International Nuclear Information System (INIS)

Selective formation of ZnO nanodots was accomplished by metalorganic chemical vapor deposition on nanopatterned SiO_2/Si substrates. Self-organized ZnO nanodots were selectively formed in nanopatterned lines of Si created by etching of SiO_2 with focused ion beam (FIB), whereas any nanodots were hardly observed on the SiO_2 surface in the vicinity of the FIB-sputtered Si areas. The mechanism of the selective formation of ZnO nanodots on FIB-nanopatterned lines is mainly attributed to the effective migration of Zn adatoms diffusing on the SiO_2 surface into the Si lines followed by the nucleation at surface atomic steps and kinks created by Ga"+ ion sputtering. Cathodoluminescence measurements confirmed that the emission originated from the selectively grown ZnO nanodots.

International Nuclear Information System (INIS)

In this paper, we present the results of Plasma-Enhanced Chemical Vapor Deposition gate-oxide (SiO_2) integrity on ELC (excimer-laser-crystallized), MILC (metal-induced lateral-crystallized) and SPC (solid-phase-crystallized) polysilicon films. We observed that gate oxide strength of poly-Si TFT strongly depends on the crystallization method for the active silicon layer. In the case of ELC films, asperities on the silicon surface reduce the SiO_2 breakdown field significantly. The metallic contaminants in MILC films are responsible for a deleterious impact on gate oxide integrity. Among the three cases, the SiO_2 breakdown field was the highest for the SPC silicon films. The breakdown fields at the 50 % failure points in Weibull plots for the ELC, MILC and SPC cases were 5.1 MV/cm, 6.2 MV/cm, and 8.1 MV/cm, respectively. We conclude that the roughness and metallic contamination of the poly-Si films are the main factors that cause enhanced ...

International Nuclear Information System (INIS)

Transient enhanced diffusion (TED) and dose loss (pile-up) are investigated for phosphorus-implanted samples covered with both oxide and nitride films. P ions were implanted into p-type (1 0 0) CZ-Si (dose 5x10"1"3 cm"-"3, 100 keV) through a chemical vapor deposition (CVD) Si_3N_4 film. For a half of samples, Si_3N_4 was etched off and SiO_2 films were grown by CVD. Both samples were annealed for 20-360 min at 700 deg. C. Diffusivity of P and the dose loss were estimated based on the secondary-ion mass spectrometry (SIMS) P profiles. Both Si/Si_3N_4 and Si/SiO_2 interfaces were investigated with transmission electron microscopy (TEM) and electron energy-loss spectroscopy (EELS). There is no significant difference in P diffusivity between the SiO_2 and Si_3N_4 films for the present annealing condition of 700 deg. C for 20-360 min. Regarding dose loss, a distinct different behavior was observed. In case of the SiO_2 cover film, amount of dose ...

International Nuclear Information System (INIS)

For obtaining radiation less damagable laser mirrors, a preliminary optimization of film fabrication suitable for the analysis of laser damage mechanism has been done as the first step. Here, the optimization requires not only the stable fabrication process but also the ideal film structure i.e., the amorphous and smooth film structure simultaneously, eliminating latently unwanted secondary effects such as light scattering during laser damage test. For this purpose, we adopted the ion assisted deposition (IAD) method and modified the deposition conditions for titanium and tantalum oxide films, both of which compose typical high index layers, and where SiO_2 layers are also chosen as low index layers because of their amorphous and smooth nature, in alternative multilayer laser mirrors. Surface and cross sectional film structures and film crystallinity are compared and characterized, using a high resolution SEM and a x-ray diffractometer, ...

International Nuclear Information System (INIS)

Fe_5_0Pt_5_0 nanodots dispersed in a SiO_2 film (Fe_5_0Pt_5_0 nanodot film) were formed by a self-assembled nanodot deposition (SAND) method in which Fe_5_0Pt_5_0 and SiO_2 are cosputtered in a high vacuum rf magnetron sputtering equipment. Fe_5_0Pt_5_0 pellets are laid on a SiO_2 target in a sputtering chamber to form the Fe_5_0Pt_5_0 nanodot film in the SAND method. The size and density of Fe_5_0Pt_5_0 nanodot were controlled by changing the ratio of the total area of Fe_5_0Pt_5_0 pellets to that of SiO_2 target. The Fe_5_0Pt_5_0 nanodot size decreases and its density increases when the ratio decreases. As-deposited Fe_5_0Pt_5_0 nanodots self-assembled to a face-centered-cubic phase of single-crystal structure. The Fe_5_0Pt_5_0 nanodot films were annealed to evaluate the nanodot size controllability, the magnetic anisotropy, and the thermal stability. Fully ordered L1_0 face-centered-tetragonal Fe_5_0Pt_5_0 nanodots with high ...

International Nuclear Information System (INIS)

Ion bombardment during deposition can significantly modify the film properties. In the partially ionized beam deposition, ions derived from the depositing material, i.e., the self-ions, are used during deposition. Cu films were deposited on SiO_2 substrates at room temperature using 1% Cu self-ions with an energy ranging between 0--4 keV. We studied the microstructures of the Cu films using x-ray diffraction and transmission electron microscopy, measured the impurity level inside the films using secondary ion mass spectrometry, and performed the resistivity measurements using a four point probe. The results indicate that there is an optimum ion energy around 2 keV at which, the integrated x-ray intensity ratio I(111)/I(200) reaches its maximum value indicating a strong left-angle 111 right-angle texture, while the impurity concentration and resisitivity are minimum. The correlation ...

International Nuclear Information System (INIS)

The band structure (BS) of crystalline Bi_2Se_2Te both pure as well as deposited on Si or SiO_2 (substrates) was calculated for the first time. The calculation approach consists of an orthogonalization of the plane wave basis set with respect to the core-like orbitals and the application of the Perdew-Alder exchange-correlation scheme. In addition, a virtual crystal approach was applied. Experimental ellipsometric spectra were used as a criterion of the advantages of the different calculation techniques. The results of traditional one-electron methods of BS calculations, using norm-conserving pseudo-potential (NCPP), and full linear augmented plane wave (FLAPW), were compared with the experimental data. Better agreement with experiment is achieved when the NCPP wave functions are orthogonalized to the 4dBi core-like states. Concerning the LMTO and the FLAPW all-electron methods, only appropriate application of the virtual crystal approximation to these approaches ...

British Library Electronic Table of Contents (United Kingdom)

Si nanocrystal floating gate MOS capacitors were formed on p-Si (100) wafers by thermal plasma jet (TPJ) annealing of SiO2/SiOx /SiO2/Si(100) stacked structure. The chemical composition of SiOx layer was controlled by changing the SiH4, He, and O2 gas flow ratio during plasma enhanced chemical vapour deposition. The MOS capacitors showed clear hysteresis in capacitance-voltage (CV) characteristics after TPJ annealing. The hysteresis width shows maximum value when initial composition x =1.7, which shows the maximum photoluminescence (PL) intensity. The maximum hysteresis width of 6.8 V was observed with gate voltage swept between 20 and -20 V in x = 1.7 sample. The result means 7.4 x 1012 cm-2 carriers are injected to or emitted from Si nanocrystals. The duration of 1 V shift in flatband vo...

International Nuclear Information System (INIS)

Full text of publication follows: Understanding the dynamic irradiation effects on silica glasses is important for developing the diagnostic systems used in fusion and fission environments. While fundamental defects having an un-pared electron such as the E' center have been extensively studied, the neutral oxygen deficiency defects have been insufficiently clarified for lack of the detection methods. The ion induced luminescence is one of the probes that can be used to detect non-paramagnetic defects, and to observe creation and annihilation behavior dynamically. In the present study, we examined the characteristics of the ion induced luminescence such as energy, fluence flux and temperature dependence of the luminescence efficiency to analyze damage process quantitatively. Samples of SiO2 glasses were commercially available fused and synthesized silica glasses, produced by Toshiba Ceramics, Co. Ltd.. A thin films of SiO2 deposited on a Si wafer was used to ...

International Nuclear Information System (INIS)

Atmospheric pressure plasma enhanced chemical vapour deposition system is built. The electrical and optical characteristics of the APPECVD system is given. The system is used to deposit conductive polymers and nano composites onto glass and metal surfaces. The morphological, optical, chemical and electrical characteristics of deposited surfaces are investigated using SEM, AFM four probe deposition purposes. The photovoltaic applications of plasma deposited polymers and nonconsumption are compared with deposited with electrochemical methods show different results. The electrical, chemical and morphological structures of the samples will be given.

International Nuclear Information System (INIS)

Complete text of publication follows. According to the new European regulations (Restrictions of Hazardous Substance Directive), there is an emerging demand for environmental friendly metal treatments instead on formerly used chromate conversion coating technique. The aim of the present investigations was to characterise and compare silicon containing protective thin layers on roughened galvanized steel surfaces (with average roughness of 0.7 microns), using FTIR microscopy and imaging techniques. The silicon containing coatings were produced either by Chemical Vapour Deposition (CVD) or by wet chemical treatment using liquid silane. FTIR techniques offer new possibilities in the characterisations and chemical mapping of differently coated thin films, besides SEM+EDS, AFM, nanoindentation, XPS measurements (P. Nemeth et al., Materials Science Forum, 589 (2008) 433-438). All measurements were carried out by a Varian FTS-7000 spectrometer with a 'Stingray' microscope ...

International Nuclear Information System (INIS)

Nitrogen doped Diamond-like carbon thin films were deposited on n-Si and SiO_2 substrates by rf magnetron sputtering using pure graphite (99.999%) as the target material and mixtures of Ar, N_2 and H_2 for plasma generation. The dependence of structural and optical properties on nitrogen content was investigated using XPS, Raman spectroscopy, FT-IR spectroscopy, and Ellipsometry studies. It was found that as the nitrogen content was increased in the plasma, sp"2 bonding favored. Also it was observed that oxygen contamination increased with nitrogen content. Typical C-H stretching modes connected with diamond-like carbon could be seen in FT-IR spectra. The I_D and I_G bands were well defined and it was observed that as nitrogen content increased I_G band was enhanced. Ellipsometry studies revealed that the optical constants like refractive index (n) and extinction co-efficient (k) increased with increase in nitrogen content as well as substrate temperature. (author)

International Nuclear Information System (INIS)

Etching of SiO_2 rods has been obtained with a dc torch with argon as the process gas in an air environment at atmospheric pressure; the high temperature of the plasma jet causes vaporization of the exposed area. The apparatus and torch operative parameters have been set up to obtain a depth etch rate of up to 0.6 mm min"-"1 corresponding to 0.826 g min"-"1. An enthalpy probe has been employed to monitor the plasma conditions before the thermal plasma etching process and from the experimental etch rate a surface rod temperature of T_s_u_r = 2057 K has been derived. Etching has been obtained with uniformity over the entire exposed area with peak to peak differences below 1%. The plasma to rod heat transfer has been simulated using a commercial CFD code Fluent (copyright). The model consists of a non-steady two-dimensional simulation for a compressible turbulent fluid, with an adapted grid calculation. Boundary conditions have been set out using the enthalpy probe ...

Energy Technology Data Exchange (ETDEWEB)

The process operation of the hot wall vapor deposition method, formation of dry organic thin film and the control of molecular arrangement were described. This equipment included a substrate on the upper end of the hot wall tube and the vapor source at the lower end. The remarkable features are the hot wall tube which plays the role to hold vaporizing molecules to the high temperature and to transport molecules, and the flip flop mechanism which gives some idle period for the molecular vaporization by shutter closing. Several experiments were carried out by using stearic acid and by changing the distance S from the upper end of hot wall quartz tube to the substrate, the furnace temperature T{sub f} and the substrate temperature T{sub s}. When T{sub f} is equal to or less than the melting point of stearic acid, molectles are preferentialy made to vertical arrangement. In the case of ...

Energy Technology Data Exchange (ETDEWEB)

The excellent high temperature strength and thermal conductivity of molybdenum-base alloys provide attractive features for components in advanced magnetic and inertial fusion devices. Refractory metal alloys react readily with oxygen and other gases. Oxidized molybdenum in turn is susceptible to losses from volatile molybdenum trioxide species, (MoO3)m, in air and the hydroxide, MoO2(OH)2, formed from water vapor. Transport of radioactivity by the volatilization, migration, and re-deposition of these volatile species during a potential accident involving a loss of vacuum or inert environment represents a safety issue. In this report we present experimental results on the oxidation, volatilization and re-deposition of molybdenum from TZM in flowing air between 400 and 800°C. These results are compared with calculations obtained from a vaporization mass transfer model using chemical thermodynamic ...

Science.gov (United States)

Thin-film solar cells on flexible, lightweight, space-qualified substrates provide an attractive approach to fabricating solar arrays with high mass-specific power. A polycrystalline chalcopyrite absorber layer is among the new generation of photovoltaic device technologies for thin film solar cells. At NASA Glenn Research Center we have focused on the development of new single-source precursors (SSPs) for deposition of semiconducting chalcopyrite materials onto lightweight, flexible substrates. We describe the syntheses and thermal modulation of SSPs via molecular engineering. Copper indium disulfide and related thin-film materials were deposited via aerosol-assisted chemical vapor deposition using SSPs. Processing and post-processing parameters were varied in order to modify morphology, stoichiometry, crystallography, electrical properties, and optical properties to optimize device quality. Growth at ...

International Nuclear Information System (INIS)

Rapid self-aggregation of Ni nanodots on Si substrate covered with a thin SiO_2 buffered layer is investigated. The Ni nanodots can hardly self-aggregate on highly heat-dissipated Si substrate with a thermal conductivity of 148 W/m K. Adding a 200-A-thick SiO_2 buffer with an ultralow thermal conductivity of 1.35 W/m K prevents the formation of NiSi_2 compounds, enhances the heat accumulation, and releases the adhesion at Ni/Si interface, which greatly accelerates the self-assembly of Ni nanodots. Dense Ni nanodots with size and density of 30 nm and 7x10"1"0 cm"-"2, respectively, can be formatted after rapid thermal annealing at 850 deg. C for 22 s.

Science.gov (United States)

Continuous wave operation of an Al/sub 0.21/Ga/sub 0.31/In/sub 0.48/P /Ga/sub 0.52/In/sub 0.48/P /Al/sub 0.21/Ga/sub 0.31/In/sub 0.48/P double heterostructure (DH) laser diode was achieved for the first time at 77 K. The device was made from a DH wafer grown by atmospheric metalorganic chemical vapor deposition using triethyl metals and phosphine as source materials. At 77 K, the lasing wavelength was 0.653 ..mu..m and the threshold current was 55 mA for a diode with a nitride-insulated, 8-..mu..m-wide and 250-..mu..m-long stripe geometry.

Science.gov (United States)

Room-temperature continuous-wave (cw) operation of a GaInP/AlGaInP multiquantum well (MQW) laser was achieved for the first time. The threshold current was 70 mA at 22 /sup 0/C for a device with an 8-..mu..m-wide and a 250-..mu..m-long planar stripe. The emission wavelength was 668 nm. The characteristic temperature T/sub 0/ was 138 K under cw operation. The wafer with the MQW structure composed of 100-A-thick GaInP wells and 40-A-thick AlGaInP barrier layers was grown by atmospheric pressure metalorganic chemical vapor deposition.

International Nuclear Information System (INIS)

The effect of electron and ion beam irradiation on the Sisub(LVV) Auger spectra of SiO_2, Si_3N_4 and Si-oxynitride films was measured by the relative intensity of the 92 eV signal, characteristic for the formation of 'free' silicon during irradiation. While in Si-oxynitride the beam effects were almost negligible, some damage was found in Si_3N_4, but SiO_2 appeared to be extremely sensitive for electron and ion beam irradiation. By low energy electron loss spectroscopy of ion bombarded SiO_2 and Si_3N_4 films new electron states due to broken Si-O and Si-N bonds could be determined within the band gap of the insulators. The measured energy losses were interpreted by means of electron energy level schemes of the amorphous films. (author).

CERN Document Server

In situ optical absorption spectroscopy was used to study the generation of E' centres in amorphous SiO_2 occurring by photo-induced breaking of Si-H groups under 4.7eV pulsed laser radiation. The dependence from laser intensity of the defect generation rate is consistent with a two-photon mechanism for Si-H rupture, while the growth and the saturation of the defects are conditioned by their concurrent annealing due to reaction with mobile hydrogen arising from the same precursor. A rate equation is proposed to model the kinetics of the defects and tested on experimental data.

British Library Electronic Table of Contents (United Kingdom)

Methods of X-ray diffraction and transmission electron microscopy were used to study the microstructure of dispersion-strengthened Cu-Al2O3 nanocomposites obtained by the method of simultaneous deposition of Cu and Al2O3 from the vapor phase. The effect of the size of particles of the oxide (Al2O3) and of their content on the electrical resistance of the composite has been considered. The results obtained make it possible to suppose that the main structural factor that determines the electrical resistance of the composite are nanodispersed particles of Al2O3 with a size of less than 20 nm.

International Nuclear Information System (INIS)

Microwave Electron Cyclotron Resonance (ECR) Plasma assisted Chemical Vapor Deposition (CVD) technology has been used to prepare Si_3N_4 films, which were analyzed by using infrared (IR) transmission spectroscopy and XPS. The analysis results show that with the increase of the deposition temperature, the H content decrease, and the densification of the film increases. When the temperature is up to 360 degree C, the stoichiometrical rate of Si:N is close to 0.75. The protective property of Si_3N_4 films is also examined

Energy Technology Data Exchange (ETDEWEB)

We have studied the nucleation and growth processes in a chemical vapor deposition (CVD) diamond film using a tomographic electron backscattering diffraction method (3D EBSD). The approach is based on the combination of a focused ion beam (FIB) unit for serial sectioning in conjunction with high-resolution EBSD. Individual diamond grains were investigated in 3-dimensions particularly with regard to the role of twinning.

Energy Technology Data Exchange (ETDEWEB)

Microcrystalline silicon carbide ({mu}c-SiC) was prepared at low substrate temperatures using Hot Wire chemical vapor deposition (HWCVD). High crystalline volume fractions were achieved at high hydrogen dilution and high deposition pressure. Without intentional doping, such material shows high dark conductivity and high optical absorption below the band gap. The material prepared at low deposition pressure or low hydrogen dilution, on the other hand, shows much lower conductivity and sub-gap absorption, but high spin densities up to 5 x 10{sup 19} cm{sup -3}. This high absorption can be attributed to free carriers, different to {mu}c-Si:H where a correlation between the sub-gap absorption and the spin density is observed.

International Nuclear Information System (INIS)

The formation of thin SiO_2 layers on silicon and metal silicides was studied by phase- and thickness measurements with Rutherford back-scattering of 2 MeV alfa particles. Thermal oxidation was done in steam and dry oxygen at temperatures between 750 degrees Celsius and 1 100 degrees Celsius, while SiO_2 formation at room temperature was carried out by anodic oxidation. The study of silicon oxidation was done on Si<100>, Si<111> and amorphous silicon substrates. Thermal oxidation of CoSi_2, CrSi_2, NiSi_2, PtSi and TiSi_2 was investigated. The oxidation rates of the silicides were found to be much higher than for silicon. The oxidation process is also diffusion-limited with a higher oxidation rate for steam as compared to dry oxygen. The silicide layers were found to stay intact during thermal oxidation. A certain amount of structural and chemical instability did appear. Chemical instabiliy was shown by metal oxidation which led to metal atoms being incorporated into the ...

International Nuclear Information System (INIS)

The cytotoxicity of 15-nm and 46-nm silica nanoparticles was investigated by using crystalline silica (Min-U-Sil 5) as a positive control in cultured human bronchoalveolar carcinoma-derived cells. Exposure to 15-nm or 46-nm SiO_2 nanoparticles for 48 h at dosage levels between 10 and 100 #mu#g/ml decreased cell viability in a dose-dependent manner. Both SiO_2 nanoparticles were more cytotoxic than Min-U-Sil 5; however, the cytotoxicities of 15-nm and 46-nm silica nanoparticles were not significantly different. The 15-nm SiO_2 nanoparticles were used to determine time-dependent cytotoxicity and oxidative stress responses. Cell viability decreased significantly as a function of both nanoparticle dosage (10-100 #mu#g/ml) and exposure time (24 h, 48 h, and 72 h). Indicators of oxidative stress and cytotoxicity, including total reactive oxygen species (ROS), glutathione, malondialdehyde, and lactate dehydrogenase, were quantitatively assessed. Exposure to SiO_2 nanoparticles increased ROS ...

International Nuclear Information System (INIS)

Marker experiments for studying the mass transport through a palladium silicide layer on a crystalline substrate during thermal oxidation at 700 to 850 deg C have been reported recently. In this work argon gas embedded in amorphous silicon during sputtering was implemented as the inert marker and the oxidation of PdSi was processed above 900 deg C. At this high-temperature oxidation silicon-rich silicide PdSisub(y), with y exceeding 5, may be obtained. This can be anticipated by considering the Pd-Si phase diagram which shows the liquid phase may appear at an annealing temperature above 892 deg C. As a result, a non-stoichiometric and non-uniform silicide layer may develop at the sample surface. Marker analysis showed that both palladium and silicon dissociated at the Pdsub(x)Si/ SiO_2 interface and moved to the substrate with the silicon being the dominant diffuser. The Rutherford backscattering spectra (RBS) showing the oxide film and composition isothermally annealed at 900 deg C is ...

Energy Technology Data Exchange (ETDEWEB)

In addition to ceramics, alloys such as tool steel and nickel- and iron-based superalloys are being considered for high temperature applications such as missile bearings and low heat rejection engines. Studies were made to lubricate a nickel-based superalloy at 500{degrees}C, by using a vaporized aryl phosphate ester, at a concentration of 0.1% in air. From deposition and wear studies it was found that it was impossible to form a good polymeric coating on the superalloy surface. Energy dispersive X-ray analyzer (EDXA) analysis showed that this was due to minute quantities of aluminum in the alloy segregating to the surface, upon being heated to 500{degrees}C, forming a passive oxide coating. It was necessary to activate the surface, in order to lubricate the material successfully. A method of activation by electrodepositing the surface with a layer of iron oxide was developed. Once activated, a good lubricous polymer was formed on the ...

British Library Electronic Table of Contents (United Kingdom)

The electrical characteristics of thin TiO2 films prepared by metal?organic chemical vapor deposition grown on a p-type InP substrate were studied. For a TiO2 film of 4.7?nm on InP without and with ammonium sulfide treatment, the leakage currents are 8.8?10?2 and 1.1?10?4?A/cm2 at +2 V bias and 1.6?10?1 and 8.3?10?4?A/cm2 at ?2?V bias. The lower leakage currents of TiO2 with ammonium sulfide treatment arise from the improvement of interface quality. The dielectric constant and effective oxide charge number density are 33 and 2.5?1013?cm2, respectively. The lowest mid-gap interface state density is around 7.6?1011?cm?2?eV?1. The equivalent oxide thickness is 0.52?nm. The breakdown electric field increases with decreasing thickness in the range of 2.5 to 7.6?nm and reaches 9.3?MV/cm at 2.5?n...

Energy Technology Data Exchange (ETDEWEB)

Continuous-wave (cw) operation at temperatures up to 23 /sup 0/C of an Al/sub 0.26/Ga/sub 0.26/In/sub 0.48/P/Ga/sub 0.52/In/sub 0.48/P/ Al/sub 0.26/Ga/sub 0.26/In/sub 0.48/P double heterostructure (DH) laser has been achieved for the first time. The threshold current was 160 mA at 20 /sup 0/C for a device with a 10-..mu..m-wide and 250-..mu..m-long ion-implanted stripe geometry. The emission wavelength was 671 nm during cw operation at 10 /sup 0/C. To reduce thermal resistance to a heat sink, a dually stacked structure made of a thin (approx.0.3 ..mu..m) p-AlGaInP layer and a p-Al/sub 0.76/Ga/sub 0.24/As layer was used as a cladding layer. The DH wafer was grown by atmospheric pressure metalorganic chemical vapor deposition.

International Nuclear Information System (INIS)

Along with the shrinkage of LSI geometries, a higher quality of ultrapure water has been continuously required. Analytical technology for ultrapure water has also progressed before ultrapure water production technology improvements. In this study, we performed optimization of the analytical conditions for the direct analysis of acid droplets, and established an analytical technology for measurements of trace amounts of metallic impurities deposited on a wafer surface by means of Vapor Phase Decomposition (VPD)/Inductively Coupled Plasma Mass Spectrometry (ICP-MS). As a result, analytical technology for metallic elements of the 1x10"8 atoms/cm"2 level on wafer surface has been established. By applying analytical technology to the wafer that has been contacted with ultrapure water, a new evaluation technology for ultrapure water quality by means of wafer surface contamination has been established. We confirmed good correlations between metal ...

International Nuclear Information System (INIS)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage measurement. The analysis of capacitance-voltage characteristics ...

International Nuclear Information System (INIS)

The intensity of erbium up-conversion luminescence could be limited by a saturation effect due to increased pump power. We studied the luminescence saturation of the 550 nm emission on erbium-doped, SiO_2-TiO_2 sol-gel powders under pulsed excitation at 979 and 1532 nm. From the latter, the up-converted luminescence intensity decreased with increasing excitation power, whereas no saturation was observed at 979 nm excitation. We proposed that the saturation effect is determined by the pump power, the erbium content and the lifetime of the corresponding first excited states at different pumping schemes.

International Nuclear Information System (INIS)

The purpose of the present study is to develop a new method for chemical state analysis by means of EPMA(Electron probe microanalyser). The measured X-ray intensity of Si-K#beta# characteristic X-ray spectra were read-out by a 16 bit microcomputer with a RS-232C interface. And using the curve fitting method the quantitative analysis of chemical compositions in a ternary compound that constituted of the same element has been established. The present method was applied to analyse of the friction and wear properties of Si-base ceramics sliding materials. It was found that the wear debris contains both the compositions of the sliding materials and SiO_2, and the SiO_2 contents in wear debris was changed with relative humidity. The results clearly showed that the proposed method is very useful for determing the compositions in the ternary compound. (author).

Energy Technology Data Exchange (ETDEWEB)

This report describes progress during the first year of a three-year project. The objective of the research is to examine new design approaches for achieving very high conversion efficiencies. The program is divided into two areas. The first centers on exploring new thin-film approaches specifically designed for III-V semiconductors. The second area centers on exploring design approaches for achieving high conversion efficiencies without requiring extremely high quality material. Research activities consisted of an experimental study of minority carrier recombination in n-type, metal-organic chemical vapor deposition (MOCVD)-deposited GaAs, an assessment of the minority carrier lifetimes in n-GaAs grown by molecular beam epitaxy, and developing a high-efficiency cell fabrication process.

Energy Technology Data Exchange (ETDEWEB)

Low-temperature polysilicon thin-film transistors (TFT's) have been fabricated from sputtered silicon films and characterized as a function of as-deposited hydrogen (H) content and laser crystallization fluence. A general trend is observed where TFT performance improves as the H content is lowered. Devices made from {approximately}0% H sputtered films perform similar to those made from low-pressure chemical-vapor deposition processes (LPCVD), but are fabricated at a much lower process temperature (300 C). The best sputtered TFT's had mobilities of {approximately}200 cm{sup 2}/Vs, and on/off current ratios of more than 10{sup 8}.

International Nuclear Information System (INIS)

Full text of publication follows: Slightly over-stoichiometric lithium orthosilicate pebbles have been selected as one optional breeder material for the European Helium Cooled Pebble Bed (HCPB) blanket. This material has been developed in collaboration of Research Center Karlsruhe and the Schott Glass, Mainz. The lithium orthosilicate pebbles are fabricated from lithium hydroxide and silica by a melting and spraying method in a semi-industrial scale facility. Lithium hydroxide was selected as the precursor since enriched lithium hydroxide is commercially available. The lithium orthosilicate pebbles produced by the process contains oxide phases besides orthosilicate, but it was also found that the oxide phases can be decomposed by annealing at high temperatures. The lithium orthosilicate pebbles produced in this way possesses satisfactory pebble characteristics. Therefore, the authors performed out-of-pile annealing tests using the lithium orthosilicate pebbles irradiated in a research ...

Energy Technology Data Exchange (ETDEWEB)

After pioneering work in the 1980s, plasma-based ion implantation (PBII) and plasma-based ion implantation and deposition (PBIID) can now be considered mature technologies for surface modification and thin film deposition. This review starts by looking at the historical development and recalling the basic ideas of PBII. Advantages and disadvantages are compared to conventional ion beam implantation and physical vapor deposition for PBII and PBIID, respectively, followed by a summary of the physics of sheath dynamics, plasma and pulse specifications, plasma diagnostics, and process modeling. The review moves on to technology considerations for plasma sources and process reactors. PBII surface modification and PBIID coatings are applied in a wide range of situations. They include the by-now traditional tribological applications of reducing wear and corrosion through the formation of hard, tough, smooth, ...

International Nuclear Information System (INIS)

By means of ESCA the composition and the thickness of passive films formed on austenitic stainless steels were investigated after the attack of nitric acid at various temperatures and acid concentrations. The outermost layers of the oxide film consist of SiO_2, then a layer rich of Cr-oxid follows, containing also some Mo in the four- and sixvalent state. Ni does not contribute to the oxide film. Cr is also enriched in the metal just below the oxide film. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The aim of this contract is to investigate, develop, and characterize laser-assisted processing techniques utilized to produce the fine-line, thin-metal grid structures that are required to fabricate high-efficiency solar cells. During the first quarter of this contract, a comprehensive literature search was carried out in the various state-of-the-art laser-assisted techniques for metal deposition, including laser chemical vapor deposition and laser photolysis of organometallics, as well as laser-enhanced electroplating. A compact system for the experiments involving laser-assisted photolysis of gas-phase compounds was designed and constructed. The work performed in the second quarter is detailed in this report. Metal deposition experiments have been carried out utilizing laser-assisted pyrolysis of a variety of metal-bearing polymer films and metallo-organic inks spun onto silicon substrates. Laser ...

International Nuclear Information System (INIS)

Uranium dendrites which were deposited at a solid cathode of an electrorefiner contained a certain amount of salts. These salts should be removed for the recovery of pure metal using a cathode processor. In the uranium deposits from the electrorefining process, there are actinide chlorides and rare earth chlorides in addition to uranium chloride in the LiCl-KCl eutectic salt. The evaporation behaviors of the actinides and rare earth chlorides in the salts should be investigated for the removal of salts in the deposits. Experiments on the salt evaporation of rare earth chlorides in a LiCl-KCl eutectic salt were carried out. Though the vapor pressures of the rare earth chlorides were lower than those of the LiCl and KCl, the rare earth chlorides were co-evaporized with the LiCl-KCl eutectic salt. The Hertz-Langmuir relation was applied for this evaporation, and also the evaporation rates of the salt were ...

Science.gov (United States)

Hybridization and thermal evolution of the Ni+C{sub 60} composites, deposited on Si(001) at room temperature, were studied using Scanning Electron Microscopy, {mu}-Raman spectroscopy and Rutherford Backscattering. As-deposited, the hybrid films exhibited a granular nano-structure with Ni nano-particles encapsulated in C{sub 60} polymerized rinds. The Ni and C (C{sub 60}) distributions in a top layer were found homogeneous with a stable Ni/C (C{sub 60}) ratio; in the larger depth the distributions were inhomogeneous and their ratio dramatically varied. At elevated temperatures, all structural parameters were changed. In the subsurface layer Ni- and C (C{sub 60})-rich zones were formed (due to the induced phase separation), C{sub 60}-molecules decayed and their fragments were transformed into amorphous carbon (a-C). The free volume distribution of the stressed hybrid matter was analyzed by the Hg marker that (in a form of ...

Energy Technology Data Exchange (ETDEWEB)

In the region of annular liquid film-mist flow, the behavior of the droplets formed from the liquid film and the rate of formation are the subjects to be clarified in connection with the forecast of dry-out point, which becomes a problem in the region of high dryness such as reactor cooling system and steam generators. Many researches have been performed on such problem in vertical tubes, but the characteristics in horizontal flow have not yet been sufficiently clarified. This series of research is to clarify various characteristics, such as the velocity of vapor phase, the flow rate distribution of droplets, the formation and adhesion of droplets and the structure of liquid film, in the region of liquid film-mist flow, where liquid film exists on the bottom of a horizontal rectangular channel, and vapor flow is accompanied by droplets. In this study, by the measurement of the flow rate distribution of droplets on respective cross sections ...

Science.gov (United States)

The growth of an oxide interfacial layer was recently found to increase the open-circuit voltage (OCV) and efficiency by up to 60 per cent in GaAs metal-semiconductor solar cells. Details of oxidation techniques to provide the necessary oxide thickness and chemical structure and using ozone, water-vapor-saturated oxygen, or oxygen gas discharges are described, as well as apparent crystallographic orientation effects. Preliminary results of the oxide chemistry obtained from X-ray, photoelectron spectroscopy are given. Ratios of arsenic oxide to gallium oxide of unity or less seem to be preferable. Samples with the highest OVC predominantly have As(+3) in the arsenic oxide rather than As(+5). A major difficulty at this time is a reduction in OCV by 100-200 mV when the antireflection coating is vacuum deposited.

Science.gov (United States)

Fabry Perot interferometry is a method of determining instantaneous velocities of an object in motion. The interferometer system is composed of the Fabry Perot interferometer, a laser, an electronic streak camera, and several focusing lenses. The first tests discussed were done on exploding bridgewire devices. During these tests, several system parameters were changed. These changes did not seem to affect the data, which appeared to be consistent. The second tests performed focused on slapper-type devices. It was determined that sandblasted, vapor-deposited aluminum on the slapper material would be required to yield quality data. Streak camera failure prevented much data from being collected. An effort is being made to replace the current streak camera. After it is replaced, a Fabry Perot and velocity interferometry system for any reflector comparison will be made. The results will be published as the conclusion to this report.

Energy Technology Data Exchange (ETDEWEB)

This paper reports advances in the development of solar cells made from GaAs-on-Si structures prepared by metalorganic chemical vapor deposition (MOCVD). The use of concentrator cells, operating at [similar to]200 suns, has led to the efficiency achievements of 21.3% (AM1.5D) for a GaAs-on-Si solar cell, and 27.6 (AM1.5D) for a homoepitaxial GaAs cell. The development of epitaxial multilayer dielectric mirrors (Bragg reflectors), as back-surface reflectors in thin-film GaAs cells, on both Si and GaAs substrates, is shown to lead to modest efficiency increases, over that of conventional designs.

Energy Technology Data Exchange (ETDEWEB)

The scale-down of a liquid mini-pump (order of 10 mm) to a micrometre scale has been attempted using a novel valveless nozzle-diffuser design and new application of an organic physical vapor-deposited membrane. The micropump employs no moving parts other than the membrane and accomplishes the rectification of fluid flow due to pressure recovery differences in the nozzle and diffuser flow directions. More specifically, liquids flow with less resistance (i.e. conduct more fluid) in the diffuser direction than the nozzle direction, for a given pressure differential. At the micrometre scale, the fabrication of the critical nozzle and diffuser elements was performed by focused ion beam (FIB) microlithography of glass slides. Etched slides were sandwiched to make two-dimensional venturis. Sternme and Sternme noted the importance of a lower Reynolds Number linfit on the desired pressure recovery which challenged the fabrication of this pump design at the scale used.

Energy Technology Data Exchange (ETDEWEB)

A gain-guiding tapered stripe laser was fabricated using a Ga/sub 0.5/In/sub 0.5/P/(Al/sub 0.5/Ga/sub 0.5/)/sub 0.5/In/sub 0.5/P double heterostructure wafer grown by metalorganic chemical vapor deposition. The laser showed a continuous wave (cw) threshold current of 48 mA, a maximum temperature for cw operation of 81 /sup 0/C, an aspect ratio of about 2, and an astigmatism near 25 ..mu..m. The emission wavelength was 684 nm. Thirty-two devices have been operating without significant degradation for more than 2000 h at 50 /sup 0/C with a constant output power of 3 mW.

International Nuclear Information System (INIS)

Carbothermal reduction-nitridation (CRN) of SiO_2 is an attractive method for manufacturing Si_3N_4 powders with controlled grain morphology. Moreover, #beta#-sialon powders could also be synthesized from either pure powder mixtures or some inexpensive raw minerals by CRN. The resultant powders have shown some advantages, especially in manufacturing sialon products at low cost. However, there have been only a few works on preparing #alpha#-sialon powders. In this work, Ca-#alpha# sialon powder was synthesized by CRN of a SiO_2-Al_2O_3 and CaCO_3 powder mixture An unusual morphology of hollow balls of 200 to 500nm with many nano size #alpha#-sialon particles of 10 to 30nm was identified from the resultant Ca-#alpha# sialon powders. This has never been previously reported for sialon ceramics. It was consequently confirmed that the morphologies of the products were clearly related to the intermediate products appearing during CRN reaction. Copyright (2000) The Australian Ceramic Society

International Nuclear Information System (INIS)

Total-dose irradiation seriously damages MOS devices and their circuit performance. Threshold voltage shifts, transconductance degradation and increase in off-state leakage current are generally observed for irradiated devices. These instabilities are essentially due to positive and/or negative charge trapping in SiO_2 and interface trap generation at the SiO_2/Si interface. Radiation hardening of CMOS VLSIs is to eliminate these trapping effects, and for this purpose, special considerations for fabrication processes and layout design are necessary. In this paper, basic mechanisms for radiation-induced charge trapping and related effects on MOS devices are reviewed. Also discussed are radiation-hardening technologies from both fabrication-process and layout-design viewpoints. Using these technologies, 1 #mu#m radiation-hard CMOS gate arrays have been successfully developed. Experimental data taken for 2k-gate test chips indicate that radiation hardness of these gate arrays is over 1 ...

International Nuclear Information System (INIS)

A dense silica glass was prepared by consolidating a highly dispersed silicic acid powder (particle size 1H magic-angle spinning (MAS) NMR confirmed an increase in hydroxyl groups in the sample prepared by SPS relative to that of the conventional SiO2 reference glass. Aside from the comparably high water content, we conclude from the similarity of the IR-reflectance and the 29Si MAS NMR spectra of the SPS sample and the corresponding spectra of the conventionally prepared silica glass, that the short- and medium-range order is virtually the same in both materials. Raman spectroscopy, however, suggests that the number of three- and four-membered rings is significantly smaller in the SPS sample compared to the conventionally prepared sample. Based on these results we conclude that it is possible to prepare glasses by compacting amorphous powders by the SPS process. The SPS process may therefore enable the preparation of glasses with compositions inaccessible by conventional methods. - ...

International Nuclear Information System (INIS)

Several metallurgical coatings have been developed that provide good tribological performances in high-temperature liquid sodium and that are relatively unaffected by neutron fluences to 6 X 10/sup 22/ n/cm/sup 2/ (E > 0.1 MeV). The coatings that have consistently provided the best tribological performance have been the nickel aluminide diffusion coatings created by the pack cementation process, chromium carbide or Tribaloy 700 trade mark (a nickel-base hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing alloy) applied by the detonation-gun process, and chromium carbide and other hardfacing materials applied by the electro-spark deposition process. The latter process is a relatively recent development for nuclear applications and is expected to find wide usage. Other coating processes, such as plasma-spray coating, sputtering, and chemical vapor deposition, were candidates ...

Science.gov (United States)

Attempt to form the Schottky barrier on mercury indium telluride (MIT) surface by deposition transparent conducting electrode (TCE) and avoid the negative results by non-rectifier contacts nature, we have investigated the oxidation of clean MIT surfaces to form an insulating layer to overcome this disadvantage by metal-insulator-semiconductor (MIS) photodetectors designing. Oxide film is grown on the MIT surface by plasma enhance chemical vapor deposition (PECVD). Previously cleaned MIT wafers were dipped and boiled in solution, which consists of mixture of bromine and an organic solvent in ratio of 1:50. By the way of using these films as intermediate slightly conducting insulator, a fast-response MIT based surface-barrier photodetectors have been developed. Pt films were used as TCE frontal electrode by vacuum magnetron sputtering (VMS). The current-voltage characteristic is described quantitatively based on the energy ...

International Nuclear Information System (INIS)

The electronic structure and surface interactions vapor-deposited Cu on single-crystal and polycrystalline Bi_2Ca/sub 1+//sub x//sub Sr>2-//sub x//sub Cu>2/O/sub 8+//sub y/ were studied using x-ray photoelectron spectroscopy. The results are compared to the Cu/YBa_2Cu_3O/sub 7-//sub x/ interface. Changes in the Cu 2p satellite emission indicate that the Cu adatoms do not disrupt Bi_2Ca/sub 1+//sub x/Sr/sub 2-//sub x/Cu_2O/sub 8+//sub y/ as extensively as YBa_2Cu_3O/sub 7-//sub x/. However, deposition of Cu induces changes in the Bi environment in the superconductor, and surface segregation of Bi metal was observed at high coverages. Core-level attenuation results suggests minimal outdiffusion of oxygen, in contrast with what is observed for Cu/YBa_2Cu_3O/sub 7-//sub x/.

International Nuclear Information System (INIS)

A mixture of powders of silica and aluminum nitride is subjected to high-energy ball milling for different milling times. This material is subsequently compacted by uniaxial pressing and sintered at 1450 deg. C. The resulting pellets are crushed and analysed by X-ray diffraction. For short milling times, the amount of phase transformation is minimal and the resulting material mostly consists of cristobalite and aluminum nitride. For long milling times, nanocrystalline #beta#-SiAl_2O_2N_2 is mainly produced.

International Nuclear Information System (INIS)

The nature and properties of inorganic "2"1"1At-species formed in aqueous solutions under alkaline, neutral, acidic and oxidative conditions are studied through extraction of At with a variety of organic solvents, followed by the determination of the chromatographic, re-extraction and interaction behaviour of the extracted activity. It is concluded from the Rsub(f) values (on SiO_2) and the different affinities for a large amount fo additives, that the extracted activity - formerly denoted as At-zero - exists of AtX compounds that may form AtXLsub(u) complexes, depending on the kind of solvent (L) used. (orig.).

Energy Technology Data Exchange (ETDEWEB)

Analyses of process system properties were continued for important chemical materials involved in the several processes under consideration for semiconductor and solar cell grade silicon production. Major activities were devoted to physical, thermodynamic and transport property data for silicon. Property data are reported for vapor pressure heat of vaporization, heat of sublimation, liquid heat capacity and solid heat capacity as a function of temperature to permit rapid usage in engineering. Chemical engineering analysis of the HSC process (Hemlock Semiconductor Corporation) for production of silicon was initiated. The process is based on hydrogen reduction of dichlorosilane (DCS) to produce the polysilicon. The chemical vapor deposition reaction for DCS is faster in rate than the conventional process route which utilizes trichlorosilane (TCS) as the silicon raw material. Status and progress are ...

International Nuclear Information System (INIS)

Epitaxial cobalt disilicide (CoSi_2) layers are grown on n-Si_0_._8_3Ge_0_._1_7/n-Si(001) using a sacrificial Si capping layer at the growth temperature T_s=650 deg. C by reactive chemical vapor deposition using cyclopentadienyl dicarbonyl cobalt (Co(#eta#"5-C_5H_5)(CO)_2). Structural and electrical properties of epi-CoSi_2/Si_0_._8_3Ge_0_._1_7/Si(001) were measured by transmission electron microscopy, X-ray diffraction, Auger electron spectroscopy and sheet resistance measurement as a function of annealing temperature. The combined results showed that the epitaxial CoSi_2 phase by the reaction of Co with the Si capping layer was formed in the as-grown layers. Rapid thermal anneals for the investigation of thermal stability of the as-grown layers showed good thermal stability of the epitaxial CoSi_2 layers with the low sheet resistance value as low as congruent with 4.4 #OMEGA#/cm up to the annealing temperature as high as 850 deg. C without ...

International Nuclear Information System (INIS)

Fluorinated amorphous carbon (a-C:F) films were deposited by radio frequency bias assisted microwave plasma electron cyclotron resonance chemical vapor deposition with tetrafluoromethane (CF_4) and acetylene (C_2H_2) as precursors. The deposition process was performed at two flow ratios R=0.90 and R=0.97, where R=CF_4/(CF_4+C_2H_2). The samples were annealed at 300 deg. C for 30 min. in a N_2 atmosphere. Both Fourier transform infrared and electron spectroscopy for chemical analyzer were used to characterize the a-C:F film chemical bond and fluorine concentration, respectively. A high resolution electron energy loss spectrometer was applied to detect the electronic structure. The higher CF_4 flow ratio (R=0.97) produced more sp"3 linear structure, and it made the a-C:F film smoother and softer. A lifetime of around 0.34 #mu#s and an energy gap of #approx#2.75 eV were observed in both the ...

Energy Technology Data Exchange (ETDEWEB)

We studied whether plasma-etching techniques can use standard screen-printed gridlines as etch masks to form self-aligned, patterned-emitter profiles on multicrystalline-silicon (mc-Si) cells from Solarex. We conducted an investigation of plasma deposition and etching processes on full-size mc-Si cells processed in commercial production lines, so that any improvements obtained would be immediately relevant to the PV industry. This investigation determined that reactive ion etching (RIE) is compatible with using standard, commercial, screen-printed gridlines as etch masks to form self-aligned, selectively doped emitter profiles. This process results in reduced gridline contact resistance when followed by plasma-enhanced chemical vapor deposition (PECVD) treatments, an undamaged emitter surface easily passivated by plasma-nitride, and a less heavily doped emitter between gridlines for reduced emitter recombination. This ...

International Nuclear Information System (INIS)

The T/sub c/ behavior of vapor-deposited Nb_3Ge and Nb_3Sn is examined as a function of low-fluence alpha-particle irradiation. It is found that for Nb_3Sn with rho_0approx.15 #mu##OMEGA#-cm the T/sub c/ is insensitive to low doses of radiation, whereas Nb_3Ge with rho_0approx.50 #mu##OMEGA#-cm has its T/sub c/ depressed immediately with irradiation. It is suggested that the T/sub c/ behavior of A-15 superconductors in the regime of small dose is strongly influenced by the initial state of the sample. Furthermore, it is argued that the behavior of the T/sub c/ with dose can be qualitatively explained by considering a sharp structure in the density of states N(E), the smearing of which by defects leads to a depression in T/sub c/.

Energy Technology Data Exchange (ETDEWEB)

Data are presented demonstrating very-short-wavelength (625 nm) room-temperature (300 K) continuous (cw) photopumped laser operation of In/sub 1-//sub y/(Al/sub x/Ga/sub 1-//sub x/)/sub y/P-In/sub 1-//sub y/ (Al/sub x/Ga/sub 1-//sub x/)/sub y/P quantum well heterostructures grown lattice matched (yapprox. =0.5) on a GaAs substrate via metalorganic chemical vapor deposition. In addition, 300 K pulsed laser operation (J/sub th/approx.10/sup 4/ A/cm/sup 2/, 625 nm) of diodes fabricated from the same crystal is described.

Energy Technology Data Exchange (ETDEWEB)

Room temperature continuous wave operation of red ([lambda][sub 0] [approximately] 660 nm) vertical cavity surface emitting laser arrays is reported. The 1 [times] 64 arrays have a pitch of 100 [mu]m with device diameters of 15 [mu]m with device diameters of 15 [mu]m. Grown by metalorganic vapor phase epitaxy, the devices consist of an AlGaInP strained quantum well optical cavity active region surrounded by AlGaAs distributed Bragg reflectors (DBR's). The top coupling DBR includes a partial dielectric stack, deposited after implanted device fabrication. All 64 devices operation simultaneously with peak output powers >0.45 mW, threshold current <1.5 mA, and threshold voltages [<=] 2.7 V. The differential quantum efficiencies exceed 10%.

Energy Technology Data Exchange (ETDEWEB)

Undoped Al /SUB 0.5/ In /SUB 0.5/ P-Ga /SUB 0.5/ In /SUB 0.5/ P double heterostructure was grown on (100) GaAs by metalorganic chemical-vapor deposition for the first time. A mirror-like grown surface was obtained. Over ten-times stronger photoluminescence-intensity was gained from the sandwiched Ga /SUB 0.5/ In /SUB 0.5/ P-layer, than that from a single epitaxially-grown Ga /SUB 0.5/ In /SUB 0.5/ P-layer on (100) GaAs, indicating that high-quality Al /SUB 0.5/ In /SUB 0.5/ P-Ga /SUB 0.5/ In /SUB 0.5/ P heterointerfaces are formed in the double heterostructure. A lasing action by optical pumping with an argon ion laser was observed in the double heterostructure at 90 K. The observed stimulated emission wavelength was 6470 A.

Energy Technology Data Exchange (ETDEWEB)

Infrared astronomical instruments require absorptive coatings on internal surfaces to trap scattered and stray photons. This is typically accomplished with any one of a number of black paints. Although inexpensive and simple to apply, paint has several disadvantages. Painted surfaces can be fragile, prone to shedding particles, and difficult to clean. Most importantly, the vacuum performance is poor. Recently a plasma enhanced chemical vapor deposition (PECVD) process was developed to apply thick (30 {micro}m) diamond-like carbon (DLC) based protective coatings to the interior of oil pipelines. These DLC coatings show much promise as an infrared black for an ultra high vacuum environment. The coatings are very robust with excellent cryogenic adhesion. Their total infrared reflectivity of < 10% at normal incidence approaches that of black paints. We measured outgas rates of <10{sup -12} Torr liter/sec cm{sup 2}, comparable to bare ...

Energy Technology Data Exchange (ETDEWEB)

Progress in the development of high-efficiency GaAs solar cells on low-cost, large-area, large-grain, optical-grade polycrystalline Ge substrates is described in this paper. First, we present results on the growth of specular GaAs-AlGaAs layers, across the various crystalline orientations of a polycrystalline Ge substrate, by metallorganic chemical vapor deposition (MOCVD). Second, we present the preliminary optimization of minority-carrier properties of GaAs-AlGaAs structures on poly-Ge substrates towards the improvement of GaAs solar cells. We have demonstrated comparable minority-carrier lifetimes in GaAs double-hetero structures grown on optical-grade poly-Ge substrates and electronic-grade single-crystal Ge substrates. In addition, we describe device-structure optimization that have led us to achieve a open-circuit voltage of {approximately}1 Volt in a GaAs solar cell on poly-Ge and to improve our previous best efficiency from ...

International Nuclear Information System (INIS)

A compact storage ring NIJI-IV free electron laser (FEL) is being developed as a tunable light source which covers a wide wavelength range from the VUV to the IR. To shorten the FEL wavelength in the VUV region, the optical cavity mirror was improved and the original loss of Al_2O_3/SiO_2 multilayer mirror around 195nm was decreased 30% compared with that of the previous one. New optical cavity system equipped with two remotely interchangeable mirrors was installed for the UV/VUV FEL to stabilize the laser and also to extend the tuning range. As for construction of the IR FEL, modification of the beam transport system to make space for installation of the optical cavity was completed. (author)

Wastenet

...Synthesis of low-temperature, fast, single-firing body for porcelain stoneware tiles with coal gangue Synthesis of low-temperature, fast, single-firing body for porcelain stoneware ... tiles with coal gangue Synthesis of low-temperature, fast, single-firing body for porcelain stoneware tiles with coal gangue Wei et al.,... Article Synthesis of low-temperature, fast, single-firing body for porcelain stoneware tiles with coal gangue Qiangwei Wei1, Wenyuan Gao1*, and Xinguo ...According to phase diagram theory, a low-temperature, fast, single-firing body mix for porcelain stoneware tiles was designed in the quaternary system CaO-MgO-Al2O3-SiO2, using ...

British Library Electronic Table of Contents (United Kingdom)

We have succeeded in aligning self-assembled structures by using a lithographically defined stripe. The 140nm wide by 100nm high SiO2 strip is shown to guide the assembly of 500nm latex spheres so that spheres are aligned along the strip and are in registration on either side of the strip. This method can be used to increase long-range ordering in magnetic storage systems without compromising the density. Inverse sphere Ni arrays were made by electrodeposition through the latex template. We also show that the hexagonal symmetry of the resulting inverse sphere Ni arrays can be simulated using the approach presented below.

British Library Electronic Table of Contents (United Kingdom)

In the present contribution, the innovative in situ Raman micro-spectroscopy was applied to investigate the in vitro reactivity of various bioactive glasses. All the investigated glasses belonged to the Na2O\\K2O-CaO-P2O5-SiO2 system, but contained sensibly different percentages of network modifiers. The glasses were immersed for increasing times, up to 96h, in simulated body fluid (SBF) and in tris-buffered (TRIS) solution. In this way, two fundamental items were addressed, i.e. the effect of the glass composition and the nature of the soaking fluid on the overall reactivity. As regards the SBF, all the glasses were able to promote the formation of a hydroxyl-carbonate apatite (HCA) surface layer in very short times. The reaction rate was particularly quick for the 45S5 Bioglass and for it...

International Nuclear Information System (INIS)

Synthesis of O'/#beta#' SiAlON composites was studied. As starting materials, Si_3N_4, Al_2O_3 and SiO_2 powders were used. Pressureless sintering was applied as consolidation technique and was performed at 1400-1700 C. Densification and reaction taking place during sintering were followed. Microstructure of O'/#beta#' composites is discussed. It was found that without additives liquid phase amount formed within the samples was below critically needed for full densification, but promoted reaction of O' and #beta#' formation. Using yttria as additive densification was enhanced. O'/#beta#' ratio decreased while H_V and K_I_c increased with increasing amount of additive. (orig.).

British Library Electronic Table of Contents (United Kingdom)

Biomass fly ash was treated with alkaline solution to enhance its adsorption capacity of Reactive Black 5 dye. The results revealed that the alkaline concentration, solution to fly ash ratio, treatment temperature and treatment time had a positive effect on the dye adsorption capacity of the treated fly ash (TFA), due to dissolving SiO2 and increasing the proportion of unburned carbon. In addition, the dye adsorption behavior of the TFA in aqueous solution was investigated. The effects of various experimental parameters (initial pH, initial dye concentration and contact time) were determined spectrophotometrically. The dye adsorption capacity of the TFA was maximized at an alkaline pH (8.2-10.4). The adsorption capacity of dye by the TFA increased with increasing initial dye concentration....

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

Short communication.

International Nuclear Information System (INIS)

Oxyfluoride aluminosilicate glasses in the composition of 50SiO2-20Al2O3-20LiF-10GdF3-0.5TmF3-xYbF3 (x = 0, 1.0, 2.5, 5, 7.5, 10, 15, 20, 25 and 30 mol%) have been prepared to study their thermal and optical properties. From the differential thermal analysis measurements, glass transition temperatures and onset crystallization temperatures have been evaluated and from them glass stability factors were calculated. Glass stabilities decreased gradually with fluoride content increment in all the studied glasses. The photoluminescence and decay measurements have also been carried out for all these glasses. In these glasses, an efficient near infrared quantum cutting with optimal quantum efficiency approaching 187% has been demonstrated, by exploring the co-operative downconversion mechanism from Tm3+ to Yb3+, with 467 nm (Tm3+ : 3H6 ? 1G4) excitation wavelength. These glasses are promising materials to achieve high efficiency silicon based solar cells by means of downconversion in the ...

Energy Technology Data Exchange (ETDEWEB)

Successful interface engineering requires compositional and electronic material characterization as a prerequisite for understanding and intentionally generating interfaces in photovoltaic devices. The paper gives an overview with several examples, all referring to Cu(In,Ga)(S,Se){sub 2} ('CIGSSe')-based solar cells, with an emphasis on characterization using highly specialized methods, such as elastic recoil detection analysis, X-ray emission spectroscopy and photoelectron spectroscopy using synchrotron and ultraviolet light for excitation, inverse photoemission spectroscopy and Kelvin probe force microscopy. First, the determination of the depth profile of the band gap energy E{sub g} in the absorber layer is demonstrated. The modification of E{sub g} towards both interfaces is discussed in terms of beneficial electronic effects. Next, the interface between absorber and buffer layers with alternative and promising non-toxic materials is considered. Between CIGSSe ...

Energy Technology Data Exchange (ETDEWEB)

Chromium nitride/Cr coating has been deposited on surface of 316L stainless steel to improve conductivity and corrosion resistance by physical vapor deposition (PVD) technology. Electrochemical behaviors of the chromium nitride/Cr coated 316L stainless steel are investigated in 0.05 M H{sub 2}SO{sub 4}+2 ppm F{sup -} simulating proton exchange membrane fuel cell (PEMFC) environments, and interfacial contact resistance (ICR) are measured before and after potentiostatic polarization at anodic and cathodic operation potentials for PEMFC. The chromium nitride/Cr coated 316L stainless steel exhibits improved corrosion resistance and better stability of passive film either in the simulated anodic or cathodic environment. In comparison to 316L stainless steel with air-formed oxide film, the ICR between the chromium nitride/Cr coated 316L stainless steel and carbon paper is about 30 m{omega} cm{sup 2} that is about one-third of ...

International Nuclear Information System (INIS)

The objectives of this research were to investigate the possibility of controlling the #alpha#'/#beta#' phase ratio and morphology in Sialon ceramics. These objectives have been sought by the control of the starting composition, and by post sintering heat treatment. The main emphasis has been on the production of a series of #alpha#' and (#alpha#'+#beta#') Sialon ceramics with a minimum amount of the glass phase by the pressureless sintering technique and using ytterbium (Yb) as an #alpha#' stabilising element. The Yb additions were made via the oxide or the alumino- silicate presynthesised glass; the latter was found to improve the density. The XRD analysis of the as sintered materials revealed #alpha#' to be the dominant phase with minor contributions from #beta#' sialon and/ or 12H A1N polytype. Additions of SiO_2 or #beta#-Si_3N_4 were made to various materials to assess potential mechanisms for obtaining control over the microstructural development of #alpha#'/#beta#' sialon ...

Science.gov (United States)

In order to reduce the air concentration of (sup 3)H in the reactor buiIding of Wolsung Heavy Water Reactor, a computer code for estimation of adsorption behavior was programmed based on an equation derived for analysis of water vapor adsorption, and a ba...

International Nuclear Information System (INIS)

The effect is reported of seven inorganic oxide additives on both the formation mechanism and the densification of X-Sialon prepared by a silicothermal process. The oxides were added to the starting mixture of halloysite clay, alumina and elemental silicon at a level of 1 wt% of the calculated final product, and fired in nitrogen at 1200-1500 deg C. The formation of X-Sialon was monitored by thermal analysis, powder XRD and 2"7"Al and "2"9Si solid state MAS NMR The effects of the additives are temperature dependent and influence the various stages of the reaction by differing degrees. The oxides which best promote the formation of crystalline X-Sialon (Y_2O_3, CaO and MgO) are also those which facilitate the conversion of initially-formed Si_3N_4 to SiO_2N_2 and SiO_3N units. Densification is most enhanced by Y_2O_3 CaO and CeO_2; MgO exerts its maximum effect on sintering at lower temperatures. Copyright (1998) Australasian Ceramic Society

International Nuclear Information System (INIS)

Inductively coupled plasma etching of InGaP, AlInP and AlGaP in BI_3 or BBr_3 discharges was investigated as a function of source power, dc chuck bias and plasma composition. InGaP etches at the fastest rates (>6000 Angstrom min"-"1) in both chemistries, followed by AlGaP. It is found that AlInP provides an excellent etch stop for the other two materials in both mixtures. The InGaP surface morphology improves with increasing BI_3 or BBr_3 content, and with increasing dc chuck bias. The etched features for this material are highly anisotropic. Etch selectivities for InGaP over SiO_2 and SiN_x of #>=#8 are obtained in both plasma chemistries, and there is no etch incubation time with either mixture, indicating that both can scavenge the native oxide on InGaP, AlGaP and AlInP. copyright 1998 American Vacuum Society.

International Nuclear Information System (INIS)

We demonstrate that the excess vacancies induced by a 1 MeV Si implant reduce the excess interstitials generated by a 40 keV Si implant during thermal annealing when these two implants are superimposed in silicon. It is shown that this previously observed reduction is dominated by vacancy annihilation and not by gettering to deeper interstitial-type extended defects. Interstitial supersaturations were measured using B doping superlattices (DSL) grown on a silicon-on-insulator (SOI) substrate. Implanting MeV and keV Si ions into the B DSL/SOI structure eliminated the B transient enhanced diffusion normally associated with the keV implant. The buried SiO_2 layer in the SOI substrate isolates the deep interstitials-type extended defects of the MeV implant, thereby eliminating the possibility that these defects getter the interstitial excess induced by the keV Si implant. copyright 1999 American Institute of Physics.

International Nuclear Information System (INIS)

An analysis of the passive films formed on amorphous alloys of the system Fe-10% Cr-5% Mo-P-metalloid and Fe-10% Cr-5% Mo-B-Si revealed that they are more markedly enriched with chromium in silicon-free alloys. In silicon-containing amorphous alloys the passive films were highly enriched with silicon, which occurred in these films in the form of a corrosion product close to SiO_2. As shown by the investigations of a study of the anodic behavior of Fe_4_0Ni_4_0P_1_4B_6 and Fe_4_0Ni_3_8Mo_4B_1_8, phosphorus facilitates the passivation of amorphous alloys by reducing the solution current in the active state and enriching the surface layers of the metal in the form of a black prepassivation film which also contains nickel and iron. The behavior of Fe-Ni amorphous alloys containing only boron as metalloid additive differs little from that of crystalline alloys of similar composition but without the boron. The authors note that in this survey they have considered the influence of only some ...

International Nuclear Information System (INIS)

A family of sealant materials has been developed for use in the solid oxide fuel cell (SOFC) and in other applications in the temperature range of 800 endash 1000 degree C. These materials are based on glasses and glass-ceramics in the SrO endash La_2O_3 endash Al_2O_3 endash B_2O_3 endash SiO_2 system. The coefficients of thermal expansion (CTE) for these materials are in the range of 8 endash 13x10"-"6/degree C, a good match with those of the SOFC components. These sealant materials bond well with the ceramics of the SOFC and, more importantly, form bonds that can be thermally cycled without failure. At the fuel cell operating temperature, the sealants have viscosities in the range of 10"4-10"6 Pa-s, which allow them to tolerate a CTE mismatch of about 20% among the bonded substrates. The gas tightness of a sample seal was demonstrated in a simple zirconia-based oxygen concentration cell. copyright 1996 Materials Research Society.

British Library Electronic Table of Contents (United Kingdom)

Cobalt supported on Beta zeolite catalysts were prepared by impregnation of metal salts in aqueous solution and were tested for the Fischer Tropsch reaction. The support consisted of a Beta zeolite composed by crystallites of nanometric dimensions and a SiO2/Al2O3 molar ratio of about 50. This support was impregnated with Co(NO3)2 aqueous solution using different metal loads of 7.5, 10, 15 and 20wt% Co. These materials were characterized by X-ray diffraction (XRD), high resolution transmission electron microscopy (HRTEM), N2 adsorption (BET), thermal programmed reduction (TPR) and FTIR of adsorbed pyridine (i.e., surface acid sites distribution). All the catalysts showed a significant catalytic activity for the F-T reaction from synthesis gas (CO+2H2), in a continuous fixed bed reactor sys...

Science.gov (United States)

This report discusses the following: (1) improving models of vapor-dominated geothermal fields: the effects of adsorption; (2) adsorption characteristics of rocks from vapor-dominated geothermal reservoir at the Geysers, CA; (3) optimizing reinjection strategy at Palinpinon, Philippines based on chloride data; (4) optimization of water injection into vapor-dominated geothermal reservoirs; and (5) steam-water relative permeability.

Science.gov (United States)

No Abstract Available

Science.gov (United States)

... Accession Number : ADD257320. Title : Sputter Deposition of Yttrium-Oxides. Descriptive Note : Journal article,. Corporate ...

Energy Technology Data Exchange (ETDEWEB)

X-ray ablation of material from the first wall and other components of an ICF (Inertial Confinement Fusion) chamber is a major threat to the laser final optics. Material condensing on these optics after a shot may cause damage with subsequent laser shots. To ensure the successful operation of the ICF facility, removal rates must be predicted accurately. The goal for this dissertation is to develop an experimentally validated x-ray response model, with particular application to the National Ignition Facility (NIF). Accurate knowledge of the x-ray and debris emissions from ICF targets is a critical first step in the process of predicting the performance of the target chamber system. A number of 1-D numerical simulations of NIF targets have been run to characterize target output in terms of energy, angular distribution, spectrum, and pulse shape. Scaling of output characteristics with variations of both target yield and hohlraum wall thickness are also described. Experiments have been ...

Energy Technology Data Exchange (ETDEWEB)

Ti and its alloys (Ti-6Al-4V) have been used in different engineering applications due to their several outstanding properties. Nevertheless, their use in practical applications is limited in many cases due to their poor tribological property. Researches are ongoing on surface modification of Ti based materials by different plasma and ion based techniques to overcome this problem. However, the conventional plasma nitriding techniques have several problems such as formation of an arc, increased possibility of surface contamination due to a comparatively higher operating pressure, production of a very thin nitrided layer after a long processing time, etc. In this present work, the possibility of a new low-pressure plasma nitriding process using a Plasma Enhanced Chemical Vapor Deposition (PECVD) based saddle field fast atom beam source on a Ti-6Al-4V alloy sample is investigated. Plasma nitriding was carried out at 900 deg. C and at a pressure ...

Energy Technology Data Exchange (ETDEWEB)

Neutron Coded Aperture Imaging is a nondestructive imaging technique that utilizes neutrons scattered from an object through specially designed apertures. Coded Aperture Imaging is an alternative technique to Computed Tomography for three-dimensional imaging. Coded Aperture Imaging has the advantage that all of the three-dimensional information is contained in a single image, whereas Computed Tomography requires several images or projections. This technique has been implemented by other using photographic film as an image recording medium and optical reconstruction or decoding of the images. In this work, the possibility of using a real-time neutron video camera to record the images, followed by digital decoding methodology has been investigated. Because only a small fraction of the neutrons incident on the object are scattered to the neutron camera, a new neutron beamport facility, with a larger neutron flux (7.3 x 10[sup 7] n/cm[sup 2]/s) than the previous facility was constructed. A ...

Energy Technology Data Exchange (ETDEWEB)

We describe the growth, fabrication, and characterization of an ultraviolet (UV) photoconductive detector based on In{sub x}Al{sub y}Ga{sub 1-x-y}N quaternary alloy that is lattice matched to GaN. The detector consisted of 0.1 {mu}m In{sub x}Al{sub y}Ga{sub 1-x-y}N alloy grown on 0.5-1.0 {mu}m GaN epilayer by metalorganic chemical vapor deposition. With varying indium concentration, the cut-off wavelength of the In{sub x}Al{sub y}Ga{sub 1-x-y}N detectors could be varied to the deep UV range. The most important and intriguing result is that the responsivity of the In{sub x}Al{sub y}Ga{sub 1-x-y}N quaternary alloy exceeded that of AlGaN alloy of a comparable cutoff wavelength by a factor of five. This makes the nitride quaternary alloy very important material for solar blind UV detectors applications particularly in the deep UV range where Al rich AlGaN alloys have problems with low quantum efficiency and cracks due in part to lattice mismatch ...

Energy Technology Data Exchange (ETDEWEB)

The optically stimulated luminescence (OSL) results a highly appropriate dosimetric technique for readings of absorbed radiation 'in alive' and 'in situ', as well as in real time. The CVD diamond on the other hand presents excellent qualities like radiation reader thanks to its reproducibility, radiation resistance, biocompatibility and non toxicity. The present work studies the answer of two diamond films pure and polluted with nitrogen (750 ppm) grown by the Chemical Vapor Deposition method (CVD) on silicon substrate (001) irradiated with beta (Sr-90) in the 0.833-100 Gy interval. The optical stimulation was carried out by 40 seconds with infrared laser (830 nm, 0.36 W/cm{sup 2}) and the filter BG-39 (300-600 nm) coupled the PM. The intensity and the decay of the hyperbolic type of the LOE curves were similar in both samples, for the non doped diamond were observed trapping states in 200-380 C being ...

International Nuclear Information System (INIS)

In order to practice design-by-analysis of thermohydraulics design of BWR fuel rod bundles, the subchannel analysis would play a major role. There, one of the immediate concerns is improvement in its predictive capability of boiling transition phenomena on the fuel rod surface. This capability strongly depends on the modeling of thermohydraulics phenomena of interests: 1) vapor-liquid redistribution by inter-subchannel exchanges due to the diversion cross flow, turbulent mixing and void drift, 2) liquid film behaviors, 3) transition of two-phase flow regimes, 4) droplet entrainment and deposition and 5) spacer-droplet interactions. These are considered to be five key factors in understanding the BT in BWR fuel rod bundles. This paper describes a progress and current status in the second year of the three year project on developing generalized boiling transition models with the above five key factors being focused on. A combined approach of ...

Energy Technology Data Exchange (ETDEWEB)

Because of the importance of water vapor, the ARM program initiated a series of three intensive operating periods (IOPs) at its CART (Cloud And Radiation Testbed) site. The goal of these IOPs is to improve and validate the state-of-the-art capabilities in measuring water vapor. To date, two of the planned three IOPs have occurred: the first was in September of 1996, with an emphasis on the lowest kilometer, while the second was conducted from September--October 1997 with a focus on both the upper troposphere and lowest kilometer. These IOPs provided an excellent opportunity to compare measurements from other systems with those made by the CART Raman lidar. This paper addresses primarily the daytime water vapor measurements made by the lidar system during the second of these IOPs.

Energy Technology Data Exchange (ETDEWEB)

This study aims to develop a particulate model combining solid waste particle combustion and heavy metal vaporization from burning particles during MSW incineration in a fluidized bed. The original approach for this model combines an asymptotic combustion model for the carbonaceous solid combustion and a shrinking core model to describe the heavy metal vaporization. A parametric study is presented. The global metal vaporization process is strongly influenced by temperature. Internal mass transfer controls the metal vaporization rate at low temperatures. At high temperatures, the chemical reactions associated with particle combustion control the metal vaporization rate. A comparison between the simulation results and experimental data obtained with a laboratory-scale fluid bed incinerator and Cd-spiked particles shows that the heavy metal vaporization is ...

Energy Technology Data Exchange (ETDEWEB)

Laser optical pumping can be used to produce polarized alkali atom beams or polarized alkali vapor targets. Polarized alkali atom beams can be converted into polarized alkali ion beams, and polarized alkali vapor targets can be used to produce polarized H/sup -/ or /sup 3/He/sup -/ ion beams. In this paper the authors discuss how the polarized alkali atom beams and polarized alkali vapor targets are used to produce polarized ion beams with emphasis on the production of polarized negative ion beams.

Energy Technology Data Exchange (ETDEWEB)

Molar enthalpies of sublimation of 1,2,4-, 1,2,3-, and 1,3,5-tri-hydroxy-benzene, were obtained from the temperature dependence of the vapor pressure measured by the transpiration method. The molar enthalpies of fusion and molar heat capacities of these compounds were measured by DSC. The measured data sets of vaporization, sublimation and fusion enthalpies were checked for internal consistency. Strength of the inter- and intra-molecular hydrogen bonding in di- and tri-hydroxy-benzenes have been assessed.

Energy Technology Data Exchange (ETDEWEB)

Using gasoline as an example of additives for cold start improvement, fuel vapor composition of methanol-gasoline mixtures, fuel evaporation rate in consideration of temperature drop due to heat of fuel evaporation, air fuel ratio, stoichiometric air fuel ratio and excess air ratio of fuel vapor were calculated. The mixture formation of methanol-gasoline mixtures at low temperature in otto cycle engines was studied. Van Laar's empirical formula was used to estimate the partial pressure of high-percentage methanol blends. It was found that the most part of fuel vapor is occupied by gasoline, even when a small amount of gasoline is added to methanol resulting to an extremely small excess air ratio. It is obvious that this vapor pressure adjustment using gasoline is the dominant factor for improvement in cold startability. (10 figs, 1 tab, 10 refs)

Energy Technology Data Exchange (ETDEWEB)

We present a 1-D heat transfer, melting, vaporization and resolidification model describing the interaction of a scanning continuous-wave laser with a metal surface wherein the beam power is constant. A physical model based on the Stefan problem is developed with appropriate boundary conditions. The effects of processing parameters on process variables are investigated numerically by varying beam diameters, scan speeds and substrate temperatures for Nickel. Relations are derived for the times to initiate melting, to initiate vaporization, to reach maximum melting depth, for melting-resolidification, and for maximum melting and vaporization depths. Surface temperatures are compared with approximate closed form solutions. (Author)

British Library Electronic Table of Contents (United Kingdom)

In radio signal-based observing systems, such as Global Positioning System (GPS) and Interferometric Synthetic Aperture Radar (InSAR), the water vapor in the atmosphere will cause delays during the signal transmission. Such delays vary significantly with terrain elevation. In the case when atmospheric delays are to be eliminated from the measured raw signals, spatial interpolators may be needed. By taking advantage of available terrain elevation information during spatial interpolation process, the accuracy of the atmospheric delay mapping can be considerably improved. This paper first reviews three elevation-dependent water vapor interpolation models, i.e., the Best Linear Unbiased Estimator in combination with the water vapor Height Scaling Model (BLUE?+?HSM), the Best Linear Unbiased Es...

Energy Technology Data Exchange (ETDEWEB)

Apparatus and method are described for the vaporization of liquid fuel oils to produce a gaseous mixture suitable for burning in a burner normally designed for operation utilizing natural gas.

British Library Electronic Table of Contents (United Kingdom)

In this study, we thoroughly analyzed abrupt behaviors, trends, and periodicity properties of water vapor flux and moisture budget entering and exiting the four edges of the Pearl River basin based on the NCAR/NCEP reanalysis dataset by using the continuous wavelet transform and the simple two-phase linear regression technique. Possible implications for hydrological cycle and water resource management of these changes are also discussed. The results indicate that: (1) the water vapor propagating through the four edges of the Pearl River basin is decreasing, and it is particularly true for the changes of the water vapor flux exiting from the north edge of the study river basin. The transition point from increase to decrease occurs in the early 1960s; (2) The wavelet transform spectra indica...

International Nuclear Information System (INIS)

In areas where radiation dose monitoring has not been performed, it is essential to use material available in the environment be able to rapidly assess doses to individuals for immediate emergency medical care or for general estimation of the radiological consequences. It was shown that certain types of telephone cards containing microchips have the potential to be used as individual radiation dosimeters in emergency situations to detect doses over 250 mGy by luminescence measurements. In order to understand the dosimetric properties of chip cards, the components obtained from INFINIEON Company at various stages of production were used for luminescence measurements. It is found that the protecting layer used above the chips so called 'globe top' is the main source of radiation induced signal in chip cards. The globe top produced by INFINIEON at that stage is found to contain SiO2 and Epoxy. In order to improve the dosimetric properties of the chip cards, the raw material of the globe ...

Energy Technology Data Exchange (ETDEWEB)

This document provides stakeholder evaluations on innovative technologies to be used in the remediation of volatile organic compounds from soils and ground water. The technologies evaluated are; in-well vapor stripping, in-situ bioremediation, and gas membrane separation.

Energy Technology Data Exchange (ETDEWEB)

This project dealt with use of condensing heat exchangers to recover water vapor from flue gas at coal-fired power plants. Pilot-scale heat transfer tests were performed to determine the relationship between flue gas moisture concentration, heat exchanger design and operating conditions, and water vapor condensation rate. The tests also determined the extent to which the condensation processes for water and acid vapors in flue gas can be made to occur separately in different heat transfer sections. The results showed flue gas water vapor condensed in the low temperature region of the heat exchanger system, with water capture efficiencies depending strongly on flue gas moisture content, cooling water inlet temperature, heat exchanger design and flue gas and cooling water flow rates. Sulfuric acid vapor condensed in both the high temperature and low temperature regions of the heat ...

Energy Technology Data Exchange (ETDEWEB)

Measurements of the double-electron-capture process in which a positive ion of iodine becomes a negative ion in a single collision with a magnesium atom are reported between 20 and 90 keV. The cross section is comparable to that for the rare gases and not as large as might be expected from a two-valence-electron atom. This process is probably insignificant in the production of negative ion beams using a magnesium-vapor target.

International Nuclear Information System (INIS)

Oxide ionic conductivities of (CeO_2)_x(Sc_2O_3)_(_0_._1_1_-_x_)(ZrO_2)_0_._8_9 (x = 0.01-0.10) electrolytes were optimized for the application in intermediate-temperature solid oxide fuel cell (IT-SOFC). Powders with different contents of CeO_2 and Sc_2O_3 were prepared via a co-precipitation method. The obtained powders and pellets were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS) and impedance spectroscopy. Among all the compositions, (CeO_2)_0_._0_4(Sc_2O_3)_0_._0_7(ZrO_2)_0_._8_9(4Ce7ScZr) gives the highest ionic conductivity of 0.065 S cm"-"1 at 800 "oC. The effects on densification and electrical properties of different sintering additives, such as SiO_2, MgO, Co_3O_4, MoO_3 and Bi_2O_3, were studied and different conducting behavior with these additives were observed. The densification temperatures of CeO_2 and Sc_2O_3 co-doped electrolytes can be reduced by around 280 "oC with the addition of 1 mol% of ...

Science.gov (United States)

In the present work, a new kind of myoglobin (Mb)/Au nanoparticles composite film was fabricated on pyrolytic graphite (PG) electrodes. Oppositely charged chitosan (CS) and silica (SiO(2)) nanoparticles were alternately adsorbed on the PG surface by the electrostatic interaction between them, forming {CS/SiO(2)}(5) layer-by-layer films. Mb and HAuCl(4) in solution were then simultaneously loaded into {CS/SiO(2)}(5) films. The loaded Au(III) in the films were electrochemically reduced into Au nanoparticles, forming nanocomposite films, designated as {CS/SiO(2)}(5)-Mb-Au. Various techniques such as cyclic voltammetry (CV), square wave voltammetry (SWV), quartz crystal microbalance (QCM), electrochemical impedance spectroscopy (EIS), scanning electron microscopy (SEM), and energy dispersive X-ray (EDX) analysis were used to characterize the films. Compared with {CS/SiO(2)}(5)-Mb films without Au nanoparticles inside, the {CS/SiO(2)}(5)-Mb-Au films exhibited much better behavior in ...

Energy Technology Data Exchange (ETDEWEB)

Chemical looping combustion (CLC) of simulated coal-derived synthesis gas was conducted with NiO oxygen carriers supported on SiO2, ZrO2, TiO2, and sepiolite. The effect of H2S on the performance of these samples for the CLC process was also evaluated. Five-cycle thermogravimetric analysis (TGA) tests at 800 C indicated that all oxygen carriers had a stable performance at 800 C, except NiO/SiO2. Full reduction/oxidation reactions of the oxygen carrier were obtained during the five-cycle test. It was found that support had a significant effect on reaction performance of NiO both in reduction and oxidation rates. The reduction reaction was significantly faster than the oxidation reaction for all oxygen carriers, while the oxidation reaction is fairly slow due to oxygen diffusion on NiO layers. The reaction profile was greatly affected by the presence of H2S, but there was no effect on the capacity due to the presence of H2S in synthesis gas. The presence of H2S decreased reduction ...

International Nuclear Information System (INIS)

... deposition evaporation fission products fluorides iodine 134 laboratory

Science.gov (United States)

... wood, kitchen wastes, and human faeces. The ash from such waste burning shall be deposited and ...

Energy Technology Data Exchange (ETDEWEB)

Short communication.

J-STORE (Japan)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

The possibilities to grow isolated structures of complex oxides by pulsed laser deposition through stencils were investigated. A stencil consisting of a SiN membrane with apertures of several hundred nanometers embedded in a Si chip is placed in front of a heated substrate (up to 750 degrees Celsius). Deposition through these apertures results in resistless, direct patterning by local deposition of complex oxides like ferroelectric Lead Zirconate Titanate. The created isolated structures were analyzed by AFM imaging. Under-deposition, in this work called broadening, is inevitable during stencil deposition and is depending on deposition parameters, especially pressure. Different causes of broadening are mapped and discussed.

International Nuclear Information System (INIS)

YBa_2Cu_3O_7_-_x thick films have been deposited on silver sheets and MgO single crystals by spray pyrolysis. Film texture is related to film thickness and sintering temperature. The X-ray intensity ratio of the 005 peak to the 110 peak is higher for thin films deposited at the higher temperatures. However, elevated temperatures promote copper diffusion and second-phase formation in films deposited on silver. Films deposited on MgO can have larger grain sizes and are more oriented than those deposited on silver.

Energy Technology Data Exchange (ETDEWEB)

A new magnetic macroparticle filter design consisting of two 90{sup o} filters forming an S-shape is described. Transport properties of this S-filter are investigated using Langmuir and deposition probes. It is shown that filter efficiency is product of the efficiencies of two 90{sup o} filters and the deposition rate is still acceptably high to perform thin film deposition. Films of amorphous hard carbon have been deposited using a 90{sup o} filter and the S-filter, and macroparticle content of the films are compared.

Energy Technology Data Exchange (ETDEWEB)

The understanding of fission product deposition in realistic steam generator conditions is needed for release estimates in PSA studies, and for the design of efficient accident management procedures. This is considered very important because primary-to-secondary leakages risk dominant sequences in many plants. Furthermore, the decay heat of the fission product deposits adds to the thermal load to the steam generator tubes also in other sequences, especially in case of cold leg leakages. This brings out the concern of induced steam generator tube ruptures in cases, where the steam generators are initially intact. The experimental data showed that the highest deposited fraction within the tubes were found in cases with lowest flow velocities. The minimum value of the deposited fraction was observed at intermediate flow velocities. With these relatively low Reynolds numbers, the results calculated with ...

Energy Technology Data Exchange (ETDEWEB)

Real-time neutron radiography has been used to study the dynamic behavior of two-phase flow and measure vapor fractions in a steam-water duct at atmospheric pressure. This unique experimental technique offers one the opportunity to observe and record on videotape now Patterns and transient behavior of two-phase flow inside opaque containers without perturbing the environment. The neutron radiographic technique is non-intrusive and requires no special transparent window region. Data are recorded simultaneously over a large area of interest. Image processing of the video data can be employed to measure bubble velocities and time-averaged and Instantaneous vapor fractions.

Science.gov (United States)

We present a numerical model of vapor-dominated reservoirs which is based on the well-known conceptual model of White, Muffler, and Truesdell. Computer simulations show that upon heat recharge at the base, a single phase liquid-dominated geothermal reservoir in fractured rock with low matrix permeability will evolve into a two-phase reservoir with B.P.D. (boiling point-for-depth) pressure and temperature profiles. A rather limited discharge event through cracks in the caprock, involving loss of only a few percent of fluids in place, is sufficient to set the system off to evolve a vapor-dominated state. The attributes of this state are discussed, and some features requiring further clarification are identified. 26 refs., 5 figs.

Energy Technology Data Exchange (ETDEWEB)

A study was made of employee exposure to oil sludge and vapors during oil-sludge removal and maintenance activities at the Alyeska Pipeline Service Company's Ballast Water Treatment Facility, Valdez, Alaska. Total hydrocarbons, except benzene, toluene, and xylene, showed concentrations from 371 to 1228mg/m3. Of eight maintenance workers, five reported headache, dizziness, or nausea when working without a respirator. The authors conclude that workers were potentially exposed to benzene vapors and total hydrocarbon vapors exceeding the evaluation criteria for these substances. The authors recommend the use of respiratory protection measures to reduce exposures during work operations.

Science.gov (United States)

Using the infrared spectroscopy method, we have studied the effect of thermal dehydration (under vacuum and in air) and treatment with water vapor on the acid centers of very high silicon zeolites of the ZSM type. We have shown that dehydration under vacuum and in air completely and irreversibly removes the OH groups at 1120/sup 0/K, while treatment with water vapor removes these groups at 770/sup 0/K. The Lewis acid centers of dehydrated zeolites (represented by two types of centers) are more heat-stable than the Bronsted acid centers, but the vapor treatment at 1020/sup 0/K leads to the disappearance of the Lewis acid centers. In this work, we discuss the reasons for destruction of the acid centers of the zeolites under different treatment conditions.

International Nuclear Information System (INIS)

Hydrogen (H) plasma treatment, oxygen (O) plasma treatment and water (H_2O)-vapor heat treatment for polycrystalline-silicon (poly-Si) thin-film transistors (TFTs) have been analyzed by separately extracting trap density at a front silicon-oxide interface (D_F) and trap density at a back interface (D_B). It is found that the H plasma treatment is apt to generate D_F and D_B. The O plasma treatment reduces D_F, while the H_2O-vapor heat treatment reduces both D_F and D_B. Improvement of transistor characteristics of poly-Si TFTs depends on understanding these results.

Energy Technology Data Exchange (ETDEWEB)

Full text of publication follows:In order to practice a design-by-analysis of thermohydraulics design of BWR fuel rod bundles, the subchannel analysis would play a major role. There, the immediate concern is improvement in its predictive capability of CHF due in particular to the film dryout (boiling transition phenomena: BT) on the fuel rod surface. Constitutive equations in the subchannel analysis formulation are responsible for the quality of calculated results. The constitutive equations are a result of integration of the local and instantaneous description of two-phase flows over the subchannel control volume. In general, they are expressed in terms of subchannel-control-volume- as well as area-averaged two-phase flow state variables. In principle the information on local and instantaneous physical phenomena taking place inside subchannels must be counted for in the algebraic form of the equations on the basis of a more mechanistic modeling approach. They should include also ...

Energy Technology Data Exchange (ETDEWEB)

This SBIR Phase I developed neutron detectors made from gallium arsenide (GaAs) p-type/ intrinsic/n-type (P-I-N) diodes grown by metalorganic chemical vapor deposition (MOCVD) onto semi-insulating (S1) bulk GaAs wafers. A layer of isotonically enriched boron-10 evaporated onto the front surface serves to convert incoming neutrons into lithium ions and a 1.47 MeV alpha particle which creates electron-hole pairs that are detected by the GaAs diode. Various thicknesses of ''intrinsic'' (I) undoped GaAs were tested, as was use of a back-surface field (BSF) formed from a layer of Al{sub x}Ga{sub 1-x}As. Schottky-barrier diodes formed from the same structures without the p+ GaAs top layer were tested as a comparison. After mesa etching and application of contacts, devices were tested in visible light before application of the boron coating. Internal quantum efficiency (IQE) of the best diode near the GaAs bandedge ...

British Library Electronic Table of Contents (United Kingdom)

A methodology for the determination of the rare earth elements in uranium oxides by ion microprobe has been set up on a Cameca ims-3f instrument. An uranium oxide reference material from a syn-metamorphic uranium deposit related to albitisation has also been developed for this type of analysis. Applications of the methodology are presented for a series of uranium oxides selected from some major uranium deposit types: from the world's highest grade unconformity-related uranium deposit from the Athabasca Basin (Saskatchewan, Canada; the Shea Creek and the McArthur River examples), a perigranitic vein-type deposit (Pen Ar Ran, Vendee, France) and a volcanic caldera-related deposit (Streltsovkoye, Transbaikalia, Russia). Each type of uranium deposit appears to have a specific REE signature. Al...

International Nuclear Information System (INIS)

A ternary nickel-base alloy Ni-W-B has been developed for surface corrosion and wear resistance to replace chromium plating, which uses environmentally hazardous solutions. The deposition conditions used an alkaline bath and insoluble anodes. The as-deposited alloy typically contains 40 wt% W and 1 wt% B and has an amorphous or partially amorphous structure. These deposits compare favorably with hexavalent chromium deposits in throwing power, color uniformity, and reflectivity. The corrosion resistance of Ni-W-B alloy was compared with hexavalent chromium and electroless nickel deposits in a variety of acids, including hydrochloric, sulfuric, fluoroboric, and phosphoric. In all cases, best results were obtained with the Ni-W-B deposits.

Energy Technology Data Exchange (ETDEWEB)

Previous analyses of binary cycles for conversion of geothermal energy from moderate temperature resources to electrical energy have shown potential gains in net geofluid effectiveness on the order of 8%, resulting from selection of turbine-expansion processes whose equilibrium states pass through the two-phase region. If condensation occurs, this gain could be reduced or eliminated by the resulting loss in turbine efficiency. Experience with many fluids, however, indicates that vapor supersaturation permits metastable pure-vapor states to exist at temperatures considerably below the saturation temperature at a given pressure; thus, by better understanding the condensation process, and properly structuring the cycle, substantial performance gains may be possible. The purpose of the present study was to assess the probability for attaining this performance gain by estimating the extent of condensation which might be expected during such an ...

Energy Technology Data Exchange (ETDEWEB)

Soil vapor extraction (SVE) is a widely accepted in-place treatment technology that uses forced air to remove contaminant vapors from zones of permeable vapor flow, thereby enhancing the volatilization of contaminants from the subsurface. The resulting off-gases are contaminated with volatiles and semi-volatiles and have to treated by catalytic or thermal destruction systems, activated carbon adsorbers, or bioreactors. Of these, activated carbon adsorption is the most commonly used technology. From the theoretical foundation of SVE and carbon adsorption, two nomographs were developed for remedial investigation, feasibility studies, planning, operation, and preliminary design purposes. An advantage of such nomographs is that they graphically indicate the sensitivity of the remediation process to different design parameters and critical ranges within a given parameter. In effect, nomographs can help to foster an intuitive ...

Science.gov (United States)

Some vapor-dominated geothermal reservoirs and low-permeability gas reservoirs exhibit anomalous behavior that may be caused by surface adsorption. For example, geothermal reservoirs in the Larderello area of Italy and reservoirs in the Geysers Geothermal...

Energy Technology Data Exchange (ETDEWEB)

A program is currently in progress at Argonne National Laboratory to evaluate and develop evaporator technology for concentrating radioactive waste streams. By concentrating radioactive waste streams, disposal costs can be significantly reduced. To effectively reduce the volume of waste, the evaporator must achieve high decontamination factors so that the distillate is sufficiently free of radioactive material. One technology that shows a great deal of potential for this application is being developed by LICON, Inc. In this program, Argonne plans to apply LICON`s evaporator designs to the processing of radioactive solutions. Concepts that need to be incorporated into the design of the evaporator include, criticality safety, remote operation and maintenance, and materials of construction. To design an effective process for concentrating waste streams, both solubility and vapor-liquid equilibrium data are needed. The key issue, however, is the high decontamination ...

UK PubMed Central (United Kingdom)

Elemental mercury has been imbued with magical properties for millennia, and various cultures use elemental mercury in a variety of superstitious and cultural practices, raising health concerns for...Full Text Available

Science.gov (United States)

Mar 1, 2011 ... The movement of hydrothermal fluids and/or fumarolic vapors through local rocks prior ... The Solar Energetic Particle Event of December 14, 2006 .... for measurement of non-precipitating cloud hydrometeors and aerosols, ...

Energy Technology Data Exchange (ETDEWEB)

In this paper uptake of tritium by market foods from tritiated water vapor in the air is investigated using cereals and beans purchased in Deep River, Canada. The concentrations of tissue free water tritium (TFWT) and organically bound tritium (OBT) range from 12 to 79% and from 10 to 38% respectively, of that estimated for atmospheric water vapor of the sampling month. The specific activity ratios of OBT to TFWT were constant for cereals, but variable for beans. The elevated OBT was shown to be the result of isotopic exchange of labile hydrogen by the fact that washing the foods with tritium free-water reduced their tritium contents to levels characteristic of their production sites.

International Nuclear Information System (INIS)

Natural convection of vaporizing Deuterium at 25 K transports the heat generated in the moderator cell of the cold neutron source to a He cooled condenser. The thermohydraulics of this thermosiphon were precalculated and the results verified by experiments in a 1:1 model using D_2 as fluid. The experimental results show that the thermosiphon operates stable. The demanded liquid content of the cell as well as wall temperatures below 50 K can be ensured by a proper design of the cell outlet flow geometry. A 7 min. loss of cryogenic power results in transient temperatures of the cell wall of not more than 300 K.

Energy Technology Data Exchange (ETDEWEB)

The production of polarized negative ion beams by ''collisional pumping'' is described. Collisional pumping utilizes repeated charge changing collisions in a thick electron-spin-polarized gas or vapor target to form a polarized fast atom beam. The polarized fast atom beam is then partially converted into a polarized negative ion beam in a vapor target. Analysis is presented for a hydrogen beam passing through either a thick polarized H atom target or a thick polarized alkali target. Large polarizations and large currents may be possible.

Energy Technology Data Exchange (ETDEWEB)

A thermodynamic model was used to estimate enthalpy of solution of carbon dioxide (CO{sub 2}) in methyldiethanolamine (MDEA) aqueous solutions. The model was based on a set of equations for chemical equilibria, phase equilibria, charge, and mass balances. Non-ideality in the liquid phase was taken into account by interaction parameters fitted to (vapor + liquid) equilibrium data. The enthalpies of solution of CO{sub 2} were derived from the model using classical thermodynamic relations and were compared to experimental values obtained in previous works.

Energy Technology Data Exchange (ETDEWEB)

The Dental Investigation Service, USAFSAM, Brooks AFB, has outlined the need for a vacuum unit to be used in the Air Force dental clinics. The unit must be capable of effectively picking up mercury and at the same time not redistribute mercury vapors throughout the dental clinic during normal operations or mercury-spill situations. The Dental Investigation Service selected the MRS-3, Minuteman Mercury Recovery System, product of American Cleaning Equipment Corporation as the mercury vacuum to be used for T E. The USAF OEHL/ECH was requested by the Dental Investigation Service to perform the T E on the MRS-3 for possible health hazards due to exposures of mercury vapors.

International Nuclear Information System (INIS)

In this paper the diffusion of tritiated water vapor into concrete walls is studied to evaluate tritiated water retention capacity of a fusion reactor concrete building. Using a model of the tritiated water diffusion determined form experimental results, depth profiles of tritiated water in concrete are calculated in the case of being exposed to air containing tritiated water vapor during the normal operational condition of a fusion reactor. A 0.5-m-thick concrete is sufficient for reactor hall walls from a viewpoint of the tritium containment.

Science.gov (United States)

Analytical relations are obtained for estimating how the distributions of temperature and heat flux vary along a steam-generating tube and how the steam-generator power output reduces due to formation and accumulation of deposits.

Science.gov (United States)

This report results from a contract tasking Eindhoven University of Technology as follows: The contractor will investigate the plasma treatment of surfaces and plasma enhanced deposition using EUT's cascade arc source as the basis for this effort.

International Nuclear Information System (INIS)

... 194 p. auger electron spectroscopy decomposition deposition interfaces oxygen

International Nuclear Information System (INIS)

Adult and newborn rats were exposed to "2"3"9PuO_2 aerosols of four different size distributions. Rats of both ages were killed at intervals between 1 hr and 60 days postexposure. There were marked age- and particle-related size differences in deposition, although retention was similar throughout. The differences in deposition are attributable to relatively greater deposition of larger particles in the upper respiratory tracts of newborns.

Energy Technology Data Exchange (ETDEWEB)

A compact cesium deposition system was used for direct deposition of cesium atoms and ions onto the inner surface of the 1/3 scale Hydrogen Negative Ion Source for the LHD-NBI system. A small, well defined amount of cesium deposition in the range of 3-200 mg was tested. Negative ion extraction and acceleration were carried out both in the pure hydrogen operation mode and in the cesium mode. Single Cs deposition of 3-30 mg to the plasma chamber have produced temporary 2-5 times increases of H-yield, but the yield was decreased within several discharge pulses to the previous steady-state value. Two consecutive 30 mg depositions done within a 3-5 hours/60 shot interval, produced a similar temporary increase of H-beam, but reached a larger H-yield steady-state value. Deposition of larger 0.1-0.2 g Cs portions with a 20-120 hours/150-270 shot interval improved the ...

Energy Technology Data Exchange (ETDEWEB)

The question about expanding the boundaries of the open pit mining method is examined. The use of methods which consider the advantages of open and underground mining operations with their joint use in horizontal and evenly dipping deposits will make it possible to objectively select the mining method, to expand the range of use of open pit mining operations in the deposits of the Far North and provide an improvement in the technical and economic indicators of mineral extraction.

Energy Technology Data Exchange (ETDEWEB)

This report measured the rate of isothermal deposition of sub-micron particles of magnetite onto the surface of Alloy 800 at pH of 4.2-9.3 at Re=10,000 and a fluid temperature of 25C. Deposition is modelled as a two-step process, the transport of particles to the surface region followed by attachment to the surface.

Energy Technology Data Exchange (ETDEWEB)

Pd/sub 2/Si formation at the Pd-Si interface induced by irradiation with ions having a wide range of nuclear energy of deposition density has been investigated. It is found that the thickness of the silicide layer formed by irradiation is proportional to the ion fluence for irradiation with ions having low energy-deposition densities, while it is proportional to the square root of the fluence for irradiation with ions having energy-deposition densities. The results indicate that Pd/sub 2/Si formation is reaction limited when the energy-deposition density at the interface is low and is diffusion limited when it is high. The results are compared with the phenomenological theory developed by Horino et al. and it is shown that such a dependence of the limiting processes on the energy depositon density is induced when the diffusion is thermally activated while the reaction at the interface is ...

Energy Technology Data Exchange (ETDEWEB)

The liquefaction reaction system of an NEDOL process coal liquefaction 1t/d PSU was opened and checked to investigate the cause of the rise of differential pressure between liquefaction reactors of the PSU. The liquefaction test at a coal concentration of 50 wt% using Tanito Harum coal was conducted, and it was found that the differential pressure between reactors was on the increase. By the two-phase flow pressure loss method, deposition thickness of deposit in pipelines was estimated at 4.4mm at the time of end operation, which agreed with a measuring value obtained from a {gamma} ray. The rise of differential pressure was caused by deposit formation in pipelines connecting reactors. The main component of the deposit is calcite (CaCO3 60-70%) and is the same as the usual one. It is also the same type as the deposit on the reactor wall. Ca in coal ash is concerned with this. To ...

Science.gov (United States)

Ion bombardment during deposition can significantly modify the film properties. In the partially ionized beam deposition, ions derived from the depositing material, i.e., the self-ions, are used during deposition. Cu films were deposited on SiO{sub 2} substrates at room temperature using 1% Cu self-ions with an energy ranging between 0--4 keV. We studied the microstructures of the Cu films using x-ray diffraction and transmission electron microscopy, measured the impurity level inside the films using secondary ion mass spectrometry, and performed the resistivity measurements using a four point probe. The results indicate that there is an optimum ion energy around 2 keV at which, the integrated x-ray intensity ratio {ital I}(111)/{ital I}(200) reaches its maximum value indicating a strong {l angle}111{r angle} texture, while the impurity concentration and resisitivity are minimum. ...

Energy Technology Data Exchange (ETDEWEB)

Cathodic arc deposition is an established and industrially applied technique for the formation of nitrides (e.g. TiN); it can also be used for metal oxide thin film formation. A cathodic arc plasma source with the desired cathode material is operated in an oxygen atmosphere of appropriate pressure, and metal oxides of various stoichiometric composition can be formed on different substrates. We report here on a series of experiments on metal oxide formation by cathodic arc deposition for different applications. Black copper oxide has been deposited on accelerator components to increase the radiative heat transfer between the parts. Various metal oxides such as tungsten oxide, niobium oxide, nickel oxide and vanadium oxide have been deposited on ITO glass to form electrochromic films for window applications. Optical waveguide structures can be formed by refractive index variation using oxide multilayers. ...

Energy Technology Data Exchange (ETDEWEB)

Data which have been collected by Los Alamos National Laboratory waste management for the hydrologic characterization of the subsurface at the low level radioactive waste disposal facility, Area G, are reported and discussed briefly. The data includes Unsaturated Flow Apparatus measurements of the unsaturated conductivity in samples from borehole G-5. Analysis compares these values to the predictions from van Genuchten estimates, and the implications for transport and data matching are discussed, especially at the location of the Vapor Phase Notch (VPN). There, evaporation drives a significant vapor flux and the liquid flux cannot be measured accurately by the UFA device. Data also include hydrologic characterization of samples from borehole G-5, Area G surface soils, Los Alamos (Cerros de Rio) basalt, Tsankawi and Cerro-Toledo layers, the Vapor Phase Notch (VPN), and additional new samples from the uppermost tuff layer at ...

Energy Technology Data Exchange (ETDEWEB)

This paper presents the performance analysis on a hybrid air-conditioning system according to the hybrid building energy system of the green building demonstration project in Shanghai, in which a 150 m{sup 2} solar collector is used to power two 10 kW adsorption chillers, a vapor compression heat pump is used to cool air in the evaporating end while the condensing heating at about 80{sup o}C is fully used to regenerate a liquid desiccant dehumidification system. In the hybrid system, the sensible cooling to the air is treated mainly by solar adsorption cooling and vapor compression cooling, whereas the latent heat is treated by the liquid desiccant dehumidification system with regeneration from the condensing heat of the heat pump. The results show that the performance of this system is 44.5% higher than conventional vapor compression system at a latent load of 30% and this improving can be achieved by 73.8% at a 42% latent ...

Energy Technology Data Exchange (ETDEWEB)

The three-dimensional (3-D), multiphase, computational fluid dynamic (CFD) code FLUENT is used to simulated two-phase flow behaviour in a CANDU header manifold under low (natural circulation) flow conditions. This behaviour was previously inferred from experimental data. The CFD simulations reported here are being used to support these inferences and to obtain a better understanding of phase distribution in the header manifold. The simulations seem to show that the vapor-water mixture models in the FLUENT code do not capture properly phase separation in the header and proper phase branching at the header-feeder connections that have been observed in experiments at low flows. The simulations using discrete-phase model in FLUENT, which tracks the pathlines of the individual vapor bubbles in the water continuum phase, show interesting, complicated and, in some cases, unexpected bubble trajectories from the point of injection of the bubbles at a ...

Energy Technology Data Exchange (ETDEWEB)

A solar energy desalination process utilizing solar radiation directly for the evaporation of salt water is described. Ambient air takes on water vapor as the air passes through an evaporative medium. It is then directed between a saline water-covered, solar absorbing surface and a solar collecting housing. The resulting heated and moisture-saturated air is cooled in a heat exchange means where condensation of fresh water occurs. Simultaneously, cool salt water is utilized as the cooling water in the heat exchange means, and takes on the heat of condensation given up by the condensing vapor. The heated salt water from the heat exchange means is partially directed over the solar absorbing surface, and at least a portion of it is also directed to wet the evaporative medium. Several optional sub-processes are described for operation of the system during periods of reduced insolation, and an alternative process is described for operation of the ...

Energy Technology Data Exchange (ETDEWEB)

This sampling and analysis plan (SAP) identifies characterization objectives pertaining to sample collection, laboratory analytical evaluation, and reporting requirements for vapor samples obtained during the operation of mixer pumps in tank 241-AZ-101. The primary purpose of the mixer pump test (MPT) is to demonstrate that the two 300 horsepower mixer pumps installed in tank 241-AZ-101 can mobilize the settled sludge so that it can be retrieved for treatment and vitrification. Sampling will be performed in accordance with Tank 241-AZ-101 Mixer Pump Test Data Quality Objective (Banning 1999) and Data Quality Objectives for Regulatory Requirements for Hazardous and Radioactive Air Emissions Sampling and Analysis (Mulkey 1999). The sampling will verify if current air emission estimates used in the permit application are correct and provide information for future air permit applications.

Energy Technology Data Exchange (ETDEWEB)

The photocatalyzed degradation of pyridine in the gas phase was investigated using titanium dioxide semiconductor supported on mordenite. The complete mineralization was found to occur over a catalyst containing 75 wt% TiO{sub 2} and 25 wt% mordenite in about 180 min in the presence of saturated water vapor at O{degrees}C (4.6 Torr). Low water vapor pressure of 0.096 Torr was found to be sufficient to achieve a reasonably high percentage and rate of degradation. Diffusion of pyridine within the catalyst adversely affects the activity when the thickness of the catalyst coating exceeds the penetration depth of illumination. The activity of the zeolite-supported catalysts was higher than that of TiO{sub 2}. The photonic efficiency for the complete mineralization of pyridine to CO{sub 2} was determined to be 0.48. 29 refs., 6 refs., 1 tab.

Energy Technology Data Exchange (ETDEWEB)

A flow pattern or flow regime is the characteristics spatial distribution of the phases of fluid in a duct. Since heat transfer and pressure drop are dependent on the characteristic distribution of the phases, it is necessary to describe flow patterns in an appropriate manner so that a hydrodynamic or heat transfer theory applicable to that pattern can be chosen. The objective of the present analysis is to create a flow regime map based on physical modeling of vapor/liquid interaction phenomena in a microgravity environment. In the present work, four basic flow patterns are defined: dispersed flow, stratified flow, slug flow, and annular flow. Fluid properties, liquid and vapor flow rates, and pipe size were chosen as the principal parameters. It is assumed that a transition from one flow pattern to another will occur when there is a change in the dominant force which controls that flow pattern. The forces considered in this modeling are ...

International Nuclear Information System (INIS)

Measurements of the statistical characteristics of channel wall static pressure fluctuations in parallel one-component boiling flow are reported. The measurements span a wide range of local subcooling and vapor volume fraction, and correspond to flow regimes ranging from highly subcooled bubbly to saturated slug-annular. Vapor volume fraction measurements at the pressure measurement station are also reported in conjunction with visual observation of the flow structure. Variation of static pressure fluctuation intensity and spectral content with local thermal-hydraulic condition is demonstrated. Finally, it is suggested that diagnosis of local two-phase flow regime on the basis of (i) statistical characteristics of the pressure data, and (ii) time trace of pressure signal, may be possible. 15 refs.

British Library Electronic Table of Contents (United Kingdom)

This paper explores the through-/in-plane characteristics of water transport in the cathode gas diffusion layer (GDL) of a polymer electrolyte fuel cell (PEFC). Theoretical analysis is performed on the non-isothermal two-phase flow under flow channels. A dimensionless group Da (Damkohler number for PEFC operation), defined as the ratio of water generation rate to water vapor-phase removal rate, is formulated to characterize the flow regimes in a PEFC. This group, lumping geometrical parameters and physical properties, compares the water vapor-phase removal capability (via water diffusion and holding capacity) with the rate of water production by the oxygen reduction reaction. We find that this dimensionless group can be used to characterize the non-isothermal, two-phase phenomena: when Da&...

British Library Electronic Table of Contents (United Kingdom)

Abstract Despite the fact that oxidation is the second most frequent degradation pathway for pharmaceuticals, means of evaluating the oxidative stability of pharmaceutical solids, especially effective stress testing, are still lacking. This paper describes a novel experimental method for peroxide-mediated oxidative stress testing on pharmaceutical solids. The method utilizes urea-hydrogen peroxide, a molecular complex that undergoes solid-state decomposition and releases hydrogen peroxide vapor at elevated temperatures (e.g., 30C), as a source of peroxide. The experimental setting for this method is simple, convenient, and can be operated routinely in most laboratories. The fundamental parameter of the system, that is, hydrogen peroxide vapor pressure, was determined using a modified spect...

Energy Technology Data Exchange (ETDEWEB)

Sputter-deposited tantalum (Ta) and reactively sputter-deposited Ta-nitride films were studied with respect to the passivation capability against copper (Cu) oxidation in thermal O{sub 2} ambient. A 200 {angstrom} Ta or Ta-nitride film was sputter-deposited on a 2,000 {angstrom} Cu film using a Ta target in an Ar/N{sub 2} gas mixture. With Ta passivation, Cu was not oxidized at temperatures up to 400 C, which can be further improved by using passivation of an amorphous Ta-nitride film deposited in an appropriate condition. The absence of long-range defects in the Ta-nitride film was presumably responsible for this improvement. However, sputtering-induced surface damage by excess N{sub 2} in the sputter gas mixture may reduce the passivation capability of Ta-nitride films. When the passivated Cu was oxidized, the Cu oxides always resided in the top surface region. That is, in the oxidation process, Cu ...

Energy Technology Data Exchange (ETDEWEB)

The properties of polycrystalline (Ti, Al)N coatings deposited on non-nitrided, classically plasma-nitrided and low pressure plasma-nitrided AISI H11 steel samples were investigated. The plasma deposition and low pressure plasma nitriding were performed in a Z700-LH magnetron sputter ion plating unit, while a separate unit was used for plasma nitriding of specimens at a pressure of several millibars. The (Ti, Al)N coating was deposited onto all the samples using the same equipment as for the plasma deposition and low pressure plasma nitriding. For the characterization of the composite structures, the following methods were used: scratch test, X-ray diffraction analysis, scanning electron microscopy, scanning tunnelling microscopy and microhardness testing. It was found that plasma nitriding prior to coating deposition strongly affects the growth and properties of hard coatings, such ...

International Nuclear Information System (INIS)

The localized Pt deposition on Si by 30 keV Ga"+ focused ion beam (FIB), 10 keV electron beam (EB) or dual beams (FIB and EB) using precursor gas has been compared by analysis using a 300 keV Be"2"+ microprobe with a beam spot size of 80 nm. The distribution of deposited Pt, Ga from the ion beam itself, and C from the precursor gas was obtained at and nearby the deposited areas by micro-RBS spectra and RBS mapping. All of the beam processed areas showed a uniform Pt distribution at the deposited areas. The amount of Pt atoms increased with the increase in ion or electron dose due to the decomposition of precursor gas. The thickness of Pt layer by EB is considerably less than that by FIB due to the reduced deposition rate. Ga atoms from the center of processed areas partly redeposited at and nearby the FIB processed areas within #approx#3 #mu#m. The Ga incorporation by dual beam ...

International Nuclear Information System (INIS)

Axial offset anomaly (AOA) is caused by the deposition of crud on the fuel cladding of a PWR. When significant levels of crud build up on the cladding, boron can accumulate in the pores of the crud as a concentrated solution or solid phase, and cause the flux depression. Numerous studies have been conducted on the primary water chemistry to reduce the amount of crud in the primary circuit to avoid radioactivity buildup and unexpected power transition in the plant. However, experiments on the crud are restricted in the laboratory because the crud is a highly radioactive material. The objective of this study is to develop a test method for simulating the deposition of crud in a nuclear power plant

Energy Technology Data Exchange (ETDEWEB)

Energy conservation and local energy deposition are investigated in the context of coupled-particle (i.e., neutrons, gamma rays, and charged particles) transport analysis. For charged particles, the concept of group splitting the 1 = 0 transfer matrix to ensure both particle and energy conservation is introduced. Although these procedures are more complex than those found in the usual neutron or coupled-neutron gamma-ray problem, they yield a consistent approach for the calculation of local energy deposition.

British Library Electronic Table of Contents (United Kingdom)

The Rosebel gold district is hosted in a Paleoproterozoic greenstone belt of the Guiana Shield and has many characteristics that enable classification of the ores as an orogenic gold deposit. Host rocks have undergone several phases of deformation. However, gold deposition occurred late in the structural history of the belt, and is considered part of a late regional metallogenic event with respect to the geotectonic evolution of the Guiana Shield. Economic gold mineralization is hosted in felsic to mafic volcanic rocks and two sedimentary successions that are differentiated into turbiditic and arenitic depositional packages. The detailed lithostratigraphic characterization and the geochemistry enable the correlation of the local rock types with the Paramaka, the Armina, and the Rosebel for...

Energy Technology Data Exchange (ETDEWEB)

In this study, liquid flame spray (LFS) was used to produce titania, silver and silver-titania deposits of nanoparticles. Titanium(IV)ethoxide (TEOT) and silver nitrate in ethanol solutions were used as precursors and sprayed into turbulent hydrogen-oxygen flame. Production rates of 1.5-40 mg/min of titania were used with silver additions of 1, 2, 4, and 8 wt% compared to titania. Nanoparticle deposits were collected by thermophoretic sampling at six different axial distances from the flame torch head: 3, 5, 10, 12, 15, and 20 cm, of which the all but the last one occurred inside the flame. The deposit samples were analysed by TEM and SAED analysis. The powder samples of the particles were also collected by electric precipitator to XPS and specific surface area analysis. Particle size and effective density after the flame in the aerosol were analysed with SMPS and ELPI. The results from the previous studies i.e. controlling ...

International Nuclear Information System (INIS)

Sep 1970. 85 p. United States Green, SJ LeTourneau, BW Peterson, AC Bettis

Science.gov (United States)

The workshop topics consist of FERS, FEGLI, FEHBP, Disability, Deposit/Redeposit ; TSP, Annual/Sick Leave, Annuity Calculation, Best Date to Retire, COLA's, ...

Energy Technology Data Exchange (ETDEWEB)

The goal of this research program is to determine whether pulsed laser deposition is an effective alternative method for growing TiCN thin films. Pulsed laser deposition (PLD) is chosen because of its well-documented capability for growing uniform, stoichiometric films in ultra-high vacuum or gaseous environments. Processing of thin films by PLD is also achieved at relatively low temperatures compared with CVD processing. Given these attributes, the primary objectives in this article are to determine whether nitrogen may be readily incorporated into films resulting from the laser-ablation of TiC in an N{sub 2} environment, determine what effect nitrogen has on mechanical properties, and determine whether nitrogen incorporation is strongly influenced by processes unrelated to laser deposition (e.g., thermally-activated surface reactions).

UK PubMed Central (United Kingdom)

Obesity is characterized by the abnormal or excessive deposition of fat in the adipose tissue. Its consequences go far beyond adverse metabolic effects on health, causing an increase in oxidative stress,...Full Text Available

International Nuclear Information System (INIS)

Spanish 2001 p. 10-18 Uruguay Ubilla, M. Lorenzo, N. Depto. de

Energy Technology Data Exchange (ETDEWEB)

Cold spray was employed as a novel low temperature approach to deposit titanium dioxide (TiO{sub 2}) photocatalytic film. The film microstructure was characterized using X-ray diffraction and scanning electron microscopy. The photocatalytic performance was examined through acetaldehyde degradation under ultraviolet illumination. Results showed that TiO{sub 2} film was successfully deposited on substrate surface through cold spray. The film thickness reached up to 15 {mu}m. The film presented a rough surface and porous structure. Owing to the low temperature of spray powder, no phase and particle size changes occurred to TiO{sub 2} during deposition. It was found that the cold-sprayed TiO{sub 2} film was active for photodegradation of acetaldehyde.

British Library Electronic Table of Contents (United Kingdom)

A procedure based on electrophoretic deposition (EPD) was developed to coat metal plates with powder catalysts. The method was tested on stainless-steel plates with three Ni-based catalysts for the steam reforming of ethanol. The catalysts (Ni/La2O3/g-Al2O3) contained 15% Ni and 8% La, and were prepared using three types of g-alumina with different textural properties. The powder catalysts were suspended in isopropanol, and EPD deposition was performed with a voltage of 100V and a distance between electrodes of 2cm. Deposition time was varied between 3 and 7min, which gave a thickness of the catalyst layer from around 30 to 100mm. The morphology of the catalyst layer was dependent on the textural characteristics of the g-Al2O3 used to prepare the catalyst. The activity of the catalyst plat...

Energy Technology Data Exchange (ETDEWEB)

Corrosion behavior of deposition coated specimens prepared by the technique proposed by the authors is investigated in salt immersion tests, and also those of pure magnesium, 3N, 4N and 6N grades, and magnesium alloys, AZ31 and AZ91E, are investigated for comparison. Inhomogeneous corrosion occurs in AZ31 and AZ91E alloys when buffered solutions with pH values of 6.5 and 9.0 including 1% NaCl and a conventional 3% NaCl solution are used for immersion tests, while 6N-Mg shows homogeneous corrosion in such solutions. Corrosion behavior of the deposition coated specimen resembles that of 6N-Mg. Purification process included in the deposition coating technique provides homogeneity in microstructural and electrochemical terms, which results in improving corrosion resistance. (orig.)

UK PubMed Central (United Kingdom)

Dosimetry parameters such as deposition, clearance, retention, and translocation and dissolution of inhaled particles in and to different lung compartments may be important for the persistence of particles...Full Text Available

Science.gov (United States)

Dec 20, 2007 ... Process 5b Federal Employee Retirement System (FERS) Deposits and ..... CSRS, CSRS Offset, or FERS ..... Advanced Sick Leave and ...

Energy Technology Data Exchange (ETDEWEB)

The method is related to hydrodynamic methods for studying wells and may be used in the prospecting and mapping of gas and gas condensate deposits and formations. The method consits of drilling exploratory wells and measurement of the physical parameters of the stratum liquid. The piezometric levels are periodically determined simultaneously in all the observation wells during a change in the atmospheric pressure, and the presence of a remoteness of the gas deposit from the well is judged from the size of the increments in the piezometric levels intime. The determinations of the piezometric levels in the wells are conducted during an abrupt change in atmospheric pressure, for instance, during the replacement of a cyclone by an anticyclone or the reverse. The atmospheric pressure is measured by a barograph, while the piezometric levels are measured by high precision level meters or pressure gauges of low pressure. The method increases the ...

Energy Technology Data Exchange (ETDEWEB)

This report discusses environmental surveillance activities conducted on the Nevada Test Site during the first calendar quarter of 1996. Surveillance activities included collection and analysis of air, noble gas, tritiated water vapor, and other water samples. Samples were analyzed for both radiological and non-radiological effluents.

CERN Document Server

It is shown that the interpretation of the experimental results reported in the publication "Storage of Light in Atomic Vapor" by D.F.Phillips et al., Phys. Rev.Lett. 86, 783 (2001) [quant-ph/0012138] is incorrect. The experimental observation of this paper can be consistently explained in the framework of standard concepts of the physics of optical pumping and has nothing to do with "storage of light", or "dynamic reduction of the group velocity", or "light pulse compression".

Energy Technology Data Exchange (ETDEWEB)

The performance of a commercial heat pipe was investigated both experimentally and theoretically. The effect of the temperature difference, the surface area ratio, and the operational conditions on the performance were studied. The heat flow rate and the vapor temperature were estimated on a ready-made commercial heat pipe. Its performance varied considerably with operational conditions. Theoretical consideration of a mathematical model and several nomographs are also presented. This work is applicable to the design and use of heat pipes in the field.

Energy Technology Data Exchange (ETDEWEB)

Results of calculation of steady thermal-hydraulic characteristics of PVG-440 horizontal steam generator are presented. Steam flows in selected sections are compared to data provided by OKB Gidropress Calculated vapor void fractions are compared to measured ones. (orig.) (3 refs., 3 figs., 8 tabs.).

Energy Technology Data Exchange (ETDEWEB)

We report on measurements of the mixing of fuel oil with air at atmospheric pressure in an industrial premixed gas turbine burner. The concentration of the vaporized fuel oil was measured with laser induced fluorescence. We reason that the fuel oil concentration can be considered with good accuracy as proportional to the fluorescence intensity. (author) 6 fig., 3 refs.

Energy Technology Data Exchange (ETDEWEB)

Means for increasing heat transfer characteristics between the surface of a solid and a boiling liquid are described in which the solid is immersed is comprised of a solid with passages which extend therethrough to the surface for the circulation of liquid through the passages for emergence from the surface to eliminate at least a portion of the unstable vapor film otherwise formed on the surface.

International Nuclear Information System (INIS)

The structure of a fragment of the germanium complex compound (GCC) with oxyethylidenediphosphonic acid and the adsorption properties of GCC films with respect to the vapors of water and some other organic liquids have been studied. The electric conductivity of GCC films has been investigated, and its mechanism has been explained.

Energy Technology Data Exchange (ETDEWEB)

PNNL, with cofunding from the Bonneville Power Administration (BPA) and Building Technologies Program, conducted a research and development activity targeted at addressing the energy efficiency goals targeted in the BPA roadmap. PNNL investigated an integrated heating, ventilation and air conditioning (HVAC) system option referred to as the low-lift cooling system that potentially offers an increase in HVAC energy performance relative to ASHRAE Standard 90.1-2004.

Energy Technology Data Exchange (ETDEWEB)

Advances made in understanding the chemistry and dynamics of the atmosphere in the approximate altitude range of 50 to 90 km are addressed. Attention is given to mesospheric structure and seasonal variations, gravity waves and gravity wave saturation, the effects of gravity waves on thermal, momentum and constituent fluxes, and the effect of gravity waves on airglow emissions. A review of research on tides and planetary waves and their effects on the mesosphere are presented as well as discussions on ozone hydroxyl, water vapor, and noctilucent cloud research. 217 refs.

Energy Technology Data Exchange (ETDEWEB)

An examination is made of the structure of the North Saremboyskiy oil field and productive lower Devonian deposits of well 15. Based on detailed lithological studies, as well as investigation of filtering-capacitance properties of rocks, the complex structure of the carbonate deposits and the dominant development of complex type collectors is indicated.