Energy Technology Data Exchange (ETDEWEB)

In our continued efforts for improving the performance of zinc anodes for a Zn/air battery, we now report the preparation of three alloys and improved performances of anodes made up with these alloys. The alloys contained zinc, nickel, and indium with different weight percentages and were calcined at two different temperatures. Out of the six alloys, the alloy which has a composition of zinc 90%, nickel 7.5% and Indium 2.5% and fired at 500{sup o}C is found to be the best. In the case of the hydrogen evolution reaction, this alloy had its potential shifted to a more negative potential. As far as the cyclic voltammograms were concerned, the difference between the anodic and cathodic part was minimal when compared with other alloys. Surprisingly, this alloy had ...

Science.gov (United States)

The biocompatibility and corrosion resistance of various materials for use as sacrificial anodes in in vivo hybrid fuel cells were studied. Aluminium, zinc, and magnesium alloy AZ31B were studied, and the results are discussed.

Energy Technology Data Exchange (ETDEWEB)

The principle of conservation and transferability of chemical bonds explains the recent discovery by extended x-ray absorption fine-structure measurements of two unequal anion-cation bond lengths R/sub A/C and R/sub B/C in A/sub x/B/sub 1-x/C zinc-blende semiconductor alloys despite the close adherence of the lattice constant to the average value (Vegard rule). This bond alternation, manifested as a structural distortion to a local chalcopyrite coordination around the anions, explains also most of the observed optical bowing in semiconductor alloys.

International Nuclear Information System (INIS)

The photon rupture method, by which oxide film and metal are removed by focused pulsed Nd-YAG laser beam irradiation, was applied to form artificial micro-pits in Zn-5 mass% Al alloy-coated steel. The zinc alloy-coated layer was removed by pulsed laser irradiation treatment for about one second in a neutral buffer solution with NaCl. The rest potential transient with the laser treatment was measured. In the early stage of the laser treatment the rest potential of zinc alloy-coated steel changed to the negative direction immediately after every irradiation of a laser pulse and then returned to the previous value. However, after the steel substrate was exposed to the solution, the rest potential moved to the positive direction immediately after every irradiation of a laser pulse and then returned to the previous value. The amplitude and duration of the potential change after the laser ...

Energy Technology Data Exchange (ETDEWEB)

Low operating power and short cycle life are 2 of the main draw-backs of zinc-air batteries, despite the fact that various attempts have been made to develop improved zinc (Zn) anodes. This study investigated the performance of a Zn anode with a substantial addition of aluminium (Al). Rolled sheets of Zn-Al alloys of varying amounts of Zn and Al were used to prepare the anodes. Results of the study showed that the cells had higher open circuit voltages (OCV) values as well as a higher specific anode capacity. It was observed that specific anode capacity increased with higher current loading. The Zn{sub 59}Al{sub 41} and Zn{sub 67}Al{sub 33} sheets showed the highest performance with high OCV values of between 1540 and 1560 mV, as well as the largest specific anode capacity of 750-800 mAh per g at a discharge current of 200 mA. The 2-phase structure of the Zn-Al sheets was considered to be useful in reducing ...

International Nuclear Information System (INIS)

The hydrogen evolution reaction (HER) was studied on bare brass (B), nickel coated brass (B/Ni), nickel-zinc alloy coated brass (B/NiZn, leached Zn), nickel (under layer)/nickel-zinc alloy coated (top layer) brass electrodes (B/Ni/NiZn, leached Zn) in 1 M NaOH solution using electrolysis, cathodic polarization and electrochemical impedance spectroscopy (EIS) techniques. Long term tests were performed in order to evaluate the electrocatalytic activity and corrosion performance of the prepared electrodes with operation time. The results showed that leached electrodes, especially B/Ni/NiZn electrode, have a smaller overpotential than the others and a good electrocatalytic activity for the HER. Its electrocatalytic activity is also stable over electrolysis time. Contrary to the HER performance, B/NiZn cannot provide an adequate corrosion protection. However, when a thin Ni layer was coated under the NiZn ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

From a macroscopic point of view, corrosion of Zn alloy coated steel sheet occurs by the coating preceding corrosion mechanism; microscopically, however, the coated layer corrosion velocity in the tip of corrosion is different. In order to find the main factors of under-film corrosion of Zn and Zn-Fe alloy coatings in the salt water spray atmospheric exposure test, the correlation between point inflation-exfoliation width and chlorine penetration behavior, point adhesion, and the difference in chlorine penetration behavior due to alloy coating components were investigated. Consequently, the following results were obtained: 1. The better correlation was observed between chlorine penetration distance and point inflation-point exfoliation width. 2. The durability of coating against chlorine penetration improved by increase in point adhesion and Zn content in the coating layer. 3. Zn-Fe (10-20%) alloy ...

International Nuclear Information System (INIS)

The description is presented of binary phase diagrams of titanium alloyed with the following elements: silver, aluminium, arsenic, gold, boron, barium, beryllium, bismuth, carbon, calcium, cadmium, cobalt, chromium, copper, iron, gallium, germanium, hydrogen, hafnium, indium, iridium, potassium, lithium, magnesium, manganese, molybdenum, nitrogen, sodium, niobium, nickel, oxygen, osmium, phosphorus, lead, palladium, platinum, plutonium, rhenium, lanthanium, cerium, preseodymium, neodymium, gadolinium, erbium, terbium, thulium, lutetium, rhodium, ruthenium, scandium, silicon, tin, strontium, tantalum, technetium, thorium, uranium, vanadium, tungsten, yttrium, ytterbium, zinc and zirconium.

International Nuclear Information System (INIS)

After being pre-plated a zinc layer, an amorphous Al-Mn alloy coating was applied onto the surface of AZ31B magnesium alloy with a bath of molten salts. Then the corrosion performance of the coated magnesium alloy was examined in 3.5% NaCl solution by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS). The results showed that the single Zn layer was active in the test solution with a high corrosion rate while the Al-Mn alloy coating could effectively protect AZ31B magnesium alloy from corrosion in the solution. The high corrosion resistance of Al-Mn alloy coating was ascribed to an intact and stable passive film formed on the coating. The performances of the passive film on Al-Mn alloy were further investigated by Mott-Schottky curve and X-ray photoelectron spectroscopy (XPS) analysis. It was ...

International Nuclear Information System (INIS)

We present a comprehensive, up-to-date compilation of band parameters for the technologically important III - V zinc blende and wurtzite compound semiconductors: GaAs, GaSb, GaP, GaN, AlAs, AlSb, AlP, AlN, InAs, InSb, InP, and InN, along with their ternary and quaternary alloys. Based on a review of the existing literature, complete and consistent parameter sets are given for all materials. Emphasizing the quantities required for band structure calculations, we tabulate the direct and indirect energy gaps, spin-orbit, and crystal-field splittings, alloy bowing parameters, effective masses for electrons, heavy, light, and split-off holes, Luttinger parameters, interband momentum matrix elements, and deformation potentials, including temperature and alloy-composition dependences where available. Heterostructure band offsets are also given, on an absolute scale that allows any material to be aligned ...

Energy Technology Data Exchange (ETDEWEB)

The effect of alloying Sn, Pb, As, Sb and P on the dezincification of commercial brass 60Cu-39Zn-1Pb has been investigated in 1% CuCl{sub 2} solution by immersion studies and electrochemical measurements. Specimens with a smooth surface finish exhibited more resistance to dezincification. Appreciable inhibitive effect on dezincification was observed for the 55Cu-40Zn-3Pb-2Sn brass composition. The galvanic coupling of lead phase with the matrix accelerated corrosion. To improve the dezincification resistance of the Sn containing brass, As, Sb and P were added at two different levels (0.05% and 0.1%). Brass of composition 48.95Cu-45Zn-5Pb-1Sn-0.05As was more resistant indicating the synergistic effect of Sn and As. The effect of 0.05 and 0.1% of arsenic addition with various concentrations of zinc was also studied. The alloy of composition 57.90Cu-40Zn-2Pb-0.1As showed better corrosion resistance than the ...

Energy Technology Data Exchange (ETDEWEB)

Grain refinement behavior of copper alloys cast in permanent molds was investigated. This is one of the least studied subjects in copper alloy castings. Grain refinement is not widely practiced for leaded copper alloys cast in sand molds. Aluminum bronzes and high strength yellow brasses, cast in sand and permanent molds, were usually fine grained due to the presence of more than 2% iron. Grain refinement of the most common permanent mold casting alloys, leaded yellow brass and its lead-free replacement EnviroBrass III, is not universally accepted due to the perceived problem of hard spots in finished castings and for the same reason these alloys contain very low amounts of iron. The yellow brasses and Cu-Si alloys are gaining popularity in North America due to their low lead content and amenability for permanent mold casting. These alloys ...

Energy Technology Data Exchange (ETDEWEB)

Field corrosion tests were conducted on eight single tube materials and two welded overlay materials in three typical Japanese waste incineration plants in an effort to develop new corrosion-resistant superheater tubes capable of functioning efficiently under temperature and pressure conditions of 500 C and 100 kgf/cm{sup 2}-g in high-efficiency waste-to-energy (WTE) plants. Austenitic alloys containing higher concentrations of chromium, nickel, and molybdenum [Cr + Ni + Mo] showed excellent corrosion-resistant properties, and the new alloys JHN24 and HR30M showed good corrosion resistance. Different corrosion rates found in each of the three plants were explained by differences in operating conditions, such as gas temperature, concentration of molten salts resulting from chlorine (Cl) content of deposits, heavy metal (zinc oxide [ZnO] + lead oxide [PbO]) content, etc. It was confirmed that the corrosion rate of materials ...

Energy Technology Data Exchange (ETDEWEB)

Fe{sub x}Zn{sub 1-x} alloys were electrochemically deposited on aluminum substrates from a sulfate bath. The K{beta}/K{alpha} x-ray intensity ratios of Zn and Fe in Fe{sub x}Zn{sub 1-x} thin films have been experimentally studied. The energy dispersive x-ray fluorescence (EDXRF) technique was used to measure K x-ray photons. Samples were excited by using 59.5 keV photons emitted by a 50 mCi {sup 241}Am radioactive source. The emitted K x-rays were detected by an Ultra-LEGe detector having a resolution of 150 eV at 5.9 keV. In addition, the effect of bath composition on the phase structure was investigated by x-ray diffraction (XRD) analysis. The composition of the thin films was analyzed by atomic absorption spectrometry analysis. Iron content was shown to strongly affect the structure of Zn-Fe alloys. It was found that the K-shell x-ray intensity ratio changed in Fe{sub x}Zn{sub 1-x} thin films for different values of x. The reason for this ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes a new idea for zinc-air battery design. The novel idea is a porous zinc electrode surrounded with a supersaturated zincate solution. 3 figs. (JDH)

Energy Technology Data Exchange (ETDEWEB)

For the development of a long-lived, electrically rechargeable zinc-air battery the structure and wettability of pasted zinc electrodes were optimized. Pasted zinc electrodes containing 1 to 10% cellulose, but having almost the same nominal capacities, were prepared and tested in zinc/oxygen cells. The effect of discharge rate on cell voltage and delivered capacity, as well as the maximum power, were measured. Furthermore, cell charge-discharge behaviour and cycle life were examined. After different times of operation, the porosity and the pore size distribution of the pasted zinc electrodes were measured by means of mercury porosimetry. The life cycle and peak power drain capability of the Zn/oxygen battery could be substantially improved by the addition of 10 wt% cellulose to the pasted zinc electrode. (author)

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The zinc-air battery/fuel cell is an old technology invented one hundred years ago. However, there is renewed interest in this technology in response to the growing need for clean energy technology. The zinc-air battery/fuel cell is more attractive than similar technologies because its characteristics include high power density, safe operation and storage, and low cost. Zinc-air battery/fuel cells can be made in milliwatts to mega watts to accommodate different applications. The zinc-air battery/fuel cell has four major designs, namely primary, mechanically rechargeable, continuous feed and electrically rechargeable zinc-air battery/fuel cells. Among the different designs, the most common is the air cathode. There are 3 generations of catalysts used in the air cathodes. This paper discussed the different designs of the zinc-air battery/fuel cell, and more ...

Energy Technology Data Exchange (ETDEWEB)

This report summarizes the results of research conducted during the sixteen month continuation of a program to develop rechargeable zinc-air batteries for electric vehicles. The zinc-air technology under development incorporates a metal foam substrate for the zinc electrode, with flow of electrolyte through the foam during battery operation. In this soluble'' zinc electrode the zincate discharge product dissolves completely in the electrolyte stream. Cycle testing at Lawrence Berkeley Laboratory, where the electrode was invented, and at MATSI showed that this approach avoids the zinc electrode shape change phenomenon. Further, electrolyte flow has been shown to be necessary to achieve significant cycle life (> 25 cycles) in this open system. Without it, water loss through the oxygen electrode results in high-resistance failure of the cell. The Phase I program, ...

Energy Technology Data Exchange (ETDEWEB)

The authors report a novel configuration for a zinc-particle, packed-bed anode in which an open structure of high hydraulic permeability is maintained indefinitely in a cell with closely spaced walls by the formation of particle bridges and associated gaps. The configuration minimizes electrolyte pumping costs, allows rapid refueling and partial recharge, and provides for 100% zinc consumption. This approach benefits zinc/air fuel batteries by allowing nearly continuous operation and fuel recycle without commercial infrastructure; it benefits Zn/[Fe(CN){sub 6}]{sup {minus}3} batteries by eliminating shape-change and polarization problems found with planar anodes.

Energy Technology Data Exchange (ETDEWEB)

The formation of ZnTe films was investigated on zinc substrates at 640 K by using the following ion exchange and chemical reaction processes,2Zn{sub (substrate)}+Te{sup 4+}{sub (inmoltensalts)}->2Zn{sup 2+}+Te{sub (onsubstrate)}Zn{sub (substrate)}+Te= {sub (onsubstrate)}-> ZnTe{sub (onsubstrate)}The Te{sup 4+} species was supplied to the substrate via the gas phase, vaporized from the eutectic LiCl-KCl molten salt containing TeCl{sub 4} (0.05-0.9 mol%). The phase of the films obtained depended on the reaction time and the TeCl{sub 4} content in the molten chloride. At low TeCl{sub 4} concentrations, ZnTe alloy was not formed over the entire surface even after 3.6 ks. On the other hand, at high TeCl{sub 4} concentrations, tellurium was detected in addition to the ZnTe compound during the first 0.3 ks of the reaction. By selecting appropriate TeCl{sub 4} concentrations and reaction times, a ZnTe film with a smooth, dense surface was ...

Scientific Electronic Library Online (English)

Abstract in english The rate of copper II/zinc cementation from copper sulphate solutions in the absence and in the presence of methanol (CH3OH) and dimethyl sulphoxide (DMSO) has been studied and the reaction was found to follow first-order kinetics. The influence of several parameters on the course of the reaction, such as cylinder rotation speed, initial concentration of Cu2+ ions, temperature and concentration of organic solvent, was investigated. In the case of CH3OH, rotating zinc cyli (more) nder was used, while in the presence of DMSO stationary zinc sheet and rotating zinc cylinder were used. It was found that (1) the percentage inhibition caused by methanol ranged from 10.70 to 58.38 depending on the concentration of the alcohol used; (2) the rate of cementation in the presence of DMSO using rotating zinc cylinder > the rate of cementation in the presence of DMSO using ...

Energy Technology Data Exchange (ETDEWEB)

For the development of a rechargeable zinc/air battery, La[sub 0.6]Ca[sub 0.4]CoO[sub 3]-catalyzed (perovskite) bifunctional oxygen electrodes and pasted zinc electrodes were prepared and tested in monopolar zinc/air cells. In addition, a bipolar Zn/air stack was tested using reticulated copper foam as substrate for the zinc deposit. The cells were cycled in moderately alkaline ZnO-saturated electrolyte with KF as an electrolyte additive. The maximum power as well as the cycle life of the cells was investigated. The differences in porosity of the zinc electrode before and after the long-term test were analyzed using mercury porosimetry. (author) 8 figs., 13 refs.

International Nuclear Information System (INIS)

By using a model dielectric matrix in electron self-energy evaluations the computational effort of a quasiparticle band-structure calculation for a semiconductor is greatly reduced. Applications to various systems with or without inversion symmetry, having narrow or wide band gaps, and semiconductor alloys demonstrate the reliability and accuracy of the method. Calculations have been performed for thirteen semiconducting or insulating materials: Si, LiCl, AlP, AlAs, AlSb, GaP, GaAs, GaSb, InP, InAs, InSb, and the Al_0_._5Ga_0_._5As and In_0_._5_3Ga_0_._4_7As alloys. Excellent agreement with experimental results is obtained for the quasiparticle energies for these materials. The only three exceptions, E(#GAMMA#_1_c) of AlP, E(L_1_c) of AlAs, and E(L_1_c) of AlSb are discussed and attributed to various experimental uncertainties. Several other quasiparticle-excitation-related properties are also examined in this work. The many-body corrections to ...

Energy Technology Data Exchange (ETDEWEB)

With specific energy of more than 200 Wh/kg, the Electric Fuel zinc-air battery delivers as much as eight times the energy of lead-acid traction battery, more than twice the energy of the nearest advanced-battery competitor, and as much energy as a tank of gasoline. (author)

UK PubMed Central (United Kingdom)

BackgroundZhx1 to 3 (zinc-fingers and homeoboxes) form a set of paralogous genes encoding multi-domain proteins. ZHX proteins consist of two zinc fingers followed...Full Text Available

UK PubMed Central (United Kingdom)

Objective: To evaluate effects of epigallocatechin-3-gallate (EGCG) on the viability, membrane properties, and zinc distribution, with and without the presence of Zn²⁺, in human prostate...Full Text Available

UK PubMed Central (United Kingdom)

Zinc modulates the activity of glutamic acid decarboxylase, the rate limiting enzyme in the synthesis of gamma-aminobutyric acid (GABA), which is a major inhibitory neurotransmitter. Low cerebrospinal...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

We report tests of a refuelable zinc/air battery of modular, bipolar-cell design, intended for fleet electric busses and vans. The stack consists of twelve 250-cm{sup 2} cells built of two units: (1) a copper-clad glass-reinforced epoxy board supporting anode and cathode current collectors, and (2) polymer frame providing for air- and electrolyte distribution and zinc fuel storage. The stack was refueled in 4 min. by a hydraulic transfer of zinc particles entrained in solution flow.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

For the development of a rechargeable zinc/air battery, La{sub 0.6}Ca{sub 0.4}CoO{sub 3}-catalyzed (perovskite) bifunctional oxygen electrodes and pasted zinc electrodes were prepared and tested in monopolar zinc/air cells. The cells were cycled in moderately alkaline electrolyte. The maximum power as well as the cycle life of the cells were investigated. Up to 450 cycles could be reached, and attractive specific energies and powers were obtained. (author) 3 figs., 4 refs.

International Nuclear Information System (INIS)

The paper reports the recovery of zinc and cadmium following 6.1 MeV alpha particle irradiation at 4.2 K as studied by means of electrical reistivity measurements. Specimens of 10 #mu#m thick have been used in order to obtain a homogeneous defect distribution over the whole thickness of the specimen. The pre-irradiation resistivity ratios were 700 and 750 for cadmium and zinc, respectively. (Auth.).

British Library Electronic Table of Contents (United Kingdom)

Water and soil samples from the area were therefore analyzed for their lead and zinc content. Computation of pollution statuses of lead and zinc revealed topsoil lead geoaccumulation indices of ?0.143 and ?0.069 and zinc geoaccumulation indices of 1.168 and 0.713 for Ishiagu and Uburu respectively. The pollution indices were determined to be 0.499 and 0.3564 for soil in Ishiagu and Uburu respectively and also 5.11 and 2.42 for water in Ishiagu and Uburu communities respectively. Water/soil concentration ratio were found to be 0.0018 and 0.0014 for lead in Ishiagu and Uburu respectively. On the other hand, the water/soil concentration ratio for zinc was computed to be 0.001 and 0.0008 for Ishiagu and Uburu respectively. These results seem to suggest that the pollution of the environment by ...

International Science & Technology Center (ISTC)

The New Titanium Alloys With Increased Mechanical Properties and Corrosion Resistance for Medical Instruments and their Coatings

CERN Document Server

Metals and alloy - Atmospheric corrosion testing

Energy Technology Data Exchange (ETDEWEB)

This document reports the progress and accomplishments of a 16 month program to develop a rechargeable zinc-air battery for electric vehicle propulsion, from October 1988 through January 1990. The program was the first stage in the transition of alkaline zinc electrode technology, invented at Lawrence Berkeley Laboratory, to private industry. The LBL invention teaches the use of a copper metal foam substrate for the zinc electrode, in combination with forced convection of electrolyte through the foam during battery operation. Research at LBL showed promise that this approach would avoid shape change (densification and dendrite growth), the primary failure mode of this electrode. The program comprised five tasks; (1) cell design, (2) capacity maximization, (3) cycle testing, (4) materials qualification, and (5) a cost/design study. The cell design contemplates a plate and frame stack, with alternating ...

International Nuclear Information System (INIS)

X-ray fluorescence analysis was used to determine the zinc content of the ''Perilacin'' powder and the ZnO content of the ''Epiderman-pix'' powder. The characteristic Ksub(#alpha#) line of zinc was excited using a "1"4"7Pm/Mo source (10"7 s"-"1) and the molybdenum Ksub(#alpha#) line (17.47 keV). 4 to 5% Zn and 45 to 49% ZnO were determined with a NaI(Tl) scintillation detector. The radiation intensity was found to decrease with particle size. (M.K.).

Energy Technology Data Exchange (ETDEWEB)

A numerical model has been developed to simulate the charging and discharge behaviour of an electrically rechargeable alkaline zinc-air battery. Further a galvanostatic experiment including three charge/discharge cycles has been performed. The cell voltages, the Zn electrode potentials versus a Zn reference, and the O{sub 2} electrode potentials versus a Zn reference calculated with the model are in fairly good agreement with the corresponding experimental data. The model is expected to be useful for zinc-air battery design and for analysis of experimental data. (author)

Energy Technology Data Exchange (ETDEWEB)

This report is an examination and analysis of the zinc-air system as the motive power source for electric vehicle propulsion. Various versions of the zinc-air system and operating schemes along with their advantages and disadvantages are discussed. Baseline cost calculations are also presented in order to compare the cost effectiveness of each of the systems. The treatise is conceptual in nature and is not based on new experimental work. The information is based on published literature and investigations carried out at ERC in the past. The study also includes recommendations and suggestions in areas that require further research and development work to achieve a smooth transition from the conceptual stage to a practical, viable, and cost effective system.

British Library Electronic Table of Contents (United Kingdom)

Abstract BACKGROUND: In Brazil, the usual forms of zinc (Zn) supply to coffee plants have limitations that compromise the element availability to the plant. This study proposes to test an alternative approach to supplying the nutrient to Coffea arabica L. using trunk implanted zinc tablets. Additionally, the effect of Zn on the production and quality of coffee beans was also evaluated. RESULTS: The highest total coffee bean production was recorded in plants implanted with Zn tablets (TA), while the lowest was recorded in the control treatment, without zinc supply (WZn), reaching a bianual production of 188.2 and 130.1 60-kg bags of processed beans per hectare, respectively. In the treatments where Zn were applied as tablet implantation or as foliage spraying (SZn); the bean size was larger...

International Nuclear Information System (INIS)

The dithiocarbamate and thiuram compounds, including disulfiram, were compared for their efficacies in influencing tissue distribution of a trace dose of intravenously injected lead plus "2"0"3Pb in rats. The tested compounds were sodium diethyldithiocarbamate (DEDTC), sodium dimethyldithiocarbamate (DMDTC), tetraethylthiuram disulfide (disulfiram), a complex of zinc and manganese ethylenebisdithiocarbamate (mancozeb), manganese ethylenebisdithiocarbamate (maneb), sodium monomethyldithiocarbamate (metham), zinc propylene bisdithiocarbamate (propineb), tetramethylthiuram disulfide (thiram), zinc ethylenebisdithiocarbamate (zineb), and zinc dimethyldithiocarbamate (ziram). The results of this study show that interactions can occur between lead and DEDTC, DMDTC, disulfiram, metham, thiram, and ziram, resulting in increased levels of lead in brain and probably potentiation of the neurotoxic effects of lead.

Energy Technology Data Exchange (ETDEWEB)

An investigation was conducted into alternative techniques for zinc and electrolyte regeneration and reuse in the refuelable zinc/air battery that was developed by LLNL and previously tested on a moving electric bus using cut wire. Mossy zinc was electrodeposited onto a bipolar array of inclined Ni plates with an energy consumption of 1.8 kWh/kg. Using a H{sub 2}-depolarized anode, zinc was deposited at 0.6 V (0.8 kA/m{sup 2}); the open circuit voltage was 0.45 V. Three types of fuel pellets were tested and compared with results for 0.75 mm cut wire: spheres produced in a spouted bed (UCB); coarse powder produced by gas-atomization (Noranda); and irregular pellets produced by chopping 1-mm plates of compacted zinc fines (Eagle-Picher, Inc.). All three types transported within the cell. The coarse powder fed continuously from hopper to cell, as did the compacted pellets (< ...

Science.gov (United States)

... MOLYBDENUM ALLOY GUN BARREL LINERS o0 in ... NEW POWDER TECHNOLOGIES FOR MOLYBDENUM ALLOY GUN BARREL LINERS ...

International Nuclear Information System (INIS)

... filters molybdenum alloys production sulfuric acid alloys chemical reactions ...

Wastenet

... Zinc-carbon/air and alkaline-manganese batteries can be reprocessed using a number of different methods, which include smelting and other thermal-metallurgical processes to ... Citron in France - thermal-metallurgical reprocessing primarily of zinc-carbon/air and alkaline-manganese (including older ones containing mercury), but also NiMH, ...

UK PubMed Central (United Kingdom)

Zinc tetraaminophthalocyanine-Fe₃O₄ nanoparticle composites were prepared by organic-inorganic complex technology and characterized. It has been proved that the ZnTAPc dispersed...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Prior to an industrial-scale test of zinc/air batteries at Greven, the TUeV Bayern-Sachsen carried out preliminary tests on behalf of the Deutsche Bundespost. The results were quite promising: The energy density of the new battery is ten times as high as that of conventional lead batteries, and the battery-powered test vehicle had a range of up to 300 km. (orig.)

Energy Technology Data Exchange (ETDEWEB)

A zinc-air battery in a case is described including a zinc particle bed supported adjacent the current feeder and diaphragm on a porous support plate which holds the particles but passes electrolyte solution. Electrolyte is recycled through a conduit between the support plate and top of the bed by convective forces created by a density of differential caused by a higher concentration of high density discharge products in the interstices of the bed than in the electrolyte recycle conduit. 7 figures.

International Nuclear Information System (INIS)

Defects are produced in zinc by 6.1 MeV #alpha#-particle irradiation at 4.2 K and the subsequent recovery between 4.2 and 22 K. No evidence is found for free migration of an interstitial in the temperature range investigated. The recovery spectra reveal a series of substages which are ascribed to recombination of close Frenkel pairs. (author).

International Nuclear Information System (INIS)

Results of hot cracking on welds with compositions between alloy 800 and AWS ER NiCr 3. Investigation of the influence of Si, Mn, Ti and Al on the hot cracking suscpetibility of the alloy 800. (orig.).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

Alloys are described which contain nickel, aluminum, boron, iron and in some instances manganese, niobium and titanium.

Energy Technology Data Exchange (ETDEWEB)

Due to the well-establish corrosion problems of Alloy 600 as a steam-generator material and the subsequent focus on thermally treated (TT) Alloy 690 and Alloy 800 as alternative materials, a systematic analysis of the corrosion behavior of these two latter alloys is warranted. Corrosion test results for Alloys 690 TT and 800 were collected and organized in the form of corrosion mode diagrams. Selected data for mill annealed (MA) Alloy 600 were also included for reference. The corrosion mode diagrams correlate the modes of corrosion degradation observed in tests as functions of the environment pH and electrochemical potential (ECP). The diagrams confirm that Alloys 690TT shows some susceptibility in caustic environments, and Alloy 800 shows susceptibility in both caustic and highly acidic environments. (authors). 6 figs., ...

Energy Technology Data Exchange (ETDEWEB)

A new method for the separation and determination of trace amounts of cadmium and zinc in water as their thenoyltrifluoroacetone (TTA) complexes with dibenzo-18-crown-6 (DB18C6) in o-dichlorobenzene has been established by means of synergistic extraction and back-extraction combined with atomic absorption spectrometry. The effect of various factors (synergism with TTA and DB18C6, shaking time, composition of the extracted species, and mutual separation etc.) on the extraction and back-extraction of cadmium and zinc has been in- vestigated. When the mixtures were extracted for 4 min at pH 4.9, only zinc was extracted quantitatively, whereas cadmium remained in the aqueous phase. After the phases were separated, cadmium was again extracted quantitatively at pH 7.5. Then, the two phases were each shaken with 0.05-0.1 mol/l HCl in order to back-extract cadmium and zinc from the organic phases; the ions were ...

Energy Technology Data Exchange (ETDEWEB)

We prepared cathodes with various types of activated carbon and measured the cathodes' electrochemical performance according to the kind of activated carbon. Activated carbon supplies airflow channels and reaction sites in the cathode of zinc air batteries. When we use activated carbon with a high specific surface area as the cathode's catalyst substrate, we expect high electrochemical performance because this type of carbon provides more air flow channels and reaction sites. We focused on investigating the relationship between the cathode's pore structure and its electrochemical characterizations. We also studied the effects of the various activated carbon materials on the zinc air batteries' performance. Increasing the macropores or mesopores in the activated carbon resulted in achieving more power from the battery. (author)

Energy Technology Data Exchange (ETDEWEB)

The biosorption of lead, copper and zinc ions on Rhizopus arrhizus has been studied for three single-component and two binary systems. The equilibrium data have been analysed using the Freundlich adsorption model. The characteristic parameters for the Freundlich adsorption model have been determined and the competition coefficients for the competitive biosorption of Pb(II)-Cu(II) at pH 4.0 and 5.0, and Pb(II)-Zn(II) at pH 5.0 have been calcualted. For the individual single-component isotherms, lead has the highest biosorption capacity followed by copper, then zinc. The capacity of lead in the two binary systems is always significantly greater than those of the other metal ions, in agreement with the single-component data. Only a partial selectivity for copper ions has been obtained at pH 4.0. (orig.)

International Nuclear Information System (INIS)

The low cycle fatigue testing was carried out to provide a basis for comparison of the behavior of the two kinds of Alloy 800 (low carbon Alloy 800 and high carbon Alloy 800H). The testing was done at temperatures of 500"0C and 650"0C either with or without hold. The results obtained were as follows: (1) At 650"0C, the low-cycle fatigue life was essentially the same for the two alloys on the basis of strain amplitude, but Alloy 800H had a longer life on the basis of stress amplitude. (2) At 500"0C, the two alloys exhibited longer lives than at 650"0C, with Alloy 800 exhibiting 2-3 times longer life than Alloy 800H when compared on the basis of plastic strain range. At this temperature the stress range showed the maximum for Alloy 800H. (3) When a creep effect was introduced either by way of a hold ...

UK PubMed Central (United Kingdom)

BackgroundChanges in ionic concentration have a fundamental effect on numerous physiological processes. For example, IP₃-gated thapsigargin sensitive intracellular calcium...Full Text Available

UK PubMed Central (United Kingdom)

The development of new methods for gene addition to mammalian genomes is necessary to overcome the limitations of conventional genetic engineering strategies. Although a variety of DNA-modifying enzymes...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The human zinc finger protein genes (ZFX/Y) were identified as a result of a systematic search for the testis-determining factor gene on the human Y chromosome. Although they play no direct role in sex determination, they are of particular interest because they are highly conserved among mammals, birds, and amphibians and because, in eutherian mammals at least, they have active alleles on both the X and the Y chromosomes outside the pseudoautosomal region. We used in situ hybridization to localize the homologues of the zinc finger protein gene to chromosome 1 of the Australian echidna and to an equivalent position on chromosomes 1 and 2 of the playtpus. The localization to platypus chromosome 1 was confirmed by Southern analysis of a Chinese hamster [times] platypus cell hybrid retaining most of platypus chromosome 1. This localization is consistent with the cytological homology of chromosome 1 between the two species. The ...

International Nuclear Information System (INIS)

Radionuclide X-ray fluorescence analysis was used for the determination of iron, calcium, potassium, copper, manganese and zinc in waste water from the production process of citric acid. (author).

UK PubMed Central (United Kingdom)

BackgroundThe zinc-finger transcription factor GLI3 is an important mediator of Sonic hedgehog signaling and crucial for patterning of many aspects of the vertebrate body plan. In...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The technical feasibility of the solar carbothermal reduction of ZnO has been successfully demonstrated in a pilot plant. The economics of this process is addressed by means of a single sensitivity analysis and a Monte-Carlo risk analysis. A medium-term and a long-term scenario have been investigated, each for a 5 and a 30 MW{sub th} plant. For a discount rate of 15% the zinc production costs vary between 482 and 245 $/t for the medium-term scenario and between 312 and 146 $/t for the long-term scenario, respectively. These costs do not account for the zinc oxide input material. In addition, a risk analysis was conducted for the 30 MW{sub th} long-term scenario. For each input parameter, a probability distribution was estimated and the probability distribution of the zinc production cost was calculated by means of a Monte-Carlo method. The expected mean zinc production costs vary from 95 $/t for a ...

Science.gov (United States)

At the St. Joe Minerals Corp.'s zinc smelter powerplant, an SO2 emission control program evolved into a cooperative program with the Bureau of Mines for installation and initial operation of a citrate process flue gas desulfurization demonstration plant. ...

Science.gov (United States)

Carbon steel, copper, zinc and aluminium samples were exposed in different sizes with known ambient parameters in Gran Canaria Island and atmospheric corrosion was investigated. Weight-loss measurements used to determine corrosion damage were complemented...

UK PubMed Central (United Kingdom)

Leaf senescence is a developmentally programmed degeneration process, which is fine tuned by a complex regulatory network for plant fitness. However, molecular regulation of leaf senescence is poorly...Full Text Available

International Nuclear Information System (INIS)

The following methods of quartz ceramics alloying were considered: alloying of initial quartz glass; introduction of alloying additive into water slip of quartz glass; porous materials impregnation with salt aqueous solutions and subsequent salt thermal decomposition with formation of stable oxides in pores of ceramics. Oxygen free compounds BN, SiB_4, SiC, Si_3N_4, REM oxides and transition metal oxides were used as alloying additives. Main properties of the materials and compositions obtained are presented.

Energy Technology Data Exchange (ETDEWEB)

The processing characteristics, tensile properties, and oxidation response of two Nb-Ti-Al-Cr alloys were investigated. One creep tests at 650{degrees}C and 172 MPa was conducted on the base alloy which contained 40Nb-40-Ti-10Al-10Cr. A second alloy was modified with 0.11 at. % carbon and 0.07 at. % yttrium. Alloys were arc melted in a chamber backfilled with argon, drop cast into a water-cooled copper mold, and cold rolled to obtain a 0.8-mm sheet. The sheet was annealed at 1100{degrees}C for 0.5 h. Longitudinal tensile specimens and oxidation specimens were obtained for both the base alloy and the modified alloy. Tensile properties were obtained for the base alloy at room temperature, 400, 600, 700, 800, 900, and 1000{degrees}C, and for the modified alloy at room temperature, 400, 600, 700, and 800{degrees}C. Oxidation ...

International Nuclear Information System (INIS)

Investigated are the characteristics of high-temperature plastic deformation the velocity sensitivity of flow stresses, deformation curves, flow stresses, deformation before rupture - as well as the structure of beryllium alloys containing nickel (0.5-4 %), yttrium (0.5-2 %) and aluminium (38 %). The alloys containing nickel (2%) and yttrium (0.5 %) are superplastic, however, deformation before fracture of the alloys is lower than that of the unalloyed beryllium. The singularities of high-temperature plastic flow of the alloys and the causes of deterioration of their plasticity are determined.

Energy Technology Data Exchange (ETDEWEB)

Since 1991, secondary side cracking has become a major concern in EDF steam generators. At 350 C, IGSCC of Alloy 600 was found in pure NaOH solutions from 4 to 500 g/l, with a maximum at 100 g/l. From the present results and available data, IGSCC of Alloy 690 occurred in pure NaOH solutions from 40 to 500 g/l, but the greatest sensitivity was observed at 100 g/l. TG/IGSCC of Alloy 800 became more severe with increasing NaOH solutions, from 10 to 500 g/l. On the whole, the ranking for SCC-resistance was Alloy 600 < Alloy 800 < Alloy 690. A significant improvement was still obtained with 690TT with intergranular carbides (industrial tubes) and perhaps with Alloy 800 NG (nuclear grade), but both alloys cracked at the highest stresses. IGSCC susceptibility of Alloy 600 MA was higher for the tubes ...

Energy Technology Data Exchange (ETDEWEB)

A rechargeable cell is disclosed which is characterized in the following manner. A positive electrode is formed from a manganese oxide electrode material. This manganese oxide electrode material contains a heavy metal selected from the group comprising lead, bismuth, and mixtures of lead and bismuth. The cell also contains a negative electrode of zinc. A separator is provided between the positive electrode and the negative electrode. An alkaline electrolyte consisting essentially of an alcohol and an alkaline hydroxide is also contained in the rechargeable cell in contact with both the positive electrode and the negative electrode.

International Nuclear Information System (INIS)

A theoretical study of structural and electronic properties of GeC, SnC and GeSn is presented using the full potential linearized augmented plane wave method. In this approach, the generalized gradient approximation was used for the exchange-correlation potential. Results are given for lattice constant, bulk modulus and its pressure derivative in both zinc-blende and rocksalt structures. Band structure, density of states and band gap pressure coefficients in zinc-blende structure are also given. The results are compared with previous calculations and with experimental measurements.

Energy Technology Data Exchange (ETDEWEB)

The electrolyte was brought into contact with air and potassium carbonate was measured with various contact time in order to check the defect of carbon dioxide in the air on zinc-air cell. The relationship between potassium carbonate concentration in electrolyte and battery capacity was also studied. The potassium carbonate concentration in the electrolyte. The rate of carbon dioxide absorption was mainly affected by the pore size of hydrophobic membrane. Our study showed that adapting the pore of hydrophobic membrane decreased the loss of cell discharge performance due to the presence of carbon dioxide or water vapor in the atmosphere. 7 refs., 12 figs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

A small scale biomass metal contacting experiment was performed to screen the optimal plant species for biosorption and bioaccumulation of cadmium, zinc, nickel, lead, and copper. Experiments were also conducted to test the ability of the biomass to lower the metal concentrations below the US Environmental Protection Agency surface water discharge criteria. The minimum residual concentration was 0.1 mg/L for zinc, 0.004 mg/L for lead, and about 0.01 mg/L for cadmium, nickel, and lead. Results indicate that water milfoil can be used for bioremoval of metals.

International Nuclear Information System (INIS)

By means of an audio frequency plasma polymerisation ultra-thin gradient plasma polymer layers were deposited on zinc and zinc-coated iron. The aim was to generate an interfacial polymeric layer which bonds to an oxidised metal as well as to a subsequently applied organic coating and acts as an interfacial barrier layer for ions and water. Surface modifications were done in an in situ plasma cell with infrared reflection absorption spectroscopy (IRRAS). The zinc surface was first activated by an oxygen plasma to provide a freshly oxidised and contamination free oxide surface. The intermediate stages of the surface reactions could be revealed. Carbon dioxide molecules as oxidation products adsorbed on the growing zinc oxide and were desorbed at a later stage. An organosilicon plasma polymer was deposited directly on top of the oxide layer from a hexamethyldisilane (HMDS) plasma. Afterwards a cyclohexene ...

International Nuclear Information System (INIS)

Three model boilers, manufactured to simulate full-size tube sheet crevices, were tested with various secondary side environments. The first was faulted with organics representative of the decomposition of humic acid. The second was faulted with sodium carbonate and sodium hydroxide, while the third was faulted with sodium sulfate and sodium hydroxide. Each model contained seven tubes, which included Alloy 600 in the mill-annealed (MA) and thermally-treated (TT) conditions and Alloy 690 in the thermally-treated condition. Two models contained Alloy 800 tubes in the mill-annealed condition and one had Alloy 800 in the mill-annealed/cold-worked/glass-bead-peened condition. Two different sizes of tubesheet crevices were used in all model boilers. In the organics-faulted boiler, tubes of Alloy 600MA, Alloy 690TT and Alloy 800MA experienced no ...

Energy Technology Data Exchange (ETDEWEB)

AZ31 and experimental ZMA611 alloys were strip cast into 2 mm thick strips. The as-cast AZ31 alloy strip consists of columnar dendrites. On the other hand, as-cast ZMA611 alloy strip shows equiaxed dendritic structure through the thickness of strip. These alloys were subjected to various thermomechanical treatments and their tensile properties were evaluated. Strip cast AZ31 alloy in H24 condition has equivalent yield and tensile strengths with similar ductility compared to commercial ingot cast AZ31-H24 alloy, indicating that strip casting is a viable process for the fabrication of Mg alloy strips. The ZMA611 alloy has a large volume fraction of fine dispersoid particles in the microstructure, resulting from the beneficial effect of strip casting on microstructural refinement. It has been shown that the ZMA611 ...

Energy Technology Data Exchange (ETDEWEB)

Resistance of ALLOY 800 as a PWR/SG tubings to IGC/IGSCC and Ni, Co release into high temperature water was evaluated as compared with ALLOYs 600 and 690. The study to improve the resistance to IGSCC and general corrosion was also made. From the results, ALLOY 800 was evaluated to be the most reliable among the high Ni alloys tested. In addition, the alloy would obtain further reliability in IGSCC and general corrosion resistance by the combined addition of Ti and Nb, and the prior oxidation treatments, respectively. (author).

Science.gov (United States)

... Accession Number : ADD151811. Title : Ultra High Strength Beta Titanium Alloy for Fasteners. Descriptive Note : Journal article,. ...

Science.gov (United States)

... Accession Number : ADD109273. Title : THERMAL STABILITY OF ALPHA-BETA TITANIUM ALLOY Ti-5Al-2Cr-1Fe,. Corporate Author : ...

Science.gov (United States)

... by the boron doping in most of the alloys except for Al66Mn9Zr25 + 50 ppm B alloy; permanent deformation at ultimate compressive strength is not ...

International Nuclear Information System (INIS)

The nickel-rich superalloys Alloy 600 and Alloy 800 have been corroded in mildly alkaline deuterated aqueous conditions typical of secondary coolant circuits in a nuclear power station. The oxide films and substrates of these alloys have been analysed by imaging SIMS depth profiling, which makes it possible to describe elemental distribution in all three dimensions. The measurement of the distribution of the secondary ions NiO"-, FeO"- and CrO"- appears useful for detailing the behaviour of nickel, iron and chromium within oxidized phases. The measurement of D"- distribution outlines the extent of oxide hydration. For Alloy 800, evidence of sodium migration into the grain boundaries of the alloy substrate is found. For Alloy 600, no grain boundary sodium ingress can be identified under comparable corrosion conditions. (author).

Energy Technology Data Exchange (ETDEWEB)

Four low activation alloy classes, two austenitic and two ferritic, have been incorporated into the MOTA-1B experiment in the FFTF reactor to provide an early assessment of the suitability of such alloys for reactor service.

International Nuclear Information System (INIS)

The effect of various hydrogen concentrations on the crystal lattice period and the hardness of titanium alloy was examined, the alloy containing about 16 at.% Mo (27.5 wt. % Mo) and having #beta# structure. The peculiar features of the mechanism of plastic deformation of the alloy were studied after adding hydrogen to it. A dependence of the crystal lattice period on the concentration of hydrogen was obtained for TixMoxH_2 alloy. It has been established that the hardness of the Ti-Mo alloy does not change when hydrogen is added to it. The presence of hydrogen introduces changes into the mechanism of deformation of #beta#-titanium alloy. The configuration of the inverse pole figures after rolling proves that the transverse slip process in an alloy with hydrogen is hampered, and that the coplanar slip process is developing in it.

Science.gov (United States)

... CLOSURE DURING HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY (PREPRINT) ... HOT WORKING OF AN ALPHA/BETA TITANIUM ALLOY ...

Science.gov (United States)

... Accession Number : ADD336001. Title : Development of a FeCoNb Alloy to be used in Eddy Current Probes for Testing Ferromagnetic Tubes,. ...

Science.gov (United States)

... Title : DUCTILITY RATIO OF AGED BETA TITANIUM ALLOY. Corporate Author : NEW YORK UNIV NY SCHOOL OF ENGINEERING AND SCIENCE. ...

International Nuclear Information System (INIS)

Stemming from their unique combination of elevated strength, low density, and good overall corrosion resistance, beta titanium alloys have become attractive candidate materials for critical, high-stress, components in corrosive services. An overview of the comparative corrosion resistance of beta alloys to conventional alpha and alpha/beta titanium alloys in common industrial and aerospace service environments generally reveals attractive behavior depending on the environment and alloy composition and, in some cases, alloy condition. Expanded performance windows are especially noted for the molybdenum-rich beta alloys, particularly in regard to resisting reducing acids, stress corrosion, and high temperature localized chloride attack, along with hydrogen and oxidation resistance. Where applicable, implications of this enhanced corrosion performance on current ...

Energy Technology Data Exchange (ETDEWEB)

Whereas supersaturated aluminum alloys demonstrate enhanced passivity, conventional aluminum alloys spontaneously pit in air-saturated chloride solutions. We have concentrated on three areas: evaluation and characterization of Al-W alloys, which exhibit the best corrosion performance of any alloy system studied to date; characterization of the passive-film structure of Al-Mo alloys; and production and characterization of Al-W and Al-Ta powders, which will be used for compaction into bulk material. Surface analysis of the Al-W passive films formed during polarization show surprising little oxidized solute compared to other alloys. These results indicate that the barrier layer formation and electrostatic repulsion mechanisms used to explain the passivity of other alloys are not involved here. Instead the W may act to stabilize the passive film ...

International Nuclear Information System (INIS)

In-reactor testing of bolt-loaded compact tension specimens was performed in 360 C water to determine the irradiation-assisted stress corrosion cracking (IASCC) behavior of HTH Alloy X-750 and direct-aged Alloy 625. New data confirm previous results showing that high irradiation levels reduce SCC resistance in Alloy X-750. Heat-to-heat variability correlates with boron content, with low boron heats showing improved IASCC properties. Alloy 625 is resistant to IASCC, as no cracking was observed in any Alloy 625 specimens. Microstructural, microchemical and deformation studies were performed to characterize the mechanisms responsible for IASCC in Alloy X-750 and the lack of an effect in Alloy 625. The mechanisms under investigation are: boron transmutation effects, radiation-induced changes in microstructure and deformation characteristics, and ...

International Nuclear Information System (INIS)

To clarify the acidic and alkaline Intergranular Stress Corrosion Cracking (IGSCC) mechanism of thermally treated alloy 690 (alloy 690 TT) and shot peened alloy 800 (alloy 800 SP), C-ring tests were conducted in deaerated HCl solutions and in deaerated NaOH solutions at 350degC, compared with the acidic and the alkaline IGSCC susceptibilities of mill-annealed alloy 600 (alloy 600 MA), full-sensitized one (alloy 600 FS) and thermally treated one (alloy 600 TT). Grain boundary characteristics, such as chromium depleted zone and chromium carbide precipitation, were examined using modified Huey test and Transmission Electron Microscopy. Potential-pH diagram for Ni, Cr, Fe-H_2O system at 350degC was constructed and the solubilities of NiO, Cr_2O_3 and Fe_3O_4 were also calculated to evaluate the stability of oxide films which ...

DEFF Research Database (Denmark)

Zinc oxide (ZnO) and alumina (Al2O3) particles are synthesized by the combustion of their volatilized acetylacetonate precursors in a premixed air-methane flame reactor. The particles are characterized by XRD, transmission electron microscopy, scanning mobility particle sizing and by measurement of the BET specific surface area. Pure (?-)alumina particles appear as dendritic aggregates with average mobile diameter 43-93 nm consisting of partly sintered, crystalline primary particles with diameter 7.1-8.8 nm and specific surface area 184-229 m2/g. Pure zinc oxide yields compact, crystalline particles with diameter 25-40 nm and specific surface area 27-43 m2/g. The crystallite size for both oxides, estimated from the XRD line broadening, is comparable to or slightly smaller than the primary particle diameter. The specific surface area increases and the primary particle size decreases with a decreasing flame temperature and a decreasing precursor ...

Energy Technology Data Exchange (ETDEWEB)

A recent road test at LLNL underscored the zinc/air battery`s capacity to give electric vehicles some of the attractive features of gas-driven cars: a 400-km range between refueling, 10-minute refueling, and highway-safe acceleration. Developed at Lawrence Livermore National Laboratory, the battery weights only one-sixth as much as standard lead/acid batteries and occupies one-third the space, yet costs less per mile to operate. What`s more, because the battery is easily refuelable, it promises trouble-free, nearly 24-hour-a-day operation for numerous kinds of electric vehicles, from forklifts to delivery vans and possibly, one day, personal automobiles. The test of a Santa Barbara Municipal Transit bus with a hybrid of zinc/air and lead/acid batteries capped a short development period for the zinc/air battery. The test run indicated the zinc/air battery`s potential savings in vehicle weight from 5.7 to ...

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The investigations carried out on Alloy 800 in aqueous high-temperature environments in France as well as in other countries are reviewed. These studies are mainly concerned with nuclear industry where Alloy 800 can be used as structural material for steam generators of PWR, breeders or HTR. As results referred to in the literature on cracking in caustic environmens do not always agree, a discussion is presented on the matter. The behaviour of Alloy 800 in superheated steam is examined. (Auth.).

International Nuclear Information System (INIS)

(Nov 1973). United States Greenfield, MA Pierce, CM Chicago, IL.

KoreaScience (Korea)

Full Text Available

International Science & Technology Center (ISTC)

Investigation of Destruction Mechanisms in Reactor Steels and Alloys under Cycling Deformation

Energy Technology Data Exchange (ETDEWEB)

Short communication. 6 refs., 2 figs.

Energy Technology Data Exchange (ETDEWEB)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

In the present work, electrochemical measurements and corrosion tests in NaCl solutions were carried out to study the effect of aging treatments on pitting corrosion behavior in a 8090 alloy and its high purity Al-Li binary alloy analogue. The pitting corrosion characteristics and corrosion resistance of the 8090 alloy have been determined in relation to precipitation microstructures. (orig.).

Science.gov (United States)

... THE STRENGTH, TOUGHNESS, AND STRESS-CORROSION CRACKING SUSCEPTIBILITY OF A METASTABLE BETA TITANIUM ALLOY (Ti-11. ...

International Nuclear Information System (INIS)

In this paper a study is made of the structure and mechanical properties of the #beta# alloy system Ti-Mo-Zr-Sn (the composition of which is equivalent to the #beta# III alloy used abroad) containing different amounts of carbon. Study of the #beta#-titanium alloy containing 0.1% C revealed the presence of particles of titanium carbide. Separation of the titanium carbide promotes a reduction in impact strength, an increased tendency toward cold shortness, and poorer workability. (author).

Energy Technology Data Exchange (ETDEWEB)

Magnesium alloys are being increasingly utilized in a variety of fields as an alternative material to organic materials and aluminum alloys, owing to excellent properties. Those include low density, and excellent damping properties. When compared to organic materials, furthermore, Mg alloy excels at recyclability, heat radiation, and electromagnetic-shielding. Though most of magnesium alloy products are manufactured through die-casting and thixo-molding at present, the demand for the expanding of magnesium wrought alloy market is increasing. Taking full advantage of a drawing technique and applying it to the conventional extruded pipe, we have developed a new type of magnesium alloy pipe. The strength of the developed pipe is significantly higher than that of the conventional one, either extruded or die-casting. Some of the excellent properties were obtained ...

Energy Technology Data Exchange (ETDEWEB)

In a work studying the corrosion and tarnishing properties of a variety of copper alloys, the alloy Cu-A110-Sn5 was found to show an excellent corrosion resistance in neutral solutions, where copper and most conventional Cu alloys are covered by thick nonprotective surface layers. The passive films formed on this alloy were characterized with electrochemical and photoelectrochemical methods. The pH dependence of the passivation and of the photocurrent behavior of the Cu-A110-Sn5 alloy clearly indicates that the passivity of this alloy in neutral solutions is due to a formation of passive film enriched with aluminum oxide. At corrosion potential a strong increase in the corrosion resistance with time is due to a gradual enrichment of the surface with aluminum oxide. This can be seen in the photocurrent spectra which change from cooper-type to aluminum-type with ...

Energy Technology Data Exchange (ETDEWEB)

It is hypothesized that the good performance of Alloy 800 in steam generator service is due to its relative immunity to two distinct mechanisms of stress corrosion cracking; the argument also applies to intergranular corrosion. One mechanism operates in the high-nickel region (Alloy 600 and nearby model alloys) and is due to internal intergranular oxidation. The other operates in the low-nickel (stainless steel) region and is due to de-alloying of Fe and/or Cr. This latter mechanism may, under special conditions, operate in high-Ni, high-Cr alloys such as 690. Some essential features of the de-alloying mechanism are demonstrated using strong caustic solutions, and the prospect of extending this approach to dilute high-temperature environments is discussed. (author)

British Library Electronic Table of Contents (United Kingdom)

Statement of problem. The popularity of base metal alloys has considerably increased in recent years because of their superior mechanical properties as well as the high cost of noble alloys. However, there is disagreement about their effect on the opaque porcelain color and the color differences among base metal alloys. Purpose. The purpose of this in vitro study was to determine and compare the influence of various commercially available base metal alloys (excluding titanium-based systems) on the resulting color of opaque porcelain with the use of a colorimetric device. Material and methods. Fourteen different types of Ni-Cr and 3 different types of Co-Cr porcelain bonding alloys were selected with a Au-Pd alloy (V-Delta SF) as the control group for colorimetric measurements and determina...

International Nuclear Information System (INIS)

The threshold stress intensities for stress corrosion crack propagation in beta titanium alloy 38-6-44, Ti3Al-8V-6Cr-4Mo-4Zr, has been determined in salt water and methanolic solutions. The alloy was immune to stress corrosion cracking (SCC) in aqueous sodium chloride solutions (marine atmosphere). However, in methanolic solutions, the alloy was very susceptible to SCC. This marked susceptibility in methanolic solutions can be mitigated by the addition of an inhibitor: sodium nitrate. Crack extension in the alloy was transgranular and failure occurred by brittle quasi-cleavage in methanolic solutions.

International Nuclear Information System (INIS)

By the methods of microstructural and electron-microscopic analyses by the tension test and impact test studied is the effect of quenching conditions on structure and mechanical properties of the TS6 titanium-#beta# alloy. It is shown that low temperature quenching from 700 deg C, recommended earlier for analogous VT15 titanium alloy, leads to appearence of intercrystalline fracture and to sharp decrease of impact strength of the TS6 alloy. Established are optimum conditions for quenching of half-finished products and articles of the TS6 alloy depending on their subsequent working or operation.

International Nuclear Information System (INIS)

Cr_2O_3 scales are found to form on Alloy 800 and a similar pure ternary alloy in air, and 1 and 50 atm. helium containing oxidizing impurities typical of those in an SGHTR. The strong temperature dependence and neglibible helium overpressure dependence indicate that gas transport through the scales is not rate controlling. Surface oxidation rates are therefore controlled by solid state diffusion and the low oxygen partial pressure dependence of the oxidation rate in Alloy 800 is ascribed to the presence of extrinsic defects in the Cr_3O_3 (due to doping by alloying elements) or to the presence of short circuit diffusion paths. (Auth.).

Energy Technology Data Exchange (ETDEWEB)

The initiation and characteristics of mossy zinc electrodeposits have been investigated. Batteries with zinc electrodes are candidates for electric vehicle applications; however, this electrode is prone to form non-compact deposits that contribute to capacity loss and battery failure. Moss is deposited when the current density is far from the limiting current. This morphology first appears only after the bulk deposit is approximately 1 {mu}m thick. In this investigation, the effects of flow rate (Re=0--4000), current density (0--50 mA/cm{sup 2}), concentration of the electroactive species (0.25 and 0.5 M), and the concentration of supporting electrolyte (3, 6, and 12 M) on the initiation of moss were examined. The rotating concentric cylinder electrode was employed for most of the experiments; and a flow channel was used to study the development of morphology. After the experiment, the deposit was characterized using microscopic, x-ray ...

International Nuclear Information System (INIS)

Nano-sized zinc oxide was synthesized and deposited onto cellulosic fibers using the sol-gel process at ambient temperature. The prepared materials were characterized using several techniques including scanning electron microscopy, transmission electron microscopy, diffuse reflectance spectroscopy, X-ray diffraction and thermogravimetric analysis. X-ray diffraction studies of the ZnO-coated fiber indicate formation of the hexagonal crystal phase which was satisfactory crystallized on the fiber surface. The electron micrographs show formation of zinc oxide nanoparticles within 10-15 nm in size which have been homogeneously dispersed on the fiber surface. The prepared materials show significant photocatalytic self-cleaning activity, which was monitored by diffuse reflectance spectroscopy. The photoactivity was studied upon measuring the photodegradation of methylene blue and eosin yellowish under UV-Vis irradiation. The photocatalytic activity of ...

International Nuclear Information System (INIS)

The main aims of the study were: 1) the evaluation of iron and zinc status in women of Lodz aged 18-45 years, 2) adaptation of the whole body counter to in vivo measurements absorption of iron given to the gastro-intestinal tract of volunteers and 3) in rat model estimation iron bioavailability from fortified wheat flour combined with products usually consumed in Poland. During five months investigations thirty seven women were examined each one twice in two months interval. Following variables were measured: iron and zinc in blood serum, in public and scalp hair and in food, taste acuity score, serum ferritin, hemoglobin, total iron binding capacity, red blood cells, mean corpuscular concentration and corpuscular volume. Prevalence of iron deficiency and iron deficient anemia were assessed by two models in terms of the depression of serum ferritin and hemoglobin concentrations. 64 refs, 6 figs, 23 tabs.

Energy Technology Data Exchange (ETDEWEB)

The use of concentrated solar energy for co-producing Zn and synthesis gas from Zn O and natural gas upgrades the calorific value of the initial reactants by 39% and, when compared to the traditional carbothermic reduction of Zn O, has the potential of reducing CO{sub 2} emissions by up to 78%. An economic assessment for an industrial thermochemical plant, 30 to 51 MW solar input, indicates that the cost of solar production of zinc ranges between 89-133 $/t (excluding the cost of Zn O feed and credit for pollution abatement), and thus might be competitive with conventional fossil-fuel-based processes at current fuel prices. The cost of solar H{sub 2}, produced by splitting water with zinc, is estimated to be in the range 0.10-0.14 $/kWh, and it is a favorable long term prospect once the cost of energy will account for the environmental externalities from fossil fuel burning such as the costs for CO{sub 2} mitigation and pollution abatement. ...

Energy Technology Data Exchange (ETDEWEB)

The time-temperature-precipitation diagrams and the resulting time-temperature-sensitization diagrams have been established and are presented for today's current nickel-chromium-molybdenum alloys C-4, C-276, 22 and the recently developed alloy 59. Compared to those materials alloy 625 behaves differently due to its high niobium content. In addition, also the precipitation and sensitization of alloy G-3 has been established. Under the materials considered alloy C-276 has the strongest tendency to precipitate the intermetallics Mu and P together with the carbide M{sub 6}C at intermediate temperatures, followed by the alloys 22 and 59. The tendency to sensitization in the sense of the 50{mu}m (2 mils) intercrystalline penetration criterion when exposed to the ASTM G-28, method A test solution is greatest with alloy C-276, and decreases ...

Energy Technology Data Exchange (ETDEWEB)

In order to investigate the role of amorphous SiO{sub 2} particles in corrosion and wear resistance of Ni-based metal matrix composite alloying layer, the amorphous nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer has been prepared by double glow plasma alloying on AISI 316L stainless steel surface, where Ni/amorphous nano-SiO{sub 2} was firstly predeposited by brush plating. The composition and microstructure of the nano-SiO{sub 2} particles reinforced Ni-based composite alloying layer were analyzed by using SEM, TEM and XRD. The results indicated that the composite alloying layer consisted of {gamma}-phase and amorphous nano-SiO{sub 2} particles, and under alloying temperature (1000 deg. C) condition, the nano-SiO{sub 2} particles were uniformly distributed in the alloying layer and still kept the amorphous structure. ...

Energy Technology Data Exchange (ETDEWEB)

Elevation of zinc protoporphyrin (ZPP) levels in the blood has served as an indicator of lead poisoning and iron deficiency anemia for many years. We have discovered that sublethal doses of whole body irradiation with x-rays also elevates ZPP 2-3-fold over normal levels. The ZPP level does not begin to increase until days 12-14 postirradiation and peaks between days 18 and 20 before returning to normal levels between days 28 and 35. Increasing the radiation dose delays the onset of the rise in ZPP, but does not affect the magnitude of the elevation. At lethal doses, ZPP elevation is not observed. Neither of the two previously described mechanisms that cause elevations of ZPP, namely iron deficiency and inhibition of ferrochelatase, are responsible for the radiation-induced elevation of ZPP. The elevation of ZPP appears to be correlated with the recovery of the hematopoietic system from radiation injury.

International Nuclear Information System (INIS)

A new reagent 7-(6-Br-2-henzthiazolilazo)-8-oxyquinoline-5-sulphoacid has been studied spectrophotometrically. Dissociation constants have been determined in 50% acetone (pK_1=2.5 and pK_2=5.9) and 50% dioxane (pK_1=1.7 and pK_2=6.1) as well as molar extinction coefficients of the reagent dissociated form in the same solvents (71.1.10"3 and 72.4.10"3). The conditions have been studied of complexing the reagent with ions of uranium (6), zinc (2), and manganese (2) in 50% dioxane (pH 2.5-4.5) and the properties of the formed complexes.

Energy Technology Data Exchange (ETDEWEB)

Mining of copper and zinc took place at the Clinton Mine located in the Estrie region of Quebec between 1973 and 1975, during which time 115,000 tons of mineral were treated at the Solbec plant. In this poster presentation, the authors provided the background information pertaining to this mine and described the state in which it was in 1994. The pit was covered with good quality water, with a pH of 7,1 and copper and zinc content ranging between 0,1 and 0,6 mg/l, and iron ranging between 0,2 and 1,8 mg/l. The tailings basin drainage was found to have a pH of between 3,6 and 6,1. A program for the characterization of the site was implemented and the concept for the restauration of the Clinton site was developed and implemented. The work carried out at the site is discussed during this presentation as well as the monitoring taking place. 27 figs.

International Nuclear Information System (INIS)

In the Carpathian Basin, significant percentage of watershed area and floodplains of rivers are utilised agriculturally. Several potential sources of poisonous metal pollution have been identified in these areas. Because of spills from some of them a few severe accidents have happened especially in the watershed area of Tisza River during the last decades. The motivation of our present work was to produce "6"2","6"5Zn and "2"0"3Pb radioisotopes because they can be used especially as tracers for studying the kinetics of uptake, transport and accumulation of zinc and lead by plants under different circumstances. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The concentrations of iron, chromium, zinc, and aluminum were measured by atomic absorption spectroscopy in the lipid-soluble fractions of tar from the process stream of an experimental coal gasifier as part of large study on the health risks of coal gasification. Lipid solubility was inferred from octanol/water-partitioning and benzene-solubility tests. The properties of the lipid-soluble metals were compared to reference compounds by Sephadex LH-20 chromatography. The ability of the lipid-soluble metals to remain lipid soluble after treatment with acid and base was also tested. Lipid-soluble iron, chromium, zinc, and aluminum were present at 360, 12, 3, and 1 ppM, respectively, in the gasifier coal tar. The presence of these metals in lipid-soluble form may have important consequences relative to the potential toxicity of the tar if persons are exposed to it.

Energy Technology Data Exchange (ETDEWEB)

The Electric Fuel zinc-air battery yielded energy densities from 6.8 to 10.2 times higher than those of the lead-acid batteries. The higher the power and the more difficult the driving cycle, the higher this ratio of energy densities grew. Not only was the Electric Fuel battery capable of extended high-power discharge, the impact of such discharge conditions on energy and driving range was show to be quite small, and was much smaller than the comparable impact on lead-acid traction batteries. At the time of writing this paper, tests are scheduled to continue with the 110-kWh battery in the Mercedes van, and preliminary plans have been made for testing of additional batteries on other vehicle types.

Energy Technology Data Exchange (ETDEWEB)

We report progress in an effort to develop and demonstrate a refuelable zinc/air battery for fleet electric vehicle applications. A refuelable module consisting of twelve bipolar cells with internal flow system has been refueled at rates of nearly 4 cells per minute refueling time of 10 minutes for a 15 kW, 55 kWh battery. The module is refueled by entrainment of 0.5-mm particles in rapidly flowing electrolyte, which delivers the particles into hoppers above each cell in a parallel-flow hydraulic circuit. The concept of user-recovery is presented as an alternative to centralized service infrastructure during market entry.

International Nuclear Information System (INIS)

The Co-ordinated Research Programme (CRP) on ''Isotope-Aided Studies on the Bioavailability of Iron and Zinc from Human Diets'' was initiated by the IAEA in 1990, and presently encompasses participating institutes in 11 countries. A summary of the discussions that took place during thr second Research Co-ordination Meeting held in Hyderabad, India, between 16-20 November 1992, is given in this report together with 12 working papers (progress reports) presented by individual participants. A separate abstract was prepared for each of these papers. Refs, figs and tabs.

Energy Technology Data Exchange (ETDEWEB)

The cyclic voltammetry indicated that the oxygen reduction reaction (ORR) proceeded by the four-electron pathway mechanism on larger Ag particles (174 nm), and that the ORR proceeded by the four-electron pathway and the two-electron pathway mechanisms on finer Ag particles (4.1 nm), simultaneously. The kinetics towards ORR was measured at a rotating disk electrode (RDE) with Ag/C electrode. The number of exchanged electrons for the ORR was found to be close to four on larger Ag particles (174 nm) and close to three on finer Ag particles (4.1 nm). The zinc-air battery with Ag/C catalysts (25.9 nm) was fabricated and examined. (author)

Energy Technology Data Exchange (ETDEWEB)

Highly water-repellent surfaces have been prepared from arrayed nanowires of zinc oxide (ZnO) by a treatment with stearic acid. The layers are electrochemically deposited on a nanocrystalline seed layer from an oxygenated aqueous zinc chloride solution. An advancing contact angle (CA) as high as 176{sup 0} is obtained with a very small hysteresis {approx}1{sup 0}. These results, supplemented by infrared spectroscopy, show that the stearic acid forms a very well-packed self-assembled monolayer. The CA measurements show a very good stability of the treated surface even when exposed to harsh conditions or long-term ambient illumination.

Energy Technology Data Exchange (ETDEWEB)

The purpose of this work was to investigate the role of chromium on hydrogen embrittlement of Ni-Cr-Fe alloys and thus to develop a better understanding of the low-temperature stress corrosion cracking (SCC) phenomenon. The effect of chromium on hydrogen embrittlement was examined using tensile tests followed by material evaluation via scanning electron microscopy (SEM) and light optical microscopy. Four alloys were prepared with chromium contents ranging from 6 to 35 wt pct. In the uncharged condition, ductility, as measured by the percent elongation or reduction in area, increased as the alloy chromium content increased. Hydrogen appeared to have only minor effects on the mechanical properties of the low-chromium alloys. The addition of hydrogen had a marked effect on the ductility of the higher-chromium alloys. In the 26 pct chromium alloy, the elongation to ...

Science.gov (United States)

The purpose of this communication is to determine whether the solubility enhancements for cold-worked Pd-Ni alloys increase or decrease with atom fraction of Ni. Substitutional Ni atoms contract and Pd lattice, in contrast to the lattice expansion resulting from substitutional Ag in Pd. The Pd-Ni alloy system forms a continuous series of fcc solid solution alloys over the whole composition range. The solubility enhancements will also be determined for a series of homogeneous, ternary Pd[sub 1[minus]x]Ni[sub 1/2x]Ag[sub 1/2x] alloys for x in the range from 0 to 0.2. For this series of ternary alloys the fcc lattice parameters do not change significantly from that of pure Pd. The alloys used in this research were purchased from Tanaka Kikinzoku Kogyo K.K. The detailed experimental procedure has been described previously. The alloys were all ...

International Nuclear Information System (INIS)

Titanium base 'alpha'-alloys (Pt-7M, RK-20 and Ti-5Al-2Zr-1.5V) are considered for their behaviour under neutron irradiation. The role of alloying elements in radiation hardening is discussed depending of neutron fluence and irradiation temperature. For PK-20 alloy three stages of change in mechanical properties are revealed which are following: incubation period and weak hardening, intense radiation hardening, radiation hardening attenuation. Irradiation temperature rise results in an increase of incubation period and threshold neutron fluence. A special attention is paid to hydrogen absorption in #alpha#-titanium alloys under irradiation. It is concluded that titanium base 'alpha'-alloys are serviceable as structural materials in nuclear plants with allowance made for peculiar features of their radiation behaviour. 4 refs.; 7 figs.; 1 tab.

International Nuclear Information System (INIS)

In connection with the different cyclical strengths of the two-phase (#alpha# + #beta#) titanium alloy in the case of the acicular and rounded formations of the #alpha#-phase, we have studied, employing the X-ray diffraction method, the phase composition of the alloy and the influence of heat treatment upon it. Using the method of electronic fractography, we examined the fractures in samples destroyed by the asymmetric twisting, in order to find out why the durability of the alloy is dependent upon the #alpha# - phase structure. It has been found that in the BT22 alloy, the decay the #beta#-phase may proceed in two ways; either with the formation of the martensite #alpha#'-phase of the acicular shape or with the separation of the non-martensite round-shaped #alpha#-phase. The character of the phase transformations #beta# - #alpha# or #beta#-#alpha#' is, to a considerable extent, the conseguence of the ...

International Nuclear Information System (INIS)

Modern commercial alloys are not suited for future steam turbines of operating temperatures beyond 700 C. #gamma#'-hardened alloys like Waspaloy have good mechanical characteristics but have defects when large batches are melted. #gamma#'/#gamma#''-hardened alloys like Inconel 706, on the other hand, are easy to produce but have insufficient microstructural long-term stability and insufficient creep strength. Mixed crystal solidified alloys like Inconel 617 have excessive yield stress at forging temperatures. Two new alloys were therefore developed. Results so far show that they have good production characteristics but insufficient mechanical characteristics. The reasons for this are currently under investigation. (orig.)

International Nuclear Information System (INIS)

Nano indentation analysis and transmission electron microscopy observation were performed to investigate a microstructural evolution and its influence on the hardening behavior in Fe-Cr alloys after an irradiation with 8 MeV Fe4+ ions at room temperature. Nano indentation analysis shows that an irradiation induced hardening is generated more considerably in the Fe-15Cr alloy than in the Fe-5Cr alloy by the ion irradiation. TEM observation reveals a significant population of the a0 dislocation loops in the Fe-15Cr alloy and an agglomeration of the 1/2a0 dislocation loops in the Fe-5Cr alloy. The results indicate that the a0 dislocation loops will act as stronger obstacles to a dislocation motion than 1/2a0 dislocation loops.

International Nuclear Information System (INIS)

Resistance of Alloy 800 as a PWR S/G tube material to IGC/IGSCC and Ni, Co release into water was evaluated as compared with Alloys 600 and 690. The study to improve the resistance to IGSCC and general corrosion was also made, including the effects of shot-peening on the distribution of the residual stress of the U-bent tubes and the susceptibility to SCC, the stabilizing elements on IGC/IGSCC, and prior oxidation on general corrosion. From the results, shot-peened Alloy 800 was estimated to be the most reliable S/G tube material among the high nickel alloys tested. In addition, the Alloy 800 tube would obtain further reliability in IGSCC and general corrosion resistance by the combined addition of Ti, and Nb, and the prior oxidation of the inner tube surface, respectively.

Energy Technology Data Exchange (ETDEWEB)

Plastic formability of cast magnesium alloy that were hot rolled after roll strip casting was investigated to ascertain the feasibility of semi-solid strip casting process of AZ31B magnesium alloy. Hot rolling and heat treatment conditions were changed to examine which conditions were appropriate for producing AZ31B wrought magnesium alloys after strip casting process. Microscopic observation of the crystals of the manufactured wrought magnesium alloys was performed. It has been found that a limiting drawing ratio of 2.7 was possible in a warm deep drawing test of the cast magnesium alloy sheets after being hot rolled. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Pd/Ag alloy hollow spheres have been synthesized in ethylene glycol solution by the solvothermal method and have been characterized extensively. TEM results have revealed the formation of Pd/Ag hollow spheres. Moreover, HRTEM results confirmed the formation of Pd/Ag alloy spheres, where the lattice fringe spacing is 0.229 nm corresponding to the (111) plane of Pd/Ag alloy. SEM, XRD and UV-vis results have further suggested the formation of alloy hollow spheres. The preliminary results showed the reaction time may be an importance factor influencing the formation of Pd/Ag alloy hollow spheres.

Energy Technology Data Exchange (ETDEWEB)

Effects of rolling conditions on warm deep drawability of cast magnesium alloy that were hot rolled after roll strip casting were investigated to ascertain the feasibility of twin-roll strip casting process of AZ31B magnesium alloy. Hot rolling and heat treatment conditions were changed to examine which conditions were appropriate for producing AZ31B wrought magnesium alloys after strip casting process. Microscopic observation of the crystals of the manufactured wrought magnesium alloys was performed. It has been found that a limiting drawing ratio of 2.7 was possible in a warm deep drawing test of the cast magnesium alloy sheets after being hot rolled. (orig.)

International Nuclear Information System (INIS)

Formation kinetics and composition of products of interaction of binary and ternary tungsten-molybdenum-rhenium alloys containing 30#+-#3 at.% (27-47 weight %) Re with products of thermal dissociation of ammonia and nitrogen-oxygeneous mixtures are studied. Mo-45% Re-10%W ternary alloy occupies intermediate position between W-27%Re and Mo-47%Re binary alloys, while its corrosion resistance and corrosion nature are close to those of W-Re and mechanical features - to those of Mo-Re alloy. It is explained by the fact, that the variation of W and Mo ration occurs in thin surface layer of ternary alloys in contrast to the initial state and the enrichment of near-the-surface layer with tungsten occurs under hot and cold deformation, at aging in the air, and during oxidation-reduction treatment. 4 refs.; 7 figs.

Energy Technology Data Exchange (ETDEWEB)

A body-centered cubic (bcc) Mg-12Li-9Al-1Zn (wt.%) alloy was fabricated in air by electrolysis from LiCl-KCl molten salt at 500 deg. C. Electrolytic deposition of Li atoms on cathode (Mg-Al-Zn alloy) and diffusion of the Li atoms formed the bcc Mg-Li-Al-Zn alloy with 12 wt.% Li and only 0.264 wt.% K. Low K concentration in the bcc Mg alloy strip after the electrolysis process resulted from 47% atomic size misfit between K and Mg atoms and low solubility of K in Mg matrix.

International Nuclear Information System (INIS)

Preliminary observations on the isothermal carbon transfer in low-carbon Alloy-800 exposed in sodium with AISI-304 type of steel at 550_0 are reported. The alloy was found to undergo a carburization comparable or slightly lower than that observed for the AISI-304 stainless steel for carbon activities above 6 x 10 /sup -3/ at 550_0C, but was not found to decarburize below such a carbon activity value. In the examined range the chemical composition of the alloys does not affect the process out of the experimental uncertainty of measure. Conclusions concerning the effective diffusion for carbon in the alloy are formulated. Preliminary relationships were found for an empirical evaluation of the carburization of the Alloy-800 in sodium of known carbon activity.

International Nuclear Information System (INIS)

Recent advances made in the area of amorphous and nanocrystalline alloys exhibiting high saturation inductions are reviewed. A new chemical composition was identified that achieves a saturation induction of 1.64 T in an iron-based amorphous alloy. This alloy, when used in electrical transformers, shows a much improved performance over the existing amorphous alloy. Nanocrystalline FeCoCuNbSiB alloys are found to have saturation induction levels reaching 1.7 T. These materials are suited for use in sensors and inductors carrying large currents. Some of these nanocrystalline alloys show a BH squareness ratio exceeding 90%, which can be utilized in pulse power devices. Recent developments in the applications of these materials are also pointed out.

International Nuclear Information System (INIS)

During the service in nuclear power plants, steam generator (SG) tubing will suffer from a vibration with a frequency from 30-40 Hz. This means that SG tubing will undergo a very high cycle fatigue process during the design life time (25 years=about 3x10"1"0cycles). The material degradation and the very high cycle fatigue life of SG tubing materials due to the vibration are therefore of concern. In this investigation, the fatigue properties of Alloy 690 and Alloy 800 SG tubing in the very high cycle fatigue regime (higher than 10"7 cycles) and strain controlled fatigue at temperatures up to 330"oC have been investigated. The fatigue properties of SG tubing of Alloy 690 are comparable to that of wrought material. The strain controlled fatigue properties of Alloy 690 and Alloy 800 are slightly better at 288"oC than at room temperature (RT). At the stress near the fatigue endurance, ...

Energy Technology Data Exchange (ETDEWEB)

By the year 2000, the Postal Service aims to reduce its diesel transport by around 15000 vehicles. The advisory service, Detecon, is reviewing alternatives for postal deliveries as part of the ''Post 2000'' initiative. One such system is an electric-powered vehicle with a zinc-air battery from the Israeli firm Electric Fluid Limited (EFL). (orig.)

UK PubMed Central (United Kingdom)

BackgroundOur previous studies indicate that either PEP-1-superoxide dismutase 1 (SOD1) or PEP-1-catalase (CAT) fusion proteins protects myocardium from ischemia-reperfusion-induced...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A cathode of improved discharge characteristics for a zinc-air battery is prepared from mixtures containing gamma-MnO/sub 2/ 33-67 wt%, C 12-40 wt% and KOH 20-28 wt%.

Energy Technology Data Exchange (ETDEWEB)

The results of Sandia National Laboratories' participation in the NASA Planetary Definition and Design Program are summarized. Areas reported include the characterization of large area cadmium zinc telluride spectrometers and the application of simulation techniques to the prediction of device performance. Also investigated was the response of mercuric iodide devices in the region from 1 to 100 KeV. A literature study to determine the status or radiation damage measurements in room temperature semiconductor devices is also reported.

UK PubMed Central (United Kingdom)

Cadmium (Cd) exposure causes glucosuria (glucose in the urine). Previously, it was shown that Cd exposure of primary cultures of mouse kidney cells (PMKC) decreased mRNA levels of the glucose...Full Text Available

International Nuclear Information System (INIS)

The present invention provides a fuel cladding tube having an excellent corrosion resistance and thus a long life, and a suitable manufacturing method therefor. Namely, in the fuel cladding tube, the outer circumference of an inner layer made of a zirconium base alloy is coated with an outer layer made of a metal more corrosion resistant than the zirconium base alloy. Ti or a titanium alloy is suitable for the corrosion resistant metal. In addition, the outer layer can be coated by a method such as vapor deposition or plating, not limited to joining of the inner layer material and the outer layer material. Specifically, a composite material having an inner layer made of a zirconium alloy coated by the outer material made of a titanium alloy is applied with hot fabrication at a temperature within a range of from 500 to 850degC and at a fabrication rate of not less than 5%. The ...

International Nuclear Information System (INIS)

Available data are presented which support the supposition that metals and alloys with a negative low-temperature Hall coefficient are apparently not superconducting. (author).

Energy Technology Data Exchange (ETDEWEB)

The possibility of rapid heat treatment (RHT) application to titanium castings has been studied. It was shown that such treatment provides a significant improvement of intragrain structure and mechanical properties of cast ({alpha}+{beta})-titanium alloys. ((orig.))

Energy Technology Data Exchange (ETDEWEB)

A process for the generation of halogens from halide-containing solutions includes the step of conducting electrolysis of the solutions in an electrolytic cell having a platinum based amorphous metal alloy anode.

Energy Technology Data Exchange (ETDEWEB)

The effect of concentration on the corrosion behavior of Mg-based alloy AZ91D was investigated in ethylene glycol-water solutions using electrochemical techniques i.e. potentiodynamic polarization, electrochemical impedance measurements (EIS) and surface examination via scanning electron microscope (SEM) technique. This can provide a basis for developing new coolants for magnesium alloy engine blocks. Corrosion behavior of AZ91D alloy by coolant is important in the automotive industry. It was found that the corrosion rate of AZ91D alloy decreased with increasing concentration of ethylene glycol. For AZ91D alloy in chloride >0.05 M or fluoride <0.05 M containing 30% ethylene glycol solution, they are more corrosive than the blank (30% ethylene glycol-70% water). However, at concentrations <0.05 for chloride or >0.05 M for fluoride containing ethylene ...

International Nuclear Information System (INIS)

The status of development and commercialization of a modified 9 Cr-1 Mo alloy is presented. The alloy is modified by the addition of 0.06 to 0.10% Nb and 0.18 to 0.25% V. The alloy is recommended for use in the normalized and tempered condition (1040"0C for 1 h, air cooled to room temperature; 760"0C for 1 h, air cooled to room temperature). Heat treatment, Charpy impact, tensile, and creep properties of the alloy are described in detail along with a brief description of other properties. The modified alloy has creep strength that exceeds that of standard 9 Cr-1 Mo and 2 1/4 Cr-1 Mo steels for the temperature range from 427 to 704"0C. The total-elongation and reduction-of-area values for all test temperatures and rupture times up to 22,500 h exceed 15 and 70%, respectively. The estimated design allowable stresses for this alloy are higher than those for standard ...

Science.gov (United States)

Quantitative metallography is often used to confirm the proper processing of aerospace metallic materials. A microstructural feature of great importance for titanium alloys processed in the alpha-beta phase field is the volume fraction of primary alpha. S...

Energy Technology Data Exchange (ETDEWEB)

The carbon transfer has been analyzed in the Alloy 800/sodium/stainless steel system by determining the carbon-uptake of Alloy 800 foils, which were exposed in liquid sodium of known carburizing potential. Under equilibrium conditions between 650 and 550/sup 0/C the measured total carbon concentrations in the Alloy 800 tabs were found to be roughly related to the carbon activities of the sodium environment by the equation already stated for the 18 Cr-8/10 Ni stainless steels, extrapolated to the chemical composition of the Ni-rich austenitic alloy. However the Alloy 800 was not found to undergo any decarburization in low-carbon activity environments. The carbon diffusion kinetics was determined as a function of temperature, it was found to be similar to that reported for the AISI-304 type of steel. The effects of sodium exposure on microstructural and mechanical properties of ...

Science.gov (United States)

The authors have presented results of an investigation of wettability of SiC particulates by liquid alloys of the Al-Si-Mg system. The evaluation of wetting has been carried out through the determination of the threshold pressure for infiltration of packed SiC particulates by the liquid alloy. The results indicate that whereas Si and Mg additions do not affect wetting, in the case of the ternary alloys the contact angle decreases in an amount proportional to the content of Mg[sub 2]Si.

International Nuclear Information System (INIS)

A series of ball-on-disc wear and friction measurements were made for surfaces which have a chemical vapour deposition carbon silicon alloy layer on a carbon substrate (fine grain POCO graphite). Nitrogen ion irradiation was used to improve the wear resistance of the carbon alloy surface. For comparison, measurements were also taken for alumina against alumina. It was found that the lowest friction coefficient and lowest wear occurred for ion irradiated coated samples containing 4% Si in the alloy and that the performance was superior to that of alumina. ((orig.)).

Energy Technology Data Exchange (ETDEWEB)

The exposure of heat-resistant alloys to high temperature can significantly change their mechanical properties. This paper presents and analyzes data on the effect of thermal exposure on the tensile and impact behavior of three cast materials -- the HK-40, HP-50, and 21Cr-32Ni-Fe alloys -- and of wrought material -- Alloy 800. The changes in tensile and impact properties caused by high-temperature exposure are reviewed. Reasons for these property changes and needs for considering them in the design, operation, and life assessment of high-temperature equipment are discussed.

Energy Technology Data Exchange (ETDEWEB)

The chemical properties of alloys in a given environment are to a large extent governed by the surface composition. Changes of the surface composition during passivation are important features in this respect. Previous studies of single crystal Ni-Mo alloys surfaces have been reported. The aim of this work was to obtain quantitative data, for the natural oxide and the passive films formed on Ni-6% Mo(100) and (110) alloys, using Rutherford backscattering spectroscopy and nuclear reaction analysis.

International Nuclear Information System (INIS)

Phase transformations occuring during cold deformation in hardened #alpha#+#beta# titanium alloy of the Ti-Al-Mo-Zr-Sn-Si system with 10% summary content of alloying elements are studied by X-ray diffraction analysis. Two stages of trapsformation of metastable #alpha#''-phase are found. A conclusiop is made that ability of the alloy containing #alpha#''-phase to cold deformation is determined by the presence of favourable texture, by high degree of metastability and by volume portion of #alpha#''-phase in the alloy structure.

International Nuclear Information System (INIS)

A computerized corrosion measuring system (EG and G model 350 A) was used to study the influence of Cr, Mo, Ti, Nb and W on the pitting corrosion of nickel base alloys in 3% NaCl at 90"0C. The electrochemical parameters under investigation are the corrosion potential E_c_o_r_r, pitting potential E_p and protection potential E_p_p. The corrosion behaviour of nickel base alloys were studied by using pitting scan and potentiostatic techniques. Values of corrosion potential, pitting potential and protection potential were used for a ranking of alloys for corrosion resistance.

International Nuclear Information System (INIS)

Formation of the soft magnetic nanostructure in amorphous Fe_1_4Ni_4_0Zr_7B_1_2 alloy due to heat treatment is studied by the Moessbauer, differential scanning calorimetry, and X-ray diffraction techniques. Annealing at temperatures 520-580 "oC leads to the formation of extremely soft nanocrystalline alloy as revealed by the rf-Moessbauer measurements. The superparamagnetic behaviour was observed for the alloy annealed at 620-640 "oC. At higher annealing temperatures good soft magnetic properties deteriorate. (author)

Energy Technology Data Exchange (ETDEWEB)

Experiments were conducted which established that the higher passivating capacity of Ni/sub 60/Nb/sub 40/ alloys in the amorphous state and higher efficiency of the anodic process of generation of chlorine (2 N NaCl + HCl to pH = 0) in comparison with the crystalline state are determined by higher homogeneity and density of the passive films formed on the amorphous alloy and by higher electron conduction which depends directly on the difference in the structure of the passive films formed on the alloys in the amorphous and crystalline states.

International Nuclear Information System (INIS)

The methods of optical and transmission electron microscopy were used to study the influence of different programmes of hot deformation on the structure formation of (#alpha#+#beta#) titanium alloy VT9. The #beta# alloy VT-15 was studied at the same time in order to simulate the dislocation structure generated in the process of hot deformation. During the hot deformation of two-phase titanium alloys in both #beta# and (#alpha#+#beta#) ranges there is found to be an optimum range of deformation in which a homogeneous, polygonized structure is formed.

International Nuclear Information System (INIS)

We propose a dissolution-passivation model to account for the electrochemical behavior of Alloy 800 and 316L stainless steel under steam generators operating conditions. This model is similar to the one defined for nickel, considering the known importance of this element on the studied alloys. The comparison of the rates of the elementary steps points out the favorable influence of dissolved oxygen and phosphate ions on the dissolution of Alloy 800, even in the presence of chloride ions. The sensitivity of 316L SS is greater, especially because of the lowest stability of oxide-like intermediate.

Energy Technology Data Exchange (ETDEWEB)

An experimental verification for long-term performance of a Pd-Ag permeation in ITER tritium fusion cleanup units (FCU) is needed. In addition, information is required on the influence of tritium and {sup 3}He decay on the physical and chemical properties of Pd-Ag alloys (V-1). The results of the investigations of alloys (V-1) (mechanical properties and microstructure) after long-term usage exposition in tritium are given in this report. The experimental conditions (temperature, pressure, clearance, {sup 3}He concentrations) and the previous conclusions on the V-1 alloy performance are presented. (orig.).

International Nuclear Information System (INIS)

Formation of basis type texture at rolling of Ti + 6.0% Al + 1.5% V + 1.0% Mo system alloy with initial prismatic texture is investigated by means of X-ray techniques. Variations of mechanical features in titanium alloy sheets depending on temperature-deformation conditions of rolling are investigated. Main conditions for formation of the intensive basis textute in the investigated alloy sheets which provides for isotropic properties in sheet plane and for increased ductility are determined.

Energy Technology Data Exchange (ETDEWEB)

The most typical kinds of corrosion of brasses are selective corrosion (dezincification) and stress corrosion. Prevention against these kinds of corrosion lies in application of arsenic alloy addition and appropriate heat treatment removing internal stresses as well as in maintaining the arsenic and phosphorus contents on a proper level. The most typical corrosion of cupronickels is the local corrosion. Selective corrosion occurs less often and corrosion cracking caused by stress corrosion in sea water does not usually occur. Crevice corrosion is found especially in places of an heterogeneous oxidation of the surface under inorganic deposits or under bio-film. Common corrosive phenomena for brasses and cupronickels are the effects caused by sea water flow and most often the impingement attack. Alloy additions improve resistance to the action of intensive sea water flow but situation in this field requires further improvement, especially if the ...

International Nuclear Information System (INIS)

Existing applications of Alloy 800 are summarized, with particular reference to its use in various types of reactor. The need for a co-ordinated research and development programme is stressed, and the variables to be explored are outlined. The papers relating to the problem of corrosion and cracking in water and steam are considered. the strength and ductility of Alloy 800 is considered. Finally, sections of the summary deal with the use of Alloy 800 for (a) sodium cooled fast reactor boiler tubes; (b) the high temperature gas cooled reactor; and (c) PWR steam generator tubes. (U.K.).

Energy Technology Data Exchange (ETDEWEB)

Two extruded magnesium alloys, AZ31 and AZ61 were selected to evaluate the influence of process parameters on the material forgeability. The processing parameters considered for forging magnesium alloys were: compression load in the range 55 KN to 60 KN and forging temperature, in the range of ambient temperature to 300 C. Uniaxial compression tests were conducted to establish the strain-temperature relationship. The influences of process parameters on the microstructure were also evaluated. (orig.)

International Nuclear Information System (INIS)

The optimum of strontium amount for good modification of AK7, AK9, AK11, AK52, AK104 alloys was determined on the base of the analysis of microstructural changes. The stability of the modifier was investigated on the way of successive remelting of billets. The influence of amount of modifier on the impact strength of the alloys was established. (author)

Energy Technology Data Exchange (ETDEWEB)

Using commercial AZ31 magnesium alloy sheets, we produced a foamable preform sheet containing titanium hydride (TiH{sub 2}) powder through diffusion-bonding and hot-rolling of four cycles. Heating the preform sheets in Ar atmosphere, we obtained closed-cell magnesium alloy foams with various porosities. The foamed specimen at 883 K showed the maximum porosities of 77%. (orig.)

Energy Technology Data Exchange (ETDEWEB)

One of the effective methods of deep modification of the surface of steels and alloys is the combination of ion implantation and plasma nitriding. In this work, the long-range effect is demonstrated in the case of combination of the effect of high- and low-energy ions of nitrogen on a martensitic steel for each ion implantation is usually not effective, and a titanium alloy used widely in industry.

International Nuclear Information System (INIS)

Cyclic strength of #alpha#+#beta#-titanium alloy BT3-1 is studied under load frequencies of 33 and 300 Hz. The increase in the cyclic strength with growing frequency is caused by formation of FCC interphase layers of titanium hydrides. Their formation is one of possible ways of raising the fatigue strength of titanium alloys. Peculiarities of FCC interlayer formation in #alpha#+#beta# phases under loading frequency variation are revealed.

Energy Technology Data Exchange (ETDEWEB)

The distribution of graphite particles in graphite containing copper alloy was further improved very significantly using several procedures and technological modifications. The developed techniques attacked the graphite distribution problem in two ways. Realizing that clustering of very fine (5um) graphite particles is one of the two major problems, a pretreatment process has been developed using aluminum powders to deagglomerate graphite particles. Along with this, a two-stage stirring technique was used to first incorporate and then to distribute uniformly the deagglomerated particles in the melt. During this year, based on these developments, several components were cast to evaluate the castability of Cu alloy-graphite melts. In addition, machinability tests were done to clearly established that addition of graphite particles improve the machinability of copper MMC alloys over and above that of monolithic copper ...