British Library Electronic Table of Contents (United Kingdom)

Rapid nitridation was used to fabricate reaction-bonded and postsintered -Si6-ZAlZOZN8-Z (Z=1) ceramics with monoclinic ZrO2 added to the starting powder. Thermo-gravimetric analysis revealed that the addition of ZrO2 reduced the starting temperature of the main nitridation reaction. Using a reaction-bonding route with heating rates of 5, 10, and 20C/min, to fabricate -SiAlON ceramics without ZrO2 resulted in unreacted silicon that bled out of the specimens and the Z=1 composition samples did not maintain the original green compact morphology. On the other hand, no such bleeding of melted silicon was observed for samples with ZrO2 additions and the samples following nitridation maintained the original green morphology. The microstructure and mechanical properties of samples produced by rap...

International Nuclear Information System (INIS)

Zirconia has demonstrated a very moderate toughening effect in nitrogen-based ceramic composites because the reaction between tetragonal zirconia (t-ZrO_2) and nitrogen results in additional zirconia stabilization to a nontransformable t' or cubic structure. In O'-SiAlON matrices, the oxygen concentration increases and the oxygen-rich intergranular glassy phase prevents zirconia from nitridation. As a result, tetragonal ZrO_2 is maintained and is transformable in the O'-SiAlON materials. The present study has provided transmission electron microscopy (TEM) evidence of the zirconia transformation and the associated toughening effect in a ZrO_2/O'-SiAlON composite. The implications and limitations of the transformation on toughening of the material are discussed.

International Nuclear Information System (INIS)

Mixed additions of Sm_2O_3 and Y_2O_3 were used in the formation of zirconia-containing O'-sialon composites, where Sm_2O_3 was used for the purpose of densification and Y_2O_3 for zirconia stabilization. Dense ZrO_2/O' -sialon composites were produced at 1500 deg C. by sintering in nitrogen for 4 hours. Tetragonal zirconia remained in the product and t#->#m transformation was observed when the sample was ground into powder. However, the improvement in fracture toughness was not significant and this was attributed to the weakened transformability of the tetragonal zirconia phase in the nitrogen-based materials. 18 refs., 4 tabs., 2 figs.

International Nuclear Information System (INIS)

New data about the structure of high-temperature resistant metalloceramic plasma sprayed coatings in micro and nano areas are presented. Application of the new instrumental methods: transmission electron microscopy combined with selected area electron diffraction mode is possible to obtain these data. The first layer in Ni based metallic bond coat shows nanocrystalline structure. External ceramic layer based on stabilised ZrO_2 is polycrystalline and contains both cubic and tetragonal crystalline phases. Local inhomogeneities in coatings phase composition are determined. (author)

International Nuclear Information System (INIS)

Ceramic matrix composites in the TiC-Ti, Y-TZP system can be synthesized by the reaction between carbon and the TiO_2-Y_2O_3-ZrO_2 solid solution nanopowder. This method results in the more homogeneous powders than those prepared by the physical mixing of TiC and zirconia s.s. powders. Twelve TiO_2-Y_2O_3-ZrO_2 solid solution nanopowders differing in the proportions of the constituent oxides were prepared by the coprecipitation- calcination route. They were reacted with the pyrolytic carbon evenly distributed within the system. Carbon was introduced by the thermal decomposition of the phenol-formaldehyde resin dissolved in ethyl alcohol and mixed with the zirconia s.s. nanopowder. Reaction was performed in vacuum. Compacts of the composite powders sintered in vacuum give dense materials of evenly distributed TiC inclusions of sizes not surpassing 400 nm. Hardness of such materials was dependent on their chemical and phase composition but was generally higher than ...

International Nuclear Information System (INIS)

This work is concerned with the development and application of ion implantation techniques for improving the corrosion resistance of zircaloy-4. The corrosion resistance in nitrogen implanted zircaloy-4 under a 120 keV nitrogen ion beam at an ion dose of 3 x 10"1"7 cm"-"2 depends on the implantation temperature. The characteristics of surface oxidation and corrosion resistance were analyzed with the change of implantation temperature. It is shown that as implantation temperature rises from 100 to 724 C, the colour of specimen surface changes from its original colour to light yellow at 100 C, golden at 175 C, pink at 300 C, blue at 440 C and dark blue at 550 C. As the implantation temperature goes above 640 C, the colour of surface changes to light black, and the surface becomes a little rough. The corrosion resistance of zircaloy-4 implanted with nitrogen is sensitive to the implantation temperature. The pitting potential of specimens increases from 176 to 900 mV ...

International Nuclear Information System (INIS)

Zirconia-toughened sialon composites have been fabricated using conventional hot-pressing techniques. The fracture toughness and microstructure were determined for CeO_2- and Y_2O_3-stabilized ZrO_2 additives and also as a function of volume percent ZrO_2. The Yttria system showed a linear increase in fracture toughness with increasing volume fraction zirconia content while the ceria-stabilized system exhibited a peak in fracture toughness at 20 vol% ZrO_2 content. The fracture toughness at 800 C was measured and correlated with the microstructure. High-temperature stability was determined and it was found that the deleterious nitride phases of zirconium could be precluded from the microstructure.

Energy Technology Data Exchange (ETDEWEB)

For rational use of energy resources, the process technology which allows harmonization and multiplication of conflicting characteristics was developed for development of new ceramic system materials. This paper summarizes the result in fiscal 1997. On a structural reaction process among creation technologies of ultra-reliable structure, study was made on structure control and hot-working technology through atmosphere control in ceramics synthesis. On basic technology for analysis and evaluation, study was made on the effect of particle bridging on strengthening and toughening of ceramic materials. Study was also made on a toughness expression mechanism, FEM model analysis of particle bridging, and crack growth resistance of ceramics. On control of solid solution precipitation, new alumina ceramics with high strength, hardness and wear resistance was obtained by transgranularly ...

Science.gov (United States)

The use of ceramics as energy absorbents has been studied by many researchers and some improvements in the ballistic performance of ceramic tiles have been made by coating them with different classes of materials (e.g. E-glass/epoxy, carbon-fiber/epoxy, etc.). Using ceramics for energy absorbing applications leads to a significant weight reduction of the system. Therefore, any modification to the ceramic configuration in the system which leads to more energy absorption with the same or less areal density is significant. On the other hand, polyurea has been proved to be an excellent energy dissipating agent in many applications. Inspired by this, we are studying the effect of coating ceramics with polyurea and other materials, on the energy absorption and ballistic performance of the resulting ceramic-based composites. In this study, we ...

British Library Electronic Table of Contents (United Kingdom)

Abstract Many (K1-xNax)NbO3 (KNN)-based ceramics with high piezoelectric performance exhibit undesirable strong temperature dependence due to the orthorhombic-tetragonal polymorphic phase transition near room temperature. In order to improve the temperature stability of the ceramics, many additives have been added into the KNN-based ceramics to shift TO-T down to below room temperature. Contrary to the previous approach (Na0.53K0.47-xAgx)Nb1-xSbxO3 (NKANS) ceramics with TO-T well above room temperature have been prepared by a conventional solid-state reaction method. The density and the electrical properties are effectively improved by the addition of AgSbO3, and optimum piezoelectric properties are found in the ceramics with 0.05---x---0.07, with maximum kp---0.46 for NKANS5 and maximum d...

International Nuclear Information System (INIS)

Technology of plasma sputtering, structure and properties of zirconium dioxide coatings were studied. Necessity of void number increase to enhance coating heat-resistance is shown. Optimal powder particle size (20-60 #mu#m) providing optimal coating porosity was determined. Weight part of stabilizating oxide (Y_2O_3) in ZrO_2 for formation in coating of microcracks serving as barriers for macro-cracks propagation was determined.

Energy Technology Data Exchange (ETDEWEB)

This is the final report of a two-year, Laboratory Directed Research and Development (LDRD) project at the Los Alamos National Laboratory (LANL). Functionally graded material is an enabling technology for lightweight body armor improvements. The objective was to demonstrate the ability to produce functionally graded ceramic-polymer and ceramic-metal lightweight armor materials. This objective involved two aspects. The first and key aspect was the development of graded-porosity boron-carbide ceramic microstructures. The second aspect was the development of techniques for liquid infiltration of lightweight metals and polymers into the graded-porosity ceramic. The authors were successful in synthesizing boron-carbide ceramic microstructures with graded porosity. These graded-porosity boron-carbide hot-pressed pieces were then successfully liquid-infiltrated in ...

International Nuclear Information System (INIS)

For several decades, ceramic matrix composite have been attracted attention in advanced structural and tribological applications. Advanced structural ceramics are presently used in diverse tribological applications such as tips for ballpoint pens, precision instrument bearings and cutting tools inserts. Design and selection of ceramics for these applications require reliable data on the effects of temperature, load and environment on the tribological behavior of these ceramics. In the present work, #alpha#-sialon matrix composites reinforced with different amounts of #beta#-sialon fibers were produced with the aim of improving their toughness to increase the industrial applications. The wear properties of #alpha#-sialon matrix composites were evaluated by carried out wear tests using a pin-on-disk tribometer under dry conditions. The #alpha#-sialon matrix composites were ...

International Nuclear Information System (INIS)

Dysprosium #alpha#-sialon ceramic has been fabricated from #alpha#-Si_3N_4, AlN, Al_2O_3 and Dy_2O_3 starting powders, using gas pressure sintering at 1800 deg C or higher temperatures under a relatively low gas pressure of 0.9MPa N_2. The resultant #alpha#-sialon grains showed significantly different features, such as equiaxed, elongated, and even a few extraordinarily large with high aspect ratio grains in the fine matrix, which has rarely been observed in #alpha#' ceramics. It is suggested that the temperature strongly influences the grain morphologies of #alpha#-sialon, playing an important role particularly in the latter stage of the 'nucleation-growth' process. Such a microstructural morphology of mixed with equiaxed and elongated grains toughens the #alpha#-sialon ceramics and leaves them still hard. Overly high temperature treatment leads to the preferential growth of a few #alpha#' grains which become excessively ...

International Nuclear Information System (INIS)

In this study nanocrystalline powders of yttria-stabilized zirconia (ZrO_2-8Y_2O_3) have been synthesized through 'polymerized complex method'. Zirconium chloride, yttrium nitrate, citric acid and ethylene glycol were polymerized at 80 "oC to produce a gel-like mass in which metallic ions were uniformly distributed. During the thermal treatment of dried gel, nanocrystalline powder was formed at 450 "oC and 650 "oC for 2 h. Thermal reactions and crystalline phase formation of the dried gel were investigated through thermal analysis and X-ray diffraction analysis, respectively. The results of thermal analysis and XRD showed the formation of nanocrystalline powder at less than 600 "oC. Chemical bonding of the dried gel was investigated by Fourier transform infrared spectroscopy analysis. Morphology of powder calcined at 650 "oC was analyzed by scanning electron microscope. Yttria-stabilized zirconia powders with the mean crystallite size of 6 nm were prepared successfully by this method.

Energy Technology Data Exchange (ETDEWEB)

This paper describes the basic principles underlying the operation of low heat loss engines and the magnitude of the efficiency improvements that are theoretically achievable. The effect of varying degrees of thermal insulation on various operating parameters is examined in some detail, as is the relationship between degree of insulation and ceramic coating thickness. The effect on ceramic materials of severe surface temperature oscillations and the resultant thermal stress gradients is also discussed. In the following section, the paper describes methods of construction adopted both for ceramic inserts and coatings, and rig tests for the assessment of thermal fatigue under both load and firing cycling. The paper does not attempt to draw any general conclusions.

Energy Technology Data Exchange (ETDEWEB)

The purpose of the invention is to improve a radiation receiver, consisting of a hollow body with an opening for the entry of radiation and a ceramic absorber situated in the hollow body, which absorbs the radiation energy entering through the opening, and emits it as thermal radiation to a heat medium, so that a higher efficiency can be achieved. According to the invention, the problem is solved by the fact that the absorber consists of ceramic material on the side towards the solar radiation, which has a low emission value and a high absorption value, and that the side of the absorber towards the heat medium has ceramic material of high emission value and low absorption value. This ensures that reradiation is prevented near the opening of the hollow body, and that the solar energy entering is largely absorbed in the hollow body.

Energy Technology Data Exchange (ETDEWEB)

Here we report detailed dielectric studies carried out on a Barium strontium titanate (BST) (95:5) composition. The material was synthesized by conventional ceramic method and microwave processing, and the later technique resulted in material with high density, improved microstructure and dielectric properties. The dielectric properties were studied as a function of frequency and temperature and well-defined ferroelectric behavior of first order transition was observed. It follows Curie-Weiss law above transition temperature (paraelectric region). Curie temperature is slightly higher for microwave sintered (MS) material.

Energy Technology Data Exchange (ETDEWEB)

The objective of this work was to identify methods of improving the performance of gas-fired radiant burners through the use of Continuous Fiber Ceramic Composites (CFCCs). Methods have been identified to improve the price and performance characteristics of the porous surface burner. Results are described.

Energy Technology Data Exchange (ETDEWEB)

Creation of new multi-composite materials is an essential issue to attain an innovative improvement of the current nuclear technology. In this paper, some highlights are focused on the research of creation of those materials and the relating subjects in NIRIM. (1) The KOH corrosion test method are expected to be efficiently available in the limited cases instead of Na corrosion test one. (2) The preliminary creation of the multi-composite ceramics were achieved by Y- ion implantation into sapphire and the RF sputtering, of which the specified orientation was realized by the existence of the buffer layer. The importance of the defect control are described with the relation to the corrosion resistance improvement. (3) The ion beam induced phenomena have been investigated on the surface change of silica glass and the crystallization of Cu film on SrTiO{sub 3}. (4) The electronic states of the alkali-metal adsorbed surfaces and ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes the experimental results of long-life solid lubricated ball bearings tested under high-vacuum of 10 exp -4 Pa, high-temperature of 300 C, and high-speed (9000 rpm) conditions. For full ball-type bearings, the thin soft metals, either Ag or Pb, which were coated on the races and balls, appeared to have good torque properties. However, the durability of such bearings was less than 300 hours. The transfer films from the lamellar solid MoS2 and metal composite retainers improved the torque and wear properties. For ceramic, i.e., silicon nitride, balls used with steel rings, wear occurred on the inner rings. All ceramic bearings with composite retainers showed improved torque and wear properties. 18 refs.

Science.gov (United States)

Ceramic and Dental Enamel Wear

Science.gov (United States)

Joint Diseases

Energy Technology Data Exchange (ETDEWEB)

In this paper coating developments for advanced gas turbine engines (diffusion aluminide coatings, overlay coatings, and ceramic thermal barrier coatings) were desorbed, a selection of current metallic coatings was made and their performance as outlined. Finally coating developments for advanced diesel engines with a view to improved turbocharging or to low heat rejection engines (adiabatic diesel concept) were dealt with. (IHOE).

British Library Electronic Table of Contents (United Kingdom)

Spherical nano-sized YSZ (yttria stabilized ZrO2) powders were successfully synthesized via a reverse microemulsion system. The water droplets in the microemulsion system of yclohexane/water/span85/Triton X-100/hexyl alcohol can act as the nano-reactors which solubilize zirconium oxychloride and ammonia water separately. The minute original reactors are favor to the formation of nano-sized spherical YSZ powders and the dispersibility of the powders can be controlled effectually by adjusting the weight ratio of the LiNO3 molten salt to the precursor. The phase transformation from cubic to monoclinic starts at and 500??C and finally monoclinic and cubic phase with increased crytallinity coexist at 800??C. The effect of LiNO3 molten salt in the formation of YSZ powders was also discussed.

International Nuclear Information System (INIS)

The design of solid breeder blankets is strongly affected by the low values of thermal conductivity and density of ceramic breeder pebble beds. A significant rise of both quantities would enhance the thermal performance and lead to an increased tritium breeding ratio. In order to improve these quantities pretreated lithium orthosilicate pebble material was dry pressed and subsequently sintered. The thermal conductivity of cylindrical pellets was determined by the heat pulse method using a laser flash device. A pebble bed characteristic sample was also investigated in order to check the measurement accuracy in comparison with previous results. Furthermore, two samples of low density cellular ceramics were also prepared by infiltration of polymer foams with a ceramic slurry. The thermal conductivity results show that the values are affected both by the particle size and the sample density. Thermal ...

Science.gov (United States)

The Swedish Ceramic Institute is an industrial research institute working with product-oriented research and development of ceramics and closely related materials. The institute works with the processing and fabrication of ceramic materials as well as with materials properties and design questions. Its website provides details of research projects (engineering ceramics, electroceramics, traditional ceramics). Publications are listed, with some downloadable files (annual reports, research reports, information leaflets). Sample materials data (mechanical properties, thermal properties) is given for oxides and non-oxide ceramics.

International Nuclear Information System (INIS)

This is the final report of a one-year, Laboratory-Directed Research and Development (LDRD) project at the Los Alamos National Laboratory (LANL). In an effort to address the problems of long term storage and nuclear waste minimization, zircon has been proposed as a host medium for plutonium and other actinides recovered from dismantled nuclear weapons. The objective of this work is to investigate the feasibility of large scale fabrication of Pu-bearing zircon. Since PuO_2 is thermodynamically less stable than ZrO_2, it is expected that the process parameters determined for synthesizing ZrSiO_4 (zircon) would be applicable to those for PuSiO_4 (Pu-zircon). Furthermore, since the foremost concern in plutonium processing is the potential for contamination release, this work emphasizes the development of process parameters, using zircon first, to anticipate potential material problems in the containment system for reaction mixtures during processing. Stoichiometric mixtures of ZrO_2 and ...

Energy Technology Data Exchange (ETDEWEB)

The goal of this project was to demonstrate that a new low-expanding ceramic (Ca{sub 0.6},Mg{sub 0.4})Zr{sub 4}(PO{sub 4}){sub 6}, hereafter referred to as CMZP, could be used as an exhaust manifold liner in off-road diesel engines and provide improved engine efficiency (by permitting higher engine operating temperature). This study has successfully demonstrated this improvement and further engine testing (and possible manufacturing) is presently underway at Caterpillar Inc. Laboratories. Basically this program involved two subcontracts: one to Virginia Tech to develop sintering procedures for CMZP, and one to Caterpillar, Inc. to develop slip casting procedures for CMZP. Nearly 100kg of CMZP were prepared by MATVA, Inc. and Virginia Tech for use by Caterpillar. Virginia Tech developed detailed sintering procedures for CMZP and Caterpillar developed slip casting procedures and manufactured several exhaust manifold elbows. ...

Energy Technology Data Exchange (ETDEWEB)

On the basis of observations of the JTEC team, it appears that Japanese universities and research institutes are leading long-term R&D thrusts for development of new materials casting technologies. Significant efforts include amorphous metals, intermetallics, application of MHD in continuous casting of steel, and energy efficient furnace technology. Industrial R&D seems focused more on process improvements than on new product technologies, but significant efforts in new cast materials included cast metal matrix composites, materials substitutions for thinner wall products, and advanced ceramic products for foundry industry applications.

International Nuclear Information System (INIS)

A series of #alpha#-sialon (#alpha#') compositions containing mixed stabilising cations were prepared, by introducing additional CaO to a basic Sm #alpha#-sialon compositions. The thermal stability of these Sm-Ca-containing #alpha#-sialon phases was investigated using XRD, SEM and EDXS techniques. It was found that the addition of calcium into the Sm #alpha#-sialon systems greatly improved the stability of the #alpha#-sialon phases. Calcium was found to be incorporated into the #alpha#-sialon structure, coexistent with the samarium, and partitioning of the calcium and samarium was observed between the #alpha#' phase and grain boundary phases. This indicates a technique which may be used to improve the thermal stability of the #alpha#' phase while maintaining good refractory phases at the sialon grain boundaries.

International Nuclear Information System (INIS)

A series of cation exchange membranes was produced by impregnating and coating both sides of a quartz web with a Nafion solution (1100 EW, 10%wt in water). Inert filler particles (SiO_2, ZrO_2 or TiO_2; 5-20%wt) were incorporated into the aqueous Nafion solution to produce robust, composite membranes. Ion-exchange capacity/equivalent weight, water take-up, thickness change on hydration and ionic and electrical conductivity were measured in 1 mol dm"-"3 sulfuric acid at 298 K. The TiO_2 filler significantly impacted on these properties, producing higher water take-up and increased conductivity. Such membranes may be beneficial for proton exchange membrane (PEM) fuel cell operation at low humidification. The PEM fuel cell performance of the composite membranes containing SiO_2 fillers was examined in a Ballard Mark 5E unit cell. While the use of composite membranes offers a cost reduction, the unit cell performance was reduced, in practice, due to drying of the ionomer at the cathode.

Energy Technology Data Exchange (ETDEWEB)

In the context of the research project, the physical basis of the direct decoupling of highly concentrated solar radiation in materials without the detour via absorbing heat exchanger walls was examined. Also, the first chemical processes suitable for the effective long-term storage of solar energy were analysed, relevant experiments were carried out and the necessary receiver techniques for high temperature applications were provided. The principle of direct coupling was examined on fluidized beds on the one hand and on cavity receivers, on the other hand. The contribution shows the results achieved in detail. It is recorded that first processes for storing solar energy in chemical reactions were able to be examined. Alkaline earth hydroxides accommodated in ceramic honeycomb structures seem to be possible as stores for medium temperature ranges around 500deg C. Investigations on receiver structure materials are also making progress. Highly transparent, high ...

Energy Technology Data Exchange (ETDEWEB)

Power plants generate a great amount of ash during coal combustion. From this process two different kinds of ashes are extracted: fly ash (FA) and bottom ash (BA). In this work possible use of both fly and bottom ash as raw material for the ceramic industry is analyzed. The samples were formed by mechanical mixing of both kinds of ashes, and density evolution during conformation as structural ceramic (packing, pressing and sintering) was studied. It was verified that powders with larger fly ash content exhibited higher packing density resulting in compacts with improved green and sintered densities. Preheating treatments at temperatures above 600{sup o}C also increased the green and sintered densities. Dilatometric curves on compacts formed from FA and BA powders were run at constant heating rate and at isothermal cycles. From the analysis of these data it can be established that liquid-phase sintering is the densification ...

Wastenet

... 300715+Ceramic+Engineering+and+Science+Proceedings 2122%28Series+Code%29+Ceramic+Engineering+and+Science+Proceedings Wiley::Ceramic Engineering and Science Proceedings WILEY KNOWLEDGE FOR ...CART | MY ACCOUNT | CONTACT US | HELP Home / Engineering & Materials Science / Materials Science / Ceramic Engineering and Science Proceedings Related Subjects Soft Matter Organic Electronics Structural ...Materials, Ceramics Structural Materials, Composites Structural Materials or Construction Materials Corrosion Electronics Materials Related Series Ceramic Transactions Series Wiley Series in Materials for ...Electronic and Optoelectric Applications Ceramic Engineering and Science Proceedings (CESP) contain proceedings from three American Ceramic Society (ACerS) meetings: ...

International Nuclear Information System (INIS)

Large, complex, high purity ceramic shapes are required by a variety of emerging technologies for their electrical insulation and high temperature strength properties coupled with their refractoriness and purity. Ceramic sealant bonding, using crystalline and vitreous sealant materials, has recently shown significant potential for joining technical ceramics to form the required shapes. Materials and techniques for joining technical ceramics including alumina, magnesia, zirconia and thoria are discussed. (orig.).

UK PubMed Central (United Kingdom)

All ceramic fixed partial dentures (FPD)s exhibit enhanced biocompatibility and esthetics as compared to metal-ceramic restorations. However, framework fractures are frequently reported especially when...Full Text Available

Science.gov (United States)

Lecture notes (pdf) on Ceramics is part of a physics course on the properties of matter from the University of Auckland, Department of Chemical and Materials Engineering. The following topics are covered: types of chemical bonding, degree of ionic character, structure of ceramics and crystallography, interstitial sites in different crystal structures, silicate structures, glasses, glass transition temperature, glass viscosity, thermal and mechanical properties of ceramics and glasses, fracture properties of ceramics and processing of ceramic materials. Keywords: ionic bonds; covalent bonds; coordination numbers; thermal shock; grain growth; sintering; green body

Energy Technology Data Exchange (ETDEWEB)

A laboratory model of a TPV generator in the kilowatt range was developed and tested. It was based on methane/oxygen combustion and a spectrally matched selective emitter/collector pair (ytterbia emitter-silicon PV cell). The system demonstrated a power output of 2.4 kilowatts at an overall efficiency of 4.5{percent} without recuperation of heat from the exhaust gases. Key aspects of the effort include: (1) process development and fabrication of mechanically strong selective emitter ceramic textile materials; (2) design of a stirred reactor emitter/burner capable of handling up to 175,000 Btu/hr fuel flows; (3) support to the developer of the production silicon concentrator cells capable of withstanding TPV environments; (4) assessing the apparent temperature exponent of selective emitters; and (5) determining that the remaining generator efficiency improvements are readily defined combustion engineering problems that do not necessitate ...

International Nuclear Information System (INIS)

In the Japan Research Reactor-II (JRR-2), the main source of _4_1Ar generation is the exhaust air from the horizontal experimental holes and the pneumatic tubes. For the horizontal experimental holes, the flow of exhaust air through the holes was decreased by improving the airtightness, and a decay duct of capacity 2.4 m_3 was installed in the middle of the exhaust line. In consequence, the release rate of _4_1Ar was reduced by 6-8%. For the pneumatic tubes, a mechanical shutter was installed in the tube. The shutter stops the exhaust air flow, except when the pneumatic tube is used. Prior to the use, the activated air in the tube is led to a decay tank. As a result, the _4_1Ar release rate was reduced by 10-20%. By the above means, the yearly exposure at the site boundary was reduced to 0.36 mR from 2.6 mR. In Hot Laboratory for metallurgical examination of spent fuel, the exhaust filtration system consists of filters in the cave, i.e. frame trap, prefilter, HEPA ...

Science.gov (United States)

International Patenting Trends in Advanced Materials: Ceramics (June 18, 1999) This report is the ... manufacturing, biotechnology, and advanced materials. Hypertext Format Portable Document Format ...

Energy Technology Data Exchange (ETDEWEB)

The diesel engine is the most efficient device for converting chemical energy stored in liquid hydrocarbon fuels into useful work. Up to 50% of the energy in the fuel is converted into output shaft work. The modern diesel engine is twice as efficient as the early diesel engines and produces as much as sixty times as much power for a given cylinder size. These developments have, in recent years, been accompanied by a substantial reduction in the noxious elements in the exhaust gas so that engines are now, relatively speaking, ecologically clean. The developments have centred around exhaust gas turbocharging and improved fuel injection systems, but recent work on low-heat-rejection engines has resulted in significant advances in structural ceramics and in high-temperature lubricating oil, as well as an enhanced understanding of heat transfer in high-temperature combustion chambers. (author).

Energy Technology Data Exchange (ETDEWEB)

The purpose of this project was to develop improved dynamic failure models for brittle materials (primarily ceramics). The approach to developing these failure models was to establish a database (ACERAM) in which fundamental material properties and processing information could be directly correlated with ballistic performance data. Under this contract, a comprehensive literature search was conducted, many contacts were established in the armor/anti-armor research and development community, and database development was undertaken. A more limited project was also undertaken to assess and compare the effects of material properties and penetration mechanisms on the ballistic performance of depleted uranium and tungsten alloy penetrators.

International Nuclear Information System (INIS)

In the present study, surfaces of cylinder head, piston, exhaust and inlet valve of a four-stroke, direct injection, single cylinder diesel engine were coated with molybdenum (Mo) by plasma spray method. Thus, thermal barrier characteristic was brought to these parts. Variances in performance and emission values of cotton methyl ester and 2D fuel mixtures were studied in the ceramic coated and uncoated engines under the same running conditions. Performance (6.0% for specific fuel consumption) and emission values (up to 18.0% for CO, 8.0% for smoke density) of the test fuel were improved in the coated engine compared with the uncoated engine. NO_x increase (4.5%) with the increased temperatures expected in the coated engine.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

The production, principal applications, characteristics and properties, advantages of the gas natural is showed. A sectorial overview of the ceramic industry and the utilization of the natural gas in the ceramic industry is presented. The expectations are systematized and the impact of the natural gas utilization in the ceramic industry is evaluated. Some conclusions are withdrawn and recommendations suggested.

International Nuclear Information System (INIS)

Short communication.

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

This paper contains literature from American Power Conference Air Toxics Being Measured Accurately, Controlled Effectively NO{sub x} and SO{sub 2} Emissions Reduced; Surface Condensers Improve Heat Rate; Usable Fuel from Municipal Solid Waste; Cofiring Technology Reduces Gas Turbine Emissions; Trainable, Rugged Microsensor Identifies of Gases; High-Tc Superconductors Fabricated; High-Temperature Superconducting Current Leads; Vitrification of Low-Level Radioactive and Mixed Wastes; Characterization, Demolition, and Disposal of Contaminated Structures; On-Line Plant Diagnostics and Management; Sulfide Ceramic Materials for Improved Batteries; Flywheel Provides Efficient Energy Storage; Battery Systems for Electric Vehicles; Polymer-Electrolyte Fuel Cells for Transportation; Solid-Oxide Fuel Cells for Transportation; Surface Acoustic Wave Sensor Monitors Emissions in Real-Time; Advance Alternative-Fueled Automotive ...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Porcelain fracture associated with an implant-supported, metal ceramic crown or fixed partial denture occurs at a higher rate than in tooth-supported restorations, according to the literature. Implant-specific and patient-specific causes of ceramic failure have not been fully evaluated. Purpose The purpose of this retrospective study was to evaluate the potential statistical predictors for porcelain fracture of implant-supported, metal ceramic restorations. Material and Methods Over a 6-month period, a consecutive series of patients having previously received implant-supported, metal ceramic fixed restorations were examined during periodic recall appointments. The number of supporting implants, number of dental units, type of restoration, date of prosthesis insertion, ...

Energy Technology Data Exchange (ETDEWEB)

In this, the last of a series of three papers, we discuss a method of forming iron phosphate ceramics by a reduction process. We report the formation of iron oxide ceramics by reducing hematite with iron in a phosphoric acid solution. The reaction results in a rapid-setting ceramic (at room temperature) with a compressive strength of 3700 psi and a density of 1.7 g/cm{sup 3}. Although the exact mineral form of the binder is difficult to determine because it is mostly amorphous and hence is not amenable to X-ray diffraction analyses, this material is expected to consist of iron hydrophosphates. The reduction process is very useful in recycling several industrial wastes that are rich in hematite, including iron mine tailings, red mud (a caustic waste from the alumina industry), and machining swarfs. Formation of ceramics with red mud and swarfs is also discussed.

International Nuclear Information System (INIS)

A combined application of several microtechniques is presented and discussed with the Ti/TiO_2 and Zr/ZrO_2-systems as an example. All measurements were carried out on single grains of technical materials in order to detect and quantify the effect of substrate microstructure on the properties of anodic passive films formed potentiodynamically in 0.5 M H_2SO_4 (dU/dt = 20 mVs"-"1). Anisotropy-micro-ellipsometry (AME) was employed to determine the crystallographic orientation of the substrate grains along with passive film thickness and crystallinity in dependence on the anodization potential. Both the isotropic (amorphous) TiO_2- and the anisotropic (crystalline) ZrO_2-films exhibit a systematic dependence of film thickness on the grain orientation. Local LASER-scanning photocurrent measurements (#lambda#=257 nm) on the same grains likewise show a heterogeneity of the photoelectrochemical reactivity in all cases. This is quantitatively explained by the results from local electrochemical ...

Energy Technology Data Exchange (ETDEWEB)

Chemical looping combustion (CLC) of simulated coal-derived synthesis gas was conducted with NiO oxygen carriers supported on SiO2, ZrO2, TiO2, and sepiolite. The effect of H2S on the performance of these samples for the CLC process was also evaluated. Five-cycle thermogravimetric analysis (TGA) tests at 800 C indicated that all oxygen carriers had a stable performance at 800 C, except NiO/SiO2. Full reduction/oxidation reactions of the oxygen carrier were obtained during the five-cycle test. It was found that support had a significant effect on reaction performance of NiO both in reduction and oxidation rates. The reduction reaction was significantly faster than the oxidation reaction for all oxygen carriers, while the oxidation reaction is fairly slow due to oxygen diffusion on NiO layers. The reaction profile was greatly affected by the presence of H2S, but there was no effect on the capacity due to the presence of H2S in synthesis gas. The presence of H2S decreased reduction ...

Energy Technology Data Exchange (ETDEWEB)

The Co-doped BaTiO{sub 3} nanosized powders and ceramics were prepared via the sol-gel process. The powders and ceramics were characterized by methods of XRD, SEM and TEM. The dielectric properties of the ceramics were also determined by these methods. The influence of sintering temperature, sintering time and Co concentration on the microstructure and dielectric properties was discussed. The results revealed that the powders were in nanometer scale (30-50 nm) and were mainly composed of cubic BaTiO{sub 3} phase and small amount of BaCO{sub 3}. After sintering, both the cubic BaTiO{sub 3} and BaCO{sub 3} were transformed into tetrahedron BaTiO{sub 3}. The sintering temperatures of the Co-doped BaTiO{sub 3} ceramics decreased (about 100 deg. C) and the Curie temperatures of the ceramics were then moved to lower temperature. In addition, the dielectric constant of the ...

Energy Technology Data Exchange (ETDEWEB)

In order to design the microstructure of ceramics with desired dielectric property, an estimation method of dielectric constant of ceramics taking into account the characteristics of microstructure of the ceramics is proposed. In the estimation model, the microstructure of ceramics is represented by the assembly of unit cells comprising of grain, pore and grain boundary. The sizes of grain and pore and the thickness of grain boundary in each unit cell were determined exactly according to their size and thickness distributions in a real ceramic. The dielectric constant of the assembly can be calculated on the basis of equivalent circuit theory. The estimated values of dielectric constant of ceramic BaTiO{sub 3} using the proposed estimation method agree well with experimental ones. The dependence of characteristics of microstructure on the dielectric constant was ...

Science.gov (United States)

... Accession Number : ADA539462. Title : 6.5 kW, Yb:YAG Ceramic Thin Disk Laser. Descriptive Note : Technical note 1 Jan-1 Dec 2010. ...

Energy Technology Data Exchange (ETDEWEB)

Today, as a result of increase in oil prices, limited fossil fuel resources, environmental consideration and global warming, the methyl ester fuels have been focused on alternative fuels. Methyl ester fuels can be used more efficiently in low heat rejection engines (LHR), in which the temperature of combustion chamber is increased by creating a thermal barrier. In this study, the piston, cylinder head, exhaust and inlet valves of a diesel engine were coated with the ceramic material Al{sub 2}O{sub 3}-TiO{sub 2} by the plasma spray method. Thus, a thermal barrier was provided for the parts of the combustion chamber with these coatings. The effects of corn oil methyl ester that produced by the transesterification method, and No. D2 fuels' performance and exhaust emissions' rate were studied by using equal in every respect coated and uncoated engines. Tests were performed on the uncoated engine, and then repeated on the coated engine and the results ...

International Nuclear Information System (INIS)

A schematic diagram shows the various processing steps to be performed during feed preparation in the Hanford Waste Vitrification Plant (HWVP). The pretreated NCAW is transferred to the slurry receipt adjustment tank (SRAT) in the HWVP for concentration. Water removed during boildown is collected in the slurry mix evaporator condensate tank (SMECT). After waste treatment the water is returned to the storage tanks for eventual disposal. The pretreated Neutralized Current Acid Waste (NCAW) is concentrated in the SRAT to approximately 125 g waste oxides/ liter. Formic acid is then added at a controlled rate to improve rheological properties and achieve a required reduction/oxidation state. Reflux boiling is initiated and continued for several hours. The concentrated slurry is cooled and pumped to the slurry mix evaporator (SME). In the SME, glass frit is added, and the slurry is further concentrated to achieve a nominal composition of 500 g total oxides/liter. This ...

International Science & Technology Center (ISTC)

Development of SHS-technologies for SiC, Si3N4 and Ceramic Composites on Their Basis from Rocks

International Nuclear Information System (INIS)

English Mar 1999 [vp.] United Kingdom Jumali, MHH Warwick Univ.,

Science.gov (United States)

... 1 ..... 14 High Dielectric Constant Ceramics for Use in Blumlein Transmission Lines ..... 14 ...

Medline Plus

... energy. It consists of a stack of piezoelectric ceramics sandwiched under high pressure between two metal cylinders. ...

CERN Document Server

Proposal for the SC Improvement

Energy Technology Data Exchange (ETDEWEB)

The addition of titanium to eutectic braze compositions causes these alloys to readily wet and bond to A1N ceramics. Electron microscopic characterizations of the metal-ceramic interfaces reveal the presence of TiN, along with other Ti- and Al-containing phases. The formation of such interfacial reaction products is an additional thermodynamic driving force for the creation of useful metal-ceramic bonds. 12 refs., 4 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

The ceramic composite armor has been lucubrated in the past 40 years. Ceramic can provide the same protection as metal, but it has lighter weight than metal. Ceramic has excellent ability of resisting kinetic energy projectile, because it can transfer energy to a large range by its fragmented cone and has higher ability of eroding the projectile than metal. But the researches indicated the full potential of the ceramic hard face has not been achieved because the significant interface between ceramic and metal has the unfavorable impedance effects and would induce tensile failure. FGM is a new type composite with continuous transition from ceramic to metal; it has no significant discrete materials interfaces between ceramic and metal. This paper deals with the impact response of Ceramic/FGM/Metal armor by numerical and ...

Energy Technology Data Exchange (ETDEWEB)

The development and experimental demonstration of a high-temperature seal for the SHARE ceramic dome cavity receiver is reported. The mechanical contact seal which was tested on one-foot-diameter silicon-carbide ceramic-dome hardware at pressure differentials to four atmospheres and dome temperatures to 2200/sup 0/F (1200/sup 0/C) showed negligible leakage at expected receiver operating conditions. Potential solar receiver applications for the technology are illustrated.

Science.gov (United States)

"Precision manufacture of ceramic parts with CNC machining capability for aerospace, lasers, semiconductors and other industries. Materials include alumina, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite and others. A.C.T. has seen the number of applications and demand for high-realiability ceramics (aluminum oxide, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite, etc...) increase continually within the aerospace, computer and the industrial markets."

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Computer-aided design/computer-aided manufacturing (CAD/CAM) titanium ceramic restorations were developed with the potential for replacing expensive, high noble metal ceramic restorations. However, there is a lack of information about the clinical performance of CAD/CAM titanium ceramic single crowns. Purpose The purpose of this study was to evaluate CAD/CAM titanium ceramic single crowns after 3 years in function. Material and methods A total of 41 crowns were fabricated for 21 patients. The titanium copings were CAD/CAM milled (Everest CAD/CAM system) with an even thickness of 0.5 mm, and low-fusing veneering porcelain (Vita Titanium Porcelain) was added incrementally. The crowns were cemented using zinc phosphate cement after confirming that there were no mechanical...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Although the esthetic outcome of a collarless metal ceramic restoration is superior to that of a restoration with a metal margin, its mechanical strength has not been evaluated. Purpose The purpose of this study was to evaluate and compare the fracture resistance of metal ceramic restorations with metal margins to that of metal ceramic restorations with circumferential porcelain margins, after exposure to masticatory simulation. Material and methods Twenty-four metal ceramic restorations were fabricated and paired with 24 cobalt-chrome tooth analogs. Twelve of the specimens had metal margins, while the remainder had circumferential porcelain margins. The restorations were cemented on the metal tooth analogs with a resin-modified glass ionomer luting agent (FujiCEM). Al...

International Nuclear Information System (INIS)

Interest in making complex net-shape ceramic parts with good surface finishing and sharp tolerances without machining is a driving force for studying the injection molding technique. This method consists of softhening the ceramic material by means of adding some plastic and heating in order to inject the mixture under pressure into a relatively cold mold where solidification takes place. Essentially, it is the same process used in thermoplastic industry but, in the present case, the ceramic powder load ranges between 80 to 90 wt.%. This work shows results obtained from the fabrication of pieces of different ceramic materials (alumina, barium titanate ferrites, etc.) in a small scale, using equipments developed and constructed in the laboratory. (Author).

Energy Technology Data Exchange (ETDEWEB)

Three phosphate based ceramics were studied for the immobilization of tri- and tetravalent actinides: britholites Ca{sub 9}Nd{sub 1-x}An{sub x} {sup IV}(PO{sub 4}){sub 5-x}(SiO{sub 4}){sub 1+x}F{sub 2}, monazites/brabantites Ln{sub 1-2x}{sup III}Ca{sub x}An{sub x}{sup IV}PO{sub 4} and Thorium Phosphate Diphosphate (TPD) Th{sub 4-x}An{sub x}{sup IV}(PO{sub 4}){sub 4}P{sub 2}O{sub 7}. For each material, the incorporation of Th, U(IV), or Ce(IV) in the structure was examined. This work was the early beginning of the incorporation of {sup 239}Pu and/or {sup 238}Pu in order to evaluate the effects of {alpha} -decay on these three crystallographic structures. The syntheses were carried out using dry chemistry methods, involving mechanical grinding then heating treatment (1100 deg C {<=} {theta} {<=} 1400 deg C). For britholites, we showed that the incorporation of thorium was complete for weight loading lower than 20 wt.% through the (Nd{sup 3+}, PO{sub ...

Energy Technology Data Exchange (ETDEWEB)

The methodology of achieving a high power density (HPD, or brake mean effective pressure) direct-injection Diesel engine has been studied, which is directed to using high fuel/air ratio, high-speed and ceramic engine components. Among the main thrust to achieve these engine changes for an advanced Diesel engine is the design of a high injection pressure (HIP) fuel system. During the course of the present study, two Cummins 903 engines mated with a Rutger-built HIP were employed to investigate the engine response to HIP and in-cylinder processes by using the Rutgers high-speed infrared (IR) spectral digital imaging system. Five separate technical publications were prepared to report results obtained from the study. The main findings include: The HIP system permits engine operation at an air/fuel ratio of as rich as 18 to 1 with smoke emission not worse than with the conventional mechanical (low pressure) injection system; A high injection pressure ...

Energy Technology Data Exchange (ETDEWEB)

The industrial policy of fine ceramics which is one of the new material expected to solve energy/environmental problem, is described. Fine ceramics are possessed with the characteristics like surpassing electromagnetic properties, heat resistance, high strength, etc. and its use as highly efficient power generation plant material, functional material for various sensors/electronic, and activation of existing industries are cited. As for the reclamation of global environment, promotion of saving energy in a global scale, development of innovative environmental technology and increase of carbon dioxide absorption source are described. Furthermore, research and development work in Japan on global environmental industrial technology for 1992 to 1993, new sunshine project and technical developments relating to fine ceramics are explained. As for the results of research and development, the results from the case study of 300kw ...

International Nuclear Information System (INIS)

Study results on long-term thermal and corrosion resistance of packs with electro-insulation layer of aluminium nitride are presented. Structural changes of nitride ceramics and contact zones between metal and ceramics are considered. It is shown that multilayer metallo-ceramic packs, manufactured by gas-phase technology have high electro- and thermophysical properties, high thermal and corrosion resistance relative to cesium vapor, vacuum density as well as high thermo-resistance. 8 refs., 4 figs.

International Nuclear Information System (INIS)

Technologic regimes of cryomotor rotor fabrication are determined. Blanks of yttrium ceramics powder are molded hydrostatically at 400-600 MPa. To confirm the serviceability of electric machines of the considered, a hysteretic 10 W power electric motor with the following dimensions of HTSC-ceramics rotor: external diameter - 56 mm; internal diameter - 45 mm, height - 60 mm, is developed and tested in the liquid nitrogen medium. 8 refs.; 8 figs.; 1 tab.

International Nuclear Information System (INIS)

Monolithic SiAlON ceramics are hard and brittle with little possibility for property design, but multi-phase SiAlON ceramics offer great scope for controlling microstructural development and desired properties. The ceramics can also be reinforced by separate additions of other hard, refractory compounds. The toughness in all these SiAlON composites can be increased by several mechanisms, and the best effect is reached if they are combined. When glassy phase is present, crack paths are affected by the strains caused by different thermal expansion of the glassy phase and the crystals and also by the interface properties. The crystal shape influence toughness, especially pronounced is the effect of the elongated #beta#- grains. Different toughening mechanisms are achieved by separately added reinforcement phases. The hardness is raised by the presence of #alpha# SiAlON and other hard constituents, such as SiC. (orig.).

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

In the present study, element interdiffusions at the cofired interface of 9/1 Ag/Pd electrode and lead magnesium niobate (PMN)-based ferroelectrics were investigated using Auger Electron Spectroscopy (AES). Intense interdiffusions at the interface were observed while Ag and Pd could penetrate into the ceramics for about 1 {mu}m. Ag-doping experiments were carried out to further study the effects of Ag diffusion on electrical properties of the ceramics. The results showed that Ag could be incorporated into solid solution of the ceramics as Ag{sup +}. As a whole, the Curie temperature (Tc) and dielectric constant of the ceramics decreased with Ag addition. However, Ag addition had no obvious effect on the insulation resistivity. The results inferred that Ag{sup +} could substitute for Pb{sup 2+} at A site of ABO{sub 3} lattice, thereby oxygen vacancies were generated.

International Nuclear Information System (INIS)

English 2004 2 p. Brazil Rocha, RM Centro Tecnico Aeroespacial (CTA),

Science.gov (United States)

... Problem: At a glass ceramic cooktop plant, workers manually lift uncut plates of glass onto a waist-high conveyor belt, where it is then stacked ...

International Nuclear Information System (INIS)

... structure crystal-phase transformations fluorescence fluorescence spectroscopy

Energy Technology Data Exchange (ETDEWEB)

The performance of advanced ceramics under cavitation loading in distilled water was studied by using a laboratory test with vibration-induced cavitation following the pattern of the ASTM standard G32-92. The hardened and tempered martensitic steel 100Cr6 was used as a reference. The aim was to identify mechanisms and the effects of important microstructural parameters on damage of polished Al{sub 2}O{sub 3}, Al{sub 2}O{sub 3}-ZrO{sub 2}, ZrO{sub 2} and SiC ceramics. Results showed that surface damage of brittle ceramics was mainly dominated by intergranular fracture, followed by detachment of single grains or fragments of them. Both incubation time and erosion rate were affected by the amount of initial surface cavities, grain sizes and secondary phases at grain boundaries. (orig.)

International Nuclear Information System (INIS)

(#alpha#+#beta#)-SiALON ceramic composites are industrially important materials. Due to their unique chemistry, crystal structure and microstructural features, #alpha#-SiAlON has superior hardness while #beta#-SiALON offers high strength and toughness. The combination of the two phases enables materials engineers to design a ceramic where the physical properties of the composite can be tailored to a particular application. This article presents a general review of the crystal structures, fabrication and properties of the (#alpha#+#beta#)-SiALON composites with special highlights outlining how microstructural tailoring can control the properties of these advanced ceramic alloys. Copyright (1997) Institute of Metals and Materials Australasia Ltd.

Energy Technology Data Exchange (ETDEWEB)

The diffusion of alkali vapours in the anode compartment of a DIR-MCFC produces the deactivation of the internal reforming catalyst. Sets of ceramic porous membranes purposed to limit the diffusion have been manufactured by different techniques and the influence of the preparation technique and of the preparative variables on the morphological characteristics of the membranes structures has been studied.

Energy Technology Data Exchange (ETDEWEB)

The peculiarities of pulsed laser melting and evaporation of the superconducting ceramics are analyzed by means of numerical simulation. The appearance of the overheated metastable states in solid and liquid phases is shown as a result of the phase front dynamics and volume nature of laser energy release. A method of dynamic adaptation for the multifront Stefan problem is proposed.

Energy Technology Data Exchange (ETDEWEB)

According to the present invention, a joined product is at least two ceramic parts, specifically bi-element carbide parts with a bond joint therebetween, wherein the bond joint has a metal silicon phase. The bi-element carbide refers to compounds of MC, M.sub.2 C, M.sub.4 C and combinations thereof, where M is a first element and C is carbon. The metal silicon phase may be a metal silicon carbide ternary phase, or a metal silicide.

Science.gov (United States)

A new dual focal point electro-optic lens that is switchable to focusing and unfocusing is proposed and successfully demonstrated. This electro-optic lens is constructed by coating transparent fine electrodes in the Fresnel-zone plate onto a PLZT ceramic plate. Its focal length changes from 1.25 m to infinity binary at 515 nm with the external voltage of 210 V. PMID:20725208

Energy Technology Data Exchange (ETDEWEB)

This document contains a listing of the written scientific information originating in the Materials Joining Group (formerly the Welding and Brazing Group), Metals and Ceramics Division, Oak Ridge National Laboratory during 1951 through June 1987. It is a registry of about 400 documents as nearly as possible in the order in which they were issued.

Energy Technology Data Exchange (ETDEWEB)

In this study, the corrosion behavior of commercially pure titanium (c.p. Ti), Ti-6Al-4V and five new experimental Ti-Cr alloys was evaluated through open-circuit potential (OCP) and potentiodynamic polarization measurement in an artificial saliva containing fluoride. Electron spectroscopy for chemical analysis (ESCA) was used to characterize the composition of the passive films on the alloy after potentiodynamic polarization measurement. It was found that in standard artificial saliva the OCP increases with higher Cr content in Ti-Cr alloys. In 0.5% NaF artificial saliva, the OCP decreases with decreasing Cr in Ti-Cr alloys, and all but Ti-5Cr remain consistently higher than those of c.p Ti and Ti-6Al-4V. Linear polarization results show that artificial saliva and artificial saliva containing 0.5% NaF result in different corrosion behavior in Ti-Cr alloys, c.p.Ti and Ti-6Al-4V. The Ti-Cr alloys had greater resistance to corrosion in the fluoride-containing artificial saliva than c.p. ...

Energy Technology Data Exchange (ETDEWEB)

There are a number of characteristics exhibited by ceramic materials that may provide potential benefits for the reciprocating internal combustion engine. However, the brittle nature of these materials together with a variability in strength has created difficulties in applying ceramic materials to the engine environment. Although a wide range of physical properties is available from contemporary ceramic materials, a material offering consistently high strength has yet to be developed. For sliding-contact applications, desirable characteristics include good wear resistance, low friction, ability to join metals and good heat dissipation. Test results have shown that cam/follower components with cast iron cam sliding on a silicon nitride follower exhibit very low wear rates. The application of silicon carbide to face seals has also shown substantial reductions in both friction and wear when compared with conventional ...

International Nuclear Information System (INIS)

This study presents the findings of radiometric analysis carried out to determine the activity concentrations of natural radionuclides in raw materials (clay, kaolin, quartz, feldspar, dolomite, alumina, bauxite, zirconium minerals, red mud and frit) and end products (glazed ceramic wall and floor tiles) in the Turkish ceramics industry. Hundred forty-six samples were obtained from various manufacturers and suppliers throughout the country and analyzed using gamma-ray spectrometer with HPGe detectors. Radiological parameters such as radium equivalent activity, activity concentration index and alpha index were calculated to assess the radiological aspects of the use of the ceramic end products as decorative or covering materials in construction sector. Results obtained were examined in the light of the relevant national and international legislation and guidance and compared with the results of similar studies reported in ...

Science.gov (United States)

The kinetics of electrical breakdown of thin (15-70 ?m) layers of polymers and ceramics in a constant-sign field at 77-480 K has been investigated. The temperature dependences of the longevity (breakdown waiting time) of both dielectrics have been found to be similar to each other. At elevated temperatures, the longevity of the dielectrics varies exponentially with increasing temperature, and at reduced temperatures, it is temperature-independent (there is an athermal plateau). The mechanisms of elementary events controlling the process of preparation of the dielectrics for breakdown at elevated and reduced temperatures are the thermal-fluctuation over-barrier electron transition from trap to trap and the tunneling (under-barrier) transition, respectively. The hopping electron transport in the field direction gives rise to critical space charges causing breakdown of the dielectrics. The transition barrier heights (trap depths) have been determined. The ...

British Library Electronic Table of Contents (United Kingdom)

A type of Si3N4-based nanocomposites ceramic cutting tool material was prepared by the addition of nano-scale Si3N4W whisker and nano-scale TiN particle. Cutting performance of the Si3N4/Si3N4W/TiN nanocomposite ceramic tool in machining of cast iron was investigated in comparison with a commercial sialon ceramic tool, and the tool wear mechanism was studied. The two types of cutting tools have similar cutting performance at relatively low cutting parameters, while Si3N4/Si3N4W/TiN nanocomposite tool exhibits a better wear resistance than sialon tool at the relatively high cutting parameters. The wear of sialon ceramic cutting tool is dominated by the plastic deformation, abrasive action, microcracking, pullout of grains and chemical action at the higher cutting parameters. The higher mech...

Energy Technology Data Exchange (ETDEWEB)

This work reports an alternative methodology for the linear attenuation coefficient determination ({mu} {rho}) of irregular form samples, in such a way that is not necessary to consider the sample thickness. With this methodology, indigenous archaeological ceramics fragments from the region of Londrina, north of Parana, were studied. These ceramics fragments belong to the Kaingaing and Tupiguarani traditions. The equation for the {mu} {rho} determination employing the two mean method was obtained and it was used for {mu} {rho} determination by the gamma ray beam attenuation if immersed ceramics, by turns, in two different means with known linear attenuation coefficient. By the other side, {mu} theoretical value was determined with the XCOM computer code. This code uses as input the ceramics chemistry composition and provides an energy versus mass attenuation coefficient table. In order to validate the ...

International Nuclear Information System (INIS)

Experimental results of compatibility tests on ceramics-metal bonded structures performed under high heat flux conditions in splash test apparatus are reported. Emphasis is placed on results of the channel wall design and its critical operating conditions under MHD environment. The module design of one cold type and three semihot type insulators have been tested. These materials were Al_2O_3, Al_2MgO_4, LaAlO_4, MgO and Sialon ceramics. The methods of cold type ceramics-metal bonding structure were studied on Al_2O_3 and Spinel spray coating technology. The refractory metallizing and ceramics-metal graded structure manufactured by HIP technologies were applied to bonding between the MgO or LaAlO_4 and metallic cooling system. The Sialon non-bonding structure was tested with mechanical supported cooling system by shrinc fitting method. The results indicated that the bonding structures made of the ...

British Library Electronic Table of Contents (United Kingdom)

Glass ceramics are commonly used as sealing materials for planar solid oxide fuel cells (SOFCs). The major requirements of stack and module builders for these materials are the stability of the coefficient of thermal expansion (CTE), excellent bonding (sticking) behaviour and the absence of volatile ingredients, which can lead to changes of the material properties and the sealing ability. SCHOTT Electronic Packaging has developed special glasses and glass-ceramics for various solid oxide fuel cell designs and operating temperatures. The glass compositions are based on the system MgO-Al2O3-BaO-SiO2-B2O3. In this study the evaluation of the developed materials was done by high temperature aging tests for up to 1000h, high temperature XRD-studies and Rietveld calculations, combined with scann...

Energy Technology Data Exchange (ETDEWEB)

The small pilot facility of a cyclone type suspension incineration system of radioactive waste was set up in order to evaluate the decontamination efficiency of a high efficiency ceramic filter. The evaluation was made by use of /sup 54/Mn, /sup 59/Fe, /sup 60/Co, /sup 65/Zn and /sup 137/Cs. 1. The decontamination factor by one line of ceramic filter for every species were over 10/sup 5/. 2. The decontamination factor increased by one oder when water vapor exists in off-gas. The same tendency was also observed when iron dioxide existed at the incineration of cation exchange resin.

International Nuclear Information System (INIS)

The use of Sialon ceramics has been restricted by the high temperature required for synthesis and the expense of the pure oxide and nitride raw materials required. For refractory applications the purity required is less demanding and it has been possible to exploit the outstanding durability of the Sialons at moderate cost. New low cost manufacturing routes are being developed by nitriding silicon metal powder at relatively low temperature with clay and various additives depending on the Sialon required. For example the introduction of carbon or fine silicon carbide allows the preparation of beta Sialons and alpha Sialons which can be stabilised by including the appropriate cations. A wide range of composite Sialon bodies with diverse properties can be prepared by a one step process. Current projects developing the synthesis routes are aimed, in the first instance, at refractory manufacture but are showing promise for more sophisticated applications. Copyright ...

Energy Technology Data Exchange (ETDEWEB)

Sintered glass-ceramics have been produced using municipal incinerator solid residues and glass cullet or an inert waste, from feldspars processing, as sintering aids. The capability of three different mixtures, either previously vitrified or not, to be sintered was investigated by means of linear shrinkage, water absorption and bulk density measurements, and by X-ray diffraction analysis and scanning electron microscopy observations. Particular attention has been addressed to the study of particle size effect on the sintering process. The conclusions that can be drawn from the experimental study are that the preliminary vitrification step is essential in order to obtain a dense sintered glass-ceramic product in the 850-1050 C temperature range developing silicate crystalline phases. The optimal powder particle size that confers a good densification degree was found to be < 45 {mu}m. (orig.)

International Nuclear Information System (INIS)

BaTi_0_._9(Ni_1_/_2W_1_/_2)_0_._1O_3 ceramics were fabricated and their dielectric properties were investigated. With the sintering temperature increasing from 1250 to 1280 deg. C, the grain size abruptly increases from 1-2 to 20-40 #mu#m, accompanying significant changes in dielectric response. The samples with larger grains exhibit giant dielectric constant characteristics, which are considered to be mainly attributed to the domain boundary effect. The activation energies of the dielectric relaxation E_r_e_l_a_x=0.325 eV reveal the existence of microdomains in larger grains. The ac conductivity results also give the evidence of the domain boundary effect in the present ceramics.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Even though metal ceramic restorations (MCRs) are widely used by clinicians, the influence of the metal on the color of overlaying porcelain is unknown. Purpose The purpose of this study was to analyze the color alterations of different types of metal ceramic alloys during several stages of metal surface preparation and to determine the effect of those changes on the resulting color of opaque porcelain (OP). Material and Methods Seven different types of alloys (3 base metal, 3 noble, and 1 high noble) were used to prepare disk-shaped specimens (1 mm x 10 mm, n=3), followed by OP application (0.1 mm). Lab values of specimens were recorded after different stages of metal surface preparation (ingot, after casting, after oxidation, and after the OP application) in addition...

Energy Technology Data Exchange (ETDEWEB)

The properties of cast basalt and alumina are examined. The ways in which these materials have been used in applications in coal preparation plants, for example in bunker and pipe linings where abrasion and corrosion resistant materials are required, are discussed.

International Nuclear Information System (INIS)

Sodium silicate is vacuum impregnated in bauxite waste (red mud) at room temperature to develop ceramics of mechanical properties comparable to the sintered ceramics. For a concentration up to 10% the fracture toughness increases from 0.12 MNm"-"3"/"2 to 0.9 MNm"-"3"/"2, and the compressive strength from 7 MNm"-"2 to 30 MNm"-"2. The mechanical properties do not deteriorate, when soaked in water for an entire week. The viscosity and the concentration of the silicate solution are crucial, both for the success of the fabrication and the economics of the process. Similar successful results have been obtained for bauxite and lime stone, even though the latter has poor weathering properties. With scanning electron microscopy and energy dispersive analysis, an attempt is made to identify the crystals formed in the composite, which are responsible for the strength. The process is an economic alternative to the sintered ceramics in ...

Energy Technology Data Exchange (ETDEWEB)

Sandia National Laboratories is currently involved in the optimization of a Plane Shock Generator Explosive Lens (PSGEL). The PSGEL component consists of a detonator, explosive, brass cone and tamper housing. The purpose of the PSGEL component is to transmit a plane shock wave through the 4340 steel bulkhead (wave separator) which has a ferro-electric (PZT)ceramic disk attached to the opposite surface of the steel bulkhead. The planar shock wave depolarizes the PZT 65/35 ferro-electric ceramic to produce an electrical output. One aspect of the optimization program involves the possible replacement of 4340 steel with PH13-8Mo steel for the bulkhead. These materials, as well as the PZT 65/35 ferro-electric ceramic and the brass for the cone, required the stock characterization with respect to Hugoniot parameters. The work presented here gives the shock Hugoniot values for these four materials and documents their measurements.

International Nuclear Information System (INIS)

A powder mixture of #alpha#-Si_3N_4, Al_2O_3, and TiO_2 was hot-pressed using different sintering cycles to search for an optimum in situ formed #beta#-O-sialon-TiN composite. The impulse excitation technique (IET), high-temperature X-ray diffraction (HTXRD), and scanning electron microscopy (SEM) were used to investigate the microstructure. Below the temperature of 1300 deg. C, the high-temperature internal friction (Q "-"1) decreases with the increase of sintering temperature, whereas the density of the material increases with the increase of sintering temperature. At a sintering temperature higher than 1850 deg. C, the ceramic could not be densified and O-sialon was not formed. Also, the mechanical properties of ceramics hot-pressed using different sintering cycles were assessed. The ceramic hot-pressed at 1700 deg. C for 10 min displays a combination of high hardness and good fracture toughness, due to an optimum ...

Science.gov (United States)

... Structures 9623595 P EPSCOR ENG DMI MATERIALS PROCESSING & MANUFCT Textile Engineering Department AL ... MPS DMR METALS, CERAMICS AND ELECT MATRS Materials and Mechanical Engineering AL Auburn University ...

Energy Technology Data Exchange (ETDEWEB)

This work has been undertaken with a view to study the effect of lanthanum content on properties of PLZT ceramics. The polycrystalline complex compounds of PLZT with Pb{sub 1-x}La{sub x}(Zr{sub 0.40}Ti{sub 0.60}){sub 1-x/4}O{sub 3}, +10% PbO formula were prepared from the nano-size individual oxides powders by hot-pressed process. Transparent PLZT (x/40/60) bulk ceramics with pure tetragonal phase was obtained. The studies of the microstructures, dielectric and ferroelectric properties of the ceramics were carried out. The experiment results showed that when La content increased from 7 to 13 mol.%, the grain size increased from 2 to 7 {mu}m. La content also effects the dielectric property obviously, the dielectric constant increased with La content increasing. Moreover, the ferroelectric properties are sensitive to the variation of La content.

Energy Technology Data Exchange (ETDEWEB)

A room-temperature process for stabilizing mineral waste streams has been developed, based on acid-base reaction between MgO and H3PO4 or acid phosphate solution. The resulting waste form sets into a hard ceramic in a few hours. In this way, various alumina industry wastes, such as red mud and treated potliner waste, can be solidified into ceramics which can be used as structural materials in waste management and construction industry. Red mud ceramics made by this process were low-porosity materials ({approx}2 vol%) with a compression strength equal to portland cement concrete (4944 psi). Bonding mechanism appears to be result of reactions of boehmite, goethite, and bayerite with the acid solution, and also encapsulation of red mud particles in Mg phosphate matrix. Possible applications include liners for ponds and thickned tailings disposal, dikes for waste ponds, and grouts. Compatability problems arising at the ...

Energy Technology Data Exchange (ETDEWEB)

The influences of compressive stress on the dielectric properties of (1 - x)Pb(In{sub 1/2}Nb{sub 1/2})O{sub 3}-xPbTiO{sub 3} (x = 0.1-0.5) ceramics was investigated in this study. The dielectric properties were measured under compressive stress applied parallel and perpendicular to electric field. The results clearly showed that the superimposed compression stress had pronounced effects on the dielectric properties of PIN-PT ceramics. In general, with increasing compressive stress the dielectric constant of the ceramics increased and decreased when the stress was applied parallel and perpendicular, respectively, to the electric field direction. The dielectric loss tangent, however, decreased in both stress cases. The observations were mainly interpreted in terms of competing influences of the domain switching through non-180 deg. domain walls, clamping of domain walls, de-ageing and the stress-induced decrease in the ...

Energy Technology Data Exchange (ETDEWEB)

This document contains a listing of the written scientific information originating in the Materials Joining (formerly the Welding and Brazing Group), Metals and Ceramics Division, Oak Ridge National Laboratory during 1951 through June 1991. This registry of documents is as much as possible, in the order of issue date.

International Nuclear Information System (INIS)

Multi-cation #alpha#-Sialon ceramics were prepared using mixtures of samarium with calcium, magnesium, yttrium and ytterbium, and compared with a pure Sm-Sialon of equivalent total stabilising cation composition. A ratio of 80eq% samarium to 20eq% of the second stabilising additive was used. Samples were fired at 1820 deg C and subsequently heat treated at 1450 deg C. XRD phase analysis showed that all additives resulted in greater #alpha#-Sialon stability, and that calcium was the most effective additive for the stabilisation of the #alpha#-Sialon phase. Copyright (1998) Australasian Ceramic Society

Science.gov (United States)

Several commercially available capacitors were evaluated at the liquid nitrogen temperature (77 K). Our primary interest was their performance under a bias voltage when used as DC link capacitors in cryogenic power electronics. In general, the performance of polymer capacitors and certain ceramic capacitors is almost independent of the temperature, DC bias, and frequency. On the other hand, ceramic capacitors based on high dielectric constant materials showed a strong dependence on the boundary conditions. Aluminum electrolytic capacitors showed a dramatic decrease of capacitance at 77 K, possibly due to the electrolyte being frozen and therefore losing its conductivity.

British Library Electronic Table of Contents (United Kingdom)

Purpose - This paper aims to describe the technology and applications of nanocomposite materials. Design/methodology/approach - This paper discusses products, applications and technological developments in polymer, ceramic and metal nanocomposites. It concludes with a brief consideration of electronic component applications. Findings - It is shown that polymer nanocomposites and the materials used in their production are commercially available and finding applications in several industries, including automotive, military, food, electronics and leisure, due to their enhanced mechanical, electrical and thermal properties. Ceramic and metallic nanocomposites are at an earlier stage of development and a critical issue to resolve is optimising the dispersion of nanomaterials in the matrices. Pa...

International Nuclear Information System (INIS)

(Pb_1_-_x La_x) (Zr_0_._6_5 Ti_0_._3_5) ceramics, with x = 0.09 (PLZT 9/65/35) were prepared using lead monoxide (Pb O) with different amount of litharge (tetragonal) and massicot (orthorhombic) phases. Results, based on x-ray diffraction patterns, remanent polarization and dielectric measurements, show that the Pb O polymorphic phase does not change the final structure of the PLZT but causes changes on the remanent polarization and dielectric permittivity temperature dependence. (author). 11 refs, 2 figs, 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

The objective of this contract is to research, develop and demonstrate a novel ceramic membrane reactor system for the low-cost conversion of natural gas to synthesis gas and hydrogen for liquid transportation fuels: the ITM Syngas process. Through an eight-year, three-phase program, the technology will be developed and scaled up to obtain the technical, engineering, operating and economic data necessary for the final step to full commercialization of the Gas-to-Liquids (GTL) conversion technology. This report is a summary of activities through February 1999.

Energy Technology Data Exchange (ETDEWEB)

The purpose of this memo is to give an update on our work on ceramic laser materials--feasibility proposal 04-FS-006. Transparent ceramic materials have several major advantages over single crystals in laser applications including, ease and robustness of manufacturing, large apertures, design flexibility, fracture toughness, high activator concentrations, uniformity of composition, no residual stress, and others discussed in the proposal. After a decade of working on making transparent YAG:Nd in 1995 Japanese workers demonstrated samples for the first time that performed as well in lasers as their single crystal counterparts. Since then several laser materials have been made and evaluated. For these reasons, developing ceramic laser materials is the most exciting and futuristic materials topic in today's major solid-state laser conferences. The highlights and executive summary of our work to date are: (1) Ordered a ...

Energy Technology Data Exchange (ETDEWEB)

The Externally-Fired Combined Cycle (EFCC) offers a method for operating high-efficiency gas and steam turbine combined cycles on coal. In the EFCC, an air heater replaces the gas turbine combustor so that the turbine can be indirectly fired. Ceramic materials are required for the heat exchange surfaces to accommodate the operating temperatures of modern gas turbines. The ceramic air heater or heat exchanger is the focus of this program, and the two primary objectives are (1) to demonstrate that a ceramic air heater can be reliably pressurized to a level of 225 psia (1.5 MPa); and (2) to show that the air heater can withstand exposure to the products of coal combustion at elevated temperatures. By replacing the gas turbine combustor with a ceramic air heater, the cycle can use coal or other ash-bearing fuels. Numerous programs have attempted to fuel high efficiency gas turbines directly with coal, often ...

CERN Document Server

Structural steels with improved atmospheric corrosion resistance

Science.gov (United States)

... Accession Number : AD0152957. Title : IMPROVED FORMULATIONS FOR COMBUSTIBLE CARTRIDGE CASES. Corporate ...

International Nuclear Information System (INIS)

Lithium Ceramics offer tremendous potential as a source for the production of tritium ("3H) for fusion power reactors. Their successful application will depend to a great extent upon the diffusion properties of the "6Li within the matrix. Consequently knowledge of "6Li concentration gradients in the ceramic matrices is an important requirement in the continued development of the technology. In this investigation, the neutron depth profile (NDP) technique has been applied to the study of concentration profiles of "6Li in lithium aluminate ceramics, doped with 1.8%, 50% and 95% "6Li isotopic concentrations. Specimen for analysis were prepared at Battelle (PNL) as pellet discs. Samples for diffusion studies were arranged as diffusion couples in the following manner: 1.8% "6Li discs/85% "6Li powder. Experiments were performed at the Texas A and M Nuclear Science Center Reactor Building, utilizing 1 MW equivalent thermal neutron ...

International Nuclear Information System (INIS)

A radioactive Waste Incineration System (WIS) with suspension combustion is noticed as effective volume reduction technology of low level radiactive wastes that are increasing every year. In order to demonstrate the decontamination efficiency of ceramic filter used on WIS, this test has been carried out with the test facilities as joint research of Central Research Institute of Electric Power Industry (CRIEPI) and Sumitomo Heavy Industries, Ltd. Miscellaneous combustible waste and power resin, to which 5 nuclides (Mn-54, Fe-59, Co-60, Zn-65, Cs-137) were added, were used as samples for incineration. As the result of the test, it was verified that Decontamination Factor (DF) of the single stage ceramic filter was usually kept over 10"5 for every nuclide, and from the results of above DF, over 10"8 is expected for real commercial plant as a total system. Therefore, it is realized that the off-gas clean up system of the WIS composed of only single ...

Energy Technology Data Exchange (ETDEWEB)

The dispersion of more than 20 vol pct submicrometer ceramic particles within a metallic matrix and the deposition of such a cermet to form a thick and tough coating presents problems. Most of the coating techniques have failed in attempting to homogeneously disperse very fine and hard particles in large amounts while avoiding their decomposition or reaction with the metal matrix during the deposition process. A simple and efficient method has been developed for producing ceramic-containing composite coatings. It consists in synthesizing cermet-based materials and in depositing them by a rapid solidification process, such as thermal spraying. Boride- and carbide-based materials have been successfully obtained by plasma spraying reactive powders comprising the basic reagents. These materials, with a microstructure of submicrometer ceramic particles dispersed in a metallic matrix, exhibit good wear-resistant properties ...

Energy Technology Data Exchange (ETDEWEB)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

Energy Technology Data Exchange (ETDEWEB)

Ceramics with composition Ba{sub 1-x}Na{sub x}Ti{sub 1-x}Nb{sub x}O{sub 3} are of either classical ferroelectric (for 0{<=}x<0.075) and ferro- or antiferroelectric (for 0.55<x{<=}1) or relaxor ferroelectric type (for 0.075{<=}x{<=}0.55), the transition at T{sub c} being only diffuse without any frequency dispersion for this last region. All the corresponding dielectric characteristics, i.e. diffusivity of the ferroelectric-paraelectric transition, frequency dispersion of {epsilon}{sub r}', shift of T{sub m} with frequency deviation from the Curie-Weiss law, are determined. The relaxor behaviour is more relaxor the more the composition deviates from BaTiO{sub 3} and NaNbO{sub 3}. This study is in the field of preparation of relaxor ceramics free from lead in the interest of the environment, which present a transition temperature close to room temperature. (author)

Energy Technology Data Exchange (ETDEWEB)

Aiming to realize ball bearings operable in a vacuum and under high temperature, silicon nitride (Si3N4) ceramic ball bearings were tested. The tested ball bearings were angular contact ball bearings composed of silicon nitride with sputtered molybdenum disulfide coating using a retainer of hot-pressed self-lubricating composite material. The time variation of the frictional torque was examined for the operations under the conditions at 500{degree}C in a vacuum at a rotational speed of 600 rpm and 50N thrust load for 5{times}10{sup 7}revolutions (1400 hours) and for 1.5{times}10{sup 8}revolutions (4200 hours). Excellent tribological performance was obtained. The ball bearings are lubricated with the molybdenum disulfide film at the initial stage of the operation and with a transfer film formed from the retainer material to the balls. In a test at 650{degree}C, low and stable frictional torque was observed up to 500 hours of operation as of the 500{degree}C test, no ...

International Nuclear Information System (INIS)

Carbide ceramics such as boron carbide due to their unique properties such as low density, high refractoriness, and high strength to weight ratio have many applications in different industries. This study focuses on direct bonding of boron carbide for high temperature applications using nickel interlayer. The process variables such as bonding time, temperature, and pressure have been investigated. The microstructure of the joint area was studied using electron scanning microscope technique. At all the bonding temperatures ranging from 1150 to 1300degC a reaction layer formed across the ceramic/metal interface. The thickness of the reaction layer increased by increasing temperature. The strength of the bonded samples was measured using shear testing method. The highest strength value obtained was about 100 MPa and belonged to the samples bonded at 1250 for 75 min bonding time. The strength of the joints decreased by increasing the bonding ...

International Nuclear Information System (INIS)

A family of sealant materials has been developed for use in the solid oxide fuel cell (SOFC) and in other applications in the temperature range of 800 endash 1000 degree C. These materials are based on glasses and glass-ceramics in the SrO endash La_2O_3 endash Al_2O_3 endash B_2O_3 endash SiO_2 system. The coefficients of thermal expansion (CTE) for these materials are in the range of 8 endash 13x10"-"6/degree C, a good match with those of the SOFC components. These sealant materials bond well with the ceramics of the SOFC and, more importantly, form bonds that can be thermally cycled without failure. At the fuel cell operating temperature, the sealants have viscosities in the range of 10"4-10"6 Pa-s, which allow them to tolerate a CTE mismatch of about 20% among the bonded substrates. The gas tightness of a sample seal was demonstrated in a simple zirconia-based oxygen concentration cell. copyright 1996 Materials Research Society.

Energy Technology Data Exchange (ETDEWEB)

The effects of Fe and B{sub 4}C on the sintering behavior and mechanical properties of TiB{sub 2} ceramics have been studied. Sintering was performed in an Ar atmosphere at 2000{degrees}C using attrition-milled TiB{sub 2} powder. When a small amount of Fe (0.5 wt%) was added, abnormal grain growth occurred and the sintered density was low. In the case of B{sub 4}C added along with 0.5 wt% Fe, however, abnormal grain growth was remarkably suppressed, and the sintered density was increased up to 95% of theoretical. But with excess Fe addition (5 wt%), B{sub 4}C grains did not act as a grain growth inhibitor, and B{sub 4}C grains were frequently trapped in large TiB{sub 2} grains. The best mechanical properties were obtained for the TiB{sub 2}-10 wt% B{sub 4}C-0.5 wt% Fe ceramics, which exhibited a three-point bending strength of 400 MPa and a fracture toughness of 5.5 MPa {center dot} m{sup 1/2}.

British Library Electronic Table of Contents (United Kingdom)

A testing methodology, which includes the evaluation of free sintering strain, stress-induced dimensional changes, and weight changes, was developed to determine the critical dimensional changes and thermomechanical response during presintering (i.e., before densification). The effects of organic binder burnout, decomposition of phases, and phase changes on the thermomechanical behavior of a ceramic green body, consisting of methylcellulose as a binder, gibbsite, silica, and alumina, were studied. The compressive stress-strain behavior was found to be nonlinear. The average compressive and tensile strengths of the sample at room temperature were -14.5 and 1.06 MPa, respectively. Both the compressive and tensile strengths decrease by two orders of magnitude with the increasing temperature a...

Energy Technology Data Exchange (ETDEWEB)

Future power plants will be more fuel efficient, environmentally benign, and economical than current power plants. A high performance power system (HIPPS), based on a coal-fired combined cycle, is currently being developed. The corrosion and temperature-strength properties of currently available metallic materials limit the maximum efficiency of this cycle. Recently, ceramic matrix composites have shown promise in overcoming the design limitations on the future power plants. In particular, the high-temperature, and corrosion and erosion resistant properties of continuous fiber ceramic composites (CFCCs) will allow engineers to design high-temperature heat exchangers, cyclone vortex finder tubes, and other components. Research being performed to evaluate candidate materials for use in future power plants is discussed.

International Nuclear Information System (INIS)

We reported in previous papers that both the near-uv and the visible photosensitivities of ferroelectric-phase PLZT (lead lanthanum zirconate titanate) ceramics are increased by as much as four orders of magnitude by ion implantation or a combination of thermal diffusion of Al and ion implantation. New results are presented here on high-energy (1 MeV) implants of Al and Ni and coimplants of Al + Ne and Ni + Ne, and these results are compared with earlier 500 keV implants of Al and Cr and coimplants of Al + Ne and Cr + Ne as surface modification techniques for increasing the visible photosensitivity of PLZT. The important role of grain size in determining optimum contrast and resolution of stored optical information is described in terms of new experimental results.

International Nuclear Information System (INIS)

The electronic structure and optical properties in tetragonal ceramics PbTiO_3, are studied by using full-potential linearized augmented plane wave method in density functional theory with the generalized gradient approximation by WIEN2K package. The theoretical calculated optical properties and energy loss spectrum yield a static refractive index of 2.59 and a plasmon energy of 22.7eV for the tetragonal phase. The effective electron number at low energy saturates near 22-23eV with the value of 50 for the effective electron number. The results show a indirect band gap of 2.2eV at the I' point in the Brillouin zone. The :calculated band structure and density of states of PbTiO_3 agree with previous experimental and theoretical results.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Because noble dental casting alloys for metal ceramic restorations have a wide range of mechanical properties, knowledge of these properties is needed for rational alloy selection in different clinical situations where cast metal restorations are indicated. Purpose The purpose of this study was to compare the mechanical properties and examine both the fracture and polished surfaces of 6 noble casting alloys that span many currently marketed systems. Five alloys were designed for metal ceramic restorations, and a sixth Type GPT has Type IV alloy for fixed prosthodontics (Maxigold KF) was included for comparison. Material and methods Specimens (n=6) meeting dimensional requirements for ISO Standards 9693 and 8891 were loaded to failure in tension using a universal testin...

Energy Technology Data Exchange (ETDEWEB)

A pillbox RF output window was developed for the L-band pulsed klystron for the Japanese Hadron Project (JHP) 1-GeV proton linac. The window was designed to withstand a peak RF power of 6 MW, where the pulse width is 600 {mu}sec and the repetition rate is 50 Hz. A high power model was fabricated using an alumina ceramic which has a low loss tangent of 2.5x10{sup -5}. A high power test was successfully performed up to a 113 kW RF average power with a 4 MW peak power, a 565 {mu}sec pulse width and a 50 Hz repetition rate. By extrapolating the data of this high power test, the temperature rise of the ceramic is estimated low enough at the full RF power of 6 MW. Thus this RF window is expected to satisfy the specifications of the L-band Klystron. (author).

Energy Technology Data Exchange (ETDEWEB)

The purpose of the present study is to develop a new method for chemical state analysis by means of EPMA(Electron probe microanalyser). The measured X-ray intensity of Si-K{beta} characteristic X-ray spectra were read-out by a 16 bit microcomputer with a RS-232C interface. And using the curve fitting method the quantitative analysis of chemical compositions in a ternary compound that constituted of the same element has been established. The present method was applied to analyse of the friction and wear properties of Si-base ceramics sliding materials. It was found that the wear debris contains both the compositions of the sliding materials and SiO{sub 2}, and the SiO{sub 2} contents in wear debris was changed with relative humidity. The results clearly showed that the proposed method is very useful for determing the compositions in the ternary compound. (author).

Energy Technology Data Exchange (ETDEWEB)

A combination of erosion and corrosion at the Victoria Junction coal preparation plant in Sydney, Nova Scotia was causing serious problems. Schedule 80 mild steel pipes were starting to fail as well as some quarter-inch steel plates in the lauders and chutes. Some corrosion tests were carried out and the high chloride level in the process water was felt to be the single most important contribution to the corrosion problem. Cast basalt was selected as a solution to the pipe wear problem. Three different types of abrasion/corrosion-resistant tiling - basalt tiles, kalceram tiles and ceramic tiles were well suited to the chloride conditions at this plant.

Energy Technology Data Exchange (ETDEWEB)

Hybrid vehicles have two power supplies as engine and electric motor which are used most efficiently corresponding to objects respectively to attain energy-saving and low pollution. In this paper, factors concerning the fuel economy of hybrid vehicles and potential thereof are examined, and the possibility of reducing fuel cost by half is described. As possible modes of highly efficient hybrid vehicles, series hybrid vehicles (SHEV) of conventional internal combustion engine, parallel hybrid vehicles using EV in combination, series-parallel hybrid vehicles (SPHV), series type fuel cell type vehicles, ceramic engine-turbo compound power generating SPHV as well as SHEV, and ceramics gas turbine engine power generating SHEV are mentioned. 10 refs., 14 figs.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

... Aluminum electrolytic capacitors have improved through the years. They are smaller, and equivalent series resistance (ESR) is improved. ...

International Nuclear Information System (INIS)

Iron oxide as sintering aid to Ce-TZP ceramics produces a beneficial effect on the tetragonal phase stabilization. It was found that ceria powder particle size of 2,0 #mu#m turns the grain-boundary electrical conductivity higher than ceria powder of smaller grain size. (author)

British Library Electronic Table of Contents (United Kingdom)

In this paper, we present the photoluminescence properties of Pr3+-, Sm3+- and Dy3+-doped germanate glasses and glass ceramics. From the X-ray diffraction measurement, the host glass structure was determined. These glasses have shown strong absorption bands in the near-infrared (NIR) region. Compared to Pr3+-, Sm3+- and Dy3+-doped glasses, their respective glass ceramics have shown stronger emissions due to the Ba2TiGe2O8 crystalline phase. For Pr3+-doped glass and glass ceramic, emission bands centered at 530nm (3P03H5), 614nm (3P03H6), 647nm (3P03F2) and 686nm (3P03F3) have been observed with 485nm (3H43P0) excitation wavelength. Of them, 647nm (3P03F2) has shown bright red emission. Emission bands of 4G5/26H5/2 (565nm), 4G5/26H7/2 (602nm) and 4G5/26H9/2 (648nm) for the Sm3+:glass and gl...

Energy Technology Data Exchange (ETDEWEB)

Research investigating applicability of lithium salts for solid electrolyte batteries was described. The studies included determinations of lithium ion conductivities in solid electrolyte systems based on Li4SiO4, LiTi2(PO4)3, and ceramic materials. Research on all solid state lithium cells utilizing TiS2 NiPS3 electrodes was also reported.

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning industrial uses and design of microwave heating equipment. Included are heating and drying of paper, industrial process heat, vulcanization, textile processing, metallurgical heat for sintering and ceramic manufacturing, food processing, and curing of polymers.(Contains 50-250 citations and includes a subject term index and title list.) (Copyright NERAC, Inc. 1995)

Energy Technology Data Exchange (ETDEWEB)

A method for bistable storage of binary optical information includes an antiferroelectric (AFE) lead lanthanum zirconate titanate (PLZT) layer having a stable antiferroelectric first phase and a ferroelectric (FE) second phase obtained by applying a switching electric field across the surface of the device. Optical information is stored by illuminating selected portions of the layer to photoactivate an FE to AFE transition in those portions. Erasure of the stored information is obtained by reapplying the switching field.

Energy Technology Data Exchange (ETDEWEB)

A 1000-watt CO/sub 2/ laser has been demonstrated as a reliable production machine tool for cutting of plastics, high strength reinforced composites, and other nonmetals. More than 40 different plastics have been laser cut, and the results are tabulated. Applications for laser cutting described include fiberglass-reinforced laminates, Kevlar/epoxy composites, fiberglass-reinforced phenolics, nylon/epoxy laminates, ceramics, and disposable tooling made from acrylic.

Science.gov (United States)

During four years of operation at the Central Receiver Test Facility (CRTF) ceramics have performed well in cyclic solar flux densities of less than 30 W/cm/sup 2/. Above 100 W/cm/sup 2/, serious limitations exist. Important application considerations include: the geometry, cyclic and long time exposures, flux density gradients, thermal shock, weathering, and soiling.

International Nuclear Information System (INIS)

This bibliography contains citations concerning the migration of food-packaging materials into foods. Plastic, glass, cardboard, metal, and ceramic containers are discussed. Techniques for analyzing packaging contamination are included. (Contains 90 citations fully indexed and including a title list.).

International Nuclear Information System (INIS)

Plasma immersion ion implantation (PIII) is an effective materials modification and synthesis technique but has seldom been applied to ceramic materials due to the high electrical resistance that reduces the ion bombardment energy and sometimes causes serious electrical arcing in the instrument. Even in cases where PIII is applicable, the surface properties of the implanted insulating materials can be seriously affected due to the low ion energy and materials damage from electrical arcing. In order to enhance the surface and mechanical properties such as wear resistance of ceramic materials used in many industrial applications, surface modification is needed. In this work, we conduct carbon implantation into sintered #alpha#-SiC (silicon carbides that are widely used in vacuum ceramic bearings) using mesh-assisted plasma immersion ion implantation to enhance the surface properties. The use of a conducting grid is ...

Energy Technology Data Exchange (ETDEWEB)

The resulting emissions of the firing of ceramic products of all type are described, the factors are enumerated to diminish the emissions in the kilns and the technologies applied in the kilns to reduce these emissions while carrying out energy saving are described briefly. (author)

Energy Technology Data Exchange (ETDEWEB)

The authors extend the Fermilab formalism for heavy quarks to develop an {Omicron}(a{sup 2}) improved relativistic action. They discuss their construction of the action, including the identification of redundant operators and the calculation of the improvement coefficients.

Energy Technology Data Exchange (ETDEWEB)

This paper deals with the externally coal-fired combined cycle (EFCC). A process simulation for different configurations of the EFCC-process is carried out as well as an investigation of the effect of the key parameters such as the gas turbine inlet temperature and the compressor intake airflow. The results show a promising potential of the efficiency. One component of this combined gas and steam turbine cycle is a high temperature heat exchanger that has to withstand the extrem chemical and thermal operating conditions. Fibre reinforced ceramics and combinations of them with monolithic ceramics seem to be the most promising materials for this application. A cost estimating of the EFCC-process shows that a competitive operation should be possible. (orig.) [Deutsch] Die Ergebnisse der Prozesssimulationen weisen ein vielversprechendes Wirkungsgradpotential des extern kohlebefeuerten Gasturbinenprozesses auf. Der fuer dieses neue Kraftwerkskonzept ...

International Nuclear Information System (INIS)

Silicon nitride-based ceramics behavior is strongly influenced by microstructural parameters, which, in turn are determined by chosen densification method. Highly covalent Si-N bond hind are the silicon nitride densification. Therefore, metal oxides are used in order to get high density. However, such oxides must be carefully selected, because they affect the general macroscopic properties of sintered bodies. In the present work, the viability of rare earth concentrate use to produce #beta#--Si_6_-_xAl_xO_xN_8_-_x and its effect on mechanical properties of the sintering ceramics are studied. Additive composition, heating rate, soaking time and sintering temperature were took as variables. Hardness, fracture toughness, Young's modulus and flexural strength were investigated. Lattice parameter compositional dependence and secondary phases crystallized after past-sintering heat treatment were also determined. The results show that rare earth ...

International Nuclear Information System (INIS)

Boron carbide is a high-technological ceramic material (it is used for lightweight armor, neutron absorbers, wear pieces, etc.). Hot pressing (2200"0C, 40 MPa, Ar atmosphere) and recently high isostatic pressing, are the best know ways for industrial preparation of boron carbide items. Pressureless sintering using metallic, inorganic, B+C, additives is not successful, since, despite having a high density, impurities remain present. Pressureless sintering of boron carbide (or silicon carbide composite) using free carbon addition, produced by in-situ pyrolysis of a Novolaque-type phenol-formaldehyde resin (#approx =# 9 wt%), is now possible in industry. A promising new method is the use of organic precursors, e.g. polycarbosilane with a small amount of phenolic resin, giving CSi and C by in-situ pyrolysis; the resulting boron carbide ceramics have high density (> 92%) and contain no free carbon and a small amount of SiC (#approx =# 5 wt%). The ...

British Library Electronic Table of Contents (United Kingdom)

Zirconium and particularly Zr-2.5wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step pro...

Energy Technology Data Exchange (ETDEWEB)

A method of kinetic analysis applicable to non-isothermal oxidation processes of ceramic nanocomposites is presented using Ti-Si-C-N powder as the substrate. The nanoparticle size and phase composition were determined using high-resolution transmission electron microscopy and X-ray diffraction (XRD). Thermogravimetric measurements were carried out for powder samples in dry air in the temperature range 298-1770 K. The following heating rates were applied: 3, 5, 10, 20 K min{sup -1}. Mass spectrometry was used to analyze gaseous oxidation products and solid products were identified by the XRD technique. The Coats-Redfern equation was applied for the kinetic analysis. For each stage of the oxidation kinetic models, the best accuracy was achieved using a series of criteria, and then the A and E parameters of the Arrhenius equations were estimated. Both linear regression and artificial neural networks were applied in testing kinetic models.

International Nuclear Information System (INIS)

The formation of the melilite solid solution phase (M'), Sm_2Si_3_-_xAl_xO_3_+_xN_4_-_x, in an #alpha#-sialon sample of overall composition Sm_0_._6Si_9_._2_8Al_2_._6_9O_1_._3_6N_1_4_._7_6, was studied as a function of time in the temperature interval 1,375--1,525 C. The #alpha#-sialon ceramic contained only minor amounts of the 21R sialon polytype and some residual grain-boundary glass before heat treatment. In situ studies by high-temperature X-ray diffraction were combined with postsintering heat treatment followed by quenching. The M'-phase was found to be formed by two different mechanisms: either crystallization of the residual grain-boundary liquid or a direct decomposition of the #alpha#-sialon phase. The liquid crystallized during the first 10--15 min of heat treatment, yielding a rapid M'-phase formation, and further formation of M'-phase continued at a much slower rate, related to the decomposition of #alpha#-sialon.

Energy Technology Data Exchange (ETDEWEB)

Currently, high temperature filter systems are in the demonstration phase with the first commercial scale hot filter systems being installed on integrated gasification combined cycle (IGCC) and pressurized fluid bed combustion cycle (PBFC) systems (70 MW). They are dependent on the development of durable and economic high temperature filter systems. These filters are mostly ceramic tubes or candles. Ceramic filter durability has not been high. Failure is usually attributed to mechanical or thermal shock: they can also undergo significant changes due to service conditions. The overall objective of this project is to commercialize weldable, crack resistant filters which will provide several years service in advanced power processes. The specific objectives of this project are to develop corrosion resistant alloys and manufacturing processes to make Iron Aluminide filter media, and to use a ``short term`` exposure apparatus supported by other ...

Science.gov (United States)

An experimental investigation of natural convection heat transfer from a commercially available semiconductor device package is presented. The package was centrally mounted on a ceramic substrate. The package-substrate assembly formed one surface of a dielectric-filled cubical enclosure of aspect ratio one. The top surface of the enclosure was maintained at prescribed temperature. Surface temperature measurements were made at various locations on the substrate, the package lid, as well as the chip center. These measurements are reported for three dielectric fluids and three enclosures top surface temperatures, both with the substrate oriented horizontally as well as vertically. The results indicate that the maximum input power without exceeding a chip junction temperature of 80 C is 2.58 watts with FC-75 as the cooling fluid and the upper boundary maintained at 15 C. This is significantly larger than the maximum of 1.21 watts allowable with the natural convection ...

Energy Technology Data Exchange (ETDEWEB)

Microwave dielectric properties and far-infrared reflectivity spectra of (Zr{sub 0.8}Sn{sub 0.2})TiO{sub 4} ceramics with 1.0mol.% Sb{sub 2}O{sub 5} or WO{sub 3} were investigated in the various sintering atmospheres. The Q{center_dot}f value of the specimens sintered in oxygen atmosphere was enhanced due to the decrease of lattice anharmonic interaction resulting from the decrease of oxygen vacancies, whereas the dielectric constants remained constant regardless of sintering atmosphere. The effects of the sintering atmosphere on the changes of ionic and electronic polarization and the intrinsic microwave losses of the specimens were investigated by using the infrared reflectivity spectra from 50 to 4000cm{sup -1}, which were evaluated using Kramers-Kronig analysis and classical oscillator model. The relative tendency of microwave dielectric properties of the specimens calculated from the reflectivity data was in good agreement with the results by the post-resonant ...

Energy Technology Data Exchange (ETDEWEB)

The need for a hydrogen economy is driven by increasing fuel prices, depleting oil reserves and uncertainty over supplies, and concerns about global warming and environmental pollution. Alternative methods to portable energy sources such as fossil fuels are being developed that are more efficient and carbon-emission-neutral. A prospective method is to produce hydrogen as an energy carrier. This paper presented a study on the degradation of materials under conditions of the sulphur-iodine (SI) thermochemical cycle. The paper provided background information on the study and presented a schematic of the SI cycle. A literature review was presented along with materials selected, such as refractory metals, reactive metals, superalloys, glassy metals, ceramics, cermets, polymers, composites, and coatings. The experimental method was then described. A capsule method was developed to rapidly quantify the decomposition rate of the candidate materials under the target ...

Energy Technology Data Exchange (ETDEWEB)

The feasibility of using hydrogen as the sole fuel in a direct injection diesel engine was investigated. An air cooled single cylinder Lister ST1 diesel engine was modified to operate as a low-heat-rejection engine for this study. Partially stabilized zirconia ceramic parts were used to shield the combustion space of the engine. Using a compression ratio of 17.9:1 and motoring the test engine at 21000 rpm, a maximum compression temperature of approximately 900 K was achieved. Under these operating conditions, all lubricants tested were found to burn. Lowering the speed to 1450 rpm and the compression ratio to 17.1, lubricant combustion and hot spots were successfully eliminated. The maximum compression temperature, when compression ignition of hydrogen was tried, was in the 800 K range. The corresponding ceramic surface temperature was estimated to reach 600-700 K. Only sporadic compression ignition of hydrogen was achievable. (author).

Energy Technology Data Exchange (ETDEWEB)

In nuclear fuel, in approximately one quarter of the fissions, one of the two formed fission products is gaseous. These are mainly the noble gases xenon and krypton with isotopes of xenon contributing up to 90% of the product gases. These noble fission gases do not combine with other species, and have a low solubility in the normally used uranium oxide matrix. They can be dissolved in the fuel matrix or precipitate in nanometer-sized bubbles within the fuel grain, in micrometer-sized bubbles at the grain boundaries, and a fraction also precipitates in fuel pores, coming from fuel fabrication. A fraction of the gas can also be released into the plenum of the fuel rod. With increasing fission, and therefore burn-up, the ceramic fuel material experiences a transformation of its structure in the 'cooler' rim region of the fuel. A subdivision occurs of the original fuel grains of few microns size into thousands of small grains of sub-micron sizes. ...

International Nuclear Information System (INIS)

A large amount of energy has been consumed so far in so called matured industries such as iron and steel, oil refinery, petrochemical, ceramic, paper and pulp manufacturing and so forth. A successive stimulation on the preceding industries has to be enhanced from a technological viewpoint in order to maintain a further development based on novel and innovative technologies. In this regard, energy technology has become and will be increasingly important in a high temperature system so that the basic concept for heat transfer augmentation methods by thermal radiation is reviewed briefly in accord with the recent developments together with theoretical background and the prominent features. The heat transfer augmentation related to thermal radiation is summarized.

International Nuclear Information System (INIS)

The study of imported ceramics found in Beirut and suspected to belong to north Syrian products will provide key evidence for the roles in trade of the various postulated centers in northern Syria and northern Lebanon. It is proposed that a comprehensive range of likely north Syrian products imported to Beirut will be chemically analyzed by PIXE (proton induced X-ray emission) in order to characterize, compare and isolate the various regional production centers that supplied the city from the Persian to Byzantine periods. In this work, we were mainly focusing on the characterization of Amrit products, by using 3 MeV proton beam and Al funny filter, as X-ray absorber.

Energy Technology Data Exchange (ETDEWEB)

A practical method to determine the ionic diffusion coefficient and activation energy by using quasielastic light scattering (QELS) is presented. It is shown that a temperature dependence curve of the QELS intensity at a fixed frequency can be well fitted by Jonscher's formula and that the diffusion parameters can be obtained from this curve fitting. This method is successfully applied not only to crystals with high optical quality, as reported earlier, but also to opaque ceramics, which are more important than the crystals from a practical point of view. The composition dependence of the ionic diffusion coefficient is studied in sintered YbSZ to show the usefulness of this method.

Energy Technology Data Exchange (ETDEWEB)

A plane stress constitutive relation is developed for laminate composites undergoing matrix cracking and therefore displaying significant nonlinear stress-strain behavior. The constitutive relation is similar in some respects to a phenomenological theory of plasticity in that it is fit to data from uniaxial tests. The constitutive equations are specialized to brittle matrix composites (especially CMCs) in the form of cross-piles and quasi-isotropic laminates. Several problems involving stress redistribution at holes and notches due to nonlinear stress-strain behavior are investigated with the aid of the constitutive law.

British Library Electronic Table of Contents (United Kingdom)

Due to the low thermal conductivity of ceramics large temperature gradients are present through the powder particles during plasma spray deposition. As a result the particles often impinge at the substrate in a semi-molten form; which in turn substantially affects the final characteristics of the coating being formed. This study is dedicated to the novel modelling development and simulation of a semi-molten droplet impingement. The study examines the impingement process during impact, spreading and solidification of semi-molten zirconia. The simulation provides an insight to the heat transfer process during impact and solidification of a semi-molten powder particle and illustrates the freezing-induced break-up mechanism at the splat periphery.

Energy Technology Data Exchange (ETDEWEB)

Tribological performance of alumina and silicon carbide ceramics as well as of the hardened steel 100Cr6 for reference was studied during reciprocating sliding and cavitation erosion in isooctane as substitute of gasoline and in distilled water. It was the aim to characterize effects of surface finish of the specimens and the liquid media on friction, resistance to sliding wear and cavitation erosion. Sliding wear tests were run on the self-mated ceramics and ceramic/steel pairs under conditions of boundary lubrication using a laboratory tribometer with cylinder-on-plate geometry. Vibratory cavitation erosion tests were conducted according to ASTM G 32-92. High initial surface roughness of coarse ground specimens led to a distinct running-in period during sliding contact with a transition from high to low values of friction coefficient and wear intensity. Incubation time was reduced with increasing surface roughness in the ...

Energy Technology Data Exchange (ETDEWEB)

A series of short articles discusses: use of a chemically bonded ceramic composite liner, WellerDensit, to protect the steel surface of pulverizer classifier cones; use of a fused cast basalt liners developed by Abresist Corp. in pipes for transporting coal and ash; a survey completed by the National Energy Technology Laboratory to identify causes of outages and other concerns expressed by PC and FBC boiler operators; and Temp-Age, Early Visc-Age and Modern Visc-Age systems for controlling the viscosity of heavy fuel oil to maintain proper combustion. 7 figs.

International Nuclear Information System (INIS)

Recently, a superconducting cryo-electron microscope in which specimens are cooled to the liquid helium temperature (4.2 K) has been developed. The main components and functional features of this new microscope are reported together with application data on polyethylene, poly (4-methyl-1-pentene), valonia cellulose, rock salt, ice crystallites and ceramic superconductor. The resistance to electron radiation damage, of beam-sensitive specimens including polymers has been increased more than ten times. Thus, the microscope has made it possible to take high resolution images and to analyze the crystal-structure of micro-areas. (orig.).

International Nuclear Information System (INIS)

This paper first reviews the history of the Port Hope uranium refinery of Eldorado Nuclear Limited. The current processes used for the production of UO_3, UO_2 and UF_6 from yellow cake are then discussed. Recent process changes and developments in the areas of solvent extraction and UO_3 production together with new processes for the production of ceramic UO_2 and UF_4, are described. Environmental and waste management problems, progress and solutions are next considered. Finally, some experience in siting a new UF_6 refinery, with respect to Environmental Impact Statements and public hearings, conclude the paper. (author).

UK PubMed Central (United Kingdom)

BackgroundThe metagenomic analysis of microbial communities holds the potential to improve our understanding of the role of microbes in clinical conditions. Recent, dramatic improvements...Full Text Available

International Nuclear Information System (INIS)

The microstructure of a pressureless sintered (1,605 C, 90 min) O' + #beta#' SiAlON ceramic with CeO_2 doping has been investigated. It is duplex in nature, consisting of very large, slablike elongated O' grains (20--30 #mu#m long), and a continuous matrix of small rodlike #beta#' grains (< 1.0 #mu#m in length). Many #alpha#-Si_3N_4 inclusions (0.1--0.5 #mu#m in size) were found in the large O' grains. CeO_2-doping and its high doping level as well as the high Al_2O_3 concentration were thought to be the main reasons for accelerating the reaction between the #alpha#-Si_3N_4 and the Si-Al-O-N liquid to precipitate O'-SiAlON. This caused the supergrowth of O' grains. The rapid growth of O' crystals isolated the remnant #alpha#-Si_3N_4 from the reacting liquid, resulting in a delay in the #alpha# #-># #beta#-Si_3N_4 transformation. The large O' grains and the #alpha#-Si_3N_4 inclusions have a pronounced effect on the strength degradation of O' + #beta#' ...

International Nuclear Information System (INIS)

We have demonstrated that optical images can be stored in transparent lead-lanthanum-zirconate-titanate (PLZT) ceramics by exposure to near-UV light with photon energies greater than the band gap energy of approx. equal to 3.35 eV. The image storage process relies on optically induced changes in the switching properties of ferroelectric domains (photoferroelectric effect). Stored images are nonvolatile but can be erased by uniform UV illumination and simultaneous application of an electric field. Although high quality images, with contrast variations of >= 100:1 and spatial resolution of approx. equal to 10 #mu#m, can be stored using the photoferroelectric effect, relatively high exposure energies (approx. equal to 100 mJ/cm"2) are required to store these images. This large exposure energy severely limits the range of possible applications of nonvolatile image storage in PLZT ceramics. We have recently found from studies of H, He and Ar ...

Energy Technology Data Exchange (ETDEWEB)

To heighten durability and safety of materials/parts for undersea oil drilling, the development of ceramic base materials was made by developing function harmony type process technology which harmonizes on a high grade contrary characteristics and various functions. The paper summed up the fiscal 1997 results. In the design of system formation, computational simulation technology was developed to the composite process and the diploid system. The development of multifunction simultaneous manifestation materials was trially made by the higher nano structure process. A study was made of control of microstructures of porous materials and matrix filling by the gas phase precipitation control. Proposed were selective control of grain growth from species crystals and the columnar particle orientation laminated structure of simultaneous manifestation of strength and toughness. By composite precipitation reaction control, studied were simultaneous dispersion of whisker and ...

Energy Technology Data Exchange (ETDEWEB)

Two kinds of Si3N4/SiC composite ceramics having different sintering auxiliaries were fabricated to investigate reproduction of crack healing phenomenon, effects of sintering auxiliaries on crack healing behavior, optimal crack healing conditions, and high-temperature strength characteristics of crack healed portions. The experiment used sinters added with SiC powder at 20% by volume, and hot-pressed under conditions of a sintering temperature of 1850 degC, time for two hours, and a pressure of 35 MPa. The sintering auxiliaries used are Y2O3 and Al2O3. In the experiment, pre-cracks were introduced into test specimens, and heat treatments were given in atmosphere and in argon gas atmosphere at 1300 degC for one hour. A four-point bending test was conducted in atmosphere as a strength test. The result of the experiment revealed that the materials which were heat-treated in atmosphere have greater crack healing effect, that the optimum heat treatment temperature ...

International Nuclear Information System (INIS)

Depth sensing indentation tests were carried out to obtain load-penetration depth curves of SiAlON-ZrO_2 ceramics under different peak loads ranging from 200 to 1800 mN. The values of indentation hardness (H_O_P, H_C_C) and reduced elastic modulus (E_O_P, E_C_C) were calculated by using Oliver-Pharr (OP) and Cheng-Cheng (CC) methods. The experimental results revealed that the indentation hardness and reduced elastic modulus exhibit peak-load dependence, i.e. indentation size effect. Both indentation hardness and reduced elastic modulus values were obtained by considering indenter tip roundness and machine compliance. These values obtained from the OP method are higher than from the CC method. On the other hand, h_f/h_m ratios were used to clarify the indentation deformation behaviour of the SiAlON-ZrO_2 ceramic. The experimental h_f/h_m values were lower than the reported critical value (0.7) for all applied test loads, which is attributed to ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

PMID:19395606

Energy Technology Data Exchange (ETDEWEB)

As a maintenance optimization project to improve the safety of Wolsung NPP (Nuclear Power Plant), reliability of diesel generators are estimated based on the operating experience, and improvement options are suggested. A reliability measure is suggested for the estimation of reliability for standby safety systems to reflect availability. It is assessed that the reliability of diesel generators can be much improved if the suggested improvement options are implemented.

Environmental Research Database

DescriptionNot supplied.

Energy Technology Data Exchange (ETDEWEB)

Short communication

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available