UK PubMed Central (United Kingdom)

The issue of beam-induced damage on diffractive hard X-ray optics is addressed. For this purpose a systematic study on the radiation damage induced by a high-power X-ray beam is carried out in both...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The solid state reaction between a Pd thin film and a Si substrate produces a single new phase, Pd/sub 2/Si, for temperatures <700/sup 0/C. When the substrate is a single crystal of (111) surface orientation, this process is particularly interesting because the silicide grows epitaxially. Growth of epitaxial interfacial Pd/sub 2/Si was the focus of this study using X-ray diffraction techniques.

International Nuclear Information System (INIS)

TlGaSe_2 compound belongs to group of layered semiconductors of A"3B"3C_2"6-type. Photoelectric and optical properties of TlGaSe_2 single crystals were investigated in detail. Influence of gamma-, electron and neutron radiation on photoelectric properties of TlGaSe_2 single crystals is investigated too. The present work deals with experimental results relative to X-ray dosimetric characteristics of TlGaSe_2 crystals at 300 K. X-ray conductivity and X-ray dosimetric characteristic measurements are carried out in low load resistance regime. The source of X-ray radiation is the installation of X-ray diffraction analysis (URS-55a) with the BCV-2(Cu). Intensity of X-ray radiation (E) is regulated by measurement with current variation in tube at each given value of X-ray radiation dose E (R/min) are measured by crystal ...

CERN Document Server

Hydroxyapatite samples were produced by two different wet-chemical methods, and characterized by x-ray diffraction, infrared and compression strength measurements. The x-ray diffraction measurements were simulated using the Rietveld method, and structural data as lattice parameters and average crystallite size were obtained. The infrared spectra showed the presence of CO$_3^{2-}$ ions in all samples, indicating a contamination by these ions. By mixing samples produced by both methods, a bioceramic was obtained and, after sintering, samples with very high compression strengths (26--30 MPa) were obtained.

British Library Electronic Table of Contents (United Kingdom)

This paper presents results about the characterisation of the biomass fly ashes sourced from a thermal power plant and from a co-generation power plant located in Portugal, and the study of new cement formulations incorporated with the biomass fly ashes. The study includes a comparative analysis of the phase formation, setting and mechanical behaviour of the new cement-fly ash formulations based on these biomass fly ashes. Techniques such as X-ray diffraction (XRD), X-ray fluorescence spectroscopy (XRF), thermal gravimetric and differential thermal analysis (TG/DTA), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM) and environmental scanning electron spectroscopy (ESEM) were used to determine the structure and composition of the formulations. Fly ash F1 from the t...

British Library Electronic Table of Contents (United Kingdom)

A galactose-specific seed lectin was purified from the legume Spatholobus parviflorus and crystallized using the hanging-drop vapour-diffusion technique. Thecrystals belonged to space group P1, with unit-cell parameters a = 60.998, b=60.792, c = 78.179-, = 101.32, = 91.38, = 104.32. X-ray diffraction data were collected under cryoconditions (100-K) to a resolution of 2.04- using a MAR image-plate detector system mounted on a rotating-anode X-ray (Cu-K) generator. Molecular replacement using legume-lectin coordinates as a search model gave a tetrameric structure.

International Nuclear Information System (INIS)

A technique for following sialon formation in situ by high temperature X-ray diffraction (HT-XRD) was developed. The composition chosen for study was an yttrium #alpha#-sialon with x=0.4. Powder compacts containing silicon nitride, aluminum nitride and yttria powders were pre-sintered at 1350 C and then studied by HT-XRD at temperatures between 1450 and 1580 C and nitrogen pressures of 0.11 MPa. The furnace was made from graphite coated with porous silicon nitride/silicon carbide. The coating prevented silicon carbide formation in the sample up to 1600 C. X-ray diffraction results show the formation of a Y_1_0Al_2Si_3O_1_8N_4 phase at 1350 C, which dissolved to form #alpha#-sialon and other phases at higher temperatures. The amounts of #alpha#-sialon formed are similar to the amounts reported by other authors. An empirical method was used for the calculation of ...

International Nuclear Information System (INIS)

X-ray imaging is a very useful plasma diagnostic method. A theoretical analysis of the x-ray phase imaging in the method based on Fresnel diffraction is given. The authors show it is a linear band pass filter, a property suit for Rayleigh-Taylor (R-T) instability measurement. The evaluation permits the possibility of R-T instability measurement in x-ray phase imaging

Energy Technology Data Exchange (ETDEWEB)

Fuel irradiation leads to a swelling resulting from the formation of gaseous (Kr, Xe) or solid fission products which are found either in solution or as solid inclusions in the matrix. This phenomena has to be evaluated to be taken into account in fuel cladding Interaction. Fuel swelling was studied as a function of burn up by measuring the corresponding cell constant evolution by X-Ray diffraction. This study was realized on Mixed Oxide Fuels (MOX) irradiated in a Pressurized Water Reactor (PWR) at different burn-up for 3 initial Pu contents. Lattice parameter evolutions were followed as a function of burn-up for the irradiated fuel with and without an annealing thermal treatment. These experimental evolutions are compared to the theoretical evolutions calculated from the hard sphere model, using the fission product concentrations determined by the APPOLO computer code. Contribution of varying ...

UK PubMed Central (United Kingdom)

α-Galactosidases from thermophilic organisms have gained interest owing to their applications in the sugar industry. The α-galactosidases AgaA, AgaB and AgaA A355E mutant from Geobacillus...Full Text Available

International Nuclear Information System (INIS)

The effect of resonance, observed in X-ray waveguide layered structures in a characteristic way influences the scattering properties of the films. It is well known that the resonant region in the reflectivity shows a series of minima, usually very deep and extremely narrow. The positions and depths of the minima depend only on X-ray waveguide and quasi X-ray waveguide film structural properties, on the X-ray wavelength and on the incident beam divergence. In the present work we propose and discuss the application of the X-ray waveguide and quasi X-ray waveguide film structures as a tools to experimental evaluation of some quantities related to X-ray reflectometric and diffractometric measurements, like the beam divergence, wavelength, or angular distance. Examples of application of X-ray waveguide as an excellent tool ...

International Nuclear Information System (INIS)

In this work we report a study of the induced changes in structure and corrosion behavior of martensitic stainless steels nitrided by plasma immersion ion implantation (PI"3) at different previous heat treatments. The samples were characterized by x-ray diffraction and glancing angle x-ray diffraction, scanning electron microscopy, energy dispersive x-ray spectroscopy, and potentiodynamic measurements. Depending on the proportion of retained austenite in the unimplanted material, different phase transformations are obtained at lower and intermediate temperatures of nitrogen implantation. At higher temperatures, the great mobility of the chromium yields CrN segregations like spots in random distribution, and the #alpha#"'-martensite is degraded to#alpha#-Fe (ferrite). The nitrided layer thickness follows a fairly linear relationship with the temperature and a ...

Energy Technology Data Exchange (ETDEWEB)

An x-ray diffraction technique for determining thin-film thickness is presented which should prove to be a valuable alternative to the array of spectroscopies (Rutherford backscattering spectrometry, Auger electron spectroscopy, etc.) currently favored for these measurements. Some of the virtues of this x-ray diffraction approach are its nondestructive nature, fast data acquisition rate (enabling in situ observations), thickness resolution better than 5 nm, and conventional equipment requirements. Results are shown for Pd/sub 2/Si thin films grown during isothermal annealing of Pd coatings (100 nm) on Si at 200 /sup 0/C for various amounts of time. A comparison of these x-ray measurements with Rutherford backscattering spectrometry data taken from the same specimens is used to demonstrate the validity of the x-ray technique.

Energy Technology Data Exchange (ETDEWEB)

New phosphates with NaZr{sub 2}(PO{sub 4}){sub 3} structure of the B{sub 0.5}FeTa(PO{sub 4}){sub 3}-type (where B-Ca, Sr, Ba) are synthesized and characterized by X-ray diffraction analysis and IR-spectroscopy. The heating behavior of the phosphates is studied using high-temperature X-ray crystallography in the range 15-625 deg. C. The unit-cell parameters, the coefficients of thermal expansion {alpha}{sub a}, {alpha}{sub c} and their thermal expansion anisotropy |{alpha}{sub c} - {alpha}{sub a}| of the phosphates under study are determined and the dependences of these characteristics on the nature of cations are established and analyzed.

International Nuclear Information System (INIS)

FexZn1-x alloys were electrochemically deposited on aluminum substrates from a sulfate bath. The K?/K? x-ray intensity ratios of Zn and Fe in FexZn1-x thin films have been experimentally studied. The energy dispersive x-ray fluorescence (EDXRF) technique was used to measure K x-ray photons. Samples were excited by using 59.5 keV photons emitted by a 50 mCi 241Am radioactive source. The emitted K x-rays were detected by an Ultra-LEGe detector having a resolution of 150 eV at 5.9 keV. In addition, the effect of bath composition on the phase structure was investigated by x-ray diffraction (XRD) analysis. The composition of the thin films was analyzed by atomic absorption spectrometry analysis. Iron content was shown to strongly affect the structure of Zn-Fe alloys. It was found that the K-shell x-ray intensity ratio changed ...

International Nuclear Information System (INIS)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Energy Technology Data Exchange (ETDEWEB)

Accelerated aging tests on gold bridgewired detonator assemblies to determine compatibility of the Au and Pd-In-Sn solder with the organic explosive, PENT, have revealed an unusual corrosion process. These tests, conducted at 74/sup 0/C and 54/sup 0/C indicated a preferential attack of the gold. A matrix of corrosion test units was established to study this corrosion problem with accelerating temperatures up to 100/sup 0/C. Scanning electron microscopy (SEM), energy dispersive x-ray (EDX), and x-ray diffraction techniques were used to determine the extent of the corrosion and identify the corrosion products. Results indicate the preferential attack of the gold was due to HCN formed by decomposition of the explosive powder (PETN) at high temperatures. Other associated reactions were also observed including subsequent attack of the solder by the gold corrosion product and degradation of the plastic ...

International Nuclear Information System (INIS)

Full text: Institute for Nuclear Research, Pitesti-Mioveni, Romania in direct cooperation with the National Institute for Laser, Plasma and Radiation Physics, Magurele, Bucharest studied and prepared for coating more than 1000 tiles made of Inconel with 7-9 #mu#m of beryllium for nuclear fusion applications at JET, Culham, UK. The principles of manufacturing processes using thermal evaporation and plasma ignited in pure metal vapors as well as by Thermionic Vacuum Arc (TVA) method and the properties of the Ni and Be coatings are presented. The prepared beryllium layers were characterized by scanning electron microscopy, transmission electron microscopy, X-ray diffraction, X-ray photoelectron spectroscopy and atomic force microscopy. (authors)

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

The NiO-samaria doped ceria (SDC) composite powders were prepared by spray pyrolysis technique at temperatures between 400 and 1000 C. The variation of the particle structure was investigated by X-ray diffraction (XRD), X-ray absorption fine structure (XAFS), scanning electron microscope (SEM), and transmission electron microscope (TEM)-energy-dispersive X-ray spectroscopy (EDS). The thermal analysis of raw materials was also carried out. The following facts became clear in this study. Ceria and nickel have been already separated at 400 C. Samaria is amorphous phase below 600 C, and is dissolved in ceria at 600 C or higher. Samaria is distributed uniformly inside the particles before dissolving in ceria. The thermal decomposition temperatures of metal nitrate are: cerium < nickel < samarium. The results of these analyses were explained without contradiction. It was ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

X-ray diffraction offers a unique combination of advantages for kinetic study which include the non-destructive nature of the measurement, the use of bulk crystals, and the convenience of the experimental arrangements. These attributes and the availability of position-sensitive detectors and high-flux synchrotron radiation sources make this technique most useful for in situ, dynamical investigations. When using diffraction techniques to determine a diffusion coefficient, the principle of analysis entails a scattering theory and a kinetic model. The former allows the kinetic parameter(s) to be extracted from measured intensity, while the latter relates the kinetic parameter(s) to the diffusion coefficient(s). Three examples are demonstrated: (1) Palladium Silicide (Pd{sub 2}Si) Layer Growth on Silicon, (2) Decomposition of an Ni-12.5at%Si Superalloy, and (3) Short-range Ordering in Cu-Au Solid Solutions.

International Nuclear Information System (INIS)

Formation of the soft magnetic nanostructure in amorphous Fe_1_4Ni_4_0Zr_7B_1_2 alloy due to heat treatment is studied by the Moessbauer, differential scanning calorimetry, and X-ray diffraction techniques. Annealing at temperatures 520-580 "oC leads to the formation of extremely soft nanocrystalline alloy as revealed by the rf-Moessbauer measurements. The superparamagnetic behaviour was observed for the alloy annealed at 620-640 "oC. At higher annealing temperatures good soft magnetic properties deteriorate. (author)

International Nuclear Information System (INIS)

Three types of titanium hydrides have been reported: #delta#, #epsilon# and #gamma# hydrides. The #delta# hydride forms in the composition range from TiH/sub 1.5/ to TiH/sub 1.99/ and has a CaF/sub 2/ structure with metal atoms on an fcc lattice and hydrogen atoms randomly occupying tetrahedral interstitial sites. At higher hydrogen concentrations, TiH/sub 2/, the fct (c/a # #epsilon# transformation is apparently diffusionless, similar to that operating in the cubic/tetragonal transformation in zirconium hydride. The metastable fct #gamma# hydride having a c/a value of 1.09 or 1.12 forms from solid solutions of hydrogen in the hcp #alpha# matrix. While the titanium hydride precipitation in #alpha#-Ti and its alloys has attracted extensive investigation, hydride formation in bcc #beta#-Ti alloys has rarely been studied because they have not been thought to be liable to hydride formation. This paper shows conclusive evidence for the fcc #delta# hydride phase ...

International Nuclear Information System (INIS)

Nano-sized zinc oxide was synthesized and deposited onto cellulosic fibers using the sol-gel process at ambient temperature. The prepared materials were characterized using several techniques including scanning electron microscopy, transmission electron microscopy, diffuse reflectance spectroscopy, X-ray diffraction and thermogravimetric analysis. X-ray diffraction studies of the ZnO-coated fiber indicate formation of the hexagonal crystal phase which was satisfactory crystallized on the fiber surface. The electron micrographs show formation of zinc oxide nanoparticles within 10-15 nm in size which have been homogeneously dispersed on the fiber surface. The prepared materials show significant photocatalytic self-cleaning activity, which was monitored by diffuse reflectance spectroscopy. The photoactivity was studied upon measuring the photodegradation of ...

International Nuclear Information System (INIS)

Single crystals of semi-organic L-histidine hydrobromide have been grown by slow evaporation technique from a mixture of L-histidine and hydrobromic acid in aqueous solution at ambient temperature. From high-resolution X-ray diffraction analysis, the crystalline perfection of the grown crystal has been studied. Single crystal X-ray diffraction analyses, Nuclear Magnetic Resonance spectral analysis, Thermo-Gravimetry (TG), Differential Thermal Analysis (DTA) and hardness test have been employed to characterize the as-grown crystals. The UV cutoff wavelength of the grown crystal is below 300 nm and has a wide transparency window, which is suitable for second harmonic generation of laser in the blue region. Nonlinear optical characteristics have been studied using Q switched Nd:YAG laser (#lambda#=1064 nm). The second harmonic generation conversion efficiency of ...

Energy Technology Data Exchange (ETDEWEB)

Nitriding leads to improved tribological and corrosive properties of iron alloy components. In order to study the effect of plasma nitriding parameters on the structure of compound layer and diffusion zone, a systematic variation of process parameters, temperature and process gas atmosphere has been carried out. Metallographic inspection, X-ray diffraction and glow discharge optical spectroscopy analysis (GDOES) were used in this investigation. The results clarified that depending on the amount of nitrogen in the gas atmosphere nitrided layers with and without compound layer can be generated in the surface of M2 tool steel for temperatures from 350 C to 500 C. For plasma nitriding in 5 vol.% Nitrogen and 95 vol.% Hydrogen no compact compound layer was formed. The gas mixture of 76 vol.% Nitrogen resulted in compound layer formation for all temperatures from 350 C to 500 C. X-ray phase analysis indicated ...

Energy Technology Data Exchange (ETDEWEB)

17-4PH stainless steel was modified by direct current (DC) plasma nitriding and titanium nitride film duplex treatment in this study. The microstructure, wear resistance and corrosion resistance were characterized by X-ray diffraction (XRD), pin-on-disk tribological test and polarization experiment. The results revealed that the DC plasma nitriding pretreatment was in favor of improving properties of titanium nitride film. The corrosion resistance and wear resistance of duplex treatment specimen was more superior to that of only coated titanium nitride film.

British Library Electronic Table of Contents (United Kingdom)

Methods of X-ray diffraction and transmission electron microscopy were used to study the microstructure of dispersion-strengthened Cu-Al2O3 nanocomposites obtained by the method of simultaneous deposition of Cu and Al2O3 from the vapor phase. The effect of the size of particles of the oxide (Al2O3) and of their content on the electrical resistance of the composite has been considered. The results obtained make it possible to suppose that the main structural factor that determines the electrical resistance of the composite are nanodispersed particles of Al2O3 with a size of less than 20 nm.

British Library Electronic Table of Contents (United Kingdom)

The mechanism of abrupt increase of the giant magneto impedance (GMI) ratio in the ion irradiated Co-based amorphous ribbon has been investigated. The grazing incident X-ray diffraction and transmission electron microscope were used to characterize the samples before and after ion irradiation. The GMI-ratio considerably increased in the ion irradiated samples and the GMI response showed strong dependence on the driving frequencies. The Barkhausen noise (BN) signals are increased for the Ar ion irradiated sample with dose of 1x10^1^7 ion/cm^2. The results are interpreted in terms of GMI variation associated with domain wall dynamics.

Energy Technology Data Exchange (ETDEWEB)

A study is reported of the use of three types of fly ash as a raw material in the production of a potassium silicate fertilizer. The results of high-temperature X-ray diffraction, calcination tests and chemical analyses indicate that a potassium silicate fertilizer conforming with fertilizer specifications can be produced by appropriate regulation of calcining temperature and the amounts of Fe/sub 2/0/sub 3/, Al/sub 2/O/sub 3/, MgO and CaO added. The results of tests of fertilizers incorporating red mud are also reported.

Energy Technology Data Exchange (ETDEWEB)

Crystal structure of monoclinic telluric acid ammonium phosphate (TAAP) has been studied by an X-ray diffraction method in the paraelectric phase at 333 K and in the ferroelectric phase at room temperature. It is confirmed that the space group in the paraelectric phase is P2/n. Comparison of the results between the two temperatures suggests that the plane which is made by the PO{sub 4} tetrahedron linked by hydrogen bonds has an important role for the ferroelectric phase transition. This plane is almost parallel to the direction of spontaneous polarization.

Energy Technology Data Exchange (ETDEWEB)

The influence of Cr on the structure and electrochemical properties of LiCoVO{sub 4} was studied using X-Ray diffraction, scanning electron microscopy, Raman Spectroscopy and cycle tests. Doping levels up to 10 mol% were achieved, which improved the electrochemical stability of the structure of LiCoVO{sub 4}, resulting in a significant increase in the initial charge and discharge capacity. The Raman spectroscopy data for the Cr-doped LiCoVO{sub 4} is similar as for LiCoVO{sub 4}. The replacement of a dopant for the Co-ion in the inverse spinel structure causes several Raman shifts. The X-ray diffraction patterns show no new phases and combined with the Raman spectroscopy data it is concluded that the Cr dopant will be located at the octahedral site (16d) where they create an electronic pathway that enhances the electronic conductivity. However, the capacity dropped significantly ...

Energy Technology Data Exchange (ETDEWEB)

A method has been developed to optimize the energy resolution of a horizontally focusing monochromator. The method consists of determining the optimum radius of curvature of the cylindrically bent monochromator crystal by minimizing the total diffracted X-ray flux measured through an X-ray absorption foil. When measured at an absorption edge a global minimum can be identified, which corresponds to the minimum energy band accepted along the entire length of the crystal. Experimental verification of this method has been validated by comparing X-ray fluorescent scans taken for a series of crystal curvatures and by directly measuring the X-ray beam profiles at the corresponding points. The actual optical configuration and asymmetric-cut parameter of the focusing monochromator on beamline X4C at the National Synchrotron Light Source are modeled and ray tracing simulations of the optical ...

International Nuclear Information System (INIS)

The structure of nano-porous carbon, obtained by means of chlorination of carbide compounds with various crystal structure (SiC, TiC, Mo_2C) is studied through the method of small-angle diffraction. The angular dependences of the scattering intensity obtained are interpreted as the result of scattering from the nanoparticles of different size. The functions of the scattering particles distribution by the m(R_g) inertia radii are determined. It is shown that in spite of the source carbide, the highest fraction of the volume in the porous carbon constitute the particles with R_g #approx# 5 A. The nanoparticles in the samples obtained from SiC, wherein the average value of the R_g"a"v < 6 A, are most uniform by size. The nanoparticles in the porous carbon, obtained from Mo_2C, are on the average by two times larger

International Nuclear Information System (INIS)

The results of X-ray and neutron diffraction experiments on molten alkali halides in which some data of our experiments by X-ray diffraction such as those of molten LiCl, NaCl, KCl, LiBr and KBr are included were summarized. The first peak positions in the radial distribution function in molten alkali halides by X-ray or neutron diffraction experiments are always longer than those by computer simulations and the differences of 0.1 -- 0.3 A exceed the experimental error. It seems to be due to the deformation of the electron shell. In the computer simulation, the shell model which has the spherical deformation was expected to have more closer value of the first peak position to the experimental one than the rigid ion model by taking the polarization of ions. However, no change in the first peak position was found. Therefore, the non-spherical deformation of ...

International Nuclear Information System (INIS)

Oxide superconducting thin films were irradiated with X-rays and ultra-violet (UV) light, and induced radiation effects on electrical and chemical properties were examined by transport measurement, X-ray diffraction analysis (XRD), diamagnetization measurement and X-ray photoemission spectroscopy (XPS). After irradiation for ErBa_2Cu_3O_x films with X-rays emitted from a Rh tube for 100 hours, superconductivity was remarkably damaged, destroying the zero-resistance state. The UV-light irradiation for Bi_2Sr_2CaCu_2O_x films was performed in He gas of about 500 Pa with a low pressure mercury lamp. The superconductivity was gradually degraded with the UV irradiation time up to 70 minutes. In both cases, adequate oxygen-annealing treatments restored superconductivity. The X-ray photoemission spectra showed that the mean Cu valence of the films was decreased ...

CERN Document Server

The resolution of X-ray diffraction microscopy is limited by the maximum dose that can be delivered prior to sample damage. In the proposed Serial Crystallography method, the damage problem is addressed by distributing the total dose over many identical hydrated macromolecules running continuously in a single-file train across a continuous X-ray beam, and resolution is then limited only by the available molecular and X-ray fluxes and molecular alignment. Orientation of the diffracting molecules is achieved by laser alignment. We evaluate the incident X-ray fluence (energy/area) required to obtain a given resolution from (1) an analytical model, giving the count rate at the maximum scattering angle for a model protein, (2) explicit simulation of diffraction patterns for a GroEL-GroES protein complex, and (3) the frequency cut off of the ...

International Nuclear Information System (INIS)

(1972). USSR Sviryakin, DI Manets, AI Kolupaev, AN v. 213 p. 111-114.

International Nuclear Information System (INIS)

Full text: The production of #beta#-sialon from kaolinite and carbon has been studied using Hulu Langat Kaolin and activated carbon as raw materials. The sintered temperature is shown to play a prominent role in the process of sialon conversion. Apart from temperature, nitrogen flow rate is also affect the production of #beta#--sialon. This study was carried out on the effect of additive, Y_2O_3 and Al_2O_3 at different temperature that will be mixed and sintered. The additives are expected to affect the formation of #beta#--sialon and Y-sialon upon the synthesis. The mineral and phase development was analysed using X-Ray Diffraction technique (Rigaku Geigerflex) while its chemical compositions through X-Ray Fluorescent Spectrophotometer (Shimadzu XRF 1700) and the particle size distribution analysis through Particle Size Analyser (Horiba, CAPA 700). The observed changes in the ...

International Nuclear Information System (INIS)

The possible existence of preferential B-site disorder in A-15 compounds recently claimed on the basis of x-ray powder diffraction data but questioned from the viewpoint of known phase diagrams is examined for some Nb-based compounds of this type. It is concluded that x-ray powder data do not allow the determination of both order and compositional variables as suggested, and the latter must therefore be determined by some other method. (author).

UK PubMed Central (United Kingdom)

PurposeThe goal of this study was to clarify the dynamics of tumor oxygen (partial pressure of oxygen, pO₂) in SCC VII murine tumors in mice after X-ray...Full Text Available

UK PubMed Central (United Kingdom)

Previous studies have shown that iterative in-line x-ray phase retrieval algorithms may have higher precision than direct retrieval algorithms. This communication compares three iterative phase...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

Here in the present paper, we report on growth of stoichiometric and nonstoichiometric nanostructured heterojunction solar cell of CdS/CuInSXSe2-X varying X from 0 to 2 in the interval of 0.5 using cost effective, simple, chemical ion exchange method at room temperature on ITO glass substrate. The as-grown varying composition solar cells annealed at 200degreeC in air and characterized for structural, compositional, optical and illumination studies. The X-ray diffraction pattern obtained from CdS/CuInSXSe2-X solar cell confirms the formation of CuInSe2, CuInS0.5Se1.5, CuInS1Se1, CuInS1.5Se0.5 and CuInS2 phases having tetragonal structure with varying crystallite size from 19, 19.37, 28, 33 and 20nm respectively. The energy dispersive X-ray analysis (EDAX) confirms the expected elemental com...

Energy Technology Data Exchange (ETDEWEB)

Ion bombardment during deposition can significantly modify the film properties. In the partially ionized beam deposition, ions derived from the depositing material, i.e., the self-ions, are used during deposition. Cu films were deposited on SiO{sub 2} substrates at room temperature using 1% Cu self-ions with an energy ranging between 0--4 keV. We studied the microstructures of the Cu films using x-ray diffraction and transmission electron microscopy, measured the impurity level inside the films using secondary ion mass spectrometry, and performed the resistivity measurements using a four point probe. The results indicate that there is an optimum ion energy around 2 keV at which, the integrated x-ray intensity ratio {ital I}(111)/{ital I}(200) reaches its maximum value indicating a strong {l angle}111{r angle} texture, while the impurity concentration and resisitivity are minimum. The correlation between ...

British Library Electronic Table of Contents (United Kingdom)

A magnetic core/shell Fe3O4/FeMnOx catalyst was prepared by a simple oxidation-precipitation method. The catalyst was characterized by X-ray diffraction, transmission electron microscope, X-ray photoelectron spectroscopy, Fourier transform infrared spectroscopy, thermogravimetric analysis and cyclic voltammetry. The characterization studies verified that Fe3O4 core was coated with a layer of Fe-Mn oxide. The Fe3O4/FeMnOx was found to be an effective and stable heterogeneous catalyst for the discoloration of methylene blue (MB) in aqueous solution by H2O2. The high catalytic activity is due to the FeMnOx shell, which not only increased the surface hydroxyl groups, but also enhanced the interfacial electron transfer. The discoloration of MB could be due to the decomposition of H2O2 into ?OH ...

International Nuclear Information System (INIS)

This paper reports on a series of experiments performed to examine the ability of ion beam assisted thermal deposition to produce good adhesion of Au metallization on GaAs left-angle 100 right-angle substrates. A study of the influence of Ar ion-assisted thermal deposition of the Au films as well as in situ pre-sputtering of the GaAs surface with low-energy Ar ions prior to thermal deposition, shows that strong adhesion can be achieved without resorting to chemical cleaning. The substrate temperature and the relative flux of Ar ions to incident Au atoms were varied in order to correlate these parameters with film adhesion. The interfaces of films processed under these various conditions were examined by XTEM, RBS and XPS. Orientation texture was studied by x-ray diffraction (XRD).

Science.gov (United States)

A high degree of structural perfection is an essential requirement for CdTe crystals used as substrates for the epitaxial growth of CdHgTe alloys. Here, a method for the evaluation of the structural perfection of CdTe crystals is proposed which is based on X-ray diffraction measurements using both two-crystal and three-crystal diffractometers (differential version). The method makes it possible to obtain more information on structural perfection both at the crystal surface and within the crystal body.

International Nuclear Information System (INIS)

Chemical effects of L X-ray intensity ratios in niobium and molybdenum compounds were studied by electron and proton bombardments. L_#gamma#_1 X-rays which involve transition of 4d electrons of the valence shell were found to be sensitive to the chemical environment. The L_#gamma#_1/L_#beta#_1 X-ray intensity ratio increased with an increase of the 4d electron occupation of niobium or molybdenum in niobium or molybdenum compounds, showing that the chemical effects can be ascribed to the 4d electron behavior of the metallic atom in its compounds. (orig.).

International Nuclear Information System (INIS)

In this paper, the influence of plasma nitriding at temperature 720 deg. C for 20 h on the surface microstructure and interface microstructure of electroplated chromium coating was investigated. In these conditions, interdiffusion, mixing and reaction phenomena of elements originating from the substrate and coating material are more likely to occur, thus increasing the bonding strength between the coating and carbon steel substrate. The change of the structures from the substrate side to the coating surface, and the effect of the substrate steel on the interface structure were studied by cross-sectional transmission electron microscope observation (XTEM). The nitride layer formed on the surface was analyzed by X-ray diffraction method (XRD). After treatment at above conditions a 6-7 #mu#m thick nitride compound layer was formed in surface region and the same thick carbide compound layer was also formed in the interface ...

British Library Electronic Table of Contents (United Kingdom)

Antibacterial activity of Transition metals (Mn, Co) doped ZnO nanopowders prepared by a DC thermal plasma method against Escherichia coli and Staphylococcus aureus are investigated. The phase and morphology studies have been carried out by X-ray diffraction, scanning electron microscopy (SEM) and transmission electron microscopy (TEM) respectively. All the samples of the present investigation are found to have hexagonal wurtzite structure and crystallite sizes are found to vary from 25nm to 30nm. Our bacteriological study showed the enhanced antibacterial activity of transition metals doped ZnO nanoparticles than undoped ZnO indicating the great potential of ZnO nanoparticles in relevant clinical and biomedical applications.

Energy Technology Data Exchange (ETDEWEB)

Three-dimensional porous Sn thin film electrodes were prepared by electroless deposition on copper foam, then its morphology and electrochemical property were studied by means of scanning electron microscope (SEM), X-ray diffraction (XRD), electrochemical cycling test and cyclic voltammetry (CV). The porous framework and micro-holes have shown a great structure advantage in restricting severe volume changes when the Sn thin film was employed as anode for lithium-ion battery. The film electrode of sample C with an initial capacity of 676 mAh g{sup -1} showed good cycle performance displayed by retaining a capacity of 313 mAh g{sup -1} after 100 cycles.

British Library Electronic Table of Contents (United Kingdom)

Dopant-free Bi2Ti2O7 thin films with pyrochlore structure and La-doped bismuth titanate thin films have been fabricated by means of chemical solution decomposition, and characterized by X-ray diffraction, atomic force microscopy, scanning electron microscopy and UV?Vis spectrophotometry in this study. Their photocatalytic activities have been evaluated by photodegrading methyl orange solution, and the optimum processing parameters for the highest photocatalytic activity have been found. Moreover, the effects of La-doping on the phase transformation and the photocalalytic activity have been studied. It has been deduced from the experiment result that substituted La3+ ions can act as a stabilizer of Aurivillus phase BLT and a grain?growth inhibitor in BLT thin films.

Energy Technology Data Exchange (ETDEWEB)

With the aim of optimizing the nitriding process, experimental studies of the plasma nitriding of four selected steels were carried out, using a d.c. glow discharge. The process parameters were varied systematically. By means of transmission and scanning electron microscopy and X-ray diffraction, the microstructures, including the thicknesses of the compound zones and the diffusion zones of the nitrided steels, were obtained. Using cross-sectional samples and a micro-Vickers indenter, hardness depth profiles were also obtained. From the time and temperature dependences of the hardness profiles, effective diffusion constants and corresponding activation enthalpies were obtained. Furthermore, in an attempt to shed some light on the atomistic nitriding mechanisms, the glow discharges were studied by measuring energy spectra of the energetic ions hitting the cathode (the steel test specimens). It was shown ...

Energy Technology Data Exchange (ETDEWEB)

Sintered glass-ceramics have been produced using municipal incinerator solid residues and glass cullet or an inert waste, from feldspars processing, as sintering aids. The capability of three different mixtures, either previously vitrified or not, to be sintered was investigated by means of linear shrinkage, water absorption and bulk density measurements, and by X-ray diffraction analysis and scanning electron microscopy observations. Particular attention has been addressed to the study of particle size effect on the sintering process. The conclusions that can be drawn from the experimental study are that the preliminary vitrification step is essential in order to obtain a dense sintered glass-ceramic product in the 850-1050 C temperature range developing silicate crystalline phases. The optimal powder particle size that confers a good densification degree was found to be < 45 {mu}m. (orig.)

Energy Technology Data Exchange (ETDEWEB)

More than 2,500 Moessbauer spectroscopic studies on minerals have been published since 1960. These papers contain approximately 8,000 sets of Moessbauer mineral data on at least 400 different minerals. This information has been compiled into a database that includes isomer shifts, quadrupole splittings, and magnetic hyperfine interactions at room, liquid nitrogen, and liquid helium temperatures. The database provides a profile of the Moessbauer research performed to date on minerals, including type and locality of minerals investigated, significance of the studies and results, and location of the research facilities. The data and information are available both in printed and magnetic form.With the establishment of this resource, the Moessbauer Effect Data Center has begun a systematic evaluation of the Moessbauer mineral data. It is anticipated that this resource can be used for the identification of minerals as powder ...

International Nuclear Information System (INIS)

Based on a literature study an actual summary of the risk-utility problems in X-ray diagnosis is outlined due to the Recommendations of the International Commission for Radiation Protection (ICRP publication 26/1977). Papers demonstrating quantitative assessment of the somatic and genetical risk in X-ray examination are preferably cited and evaluated. It is concluded that the somatic and genetical risk is low in diagnostic ratiology. However, it must not be neglected and has always to be compared to the utility of an examination as well as to other risks of the examination. (author).

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction enhanced imaging (DEI) is one of X-ray phase-contrast imaging methods, which is applied to inspect internal structures of weakly absorbing low-Z samples. The key problem of the DEI is how to extract phase information which is expressed by refraction-angle images from a series of DEI images measured in different positions of the rocking curve of the analyzer. Three effective extraction methods are presented in this paper: the statistical geometric-optics-approximation method, the maximum refraction-angle method and the Gaussian curve fitting method. They are compared with the existing methods, such as the D. Chapman's geometric optics approximation method and the multiple-images statistical method. A 2D computer simulation experiment is performed to draw comparisons of these methods. The experimental results prove that the above three methods have more precision of refraction-angle values than ...

International Nuclear Information System (INIS)

We have investigated the microstructure evolutions in the Ti17 near #beta# titanium alloy during heat treatments. The phase transformation has first been studied experimentally by combining X-ray diffraction analysis, electrical resistivity and microscopy observations. From a series of isothermal treatments, a IT diagram has been determined, which takes into account the different morphologies. Then, a Johnson-Mehl-Avrami-Kolmogorov (JMAK) model has been successfully used to describe the phase transformation kinetics during either isothermal or cooling treatments. Finally, the coupling of the JMAK model to the finite element software ZeBuLoN allowed us to investigate the evolution of the spatial distribution of the different morphologies during the cooling of an aircraft engine shaft disk after forging.

British Library Electronic Table of Contents (United Kingdom)

A series of novel triazolinones were synthesized and their structures were characterized by 1H NMR, elemental analysis and single-crystal X-ray diffraction analysis. The herbicidal activities were evaluated against Echinochloa crusgalli (L.) Beauv., Digitaria adscendens, Brassica napus and Amaranthus retroflexus. The herbicidal activity data indicated that the title compounds had higher activities with substituted benzyl group moieties than with other groups such as sulfonyl, alkyl, etc. To further investigate the structure-activity relationship, comparative molecular field analysis was performed on the basis of herbicidal activity data. Both the steric and electronic field distributions of comparative molecular field analysis are in good agreement in this work. The results showed that a b...

International Nuclear Information System (INIS)

Nuclear forensic activities, such as in illicit trafficking, can solve a problem who did it and can gain the basis for a response. Other than that, the forensics can be also applied to solve on what are materials, who is responsible, is there more, where was material diverted and what route did the material taken. BATAN, in fact , owns a lot of equipment which can be supported for nuclear forensics activities, such as, Transmission Electron Microscope (TEM), Scanning Electron Microscope (SEM) as well as X-Ray Diffraction (XRD). For the first step, BATAN has to be an active, participate member of The International Technical Working Group on Nuclear Smuggling (ITWG). BATAN can then collaborate not only with Indonesia Arm Forces and Police, but also with other foreign institutions to develop this activity with mutual advantages agreement.

International Nuclear Information System (INIS)

The constituent phases and associated deformed microstructure of the quenched Ti-xNb-(0.5-1.5) at.% Si alloy consisting of non-cytotoxicity elements, where x = 24-30 at.%, were investigated to provide pseudoelasticity for biomedical and sensor applications. Optical microscopy revealed that stress-induced martensitic transformation takes place during the deformation in the present alloys. It is confirmed from the X-ray diffraction results of the deformed specimens that the crystal structure of the stress-induced martensite phase is the orthorhombic so-called #alpha#'' structure. Within the alloys having #beta#(bcc) phase studied Nb-poor region appeared to exhibit a dominant behavior for stress-induced martensitic transformation than Nb-rich region. This result suggests that metastable #beta# phase is superior to stable #beta# phase for the occurrence of stress-induced martensitic transformation in the present alloy system.

British Library Electronic Table of Contents (United Kingdom)

Indium sulfide thin films consisting of porous network of nanoplatelets, have been deposited using chemical bath deposition (CBD) method onto the tin-doped indium oxide (ITO) coated glass substrate. Aqueous solutions of indium sulfate and thioacetamide have been used as indium and sulfur precursors. As a complexing agent, acetic acid was used. The chemically deposited indium sulfide thin films were examined for their structural, surface morphological and optical characterizations. The X-ray diffraction analysis revealed the formation of the cubic b-In2S3 onto the substrate. From scanning electron micrograph, it is observed that the surface of substrate is covered by nanoporous platelets type morphology. The optical studies showed a direct band gap of 2.84eV for indium sulfide platelets. Ph...

British Library Electronic Table of Contents (United Kingdom)

The growth of silver chloride nanoparticles on ancient textile was achieved by sequential dipping steps in alternating bath of potassium chloride and silver nitrate under ultrasound irradiation. The effect of ultrasound irradiation and sequential dipping steps in growth of the AgCl nanoparticles has been studied. These systems depicted a decrease in the particles size accompanying a decrease in the sequential dipping steps. The samples were characterized with powder X-ray diffraction (XRD) and scanning electron microscopy. XRD analyses indicated that the prepared AgCl nanoparticles on fiber were crystalline. The textile samples containing AgCl nanoparticles were tested for their antibacterial efficacy against Escherichia coli and were found to possess significant antibacterial activity.

Energy Technology Data Exchange (ETDEWEB)

Microalloyed or high strength low alloy (HSLA) steels are carbon-manganese steels containing small amounts of Nb, V or Ti. The excellent mechanical properties of these alloys, particularly high yield strength, usually obviate the need for expensive quench and tempering operations. Furthermore, the presence of a significant amount of nitride-forming elements in some microalloyed steels has generated interest in the applicability of these alloys as a new generation of nitriding steels. In this paper, a study of the plasma nitriding behaviour of a commercially available microalloyed steel MAXIMA{sup TM} is reported. A comparison is made with a traditional quenched and tempered nitriding steel (En19), plasma nitrided under similar conditions. Optical and scanning electron microscopy in conjunction with microhardness measurements and X-ray diffraction were utilized to characterize the nitrided surfaces. The observed differences ...

Energy Technology Data Exchange (ETDEWEB)

We present a synchrotron x-ray diffraction study of melting in stacks of two-dimensional crystalline arrays of the membrane protein bacteriorhodopsin. Two distinct regimes have been found as a function of the intermembrane distance d . In the {open_quotes}coupled{close_quotes} regime for d{lt}250 {Angstrom} the temperature (T{sub m}) of the melting transition decreases with increasing d , demonstrating the effect of the repulsive membrane interactions on the intramembrane protein ordering. For d{gt}250 {Angstrom} a {open_quotes}decoupled{close_quotes} regime is found with higher T{sup *}{sub m} independent of d . Below T{sup *}{sub m} a solid-liquid-solid reentrant behavior is observed as d is increased. {copyright} {ital 1999} {ital The American Physical Society}

Energy Technology Data Exchange (ETDEWEB)

The microstructure of the layers produced by plasma nitriding austenitic stainless steel at different treatment temperatures (400 and 500 C) were studied by transmission electron microscopy (TEM) together with X-ray diffraction (XRD) and scanning electron microscopy (SEM). The results show that the microstructures were composed of 'expanded austenite' ({gamma}{sub N}) and {alpha}(ferrite)+CrN following plasma nitriding at lower and higher treatment temperatures, respectively. The former contains stacking faults and deformed twin substructures, while the latter is made up of colonies displaying a lamellar structure. Kurdjumov-Sachs or Nishiyama-Wassermann orientation relationships between the {alpha} and CrN layer were observed. (orig.)

International Nuclear Information System (INIS)

Silicon layered structures containing porous silicon modified with various thermal treatments and epitaxial layers deposited on porous layers were studied with a number of complementary X-ray diffraction methods using synchrotron source. The methods of characterization included recording of rocking curves for reflections with various asymmetry as well as projection, section and micro-Laue topography. It was found that oxidizing and sintering of porous silicon seriously modified the strains in the porous layer and in some cases even inverting the sense of strain with respect to that in initially formed porous layer. Consequently the deposited epitaxial layer usually was not laterally coherent with the substrate. Some of investigated layers were not stable in time and after few months period exhibited significant lost of coherence of porous skeleton. (author)

International Nuclear Information System (INIS)

To study #beta# #reversible# #omega#-transformation in pseudo-#beta#-titanium alloy VT30, doped by hydrogen, methods of X-ray diffraction and thermodifferential analyses are used. It is established that in the process of heating of the hardened alloy from 0.004-0.1% H first formation and then dissolution of #omega# phase take place. An increase in hydrogen content to 0.1% decreases thermal effect of the processes and does not affect the temperature of #beta# #reversible# #omega#-transformation. Introduction of hydrogen in the concentration of 0.2% and higher suppresses completely #beta# #reversible# #omega# - transformation. A decrease in heating rate displaces #beta# #reversible# #omega#-transformation to lower temperatures.

Science.gov (United States)

The phase stability of silicides of Ni, Pt and Pd in contact with single crystal or amorphous silicon is examined. The presence of a particular silicide phase is identified by X-ray diffraction, and Rutherford backscattering is used to study composition. It is concluded that Pt or Pd silicides are suitable for Schottky barriers. Layers of silicon can be grown quickly by solid phase epitaxy at temperatures of 300-500C and using an intermediate metal film. Experimental results are reported. Doped layers have been obtained which have electrical characteristics suitable for the junctions in solar cells. The effects of impurities and orientation of the substrate on the growth kinetics are discussed.

International Nuclear Information System (INIS)

Ferroelectric [Pb_0_._9_2(La_1_-_zSb _z)_0_._0_8][Zr_0_._6_0Ti_0_._4_0]O_3 for z = 0.0, 0.3, 0.6, 0.9 and 1 were prepared from their constituent oxides by a solid state reaction technique. The powders were calcined in the temperature range of 1000 deg. C for 6 h. Phase formation, crystal structure and lattice parameter were investigated by X-ray diffraction (XRD) technique. The compacts were sintered at 1250 deg. C for 2 h and their dielectric, ferroelectric and conductive properties were measured. The ferroelectric behavior of the doped samples was studied from their hysteresis loop.

Energy Technology Data Exchange (ETDEWEB)

The authors present results of grazing incidence X-ray diffraction studies concerning the effect of pH (and thus, of headgroup dissociation) on Langmuir monolayers of fatty acids, in the absence of any divalent cations in the aqueous subphase. An increase in pH transforms the distorted-hexagonal S phase first to the partially disordered Rotator-I phase with less distortion, and then to the completely disordered Rotator-II phase with an undistorted hexagonal structure. The S-Rotator-I and Rotator-I-Rotator-II transitions are pushed to lower temperatures with increase in pH. The fact that the effects of pH increase are almost identical to the effects of increasing temperature indicates the important role of headgroup-headgroup interactions in these monolayer phases.

British Library Electronic Table of Contents (United Kingdom)

In the present study the optical properties of co-evaporated indium sulfide thin films are investigated. Before being optically characterized, the composition as well as the crystalline properties of the film have been checked with the help of energy dispersive spectroscopy (EDX) and X-Ray diffraction (XRD) analyses. The optical absorption coefficient ? of this indium sulfide film has been deduced from reflectivity R(?) and transmission T(?) measurements. The fit of the curve representing ?(h?) suggests that the ?-In2S3 has an indirect bandgap of 2.01?eV. Density functional theory (DFT) calculations are performed on this indium sulfide compound, using TB-LMTO code. Through these band structure investigations, an indirect bandgap is predicted as observed experimentally. The top of the valen...

International Nuclear Information System (INIS)

The compounds CePdSi_2, CeIrSi_2 and CeRhSn_2 have been synthesized and studied by X-ray diffraction, electrical resistivity and magnetic susceptibility. The magnetic susceptibility of CePdSi_2 exhibits two peaks at 6.8 K and 2.5 K, respectively, indicating two antiferromagnetic phase transitions, while that of CeIrSi_2 shows a broad maximum at 150 K, characteristic of valence fluctuating Ce-compounds. CeRhSn_2 remains paramagnetic down to 5 K. The resistivity of CeIrSi_2 exhibits a T"2 dependence at low temperatures, indicating a Fermi-liquid ground state, while those of CePdSi_2 and CeRhSn_2 shows the presence of Kondo and crystal field effects. (orig.).

British Library Electronic Table of Contents (United Kingdom)

A novel liquid phase alkylation of aniline with methanol over Zn/Cu salts modified kaolin assisted with a pair of porous carbon electrode in slurry-bed reactor under constant current intensity, room temperature and atmospheric pressure was reported. The Zn/Cu salts modified kaolin catalysts were synthesized and characterized by infrared spectrometer (IR), powder X-ray diffraction (XRD) and scanning electron microscopy (SEM), which showed that the transition metals were completely supported on kaolins structure and formed a pored one. The effect parameters, such as initial pH, electrolysis time, metal ratio with kaolin and salts composition in this electrochemical catalytic system, were studied. The procedure was inspected by ultraviolet-visible spectrum (UV-vis), and the product distributi...

Energy Technology Data Exchange (ETDEWEB)

The peak flux relationship between hard X-rays and microwaves from solar flares is studied using about 400 events simultaneously recorded with the hard X-ray burst spectrometer on the SMM satellite and the Nobeyama 17 GHz radiometer. The data indicate that the hard X-ray and microwave peak fluxes correlate best for X-ray energies of less than about 80 keV for impulsive flares and greater than about 360 keV for extended flares. By postulating that electrons responsible for microwave emission at 17 GHz are those emitting hard X-rays at these photon energies, it is concluded that: (1) in impulsive flares, microwaves at about 20 GHz are emitted mainly by electrons of less than about 200 keV from a layer through which the electrons stream down into the thick-target hard X-ray source; and (2) in extended flares, microwaves are emitted mainly by ...

International Nuclear Information System (INIS)

Field emitter devices are being developed for the gigatron, a high-efficiency, high frequency and high power microwave source. One approach being investigated is porous silicon, where a dense matrix of nanoscopic pores are galvanically etched into a silicon surface. In the present paper pore morphologies were used to characterize these materials. Using of Scanning Electron Microscope (SEM) and Transmission Electron Microscope (TEM) images of both N-type and P-type porous layers, it is found that pores propagate along the <100> crystallographic direction, perpendicular to the surface of (100) silicon. Distinct morphologies were observed systematically near the surface, in the main bulk and near the bottom of N-type (100) silicon lift-off samples. It is seen that the pores are not cylindrical but exhibit more or less approximately square cross sections. X-ray diffraction spectra and electron diffraction patterns ...

International Nuclear Information System (INIS)

The structure of ammonium azide (NH_4)N_3 was (re-)determined ab initio from x-ray powder diffraction experiment using synchrotron radiation. We tried to detail and comment the different steps involved in the structure determination. The compound crystallize in the orthorhombic Pmna space group (no.53) with a = 8.937(1) A, b= 3.8070(5) A, c = 8.664(1) A, V = 294.79(7) A"3; Z= 4. It was possible to locate and refine the hydrogen coordinates, in two different approaches, and to establish the H-bonds. The final structural parameters are in good agreement with previous results based on three-dimensional neutron diffraction. (Author)

International Nuclear Information System (INIS)

Microstructure and electrical properties of iron oxide Fe_2O_3 thin films prepared by spray pyrolysis method have been experimentally characterized. The effect of substrate temperature as well as deposition time on the structural features (crystallite size and microstrain) and electric resistivity of these films has been investigated. X-ray diffraction (XRD) and scanning electron microscope (SEM) characterized the structure study. The results of X-ray diffraction showed that with increasing substrate temperature bias the film structure changed from amorphous to crystalline at the same deposition time. At a substrate temperature of 350 deg. C and low deposition time, #alpha#-Fe_2O_3 appears almost in amorphous form. With rising the substrate temperature and deposition time, the crystallinity was improved. At T_s_u_b>350 deg. C, a well-crystallized rhombohedral phase of ...

Energy Technology Data Exchange (ETDEWEB)

The Synchrotron Resource of the Howard Hughes Medical Institute will be dedicated to structural analyses of biological macromolecules, primarily through crystallography. This facility is under construction at the X4 port of the National Synchrotron Light Source at Brookhaven National Laboratory, and it will comprise three beamlines. The first line to be built has been devised to apply the multiwavelength anomalous diffraction method which provides direct estimates for the phases of reflections. The second line will be devoted to rapid and essentially routine diffraction measurements, mainly through the rotation method. These two experimental stations are contained within refrigerated radiation enclosures that will maintain clean environments, narrowly defined constant temperatures, and protection against biohazard at biosafety level BL-2. At the same time as the second line will be developed, the swath center is planned to first serve as a ...

Energy Technology Data Exchange (ETDEWEB)

This thesis is concerned with the optimization and development of the production of nanofocusing refractive X-ray lenses. These optics made of either silicon or diamond are well-suited for high resolution X-ray microscopy. The goal of this work is the design of a reproducible manufacturing process which allows the production of silicon lenses with high precision, high quality and high piece number. Furthermore a process for the production of diamond lenses is to be developed and established. In this work, the theoretical basics of X-rays and their interaction with matter are described. Especially, aspects of synchrotron radiation are emphasized. Important in X-ray microscopy are the different optics. The details, advantages and disadvantages, in particular those of refractive lenses are given. To achieve small X-ray beams well beyond the 100 nm range a small focal length is ...

International Nuclear Information System (INIS)

The following are reported: colorimetric determination of Ti in Cr, decontamination of metals by anodic dissolution, computer code for x-ray peak identification, gel-permeation chromatography of CoRezyn 1664 polyester resin, infrared monitoring of gases and vapors, particle size analysis of dusts, nondestructive analysis of Oralloy for removable alpha contamination, dissolution (digestion) of high-fired oxides, assay of U in a Pu-U alloy, measurement of oxide thickness on Pu metal by x-ray diffraction, analysis of precipitated Pu peroxide, differentiation of Dowex SBR and 11 resins, and determination of Pu solubility in simulated lung fluid.

Science.gov (United States)

An x-ray diffraction approach has been developed for determination of the kinetics of growth of Pd/sub 2/Si layers. Epitaxial Pd/sub 2/Si films were grown on Si(111) substrates over a temperature range of 160-222/sup 0/C by a solid-state reaction between the substrates and the Pd overlayers. The parabolic rate equation was verified and rate constants showed Arrhenius behavior with an activation energy E/sub a/ = 1.06 eV and prefactor k/sub 0/ = 7 x 10/sup -4/ cm/sup 2//s. The low value of E/sub a/ suggests a short-circuit diffusion mechanism. It is reasonable to expect that impurities and microstructure may play important roles in the growth process. Impurity levels in the specimens were evaluated by analytic techniques suited to thin-film study: Rutherford backscattering spectrometry, secondary ion mass spectrometry, and Auger electron spectrometry. No impurities were present at concentrations approaching 1 at. %. Some O, ...

CERN Document Server

We briefly review capabilities and requirements for future instrumentation in UV- and X-ray astronomy that can contribute to advancing our understanding of the diffuse, highly ionised intergalactic medium.

International Nuclear Information System (INIS)

The purpose of this research is to investigate the micro-mechanism of deformation behavior of metallic glasses. We report the results of direct observations of short-range and medium-range structural change during tensile deformation of metallic glasses by high energy X-ray diffraction method. Cu50Zr50 and Ni30Zr70 metallic glass samples in the ribbon shape (1.5 mm width and 25 ?m) were made by using rapid quenching method. Tensile deformation added to the sample was made by using special equipment adopted for measuring the high energy X-ray diffraction. The peaks in pair distribution function g(r) for Cu50Zr50 and N30iZr70 metallic glasses move zigzag into front and into rear during tensile deformation. These results of direct observation on atomic distribution change for Cu50Zr50 and Ni30Zr70 metallic glass ribbons during tensile deformation suggest that the micro-relaxations occur.

Energy Technology Data Exchange (ETDEWEB)

The physical properties of polymer blends consisting of one or more crystallizable components are affected by the microstructure of these materials. In particular, the degree of crystallinity can be influenced by processing parameters, and the crystallinity, as well as the phase distribution, may vary as a function of depth through an injection molded part Conventional x-ray diffraction techniques can provide information regarding both phase composition and degree of crystallinity, but, because of the relative transparency of these materials to wavelengths generally available in the laboratory, these techniques provide information representative of only the bulk. By employing parallel beam optics at varying grazing incidence angles, the x-ray sampling depth can be varied without loss of resolution. This technique can be used to vary the effective analysis depth from the top several hundred angstroms for low razing incidence ...

International Nuclear Information System (INIS)

The results of studies of the time-resolved luminescence of self-trapped excitons (STE) with different multiplicity as well as the X-ray emission in oriented BeO crystals under excitation in the vicinity of the 1 s Be photoabsorption edge are presented. The branching of the electronic excitations relaxation depends strongly on the crystal orientation after the inner-shell excitation. The common features between the processes of the STE luminescence and resonantly excited X-ray fluorescence have been discussed.

Energy Technology Data Exchange (ETDEWEB)

High-spatial-resolution microfocus-based X-ray imaging technology, both real-time and film, has been used to study the thickness variation that occurs in the oxide core of silver-sheathed BSCCO ribbons produced by the powder-in-tube method. This thickness variation (also called ``sausaging``) occurs during incremental rolling and degrades the critical current densities of the ribbons. Using X-ray image data the authors determined the onset and severity of sausaging. Onset occurred at a ribbon thickness of 203 {micro}m, and the severity increased with subsequent rolling reductions. Scanning electron microscopy was used to confirm the X-ray image data. X-ray imaging provides several advantages over more traditional methods for characterizing the superconductors such as optical or scanning electron microscopy. The X-ray imaging provides nondestructive information ...

Energy Technology Data Exchange (ETDEWEB)

High-energy synchrotron x-ray diffraction (XRD) has been used to quantify load transfer in bovine plexiform bone. By using both wide-angle and small-angle XRD, strains in the mineral as well as the collagen phase of bone were measured as a function of applied compressive stress. We suggest that a greater proportion of the load is borne by the more mineralized woven bone than the lamellar bone as the applied stress increases. With a further increase in stress, load is shed back to the lamellar regions until macroscopic failure occurs. The reported data fit well with reported mechanisms of microdamage accumulation in bovine plexiform bone.

British Library Electronic Table of Contents (United Kingdom)

The study aimed to determine the chemical effects on the K and L X-ray intensity ratios and the K and L X-ray production cross sections for gold compounds. The K shell fluorescence yields and L shell average yields were also investigated. The samples were excited by 59.5keV ?-rays from an 241Am annular radioactive source and 123.6keV ?-rays from a 57Co annular radioactive source. K and L X-rays emitted from samples were counted by an Ultra-LEGe detector with a resolution of 0.150keV at 5.9keV. The experimental values were compared with theoretical, the semi-empirical and other experimental values.

International Nuclear Information System (INIS)

Energy-filtered X-ray photoemission electron microscopy (EXPEEM) is a microscopy technique which has the potential to provide surface chemical mapping during surface chemical processes on the nanometer scale. We studied the possibilities of EXPEEM using a Wien filter type energy analyzer in the high energy X-ray region above 1000 eV. We have successfully observed the EXPEEM images of Au islands on a Ta sheet using Au 3d_5_/_2 and Ta 3d_5_/_2 photoelectron peaks which were excited by 2380 eV X-rays emitted from an undulator (BL2A) at Photon Factory. Our recent efforts to improve the sensitivity of the Wien filter energy analyzer will also be discussed.

International Nuclear Information System (INIS)

The transport properties of a 'thin' polycrystalline diamond film are analyzed after the sample exposure to 8.06-keV x-ray radiation. Structure and morphology of the as-grown film have been evaluated by Raman, x-ray diffraction, and scanning electron microscopy techniques. The transport properties have been investigated by measuring dark current-voltage characteristics in the temperature range of 60 to 360 K. Ohmic transport has been evidenced on the as-grown film up to 1.16x10"5 V/cm. After irradiation, nonlinear contributions to the dark current have been evidenced and related to field-assisted thermal ionization of traps. Below 200 K, hopping mechanisms have been observed. Correlations have been found among x-ray irradiation, density of traps involved in the transport processes, and the nonhomogeneous nature of the sample. A simple model of the grain boundary structure is proposed to explain the ...

International Nuclear Information System (INIS)

In this study, WO3 thin films were grown on glass substrates using an aqueous solution containing tungstate (NH4)2WO4 as precursor. The substrate temperature incremented from 250 to 500 deg. C, by steps of 50 deg. C. The structural properties were investigated using XRD, atomic force microscopy and scanning electronic microscopy techniques. Microprobe analyses showed that a balanced stoichiometric composition was obtained for thin films prepared at Ts = 350 and 400 deg. C. The X-ray diffraction analyses showed different structure crystallography in function of the substrate temperature. Moreover, films deposited at 400 deg. C were annealed in air for 2 h at 450 and 500 deg. C, respectively and the structural changes due to heat treatment were studied. Finally, the optical properties of these films were carried out using optical measurements of transmittance T(?) and reflectance R(?) spectra in 300-1800 ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical method has been used to deposit zinc oxide (ZnO) thin films from aqueous zinc nitrate solution at 80 deg. C onto fluorine doped tin oxide (FTO) coated glass substrates. ZnO thin films were grown between - 0.900 and - 1.025 V vs Ag/AgCl as established by voltammogram. Characterisation of ZnO films was carried out for both as-deposited and annealed films in order to study the effect of annealing. Structural analysis of the ZnO films was performed using X-ray diffraction, which showed polycrystalline films of hexagonal phase with (002) preferential orientation. Atomic force microscopy was used to study the surface morphology. Optical studies identified the bandgap to be {approx} 3.20 eV and refractive index to 2.35. The photoelectrochemical cell signal indicated that the films had n-type electrical conductivity and current-voltage measurements showed the ...

Science.gov (United States)

Multiple treatment of engineering surfaces can provide improved surface properties that cannot be obtained by a single surface treatment. Consequently, this study investigates the effects of laser melting on the microstructures of plasma nitrided Ti-6Al-4V alloy. The study consists of two parts. In the first part, governing equations pertinent to the laser melting process are developed, and temperature variation across the melted zone is predicted. In the second, an experiment is conducted to nitride the surface of the alloy through plasma nitriding process and to melt the plasma nitrided and the untreated alloy surfaces with a CO2 laser beam. The resulting metallurgical changes are examined using x-ray diffraction (XRD), bdenergy-dispersive spectrometry (EDS), and scanning electron microscopy (SEM) techniques. It is shown that three distinct nitride layers are formed in the vicinity of the alloy ...

Energy Technology Data Exchange (ETDEWEB)

In this work, {beta}-SnS{sub 2} thin films have been prepared on glass substrates by the spray pyrolysis technique using an alcohol solution which contains tin chloride (SnCl{sub 4}) and thiourea (SC(NH{sub 2}){sub 2}) as precursors. The structural study shows that {beta}-SnS{sub 2} thin film prepared using optimal experimental conditions: substrate temperature T{sub s} = 280 deg. C and the concentration ratio of sulfur and tin elements in the spray solution x = [S]/[Sn] = 2.5, crystallizes in the hexagonal phase with a strong (0 0 1) X-ray diffraction line. In the same way, microprobe analyses (EPMA) as well as X-ray photoelectron spectroscopy (XPS) show the presence of undiserable phase of SnO{sub 2}. From the transmission and reflectance spectra, the band gap energy is 2.65 eV. On the other hand, the photothermal properties of such films have been studied, the thermal ...

Energy Technology Data Exchange (ETDEWEB)

This work presents a comparative study of low-alloy steel nitriding for different possible techniques. Active screen plasma nitriding (ASPN) is a successful surface modification method that has many advantages over the conventional DC plasma nitriding (CPN). The corrosion behavior of 30CrNiMo8 low-alloy steel has been examined using anodic polarization tests in 3.5% NaCl solution under varying conditions of ASPN and CPN processes. The process variables included active screen setup parameters, treatment temperature (550 and 580 deg. C), gas mixture (25/75 and 75/25 of N{sub 2}/H{sub 2}) and treatment time (5 and 10 h) in 500 Pa pressure. The structure and phases composition of the compound layer was studied by X-ray diffraction (XRD), microhardness tests, optical microscopy and scanning electron microscopy (SEM). It was observed that ASPN treated samples surface enhanced corrosion resistance while the ...

International Nuclear Information System (INIS)

An alloy of composition Ti-4.4 wt.% Ta-1.9 wt.% Nb is being developed as a structural material for corrosion applications, as titanium and its alloys possess excellent corrosion resistance in many oxidizing media. The primary physical metallurgy database for the Ti-4.4 wt.% Ta-1.9 wt.% Nb alloy is being presented for the first time. Determination of the #beta# transus, M_s temperature and classification of the alloy have been carried out, employing a variety of microscopy techniques, X-ray diffraction (XRD), micro-hardness and differential scanning calorimetry (DSC). The #beta# transition temperature or #beta# transus determined using different experimental techniques was found to agree very well with evaluations based on empirical calculations. Based on chemistry and observed room temperature microstructure, the alloy has been classified as an #alpha# + #beta# titanium alloy. The high temperature #beta# transforms to either #alpha#' or #alpha# ...

International Nuclear Information System (INIS)

New rare earth metal rich cadmium compounds RE_4CoCd and RE_4RhCd (RE = Tb, Dy, Ho) were prepared by high-frequency melting of the elements in sealed tantalum tubes. The samples were studied by x-ray powder and single-crystal diffraction. All the compounds crystallize with Gd_4RhIn-type structure, with space group F4-bar3m. The structures are built up from rigid three-dimensional networks of condensed, cobalt (rhodium) centred trigonal RE_6 prisms. The voids left by these networks are filled by Cd_4 cluster units and the coordination number 14 polyhedra of the RE1 atoms. The terbium and dysprosium compounds in both series undergo antiferromagnetic ordering, whereas the holmium compounds exhibit ferromagnetic ordering. The magnetic ordering in these compounds is characterized by broad peaks around the transition temperatures. The results of detailed crystallographic investigations and preliminary magnetic and specific heat ...

Energy Technology Data Exchange (ETDEWEB)

In this study, SnO{sub 2} thin films have been grown using spray pyrolysis technique on glass substrates under a substrate temperature (T{sub s} = 440 {sup o}C). The precursors were methanol CH{sub 4}O and anhydrous tin tetrachloride. XRD analyses yielded strong (1 1 0)-(1 0 1)-(2 0 0) X-ray diffraction peaks which are characteristics to tetragonal crystals. Atomic Force Microscopy (AFM) analyses showed the existence of clusters with particular pyramidal shapes. The main part of this study concerns the optical measurements of transmittance T({lambda}) and reflectance R({lambda}) spectra inside 250-1800 nm domain. Conjoint optical and thermal properties were deduced using the Amlouk-Boubaker Opto-Thermal Expansivity {psi}{sub AB}. The obtained value: {psi}{sub AB} {approx} 23.4 m{sup 3} s{sup -1} helped situating the performance of the as-grown SnO{sub 2} compound among most known PV-T oxides like ZnO ...

Energy Technology Data Exchange (ETDEWEB)

Petrographic research for the Nevada Nuclear Waste Storage Investigations focused on xenolithic variability in the Topopah Spring Member and on variations of clinoptilolite composition at Yucca Mountain. Zeolite and smectite occurrences were considered in terms of their relation to a disturbed zone beneath the potential repository, and mineral stability experiments have produced a new clinoptilolite structure as a result of prolonged heating at low temperature. Limitations were defined on the abundance of erionite and of sulfur. X-ray diffraction studies lead to improved analytical methods. Progress was made in the comparative study of mineralogy in sand ramps and in faults. Geological modeling considered the differences of the diffusion of nonsorbing tracers in vertically and in horizontally fractured rock. Modeling also treated the diffusion of a nonsorbing tracer in devitrified and in zeolitized ...

British Library Electronic Table of Contents (United Kingdom)

A series of new non-discoid chiral copper(ii)-salen type complexes, [Cu((4-CnH2n+1O)2salen)], n = 14, 16, 18 and salen = N,N'-cyclohexane bis (salicylideneiminato), containing 4-substituted alkoxy tails in the side aromatic rings and a cyclohexane spacer, have been prepared and their mesogenic properties investigated. The compounds were characterised by Fourier transform infra-red spectroscopy, 1H and 13C nuclear magnetic resonance spectroscopy, UV-vis spectroscopy and fast atom bombardment mass spectrometry. Mesomorphic properties of these compounds were studied by polarising optical microscopy, differential scanning calorimetry and X-ray diffraction (XRD). The ligands are non-mesogenic but the complexes exhibited enantiotropic rectangular columnar mesophases (Colr) with extended temperat...

International Nuclear Information System (INIS)

The formation of the melilite solid solution phase (M'), Sm_2Si_3_-_xAl_xO_3_+_xN_4_-_x, in an #alpha#-sialon sample of overall composition Sm_0_._6Si_9_._2_8Al_2_._6_9O_1_._3_6N_1_4_._7_6, was studied as a function of time in the temperature interval 1,375--1,525 C. The #alpha#-sialon ceramic contained only minor amounts of the 21R sialon polytype and some residual grain-boundary glass before heat treatment. In situ studies by high-temperature X-ray diffraction were combined with postsintering heat treatment followed by quenching. The M'-phase was found to be formed by two different mechanisms: either crystallization of the residual grain-boundary liquid or a direct decomposition of the #alpha#-sialon phase. The liquid crystallized during the first 10--15 min of heat treatment, yielding a rapid M'-phase formation, and further formation of M'-phase continued at a much slower rate, related to the ...

Energy Technology Data Exchange (ETDEWEB)

A great amount of naturally produced manganese dioxide has been widely used as cell active material since 1880's, but nowadays synthetic manganese dioxides such as electrolytic manganese dioxides (EMD) and chemically prepared manganese dioxides (CMD), etc. are used therefor and cell performances have considerably been improved. The synthetic manganese dioxides which are being used widely as the above cell active materials are active materials designed and reformed as manganese-oxygen-proton based active materials. In this study, electrochemical behaviors of synthetic manganese dioxides (layered manganese dioxides and spinel-related manganese dioxides) were examined in a 1MLiClO4 propylene carbonate/tetrahydrofuran (1:1) solution. A discharge curve shown by the layered manganese dioxide presented a distorted S-shape and that of the spinel-related manganese dioxide showed the two steps. The way of changes of crystal phase was measured by the ...

International Nuclear Information System (INIS)

In this study, perovskite type oxide YAlO_3 has been doped with different amounts of the divalent cation Ca to synthesize Y_1_-_xCa_xAlO_3_-_#delta# (x = 0-0.21) compositions. The effect of dopant concentration on the crystal structure and electrical properties of YAlO_3 synthesized by citrate gel route has been investigated. The phase purity of the samples has been carried out using X-ray diffraction. The microstructural evaluation of the samples has been conducted by scanning electron microscopy and energy dispersive spectrum analysis. Thermal analysis has been conducted to monitor the decomposition of the intermediate products. The electrical conductivity studies have been performed using a.c. impedance spectroscopy as a function of temperature in the range 200-800 "oC in air. The Y_0_._9_4Ca_0_._0_6AlO_3_-_#delta# composition exhibits a total conductivity of 2.5 mS/cm at 800 "oC.

Energy Technology Data Exchange (ETDEWEB)

One aspect of the research program SFB 570 'Distortion engineering' is the in situ X-Ray diffraction analysis of phases and residual stresses during complete heat treatment cycles. These investigations result in experimental evidence available for the extensive computations. The optimisation of the instrumentation will be reported. A surface decarburisation of samples made from the ball bearing steel 100Cr6 could be avoided for a temperature range from 800 to 900 C and a holding time of one hour by a combination of evacuate the furnace and using a certain nitrogen flow as protective gas. At lower temperatures small amounts of ferrite caused by an increased diffusion rate of carbon lead again to a surface decarburisation up to a depth of 2 {mu}m. It was proved that with an evacuation of the X-Ray beam path at constant power of the X-Ray source the intensity of ...

International Nuclear Information System (INIS)

Particularly high coherence of the x-ray beam is associated, on the ID19 beamline at ESRF, with the small angular size of the source as seen from a point of the sample (0.1-1 #mu#rad). This feature makes the imaging of phase objects extremely simple, by using a 'propagation' technique. The physical principle involved is Fresnel diffraction. Phase imaging is being simultaneously developed as a technique and used as a tool to investigate light natural or artificial materials introducing phase variations across the transmitted x-ray beam. They include polymers, wood, crystals, alloys, composites or ceramics, exhibiting inclusions, holes, cracks, ... . 'Tomographic' three-dimensional reconstruction can be performed with a filtered back-projection algorithm either on the images processed as in attenuation tomography, or on the phase maps retrieved from the images with a reconstruction procedure similar to that used for electron ...

International Nuclear Information System (INIS)

The feasibility was studied of the application of radionuclide X-ray fluorescence analysis to the identification and determination of chemical elements in the air. A description of the method is presented, the main stages of the analysis are discussed (sample preparation and standards, selection of radioactive radiation sources, geometry of measurement and evaluation of results). The method is illustrated on the determination of elements Fe, Cu, Zn, Br, and Pb in air samples taken in the city of Prague. (author) 2 tabs., 2 figs., 14 refs.

Energy Technology Data Exchange (ETDEWEB)

3d occupation numbers of the transition elements corresponding to various types of atomic configurations are calculated by means of the linear muffin-tin orbital (LMTO) method. This data is used with the multiconfiguration Dirac-Fock (MCDF) X-ray intensity ratios to estimate the electron populations of the 3d metals in alloys.

International Nuclear Information System (INIS)

A survey is presented of studies dealing with radionuclide X-ray fluorescence analysis (RXFA) of impurities in the air, water, soil, sediments and biological materials, mainly blood, urine, hair, soft tissues and bones. Tabulated are lists of published works on RXFA of the air, water and biological materials. (ES).

International Nuclear Information System (INIS)

We present differential scanning calorimetry (DSC), X-ray diffractometry, in situ Moessbauer spectroscopy (MS), and transmission electron microscopy (TEM) studies in Metglas ribbons subjected to different heat treatments. The temperature evolution of the hyperfine field H_h_f(T) and the Curie temperature (T_c) of the amorphous phase are determined. The magnetic field originally present in the amorphous phase has a 'normal' behavior, in the sense that it can be described by the Weiss molecular field theory. The total angular momentum of the iron atoms turns out to be 5/2 and this implies Fe"3"+ in which the electronic spins are uncoupled. When the samples are maintained near T_c (#approx#673 K), three new magnetic phases are detected in the Moessbauer spectra, indicating an onset of a crystallization process well below the first crystallization temperature (T_X_1), as determined by DSC (#approx#820 K). The magnetic behavior of these phases is ...

International Nuclear Information System (INIS)

Several Mg-Y binary ribbons with Y content up to #approx#17.9 at.% were fabricated by melt-spinning. X-ray diffraction (XRD) revealed that the phase structure changes with increasing Y content from extended solid solution to partially amorphous, and then fully intermetallic Mg_2_4Y_5. Anodic potentiodynamic polarization performed in 0.01 M NaCl electrolyte (pH=12) revealed improved anodic passivity behavior compared to pure Mg for all the Mg-Y alloys. X-ray photoelectron spectroscopy (XPS) revealed that the improved passivity of Mg-Y was more related to the elemental oxidation state rather than the concentration of the surface components. To study the effect of Cl"- ion on the passivity behavior, anodic potentiodynamic and potentiostatic polarization were performed on Mg-17.9 at.% Y in alkaline (pH=12) NaCl electrolytes containing Cl"- ion in the concentration range from 0.00 to 0.50 M. The passive ...

International Nuclear Information System (INIS)

Plasma-deposited thin films prepared at room temperature, ranging from 46 to 250 A of PdAu on #approx#45-50 A Si-oxide and Si-oxynitride films grown on Si wafers were studied. Grazing incidence X-ray diffraction, X-ray reflectivity, and XPS depth profile techniques were used to characterize the thin films. A reactive interface involving Pd- and Au-silicides is formed, linking the thin film to the Si-oxide and Si-oxynitride films: a small fraction of Pd and Au atoms from PdAu migrate into the Si substrate, first penetrating the oxide layer, and the small fraction of Si atoms from the oxide layer migrate into the PdAu film and form a silicide interlayer consisting of a reactive interface made up of mixtures of Au- and Pd-silicides interspersed within the matrix of PdAu and substrate. The concentration profiles of these silicides have a maximum at the interface with decay on both sides. The density and the ...

International Nuclear Information System (INIS)

Tl(InS_2)_1_-_x(FeSe_2)_x single crystals (where x=0; 0.001; 0.005; 0.01 and 0.015) were grown by the Bridgman-Stockbarger method. Obtained single crystals were crystallized in monoclinic structure. The present paper deals with experimental results relative to X-ray dosimetric characteristics of the Tl(InS_2)_1_-_x(FeSe_2)_x solid solutions at 300 K. Installation URS-55a was the source of radiation. X-ray radiation dose (E) falling on the crystals is measured by the crystalline X-ray dosimeter DRGZ-02. The value of X-ray conductivity coefficient K_#sigma# characterising X-ray sensitivity is defined as K_#sigma#= (#sigma#_E-#sigma#_0)/E#sigma#_0. where #sigma#_E is conductivity under the effect of X-ray radiation by intensity E, #sigma#_0 is conductivity in the lack of radiation. Comparing X-ray dosimetric characteristics of TlInS_2 and ...

Energy Technology Data Exchange (ETDEWEB)

The structural variations of amorphous metals, such as Pd/sub 80/Si/sub 20/, with irradiation of helium ion, neutron, and gamma ray have been mainly pursued by the method of X-ray diffraction and thermal analysis. It should be noticed that the amorphous metals show a radiation resistance, that is, no remarkable structural changes under helium ion, neutron, and gamma ray irradiation.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction was used to monitor the {ital in} {ital situ} reaction of Pd deposited on Si(111) at room temperature. An ordered silicide forms spontaneously beneath a poorly ordered overlayer. It is commensurate and strained at low coverage, but relaxes to an unstrained state above a critical thickness of 18 A. During both phases of growth sustained intensity oscillations are seen that correspond to a layerwise consumption of the substrate at the buried interface.

Energy Technology Data Exchange (ETDEWEB)

The radial distribution function (RDF) derived from wide angle X-ray diffraction patterns gives additional information about the spatial distribution of atoms. Their radial distances and relative average coordination numbers can be calculated using appropriate mathematical procedures. 7 refs.

Energy Technology Data Exchange (ETDEWEB)

The wear behaviour of 722M24 (En40B) steel plasma nitrided at high temperatures for long durations was investigated. Under dry sliding and abrasive-containing lubricated conditions, the wear characteristics of the steel were studied as a function of load, time and white layer thickness. The white layer and the wear debris were characterized by X-ray diffraction. The topography of the wear surface was examined in a scanning electron microscope. The plasma nitriding process was carried out using a 20 kW plasma processing unit in cracked ammonia atmosphere. Treatment times of up to 100 h were employed with temperatures of 550, 570 and 590 C. Wear tests were performed with plasma nitrided AMS 6472 as the counterface material. The tests under abrasive-containing lubricated conditions were carried out with 10% carborundum powder 10 [mu]m in size in SAE-30 machine oil. The wear resistance of the steel was improved by plasma ...

Energy Technology Data Exchange (ETDEWEB)

Mixed-conducting Sr-Fe-Co oxides have potential applications in dense ceramic membranes for high-purity oxygen separation and/or methane conversion to produce syngas (CO + H{sub 2}), because of their combined high electronic/ionic conductivity and significant oxygen permeability. We studied the crystal structure and microstructure of the system in X-ray diffraction experiments and by using scanning electron microscopy, respectively. Thermogravimetric analysis was conducted on the SrFeCo{sub 0.5}O{sub x} sample in environments of various oxygen partial pressures (pO{sub 2}). Conductivity increased while weight decreased with increasing temperature. Activation energy decreased while conductivity increased with increasing pO{sub 2}. The pO{sub 2}-dependent conducting behavior of the SrFeCo{sub 0.5}O{sub x} system can be understood by considering the trivalent-to-divalent transition of transition-metal ions.

International Nuclear Information System (INIS)

Molybdenum oxide nanostructures were synthesized utilizing the solution combustion method where the ammonium molybdate powder and an organic additive were used as precursors. Different organic additives including ethylene diamine tetra-acetic acid (EDTA), polyethylene glycol 200 (PEG 200), sorbitol and urea were used as surfactants in order to investigate the effect of additive structure on morphology and particle size of products. Also various reaction parameters such as the additive/Mo molar ratio, concentration of metal ion in solution, pH of the reaction, and temperature of the synthesis media were changed to study effects on product morphology and size. Outcomes were characterized by Scanning Electron Microscopy (SEM), X-ray diffraction, and Transmission Electron Microscopy (TEM) techniques. Results show a variety of MoO_3 nanoparticles and nanorods produced within the size range of 10-80 nm. Furthermore, microrods and ...

International Nuclear Information System (INIS)

The Ti-6Al-4V alloy was treated by inductively coupled rf plasma nitriding. The effects of plasma-processing time in the range of 5-35 min on the microstructure and the mechanical properties of the plasma-nitrided Ti-6Al-4V samples were studied. The plasma power input was adjusted at 450 W and pure N_2 gas was introduced to establish a treatment pressure of 8.0-8.4 x 10"-"2 mbar. The characteristics of the nitrided layers have been investigated by microhardness testing, surface roughness measurements, optical microscopy, and x-ray diffraction. The results show that the surface microhardness increases as the plasma-processing time increases to reach 2000 HV0.1 at a plasma-processing time of 35 min. A high nitriding rate of 2.81 #mu#m"2 s"-"1 at a plasma-processing time of 25 min was achieved. The formation of the hard phases TiN, Ti_2N, and Ti(N) in the Ti-6Al-4V surfaces are found to be the reason for the increased ...

International Nuclear Information System (INIS)

Radio frequency (RF) plasma nitriding using different input plasma processing powers (250-600 W) improves the surface of titanium by forming hard phases of TiN, Ti_2N, and Ti (N) into the surface. The characteristics of the compound layer have been investigated by optical microscopy, microhardness measurements, and X-ray diffraction. The effect of plasma power on the sample temperature, electron temperature, and plasma density was studied using Langmuir double probe. The measured surface hardness value of the compound layer is 2190 HV 0.1 for treated sample at plasma power 500 W. The compound thickness continuously increases as the plasma power increases. The highest nitriding rate of 5.88 #mu#m"2/s was recorded when the input plasma power was adjusted at 550 W. This high nitriding rate of treated titanium samples is ascribed to the high concentration of active nitrogen species in the plasma atmosphere and the formed ...

British Library Electronic Table of Contents (United Kingdom)

Potassium dichlorido(l-prolinato)platinate(II), K[PtCl"2(l-pro"?"H)] (1), and chlorido(dimethyl sulfoxide)(l-prolinato)platinum(II), [PtCl(l-pro"?"H)(dmso)] (2), were synthesized by ligand substitution reactions. Both complexes were characterized by ^1H, ^1^3C, and ^1^9^5Pt NMR spectroscopy, elemental analysis, and HR-ESI-MS. The molecular structures of 1 and 2 were determined by single crystal X-ray diffraction, proving bidentate coordinated l-prolinato ligand and SP-4-4 configuration of 2a. With the help of DFT calculations stability of possible isomers of 1 and 2 was studied. A considerable difference in the in vitro cytotoxicity of 1 versus 2a (exchange of one chlorido ligand by dmso) against four human cancer cell lines was found.

Energy Technology Data Exchange (ETDEWEB)

Stearic acid gel is employed to study the phase evolution of MgTiO{sub 3} nanoparticles by thermal gravimetric analysis, X-ray diffraction, and Fourier transform infrared. During the preparation of stearic acid gel, tetrabutyl titanate easily absorbed moisture to hydrolyze into Ti(OH){sub 4} firstly, and then reacts with stearic acid and magnesium stearate to form magnesium-titanium oxide network polymer gel, meanwhile n-butanol is generated. When stearic acid gel is calcined in air, a series of oxidation and combustion reactions occur, meanwhile apparent heat is given off. The results show that a metastable intermediate phase Mg{sub 2}TiO{sub 4} is generated at 450 {sup o}C and nearly disappeared at 550 {sup o}C. Simultaneously, a new solid phase of MgTiO{sub 3} appears. The metastable intermediate phase Mg{sub 2}TiO{sub 4} is successfully identified in the current work.

International Nuclear Information System (INIS)

Zinc oxide thin films were obtained by laser ablation of a Zn target in oxygen reactive atmosphere, the oxygen being supplied either by a standard gas inlet valve or from a radio-frequency (rf) oxygen plasma. Pt-coated silicon and MgO were used as substrates. The influence of the deposition parameters as laser wavelength (266, 355, 1064 nm), laser fluence (1.5-20 J/cm2) and oxygen pressure (1-60 Pa) was studied. The influence of the rf plasma beam addition on the morphological proprieties of zinc oxide films was particularly investigated, simultaneously with several configurations of the direction of the ablation plasma, the rf plasma beam and the substrate. The obtained films, with thicknesses in the range of 50 nm to 1 ?m have been characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM).

Energy Technology Data Exchange (ETDEWEB)

This paper introduces a new method to produce nano-composite powder for the preparation of high performance ZnO varistors. ZnO particles were coated with Bi{sub 2}O{sub 3}, Sb{sub 2}O{sub 3}, Co{sub 2}O{sub 3}, Cr{sub 2}O{sub 3} and other additives via liquid nano-coating technique. Then the prepared powder was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermal gravity and differential scanning calorimetry (TG-DSC) and particle size distribution. The results showed that the ZnO composite powder is homogeneously coated and ultrafine. The densification, phase composition and microstructure of ZnO varistors was studied by linear shrinkage, X-ray diffraction (XRD) and SEM, respectively. The preliminary electrical parameters of ZnO varistors showed that the breakdown voltage V {sub b} (1 mA/cm{sup 2}) and nonlinear coefficient {alpha} is 5400 V/cm and 50, respectively, much ...

International Nuclear Information System (INIS)

Li_1_._3Al_0_._3Ti_1_._7(PO_4)_3 thin films were successfully prepared by the solution deposition using lithium acetate, aluminum nitrate, ammonium dihydrogen phosphate and titanium butoxide as starting materials. The structure, surface morphology, electrochemical window, and ionic conductivity of the films were studied by X-ray diffraction, scanning electron microscopy, cyclic voltammetry and AC impedance. The results showed that Li_1_._3Al_0_._3Ti_1_._7(PO_4)_3 thin films annealed between 750 deg. C and 900 deg. C prepared by this method were well crystallized, homogenous and crack-free. The electrochemical window was beyond 2.4 V and the ionic conductivity was approximately 1.57x10"-"5 S/cm at room temperature for the film annealed at 800 deg. C for 30 min.

International Nuclear Information System (INIS)

The effects of neutron irradiation on the superconducting and normal state properties of alloys and compounds are presented. Particular emphasis is placed on the A-15 compounds where the effects of neutron irradiation on Tsub(c), Hsub(c_2), long range order parameter and lattice parameter are described. Large depressions (up to 80%) in Tsub(c) are observed for all the A-15 compounds studied with the exception of Mo_3Os where much smaller decreases in Tsub(c) are seen. Along with the decrease in Tsub(c) and increase in lattice parameter, the degree of long range order, as measured by X-ray and neutron diffraction, decreases. Also presented are the results of isothermal and isochronal anneals up to 900"0C. The unirradiated value of Tsub(c) can be restored by annealing, and for those systems where measurements have been made, recovery of the lattice parameter and order parameter also takes place. The effects observed in ...

Energy Technology Data Exchange (ETDEWEB)

In order to enhance the performance of CMOS transistors, embedded epitaxial layers of Si:C can be used. In the present work, Si:C layers with Carbon contents up to 1.9 at-% and in-situ Phosphorus doping up to 4 x 10{sup 20}At/cm{sup 3} have been investigated. Due to the low solubility of Carbon in Silicon (0.0004 at.-% at the melting point), all layers considered in this work are metastable and tend to relax. Since it is crucial to the application to retain the strain of those layers, the responsible mechanisms must be understood. The relaxation during thermal treatment was studied by high resolution X-ray diffraction and was found to behave differently, depending on Carbon content and Phosphorus doping concentration. In this work, we propose a relaxation mechanism based on a kick-out reaction of substitutional Carbon which is accelerated by Phosphorus content through transient enhanced diffusion. We simulate the time ...

Energy Technology Data Exchange (ETDEWEB)

Quasi-carbon fibers (QCFs) were prepared from Polyacrylonitrile (PAN) precursor by pyrolysis in the temperature range from 400{degrees}C to 950{degrees}C. The QCF-reinforced composites were fabricated by impregnating the QCFs with the PAN resin. The microstructural changes of both QCFs and their composites were characterized by the X-ray diffraction method. The stacking size and the crystallinity of the QCFs increased with the increasing heat treatment temperature (HTT). The crystallinity of the PAN matrix in a composite was also affected by various QCFs. DSC data indicated that thermal reaction mechanism of the composite could be altered due to the interaction between the fiber and the matrix. DMTA studies showed that good adhesion existed at the interface of the QCF-reinforced composites containing lower HTT fibers. The modulus magnitudes of QCFs and their composites increased with the QCF pyrolysis temperature. Although ...

Science.gov (United States)

A number of agricultural and engineering uses for fixated flue gas desulfurization (FGD) material exist; however, the potential for leaching of hazardous elements has limited widespread application and the processes controlling the leaching of this material are poorly understood. In this study, a flow-through rotating-disk system was applied to elucidate the relative importance of bulk diffusion, pore diffusion, and surface chemical reaction in controlling the leaching of fixated FGD material under pH conditions ranging from 2.2 to 6.8. Changing the hydrodynamics in the rotating disk system did not affect the leaching kinetics at both pH 2.2 and 6.8, indicating that bulk diffusion was not the kinetic-limiting step. Application of the shrinking core model (SCM) to the data suggested a surface reaction-controlled mechanism, rather than a pore diffusion mechanism. The leaching of fixated FGD material increased with decreasing pH, suggesting it can be described by a ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline ZnO films were fabricated via a simple method involving the oxidation of Zn films at a remarkably low temperature of 380 C. X-ray diffraction study confirmed that the Zn films were completely oxidized even at the low temperature of 380 C and the ZnO films fabricated were of polycrystalline wurtzite structure. Room temperature optical pumping using a frequency-quintupled Q-switched Nd:YAG laser ({lambda}=213 nm) exhibited that sharp peaks at around 3.12 eV emerged above excitation powers of {proportional_to}7 MW/cm{sup 2}, demonstrating lasing in the ZnO films. These results represent that the process is a simple, promising approach for fabricating ZnO of sufficient optical performance for use as ultraviolet (UV) light emitters and an alternative UV laser source; both are key components in short-wavelength photonic devices. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The effects of the plasma nitriding with the formation of compound nitride and diffusion zones and of the boronising with the different ion doses on hydrogen distribution and hydrogen induced deterioration of a surface layer were examined in the case of Armco iron. Electrochemical studies of hydrogen permeation rate, hydrogen vacuum extraction measurements, optical and scanning microscopy, X-ray diffraction and elastic recoil detection analysis (ERDA) were used. Accumulation of entering hydrogen within the various constituent zones of the modified layer inhibits the hydrogen transport into the metal and thus, decreases the mean hydrogen content in the deeper zones and in the core. Hydrogen accumulation within the compact nitride zone causes the expansion of the nitride lattice, nitride phase transformation and deterioration. The ion boronising enhances the hydrogen effects in the plasma nitrided layers. Therefore, ...

Energy Technology Data Exchange (ETDEWEB)

The present article describes a novel synthesis route for nano-sized goethite ({alpha}-FeOOH) using hydrazine sulphate as an additive. The X-ray diffraction (XRD) peaks of synthesized powder matched well with those of {alpha}-FeOOH. Transmission electron microscopy (TEM) showed the particles of irregular shape in the range of 1-10 nm. Batch adsorption experiments for fluoride uptake were performed to study the influence of various experimental parameters such as contact time (10 min to 7 h), initial fluoride concentration (10-150 mg L{sup -1}), pH (2-11.6) and the presence of competing anions. The time data fitted well to pseudo-second-order kinetic model. The fluoride removal passed through broad maxima in pH ranges of 6-8. High adsorption capacity of 59 mg g{sup -1} goethite was obtained. The isothermic data fitted well to Freundlich model. The presence of other ions namely chloride and sulphate adversely affected ...

Energy Technology Data Exchange (ETDEWEB)

The sequence of nitride formation during the early stages of plasma nitriding of pure iron was studied by optical microscopy, SEM, TEM and x-ray diffraction. Plasma nitriding at {approximately}490 C in a 25 vol.%H{sub 2} + 75 vol.%N{sub 2} mixture starts with the formation of {gamma}{prime}-Fe{sub 4}N after 40s. Once {gamma}{prime} nucleates, it mainly spreads laterally due to diffusion shortcuts in the discontinuous surface nitride layer. Before {gamma}{prime} is continuous on the surface, {epsilon} nucleates on top of it shortly after 40S. Epsilon is then observed to grow, both inwardly and laterally along with {gamma}{prime}. A compact {gamma}{prime}/{epsilon} bilayer forms on the surface at around 100s. The kinetics of nucleation, growth and compactation of the nitrides observed in the present work was significantly more rapid than in any of the nitriding process reported in the literature, including plasma nitriding. ...

Energy Technology Data Exchange (ETDEWEB)

Four types of cellulose, in particular carboxy methyl cellulose (CMC), are tested as potential binding materials in graphitic anodes for lithium ion batteries. It is shown that a minimum content of a cellulose which gives acceptable anode properties (reversible capacity > 300 mA hg{sup -1} during the first 10 cycles, irreversible loss < 20%) is about 2 wt.%, which is less than in the case of conventional polymeric binders (5-10 wt.%). Kinetics of insertion-deinsertion and passivation processes seem not to be affected by the presence of cellulose. Explanation for the electrode failure at cellulose contents lower than 1 wt.% is given based on X-ray diffraction and microscopy investigations. Finally, the structure (distribution) of cellulose in the composite anode material is discussed and (indirectly) checked with a series of experiments. Most results are compared with the corresponding results obtained either with gelatin or ...

Energy Technology Data Exchange (ETDEWEB)

A new preparation method for LiNiVO{sub 4} has been developed. LiNiVO{sub 4} can be readily obtained from the solid state reaction of LiNiO{sub 2} and V{sub 2}O{sub 3} or V{sub 2}O{sub 5} at 700 C for 2 h in air. The quarternary Li-Ni-V-O reaction is strongly dependent on vanadium starting materials, reaction environment atmosphere, reactant stoichiometry and synthesis temperature. Individual particles of LiNiVO{sub 4} powders are well-formed crystallites shown clearly by scanning electron microscopy results to be in the shape of an octahedron. Powder X-ray diffraction studies of this crystalline material indicate that LiNiVO{sub 4} has an inverse spinel structure different from that of known cathode materials such as LT-LiCoO{sub 2} and LiMn{sub 2}O{sub 4}. The Li/LiNiVO{sub 4} cell can be charged and discharged at about 4.8 V versus metallic Li. To our knowledge, this is the Li intercalation reaction with the highest ...

Energy Technology Data Exchange (ETDEWEB)

In the framework of the search for a ceramic material usable in the radioactive waste storage, uranium and thorium phosphates have been investigated. Their experimental synthesis conditions have been entirely reviewed, they lead to the preparation of four new compounds: U(UO{sub 2})(PO{sub 4}){sub 2}, U{sub 2}O(PO{sub 4}){sub 2}, UCIPO{sub 4}, 4H{sub 2}O, and Th{sub 4}(PO{sub 4}){sub 4}P{sub 2}O{sub 7}. Experimental evidenced are advanced for non existent compounds such as: U{sub 3}(PO{sub 4}){sub 4}, U{sub 2}O{sub 3}P{sub 2}O{sub 7} and Th{sub 3} (PO{sub 4}){sub 4}. Characterization by several techniques (X-rays and neutron powder diffractions, UV-Visible and Infra-red spectroscopies, XPS,...) were performed. The ab initio structure determination of U(UO{sub 2})(PO{sub 4}){sub 2} has been achieved by X-rays and refined by neutron diffractions. Through its physico-chemical analysis, we found that this ...

CERN Document Server

We review X-ray plasma diagnostics based on the line ratios of He-like ions. Triplet/singlet line intensities can be used to determine electronic temperature and density, and were first developed for the study of the solar corona. Since the launches of the X-ray satellites Chandra and XMM-Newton, these diagnostics have been extended and used (from CV to Si XIII) for a wide variety of astrophysical plasmas such as stellar coronae, supernova remnants, solar system objects, active galactic nuclei, and X-ray binaries. Moreover, the intensities of He-like ions can be used to determine the ionization process(es) at work, as well as the distance between the X-ray plasma and the UV emission source for example in hot stars. In the near future thanks to the next generation of X-ray satellites (e.g., Astro-H and IXO), higher-Z He-like lines (e.g., iron) will be resolved, ...

CERN Document Server

We examine the accretion properties in a sample of 42 hard (3-60keV) X-ray selected nearby broad-line AGNs. The energy range in the sample is harder than that usually used in the similar previous studies. These AGNs are mainly complied from the RXTE All Sky Survey (XSS), and complemented by the released INTEGRAL AGN catalog. The black hole masses, bolometric luminosities of AGN, and Eddington ratios are derived from their optical spectra in terms of the broad H$\\beta$ emission line. The tight correlation between the hard X-ray (3-20keV) and bolometric/line luminosity is well identified in our sample. Also identified is a strong inverse Baldwin relationship of the H$\\beta$ emission line. In addition, all these hard X-ray AGNs are biased toward luminous objects with high Eddington ratio (mostly between 0.01 to 0.1) and low column density ($<10^{22} \\mathrm{cm^{-2}}$), which is most likely due to the ...

International Nuclear Information System (INIS)

Six uranyl coordination compounds, UO_2(OH)(PYCA) (1), UO_2(PYCA)_2(H_2O).2H_2O (2), UO_2(PIC)_2 (3), UO_2(H_2O)_2(NIC)_2 (4), UO_2(OH)(HINIC)(INIC) (5), and UO_2(PYTAC)_2(H_2O)_2 (6) were grown as single crystals via hydrothermal synthesis (PYCA - pyrazine-2-carboxylate, PIC - picolinate, NIC - nicotinate, INIC - iso-nicotinate, and PYTAC - 2-(pyridin-4-yl)thiazole-5-carboxylate) to study their optical properties. All six compounds have been identified via single crystal X-ray diffraction and fully characterized via powder X-ray diffraction, infrared spectroscopy, UV-Vis spectroscopy, and fluorescence spectroscopy. Three of the complexes, 1, 3, and 6, represent new structures, and their synthesis and structural characterization is detailed within. The structures of 2, 4, and 5 have previously been reported in the literature. Coordination polymer 1 crystallizes in the orthorhombic ...

International Nuclear Information System (INIS)

SiC-AlN and SiC-SiAlON refractory composites were obtained by means of nitridation of the mixtures of silicon carbide (SiC) powder with a broad granulometric distribution and powders of aluminium (Al) and aluminium-silicon (Al-Si) mixtures. The mixtures of the composition Al-25% Si, Al-50% Si and Al-75% Si were previously prepared by means of 'mechanical alloying' technique. Thermodynamic analysis was accomplished in order to evaluate the viability of SiC-SiAlON and SiC-AlN refractories production by the chosen processing method, and the results confirmed viability of such. Investigation of nitridation of Al and Al-Si powder compacts in order to obtain the AlN and #beta#-SiAlON matrix phases of the composite was accomplished by means of differential thermal analysis (DTA) and thermogravimetric analysis (TG). The results of the thermal analysis show that nitridation of the Al-25% Si, Al-50% Si and Al-75% Si resulting in p-SiAlON formation occur at temperatures of 910 deg C, 811 deg C ...

Science.gov (United States)

Self-amplifying spontaneous radiation free-electron lasers, such as the LCLS or the European X-FEL, rely on the incoherent, spontaneous radiation as the seed for the amplifying process. Though this method overcomes the need for an external seed source one drawback is the incoherence of the effective seed signal. The FEL process allows for a natural growth of the coherence because the radiation phase information is spread out within the bunch due to slippage and diffraction of the radiation field. However, at short wavelengths this spreading is not sufficient to achieve complete coherence. In this presentation we report on the results of numerical simulations of the LCLS X-ray FEL. From the obtained radiation field distribution the coherence properties are extracted to help to characterize the FEL as a light source.

International Nuclear Information System (INIS)

Metal-organic chemical vapor deposition (MOCVD) made layers of strontium-bismuth-tantalate (SBT) were characterized by spectroscopic ellipsometry (SE) using the Adachi model [S. Adachi, Phys. Rev. B 35 (1987) 7454-7463]. The evaluated optical parameters were correlated with the physical and chemical behavior examined by X-ray diffraction (XRD). As a result, it was possible to fit the measured spectra with the Adachi model in a wide range covering the region of the band gap. The Adachi model provides electronic layer parameters like the transition energy E 0 and broadening ?. Our investigations established a correlation between XRD-determined average grain size and the electronic layer parameters.

CERN Document Server

In order to reduce the activation temperature of the TiZrV alloy, thin films of various compositions were produced by three-cathode magnetron sputtering on stainless-steel substrates. For the characterisation of the activation behaviour the surface chemical composition has been monitored by Auger electron spectroscopy during specific in situ thermal cycles. The volume elemental composition of the film has been measured by energy dispersive X-ray spectroscopy and the morphology (crystal structure and size of the crystallites) has been investigated by X-ray diffraction. The criteria indicating the sample quality and its dependence on film structure and chemical composition are presented and discussed. (13 refs).

International Nuclear Information System (INIS)

This investigation of a brain cancer cluster in Missouri used two approaches to investigate associations with potential risk factors. In a case-control study in a rural town, we interviewed surrogates of cases and controls about potential risk factors. We found a statistically significant positive association of brain cancer with reported exposure to dental x-rays. Occupation was not associated with the cluster in the rural town. In a standardized proportional mortality study for the state of Missouri, we calculated the observed and expected proportion of brain cancers by occupation and industry in Missouri decedents. We found that motor vehicle manufacturers, beauty shop workers, managers and administrators, elementary school teachers, and hairdressers and cosmetologists had significantly elevated proportions of brain cancer. Brain tumors are inconsistently associated with occupation in the literature. Further ...

CERN Document Server

Energy Dispersive X-ray Analysis in the Electron Microscope

International Nuclear Information System (INIS)

We describe a camera to record coherent scattering patterns with a soft-x-ray free-electron laser (FEL). The camera consists of a laterally graded multilayer mirror, which reflects the diffraction pattern onto a CCD detector. The mirror acts as a bandpass filter for both the wavelength and the angle, which isolates the desired scattering pattern from nonsample scattering or incoherent emission from the sample. The mirror also solves the particular problem of the extreme intensity of the FEL pulses, which are focused to greater than 10"1"4 W/cm"2. The strong undiffracted pulse passes through a hole in the mirror and propagates onto a beam dump at a distance behind the instrument rather than interacting with a beam stop placed near the CCD. The camera concept is extendable for the full range of the fundamental wavelength of the free electron laser in Hamburg (FLASH) FEL (i.e., between 6 and 60 nm) and into the water window. We have fabricated and ...

International Nuclear Information System (INIS)

We have studied L x-rays from 64 MeV iodine projectile in collision with various gas targets, Z_2 #18, do not arise from selective M subshell vacancy population, has been conclusively established by the observations by Datz et al (1971) and by Saha et al (1996) that the measured intensity ratio of the Ll and L#alpha# lines, which arise because of transitions from different M subshells into the same L, subshell, does not show any periodic behaviour with Z, but stays rather constant. Differences in the measured L#beta#_1/L#alpha# intensity ratio of iodine with 7"+ and 24"+ charge states impinging on Kr target established the minor role of the electrons in the N shell of the projectile in the x-ray production mechanism. (author)

Energy Technology Data Exchange (ETDEWEB)

The energy dispersive beamline X6A at the National Synchrotron Light Source employs a curved crystal monochromator (polychromator) which focuses a range ([similar to]1 keV) of x-ray energies into a narrow (100--120 [mu]m) line image. Although this beamline was constructed primarily for time-dependent EXAFS experiments, we have begun to explore the use of this instrument for energy dispersive diffraction experiments with different types of sample including macromolecular crystals. The tunability ([ital E]=6.5 to 21 keV) and flexibility ([Delta][ital E]=100--1000 eV) of the instrument makes the beamline ideal as a test bed for the application of polychromatic single-crystal diffraction techniques to different chemical or biological materials.

Energy Technology Data Exchange (ETDEWEB)

Simulations of the x-ray free-electron laser (FEL) oscillator are presented that include transverse effects and realistic Bragg crystal properties with the two-dimensional code GINGER. In the present cases considered the radiation divergence is much narrower than the crystal acceptance, and the numerical algorithm can be simplified by ignoring the finite angular bandwidth of the crystal. In this regime GINGER shows that the saturated x-ray pulses have 109 photons and are nearly Fourier-limited with peak powers in excess of 1 MW. Wealso include preliminary results for a four-mirror cavity that can be tuned in wavelength over a few percent, with future plans to incorporate the full transverse response of the Bragg crystals into GINGER to more accurately model this tunable source.

UK PubMed Central (United Kingdom)

San Francisco Bay has been contaminated historically by mercury from mine tailings as well as contemporary industrial sources. Native Spartina foliosa and non-native S....Full Text Available

UK PubMed Central (United Kingdom)

To treat or prevent some of the 795,000 annual strokes in the U.S., self-expanding endo-vascular stents deployed under fluoroscopic image guidance are often used. Neuro-interventionalists need...Full Text Available

UK PubMed Central (United Kingdom)

The localization of gold in the synovial membrane of rheumatoid arthritis patients treated with sodium aurothiomalate was examined and quantitative analysis of epon-embedded sections was carried out...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The applicability of two nuclear analytical methods: radionuclide X-ray fluorescence analysis and radiometric titrations based on precipitate formations was studied in order to determine the heptacaine hydrochloride in solutions. The applied methods were evaluated based on the obtained sensitivity values.

Science.gov (United States)

Examples are used to demonstrate that a shift in the point of emphasis is necessary with regard to radiation hazard in medicinal X-ray diagnosis. The parameters employed in this study to calculate somatic dose (SD) and somatically significant dose (SSD) m...

Energy Technology Data Exchange (ETDEWEB)

Nano materials are usually difficult to prepare. This work presents a simple way of preparing LiMn{sub 2}O{sub 4} nano powders using the high-energy ball milling method. This method has the advantage of producing pure, single-phase and crystalline nano powders. The milling method is carefully controlled to avoid unwanted chemical reactions that may change the stoichiometry of the material. Nano powders of between 30 and 50 nm are obtained. Structural studies of the nano powders, as well as the more conventional micron-sized LiMn{sub 2}O{sub 4}, are made using X-ray diffraction and neutron diffraction methods. Electrochemical evaluation of the materials is undertaken with a three-probe cyclic voltammetry technique and galvanostatic charge-discharge measurements. Structural studies reveal that not only are the crystallites of the nano powders much reduced in size from the normal ...

International Nuclear Information System (INIS)

Small-angle X-ray scattering method recognised to be very useful in the studies of structural problems of materials in homogeneous in nanoscale. Studies by small-angle X-ray scattering on the Al-Ag alloys are presented. The size distributions of spherical Guinier-Person zones were calculated using Vonk's and Glatter's methods. Small-angle X-ray scattering studies were performed on Al-5.0 at.%Ag alloy containing Guinier-Preson zones in the #eta#-state. For this alloy one can assume that scattering particles are of spherical shape, have uniform electron density and scatter independently. Moreover, the size distributions were calculated for Al-1.6 at.%Ag alloy containing Guinier-Preston zones in #epsilon#-state (scattering particles with not uniform electron density). Both, Vonk's and Glatter's, methods gave similar size distributions. Profiles of size ...

International Nuclear Information System (INIS)

The usefulness and clinical applicability of computed radiography(FCR) in X-ray examination of the stomach were evaluated in comparison with film-screen (FS) radiography by both phantom experiments and clinical studies. Receiver operating characteristic (ROC) curve analysis consisting of 25 normal and 25 artificially created simulated lesions on an orginally created Styrofoam phantom showed no difference in lesion detectability between FCR and FS radiography. Both were also equal in evaluation of the internal structure and margin of the 25 lesions by visual ranking. ROC curve analysis of clinical cases was performed in 30 cases, 20 normal and 10 abnormal, while evaluation by visual ranking was performed on 18 lesions. There was no significant difference between FCR and FS radiography either with ROC curve analysis or visual ranking, although the variations were somewhat greater in the clinical cases than in the phantom ...

International Nuclear Information System (INIS)

The development of the microstructure on aging of an (#alpha# + #beta#) type titanium alloy containing 6Al-1.6Zr-3.3Mo-0.3Si (VT9) (in weight percent) has been studied. The #beta#-transus temperature of this alloy is approximately 1243 K. Solution treatment in the #beta#-phase field of the alloy followed by quenching in water at room temperature resulted in the formation of a single-phase martensite structure. The martensitic structure was confirmed to be orthorhombic (#alpha# double-prime) using X-ray diffraction. The water-quenched (WQ) specimens were subjected to aging treatments at temperatures of 823, 873, and 973 K for various lengths of time. Aging at 823 K for times between 24 and 100 hours did not bring about any noticeable change in the microstructure. Aging at 823 K for 200 and 300 hours resulted in the heterogeneous precipitation of s_2 silicide particles and thin films of #beta# sandwiched between the ...

Energy Technology Data Exchange (ETDEWEB)

In this work a comprehensive metallophysical study was carried out for two aluminosilicide slip coatings of the systems Al-Si and Al-Nb-Si and an electron-beam Co-Cr-Al-Y coating on alloy EP-539 (17...19% Cr, 4...6% Co, 2.5...4% W, 4.5...6.5% Mo, 2...3% Ti, 3...4% Al, 1.4...2% Nb, balance Ni) after high-temperature testing. The protective properties of the coatings were evaluated from the results of laboratory tests for heat resistance at 1000/sup 0/C in the combustion products of diesel fuel with added sulfur at 970, 1000, and 1060/sup 0/C for 100 h and after full-scale tests for 150, 250, 400, and 700 h. Metallographic, hardness, x-ray, and micro x-ray studies of the coating were carried out. Layer-by-layer phase composition and the lattice spacing of the main phases were determined. X-ray analysis was carried out in an a DRON-1 diffractometer in copper K/sub ...

International Nuclear Information System (INIS)

Radionuclide X-ray fluorescence analysis (XFA) was used in the determination of the contents of metal residues in dosing plates for coin minting. XFA was also used for the determination of the strontium/calcium ratio in bone samples of different animals with the aim to obtain information on the food composition of these animals. It was found that bones of different animals can be distinguished based on the Sr/Ca ratio. No significant differences in the Sr/Ca ratio were observed in human bones of individuals from different social groups. (author). 1 fig., 5 tabs., 4 refs.

International Nuclear Information System (INIS)

The results of the examination of 23 children with Ewing's sarcoma of the rib were analyzed: panoramic chest X-rays in 4 projections, spot radiographs of the robs, superexposed pictures, laterograms, urography, angiography, computerized tomography, and scanning of the skeleton. Causes of diagnostic errors made at the first consultation by a physician, were identified. Peculiarities of X-ray signs of tumors of this site in children were studied. Diagnostic difficulties in tumors complicated by pleurisy and in tumors of small sizes with extrapleural growth were shown. Inclusions in the extraoseous tumor component were noted in 8.7% of the cases.

International Nuclear Information System (INIS)

The total and differential atomic pair-correlation functions of an icosahedral (quasicrystalline) solid were determined for the first time, directly by the differential anomalous-x-ray-scattering technique using synchrotron radiation. The observed atomic distances involving uranium atoms in icosahedral Pd/sub 58.8/U/sub 20.6/Si/sub 20.6/ suggest the presence of a quasicrystalline sublattice with vertex decoration. The pair distribution functions in the icosahedral and amorphous phases are similar up to the second-nearest neighbors, or up to 6 A-circle.

International Nuclear Information System (INIS)

A theoretical analysis is presented for the method of determining the concentration distribution of admixtures in zone melting and in the study of diffusion in melts. Continuous mode X-ray fluorescence analysis is considered. The convolution integral interpreting the analog output of the ratemeter was solved applying the mathematical apparatus of Z transformation. The feasibility of the method is tested on an example of the determination of tin distribution in tungsten. With respect to the statistical error (#delta#<1.5%), the maximum integration constant (100 s) and a very slow sample feed (0.025 mm/s) were used. The calculated transfer function reflects the total transfer function of the ratemeter and the recorder used. (M.D.).

Energy Technology Data Exchange (ETDEWEB)

The proposed short wavelength coherent light source driven by the SLAC 3 km linac might be used to induce transitions between nuclear isomeric states. If an isotope were found with energetically adjacent isomeric states, one short-lived and one long-lived, and it were possible to separate and concentrate the long-lived species, and other nuclear and solid-state parameters were favorable, it might be possible to convert sufficient population to the short-lived state to realize [gamma]-ray lasing. Even if the x-ray intensity were insufficient, study of such driven transitions would be quite valuable.

International Nuclear Information System (INIS)

The results of a combined investigation of splat-quenched Fe-Csub(x) (x<0.05) alloys by resistivity, X-ray diffraction and Moessbauer spectroscopy are presented. The residual resistivity increases linearly with the carbon content (#DELTA#rho=5#mu##OMEGA#cm/at.%) with a slope identical to that observed in the dilute ferritic phase. X-ray diffraction reveals the presence of a martensite structure in addition to a small fraction of residual austenite; the dependence of the a and c lattice parameters on xsub(c) agrees with earlier measurements. A detailed investigation of the relative reflexion intensities shows that the as-quenched martensites consist of a mixing of massive martensite and tetragonal martensite for low carbon content and of tetragonal martensite only for xsub(c) approximately 0.05. The Moessbauer spectra reveal 3 or 4 magnetically non equivalent iron sites. From a detailed analysis of ...

Energy Technology Data Exchange (ETDEWEB)

Nanocomposites containing polyethylene (PE) and montmorillonite clay organically modified (OMMT) with quaternary ammonium salts were obtained via direct melt intercalation. A montmorillonite sample from the Brazilian state of Paraiba was treated with four different types of quaternary ammonium salts. After the treatment, the powder was characterized by X-ray diffraction and scanning electron microscopy. The dispersion and morphologies of OMMT within PE were investigated by X-ray diffraction and transmission electron microscopy. The results revealed the formation of intercalated montmorillonite layers in the PE matrix. The thermal stability and flammability of the PE/montmorillonite clay nanocomposites were measured by thermogravimetry and horizontal burning tests for HB classification, Underwrites Laboratories (UL 94), respectively. It was shown that the samples do not degrade at the processing ...

International Nuclear Information System (INIS)

X-ray magnetic diffraction (XMD) technique was applied to an orbital ordering compound of ferromagnetic YTiO_3 for the first time. The orbital-magnetic form factor #mu# _L(k) and the spin-magnetic form factor #mu# _S(k) were independently measured by utilizing the LS separation ability of the XMD. The #mu# _L(k) was measured for ten reciprocal-lattice points. No significant values of the #mu# _L(k) were observed for most of the reciprocal-lattice points within the estimated statistical errors, which suggested quenching of the orbital moment. The #mu# _S(k) was measured for 22 reciprocal-lattice points. Fourier synthesis of the #mu# _S(k) gave the spin density distribution m _S(r) in the real space. The obtained m _S(r) map shows the characteristic feature of the electron distribution of 3d electron in the t_2_g state of a Ti atom coordinated by O"2"- ions, in which the electrons are distributed away from the negative O"2"- ions. It is concluded ...

Energy Technology Data Exchange (ETDEWEB)

Chemical looping combustion (CLC) is a novel technology where CO{sub 2} is inherently separated during combustion. Due to the existence of sulfur contaminants in the fossil fuels, the gaseous products of sulfur species and the interaction of sulfur contaminants with oxygen carrier are a big concern in the CLC practice. The reactivity of NiO/Al{sub 2}O{sub 3} oxygen carrier reduction with a gas mixture of CO/H{sub 2} and H{sub 2}S is investigated by means of a thermogravimetric analyzer (TGA) and Fourier Transform Infrared spectrum analyzer in this study. An X-ray photoelectron spectroscopy (XPS), X-ray diffraction (XRD) and scanning electron microscope (SEM) are used to evaluate the phase characterization of reacted oxygen carrier, and the formation mechanisms of the gaseous products of sulfur species are elucidated in the process of chemical looping combustion with a gaseous fuel containing hydrogen ...

International Nuclear Information System (INIS)

K?-to-K? X-ray intensity ratios of Ti and Ni have been measured in pure metals and in alloys of TixNi1-x (x=0.7, 0.6, 0.5, 0.4 and 0.3) following excitation by 22.69 keV X-rays from a 10 mCi 109Cd radioactive point source. The valence-electron configurations of these metals were determined by corporation of measured K?-to-K? X-ray intensity ratios with the results of multiconfiguration Dirac-Fock calculation for various valence-electron configurations. Valence-electron configurations of 3d-transition metals in alloys indicate significant differences with respect to the pure metals. Our analysis indicates that these differences arise from delocalization and/or charge transfer phenomena in alloys. Namely, the observed change of the valence-electron configurations of metals in alloys can be explained with the transfer of 3d electrons from one element to the other element and/or the rearrangement of electrons between 3d and 4s, ...

Energy Technology Data Exchange (ETDEWEB)

When chest radiographs are obtained using an anti-scatter grid in a mobile x-ray unit by Fuji Computed Radiography (FCR), right lung densities may differ from left lung densities owing to misalignment caused by an oblique x-ray beam. Such misalignment is considered to be caused by factors such as the shape of the bed and angle of the x-ray tube. Misalignment is especially frequent when exposure is carried out in the sitting position. Although a low-ratio grid has been reported to offer improvement, the misalignment is not completely eliminated. Therefore, we used a copper plate without a lattice feature instead of grid, and examined the results. The copper plate was found to have the ability of a grid to eliminate radiation scatter, and, furthermore, to offer the physical capabilities of a grid as determined by Carlin's new grid assessment method. Image quality was demonstrated through contrast manipulation to be ...

International Nuclear Information System (INIS)

In recent years it has become evident from epidemiological and experimental data that a large number of environmental factors, including diet, play a role in modifying the incidence of cancer. Cell culture systems in which oncogenic transformation serves as an end point are powerful tools for evaluating these questions. Using such systems it has been shown recently that pyrolysis products from charred surfaces of broiled meat and fish can transform hamster embryo cells in vitro as well as produce tumors in the animal. Our studies in vitro have demonstrated the oncogenic potential of ionizing radiation in both hamster and human cells and have established in hamster cells the dose response relationship at doses ranging from 1 to 600 rad for x-rays and 0.1 to 150 rad for neutrons. The present work was aimed at evaluating whether there exists a cocarcinogenic interaction between a pyrolysis product and x-rays in their ability ...

British Library Electronic Table of Contents (United Kingdom)

We performed experimental studies on the convolution/superposition method reported in the former companion paper (Iwasaki in Radiol Phys Technol 4, 2011) using 10-MV X-ray beams from open-jaw-collimated fields. The method uses primary and scatter dose kernels formed for energy bins of X-ray spectra reconstructed as a function of off-axis distance. We made a comparison of calculations and measurements in water phantoms and thorax-like phantoms with respect to percentage depth dose curves, tissue???phantom ratio curves, and dose profiles. We made the dose calculation by taking into account the beam-hardening effect with depth and the off-axis radiation-softening effect. We found that the method could be used, in general, for performing accurate dose calculations.

International Nuclear Information System (INIS)

HgTe rod-shape composed of crystalline particles has been prepared by a hydrothermal method, and characterized by means of X-ray powder diffraction (XRD), scanning electron microscopy (SEM), and transition electron microscopy (TEM). The effects of capping agents, reductants, reaction temperatures, and reaction times on crystal structures and shapes of HgTe have been investigated. The results showed that the CTAB as capping agent plays a crucial role in the hydrothermal process. The synthesis procedure is simple and uses less toxic reagents than the previously reported methods.

International Nuclear Information System (INIS)

The low alloy steels were nitrided in the plasma atmosphere generated by using hollow cathode discharge. For comparison, specimens of 40 Cr steel were in two different potential states. One kind is isolated from cathode and anode between them the discharge was created. The other kind is placed on the plate which is connected to the cathode. The nitriding was carried out at different temperatures. The surface morphology, phase of compound layers and microhardness profiles were analyzed. The optical microscopy observation and X-ray diffraction showed that the compound layers were formed in all experiments. The results of the nitriding treatment are weakly dependent on the potentials applied on the specimens.

International Nuclear Information System (INIS)

(Pb_1_-_x La_x) (Zr_0_._6_5 Ti_0_._3_5) ceramics, with x = 0.09 (PLZT 9/65/35) were prepared using lead monoxide (Pb O) with different amount of litharge (tetragonal) and massicot (orthorhombic) phases. Results, based on x-ray diffraction patterns, remanent polarization and dielectric measurements, show that the Pb O polymorphic phase does not change the final structure of the PLZT but causes changes on the remanent polarization and dielectric permittivity temperature dependence. (author). 11 refs, 2 figs, 2 tabs.