International Nuclear Information System (INIS)

Lead lanthanum zirconate titanate (PLZT) nanopowders with chemical compositions x/65/35 PLZT (x = 6 - 10 mol%) were prepared by sol-gel method. PLZT ceramics was obtained by the conventional sintering method and utilizing the hot pressing method. The investigations of dielectric and ferroelectric measurements of as obtained PLZT ceramics have revealed the influence of lanthanum concentration on the properties of PLZT electroceramics. (author)

International Nuclear Information System (INIS)

Interest in making complex net-shape ceramic parts with good surface finishing and sharp tolerances without machining is a driving force for studying the injection molding technique. This method consists of softhening the ceramic material by means of adding some plastic and heating in order to inject the mixture under pressure into a relatively cold mold where solidification takes place. Essentially, it is the same process used in thermoplastic industry but, in the present case, the ceramic powder load ranges between 80 to 90 wt.%. This work shows results obtained from the fabrication of pieces of different ceramic materials (alumina, barium titanate ferrites, etc.) in a small scale, using equipments developed and constructed in the laboratory. (Author).

British Library Electronic Table of Contents (United Kingdom)

Zirconium and particularly Zr-2.5wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step pro...

Energy Technology Data Exchange (ETDEWEB)

A method for bistable storage of binary optical information includes an antiferroelectric (AFE) lead lanthanum zirconate titanate (PLZT) layer having a stable antiferroelectric first phase and a ferroelectric (FE) second phase obtained by applying a switching electric field across the surface of the device. Optical information is stored by illuminating selected portions of the layer to photoactivate an FE to AFE transition in those portions. Erasure of the stored information is obtained by reapplying the switching field.

International Nuclear Information System (INIS)

The authors observed an extremely high permittivity (#approx#35 000 at T_C) in barium zirconate titanate (BaZr_0_._1Ti_0_._9O_3) ceramics with holmium substitution (1-5 mol %) in Ba site. Careful microstructural investigation and energy dispersive spectroscopy analysis of the 1-2 mol % of Ho substituted ceramics showed the enrichment of a Ho-phase along the grain boundaries with a composition close to the Ho_2Ti_2O_7 pyrochlore. The formation of Ho rich phase resulted in the Maxwell-Wagner polarization mechanism, which leads to this unusually high permittivity. Ceramics with 3 mol % or higher Ho content showed lesser permittivity values compared to 1-2 mol %, probably due to the increase in pyrochlore phase. These high dielectric constant ceramics are useful in nanoscale devices.

British Library Electronic Table of Contents (United Kingdom)

In this work, we report the preparation of lead titanate (PT) nanoceramics (with an average grain size of ~200nm in diameter) by using hydrothermal PT nanoparticles as start materials and characterized the dielectric and ferroelectric properties. The dielectric constant of the ceramic was found to be ~180 (at 1kHz) at room temperature and reached a maximum value of 8330 at ~490^oC, suggesting that the Curie temperature of the nanoceramics is consistent with the known value of PT crystals. Ferroelectric domains and hysteresis loops were obtained through piezoelectric force microscopy measurements, which provide direct and clear evidence for the ferroelectricity in the nanoceramic samples.

Energy Technology Data Exchange (ETDEWEB)

The incorporation of (a) Cs/Sr as simulated heat-generating isotopes contained in Purex reprocessing waste, (b) simulated actinides, and (c) simulated Purex waste in sodium zirconium phosphate (NZP) has been studied. The samples were prepared by sintering, by hot pressing and by hot isostatic pressing in metal bellows containers. The short-term chemical durability of the phosphate-based material containing Purex waste was within an order of magnitude of that for Synroc-C, as measured by 7-day MCC-1 tests at 90{degrees}C. The dissolution behavior showed evidence of re-precipitation phenomena, even after times as short as 28 days. Potential for improvement of NZP-based ceramics for HLW management is discussed. 19 refs., 4 figs., 3 tabs.

International Nuclear Information System (INIS)

This study presents the findings of radiometric analysis carried out to determine the activity concentrations of natural radionuclides in raw materials (clay, kaolin, quartz, feldspar, dolomite, alumina, bauxite, zirconium minerals, red mud and frit) and end products (glazed ceramic wall and floor tiles) in the Turkish ceramics industry. Hundred forty-six samples were obtained from various manufacturers and suppliers throughout the country and analyzed using gamma-ray spectrometer with HPGe detectors. Radiological parameters such as radium equivalent activity, activity concentration index and alpha index were calculated to assess the radiological aspects of the use of the ceramic end products as decorative or covering materials in construction sector. Results obtained were examined in the light of the relevant national and international legislation and guidance and compared with the results of similar ...

J-STORE (Japan)

Full Text Available

International Nuclear Information System (INIS)

This paper reports that grinding and polishing affected the orientation of 90 degrees domains at the surface of lead zirconate titanate (PZT) ceramics. This was quantified by using changes in the intensity ratio of the (002) and (200) X-ray reflections. Grinding unpoled PZT with 600-grit SiC paper gave X-ray intensity ratios similar to those of poled material. This implies that 90 degrees domain realignments had occurred in the near surface region probed by the X-rays. Grinding poled samples with 600-grit SiC further increased the X-ray intensity ratio beyond that caused by poling, indicating that additional surface reorientation of 90 degrees domains had occurred. The effects of diamond polishing depended on the size of the diamond particles. The use of 6-#mu#m diamond had no effect on the (002)/(200) intensity ratio of either poled or unpoled samples, while polishing with 15- or 45-#mu#m diamond significantly enhanced the 90 degrees domain ...

Science.gov (United States)

A number of alloys of zirconium have been investigated as part of a program aimed at improving the high-temperature tensile and creep strength of zirconium. These alloys include aluminum, beryllium, lead, magnesium, molybdenum, niobium, tantalum, tin, titanium, tungsten, vanadium, and zinc, binary and ternary alloys. The data indicate that aluminum, lead, molybdenum niobium, tin, titanium, tungsten, and vanadium can be used successfully to harden zirconium, and that aluminum, tin, titanium, and vanadium are particularly effective in maintaining the strength of zirconium at elevated temperatures.

Energy Technology Data Exchange (ETDEWEB)

BaTiO{sub 3} compacts, when fluxed with {lt} 2 vol% of a complex borate glass phase, were sintered to near theoretical density at temperatures {lt} 1175{degrees}C in 2 h. Microstructural analysis showed a uniform grain size {lt} 1.0 {mu}m with 0.75 wt% ZrO{sub 2} added to the flux phase as a grain growth inhibitor. TEM analysis revealed a microcrystalline grain-boundary phase with the ZrO{sub 2} resident along the grain boundaries. These samples displayed an essentially flat dielectric profile, low dissipation factors ({lt} 2%) over the range 25{degrees} to 125{degrees}C, a near linear dependence ({approx} {+-} 15%) between 25{degrees} and {minus} 55{degrees}C, and significantly increased voltage stability. X-ray diffraction analysis of these small-grained materials indicates a suppression of the tetragonal structure toward a more cubic modification.

Energy Technology Data Exchange (ETDEWEB)

The complex formation of zirconium with biphenyl mono- and biscatecholyazo derivatives has been studied spectrophotometrically. The composition of the complexes, form and charge of complex-forming zirconium ions have been established. A procedure is suggested for calculation of molar absorptivities and stability constants for each of the complexes formed simultaneously in the system. Possible complex formation schemes have been studied. The data obtained were used to develop a spectrophotometric method of determining zirconium in the presence of large amounts of copper.

British Library Electronic Table of Contents (United Kingdom)

Titanate nanotubes were hydrothermally synthesized and their adsorption performances for lead(II) ion removal were studied. The results showed that titanate nanotubes ruptured in the adsorption process resulting in two distinct adsorption stages, thus achieving a maximum adsorption capacity of 3.752mmolg^-^1 of lead(II). Furthermore, it was found that the regeneration of titanate nanotubes loaded with the lead(II) ions can be readily achieved using the saturated EDTA disodium salt aqueous solution, thereby avoiding the trouble of disposal of adsorbent. The adsorption mechanism was also discussed in detail.

CERN Document Server

PLZT Ceramics Prepared from Conventional and Microwave Hydrothermal Powders

International Science & Technology Center (ISTC)

Development of Ceramic Composite Materials and Structural Elements for High-Temperature Nuclear Reactors

Energy Technology Data Exchange (ETDEWEB)

For a wider application of GaAs single crystals for semiconductor devices a cheaper process to grow crystals with high purity and low dislocation density is required. According to todays knowledge the Czochralski method with a hot wall vessel should be the choice. The temperature of the vessel has to be 700deg C to avoid condensation of arsenic which vapourizes from the 1240deg C hot melt. Arsenic vapour is very agressive against all metals. Therefore the corrosion resistance of metals and alloys with a high melting point and also ceramics has been tested. All the alloys under investigation are corroded severely so that they have to be excluded as a material for the vessel. The metals tantalum, molybdenum and tungsten are more resistent, titanium forms initially a thick protection layer and further corrosion is greatly reduced. The ceramics investigated (TiB{sub 2}; ALN; Makor; BN) are not attacked by arsenic though they may store some arsenic. ...

International Nuclear Information System (INIS)

Zirconium phosphate was one of the earliest inorganic ion-exchange suggested for removing strontium and cesium from aqueous nuclear waste. This paper studied ionic exchange to remove Cs-137 and Sr-90 by using different cationic of zirconium phosphate. In this case the parameters studied were the effect of temperature and ion concentration to percent up take and distribution coefficients. It is also conducted the study on column experiments to determine the breakthrough curves for Cs-137 and Sr-90. The result showed the potential of use of zirconium phosphate in radioactive waste treatment. (author)

International Nuclear Information System (INIS)

Zirconium is a transition element located along with sister elements titanium and hafnium in Group IVB of the periodic table. It is grayish white metal, with a density somewhat less than carbon steel. Zirconium is the ninth most common metallic element in the earth's crust, and is more abundant than zinc, lead, nickel, or even copper. Zirconium is exceptionally resistant to corrosion by many common acids and alkalis. It is resistant to most organic acids, such as formic, acetic, lactic, and oxalic acids. It also has a high resistance to localized forms of corrosion, such as pitting, crevice corrosion, and stress corrosion cracking. Its corrosion resistance is caused by the formation of a dense, tenaciously adherent, chemically inert oxide film on the surface. This oxide film protects the base metal from both chemical and mechanical attack at temperatures up to about 400 C (750 F). This article describes ...

Science.gov (United States)

The Swedish Ceramic Institute is an industrial research institute working with product-oriented research and development of ceramics and closely related materials. The institute works with the processing and fabrication of ceramic materials as well as with materials properties and design questions. Its website provides details of research projects (engineering ceramics, electroceramics, traditional ceramics). Publications are listed, with some downloadable files (annual reports, research reports, information leaflets). Sample materials data (mechanical properties, thermal properties) is given for oxides and non-oxide ceramics.

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

This paper presents the results of experimental study carried out to know whether the salicylic acid used as an additive during the precipitation of zirconium using ammonium hydroxide solution goes into the filtrate, remains in the hydrated zirconia or gets distributed between the both under the ambient conditions of precipitation. Keeping its simplicity and amenability to adopt on a routine basis, spectrophotometric method has been chosen for the purpose among the many methods available and the problems associated in determining salicylic acid in the presence of zirconium and the medial measures to circumvent the same have been brought out in detail. (author)

Energy Technology Data Exchange (ETDEWEB)

The initiation and inhibition of pitting corrosion on zirconium and hafnium in aqueous solutions have been investigated by potentiodynamic, potentiostatic and galvanostatic measurements at 25/sup 0/C. Effects of Cl/sup -/, Br/sup -/and I/sup -/ have been examined over a range of salt concentrations and pH. All three halide ions cause pitting attack on the two metals, but this may be inhibited by other anions. The results show that hafnium is more easily protected against pitting than is zirconium. The data are treated by the Butler-Volmer equation to yield more information about the mechanisms of the pitting corrosion.

International Nuclear Information System (INIS)

Degradation of contacts of the electronic equipment at the raised temperatures is connected with active diffusion redistribution of components contact - metalized systems (CMS) and phase production on interphase borders. One of systems diffusion barriers (DB) are polycrystalline silicide a film, in particular silicides of the titan. Reception disilicide the titan (TiSi_2) which on the parameters is demanded for conditions of microelectronics from known silicides of system Ti-Si, is possible as a result of direct reaction of a film of the titan and a substrate of silicon, and at sedimentation of layer Ti-Si demanded stoichiometric structure. Simultaneously there is specific problem polycrystalline diffusion a barrier (PDB): the polycrystalline provides structural balance and metastability film disilicide, but leaves in it borders of grains - easy local ways of diffusion. In clause the analysis diffusion permeability ...

Energy Technology Data Exchange (ETDEWEB)

A process is claimed for selectively preparing alpha-olefins having from 2 to about 22 carbon atoms by contacting a gaseous mixture containing carbon monoxide and hydrogen with an iron titanate alkali metal hydroxide catalyst at reaction conditions correlated so as to favor the formation of a substantial proportion of such alpha-olefin product.

International Nuclear Information System (INIS)

Using the PMR method the interaction of zirconium and hafnium tetrachlorides with tri.tet.butylphenyl ester of 1,2- naphthoquinonediazide (2)-5-sulfonic acid is studied. The formation of MCl_4xNQD complexes is established, the equilibrium constants and thermodynamic parameters of complexing reaction are determined. The presence of rapid ligand exchange, proceeding according to associative mechanism, is detected. The rate constants and activation energies of the exchange reaction are calculated.

International Nuclear Information System (INIS)

Technology of plasma sputtering, structure and properties of zirconium dioxide coatings were studied. Necessity of void number increase to enhance coating heat-resistance is shown. Optimal powder particle size (20-60 #mu#m) providing optimal coating porosity was determined. Weight part of stabilizating oxide (Y_2O_3) in ZrO_2 for formation in coating of microcracks serving as barriers for macro-cracks propagation was determined.

Energy Technology Data Exchange (ETDEWEB)

An energy dispersive x-ray fluorescence technique was used for the determination of Titanium (Ti) and Zirconium (Zr) in red mud by using a standard addition method. An annular {sup 241}Am source is employed for excitation of K shells of elements. 13 refs., 2 figs., 1 tab.

Wastenet

... 300715+Ceramic+Engineering+and+Science+Proceedings 2122%28Series+Code%29+Ceramic+Engineering+and+Science+Proceedings Wiley::Ceramic Engineering and Science Proceedings WILEY KNOWLEDGE FOR ...CART | MY ACCOUNT | CONTACT US | HELP Home / Engineering & Materials Science / Materials Science / Ceramic Engineering and Science Proceedings Related Subjects Soft Matter Organic Electronics Structural ...Materials, Ceramics Structural Materials, Composites Structural Materials or Construction Materials Corrosion Electronics Materials Related Series Ceramic Transactions Series Wiley Series in Materials for ...Electronic and Optoelectric Applications Ceramic Engineering and Science Proceedings (CESP) contain proceedings from three American Ceramic Society (ACerS) meetings: ...

Energy Technology Data Exchange (ETDEWEB)

Characteristics of lead-zirconate-titanate (PZT) elements were studied by directly irradiating them with a 400 MeV/n Xe beam. The elements were sensitive to 10{sup 4} Xe ions and their output amplitudes were proportional to the beam intensity. An ensemble of those output amplitudes displayed a Bragg-curve-like response towards the range of 400 MeV/n Xe ion. We discuss the potential of PZT elements as a radiation detector and their application to high-intensity and high-energy detectors. (author)

Energy Technology Data Exchange (ETDEWEB)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. This paper describes the roles on corrosion. A corrosion test on precipitate-containing and precipitate-free materials made from pure zirconium and a small quantity of iron and chromium, rest potential measurements on an intermetallic compound of Zr(FeCr){sub 2} and zirconium matrix, and a galvanic coupling test of those were performed. Results showed that corrosion behavior of zirconium alloys could be attributed to the electrochemical properties of intermetallic compounds precipitated in each alloy. Namely, the cathodic and anodic polarization characteristics were associated with anodic protection provided by the precipitates on the alloys and the precipitates degradation in ...

Science.gov (United States)

A novel reactor combining a flame-deposited nanostructured titanium dioxide film and a set of embedded ceramic electrodes was designed, developed and tested for degradation of methyl tert-butyl ether (MTBE) in water. On applying a voltage to the ceramic electrodes, a surface coro...

Science.gov (United States)

Courses in Ceramic Engineering from the Course Catalog at the University of Illinois at Urbana-Champaign. List includes: CER E 299. Senior Thesis CER E 320. Ceramic Materials and Properties CER E 321. Ceramic Processing and Microstructure Development CER E 322. Process Design CER E 323. Ceramic Engineering Processing Laboratory CER E 324. Refractory Technology CER E 326. Chemistry and Technology of Glass CER E 327. Ceramic Microscopy CER E 328. Electrical Ceramics CER E 330. Chemically Bonded Ceramics CER E 390. Special Topics in Ceramics CER E 420. Ceramic Chemistry CER E 422. Dielectric Properties of Ceramic Materials CER E 425. Physical Chemistry of Clays and Soils CER E 426. Mineralogy of Clays CER E 427. Petrology of Clay Minerals CER E 429. Seminar in ...

Science.gov (United States)

International Patenting Trends in Advanced Materials: Ceramics (June 18, 1999) This report is the ... manufacturing, biotechnology, and advanced materials. Hypertext Format Portable Document Format ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Stress relaxation was studied at 408 K on AZ31 reinforced by ceramic foam produced by in situ foaming of filler loaded preceramic polymer melt. Reinforcement causes significant enhancement of the resistance against stress relaxation compared to AZ91. It is correlated with hardening by the ceramic skeleton as well as ceramic particles formed in the AZ31-matrix. (orig.)

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

Not Available

Science.gov (United States)

Language: English ...

International Nuclear Information System (INIS)

The methods of surface modification of Ti-Zr alloy by laser treatment are considered. Characteristics of laser modification without- and with surface melting and with melting in different gaseous environments and with nickel microalloying are presented. Maximum depth, hardness and corrosion resistance are observed under nickel laser alloying.

Energy Technology Data Exchange (ETDEWEB)

Using an expanded nuclear data base, the activation of nitrogen, aluminum, iron, nickel, copper, zirconium, niobium, molybdenum, tungsten, and lead were calculated for the first wall positions of the STARFIRE and MARS conceptual fusion reactors.

British Library Electronic Table of Contents (United Kingdom)

Abstract Introduction.- Infection is the worst complication seen with inflatable penile prosthesis (IPP). Both the American Medical Systems (AMS) and Coloplast IPP have infection retardant coatings. AMS is coated at the factory with rifampicin and minocycline (InhibiZone). The Coloplast IPP has a hydrophilic coating covalently bonded to its components that will absorb any aqueous solution before implantation and provides increased surface lubricity to decrease bacterial adherence. Aim.- We tested several antibiotic dips comparing zones of inhibition (ZOI) against five commonly infecting bacteria with coated Coloplast implants. Results were compared with those ZOI created with strips of an AMS IPP precoated with InhibiZone. Methods.- Pieces of sterile Coloplast Titan IPP were dipped in (i) ...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Porcelain fracture associated with an implant-supported, metal ceramic crown or fixed partial denture occurs at a higher rate than in tooth-supported restorations, according to the literature. Implant-specific and patient-specific causes of ceramic failure have not been fully evaluated. Purpose The purpose of this retrospective study was to evaluate the potential statistical predictors for porcelain fracture of implant-supported, metal ceramic restorations. Material and Methods Over a 6-month period, a consecutive series of patients having previously received implant-supported, metal ceramic fixed restorations were examined during periodic recall appointments. The number of supporting implants, number of dental units, type of restoration, date of prosthesis insertion, ...

Energy Technology Data Exchange (ETDEWEB)

In this, the last of a series of three papers, we discuss a method of forming iron phosphate ceramics by a reduction process. We report the formation of iron oxide ceramics by reducing hematite with iron in a phosphoric acid solution. The reaction results in a rapid-setting ceramic (at room temperature) with a compressive strength of 3700 psi and a density of 1.7 g/cm{sup 3}. Although the exact mineral form of the binder is difficult to determine because it is mostly amorphous and hence is not amenable to X-ray diffraction analyses, this material is expected to consist of iron hydrophosphates. The reduction process is very useful in recycling several industrial wastes that are rich in hematite, including iron mine tailings, red mud (a caustic waste from the alumina industry), and machining swarfs. Formation of ceramics with red mud and swarfs is also discussed.

International Nuclear Information System (INIS)

Europium (Eu) ions-doped titanate nanowires were synthesized via a sol-gel-hydrothermal chemistry and they were found to be roll multilayered trititanate-type nanowires intercalated with Eu3+ and alkali ions. The average diameter was about 20 nm for nanowires synthesized in NaOH solution and about 10 nm for nanowires synthesized in KOH solution. Under ultraviolet excitation the nanowires showed bright red emission corresponding to 5D0-7Fj of Eu3+ ions at room temperature, which was attributed to the non-radiative energy transfer from the surrounding Ti-O octahedral nanosheets to the central Eu3+ ions in interlayer. The luminescent properties of nanowires were influenced by the type of co-intercalated alkali ions, doping degree, hydrothermal and annealing temperatures. The intensity ratio of 5D0-7F2 to 5D0-7F1 of titanate nanowires intercalated with Eu3+ and Na+ ions was higher than that of titanate nanowires intercalated ...

International Nuclear Information System (INIS)

Alloys of zirconium are widely used in various core components of power reactors. Nuclear assemblies require high degree of reliability and integrity for performing in radiation and corrosive atmosphere. The hostile environments of reactor core and inaccessibility for repairs make it mandatory to select only those joining techniques which produce not only superior quality but are also amenable to NDT methods and such other techniques which ensure acceptable performance. The author has worked on various types of welding of zirconium alloys for different applications. Modern techniques in electron beam (EB) welding, resistance welding, GTAW welding and laser welding have been developed for joining Zr alloys components for different types of reactors. Many of these have been standardized and successfully used in production. Several advancements have been made in the welding technologies towards achieving high productivity and increased reliability ...

British Library Electronic Table of Contents (United Kingdom)

(1-x)(Na0.5K0.5)NbO3-xAgSbO3 lead-free piezoelectric ceramics were prepared by normal sintering. The effects of the AgSbO3 on the phase structure and piezoelectric properties of the ceramics were systematically studied. These results show that the AgSbO3-modified (K0.50Na0.50)NbO3 lead-free piezoelectric ceramics form stable solution with orthorhombic structure, and the Curie temperature and the polymorphic phase transition of the ceramics decreased with increasing AgSbO3. The result shows that the piezoelectric properties of the ceramics strongly depend on the AgSbO3. The ceramics with x=0.05 possess optimum properties (d33=192 pC/N, kp=43%, Tc=348degreeC, To-t=145degreeC, ?r632, and tan d3.5%). These results indicate that the ceramic is a promising candidate material for lead-free piezoe...

International Science & Technology Center (ISTC)

Development of New Resource-Saving Technologies for Ceramic Material Production: High resistant Pigments, Heat Shielding, Plasters, Filters, etc.; by the Method of Controllable Thermosynthesis in Combustion Wave Using Industrial Metal-Containing Wastes

International Nuclear Information System (INIS)

English 2006 2 p. Brazil Rocha, RM Centro Tecnico Aeroespacial, Sao

Science.gov (United States)

Sensitivity to Dental Cements; Dental Crowns; Dental Three-unit Bridges

Science.gov (United States)

PMID:21846114

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The addition of titanium to eutectic braze compositions causes these alloys to readily wet and bond to A1N ceramics. Electron microscopic characterizations of the metal-ceramic interfaces reveal the presence of TiN, along with other Ti- and Al-containing phases. The formation of such interfacial reaction products is an additional thermodynamic driving force for the creation of useful metal-ceramic bonds. 12 refs., 4 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

The ceramic composite armor has been lucubrated in the past 40 years. Ceramic can provide the same protection as metal, but it has lighter weight than metal. Ceramic has excellent ability of resisting kinetic energy projectile, because it can transfer energy to a large range by its fragmented cone and has higher ability of eroding the projectile than metal. But the researches indicated the full potential of the ceramic hard face has not been achieved because the significant interface between ceramic and metal has the unfavorable impedance effects and would induce tensile failure. FGM is a new type composite with continuous transition from ceramic to metal; it has no significant discrete materials interfaces between ceramic and metal. This paper deals with the impact response of Ceramic/FGM/Metal armor by numerical and ...

Energy Technology Data Exchange (ETDEWEB)

The development and experimental demonstration of a high-temperature seal for the SHARE ceramic dome cavity receiver is reported. The mechanical contact seal which was tested on one-foot-diameter silicon-carbide ceramic-dome hardware at pressure differentials to four atmospheres and dome temperatures to 2200/sup 0/F (1200/sup 0/C) showed negligible leakage at expected receiver operating conditions. Potential solar receiver applications for the technology are illustrated.

Science.gov (United States)

The use of ceramics as energy absorbents has been studied by many researchers and some improvements in the ballistic performance of ceramic tiles have been made by coating them with different classes of materials (e.g. E-glass/epoxy, carbon-fiber/epoxy, etc.). Using ceramics for energy absorbing applications leads to a significant weight reduction of the system. Therefore, any modification to the ceramic configuration in the system which leads to more energy absorption with the same or less areal density is significant. On the other hand, polyurea has been proved to be an excellent energy dissipating agent in many applications. Inspired by this, we are studying the effect of coating ceramics with polyurea and other materials, on the energy absorption and ballistic performance of the resulting ceramic-based composites. In this study, we investigate the effect of ...

International Nuclear Information System (INIS)

The present invention provides a fuel cladding tube having an excellent corrosion resistance and thus a long life, and a suitable manufacturing method therefor. Namely, in the fuel cladding tube, the outer circumference of an inner layer made of a zirconium base alloy is coated with an outer layer made of a metal more corrosion resistant than the zirconium base alloy. Ti or a titanium alloy is suitable for the corrosion resistant metal. In addition, the outer layer can be coated by a method such as vapor deposition or plating, not limited to joining of the inner layer material and the outer layer material. Specifically, a composite material having an inner layer made of a zirconium alloy coated by the outer material made of a titanium alloy is applied with hot fabrication at a temperature within a range of from 500 to 850degC and at a fabrication rate of not less than 5%. The fabrication method includes any of extrusion, ...

Science.gov (United States)

The interaction of Pu(IV) and Zr(IV) with citric acid in nitric acid solutions (C/sub HNO/sub 3// greater than 0.1 M) of lithium nitrate was studied by the distribution method in the interval of nitrate ion concentrations from 1 to 6 g-eq/liter. A 40 percent solution of TBP in decane was used as the extraction reagent. It was established that within the range of concentrations studied, complex compounds of plutonium and zirconium are formed: PuHCit/sup 2 +/ and ZrH/sub 2/Cit/sup 3 +/. The concentration equilibrium constants of the reactions of formation of these compounds retain a constant value at constant ionic strength and undergo substantial variation when the total concentration of the nitrate ion in solution is varied. The values of the effective equilibrium constants, calculated considering the change in the activity coefficient of the hydrogen ion, retain a constant value within a wide range of nitrate ion concentrations. It was shown that the effectiveness ...

International Nuclear Information System (INIS)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. In the previous paper, corrosion mechanism was elucidated by the anodic protection-precipitates degradation model. This paper describes the roles on hydrogen pickup. 633 K pure water autoclave test was performed on high purity zirconium, Zr-0.2Fe, Zr-0.2Cr, and Zr-0.1Fe-0.1Cr alloys. Hydrogen analysis after the corrosion test showed that hydrogen pickup ratio of Zr-0.2Fe alloy was about 80%. It was much higher than about 30% of pure Zr and about 10% of both Zr-0.2Cr and Zr-0.1Fe-0.1Cr alloys. Larger hydrogen content was introduced into Zr-0.2Fe alloy than the other ones by the cathodic hydrogen charging under coulombic equivalence. The precipitates at metal-oxide interface could act not only as cathodic sites in the ...

International Nuclear Information System (INIS)

There are reported the results of corrosion resistance investigation of aluminium bronzes, containing about 8 and 10% of aluminium and modifying quantities of zirconium. The tests of corrosion resistance were carried out in synthetic seawater, in 3% NaCl aqueous solution and in 10% H_2SO_4 aqueous solution, with reference to industrial bronze BA93 (CuAl9Fe3). The bronzes were tested in an annealed, hardened, tempered state and after plastic hot working. The conclusion is that corrosion resistance of aluminium bronzes, especially against selective corrosion, depends more on material structure, resulted form heat treatment, than on chemical composition. (author). 6 refs, 8 figs, 6 tabs.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Computer-aided design/computer-aided manufacturing (CAD/CAM) titanium ceramic restorations were developed with the potential for replacing expensive, high noble metal ceramic restorations. However, there is a lack of information about the clinical performance of CAD/CAM titanium ceramic single crowns. Purpose The purpose of this study was to evaluate CAD/CAM titanium ceramic single crowns after 3 years in function. Material and methods A total of 41 crowns were fabricated for 21 patients. The titanium copings were CAD/CAM milled (Everest CAD/CAM system) with an even thickness of 0.5 mm, and low-fusing veneering porcelain (Vita Titanium Porcelain) was added incrementally. The crowns were cemented using zinc phosphate cement after confirming that there were no mechanical...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Although the esthetic outcome of a collarless metal ceramic restoration is superior to that of a restoration with a metal margin, its mechanical strength has not been evaluated. Purpose The purpose of this study was to evaluate and compare the fracture resistance of metal ceramic restorations with metal margins to that of metal ceramic restorations with circumferential porcelain margins, after exposure to masticatory simulation. Material and methods Twenty-four metal ceramic restorations were fabricated and paired with 24 cobalt-chrome tooth analogs. Twelve of the specimens had metal margins, while the remainder had circumferential porcelain margins. The restorations were cemented on the metal tooth analogs with a resin-modified glass ionomer luting agent (FujiCEM). Al...

Energy Technology Data Exchange (ETDEWEB)

Resulting of the remarkably growth on economical development in each countries of Asia, ceramics low heat rejection engines are paid attention as a technique corresponding with the third oil shock which is presumed in near future. On the other hand, in order to construct the low heat rejection engines, using the quite different property materials from metals which called ceramics, it is necessary to determine design and combustion method fitted to the feature of this different kind materials. Though the development of ceramics low heat rejection engines have been given up in the world, recently, the development of ceramics engines is again required for the purpose of realizing an engine with low fuel consumption. Authors have successfully solved the problems, such as the disuse of cooling system, the improvement of combustion to reduce fuel consumption and exhaust emissions, and the realization of ...

International Nuclear Information System (INIS)

A suspension-firing type radioactive waste incineration system is developed and cold demonstration testing of ceramic filters for the system are carried out. The incineration system, which is useful for a wide variety of waste materials, can serve to simplify the facilities and to reduce the costs for waste disposal. The incineration system can be used for drying-processing of concentrated waste liquids and disposal of flame resistant materials including ion exchange resins and rubber, as well as for ordinary combustible solid materials. An on-line backwash system is adopted to allow the ceramic filters to operate stably for a long period of time. For one-step filtering using the ceramic filter, the decontamination factor is greater than 10"5 for the processing of various wastes. In a practical situation, there exist vapor produced by the spray drier and the cladding in used ion exchange resin, which act to increase the ...

Energy Technology Data Exchange (ETDEWEB)

The solubilities of plutonium and uranium have been determined for alkaline salt solutions having compositions which bound those which will be processed in the In-Tank Precipitation (ITP) process. Loadings of plutonium and uranium onto monosodium titanate (MST) have been determined at temperatures bounding those expected to occur during ITP and using a salt solution which was determined to have the maximum solubility for uranium and plutonium. Fissile loadings increase with decreasing amounts of MST in contact with the salt solutions saturated in plutonium and uranium. At MST concentrations bounding those which are planned for the ITP process, expressions for the maximum loadings (wt %) are determined to be 0.29 - 0.20x[MST] for plutonium and 1.8 - 0.29x[MST] for uranium, where [MST] is the concentration of MST in grams/liter. These expressions are valid over the range of MST concentrations from 0.05 to 0.51 g/L and temperatures of 17[degrees]--74[degrees]C. These ...

International Nuclear Information System (INIS)

Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at substrate temperatures of ...

International Nuclear Information System (INIS)

Novel hybrid organic/inorganic nanocomposites made of metal oxide and conjugated polymer nanocomposite and its application in bulk-heterojunction solar cells were studied. The composite was composed of different concentrations of strontium titanate (SrTiO_3) and polyaniline doped phosphoric acid. The optimum concentration of strontium titanate was found to be 0.2 v/v. An inorganic-organic photovoltaic device with a structure of Ag/Pani-H_3PO_4-SrTiO_3/Al has been fabricated. The ideality factor value of the diode was found to be 1.8. This n value of the diode implies a deviation from ideal junction behaviour. The barrier height #phi#_b value for the diode was found to be 0.56 eV. The Ag/Pani-H_3PO_4-SrTiO_3/Al diode shows a photovoltaic behaviour with a maximum open-circuit voltage V_o_c of 2.49 V, and short-circuit current I_s_c of 5.6 mA under light illumination #lambda# = 460 nm. The conversion efficiency was found to be 5.2%. It is ...

International Nuclear Information System (INIS)

Zircaloy fabrication plant manufactures all the necessary Zr-2 components like fuel canning tubes, calandria tubes and other rod and sheet products. This plant is having a capacity of producing about 4 lakh nos. of PHWR fuel tubes per annum. These tubes are seamless, thin walled with close dimensional tolerances and stringent mechanical properties. The plant has established all the facilities required to produce these tubes with required quality.

International Nuclear Information System (INIS)

This paper reviews the mill flowsheet applied at the SOMAIR (Societe des Mines de l'Air) uranium mill in Niger. It focuses on the yellow cake quality improvements achieved by molybdenum and zirconium elimination through double yellow cake precipitation in tanks at first stage and through size/density control in a fluidized bed precipitator at second stage. Water saving aspects in the plant are also presented. (author)

British Library Electronic Table of Contents (United Kingdom)

The review provides a general idea about the types of metallic alloys and the pure metals used as implant materials in dental and orthopedic surgery. Their corrosive behavior in both real solutions and various media that model human biological fluids is described. Based on the literature data, it is concluded that multicomponent alloys containing titanium, niobium, zirconium, tungsten, molybdenum, aluminum, and silicon are the most resistant to corrosion. Implants made of different types of stainless steel are preferred when manufacturing orthopedic devices for short-term use.

Energy Technology Data Exchange (ETDEWEB)

In this work, the ability of a number of Zr-containing intermetallic compounds with the Zr{sub 2}Me stoichiometry, including Zr{sub 2}Fe, Zr{sub 2}Ni, Zr{sub 2}Co and Zr{sub 4}Fe{sub 2}O{sub 0.6}, to participate in the Hydrogenation-Disproportionation-Desorption-Recombination process was investigated, revealing for the first time that the HDDR route can be employed successfully for all these compounds. 24 refs.

International Nuclear Information System (INIS)

The electrochemical behavior of some zirconium alloys including Zry-2 with various #SIGMA#Ai from 2.5 x 10"-"2"0 to 1.2 x 10"-"1"7 (h), modified Zry-2 with iron contents of 0.15, 0.25, and 0.5%, and standard Zry-4 was studied by measuring anodic polarization curves in sulfuric acid solution. The results of these electrochemical tests were compared with those of steam autoclave tests. In Zry-2, the current peak was observed at 1250 mV (versus SCE) on the anodic polarization curve, and this peak area increased with #SIGMA#Ai and with the size of secondary precipitates. Also, this peak was closely correlated with nodular corrosion resistance as expected from the above results. As iron contents in modified Zry-2 increased, the current peak at 1,250 mV decreased and a new peak at 1,900 mV appeared. The former peak disappeared and the latter peak increased further at 0.5% iron. In Zry-4, the current peak was observed at 1,900 mV, but not at 1,250 mV, and this behavior ...

Energy Technology Data Exchange (ETDEWEB)

For several decades most of the efforts to develop new scintillator materials have concentrated on high-light-yield inorganic single-crystals while polycrystalline ceramic scintillators, since their inception in the early 1980 s, have received relatively little attention. Nevertheless, transparent ceramics offer a promising approach to the fabrication of relatively inexpensive scintillators via a simple mechanical compaction and annealing process that eliminates single-crystal growth. Until recently, commonly accepted concepts restricted the polycrystalline ceramic approach to materials exhibiting a cubic crystal structure. Here, we report our results on the development of two novel ceramic scintillators based on the non-cubic crystalline materials: Lu SiO:Ce (LSO:Ce) and LaBr:Ce. While no evidence for texturing has been found in their ceramic microstructures, our LSO:Ce ...

Energy Technology Data Exchange (ETDEWEB)

The industrial policy of fine ceramics which is one of the new material expected to solve energy/environmental problem, is described. Fine ceramics are possessed with the characteristics like surpassing electromagnetic properties, heat resistance, high strength, etc. and its use as highly efficient power generation plant material, functional material for various sensors/electronic, and activation of existing industries are cited. As for the reclamation of global environment, promotion of saving energy in a global scale, development of innovative environmental technology and increase of carbon dioxide absorption source are described. Furthermore, research and development work in Japan on global environmental industrial technology for 1992 to 1993, new sunshine project and technical developments relating to fine ceramics are explained. As for the results of research and development, the results from the case study of 300kw ...

Energy Technology Data Exchange (ETDEWEB)

This is the final report of a two-year, Laboratory Directed Research and Development (LDRD) project at the Los Alamos National Laboratory (LANL). Functionally graded material is an enabling technology for lightweight body armor improvements. The objective was to demonstrate the ability to produce functionally graded ceramic-polymer and ceramic-metal lightweight armor materials. This objective involved two aspects. The first and key aspect was the development of graded-porosity boron-carbide ceramic microstructures. The second aspect was the development of techniques for liquid infiltration of lightweight metals and polymers into the graded-porosity ceramic. The authors were successful in synthesizing boron-carbide ceramic microstructures with graded porosity. These graded-porosity boron-carbide hot-pressed pieces were then successfully liquid-infiltrated in vacuum with molten ...

International Nuclear Information System (INIS)

The paper presents results of measurements of the natural radioactivity of tap water where samples were taken in front of, and behind the ceramic filter commonly used in houses for the purification of tap water. Altogether, 289 samples were taken, processed and measured during 1985-1986 in Kuwait. Results reveal the fact that ceramic filters reduce substantially the natural radioactivity in water (the 'gross' alpha activity reduced by the factor 2.18 #+-# 18%; the 'gross' beta by 1.53 #+-# 1.6%. (author).

International Nuclear Information System (INIS)

The fabrication of the ZT-40 torus, a large complex all-ceramic toroidal plasma containment vessel, is described. Several glass sealants covering the temperature range of 500 to 1300"0C, were developed and used to ''braze'' segments of the torus together, sapphire windows to the torus and the required pump-out and diagnostic parts to the ceramic vacuum vessel. Designs of window seals were developed that allowed sealing of the sapphire windows in a vertical position with minimum sealing glass flow.

Science.gov (United States)

Pore Fraction in Yttrium-Barium-Copper-Oxide and. Other Polycrystalline. Materials ...... Properties of Yttrium Ceramic. Sov. J. LowTemp.Phys. 14:395-402 . ...

British Library Electronic Table of Contents (United Kingdom)

The addition of ?-Sialon nanoparticles to lubricants in heavy-duty frictional joints is shown to be effective.

International Nuclear Information System (INIS)

... INIS-UA--158 488 p. MATERIALS SCIENCE additives aluminium oxides

International Nuclear Information System (INIS)

English 2004 2 p. Brazil Rocha, RM Centro Tecnico Aeroespacial (CTA),

Science.gov (United States)

... Problem: At a glass ceramic cooktop plant, workers manually lift uncut plates of glass onto a waist-high conveyor belt, where it is then stacked ...

International Nuclear Information System (INIS)

... structure crystal-phase transformations fluorescence fluorescence spectroscopy

Energy Technology Data Exchange (ETDEWEB)

The performance of advanced ceramics under cavitation loading in distilled water was studied by using a laboratory test with vibration-induced cavitation following the pattern of the ASTM standard G32-92. The hardened and tempered martensitic steel 100Cr6 was used as a reference. The aim was to identify mechanisms and the effects of important microstructural parameters on damage of polished Al{sub 2}O{sub 3}, Al{sub 2}O{sub 3}-ZrO{sub 2}, ZrO{sub 2} and SiC ceramics. Results showed that surface damage of brittle ceramics was mainly dominated by intergranular fracture, followed by detachment of single grains or fragments of them. Both incubation time and erosion rate were affected by the amount of initial surface cavities, grain sizes and secondary phases at grain boundaries. (orig.)

International Nuclear Information System (INIS)

(#alpha#+#beta#)-SiALON ceramic composites are industrially important materials. Due to their unique chemistry, crystal structure and microstructural features, #alpha#-SiAlON has superior hardness while #beta#-SiALON offers high strength and toughness. The combination of the two phases enables materials engineers to design a ceramic where the physical properties of the composite can be tailored to a particular application. This article presents a general review of the crystal structures, fabrication and properties of the (#alpha#+#beta#)-SiALON composites with special highlights outlining how microstructural tailoring can control the properties of these advanced ceramic alloys. Copyright (1997) Institute of Metals and Materials Australasia Ltd.

Energy Technology Data Exchange (ETDEWEB)

Theoretical thermodynamical calculations for the ZrO/sub 2/- Al/sub 2/O/sub 3/-SiO/sub 2/ system are given to expose the regions of the most chemically stable products of crystallization. It is established that ceramics on the base of mullite with zircon addition and containing the minimum quantity of glass phase should be preferably used in chemical media containing HCl.

Science.gov (United States)

This paper reports Palladium alloy compositions investigated for suitability as a nonreactive material for the processing of ceramic superconductors. Barium-based superconductors were tested on Pd-Au and Pd-Ag alloys for reactivity. Bismuth-based superconductors were tested on a Pd-Ag alloy. The least reactive was found to be 70% Pd-30% Ag for the barium-based high-temperature superconductors (HTSC), whereas 30% Pd-70% Ag was found to be least reactive for bismuth-based HTSC.

Science.gov (United States)

A new dual focal point electro-optic lens that is switchable to focusing and unfocusing is proposed and successfully demonstrated. This electro-optic lens is constructed by coating transparent fine electrodes in the Fresnel-zone plate onto a PLZT ceramic plate. Its focal length changes from 1.25 m to infinity binary at 515 nm with the external voltage of 210 V. PMID:20725208

Energy Technology Data Exchange (ETDEWEB)

For many industrial applications, materials are desired which combine light weight, high temperature strength, and stability in corrosive environments. Among competing materials, ceramics are noteworthy candidates for such applications. The use of ceramics is often constrained, however, by brittleness; i.e., low toughness. Ceramic composites are being developed to overcome this limitation. With recent advances in ceramic fiber technology, it is possible to design a composite material based on continuous ceramic fibers embedded in a ceramic matrix. The use of ceramic composites in industrial applications will result in reduced fuel consumption, but will also prevent airborne pollution (principally NO, SO{sub x}, CO{sub 2}, and particulates), and economically benefit the end user through energy and environmental savings and increased ...

Energy Technology Data Exchange (ETDEWEB)

Theoretical assessment on the chromatographic {sup 99m}Tc generator preparation using (n, {gamma}) {sup 99}Mo produced ex-natural molybdenum was carried out. The relationship between the neutron flux for MoO{sub 3} target activation, Mo-content or Mo adsorption capacity of column packing material, {sup 99m}Tc pertechnetate concentration and/or {sup 99m}Tc radioactivity of eluate was established. The reasonably lower limit of neutron flux of reactor and Molybdenum content of column packing material were found out to estimate the production of portable chromatographic generators available for nuclear medicine application. The concentration of {sup 99m}Tc pertechnetate eluate of low {sup 99m}Tc concentration using the column elution technique was also evaluate theoretically and conducted successfully in practice. Three options of {sup 99m}Tc generator using Titanium-Molybdate, Zirconium-Molybdate and Zirconium Oxide as generator column-packing ...

International Nuclear Information System (INIS)

The cold-worked Zr-2.5%Nb alloy is used as material for the pressure tubes in CANDU nuclear reactors. During the service life in reactor, diffusion of hydrogen and/or deuterium in the pressure tubes wall occur. Below a certain temperature, a stable hydride of zirconium is formed, as a brittle phase which can lead to catastrophic failures. For this reason, it is very important to be able to investigate the hydrogen effect on the micro structural properties of zirconium alloys. In the present paper a non-destructive testing technique is used, known as ultrasonic spectral analysis. When an ultrasonic signal traverses a medium, the frequency components associated with the input signal are altered. By frequency analysing the reflected signals, it is possible to study and compare the material properties. The two major parameters measured in ultrasonic spectroscopy are the attenuation and the velocity of the waves. Attenuation is determined by the ...

International Nuclear Information System (INIS)

A zirconium alloy comprising from 0.8 to 1.6wt% of Sn, from 0.17 to 0.25wt% of Fe, from 0.15 to 0.25wt% of Cr and from 0.01 to 0.08wt% of Ni and Si at a concentration of 120ppm or lower as an impurity and the balance of Zr is melted into cast pieces and then subjected to an #beta# annealing. It is controlled so as to satisfy Fe + Cr + Ni #<=# 0.52wt%. Then, rolling and annealing are applied so that the total heat injection amount #SIGMA#A_i to the materials is within a range of from 1 x 10"-"1"9 to 1 x 10"-"1"7. #SIGMA#A_i = #SIGMA#t_i #centre dot# exp(-Q/RT_i), in which t_i represents processing time (hour) at an ith heat treatment step after the #beta# annealing, T_i represents a processing temperature (K) in the step i. Q represents an activating energy, R represents a gas constant, and Q/R 40,000. (I.N.).

International Nuclear Information System (INIS)

Ten different alloys of zirconium have been tested with regard to the effect of irradiation on their mechanical properties and their sensitivity to environmentally induced failure. Two different environments were used: iodine vapour and liquid cesium with an addition of 2% cadmium. The neutron dose was 10"2"1n/cm"2 (E>1MeV) and the irradiation temperature was about 300 degrees C. All alloy additions increased the irradiation hardening. Especially notable was the large effect of titanium and tin on irradiation hardening. A limited amount of transmission electron microscopy was carried out in order to find an explanation to the effects. The testing in different environments showed that there is no clear correlation between environmental sensitivity and yield stress. For materials of similar yield stress an alloyed material tends to be more sensitive to environmental cracking than a material which only contains oxygen as an impurity. There also seems to be an ...

International Nuclear Information System (INIS)

For several decades, ceramic matrix composite have been attracted attention in advanced structural and tribological applications. Advanced structural ceramics are presently used in diverse tribological applications such as tips for ballpoint pens, precision instrument bearings and cutting tools inserts. Design and selection of ceramics for these applications require reliable data on the effects of temperature, load and environment on the tribological behavior of these ceramics. In the present work, #alpha#-sialon matrix composites reinforced with different amounts of #beta#-sialon fibers were produced with the aim of improving their toughness to increase the industrial applications. The wear properties of #alpha#-sialon matrix composites were evaluated by carried out wear tests using a pin-on-disk tribometer under dry conditions. The #alpha#-sialon matrix composites were manufactured by slip casting and ...

Energy Technology Data Exchange (ETDEWEB)

Sintered glass-ceramics were produced from coal fly ashes, red mud from aluminum production and silica fume. The capabilities of Tuncbilek fly ash and a mixture of Orhaneli fly ash, red mud and silica fume to be vitrified and devitrified by sintering process were investigated by means of scanning electron microscopy and X-ray diffraction analysis. To determine the effect of binder in the sintering technique, glass powders were pressed without or with the addition of polyvinyl alcohol. Owing to microstructural observations, density and hardness measurements, it can be said that physical properties and the hardness of the produced samples strongly depended on the crystallization degree of the samples. Toxicity characteristic leaching procedure test results showed that glass-ceramic samples produced by using sintering technique could be considered as nonhazardous materials. Chemical durability of the sintered glass-ceramic ...

International Nuclear Information System (INIS)

Dysprosium #alpha#-sialon ceramic has been fabricated from #alpha#-Si_3N_4, AlN, Al_2O_3 and Dy_2O_3 starting powders, using gas pressure sintering at 1800 deg C or higher temperatures under a relatively low gas pressure of 0.9MPa N_2. The resultant #alpha#-sialon grains showed significantly different features, such as equiaxed, elongated, and even a few extraordinarily large with high aspect ratio grains in the fine matrix, which has rarely been observed in #alpha#' ceramics. It is suggested that the temperature strongly influences the grain morphologies of #alpha#-sialon, playing an important role particularly in the latter stage of the 'nucleation-growth' process. Such a microstructural morphology of mixed with equiaxed and elongated grains toughens the #alpha#-sialon ceramics and leaves them still hard. Overly high temperature treatment leads to the preferential growth of a few #alpha#' grains which become excessively ...

British Library Electronic Table of Contents (United Kingdom)

A type of Si3N4-based nanocomposites ceramic cutting tool material was prepared by the addition of nano-scale Si3N4W whisker and nano-scale TiN particle. Cutting performance of the Si3N4/Si3N4W/TiN nanocomposite ceramic tool in machining of cast iron was investigated in comparison with a commercial sialon ceramic tool, and the tool wear mechanism was studied. The two types of cutting tools have similar cutting performance at relatively low cutting parameters, while Si3N4/Si3N4W/TiN nanocomposite tool exhibits a better wear resistance than sialon tool at the relatively high cutting parameters. The wear of sialon ceramic cutting tool is dominated by the plastic deformation, abrasive action, microcracking, pullout of grains and chemical action at the higher cutting parameters. The higher mech...

Energy Technology Data Exchange (ETDEWEB)

The CeO{sub 2}-ZrO{sub 2}-Bi{sub 2}O{sub 3} samples with different bismuth content were prepared in this study. By the doping of Bi{sub 2}O{sub 3} into the lattice, TPR profiles of the CeO{sub 2}-ZrO{sub 2} shifted to lower temperatures and oxygen storage capacity increased remarkably. It is concluded that the reason for such a behavior is probably due to both the formation of oxygen vacancies which enhance the oxygen mobility and the simultaneous reduction of Ce{sup 4+} and Bi{sup 3+} in the mixed oxides. (authors)

International Nuclear Information System (INIS)

The description is presented of binary phase diagrams of titanium alloyed with the following elements: silver, aluminium, arsenic, gold, boron, barium, beryllium, bismuth, carbon, calcium, cadmium, cobalt, chromium, copper, iron, gallium, germanium, hydrogen, hafnium, indium, iridium, potassium, lithium, magnesium, manganese, molybdenum, nitrogen, sodium, niobium, nickel, oxygen, osmium, phosphorus, lead, palladium, platinum, plutonium, rhenium, lanthanium, cerium, preseodymium, neodymium, gadolinium, erbium, terbium, thulium, lutetium, rhodium, ruthenium, scandium, silicon, tin, strontium, tantalum, technetium, thorium, uranium, vanadium, tungsten, yttrium, ytterbium, zinc and zirconium.

Energy Technology Data Exchange (ETDEWEB)

The theoretical principles underlying the formation of oxide and, in particular, anodic oxide coatings on metals produced by chemical oxidation, anodizing in solutions, and anodizing in cold plasmas are reviewed. The mechanisms and conditions of anodic oxidation are described, and the structure of anodic oxide coatings on aluminum, magnesium, beryllium, zinc, cadmium, iron, cobalt, nickel, titanium, zirconium, tantalum, and chromium alloys is examined. Attention is also given to various applictins of anodized coatings. 54 references.

Energy Technology Data Exchange (ETDEWEB)

Recognizing the importance of {sup 99m}Tc and {sup 99m}Tc-based radiopharmaceuticals in nuclear medicine, the Philippine Nuclear Research Institute has initiated research on the development of column-type generators for {sup 99m}Tc using {sup 99}Mo in the form of a gel. The use of reactor-produced {sup 99}Mo will reduce the country's dependence on the importation of commercial generators based on fission product molybdenum-99. However, the relatively low specific activity of {sup 99}Mo must be compensated by the high adsorption capacity of the column material for molybdenum. A procedure based on the incorporation of low activity {sup 99}Mo into a zirconium molybdate gel matrix was adopted with reasonable success. Because the properties of the gel vary considerably with conditions of synthesis, the following parameters were carefully controlled: pH, concentration, temperature, order of mixing of the reactant solutions and conditions of aging, washing and ...

Energy Technology Data Exchange (ETDEWEB)

The Kernel Polynomial Method (KPM) has been successfully applied to tight-binding electronic structure calculations as an O(N) method. Here the authors extend this method to nonorthogonal basis sets with a sparse overlap matrix S and a sparse Hamiltonian H. Since the KPM method utilizes matrix vector multiplications it is necessary to apply S{sup {minus}1}H onto a vector. The multiplication of S{sup {minus}1} is performed using a preconditioned conjugate gradient method and does not involve the explicit inversion of S. Hence the method scales the same way as the original KPM method, i.e. O(N), although there is an overhead due to the additional conjugate gradient part. The authors show an application of this method to defects in a titanate/platinum interface and to a large scale electronic structure calculation of amorphous diamond.

Energy Technology Data Exchange (ETDEWEB)

The irradiation behavior of Li{sub 2}TiO{sub 3} under a fusion reactor environment was simulated by simultaneous irradiation of Li{sub 2}TiO{sub 3} by the triple ion beams and the respective single ion beams of O{sup 2+}, He{sup +} and H{sup +}. The microstructural changes in Li{sub 2}TiO{sub 3} caused by the irradiation were measured by Raman spectroscopy and FT-IR photoacoustic spectroscopy. The results suggest that the formation of TiO{sub 2} due to displacements by irradiation occurs, and the irradiation defects generated by irradiation trap hydrogen and increase the amount of hydroxyl near the surface. Such phenomena are believed to significantly affect the chemical form of the released tritium and the tritium inventory in the breeding materials of a fusion reactor.

Science.gov (United States)

The dynamic dielectric susceptibility and the elastic compliance of the relaxor ferroelectric lanthanum lead zirconate titanate (PLZT) 9/65/35 have been measured under different cooling and heating protocols in order to study aging and memory. The memory of multiple aging stages at different temperatures has been found (several dips in the susceptibility curves on heating), as in spin glass systems below the glass transition. Remarkably, in PLZT the memory of several aging stages is retained also above the freezing temperature deduced from the dynamic susceptibilities. The results are discussed in light of the existing models of aging and memory in spin and dipolar glasses. PMID:15447139

Science.gov (United States)

An 80-K Joule-Thomson (J-T) cooling system designed for the Probe Infrared Laser Spectrometer (PIRLS) proposed for the Huygens Titan Probe of the Cassini Saturn orbiter mission is presented. The cryogenic cooling requirements of the PIRLS instrument are listed, and the cooler system design including details of a J-T cryostat, cold head, and dewar design is described along with the results of a thermal modeling effort and lab cooler performance testing. It is shown that by using active feedback temperature control of the cold head in combination with the self-regulating action of the J-T cryostat, a temperature stability of less than 0.1 mK/min is achieved by the cooler weighting 1.8 kg.

Energy Technology Data Exchange (ETDEWEB)

This work reports an alternative methodology for the linear attenuation coefficient determination ({mu} {rho}) of irregular form samples, in such a way that is not necessary to consider the sample thickness. With this methodology, indigenous archaeological ceramics fragments from the region of Londrina, north of Parana, were studied. These ceramics fragments belong to the Kaingaing and Tupiguarani traditions. The equation for the {mu} {rho} determination employing the two mean method was obtained and it was used for {mu} {rho} determination by the gamma ray beam attenuation if immersed ceramics, by turns, in two different means with known linear attenuation coefficient. By the other side, {mu} theoretical value was determined with the XCOM computer code. This code uses as input the ceramics chemistry composition and provides an energy versus mass attenuation coefficient table. In order to validate the ...

International Nuclear Information System (INIS)

Experimental results of compatibility tests on ceramics-metal bonded structures performed under high heat flux conditions in splash test apparatus are reported. Emphasis is placed on results of the channel wall design and its critical operating conditions under MHD environment. The module design of one cold type and three semihot type insulators have been tested. These materials were Al_2O_3, Al_2MgO_4, LaAlO_4, MgO and Sialon ceramics. The methods of cold type ceramics-metal bonding structure were studied on Al_2O_3 and Spinel spray coating technology. The refractory metallizing and ceramics-metal graded structure manufactured by HIP technologies were applied to bonding between the MgO or LaAlO_4 and metallic cooling system. The Sialon non-bonding structure was tested with mechanical supported cooling system by shrinc fitting method. The results indicated that the bonding structures made of the ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes the basic principles underlying the operation of low heat loss engines and the magnitude of the efficiency improvements that are theoretically achievable. The effect of varying degrees of thermal insulation on various operating parameters is examined in some detail, as is the relationship between degree of insulation and ceramic coating thickness. The effect on ceramic materials of severe surface temperature oscillations and the resultant thermal stress gradients is also discussed. In the following section, the paper describes methods of construction adopted both for ceramic inserts and coatings, and rig tests for the assessment of thermal fatigue under both load and firing cycling. The paper does not attempt to draw any general conclusions.

British Library Electronic Table of Contents (United Kingdom)

Glass ceramics are commonly used as sealing materials for planar solid oxide fuel cells (SOFCs). The major requirements of stack and module builders for these materials are the stability of the coefficient of thermal expansion (CTE), excellent bonding (sticking) behaviour and the absence of volatile ingredients, which can lead to changes of the material properties and the sealing ability. SCHOTT Electronic Packaging has developed special glasses and glass-ceramics for various solid oxide fuel cell designs and operating temperatures. The glass compositions are based on the system MgO-Al2O3-BaO-SiO2-B2O3. In this study the evaluation of the developed materials was done by high temperature aging tests for up to 1000h, high temperature XRD-studies and Rietveld calculations, combined with scann...

Energy Technology Data Exchange (ETDEWEB)

The small pilot facility of a cyclone type suspension incineration system of radioactive waste was set up in order to evaluate the decontamination efficiency of a high efficiency ceramic filter. The evaluation was made by use of /sup 54/Mn, /sup 59/Fe, /sup 60/Co, /sup 65/Zn and /sup 137/Cs. 1. The decontamination factor by one line of ceramic filter for every species were over 10/sup 5/. 2. The decontamination factor increased by one oder when water vapor exists in off-gas. The same tendency was also observed when iron dioxide existed at the incineration of cation exchange resin.

Energy Technology Data Exchange (ETDEWEB)

The purpose of the invention is to improve a radiation receiver, consisting of a hollow body with an opening for the entry of radiation and a ceramic absorber situated in the hollow body, which absorbs the radiation energy entering through the opening, and emits it as thermal radiation to a heat medium, so that a higher efficiency can be achieved. According to the invention, the problem is solved by the fact that the absorber consists of ceramic material on the side towards the solar radiation, which has a low emission value and a high absorption value, and that the side of the absorber towards the heat medium has ceramic material of high emission value and low absorption value. This ensures that reradiation is prevented near the opening of the hollow body, and that the solar energy entering is largely absorbed in the hollow body.

Energy Technology Data Exchange (ETDEWEB)

The use of selective additives such as MgO as a sintering aid and a rare earth oxide as a grain growth inhibitor, has allowed the manufacture of beryllia ceramics having close to theoretical density. The grain size and grain size distribution can be controlled by an optimum firing schedule leaving a remnant porosity which is extremely fine (0.2 {mu}m). This structure is compared with conventional BeO ceramics, densified by liquid phase sintering, which develops a glassy grain boundary and retains large pores up to 3 {mu}m. The significantly improved strength properties, extremely fine pores,the 'pinning effect' of rare earth oxide, and the superior surface finish both in the as-fired and polished state are discussed in relation to the micro-structure. (orig.).

British Library Electronic Table of Contents (United Kingdom)

Rapid nitridation was used to fabricate reaction-bonded and postsintered -Si6-ZAlZOZN8-Z (Z=1) ceramics with monoclinic ZrO2 added to the starting powder. Thermo-gravimetric analysis revealed that the addition of ZrO2 reduced the starting temperature of the main nitridation reaction. Using a reaction-bonding route with heating rates of 5, 10, and 20C/min, to fabricate -SiAlON ceramics without ZrO2 resulted in unreacted silicon that bled out of the specimens and the Z=1 composition samples did not maintain the original green compact morphology. On the other hand, no such bleeding of melted silicon was observed for samples with ZrO2 additions and the samples following nitridation maintained the original green morphology. The microstructure and mechanical properties of samples produced by rap...

British Library Electronic Table of Contents (United Kingdom)

Fine-grained BaTiO3-based X7R ceramic materials were prepared and the effects of milling process on the core-shell structures and dielectric properties were investigated using scanning electron microscope, transmission electron microscope, and energy dispersive spectroscopy (EDS). As the milling time extends, the dielectric constant of the ceramics increases, whereas the temperature coefficient of capacitance at 125degreeC drops quickly. The changes in dielectric properties are considered relevant to the microstructure evolution caused by the milling process. Defects on the surface of BaTiO3 particles increase because of the effects of milling process, which will make it easier for additives to diffuse into the interior grains. As the milling time increases, the shell region gets thicker a...

Energy Technology Data Exchange (ETDEWEB)

In 1976 the design and fabrication began of an 1 MWt Bench Model Solar Receiver (BMSR) to demonstrate and further develop the ceramic tube central receiver concept. Although many of the properties of silicon carbide are well documented, this material has never been utilized in an application of this type and size. Further investigation was undertaken to confirm the choice of silicon carbide against available metals and other ceramic materials. The BMSR is configured for testing at the Department of Energy's Central Receiver Test Facility in Albuquerque, New Mexico. Design and fabrication of the BMSR are highlighted in this report. Completion and testing of the BMSR are planned for the next phase of the project.

International Nuclear Information System (INIS)

The formation of a porous coating is the decisive feature for the bio-compatibility of silica-free calcium phosphate glass ceramics on alloy surfaces like the #beta#-Ti structured Ti-29Nb-13Ta-4.6Zr used in this work. The ceramic composition is highly important: 50CaO-40P_2O_5-7Na_2O-3TiO_2 glass powder produces a pore-free coating unable to bind hydroxyapatite, whereas 60CaO-30P_2O_5-7Na_2O-3TiO_2 glass incorporates pores from which a crystalline hydroxyapatite phase can grow over the surface from simulated body fluid (see Figure). (Abstract Copyright [2003], Wiley Periodicals, Inc.)

Energy Technology Data Exchange (ETDEWEB)

Savannah River National Laboratory (SRNL) evaluated the previous monosodium titanate (MST) purchase specifications for particle size and strontium decontamination factor. Based on the measured particle size and filtration performance characteristics of several MST samples with simulated waste solutions and various filter membranes we recommend changing the particle size specification as follows. The recommended specification varies with the size and manufacturer of the filter membrane as shown below. We recommend that future batches of MST received at SRS be tested for particle size and filtration performance. This will increase the available database and provide increased confidence that particle size parameters are an accurate prediction of filtration performance. Testing demonstrated the feasibility of a non-radiochemical method for evaluating strontium removal performance of MST samples. Using this analytical methodology we recommend that the purchase ...

Energy Technology Data Exchange (ETDEWEB)

Development of electronic devices with better performance and smaller size requires the passive components to be embedded within a printed wire board (PWB). The 'film-on-foil' approach is the most viable method for embedding these components within a PWB. We have deposited high-permittivity ferroelectric lead lanthanum zirconate titanate (Pb{sub 0.92}La{sub 0.08}Zr{sub 0.52}Ti{sub 0.48}O{sub x}, PLZT 8/52/48) films on base metal foils by chemical solution deposition. These prefabricated capacitor sheets can be embedded into PWBs for power electronic applications. To eliminate the parasitic effect caused by the formation of a low-permittivity interfacial oxide, a conductive buffer layer of lanthanum nickel oxide (LNO) was applied by chemical solution deposition on nickel foil before the deposition of PLZT. With a {approx} 0.7-{micro}m-thick ferroelectric PLZT film grown on LNO-buffered nickel foil, we measured capacitance densities of 1.5 ...

Science.gov (United States)

was to mount Pd-Ag terminated MLCCs onto gold plated mounting pads of a ... to protect against incorrect shipment of pure tin-plated MLCCs when Pd-Ag ...

Energy Technology Data Exchange (ETDEWEB)

Progress is reported in the following areas: metallurgy and ceramics (structure of materials, mechanical properties, physical properties), experimental research, and particle-solid interactions (irradiation effects on alloys). (DLC)

Energy Technology Data Exchange (ETDEWEB)

Sandia National Laboratories is currently involved in the optimization of a Plane Shock Generator Explosive Lens (PSGEL). The PSGEL component consists of a detonator, explosive, brass cone and tamper housing. The purpose of the PSGEL component is to transmit a plane shock wave through the 4340 steel bulkhead (wave separator) which has a ferro-electric (PZT)ceramic disk attached to the opposite surface of the steel bulkhead. The planar shock wave depolarizes the PZT 65/35 ferro-electric ceramic to produce an electrical output. One aspect of the optimization program involves the possible replacement of 4340 steel with PH13-8Mo steel for the bulkhead. These materials, as well as the PZT 65/35 ferro-electric ceramic and the brass for the cone, required the stock characterization with respect to Hugoniot parameters. The work presented here gives the shock Hugoniot values for these four materials and documents their measurements.

Energy Technology Data Exchange (ETDEWEB)

A neutron irradiation test on superplastic ceramic materials at high temperature has been proposed as an innovative basic research on high-temperature engineering using the High Temperature Engineering Test Reactor (HTTR). We investigated mechanical properties, such as the hardness and Young's modulus, of ceramic specimens after superplastic deformation. The tested material was 3Y-TZP (3mol% Yttria stabilized Tetragonal Zirconia Polycrystal) which is one of the representative superplastic ceramics. The properties were measured by a microindentation method. We also studied the relationship between crystal microstructures and the mechanical properties of deformed 3Y-TZP by scanning electron microscope (SEM). The indentation test showed that the mechanical properties of the specimens were reduced to about 1/2 by 30% deformation and to about 1/4 by 150% deformation. The SEM images showed that average grain size and ...

Energy Technology Data Exchange (ETDEWEB)

Externally Fired Combined Cycles (EFCCs) can increase the amount of electricity produced from ash bearing fuels up to 40%, with overall powerplant efficiencies in excess of 45%. Achieving such high efficiencies requires high temperature-high pressure air heaters capable of driving modern gas turbines from gas streams containing the products of coal combustion. A pilot plant has been constructed in Kennebunk, Maine to provide proof of concept and evaluation of system components. Tests using pulverized Western Pennsylvania bituminous coal have been carried out since April, 1995. The ceramic air heater extracts energy from the products of coal combustion to power a gas turbine. This air heater has operated at gas inlet temperatures over 1,095 C and pressures over 7.0 atm without damage to the ceramic tube string components. Stable gas turbine operation has been achieved with energy input from the air heater and a supplementary gas fired combustor. ...

Energy Technology Data Exchange (ETDEWEB)

This work has been undertaken with a view to study the effect of lanthanum content on properties of PLZT ceramics. The polycrystalline complex compounds of PLZT with Pb{sub 1-x}La{sub x}(Zr{sub 0.40}Ti{sub 0.60}){sub 1-x/4}O{sub 3}, +10% PbO formula were prepared from the nano-size individual oxides powders by hot-pressed process. Transparent PLZT (x/40/60) bulk ceramics with pure tetragonal phase was obtained. The studies of the microstructures, dielectric and ferroelectric properties of the ceramics were carried out. The experiment results showed that when La content increased from 7 to 13 mol.%, the grain size increased from 2 to 7 {mu}m. La content also effects the dielectric property obviously, the dielectric constant increased with La content increasing. Moreover, the ferroelectric properties are sensitive to the variation of La content.

Energy Technology Data Exchange (ETDEWEB)

A room-temperature process for stabilizing mineral waste streams has been developed, based on acid-base reaction between MgO and H3PO4 or acid phosphate solution. The resulting waste form sets into a hard ceramic in a few hours. In this way, various alumina industry wastes, such as red mud and treated potliner waste, can be solidified into ceramics which can be used as structural materials in waste management and construction industry. Red mud ceramics made by this process were low-porosity materials ({approx}2 vol%) with a compression strength equal to portland cement concrete (4944 psi). Bonding mechanism appears to be result of reactions of boehmite, goethite, and bayerite with the acid solution, and also encapsulation of red mud particles in Mg phosphate matrix. Possible applications include liners for ponds and thickned tailings disposal, dikes for waste ponds, and grouts. Compatability problems arising at the ...

Energy Technology Data Exchange (ETDEWEB)

The influences of compressive stress on the dielectric properties of (1 - x)Pb(In{sub 1/2}Nb{sub 1/2})O{sub 3}-xPbTiO{sub 3} (x = 0.1-0.5) ceramics was investigated in this study. The dielectric properties were measured under compressive stress applied parallel and perpendicular to electric field. The results clearly showed that the superimposed compression stress had pronounced effects on the dielectric properties of PIN-PT ceramics. In general, with increasing compressive stress the dielectric constant of the ceramics increased and decreased when the stress was applied parallel and perpendicular, respectively, to the electric field direction. The dielectric loss tangent, however, decreased in both stress cases. The observations were mainly interpreted in terms of competing influences of the domain switching through non-180 deg. domain walls, clamping of domain walls, de-ageing and the stress-induced decrease in the ...

Energy Technology Data Exchange (ETDEWEB)

This document contains a listing of the written scientific information originating in the Materials Joining (formerly the Welding and Brazing Group), Metals and Ceramics Division, Oak Ridge National Laboratory during 1951 through June 1991. This registry of documents is as much as possible, in the order of issue date.

International Nuclear Information System (INIS)

Multi-cation #alpha#-Sialon ceramics were prepared using mixtures of samarium with calcium, magnesium, yttrium and ytterbium, and compared with a pure Sm-Sialon of equivalent total stabilising cation composition. A ratio of 80eq% samarium to 20eq% of the second stabilising additive was used. Samples were fired at 1820 deg C and subsequently heat treated at 1450 deg C. XRD phase analysis showed that all additives resulted in greater #alpha#-Sialon stability, and that calcium was the most effective additive for the stabilisation of the #alpha#-Sialon phase. Copyright (1998) Australasian Ceramic Society

Science.gov (United States)

Several commercially available capacitors were evaluated at the liquid nitrogen temperature (77 K). Our primary interest was their performance under a bias voltage when used as DC link capacitors in cryogenic power electronics. In general, the performance of polymer capacitors and certain ceramic capacitors is almost independent of the temperature, DC bias, and frequency. On the other hand, ceramic capacitors based on high dielectric constant materials showed a strong dependence on the boundary conditions. Aluminum electrolytic capacitors showed a dramatic decrease of capacitance at 77 K, possibly due to the electrolyte being frozen and therefore losing its conductivity.

British Library Electronic Table of Contents (United Kingdom)

Purpose - This paper aims to describe the technology and applications of nanocomposite materials. Design/methodology/approach - This paper discusses products, applications and technological developments in polymer, ceramic and metal nanocomposites. It concludes with a brief consideration of electronic component applications. Findings - It is shown that polymer nanocomposites and the materials used in their production are commercially available and finding applications in several industries, including automotive, military, food, electronics and leisure, due to their enhanced mechanical, electrical and thermal properties. Ceramic and metallic nanocomposites are at an earlier stage of development and a critical issue to resolve is optimising the dispersion of nanomaterials in the matrices. Pa...

International Nuclear Information System (INIS)

(Pb_1_-_x La_x) (Zr_0_._6_5 Ti_0_._3_5) ceramics, with x = 0.09 (PLZT 9/65/35) were prepared using lead monoxide (Pb O) with different amount of litharge (tetragonal) and massicot (orthorhombic) phases. Results, based on x-ray diffraction patterns, remanent polarization and dielectric measurements, show that the Pb O polymorphic phase does not change the final structure of the PLZT but causes changes on the remanent polarization and dielectric permittivity temperature dependence. (author). 11 refs, 2 figs, 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

The objective of this contract is to research, develop and demonstrate a novel ceramic membrane reactor system for the low-cost conversion of natural gas to synthesis gas and hydrogen for liquid transportation fuels: the ITM Syngas process. Through an eight-year, three-phase program, the technology will be developed and scaled up to obtain the technical, engineering, operating and economic data necessary for the final step to full commercialization of the Gas-to-Liquids (GTL) conversion technology. This report is a summary of activities through February 1999.

Energy Technology Data Exchange (ETDEWEB)

The purpose of this memo is to give an update on our work on ceramic laser materials--feasibility proposal 04-FS-006. Transparent ceramic materials have several major advantages over single crystals in laser applications including, ease and robustness of manufacturing, large apertures, design flexibility, fracture toughness, high activator concentrations, uniformity of composition, no residual stress, and others discussed in the proposal. After a decade of working on making transparent YAG:Nd in 1995 Japanese workers demonstrated samples for the first time that performed as well in lasers as their single crystal counterparts. Since then several laser materials have been made and evaluated. For these reasons, developing ceramic laser materials is the most exciting and futuristic materials topic in today's major solid-state laser conferences. The highlights and executive summary of our work to date are: (1) Ordered a ...

Energy Technology Data Exchange (ETDEWEB)

The Externally-Fired Combined Cycle (EFCC) offers a method for operating high-efficiency gas and steam turbine combined cycles on coal. In the EFCC, an air heater replaces the gas turbine combustor so that the turbine can be indirectly fired. Ceramic materials are required for the heat exchange surfaces to accommodate the operating temperatures of modern gas turbines. The ceramic air heater or heat exchanger is the focus of this program, and the two primary objectives are (1) to demonstrate that a ceramic air heater can be reliably pressurized to a level of 225 psia (1.5 MPa); and (2) to show that the air heater can withstand exposure to the products of coal combustion at elevated temperatures. By replacing the gas turbine combustor with a ceramic air heater, the cycle can use coal or other ash-bearing fuels. Numerous programs have attempted to fuel high efficiency gas turbines directly with coal, often ...

Energy Technology Data Exchange (ETDEWEB)

Grain refinement behavior of copper alloys cast in permanent molds was investigated. This is one of the least studied subjects in copper alloy castings. Grain refinement is not widely practiced for leaded copper alloys cast in sand molds. Aluminum bronzes and high strength yellow brasses, cast in sand and permanent molds, were usually fine grained due to the presence of more than 2% iron. Grain refinement of the most common permanent mold casting alloys, leaded yellow brass and its lead-free replacement EnviroBrass III, is not universally accepted due to the perceived problem of hard spots in finished castings and for the same reason these alloys contain very low amounts of iron. The yellow brasses and Cu-Si alloys are gaining popularity in North America due to their low lead content and amenability for permanent mold casting. These alloys are prone to hot tearing in permanent mold casting. Grain refinement is one of the solutions for reducing this problem. However, to use this ...

International Nuclear Information System (INIS)

All stable even-A molybdenum isotopes and sup(90,92)Zr have been investigated with the (d, "6Li) reaction at Esub(d) = 45 MeV to study proton- and neutron-pair correlations. Differential cross sections were measured for states up to Esub(x) = 3 MeV in "8"6Sr, sup(88,92,94,96)Zr and up to 6 MeV in "8"8Sr and "9"0Zr. Particular attention was paid to the comparison of #alpha#-pickup data with two-nucleon pickup data. The population of low-lying 0"+ and 5"- states for two-neutron and four-nucleon pickup reactions was calculated using simple phenomenological wave functions for the initial and final states. The results of these calculations are in satisfactory agreement with the data. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The distribution of the alkaline earth elements strontium and barium between the solid phases of phosphates of transition elements of group 4 and chloride melts was studied. The distribution coefficients of strontium and barium were found at T = 700-800/sup 0/C. Phosphates of the type NaM/sub 2//sup (IV)/(PO/sub 4/)/sub 3/, where M/sub (IV)/ represents titanium, zirconium, and hafnium, were used as the solid phases. It was established that there is an enrichment of the precipitates with the distributed components. The distribution coefficient depends on the nature of the solid phase and the temperature. It was suggested that M/sup (II)/ x M/sub 4//sup (IV)/(PO/sub 4/)/sub 6/ is formed in processes of distribution, where M/sup (II)/ represents Sr, Ba.

British Library Electronic Table of Contents (United Kingdom)

Spherical nano-sized YSZ (yttria stabilized ZrO2) powders were successfully synthesized via a reverse microemulsion system. The water droplets in the microemulsion system of yclohexane/water/span85/Triton X-100/hexyl alcohol can act as the nano-reactors which solubilize zirconium oxychloride and ammonia water separately. The minute original reactors are favor to the formation of nano-sized spherical YSZ powders and the dispersibility of the powders can be controlled effectually by adjusting the weight ratio of the LiNO3 molten salt to the precursor. The phase transformation from cubic to monoclinic starts at and 500??C and finally monoclinic and cubic phase with increased crytallinity coexist at 800??C. The effect of LiNO3 molten salt in the formation of YSZ powders was also discussed.

International Nuclear Information System (INIS)

Zirconium alloys have anisotropic mechanical properties depending on their physical orientations and are widely used as nuclear materials such as cladding tube material. An operation condition of the nuclear reactor requires a high creep resistance, because it is subjected to long period operations, high temperature and high pressure. Generally, it takes a few days or months to do the creep experiment, so it is difficult to get a data in short period. However, there is a way to predict a creep property by using the stress-relaxation in the short term. These studies realized the stress-relaxation through a compressive test of HANA-6 (Zr-1.1Nb-0.05Cu) alloy that was developed by KAERI (Korea Atomic Energy Research Institute), and then predicted the creep property

Energy Technology Data Exchange (ETDEWEB)

The project is intended to yield information on the transfer factors describing the transfer of ingested radionuclides to breast milk for the following elements: antimony, cerium, chromium, cobalt, gallium, lanthanum, molybdenum, niobium, radium, ruthenium, silver, thorium, titanium, and uranium. Those yet unknown or poorly known transfer factors are required in order to be able to develop a reliable model for description and assessment of the transfer of the radionuclides and the possibly resulting hazardous doses to infants, and for subsequent formulation of recommendations for radiological protection of the population. (orig./CB) [German] Ziel des Projektes ist die Ermittlung von Transferfaktoren fuer den Uebergang von Radionukliden aus der Nahrung der Muetter in die Muttermilch fuer die Elemente Antimon, Cer, Chrom, Cobalt, Gallium, Lanthan, Molybdaen, Niob, Radium, Ruthenium, Silber, Thorium, Titan und Uran. Um die Exposition und damit die moegliche Gefaehrung ...

British Library Electronic Table of Contents (United Kingdom)

In this work, bismuth sodium titanate (Bi0.5Na0.5)TiO3 (BNT) and praseodymium (Pr)-doped BNT were successfully produced using the soft combustion technique. The effects of Pr doping on stoichiometry, microstructure, density and dielectric properties were studied. Pure Pr-doped BNT was obtained in all samples containing 5, 10 and 20mol% Pr after calcination at 800^oC for 3h. The produced powders were then pressed into pellets and sintered at 1100^oC for 3h. The very similar ionic radii of Pr^3^+ with Bi^3^+ and Na^+ made it possible to substitute both Bi and Na. The crystallite size and grain size decreased with increasing Pr amount because Pr acted as grain growth inhibitor, both for calcined powders and for sintered pellets. Maximum density was obtained in 5mol% Pr-doped BNT, beyond which...

International Nuclear Information System (INIS)

Praseodymium-doped Bi_4Ti_3O_1_2 (BIT) with various compositions of dopant, Pr (x = 0.5, 0.6, 0.7, 0.8) in Bi_4_-_xPr_xTi_3O_1_2 (BPT) were synthesized using a low temperature wet chemical technique. Powders calcined at 800 deg. C exhibit a single phase polycrystalline perovskite bismuth-layered structure. Randomly oriented plate-like structures were observed under Scanning Electron Microscope (SEM). A small amount of Pr doping (x = 0.5) resulted in dramatically reduced of grain size from 2 #mu#m to less than 50 nm in which Pr plays the role as a grain growth inhibitor. However, by increasing the composition of Pr, bigger grain size of up to 1 #mu#m was observed for x = 0.8 that was caused by diffusion of Pr in the perovskite structure. Dielectric properties showed that dielectric permittivity decreased with the addition of x = 0.50, and increasing with further addition of Pr. Dissipation factor (tan #delta#) followed the same trend as dielectric constant that was attributed to the ...

Energy Technology Data Exchange (ETDEWEB)

Stearic acid gel is employed to study the phase evolution of MgTiO{sub 3} nanoparticles by thermal gravimetric analysis, X-ray diffraction, and Fourier transform infrared. During the preparation of stearic acid gel, tetrabutyl titanate easily absorbed moisture to hydrolyze into Ti(OH){sub 4} firstly, and then reacts with stearic acid and magnesium stearate to form magnesium-titanium oxide network polymer gel, meanwhile n-butanol is generated. When stearic acid gel is calcined in air, a series of oxidation and combustion reactions occur, meanwhile apparent heat is given off. The results show that a metastable intermediate phase Mg{sub 2}TiO{sub 4} is generated at 450 {sup o}C and nearly disappeared at 550 {sup o}C. Simultaneously, a new solid phase of MgTiO{sub 3} appears. The metastable intermediate phase Mg{sub 2}TiO{sub 4} is successfully identified in the current work.

International Nuclear Information System (INIS)

The local environment of Ca dopants in barium titanate, BaTiO_3, is investigated by Ca K-edge X-ray absorption near-edge structure (XANES) spectroscopy. In conjunction with experiments, first-principles calculations by two methods are systematically made. The projector-augmented wave (PAW) method is used to optimize the local structure and obtain the formation energy. The augmented plane wave plus local orbitals method is adopted to obtain theoretical XANES spectra. A comparison between experimental and theoretical XANES spectra shows that Ca dopants are located at the Ba"2"+ sites forming Ca"2"+. Formation energy calculations of Ca doped BaTiO_3 by the PAW method also give the same results. The Ca atom in BaTiO_3 is off-centering in comparison with the Ba site in BaTiO_3. The off-centering of Ca atom is newly revealed by the combination of XANES spectroscopy and first-principles DFT calculations.

International Nuclear Information System (INIS)

The irradiation behavior of Li_2TiO_3 under a fusion reactor environment was simulated by simultaneous irradiation of Li_2TiO_3 by the triple ion beams and the respective single ion beams of O"2"+, He"+ and H"+. The microstructural changes in Li_2TiO_3 caused by the irradiation were measured by FT-IR photoacoustic spectroscopy. The results suggest that the amount of TiO_2 formed is proportional to the dpa and that the method of irradiation does not affect the dependence of formation of TiO_2. On the other hand, the amount of defects and/or radiolytic products generated by irradiation, which is considered to trap hydrogen near the surface, is found to be affected by the method of irradiation. Such phenomena are believed to affect the tritium release behavior from Li_2TiO_3, and durability of Li_2TiO_3 and compatibility of Li_2TiO_3 with other components of the breeder blanket such as structural materials in the fusion reactor system under operation.

Energy Technology Data Exchange (ETDEWEB)

This semiannual report for the period October 1983-March 1984 summarizes activities in Sandia National Laboratories' continuing program of coal liquefaction research. The primary goals are to: explore novel catalytic concepts and materials for conversion of coal to liquid fuels; determine the effects of process variables on catalyst deactivation; determine the effects of coal structure and solvent properties on low temperature dissolution; study the kinetics and catalysis of hydrogen transfer reactions; develop an understanding of slurry gelling phenomena; and provide a technical assessment of coal liquefaction processes. During this period, work was performed on: the use of pyrene as a chemical probe of catalyst activity; analysis of catalysts from Wilsonville run 242 using ESCA; atmospheric pressure model compound activity testing of regenerated catalysts from Wilsonville run 242; base displacement experiments with a coal-indole complex; preliminary hydrogenation tests with ...

International Nuclear Information System (INIS)

Lead 203 has been used as a tracer for lead in the field of nuclear medicine for several years. It is produced in a cyclotron usually by proton or deuteron bombardment of a thallium target principally by the p,n or d,2n reaction on "2"0"3Tl or the p,3n or d,4n reaction on "2"0"5Tl. Several different methods have been reported for the separation of "2"0"3Pb from the thallium target. These generally involve a combination of precipitation and solvent extraction techniques. A new method has been developed for the separation of Pb from Tl using ion exchange chromatography over hydrous zirconium oxide (HZO). Lead is taken up by this inorganic ion exchanger at pH > 3 whereas Tl(I) is not. Lead can subsequently be eluted with acid of pH 1-1.5. The recovery of "2"0"3Pb has been approximately 75% and the Tl impurity level has not been in excess of 10 ppm. Reference is made to the application of this separation method to the preparation of "2"0"1Tl from the reaction ...

International Nuclear Information System (INIS)

Immobilization of long-lived fission products (LLFP) such as radioactive Tc, Cs and Sr into #alpha#-SiAlON ceramics was evaluated using stable isotopes instead of radioactive isotopes, and the applicability of #alpha#-SiAlON ceramics as the inert matrix for transmutation of LLFP was investigated. In the case of single addition of SrO, SrCO_3, Cs_2CO_3 or ReO_2 to the starting materials, #alpha#-SiAlON, single phase was not formed after hot-pressing. When Y_2O_3 was added with SrO, SrCO_3 or Cs_2CO_3 to the starting materials (#alpha#-Si_3N_4, AlN and #alpha#-Al_2O_3) in optimum compositions, #alpha#-SiAlON single phase was obtained after hot-pressing at 1700degC or 1800degC. From the EDS analysis, Sr and Y were detected from grains. It is suggested that Y would assist the expansion of interstices of #alpha#-SiAlON lattice, resulting in the incorporation of Sr"2"+ into #alpha#-SiAlON lattice. In the case of Cs addition with Y, Cs was not ...

Energy Technology Data Exchange (ETDEWEB)

A radioactive Waste Incineration System (WIS) with suspension combustion is noticed as effective volume reduction technology of low level radiactive wastes that are increasing every year. In order to demonstrate the decontamination efficiency of ceramic filter used on WIS, this test has been carried out with the test facilities as joint research of Central Research Institute of Electric Power Industry (CRIEPI) and Sumitomo Heavy Industries, Ltd. Miscellaneous combustible waste and power resin, to which 5 nuclides (Mn-54, Fe-59, Co-60, Zn-65, Cs-137) were added, were used as samples for incineration. As the result of the test, it was verified that Decontamination Factor (DF) of the single stage ceramic filter was usually kept over 10/sup 5/ for every nuclide, and from the results of above DF, over 10/sup 8/ is expected for real commercial plant as a total system. Therefore, it is realized that the off-gas clean up system of the WIS composed of ...

International Nuclear Information System (INIS)

In this letter a method to estimate the visco-elastic response of monolithic ceramics to cyclic loading conditions at high temperatures is proposed. A relation is observed between the visco-elastic energy dissipation measured for two silicon nitride materials, and the structural characteristics of their respective intergranular phases. Some consequences for the fatigue resistance of the tested materials, and of non-transforming monolithic ceramics in general, are discussed. Two batches (G for glassy and C for crystalline) of SiAlON have been studied. The G-batch is obtained by pressureless sintering of silicon nitride powder with Y_2O_3 (6 wt%) and 6AlN-SiO_2 (5 wt%) as sintering additives. The main phase after sintering is #beta#-sialon. Upon cooling from the sintering temperature the amorphous intergranular residues of the sintering additives and of SiO_2, which is unavoidably present as a thin layer on the silicon nitride powder, crystallize ...

International Nuclear Information System (INIS)

The design of solid breeder blankets is strongly affected by the low values of thermal conductivity and density of ceramic breeder pebble beds. A significant rise of both quantities would enhance the thermal performance and lead to an increased tritium breeding ratio. In order to improve these quantities pretreated lithium orthosilicate pebble material was dry pressed and subsequently sintered. The thermal conductivity of cylindrical pellets was determined by the heat pulse method using a laser flash device. A pebble bed characteristic sample was also investigated in order to check the measurement accuracy in comparison with previous results. Furthermore, two samples of low density cellular ceramics were also prepared by infiltration of polymer foams with a ceramic slurry. The thermal conductivity results show that the values are affected both by the particle size and the sample density. Thermal conductivity values of ...

Energy Technology Data Exchange (ETDEWEB)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

Energy Technology Data Exchange (ETDEWEB)

The meeting was arranged into the following sessions: introductory; advanced ceramics and ceramic composites; ceramic and metal matrix composites; electronic materials and devices; acoustoelasticity, stress, and texture; composites-porosity, strength, and UT propagation; process modeling and monitoring; thermal wave physics; material properties, composites, surfaces, and interfaces; acoustic emission; ferromagnetic materials; new sensors; NDE reliability assessment; elastic wave scattering and propagation; image analysis, data storage, and signal processing; UT transducers; weldments and bonded materials; eddy current models; unified life cycle engineering; x rays, CT, and NMR; eddy current probes and instruments; acoustic microscopy imaging, and reconstruction; signal processing, measurement techniques, and systems; NDE applications of artificial intelligence; crack behavior influenced by history; inversion procedures for ...

Energy Technology Data Exchange (ETDEWEB)

Ceramics with composition Ba{sub 1-x}Na{sub x}Ti{sub 1-x}Nb{sub x}O{sub 3} are of either classical ferroelectric (for 0{<=}x<0.075) and ferro- or antiferroelectric (for 0.55<x{<=}1) or relaxor ferroelectric type (for 0.075{<=}x{<=}0.55), the transition at T{sub c} being only diffuse without any frequency dispersion for this last region. All the corresponding dielectric characteristics, i.e. diffusivity of the ferroelectric-paraelectric transition, frequency dispersion of {epsilon}{sub r}', shift of T{sub m} with frequency deviation from the Curie-Weiss law, are determined. The relaxor behaviour is more relaxor the more the composition deviates from BaTiO{sub 3} and NaNbO{sub 3}. This study is in the field of preparation of relaxor ceramics free from lead in the interest of the environment, which present a transition temperature close to room temperature. (author)

Energy Technology Data Exchange (ETDEWEB)

Aiming to realize ball bearings operable in a vacuum and under high temperature, silicon nitride (Si3N4) ceramic ball bearings were tested. The tested ball bearings were angular contact ball bearings composed of silicon nitride with sputtered molybdenum disulfide coating using a retainer of hot-pressed self-lubricating composite material. The time variation of the frictional torque was examined for the operations under the conditions at 500{degree}C in a vacuum at a rotational speed of 600 rpm and 50N thrust load for 5{times}10{sup 7}revolutions (1400 hours) and for 1.5{times}10{sup 8}revolutions (4200 hours). Excellent tribological performance was obtained. The ball bearings are lubricated with the molybdenum disulfide film at the initial stage of the operation and with a transfer film formed from the retainer material to the balls. In a test at 650{degree}C, low and stable frictional torque was observed up to 500 hours of operation as of the 500{degree}C test, no ...

International Nuclear Information System (INIS)

Carbide ceramics such as boron carbide due to their unique properties such as low density, high refractoriness, and high strength to weight ratio have many applications in different industries. This study focuses on direct bonding of boron carbide for high temperature applications using nickel interlayer. The process variables such as bonding time, temperature, and pressure have been investigated. The microstructure of the joint area was studied using electron scanning microscope technique. At all the bonding temperatures ranging from 1150 to 1300degC a reaction layer formed across the ceramic/metal interface. The thickness of the reaction layer increased by increasing temperature. The strength of the bonded samples was measured using shear testing method. The highest strength value obtained was about 100 MPa and belonged to the samples bonded at 1250 for 75 min bonding time. The strength of the joints decreased by increasing the bonding ...

International Nuclear Information System (INIS)

A family of sealant materials has been developed for use in the solid oxide fuel cell (SOFC) and in other applications in the temperature range of 800 endash 1000 degree C. These materials are based on glasses and glass-ceramics in the SrO endash La_2O_3 endash Al_2O_3 endash B_2O_3 endash SiO_2 system. The coefficients of thermal expansion (CTE) for these materials are in the range of 8 endash 13x10"-"6/degree C, a good match with those of the SOFC components. These sealant materials bond well with the ceramics of the SOFC and, more importantly, form bonds that can be thermally cycled without failure. At the fuel cell operating temperature, the sealants have viscosities in the range of 10"4-10"6 Pa-s, which allow them to tolerate a CTE mismatch of about 20% among the bonded substrates. The gas tightness of a sample seal was demonstrated in a simple zirconia-based oxygen concentration cell. copyright 1996 Materials Research Society.

International Nuclear Information System (INIS)

4.82 wt% AIN and 2.98 wt% Y_2O_3 were added to Si_3N_4 as sintering agents in order to have #alpha#_Sialon composition of x=0.15 and monoclinic ZrO_2 between 0 to 10 wt% was admixed with Si_3N_4 based ceramics were fabricated by hot-pressing at 1,750 deg C for 90 min under 30 MPa in argon and nitrogen atmospheres effects of sintering atmospheres and addition of ZrO_2 on mechanical properties of Si_3N_4 based ceramics were investigated. As ZrO_2 content increased, the fraction of #alpha#-Sialon tended to decrease and the amount of cubic ZrO_2 increased because Y_2O_3 acted as the stabilizer of ZrO_2. The sintering atmospheres didn't affect on the sintering behavior and the product phases in hot-pressing of Si_3N_4. Bending strength increased when ZrO_2 content. ZrO_2 didn't contribute to the increase of fracture toughness because stabilized cubic ZrO_2 was produced by the added Y_2O_3. (Author).

International Nuclear Information System (INIS)

The effects of Fe and B_4C on the sintering behavior and mechanical properties of TiB_2 ceramics have been studied. Sintering was performed in an Ar atmosphere at 2000 degrees C using attrition-milled TiB_2 powder. When a small amount of Fe (0.5 wt%) was added, abnormal grain growth occurred and the sintered density was low. In the case of B_4C added along with 0.5 wt% Fe, however, abnormal grain growth was remarkably suppressed, and the sintered density was increased up to 95% of theoretical. But with excess Fe addition (5 wt%), B_4C grains did not act as a grain growth inhibitor, and B_4C grains were frequently trapped in large TiB_2 grains. The best mechanical properties were obtained for the TiB_2-10 wt% B_4C-0.5 wt% Fe ceramics, which exhibited a three-point bending strength of 400 MPa and a fracture toughness of 5.5 MPa #centre dot# m"1"/"2.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem The use of titanium has increased for metal ceramic restorations, as well as for use in titanium implants, with developments in CAD/CAM technology. Some surface treatments of titanium have been introduced to enhance the titanium bond strength to low-fusing porcelains; however, a more reliable, easily used dental laboratory method has not been established. Purpose The purpose of this study was to compare the effect of laser etching as a titanium surface treatment with 3 other surface treatments (machining, airborne-particle abrasion, and acid etching), evaluating their ability to enhance the bond strength between a titanium substrate and porcelain. Material and methods A total of 64 specimen rods of commercially pure titanium (ASTM grade 2, 20 mm in length and 5.7 mm in...

International Nuclear Information System (INIS)

Ceramic fuel element is one of the most important items of HTGR technology, and the corrosion resistance of is matrix materials is vital to the operational performance of HTGR. In the paper, based on the oxidation study of the matrix materials, it has been proposed that the corrosion resistance of the matrix materials might be improved through forming carbon -ceramic composite. The experiment results have shown that the corrosion resistance of matrix materials has been improved by addition of SiC superfine powders, and that the matrix materials containing SiC superfine powders and heat-treated at 1600 deg. C had an oxidation rate lower than the general one containing no SiC superfine powder and heat-treated at 1950 deg. C. (author). 5 refs, 8 figs.

British Library Electronic Table of Contents (United Kingdom)

Porous ?-SiAlON ceramics are synthesized by reaction bonded method using hollow alumina spheres (HASs) as both sintering aids and pore-forming agents. Both micropores and macropores, which are constructured by SiAlON grains with different morphologies, are formed in the final SiAlON samples. The micropores are three-dimentional, and are built by equiaxial grains. While the hollow macropores, which have the similar morphology to hollow alumina sphere, are packed by elongated grains. In the sintering process, the solid dissolution process takes place, giving rise to the different alumina concentration of liquid phase, and thus resulting in the formation of two kinds of grains, the equiaxial grain and the elongated grain.

International Nuclear Information System (INIS)

The electronic structure and optical properties in tetragonal ceramics PbTiO_3, are studied by using full-potential linearized augmented plane wave method in density functional theory with the generalized gradient approximation by WIEN2K package. The theoretical calculated optical properties and energy loss spectrum yield a static refractive index of 2.59 and a plasmon energy of 22.7eV for the tetragonal phase. The effective electron number at low energy saturates near 22-23eV with the value of 50 for the effective electron number. The results show a indirect band gap of 2.2eV at the I' point in the Brillouin zone. The :calculated band structure and density of states of PbTiO_3 agree with previous experimental and theoretical results.

International Nuclear Information System (INIS)

Conductive TiN/Si_3N_4 ceramic composites were processed by electrical discharge machining (EDM) and their microstructure and conductivity were investigated. The whole process of tool electrode wear is evaluated by sinker-EDM. The machined surfaces of TiN/Si_3N_4 ceramic composites were examined by scanning electron microscopy (SEM) and profilometry to determine the surface finish. The electrode wear rate of brass is higher than copper electrode for all EDMed tests. The surface texture was found to have greater dependence on pulse energy. It was observed that the sinker-EDM at higher pulse energy caused severe microdamage in the surface. The surface roughness (Ra) values also increase with increasing pulse energy.

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Titanium is the most biocompatible metal used for dental casting; however, there is concern about its marginal accuracy after porcelain application since this aspect has direct influence on marginal fit. Purpose The purpose of this study was to determine the effect that metal selection and the porcelain firing procedure have on the marginal accuracy of metal ceramic prostheses. Material and methods Cast CP Ti, milled CP Ti, cast Ti-6Al-7Nb, and cast Ni-Cr copings (n=5) were fired with compatible porcelains (Triceram for titanium-based metals and VITA VMK 95 for Ni-Cr alloy). The Ni-Cr alloy fired with its porcelain served as the control. Photographs of metal copings placed on a master die were made. Marginal discrepancy was determined on the photographs using an image ...

Energy Technology Data Exchange (ETDEWEB)

A pillbox RF output window was developed for the L-band pulsed klystron for the Japanese Hadron Project (JHP) 1-GeV proton linac. The window was designed to withstand a peak RF power of 6 MW, where the pulse width is 600 {mu}sec and the repetition rate is 50 Hz. A high power model was fabricated using an alumina ceramic which has a low loss tangent of 2.5x10{sup -5}. A high power test was successfully performed up to a 113 kW RF average power with a 4 MW peak power, a 565 {mu}sec pulse width and a 50 Hz repetition rate. By extrapolating the data of this high power test, the temperature rise of the ceramic is estimated low enough at the full RF power of 6 MW. Thus this RF window is expected to satisfy the specifications of the L-band Klystron. (author).

Energy Technology Data Exchange (ETDEWEB)

The purpose of the present study is to develop a new method for chemical state analysis by means of EPMA(Electron probe microanalyser). The measured X-ray intensity of Si-K{beta} characteristic X-ray spectra were read-out by a 16 bit microcomputer with a RS-232C interface. And using the curve fitting method the quantitative analysis of chemical compositions in a ternary compound that constituted of the same element has been established. The present method was applied to analyse of the friction and wear properties of Si-base ceramics sliding materials. It was found that the wear debris contains both the compositions of the sliding materials and SiO{sub 2}, and the SiO{sub 2} contents in wear debris was changed with relative humidity. The results clearly showed that the proposed method is very useful for determing the compositions in the ternary compound. (author).

Energy Technology Data Exchange (ETDEWEB)

A combination of erosion and corrosion at the Victoria Junction coal preparation plant in Sydney, Nova Scotia was causing serious problems. Schedule 80 mild steel pipes were starting to fail as well as some quarter-inch steel plates in the lauders and chutes. Some corrosion tests were carried out and the high chloride level in the process water was felt to be the single most important contribution to the corrosion problem. Cast basalt was selected as a solution to the pipe wear problem. Three different types of abrasion/corrosion-resistant tiling - basalt tiles, kalceram tiles and ceramic tiles were well suited to the chloride conditions at this plant.

Energy Technology Data Exchange (ETDEWEB)

Hybrid vehicles have two power supplies as engine and electric motor which are used most efficiently corresponding to objects respectively to attain energy-saving and low pollution. In this paper, factors concerning the fuel economy of hybrid vehicles and potential thereof are examined, and the possibility of reducing fuel cost by half is described. As possible modes of highly efficient hybrid vehicles, series hybrid vehicles (SHEV) of conventional internal combustion engine, parallel hybrid vehicles using EV in combination, series-parallel hybrid vehicles (SPHV), series type fuel cell type vehicles, ceramic engine-turbo compound power generating SPHV as well as SHEV, and ceramics gas turbine engine power generating SHEV are mentioned. 10 refs., 14 figs.

International Nuclear Information System (INIS)

Iron oxide as sintering aid to Ce-TZP ceramics produces a beneficial effect on the tetragonal phase stabilization. It was found that ceria powder particle size of 2,0 #mu#m turns the grain-boundary electrical conductivity higher than ceria powder of smaller grain size. (author)

British Library Electronic Table of Contents (United Kingdom)

In this paper, we present the photoluminescence properties of Pr3+-, Sm3+- and Dy3+-doped germanate glasses and glass ceramics. From the X-ray diffraction measurement, the host glass structure was determined. These glasses have shown strong absorption bands in the near-infrared (NIR) region. Compared to Pr3+-, Sm3+- and Dy3+-doped glasses, their respective glass ceramics have shown stronger emissions due to the Ba2TiGe2O8 crystalline phase. For Pr3+-doped glass and glass ceramic, emission bands centered at 530nm (3P03H5), 614nm (3P03H6), 647nm (3P03F2) and 686nm (3P03F3) have been observed with 485nm (3H43P0) excitation wavelength. Of them, 647nm (3P03F2) has shown bright red emission. Emission bands of 4G5/26H5/2 (565nm), 4G5/26H7/2 (602nm) and 4G5/26H9/2 (648nm) for the Sm3+:glass and gl...

International Nuclear Information System (INIS)

The cathodic vacuum arc provides a means of producing large currents of positive ions of a wide variety of materials. These ions can be utilized to produce coatings with improved properties such as higher density and adhesion. The processing is particularly useful in reactive deposition of ceramic coatings having excellent stoichiometry. In this review, emerging aspects of the technology are emphasized.

Energy Technology Data Exchange (ETDEWEB)

The method of production of xAl{sub 2}O{sub 3}-yTiO{sub 2} compositions provides for the depth distribution of coating components and specifies its mechanical properties. In case of the composition obtained by cladding, titanium is mainly concentrated at the substrate. In case of mechanical mixture or composition obtained by sintering the oxides, the depth distribution of coating components is random.

Energy Technology Data Exchange (ETDEWEB)

This investigation involves a study of the influence of key processing parameters on the heating of materials using microwave energy. Selective and localized heating characteristics of microwaves will be utilized in the sintering of ceramics without hydrostatic pressure. In addition, combustion synthesis will be studied for the production of powders, carbides, and nitrides by combining two or more solids or a solid and a gas to form new materials. The insight gained from the interaction of microwaves with various materials will be utilized in the mobilization and subsequent redeposition of uranium.

Energy Technology Data Exchange (ETDEWEB)

A 1000-watt CO/sub 2/ laser has been demonstrated as a reliable production machine tool for cutting of plastics, high strength reinforced composites, and other nonmetals. More than 40 different plastics have been laser cut, and the results are tabulated. Applications for laser cutting described include fiberglass-reinforced laminates, Kevlar/epoxy composites, fiberglass-reinforced phenolics, nylon/epoxy laminates, ceramics, and disposable tooling made from acrylic.

Science.gov (United States)

During four years of operation at the Central Receiver Test Facility (CRTF) ceramics have performed well in cyclic solar flux densities of less than 30 W/cm/sup 2/. Above 100 W/cm/sup 2/, serious limitations exist. Important application considerations include: the geometry, cyclic and long time exposures, flux density gradients, thermal shock, weathering, and soiling.

International Nuclear Information System (INIS)

This bibliography contains citations concerning the migration of food-packaging materials into foods. Plastic, glass, cardboard, metal, and ceramic containers are discussed. Techniques for analyzing packaging contamination are included. (Contains 90 citations fully indexed and including a title list.).

International Nuclear Information System (INIS)

Plasma immersion ion implantation (PIII) is an effective materials modification and synthesis technique but has seldom been applied to ceramic materials due to the high electrical resistance that reduces the ion bombardment energy and sometimes causes serious electrical arcing in the instrument. Even in cases where PIII is applicable, the surface properties of the implanted insulating materials can be seriously affected due to the low ion energy and materials damage from electrical arcing. In order to enhance the surface and mechanical properties such as wear resistance of ceramic materials used in many industrial applications, surface modification is needed. In this work, we conduct carbon implantation into sintered #alpha#-SiC (silicon carbides that are widely used in vacuum ceramic bearings) using mesh-assisted plasma immersion ion implantation to enhance the surface properties. The use of a conducting grid is ...

Energy Technology Data Exchange (ETDEWEB)

A necessary condition for crevice corrosion is that a crevice former create a sufficiently tight, restricted geometry on the metal surface to support the development of critical crevice chemistry. Crevice corrosion is affected by the crevice geometry (tightness) and the properties of the crevice former. The objective of this study is to determine the effect of the crevice former material on the evolution of localized corrosion-damage. A standard crevice corrosion test method is modified by (a) the use of ceramic, metal or polymer materials as the crevice former and (b) the variation of size and shape of the crevice. This study focuses on the post initiation stage of crevice corrosion and addresses factors that may limit the initiation of localized corrosion and also slow or stop the continued propagation of corrosion. Controlled crevice corrosion tests are performed under aggressive, accelerated conditions on Ni-Cr-Mo alloy C-22 and other alloys for comparison. ...

Energy Technology Data Exchange (ETDEWEB)

The resulting emissions of the firing of ceramic products of all type are described, the factors are enumerated to diminish the emissions in the kilns and the technologies applied in the kilns to reduce these emissions while carrying out energy saving are described briefly. (author)

International Nuclear Information System (INIS)

Uranium-aluminum alloys with a significant enrichment of uranium with "2"3"3U or "2"3"5U serve as nuclear fuels in research reactors. The quality assurance of this fuel requires, among other things, precise knowledge that all trace metal constituents that affect neutron economy, fuel integrity, and fuel fabrication process parameters are well within the specification limits. Trace metal characterization of "2"3"5U-Al alloy has been carried out by atomic spectrometry. The trace metal constituents of interest are grouped into common metals (silver, boron, calcium, cadmium, cobalt, chromium, copper, iron, magnesium, manganese, molybdenum, sodium, nickel, lead, silicon, tin, titanium, vanadium, tungsten, and zinc) and lanthanides (cerium, dysprosium, europium, gadolinium, holminium, lutetium, samarium, and terbium). The elements yttrium and zirconium are grouped with the latter in view of the chemical separation procedure used. The alloy samples are dissolved in 6 M ...

International Nuclear Information System (INIS)

The present design of Blanket Shield and Primary Wall for ITER envisages construction of the wall with a water cooled, stainless steel outer layer and a water cooled, copper liner on the inside plasma facing surface. Protection of the inner copper surface with an armour layer is necessary to cope with plasma to wall interaction. There are a number of armour materials under consideration, for this project beryllium was used. The scope of work was to produce a series of mock-ups, each consisting of a different combination of materials, which included Dispersion Strengthened Copper, Copper-Chrome-Zirconium alloy, Beryllium and Stainless Steel. Hot Isostatic Pressing (HIP) was the method used to ensure that a fully diffused bonded joint was achieved giving the necessary strength and thermal conductivity. The first five of the mock ups have been successfully completed and are being tested at the various laboratories in Europe. The remaining mock ups are awaiting the ...

Energy Technology Data Exchange (ETDEWEB)

A type of mesoporous ZrO{sub 2} was synthesized and its phosphate removal potential was investigated in this study. The adsorption isotherm, pH effect, ionic strength effect and desorption were examined in batch experiments. The adsorption data fitted well to the Langmuir model with which the maximum P adsorption capacity was estimated to be 29.71 mg P/g. The amount of phosphate adsorbed increased rapidly in the first 5 h and slowly towards the end of the run, suggesting the possible monolayer coverage of phosphate ions on the surface of the adsorbent. The phosphate adsorption tended to increase with a decrease of pH and an increase of ionic strength. A phosphate desorbability of approximately 60% was observed with 0.5 M NaOH, which indicated a relatively strong bonding between the adsorbed PO{sub 4}{sup 3-} and the sorptive sites on the surface of the adsorbent. The immobilization of phosphate probably occurs by the mechanisms of ion exchange and physicochemical attraction. Due to its ...

Energy Technology Data Exchange (ETDEWEB)

Propylene polymerizations were carried out with {phi}{sub 2}C(Flu)(Cp)ZrCl{sub 2} and SiMe{sub 2}(Ind)2ZrCl{sub 2} catalysts supported on silica, zeolite sodic mordenite (NaM) and acid mordenite (HM). The polymerizations were performed at different temperatures and varying aluminium/zirconium molar ratios ([Al]/[Zr]). The effect of these reaction parameters on the catalyst activity was investigated using a proposed statistical experimental planning. In the case of f{sub 2}C(Flu)(Cp)ZrCl{sub 2}, SiO{sub 2} and NaM were used as support and the catalyst performance evaluated using toluene and pentane as polymerization solvent. The molecular weight, molecular weight distribution, melting point and crystallinity of the polymers were examined. The results indicate very high activities for the syndiospecific heterogeneous system. Also, the polymers obtained had superior Mw and stereo regularity. (author)

International Nuclear Information System (INIS)

The corrosion resistance of zircaloy is affected by conditions of heat treatment in the manufacturing steps to be formed into a final product as a structural material. In the manufacturing method of the present invention, a Zr alloy controlled to contain Sn: 0.8 to 1.2wt%, Fe: 0.17 to 0.28wt%, Cr: 0.05 to 0.15wt%, Ni: 0.04 to 0.10wt%, Nb: 0.01 to 0.09wt%, oxygen: 1,000 to 1,500ppm and Si, an Si impurity at a concentration of 120ppm or less and balance of Zr is melted into a cast piece, to which #beta# hardening is applied. Then, rolling and annealing treatment are applied so that the total heat input amount to the material: #SIGMA#Ai ranges from 1 x 10"-"1"9 to 1 x 10"-"1"7. With such procedures, a Zr alloy structural material for a reactor core having excellent homogeneous corrosion resistance and hydrogen absorption resistance for a long period of time while having a sufficient strength can be obtained even in a case where Sn content is relatively low as from 0.8 to 1.2wt%. (T.M.).

International Nuclear Information System (INIS)

Three types of titanium hydrides have been reported: #delta#, #epsilon# and #gamma# hydrides. The #delta# hydride forms in the composition range from TiH/sub 1.5/ to TiH/sub 1.99/ and has a CaF/sub 2/ structure with metal atoms on an fcc lattice and hydrogen atoms randomly occupying tetrahedral interstitial sites. At higher hydrogen concentrations, TiH/sub 2/, the fct (c/a # #epsilon# transformation is apparently diffusionless, similar to that operating in the cubic/tetragonal transformation in zirconium hydride. The metastable fct #gamma# hydride having a c/a value of 1.09 or 1.12 forms from solid solutions of hydrogen in the hcp #alpha# matrix. While the titanium hydride precipitation in #alpha#-Ti and its alloys has attracted extensive investigation, hydride formation in bcc #beta#-Ti alloys has rarely been studied because they have not been thought to be liable to hydride formation. This paper shows conclusive evidence for the fcc #delta# hydride phase ...

British Library Electronic Table of Contents (United Kingdom)

The electroreduction process of Zr(IV) was studied at molybdenum electrode in LiCl-KCl-K2ZrF6 molten salt. The transient electrochemical techniques, such as cyclic voltammetry and chronopotenimetry were used. The experimental results showed that the electrochemical reduction of Zr(II)/Zr and Zr(IV)/Zr(II) were both diffusion-controlled process. In the 773-973K range, the diffusion coefficients of Zr(ii) and Zr(IV) were determined: DZr(II)=0.15567exp{-69.65x10^3RT(K)}cm^2/s, DZr(IV)=1.09x10^-^4exp{-44.39x10^3RT(K)}cm^2/s. The activation energy values for the diffusion process were 69.65kJ/mol and 44.39kJ/mol, respectively.

International Nuclear Information System (INIS)

During 17 years since the start of operation of the first commercial LWR in Japan, many LWRs have experienced various corrosion damages, but the causes of them were clarified, and the counter-measures were executed effectively in actual plants, as the results, the cause of corrosion damage decreased remarkably, and now, the high rate of operation has become to be maintained. In this paper, the major cases of corrosion damage experienced in LWRs in Japan and foreign countries, the causes of them and the countermeasures, the problems of hereafter and so on are described. The corrosion damage of metallic materials in the environment of LWRs occurs in the parts in contact with high temperature, high pressure water and steam, such as stainless steel piping in the primary cooling system of BWRs, and nickel alloy heating tubes of steam generators, carbon steel feed water piping and zirconium alloy fuel cladding tubes in PWRs. Recently, accompanying the advance of LWR ...

Energy Technology Data Exchange (ETDEWEB)

This report describes experimental results for the selective removal of strontium and cesium from simulated waste solutions using monosodium titanate (MST) and crystalline silicotitanate (CST)-laden filter cartridges. Four types of ion exchange cartridge media (CST and MST designed by both 3M and POROX{reg_sign}) were evaluated. In these proof-of-principle tests effective uptake of both Sr-85 and Cs-137 was observed. However, the experiments were not performed long enough to determine the saturation levels or breakthrough curve for each filter cartridge. POREX{reg_sign} MST cartridges, which by design were based on co-sintering of the active titanates with polyethylene particles, seem to perform as well as the 3M-designed MST cartridges (impregnated filter membrane design) in the uptake of strontium. At low salt simulant conditions (0.29 M Na{sup +}), the instantaneous decontamination factor (D{sub F}) for Sr-85 with the 3M-design MST cartridge ...