International Nuclear Information System (INIS)

An improved coating for Advanced Gas Cooled Nuclear Reactor austenitic stainless steel fuel cans is described which, tests have shown, inhibits the deposition of carbon on the cans in carbon-containing ionising radiation environments. The coating comprises a refractory oxide which has been prepared by a vapour phase condensation method, in combination with a noble metal. (U.K.).

International Nuclear Information System (INIS)

A series of ball-on-disc wear and friction measurements were made for surfaces which have a chemical vapour deposition carbon silicon alloy layer on a carbon substrate (fine grain POCO graphite). Nitrogen ion irradiation was used to improve the wear resistance of the carbon alloy surface. For comparison, measurements were also taken for alumina against alumina. It was found that the lowest friction coefficient and lowest wear occurred for ion irradiated coated samples containing 4% Si in the alloy and that the performance was superior to that of alumina. ((orig.)).

Energy Technology Data Exchange (ETDEWEB)

Deposition of hard coatings may influence the mechanical properties of the bulk material and its corrosion resistance. In this work we study the hardness of the coated and the back side of 100Cr6 steel plates. Electrochemical corrosion tests were performed in O{sub 2}-saturated acetate buffer of pH 5.6 at 25degC. Chromium nitride and titanium nitride coatings prepared by different physical vapour deposition processes, such as arc, thermionic arc evaporation, magnetron sputtering and ion-beam-assisted deposition (IBAD) were compared. The results show that, for sufficient corrosion protection, chromium nitride layers have to be thicker than 500 nm. An increased nitrogen partial pressure in the evaporation chamber of the IBAD process improves the corrosion resistance significantly. The hardness of the substrates was reduced in the case of ...

Energy Technology Data Exchange (ETDEWEB)

In this study samples of AISI 4140 steel were pretreated by plasma nitriding and coated with two different physical vapour deposited coatings (TiN and TiAlN). A hardened AISI 4140 sample and a coated sample were also included in the investigation. To examine the influence of the nitrided zone on the performance of the coating-substrate composite, two different nitriding conditions - a conventional 25% N{sub 2} and an N{sub 2}-poor gas mixture - were used. The specimens were investigated with respect to their microhardness, surface roughness, scratch adhesion and dry sliding wear resistance. Wear tests in which the duplex-treated pins were mated to hardened ball bearing steel discs were performed in a pin-on-disc machine under dry sliding conditions. Metallography, scanning electron microscopy and profilometry were used to analyse the worn surfaces in order to ...

International Nuclear Information System (INIS)

A wide variety of thin film coatings, deposited by different techniques and with potential applications in various important areas, have been characterised by the Phase Modulated Spectroscopic Ellipsometer, installed recently in the Spectroscopy Division, B.A.R.C. The Phase Modulated technique provides a faster and more accurate data acquisition process than the conventional ellipsometry. The measured Ellipsometry spectra are fitted with theoretical spectra generated assuming an appropriate model regarding the sample. The fittings have been done objectively by minimising the squared difference (#chi#"2) between the measured and calculated values of the ellipsometric parameters and thus accurate information have been derived regarding the thickness and optical constants (viz, the refractive index and extinction coefficient) of the different layers, the surface roughness and the inhomogeneities present in the layers. Measurements have been done ...

International Nuclear Information System (INIS)

Complete text of publication follows. According to the new European regulations (Restrictions of Hazardous Substance Directive), there is an emerging demand for environmental friendly metal treatments instead on formerly used chromate conversion coating technique. The aim of the present investigations was to characterise and compare silicon containing protective thin layers on roughened galvanized steel surfaces (with average roughness of 0.7 microns), using FTIR microscopy and imaging techniques. The silicon containing coatings were produced either by Chemical Vapour Deposition (CVD) or by wet chemical treatment using liquid silane. FTIR techniques offer new possibilities in the characterisations and chemical mapping of differently coated thin films, besides SEM+EDS, AFM, nanoindentation, XPS measurements (P. Nemeth et al., Materials Science Forum, 589 (2008) 433-438). All ...

International Nuclear Information System (INIS)

The paper describes the production of highly enriched isotopes of uranium, plutonium, americium and curium by electromagnetic separation for scientific and applied researches in physics, chemistry, geology, medicine, biology and other fields. Using the equipment described, the isotopes are produced in quantities sufficient to set up nuclear physical experiments, to produce nuclear reference materials and standard sources for calibration of radiometrical and mass spectrometrical equipment, in radionuclide metrology, etc. For the following isotopes the indicated degrees of isotopic enrichment were achieved: "2"3"3U-99.97%; "2"3"5U-99.97%; "2"3"6U-98.0%; "2"3"8U-99.997%; "2"3"8Pu-99.6%; "2"3"9Pu-99.9977%; "2"4"0Pu-99.9-100%; "2"4"1Pu-96.998%; "2"4"2Pu-97.8-99.96%; "2"4"4Pu-96.7%; "2"4"1Am-99.6%; "2"4"2"mAm-73.6%; "2"4"3Am-99.2-99.94%; "2"4"3Cm-99.99%; "2"4"5Cm-99.998%; "2"4"6Cm-99.8%; "2"4"7Cm-90%, "2"4"8Cm-97%. Methods for preparing layers of highly enriched isotopes on various ...

International Nuclear Information System (INIS)

The structure and properties of composite powder coatings on the base of titanium carbide are studied. It is shown the electron-beam welding deposition of powders on the base of nickel and titanium carbide allows to produce of high-quality wear-resistant coatings which superior in density and hardness compared with sputtered ones. Changes of hardening phase volume percentage as well as composition of metal matrix make possible to control coatings hardness

British Library Electronic Table of Contents (United Kingdom)

The purpose of this study is to investigate the influence of tungsten carbide/carbon (WC/C) coating on the surface durability of casehardened steel gear. Two kinds of WC/C coatings were deposited on the ground gear pair made of chromium molybdenum steel with carburizing and quenching. One is the conventional WC/C coating, and the other is WC/C coating with about 1 ?m CrN interlayer. Here, the WC/C-coated test pinion and the WC/C-coated one with CrN interlayer are represented by WT and ST, respectively. Non-coated test pinion is represented by NT. The surface roughness along the tooth profile direction of WT and ST was almost the same as that of NT. A spur gear test was carried out with an IAE power circulating type gear test rig under EP gear oil lubricating condition. The fatal failure mo...

International Nuclear Information System (INIS)

Iron oxide films have been deposited on Si(100) substrates by chemical vapour deposition (CVD) of iron(III) tert-butoxide ([Fe(O "tBu)_3]_2) in the temperature range 350-450 deg. C. The precursor flux and substrate temperature were varied to control the phase composition, average grain size and film thickness. The nature of substrate and deposition temperature markedly influence the morphology and iron-oxygen stoichiometry in the CVD deposits. Phase transformations in iron oxide films were achieved through precise local and periodic heating of the films by interfering laser beams. The interaction of iron oxide films with short laser pulses (Nd:YAG, 355 nm) induced partial transformation of hematite (#alpha#-Fe_2O_3) to magnetite (Fe_3O_4) or magnetite to wuestite (Fe_1_-_xO), respectively. The phase characterization and morphology of the hematite and magnetite films were ...

Energy Technology Data Exchange (ETDEWEB)

There is an increasing number of applications for hard coatings in engineering where the properties of the single-layer coating are not sufficient. One way to solve this problem is to use a multilayer coating that combines the properties of several coating materials. In this study, TiN-CrAlN and CrN-CrAlN multilayer coatings were deposited on 100Cr6 and S6-5-2 (DIN) steel substrates, by means of unbalanced magnetron sputtering. For comparison, TiN, CrN and CrAlN single-layer coatings were also prepared. For all depositions the coating temperature was below 473 K. Indentation testing, hardness measurements and scratch tests were performed to characterize the mechanical properties. The correlation between the wear behavior in rolling contact and the mechanical properties of the multilayer ...

Energy Technology Data Exchange (ETDEWEB)

Corrosion behavior of deposition coated specimens prepared by the technique proposed by the authors is investigated in salt immersion tests, and also those of pure magnesium, 3N, 4N and 6N grades, and magnesium alloys, AZ31 and AZ91E, are investigated for comparison. Inhomogeneous corrosion occurs in AZ31 and AZ91E alloys when buffered solutions with pH values of 6.5 and 9.0 including 1% NaCl and a conventional 3% NaCl solution are used for immersion tests, while 6N-Mg shows homogeneous corrosion in such solutions. Corrosion behavior of the deposition coated specimen resembles that of 6N-Mg. Purification process included in the deposition coating technique provides homogeneity in microstructural and electrochemical terms, which results in improving corrosion resistance. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Anti-reflective coatings made with Teflon AF2400 had the highest damage thresholds recorded for physical vapor deposited coatings at the Lawrence Livermore National Laboratory damage facility. Physical vapor deposited layers of Teflon AF2400, a perfluorinated amorphous polymer, maintained the bulk optical properties of a high transmittance from 200 nm to 1600 nm, and a low refractive index. In addition, the refractive index can be intentionally reduced by control of two common deposition parameters, deposition rate and substrate temperature. Scanning electron microscopy and nuclear magnetic resonance observations indicated that morphological changes caused the variations in the refractive index rather than compositional changes. The coatings adhered to fused silica and silicon wafers under normal laboratory handling conditions.

International Nuclear Information System (INIS)

The cathodic vacuum arc provides a means of producing large currents of positive ions of a wide variety of materials. These ions can be utilized to produce coatings with improved properties such as higher density and adhesion. The processing is particularly useful in reactive deposition of ceramic coatings having excellent stoichiometry. In this review, emerging aspects of the technology are emphasized.

Energy Technology Data Exchange (ETDEWEB)

TiB{sub 2} appears to be a promising material for the wear protection in various tribological systems, e.g. the diecasting of Al. This study focuses on the development of titanium boride coatings deposited by PACVD, a deposition method which is most suitable for the coating of substrates with complex shapes. All layers analysed are very smooth and exhibit a quasi-amorphous fracture surface. XRD and TEM analysis indicate a nanocrystalline structure with grain sizes in the order of 2 nm. The diffraction patterns can well be correlated to titanium diboride. WDS reveals an over stoichiometric B/Ti ratio. The layer hardness reaches the value of 33 GPa and the critical load in scratch tests rises to 35 N. Neither 100Cr6 nor Al as a counterpart in pin-on-disk tests leads to wear of the coating. (orig.)

International Nuclear Information System (INIS)

Several metallurgical coatings have been developed that provide good tribological performances in high-temperature liquid sodium and that are relatively unaffected by neutron fluences to 6 X 10/sup 22/ n/cm/sup 2/ (E > 0.1 MeV). The coatings that have consistently provided the best tribological performance have been the nickel aluminide diffusion coatings created by the pack cementation process, chromium carbide or Tribaloy 700 trade mark (a nickel-base hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing materials applied by the electro-spark deposition process. The latter process is a relatively recent development for nuclear applications and is expected to find wide usage. Other coating processes, such as plasma-spray ...

International Nuclear Information System (INIS)

Polycrystalline silicon films have been grown from Si_2H_6 by low-pressure chemical vapour deposition at 800 K and in situ laser annealing (LA) on amorphous silicon seed layers deposited on a metallic Ti/Pd/Ag multilayer. The crystalline volume fraction in the seed layer was controlled by thermal annealing. According to the metal-induced crystallization effect, the presence of the metal induces a lower-temperature crystallization of silicon in the seed layers. X-ray diffraction and scanning electron microscopy data show that the formation of palladium silicides in the seed layer drives the growth of wire-like columns which are found to change morphology depending on the seed layer microstructure and LA parameters. It is suggested that superficial palladium was found to affect also the growth rate by enhancing the Si_2H_6 dissociation.

International Nuclear Information System (INIS)

With the deposition of PVD hard coatings on the tools applied in machining operations it is possible to achieve significant improvements in the performance and quality of the machining processes. Depending on the machined material and the operating principle, e.g. turning, milling or drilling, not only different machining parameters but also different coating materials are necessary. In interrupted cut machining of tempered steel, for example, the life time of Ti-C-N coated inserts is several times greater than the Ti-C-N coated ones. This is a result of the favourable thermophysical and tribological properties of Ti-N-C. The potential for tool protection by CrN coatings is a result of the high ductility and low internal stress of this coating materials. CrN films can be deposited with greater film thickness, still ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces which are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

Energy Technology Data Exchange (ETDEWEB)

Plasma nitriding as a diffusion process is the oldest plasma-assisted process for the surface treatment of metals. Although the use of this process in industry is already well developed and established there are still several scientific questions in the basic understanding of the process and consequently some problems and limits concerning its upscaling for industrial use. Therefore it is necessary to get reproducible results for different geometries of workpieces and for different workload sizes. Correlations between different plasma and treatment parameters, especially in big plants, have to be considered. To understand the process handling using some simple but impressive models the difficulties of treating single parts or mixed workloads are explained. For profitable applications of plasma nitriding plants, some guidelines for the use and selection of a suitable process and a device are given. By the use of a pulsed d.c. power supply for plasma generation most of the industrial ...

Energy Technology Data Exchange (ETDEWEB)

Duplex-coating procedures consisting of plasma nitriding and Me-C:H hard coating lead to an improved performance of the devices because the Me-C:H coating is supported by the nitrided phase and, therefore, the `eggshell-effect` is avoided. Furthermore, this support leads to a higher load-bearing capacity of the thin film. Two standard procedures (classical high-pressure plasma nitriding and unbalanced magnetron sputtering of Ti-C:H) were performed subsequently to prepare the duplex coatings on X20Cr13 ferritic stainless steel. The corrosion resistance of the steel could be improved by nitriding at 450 C compared to the untreated ferritic substrate. The roughness is determined by the nitriding step. The weakest point of the coating is the transition zone between the nitrided and the untreated substrate and not the interface between the Ti-C:H coating and the ...

International Nuclear Information System (INIS)

The physical, chemical and mechanical properties of magnesium alloys make them attractive materials for automotive and aerospace applications. However, these materials are susceptible to corrosion and wear. This work discusses the potential of using sol-gel based coatings consisting of ZrO_2 and 15 wt.% of CeO_2. The CeO_2 component provides enhanced corrosion protection, while ZrO_2 impart corrosion as well as wear resistance. Coating deposition was performed by the dip coating technique on two magnesium alloy substrates with different surface finishes: AZ91D (as-casted, sand-blasted, and machined) and AZ31 (rolled and machined). All as-deposited coatings (xerogel coatings) were then subjected to 10 h annealing: a temperature of 180 C was applied to the AZ91D alloy and 140 C to the AZ31 alloy. Morphological and structural properties of the ...

International Nuclear Information System (INIS)

A ternary nickel-base alloy Ni-W-B has been developed for surface corrosion and wear resistance to replace chromium plating, which uses environmentally hazardous solutions. The deposition conditions used an alkaline bath and insoluble anodes. The as-deposited alloy typically contains 40 wt% W and 1 wt% B and has an amorphous or partially amorphous structure. These deposits compare favorably with hexavalent chromium deposits in throwing power, color uniformity, and reflectivity. The corrosion resistance of Ni-W-B alloy was compared with hexavalent chromium and electroless nickel deposits in a variety of acids, including hydrochloric, sulfuric, fluoroboric, and phosphoric. In all cases, best results were obtained with the Ni-W-B deposits.

International Nuclear Information System (INIS)

Focused Ion Beams are an important approach for nanostructure fabrication in the semiconductor industry and material sciences. Applications in sputtering and ion induced deposition of materials are investigated. The IMSA FIB system equipped with the high resolution Orsay Physics CANION M31plus ion column with current densities up to 10 A/cm"2 including a gas injection system is applied. In this work the ion beam induced chemical vapour deposition of tungsten, wherefore tungsten hexacarbonyl as precursor gas is used for a first investigation. Conductive tungsten-nanowires with smallest cross-section upon a substrate of Si and SiO_2 are produced. The ion beam parameters of this focused ion beam system are optimized for the metal deposition. A short insight in the theory of layer nucleation and growth induced by the ion beam during the metal deposition is given. The layer quality is ...

Energy Technology Data Exchange (ETDEWEB)

PVD-coatings based on TiB{sub 2} are expected to show high wear resistance and low tendency of adhesion on metal forming tools. Coating adhesion and morphology can be modified over a wide range by varying the content of nitrogen (N{sub 2}) and the deposition parameters power and bias voltage. All coatings were deposited using commercial unbalanced magnetron equipment, the deposition was homogeneous in a volume of 400 x 400 x 400 mm{sup 3}. Hipped and hot pressed TiB{sub 2}-targets were used, nitrogen (N{sub 2}) was added as gas, Ti and Al by a solid Ti-Al-target. The tribological behaviour was tested by a pin-on-disc wear test. The coatings investigated were TiB{sub 2}, TiAlB(N), TiAl(N) and TiB{sub 2}/TiAl(N). As counterpart in the pin-on-disc wear test, 6 mm diameter spheres of steel (100Cr6), aluminium, brass and bronze were used. The ...

Energy Technology Data Exchange (ETDEWEB)

Titanium alloys are characterized by poor tribological properties, and the traditional use of titanium alloys has been restricted to nontribological applications. The deposition of a well adherent diamond coating is a promising way to solve this problem. In this study, the tribological properties of diamond-coated titanium were studied using a pin-on-disk tribometer, and the results were compared with those of pure titanium and plasma nitrided titanium. The tribological behavior of pure titanium was characterized by high coefficient of friction and rapid wear of materials. Plasma nitriding improved the wear resistance only under low normal load; however, this hardened layer was not efficient in improving the wear resistance and the friction properties under high normal load. Diamond coating on pure titanium improved the wear resistance of titanium significantly. Surface profilometry measurement ...

Energy Technology Data Exchange (ETDEWEB)

Chromium nitride/Cr coating has been deposited on surface of 316L stainless steel to improve conductivity and corrosion resistance by physical vapor deposition (PVD) technology. Electrochemical behaviors of the chromium nitride/Cr coated 316L stainless steel are investigated in 0.05 M H{sub 2}SO{sub 4}+2 ppm F{sup -} simulating proton exchange membrane fuel cell (PEMFC) environments, and interfacial contact resistance (ICR) are measured before and after potentiostatic polarization at anodic and cathodic operation potentials for PEMFC. The chromium nitride/Cr coated 316L stainless steel exhibits improved corrosion resistance and better stability of passive film either in the simulated anodic or cathodic environment. In comparison to 316L stainless steel with air-formed oxide film, the ICR between the chromium nitride/Cr coated 316L stainless steel and carbon ...

International Nuclear Information System (INIS)

There is currently great interest in combining focused ion beam (FIB) and scanning electron microscopy technologies for advanced studies of polymeric materials and biological microstructures, as well as for sophisticated nanoscale fabrication and prototyping. Irradiation of electrically insulating materials with a positive ion beam in high vacuum can lead to the accumulation of charge, causing deflection of the ion beam. The resultant image drift has significant consequences upon the accuracy and quality of FIB milling, imaging and chemical vapour deposition. A method is described for suppressing ion beam drift using a defocused, low-energy primary electron beam, leading to the derivation of a mathematical expression to correlate the ion and electron beam energies and currents with other parameters required for electrically stabilizing these challenging materials.

Energy Technology Data Exchange (ETDEWEB)

As a result of health and safety issues surrounding the use of radioactive materials on coated optical components, there has been renewed interest in coating materials whose optical and mechanical properties approach those offered by their radioactive counterparts. Due to the radioactive nature of ThF{sub 4} and its widespread use in optical coatings, the coating industry is examining other low index and non-radioactive fluorides as possible alternatives. In this paper, the authors present the results of an experimental study on the optical and mechanical properties of thermally evaporated ThF{sub 4}, DyF{sub 3}, CeF{sub 3}, LiF, HfF{sub 4}, IRX, and IRB thin films, where the materials were deposited at different substrate temperatures. The objective is to examine this series of fluorides under comparable deposition conditions and with respect to such material ...

British Library Electronic Table of Contents (United Kingdom)

A procedure based on electrophoretic deposition (EPD) was developed to coat metal plates with powder catalysts. The method was tested on stainless-steel plates with three Ni-based catalysts for the steam reforming of ethanol. The catalysts (Ni/La2O3/g-Al2O3) contained 15% Ni and 8% La, and were prepared using three types of g-alumina with different textural properties. The powder catalysts were suspended in isopropanol, and EPD deposition was performed with a voltage of 100V and a distance between electrodes of 2cm. Deposition time was varied between 3 and 7min, which gave a thickness of the catalyst layer from around 30 to 100mm. The morphology of the catalyst layer was dependent on the textural characteristics of the g-Al2O3 used to prepare the catalyst. The activity of the catalyst plat...

Energy Technology Data Exchange (ETDEWEB)

Infrared astronomical instruments require absorptive coatings on internal surfaces to trap scattered and stray photons. This is typically accomplished with any one of a number of black paints. Although inexpensive and simple to apply, paint has several disadvantages. Painted surfaces can be fragile, prone to shedding particles, and difficult to clean. Most importantly, the vacuum performance is poor. Recently a plasma enhanced chemical vapor deposition (PECVD) process was developed to apply thick (30 {micro}m) diamond-like carbon (DLC) based protective coatings to the interior of oil pipelines. These DLC coatings show much promise as an infrared black for an ultra high vacuum environment. The coatings are very robust with excellent cryogenic adhesion. Their total infrared reflectivity of < 10% at normal incidence approaches that of black paints. We measured outgas rates of ...

Energy Technology Data Exchange (ETDEWEB)

Silica microspheres were deposited into two-dimensional periodic arrays and coated with a thin layer of silicon nanocrystals. The luminescence from the silicon nanocrystals coupled into the whispering gallery modes of the spheres, with Q factors that depended on a range of parameters including sphere size, position on the sphere, viewing direction, and thickness of the nanocrystal coating. Scattering from the film-sphere and/or the sphere-substrate contacts resulted in a lower Q for modes that intersect these regions. The highest Q factors obtained in this work were {approx}1500. The results suggest that silica microspheres may be promising candidates for high-Q cavities that incorporate silicon nanocrystals for cavity QED or nonlinear optical effects.

International Nuclear Information System (INIS)

The use of polymer matrix composites in aerospace propulsion applications is currently limited by insufficient resistance to erosion by abrasive media. Erosion resistant coatings may provide necessary protection; however, adhesion to many high temperature polymer matrix composite (PMC) materials is poor. A low pressure oxygen plasma treatment process was developed to improve adhesion of CN_x coatings to a carbon reinforced, fluorinated polymer matrix composite. Fullerene-like CN_x was selected as an erosion resistant coating for its high hardness-to-elastic modulus ratio and elastic resilience which were expected to reduce erosion from media incident at different angles (normal or glancing) relative to the surface. In situ x-ray photoelectron spectroscopy was used to evaluate the effect of the plasma treatment on surface chemistry, and electron microscopy was used to identify changes in the surface morphology of the PMC ...

International Nuclear Information System (INIS)

In this work we present the electrical characterization of non self-aligned p-channel thin film transistors fabricated by using laser doping technique for source/drain contact formation and gate oxide deposited at room temperature by Electron Cyclotron Resonance Plasma Enhanced Chemical Vapour Deposition. These techniques are suitable for a very low temperature process for TFT fabrication. The output characteristics show a current increase at high drain voltage ('kink' effect) rather moderate, if compared to self aligned polysilicon TFTs, probably due to the gradual doping profile induced by laser doping process. After bias stress at low gate voltage and high drain voltage condition a strong reduction of kink current has been observed in the output characteristics at high drain voltage, whereas minor changes has been observed in the transfer characteristics. This behaviour is similar to what observed in n-channel Gate ...

Energy Technology Data Exchange (ETDEWEB)

This patent describes an improved zinc electrode for a rechargeable zinc-air battery comprising an outer frame and a porous foam electrode support within the frame which is treated prior to the deposition of zinc thereon to inhibit the formation of zinc dendrites on the external surface thereof. The outer frame is provided with passageways for circulating an alkaline electrolyte through the treated zinc-coated porous foam. A novel rechargeable zinc-air battery system is also disclosed.

International Nuclear Information System (INIS)

A novel composite film, comprising of hydrophobic ionic liquid (IL), multi-walled carbon nanotubes (MWNTs) and gold nanoparticles (GNP), was fabricated and characterized. The GNP was introduced through electrochemical deposition on IL-MWNT gel film coated glassy carbon electrodes (GCE). Experiments showed that both IL and MWNTs could facilitate the GNP deposition. With GNP the composite film exhibited smaller electron transfer resistance and higher sensitivity in sensing guanine (G) and adenine (A). Under the optimized experimental conditions, the anodic peak currents were linear to the analyte concentration in the ranges of 0.008-2.0 ?M. The detection limits were down to nanomole level after an accumulation of 150 s on open-circuit. In addition, on the composite film coated GCE, the anodic peaks of G and A were well separated, and their response sensitivities kept almost unchanged no matter whether ...

Energy Technology Data Exchange (ETDEWEB)

In the present paper the tribological behavior of the coatings are discussed. Duplex coatings were applied on cold working steel 100Cr6. Samples were plasma nitrided at different thickness of plasma surface layers. TiN was deposited with a classic BALZERS PVD equipment and subsequent ion implantation. Ion implantation was provided with N{sup 5+} ions. The other samples were produced with IBAD technology in DANFYSIK chamber. Wear resistance and exchanges of friction coefficient were measured with on-line test using special designed tribology equipment. Following the tests, the wear zone morphology and characteristics of surface layer structure as well as important properties were investigated by scanning electron microscopy (SEM) and X-ray diffraction analysis (XRD). Scratch adhesion testing was performed using commercially available equipment. Energy dispersive X-ray analysis (EDAX) of the wear-scars on pins provided ...

International Nuclear Information System (INIS)

This work showed the formation of phospholipid vesicle coating on inorganic sericite surface with characterization by combining electron microscopy of FE-SEM, TEM, AFM, and qualitatively evaluated the coated phospholipid vesicle by XPS as a function of etching time. The possibility of phospholipid vesicle mobility on the surface was restrained by the chelation effect of magnesium cation. The stabilization properties of phospholipid vesicles on sericite surface were demonstrated by the various concentration of magnesium cation. The presence of magnesium was found to have a much more pronounced influence on the lipid deposition process. The Mg cation plays an important role for attaching the phospholipids with optimum concentration of 7 mM. Totally, the phospholipid vesicles coating on inorganic powder could be useful for bio-related fields such as cosmetics and drug delivery system as the key functional ...

Energy Technology Data Exchange (ETDEWEB)

The passive films formed in stainless steels are thin and fine oxide films, a high corrosion resistance can be provided by these films. This study formed SiO2 protective coating on the substrate of SUS 304 stainless steels by chemical vapor deposition using TEOS-O3 system. Firstly, relations of substrate temperature and deposition rate of films, chemical composition, refractive index of films were investigated. Then, the corrosion resistance of SUS 304 stainless steels coated SiO2 films was examined by activation time and an anodic polarization curve in 1 kmol[center dot]m[sup -3] HCl solution. The results were obtained as follows. Thickness of SiO2 films linearly increases with time at the deposition temperature of 473 to 673 K. Si-OH bonds would disappear above the deposition temperature of 573 K, almost perfect SiO2 films were obtained. The activation time in ...

Energy Technology Data Exchange (ETDEWEB)

Olive field is oil productive from a thin stratigraphically trapped sandstone within the Upper Cretaceous lower Tuscaloosa Formation. The discovery of Olive in 1981 led to renewed interest in the Mid-Dip Tuscaloosa Trend that continues today. Discovery and development was based on the correlation of the B sandstone to a mappable soft seismic event at a depth of 10,500 ft. The field was developed by 25 wells on 40-acre spacing. Olive has been waterflooded since 1983 and is a target for enhanced recovery using carbon dioxide. A total of 7.5 million stock tank bbl or approximately 75% of the original oil in place is estimated to be recoverable by conventional and enhanced recovery methods. The B sandstone was deposited by a northwest to southeast-flowing high-sinuosity meandering river system. Point bar, channel, and channel abandonment deposits are present. The point bar formed from the lateral migration of the river system from west to east, and ...

British Library Electronic Table of Contents (United Kingdom)

Si nanocrystal floating gate MOS capacitors were formed on p-Si (100) wafers by thermal plasma jet (TPJ) annealing of SiO2/SiOx /SiO2/Si(100) stacked structure. The chemical composition of SiOx layer was controlled by changing the SiH4, He, and O2 gas flow ratio during plasma enhanced chemical vapour deposition. The MOS capacitors showed clear hysteresis in capacitance-voltage (CV) characteristics after TPJ annealing. The hysteresis width shows maximum value when initial composition x =1.7, which shows the maximum photoluminescence (PL) intensity. The maximum hysteresis width of 6.8 V was observed with gate voltage swept between 20 and -20 V in x = 1.7 sample. The result means 7.4 x 1012 cm-2 carriers are injected to or emitted from Si nanocrystals. The duration of 1 V shift in flatband vo...

International Nuclear Information System (INIS)

The removal of tritiated water vapour was tested by use of a small burning apparatus and a clinoptilolite filter. It was found that decontamination factor of about 10"4 could be obtained by a clinoptilolite filter. The adsorption of HTO in the clinoptilolite is caused by the diffusion, so it is necessary that filtration velocity is maintained below 0.01 m/sec. Decontamination factor was not influence by the moisture content of a clinoptilolite and tritiated water vapour once adsorbed on a filter was hardly removed. (auth.).

International Nuclear Information System (INIS)

By means of an audio frequency plasma polymerisation ultra-thin gradient plasma polymer layers were deposited on zinc and zinc-coated iron. The aim was to generate an interfacial polymeric layer which bonds to an oxidised metal as well as to a subsequently applied organic coating and acts as an interfacial barrier layer for ions and water. Surface modifications were done in an in situ plasma cell with infrared reflection absorption spectroscopy (IRRAS). The zinc surface was first activated by an oxygen plasma to provide a freshly oxidised and contamination free oxide surface. The intermediate stages of the surface reactions could be revealed. Carbon dioxide molecules as oxidation products adsorbed on the growing zinc oxide and were desorbed at a later stage. An organosilicon plasma polymer was deposited directly on top of the oxide layer from a hexamethyldisilane (HMDS) plasma. Afterwards a cyclohexene ...

International Nuclear Information System (INIS)

The possibility of surface modification of high-speed steel cutting tool by means of vacuum-plasma treatment including ion nitriding in gas plasma followed by the deposition of wear resistant (Ti, Al)N coatings in metal-gas plasma of a vacuum arc discharge is studied. The regularities of nitrided layer formation and the structure of these layers under various operation conditions of cutting tool are investigated. Optimum conditions of vacuum-plasma treatment providing the best wear resistance of cutting are determined

Energy Technology Data Exchange (ETDEWEB)

Objective of the project is characterization of electrode reactions in molten salt by using metal oxides and silica-based electrode. The scope of project are characterization of metal oxide properties in molten salt and miniaturization of 3-electrode electrochemical test cell. Electrochemical micro-cell for actinide-LiCl-KCl molten salt was newly designed. Electroless and electrochemical deposition technique was applied to Mo coating on quartz tube. From the design of electrode and 3-electrode electrochemical cell suitable for the tests in molten salt electrolyte, so it is anticipated to get the information on the electrochemical behavior of metallic electrode in molten salt and to secure the information on oxidation/reduction behavior of actinide

Science.gov (United States)

... SCREENING GUN BARREL COATING'S RESPONSE ... SCREENING GUN BARREL COATINGS' RESPONSE TO COMBUSTION GASES ...

Energy Technology Data Exchange (ETDEWEB)

The surface of low alloy steel (En40B) has been engineered in the plasma of a glow discharge via plasma nitriding and ion plating of titanium nitride (TiN) coatings on the nitrided substrates with the purpose of enhancing the surface properties and fatigue strength. The nitriding response of the steel has been accessed by the evaluation of phase composition, layer thickness, hardness profile, residual stresses and nitrogen and carbon distributions. The wear and fatigue characteristics of the plasma-nitrided steel have been investigated and simple models have been developed to describe the influence of such properties as depth and strength of the nitrided case on the fatigue limit and load-bearing capacity of the nitrided steel. In order to further improve the tribological properties and load-bearing capacity of the low alloy steel, a duplex plasma surface-engineering technique has been developed. This is achieved by plasma nitriding the steel first so as to produce ...

Energy Technology Data Exchange (ETDEWEB)

Carbon dioxide is receiving renewed interest as an efficient and environmentally safe refrigerant in a number of applications, including mobile air conditioning and heat pump systems, and hot water heat pumps. Compact heat exchangers for CO{sub 2} systems are designed with small-diameter tubing. The purpose of this study is therefore to provide a better basis for understanding and predicting heat transfer and pressure drop during flow vaporization of CO{sub 2} in microchannels. The ''unusual'' properties of carbon dioxide give heat transfer and two-phase flow characteristics that are very different from those of conventional refrigerants. Examples of these differences are the much higher pressure, the resulting high vapour density, a very low surface tension, and a low liquid viscosity. High pressure and low surface tension has a major effect on nucleate boiling characteristics, and earlier test data have shown a clear dominance ...

Energy Technology Data Exchange (ETDEWEB)

Photoelectrochemical oxidation is a potentially interesting method for destroying toxic organic materials. We have studied the photoelectrocatalytic activity of TiO{sub 2} films made by thermal oxidation of titanium, low pressure chemical vapour deposition (LPCVD), and anodisation of titanium. Two model organic compounds have been investigated for photooxidation: methyl phosphonic acid (MPA) which is a nerve gas analogue and 4-chlorophenol (4-CP) which is a chlorinated aromatic compound considered a standard for the evaluation of the TiO{sub 2} / UV processes. In addition to photoelectrochemical characterisation the films have been characterised by profilometry, XRD, AFM, photocurrent spectroscopy and Raman microscopy. Correlations have been made between the physical properties of the thin films and their catalytic activities. The most catalytic sample of thermally oxidised titanium was prepared at 400 deg C, and the presence of anatase was ...

International Science & Technology Center (ISTC)

New Composite Multifunctional Coatings Produced Using SHS-Electrodes

International Science & Technology Center (ISTC)

Development of the Method of Electrodepositing Nanostructured Composite Coatings with Improved Engineering Properties

International Nuclear Information System (INIS)

In the first part of this paper, IrO_2 electrodes produced by thermal decomposition of H_2IrCl_6 precursor were manufactured using the spin coating deposition technique, where centrifugal forces spread the precursor solution with simultaneous evaporation of the solvent on the rotating Ti substrate. It was found using this technique, that it is possible to obtain thin and uniform IrO_2 coatings with controlled loadings. The influence of the concentration of iridium salt in the precursor solution (c_0) as well as the influence of the rotation speed at which the substrate spins (#omega#) on the IrO_2 loading have been studied using voltammetric charge measurements. From these results, a simple relation has been proposed for the estimation of the IrO_2 loading for a given c_0 and #omega#. In the second part of this paper and from measurements performed using different IrO_2 loadings and formic acid concentrations, the kinetic ...

Energy Technology Data Exchange (ETDEWEB)

In addition to ceramics, alloys such as tool steel and nickel- and iron-based superalloys are being considered for high temperature applications such as missile bearings and low heat rejection engines. Studies were made to lubricate a nickel-based superalloy at 500{degrees}C, by using a vaporized aryl phosphate ester, at a concentration of 0.1% in air. From deposition and wear studies it was found that it was impossible to form a good polymeric coating on the superalloy surface. Energy dispersive X-ray analyzer (EDXA) analysis showed that this was due to minute quantities of aluminum in the alloy segregating to the surface, upon being heated to 500{degrees}C, forming a passive oxide coating. It was necessary to activate the surface, in order to lubricate the material successfully. A method of activation by electrodepositing the surface with a layer of iron oxide was developed. Once activated, a good lubricous polymer was ...

Energy Technology Data Exchange (ETDEWEB)

The aim of this work is to combine the MCFC cathode Li{sub x}Ni{sub 1-x}O properties to those of the protective coatings of LiCoO{sub 2}, Li{sub 2}TiO{sub 3} or of CeO{sub 2}, less soluble in the molten carbonates. In the cases of LiCoO{sub 2}, have been carried out by controlled potential coulometry in aqueous solution, a deposition of Co{sub 3}O{sub 4} on dense Ni. The cobalt oxide reacts rapidly in the Li{sub 2}CO{sub 3}-Na{sub 2}CO{sub 3} medium at 650 C to give LiCoO{sub 2}, a spinel cubic phase revealed by Raman spectroscopy. (O.M.)

Energy Technology Data Exchange (ETDEWEB)

Thin films of new metastable materials from the system Ti-B-C-N were deposited on metallic substrates by d.c. magnetron sputtering in different Ar+N{sub 2} atmospheres. The multiphase compound targets used were based on various compositions on the TiC-TiB{sub 2} and TiB{sub 2}-C tie lines of the Ti-B-C phase diagram. The structure and chemical composition of the films were characterized by electron microprobe analysis, depth profiling Auger electron spectroscopy, X-ray diffraction and transmission electron microscopy. The hardness, critical load of failure and the tribological behavior of the coatings were investigated. Superhard single-phase crystalline metastable Ti-B-C-N layers with hardness values exceeding 5000 HV{sub 0.05} and extremely low sliding wear against 100Cr6 and Al{sub 2}O{sub 3} counterparts could be produced by reactive sputtering of various TiC-TiB{sub 2} targets in Ar+N{sub 2} atmospheres with low nitrogen flows. In the case ...

Science.gov (United States)

The growth of an oxide interfacial layer was recently found to increase the open-circuit voltage (OCV) and efficiency by up to 60 per cent in GaAs metal-semiconductor solar cells. Details of oxidation techniques to provide the necessary oxide thickness and chemical structure and using ozone, water-vapor-saturated oxygen, or oxygen gas discharges are described, as well as apparent crystallographic orientation effects. Preliminary results of the oxide chemistry obtained from X-ray, photoelectron spectroscopy are given. Ratios of arsenic oxide to gallium oxide of unity or less seem to be preferable. Samples with the highest OVC predominantly have As(+3) in the arsenic oxide rather than As(+5). A major difficulty at this time is a reduction in OCV by 100-200 mV when the antireflection coating is vacuum deposited.

British Library Electronic Table of Contents (United Kingdom)

Nanocapsules coated by medicinal plants have many applications in drug manufacturing. Medicinal plants can be loaded on nanocapsules with polyesteric triblock copolymer poly ethylene glycol-poly butylene adipate-poly ethylene glycol (PEG-PBA-PEG) as shell and olive oil can be introduced as a core of nanocapsules by a method known as polymer deposition solvent evaporation method. In this research, first, certain amount of polymer, Matricaria recutita extract and olive oil were mixed with acetone and then, water was added to the solution using magnetic stirrer. After which the acetone was removed by vacuuming and finally nanocapsules were found by freezing-drier. The study showed the size of nanocapsules depends on variety of factors such as the ratio of polymer to oil and concentration of p...

British Library Electronic Table of Contents (United Kingdom)

Asphalt emulsions were evaluated as a means to immobilize radiological contaminants deposited on urban surfaces after a dirty bomb attack. Contaminated surfaces would be sprayed with thin coatings of asphalt emulsion to encapsulate the radioactive particles until the site can be safely remediated. This research investigated applications of an asphalt emulsion (Topein C, Encapco Technologies, LLC, Napa, CA) to treat (zero-valent) iron, lead, and uranium powders on various building material surfaces. Initial studies found that some of the building materials (limestone, concrete, and metal) reacted with the emulsion producing gas bubbles, which formed 0.001 to 1 cm vesicles in the cured asphalt emulsion. These vesicles, however, did not expose the building material surface, and the reaction a...

Energy Technology Data Exchange (ETDEWEB)

Solid recycling of AZ31 Mg alloy with vapor deposition coating layer of high purity Mg was evaluated. In the open die forging experiments, two AZ31 Mg alloy specimens with the pure Mg layer were sufficiently bonded by forging at 673 K. Furthermore, the Al and Zn of the AZ31 substrate diffused up to the center of the pure Mg layer. By the theoretical analysis, it is suggested that the grain boundary diffusion enhanced by grain refinement due to hot forging contributes to the solid state bonding of the specimens. Also, the solid recycled specimen was fabricated from the AZ31 Mg substrate with pure Mg layer by hot extrusion at 673 K. The solid recycled specimen showed almost the same tensile properties as the virgin extruded specimen. This is probably related not only to the grain boundary diffusion but also severe plastic deformation by hot extrusion. (orig.)

International Nuclear Information System (INIS)

Iron oxide thin films were prepared by spray pyrolysis technique onto glass substrates from iron chloride solution. They were characterized by X-ray diffractometry (XRD), scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS) and (UV-vis) spectroscopy. The films deposited at T _s #<=# 450 deg. C were amorphous; while those produced at T _s_u_b = 500 deg. C were polycrystalline #alpha#-Fe_2O_3 with a preferential orientation along the (1 0 4) direction. By observing scanning electron microscopy (SEM), it was seen that iron oxide films were relatively homogeneous uniform and had a good adherence to the glass substrates. The grain size was found (by RX) between 19 and 25 nm. The composition of these films was examined by X-ray photoelectron spectroscopy and electron probe microanalysis (EPMA). These films exhibited also a transmittance value about 80% in the visible and infrared range. The cyclic voltammetry study showed that the films of ...

British Library Electronic Table of Contents (United Kingdom)

Abstract Visible blue cathodoluminescence (CL), photoluminescence (PL), x-ray excited optical luminescence (XEOL) and electroluminescence (EL) via Zf free excitonic emission have been obtained from CuBr thin films deposited on glass, Cr coated glass, GaAs and Si substrates. In addition to the Zf emission several peaks corresponding to Cu+ emissions via 3d94s - d10 transitions were observed on the AC EL spectrum at 2.10, 2.7, 3.03, 3.07 and 3.80 eV. X-ray diffraction (XRD) measurements confirmed that the vacuum evaporated CuBr thin films grow preferentially with a (111) orientation irrespective of the substrate. While the AC voltage source was found to have no detrimental effects on CuBr thin films, cathodic deposition of Cu metal via electrolytic decomposition was observed under steady sta...

Energy Technology Data Exchange (ETDEWEB)

Si nanocrystal floating gate MOS capacitors were formed on p-Si (100) wafers by thermal plasma jet (TPJ) annealing of SiO{sub 2}/SiO{sub x} /SiO{sub 2}/Si(100) stacked structure. The chemical composition of SiO{sub x} layer was controlled by changing the SiH{sub 4}, He, and O{sub 2} gas flow ratio during plasma enhanced chemical vapour deposition. The MOS capacitors showed clear hysteresis in capacitance-voltage (CV) characteristics after TPJ annealing. The hysteresis width shows maximum value when initial composition x =1.7, which shows the maximum photoluminescence (PL) intensity. The maximum hysteresis width of 6.8 V was observed with gate voltage swept between 20 and -20 V in x = 1.7 sample. The result means 7.4 x 10{sup 12} cm{sup -2} carriers are injected to or emitted from Si nanocrystals. The duration of 1 V shift in flatband voltage was {proportional_to}0.1 ms with 20 V pulse, and charged carriers were stably maintained for ...

Energy Technology Data Exchange (ETDEWEB)

Desiccants have been used in many applications to provide dehumidification. This paper describes an application of desiccants which provide both dehumidification and sensible cooling, with little or no use of conventional vapour-compression refrigeration plant. Through a parametric study, the energy consumption and costs of a desiccant cooling system are compared with those of a conventional vapour-compression refrigeration-based air-conditioning system. (author)

Wastenet

as well as their use in optimizing the coating process .It will be shown how the differences

Science.gov (United States)

A critical review of the literature revealed no experiments on uranyl ion transfer from an aqueous to a tributyl phosphate phase which positively measured the kinetics of the chemical reaction at the interphase. Drawing isorhythmic lines on a three component diagram gives a complex correlation for the compaction of three sizes of glass beads. Neither the use of thoria sols nor high feed solution concentrations of thorium nitrate gave any significant increase in mean particle diameters over those obtained from nitrate solutions of lower concentrations in flame denitration. A hydraulic film resistance has been detected in the anion exchange of uranyl sulfate into Dowex 2lK, and chloride elution was found to give a higher apparent uranium diffusion coefficient than nitrate elution. The rate of dissolution of mixed thorium-uranium oxides was determined as a function of the per cent of mixed oxides dissolved. Mixing in tanks packed with boron glass Raschig rings ...

Energy Technology Data Exchange (ETDEWEB)

Nylon 6 and nylon 66 films have been treated with aqueous sulfonated aromatic compound (SAC) solutions at concentrations ranging from 0.005 to 1.0 wt%. SAC uptakes at different treatment concentrations were measured and found to follow a BET isotherm. The surface morphologies of nylon film samples, including the original and SAC-treated films, have been characterized by atomic force microscopy (AFM). For untreated nylon 6 and nylon 66 films, AFM images show a randomly distributed fibrillar surface structure. Characteristic widths of fibrils in the nylon 66 and 6 films were 150-225 and 75-150 nm, respectively. For SAC-treated nylon films, the AFM images revealed that the surfaces of the films became covered with nodule-like features having a diameter range of 25-60 nm. AFM analysis provides evidence that SAC treatment deposited a surface coating on nylon films. AFM images of SAC-treated nylon films suggest a mechanism for stain resistance in ...

Science.gov (United States)

... Descriptors : *PROTECTIVE COATINGS, *WATER REPELLENTS, *COMBUSTIBLE CARTRIDGE CASES, COMPUTER PROGRAMS, SOLVENTS ...

Science.gov (United States)

... Descriptors : *Combustible cartridge cases, *Water repellents, *Protective coatings, *Patents, Silica gel, Aluminum compounds, Binders ...

Energy Technology Data Exchange (ETDEWEB)

In vitro cytocompatibility and cellular interactions of lauric acid and dextran-coated magnetite nanoparticles were evaluated with two different cell lines (mouse fibroblast and human cervical carcinoma). Lauric acid-coated magnetite nanoparticles were less cytocompatible than dextran-coated magnetite nanoparticles and cellular uptake of lauric acid-coated magnetic nanoparticles was more than that of dextran-coated magnetite nanoparticles. Lesser cytocompatibility and higher uptake of lauric acid-coated magnetite nanoparticles as compared to dextran-coated magnetic nanoparticles may be due to different cellular interactions by coating material. Thus, coating plays an important role in modulation of biocompatibility and cellular interaction of magnetic nanoparticles.

International Nuclear Information System (INIS)

Reliable and consistent characterization of the stable isotope composition of atmospheric water vapour and its temporal variability are important prerequisites to the wider application of isotope mass balance methods in atmospheric and water balance studies. A new approach is proposed which utilizes standard class-A evaporation pans, which have sufficient volume to buffer short-term transient variations in atmospheric conditions, justifying the assumption of constant kinetic isotopic fractionation effects in concert with precisely measured temperature and relative humidity to derive vapour isotopic composition. The results of the studies suggest that isotopic sampling of existing, conventionally operated class-A evaporation pans could offer a straightforward and cost-effective solution to the problem of documenting the shifting isotopic distribution in atmospheric moisture

Energy Technology Data Exchange (ETDEWEB)

Oil exploration began in Florida in 1901, but no oil was found until 1943. In November of that year, Humble Oil and Refining Co. made a discovery near Sunniland in southern Florida. This field and the producing zone were called Sunniland. No further discoveries were made in southern Florida until 1954 when the Forty-Mile field was discovered by Gulf Oil Co. Ten years later, in 1964, the Sunoco Felda field was discovered by Sun Oil Co., followed by West Sunoco Felda field in 1968. The examination of numerous cores and thin sections of this formation, both from producing fields and wildcat wells, reveals a sequence of deposition in the Sunniland formation. It has been reported that tintinnids or calpionellids have been observed in the lower mud section, but investigation of many thin sections from this section revealed only ostracod particles. Above the mudstone, the section becomes increasingly plentiful in fragmented microbored rudist particles and forams such as ...

J-STORE (Japan)

Full Text Available

UK PubMed Central (United Kingdom)

The effects of thiol-specific reagents on the amplitude of the electro-olfactogram (E.O.G.) responses elicited from frog olfactory mucosa by pulses of odorant vapours was studied. The impermeant thiol-specific...Full Text Available

Science.gov (United States)

Lunar resource utilization has focused principally on the extraction of oxygen from the lunar regolith. A number of schemes have been proposed for oxygen extraction from Ilmenite and Anorthite. Serendipitously, these schemes have as their by-products (or more directly as their "waste products"), materials needed for the fabrication of thin film silicon solar cells. Thus lunar surface possesses both the elemental components needed for the fabrication of silicon solar cells and a vacuum environment that allows for vacuum deposition of thin film solar cells directly on the surface of the Moon without the need for vacuum chambers. In support of the US space exploration initiative a new architecture for the production of thin film solar cells on directly on the lunar surface is proposed. The paper discusses experimental data on the fabrication and properties of lunar glass substrates, evaporated lunar regolith thin films (anti-reflect coatings and ...

British Library Electronic Table of Contents (United Kingdom)

The pentenary compound semiconductor Cu(In,Ga)(Se,S)2 is one of the most attractive materials for high-efficiency solar cells due to its tunable band gap to match well the solar spectrum. In this study, semiconducting Cu(In,Ga)(Se,S)2 thin films were prepared by a classical two-step growth process, which involves the selenization and/or sulfurization of In/Cu?Ga precursor. During the precursor formation step metallic In/Cu?Ga alloys were deposited onto the Mo-coated soda-lime glass substrates by DC magnetron sputter process. The respective precursors were subsequently reacted with H2Se and/or H2S gasses, at elevated temperatures. By optimizing the selenization parameters, such as the gas concentrations, reaction time, reaction temperature, and the flow of H2Se and H2S, high quality, single...

International Nuclear Information System (INIS)

Zinc oxide thin films were obtained by laser ablation of a Zn target in oxygen reactive atmosphere, the oxygen being supplied either by a standard gas inlet valve or from a radio-frequency (rf) oxygen plasma. Pt-coated silicon and MgO were used as substrates. The influence of the deposition parameters as laser wavelength (266, 355, 1064 nm), laser fluence (1.5-20 J/cm2) and oxygen pressure (1-60 Pa) was studied. The influence of the rf plasma beam addition on the morphological proprieties of zinc oxide films was particularly investigated, simultaneously with several configurations of the direction of the ablation plasma, the rf plasma beam and the substrate. The obtained films, with thicknesses in the range of 50 nm to 1 ?m have been characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM).

International Nuclear Information System (INIS)

Nano-sized zinc oxide was synthesized and deposited onto cellulosic fibers using the sol-gel process at ambient temperature. The prepared materials were characterized using several techniques including scanning electron microscopy, transmission electron microscopy, diffuse reflectance spectroscopy, X-ray diffraction and thermogravimetric analysis. X-ray diffraction studies of the ZnO-coated fiber indicate formation of the hexagonal crystal phase which was satisfactory crystallized on the fiber surface. The electron micrographs show formation of zinc oxide nanoparticles within 10-15 nm in size which have been homogeneously dispersed on the fiber surface. The prepared materials show significant photocatalytic self-cleaning activity, which was monitored by diffuse reflectance spectroscopy. The photoactivity was studied upon measuring the photodegradation of methylene blue and eosin yellowish under UV-Vis irradiation. The photocatalytic activity of ...

Energy Technology Data Exchange (ETDEWEB)

A lightweight, low permeability liner for graphite epoxy composite compressed gas storage vessels. The liner is composed of polymers that may or may not be coated with a thin layer of a low permeability material, such as silver, gold, or aluminum, deposited on a thin polymeric layer or substrate which is formed into a closed bladder using torispherical or near torispherical end caps, with or without bosses therein, about which a high strength to weight material, such as graphite epoxy composite shell, is formed to withstand the storage pressure forces. The polymeric substrate may be laminated on one or both sides with additional layers of polymeric film. The liner may be formed to a desired configuration using a dissolvable mandrel or by inflation techniques and the edges of the film seamed by heat sealing. The liner may be utilized in most any type of gas storage system, and is particularly applicable for hydrogen, gas mixtures, and oxygen ...

International Nuclear Information System (INIS)

Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at ...

Science.gov (United States)

The commercial solid phase microextraction (SPME) fibers are not stable enough in organic solvent and tend to swell and strip off from the silica fiber in the high performance liquid chromatography (HPLC) mobile phase, and therefore the application of SPME coupled online with HPLC is limited. In this study, an SPME fiber coated with single walled carbon nanotubes (SWCNTs), prepared by means of electrophoretic deposition, was coupled on line to HPLC for the determination of four endocrine-disrupting compounds, i.e. bisphenol A (BPA), estrone (E(1)), 17?-ethynylestradiol (EE(2)) and octylphenol (OP), in aqueous samples. The results showed that the SWCNTs coating on the prepared fiber did not swell and strip off from the platinum fiber throughout the experiment, thus indicating a high resistance to the HPLC mobile phase, the mixture of water and acetonitrile. The SWCNTs fiber had similar (for OP) or higher (for BPA, EE(2) and ...

Science.gov (United States)

An investigation was conducted to determine the cause of coating residue found in the test gun chambers during qualification firing of 120-mm combustible cartridge case (CCC) ammunition for the MlAl/A2 main battle tank. The CCC is coated with a clear epox...

Science.gov (United States)

... Mirrors (Preprint) Ryan Conk et al. 15 September 2006 ... 4. TITLE AND SUBTITLE Stress Coatings for Large Scale Membrane Mirrors (Preprint) 5a. ...

Science.gov (United States)

A waterjet coating-removal system was developed at NASA's Marshall Space Flight Center in Huntsville, Ala., to remove thermal protective coatings from the ...

Wastenet

Hexavalent chromium in corrosion preventive coating 64 ...To prevent corrosion of rims, weights can be provided with a coating. ...integrated clips brought up technical problems due to corrosion

Science.gov (United States)

Results showed that a simple yttrium coating offered more potential for ... was from 70 to 150 K (125' to 200' F) above that for the yttrium coating. ...

Science.gov (United States)

Sputtering of glass coatings on cadmium sulfide thin film solar cells

International Nuclear Information System (INIS)

This study demonstrates amplified spontaneous emission (ASE) of the ultraviolet (UV) electroluminescence (EL) from ZnO at #lambda##approx#380 nm in the n-ZnO/ZnO nanodots-SiO_2 composite/p- Al_0_._1_2Ga_0_._8_8N heterojunction light-emitting diode. A SiO_2 layer embedded with ZnO nanodots was prepared on the p-type Al_0_._1_2Ga_0_._8_8N using spin-on coating of SiO_2 nanoparticles followed by atomic layer deposition (ALD) of ZnO. An n-type Al-doped ZnO layer was deposited upon the ZnO nanodots-SiO_2 composite layer also by the ALD technique. High-resolution transmission electron microscopy (HRTEM) reveals that the ZnO nanodots embedded in the SiO_2 matrix have diameters of 3-8 nm and the wurtzite crystal structure, which allows the transport of carriers through the thick ZnO nanodots-SiO_2 composite layer. The high quality of the n-ZnO layer was manifested by the well crystallized lattice image in the HRTEM picture and the ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes a feasibility demonstration of a thermal scanning NDE system for thermal spray coatings. Non-bonds were detected between several types of coatings and their substrates. Aluminum anti-skid coatings having very rough surfaces were included. A technique for producing known non-bond areas for calibrating and demonstrating NDE methods was developed.

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the structural properties of sputtered tantalum and tantalum compounds. The preparation of thin film capacitors and resistors is described. The electrical properties of the sputtered films are also included. The influence of the substrate on the properties of the coatings is considered, including adherence of the coating to the substrate, and the effects of impurities on coating integrity. (Contains 250 citations and includes a subject term index and title list.)

Energy Technology Data Exchange (ETDEWEB)

Non-destructive methods for measuring the remaining anticorrosive or antioxidative ability of coatings are investigated. For anticorrosive chromium coatings the increasing ferromagnetism caused by loss of chromium is measured by a permeability probe. Measured values on blades after operation are correlated with the progress of corrosion as determined by metallographic methods. For antioxidative aluminum coatings the diminishing layer thickness is taken as indication for the exhaustion of their protection ability. The layer thickness is measured eddy current probes, especially developed for this application.

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Simulated atmospheric corrosion studies were performed to determine the corrosion protection provided by galvanized zinc coatings on depleted uranium, U-0.75 Ti alloy, and U-6 Nb alloys. The accelerated ASTM tests consisted of exposing the galvanized samples to aqueous and aqueous chloride environments. The test results showed that anodic protection was provided by the electronegative zinc coatings on uranium and uranium alloys. Treating zinc with chromate conversion coatings also provided more protection.

British Library Electronic Table of Contents (United Kingdom)

The effect of heat treatment on the corrosion behavior of reactive plasma sprayed TiN coatings in simulated seawater was investigated by electrochemical methods such as the corrosion potential-time curve (Ecorr-t), potentiodynamic polarization, electrochemical impedance spectroscopy (EIS) and SEM, etc. The results showed that the corrosion potential of TiN coatings increased after heat treatment; the corrosion current of the TiN coatings after heat treatment (be hereafter referred to as HT-TiN) was 13.3% of the untreated coatings (be hereafter referred to as UT-TiN), and the polarization resistance of HT-TiN was 20 times of UT-TiN, which indicated that the heat treatment had significantly increased the corrosion resistance of the coatings. The corrosion behavior of the coatings was mainly ...

Energy Technology Data Exchange (ETDEWEB)

From a macroscopic point of view, corrosion of Zn alloy coated steel sheet occurs by the coating preceding corrosion mechanism; microscopically, however, the coated layer corrosion velocity in the tip of corrosion is different. In order to find the main factors of under-film corrosion of Zn and Zn-Fe alloy coatings in the salt water spray atmospheric exposure test, the correlation between point inflation-exfoliation width and chlorine penetration behavior, point adhesion, and the difference in chlorine penetration behavior due to alloy coating components were investigated. Consequently, the following results were obtained: 1. The better correlation was observed between chlorine penetration distance and point inflation-point exfoliation width. 2. The durability of coating against chlorine penetration improved by increase in point adhesion and Zn content in the ...

International Nuclear Information System (INIS)

The effect of a substrate on the results of measuring tantalum coating thickness in two-layer compositions according to gamma radiation scattered by the substrate is studied. It is shown that by means of an albedo-radiometer realizing the physical model absorber-scatterer one can determine the thickness (application uniformity) of tantalum coatings up to 150-300 #mu#m depending on the substrate material (plexiglas, aluminium, iron, copper). In case of testing coatings on substrates of alloys and high-alloy steels in order to ensure high accuracy of measrurement it is expedient with the above albedo-radiometer to determine the value of the backscattered radiation flux for the substrate before coating application.

Energy Technology Data Exchange (ETDEWEB)

For the protection of buried steel pipeline, it is common practice to coat the pipelines with highly insulating coating and apply a cathodic current to insulate the pipe from the aggressive environment. Cathodic current protects holidays or damaged area of coating which required less current than would be needed for an uncoated pipe, but because of the cathodic reactions evolution will be taken H{sub 2} and OH{sup -} on holidays which exposed metal to the environment place. This effect is to cause loss bond of coating around the holidays called cathodic dis-bonding. In this paper we measured cathodic dis-bonding of three types of coatings at - 1.5 V(Cu/CuSO{sub 4}) according to ASTM G8. We studied on cathodic dis-bonding resistance of petroleum-base, coal tar-base and polyethylene plastic tape coatings. After 30 days immersion in electrolyte it was found that ...

International Nuclear Information System (INIS)

The production of ozone in a negative corona discharge fed by carbon dioxide with embedded traces of oxygen and water has been studied. The presence of traces of oxygen in both pure and dry CO_2 leads to an increase in nascent ozone concentrations. In contrast, traces of water vapour (0-800 ppm) are shown to rapidly suppress ozone concentrations with the largest decreases being observed at lowest gas pressures in the discharge (300 Torr). The presence of water vapour did not considerably affect the electrical properties of negative dc corona suggesting that a chemical process is responsible for the ozone loss. We have shown that the addition of water up to a concentration of 1500 ppm has only a marginal effect on the processes of ozone formation but the catalytic cycle of ozone destruction involving OH radicals can be the reason for observed decrease in the total ozone concentration with increasing water concentration.

International Nuclear Information System (INIS)

Throughout the last decades, plasma technology has been established in a series of surface treatment applications, e.g. for semiconductor processing or optical coatings. The majority of plasma assisted technologies is based on low pressure processes. In recent years, however, non-thermal atmospheric pressure discharges have attracted considerable interest because of their simplified technical devices for industrial applications as compared to low pressure processes which require vacuum equipment. Hence, batch processing can be avoided, thus facilitating the implementation of plasma process steps into production lines. Investment costs are cut down significantly. The use of atmospheric pressure plasmas for technical applications dates back to the ozone production with dielectric barrier discharges (DBD) by Siemens in 1857. Lately, the application of atmospheric pressure plasmas for surface treatment has been reported, e.g. for the treatment of foils to improve ...

Science.gov (United States)

No abstract prepared.

Science.gov (United States)

... Accession Number : ADD001040. Title : Process for Uniformly Depositing Resin in Combustible Cartridge Cases. Descriptive Note : Patent,. ...

Energy Technology Data Exchange (ETDEWEB)

In the framework of the European Fusion Technology Programme ECN participates in a NET task PSM-8 `Coatings and Surface Effects on Stainless Steel 316L`. High emissivity coatings were developed for enhanced heat transfer from graphite tiles to a Stainless Steel First Wall. Four candidate materials, Cr{sub 2}O{sub 3}, Black Cr, Al{sub 2}O{sub 3}/TiO{sub 2} and TiC were tested as candidate high emissivity coatings. These coatings were manufactured by atmospheric and vacuum plasma spraying technique and the Black Chromium coatings were manufactured by a galvanic coating technique. The tests included total emissivity measurements and Low Cycle Fatigue (LCF) experiments. The total emissivity of two TiC coatings at 525 K appeared to be 0.62 and 0.64. The total emissivity of the TiC and 5 wt% TiO{sub 2}/Al{sub 2}O{sub 3} ...

International Nuclear Information System (INIS)

In this paper, the influence of plasma nitriding at temperature 720 deg. C for 20 h on the surface microstructure and interface microstructure of electroplated chromium coating was investigated. In these conditions, interdiffusion, mixing and reaction phenomena of elements originating from the substrate and coating material are more likely to occur, thus increasing the bonding strength between the coating and carbon steel substrate. The change of the structures from the substrate side to the coating surface, and the effect of the substrate steel on the interface structure were studied by cross-sectional transmission electron microscope observation (XTEM). The nitride layer formed on the surface was analyzed by X-ray diffraction method (XRD). After treatment at above conditions a 6-7 #mu#m thick nitride compound layer was formed in surface region and the same thick carbide compound layer was also formed ...

British Library Electronic Table of Contents (United Kingdom)

Assembly of icosahedral capsids of proper size and symmetry is not understood. Residue F170 in bacteriophage P22 coat protein is critical for conformational switching during assembly. Substitutions at this site cause assembly of tubes of hexamerically arranged coat protein. Intragenic suppressors of the ts phenotype of F170A and F170K coat protein mutants were isolated. Suppressors were repeatedly found in the coat protein telokin-like domain at position 285, which caused coat protein to assemble into petite procapsids and capsids. Petite capsid assembly strongly correlated to the side chain volume of the substituted amino acid. We hypothesize that larger side chains at position 285 torque the telokin-like domain, changing flexibility of the subunit and intercapsomer contacts. Thus, a sing...

International Nuclear Information System (INIS)

The article deals with the effects of various hazardous materials in the working environment. Some of these may be detrimental to the safety and health of the worker. The absorption of hazardous substances by the human body is discussed, as well as the effects of toxic substances. The hazardous substances are classified into the following categories: irritants, asphyxiants, anaesthetics and narcotics, carcinogens, mutagens, teratogens, systemic poisons, hazardous particulate matter and the biotransformation of toxic substances. Examples of hazardous substances include: industrial solvents, fumes and vapours, lead, mercury and uranium.

Energy Technology Data Exchange (ETDEWEB)

The effective half-life based on urine bioassay results of Wolsung NPP's worker was calculated. The effective half-life for tritiated water vapour obtained was 5 {approx} 9 days. In comparison to 10 days reported for ICRP-30, it is lower than the corresponding half-life for Reference Man. Also, the half-life was calculated based on intake amount of daily water. According to this result, the metabolism was reviewed.

UK PubMed Central (United Kingdom)

The objective of this work was to evaluate the physical properties and in vivo circulation of chitosan (CH)-coated liposomes of mitoxantrone (MTO). Changes in particle size and zeta...Full Text Available

UK PubMed Central (United Kingdom)

A serological trapping technique for detecting rotaviruses is described which involves coating electron microscope grids with protein A and specific rotavirus antiserum. The presence of a layer of antibodies...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This study investigates the effect of solid and liquid lubrication on friction and wear performance of silicon nitride (Si{sub 3}N{sub 4}) and cast iron. The solid lubricant was a thin silver film ({approx}2 {mu}m thick) produced on Si{sub 3}N{sub 4} by ion-beam-assisted deposition. A high-temperature polyol-ester-base synthetic oil served as the liquid lubricant. Friction and wear tests were performed with pin-on-disk and oscillating-slider wear test machines at temperatures up to 300{degrees}C. Without the silver films, the friction coefficients of Si{sub 3}N{sub 4}/Si{sub 3}N{sub 4} test pairs were 0.05 to 0.14, and the average wear rates of Si{sub 3}N{sub 4} pins were {approx}5 x 10{sup -8} mm{sup 3} N{sup -1}. The friction coefficients of Si{sub 3}N{sub 4}/cast iron test pairs ranged from 0.08 to 0.11, depending on test temperature. The average specific wear rates of cast iron pins were {approx}3 x 10{sup -7} mm{sup 3} N{sup -1} m{sup -1}. However, ...

Energy Technology Data Exchange (ETDEWEB)

YBCO films were fabricated on PLD-CeO{sub 2}/IBAD-Gd{sub 2}Zr{sub 2}O{sub 7}/Hastelloy substrates using the advanced TFA-MOD process. The effective thickness of the CeO{sub 2} buffer layer for obtaining high I{sub c} was investigated in short samples of YBCO films. The CeO{sub 2} buffer layer was epitaxially grown on an IBAD-Gd{sub 2}Zr{sub 2}O{sub 7} template tape with 18 deg. of {delta}{phi} by a reel-to-reel PLD system. The in-plane grain alignment of PLD-CeO{sub 2} buffer layers rapidly improved with the thickness and saturated at a critical thickness of 0.8 {mu}m. The size of CeO{sub 2} grains was about 1 {mu}m at the saturated thickness of {delta}{phi}. YBCO films with the thickness of 1 {mu}m were deposited by the TFA-MOD on the CeO{sub 2} buffer layer with different thickness films. Improvement of the CeO{sub 2} in-plane grain alignment resulted in increase of I{sub c}. The I{sub c} values of 250-290 A were obtained with the CeO{sub 2} layer thicker than ...

International Nuclear Information System (INIS)

A report is given on an improved filler-binder mixing method in the manufacture of artificial graphite, the so-called coat-mix process. The individual graphite-filler grains are coated completely with uniform binder coatings (phenol formaldehyde resin) in a continuous process. Methanol is used as solvent for the resin. In a modified further development of the process, the use of organic solvents can be disregarded by dissolving the binder resin in caustic soda and injecting the slurry into water diluted acid. The manufacture of casting molds from coat-mix powders, their properties and industrial application are given. Finally, the advantages of using carbon bodies of coal-mix material for conversion to silicon carbide are indicated. (IHOE).

Science.gov (United States)

... The data were transformed into total hemispherical emittance values and correlated with respect to ceramic coating thickness and temperature ...

Energy Technology Data Exchange (ETDEWEB)

This book describes the uses, coatings, and fabrication of laser materials. Topics considered include: optical waveguide materials; optical storage materials; holographic recording materials; phase conjunction materials; holographic recording materials; phase conjunction materials; laser crystals; laser glasses; quantum counter materials; thin films and coatings; multilayer dielectric coatings; graded-index surfaces and films; optical materials fabrication; fabrication techniques; fabrication procedures for specific materials.

Energy Technology Data Exchange (ETDEWEB)

The theoretical principles underlying the formation of oxide and, in particular, anodic oxide coatings on metals produced by chemical oxidation, anodizing in solutions, and anodizing in cold plasmas are reviewed. The mechanisms and conditions of anodic oxidation are described, and the structure of anodic oxide coatings on aluminum, magnesium, beryllium, zinc, cadmium, iron, cobalt, nickel, titanium, zirconium, tantalum, and chromium alloys is examined. Attention is also given to various applictins of anodized coatings. 54 references.

Energy Technology Data Exchange (ETDEWEB)

The method of production of xAl{sub 2}O{sub 3}-yTiO{sub 2} compositions provides for the depth distribution of coating components and specifies its mechanical properties. In case of the composition obtained by cladding, titanium is mainly concentrated at the substrate. In case of mechanical mixture or composition obtained by sintering the oxides, the depth distribution of coating components is random.

International Nuclear Information System (INIS)

Research highlights: ? Reports a high protection system for the alloy in corrosive environment. ? Describes an interfacial process with self-healing properties. ? Reports the influence of substrate pre-treatment in the coating performance. - Abstract: In this paper the interface of poly(vinylidene fluoride) coatings prepared by the dip coating method and HF-treated AZ31 magnesium alloy was evaluated. The best performance of this system in corrosion tests compared to ground, as-received and acetic acid cleaned substrates is related to an acid-base interaction at the interface and to interfacial reactions which resulted in a self-healing process. The protectiveness of the samples was investigated using impedance and immersion tests while the coating morphology and interface stability were investigated by scanning electron microscopy, X-ray photoelectron spectroscopy and adhesion tests.

Energy Technology Data Exchange (ETDEWEB)

The effect of the coated composite surface of particles on the mechanical properties of the powder bed was investigated. Polyethylene-silica surface composite powder was prepared at several coating ratios with Hybridizer. Various tests on mechanical properties of the powder bed were carried out with the prepared powder, and the following results were obtained: The ultimate tensile strength depends only on the cohesive force between particles, and the contact probability model of composite particles led to good agreement between the experimental and calculated values. The coefficient of internal friction and cohesive shear strength were influenced due to the interlocking effect of the surface roughness of composite particles. The effects of coating particles became small with dynamic properties like angle of repose. It is possible to control the mechanical properties in a step wise fashion by changing the ...

British Library Electronic Table of Contents (United Kingdom)

Analysis reproducibility and detection sensitivity of capillary electrophoresis (CE) are often questioned by applied scientists, which has hindered its application as a routine method. To address these issues, a simple, precise, and reproducible dynamic coating method was developed by applying carboxymethyl chitosan (CMC) dynamic coating on fused silica capillary. The proposed coating was accomplished by simply rinsing the capillary with CMC solution for 1?min in between runs, with no regeneration procedure or buffer additives needed. Electroosmotic flow could be well controlled by adjusting the pH of background electrolyte, and the adsorption of analytes onto the capillary inner wall was effectively eliminated. The main parameters of the coating condition were optimized, and extensive app...

Energy Technology Data Exchange (ETDEWEB)

Ion storage CeO{sub 2} and CeO{sub 2}/SnO{sub 2} coatings were prepared by sol-gel dip-coating method using aqueous-based process. The influence of added SnO{sub 2} in the CeO{sub 2} oxide coatings on the inserted/extracted charge was determined by chronocoulometric measurements. It was found that for 60 nm thick film the inserted/extracted charge was twice larger (Q = 10mC/cm{sup 2}) for films containing 17 mol % SnO{sub 2} if compared to pure CeO{sub 2}. The addition of SnO{sub 2} to the mixed oxides coatings on their optical properties and structural characteristics were studied.

British Library Electronic Table of Contents (United Kingdom)

The determination of residual stress (RS) in case-hardened steel gear truck synchronisers coated with thermal sprayed molybdenum was carried out using neutron and synchrotron X-ray diffraction. Two samples with different coating thicknesses (about 120 ?m and 1.4 mm) and different steel substrates (16MnCr5 and SAE4140, respectively) were investigated. Microanalysis revealed substantial porosity in both samples and some debonding was observed between the thin coating and the substrate. The bulk hardness of the SAE 4140 proved to be much higher than the 16MnCr5 and the surface case-hardening increased it by a further 20%. The full three-dimensional stress depth-profile was determined by neutron diffraction (ND) in both the coatings and the substrates, while synchrotron radiation allowed a dep...

British Library Electronic Table of Contents (United Kingdom)

Abstract Introduction.- Infection is the worst complication seen with inflatable penile prosthesis (IPP). Both the American Medical Systems (AMS) and Coloplast IPP have infection retardant coatings. AMS is coated at the factory with rifampicin and minocycline (InhibiZone). The Coloplast IPP has a hydrophilic coating covalently bonded to its components that will absorb any aqueous solution before implantation and provides increased surface lubricity to decrease bacterial adherence. Aim.- We tested several antibiotic dips comparing zones of inhibition (ZOI) against five commonly infecting bacteria with coated Coloplast implants. Results were compared with those ZOI created with strips of an AMS IPP precoated with InhibiZone. Methods.- Pieces of sterile Coloplast Titan IPP were dipped in (i) ...

British Library Electronic Table of Contents (United Kingdom)

A Ni3Al coating was prepared by plasma spraying technique on the surface of titanium alloy. Ni-Al mixed powders, coatings and reaction products were investigated by scanning electron microscope, EDS, DSC and XRD. A tight bonding between the coating and the substrate was formed. The X-ray diffraction analysis of the patterns showed that the coating not only had Ni3Al phase, but also had NiO and Al2O3 phase microcontent. Comparing Ni coated Al to Ni3Al at 900^oC, the diffusion was stronger and the diffusion layer was thicker. A minute pore structure was formed at 1200^oC in the front edge of solid-state reaction layer. So Ni3Al restrained the solid-state reaction of the coating with the substrate, and as a whole weakened the entry of oxygen atoms into the substrate and quenched the out-diffu...

Energy Technology Data Exchange (ETDEWEB)

This SBIR Phase I developed neutron detectors made from gallium arsenide (GaAs) p-type/ intrinsic/n-type (P-I-N) diodes grown by metalorganic chemical vapor deposition (MOCVD) onto semi-insulating (S1) bulk GaAs wafers. A layer of isotonically enriched boron-10 evaporated onto the front surface serves to convert incoming neutrons into lithium ions and a 1.47 MeV alpha particle which creates electron-hole pairs that are detected by the GaAs diode. Various thicknesses of ''intrinsic'' (I) undoped GaAs were tested, as was use of a back-surface field (BSF) formed from a layer of Al{sub x}Ga{sub 1-x}As. Schottky-barrier diodes formed from the same structures without the p+ GaAs top layer were tested as a comparison. After mesa etching and application of contacts, devices were tested in visible light before application of the boron coating. Internal quantum efficiency (IQE) of the best diode near the GaAs bandedge ...

Energy Technology Data Exchange (ETDEWEB)

We report for the first time about a micromachined mass flow sensor directly integrated between the double guidance and the needle seat into the body of a Common Rail (CR) injection nozzle. The thermal measurement principle was chosen because gaseous as well as liquid mass flows can be determined fast and precisely. Additionally, with glass-ceramic materials fabricated in a low cost batch process, a high temperature and especially pressure stable substrate can be used. The flow sensitive thin film is realized by an e-beam evaporated 110 nm thick molybdenum (Mo) layer. The latter is electrically characterized by the resistivity of {rho} = 8.2 x 10{sup -7} {omega} m ({+-}2%) at room temperature as well as by the first {alpha}=4.5 x 10{sup -4} K{sup -1} ({+-}5%) and second {beta}=3.0 x 10{sup -6} K{sup -2} ({+-}12%) temperature coefficients of resistance up to 300 C. The static temperature field at and around the thin film sensor on the glass-ceramic substrate is investigated with an IR ...

Energy Technology Data Exchange (ETDEWEB)

Out of concern for the global environment, technologies for coal-fired combined cycle power generation are under development throughout the world today, aiming at highly efficient use of coal. Under these circumstances, the authors and others, with the intention of producing a coal-fired combined cycle power generation system with higher plant efficiency, lower construction cost, and higher reliability than conventional systems, proposed a new gasification combined cycle power generation system that differs from the conventional IGCC system. The authors studied system configuration and conducted elementary research necessary for implementing the system. This report deals with the basic concepts of the system and the results of basic studies carried out to realize of the concepts, including a study on alkali metal vapour concentration in relation to heat corrosion; the relation between gas de-dusting temperature and gas alkali metal vapour ...

International Nuclear Information System (INIS)

Research highlights: The dental implant of titanium could be modified by anodic oxidation. It was found that incorporation of strontium ions into the matrix increase the bone formation. In this study, we try to investigate the effect of corrosion property and bioactivity on coatings containing strontium by anodic oxidation. The results suggest that coatings containing strontium on titanium by anodic oxidation has the potential to show the stability and bioactivity in the clinical use. - Abstract: Pure titanium (Ti) and titanium alloys are considered as bio-inert materials in clinical use. Bioactivity is the ability to induce bone-like apatite on the material surface. The micro-arc oxidation (MAO) technique is an effective method for improving the surface properties of titanium. The aim of this study was to investigate the bioactivity and corrosion behavior of MAO coatings containing strontium, which is beneficial for ...

International Nuclear Information System (INIS)

Microbial population and moisture content of traditional herbal medicines contaminated with 3 kinds of aerobic microbes, packed in 5 kinds of plastic packaging materials, followed by irradiation at minimum dose of 5 kGy and stored for 6 months were investigated. The highest reduction of microbial counts during storage was observed on samples packed in polyethylene bags. All of packaging materials used were found to be impermeable to microbes and water vapour. Radiation and packaging materials used acted synergistically to inactivate microbes durind storage. The microbial counts decreased as much as 2 to 4 log cycles during storage. (author).

International Nuclear Information System (INIS)

The foils of various materials were irradiated with "6"0Co with an activity of 11,538 TBq. The minimum radiation dose was 25 kGy. Changes in chemico-physical properties were evaluated by infrared spectroscopy and were not detected after irradiation with 25 kGy. Packing foils were subjected to the following tests: mechanical tests, tests of weld strength, tests of impact resistance, free fall tests, permeability tests for water vapour and microbiological tests. The results of all tests were tabulated. The tests showed that the foils are impermeable for microorganisms and provided the welds are airtight the packed products remain sterile. (J.P.).

International Nuclear Information System (INIS)

Tritium is produced in large quantities at heavy water nuclear power reactors via the neutron activation reaction "2H(n,#gamma#)"3H. At Wolsung nuclear power plant which has a CANDU reactor, the tritium concentrations in coolant and in moderator systems are 1.5 Ci/Kg-D_2O and 35 Ci/kg-D_2O, respectively, after 12 years of operation. The airborne tritium concentration in main access area is normally less than 5 MPCa except short-term peaks. The average tritium concentrations in main access controlled areas are normally less than 100 MPCa. Tritium is mainly present in the air of workplace of CANDU reactors as a tritiated water vapour. Airborne tritiated water vapour enters the workers body via inhalation and absorption through skin and can result in a significant dose. The occupational doses from tritium at Wolsung NPP have been maintained below 1 man-Sv per year so far. The tritium contribution to the total plant man-Sv changes between 30 ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes an investigation of electrodeposited Zn-14% Ni and aluminium-based SermeTel 1140/962 coatings as possible replacements for cadmium. Slow strain rate tests were performed to measure the extent of direct hydrogen embrittlement of a high strength steel substrate as a result of the coating process and of hydrogen re-embrittlement caused by coating corrosion. The level of re-embrittlement was shown to depend on both the electrochemical potential of the coating and its barrier properties. Zn-14% Ni coatings caused the most re-embrittlement as they had the most active potential and contained through-thickness defects which left the steel exposed to hydrogen uptake. The microstructure of the high strength steel was also shown to be an important factor affecting the extent of embrittlement. AerMet 100 steel was more resistant than 300M steel and this was attributed to ...

Energy Technology Data Exchange (ETDEWEB)

Several types of coatings have previously been visually identified on the surface of 105-K East and 105-K West Basins fuel elements. One type of coating (found only in K West Basin) in particular was found to be a thick translucent material that was often seen to be dislodged from the elements as flakes when the elements were handled during visual examinations (Pitner 1997). Subsequently it was determined (for one element only in a hot cell) that this material, in the dry condition, could easily be removed from the element using a scraping tool. The coating was identified as Al(OH){sub 3} through X-ray diffraction (XRD) analyses and to be approximately 60 {micro}m thick via scanning electron microscopy (SEM). However, brushing under water in the basin using numerous mechanical strokes failed to satisfactorily remove these coatings in their thickest form as judged by appearance. Such brushing was done ...

International Nuclear Information System (INIS)

The photon rupture method, by which oxide film and metal are removed by focused pulsed Nd-YAG laser beam irradiation, was applied to form artificial micro-pits in Zn-5 mass% Al alloy-coated steel. The zinc alloy-coated layer was removed by pulsed laser irradiation treatment for about one second in a neutral buffer solution with NaCl. The rest potential transient with the laser treatment was measured. In the early stage of the laser treatment the rest potential of zinc alloy-coated steel changed to the negative direction immediately after every irradiation of a laser pulse and then returned to the previous value. However, after the steel substrate was exposed to the solution, the rest potential moved to the positive direction immediately after every irradiation of a laser pulse and then returned to the previous value. The amplitude and duration of the potential change after the laser irradiation increased with repetition of ...

Energy Technology Data Exchange (ETDEWEB)

Lower cost painting flock-like in appearance and touch feeling was developed as a new surface softening method for automobile interior plastic molded parts. The base coat with the same color as piles mixed into a top coat was first painted on the surface of a plastic molded part after cleaning, and after the top coat with less pitch mixed with piles was painted on the wet base coat and dried by a heater, excess piles were removed with suction and air blowing to produce flock-like appearance. Nylon 66 of 0.4mm in length was used as piles, and mixed into the top coat by 8.0wt% in content. This painting method was applicable to even such parts as one with a complex configuration, and one impossible to set piles on it by conventional methods because of poor durability. As a certain amount of piles with different colors were mixed into the top coat, sprinkly colored ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Researchers are developing polymer-based coating systems to reduce scaling and corrosion of air-cooled condensers that use a geothermal fluid spray for heat transfer augmentation. These coating systems act as barriers to corrosion to protect aluminum fins and steel tubing; they are formulated to resist the strong attachment of scale. Field tests have been done to determine the corrosion and scaling issues related to brine spraying and a promising organometallic polymer has been evaluated in salt spray tests.

Energy Technology Data Exchange (ETDEWEB)

A zinc/air battery is claimed whose performance is improved by omitting separating elements such as diaphragms etc. The cathode and anode spaces are separated by a collector with holes big enough to permit the electrons to pass freely while restraining the anode material. Further, the active material consists of a spherical care of inert material with a zinc coating. Under the zinc coating, the spherical particles have another thin coating of an electropositive material, e.g. nickel. The cell also contains means for circulating the anode suspension.

Energy Technology Data Exchange (ETDEWEB)

On the basis of cylindrical roller thrust bearings it was systematically examined to what extent PVD-coatings are able to take over the function of EP/AW-additives. The bearings were tested under heavy-duty conditions in order to distinguish very fast the efficiency of different coating-substrate-systems. Several coatings were tested for their ability to protect an un-coated counterpart. So just the washers of the roller bearings were coated, the rollers stayed un-coated. Four Me-C:H-coatings showed the best performance and fulfilled the required criterion for roller bearings in the boundary friction: low loss of mass and hardly surface deviation. Material carryover from the carbonaceous coating to the 100Cr6 steel surface was developed by the Me-C:H-coatings during the tests. This mechanism was able ...

International Nuclear Information System (INIS)

The possibilities to grow isolated structures of complex oxides by pulsed laser deposition through stencils were investigated. A stencil consisting of a SiN membrane with apertures of several hundred nanometers embedded in a Si chip is placed in front of a heated substrate (up to 750 degrees Celsius). Deposition through these apertures results in resistless, direct patterning by local deposition of complex oxides like ferroelectric Lead Zirconate Titanate. The created isolated structures were analyzed by AFM imaging. Under-deposition, in this work called broadening, is inevitable during stencil deposition and is depending on deposition parameters, especially pressure. Different causes of broadening are mapped and discussed.

British Library Electronic Table of Contents (United Kingdom)

A stable BSA blocking poly(dimethylsiloxane) (PDMS) microchannel was prepared based on in situ synthesized PDMS-gold nanoparticles composite films. The modified microchip could successfully suppress protein adsorption. The assembly was followed by contact angle, charge-coupled device (CCD) imaging, electroosmotic flow (EOF) measurements and electrophoretic separation methods. Contact angle measurements revealed the coated surface was hydrophilic, water contact angle for coated chips was 45.2^o compared to a water contact angle for native PDMS chips of 88.5^o. The coated microchips exhibited reproducible and stable EOF behavior. With FITC-labeled myoglobin incubation in the coated channel, no fluorescence was observed with CCD image, and the protein exhibited good electrophoretic effect in ...

Science.gov (United States)

drical Enclosures Using a Numerical Ray Tracing Technique. NASA. TM-I02527, 1990 . Buckley, H.: Radiation from the Interior of a Reflecting Cylinder. Philos. ...

Science.gov (United States)

... 31. New electric forming methods offer potentials for light metals; magnetic forming and plasma forming. ... 3, 25 Magnetic Forming ..... ...

Science.gov (United States)

COATINGS FOR THE METAL-SEMICONDUCTOR SOLAR CELLS 3S GIVEN. THIS METHOD UTILIZES THE MEASURED EQUIVALENT INDEX OF. REFRACTION OBTAINED FROM ELLIPSOMETRY ...

Energy Technology Data Exchange (ETDEWEB)

The main purpose of solid or fluid lubricants in ball-bearings is to separate the balls and races from contacting each other in so-called asperity collisions. Steel to steel contacts lead to microwelds which roughen functional rolling-contacting surfaces and deteriorate the lubricant. By using balls with a ceramic TiC coating, two goals are achieved. First, there are fewer asperity collisions because of the extreme smoothness of the high precision polished TiC coated balls. Second, if collisions do occur, there is practically no microwelding taking place, leaving the surfaces and the lubricant in good condition. Examples are given where the bearing lifetime is increased up to 10 times if the steel balls are replaced by TiC-coated balls. (orig.).

British Library Electronic Table of Contents (United Kingdom)

Polymer-coated magnetic nanoparticles (MNPs) have been prepared and used as an immobilization matrix for the fabrication of solid-state tris(2,2prime-bipyridyl)ruthenium(II) (Ru(bpy)32+) electrogenerated chemiluminescence (ECL) sensor. The pre-synthesized maghemite (g-Fe2O3) MNPs were coated with poly(3-thiopheneacetic acid) based on an oxidative polymerization method using KMnO4. The poly(3-thiopheneacetic acid)-coated MNPs have formed the clusters with average diameter of 200-500nm. The multilayer films of poly(3-thiopheneacetic acid)-coated MNPs were uniformly formed on the surface of a Pt electrode by an external magnet. The Ru(bpy)32+ was rapidly incorporated into the multilayer films within 5min through the electrostatic interaction between the Ru(bpy)32+ and the negatively charged c...

British Library Electronic Table of Contents (United Kingdom)

A test bench was designed and assembled to carry out impact tests on samples and components. The system allows simple and rapid adjustment of the test parameters, such as the shot size and air pressure, with good repeatability of the results. Tests on steel and light alloys were carried out under both as-produced condition and on thin hard-coated samples. Significant reductions in dimple dimensions were seen after coating. FE models simulating the experiments overestimated the dimple depths, although the parameter trend was satisfactorily captured. The residual stresses from coating and shot peening determined numerically are believed to have been proven effective against fatigue.

British Library Electronic Table of Contents (United Kingdom)

Fluorocarbon polymers are used to enhance thermal stability and electrostatic protection of composite propellant compositions. A precipitation technique has been developed to coat ammonium perchlorate (AP) using a copolymer of hexafluoropropylene and vinylidene fluoride (HFP-VF) with the help of solvent-counter solvent method. The coated AP has been used to prepare propellant compositions in different ratio based on hydroxyl terminated polybutadiene (HTPB), aluminium powder along with uncoated AP and studied for viscosity build-up and visco-elastic behaviour as well as mechanical, ballistic, thermal and sensitivity properties keeping 86% solid loading. The data on viscosity build-up indicate that as the percentage of viton coated AP increases end of mix viscosity and viscosity build-up inc...

International Nuclear Information System (INIS)

In the present study, surfaces of cylinder head, piston, exhaust and inlet valve of a four-stroke, direct injection, single cylinder diesel engine were coated with molybdenum (Mo) by plasma spray method. Thus, thermal barrier characteristic was brought to these parts. Variances in performance and emission values of cotton methyl ester and 2D fuel mixtures were studied in the ceramic coated and uncoated engines under the same running conditions. Performance (6.0% for specific fuel consumption) and emission values (up to 18.0% for CO, 8.0% for smoke density) of the test fuel were improved in the coated engine compared with the uncoated engine. NO_x increase (4.5%) with the increased temperatures expected in the coated engine.

International Nuclear Information System (INIS)

YBa_2Cu_3O_7_-_x thick films have been deposited on silver sheets and MgO single crystals by spray pyrolysis. Film texture is related to film thickness and sintering temperature. The X-ray intensity ratio of the 005 peak to the 110 peak is higher for thin films deposited at the higher temperatures. However, elevated temperatures promote copper diffusion and second-phase formation in films deposited on silver. Films deposited on MgO can have larger grain sizes and are more oriented than those deposited on silver.

Energy Technology Data Exchange (ETDEWEB)

A new magnetic macroparticle filter design consisting of two 90{sup o} filters forming an S-shape is described. Transport properties of this S-filter are investigated using Langmuir and deposition probes. It is shown that filter efficiency is product of the efficiencies of two 90{sup o} filters and the deposition rate is still acceptably high to perform thin film deposition. Films of amorphous hard carbon have been deposited using a 90{sup o} filter and the S-filter, and macroparticle content of the films are compared.

Energy Technology Data Exchange (ETDEWEB)

The understanding of fission product deposition in realistic steam generator conditions is needed for release estimates in PSA studies, and for the design of efficient accident management procedures. This is considered very important because primary-to-secondary leakages risk dominant sequences in many plants. Furthermore, the decay heat of the fission product deposits adds to the thermal load to the steam generator tubes also in other sequences, especially in case of cold leg leakages. This brings out the concern of induced steam generator tube ruptures in cases, where the steam generators are initially intact. The experimental data showed that the highest deposited fraction within the tubes were found in cases with lowest flow velocities. The minimum value of the deposited fraction was observed at intermediate flow velocities. With these relatively low Reynolds numbers, the results calculated with ...

Energy Technology Data Exchange (ETDEWEB)

Micron-size Ni-base alloy (NBA) powders were mixed with both 1.5 wt.% (hereinafter %) micron-size CeO{sub 2} (m-CeO{sub 2}) and also 1.5% and 3.0% nano-size CeO{sub 2} (n- CeO{sub 2}) powders. These mixtures were coated on low-carbon steel (Q235) by 2.0 kW CO{sub 2} laser cladding. The effects on the microstructures, phases and electrochemical corrosion of the coatings upon the addition of m- and n- CeO{sub 2} powders to NBA (m- and n- CeO{sub 2} /NBA) have been investigated. The results showed that a smooth coating was prepared under suitable processing parameters (P= 2.0 kW, V= 180 mm min{sup -1}) by adding 1.5% n- CeO{sub 2}. In addition to the primary phases of {gamma}-Ni, Cr{sub 23} C{sub 6} and Ni{sub 3} B in the Ni-base alloy coating, CeNi{sub 3} was formed in Ni-base alloy coatings with both n- CeO{sub 2} and m-CeO{sub 2} particles, and CeNi{sub 5} appeared in the ...

International Nuclear Information System (INIS)

This rebuttal to a previous article provides new insight into the use of sprayed sealants in uranium mines. The author rejects the idea that the value of rock sealant on radon control is destroyed by changes in barometric pressure, showing that this is not necessarily true. The analyses described demonstrate that radon contamination resulting from changing barometric pressures is reduced by a rock coating. The overall use of coatings depends on their costs and effectiveness as compared with other radon control measures. 6 refs.

International Nuclear Information System (INIS)

A super-hydrophobic coating was prepared by combining a rigid base film with crater-like hemispherical holes and acicular nanoparticles. The acicular boehmite powder provides a high contact angle on the film surface. The rigid base film with crater-like hemispherical holes inhibits the rapid decrease of contact angle by surface rubbing. The combination of different roughness is an effective method for improving the abrasion resistance of super-hydrophobic films.

Energy Technology Data Exchange (ETDEWEB)

Thin solid films of CeO[sub 2] and mixed CeO[sub 2]-TiO[sub 2] were prepared by the sol-gel route via the dip-coating technique. Particulate sols of ceria were made from inorganic ((NH[sub 4])[sub 2]Ce(NO[sub 3])[sub 6]) precursor which were used for preparation of CeO[sub 2] thin solid films while CeO[sub 2]-TiO[sub 2] coatings have been made by using mixed organic-inorganic (Ti(OiPr)[sub 4] and CeCl[sub 3].7H[sub 2]O) precursors. The solar transmission values (T[sub s]) of both coatings are in the range 0.6-0.8 and depend on coating thickness. Cyclic voltammetric (CV) measurements show that the CeO[sub 2]/LiOH system exhibits higher overall electrochemical reversibility when compared to the CeO[sub 2]-TiO[sub 2]/LiOH system. The CeO[sub 2]/LiOH system is also less sensitive with regard to the coating thickness. Coulometric measurements show that CeO[sub 2] exhibits a larger ...

Energy Technology Data Exchange (ETDEWEB)

A portable fiber optic detector that senses the presence of specific target chemicals by electrostatically attracting the target chemical to an aromatic compound coating on an optical fiber. Attaching the target chemical to the coated fiber reduces the fluorescence so that a photon sensing detector records the reduced light level and activates an appropriate alarm or indicator.

Energy Technology Data Exchange (ETDEWEB)

Coatings and sensors having both steric and chemical selectivity. Controlled porosity provides the steric selectivity, whereas chemically tailored film properties, using controlled composition or modification by coupling agents, chemical species replacement, or chemical species within pores, provide the chemical selectivity. Single or multiple layers may be provided.

Energy Technology Data Exchange (ETDEWEB)

In this work a comprehensive metallophysical study was carried out for two aluminosilicide slip coatings of the systems Al-Si and Al-Nb-Si and an electron-beam Co-Cr-Al-Y coating on alloy EP-539 (17...19% Cr, 4...6% Co, 2.5...4% W, 4.5...6.5% Mo, 2...3% Ti, 3...4% Al, 1.4...2% Nb, balance Ni) after high-temperature testing. The protective properties of the coatings were evaluated from the results of laboratory tests for heat resistance at 1000/sup 0/C in the combustion products of diesel fuel with added sulfur at 970, 1000, and 1060/sup 0/C for 100 h and after full-scale tests for 150, 250, 400, and 700 h. Metallographic, hardness, x-ray, and micro x-ray studies of the coating were carried out. Layer-by-layer phase composition and the lattice spacing of the main phases were determined. X-ray analysis was carried out in an a DRON-1 diffractometer in copper K/sub ..-->../-radiation, and x-ray ...

Energy Technology Data Exchange (ETDEWEB)

This paper introduces a new method to produce nano-composite powder for the preparation of high performance ZnO varistors. ZnO particles were coated with Bi{sub 2}O{sub 3}, Sb{sub 2}O{sub 3}, Co{sub 2}O{sub 3}, Cr{sub 2}O{sub 3} and other additives via liquid nano-coating technique. Then the prepared powder was characterized by scanning electron microscopy (SEM), transmission electron microscopy (TEM), thermal gravity and differential scanning calorimetry (TG-DSC) and particle size distribution. The results showed that the ZnO composite powder is homogeneously coated and ultrafine. The densification, phase composition and microstructure of ZnO varistors was studied by linear shrinkage, X-ray diffraction (XRD) and SEM, respectively. The preliminary electrical parameters of ZnO varistors showed that the breakdown voltage V {sub b} (1 mA/cm{sup 2}) and nonlinear coefficient {alpha} is 5400 V/cm and 50, respectively, much ...

CERN Document Server

Non-evaporable thin film getters of various compositions have been produced by sputtering. Among about 20 materials which have been studied, the lowest activation temperature (about 180 degree C) has been displayed by a Ti-Zr-V coating obtained from a cathode made of intertwisted elemental wires. In order to optimize the vacuum properties of this film various production parameters, including the substrate temperature during coating, have been varied. The films have been characterized by pumping speed measurement, secondary electron microscopy, and X-ray diffraction. It has been found that the substrate coating temperature affects significantly the activation temperature, the pumping speed and the gas surface capacity. The highest pumping speed values, obtained for substrate coating temperatures of 250 degree C and 300 degree C, are clearly correlated with the increased surface roughness and porosity of ...

Energy Technology Data Exchange (ETDEWEB)

A device for detecting neutrons includes a semi-insulated bulk semiconductor substrate having opposed polished surfaces. A blocking Schottky contact comprised of a series of metals such as Ti, Pt, Au, Ge, Pd, and Ni is formed on a first polished surface of the semiconductor substrate, while a low resistivity ("ohmic") contact comprised of metals such as Au, Ge, and Ni is formed on a second, opposed polished surface of the substrate. In one embodiment, n-type low resistivity pinout contacts comprised of an Au/Ge based eutectic alloy or multi-layered Pd/Ge/Ti/Au are also formed on the opposed polished surfaces and in contact with the Schottky and ohmic contacts. Disposed on the Schottky contact is a neutron reactive film, or coating, for detecting neutrons. The coating is comprised of a hydrogen rich polymer, such as a polyolefin or paraffin; lithium or lithium fluoride; or a heavy metal fissionable material. By varying the ...

British Library Electronic Table of Contents (United Kingdom)

A methodology for the determination of the rare earth elements in uranium oxides by ion microprobe has been set up on a Cameca ims-3f instrument. An uranium oxide reference material from a syn-metamorphic uranium deposit related to albitisation has also been developed for this type of analysis. Applications of the methodology are presented for a series of uranium oxides selected from some major uranium deposit types: from the world's highest grade unconformity-related uranium deposit from the Athabasca Basin (Saskatchewan, Canada; the Shea Creek and the McArthur River examples), a perigranitic vein-type deposit (Pen Ar Ran, Vendee, France) and a volcanic caldera-related deposit (Streltsovkoye, Transbaikalia, Russia). Each type of uranium deposit appears to have a specific REE signature. Al...

British Library Electronic Table of Contents (United Kingdom)

In this work an experimental study is carried out to determine the thermo-hydraulic performance of an intercooler (IC) with flat tubes provided with triangular plain internal fins and louvered external fins when it is used on a car equipped with a low pressure EGR. The main unknowns to be answered are the thermo-hydraulic characteristics of the IC working under humid conditions induced by EGR, the conditions under which the water content in the mixture of air and exhaust gases begins to condense and the conditions under which the condensed water will be retained inside the IC. The exhaust gases are here replaced by a mixture of dry air and water vapour which are mixed upstream of the IC. The IC is submitted at the following testing conditions: on the ambient air side, the air temperature i...

British Library Electronic Table of Contents (United Kingdom)

Nanomaterials are increasingly being used to modify adhesives used in aerospace and materials applications. Improvements in thermal and mechanical properties have been found by incorporation of small amounts of nanosize materials in to such adhesives. However, the introduction of nanomaterials to adhesives used in civil engineering applications is still a new approach which needs to be explored, especially in retrofitting of structures. This paper presents part of an ongoing research to address the effect of adding nanomaterials to modify a thermosetting adhesive used for bonding carbon fibre reinforced polymer (CFRP) composites to concrete members. Vapour grown carbon fiber (VGCF) was chosen to modify the adhesive. Different concentrations of carbon nanofibres PR-24 XT-LHT were adopted fo...

International Nuclear Information System (INIS)

Autoionizing and Auger transitions in atomic manganese and samarium have been experimentally investigated by observation of the ejected electrons in the energy region 0 to 40 eV following electron impact excitation with incident beams in the energy range 15-500 eV. Seventy-four spectral features are tabulated for manganese and a number of new assignments have been made based on pseudo-relativistic Hartree-Fock calculations and quantum defect analysis. A similar study of samarium reveals only a number of broad features in the ejected-electron energy range 8-10 eV. Three features have been observed consistently in the ejected-electron spectrum of samarium and assigned by comparison with previous work. (author).

Energy Technology Data Exchange (ETDEWEB)

Solar cells and organic electronic devices require an encapsulation to ensure sufficient lifetime. Key parameters of the encapsulation are permeation barrier, UV stability, temperature stability, optical transmission spectra and mechanical stability. The requirements depend very much on the specific application. Many work groups suggest multilayer stacks to meet the permeation requirements. In this paper the permeation barrier properties of the different constituents of such a multilayer stack are characterized. Different layer materials are compared regarding their water vapour and oxygen permeability as well as the influence of process parameters is examined. Finally temperature dependent permeation measurements are used to characterize the permeation mechanisms in the different constituents of the multilayer barrier.

British Library Electronic Table of Contents (United Kingdom)

A galactose-specific seed lectin was purified from the legume Spatholobus parviflorus and crystallized using the hanging-drop vapour-diffusion technique. Thecrystals belonged to space group P1, with unit-cell parameters a = 60.998, b=60.792, c = 78.179-, = 101.32, = 91.38, = 104.32. X-ray diffraction data were collected under cryoconditions (100-K) to a resolution of 2.04- using a MAR image-plate detector system mounted on a rotating-anode X-ray (Cu-K) generator. Molecular replacement using legume-lectin coordinates as a search model gave a tetrameric structure.

International Nuclear Information System (INIS)

Ultraveiolet spectroscopy of molecules in vapour phase gives valuable information about electronic structure of free molecules. But in many cases vaipour phase investigations are not possible and in order to isolate molecules within solid lattice, we used cryogenic temperature and high vacuum technology to study absorption spectrum within the spectral range (230-270)nm of an isolated benzene molecule in Argon, Krpton, Nitrogen, Carbon and methane matrices. The spectra shifts were measured and calculated in the matrix environment for the electronnic transition (B 24--A 19) in benzene molecule using the matrices mentioned above. Molar extinction coefficients and oscillator strength were measured too. (7 tabs., 32 figs., 50 refs.).

British Library Electronic Table of Contents (United Kingdom)

Analytical relations are obtained for estimating how the distributions of temperature and heat flux vary along a steam-generating tube and how the steam-generator power output reduces due to formation and accumulation of deposits.

International Nuclear Information System (INIS)

The reactive evaporation process was successfully used to deposit films of the A-15 Nb_3Ge phase. This is the first report, to the best of our knowledge, illustrating the use of such processes for the deposition of A-15 compounds. In this process, niobium vapors from an electron-beam-heated evaporation source react with germane gas introduced into the vacuum chamber at low partial pressures (approximately 10"-"4 Torr) to produce Nb_3Ge deposits. The process variables studied were the deposition temperature, the niobium-to-germanium impingement ratio on the substrate and the plasma-enhanced deposition, in this case the activated reactive evaporation process. At low deposition temperatures (below 450"0C) the deposit is amorphous (or microcrystalline) and can be crystallized to the Nb_3Ge phase by heat treatment, e.g. at 850"0C for 1 h in ...

Science.gov (United States)

This report results from a contract tasking Eindhoven University of Technology as follows: The contractor will investigate the plasma treatment of surfaces and plasma enhanced deposition using EUT's cascade arc source as the basis for this effort.

International Nuclear Information System (INIS)

... 194 p. auger electron spectroscopy decomposition deposition interfaces oxygen

International Nuclear Information System (INIS)

Adult and newborn rats were exposed to "2"3"9PuO_2 aerosols of four different size distributions. Rats of both ages were killed at intervals between 1 hr and 60 days postexposure. There were marked age- and particle-related size differences in deposition, although retention was similar throughout. The differences in deposition are attributable to relatively greater deposition of larger particles in the upper respiratory tracts of newborns.

Energy Technology Data Exchange (ETDEWEB)

CeO{sub 2}-coated LiMn{sub 2}O{sub 4} spinel cathode was synthesized using two-step synthesis method. All the samples exhibited a pure cubic spinel structure without any impurities in the XRD patterns. The results of the electrochemical performances on CeO{sub 2}-coated electrode are compared to those of electrodes based on LiMn{sub 2}O{sub 4} spinel without CeO{sub 2} coating. CeO{sub 2}-coated LiMn{sub 2}O{sub 4} cathode improved the cycling stability of the electrode. The capacity retention of 2 wt% CeO{sub 2}-coated LiMn{sub 2}O{sub 4} was more than 82% after 150 cycles between 3.0 and 4.4 V at room temperature and 82% after 40 cycles at elevated temperature of 60 C. The amounts of dissolved manganese-ions in CeO{sub 2}-coated LiMn{sub 2}O{sub 4} significantly are smaller than pristine LiMn{sub 2}O{sub 4} systems especially at elevated temperatures. ...

Energy Technology Data Exchange (ETDEWEB)

As surface treated steel sheets, steel sheets with Zn-Fe coatings as well as double-layer steel sheets with Fe-P alloy coatings on Zn-Fe alloy coatings are often used practically. Two treatment methods, which are used to dissolve only alloy layers without dissolving steel sheets in order to find amount and composition of alloy layersr have already been reported. This report investigates the mechanisms of these methods, particularly the mechanisms to control dissolution of steel sheets. In the alkali-dissolution method, Zn-Fe alloy coatings are dissolved in a strong alkaline solution(NaOH-triethanolamine (TEA)-H{sub 2}O{sub 2}). In this case, steel sheets are insoluble because passive films are formed on the surface. In the cathodic polarization electrolysis method, alloy layers are electrolyzed({minus}l.2V) and dissolved in an ammonium nitrate-0-phen electrolyte. At this potential, dissolution of steel ...

Energy Technology Data Exchange (ETDEWEB)

The hydrogen evolution reaction (HER) was studied on Ni-P{sub x} electrodes containing 8 to 16 weight percent P prepared by potentiostatic deposition. The amount of P in the alloy varied with deposition potential. The activity of the electrodes was dependent on the P concentration, and the formation of a passive film. Cyclic voltametry was used to study the removal of this film. 3 refs.

UK PubMed Central (United Kingdom)

Amyloid-β (Aβ) deposits have been identified as key players in the progression of Alzheimer’s disease (AD). Recent evidence indicates that the deposits probably precede...Full Text Available

British Library Electronic Table of Contents (United Kingdom)

In this study, the effects of channel surface wettability, cross-sectional geometry and orientation on the two-phase flow in parallel gas channels of proton exchange membrane fuel cells (PEMFCs) are investigated. Ex situ experiments were conducted in flow channels with three different surface wettability (hydrophilically coated, uncoated, and hydrophobically coated), three cross-sectional geometries (rectangular, sinusoidal and trapezoidal), and two orientations (vertical and horizontal). Flow pattern map, individual channel flow variation due to maldistribution, pressure drop and flow visualization images were used to analyze the two-phase flow characteristics. It is found that hydrophilically coated gas channels are advantageous over uncoated or slightly hydrophobic channels regarding un...

Energy Technology Data Exchange (ETDEWEB)

In order to improve the well-known short operational life time of BF3 counters, three potential adsorbents for impurity gases (graphite, activated charcoal and a zirconium-aluminum mixture) were introduced into BF3 counters in the form of coating on the aluminum cathode surface. Tests in el fields revealed that a partial coating of activated charcoal provides the best result. The improvement of their operational life in el fields was about three orders of magnitude in terms of tolerable exposure. Many counters with a partial coating of activated charcoal were further tested from the following viewpoints: background noise, vibration and shock, el pulse discrimination, operational life in a neutron field and non-operational in-reactor exposure life. The results were satisfactory for reactor control and protection usage. (author).