Enhanced biosorptive removal of cadmium from aqueous solutions by silicon dioxide nano-powder, heat inactivated and immobilized Aspergillus ustus  

British Library Electronic Table of Contents (United Kingdom)

Heat inactivated Aspergillus ustus (Asp), silicon dioxide-nano-powder (N Si), and silicon dioxide nano-powder-combined-heat inactivated Aspergillus ustus (N Si Asp) were used to study the biosorption of Cd(II) from aqueous solutions via batch equilibrium technique. Surface characterization and immobilization of the fungal cells on silicon dioxide-nano-powder were examined and confirmed by using FT-IR and ESM analysis. Cadmium biosorption processes were investigated under the effect of pH, contact time, sorbent dosage and initial metal concentration. The three examined sorbents were found to exhibit maximum mmolg^-^1 capacity values in pH 7.0. The maximum determined cadmium capacity by silicon dioxide-nano-powder (N Si) (600mmolg^-^1) was found higher than that exhibited by the heat inactiv...

2011-01-01

2

Investigation of cell parameters, microstructures and electrochemical behaviour of LiMn{sub 2}O{sub 4} normal and nano powders  

Energy Technology Data Exchange (ETDEWEB)

Nano materials are usually difficult to prepare. This work presents a simple way of preparing LiMn{sub 2}O{sub 4} nano powders using the high-energy ball milling method. This method has the advantage of producing pure, single-phase and crystalline nano powders. The milling method is carefully controlled to avoid unwanted chemical reactions that may change the stoichiometry of the material. Nano powders of between 30 and 50 nm are obtained. Structural studies of the nano powders, as well as the more conventional micron-sized LiMn{sub 2}O{sub 4}, are made using X-ray diffraction and neutron diffraction methods. Electrochemical evaluation of the materials is undertaken with a three-probe cyclic voltammetry technique and galvanostatic charge-discharge measurements. Structural studies reveal that not only are the crystallites ...

2009-03-01

3

Particulate composites in the TiC-TiYTZP system  

International Nuclear Information System (INIS)

Twelve powders of TiO_2-Y_2O_3-ZrO_2 solid solution of the methodically changed composition were prepared by a coprecipitation-calcination technique. After mixing with phenol-formaldehyde resin, the powders were calcinated for 2 hours at 1200"oC in vacuum. The resultant composite powders contained TiC and non-reacted carbon. Green compacts were sintered in vacuum at 1500"oC for 2 hours. A temperature increase was stopped at 1200"oC to react remains of carbon. There were two carbides in the composites TiC and ZrC. TiC non-stoichiometry depended on carbon content in the system. Phase composition of the depended on of titania and yttria in zirconia solid solution. The majority of the samples showed two tetragonal zirconia phases differing in lattice parameter and tetragonality. (author)

2004-09-12

4

Spark plasma sintered tantalum carbide: Effect of pressure and nano-boron carbide addition on microstructure and mechanical properties  

British Library Electronic Table of Contents (United Kingdom)

TaC and TaC-1wt.% B4C powders were consolidated using spark plasma sintering (SPS) at 1850^oC and varying pressure of 100, 255 and 363MPa. The effect of pressure on the densification and grain size is evaluated. The role of nano-sized B4C as sintering aid and grain growth inhibitor is studied by means of XRD, SEM and high resolution TEM. Fully dense TaC samples were produced at a pressure of 255MPa and higher at 1850^oC. The increasing pressure also resulted in an increase in TaC grain size. Addition of B4C leads to an increase in the density of 100MPa sample from 89% to 97%. B4C nano-powder resists grain growth even at high pressure of 363MPa. The formation of TaB2/Carbon at TaC grain boundaries helps in pinning the grain boundary and inhibiting grain growth. The effect of B4C addition on...

2011-01-01

5

Microstructural and mechanical characterization of high energy ball milled and sintered WC-10wt%Co-xTaC nano powders  

British Library Electronic Table of Contents (United Kingdom)

Ultra fine tungsten carbide and cobalt powders were milled by high energy planetary ball mill at different ball to powder weight ratios (BPR) to produce particles of WC-10wt%Co hard metal in nanometer scale size. Microstructural characterizations by TEM show that the particle size of tungsten carbide was achieved to 32nm after milling at 15 BPR during 10h. In order to reduce the WC grain growth during the sintering process, tantalum carbide was added to the hard metal as a WC grain growth inhibitor. The nano hard metal powders were compacted at 200MPa pressure and sintered at 1370-1450degreeC temperatures in a high purity hydrogen atmosphere. The results show that the addition of 0.6wt% of TaC improves the hardness and fracture toughness from 1493 HV30 and 11.8MPam (for TaC free sample) to...

2009-01-01