International Nuclear Information System (INIS)

Zirconium-base alloys are used primarily as fuel cladding material and other core structure material in water cooled nuclear power reactors. Main research achievements and problems about corrosion of zirconium alloys are reviewed; the present theories and challenge are summarized. In the 1980s, great progress had been made towards correlating alloy composition, microstructure and irradiation with corrosion resistance. In the 1990s, main researches are focused on exploring actual mechanism of corrosion, optimizing both alloy composition and microstructure in order to minimize the fuel cycle costs through burnup optimization.

International Nuclear Information System (INIS)

The present invention concerns a method of evaluating corrosion resistance of a zirconium alloy easily and in a short period of time. An anode polarization curve of the zirconium alloy is measured to obtain an anode polarization curve expressed by logarithm. The curve is converted to a potential-current density curve expressed by absolute values. The peak area in the curve of the converted potential-current density is indicated by numerical values. Further, the corrosion resistance of the zirconium alloy is evaluated based on the peak area converted into the numerical values as a reference. This method is based on the finding that the peak area has a close relation with nodular corrosion resistance, and the corrosion resistance can be judged with respect to a specific zircaloy-2. (T.M.).

International Nuclear Information System (INIS)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. This paper describes the roles on corrosion. A corrosion test on precipitate-containing and precipitate-free materials made from pure zirconium and a small quantity of iron and chromium, rest potential measurements on an intermetallic compound of Zr(FeCr)_2 and zirconium matrix, and a galvanic coupling test of those were performed. Results showed that corrosion behavior of zirconium alloys could be attributed to the electrochemical properties of intermetallic compounds precipitated in each alloy. Namely, the cathodic and anodic polarization characteristics were associated with anodic protection provided by the ...

Energy Technology Data Exchange (ETDEWEB)

Substantial roles of precipitates such as Zr-Fe-Cr type intermetallic compounds on uniform corrosion and hydrogen pickup of zirconium alloys in pure water autoclave tests were investigated from an electrochemical point of view. In the previous paper, corrosion mechanism was elucidated by the anodic protection-precipitates degradation model. This paper describes the roles on hydrogen pickup. 633 K pure water autoclave test was performed on high purity zirconium, Zr-0.2Fe, Zr-0.2Cr, and Zr-0.1Fe-0.1Cr alloys. Hydrogen analysis after the corrosion test showed that hydrogen pickup ratio of Zr-0.2Fe alloy was about 80%. It was much higher than about 30% of pure Zr and about 10% of both Zr-0.2Cr and Zr-0.1Fe-0.1Cr alloys. Larger hydrogen content was introduced into Zr-0.2Fe alloy than the other ones by the cathodic hydrogen charging under ...

British Library Electronic Table of Contents (United Kingdom)

Zirconium and particularly Zr-2.5wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step pro...

British Library Electronic Table of Contents (United Kingdom)

The review provides a general idea about the types of metallic alloys and the pure metals used as implant materials in dental and orthopedic surgery. Their corrosive behavior in both real solutions and various media that model human biological fluids is described. Based on the literature data, it is concluded that multicomponent alloys containing titanium, niobium, zirconium, tungsten, molybdenum, aluminum, and silicon are the most resistant to corrosion. Implants made of different types of stainless steel are preferred when manufacturing orthopedic devices for short-term use.

International Nuclear Information System (INIS)

Alloys of zirconium are widely used in various core components of power reactors. Nuclear assemblies require high degree of reliability and integrity for performing in radiation and corrosive atmosphere. The hostile environments of reactor core and inaccessibility for repairs make it mandatory to select only those joining techniques which produce not only superior quality but are also amenable to NDT methods and such other techniques which ensure acceptable performance. The author has worked on various types of welding of zirconium alloys for different applications. Modern techniques in electron beam (EB) welding, resistance welding, GTAW welding and laser welding have been developed for joining Zr alloys components for different types of reactors. Many of these have been standardized and successfully used in production. Several advancements have been made in the welding ...

International Nuclear Information System (INIS)

Zircaloy fabrication plant manufactures all the necessary Zr-2 components like fuel canning tubes, calandria tubes and other rod and sheet products. This plant is having a capacity of producing about 4 lakh nos. of PHWR fuel tubes per annum. These tubes are seamless, thin walled with close dimensional tolerances and stringent mechanical properties. The plant has established all the facilities required to produce these tubes with required quality.

International Nuclear Information System (INIS)

The electrochemical behavior of some zirconium alloys including Zry-2 with various #SIGMA#Ai from 2.5 x 10"-"2"0 to 1.2 x 10"-"1"7 (h), modified Zry-2 with iron contents of 0.15, 0.25, and 0.5%, and standard Zry-4 was studied by measuring anodic polarization curves in sulfuric acid solution. The results of these electrochemical tests were compared with those of steam autoclave tests. In Zry-2, the current peak was observed at 1250 mV (versus SCE) on the anodic polarization curve, and this peak area increased with #SIGMA#Ai and with the size of secondary precipitates. Also, this peak was closely correlated with nodular corrosion resistance as expected from the above results. As iron contents in modified Zry-2 increased, the current peak at 1,250 mV decreased and a new peak at 1,900 mV appeared. The former peak disappeared and the latter peak increased further at 0.5% iron. In Zry-4, the current peak was observed at 1,900 mV, but not at 1,250 mV, ...

International Nuclear Information System (INIS)

The cold-worked Zr-2.5%Nb alloy is used as material for the pressure tubes in CANDU nuclear reactors. During the service life in reactor, diffusion of hydrogen and/or deuterium in the pressure tubes wall occur. Below a certain temperature, a stable hydride of zirconium is formed, as a brittle phase which can lead to catastrophic failures. For this reason, it is very important to be able to investigate the hydrogen effect on the micro structural properties of zirconium alloys. In the present paper a non-destructive testing technique is used, known as ultrasonic spectral analysis. When an ultrasonic signal traverses a medium, the frequency components associated with the input signal are altered. By frequency analysing the reflected signals, it is possible to study and compare the material properties. The two major parameters measured in ultrasonic spectroscopy are the attenuation and the velocity of the ...

International Nuclear Information System (INIS)

A zirconium alloy comprising from 0.8 to 1.6wt% of Sn, from 0.17 to 0.25wt% of Fe, from 0.15 to 0.25wt% of Cr and from 0.01 to 0.08wt% of Ni and Si at a concentration of 120ppm or lower as an impurity and the balance of Zr is melted into cast pieces and then subjected to an #beta# annealing. It is controlled so as to satisfy Fe + Cr + Ni #<=# 0.52wt%. Then, rolling and annealing are applied so that the total heat injection amount #SIGMA#A_i to the materials is within a range of from 1 x 10"-"1"9 to 1 x 10"-"1"7. #SIGMA#A_i = #SIGMA#t_i #centre dot# exp(-Q/RT_i), in which t_i represents processing time (hour) at an ith heat treatment step after the #beta# annealing, T_i represents a processing temperature (K) in the step i. Q represents an activating energy, R represents a gas constant, and Q/R 40,000. (I.N.).

Energy Technology Data Exchange (ETDEWEB)

The theoretical principles underlying the formation of oxide and, in particular, anodic oxide coatings on metals produced by chemical oxidation, anodizing in solutions, and anodizing in cold plasmas are reviewed. The mechanisms and conditions of anodic oxidation are described, and the structure of anodic oxide coatings on aluminum, magnesium, beryllium, zinc, cadmium, iron, cobalt, nickel, titanium, zirconium, tantalum, and chromium alloys is examined. Attention is also given to various applictins of anodized coatings. 54 references.

International Nuclear Information System (INIS)

Zirconium alloys have anisotropic mechanical properties depending on their physical orientations and are widely used as nuclear materials such as cladding tube material. An operation condition of the nuclear reactor requires a high creep resistance, because it is subjected to long period operations, high temperature and high pressure. Generally, it takes a few days or months to do the creep experiment, so it is difficult to get a data in short period. However, there is a way to predict a creep property by using the stress-relaxation in the short term. These studies realized the stress-relaxation through a compressive test of HANA-6 (Zr-1.1Nb-0.05Cu) alloy that was developed by KAERI (Korea Atomic Energy Research Institute), and then predicted the creep property

Energy Technology Data Exchange (ETDEWEB)

A theoretical model, which describes subband gap photoexcitation involving localized electronic states, was developed. The escape probability of a charge carrier trapped in a localized state is considered via Poole-Frenkel, direct tunneling, or phonon-assisted tunneling processes, as competing escape mechanisms. Photoelectrochemical experiments were performed on the passive films formed on zirconium and amorphous iron-zirconium alloys and on pure HfO/sub 2/ films and HfO/sub 2/ films implanted with varying concentrations of xenon. These films were found to possess some degree of disorder depending on the substrate, the thickness of the film, and the extent of implantation. The spectral dependence of the photocurrent in all of the films studied is considerably different from what was found for crystalline passive films. The potential dependence of the photocurrent yields Poole-Frenkel behavior. Reverse tunneling processes ...

International Nuclear Information System (INIS)

The corrosion resistance of zircaloy is affected by conditions of heat treatment in the manufacturing steps to be formed into a final product as a structural material. In the manufacturing method of the present invention, a Zr alloy controlled to contain Sn: 0.8 to 1.2wt%, Fe: 0.17 to 0.28wt%, Cr: 0.05 to 0.15wt%, Ni: 0.04 to 0.10wt%, Nb: 0.01 to 0.09wt%, oxygen: 1,000 to 1,500ppm and Si, an Si impurity at a concentration of 120ppm or less and balance of Zr is melted into a cast piece, to which #beta# hardening is applied. Then, rolling and annealing treatment are applied so that the total heat input amount to the material: #SIGMA#Ai ranges from 1 x 10"-"1"9 to 1 x 10"-"1"7. With such procedures, a Zr alloy structural material for a reactor core having excellent homogeneous corrosion resistance and hydrogen absorption resistance for a long period of time while having a sufficient strength can be obtained even in a case where Sn content is ...

Energy Technology Data Exchange (ETDEWEB)

The desire to increase uranium utilization and to minimize spent fuel storage requirements provides an incentive to extend the average fuel rod discharge burnup to about 70,000MWd/MTU. For these higher burnups data are needed to determine if waterside corrosion of the cladding may be a life-limiting feature of fuel rod design. It is apparent that many factors can influence waterside corrosion, and these need to be better understood in order to minimize corrosion at these higher target burnups. The objective of this report is to review published data relevant to the corrosion of Zircaloy under PWR operating conditions. (author). 100 refs., 4 tabs., 21 figs.

J-STORE (Japan)

Full Text Available

International Nuclear Information System (INIS)

During 17 years since the start of operation of the first commercial LWR in Japan, many LWRs have experienced various corrosion damages, but the causes of them were clarified, and the counter-measures were executed effectively in actual plants, as the results, the cause of corrosion damage decreased remarkably, and now, the high rate of operation has become to be maintained. In this paper, the major cases of corrosion damage experienced in LWRs in Japan and foreign countries, the causes of them and the countermeasures, the problems of hereafter and so on are described. The corrosion damage of metallic materials in the environment of LWRs occurs in the parts in contact with high temperature, high pressure water and steam, such as stainless steel piping in the primary cooling system of BWRs, and nickel alloy heating tubes of steam generators, carbon steel feed water piping and zirconium alloy fuel cladding tubes in PWRs. ...

International Nuclear Information System (INIS)

Alloying elements such as Fe and Cr are generally considered to be effective even in small quantities for corrosion resistance of Zircaloy-4. The maximum total solubility of Fe + Cr in a Zr-Sn matrix has been reported to be very low. Therefore, most of these elements are observed in the form of ternary Zr-Fe-Cr-type precipitates. To clarify the effects of precipitates on corrosion property, Zr-1.3 Sn-(Fe,Cr) alloys containing Fe + Cr from 45 up to 180 ppm (the Fe to Cr ratio is about 2) were melted from pure zirconium (X-bar Zr and EB-Zr) and pure alloying elements. They were subjected to corrosion testing in 633 K water and microstructural analysis. It was found that precipitate-free materials showed much larger weight gains than precipitate-containing materials even at the same alloy compositions. Subsequently, a corrosion test on the precipitate-free material galvanically coupled ...

Energy Technology Data Exchange (ETDEWEB)

Total hemispherical emittance was measured for the SP-100 reactor fuel cladding alloy (Nb-l% Zr). Based on a standard test method (ASTM C 835-82), experiments were conducted on a reference sample of oxidized stainless steel and then on a sample of actual cladding. The sample is heated in a vacuum by passing DC current through it until reaching equilibrium. Measurements are made of the electrical power dissipated in the sample and of the surface temperature. Using the Stefan-Boltzmann Law and some key assumptions concerning conductive and radiative heat transfer, the measured quantities are used to calculate emittance. Calculated values for unoxidized cladding range from 0.159 +/- 5.35% at 913 K to 0.200 +/- 4.51% at 1091 K. Highest value measured after onset of visible oxidation was 0.339 +/- 3.92% at 1269 K.... SP-100, Reactor, Emittance, Niobium, Fuel cladding, Emissivity.

International Nuclear Information System (INIS)

Zirconium phosphate was one of the earliest inorganic ion-exchange suggested for removing strontium and cesium from aqueous nuclear waste. This paper studied ionic exchange to remove Cs-137 and Sr-90 by using different cationic of zirconium phosphate. In this case the parameters studied were the effect of temperature and ion concentration to percent up take and distribution coefficients. It is also conducted the study on column experiments to determine the breakthrough curves for Cs-137 and Sr-90. The result showed the potential of use of zirconium phosphate in radioactive waste treatment. (author)

International Nuclear Information System (INIS)

Zirconium is a transition element located along with sister elements titanium and hafnium in Group IVB of the periodic table. It is grayish white metal, with a density somewhat less than carbon steel. Zirconium is the ninth most common metallic element in the earth's crust, and is more abundant than zinc, lead, nickel, or even copper. Zirconium is exceptionally resistant to corrosion by many common acids and alkalis. It is resistant to most organic acids, such as formic, acetic, lactic, and oxalic acids. It also has a high resistance to localized forms of corrosion, such as pitting, crevice corrosion, and stress corrosion cracking. Its corrosion resistance is caused by the formation of a dense, tenaciously adherent, chemically inert oxide film on the surface. This oxide film protects the base metal from both chemical and mechanical attack at temperatures up to about 400 C (750 F). This article describes ...

International Nuclear Information System (INIS)

Zircaloy-2 and Zircaloy-4 tubing materials were irradiated with 1 MeV proton at 350 degrees C to doses of 0.01, 0.1, and 1 dpa respectively. Both microstructure examination and nodular corrosion test (500 degrees C, 1500 psi steam) were performed in order to understand the relationship between the microstructural evolution and the corrosion resistance of these alloys under irradiation. Neutron-irradiated Zircaloy-2 specimens which were obtained from a failed BWR fuel rod cladding were also studied. Specimens of three different neutron fluences were investigated; namely, 2.6x10"2"4, 3.2x10"2"5, 3.8x10"2"5, (E_n#>=#1MeV). The results indicated that the higher the irradiation dose the better the nodular corrosion resistance of both Zircaloy-2 and Zircaloy-4. It is concluded that irradiation-induced precipitate dissolution and irradiation-enhanced diffusion may increase the solute concentration in the matrix and make it distributed more evenly which in turn ...

Energy Technology Data Exchange (ETDEWEB)

The initiation and inhibition of pitting corrosion on zirconium and hafnium in aqueous solutions have been investigated by potentiodynamic, potentiostatic and galvanostatic measurements at 25/sup 0/C. Effects of Cl/sup -/, Br/sup -/and I/sup -/ have been examined over a range of salt concentrations and pH. All three halide ions cause pitting attack on the two metals, but this may be inhibited by other anions. The results show that hafnium is more easily protected against pitting than is zirconium. The data are treated by the Butler-Volmer equation to yield more information about the mechanisms of the pitting corrosion.

International Nuclear Information System (INIS)

Using the PMR method the interaction of zirconium and hafnium tetrachlorides with tri.tet.butylphenyl ester of 1,2- naphthoquinonediazide (2)-5-sulfonic acid is studied. The formation of MCl_4xNQD complexes is established, the equilibrium constants and thermodynamic parameters of complexing reaction are determined. The presence of rapid ligand exchange, proceeding according to associative mechanism, is detected. The rate constants and activation energies of the exchange reaction are calculated.

International Nuclear Information System (INIS)

Technology of plasma sputtering, structure and properties of zirconium dioxide coatings were studied. Necessity of void number increase to enhance coating heat-resistance is shown. Optimal powder particle size (20-60 #mu#m) providing optimal coating porosity was determined. Weight part of stabilizating oxide (Y_2O_3) in ZrO_2 for formation in coating of microcracks serving as barriers for macro-cracks propagation was determined.

Energy Technology Data Exchange (ETDEWEB)

An energy dispersive x-ray fluorescence technique was used for the determination of Titanium (Ti) and Zirconium (Zr) in red mud by using a standard addition method. An annular {sup 241}Am source is employed for excitation of K shells of elements. 13 refs., 2 figs., 1 tab.

UK PubMed Central (United Kingdom)

The management of the interim phase of a complete oral rehabilitation in patients with severely worn dentition is often challenging due to the loss of occlusal vertical dimension, loss of tooth structure,...Full Text Available

Science.gov (United States)

The corrosion behavior of Ta, Ti, and Zr in inorganic acids, bases, chlorides and miscellaneous salts, waters and gases, and organic acids and miscellaneous organic chemicals is summarized. (W.L.H)

International Science & Technology Center (ISTC)

The New Titanium Alloys With Increased Mechanical Properties and Corrosion Resistance for Medical Instruments and their Coatings

CERN Document Server

Metals and alloy - Atmospheric corrosion testing

International Nuclear Information System (INIS)

The "6"2Zn-"6"2Cu generator system is one of the few which yield a pure positron emitting daughter. The authors have developed a method for the preparation of this generator system following 32 MeV #alpha# particle bombardment of nickel targets. The chemical processing involves two stages: first a hydrous zirconium oxide column is used at pH 4-5 to separate the zinc and copper activities produced in the target nickel, and secondly, a conventional anion exchange column is used to retain the "6"2Zn and remove all copper activities in 2M HCl. This column serves as the "6"2Cu generator which will yield pure "6"2Cu repeatedly, free from "6"2Zn and other impurities, in a mixture of HCl and NaCl. A method is outlined also to obtain a solution of "6"2Zn using the hydrous zirconium oxide (HZO) column. "6"1Cu can be prepared as a by-product in the above procedure, but a method for the preparation of "6"1Cu alone using an 18 MeV #alpha# particle beam on a ...

International Nuclear Information System (INIS)

... base alloys alloys beams chemical reactions elements hardness irradiation

International Nuclear Information System (INIS)

German (Dec 1973). Germany Carlen, JC Blom, U. Sandvik Steel Works,

International Nuclear Information System (INIS)

Observations concerned with the formation of isothermal #omega# in the beta-titanium alloy RMI (38-6-44) are presented as part of a more general study of the aging characteristics of the alloy.

International Nuclear Information System (INIS)

There are reported the results of corrosion resistance investigation of aluminium bronzes, containing about 8 and 10% of aluminium and modifying quantities of zirconium. The tests of corrosion resistance were carried out in synthetic seawater, in 3% NaCl aqueous solution and in 10% H_2SO_4 aqueous solution, with reference to industrial bronze BA93 (CuAl9Fe3). The bronzes were tested in an annealed, hardened, tempered state and after plastic hot working. The conclusion is that corrosion resistance of aluminium bronzes, especially against selective corrosion, depends more on material structure, resulted form heat treatment, than on chemical composition. (author). 6 refs, 8 figs, 6 tabs.

Energy Technology Data Exchange (ETDEWEB)

The aims of the present work were to investigate possible compatibility between sodium zirconium phosphate (NZP) and Synroc titanate phases, to prepare NZP-based waste forms by hot-pressing rather than sintering, and to investigate the incorporation in NZP of (a) Cs/Sr as simulated heat-generating nuclides; (b) simulated actinides; and (c) simulated Purex waste. The NZP samples were prepared by methods similar to those used for Synroc. The precursor NZP phase was formed from tetrabutyl zirconate Zr(OC{sub 4}H{sub 9}){sub 4}, sodium nitrate, and 85% orthophosphoric acid. Simulated waste nitrate solutions were then mixed with the liquid precursor. After stir drying of the precursor, calcination was carried out at 700{degree}C to remove nitrates and organics.

Energy Technology Data Exchange (ETDEWEB)

NO abstract prepared.

CERN Document Server

Metals and alloys : atmospheric corrosion testing : General requirements for field tests

Science.gov (United States)

... Title : Effect of Yttrium on the Microstructure of Titanium Alloys,. ... The yttrium was added in the melting stage as an oxide or in the elemental form. ...

International Nuclear Information System (INIS)

The importance that must be attached to the phenomenon of stress corrosion cracking of austenitic alloys is emphasized. The relation between chemical composition of various alloys and their sensitivity to cracking is shown with particular reference to the behaviour of Alloy 800. The different effects of alkaline anc chloride environments are discussed. Studies are reported of the general corrosion of Alloy 800 and other alloys in an environment representative of the primary coolant of PWR reactors; and of the behaviour of various alloys (including Alloy 800) in the conditions envisaged for their use for steam generators with superheat up to about 550 deg.C. (U.K.).

International Nuclear Information System (INIS)

This paper reviews the mill flowsheet applied at the SOMAIR (Societe des Mines de l'Air) uranium mill in Niger. It focuses on the yellow cake quality improvements achieved by molybdenum and zirconium elimination through double yellow cake precipitation in tanks at first stage and through size/density control in a fluidized bed precipitator at second stage. Water saving aspects in the plant are also presented. (author)

Energy Technology Data Exchange (ETDEWEB)

The evaluated data testing for Si, Zr, Nb and Fe materials has been performed through the analyses of the neutron leakage spectrum from spherical assemblies measured in integral benchmark experiments with (d,t) and Cf fission neutron sources. Intercomparisons of the calculated from BROND-2, ENDF/B-6 and JENDL-3 data files with experimental results are presented.

International Nuclear Information System (INIS)

Due to the well-establish corrosion problems of Alloy 600 as a steam-generator material and the subsequent focus on thermally treated (TT) Alloy 690 and Alloy 800 as alternative materials, a systematic analysis of the corrosion behavior of these two latter alloys is warranted. Corrosion test results for Alloys 690 TT and 800 were collected and organized in the form of corrosion mode diagrams. Selected data for mill annealed (MA) Alloy 600 were also included for reference. The corrosion mode diagrams correlate the modes of corrosion degradation observed in tests as functions of the environment pH and electrochemical potential (ECP). The diagrams confirm that Alloys 690TT shows some susceptibility in caustic environments, and Alloy 800 shows susceptibility in both caustic and highly acidic environments. (authors). 6 figs., ...

International Nuclear Information System (INIS)

Consideration is given to the process of the formation of a titanium sponge alloyed with niobium or tantalum, in the joint metallic reduction of titanium, niobium and tantanum chlorides. A percentage composition of the phases observed and the structure of the alloyed sponge have been studied. It is shown that after one remelting operation of the alloyed sponge the alloys of titanium with niobium and tantalum have a uniform component distribution. At the stage of chloride reduction there appear solid solutions based on titanium and an alloying component. The stage of vacuum separation of the reaction mass is associated with a mutual dissolution of the primary phases and the formation of the solid solutions of the alloyed titanium sponge, which, by their composition, are close to the desired alloy composition. The principal features of the ...

International Nuclear Information System (INIS)

The following methods of quartz ceramics alloying were considered: alloying of initial quartz glass; introduction of alloying additive into water slip of quartz glass; porous materials impregnation with salt aqueous solutions and subsequent salt thermal decomposition with formation of stable oxides in pores of ceramics. Oxygen free compounds BN, SiB_4, SiC, Si_3N_4, REM oxides and transition metal oxides were used as alloying additives. Main properties of the materials and compositions obtained are presented.

Energy Technology Data Exchange (ETDEWEB)

The processing characteristics, tensile properties, and oxidation response of two Nb-Ti-Al-Cr alloys were investigated. One creep tests at 650{degrees}C and 172 MPa was conducted on the base alloy which contained 40Nb-40-Ti-10Al-10Cr. A second alloy was modified with 0.11 at. % carbon and 0.07 at. % yttrium. Alloys were arc melted in a chamber backfilled with argon, drop cast into a water-cooled copper mold, and cold rolled to obtain a 0.8-mm sheet. The sheet was annealed at 1100{degrees}C for 0.5 h. Longitudinal tensile specimens and oxidation specimens were obtained for both the base alloy and the modified alloy. Tensile properties were obtained for the base alloy at room temperature, 400, 600, 700, 800, 900, and 1000{degrees}C, and for the modified alloy at room temperature, 400, 600, 700, and 800{degrees}C. Oxidation ...

International Nuclear Information System (INIS)

Investigated are the characteristics of high-temperature plastic deformation the velocity sensitivity of flow stresses, deformation curves, flow stresses, deformation before rupture - as well as the structure of beryllium alloys containing nickel (0.5-4 %), yttrium (0.5-2 %) and aluminium (38 %). The alloys containing nickel (2%) and yttrium (0.5 %) are superplastic, however, deformation before fracture of the alloys is lower than that of the unalloyed beryllium. The singularities of high-temperature plastic flow of the alloys and the causes of deterioration of their plasticity are determined.

Energy Technology Data Exchange (ETDEWEB)

Since 1991, secondary side cracking has become a major concern in EDF steam generators. At 350 C, IGSCC of Alloy 600 was found in pure NaOH solutions from 4 to 500 g/l, with a maximum at 100 g/l. From the present results and available data, IGSCC of Alloy 690 occurred in pure NaOH solutions from 40 to 500 g/l, but the greatest sensitivity was observed at 100 g/l. TG/IGSCC of Alloy 800 became more severe with increasing NaOH solutions, from 10 to 500 g/l. On the whole, the ranking for SCC-resistance was Alloy 600 < Alloy 800 < Alloy 690. A significant improvement was still obtained with 690TT with intergranular carbides (industrial tubes) and perhaps with Alloy 800 NG (nuclear grade), but both alloys cracked at the highest stresses. IGSCC susceptibility of Alloy 600 MA was higher for the tubes ...

International Nuclear Information System (INIS)

Three model boilers, manufactured to simulate full-size tube sheet crevices, were tested with various secondary side environments. The first was faulted with organics representative of the decomposition of humic acid. The second was faulted with sodium carbonate and sodium hydroxide, while the third was faulted with sodium sulfate and sodium hydroxide. Each model contained seven tubes, which included Alloy 600 in the mill-annealed (MA) and thermally-treated (TT) conditions and Alloy 690 in the thermally-treated condition. Two models contained Alloy 800 tubes in the mill-annealed condition and one had Alloy 800 in the mill-annealed/cold-worked/glass-bead-peened condition. Two different sizes of tubesheet crevices were used in all model boilers. In the organics-faulted boiler, tubes of Alloy 600MA, Alloy 690TT and Alloy 800MA experienced no ...

Energy Technology Data Exchange (ETDEWEB)

Theoretical assessment on the chromatographic {sup 99m}Tc generator preparation using (n, {gamma}) {sup 99}Mo produced ex-natural molybdenum was carried out. The relationship between the neutron flux for MoO{sub 3} target activation, Mo-content or Mo adsorption capacity of column packing material, {sup 99m}Tc pertechnetate concentration and/or {sup 99m}Tc radioactivity of eluate was established. The reasonably lower limit of neutron flux of reactor and Molybdenum content of column packing material were found out to estimate the production of portable chromatographic generators available for nuclear medicine application. The concentration of {sup 99m}Tc pertechnetate eluate of low {sup 99m}Tc concentration using the column elution technique was also evaluate theoretically and conducted successfully in practice. Three options of {sup 99m}Tc generator using Titanium-Molybdate, Zirconium-Molybdate and Zirconium Oxide as generator column-packing ...

International Nuclear Information System (INIS)

Reaction of formation of 3, 5, 7, 3', 4', 5' - hexaoxiflavone - myricetin complexes with zirconium and hafnium ions has been the basis for development of luminescent method of determining these elements. Optimum conditions for complexing have been determined. For Hf they are : 8-9 HCl concentration, maximum fluorescence wave length (lambda fl.)of 520 nm, wave length of exciting light (lambda el) of 436 nm, for Zr lambda fl = 536nm, lambda el = 436 nm. Stable fluorescence establishes after 25 min. for Zr and after 15 min for Hf in the presence of 40% ethanol. Usage of various camouflage agents has permitted to attain high selectivity of the method. Possibility for determination of Zr with myricetin in the presence of a 10-time excess of Hf, Cr, Cu, 50-time excess of Mo and Ti is shown. Sensitivity of Zr determination is 2.0x10 #mu#g"-"2/ml, for Hf it is 9.0x10 #mu#g"-"3 and mineral waters.

Energy Technology Data Exchange (ETDEWEB)

Laser surface alloying with gaseous nitrogen was utilized to improve the wear resistance of a Ti-6Al-4V alloy. Wear-resistant composite coatings reinforced by hard TiN dendrites were produced 'in-situ' on a substrate of a Ti-6Al-4V alloy. The hardness and wear resistance of the laser alloyed coating under two-body abrasive and block-on-ring full-sliding wear conditions were significantly enhanced. (orig.)

International Nuclear Information System (INIS)

Corrosion testings of model alloys, corresponding by chemical composition to simple and complex-alloyed #gamma#- and #gamma#'-phases of nickel heat-resistant alloys are conducted in sodium sulfate and chloride melts. It is ascertained that heat resistant nickel alloys containing over 50 % of hardening #gamma#'-phase, are subject to disastrous sulfide corrosion (SC). Resistance against SC alloys containing below 50 % of #gamma#'-phase is determined by the resistance of #gamma#-solid solution. 10 refs., 3 figs., 2 tabs.

International Nuclear Information System (INIS)

The method of programmed thermodesorption has been used to study the forms of hydrogen adsorption in ZrNiHsub(x) hydride. It is shown that high concentration of the hydrogen, which extracted from hydride in the temperature range of 240-260 deg C results in appearance of ''reverse'' peak. Charge of hydride adsorption properties during its oxidation-reduction treatment is studied. Comparison with spectra of hydrogen thermodesorption from the surface of Ni/ZrO_2 deposited catalyst and zirconium oxide is carried out.

International Nuclear Information System (INIS)

Instrumental neutron activation analysis is used for simultaneously determination of macrocomponents in ferroelectric materials LLZT. Pb, Zr, Ti have been determined by "2"0"3Pb, "8"9Zr and "4"8Sc nuclides created by fast neutron (14.5 MeV) activation. Application of paraffine as neutron moderator and reflector allows to simultaneously determine lanthanum by "1"4"0La nuclide. It has been shown that zirconium, titanium and lanthanum can be determined with the accuracy of #+-#0.1 mas. % and lead - #+-#0.7 mas. %.

Science.gov (United States)

... Accession Number : ADD151811. Title : Ultra High Strength Beta Titanium Alloy for Fasteners. Descriptive Note : Journal article,. ...

Science.gov (United States)

... Accession Number : ADD109273. Title : THERMAL STABILITY OF ALPHA-BETA TITANIUM ALLOY Ti-5Al-2Cr-1Fe,. Corporate Author : ...

Science.gov (United States)

... by the boron doping in most of the alloys except for Al66Mn9Zr25 + 50 ppm B alloy; permanent deformation at ultimate compressive strength is not ...

International Nuclear Information System (INIS)

The nickel-rich superalloys Alloy 600 and Alloy 800 have been corroded in mildly alkaline deuterated aqueous conditions typical of secondary coolant circuits in a nuclear power station. The oxide films and substrates of these alloys have been analysed by imaging SIMS depth profiling, which makes it possible to describe elemental distribution in all three dimensions. The measurement of the distribution of the secondary ions NiO"-, FeO"- and CrO"- appears useful for detailing the behaviour of nickel, iron and chromium within oxidized phases. The measurement of D"- distribution outlines the extent of oxide hydration. For Alloy 800, evidence of sodium migration into the grain boundaries of the alloy substrate is found. For Alloy 600, no grain boundary sodium ingress can be identified under comparable corrosion conditions. (author).

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

International Nuclear Information System (INIS)

The effect of various hydrogen concentrations on the crystal lattice period and the hardness of titanium alloy was examined, the alloy containing about 16 at.% Mo (27.5 wt. % Mo) and having #beta# structure. The peculiar features of the mechanism of plastic deformation of the alloy were studied after adding hydrogen to it. A dependence of the crystal lattice period on the concentration of hydrogen was obtained for TixMoxH_2 alloy. It has been established that the hardness of the Ti-Mo alloy does not change when hydrogen is added to it. The presence of hydrogen introduces changes into the mechanism of deformation of #beta#-titanium alloy. The configuration of the inverse pole figures after rolling proves that the transverse slip process in an alloy with hydrogen is hampered, and that the coplanar slip process is developing in it.

Science.gov (United States)

... CLOSURE DURING HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY (PREPRINT) ... HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY ...

Science.gov (United States)

... Accession Number : ADD336001. Title : Development of a FeCoNb Alloy to be used in Eddy Current Probes for Testing Ferromagnetic Tubes,. ...

Science.gov (United States)

... Title : DUCTILITY RATIO OF AGED BETA TITANIUM ALLOY. Corporate Author : NEW YORK UNIV NY SCHOOL OF ENGINEERING AND SCIENCE. ...

International Nuclear Information System (INIS)

Stemming from their unique combination of elevated strength, low density, and good overall corrosion resistance, beta titanium alloys have become attractive candidate materials for critical, high-stress, components in corrosive services. An overview of the comparative corrosion resistance of beta alloys to conventional alpha and alpha/beta titanium alloys in common industrial and aerospace service environments generally reveals attractive behavior depending on the environment and alloy composition and, in some cases, alloy condition. Expanded performance windows are especially noted for the molybdenum-rich beta alloys, particularly in regard to resisting reducing acids, stress corrosion, and high temperature localized chloride attack, along with hydrogen and oxidation resistance. Where applicable, implications of this enhanced corrosion performance on current ...

International Nuclear Information System (INIS)

Basic studies of the oxidation resistance of Fe-Cr binary and Fe-Cr-Ni ternary alloys in pure oxygen have shown that the excellent corrosion resistance of Alloy 800 is explicable in terms of the low defect concentrations and diffusion rates in the oxide forming on alloys of this composition in sufficiently oxidising environments. The performance of Alloy 800 in environments of particular importance to nuclear power generation is briefly reviewed to determine to what extent ideas derived from the basic studies of Fe-Cr-Ni ternary alloys are borne out in practice. The good corrosion resistance of Alloy 800 in steam and CO_2 and, to some extent, in molten salt environments is in agreement with the behaviour of ternary alloys in oxygen. Minor aliovalent alloying additions are only expected to have a significant effect on the ...

International Nuclear Information System (INIS)

At 650"0C, the low-cycle fatigue life was essentially the same for the two alloys on the basis of strain amplitude, but Alloy 800H had a longer life on the basis of stress amplitude. A 500"0C, Alloy 800 and 800H exhibited longer fatigue lifetime than at 650"0C, with Alloy 800 exhibiting a 2-3 times longer life than Alloy 800H when compared on the basis of plastic strain range, whereas the difference was less pronounced when compared on the basis of stress amplitude. When a creep effect was introduced either by way of a hold time or a reduced frequency, Alloy 800 exhibited a greater reduction in life than did Alloy 800H. The dislocation structure changed from planar to cellular with increase in strain range, and extensive precipitation of M_2_3C_6 was noted within the grains for Alloy 800H and along grain boundaries for ...

Energy Technology Data Exchange (ETDEWEB)

To clarify the acidic and alkaline Intergranular Stress Corrosion Cracking (IGSCC) mechanism of thermally treated alloy 690 (alloy 690 TT) and shot peened alloy 800 (alloy 800 SP), C-ring tests were conducted in deaerated HCl solutions and in deaerated NaOH solutions at 350degC, compared with the acidic and the alkaline IGSCC susceptibilities of mill-annealed alloy 600 (alloy 600 MA), full-sensitized one (alloy 600 FS) and thermally treated one (alloy 600 TT). Grain boundary characteristics, such as chromium depleted zone and chromium carbide precipitation, were examined using modified Huey test and Transmission Electron Microscopy. Potential-pH diagram for Ni, Cr, Fe-H{sub 2}O system at 350degC was constructed and the solubilities of NiO, Cr{sub 2}O{sub 3} and Fe{sub 3}O{sub 4} were also calculated to evaluate the ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The investigations carried out on Alloy 800 in aqueous high-temperature environments in France as well as in other countries are reviewed. These studies are mainly concerned with nuclear industry where Alloy 800 can be used as structural material for steam generators of PWR, breeders or HTR. As results referred to in the literature on cracking in caustic environmens do not always agree, a discussion is presented on the matter. The behaviour of Alloy 800 in superheated steam is examined. (Auth.).

International Nuclear Information System (INIS)

(Nov 1973). United States Greenfield, MA Pierce, CM Chicago, IL.

KoreaScience (Korea)

Full Text Available

International Science & Technology Center (ISTC)

Investigation of Destruction Mechanisms in Reactor Steels and Alloys under Cycling Deformation

Energy Technology Data Exchange (ETDEWEB)

Short communication. 6 refs., 2 figs.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

In the present work, electrochemical measurements and corrosion tests in NaCl solutions were carried out to study the effect of aging treatments on pitting corrosion behavior in a 8090 alloy and its high purity Al-Li binary alloy analogue. The pitting corrosion characteristics and corrosion resistance of the 8090 alloy have been determined in relation to precipitation microstructures. (orig.).

Science.gov (United States)

... THE STRENGTH, TOUGHNESS, AND STRESS-CORROSION CRACKING SUSCEPTIBILITY OF A METASTABLE BETA TITANIUM ALLOY (Ti-11. ...

Energy Technology Data Exchange (ETDEWEB)

Simulated atmospheric corrosion studies were performed to determine the corrosion protection provided by galvanized zinc coatings on depleted uranium, U-0.75 Ti alloy, and U-6 Nb alloys. The accelerated ASTM tests consisted of exposing the galvanized samples to aqueous and aqueous chloride environments. The test results showed that anodic protection was provided by the electronegative zinc coatings on uranium and uranium alloys. Treating zinc with chromate conversion coatings also provided more protection.

International Nuclear Information System (INIS)

A new high strength titanium alloy has been developed primarily intended for fastener applications. While Ti-6Al-4V is used extensively as a fastener alloy in the aerospace industry, its shear strength allowable is limited to 655 MPa (95 ksi). For higher shear strength requirements, various steels or nickel-based alloys are used (up to 860 MPa (125 ksi)), but with the attendant density penalty. This new alloy is intended to provide the 860 MPa shear strength at roughly a 40% weight savings. After screening various alloy systems, the optimum chemistry has been selected as follows: Ti-6.0V-6.2Mo-5.7Fe-3Al. In light of its 125 ksi shear strength goal, the alloy has been designated TIMETAL reg-sign 125.

International Nuclear Information System (INIS)

In order to substitute expensive cast titanium alloys by powder ones the possibility of introduction of powder additions by mechanical stock mixing is studied. It is shown that microstructure of powder alloys of Ti-Zr(1-9%) system is typical for one-phase cast #alpha#-alloys. The Ti-Mo(1-9%) and Ti-Nb(1-9%) system alloys have microstructure typical for two-phase (#alpha#+#beta#)-alloys. For homogeneous structure to be obtained the high temprature annealing is advisable after hot pressing. Alloying with Mo, Zr and Nb permits to increase considerable the strength of powder titanium products (at 9% Mo more than two times).

Energy Technology Data Exchange (ETDEWEB)

In this book over 250 alloys are organized by AISI number into 10 major sections: Irons, Carbon Steels, Alloy Steels, Low Alloy Constructional Steels, Ultra High Strength Steels, Tool Steels, Maraging Steels, Wrought Stainless Steels, Heat Resistnat Casting Alloys, and Iron Based Rought Superalloys. Each alloy record lists the designation, specifications, UNS number, composition, product forms and a comment on the high-temperature properties and applications. Referenced data is then given for physical properties such as density, specific heat, thermal conductivity, thermal expansion, electrical conductivity, Poisson's ratio, moduli of elasticity and rigidity, etc. Mechanical properties follow, and include tensile properties, shearing and bearing properties, impact properties, creep, stress rupture and stress relaxation and fatigue properties. The last part of the ...

Energy Technology Data Exchange (ETDEWEB)

Magnesium alloys show a high specific strength and are therefore increasingly used for light-weight constructions in transportation industry.{sup [1,2]} To predict the behaviour of the material under the influence of cyclic loading it is vital to understand the fatigue behaviour of magnesium alloys. Only when understood properly, it is possible to fully apply the potential weight reduction by using magnesium alloys. A very important aspect in fatigue of magnesium alloys is the influence of a corrosive media and elevated temperatures, of which both are relevant in automotive applications. These two factors tend to have deleterious effects on magnesium alloys and therefore also have to be considered in investigations on the fatigue behaviour of magnesium alloys. (Abstract Copyright [2004], Wiley Periodicals, Inc.)

International Nuclear Information System (INIS)

The threshold stress intensities for stress corrosion crack propagation in beta titanium alloy 38-6-44, Ti3Al-8V-6Cr-4Mo-4Zr, has been determined in salt water and methanolic solutions. The alloy was immune to stress corrosion cracking (SCC) in aqueous sodium chloride solutions (marine atmosphere). However, in methanolic solutions, the alloy was very susceptible to SCC. This marked susceptibility in methanolic solutions can be mitigated by the addition of an inhibitor: sodium nitrate. Crack extension in the alloy was transgranular and failure occurred by brittle quasi-cleavage in methanolic solutions.

International Nuclear Information System (INIS)

By the methods of microstructural and electron-microscopic analyses by the tension test and impact test studied is the effect of quenching conditions on structure and mechanical properties of the TS6 titanium-#beta# alloy. It is shown that low temperature quenching from 700 deg C, recommended earlier for analogous VT15 titanium alloy, leads to appearence of intercrystalline fracture and to sharp decrease of impact strength of the TS6 alloy. Established are optimum conditions for quenching of half-finished products and articles of the TS6 alloy depending on their subsequent working or operation.

International Nuclear Information System (INIS)

Cr_2O_3 scales are found to form on Alloy 800 and a similar pure ternary alloy in air, and 1 and 50 atm. helium containing oxidizing impurities typical of those in an SGHTR. The strong temperature dependence and neglibible helium overpressure dependence indicate that gas transport through the scales is not rate controlling. Surface oxidation rates are therefore controlled by solid state diffusion and the low oxygen partial pressure dependence of the oxidation rate in Alloy 800 is ascribed to the presence of extrinsic defects in the Cr_3O_3 (due to doping by alloying elements) or to the presence of short circuit diffusion paths. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

The time-temperature-precipitation diagrams and the resulting time-temperature-sensitization diagrams have been established and are presented for today's current nickel-chromium-molybdenum alloys C-4, C-276, 22 and the recently developed alloy 59. Compared to those materials alloy 625 behaves differently due to its high niobium content. In addition, also the precipitation and sensitization of alloy G-3 has been established. Under the materials considered alloy C-276 has the strongest tendency to precipitate the intermetallics Mu and P together with the carbide M{sub 6}C at intermediate temperatures, followed by the alloys 22 and 59. The tendency to sensitization in the sense of the 50{mu}m (2 mils) intercrystalline penetration criterion when exposed to the ASTM G-28, method A test solution is greatest with alloy C-276, and decreases ...

Energy Technology Data Exchange (ETDEWEB)

In order to investigate the role of amorphous SiO{sub 2} particles in corrosion and wear resistance of Ni-based metal matrix composite alloying layer, the amorphous nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer has been prepared by double glow plasma alloying on AISI 316L stainless steel surface, where Ni/amorphous nano-SiO{sub 2} was firstly predeposited by brush plating. The composition and microstructure of the nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer were analyzed by using SEM, TEM and XRD. The results indicated that the composite alloying layer consisted of {gamma}-phase and amorphous nano-SiO{sub 2} particles, and under alloying temperature (1000 deg. C) condition, the nano-SiO{sub 2} particles were uniformly distributed in the alloying layer and still kept the amorphous structure. ...

Energy Technology Data Exchange (ETDEWEB)

In our continued efforts for improving the performance of zinc anodes for a Zn/air battery, we now report the preparation of three alloys and improved performances of anodes made up with these alloys. The alloys contained zinc, nickel, and indium with different weight percentages and were calcined at two different temperatures. Out of the six alloys, the alloy which has a composition of zinc 90%, nickel 7.5% and Indium 2.5% and fired at 500{sup o}C is found to be the best. In the case of the hydrogen evolution reaction, this alloy had its potential shifted to a more negative potential. As far as the cyclic voltammograms were concerned, the difference between the anodic and cathodic part was minimal when compared with other alloys. Surprisingly, this alloy had reversibility even after 100 cycles of the cyclic ...

Energy Technology Data Exchange (ETDEWEB)

A series of cyclic strain controlled tests have been carried out at 600/sup 0/C on three high temperature austenitic iron-based alloys, AISI type 316 stainless steel, Alloy 800 H and Sandvik 253 MA. The tests were carried out under constant total strain control using a constant strain rate of 0.005 s/sup -1/. By considering the changes in modulus throughout the life of each specimen it was found that damage evolution could be successfully predicted as a function of plastic strain range despite the fact that each alloy had been chosen because of a different stress response at 600/sup 0/C. Although each alloy accumulated fatigue damage in a similar manner the longer lives of Sandvik 253 MA and Alloy 800 H at a given total strain range were due to a smaller plastic strain component and a reduced stage I crack propagation rate. In the 253 MA alloy, slip was ...

Energy Technology Data Exchange (ETDEWEB)

Papers are presented on the development of oxidation- and sulfidation-resistant ferritic alloys; the microstructural stability of sulfidation-resistant FeCrAl stainless steels around 500 C; age hardening in Fe-Mn-Al-C austenitic alloys; the oxidation/corrosion behavior of low-Cr Fe-Cr-Ni alloys containing Zr or Nb; the high temperature oxidation/corrosion of iron-based superalloys; and the role of Mo in the Na/sub 2/SO/sub 4/ induced corrosion of superalloys at high temperature. Topics discussed include the effect of variations of Co content on the cyclic oxidation resistance of selected Ni-base superalloys; high temperature oxidation of Fe based alloys; the morphological development of high temperature oxide scales of Fe-Mn-Al base alloys; and the oxidation of an Fe-Mn-Al-C alloy at 1000 C. Consideration is given to the corrosion properties of Fe-Mn-Al ...

British Library Electronic Table of Contents (United Kingdom)

Gas nitridation has shown excellent promise to form dense, electrically conductive and corrosion-resistant Cr-nitride surface layers on Ni-Cr base alloys for use as proton exchange membrane fuel cell (PEMFC) bipolar plates. Due to the high cost of nickel, Fe-base bipolar plate alloys are needed to meet the cost targets for many PEMFC applications. Unfortunately, nitridation of Fe-base stainless steel alloys typically leads to internal Cr-nitride precipitation rather than the desired protective surface nitride layer formation, due to the high permeability of nitrogen in these alloys. This paper reports the finding that it is possible to form a continuous, protective Cr-nitride (CrN and Cr2N) surface layer through nitridation of Fe-base stainless steel alloys. The key to form a protective Cr...

Energy Technology Data Exchange (ETDEWEB)

In this work, we have investigated the capability of different bimetallic nanoparticle alloy combinations to be used in fibre optic sensors based on the technique of surface plasmon resonance. The metals considered for this analysis are silver, gold, copper and aluminium. The performance of the sensor with different bimetallic nanoparticle alloy combinations is evaluated and compared numerically. The performance is analysed in terms of three parameters: sensitivity, signal-to-noise ratio (SNR) and operating range for the sensing layer refractive index values. On the basis of the comparison and some logistic criteria, the best possible bimetallic alloy combinations along with a requisite alloy composition ratio are predicted. The bimetallic nanoparticle alloy combination is capable of simultaneously providing larger values of sensitivity, SNR and operating range, which is not ...

British Library Electronic Table of Contents (United Kingdom)

Statement of problem Because noble dental casting alloys for metal ceramic restorations have a wide range of mechanical properties, knowledge of these properties is needed for rational alloy selection in different clinical situations where cast metal restorations are indicated. Purpose The purpose of this study was to compare the mechanical properties and examine both the fracture and polished surfaces of 6 noble casting alloys that span many currently marketed systems. Five alloys were designed for metal ceramic restorations, and a sixth Type GPT has Type IV alloy for fixed prosthodontics (Maxigold KF) was included for comparison. Material and methods Specimens (n=6) meeting dimensional requirements for ISO Standards 9693 and 8891 were loaded to failure in tension using a universal testin...

Energy Technology Data Exchange (ETDEWEB)

Resistance of Alloy 800 as a PWR S/G tube material to IGC/IGSCC and Ni, Co release into water was evaluated as compared with Alloys 600 and 690. The study to improve the resistance to IGSCC and general corrosion was also made, including the effects of shot-peening on the distribution of the residual stress of the U-bent tubes and the susceptibility to SCC, the stabilizing elements on IGC/IGSCC, and prior oxidation on general corrosion. From the results, shot-peened Alloy 800 was estimated to be the most reliable S/G tube material among the high nickel alloys tested. In addition, the Alloy 800 tube would obtain further reliability in IGSCC and general corrosion resistance by the combined addition of Ti, and Nb, and the prior oxidation of the inner tube surface, respectively.

Energy Technology Data Exchange (ETDEWEB)

Results of strain controlled fatigue and tensile tests are presented for two nickel base solution hardened alloys which are reference structural alloys for use in several high temperature gas cooled reactor concepts. These alloys, Hastelloy X Inconel 617, were tested at temperatures ranging from room temperature to 871/sup 0/C in air and impure helium. Materials were tested in the solution annealed as well as in the pre-aged condition where aging consisted of isothermal exposure at one of several temperatures for periods of up to 20,000 h. Comparisons are also given between the strain controlled fatigue lives of these alloys and several other commonly used alloys all tested at 538/sup 0/C.

Energy Technology Data Exchange (ETDEWEB)

In order to develop the filler metal for Hastelloy alloy XR structure with thick wall, the weldability and high temperature strength properties of Hastelloy alloy XR weldment were investigated using the filler metals, which were alloy-designed on the basis of multiple regression analysis. The former was examined through the chemical analysis in the deposited metal, bend test, FISCO cracking test, optical microscopy and hardness measurement. The latter was investigated by means of tensile and creep test. It was found from these results that the crack susceptibility in the weldment was apparent to be lowered without degrading the high temperature strength properties. Therefore, it is concluded that these filler metals possess excellent performance as the filler metal for Hastelloy alloy XR structure with thick wall. (author).

Energy Technology Data Exchange (ETDEWEB)

The effect of the composition of multicomponent Zr-Ti-V-Mn-Cr-Ni alloys on their hydrogen-storage capacity and on the rate of electrosorption/desorption hydrogen was investigated under potentiodynamics as well as single-pulse and long-term galvanostatic conditions. The main characteristics of alloys and alloy electrodes were determined by their structural analysis by means of X-ray diffraction and scanning electron microscope, by specific surface area test and by determination of the hydrogen absorption/desorption isotherms in the gas/solid phase system. It was found that only the alloys with a manganese content below a threshold could be used as electrode materials for Ni-MH batteries, whereas the modification of the electrode material by micro-encapsulation of alloy particles should limit the dissolution of manganese from the electrode material in a strong alkaline solution. ...

Energy Technology Data Exchange (ETDEWEB)

Recent developments on plastic forming technology of magnesium alloys are presented. Attempts have been undergoing with an aim at forming magnesium alloy parts at lower temperatures. It is believed that fine microstructure magnesium alloys usually have much higher plasticity at lower temperatures and even room temperatures. Extrusion is a method to form magnesium profile products and tube products, which is also one of the effective ways to make fine microstructure magnesium alloys. Superplasticity forming is another method to form high plasticity magnesium alloys. Hot forming of magnesium sheet parts is an important process to form magnesium products. Some developments related to above issues are discussed in the present paper. (orig.)

International Nuclear Information System (INIS)

The corrosion behavior of the sputter-deposited amorphous or nanocrystalline W-Nb alloys is studied in 10% NaCl, 0.1 and 1 M NaOH solutions at 24 deg. C, open to air using immersion tests and electrochemical measurements. Niobium metal acts synergistically with tungsten in enhancing the corrosion resistance of the W-Nb alloys so as to show lower corrosion rates than the corrosion rates of the alloy-constituting elements in almost all examined solutions. Corrosion rates of W-Nb alloys are about more than one order of magnitude less than that of the sputter-deposited tungsten and even lower than that of sputter-deposited niobium. The stability of the anodic passive films formed on the W-Nb alloys increase with niobium content.

British Library Electronic Table of Contents (United Kingdom)

A body-centered cubic (bcc) Mg-12Li-9Al-1Zn (wt.%) alloy was fabricated in air by electrolysis from LiCl-KCl molten salt at 500degreeC. Electrolytic deposition of Li atoms on cathode (Mg-Al-Zn alloy) and diffusion of the Li atoms formed the bcc Mg-Li-Al-Zn alloy with 12wt.% Li and only 0.264wt.% K. Low K concentration in the bcc Mg alloy strip after the electrolysis process resulted from 47% atomic size misfit between K and Mg atoms and low solubility of K in Mg matrix.

Energy Technology Data Exchange (ETDEWEB)

The authors examine the relationship of the structure and mechanical properties of similar alloys of tungsten with rhenium produced by the powder metallurgy method by sintering powders. Since the alloys were deformed by rolling, we examine the effect of the resultant anisotropy of the structure on the properties of the metal in various directions. The tests were conducted on an alloy of tungsten with 2 wt.% rhenium and, for comparison purposes, an alloy of tungsten with additions of oxides of yttrium and hafnium. The mechanical properties of the alloys, i.e., strength, cracking resistance, cold shortness temperature, were determined in the bend test. Structural examination was carried out using an optical microscope, electron scanning microscopy, and the method of transmission electron microscopy.

International Nuclear Information System (INIS)

The cross section and activity profile of different radioisotopes produced by #alpha#-induced nuclear reaction on natural zirconium, have been obtained by stacked foil activation using 40 MeV #alpha#-particles from Variable Energy Cyclotron (VEC) machine at Calcutta. The activity profile would be used to study the surface loss of zircaloy materials of engineering components by thin layer activation (TLA) technique. Generally, isotopes with suitable #gamma#-rays and long half-lives are the most useful in TLA technique, e.g., "9"2Nb, "9"5"gNb and "9"5Zr. (author). 2 refs., 1 tab.

International Nuclear Information System (INIS)

Stable boiloff of core water during a severe LWR accident, that is, boiloff driven only by the decay power generated below the water level, is tractable analytically and is relatively insensitive to axial power distribution. As might be expected, calculated accident event times are sensitive to the fidelity of the decay power model. During later stages of boiloff, heat transfer or transport of energy from above the water level to the residual water can result in an unstable condition during which the boiloff rate increases greatly. The unstable boiloff phenomenon illustrates the highly nonlinear influence of core heat transfer during meltdown and emphasizes the great accuracy requirements which attend the modeling of the accident during periods of enhanced heat transfer when significant zirconium oxidation is possible.

International Nuclear Information System (INIS)

Zirconia-toughened sialon composites have been fabricated using conventional hot-pressing techniques. The fracture toughness and microstructure were determined for CeO_2- and Y_2O_3-stabilized ZrO_2 additives and also as a function of volume percent ZrO_2. The Yttria system showed a linear increase in fracture toughness with increasing volume fraction zirconia content while the ceria-stabilized system exhibited a peak in fracture toughness at 20 vol% ZrO_2 content. The fracture toughness at 800 C was measured and correlated with the microstructure. High-temperature stability was determined and it was found that the deleterious nitride phases of zirconium could be precluded from the microstructure.

British Library Electronic Table of Contents (United Kingdom)

Spherical nano-sized YSZ (yttria stabilized ZrO2) powders were successfully synthesized via a reverse microemulsion system. The water droplets in the microemulsion system of yclohexane/water/span85/Triton X-100/hexyl alcohol can act as the nano-reactors which solubilize zirconium oxychloride and ammonia water separately. The minute original reactors are favor to the formation of nano-sized spherical YSZ powders and the dispersibility of the powders can be controlled effectually by adjusting the weight ratio of the LiNO3 molten salt to the precursor. The phase transformation from cubic to monoclinic starts at and 500??C and finally monoclinic and cubic phase with increased crytallinity coexist at 800??C. The effect of LiNO3 molten salt in the formation of YSZ powders was also discussed.

International Nuclear Information System (INIS)

Ionizing radiations that differ in number, size, and distribution of energy deposition events might be expected to cause different effects for the same absorbed dose. Furthermore, microdosimetry calculations suggest that large variations in biological effectiveness might be expected for internally deposited alpha-emitting radionuclides for the same absorbed dose, depending upon the specific activity and spatial distribution of the sources in tissue. The study described in this article was designed to demonstrate these phenomena in vitro. Cultured Chinese hamster ovary (CHO-K1 BH4) cells were exposed in vitro to inert, insoluble ceramic microspheres in zirconium dioxide labeled with "2"3"9Pu. The average exit energy of the 5.15 MeV alpha particle was calculated to be 4.3 MeV. Exposure times varied from four to seven hours to achieve the desired dose level.

International Nuclear Information System (INIS)

During the service in nuclear power plants, steam generator (SG) tubing will suffer from a vibration with a frequency from 30-40 Hz. This means that SG tubing will undergo a very high cycle fatigue process during the design life time (25 years=about 3x10"1"0cycles). The material degradation and the very high cycle fatigue life of SG tubing materials due to the vibration are therefore of concern. In this investigation, the fatigue properties of Alloy 690 and Alloy 800 SG tubing in the very high cycle fatigue regime (higher than 10"7 cycles) and strain controlled fatigue at temperatures up to 330"oC have been investigated. The fatigue properties of SG tubing of Alloy 690 are comparable to that of wrought material. The strain controlled fatigue properties of Alloy 690 and Alloy 800 are slightly better at 288"oC than at room temperature (RT). At the stress near the fatigue endurance, ...

International Nuclear Information System (INIS)

Available data are presented which support the supposition that metals and alloys with a negative low-temperature Hall coefficient are apparently not superconducting. (author).

Energy Technology Data Exchange (ETDEWEB)

The possibility of rapid heat treatment (RHT) application to titanium castings has been studied. It was shown that such treatment provides a significant improvement of intragrain structure and mechanical properties of cast ({alpha}+{beta})-titanium alloys. ((orig.))

Energy Technology Data Exchange (ETDEWEB)

A process for the generation of halogens from halide-containing solutions includes the step of conducting electrolysis of the solutions in an electrolytic cell having a platinum based amorphous metal alloy anode.

Energy Technology Data Exchange (ETDEWEB)

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride <0.05 M containing 30% ethylene glycol solution, they are more corrosive than the blank (30% ethylene glycol-70% water). However, at concentrations <0.05 for chloride or >0.05 M for fluoride containing ethylene ...

International Nuclear Information System (INIS)

The status of development and commercialization of a modified 9 Cr-1 Mo alloy is presented. The alloy is modified by the addition of 0.06 to 0.10% Nb and 0.18 to 0.25% V. The alloy is recommended for use in the normalized and tempered condition (1040"0C for 1 h, air cooled to room temperature; 760"0C for 1 h, air cooled to room temperature). Heat treatment, Charpy impact, tensile, and creep properties of the alloy are described in detail along with a brief description of other properties. The modified alloy has creep strength that exceeds that of standard 9 Cr-1 Mo and 2 1/4 Cr-1 Mo steels for the temperature range from 427 to 704"0C. The total-elongation and reduction-of-area values for all test temperatures and rupture times up to 22,500 h exceed 15 and 70%, respectively. The estimated design allowable stresses for this alloy are higher than those for standard ...

Science.gov (United States)

Quantitative metallography is often used to confirm the proper processing of aerospace metallic materials. A microstructural feature of great importance for titanium alloys processed in the alpha-beta phase field is the volume fraction of primary alpha. S...

Energy Technology Data Exchange (ETDEWEB)

The carbon transfer has been analyzed in the Alloy 800/sodium/stainless steel system by determining the carbon-uptake of Alloy 800 foils, which were exposed in liquid sodium of known carburizing potential. Under equilibrium conditions between 650 and 550/sup 0/C the measured total carbon concentrations in the Alloy 800 tabs were found to be roughly related to the carbon activities of the sodium environment by the equation already stated for the 18 Cr-8/10 Ni stainless steels, extrapolated to the chemical composition of the Ni-rich austenitic alloy. However the Alloy 800 was not found to undergo any decarburization in low-carbon activity environments. The carbon diffusion kinetics was determined as a function of temperature, it was found to be similar to that reported for the AISI-304 type of steel. The effects of sodium exposure on microstructural and mechanical properties of ...

Science.gov (United States)

The authors have presented results of an investigation of wettability of SiC particulates by liquid alloys of the Al-Si-Mg system. The evaluation of wetting has been carried out through the determination of the threshold pressure for infiltration of packed SiC particulates by the liquid alloy. The results indicate that whereas Si and Mg additions do not affect wetting, in the case of the ternary alloys the contact angle decreases in an amount proportional to the content of Mg[sub 2]Si.

International Nuclear Information System (INIS)

A series of ball-on-disc wear and friction measurements were made for surfaces which have a chemical vapour deposition carbon silicon alloy layer on a carbon substrate (fine grain POCO graphite). Nitrogen ion irradiation was used to improve the wear resistance of the carbon alloy surface. For comparison, measurements were also taken for alumina against alumina. It was found that the lowest friction coefficient and lowest wear occurred for ion irradiated coated samples containing 4% Si in the alloy and that the performance was superior to that of alumina. ((orig.)).

Energy Technology Data Exchange (ETDEWEB)

The exposure of heat-resistant alloys to high temperature can significantly change their mechanical properties. This paper presents and analyzes data on the effect of thermal exposure on the tensile and impact behavior of three cast materials -- the HK-40, HP-50, and 21Cr-32Ni-Fe alloys -- and of wrought material -- Alloy 800. The changes in tensile and impact properties caused by high-temperature exposure are reviewed. Reasons for these property changes and needs for considering them in the design, operation, and life assessment of high-temperature equipment are discussed.

Energy Technology Data Exchange (ETDEWEB)

The chemical properties of alloys in a given environment are to a large extent governed by the surface composition. Changes of the surface composition during passivation are important features in this respect. Previous studies of single crystal Ni-Mo alloys surfaces have been reported. The aim of this work was to obtain quantitative data, for the natural oxide and the passive films formed on Ni-6% Mo(100) and (110) alloys, using Rutherford backscattering spectroscopy and nuclear reaction analysis.

International Nuclear Information System (INIS)

Phase transformations occuring during cold deformation in hardened #alpha#+#beta# titanium alloy of the Ti-Al-Mo-Zr-Sn-Si system with 10% summary content of alloying elements are studied by X-ray diffraction analysis. Two stages of trapsformation of metastable #alpha#''-phase are found. A conclusiop is made that ability of the alloy containing #alpha#''-phase to cold deformation is determined by the presence of favourable texture, by high degree of metastability and by volume portion of #alpha#''-phase in the alloy structure.

International Nuclear Information System (INIS)

A computerized corrosion measuring system (EG and G model 350 A) was used to study the influence of Cr, Mo, Ti, Nb and W on the pitting corrosion of nickel base alloys in 3% NaCl at 90"0C. The electrochemical parameters under investigation are the corrosion potential E_c_o_r_r, pitting potential E_p and protection potential E_p_p. The corrosion behaviour of nickel base alloys were studied by using pitting scan and potentiostatic techniques. Values of corrosion potential, pitting potential and protection potential were used for a ranking of alloys for corrosion resistance.

International Nuclear Information System (INIS)

Formation of the soft magnetic nanostructure in amorphous Fe_1_4Ni_4_0Zr_7B_1_2 alloy due to heat treatment is studied by the Moessbauer, differential scanning calorimetry, and X-ray diffraction techniques. Annealing at temperatures 520-580 "oC leads to the formation of extremely soft nanocrystalline alloy as revealed by the rf-Moessbauer measurements. The superparamagnetic behaviour was observed for the alloy annealed at 620-640 "oC. At higher annealing temperatures good soft magnetic properties deteriorate. (author)

Energy Technology Data Exchange (ETDEWEB)

Experiments were conducted which established that the higher passivating capacity of Ni/sub 60/Nb/sub 40/ alloys in the amorphous state and higher efficiency of the anodic process of generation of chlorine (2 N NaCl + HCl to pH = 0) in comparison with the crystalline state are determined by higher homogeneity and density of the passive films formed on the amorphous alloy and by higher electron conduction which depends directly on the difference in the structure of the passive films formed on the alloys in the amorphous and crystalline states.

International Nuclear Information System (INIS)

The methods of optical and transmission electron microscopy were used to study the influence of different programmes of hot deformation on the structure formation of (#alpha#+#beta#) titanium alloy VT9. The #beta# alloy VT-15 was studied at the same time in order to simulate the dislocation structure generated in the process of hot deformation. During the hot deformation of two-phase titanium alloys in both #beta# and (#alpha#+#beta#) ranges there is found to be an optimum range of deformation in which a homogeneous, polygonized structure is formed.

International Nuclear Information System (INIS)

We propose a dissolution-passivation model to account for the electrochemical behavior of Alloy 800 and 316L stainless steel under steam generators operating conditions. This model is similar to the one defined for nickel, considering the known importance of this element on the studied alloys. The comparison of the rates of the elementary steps points out the favorable influence of dissolved oxygen and phosphate ions on the dissolution of Alloy 800, even in the presence of chloride ions. The sensitivity of 316L SS is greater, especially because of the lowest stability of oxide-like intermediate.

Energy Technology Data Exchange (ETDEWEB)

An experimental verification for long-term performance of a Pd-Ag permeation in ITER tritium fusion cleanup units (FCU) is needed. In addition, information is required on the influence of tritium and {sup 3}He decay on the physical and chemical properties of Pd-Ag alloys (V-1). The results of the investigations of alloys (V-1) (mechanical properties and microstructure) after long-term usage exposition in tritium are given in this report. The experimental conditions (temperature, pressure, clearance, {sup 3}He concentrations) and the previous conclusions on the V-1 alloy performance are presented. (orig.).

International Nuclear Information System (INIS)

Formation of basis type texture at rolling of Ti + 6.0% Al + 1.5% V + 1.0% Mo system alloy with initial prismatic texture is investigated by means of X-ray techniques. Variations of mechanical features in titanium alloy sheets depending on temperature-deformation conditions of rolling are investigated. Main conditions for formation of the intensive basis textute in the investigated alloy sheets which provides for isotropic properties in sheet plane and for increased ductility are determined.

Energy Technology Data Exchange (ETDEWEB)

The most typical kinds of corrosion of brasses are selective corrosion (dezincification) and stress corrosion. Prevention against these kinds of corrosion lies in application of arsenic alloy addition and appropriate heat treatment removing internal stresses as well as in maintaining the arsenic and phosphorus contents on a proper level. The most typical corrosion of cupronickels is the local corrosion. Selective corrosion occurs less often and corrosion cracking caused by stress corrosion in sea water does not usually occur. Crevice corrosion is found especially in places of an heterogeneous oxidation of the surface under inorganic deposits or under bio-film. Common corrosive phenomena for brasses and cupronickels are the effects caused by sea water flow and most often the impingement attack. Alloy additions improve resistance to the action of intensive sea water flow but situation in this field requires further improvement, especially if the ...

International Nuclear Information System (INIS)

Existing applications of Alloy 800 are summarized, with particular reference to its use in various types of reactor. The need for a co-ordinated research and development programme is stressed, and the variables to be explored are outlined. The papers relating to the problem of corrosion and cracking in water and steam are considered. the strength and ductility of Alloy 800 is considered. Finally, sections of the summary deal with the use of Alloy 800 for (a) sodium cooled fast reactor boiler tubes; (b) the high temperature gas cooled reactor; and (c) PWR steam generator tubes. (U.K.).

Energy Technology Data Exchange (ETDEWEB)

Two extruded magnesium alloys, AZ31 and AZ61 were selected to evaluate the influence of process parameters on the material forgeability. The processing parameters considered for forging magnesium alloys were: compression load in the range 55 KN to 60 KN and forging temperature, in the range of ambient temperature to 300 C. Uniaxial compression tests were conducted to establish the strain-temperature relationship. The influences of process parameters on the microstructure were also evaluated. (orig.)

International Nuclear Information System (INIS)

The optimum of strontium amount for good modification of AK7, AK9, AK11, AK52, AK104 alloys was determined on the base of the analysis of microstructural changes. The stability of the modifier was investigated on the way of successive remelting of billets. The influence of amount of modifier on the impact strength of the alloys was established. (author)

Energy Technology Data Exchange (ETDEWEB)

Using commercial AZ31 magnesium alloy sheets, we produced a foamable preform sheet containing titanium hydride (TiH{sub 2}) powder through diffusion-bonding and hot-rolling of four cycles. Heating the preform sheets in Ar atmosphere, we obtained closed-cell magnesium alloy foams with various porosities. The foamed specimen at 883 K showed the maximum porosities of 77%. (orig.)

Energy Technology Data Exchange (ETDEWEB)

One of the effective methods of deep modification of the surface of steels and alloys is the combination of ion implantation and plasma nitriding. In this work, the long-range effect is demonstrated in the case of combination of the effect of high- and low-energy ions of nitrogen on a martensitic steel for each ion implantation is usually not effective, and a titanium alloy used widely in industry.

International Nuclear Information System (INIS)

Cyclic strength of #alpha#+#beta#-titanium alloy BT3-1 is studied under load frequencies of 33 and 300 Hz. The increase in the cyclic strength with growing frequency is caused by formation of FCC interphase layers of titanium hydrides. Their formation is one of possible ways of raising the fatigue strength of titanium alloys. Peculiarities of FCC interlayer formation in #alpha#+#beta# phases under loading frequency variation are revealed.

Energy Technology Data Exchange (ETDEWEB)

The distribution of graphite particles in graphite containing copper alloy was further improved very significantly using several procedures and technological modifications. The developed techniques attacked the graphite distribution problem in two ways. Realizing that clustering of very fine (5um) graphite particles is one of the two major problems, a pretreatment process has been developed using aluminum powders to deagglomerate graphite particles. Along with this, a two-stage stirring technique was used to first incorporate and then to distribute uniformly the deagglomerated particles in the melt. During this year, based on these developments, several components were cast to evaluate the castability of Cu alloy-graphite melts. In addition, machinability tests were done to clearly established that addition of graphite particles improve the machinability of copper MMC alloys over and above that of monolithic copper ...

International Nuclear Information System (INIS)

Peculiarities of metastable #beta#-solid solution decmposition in titanium alloy VT30 in the process of isothermal ageing in the range 500-650 deg C are investigated. Using the methods of transmittion electron microscopy, X-ray diffraction analysis, etc., it is shown that in the case of alloy quenching from the temperature below the point of complete polymorphous transformation (T_t_._t_.), as well as after warm rolling the course of subsequent decomposition of solid solution can be consierably complicated.

International Nuclear Information System (INIS)

A historical overview of corrosion problems found in power plant condensers and mitigation procedures is presented. The paper is organized according to alloy type and failure mode. Alloys considered are copper-base alloys, stainless steels and titanium. Failure modes discussed include erosion-corrosion, sulfide attack, environmentally assisted cracking, galvanic corrosion, steam condensate corrosion, pitting corrosion, and dealloying. Mitigation procedures discussed include cathodic protection, ferrous ion injection, as well as tube cleaning and layup practices.

Energy Technology Data Exchange (ETDEWEB)

The present results indicate that maximum selectivity to acrylic acid can be reached over V-P-Zr-O catalysts. When the hydrocarbon concentration is 5.1 vol.% the selectivity is about 30% at quite high paraffin conversion. Conclusively, some explanations to the observed facts can be given. The V-P-O catalyst promotion with lanthanum by means of mechanochemical treatment is distinguished by the additive uniform spreading all over the matrix surface. Such twophase system is highly active in propane conversion (lanthanum oxide) and further oxidation of the desired products. The similar properties are attributed to V-P-Bi-La-O catalyst. Bismuth, tellurium and zirconium additives having clearly defined acidic properties provoke the surface acidity strengthening and make easier desorption of the acidic product (acrylic acid) from the surface lowering its further oxidation. Additionally, since bismuth and zirconium are able to form phosphates and, ...

Energy Technology Data Exchange (ETDEWEB)

Purification parameters of the vacuum distillation process for AM50A and AZ31B magnesium alloy were studied. The vacuum distillation tests were kept at 580 C to 620 C up to 10 h under a vacuum pressure of about 1 Pa. The purification ratio for AM50A magnesium alloy increases with increasing the purification time. The chemical compositions of materials deposited purifying at 580 C for AM50A magnesium alloy almost satisfy the values for pure magnesium specified by JIS standard specification. The chemical compositions of deposited materials at 600 C for AZ31B magnesium alloy satisfy the values specified by the standard specification except for Zn. (orig.)

International Nuclear Information System (INIS)

Thermohydrogen treatment effect on microstructure and mechanical properties is studied for a cast heat resistant pseudo-#alpha#-titanium alloy Ti-6242 (Ti-6Al-2Sn-4Zn-2Mo) widely used as a heat resistant material with operating temperature up to 500 deg C. It is shown that reversible hydrogen alloying is a promising alternative to thermomechanical treatment for transformation of (#alpha#+#beta#)-titanium alloy structure. The application of thermohydrogen treatment is noted to be of particular efficiency for shaped casting technology as it allows a noticeable increase of mechanical properties at a lower cost. The alloy after thermohydrogen treatment and subsequent heat treatment in the (#alpha#+#beta#) - range possesses high values of yield strength fatigue properties, creep resistance and has a satisfactory ductility. A consideration is also given to thermohydrogen treatment effect on fatigue crack ...

International Nuclear Information System (INIS)

The constituent phases and associated deformed microstructure of the quenched Ti-xNb-(0.5-1.5) at.% Si alloy consisting of non-cytotoxicity elements, where x = 24-30 at.%, were investigated to provide pseudoelasticity for biomedical and sensor applications. Optical microscopy revealed that stress-induced martensitic transformation takes place during the deformation in the present alloys. It is confirmed from the X-ray diffraction results of the deformed specimens that the crystal structure of the stress-induced martensite phase is the orthorhombic so-called #alpha#'' structure. Within the alloys having #beta#(bcc) phase studied Nb-poor region appeared to exhibit a dominant behavior for stress-induced martensitic transformation than Nb-rich region. This result suggests that metastable #beta# phase is superior to stable #beta# phase for the occurrence of stress-induced martensitic transformation in the present ...

Energy Technology Data Exchange (ETDEWEB)

In this work, we have investigated the capability of different bimetallic nanoparticle alloy combinations to be used in fibre optic temperature sensing based on the technique of surface plasmon resonance (SPR). The metals considered for the present analysis are silver, gold and aluminium. The analysis is derived mainly from the thermo-optic effect along with some fundamental concepts of metal optics such as surface scattering, phonon-electron scattering and electron-electron scattering. The performance of the sensor with three different bimetallic nanoparticle alloy combinations is evaluated and compared, numerically, in terms of its sensitivity and accuracy. On the basis of the comparison and some logistic criterion, we predict the best possible bimetallic alloy combination along with a requisite alloy composition ratio that simultaneously provides higher values of both sensitivity and accuracy which ...

International Nuclear Information System (INIS)

Transmission electron microscopy studies on solution-annealed Alloy 800 revealed small (100-200 nm), spherical-shaped titanium carbide (face centered cubic structure) and large (200 nm-5 #mu#m), faceted titanium nitride (hexagonal structure) particles randomly distributed in the austenite matrix. The volume fraction of former particles was found to be greater than that of the latter. Corrosion studies of the alloy in acidic, chlorides and acidic chloride environments at room temperature indicated that the passivity of Alloy 800 was adversely affected by the addition Cl"- ions. X-ray photoelectron spectroscopy revealed that the surface film formed on the alloy at the onset of passivity consisted of Cr"3"+ (as Cr_2O_3), without any Fe"3"+/Fe"2"+ or Ni"2"+. Scanning electron microscopy studies indicated initiation of pitting at large, faceted particles, not at small, spherical-shaped ones.

International Nuclear Information System (INIS)

High purity Fe-50mass%Cr alloys containing (C+N) in the range of 30 to 500 mass ppm were prepared and their corrosion resistance was investigated. Pitting potential in a 3.5mass%NaCl solution at 343K rose with reducing (C+N) content. Alloys containing (C+N) at less than 100 mass ppm did not sustain pitting corrosion. However, alloys containing 500 mass ppm (C+N) corroded severely in 6%FeCl_3+1/20N HCl solutions. Heat treatment at 923K was recognized as influencing corrosion resistance due to precipitation of carbonitrides only in the case of the alloy containing 500 mass ppm (C+N). (orig.).

International Nuclear Information System (INIS)

The powder particle size, D, influences the creep behaviour of Al-Cr-Zr alloys. The alloy studied in this work, Al-5Cr-2Zr (mass%), was prepared by argon atomization. Three size fractions of powder particles were selected: 24-50 #mu#m, 50-100#mu#m and 100-200 #mu#m in diameter. They were consolidated by extrusion. Independently of D, the flow behaviour of the alloy can be described by the power law equation. As test temperature increases, the stress exponent n decreases up to a value close to 5. A decrease of D causes an increase of n and delays the alloy degradation at high temperature. (Author) 11 refs.

British Library Electronic Table of Contents (United Kingdom)

A microanalytical characterization of cast magnesium alloys of eutectic origin based on the Mg?Al?Ca ternary matrix system has been carried out in order to investigate the influence of alloying elements on their microstructure as well as microchemistry-processing-microstructural relations using structure-sensitive techniques of electron microscopy, mechanical spectroscopy (internal friction), X-ray diffractometry, and advanced microanalytical methods including electron probe compositional analysis. Following the data obtained here there is direct correlation of microstructure with creep properties of the new experimental magnesium alloys. The creep and heat-induced properties of the multicomponent magnesium alloys containing low range of inexpensive additions of titanium (0.07?0.2%) or str...

International Nuclear Information System (INIS)

Alloy 800 and Alloy 600 are well known for their resistance to corrosion in an aqueous medium at high pressure and temperature, for which they have been widely used for more than 3 decades in different structural components of water refrigerated nuclear reactors, especially as material for the steam generator tubes (SG) in these nuclear plants. The SG tubes in the Atucha I and Embalse Nuclear Plants are made with Alloy 800. The speed of corrosion of these materials in a reactor's refrigerant medium, while very small is perfectly measurable and can be described by parabolic or logarithmic type kinetics. In other words this speed is high in the first states of growth during the formation of a protective oxide film but then drops to almost stationary values. One characteristic of these films is the formation of a double layer (or duplex): i) an internal adhering layer, of approximately constant thickness, formed by small ...

British Library Electronic Table of Contents (United Kingdom)

In the present work, bulk amorphous and nanocrystalline Al83Fe17 alloys were obtained by consolidation of mechanically alloyed powders. Mechanical alloying of Al-17% Fe powder mixture yielded powder with an amorphous structure. Thermal behaviour of the milling product was examined using differential scanning calorimetry. This investigation revealed that the amorphous phase crystallised above 380^oC. The amorphous powder was compacted under a pressure of 7.7GPa in different conditions: at 380^oC for 600s and at 1000^oC for 180s. Structural investigations of the bulk material revealed that the amorphous structure was retained after consolidation process applied at 380^oC. Compaction under high pressure at 1000^oC caused crystallisation of the amorphous phase and appearance of metastable nano...

International Nuclear Information System (INIS)

In view of the importance of the material Alloy 800 in high-temperature reactor plants (HTR), a material data bank was established which is used for statistical evaluation of mechanical and physical material behaviour. Based on investigations on the interconnection between the mechanical properties at high temperatures and the metallurgical parameters, different types of Alloy 800 were specified in compliance with the component requirements. In addition, aspects of corrosion and toughness behaviour were taken into consideration. The specifications and strength characteristics for the different variants of Alloy 800 were incorporated into draft DIN standards after discussion and approval in expert committees. Further important characteristics of the mechanical and physical material behaviour were summarized in HTR material data sheets so as to furnish an improved basis for the design and stress analyses of ...

Energy Technology Data Exchange (ETDEWEB)

The corrosion behaviour of the stainless steels 304, 316 Ti, 25Cr-20Ni-Mo-Ti, nickel base alloys Hastelloy C4, Inconel 625, Incoloy 800, Ti and Ti-0.2% Pd alloy has been studied in the aerated or deaerated solutions at 20/sup 0/C and 90/sup 0/C whose compositions are representative of interstitial ground waters: granitic or clay waters or salt brine. The electrochemical techniques used are voltametry, polarization resistance and complexe impedance measurements. Electrochemical data show the respective influence of the parameters such as temperature, solution composition and dissolved oxygen, addition of soluble species chloride, fluoride, sulfide and carbonates, on which depend the corrosion current density, the passivation and the pitting potential. The inhibition efficiency of carbonate and bicarbonate activities against pitting corrosion is determined. In clay water at 90/sup 0/C, Ti and Ti-Pd show very high passivation aptitude and a broad ...

International Nuclear Information System (INIS)

Effects of PbO on the repassivation kinetics of alloy 690TT were examined using the rapid scratching electrode technique under a potentiostatic condition to elucidate the influence of PbO on SCC resistance of the alloy. The repassivation kinetics of the alloy was analyzed in terms of the current density flowing from the scratch, i(t), as a function of the charge density that has flowed from the scratch, q(t). Repassivation on the scratched surface of the alloy occurred in two kinetically different processes; passive film initially nucleated and grew according to the place exchange model in which log i(t) is linearly proportional to q(t) with a slope of 1/K, and then grew according to the high field ion conduction model in which log i(t) is linearly proportional to 1/q(t) with a slope of cBV. 1/K and cBV are parameters representing the SCC susceptibility as well as repassivation rate of the ...

Energy Technology Data Exchange (ETDEWEB)

The present work describes the surface improvement and biocompatibility of TiAl{sub 24}Nb{sub 10} intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to formation of a thin ...

International Nuclear Information System (INIS)

An alloy of composition Ti-4.4 wt.% Ta-1.9 wt.% Nb is being developed as a structural material for corrosion applications, as titanium and its alloys possess excellent corrosion resistance in many oxidizing media. The primary physical metallurgy database for the Ti-4.4 wt.% Ta-1.9 wt.% Nb alloy is being presented for the first time. Determination of the #beta# transus, M_s temperature and classification of the alloy have been carried out, employing a variety of microscopy techniques, X-ray diffraction (XRD), micro-hardness and differential scanning calorimetry (DSC). The #beta# transition temperature or #beta# transus determined using different experimental techniques was found to agree very well with evaluations based on empirical calculations. Based on chemistry and observed room temperature microstructure, the alloy has been classified as an #alpha# + #beta# titanium ...

International Nuclear Information System (INIS)

The possibility of Pt-Cr surface alloys formation on Pt(0 0 1) was investigated and their magnetism was calculated by the full-potential linearized augmented plane wave (FLAPW) method with eight different atomic configurations. The most stable structure was calculated to be the Pt-segregated L1_2 ferromagnetic surface alloy. A_3B types (L1_2 or D0_2_2) were more stable compared to AB types (L1_0). It implies that the A_3B type surface alloys may be formed when depositing a monolayer of Cr on Pt(0 0 1). It was found from the total energy calculations that there exists a strong tendency of the Pt segregation. The segregation further stabilizes the surface alloy significantly. The work function of the most stable surface alloy was calculated to be 6.02 eV and the magnetic moment of the surface Cr was much enhanced to 3.3 #mu# _B. It is a quite interesting finding that the coupling ...

Energy Technology Data Exchange (ETDEWEB)

Secondary ion mass spectrometry (SIMS) has been used to investigate changes that occur in an advanced Ir-0.3W alloy during high temperature aging. This alloy is used to clad /sup 238/PuO/sub 2/ heat sources used in thermoelectric generators for deep space reconnaissance satellites. Long-term direct contact with PuO/sub 2/ at 1400/sup 0/C leads to physical and chemical changes within the cladding alloy that affect its metallurgical properties. SIMS was used to show that Cr, Fe, Ni, and in some cases O, diffuse from the PuO/sub 2/ into the alloy. Thorium and aluminum diffuse out of the alloy in these same regions. This SIMS study suggests that inward O diffusion and subsequent formation of ThO/sub 2/ on grain boundaries may stabilize the alloy against enhanced grain growth.

International Nuclear Information System (INIS)

The AMSE Boiler Code development of design stresses and their optimization for alloys 800 and 800H for conventional and nuclear power plants have coincided with many successful trial installations of these grades of alloy 800. These trial installations, along with laboratory tests, have shown that alloy 800H can be used for long times with a retention of good mechanical properties, including ductility. While gamma prime can be formed, it soon loses its detrimental effect on ductility in service. Sensitization of the alloy also occurs but it, too, has a decreasing effect on corrosion resistance with time in service, especially at elevated temperatures. The authors discuss all of these aspects and conclude that alloy 800 perhaps with low carbon control in the annealed (1800 to 1950degF)(982 to 1066degC) condition gives the optimum combination of properties to 1050degF(566degC) and ...

International Nuclear Information System (INIS)

Ti-15Mo-2.7Nb-3Al-0.2Si (Timetal-21S), a metastable #beta#-titanium alloy, is a candidate material for titanium matrix composite structures in hydrogen-fueled hypersonic planes because of its excellent formability and adequate mechanical properties in the 500--800 C temperature range. The alloy is strengthened through the precipitation of fine #alpha# particles in the #beta# matrix. The mechanical properties and microstructures are controlled by a solutionizing/aging heat treatment. A major concern in using titanium alloys in hydrogen service is the embrittlement caused by the precipitation of hydrides. It is believed that the large solubility of hydrogen in the #beta#-phase would preclude the precipitation of hydrides in Beta titanium alloys, especially at low hydrogen pressures. However, depending on the hydrogen content, a shift in the ductile/brittle transition temperatures to levels much higher ...

International Nuclear Information System (INIS)

The weldability and high temperature strength properties of tungsten-inert-gas (TIG) weldments of Hastelloy alloy XR were investigated by using two different heats of filler metals; the first (HXRF1) was designed on the basis of multiple regression analysis; the second (HXRF2) was the reference material. Bend tests, the FISCO cracking test and optical metallography were used to evaluate weldability. Tensile and creep tests were performed at 900deg C to evaluate high temperature strength properties. The results of weldability tests for both alloys showed good performance. The tensile properties of the weldments were remarkably improved in particular with respect to high temperature ductility. The creep rupture strength in the weldments made with alloy-designed HXRF1 was much higher than those of the Hastelloy alloy XR-II base metal with a higher B content. Furthermore, the creep properties were stable ...

Energy Technology Data Exchange (ETDEWEB)

Alloy 800 has been proposed for use in the receiver tube panel arrays of advanced solar central receiver (SCR) designs. In this application the alloy will be exposed to a molten mixture of sodium and potassium nitrate salts at temperatures ranging up to approximately 600/sup 0/C While these salts are routinely used in a variety of applications including metal heat treating and process heat transfer, common industrial experience has been limited to maximum temperatures of 400/sup 0/C - 450/sup 0/C. There is, therefore, considerable interest in the compatibility of these salts with containment alloys at the higher temperatures associated with SCR designs. Additionally, the containment alloy may be subject to thermally induced fatigue damage resulting from intermittent cloud cover and diurnal cycling. Previous work has found that slower near-threshold fatigue crack growth rates (FCGR) in ...

Energy Technology Data Exchange (ETDEWEB)

In response to European operating experience regarding Alloy 800 steam generator (SG) tube cracking, New Brunswick Power Nuclear (NBPN) recognized two important shortcomings in the industry SG technical support framework. First, information exchange networks between utilities with Alloy 800 SG tubing should be strengthened. Second and more importantly, there is a need for consistent industry guidance for Alloy 800 SG tubing degradation management, supported by clear technical bases. It is NBPN's perspective that this guidance can be improved immediately using the extensive amount of laboratory and field data that is available for Alloys 600, 690, and 800, and EPRI methodology developed to predict the performance of Alloy 690. NBPN has initiated the development of a performance-based inspection plan. This effort is based on demonstrated improvement factors for ...

Energy Technology Data Exchange (ETDEWEB)

Austenitic stainless steels (304-type) have been implanted with nitrogen ions in order to investigate the effects of implanted nitrogen on their electrochemical behaviour and on the nature of the passive film formed on the steels in acid (0.5M H{sub 2}SO{sub 4}). Alloys with two nitrogen doses have been prepared (2.5x10{sup 16} and 2x10{sup 17} N atoms/cm{sup 2}). The implanted alloys have been characterized by {sup 15}N-NRA (nuclear reaction analysis) and XPS (X-ray photoelectron spectroscopy). Alloy surfaces with well-defined N concentrations were prepared, prior to the electrochemical measurements, by argon-ion sputtering of the implanted material for a fixed time in order to reach a well-defined point on the nitrogen depth profile. The samples were then transferred without exposure to air to an electrochemical cell mounted in an inert gas glove box. The implanted nitrogen modifies the electrochemical behaviour of the ...

Energy Technology Data Exchange (ETDEWEB)

An Fe-19Cr-8Al-0.5Hf alloy has been roll bonded to Alloy 800 to form a protective clad material suitable for use in coal conversion atmospheres. The commercial producibility of both the Fe-19Cr-8Al-0.5Hf alloy and the clad composite has been demonstrated. The clad composite has been shown to exhibit resistance to sulfidation in high sulfur, coal gasification atmospheres low Btu for 2000 hrs at 1800/sup 0/F (1255K). The FeCrAlHf alloy must be preoxidized in the absence of sulfur to form fully protective alumina scales on all surfaces. Useful life of the composite at temperatures of 1400 to 2000/sup 0/F (1033 to 1366K) is governed by reactions at the FeCrAlHf clad alloy 800 interface. The rate of interdiffusion decreases with increasing Ni content and a high Ni alloy such as RA333 appears to be a better substrate than Alloy 800 for a FeCrAlHf ...

International Nuclear Information System (INIS)

Steam generators (SGs) in PWRs and CANDUs are designed for at least a 30-year operating life. However, in the 15-25 years that SGs tubed with Alloy 600 have operated commercially, they have experienced reduced reliability, mainly due to SG tubing degradation. One of the degradation mechanisms that Alloy 600 SG tubing has suffered from is lead-induced stress corrosion cracking (PbSCC) in AVT and near-neutral SG environments. In contrast to Alloy 600 tubing, test data obtained in high temperature water indicate that Alloy 800 is resistant to cracking by lead and lead compounds. For Alloy 800 (cold worked, shot peened), the most aggressive environment is reported to be alkaline with minor concentration of PbO (80 ppm). Work by Max Helie et al. also concluded that Alloy 800 is not sensitive to lead assisted SCC for pH values close to neutrality, whereas it could be ...

Energy Technology Data Exchange (ETDEWEB)

In this study, the corrosion behavior of commercially pure titanium (c.p. Ti), Ti-6Al-4V and five new experimental Ti-Cr alloys was evaluated through open-circuit potential (OCP) and potentiodynamic polarization measurement in an artificial saliva containing fluoride. Electron spectroscopy for chemical analysis (ESCA) was used to characterize the composition of the passive films on the alloy after potentiodynamic polarization measurement. It was found that in standard artificial saliva the OCP increases with higher Cr content in Ti-Cr alloys. In 0.5% NaF artificial saliva, the OCP decreases with decreasing Cr in Ti-Cr alloys, and all but Ti-5Cr remain consistently higher than those of c.p Ti and Ti-6Al-4V. Linear polarization results show that artificial saliva and artificial saliva containing 0.5% NaF result in different corrosion behavior in Ti-Cr alloys, c.p.Ti and Ti-6Al-4V. The ...

Energy Technology Data Exchange (ETDEWEB)

Austenitic stainless steels have been implanted with molybdenum ions (Mo[sup +], 100 keV, 2.5 x 10[sup 16] atoms cm[sup -2]). The implanted material has been characterized by XPS and RBS. The implanted region has a thickness of [approx] 1000 A with a maximum molybdenum concentration of [approx] 9 at.% Mo located at [approx] 210 A from the surface. The effects of implanted molybdenum on the passivation of the alloy in 0.5 M H[sub 2]SO[sub 4] have been investigated by electrochemistry and XPS. After XPS analysis the samples were transferred without exposure to air into a glove-box with an inert atmosphere. The electrochemical behaviour of the alloy is significantly modified by the implanted molybdenum. The major effect is that the activation peak disappears. A bilayer structure (outer hydroxide/inner oxide) of the passive film is observed for both the implanted and non-implanted alloys and the thicknesses of the films are ...

Energy Technology Data Exchange (ETDEWEB)

We have been developing an innovative Steam Generator concept of Fast Breeder Reactors by using liquid-liquid direct contact heat transfer. In this concept, the SG shell is filled with a molten alloys, which is heated by primary sodium. Water is fed into the high temperature molten alloy, and evaporates by direct contact heating. In order to obtain the fundamental information to discuss the heat transfer mechanisms of the direct contact between the water and the alloy, this phenomenon was visualized by real-time neutron radiography. JRR-3M real-time thermal neutron radiography in Japan Atomic Energy Research Institute was used. Followings are main results. (1) The vigorous evaporation occurs in the molten alloy. This phenomena is different from the known phenomenon such as the evaporation of refrigerant R-113 in the water. (2) The evaporation in the bubble has finished in a moment due to high heat ...

International Nuclear Information System (INIS)

Generally, neutron, ion and electron Irradiations cause a substantial amount of hardening and significantly alter the deformation behavior of metals and alloys at relatively low irradiation temperatures. A radiation hardening is caused by the formation of microstructural defects such as dislocation loops, voids and precipitates under irradiation. Therefore, it is important to have a better knowledge of the irradiation induced microstructural defects under irradiation condition. As a part of the National mid- and long-term atomic energy R and D program, we are dealing with the radiation hardening behavior in Fe-Cr binary alloy. Fe-Cr binary alloy is a base alloy of Ferritic/Martensitic steel(F/M steel) planning to use for the Gen IV nuclear system. In this work, we investigated the radiation hardening and microstructural defect evolution in ion irradiated Fe-Cr alloys with ...

Energy Technology Data Exchange (ETDEWEB)

the medium to long freezing range alloys of aluminum such as A356, A357, A206, 319 for example are known to exhibit dispersed porosity, which is recognized as a factor affecting ductility, fracture toughness, and fatigue resistance of light alloy castings. The local thermal environment, for example, temperature gradient and freezing from velocity, affect the mode of solidification which, along with alloy composition, heat treatment, oxide film occlusion, hydrogen content, and the extent to which the alloy contracts on solidification, combine to exert strong effects on the porosity formation in such alloys. In addition to such factors, the availability of liquid metal and its ability to flow through the partially solidified casting, which will be affect by the pressure in the liquid metal, must also be considered. The supply of molten metal will thus be controlled by the volume of ...

Energy Technology Data Exchange (ETDEWEB)

Material testing of SPF-sheet is usually done with coupon hot tensile testing. The optimum range of strain rates is determined with stepped strain tests. To overcome the problem of very few available testing facilities and time consuming and costly procedure, cone cup testing has been developed since long. This test can be generated directly in the workshop, no machining of samples is necessary and it is very much related to the real SPF-process. The analysis of suitable temperature and strain rate is done by simple measurement of resulting cone height. This paper describes a unique and novel variant of the above mentioned baseline design. It provides on-line data of the actual status of the cone cup forming resulting from the applied, constant pressure. Strain rate variations as a result from texture or from the alloy-related behaviour is detectable. Thinning and ''hardening'' behaviour of different alloys ...

Energy Technology Data Exchange (ETDEWEB)

Refractory metal alloys based on Mo, W, Re, Ta, and Nb (Cb) find applications in a wide range of aerospace applications because of their high melting points and high-temperature strength. This paper, presents recent progress in understanding and applications of these alloys. Recent studies to improve the oxidation and mechanical behavior of refractory metal alloys, and particularly Nb alloys, are also discussed. Some Re structures, for extremely high temperature applications (> 2000C), made by CVD and P/M processes, are also illustrated. Interesting work on the development of new W alloys (W-HfC-X) and the characterization of some commercial refractory metals, e.g., K-doped W, TZM, and Nb-1%Zr, continues. Finally, recent developments in high temperature composites reinforced with refractory metal filaments, and refractory metal-based intermetallics, e.g., Nb{sub 3}Al, Nb{sub ...

International Nuclear Information System (INIS)

The development of light-weight vehicle is in great demand for enhancement of fuel efficiency and dynamic performance. The vehicle weight can be reduced effectively by using lightweight materials such as magnesium alloys. However, the use of magnesium alloys in sheet forming processes is still limited because of their low formability at room temperature and the lack of understanding of the forming process of magnesium alloys at elevated temperatures. In this study, uniaxial tensile tests of the magnesium alloy AZ31B-O at various temperatures were performed to evaluate the mechanical properties of this alloy relevant for forming of magnesium sheets. To construct a FLD (forming limit diagram), a forming limit test were conducted at temperature of 100 and 200 deg. C. For the evaluation of the effects of the punch temperature on the formability of a rectangular cup drawing with AZ31B-O, ...

Energy Technology Data Exchange (ETDEWEB)

Fine-grained AZ31 magnesium alloy sheets were prepared through hot rolling process. The superplastic properties of hot-rolled AZ31 Mg alloy was examined by uniaxial tensile tests at a temperature range 250{proportional_to}450 C and strain rate range 0.7 x 10{sup -3}{proportional_to}1.4 x 10{sup -1} s{sup -1}. Optical and scanning electronic microscope (SEM) were used to observe the microstructure evolution and fracture behavior in superplastic deformation of AZ31 Mg alloy and the values of deformation activation energy at various temperatures were calculated. It is demonstrated that, the hot-rolled AZ31 alloy begins to exhibit superplasticity from 300 C and a maximum elongation of 362.5% is obtained at 400 C and 0.7 x 10{sup -3} s{sup -1}. In the temperature range 300{proportional_to}400 C, the dominant superplastic deformation mechanism is grain boundary sliding (GBS) controlled by grain boundary ...