International Nuclear Information System (INIS)

Iron oxide films have been deposited on Si(100) substrates by chemical vapour deposition (CVD) of iron(III) tert-butoxide ([Fe(O "tBu)_3]_2) in the temperature range 350-450 deg. C. The precursor flux and substrate temperature were varied to control the phase composition, average grain size and film thickness. The nature of substrate and deposition temperature markedly influence the morphology and iron-oxygen stoichiometry in the CVD deposits. Phase transformations in iron oxide films were achieved through precise local and periodic heating of the films by interfering laser beams. The interaction of iron oxide films with short laser pulses (Nd:YAG, 355 nm) induced partial transformation of hematite (#alpha#-Fe_2O_3) to magnetite (Fe_3O_4) or magnetite to wuestite (Fe_1_-_xO), respectively. The phase characterization and ...

International Nuclear Information System (INIS)

In this work we present the electrical characterization of non self-aligned p-channel thin film transistors fabricated by using laser doping technique for source/drain contact formation and gate oxide deposited at room temperature by Electron Cyclotron Resonance Plasma Enhanced Chemical Vapour Deposition. These techniques are suitable for a very low temperature process for TFT fabrication. The output characteristics show a current increase at high drain voltage ('kink' effect) rather moderate, if compared to self aligned polysilicon TFTs, probably due to the gradual doping profile induced by laser doping process. After bias stress at low gate voltage and high drain voltage condition a strong reduction of kink current has been observed in the output characteristics at high drain voltage, whereas minor changes has been observed in the transfer characteristics. This behaviour is similar to what observed in ...

International Nuclear Information System (INIS)

Atmospheric pressure plasma enhanced chemical vapour deposition system is built. The electrical and optical characteristics of the APPECVD system is given. The system is used to deposit conductive polymers and nano composites onto glass and metal surfaces. The morphological, optical, chemical and electrical characteristics of deposited surfaces are investigated using SEM, AFM four probe deposition purposes. The photovoltaic applications of plasma deposited polymers and nonconsumption are compared with deposited with electrochemical methods show different results. The electrical, chemical and morphological structures of the samples will be given.

Energy Technology Data Exchange (ETDEWEB)

Photoelectrochemical oxidation is a potentially interesting method for destroying toxic organic materials. We have studied the photoelectrocatalytic activity of TiO{sub 2} films made by thermal oxidation of titanium, low pressure chemical vapour deposition (LPCVD), and anodisation of titanium. Two model organic compounds have been investigated for photooxidation: methyl phosphonic acid (MPA) which is a nerve gas analogue and 4-chlorophenol (4-CP) which is a chlorinated aromatic compound considered a standard for the evaluation of the TiO{sub 2} / UV processes. In addition to photoelectrochemical characterisation the films have been characterised by profilometry, XRD, AFM, photocurrent spectroscopy and Raman microscopy. Correlations have been made between the physical properties of the thin films and their catalytic activities. The most catalytic sample of thermally oxidised titanium was prepared at 400 ...

Energy Technology Data Exchange (ETDEWEB)

A 15-nm lithium fluoride (LiF) thin film evaporated on glass substrate is shown to enhance the nucleation of microcrystalline Si grown by plasma enhanced chemical vapour deposition at the amorphous/microcrystalline boundary conditions. The effect is more pronounced at low substrate temperatures, nucleation density being 10 times higher at {approx} 80 {sup o}C. The effect is ascribed to the ionic chemical nature of LiF, the low work function material used in organic electronic devices, and we propose its use for micro patterning crystalline Si regions in otherwise amorphous Si film.

Energy Technology Data Exchange (ETDEWEB)

Polycrystalline silicon films have been grown from Si{sub 2}H{sub 6} by low-pressure chemical vapour deposition at 800 K and in situ laser annealing (LA) on amorphous silicon seed layers deposited on a metallic Ti/Pd/Ag multilayer. The crystalline volume fraction in the seed layer was controlled by thermal annealing. According to the metal-induced crystallization effect, the presence of the metal induces a lower-temperature crystallization of silicon in the seed layers. X-ray diffraction and scanning electron microscopy data show that the formation of palladium silicides in the seed layer drives the growth of wire-like columns which are found to change morphology depending on the seed layer microstructure and LA parameters. It is suggested that superficial palladium was found to affect also the growth rate by enhancing the Si{sub 2}H{sub 6} dissociation.

Energy Technology Data Exchange (ETDEWEB)

Cathodic arc deposition is an established and industrially applied technique for the formation of nitrides (e.g. TiN); it can also be used for metal oxide thin film formation. A cathodic arc plasma source with the desired cathode material is operated in an oxygen atmosphere of appropriate pressure, and metal oxides of various stoichiometric composition can be formed on different substrates. We report here on a series of experiments on metal oxide formation by cathodic arc deposition for different applications. Black copper oxide has been deposited on accelerator components to increase the radiative heat transfer between the parts. Various metal oxides such as tungsten oxide, niobium oxide, nickel oxide and vanadium oxide have been ...

International Nuclear Information System (INIS)

The possibilities to grow isolated structures of complex oxides by pulsed laser deposition through stencils were investigated. A stencil consisting of a SiN membrane with apertures of several hundred nanometers embedded in a Si chip is placed in front of a heated substrate (up to 750 degrees Celsius). Deposition through these apertures results in resistless, direct patterning by local deposition of complex oxides like ferroelectric Lead Zirconate Titanate. The created isolated structures were analyzed by AFM imaging. Under-deposition, in this work called broadening, is inevitable during stencil deposition and is depending on deposition parameters, especially pressure. Different causes of broadening are mapped and discussed.

Energy Technology Data Exchange (ETDEWEB)

A series of ball-on-disc wear and friction measurements were made for surfaces which have a chemical vapour deposition carbon silicon alloy layer on a carbon substrate (fine grain POCO graphite). Nitrogen ion irradiation was used to improve the wear resistance of the carbon alloy surface. For comparison, measurements were also taken for alumina against alumina. It was found that the lowest friction coefficient and lowest wear occurred for ion irradiated coated samples containing 4% Si in the alloy and that the performance was superior to that of alumina. ((orig.))

Energy Technology Data Exchange (ETDEWEB)

Deposition of hard coatings may influence the mechanical properties of the bulk material and its corrosion resistance. In this work we study the hardness of the coated and the back side of 100Cr6 steel plates. Electrochemical corrosion tests were performed in O{sub 2}-saturated acetate buffer of pH 5.6 at 25degC. Chromium nitride and titanium nitride coatings prepared by different physical vapour deposition processes, such as arc, thermionic arc evaporation, magnetron sputtering and ion-beam-assisted deposition (IBAD) were compared. The results show that, for sufficient corrosion protection, chromium nitride layers have to be thicker than 500 nm. An increased nitrogen partial pressure in the evaporation chamber of the IBAD process improves the corrosion resistance significantly. The hardness of the substrates was reduced in the case of thermoionic arc evaporation only, indicating a ...

International Nuclear Information System (INIS)

Focused Ion Beams are an important approach for nanostructure fabrication in the semiconductor industry and material sciences. Applications in sputtering and ion induced deposition of materials are investigated. The IMSA FIB system equipped with the high resolution Orsay Physics CANION M31plus ion column with current densities up to 10 A/cm"2 including a gas injection system is applied. In this work the ion beam induced chemical vapour deposition of tungsten, wherefore tungsten hexacarbonyl as precursor gas is used for a first investigation. Conductive tungsten-nanowires with smallest cross-section upon a substrate of Si and SiO_2 are produced. The ion beam parameters of this focused ion beam system are optimized for the metal deposition. A short insight in the theory of layer nucleation and growth induced by the ion beam during the metal deposition is given. The layer quality is ...

UK PubMed Central (United Kingdom)

Obesity is characterized by the abnormal or excessive deposition of fat in the adipose tissue. Its consequences go far beyond adverse metabolic effects on health, causing an increase in oxidative stress,...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In this work we present an ultra-low temperature method for the oxidation of an amorphous silicon-carbide-nitride (SiCN) material. The SiCN is deposited on silicon substrates by plasma enhanced chemical vapor deposition using CH{sub 4}, SiH{sub 4}, and N{sub 2} chemistry. The physical and chemical properties are characterized for the as-deposited SiCN and post-oxidized films are discussed. The SiCN film is exposed to oxygen plasma, where it undergoes a chemical transformation into a binary SiO{sub 2} material system. A 1.7 nm/min oxidation rate is typical for this process and compares favorably to oxidation methods utilizing much higher temperatures. The substrate temperature remains extremely low throughout the oxidation process, T{sub s} < 200 deg. C. Changes in film stress, optical constants, film thickness, ...

Energy Technology Data Exchange (ETDEWEB)

Means of intensifying heat transfer with nucleate boiling, based on boiling under constrained conditions (in slots, on a capillary-porous surface) are the most promising since a high intensity of heat transfer is ensured. In the present work we attempt to evolve the main assumptions for the physical model of the process of vapour formation under constrained conditions and to extend them to the boiling of cryogenic liquids on surfaces with a capillary-porous deposit; also, the results are given of experimental investigations of heat transfer with the boiling of nitrogen, oxygen and hydrogen at atmospheric perssures and below on capillary-porous surfaces of various metals of different structure produced by an electric arc method of gasothermal spray coating.

Science.gov (United States)

The growth of an oxide interfacial layer was recently found to increase the open-circuit voltage (OCV) and efficiency by up to 60 per cent in GaAs metal-semiconductor solar cells. Details of oxidation techniques to provide the necessary oxide thickness and chemical structure and using ozone, water-vapor-saturated oxygen, or oxygen gas discharges are described, as well as apparent crystallographic orientation effects. Preliminary results of the oxide chemistry obtained from X-ray, photoelectron spectroscopy are given. Ratios of arsenic oxide to gallium oxide of unity or less seem to be preferable. Samples with the highest OVC predominantly have As(+3) in the arsenic oxide rather than As(+5). A major difficulty at this time is a reduction in OCV by 100-200 mV when the antireflection coating is vacuum deposited.

Energy Technology Data Exchange (ETDEWEB)

Solar cells and organic electronic devices require an encapsulation to ensure sufficient lifetime. Key parameters of the encapsulation are permeation barrier, UV stability, temperature stability, optical transmission spectra and mechanical stability. The requirements depend very much on the specific application. Many work groups suggest multilayer stacks to meet the permeation requirements. In this paper the permeation barrier properties of the different constituents of such a multilayer stack are characterized. Different layer materials are compared regarding their water vapour and oxygen permeability as well as the influence of process parameters is examined. Finally temperature dependent permeation measurements are used to characterize the permeation mechanisms in the different constituents of the multilayer barrier.

International Nuclear Information System (INIS)

The effect of atmospheric radioactive emissions from United Kingdom nuclear installations on acid deposition is assessed. Nitrogen oxide and ozone production resulting from and associated with discharges of airborne radioactivity, comparison with conventional emissions, and the direct effects of radioactive emissions on trees, are all discussed. (UK).

International Nuclear Information System (INIS)

Yttria stabilized zirconia (YSZ) with 8 mol% Y was deposited by reactive magnetron sputtering onto oxidized (100) silicon substrates. It was possible to switch film texture from (111) to (200) by applying a strong RF substrate bias. Transmission electron microscopy showed that the film deposited under bias is porous and exhibits nanoscaled grains, whereas the film deposited without bias is dense and columnar. The ionic conductivity as a function of temperature revealed an activation energy of 1.04 eV. The mechanical stress could be tuned to low values by thermal post-annealing. Using the dense (111) film as electrolyte layer, and the porous (200) film as an interlayer to a porous Pt anode, an open circuit voltage of 0.85 V was obtained in a micro machined fuel cell structure.

International Nuclear Information System (INIS)

Crystalline and non-crystalline iron oxide (#alpha#-Fe_2O_3) thin films were obtained by spray pyrolysis onto glass substrate at different temperatures. The results of X-ray diffraction showed that with increasing the deposition time, the film structure changed from non-crystalline to crystalline at the same substrate temperature. At different substrate temperatures and low deposition times (5 min), iron oxide appears almost in non-crystalline form. With rising the substrate temperature and deposition time, the crystallinity was improved. The effect of substrate temperature as well as deposition time on the optical features (absorption coefficient and bandgap) and optical constants of these films has been investigated. Optical constants of the films were determined from spectrophotometric measurement of reflectance and transmittance. Analysis of the results ...

British Library Electronic Table of Contents (United Kingdom)

Si nanocrystal floating gate MOS capacitors were formed on p-Si (100) wafers by thermal plasma jet (TPJ) annealing of SiO2/SiOx /SiO2/Si(100) stacked structure. The chemical composition of SiOx layer was controlled by changing the SiH4, He, and O2 gas flow ratio during plasma enhanced chemical vapour deposition. The MOS capacitors showed clear hysteresis in capacitance-voltage (CV) characteristics after TPJ annealing. The hysteresis width shows maximum value when initial composition x =1.7, which shows the maximum photoluminescence (PL) intensity. The maximum hysteresis width of 6.8 V was observed with gate voltage swept between 20 and -20 V in x = 1.7 sample. The result means 7.4 x 1012 cm-2 carriers are injected to or emitted from Si nanocrystals. The duration of 1 V shift in flatband vo...

International Nuclear Information System (INIS)

For obtaining radiation less damagable laser mirrors, a preliminary optimization of film fabrication suitable for the analysis of laser damage mechanism has been done as the first step. Here, the optimization requires not only the stable fabrication process but also the ideal film structure i.e., the amorphous and smooth film structure simultaneously, eliminating latently unwanted secondary effects such as light scattering during laser damage test. For this purpose, we adopted the ion assisted deposition (IAD) method and modified the deposition conditions for titanium and tantalum oxide films, both of which compose typical high index layers, and where SiO_2 layers are also chosen as low index layers because of their amorphous and smooth nature, in alternative multilayer laser mirrors. Surface and cross sectional film structures and film crystallinity are compared and characterized, using a high resolution SEM and a x-ray ...

International Nuclear Information System (INIS)

One of the main problems related to optical thin film materials used in high power laser environments is the catastrophic damage caused to them due to laser irradiation. While the influence of ion bombardment on the optical properties of oxide thin films is now a well understood subject, the morphology and crystalline behaviour of these films under ion incidence is not so well studied. Hence, it is of great importance to investigate the effects of ion bombardment during growth on the microstructure and crystalline behaviour of oxide materials.

International Nuclear Information System (INIS)

The influence of high energy electron (23 MeV) irradiation on the electrical characteristics of p-channel polysilicon thin film transistors (PSTFTs) was studied. The channel 220 nm thick LPCVD (low pressure chemical vapor deposition) deposited polysilicon layer was phosphorus doped by ion implantation. A 45 nm thick, thermally grown, SiO_2 layer served as gate dielectric. A self-alignment technology for boron doping of the source and drain regions was used. 200 nm thick polysilicon film was deposited as a gate electrode. The obtained p-channel PSTFTs were irradiated with different high energy electron doses. Leakage currents through the gate oxide and transfer characteristics of the transistors were measured. A software model describing the field enhancement and the non-uniform current distribution at textured polysilicon/oxide interface was developed. In order to assess the ...

Energy Technology Data Exchange (ETDEWEB)

A thin film microoxidation test utilizing the concept of the Lubricant Stability Map has been used to study the effect of temperature on deposit formation by lubricants on upper piston locations of low heat rejection engines. The stability maps were established for two formulated lubricants in this study. These two lubricants were also evaluated in a series of engine tests with various piston temperatures. The deposition phenomena observed in the engine tests have been adequately simulated and described by the stability maps. It is concluded that lubricants at upper piston locations are under a thin film condition similar to that achieved by the thin film microoxidation test. The deposit formation trend is determined by the volatility, thermal stability, and oxidative stability of the base stock. Additives have little effect on deposit formation at very high temperatures. A combined ...

Energy Technology Data Exchange (ETDEWEB)

The aim was to gain experience on how to produce Alkali Metal Thermo-Electric-Converter (AMTEC) cells, for the demonstration of their principles and potentials, as a basis for future commercialization. These cells should be able to present an efficient and direct conversion of thermal energy to electric energy. The system is based on an electro-chemical concentration cell built around a {beta}`` aluminium oxide membrane that separates the two chambers. This material is a good conductor of sodium and a bad conductor of electrons, and it is this property which is taken advantage of. In the two chambers of the cell is found saturated sodium vapour at two temperatures. The motive power is the expansion over the membrane where the sodium ions are transported through it whilst the electrons are forced through the outer cycle. This concept is described in detail in addition to the choice of materials, performance testing and results. It was found ...

British Library Electronic Table of Contents (United Kingdom)

Methods of X-ray diffraction and transmission electron microscopy were used to study the microstructure of dispersion-strengthened Cu-Al2O3 nanocomposites obtained by the method of simultaneous deposition of Cu and Al2O3 from the vapor phase. The effect of the size of particles of the oxide (Al2O3) and of their content on the electrical resistance of the composite has been considered. The results obtained make it possible to suppose that the main structural factor that determines the electrical resistance of the composite are nanodispersed particles of Al2O3 with a size of less than 20 nm.

International Nuclear Information System (INIS)

By means of an audio frequency plasma polymerisation ultra-thin gradient plasma polymer layers were deposited on zinc and zinc-coated iron. The aim was to generate an interfacial polymeric layer which bonds to an oxidised metal as well as to a subsequently applied organic coating and acts as an interfacial barrier layer for ions and water. Surface modifications were done in an in situ plasma cell with infrared reflection absorption spectroscopy (IRRAS). The zinc surface was first activated by an oxygen plasma to provide a freshly oxidised and contamination free oxide surface. The intermediate stages of the surface reactions could be revealed. Carbon dioxide molecules as oxidation products adsorbed on the growing zinc oxide and were desorbed at a later stage. An organosilicon plasma polymer was deposited directly on top of the oxide layer from a ...

British Library Electronic Table of Contents (United Kingdom)

In situ composite coating of hydroxyapatite (HA)/TiO2 were produced on titanium (Ti) substrate by micro-arc oxidation coupled with electrophoretic deposition (MAO&EPD) technique with different concentrations of HA particles in the 0.2M NaOH electrolyte solution. The surface morphology and chemical composition of the hybrid coating were effected by HA concentration. The amount of HA particles incorporated into coating layer increased with increasing HA concentration used in the electrolyte solution. The corrosion behavior of the coating layer in simulated body fluids (SBF) was evaluated using a potentiodynamic polarization test. The corrosion resistance of the coated sample was increased compared to the untreated Ti sample. The in vitro bioactivity assessment showed that the MAO&EPD treated...

International Nuclear Information System (INIS)

A wide variety of thin film coatings, deposited by different techniques and with potential applications in various important areas, have been characterised by the Phase Modulated Spectroscopic Ellipsometer, installed recently in the Spectroscopy Division, B.A.R.C. The Phase Modulated technique provides a faster and more accurate data acquisition process than the conventional ellipsometry. The measured Ellipsometry spectra are fitted with theoretical spectra generated assuming an appropriate model regarding the sample. The fittings have been done objectively by minimising the squared difference (#chi#"2) between the measured and calculated values of the ellipsometric parameters and thus accurate information have been derived regarding the thickness and optical constants (viz, the refractive index and extinction coefficient) of the different layers, the surface roughness and the inhomogeneities present in the layers. Measurements have been done on (i) ion-implanted ...

International Nuclear Information System (INIS)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage measurement. The ...

Energy Technology Data Exchange (ETDEWEB)

Surface doping of conjugated polymers is realized by depositing a thin layer of graphene oxide (GO) on top of the polymers. The high proton density and the unique 2D structure of GO facilitate the protonic surface doping of conjugated polymers to achieve high conductivities. This finding represents a new strategy for improving charge transport across the metal/conjugated polymer interface to achieve much improved performance in organic solar cells. (Copyright copyright 2011 WILEY-VCH Verlag GmbH and Co. KGaA, Weinheim)

International Nuclear Information System (INIS)

The present process allows to eliminate the corrosion products formed on the tube plates and in the interstices of plate-tube crosspieces of a PWR steam generator in order to avoid a corrosion phenomenon which may cause denting by presence of oxides. The process consists in applying on these oxides at about 50-100 degrees, an aqueous solution containing 6-8% of gluconic acid, 3-5% of citric acid, about 0.5% of a corrosion inhibitor and ammonia until a pH of 3-9.5 is obtained.

International Nuclear Information System (INIS)

Technology of plasma sputtering, structure and properties of zirconium dioxide coatings were studied. Necessity of void number increase to enhance coating heat-resistance is shown. Optimal powder particle size (20-60 #mu#m) providing optimal coating porosity was determined. Weight part of stabilizating oxide (Y_2O_3) in ZrO_2 for formation in coating of microcracks serving as barriers for macro-cracks propagation was determined.

Science.gov (United States)

The Advanced Statistical Trajectory Regional Air Pollution (ASTRAP) model simulates long-term transport and deposition of oxides of and nitrogen. t is a potential screening tool for assessing long-term effects on regional visibility from sulfur emission sources. owever, a rigorou...

Energy Technology Data Exchange (ETDEWEB)

Development of electronic devices with better performance and smaller size requires the passive components to be embedded within a printed wire board (PWB). The 'film-on-foil' approach is the most viable method for embedding these components within a PWB. We have deposited high-permittivity ferroelectric lead lanthanum zirconate titanate (Pb{sub 0.92}La{sub 0.08}Zr{sub 0.52}Ti{sub 0.48}O{sub x}, PLZT 8/52/48) films on base metal foils by chemical solution deposition. These prefabricated capacitor sheets can be embedded into PWBs for power electronic applications. To eliminate the parasitic effect caused by the formation of a low-permittivity interfacial oxide, a conductive buffer layer of lanthanum nickel oxide (LNO) was applied by chemical solution deposition on nickel foil before the deposition of PLZT. With a {approx} 0.7-{micro}m-thick ...

International Nuclear Information System (INIS)

The deposit of radioactive corrosion products in the cooling systems of nuclear reactors becomes a serious problem for the personnel of facilities. Crud has an important role in the process of depositing radioactive corrosion products. The main components of crud are hematite, magnetite, nickel ferrite and so on, and the particles of these oxide compounds are distributed in water. Most of the behavior of crud are still not known. As for the mechanism of the production of crud, the Potter-Mann model has been proposed. However, the precipitation process of iron ions in water is unknown. The crud is defined as the particles filtered by 0.45 micrometer millipore filters. However, it is not known whether there are crud particles smaller than this size. The crud particles can be adsorbed on the filters by the surface electrochemical interaction. The adsorption of cations to crud particles was studied. The adhesion of crud ...

Energy Technology Data Exchange (ETDEWEB)

The reduction of oxygen was studied in 0.1 M KCl at 70 deg. C using the rotating disk electrode (RDE) technique on platinum and electrodeposited ZnO thin film electrodes deposited on platinum substrates. In the absence of Zn{sup 2+} ions in solution, a Tafel slope of 139 mV dec{sup -1} was obtained, a value close to that measured on bare platinum electrode (133 mV dec{sup -1}) and ascribed to the limitation of the reaction rate by the first electron transfer. The main difference between the noble metal and the oxide electrode was a shift of the curves towards more negative potentials. In the presence of Zn{sup 2+} ions, the current density decreased significantly and the Tafel slope was measured at 282 mV dec{sup -1} showing that the electrode was partially blocked by zinc oxide formation reaction intermediates.

Energy Technology Data Exchange (ETDEWEB)

In an aim to develop photo-responsive composites, the UV photo-reduction of aqueous titanium oxide nanoparticle-graphene oxide (TiO{sub 2}-GO) dispersions (Lambert et al. J Phys. Chem. 2010 113 (46), 19812-19823) was undertaken. Photo-reduction led to the formation of a black precipitate as well as a soluble portion, comprised of titanium oxide nanoparticle-reduced graphene oxide (TiO{sub 2}-RGO). When allowed to slowly evaporate, self assembled titanium oxide nanoparticle-graphene oxide (SA-TiO{sub 2}-RGO) films formed at the air-liquid interface of the solution. The thickness of SARGO-TiO{sub 2} films range from {approx}30-100 nm when deposited on substrates, and appear to be comprised of a mosaic assembly of graphene nanosheets and TiO{sub 2}, as observed by scanning electron microscopy. Raman spectroscopy and X-ray photoelectron ...

International Nuclear Information System (INIS)

Iron oxide thin films were prepared by spray pyrolysis technique onto glass substrates from iron chloride solution. They were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and (UV-vis) spectroscopy. The films deposited at T _s #<=# 450 deg. C were amorphous; while those produced at T _s_u_b = 500 deg. C were polycrystalline #alpha#-Fe_2O_3 with a preferential orientation along the (1 0 4) direction. By observing scanning electron microscopy (SEM), it was seen that iron oxide films were relatively homogeneous uniform and had a good adherence to the glass substrates. The grain size was found (by RX) between 19 and 25 nm. The composition of these films was examined by X-ray photoelectron spectroscopy and electron probe microanalysis (EPMA). These films exhibited also a transmittance value about 80% in the visible and infrared range. The cyclic ...

Energy Technology Data Exchange (ETDEWEB)

The excellent high temperature strength and thermal conductivity of molybdenum-base alloys provide attractive features for components in advanced magnetic and inertial fusion devices. Refractory metal alloys react readily with oxygen and other gases. Oxidized molybdenum in turn is susceptible to losses from volatile molybdenum trioxide species, (MoO3)m, in air and the hydroxide, MoO2(OH)2, formed from water vapor. Transport of radioactivity by the volatilization, migration, and re-deposition of these volatile species during a potential accident involving a loss of vacuum or inert environment represents a safety issue. In this report we present experimental results on the oxidation, volatilization and re-deposition of molybdenum from TZM in flowing air between 400 and 800°C. These results are compared with calculations obtained from a vaporization mass transfer model using chemical thermodynamic ...

International Nuclear Information System (INIS)

In this work we investigate an iron oxide thin film grown with atomic layer deposition for a gas sensor application. The objective is to characterize the structural, chemical, and electrical properties of the film, and to demonstrate its gas-sensitivity. The obtained scanning electron microscopy and atomic force microscopy results indicate that the film has a granular structure and that it has grown mainly on the glass substrate leaving the platinum electrodes uncovered. X-ray diffraction results show that iron oxide is in the #alpha#-Fe_2O_3 (hematite) phase. X-ray photoelectron spectra recorded at elevated temperature imply that the surface iron is mainly in the Fe"3"+ state and that oxygen has two chemical states: one corresponding to the lattice oxygen and the other to adsorbed oxygen species. Electric conductivity has an activation energy of 0.3-0.5 eV and almost Ohmic current-voltage dependency. When exposed to O_2 ...

Energy Technology Data Exchange (ETDEWEB)

The effect of flame temperature on the Moza-Austin sticking test has been evaluated by increasing the adiabatic flame temperature used to melt the pellet and make it drop. It was found that the variation of apparent contact angle with substrate temperature, for an oxidized steel substrate, was almost independent of flame temperature over the range of 1750-2500 C. However, the strength of adhesion to the substrate increased with higher flame temperature at each substrate temperature. The adhesion force of a drop frozen on the substrate at constant temperature also increased with time up to about one h. This indicated that the adhesion was not caused solely by mechanical anchoring of solidified glass in the pores of the oxide layer. Reduction of the substrate temperature to lower temperatures after attachment of the drop caused lower strength of adhesion, but this was partially restored by raising the temperature. This also suggested a continuing ...

Energy Technology Data Exchange (ETDEWEB)

Over one-third of Canada's coal resources occurs in the southern Canadian Rocky Mountains, with major deposits in the Front Ranges, Inner Foothills and Outer Foothills. In the Front Ranges, deposits of metallurgical and thermal, high-volatile bituminous to semi-anthracite coal occur in the Late Jurassic-Early Cretaceous Mist Mountain Formation. In the Inner Foothills of northeastern British Columbia and west-central Alberta, resources of metallurgical and thermal medium- and low-volatile bituminous coal occur in Early Cretaceous strata of the Gething and Gates Formations. In the Outer Foothills resources of thermal, high-volatile bituminous coal occur in Late Cretaceous and Paleocene strata of the Belly River Coalspur and Paskapoo Formations. The major deposits of the Front Ranges and Inner Foothills accumulated within the coastal plains of the Fernie and Moosebar-Clearwater seas. Shorelines prograded to the north ...

International Nuclear Information System (INIS)

The paper describes the production of highly enriched isotopes of uranium, plutonium, americium and curium by electromagnetic separation for scientific and applied researches in physics, chemistry, geology, medicine, biology and other fields. Using the equipment described, the isotopes are produced in quantities sufficient to set up nuclear physical experiments, to produce nuclear reference materials and standard sources for calibration of radiometrical and mass spectrometrical equipment, in radionuclide metrology, etc. For the following isotopes the indicated degrees of isotopic enrichment were achieved: "2"3"3U-99.97%; "2"3"5U-99.97%; "2"3"6U-98.0%; "2"3"8U-99.997%; "2"3"8Pu-99.6%; "2"3"9Pu-99.9977%; "2"4"0Pu-99.9-100%; "2"4"1Pu-96.998%; "2"4"2Pu-97.8-99.96%; "2"4"4Pu-96.7%; "2"4"1Am-99.6%; "2"4"2"mAm-73.6%; "2"4"3Am-99.2-99.94%; "2"4"3Cm-99.99%; "2"4"5Cm-99.998%; "2"4"6Cm-99.8%; "2"4"7Cm-90%, "2"4"8Cm-97%. Methods for preparing layers of highly enriched isotopes on various ...

International Nuclear Information System (INIS)

Full text of publication follows: Slightly over-stoichiometric lithium orthosilicate pebbles have been selected as one optional breeder material for the European Helium Cooled Pebble Bed (HCPB) blanket. This material has been developed in collaboration of Research Center Karlsruhe and the Schott Glass, Mainz. The lithium orthosilicate pebbles are fabricated from lithium hydroxide and silica by a melting and spraying method in a semi-industrial scale facility. Lithium hydroxide was selected as the precursor since enriched lithium hydroxide is commercially available. The lithium orthosilicate pebbles produced by the process contains oxide phases besides orthosilicate, but it was also found that the oxide phases can be decomposed by annealing at high temperatures. The lithium orthosilicate pebbles produced in this way possesses satisfactory pebble characteristics. Therefore, the authors performed out-of-pile annealing tests using the lithium ...

Energy Technology Data Exchange (ETDEWEB)

Desiccants have been used in many applications to provide dehumidification. This paper describes an application of desiccants which provide both dehumidification and sensible cooling, with little or no use of conventional vapour-compression refrigeration plant. Through a parametric study, the energy consumption and costs of a desiccant cooling system are compared with those of a conventional vapour-compression refrigeration-based air-conditioning system. (author)

Energy Technology Data Exchange (ETDEWEB)

A complex modulated structure is described for reactive elements that have the capability of considerably more heat than organic explosives while generating a working fluid or gas. The explosive and method of fabricating same involves a plurality of very thin, stacked, multilayer structures, each composed of reactive components, such as aluminum, separated from a less reactive element, such as copper oxide, by a separator material, such as carbon. The separator material not only separates the reactive materials, but it reacts therewith when detonated to generate higher temperatures. The various layers of material, thickness of 10 to 10,000 angstroms, can be deposited by magnetron sputter deposition. The explosive detonates and combusts a high velocity generating a gas, such as CO, and high temperatures. 2 figs.

International Nuclear Information System (INIS)

Under operational conditions in nuclear power plants, the carbon steel components of the primary and secondary circuits react with high temperature cooling agent forming several iron oxides and oxyhydroxides. These deposits can result in tubes' constrictions, pitting and intergranular corrosion and finally to heat transfer reducing and increasing of radiation fields around the circuits, as well. The descaling process involves the chemical dissolution of the corrosion deposits by means of diluted organic acidic solutions containing usually a carboxylic acid, a reductant and one or more corrosion inhibitors. To evaluate the removing rates of these superficial films two types of methods were used, the gravimetric and potentiodynamic techniques. By correlating the experimental results, we established the chemical composition of descaling solution and two models of mechanisms applicable to our specific conditions. (authors)

International Nuclear Information System (INIS)

Rapid corrosion of PWR steam generator carbon steel support structures and consequential denting of steam generator tubes led to considerable investigation of the mechanism of corrosion and for palliatives. The basic mechanism is now fairly well understood. Chloride present in the boiler feedwater from condenser leakage is concentrated in the support plate crevice as a result of the superheat present. This leads to the formation of a low pH acid ferrous chloride environment either through the hydrolysis of a weak base chloride such as MgCl_2 or the combined action of a neutral chloride with an oxidizing agent. Rapid attack of the carbon steel ensues with the Fe_3O_4 corrosion product forming at the metal/oxide interface. This oxide has a volume approximately twice that of the steel consumed and thus eventually fills the crevice between the tube and the support plate. Oxide growth continues leading to ...

Energy Technology Data Exchange (ETDEWEB)

Based on the air pollution values typical of brown coal furnaces the paper discusses pollution abatement measures on the part of fuel engineering and flue gas technology. Fuel engineering contributes to air pollution abatement by measures such as stepped air supply, stepped fuel supply and flue gas draw-in. Flue gas technology largely relies on measures such as the SCR method using different catalytic converters, the noncatalytic reduction of nitrogen oxides, the simultaneous separation of sulfur dioxides and nitrogen oxides, and the Denox-Luvo method. The paper concludes with remarks on the RWE brown coal power plant retrofitting scheme planning to have all power plants equipped with adequate denitrification systems until the end of 1989 at the latest. (orig./PW)

International Nuclear Information System (INIS)

High-resolution sequence stratigraphy has been applied widely in the petroleum exploration and development, many achievements have been achieved. However, it is in the beginning stage that high-resolution sequence stratigraphy is applied to explore the sandstone-type uranium deposits in Erlian Basin. By applying principles of high-resolution sequence stratigraphy and taking typical boreholes as an example, sedimentary cycles of Saihan Formation, the ore-bearing formation in Baiyinwula area are divided and correlated through cross sections. One long-term cycle (LSC_1), two middle-term cycles (MSC_1, MSC_2) have been identified in this study. Based on this and combined with the mineralization character of sandstone uranium deposits in this area, it is presented that the interlayer oxidation zone is developed mainly in the rising hemicycle of MSC_1 and uranium ore bodies predominantly in channel sand bodies that were developed ...

Energy Technology Data Exchange (ETDEWEB)

An analysis was made on corrosion suppression mechanism of glycoletherdiaminetetraacetic acid (GEDTA) film made from GEDTA on stainless steel, and its corrosion inhibition effect. Results of analysis using IR spectrum, IR-ATR spectrum, {sup 1} HNMR spectrum, and ESCA spectrum indicated the deposition of the GEDTA film is a chemical deposition. In polarization tests at pH = 5 and 7, both polarization curves shifted to the constant current density side, showing suppression effect in reactions at both pH. When the corrosion environment is made severer, such as to pH = 2 and 4, the corrosion suppression effect of GEDTA became more distinctive. A ferroxyl test identified very little difference between untreated and treated materials. In a chemical pitting test, because oxidant and corrosive anion coexist in the test solution, and GEDTA is stable against corrosive anion Cl {sup {minus}}, the film is unstable against the ...

Energy Technology Data Exchange (ETDEWEB)

We present device results from polysilicon thin film transistors (TFTs) fabricated at a maximum temperature of 100&hthinsp;{degree}C on polyester substrates. Critical to our success has been the development of a processing cluster tool containing chambers dedicated to laser crystallization, dopant deposition, and gate oxidation. Our TFT fabrication process integrates multiple steps in this tool, and uses the laser to crystallize deposited amorphous silicon as well as create heavily doped TFT source/drain regions. By combining laser crystallization and doping, a plasma enhanced chemical vapor deposition SiO{sub 2} layer for the gate dielectric, and postfabrication annealing at 150&hthinsp;{degree}C, we have succeeded in fabricating TFTs with I{sub ON}/I{sub OFF} ratios {gt}5{times}10{sup 5} and electron mobilities {gt}40 cm{sup 2}/V&hthinsp;s on polyester substrates. {copyright} {ital 1999 ...

Energy Technology Data Exchange (ETDEWEB)

Cyclic voltammetry (CV), scanning electron microscopy (SEM), and energy dispersive spectroscopy (EDS) were employed to investigate the electrodeposition of Eu and Al in an LiCl-KCl eutectic melt containing Eu{sup 2+} and Al{sup 3+} at 450 deg. C. In order to deposit a pure Eu and Al alloy, the stoichiometrically lower concentration of Al{sup 3+} than that of Eu{sup 2+} and Al wires as a counter electrode was introduced into the bath of LiCl-KCl melt for the electrodeposition. The electrodeposition takes place at a potential more negative than -1.95 V vs. Ag|Ag{sup +} while the deposit is oxidized at more positive potential than -1.92 V. Two new reduction peaks and an anodic peak on a W working electrode were observed at -2.39 V, -2.42 V, and -2.1 V, vs. Ag|Ag{sup +}, respectively, suggesting that the potential window of the Al system in LiCl-KCl melt can be extended to -2.43 V vs. Ag|Ag{sup +}. The EDS analysis indicated ...

Energy Technology Data Exchange (ETDEWEB)

Isothermal transformation kinetics of austenite to acicular ferrite and allotriomorphic ferrite were measured in reheated low alloy steel weld deposits with similar weld compositions and austenite grain size but different inclusion characteristics. Accelerated kinetics of transformation to acicular ferrite were observed in weld metal containing coarser and titanium-rich inclusions. In contrast, kinetics of transformation to allotriomorphic ferrite were not influenced by inclusion characteristics, but, rather, by the austenite grain size and carbon concentration.

International Nuclear Information System (INIS)

We studied the epitaxial growth of iron silicide (#epsilon#-FeSi,#beta#-FeSi_2, and #alpha#-FeSi_2) nanodots on Si (111) substrates by Fe deposition on Si nanodots on Si (111) substrates with ultrathin Si oxide films using reflection high-energy electron diffraction, scanning tunneling microscopy, and transmission electron microscope (TEM). We formed almost single phase iron silicide nanodots by controlling the Fe deposition conditions; growth temperature, deposition rate, and amount. The #epsilon#-FeSi or #alpha#-FeSi_2 nanodots were epitaxially grown in a dome shape with an average size of #approx#5 nm and an ultrahigh density (>10"1"2 cm"-"2) on the surface. We formed #approx#2-nm high and #approx#8-nm wide #beta#-FeSi_2 nanodots in a dome shape with a density of #approx#5x10"1"1 cm"-"2 on the surface. Cross-sectional TEM images revealed that the #beta#-FeSi_2 growth continued beneath the Si ...

International Nuclear Information System (INIS)

Present and potential future changes to the global environment have important implications for marine pollution and for the air-sea exchange of both anthropogenic and natural substances. This report addresses three issues related to the potential impact of global change on the air-sea exchange of chemicals: Global change and the air-sea transfer of the nutrients nitrogen and iron. Global change and the air-sea exchange of gases. Oceanic responses to radiative and oxidative changes in the atmosphere. The deposition of atmospheric anthropogenic nitrogen has probably increased biological productivity in coastal regions along many continental margins. Atmospheric deposition of new nitrogen may also have increased productivity somewhat in mid-ocean regions. The projected future increases of nitrogen oxide emissions from Asia, Africa and South America will provide significant increases in the rate of ...

Energy Technology Data Exchange (ETDEWEB)

The passive films formed in stainless steels are thin and fine oxide films, a high corrosion resistance can be provided by these films. This study formed SiO2 protective coating on the substrate of SUS 304 stainless steels by chemical vapor deposition using TEOS-O3 system. Firstly, relations of substrate temperature and deposition rate of films, chemical composition, refractive index of films were investigated. Then, the corrosion resistance of SUS 304 stainless steels coated SiO2 films was examined by activation time and an anodic polarization curve in 1 kmol[center dot]m[sup -3] HCl solution. The results were obtained as follows. Thickness of SiO2 films linearly increases with time at the deposition temperature of 473 to 673 K. Si-OH bonds would disappear above the deposition temperature of 573 K, almost perfect SiO2 films were obtained. The activation time in 1 kmol[center ...

International Nuclear Information System (INIS)

Production of Fe_2O_3, Y_2O_3, YFeO_3, Y_3Fe_5O_1_2 powders using the alkoxomethod - during hydrolysis by yttrium and iron alcohol solutions, is studied. It is stated that production of the powders of Y_2O_3-Fe_2O_3 system oxides using alkoxomethod permits to decrease essentially the reaction volumes, number of operations, their duration as compared to the cooxidation of oxide hydrates from inorganic salt aqueous solutions. During heat treatment of iron (3) alcohol hydrolysis products #gamma#-Fe_2O_3 is first crystallized by contrast to #alpha#-FeOOH, usually produced by deposition from solutions. Further heat treatment of #gamma#-Fe_2O_3 results in production of #alpha#-Fe_2O_3. Conditions for crystallization of Y_3Fe_5O_1_2 and YFeO_3 phases, prepared by both methods, and their crystallite mean sizes are close, but the powders obtained from alcohols are more homogeneous.

Energy Technology Data Exchange (ETDEWEB)

Carbon nanofiber (CNF) supported cobalt oxide composites as high-capacity anode materials were prepared through a facile, effective method for potential use in rechargeable lithium-ion batteries. The effects of the calcining temperature on the crystallinity, grain size, specific surface area of Co{sub 3}O{sub 4} and phase transformation from Co{sub 3}O{sub 4} to CoO were studied in detail. Both the specific surface area and CNF content in CNF-cobalt oxide composites strongly affect the electrochemical performance of these series composites. The CNF-Co{sub 3}O{sub 4} composite with 24.3% CNF pyrolyzed at 500{sup o}C in Ar shows an excellent cycling performance, retaining a specific capacity of 881 mAh g{sup -1} beyond 100 cycles. Homogeneous deposition and distribution of nanosized Co{sub 3}O{sub 4} particles on the surface of CNF can stabilize the electronic and ionic conductivity as well as the morphology of Co{sub 3}O{sub ...

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the co-deposition of chromium and silicon into a 2.25Cr-1.0Mo-0.15C steel, alloy 800, and type 304 stainless steel has been achieved using the pack cementation process. The ferritic coating produced on the 2.25 Cr-1.0Mo steel was approximately 225 {mu}m (9 mils) thick, whereas the inward diffusion of chromium and silicon produced a two-phase structure of ferrite and austenite for type 304. Chromium and silicon were incorporated into the austenitic solid solution upon diffusion into alloy 800. All coatings had approximately 25 to 35 wt% Cr and 2 to 3% Si at the surface. Cyclic oxidation testing in air of the coated 2.25Cr-1.0Mo steel (T = 700{degrees} C) and type 304 (T = 1035{degrees} C) showed a dramatic decrease in the oxidation kinetics compared to the original uncoated alloys. The cyclic oxidation of alloy 800 was also improved.

UK PubMed Central (United Kingdom)

The effects of thiol-specific reagents on the amplitude of the electro-olfactogram (E.O.G.) responses elicited from frog olfactory mucosa by pulses of odorant vapours was studied. The impermeant thiol-specific...Full Text Available

CERN Document Server

Third World Congress on Oxidation Catalysis

International Nuclear Information System (INIS)

Based on the results obtained for C-N and Si-C-N films, a systematic investigation of reactive magnetron sputtering of hard quaternary Si-B-C-N materials has been carried out. The Si-B-C-N films were deposited on p-type Si(100) substrates by dc magnetron co-sputtering using a single C-Si-B target (at a fixed 20% boron fraction in the target erosion area) in nitrogen-argon gas mixtures. Elemental compositions of the films, their surface bonding structure and mechanical properties, together with their oxidation resistance in air, were controlled by the Si fraction (5-75%) in the magnetron target erosion area, the Ar fraction (0-75%) in the gas mixture, the rf induced negative substrate bias voltage (from a floating potential to -500 V) and the substrate temperature (180-350 deg. C). The total pressure and the discharge current on the magnetron target were held constant at 0.5 Pa and 1 A, respectively. The energy and flux of ions bombarding the ...

British Library Electronic Table of Contents (United Kingdom)

This study investigates the applicability of n-type TiO2 and p-type NiO on the FTO-glass (Fluorine doped tin oxide, SnO2:F) substrate of the working electrode in a dye-sensitized solar cell (DSSC). The working electrode was designed and fabricated by depositing a film of TiO2/NiO composite particles, which were prepared by mixing the Ni powder with TiO2 particles using dry mixing method, on a FTO-glass substrate using a spin coating process. The working electrode was then immersed in the solution of N-719 (Ruthenium) dye at a temperature of 70degreeC for 6h. Moreover, a thin film of platinum (Pt) was deposited on the FTO-glass substrate of the counter electrode using an E-beam evaporator. Finally, the DSSC was assembled, and the short-circuit photocurrent, the open-circuit photovoltage and...

Energy Technology Data Exchange (ETDEWEB)

The effective electron mobility was measured as a function of surface field in polysilicon thin film transistors having the following three types of gate dielectrics; silicon dioxide deposited by low temperature (350degC) plasma-enhanced chemical vapor deposition (PECVD), low temperature (400degC) nitrogen-rich PECVD silicon nitride and high temperature (1050degC) thermally grown silicon dioxide. At low surface fields, the maximum true effective electron mobility was 40[+-]3 cm[sup 2] V[sup -1] s[sup -1] in all devices independent of the type of gate dielectric, indicating that the quality of the interface is the same. However, at high surface fields a stronger degradation of the mobility was observed in devices having the thermally grown silicon dioxide as gate dielectric, indicating the presence of surface roughness within the interfacial region. The polysilicon structure was studied by transmission electron microscopy in order to ensure that ...

Science.gov (United States)

We have grown crack-free antiferroelectric (AFE) Pb{sub 0.92}La{sub 0.08}Zr{sub 0.95}Ti{sub 0.05}O{sub 3} (PLZT) films on nickel foils by chemical solution deposition. To eliminate the parasitic effect caused by the formation of a low-permittivity interfacial oxide, we applied a conductive buffer layer of lanthanum nickel oxide (LNO) on the nickel foil by chemical solution deposition prior to the PLZT deposition. Use of the LNO buffer allowed high-quality film-on-foil capacitors to be prepared at high temperatures in air. With the AFE PLZT deposited on LNO-buffered Ni foils, we observed field-induced phase transformations of AFE to ferroelectric (FE). The AFE-to-FE phase transition field, E{sub AF} = 260 kV cm{sup -1}, and the reverse phase transition field, E{sub FA} = 220 kV cm{sup -1}, were measured at room temperature on a {approx}1.15 {micro}m thick PLZT ...

Energy Technology Data Exchange (ETDEWEB)

Nanocrystalline MnO thin film has been prepared by a pulsed laser deposition (PLD) method. The reversible lithium storage capacity of the MnO thin film electrodes at 0.125C is over 472 mAh g{sup -1} (3484 mAh cm{sup -3}) and can be retained more than 90% after 25 cycles. At a rate of 6C, 55% value of the capacity at 0.125C rate can be obtained for both charge and discharge. As-prepared MnO thin film electrodes show the lowest values of overpotential for both charge and discharge among transition metal oxides. All these performances make MnO a promising high capacity anode material for Li-ion batteries. (author)

Energy Technology Data Exchange (ETDEWEB)

A prototype trumpet type nonimaging secondary concentrator has been designed and fabricated for use with the Cummins Power Generation (CPG) 7.5 kW(e) dish-Stirling system and a preliminary set of operating tests has been carried out. The secondary is 26.7 cm (10.5 in.) deep by about 69 cm (27 in.) wide, and has a geometric concentration of 1.7X. The test units were fabricated from polished copper spinnings, overcoated with vapor deposited aluminum and aluminum oxide layers and are water cooled. The basic design considerations are reviewed, the objectives and test procedures for the experiment are summarized and some preliminary results are presented.

Energy Technology Data Exchange (ETDEWEB)

Highly water-repellent surfaces have been prepared from arrayed nanowires of zinc oxide (ZnO) by a treatment with stearic acid. The layers are electrochemically deposited on a nanocrystalline seed layer from an oxygenated aqueous zinc chloride solution. An advancing contact angle (CA) as high as 176{sup 0} is obtained with a very small hysteresis {approx}1{sup 0}. These results, supplemented by infrared spectroscopy, show that the stearic acid forms a very well-packed self-assembled monolayer. The CA measurements show a very good stability of the treated surface even when exposed to harsh conditions or long-term ambient illumination.

International Nuclear Information System (INIS)

In this paper, we report the systematic investigation on the melt characteristics of silicon during laser thermal processing (LTP) of amorphous silicon (a-Si) gates on ultrathin gate oxides. LTP is used to reduce the gate depletion effect in advanced semiconductor devices. The influence of implantation-induced damage and chemical inhomogeneities on the melt behavior of ion-implanted a-Si is studied using in situ time-resolved reflectance (TRR) measurements and ex situ secondary ion mass spectrometry. The results from TRR measurements indicate the presence of a buried melt for a-Si implanted with B"+ at a subamorphizing dose. In contrast, such a melt behavior is not observed during LTP of undoped a-Si and a-Si implanted with As"+ at an amorphizing dose. We attribute the marked difference in the melt characteristics to the competitive effects between compositional inhomogeneities and the extent of amorphization in the a-Si layer. It should be noted that the ...

International Nuclear Information System (INIS)

Zinc oxide thin films were obtained by laser ablation of a Zn target in oxygen reactive atmosphere, the oxygen being supplied either by a standard gas inlet valve or from a radio-frequency (rf) oxygen plasma. Pt-coated silicon and MgO were used as substrates. The influence of the deposition parameters as laser wavelength (266, 355, 1064 nm), laser fluence (1.5-20 J/cm2) and oxygen pressure (1-60 Pa) was studied. The influence of the rf plasma beam addition on the morphological proprieties of zinc oxide films was particularly investigated, simultaneously with several configurations of the direction of the ablation plasma, the rf plasma beam and the substrate. The obtained films, with thicknesses in the range of 50 nm to 1 ?m have been characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM).

Energy Technology Data Exchange (ETDEWEB)

The ability to monitor the corrosion degradation of key components in fossil fuel power plants is of utmost importance for Futuregen and ultra-supercritical power plants. Fireside corrosion occurs in the high temperature sections of energy production facilities due to a number of factors: ash deposition, coal composition, thermal gradients, and low NOx conditions, among others. Problems occur when equipment designed for either oxidizing or reducing conditions is exposed to alternating oxidizing and reducing conditions. This can happen especially near the burners. The use of low NOx burners is becoming more commonplace and can produce reducing environments that accelerate corrosion. One method of addressing corrosion of these surfaces is the use of corrosion probes to monitor when process changes cause corrosive conditions. In such a case, corrosion rate could become a process control variable that directs the operation of a ...

British Library Electronic Table of Contents (United Kingdom)

Ferroelectric thin films such as BST, PZT and PLZT are extensively being studied for the fabrication of DRAMS since they have high dielectric constant. The large and reversible remnant polarization of these materials makes it attractive for nonvolatile ferroelectric RAM application. In this paper we report the characterization of Ba0.7Sr0.3TiO3 (BST) thin films grown by pulsed laser ablation on oxide electrodes. The structural and electrical properties of the fabricated devices were studied. Growth of crystalline BST films was observed on La0.5Sr0.5CoO3 (LSCO) thin film electrodes at relatively low substrate temperature compared to BST grown on PtSi substrates. Electrical characterization was carried out by fabricating PtSi/LSCO/BST/LSCO heterostructures. The leakage current of the heteros...

International Nuclear Information System (INIS)

Coaxial nanocables with a single-crystalline zinc telluride (ZnTe) nanowire core and an amorphous silicon oxide (SiO_x) shell have been synthesized via a simple one-step chemical vapor deposition (CVD) method on gold-decorated silicon substrates. The single-crystal ZnTe nanowire core is in zinc-blende structure along the [111] direction, while the uniform SiO_x shell fully covers the core with no observable pin-hole or crack. Formation mechanisms of the ZnTe-SiO_x nanocables are discussed. The ZnTe nanowire core shows p-type electrical properties while the SiO_x shell acts as an effective insulating layer. The ZnTe-SiO_x nanocables may have potential applications in nanoscale devices, such as p-type FETs and nanosensors.

Energy Technology Data Exchange (ETDEWEB)

Digital control technology using micro-processor is widely used in Factory Automation area since 1980`s. However, the D{sub 2}O Vapour Recovery System in Wolsung 1 N.P.P is controlled by mechanical timer without considering the moisture condition in the Reactor Building and bed temperature, because it was designed using analog technology of 1960`s. This leads to the inefficient system operation and low D{sub 2}O recovery rate in addition to the high internal dose rate of operator. The goal of this phase II study is to develope a optimal automatic controller of D{sub 2}O vapour recovery system using PLC. We developed a control algorithm for Dual Tower Drier, a PLC control program, a operation change program and the monitoring system with a real-time simulator for system verification. (author). 15 refs., 11 figs., 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

A major factor for the achievement of the desirable performance, efficiency and lifetime of flexible organic electronic devices is the optimization of the encapsulation layers that protect the device active layers by atmospheric gas molecule permeation. The active layers consisted of small molecule and/or polymer organic semiconductors as well as the organic conductors need to be encapsulated into a transparent medium that will provide the necessary protection and maintain their charge generation and transport characteristics. The encapsulation layers are generally consisted of inorganic thin films (silicon oxide-SiO{sub x} and aluminium oxide-AlO{sub x}) deposited onto the polymeric substrates, such as PolyEthylene Terephthalate (PET). In this work, in situ and real-time Spectroscopic Ellipsometry in the ultraviolet spectral region has been implemented in order to investigate the growth of inorganic SiO{sub x} and AlO{sub ...

Energy Technology Data Exchange (ETDEWEB)

Alkaline promoted active carbon supported iron catalysts are very active in the oxidative dehydrogenation of ethylbenzene to styrene in the presence of carbon dioxide. The best results were obtained at 550 C for a Li-promoted catalyst with a conversion of ethylbenzene of 75% and a selectivity towards styrene of nearly 95%. These results are better than those obtained with industrial catalysts which perform the dehydrogenation process with an excess of water. The main product of the dehydrogenation reaction with CO{sub 2} was styrene, but the following by-products were detected - benzene and toluene. The selectivity towards toluene was always higher than towards benzene. We observed also the formation of carbon monoxide and water, which were produced with a constant molar ratio of about 0.8. The weight of the catalysts increased up to 20% during the reaction due to deposition of carbon. Using a too large excess of CO{sub 2} (CO{sub 2}/EB>10) ...

International Nuclear Information System (INIS)

The partial pressures of the components (ThCl_4, MCl and MThCl_5) in the saturated vapours of ThCl_4 solutions in molten LiCl, NaCl, KCl, RbCl and CsCl are determined as a function of temperature (900 to 1200 K) and ThCl_4 concentration (2 to 50 mol% ThCl_4) by dynamic method. Thorium tetrachloride volatility is shown to exceed that of alkali chloride from the melts containing less than 98 LiCl or NaCl, 83 KCl, 67 RbCl and 48 mol% CsCl. From experimental observations the decomposition potential of the electrolytes under investigation was estimated in temperature and concentration ranges of our measurements. Under otherwise equal conditions, it increases in the series of alkali chlorides from LiCl to CsCl. (author).

Energy Technology Data Exchange (ETDEWEB)

Two perfluorosulfonic acid membranes, Nafion{sup R} 105 and Nafion{sup R} 115 with the same thickness but different equivalent weights (EW = 1000 g/eq. resp. 1100 g/eq.) were characterised by conductivity measurements at different water vapour activities in the temperature range of 25-70{sup o}C. The results demonstrate that a lower membrane equivalent weight opens the possibility to obtain the needed proton conductivity at lower water vapour activity. This is especially important for those fuel cell applications, in which the cell is operated without external humidification of the fuel gases. (author) 5 figs., 5 refs.

Science.gov (United States)

No abstract prepared.

Science.gov (United States)

The study of the intrinsic behavior of high transition temperature copper-oxide superconductors (HTSC) has proven to be challenging because of the extreme sensitivity of their transport properties on material quality. These compounds are characterized by a high degree of structural and electrical anisotropy, and a very short superconductive coherence length of the same order as the size of the crystalline unit cell (~5-30 A). As a result, microscopic defects such as oxygen vacancies, cationic disorder, and the presence of minute impurities have a significant effect on electrical transport in these materials. Therefore, much effort has been expended in synthesizing sizable samples that are homogeneous, well characterized, and emenable to the study of the anisotropic properties of the HTSC. We have demonstrated that thin films of HTSC compounds such as rm YBa_2Cu_3O_{7 -delta}, which is a 92 K superconductor, can be synthesized easily by a technique known as pulsed ...

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A zinc-air battery using zinc regeneration electrolysis with propanol oxidation as a counter electrode reaction is reported in this paper. It possesses functions of both zincate reduction and electrochemical preparation, showing the potential for increasing the electronic energy utilization. Charge/discharge tests and scanning electron microscopy (SEM) micrographs reveal that when a nickel sheet plated with the high-H{sub 2}-overpotential metal, cadmium, was used as the negative substrate electrode, the dendritic formation and hydrogen evolution are suppressed effectively, and granular zinc deposits become larger but relatively dense with the increase of charge time. The performance of batteries is favorable even if the charge time is as long as 5 h at the current density of 20 mA cm{sup -2}. Better discharge performance is achieved using a 'cavity-opening' configuration for the discharge cell rather than a ...

International Nuclear Information System (INIS)

The article deals with the effects of various hazardous materials in the working environment. Some of these may be detrimental to the safety and health of the worker. The absorption of hazardous substances by the human body is discussed, as well as the effects of toxic substances. The hazardous substances are classified into the following categories: irritants, asphyxiants, anaesthetics and narcotics, carcinogens, mutagens, teratogens, systemic poisons, hazardous particulate matter and the biotransformation of toxic substances. Examples of hazardous substances include: industrial solvents, fumes and vapours, lead, mercury and uranium.

Energy Technology Data Exchange (ETDEWEB)

The effective half-life based on urine bioassay results of Wolsung NPP's worker was calculated. The effective half-life for tritiated water vapour obtained was 5 {approx} 9 days. In comparison to 10 days reported for ICRP-30, it is lower than the corresponding half-life for Reference Man. Also, the half-life was calculated based on intake amount of daily water. According to this result, the metabolism was reviewed.

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

Spent oxide fuels are reduced in a molten salt of CaCl_2-CaF_2 to convert them into metals, then melted in an Fe-U bath disposed in an electrolytic refining vessel and brought into contact with molten Mg, to extract transuranium elements and rare earth elements contained in the Fe-U bath as metals in the molten Mg. Then molten Mg is removed and the residue is brought into contact with KCl-LiCl molten salt and electrolyzed using the Fe-U as an anode. Then, uranium is recovered by deposition on an iron cathode disposed in chloride electrolytes of the electrolytic refining vessel. Uranium and transuranium elements can be thus separated and, for example, depleted uranium for use in blanket fuels can be recovered easily. This can greatly reduce the temporary storage amount of depleted uranium, to eliminate requirement for a large-scaled facility used exclusively for storing uranium and long time management for uranium. (T.M.).

Science.gov (United States)

A new method, near-infrared laser desorption/ionization aerosol mass spectrometry (NIR-LDI-AMS), is described for the real time analysis of organic aerosols at atmospherically relevant mass loadings. Use of a single NIR laser pulse to vaporize and ionize particle components deposited on an aluminum probe results in minimal fragmentation to produce exclusively intact pseudomolecular anions at [M-H](-). Limits of detection (total particulate mass sampled) for oxidized compounds of relevance to atmospheric primary and secondary organic aerosol range from 89 fg for pinic acid to 8.8 pg for cholesterol. NIR-LDI-AMS was used in conjunction with the University of Vermont Environmental Chamber to study secondary organic aerosol (SOA) formation from ozonolysis of limonene at total aerosol mass loadings ranging from 3.2 to 25.0 ?g m(-3) and with a time resolution of several minutes. NIR-LDI-AMS permitted direct delineation between gas-phase, homogeneous ...

Energy Technology Data Exchange (ETDEWEB)

Combustion of extremely fuel-rich ({phi}=4) methane/air mixtures at elevated pressures is investigated as a potential means to generate molecular hydrogen by non-catalytic partial oxidation. This system is investigated both computationally and experimentally. The computations use a perfectly-stirred reactor model and an explicit methane cool-flame mechanism to investigate the effects of reactor parameters on reaction time and product composition. Under adiabatic conditions, such mixtures are predicted to autoignite at low temperatures {approx}700 K for pressures exceeding 8.5 atm. Above 15 atm, conversion to products is complete in roughly 1 s. The dependence of reaction time and hydrogen yield is investigated as a function of inlet temperature, system pressure, and flame equivalence ratio. Actual product yields are measured in a tube reactor facility, and many of the predictions of the model, including long relaxation times to chemical equilibrium and temperatures ...

Energy Technology Data Exchange (ETDEWEB)

Proof-of-principle experiments are reported for a new concept in electrically rechargeable zinc-air battery. The zinc electrode is a porous flow-thru type using a copper foam metal substrate with zinc deposition onto the foam metal from concentrated zincate electrolyte (as used in zinc-slurry type batteries). The bifunctional air electrode employs low-cost materials, being fabricated entirely from carbon-based precursors and small amounts of nickel and/or cobalt oxide. Corrosion measurements on the graphite materials in the air electrode indicate sufficient corrosion resistance for 8000 h life on charge. A prototype single cell was constructed having 1.5 Ah capacity producing 1.2 V discharge -2.0 charge at the three hour rate and has produced stable voltages for more than 150 cycles. Based on the 1.5 Ah prototype characteristics, design calculations for a 32 kWh battery project an energy density of about 110 Wh/kg, peak power density of 140 ...

International Nuclear Information System (INIS)

The growth of epitaxial MnO(100) and MnO(111) layers on Pd(100) surface has been investigated by spot-profile analysis low-energy electron diffraction, dynamic atomic force microscopy, photoemission and high-resolution electron energy loss spectroscopy, and density functional theory. We have found that despite the large lattice mismatch to the Pd(100) substrate, the MnO(100) layers are kinetically stabilized at low temperatures (?350 deg. C) and at oxygen pressures between 2x10-7 and 5x10-7 mbar. Annealing in ultrahigh vacuum at 650 deg. C or, alternatively, deposition of manganese metal in oxygen pressure -7 mbar causes the transformation of the MnO(100) to a polar MnO(111) surface, which is decorated by triangular pyramids with (100) side facets. It is suggested that the growth of MnO(111) layers is energetically preferred over MnO(100) due to the epitaxial stabilization at the metal-oxide interface.

Energy Technology Data Exchange (ETDEWEB)

This report discusses the development of transition metal oxide semiconductors for photoelectrolysis of water. More specifically, it involves preparation of TiO/sub 2/ films by sputtering and evaluating their physicochemical characteristics primarily as they relate to the behaviour of the films as photoanodes. Impedance, photoelectrochemical, and photoconduction properties of TiO/sub 2/ films sputtered in pure O/sub 2/ onto heated substrates have been determined as a function of O/sub 2/ pressure during sputtering, film thickness, Pt overcoating, and cathodic treatment. The capacitance data before cathodic treatment are of the form expected. The capacitance is essentially independent of potential, while for potentials increasingly cathodic of this value, the capacitance increases very rapidly. Cathodic treatment alters the impedance characteristics of the films but leads to either no detectible change in their photoelectrochemical properties or to an increase in ...

Energy Technology Data Exchange (ETDEWEB)

Chemical-looping combustion is a promising technology for the combustion of gas or solid fuel with efficient use of energy and inherent separation of CO{sub 2}. Chemical-looping combustion of methane with calcium sulfate as a novel oxygen carrier was conducted in a laboratory scale fixed bed reactor. The effects of reaction temperature, gas flow rate, sample mass, and particle size on reduction reactions were investigated and an optimum operating condition was determined. The results show that this novel oxygen carrier has a high reduction reactivity and stability in a long-time reduction/oxidation test. The conversions of CH{sub 4} increased with a higher temperature, smaller gas flow rate, larger sample mass and smaller particle size. The suitable reaction temperature seems to be around 950 deg. C. Low temperatures lead to a low CH{sub 4} conversion, but a significant SO{sub 2} formation was observed at a higher temperature. The release of SO{sub 2}, CO, H{sub 2} ...

Energy Technology Data Exchange (ETDEWEB)

As the first step for development of the corrosion resistant superheater tube materials of 500 C, 100 ata used in high efficient waste-to-energy plants, field corrosion tests of six conventional alloys were carried out at metal temperatures of 450 C and 550 C for 700 and 3,000 hours in four typical Japanese waste incineration plants. The test results indicate that austenitic alloys containing approximately 80 wt% [Cr+Ni] show excellent corrosion resistance. When the corrosive environment is severe, intergranular corrosion of 40{approximately}200 {micro}m depth occurs in stainless steel and high alloyed materials. It is confirmed quantitatively that corrosion behavior is influenced by environmental corrosion factors such as Cl concentration and thickness of deposits on tube surface, metal temperature, and flue gas temperature. The excellent corrosion resistance of high [Cr+Ni+Mo] alloys such as Alloy 625 is explained by the stability of its protective ...

International Nuclear Information System (INIS)

This study was carried out mainly to produce uranium trioxide (UO_3), matching standard commercial specification from rock phosphate deposits in Uro and Kurun at eastern part of the Nuba Mountains. A simplified hydrometallurgical procedure has been adopted for production of yellow cake from the ore. The powdered ore sample was leached with concentrated H_2SO_4 acid with and without addition of KCIO_3 as an oxidant. The crude yellow cake was precipitated from the resulting green solution of phosphoric acid as Na_2U_2O_7 and (NH_4)_2U_2O_7 and subsequently purified by TBP extraction (tributylphosphate) and hydrogen peroxide as UO_4.2H_2O. TBP purified product was dried and calcined to UO_3 whereas UO_4.2H-2O was dried and reduced to UO_3 by Na_2S_2O_3. Prior to precipitation of crude yellow cake, Fe in the phosphoric acid solution was precipitated using magnesia. Elemental analysis has shown that the ore is rich in Ca and deficient in elements of ...

International Nuclear Information System (INIS)

Transparent aluminum doped zinc oxide (ZnO:Al, AZO) conducting thin films with a high-preferential c-axis orientation were synthesized using a new sol-gel formula. The films were deposited using a spin-coating route onto borosilicate glass substrates. We used propylene glycol methyl ether (PGME) as the solvent in place of ethylene glycol monomethyl ether (EGME), which is commonly used because it is easier to deposit onto the substrates. PGME is also superior in terms of health and safety. PGME solvent does not need to settle for several days before use and can be spin-coated as soon as the raw material and solvent are mixed. The effects of this novel solvent on the structural, morphological, electrical and optical properties are discussed using XRD, SEM, a four-point probe and UV-VIS spectrophotometry. It was found that the films produced with PGME showed a high-preferential c-axis orientation and compact microstructure in ...

International Nuclear Information System (INIS)

This study was carried out mainly to produce uranium trioxide (UO_3), with the standard of commercial specifications from rock phosphate deposits in eastern part of Nuba mountains, south Kurdufan state. A simplified hydrometallurgical procedure has been adopted for production of yellow cake from the ore. Elemental analysis has shown that the ore is rich in Ca and deficient in elements of potential interest such as Fe, Cu and Zn. Uranium content in ore, phosphoric acid and purified yellow cake (UO_3) obtained with different precipitants was analyzed using alpha-spectrometry. On the average, the activity concentration of uranium in ore corresponds to 82 #+-# 24 ppm (0.10%). From the data of pregnant liquor, it was observed that the addition of KCIO_3 as an oxidant improves the dissolution of uranium from the ore by almost 20%. Data has also indicated that the yellow cake purified by hydrogen peroxide has higher concentration of uranium by 44.5% ...

Energy Technology Data Exchange (ETDEWEB)

We report on studies of device degradation in organic photovoltaic devices based on blends of poly(3-hexylthiophene) (P3HT) and [6,6]-phenyl C61-butyric acid methyl ester (PCBM). Since delamination, oxidation, and chemical interactions at the metal electrode/organic interface have long been posited as degradation pathways in organic electronic devices, we first investigated the stability of a variety of electrodes for devices stored in an inert, dark environment. Second, a set of experiments was designed to separate the effects at the metal/organic interface from the degradation of the active layer or the hole extraction interface. To do this, Ca/Al electrodes were deposited to complete half of a substrate's devices, and samples were left both under constant illumination and 10% illumination (10% duty cycle of 1 sun illumination) in a glovebox environment. After more than 200 h of measurement, additional electrodes were ...

Energy Technology Data Exchange (ETDEWEB)

Both the sign and magnitude of residual stress can vary with the thickness of sputter deposited films. The origins of this behavior are not well understood. In this work, the authors consider the correlation between the residual stress behavior and the depth dependence of impurities in thin (2.5 nm--150 nm) sputtered Mo and Ta films. They also consider the effects of phase transformations and microstructural changes on the stress behavior. Films were deposited onto Si substrates with native oxide. The residual stress observed in the Mo films varied from highly compressive at 2.5 nm film thickness to {approximately}0 at 10 nm thickness. Ta films also exhibited a high compressive stress, which relaxed from highly compressive to tensile between 10 nm and 50 nm film thickness. Impurities in the films may originate from the sputtering targets, the background gases, and the substrate surfaces. Auger Electron Spectroscopy (AES) ...

International Nuclear Information System (INIS)

Nanometre-sized materials, like nanowires, nanoparticles or nanobelts, are gaining huge interest as building blocks of modern electronic nanodevices. Their fabrication feasibility has been demonstrated in the last years, and different routes are already well established in order to synthesize these materials. However, the assessment of their electrical properties is still a challenging issue, due to the difficulty to perform a precise nanolithography process allowing the access to such small structures. The fabrication of metallic contacts with precision in the nanometre range is necessary, as well as achieving a flexible system that allows to contact individual structures. Such a system could be a dual-beam Focused Ion Beam instrument, which combines Scanning Electron Microscopy (SEM) and Focused Ion Beam (FIB) in one machine, able to assist deposition of materials with nanometre precision. In this work, the methodology of fabrication of metallic nanocontacts to ...

Energy Technology Data Exchange (ETDEWEB)

The corrosion properties of sputtered molybdenum and molybdenum silicide films in hydrochloric acid (HCl) have been studied by means of potentiodynamic measurements. Contributions from the substrate to the corrosion behaviour was avoided by depositing the films on inert aluminium oxide (Al{sub 2}O{sub 3}). The compositions studied were Mo, MoSi{sub 0.58}, MoSi{sub 1.04}, MoSi{sub 1.4} and MoSi{sub 1.9-2.1}. Characterisation of the samples was made by X-ray diffraction (XRD) and scanning electron microscopy (SEM) before and after corrosion. X-ray photoelectron spectroscopy (XPS) and Auger electron spectroscopy (AES) were used to analyse the polarised films. Corrosion of Mo{sub 3}Si was found in the molybdenum-rich samples (MoSi{sub 0.58}) containing the two phases Mo{sub 3}Si and Mo{sub 5}Si{sub 3}. Polarisation curves for these films showed one passivation peak at 228 mV vs. the saturated calomel electrode (SCE). The MoSi{sub 1.9-2.1} films had ...

Science.gov (United States)

A critical review of the literature revealed no experiments on uranyl ion transfer from an aqueous to a tributyl phosphate phase which positively measured the kinetics of the chemical reaction at the interphase. Drawing isorhythmic lines on a three component diagram gives a complex correlation for the compaction of three sizes of glass beads. Neither the use of thoria sols nor high feed solution concentrations of thorium nitrate gave any significant increase in mean particle diameters over those obtained from nitrate solutions of lower concentrations in flame denitration. A hydraulic film resistance has been detected in the anion exchange of uranyl sulfate into Dowex 2lK, and chloride elution was found to give a higher apparent uranium diffusion coefficient than nitrate elution. The rate of dissolution of mixed thorium-uranium oxides was determined as a function of the per cent of mixed oxides dissolved. Mixing in ...

Energy Technology Data Exchange (ETDEWEB)

We report for the first time about a micromachined mass flow sensor directly integrated between the double guidance and the needle seat into the body of a Common Rail (CR) injection nozzle. The thermal measurement principle was chosen because gaseous as well as liquid mass flows can be determined fast and precisely. Additionally, with glass-ceramic materials fabricated in a low cost batch process, a high temperature and especially pressure stable substrate can be used. The flow sensitive thin film is realized by an e-beam evaporated 110 nm thick molybdenum (Mo) layer. The latter is electrically characterized by the resistivity of {rho} = 8.2 x 10{sup -7} {omega} m ({+-}2%) at room temperature as well as by the first {alpha}=4.5 x 10{sup -4} K{sup -1} ({+-}5%) and second {beta}=3.0 x 10{sup -6} K{sup -2} ({+-}12%) temperature coefficients of resistance up to 300 C. The static temperature field at and around the thin film sensor on the glass-ceramic substrate is investigated with an IR ...

Energy Technology Data Exchange (ETDEWEB)

Out of concern for the global environment, technologies for coal-fired combined cycle power generation are under development throughout the world today, aiming at highly efficient use of coal. Under these circumstances, the authors and others, with the intention of producing a coal-fired combined cycle power generation system with higher plant efficiency, lower construction cost, and higher reliability than conventional systems, proposed a new gasification combined cycle power generation system that differs from the conventional IGCC system. The authors studied system configuration and conducted elementary research necessary for implementing the system. This report deals with the basic concepts of the system and the results of basic studies carried out to realize of the concepts, including a study on alkali metal vapour concentration in relation to heat corrosion; the relation between gas de-dusting temperature and gas alkali metal vapour ...

International Nuclear Information System (INIS)

The structural ordering of oxygen deficient and Co-doped YBCO (YBa_2Cu_3_-_yCo_yO_6_+_x) have been studied experimentally, and by computer simulations of the oxygen ordering in the basal plane of the structure. The calculations are based on the two-dimensional ASYNNNI model and its modifications. Good agreement is established between the ASYNNNI calculations and the experimentally observed structural properties of the double cell ortho-II structure and the oxygen disordering process from Co-doping into the basal plane. A model that relates the superconducting transition temperature T_c(x) of undoped YBCO and T_c(y) of Co-doped YBCO to the formation of specific domains of the two orthorhombic ordered oxygen phases, ortho-I and ortho-II, shows a close agreement with experimental T_c(x) and T_c(y) data of samples prepared under equilibrium conditions. The structural changes as a result of metal ion substitutions and oxidation/reduction processes have been studied by ...

Energy Technology Data Exchange (ETDEWEB)

The reaction of RbC/sub 24/ with C/sub 6/D/sub 6/ vapour was studied by neutron diffraction on a time scale of 5 min/spectrum. As for the reaction of KC/sub 24/, a second stage phase RbC/sub 24/(C/sub 6/D/sub 6/)sub(y) is initially formed and subsequently transformed into a first stage phase. Model calculations indicate that the benzene rings are canted against the graphite planes both in the first and in the second stage phase.

International Nuclear Information System (INIS)

The reaction of RbC_2_4 with C_6D_6 vapour was studied by neutron diffraction on a time scale of 5 min/spectrum. As for the reaction of KC_2_4, a second stage phase RbC_2_4(C_6D_6)sub(y) is initially formed and subsequently transformed into a first stage phase. Model calculations indicate that the benzene rings are canted against the graphite planes both in the first and in the second stage phase. (Auth.).

International Nuclear Information System (INIS)

Tritium is produced in large quantities at heavy water nuclear power reactors via the neutron activation reaction "2H(n,#gamma#)"3H. At Wolsung nuclear power plant which has a CANDU reactor, the tritium concentrations in coolant and in moderator systems are 1.5 Ci/Kg-D_2O and 35 Ci/kg-D_2O, respectively, after 12 years of operation. The airborne tritium concentration in main access area is normally less than 5 MPCa except short-term peaks. The average tritium concentrations in main access controlled areas are normally less than 100 MPCa. Tritium is mainly present in the air of workplace of CANDU reactors as a tritiated water vapour. Airborne tritiated water vapour enters the workers body via inhalation and absorption through skin and can result in a significant dose. The occupational doses from tritium at Wolsung NPP have been maintained below 1 man-Sv per year so far. The tritium contribution to the total plant man-Sv changes between 30 ...

UK PubMed Central (United Kingdom)

The oxidative stress theory of aging predicts that manipulations that alter oxidative stress/damage will alter aging. The gold standard for determining whether aging is altered is lifespan,...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Short communication.

International Nuclear Information System (INIS)

Short communication.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... wood, kitchen wastes, and human faeces with the ash from such burning deposited and retained in an ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In order to apply chemical-looping combustion to a practical power plant, carbon deposition on the solid particle is one of the key problems to be overcome. Six kinds of solid particles were examined to clarify the kinetic behavior of carbon deposition. The effects of the solid composition, feed gas composition, and reaction temperature on carbon deposition were investigated by thermogravimetrical reactor on the basis of NiO/YSZ particle. From the viewpoints of both reactivity and resistance against carbon deposition, the particle of NiO mixed with YSZ (i.e., yttria-stabilized zirconia) was found to be a good candidate for chemical-looping combustion. It has been observed that carbon deposition could be completely avoided with very low concentration of water vapor. By means of a proposed model, the condition that carbon deposition would be avoided was ...

International Science & Technology Center (ISTC)

Development of Method and Technical Project of the Plant for Thermo-Vacuum Desorption of Tritium Oxide (HTO) from the Environmental Samples

Energy Technology Data Exchange (ETDEWEB)

Chemical oxidation is a treatment technology that uses powertul chemical oxidizers to destroy organic contaminants. Typical oxidizers used in chemical oxidation processes include ozone, hydrogen peroxide, chlorine, and potassium permanganate. The chemical reaction products are usually simple organic compounds, such as carboxylic acids, and/or inorganic compounds, such as carbon dioxide, water, and simple inorganic complexes (e.g., chloride salts, in the case of chemical oxidation treatment of chlorinated solvents).

International Nuclear Information System (INIS)

Energy deposition process by relativistic fast electrons produced by ultra-intense laser pulses is discussed. The process is calculated with a two dimensional Fokker-Planck simulation code including binary and collective collisions coupled with electromagnetic field. We focused on Velocity Distribution Function (VDF) dependence in the simulation. The results show that the spread angle of the fast electrons distribution affects energy deposition area and deposited energy is concentrated in the vicinity of the propagation axis of the fast electrons. It may be also suggested that self-pinch effect of a fast electron beam causes large deposition energy. (author)

Energy Technology Data Exchange (ETDEWEB)

Results are given for deep-level petroleum and gas drilling probes in various coastal zones of Southern Sakhalin covering the Poronai depression and the Aniv Bay trough. The exploratory probes indicate that the Middle Miocence deposits of the Boundary trough contain commercial-size deposits of petroleum, that commercial-size gas deposits are in the upper Myocene deposits of the Aliv Bay trough, and that the upper Cretaceous and Cenozoic deposits of the eastern section of Southern Sakhalin lack folded deformations. 7 references, 2 figures.

Energy Technology Data Exchange (ETDEWEB)

The understanding of fission product deposition in realistic steam generator conditions is needed for release estimates in PSA studies, and for the design of efficient accident management procedures. This is considered very important because primary-to-secondary leakages risk dominant sequences in many plants. Furthermore, the decay heat of the fission product deposits adds to the thermal load to the steam generator tubes also in other sequences, especially in case of cold leg leakages. This brings out the concern of induced steam generator tube ruptures in cases, where the steam generators are initially intact. The experimental data showed that the highest deposited fraction within the tubes were found in cases with lowest flow velocities. The minimum value of the deposited fraction was observed at intermediate flow velocities. With these relatively low Reynolds numbers, the results calculated with ...

British Library Electronic Table of Contents (United Kingdom)

Oxidation of propylene with oxygen, air and a mixture of nitrogen?oxygen in a barrier discharge is investigated. The selectivity towards formation of propylene oxide in pure oxygen is shown to be as high as 45 wt% and the propylene conversion ratio is found to be 12.9 wt%. In the oxidation with air, the propylene oxide selectivity is 23 wt%, while the conversion is 7.5 wt%. The values of propylene conversion and selectivity towards formation of propylene oxide in a barrier discharge are consistent with those obtained by the thermocatalytic methods for production of propylene oxide.

British Library Electronic Table of Contents (United Kingdom)

In this paper we demonstrate the electrodeposition of nickel, a common ferromagnetic material, in various magnetically desirable shapes including nanowires, nanoparticles and highly faceted shells. In order to obtain three dimensional mesostructures, the electrochemical deposition of nickel was performed on highly oriented pyrolytic graphite (HOPG) under different electrolyte composition and deposition potential conditions. Under potentiostatic deposition at one distinct potential negative with respect to the reversible potential of nickel, three stages of nucleation and growth take place leading to a complex morphology of deposits. However, dual-pulse potential deposition and electrodeposition in low pH solutions causing hydrogen evolution, lead to nickel deposits in the form of nanowires...

Science.gov (United States)

The identification and characterization of carbonaceous materials (CMs) that control hydrophobic organic chemical (HOC) sorption is essential to predict the fate and transport of HOCs in soils and sediments. The objectives of this paper are to determine the types of CMs that control HOC sorption in the oxidized and reduced zones of a glacially deposited groundwater sediment in central Illinois, with a special emphasis on the roles of kerogen and black carbon. After collection, the sediments were treated to obtain fractions of the sediment samples enriched in different types of CMs (e.g., humic acid, kerogen, black carbon), and selected fractions were subject to quantitative petrographic analysis. The original sediments and their enrichment fractions were evaluated for their ability to sorb trichloroethene (TCE), a common groundwater pollutant. Isotherm results and mass fractions of CM enrichments were used to calculate sorption contributions of ...

International Nuclear Information System (INIS)

Gabal Ralal is one of the major asymmetrical doubly- plunging anticlinal fold belts (50 Km length) related to the Syrian Arc System in northern Sinai, Egypt. The exposed rock units at Gabal Ralal range from Cretaceous to Quaternary and are divided into eight formations which are from base to top: Malha, Ralal, Wata, Themed, Sudr, Beida, Egma and Quaternary wadi deposits. The image processing is applied using Landsat-7 satellite data to discriminate structure and lithology for defining the horizons of the radioactive anomalies of each rock unit. The extracted structural lineaments, using Ge Analyst-PCl package, from digital ETM data showed that the main structural trends are NE-SW and NW-SE normal faults which originated as extensional fractures with lateral dip-slip displacement. The axial trace of Gabal Ralal fold is curved and plunging to Wand SW directions while the northeastern part (Gabal Dalfa) is plunging to NE direction. The use of remote sensing data and ...

International Nuclear Information System (INIS)

In this work, a focused ion beam (FIB) milling process has been developed to fabricate 50 nm Bi nanowire and transistor structures using FEI-200 dual beam FIB system. For the fabrication, 50 nm bismuth film was thermally evaporated through EBL patterned PMMA windows onto SiO_2 substrates with pre-defined contact pads. Bi nanowire widths ranging from 30 nm to 100 nm have been successfully fabricated by milling out unwanted areas using 30 KeV Ga+ ion beam. A single-pixel-line ion beam blanking technique has been utilised to fabricate Bi nanowire as small as 30 nm in diameter and few micrometers long. In order to form good ohmic contacts for sub 50 nm bismuth nanowires, a drill-and-fill process has been developed using FIB to sputter away the surface oxide of bismuth after the in-situ platinum nanowire contacts deposition. To our knowledge, this is the first time a focused ion beam process has been used to fabricate bismuth nanowire. The ...

International Nuclear Information System (INIS)

Transient enhanced diffusion (TED) and dose loss (pile-up) are investigated for phosphorus-implanted samples covered with both oxide and nitride films. P ions were implanted into p-type (1 0 0) CZ-Si (dose 5x10"1"3 cm"-"3, 100 keV) through a chemical vapor deposition (CVD) Si_3N_4 film. For a half of samples, Si_3N_4 was etched off and SiO_2 films were grown by CVD. Both samples were annealed for 20-360 min at 700 deg. C. Diffusivity of P and the dose loss were estimated based on the secondary-ion mass spectrometry (SIMS) P profiles. Both Si/Si_3N_4 and Si/SiO_2 interfaces were investigated with transmission electron microscopy (TEM) and electron energy-loss spectroscopy (EELS). There is no significant difference in P diffusivity between the SiO_2 and Si_3N_4 films for the present annealing condition of 700 deg. C for 20-360 min. Regarding dose loss, a distinct different behavior was observed. In case of the SiO_2 cover film, amount of dose ...

Energy Technology Data Exchange (ETDEWEB)

The goal of this paper is to explore how compliance with the Clean Air Act Amendments of 1990 (CAAA), especially Title IV and emission trading under it, will affect the current relationship between state and federal regulation. It is difficult, with the limited experience we have had under Title IV, to be definitive about or to be a very strong advocate of too many policy positions. What may be most helpful at this point is to identify where the difficult issues in state/federal relations might arise; and then to explore ways in which tensions might be either avoided or resolved. One anticipated conclusion is that a traditional regulatory mindset could be very destructive if applied to this new area of oversight without due sensitivity to what Congress is trying to achieve in Title IV. That concern pervaded the early legislative debates; and it persists today. Title IV presents some unique challenges to state regulators and will require some creative solutions and fresh thinking if the ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical oxidation as a method to destroy drug residues like Aspirin {sup trademark}, tetracycline or gentamicin in water was investigated with C-Anode (modified by manganese oxides) and Pt Anode. The mechanism of Aspirin {sup trademark} and tetracycline oxidation and the influence of the biocide effect was observed using GC-MS and three different microbiological tests. In general the biological availability increases with progressive oxidation of the antibiotics. (orig.)

British Library Electronic Table of Contents (United Kingdom)

In this study, wood samples were exposed to light irradiations (direct sunlight, xenon lamp, mercury vapour lamp) and thermal treatments were carried out in dry- and in humid conditions at 90degreeC. One part of the samples was covered by an aluminium plate during light irradiation. The samples under the aluminium plate also suffered considerable chemical changes, monitored by infrared technique and colour measurement. The sunlight produced greater colour change under the aluminium plate than the artificial light sources. During light irradiation, the carbonyl band having two maximum at 1700 and 1746cm-1 increased and the peak of the aromatic skeletal vibration arising from lignin (1510cm-1) decreased together with the guaiacyl vibrations at 1275cm-1. There was absorption decrease at 1174c...

International Nuclear Information System (INIS)

Autoionizing and Auger transitions in atomic manganese and samarium have been experimentally investigated by observation of the ejected electrons in the energy region 0 to 40 eV following electron impact excitation with incident beams in the energy range 15-500 eV. Seventy-four spectral features are tabulated for manganese and a number of new assignments have been made based on pseudo-relativistic Hartree-Fock calculations and quantum defect analysis. A similar study of samarium reveals only a number of broad features in the ejected-electron energy range 8-10 eV. Three features have been observed consistently in the ejected-electron spectrum of samarium and assigned by comparison with previous work. (author).

International Nuclear Information System (INIS)

When operating a nuclear power plant the necessity arise to eliminate various defects of building constructions, to seal joints and transitional elements. The authors present data concerning the production of a sealing composition made of epoxy resin and used for NPP premises of emergency location. Analytical relations are presented between the properties of the composition (adhesion strength, water absorption and others) and its structure. Physical, mechanical and thermal properties and structural peculiarities are determined in the process of interaction between the filling and binding agents. The composition sustains sealing properties under environmental conditions at he presence of an air - vapour mixture with 160 degrees C"o temperature and 0.3 MPa surplus pressure. (author).

Energy Technology Data Exchange (ETDEWEB)

The Eddy covariance technique allows to measure different components of turbulent air fluxes, including the flow of water vapour. Sap flux measurements determine directly the water flow in tree stems. We compared the water flux just above the crowns of trees in a forest by the technique of Eddy covariance and the water flux by the xylem sap flux method. These two completely different approaches showed a good qualitative correspondence. The correlation coefficient is 0.8. With an estimation of the crown diameter of the measured tree we also find a very good quantitative agreement. (author) 3 figs., 5 refs.

Energy Technology Data Exchange (ETDEWEB)

This paper presents the application of artificial neural networks to adiabatic flame temperature prediction of hydrocarbon fuels. The investigation was conducted over a wide range of operating conditions in terms of fuel composition, pressure and temperature of reactants, fuel-air equivalence ratio and fuel vapour fraction. Several neural network models for predicting the flame temperature for different applicable fuel ranges were built and examined. The proper preparation of network training data and the appropriate choice of network parameters for achieving better prediction accuracy are discussed. The neural network prediction results were compared with those calculated by a thermodynamic and chemical equilibrium-based computer code - the NASA program CET89. It was shown that trained neural network models can provide the adiabatic flame temperature prediction with a good level of accuracy over a wide range of operating conditions. 16 refs., 5 figs., 1 tab.

Science.gov (United States)

Analytical relations are obtained for estimating how the distributions of temperature and heat flux vary along a steam-generating tube and how the steam-generator power output reduces due to formation and accumulation of deposits.

CERN Document Server

Residual Stresses in Ta, Mo, Al and Pd Thin Films Deposited by E-Beam Evaporation Process on Si and Si/SiO 2 Substrates

Energy Technology Data Exchange (ETDEWEB)

Pulsed laser deposition (PLD) is known for its capacity to reproduce a target composition on a substrate. The authors have used this deposition technique to produce thin films of transition metal chalcogenides. However, the deposits were always deficient in Te relative to the starting material (composed by a refractory metal (niobium) and a chalcogene (tellurium)). Variations of the interreticular distances have been observed with respect to fluence and substrate temperature. The authors show that spatial composition of the films is determined by a degree of crystallinity of deposit and by the reaction of formation of Te{sub 2} molecule within laser induced plume. Two kinds of deposits have been obtained: Nb{sub 5}Te{sub 4}-type thin films which have a one-dimensional structure and NbTe{sub 2}-type thin films which have a two-dimensional structure. While NbTe{sub 2} films have been ...

International Nuclear Information System (INIS)

The report is divided into six working group discussions on the following subjects: 1) Chemical and physical mechanisms in the formation of uranium mineralization, geochronology, isotope geology and mineralogy; 2) Sedimentary basins and sandstone-type uranium deposits; 3) Uranium in quartz-pebble conglomerates; 4) Vein and similar type deposits (pitchblende); 5) Other uranium deposits; 6) Relation of metallogenic, tectonic and zoning factors to the origin of uranium deposits. Each working group paper contains a short introductory part followed by a discussion by the working group members.

Science.gov (United States)

... analyzer section for angle resolved measurements, and a thin film evaporator with a quartz crystal microbalance to measure the mass deposition. ...

UK PubMed Central (United Kingdom)

The widely accepted oxidative stress theory of aging postulates that aging results from accumulation of oxidative damage. Surprisingly, data from the longest-living rodent known, naked mole-rats [MRs;...Full Text Available

UK PubMed Central (United Kingdom)

Oxidative stress occurs when the level of prooxidants exceeds the level of antioxidants in cells resulting in oxidation of cellular components and consequent loss of cellular function. Oxidative...Full Text Available

Science.gov (United States)

The catalytic effects of copper-aluminium-magnesium oxides in the oxidative coupling of phenylethyne is described. The importance of surface properties as a redox site are discussed.

UK PubMed Central (United Kingdom)

Potato tuber mitochondria oxidizing malate respond to NAD⁺ addition with increased oxidation rates, whereas mung bean hypocotyl mitochondria do not. This is traced to a low endogenous content...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A compact cesium deposition system was used for direct deposition of cesium atoms and ions onto the inner surface of the 1/3 scale Hydrogen Negative Ion Source for the LHD-NBI system. A small, well defined amount of cesium deposition in the range of 3-200 mg was tested. Negative ion extraction and acceleration were carried out both in the pure hydrogen operation mode and in the cesium mode. Single Cs deposition of 3-30 mg to the plasma chamber have produced temporary 2-5 times increases of H-yield, but the yield was decreased within several discharge pulses to the previous steady-state value. Two consecutive 30 mg depositions done within a 3-5 hours/60 shot interval, produced a similar temporary increase of H-beam, but reached a larger H-yield steady-state value. Deposition of larger 0.1-0.2 g Cs portions with a 20-120 hours/150-270 shot interval improved the ...

Energy Technology Data Exchange (ETDEWEB)

The question about expanding the boundaries of the open pit mining method is examined. The use of methods which consider the advantages of open and underground mining operations with their joint use in horizontal and evenly dipping deposits will make it possible to objectively select the mining method, to expand the range of use of open pit mining operations in the deposits of the Far North and provide an improvement in the technical and economic indicators of mineral extraction.

Energy Technology Data Exchange (ETDEWEB)

This report measured the rate of isothermal deposition of sub-micron particles of magnetite onto the surface of Alloy 800 at pH of 4.2-9.3 at Re=10,000 and a fluid temperature of 25C. Deposition is modelled as a two-step process, the transport of particles to the surface region followed by attachment to the surface.

Energy Technology Data Exchange (ETDEWEB)

The theoretical principles underlying the formation of oxide and, in particular, anodic oxide coatings on metals produced by chemical oxidation, anodizing in solutions, and anodizing in cold plasmas are reviewed. The mechanisms and conditions of anodic oxidation are described, and the structure of anodic oxide coatings on aluminum, magnesium, beryllium, zinc, cadmium, iron, cobalt, nickel, titanium, zirconium, tantalum, and chromium alloys is examined. Attention is also given to various applictins of anodized coatings. 54 references.

Energy Technology Data Exchange (ETDEWEB)

The potential use of uranium in the field of catalysis is presented in the first part of this paper. Numerous applications of uranium binary oxides, as well as mixed oxides, are reviewed with a special emphasis on the role of U-Sb-O catalysts in selective oxidation (and ammoxidation) processes. Attempts are made to correlate the electronic structure of uranium, and especially the role that 5f electrons play in bonding, with its promising catalytic properties. In the second part, new data are given for uranium-bismuth mixed oxides in the catalytic oxidation of CO by O/sub 2/. Kinetic tests performed in a flow microreactor allow a mechanism to be proposed that involves the direct participation of lattice oxygen of the catalyst in the chemical process (redox mechanism). The high activity can be related to the ability of uranium to change reversibly its oxidation ...

UK PubMed Central (United Kingdom)

Ethane oxidation was studied in ethane-grown resting cells (mycelia) of an Acremonium sp. and in cell-free preparations of such mycelia. From resting cell experiments evidence was found for a pathway...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This patent describes a catalyst composition. It consists of the catalytic oxides of iron, bismuth, molybdenum and magnesium as essential components and optionally the oxides of cobalt, nickel, phosphorus and arsenic.

Science.gov (United States)

May 31, 2011 ... A Theoretical Solid Oxide Fuel Cell Model for System Controls and Stability Design AUTHOR(S): Kopasakis, George; Brinson, Thomas; Credle, ...

International Nuclear Information System (INIS)

Between December 2001 and May 2004, a ventilation experiment (VE) was performed in the Mont Terri Underground Research Laboratory (URL) and co-financed by the Commission of the European Communities. The objective was to investigate the desaturation of consolidated clay formations in consequence of the ventilation of underground openings of a repository in such a formation. The results of the geoelectric measurements performed in the second phase of the Mont Terri ventilation test can be summarized as follows: Geoelectric tomography has been found suitable for monitoring ventilation-induced saturation changes in the Opalinus clay. During ventilation with dry air a desaturation down to below 50% could be detected in both desaturation cycles. The desaturated zone extends less than 0.5 m into the rock around the microtunnel. During the second resaturation phase, ventilation with humid air led to quick resaturation at the tunnel surface, while resaturation of the rock mass took months. The ...

International Nuclear Information System (INIS)

Understanding the erosion and deposition rates in a small watershed is important for designing soil and water conservation measures. The objective of this study is to estimate the net soil loss and gain at points with various land use types and landform positions in a small watershed in the Sichuan Hilly Basin of China by the 137Cs tracing technique. Among various land use types, the order of erosion rate was bare rock > sloping cultivated land > forest land. The paddy field and Caotu (a kind of cultivated land located at the foot of hills) were depositional areas. The erosion rate under different landform was in this order: hillside > saddle > hilltop. The footslope and the valley were depositional areas. The 137Cs technique was shown to provide an effective means of documenting the spatial distribution of soil erosion and deposition within the small watershed.

Energy Technology Data Exchange (ETDEWEB)

Anti-reflective coatings made with Teflon AF2400 had the highest damage thresholds recorded for physical vapor deposited coatings at the Lawrence Livermore National Laboratory damage facility. Physical vapor deposited layers of Teflon AF2400, a perfluorinated amorphous polymer, maintained the bulk optical properties of a high transmittance from 200 nm to 1600 nm, and a low refractive index. In addition, the refractive index can be intentionally reduced by control of two common deposition parameters, deposition rate and substrate temperature. Scanning electron microscopy and nuclear magnetic resonance observations indicated that morphological changes caused the variations in the refractive index rather than compositional changes. The coatings adhered to fused silica and silicon wafers under normal laboratory handling conditions.

Energy Technology Data Exchange (ETDEWEB)

TiO{sub 2} is a vital material in several technologies including, photocatalysis, gas sensing, biomaterials and optical coatings. Among the several crystal structures of this oxide, rutile has the highest density and microhardness, the highest index of refraction and the highest temperature stability. The processing of dense polycrystalline materials often includes the addition of a liquid-forming phase at higher temperatures. This technique is known as liquid-phase sintering and has been studied extensively. Rutile boundaries containing an amorphous phase have been used to study boundary migration and grain-boundary grooving. Visible-light (VLM), scanning electron (SEM) and transmission electron microscopy (TEM) in addition to electron-backscatter diffraction (EBSD) and a focused-ion beam (FIB) tool were used to characterize boundary migration in rutile. EBSD analysis was carried out on a Philips XL30 FEG SEM equipped with a DigiView 1612 high-resolution, ...

International Nuclear Information System (INIS)

Alloy 800 has been used for steam generator (SG) tubing for more than 30 years, primarily in CANDU reactors and in reactors in Germany. The grade of Alloy 800 tubing used for this service has a controlled Ti/C ratio (#>=#12 for CANDU SGs), and this specification is sometimes termed Alloy 800 M or Alloy 800 NG . There have been very few corrosion-related flaws detected in this material in SG service, and, until recently, no incidences of cracking. There has been extensive R and D carried out on Alloy 800 tubing, both in Canada and elsewhere, under a variety of operating conditions, including shutdowns, which show that it has excellent resistance to corrosion-related degradation under specified and appropriate operating conditions. These R and D findings are reflected in the in-service experience. It has been shown from the R and D that Alloy 800 is susceptible to corrosion under acidic conditions, in particular those that can arise as a consequence of phosphate water treatment or ...

Energy Technology Data Exchange (ETDEWEB)

The liquefaction reaction system of an NEDOL process coal liquefaction 1t/d PSU was opened and checked to investigate the cause of the rise of differential pressure between liquefaction reactors of the PSU. The liquefaction test at a coal concentration of 50 wt% using Tanito Harum coal was conducted, and it was found that the differential pressure between reactors was on the increase. By the two-phase flow pressure loss method, deposition thickness of deposit in pipelines was estimated at 4.4mm at the time of end operation, which agreed with a measuring value obtained from a {gamma} ray. The rise of differential pressure was caused by deposit formation in pipelines connecting reactors. The main component of the deposit is calcite (CaCO3 60-70%) and is the same as the usual one. It is also the same type as the deposit on the reactor wall. Ca in coal ash is concerned with this. To ...

Energy Technology Data Exchange (ETDEWEB)

Ion bombardment during deposition can significantly modify the film properties. In the partially ionized beam deposition, ions derived from the depositing material, i.e., the self-ions, are used during deposition. Cu films were deposited on SiO{sub 2} substrates at room temperature using 1% Cu self-ions with an energy ranging between 0--4 keV. We studied the microstructures of the Cu films using x-ray diffraction and transmission electron microscopy, measured the impurity level inside the films using secondary ion mass spectrometry, and performed the resistivity measurements using a four point probe. The results indicate that there is an optimum ion energy around 2 keV at which, the integrated x-ray intensity ratio {ital I}(111)/{ital I}(200) reaches its maximum value indicating a strong {l angle}111{r angle} texture, while the impurity concentration and resisitivity are minimum. ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

International Nuclear Information System (INIS)

Short communication.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The influence of MeV electrons irradiation on the gate oxide layers of hydrogenated polysilicon thin film transistors (TFTs) was investigated by measuring gate leakage currents and threshold voltages. The experimental data revealed a decrease of oxide trap density and increase of positive oxide charge. Improvement in the interface roughness and in the oxide quality near the bottom interface was observed.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

We report on the fouling of Focused Ion Beam (FIB)-fabricated silicon oxide nanopores after exposure to tap water for two weeks. Pore clogging was monitored by Scanning Electron Microscopy (SEM) on both bare silicon oxide and chemically functionalized nanopores. While fouling occurred on hydrophilic silicon oxide pore walls, the hydrophobic nature of alkane chains prevented clogging on the chemically functionalized pore walls. These results have implications for nanopore sensing platform design.

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

DEFF Research Database (Denmark)

ATPase, endoplasmic reticulum, calcium, ischaemia

International Nuclear Information System (INIS)

By means of ESCA the composition and the thickness of passive films formed on austenitic stainless steels were investigated after the attack of nitric acid at various temperatures and acid concentrations. The outermost layers of the oxide film consist of SiO_2, then a layer rich of Cr-oxid follows, containing also some Mo in the four- and sixvalent state. Ni does not contribute to the oxide film. Cr is also enriched in the metal just below the oxide film. (orig.).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Science.gov (United States)

... AT THE INTERFACE, A THIN OXIDE LAYER IS OBSERVED ALONG WITH POSSIBLE PALLADIUM SILICIDES. PALLADIUM ...

Energy Technology Data Exchange (ETDEWEB)

The effect of sodium on the partial oxidation of methane over MoO{sub 3}-SiO{sub 2} in the presence of molecular oxygen has been investigated. As in the sodium-free case, the major products are formaldehyde, carbon monoxide, carbon dioxide, and water. Kinetic analysis indicates that methane is directly oxidized to formaldehyde and carbon dioxide. Formaldehyde is oxidized to carbon monoxide, which is itself further oxidized, providing an alternative route to carbon dioxide. The kinetic model shows that sodium poisons the direct oxidation of methane to formaldehyde and carbon dioxide, but promotes the oxidation of formaldehyde and carbon monoxide. Model predictions of rates and selectivities are in good agreement with the experimental data. A mechanism that explains both the poisoning and promotion effects of sodium on MoO{sub 3}-SiO{sub 2} is proposed.

Energy Technology Data Exchange (ETDEWEB)

Titanium oxides were grown anodically to selected final potentials on grade II polycrystalline titanium under different anodization rates. XPS and RBS results show that the oxide consists of primarily TiO2 with a non-stoichiometric oxide/metal interface, with the slower growth rate associated with a thicker layer at the interface. Characterization using TEM reveals that the structure of the oxide evolves from a primarily amorphous phase to islands of crystallites in an amorphous matrix, to an entirely crystalline phase by increasing the polarization potential. Slower growth rates tend to remain crystalline at higher potentials. The mechanical strength of oxide films extracted from load-depth data by nanoindentation varies dramatically for oxide films grown by different rates at 9.4 V, and to a lesser extent at lower potentials. The variation of film strength is ...

International Nuclear Information System (INIS)

Synergism has been observed during inhibiting initiated oxidation of styrene or tetralin by organic phosphites in the presence of complex compounds of some transition metals. The results are given of non-additive intensification of antioxidative activity of triphenylphosphite (TPP) and tri-(4-methyl-6-tert.-- butyl)-phenyl-phosphite (TMBP) in the process of initiated oxidation of styrene or tetralin with addition of acetylacetonates of cobalt and vanadyl. During styrene oxidation, inhibition of the reaction with chelate complex of vanadyl is weakened considerably when phosphite is added into the reaction system. During tetralin oxidation, postcatalytic (or branched) oxidation is observed only for large concentration of vanadyl complex. Addition of TPP to above complex sharply increases the induction period. When the induction period is completed, oxidation of ...

Energy Technology Data Exchange (ETDEWEB)

Our goal was a process to convert methane to higher hydrocarbons oxidatively, since this circumvents thermodynamic yield limits of a strictly degydrogenative process. Keller and Bhasin converted thermodynamic yield limits of a strictly dehydrogenative process. Keller and Bhasin converted methane to higher hydrocarbons by using metal oxides as oxidants, without co-fed oxygen. They stated that selectivity is necessarily poor if gaseous oxygen is present. Jones and Sofranko have also used reducible metal oxides as oxidants in a group of their parents, but later used some of those materials with continuous O{sub 2} feed without much loss of selectivity. Baerns, Lunsford and Otsuka have shown that high selectivity could be possible with co-fed O{sub 2} at least for low O{sub 2} partial pressures, over PbO-A1{sub 2}O{sub 3}, Li-MgO and rare earths. The performance of a group of ...

Science.gov (United States)

Data are presented on the insulating properties and capacitance-voltage (CV) characteristics of metal-oxide-semiconductor (MOS) device-thickness (below approx. 100 nm) native oxides formed by wet thermal oxidation of thin InAlP epilayers lattice matched to GaAs. Low leakage current densities of J=1.4 x 10-9 A/cm2 and J=8.7 x 10-11 A/cm2 are observed at an applied field of 1 MV/cm for MOS capacitors fabricated with 17 nm and 48 nm oxides, respectively. TEM images show that the In-rich interfacial particles which exist in 110 nm oxides are absent in 17 nm oxide films. Quasi-static capacitance-voltage measurements of MOS capacitors fabricated on both n-type and p-type GaAs show that the InAlP oxide-GaAs interface is sufficiently free of traps to support inversion, indicating an unpinned Fermi level. These data suggest that InAlP native ...