International Nuclear Information System (INIS)

Zirconium-base alloys are used primarily as fuel cladding material and other core structure material in water cooled nuclear power reactors. Main research achievements and problems about corrosion of zirconium alloys are reviewed; the present theories and challenge are summarized. In the 1980s, great progress had been made towards correlating alloy composition, microstructure and irradiation with corrosion resistance. In the 1990s, main researches are focused on exploring actual mechanism of corrosion, optimizing both alloy composition and microstructure in order to minimize the fuel cycle costs through burnup optimization.

Science.gov (United States)

A number of alloys of zirconium have been investigated as part of a program aimed at improving the high-temperature tensile and creep strength of zirconium. These alloys include aluminum, beryllium, lead, magnesium, molybdenum, niobium, tantalum, tin, titanium, tungsten, vanadium, and zinc, binary and ternary alloys. The data indicate that aluminum, lead, molybdenum niobium, tin, titanium, tungsten, and vanadium can be used successfully to harden zirconium, and that aluminum, tin, titanium, and vanadium are particularly effective in maintaining the strength of zirconium at elevated temperatures.

Science.gov (United States)

The TTT diagrams describing the beta to alpha isothermal transformation have been made by isothermal dilatometry for pure uranium and 21 alloys based on chromium, silicon, molybdenum, iron, aluminium, zirconium. The thermal cycle preceeding the isothermal...

Energy Technology Data Exchange (ETDEWEB)

Grain refinement behavior of copper alloys cast in permanent molds was investigated. This is one of the least studied subjects in copper alloy castings. Grain refinement is not widely practiced for leaded copper alloys cast in sand molds. Aluminum bronzes and high strength yellow brasses, cast in sand and permanent molds, were usually fine grained due to the presence of more than 2% iron. Grain refinement of the most common permanent mold casting alloys, leaded yellow brass and its lead-free replacement EnviroBrass III, is not universally accepted due to the perceived problem of hard spots in finished castings and for the same reason these alloys contain very low amounts of iron. The yellow brasses and Cu-Si alloys are gaining popularity in North America due to their low lead content and amenability for permanent mold casting. These alloys ...

Energy Technology Data Exchange (ETDEWEB)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. This paper describes the roles on corrosion. A corrosion test on precipitate-containing and precipitate-free materials made from pure zirconium and a small quantity of iron and chromium, rest potential measurements on an intermetallic compound of Zr(FeCr){sub 2} and zirconium matrix, and a galvanic coupling test of those were performed. Results showed that corrosion behavior of zirconium alloys could be attributed to the electrochemical properties of intermetallic compounds precipitated in each alloy. Namely, the cathodic and anodic polarization characteristics were associated with anodic protection provided by the ...

International Nuclear Information System (INIS)

In association with periodic inspection of CANDU nuclear power plant components, Canadian Standards Association issued CSA N285.8 in 2005 as technical requirements for in-service evaluation of zirconium alloy pressure tubes in CANDU reactors. This first version, CSA N285.8 involves procedures for, firstly, the evaluation of pressure tube flaws, secondly, the evaluation of pressure tube to calandria tube contact and, thirdly, the assessment of a reactor core, and material properties and derived quantities. The evaluation of pressure tube flaws includes delayed hydride cracking evaluation the procedures of which are stipulated based on the existing delayed hydride cracking models. For example, the evaluation of flaw-tip hydride precipitation during reactor cooldown involves a procedure to calculate the equilibrium hydrogen equivalent concentration in solution at the flaw tip, Htipas follows: Htip=Hfexp[- (VH delta no.)/RT], ...

British Library Electronic Table of Contents (United Kingdom)

Flame propagating through zirconium particle cloud in a small-scale vertical rectangle chamber was investigated experimentally. In the experiments, the zirconium quoted 99% purity was used and the diameter of particles was distributed 1?22 ?m. The zirconium dust was dispersed into the chamber by air flow and ignited by an electrode spark. A high-speed video camera was used to record the images of the propagating flame. Micro-thermocouples, schlieren optical system and microscopic lens were used to obtain temperature profiles and flame structure, respectively. Based on the experimental results, flame propagation characteristics and flame structure of zirconium particle cloud were analyzed. The propagation velocity of the flame is quite slow in the initial 14 ms and then accelerates to maxim...

Energy Technology Data Exchange (ETDEWEB)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. In the previous paper, corrosion mechanism was elucidated by the anodic protection-precipitates degradation model. This paper describes the roles on hydrogen pickup. 633 K pure water autoclave test was performed on high purity zirconium, Zr-0.2Fe, Zr-0.2Cr, and Zr-0.1Fe-0.1Cr alloys. Hydrogen analysis after the corrosion test showed that hydrogen pickup ratio of Zr-0.2Fe alloy was about 80%. It was much higher than about 30% of pure Zr and about 10% of both Zr-0.2Cr and Zr-0.1Fe-0.1Cr alloys. Larger hydrogen content was introduced into Zr-0.2Fe alloy than the other ones by the cathodic hydrogen charging under ...

British Library Electronic Table of Contents (United Kingdom)

Zirconium and particularly Zr-2.5wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step pro...

Energy Technology Data Exchange (ETDEWEB)

An austenitic alloy having good thermal stability and resistance to sodium corrosion at 700.degree. C. consists essentially of 35-45% nickel 7.5-14% chromium 0.8-3.2% molybdenum 0.3-1.0% silicon 0.2-1.0% manganese 0-0.1% zirconium 2.0-3.5% titanium 1.0-2.0% aluminum 0.02-0.1% carbon 0-0.01% boron and the balance iron.

Energy Technology Data Exchange (ETDEWEB)

Using an expanded nuclear data base, the activation of nitrogen, aluminum, iron, nickel, copper, zirconium, niobium, molybdenum, tungsten, and lead were calculated for the first wall positions of the STARFIRE and MARS conceptual fusion reactors.

UK PubMed Central (United Kingdom)

BackgroundThe successful use of zirconia ceramics in orthopedic surgery led to a demand for dental zirconium-based implant systems. Because of its excellent biomechanical characteristics,...Full Text Available

International Nuclear Information System (INIS)

Ten different alloys of zirconium have been tested with regard to the effect of irradiation on their mechanical properties and their sensitivity to environmentally induced failure. Two different environments were used: iodine vapour and liquid cesium with an addition of 2% cadmium. The neutron dose was 10"2"1n/cm"2 (E>1MeV) and the irradiation temperature was about 300 degrees C. All alloy additions increased the irradiation hardening. Especially notable was the large effect of titanium and tin on irradiation hardening. A limited amount of transmission electron microscopy was carried out in order to find an explanation to the effects. The testing in different environments showed that there is no clear correlation between environmental sensitivity and yield stress. For materials of similar yield stress an alloyed material tends to be more sensitive to environmental cracking than a material which only ...

Energy Technology Data Exchange (ETDEWEB)

In this work, the ability of a number of Zr-containing intermetallic compounds with the Zr{sub 2}Me stoichiometry, including Zr{sub 2}Fe, Zr{sub 2}Ni, Zr{sub 2}Co and Zr{sub 4}Fe{sub 2}O{sub 0.6}, to participate in the Hydrogenation-Disproportionation-Desorption-Recombination process was investigated, revealing for the first time that the HDDR route can be employed successfully for all these compounds. 24 refs.

International Nuclear Information System (INIS)

... base alloys alloys beams chemical reactions elements hardness irradiation

J-STORE (Japan)

Full Text Available

International Nuclear Information System (INIS)

A zirconium alloy comprising from 0.8 to 1.6wt% of Sn, from 0.17 to 0.25wt% of Fe, from 0.15 to 0.25wt% of Cr and from 0.01 to 0.08wt% of Ni and Si at a concentration of 120ppm or lower as an impurity and the balance of Zr is melted into cast pieces and then subjected to an #beta# annealing. It is controlled so as to satisfy Fe + Cr + Ni #<=# 0.52wt%. Then, rolling and annealing are applied so that the total heat injection amount #SIGMA#A_i to the materials is within a range of from 1 x 10"-"1"9 to 1 x 10"-"1"7. #SIGMA#A_i = #SIGMA#t_i #centre dot# exp(-Q/RT_i), in which t_i represents processing time (hour) at an ith heat treatment step after the #beta# annealing, T_i represents a processing temperature (K) in the step i. Q represents an activating energy, R represents a gas constant, and Q/R 40,000. (I.N.).

Energy Technology Data Exchange (ETDEWEB)

The theoretical principles underlying the formation of oxide and, in particular, anodic oxide coatings on metals produced by chemical oxidation, anodizing in solutions, and anodizing in cold plasmas are reviewed. The mechanisms and conditions of anodic oxidation are described, and the structure of anodic oxide coatings on aluminum, magnesium, beryllium, zinc, cadmium, iron, cobalt, nickel, titanium, zirconium, tantalum, and chromium alloys is examined. Attention is also given to various applictins of anodized coatings. 54 references.

Energy Technology Data Exchange (ETDEWEB)

The aims of the present work were to investigate possible compatibility between sodium zirconium phosphate (NZP) and Synroc titanate phases, to prepare NZP-based waste forms by hot-pressing rather than sintering, and to investigate the incorporation in NZP of (a) Cs/Sr as simulated heat-generating nuclides; (b) simulated actinides; and (c) simulated Purex waste. The NZP samples were prepared by methods similar to those used for Synroc. The precursor NZP phase was formed from tetrabutyl zirconate Zr(OC{sub 4}H{sub 9}){sub 4}, sodium nitrate, and 85% orthophosphoric acid. Simulated waste nitrate solutions were then mixed with the liquid precursor. After stir drying of the precursor, calcination was carried out at 700{degree}C to remove nitrates and organics.

International Nuclear Information System (INIS)

Zirconium alloys have anisotropic mechanical properties depending on their physical orientations and are widely used as nuclear materials such as cladding tube material. An operation condition of the nuclear reactor requires a high creep resistance, because it is subjected to long period operations, high temperature and high pressure. Generally, it takes a few days or months to do the creep experiment, so it is difficult to get a data in short period. However, there is a way to predict a creep property by using the stress-relaxation in the short term. These studies realized the stress-relaxation through a compressive test of HANA-6 (Zr-1.1Nb-0.05Cu) alloy that was developed by KAERI (Korea Atomic Energy Research Institute), and then predicted the creep property

International Nuclear Information System (INIS)

The influence of various alloy elements on tensile strength of the eutectic, directionally solidified superalloy 73 C was determined. The tensile properties of the base alloy has been increased by Al, Y and C as alloying elements, while Ni and Ti showed a decreasing effect (alloy softening). However, ductility and thermo-fatigue behaviour had been influenced in a positive way by these elements. The specific meachanism caused by the different elements are discussed. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The processing characteristics, tensile properties, and oxidation response of two Nb-Ti-Al-Cr alloys were investigated. One creep tests at 650{degrees}C and 172 MPa was conducted on the base alloy which contained 40Nb-40-Ti-10Al-10Cr. A second alloy was modified with 0.11 at. % carbon and 0.07 at. % yttrium. Alloys were arc melted in a chamber backfilled with argon, drop cast into a water-cooled copper mold, and cold rolled to obtain a 0.8-mm sheet. The sheet was annealed at 1100{degrees}C for 0.5 h. Longitudinal tensile specimens and oxidation specimens were obtained for both the base alloy and the modified alloy. Tensile properties were obtained for the base alloy at room temperature, 400, 600, 700, 800, 900, and 1000{degrees}C, and for the modified alloy ...

International Nuclear Information System (INIS)

Uranium-aluminum alloys with a significant enrichment of uranium with "2"3"3U or "2"3"5U serve as nuclear fuels in research reactors. The quality assurance of this fuel requires, among other things, precise knowledge that all trace metal constituents that affect neutron economy, fuel integrity, and fuel fabrication process parameters are well within the specification limits. Trace metal characterization of "2"3"5U-Al alloy has been carried out by atomic spectrometry. The trace metal constituents of interest are grouped into common metals (silver, boron, calcium, cadmium, cobalt, chromium, copper, iron, magnesium, manganese, molybdenum, sodium, nickel, lead, silicon, tin, titanium, vanadium, tungsten, and zinc) and lanthanides (cerium, dysprosium, europium, gadolinium, holminium, lutetium, samarium, and terbium). The elements yttrium and zirconium are grouped with the latter in view of the chemical separation procedure used. ...

International Nuclear Information System (INIS)

The corrosion resistance of zircaloy is affected by conditions of heat treatment in the manufacturing steps to be formed into a final product as a structural material. In the manufacturing method of the present invention, a Zr alloy controlled to contain Sn: 0.8 to 1.2wt%, Fe: 0.17 to 0.28wt%, Cr: 0.05 to 0.15wt%, Ni: 0.04 to 0.10wt%, Nb: 0.01 to 0.09wt%, oxygen: 1,000 to 1,500ppm and Si, an Si impurity at a concentration of 120ppm or less and balance of Zr is melted into a cast piece, to which #beta# hardening is applied. Then, rolling and annealing treatment are applied so that the total heat input amount to the material: #SIGMA#Ai ranges from 1 x 10"-"1"9 to 1 x 10"-"1"7. With such procedures, a Zr alloy structural material for a reactor core having excellent homogeneous corrosion resistance and hydrogen absorption resistance for a long period of time while having a sufficient strength can be obtained even in a case where Sn content is ...

Energy Technology Data Exchange (ETDEWEB)

Welded Ni-base alloys and Alloy 800 were exposed under metal dusting conditions at 600 C and 650 C for up to 6000 hours. Alloy 800 was attacked very strongly already in the first days and Alloy 600 also rather soon and widespread, on both materials attack started mainly in the heat affected zone. Several surface states of Alloy 600: brushed, ground, sand-blasted and pickled were tried only grinding caused a modest delay and decrease of metal dusting attack. Generally the attack was less widespread but deeper at 650 C than at 600 C, also for Alloy 601 and 602. The latter alloys show minor, mainly local attack, but especially the welds are affected. TIG welding led to better resistance than hand-welding. (Abstract Copyright [2003], Wiley Periodicals, Inc.)

Energy Technology Data Exchange (ETDEWEB)

Papers are presented on the development of oxidation- and sulfidation-resistant ferritic alloys; the microstructural stability of sulfidation-resistant FeCrAl stainless steels around 500 C; age hardening in Fe-Mn-Al-C austenitic alloys; the oxidation/corrosion behavior of low-Cr Fe-Cr-Ni alloys containing Zr or Nb; the high temperature oxidation/corrosion of iron-based superalloys; and the role of Mo in the Na/sub 2/SO/sub 4/ induced corrosion of superalloys at high temperature. Topics discussed include the effect of variations of Co content on the cyclic oxidation resistance of selected Ni-base superalloys; high temperature oxidation of Fe based alloys; the morphological development of high temperature oxide scales of Fe-Mn-Al base alloys; and the oxidation of an Fe-Mn-Al-C ...

International Nuclear Information System (INIS)

In one of the first uses of high Tc superconductors in an end-use product, Lake Shore Cryotronics and a Swiss lab have developed a liquid nitrogen level sensor using a high Tc thin film. The probe is manufactured using a seamless stainless steel tube with an yttrium-based zirconium oxide flame-sprayed on the tube. A plasma-sprayed superconductor compound is deposited on top of that. The probe is coated with a sealant that protects the superconducting film from the atmosphere. This manufacturing method has yielded an extremely durable product. Unaffected by ice formation and related mechanical problems, the superconducting level sensor can be kept in the dewar for long periods of time.

Energy Technology Data Exchange (ETDEWEB)

Recognizing the importance of {sup 99m}Tc and {sup 99m}Tc-based radiopharmaceuticals in nuclear medicine, the Philippine Nuclear Research Institute has initiated research on the development of column-type generators for {sup 99m}Tc using {sup 99}Mo in the form of a gel. The use of reactor-produced {sup 99}Mo will reduce the country's dependence on the importation of commercial generators based on fission product molybdenum-99. However, the relatively low specific activity of {sup 99}Mo must be compensated by the high adsorption capacity of the column material for molybdenum. A procedure based on the incorporation of low activity {sup 99}Mo into a zirconium molybdate gel matrix was adopted with reasonable success. Because the properties of the gel vary considerably with conditions of synthesis, the following parameters were carefully controlled: pH, concentration, temperature, order of mixing of ...

Energy Technology Data Exchange (ETDEWEB)

The complex formation of zirconium with biphenyl mono- and biscatecholyazo derivatives has been studied spectrophotometrically. The composition of the complexes, form and charge of complex-forming zirconium ions have been established. A procedure is suggested for calculation of molar absorptivities and stability constants for each of the complexes formed simultaneously in the system. Possible complex formation schemes have been studied. The data obtained were used to develop a spectrophotometric method of determining zirconium in the presence of large amounts of copper.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

This patent describes a process for preparing of an ion exchanger, comprising: treating an ionically inert activated charcoal porous support with an aqueous solution of metal oxychloride selected from the group consisting of zirconium and titanium oxychlorides so as to impregnate the pores of the support with the solution; separating the treated support from excess metal oxychloride solution; converting the metal oxychloride to a hydrous metal oxide precipitate in the pores of the support at a pH above 8 and above the pH whereat the hydrous metal oxide and activated charcoal support have opposite zeta potentials and sufficient to hydrolyze the metal oxychloride. It also describes a process for preparing an ion exchanger comprising: treating granulated activated charcoal with a concentrated solution of a metal oxychloride from the group consisting of zirconium and titanium oxychlorides, degassing the mixture; and treating the resultant mixture ...

International Nuclear Information System (INIS)

During 17 years since the start of operation of the first commercial LWR in Japan, many LWRs have experienced various corrosion damages, but the causes of them were clarified, and the counter-measures were executed effectively in actual plants, as the results, the cause of corrosion damage decreased remarkably, and now, the high rate of operation has become to be maintained. In this paper, the major cases of corrosion damage experienced in LWRs in Japan and foreign countries, the causes of them and the countermeasures, the problems of hereafter and so on are described. The corrosion damage of metallic materials in the environment of LWRs occurs in the parts in contact with high temperature, high pressure water and steam, such as stainless steel piping in the primary cooling system of BWRs, and nickel alloy heating tubes of steam generators, carbon steel feed water piping and zirconium alloy fuel cladding tubes in PWRs. ...

Energy Technology Data Exchange (ETDEWEB)

In order to investigate the role of amorphous SiO{sub 2} particles in corrosion and wear resistance of Ni-based metal matrix composite alloying layer, the amorphous nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer has been prepared by double glow plasma alloying on AISI 316L stainless steel surface, where Ni/amorphous nano-SiO{sub 2} was firstly predeposited by brush plating. The composition and microstructure of the nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer were analyzed by using SEM, TEM and XRD. The results indicated that the composite alloying layer consisted of {gamma}-phase and amorphous nano-SiO{sub 2} particles, and under alloying temperature (1000 deg. C) condition, the nano-SiO{sub 2} particles were uniformly distributed in the ...

Energy Technology Data Exchange (ETDEWEB)

Alloying elements such as Fe and Cr are generally considered to be effective even in small quantities for corrosion resistance of Zircaloy-4. The maximum total solubility of Fe + Cr in a Zr-Sn matrix has been reported to be very low. Therefore, most of these elements are observed in the form of ternary Zr-Fe-Cr-type precipitates. To clarify the effects of precipitates on corrosion property, Zr-1.3 Sn-(Fe,Cr) alloys containing Fe + Cr from 45 up to 180 ppm (the Fe to Cr ratio is about 2) were melted from pure zirconium (X-bar Zr and EB-Zr) and pure alloying elements. They were subjected to corrosion testing in 633 K water and microstructural analysis. It was found that precipitate-free materials showed much larger weight gains than precipitate-containing materials even at the same alloy compositions. Subsequently, a corrosion test on the precipitate-free material galvanically coupled ...

Energy Technology Data Exchange (ETDEWEB)

The aim of our research was to identify structures and chemical compositions of phases formed during internal oxidation of multi-component Ag-Zn-Mg-based alloys. Since the ability of inoculation mostly depends on large free energy of formation of oxides of microalloying elements and their crystallographic similarity, Mg in quantities of 0.001-0.5 mass% was selected as a micro-alloying element. These correspond to the quantities of 0.005-2.5 vol.% of MgO in the selected Ag-Zn-based alloys. Ag-based metal matrix, heterogeneous nuclei of MgO and oxide (ZnO) of the main alloying element were analysed by transmission electron microscopy (TEM). Structural inter-connections among them were also investigated and analysed. In situ phenomenon of heterogeneous nucleation of MgO and ZnO was proved. (orig.)

Energy Technology Data Exchange (ETDEWEB)

In this book over 250 alloys are organized by AISI number into 10 major sections: Irons, Carbon Steels, Alloy Steels, Low Alloy Constructional Steels, Ultra High Strength Steels, Tool Steels, Maraging Steels, Wrought Stainless Steels, Heat Resistnat Casting Alloys, and Iron Based Rought Superalloys. Each alloy record lists the designation, specifications, UNS number, composition, product forms and a comment on the high-temperature properties and applications. Referenced data is then given for physical properties such as density, specific heat, thermal conductivity, thermal expansion, electrical conductivity, Poisson's ratio, moduli of elasticity and rigidity, etc. Mechanical properties follow, and include tensile properties, shearing and bearing properties, impact properties, creep, stress rupture and stress relaxation and fatigue properties. The last ...

Energy Technology Data Exchange (ETDEWEB)

In this work, we have investigated the capability of different bimetallic nanoparticle alloy combinations to be used in fibre optic sensors based on the technique of surface plasmon resonance. The metals considered for this analysis are silver, gold, copper and aluminium. The performance of the sensor with different bimetallic nanoparticle alloy combinations is evaluated and compared numerically. The performance is analysed in terms of three parameters: sensitivity, signal-to-noise ratio (SNR) and operating range for the sensing layer refractive index values. On the basis of the comparison and some logistic criteria, the best possible bimetallic alloy combinations along with a requisite alloy composition ratio are predicted. The bimetallic nanoparticle alloy combination is capable of simultaneously providing larger values of sensitivity, SNR and operating range, ...

International Nuclear Information System (INIS)

The optimum of strontium amount for good modification of AK7, AK9, AK11, AK52, AK104 alloys was determined on the base of the analysis of microstructural changes. The stability of the modifier was investigated on the way of successive remelting of billets. The influence of amount of modifier on the impact strength of the alloys was established. (author)

International Nuclear Information System (INIS)

Modern commercial alloys are not suited for future steam turbines of operating temperatures beyond 700 C. #gamma#'-hardened alloys like Waspaloy have good mechanical characteristics but have defects when large batches are melted. #gamma#'/#gamma#''-hardened alloys like Inconel 706, on the other hand, are easy to produce but have insufficient microstructural long-term stability and insufficient creep strength. Mixed crystal solidified alloys like Inconel 617 have excessive yield stress at forging temperatures. Two new alloys were therefore developed. Results so far show that they have good production characteristics but insufficient mechanical characteristics. The reasons for this are currently under investigation. (orig.)

International Nuclear Information System (INIS)

Recent advances made in the area of amorphous and nanocrystalline alloys exhibiting high saturation inductions are reviewed. A new chemical composition was identified that achieves a saturation induction of 1.64 T in an iron-based amorphous alloy. This alloy, when used in electrical transformers, shows a much improved performance over the existing amorphous alloy. Nanocrystalline FeCoCuNbSiB alloys are found to have saturation induction levels reaching 1.7 T. These materials are suited for use in sensors and inductors carrying large currents. Some of these nanocrystalline alloys show a BH squareness ratio exceeding 90%, which can be utilized in pulse power devices. Recent developments in the applications of these materials are also pointed out.

International Nuclear Information System (INIS)

A one-nanometer scale transmission electron microscope electron probe X-ray microanalysis characterization of as-deposited and annealed aluminum--11.5 at.% zirconium multilayer samples in cross-section synthesized by magnetron sputtering is reported on here. Composition line profiles were acquired across Zr layers in as-deposited material and samples isochronally annealed in a differential scanning calorimeter to temperatures of 290 C and 485 C. A spatial resolution of approximately 1.5 to 2.0 nm was achieved in these experiments and will be improved by deconvolution of the instrumental electron probe function from the data. The as-deposited structure consisted of crystalline Al and Zr layers with thin amorphous layers at the Al/Zr interfaces. The amorphous interface layers increased in thickness upon annealing to 290 C. Additionally, at 290 C a metastable cubic alloy forms at the Zr deposited on Al interface. Upon heating to 485 C a multilayer ...

International Nuclear Information System (INIS)

... Sergio Department of Materials, University of Oxford, Oxford (United Kingdom)

International Nuclear Information System (INIS)

Zirconium phosphate was one of the earliest inorganic ion-exchange suggested for removing strontium and cesium from aqueous nuclear waste. This paper studied ionic exchange to remove Cs-137 and Sr-90 by using different cationic of zirconium phosphate. In this case the parameters studied were the effect of temperature and ion concentration to percent up take and distribution coefficients. It is also conducted the study on column experiments to determine the breakthrough curves for Cs-137 and Sr-90. The result showed the potential of use of zirconium phosphate in radioactive waste treatment. (author)

International Nuclear Information System (INIS)

The study of passive films formed on a nickel base alloy type Inconel 600 is performed by capacitance measurements (Mott-Schottky approach). This research is supported by the passivation study of the alloying elements Ni, Cr, Fe and high purity alloys Ni-Cr, Ni-Fe, Ni-Cr-Fe. The results obtained show that the capacitive behaviour of the Inconel 600 in the passive state is similar to that on a p-n heterojunction to which a barrier zone of nickel oxide is added. The individual or combined action of alloying elements on the development of this kind of electronic structure is discussed. (authors). 5 refs., 6 figs.

International Nuclear Information System (INIS)

We propose a dissolution-passivation model to account for the electrochemical behavior of Alloy 800 and 316L stainless steel under steam generators operating conditions. This model is similar to the one defined for nickel, considering the known importance of this element on the studied alloys. The comparison of the rates of the elementary steps points out the favorable influence of dissolved oxygen and phosphate ions on the dissolution of Alloy 800, even in the presence of chloride ions. The sensitivity of 316L SS is greater, especially because of the lowest stability of oxide-like intermediate.

International Nuclear Information System (INIS)

Repassivation behavior and IGA resistance of nickel base alloys containing 0#approx#30 wt% chromium was investigated in high temperature acid sulfate solution. (1) The repassivation rate was increased with increasing chromium content. And so the amounts of charge caused by the metal dissolution were decreased with increasing chromium content. (2) Mill-annealed Alloy 600 suffered IGA at low pH environment below about 3.5 at the fixed potentials above the corrosion potential in 10%Na_2SO_4+H_2SO_4 solution at 598K. On the other hand, thermally-treated Alloy 690 was hard to occur IGA at low pH environments which mill-annealed Alloy 600 occurred IGA. (3) It was considered that the reason, why nickel base alloys containing high chromium content such as Alloy 690 (60%Ni-30%Cr-10%Fe) had high IGA/SCC resistance in high ...

International Nuclear Information System (INIS)

In response to European operating experience regarding Alloy 800 steam generator (SG) tube cracking, New Brunswick Power Nuclear (NBPN) recognized two important shortcomings in the industry SG technical support framework. First, information exchange networks between utilities with Alloy 800 SG tubing should be strengthened. Second and more importantly, there is a need for consistent industry guidance for Alloy 800 SG tubing degradation management, supported by clear technical bases. It is NBPN's perspective that this guidance can be improved immediately using the extensive amount of laboratory and field data that is available for Alloys 600, 690, and 800, and EPRI methodology developed to predict the performance of Alloy 690. NBPN has initiated the development of a performance-based inspection plan. This effort is based ...

Energy Technology Data Exchange (ETDEWEB)

The corrosion behaviour of the stainless steels 304, 316 Ti, 25Cr-20Ni-Mo-Ti, nickel base alloys Hastelloy C4, Inconel 625, Incoloy 800, Ti and Ti-0.2% Pd alloy has been studied in the aerated or deaerated solutions at 20/sup 0/C and 90/sup 0/C whose compositions are representative of interstitial ground waters: granitic or clay waters or salt brine. The electrochemical techniques used are voltametry, polarization resistance and complexe impedance measurements. Electrochemical data show the respective influence of the parameters such as temperature, solution composition and dissolved oxygen, addition of soluble species chloride, fluoride, sulfide and carbonates, on which depend the corrosion current density, the passivation and the pitting potential. The inhibition efficiency of carbonate and bicarbonate activities against pitting corrosion is determined. In clay water at 90/sup 0/C, Ti and Ti-Pd show very high passivation ...

Energy Technology Data Exchange (ETDEWEB)

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride <0.05 M containing 30% ethylene glycol solution, they are more corrosive than the blank (30% ethylene glycol-70% water). However, at concentrations <0.05 for chloride or >0.05 M for fluoride ...

International Nuclear Information System (INIS)

An alloy of composition Ti-4.4 wt.% Ta-1.9 wt.% Nb is being developed as a structural material for corrosion applications, as titanium and its alloys possess excellent corrosion resistance in many oxidizing media. The primary physical metallurgy database for the Ti-4.4 wt.% Ta-1.9 wt.% Nb alloy is being presented for the first time. Determination of the #beta# transus, M_s temperature and classification of the alloy have been carried out, employing a variety of microscopy techniques, X-ray diffraction (XRD), micro-hardness and differential scanning calorimetry (DSC). The #beta# transition temperature or #beta# transus determined using different experimental techniques was found to agree very well with evaluations based on empirical calculations. Based on chemistry and observed room temperature microstructure, the alloy has been classified as ...

Energy Technology Data Exchange (ETDEWEB)

In view of the importance of the material Alloy 800 in high-temperature reactor plants (HTR), a material data bank was established which is used for statistical evaluation of mechanical and physical material behaviour. Based on investigations on the interconnection between the mechanical properties at high temperatures and the metallurgical parameters, different types of Alloy 800 were specified in compliance with the component requirements. In addition, aspects of corrosion and toughness behaviour were taken into consideration. The specifications and strength characteristics for the different variants of Alloy 800 were incorporated into draft DIN standards after discussion and approval in expert committees. Further important characteristics of the mechanical and physical material behaviour were summarized in HTR material data sheets so as to furnish an improved basis for the design and stress analyses ...

Energy Technology Data Exchange (ETDEWEB)

Metal dusting corrosion has been a serious problem in the petroleum and petrochemical industries, such as reforming and syngas production systems. This form of deterioration has led to worldwide material loss for 50 years. For the past three years, we have studied the mechanism of metal dusting for Fe- and Ni-base alloys. In this report, we present a correlation between the weight loss and depth of pits that form in Ni-base alloys. Nickel-base alloys were also tested at 1 and 14.8 atm (210 psi), in a high carbon activity environment. Higher system pressure was found to accelerate corrosion in most Ni-base alloys. To reduce testing time, a pre-pitting method was developed. Mechanical scratches on the alloy surface led to fast metal dusting corrosion. We have also developed preliminary data on the ...

Energy Technology Data Exchange (ETDEWEB)

Alloy 800 has been used for steam generator (SG) tubing for more than 30 years, primarily in CANDU reactors worldwide and in reactors in Germany. Extensive laboratory testing and in-service experience suggest that the Alloy 800 tubing has excellent resistance to corrosion-related degradation under appropriate operating conditions. In planning refurbishment of nuclear plants stations, a key concern is the longevity of existing SGs up to the 60-year lifetime of the refurbished plant. The paper reviews an existing methodology based on the concept of the improvement factor, and refines its estimation based on data specific to CANDU operating conditions. The paper presents a more advanced Bayesian probabilistic approach to estimate the degradation free lifetime distribution of Alloy 800 tubing, which is used to quantify the probability of degradation during the service life and to ...

Science.gov (United States)

Ni-free shape memory alloys are promising functional materials for medical applications. A newly developed Ti-Mo based shape memory alloy shows superelasticity after thermomechanical treatment. However, the microstructure evolution and precipitation during thermomechanical processes are still not well understood. In the present paper, compressive deformation behavior at a series of temperatures of 298K - 973K and tensile deformation behavior of the alloy after aged at 573K - 973K have been investigated systematically. It is found that the compressive yield stress and ultimate compressive strength change with the deformation temperature. The ultimate tensile strength and yield stress of aged specimens also change with the aging temperature following a non-linear relationship. Microstructures of aged specimens as well as effects of lattice softening and aging-induced precipitates on the deformation ...

Energy Technology Data Exchange (ETDEWEB)

A comprehensive review was conducted of primary helium coolant chemistry data, based on current and past operating histories of helium-cooled, high-temperature reactors (HTGRs), including the Fort St. Vrain (FSV) HTGR. A reference observed FSV reactor coolant environment was identified. Further, a slightly drier expected FSV coolant chemistry was predicted for reactor operation at 100% of full power. The expected environment was compared with helium test environments used in the US, United Kingdom, Germany, France, and Japan. Based on a comprehensive review and analysis of mechanical property data reported for Alloy 800 tested in controlled-impurity helium environments (and in air when appropriate for comparison), an assessment was made of the effect of FSV expected helium chemistry on material properties of alloy 800, with emphasis on design properties of the Alloy 800 material ...

Energy Technology Data Exchange (ETDEWEB)

Alloy 800 has been used for steam generator (SG) tubing for more than 30 years, primarily in CANDU reactors and in reactors in Germany. Extensive laboratory testing and in-service experience suggest that the Alloy 800 tubing has excellent resistance to corrosion-related degradation under specified and appropriate operating conditions. In planning refurbishment of CANDU stations, a key concern is the longevity of existing SGs up to the 60 year lifetime of the refurbished plant. The paper reviews an existing methodology based on the concept of the improvement factor, and estimates it based on experimental data specific to CANDU operating conditions. The paper presents a more advanced probabilistic approach to estimate the degradation free lifetime distribution of Alloy 800 tubing, which is used to quantify the probability of degradation during the service life and to evaluate the ...

Energy Technology Data Exchange (ETDEWEB)

The distribution of graphite particles in graphite containing copper alloy was further improved very significantly using several procedures and technological modifications. The developed techniques attacked the graphite distribution problem in two ways. Realizing that clustering of very fine (5um) graphite particles is one of the two major problems, a pretreatment process has been developed using aluminum powders to deagglomerate graphite particles. Along with this, a two-stage stirring technique was used to first incorporate and then to distribute uniformly the deagglomerated particles in the melt. During this year, based on these developments, several components were cast to evaluate the castability of Cu alloy-graphite melts. In addition, machinability tests were done to clearly established that addition of graphite particles improve the machinability of copper MMC alloys over and above that of ...

Energy Technology Data Exchange (ETDEWEB)

Gas nitridation has shown excellent promise to form dense, electrically conductive and corrosion-resistant Cr-nitride surface layers on Ni-Cr base alloys for use as proton exchange membrane fuel cell (PEMFC) bipolar plates. Due to the high cost of nickel, Fe-base bipolar plate alloys are needed to meet the cost targets for many PEMFC applications. Unfortunately, nitridation of Fe-base stainless steel alloys typically leads to internal Cr-nitride precipitation rather than the desired protective surface nitride layer formation, due to the high permeability of nitrogen in these alloys. This paper reports the finding that it is possible to form a continuous, protective Cr-nitride (CrN and Cr{sub 2}N) surface layer through nitridation of Fe-base stainless steel alloys. The key to form a protective ...

Energy Technology Data Exchange (ETDEWEB)

The weldability and high temperature strength properties of tungsten-inert-gas (TIG) weldments of Hastelloy alloy XR were investigated by using two different heats of filler metals; the first (HXRF1) was designed on the basis of multiple regression analysis; the second (HXRF2) was the reference material. Bend tests, the FISCO cracking test and optical metallography were used to evaluate weldability. Tensile and creep tests were performed at 900deg C to evaluate high temperature strength properties. The results of weldability tests for both alloys showed good performance. The tensile properties of the weldments were remarkably improved in particular with respect to high temperature ductility. The creep rupture strength in the weldments made with alloy-designed HXRF1 was much higher than those of the Hastelloy alloy XR-II base metal with a higher B content. Furthermore, the creep ...

Energy Technology Data Exchange (ETDEWEB)

Refractory metal alloys based on Mo, W, Re, Ta, and Nb (Cb) find applications in a wide range of aerospace applications because of their high melting points and high-temperature strength. This paper, presents recent progress in understanding and applications of these alloys. Recent studies to improve the oxidation and mechanical behavior of refractory metal alloys, and particularly Nb alloys, are also discussed. Some Re structures, for extremely high temperature applications (> 2000C), made by CVD and P/M processes, are also illustrated. Interesting work on the development of new W alloys (W-HfC-X) and the characterization of some commercial refractory metals, e.g., K-doped W, TZM, and Nb-1%Zr, continues. Finally, recent developments in high temperature composites reinforced with refractory metal filaments, and refractory metal-based ...

Science.gov (United States)

Intermetallic compounds are regarded as highly promising for applications as high temperature structural materials. However, recent studies have demonstrated that a number of ordered alloys exhibit environmental embrittlement when tested in various environments at ambient temperature. When exposed to hydrogen gas or electrolytically charged with hydrogen, a significant ductility loss has been reported. The reaction of water vapor with reactive elements in the crack tip results in the generation of atomic hydrogen which diffuses from the surface to the interior and causes embrittlement. In this paper, the authors try to analyze the sensitivity of hydrogen embrittlement of ordered alloys based upon energetical considerations.

International Nuclear Information System (INIS)

Ab initio total-energy calculations, based on the exact muffin-tin orbital method, are used to determine the elastic properties of Pd1-xAgx random alloys in the face-centered-cubic crystallographic phase. The compositional disorder is treated within the coherent-potential approximation. The single crystal and polycrystalline elastic constants and the Debye temperature are calculated for the whole range of concentration, 0?x?1. It is shown that the variation in the elastic parameters of Pd-Ag alloys with chemical composition strongly deviates from a simple linear or parabolic trend. The complex electronic origin of these anomalies is demonstrated.

Energy Technology Data Exchange (ETDEWEB)

Recently the increase of steam temperature and pressure of power plant is required to enhance the thermal efficiency and reduce the CO{sub 2} emission. For the application to advanced USC (Ultra Super Critical) boiler with steam temperature around 700 C, the application of Ni-based alloy such as Alloy617 will be necessary. A new Ni-based alloy USC141 (20Cr-10Mo-2Ti-Al-bal.Ni) with excellent creep rupture strength and low thermal expansion has been developed by Hitachi Ltd. and Hitachi Metals Ltd. as the candidate material for 700 C USC turbine components. In present work, to investigate the possibility for boiler tube application of USC141, its weldability and high temperature strength properties were experimentally examined. The tested material as solution-treated condition shows higher creep rupture strength than that of Alloy617. GTAW (Gas Tungsten Arc ...

Energy Technology Data Exchange (ETDEWEB)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically- conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of two high Cr (30-35 wt%) commercially available Ni-Cr alloys and a ferritic high Cr (29 wt.%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved via nitridation. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effects for the Ni-Cr base alloys, but beneficial effects for the stainless ...

Energy Technology Data Exchange (ETDEWEB)

The study of passive films formed on a nickel base alloy type Inconel 600 is performed by capacitance measurements (Mott-Schottky approach). This research is supported by the passivation study of the alloying elements Ni, Cr, Fe and high purity alloys Ni-Cr, Ni-Fe, Ni-Cr-Fe. The results obtained show that the capacitive behaviour of the Inconel 600 in the passive state is similar to that on a p-n heterojunction to which a barrier zone of nickel oxide is added. The individual or combined action of alloying elements on the development of this kind of electronic structure is discussed. (authors). 5 refs., 6 figs.

International Nuclear Information System (INIS)

This paper presents the results of experimental study carried out to know whether the salicylic acid used as an additive during the precipitation of zirconium using ammonium hydroxide solution goes into the filtrate, remains in the hydrated zirconia or gets distributed between the both under the ambient conditions of precipitation. Keeping its simplicity and amenability to adopt on a routine basis, spectrophotometric method has been chosen for the purpose among the many methods available and the problems associated in determining salicylic acid in the presence of zirconium and the medial measures to circumvent the same have been brought out in detail. (author)

International Nuclear Information System (INIS)

Structural relaxation, crystallization and optimisation processes in soft magnetic amorphous alloys based on iron are examined by applying different experimental techniques: X-ray diffraction analysis, high-resolution electron microscopy, measurements of magnetic and electric properties (permeability, after-effect resistivity). The presented results are discussed in terms of annealing out of microvoids, formation of nanocrystalline phase and changes of effective magnetostriction constant. (author)

Energy Technology Data Exchange (ETDEWEB)

An extensive R and D program on the development of the joining technologies between armour (beryllium, tungsten and carbon fibre composites)/copper alloys heat sink and copper alloys/ stainless steel has been carried out by ITER Home Teams. A brief review of this R and D program is presented in this paper. Based on the results, reference technologies for use in ITER have been selected and recommended for further development. (author)

International Nuclear Information System (INIS)

Magnesium alloys have been increasingly used in automotive and electronic industries because of their excellent strength to weight ratio and EMI shielding properties. However, magnesium alloys have low formability at room temperature due to their unique mechanical behavior (twinning and untwining), prompting for forming at an elevated temperature. In this study, a temperature dependent constitutive model for magnesium alloy (AZ31B) sheet is developed. A hardening law based on non linear kinematic hardening model is used to consider Bauschinger effect properly. Material parameters are determined from a series of uni-axial cyclic experiments (T-C-T or C-T-C) with the temperature ranging 150-250 deg. C. The influence of temperature on the constitutive equation is introduced by the material parameters assumed to be functions of temperature. Fitting process of the assumed model to measured data is presented ...

International Nuclear Information System (INIS)

Strain embrittlement in Ti base alloys during tensile testing was investigated. Results show that in an #alpha#-#beta# titanium alloy the local activity of H in alpha phase (#alpha#/sub H//sup #alpha#) increases and activity of H in beta phase (#alpha#/sub H//sup #beta#) decreases as the equiaxed #alpha# particle size decreases at constant volume fraction of phases. Thus with decreasing particle size there would be a tendency for H to move from #alpha# to #beta#, decreasing the H content of #alpha#. Also whether H tended to move from #beta# to #alpha# or from #alpha# interiors to the #alpha#-#beta# interface this tendency would be reduced by surface tension effects, making the alloy less susceptible to embrittlement.

Energy Technology Data Exchange (ETDEWEB)

The program introduced here for determining and describing the multi-axial creep of pipes is based, on the one hand, on the results of the nuclear process heat prototype plant material program and, on the other hand, on the possible load conditions which arise for evaluating accidents or extreme working situations. The basis of a theoretical description of multi-axial creep is the invariant theory in which both the von Mises configuration change hypothesis and the Norton creep law are included. Combined tension and torsion are also considered in detail, the superimposition of cyclic stresses in the tensile threshold area is discussed and cases of partial relaxation are explained. Experimental results for the discussed loads are introduced, which have led to satisfactory agreement between theory and experiment. (orig./MM).

Energy Technology Data Exchange (ETDEWEB)

The phase transformations and properties of a precipitation-hardened Ni-Cr-based alloy are investigated as a function of C, B, Nb, and Cr contents. It is found that the primary role of Nb consists in the formation of an independent phase, delta-Ni3Nb, a part of a gamma/gamma-prime-delta eutectoid (for high C and B concentrations) and in stimulating the gamma-sigma reaction consecutively with the gamma double prime-delta reaction (for low C and B concentrations). In both cases, the long-term strength characteristics of the Nb-alloyed system are relatively low. The substitution of boron for carbon contributes to a reduction in the number of nucleation sites for topologically close-packed phases and to the formation of more stable (with respect to excess compounds) M3B2 and MB2 borides. The high-boron material exhibits better properties and phase stability under mechanical and thermal loading. 13 references.

Energy Technology Data Exchange (ETDEWEB)

The chemical composition and the semiconducting properties of passive films formed on nickel based alloy (Alloy 600) in acidic sulphate solution, pH 2.0 at room temperature were studied using Auger analysis, voltammetric techniques and the Mott-Schottky approach. The results obtained revealed that the presence of both chromium and mixed nickel-iron oxides in the films leads to the development of a p-n heterojunction, which controls their electronic structure, similarly manner to the case of stainless steels and Alloy 600 in borate buffer solution. This behavior has been interpreted as representing of an oxide system, which has a duplex character, with an inner p-type semiconducting region, mainly formed by chromium oxide and an outer n-type semiconducting region, containing iron oxide. It could also be observed that the nickel oxide present in the films acts as a barrier layer conferring improved ...

International Nuclear Information System (INIS)

Generally, neutron, ion and electron Irradiations cause a substantial amount of hardening and significantly alter the deformation behavior of metals and alloys at relatively low irradiation temperatures. A radiation hardening is caused by the formation of microstructural defects such as dislocation loops, voids and precipitates under irradiation. Therefore, it is important to have a better knowledge of the irradiation induced microstructural defects under irradiation condition. As a part of the National mid- and long-term atomic energy R and D program, we are dealing with the radiation hardening behavior in Fe-Cr binary alloy. Fe-Cr binary alloy is a base alloy of Ferritic/Martensitic steel(F/M steel) planning to use for the Gen IV nuclear system. In this work, we investigated the radiation hardening and microstructural defect evolution in ion irradiated Fe-Cr ...

Energy Technology Data Exchange (ETDEWEB)

The present paper describes the development of ultra-fine grains on the surface of AZ31 alloys caused by hydrogenation and dehydrogenation treatment, so-called HDDR process. Upon hydrogenation process, disproportionation reaction occurred in forming of MgH{sub 2}, Mg{sub 0.42}Al{sub 0.58}, and Al phases. In the following desorption process, the three phases were re-solved into the AZ31 alloy. As a result of the HDDR phenomena, the grain size of AZ31 alloy powders was reduced down to about 100 nm after the heat treatment at 350 C under a hydrogen pressure of 7 MPa for 24 h. The grain size tended to be increased with increasing process temperatures. In addition, the HDDR process was also applied to AZ31 alloy plates. By the HDDR process at 450 C, the grain size was reduced to less than 500 nm, where hydrogenated layer thickness was limited to be in the range of about 20 {mu}m from the surface. The Vickers ...

International Nuclear Information System (INIS)

Application of Alloy 800 in steam generator tubing of fast reactors, where continuous service temperature of the order of 550"0C is experienced, has been analyzed with respect to small variations in its chemical composition. Several laboratory melts of Alloy 800 have been prepared and their microstructural and mechanical property changes during simple aging and creep tests at 500 to 600"0C have been studied. It has been found that in the above temperature range precipitation of M_2_3C_6 on the grain boundaries is independent of the Ti : C ratio generally specified for Alloy 800. Gamma prime precipitation occurred in alloys containing as low as 0.5 percent Ti + Al after 1000 h of aging and was accompanied with a creep ductility decline. Upon #gamma# precipitation creep rate was retarded and its reacceleration for test times up to 8500 h at 550"0C was not observed. Based on the ...

International Nuclear Information System (INIS)

May 2010 p. 81-84 Japan Ishizawa, Makoto JFE Steel Corporation, Tokyo

International Nuclear Information System (INIS)

Classification and ranking of the solid solution on their reaction to the irradiation is suggested on the basis of binary system structure controlled by mixing enthalpy sign, melting temperatures relation of components and solidus curves slope. Several combinations of these characteristics permit to pick out three groups of substitutional elements capable of forming the vacancy-solute atom complexes either low-mobile or fast-mobile ones as compared to monovacancies migration. The radiation hardening (and embrittlement) of binary alloys should be intensified respectively either due to heterogeneous point defect clusters nucleation on solute traps or due to solute atom clusters/ precipitate formation. A local cohesion decrease may also occur especially if low-melting elements (characterized by low surface energy) are segregating on internal sinks or grain boundaries. The predicted specifics of different alloy group under irradiation and during ...

Energy Technology Data Exchange (ETDEWEB)

Some hypo-stoichiometric Zr-based Laves phase alloys were prepared and studied from a viewpoint of discharge capacity for electrochemical application. After careful alloy design of ZrMn{sub 2}-based hydrogen storage alloys through changing their stoichiometry while substituting or adding some alloying elements, the Zr(Mn{sub 0.2}V{sub 0.2}Ni{sub 0.6}){sub 1.8} alloy reveals relatively good properties with regard to hydrogen storage capacity, hydrogen equilibrium pressure and electrochemical discharge capacity. In order to improve the discharge capacity and rate-capability, Zr is partially replaced by Ti. The discharge capacity of Zr{sub 1-x}Ti{sub x}(Mn{sub 0.2}V{sub 0.2}Ni{sub 0.6}){sub 1.8} (x=0.0, 0.2, 0.3, 0.4, 0.6) alloy electrodes at 30 C reaches a maximum value and decreases as the Ti fraction increases. In view ...

Energy Technology Data Exchange (ETDEWEB)

The microstructure evolution of nine samples from three Ir-base ternary systems, Ir-Nb-Hf, Ir-Nb-Ta, and Ir-Nb-Ti, was investigated by microstructure observation using scanning electron microscopy (SEM), composition map-analysis using electron probe microscopy analysis (EPMA), and phase determination using X-ray diffraction (XRD) patterns. The fcc/L1{sub 2} two-phase structure was detected in all the samples. Lattice misfits between fcc and L1{sub 2} phases were calculated. Ir-Nb-Ta and Ir-Nb-Ti alloys exhibited a microstructure quite similar to that of Ni-base superalloys, and the cuboidal L1{sub 2} precipitates in Ir-Nb-Ta and Ir-Nb-Ti alloys could maintain up to 1900 {sup o}C.

British Library Electronic Table of Contents (United Kingdom)

Nitridation of Cr-bearing alloys can yield low interfacial contact resistance (ICR), electrically conductive and corrosion-resistant CrN or Cr2N base surfaces of interest for a range of electrochemical devices, including fuel cells, batteries, and sensors. This paper presents results of exploratory studies of the nitridation of commercially available, high Cr (30-35wt%) Ni-Cr alloys and a ferritic high Cr (29wt%) stainless steel for proton exchange membrane fuel cell (PEMFC) bipolar plates. A high degree of corrosion resistance in sulfuric acid solutions designed to simulate bipolar plate conditions and low ICR values were achieved. Oxygen impurities in the nitriding environment were observed to play a significant role in the nitrided surface structures that formed, with detrimental effect...

International Nuclear Information System (INIS)

Concentration profiles of passive films formed on electrolytically anodized niobium and niobium-base alloys are obtained by Auger Electron Spectroscopy with simultaneous ion beam etching. The alloys investigated include 5Zr-Nb, 3Zr-10Ti-Nb, 2.5Zr-2W-Nb, and 1Zr-5Mo-5V-Nb. Experiments demonstrate that AES is among the most fascinating techniques for solving various characterization problems related to the structure and composition of the thin films formed by anodization. Data presented supports evidence that combined anodic and cathodic movements take place during film growth. 11 figures.

Energy Technology Data Exchange (ETDEWEB)

Using the PMR method the interaction of zirconium and hafnium tetrachlorides with tri.tet.butylphenyl ester of 1,2- naphthoquinonediazide (2)-5-sulfonic acid is studied. The formation of MCl/sub 4/xNQD complexes is established, the equilibrium constants and thermodynamic parameters of complexing reaction are determined. The presence of rapid ligand exchange, proceeding according to associative mechanism, is detected. The rate constants and activation energies of the exchange reaction are calculated.

International Nuclear Information System (INIS)

A method has been developed for the adsorption of Sc"I"I"I employing inorganic ion exchanger zirconium phosphosilicate by batch method. Effects of various parameters have been evaluated on the percentage adsorption of Sc"I"I"I. Separation of Sc"I"I"I from various other elements is standardized. (author)

Energy Technology Data Exchange (ETDEWEB)

An energy dispersive x-ray fluorescence technique was used for the determination of Titanium (Ti) and Zirconium (Zr) in red mud by using a standard addition method. An annular {sup 241}Am source is employed for excitation of K shells of elements. 13 refs., 2 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

We describe the growth, fabrication, and characterization of an ultraviolet (UV) photoconductive detector based on In{sub x}Al{sub y}Ga{sub 1-x-y}N quaternary alloy that is lattice matched to GaN. The detector consisted of 0.1 {mu}m In{sub x}Al{sub y}Ga{sub 1-x-y}N alloy grown on 0.5-1.0 {mu}m GaN epilayer by metalorganic chemical vapor deposition. With varying indium concentration, the cut-off wavelength of the In{sub x}Al{sub y}Ga{sub 1-x-y}N detectors could be varied to the deep UV range. The most important and intriguing result is that the responsivity of the In{sub x}Al{sub y}Ga{sub 1-x-y}N quaternary alloy exceeded that of AlGaN alloy of a comparable cutoff wavelength by a factor of five. This makes the nitride quaternary alloy very important material for solar blind UV detectors applications particularly in the deep UV range where Al rich AlGaN ...

Energy Technology Data Exchange (ETDEWEB)

A heat resistant nickel base alloy which is excellent in not only hot and cold workability but also high temperature strength properties and which also possesses satisfactory oxidation resistance. The nickel base alloy consists essentially of 0.001-0.15 percent carbon, 0.0005-0.05 percent calcium, 20.0-126.0 percent chromium, 4.7-9.4 percent cobalt, 5.0-16.0 percent molybdenum, 0.5-4.0 percent tungsten, with the total of molybdenum plus tungsten being from 9.0 to 16.5 percent, and the balance nickel and inevitable impurities. The alloy may further contain one selected from the group consisting of (1) 0.3-1.5 percent aluminum and 0.1-1.0 percent titanium, (2) 0.001-0.30 percent at least one of yttrium and rare earth elements, and (3) 0.001-1.0 percent at least one of niobium, vanadium and tantalum, whereby the aforementioned characteristics are further enhanced.

Science.gov (United States)

The authors develop a procedure for the determination of the Al, Ti, V, Cu, Mn, Mo, and W content of nickel-base alloys by neutron activation analysis. An M-10 microtron with a beryllium target in a paraffin microtron (with a beryllium target) in a paraffin moderator served as the neutron source. In order to evaluate the procedure for quantitative analysis, the authors determined the contents of the above elements in five reference standards, the bulk density of which was 2.94-4.17 g/cm/sup 3/. The difference in the self-absorption of the gammaquanta was assessed by determining the number of gamma-quanta with energies in the range 60-1332 keV that had passed through the RS N4 and N8 which showed the greatest difference in their composition. The results of the determination are presented. The proposed procedure is simple and rapid and can be used to determine the alloying components of nickel-based ...

Energy Technology Data Exchange (ETDEWEB)

Transition joints in power plants between ferritic steels and austenitic stainless steels suffer from a mismatch in coefficients of thermal expansion (CTE) and the migration of carbon during service from the ferritic to the austenitic steel. To overcome these, nickel-based consumables are commonly used. The use of a trimetallic combination with an insert piece of intermediate CTE provides for a more effective lowering of thermal stresses. The current work envisages a trimetallic joint involving modified 9Cr-1Mo steel and 316LN austenitic stainless steel as the base materials and Alloy 800 as the intermediate piece. Of the two joints involved, this paper describes the choice of welding consumables for the joint between Alloy 800 and 316LN. Four consumables were examined: 316, 16-8-2, Inconel 82 and Inconel 182. The comparative evaluation was based on hot cracking tests and estimation ...

International Nuclear Information System (INIS)

After being pre-plated a zinc layer, an amorphous Al-Mn alloy coating was applied onto the surface of AZ31B magnesium alloy with a bath of molten salts. Then the corrosion performance of the coated magnesium alloy was examined in 3.5% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results showed that the single Zn layer was active in the test solution with a high corrosion rate while the Al-Mn alloy coating could effectively protect AZ31B magnesium alloy from corrosion in the solution. The high corrosion resistance of Al-Mn alloy coating was ascribed to an intact and stable passive film formed on the coating. The performances of the passive film on Al-Mn alloy were further investigated by Mott-Schottky curve and X-ray photoelectron spectroscopy (XPS) analysis. It was confirmed that the ...

International Nuclear Information System (INIS)

As part of a coordinated program, AECL is developing a set of tools to aid with the prediction and management of steam generator performance. Although stress corrosion cracking (of Alloy 800) has not been detected in any operating steam generator, for life management it is necessary to develop mechanistic models to predict the conditions under which stress corrosion cracking is plausible. Therefore, constant extension rate tests were carried out for Alloy 800 under various steam generator crevice chemistry conditions at applied potentials. These tests were designed to evaluate the stress corrosion cracking susceptibility of Alloy 800 under CANDU( steam generator operating conditions. Based on the experimental results, the recommended electrochemical corrosion potential/pH zone for Alloy 800 determined by electrochemical polarization measurements was verified with the respect of ...

International Nuclear Information System (INIS)

Superconductivity of binary alloys spanning the A-15 compounds V_3Si, V_3Ge, V_3Ga, and V_3Al and the pseudobinary derivatives of these stoichiometric compounds was surveyed by studying samples prepared by rf-sputtering from alloy cathodes. The possible formation of the hypothetical A-15 binaries ''V_3P,'' ''V_3B,'' and ''V_3C'' and their pseudobinary formation with V_3Si was also explored. Efforts to form these hypothetical alloys were not successful. The T/sub c/'s were measured resistively and the structure and lattice constants were determined by x-ray analysis. A maximum T/sub c/ of 11.7"0K was obtained for A-15 V_3Al, and the importance of a suitable deposition temperature and high sputtering pressures was examined. It is proposed that large variations of T/sub c/ among pseudobinary alloys imply a rapid variation of the density of states at the Fermi level.

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the co-deposition of chromium and silicon into a 2.25Cr-1.0Mo-0.15C steel, alloy 800, and type 304 stainless steel has been achieved using the pack cementation process. The ferritic coating produced on the 2.25 Cr-1.0Mo steel was approximately 225 {mu}m (9 mils) thick, whereas the inward diffusion of chromium and silicon produced a two-phase structure of ferrite and austenite for type 304. Chromium and silicon were incorporated into the austenitic solid solution upon diffusion into alloy 800. All coatings had approximately 25 to 35 wt% Cr and 2 to 3% Si at the surface. Cyclic oxidation testing in air of the coated 2.25Cr-1.0Mo steel (T = 700{degrees} C) and type 304 (T = 1035{degrees} C) showed a dramatic decrease in the oxidation kinetics compared to the original uncoated alloys. The cyclic oxidation of alloy 800 was also improved.

Energy Technology Data Exchange (ETDEWEB)

As part of a coordinated program, AECL is developing a set of tools to aid with the prediction and management of steam generator performance. Although stress corrosion cracking (of Alloy 800) has not been detected in any operating steam generator, for life management it is necessary to develop mechanistic models to predict the conditions under which stress corrosion cracking is plausible. Therefore, constant extension rate tests were carried out for Alloy 800 under various steam generator crevice chemistry conditions at applied potentials. These tests were designed to evaluate the stress corrosion cracking susceptibility of Alloy 800 under CANDU( steam generator operating conditions. Based on the experimental results, the recommended electrochemical corrosion potential/pH zone for Alloy 800 determined by electrochemical polarization measurements was verified with the respect of ...

Energy Technology Data Exchange (ETDEWEB)

Acrylonitrile electropolymerization (in an aprotic and anhydrous medium) has been used as a way to build thin, homogeneous and covering polyacrylonitrile layers grafted on the surface of usual metals and specially on copper-based shape memory alloy: Cu-Zn-Al. The results of the study first confirm the possibility of grafting thin and covering polyacrylonitrile layers on Cu-Zn-Al surface. The morphology of the films however is influenced by the geometry of the polycristalline structure of the alloy and its superficial defects. Samples obtained after grafting polyacrylonitrile films were submitted to corrosion tests based on Electrochemical Impedance Spectroscopy (EIS) measurements in a NaCl/H{sub 2}O medium. Results show that some post-treatments of the grafted films are necessary to improve their protective role, while preserving the strong interfacial bondings. Actually, thermal and mechanical cycling ...

International Nuclear Information System (INIS)

Alloy 690 and Alloy600 are used as a material for the steam generator tubing in the pressurized water reactor(PWR) of nuclear power plants due to its high corrosion resistance. Although those are a highly corrosion resistance material, their stress corrosion cracking(SCC) have been found on occasion, which are deeply related to a surface oxide film on a base material which have occurred on the primary side as well as the secondary side of a tubing. And The SCC is accelerated in the existing Pb which is the impurity of secondary steam generator components. The Oxide on a steel surface in an aqueous solution above 100 .deg. C is composed of a duplex film structure. The inner layer of the oxide is dense and less porous, which is formed by a growth of the oxide layer on the metal surface. The outer layer of the oxide is less adhesive, which is formed by a dissolution and precipitation mechanism. Growth processes of the inner ...

Energy Technology Data Exchange (ETDEWEB)

There are many factors affecting diffusion bonding in order to obtain high quality joining. Therefore, in the beginning, we constructed diffusion bonding model based on void growth mechanism to predict bonding pressures and times. In addition, in order to compare theoretical values with experimental values, diffusion bonding tests were carried out by using commercial AZ31 magnesium alloy sheets with different grain sizes, 16 and 130 {mu}m. The present AZ31 alloys were successfully diffusion bonded at several conditions, and the bonding strength was more than 0.8 of each parent materials. The experimental bonding conditions in high quality joining, times and pressures, were good agreed with prediction analysis. (orig.)

International Nuclear Information System (INIS)

Research highlights: ? Reports a high protection system for the alloy in corrosive environment. ? Describes an interfacial process with self-healing properties. ? Reports the influence of substrate pre-treatment in the coating performance. - Abstract: In this paper the interface of poly(vinylidene fluoride) coatings prepared by the dip coating method and HF-treated AZ31 magnesium alloy was evaluated. The best performance of this system in corrosion tests compared to ground, as-received and acetic acid cleaned substrates is related to an acid-base interaction at the interface and to interfacial reactions which resulted in a self-healing process. The protectiveness of the samples was investigated using impedance and immersion tests while the coating morphology and interface stability were investigated by scanning electron microscopy, X-ray photoelectron spectroscopy and adhesion tests.

British Library Electronic Table of Contents (United Kingdom)

The age hardening behavior of Al-4.5%Cu alloy composite reinforced with zircon sand particulates and produced by stir casting route has been investigated in different quenching media viz, water, oil, and salt brine solution (7wt%). Optical microscopy of the as cast alloy composite indicates that the matrix of the composite has the cellular structure. Copper rich CuAl2 precipitates have been found near particle matrix interface. The results of ageing demonstrate that the microhardness of age hardenable Al-Cu based alloy composites depend on the quenching medium in which they are heat treated. Salt brine quenching is faster as compared to water and oil, even if higher strength is obtained but cannot be used for complex shapes and thin sections where oil quenching is the alternative due to mi...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Even though metal ceramic restorations (MCRs) are widely used by clinicians, the influence of the metal on the color of overlaying porcelain is unknown. Purpose The purpose of this study was to analyze the color alterations of different types of metal ceramic alloys during several stages of metal surface preparation and to determine the effect of those changes on the resulting color of opaque porcelain (OP). Material and Methods Seven different types of alloys (3 base metal, 3 noble, and 1 high noble) were used to prepare disk-shaped specimens (1 mm x 10 mm, n=3), followed by OP application (0.1 mm). Lab values of specimens were recorded after different stages of metal surface preparation (ingot, after casting, after oxidation, and after the OP application) in addition...

Energy Technology Data Exchange (ETDEWEB)

Microstructure characterization is important for controlling the quality of laser welding. In the present work, a detailed microstructure characterization by transmission electron microscopy was carried out on the laser welding cast Ni-based superalloy K418 turbo disk and alloy steel 42CrMo shaft and an unambiguous identification of phases in the weldment was accomplished. It was found that there are {gamma}-FeCrNiC austenite solid solution dendrites as the matrix, (Nb, Ti) C type MC carbides, fine and dispersed Ni{sub 3} Al {gamma}' phase as well as Laves particles in the interdendritic region of the seam zone. A brief discussion was given for their existence based on both kinetic and thermodynamic principles.

International Nuclear Information System (INIS)

The size distributions of precipitated Ni clusters on the surface of a LaNi_5-based alloy immersed in alkaline solution (alkaline treatment) at 383 K for 0-110 min were precisely determined by combining superparamagnetic analysis and transmission electron microscopy (TEM) observations. The superparamagnetic analysis indicated that the diameters of the Ni clusters were smaller than #approx#25 nm in all samples, while their average values increased approximately from 5 to 9 nm with increasing alkaline treatment time. The spatial distribution of the Ni clusters was successively observed by TEM, which agreed fairly well with the estimated size distribution by superparamagnetic analysis. Therefore, estimation of the actual size distribution of Ni clusters by superparamagnetic analysis was proved to be feasible. Based on the above results, a precipitation process for Ni clusters by alkaline treatment is proposed.

International Nuclear Information System (INIS)

Solid solution-strengthened nickel base alloys have been used for nuclear stream generator tubing in pressurized water reactors since the beginnings of commercial nuclear power. The purpose of this paper is to recap and update the authors understanding of the relationship between processing, resulting structure, and properties for Alloy 600 and to discuss the requirements for optimized performance in both primary and secondary environments. Potential replacement materials and their performance will be discussed. Also discussed is the role and importance of system chemistry, bulk and local, and control and its relationship to performance. A discussion of potential mechanisms of environmentally assisted failure is also discussed.

Energy Technology Data Exchange (ETDEWEB)

The report covers the results of exposing materials for steam turbines to increased steam temperatures in two modules of the KOMET 650 testing facility at the Westfalen power plant. Ferritic/martensitic steels with 9 to 12% Cr and austenite and nickel-based alloys were investigated. Some experimental coatings on low-alloy Cr steel were also tested. The principal findings are presented. It will become possible to construct advanced power stations to be operated at higher temperatures. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The goal of this project is to provide materials engineers, chemical engineers and plant operators with a software tool that will enable them to predict localized corrosion of process equipment including fabricated components as well as base alloys. For design and revamp purposes, the software predicts the occurrence of localized corrosion as a function of environment chemistry and assists the user in selecting the optimum alloy for a given environment. For the operation of existing plants, the software enables the users to predict the remaining life of equipment and help in scheduling maintenance activities. This project combined fundamental understanding of mechanisms of corrosion with focused experimental results to predict the corrosion of advanced, base or fabricated, alloys in real-world environments encountered in the chemical industry. At the heart of this approach is the ...

Energy Technology Data Exchange (ETDEWEB)

In this work a Ni-based superalloy GMR 235 was investigated. We determined convenient metallographic methods for preparation of bulk metallographic specimens, extraction carbon replicas, transparent metallic foils and minor phase extraction. In addition, the alloy microstructure was characterised using different metallographic techniques. (orig.)

International Nuclear Information System (INIS)

Past elastic-plastic fracture studies for leak-before-break (LBB) assessment of low alloy steel pipings have been focused mostly on the behavior of base metals and their weld metals. In contrast, the heat-affected zone (HAZ) of a welded pipe has not been studied in detail primarily because the size of the HAZ is too small to make specimens for mechanical properties measurements. In this study, microstructural analyses, microhardness tests, tensile tests and J-R tests have been conducted as a function of distance from a fusion line and temperature for HAZ materials of SA106Gr.C low alloy piping steels. For the ferrite-pearlite steels such as SA106Gr.C, the HAZ specimens showed a higher yield strength and fracture toughness compared with those of its base metal. These characteristics, despite of grain coarsening, can be explained by cleaner microstructures of HAZ materials with a finer morphology of ...

Energy Technology Data Exchange (ETDEWEB)

It is necessary to measure strength and creep behavior to guarantee the safe and reliable usage of refractory alloys at extremely high temperatures. In the literature there is very little information available about the properties of Mo-Re alloys at temperatures higher than 1000 C. A special test facility has been designed and built for stress-rupture testing at very high temperatures (up to 3000 C) of refractory metals and alloys in inert atmospheres. - The stress-rupture strength as well as the creep behavior of molybdenum-rhenium alloys with rhenium contents between 41 and 51 wt.% have been determined at temperatures ranging from 1200 to 2000 C, and rupture times of up to 10 hours using this facility. Previous measurements of stress-rupture strength and creep behavior of pure rhenium have been compared with the measurement results of Mo-Re alloys. - The discussion of the values ...

International Nuclear Information System (INIS)

Surface analytical studies of high nitrogen austenitic stainless steels exposed to deaerated 0.1M HCl have revealed that nitrogen alloying additions influence the composition of salt layers and the passive film/alloy interface. In this study the authors employ electrochemical techniques and variable angle X-ray Photoelectron Spectroscopy (XPS) to examine the passive films formed on a series of austenitic stainless steels, Fe18Cr8Ni, Fe18Cr8Ni0.2N, Fe20Cr20Ni, Fe20Cr20Ni6Mo and Fe20Cr20Ni6Mo0.2N, in acidic chloride aqueous solution. In addition, several other model alloys, Fe19Cr, Fe19Cr9Ni, Fe19Cr2.5Mo, and Fe19Cr9Ni2.5Mo, were examined before and after electrochemical surface nitriding, a technique proven to have an effect analogous to N alloying. It was shown that nitrogen, nickel and molybdenum additions independently and in certain combinations stimulate selective dissolution of iron, resulting in a ...

Energy Technology Data Exchange (ETDEWEB)

This report presents the results of cladding technology development under the Coal-Fired Combined Cycle DOE Project. Clad Alloy Development, involved the selection, fabrication and burner rig evaluation of advanced clad alloy composition diffusion-bonded to IN-738. Testing was conducted for up to 5800 hours at 1600/sup 0/F in a simulated PFB environment. Metallographic evaluation showed Co-base cladding alloys PFB-5PM and PFB-6PM (aluminided) and Fe-base alloy GE-2541 to be the most corrosion resistant. The formability and fabricability of sheet material was significantly improved for these alloys by utilizing powder metallurgy techniques. Clad Process Development encompassed processing activities to evaluate sheet alloy formability, bucket surface preparation techniques, platform clad forming, and the activated ...

International Nuclear Information System (INIS)

The physical, chemical and mechanical properties of magnesium alloys make them attractive materials for automotive and aerospace applications. However, these materials are susceptible to corrosion and wear. This work discusses the potential of using sol-gel based coatings consisting of ZrO_2 and 15 wt.% of CeO_2. The CeO_2 component provides enhanced corrosion protection, while ZrO_2 impart corrosion as well as wear resistance. Coating deposition was performed by the dip coating technique on two magnesium alloy substrates with different surface finishes: AZ91D (as-casted, sand-blasted, and machined) and AZ31 (rolled and machined). All as-deposited coatings (xerogel coatings) were then subjected to 10 h annealing: a temperature of 180 C was applied to the AZ91D alloy and 140 C to the AZ31 alloy. Morphological and structural properties of the annealed coatings were investigated by ...

Energy Technology Data Exchange (ETDEWEB)

The objective of the project was to develop an infiltration material based on SiC that should have improved corrosion resistance and should permit higher operating temperatures. From a variety of tested doping agents, zirconium silicide and molybdenum proved to be the most appropriate agents. The respective infiltration materials permit a combination of advantages of the SSiC with those of the SiSiC. Silicide SiC, analogous to the SiSiC, is almost nonshrinking, and above all is more corrosion-resistant than SiSiC in the alkaline regime, due to the replacement of free silicon by silicide phases. The operating temperature of the molybdenum-base variant is 1600 C. (orig./CB) [Deutsch] Ziel des Vorhabens war die Entwicklung eines Infiltrationswerkstoffes auf SiC-Basis mit verbesserter Korrosionsbestaendigkeit und hoeherer Einsatztemperatur. Aus einer Vielzahl von getesteten Dotierungsmoeglichkeiten kristallisierten sich ...

Energy Technology Data Exchange (ETDEWEB)

Semiconductor properties of passive films formed on the Fe-18Cr alloy in a borate buffer solution (pH = 8.4) and 0.1 M H{sub 2}SO{sub 4} solution were examined using a photoelectrochemical spectroscopy and an electrochemical impedance spectroscopy. Photo current reveals two photo action spectra that derived from outer hydroxide and inner oxide layers. A typical n-type semiconductor behaviour is observed by both photo current and impedance for the passive films formed in the borate buffer solution. On the other hand, a negative photo current generated, the absolute value of which decreased as applied potential increased in the sulfuric acid solution. This indicates that the passive film behaves as a p-type semiconductor. However, Mott-Schottky plot revealed the typical n-type semiconductor property. It is concluded that the passive film on the Fe-18Cr alloy formed in the borate buffer solution is composed of both n-type outer hydroxide and inner ...

International Nuclear Information System (INIS)

Fe-Cu binary alloys are often used to mimic the behaviour of reactor pressure vessel steels. Their study allows identifying some of the defects responsible for irradiation-induced hardening. But recently the influence of manganese and nickel in low-Cu steels has been found to be important as well. In contrast with existing models found in the literature, which predict that hardening saturates after a certain dose, Fe alloys containing nickel and manganese irradiated in a material test reactor (BR2) show a continuous increase of hardening, up to doses equivalent to about 40 years of operation. Considerations based on positron annihilation spectroscopy analyses suggest that the main objects causing hardening in Cu-free alloys are most probably self-interstitial clusters decorated with manganese. In low-Cu reactor pressure vessel steels and in Fe-CuMnNi alloys, the main effect is still ...

International Nuclear Information System (INIS)

We present a comprehensive, up-to-date compilation of band parameters for the technologically important III - V zinc blende and wurtzite compound semiconductors: GaAs, GaSb, GaP, GaN, AlAs, AlSb, AlP, AlN, InAs, InSb, InP, and InN, along with their ternary and quaternary alloys. Based on a review of the existing literature, complete and consistent parameter sets are given for all materials. Emphasizing the quantities required for band structure calculations, we tabulate the direct and indirect energy gaps, spin-orbit, and crystal-field splittings, alloy bowing parameters, effective masses for electrons, heavy, light, and split-off holes, Luttinger parameters, interband momentum matrix elements, and deformation potentials, including temperature and alloy-composition dependences where available. Heterostructure band offsets are also given, on an absolute scale that allows any material to be aligned ...

International Nuclear Information System (INIS)

The thermal transformation of Al-base icosahedral phases was studied in-situ by real time neutron powder diffraction. Different compositions have been selected in order to vary the initial phase morphology and change the neutron scattering contrast between species. Alloys with low silicon and large aluminium contents produce first the orthorhombic O-Al_6Mn modification. In alloys with larger silicon content, the #alpha#-AlMnSi cubic phase appears soon after the beginning of the transformation but is still preceeded by O-Al_6Mn. Depending on compositions, the crystallization of the icosahedral phase is controlled either by the diffusion of Al through its interface with the residual fcc aluminium or that of Si within the bulk. The results are discussed in the light of current structural models. (author) 40 refs., 14 figs., 3 tabs.

International Nuclear Information System (INIS)

Up to 90% of the life time of cyclically loaded components is determined by short crack initiation and propagation. This stage of the fatigue damage process is strongly influenced by microstructural features, e.g. grain boundaries and crystallographic grain orientation. Therefore LEFM can not be applied in a reasonable manner explaining the demand for a mechanism-related modelling method. The present study deals with mechanical testing and microstructural examinations applied to the relatively new #beta#-titanium alloy LCB. The results are used as data base to develop a new short crack model that is based on the model of Navarro and de los Rios. By using various techniques such as electron back-scattered diffraction and finite-element calculations the origin of crack initiation is revealed and the characteristics of crack propagation is determined. (orig.)

International Nuclear Information System (INIS)

The temperature dependences of the heat capacity of commercial titanium VT1-0 and alloys on its base, VT5 and VT5-1, have been derived in the temperature range of 4 to 290 K. For comparison, similar measurements have been conducted on pure titanium and specially prepared solid solutions on its base (Ti+3.7 at.% Al and Ti+0.82 at.% Sn). The measurement accuracy has been sufficient for comparing the results with calculation data. The obtained results are interpreted using the known concepts of the role of the mass of interstitial atoms and changes in the interatomic bond forces. It is shown that the phonon components of the molar heat capacities of solid solutions of Al in titanium have lower values in the entire temperature range, as compared to titanium. The corresponding differences are proportional to the Al concentrations. The lower molar heat capacity in the case of dissolution of Al is due to the low mass of the ...

Energy Technology Data Exchange (ETDEWEB)

Stress corrosion cracking tests in constant extension rate tensile (CERT) and constant load tensile (CLT) tests were conducted on Ni-xCr- 9Fe-yC in Ar, water, and a LiOH-boric acid solution. Cr and C improve the resistance of Ni-base alloys to IG cracking in both Ar and water at 360C. Since creep plays a role in IG cracking, one possible explanation for the role of the environment involves its effect on the creep. Experiments were conducted on the role of C in the deformation behavior and failure mode of Ni-16Cr-9Fe. Constant load experiments were conducted on Ni-16Cr-9Fe to determine if the CLT test is more aggressive than CERT. The electron backscattering technique in a SEM is being developed in order to extend the IG cracking studies to grain sizes typical of commercial alloys, 20-30 microns.

Energy Technology Data Exchange (ETDEWEB)

Weldability and high temperature strength properties of Hastelloy Alloy XR were investigated in order to evaluate the materials performance of base metal and filler metal for the High Temperature Engineering Test Reactor (HTTR) uses. The weldability was examined by means of the chemical analysis in the deposited metals, optical microscopy, FISCO test, hardness measurements and bend test. The high temperature strength properties were investigated through tensile tests at R.T., 800, 900 and 950degC in air, and creep and creep rupture tests at 900 and 950degC in air. The results obtained by each test showed favorable performance. In particular, the bend test which is considered to be critical pass demonstrated low susceptibility to weld cracking through the optimization of B and C contents in the filler metal and by narrowing the groove. Creep rupture strength was nearly equal or higher than those of Hastelloy Alloy XR master ...

Energy Technology Data Exchange (ETDEWEB)

A joint materials test program developed by the Institute for Mining and Minerals Research (IMMR) and the Tennessee Valley Authority (TVA) involved the postexposure mechanical properties and corrosion behavior of candidate structural materials in an experimental, atmospheric fluidized-bed combustor (AFBC). This combustor was operated by Accurex Corporation at Research Triangle Park, North Carolina, under the direction of TVA. The materials studied were Type 304, Type 310, and INCOLOY alloy 800 in the form of disc coupons with and without crevice configurations. Type 304 was also used for mechanical property measurements. The alloys were exposed to the combustor environment at about840/sup 0/C for approximately 330 hours. The ranking in terms of decreasing weight loss was: (1) Type 304, (2) Type 310, and (3) INCOLOY alloy 800. The presence of tight crevices did not enhance the corrosion rate. In addition, the corrosion ...

Energy Technology Data Exchange (ETDEWEB)

A molybdenum (Mo) adsorbent called PZC (Poly Zirconium Compound) with high efficiency of Mo adsorption has been developed in order to generate {sup 99m}Tc from {sup 99}Mo produced from natural Mo by (n, gamma) method. The {sup 99m}Tc generator using PZC has cleared mostly the technical subjects. By the results of many experiments, cold and hot test with {sup 99}Mo activity from low level (10{sup 5} Bq) to high level (10{sup 10} Bq), it has been confirmed that the PZC method can be practically applied for the (n, gamma) {sup 99}Mo-{sup 99m}Tc generator. From the reasons that PZC has the ability and many merits such as high adsorption capacity (>250 mg-Mo/g-PZC) of Mo, high elution yield (av. 80%) of {sup 99m}Tc, the low breakthrough (<0.05 kBq-{sup 99m}Mo/MBq-{sup 99m}Tc) of {sup 99}Mo and others, the current (n, fission) {sup 99m}Tc generator utilizing {sup 99}Mo produced from enriched uranium will be taken the place by PZC method. In this paper, the ...

Energy Technology Data Exchange (ETDEWEB)

Four subprojects were completed: development and evaluation of die coatings, accelerated die life characterization of die materials, evaluation of fluid flow and solidification modeling programs, selection and characterization of Al-based die casting alloys, and influence of die materials and coatings on die casting quality.

International Nuclear Information System (INIS)

The main compositions of iron-base amorphous self-fluxing alloy powders of 150 mesh, used in this work, are Fe, Cr, Ni, W, Mo, B, Si and C. The ranges of each element in at% are (65-70)Fe, (3-5)Cr, (2-4)Ni, (2-4)W, (1-2)Mo, (10-14)B, (4-7)Si and (2-3)C. The atomic ratio of metal-metalloid is about 80:20, so this alloy is abbreviated as M_8_0X_2_0. The material on which coatings were deposited is 1020 steel, austenitized for 1h at 880 C, water quenched, and tempered at 180 C for 1h. This heat treatment resulted in a low carbon martensite structure with a hardness of HRC35-45. After cleaning, shot blasting and preheating the steel to about 200 C, the authors sprayed a thin Ni-Al alloy layer of about 0.1--0.15mm in thickness onto the specimen by means of an oxygen-acetylene torch to provide better bonding of the coating with substrate. Then the M_8_0X_2_0 and M_8_0X_2_0+8%CeO_2 alloy ...

International Science & Technology Center (ISTC)

Determination of Special Molybdenum Alloys Optimal Structure Using the Cybernetic Method

International Science & Technology Center (ISTC)

Development of the Corrosion Protection Technology for Special Steels and Alloys

International Nuclear Information System (INIS)

In order to improve the reliability of PWR steam generators, we have performed research to improve the tubing material and tube-support-plate configuration, based on our wide operating experience, and have developed and verified Alloy TT690 as the optimum tubing material and the BEC (Broached Egg Crate) type tube-support design. In the research, we have studied the metallurgical mechanism of the alloy to improve its corrosion resistance, evaluated corrosion susceptible region quantitatively, estimated the actual environment in a steam generator and confirmed the reliability by a model boiler test over a long period. It has been verified that the steam generator with the latest design has higher reliability with respect to the corrosion resistance of tubes. (author).

Energy Technology Data Exchange (ETDEWEB)

Mechanical alloying is an important pre-requisite for the manufacturing of heat resistant oxide-dispersion-strengthened superalloys. Though the microstructure of these materials after hot extrusion and recrystallization treatment is well documented, little is known about the microstructural evolution during ball-milling. A method was tested to prepare electron transparent foils and extraction replica from powder particles for TEM investigations. The microstructure was found to consist of a Ni-Cr-Al solid solution in which submicron particles of refractory metals were embedded. The extremely fine grainize of about 50 nm is the consequence of severe plastic deformation. Yttria particles could not be detected in the powder after ball milling, but after a heat treatment at 1000 C the well-known fine dispersion of oxide particles was evident. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Materials for the construction of cold neutron sources must satisfy a range of demands. The cryogenic temperature and irradiation create a severe environment. Candidate materials are identified and existing cold sources are briefly surveyed to determine which materials may be used. Aluminum- and magnesium-based alloys are the preferred materials. Existing data for the effects of cryogenic temperature and near-ambient irradiation on the mechanical properties of these alloys are briefly reviewed, and the very limited information on the effects of cryogenic irradiation are outlined. Generating mechanical property data under cold source operating conditions is a daunting prospect. It is clear that the cold source material will be degraded by neutron irradiation, and so the cold source must be designed as a brittle vessel. The continued effective operation of many different cold sources at a number of reactors makes it clear ...

International Nuclear Information System (INIS)

The grain size dependence of the tensile properties and the deformation mechanisms responsible for those properties are examined for Mg alloy, AZ31B, sheet. Specifically, the Hall-Petch effect and strain anisotropy (r-value) are characterized experimentally, and interpreted using polycrystal plasticity modeling. {1 0 . 2} extension twins, {1 0 . 1} contraction twins, and so-called 'double-twins' are observed via microscopy and diffraction-based techniques, and the amount of twinning is found to increase with increasing grain size. For the sheet texture and tensile loading condition examined, {1 0 . 2} extension twinning is not expected, yet the polycrystal plasticity model predicts the observed behavior, including this 'anomalous' tensile twinning. The analysis shows that the Hall-Petch strength dependence, of the polycrystal as a whole, is primarily determined by the grain size dependence of the strength of the prismatic slip systems.

International Nuclear Information System (INIS)

The gliding modes of a duplex Ti-6Al-4V titanium alloy were investigated through in situ (scanning electron microscopy) tensile tests. A method based on electron back-scattering diffraction (EBSD) measurements was used to identify activated slip systems. The approach applied to a large number of grains allowed a statistical analysis of the nature (basal, prismatic, pyramidal) and distribution of the slip systems according to the crystallographic texture. A discussion concerning the pertinence of Schmid's law to explain the occurrence and succession of slip events is then proposed. The domain in favor of each type of slip system is finally presented by using inverse pole figures mapped with Schmid's factor iso-curves.

International Nuclear Information System (INIS)

Ti and its alloys (Ti-6Al-4V) have been used in different engineering applications due to their several outstanding properties. Nevertheless, their use in practical applications is limited in many cases due to their poor tribological property. Researches are ongoing on surface modification of Ti based materials by different plasma and ion based techniques to overcome this problem. However, the conventional plasma nitriding techniques have several problems such as formation of an arc, increased possibility of surface contamination due to a comparatively higher operating pressure, production of a very thin nitrided layer after a long processing time, etc. In this present work, the possibility of a new low-pressure plasma nitriding process using a Plasma Enhanced Chemical Vapor Deposition (PECVD) based saddle field fast atom beam source on a Ti-6Al-4V alloy sample is investigated. ...

International Nuclear Information System (INIS)

We provide a numerically efficient procedure to perform LDA+Hubbard I calculations including self-consistency over the charge density in the FP-LAPW basis. The method is applied to Pu, Am, and PuAm and PuCe alloys. Our results for valence photoemission spectra (PES) agree with experimental data and with previous LDA+DMFT calculations. Analysis of the J=5/2 and J=7/2 contributions to the f-occupation supports the intermediate-coupling picture of f-states in heavy actinides. The electronic specific heat coefficient is calculated for PuAm and PuCe alloys in reasonable agreement with recent experiments. We show that Pu atoms keep their mixed-valence character in these alloys. Next, we study electronic and spectral properties of Pu-based superconductor PuCoGa_5 and obtain good agreement with experimental PES. Finally, we analyze surface effects. In Pu monolayer, we find substantial modification of PES due to ...

Energy Technology Data Exchange (ETDEWEB)

The excellent high temperature strength and thermal conductivity of molybdenum-base alloys provide attractive features for components in advanced magnetic and inertial fusion devices. Refractory metal alloys react readily with oxygen and other gases. Oxidized molybdenum in turn is susceptible to losses from volatile molybdenum trioxide species, MoO{sub 3}(m), in air and the hydroxide, MoO{sub 2}(OH){sub 2}, formed from water vapor. Transport of radioactivity by the volatilization, migration, and re-deposition of these volatile species during a potential accident involving a loss of vacuum or inert environment represents a safety issue. In this report the authors present experimental results on the oxidation, volatilization and re-deposition of molybdenum from TZM in flowing air between 400 and 800 C. These results are compared with calculations obtained from a vaporization mass transfer model using chemical thermodynamic ...

British Library Electronic Table of Contents (United Kingdom)

The effect of Mo addition on the glass-forming ability (GFA), magnetic properties, mechanical properties and corrosion resistance of (Fe0.76Si0.096B0.084P0.06)100-xMox (x=0, 2, 4 and 6at.%) bulk glassy alloys (BGAs) with high Fe contents was investigated. The 2at.% Mo addition makes the alloy composition approach towards a eutectic point, which could result in an increase in the GFA. The BGA rod with diameters up to 3.5mm was produced by copper mold casting. These BGAs exhibit a rather high saturation magnetization of 0.98-1.51T and lower coercive force of 1.7-2.1A/m. A significant improvement in corrosion resistance was observed with microalloying Mo element in 1N H2SO4 solution. Furthermore, these Fe-based BGAs show super-high strength of ~3.3GPa and Young's modulus of 200GPa.

Energy Technology Data Exchange (ETDEWEB)

Alkaline fuel cells (AFCs) provide a less corrosive environment and can provide higher electrode reaction kinetics than proton exchange membrane fuel cells (PEMFCs). The alkaline media also allows for the replacement of platinum (Pt) based electrocatalysts with non-Pt electrocatalysts. Studies have shown that palladium (Pd) and silver (Ag) form a homogenous solid solution with a face-centred cubic structure within a large range of temperatures. This study described the results of an oxygen reduction reaction (ORR) on lead-silver (Pd-Ag) alloy electrodes in alkaline media. The reaction was compared with Pd and Ag electrodes. The alloys were synthesized as thin films using a sequential electroless deposition of Pd and Ag on stainless steel discs followed by an annealing procedure in an Ar stream. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used to characterize ...

Energy Technology Data Exchange (ETDEWEB)

Metals for potential use in the dissociator and the synthesizer reactors of a distributed solar receiver thermochemical transport loop utilizing SO/sub 3//SO/sub 2//O/sub 2/ molecular chemistry includes stainless steels and iron-base, nickel-base and cobalt-base superalloys. We tested these alloys in SO/sub 2//O/sub 2/ mixtures and SO/sub 3/ gas at 500/sup 0/C and 900/sup 0/C, respectively, for times of up to four weeks. Weight gain measurements were used to determine the oxidation/sulfidation kinetics and electron microprobe analysis was used to measure penetration of oxygen and sulfur into the metal and to identify the formation of internal oxides and sulfides. Results of these tests showed that the most promising candidates are those containing sufficient quantities of both aluminum and chromium alloying additions to be alumina and chromia formers, such as Kanthal A-1, Nimonic ...

Energy Technology Data Exchange (ETDEWEB)

Out of the R and D of mesoscopic metal group composite materials, the paper described the fiscal 1997 results. In the in-situ method as a composite material making method, elucidated to some degree were chemical composition of Fe-C-Cr-V-Nb-Mo-W-Ni base multi-dimensional alloys, and wear resistance and oxidation resistance of MC type carbide dispersion multi-phase texture crystallizing as primary crystal and eutectic. In the composite material making with ceramic fiber and alloy by the pressure infiltration method, the paper clarified the texture formation mechanism in solidification/heat treatment by a combination of Al alloys and alumina long fiber, and the relation between fiber configuration and wear resistance. By MA and MG methods as the powder metallurgy composite material making method, a composed body of {alpha}-stainless steel of Fe-12%Cr composition and M23C6 of 40-90vol% are designed for ...

International Nuclear Information System (INIS)

The "6"2Zn-"6"2Cu generator system is one of the few which yield a pure positron emitting daughter. The authors have developed a method for the preparation of this generator system following 32 MeV #alpha# particle bombardment of nickel targets. The chemical processing involves two stages: first a hydrous zirconium oxide column is used at pH 4-5 to separate the zinc and copper activities produced in the target nickel, and secondly, a conventional anion exchange column is used to retain the "6"2Zn and remove all copper activities in 2M HCl. This column serves as the "6"2Cu generator which will yield pure "6"2Cu repeatedly, free from "6"2Zn and other impurities, in a mixture of HCl and NaCl. A method is outlined also to obtain a solution of "6"2Zn using the hydrous zirconium oxide (HZO) column. "6"1Cu can be prepared as a by-product in the above procedure, but a method for the preparation of "6"1Cu alone using an 18 MeV #alpha# particle beam on a ...

Energy Technology Data Exchange (ETDEWEB)

Aluminium AA5182 coupons covered by a polyaniline film in the emeraldine base (EB) form showed increasing corrosion potential and decreasing corrosion current as a function of the thickness of the polymer layer. The cathodic reaction was proved not limited by diffusion of species inside the electrolyte solution and oxygen had no effect on the electrochemical behaviour of the coated samples. An EB coating on indium tin oxide conducting layer appeared slightly electroactive in neutral media. The IR spectra of aluminium coated samples, before and after heating in argon atmosphere, confirmed a redox reaction between the polymer film and the metal. This galvanic coupling can explain the good protective behaviour of emeraldine base against corrosion of aluminium.

Science.gov (United States)

... MOLYBDENUM ALLOY GUN BARREL LINERS o0 in ... NEW POWDER TECHNOLOGIES FOR MOLYBDENUM ALLOY GUN BARREL LINERS ...

International Nuclear Information System (INIS)

... filters molybdenum alloys production sulfuric acid alloys chemical reactions ...

International Nuclear Information System (INIS)

This patent describes the producing of a refractory metal wherein a sponge refractory metal is produced as an intermediate product by the use of magnesium with the incidental production of magnesium chloride, and wherein residual magnesium is separated from the magnesium chloride and from refractory metal to a vacuum distillation step which fractionally distills the magnesium, the magnesium chloride, and the metal sub-chlorides; the steps of: recovering fractionally distilled vapors of magnesium chloride and metal sub-chlorides from a sponge refractory metal; separately condensing the vapors as separately recovered; and recycling the separately recovered magnesium at a purity of at least about 96%.

Energy Technology Data Exchange (ETDEWEB)

The corrosion behaviour of friction stir welded (FSW) joints of AA 5083 has been compared to that of MIG welded joints. Pitting and stress corrosion cracking (SCC) resistance in 3.5% NaCl + 0.3 g/l H{sub 2}O{sub 2} and in EXCO (4 M KCl + 0.5 M KNO{sub 3} + 0.1 M HNO{sub 3}) solutions has been determined at 25 C. SCC susceptibility was evaluated by slow strain rate tests (SSRT), at a strain rate of 1 x 10{sup -6}s{sup -1}. Welds obtained by FSW technique showed a higher corrosion resistance in EXCO solution and a lower pitting tendency than the base alloy. Electrochemical measurements (corrosion potential measurements, polarization curves recording) evidenced that FSW weld was cathodic to base alloy. FSW joints were not susceptible to SCC in both test solutions, whereas MIG joints cracked in both solutions. (orig.)

Science.gov (United States)

Experimental trials of autogenous deep penetration welding between dissimilar cast Ni-based superalloy K418 and alloy steel 42CrMo flat plates with 5.0 mm thickness were conducted using a 3 kW continuous wave (CW) Nd:YAG laser. The influences of laser output power, welding velocity and defocusing distance on the morphology, welding depth and width as well as quality of the welded seam were investigated. Results show that full keyhole welding is not formed on both K418 and 42CrMo side, simultaneously, due to the relatively low output power. Partial fusion is observed on the welded seam near 42CrMo side because of the large disparity of thermal physical and high-temperature mechanical properties of these two materials. The microhardness of the laser-welded joint was also examined and analyzed. It is suggested that applying negative defocusing in the range of Raylei length can increase the welding depth and improve the coupling efficiency of the ...

International Nuclear Information System (INIS)

In this work, the Calibration-Free approach for Laser-Induced Breakdown Spectroscopy (CF-LIBS) was applied for the first time to radially resolved spectra emitted by a laser-induced plasma. The radial profiles of plasma temperature and electron number density were used to calculate the local relative concentration of the elements of interest. We analyzed a set of profiles of the local spectral emission coefficient obtained previously by means of spatial deconvolution of the spectra from a copper-based alloy (Cu 93, Fe 5, Mn 1, Ni 1 wt.%) laser-induced plasma. A spatially integrated spectrum of the same plasma was also analyzed for comparison purpose. The relative abundance of the minor components Fe, Mn and Ni was calculated. The results obtained from the central region of the plasma were closer to the nominal concentrations than those obtained from the spatially integrated spectrum. However, an increasing deviation was observed towards the ...

Science.gov (United States)

A general model for the dissolution of particles in multi-component alloys is proposed and analyzed. The model is based on diffusion equations with cross-terms for the several species, combined with a Stefan condition as the equation of motion of the interface between the particle and diffusive phase. Several numerical schemes for the solution of the Stefan problem are proposed and compared. It turns out that diagonalization is useful for numerical purposes. However, for the case of position-dependent diffusion coefficients one has to use a different scheme. Here, we analyze stability and workload of several time integration methods.

International Nuclear Information System (INIS)

The single specimen unloading compliance technique has become the preferred method for evaluating J-integrals. It involves data acquisition and analysis using a computer. This paper describes in detail the development of a simple experimental system and related software that can be used in a laboratory equipped with a microcomputer and with access to a minicomputer. The effects of loading rate, test temperature, specimen geometry and material composition can be readily evaluated using this system. The results on a pressure vessel steel and an #alpha#-#beta# titanium alloy are discussed in Part II. (author).

Energy Technology Data Exchange (ETDEWEB)

NO abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

In order to overcome the inherent disadvantages of Ti-V-based hydrogen storage alloys, such as poor activation behavior and low high-rate dischargeability, the novel composites Ti{sub 0.17}Zr{sub 0.08}V{sub 0.35}Cr{sub 0.1}Ni{sub 0.3}-x wt.% La{sub 0.7}Mg{sub 0.3}Ni{sub 2.75}Co{sub 0.75} (x = 0, 5, 10 and 20) were successfully synthesized by ball milling method in the present study. And the structure and overall electrochemical properties of as-prepared composites are investigated systemically. The electrochemical studies show that the maximum discharge capacity of the composite electrodes displays no variation with the increase of La{sub 0.7}Mg{sub 0.3}Ni{sub 2.75}Co{sub 0.75} content, whereas the high-rate dischargeability (HRD) and the activation behavior are distinctly improved with increasing x. The electrochemical hydrogen kinetics of composite electrodes is also studied by means of electrochemical impedance spectroscopy (EIS), linear ...

Energy Technology Data Exchange (ETDEWEB)

For joining type 316LN austenitic stainless steel to modified 9Cr-1Mo steel for power plant application, a trimetallic configuration using an insert piece (such as alloy 800) of intermediate thermal coefficient of expansion (CTE) has been sometimes suggested for bridging the wide gap in CTE between the two steels. Two joints are thus involved and this paper is concerned with the weld between 316LN and alloy 800. These welds were produced using three types of filler materials: austenitic stainless steels corresponding to 316,16Cr-8Ni-2Mo, and the nickel-base Inconel 182{sup 1}. The weld fusion zones and the interfaces with the base materials were characterised in detail using light and transmission electron microscopy. The 316 and Inconel 182 weld metals solidified dendritically, while the 16-8-2(16%Cr-8%Ni-2%Mo) weld metal showed a predominantly cellular substructure. The Inconel weld metal contained a ...

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

Alloys are described which contain nickel, aluminum, boron, iron and in some instances manganese, niobium and titanium.

Science.gov (United States)

A large double-focusing mass spectrometer was used to obtain new values for the masses of Sr/sup 86/, Sr/sup 88/, and Zr/sup 90/. Mass differences calculated from these values are found to be in better agreement with nuclear transmutation information than were previous mass spectroscopically derived values. (auth)

Science.gov (United States)

The production of water from a subterranean formation is reduced by contacting the formation with a water dispersible hydrophilic organic polymer having a molecular weight greater than 100,000 and containing carboxyl functionality and a crosslinking composition comprising water, a zirconium compound having a value of 4+, an alpha-hydroxy acid and an amine compound.

International Nuclear Information System (INIS)

The Self Actuated Shutdown System (SASS) is now under development for use in a large scale FBR, in order to establish the passive shutdown capability against the postulated ATWS events, i.e. ULOF, UTOP and ULOHS. The function of SASS makes use of the safety characteristics of a liquid metal cooled FBRs such as a large subcooling and low pressure system. The insertion of the control rods insertion is assured even in the most conservative seismic design condition by employing articulate rods and the SASS will be installed into the detaching mechanism employing a curie point the magnet alloy. ULOF analysis of the present FBR shows that coolant boiling inception is prevented if a control rod of the SASS is detached at the uppermost temperature of 680degC for the Curie point magnet, and after the reactor shutdown the coolant temperature is kept below 600degC by the pony motor flow. Therefore the SASS will establish passive shutdown capability without affecting the core ...

Energy Technology Data Exchange (ETDEWEB)

The Neutral Beam Test Facility (NBTF) to be realized in Padoa will test the Neutral Beam Injection (NBI), one of the Heating and Current Drive Systems foreseen for ITER. The NBI is based on the acceleration of hydrogen or deuterium negative ions up to 1 MeV. This work has been aimed at assessing the tritium release from the NBTF in order to provide data for the safety analysis. In particular, the diffusion of the tritium through the neutral beam target material (the CuCrZr alloy calorimeter panels) has been assessed by using literature data of the diffusion coefficient. The tritium generated inside the calorimeter panels moves into both the vacuum and water side: the tritium diffusion flux has been evaluated during the beam-on (200 deg. C) and the beam-off (20 deg. C) phases of the NBTF experiments consisting of an interim campaign and a final test. The penetration depth of the tritium through the 2 mm thick CuCrZr alloy ...

International Nuclear Information System (INIS)

Proposals for use of Alloy 800 as a H.T.R. boiler material have prompted studies of its creep and high temperature fatigue properties in impure helium with comparative tests in air. In impure helium, as expected in a H.T.R., reactions of potential importance are selective oxidation (of chromium, aluminium and titanium) and possibly carburisation from carbon monoxide or methane. In air, general oxidation will occur, possibly accompanied by nitridation. The effects of these reactions will depend on specimen geometry and the nature of the deformation. Two important possibilities are: (i) that environment affects the structure and properties of a surface zone of material undegoing uniform deformation (this may modify creep rate and crack nucleation); and (ii) that environment affects behaviour of a small region (e.g. at the root of a notch or ahead of a crack) in a specimen undergoing non-uniform deformation (this will modify crack growth and hence rupture life or ...

International Nuclear Information System (INIS)

Dynamic recrystallization (DRX) is the main softening mechanism of magnesium alloy AZ31B in hot deformation. Theoretically, in the flow rule the atomic diffusibility and the driving force of dislocation migration are dependent on the temperature, and the dislocation density and the cumulation of grain boundary energy are dependent on the strain rate. The peak stress will appear when the flow driving force and resistance force reach a balance, after which the stress descending will take place due to recrystallization fraction. Since the DRX is a thermally activated process, the recrystallized volume fraction can be regarded as the function of strain through Avrami equation. Based on this idea, the paper proposes a new constitutive model characterizing dynamic recrystallization for magnesium alloy AZ31B. The model is described by a peak stress and a strain softening rate, in which the peak stress depends only on ...

Energy Technology Data Exchange (ETDEWEB)

Hydrogen storage alloy composites La{sub 0.7}Mg{sub 0.25}Zr{sub 0.05}(Ni{sub 0.85}Co{sub 0.15}){sub 3.5}(x=0,5,10) were prepared by ball milling method. Their structures, morphologies and the hydrogen storage characteristics were intensively studied in the present work. It was found that the bulk of composites maintained the hexagonal C14 Laves phase structure after ball milling with additional La-Mg-based alloy for two hours. Scanning electron microscopy (SEM) observations revealed that the average size of Ti{sub 0.9}Zr{sub 0.2}Mn{sub 1.5}Cr{sub 0.3}V{sub 0.3} and La{sub 0.7}Mg{sub 0.25}Zr{sub 0.05}(Ni{sub 0.85}Co{sub 0.15}){sub 3.5} particles were reduced to several hundred nanometers after ball milling process. Energy dispersive X-ray spectrometer (EDS) patterns of the composites showed that the La{sub 0.7}Mg{sub 0.25}Zr{sub 0.05}(Ni{sub 0.85}Co{sub 0.15}){sub 3.5} phase was uniformly distributed on the surface of Ti{sub ...

International Nuclear Information System (INIS)

Due to the well-establish corrosion problems of Alloy 600 as a steam-generator material and the subsequent focus on thermally treated (TT) Alloy 690 and Alloy 800 as alternative materials, a systematic analysis of the corrosion behavior of these two latter alloys is warranted. Corrosion test results for Alloys 690 TT and 800 were collected and organized in the form of corrosion mode diagrams. Selected data for mill annealed (MA) Alloy 600 were also included for reference. The corrosion mode diagrams correlate the modes of corrosion degradation observed in tests as functions of the environment pH and electrochemical potential (ECP). The diagrams confirm that Alloys 690TT shows some susceptibility in caustic environments, and Alloy 800 shows susceptibility in both caustic and highly acidic environments. (authors). 6 figs., ...

International Nuclear Information System (INIS)

Several metallurgical coatings have been developed that provide good tribological performances in high-temperature liquid sodium and that are relatively unaffected by neutron fluences to 6 X 10/sup 22/ n/cm/sup 2/ (E > 0.1 MeV). The coatings that have consistently provided the best tribological performance have been the nickel aluminide diffusion coatings created by the pack cementation process, chromium carbide or Tribaloy 700 trade mark (a nickel-base hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing materials applied by the electro-spark deposition process. The latter process is a relatively recent development for nuclear applications and is expected to find wide usage. Other coating processes, such as plasma-spray coating, sputtering, and chemical vapor deposition, were candidates ...

Energy Technology Data Exchange (ETDEWEB)

Safety and environmental assessments have been made of conceptual fusion power plant designs employing silicon carbide composites (SiC/SiC) as the first wall and blanket structure material. These have used similar analysis methods to earlier studies of designs based on vanadium alloy or low-activation martensitic steel, allowing direct comparisons. The very low short-term activation of silicon carbide results in an almost insignificant level of decay heat in postulated loss of coolant accidents, and a lower {gamma}-dose rate on the timescale of relevance to handling for maintenance operations. However on the longer time-scale, of interest in possible recycling operations, decommissioning and waste management, SiC/SiC appears to perform no better than vanadium alloy or low-activation martensitic steel, due in part to the activation of impurities in a realistic composition. Furthermore, its increased neutron transparency may ...

Energy Technology Data Exchange (ETDEWEB)

In order to enhance the performance of CMOS transistors, embedded epitaxial layers of Si:C can be used. In the present work, Si:C layers with Carbon contents up to 1.9 at-% and in-situ Phosphorus doping up to 4 x 10{sup 20}At/cm{sup 3} have been investigated. Due to the low solubility of Carbon in Silicon (0.0004 at.-% at the melting point), all layers considered in this work are metastable and tend to relax. Since it is crucial to the application to retain the strain of those layers, the responsible mechanisms must be understood. The relaxation during thermal treatment was studied by high resolution X-ray diffraction and was found to behave differently, depending on Carbon content and Phosphorus doping concentration. In this work, we propose a relaxation mechanism based on a kick-out reaction of substitutional Carbon which is accelerated by Phosphorus content through transient enhanced diffusion. We simulate the time evolution of layer relaxation as a function of ...

British Library Electronic Table of Contents (United Kingdom)

The nanocomposite WC-Co powders were prepared through planetary ball milling method. Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer, scanning electron microscope and mechanical property tester. The results show that VC and NbC additions can refine the WC grains, decrease the volume fraction of Co3W3C phase in ultrafine WC-10Co cemented carbides, and increase the hardness and fracture toughness of the base alloys. After sintering for 60 min at 1400 degreeC, the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5, respectively. The fracture toughness of cemented carbide WC-10Co-1NbC alloy...

International Nuclear Information System (INIS)

Alloy HT-9 is being used for both duct and cladding applications in advanced liquid-metal reactor (LMR) experiments. This tempered martensitic steel was selected for use as an LMR core component material primarily because of its excellent resistance to radiation-induced swelling. Experiments conducted in the Fast Flux Test Facility (FFTF) at 410 degree C and exposures in the range of 150 to 175 displacements per atom (dpa) have shown that Ht-9 exhibits only a 0.2 to 0.3% increase in volume. Cold-worked austenitic steels exhibit volumetric increases of 20 to 30% at 410 degree C, Alloy HT-9 is being used for a series of fuel pin experiments in the FFTF, and these tests have achieved a burnup of 175 MWd/kg metal and a fluence of 25 x 10"2"2 n/cm"2 (E > 0.1 MeV) without fuel pin breach. The high confidence placed in HT-9 is based on a wide series of in- and ex-reactor experiments. Test results for these experiments are ...

International Nuclear Information System (INIS)

The crystallography of #alpha#(hcp) precipitates formed on the #beta#(bcc) matrix grain boundaries has been studied with transmission electron microscopy (TEM) in a Ti-15V-3Cr-3Sn-3Al alloy. The #alpha# precipitates have a near-Burgers orientation relationship with respect to at least one of the adjacent #beta# grains. Among the possible 12 variants in this orientation relationship, the variant that [11 bar 20]_#alpha# is parallel to the _#beta# closest to the grain boundary plane tends to be preferred by the #alpha# precipitates. Additionally, further variant selections are made so as to minimize the deviation of orientation relationship with respect to the ''opposite'' #beta# grain from the Burgers one. Such rules in variant selection often result in the formation of precipitates with a single variant at a planar grain boundary. Prior small deformation of #beta# matrix changes the variant of #alpha# precipitates at the deformed portion of grain boundary. It is ...

International Nuclear Information System (INIS)

A tri-functional polyhedral oligomeric silsesquioxane (POSS) based silane precursor R_xR_yR_z(SiO_3_/_2)_n (x + y + z = n = 6, 8, 10, ...) bearing 3-(N-(3-triethoxysilylpropyl)ureido)propyl, isooctyl and perfluoropropyl groups was synthesized and investigated as corrosion protective coating for AA 2024 alloy. Infrared reflection-absorption (IR RA) combined with X-ray photoelectron spectroscopy and atomic force microscopy provided information about partial self-assembling of coatings having a fluorine enriched upper layer with a low surface energy (#gamma#"t"o"t = 12.37 mN/m). The structural changes that accompanied corrosion produced under chronocoulometrical conditions were assessed from ex-situ IR RA spectra. A new band at 1690-1700 cm"-"1 appeared above the corrosion potential, and was assigned to the formation of amidonium ions and consequent relaxation of urea-urea associations.

International Nuclear Information System (INIS)

Exploratory experiments of laser welding cast Ni-based superalloy K418 turbo disk and alloy steel 42CrMo shaft were conducted. Microstructure of the welded seam was characterized by optical microscopy (OM), scanning electron microscopy (SEM), X-ray diffraction (XRD), energy-dispersive spectrometer (EDS). Mechanical properties of the welded seam were evaluated by microhardness and tensile strength testing. The corresponding mechanisms were discussed in detail. Results showed that the laser-welded seam had non-equilibrium solidified microstructures consisting of FeCr_0_._2_9Ni_0_._1_6C_0_._0_6 austenite solid solution dendrites as the dominant and some fine and dispersed Ni_3Al #gamma#' phase and Laves particles as well as little amount of MC short stick or particle-like carbides distributed in the interdendritic regions. The average microhardness of the welded seam was relatively uniform and lower than that of the base metal ...

International Nuclear Information System (INIS)

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as their mixed oxides. In addition to bulk oxides, the structure and ...