Energy Technology Data Exchange (ETDEWEB)

Supermetal with critical characteristics is under advanced investigation for further improvement of metal materials. Although iron is most frequently used as structural material among various metals, it should be used more carefully and effectively because of resource limitation and global environmental problem. It is essential to draw various excellent properties much more from iron and to improve recyclability. In particular, the best way to meet these requirements is achievement of more fine structure and higher purity. Since the lowest crystalline grain size is now limited to nearly 10{mu}m, metallic structure composed of grains below 1{mu}m is expected by mesoscopic control. Various methods have been studied to achieve ultra-fine crystalline structure, and study of precise heat treatment control and ultra-strength metallurgy is required. Heat treatment in magnetic field and layered structure by mechanical alloying are ...

Energy Technology Data Exchange (ETDEWEB)

Experimental discussions were given on effect of V and W addition on the high temperature strength properties of 12% Cr-15% Mn austenite steels. The test samples were added with W at 0% to 3.5% and V at 0% to 0.5% in addition to C and N, and were given aging treatment or solution treatment. This paper describes the following matters on the results of high-temperature strength measurements and structural observation: A remarkable trend was observed that M23 Cb type carbides precipitate in the aging treatment, wherein aging hardening appears prominently which is attributable to ultra-fine deposits of vanadium nitride (VN) in the V-added material; the V addition is very effective in increasing the high-temperature tensile strength and creep fracture strength as compared with single W addition, wherein the said carbides that accelerate the precipitation as a result of the V addition make a large contribution, in addition to that by ...

Energy Technology Data Exchange (ETDEWEB)

The present paper describes the development of ultra-fine grains on the surface of AZ31 alloys caused by hydrogenation and dehydrogenation treatment, so-called HDDR process. Upon hydrogenation process, disproportionation reaction occurred in forming of MgH{sub 2}, Mg{sub 0.42}Al{sub 0.58}, and Al phases. In the following desorption process, the three phases were re-solved into the AZ31 alloy. As a result of the HDDR phenomena, the grain size of AZ31 alloy powders was reduced down to about 100 nm after the heat treatment at 350 C under a hydrogen pressure of 7 MPa for 24 h. The grain size tended to be increased with increasing process temperatures. In addition, the HDDR process was also applied to AZ31 alloy plates. By the HDDR process at 450 C, the grain size was reduced to less than 500 nm, where hydrogenated layer thickness was limited to be in the range of about 20 {mu}m from the ...

International Nuclear Information System (INIS)

Critical experiments have been analyzed to verify a nuclear analysis system for fast reactors used in Japan Nuclear Cycle Development Institute (JNC). The experiments were performed in a collaboration work between JNC and the Institute of Physics and Power Engineering of Russia to dispose Russian surplus weapons plutonium, focusing on the effect of the introduction of uranium-plutonium mixed-dioxide (MOX) fuel and stainless steel reflector into the current BN-600 core that is comprised of UO_2 fuel and blanket. The analysis results agreed well with measured values on most of the nuclear characteristics. The accuracies are comparable to those obtained for the conventional MOX fueled fast reactors. It suggests that the JNC analysis system can analyze accurately nuclear characteristics in uranium fueled cores as well. A significant improvement was achieved on the sodium void reactivity by employing an ultra fine group cell ...

International Nuclear Information System (INIS)

A-15 compounds are extremely brittle and difficult to process for practical applications. A novel processing technique was developed to greatly improve the mechanical and superconducting properties of A-15 alloys. The new processing technique can be described as follows: (1) to select compounds that can form the A-15 phase (the selected A-15 compounds in this research were Ti3Nb6Mo3Si4 and Nb99.5-(x + y)AlxSiyB0.5 alloys); (2) to rapidly solidify them into the amorphous state; (3) to anneal the quenched amorphous products into ultra fine-grained single A-15 phase. The extreme grain refinement greatly improved the flexibility and the critical current density of the alloys. The melt spinning technique was used to rapidly solidify Ti3Nb6Mo3Si4 and Nb99.5-(x + y)AlxSiyB0.5 alloys. Ti3Nb6Mo3Si4 alloys were relatively easily formed into the amorphous state. Nb3Al alloys required the addition of glass forming elements Si and B. It ...

British Library Electronic Table of Contents (United Kingdom)

Ultrafine grained steels with different carbon contents were produced through warm caliber rolling and evaluated for their stress-strain behavior along with the reduction in area. It was found that the reduction in area-tensile strength balance is far better than the conventional ferrite+pearlite steels and even superior to bainitic steels for all materials tested in the present study.

Energy Technology Data Exchange (ETDEWEB)

It is known that in size reduction of the granular structure of ferrite and ferrite-pearlite steels the temperature of the transformation from ductile to brittle condition is lowered. This effect can also be caused by an increase in the dispersity of intragrain and intergrain segregations (sulfides, carbonitrides, and segregations of impurity atoms), which accompanies grain size reduction and promotes initiation and propagation of cracks. In order to clarify the mechanism of fracture of steel in the region of the ductile-brittle transition steel 45 with different grain sizes and pearlite morphologies has been investigated.

International Nuclear Information System (INIS)

Effect of scale on determination of 12Kh18N10T steel tendency to intergranular corrosion (IGC) by rapid electrochemical techniques in solution of 10 % H_2SO_4+0.0025 g/l KCNS was investigated. It is shown that scale presence of steel surface accelerates anode dissolving, activates grain boundaries. All this results to the effect of tendency to IGC in steels, not inclined to it. The scale is not completely removed from the surface, but remains partially along grain boundaries in result of successive pickling of scale and then a surface layer of metal. This also couses the effect of tendency to IGC.

British Library Electronic Table of Contents (United Kingdom)

A ferritic steel with finely dispersed precipitates was investigated to reveal the fundamental strengthening mechanisms. The steel has a yield strength of 760MPa, approximately three times higher than that of conventional Ti-bearing high strength hot-rolled sheet steels, and its ultimate tensile strength reaches 850MPa with an elongation-to-failure value of 18%. Using energy dispersive X-ray spectroscopy (EDXS) and transmission electron microscope (TEM), fine carbides TiC with an average diameter of 10nm were observed in the ferrite matrix of the 0.08%Ti steel, and some cubic M23C6 precipitates were also observed at the grain boundaries and the interior of the grains. The finely dispersed TiC precipitates in the matrix provide matrix strengthening. The estimated magnitude of precipitation ...

Energy Technology Data Exchange (ETDEWEB)

The global production of steel is predicted to increase rapidly to meet future demands. In order to conserve the natural resources, certain measures must be taken. These include perfecting the recycling of steel, improving the performance to extend the life of the material, and reduce the need for massive production of steel by increasing the strength of the material. This paper presented a design concept for ultrafine complex microstructure steel. The National Research Institute for Metals in Japan has worked on a project which investigated 800 MPa ferrite steel for welded structures with a chemical composition similar to 400 MPa-class plain carbon steel. The doubled strength was attributed to grain refinement. Novel welding techniques were also used for joining the ultrafine microstructure. In this study, low carbon Si-Mn ferrite-pearlite ...

Energy Technology Data Exchange (ETDEWEB)

Isothermal transformation kinetics of austenite to acicular ferrite and allotriomorphic ferrite were measured in reheated low alloy steel weld deposits with similar weld compositions and austenite grain size but different inclusion characteristics. Accelerated kinetics of transformation to acicular ferrite were observed in weld metal containing coarser and titanium-rich inclusions. In contrast, kinetics of transformation to allotriomorphic ferrite were not influenced by inclusion characteristics, but, rather, by the austenite grain size and carbon concentration.

Energy Technology Data Exchange (ETDEWEB)

Microstructural analyses by advanced metallographic techniques were conducted on mockup welds and a cracked BWR core shroud weld fabricated from Type 304L stainless steel. heat-affected zones of the shroud weld and mockup shielded-metal-arc welds were free of grain-boundary carbide, martensite, delta ferrite, or Cr depletion near grain boundaries. However, as a result of exposure to welding fumes, the heat-affected zones of the welds were significantly contaminated by fluorine and oxygen which migrate to grain boundaries. Significant oxygen contamination promotes fluorine contamination and suppresses classical thermal sensitization, even in Type 304 steels. Results of slow-strain-rate tensile tests indicate that fluorine exacerbates the susceptibility of irradiated steels to intergranular stress corrosion cracking. These observations, combined with previous ...

British Library Electronic Table of Contents (United Kingdom)

An ultrafine-grained ferrite/cementite (UGF/C) steel with a local high density of cementite particles was fabricated through caliber-warm-rolling followed by annealing and resulted in a bimodal-sized microstructure. The characteristic bimodal-sized microstructure was attributed to the original ferrite-pearlite structure and cementite spacing, and reflected the original ferrite-pearlite structure. The smaller-sized clusters corresponded to the former pearlite regions and the larger-sized clusters to the proeutectoid ferrite regions. The cementite particles naturally localized within the former pearlite region. Most of the ferrite coarsening did not occur until the cementite particle spacing reached a critical value. The UGF/C microstructure with a bimodal grain size showed a yield strength ...

Energy Technology Data Exchange (ETDEWEB)

In this paper, the state-of-the-art ultrasonic and magnetic measuring techniques developed at Kawasaki Steel and used in the production process of steel sheets are described. Representative examples shown here are as follows: (1) Magnetic flux leakage testing system for the detection of nonmetallic inclusions, (2) Nondestructive orientation measurement for secondary re-crystallized grains in grain-oriented electrical steel by ultrasonic interferometry, (3) Immersion testing method for the detection of nonmetallic inclusions, (4) Surface wave probe for the detection of surface flaws in rolls used in rolling mills. Developments of these techniques and their applications to actual steel sheets production processes have contributed to advance in technologies for quality assurance and control. With the help of these techniques, steel sheet ...

British Library Electronic Table of Contents (United Kingdom)

Background, aim, and scope Semi-trailers with load boxes are the most important mode of grain transport by land in the world. Load boxes can be produced with different materials such as: wood, steel, and synthetic material. They are responsible for effectiveness retention and quality of grains during the transport. Among the main aspects to be considered and valued when selecting materials for load boxes are the final mass of the semi-trailer, loss of grains, and mechanical properties. Environmental performance is another important aspect to be taken into account for developing and selecting new materials in this kind of application. This study presents a comparative environmental evaluation of load boxes built from two different materials (a wood panel and a three-layer synthetic (TLS) pa...

Energy Technology Data Exchange (ETDEWEB)

Increased nitrogen levels have been correlated with decreased ductility and elevated ductile-to-brittle transition temperature in pressure vessel steels [1]. However, the exact role played by nitrogen in the embrittlement of steels remains unclear. Miller and Burke have reported atom probe ion microscopy findings from neutron-irradiated low-alloy pressure vessel steel showing the presence of a 1 to 2 ruonolayer thick film of Mo, N, and C at prior austenitic grain boundaries (GB's) [2], suggesting a role for nitrogen as an intergranular embrittler. It is of interest for the development of mitigation strategies whether nitrogen must combine with other impurities to form nitride precipitates in order to exert an embrittling effect. Briant et al [1] have associated the embrittling effect of N in steels exclusively with intergranular nitride formation. This association suggests ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical metal dissolution of 100Cr6 steel in sodium chloride solution, applying high electrolyte flow rates and high current densities, has been studied with a view to the influence of material heterogeneities such as carbide segregation lines in the steel matrix. It was shown that the presence of such segregations is responsible for the formation of troughs on the specimen surface during electrochemical dissolution. A mechanism for trough formation was proposed. A dedicated heat treatment applied to the 100Cr6 steel eliminated the carbide segregation lines and established a soft annealed, fine-grained microstructure containing globular carbides. Subsequent electrochemical dissolution did not show any development of surface irregularities as troughs. (orig.)

International Nuclear Information System (INIS)

The effect of W and V on the high temperature strength properties of 12%Cr-15%Mn austenitic steels was studied from the view point of precipitation hardening and internal stress. The contribution of W addition to the tensile and creep-rupture strength was not so large. By contrast the combined addition of W and V increased the strength considerably. These are resulted from the precipitation of fine vanadium nitride (VN) within grains and the enhancement of M_2_3C_6 type carbide precipitation at grain boundaries. The V added material had large internal stress value which is considered to be due to dislocation movement disturbed by fine vanadium nitrides. (author).

Energy Technology Data Exchange (ETDEWEB)

Alloy 800 is an austenitic Fe-Ni-Cr steel containing relatively minor but important amounts of carbon, aluminium and titanium. Special grades of alloy 800 known as 800H, 800HT and 800LC differ in the concentrations of these elements. In addition to these industrial specifications, further melts were prepared containing phosphorous or sulphur. Using a radioactive tracer method the bulk and grain-boundary diffusion of {sup 59}Fe was investigated in these alloys in the temperature range 800 to 1000 C. For evaluation of the diffusion profiles the approximation of Suzuoka was used, which considers the depletion of the tracer on the surface. By autoradiography it was confirmed that such depletion occurs. In alloy 800H the activation energy of grain-boundary diffusion of {sup 59}Fe was found to be (209{+-}17) kJ/mol; dissolved elements, especially phosphorous, increase the activation energy. The same materials - aged at 800 C for ...

Energy Technology Data Exchange (ETDEWEB)

By magnetron sputtering model steel films with specific properties can be prepared for purposive surveys. By changing the deposition parameters certain properties of these films can be influenced. For this thesis steel films with 18% Cr and 8% Ni have been prepared in order to study specific parameters on the corrosion resistance of bulk stainless steel. Chemical composition, microstructure, and surface morphology of these films have been characterized. In comparison to bulk steel sheets with the same chemical composition they have a smaller grain size and a ferritic structure. In contrast to bulk steel sheets they don`t contain any nonmetallic inclusions like Mn-sulfides. The influence of these structural differences on the corrosion resistance has been studied. For this purpose the electrochemical properties of the sputter-deposited steels ...

International Nuclear Information System (INIS)

In this study, dissimilar welds between HP heat-resistant steel and Incoloy 800 were made with four different filler materials including: 309 stainless steel and nickel-based Inconel 82, 182 and 617. The microstructure of the base metals, weld metals and their interfaces were characterized by utilizing optical and scanning electron microscopy. Grain boundaries migration in the weld metals was studied. It was found that the migration of grain boundaries in the Inconel 82 weld metal was very extensive. Precipitates of TiC and M_2_3C_6 (M = Cr and Mo) in the Inconel 617 weld metal are identified. The necessary conditions for the formation of cracks close to the fusion line of the 309-HP joints are described. Furthermore unmixed zone near the fusion line between HP steel base metal and Inconel 82 weld metal is discussed. An epitaxial growth is characterized at the fusion line of the ...

International Nuclear Information System (INIS)

This study aims to evaluate fatigue strength properties at long-term high temperature of 316FR steels developed for structural materials applied to high temperature components in the 21st Century such as Demonstration FBR, and to obtain design indicators on high temperature strength properties arranged on chemical composition and grain size on a base of 316FR stainless steels. As results obtained by the study, it could be found that as a result of systematic examinations on temperatures and strain rate dependence on symmetric triangular strain waveform of 316FR steels between 500 to 600degC, temperature of fatigue life, and strain rate dependence can be integrally evaluated by a parameter analysis method developed by authors and life prediction at ultra low strain rate of less than 10"-"6/s and its experimental verification could be carried out. And, it was also found that as a result of evaluation of ...

International Nuclear Information System (INIS)

Localized deformation may play a key role in the underlying mechanism of irradiation assisted stress corrosion cracking (IASCC) in light water reactor core components. In this study, four austenitic alloys, 18Cr8Ni, 15Cr12Ni, 13Cr15Ni and 21Cr32Ni, with different stacking fault energies were irradiated to 1 and 5 dpa at 360 deg. C using 3.2 MeV protons. Interrupted constant extension rate tensile (CERT) tests were conducted in a simulated BWR environment to determine IASCC susceptibility. In order to characterize the localized deformation in slip channels and grain boundaries, parallel CERT experiments were also performed in an argon atmosphere. Results show that the IASCC susceptibility of the tested alloys increases with increasing irradiation dose and decreasing stacking fault energy. IASCC tends to initiate at locations where slip channels intersect grain boundaries. Localized deformation in the form of grain boundary ...

International Nuclear Information System (INIS)

By using a plasma nitriding procedure at the PUPR Mirror Cusp Plasma machine, surface hardness is increased in 302/304-type stainless steel samples by exposing them to high-ion-density plasma at high vacuum. This method successfully dopes the surface of the material with strengthening nitrogen ions, without the use of chemical procedures that sacrifice the resistance to corrosion of the given material. A 500 V negative bias is placed on the sample exposed to the nitrogen plasma, where high-energy ions are therefore attracted and immersed into the metallic matrix microns into the surface of the stainless steel. This potential maintains a constant surface temperature at approximately 800 deg. C. The plasma parameters including ion density and plasma temperature were diagnosed using single Langmuir probes. The stainless steel samples were then tested using scanning electron microscopy (SEM), and Vickers micro-hardness testing ...

Energy Technology Data Exchange (ETDEWEB)

The influence of high C martensite on the strength and impact behavior of C-Mn-Nb-Al steels has been determined for two distributions: films surrounding the ferrite grains and distinct colonies. In the former case, the impact behavior markedly deteriorated, this deterioration increasing with martensite level. The changes in impact behavior could be explained by regarding the films of martensite as being similar to the brittle grain boundary carbides that are present in ferrite-pearlite steels. These films readily crack, yet are always thick enough to produce a sufficient wide crack to render crack propagation easy. The critical event in fracture then becomes the ability to propagate the cracks through the grain boundaries. The greater the grain boundary coverage by these films, the easier this becomes and the worse is the impact behavior. When the martensite is ...

Energy Technology Data Exchange (ETDEWEB)

Time-temperature-precipitation diagrams have been established for two steels with 6% Mo, 21% Cr, 25% Ni, 0.14 and 0.19% N (Cronifer 1925 h Mo = 1.4529, UNS N 08925) and for one steel with 6% Mo, 20% Cr, 18% Ni and 0.21% N (UNS S 31 254). The corresponding time-temperature-sensitization diagrams (in accordance to SEP 1877/II) and time-temperature-pitting diagrams (testing in 6% FeCl{sub 3} solution) have been evaluated as well. Precipitation of intermetallics occurs rapidly especially in the range between 700 and 1000{sup 0}C. In case of the 18% Ni steel and the 25% Ni/0.14% N steel grain boundaries are covered to a large extent with precipitates after only 15 min at 850 or 950{sup 0}C. In case of the 25% Ni/0.19% N steel precipitation is considerably slower. Therefore, when welding according to established rules and recommendations, no deterioration of the ...

British Library Electronic Table of Contents (United Kingdom)

Ultra-fine ZnAl2O4 spinel hydrogel precursor synthesized from mixed salt solutions of Zn^2^+ and Al^3^+ ions using ammonium hydroxide-hexamethylenetetramine as basic media for co-precipitation was used as bonding material and sintering aid for pure alumina system. The hydrogel powder exhibited some well-defined ZnAl2O4 spinel phases at 800^oC. Alumina compacts were fabricated by incorporating small proportions of the precursor in alumina powder and firing at different temperatures (1350-1500^oC). The degree of densification was studied by measurement of fired shrinkage, apparent porosity, bulk density and cold crushing strength. Phase compositions and microstructural features of sintered samples were evaluated by XRD and SEM respectively. Addition of 0.2% hydrogel powder to alumina exhibit...

International Nuclear Information System (INIS)

As an unconventional surface alloying process, ion implantation has been utilized to improve the active-passive behavior and the pitting resistance of martensitic M50 engineering alloy. In a field simulation study, Cr-implantation only at 150 kev to a fluence of 2 x 10"1"7 ions/cm"2 prevented pitting. The best pitting resistance of the steel was obtained with multiple implantations of Cr and Mo. The intermixing effect of high fluence P-implantation into 304 stainless produced an amorphous surface alloy. The removal of the grain boundaries and the uniformity of the resulting structure had a great influence on corrosion properties. REED analysis indicated that the anodic passive films formed on P-implanted 304 stainless steel at 250 mV (SCE) in 0.5M H_2SO_4 was amorphous. Phosphorus and boron were implanted into 316 stainless steel to study the passivity of 316 stainless. Electrochemical experiments were ...

Energy Technology Data Exchange (ETDEWEB)

Studies conducted at the Pacific Northwest National Laboratory (PNNL) in Richland, Washington have focused on developing and evaluating the reliability of nondestructive testing (NDT) approaches for coarse-grained stainless steel reactor components. The objective of this work is to provide information to the United States Nuclear Regulatory Commission (NRC) on the utility, effectiveness and limitation of NDT techniques as related to inservice testing of primary system piping components in pressurized water reactors. We examined cast stainless steel pipe specimens containing thermal and mechanical fatigue cracks located close to the weld roots and having inner and outer diameter surface geometrical conditions that simulate several water reactor primary piping configurations. In addition, segments of vintage centrifugally cast piping were examined to characterize the inherent acoustic noise and scattering caused by ...

Energy Technology Data Exchange (ETDEWEB)

A series of stainless austenitic and ferritic materials was exposed for 100 days to boiling nitric acid which contained no corrosion products; the corrosion rates and depths of the grain boundary attack were observed. - Provided the structure is precipitation-free, the following are suitable for long-term exposure; the austenitic steels X 2 CrNi 19 11, X 1 CrNi 25 21, X 1 CrNiMoN 25 22 2 and X 1 NiCrMoCu 31 27 4, the practically Mo-free and Cu-free development steel X 1 NiCr 31 27, and the highly Mo-alloyed variant X 1 NiCrMoCu 31 27 5. - In the case of alloy NiCr21Mo it is advisable to limit the concentration and/or temperature of the nitric acid. - The 'superferrite' X 1 CrNiMoNb 28 4 2, the Japanese steel X 1 CrNiNb 30 2 and the austenitic steels X 2 CrNiMoN 17 13 3 and X 1 CrNiMoN 25 22 2 in the version with high nickel content are unsuitable. The decisive ...

International Nuclear Information System (INIS)

Constant pull rate tests were conducted on tensile specimens of Inconel Alloy 600, Incoloy Alloy 800, and Type 304 stainless steel in deaerated 10% NaOH solution at 288 C (550 F) with a cover gas of 5% H_2 in N_2. The pull rate used for most experiments was 3.3 x 10"-"6 cm/s, which corresponds to an initial strain rate of 3 x 10"-"6 s"-"1. The electrical potential of the specimens was controlled by a potentiostat using a nickel wire as a hydrogen reference electrode. Under open circuit conditions, Type 304 stainless steel specimens cracked rapidly, but Alloys 600 and 800 specimens exhibited only ductile fracture. However, cracks readily formed in Alloy 800 specimens at potentials in the +50 to +300 mV range and in Alloy 600 specimens at potentials in the +150 to +250 mV range. Scanning electron microscope (SEM) photographs of some of the cracked specimen surfaces showed the transition from ductile to brittle fracture as a consequence of changes ...

Energy Technology Data Exchange (ETDEWEB)

Exhaust fine and ultra fine particle numbers, particle sizes, mass, shape, structure and density were studied from Euro II - EEV emission level heavy-duty vehicles. For total particle emission factors city buses were run on dynamic conditions simulating city bus driving. The new heavy-duty chassis dynamometer of VTT was used. Vehicles were a comprehensive sample of current city bus fleet, the type approved emission level of which was Euro II - Euro III. Also cleaner engines of Euro IV to EEV targeted emission level were included: CRT, CNG, DPF. Particle emissions of these buses were extremely low; numbers 1/100 - 1/1000 and masses 1/10 - 1/100 of those of the predominating techniques. Morphological properties of fine particle populations that represent majority of particle size distribution (Da < 500 nm) are being analyzed by image processing (Matlab) from electron microscopical images (SEM, ESEM and TEM) as a function of particle size. ...

Energy Technology Data Exchange (ETDEWEB)

Irradiation-assisted stress corrosion cracking (IASCC) of several types of BWR field components fabricated from solution-annealed austenitic stainless steels (SSs), including a core internal weld, were investigated by means of slow-strain-rate test (SSRT), scanning electron microscopy (SEM), Auger electron spectroscopy (AES), and field-emission-gun advanced analytical electron microscopy (FEG-AAEM). Based on the results of the tests and analyses, separate effects of neutron fluence, tensile properties, alloying elements and major impurities identified in the American Society for Testing and Materials (ASTM) specifications, minor impurities, water chemistry, and fabrication-related variables were determined. The results indicate strongly that minor impurities not specified by the ASTM-specifications play important roles, probably through a complex synergism with grain-boundary Cr depletion. These impurities, typically associated with steelmaking ...

CERN Document Server

Structural steels with improved atmospheric corrosion resistance

International Science & Technology Center (ISTC)

Investigation of Destruction Mechanisms in Reactor Steels and Alloys under Cycling Deformation

Science.gov (United States)

Not Available

British Library Electronic Table of Contents (United Kingdom)

In this research, the interactive effect of grain and specimen sizes on the flow stress of sheet metal in microforming is investigated via the tensile test of pure copper and numerical modeling. Models based on different assumptions are proposed to analyze the size effect phenomenon. It is found that the flow stress decreases linearly with the decrease of the ratio of specimen to grain sizes. The grain boundary thickness decreases and its volume fraction increases with the decrease of grain size. The variation of grain boundary thickness is not proportional to the variation of grain size. Furthermore, the fraction of grain boundary increases with the strain and the ratio of specimen to grain sizes. Based on the FE simulation, it is found that the simulated flow stress, which is modeled bas...

Energy Technology Data Exchange (ETDEWEB)

The effect of WC particle size with the addition of VC as a grain growth inhibitor was investigated during the liquid phase sintering of WC-Co system. With increasing WC particle size at the same VC content, the effect of grain growth inhibition was increased. Also, with increasing the VC content, the grain shape of WC was changed from the faceted shape to the distorted shape, and the step density of the WC grain was increased. (orig.)

Energy Technology Data Exchange (ETDEWEB)

To simulate radiation damage under a future Spallation Neutron Source (SNS) environment, irradiation experiments were conducted on a candidate 9Cr-2WVTa ferritic/martensitic steel using the Triple Ion Facility (TIF) at ORNL. Irradiation was conducted in single, dual, and triple ion beam modes using 3.5 MeV Fe{sup ++}, 360 keV He{sup +}, and 180 keV H{sup +} at 80, 200, and 350{degrees}C. These irradiations produced various defects comprising black dots, dislocation loops, line dislocations, and gas bubbles, which led to hardening. The largest increase in hardness, over 63 %, was observed after 50 dpa for triple beam irradiation conditions, revealing that both He and H are augmenting the hardening. Hardness increased less than 30 % after 30 dpa at 200{degrees}C by triple beams, compatible with neutron irradiation data from previous work which showed about a 30 % increase in yield strength after 27.2 dpa at 365{degrees}C. However, the very large concentrations of gas ...

International Nuclear Information System (INIS)

Type 304 stainless steel (SS) specimens sensitised at 873 K and 973 K for 1, 10 and 100 hours respectively were ion implanted using a 150 keV accelerator at an energy of 70 keV in two different doses of nitrogen namely 1 x 10"1"6 to 1 x 10"1"7 ions/cm"2. Ion implantation at 1 x 10"1"6 ions/cm"2 did not show any improvement in pitting resistance, however, the specimens implanted at 1 x 10"1"7 ions/cm"2 showed significant increase in pitting corrosion resistance when potentiodynamic anodic polarisation studies were carried out in acidic chloride medium. For specimens aged at 873 K, nitrogen ion implantation at 1 x 10"1"6 ions/cm"2 increased the intergranular corrosion susceptibility compared to that of unimplanted specimens. However, at the dose of 1 x 10"1"7 ions/cm"2, insignificant IGC attack was noticed. The IGC resistance increased with increase in the dose for all the specimens aged at 973 K, and the reduction in the electrochemical potentiodynamic reactivation ...

Science.gov (United States)

... Accession Number : ADA137272. Title : Effects of Yttrium Microalloying on the Epitaxial Grain Growth in Ti-6Al-4V Weld Fusion Zones. ...

Energy Technology Data Exchange (ETDEWEB)

This paper reviews our simulation study by numerical calculation based on two-, three- and multi-grain-size models on WC grain growth in fine grained WC-Co hardmetal doped with VC. The study aimed to presume or predict the following: (1) the cause and conditions for the abnormal grain growth which occurs in some cases in the fine grained hardmetal prepared from fine WC powders with mean grain size below about 0.2{mu}m, and (2) how the mean grain size of the hardmetal varies with decreasing mean grain size of the WC starting powder to 0.1 pm or nano-meter size. The calculation results by these three kinds of models suggested the following, respectively: (1) the occurrence of the abnormal grain growth is generally substantial for WC starting powder with bimodal size-distribution and mean gram size ...

International Science & Technology Center (ISTC)

Research on Diffusion Zinc Cladding of Structural Steels, as Well as Their Mechanical and Corrosion Properties to Replace Their Cyanic Cadmium Plating

Energy Technology Data Exchange (ETDEWEB)

Microstructure evolution under hot deformation was investigated in compression of a magnesium alloy AZ31 at 673 K (0.73T{sub m}). Two kinds of samples were machined along the parallel and transverse direction of the extruded rods. New fine grains are evolved at corrugated grain boundaries at low strains and developed rapidly in grain interiors in the medium range of strain, finally leading to a roughly full evolution of equiaxial fine grains. Kink bands are evolved at corrugated grain boundaries and in grain interiors at low strains. The boundary misorientation of kink band increases rapidly with increasing strain. These characteristics of new grain evolution process are not changed by the orientation of the samples, while the flow behaviors clearly depend on it. It is concluded that new grain evolution can be controlled ...

Energy Technology Data Exchange (ETDEWEB)

Using a radioactive tracer method the bulk and grain boundary diffusion of {sup 59}Fe was determined in industrial alloy 800 and melts of alloy 800 with additional P and S in the temperature range 800 to 1000 C. The use of the approximation of Suzuoka was confirmed by autoradiographs. In alloy 800 H the activation energy of grain boundary diffusion of {sup 59}Fe is (209 {+-} 17)kJ/mol. Dissolved elements especially P increase the activation energy of the grain boundary diffusion of Fe by their segregation to the grain boundaries. In addition the influence of the grain boundary diffusion on the growth of creep cavities was investigated in the same materials, and the chemical composition of the creep cavities and grain boundaries were analysed by Auger electron spectroscopy (AES). For alloy 800 + 0.088 wt-%P an enrichment of about 14 at-%P was observed at the ...

Energy Technology Data Exchange (ETDEWEB)

Sprayforming offers the possibility to produce a variety of preforms in a single step directly from the melt. Numerous processing parameters ensure high flexibility but require detailed knowledge concerning the microstructure of sprayformed material depending on chemical composition and processing parameters. Within the current study fundamental investigations using unalloyed and low alloy steel grades (C15, C105, 100Cr6) for sprayforming of plates and billets have been performed concerning the influence of chromium and carbon content and selected processing parameters. Sprayformed preforms revealed austenite grain sizes up to 500 {mu}m depending on the development of porosity. Different types of porosity have been detected which can be associated with incomplete densification due to high cooling rates, solidification shrinkage and entrapped nitrogen. Atomisation gas pressure and carbon content are parameters of primary importance. (Abstract ...

British Library Electronic Table of Contents (United Kingdom)

Porous ?-SiAlON ceramics are synthesized by reaction bonded method using hollow alumina spheres (HASs) as both sintering aids and pore-forming agents. Both micropores and macropores, which are constructured by SiAlON grains with different morphologies, are formed in the final SiAlON samples. The micropores are three-dimentional, and are built by equiaxial grains. While the hollow macropores, which have the similar morphology to hollow alumina sphere, are packed by elongated grains. In the sintering process, the solid dissolution process takes place, giving rise to the different alumina concentration of liquid phase, and thus resulting in the formation of two kinds of grains, the equiaxial grain and the elongated grain.

International Nuclear Information System (INIS)

Depletion studies are used to infer the presence of mantles and to constrain grain evolutionary models in the diffuse interstellar medium. The presence of these mantles appears to be important in the evolution of the grains inside diffuse as well as dense clouds. In dense clouds where the element-to-element abundances sometimes differ from those found in diffuse clouds, empirical relationships are starting to emerge between gas abundances and various types of peculiar selective extinction. These peculiar extinction curves may be the results of nonvolatile mantle formation on grain cores or may reflect chemical differences due to variations in the intrinsic metalicity from one cloud to another. A simple model of the time evolution of a parcel of gas and dust as observed by the depletion of two elements is presented. Different studies of grain evolution and selective extinction are discussed and compared.

Energy Technology Data Exchange (ETDEWEB)

The automotive industry desires to optimize safety and lightweight construction for the production of cars and trucks. The resulting task for steel suppliers is to make steel grades available that can fulfil these requirements. Different projects have shown optimistic outlooks for optimization of safety and reduction of the weight of automobile bodies by using different high strength and ultra high strength steels. In the last group the dual phase steels play the lead. In recent years different steel grades have been developed and optimized for these applications. On one hand developing the mechanical properties as well as joining and forming of dual phase steels is one of the first steps. On the other hand different coated surfaces for various applications of dual phase steels is another step. Starting with characteristic production ...

Energy Technology Data Exchange (ETDEWEB)

The deformation behavior and structure changes of magnesium alloy AZ31 were studied in compression at temperatures ranging from 523 K to 673 K and at a strain rate of 3 x 10{sup -3} s{sup -1}. They depend sensitively on deformation temperature. At high temperatures, grain fragmentation takes place due to frequent formation of kink bands initially at corrugated grain boundaries and then in grain interiors, followed by full development of new grains in high strain. At lower temperatures, in contrast, twinning takes place in rather coarse grains and kink bands are formed mainly in finer original ones in low strain. It is concluded that new grain evolution can be controlled by a deformation-induced continuous reaction resulting in grain fragmentation by kink bands, i.e. continuous dynamic recrystallization (cDRX). The latter is discussed ...

Energy Technology Data Exchange (ETDEWEB)

Abstract not provided

CERN Document Server

Constrained quantum dynamics is used to propose a nonlinear dynamical equation for pure states of a generalized coarse-grained system. The relevant constraint is given either by the generalized purity or by the generalized invariant fluctuation, and the coarse-grained pure states correspond to the generalized coherent i.e. generalized nonentangled states. Open system model of the coarse-graining is discussed. It is shown that in this model and in the weak coupling limit the constrained dynamical equations coincide with an equation for pointer states, based on Hilbert-Schmidt distance, that was previously suggested in the context of the decoherence theory.

Science.gov (United States)

Not Available

Energy Technology Data Exchange (ETDEWEB)

Evaluation of grain boundary composition and structure in superplastically deformed AA5083-based alloys (Al-4.5Mg-1.6Mn-0.2Zr) was carried out in a field-emission gun transmission electron microscope (FEG-TEM). During superplastic deformation at high homologous temperatures materials undergo extensive grain boundary sliding (GBS) which creates a flow of defects in the near-boundary region. Recent literature has shown that the grain-boundary composition in Al-Mg alloys is not necessarily the same as the matrix, and that these differences can have an effect on GBS.

Science.gov (United States)

... COMPUTERIZED SIMULATION, MOLDINGS, PROPELLANT GRAINS, IGNITION, COMBUSTIBLE CARTRIDGE CASES, COMBUSTION, HEAT ...

International Nuclear Information System (INIS)

The influence of chemical composition and heat treatment on a low-carbon steel, chromium steel and high speed steel has been examined by polarisation curves and electrochemical parameters deduced from the Tafel plots. The electrochemical corrosion resistance, which is small between the as-received steels become greater after heat treatment, following the order: carbon steel < chromium steel #approx# high speed steel. To explain these differences, the nano- and microstructure of the steels has been characterized by the ex situ techniques of atomic force microscopy and optical microscopy, before and after surface etching with Nital (a solution of 5% HNO_3 in ethanol). This causes preferential attack of the ferrite phases showing the carbide phases more clearly. From these nanostructural studies it was possible to better ...

International Nuclear Information System (INIS)

Nanocrystalline materials can exhibit properties which are considerably different from their coarse-grained counterparts, making them unique for basic or applied research and also very promising for potential applications. The topics which are addressed in the present paper are magnetic properties and magnetic correlations on the nanometer scale, mechanical properties, in particular the influence of grain boundaries on the elastic and plastic behaviour, and vibration models of grain boundary atoms in nanostructured materials. (author)

International Nuclear Information System (INIS)

The ductility of extruded heavy-section Ti-base--Mo--V--Fe--Al alloy was studied. Metallographic evidence for the large effect of grain size on ductility is presented. Fracture was found to occur in large-grain material after less deformation than in smaller grain size specimens.

Science.gov (United States)

... rate on the tensile properties of SA-106 carbon steel pipe, in support of analysis and experimental modeling of postulated pipe whip in nuclear ...

CERN Document Server

Differences in synchrotron radiation induced gas desorption from stainless steel and aluminium alloy

Energy Technology Data Exchange (ETDEWEB)

There are two types in quench distortion of steel parts: thermal distortion and transformation distortion. Quench distortion is caused mainly by uneven cooling rate of steel parts from Austenitising temperature. The rapid cooled side is lengthened (convex deformation); the slow cooled side is shortened (concave deformation). So, to control the quench distortion, it is necessary to regulate the cooling rate of steel parts during quenching. TWO COMPONENTS produce the quench distortion of steel parts: the thermal stress and transformation stress. Generally, the effect of the thermal stress on the quench distortion is stronger than the transformation stress. The quench distortion is caused by uneven cooling rate of the steel parts, from Austenitising temperature to Ms point and Ms-Mf range. So, to control the quench distortion, it is very important to regulate the cooling rate of the ...

International Nuclear Information System (INIS)

Russian (Jan 1976). USSR Mironov, Yu.M. Makarov, VA Nauchno-

Energy Technology Data Exchange (ETDEWEB)

Past movement on faults can be dated by measurement of the intensity of ESR signals in quartz. These signals are reset by local lattice deformation and local frictional heating on grain contacts at the time of fault movement. The ESR signals then trow back as a result of bombardment by ionizing radiation from surrounding rocks. The age is obtained from the ratio of the equivalent dose, needed to produce the observed signal, to the dose rate. Fine grains are more completely reset during faulting, and a plot of age vs grain size shows a plateau for grains below critical size : these grains are presumed to have been completely zeroed by the last fault activity. We carried out ESR dating of fault rocks collected from the Yangsan fault system. ESR dates from the this fault system range from 870 to 240 ka. Results of this research suggest that long-term cyclic fault activity continued ...

British Library Electronic Table of Contents (United Kingdom)

TaC and TaC-1wt.% B4C powders were consolidated using spark plasma sintering (SPS) at 1850^oC and varying pressure of 100, 255 and 363MPa. The effect of pressure on the densification and grain size is evaluated. The role of nano-sized B4C as sintering aid and grain growth inhibitor is studied by means of XRD, SEM and high resolution TEM. Fully dense TaC samples were produced at a pressure of 255MPa and higher at 1850^oC. The increasing pressure also resulted in an increase in TaC grain size. Addition of B4C leads to an increase in the density of 100MPa sample from 89% to 97%. B4C nano-powder resists grain growth even at high pressure of 363MPa. The formation of TaB2/Carbon at TaC grain boundaries helps in pinning the grain boundary and inhibiting grain growth. The effect of B4C addition on...

Science.gov (United States)

The progress made during the first two years of a program to study the migration of grain boundaries in ceramic oxides is reported. The principal results of the program are concerned with the structure of grain boundaries in ..cap alpha..-Al/sub 2/O/sub 3/, although important new information has also been obtained on grain boundaries in spinels and both germanlum and silicon. Attention is focused on the basal twin boundary in ..cap alpha..-Al/sub 2/O/sub 3/ which had been identified as a model interface in early work. A series of new grain boundaries exemplified by the (11anti23) twin are also discussed briefly as is the rhombohedral twin interface. Earlier results on the first-order (..sigma..=3) twin in spinel have been extended with the development of models for the computer-simulation of high-resolution TEM images of these interfaces. A study of low-angle grain boundaries in ...

Science.gov (United States)

An in-depth industrial hygiene survey was conducted to evaluate worker exposures to phosphine during fumigation of grain at the Early and Daniel Co. grain elevator in Louisville, Kentucky. Stored grain was fumigated using aluminum phosphide. Aluminum-phosphide pellets were also added directly to the grain by the blender as it was poured into the storage containers. Local exhaust ventilation was used at points in the grain-moving system where grain dust was generated. Air samples were taken during full-shift periods at the breathing zone of the weighmaster, two bin floormen, and the blender. Area monitoring samples were also taken. If the operators spend considerable time in the vicinity of a bin which is being filled with grain, there is a likelihood of far greater exposure levels being noted. According to the author, further studies of the ...

Energy Technology Data Exchange (ETDEWEB)

The kinetics of {sup 14}C-photosynthate import by developing wheat grains was followed after pulse-labeling the flag leaf with {sup 14}CO{sub 2}. Samples were collected from four successive points along the transport pathway to and within the grain: exuding aphid stylets on the peduncle, exuding grain pedicels, the grain crease tissues, and the liquid contents of the endosperm cavity. In addition, microautoradiographs were prepared of the grain crease tissues during movement of the {sup 14}C pulse into the grain. At all times, sucrose accounted for 93 to 97% of the total {sup 14}C present at all four sampling sites. The main features of the {sup 14}C kinetics could be accounted for by a simple compartmental model consisting of sucrose pools in series. Microautoradiographs of the crease tissues showed fairly uniform labeling of vascular parenchyma at all times, ...

Science.gov (United States)

Not Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Short communication

International Nuclear Information System (INIS)

... Engineering, Kitakyushu, Fukuoka (Japan) Hattanda, Takumi NTT Advanced

International Nuclear Information System (INIS)

Both the price of nickel and the allergic reaction that it can cause to human beings make it desirable to develop and use nickel-free austenitic stainless steels. The steels should be austenitic so as to avoid ferro-magnetism, a condition which has to be fulfilled for a number of requirements, including its use as implants in the human body, for wrist watch cases and many others. The paper presents the development of a nickel-free steel containing 11 percent manganese, 17 percent chromium, 4 percent molybdenum, and 0.9 percent nitrogen. This austenitic stainless steel has exceptional strength and corrosion resistance. These properties could result in numerous applications of the steel. A limitation, however, is that the steel is not weldable.

Energy Technology Data Exchange (ETDEWEB)

In this book over 250 alloys are organized by AISI number into 10 major sections: Irons, Carbon Steels, Alloy Steels, Low Alloy Constructional Steels, Ultra High Strength Steels, Tool Steels, Maraging Steels, Wrought Stainless Steels, Heat Resistnat Casting Alloys, and Iron Based Rought Superalloys. Each alloy record lists the designation, specifications, UNS number, composition, product forms and a comment on the high-temperature properties and applications. Referenced data is then given for physical properties such as density, specific heat, thermal conductivity, thermal expansion, electrical conductivity, Poisson's ratio, moduli of elasticity and rigidity, etc. Mechanical properties follow, and include tensile properties, shearing and bearing properties, impact properties, creep, stress rupture and stress relaxation and fatigue ...

Energy Technology Data Exchange (ETDEWEB)

Grain refinement behavior of copper alloys cast in permanent molds was investigated. This is one of the least studied subjects in copper alloy castings. Grain refinement is not widely practiced for leaded copper alloys cast in sand molds. Aluminum bronzes and high strength yellow brasses, cast in sand and permanent molds, were usually fine grained due to the presence of more than 2% iron. Grain refinement of the most common permanent mold casting alloys, leaded yellow brass and its lead-free replacement EnviroBrass III, is not universally accepted due to the perceived problem of hard spots in finished castings and for the same reason these alloys contain very low amounts of iron. The yellow brasses and Cu-Si alloys are gaining popularity in North America due to their low lead content and amenability for permanent mold casting. These alloys are prone to hot tearing in permanent mold casting. ...

International Nuclear Information System (INIS)

Growing competitiveness of alternative manufacturing routes requires cost minimization in the production of drop forged components. The authors analyse the potential of medium carbon, vanadium microalloyed steels for drop forging. Laboratory and industrial experiments have been carried out emphasizing deformation and temperature cycles, strain rates and dwell times showing a typical processing path, associated mechanical properties and corresponding microstructures. The steels the required levels of mechanical properties on cooling after forging, eliminating subsequent heat treatment. The machinability of V-microalloyed steels is also improved when compared with plain medium carbon steels. (author)

International Nuclear Information System (INIS)

The effect of the rare earth element, yttrium, on the mechanical properties of 9Cr-2WVTa low active martensite steel for fusion reactor was studied and the metallurgical behavior of yttrium in the steel was primarily analyzed. The results show that it is easy for yttrium to aggregate and form the blocky yttrium rich inclusions in the steel, which can dissever the continuity of the matrix and produce micro-cracks for fracture. The yttrium rich inclusions were distributed along the rolling direction, which made the fracture surface delaminated in the tensile and impact samples, and reduced the mechanical properties of the steel. (authors)

International Nuclear Information System (INIS)

This paper proposes a model to explain tritium release behavior of an irradiated Li_4SiO_4 sample made by Forschungszentrum Karlsruhe. The release curves were obtained in a series of experiments carried out using out-pile temperature programmed desorption techniques in the Kyoto University Reactor (KUR). Tritium release curves obtained for different purge gas compositions (N_2, N_2 + H_2, N_2 + H_2O) were compared for selection of suitable conditions to determine the apparent diffusivity of tritium in a crystal grain of Li_4SiO_4.In the model formation, some mass transfer steps in the bulk of the crystal grain and those on the surface of the grain were taken into account, which were diffusion of tritium in the grain, adsorption and desorption of water on the surface of the grain, two types of isotope exchange reactions, and water formation reaction by the addition of hydrogen to the ...

Energy Technology Data Exchange (ETDEWEB)

Deformation mechanisms were investigated in fine-grain (d=7 {mu}m) AZ31 Mg alloy in order to understand their excellent room-temperature ductility. Dislocation cross slip from basal to non-basal planes was found to occur easily at room temperature at a plastic anisotropy factor of only 1.5 instead of several tens to 100 expected from the single crystal CRSS data. Enhanced grain-boundary sliding (GBS) was also found to occur at room temperature. The contribution of GBS strain was found to be approximately 8% of total strain. The enhanced activity of non-basal dislocation slip and GBS was attributed to grain-boundary compatibility effects. Moreover, dynamic recovery was found to occur during deformation at room temperature associated with the formation of recovery twins and small-angle grain boundaries. The occurrence of these deformation mechanisms at room temperature was considered to be a major reason ...

Science.gov (United States)

A "hemispheres-in-cell" geometry is provided for prediction of colloid retention during transport in porous media. This new geometry preserves the utilities provided in the Happel sphere-in-cell geometry; namely, the ability to predict deposition for a range of porosities, and representation of the influence of neighboring collectors on the fluid flow field. The new geometry, which includes grain to grain contact, is justified by the eventual goal of predicting colloid deposition in the presence of energy barriers, which has been shown in previous literature to involve deposition within grain to grain contacts for colloid:collector ratios greater than approximately 0.005. In order to serve as a platform for predicting deposition in the presence of energy barriers, the model must be shown capable of quantitatively predicting deposition in the absence of energy barriers, which is a requirement that was ...

International Nuclear Information System (INIS)

The effects of the dopants, Mg"2"+, Sr"2"+, Sc"3"+, Yb"3"+, Gd"3"+, La"3"+, Ti"4"+, Zr"4"+, Ce"4"+, and Nb"5"+, on the grain boundary mobility of dense Y_2O_3 have been investigated from 1,500 to 1,650 C. Parabolic grain growth has been observed in all cases over a grain size from 0.31 to 12.5 microm. Together with atmospheric effects, the results suggest that interstitial transport is the rate-limiting step for diffusive processes in Y_2O_3, which is also the case in CeO_2. The effect of solute drag cannot be ascertained but the anomalous effect of undersized dopants (Ti and Nb) on diffusion enhancement, previously reported in CeO_2, is again confirmed. Indications of very large binding energies between aliovalent dopants and oxygen defects are also observed. Overall, the most effective grain growth inhibitor is Zr"4"+, while the most potent grain growth promoter is Sr"2"+, both at ...

Energy Technology Data Exchange (ETDEWEB)

The effects of Fe and B{sub 4}C on the sintering behavior and mechanical properties of TiB{sub 2} ceramics have been studied. Sintering was performed in an Ar atmosphere at 2000{degrees}C using attrition-milled TiB{sub 2} powder. When a small amount of Fe (0.5 wt%) was added, abnormal grain growth occurred and the sintered density was low. In the case of B{sub 4}C added along with 0.5 wt% Fe, however, abnormal grain growth was remarkably suppressed, and the sintered density was increased up to 95% of theoretical. But with excess Fe addition (5 wt%), B{sub 4}C grains did not act as a grain growth inhibitor, and B{sub 4}C grains were frequently trapped in large TiB{sub 2} grains. The best mechanical properties were obtained for the TiB{sub 2}-10 wt% B{sub 4}C-0.5 wt% Fe ceramics, which exhibited a three-point bending strength of 400 MPa and a fracture toughness of ...

Energy Technology Data Exchange (ETDEWEB)

Theoretical work supported by this grant has lead to the concept of the specific pinning force Q and the development of new methods to sum elementary interaction forces to find Q. Pinning due to changes in transition temperature or thermodynamic critical field in thin layers (e.g., a grain boundary), is greatly reduced due to the proximity effect and the stress field interaction due to the dislocations in the grain boundary has been shown to be negligible. The crystalline anisotropy (CA) and electron scattering (ES) interactions have been computed for the first time for an arbitrary boundary. Experiments on niobium bicrystals, polycrystalline niobium thin foils doped with oxygen, lead-bismuth alloy thin films and lead-bismuth alloy films in which either lead or thallium has been allowed to diffuse down the grain boundaries and out into the grains provide evidence that confirms the predictions of the ...

Energy Technology Data Exchange (ETDEWEB)

The microstructures of magnesium AZ31 are examined following hot compression testing and annealing. The grain size, fraction dynamically recrystallized and, in a couple of cases, the crystallographic texture are reported. It was found that the progress of dynamic recrystallization is strongly sensitive to processing conditions but that the dynamically recrystallized grain size was less sensitive to stress than in other metals. It was also found that, for structures containing between 80 and 95% dynamic recrystallization, abnormal grain growth occurs during annealing. The crystallographic texture produced is also sensitive to the deformation conditions. (orig.)

Energy Technology Data Exchange (ETDEWEB)

The grain boundary crystallographic misorientations of magnetic-pulse-welded (MPW) aluminum alloy (AA) 6061-T6 in linear and tubular configurations were examined using the electron backscattered diffraction (EBSD) technique. A refined structure of heavily deformed grains with higher grain boundary angles was observed in linear welds. Significant spalling was observed away from the joints, in the interior of tubular welds. The results show the complex interaction of shock waves with the materials during this impact welding process.

Energy Technology Data Exchange (ETDEWEB)

The efficiency of NbC on WC grain coarsening in a WC-10wt.%Co hardmetal alloy was demonstrated by hardness measurement and WC granulation observation. The heterogeneous and overall grain growth were controlled. A low temperature experimentally produced NbC was used and compared to the inhibition potential of a commercial NbC powder. The results were the same in terms of structural fineness and hardness. The dispersion of the experimental NbC was not a problem, in spite of its size. The experimental NbC has very large particles, formed by agglomerates of small crystallites. During milling these agglomerates could be broken down. (orig.)

Energy Technology Data Exchange (ETDEWEB)

This paper describes the test results on high-temperature strength properties of fire resistant steel(FR steel) for building, the formulation, and the examples of application to member tests and actual buildings. Because of its components and manufacturing method, FR steel excels in strength at elevated temperature due to precipitation and dispersion strengthening. Tests on high temperature properties of FR steel showed that every property such as strength, stress-strain curve, elastic modulus, and creep performance at high temperature was superior to those of conventional steels. Then, it was confirmed in the tensile tests at room temperature and high temperature after heat history that FR steel could be reused after fire. It was also found in the member tests that columns and beams of FR steel could support loadings equivalent to long-term ...

International Nuclear Information System (INIS)

68 replaced carbon steel piping in secondary system of pressurized water reactor (PWR) has been investigated by visual examination for checking thinning conditions. It is well known that the flow-accelerated corrosion (FAC) was inhibited by traces of Cr in steel. Therefore, the chemical compositions of those steels have been measured. In addition, the micro structure and hardness of those steels have been investigated. And the relationship between those material variables and FAC rate was considered. As the results, (1) The Cr contents in those steels were below 0.1 wt% except one sample. Minute quantities of chromium increase the resistance against FAC. But the water velocity was thought to be the dominant factor rather than chemical composition in steel, at least such as below 0.1%Cr. (2) Hardness of all piping has been satisfied the specifications of each ...

British Library Electronic Table of Contents (United Kingdom)

In the paper, the effect of Ni content, WC grain size and Mo2C addition on WC-6.25wt%TiC-9.3wt%Ni cemented carbide were investigated to improve the properties of Ni-bonded cemented carbides. The results show that the decrease of Ni content will result in the decrease of transverse rupture strength and increase of hardness; with the decrease of WC particle size, hardness increases due to the refinement of WC grains, however, the transverse rupture strength decrease due to the decrease of Ni binder thickness; Mo2C proves to be an effective grain growth inhibitor. With the increase of Mo2C content, the WC grains are refined and the hardness and transverse rupture strength are improved. Generally, when the Ni content is decreased to 8.4wt%, 13.45mm WC is used and 1.2wt% Mo2C is added, a higher...

Science.gov (United States)

... Astronomy & Space Biology Chemistry & Materials Computing Earth & Environment Education ... Materials Research Center at the University of Chicago, one of nearly 30 NSF-supported Materials ...

Science.gov (United States)

The general goals of this research effort is to explore the potential applications and performance of fine grained computer architectures for vision. The body of this report gives a brief overview of the results of the research during the first twelve mon...

Energy Technology Data Exchange (ETDEWEB)

The use of selective additives such as MgO as a sintering aid and a rare earth oxide as a grain growth inhibitor, has allowed the manufacture of beryllia ceramics having close to theoretical density. The grain size and grain size distribution can be controlled by an optimum firing schedule leaving a remnant porosity which is extremely fine (0.2 {mu}m). This structure is compared with conventional BeO ceramics, densified by liquid phase sintering, which develops a glassy grain boundary and retains large pores up to 3 {mu}m. The significantly improved strength properties, extremely fine pores,the 'pinning effect' of rare earth oxide, and the superior surface finish both in the as-fired and polished state are discussed in relation to the micro-structure. (orig.).

Science.gov (United States)

An in/depth industrial hygiene survey of exposures to phosphine during the use of aluminum phosphide was conducted as part of a survey on exposure to grain fumigants. Area monitoring and breathing-zone sampling for phosphine were conducted during the addition of aluminum phosphide to grain during turning operations; source samples and peak personal exposures were also analyzed. Major sources of personal exposure included the escape of air from the bin headspace during filling with treated grain, filling and emptying of the phosphide pellet dispenser, and infiltration from the treated grain bin and from the pellet dispenser itself into adjacent air space. Relatively good dust control was indicated by the total dust samples collected during the survey. Measures recommended by the author are in the report.

Science.gov (United States)

Proceedings of the 11th IWGS Proceedings of the 8th IOC TREP, Release 10 Barley QTL Community Curation Workbook CIMMYT International Nursery Data Brachypodium website Rye...

Science.gov (United States)

Wit?,-grain ultimate compressive strength of multiply extruded graphite rods made with G-18 flour,. V. 5. " TOTAL n ACCESSIBLE TO Hp AT 2600 psi ...

Energy Technology Data Exchange (ETDEWEB)

Necessary conditions are derived for compact aggregates of solid matter to develop from loose local clumps of dust grains in a contracting protostellar cloud.

Energy Technology Data Exchange (ETDEWEB)

With the aim of optimizing the nitriding process, experimental studies of the plasma nitriding of four selected steels were carried out, using a d.c. glow discharge. The process parameters were varied systematically. By means of transmission and scanning electron microscopy and X-ray diffraction, the microstructures, including the thicknesses of the compound zones and the diffusion zones of the nitrided steels, were obtained. Using cross-sectional samples and a micro-Vickers indenter, hardness depth profiles were also obtained. From the time and temperature dependences of the hardness profiles, effective diffusion constants and corresponding activation enthalpies were obtained. Furthermore, in an attempt to shed some light on the atomistic nitriding mechanisms, the glow discharges were studied by measuring energy spectra of the energetic ions hitting the cathode (the steel test specimens). It was shown that an increase of ...

Wastenet

...3 MtC, with 78% of these emissions from integrated steel making (26.9 MtC) and the rest (22%)...6 MtC, with 71% of these emissions from integrated steel making (21.9 MtC) and the rest (29%)...1 million ton of carbon (MtC) in 1994 (3.9 MtC from integrated steel making, and 2.2 MtC from secondary ...7 MtC in 2002 (3.7 MtC from integrated steel making, and 2.0 MtC from secondary steel making), corresponding ...

Science.gov (United States)

This study deals with the torsional response of Ti-8823 and 18Ni (200) maraging steel. The effect of different heat treatments and the subsequent change in microstructure are investigated. In the case of the Ti-8823, a comparison was made between the solu...

UK PubMed Central (United Kingdom)

OBJECTIVE: To study cause specific mortality and cancer morbidity in workers exposed to the dust of grinding materials, grinding agents, and stainless steel, especially with regard to a possibly increased...Full Text Available

International Nuclear Information System (INIS)

Iron oxide as sintering aid to Ce-TZP ceramics produces a beneficial effect on the tetragonal phase stabilization. It was found that ceria powder particle size of 2,0 #mu#m turns the grain-boundary electrical conductivity higher than ceria powder of smaller grain size. (author)

UK PubMed Central (United Kingdom)

Physiological properties involved in divergent cadmium (Cd) accumulation among rice genotypes were characterized using the indica cultivar ‘Habataki’ (high Cd in grains)...Full Text Available

International Nuclear Information System (INIS)

The influence of structure on mechanical properties in the course of tensile tests in a wide range of temperatures was studied, using the VT16 structure thermally strengthened (alpha+beta)-titanium alloy by way of example. It is ascertained that transition from ductile to brittle fracture at the temperature of -196 deg C is observed only in coarse-grain alloy having alpha-eldging of beta grains.

International Nuclear Information System (INIS)

The effect of electron beam welding parameters on fusion zone (FZ) microstructure and porosity in a Ti-6.8 Al-3.42 Mo-1.9 Zr-0.21 Si alloy (Russian designation VT 9) has been investigated. It has been observed that the FZ grain width increased continuously with increase in heat input when the base metal was in the #beta# heat-treated condition, while in the #alpha# + #beta# heat-treated base metal welds, the FZ grain width increased only after a threshold energy input. The difference is attributed to both the weld thermal cycle and the pinning effect of equiaxed primary alpha on grain growth in the heat-affected zone (HAZ) of #alpha# + #beta# heat-treated base metal. Postweld heat treatment (PWHT) in the subtransus and supertransus regions did not alter the columnar grain morphology in the FZ, possibly due to the lack of enough driving force for the formation of new grains by the ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

Energy Technology Data Exchange (ETDEWEB)

Steel is one of the most versatile materials known to mankind. It is used in a variety of applications. In many of these applications, it is exposed to the atmosphere, leading to rust formation, which weakens structures made using steel. Hence, protection is important. The popular methods to prevent corrosion are painting, galvanizing, electroplating etc. The widely used Chrome etching process is very effective in corrosion inhibition as well as in hardening the steel. But, Chromium and its compounds are highly placed among the toxic chemicals listed under pollution prevention initiatives of the EPA. Hence, it was decided to find alternatives to this process.

Energy Technology Data Exchange (ETDEWEB)

In recent years, the phase stability of austenitic stainless steels, and its effect on the mechanical properties of stainless steels, have been the subject of much interest. With the availability of new experimental techniques, new theoretical methods, and new computational procedures, significant advances have been made in understanding, and being able to predict, phase stability and mechanical properties of stainless steel welds. This paper reviews some of these developments, with an emphasis on recent work that has been done at Oak Ridge National Laboratory.

International Nuclear Information System (INIS)

Mixed microstructures have been studied in low- carbon microalloyed steels suitable for automotive applications, after continuous cooling from the hot-rolled condition. Microstructural features such as polygonal ferrite, bainitic and acicular ferrite and microphase constituent are identified using transmission electron microscopy. The influence of these mixed structures on the tensile strength, impact toughness and fracture behaviour is examined. It is found that improvements in impact toughness as compared with microalloyed medium- carbon ferrite/pearlite steels can be achieved from these predominantly acicular structures developed by controlling alloy composition and continuous cooling of these lower carbon steels. (orig.).

International Nuclear Information System (INIS)

A study is made into microhardness and structure of coatings on various system steels (37G2S, 25Kh5M, R6M5), obtained by ion nitriding in a low pressure (10"-"1 Pa) arc discharge plasma. A comparison of properties is accomplished for steels nitrided in an arc gas discharge and in a furnace. It is stated that ion-plasma nitriding in an arc gas plasma generator is an efficient method of alloy steels hardening which allows changing the structure and increasing the hardness of a surface layer up to rather great depth

International Nuclear Information System (INIS)

The additional error in measurement of the thickness of Kh18N10T steel for possible changes in composition with an energy of the photons of ionizing radiation of 10-80 keV was evaluated. The desirability of use of a type REIS-I x-ray emitter in measurement of the thickness of steel up to 1 mm is shown. The instrument provides measurement of the thickness of steel in the 0.1-1.0 mm range with a reproducibility of the results with an error not exceeding 0.5-1.0%. The measurement error with corrugations characteristic of bellows does not exceed 5%.

Energy Technology Data Exchange (ETDEWEB)

Short communication

International Nuclear Information System (INIS)

... Yoshiaki Toshiba Corp., Nuclear Power Division, Yokohama, Kanagawa (Japan)

Science.gov (United States)

No abstract available.

Energy Technology Data Exchange (ETDEWEB)

Stress-rupture strength tests were made of metal steam pipe (12Kh1MF steel) in various conditions, the original, after aging under laboratory conditions (580{degrees}C, 10,000 h), and after long service. It was shown that the more the steel is hardened by heat treatment or cold plastic working in the original condition, the less it hardens in creep. It was established that softening in creep of steel with a moderate yield strength is caused primarily by aging and with a high yield strength by pore formation.

Energy Technology Data Exchange (ETDEWEB)

Silicon nitride based ceramics have attracted considerable attention as good candidates for structural applications due to their excellent mechanical properties including strength, hardness, fracture toughness, and high temperature strength. These properties are strongly influenced by grain size and morphology, and by the degree of crystallinity and chemistry of grain boundary phases. In this work, the microstructure of Si{sub 3}N{sub 4} densified with Nd{sub 2}O{sub 3}, Y{sub 2}O{sub 3} and Al{sub 2}O{sub 3} sintering additives was studied. Sintered samples were polished and plasma etched for microstructural analysis using scanning electron microscope. Quantitative evaluation of materials microstructure was accomplished using Quantikov software. Fracture toughness was measured by Vickers indentation method. The observed microstructure is typical of silicon nitride based materials and is characterized by high aspect ratio.-Si{sub 3}N{sub 4} ...

Energy Technology Data Exchange (ETDEWEB)

A Fe-20at.%Cr-10%Al matrix was dispersed with a wide range of different oxides in order to study the effect of oxygen-active dopants on the high-temperature growth and adhesion of {alpha}-Al{sub 2}O{sub 3} scales. Effect of these various cation dopants on the alumina scale microstructure was correlated with dopant ion segregation to the {alpha}-Al{sub 2}O{sub 3} grain boundaries using analytical electron microscopy. Elements such as Mn and V showed little effect on the oxide scale and were not observed to segregate. Elements such as Y and Gd resulted in finer, more columnar {alpha}-Al{sub 2}O{sub 3} grains and were segregated to scale grain boundaries. However, Ti, Ta, Ca, and Nb also were found to segregate but had a lesser effect on scale morphology. This indicates that cation segregation to scale grain boundaries is not a sufficient condition to achieve beneficial oxidation effects. The driving force ...

Energy Technology Data Exchange (ETDEWEB)

Past movement on faults can be dated by measurement of the intensity of ESR signals in quartz. These signals are reset by local lattice deformation and local frictional heating on grain contacts at the time of fault movement. The ESR signals then grow back as a result of bombardment by ionizing radiation from surrounding rocks. The age is obtained from the ratio of the equivalent dose, needed to produce the observed signal, to the dose rate. Fine grains are more completely reset during faulting, and a plot of age vs. grain size shows a plateau for grains below critical size; these grains are presumed to have been completely zeroed by the last fault activity. We carried out ESR dating of fault rocks collected near the Gori nuclear reactor. Most of the ESR signals of fault rocks collected from the basement are saturated. This indicates that the last movement of the faults had occurred ...

Energy Technology Data Exchange (ETDEWEB)

BaTiO{sub 3} compacts, when fluxed with {lt} 2 vol% of a complex borate glass phase, were sintered to near theoretical density at temperatures {lt} 1175{degrees}C in 2 h. Microstructural analysis showed a uniform grain size {lt} 1.0 {mu}m with 0.75 wt% ZrO{sub 2} added to the flux phase as a grain growth inhibitor. TEM analysis revealed a microcrystalline grain-boundary phase with the ZrO{sub 2} resident along the grain boundaries. These samples displayed an essentially flat dielectric profile, low dissipation factors ({lt} 2%) over the range 25{degrees} to 125{degrees}C, a near linear dependence ({approx} {+-} 15%) between 25{degrees} and {minus} 55{degrees}C, and significantly increased voltage stability. X-ray diffraction analysis of these small-grained materials indicates a suppression of the tetragonal structure toward a more cubic modification.

International Nuclear Information System (INIS)

Results of researches on nitriding process of EJ961 steel are presented in this work. This steel was subjected to nitriding both on the cathode and on the isolated from cathode and anode substrate, that is at so called potential of glow discharged plasma. Nitriding processes were performed using device for glow discharge treatments with cooled anode. (author)

International Nuclear Information System (INIS)

Structure of ferrite in drawn pearlitic steel containing 0.9 mass% C was investigated with X-ray diffraction technique using synchrotron radiation. In the detailed analysis of diffraction peaks of ferrite during the drawing process, it was experimentally revealed that the transformation of ferrite from bcc to bct due to the supersaturation of carbon in ferrite of heavily drawn pearlitic steel.

Energy Technology Data Exchange (ETDEWEB)

Azobenzene dyes are effective inhibitors for austenitic 304 L and 316 L stainless steel corrosion in high acidic medium up to 7N. A good efficiency is obtained from weight loss and electrochemical Rsub(p) measurements in hydrochloric acid, while no inhibition is observed in sulfuric solutions. Transformation from the primarily azobenzene to other compounds give rise to enhanced protection of steel samples, and probable structures of the inhibiting species are proposed in view of our results.

International Nuclear Information System (INIS)

Paper estimates the corrosion resistance and studies the character of dissolving of silicon-bearing austenite stainless steels in strongly oxidizing media containing phosphate and fluoride admixtures. Corrosion behaviour of the studied steels is determined to depend essentially on the content of admixture or alloying silicon, as well as, on their phase composition in many respects determined by the thermal treatment condition. Refs. 22, figs. 1, tabs. 2.

International Nuclear Information System (INIS)

Pitting corrosion is a kind of electrolytic corrosion by which the surface of a material is locally affected owing to inhomogeneities on the part of the material or medium. The paper deals briefly with questions relating to the importance, to parameters medium or materialwise, influence on production and construction, as well as the general conditions for pitting corrosion. In particular oxygen corrosion in unalloyed and low-alloy steel, and pitting corrosion in ferritic chromium-steel and austenitic chromium-nickel (molybdenum) steel is described. (DG).

Energy Technology Data Exchange (ETDEWEB)

The use of nickel alloys in Flue Gas Desulfurization (FGD) applications is described. Recently, nickel alloys 625 and C-276 have been clad to carbon steel plate. Production and properties of the clad plate are reviewed and a brief discussion is presented on production, fabrication and welding. Laboratory and field corrosion tests in SO/sub 2/ scrubber environments suggest that alloy 625 and C-276 clad steel plates are as corrosion resistant as the solid alloy plate.

Energy Technology Data Exchange (ETDEWEB)

A number of properties in steel components are detrimentally influenced when exposed to hydrogen environments. Under these conditions, atomic hydrogen is adsorbed on the steel surface, then absorbed and preferentially transported towards tri-dimensional stressed regions in the crystal lattice and into defects such as interfaces or dislocations. The hydrogen embrittlement susceptibility is strongly influenced by various microstructural parameters including the type of inclusions, steel composition and heat treating conditions. One of the alternatives employed in minimizing hydrogen embrittlement is the use of surface barriers for hydrogen permeation. In particular, the presence of surface nitride layers in steels can be considered as an effective barrier. Nitride steel surface layers can be produced by plasma nitriding with the concomitant benefits of improved surface hardness, as ...

Energy Technology Data Exchange (ETDEWEB)

Discussion is presented of world crude steel production, the Japanese steel industry and its expectations of the Canadian coal industry. It is concluded that the Canadian coal industry should pay attention to the trend in customer's requirements regarding coal quality, maintain price competitiveness in the international market place, and remain flexible with regard to the market trend.

International Nuclear Information System (INIS)

Effect of hydroxide nature, concentration and temperature on corrosion resistance of domestic steels and alloys to hot NaOH, KOH, LiOH solutions is considered. It is ascertained that by corrosion growth in relation to stainless steels and nickel alloys, the hydroxides are placed in the following sequence: LiOHsteel and nickel alloy tendency to cracking is manifested, are determined. 12 refs., 12 figs.

International Nuclear Information System (INIS)

Test Blanket Modules (TBM) will be tested in ITER to verify the capability of tritium breeding and recovery and the extraction of thermal energy suitable for the production of electricity. A Helium Cooled Solid Breeder (HCSB) TBM has been developed in Korea to accomplish these goals. Reduced Activation Ferritic/Martensitic (RAFM) steel has been chosen as the primary candidate structural material for Korean TBM. Due to the complexity of the First wall (FW) and Side wall (SW), it is necessary to develop various joining technologies, such as Hot Isostatic Pressing (HIP), Electron Beam Welding (EBW) and Tungsten Inert Gas (TIG) welding, for the successful fabrication of TBM. In this study, the mechanical properties of TIG welded RAFM steel were investigated. Various mechanical tests of TIG-welded RAFM steel were performed to obtain the optimized TIG welding process for RAFM steel

International Nuclear Information System (INIS)

The critical part of the trimetallic transition joint (type 304 stainless steel/Alloy 800/2.25 Cr-1 Mo steel), the Alloy 800/2.25 Cr-1 Mo steel joint welded with Inconel 182, was subjected to thermal cycling between room temperature and 873 K. The thermal cycling test procedure used produces accelerated failures in transition joints similar to those observed in steam generators of operating power plants. On thermal cycling, precipitation at the weld/ferritic steel interface decreased on post-weld heat treatment. This precipitation increased with increased prior ageing and applied stress. The results of these tests indicated a considerable improvement in performance of the trimetallic transition joint compared to the direct (bimetallic) transition joint. (orig.).

British Library Electronic Table of Contents (United Kingdom)

A fully lamellar ferrite/cementite nanostructure was designed in a low C steel by using a specific thermal treatment. The strengthening of such microstructure has been investigated as a function of prestrain by rolling up to a deformation of 300%. As in usual pearlitic structure, its work-hardening shows no saturation and its elongation to fracture remains rather constant instead of decreasing drastically as conventional steels. The hardening by a similitude effect is thus not the privilege of pearlitic steels. Nevertheless, its lower initial work-hardening rate at low strain compared to an equivalent pearlitic steel and a lower hardening potential at high strain let us suspect major differences in the nature and the behaviour of ferrite channels in relation to the morphogenesis of the mic...

Energy Technology Data Exchange (ETDEWEB)

In an effort to minimize the distortion of bearing steel rings during the production process, 100Cr6 steel billets are spray formed with a unique cooling control system to control the cooling and solidification behavior of the deposits. Effects of heating around the deposits, gas cooling at the substrate bottom and the gas flow over the deposits are investigated both by numerical simulation and experiment. Porosity profiles and microstructures of spray formed bearing steel are examined and evaluated. The investigation results show that the thermal boundary conditions of the deposits play important roles on the cooling and solidification behavior of the deposits, especially at the deposit periphery. Porosity in the 100Cr6 bearing steel deposit can be reduced significantly with the special cooling control system.

International Nuclear Information System (INIS)

Nitrogen has been added to stainless steels to improve mechanical strength and corrosion resistance. High nitrogen steel production is limited by high gas pressure requirements and low nitrogen solubility in the melt. One way to overcome this limitation is the addition of nitrogen in solid state because of its higher solubility in austenite. However, gas and salt bath nitriding have been done at temperatures around 550 C, where nitrogen solubility in the steel is still very low. High temperature nitriding has been, thus proposed to increase nitrogen contents in the steel but the presence of oxide layers on top of the steel is a barrier to nitrogen intake. In this paper a modified plasma nitriding process is proposed. The first step of this process is a hydrogen plasma sputtering for oxide removal, exposing active steel surface improving nitrogen pickup. This is ...

Science.gov (United States)

After each archwire was ligated into a bracket with a 0.010-in stainless steel wire, both stainless steel and beta-titanium archwires (0.017- x 0.025-in) were slid through commercially pure titanium brackets (0.018-in slot size) at 34 degrees C in both the dry and wet conditions. As controls, stainless steel archwire versus stainless steel bracket couples were used with comparable dimensions. The drawing forces were measured at 5 angulations (0 degrees, 3 degrees, 7 degrees, 9 degrees, and 11 degrees ) for 5 normal forces (nominally 0.2, 0.4, 0.6, 0.8, and 1.0 kg). Regression lines were determined for each frictional couple (P <.05). In the passive configuration, the kinetic frictional coefficients of control and test couples in the dry condition were comparable to previously reported values at 0.11 +/- 0.01 for stainless steel versus stainless steel, 0.12 ...

International Nuclear Information System (INIS)

Rapid corrosion of PWR steam generator carbon steel support structures and consequential denting of steam generator tubes led to investigation of alternative support designs and materials. In recent designs of steam generators the carbon steel drilled hole tube support plate has been replaced by one of quatrefoil or trefoil shape to minimize the contact area. These plates are now made of more corrosion resistant chromium steel (approx. 12%Cr) to ensure that they are less vulnerable to attack in the event of adverse boiler water chemistry. This study was initiated to examine the corrosion behavior of a range of chromium steels in the acid chloride environments characteristic of tube/support plate crevices under adverse boiler water conditions. Objectives of the study were to: 1) determine the relative susceptibility of candidate tube support plate steels to acid chloride corrosion; ...

International Nuclear Information System (INIS)

Ferritic/martensitic steel, modified 9Cr-1Mo steels have been used most extensively in the power generation industry throughout the world due to having superior high temperature properties such as high strength, creep resistance, and good microstructure stability. These steels are also the primary candidate for the RPVs(Reactor Pressure Vessels) of High Temperature Gas-Cooled Reactors. Currently, many studies has been conducted in laboratory-scale for mod. 9Cr-1Mo steels. However, there is a lack of the study on forged thick- section for RPVs. The differences in characteristics including the through thickness microstructure and mechanical properties between internal and external locations may occur during cooling after austenitization, because the thickness of RPVs is over about 200mm. Therefore, in order to use ferritic/martensitic steel as RPVs, a detailed assessment of the ...

Energy Technology Data Exchange (ETDEWEB)

Superplasticity can be generally achieved by grain boundary sliding (GBS). The GBS in polycrystalline materials sometimes accompanies with intergranular fracture because of stress concentrations at triple points and/or GB irregularities. To develop the superplastic flow, it is necessary to suppress the intergranular cracking. In the present study, therefore, polycrystalline molybdenum with distinct GB microstructures, such as grain boundary character distribution (GBCD), has been employed to clarify the relationship between fracture behaviour and GB microstructures. Microstructures were analyzed using a FE-SEM/EBSP/OIM system prior to 4-points bending tests at 77K, thereafter, crack propagation was observed. The main results obtained are as follows. Stress fluctuations on stress - strain curves were observed for specimens with random oriented grains, whereas such behaviour rarely occurred for ones with textured ...

Energy Technology Data Exchange (ETDEWEB)

We present the first 3.8 {micro}m image of the dusty ring surrounding the young binary system GG Tau, obtained with the W. M. Keck II 10m telescope's adaptive optics system. THis is the longest wavelength at which the ring has been detected in scattered light so far, allowing a multi-wavelength analysis of the scattering proiperties of the dust grains present in this protoplanetary disk in combination with previous, shorter wavelengths, HST images. We find that the scattering phase function of the dust grains in the disk is only weakly dependent on the wavelength. This is inconsistent with dust models inferred from observations of the interstellar medium or dense molecular clouds. In particular, the strongly forward-throwing scattering phase function observed at 3.8 {micro}m implies a significant increase in the population of large ({approx}> 1 {micro}m) grains, which provides direct evidence for ...

British Library Electronic Table of Contents (United Kingdom)

The contribution of ear photosynthesis to grain filling in wheat (Triticum aestivum L.) is not well known. The main objective of this work was to evaluate this contribution through three different experimental approaches: (1) ear photosynthesis was reduced by removing awns or shading the ears (in combination with a defoliation treatment), (2) grain weight per ear was compared in an 'all shaded' crop versus plants where only the vegetative parts were shaded ('ear emerging'), and (3) ear photosynthesis was reduced with DCMU (3-(3,4-dichlorophenyl)-1,1-dimethylurea), a specific inhibitor of photosystem II. In field experiments in La Plata (Argentina), cultivars Klein Escudo and BioINTA 3000 were subjected to awn removal and ear shading treatments, with or without severe defoliation, and to 'a...

British Library Electronic Table of Contents (United Kingdom)

This study reports a determination of the polarity of WC facets in WC-Co alloys sintered at the liquid state. In these alloys, WC grains are delimited by basal facets and two sets of {101 0} prismatic facets, one set of facets being much more developed than the other. A variation of the shape is observed as a function of the composition of the alloy. High resolution transmission electron microscopy is used to investigate the polarity of the prismatic facets owing to the typical triangular patterns appearing on the images. The effect of the composition is investigated using two alloys with different carbon potentials and one containing VC and Cr3C2 as grain growth inhibitors. The interpretation of the images shows that in all cases, the same set of prismatic planes is favoured.

British Library Electronic Table of Contents (United Kingdom)

The microstructure and tensile properties of Ti-44Al-6V-3Nb-0.3Y (at.%) alloy after canned forging were investigated. SEM results showed that the TiAl pancake exhibits inhomogeneous microstructure, which can be ascribed to the temperature drop and friction between billet and outer pack during forging, as well as the intrinsic anisotropy of lamellar colony. By means of TEM observation and EBSD analysis, the microstructure in the dominant area of the pancake was further characterized. This deformation area consists of 87.7% content of g grains plus some refined lamellar colonies and the rest of B2 grains. The grain size ranges between 1mm and 8.5mm. High-angle boundaries dominate the deformation microstructure, several substructures and twins are observed as well. Additionally, current forge...

International Nuclear Information System (INIS)

High temperature deformation behaviour of an experimental Beta-titanium alloy Ti-10V has been studied in the temperature range 800 to 945 degree C by using the method of crosshead speed cycling. Although subgrain formation was observed but the alloy did not exhibit superplastic behaviour in the entire temperature range studied. A very large initial grain size and elongation of grains during the deformation are considered the main factors responsible for absence of superplastic behaviour. The activation energy values for regions II and III of the ln sigma vs. ln small epsilon plots are close to the lower of the two activation energy values proposed together to describe self diffusion in beta-phase suggesting that the rate controlling mechanism is that for lattice diffusion rather then grain boundary diffusion. (author)

Energy Technology Data Exchange (ETDEWEB)

The distribution of /sup 35/S-sulfate and /sup 3/H-glucosamine in the angular region of the hamster was studied by light and electron microscopic autoradiography following intraperitoneal injection of these compounds to hamsters. Exposed silver grains of /sup 35/S-sulfate were concentrated in the trabecular meshwork, sclera, and cornea, and grains of /sup 3/H-glucosamine were localized in the trabecular region. The radioactivity of both isotopes was observed in the Golgi apparatuses of the endothelial cells of the angular aqueous plexus and the trabecular meshwork. The grains were noted over the entire cytoplasm, except for the nucleus, and then were incorporated into the amorphous substance and collagen fibers in the region adjacent to the angular aqueous sinus. These results suggest that endothelial cells in the angular region synthesize and secrete the sulfated glycosaminoglycans and hyaluronic acid.

International Nuclear Information System (INIS)

Densification of Y_2O_3 by HIP was investigated in the range 1250"0C-1550"0C at a pressure of 150 MPa. Runs were made in metallic capsules with 200 g of powder. The powder under investigation is 99.9% purity, supplied by RHONE-POULENC. The study reveals the importance of residual gases in the HIP technique of powder densification. The density of the final product is in the range 93% to 100% of theoretical density depending on pretreatment (or outgassing) of the powder. Residual gases have been identified. Final products have been characterized by microscopy (grain size, porosity, microhardness). Porosity and grain size depend on pretreatment conditions. In particular a 1200"0C pretreatment results in zero porosity and significant decrease of grain size. 4 tables, 11 figs, 16 refs.

Energy Technology Data Exchange (ETDEWEB)

Car weight corresponds directly to fuel consumption and driving performance. So in order to improve the fuel efficiency and performance of a car the weight has to be reduced. Magnesium as a light metal offers a wide range of weight saving opportunities, especially Magnesium wrought alloys with their improved mechanical properties have a high potential for structural applications. Mechanical properties in terms of their quality and anisotropy are dependent on the microstructure of the material and can be characterized by their degree of inhomogeneity, their grain size distribution and their crystallographic texture. Therefore the orientation distribution of grains, the grain size, its size distribution, the chemical composition (precipitates) itself influence the mechanical parameters and their anisotropy. In this presentation first results of mechanical anisotropy are given: differences in yield stress, r-values and their ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical dissolution behaviour of armco-iron and of the steels C15, C45, C60 and 100Cr6 in concentrated sodium chloride media has been investigated. Anodic metal dissolution experiments have been carried out using the flow channel cell (parallel plate reactor), the rotating cylinder electrode (RCE) and the capillary cell. The microstructure of the steel has been varied through variation of carbon content and heat treatment (e.g. soft annealed with globular carbides or pearlitic). Current-efficiency values have been obtained by gravimetric measurements in the current-density range from i=5 to 60 A/cm{sup 2}. For the soft annealed steels, the divalent ferrite dissolution in combination with electroless cementite removal dominates. For the pearlitic steels, the occurrence of oxygen evolution electronically conductive metal carbides or trivalent ferrite dissolution, depending on the current ...

UK PubMed Central (United Kingdom)

A monoclonal antibody raised against carboxyl-linked IAA was used in Western blot analysis of storage proteins from kernels of Avena sativa, Pennisetum americanum, Sorghum bicolor,...Full Text Available

UK PubMed Central (United Kingdom)

The rapid global loss of natural habitats and biodiversity, and limited resources, place a premium on maximizing the expected benefits of conservation actions. The scarcity of information on the fine-grained...Full Text Available

UK PubMed Central (United Kingdom)

During reproduction in flowering plants, pollen grains form a tube that grows in a polarized fashion through the female tissues to eventually fertilize the egg cell. These highly polarized pollen tubes...Full Text Available

International Nuclear Information System (INIS)

Praseodymium-doped Bi_4Ti_3O_1_2 (BIT) with various compositions of dopant, Pr (x = 0.5, 0.6, 0.7, 0.8) in Bi_4_-_xPr_xTi_3O_1_2 (BPT) were synthesized using a low temperature wet chemical technique. Powders calcined at 800 deg. C exhibit a single phase polycrystalline perovskite bismuth-layered structure. Randomly oriented plate-like structures were observed under Scanning Electron Microscope (SEM). A small amount of Pr doping (x = 0.5) resulted in dramatically reduced of grain size from 2 #mu#m to less than 50 nm in which Pr plays the role as a grain growth inhibitor. However, by increasing the composition of Pr, bigger grain size of up to 1 #mu#m was observed for x = 0.8 that was caused by diffusion of Pr in the perovskite structure. Dielectric properties showed that dielectric permittivity decreased with the addition of x = 0.50, and increasing with further addition of Pr. Dissipation factor (tan #delta#) followed the ...

Energy Technology Data Exchange (ETDEWEB)

Aerospace gas turbine disks operate in an environment of relatively high stresses caused by centrifugal forces and elevated temperatures. These severe conditions necessitate the need for materials with high temperature strength and good low cycle fatigue resistance. One class of alloys used for this task is the nickel base superalloys, out of which, IN 718 is the most widely used in the aerospace industry. The properties of IN 718 are attributed to the combined effects of the chemistry, heat treatment, and microstructure. The chemistry is tailored not only for solid solution strengthening but also for precipitation hardening developed during heat treatment, which combined with a fine grained microstructure lead to excellent mechanical properties such as low cycle fatigue resistance and elevated temperature strength. The properties of a gas turbine disk are sensitive to the microstructure, in particular the grain size, which is dependent on the ...

British Library Electronic Table of Contents (United Kingdom)

This study examined the oxygen permeation behavior of Ce0.9Gd0.1O2-d (Gadolinium-Doped Ceria, GDC)/Ba0.5Sr0.5Co0.8Fe0.2O3-d (BSCF) composite membranes fabricated using a conventional sintering technique. GDC/BSCF composite membranes with a relative density >95% could be obtained when a green compact of BSCF and GDC was sintered at 1150^oC for 5h. It appears that GDC serves as a grain growth inhibitor because the average grain size of the composite decreased with increasing GDC content. The oxygen permeability of the BSCF and GDC/BSCF composite membranes strongly depends on the grain size and membrane thickness. The addition of GDC to BSCF resulted in a small grain size, low thermal expansion coefficient and high hardness. However, it is believed that oxygen permeation was blocked by GDC, a...

Science.gov (United States)

During Phase II multi-junction solar cell will be grown on the large grain thin film produced during Phase I on flexible/low cost metal foil substrate. ...

Energy Technology Data Exchange (ETDEWEB)

The effects of gate and drain bias stresses on thin film transistors fabricated in polysilicon films crystallized using the advanced sequential lateral solidification excimer laser annealing (SLS ELA) process, which yields very elongated polysilicon grains and allows the fabrication of TFTs without grain boundary barriers to current flow, are investigated as a function of the active layer thickness and of the TFT orientation relative to the grains. The application of hot carrier stress, with a condition of V{sub GS} = V{sub DS}/2, was determined to induce threshold voltage, subthreshold swing and transconductance degradation for TFTs in thicker polysilicon films and the associated stress-induced increase in the active layer trap density was evaluated. However, this device degradation was drastically reduced for TFTs fabricated in ultra-thin films. Furthermore, the application of the same stress condition to TFTs oriented ...

British Library Electronic Table of Contents (United Kingdom)

The nanocomposite WC-Co powders were prepared through planetary ball milling method. Effects of grain growth inhibitor addition and the vacuum sintering parameters on the microstructure and properties of ultrafine WC-10Co cemented carbides were investigated using X-ray diffractometer, scanning electron microscope and mechanical property tester. The results show that VC and NbC additions can refine the WC grains, decrease the volume fraction of Co3W3C phase in ultrafine WC-10Co cemented carbides, and increase the hardness and fracture toughness of the base alloys. After sintering for 60 min at 1400 degreeC, the average grain size and hardness of ultrafine-grained WC-10Co-1VC cemented carbide are 470 nm and HRA 91.5, respectively. The fracture toughness of cemented carbide WC-10Co-1NbC alloy...

UK PubMed Central (United Kingdom)

Food-deprived pigeons were presented with a row of four response keys situated above a grain hopper aperture. At the start of a trial, three of four keys were randomly selected and illuminated white...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Niobium carbide can be used to inhibit WC grain growth in hardmetal. The performance of a NbC powder produced at low temperature by solid-gas reaction (an experimental powder) as WC grain growth inhibitor is compared with that of a commercial NbC powder. It is verified that NbC effectively inhibits heterogeneous WC coarsening. This results in an increase in hardness. The commercial and experimental NbC powders exhibit a comparable performance in inhibiting the WC grain coarsening, in spite of a significant difference in particle size and shape. The commercial NbC powder is very fine while the experimental one is coarse and porous, but its crystallites are finer than those of the commercial product. The milling procedure used to prepare the alloys is able to reduce the particle size of the experimental NbC, and thus guarantee a dispersion of the particles with a quality level comparable to that found for the alloy prepared ...

British Library Electronic Table of Contents (United Kingdom)

Rare-earth oxides are doped into ZnO varistors as grain growth inhibitors for increasing the varistors' voltage gradients. However, their leakage currents become large and their nonlinear coefficients decrease at the same time. The reasonable explanation for such a phenomenon has not yet been available. In this paper, the temperature dependences of varistor samples' leakage currents are investigated, which reveal that the increased leakage currents of ZnO varistors with Y2O3 doping are mainly due to the bypass paths through the intergranular materials at grain corners.

CERN Document Server

Motivated by the numerical investigations of Laval, Dubrulle & Nazarenko (1999), we develop a quasilinear theory of the 2D Euler equation and derive an integro-differential equation for the evolution of the coarse-grained vorticity. This equation respects all the invariance properties of the Euler equation and conserves angular momentum in a circular domain and linear impulse in a channel (as well as in an infinite domain). The explicit energy is not rigorously conserved as it is partly transfered into fine-grained fluctuations but the total energy is conserved. We prove a H-theorem for the Fermi-Dirac entropy and make the connection with statistical theories of 2D turbulence.

Science.gov (United States)

Deformation experiments performed in-situ in the transmission electron microscope have led to an increased understanding of dislocation dynamics. To illustrate the capability of this technique two examples will be presented. In the first example, the processes of work hardening in Mo at room temperature will be presented. These studies have improved our understanding of dislocation mobility, dislocation generation, and dislocation-obstacle interactions. In the second example, the interaction of matrix dislocations with grain boundaries will be described. From such studies predictive criteria for slip transfer through grain boundaries have been developed.

International Nuclear Information System (INIS)

In a program to develop a metastable beta alloy with improved fracture toughness, it was found that the tensile ductility of the alloy Ti-8 Mo-4.5 Cr-2.5 Al was strongly dependent on both processing history and annealing temperature. Evaluation of the microfracture mode of tensile samples by scanning electron microscope and metallographic techniques showed that the presence of a continuous grain boundary alpha is the most significant parameter controlling the ductility and is highly detrimental. It is concluded that, for optimum processing, the material must be worked prior to aging to avoid this grain boundary phase.

Science.gov (United States)

The critical currents of A-15 phase Nb(,3)Sn, V(,3)Si, Nb(,3)Ge, V(,3)Ga, and Nb-Sn with a few at.% Ga and Al(,2)O(,3) have been measured at temperatures up to T(,c) and in magnetic fields up to 8T to study fundamental flux pinning interactions as a function of defect size and density. The samples are electron beam evaporated films typically 2 (mu)m thick. Their particular usefulness for this study is that they span the clean to dirty limits and their normal state resistivity and grain size can be controlled by deposition parameters. The grain boundaries are the defects most responsible for flux pinning. The electron scattering mechanism is based on the local change in the coherence length due to increased conduction electron scattering and is chosen from among several possible mechanisms to calculate the elementary pinning force at a grain boundary. A direct summation of the elementary pinning force of each boundary is ...

Energy Technology Data Exchange (ETDEWEB)

The wear behaviour of 722M24 (En40B) steel plasma nitrided at high temperatures for long durations was investigated. Under dry sliding and abrasive-containing lubricated conditions, the wear characteristics of the steel were studied as a function of load, time and white layer thickness. The white layer and the wear debris were characterized by X-ray diffraction. The topography of the wear surface was examined in a scanning electron microscope. The plasma nitriding process was carried out using a 20 kW plasma processing unit in cracked ammonia atmosphere. Treatment times of up to 100 h were employed with temperatures of 550, 570 and 590 C. Wear tests were performed with plasma nitrided AMS 6472 as the counterface material. The tests under abrasive-containing lubricated conditions were carried out with 10% carborundum powder 10 [mu]m in size in SAE-30 machine oil. The wear resistance of the steel was improved by plasma ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes an investigation of electrodeposited Zn-14% Ni and aluminium-based SermeTel 1140/962 coatings as possible replacements for cadmium. Slow strain rate tests were performed to measure the extent of direct hydrogen embrittlement of a high strength steel substrate as a result of the coating process and of hydrogen re-embrittlement caused by coating corrosion. The level of re-embrittlement was shown to depend on both the electrochemical potential of the coating and its barrier properties. Zn-14% Ni coatings caused the most re-embrittlement as they had the most active potential and contained through-thickness defects which left the steel exposed to hydrogen uptake. The microstructure of the high strength steel was also shown to be an important factor affecting the extent of embrittlement. AerMet 100 steel was more resistant than 300M steel and this was attributed to ...

International Nuclear Information System (INIS)

The photon rupture method, by which oxide film and metal are removed by focused pulsed Nd-YAG laser beam irradiation, was applied to form artificial micro-pits in Zn-5 mass% Al alloy-coated steel. The zinc alloy-coated layer was removed by pulsed laser irradiation treatment for about one second in a neutral buffer solution with NaCl. The rest potential transient with the laser treatment was measured. In the early stage of the laser treatment the rest potential of zinc alloy-coated steel changed to the negative direction immediately after every irradiation of a laser pulse and then returned to the previous value. However, after the steel substrate was exposed to the solution, the rest potential moved to the positive direction immediately after every irradiation of a laser pulse and then returned to the previous value. The amplitude and duration of the potential change after the laser irradiation increased with repetition of ...

International Nuclear Information System (INIS)

Previous corrosion studies identified the materials Hastelloy C4, Ti 99.8-Pd, and carbon steels as promising for the manufacture of long-lived high-level waste containers that could act as an engineered barrier in a rock-salt repository. Here, the efficiency of the corrosion-resistant concept using surface-welded Hastelloy C4 as corrosion protection of carbon steel containers is compared with the corrosion-allowance concept using unalloyed or low-alloyed steels. The materials are examined in three disposal relevant brines (two rich in MgCl_2, one rich in NaCl) at 150 C. The results indicate that welded Hastelloy C4 is highly resistant to corrosion in the NaCl-rich brine. In the presence of sulfides or MgCl_2-rich brines, however, severe pitting corrosion occurs. The three steels investigated are resistant to pitting corrosion in all brines, and their general corrosion rates imply corrosion allowances ...

International Nuclear Information System (INIS)

The interaction of Np(V), Pu(VI) and Tc(VII) with metal reductants Zn, Cr, Sn and their alloys was investigated in 0.5-4 mol l"-"1 NaOH solutions in static and dynamic conditions (by filtration of solutions through the column filled with grains of metal). In this paper, it was found that the reduction and succeeding precipitation hydroxides of these elements, on the surface of metal grains from 0.5 to 4 mol l"-"1 NaOH solutions, gives a decontamination factor (DF) from 1.1 to 67. The best result was achieved for Pu (DF=67) on Cr grains after 2.5 h contact at 60 C with 0.5 mol l"-"1 NaOH solution containing Pu(VI). Increasing the NaOH concentration, and the addition of chromate ions and complex-forming agents to alkaline solution results in a decrease of the decontamination factor (DF). A better result for Np sorption from 1 mol l"-"1 NaOH solutions was achieved after longer contact, than for Pu, with Cr and Zn ...

Energy Technology Data Exchange (ETDEWEB)

Inhibition efficiency of some water-soluble hydrazones for C-steel corrosion in hydrochloric acid has been tested by weight loss, polarisation measurements and open circuit technique. The inhibition effect was attributed to the adsorption of the additives on the C-steel surface as supported by adsorption measurements at Pt electrode using cyclic voltammetry. Electrochemical measurements indicated that all the additives behave as cathodic-type inhibitors. The data obtained fit well to both the Temkin adsorption isotherm and the kinetic-thermodynamic model. The inhibition behaviour and its order were explained with the help of the proposed skeletal representation.

International Nuclear Information System (INIS)

The low alloy steels were nitrided in the plasma atmosphere generated by using hollow cathode discharge. For comparison, specimens of 40 Cr steel were in two different potential states. One kind is isolated from cathode and anode between them the discharge was created. The other kind is placed on the plate which is connected to the cathode. The nitriding was carried out at different temperatures. The surface morphology, phase of compound layers and microhardness profiles were analyzed. The optical microscopy observation and X-ray diffraction showed that the compound layers were formed in all experiments. The results of the nitriding treatment are weakly dependent on the potentials applied on the specimens.

Energy Technology Data Exchange (ETDEWEB)

Once again residual austenite as one component of the microstructure of steels is the basis for discussion among experts. Very often the phenomen of the stabilisation of residual austenite is the focus of interest. In this paper the influence of ageing on residual austenite transformations is discussed, with ageing taking place in a temperature range between ambient and M/sub s/-temperature after quenching from different austenitizing temperatures by means of subzero refrigeration. Results which are typical for 100Cr6 steel are presented and discussed.

Energy Technology Data Exchange (ETDEWEB)

Voestalpine AG (Linz, Austria) produces heavy steel for steam turbines, compressors for the promotion of oil and gas as well as for the chemical industry, mechanical engineering and for the offshore technology. A weight range between 1 and 200 tons can be covered. The author of the contribution under consideration is limited to characteristics which have to be managed by a large steel foundry within the range of the steam power plants. This is described on the basis of produced steam turbines for power stations in the highest performance segment (1,600 MW).

International Nuclear Information System (INIS)

This paper deals with the pitting corrosion of evaporators in the liquid - radwaste system of nuclear power stations. Corrosion testrs were conducted by the anodic polalization of specimen in the chloride solution. (1) The initiation of the pitting in SUS 304, SUS 316 stainless steels was inhibited by addition of NaOH and H_3BO_3, however, these addition had no effect on the pitting propagation. (2) Inconel 625 had the resitivity against the pitting initiation superior to that of stainless steels, but this was not necessarily in the case of the pitting propagation. (3) It is noticed for pitting prevention that the environmental and material effect on the pitting initiation differed from that on the pitting propagation. (author).

Energy Technology Data Exchange (ETDEWEB)

The effect of aging on the microstructure and tensile properties of a type 316LN stainless steel/Alloy 800 joint, welded with 16-8-2 stainless steel consumable, has been studied to characterize and evaluate the joint for long-term elevated temperature service. The joint was subjected to accelerated againg heat treatments at 873 K up to 5000 h to simulate long-term service exposures. Analysis of the results from this investigation shows that this joint has adequate stability of microstructure and tensile properties even after prolonged exposure at elevated temperatures. (orig.)

Science.gov (United States)

Three bonding agents were evaluated to determine which were most effective in enhancing the bond of resin composite to stainless steel. A light-activated resin composite was bonded to a total of 60 stainless steel specimens using Panavia, Cover-Up, or Silicoating. Tensile bond strength measurements revealed that all three agents provide a satisfactory means of increasing adherence of the esthetic veneer without decreasing bonding through thermocycling of the specimens. Panavia and Cover-Up were significantly more effective than Silicoating and appear to be easier to use. PMID:8297460

Science.gov (United States)

The Asarco-Mission complex (image left) is an active producer of copper and molybdenum (important in making steel and other metal alloys), ...

British Library Electronic Table of Contents (United Kingdom)

Irradiation of EP-823 (16Cr12MoWsiVNbB) ferritic-martensitic steel with 7-MeV Ni++ ions and with 30- and 70-keV He+ ions at a temperature of 500?C was followed by an increase in the microhardness, which was due to both radiation point defects and changes in the phase composition and the dislocation structure of the steel. It was found that the dependence of the largest relative increase in the microhardness on the concentration of radiation-induced point defects in the near-surface region of the steel under irradiation with different ions correlated with an analogous dependence of the surface segregation of silicon and chromium.

Science.gov (United States)

... 36 7 Corrugated Steel Pipe Concept Layout--Elevation ..... 37 viii ... revetment. 3. Land Use ... Corner modules and capping blocks are available. ...

UK PubMed Central (United Kingdom)

A survey was carried out in a steel foundry in Brisbane to evaluate the nature and frequency of respiratory symptoms and to assess ventilatory function. The foundry used many moulding processes including...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In this article a production method of a magnetorheological suspension composed with silicon steel particles of size 0.1-0.15 mm and 4% silicon content is described. Steel particles were dispersed in a conducting carrier of a by mixture of graphite particles with size 2-5 {mu}m and cedar wood oil. The filling factor of the suspension with the silicon steel particles and with graphite particles amounted to 0.25-0.40. Samples of this suspension were placed in a rectangular vessel with electrodes and used for the investigation of the Hall effect in magnetic field with induction 0-8 T, generated by Bitter-type magnet. A non-linear dependence of Hall voltage on the induction of the applied magnetic field and a hysteresis loop of this voltage in the shape of inclined digit eight were found. The causes of the observed effects is the ordering of silicon steel particles and graphite particles along the side of ...

British Library Electronic Table of Contents (United Kingdom)

On the basis of a numerical model, the temperature and liquid fraction of spray-formed H13 tool steel are calculated as a function of time. Results show that a preheated substrate at the appropriate temperature can lead to very low porosity by increasing the liquid fraction in the deposited steel. The calculated cooling rate can lead to a microstructure consisting of martensite, lower bainite, retained austenite, and proeutectoid carbides in as-spray-formed material. In the temperature range between the solidus and liquidus temperatures, the calculated temperature of the spray-formed material increases with increasing substrate preheat temperature, resulting in a very low porosity by increasing the liquid fraction of the deposited steel. In the temperature region where austenite decomposit...