International Nuclear Information System (INIS)

Air flow rates and carbon dioxide concentrations of air entering and exiting eight H-Area waste tanks were monitored for a period of one year. The average instanteous concentration of carbon dioxide in air is within the range reported offsite, and therefore is not affect by operation of the coal-fired power plant adjacent to the tank farm. Waste solutions in each of the tanks were observed to be continuously absorbing carbon dioxide. The rate of absorption of carbon dioxide decreased linearly with the pH of the solution. Personnel exposure associated with the routine sampling and analysis of radioactive wastes stored at SRP to determine the levels of corrosion inhibitors in solution could be reduced by monitoring the absorption of carbon dioxide and using the relationship between pH and carbon dioxide absorption to determine the free hydroxide concentration in ...

Energy Technology Data Exchange (ETDEWEB)

Six safety initiatives have been identified for accelerating the resolution of waste tank safety issues and closure of unreviewed safety questions. Safety Initiative 5 is to reduce safety and environmental risk from tank leaks. Item d of Safety Initiative 5 is to complete corrosion studies of single-shell tanks to determine failure mechanisms and corrosion control options to minimize further degradation by June 1994. This report has been prepared to fulfill Safety Initiative 5, Item d. The corrosion mechanisms that apply to Hanford Site single-shell tanks are stress corrosion cracking, pitting/crevice corrosion, uniform corrosion, hydrogen embrittlement, and microbiologically influenced corrosion. The corrosion data relevant to the ...

Science.gov (United States)

A corrosion-testing program has been initiated in Purex and Redox storage tnnks to obtain corrosion data on carbon steel and three associated materials in neutralized process wastes. (C.W.H.)

Energy Technology Data Exchange (ETDEWEB)

SRS high-level radioactive waste tanks will not experience erosion corrosion to any significant degree during slurry pump operations. Erosion corrosion in carbon steel structures at reported pump discharge velocities is dominated by electrochemical (corrosion) processes. Interruption of those processes, as by the addition of corrosion inhibitors, sharply reduces the rate of metal loss from erosion corrosion. The well-inhibited SRS waste tanks have a near-zero general corrosion rate, and therefore will be essentially immune to erosion corrosion. The experimental data on carbon steel erosion corrosion most relevant to SRS operations was obtained at the Hanford Site on simulated Purex waste. A metal loss rate of 2.4 mils per year was measured at a temperature of 102 C and a slurry ...

Science.gov (United States)

... Title : ON-LINE MONITORING OF FLUE GAS DESULFURIZATION SCRUBBER CORROSION WITH ELECTROCHEMICAL TECHNIQUES. ...

Energy Technology Data Exchange (ETDEWEB)

Plans for the disposal of radioactive liquid and solid wastes presently stored in double-shell tanks at the Hanford Site call for retrieval and processing of the waste to create forms suitable for permanent disposal. Waste will be retrieved from a tank using a submerged slurry pump in conjunction with one or more rotating slurry jet mixer pumps. Pacific Northwest Laboratory (PNL) has conducted tests using simulated waste slurries to assess the effects of a impinging slurry jet on the corrosion rate of the tank wall and floor, an action that could potentially compromise the tank`s structural integrity. Corrosion processes were investigated on a laboratory scale with a simulated neutralized cladding removal waste (NCRW) slurry and in a subsequent test with simulated neutralized current acid waste (NCAW) slurry. The test slurries simulated the actual NCRW and NCAW ...

Energy Technology Data Exchange (ETDEWEB)

Plans for the disposal of radioactive liquid and solid wastes presently stored in double-shell tanks at the Hanford Site call for retrieval and processing of the waste to create forms suitable for permanent disposal. Waste will be retrieved from a tank using a submerged slurry pump in conjunction with one or more rotating slurry jet mixer pumps. Pacific Northwest Laboratory (PNL) has conducted tests using simulated waste slurries to assess the effects of a impinging slurry jet on the corrosion rate of the tank wall and floor, an action that could potentially compromise the tank's structural integrity. Corrosion processes were investigated on a laboratory scale with a simulated neutralized cladding removal waste (NCRW) slurry and in a subsequent test with simulated neutralized current acid waste (NCAW) slurry. The test slurries simulated the actual NCRW ...

CERN Document Server

Helium Tank point5

International Nuclear Information System (INIS)

Corrosion is a materials degradation process that engineering personnel in the pulp and paper industry have had to accept as unavoidable to some degree, due to aggressive processing conditions prevalent in paper mills. The increasing incidence of corrosion-related failures in plant and equipment has resulted in the introduction of new techniques to monitor corrosion rates, since many of the more traditional methods do not provide data that is either recent or accurate enough. Thin layer activation (TLA) is a new corrosion monitoring technique which has recently been employed to measure corrosion trends inside a continuous pulp digester. With TLA a surface is irradiated by a particle beam from a nuclear accelerator, causing it to be labelled with an accurate depth profile and low level radioactivity. By monitoring this ...

Energy Technology Data Exchange (ETDEWEB)

Gas transmission pipelines are susceptible to both internal (gas side) and external (soil side) corrosion attack. Internal corrosion is caused by the presence of salt laden moisture, CO{sub 2}, H{sub 2}S, and perhaps O{sub 2} in the natural gas. Internal corrosion usually manifests itself as general corrosion. However, the presence of chlorides in entrained water also can lead to pitting corrosion damage. The electrochemical noise technique can differentiate general from localized corrosion and provide estimates of corrosion rates without external perturbation of the corroding system. It is increasingly being applied to field and industrial installations for in situ corrosion monitoring. It has been used here to determine its suitability for monitoring internal and external ...

Energy Technology Data Exchange (ETDEWEB)

Aluminum is a principal element in alkaline nuclear sludge waste stored in high level waste (HLW) tanks at the Savannah River Site. The mass of sludge in a HLW tank can be reduced through the caustic leaching of aluminum, i.e. converting aluminum oxides (gibbsite) and oxide-hydroxides (boehmite) into soluble hydroxides through reaction with a hot caustic solution. The temperature limits outlined by the chemistry control program for HLW tanks to prevent caustic stress corrosion cracking (CSCC) in concentrated hydroxide solutions will potentially be exceeded during the sludge mass reduction (SMR) campaign. Corrosion testing was performed to determine the potential for CSCC under expected conditions. The experimental test program, developed based upon previous test results and expected conditions during the current SMR campaign, consisted of electrochemical and mechanical testing to ...

Energy Technology Data Exchange (ETDEWEB)

'Objective of this project is to develop and use Electrochemical Emission Spectroscopy (EES) and other electrochemical techniques as in situ tools for exploring corrosion mechanisms of iron and carbon steel in highly alkaline solutions and for continuously monitoring corrosion on structural materials in DOE liquid waste storage system. In particular, the author will explore the fundamental aspects of the passive behavior of pure iron since breakdown of passivity leads to localized corrosion. This report summarizes work after 1 year of a 3 year project.'

Energy Technology Data Exchange (ETDEWEB)

At the reference plant (Wolsung unit No. 1) a manual poison sampling system is provided to periodically sample gadolinium from each tank and analyze it in the laboratory to provide assurance that adequate poison concentration in each tank is maintained. The AECB required a continuous, on-line monitoring system. On Wolsung unit No. 2, process piping adapter and new instrument loops added to the Liquid Injection Shutdown System(LISS) which is part of SDS2. The new instrument loops continuously monitor SDS2 poison conductivity and initiate an alarm when the poison concentration is too low. 8 refs., 1 fig. (author).

International Nuclear Information System (INIS)

In order to prevent corrosion failures of machines and structures, it is desirable to know in advance when the corrosion damage will take place, and appropriate measures are needed to mitigate the damage. The corrosion predictions are needed both at development as well as operational stage of machines and structures. There are several forms of corrosion process through which varying degrees of damage can occur. Under certain conditions these corrosion processes at alone and in other set of conditions, several of these processes may occur simultaneously. For a certain type of machine elements and structures, such as gears, bearing, tubes, pipelines, containers, storage tanks etc., are particularly prone to pitting corrosion which is an insidious form of corrosion. The corrosion predictions are usually ...

International Nuclear Information System (INIS)

By varying different variables (potential, chloride content, surface pretreatment etc.) it is possible to show the effect of increasingly harsher corrosion conditions on passive-layer stability. These changes will not be detected by conventional methods e.g. measurement of passive current density, until a very late stage. Electrochemical noise measurement will allow the action of inhibitors to be detected in a rapid and effective manner. High-alloy steels and titanium claddings subjected to pitting corrosion in chloride-containing media demonstrate how to use this method for problem solutions and to open up new practical applications. The effect of mechanical stresses (natural, tensile) on the corrosion system can be detected by electrochemical noise which opens up new methods for crack corrosion studying and monitoring. (orig./DG).

Energy Technology Data Exchange (ETDEWEB)

Waste Management Area U (WMA U) includes the U Tank Farm, is currently regulated under RCRA interim-status regulations, and is scheduled for closure probably post-2030. Groundwater monitoring has been under an evaluation program that compared general contaminant indicator parameters from downgradient wells to background values established from upgradient wells. One of the indicator parameters, specific conductance, exceeded its background value in one downgradient well triggering a change from detection monitoring to a groundwater quality assessment program. The objective of the first phase of this assessment program is to determine whether the increased concentrations of nitrate and chromium in groundwater are from WMA U or from an upgradient source. Based on the results of the first determination, if WMA U is not the source of contamination, then the site will revert to detection monitoring. If WMA U ...

Energy Technology Data Exchange (ETDEWEB)

A large temperature differential (10K) thermal storage system in a small (4400 m{sup 2}) 8-storey office building is discussed and the monitoring results are analyzed in comparison with computer simulations. Requirements were a comfortable indoor environment and system cost effectiveness. Out of four potential system concepts, the Large Temperature Differential System was chosen. It comprises a flat-type thermal stratification heat storage tank in the under floor pit of the building as the heat source for a variable flow heat pump chiller. The heat sink is a set of serially connected air handling and fan coil units. The tank`s capacity is sized for one day operation and is made as large as possible to shift the electricity demand to night time. To avoid a large size and high cost, the water temperature differential was enlarged. The role of Tokyo Electric Power Company (TEPCO) was to develop the chiller and its control ...

Energy Technology Data Exchange (ETDEWEB)

During 17 years since the start of operation of the first commercial LWR in Japan, many LWRs have experienced various corrosion damages, but the causes of them were clarified, and the counter-measures were executed effectively in actual plants, as the results, the cause of corrosion damage decreased remarkably, and now, the high rate of operation has become to be maintained. In this paper, the major cases of corrosion damage experienced in LWRs in Japan and foreign countries, the causes of them and the countermeasures, the problems of hereafter and so on are described. The corrosion damage of metallic materials in the environment of LWRs occurs in the parts in contact with high temperature, high pressure water and steam, such as stainless steel piping in the primary cooling system of BWRs, and nickel alloy heating tubes of steam generators, carbon steel feed water piping and zirconium alloy fuel ...

Energy Technology Data Exchange (ETDEWEB)

Nomographs are presented that estimate the evaporation loss from external floating-roof tanks using tank diameter, type of seal, product vapor pressure, and wind velocity.

Energy Technology Data Exchange (ETDEWEB)

Vermicomposts as a biofertilizer can be a great option for pond manuring as they never cause any long term harm to the soil like chemical fertilizer. In this study vegetable and horticulture waste was used as an important media for vermiculture. Three separate cemented tanks (6 m{sup 3} each) were used in the system as control tank, vermicompost fertilized tank and inorganic fertilizer manured tank. Monoculture of fish was carried out with cat fish, Clarias batrachus. The produced earthworms were used as fish feed. Regular monitoring of water parameter was conducted in three different ponds. Specifically, the algal biomass variation was quite helpful in analysing the behavior of the ponds. NPK value of soil samples was analyzed intermittently to know the eutrophication level. Despite the hot summer temperature in northern part of India, which is not ideal for fish growth, we have ...

Science.gov (United States)

... TANK GUNS, GUNS, CHAMBERS, IGNITERS, INTERIOR BALLISTICS, INTERNAL PRESSURE, COMBUSTIBLE CARTRIDGE CASES, METALS. ...

Energy Technology Data Exchange (ETDEWEB)

The Alloy 800 tubes used in CANDU 6 steam generators have not experienced significant corrosion damage to date, which may be attributed to successful water chemistry control strategies. However, it is known that Alloy 800, like other steam generator (SG) tubing materials, is not immune to corrosion, especially pitting, under some plausible but off-specification operating scenarios. Electrochemical measurements provide information on corrosion susceptibility and rate, which are known to be a function of water chemistry. Using laboratory data in combination with chemistry monitoring and diagnostic software it is possible to assess the impact of plant operating conditions on SG tube corrosion for plant life management (PLIM). In this context, this paper discusses the results of electrochemical measurements made to elucidate the corrosion behaviour of Alloy 800 SG ...

Energy Technology Data Exchange (ETDEWEB)

Monitoring brine chemistry to determine the extent of potential adverse reactions has been simplified by the development of a field-brine test kit and a series of nomographs. Results of the kit analyses serve as input to the nomographs, which provide a graphic means of determining the scaling tendency (Saturation Index value) of a brine. Brines that do not tend to form scale may be corrosive. Saturation Index values were correlated with various processes using data from geopressured wells in the Gulf Coast area. Control of scale in surface equipment with chemical inhibitors has been successful. Numerous laboratory simulations of inhibitor squeeze operations were completed using core material with calcite present and absent. The corresponding wells were squeezed with phosphorous-containing inhibitors, and the flowback of brine was monitored for phosphorous concentrations vs time. A new procedure to measure the concentration ...

Energy Technology Data Exchange (ETDEWEB)

This report describes the results of a program conducted at the Pacific Northwest Laboratory (PNL) and Westinghouse Hanford Company (WHC) to identify alternative methods to measure the surface level in the waste tanks. This program examined commercially available devices for measuring the distance to a target. This is a continuation of a program started in FY93. In the first test sequence, tests were performed.on five devices to determine their applicability to measure the surface level in the waste tanks. The devices were the Enraf-Nonius{trademark} Model 872 Radar Gauge, the Enraf-Nonius{trademark} Model 854 Advanced Technology Gauge (ATG), the Stanley Tool Laser Measuring Device, the Robertshaw Inven-Tel{reg_sign} Precision Level Gauge, and the Micro Switch Model 942 Acoustic Sensor. In addition, discussions were held with several manufacturer representatives regarding other potential devices. The results of these tests were documented in a ...

Science.gov (United States)

The Interim Decay Storage tank (IDS) will be located in a concrete cell in the FFTF reactor building. The tank will have capacity to store 112 driver fuel assemblies and 10 test assemblies in sodium. A criticality safety analysis for the design of the IDS tank was performed. From the analysis, it is concluded that under normal operating conditions and minor abnormal conditions that might shift the fuel, the IDS tank will remain adequately subcritical. (auth)

International Nuclear Information System (INIS)

The feasibility of developing a fusion power monitor based on a fluid activation detector is considered here. The activation fluid may be either a liquid or a gas and its composition can be selected from a number of candidate materials to provide desired activation and decay characterisitcs. Performance calculations indicate that ordinary water would be a nearly ideal activation fluid. The "1"6O(n,p)"1"6N reaction has a threshold at about 10 MeV and a cross section energy dependence giving it a predominant response for unmoderated D-T fusion neutrons. Adequate activation can be obtained at moderate flow rates for remote counting away from the high radiation area of the reactor. The 7.16 sec half-life of "1"6N is ideal for remote counting with subsequent decay in a small hold-up tank to eliminate activity build-up in the recycled water.

International Nuclear Information System (INIS)

The decontamination of the dissolution tank from spent fuel reprocessing out-ling device is studied, by using FL-AP decontamination agent. The decontamination factor per step is 2.2, 2.4, respectively for #alpha#, #beta# activities. After dissecting the tank, residual contamination in inner surface of the tank was found to be non-uniform. The exact original contamination value of the tank surface could be approximated by calculating the total amounts of radionuclide distributed on the hanging specimens, the dissecting specimen, and radioactive level in waste decontamination agent. Therefore, it can be concluded that the hanging specimens method is feasible for measuring the decontamination factor of spent fuel dissolution tank. (authors)

Energy Technology Data Exchange (ETDEWEB)

Electrochemical noise generated during stress corrosion cracking (SCC) of type 304 stainless steel (UNS S30400) and {alpha}-brass were studied. Noise patterns showed common characteristics (i.e., a quick drop and slow recovery of the potential). The quick drop corresponded to the initiation of localized events where fresh metal was exposed. The slow recovery corresponded to the repassivation process of the exposed bare metal. The potential drop rate and recovery rate were almost constant during the SCC process for a given SCC system. For random noise, rates of potential rise and drop were similar. Frequency of the noise generated during SCC increased with an increase in applied stress. SCC initiation could be monitored and determined according to noise characteristics and distribution. Since the shift of background potentials had an obvious influence on characteristics of power spectrum density (PSD), the direct current (DC) component should be ...

International Nuclear Information System (INIS)

The objectives of the project were to develop operational techniques for promoting contaminant hideout return from tube support crevices and to identify the effect of chemical inhibitor application on corrodent transport. The implementation of routine procedures for promoting the return of sequestered corrodents could retard the progression of denting or other corrosion processes and improve steam generator availability. Tests also quantified the effect of inhibitor application on crevice hideout and hideout return processes, with the intention of developing a better understanding of the inhibition mechanism. By carefully monitoring the hideout and hideout return inventories, the program also has provided the opportunity to study steam generator concentration processes in general.

Energy Technology Data Exchange (ETDEWEB)

Maximum metal loss rate of Alloy 800 coupons was about 0.5 mil/year and occurred at the maximum temperature of 600/sup 0/C. Significantly greater oxide penetration into the alloy occurred in unabraded as-received tubing. Since the corrosion rate of unabraded tubing was less temperature sensitive than polished coupons, and attained a maximum value at temperatures in the range of 550 to 565/sup 0/C, a value of 1 mil/year should be used as the corrosion rate for design purposes. Because daily thermal cycling is inherent in solar central receiver operation, oxidation and chromium depletion rates can be expected to increase if surface oxide layers spall. The oxide layers formed on Alloy 800 appeared to be adherent, and adherence will benefit further from growth-derived compressive stresses in oxide layers on the salt-exposed inner diameter of receiver tubes. Since the lower duty factor in diurnal solar service may offset the accelerated metal loss ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

A geothermal heat pump (GHP) system with three ground coils was installed in a residence in northern Idaho with a portion of the ground heat exchanger wrapped around the residential septic tank. The septic coil provided a significant portion of the heating for the residence over the heating season. There was no evidence of the septic tank freezing up or failing to properly function. Utilizing a septic tank as a heat source for GHP systems is feasible design option if the septic tank is used on a full-time basis. However, the tank should be surrounded on all sides by a large amount of soil and/or insulated from the ground surface to ensure that ground temperatures near the tank remain warm during the winter.

Science.gov (United States)

Specialized tests can be designed to study impingement-corrosion, erosion- corrosion, cathodic protection systems, cavitation and other velocity effects. ...

International Nuclear Information System (INIS)

A number of ion exchange materials are being evaluated as part of the Tank Waste Remediation System (TWRS) Pacific Northwest Laboratory (PNL) Pretreatment Project for the removal of "1"3"7Cs from aqueous tank wastes. Two of these materials are organic resins; a phenol-formaldehyde resin (Duolite CS-100) produced by Rohm and Haas Co. (Philadelphia, Pennsylvania) and a resorcinol-formaldehyde (RF) resin produced by Boulder Scientific Co. (Mead, Colorado). One of the key parameters in the assessment of the organic based ion exchange materials is its useful lifetime in the radioactive and chemical environment that will be encountered during waste processing. The focus of the work presented in this report is the radiation stability of the CS-100 and the RF resins. The scope of the testing included one test with a sample of the CS-100 resin and testing of two batches of the RF resin (BSC-187 and BSC-210). Samples of the exchangers were irradiated ...

Energy Technology Data Exchange (ETDEWEB)

Here we report a new method for measuring the heterogeneous chemistry of submicron organic aerosol particles using a continuous flow stirred tank reactor. This approach is designed to quantify the real time heterogeneous kinetics, using a relative rate method, under conditions of low oxidant concentration and long reaction times that more closely mimic the real atmosphere. A general analytical expression, which couples the aerosol chemistry with the flow dynamics in the chamber is developed and applied to the heterogeneous oxidation of squalane particles by hydroxyl radicals (OH) in the presence of O2. The particle phase reaction is monitored via photoionization aerosol mass spectrometry and yields a reactive uptake coefficient of 0.51+-0.10, using OH concentrations of 1-7x108 molec cdot cm-3 and reaction times of 1.5+-3 hours. This uptake coefficient is larger than that found for the reaction carried out under high OH concentrations (~;;1x1010 ...

Energy Technology Data Exchange (ETDEWEB)

Atomic Energy of Canada Limited (AECL) operates the Waste Treatment Centre (WTC) to treat and immobilize some of the low- level radioactive waste (LLRW) streams at the Chalk River Laboratories (CRL). The WTC at treats low- level radioactive liquid waste by removing the contaminants from the wastewater, concentrating them, and immobilizing them. The fundamental design concept for the WTC is to process the waste streams using forced circulation type liquid waste evaporation (LWE), to solidify the concentrates using thin film evaporator and to discharge the purified effluent into the Ottawa River following verification monitoring. The solidified product drums are stored in existing storage facilities in the CRL. The LWE was installed in the WTC to treat the LLRW. After about four (4) years of design, construction and cold commissioning, the active commissioning of the evaporator process using radioactive waste streams commenced in February 2000. The LWE has overcome ...

Energy Technology Data Exchange (ETDEWEB)

This paper describes the design and feasibility tests of a 570 mm bore 4 stroke low pressure (L.P.) dual fuel engine rated at 20.9 bar BMEP meant for the propulsion of LNG carriers. The basic design features which are to be in accordance with classification societies safety rules are described: individual electro hydraulic valves located in the air manifold ducts, pilot injection, monitoring system etc. The engine capability to burn variable liquid/gas fuel proportions have been investigated with diesel oil and heavy fuel and possible running zones are defined. This ensures the possibility of the engine to cope with the different boil off gas quantity emanating from the ship`s tank during her loaded - and ballast - journeys. With the very lean setting of this engine, no adverse influence of the high ash lube-oil additives were found during the tests. Further tests are necessary to confirm that possible more significant fouling of the combustion ...

Energy Technology Data Exchange (ETDEWEB)

The US Department of Energy (DOE) has millions of gallons of high level nuclear waste stored in underground tanks at Hanford, Washington and Savannah River, South Carolina. These tanks will eventually be emptied and decommissioned. This will leave a residue of sludge adhering to the interior tank surfaces that may contaminate nearby groundwaters with radionuclides and RCRA metals. Performance assessment (PA) calculations must be carried out prior to closing the tanks. This requires developing radionuclide release models from the sludges so that the PA calculations can be based on credible source terms. These efforts continued to be hindered by uncertainties regarding the actual nature of the tank contents and the distribution of radionuclides among the various phases. In particular, it is of vital importance to know what radionuclides are associated with solid sludge components. ...

CERN Document Server

Metals and alloy - Atmospheric corrosion testing

Energy Technology Data Exchange (ETDEWEB)

Although ultrasonic testing inspection technology and tools have improved significantly, there is still a need for more reliable detection, monitoring, and accurate sizing of crack-like and planar defects, complex corrosion damage, and detection of secondary features within deformed pipe. Ultrasonic two dimensional (2D) matrix phased array technology offers some unique advantages that make the technology promising for improving detection and sizing of pipeline flaws resulting from welding or from in-service damage. Ultrasonic modeling and simulation has been conducted to evaluate the detection and sizing capabilities of 2D matrix arrays for various pipeline inspection concepts. Simulations have been performed using both flexible and rigid array probes. Inspection concepts using rigid probes were evaluated for inspections from both the outside and inside pipe surfaces, while flexible probes were evaluated primarily for inspection from the ...

Energy Technology Data Exchange (ETDEWEB)

The very low-pressure expansion tank of the title invention is connected to the water in the central heating installation via a connecting pipe with a pump and valves on one side, and on the other side the tank is connected via a connecting pipe with valve to the tap water mains, so that the supply of water can be regulated automatically. Within the expansion tank contact with the outside air is not possible because of an air/water separating floater. By means of recording and control (also remote) of the contents of the expansion tank, the installation pressure and the quantity of supplied water from the expansion tank and the tap water mains, failures and water damage are prevented. 4 figs.

Energy Technology Data Exchange (ETDEWEB)

Thin passive layers of uranium nitride were formed by nitriding pure metallic uranium in non-equilibrium, low pressure radio-frequency plasma of nitrogen. Plasma nitriding at low substrate temperature of 230 C-250 C was found to cause the formation of adherent layers of uranium sesquinitride ({alpha}-U{sub 2}N{sub 3}) which provide a considerable protection against hydrogen attack. The characteristics of these passivation layers were determined by X-ray diffraction and Auger electron spectroscopy. The incipient hydriding kinetics of the plasma-treated samples were compared with those of untreated and nitrogen-ion implantation ones, utilizing a hot-stage microscope that was monitored continuously with a TV camera and videotape. (orig.)

Energy Technology Data Exchange (ETDEWEB)

Nomographs have been constructed to estimate the average evaporation loss from internal floating-roof tanks. Loss determined from the charts can be used to evaluate the economics of seal conversion and to reconcile refinery, petrochemical plant, and storage terminal losses. The losses represent average standing losses only. They do not cover losses associated with the movement of product into or out of the tank. The average standing evaporation loss from an internal floating-roof tank depends on: vapor pressure of the product; type and condition of roof seal; tank diameter; and type of fixed roof support. The nomographs can estimate evaporation loss for product true vapor pressures (TVP) ranging from 1.5 to 14 psia, the most commonly used seals for average and tight fit conditions, tank diameters ranging from 50 to 250 ft, welded and bolted designs, and both self-supporting and ...

International Nuclear Information System (INIS)

Object: To provide a tank, which can safely and reliably accommodate high temperature sodium containing radioactive substance in case of occurrence of an accident in a sodium system and thus prevent spread of contamination. Structure: A sodium drain duct inserted into a tank from above the tank is provided at the position of its lower end with a buffer means for preventing direct flow-down of sodium to a bottom plate. A means for preventing the discharge of radioactive substance to the cover gas is provided above the lower end of the sodium drain tube so as to surround the sodium drain tube. (Kamimura, M.).

Energy Technology Data Exchange (ETDEWEB)

PUREX high-level waste (HLW) is contained at the West Valley Demonstration Project (WVDP) in an underground carbon-steel storage tank. The HLW consists of a precipitated sludge and an alkaline supernate. This report describes the system that the WVDP has developed and implemented to resuspend and wash the HLW sludge from the tank. The report discusses Sludge Mobilization and Wash System (SMWS) equipment design, installation, and testing. The storage tank required modifications to accommodate the SMWS. These modifications are discussed as well.

Energy Technology Data Exchange (ETDEWEB)

The need for a Combustion and Melting Research Facility focused on the solution of glass manufacturing problems common to all segments of the glass industry was given high priority in the earliest version of the Glass Industry Technology Roadmap (Eisenhauer et al., 1997). Visteon Glass Systems and, later, PPG Industries proposed to meet this requirement, in partnership with the DOE/OIT Glass Program and Sandia National Laboratories, by designing and building a research furnace equipped with state-of-the-art diagnostics in the DOE Combustion Research Facility located at the Sandia site in Livermore, CA. Input on the configuration and objectives of the facility was sought from the entire industry by a variety of routes: (1) through a survey distributed to industry leaders by GMIC, (2) by conducting an open workshop following the OIT Glass Industry Project Review in September 1999, (3) from discussions with numerous glass engineers, scientists, and executives, and (4) during visits to ...

Energy Technology Data Exchange (ETDEWEB)

This document provides data on aerosol concentrations in tank headspaces, total mass of aerosols in the tank headspace, and mass of aerosols sent to the exhauster during rotary mode core sampling from November 1994 through June 1999. A decontamination factor for the RMCS exhauster filter housing is calculated based upon operational data and non-destructive assay.

Wastenet

Hexavalent chromium in corrosion preventive coating 64 ...To prevent corrosion of rims, weights can be provided with a coating. ...integrated clips brought up technical problems due to corrosion

Wastenet

... Corrosion Inhibitors Equipment on Environmental Expert Find and compare a variety of corrosion inhibitors equipment on the world's largest environmental industry portal. View ...

Energy Technology Data Exchange (ETDEWEB)

The corrosion behavior of steel in water from certain oil fields with various organic inhibitors was studied by applying potentiodynamic technique at pH 5.9. The inhibitors which were used include 2-methylbenzimidazole (I), 2-mercaptobenzimidazole (II), 2-mercapto-5-methylbenzimidazole (III), and 2-mercaptothiazole (IV). The inhibiting efficiency of the different additives was evaluated from their anodic and cathodic polarization curves at different temperatures. A comparative study of curve fitting procedures using the kinetic thermodynamic model and those utilizing well-known adsorption isotherms was undertaken. Three types of isotherms were used, Langmuir, Frumkin and Flory-Huggins isotherm. The results show that the kinetic-thermodynamic model and Flory-Huggins isotherms are more suitable to fit the data for the four inhibitors, at all applied temperatures. From the values of binding constants, K, the order of inhibitor efficiency is: III > IV > ...

International Nuclear Information System (INIS)

The effect of uniaxial tensile stress on intergranular corrosion (IGC) of AA2024-T3 was studied using the foil penetration technique. Standard ASTM G49 fixed-displacement jigs were modified to allow the use of sheet samples, which were then attached to an electrochemical cell as in the foil penetration setup. The time for IGC to penetrate samples of varying thickness was monitored. This method provides a new approach to bridge the gap between IGC and intergranular stress corrosion cracking (IGSCC). Samples with various orientations relative to the rolling direction were studied in 1.0 M NaCl at controlled anodic potentials. Potentiodynamic polarization measurements indicated that the two breakdown potentials typically observed for AA2024-T3 were lower for stressed samples than for unstressed samples, and the current at a given potential was higher. The penetration rate depended on potential and was higher for stressed ...

International Nuclear Information System (INIS)

The underground storage tanks at the Hanford Complex contain mixed wastes generated over many years from plutonium production and recovery processes. The chemical changes of the organic materials used in the extraction processes and disposed to the tanks have a direct bearing on several specific safety issues, including potential energy releases from these tanks. This paper will give details of a study that is directed towards elucidating thermal and radiological decomposition mechanisms and products of the organic contents of the tanks. The study is being conducted in two parts. The first part, an aging study, will determine kinetics and products of the degradation of a simulated waste subjected to #gamma#-radiation from an external source. Although the simulant will not contain radioactive elements, it will contain other representative inorganic compounds and the primary organic compounds thought to ...

CERN Document Server

Anodic protection

Science.gov (United States)

Scratch and Corrosion Resistance of an Aluminum Flange with an Electron Beam Modified Seal Edge

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

... FIELD CORROSION TESTS WERE MADE DURING THE VOYAGES OF THE SCIENTIFIC-RESEARCH SHIPS ACADEMICIAN VERNADSKII AND ...

International Nuclear Information System (INIS)

A historical overview of corrosion problems found in power plant condensers and mitigation procedures is presented. The paper is organized according to alloy type and failure mode. Alloys considered are copper-base alloys, stainless steels and titanium. Failure modes discussed include erosion-corrosion, sulfide attack, environmentally assisted cracking, galvanic corrosion, steam condensate corrosion, pitting corrosion, and dealloying. Mitigation procedures discussed include cathodic protection, ferrous ion injection, as well as tube cleaning and layup practices.

Energy Technology Data Exchange (ETDEWEB)

Corrosion failures in circuits of foreign NPPs are considered. According to American statistics there are more corrosion failures in two-circuit NPPs than in NPPs with one circuit. Steam generators mostly suffer from ''corrosion denting''. Lately pitting corrosion becomes a potentially serious problem. Steam generator vertical tubes are mainly subjected to this corrosion type. Attention is drawn to intercrystalline corrosion. The causes of corrosion are described. The problem of optimization of structural materials is discussed to reduce corrosion failures as well as other methods of decreasing corrosion failures. Organization of nondestructive testing, increased requirements to water and steam purity are of great importance.

Energy Technology Data Exchange (ETDEWEB)

A precise admixtures system is needed when using high-volume fly ash concrete as fresh concrete occasionally undergoes rapid slump loss after mixing, which can cause problems with casting, pumping and finishing of the concrete in hot weather. This paper provided details of a study conducted to implement high-volume fly ash concrete technology in India. Different families of admixtures were investigated to determine their water reduction capacities. A set-retarding admixture was used in some of the concrete mixtures in order to determine its efficacy. An Indian Portland cement was used to create a total of 22 different concrete mixtures. Four different fly ashes were used to replace portions of the concrete. The slump of the fresh concrete mixture was monitored for 2 to 3 hours. Unit weight and temperature of the concrete was measured. Specimens were cast in steel moulds in order to determine the compressive strength and unit weight of the hardened concrete. The ...

Science.gov (United States)

... to maintaining healthy terrapin populations in the Chesapeake. Biology and Monitoring of Diamondback Terrapins in the Chesapeake ... ...

Science.gov (United States)

Permeable reactive barriers (PRB) are a promising technology for the remediation of groundwater containing a range of organic and inorganic contaminants. Although there are number of different types of reactive barriers, some of the most important are constructed from granular zero valent iron (ZVI). One challenge in the large- scale, long-term implementation of PRBs is to monitor the change in barrier properties over time. For example, mineral precipitates can reduce the effectiveness of the barrier by either insulating the reaction surfaces of the ZVI particles and/or by filling the pore space in the barrier and thus reducing its hydraulic permeability. Previous research has shown that resistivity and induced polarization (IP) measurements are sensitive to corrosion and precipitation due to redox reactions between ions in solution and the ZVI mineral surface. New field studies, supported by additional laboratory studies appear to confirm ...

Energy Technology Data Exchange (ETDEWEB)

An independent chemical compatibility review of various wrapping and absorbent/padding materials was conducted to evaluate resistance to chemicals and constituents present in liquid waste from the Hanford underground tanks. These materials will be used to wrap long-length contaminated equipment when such equipment is removed from the tanks and prepared for transportation and subsequent disposal or storage. The materials studied were Cooley L18KU, Herculite, and Elephant Mat. The study concludes that these materials are appropriate for use in this application.

Science.gov (United States)

... Two types of combustible cartridge cases, post impregnated (PI) and beater additive (B/A) are available for the 120 mm tank gun system. ...

Science.gov (United States)

... INFANTRY PARTIPI ACT 278 DATA POINTS 60 48 ... Page 21. 29 TISE HISTOGRAN-CUN CURUE INFANTRY PARTIP2 EST 895 DATA POINTS ...

Science.gov (United States)

... ammunition is stored. Combustible cartridge cases could absorb moisture, swell, and not chamber properly. Additionally, moisture ...

Energy Technology Data Exchange (ETDEWEB)

The removal of paraffinic bottom accumulations from refinery storage tanks represents an increasingly costly area of petroleum storage management. Microorganisms can be used to reduce paraffinic bottoms by increasing the solubility of bottom material and by increasing the wax-carrying capacity of carrier oil used in the cleaning process. The economic savings of such treatments are considerable. The process is also intrinsically safer than alternative methods, as it reduces and even eliminates the need for personnel to enter the tank during the cleaning process. Both laboratory and field sample analyses can be used to document changes in tank material during the treatment process. These changes include increases in volatile content and changes in wax distribution. Several case histories illustrating these physical and chemical changes are presented along with the economics of treatment.

International Nuclear Information System (INIS)

The dynamic response of thin liquid storage tanks to earthquakes is a very complicated phenomenon, because it can be highly non linear. Among others, one can meet material and geometric non linearities of the tank shell leading eventually to static or dynamic buckling non linear behavior of anchor bolts, contact non-linearities due to the uplift of the tank base and to the unilateral character of the fluid pressure on the shell and high amplitude fluid oscillations. Moreover, linear or non linear soil structure interaction affects considerably the response of the fluid structure system under consideration. In this paper we focus attention on problems related only to the base uplift and anchors plastification. We study a tank similar to the Hualien project tank, but we neglect the soil structure interaction. The studied tank is representative of medium height to ...

Science.gov (United States)

Seriously, generally fish waste does drop, but quite slowly. But a good group of snails should still do a fine job of cleaning the tank. ...

Energy Technology Data Exchange (ETDEWEB)

Type 440C stainless steel is a high-C, high-Cr martensitic steel used in applications requiring high hardness and wear resistance in combination with moderate corrosion resistance. Typical applications include precision aerospace bearings and critical components in computer disk drives. The properties of passive films formed on 440C steel were investigated using advanced electrochemical techniques with a view to establishing a method to measure film stability directly in the passivation baths. Electrochemical measurements were sensitive to the passive film properties and were able to quantify the effect of cooling rate on passive film stability. The techniques used included linear polarization, AC impedance, small amplitude cyclic voltammetry, and coulostatic transient measurements. These provided results that exhibited excellent agreement with the AC impedance technique providing the most information about the interfacial reactions. It was found that the full ...

International Nuclear Information System (INIS)

Briefly described is knowledge of crevice corrosion, corrosion cracking and denting. In evaluating the corrosion resistance of steam generator materials it is necessary to distinguish corrosion problems caused by the primary coolant eide and by the secondary circuit side. At present tubes are manufactured of 7 austenitic alloys of a different chemical composition, and available information shows that views on their corrosion resistance differ. Greatest attention has been devoted to corrosion cracking in the presence of HaOH. Findings related to I-600, I-800, I-690 and AISI 316 are given. Corrodibility by sulfur-containing products is now being studied, namely the intercrystalline corrosion cracking caused by the presence of H_2S_4O_6. Knowledge gained in this respect is summed up. (J.P.).

Energy Technology Data Exchange (ETDEWEB)

Thermogalvanic corrosion of St3 steel in a temperature range from 25 to 50{degrees}C with a 3.84{degrees}C/cm gradient was studied in a neutral media flow. It is shown that the thermogalvanic effect on the pitting corrosion of water-cooled heat exchangers is decisive but dual. Depending on the composition of the cooling medium, thermogalvanic corrosion may either enhance (0.5 M NaCl) or inhibit (tap water) pitting corrosion.

Energy Technology Data Exchange (ETDEWEB)

Since first PWR in Japan started commercial operation in 1970, we have encountered the various modes of corrosion on primary and secondary side components. We have paid much efforts for resolving these corrosion problems, that is, investigating the causes of corrosion and establishing the countermeasures for these corrosion. We summarize these efforts in this article. (author)

Energy Technology Data Exchange (ETDEWEB)

In the present work, electrochemical measurements and corrosion tests in NaCl solutions were carried out to study the effect of aging treatments on pitting corrosion behavior in a 8090 alloy and its high purity Al-Li binary alloy analogue. The pitting corrosion characteristics and corrosion resistance of the 8090 alloy have been determined in relation to precipitation microstructures. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The most typical kinds of corrosion of brasses are selective corrosion (dezincification) and stress corrosion. Prevention against these kinds of corrosion lies in application of arsenic alloy addition and appropriate heat treatment removing internal stresses as well as in maintaining the arsenic and phosphorus contents on a proper level. The most typical corrosion of cupronickels is the local corrosion. Selective corrosion occurs less often and corrosion cracking caused by stress corrosion in sea water does not usually occur. Crevice corrosion is found especially in places of an heterogeneous oxidation of the surface under inorganic deposits or under bio-film. Common corrosive phenomena for brasses and cupronickels are the effects caused by sea water flow and ...

International Nuclear Information System (INIS)

Information is presented concerning solute concentration in a porous layer; solute concentration in a packed crevice; corrosion of a packed carbon steel crevice in NaCl-O"2 solutions; and effect of copper on corrosion in NaCl-O"2 solutions.

Science.gov (United States)

Carbon steel, copper, zinc and aluminium samples were exposed in different sizes with known ambient parameters in Gran Canaria Island and atmospheric corrosion was investigated. Weight-loss measurements used to determine corrosion damage were complemented...

Energy Technology Data Exchange (ETDEWEB)

Waste tank W-12 is a tank in the ORNL Low-Level Liquid Waste (LLLW) system that collected waste from Building 3525. Because of a leaking flange in the discharge line from W-12 to the evaporator service tank (W-22) and continual inleakage into the tank from an unknown source, W-12 was removed from service to comply with the Federal Facilities Agreement requirement. The initial response was to decontaminate the valve pit between tank W-12 and the evaporator service tank (W-22) to determine if personnel could enter the pit to attempt repair of the leaking flange. Preventing the spread of radioactive contamination from the pit to the environment and to other waste systems was of concern during the decontamination. The drain in the pit goes to the process waste system; therefore, if high-level liquid waste were generated during decontamination activities, it would ...

Energy Technology Data Exchange (ETDEWEB)

Operational Final Test Report for Integrated Systems, Project W-030 (Phase 2 test, RECIRC and HIGH-HEAT Modes). Project W-030 provides a ventilation upgrade for the four Aging Waste Facility tanks, including upgraded vapor space cooling and filtered venting of tanks AY101, Ay102, AZ101, AZ102.

Energy Technology Data Exchange (ETDEWEB)

This report is an Implementation Guide for Hanford Tanks Initiative C-106 heel retrieval contract management HNF-2511 to provide a set of uniform instructions for managing the two contractors selected. The primary objective is to produce the necessary deliverables and services for the HTI project within schedule and budget.

International Nuclear Information System (INIS)

A possibility of short-lived isotopes production in inter-tank section between the first and the second drift tube tanks (20.45 MeV) in INR linac is considered. At the initial stage the main efforts are concentrated on production of fluorine-18 used for positron emission tomography. The results of beam forming calculations, target heating calculations, equipment activation calculations as well as installation configuration and design are presented.

International Nuclear Information System (INIS)

Three different techniques for pitting corrosion potential measurement on austenitic stainless steel (Fe18Cr10Ni) were compared: conventional polarization method, a new Avesta electrochemical corrosion measurement cell and a scratch technique. Special attention was paid to the effects of crevice corrosion during pitting corrosion potential measurement and to their elimination. Development of a rapid test technique for reliable pitting corrosion potential determination was aimed at and resulted from comparison of the different techniques.

Energy Technology Data Exchange (ETDEWEB)

Superheater corrosion causes vast annual losses to the power companies. If the corrosion could be reliably predicted, new power plants could be designed accordingly, and knowledge of fuel selection and determination of process conditions could be utilized to minimize superheater corrosion. If relations between inputs and the output are poorly known, conventional models depending on corrosion theories will fail. A prediction model based on a neural network is capable of learning from errors and improving its performance as the amount of data increases. The neural network developed during this study predicts superheater corrosion with 80 % accuracy at early stage of the project. (orig.) 10 refs.

Energy Technology Data Exchange (ETDEWEB)

The rate of corrosion of hardened cement paste in solutions of nitric, hydrochloric, sulfuric, acetic and formic acids was compared. Corrosion in solutions of acetic and nitric acids with different concentrations was studied in more detail. The results made it possible to obtain the relationships expressing the influence of concentration and the time of action of acid solutions on the depth of corrosion. The rates of corrosion in nitric acid solutions during the first 3 years were about 2 to 4 times that in acetic acid solutions, depending on the concentration.

Energy Technology Data Exchange (ETDEWEB)

Carbon steel, copper, zinc and aluminium samples were exposed in different sizes with known ambient parameters in Gran Canaria Island and atmospheric corrosion was investigated. Weight-loss measurements used to determine corrosion damage were complemented with metallographic and XP S determination in order to characterize the structure and morphology of surface corrosion products. The ambient aggressiveness could be well evaluated from meteorological and pollution data. All atmospheric corrosion and environmental data were statistically processed for establishing general corrosion damage functions for carbon steel, copper, aluminium and zinc in terms of Gran Canaria extreme meteorological and pollution parameters. (Author)

UK PubMed Central (United Kingdom)

Monitoring describes the prospective supervision, observation, and testing of an ongoing process. The result of monitoring provides reassurance that the goal has been or will be achieved, or suggests...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The improvement in the functions of the viscous flow calculation method VEGA-SHIP around a ship and the expansion of application range were described as the numerical flow simulation in ship and ocean engineering and at the same time application examples to the ocean engineering by the general-purpose flow simulation code FLOW-3D handling the non-steady flow with a free surface were introduced as the numerical simulation regarding such products as a water gate and a dam. In the VEGA-SHIP, water surface was handled as a fixed wall so that wave could not be calculated. Therefore, an algorithm for calculating wave on the water surface was added to the VEGA-SHIP and a calculation method simultaneously considering the creation of wave around the ship and viscosity was developed. The FLOW-3D was used to calculate the phenomenon where inside liquid moved greatly due to the oscillation of a tank and hit against and damaged the tank ceiling in the ...

Science.gov (United States)

... the effect of MBH on steam generator crevice corrosion; model boiler test results show that MBH is effective against denting corrosion and Alloy 600 ...

British Library Electronic Table of Contents (United Kingdom)

The static corrosion tests in lead-bismuth eutectic (LBE) were conducted from 450degreeC to 600degreeC to understand corrosion behavior and develop corrosion resistant materials for heavy liquid metal systems. While increase of Cr content in steels enhances corrosion resistance in LBE, the effect approaches a constant value above 12wt% of Cr. Corrosion depth in LBE increases with increasing temperature and corrosion attack becomes severe above 550degreeC even under the condition of high oxygen concentration. Nickel dissolution and Pb-Bi penetration occur in 316SS and JPCA above 550degreeC under the condition of high oxygen concentration. When oxygen concentration decreases below the level of Fe oxide formation, corrosion attack on these steels also becomes violent due to dissolution of var...

Science.gov (United States)

HQ AFSPC/LG / CORR.PPT. 2. 01/16/02. UNCLASSIFIED. UNCLASSIFIED. Overview. " Corrosion Control Areas. " Support Activities. " Test Projects ...

Energy Technology Data Exchange (ETDEWEB)

The corrosion behavior of 304 stainless steel was characterized with cyclic voltammetry in a eutectic Li/K and Li/Na carbonate melt under anode and cathode gas of the molten-carbonate fuel cell (MCFC). The corrosion rate of 304 steel was determined in four different environments of the MCFC with electrochemical methods and from cross-sectional analysis of corrosion layers. These four environments were open-circuit and MCFC-load conditions both under anode and cathode gas. At open-circuit conditions corrosion was more severe under the oxidizing cathode gas then under the reducing anode gas. On the contrary, at load conditions corrosion was more severe under anode than under cathode gas. The anodic polarization under anode gas enhances corrosion, whereas the high anodic polarization under cathode gas leads to anodic protection. Corrosion ...

International Nuclear Information System (INIS)

As the first step for development of the corrosion resistant superheater tube materials of 500 C, 100 ata used in high efficient waste-to-energy plants, field corrosion tests of six conventional alloys were carried out at metal temperatures of 450 C and 550 C for 700 and 3,000 hours in four typical Japanese waste incineration plants. The test results indicate that austenitic alloys containing approximately 80 wt% [Cr+Ni] show excellent corrosion resistance. When the corrosive environment is severe, intergranular corrosion of 40#approx#200 microm depth occurs in stainless steel and high alloyed materials. It is confirmed quantitatively that corrosion behavior is influenced by environmental corrosion factors such as Cl concentration and thickness of deposits on tube surface, metal temperature, and flue gas temperature. The excellent ...

International Nuclear Information System (INIS)

Short communication.

Energy Technology Data Exchange (ETDEWEB)

Significant environmental issues and regulatory proceedings in Alberta were discussed. The Mackenzie Valley Pipeline Project was reviewed in relation to the Deh Cho First Nation's advanced actions in the federal court to enjoin the review panel from proceeding with the review process. The Deh Cho First Nation is seeking a declaration that the plan violates their rights under the Canadian Charter of Rights and Freedoms and the Constitution Act. Various regulatory and government agencies have now developed a plan to coordinate their different regulatory processes and approvals in the Cooperation Plan for the Environmental Impact Assessment and Regulatory Review of the Northern Gas Pipeline project. The Deh Cho allege that they were not afforded the opportunity to participate in the development and implementation of the plan. A review panel plans to proceed once the environmental and social impacts are determined, and the consortiums plan to minimize harm has been submitted. ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

A.C.R.O. (Association pour le Controle de la Radioactivite dans l Ouest) is a French non governmental organisation that operates a laboratory for radioactivity analysis. It was created in 1986 as a response to people demands for information and reliable, independent testing. The organisation mainly carries out missions of information and training for its correspondents and more generally for a wide audience, particularly for people who worry about problems of environment, health, management of radioactive waste and emissions. Thanks to its structure, it enables citizens to involve themselves together with scientists so as to gain access to information that was hither to reserved to specialists. The organisation can vouchsafe its independence from the diversity of its members and volunteers, as well as from the diversity of its money resources. Besides its headquarters situated on the city of Caen area (Normandy), three branches situated in North Normandy, in Touraine and North Cotentin ...

Energy Technology Data Exchange (ETDEWEB)

Pitting corrosion is localized accelerated dissolution of metal that occurs as a result of a breakdown of the otherwise protective passive film on the metal surface. This paper provides an overview of the critical factors influencing the pitting corrosion of metals. The phenomenology of pitting corrosion is discussed, including the effects of alloy composition, environment, potential, and temperature. A summary is then given of studies that have focused on various stages of the pitting process, including breakdown of the passive film, metastable pitting, and pit growth. 120 refs.

International Nuclear Information System (INIS)

... Systems Research and Development Center, Yokohama, Kanagawa (Japan)

International Nuclear Information System (INIS)

... FUEL CYCLE AND FUEL MATERIALS MATERIALS SCIENCE chromium-nickel

International Nuclear Information System (INIS)

In order to qualify corrosion resistant materials for high level waste (HLW) packagings acting as a long-term barrier in a rock salt repository, the corrosion behaviour of the preselected materials Ti 99.8-Pd, Hastelloy C4 and two unalloyed steels was investigated. The resistance of the materials to general corrosion, local corrosion and stress corrosion cracking was examined under postulated accident conditions in the repository by long-term immersion tests of up to 4 years duration and electrochemical methods. The parameters investigated were different salt brines, temperatures of 90 deg. C, 170 deg. C and 200 deg. C as well as a gamma radiation field of 10"3Gy/h (10"5rad/h). Among the materials studied, Ti 99.8-Pd exhibited the highest corrosion resistance. This material corroded at a very low rate (

International Nuclear Information System (INIS)

Corrosion resistance of Cu-W system condensates in tap water was studies. It is shown that with an increase in W concentration in the condensates of the Cu-W system their corrosion in tap water enhances. In the material designated for power supply facilities the optimal tungsten content is up to 6%. Owing to formation of oxide film on the surface of the samples corrosion is stabilitized 40 h after the test start.

Energy Technology Data Exchange (ETDEWEB)

A necessary condition for crevice corrosion is that a crevice former create a sufficiently tight, restricted geometry on the metal surface to support the development of critical crevice chemistry. Crevice corrosion is affected by the crevice geometry (tightness) and the properties of the crevice former. The objective of this study is to determine the effect of the crevice former material on the evolution of localized corrosion-damage. A standard crevice corrosion test method is modified by (a) the use of ceramic, metal or polymer materials as the crevice former and (b) the variation of size and shape of the crevice. This study focuses on the post initiation stage of crevice corrosion and addresses factors that may limit the initiation of localized corrosion and also slow or stop the continued propagation of corrosion. Controlled crevice ...

International Nuclear Information System (INIS)

Zirconium is a transition element located along with sister elements titanium and hafnium in Group IVB of the periodic table. It is grayish white metal, with a density somewhat less than carbon steel. Zirconium is the ninth most common metallic element in the earth's crust, and is more abundant than zinc, lead, nickel, or even copper. Zirconium is exceptionally resistant to corrosion by many common acids and alkalis. It is resistant to most organic acids, such as formic, acetic, lactic, and oxalic acids. It also has a high resistance to localized forms of corrosion, such as pitting, crevice corrosion, and stress corrosion cracking. Its corrosion resistance is caused by the formation of a dense, tenaciously adherent, chemically inert oxide film on the surface. This oxide film protects the base metal from both chemical and mechanical attack at temperatures up to about 400 C (750 F). ...

British Library Electronic Table of Contents (United Kingdom)

Erosion-corrosion (E-C) of 3003 aluminum (Al) alloy in ethylene glycol-water solutions were studied by weight-loss and electrochemical measurements as well as surface characterization through an impingement jet system. Al alloy E-C is dominated by erosion components, i.e., pure erosion and corrosion-enhanced erosion, which account for 92-97% of the total E-C rate under the various conditions in this work. Contribution from corrosion components, including pure corrosion and erosion-enhanced corrosion, is slight. With the increase of fluid flow velocity and sand concentration, the total E-C rate increases. Compared with the significant increase of the rates of erosion components, the increase of the rate of corrosion component is negligible. Upon fluid flow, passivity of Al alloy that develo...

Energy Technology Data Exchange (ETDEWEB)

Accelerated aging tests on gold bridgewired detonator assemblies to determine compatibility of the Au and Pd-In-Sn solder with the organic explosive, PENT, have revealed an unusual corrosion process. These tests, conducted at 74/sup 0/C and 54/sup 0/C indicated a preferential attack of the gold. A matrix of corrosion test units was established to study this corrosion problem with accelerating temperatures up to 100/sup 0/C. Scanning electron microscopy (SEM), energy dispersive x-ray (EDX), and x-ray diffraction techniques were used to determine the extent of the corrosion and identify the corrosion products. Results indicate the preferential attack of the gold was due to HCN formed by decomposition of the explosive powder (PETN) at high temperatures. Other associated reactions were also observed including subsequent attack of the solder by the gold corrosion ...

International Nuclear Information System (INIS)

Due to the well-establish corrosion problems of Alloy 600 as a steam-generator material and the subsequent focus on thermally treated (TT) Alloy 690 and Alloy 800 as alternative materials, a systematic analysis of the corrosion behavior of these two latter alloys is warranted. Corrosion test results for Alloys 690 TT and 800 were collected and organized in the form of corrosion mode diagrams. Selected data for mill annealed (MA) Alloy 600 were also included for reference. The corrosion mode diagrams correlate the modes of corrosion degradation observed in tests as functions of the environment pH and electrochemical potential (ECP). The diagrams confirm that Alloys 690TT shows some susceptibility in caustic environments, and Alloy 800 shows susceptibility in both caustic and highly acidic environments. (authors). 6 figs., 5 refs.

International Nuclear Information System (INIS)

Results from a heavily fouled 19 tube C-E model boiler test to investigate the potential for egg crate corrosion in aggressively fouled AVT chemistry are reported. Substantial support plate and egg crate corrosion was produced in this test. Carbon steel drilled support plates exhibited extensive denting which resulted in flow hole ligament cracking. Corrosion of the carbon steel egg crate, through-wall at areas of tube contact, resulted in denting of the Alloy 600 heat transfer tubes. Corrosion performance of the 409 stainless steel egg crate was improved compared to the carbon steel egg crate although localized through-wall corrosion was noted. The results from the above test and previously reported tests were compared based on the following simplifying assumptions: maximum dent size and/or corrosion penetrations utilized, average bulk water chloride ...

International Nuclear Information System (INIS)

The purpose of this text is to train engineers and technologists not just to understand corrosion but to control it. Materials selection, coatings, chemical inhibitors, cathodic and anodic protection, and equipment design are covered in separate chapters. High-temperature oxidation is discussed in the final two chapters ne on oxidation theory and one on controlling oxidation by alloying and with coatings. This book treats corrosion and high-temperature oxidation separately. Corrosion is divided into three groups: (1) chemical dissolution including uniform attack, (2) electrochemical corrosion from either metallurgical or environmental cells, and (3) stress-assisted corrosion. Corrosion is logically grouped according to mechanisms rather than arbitrarily separated into different types of corrosion as if they were unrelated. For those ...

Energy Technology Data Exchange (ETDEWEB)

Separation of the bulk soluble chemical salts from the insoluble metal hydroxides and radionuclides is central to the strategy of disposing Hanford tank waste. Sludge washing and caustic leaching have been selected as the primary methods for processing the 230 million L (61,000,000 gal) of Hanford tank waste. These processes are very similar to those selected for processing waste at the West Valley Site in New York and the Savannah River Site in South Carolina. The purpose of sludge washing is to dissolve and remove the soluble salts in the waste. Leaching of the insoluble solids with caustic will be used to dissolve aluminum hydroxide and chromium hydroxide, and convert insoluble bismuth phosphate to soluble phosphate. The waste will be separated into a high-level solids fraction and a liquid fraction that can be disposed of as low-level waste after cesium removal. The washing and leaching operations involve batchwise mixing, settling, and ...

International Nuclear Information System (INIS)

This paper describes two research programs which are currently underway in the author's laboratory to investigate the effect of fluid flow on the degradation of power plant materials in high temperature/high pressure aqueous environments. These programs include the design and operation of a controlled hydrodynamic corrosion testing apparatus that can be used to study the general and localized corrosion characteristics of alloys in simulated nuclear reactor environments, and a study of the effect of flow velocity on the stress corrosion cracking of ASTM A508 C1.2 steel and Type 304SS in simulated BWR heat transport fluids.

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the pitting corrosion of copper and copper alloys, in different media, with some references to methods for protecting against such corrosion. Included are factors contributing to the onset of pitting corrosion. Emphasis is placed on exposure to water, especially in tubing for heat exchangers and water conduits. Many of the citations present studies on exposure to sea water. Some references pertain to the detection of pitting corrosion in installations and the evaluation of the degree of pitting present. (Contains 250 citations and includes a subject term index and title list.)

Energy Technology Data Exchange (ETDEWEB)

Electrochemical cyclic potentiodynamic polarization experiments were performed on several candidate waste package container materials to evaluate their susceptibility to pitting corrosion at 90 degrees C in aqueous environments relevant to the potential underground high-level nuclear waste repository. Results indicate that of all the materials tested, Alloy C-22 and Ti Grade-12 exhibited the maximum corrosion resistance, showing no pitting or observable corrosion in any environment tested. Efforts were also made to study the effect of chloride ion concentration and pH on the measured corrosion potential (Ecorr), critical pitting and protection potential values.

International Nuclear Information System (INIS)

The aquatic monitoring program consists of onsite monitoring of surface runoff, monitoring of point source discharges identified in the NPDES permit, and limited instream biological monitoring. The program is tied to a feedback mechanism for implementing corrective action before significant adverse impacts occur in the Holston River. This report evaluates the aquatic monitoring program for the second year (October 19, 1978 through October 18, 1979) of construction as required by the NPDES permit, Part III, Section I. Included in this report are data from peripheral runoff monitoring, selected heavy rainfall sampling, ground water monitoring, instream aquatic macroinvertebrate monitoring, and aquatic macrophyte monitoring.

Energy Technology Data Exchange (ETDEWEB)

With specific energy of more than 200 Wh/kg, the Electric Fuel zinc-air battery delivers as much as eight times the energy of lead-acid traction battery, more than twice the energy of the nearest advanced-battery competitor, and as much energy as a tank of gasoline. (author)

Energy Technology Data Exchange (ETDEWEB)

For the expansion to 2.0 MTPY of the CVG Bauxilum alumina plant, the area of clarification and red mud washing was rearranged from four 2-thickener-5-washer trains to two 1-thickener-7-washer trains. As a result of this modification, the specific mud handling capacity of the existing tanks should be increased by almost 3-times. The time allowed for control actions was then significantly reduced, leading to the need of an on-line level detection system, in order to achieve a better and faster control of the operation. With this scope, it was developed and installed a new continuous mud level detector that gives the measurement of both mud and turbid zone levels in the tanks. The development of the new instrument started with an existing instrument for density measurements which was completely re-engineered in order to obtain the maximum readability in the densities founded along the full range of the tank height. Actually 28 ...

Science.gov (United States)

An investigation was conducted to determine the cause of coating residue found in the test gun chambers during qualification firing of 120-mm combustible cartridge case (CCC) ammunition for the MlAl/A2 main battle tank. The CCC is coated with a clear epox...

Energy Technology Data Exchange (ETDEWEB)

The Tank Waste Remediation System (TWRS) Program mission is to store, treat, and immobilize highly radioactive Hanford Site waste (current and future tank waste and the strontium/cesium capsules) in an environmentally sound, safe, and cost-effective manner. The scope of the TWRS Waste Pretreatment Program is to treat tank waste and separate that waste into HLW and LLW fractions and provide additional treatment as required to feed LLW and HLW immobilization facilities. Enhanced sludge washing was chosen as the baseline process for separating Hanford tank waste sludge. Section 1.0 briefly discusses the purpose of the evaluation plan and provides the background that led to the choice of enhanced sludge washing as the baseline process. Section 2.0 provides a brief summary of the evaluation plan details. Section 3.0 discusses, in some detail, the technical work planned to support the evaluation of enhanced ...

Science.gov (United States)

Baldwin County is located on the Gulf of Mexico in Alabama and has a rapidly growing population. Almost 3,000 permits for septic systems are approved annually by by the Baldwin County Health Department. More than 50% of the county's residents rely on septic systems for their d...

Science.gov (United States)

...limited to, emission control devices, pumps, filters, muck cookers, stills, solvent tanks, solvent containers, water separators...facility that meets the conditions of § 63.320(g). Muck cooker means a device for heating perchloroethylene-laden...

Energy Technology Data Exchange (ETDEWEB)

The present invention is a device for a solar heating system having a solar collector, a storage tank connected to the solar collector, a pump for circulating liquid from the tank to the solar collector, a supply of liquid at a temperature above freezing and a connection from the supply of liquid to the solar collector for replacing any liquid lost from said solar collector. The device comprises a sensor for sensing the temperature of liquid in the solar collector, and a valve for bleeding liquid from the solar collector when the sensed temperature falls below a predetermined minimum whereby cool liquid in the solar collector is automatically replaced by liquid at a temperature above freezing.

Energy Technology Data Exchange (ETDEWEB)

Corrosion is a primary determinant of waste package performance at the proposed Yucca Mountain Repository and will control the delay time for radionuclide transport from the waste package. Corrosion is the most probable and most likely degradation process that will determine when packages will be penetrated and the shape, size, and distribution of those penetrations. The general issues in corrosion science, materials science and electrochemistry are well defined, and the knowledge base is substantial for understanding corrosion processes. In this paper, the Yucca Mountain Repository is viewed from a corrosion perspective. A major component of the long-term strategy for safe disposal of nuclear waste at the Yucca Mountain Repository is first to completely isolate the radionuclides in the waste packages for long times and to greatly retard the egress and transport of radionuclides ...

Energy Technology Data Exchange (ETDEWEB)

Pitting corrosion measuring method for almunum alloys sold on the market was studied. By addition of a little quantity of Cu {sup ++} ion, corrosion potential of alminum alloys rapidly approachs to pitting corrosion potential in the solution including chloride. After Cu {sup ++} ion of 5ppm is added in advance into the solution including chrolide to measure the pitting corrosion potential, alminum alloy test pieces are imersed into the solution in the atmospheric air, then the stable corrosion potential is shown after three-minite imersion, and this potential is defined to the pitting corrosion potential. The pitting corrosion potential can be easily measured by this method stated above (copper ion method). The values measured by copper ion method is comparatively agreed with that measured by the existing potentio dynamic method. The pitting ...

International Nuclear Information System (INIS)

Power plant components exposed to environments such as water and soil are susceptible to severe corrosion. Many times the effect of corrosion in power plant components can be catastrophic. The problem is aggravated for underground pipelines due to additional factors such as large network of pipelines, proximity to earth mat, high voltage transmission lines, corrosive chemicals, inadequate approach etc. Other components such as condenser water boxes, internals of pipelines, clarifier bridge structures, cooling water inlet gates and pipes etc. which are in continuous contact with water, are subjected to severe corrosion. The nature and locations of all such components are at places which are not accessible for routine maintenance and hence they require long term reliable protection against corrosion. Experience has shown that anti-corrosive coatings are inadequate ...

International Nuclear Information System (INIS)

In PWR's steam generators, ''denting'' resulted from corrosion of support plate material, carbon steel is an important problem. The role of chlorides in corrosion acceleration of mild steel was studied. Corrosion tests were conducted at temperature from 100"0C to 280"0C in deaerated solutions of NaCl and MgCl_2 which are main content of sea water. 1) Solution of MgCl_2 was more corrosive than that of NaCl. The more increased in concentration of each chloride solution, the more corrosive in MgCl_2 soln. but the less corrosive in NaCl soln. 2) The rate of corrosion in the mixed solution of NaCl and MgCl_2 was governed by the concentration of MgCl_2 soln. The corrosion behaviour in sea water was suggested to be not controlled by NaCl but by MgCl_2. 3) Acidification of MgCl_2 soln. could be evaluated by experiment at 100"0C, ...

Energy Technology Data Exchange (ETDEWEB)

This document is the third annual revision of the plans and schedules for implementing the Federal Facility Agreement (FFA) compliance program, originally submitted in 1992 as ES/ER-17&D1, Federal Facility Agreement Plans and Schedules for Liquid Low-Level Radioactive Waste Tank Systems at Oak Ridge National Laboratory, Oak Ridge, Tennessee. This document summarizes the progress that has been made to date in implementing the plans and schedules for meeting the FFA commitments for the Liquid Low-Level Waste (LLLW) System at Oak Ridge National Laboratory (ORNL). Information presented in this document provides a comprehensive summary to facilitate understanding of the FFA compliance program for LLLW tank systems and to present plans and schedules associated with remediation, through the Comprehensive Environmental Response, Compensation, and Liability Act (CERCLA) process, of LLLW tank systems that have been removed from ...

British Library Electronic Table of Contents (United Kingdom)

The corrosion behavior of hard metals with VC and Cr3C2 grain growth inhibitors was investigated in alkaline solutions by electrochemical methods. The two inhibitors have opposite effects on the corrosion behavior: Cr3C2 significantly improves the corrosion behavior, whereas VC-containing alloys show a poor resistance. Time-of-flight secondary ion mass spectrometry (ToF-SIMS) and analytical transmission electron microscopy (TEM) analyses of the distributions of Cr and V in the composite material, as well as in the surface layers formed during corrosion were employed to clarify the influence of these elements on the corrosion behavior. The measurements showed that VC is precipitated mostly along the WC/binder interface after the liquid-phase sintering process, while Cr3C2 is almost homogene...

British Library Electronic Table of Contents (United Kingdom)

Flue gas desulfurization systems (FGDs) are operated in severely corrosive environments that cause sulfuric acid dew-point corrosion. The corrosion behavior of low-alloy steels was tested using electrochemical techniques (electrochemical impedance spectroscopy, potentiodynamic tests, potentiostatic tests), and the corrosion products were analyzed by scanning electron microscopy and X-ray photoelectron spectroscopy. The electrochemical results showed that alloying W with small amounts of Sb, Cu, and Co improves the corrosion resistance of steels. The results of surface analyses showed that the surface of the steels alloyed with W consisted of W oxides and higher amounts of Sb and Cu oxides. This suggests that the addition of W promotes the formation of a protective WO3 film, in addition to ...

Energy Technology Data Exchange (ETDEWEB)

Corrosion behavior of deposition coated specimens prepared by the technique proposed by the authors is investigated in salt immersion tests, and also those of pure magnesium, 3N, 4N and 6N grades, and magnesium alloys, AZ31 and AZ91E, are investigated for comparison. Inhomogeneous corrosion occurs in AZ31 and AZ91E alloys when buffered solutions with pH values of 6.5 and 9.0 including 1% NaCl and a conventional 3% NaCl solution are used for immersion tests, while 6N-Mg shows homogeneous corrosion in such solutions. Corrosion behavior of the deposition coated specimen resembles that of 6N-Mg. Purification process included in the deposition coating technique provides homogeneity in microstructural and electrochemical terms, which results in improving corrosion resistance. (orig.)

International Nuclear Information System (INIS)

The major degradation mechanisms acting during the aging of selected WWER-440/213 primary circuit facilities were assessed critically. The analysis gave evidence that such mechanisms include radiation and fatigue damage of the reactor pressure vessel (effect of the neutron flow, cyclic fatigue promoted by the corrosive medium, effect of thermal aging), corrosion-mechanical and thermo-mechanical (fatigue) damage of the steam generator (stress corrosion cracking, erosion corrosion, thermal aging, wear), thermal and dynamic aging of the pressurizer, and corrosion-mechanical damage of the primary circuit piping (thermal aging, corrosion). (J.B.). 5 tabs., 1 fig., 62 refs.

International Nuclear Information System (INIS)

Economic and safe operation of nuclear power plants requires reliable steam turbines with high efficiencies. The progress in flow mechanics achieved over the past few years has allowed the use of powerful methods of flow calculation in developments of new blading with greatly enhanced efficiencies. Thanks to the latest manufacturing techniques, the newly developed blading systems can be produced at low cost. Next to progress in flow mechanics, also the broadbased use of advanced finite-element calculations resulted in a more thorough grasp of the many problems associated with structural mechanics assessment of steam turbine components. The theoretical methods have been supplemented by comprehensive efforts in fracture mechanics and experimental materials studies, thus helping to create a reliable knowledge base which will help to avoid the dreaded stress corrosion cracking phenomenon, in components of steam turbines. The measures introduced to improve operational ...

Energy Technology Data Exchange (ETDEWEB)

The author describes the layout of the environmental monitoring scheme at Devco's No. 26 Colliery in Canada, which includes wall face ventilation, fan performance, and methane drainage monitoring. He gives details of the sensors, outstations, and the surface control room.

Energy Technology Data Exchange (ETDEWEB)

This article consists of a series of manufacturer's descriptions outlining specifications of underground monitoring equipment which range in complexity from gas sensitive personal badges to full mine monitoring systems. 8 figs.

Science.gov (United States)

The objective of this project is to reduce energy consumption in 203 buildings by providing a new EMCS (Energy Monitoring Control System) to control and monitor systems.

Science.gov (United States)

The corrosion behavior of Ta, Ti, and Zr in inorganic acids, bases, chlorides and miscellaneous salts, waters and gases, and organic acids and miscellaneous organic chemicals is summarized. (W.L.H)

Energy Technology Data Exchange (ETDEWEB)

The effect of dissolved oxygen and copper on denting corrosion at 280/sup 0/C in solutions of NaCl at pH 9 with ammonia was investigated using a packed tube/support plate crevice in a laboratory simulation. The onset of corrosion was detected with a hydrogen analyzer sensitive to 0.2 ppB. In the absence of copper, rapidly rising hydrogen concentrations were detected only when the product of the chloride and oxygen concentrations were detected only when the product of the chloride and oxygen concentrations in the boiler-water exceeded 25 (ppM)/sup 2/, but at these high concentrations, unheated low-carbon steel surfaces in the system were as sensitive to corrosion as the heated crevice. When copper metal was present in the feed system, corrosion of the heated crevice occurred in the absence of oxygen, provided the copper had previously been exposed to dissolved oxygen. Dosing hydrazine into the feedwater ...

International Nuclear Information System (INIS)

The following conclusions are drawn from the study of the effects of dissolved oxygen on corrosion denting: 1) Following the ingress of fresh-water contamination into a PWR boiler, an acidic chloride solution can be formed in the crevice between tube and tube support plate when an oxidant such as dissolved oxygen or copper ions is present in the boiler water. 2) In the absence of copper, very high levels of dissolved oxygen and neutral chloride are necessary to initiate corrosion. 3) When copper is present in the feed system, sufficient copper ions to initiate corrosion within the crevice are released when the chloride concentration is 0.8 mg/kg and probably also at lower chloride values. Corrosion initiation however may require prior exposure of the copper to dissolved oxygen and can be suppressed by pretreatment with hydrazine. 4) The effect of dissolved oxygen on corrosion ...

Energy Technology Data Exchange (ETDEWEB)

The susceptibility to pitting corrosion of AA2024-T4, AA7075-T651 and AA7475-T761 aluminium alloys was investigated in aqueous neutral chloride solution for the purpose of comparison using electrochemical noise measurement. The experimentally measured electrochemical noises were analysed based upon the combined stochastic theory and shot-noise theory using the Weibull distribution function. From the occurrence of two linear regions on one Weibull probability plot, it was suggested that there existed two stochastic processes of uniform corrosion and pitting corrosion; pitting corrosion was distinguished from uniform corrosion in terms of the frequency of events in the stochastic analysis. Accordingly, the present analysis method allowed us to investigate pitting corrosion independently. The susceptibility to pitting corrosion was ...

International Nuclear Information System (INIS)

Rapid corrosion of PWR steam generator carbon steel support structures and consequential denting of steam generator tubes led to considerable investigation of the mechanism of corrosion and for palliatives. The basic mechanism is now fairly well understood. Chloride present in the boiler feedwater from condenser leakage is concentrated in the support plate crevice as a result of the superheat present. This leads to the formation of a low pH acid ferrous chloride environment either through the hydrolysis of a weak base chloride such as MgCl_2 or the combined action of a neutral chloride with an oxidizing agent. Rapid attack of the carbon steel ensues with the Fe_3O_4 corrosion product forming at the metal/oxide interface. This oxide has a volume approximately twice that of the steel consumed and thus eventually fills the crevice between the tube and the support plate. Oxide growth continues leading to compression of the ...

International Nuclear Information System (INIS)

... 1343-3563 v. 57(1) SPECIFIC NUCLEAR REACTORS AND ASSOCIATED

International Nuclear Information System (INIS)

... Toshiba Corporation, Isogo Engineering Center, Yokohama, Kanagawa (Japan)

International Nuclear Information System (INIS)

Zirconium-base alloys are used primarily as fuel cladding material and other core structure material in water cooled nuclear power reactors. Main research achievements and problems about corrosion of zirconium alloys are reviewed; the present theories and challenge are summarized. In the 1980s, great progress had been made towards correlating alloy composition, microstructure and irradiation with corrosion resistance. In the 1990s, main researches are focused on exploring actual mechanism of corrosion, optimizing both alloy composition and microstructure in order to minimize the fuel cycle costs through burnup optimization.

International Nuclear Information System (INIS)

A review of the performance of steam generator tubes in 116 water-cooled nuclear power reactors showed that tubes were plugged at 54 (46 percent) of the reactors. The number of tubes removed from service decreased from 4 692 (0.30 percent) in 1981 to 3 222 (0.20 percent) in 1982. The leading causes of tube failures were stress corrosion cracking from the primary side, stress corrosion cracking (or intergranular attack) from the secondary side and pitting corrosion. The lowest incidence of corrosion-induced defects from the secondary side occurred in reactors that have used only volatile treatment, with or without condensate demineralization.

Science.gov (United States)

... by the Bureau. A canvas of supply sources produced only one other, the Flexo roller bearing swivel. Accordingly, only the ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

International Nuclear Information System (INIS)

Eight years ago, corrosion and tube denting seriously threatened the reliability and design life of steam generators, especially for closed loop arrangements in pressurized water reactors (PWRs). Concentrated research by the Steam Generator Owners Group (SGOG) diagnosed the causes and produced effective solutions, notably guidelines for water chemistry control in the secondary loop. The guidelines recommend specific levels of water impurities and remedial actions to prevent cooling-water leaks in the condenser, prevent air leaks, limit corrosion product buildup, and remove some impurities while neutralizing others. Continued research in SGOB-II is investigating intergranular corrosion and stress corrosion cracking. 3 figures.

International Nuclear Information System (INIS)

The influence of microalloying vanadium or titanium on improving the corrosion resistance of mild steel in saturated calcium hydroxide solution was investigated. Potential-time, potentiodynamic polarization, and impedance measurement techniques were employed. The corrosion products have been examined by infrared and X-ray diffraction analysis and by scanning electron microscopy. It has been shown that the grain refining, due to microalloying, plays an important role in enhancing the corrosion resistance of steel. Scales of calcite and iron oxides on top of a protective oxide are formed on the investigated steels.

International Nuclear Information System (INIS)

The influence of deformation on the corrosion behavior of a newly developed multifunctional beta titanium alloy Ti-23Nb-0.7Ta-2Zr-O (mol%) in Ringer's solution at 310 K was evaluated using an electron backscatter diffraction technique and electrochemical measurements. The results showed that the effect of deformation on the corrosion resistance of the beta titanium alloy is complicated. Small levels of plastic deformation are detrimental to the corrosion resistance, whereas large deformations tend to eliminate this detrimental effect.

International Science & Technology Center (ISTC)

Research on Diffusion Zinc Cladding of Structural Steels, as Well as Their Mechanical and Corrosion Properties to Replace Their Cyanic Cadmium Plating

International Nuclear Information System (INIS)

... Japan) Kobayashi, Minoru AITEL Corp., Yokohama, Kanagawa (Japan)

International Nuclear Information System (INIS)

The importance that must be attached to the phenomenon of stress corrosion cracking of austenitic alloys is emphasized. The relation between chemical composition of various alloys and their sensitivity to cracking is shown with particular reference to the behaviour of Alloy 800. The different effects of alkaline anc chloride environments are discussed. Studies are reported of the general corrosion of Alloy 800 and other alloys in an environment representative of the primary coolant of PWR reactors; and of the behaviour of various alloys (including Alloy 800) in the conditions envisaged for their use for steam generators with superheat up to about 550 deg.C. (U.K.).

British Library Electronic Table of Contents (United Kingdom)

Purpose - The purpose of this paper is to evaluate the corrosion inhibition potential of mangrove (Rhizopora apiculata) tannin in hydrochloric acid medium on copper with the view of developing a natural corrosion inhibitor. Design/methodology/approach - The mangrove tannin was extracted from the mangrove bark and its anticorrosion potential was studied by weight loss, electrochemical and scanning electron microscopy (SEM) analysis. Findings - It has been found that the mangrove tannin effectively inhibits the corrosion on copper metal in hydrochloric acid solution. The results of the electrochemical and weight loss methods showed that the inhibition efficiency of mangrove tannin increases with increasing its concentration. Inhibition is achieved through the adsorption of tannin molecules o...

UK PubMed Central (United Kingdom)

This is a review of health and sports monitoring research that uses or could benefit from wireless connectivity. New, enabling wireless connectivity standards are evaluated for their suitability, and...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This report documents the technical basis by which the workplace air monitoring and sampling program is operated in the 324 and 327 Buildings.

UK PubMed Central (United Kingdom)

There is a requirement for a noninvasive technique to monitor stem cell differentiation. Several candidates based on optical spectroscopy are discussed in this review: Fourier transform infrared (FTIR)...Full Text Available

International Science & Technology Center (ISTC)

Comparative Molecular Genetic Monitoring of Myxoviruses Circulating in Populations of Seals Phoca Caspia and Phoca Sibirica in Northern Caspian Region and Lake Baikal

International Nuclear Information System (INIS)

The principal types of corrosion are presented which can occur in CANDU steam generator. There are also presented the operation conditions, the specifications referring to the water chemistry and the construction materials of Steam Generator, the factors that have a great influence on the corrosion behaviour during the whole exploitation period of this equipment. The most important elements of CANDU Steam Generator ageing management program are also discussed. (R. P.)

International Nuclear Information System (INIS)

Paper estimates the corrosion resistance and studies the character of dissolving of silicon-bearing austenite stainless steels in strongly oxidizing media containing phosphate and fluoride admixtures. Corrosion behaviour of the studied steels is determined to depend essentially on the content of admixture or alloying silicon, as well as, on their phase composition in many respects determined by the thermal treatment condition. Refs. 22, figs. 1, tabs. 2.

Energy Technology Data Exchange (ETDEWEB)

The effect of small misch metal additions (0.25 to 1 wt.%) on the corrosion behaviour of aluminium was studied through electrochemical polarization in 0.1 N inorganic and organic acids at room temperature. It has been observed that rare earth addition improves the corrosion resistance of aluminium. (orig.).

Energy Technology Data Exchange (ETDEWEB)

In the aim to fight against tubes corrosion of geothermal wells which exploit the aquifer of Dogger reservoir in the Parisian basin, injection of corrosion inhibitors in the geothermal fluid has been generalized since 1989 by using an additive injection tube in the bottom of the well, allowing the protection of the two wells from the geothermal doublet. 3 annexes. 46 refs. 13 tabs. 9 figs.

Energy Technology Data Exchange (ETDEWEB)

A growth model of pitting corrosion of carbon steel in cooling water systems was developed on microscopic observations of pits and electrochemical studies. Results of pitting corrosion measurements in laboratory and field conditions with the model, using a newly developed electrochemical device, are discussed. For an actual heat exchanger up to a year operation, the values of pitting depth estimated were in good agreement with the measured values.

International Nuclear Information System (INIS)

General corrosion behavior of ALLOY 800 in high temperature water was studied in relation to its surface film structure. The surface film formed in water was found to decrease the corrosion rate of ALLOY 800. This film is composed of Ni ferrite, and can be obtained by oxidation in air or steam. Based on these results, air or steam oxidation treatment to inhibit Ni and Co release of ALLOY 800 into high temperature water is proposed. (author).

Energy Technology Data Exchange (ETDEWEB)

Qualifying corrosion inhibitors for use in high velocity multiphase flowlines in arctic or subsea environments is discussed. The tests include high velocity flow loop corrosion tests, pumpability through 0.125 (0.318 cm) inch capillary at low temperatures, compatibility with Nylon 11, emulsion tendency testing, and partitioning characteristics. Laboratory and field data show the importance for using the above criteria for inhibitor selection.

International Nuclear Information System (INIS)

Effect of hydroxide nature, concentration and temperature on corrosion resistance of domestic steels and alloys to hot NaOH, KOH, LiOH solutions is considered. It is ascertained that by corrosion growth in relation to stainless steels and nickel alloys, the hydroxides are placed in the following sequence: LiOH

Energy Technology Data Exchange (ETDEWEB)

This compact book of tables attempts to give practicians a survey of the corrosion behaviour of common structural and coating materials. Corrosion resistances are presented for steels, alloys, plastics, elastomers, graphite, glasses, and stoneware in environments of NaOH, HNO{sub 3}, SO{sub 2}, ZnCl{sub 2}, NH{sub 3}, H{sub 2}O{sub 2}, ethyl chloride, sodium acetate, and many others. (MM).

Energy Technology Data Exchange (ETDEWEB)

A knowledge based system for pitting corrosion is presented. It can be used for material selection for specific pitting corrosion conditions or to check the suitability of a chosen material. The user can enter his own knowledge. The expert system is an integration of traditional expert system technology and neural networks. (orig.)

Energy Technology Data Exchange (ETDEWEB)

CNG vehicles suffer from an uncontrolled temperature rise of the gas inside the tank during the filling process and heat exchange with the environment leads to variable filling levels. A partly filled tank reduces the range of CNG vehicles and works as a impediment to the spreading of environmentaly more friendly CNG vehicles. The increase of the pressure inside the tank combined with a prolongation of the filling time beyond three minutes can reduce the deficit of the filling process. For economic reasons the time required for refuelling should be as short as possible without the need to operate the filling station with a critical pressure. To meet this target the current technique requires further improvement. (orig.) [Deutsch] Die betriebliche Praxis bei Tankvorgaengen von Erdgasfahrzeugen zeigt, dass waehrend des Tankvorganges die Temperatur des getankten Erdgases im Fahrzeugtank ansteigt. Waehrend und nach Beendigung ...

Energy Technology Data Exchange (ETDEWEB)

As part of a coordinated program, AECL is developing a set of tools to aid with the prediction and management of steam generator performance. Although stress corrosion cracking (of Alloy 800) has not been detected in any operating steam generator, for life management it is necessary to develop mechanistic models to predict the conditions under which stress corrosion cracking is plausible. Therefore, constant extension rate tests were carried out for Alloy 800 under various steam generator crevice chemistry conditions at applied potentials. These tests were designed to evaluate the stress corrosion cracking susceptibility of Alloy 800 under CANDU( steam generator operating conditions. Based on the experimental results, the recommended electrochemical corrosion potential/pH zone for Alloy 800 determined by electrochemical polarization measurements was verified with the respect of stress ...

International Nuclear Information System (INIS)

The steam generator availability is one of the important problems encountered during the pressurized water nuclear plant operation. Various kinds of corrosion phenomena were observed in the past. These phenomena result from the concentration of impurities mainly in three locations in the steam generators: the tubesheet crevices, the tube support plate crevices, and the sludge pile. Corrections were made in the design and the materials used but a number of steam generators suffer or will suffer from corrosion processes inducing in many cases forcing their replacement. In order to prevent or to retard the corrosions several laboratories have performed experiments to reproduce and to study the corrosion processes. The first step of the degradation is the concentration of chemical species. A method using /sup 24/Na as a radioactive tracer was used to establish the concentration kinetics of caustic which was ...

British Library Electronic Table of Contents (United Kingdom)

The effect of sodium gluconate anion (SG) on the corrosion and scale inhibition of ordinary steel in simulated cooling water has been studied using weight loss, polarisation curves, electrochemical impedance spectroscopy (EIS) and scanning electron microscopy (SEM) techniques. SG was studied in concentration from 10-4M to 10-1M. Results obtained reveal that SG perform excellently as corrosion and scaling inhibitor for ordinary steel in simulated cooling water. An increase of SG concentration leads to the increase of the corrosion potential towards the positive direction. The inhibition efficiency was a low temperature dependence. The inhibitor mechanism was treated as an adsorption process according to Langmuir adsorption isotherm. The SEM/EDAX data show that was a corrosion and scale inhi...

Energy Technology Data Exchange (ETDEWEB)

Stainless steels can get pitting corrosion in halide containing solution, which make them a big risk in industrial production. Many investigations were made in the past in order to understand processes involved in pitting corrosion, pit initiation and pit growth. Results about the influence of alloying elements, their contents, the state of the structure, the condition of the surface, the content of chloride, the temperature, the pH-value, the velocity of flow and of the oxidizer on the chloride induced pitting corrosion of passive stainless steels are presented. Electrochemical measurements and the application of surface analytical methods (SEM, SAM, XPS) with high lateral resolution are carried out. A part of the samples received a diffusion annealing in order to obtain reproducible results. Pitting Resistance Equivalents (PRE) - Pitting Index - with different multipliers are given and discussed critical. An ...

British Library Electronic Table of Contents (United Kingdom)

Considering the status of knowledge on corrosion and corrosion protection and especially the need for long term compatibility data of structural materials in HLM a set of experiments to generate reliable long term data was defined and performed. The long term corrosion behaviour of the two structural materials foreseen in ADS, 316L and T91, was investigated in the design relevant temperature field, i.e. from 300 to 550degreeC. The operational window of the two steels in this temperature range was identified and all oxidation data were used to develop and validate the models of oxide scale growth in PbBi. A mechanistic model capable to predict the oxidation rate applying some experimentally fitted parameters has been developed. This model assumes parabolic oxidation and might be used for de...

British Library Electronic Table of Contents (United Kingdom)

This paper presents the corrosion inhibition performance of soluble self-doped copolymers of aniline and 4-amino-3-hydroxy-naphthalene-1-sulfonic acid synthesized by chemical oxidative polymerization method. The corrosion inhibition behaviour of the copolymers in 1.0M HCl has been evaluated using Tafel Extrapolation method and electrochemical impedance spectroscopy (EIS) which was also used to propose the mechanism besides surface morphology. The results showed that the copolymer film exhibited the significant shifting in the corrosion potential and greater charge transfer resistance. The corrosion inhibition efficiency was found to increase from 50% to 90% by increasing the concentration of copolymer from 10 to 70mg/l in HCl medium. Moreover, the copolymer showed the larger degree of surf...

International Nuclear Information System (INIS)

An Ultra-Low-Carbon 19% Cr-11% Ni Stainless Steels used in nuclear fuel reprocessing plants where highly corrosion resistance in nitric acid is required has been developed. This steel has optimized the chemistry composition to decrease inclusions and deformation-induced martensitic transformation. The formation of deformation-induced martensite has the potential danger of accelerating corrosion in nitric acid. In this paper, effects of cold reduction and martensitic transformation on corrosion resistance of Ultra-Low-Carbon Stainless Steels in nitric acid are discussed. The developed steel showed excellent corrosion resistance during long-term exposure to nitric acid. (author).

British Library Electronic Table of Contents (United Kingdom)

A study of the ordinary mild steel/cooling water interface, with and without inhibitor, was carried out using electrochemical impedance spectroscopy (EIS). EIS spectra in uninhibited medium reveal that a layer of corrosion and scale products is formed naturally and evolves with the immersion time. Monosaccharides derivatives were used as corrosion inhibitors. Most of them exhibit good behaviour against corrosion of ordinary steel in simulated water systems. Their inhibiting efficiency increases with concentration rise and depends on molecular structure especially -OH groups' position on two adjacent carbons and their number. In addition, the effect of MoO4^2^- on the corrosion inhibition in the presence of the best inhibitor was also studied by EIS. The addition of MoO4^2^- enhanced the in...

International Nuclear Information System (INIS)

Stemming from their unique combination of elevated strength, low density, and good overall corrosion resistance, beta titanium alloys have become attractive candidate materials for critical, high-stress, components in corrosive services. An overview of the comparative corrosion resistance of beta alloys to conventional alpha and alpha/beta titanium alloys in common industrial and aerospace service environments generally reveals attractive behavior depending on the environment and alloy composition and, in some cases, alloy condition. Expanded performance windows are especially noted for the molybdenum-rich beta alloys, particularly in regard to resisting reducing acids, stress corrosion, and high temperature localized chloride attack, along with hydrogen and oxidation resistance. Where applicable, implications of this enhanced corrosion performance on current and perspective beta ...

Energy Technology Data Exchange (ETDEWEB)

The desire to increase uranium utilization and to minimize spent fuel storage requirements provides an incentive to extend the average fuel rod discharge burnup to about 70,000MWd/MTU. For these higher burnups data are needed to determine if waterside corrosion of the cladding may be a life-limiting feature of fuel rod design. It is apparent that many factors can influence waterside corrosion, and these need to be better understood in order to minimize corrosion at these higher target burnups. The objective of this report is to review published data relevant to the corrosion of Zircaloy under PWR operating conditions. (author). 100 refs., 4 tabs., 21 figs.