization and coercivity are measured using Vibrating Sample Magnetometer. The thermomagnetization study is also conducted to evaluate the Curie temperature values of the composites. The effect of cycling on the structural and magnetic characteristics of the two composites are dealt in detail. A comparison between the different characteristics of the two nanocomposites is also provided.

  16. Theoretical investigation of the electronic structure of a substituted nickel phthalocyanine

    Energy Technology Data Exchange (ETDEWEB)

    Kaur, Prabhjot, E-mail: prabhphysics@gmail.com; Sachdeva, Ritika [Department of Physics, Panjab University Chandigarh-160014, Chandigarh (India); Singh, Sukhwinder [Department of Physics, Govt. College for Girls, Ludhiana-141008, Ludhiana (India)

    2016-05-23

    The optimized geometry and electronic structure of an organic compound nickel phthalocyanine tetrasulfonic acid tetra sodium salt have been investigated using density functional theory. We have also optimized the structure of nickel phthalocyanine tetrasulfonic acid tetra sodium salt in dimethyl sulfoxide to study effects of solvent on the electronic structure and transitions. Experimentally, the electronic transitions have been studied using UV-VIS spectroscopic technique. It is observed that the electronic transitions obtained from the theoretical studies generally agree with the experiment.

  17. Laboratory procedure for sizing and electroless nickel plating assembled steel bearings

    International Nuclear Information System (INIS)

    Wright, R.R.; Petit, G.S.

    1976-01-01

    The bearing is placed in a holder and degreased in methyl chloroform. The entire bearing is etched in hydrochloric acid and sized in an ammonium bifluoride-hydrogen peroxide solution (NH 4 F.HF--H 2 O 2 ). The bearing is removed from the holder, activated in hydrochloric acid and plated with 0.001 in. of nickel in a plating tumbler immersed in a heated electroless nickel plating bath. The bearing is water-rinsed and air-dried

  18. Point defects in nickel

    International Nuclear Information System (INIS)

    Peretto, P.

    1969-01-01

    The defects in electron irradiated nickel (20 deg. K) or neutron irradiated nickel (28 deg. K) are studied by simultaneous analysis using the magnetic after-effect, electron microscopy and electrical resistivity recovery. We use zone refined nickel (99.999 per cent) which, for some experiments, is alloyed with a small amount of iron (for example 0.1 per cent Fe). The temperature dependant electrical recovery may be divided in four stages. The sub-stages I B (31 deg. K), I C (42 deg. K), I D (from to 57 deg. K) and I E (62 deg. K) of stage I are due to the disappearance of single interstitials into vacancies. The interstitial defect has a split configuration with a migration energy of about 0.15 eV. In the close pair which disappears in stage I B the interstitial is found to be in a 3. neighbour position whilst in stage I D it is near the direction from the vacancy. In stage I E there is no longer any interaction between the interstitial and the vacancy. The stage II is due to more complicated interstitial defects: di-interstitials for stage II B (84 deg. K) and larger and larger interstitial loops for the following sub-stages. The loops may be seen by electron microscopy. Impurities can play the role of nucleation centers for the loops. Stages III A (370 deg. K) and III B (376 deg. K) are due to two types of di-vacancies. During stage IV (410 deg. K) the single vacancies migrate. Vacancy type loops and interstitial type loops grow concurrently and disappear at about 800 deg. K as observed by electron microscopy. (author) [fr

  19. Nickel, cobalt, and their alloys

    CERN Document Server

    2000-01-01

    This book is a comprehensive guide to the compositions, properties, processing, performance, and applications of nickel, cobalt, and their alloys. It includes all of the essential information contained in the ASM Handbook series, as well as new or updated coverage in many areas in the nickel, cobalt, and related industries.

  20. Synthesis and Electrical Resistivity of Nickel Polymethacrylate

    Science.gov (United States)

    Chohan, M. H.; Khalid, A. H.; Zulfiqar, M.; Butt, P. K.; Khan, Farah; Hussain, Rizwan

    Synthesis of nickel polymethacrylate was carried out using methanolic solutions of sodium hydroxide and polymethacrylic acid. The electrical resistivity of the pellets made from Ni-polymethacrylate was measured at different voltages and temperatures. Results showed that the electrical resistivity of Ni-polymethacrylate decreases significantly with voltage in high temperature regions but the decrease is insignificant at temperatures nearing room temperature. The activation energy at low temperatures is approximately 0.8 eV whereas at high temperature it is in the range 0.21-0.27 eV.

  1. Characterization and assessment of dermal and inhalable nickel exposures in nickel production and primary user industries.

    Science.gov (United States)

    Hughson, G W; Galea, K S; Heim, K E

    2010-01-01

    The aim of this study was to measure the levels of nickel in the skin contaminant layer of workers involved in specific processes and tasks within the primary nickel production and primary nickel user industries. Dermal exposure samples were collected using moist wipes to recover surface contamination from defined areas of skin. These were analysed for soluble and insoluble nickel species. Personal samples of inhalable dust were also collected to determine the corresponding inhalable nickel exposures. The air samples were analysed for total inhalable dust and then for soluble, sulfidic, metallic, and oxidic nickel species. The workplace surveys were carried out in five different workplaces, including three nickel refineries, a stainless steel plant, and a powder metallurgy plant, all of which were located in Europe. Nickel refinery workers involved with electrolytic nickel recovery processes had soluble dermal nickel exposure of 0.34 microg cm(-2) [geometric mean (GM)] to the hands and forearms. The GM of soluble dermal nickel exposure for workers involved in packing nickel salts (nickel chloride hexahydrate, nickel sulphate hexahydrate, and nickel hydroxycarbonate) was 0.61 microg cm(-2). Refinery workers involved in packing nickel metal powders and end-user powder operatives in magnet production had the highest dermal exposure (GM = 2.59 microg cm(-2) soluble nickel). The hands, forearms, face, and neck of these workers all received greater dermal nickel exposure compared with the other jobs included in this study. The soluble nickel dermal exposures for stainless steel production workers were at or slightly above the limit of detection (0.02 microg cm(-2) soluble nickel). The highest inhalable nickel concentrations were observed for the workers involved in nickel powder packing (GM = 0.77 mg m(-3)), although the soluble component comprised only 2% of the total nickel content. The highest airborne soluble nickel exposures were associated with refineries using

  2. The potential use of rainwater as alternative source of drinking water by using laterite soil as natural adsorbent

    Science.gov (United States)

    Omar, Khairunnisa Fakhriah Mohd; Palaniandy, Puganeshwary; Adlan, Mohd Nordin; Aziz, Hamidi Abdul; Subramaniam, Ambarasi

    2017-10-01

    Generally, the rainwater has low concentration of pollutants, whereby it is applicable for domestic water supply. Due to the low concentration of pollutants, further treatment such as adsorption is necessary to treat the harvested rainwater as an alternative source of drinking water supply. Therefore, this research has been carried out to determine the quality of rainwater from different types of locations, which are; rural residential area, urban residential area, agricultural area, industrial area, and open surface. The rainwater sampling was carried out from September 2014 to December 2015. The parameters that have been analysed during the sampling process are chemical oxygen demand (COD), turbidity, heavy metals, and Escherichia coli (E.coli). The sampling results show that the rainwater provides low concentration of contaminants. Thus, it has high potential to be used as alternative source of potable and non potable water supply with a suitable treatment. Due to that, an experimental work contained of 86 of designated experiments for a batch study has been carried out to determine the performance of laterite soil as an adsorbent to remove pollutants that present in the rainwater (i.e. zinc, manganese, and E.coli). The operating factors involved in the experimental works are pH, mass of adsorbents, contact time, initial concentration of zinc, manganese, and E.coli. In this study, the experimental data of the batch study was analysed by developing regression model equation and analysis of variance. Perturbation plots were analysed to determine the effectiveness of the operating factors by developing response surface model, resulting that the high removals of zinc, manganese, and E.coli are 95.8%, 94.05% and 100%, respectively. Overall, this research works found out that the rainwater has a good quality as alternative source of drinking water by providing a suitable treatment. The application of laterite soil as natural adsorbent shows that it has potential to be

  3. Discovery of Ni-smectite-rich saprolite at Loma Ortega, Falcondo mining district (Dominican Republic): geochemistry and mineralogy of an unusual case of "hybrid hydrous Mg silicate - clay silicate" type Ni-laterite

    Science.gov (United States)

    Tauler, Esperança; Lewis, John F.; Villanova-de-Benavent, Cristina; Aiglsperger, Thomas; Proenza, Joaquín A.; Domènech, Cristina; Gallardo, Tamara; Longo, Francisco; Galí, Salvador

    2017-10-01

    Hydrous Mg silicate-type Ni-laterite deposits, like those in the Falcondo district, Dominican Republic, are dominated by Ni-enriched serpentine and garnierite. Recently, abundant Ni-smectite in the saprolite zone have been discovered in Loma Ortega, one of the nine Ni-laterite deposits in Falcondo. A first detailed study on these Ni-smectites has been performed (μXRD, SEM, EPMA), in addition to a geochemical and mineralogical characterisation of the Loma Ortega profile (XRF, ICP-MS, XRD). Unlike other smectite occurrences in laterite profiles worldwide, the Loma Ortega smectites are trioctahedral and exhibit high Ni contents never reported before. These Ni-smectites may be formed from weathering of pyroxene and olivine, and their composition can be explained by the mineralogy and the composition of the Al-depleted, olivine-rich parent ultramafic rock. Our study shows that Ni-laterites are mineralogically complex, and that a hydrous Mg silicate ore and a clay silicate ore can be confined to the same horizon in the weathering profile, which has significant implications from a recovery perspective. In accordance, the classification of "hybrid hydrous Mg silicate - clay silicate" type Ni-laterite deposit for Loma Ortega would be more appropriate.

  4. Syntheses, X-ray, MSn, NMR and CD structure determination of nickel(II) complexes of Schiff bases of (S)-N-(2-benzoylphenyl)-1-benzylpyrrolidine-2-carboxamide and aromatic alpha-amino acids

    NARCIS (Netherlands)

    Nadvornik, Milan; Langer, Vratislav; Jirasko, Robert; Holcapek, Michal; Weidlich, Tomas; Lycka, Antonin; Popkov, Alexander

    2008-01-01

    A preparative procedure for the synthesis of an important chiral synthon of side-chain protected tyrosine was developed and optimised for the minimisation of nickel salts waste. While preparing a similar side-chain protected tryptophan synthon, an unexpected low stability was found of the

  5. Nickel Excretion in Urine after Oral Administration

    DEFF Research Database (Denmark)

    Menne, T.; Mikkelsen, H. I.; Solgaard, Per Bent

    1978-01-01

    In recent years the importance of internal exposure to nickel in patients with recurrent hand eczema and nickel allergy has become evident. The present study was performed in order to investigate the value of urinary nickel determinations as an index of oral nickel intake. After oral administration...

  6. Drinking water pollution with nickel from water boilers; Nickel-Eintrag aus Wasserkochern ins Trinkwasser

    Energy Technology Data Exchange (ETDEWEB)

    Helmers, E. [Amt fuer Umweltschutz, Stuttgart (Germany). Chemisches Inst.

    1998-07-01

    The EU is planning to drop the threshold value for nickel in drinking water down to 20 {mu}g/l (present German threshold value: 50 {mu}g/l). Since ICP-MS-screenings of spot checks of water cookers were striking with respect to nickel, emissions of electrical water cookers have been investigated systematically within this study. As a result, water cookers with open heating coils are emitting relevant amounts of nickel into the water while it is brought to the boil. Investigation of eight preused water cookers with open heating coils revealed that the boiled water contained more than 50 {mu}g Ni/l in one case, more than 20 {mu}g Ni/l in two cases and, between 10 and 20 {mu}g Ni/l in two more cases, respectively. Removing of the lime by the aid of citric acid is increasing the nickel concentrations by a factor of up to 50 (max. 640 {mu}g/l). A new device was checked in a long-term test. During standard use with tapwater, Ni concentrations fall below the detection limit of 5 {mu}g Ni/l (120 cooking events). However, after removing of the lime, 5 times of cooking were necessary in order to diminish the Ni concentrations below the limit of 20 {mu}g/l. In the case of dionized water Ni concentrations below the limit of 20 {mu}g/l. In the case of deionized water Ni concentrations remained between 94 und 190 {mu}g/l. Health risk assessment: The intake of nickel with beverages made from hot water out of these cookers is in the range of 26 {mu}g/day. Considering an alltogether dietary nickel intake of 130-170 (900) {mu}g/day, this is not beyond the scope. However, according to the fact that nickel allergies (dermatitis) are very frequent (up to 13% of the population), this source should be limited or closed. (orig.) [Deutsch] Aus Anlass der geplanten Absenkung des Trinkwassergrenzwertes fuer Nickel auf 20 {mu}g/l sowie aufgrund von Auffaelligkeiten bei Stichprobenuntersuchungen wurde das Nickel-Emissionsverhalten von elektrischen Wassererhitzern betrachtet. Hierbei erwies sich

  7. High calcium fly ash geopolymer stabilized lateritic soil and granulated blast furnace slag blends as a pavement base material.

    Science.gov (United States)

    Phummiphan, Itthikorn; Horpibulsuk, Suksun; Rachan, Runglawan; Arulrajah, Arul; Shen, Shui-Long; Chindaprasirt, Prinya

    2018-01-05

    Granulated Blast Furnace Slag (GBFS) was used as a replacement material in marginal lateritic soil (LS) while class C Fly Ash (FA) was used as a precursor for the geopolymerization process to develop a low-carbon pavement base material at ambient temperature. Unconfined Compression Strength (UCS) tests were performed to investigate the strength development of geopolymer stabilized LS/GBFS blends. Scanning Electron Microscopy and X-ray Diffraction analysis were undertaken to examine the role of the various influencing factors on UCS development. The influencing factors studied included GBFS content, Na 2 SiO 3 :NaOH ratio (NS:NH) and curing time. The 7-day soaked UCS of FA geopolymer stabilized LS/GBFS blends at various NS:NH ratios tested was found to satisfy the specifications of the Thailand national road authorities. The GBFS replacement was found to be insignificant for the improvement of the UCS of FA geopolymer stabilized LS/GBFS blends at low NS:NH ratio of 50:50. Microstructural analysis indicated the coexistence of Calcium Silicate Hydrate (CSH) and Sodium Alumino Silicate Hydrate products in FA geopolymer stabilized LS/GBFS blends. This research enables GBFS, which is traditionally considered as a waste material, to be used as a replacement and partially reactive material in FA geopolymer pavement applications. Copyright © 2017 Elsevier B.V. All rights reserved.

  8. On the Origin of Bastnaesite-(La,Nd,Y in the Nissi (Patitira Bauxite Laterite Deposit, Lokris, Greece

    Directory of Open Access Journals (Sweden)

    Sofia Kalatha

    2017-03-01

    Full Text Available A detailed geochemical study and a thorough mineralogical description of the rare-earth elements (REE-minerals and associated minerals were carried out in two vertical profiles of approximately 4 m length, from the Nissi (Patitira bauxite laterite deposit, Lokris, Greece, characterized by the presence of goethite in small sizes resembling bacterial cell coated by goethite and a significant REE enrichment. The enrichment of the REE concentrated in bastnaesite-group minerals, the intergrowths between REE-minerals and Al–Ni–silicates with significant sulfur contents and their association with goethite microtextures interpreted as bacteriomorphic, indicate REE remobilization along with iron bio-leaching and re-precipitation on karstified limestone. In addition to the previous-reported hydroxylbastnaesites, a (La,Nd,Y(CO3F member of the bastnaesite-group associated with Al–Ni–silicates were identified, the stability of which may reflect the dependence on the source rocks and the local variations of pH-Eh. Interaction between downward percolating water and carbonate rocks seems to be a very effective mechanism for REE fluorocarbonates deposition under alkaline and reducing conditions.

  9. Nickel aggregates produced by radiolysis

    International Nuclear Information System (INIS)

    Marignier, J.L.; Belloni, J.

    1988-01-01

    Nickel aggregates with subcolloidal size and stable in water have been synthesized by inhibiting the corrosion by the medium. The protective effect of the surfactant is discussed in relation with the characteristics of various types of polyvinyl alcohol studied. The reactivity of aggregates towards oxidizing compounds, nitro blue tetrazolium, methylene blue, silver ions, oxygen, methylviologen, enables an estimation of the redox potential of nickel aggregates (E = - 04 ± 0.05 V). It has been applied to quantitative analysis of the particles in presence of nickel ions. 55 refs [fr

  10. Mechanisms of nickel toxicity in microorganisms

    OpenAIRE

    Macomber, Lee; Hausinger, Robert P.

    2011-01-01

    Nickel has long been known to be an important human toxicant, including having the ability to form carcinomas, but until recently nickel was believed to be an issue only to microorganisms living in nickel-rich serpentine soils or areas contaminated by industrial pollution. This assumption was overturned by the discovery of a nickel defense system (RcnR/RcnA) found in microorganisms that live in a wide range of environmental niches, suggesting that nickel homeostasis is a general biological co...

  11. Respiratory carcinogenicity assessment of soluble nickel compounds.

    OpenAIRE

    Oller, Adriana R

    2002-01-01

    The many chemical forms of nickel differ in physicochemical properties and biological effects. Health assessments for each main category of nickel species are needed. The carcinogenicity assessment of water-soluble nickel compounds has proven particularly difficult. Epidemiologic evidence indicates an association between inhalation exposures to nickel refinery dust containing soluble nickel compounds and increased risk of respiratory cancers. However, the nature of this association is unclear...

  12. Mercury and nickel contents in fish meat

    Directory of Open Access Journals (Sweden)

    Tomas Toth

    2016-10-01

    Full Text Available The main aim of our work was to identify the content of mercury and nickel in selected fish species. Consumers today are increasingly aware of the association between diet and health, and thus in Europe consume more and more fish. Fish is a valuable source of high quality protein, minerals and vitamins, and fatty fish are also rich in omega-3-polyunsaturated fatty acids, which are normally considered to be beneficial to health. In our work we determined content of mercury and nickel harvested fish in particular were the following species: Common goldfish (Carassius auratus, L., Common roach (Rutilus rutilus, L. and Common bream (Abramis brama, L. Concentrations of mercury and nickel was analyzed and results evaluated according to current standards and compared to the values ​​established by the Codex Alimentarius of the Slovak Republic and the EU Commission Regulation no. 1881/2006, as well as in the EU Commission Regulation no. 420/2011 and no. 269/2008. In our research area we analysed 19 samples of fish muscle. Samples were taken from two water reservoirs – Golianovo and Vráble.  The highest mercury content was in sample Rutilus 1 - 0.052632 mg/kg. Lowest mercury content was in sample Abramis 2  - 0.010431 mg/kg. Largest nickel content was in meat of Abramis  - sample 2  - 0.78 mg/kg. Minimum content of nickel was in sample Carassius 1  - 0.11 mg/kg. We got out of the limit values ​​specified: Codex Alimentarius SR - Mercury 0.5 mg/kg and  Regulation of the EU Commission no. 1881/2006, no. 420/2011 and no. 629/2008. To optimize the protection of the population, it is necessary to continue to monitor the concentration of mercury in fish and fish products. Risk management strategy must focus on reducing potential exposure derived from consumption of fish. In particular, the definition of maximum levels for methylmercury, advising consumers and environmental activities oriented to reduce contamination.

  13. Spectrochemical analysis of impurities in nickel and in nickel oxide

    International Nuclear Information System (INIS)

    Goldbart, Z.; Lorber, A.; Harel, A.

    1981-11-01

    Various spectrochemical methods are described for the quantitative determination of 23 impurities in metallic nickel and in nickel oxide. The average limit of detection is from 1 to 5 ppm and the dynamic range lies over 2.5 orders of magnitude. The elements that were determined are: Al,B,Ba,Bi,Ca,Cd,Co,Cu,Fe,Ga,Ge,In,Mg,Mn,Mo,Nb,Si,Sn,Sr,Ti,Cr,V. (author)

  14. Removing nickel from nickel-coated carbon fibers

    Science.gov (United States)

    Hardianto, A.; Hertleer, C.; De Mey, G.; Van Langenhove, L.

    2017-10-01

    Conductive fibers/yarns are one of the most important materials for smart textiles because of their electrically conductive functionality combined with flexibility and light weight. They can be applied in many fields such as the medical sector, electronics, sensors and even as thermoelectric generators. Temperature sensors, for example, can be made using the thermocouple or thermopile principle which usually uses two different metal wires that can produce a temperature-dependent voltage. However, if metal wires are inserted into a textile structure, they will decrease the flexibility properties of the textile product. Nickel-coated Carbon Fiber (NiCF), a conductive textile yarn, has a potential use as a textile-based thermopile if we can create an alternating region of carbon and nickel along the fiber which in turn it can be used for substituting the metallic thermopile. The idea was to remove nickel from NiCF in order to obtain a yarn that contains alternating zones of carbon and nickel. Due to no literature reporting on how to remove nickel from NiCF, in this paper we investigated some chemicals to remove nickel from NiCF.

  15. Reconstruction of Post-Deccan topographies from mapping of relict lateritic paleosurfaces: Implications for long-term denudation of Peninsular India

    Science.gov (United States)

    Jean, Amandine; Beauvais, Anicet; Chardon, Dominique; Bonnet, Nicolas; Mudlappa, Jayananda; Janwari, Shazia; Mathé, Pierre-Etienne

    2017-04-01

    Cenozoic topographic rejuvenation of divergent continental margins and their cratonic hinterland is a matter of debate. For instance, continental scale tilt has been advocated as a cause of Late Cenozoic relief growth of the Indian Peninsula. Our work aims at providing independent geomorphological constraints to test such assertions. The western margin of the Peninsula bears the Western Ghats Escarpment (WGE), which carves both Precambrian rocks and 65 Ma old Deccan Traps. The escarpment separates a narrow coastal lowland plain drained to the Arabian Sea from a highland plateau drained towards the Bengal Sea. Alternating and coupled chemical weathering and erosion led to formation and dissection of lateritic paleolandscapes preserved both sides of the WGE. In the highland, the relicts of three distinctive lateritic surfaces are recognized. They formed successively from 53 Ma to 23 Ma on the basis of ages obtained by Ar-Ar dating of K-rich manganese oxides [1]. The first surface is topped by a duricrust rich in Al (bauxite) forming mesas at altitudes of 960 to 1400 m. The second surface called "Intermediate" is mantled by a ferricrete, whose relicts remain 100 m below the bauxite at altitudes of 850 to 1250 m. The third surface corresponds to the relicts of a lateritic pediment, which may be capped by a ferricrete at altitudes of 600 to 900 m. Three lateritic surfaces have been documented in the lowland. The Ar-Ar ages obtained indicate common lateritic weathering in both the highland and the lowland between at 53-45 Ma, then a divergence later on [1]. The oldest remnants of lateritic surface in the lowland are preserved at maximum elevation of 400-500 m close to the WGE and correspond to a pediment. This ancient landform was re-altered at 24-19 Ma to form residual hills of the "Intermediate" relief (ca. 350-200 m). A younger pediment formed around the residual hills and is preserved at ca. 150-50 m elevation. Relicts' elevations of the three surfaces have been

  16. Excessive nickel release from mobile phones--a persistent cause of nickel allergy and dermatitis

    DEFF Research Database (Denmark)

    Jensen, Peter; Johansen, Jeanne D; Zachariae, Claus

    2011-01-01

    Despite the political intention to limit nickel allergy and dermatitis in Europeans, nickel allergy remains frequent. There are several explanations for the persistence of nickel allergy and dermatitis, including the increasing use of mobile phones. Before regulation of nickel release from mobile...... phones, we showed that eight (19.5%) of 41 mobile phones marketed in Denmark between 2003 and 2007 released nickel in concentrations that may result in nickel allergy and dermatitis. In 2009, the EU Nickel Directive was revised to include nickel-releasing mobile phones....

  17. Excessive nickel release from mobile phones--a persistent cause of nickel allergy and dermatitis

    DEFF Research Database (Denmark)

    Jensen, Peter; Johansen, Jeanne D; Zachariae, Claus

    2011-01-01

    phones, we showed that eight (19.5%) of 41 mobile phones marketed in Denmark between 2003 and 2007 released nickel in concentrations that may result in nickel allergy and dermatitis. In 2009, the EU Nickel Directive was revised to include nickel-releasing mobile phones.......Despite the political intention to limit nickel allergy and dermatitis in Europeans, nickel allergy remains frequent. There are several explanations for the persistence of nickel allergy and dermatitis, including the increasing use of mobile phones. Before regulation of nickel release from mobile...

  18. Nickel Hydrogen Battery Expert System

    Science.gov (United States)

    Johnson, Yvette B.; Mccall, Kurt E.

    1992-01-01

    The Nickel Cadmium Battery Expert System-2, or 'NICBES-2', which was used by the NASA HST six-battery testbed, was subsequently converted into the Nickel Hydrogen Battery Expert System, or 'NICHES'. Accounts are presently given of this conversion process and future uses being contemplated for NICHES. NICHES will calculate orbital summary data at the end of each orbit, and store these files for trend analyses and rules-generation.

  19. Solution-processed copper-nickel nanowire anodes for organic solar cells

    Science.gov (United States)

    Stewart, Ian E.; Rathmell, Aaron R.; Yan, Liang; Ye, Shengrong; Flowers, Patrick F.; You, Wei; Wiley, Benjamin J.

    2014-05-01

    This work describes a process to make anodes for organic solar cells from copper-nickel nanowires with solution-phase processing. Copper nanowire films were coated from solution onto glass and made conductive by dipping them in acetic acid. Acetic acid removes the passivating oxide from the surface of copper nanowires, thereby reducing the contact resistance between nanowires to nearly the same extent as hydrogen annealing. Films of copper nanowires were made as oxidation resistant as silver nanowires under dry and humid conditions by dipping them in an electroless nickel plating solution. Organic solar cells utilizing these completely solution-processed copper-nickel nanowire films exhibited efficiencies of 4.9%.This work describes a process to make anodes for organic solar cells from copper-nickel nanowires with solution-phase processing. Copper nanowire films were coated from solution onto glass and made conductive by dipping them in acetic acid. Acetic acid removes the passivating oxide from the surface of copper nanowires, thereby reducing the contact resistance between nanowires to nearly the same extent as hydrogen annealing. Films of copper nanowires were made as oxidation resistant as silver nanowires under dry and humid conditions by dipping them in an electroless nickel plating solution. Organic solar cells utilizing these completely solution-processed copper-nickel nanowire films exhibited efficiencies of 4.9%. Electronic supplementary information (ESI) available. See DOI: 10.1039/c4nr01024h

  20. Electrocatalytic oxidation of some anti-inflammatory drugs on a nickel hydroxide-modified nickel electrode

    Energy Technology Data Exchange (ETDEWEB)

    Hajjizadeh, M. [Department of Chemistry, Faculty of Science, K. N. Toosi University of Technology, P.O. Box 16315-1618, Tehran (Iran, Islamic Republic of); Jabbari, A. [Department of Chemistry, Faculty of Science, K. N. Toosi University of Technology, P.O. Box 16315-1618, Tehran (Iran, Islamic Republic of)], E-mail: jabbari@kntu.ac.ir; Heli, H.; Moosavi-Movahedi, A.A. [Institute of Biochemistry and Biophysics, University of Tehran, Tehran (Iran, Islamic Republic of); Haghgoo, S. [Center of Quality Control of Drug, Tehran (Iran, Islamic Republic of)

    2007-12-31

    The electrocatalytic oxidation of several anti-inflammatory drugs (mefenamic acid, diclofenac and indomethacin) was investigated on a nickel hydroxide-modified nickel (NHMN) electrode in alkaline solution. This oxidation process and its kinetics were studied using cyclic voltammetry, chronoamperometry, and electrochemical impedance spectroscopy techniques. Voltammetric studies indicated that in the presence of drugs, the anodic peak current of low-valence nickel species increases, followed by a decrease in the corresponding cathodic current. This pattern indicates that drugs were oxidized on the redox mediator immobilized on the electrode surface via an electrocatalytic mechanism. A mechanism based on the electrochemical generation of Ni(III) active sites and their subsequent consumption by drugs was also investigated. The corresponding rate law under the control of charge transfer was developed and kinetic parameters were derived. In this context, the charge-transfer resistance accessible both theoretically and through impedancemetry was used as a criterion. The rate constants of the catalytic oxidation of drugs and the electron-transfer coefficients are reported. A sensitive, simple and time-saving amperometric procedure was developed for the analysis of these drugs in bulk form and for the direct assay of tablets, using the NHMN electrode.

  1. Electrocatalytic oxidation of some anti-inflammatory drugs on a nickel hydroxide-modified nickel electrode

    International Nuclear Information System (INIS)

    Hajjizadeh, M.; Jabbari, A.; Heli, H.; Moosavi-Movahedi, A.A.; Haghgoo, S.

    2007-01-01

    The electrocatalytic oxidation of several anti-inflammatory drugs (mefenamic acid, diclofenac and indomethacin) was investigated on a nickel hydroxide-modified nickel (NHMN) electrode in alkaline solution. This oxidation process and its kinetics were studied using cyclic voltammetry, chronoamperometry, and electrochemical impedance spectroscopy techniques. Voltammetric studies indicated that in the presence of drugs, the anodic peak current of low-valence nickel species increases, followed by a decrease in the corresponding cathodic current. This pattern indicates that drugs were oxidized on the redox mediator immobilized on the electrode surface via an electrocatalytic mechanism. A mechanism based on the electrochemical generation of Ni(III) active sites and their subsequent consumption by drugs was also investigated. The corresponding rate law under the control of charge transfer was developed and kinetic parameters were derived. In this context, the charge-transfer resistance accessible both theoretically and through impedancemetry was used as a criterion. The rate constants of the catalytic oxidation of drugs and the electron-transfer coefficients are reported. A sensitive, simple and time-saving amperometric procedure was developed for the analysis of these drugs in bulk form and for the direct assay of tablets, using the NHMN electrode

  2. EPIDEMIOLOGICAL AND PATHOGENETIC ASPECTS OF NICKEL POISONING

    Directory of Open Access Journals (Sweden)

    Vladmila Bojanic

    2007-04-01

    Full Text Available Nickel is widely distributed in the environment. High consumption of nickel containing products inevitably leads to environmental pollution by nickel and its derivatives at all stages of production, utilization, and disposal.Human exposure to nickel occurs primarily via inhalation and ingestion and is particularly high among nickel metallurgy workers. In addition, implantation of nickel-containing endoprostheses and iatrogenic administration of nickel-contaminated medica-tions leads to significant parenteral exposures. Exposure to nickel compounds can produce a variety of adverse effects on human health. Nickel allergy in the form of contact dermatitis is the most common reaction.A frontal headache, vertigo, nausea, vomiting, insomnia, and irritability are the most common signs of acute poisoning with nickel compounds. The respiratory tract, kidneys and liver suffer the most significant changes like nickel pneumoconiosis, chronic rhinitis and sinonasal tumors and transitory nephropathy. Although the accumulation of nickel in the body through chronic exposure can lead to lung fibrosis, cardiovascular and kidney diseases, the most serious concerns relate to nickel’s carcinogenic activity. Nickel compounds are carcinogenic to humans and metallic nickel is possibly carcinogenic to humans.

  3. Relationship between nickel allergy and diet

    Directory of Open Access Journals (Sweden)

    Sharma Ashimav

    2007-01-01

    Full Text Available Nickel is a ubiquitous trace element and it occurs in soil, water, air and of the biosphere. It is mostly used to manufacture stainless steel. Nickel is the commonest cause of metal allergy. Nickel allergy is a chronic and recurring skin problem; females are affected more commonly than males. Nickel allergy may develop at any age. Once developed, it tends to persist life-long. Nickel is present in most of the dietary items and food is considered to be a major source of nickel exposure for the general population. Nickel content in food may vary considerably from place to place due to the difference in nickel content of the soil. However, certain foods are routinely high in nickel content. Nickel in the diet of a nickel-sensitive person can provoke dermatitis. Careful selection of food with relatively low nickel concentration can bring a reduction in the total dietary intake of nickel per day. This can influence the outcome of the disease and can benefit the nickel sensitive patient.

  4. Synthesis and dissolution studies of nickel ferrite in PDCA based formulations

    International Nuclear Information System (INIS)

    Ranganathan, S.; Raghavan, P.S.; Gopalan, R.; Srinivasan, M.P.; Narasimhan, S.V.

    2000-01-01

    Nickel ferrite is one of the important corrosion product in the pipeline surfaces of water cooled nuclear reactors. The dissolution of the nickel ferrite by chelating agents is very sensitive to nature of the chelant, nature of the reductant used in the formulation and the temperature at which the dissolution studies have been performed. The dissolution is dominated by the adsorption of the complexing agent at the oxide surface, but mainly controlled by the reductive dissolution of the ferrite particles. This is due to the in situ release of Fe 2+ ions or the generation of Fe 2+ ions by the reduction of Fe 3+ ions by the reductants in the solution. This study deals with the leaching of iron and nickel from nickel ferrite prepared by the solid state method. The prepared nickel ferrite samples are characterised by XRD to confirm the ferrite formation. The dissolution studies are performed in PDCA formulations containing organic reductants like ascorbic acid and LOMI reductants like Fe(II)-PDCA. The dissolution rate of nickel ferrite at 85degC increased with the increase of Fe 2+ ion content in the crystal lattice. Fe(II)-PDCA was found to be better reductants in dissolving the nickel ferrite in comparison with ascorbic acid. (author)

  5. Nickel stabilization efficiency of aluminate and ferrite spinels and their leaching behavior.

    Science.gov (United States)

    Shih, Kaimin; White, Tim; Leckie, James O

    2006-09-01

    Stabilization efficiencies of spinel-based construction ceramics incorporating simulated nickel-laden waste sludge were evaluated and the leaching behavior of products investigated. To simulate the process of immobilization, nickel oxide was mixed alternatively with gamma-alumina, kaolinite, and hematite. These tailoring precursors are commonly used to prepare construction ceramics in the building industry. After sintering from 600 to 1480 degrees C at 3 h, the nickel aluminate spinel (NiAl204) and the nickel ferrite spinel (NiFe204) crystallized with the ferrite spinel formation commencing about 200-300 degrees C lower than for the aluminate spinel. All the precursors showed high nickel incorporation efficiencies when sintered at temperatures greater than 1250 degrees C. Prolonged leach tests (up to 26 days) of product phases were carried out using a pH 2.9 acetic acid solution, and the spinel products were invariably superior to nickel oxide for immobilization over longer leaching periods. The leaching behavior of NiAl2O4 was consistent with congruent dissolution without significant reprecipitation, but for NiFe2O4, ferric hydroxide precipitation was evident. The major leaching reaction of sintered kaolinite-based products was the dissolution of cristobalite rather than NiAl2O4. This study demonstrated the feasibility of transforming nickel-laden sludge into spinel phases with the use of readily available and inexpensive ceramic raw materials, and the successful reduction of metal mobility under acidic environments.

  6. The EU Nickel Directive revisited--future steps towards better protection against nickel allergy

    DEFF Research Database (Denmark)

    Thyssen, Jacob P; Uter, Wolfgang; McFadden, John

    2011-01-01

    In July 2001, the EU Nickel Directive came into full force to protect European citizens against nickel allergy and dermatitis. Prior to this intervention, Northern European governments had already begun to regulate consumer nickel exposure. According to part 2 of the EU Nickel Directive and the D......In July 2001, the EU Nickel Directive came into full force to protect European citizens against nickel allergy and dermatitis. Prior to this intervention, Northern European governments had already begun to regulate consumer nickel exposure. According to part 2 of the EU Nickel Directive...... and the Danish nickel regulation, consumer items intended to be in direct and prolonged contact with the skin were not allowed to release more than 0.5 µg nickel/cm2/week. It was considered unlikely that nickel allergy would disappear altogether as a proportion of individuals reacted below the level defined...

  7. Relationship between nickel allergy and diet

    OpenAIRE

    Sharma Ashimav

    2007-01-01

    Nickel is a ubiquitous trace element and it occurs in soil, water, air and of the biosphere. It is mostly used to manufacture stainless steel. Nickel is the commonest cause of metal allergy. Nickel allergy is a chronic and recurring skin problem; females are affected more commonly than males. Nickel allergy may develop at any age. Once developed, it tends to persist life-long. Nickel is present in most of the dietary items and food is considered to be a major source of nickel exposure for the...

  8. Fibrous Platinum-Group Minerals in “Floating Chromitites” from the Loma Larga Ni-Laterite Deposit, Dominican Republic

    Directory of Open Access Journals (Sweden)

    Thomas Aiglsperger

    2016-11-01

    Full Text Available This contribution reports on the observation of enigmatic fibrous platinum-group minerals (PGM found within a chromitite body included in limonite (“floating chromitite” from Ni-laterites in the Dominican Republic. Fibrous PGM have a Ru-Os-Ir-Fe dominated composition and are characterized by fibrous textures explained by grain-forming fibers which are significantly longer (1–5 µm than they are wide (~100 nm. Back-scattered electron (BSE images suggest that these nanofibers are platinum-group elements (PGE-bearing and form <5 µm thick layers of bundles which are oriented orthogonal to grains’ surfaces. Trace amounts of Si are most likely associated with PGE-bearing nanofibers. One characteristic fibrous PGM was studied in detail: XRD analyses point to ruthenian hexaferrum. However, the unpolished fibrous PGM shows numerous complex textures on its surface which are suggestive for neoformation processes: (i features suggesting growth of PGE-bearing nanofibers; (ii occurrence of PGM nanoparticles within film material (biofilm? associated with PGE-bearing nanofibers; (iii a Si-rich and crater-like texture hosting PGM nanoparticles and an Ir-rich accumulation of irregular shape; (iv complex PGM nanoparticles with ragged morphologies, resembling sponge spicules and (v oval forms (<1 µm in diameter with included PGM nanoparticles, similar to those observed in experiments with PGE-reducing bacteria. Fibrous PGM found in the limonite may have formed due to supergene (bio-weathering of fibrous Mg-silicates which were incorporated into desulphurized laurite during stages of serpentinization.

  9. A socio-economic study along with impact assessment for laterite based technology demonstration for arsenic mitigation.

    Science.gov (United States)

    Mondal, Sourav; Roy, Anirban; Mukherjee, Raka; Mondal, Mrinmoy; Karmakar, Sankha; Chatterjee, Somak; Mukherjee, Munmun; Bhattacharjee, Saikat; De, Sirshendu

    2017-04-01

    Arsenic contamination mitigation technologies have been adsorption-based, but the most widely-used and traditionally available adsorbents suffered inherent limitations, including cost infeasibility and problems associated with regeneration and disposal of the spent adsorbent. The present technology is based on indigenously developed activated laterite prepared from the naturally and abundantly available material, and can hence easily be scaled up for community usage and large scale implementation. The total arsenic removal capacity is 32.5mg/g, which is the highest among all naturally occurring arsenic adsorbents. A major issue in earlier adsorbents was that during regeneration, the adsorbed arsenic would be released back into the environment (leaching), and would eventually contaminate the groundwater again. But the adsorbent in this filter does not require regeneration during its five-year lifespan and does not leach upon disposal. An attempt is made to test and demonstrate the practical implementation of the technology - its effectiveness and viability in three community (primary schools - one in Malda and two in north 24 Parganas, West Bengal, India) and 20 household filters, catering to over 5000 people in different areas of West Bengal exposed to high arsenic contamination of groundwater (ranging from 0.05 to 0.5mg/l). The work also focuses on the social impact of the real life technological solution on the lives on the affected people in the worst hit arsenic affected communities, perhaps the greatest public health risk emergency of the decade. Copyright © 2017 Elsevier B.V. All rights reserved.

  10. Effects of wood saw dust ash admixed with treated sisal fibre on the geotechnical properties of lateritic soil

    Directory of Open Access Journals (Sweden)

    John Engbonye SANI

    2017-12-01

    Full Text Available The preliminary investigation conducted on the lateritic soil collected at Shika, Zaria shows that it falls under A-7-6 (10 classification for AASHTO (1986 and CL according to unified soil classification system USCS (ASTM 1992. The soil was treated with both wood saw dust ash (WSDA and treated sisal fiber, in stepped concentration of 0,2,4,6, and 8% for WSDA and 0, 0.25, 0.5, 0.75 and 1% treated sisal fibre by dry weight of soil using Standard proctor. The Sisal Fibre was treated with Sodium Borohydride (NaBH4 (1% wt/vol for 60 minutes at room temperature to remove the cellulose content present in the Fibre. Statistical analysis was carried out on the obtained results using XLSTART 2017 software and analysis of variance with the Microsoft Excel Analysis Tool Pak Software Package. The liquid limit (LL of the soil was found to be 48% while the plastic limit(PL is 21.27%. The maximum dry density(MDDhowever, decreases generally from a value of 1.85 Mg/m3 to 1.68Mg/m3 at 0.25% sisal fiber content/0% WSDA. It has its least value of 1.57Mg/m3 at 1% sisal fiber and 8% WSDA. The OMC increased from 18 % of the natural soil to 23.7% at 0.75% sisal fiber / 6% WSDA content. There was a general increase in the value of UCS of the soil-sisal fibre mixture with WSDA content from 100 kN/m2 of the natural soil to 696 kN/m2 at 0.75 % sisal fibre content / 6% WSDA. The UCS value met the standard of 687-1373 kN/m2 requirements of sub base for adequate lime and cement stabilization, respectively (Ingas and Metcalf 1972.

  11. Effects of nickel exposure on testicular function, oxidative stress, and male reproductive dysfunction in Spodoptera litura Fabricius.

    Science.gov (United States)

    Sun, Hongxia; Wu, Wenjing; Guo, Jixing; Xiao, Rong; Jiang, Fengze; Zheng, Lingyan; Zhang, Guren

    2016-04-01

    Nickel is an environmental pollutant that adversely affects the male reproductive system. In the present study, the effects of nickel exposure on Spodoptera litura Fabricius were investigated by feeding larvae artificial diets containing different doses of nickel for three generations. Damage to testes and effects on male reproduction were examined. The amount of nickel that accumulated in the testes of newly emerged males increased as the nickel dose in the diet increased during a single generation. Nickel exposure increased the amount of thiobarbituric acid reactive substances and decreased the amount of glutathione in treatment groups compared with the control. The activity levels of the antioxidant response indices superoxide dismutases, catalase, and glutathione peroxidase in the testes showed variable dose-dependent relationships with nickel doses and duration of exposure. Nickel doses also disrupted the development of the testes by decreasing the weight and volume of testes and the number of eupyrene and apyrene sperm bundles in treatment groups compared with the control. When the nickel-treated males mated with normal females, fecundity was inhibited by the higher nickel doses in all three generations, but fecundity significantly increased during the second generation, which received 5 mg kg(-1) nickel. Hatching rates in all treatments significantly decreased in a dose-dependent manner in the three successive generations. The effects of nickel on these parameters correlated with the duration of nickel exposure. Results indicate assays of testes may be a novel and efficient means of evaluating the effects of heavy metals on phytophagous insects in an agricultural environment. Copyright © 2015 Elsevier Ltd. All rights reserved.

  12. NICKEL HYDROXIDE FILMS IN CONTACT WITH AN ELECTROACTIVE SOLUTION. A STUDY EMPLOYING ELECTROCHEMICAL IMPEDANCE MEASUREMENTS

    OpenAIRE

    RICARDO TUCCERI

    2018-01-01

    The deactivation of nickel hydroxide films after prolonged storage times without use was studied. This study was carried out in the context of the Rotating Disc Electrode Voltammetry (RDEV) and Electrochemical Impedance Spectroscopy (EIS) when the nickel hydroxide film contacts an electroactive solution and a redox reaction occurs at the Au-Ni(OH)2|electrolyte interface. Deferasirox (4-(3,5-bis(2- hydroxyphenyl)-1,2,4-triazol-1-yl) benzoic acid) was employed as redox species in solution. Limi...

  13. Mechanisms of nickel toxicity in microorganisms

    Science.gov (United States)

    Macomber, Lee

    2014-01-01

    Summary Nickel has long been known to be an important human toxicant, including having the ability to form carcinomas, but until recently nickel was believed to be an issue only to microorganisms living in nickel-rich serpentine soils or areas contaminated by industrial pollution. This assumption was overturned by the discovery of a nickel defense system (RcnR/RcnA) found in microorganisms that live in a wide range of environmental niches, suggesting that nickel homeostasis is a general biological concern. To date, the mechanisms of nickel toxicity in microorganisms and higher eukaryotes are poorly understood. In this review, we summarize nickel homeostasis processes used by microorganisms and highlight in vivo and in vitro effects of exposure to elevated concentrations of nickel. On the basis of this evidence we propose four mechanisms of nickel toxicity: 1) nickel replaces the essential metal of metalloproteins, 2) nickel binds to catalytic residues of non-metalloenzymes; 3) nickel binds outside the catalytic site of an enzyme to inhibit allosterically, and 4) nickel indirectly causes oxidative stress. PMID:21799955

  14. Decarbonylative Silylation of Esters by Combined Nickel and Copper Catalysis for the Synthesis of Arylsilanes and Heteroarylsilanes

    KAUST Repository

    Guo, Lin

    2016-08-25

    An efficient nickel/copper-catalyzed decarbonylative silylation reaction of carboxylic acid esters with silylboranes is described. This reaction provides access to structurally diverse silanes with high efficiency and excellent functional-group tolerance starting from readily available esters.

  15. Decarbonylative Silylation of Esters by Combined Nickel and Copper Catalysis for the Synthesis of Arylsilanes and Heteroarylsilanes

    KAUST Repository

    Guo, Lin; Chatupheeraphat, Adisak; Rueping, Magnus

    2016-01-01

    An efficient nickel/copper-catalyzed decarbonylative silylation reaction of carboxylic acid esters with silylboranes is described. This reaction provides access to structurally diverse silanes with high efficiency and excellent functional-group tolerance starting from readily available esters.

  16. Nickel hydrogen battery cell storage matrix test

    Science.gov (United States)

    Wheeler, James R.; Dodson, Gary W.

    1993-01-01

    Test were conducted to evaluate post storage performance of nickel hydrogen cells with various design variables, the most significant being nickel precharge versus hydrogen precharge. Test procedures and results are presented in outline and graphic form.

  17. Mineralized lateritic profile in Sn, Zr, Th, Nb, Y and ETR (Serra do Madeira - Pitinga - AM): mineralogical characteristics and geochemical evolution

    International Nuclear Information System (INIS)

    Horbe, Adriana M.C.; Costa, Marcondes L. da

    1997-01-01

    The Pitinga region is located in the north 250 km far from Manaus, in the Amazonas State, Brazil. The Serra do Madeira is the local name of one hill located in the Madeira granite with important primary and supergenic mineralizations of Sn (cassiterite), Zr (zircon), Th (thorite), Nb (columbite and pyroclore), Y and REE (xenotime). The Serra do Madeira was constituted by a lateritic profile with 20 m of thickness where were identified seven horizons: parent rock, saprolite, clayey, bauxitic, concretionary, coluvion and latosol. The lateritization promoted the chemistry instability of the parent-rock forming a clayey material where Al 2 O 3 , Fe 2 O 3 , Sn, Th and Nb were enriched as kaolinite, gibbsite, hematite, goethite, cassiterite, zircon, thorite and columbite; SiO 2 , FeO, CaO, Na 2 O, K 2 O, F, Pb, Rb, and U were leached as quartz, K-feldspar, plagioclase, riebeckite/arfvedsonite, biotite, and iron sulfides; Y, P and ETR were enriched and leached correlated to xenotime, bastnaesite, fluorcerite and probably churchite and ytriofluorite

  18. Nickel exposure and plasma levels of biomarkers for assessing oxidative stress in nickel electroplating workers.

    Science.gov (United States)

    Tsao, Yu-Chung; Gu, Po-Wen; Liu, Su-Hsun; Tzeng, I-Shiang; Chen, Jau-Yuan; Luo, Jiin-Chyuan John

    2017-07-01

    The mechanism of nickel-induced pathogenesis remains elusive. To examine effects of nickel exposure on plasma oxidative and anti-oxidative biomarkers. Biomarker data were collected from 154 workers with various levels of nickel exposure and from 73 controls. Correlations between nickel exposure and oxidative and anti-oxidative biomarkers were determined using linear regression models. Workers with a exposure to high nickel levels had significantly lower levels of anti-oxidants (glutathione and catalase) than those with a lower exposure to nickel; however, only glutathione showed an independent association after multivariable adjustment. Exposure to high levels of nickel may reduce serum anti-oxidative capacity.

  19. Effects of ascorbic acid on carcinogenicity and acute toxicity of nickel subsulfide, and on tumor transplants growth in gulonolactone oxidase knock-out mice and wild-type C57BL mice

    Energy Technology Data Exchange (ETDEWEB)

    Kasprzak, Kazimierz S. [Laboratory of Comparative Carcinogenesis, National Cancer Institute at Frederick, Frederick, MD 21702 (United States); Diwan, Bhalchandra A. [Basic Research Program, Science Applications International Corporation-Frederick, Inc., National Cancer Institute at Frederick, Frederick, MD 21702 (United States); Kaczmarek, Monika Z. [Laboratory of Comparative Carcinogenesis, National Cancer Institute at Frederick, Frederick, MD 21702 (United States); Logsdon, Daniel L. [Laboratory Animal Sciences Program, Science Applications International Corporation-Frederick, Inc., National Cancer Institute at Frederick, Frederick, MD 21702 (United States); Fivash, Mathew J. [Data Management Services, National Cancer Institute at Frederick, Frederick, MD 21702 (United States); Salnikow, Konstantin, E-mail: salnikok@mail.nih.gov [Laboratory of Comparative Carcinogenesis, National Cancer Institute at Frederick, Frederick, MD 21702 (United States)

    2011-11-15

    The aim of this study was to test a hypothesis that ascorbate depletion could enhance carcinogenicity and acute toxicity of nickel. Homozygous L-gulono- < gamma > -lactone oxidase gene knock-out mice (Gulo-/- mice) unable to produce ascorbate and wild-type C57BL mice (WT mice) were injected intramuscularly with carcinogenic nickel subsulfide (Ni{sub 3}S{sub 2}), and observed for the development of injection site tumors for 57 weeks. Small pieces of one of the induced tumors were transplanted subcutaneously into separate groups of Gulo-/- and WT mice and the growth of these tumors was measured for up to 3 months. The two strains of mice differed significantly with regard to (1) Ni{sub 3}S{sub 2} carcinogenesis: Gulo-/- mice were 40% more susceptible than WT mice; and (2) transplanted tumors development: Gulo-/- mice were more receptive to tumor growth than WT mice, but only in terms of a much shorter tumor latency; later in the exponential phase of growth, the growth rates were the same. And, with adequate ascorbate supplementation, the two strains were equally susceptible to acute toxicity of Ni{sub 3}S{sub 2}. Statistically significant effects of dietary ascorbate dosing levels were the following: (1) reduction in ascorbate supplementation increased acute toxicity of Ni{sub 3}S{sub 2} in Gulo-/- mice; (2) ascorbate supplementation extended the latency of transplanted tumors in WT mice. In conclusion, the lack of endogenous ascorbate synthesis makes Gulo-/- mice more susceptible to Ni{sub 3}S{sub 2} carcinogenesis. Dietary ascorbate tends to attenuate acute toxicity of Ni{sub 3}S{sub 2} and to extend the latency of transplanted tumors. The latter effects may be of practical importance to humans and thus deserve further studies. -- Highlights: Black-Right-Pointing-Pointer Ascorbate depletion enhances carcinogenicity and acute toxicity of nickel. Black-Right-Pointing-Pointer Gulo-/- mice unable to synthesize ascorbate were used in this study. Black

  20. Effects of ascorbic acid on carcinogenicity and acute toxicity of nickel subsulfide, and on tumor transplants growth in gulonolactone oxidase knock-out mice and wild-type C57BL mice

    International Nuclear Information System (INIS)

    Kasprzak, Kazimierz S.; Diwan, Bhalchandra A.; Kaczmarek, Monika Z.; Logsdon, Daniel L.; Fivash, Mathew J.; Salnikow, Konstantin

    2011-01-01

    The aim of this study was to test a hypothesis that ascorbate depletion could enhance carcinogenicity and acute toxicity of nickel. Homozygous L-gulono- -lactone oxidase gene knock-out mice (Gulo−/− mice) unable to produce ascorbate and wild-type C57BL mice (WT mice) were injected intramuscularly with carcinogenic nickel subsulfide (Ni 3 S 2 ), and observed for the development of injection site tumors for 57 weeks. Small pieces of one of the induced tumors were transplanted subcutaneously into separate groups of Gulo−/− and WT mice and the growth of these tumors was measured for up to 3 months. The two strains of mice differed significantly with regard to (1) Ni 3 S 2 carcinogenesis: Gulo−/− mice were 40% more susceptible than WT mice; and (2) transplanted tumors development: Gulo−/− mice were more receptive to tumor growth than WT mice, but only in terms of a much shorter tumor latency; later in the exponential phase of growth, the growth rates were the same. And, with adequate ascorbate supplementation, the two strains were equally susceptible to acute toxicity of Ni 3 S 2 . Statistically significant effects of dietary ascorbate dosing levels were the following: (1) reduction in ascorbate supplementation increased acute toxicity of Ni 3 S 2 in Gulo−/− mice; (2) ascorbate supplementation extended the latency of transplanted tumors in WT mice. In conclusion, the lack of endogenous ascorbate synthesis makes Gulo−/− mice more susceptible to Ni 3 S 2 carcinogenesis. Dietary ascorbate tends to attenuate acute toxicity of Ni 3 S 2 and to extend the latency of transplanted tumors. The latter effects may be of practical importance to humans and thus deserve further studies. -- Highlights: ► Ascorbate depletion enhances carcinogenicity and acute toxicity of nickel. ► Gulo−/− mice unable to synthesize ascorbate were used in this study. ► The reduction in ascorbate levels in Gulo−/− mice increased acute toxicity induced by Ni 3 S 2 .

  1. Oral nickel exposure may induce Type I hypersensitivity reaction in nickel-sensitized subjects.

    Science.gov (United States)

    Büyüköztürk, Suna; Gelincik, Aslı; Ünal, Derya; Demirtürk, Mustafa; Çelik, Dolay Damla; Erden, Sacide; Çolakoğlu, Bahattin; Erdem Kuruca, Serap

    2015-05-01

    Little is known about the clinical and immunological changes in the nickel allergic patients with systemic symptoms. We aimed to evaluate T helper cell responses of patients with different clinical presentations due to nickel. Patients having various allergic symptoms and positive patch test results to nickel and 20 controls underwent skin prick tests with nickel. IL-10, IL-4, IL-5 and IFN-gamma were measured in the culture supernatants of PBMC stimulated by nickel during lymphocyte proliferation test (LTT). 69 patients (56 female, mean age: 49.2 ± 13.1), 97% having nickel containing dental devices and 20 controls (8 female, mean age 34.9 ± 12.06) were evaluated. Skin prick tests with nickel were positive in 70% of the patients (pnickel. Nickel containing dental alloys and oral nickel intake seem to trigger systemic symptoms in previously nickel sensitized patients. Copyright © 2015 Elsevier B.V. All rights reserved.

  2. The EU Nickel Directive revisited--future steps towards better protection against nickel allergy

    DEFF Research Database (Denmark)

    Thyssen, Jacob P; Uter, Wolfgang; McFadden, John

    2011-01-01

    In July 2001, the EU Nickel Directive came into full force to protect European citizens against nickel allergy and dermatitis. Prior to this intervention, Northern European governments had already begun to regulate consumer nickel exposure. According to part 2 of the EU Nickel Directive...... by the EU Nickel Directive. Despite this, the EU Nickel Directive part 2 was expected to work as an operational limit that would sufficiently protect European consumers against nickel allergy and dermatitis. This review presents the accumulation of epidemiological studies that evaluated the possible effect...... and the Danish nickel regulation, consumer items intended to be in direct and prolonged contact with the skin were not allowed to release more than 0.5 µg nickel/cm2/week. It was considered unlikely that nickel allergy would disappear altogether as a proportion of individuals reacted below the level defined...

  3. Tungsten determination in heat resistant nickel-base-alloys by the method of atomic absorption

    International Nuclear Information System (INIS)

    Gregorczyk, S.; Wycislik, A.

    1980-01-01

    A method of atomic absorption was developed. It allows for the tungsten to be determined in heatresistant nickel-base-alloys within the range 0.01 to 7%. It consists in precipitating tungsten acid in the presence of alkaloids with its following decomposition by hydrofluoric acid in the teflon bomb. (author)

  4. Nickel may be released from laptop computers

    DEFF Research Database (Denmark)

    Jensen, Peter; Jellesen, Morten Stendahl; Møller, Per

    2012-01-01

    Consumer nickel sensitization and dermatitis is caused by prolonged or repeated skin exposure to items that release nickel, for example jewellery, belts, buttons, watches, and mobile phones (1–3). We recently described a patient in whom primary nickel contact sensitization and dermatitis develope...

  5. Electrodeposition of zinc--nickel alloys coatings

    Energy Technology Data Exchange (ETDEWEB)

    Dini, J W; Johnson, H R

    1977-10-01

    One possible substitute for cadmium in some applications is a zinc--nickel alloy deposit. Previous work by others showed that electrodeposited zinc--nickel coatings containing about 85 percent zinc and 15 percent nickel provided noticeably better corrosion resistance than pure zinc. Present work which supports this finding also shows that the corrosion resistance of the alloy deposit compares favorably with cadmium.

  6. Sintering of nickel steam reforming catalysts

    DEFF Research Database (Denmark)

    Sehested, Jens; Larsen, Niels Wessel; Falsig, Hanne

    2014-01-01

    . In this paper, particle migration and coalescence in nickel steam reforming catalysts is studied. Density functional theory calculations indicate that Ni-OH dominate nickel transport at nickel surfaces in the presence of steam and hydrogen as Ni-OH has the lowest combined energies of formation and diffusion...

  7. Phase transformation in nickel during tribotesting

    Energy Technology Data Exchange (ETDEWEB)

    Hershberger, J. [Energy Technology Division, Argonne National Laboratory, Building 212 Room D204, 9700 S Cass Avenue, Argonne, IL 60439 (United States)]. E-mail: jhersh@anl.gov; Ajayi, O.O. [Energy Technology Division, Argonne National Laboratory, Building 212 Room D204, 9700 S Cass Avenue, Argonne, IL 60439 (United States); Fenske, G.R. [Energy Technology Division, Argonne National Laboratory, Building 212 Room D204, 9700 S Cass Avenue, Argonne, IL 60439 (United States)

    2005-12-15

    Commercially pure nickel was subjected to a polyalphaolefin-lubricated reciprocating tribotest with increasing load. A friction transition was observed and X-ray diffraction was performed on low-friction and high-friction areas. Hexagonal nickel or nickel carbide was formed at high friction. Broadening of the face-centered cubic peaks did not show dislocation structures characteristic of scuffing.

  8. Phase transformation in nickel during tribotesting

    International Nuclear Information System (INIS)

    Hershberger, J.; Ajayi, O.O.; Fenske, G.R.

    2005-01-01

    Commercially pure nickel was subjected to a polyalphaolefin-lubricated reciprocating tribotest with increasing load. A friction transition was observed and X-ray diffraction was performed on low-friction and high-friction areas. Hexagonal nickel or nickel carbide was formed at high friction. Broadening of the face-centered cubic peaks did not show dislocation structures characteristic of scuffing

  9. Nickel-accumulating plant from Western Australia

    Energy Technology Data Exchange (ETDEWEB)

    Severne, B C; Brooks, R R

    1972-01-01

    A small shrub Hybanthus floribundus (Lindl.) F. Muell. Violaceae growing in Western Australia accumulates nickel and cobalt to a very high degree. Values of up to 23% nickel in leaf ash may represent the highest relative accumulation of a metal on record. The high accumulation of nickel poses interesting problems in plant physiology and plant biochemistry. 9 references, 2 figures, 1 table.

  10. Investigation of hydrogen evolution activity for the nickel, nickel-molybdenum nickel-graphite composite and nickel-reduced graphene oxide composite coatings

    International Nuclear Information System (INIS)

    Jinlong, Lv; Tongxiang, Liang; Chen, Wang

    2016-01-01

    Graphical abstract: - Highlights: • Improved HER efficiency of Ni-Mo coatings was attributed to ‘cauliflower’ like microstructure. • RGO in nickel-RGO composite coating promoted refined grain and facilitated HER. • Synergistic effect between nickel and RGO facilitated HER due to large specific surface of RGO. - Abstract: The nickel, nickel-molybdenum alloy, nickel-graphite and nickel-reduced graphene oxide composite coatings were obtained by the electrodeposition technique from a nickel sulfate bath. Nanocrystalline molybdenum, graphite and reduced graphene oxide in nickel coatings promoted hydrogen evolution reaction in 0.5 M H_2SO_4 solution at room temperature. However, the nickel-reduced graphene oxide composite coating exhibited the highest electrocatalytic activity for the hydrogen evolution reaction in 0.5 M H_2SO_4 solution at room temperature. A large number of gaps between ‘cauliflower’ like grains could decrease effective area for hydrogen evolution reaction in slight amorphous nickel-molybdenum alloy. The synergistic effect between nickel and reduced graphene oxide promoted hydrogen evolution, moreover, refined grain in nickel-reduced graphene oxide composite coating and large specific surface of reduced graphene oxide also facilitated hydrogen evolution reaction.

  11. Investigation of hydrogen evolution activity for the nickel, nickel-molybdenum nickel-graphite composite and nickel-reduced graphene oxide composite coatings

    Energy Technology Data Exchange (ETDEWEB)

    Jinlong, Lv, E-mail: ljlbuaa@126.com [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China); Tongxiang, Liang; Chen, Wang [Beijing Key Laboratory of Fine Ceramics, Institute of Nuclear and New Energy Technology, Tsinghua University, Zhongguancun Street, Haidian District, Beijing 100084 (China); State Key Lab of New Ceramic and Fine Processing, Tsinghua University, Beijing 100084 (China)

    2016-03-15

    Graphical abstract: - Highlights: • Improved HER efficiency of Ni-Mo coatings was attributed to ‘cauliflower’ like microstructure. • RGO in nickel-RGO composite coating promoted refined grain and facilitated HER. • Synergistic effect between nickel and RGO facilitated HER due to large specific surface of RGO. - Abstract: The nickel, nickel-molybdenum alloy, nickel-graphite and nickel-reduced graphene oxide composite coatings were obtained by the electrodeposition technique from a nickel sulfate bath. Nanocrystalline molybdenum, graphite and reduced graphene oxide in nickel coatings promoted hydrogen evolution reaction in 0.5 M H{sub 2}SO{sub 4} solution at room temperature. However, the nickel-reduced graphene oxide composite coating exhibited the highest electrocatalytic activity for the hydrogen evolution reaction in 0.5 M H{sub 2}SO{sub 4} solution at room temperature. A large number of gaps between ‘cauliflower’ like grains could decrease effective area for hydrogen evolution reaction in slight amorphous nickel-molybdenum alloy. The synergistic effect between nickel and reduced graphene oxide promoted hydrogen evolution, moreover, refined grain in nickel-reduced graphene oxide composite coating and large specific surface of reduced graphene oxide also facilitated hydrogen evolution reaction.

  12. Void formation in irradiated binary nickel alloys

    International Nuclear Information System (INIS)

    Shaikh, M.A.; Ahmed, M.; Akhter, J.I.

    1994-01-01

    In this work a computer program has been used to compute void radius, void density and swelling parameter for nickel and binary nickel-carbon alloys irradiated with nickel ions of 100 keV. The aim is to compare the computed results with experimental results already reported

  13. Ecological Considerations on Nickel Dermatitis

    Science.gov (United States)

    Marcussen, Poul V.

    1960-01-01

    The incidence of nickel dermatoses has shifted from the plating industry to other occupations and particularly to non-occupational causes. A Danish survey of 621 cases shows that 4% are due to nickel plating, 9·5% to other occupations, and 86·5% were not due to occupation. A primary eruption not due to occupation had occurred in 14% of the occupational cases. The importance of preventive measures for the community more than for the adequately controlled industry is underlined. PMID:14420983

  14. A PIXE/PIGE study of gold mineralisation in lateritic terrain, Tanami Desert, Australia

    International Nuclear Information System (INIS)

    Van Moort, J.C.; Li, X.

    1997-01-01

    Proton induced X-ray and γ-ray emission (PIXE/PIGE) have been used to analyze major and trace elements in a suite of 140 core samples from around of the Jim's Find South gold anomaly in the Tanami desert, located in heavily weathered terrain. Simultaneous analyses were obtained for 30 elements, ranging in atomic number from 3 Li to 90 Th. The method was chosen because of its speed and the wide range of determination, its flexibility, precision and low detection limits. The regolith powder samples were treated by hot aqua regia before making them into pills. The PIXE/PIGE data of the acid insoluble residue give three factor analysis clusters. The first cluster comprises the elements F, Al, K, V, Mn, Fe, Ga, Rb, W and Au and is essentially related to sericitic wallrock alteration. The second cluster consists of Ti, As, Y, Zr, and Nb and is largely related to resistant minerals. The third cluster consists of Na, Ca and Sr and is interpreted to comprise elements in weatherable minerals such as feldspar and thus represents weathering intensity. While the Rb/K ratio and the product of As x Cu x Ni provide the best surface expression of the gold mineralisation, the Rb/AI ratio provides the best expression of the sericitic alteration around the ore body

  15. Carbon formation on nickel and nickel-copper alloy catalysts

    Energy Technology Data Exchange (ETDEWEB)

    Alstrup, I.; Soerensen, O.; Rostrup-Nielsen, J.R. [Haldor Topsoe Research Labs., Lyngby (Denmark); Tavares, M.T.; Bernardo, C.A.

    1998-05-01

    Equilibrium, kinetic and morphological studies of carbon formation in CH{sub 4} + H{sub 2}, CO, and CO + H{sub 2} gases on silica supported nickel and nickel-copper catalysts are reviewed. The equilibrium deviates in all cases from graphite equilibrium and more so in CO + CO{sub 2} than in CH{sub 4} + H{sub 2}. A kinetic model based on information from surface science results with chemisorption of CH{sub 4} and possibly also the first dehydrogenation step as rate controlling describes carbon formation on nickel catalyst in CH{sub 4} + H{sub 2} well. The kinetics of carbon formation in CO and CO + H{sub 2} gases are in agreement with CO disproportionation as rate determining step. The presence of hydrogen influences strongly the chemisorption of CO. Carbon filaments are formed when hydrogen is present in the gas while encapsulating carbon dominates in pure CO. Small amounts of Cu alloying promotes while larger amounts (Cu : Ni {>=} 0.1) inhibits carbon formation and changes the morphology of the filaments (``octopus`` carbon formation). Adsorption induced nickel segregation changes the kinetics of the alloy catalysts at high carbon activities. Modifications suggested in some very recent papers on the basis of new results are also briefly discussed. (orig.) 31 refs.

  16. Synthesis and growth mechanism of sponge-like nickel using a hydrothermal method

    Science.gov (United States)

    Shao, Bin; Yin, Xueguo; Hua, Weidong; Ma, Yilong; Sun, Jianchun; Li, Chunhong; Chen, Dengming; Guo, Donglin; Li, Kejian

    2018-05-01

    Sponge-like nickel composed of micro-chains with a diameter of 1-5 μm was selectively synthesized by the hydrothermal method, using sodium hydroxide (NaOH) as the alkaline reagent, aqueous hydrazine as reducing agent and citric acid as a coordination agent. The time-dependent samples prepared at different NaOH concentrations were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM) and Fourier transform infrared spectrometer (FTIR). The results showed that the agglomerates of nickel citrate hydrazine complex nanoplates were first precipitated and then reduced to prickly nickel micro-chains at a lower NaOH concentration, which played a role in the further formation of sponge-like nickel. Also, the probable growth mechanism of the sponge-like nickel was proposed. The magnetic properties of sponge-like nickel were studied using a vibrating sample magnetometer. The sponge-like nickel exhibited a ferromagnetic behavior with a saturation magnetization value of 43.8 emu g-1 and a coercivity value of 120.7 Oe.

  17. Nickel exposure from keys: a Brazilian issue.

    Science.gov (United States)

    Suzuki, Nathalie Mie; Duarte, Ida Alzira Gomes; Hafner, Mariana de Figueiredo Silva; Lazzarini, Rosana

    2017-01-01

    Keys are a significant source of exposure to metal allergens and can be a relevant problem for nickel-allergic individuals. This study aimed to perform nickel and cobalt spot testing among the 5 most common Brazilian brands of keys. Among the tested keys, 100% showed positive result to nickel spot test, 83,3% presented strong positive reaction. 50% exhibited cobalt release as well. Nickel release from keys is very common in our country and may cause a negative impact on sensitized individual's quality of life. Study's results highlight the importance of establishing directives to regulate nickel release in Brazil.

  18. Ultrasonic preparation of nano-nickel/activated carbon composite using spent electroless nickel plating bath and application in degradation of 2,6-dichlorophenol.

    Science.gov (United States)

    Su, Jingyu; Jin, Guanping; Li, Changyong; Zhu, Xiaohui; Dou, Yan; Li, Yong; Wang, Xin; Wang, Kunwei; Gu, Qianqian

    2014-11-01

    Ni was effectively recovered from spent electroless nickel (EN) plating baths by forming a nano-nickel coated activated carbon composite. With the aid of ultrasonication, melamine-formaldehyde-tetraoxalyl-ethylenediamine chelating resins were grafted on activated carbon (MFT/AC). PdCl2 sol was adsorbed on MFT/AC, which was then immersed in spent electroless nickel plating bath; then nano-nickel could be reduced by ascorbic acid to form a nano-nickel coating on the activated carbon composite (Ni/AC) in situ. The materials present were carefully examined by Fourier transform infrared spectroscopy, X-ray diffraction, field emission scanning electron microscopy, X-ray photoelectron spectroscopy and electrochemistry techniques. The resins were well distributed on the inside and outside surfaces of activated carbon with a size of 120 ± 30 nm in MFT/AC, and a great deal of nano-nickel particles were evenly deposited with a size of 3.8 ± 1.1 nm in Ni/MFT. Moreover, Ni/AC was successfully used as a catalyst for ultrasonic degradation of 2,6-dichlorophenol. Copyright © 2014. Published by Elsevier B.V.

  19. Effect of industrial, municipal and agricultural wastes on peanut in lateritic sandy loam soil

    International Nuclear Information System (INIS)

    Sarkar, S.; Khan, A.R.

    2002-06-01

    Modern agriculture, worldwide, depends upon the external application of plant nutrients supplied mostly through chemical fertilizer to meet the crop needs. The natural recycling cannot provide the very large amount of nutrients needed year after year in an intensive cropping system and nutrients being a major constraint harvesting the nutrient energy from biological and industrial waste are of prime importance for maximizing the food grain production in the world. A number of industrial wastes like fly ash from thermal power plants, paper factory sludge from paper factory, sewage sludge from municipal source and farmyard manure from livestock farming are the important waste resources, having potentiality in recycling in agricultural land. When these wastes are recycled through soil for crop production, due to the degradative and assimilative capacity of soil, the pollution hazards of these wastes can be minimized to a greater extent as compared to direct disposing of at the site. Fly ash is a waste product residue resulting from the combustion of pulverised coal in coal-fired power generating station. Physico - chemical analysis of fly ash has revealed the presence of both macro-micro nutrients, which can sustain plant growth. Its application in the agricultural land acts as a liming material and improves crop growth by neutralizing the soil acidity, increasing the water availability for the plants and supplement of nutrients (Adriano et al, 1980, Molliner and Street, 1982, Schnappinger et al, 1975). Application of paper factory sludge has been reported to increase the organic carbon content in soil and nutrient content like P, K, Ca, Mg and micronutrients (Guerini et al, 1994, Muse and Mitchell, 1995). Sludge application also improves the organic carbon content of the soil and availability of nutrients like Ca, K and Mg besides improvement of physical properties (Pitchel and Hayes, 1990). Much is known regarding crop performance and changes in physical and

  20. Assaying environmental nickel toxicity using model nematodes.

    Directory of Open Access Journals (Sweden)

    David Rudel

    Full Text Available Although nickel exposure results in allergic reactions, respiratory conditions, and cancer in humans and rodents, the ramifications of excess nickel in the environment for animal and human health remain largely undescribed. Nickel and other cationic metals travel through waterways and bind to soils and sediments. To evaluate the potential toxic effects of nickel at environmental contaminant levels (8.9-7,600 µg Ni/g dry weight of sediment and 50-800 µg NiCl2/L of water, we conducted assays using two cosmopolitan nematodes, Caenorhabditis elegans and Pristionchus pacificus. We assayed the effects of both sediment-bound and aqueous nickel upon animal growth, developmental survival, lifespan, and fecundity. Uncontaminated sediments were collected from sites in the Midwestern United States and spiked with a range of nickel concentrations. We found that nickel-spiked sediment substantially impairs both survival from larval to adult stages and adult longevity in a concentration-dependent manner. Further, while aqueous nickel showed no adverse effects on either survivorship or longevity, we observed a significant decrease in fecundity, indicating that aqueous nickel could have a negative impact on nematode physiology. Intriguingly, C. elegans and P. pacificus exhibit similar, but not identical, responses to nickel exposure. Moreover, P. pacificus could be tested successfully in sediments inhospitable to C. elegans. Our results add to a growing body of literature documenting the impact of nickel on animal physiology, and suggest that environmental toxicological studies could gain an advantage by widening their repertoire of nematode species.

  1. Assaying environmental nickel toxicity using model nematodes

    Science.gov (United States)

    Rudel, David; Douglas, Chandler; Huffnagle, Ian; Besser, John M.; Ingersoll, Christopher G.

    2013-01-01

    Although nickel exposure results in allergic reactions, respiratory conditions, and cancer in humans and rodents, the ramifications of excess nickel in the environment for animal and human health remain largely undescribed. Nickel and other cationic metals travel through waterways and bind to soils and sediments. To evaluate the potential toxic effects of nickel at environmental contaminant levels (8.9-7,600 µg Ni/g dry weight of sediment and 50-800 µg NiCl2/L of water), we conducted assays using two cosmopolitan nematodes, Caenorhabditis elegans and Pristionchus pacificus. We assayed the effects of both sediment-bound and aqueous nickel upon animal growth, developmental survival, lifespan, and fecundity. Uncontaminated sediments were collected from sites in the Midwestern United States and spiked with a range of nickel concentrations. We found that nickel-spiked sediment substantially impairs both survival from larval to adult stages and adult longevity in a concentration-dependent manner. Further, while aqueous nickel showed no adverse effects on either survivorship or longevity, we observed a significant decrease in fecundity, indicating that aqueous nickel could have a negative impact on nematode physiology. Intriguingly, C. elegansand P. pacificus exhibit similar, but not identical, responses to nickel exposure. Moreover, P. pacificus could be tested successfully in sediments inhospitable to C. elegans. Our results add to a growing body of literature documenting the impact of nickel on animal physiology, and suggest that environmental toxicological studies could gain an advantage by widening their repertoire of nematode species.

  2. Heat treatment of nickel alloys

    International Nuclear Information System (INIS)

    Smith, D.F. Jr.; Clatworthy, E.F.

    1975-01-01

    A heat treating process is described that can be used to produce desired combinations of strength, ductility, and fabricability characteristics in heat resistant age-hardenable alloys having precipitation-hardening amounts of niobium, titanium, and/or tantalum in a nickel-containing matrix. (U.S.)

  3. Electrolytic nickel deposits upon uranium

    International Nuclear Information System (INIS)

    Baudin, G.; Chauvin, G.; Coriou, H.; Hure, J.

    1958-01-01

    The authors present a new possibility to protect uranium by very adherent nickel deposits got by aqueous medium electrolysis. Surface treatment of uranium is based upon the chemical etching method from Lietazke. After thermal treatments at 600, 700 and 800 deg. C, under vacuum, a good intermetallic U-Ni diffusion is observed for each case. (author) [fr

  4. Iron-nickel-chromium alloys

    International Nuclear Information System (INIS)

    Karenko, M.K.

    1981-01-01

    A specification is given for iron-nickel-chromium age-hardenable alloys suitable for use in fast breeder reactor ducts and cladding, which utilize the gamma-double prime strengthening phase and are characterized in having a delta or eta phase distributed at or near grain boundaries. A range of compositions is given. (author)

  5. ELECTRODEPOSITION OF NICKEL ON URANIUM

    Science.gov (United States)

    Gray, A.G.

    1958-08-26

    A method is described for preparing uranium objects prior to nickel electroplating. The process consiats in treating the surface of the uranium with molten ferric chloride hexahydrate, at a slightiy elevated temperature. This treatment etches the metal surface providing a structure suitable for the application of adherent electrodeposits and at the same time plates the surface with a thin protective film of iron.

  6. Aqueous processing of nickel spent catalyst for a value added product

    International Nuclear Information System (INIS)

    Sheik, Abdul Rauf; Ghosh, Malay Kumar; Sanjay, Kali; Subbaiah, Tondepu; Mishra, Barada Kanta; Baba, Abdullahi Aalafara

    2013-01-01

    Nickel was recovered from a fertilizer industry spent catalyst by leaching with nitric acid followed by nickel hydroxide precipitation. The optimization of temperature, initial acid concentration and particle size for leaching of the spent catalyst was done through 2 3 factorial design. A maximum extraction of 91.9% was achieved at 90 .deg. C, 1.5M HNO 3 and 62.5 µm particle size. Temperature and acid concentration showed positive effect, while particle size showed no effect. A regression equation was developed and employed to predict conditions for 100% extraction which were experimentally tested. Nickel hydroxide was electrochemically precipitated from the leach liquor and its maximum discharge capacity was found to be 155 mAh/g. A 3-stage counter current leaching circuit was designed to obtain a leach liquor of suitable pH. XRD characterization of the precipitated Ni(OH) 2 shows to consist of both α- and β-forms

  7. Magnetic behavior of nickel ferrite nanoparticles prepared by co-precipitation route

    International Nuclear Information System (INIS)

    Maaz, K.; Mashiatullah, A.; Javed, T.; Ali, G.; Karim, S.

    2008-01-01

    Magnetic nanoparticles of nickel ferrite (NiFe/sub 2/O/sub 4/) have been synthesized by co-precipitation route using stable ferric and nickel salts with sodium hydroxide as the precipitating agent and oleic acid as the surfactant. X-ray Diffraction (XRD) and Transmission Electron Microscope (TEM) analyses confirmed the formation of single phase nickel ferrite nanoparticles in the range 8-28 nm. The size of the particles was observed to be increasing linearly with increasing annealing temperature of the sample. Typical blocking effects were observed below -225 K for all the prepared samples. The superparamagnetic blocking temperature was found to be continuously increasing with increasing particle sizes that has been attributed to the increased effective anisotropy of the nanoparticles. The saturation moment of all the samples was found much below the bulk value of nickel ferrite that has been attributed to the disordered surface spins of these nanoparticles. (author)

  8. Nickel in nails, hair and plasma from nickel-hypersensitive women

    DEFF Research Database (Denmark)

    Gammelgaard, Bente; Veien, Niels

    1990-01-01

    The concentrations of nickel in finger-nails, toe-nails, hair and plasma from 71 nickel-hypersensitive women and 20 non-hypersensitive women were determined. Nickel concentrations in finger-nails were significantly higher than in toe-nails in both the nickel-hypersensitive group and the control...... group. Nickel-sensitive women had significantly higher levels of nickel in toe-nails, hair and plasma than had control subjects, whereas there was no significant difference in nickel concentration in finger-nails between the two groups. No correlation could be demonstrated between nickel levels in any...... combination of nails, hair and plasma in the nickel-hypersensitive or in the control group....

  9. Excessive nickel release from mobile phones--a persistent cause of nickel allergy and dermatitis.

    Science.gov (United States)

    Jensen, Peter; Johansen, Jeanne D; Zachariae, Claus; Menné, Torkil; Thyssen, Jacob P

    2011-12-01

    Despite the political intention to limit nickel allergy and dermatitis in Europeans, nickel allergy remains frequent. There are several explanations for the persistence of nickel allergy and dermatitis, including the increasing use of mobile phones. Before regulation of nickel release from mobile phones, we showed that eight (19.5%) of 41 mobile phones marketed in Denmark between 2003 and 2007 released nickel in concentrations that may result in nickel allergy and dermatitis. In 2009, the EU Nickel Directive was revised to include nickel-releasing mobile phones. To investigate the proportion of mobile phones sold in Denmark that release nickel after regulation. Metallic parts from 50 randomly selected mobile phones currently for sale in Denmark were tested for nickel release by use of the dimethylglyoxime (DMG)-nickel spot test. Nine (18%) phones showed at least one positive DMG test reaction and two phones had more than one DMG test-positive spot. Apparently, the proportion of mobile phones with significant nickel release remains unchanged, despite the 2009 revision of the EU Nickel Directive. We encourage manufacturers to measure nickel release from metallic components used in the assembly of mobile phones to ensure safe products. © 2011 John Wiley & Sons A/S.

  10. Electroplated tin-nickel coatings as a replacement for nickel to eliminate nickel dermatitis

    DEFF Research Database (Denmark)

    Møller, Per; Boyce, Jan M.; Nielsen, Lars Pleth

    2013-01-01

    . The main focus will be on the corrosion properties where the following corrosion investigations will be covered; corrosion potential measurements for the different coatings, estimation of corrosion rates for materials in galvanic coupling with tin/nickel coatings, salt spray test, medical tests...

  11. A biotemplated nickel nanostructure: Synthesis, characterization and antibacterial activity

    Energy Technology Data Exchange (ETDEWEB)

    Ashtari, Khadijeh [Department of Nanobiotechnology, Faculty of Biological Science, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Fasihi, Javad [Department of Analytical Chemistry, Faculty of Science, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Mollania, Nasrin [Department of Biochemistry, Faculty of Biological Science, Tarbiat Modares University, P.O. Box 14115-175, Tehran (Iran, Islamic Republic of); Khajeh, Khosro, E-mail: khajeh@modares.ac.ir [Department of Nanobiotechnology, Faculty of Biological Science, Tarbiat Modares University, Tehran (Iran, Islamic Republic of); Department of Biochemistry, Faculty of Biological Science, Tarbiat Modares University, P.O. Box 14115-175, Tehran (Iran, Islamic Republic of)

    2014-02-01

    Highlights: • Nickel nanostructure-encapsulated bacteria were prepared using electroless deposition. • Bacterium surface was activated by red-ox reaction of its surface amino acids. • Interfacial changes at cell surfaces were investigated using fluorescence spectroscopy. • TEM and AFM depicted morphological changes. • Antibacterial activity of nanostructure was examined against different bacteria strains. - Abstract: Nickel nanostructure-encapsulated bacteria were prepared using the electroless deposition procedure and activation of bacterium cell surface by red-ox reaction of surface amino acids. The electroless deposition step occurred in the presence of Ni(II) and dimethyl amine boran (DMAB). Interfacial changes at bacteria cell surfaces during the coating process were investigated using fluorescence spectroscopy. Fluorescence of tryptophan residues was completely quenched after the deposition of nickel onto bacteria surfaces. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) depicted morphological changes on the surface of the bacterium. It was found that the Ni coated nanostructure was mechanically stable after ultrasonication for 20 min. Significant increase in surface roughness of bacteria was also observed after deposition of Ni clusters. The amount of coated Ni on the bacteria surface was calculated as 36% w/w. The antibacterial activity of fabricated nanostructure in culture media was examined against three different bacteria strains; Escherichia coli, Bacillus subtilis and Xantomonas campestris. The minimum inhibitory concentrations (MIC) were determined as 500 mg/L, 350 mg/L and 200 mg/L against bacteria, respectively.

  12. Gold, nickel and copper mining and processing.

    Science.gov (United States)

    Lightfoot, Nancy E; Pacey, Michael A; Darling, Shelley

    2010-01-01

    Ore mining occurs in all Canadian provinces and territories except Prince Edward Island. Ores include bauxite, copper, gold, iron, lead and zinc. Workers in metal mining and processing are exposed, not only to the metal of interest, but also to various other substances prevalent in the industry, such as diesel emissions, oil mists, blasting agents, silica, radon, and arsenic. This chapter examines cancer risk related to the mining of gold, nickel and copper. The human carcinogenicity of nickel depends upon the species of nickel, its concentration and the route of exposure. Exposure to nickel or nickel compounds via routes other than inhalation has not been shown to increase cancer risk in humans. As such, cancer sites of concern include the lung, and the nasal sinus. Evidence comes from studies of nickel refinery and leaching, calcining, and sintering workers in the early half of the 20th century. There appears to be little or no detectable risk in most sectors of the nickel industry at current exposure levels. The general population risk from the extremely small concentrations detectable in ambient air are negligible. Nevertheless, animal carcinogenesis studies, studies of nickel carcinogenesis mechanisms, and epidemiological studies with quantitative exposure assessment of various nickel species would enhance our understanding of human health risks associated with nickel. Definitive conclusions linking cancer to exposures in gold and copper mining and processing are not possible at this time. The available results appear to demand additional study of a variety of potential occupational and non-occupational risk factors.

  13. New views on the hypothesis of respiratory cancer risk from soluble nickel exposure; and reconsideration of this risk's historical sources in nickel refineries

    Directory of Open Access Journals (Sweden)

    Heller James G

    2009-08-01

    electrolysis department that were previously overlooked in favour of only soluble nickel exposure; and the absence of comparable insoluble nickel exposures in PCNR's tankhouse, a finding that is consistent with the absence of respiratory cancer risk there. The most recent KNR evidence linking soluble nickel with lung cancer risk arose in a reconfiguration of KNR's historical exposures. But the resulting job exposure matrix lacks an objective, protocol-driven rationale that could provide a valid and reliable basis for analyzing the relationship of KNR lung cancer risk with any nickel species. Evidence of significant arsenic exposure during the processing step in the Clydach refinery's hydrometallurgy department in the 1902–1934 time period likely accounts for most of the elevated respiratory cancer risk observed at that time. An understanding of the mechanism for nickel carcinogenicity remains an elusive goal of toxicological research; as does its capacity to confirm the human health evidence on this subject with animal studies. Concluding remarks Epidemiological methods have failed to accurately identify the source(s of observed lung cancer risk in at least one nickel refinery (KNR. This failure, together with the negative long-term animal inhalation studies on soluble nickel and other toxicological evidence, strongly suggest that the designation of soluble nickel as carcinogenic should be reconsidered, and that the true causes of historical lung cancer risk at certain nickel refineries lie in other exposures, including insoluble nickel compounds, arsenic, sulphuric acid mists and smoking.

  14. Role of phosphate solubilizing Burkholderia spp. for successful colonization and growth promotion of Lycopodium cernuum L. (Lycopodiaceae) in lateritic belt of Birbhum district of West Bengal, India.

    Science.gov (United States)

    Ghosh, Ranjan; Barman, Soma; Mukherjee, Rajib; Mandal, Narayan C

    2016-02-01

    Profuse growth of Lycpodium cernuum L. was found in phosphate deficient red lateritic soil of West Bengal, India. Interaction of vesicular-arbuscular mycorrhiza (VAM) with Lycopodium rhizoids were described earlier but association of PGPR with their rhizoids were not studied. Three potent phosphate solubilizing bacterial strains (P4, P9 and P10) associated with L. cernuum rhizoids were isolated and identified by 16S rDNA homologies on Ez-Taxon database as Burkholderia tropica, Burkholderia unamae and Burkholderia cepacia respectively. Day wise kinetics of phosphate solubilization against Ca3(PO4)2 suggested P4 (580.56±13.38 μg ml(-1)) as maximum mineral phosphate solubilizer followed by P9 (517.12±17.15 μg ml(-1)) and P10 (485.18±14.23 μg ml(-1)) at 28 °C. Release of bound phosphates by isolated strains from ferric phosphate (FePO4), aluminum phosphate (AlPO4) and four different complex rock phosphates indicated their very good phosphate solubilizng efficacy. Nitrogen independent solubilizition also supports their nitrogen fixing capabilities. Inhibition of P solubilization by calcium salts and induction by EDTA suggested pH dependent chelation of metal cations by all of the isolates. Rhizoidal colonization potentials of Burkholderia spp. were confirmed by in planta experiment and also using scanning electron microscope (SEM). Increases of total phosphate content in Lycopodium plants upon soil treatment with these isolates were also recorded. In addition siderophore production on CAS agar medium, tryptophan dependent IAA production and antifungal activities against pathogenic fungi by rhizospheric isolates deep-rooted that they have definite role in nutrient mobilization for successful colonization of L. cernuum in nutrient deficient lateritic soil. Copyright © 2015 Elsevier GmbH. All rights reserved.

  15. L-carnitine protects against nickel-induced neurotoxicity by maintaining mitochondrial function in Neuro-2a cells

    International Nuclear Information System (INIS)

    He Mindi; Xu Shangcheng; Lu Yonghui; Li Li; Zhong Min; Zhang Yanwen; Wang Yuan; Li Min; Yang Ju; Zhang Guangbin; Yu Zhengping; Zhou Zhou

    2011-01-01

    Mitochondrial dysfunction is thought to be a part of the mechanism underlying nickel-induced neurotoxicity. L-carnitine (LC), a quaternary ammonium compound biosynthesized from the amino acids lysine and methionine in all mammalian species, manifests its neuroprotective effects by improving mitochondrial energetics and function. The purpose of this study was to investigate whether LC could efficiently protect against nickel-induced neurotoxicity. Here, we exposed a mouse neuroblastoma cell line (Neuro-2a) to different concentrations of nickel chloride (NiCl 2 ) (0.25, 0.5, 1, and 2 mM) for 24 h, or to 0.5 mM and 1 mM NiCl 2 for various periods (0, 3, 6, 12, or 24 h). We found that nickel significantly increased the cell viability loss and lactate dehydrogenase (LDH) release in Neuro-2a cells. In addition, nickel exposure significantly elevated reactive oxygen species (ROS) and malondialdehyde (MDA) levels, disrupted the mitochondrial membrane potential (ΔΨ m ), reduced adenosine-5'-triphosphate (ATP) concentrations and decreased mitochondrial DNA (mtDNA) copy numbers and mtRNA transcript levels. However, all of the cytotoxicities and mitochondrial dysfunctions that were triggered by nickel were efficiently attenuated by pretreatment with LC. These protective effects of LC may be attributable to its role in maintaining mitochondrial function in nickel-treated cells. Our results suggest that LC may have great pharmacological potential in protecting against the adverse effects of nickel in the nervous system.

  16. Synthesis of Nickel and Nickel Hydroxide Nano powders by Simplified Chemical Reduction

    International Nuclear Information System (INIS)

    Tientong, J.; Garcia, S.; Thurber, C.R.; Golden, T.D.

    2014-01-01

    Nickel nano powders were synthesized by a chemical reduction of nickel ions with hydrazine hydrate at ph ∼ 12.5. Sonication of the solutions created a temperature of 54-65 °C to activate the reduction reaction of nickel nanoparticles. The solution ph affected the composition of the resulting nanoparticles. Nickel hydroxide nanoparticles were formed from an alkaline solution (ph ∼10) of nickel-hydrazine complexed by dropwise titration. X-ray diffraction of the powder and the analysis of the resulting Williamson-Hall plots revealed that the particle size of the powders ranged from 12 to 14 nm. Addition of polyvinylpyrrolidone into the synthesis decreased the nickel nanoparticle size to approximately 7 nm. Dynamic light scattering and scanning electron microscopy confirmed that the particles were in the nanometer range. The structure of the synthesized nickel and nickel hydroxide nanoparticles was identified by X-ray diffraction and Fourier transform infrared spectroscopy.

  17. Characterization and Growth Mechanism of Nickel Nanowires Resulting from Reduction of Nickel Formate in Polyol Medium

    Directory of Open Access Journals (Sweden)

    Olga A. Logutenko

    2016-01-01

    Full Text Available Nickel linear nanostructures were synthesized by reduction of nickel formate with hydrazine hydrate in ethylene glycol medium in the absence of any surfactants or capping agents for direction of the particles growth. The effect of the synthesis conditions such as temperature, reduction time, type of polyol, and nickel formate concentration on the reduction products was studied. The size and morphology of the nickel nanowires were characterized by X-ray diffraction, scanning, and transmission electron microscopy. It was shown that the nickel nanocrystallites were wire-shaped with a face-center-cubic phase. Ethylene glycol was found to play a crucial role in the formation of the nickel nanowires. The possible growth processes of the wire-shaped particles taking place at 110 and 130°C are discussed. It was shown that, under certain synthesis conditions, nickel nanowires grow on the surface of the crystals of the solid intermediate of nickel with hydrazine hydrate.

  18. Nickel and cobalt base alloys

    International Nuclear Information System (INIS)

    Houlle, P.

    1994-01-01

    Nickel base alloys have a good resistance to pitting, cavernous or cracks corrosion. Nevertheless, all the nickel base alloys are not equivalent. Some differences exit between all the families (Ni, Ni-Cu, Ni-Cr-Fe, Ni-Cr-Fe-Mo/W-Cu, Ni-Cr-Mo/W, Ni-Mo). Cobalt base alloys in corrosive conditions are generally used for its wear and cracks resistance, with a compromise to its localised corrosion resistance properties. The choice must be done from the perfect knowledge of the corrosive medium and of the alloys characteristics (chemical, metallurgical). A synthesis of the corrosion resistance in three medium (6% FeCl 3 , 4% NaCl + 1% HCl + 0.1% Fe 2 (SO 4 ) 3 , 11.5% H 2 SO 4 + 1.2% HCl + 1% Fe 2 (SO 4 ) 3 + 1% CuCl 2 ) is presented. (A.B.). 11 refs., 1 fig., 12 tabs

  19. Nickel-Hydrogen Battery Reconditioning

    Science.gov (United States)

    Levine, Erik L.

    1997-01-01

    Reconditioning has traditionally been used as a means of maintaining the performance of normal cells and batteries. This paper describes methods and results in which reconditioning was used to improve the performance of nickel-hydrogen batteries. The following method are discussed: (1) SS/L reconditioning implementation; (2) Superbird reconditioning - pressure/capacity growth; (3) INTELSAT 7/7A reconditioning - cell voltage plateaus and life testing; and (4) N-Star reconditioning - cell voltage plateaus (capacity fading and recovery).

  20. Liquid Membranes as a Tool for Chemical Speciation of Metals in Natural Waters: Organic and Inorganic Complexes of Nickel.

    Science.gov (United States)

    Vergel, Cristina; Mendiguchía, Carolina; Moreno, Carlos

    2018-04-15

    The different species of nickel present in natural waters exhibit different transport behaviour through bulk liquid membranes (BLMs). This fact has been used to design and optimise a separation/pre-concentration system applicable to separate labile and non-labile nickel fractions. A hydrazone derivative-1,2-cyclohexanedione bis-benzoyl-hydrazone (1,2-CHBBH) dissolved in toluene/dimethyl formamide (2% DMF)-was used as a chemical carrier of nickel species, from an aqueous source solution (sample) to a receiving acidic solution. Both chemical and hydrodynamic conditions controlling the transport system were studied and optimised. Under optimum conditions, variations in the transport of nickel ions as a function of organic (humic acids) and inorganic (chloride ions) ligands were studied. Relationships between the permeability coefficient ( P ) or recovery efficiency (%R) and the concentrations of ligands and nickel species were analysed using Winhumic V software. A negative correlation between P and the concentration of organic nickel complexes was found, suggesting that only labile nickel species are transported through the liquid membrane, with non-labile complexes remaining in the water sample; allowing for their separation and subsequent quantification in natural waters.

  1. Liquid Membranes as a Tool for Chemical Speciation of Metals in Natural Waters: Organic and Inorganic Complexes of Nickel

    Directory of Open Access Journals (Sweden)

    Cristina Vergel

    2018-04-01

    Full Text Available The different species of nickel present in natural waters exhibit different transport behaviour through bulk liquid membranes (BLMs. This fact has been used to design and optimise a separation/pre-concentration system applicable to separate labile and non-labile nickel fractions. A hydrazone derivative—1,2-cyclohexanedione bis-benzoyl-hydrazone (1,2-CHBBH dissolved in toluene/dimethyl formamide (2% DMF—was used as a chemical carrier of nickel species, from an aqueous source solution (sample to a receiving acidic solution. Both chemical and hydrodynamic conditions controlling the transport system were studied and optimised. Under optimum conditions, variations in the transport of nickel ions as a function of organic (humic acids and inorganic (chloride ions ligands were studied. Relationships between the permeability coefficient (P or recovery efficiency (%R and the concentrations of ligands and nickel species were analysed using Winhumic V software. A negative correlation between P and the concentration of organic nickel complexes was found, suggesting that only labile nickel species are transported through the liquid membrane, with non-labile complexes remaining in the water sample; allowing for their separation and subsequent quantification in natural waters.

  2. Impacts of Nickel Nanoparticles on Mineral Carbonation

    Directory of Open Access Journals (Sweden)

    Marius Bodor

    2014-01-01

    Full Text Available This work presents experimental results regarding the use of pure nickel nanoparticles (NiNP as a mineral carbonation additive. The aim was to confirm if the catalytic effect of NiNP, which has been reported to increase the dissolution of CO2 and the dissociation of carbonic acid in water, is capable of accelerating mineral carbonation processes. The impacts of NiNP on the CO2 mineralization by four alkaline materials (pure CaO and MgO, and AOD and CC steelmaking slags, on the product mineralogy, on the particle size distribution, and on the morphology of resulting materials were investigated. NiNP-containing solution was found to reach more acidic pH values upon CO2 bubbling, confirming a higher quantity of bicarbonate ions. This effect resulted in acceleration of mineral carbonation in the first fifteen minutes of reaction time when NiNP was present. After this initial stage, however, no benefit of NiNP addition was seen, resulting in very similar carbonation extents after one hour of reaction time. It was also found that increasing solids content decreased the benefit of NiNP, even in the early stages. These results suggest that NiNP has little contribution to mineral carbonation processes when the dissolution of alkaline earth metals is rate limiting.

  3. Characterization and Growth Mechanism of Nickel Nanowires Resulting from Reduction of Nickel Formate in Polyol Medium

    OpenAIRE

    Logutenko, Olga A.; Titkov, Alexander I.; Vorob’yov, Alexander M.; Yukhin, Yriy M.; Lyakhov, Nikolay Z.

    2016-01-01

    Nickel linear nanostructures were synthesized by reduction of nickel formate with hydrazine hydrate in ethylene glycol medium in the absence of any surfactants or capping agents for direction of the particles growth. The effect of the synthesis conditions such as temperature, reduction time, type of polyol, and nickel formate concentration on the reduction products was studied. The size and morphology of the nickel nanowires were characterized by X-ray diffraction, scanning, and transmission ...

  4. Effect on growth and nickel content of cabbage plants watered with nickel solutions

    Energy Technology Data Exchange (ETDEWEB)

    Christensen, O B

    1979-01-01

    Chinese cabbage plants were watered with different concentrations of NiCl/sub 2/ solutions and the effect on growth and uptake of nickel in the plants were studied. No toxic effect on plant growth was observed. A higher content of nickel was found in the plants exposed to more concentrated nickel solutions. Nickel contamination and its clinical consequences are discussed. 29 references, 1 figure, 1 table.

  5. Respiratory carcinogenicity assessment of soluble nickel compounds.

    Science.gov (United States)

    Oller, Adriana R

    2002-10-01

    The many chemical forms of nickel differ in physicochemical properties and biological effects. Health assessments for each main category of nickel species are needed. The carcinogenicity assessment of water-soluble nickel compounds has proven particularly difficult. Epidemiologic evidence indicates an association between inhalation exposures to nickel refinery dust containing soluble nickel compounds and increased risk of respiratory cancers. However, the nature of this association is unclear because of limitations of the exposure data, inconsistent results across cohorts, and the presence of mixed exposures to water-insoluble nickel compounds and other confounders that are known or suspected carcinogens. Moreover, well-conducted animal inhalation studies, where exposures were solely to soluble nickel, failed to demonstrate a carcinogenic potential. Similar negative results were seen in animal oral studies. A model exists that relates respiratory carcinogenic potential to the bioavailability of nickel ion at nuclear sites within respiratory target cells. This model helps reconcile human, animal, and mechanistic data for soluble nickel compounds. For inhalation exposures, the predicted lack of bioavailability of nickel ion at target sites suggests that water-soluble nickel compounds, by themselves, will not be complete human carcinogens. However, if inhaled at concentrations high enough to induce chronic lung inflammation, these compounds may enhance carcinogenic risks associated with inhalation exposure to other substances. Overall, the weight of evidence indicates that inhalation exposure to soluble nickel alone will not cause cancer; moreover, if exposures are kept below levels that cause chronic respiratory toxicity, any possible tumor-enhancing effects (particularly in smokers) would be avoided.

  6. Flare up of Nickel Contact Dermatits Following Oral Challenge

    Directory of Open Access Journals (Sweden)

    C R Srinivas

    1988-01-01

    Full Text Available A patient having contact dermatitis due to nickel on the wrist, sides of neck, thighs and legs, confirmed by patch tests with nickel sulphate, showed aggravation of the dermatitis following oral provocation with 25 mg nickel sulphate.

  7. Air Force standards for nickel hydrogen battery

    Science.gov (United States)

    Hwang, Warren; Milden, Martin

    1994-01-01

    The topics discussed are presented in viewgraph form and include Air Force nickel hydrogen standardization goals, philosophy, project outline, cell level standardization, battery level standardization, and schedule.

  8. Nickel-hydrogen bipolar battery system

    Science.gov (United States)

    Thaller, L. H.

    1982-01-01

    Rechargeable nickel-hydrogen systems are described that more closely resemble a fuel cell system than a traditional nickel-cadmium battery pack. This was stimulated by the currently emerging requirements related to large manned and unmanned low Earth orbit applications. The resultant nickel-hydrogen battery system should have a number of features that would lead to improved reliability, reduced costs as well as superior energy density and cycle lives as compared to battery systems constructed from the current state-of-the-art nickel-hydrogen individual pressure vessel cells.

  9. On the reflectivity of nickel neutron mirrors

    Energy Technology Data Exchange (ETDEWEB)

    Adib, M.; Maayouf, R.M.A.; Abdel-Kawy, A.; Habib, N. (Atomic Energy Establishment, Cairo (Egypt). Reactor and Neutron Physics Dept.); Kenawy, M.A.; Wahba, M.; Ashry, A.H. (Ain Shams Univ., Cairo (Egypt))

    1991-02-01

    Neutron reflectivities were determined for 300 nm thick films of natural nickel and nickel 58 coated on glass plates. The measurements were performed at glancing angles between 40' and 60'. The incident neutron beam from one of the ET-RR-1 reactor horizontal channels covered neutron wavelengths between 0.55 and 0.80 nm. It was found that nickel 58, because of the high value of its critical glancing angle, is more efficient as a neutron mirror than natural nickel. (orig.).

  10. METHOD OF APPLYING NICKEL COATINGS ON URANIUM

    Science.gov (United States)

    Gray, A.G.

    1959-07-14

    A method is presented for protectively coating uranium which comprises etching the uranium in an aqueous etching solution containing chloride ions, electroplating a coating of nickel on the etched uranium and heating the nickel plated uranium by immersion thereof in a molten bath composed of a material selected from the group consisting of sodium chloride, potassium chloride, lithium chloride, and mixtures thereof, maintained at a temperature of between 700 and 800 deg C, for a time sufficient to alloy the nickel and uranium and form an integral protective coating of corrosion-resistant uranium-nickel alloy.

  11. [Nickel levels in female dermatological patients].

    Science.gov (United States)

    Schwegler, U; Twardella, D; Fedorov, M; Darsow, U; Schaller, K-H; Habernegg, R; Behrendt, H; Fromme, H

    2009-07-01

    Nickel levels in urine were determined among 163 female dermatological patients aged 18 to 46 years. Data on life-style factors were collected in parallel via a questionnaire. Urinary nickel excretion was in the normal range of the German female population (0.2-46.1 microg Ni/g creatinine). The 95th percentile (3.9 microg Ni/l urine) exceeded the German reference value (3.0 microg Ni/l urine). In the multivariate regression analyses we found a statistically significant increase of ln-transformed nickel levels with increase in age and in women using dietary supplements. The following variables were not associated with Nickel urine levels: suffering from nickel eczema, smoking, drinking stagnated water, eating foods with high nickel contents and using nickel-containing kitchen utensils as, for example, an electric kettle with an open heater coil. We conclude that personal urinary levels should be assessed with simultaneous consideration of habits and life-style factors. A German national survery would be useful. Those patients who experience the exacerbation of their eczema in cases of oral provocation, for example, by a high nickel diet should be aware of potential sources of nickel, such as supplements.

  12. Nickel-induced cytokine production from mononuclear cells in nickel-sensitive individuals and controls. Cytokine profiles in nickel-sensitive individuals with nickel allergy-related hand eczema before and after nickel challenge

    DEFF Research Database (Denmark)

    Borg, L; Christensen, J M; Kristiansen, J

    2000-01-01

    Exposure to nickel is a major cause of allergic contact dermatitis which is considered to be an inflammatory response induced by antigen-specific T cells. Here we describe the in vitro analysis of the nickel-specific T-cell-derived cytokine response of peripheral blood mononuclear cells from 35...... was somewhat of a surprise, since previous studies have suggested a Th1 response in nickel-mediated allergic contact dermatitis. Subsequently, the nickel-allergic individuals were randomized to experimental exposure to nickel or vehicle in a double-blind design. A daily 10-min exposure of one finger to 10 ppm...... nickel solution for 1 week followed by 100 ppm for an additional week evoked a clinical response of hand eczema in the nickel-exposed group. Blood samples were drawn on days 7 and 14 after the start of this exposure to occupationally relevant concentrations of nickel. No statistically significant...

  13. Enterobacter asburiae KUNi5, a Nickel Resistant Bacterium for Possible Bioremediation of Nickel Contaminated Sites.

    Science.gov (United States)

    Paul, Anirudha; Mukherjee, Samir Kumar

    2016-01-01

    Nickel resistant bacterial strain Enterobacter asburiae KUNi5 was isolated and showed resistance up to 15 mM and could remove Ni optimally better at 37 degrees C and pH 7. Maximum removal was found at initial concentration of 0.5 to 2 mM, however, growth and Ni removal were affected by other heavy metals. Major amount of the metal was accumulated in the membrane fractions and certain negatively charged groups were found responsible for Ni binding. KUNi5 could also produce 1-aminocyclopropane-1-carboxylate deaminase, indole-acetic acid and siderophore. It seems that KUNi5 could be a possible candidate for Ni detoxification and plant growth promotion in Ni-contaminated field.

  14. Risk assessment of nickel carcinogenicity and occupational lung cancer.

    OpenAIRE

    Shen, H M; Zhang, Q F

    1994-01-01

    Recent progress in risk assessment of nickel carcinogenicity and its correlation with occupational lung cancer in nickel-exposed workers is reviewed. Epidemiological investigations provide reliable data indicating the close relation between nickel exposure and high lung cancer risk, especially in nickel refineries. The nickel species-specific effects and the dose-response relationship between nickel exposure and lung cancer are among the main questions that are explored extensively. It is als...

  15. Metallic nickel nanoparticles and their effect on the embryonic development of the sea urchin Paracentrotus lividus

    International Nuclear Information System (INIS)

    Kanold, Julia Maxi; Wang, Jiabin; Brümmer, Franz; Šiller, Lidija

    2016-01-01

    The presence of nanoparticles in many industrial applications and daily products is making it nowadays crucial to assess their impact when exposed to the environment. Metallic nickel nanoparticles (Ni NPs) are of high industrial interest due to their ability to catalyze the reversible hydration of CO_2 to carbonic acid at ambient conditions. We characterized metallic Ni NPs by XRD, HRTEM and EDS and determined the solubility of free nickel ions from 3 mg/L metallic Ni NPs in seawater by ICP-MS over 96 h, which was below 3%. Further, embryonic development of the sea urchin Paracentrotus lividus was investigated for 48 h in the presence of metallic Ni NPs (0.03 mg/L to 3 mg/L), but no lethal effects were observed. However, 3 mg/L metallic Ni NPs caused a size reduction similar to 1.2 mg/L NiCl_2*6 H_2O. The obtained results contribute to current studies on metallic Ni NPs and point to their consequences for the marine ecosystem. - Highlights: • Low solubility of nickel ions from metallic nickel nanoparticles in seawater. • No lethality of sea urchin embryos up to 3 mg/L metallic nickel nanoparticles. • Considerable size reduction after 48 h was comparable to the reduction for 1.2 mg/L nickel salt. • Contributes to the overall understanding of metallic Ni NPs in the marine environment. - Metallic nickel nanoparticles display weak dissolution rates in seawater, but higher concentrations resulted in similar effects on sea urchin embryonic development as nickel salt.

  16. Detoxification of rats subjected to nickel chloride by a biomaterial-based carbonated orthophosphate.

    Science.gov (United States)

    Boulila, S; El Feki, A; Oudadesse, H; Kallel, C; El Feki, H

    2014-09-01

    Recently, the therapeutic approaches of the detoxification against the metals (nickel) in the body are the use of biomaterials such as carbonated hydroxyapatite. The aim of this study is therefore to analyze the physiological and physicochemical parameters of strain white rats "Wistar" receiving nickel chloride and to study the protective associative of apatite against adverse effects of this metal, and this in comparison with control rats. Our results showed that the nickel induced in rats an oxidative stress objectified by elevated levels of thiobarbituric acid-reactive substances and conjugated dienes associated with inhibition of the activity of the antioxidant defense system such as glutathione peroxidase, superoxide dismutase and catalase in the liver, kidney, spleen and erythrocyte. Disorders balances of ferric, phosphocalcic, a renal failure and a liver toxicity were observed in rats exposed to nickel. As well as a significant increase in the rate of nickel in the bones and microcytic anemia was revealed. However, the implantation of carbonated hydroxyapatite in capsule form protects rats intoxicated by the nickel against the toxic effects of this metal by lowering the levels of markers of lipid peroxidation and improving the activities of defense enzymes. Our implantation technique is effective to correct ferric balance and phosphocalcic equilibrium, to protect liver and kidney function, to reduce the rate of bone nickel and to correct anemia. They clearly explain the beneficial and protective of our biomaterial which aims the detoxification of rats receiving nickel by substituting cationic (Ca(2+) by Ni(2+)) and anionic (OH(-) by Cl(-)) confirmed by physicochemical characterization like the IR spectroscopy and X-ray diffraction. These techniques have shown on the one hand a duplication of OH(-) bands (IR) and on the other hand the increase of the volume of the apatite cell after these substitutions (X-ray diffraction). Copyright © 2014 Elsevier Masson

  17. Behavioral interventions to reduce nickel exposure in a nickel processing plant.

    Science.gov (United States)

    Rumchev, Krassi; Brown, Helen; Wheeler, Amanda; Pereira, Gavin; Spickett, Jeff

    2017-10-01

    Nickel is a widely-used material in many industries. Although there is enough evidence that occupational exposure to nickel may cause respiratory illnesses, allergies, and even cancer, it is not possible to stop the use of nickel in occupational settings. Nickel exposure, however, can be controlled and reduced significantly in workplaces. The main objective of this study was to assess if educational intervention of hygiene behavior could reduce nickel exposure among Indonesian nickel smelter workers. Participants were randomly assigned to three intervention groups (n = 99). Group one (n = 35) received only an educational booklet about nickel, related potential health effects and preventive measures, group two (n = 35) attended a presentation in addition to the booklet, and group three (n = 29) received personal feedback on their biomarker results in addition to the booklet and presentations. Pre- and post-intervention air sampling was conducted to measure concentrations of dust and nickel in air along with worker's blood and urine nickel concentrations. The study did not measure significant differences in particles and nickel concentrations in the air between pre- and post-interventions. However, we achieved significant reductions in the post intervention urine and blood nickel concentrations which can be attributed to changes in personal hygiene behavior. The median urinary nickel concentration in the pre-intervention period for group one was 52.3 µg/L, for group two 57.4 µg/L, and group three 43.2 µg/L which were significantly higher (pnickel with significantly (p nickel levels of 0.1 µg/L for all groups. The study showed that educational interventions can significantly reduce personal exposure levels to nickel among Indonesian nickel smelter workers.

  18. Nickel detoxification and plant growth promotion by multi metal resistant plant growth promoting Rhizobium species RL9.

    Science.gov (United States)

    Wani, Parvaze Ahmad; Khan, Mohammad Saghir

    2013-07-01

    Pollution of the biosphere by heavy metals is a global threat that has accelerated dramatically since the beginning of industrial revolution. The aim of the study is to check the resistance of RL9 towards the metals and to observe the effect of Rhizobium species on growth, pigment content, protein and nickel uptake by lentil in the presence and absence of nickel. The multi metal tolerant and plant growth promoting Rhizobium strain RL9 was isolated from the nodules of lentil. The strain not only tolerated nickel but was also tolerant o cadmium, chromium, nickel, lead, zinc and copper. The strain tolerated nickel 500 μg/mL, cadmium 300 μg/mL, chromium 400 μg/mL, lead 1,400 μg/mL, zinc 1,000 μg/mL and copper 300 μg/mL, produced good amount of indole acetic acid and was also positive for siderophore, hydrogen cyanide and ammonia. The strain RL9 was further assessed with increasing concentrations of nickel when lentil was used as a test crop. The strain RL9 significantly increased growth, nodulation, chlorophyll, leghaemoglobin, nitrogen content, seed protein and seed yield compared to plants grown in the absence of bioinoculant but amended with nickel The strain RL9 decreased uptake of nickel in lentil compared to plants grown in the absence of bio-inoculant. Due to these intrinsic abilities strain RL9 could be utilized for growth promotion as well as for the remediation of nickel in nickel contaminated soil.

  19. Systemic nickel: the contribution made by stainless-steel cooking utensils.

    Science.gov (United States)

    Flint, G N; Packirisamy, S

    1995-04-01

    An extensive programme of cooking operations, using household recipes, has shown that, apart from aberrant values associated with new pans on first use, the contribution made by 19 Cr/9 Ni stainless-steel cooking utensils to nickel in the diet is negligible. The amount of nickel (0 to 8 micrograms) derived from the utensils in standard portions of various "aggressive" foodstuffs tested was less than that to be found occurring in 1 square of a bitter-sweet chocolate bar. New pans, if first used with acid fruits, can show a greater pick-up of nickel, which, in the worst case observed, amounted to approximately 1/5 of the normal daily intake for the average person (ca. 200 micrograms). This situation does not recur in subsequent usage, even after the pan has been cleaned by abrasion. A higher rate of nickel release was observed in new pans on first use from 4 manufacturers located in different countries and appears to be a general phenomenon. This could provide a possible explanation for the high pick-up of nickel by acid fruits reported in 1 instance in the literature.

  20. A simple and efficient method of nickel electrodeposition for the cyclotron production of 64Cu

    International Nuclear Information System (INIS)

    Manrique-Arias, Juan C.; Avila-Rodriguez, Miguel A.

    2014-01-01

    Nickel targets for the cyclotron production of 64 Cu were prepared by electrodeposition on a gold backing from nickel chloride solutions using boric acid as buffer. Parameters studied were nickel chloride and boric acid concentration, temperature and current density. All plating conditions studied were successful obtaining efficiencies of approximately 90% in 2–3 h, reaching almost quantitative plating (>97%) in 10–20 h depending on the current density. All plated targets withstood proton irradiations up to 40 µA for 2 h. Recovered nickel was successfully recycled and reused with an overall efficiency >95%. - Highlights: • Simple and efficient method of Ni electrodeposition from NiCl 2 solutions. • Represents an improvement over current methods for the preparation of Ni targets. • All plated targets underwent irradiation and withstood currents up to 40 µA for 2 h. • Nickel target material was recycled and reused with an overall efficiency >95%. • Specific activity of 64 Cu was similar than that obtained with older methods of Ni plating

  1. Histidine protects against zinc and nickel toxicity in Caenorhabditis elegans.

    Directory of Open Access Journals (Sweden)

    John T Murphy

    2011-03-01

    Full Text Available Zinc is an essential trace element involved in a wide range of biological processes and human diseases. Zinc excess is deleterious, and animals require mechanisms to protect against zinc toxicity. To identify genes that modulate zinc tolerance, we performed a forward genetic screen for Caenorhabditis elegans mutants that were resistant to zinc toxicity. Here we demonstrate that mutations of the C. elegans histidine ammonia lyase (haly-1 gene promote zinc tolerance. C. elegans haly-1 encodes a protein that is homologous to vertebrate HAL, an enzyme that converts histidine to urocanic acid. haly-1 mutant animals displayed elevated levels of histidine, indicating that C. elegans HALY-1 protein is an enzyme involved in histidine catabolism. These results suggest the model that elevated histidine chelates zinc and thereby reduces zinc toxicity. Supporting this hypothesis, we demonstrated that dietary histidine promotes zinc tolerance. Nickel is another metal that binds histidine with high affinity. We demonstrated that haly-1 mutant animals are resistant to nickel toxicity and dietary histidine promotes nickel tolerance in wild-type animals. These studies identify a novel role for haly-1 and histidine in zinc metabolism and may be relevant for other animals.

  2. Uptake, distribution and metabolic fate of 59Fe, 58Co, 54Mn and 65Zn in plants and their mobility and availability to crops in typical black and laterite soils

    International Nuclear Information System (INIS)

    D'Souza, T.J.; Mistry, K.B.

    1979-01-01

    Studies were undertaken on typical soils of India. Nutrient culture experiments indicated that with identical plant growth periods the accumulation in aerial tissues of 65 Zn and 54 Mn was greater than that of 58 Co and 59 Fe. The distribution of 59 Fe, 58 Co and 65 Zn in the various aerial organs of bean plants was generally uniform whereas the distribution of 54 Mn followed an acropetal gradient. The chemical association of 59 Fe, 58 Co and 65 Zn in the edible bean pods was predominantly with lipids and ionic forms whereas 54 Mn association was mainly with ionic forms. The plant uptake of these radionuclides from typical black and laterite soils showed maximum accumulation of 54 Mn followed by 65 Zn, 59 Fe and 58 Co in both soil types and the uptake was greater from the laterite soil than from the black soil. Flooding treatment of rice, while showing a reduction of 59 Fe uptake, showed an increase in plant uptake of 58 Co, 54 Mn and 65 Zn in both soil types. Organic matter addition resulted in a significant reduction of 59 Fe and 58 Co in the laterite soil and of 65 Zn in the black soil. All the four nuclides were completely immobile in the two soil types when leached with rain water or irrigation waters or when treated with organic matter. However, leaching with 10 -2 M EDTA solution induced a rapid breakthrough of all the four radionuclides. (author)

  3. Cross-Coupling of Amides with Alkylboranes via Nickel-Catalyzed C–N Bond Cleavage

    KAUST Repository

    Liu, Xiangqian; Hsiao, Chien-Chi; Guo, Lin; Rueping, Magnus

    2018-01-01

    A protocol for the nickel-catalyzed alkylation of amides was established. The use of alkylboranes as nucleophilic partners allowed the use of mild reaction conditions and compatibility of various functional groups with respect to both coupling partners. The catalytic alkylation proceeded selectively at the amides in the presence of other functional groups as well as other carboxylic acid derived moieties.

  4. Cross-Coupling of Amides with Alkylboranes via Nickel-Catalyzed C–N Bond Cleavage

    KAUST Repository

    Liu, Xiangqian

    2018-05-09

    A protocol for the nickel-catalyzed alkylation of amides was established. The use of alkylboranes as nucleophilic partners allowed the use of mild reaction conditions and compatibility of various functional groups with respect to both coupling partners. The catalytic alkylation proceeded selectively at the amides in the presence of other functional groups as well as other carboxylic acid derived moieties.

  5. Surface preparation process of a uranium titanium alloy, in particular for chemical nickel plating

    International Nuclear Information System (INIS)

    Henri, A.; Lefevre, D.; Massicot, P.

    1987-01-01

    In this process the uranium alloy surface is attacked with a solution of lithium chloride and hydrochloric acid. Dissolved uranium can be recovered from the solution by an ion exchange resin. Treated alloy can be nickel plated by a chemical process [fr

  6. Nickel allergy in a Danish population 25 years after the first nickel regulation

    DEFF Research Database (Denmark)

    Ahlström, Malin G; Menné, Torkil; Thyssen, Jacob P

    2017-01-01

    BACKGROUND: Nickel in metallic items has been regulated in Denmark since 1990; however, 10% of young Danish women are still sensitized to nickel. There is a need for continuous surveillance of the effect of regulation. OBJECTIVES: To identify current self-reported metallic exposures leading...... reactions within 30 min of contact were reported by 30.7% of patients. CONCLUSIONS: Nickel exposures that led to the implementation of a nickel regulation seem to persist. The durations of contact with metallic items to fall under the current REACH regulation of nickel correspond well with the results...... to dermatitis in nickel-allergic patients, and the minimum contact time needed for dermatitis to occur. METHODS: A questionnaire was sent to all patients who reacted positively to nickel sulfate 5% pet. within the last 5 years at the Department of Dermatology and Allergy, Gentofte Hospital. RESULTS...

  7. Nickel concentrations in fingernails as a measure of occupational exposure to nickel

    DEFF Research Database (Denmark)

    Peters, K; Gammelgaard, Bente; Menné, T

    1991-01-01

    in nails (p less than 0.001). The difference between the 2 levels was also significant (p less than 0.001). No correlation between the nickel concentration in fingernails and the duration of exposure could be demonstrated. It was concluded that the higher the nickel level in the fingernails, the greater...... is the possibility that the person is occupationally exposed to nickel. Nail analysis is suggested as a measure of occupational exposure to nickel.......The nickel concentration in fingernails from 2 groups of people occupationally exposed to nickel was determined. In one group, comprising 83 persons moderately exposed to nickel, the mean +/- standard deviation (SD) was 29.2 micrograms/g +/- 56.7 micrograms/g and the median 13.8 micrograms/g (range...

  8. Prevalence of nickel allergy in Europe following the EU Nickel Directive - a review

    DEFF Research Database (Denmark)

    Ahlström, Malin G; Thyssen, Jacob P; Menné, Torkil

    2017-01-01

    .4% versus 19.8%) (p = 0.02), in female dermatitis patients aged ≤17 years (14.3% versus 29.2%) (p women: 20.2% versus 36.6%) (p men: 4.9% versus 6.6%) (p ..., and generally remained high, affecting 8-18% of the general population. A consistent pattern of decreasing prevalence of nickel allergy in some EU countries was observed, although the prevalence among young women remains high. Steps should be taken for better prevention of nickel allergy in EU countries.......Nickel contact allergy remains a problem in EU countries, despite the EU Nickel Directive. To study the prevalence of nickel allergy in EU countries following the implementation of the EU Nickel Directive, we performed a systematic search in PubMed for studies that examined the prevalence of nickel...

  9. Coin exposure may cause allergic nickel dermatitis

    DEFF Research Database (Denmark)

    Thyssen, Jacob P; Gawkrodger, David J; White, Ian R

    2012-01-01

    Nickel is used in coins because the metal has beneficial properties, including price, colour, weight, and corrosion resistance, and also because it is easy to stamp. It has often been claimed that the duration of skin contact with coins is too short to cause nickel release and dermatitis. However...

  10. Microwave dielectric properties of nanostructured nickel ferrite

    Indian Academy of Sciences (India)

    Wintec

    Abstract. Nickel ferrite is one of the important ferrites used in microwave devices. In the present work, we have synthesized nanoparticles of nickel ferrite using chemical precipitation technique. The crystal structure and grain size of the particles are studied using XRD. The microwave dielectric properties of nanostructured.

  11. Technology development for producing nickel metallic filters

    International Nuclear Information System (INIS)

    Hubler, C.H.

    1990-01-01

    A technology to produce metallic filters by Instituto de Engenharia Nuclear (IEN-Brazilian CNEN) providing the Instituto de Pesquisas Energeticas e Nucleares (IPEN-Brazilian CNEN) in obtaining nickel alloy filters used for filtration process of uranium hexafluoride, was developed. The experiences carried out for producing nickel conical trunk filters from powder metallurgy are related. (M.C.K.)

  12. Method of nickel-plating large components

    International Nuclear Information System (INIS)

    Wilbuer, K.

    1997-01-01

    The invention concerns a method of nickel-plating components, according to which even large components can be provided with an adequate layer of nickel which is pore- and stress-free and such that water is not lost. According to the invention, the component is heated and, after heating, is pickled, rinsed, scoured, plated in an electrolysis process, and rinsed again. (author)

  13. Evolution of the nickel/zirconia interface

    International Nuclear Information System (INIS)

    Shinde, S.L.; Olson, D.A.; De Jonghe, L.C.; Miller, R.A.

    1986-01-01

    The changes taking place at the nickel zirconia interface during oxidation in air at 900 0 C were studied using analytical electron microscopy (AEM). The nickel oxide layer growing at the interface and the stabilizers used in zirconia interact, giving different interface morphologies

  14. Systemic contact dermatitis due to nickel

    Directory of Open Access Journals (Sweden)

    Taruli Olivia

    2015-08-01

    Full Text Available Introduction: Systemic contact dermatitis (SCD is a systemic reactivation of a previous allergic contact dermatitis. The initial exposure may usually be topical, followed by oral, intravenous or inhalation exposure leading to a systemic hypersensitivity reaction. A case of a 27 year-old male with SCD due to nickel is reported Case Report: A 27 year-old male presented with recurrent pruritic eruption consist of deep seated vesicles on both palmar and left plantar since 6 months before admission. This complaint began after patient consumed excessive amounts of chocolate, canned food, and beans. The patient worked as a technician in a food factory. History of allergy due to nickel was acknowledged since childhood. The clinical presentation was diffuse deep seated vesicles, and multiple erythematous macules to plaques, with collarette scale. Patch test using the European standard showed a +3 result to nickel. The patient was diagnosed as systemic contact dermatitis due to nickel. The treatments were topical corticosteroid and patient education of avoidance of both contact and systemic exposure to nickel. The patient showed clinical improvement after 2 weeks. Discussion: SCD was diagnosed due to the history of massive consumption of food containing nickel in a patient who had initial sensitization to nickel, with clinical features and the patch test result. Advice to be aware of nickel and its avoidance is important in SCD management.

  15. Structure investigations of electrodeposited nickel

    International Nuclear Information System (INIS)

    Vertes, A.; Czako-Nagy, I.; Lakatos-Varsanyi, M.; Brauer, G.; Leidheiser, H. Jr

    1981-01-01

    Electrodeposited nickel samples were investigated by positron annihilation (lifetime and Doppler-broadening), Moessbauer effect and X-ray diffraction measurements. Two-component positron lifetime spectra were obtained. The first component is thought to result from bulk annihilation and trapping at single trapping centres (TC), their concentrations are obtained from the trapping model. The second one possibly denotes annihilation at voids, the number of which is dependent on the stress in the deposit. The Moessbauer results show differences in the magnetic orientation in the three samples examined. (author)

  16. Electrodeposited tungsten-nickel-boron: A replacement for hexavalent chromium

    International Nuclear Information System (INIS)

    Steffani, C.; Meltzer, M.

    1995-04-01

    Chromium, deposited from acidic solutions of its hexavalent ion, has been the rule for wear resistant, corrosion resistant coatings for many years. Although chromium coatings are durable, the plating process generates air emissions, effluent rinse waters, and process solutions that are toxic, suspected carcinogens, and a risk to human health and the environment. Tungsten-nickel-boron (W-Ni-B) alloy deposition is a potential substitute for hexavalent chrome. It has excellent wear, corrosion, and mechanical properties and also may be less of an environmental risk. This study examines the electroplating process and deposit properties of W-Ni-B and compares them with those of hexavalent chrome

  17. Galvanic corrosion resistance of welded dissimilar nickel-base alloys

    International Nuclear Information System (INIS)

    Corbett, R.A.; Morrison, W.S.; Snyder, R.J.

    1986-01-01

    A program for evaluating the corrosion resistance of various dissimilar welded nickel-base alloy combinations is outlined. Alloy combinations included ALLCORR, Hastelloy C-276, Inconel 72 and Inconel 690. The GTAW welding process involved both high and minimum heat in-put conditions. Samples were evaluated in the as-welded condition, as well as after having been aged at various condtions of time and temperature. These were judged to be most representative of process upset conditions which might be expected. Corrosion testing evaluated resistance to an oxidizing acid and a severe service environment in which the alloy combinations might be used. Mechanical properties are also discussed

  18. Nickel-cadmium battery system for electric vehicles

    Science.gov (United States)

    Klein, M.; Charkey, A.

    A nickel-cadmium battery system has been developed and is being evaluated for electric vehicle propulsion applications. The battery system design features include: (1) air circulation through gaps between cells for thermal management, (2) a metal-gas coulometric fuel gauge for state-of-charge and charge control, and (3) a modified constant current ac/dc power supply for the charger. The battery delivers one and a half to two times the energy density of comparable lead-acid batteries depending on operating conditions.

  19. Aluminium and nickel in human albumin solutions

    DEFF Research Database (Denmark)

    Gammelgaard, Bente; Sandberg, E

    1989-01-01

    Five different brands of commercially available human albumin solutions for infusion were analysed for their aluminium and nickel contents by atomic absorption spectrometry. The aluminium concentrations ranged from 12 micrograms/l to 1109 micrograms/l and the nickel concentrations ranged from 17...... micrograms/l to 77 micrograms/l. Examination of the aluminium and nickel contents of the constituents for the production of one brand showed too low levels to explain the final contamination of the product. By following the aluminium and nickel concentrations of the same brand during the production...... of a batch of albumin solution, filtration was shown to contribute to contamination, although the largest increase in aluminium as well as nickel concentrations appeared during the bulk concentrating process. To avoid health risks to certain patients, regulations should be established requiring aluminium...

  20. Analysis of continuous solvent extraction of nickel from spent electroless nickel plating baths by a mixer-settler.

    Science.gov (United States)

    Huang, Ying; Tanaka, Mikiya

    2009-05-30

    It is urgent to develop an effective technique to treat the large amount of spent electroless nickel plating bath and recycle the high concentration nickel. In our previous study, high recycling efficiency of nickel from the model spent bath was obtained by continuous solvent extraction with 2-hydroxy-5-nonylacetophenone oxime (LIX84I) as the extractant and 2-ethylhexylphosphonic acid mono-2-ethylhexyl ester (PC88A) as the accelerator using a mixer-settler extractor. It was observed that the extraction efficiency was affected by the operation parameters such as the flow rates of the aqueous and organic phases and the total stage number. In the present study, the effects of the operation parameters on the extraction efficiency were quantitatively studied on the basis of the pseudo-first-order interfacial extraction rate equation together with the hydrodynamic properties in the mixer. The organic phase holdup, measured under varying conditions of the flow rates of both phases, was analyzed by the Takahashi-Takeuchi holdup model in order to estimate the specific interfacial area. The overall extraction rate coefficients defined by the product of the interfacial extraction rate constant and the specific interfacial area were evaluated using the experimental data and ranged from 3.5 x 10(-3) to 6.7 x 10(-3)s(-1), which was close to the value of 3.4 x 10(-3)s(-1) obtained by batch extraction. Finally, an engineering simulation method was established for assessing the extraction efficiency of nickel during a multistage operation.

  1. Analysis of continuous solvent extraction of nickel from spent electroless nickel plating baths by a mixer-settler

    Energy Technology Data Exchange (ETDEWEB)

    Huang, Ying, E-mail: huang-ying@aist.go.jp [Metals Recycling Group, Research Institute for Environmental Management Technology, National Institute of Advanced Industrial Science and Technology (AIST), 16-1 Onogawa, Tsukuba, Ibaraki 305-8569 (Japan); Tanaka, Mikiya, E-mail: mky-tanaka@aist.go.jp [Metals Recycling Group, Research Institute for Environmental Management Technology, National Institute of Advanced Industrial Science and Technology (AIST), 16-1 Onogawa, Tsukuba, Ibaraki 305-8569 (Japan)

    2009-05-30

    It is urgent to develop an effective technique to treat the large amount of spent electroless nickel plating bath and recycle the high concentration nickel. In our previous study, high recycling efficiency of nickel from the model spent bath was obtained by continuous solvent extraction with 2-hydroxy-5-nonylacetophenone oxime (LIX84I) as the extractant and 2-ethylhexylphosphonic acid mono-2-ethylhexyl ester (PC88A) as the accelerator using a mixer-settler extractor. It was observed that the extraction efficiency was affected by the operation parameters such as the flow rates of the aqueous and organic phases and the total stage number. In the present study, the effects of the operation parameters on the extraction efficiency were quantitatively studied on the basis of the pseudo-first-order interfacial extraction rate equation together with the hydrodynamic properties in the mixer. The organic phase holdup, measured under varying conditions of the flow rates of both phases, was analyzed by the Takahashi-Takeuchi holdup model in order to estimate the specific interfacial area. The overall extraction rate coefficients defined by the product of the interfacial extraction rate constant and the specific interfacial area were evaluated using the experimental data and ranged from 3.5 x 10{sup -3} to 6.7 x 10{sup -3} s{sup -1}, which was close to the value of 3.4 x 10{sup -3} s{sup -1} obtained by batch extraction. Finally, an engineering simulation method was established for assessing the extraction efficiency of nickel during a multistage operation.

  2. Analysis of continuous solvent extraction of nickel from spent electroless nickel plating baths by a mixer-settler

    International Nuclear Information System (INIS)

    Huang, Ying; Tanaka, Mikiya

    2009-01-01

    It is urgent to develop an effective technique to treat the large amount of spent electroless nickel plating bath and recycle the high concentration nickel. In our previous study, high recycling efficiency of nickel from the model spent bath was obtained by continuous solvent extraction with 2-hydroxy-5-nonylacetophenone oxime (LIX84I) as the extractant and 2-ethylhexylphosphonic acid mono-2-ethylhexyl ester (PC88A) as the accelerator using a mixer-settler extractor. It was observed that the extraction efficiency was affected by the operation parameters such as the flow rates of the aqueous and organic phases and the total stage number. In the present study, the effects of the operation parameters on the extraction efficiency were quantitatively studied on the basis of the pseudo-first-order interfacial extraction rate equation together with the hydrodynamic properties in the mixer. The organic phase holdup, measured under varying conditions of the flow rates of both phases, was analyzed by the Takahashi-Takeuchi holdup model in order to estimate the specific interfacial area. The overall extraction rate coefficients defined by the product of the interfacial extraction rate constant and the specific interfacial area were evaluated using the experimental data and ranged from 3.5 x 10 -3 to 6.7 x 10 -3 s -1 , which was close to the value of 3.4 x 10 -3 s -1 obtained by batch extraction. Finally, an engineering simulation method was established for assessing the extraction efficiency of nickel during a multistage operation.

  3. A review of nickel hydrogen battery technology

    Energy Technology Data Exchange (ETDEWEB)

    Smithrick, J.J.; Odonnell, P.M.

    1995-05-01

    This paper on nickel hydrogen batteries is an overview of the various nickel hydrogen battery design options, technical accomplishments, validation test results and trends. There is more than one nickel hydrogen battery design, each having its advantage for specific applications. The major battery designs are individual pressure vessel (IPV), common pressure vessel (CPV), bipolar and low pressure metal hydride. State-of-the-art (SOA) nickel hydrogen batteries are replacing nickel cadmium batteries in almost all geosynchronous orbit (GEO) applications requiring power above 1 kW. However, for the more severe low earth orbit (LEO) applications (greater than 30,000 cycles), the current cycle life of 4000 to 10,000 cycles at 60 percent DOD should be improved. A NASA Lewis Research Center innovative advanced design IPV nickel hydrogen cell led to a breakthrough in cycle life enabling LEO applications at deep depths of discharge (DOD). A trend for some future satellites is to increase the power level to greater than 6 kW. Another trend is to decrease the power to less than 1 kW for small low cost satellites. Hence, the challenge is to reduce battery mass, volume and cost. A key is to develop a light weight nickel electrode and alternate battery designs. A common pressure vessel (CPV) nickel hydrogen battery is emerging as a viable alternative to the IPV design. It has the advantage of reduced mass, volume and manufacturing costs. A 10 Ah CPV battery has successfully provided power on the relatively short lived Clementine Spacecraft. A bipolar nickel hydrogen battery design has been demonstrated (15,000 LEO cycles, 40 percent DOD). The advantage is also a significant reduction in volume, a modest reduction in mass, and like most bipolar designs, features a high pulse power capability. A low pressure aerospace nickel metal hydride battery cell has been developed and is on the market.

  4. Recent progress in nickel carcinogenesis

    Energy Technology Data Exchange (ETDEWEB)

    Sunderman, F.W. Jr.

    1984-01-01

    Positive bacterial mutagenesis tests have been obtained with Ni(II) in Corynybacterium, but not in E. coli, S. typhimurium, or B. subtilis. Transformation assays of several soluble and crystalline Ni compounds have been positive in Syrian hamster embryo cells. Ni(II) binds to DNA, RNA, and nucleoproteins, and becomes localized in nucleoli. Genotoxic effects of Ni include: (a) chromosomal aberrations, including sister-chromatid exchanges, (b) DNA strandbreaks and DNA-protein crosslinks, (c) inhibition of DNA and RNA synthesis, (d) infidelity of DNA transcription, and (e) mutations at the HGPRTase locus in Chinese hamster cells and the TK locus in mouse lymphoma cells. These findings are consistent with somatic mutation as the mechanism for initiation of nickel carcinogenesis. Ni compounds cause reversible transition of double-stranded poly(dG-dC) DNA from the right-handed B-helix to the left-handed Z-helix, suggesting a mechanism whereby nickel might modulate oncogene expression. 99 references, 4 tables.

  5. Influence of iron doping on tetravalent nickel content in catalytic oxygen evolving films

    Energy Technology Data Exchange (ETDEWEB)

    Li, Nancy; Bediako, D. Kwabena; Hadt, Ryan G.; Hayes, Dugan; Kempa, Thomas J.; von Cube, Felix; Bell, David C.; Chen, Lin X.; Nocera, Daniel G.

    2017-01-30

    Iron doping of nickel oxide films results in enhanced activity for promoting the oxygen evolution reaction (OER). Whereas this enhanced activity has been ascribed to a unique iron site within the nickel oxide matrix, we show here that Fe doping influences the Ni valency. The percent of Fe3+ doping promotes the formation of formal Ni4+, which in turn directly correlates with an enhanced activity of the catalyst in promoting OER. The role of Fe3+ is consistent with its behavior as a superior Lewis acid.

  6. Copper removal and nickel for exchange cationic with a natural zeolite

    International Nuclear Information System (INIS)

    Estupinan, Arnoldy; Sarmiento, Diego; Belalcazar de Galvis, Ana Maria

    1998-01-01

    Natural zeolite clinoptilolite, was used to remove copper and nickel from waste waters of a galvanotechnical company. Exchange capacity determined for the zeolite after its transformation to homoionic sodium form, was 0.794 meq/g for copper and 0.447 meq/g for nickel. There were made batch and column experiments, reaching the last one a better approach to the equilibrium. From the degeneration essays, the sodical zeolite concentrates the copper in the waste waters to 23.5 up times the level found for the acid rinsing waters; it shows its potential use in treatment of these waste, because its effectiveness and low cost

  7. Unraveling climatic changes from intra-profile variation in oxygen and hydrogen isotopic composition of goethite and kaolinite in laterites: An integrated study from Yaou, French Guiana

    Science.gov (United States)

    Girard, Jean-Pierre; Freyssinet, Philippe; Chazot, Gilles

    2000-02-01

    An integrated study of O and H isotopes in the lateritic profile of Yaou, French Guiana, was undertaken to investigate the usefulness of stable isotopes as tracers of climatic changes in continental environments. The studied profile is composed of a 27 m thick saprolite, mostly developed in the past under wet-and-dry tropical climate in association with a duricrust, overlain by a 3 m thick yellow latosol formed more recently under present equatorial hot and humid climate. δ 18O-δD values determined for weathering goethite (pseudomorphs after pyrite) and kaolinite (microcrystalline clay groundmass) throughout the 30 m deep profile reflect formation temperatures consistent with present (25°C) and realistic past climatic temperatures (20°C-30°C), indicating that weathering minerals formed in isotopic equilibrium with their genetic environment and were not subjected to significant isotope exchange after formation. A distinct shift downward (2‰ for δ 18O, 15‰ for δD) from low to high δ 18O-δD values occurs around 20 m depth in the saprolite. It is interpreted as recording the change from the past tropical to the present equatorial climate. Goethite and kaolinite in the 5-10 m thick saprolite interval immediately above the active basement weathering front are in isotopic equilibrium with modern water and must have formed under present equatorial-humid conditions. In contrast, goethite and kaolinite found higher up in the saprolite and in the duricrust formed in the past under tropical wet and dry climate from waters distinctly depleted in 18O and D relative to modern water. The marked depletion of paleo-meteoric water at Yaou most likely reflects a more contrasted or "monsoonal" character of the ancient tropical climate. The present study shows that ancient weathering minerals in lateritic profiles preserve their δ 18O-δD values and carry a time signal. The time signal is best expressed in minerals formed rapidly at the weathering front and not subjected

  8. Support acidity influence in NiMoS (Nickel and Molybdenum) catalyst for Marlim diesel; Influencia da acidez do suport de catalisadores NiMoS (Niquel e Molibidenio) no hidrotratamento de diesel Marlim

    Energy Technology Data Exchange (ETDEWEB)

    Ferraz, Sheila Guimaraes de Almeida; Zotin, Jose Luiz; Jesus, Anderson Gomes de; Santos, Bruno Martins; Medeiros, Marcus Vinicius Costa [PETROBRAS S.A., Rio de Janeiro, RJ (Brazil). Centro de Pesquisas (CENPES)

    2008-07-01

    The specification of diesel points to the reduction of the sulfur content, of the final boiling point, of the density range and increase of the cetane number. These two last properties are directly related with the ability of the hydrotreating catalytic system in promoting the hydrogenation of aromatic structures and ring opening of the naphthenic compounds, which are both associated to low cetane number. In such way, more acidic catalysts, able to promote the cracking of naphthenic structures, should be evaluated for the diesel HDT. Three bifunctional NiMo catalysts with the same metal content, different acidity and similar active phase dispersion were prepared using alumina, silica-alumina and alumina-Y zeolite as supports. These catalysts were evaluated in a micro-reactor unit for diesel HDT aiming to correlate their activity with the support acidity. The alumina and alumina-zeolite supported catalysts presented better performance than the one supported on silica-alumina. NiMo/alumina-zeolite showed higher cetane and density improvement, associated with a slight decrease in the initial boiling point. (author)

  9. Nickel accumulation and storage in bradyrhizobium japonicum

    International Nuclear Information System (INIS)

    Maier, R.J.; Pihl, T.D.; Stults, L.; Sray, W.

    1990-01-01

    Hydrogenase-depressed (chemolithotrophic growth conditions) and heterotrophically grown cultures of Bradyrhizobium japonicum accumulated nickel about equally over a 3-h period. Both types of cultures accumulated nickel primarily in a form that was not exchangeable with NiCl 2 , and they accumulated much more Ni than would be needed for the Ni-containing hydrogenase. The nickel accumulated by heterotrophically incubated cultures could later be mobilized to allow active hydrogenase synthesis during derepression in the absence of nickel, while cells both grown with Ni and the derepressed without nickel had low hydrogenase activities. The level of activity in cells grown with Ni and then derepressed without nickel was about the same as that in cultures derepressed in the presence of nickel. The Ni accumulated by heterotrophically grown cultures was associated principally with soluble proteins rather than particulate material, and this Ni was not lost upon dialyzing an extract containing the soluble proteins against either Ni-containing or EDTA-containing buffer. However, this Ni was lost upon pronase or low pH treatments. The soluble Ni-binding proteins were partially purified by gel filtration and DEAE chromatography. They were not antigenically related to hydrogenase peptides. Much of the 63 Ni eluted as a single peak of 48 kilodaltons. Experiments involving immunuprecipitation of 63 Ni-containing hydrogenase suggested that the stored source of Ni in heterotrophic cultures that could later be mobilized into hydrogenase resided in the nonexchangeable Ni-containing fraction rather than in loosely bound or ionic forms

  10. Environmental and human toxicology of nickel - a review; Umwelt- und Humantoxikologie von Nickel - eine aktuelle Uebersicht

    Energy Technology Data Exchange (ETDEWEB)

    Beyersmann, D. [Fachbereich Biologie und Chemie, Univ. Bremen (Germany)

    2006-07-01

    Nickel is a relatively rare element, and its concentrations in ambient air, soils and waters are very low. Higher burdens of nickel are found in nickel industries and their proximity. The human uptake of nickel from the ambient air is neglectably low, except in industrial exposures. The main fraction of human nickel uptake is from food, nearly 50% stems from vegetables. Only about 2% of the oral uptake of nickel are resorbed and distributed over all organs investigated. The uptake of nickel compounds through the skin generally is very low. However, chronic skin contact with nickel and nickel compounds causes a specific contact allergy. This disease was observed after occupational exposure but also frequently in the general population. The number of new cases has dropped considerably due to reinforced prevention. Epidemiological studies with workers of nickel smelting and refining plants have demonstrated increased risks of nose and lung cancer. Human data are supported by results from animal experiments which have shown that inhalation of various nickel compounds caused lung cancer. Furthermore, animal experiments have yielded evidence that oral and inhalative exposure to nickel compounds impair reproduction. National and international agencies have classified various nickel compounds as carcinogenic to humans. The unit cancer risk attributed to life-long inhalation of 1 {mu}g Ni/m{sup 3} air is estimated to be between 2 x 10{sup -4} and 7 x 10{sup -4}. Occupational exposure limits in Germany have been the Technical Guidance Values of 0.5 mg/m{sup 3} for nickel and weakly soluble nickel compounds and of 0.05 mg/m{sup 3} for inhalable droplets of soluble nickel salts. The German limit value for ambient immission is 0.015 mg Ni/m{sup 2}. d, and for emission 0,5 mg Ni/m{sup 3}. Limit values for nickel in air are to be taken not as safe thresholds but as guidance values for the delimitation of the cancer risk. (orig.)

  11. A novel rhombohedron-like nickel ferrite nanostructure: Microwave combustion synthesis, structural characterization and magnetic properties

    Directory of Open Access Journals (Sweden)

    G. Suresh Kumar

    2016-09-01

    Full Text Available Research on nickel ferrite nanostructures has drawn a great interest because of its inherent chemical, physical and electronic properties. In this study, we have synthesized rhombohedron – like nickel ferrite nanostructure by a rapid microwave assisted combustion method using ethylenediamminetetraacetic acid as a chelating agent. X-ray diffraction, Fourier transform infrared spectrometer, transmission electron microscope and energy dispersive X-ray microanalyser were used to characterize the prepared sample. The magnetic behaviour was analysed by means of field dependent magnetization measurement which indicates that the prepared sample exhibits a soft ferromagnetic nature with saturation magnetization of 63.034 emu/g. This technique can be a potential method to synthesize novel nickel ferrite nanostructure with improved magnetic properties.

  12. Data on electrical properties of nickel modified potassium polytitanates compacted powders.

    Science.gov (United States)

    Goffman, V G; Gorokhovsky, A V; Gorshkov, N V; Fedorov, F S; Tretychenko, E V; Sevrugin, A V

    2015-09-01

    Potassium polytitanates are new promising type of ferroelectric ceramic materials with high ionic conductivity, highly polarizable structure and extremely high permittivity. Its structure is formed by [TiO6] octahedral units to layers with mobile potassium and hydroxonium ions in-between. The treatment in solutions containing nickel ions allows forming heterostructured materials which consist of potassium polytitanate particles intercalated by Ni(2+) ions and/or decorated by nickel oxides NiO x . This modification route is fully dependant on solution pH, i.e. in acidic solutions the intercalation process prevails, in alkaline solutions potassium polytitanate is mostly decorated by the oxides. Therefore, electronic structure and electrical properties can be regulated depending on modification conditions, pH and ions concentration. Here we report the data on electric properties of potassium titanate modified in nickel sulfate solutions at different pH.

  13. Data on electrical properties of nickel modified potassium polytitanates compacted powders

    Directory of Open Access Journals (Sweden)

    V.G. Goffman

    2015-09-01

    Full Text Available Potassium polytitanates are new promising type of ferroelectric ceramic materials with high ionic conductivity, highly polarizable structure and extremely high permittivity. Its structure is formed by [TiO6] octahedral units to layers with mobile potassium and hydroxonium ions in-between. The treatment in solutions containing nickel ions allows forming heterostructured materials which consist of potassium polytitanate particles intercalated by Ni2+ ions and/or decorated by nickel oxides NiOx. This modification route is fully dependant on solution pH, i.e. in acidic solutions the intercalation process prevails, in alkaline solutions potassium polytitanate is mostly decorated by the oxides. Therefore, electronic structure and electrical properties can be regulated depending on modification conditions, pH and ions concentration. Here we report the data on electric properties of potassium titanate modified in nickel sulfate solutions at different pH.

  14. Development of a Micro-Fiber Nickel Electrode for Nickel-Hydrogen Cell

    Science.gov (United States)

    Britton, Doris L.

    1996-01-01

    The development of a high specific energy battery is one of the objectives of the lightweight nickel-hydrogen (NiH2) program at the NASA Lewis Research Center. The approach has been to improve the nickel electrode by continuing combined in-house and contract efforts to develop a more efficient and lighter weight electrode for the nickel-hydrogen fuel cell. Small fiber diameter nickel plaques are used as conductive supports for the nickel hydroxide active material. These plaques are commercial products and have an advantage of increased surface area available for the deposition of active materials. Initial tests include activation and capacity measurements at different discharge levels followed by half-cell cycle testing at 80 percent depth-of-discharge in a low Earth orbit regime. The electrodes that pass the initial tests are life cycle tested in a boiler plate nickel-hydrogen cell before flightweight designs are built and tested.

  15. Nickel and titanium nanoboride composite coating

    International Nuclear Information System (INIS)

    Efimova, K A; Galevsky, G V; Rudneva, V V; Kozyrev, N A; Orshanskaya, E G

    2015-01-01

    Electrodeposition conditions, structural-physical and mechanical properties (microhardness, cohesion with a base, wear resistance, corrosion currents) of electroplated composite coatings on the base of nickel with nano and micro-powders of titanium boride are investigated. It has been found out that electro-crystallization of nickel with boride nanoparticles is the cause of coating formation with structural fragments of small sizes, low porosity and improved physical and mechanical properties. Titanium nano-boride is a component of composite coating, as well as an effective modifier of nickel matrix. Nano-boride of the electrolyte improves efficiency of the latter due to increased permissible upper limit of the cathodic current density. (paper)

  16. Clinical bending of nickel titanium wires

    Directory of Open Access Journals (Sweden)

    Stephen Chain

    2015-01-01

    Full Text Available Since the evolution and the involvement of Nickel Titanium wires in the field of Orthodontics. The treatment plan has evolved with the use of low force Nickel Titanium wires. Because of their high springback, low stiffness, they are the key initial wires in leveling and alignment but have poor formability. Since poor formability limits its ability to create variable arch forms thus; limits the form of treatment. We have devised a method to bend the Nickel Titanium wires to help in our inventory but also customized the wire according to the treatment.

  17. Determination of electroless deposition by chemical nickeling

    Directory of Open Access Journals (Sweden)

    M. Badida

    2013-07-01

    Full Text Available Increasing of technical level and reliability of machine products in compliance with the economical and ecological terms belongs to the main trends of the industrial development. During the utilisation of these products there arise their each other contacts and the interaction with the environment. That is the reason for their surface degradation by wear effect, corrosion and other influences. The chemical nickel-plating allows autocatalytic deposition of nickel from water solutions in the form of coherent, technically very profitable coating without usage of external source of electric current. The research was aimed at evaluating the surface changes after chemical nickel-plating at various changes of technological parameters.

  18. Protection of uranium by electrodeposition of nickel and diffusion

    International Nuclear Information System (INIS)

    Chauvin, G.; Coriou, H.; Hure, J.

    1959-01-01

    This work forms part of the overall scheme for investigating uranium canning for nuclear reactors. It is necessary to: - Protect the fuel (uranium) against corrosion by the cooling medium (heavy water, CO 2 , etc.), in the case of a rupture of the can; - Avoid dangerous U-Al diffusion (when it is question of an aluminium can) by using an intermediate layer of a metal whose rate of diffusion in uranium is very much less than that of aluminium under the same conditions. In the present work based on the use of an intermediate layer of nickel the following points are apparent: 1) After having treated the uranium surface it is possible to electroplate nickel on it in such a way that after annealing without the application of any pressure these deposits give a very good intermetallic U-Ni diffusion. Though this diffusion is inferior to that of the UAl system, it enables the protection to be reinforced and thus the corrosion resistance to be increased. 2) When no other factor varies, the experiments show that the quality of the diffusion zones obtained depends on the nature of the electrolytic nickel bath. 3) The classical nickel baths used previously for this type of work contain 20 to 40 g/l of boric acid acting as an electrolytic buffer. As a result of this, the deposits are highly contaminated by boron (400 to 500 ppm of boron). We shall show that with a bath which does not contain nuclear poisons, a very clean U-Ni diffusion zone can be obtained. 4) After annealing for 100 hours at 700 deg. C, microscopic examination of the diffusion front reveals the existence of five layers under bright field illumination and six Layers in polarised light: at least four of these layers are well crystallised. 5) Important irregularities in the interface between uranium and the first intermetallic compound U 6 Ni seem to be result of barriers to the diffusion caused by certain impurities in the uranium. 6) Of the seven definite compounds which can be formed during the diffusion, that

  19. Comparison of chromium and nickel uptake of plants grown in different soils

    Energy Technology Data Exchange (ETDEWEB)

    Vago, I. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary); Gyoeri, Z. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary); Loch, J. [University of Agriculture, Faculty of Agronomy, H-4015 Debrecen, P.O. Box 36 (Hungary)

    1996-03-01

    The chromium and nickel uptake of ryegrass has been examined in pot experiments in extremely different soils, poor sandy and fertile black chernozem. The effect of calcium carbonate doses and nitrogen supply on heavy metal uptake of the plant has been studied for chromium and nickel loadings (0-100 mg/kg Cr{sup 3+} or Ni{sup 2+}) applied as inorganic salts. The ability to uptake Cr{sup 3+} and Ni{sup 2+} differs significantly and is highly affected by the characteristics of soils, and depends on the metal investigated. The heavy metal uptake of the plant differs significantly in acid, colloid deficient sandy soils; while artificial chromium contamination did not modify the dry-matter production in the pots in either soil, a large quantity of nickel reduced the yields significantly. Nitrogen application did not change significantly the uptake of heavy metals. Lime application reduced the Ni{sup 2+} uptake of plants considerably, especially in sandy soil. In case of a calcium carbonate addition the dry-matter production of the plant was not affected by nickel. In chernozem soil the effect of lime application - i.e., the reduction of nickel uptake - was of a lesser degree. The significantly lesser Cr{sup 3+} uptake was further limited by a calcium carbonate application for both soils studied. A graphic presentation of these effects is given. (orig.). With 3 figs., 3 tabs.

  20. Selective Electroless Nickel Plating on PMMA using Chloroform Pre-Treatment

    Science.gov (United States)

    Sipes, Nicholas

    In the past 5 years, we have discovered that chloroform promotes the adhesion of thin gold films to Poly(methyl methacrylate) surfaces. Based on this new understanding of the interaction of chloroform with PMMA and metal atoms, we were curious to see if chloroform would promote the adhesion of Nickel to PMMA deposited by electroless plating. My goal was to selectively electroless plate Nickel onto PMMA. Chloroform was spun-cast onto 1 inch square PMMA substrates. I used electrical tape to shield one half of the PMMA from the chloroform during spin-casting; this allowed for a direct comparison of treated vs. untreated. The samples were then put through hydrochloric acid and a series of baths provided by Transene Company Inc. to electrolessly deposit nickel on the sample. After many trials, there was a clear distinction in the adhesion strength of the Nickel to the plain PMMA surface vs. the chloroform pre-treated surface. Showing that it is possible to create chloroform sites via spin-casting for electroless nickel plating on PMMA opens up the challenge to better understand the chemistry taking place and to perfect the electroless plating process.

  1. Corrosion Behaviour of Nickel Plated Low Carbon Steel in Tomato Fluid

    Directory of Open Access Journals (Sweden)

    Oluleke OLUWOLE

    2010-12-01

    Full Text Available This research work investigated the corrosion resistance of nickel plated low carbon steel in tomato fluid. It simulated the effect of continuous use of the material in a tomato environment where corrosion products are left in place. Low carbon steel samples were nickel electroplated at 4V for 20, 25, 30 and 35 mins using Watts solution.The plated samples were then subjected to tomato fluid environment for for 30 days. The electrode potentials mV (SCE were measured every day. Weight loss was determined at intervals of 5 days for the duration of the exposure period. The result showed corrosion attack on the nickel- plated steel, the severity decreasing with the increasing weight of nickel coating on substrate. The result showed that thinly plated low carbon steel generally did not have any advantage over unplated steel. The pH of the tomato solution which initially was acidic was observed to progress to neutrality after 4 days and then became alkaline at the end of the thirty days test (because of corrosion product contamination of the tomatocontributing to the reduced corrosion rates in the plated samples after 10 days. Un-plated steel was found to be unsuitable for the fabrication of tomato processing machinery without some form of surface treatment - thick nickel plating is suitable as a protective coating in this environment.

  2. Absorption and retention of nickel from drinking water in relation to food intake and nickel sensitivity.

    Science.gov (United States)

    Nielsen, G D; Søderberg, U; Jørgensen, P J; Templeton, D M; Rasmussen, S N; Andersen, K E; Grandjean, P

    1999-01-01

    Two studies were performed to examine the influence of fasting and food intake on the absorption and retention of nickel added to drinking water and to determine if nickel sensitization played any role in this regard. First, eight nonallergic male volunteers fasted overnight before being given nickel in drinking water (12 micrograms Ni/kg) and, at different time intervals, standardized 1400-kJ portions of scrambled eggs. When nickel was ingested in water 30 min or 1 h prior to the meal, peak nickel concentrations in serum occurred 1 h after the water intake, and the peak was 13-fold higher than the one seen 1 h after simultaneous intake of nickel-containing water and scrambled eggs. In the latter case, a smaller, delayed peak occurred 3 h after the meal. Median urinary nickel excretion half-times varied between 19.9 and 26.7 h. Within 3 days, the amount of nickel excreted corresponded to 2.5% of the nickel ingested when it was mixed into the scrambled eggs. Increasing amounts were excreted as the interval between the water and the meal increased, with 25.8% of the administered dose being excreted when the eggs were served 4 h prior to the nickel-containing drinking water. In the second experiment, a stable nickel isotope, 61Ni, was given in drinking water to 20 nickel-sensitized women and 20 age-matched controls, both groups having vesicular hand eczema of the pompholyx type. Nine of 20 nickel allergic eczema patients experienced aggravation of hand eczema after nickel administration, and three also developed a maculopapular exanthema. No exacerbation was seen in the control group. The course of nickel absorption and excretion in the allergic groups did not differ and was similar to the pattern seen in the first study, although the absorption in the women was less. A sex-related difference in gastric emptying rates may play a role. Thus, food intake and gastric emptying are of substantial significance for the bioavailability of nickel from aqueous solutions

  3. Recovery of vanadium, and nickel from fly ash produced from heavy oil-fired electrical power station

    International Nuclear Information System (INIS)

    Stas, J.; Dahdouh, A.; Al-Chayah, O.

    2006-05-01

    After some preliminary tests, two leaching stages of fly ash to recover vanadium, molybdenum and nickel were selected. A first stage alkaline leaching of fly ash to recover vanadium and molybdenum followed by a second stage sulfuric acid leaching of the residual ash to recover nickel. The impact of some operational parameters (L/S, leaching temperature, mixing time, and agent leaching concentrations) on the recovery of V, Ni was investigated. Conditions of precipitation of V and Mo from alkaline medium and Ni from sulfuric acid solution were established. (author)

  4. Point defects in nickel; Les defauts ponctuels dans le nickel

    Energy Technology Data Exchange (ETDEWEB)

    Peretto, P [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1969-07-01

    The defects in electron irradiated nickel (20 deg. K) or neutron irradiated nickel (28 deg. K) are studied by simultaneous analysis using the magnetic after-effect, electron microscopy and electrical resistivity recovery. We use zone refined nickel (99.999 per cent) which, for some experiments, is alloyed with a small amount of iron (for example 0.1 per cent Fe). The temperature dependant electrical recovery may be divided in four stages. The sub-stages I{sub B} (31 deg. K), I{sub C} (42 deg. K), I{sub D} (from to 57 deg. K) and I{sub E} (62 deg. K) of stage I are due to the disappearance of single interstitials into vacancies. The interstitial defect has a split configuration with a migration energy of about 0.15 eV. In the close pair which disappears in stage I{sub B} the interstitial is found to be in a 3. neighbour position whilst in stage I{sub D} it is near the <110> direction from the vacancy. In stage I{sub E} there is no longer any interaction between the interstitial and the vacancy. The stage II is due to more complicated interstitial defects: di-interstitials for stage II{sub B} (84 deg. K) and larger and larger interstitial loops for the following sub-stages. The loops may be seen by electron microscopy. Impurities can play the role of nucleation centers for the loops. Stages III{sub A} (370 deg. K) and III{sub B} (376 deg. K) are due to two types of di-vacancies. During stage IV (410 deg. K) the single vacancies migrate. Vacancy type loops and interstitial type loops grow concurrently and disappear at about 800 deg. K as observed by electron microscopy. (author) [French] Les defauts crees dans le nickel par irradiation avec des electrons a la temperature de 20 deg. K et par irradiation avec des neutrons a la temperature de 28 deg. K sont etudies par l'analyse simultanee du trainage magnetique, de la microscopie electronique et de la restauration de la resistivite electrique. Les echantillons sont en nickel, purifie par la methode de la zone fondue

  5. Point defects in nickel; Les defauts ponctuels dans le nickel

    Energy Technology Data Exchange (ETDEWEB)

    Peretto, P. [Commissariat a l' Energie Atomique, Grenoble (France). Centre d' Etudes Nucleaires

    1969-07-01

    The defects in electron irradiated nickel (20 deg. K) or neutron irradiated nickel (28 deg. K) are studied by simultaneous analysis using the magnetic after-effect, electron microscopy and electrical resistivity recovery. We use zone refined nickel (99.999 per cent) which, for some experiments, is alloyed with a small amount of iron (for example 0.1 per cent Fe). The temperature dependant electrical recovery may be divided in four stages. The sub-stages I{sub B} (31 deg. K), I{sub C} (42 deg. K), I{sub D} (from to 57 deg. K) and I{sub E} (62 deg. K) of stage I are due to the disappearance of single interstitials into vacancies. The interstitial defect has a split configuration with a migration energy of about 0.15 eV. In the close pair which disappears in stage I{sub B} the interstitial is found to be in a 3. neighbour position whilst in stage I{sub D} it is near the <110> direction from the vacancy. In stage I{sub E} there is no longer any interaction between the interstitial and the vacancy. The stage II is due to more complicated interstitial defects: di-interstitials for stage II{sub B} (84 deg. K) and larger and larger interstitial loops for the following sub-stages. The loops may be seen by electron microscopy. Impurities can play the role of nucleation centers for the loops. Stages III{sub A} (370 deg. K) and III{sub B} (376 deg. K) are due to two types of di-vacancies. During stage IV (410 deg. K) the single vacancies migrate. Vacancy type loops and interstitial type loops grow concurrently and disappear at about 800 deg. K as observed by electron microscopy. (author) [French] Les defauts crees dans le nickel par irradiation avec des electrons a la temperature de 20 deg. K et par irradiation avec des neutrons a la temperature de 28 deg. K sont etudies par l'analyse simultanee du trainage magnetique, de la microscopie electronique et de la restauration de la resistivite electrique. Les echantillons sont en nickel, purifie par la methode de la zone

  6. Nickel nanostructured materials from liquid phase photodeposition

    International Nuclear Information System (INIS)

    Giuffrida, Salvatore; Condorelli, Guglielmo G.; Costanzo, Lucia L.; Ventimiglia, Giorgio; Nigro, Raffaella Lo; Favazza, Maria; Votrico, Enrico; Bongiorno, Corrado; Fragala, Ignazio L.

    2007-01-01

    Liquid Phase Photo-Deposition (LPPD) technique has been used to obtain both colloidal particles and thin films of metallic and chloride nickel from solutions of only precursor Ni(acac) 2 (acac=2,4-pentandionato). Metallic nickel was obtained from ethanol solutions by direct nickel(II) photoreduction at 254 nm and by acetone sensitised reaction at 300 nm. In this latter process the rate was higher than in the first one. NiCl 2 was formed from CCl 4 solution by a solvent-initiated reaction. TEM analysis, performed on colloidal particles of nickel, showed that their dimensions are in the range 2-4 nm. The films did not present carbon contamination and were characterized by AFM, XPS and GIXRD. Metallic films consisted of particles of 20-40 nm that are the result of the aggregation of smaller crystallites (4-5 nm). Larger agglomerations (around 200 nm) have been observed for NiCl 2 films

  7. Annealing texture of rolled nickel alloys

    International Nuclear Information System (INIS)

    Meshchaninov, I.V.; Khayutin, S.G.

    1976-01-01

    A texture of pure nickel and binary alloys after the 95% rolling and annealing has been studied. Insoluble additives (Mg, Zr) slacken the cubic texture in nickel and neral slackening of the texture (Zr). In the case of alloying with silicium (up to 2%) the texture practically coinsides with that of a technical-grade nickel. The remaining soluble additives either do not change the texture of pure nickel (C, Nb) or enhance the sharpness and intensity of the cubic compontnt (Al, Cu, Mn, Cr, Mo, W, Co -at their content 0.5 to 2.0%). A model is proposed by which variation of the annealing texture upon alloying is caused by dissimilar effect of the alloying elements on the mobility of high- and low-angle grain boundaries

  8. A PIXE/PIGE study of lateritic gold mineralization from the regolith of the Mystery Zone, Mt Percy, Western Australia

    International Nuclear Information System (INIS)

    Li, X.; Van Moort, J.C.

    1998-01-01

    PIXE/PIGE have been utilized extensively in the search for gold and volcanic hosted massive sulphide deposits, using rock powders from relatively fresh rock. The present study uses regolith samples, from which weathering products (oxides, hydroxides, carbonates, sulphates and clay) have been removed by sequential treatment with aqua regia and sulphuric acid. The samples come from the Mystery Zone, Mt Percy, Kalgoorlie, comprising both mineralized and barren samples. The acid insoluble residue consist essentially of quartz with minor sericite. The PlXE/PIGE data from the acid insoluble residue shows that the geochemical character of W, Al, K, Ca, V, Ga, Rb, Rb/K and Rb/Al could correctly define the location of underlying mineralization at depth. The ratio of Ti/Zr remained relatively constant in different geological units and can be used to distinguish lithologies. (authors)

  9. A PIXE/PIGE study of lateritic gold mineralization from the regolith of the Mystery Zone, Mt Percy, Western Australia

    Energy Technology Data Exchange (ETDEWEB)

    Li, X.; Van Moort, J.C. [Tasmania Univ., Sandy Bay, TAS (Australia). Dept. of Geology

    1998-06-01

    PIXE/PIGE have been utilized extensively in the search for gold and volcanic hosted massive sulphide deposits, using rock powders from relatively fresh rock. The present study uses regolith samples, from which weathering products (oxides, hydroxides, carbonates, sulphates and clay) have been removed by sequential treatment with aqua regia and sulphuric acid. The samples come from the Mystery Zone, Mt Percy, Kalgoorlie, comprising both mineralized and barren samples. The acid insoluble residue consist essentially of quartz with minor sericite. The PlXE/PIGE data from the acid insoluble residue shows that the geochemical character of W, Al, K, Ca, V, Ga, Rb, Rb/K and Rb/Al could correctly define the location of underlying mineralization at depth. The ratio of Ti/Zr remained relatively constant in different geological units and can be used to distinguish lithologies. (authors). Extended abstract. 5 refs.

  10. A review of nickel hydrogen battery technology

    Energy Technology Data Exchange (ETDEWEB)

    Smithrick, J.J.; O`Donnell, P.M. [NASA Lewis Research Center, Cleveland, OH (United States)

    1995-12-31

    This paper on nickel hydrogen batteries is an overview of the various nickel hydrogen battery design options, technical accomplishments, validation test results and trends. There is more than one nickel hydrogen battery design, each having its advantage for specific applications. The major battery designs are individual pressure vessel (IPV), common pressure vessel (CPV), bipolar and low pressure metal hydride. State-of-the-art (SOA) nickel hydrogen batteries are replacing nickel cadmium batteries in almost all geosynchronous orbit (GEO) applications requiring power above 1 kW. However, for the more severe low earth orbit (LEO) applications (>30,000 cycles), the current cycle life of 4,000 to 10,000 cycles at 60 percent DOD should be improved. A NASA Lewis Research Center innovative advanced design IPV nickel hydrogen cell led to a breakthrough in cycle life enabling LEO applications at deep depths of discharge (DOD). A trend for some future satellites is to increase the power level to greater than 6 kW. Another trend is to decrease the power to less than 1 kW for small low cost satellites. Hence, the challenge is to reduce battery mass, volume and cost. A key is to develop a light weight nickel electrode and alternate battery designs. A common pressure vessel (CPV) nickel hydrogen battery is emerging as a viable alternative to the IPV design. It has the advantage of reduced mass, volume and manufacturing costs. A 10 Ah CPV battery has successfully provided power on the relatively short lived Clementine Spacecraft.

  11. Development of nickel hydrogen battery expert system

    Science.gov (United States)

    Shiva, Sajjan G.

    1990-01-01

    The Hubble Telescope Battery Testbed employs the nickel-cadmium battery expert system (NICBES-2) which supports the evaluation of performances of Hubble Telescope spacecraft batteries and provides alarm diagnosis and action advice. NICBES-2 also provides a reasoning system along with a battery domain knowledge base to achieve this battery health management function. An effort to modify NICBES-2 to accommodate nickel-hydrogen battery environment in testbed is described.

  12. Study on Corrosion of Materials by Fluoric Acid and Silicofluoric Acid

    International Nuclear Information System (INIS)

    Park, Kun You; Kwon, Yeong Soo; Kuk, Myung Ho; Kim, Myun Sup

    1986-01-01

    The corrosion properties of 304 Stainless steel, Cupro-nickel, NiCrMo alloy in hydrofluoric acid and silicofluoric acid has been studied. The corrosion resistance of NiCrMo alloy and Cupro-nickel in hydrofluoric acid or mixed acid of hydrofluoric and sulfuric acid is excellent. Because of lower corrosion resistance of 304 Stainless steel, it would not be used for these corrosion resistant materials. The corrosion activation energy of 304 Stainless steel, Cupro-nickel and NiCrMo alloy in 40% HF solution are 42.7, 58.9 and 89.7 kJ/mol, respectively. By these values, it is assumed that the corrosion rate determining step is the chemical reaction on surface of metals. In the plastics, Teflon and polychloro tetrafluoroethylene are most excellent for corrosion resistance in hydrofluoric acid

  13. Phytoremediation of mixed-contaminated soil using the hyperaccumulator plant Alyssum lesbiacum: Evidence of histidine as a measure of phytoextractable nickel

    International Nuclear Information System (INIS)

    Singer, Andrew C.; Bell, Thomas; Heywood, Chloe A.; Smith, J.A.C.; Thompson, Ian P.

    2007-01-01

    In this study we examine the effects of polycyclic aromatic hydrocarbons (PAHs) on the ability of the hyperaccumulator plant Alyssum lesbiacum to phytoextract nickel from co-contaminated soil. Planted and unplanted mesocosms containing the contaminated soils were repeatedly amended with sorbitan trioleate, salicylic acid and histidine in various combinations to enhance the degradation of two PAHs (phenanthrene and chrysene) and increase nickel phytoextraction. Plant growth was negatively affected by PAHs; however, there was no significant effect on the phytoextraction of Ni per unit biomass of shoot. Exogenous histidine did not increase nickel phytoextraction, but the histidine-extractable fraction of soil nickel showed a high correlation with phytoextractable nickel. These results indicate that Alyssum lesbiacum might be effective in phytoextracting nickel from marginally PAH-contaminated soils. In addition, we provide evidence for the broader applicability of histidine for quantifying and predicting Ni phytoavailability in soils. - Alyssum lesbiacum was shown to phytoextract nickel from PAH-contaminated soils from which the pool of nickel accessed for phytoextraction is closely modelled by a histidine-soil extract

  14. Phytoremediation of mixed-contaminated soil using the hyperaccumulator plant Alyssum lesbiacum: Evidence of histidine as a measure of phytoextractable nickel

    Energy Technology Data Exchange (ETDEWEB)

    Singer, Andrew C. [Centre for Ecology and Hydrology-Oxford, Mansfield Road, Oxford OX1 3SR (United Kingdom)]. E-mail: acsi@ceh.ac.uk; Bell, Thomas [Department of Zoology, University of Oxford, South Parks Road, Oxford OX1 3PS (United Kingdom); Heywood, Chloe A. [Centre for Ecology and Hydrology-Oxford, Mansfield Road, Oxford OX1 3SR (United Kingdom); Smith, J.A.C. [Department of Plant Sciences, University of Oxford, South Parks Road, Oxford OX1 3RB (United Kingdom); Thompson, Ian P. [Centre for Ecology and Hydrology-Oxford, Mansfield Road, Oxford OX1 3SR (United Kingdom)

    2007-05-15

    In this study we examine the effects of polycyclic aromatic hydrocarbons (PAHs) on the ability of the hyperaccumulator plant Alyssum lesbiacum to phytoextract nickel from co-contaminated soil. Planted and unplanted mesocosms containing the contaminated soils were repeatedly amended with sorbitan trioleate, salicylic acid and histidine in various combinations to enhance the degradation of two PAHs (phenanthrene and chrysene) and increase nickel phytoextraction. Plant growth was negatively affected by PAHs; however, there was no significant effect on the phytoextraction of Ni per unit biomass of shoot. Exogenous histidine did not increase nickel phytoextraction, but the histidine-extractable fraction of soil nickel showed a high correlation with phytoextractable nickel. These results indicate that Alyssum lesbiacum might be effective in phytoextracting nickel from marginally PAH-contaminated soils. In addition, we provide evidence for the broader applicability of histidine for quantifying and predicting Ni phytoavailability in soils. - Alyssum lesbiacum was shown to phytoextract nickel from PAH-contaminated soils from which the pool of nickel accessed for phytoextraction is closely modelled by a histidine-soil extract.

  15. Nickel acts as an adjuvant during cobalt sensitization

    DEFF Research Database (Denmark)

    Bonefeld, Charlotte Menne; Nielsen, Morten Milek; Vennegaard, Marie T.

    2015-01-01

    Metal allergy is the most frequent form of contact allergy with nickel and cobalt being the main culprits. Typically, exposure comes from metal-alloys where nickel and cobalt co-exist. Importantly, very little is known about how co-exposure to nickel and cobalt affects the immune system. We...... investigated these effects by using a recently developed mouse model. Mice were epicutaneously sensitized with i) nickel alone, ii) nickel in the presence of cobalt, iii) cobalt alone, or iv) cobalt in the presence of nickel, and then followed by challenge with either nickel or cobalt alone. We found...... that sensitization with nickel alone induced more local inflammation than cobalt alone as measured by increased ear-swelling. Furthermore, the presence of nickel during sensitization to cobalt led to a stronger challenge response to cobalt as seen by increased ear-swelling and increased B and T cell responses...

  16. Effects of repeated skin exposure to low nickel concentrations

    DEFF Research Database (Denmark)

    Nielsen, N H; Menné, T; Kristiansen, J

    1999-01-01

    and nickel allergy, either on normal or on SLS-treated forearm skin. The present study strongly suggests that the changes observed were specific to nickel exposure. Standardized methods to assess trace to moderate nickel exposure on the hands, and the associated effects in nickel-sensitized subjects......We studied the effects of repeated daily exposure to low nickel concentrations on the hands of patients with hand eczema and nickel allergy. The concentrations used were chosen to represent the range of trace to moderate occupational nickel exposure. The study was double-blinded and placebo...... controlled. Patients immersed a finger for 10 min daily into a 10-p.p.m. nickel concentration in water for the first week, and during the second week into a 100-p.p.m. nickel concentration. This regimen significantly increased (P = 0.05) local vesicle formation and blood flow (P = 0.03) as compared...

  17. Simulations on Nickel target preparation and separation of Ni(II)-Cu(II) matrix for production of radioisotope "6"4Cu

    International Nuclear Information System (INIS)

    Sunarhadijoso Soenarjo; Wira Y Rahman; Sriyono; Triyanto

    2011-01-01

    The simulations on Nickel target preparation and separation of Ni(II)-Cu(II) matrix has been carried out as a preliminary study for production of medical radioisotope Cu-64 based on nuclear reaction of "6"4Ni (p,n) "6"4Cu. The nickel target preparation was performed by means of electroplating method using acidic solution of nickel chloride - boric acid mixture and basic solution of nickel sulphate - nickel chloride mixture on a silver - surfaced-target holder. The simulated solution of Ni(II) - Cu(II) matrix was considered as the solution of post-proton-irradiated nickel target containing both irradiated nickel and radioactive copper, but in the presented work the proton irradiation of nickel target was omitted, while the radioactive copper was originally obtained from neutron irradiation of CuO target. The separation of radioactive copper from the nickel target matrix was based on anion exchange column chromatography in which the radiocopper was conditioned to form anion complex CuCl_4"2"- and retained on the column while the nickel was kept in the form of Ni"2"+ cation and eluted off from the column. The retained radioactive copper was then eluted out the column in the condition of dilute HCl changing back the copper anion complex into Cu"2"+ cation. It was found that the electroplating result from the acidic solution was more satisfied than that from the basic solution. By conditioning the matrix solution at HCl 6 M, the radioactive copper was found in the forms of Cu"2"+ and CuCl_4"2"- while the nickel was totally in the form of Ni"2"+. In the condition of HCl 9 M, the radioactive copper was mostly in the form of CuCl_4"2"- while the nickel was found as both Ni"2"+ and NiCl_4"2"-. The best condition of separation was in HCl 8 M in which the radioactive copper was mostly in the form of CuCl_4"2"- while the nickel was mostly in the form of Ni"2"+. The retained CuCl_4"2"- was then changed back into Cu_2_+ cation form and eluted out the column by using HCl 0.05 M

  18. Corrigendum to “Comparing activated alumina with indigenous laterite and bauxite as potential sorbents for removing fluoride from drinking water in Ghana” [Appl. Geochem. 56 (2015) 50–66

    Science.gov (United States)

    Craig, Laura; Stillings, Lisa; Decker, David L.; Thomas, James M.

    2015-01-01

    The authors regret that the application of the t-plot to determine the presence of micropores in the three sorbents needs the following corrections: (1) Fig. 1a, c, e are N2(g) adsorption and desorption isotherms” (remove “BET”). This correction applies to descriptions in the text as well. (2) Table 2, the column titled “Micropores” is mislabelled, and should be labelled “Film thickness”, which may not equal the pore width. The column titled “Micropore volume” is a correct description for laterite volume 0.0022 cm3 g−1 (t = 0.3–0.5 nm), but the other pore volumes listed cannot be identified as corresponding to micropores. They likely comprise both micropores and mesopores in laterite, while the presence of micropores in activated alumina is not clear. The positive y-intercept for the lowest linear portion of the laterite t-plot curve indicates micropores (Fig. 1f), and the shape of the t-plot curve suggests the presence of both micropores and mesopores. The shape of the activated alumina t-plot curve suggests the presence of micropores and mesopores, but the zero intercept for the lowest linear portion of the curve (Fig. 1b) creates uncertainty regarding the presence of micropores. Also see Storck et al., 1998; Hay et al. 2011 and references therein. (Additional note: analytical instrument Micromeritics® was misspelled as “Micrometrics”).The authors would like to apologise for any inconvenience caused.

  19. Corrosion properties of plasma deposited nickel and nickel-based alloys

    Czech Academy of Sciences Publication Activity Database

    Voleník, Karel; Pražák, M.; Kalabisová, E.; Kreislová, K.; Had, J.; Neufuss, Karel

    2003-01-01

    Roč. 48, č. 3 (2003), s. 215-226 ISSN 0001-7043 R&D Projects: GA ČR GA106/99/0298 Institutional research plan: CEZ:AV0Z2043910 Keywords : plasma deposits, nickel, nickel-based alloys Subject RIV: JK - Corrosion ; Surface Treatment of Materials

  20. Synthesis of Nickel and Nickel Hydroxide Nanopowders by Simplified Chemical Reduction

    Directory of Open Access Journals (Sweden)

    Jeerapan Tientong

    2014-01-01

    Full Text Available Nickel nanopowders were synthesized by a chemical reduction of nickel ions with hydrazine hydrate at pH ~12.5. Sonication of the solutions created a temperature of 54–65°C to activate the reduction reaction of nickel nanoparticles. The solution pH affected the composition of the resulting nanoparticles. Nickel hydroxide nanoparticles were formed from an alkaline solution (pH~10 of nickel-hydrazine complexed by dropwise titration. X-ray diffraction of the powder and the analysis of the resulting Williamson-Hall plots revealed that the particle size of the powders ranged from 12 to 14 nm. Addition of polyvinylpyrrolidone into the synthesis decreased the nickel nanoparticle size to approximately 7 nm. Dynamic light scattering and scanning electron microscopy confirmed that the particles were in the nanometer range. The structure of the synthesized nickel and nickel hydroxide nanoparticles was identified by X-ray diffraction and Fourier transform infrared spectroscopy.

  1. Performance improvement of pasted nickel electrodes with multi-wall carbon nanotubes for rechargeable nickel batteries

    International Nuclear Information System (INIS)

    Song, Q.S.; Aravindaraj, G.K.; Sultana, H.; Chan, S.L.I.

    2007-01-01

    Carbon nanotubes (CNTs) were employed as a functional additive to improve the electrochemical performance of pasted nickel-foam electrodes for rechargeable nickel-based batteries. The nickel electrodes were prepared with spherical β-Ni(OH) 2 powder as the active material and various amounts of CNTs as additives. Galvanostatic charge/discharge cycling tests showed that in comparison with the electrode without CNTs, the pasted nickel electrode with added CNTs exhibited better electrochemical properties in the chargeability, specific discharge capacity, active material utilization, discharge voltage, high-rate capability and cycling stability. Meanwhile, the CNT addition also lowered the packing density of Ni(OH) 2 particles in the three-dimensional porous nickel-foam substrate, which could lead to the decrease in the active material loading and discharge capacity of the electrode. Hence, the amount of CNTs added to Ni(OH) 2 should be optimized to obtain a high-performance nickel electrode, and an optimum amount of CNT addition was found to be 3 wt.%. The superior electrochemical performance of the nickel electrode with CNTs could be attributed to lower electrochemical impedance and less γ-NiOOH formed during charge/discharge cycling, as indicated by electrochemical impedance spectroscopy and X-ray diffraction analyses. Thus, it was an effective method to improve the electrochemical properties of pasted nickel electrodes by adding an appropriate amount of CNTs to spherical Ni(OH) 2 as the active material

  2. Absorption and retention of nickel from drinking water in relation to food intake and nickel sensitivity

    DEFF Research Database (Denmark)

    Nielsen, G D; Søderberg, U; Jørgensen, Poul Jørgen

    1999-01-01

    nickel in drinking water (12 micrograms Ni/kg) and, at different time intervals, standardized 1400-kJ portions of scrambled eggs. When nickel was ingested in water 30 min or 1 h prior to the meal, peak nickel concentrations in serum occurred 1 h after the water intake, and the peak was 13-fold higher...... than the one seen 1 h after simultaneous intake of nickel-containing water and scrambled eggs. In the latter case, a smaller, delayed peak occurred 3 h after the meal. Median urinary nickel excretion half-times varied between 19.9 and 26.7 h. Within 3 days, the amount of nickel excreted corresponded...... to 2.5% of the nickel ingested when it was mixed into the scrambled eggs. Increasing amounts were excreted as the interval between the water and the meal increased, with 25.8% of the administered dose being excreted when the eggs were served 4 h prior to the nickel-containing drinking water...

  3. AN ELECTROPLATING METHOD OF FORMING PLATINGS OF NICKEL, COBALT, NICKEL ALLOYS OR COBALT ALLOYS

    DEFF Research Database (Denmark)

    1997-01-01

    An electroplating method of forming platings of nickel, cobalt, nickel alloys or cobalt alloys with reduced stresses in an electrodepositing bath of the type: Watt's bath, chloride bath or a combination thereof, by employing pulse plating with periodic reverse pulse and a sulfonated naphthalene...

  4. Repeated patch testing to nickel during childhood do not induce nickel sensitization

    DEFF Research Database (Denmark)

    Søgaard Christiansen, Elisabeth

    2014-01-01

    Background: Previously, patch test reactivity to nickel sulphate in a cohort of unselected infants tested repeatedly at 3-72 months of age has been reported. A reproducible positive reaction at 12 and 18 months was selected as a sign of nickel sensitivity, provided a patch test with an empty Finn...

  5. Exposure of nickel and the relevance of nickel sensitivity among hospital cleaners

    Energy Technology Data Exchange (ETDEWEB)

    Clemmensen, O J; Menne, T; Kaaber, K; Solgaard, P

    1981-01-01

    The nickel content of water specimens from consecutive stages during the cleaning process in a Danish hospital was analyzed. Statistically significant increases of the nickel concentrations were found from step to step of the cleaning, eventually exceeding the theoretical sensitizing safety limit. The relevance of the findings in relation to hand eczema is discussed.

  6. Different Dimensional and Structural Variations in Coordination Compounds of Cadmium, Manganese and Nickel Constructed from the Ligand 2,2'-Bipyidine-3,3',6,6'-tetracarboxylic Acid (H{sub 4}bptc)

    Energy Technology Data Exchange (ETDEWEB)

    Xiang, Jing; Yang, Tiantian; Fu, Lulu; Luo, Ya; Wu, Jiashou [Yangtze Univ., Jingzhou (China)

    2013-09-15

    The reactions of hydrated CdCl{sub 2}, MnCl{sub 2}, and NiCl{sub 2} with 2,2'-bipyidine-3,3',6,6'-tetracarboxylic acid (H{sub 4}bptc) afforded the mononuclear [Cd{sup II}(H{sub 2}bptc)(H{sub 2}O){sub 3}]·H{sub 2}O (1), linear [Cd(H{sub 2}bptc)(H{sub 2}O)]·3H{sub 2}O{sub n} (2), 3-D hetero-bimetallic [NaCd(Hbptc)(H{sub 2}O)] (3), layer [Mn(H{sub 2}bptc)(H{sub 2}O)]n (4) and a dinuclear compound [Ni{sub 2}(H{sub 2}bptc)-(H{sub 2}O){sub 2}]·6H{sub 2}O (5). These compounds have been characterized by elemental analysis, IR, and their structures have been determined by X-ray crystallography. The thermal stabilities of 1-3 were measured by thermogravimetric analysis (TGA) and their solid state luminescence properties together with the free ligand H{sub 4}bptc were investigated at room temperature.

  7. A review of nickel hydrogen battery technology

    Science.gov (United States)

    Smithrick, John J.; Odonnell, Patricia M.

    1995-01-01

    This paper on nickel hydrogen batteries is an overview of the various nickel hydrogen battery design options, technical accomplishments, validation test results and trends. There is more than one nickel hydrogen battery design, each having its advantage for specific applications. The major battery designs are individual pressure vessel (IPV), common pressure vessel (CPV), bipolar and low pressure metal hydride. State-of-the-art (SOA) nickel hydrogen batteries are replacing nickel cadmium batteries in almost all geosynchronous orbit (GEO) applications requiring power above 1 kW. However, for the more severe low earth orbit (LEO) applications (greater than 30,000 cycles), the current cycle life of 4000 to 10,000 cycles at 60 percent DOD should be improved. A NASA Lewis Research Center innovative advanced design IPV nickel hydrogen cell led to a breakthrough in cycle life enabling LEO applications at deep depths of discharge (DOD). A trend for some future satellites is to increase the power level to greater than 6 kW. Another trend is to decrease the power to less than 1 kW for small low cost satellites. Hence, the challenge is to reduce battery mass, volume and cost. A key is to develop a light weight nickel electrode and alternate battery designs. A common pressure vessel (CPV) nickel hydrogen battery is emerging as a viable alternative to the IPV design. It has the advantage of reduced mass, volume and manufacturing costs. A 10 Ah CPV battery has successfully provided power on the relatively short lived Clementine Spacecraft. A bipolar nickel hydrogen battery design has been demonstrated (15,000 LEO cycles, 40 percent DOD). The advantage is also a significant reduction in volume, a modest reduction in mass, and like most bipolar designs, features a high pulse power capability. A low pressure aerospace nickel metal hydride battery cell has been developed and is on the market. It is a prismatic design which has the advantage of a significant reduction in volume and a

  8. Synthesis and electrochemical characterization of stabilized nickel nanoparticles

    Energy Technology Data Exchange (ETDEWEB)

    Dominguez-Crespo, M.A.; Ramirez-Meneses, E.; Torres Huerta, A.M. [Centro de Investigacion en Ciencia Aplicada y Tecnologia Avanzada, CICATA-IPN Unidad Altamira, Carretera Tampico-Puerto Industrial, C.P. 89600 Altamira, Tamaulipas (Mexico); Montiel-Palma, V. [Centro de Investigaciones Quimicas, Universidad Autonoma del Estado de Morelos, Av. Universidad 1001, Colonia Chamilpa, C.P.62201 Cuernavaca, Morelos (Mexico); Dorantes Rosales, H. [Departamento de Metalurgia, Escuela Superior de Ingenieria Quimica e Industrias Extractivas - IPN, C.P. 07300, D.F. (Mexico)

    2009-02-15

    Nickel stabilized nanoparticles produced by an organometallic approach (Chaudret's method) starting from the complex Ni(1,5-COD){sub 2} were used as electrode materials for hydrogen evolution in NaOH at two temperatures (298 and 323 K). The synthesis of the nickel nanoparticles was performed in the presence of two different stabilizers, 1,3-diaminopropane (DAP) and anthranilic acid (AA), by varying the molar ratios (1:1, 1:2 and 1:5 metal:ligand) in order to evaluate their influence on the shape, dispersion, size and electrocatalytic activity of the metallic particles. The presence of an appropriate amount of stabilizer is an effective alternative to the synthesis of small monodispersed metal nanoparticles with diameters around 5 and 8 nm for DAP and AA, respectively. The results are discussed in terms of morphology and the surface state of the nanoparticles. The importance of developing a well-controlled synthetic method which results in higher performances of the resulting nanoparticles is highlighted. Herein we found that the performance with respect to the HER of the Ni electrodes dispersed on a carbon black Vulcan substrate is active and comparable to that reported in the literature for the state-of-the-art electrocatalysts. Appreciable cathodic current densities of {proportional_to}240 mA cm{sup -2} were measured with highly dispersed nickel particles (Ni-5{sub DAP}). This work demonstrates that the aforementioned method can be extended to the preparation of highly active stabilized metal particles without inhibiting the electron transfer for the HER reaction, and it could also be applied to the synthesis of bimetallic nanoparticles. (author)

  9. Nickel allergy from adolescence to adulthood in the TOACS cohort

    DEFF Research Database (Denmark)

    Mortz, Charlotte G; Bindslev-Jensen, Carsten; Andersen, Klaus Ejner

    2013-01-01

    Background In 1995, we established a cohort of 1501 unselected eighth-grade schoolchildren to investigate the course of nickel allergy into adult life. Objectives To follow the course of nickel allergy and clinically relevant nickel dermatitis over 15 years from adolescence to adulthood, and the ......Background In 1995, we established a cohort of 1501 unselected eighth-grade schoolchildren to investigate the course of nickel allergy into adult life. Objectives To follow the course of nickel allergy and clinically relevant nickel dermatitis over 15 years from adolescence to adulthood...

  10. Mua (HP0868) Is a Nickel-Binding Protein That Modulates Urease Activity in Helicobacter pylori

    Science.gov (United States)

    Benoit, Stéphane L.; Maier, Robert J.

    2011-01-01

    A novel mechanism aimed at controlling urease expression in Helicobacter pylori in the presence of ample nickel is described. Higher urease activities were observed in an hp0868 mutant (than in the wild type) in cells supplemented with nickel, suggesting that the HP0868 protein (herein named Mua for modulator of urease activity) represses urease activity when nickel concentrations are ample. The increase in urease activity in the Δmua mutant was linked to an increase in urease transcription and synthesis, as shown by quantitative real-time PCR, SDS-PAGE, and immunoblotting against UreAB. Increased urease synthesis was also detected in a Δmua ΔnikR double mutant strain. The Δmua mutant was more sensitive to nickel toxicity but more resistant to acid challenge than was the wild-type strain. Pure Mua protein binds 2 moles of Ni2+ per mole of dimer. Electrophoretic mobility shift assays did not reveal any binding of Mua to the ureA promoter or other selected promoters (nikR, arsRS, 5′ ureB-sRNAp). Previous yeast two-hybrid studies indicated that Mua and RpoD may interact; however, only a weak interaction was detected via cross-linking with pure components and this could not be verified by another approach. There was no significant difference in the intracellular nickel level between wild-type and mua mutant cells. Taken together, our results suggest the HP0868 gene product represses urease transcription when nickel levels are high through an as-yet-uncharacterized mechanism, thus counterbalancing the well-described NikR-mediated activation. PMID:21505055

  11. The effect of current density and saccharin addition on the grain size of nickel coatings

    Energy Technology Data Exchange (ETDEWEB)

    Uhm, Young Rang; Park, Keun Yung; Son, Kwang Jae; Shim, Young Ho; Choi, Sun Ju [KAERI, Daejeon (Korea, Republic of)

    2012-10-15

    Recently, the main advantage of a radioisotope 'fuel' is concentrated, because it is 'burned' at the rate of the isotopes half life. In other words, given a half life of 100 years, a nuclear battery would still produce half of its initial starting power after 100 years. A speck of a radioisotope like nickel 63, for example, contains enough energy to power a nano nuclear battery for decades, and to do so safely. Ni 63, a beta radiation source, is prepared by electrical deposition of radioactive Ni 63 ions on thin non radioactive nickel foil. Ni 63 plating is similar to other electroplating processes that employ soluble metal anodes. It requires the passage of a direct current between two electrodes that are immersed in a conductive, aqueous solution of nickel salts. The charged Ni ions are formed by sulfate, sulfamate, chloride, and a Watts bath. However, the charged Ni 63 ions are formed by dissolving metal Ni 63. To establish the coating condition of Ni 63, non radioactive metal Ni particles were dissolved in an acid solution and electroplated on the Ni sheet. A continuous increase in the grain size versus current density has also been recognized in the direct current electrodeposition of nickel coating. On the other hand, A runa et al. reported that the current density has no significant effect on the grain size of nickel electro deposits. A review of the literature shows that saccharin has often been added to a nickel plating bath since the 1980s to improve the ductility and brightness, and in later periods as a grain refiner agent. In the present paper, not only the preparation of the Ni plating solution prepared by dissolving metal particles but also an optimization of the deposition conditions, such as the influence of current density and saccharin concentration on the grain size, was investigated. The proposed model can also be applied for radioactive Ni 63 electroplating.

  12. The effect of current density and saccharin addition on the grain size of nickel coatings

    International Nuclear Information System (INIS)

    Uhm, Young Rang; Park, Keun Yung; Son, Kwang Jae; Shim, Young Ho; Choi, Sun Ju

    2012-01-01

    Recently, the main advantage of a radioisotope 'fuel' is concentrated, because it is 'burned' at the rate of the isotopes half life. In other words, given a half life of 100 years, a nuclear battery would still produce half of its initial starting power after 100 years. A speck of a radioisotope like nickel 63, for example, contains enough energy to power a nano nuclear battery for decades, and to do so safely. Ni 63, a beta radiation source, is prepared by electrical deposition of radioactive Ni 63 ions on thin non radioactive nickel foil. Ni 63 plating is similar to other electroplating processes that employ soluble metal anodes. It requires the passage of a direct current between two electrodes that are immersed in a conductive, aqueous solution of nickel salts. The charged Ni ions are formed by sulfate, sulfamate, chloride, and a Watts bath. However, the charged Ni 63 ions are formed by dissolving metal Ni 63. To establish the coating condition of Ni 63, non radioactive metal Ni particles were dissolved in an acid solution and electroplated on the Ni sheet. A continuous increase in the grain size versus current density has also been recognized in the direct current electrodeposition of nickel coating. On the other hand, A runa et al. reported that the current density has no significant effect on the grain size of nickel electro deposits. A review of the literature shows that saccharin has often been added to a nickel plating bath since the 1980s to improve the ductility and brightness, and in later periods as a grain refiner agent. In the present paper, not only the preparation of the Ni plating solution prepared by dissolving metal particles but also an optimization of the deposition conditions, such as the influence of current density and saccharin concentration on the grain size, was investigated. The proposed model can also be applied for radioactive Ni 63 electroplating

  13. [Effects of slopes on nitrogen transport along with runoff from sloping plots on a lateritic red soil amended with sewage sludge].

    Science.gov (United States)

    Chen, Yan-Hui; Chen, Ming-Hua; Wang, Guo; Chen, Wen-Xiang; Yang, Shun-Cheng; Chai, Peng

    2010-10-01

    The effects of different slopes on nitrogen transport along with runoff from sloping plots amended with sewage sludge on a lateritic red soil were studied under simulated rainfall conditions. When the sludge was broadcasted and mixed with surface soils (BM), the MTN (total nitrogen of mixing sample), STN (total nitrogen of settled sample), TPN (total particulate nitrogen), TSN (total suspended nitrogen), TDN (total dissolved nitrogen) and NH4(+) -N concentrations and nitrogen loss amounts in runoff of all treatments were highest at 1 day or 18 days after application. The highest concentrations and the loss amounts of MTN and STN in the slope runoff for the BM treatment increased with slope degree, showing increasing pollution risks to the surface waters. The STN concentration and loss amounts from the 25 degrees plots were 126.1 mg x L(-1) and 1788.6 mg x m(-2), respectively, being 4.6 times and 5.8 times of the corresponding values from the 10 degrees plots, respectively. Then the concentrations and the loss amounts of nitrogen (except NO3(-) -N) from the BM plots diminished rapidly first and then tended to be stable with dwindling differences between the slopes. The loss of MTN and STN in early runoff (1 day and 18 days) accounted for 68.6% -73.4% and 62.3% -66.7% of the cumulative loss amounts during the experimental period for all the broadcasted treatments. Runoff loss coefficients of MTN increased in the order of 20 degrees > 25 degrees > 15 degrees > 10 degrees. Nitrogen was largely lost in dissolved species while large portion of NH4(+) -N was lost with particulates.

  14. Nickel release from inexpensive jewelry and hair clasps purchased in an EU country - Are consumers sufficiently protected from nickel exposure?

    DEFF Research Database (Denmark)

    Thyssen, Jacob Pontoppidan; Menné, Torkil; Johansen, Jeanne Duus

    2009-01-01

    BACKGROUND: Nickel allergic subjects are at risk factor of acquiring hand eczema. In 1990 and 1994, respectively, Denmark and member states in the EU regulated nickel release from selected consumer products. The intention was that the nickel epidemic could be controlled and prevented if the general...... population was protected from high cutaneous nickel concentrations. Despite a decrease, the prevalence of nickel allergy remains high as nearly 10% of young women are nickel allergic. OBJECTIVE: This study aimed to perform dimethylglyoxime (DMG) testing of inexpensive jewelry and hair clasps purchased from...

  15. Nickel exposure from keys: alternatives for protection and prevention.

    Science.gov (United States)

    Hamann, Dathan; Scheman, Andrew J; Jacob, Sharon E

    2013-01-01

    Keys are an important exposure source of metal allergens to consumers and confer a significant problem for nickel-allergic individuals because of repeated daily use. The aims of this study were to investigate the frequency of nickel and cobalt release in keys and to consider the effectiveness of coatings for preventing metallic allergen release from common metal allergen-releasing keys. Keys from a variety of common stores were nickel and cobalt spot tested. Nickel-releasing keys were coated with enamel sprays, subjected to a use test, and retested to assess for metal allergen release. Of 55 tested keys, 80% showed a strong positive result to the nickel spot test. None of the tested keys exhibited cobalt release. No keys initially released nickel after enamel coatings. Key coatings chipped at the portion inserted into a lock after 30 insertions, and keys were found to release nickel. The handle of the key was not found to release nickel after 60 insertions. Nickel release from keys is very common; nickel-allergic consumers should consider purchasing keys that do not release nickel (eg, brass, anodized). Enamel coating may be useful in protecting nickel-sensitive individuals from their keys but cannot consistently prevent nickel-release from portions used frequently.

  16. Three-dimensional hybrid networks based on aspartic acid

    Indian Academy of Sciences (India)

    WINTEC

    Keywords. Aspartic acid; hybrid compounds; nickel aspartate; lead aspartate; achiral frameworks. ..... and coordinated to water molecules as well as car- .... (b) Dan M 2004 J. Mol. Struct. ... Sheldrick G M 1994 SADABS: Siemens area detector.

  17. Synthesis and Characterization of Nanostructured Nickel Diselenide NiSe2 from the Decomposition of Nickel Acetate, (CH3CO2)2Ni

    OpenAIRE

    Yin, Ming; O’Brien, Stephen

    2014-01-01

    Solution processed NiSe2 nanorods were synthesized by a modified colloidal synthesis technique, by chemical reaction of TOPSe and nickel acetate at 150°C. The rods exist as an oleic acid ligand stabilized solution, with oleic acid acting as a capping group. Structural characterization by X-ray diffraction and transmission electron microscopy indicates that the particles are rod-like shaped crystals with a high and relatively constant aspect ratio (30 : 1). TEM shows that the width and the len...

  18. Cobalt release from inexpensive jewellery: has the use of cobalt replaced nickel following regulatory intervention?

    DEFF Research Database (Denmark)

    Thyssen, Jacob Pontoppidan; Jellesen, Morten S; Menné, Torkil

    2010-01-01

    Before the introduction of the EU Nickel Directive, concern was raised that manufacturers of jewellery might turn from the use of nickel to cobalt following the regulatory intervention on nickel exposure.......Before the introduction of the EU Nickel Directive, concern was raised that manufacturers of jewellery might turn from the use of nickel to cobalt following the regulatory intervention on nickel exposure....

  19. Methods to Quantify Nickel in Soils and Plant Tissues

    Directory of Open Access Journals (Sweden)

    Bruna Wurr Rodak

    2015-06-01

    Full Text Available In comparison with other micronutrients, the levels of nickel (Ni available in soils and plant tissues are very low, making quantification very difficult. The objective of this paper is to present optimized determination methods of Ni availability in soils by extractants and total content in plant tissues for routine commercial laboratory analyses. Samples of natural and agricultural soils were processed and analyzed by Mehlich-1 extraction and by DTPA. To quantify Ni in the plant tissues, samples were digested with nitric acid in a closed system in a microwave oven. The measurement was performed by inductively coupled plasma/optical emission spectrometry (ICP-OES. There was a positive and significant correlation between the levels of available Ni in the soils subjected to Mehlich-1 and DTPA extraction, while for plant tissue samples the Ni levels recovered were high and similar to the reference materials. The availability of Ni in some of the natural soil and plant tissue samples were lower than the limits of quantification. Concentrations of this micronutrient were higher in the soil samples in which Ni had been applied. Nickel concentration differed in the plant parts analyzed, with highest levels in the grains of soybean. The grain, in comparison with the shoot and leaf concentrations, were better correlated with the soil available levels for both extractants. The methods described in this article were efficient in quantifying Ni and can be used for routine laboratory analysis of soils and plant tissues.

  20. Chitosan doped with nanoparticles of copper, nickel and cobalt.

    Science.gov (United States)

    Cárdenas-Triviño, Galo; Elgueta, Carolina; Vergara, Luis; Ojeda, Javier; Valenzuela, Ariel; Cruzat, Christian

    2017-11-01

    Metal colloids in 2 propanol using nanoparticles (NPs) of copper, nickel and cobalt were prepared by Chemical Liquid Deposition (CLD) method. The resulting colloidal dispersions were characterized by Transmission Electron Microscopy (TEM). The colloids were supported in chitosan. Then, microbiological assays were performed using E. coli and S. aureus in order to determine the bactericide/bacteriostatic activity of nanoparticles (NPs) trapped or chelated with chitosan. Finally, the toxicity of the metal colloids Cu, Ni and Co was tested. Bio-assays were conducted in three different animal species. First of all on earth warms (Eisenia foetida) to evaluate the toxicity and the biocompatibility of chitosan in lactic acid (1% and 0.5%). Secondly bio-assay done in fishes (rainbow trout), the liver toxicity of NPs in vivo was evaluated. Finally, a bio-assay was conducted in Sprange-Dawley rats of 100g weight, which were injected intraperitoneally with different solutions of chitosan metal colloids. Then, the minimum and maximum concentration were determined for copper, nickel and cobalt. The purpose of the use of chitosan was acting as a carrier for some magnetic NPs, which toxicity would allow to obtain new polymeric materials with potential applications as magnet future drugs carrier. Copyright © 2017 Elsevier B.V. All rights reserved.

  1. Incorporation of iridium into electrodeposited rhenium–nickel alloys

    International Nuclear Information System (INIS)

    Cohen Sagiv, Maayan; Eliaz, Noam; Gileadi, Eliezer

    2013-01-01

    Rhenium (Re), a refractory metal that has gained significant recognition as a high performance engineering material, is mostly used in military, aircraft and aerospace applications, as well as for catalysis in the petrochemical industry. However, its performance at high temperature in humid air is limited by the formation of rhenium heptoxide (Re 2 O 7 ), which penetrates the grain boundaries and causes brittleness. Improvement of this is being sought through the incorporation of iridium (Ir) into Re deposits. To this end, suitable plating baths for Re–Ir–Ni coatings were developed. These alloys were deposited from different aqueous solutions on copper substrates under galvanostatic conditions, in a three-electrode cell. The plating bath consisted of iridium tri-chloride, ammonium perrhenate and nickel sulfamate as the electroactive species, and citric acid as the complexing agent. The effects of bath composition and operating conditions on the Faradaic efficiency (FE), partial current densities, as well as on the thickness of the coatings and their composition were studied. Re–Ir–Ni coatings as thick as 18 μm, with Re-content as high as 73 at.% and Ir-content as high as 29 at.%, were obtained, using different plating baths. A mechanism of the electrochemical process was suggested. It was found that both an HCP Ir 0.4 Re 0.6 phase and an HCP Ni phase with nanometric crystallites were formed, possibly together with a hexagonal nickel hydride (Ni 2 H) phase

  2. Rehabilitating acid soils for increasing crop productivity through low-cost liming material.

    Science.gov (United States)

    Bhat, Javid Ahmad; Kundu, Manik Chandra; Hazra, Gora Chand; Santra, Gour Hari; Mandal, Biswapati

    2010-09-15

    Productivity of red and lateritic soils is low because of their acidity and deficiencies in few essential nutrients viz., nitrogen, phosphorus, calcium, zinc, boron, molybdenum etc. We compared the effectiveness of basic slag, a low-cost liming material, with that of calcite as an ameliorant for these soils using mustard followed by rice as test crops. Experiments were conducted with three levels of each of basic slag and calcite along with a control on farmers' fields at 14 different locations. Influence of farmyard manure (FYM) and poultry manure (PM) on the effectiveness of the slag was also tested. On an average, basic slag performed better than calcite in increasing yields of both mustard and rice and left over higher amounts of available Ca, Si and Zn in residual soils. The slag also improved N, P, K and Ca nutrition of mustard and Si and Zn nutrition of rice with a favorable benefit:cost (B:C) ratio over the calcite (4.82 vs. 1.44). Effectiveness of the basic slag improved when it was applied in combination with FYM or PM (B:C, 5.83 and 6.27). Basic slag can, therefore, be advocated for use in the acidic red and lateritic soils for economically improving their productivity. Copyright 2010 Elsevier B.V. All rights reserved.

  3. Rehabilitating acid soils for increasing crop productivity through low-cost liming material

    International Nuclear Information System (INIS)

    Bhat, Javid Ahmad; Kundu, Manik Chandra; Hazra, Gora Chand; Santra, Gour Hari; Mandal, Biswapati

    2010-01-01

    Productivity of red and lateritic soils is low because of their acidity and deficiencies in few essential nutrients viz., nitrogen, phosphorus, calcium, zinc, boron, molybdenum etc. We compared the effectiveness of basic slag, a low-cost liming material, with that of calcite as an ameliorant for these soils using mustard followed by rice as test crops. Experiments were conducted with three levels of each of basic slag and calcite along with a control on farmers' fields at 14 different locations. Influence of farmyard manure (FYM) and poultry manure (PM) on the effectiveness of the slag was also tested. On an average, basic slag performed better than calcite in increasing yields of both mustard and rice and left over higher amounts of available Ca, Si and Zn in residual soils. The slag also improved N, P, K and Ca nutrition of mustard and Si and Zn nutrition of rice with a favorable benefit:cost (B:C) ratio over the calcite (4.82 vs. 1.44). Effectiveness of the basic slag improved when it was applied in combination with FYM or PM (B:C, 5.83 and 6.27). Basic slag can, therefore, be advocated for use in the acidic red and lateritic soils for economically improving their productivity.

  4. Rehabilitating acid soils for increasing crop productivity through low-cost liming material

    Energy Technology Data Exchange (ETDEWEB)

    Bhat, Javid Ahmad [Directorate of Research, Bidhan Chandra Krishi Viswavidyalaya, Kalyani - 741 235, West Bengal (India); Kundu, Manik Chandra, E-mail: mckundu@rediffmail.com [Directorate of Research, Bidhan Chandra Krishi Viswavidyalaya, Kalyani - 741 235, West Bengal (India); Hazra, Gora Chand [Directorate of Research, Bidhan Chandra Krishi Viswavidyalaya, Kalyani - 741 235, West Bengal (India); Santra, Gour Hari [Department of Soil Science and Agril. Chemistry, Orissa University of Agriculture and Technology, Bhubaneswar - 751003, Orissa (India); Mandal, Biswapati [Directorate of Research, Bidhan Chandra Krishi Viswavidyalaya, Kalyani - 741 235, West Bengal (India)

    2010-09-15

    Productivity of red and lateritic soils is low because of their acidity and deficiencies in few essential nutrients viz., nitrogen, phosphorus, calcium, zinc, boron, molybdenum etc. We compared the effectiveness of basic slag, a low-cost liming material, with that of calcite as an ameliorant for these soils using mustard followed by rice as test crops. Experiments were conducted with three levels of each of basic slag and calcite along with a control on farmers' fields at 14 different locations. Influence of farmyard manure (FYM) and poultry manure (PM) on the effectiveness of the slag was also tested. On an average, basic slag performed better than calcite in increasing yields of both mustard and rice and left over higher amounts of available Ca, Si and Zn in residual soils. The slag also improved N, P, K and Ca nutrition of mustard and Si and Zn nutrition of rice with a favorable benefit:cost (B:C) ratio over the calcite (4.82 vs. 1.44). Effectiveness of the basic slag improved when it was applied in combination with FYM or PM (B:C, 5.83 and 6.27). Basic slag can, therefore, be advocated for use in the acidic red and lateritic soils for economically improving their productivity.

  5. Characterization in Helicobacter pylori of a Nickel Transporter Essential for Colonization That Was Acquired during Evolution by Gastric Helicobacter Species

    Science.gov (United States)

    Turlin, Evelyne; Mancuso, Francesco; Michel, Valérie; Richaud, Pierre; Veyrier, Frédéric J.; De Reuse, Hilde; Vinella, Daniel

    2016-01-01

    Metal acquisition is crucial for all cells and for the virulence of many bacterial pathogens. In particular, nickel is a virulence determinant for the human gastric pathogen Helicobacter pylori as it is the cofactor of two enzymes essential for in vivo colonization, urease and a [NiFe] hydrogenase. To import nickel despite its scarcity in the human body, H. pylori requires efficient uptake mechanisms that are only partially defined. Indeed, alternative ways of nickel entry were predicted to exist in addition to the well-described NixA permease. Using a genetic screen, we identified an ABC transporter, that we designated NiuBDE, as a novel H. pylori nickel transport system. Unmarked mutants carrying deletions of nixA, niuD and/or niuB, were constructed and used to measure (i) tolerance to toxic nickel exposure, (ii) intracellular nickel content by ICP-OES, (iii) transport of radioactive nickel and (iv) expression of a reporter gene controlled by nickel concentration. We demonstrated that NiuBDE and NixA function separately and are the sole nickel transporters in H. pylori. NiuBDE, but not NixA, also transports cobalt and bismuth, a metal currently used in H. pylori eradication therapy. Both NiuBDE and NixA participate in nickel-dependent urease activation at pH 5 and survival under acidic conditions mimicking those encountered in the stomach. However, only NiuBDE is able to carry out this activity at neutral pH and is essential for colonization of the mouse stomach. Phylogenomic analyses indicated that both nixA and niuBDE genes have been acquired via horizontal gene transfer by the last common ancestor of the gastric Helicobacter species. Our work highlights the importance of this evolutionary event for the emergence of Helicobacter gastric species that are adapted to the hostile environment of the stomach where the capacity of Helicobacter to import nickel and thereby activate urease needs to be optimized. PMID:27923069

  6. Numerous dilemmas surrounding the 1917 nickel coins

    Directory of Open Access Journals (Sweden)

    Pantelić Svetlana

    2017-01-01

    Full Text Available The Law on Extraordinary Loans Amounting to 200 Million Dinars and the Minting of Silver and Nickel Coins in 1916 was the legal basis for minting the 5-, 10-, and 20-para nickel coins of the Kingdom of Serbia featuring the year 1917 as their minting year. Some authors believe that these coins were minted in the Minting House in Paris, whereas the others agree that they were certainly minted in France, but in a still unidentified minting house. There are authors who in recent reference literature underline the possibility of their minting in the USA Gorham Company, in Providence, Rhode Island. These coins had all the characteristics of the nickel coins of the Kingdom of Serbia from 1883, 1884, 1904 and 1912. Although, according to the Law, the Minister of Finance was authorized to mint 10 million dinars of these nickel coins, only 5 million pieces in each denomination were actually minted, in the total nominal value of just 1,750,000 dinars. The general opinion is that after the war only a small amount of these nickel coins reached Serbia, because the ships transporting the Serbian coins from the minting house sank on their way. The only varying aspect in this explanation is the location from which the ships were sailing towards Corfu, i.e. from the USA or from France. These coins stopped being legal tender as of 30 November 1931.

  7. Long-Term Effects of Soldering By-Products on Nickel-Coated Copper Wire

    Science.gov (United States)

    Rolin, T. D.; Hodge, R. E.

    2008-01-01

    An analysis of thirty-year-old, down graded flight cables was conducted to determine the makeup of a green material on the surface of the shielded wire near soldered areas and to ascertain if the green material had corroded the nickel-coated copper wire. Two likely candidates were possible due to the handling and environments to which these cables were exposed. The flux used to solder the cables is known to contain abietic acid, a carboxylic acid found in many pine rosins used for the soldering process. The resulting material copper abietate is green in color and is formed during the application of heat during soldering operations. Copper (II) chloride, which is also green in color is known to contaminate flight parts and is corrosive. Data is presented that shows the material is copper abietate, not copper (II) chloride, and more importantly that the abietate does not aggressively attack nickel-plated copper wire.

  8. Monoliths of activated carbon from coconut shell and impregnation with nickel and copper

    International Nuclear Information System (INIS)

    Giraldo, Liliana; Moreno, Juan

    2008-01-01

    A series of different monoliths of activated carbon were prepared from coconut shell By means of chemical activation with phosphoric acid at different concentrations Without using binders or plastics. The monolith that developed the biggest surface area was impregnated by humidic route with solutions of Ni and Cu at different molar relations. The structures were characterized by N2 adsorption at 77 K, and the morphology was explored by means of scanning electron microscopy. The carbonaceous materials obtained, Nickel-Copper-Monolith, were analyzed by Thermal Programmed Reduction (TPR). The experimental results indicated that the activation with the acid generated a micro porosity, with micropores volume between 0.40 and 0.81 cm 3 g-1 and surface areas between 703 and 1450 m 2 g-1, and a good mechanical properties. It shows that, both the copper and the nickel, are fixed to the monolith and TPR's results are interpreted when these molar relation are modified.

  9. Mechanical Properties of Electrolyte Jet Electrodeposited Nickel Foam

    Directory of Open Access Journals (Sweden)

    Jinsong Chen

    2013-07-01

    Full Text Available Principles of the preparation of nickel foam by electrolyte jet electrodeposition were introduced, Nickel foam samples with different porosity were fabricated. Effect of different porosity on microhardness and uniaxial tensile properties of nickel foam was discussed. The results show that the microhardness of nickel foam is 320~400 HV, lower than entitative metal clearly. The lower the porosity of nickel foam, the higher the microhardness is. During the process of uniaxial tensile, nickel foam is characterized by three distinct regions, e.g. elastic deforming region, plastic plateau region and densification region. The higher the porosity of nickel foam, the lower the plastic plateau and the poorer the strength of nickel foam, accordingly

  10. THE LOCAL LASER-STIMULATED ELECTRODEPOSITION OF THE NICKEL

    Directory of Open Access Journals (Sweden)

    V. A. Zabludovskyi

    2009-12-01

    Full Text Available The mask-free method for obtaining the local nickel coatings using laser radiation is developed. The parameters of local nickel coatings are calculated. The rate of electroplating process is estimated.

  11. Occupational exposure to nickel salts in electrolytic plating.

    Science.gov (United States)

    Kiilunen, M; Aitio, A; Tossavainen, A

    1997-04-01

    An occupational hygiene survey was made in 38 nickel plating shops in Finland and exposure to nickel was studied by means of biological measurements and, in three shops, by using air measurements. The average after-shift urinary nickel concentration of 163 workers was 0.16 mumol l.-1 (range 0.001-4.99 mumol l.-1). After the 1-5 week vacation the urinary nickel concentration was higher than the upper reference limit of non-exposed Finns indicating that a part of water-soluble nickel salts is accumulated in the body. Urinary nickel concentrations in the shops considered clean in the industrial hygiene walk-through were not different from those observed in the shops considered dirty. The correlation between the concentrations of nickel in the air and in the urine was low, and the amount of nickel excreted in the urine exceeded the calculated inhaled amounts, indicating exposure by other routes such as ingestion.

  12. Systemic contact dermatitis after oral exposure to nickel

    DEFF Research Database (Denmark)

    Jensen, Christian Stab; Menné, Torkil; Johansen, Jeanne Duus

    2006-01-01

    Systemic contact dermatitis can be elicited experimentally in nickel-sensitive individuals by oral nickel exposure. A crucial point interpreting such experiments has been the relevance of nickel exposure from drinking water and diet. The aim of this meta-analysis study on former nickel......-exposure investigations was to provide the best possible estimation of threshold values of nickel doses that may cause systemic contact dermatitis in nickel-sensitive patients. 17 relevant investigations were identified, and statistical analyses were performed in a stepwise procedure. 9 studies were included in the final...... of the doses that, theoretically, would cause systemic contact dermatitis in exposed nickel-sensitive patients. The results from the 2 most sensitive groups show that 1% of these individuals may react with systemic contact dermatitis at normal daily nickel exposure from drinking water and diet, i.e. 0...

  13. Preparation of Ultra-Fine Nickel Manganite Powders and Ceramics by a Solid-State Coordination Reaction

    NARCIS (Netherlands)

    Fang, Dao-lai; Wang, Zhongbing; Wang, Zhichun; Yang, Pinghua; Liu, W.; Liu, Wei; Winnubst, Aloysius J.A.; Chen, Chusheng

    2006-01-01

    A solid-state coordination reaction was adopted to prepare negative temperature coefficient ceramics. A mixed oxalate NiMn2(C2O4)3·6H2O, a coordination compound, was synthesized by milling a mixture of nickel acetate, manganese acetate, and oxalic acid for 5 h at room temperature. An ultrafine

  14. Supercapacitors Based on Nickel Oxide/Carbon Materials Composites

    OpenAIRE

    Lota, Katarzyna; Sierczynska, Agnieszka; Lota, Grzegorz

    2011-01-01

    In the thesis, the properties of nickel oxide/active carbon composites as the electrode materials for supercapacitors are discussed. Composites with a different proportion of nickel oxide/carbon materials were prepared. A nickel oxide/carbon composite was prepared by chemically precipitating nickel hydroxide on an active carbon and heating the hydroxide at 300 ∘C in the air. Phase compositions of the products were characterized using X-ray diffractometry (XRD). The morphology of the composite...

  15. Essential elucidation for preparation of supported nickel phosphide upon nickel phosphate precursor

    International Nuclear Information System (INIS)

    Liu, Xuguang; Xu, Lei; Zhang, Baoquan

    2014-01-01

    Preparation of supported nickel phosphide (Ni 2 P) depends on nickel phosphate precursor, generally related to its chemical composition and supports. Study of this dependence is essential and meaningful for the preparation of supported Ni 2 P with excellent catalytic activity. The chemical nature of nickel phosphate precursor is revealed by Raman and UV–vis spectra. It is found that initial P/Ni mole ratio ≥0.8 prohibits the Ni-O-Ni bridge bonding (i.e., nickel oxide). This chemical bonding will not result in Ni 2 P structure, verified by XRD characterization results. The alumina (namely, γ-Al 2 O 3 , θ-Al 2 O 3 , or α-Al 2 O 3 ) with distinct physiochemical properties also results in diverse chemical nature of nickel phosphate, and then different nickel phosphides. The influence of alumina support on producing Ni 2 P was explained by the theory of surface energy heterogeneity, calculated by the NLDFT method based on N 2 -sorption isotherm. The uniform surface energy of α-Al 2 O 3 results only in the nickel phosphosate precursor and thus the Ni 2 P phase. - Graphical abstract: Surface energy heterogeneity in alumina (namely α-Al 2 O 3 , θ-Al 2 O 3 , and γ-Al 2 O 3 ) supported multi-oxidic precursors with different reducibilities and thus diverse nickel phosphides (i.e., Ni 3 P, Ni 12 P 5 , Ni 2 P). - Highlights: • Preparing pure Ni 2 P. • Elucidating nickel phosphate precursor. • Associating with surface energy

  16. Synthesis of Nickel Oxide Nanoparticles Using Gelatine as a Green Template for Photocatalytic Degradation of Dye

    OpenAIRE

    JAY YANG LEE

    2018-01-01

    Nickel oxide (NiO) nanoparticles were synthesized through sol-gel method with an environmentally friendly templating agent, which is gelatin. The synthesized NiO were characterized to determine the chemical and physical properties of the nanoparticles. The optimum synthesis parameters were used in photocatalytic degradation of Reactive Black 5 and Acid Yellow 25 dye to determine the catalytic activity of the nanoparticles.

  17. Lung cancer mortality in nickel/chromium platers, 1946-95

    OpenAIRE

    Sorahan, T.; Burges, D. C.; Hamilton, L.; Harrington, J. M.

    1998-01-01

    OBJECTIVES: To investigate mortality from lung cancer in nickel/chromium platers. METHODS: The mortality experience of a cohort of 1762 chrome workers (812 men, 950 women) from a large electroplating and light engineering plant in the Midlands, United Kingdom, was investigated for the period 1946-95. All subjects were first employed in chrome work at the plant during the period 1946-75, and had at least six months employment in jobs associated with exposure to chromic acid mist (hexaval...

  18. Iodometric determination of decahydrodecaborate (2-) salts in aqueous solutions and nickel plating electrolytes

    International Nuclear Information System (INIS)

    Egorova, N.V.; Svitsyn, R.A.

    1991-01-01

    A method for decahydrodecaborate (2-) anion determination in aqueous solutions and in electrolyte of nickel plating in the range of concentrations 0.002-100 mass % was described. The method is based on the interaction of the compound analyzed with iodine in the presence of acetic acid in the process of heating and subsequent titration of iodine excess by sodium thiosulfate. Relative error of the determination is 1 %

  19. Nickel exposure and prevalent albuminuria and β2-microglobulinuria: evidence from a population-based study.

    Science.gov (United States)

    Liu, Gang; Sun, Qi; Zhu, Mingjiang; Sun, Liang; Wang, Zhenzhen; Li, Huaixing; Li, Zi; Chen, Yan; Yin, Huiyong; Lin, Xu

    2016-05-01

    High exposure to nickel could induce renal dysfunction in rodents and occupational workers. However, little is known about the effects of non-occupational exposure to nickel on renal health in the general population. We aimed to examine the associations of urinary nickel concentrations with albuminuria and β2-microglobulinuria in Chinese adults. 2115 non-institutionalised Chinese men and women aged 55-76 years from Beijing and Shanghai were included. Urinary nickel concentrations were assessed by inductively coupled plasma mass spectroscopy. Plasma uric acid, urea nitrogen, C reactive protein and urinary albumin, β2-microglobulin and creatinine were measured. Albuminuria was defined as urinary albumin ≥30 mg/g creatinine, and β2-microglobulinuria was defined as urinary β2-microglobulin ≥200 µg/g creatinine. Median concentration of urinary nickel was 3.95 μg/g creatinine (IQR: 2.57-6.71 μg/g creatinine), and prevalence of albuminuria, β2-microglobulinuria and both albuminuria and β2-microglobulinuria was 22.1%, 24.5% and 9.7%, respectively. Comparing the highest with the lowest quartile of urinary nickel, the ORs (95% CIs) were 1.99 (1.46 to 2.78) for albuminuria, 1.44 (1.07 to 1.95) for β2-microglobulinuria, and 2.95 (1.74 to 4.97) for both albuminuria and β2-microglobulinuria, after adjustment for demographic characteristics, lifestyle behaviours, body mass index, hypertension and diabetes. The association remained significant when further controlling for inflammatory markers or other heavy metals (all p trend nickel levels were positively associated with albuminuria and β2-microglobulinuria in Chinese men and women, who had relatively low background nickel exposure. More prospective studies are needed to confirm our findings. Published by the BMJ Publishing Group Limited. For permission to use (where not already granted under a licence) please go to http://www.bmj.com/company/products-services/rights-and-licensing/

  20. Nickel - iron battery. Nikkel - jern batteri

    Energy Technology Data Exchange (ETDEWEB)

    Petersen, H. A.

    1989-03-15

    A newer type of nickel-iron battery, (SAFT 6v 230 Ah monobloc), which could possibly be used in relation to electrically driven light road vehicles, was tested. The same test methods used for lead batteries were utilized and results compared favourably with those reached during other testings carried out, abroad, on a SAFT nickle-iron battery and a SAB-NIFE nickel-iron battery. Description (in English) of the latter-named tests are included in the publication as is also a presentation of the SAFT battery. Testing showed that this type of battery did not last as long as had been expected, but the density of energy and effect was superior to lead batteries. However energy efficiency was rather poor in comparison to lead batteries and it was concluded that nickel-iron batteries are not suitable for stationary systems where recharging under a constant voltage is necessary. (AB).

  1. Electrodeposition of nickel nano wire arrays

    International Nuclear Information System (INIS)

    Nur Ubaidah Saidin; Kok Kuan Ying; Ng Inn Khuan; Nurazila Mat Zali; Siti Salwa Zainal Abidin

    2010-01-01

    Synthesis, characterization and assembly of one-dimensional nickel nano wires prepared by template directed electrodeposition are discussed in this paper. Parallel arrays of high aspect ratio nickel nano wires were electrodeposited using electrolytes with different cations and pH. The nano wires were characterized using X-ray diffractometry and scanning electron microscopy. It was found that the orientations of the electro deposited Ni nano wires were governed by the deposition current and the electrolyte conditions. Free standing nickel nano wires can be obtained by dissolving the template. Due to the magnetic nature of the nano wires, magnetic alignment was employed to assemble and position the free standing nano wires in the device structure. (author)

  2. Platinum-Group Minerals in Chromitites of the Niquelândia Layered Intrusion (Central Goias, Brazil: Their Magmatic Origin and Low-Temperature Reworking during Serpentinization and Lateritic Weathering

    Directory of Open Access Journals (Sweden)

    Nelson Angeli

    2012-10-01

    Full Text Available A variety of platinum-group-minerals (PGM have been found to occur associated with the chromitite and dunite layers in the Niquelândia igneous complex. Two genetically distinct populations of PGM have been identified corresponding to phases crystallized at high temperatures (primary, and others formed or modified during post-magmatic serpentinization and lateritic weathering (secondary. Primary PGM have been found in moderately serpentinized chromitite and dunite, usually included in fresh chromite grains or partially oxidized interstitial sulfides. Due to topographically controlled lateritic weathering, the silicate rocks are totally transformed to a smectite-kaolinite-garnierite-amorphous silica assemblage, while the chromite is changed into a massive aggregate of a spinel phase having low-Mg and a low Fe3+/Fe2+ ratio, intimately associated with Ti-minerals, amorphous Fe-hydroxides, goethite, hematite and magnetite. The PGM in part survive alteration, and in part are corroded as a result of deep chemical weathering. Laurite is altered to Ru-oxides or re-crystallizes together with secondary Mg-ilmenite. Other PGM, especially the Pt-Fe alloys, re-precipitate within the altered chromite together with kaolinite and Fe-hydroxides. Textural evidence suggests that re-deposition of secondary PGM took place during chromite alteration, controlled by variation of the redox conditions on a microscopic scale.

  3. Extraction and Separation of Cobalt and Nickel with Extractants Cyanex 302, Cyanex 272 and Their Mixture

    Directory of Open Access Journals (Sweden)

    Lenhard, Z.

    2008-09-01

    Full Text Available The extraction and separation of cobalt(II and nickel(II from sulphate solutions with different initial volume fractions of commercial organophosphorus extractants Cyanex 302, Cyanex 272 and their mixture, in kerosene as diluent, were investigated. Prepared samples contained the mixture of cobalt(II and nickel(II in mass concentrations chosen to approximate the mass concentrations of the two metals in solutions obtained by leaching typical low-grade ores or waste materials with sulphuric acid. The experiments were carried out at two concentration ratios of nickel to cobalt(ζNi/Co, 25 and 125. The latter ratio was chosen as model for the solutions of naturally occurring ores and other materials in which the concentration of nickel is much higher than that of cobalt. In all cases, the concentration of cobalt was approximately y= 0.15 g L–1, and the concentration of nickel was approximately g= 3.80 g L–1 (at ζNi/Co = 25 and 18.80 g L–1 (at ζNi/Co = 125. Other initial values were based on conditions found to be optimal in previous investigations, and kept constant in all experiments: pH0= 8, θ0 = 25 °C, phase volume ratio organic to aqueous ψ = 1 and 0.5, contact time 2 minutes.The tested fractions of extractants (Cyanex 302 or Cyanex 272, diluted in kerosene, were j = 2.5, 5.0, 7.5 and φ = 10 %. The studies of the mixture of extractants were carried out at two sets of fractions. In the first set, the fraction of Cyanex 302 was kept at φ = 10 %, and Cyanex 272 was varied in the range φ = 2.5 –10 %. In the second set, the mass concentration of each of the two extractants was varied in the range φ = 2.5–10 % so that the total fraction of the two extractants always added up to φ= 10 %.The obtained results describe the influences of type and initial volume fraction of extractant on the separation and extraction of cobalt and nickel. Under the investigated range of conditions, Cyanex 302 outperformed Cyanex 272 in cobalt-nickel

  4. Characterization and Growth Mechanism of Nickel Nano wires Resulting from Reduction of Nickel Formate in Polyol Medium

    International Nuclear Information System (INIS)

    Logutenko, O.A.; Titkov, A.I.; Vorobyov, A.M.; Yukhin, Y.M.; Lyakhov, N.Z.

    2016-01-01

    Nickel linear nano structures were synthesized by reduction of nickel formate with hydrazine hydrate in ethylene glycol medium in the absence of any surfactants or capping agents for direction of the particles growth. The effect of the synthesis conditions such as temperature, reduction time, type of polyol, and nickel formate concentration on the reduction products was studied. The size and morphology of the nickel nano wires were characterized by X-ray diffraction, scanning, and transmission electron microscopy. It was shown that the nickel nano crystallites were wire-shaped with a face-center-cubic phase. Ethylene glycol was found to play a crucial role in the formation of the nickel nano wires. The possible growth processes of the wire-shaped particles taking place at 110 and 130 degree are discussed. It was shown that, under certain synthesis conditions, nickel nano wires grow on the surface of the crystals of the solid intermediate of nickel with hydrazine hydrate.

  5. Chemistry of nickel and copper production from sulphide ores | Love ...

    African Journals Online (AJOL)

    Nickel is one of Zimbabwe's principle metallurgical exports. It is processed to a very high level of purity and hence has a high value. The economics of nickel production can be difficult, as the selling value of nickel varies tremendously with time, from a low of US$ 3 900 per ton in late 1998 to US$ 10 100 per ton in May 2000, ...

  6. Impact of nickel (Ni) on hematological parameters and behavioral ...

    African Journals Online (AJOL)

    Jane

    2011-10-17

    Oct 17, 2011 ... The effect of nickel on hematological parameters and behaviour in Cyprinus carpio after a 96 h exposure to nickel test was investigated. .... important food item in human diet. Nickel is a natural element in the earth's makeup. This must be a factor in assessing its ability to harm the environment. Although,.

  7. Relationship between nickel and cobalt sensitization in hard metal workers

    Energy Technology Data Exchange (ETDEWEB)

    Rystedt, I; Fischer, T

    1983-05-01

    Eight hundred fifty-three hard metal workers were examined and patch tested with 20 substances from their environment, including nickel and cobalt. Nickel sensitivity was found in 2 men and 38 women. 88% of the nickel-sensitive individuals had developed a jewelry dermatitis prior to employment in the hard metal industry or before the appearance of hand eczema. 29% of the hard metal workers gave a history of slight irritant dermatitis. In the nickel sensitized group, 40% had had severe hand eczema which generally appeared 6-12 months after starting employment. In 25% of the cases, nickel sensitive individuals developed cobalt allergy, compared with 5% in the total population investigated. Most facts indicate that nickel sensitivity and irritant hand eczema precede cobalt sensitization. Hard metal workers with simultaneous nickel and cobalt sensitivity had a more severe hand eczema than those with isolated cobalt or nickel sensitivity or only irritant dermatitis. 64% of the female population had pierced ear lobes. Among the nickel allergic women, 95% had pierced ear lobes. The use of earrings containing nickel after piercing is strongly suspected of being the major cause of nickel sensitivity. Piercing at an early age seems to increase the risk of incurring nickel sensitivity.

  8. Nickel sensitisation in mice: a critical appraisal.

    Science.gov (United States)

    Johansen, Pål; Wäckerle-Men, Ying; Senti, Gabriela; Kündig, Thomas M

    2010-06-01

    The market release of new domestic and industrial chemical and metal products requires certain safety certification, including testing for skin sensitisation. Although various official guidelines have described how such testing is to be done, the validity of the available test models are in part dubious, for which reason regulatory agencies and research aim to further improve and generalise the models for testing of skin sensitisation. We applied a recently published murine model of nickel allergy as to test its applicability in a regulatory setting and to study and better understand the events leading to type-IV hypersensitivity. Nickel was chosen as model hapten since it induces allergic contact dermatitis with high incidence in the general population. Typically, C57BL/6 mice were sensitised and challenged by intradermal applications of nickel, and cutaneous inflammation was analysed by the mouse ear-swelling test, by histology, and by lymphocyte reactivity in vitro. Surprisingly, the study suggested that the skin reactions observed were results of irritant reactions rather than of adaptive immune responses. Non-sensitised mice responded with cutaneous inflammation and in vitro lymphocyte reactivity which were comparable with nickel-sensitised mice. Furthermore, histological examinations as well as experiments in T-cell deficient mice demonstrated that lymphocytes were not involved and that nickel caused an irritant contact dermatitis rather a true allergic type-IV contact dermatitis. The authors question the validity of the described murine model of nickel allergy. Copyright 2010 Japanese Society for Investigative Dermatology. Published by Elsevier Ireland Ltd. All rights reserved.

  9. Prototype nickel component demonstration. Final report

    International Nuclear Information System (INIS)

    Boss, D.E.

    1994-01-01

    We have been developing a process to produce high-purity nickel structures from nickel carbonyl using chemical vapor deposition (CVD). The prototype demonstration effort had been separated into a number of independent tasks to allow Los Alamos National Laboratory (LANL) the greatest flexibility in tailoring the project to their needs. LANL selected three of the proposed tasks to be performed--Task 1- system modification and demonstration, Task 2-stainless steel mandrel trials, and Task 4-manufacturing study. Task 1 focused on converting the CVD system from a hot-wall to a cold-wall configuration and demonstrating the improved efficiency of the reactor type by depositing a 0.01-inch-thick nickel coating on a cylindrical substrate. Since stainless steel substrates were preferred because of their low α-emitter levels, Task 2 evaluated mandrel configurations which would allow removal of the nickel tube from the substrate. The manufacturing study was performed to develop strategies and system designs for manufacturing large quantities of the components needed for the Sudbury Nuetrino Observatory (SNO) program. Each of these tasks was successfully completed. During these efforts, BIRL successfully produced short lengths of 2-inch-diameter tubing and 6-inch-wide foil with levels of α-radiation emitting contaminants lower than either conventional nickel alloys or electroplated materials. We have produced both the tubing and foil using hot-substrate, cold-wall reactors and clearly demonstrated the advantages of higher precursor efficiency and deposition rate associated with this configuration. We also demonstrated a novel mandrel design which allowed easy removal of the nickel tubing and should dramatically simplify the production of 1.5-meter-long tubes in the production phase of the program

  10. Separation and purification of carrier-free cobalt-58 from neutron irradiated nickel foil for electrochemical studies

    International Nuclear Information System (INIS)

    Egamediev, S.; Nurbaeva, D.; Rakhmanov, A.

    2004-01-01

    Full text: Cobalt-58 will be used for tracer studies of the behaviour of cobalt radionuclides in no- carrier-added form during electrochemical deposition on metal backing. The 58 Co can be produced by using 58 Ni(n,p) 58 Co nuclear reaction in nuclear reactor. 58 Co (T 1/2 =71 days) decays by positron emitting (15%) and electron capture (85%) with simultaneous γ -irradiation. In this study, we have developed the simple method for separation and purification of 58 Co in no- carrier-added form from neutron irradiated nickel foil. Previously, we have studied the dissolution of nickel foil in various media to find best conditions for rapid dissolution of nickel target. It was found that nickel foil dissolved completely without heating in 6.3 M hydrobromic acid with addition a few drops of hydrogen peroxide. After dissolution of the target material, the cobalt-58 is separated from nickel, copper, iron and other elements by extraction chromatography. The solution in 6.3 M hydrobromic acid is passed through a column containing suspension of polytetrafluoroethylene powder with 0.5 M trioctylamine in xylene, equilibrated with the same acid. Nickel is not extracted and passed through column. Cobalt is retained and finally eluted with 3 M HBr in the one free column volume. The cobalt fraction is percolated through a column filled with suspension of pure polytetrafluoroethylene powder to purify from the admixture of extractant. The obtained solution is evaporated to dryness and the dry residue is treated by evaporation with aqua regia. After treatment the damp residue is dissolved in electrolyte and the obtained solution is used to study of 58 Co electrochemical deposition procedure. The yield of cobalt-58 was higher than 93% and the radiochemical purity was more than 99%. This method will be used for separation and purification of cobalt-57 to make of sealed sources for X-ray fluorescence analysis

  11. Nickel adsorption on chalk and calcite

    DEFF Research Database (Denmark)

    Belova, Dina Alexandrovna; Lakshtanov, Leonid; Carneiro, J.F.

    2014-01-01

    Nickel uptake from solution by two types of chalk and calcite was investigated in batch sorption studies. The goal was to understand the difference in sorption behavior between synthetic and biogenic calcite. Experiments at atmospheric partial pressure of CO2, in solutions equilibrated with calcite...... = - 1.12 on calcite and log KNi = - 0.43 and - 0.50 on the two chalk samples. The study confirms that synthetic calcite and chalk both take up nickel, but Ni binds more strongly on the biogenic calcite than on inorganically precipitated, synthetic powder, because of the presence of trace amounts...... of polysaccharides and clay nanoparticles on the chalk surface....

  12. Nitrogen solubility in nickel base multicomponent melts

    International Nuclear Information System (INIS)

    Bol'shov, L.A.; Stomakhin, A.Ya.; Sokolov, V.M.; Teterin, V.G.

    1984-01-01

    Applicability of various methods for calculation of nitrogen solubility in high-alloyed nickel base alloys, containing Cr, Fe, W, Mo, Ti, Nb, has been estimated. A possibility is shown to use the formUla, derived for the calculation of nitrogen solubility in iron on the basis of statistical theory for a grid model of solution which does not require limitations for the content of a solvent component. The calculation method has been used for nickel alloys, with the concentration of solvent, iron, being accepted equal to zero, and employing parameters of nitrogen interaction as determined for iron-base alloys

  13. Nickel contaminated titanium weld wire study

    International Nuclear Information System (INIS)

    Coffin, G.R.; Sumstine, R.L.

    1979-01-01

    Attachment of thermocouples to fuel rod welding problems at Exxon Nuclear Company and INEL prompted an investigation study of the titanium filler wire material. It was found that the titanium filler wire was contaminated with nickel which was jacketed on the wire prior to the drawing process at the manufacturers. A method was developed to 100% inspect all filler wire for future welding application. This method not only indicates the presence of nickel contamination but indicates quantity of contamination. The process is capable of high speed inspection necessary for various high speed manufacturing processes

  14. Surface-Enhanced Infrared Absorption of o-Nitroaniline on Nickel Nanoparticles Synthesized by Electrochemical Deposition

    Directory of Open Access Journals (Sweden)

    Yufang Niu

    2014-01-01

    Full Text Available Nickel nanoparticles were electrochemically deposited on indium-tin oxide (ITO coated glass plate in a modified Watt’s electrolyte. The surface-enhanced infrared absorption (SEIRA effect of the nanoparticles was evaluated by attenuated total reflection spectroscopy (ATR-FTIR using o-nitroaniline as a probe molecule. Electrodeposition parameters such as deposition time, pH value, and the type of surfactants were investigated. The morphology and the microstructure of the deposits were characterized by the field emission scanning electron microscope (FESEM and the atomic force microscope (AFM, respectively. The results indicate that the optimum parameters were potential of 1.3 V, time of 30 s, and pH of 8.92 in the solution of 0.3756 mol/L diethanolamine, 0.1 mol/L nickel sulfate, 0.01 mol/L nickel chloride, and 0.05 mol/L boric acid. The FESEM observation shows that the morphology of nickel nanoparticles with best enhancement effect is spherical and narrowly distributed particles with the average size of 50 nm. SEIRA enhancement factor is about 68.

  15. Synthesis and magnetic characterization of nickel ferrite nanoparticles prepared by co-precipitation route

    Science.gov (United States)

    Maaz, K.; Karim, S.; Mumtaz, A.; Hasanain, S. K.; Liu, J.; Duan, J. L.

    2009-06-01

    Magnetic nanoparticles of nickel ferrite (NiFe 2O 4) have been synthesized by co-precipitation route using stable ferric and nickel salts with sodium hydroxide as the precipitating agent and oleic acid as the surfactant. X-ray diffraction (XRD) and transmission electron microscope (TEM) analyses confirmed the formation of single-phase nickel ferrite nanoparticles in the range 8-28 nm depending upon the annealing temperature of the samples during the synthesis. The size of the particles ( d) was observed to be increasing linearly with annealing temperature of the sample while the coercivity with particle size goes through a maximum, peaking at ˜11 nm and then decreases for larger particles. Typical blocking effects were observed below ˜225 K for all the prepared samples. The superparamagnetic blocking temperature ( T B) was found to be increasing with increasing particle size that has been attributed to the increased effective anisotropy energy of the nanoparticles. The saturation moment of all the samples was found much below the bulk value of nickel ferrite that has been attributed to the disordered surface spins or dead/inert layer in these nanoparticles.

  16. Determination of Selenium and Nickel in Asphaltite from Milli (Sirnak) Deposit in SE Anatolia of Turkey

    Science.gov (United States)

    Aydin, Isil; Fidan, Celal; Kavak, Orhan; Erek, Figen; Aydin, Firat

    2017-12-01

    Asphaltite is one of the naturally occurring black, solid bitumen’s, which are soluble at heating in carbon disulphide band fuse. Asphaltite is also a solidified hydro carbon compound derived from petroleum [1]. According to the World Energy Council, Turkish National Committee (1998), the total reserve of the asphaltic substances that are found in south eastern Turkey is about 82 million tons, with Silopi and Sirnak reserves to get her comprising the major part of the Asphaltite deposits. Selenium and Nickel are very important elements both environmental and health. Selenium plays an important role in the formation of the enzyme antioxidant effect in the cell. The need for Selenium increases in situations such as pregnancy, menopause, grow than development, air pollution. Nickel is used for preventing iron-poor blood, increasing iron absorption, and treating weak bones. In this study, asphaltites were taken from Milli vein from Sirnak deposit in SE Anatolia of Turkey. A total of 6.500.000 tons of Asphaltite reserves have been identified as asphaltites in Milli (Sirnak). The sample preparation method was developed in Asphaltite by spectroanalytical techniques, wet acid digestion. MW-AD followed by ICP-OES were used for the determination of Selenium and Nickel in Asphaltite. Proximate analysis of Asphaltite fly ash samples was made. It also, Selenium and Nickel element analysis in Asphaltite were made.

  17. Nickel foam-supported polyaniline cathode prepared with electrophoresis for improvement of rechargeable Zn battery performance

    Science.gov (United States)

    Xia, Yang; Zhu, Derong; Si, Shihui; Li, Degeng; Wu, Sen

    2015-06-01

    Porous nickel foam is used as a substrate for the development of rechargeable zinc//polyaniline battery, and the cathode electrophoresis of PANI microparticles in non-aqueous solution is applied to the fabrication of Ni foam supported PANI electrode, in which the corrosion of the nickel foam substrate is prohibited. The Ni foam supported PANI cathode with high loading is prepared by PANI electrophoretic deposition, and followed by PANI slurry casting under vacuum filtration. The electrochemical charge storage performance for PANI material is significantly improved by using nickel foam substrate via the electrophoretic interlayer. The specific capacity of the nickel foam-PANI electrode with the electrophoretic layer is higher than the composite electrode without the electrophoretic layer, and the specific capacity of PANI supported by Ni foam reaches up to 183.28 mAh g-1 at the working current of 2.5 mA cm-2. The present electrophoresis deposition method plays the facile procedure for the immobilization of PANI microparticles onto the surface of non-platinum metals, and it becomes feasible to the use of the Ni foam supported PANI composite cathode for the Zn/PANI battery in weak acidic electrolyte.

  18. Long Life Nickel Electrodes for Nickel-Hydrogen Cells: Fiber Substrates Nickel Electrodes

    Science.gov (United States)

    Rogers, Howard H.

    2000-01-01

    Samples of nickel fiber mat electrodes were investigated over a wide range of fiber diameters, electrode thickness, porosity and active material loading levels. Thickness' were 0.040, 0.060 and 0.080 inches for the plaque: fiber diameters were primarily 2, 4, and 8 micron and porosity was 85, 90, and 95%. Capacities of 3.5 in. diameter electrodes were determined in the flooded condition with both 26 and 31% potassium hydroxide solution. These capacity tests indicated that the highest capacities per unit weight were obtained at the 90% porosity level with a 4 micron diameter fiber plaque. It appeared that the thinner electrodes had somewhat better performance, consistent with sintered electrode history. Limited testing with two-positive-electrode boiler plate cells was also carried out. Considerable difficulty with constructing the cells was encountered with short circuits the major problem. Nevertheless, four cells were tested. The cell with 95% porosity electrodes failed during conditioning cycling due to high voltage during charge. Discharge showed that this cell had lost nearly all of its capacity. The other three cells after 20 conditioning cycles showed capacities consistent with the flooded capacities of the electrodes. Positive electrodes made from fiber substrates may well show a weight advantage of standard sintered electrodes, but need considerably more work to prove this statement. A major problem to be investigated is the lower strength of the substrate compared to standard sintered electrodes. Problems with welding of leads were significant and implications that the electrodes would expand more than sintered electrodes need to be investigated. Loading levels were lower than had been expected based on sintered electrode experiences and the lower loading led to lower capacity values. However, lower loading causes less expansion and contraction during cycling so that stress on the substrate is reduced.

  19. Co-catalytic effect of nickel in Pt-Ru/C and Pt-Sn/C electrocatalysts for ethanol electrooxidation

    OpenAIRE

    Ribadeneira, R. E.; Hoyos, B. A.

    2010-01-01

    In the present study, we examined the effect of adding nickel to Pt-Ru and Pt-Sn catalysts for ethanol electrooxidation. The alcohol-reduction process with ethylene glycol was used to prepare ten electrocatalysts. These were microchemically and physically characterized by EDX and XRD analysis. The electrocatalysts were evaluated at mini-electrodes with cyclic voltammetry at 25 and 50 °C in sulfuric acid and ethanol solutions, and as anodes in fuel cell tests. Nickel addition to Pt-Ru mixtures...

  20. Long life nickel electrodes for a nickel-hydrogen cell: Cycle life tests

    Science.gov (United States)

    Lim, H. S.; Verzwyvelt, S. A.

    1985-01-01

    In order to develop a long life nickel electrode for a Ni/H2 cell, the cycle life of nickel electrodes was tested in Ni/H2 boiler plate cells. A 19 test cell matrix was made of various nickel electrode designs including three levels each of plaque mechanical strength, median pore size of the plaque, and active material loading. Test cells were cycled to the end of their life (0.5v) in a 45 minute low Earth orbit cycle regime at 80% depth-of-discharge. It is shown that the active material loading level affects the cycle life the most with the optimum loading at 1.6 g/cc void. Mechanical strength does not affect the cycle life noticeably in the bend strength range of 400 to 700 psi. It is found that the best plaque is made of INCO nickel powder type 287 and has median pore size of 13 micron.