A procedure based on electrophoretic deposition (EPD) was developed to coat metal plates with powder catalysts. The method was tested on stainless-steel plates with three Ni-based catalysts for the steam reforming of ethanol. The catalysts (Ni/La2O3/g-Al2O3) contained 15% Ni and 8% La, and were prepared using three types of g-alumina with different textural properties. The powder catalysts were suspended in isopropanol, and EPD deposition was performed with a voltage of 100V and a distance between electrodes of 2cm. Deposition time was varied between 3 and 7min, which gave a thickness of the catalyst layer from around 30 to 100mm. The morphology of the catalyst layer was dependent on the textural characteristics of the g-Al2O3 used to prepare the catalyst. The activity of the catalyst plat...