International Nuclear Information System (INIS)

Bi-U mixed oxides were synthesized by two methods and characterized by X-ray diffraction and X-ray photoelectron spectroscopy. The samples were tested for the catalytic oxidation of carbon monoxide by oxygen. A stepwise redox mechanism consistent with the kinetic results is proposed. (orig.).

International Nuclear Information System (INIS)

Oxide superconducting thin films were irradiated with X-rays and ultra-violet (UV) light, and induced radiation effects on electrical and chemical properties were examined by transport measurement, X-ray diffraction analysis (XRD), diamagnetization measurement and X-ray photoemission spectroscopy (XPS). After irradiation for ErBa_2Cu_3O_x films with X-rays emitted from a Rh tube for 100 hours, superconductivity was remarkably damaged, destroying the zero-resistance state. The UV-light irradiation for Bi_2Sr_2CaCu_2O_x films was performed in He gas of about 500 Pa with a low pressure mercury lamp. The superconductivity was gradually degraded with the UV irradiation time up to 70 minutes. In both cases, adequate oxygen-annealing treatments restored superconductivity. The X-ray photoemission spectra showed that the mean Cu valence of the films was decreased ...

International Nuclear Information System (INIS)

The possibilities of using both selective heavy ion induced X-ray emission and secondary ion mass spectroscopy (SIMS), for the identification of impurities present at low concentrations in cadmium telluride are examined. The relative concentrations of the impurities along CdTe crystals have been determined by exciting the X-ray emission of the elements in several slices with Ar and Kr ions and by comparing the relative characteristic X-ray emission yields. As a consequence of the quasimolecular inner shell ionization mechanism in heavy ion-atom collisions, Ar and Kr ions allow a strong excitation of the main impurities seen by SIMS namely Si, Cl and Ge, As, with only a minor contribution of Cd and Te. From the changes of the concentrations of the various impurities along the crystal, informations about segregation coefficients and compensation can be obtained.

Science.gov (United States)

The development of new efficient afterglow phosphors is currently hampered by a limited understanding of the persistent luminescence mechanism. Radioluminescence (RL) and x-ray absorption measurements on the persistent phosphor SrAl2O4:Eu,Dy were combined to reveal possible valence state changes for the rare earth (co)dopants. Traps in the phosphor material are quickly filled when exposing thermally emptied SrAl2O4:Eu,Dy powder to x rays. On the same time scale a partial oxidation of Eu2+ to Eu3+ is observed by x-ray absorption near-edge spectroscopy (XANES), while for the trivalent dysprosium the valence state remains unchanged. The impact of these observations on the recently proposed models for persistent luminescence is discussed.

Energy Technology Data Exchange (ETDEWEB)

The transformation of Pd/Si to Pd{sub 2}Si/Si is investigated using depth-resolved positron annihilation, x-ray diffraction and Auger electron spectroscopy studies. The observed defect-sensitive positron S-parameter value of 1.022-1.054 indicates the existence of divacancies across the silicide/silicon interface and Si substrate region. Our experimental observation of vacancy defects is consistent with the model proposed for excess vacancy generation across the interface consequent to Si diffusion. (letter to the editor)

CERN Document Server

Context. The high energies of protostellar jets, implied by recent observations of X-rays from such flows, came very much as a surprise. Inferred shock velocities are considerably higher than what was previously known, hence putting even larger energy demands on the driving sources of the jets. The statistics of X-ray emitting jets are still poor, yet a few cases exist which seem to imply a correlation between the presence of HeI 1.0830 mu emission and X-ray radiation in a given source. Aims. This tentative correlation needs confirmation and explanation. If the jet regions of HeI 1.0830 mu emission are closely associated with those producing X-rays, high resolution infared spectroscopy can be used to observationally study the velocity fields in the hot plasma regions of the jets. This would provide the necessary evidence to test and further develop theoretical models of ...

International Nuclear Information System (INIS)

For many centuries paper was the main material for recording cultural achievements all over the world. Paper is mostly made from cellulose with small amounts of organic and inorganic additives, which allow its identification and characterization and may also contribute to its degradation. Prior to 1850, paper was made entirely from rags, using hemp, flax and cotton fibres. After this period, due to the enormous increase in demand, wood pulp began to be commonly used as raw material, resulting in rapid degradation of paper. Spectroscopic techniques represent one of the most powerful tools to investigate the constituents of paper documents in order to establish its identification and its state of degradation. This review describes the application of selected spectroscopic techniques used for paper characterization and conservation. The spectroscopic techniques that have been used and will be reviewed include: Fourier-Transform Infrared spectroscopy, Raman ...

International Nuclear Information System (INIS)

Composite nitrides (such as BN, TiN) are widely used in various industrial applications because of their extreme wear and corrosion resistance, thermal and electrical properties. in order to obtain composite materials with these optimal properties, it is important to elucidate whether any chemical reactions occur at nitride/metal interfaces, e.g., those involving BN-Ti/TiN. Materials of interest include the deposition by PVD of Ti and TiN on BN substrates. Some of these systems were then subjected to varying degrees of physical and thermal alteration. Detailed X-ray photoelectron spectroscopy (XPS) has therefore been rendered of these interfaces using cross-sectional display and sputter etching. Resulting structural and morphological features have been investigated with transmission electron microscopy (TEM) and X-ray diffraction (XRD). Diffusion of the nitridation, oxynitride formation and interfacial growth are of general ...

Energy Technology Data Exchange (ETDEWEB)

The paper presents an integrated approach to the problem of electron temperature diagnostics of the plasma in a reversed field pinch. Three different methods, sampling different portions of the electron distribution function, are adopted, namely Thomson scattering, soft X-ray spectroscopy by pulse-height analysis and filtered soft X-ray intensity ratio. A careful analysis of the different sources of systematic errors is performed and a novel statistical approach is adopted to mutually validate the three independent measurements. A satisfactory agreement is obtained over a large range of experimental conditions, indicating that in the plasma core the energy distribution function is well represented by a maxwellian. (author)

Science.gov (United States)

Polycrystalline powders of Na{sub 2x}Mn{sub 1-x}PS{sub 3} have been synthesized from layered MnPS{sub 3} material by successive ion-exchange intercalation of potassium and sodium ions. Their x-ray photoelectron spectroscopy (XPS) and x-ray excited Auger spectroscopy spectra have been measured at room temperature using Mg K{alpha} (1253.6 eV) x-ray source. In particular, the Mn, P, and S 2p and Na 1s and 2p core-level regions and the Na Auger KL{sub 23}L{sub 23} transition have been investigated. All the analyzed XPS core-level spectra display a single-peak structure, suggesting the absence of nonequivalent atoms of Na, Mn, P, and S. The manganese XPS spectrum shows, as observed in MnPS{sub 3} and in its cesium and potassium intercalation compounds, typical shake-up satellites, suggesting that the Mn-S bond is yet mainly ionic in nature. The comparison with the XPS spectra relative ...

International Nuclear Information System (INIS)

Iron oxide thin films were prepared by spray pyrolysis technique onto glass substrates from iron chloride solution. They were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and (UV-vis) spectroscopy. The films deposited at T _s #<=# 450 deg. C were amorphous; while those produced at T _s_u_b = 500 deg. C were polycrystalline #alpha#-Fe_2O_3 with a preferential orientation along the (1 0 4) direction. By observing scanning electron microscopy (SEM), it was seen that iron oxide films were relatively homogeneous uniform and had a good adherence to the glass substrates. The grain size was found (by RX) between 19 and 25 nm. The composition of these films was examined by X-ray photoelectron spectroscopy and electron probe microanalysis (EPMA). These films exhibited also a transmittance value ...

Energy Technology Data Exchange (ETDEWEB)

The present paper is a comparative study of the cerium-containing nickel catalysts supported on x- and y-zeolites. In general, the addition of cerium ions caused an increase in the catalytic activity for CO hydrogenation and shifted the product selectivity to high molecular weight hydrocarbons. The degree of the effect of cerium additive depends on the ratio of cerium to nickel contents, the reduction temperature, and the nature of the supporting materials. Catalyst characterization, including volumetric hydrogen chemisorption, temperature programmed reduction/desorption, x-ray diffraction, surface area measurements, in-situ infrared spectroscopy and x-ray photoelectron spectroscopy, was performed in order to interpret the phenomena due to the effects of cerium additives and the support effect on Ni/zeolite catalysts.

CERN Document Server

In order to reduce the activation temperature of the TiZrV alloy, thin films of various compositions were produced by three-cathode magnetron sputtering on stainless-steel substrates. For the characterisation of the activation behaviour the surface chemical composition has been monitored by Auger electron spectroscopy during specific in situ thermal cycles. The volume elemental composition of the film has been measured by energy dispersive X-ray spectroscopy and the morphology (crystal structure and size of the crystallites) has been investigated by X-ray diffraction. The criteria indicating the sample quality and its dependence on film structure and chemical composition are presented and discussed. (13 refs).

Energy Technology Data Exchange (ETDEWEB)

This work reports studies of ethanol oxidation on Pt-Sn/C catalysts with nearly the same particle size and identical overall composition having different amounts of oxide and alloyed phases. Results of characterization of physical properties by transmission electron microscopy (TEM), X-ray diffraction (XRD), differential scanning calorimetry (DSC), X-ray photoelectron spectroscopy (XPS), and in situ dispersive X-ray absorption spectroscopy (DXAS) are presented. The variation in the amount of oxide and alloyed phases, promoted by heat treatments in mild temperature conditions, does not produce any significant particle growth. Cyclic voltammetry and oxidation of adsorbed CO in acid medium are used to probe the surface conditions. Data on the electrocatalytic activity towards ethanol oxidation, obtained by potential sweeps and chronoamperometry, are discussed and correlate well with ...

CERN Document Server

Energy Dispersive X-ray Analysis in the Electron Microscope

International Nuclear Information System (INIS)

A comparative study by Eu-L_I_I_I X-ray absorption and "1"5"1Eu-Moessbauer spectroscopy is presented for the EuPd_2_-_xAu_x Si_2 series. Possible ways to distinguish between mixed-valent behaviour and final-state effects in the L_I_I_I-edge spectra are discussed.

Energy Technology Data Exchange (ETDEWEB)

By means of infrared spectroscopy, x-ray diffraction, and differential thermal analysis, the authors investigate the pyrolysis of dichlorodithiourea cadmium, the vapor phase epitaxy of the cadmium sulfide film, and the composition of the solid and gaseous pyrolysis products. Those products are found to include the thiocyanates of guanidine, ammonium, and hydrogen along with cadmium oxides and sulfates and hydrochloric acid.

International Nuclear Information System (INIS)

First-principles self-consistent band-structure calculations of potassium titanyl arsenate, KTiOAsO_4 (KTA), have been made using the full potential linearized augmented plane wave (FP-LAPW) method. Total and partial densities of states of the constituent atoms of KTA have been derived. The results obtained show that the valence band of KTA is dominated by contributions of the O 2p-like states, while the Ti 3d-like states are the main contributors into the conduction band of the compound. Additionally, the FP-LAPW calculations have revealed that potassium atoms are highly ionized in KTA. In the present work, the X-ray emission spectroscopy (XES) and X-ray photoelectron spectroscopy (XPS) methods were also employed to investigate experimentally the electronic structure of potassium titanyl arsenate. For the mentioned compound, the XES K Ll, Ti L#alpha#, As K#beta#_2 and O K#alpha# bands reflecting the ...

Science.gov (United States)

Arsenic in soils from the Asarco Lead Smelter in East Helena, Montana was characterized by X-ray absorption spectroscopy (XAS). As oxidation state and geochemical speciation were analyzed as a function of depth (two sampling sites) and surface distribution. These results were c...

British Library Electronic Table of Contents (United Kingdom)

The combination of functional and morphological imaging technologies such as positron emission tomography (PET) and X-ray computed tomography (CT) has shown its value in the clinical and preclinical field. However, CT provides only very limited soft-tissue contrast and exposes the examined patient or laboratory animal to a high X-ray radiation dose. In comparison to CT, magnetic resonance tomography (MRI) provides excellent soft-tissue contrast and allows for nuclear magnetic resonance spectroscopy (NMRS) or functional MRI (fMRI). Thus, the combination of PET and MRI has been pursued for several years. First approaches have succeeded using conventional photo multiplier tube (PMT) technology together with light fibers to transfer scintillation light away from the high magnetic field. Latest...

CERN Document Server

We present constraints on theoretical models of Type Ia SNe using spatially resolved ASCA X-ray spectroscopy of four galaxy clusters: Abell 496, Abell 2199, Abell 3571 & Perseus. All four clusters have central Fe abundance enhancements and an ensemble of abundance ratios are used to show that most of the Fe in the central regions of the clusters comes from SN Ia. At the center of each cluster, simultaneous analysis of spectra from all ASCA instruments shows that the Ni to Fe abundance ratio (normalized by the solar ratio) is ~ 4. We use the Ni/Fe ratio as a discriminator between SN Ia explosion models: the Ni/Fe ratio of ejecta from the "Convective Deflagration" model W7 is consistent with the observations, while those of "delayed detonation" models are not consistent at the 90% confidence level.

British Library Electronic Table of Contents (United Kingdom)

SBA-15 supported nano-scaled copper oxide was synthesized by impregnation method via ultrasonic-assisted route. The removal test from gas mixture containing 0.1?vol.% hydrogen sulfide was carried out over this material at atmospheric conditions. The effects of the chemical nature of copper oxide and the textural properties of the material on removal capacity were studied. The materials before and after the removal test were analyzed by nitrogen adsorption, X-ray diffraction, Transmission Electron Microscope, X-ray photoelectron Spectroscopy, Fourier Transform Infrared Spectrometer and Inductive Coupled Plasma. The results showed that copper species are located predominantly in mesopore channels, existing as copper oxide nanoparticles. Mesopores are active sites for removal reaction. The ou...

International Nuclear Information System (INIS)

Full text: Institute for Nuclear Research, Pitesti-Mioveni, Romania in direct cooperation with the National Institute for Laser, Plasma and Radiation Physics, Magurele, Bucharest studied and prepared for coating more than 1000 tiles made of Inconel with 7-9 #mu#m of beryllium for nuclear fusion applications at JET, Culham, UK. The principles of manufacturing processes using thermal evaporation and plasma ignited in pure metal vapors as well as by Thermionic Vacuum Arc (TVA) method and the properties of the Ni and Be coatings are presented. The prepared beryllium layers were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and atomic force microscopy. (authors)

British Library Electronic Table of Contents (United Kingdom)

A novel single-step synthetic method for the preparation of anatase N-doped TiO"2 nanocrystalline at low temperature has been devoleped. The N-doped anatase TiO"2 nanoparticles were synthesized by sonication of the solution of tetraisopropyl titanium and urea in water and isopropyl alcohol at 80^oC for 150min. The as-prepared sample was characterized by X-ray diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy and UV-vis absorption spectrum. The product structure depends on the reaction temperature and reaction time. The photocatalytic activity of the as-prepared photocatalyst was evaluated via the photodegradation of an azo dye direct sky blue 5B. The results show that the N-doped TiO"2 nanocrystalline prepared via sonication exhibit an excellent photocatalytic...

International Nuclear Information System (INIS)

In this work we report a study of the induced changes in structure and corrosion behavior of martensitic stainless steels nitrided by plasma immersion ion implantation (PI"3) at different previous heat treatments. The samples were characterized by x-ray diffraction and glancing angle x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, and potentiodynamic measurements. Depending on the proportion of retained austenite in the unimplanted material, different phase transformations are obtained at lower and intermediate temperatures of nitrogen implantation. At higher temperatures, the great mobility of the chromium yields CrN segregations like spots in random distribution, and the #alpha#"'-martensite is degraded to#alpha#-Fe (ferrite). The nitrided layer thickness follows a fairly linear relationship with the temperature and a parabolic law with the process time. The ...

Energy Technology Data Exchange (ETDEWEB)

Pd/sub 2/Si layers produced by evaporation or sputtering onto silicon substrates were examined by high resolution electron microscopy, microdiffraction, X-ray, energy loss and Auger spectroscopy. The Si-Pd/sub 2/Si interfaces produced by evaporation were in all cases rougher and more polycrystalline than those produced by sputtering. X-ray microanalysis showed the predictable variation in palladium distribution across the interface but quantification did not produce the expected palladium-to-silicon ratios, primarily because of probe broadening and X-ray-induced fluorescence. Energy loss spectra showed plasmon energy shifts and changes in Si L edge shape due to bond formation with palladium. Auger data provided evidence for a small amount of oxygen at the Si-Pd/sub 2/Si interface. Electrical measurements of the ideality factor for Schottky barriers made from the materials produced higher values for the ...

Energy Technology Data Exchange (ETDEWEB)

Full text of publication follows: Large-scale problems such as nuclear waste disposal are increasingly recognized to be interconnected to small scale-mechanisms. Thus, synchrotron-based high-resolution analytical X-ray probes become important tools for exploring the micro-scale chemical reactivity of heterogeneous barrier materials used in nuclear waste repositories. In this study the layout of the micro-XAS beamline at the Swiss Light Source (SLS) will be presented. The beamline is optimized towards micro beam experiments ({approx}1 x 1 {mu}m{sup 2}) in the hard-X-ray regime (4 - {approx}22 keV) and allows to combine micro X-ray fluorescence (micro-XRF), micro X-ray absorption spectroscopy (micro- XAS), and micro X-ray diffraction (micro-XRD) investigations with radioactive samples. Furthermore, the potential of micro-XRF/XAS/XRD for acquiring spatially ...

Science.gov (United States)

The principles of radionuclide excitation of X-ray fluorescence radiation and its application in

International Nuclear Information System (INIS)

Heusler films with L2_1 and B2 structure are deposited simultaneously on amorphous carbon films, Si(100) surfaces, and in situ cleaved InAs(110) surfaces by coevaporation of Ni and the alloy MnIn. Morphology, structure, and stoichiometry are investigated with transmission-electron microscopy, electron diffraction, and X-ray spectroscopy. The almost perfect lattice match supports highly oriented growth of Ni_2MnIn on InAs, which is proven by electron diffraction under grazing incidence. The electrical resistivity of thin films on Si show metallic behavior. At temperatures of liquid helium point-contact Andreev reflection spectroscopy is performed on films grown on Si(100) and in situ cleaved InAs(110) surfaces yielding spin polarizations comparable to the ones of Fe, Ni, Co, and permalloy (Ni_8_0Fe_2_0).

Energy Technology Data Exchange (ETDEWEB)

Manganese model complexes, relevant to the oxygen-evolving complex (OEC) in photosynthesis, were studied with Mn K-edge X-ray absorption near-edge spectroscopy (XANES), Mn Kb X-ray emission spectroscopy (XES), and vibrational spectroscopy. A more detailed understanding was obtained of the influence of nuclearity, overall structure, oxidation state, and ligand environment of the Mn atoms on the spectra from these methods. This refined understanding is necessary for improving the interpretation of spectra of the OEC. Mn XANES and Kb XES were used to study a di-(mu)-oxo and a mono-(mu)-oxo di-nuclear Mn compound in the (III,III), (III,IV), and (IV,IV) oxidation states. XANES spectra show energy shifts of 0.8 - 2.2 eV for 1-electron oxidation-state changes and 0.4 - 1.8 eV for ligand-environment changes. The shifts observed for Mn XES spectra were approximately 0.21 eV for oxidation ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

ScienceCinema

...english ...

Energy Technology Data Exchange (ETDEWEB)

It has been discovered that the presence of MoO/sub 3/ lowers the ..cap alpha..-..beta.. transition in Sb/sub 2/O/sub 4/ from 935 to 850/sup 0/C with concurrent dissolution of Mo in the high-temperature (..beta..) form. The structure of Mo-doped ..beta..-Sb/sub 2/O/sub 4/ has been investigated by powder neutron diffraction, extended X-ray absorption fine structure (EXAFS) and Raman spectroscopies, and scanning-electron microscopy (SEM). Cell parameters: a = 12.0571 (12) A, b = 4.8335 (1) A, c = 5.3838 (6) A, ..beta.. = 105.579 (5)/sup 0/, monoclinic, space group C2/c, Z = 4. Combining the results of these techniques leads to the hypothesis that Mo is located interstitially within channels of electron density in the Sb/sub 2/O/sub 4/ structure with concurrent vacancy of two Sb/sup III/ atoms. There is no apparent oxygen deficiency in the resulting structure. 25 references, 6 figures, 3 tables.

Energy Technology Data Exchange (ETDEWEB)

Research highlights: {yields} The polarization curve of 316L SS possesses five turning potentials in passive region. {yields} Films formed at turning potentials perform different electrochemical and semiconductor properties. {yields} Dissolutions and regenerations of passive film at turning potentials are obtained by AAS and XPS. {yields} Turning potentials appearing in passive region are ascribed to the changes of the compositions of the passive films. - Abstract: The passivity of 316L stainless steel in borate buffer solution has been investigated by Mott-Schottky, atomic absorption spectrometry (AAS) and X-ray photoelectron spectroscopy (XPS). The results indicate that the polarization curve in the passive region possesses several turning potentials (0 V{sub SCE}, 0.2 V{sub SCE}, 0.4 V{sub SCE}, 0.6 V{sub SCE} and 0.85 V{sub SCE}). The passive films formed at turning potentials perform different electrochemical and semiconductor properties. ...

British Library Electronic Table of Contents (United Kingdom)

A magnetic core/shell Fe3O4/FeMnOx catalyst was prepared by a simple oxidation-precipitation method. The catalyst was characterized by X-ray diffraction, transmission electron microscope, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis and cyclic voltammetry. The characterization studies verified that Fe3O4 core was coated with a layer of Fe-Mn oxide. The Fe3O4/FeMnOx was found to be an effective and stable heterogeneous catalyst for the discoloration of methylene blue (MB) in aqueous solution by H2O2. The high catalytic activity is due to the FeMnOx shell, which not only increased the surface hydroxyl groups, but also enhanced the interfacial electron transfer. The discoloration of MB could be due to the decomposition of H2O2 into ?OH ...

Energy Technology Data Exchange (ETDEWEB)

Depth resolved positron annihilation studies on Pd/Si thin film system have been carried out to investigate silicide phase formation and vacancy defect production induced by thermal annealing. The evolution of defect sensitive S-parameter clearly indicates the presence of divacancy defects across the interface, due to enhanced Si diffusion beyond 870 K consequent to silicide formation. Corroborative glancing incidence X-ray diffraction (GIXRD), Auger electron spectroscopy (AES) and Rutherford backscattering spectrometry (RBS) have elucidated the aspects related to silicide phase formation and Si surface segregation.

International Nuclear Information System (INIS)

The room-temperature anisotropy of amorphous Fe_4_0Ni_3_8Mo_4B_1_8 (METGLAS 2628MB) ribbons after various heat treatments has been studied by Moessbauer spectroscopy. The average magnetization direction becomes significantly more out-of-plane after heating above 650 K but below the crystallization temperature. X-ray diffractograms suggest an atomic rearrangement has occurred. (orig.).

Science.gov (United States)

The crystal structure and optical reflectivity of AlP has been studied in a diamond anvil cell using energy dispersive x-ray diffraction to 43 GPa and micro-optical reflectance spectroscopy to 36 GPa. AlP undergoes a first order phase transformation from zincblende to a NiAs structure which exhibits metallic reflectivity in the near-infrared. The decrease in volume on transformation is 17%[plus minus]1%. The transformation is reversible but has large hysteresis. The equilibrium transformation pressure is 9.5[plus minus]5 GPa.

Energy Technology Data Exchange (ETDEWEB)

This was a project to investigate the crystal chemistry of OH and H{sub 2}O substitution in silicate minerals by use of X-ray and neutron diffraction methods combined with IR spectroscopy and to interpret and generalize the results using an electrostatic model for these mineral structures. Using these data together with published H position data electrostatic parameters for H sites were calculated from a simple electrostatic model. The data were then used to refine the model for incorporation of H into the wadsleyite structure. This has led to recent work on the synthesis and characterization of hydrous wadsleyites.

Energy Technology Data Exchange (ETDEWEB)

Nitriding leads to improved tribological and corrosive properties of iron alloy components. In order to study the effect of plasma nitriding parameters on the structure of compound layer and diffusion zone, a systematic variation of process parameters, temperature and process gas atmosphere has been carried out. Metallographic inspection, X-ray diffraction and glow discharge optical spectroscopy analysis (GDOES) were used in this investigation. The results clarified that depending on the amount of nitrogen in the gas atmosphere nitrided layers with and without compound layer can be generated in the surface of M2 tool steel for temperatures from 350 C to 500 C. For plasma nitriding in 5 vol.% Nitrogen and 95 vol.% Hydrogen no compact compound layer was formed. The gas mixture of 76 vol.% Nitrogen resulted in compound layer formation for all temperatures from 350 C to 500 C. X-ray phase analysis indicated an almost 100% ...

Energy Technology Data Exchange (ETDEWEB)

Nanosized CaSnO{sub 3} is synthesized by a hydrothermal process and characterized by X-ray diffraction (XRD), Raman spectroscopy, and scanning electron microscopy (SEM). The SEM observation shows the sample has a porous flowerlike morphology. The electrochemical results exhibit that the stable and reversible capacity of 547 mAh g{sup -1} is obtained after 50 cycles at 60 mA g{sup -1} (0.1 C) and the corresponding charge capacity is determined to be 316 mAh g{sup -1} at the current density of 2.5 C. Cyclic voltammetry and electrochemical impedance spectroscopy data are analyzed to complement the galvanostatic results. The observed excellent performance is attributed to the porous structure and large surface area of flowerlike CaSnO{sub 3}.

Energy Technology Data Exchange (ETDEWEB)

The effect of Mo addition as an alloying element to stainless steel alloys is investigated by capacitance (Mott Schottky approach), and photoelectrochemistry measurements. Complementary studies were made using Auger electron spectroscopy and X-ray photoelectron spectroscopy. The Mott-Schottky approach and the photoelectrochemical studies showed that the presence of Mo as an alloying element affects the semiconductive properties of the oxide films. The analytical results have shown that the oxide films formed on stainless steels are composed by an external Fe rich region and an inner Cr rich region. No significant amount of Mo was found in the outer layers of the film. The presence of Mo leads to an increase of the chromium content in the inner layers of the film, although without increasing the film thickness. (orig.) 30 refs.

British Library Electronic Table of Contents (United Kingdom)

The homogeneity of a helium dielectric barrier discharge, working at atmospheric pressure and containing oxygen as contaminant, is assessed by mapping the spatial distribution of oxygen metastable atoms in relation to the uniformity of surface properties. Tunable diode laser absorption spectroscopy is used to monitor the time evolution of the absorption coefficient corresponding to the oxygen metastable atoms on the 35S2 level, as a function of the laser absorbing path, whereas bi-dimensional Abel transform is used to obtain local information on the space distribution of the metastable atoms in the discharge. The radial distribution of the surface properties is investigated using atomic force microscopy, contact angle measurement and X-ray photoelectron spectroscopy. The results show that ...

Energy Technology Data Exchange (ETDEWEB)

Chemical characterization of passive films formed on AISI 304 austenitic stainless steel, in a borate/boric acid solution at pH 9.2, under various conditions of potential, temperature, and polarizations time, was made by Auger electron spectroscopy combined with ion sputtering, and x-ray photoelectron spectroscopy (XPS). The depth chemical composition, thickness, and duplex character of the passive layers were determined after processing AES sputter profiles by their quantitative approach based on the sequential layer sputtering model. Moreover, separated contributions of elements in their oxidized and unoxidized state could be disclosed from part to part of the oxide-alloy interface. The XPS study specified the chemical bondings which take placed inside the film, between Fe and oxygen (and water).

British Library Electronic Table of Contents (United Kingdom)

Bio-inspired palladium nanoparticles were synthesized by using banana peel extract (BPE), a non-toxic eco-friendly material. Boiled, crushed, acetone precipitated, air-dried peel powder was used to reduce palladium chloride. The palladium nanoparticles were characterized by using UV-Visible spectroscopy, scanning electron microscope-energy dispersive spectra (SEM-EDS) and X-ray diffraction (XRD) analysis. Dynamic light scattering (DLS) studies revealed the average size of nanoparticles to be 50nm. Fourier transform infra red spectroscopy (FTIR) implicated the role of carboxyl, amine and hydroxyl groups in the synthetic process. This paper thus describes a novel green method for the synthesis of palladium nanoparticles.

Energy Technology Data Exchange (ETDEWEB)

Sulfur K-edge X-ray absorption spectroscopy is a powerful in situ probe of sulfur biochemistry in intact cells and tissues. Under favorable circumstances the technique can provide quantitative information on the chemical identify of the sulfur species that are present in a sample. Prange et al. have recently reported an X-ray absorption spectroscopic study of bacterial sulfur storage globules. Unfortunately there are substantial problems with the experimental technique employed that, they contend, lead to completely erroneous conclusions. In the more recent of their two papers Prange et al. employed a curve-fitting method similar to that used by us (for more than 10 years). In essence, the method employs simply fitting a linear combination of the spectra of standard compounds to that of the unknown, in this case cultures of bacterial cells. This type of analysis can provide quantitative estimates of the individual sulfur ...

CERN Document Server

We present a detailed spectral analysis of point-like X-ray sources in the XMM-COSMOS field. Our sample of 135 sources only includes those that have more than 100 net counts in the 0.3-10 keV energy band and have been identified through optical spectroscopy. The majority of the sources are well described by a simple power-law model with either no absorption (76%) or a significant intrinsic, absorbing column (20%).As expected, the distribution of intrinsic absorbing column densities is markedly different between AGN with or without broad optical emission lines. We find within our sample four Type-2 QSOs candidates (L_X > 10^44 erg/s, N_H > 10^22 cm^-2), with a spectral energy distribution well reproduced by a composite Seyfert-2 spectrum, that demonstrates the strength of the wide field XMM/COSMOS survey to detect these rare and underrepresented sources.

International Nuclear Information System (INIS)

For the first time, rheological phase method, a simple and effective route, is applied to synthesize novel cathode material LiCoPO4. X-ray diffraction spectrometer (XRD), X-ray photoelectron spectrometer (XPS), transmission electron microscope (TEM) and electrochemical impedance spectroscopy (EIS) are taken to investigate this material, respectively. XRD figure shows that the rheological sample is better crystallized than the solid-state one. XPS result of the rheological sample exhibits that the valence of Co is 2+. TEM images show that better dispersed particles with smaller size can be formed by rheological method comparing to the solid-state route. Charge-discharge test is carried out in the range of 3.0-5.0 V at 0.2 mA cm-2. The initial discharge capacity for rheological phase and solid-state powder is 71.5 and 30.9 mAh g-1, respectively. The better electrochemical property should be ascribed to the better crystallized ...

Energy Technology Data Exchange (ETDEWEB)

Silver silica nanocomposites were obtained by the sol-gel technique using tetraethyl orthosilicate (TEOS) and silver nitrate (AgNO{sub 3}) as precursors. The silver nitrate concentration was varied for obtaining composites with different nanoparticle sizes. The structural and microstructural properties were determined by x-ray diffractometry (XRD), Fourier transform infrared spectroscopy (FTIR) and transmission electron microscopy (TEM). X-ray photoelectron spectroscopic (XPS) studies were done for determining the chemical states of silver in the silica matrix. For the lowest AgNO{sub 3} concentration, monodispersed and spherical Ag crystallites, with an average diameter of 5 nm, were obtained. Grain growth and an increase in size distribution was observed for higher concentrations. The occurrence of surface plasmon resonance (SPR) bands and their evolution in the size range 5-10 nm is studied. For decreasing nanoparticle ...

British Library Electronic Table of Contents (United Kingdom)

Homogeneous mixtures of Ce0.8Gd0.2O1.9 (GDC) and La0.6Sr0.4Co0.2Fe0.8O3 (LSCF) nanopowders were successfully synthesized using induction plasma by axial injection of a solution. The resulting nanocomposite powders consisted of two kinds of nanopowders with different mass ratio of GDC/LSCF, such as 3/7 and 6/4. The morphological features, crystallinity, and the phases of the synthesized powders were characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), local energy-dispersive x-ray spectroscopy (EDS) analysis, and x-ray diffraction (XRD). The nanopowders are almost globular in shape with a diameter smaller than 100?nm and their BET specific areas are around 20?m2?g?1. The GDC and LSCF phases are well distributed in the nanopowders. In addition, suspens...

British Library Electronic Table of Contents (United Kingdom)

Herein, we report engineering of nanostructured p-CuIn3Se5/n-CdS heterojunction thin film on a glass substrate, which is prepared at room temperature using simple wet chemical approach involving ion exchange reactions between CdS and Cu^+, In^3^+ and Se^2^- ions in alkaline medium. The uniform deposition of heterojunction thin films is achieved by optimizing the pH, temperature and molarity of the reactant bath. The as-deposited thin-films were annealed at 200^oC in air for 1h and further characterized for structural, optical and electrical properties using UV-Vis spectrophotometer, X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy (XPS), Hall effect for type of conductivity, and I-V measurement to investigate the char...

Science.gov (United States)

A knowledge of surface film growth kinetics can be quite useful in the production of materials for uses ranging from protective coatings to microelectronic devices. A technique for determining the kinetics of film growth is presented which should prove to be a valuable alternative to the array of spectroscopies (AES, RBS, etc.) currently favored for these measurements. Some of the virtues of this X-ray diffraction approach are its non-destructive nature, thickness resolution better than 50 {angstrom} and conventional equipment requirements. Results obtained for the growth of Pd{sub 2}Si films during thermal annealing of Pd coatings on Si, indicate parabolic growth over a temperature range of 160-222 C. The rate constant was found to be k{prime} = 7 {times} 10{sup {minus}4} exp ({minus}1.06 eV/kT) cm{sup 2}/sec, where (film thickness){sup 2} = k{prime} x time. This activation energy is in agreement with results obtained by other techniques. A ...

British Library Electronic Table of Contents (United Kingdom)

Monodisperse europium-activated titania hollow phosphors had been synthesized by a facile one-pot hydrothermal method using carbon spheres as hard templates. Samples were characterized by X-ray powder diffraction, transmission electron microscopy, X-ray photoelectron spectroscopy, energy dispersive spectrometer and photoluminescence spectrum. The strongest emission intensity was observed with TiO2:Eu0.2 hollow spheres and TiO2:Eu0.2 hollow spheres calcining at 550^oC. Moreover, the strongest excitation of TiO2:Eu0.2 hollow spheres transferred from 400 to 500^oC and the effective nonradiative energy transfer from the TiO2 hollow spheres host matrix to Eu^3^+ ions crystal field states was realized due to changes of crystalline field in the environment around Eu^3^+ ions occupying Ti^4^+ site...

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on iron metal, alloys or stainless steel are extremely thin oxides or hydroxides and possess the properties of high chemical stability in the environment. These films show characteristics interested both electrical as well as electrochemical point of view due to the thin thickness of the films. Auger Electron Spectroscopy, X-ray Photoelectron spectroscopy and so on which are the conventional electrochemical measurement methods or the surface analysis methods are used for the analysis and evaluation of these films, however, at present, the application of research technique focusing the superconductor characteristics of the films are tried. Although, the potential modulation reflection spectroscopy method has merits like possibility of in-situ measurement, high precision, possibility of stable analysis even for extremely thin film and so forth, it has also demerits like difficulty ...

Science.gov (United States)

The properties and kinetics of x-ray stars in globular clusters are described. Locations, configurations, star evolution, massive close binary systems, various mechanisms, and the x-ray burster properties are included. (JFP)

International Nuclear Information System (INIS)

ASTROSAT, India's first dedicated astronomy satellite is slated for launch in 2007. The primary science objective of ASTROSAT is to explore the Universe using broad-band instruments covering optical, UV, soft X-ray and hard X-ray studies

Energy Technology Data Exchange (ETDEWEB)

The X-ray photoacoustic spectra of copper and brass (64.7 wt.% Cu and 35.3 wt.% Zn) have been measured at XANES (X-ray absorption near-edge structure) regions using synchrotron radiation. These spectra were compared with optical density of X-ray spectra. It is shown that the information derived from XANES is also included in the X-ray photoacoustic spectrum which reflects the heat production processes in copper and brass. However, the results showed that the increases and changes of the photoacoustic signal were different from those of the X-ray absorption coefficient at XANES regions. (author).

International Nuclear Information System (INIS)

Hybrid organic-inorganic coatings with phosphonate functionalities have been synthesized and evaluated as prospective surface treatments for magnesium materials. These coatings have been processed via a sol-gel route by hydrolysis and condensation of a mixture of diethylphosphonatoethyltriethoxy-silane and tetraethoxy-silane with variable molar ratios. The coatings morphology and the surface chemistry at the coating/substrate interface have been characterized using scanning electron microscopy, X-ray photoelectron spectroscopy, "3"1P nuclear magnetic resonance spectroscopy, and time-of-flight secondary ion mass spectrometry. The corrosion protection performance of the coatings deposited on magnesium alloy AZ31B has been examined by a group of electrochemical techniques including potentiodynamic polarization and electrochemical impedance spectroscopy. In addition, a scanning Kelvin probe technique has ...

Science.gov (United States)

Mar 1, 2011 ... Radionuclide X-ray fluorescence analysis. 2: Detection of the X-ray fluorescence radiation excited by radionuclide radiation ...

Science.gov (United States)

Aug 1, 1972 ... The principles of radionuclide excitation of X-ray fluorescence radiation and its application in analytic chemistry are discussed.

International Nuclear Information System (INIS)

The future use of single-molecule magnets in applications will require the ability to control and manipulate the spin state and magnetization of the magnets by external means. There are different approaches to this control, one being the modification of the magnets by adsorption of small ligand molecules. In this paper we use iron phthalocyanine supported by an Au(111) surface as a model compound and demonstrate, using x-ray photoelectron spectroscopy and density functional theory, that the spin state of the molecule can be tuned to different values (S #approx# 0, 1/2, 1) by adsorption of ammonia, pyridine, carbon monoxide or nitric oxide on the iron ion. The interaction also leads to electronic decoupling of the iron phthalocyanine from the Au(111) support. (fast track communication)

Energy Technology Data Exchange (ETDEWEB)

Biosorption of elements is a little understood phenomenon exhibited by some types of even nonliving microbial biomass. A common fungus Rhizopus arrhizus has been reportd to take up uranium from adqueous solutions to the extent of 180 mg U/sup 6 +//g. The mechanism of uranium sequestering by this type of biomass was studied by using experimental techniques such as electron microscopy, x-ray energy dispersion analysis, IR spectroscopy, and supporting evidence was obtained for a biosorption mechanism consisting of at least three processes. Uranium coordination and adsorption in the cell-wall chitin structure occur simultaneously and rapidly whereas precipitation of uranylhdroxide within the chitin microcrystalline cell-wall structure takes place at a lower rate. Interference of Fe/sup 2/ and Zn/sup 2 +/ coions with uranium biosorption is indicated.

British Library Electronic Table of Contents (United Kingdom)

A novel difunctional acylhydrazone has been synthesized by the reaction of 5-methylisoxazole-4-carboyl hydrazine with benzaldehyde and characterized by X-ray crystallography and spectroscopy. The obtained results demonstrate the crystal belongs to triclinic, space group Formula Not Shown . Moreover, the spectroscopic properties were evaluated through density functional theory (DFT) and time-dependent density functional theory (TD DFT) calculations. The results reveal that UV-Vis absorption peaks at 194, 217.5 and 290.5nm are mainly attributed to (p, p)p*, partly (p, p)p* and partly pp*, and predominantly pp*, respectively, with intraligand charge-transfer transition (ILCT) character. The fluorescence emission peak at 485.96nm should be assigned to ILCT. In addition, the results of antibact...

Energy Technology Data Exchange (ETDEWEB)

LiNi{sub 0.8}Co{sub 0.2}O{sub 2} particles from high-power lithium-ion cells were examined to determine material changes that result from accelerated aging tests. X-ray absorption spectroscopy (XAS) and transmission electron microscope (TEM) data indicated a Li{sub x}Ni{sub 1-x}O-type layer on the particle surfaces. The greater thickness on particles from high-power fade cells indicate that these surface layers are a significant contributor to cathode impedance rise observed during cell tests.

Energy Technology Data Exchange (ETDEWEB)

To study the effect of CuO on the electrochemical properties of MgNi alloy, the MgNi-xCuO (x = 3, 5 and 10 wt%) composites were prepared by ball-milling method. The X-ray diffraction (XRD) analysis showed that the structures of the composites were amorphous. The cycle stability of the composites was improved compared to pure MgNi alloy due to the enhancement of the anti-corrosion property in the alkaline electrolyte, and the composite with 5 wt% CuO ball-milled for 15 h exhibited the best performance. Electrochemical impedance spectroscopy (EIS) and potential-step measurements indicated that the electrochemical kinetics of the composites was improved.

British Library Electronic Table of Contents (United Kingdom)

Soluble starch?based biodegradable and microporous microspheres (SDM-Ms) were prepared by emulsion chemical cross-linking technique using trisodium trimetaphosphate (TSTP) as the cross-linker. The resultant amorphous SDM-Ms were excellently identified by scanning electron microscopy (SEM), X-ray diffraction (XRD), and Fourier transform infrared spectroscopy (FT-IR). The internal rupture and surface-controlled erosion were the predominant degradation mechanisms for SDM-Ms. The obtained SDM-Ms were applied to adsorb coix seed oil (CSO) by immersing method. The adsorption capacity of CSO within SDM-Ms was determined, namely 0.5238?g/g, and the thermal stability was shown higher than that of the free CSO. A burst release appeared in the second hour, followed by controlled release. Diffusion, d...

International Nuclear Information System (INIS)

Experimentally, a feasibility study for adsorption and catalytic pyrolysis of spill oils on Cu/ZSM-5 for recycling of light oils has been conducted in the present work. The adsorption and pyrolysis of model compounds such as heptane, toluene, and diesel (to stimulate the spill oils) on Cu/ZSM-5 have been investigated on a continuous fixed-bed reactor. By component fitted X-ray absorption near edge structural (XANES) spectroscopy, catalytic active species such as metallic copper (Cu) (77-84%) and Cu2O (6-7%) are found in the channels of ZSM-5 during pyrolysis of heptane or toluene. Pyrolysis of diesel effected by Cu/ZSM-5 yields gas (C1-C5) (32%) and light oil (68%) that can be used as auxiliary fuels.

International Nuclear Information System (INIS)

A kind of polymer-metal complex gel electrolyte is successfully prepared and is used in dye-sensitized solar cells. Raman and X-ray photoelectron spectroscopy confirm the structure of this complex and is found that the metal ion reacts with nitrogen in the polymer. This novel electrolyte shows apparent diffusion coefficient of iodide of 8.37 x 10-7 cm2 s-1 and the energy conversion efficiency of 6.10% when the amount of ZnI2 is 0.04 M. By studying the dissociation active energy of the inorganic salt in electrolytes, we find that the metal salts can dissociate more easily after reacting with polymer and as a result can provide extra free iodide ion. The cell maintains ca. 93% of its initial efficiency after 20 d without further sealing, which shows good long-time stability.

Energy Technology Data Exchange (ETDEWEB)

Thin passive layers of uranium nitride were formed by nitriding pure metallic uranium in non-equilibrium, low pressure radio-frequency plasma of nitrogen. Plasma nitriding at low substrate temperature of 230 C-250 C was found to cause the formation of adherent layers of uranium sesquinitride ({alpha}-U{sub 2}N{sub 3}) which provide a considerable protection against hydrogen attack. The characteristics of these passivation layers were determined by X-ray diffraction and Auger electron spectroscopy. The incipient hydriding kinetics of the plasma-treated samples were compared with those of untreated and nitrogen-ion implantation ones, utilizing a hot-stage microscope that was monitored continuously with a TV camera and videotape. (orig.)

British Library Electronic Table of Contents (United Kingdom)

Commercially available organoclay (Closite 30B) was modified by using 3-aminopropyltriethoxysilane (APS) via a silylation reaction. Sodium clay (Closite Na) was treated by APS directly as a control. Such modified clays were further melt-compounded with polybutylene terephthalate (PBT). The morphology and properties of the modified organoclays were characterized with X-ray diffraction (XRD), transmission electrical microscopy (TEM), Infra-red spectroscopy, contact angle measurement, and thermogravimetric analysis (TGA). The effects of modified clays on the crystallization behavior of PBT were characterized by differential scanning calorimetry. The basal spacing of Closite Na was enlarged from 1.01 to 1.41 nm after APS treatment, indicating that the APS was intercalated into the clay interga...

British Library Electronic Table of Contents (United Kingdom)

Regularities of deformation-induced dissolution of a surface layer of iron oxides in matrixes of iron-based alloys with bcc and fcc lattices have been studied by the methods of M?ssbauer spectroscopy, transmission electron microscopy, and X-ray diffraction. A method of producing iron alloys strengthened by dispersed oxide nanoparticles and alloyed with elements possessing a high affinity to oxygen (titanium and yttrium) has been proposed, which implies a dynamic dissolution of a surface layer of iron oxides upon strong cold deformation and a precipitation of secondary yttrium and titanium nanooxides upon a subsequent high-temperature sintering of mechanically alloyed powders. There has been demonstrated a possibility of oxide strengthening of pure iron upon its interaction with air without...

International Nuclear Information System (INIS)

Fe-Cr amorphous films have been formed by both in situ evaporation of multilayered films and ion beam mixing in a target chamber of a 200 keV implanter. The effects of Cr content and ion irradiation on the amorphization of films were examined by transmission electron microscope (TEM). Corrosion of film was investigated by means of a potential dynamic polarization. Corrosion resistance of amorphous film in 0.5 mol H-2SO-4 solution is considerably increased than that of pure iron. Using X ray photoelectron spectroscopy (XPS) corrosion resistance in atmosphere of amorphous Fe-Cr passive films formed by P"+ mixing was studied. Results show that the richness of Cr and P exist at the surface of Fe-Cr film.

Energy Technology Data Exchange (ETDEWEB)

Hybrid electric vehicles (HEV) need long-lived high-power batteries as energy storage devices. Batteries based on lithium-ion technology can meet the high-power goals but have been unable to meet HEV calendar-life requirements. As part of the US Department of Energy's Advanced Technology Development (ATD) Program, diagnostic studies are being conducted on 18650-type lithium-ion cells that were subjected to accelerated aging tests at temperatures ranging from 40 to 70 C. This article summarizes data obtained by gas chromatography, liquid chromatography, electron microscopy, X-ray spectroscopy and electrochemical techniques, and identifies cell components that are responsible for the observed impedance rise and power fade.

British Library Electronic Table of Contents (United Kingdom)

A sensitive hydrogen peroxide (H2O2) sensor was fabricated based on graphene-Pt (GN-Pt) nanocomposite. The GN-Pt was synthesized by photochemical reduction of K2PtCl4 on GNs, and characterized by atomic force microscope (AFM), transmission electron microscope (TEM), and energy-dispersive X-ray spectroscopy (EDS). Electrochemical investigations indicated that the GN-Pt exhibited a high peak current and low overpotential towards the reduction of H2O2. The GN-Pt modified glass carbon electrode displayed a wide linear range (2-710mM), low limit of detection (0.5mM) and good selectivity for detection of H2O2 with a much higher sensitivity than that of Pt nanoparticles or graphene modified electrode.

Energy Technology Data Exchange (ETDEWEB)

Organic/metal interface properties are of high interest for the application of molecular (sub)monolayers to modify surface properties. They are applied for, e.g., molecular electronics, chemical sensing, or the tuning of injection barriers in organic electronic devices. We present a joint theoretical and experimental study of F{sub 4}TCNQ adsorbed on Cu(111). The electronic and structural properties were determined by ultraviolet photoelectron spectroscopy (UPS) and X-ray standing wave (XSW) measurements. To better understand the complex process of binding, we modelled the system using density-functional theory. We find forward-donation from the lone pairs of the molecule into metallic states and back-donation from the metal into the LUMO of the molecule. The data on Cu(111) are compared to F4TCNQ on Au(111) and Ag(111) as well as to investigations of pyrenetetraone on various coinage metals.

International Nuclear Information System (INIS)

Passive films formed on Alloy 690 in high-temperature alkaline environments were investigated by potentiodynamic polarization, X-ray photoelectron spectroscopy, transmission electron microscopy and Mott-Schottky approach. Passive current density and donor density of the passive films increase with increasing temperature, due to increased diffusion rates of metallic ions and dehydration of hydroxide phases. The passive films show a duplex structure including an inner layer of fine-grained Cr oxide or spinel oxide and an outer layer of Ni-Fe spinel oxide and Ni hydroxide. A growth model of the passive films on Alloy 690 in high-temperature alkaline environments is proposed and discussed.

British Library Electronic Table of Contents (United Kingdom)

Polyacrylonitrile (PAN)-based carbon fabric (CF) was modified with strong HNO3 oxidation and then introduced into polyimide (PI) composites. The friction and wear properties of the carbon fabric reinforced polyimide composites (CFRP), sliding against GCr15 stainless steel rings, were investigated on an M-2000 model ring-on-block test rig under dry sliding. Experimental results revealed that the carbon fiber surface treatment largely reduced the friction and wear of the CFRP. Compared with the untreated ones, the surface-modified CF can enhance the tribological properties of CFRP efficiently due to the improved adhesion between the CF and the PI matrix. Scanning electron microscope (SEM) and X-ray photoelectron spectroscopy (XPS) study of the carbon fiber surface showed that the fiber surfa...

International Nuclear Information System (INIS)

Reducing count losses and pile-up pulse effects in quantitative and qualitative analysis is necessary for accuracy of analysis. Therefore, the optimum peaking time for particular detector systems is important. For this purpose, pure Se and Zn elements were excited by 59.5 keV ?-rays from a 50 mCi 241Am annular radioactive source in this study. The characteristic x-rays emitted from pure Se and Zn elements were detected by using an ultra low energy Ge (Ultra-LEGe) detector connecting Tennelec TC 244 spectroscopy amplifier at different peaking time modes. Overall pulse widths were determined by HM 203-7 oscilloscope connecting amplifier. The proper peaking time for ultra low energy germanium detector (Ultra-LEGe) is determined about 4 ?s.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction, infrared spectroscopy, thermal analysis, scanning electron microscopy, and particle size analysis were used to characterize the product of the thiosulfate process. It was found to consist of a mixture of a solid solution of calcium sulfate in calcium sulfite hemihydrate, calcium sulfate dihydrate, and calcium carbonate. Reactions taking place on heating the byproduct were identified in oxidizing and reducing atmospheres. Pure calcium sulfite hemihydrate as well as solid solutions of CaSO[sub 4] in CaSO[sub 3] [center dot] (1/2)H[sub 2]O with different sulfate concentrations were synthesized in the laboratory. Thermal analyses of pure solid solutions proved that the higher the sulfate content, the higher is the dehydration temperature. Accordingly, taking SO[sub 4][sup 2[minus

British Library Electronic Table of Contents (United Kingdom)

In this paper, it is shown that (In1?xAlx)2S3 thin films can be grown through the co-evaporation of elemental indium, aluminum and sulfur. It is nevertheless observed that the introduction of aluminum within the indium sulfide thin films hinders the crystallites size and even yields almost amorphous films when x is 0.2. The investigations of the optical properties of the films reveal that contrary to what could be expected, the band gap increase is low; the highest values measured do not exceed 2.2eV. However, as suggested by X-ray photoelectron spectroscopy measurements, such widening most probably affects the lower conduction band states.

British Library Electronic Table of Contents (United Kingdom)

A ferritic steel with finely dispersed precipitates was investigated to reveal the fundamental strengthening mechanisms. The steel has a yield strength of 760MPa, approximately three times higher than that of conventional Ti-bearing high strength hot-rolled sheet steels, and its ultimate tensile strength reaches 850MPa with an elongation-to-failure value of 18%. Using energy dispersive X-ray spectroscopy (EDXS) and transmission electron microscope (TEM), fine carbides TiC with an average diameter of 10nm were observed in the ferrite matrix of the 0.08%Ti steel, and some cubic M23C6 precipitates were also observed at the grain boundaries and the interior of the grains. The finely dispersed TiC precipitates in the matrix provide matrix strengthening. The estimated magnitude of precipitation ...

Energy Technology Data Exchange (ETDEWEB)

Here we examine Fe speciation within Fe-encrusted biofilms formed during 2-month seafloor incubations of sulfide mineral assemblages at the Main Endeavor Segment of the Juan de Fuca Ridge. The biofilms were distributed heterogeneously across the surface of the incubated sulfide and composed primarily of particles with a twisted stalk morphology resembling those produced by some aerobic Fe-oxidizing microorganisms. Our objectives were to determine the form of biofilm-associated Fe, and identify the sulfide minerals associated with microbial growth. We used micro-focused synchrotron-radiation X-ray fluorescence mapping (mu XRF), X-ray absorption spectroscopy (mu EXAFS), and X-ray diffraction (mu XRD) in conjunction with focused ion beam (FIB) sectioning, and highresolution transmission electron microscopy (HRTEM). The chemical and mineralogical composition of an Fe-encrusted biofilm was queried at ...

International Nuclear Information System (INIS)

Brief item.

International Nuclear Information System (INIS)

Global angular momentum balance suggests that the neutron stars in Be/X-ray binaries are not spinning in equilibrium. This requires an X-ray lifetime ''approx <'' 10"5 yr, and suggests that there are many 'dead' Be/X-ray binaries in the Galaxy. Some of these may be turned up as millisecond radio pulsars with Be star companions. (author).

International Nuclear Information System (INIS)

Published in summary form only.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

Examples are given of the applicability and importance of radionuclide fluorescence analysis as a

International Nuclear Information System (INIS)

X-ray imaging is a very useful plasma diagnostic method. A theoretical analysis of the x-ray phase imaging in the method based on Fresnel diffraction is given. The authors show it is a linear band pass filter, a property suit for Rayleigh-Taylor (R-T) instability measurement. The evaluation permits the possibility of R-T instability measurement in x-ray phase imaging

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

... such as renal flow scan or a formal kidney X-ray, called an intravenous pyelogram ( IVP ), may help ...

International Nuclear Information System (INIS)

Published in summary form only.

Energy Technology Data Exchange (ETDEWEB)

ZnO thin films were electrodeposited in aqueous solution on gilded p-type Si wafer substrates. Thermal treatments were carried out on different films in Ar atmosphere at different temperatures, between 200 and 600 {sup 0}C. Surface morphology studies using scanning electron microscopy and atomic force microscopy show a smooth surface for an annealing temperature of 400 {sup 0}C with a roughness mean square value of about 15 nm and a precipitation of ZnO microcrystals on the deposit surface at 600 {sup 0}C. X-ray diffraction experiments reveal a decrease in the c-parameter value from 5.223 to 5.206 A after treatment at 600 {sup 0}C, due to the removal of hydrogen from the film. Raman spectroscopy analyses show an improvement in the crystal quality of the film and a decrease in the compressive stress inside the deposit. Photoluminescence observations reveal an important change in the UV emission band after annealing at 200 {sup 0}C. A visible ...

International Nuclear Information System (INIS)

In this work, ?-SnS2 thin films have been prepared on glass substrates by the spray pyrolysis technique using an alcohol solution which contains tin chloride (SnCl4) and thiourea (SC(NH2)2) as precursors. The structural study shows that ?-SnS2 thin film prepared using optimal experimental conditions: substrate temperature Ts = 280 deg. C and the concentration ratio of sulfur and tin elements in the spray solution x = [S]/[Sn] = 2.5, crystallizes in the hexagonal phase with a strong (0 0 1) X-ray diffraction line. In the same way, microprobe analyses (EPMA) as well as X-ray photoelectron spectroscopy (XPS) show the presence of undiserable phase of SnO2. From the transmission and reflectance spectra, the band gap energy is 2.65 eV. On the other hand, the photothermal properties of such films have been studied, the thermal conductivity was Kc = 0.85 W m-1 K-1 and the thermal diffusivity was Dc = 14.5 x 10-6 m2 s-1. The ...

Energy Technology Data Exchange (ETDEWEB)

This award provided for an automated computer-controlled goniometer/diffractometer/manipulator with hot and cold stages and data acquisition system that was interfaced with the high resolution Scienta ESCA-300 X-ray photoelectron spectrometer at Lehigh University. The automation allows angular dependent X-ray photoelectron spectroscopy (XPS) and ultraviolet photoelectron spectroscopy (UPS) data to be accurately and rapidly collected without the very time-consuming and labor-intensive manual method that was previously required. It also provides for automated multi-sample analyses, collecting both wide survey scans and selected binding energy range analyses, with complete computer control and data storage. This allows 24 hour data collection without requiring the continuous presence of operators. The overall result is a greater productivity for the XPS laboratory, approximately doubling the output of the ...

International Nuclear Information System (INIS)

Free Electron Laser (FEL) with the wide wavelength tunability has been developed and used for various applications. The FEL gives high efficiency for the photo-induced ablation when the laser is tuned to an absorption maximum of the target. The FEL was tuned to 9.4 #mu#m, which is an absorption maximum of phosphoric acid ion, a known major component of dentine. The FEL pulse length was several ps. The average output power was varied from 5 to 20 mW by filters. The change of irradiated dentine surface was analyzed by mass spectroscopy and Energy Dispersive X-ray (EDX) spectroscopy. Positive ions which correspond to Na"+, CO_3"+ and many phosphoric acid ions were measured. It was found that atomic ratio of P/Ca had reduced from 0.65-0.60. The atomic ratio of P/Ca, however had not changed with irradiation by Er:YAG laser (2.9 #mu#m), or CO_2 laser (10.6 #mu#m). These results indicate the selective ablation of phosphoric acid ...

CERN Document Server

We construct a sample of low-redshift Ly-alpha emission-line selected sources from GALEX grism spectroscopy of nine deep fields to study the role of Ly-alpha emission in galaxy populations with cosmic time. Our final sample consists of 122 (142) sources selected in the redshift interval z=0.195-0.44 (z=0.65-1.25) from the FUV (NUV) channel. We classify the Ly-alpha sources as AGNs if high-ionization emission lines are present in their UV spectra and as galaxies otherwise. These classifications are broadly supported by comparisons with X-ray and optical spectroscopic observations. We classify additional sources as AGNs using line widths for our Ly-alpha emitter (LAE) analysis. Defining the GALEX LAE sample in the same way as high-redshift LAE samples, we show that LAEs constitute only about 5% of NUV-continuum selected galaxies at z~0.3. We also show that they are less common at z~0.3 than they are at z~3. We find that the z~0.3 ...

Energy Technology Data Exchange (ETDEWEB)

The objective of this work was to investigate the efficiency of imidazole derivatives for corrosion inhibition of copper in 0.5 M hydrochloric acid. Corrosion inhibition was studied using impedance spectroscopy. Imidazole and its derivatives 4-methylimida-zole, 4-methyl-5-hydroxymethylimidazole, 1-phenyl-4-methylimidazole, 1-(p-tolyl)-4-methylimidazole were investigated. These studies have shown that 1-(p-tolyl)-4-methylimidazole is the best inhibitor in this series and that it acts as mixed inhibitor. The nature of the chemical interaction between these molecules and the copper surface was investigated by Cu exposed to solutions having two very different pH values: 0.5 M HCl and unbuffered purified water. X-ray photoelectron spectroscopy and secondary ion mass spectrometry were used to explore the nature of the interaction. Possible mechanisms of corrosion inhibition for these molecules are discussed.

International Nuclear Information System (INIS)

The fundamental optical properties of dysprosium (Dy) doped strontium sulfide bulk samples for various dopant concentrations from 0.1 to 1.0 at.% were investigated by X-ray diffraction (XRD), electron paramagnetic resonance spectroscopy (EPR), room temperature photoluminescence (PL), photoluminescence excitation (PLE) and diffuse reflectance spectroscopy (DRS). Investigations by electron paramagnetic resonance yielded the state of Dy in the sample as Dy3+. An additional ESR line due to F+ center was observed. The PL emission spectrum consisted of several intense lines and a number of weaker ones which were identified as transitions between energy levels of Dy3+. The optimum doping concentration for maximum intensity was found to be 0.25 at.%. Blue shift of the absorption edge energy and red shift of the PLE spectrum were observed with increasing doping concentration. The former is due to Burstein-Moss (BM) effect and the ...

British Library Electronic Table of Contents (United Kingdom)

Abstract We prepared BiOCl1-xBrx (x=0-1) solid solutions and characterized their structures, morphologies, and photocatalytic properties by X-ray diffraction, diffuse reflectance spectroscopy, scanning electron microscopy, Raman spectroscopy, photocurrent and photocatalytic activity measurements and also by density functional theory calculations for BiOCl, BiOBr, BiOCl0.5Br0.5. Under visible-light irradiation BiOCl1-xBrx exhibits a stronger photocatalytic activity than do BiOCl and BiOBr, with the activity reaching the maximum at x=0.5 and decreasing gradually as x is increased toward 1 or decreased toward 0. This trend is closely mimicked by the photogenerated current of BiOCl1-xBrx, indicating that the enhanced photocatalytic activity of BiOCl1-xBrx with respect to those of BiOCl and BiO...

International Nuclear Information System (INIS)

Careful sample preparation and secondary ion mass spectroscopy have been used to characterize arsenic dose loss to the silicon-oxide interface. Using high resolution x-ray photoelectron spectroscopy for microprofiling, we have directly observed the pileup of arsenic at the silicon dioxide-silicon interface. At least half of the pileup is shown to be on the silicon side of the interface in the first monolayer of silicon. Monolayer chemical oxidation and etching are successfully used to profile this pileup in silicon. This pileup contains most of the arsenic dose loss that occurs during transient enhanced diffusion. This result is crucial to correctly model the dose loss and provides physical justification for using a trap/detrap model at the interface, which is necessary to account for the fact that the arsenic surface concentration remains constant during an anneal and the fact that the dose loss is partially reversible. ...

International Nuclear Information System (INIS)

The electrochemical behaviour of passive films formed on one austenitic stainless steel (AISI 304) and one ferritic stainless steel (AISI 446) in solutions with pH between 0.6 and 8.4 was studied by capacitance measurements and photocurrent spectroscopy. Compositional characterization of the passive films was done by X-ray photoelectron spectroscopy. The capacitance increases with decreasing pH. Doping densities evaluated from Mott-Schottky plots are in the range 2-6 x 10"2"0 cm"-"3 and increased with the pH in the neutral/alkaline range while in pH 0.6, values above 10"2"1 cm"-"3 were found. The bandgap energy indicates two transitions, at 2.5-2.8 and 3.2 eV. The analytical data reveal that, as the pH increased, the films become enriched in Fe(II) and Fe(III), whereas the Cr(III) gradually decreases. The films formed at very low pH had a behaviour that contrasts with that of the films formed in the neutral/alkaline media. ...

Energy Technology Data Exchange (ETDEWEB)

Natural, formaldehyde-treated and copolymer-grafted orange peels were evaluated as adsorbents to remove lead ions from aqueous solutions. The optimum pH for lead adsorption was found to be pH 5. The adsorption process was fast, reaching 99% of sorbent capacity in 10 min for the natural and treated biomasses and 20 min for the grafted material. The treated biomass showed the highest sorption rate and capacity in the batch experiments, with the results fitting well to a pseudo-first order rate equation. In the continuous test with the treated biomass, the capacity at complete exhaustion was 46.61 mg g{sup -1} for an initial concentration of 150 mg L{sup -1}. Scanning electronic microscopy and energy dispersive X-ray spectroscopy indicated that the materials had a rough surface, and that the adsorption of the metal took place on the surface. Fourier transform infrared spectroscopy revealed that the functional groups ...

International Nuclear Information System (INIS)

The author's achievements in the title field are summarized and discussed. The following topics are dealt with: (i) principles of radionuclide X-ray fluorescence analysis; (ii) mathematical methods in X-ray fluorescence analysis; (iii) Ross differential filters; (iv) application of radionuclide X-ray fluorescence analysis in the coal industry (with emphasis on the determination of the ash content, sulfur content, and arsenic content of coal); and (v) evaluation of the X-ray fluorescence analyzer from the radiological safety point of view. (P.A.).

Energy Technology Data Exchange (ETDEWEB)

Discusses methods for determining ash content in coal using backscattering in X-ray fluorescence. The following aspects are evaluated: principle of ash content determination, energy sources, factors that influence measurement accuracy, reliability. Types of X-ray fluorescence analyzers developed in Czechoslovakia and manufactured in the Czech Republic are comparatively evaluated. Operation of the RPM 113.1 radionuclide X-ray fluorescence analyzer developed by the PAR company and used for measuring ash content in coal and coal calorific value is discussed. 7 refs.

International Nuclear Information System (INIS)

Phase contrast X-ray imaging has been studied intensively using X-rays from synchrotron radiation and micro-focus X-ray tubes. However, these studies have revealed the difficulty of this technique's application to practical medical imaging. We have created a phase contrast imaging technique using a molybdenum X-ray tube with a small focal spot size for mammography. We identified the radiographic conditions in phase contrast magnification mammography with a screen-film system, where edge effect due to phase contrast overcomes geometrical unsharpness caused by the 0.1 mm-focal spot of a molybdenum X-ray tube. The edge enhancement due to phase imaging was observed in an image of a plastic tube, and then geometrical configuration of the X-ray tube, the object and the screen-film system was determined for phase imaging of mammography. In order to investigate a ...

International Nuclear Information System (INIS)

After having discussed the peculiarities of children in X-ray diagnosis the application of the effective as well as the mean equivalent doses as to the determination of the radiation exposure in children is represented. In using computerized tomograms to determine position and extent of an organ the exposure by repeated X-raying was calculated referring to the entrance dose. Entrance dose measurements for all types of X-ray examination in hospitals and ascertainments of the frequency of radiograms in 20 X-ray departments were used to determine per capita and collective doses, resp., in several age groups. Alltogether, the per capita dose of children in the GDR amounts to 30% of that of adults. Conclusions were drawn as to taking measures to further reduction of radiation exposure: (1) Technical measures, such as positioning of patients, shielding of organs, quality assurance; (2) elaboration of ...

Energy Technology Data Exchange (ETDEWEB)

A number of diagnostic X-ray units in Poland were subjected to analysis. The air kerma on X-ray tables was measured for the X-ray parameters used routinely during lumbo-sacral spine radiography of standard adult patient. Measurements of air kerma were performed using TLD made of lithium-fluoride. The doses received by patients in different X-ray departments can differ more than two orders of magnitude (from 0.42 mGy up to 72.11 mGy), for the same X-ray examination. The dose can be significantly reduced if fluorescent screens made from components of rare earth are used. (author). 10 refs, 1 fig., 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

Several Mg-Y binary ribbons with Y content up to {approx}17.9 at.% were fabricated by melt-spinning. X-ray diffraction (XRD) revealed that the phase structure changes with increasing Y content from extended solid solution to partially amorphous, and then fully intermetallic Mg{sub 24}Y{sub 5}. Anodic potentiodynamic polarization performed in 0.01 M NaCl electrolyte (pH=12) revealed improved anodic passivity behavior compared to pure Mg for all the Mg-Y alloys. X-ray photoelectron spectroscopy (XPS) revealed that the improved passivity of Mg-Y was more related to the elemental oxidation state rather than the concentration of the surface components. To study the effect of Cl{sup -} ion on the passivity behavior, anodic potentiodynamic and potentiostatic polarization were performed on Mg-17.9 at.% Y in alkaline (pH=12) NaCl electrolytes containing Cl{sup -} ion in the concentration range from 0.00 to 0.50 M. The passive films ...

Energy Technology Data Exchange (ETDEWEB)

In order to understand the chemistry of altermetal dopants in antimony oxide, the detailed structural characterization of two ..beta..-Sb/sub 2/O/sub 4/ compounds is reported, Mo-doped ..beta..-Sb/sub 2/O/sub 4/ (1.5 metal%) and V-doped ..beta..-Sb/sub 2/O/sub 4/ (5 metal%). The methods used to characterize these materials are X-ray and neutron diffraction, scanning electron microscopy, Mo K-edge extended X-ray absorption fine structure spectroscopy, and elemental analysis. The atomic position of each of these dopants in Sb/sub 2/O/sub 4/ is radically different as is the overall effect on the host structure. Molybdenum does not substitute for Sb atoms, rather the Mo atoms are found in channels of electron density formed by Sb/sup 3 +/ lone pairs. The two nearest Sb/sup 3 +/ are absent and the oxygen stoichiometry is preserved. The formula is Sb/sub 1.97/Mo/sub 0.015/O/sub 4/. Vanadium incorporates substitutionally for the ...

International Nuclear Information System (INIS)

Using the full potential linearized augmented plane wave (FLAPW) method, the magnetic properties of two-dimensional Ru and Rh monolayers (MLs) on a NiAl(001) surface have been investigated. It has been found that free standing one monolayer Ru and Rh films have ferromagnetic ground state with magnetic moments of 2.21 and 1.48 #mu#_B, respectively. The ferromagnetism is still observed even on a Ni terminated NiAl(001) surface, while no magnetic state is found on an Al terminated surface. The calculated magnetic moments of Ru and Rh atoms are 1.56 and 0.88 #mu#_B, respectively. In addition, an induced magnetic moment in surface Ni is observed. It has been found that the free standing Ru film has perpendicular magnetization to the film surface with a magnetocrystalline anisotropy (MCA) energy of 0.66 meV/atom, while an in-plane MCA energy of 0.37 meV/atom is achieved in Rh film. Very interestingly, we find that both Ru/NiAl(001) and Rh/NiAl(001) films have perpendicular magnetic ...

Science.gov (United States)

Five hydrated inorganic divalent cations, Mg[sup 2+], Co[sup 2+], Ni[sup 2+], Cu[sup 2+], and Zn[sup 2+], have successfully been used as templates for the synthesis of manganese oxide octahedral molecular sieves (OMS-1) having the todorokite structure. The OMS-1 samples have been well characterized by X-ray diffraction, differential scanning calorimetry, thermogravimetric analysis, scanning electron microscopy/energy dispersive X-ray studies, inductively coupled plasma analysis, electron paramagnetic resonance, Fourier transform infrared spectroscopy, thiosulfate titration, and cyclohexane sorption. Catalytic CO oxidation and 2-propanol decomposition were carried out. Results show that these OMS-1 samples with a tunnel size of about 6.9 angstroms are crystalline and chemically pure. They have the following formulas: Mg[sub 3.17]Mn[sub 5.05]O[sub 12] [center dot] 4.52H[sub 2]O, Co[sub 1.84]Mn[sub 5.59]O[sub 12] [center dot] ...

Energy Technology Data Exchange (ETDEWEB)

Electrodeposited Zn alloys with Fe group metals are known to be more resistant than pure Zn. However, the role of the corrosion products on the corrosion inhibition is not considered up to date. The aim of the present work was to examine the composition of corrosion products, which form on the Zn and Zn alloy surfaces under atmospheric corrosion conditions up to 3 year of exposure, trying to correlate it with the differences in their corrosion resistance. Zn corrosion products have been characterized by X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). Corrosion film composition was determined to depend on the sample exposure she, as well on the coating type. During the initial exposure stages oxide film was found to be the principal reaction product (XPS data), which in marine station consists from hydroxide phase exceptionally, while in urban one, contain up to 6-12 % of oxide. Succeeding corrosion ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline zeolites with discrete crystal sizes of less than 100 nm have different properties relative to zeolites with larger crystal sizes. Nanocrystalline zeolites have improved mass transfer properties and very large internal and external surface areas that can be exploited for many different applications. The additional external surface active sites and the improved mass transfer properties of nanocrystalline zeolites offer significant advantages for selective catalytic reduction (SCR) catalysis with ammonia as a reductant in coal-fired power plants relative to current zeolite based SCR catalysts. Nanocrystalline NaY was synthesized with a crystal size of 15-20 nm and was thoroughly characterized using x-ray diffraction, electron paramagnetic resonance spectroscopy, nitrogen adsorption isotherms and Fourier Transform Infrared (FT-IR) spectroscopy. Copper ions were exchanged into nanocrystalline NaY to increase the ...

International Nuclear Information System (INIS)

TlGaSe_2 compound belongs to group of layered semiconductors of A"3B"3C_2"6-type. Photoelectric and optical properties of TlGaSe_2 single crystals were investigated in detail. Influence of gamma-, electron and neutron radiation on photoelectric properties of TlGaSe_2 single crystals is investigated too. The present work deals with experimental results relative to X-ray dosimetric characteristics of TlGaSe_2 crystals at 300 K. X-ray conductivity and X-ray dosimetric characteristic measurements are carried out in low load resistance regime. The source of X-ray radiation is the installation of X-ray diffraction analysis (URS-55a) with the BCV-2(Cu). Intensity of X-ray radiation (E) is regulated by measurement with current variation in tube at each given value of X-ray radiation dose E (R/min) are measured by crystal dosimeter DRGZ-02. ...

UK PubMed Central (United Kingdom)

Microplanar beam radiation therapy has been proposed to treat brain tumors by using a series of rapid exposures to an array of parallel x-ray beams, each beam having uniform microscopic thickness and...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Radionuclide X-ray fluorescence analysis was used for the determination of iron, calcium, potassium, copper, manganese and zinc in waste water from the production process of citric acid.

International Nuclear Information System (INIS)

Exact anatomic knowledge about the location of the gonads and the application of corresponding measures of radiation protection are the preconditions for an efficient reduction of the danger of a possible genetic damage as a result of radiation exposition during X-ray examination of the hip joint of newborns. (VJ).

International Nuclear Information System (INIS)

The optoelectronic compounds of GaAs and ZnSe are difficult to analyze by PIXE (particle-induced X-ray emission) due to the strong absorption of the As and Se K_#alpha# X-rays. As part of a program to investigate optoelectronic materials using ion beam techniques, we have explored the possibility of using the high sensitivity of PIXE to check these materials for stoichiometry and dopant concentrations. The K_#alpha# X-ray intensity ratios of Ga to As and Zn to Se have been investigated using H beams of 0.5 to 2.5 MeV and He beams of 1.0 to 2.5 MeV. The variation in the X-ray intensity ratio with beam energy and target thickness is modelled in terms of the cross section for X-ray production and the absorption coefficients of the X-rays in the target. The results of this model show the experimental conditions that must be satisfied in order that the ...

UK PubMed Central (United Kingdom)

An examination of the noise of polycrystalline silicon thin film transistors, in the context of flat panel x-ray imager development, is reported. The study was conducted in the spirit of exploring...Full Text Available

UK PubMed Central (United Kingdom)

In this paper, we report a method of precise in situ x-ray scattering measurements on protein solutions using small stationary sample cells. Although reduction in the radiation damage...Full Text Available

International Nuclear Information System (INIS)

Differential phase-contrast X-ray imaging has been performed in a Talbot-Lau configuration, where a multiline X-ray source was used instead of a combination of a hard-X-ray multiple slit and a normal focus X-ray generator. When the multiple slit is used, a high aspect ratio structure is needed and slit width should be below 10 ?m for its function. The fabrication and use of such a multislit can be omitted using the presented configuration. The multiline X-ray source was developed by making grooves on a tungsten rotating anode, which was irradiated by an electron beam to generate X-rays. An array of 10?m line sources with a pitch of 30?m was formed and combined with a 4.5 ?m pitch phase grating and a 5.3 ?m pitch amplitude grating to generate differential phase contrast. With a total exposure time of 40 s, a differential phase image depicting cartilages was ...

International Nuclear Information System (INIS)

A photon-induced x-ray fluorescence method allowing the simultaneous determination of iron, copper, zinc, bromine and rubidium in human blood and blood plasma samples is described. The method is reliable and has a good sensitivity for a wide range of elements. (author).

International Nuclear Information System (INIS)

K_#beta#/ K_#alpha# x-ray intensity ratio of chromium were measured in different chromium compounds. The results show the variation of the intensity ratio as a function of the chemical environment around the metal ion. (author)

Science.gov (United States)

picture will download the highest resolution version available. M51: X-Rays from the Whirlpool Credit: A. Wilson (UMD) et al., CXC, NASA Explanation: Fresh from yesterday's...

International Nuclear Information System (INIS)

Certain applications are described of radionuclide X-ray fluorescence analysis in the ore dressing industry, in the manufacture of building materials, in metallurgy, pharmacy, in the chemical, photographic and paper industries, in space exploration, in archeology and for measuring the thicknesses of thin layers of coatings. (ES).

Energy Technology Data Exchange (ETDEWEB)

To understand the effect of heat treatment and mechanical polishing of a Nitinol wire on the chemical composition and physical morphology of the wire surface. Stents with a diameter of 1.0 cm, length of 8-10 cm, and composed of a Nitinol wire, were heat-treated at 500 .deg. C for 30 minutes, and mechanically polished with walnut shell granules. The wire surface morphology was studied with both an optical and a scanning electron microscope (SEM). In addition, an elemental analysis was performed by Energy Dispersive X-ray spectroscopy (EDX). Long microcracks along the wire direction and short microcracks across the wire were observed by SEM from the raw Nitinol wire. Upon heat treatment, the color of the wire turned blue, and Na, K, Cl, Si, Al atoms were seen from the EDX of the heat treated wire, which were absent in the original wire. The microcracks disappeared with the mechanical polishing, and the Na, K, Cl, Si, Al atoms all disappeared ...

International Nuclear Information System (INIS)

Ultrafine particles of Sn-Sb alloys with different chemical composition have been prepared by hydrogen plasma-metal reaction. Structure, morphology, size and chemical composition of the Sn-Sb ultrafine particles were investigated by transmission electron microscopy, X-ray diffraction, BET gas adsorption, and induction-coupled plasma spectroscopy. It was found that all the particles have spherical shapes, with average particle size in the range of 100-300 nm. The electrochemistry properties as an alternative anode material for lithium-ion batteries have been characterized by constant current cycling and cyclic voltammetry. Electrochemical measurements showed that the alloys with Sn-46.5 at.% Sb have best reversible capacity and capacity retention. It exhibited a high reversible lithium-ion storage capacity of 701 mAh g"-"1 in the initial cycle, which has remained at 81% (i.e., 566 mAh g"-"1) of its original capacity after 20 cycles.

International Nuclear Information System (INIS)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

Energy Technology Data Exchange (ETDEWEB)

Self-assembled monolayers (SAMs) on various metal, semiconductor or insulator substrates can be easily modified with specific functional groups of interest and have promising applications in surface wetting (hydrophobic/hydrophilic modification), tribology, corrosion protection, sensor electrodes modification, molecular and biomolecular recognition, protein adsorption, cell adhesion, and molecular- or organic-electronic device fabrications. In this paper, we highlight recent progress in the development of SAMs on solid substrates as well as their practical applications, with particular emphasis on the characterization of self-assembled aromatic thiol monolayers with different functional groups on Au(1 1 1) using synchrotron-based photoemission spectroscopy and near-edge X-ray absorption fine structure measurements. The SAM-related molecular orientation, electronic structures, and chemical bonding are presented. Using copper(II) phthalocyanine ...

International Nuclear Information System (INIS)

The present work describes the surface improvement and biocompatibility of TiAl_2_4Nb_1_0 intermetallic alloy using rf plasma nitriding. The nitriding process was carried out at different plasma power from 400 W to 650 W where the other plasma conditions were fixed. Grazing incidence X-ray diffractometry (GIXRD), Auger electron spectroscopy (AES), tribometer and a nanohardness tester were employed to characterize the nitrided layer. Further potentiodynamic polarization method was used to describe the corrosion behavior of the un-nitrided and nitrided alloy. It has been found that the Vickers hardness (HV) and corrosion resistance values of the nitrided layers increase with increasing plasma power while the wear rates of the nitrided layers reduce by two orders of magnitude as compared to those of the un-nitrided layer. This improvement in surface properties of the intermetallic alloy is due to formation of a thin modified layer which is ...

British Library Electronic Table of Contents (United Kingdom)

Potassium dichlorido(l-prolinato)platinate(II), K[PtCl"2(l-pro"?"H)] (1), and chlorido(dimethyl sulfoxide)(l-prolinato)platinum(II), [PtCl(l-pro"?"H)(dmso)] (2), were synthesized by ligand substitution reactions. Both complexes were characterized by ^1H, ^1^3C, and ^1^9^5Pt NMR spectroscopy, elemental analysis, and HR-ESI-MS. The molecular structures of 1 and 2 were determined by single crystal X-ray diffraction, proving bidentate coordinated l-prolinato ligand and SP-4-4 configuration of 2a. With the help of DFT calculations stability of possible isomers of 1 and 2 was studied. A considerable difference in the in vitro cytotoxicity of 1 versus 2a (exchange of one chlorido ligand by dmso) against four human cancer cell lines was found.

International Nuclear Information System (INIS)

Nanocrystalline samples of Fe_8_0Mo_2_0 and Fe_5_0Mo_5_0 alloys were prepared by the mechanical milling method. The structure, lattice parameters, and crystallite size were determined by the X-ray diffraction. The magnetic properties of the milled products were determined by the Moessbauer spectroscopy. It was observed that in the case of the Fe_8_0Mo_2_0 alloy a solid solution of Mo in Fe was formed with the lattice parameters of the Fe increasing from 0.28659 nm to 0.29240 nm and the crystallite size decreasing from 250 nm to 20 nm. In the case of the Fe_5_0Mo_5_0 alloy there were no clear changes in values of the lattice parameters of Fe and Mo during the milling process, but the crystallite size decreased from 200 to 15 nm. Moessbauer spectra revealed different magnetic phases in the machanosynthesized Fe_Mo samples. In the case of the Fe_8_0Mo_2_0 alloy, the spectrum for the milled mixture indicated the formation of solid solution. In ...

Energy Technology Data Exchange (ETDEWEB)

The structural change of the (100-x)(0.6Li[sub 2]S[center dot]0.4SiS[sub 2])centre dotxLi[sub 3]PO[sub 4] oxysulfide glassesduring crystallization was analyzed by means of solid-state nuclear magnetic resonance (NMR) and X-ray photoelectron spectroscopy (XPS). The unique tetrahedral units of SiO[sub n]S[sub 4-n] (n=1,2,3) and PO[sub n]S[sub 4-n] (n=1,2,3) present in the glass samples vanished and the SiS[sub 4], PS[sub 4], SiO[sub 4] units increased with proceeding of the crystallization process. Nonbridging sulfur and oxygen atoms decreased while bridging oxygens and S[sup 2-] increased with proceeding of the crystallization process. Large structural difference between the glass and the corresponding crystallized sample explained the high stability against crystallization found in the oxysulfide glass with the composition of X=5. (author)

Energy Technology Data Exchange (ETDEWEB)

Crystalline MnMoO{sub 4} was synthesized using a conventional solid reaction method and investigated for its physical and electrochemical properties as an anode material for Li secondary battery. The reversible amount of Li insertion/removal of MnMoO{sub 4} anode during the first cycle was about 800 mA h/g, accompanied by irreversible structural transformation into amorphous material. The amorphization during the first Li insertion was investigated by structural analysis using XRD of electrode. The charge compensation during Li insertion/removal was examined by measurement of X-ray Absorption Near Edge Structure (XANES) spectroscopy. Despite its irreversible structural transformation to amorphous during the first lithiation, subsequent cycles showed a reasonable cyclability. This paper presents the electrochemical properties of MnMoO{sub 4} and discusses the mechanism underlying the Li insertion/removal process.

International Nuclear Information System (INIS)

The CaWO_4:Ln"3"+ SiO_2 (Ln=Tb, Dy and Ho) nanoparticles were synthesized via a combustion process at 800 "oC, using citric acid as chelating agent and fuel, ammonium nitrate as fuel, boric acid as flux material and silica as supports. The persistent phosphor nanoparticles were characterized by X-ray diffraction (XRD), reflectance UV-vis and fluorescence spectroscopy (PL) and transmission electron microscopy (TEM) techniques. XRD patterns indicated that crystalline calcium tungstate with scheelite structure was produced. The reflectance UV-vis spectra showed the broad absorption band of WO_4"2"- groups and the PL spectra showed the WO_4"2"- wide excitation band, broad emission band of WO_4"2"- and characteristic emissions of Ln"3"+ ions. The average particle sizes were determined by TEM, which are about 50 nm.

International Nuclear Information System (INIS)

Here we describe the use of low energy plasma immersion with active screen as a convenient approach for polypropylene (PP) surface modification. Employing a stainless steel cathodic cage coated with carbon in order to prevent the sputtering of iron from the grid and its deposition onto the polymer sample, the physical chemical properties of PP surface could be effectively modified through the plasma-induced incorporation/formation of nitrogen- and oxygen-containing species. The areal densities of these elements depended on the plasma excitation source, as determined by Rutherford backscattering spectrometry (RBS). Newly formed C-O, C-N, and C=O/O=C-O/N-C=O bonds along with C-C linkages from the PP backbone were identified at the near surface region of the specimens by X-ray photoelectron spectroscopy (XPS). The insertion of such polar reactive functionalities was further confirmed by a substantial decrease in the water contact angle upon plasma ...

International Nuclear Information System (INIS)

Nanodimensional powders of cubic copper ferrite are synthesized by two-steps procedure of co-precipitation of copper and iron hydroxide carbonates, followed by mechanochemical treatment. X-ray powder diffraction, Moessbauer spectroscopy and temperature-programmed reduction are used for the characterization of the obtained materials. Their catalytic behavior is tested in methanol decomposition to hydrogen and CO and total oxidation of toluene. Formation of nanosized ferrite material is registered even after one hour of milling time. It is established that the prolonging of treatment procedure decreases the dispersion of the obtained product with the appearance of Fe2O3. It is demonstrated that the catalytic behavior of the samples depends not only on their initial phase composition, but on the concomitant ferrite phase transformations by the influence of the reaction medium. -- Graphical abstract: It is demonstrated that the catalytic behavior ...

CERN Document Server

NGC 2770 has been the host of three supernovae of Type Ib during the last 10 years, SN 1999eh, SN 2007uy and SN 2008D. SN 2008D attracted special attention due to the serendipitous discovery of an associated X-ray transient. In this paper, we study the properties of NGC 2770 and specifically the three SN sites to investigate whether this galaxy is in any way peculiar to cause a high frequency of SNe Ib. We model the global SED of the galaxy from broadband data and derive a star-formation and SN rate comparable to the values of the Milky Way. We further study the galaxy using longslit spectroscopy covering the major axis and the three SN sites. From the spectroscopic study we find subsolar metallicities for the SN sites, a high extinction and a moderate star-formation rate. In a high resolution spectrum, we also detect diffuse interstellar bands in the line-of-sight towards SN 2008. A comparison of NGC 2770 to the global properties of a galaxy ...

International Nuclear Information System (INIS)

Focused ion beam (FIB) irradiation of a thin Ni_2Si layer deposited on a Si substrate was carried out and studied using an in-situ transmission electron microscope (in-situ TEM). Square areas on sides of 4 by 4 and 9 by 9 microm were patterned at room temperature with a 25 keV Ga"+-FIB attached to the TEM. The structural changes of the films indicate a uniform milling, sputtering of the Ni_2Si layer and the damage introducing to the Si substrate. Annealing at 673 K results in the change of the Ni_2Si layer into an epitaxial NiSi_2 layer outside the FIB irradiated area, but several precipitates appear around the treated area. Precipitates was analyzed by energy dispersive X-ray spectroscopy (EDS). Larger amount of Ni than the surrounding matrix was found in precipitates. Selected area diffraction (SAD) patterns of the precipitates and the corresponding dark field images imply the formation of a Ni rich silicide. The relation between the FIB tail ...

British Library Electronic Table of Contents (United Kingdom)

A variety of platinum(II) complexes of methimazole (2-mercapto-1-methylimidazole; HImS=neutral form and ImS=thiolate form), coordinated in both thione and thiolate forms, have been isolated by reacting methimazole with [PtCl(terpy)]Cl (terpy=2,2prime:6prime,2Prime terpyridine), [PtCl2(bipy)] (bipy=bipyridine), [PtCl2(o-phen)] (o-phen=o-phenanthroline), [PtCl2(CH3CN)2] and [PtCl2(COD)] (COD=1,5-cyclooctadiene). These complexes were characterized by electronic absorption, IR and NMR (1H, 13C, 195Pt) spectroscopies. Molecular structure of [Pt(bipy)(HImS)2]Cl23H2O (3a3H2O) has been established by single crystal X-ray crystallography. Platinum thiolate complex, [Pt(ImS)2(HImS)2] (5), could be obtained by treatment of [Pt(HImS)4]Cl2 with sodium methoxide in methanol. The solution of 5 in organic...

Energy Technology Data Exchange (ETDEWEB)

The temperature effect on corrosion behaviors of PbCaSnCe alloy in 4.5 M H{sub 2}SO{sub 4} solution was investigated by using potentiodynamic curve, electrochemical impedance spectra (EIS), Mott-Schottky plot and photocurrent response methods. It was found that PbCaSnCe alloy was in passive state in sulfuric acid solution, a passive film can be formed on alloy surface. The compositions of passive films formed at 0.9 V for 2 h under different temperatures were detected by X-ray photoelectron spectroscopy (XPS). The results showed that the film resistance and the transfer resistance decreased with the increment of the solution temperature. Mott-Schottky analysis and the photocurrent response revealed that the passive film exhibited n-type semi-conductive character, the donor density of the passive film decreased with increasing the solution temperature. Photocurrent response revealed that the photocurrent increased with increasing temperature. ...

Energy Technology Data Exchange (ETDEWEB)

Industrial applications of thermoplastic polymers are often limited by their poor adhesion properties. In this work the effect of surface oxyfluorination on the adhesion properties was investigated for polyethylene (PE), polyoxymethylene (POM), polybutylene terephthalate (PBT) and polyamide 6 (PA6). The adhesive joint strength was quantified using lap-shear tests. These results were correlated with the changes in the chemical composition of the surface, determined by X-ray photoelectron spectroscopy (XPS), in the surface free energy, measured by the contact angle method, and in the topography, using white-light confocal microscopy. The adhesive strength is strongly improved for all four polymers, but the degree of this increase depends on the polymer type. The surface free energy shows a similar trend for all four polymers. A high surface free energy exceeding 50 mN/m was observed after oxy-fluorination, whereby the polar component was strongly ...

British Library Electronic Table of Contents (United Kingdom)

High lithium-ion (Li^+) conductive garnet-structured lanthanum lithium zirconate (LLZ) solid electrolyte is prepared by incorporation of appropriate amounts of silicon (Si) and aluminum (Al). The resultant pelletized LLZ obtains total Li^+ conductivity of 6.8x10^-^4Scm^-^1 at 298K. This improved conductivity is nearly identical with the bulk Li^+ conductivity of the LLZ reported earlier, suggesting that the grain boundary resistance is effectively reduced by the incorporation of Si and Al. Microanalyses by transmission electron microscopy coupled with energy-dispersive X-ray microanalysis and electron energy-loss spectroscopy revealed the presence of amorphous Li-Al-Si-O with nano crystalline LiAlSiO4 at grain boundaries. Fast lithium-ion transport around the amorphous Li-Al-Si-O/LiAlSiO4 ...

Energy Technology Data Exchange (ETDEWEB)

Alkaline fuel cells (AFCs) provide a less corrosive environment and can provide higher electrode reaction kinetics than proton exchange membrane fuel cells (PEMFCs). The alkaline media also allows for the replacement of platinum (Pt) based electrocatalysts with non-Pt electrocatalysts. Studies have shown that palladium (Pd) and silver (Ag) form a homogenous solid solution with a face-centred cubic structure within a large range of temperatures. This study described the results of an oxygen reduction reaction (ORR) on lead-silver (Pd-Ag) alloy electrodes in alkaline media. The reaction was compared with Pd and Ag electrodes. The alloys were synthesized as thin films using a sequential electroless deposition of Pd and Ag on stainless steel discs followed by an annealing procedure in an Ar stream. X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) were used to characterize catalyst structure, ...

Energy Technology Data Exchange (ETDEWEB)

In this work, a new class of thiadiazole derivatives, namely 3,5-bis(2-thienyl)-1,3,4-thiadiazole (2-TTH) and 3,5-bis(3-thienyl)-1,3,4-thiadiazole (3-TTH), have been studied as possible corrosion inhibitors for mild steel in molar hydrochloric acid (1M HCl). Polarisation curves and AC impedance methods have been used. These studies have shown that the thiadiazole derivatives were very good inhibitors for mild steel in 1M HCl. Comparison of results showed that 3-TTH was the best inhibitor. The potential of zero charge (PZC) of mild steel was studied by ac impedance method, and the mechanism of adsorption has been predicted. X-ray photoelectron spectroscopy surface analysis with thiadiazole derivatives shows that it chemisorbed at the mild steel/HCl interface. The adsorption of these inhibitors followed Langmuir's adsorption isotherm. The electronic properties of 2-TTH and 3-TTH, obtained using the AM1 semi-empirical quantum chemical ...

International Nuclear Information System (INIS)

Si/Ni alloy and graphite composites were synthesized using arc-melting followed by high energy mechanical milling (HEMM). Alloy particles comprising of NiSi2, NiSi and Si phases were distributed finely and uniformly on the surface of graphite in the composites obtained after Hem. The composite containing 60 wt.% of Si/Ni alloy exhibited a stable capacity of ?780 mAh/g. Fourier transform infrared spectroscopy (FTIR) analysis confirmed that some bonds were formed between alloy and graphite after HEMM, which appeared to retain the electrical connection between alloy and graphite during cycling. X-ray diffraction (XRD) analysis indicated that NiSi2 and NiSi phases, which acted as an inactive alloy matrix remained invariant during charge and discharge. In addition to NiSi2 and NiSi phases, disordered graphite layers also played the role of media for the accommodation of large volume change of Si during cycling. The large reversible capacity and good ...

Energy Technology Data Exchange (ETDEWEB)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage measurement. The analysis of capacitance-voltage characteristics ...

Science.gov (United States)

The effect of hydrogen sulfide (H2S) on the chemical looping combustion of coal-derived synthesis gas with bentonite-supported metal oxidesssuch as iron oxide, nickel oxide, manganese oxide, and copper oxideswas investigated by thermogravimetric analysis, mass spectrometry, and X-ray photoelectron spectroscopy (XPS). During the reaction with synthesis gas containing H2S, metal-oxide oxygen carriers were first reduced by carbon monoxide and hydrogen, and then interacted with H2S to form metal sulfide, which resulted in a weight gain during the reduction/sulfidation step. The reduced/sulfurized compounds could be regenerated to form sulfur dioxide and oxides during the oxidation reaction with air. The reduction/oxidation capacities of iron oxide and nickel oxide were not affected by the presence of H2S, but both manganese oxide and copper oxide showed decreased reduction/oxidation capacities. However, the rates of reduction and oxidation ...

British Library Electronic Table of Contents (United Kingdom)

Dye-sensitized solar cells (DSSCs) based on anatase TiO2 hollow spheres (TiO2HS)/multi-walled carbon nanotubes (CNT) nanocomposite films are prepared by a directly mechanical mixing and doctor blade method. The prepared samples are characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, UV-vis absorption spectroscopy and N2 adsorption-desorption isotherms. The photoelectric conversion performances of the DSSCs based on TiO2HS/CNT composite film electrodes are also compared with commercial-grade Degussa P25 TiO2 nanoparticles (P25)/CNT composite solar cells at the same film thickness. The results indicate that the photoelectric conversion efficiencies () of the TiO2HS/CNT composite DSSCs are dependent on CNT loading in the electrodes. A small amou...

International Nuclear Information System (INIS)

The electronic structure and surface interactions vapor-deposited Cu on single-crystal and polycrystalline Bi_2Ca/sub 1+//sub x//sub Sr>2-//sub x//sub Cu>2/O/sub 8+//sub y/ were studied using x-ray photoelectron spectroscopy. The results are compared to the Cu/YBa_2Cu_3O/sub 7-//sub x/ interface. Changes in the Cu 2p satellite emission indicate that the Cu adatoms do not disrupt Bi_2Ca/sub 1+//sub x/Sr/sub 2-//sub x/Cu_2O/sub 8+//sub y/ as extensively as YBa_2Cu_3O/sub 7-//sub x/. However, deposition of Cu induces changes in the Bi environment in the superconductor, and surface segregation of Bi metal was observed at high coverages. Core-level attenuation results suggests minimal outdiffusion of oxygen, in contrast with what is observed for Cu/YBa_2Cu_3O/sub 7-//sub x/.

Energy Technology Data Exchange (ETDEWEB)

Most of the organic electronic devices are nowadays fabricated under poor vacuum conditions. In this regard, there is only little knowledge about the impact of contamination of the metal electrode on the charge injection barrier in this kind of electronic devices. In our study we have performed X-ray and ultra violet photoemission spectroscopy (XPS, UPS) on interfaces between the organic semiconductor -sexithiophene and sputter cleaned (ideal) metals as well as contaminated (realistic) metals. As metal substrates we have used silver, gold, palladium, and platinum. These metals provide us a wide range of metal work functions from 4.2 eV for silver up to 5.5 eV for platinum. For all interfaces of -sexithiophene and contaminated metals we have observed a reduction of the interface dipole and the hole injection barrier. The charge injection barrier in all four cases is almost independent of the underlying metal (within an error of 0.2 eV) and the ...

Energy Technology Data Exchange (ETDEWEB)

Eu 4f electronic structures of a temperature-induced valence transition system EuPd{sub 2}Si{sub 2} have been investigated by bulk-sensitive high-resolution photoemission spectroscopy at temperatures from 20 to 300 K. The bulk Eu{sup 2+} 4f component is definitely distinguished from two surface Eu{sup 2+} 4f components. The changes in the spectral intensity of the bulk Eu{sup 2+} and Eu{sup 3+} 4f configurations and in the energy separation between these states are observed in the temperature dependent photoemission spectra. These temperature dependences are related to the valence transition of EuPd{sub 2}Si{sub 2}. The Eu mean valence is evaluated to be 2.75{+-}0.03 at 20 K and 2.30{+-}0.05 at 300 K. These values are in good agreement with those evaluated from Moessbauer and Eu L{sub III}-edge X-ray absorption measurements.

Energy Technology Data Exchange (ETDEWEB)

We report a templated-synthetic approach based on apoferritin to prepare radionuclide nanoparticle (NP) conjugates. Non-radioactive yttrium (89Y) was used as model target and surrogate for radioyttrium (90Y) to prepare the nanoparticle conjugate. The center cavity and multiple channel structure of apoferritin offer a fast and facile method to precipitate yttrium phosphate by diffusing yttrium and phosphate ions into the cavity of apofrritin, resulting a core-shell nanocomposite. The yttrium phosphate/apoferritin nanoparticle was functionalized with biotin for further application. The synthesized nanoparticle was characterized by transmission electron microscopy (TEM) and x-ray photoelectron spectroscopy (XPS). We found that the resulting nanoparticles were uniform in size, with a diameter of around 8 nm. We tested the pre-targeting capability of the biotin-modified yttrium phosphate/apoferritin nanoparticle (yttrium phosphate/apoferritin ...

Energy Technology Data Exchange (ETDEWEB)

X-ray photoelectron spectroscopy (XPS) and transmission electron microscopy (TEM) have been conducted on a new fuel cell electrocatalytic material based on a highly porous carbonized polyacrylonitrile (PAN) microcellular foam with very low platinum loading ({approximately}13 to 23 {micro}g/cm{sup 2}). TEM images of this material clearly show the existence of nanometer size platinum particles which are homogeneously distributed in the highly porous carbonized PAN matrix. An XPS study of Pt-loaded PAN indicates that C 1s, O 1s, and N 1s peaks shift to lower binding energies, compared to virgin PAN. It was concluded that special metal-support interaction exists, through the formation of a charge-transfer complex between platinum and pyridine-type nitrogen atoms of PAN support. This interaction leads to the enhancement of the catalytic activity, and the improvement of the long-time stability of this electrocatalyst.

CERN Document Server

We present a new Chandra observation of supernova remnant (SNR) G350.1-0.3. The high resolution X-ray data reveal previously unresolved filamentary structures and allow us to perform detailed spectroscopy in the diffuse regions of this SNR. Spectral analysis demonstrates that the region of brightest emission is dominated by hot, metal-rich ejecta while the ambient material along the perimeter of the ejecta region and throughout the remnant's western half is mostly low-temperature, shocked interstellar/circumstellar medium (ISM/CSM) with solar-type composition. The data reveal that the emission extends far to the west of the ejecta region and imply a lower limit of 6.6 pc on the diameter of the source (at a distance of 4.5 kpc). We show that G350.1-0.3 is likely in the free expansion (ejecta-dominated) stage and calculate an age of 600-1200 years. The derived relationship between the shock velocity and the electron/proton temperature ratio is ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

International Nuclear Information System (INIS)

Czech May 1979. p. 32-33. Czechoslovakia Benada, J. Spacek, B. Ustav

International Nuclear Information System (INIS)

... Union (INTAS), Brussels (Belgium) Science and Technology Center in Unkraine,

International Nuclear Information System (INIS)

An interferometric technique for hard X-rays is presented. It is based on two transmission gratings and a phase-stepping technique, and it provides separate radiographs of the phase and absorption profiles of bulk samples. Tomographic reconstruction yields quantitative three-dimensional maps of the X-ray refractive index and of the attenuation coefficient, with a spatial resolution down to a few microns. The method is mechanically robust, it requires little monochromaticity, and can be scaled up to large fields of view. These are important prerequisites for use with laboratory X-ray sources. Numerous applications ranging from wave front sensing to medical radiography are presently under investigation.

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

The ELXS concept is a novel, portable, micro-instrument targeted for the detection of mineralogic

International Nuclear Information System (INIS)

High (spatial) resolution imaging detectors for X-ray astronomy were developed. Several prototype detectors built and their feasibility and baseline performance were assessed. Two of these detector types are proposed for investigations on the advanced X-ray astrophysics facility (AXAF). The readiness of a new X-ray imaging system, the charge coupled device (CCD) imaging specctrometer is outlined, and state of the art performance parameters for microchannel plate (MCP) and CCD detectors are measured. Laboratory facilities and procedures for coating MCP are developed general high resolution imagery systems are analyzed.

Energy Technology Data Exchange (ETDEWEB)

Chemical effects of L X-ray intensity ratios in niobium and molybdenum compounds were studied by electron and proton bombardments. L{sub {gamma}1} X-rays which involve transition of 4d electrons of the valence shell were found to be sensitive to the chemical environment. The L{sub {gamma}1}/L{sub {beta}1} X-ray intensity ratio increased with an increase of the 4d electron occupation of niobium or molybdenum in niobium or molybdenum compounds, showing that the chemical effects can be ascribed to the 4d electron behavior of the metallic atom in its compounds. (orig.).

CERN Document Server

Bragg curve spectroscopy

International Nuclear Information System (INIS)

These proceedings represent papers presented at the Astrophysics Conference in Maryland, USA. The topic of the Conference was the evolution of x-ray binaries and the papers encompass a wide range of subjects on x-ray astronomy. There were one hundred eighteen papers presented at the Conference and out of these three have been abstracted for the Energy Science and Technology database.

International Nuclear Information System (INIS)

The quantitative imaging of a phase object using 16 keV x-rays is reported. The theoretical basis of the techniques is presented along with its implementation using a synchrotron x-ray source. It is found that the phase image is in quantitative agreement with independent measurements of the object. 13 refs., 5 figs.

Science.gov (United States)

The achievement of inner-shell photoionization of Zn-like Pd by means of two exploding foils is described. This resulted in the soft X-ray transition 3d94s2-3d104p at 46 A. It is shown that the photoionization of inner shell electrons in highly stripped ions can lead to X-ray transitions which may be candidates for X-ray lasers under 50 A.

Energy Technology Data Exchange (ETDEWEB)

A brilliant X ray source is proposed for lithography instruments with use of a multi-mirror system. The inverse Compton scattering between the stored electron beam in the storage ring and the stored photon beam in the multi-mirror system, is applied for the X-ray generation. (author)

International Nuclear Information System (INIS)

Based on a literature study an actual summary of the risk-utility problems in X-ray diagnosis is outlined due to the Recommendations of the International Commission for Radiation Protection (ICRP publication 26/1977). Papers demonstrating quantitative assessment of the somatic and genetical risk in X-ray examination are preferably cited and evaluated. It is concluded that the somatic and genetical risk is low in diagnostic ratiology. However, it must not be neglected and has always to be compared to the utility of an examination as well as to other risks of the examination. (author).

International Nuclear Information System (INIS)

The basic principles of determination of the ash content of coal by the title methods are outlined. A brief technical characteristic of the ash meters and radionuclide X-ray fluorescence analyzers manufactured by the PAR company is presented. (Z.S.). 4 figs., 7 refs.

Energy Technology Data Exchange (ETDEWEB)

Successful interface engineering requires compositional and electronic material characterization as a prerequisite for understanding and intentionally generating interfaces in photovoltaic devices. The paper gives an overview with several examples, all referring to Cu(In,Ga)(S,Se){sub 2} ('CIGSSe')-based solar cells, with an emphasis on characterization using highly specialized methods, such as elastic recoil detection analysis, X-ray emission spectroscopy and photoelectron spectroscopy using synchrotron and ultraviolet light for excitation, inverse photoemission spectroscopy and Kelvin probe force microscopy. First, the determination of the depth profile of the band gap energy E{sub g} in the absorber layer is demonstrated. The modification of E{sub g} towards both interfaces is discussed in terms of beneficial electronic effects. Next, the interface between absorber and buffer layers ...

Energy Technology Data Exchange (ETDEWEB)

A method has been developed to optimize the energy resolution of a horizontally focusing monochromator. The method consists of determining the optimum radius of curvature of the cylindrically bent monochromator crystal by minimizing the total diffracted X-ray flux measured through an X-ray absorption foil. When measured at an absorption edge a global minimum can be identified, which corresponds to the minimum energy band accepted along the entire length of the crystal. Experimental verification of this method has been validated by comparing X-ray fluorescent scans taken for a series of crystal curvatures and by directly measuring the X-ray beam profiles at the corresponding points. The actual optical configuration and asymmetric-cut parameter of the focusing monochromator on beamline X4C at the National Synchrotron Light Source are modeled and ray tracing simulations of the optical system are compared ...

International Nuclear Information System (INIS)

Lifetime of minority charae carriers in the Si and Ge p-n unctions has been measured by pulse method of conductivity modulation of base. Its dependence on the X-ray radiation dose has been investigated. Dependence of current transmission coefficients on the dose has been measured and their sharp decrease at low doses and the following saturation at high doses have been observed. Linear dependence of lifetime on X-ray radiation dose has been obtained. Resulting from the comparison of regularities of the change of lifetime due to current characteristics, it has been shown that X-ray radiation leads to the formation of the surface defects, influencing the change of current characteristics as well as to stationary structural defects, causing the decrease of lifetime of the charge carriers with the increase of X-ray radiation dose.

Energy Technology Data Exchange (ETDEWEB)

The {ital L}{sub 2}-{ital L}{sub 3} Coster-Kronig transition probability ({ital f}{sub 23}) in Tm was measured by multiparameter {ital K} versus {ital L} x-ray coincidence techniques. The Tm x rays were obtained from a radioactive source of {sup 169}Yb and were detected with cooled germanium and silicon detectors of high-energy resolution. Corrections were applied for the contribution of {ital K}{alpha}{sub 1} x rays to the {ital K}{alpha}{sub 2} x-ray peak and for the contribution of unresolved {ital L}{eta} x rays to the {ital L}{alpha}{sub 1,2} x-ray peak. The contribution of {ital K}{alpha}{sub 1} x rays to the {ital K}{alpha}{sub 2} x-ray peak was determined solely from the results of the coincidence measurements using a method of ...

Energy Technology Data Exchange (ETDEWEB)

The interaction of intense, sub-picosecond laser pulses with solid targets produces intense picosecond x-ray pulses. With focused laser pulses of several 10 {sup 18} W/cm{sup 2}, He-like and H-like line radiation from targets such as aluminum and silicon has been produced. The energy conversion efficiency from the laser pulse energy to the 1--2 keV line x-rays is nearly one percent. The duration of the line x-ray radiation is of the order of ten picoseconds, although this may be an upper estimate because of the temporal resolution of the x-ray streak camera. The spatial extent of the x-ray source region is only slightly larger than the laser focal spot, or about 10 {mu}m in diameter. With these characteristics, such x-ray sources emit an intensity of nearly 10{sup 14} W/cm{sup 2}. Experiments and modeling which led to the above conclusions will be discussed.

CERN Document Server

Context: The colliding-wind binary Eta Car exhibits soft X-ray thermal emission that varies strongly around periastron, and non-thermal emission seen in hard X-rays and gamma-rays. Aims: To definitively identify Eta Car as the source of the hard X-ray emission, to examine how changes in the 2-10 keV band influence changes in the hard X-ray band, and to understand more clearly the mechanisms producing the non-thermal emission using new INTEGRAL observations obtained close to periastron. Methods: A Chandra observation encompassing the ISGRI error circle was analysed, and all other soft X-ray sources (including the outer shell of Eta Car itself) were discarded as likely counter-parts. New hard X-ray images of Eta Car were studied close to periastron, and compared to previous observations far from periastron. Results: The INTEGRAL component, when represented by a ...

International Nuclear Information System (INIS)

Based on a recently introduced phase X-ray imaging approach, a dual-detector prototype was developed for in-line X-ray phase imaging and phase retrieval utilizing a micro-focus X-ray source and two computed radiography (CR) cassette detectors. The system was built on a horizontal optical rail to facilitate manual adjustment of the positions of the X-ray source, the sample and the detectors. The novel design of the detector-1 is essential, it detects a portion of radiation to form an attenuation image; allows the rest of radiation to reach the detector-2 to form a phase contrast image, and the two images are used to retrieve a phase map. The two detectors are balanced for optimal phase-retrieval with reasonable radiation dose to the object to be imaged. The system was examined in terms of the linearity, the fractions of the X-ray photons detected by the two detectors, respectively ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes Fuji computed radiography (FCR) of Fuji Film for NDT (non-destructive testing). Imaging plate (IP) is a two-dimensional detector of X-ray, and shows higher photographic sensitivity than X-ray film. The output emission of IP provides a good linear relationship to X-ray intensity in a wide intensity range. When this emission can be digitized, the X-ray intensity can be also digitized. IP is applied to NDT as an inspection using X-ray. FCR provides higher photographic sensitivity than the conventional X-ray film method, which results in one-fifth to one-twentieth of irradiation time. Images with stable density can be obtained independent of the intensity. Since IP has a wide dynamic range, the variation of X-ray intensity of 1:500 can be expressed in a single image by single shot. High density record including 1000 images ...

Energy Technology Data Exchange (ETDEWEB)

In the framework of the search for a ceramic material usable in the radioactive waste storage, uranium and thorium phosphates have been investigated. Their experimental synthesis conditions have been entirely reviewed, they lead to the preparation of four new compounds: U(UO{sub 2})(PO{sub 4}){sub 2}, U{sub 2}O(PO{sub 4}){sub 2}, UCIPO{sub 4}, 4H{sub 2}O, and Th{sub 4}(PO{sub 4}){sub 4}P{sub 2}O{sub 7}. Experimental evidenced are advanced for non existent compounds such as: U{sub 3}(PO{sub 4}){sub 4}, U{sub 2}O{sub 3}P{sub 2}O{sub 7} and Th{sub 3} (PO{sub 4}){sub 4}. Characterization by several techniques (X-rays and neutron powder diffractions, UV-Visible and Infra-red spectroscopies, XPS,...) were performed. The ab initio structure determination of U(UO{sub 2})(PO{sub 4}){sub 2} has been achieved by X-rays and refined by neutron diffractions. Through its physico-chemical analysis, we found that this compound was a new ...

Energy Technology Data Exchange (ETDEWEB)

An historic Strontianite-type specimen from Strontian, Scotland, UK, was characterized to broaden our knowledge on luminescence properties of common carbonates. These fibrous aggregates are Strontianite (Sr{sub x}Ca{sub 1-x}CO{sub 3}) with circa 6% of CaO, interfacial water, hydrosilicate anions and substitutional divalent cations, e.g., Ca{sup 2+}, Mn{sup 2+}, Fe{sup 2+} in structural Sr{sup 2+} positions. The specimen was analyzed by X-ray Fluorescence Spectrometry (XRF), Environmental Scanning Electron Microscopy coupled with an Energy Dispersive X-ray Spectroscopy (ESEM-EDS) probe, Spatially-resolved Cathodoluminescence under the Scanning Electron Microscope (SEM-CL), Differential-Thermal Analyses (DTA), Thermogravimetry (TG), Thermoluminescence (TL), Radioluminescence (RL) and High Resolution Spectra Thermoluminescence (3DTL), to gain an overview of the spectral emissions, the defect linkages were modified by heating ...

International Nuclear Information System (INIS)

SiC-AlN and SiC-SiAlON refractory composites were obtained by means of nitridation of the mixtures of silicon carbide (SiC) powder with a broad granulometric distribution and powders of aluminium (Al) and aluminium-silicon (Al-Si) mixtures. The mixtures of the composition Al-25% Si, Al-50% Si and Al-75% Si were previously prepared by means of 'mechanical alloying' technique. Thermodynamic analysis was accomplished in order to evaluate the viability of SiC-SiAlON and SiC-AlN refractories production by the chosen processing method, and the results confirmed viability of such. Investigation of nitridation of Al and Al-Si powder compacts in order to obtain the AlN and #beta#-SiAlON matrix phases of the composite was accomplished by means of differential thermal analysis (DTA) and thermogravimetric analysis (TG). The results of the thermal analysis show that nitridation of the Al-25% Si, Al-50% Si and Al-75% Si resulting in p-SiAlON formation occur at temperatures of 910 deg C, 811 deg C ...

Energy Technology Data Exchange (ETDEWEB)

Metal nanoparticles have many potential technological applications. Biological routes to the synthesis of these particles have been proposed including production by vascular plants, known as phytoextraction. While many studies have looked at metal uptake by plants, particularly with regard to phytoremediation and hyperaccumulation, few have distinguished between metal deposition and metal salt accumulation. This work describes the uptake of AgNO{sub 3}, Na{sub 3}Ag(S{sub 2}O{sub 3}){sub 2}, and Ag(NH{sub 3}){sub 2}NO{sub 3} solutions by hydroponically grown Brassica juncea and the quantitative measurement of the conversion of these salts to silver metal nanoparticles. Using X-ray absorption near edge spectroscopy (XANES) to determine the metal speciation within the plants, combined with atomic absorption spectroscopy (AAS) for total Ag, the quantity of reduction of Ag{sup I} to Ag{sup 0} is reported. Transmission electron ...

International Nuclear Information System (INIS)

Complimentary spectroscopic, microscopic and electrochemical studies were performed to characterise the barrier properties as well as the interface structure of model iron substrates covered with thin plasma polymer films. Cathodic plasma polymers were deposited which show high barrier properties. The metal surface was pre-treated by a reducing or oxidising plasma. This allowed the adjustment of the oxidation state of the interface layer. The interface structure was characterised by means of X-ray photoelectron sputter profiles, infrared spectroscopy and the application of a Kelvin probe. The investigations show that the measured Voltapotential on the plasma polymer surface can be correlated with the oxidation state of the interface. Reducing plasmas lead to an almost oxide free surface. After deposition of the plasma polymer, this reduced state of the oxide is sensitive to re-oxidation of the interface by oxygen that diffuses through the ...

International Nuclear Information System (INIS)

The measurements obtained here indicate ways in which micro-Raman spectroscopy can be used to elucidate structural characteristics and distribution of carbon in meteorites and interplanetary dust particles (IDPs). Existing information about structurally significant aspects of Raman measurements of graphite is combined with structurally relevant findings from the present micro-Raman studies of carbons prepared by carbonization of polyvinylidine chloride (PVDC) at various temperatures and natural material, as well as several acid residues from the Allende and Murchison meteorites in order to establish new spectra-structure relationships. Structural features of many of the materials in this study have been measured by x ray analysis and electron microscopy: thus, their structural differences can be directly correlated with differences in the Raman spectra. The spectral parameters consequently affirmed as indicators of ...