Energy Technology Data Exchange (ETDEWEB)

Alumina (94 and 99.8% grade compositions) was brazed directly to itself with gold-based active brazing alloys (ABA's) containing vanadium additions of 1,2 and 3 weight percent. The effects of brazing conditions on the joint properties were investigated. Wetting behavior, interfacial reactions, microstructure, hermeticity and tensile strength were determined. Wetting was fair to good for the ABA and base material combinations. Microanalysis identified a discontinuous Al-V-O spinel reaction product at the alumina-braze interface. Tensile strength results for 94% alumina were uniformly good and generally not sensitive to the vanadium concentration, with tensile values of 85-105 MPa. There was more variability in the 99.8% alumina strength results, with values ranging from 25-95 MPa. The highest vanadium concentration (3 wt. %) yielded the highest joint strength for the brazed 99.8% ...

International Nuclear Information System (INIS)

A series of ball-on-disc wear and friction measurements were made for surfaces which have a chemical vapour deposition carbon silicon alloy layer on a carbon substrate (fine grain POCO graphite). Nitrogen ion irradiation was used to improve the wear resistance of the carbon alloy surface. For comparison, measurements were also taken for alumina against alumina. It was found that the lowest friction coefficient and lowest wear occurred for ion irradiated coated samples containing 4% Si in the alloy and that the performance was superior to that of alumina. ((orig.)).

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared

International Nuclear Information System (INIS)

English 2005 p. 52-59 International Atomic Energy Agency (IAEA) Collier,

International Nuclear Information System (INIS)

The total hemispherical emittance of an oxide film that formed on 6061-T6 aluminium alloy parts in the Tower Shielding Reactor-II at Oak Ridge National Laboratory was measured from 295 to 773 K using an emissometer and/or a calorimeter. The emittance of this film was critically needed for heat transfer calculations in a simulated loss-of-coolant accident of the reactor. X-ray diffraction analysis identified the film as boehmite (Al_2O_3 x H_2O), which dehydrated to alumina (Al_2O_3) upon heating above 473 K. The measured emittances for the alumina film are in excellent agreement with published values for anodized aluminum films and for bulk alumina. Published values of the emittance of boehmite could not be found for comparison, but evidence is presented that some anodization processes for aluminum yield boehmite and not alumina films.

Energy Technology Data Exchange (ETDEWEB)

An Fe-19Cr-8Al-0.5Hf alloy has been roll bonded to Alloy 800 to form a protective clad material suitable for use in coal conversion atmospheres. The commercial producibility of both the Fe-19Cr-8Al-0.5Hf alloy and the clad composite has been demonstrated. The clad composite has been shown to exhibit resistance to sulfidation in high sulfur, coal gasification atmospheres low Btu for 2000 hrs at 1800/sup 0/F (1255K). The FeCrAlHf alloy must be preoxidized in the absence of sulfur to form fully protective alumina scales on all surfaces. Useful life of the composite at temperatures of 1400 to 2000/sup 0/F (1033 to 1366K) is governed by reactions at the FeCrAlHf clad alloy 800 interface. The rate of interdiffusion decreases with increasing Ni content and a high Ni alloy such as RA333 appears to be a better substrate than Alloy 800 for a FeCrAlHf composite. The mechanical properties of the clad composite have been evaluated at both ambient (tensile ...

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The catalytic properties of molybdena-alumina catalysts reduced in hydrogen were studied in the function of the reduction temperature, i.e. in the function of the extent of reduction. The deuterium exchange reaction of benzene was used as model catalytic reaction. It was concluded that the reaction rate constant and the multiplicity factor decreased with the extent of reduction parallel with the change in the extent of dehydroxylation of the catalysts. (orig.)

International Nuclear Information System (INIS)

An energy sensitive Si(Li) detector XRF analyzer built by ATOMKI, Hungary, has been applied for various analytical purposes in alumina production at the Almasfuezitoe Alumina Company, Hungary. Specifically, the CaO content in red mud was determined by the new XRF technique using isotope excitation sources. The analysis of other components is under way. (R.P.).

Energy Technology Data Exchange (ETDEWEB)

The total hemispherical emittance of an oxide film that formed on 6061-T6 aluminium alloy parts in the Tower Shielding Reactor-II at Oak Ridge National Laboratory was measured from 295 to 773 K using an emissometer and/or a calorimeter. The emittance of this film was critically needed for heat transfer calculations in a simulated loss-of-coolant accident of the reactor. X-ray diffraction analysis identified the film as boehmite (Al{sub 2}O{sub 3} {times} H{sub 2}O), which dehydrated to alumina (Al{sub 2}O{sub 3}) upon heating above 473 K. The measured emittances for the alumina film are in excellent agreement with published values for anodized aluminum films and for bulk alumina. Published values of the emittance of boehmite could not be found for comparison, but evidence is presented that some anodization processes for aluminum yield boehmite and not alumina films.

Energy Technology Data Exchange (ETDEWEB)

The friction and wear properties of glass fiber reinforced composites of nylons (nylon 6, nylon 66 and nylon 46) with different crystallinities due to their molecular structures were investigated by sliding them with alumina ceramics and using a pin-on-disk friction machine. The friction coefficients of the glass fiber reinforced nylons in oil were lower and more stable than those in air from the initial stage of friction. The transfer of nylon matrix to adhere onto the alumina surface in air was so much greater than in oil that the alumina surface could not be recognized. Consequently, a different between the friction and wear properties in air and in oil was resulted. Reinforcement of nylons with glass fiber remarkably improved their friction properties in oil by its lubricating action, while the wears were rather high contrary to what was expected. This tendency was conspicuous for nylon 46 with high crystallinity. ...

British Library Electronic Table of Contents (United Kingdom)

Alumina-reinforced carbon nanofiber nanocomposites were prepared using different routes; powders mixture, colloidal route and sol?gel process followed by spark plasma sintering (SPS). CNFs/xAl2O3 (x = 10?50 vol.%) were prepared through nanopowders mixing in a high-energy attrition milling. The main limitations in the preparation of this kind of nanocomposites are related to the difficulty in obtaining materials with a homogeneous distribution of both phases and the different chemical nature of CNFs and Al2O3, which causes poor interaction between them. A surface coating of CNFs by wet chemical routes with an alumina precursor is proposed as a very effective way to improve the interaction between CNFs and Al2O3. An improvement of 50% in fracture strength was found for similar nanocomposite ...

International Nuclear Information System (INIS)

Polycrystalline specimens of spinel (MgAl_2O_4) and alumina (Al_2O_3) were irradiated at room temperature and 650deg C with either dual- or triple-ion beams in order to investigate the effects of simultaneous displacement damage and helium implantation on cavity formation. The cavities in alumina were aligned along the direction of the c-axis, with diameters ranging from < 2 to 10 nm. The cavities in spinel were preferentially associated with dislocation loops and were of similar size as the cavities in alumina. Catastrophic amounts of cavitation were observed at the grain boundaries in spinel when the displacement damage level exceeded a critical value (#approx =# 20 dpa) in the presence of a fusion-relevant (#approx =# 60 appm/dpa) helium environment. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The properties of cast basalt and alumina are examined. The ways in which these materials have been used in applications in coal preparation plants, for example in bunker and pipe linings where abrasion and corrosion resistant materials are required, are discussed.

Energy Technology Data Exchange (ETDEWEB)

The electrical conductivity of Vitox-alumina (99.2%), Wesgo-alumina (99.9%) and AlN (99.6%) has been measured during and after irradiation with an experimental set-up which allows fusion relevant loading conditions. All irradiations were performed in high vacuum at 450 C using a 104 MeV {alpha}-particle beam with an applied DC electric field of 100 kV/m. In the high purity Vitox-alumina the in-situ and postirradiation bulk conductivities {sigma} and {sigma}{sub 0} show the highest irradiation induced electrical breakdown ever observed. The saturation level near 4 x 10{sup -2} ({Omega}m){sup -1}, reached already after 0.015 dpa (O-sublattice), is already above the critical value necessary to avoid MHD pressure drop with 10 {mu}m coatings in flowing liquid metal coolants. Under the same conditions no radiation induced electrical degradation at all has been found in Wesgo-alumina and AlN. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The overall objective of this research work was to prepare hydrocracking catalysts using amorphous silica-alumina (ASA) supports in combination with USY and {beta}-zeolites. Three supports: namely silica-alumina, USY and {beta}-zeolites were selected to prepare the extrudates using AP-1 as a binder, while two metal pairs: namely Ni-W and Ni-Mo were loaded on the extrudates through co-impregnation using incipient wetness technique. The catalysts were then calcined at 550C for 2h. The catalysts were tested in a fixed-bed flow reaction system for their activity, using desulfurized vacuum gas oil (DS-VGO) as a feedstock. The catalytic evaluation results of the catalysts showed that {beta}-zeolite alone and in combination with the ASA used in this study, has a potential as a support for developing heavy oil hydrocracking catalysts. A balance of weak and strong acidities of {beta}-zeolite provides control cracking, while high surface area and bigger ...

International Nuclear Information System (INIS)

The prospect for the recovery of rare earths from red mud, the bauxite tailings from the production of alumina is examined. The Jamaican red mud by far has the higher trace concentrations of lanthanum, cerium, neodymium, and yttrium. Scandium is also present. The dissolution of the rare earth is a major extraction problem because of the large volume of other materials. The recovery processes that have been proposed include the production of co-products such as iron, alumina, and titanium concentrates, with the rare earths going with the titanium. In this paper a critical examination of the possible processes are presented with the recommended research projects to be carried out.

Science.gov (United States)

An inner surface substrate of metal tubes is provided with a single layer of randomly distributed metal bodies bonded to the substrate, spaced from each other, and substantially surrounded by the substrate to form body void space.

Energy Technology Data Exchange (ETDEWEB)

In this work, the thermal performance of a conventional collector is improved by inserting porous substrates at the inner walls of the collector tubes. The porous substrates improve the convective heat transfer coefficient between the tube wall and the fluid. This improvement is investigated numerically and its effects on the efficiency and the useful gain of the collector are evaluated. It is found that inserting the porous substrate may raise the collector efficiency considerably, especially at high values of the overall heat loss coefficient.

International Nuclear Information System (INIS)

During 1993 and 1994 a working group of biologists operating in Region Lombardia has carried out a study to evaluate the reliability of artificial substrates in the assessment of water quality by the Extended Biotic Index. Macroinvertebrate samples were collected by means of hand net and artificial substrates (up to 3 replicates) in 22 sampling sites of 15 watercourses of different typology (river, stream, irrigation channel) and water quality. Sampling efficiency and reliability in the calculation of E.B.I. and Quality Class by 1, 2 and 3 artificial substrates with respect to hand net have been evaluated. Influence of water quality, typology and original prevailing substrate in watercourses on the performance of artificial substrates has also been investigated. Results show a good agreement with other Authors' papers, confirming that artificial substrates ...

Science.gov (United States)

MILSTAR's Flexible Substrate Solar Array (FSSA) is an evolutionary development of the lightweight, flexible substrate design pioneered at Lockheed during the seventies. Many of the features of the design are related to the Solar Array Flight Experiment (SAFE), flown on STS-41D in 1984. FSSA development has created a substantial technology base for future flexible substrate solar arrays such as the array for the Space Station Freedom. Lessons learned during the development of the FSSA can and should be applied to the Freedom array and other future flexible substrate designs.

International Nuclear Information System (INIS)

Fine ceramic particles of zirconia toughened alumina (ZTA), titania toughened alumina (TTA), and zirconia-titania toughened alumina (ZTTA) have been synthesized by ultrasonic spray pyrolysis (USP) at various temperatures from starting salt solutions of various compositions aiming for the development of catalytic material. These particles were characterized for properties such as shape, size and size distribution, diffraction pattern, and chemical and phase composition of elements by scanning electron microscopy (SEM), particle size analyzer (PSA), x-ray diffraction (XRD), and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). Chemical compositions and sizes of ceramic composites have been controlled by the stoichiometry of salt solutions and the flow rate of spraying solutions. The optimum experimental conditions for the various composite particle synthesis have been proposed.

International Nuclear Information System (INIS)

Research highlights: #-># Morphological and chemical characterization at atomic scale of porous alumina layers anodised in ordered regimes. #-># Characterization based on the use of FEG-SEM, STEM-HAADF, STEM-EELS and STEM-X-EDS. #-># Nanoscale distribution of P-, C- and S-bearing species in the pore wall. - Abstract: Ordered porous alumina layers prepared by two-step anodising in phosphoric, oxalic and sulphuric acids have been characterized at sub-nanometer scale using electron microscopy techniques. FEG-SEM and STEM-HAADF images allowed estimating the pore size, cell wall and pore wall thicknesses of the layers. Nanoanalytical characterization has been performed by STEM-EELS and STEM-X-EDS. Detailed features of the spatial distribution of anions in the pore wall of the films have been obtained. Maximum concentration of P-species occurs, approximately, at the middle of the pore wall; adjacent to the pore for C-species, whereas the ...

Energy Technology Data Exchange (ETDEWEB)

An inorganic particulate adsorbent of a titania-alumina is described for treating a superheated water containing radioactive materials such as cobalt ions, which is free from release of corrosive impruities, and which has a high adsorption capacity of radioactive materials and a high mechanical strength is prepared by hydrolyzing a titanium alkoxide and an aluminum alkoxide, thereby forming a hydrous titanium oxide and a hydrous aluminum oxide, respectively; precalcining the hydrous titanium oxide and aluminum oxide, mixing and molding the resulting titania and alumina into a particulate mixture thereof having a titania mole fraction of 0.2 to 0.9, and calcining the particulate mixture at 500/sup 0/-700/sup 0/C. This absorbent is effectively used in treat boiling water-type nuclear reactor core-circulating water to remove radioactive substances therefrom.

International Nuclear Information System (INIS)

Highly ordered arrays of Ni nanoholes and Fe20Ni80 antidots have been prepared, respectively, by replica/antireplica processing and sputtering techniques using nanoporous alumina membranes as templates. Geometrical characteristics as nanohole/antidot diameter, interpore distance and the overall hexagonal symmetry of arrays are controlled through the original templates. Experimental data on their hysteresis and magnetic domain structure have been taken by vibrating sample magnetometry and magnetic force microscopy, respectively. An analysis of the magnetization process, resulting magnetic anisotropy and magnetic domain structure is summarized considering the influence of those geometry aspects. In particular, the hexagonal symmetry and the density of nanohole/antidots determine the overall magnetic behavior, which is of interest in future high-density magnetic storage systems.

Energy Technology Data Exchange (ETDEWEB)

Solid particle erosion (SPE) testing was made on Sandvik CRC 262 with different heat treatments and on the steels Type 321 and 15Mo3. The Studsvik Erofuge, a centrifugal erosion tester, was used and the testing was performed in air at room temperature. Alumina and olivine sand particles were used at a particle velocity of 60 m/s and at impingement angles of 60 degrees and 90 degrees. Differences in erosion resistance were obtained for CRC 262 depending on the heat treatment. Olivine sand resulted in lower erosion of CRC 262 than when using alumina. The particle type dependence is low for the other materials, Tp 321 and 15Mo3. CRC 262 has a slightly higher erosion resistance than Tp 321 and 15Mo3 and the differences are most pronounced when using olivine sand

International Nuclear Information System (INIS)

It is essential that alumina used for manufacturing electronic devices should contain an extremely low level of alpha-radiation. The principal source of alpha-radiation in alumina is uranium, a minor source being thorium. Uranium in bauxite dissolves into the liquor in the digestion process and is fixed to the red mud as the desilication reaction progresses. A part of uranium remaining in the liquor precipitates together with aluminum hydroxide in the precipitation process. The uranium content of aluminum hydroxide becomes lower as the precipitation velocity per unit surface area of the seed becomes slower. Organic matters in the Bayer liquor has an extremely significant impact on the uranium content of aluminum hydroxide. Aluminum hydroxide free of uranium is obtainable from the liquor that does not contain organic matters.

CERN Document Server

Residual Stresses in Ta, Mo, Al and Pd Thin Films Deposited by E-Beam Evaporation Process on Si and Si/SiO 2 Substrates

UK PubMed Central (United Kingdom)

The acetogenic bacterium Clostridium thermoaceticum ATCC 39073 grew at the expense of the two-carbon substrates oxalate and glyoxylate. Other two-carbon substrates (acetaldehyde, acetate,...Full Text Available

Science.gov (United States)

During Phase II multi-junction solar cell will be grown on the large grain thin film produced during Phase I on flexible/low cost metal foil substrate. ...

UK PubMed Central (United Kingdom)

BackgroundIn vitro data suggest that changes in myocardial substrate metabolism may contribute to impaired myocardial function in diabetic cardiomyopathy (DCM)....Full Text Available

Energy Technology Data Exchange (ETDEWEB)

This invention pertains to a Fischer Tropsch process for converting synthesis gas to an oxygenated hydrocarbon with particular emphasis on dimethyl ether. Synthesis gas comprising carbon monoxide and hydrogen are converted to dimethyl ether by carrying out the reaction in the presence of an alkali metal-manganese-iron carbonyl cluster incorporated onto a zirconia-alumina support.

Energy Technology Data Exchange (ETDEWEB)

A focused ion beam (FIB) system has been applied to prepare a thin foil specimen of Si, MgO and alumina which contained cracks in the plan of foil. It was possible to observe a much larger area at and near a crack tip than has been hitherto possible. FIB was also applied to observation of microstructure near a crack tip evolved during severe rolling contact fatigue in a steel.

International Nuclear Information System (INIS)

Load-deflection characteristics of alumina and alumino-silicate fibrous blankets were experimentally determined. Load retention and springback capability of combinations of these materials were measured in a 10,000-hour test at surface temperatures of 650 to 1000"0C (1200 to 1832"0F). Experimental results are presented and future testing plans are discussed.

Energy Technology Data Exchange (ETDEWEB)

This heat exchanger is a critical step in the development of the Externally Fired Combined Cycle power system, a direct-coal combustion power plant (gas turbine). SiC is the only material with the needed resistance to creep, thermal shock, and oxidation; however a protective coating is needed. Ten candidate materials were identified: alumina-based materials, materials stable with SiO, and low expansion materials. An initial screening study should be performed.

Science.gov (United States)

"Precision manufacture of ceramic parts with CNC machining capability for aerospace, lasers, semiconductors and other industries. Materials include alumina, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite and others. A.C.T. has seen the number of applications and demand for high-realiability ceramics (aluminum oxide, zirconia, glass, ferrites, silicon carbide, silicon nitride, sapphire, cordierite, mullite, etc...) increase continually within the aerospace, computer and the industrial markets."

Science.gov (United States)

There are about fifty SET domain protein methyltransferases (PMTs) in the human genome, that transfer a methyl group from S-adenosyl-L-methionine (SAM) to substrate lysines on histone tails or other peptides. A number of structures in complex with cofactor, substrate, or inhibitors revealed the mechanisms of substrate recognition, methylation state specificity, and chemical inhibition. Based on these structures, we review the structural chemistry of SET domain PMTs, and propose general concepts towards the development of selective inhibitors.

UK PubMed Central (United Kingdom)

The hydrogen bonding of ligated water in ferric, high-spin, resting-state substrate complexes of heme oxygenase from Neisseria meningitidis has been systematically perturbed...Full Text Available

International Nuclear Information System (INIS)

In this paper, the influence of plasma nitriding at temperature 720 deg. C for 20 h on the surface microstructure and interface microstructure of electroplated chromium coating was investigated. In these conditions, interdiffusion, mixing and reaction phenomena of elements originating from the substrate and coating material are more likely to occur, thus increasing the bonding strength between the coating and carbon steel substrate. The change of the structures from the substrate side to the coating surface, and the effect of the substrate steel on the interface structure were studied by cross-sectional transmission electron microscope observation (XTEM). The nitride layer formed on the surface was analyzed by X-ray diffraction method (XRD). After treatment at above conditions a 6-7 #mu#m thick nitride compound layer was formed in surface region and the same thick carbide compound layer was also formed ...

Energy Technology Data Exchange (ETDEWEB)

The effect of flame temperature on the Moza-Austin sticking test has been evaluated by increasing the adiabatic flame temperature used to melt the pellet and make it drop. It was found that the variation of apparent contact angle with substrate temperature, for an oxidized steel substrate, was almost independent of flame temperature over the range of 1750-2500 C. However, the strength of adhesion to the substrate increased with higher flame temperature at each substrate temperature. The adhesion force of a drop frozen on the substrate at constant temperature also increased with time up to about one h. This indicated that the adhesion was not caused solely by mechanical anchoring of solidified glass in the pores of the oxide layer. Reduction of the substrate temperature to lower temperatures after attachment of the drop caused lower strength of adhesion, but this ...

International Nuclear Information System (INIS)

Xe ion irradiation of NiSi, PdSi, and PtSi on Si was performed at various substrate temperatures. The phase formation and mixing behavior of the three monosilicides with their Si substrates are quite different. For NiSi, NiSi_2 was formed on amorphous Si substrates at 350 "0C, while NiSi remained stable on crystalline Si substrates even at 400 "0C. PtSi reacted with Si to form a metastable Pt_4Si_9 phase, which decomposed back to PtSi and Si by successive irradiation at higher temperatures. The decomposition of the metastable Pt_4Si_9 was easier on crystalline Si substrates than on amorphous substrates. No mixing was observed for PdSi on Si in the temperature range of 35--400 "0C. The ion mixing results were compared with those from thermal annealing. The importance of demixing of a thermally stable system was explored.

International Nuclear Information System (INIS)

The efficiency of the synthesized zeolite NaY from rice husk ash (RHA) in the removal of Cr(III) from aqueous solution was studied. Zeolite NaY was synthesized from RHA via seeding technique and the identification of its structure was done by X-ray Diffraction (XRD) technique and the elemental analysis was carried out by X-ray Fluorescence (XRF). The physicochemical properties which were related to the use of the zeolite NaY as a sorbent was also investigated. The synthesized zeolite NaY has higher cation exchange capacity (CEC) than the commercial zeolite NaY due to the higher amount of sodium content in the synthesized as well as the lower ratio of silica to alumina. The synthesized zeolite NaY together with the commercial one as comparison was used in the sorption of the Cr(III) in aqueous solution by batch sorption experiments. The kinetic study showed that the Cr(III) uptake by both zeolites were based on the pseudo second order model. Synthesized zeolite NaY ...

Science.gov (United States)

Catalytic reactions of 3-methylpentane and 2,3-dimethylbutane on HY, amorphous silica-alumina, and HZSM-5 have been studied at 500{degree}C. Both kinetic phenomena and product selectivities have been reported. Cracking reactions an HZSM-5 can be attributed to initiation through protonation occurring at Bronsted sites. Bimolecular processes leading to chain reaction via hydride transfer are restricted within the narrow pore pentasil zeolite. On HY and amorphous silica-alumina, initiation of cracking also occurs at Bronsted sited. No direct evidence was found for participation of Lewis acid sites on the catalyst framework itself. Following initiation, reactions on these catalysts are accelerated through a chain process occurring at Lewis sites generated by adsorption of product olefins at Bronsted sites. The resulting change in the dominant cracking mechanism is reflected in the product selectivity, illustrated here by a falling off in formation ...

Energy Technology Data Exchange (ETDEWEB)

Reductive quenching of two photoexcited ruthenium(II) complexes by an anionic electron donor, 2,2{prime}-azinobis(3-ethyl-benzothiazoline-6-sulfonate) (ABTS{sup 2{minus}}), in aqueous solution was examined by laser flash photolysis before and after adding positively charged colloidal (250-{angstrom} diameter) alumina-coated silica particles. The kinetics and quantum yields of electron transfer with an anionic sensitizer, RuL{sub 3}{sup 4{minus}} (L = bathophenanthroline disulfonate), and a cationic one, Ru(bpy){sub 3}{sup 2+} (bpy = 2,2{prime}-bipyridine), were compared. Coadsorption of ABTS{sup 2{minus}} and RuL{sub 3}{sup 4{minus}} by the particles greatly enhanced the rate of quenching such that only the reaction occurring on the surfaces of the particles was observed. Electron transfer from ABTS{sup 2{minus}} to RuL{sub 3}{sup 4-*} occurred by a static (nondiffusional) process, and the quenching efficiency was maximal when there was close to monolayer coverage ...

Energy Technology Data Exchange (ETDEWEB)

The NiMo sulfide supported on Ketjen Black (KB) was more effective and yielded lighter oil products containing light fractions with their boiling point below 300{degree}C during the two stage liquefaction combining low temperature and high temperature hydrogenation the conventional NiMo/alumina catalyst and FeS2 catalyst. Although the NiMo/alumina yielded increased oil products during the two stage liquefaction, the lighter oil fractions did not increase and the heavier fractions increased mainly. This suggests that the hydrogenation of aromatic rings and successive cleavage of the rings are necessary for producing the light oil, which is derived from the sufficient hydrogenation of aromatic rings using catalysts. For the two stage reaction with NiMo/KB catalyst, it was considered that sufficient hydrogen was directly transferred to coal molecules at the first stage of the low temperature reaction, which promoted the solubilization of coal and ...

International Nuclear Information System (INIS)

Kaolinite intercalated with potassium acetate is of great interest in the areas of environmental remediation and industrial application; however, its exact atomic structure and the changes which occur when heated have remained largely elusive. Here, neutron pair distribution function analysis is used to investigate the local structural characteristics of this complex material, revealing that hydrated potassium acetate exists as a single layer in the interlamellar spacing of kaolinite. Furthermore, the potassium ions within the intercalated complex are most likely associated with the resonance structure of the acetate molecules, and upon heating (and decomposition of the carbon containing molecules), these ions become strongly associated with the negative charge located on the oxygen atoms in the alumina layers of dehydroxylated kaolinite. Several possible orientations of hydrated potassium acetate within the interlamellar spacing of kaolinite have been proposed and ...

CERN Document Server

Volume sources is used for standard sources by radioactive measurement using Ge semiconductor detector of environmental sample, e.g. water, soil and etc. that require large volume. The commercial volume source used in measurement of the water sample is made of agar-agar, and that used in measurement of the soil sample is made of alumina powder. When the plastic receptacles of this two kinds of volume sources were damaged, the leakage contents cause contamination. Moreover, if hermetically sealing performance of volume source made of agar-agar fell, volume decrease due to an evaporation off moisture gives an error to radioactive measurement. Therefore, we developed the two type methods using unsaturated polyester resin, vinilester resin, their hardening agent and acrylicresin. The first type is due to dispersing the hydrochloric acid solution included the radioisotopes uniformly in each resin and hardening the resin. The second is due to dispersing the ...

International Nuclear Information System (INIS)

Red mud is a kind of alumina production, characterized by high content of fine-dispersion Fe, Al and Ti oxyhydrates; it is studied from the viewpoint of its application as a sorbent for Sr. The red mud specific surface constitutes 23-25 m"2/g, the density is of 3.3-3.4 g/cm"3 and the melting temperature is 1350-1370 deg C. It is established that the maximum sorption capacity of the red mud for strontium equals 420 #+-# 24 mg-eq/100 g. The red mud high sorption properties make it possible to recommend it as a sorbent by constructing technogenic barriers at the radioactive wastes disposal sites

Energy Technology Data Exchange (ETDEWEB)

Red mud, and red mud activated by dissolution in hydrochloric acid and reprecipitation with ammonia, were tested as catalysts for the hydrogenation of an anthracene oil in a trickle-bed reactor. Conversion data were determined for the different polyaromatic compounds in the anthracene oil. Red mud shows appreciable catalytic activity, which is enhanced by the activation. Although both red mud and activated red mud are less active than a commercial Ni-Mo/[gamma]-alumina hydrotreating catalyst, the difference in activity is smaller when conversion to hydroaromatics instead of total conversion of reactants is considered. 20 refs., 8 figs., 3 tabs.

Energy Technology Data Exchange (ETDEWEB)

PVD-chromium-nitride coated samples of substrates of the magnesium alloy AZ91hp and the roller and ball bearing steel 100Cr6 were investigated regarding structure, mechanical characteristics, adhesion and internal stresses. For the coatings the parameters layer thickness and substrate BIAS voltage were varied. Both substrate materials were coated in one lad. Results of the X-ray analysis of the internal stresses show significant differences between the coated magnesium and the coated steel substrates. In the case of the variation of the substrate BIAS voltage, for the coated steel a dependency of the internal stresses to coating parameters could be obtained. For the coated magnesium no dependency was recognizable. The coating structure was examined with scanning electron microscopy. Element depth profiles of the coated samples were performed with SIMS. (orig.)

Energy Technology Data Exchange (ETDEWEB)

We have researched several new focused ion beam (FIB) micro-fabrication techniques that offer control of feature shape and the ability to accurately define features onto nonplanar substrates. These FIB-based processes are considered useful for prototyping, reverse engineering, and small-lot manufacturing. Ion beam-based techniques have been developed for defining features in miniature, nonplanar substrates. We demonstrate helices in cylindrical substrates having diameters from 100 {micro}m to 3 mm. Ion beam lathe processes sputter-define 10-{micro}m wide features in cylindrical substrates and tubes. For larger substrates, we combine focused ion beam milling with ultra-precision lathe turning techniques to accurately define 25-100 {micro}m features over many meters of path length. In several cases, we combine the feature defining capability of focused ion beam bombardment with ...

International Nuclear Information System (INIS)

FT-IR spectra of the products obtained in each step of the tetramethyltin (TMT)/3-wt.% Re_2O_7/Al_2O_3-SiO_2 and TMT/Al_2O_3-SiO_2 system preparation are presented and discussed. The obtained spectra show that TMT reacts with alumina-silica hydroxyl groups already at room temperature, yielding surface methyltin compounds; NH_4ReO_4 reacts with alumina-silica surface at temperatures up to 423 K, yielding rhenium surface species and ammonia, which is strongly bonded by acidic sites of the Broensted kind. FT-IR spectrum of the system (TMT)/3-wt.% Re_2O_7/Al_2O_3-SiO_2 indicated the absence of surface methyl tin compounds observed on the surface system TMT/Al_2O_3-SiO_2 , and the presence of physically adsorbed TMT; after 5 h of evacuation of the TMT/3-wt.% Re_2O_7/Al_2O_3-SiO_2 system, the FT-IR spectrum indicated the presence of only a single band at 2977 cm"-"1, which may be assigned to the C-H bond stretching of the methyl group in the surface ...

Energy Technology Data Exchange (ETDEWEB)

The key component for improving the energy efficiency and cycle life of the electrically rechargeable zinc-air battery is the bifunctional air electrode. The air electrodes described in this paper contained different types of carbon black as the substrate for the perovskite catalyst (La{sub 0.6}Ca{sub 0.4}CoO{sub 3}). Morphological and physical properties of the carbon substrates play an important role in enhancing the activity and stability of the bifunctional air electrode. Current-potential curves and cycle-life tests were applied in order to gather information on the activity and stability of these electrodes. (authors)

Energy Technology Data Exchange (ETDEWEB)

Supercritical CO2 is used as a new solvent for immersion deposition, a galvanic displacement process traditionally carried out in aqueous HF solutions containing metal ions, to selectively develop metal films on featured or non-featured silicon substrates. Components of supercritical fluid immersion deposition (SFID) solutions for fabricating Cu and Pd films on silicon substrates are described along with the corresponding experimental setup and procedure. Only silicon substrates exposed and reactive to SFID solutions can be coated. The highly pressurized and gas-like supercritical CO2, combined with the galvanic displacement property of immersion deposition, enables the SFID technique to selectively deposit metal films in small features. SFID may also provide a new method to fabricate palladium silicide in small features or to metallize porous silicon.

International Nuclear Information System (INIS)

Manganese is a common contaminant of mine water and other waste waters. Due to its high solubility over a wide pH range, it is notoriously difficult to remove from contaminated waters. Previous systems that effectively remove Mn from mine waters have involved oxidising the soluble Mn(II) species at an elevated pH using substrates such as limestone and dolomites. However it is currently unclear what effect the substrate type has upon abiotic Mn removal compared to biotic removal by in situ micro-organisms (biofilms). In order to investigate the relationship between substrate type, Mn precipitation and the biofilm community, net-alkaline Mn-contaminated mine water was treated in reactors containing one of the pure materials: dolomite, limestone, magnesite and quartzite. Mine water chemistry and Mn removal rates were monitored over a 3-month period in continuous-flow reactors. For all substrates except ...

Energy Technology Data Exchange (ETDEWEB)

An ion processing element employing composite media disposed in a porous substrate, for facilitating removal of selected chemical species from a fluid stream. The ion processing element includes a porous fibrous glass substrate impregnated by composite media having one or more active components supported by a matrix material of polyacrylonitrile. The active components are effective in removing, by various mechanisms, one or more constituents from a fluid stream passing through the ion processing element. Due to the porosity and large surface area of both the composite medium and the substrate in which it is disposed, a high degree of contact is achieved between the active component and the fluid stream being processed. Further, the porosity of the matrix material and the substrate facilitates use of the ion processing element in high volume applications where it is desired to effectively process a high ...

UK PubMed Central (United Kingdom)

The bacterium Serratia marcescens produces a plethora of multicellular shapes of different colorations on solid substrates, allowing immediate visual detection of varieties. Such a...Full Text Available

UK PubMed Central (United Kingdom)

Succinyl(carbadethia)-coenzyme A, a synthetic substrate for adenosylcobalamin-dependent methylmalonyl-CoA mutase, has been prepared by a simplified procedure. When recombinant mutase was mixed with...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The bibliography contains citations concerning the structural properties of sputtered tantalum and tantalum compounds. The preparation of thin film capacitors and resistors is described. The electrical properties of the sputtered films are also included. The influence of the substrate on the properties of the coatings is considered, including adherence of the coating to the substrate, and the effects of impurities on coating integrity. (Contains 250 citations and includes a subject term index and title list.)

International Nuclear Information System (INIS)

Fe and Zn were determined in various parts of maize (Zea mays) in dependence on quantity of organic substrate EKOFERT as organic fertilizer in soil, using radionuclide X-ray fluorescence analysis. The increase of quantity of organic substrate EKOFERT in soil causes a decrease of heavy metal concentrations in certain parts of the plant. (author). 4 refs., 1 tab.

International Nuclear Information System (INIS)

We report a new method of generating nano and micro patterns using focused ion beam (FIB) induced adhesion. The method utilizes selective irradiation of thin metallic films grown on substrates by focused ion beam followed by peel off. After peel off of the irradiated thin film it is observed that the ion beam scanned portions are retained on the substrate, creating nano and micro patterns. The method is suitable for materials of which the adhesion to the substrate can be improved by ion bombardment. The phenomenon has been demonstrated by creating gold nano patterns of different shapes and sizes ranging from 500 nm to 5 #mu#m on SiO_2-Si substrate using 10-30 keV Ga FIB at beam currents up to 10 pA. The mechanism involved in the process has been discussed. The technique could be utilized to prepare micro and nano patterns of thin films deposited on an appropriate substrate for ...

Energy Technology Data Exchange (ETDEWEB)

GaAs material and device structure optimization studies on optical-grade, millimeter-and-less grain-size polycrystalline Ge substrates are presented. We discuss the growth of high-quality epitaxial layers across various crystalline orientations of a polycrystalline substrate; this is important for obtaining high-performance solar cells. The GaAs solar cell on n-type poly-Ge substrate is a p-on-n type, with an undoped spacer between the p-emitter and the n-base. An experimental study of dark currents in these junctions, with and without the spacer, as a function of temperature (77K to 288K) is presented; this study suggests that the spacer reduces the tunneling contribution to dark current. In addition, we describe device-structure optimization studies that have led us to achieve an open-circuit voltage (V{sub oc}) exceeding 1 Volt and an AM1.5 efficiency of {approximately}19{percent} for a 4-cm{sup 2}-area GaAs cell on ...

Energy Technology Data Exchange (ETDEWEB)

For a new and practical {sup 99m}Tc generator using not (n, f){sup 99}Mo, but (n, {gamma}){sup 99}Mo, an inorganic polymer adsorbent framed with oxygen-zirconium-chlorine bonds with a high adsorption performance of Mo has been developed; the polymer adsorbent was named PZC. The amounts of {sup 99}Mo (Mo) adsorbed are stably more than 250 mg/g(PZC). But, the current experiments with 0.5 MBq to 1.85 GBq of {sup 99}Mo gave a subject that the breakthrough of {sup 99}Mo in the elution of {sup 99m}Tc from the adsorbent was 0.05-0.5 %, although the breakthrough of Zr was less than the detection limit of 5 x 10{sup -2} mg(Zr) to 1 g of PZC, and {sup 99m}Tc was eluted constantly with 78{+-}4%. To apply the adsorbent as a generator commercially in Japan, the {sup 99}Mo breakthroughed from the generator must be suppressed to less than 0.15 kBp({sup 99}Mo)/MBq({sup 99m}Tc) by law which is equivalent to 0.015 %, and the {sup 99}Mo breakthrough is controlled practically to less than 10{sup -2} of ...

International Nuclear Information System (INIS)

Crystalline and non-crystalline iron oxide (#alpha#-Fe_2O_3) thin films were obtained by spray pyrolysis onto glass substrate at different temperatures. The results of X-ray diffraction showed that with increasing the deposition time, the film structure changed from non-crystalline to crystalline at the same substrate temperature. At different substrate temperatures and low deposition times (5 min), iron oxide appears almost in non-crystalline form. With rising the substrate temperature and deposition time, the crystallinity was improved. The effect of substrate temperature as well as deposition time on the optical features (absorption coefficient and bandgap) and optical constants of these films has been investigated. Optical constants of the films were determined from spectrophotometric measurement of reflectance and transmittance. Analysis of the results showed that, for ...

Energy Technology Data Exchange (ETDEWEB)

The purpose of this investigation was to simulate a machining front from an abrasive waterjet and its movements in a ceramic material. Wear factors affecting the abrasive waterjet nozzle were also to be established. Therefore, a low inclination angle (9[degree]) was used between the nozzle and test sample, simulating a moving machine front. A standard nozzle with an inner diameter of 0.76 mm was used in the test, and it was placed close to the samples. The outer diameter of the abrasive nozzle was 9.5 mm. The high wear rate from abrasive waterjets makes it possible to machine hard ceramics-including dense alumina, titanium boride, silicon nitride, and composites-at high machining speeds.

International Nuclear Information System (INIS)

The extraction of rare earth elements, yttrium and aluminium from red mud resulting from alumina production with the ion-exchange resin KU-2-8n was studied. Experimental results are presented. The technology of hydrometallurgical processing of pulps obtained by sorption extraction of scandium from red mud is developed. It is shown that in the process of precipitation from sulfate sulfuric acid desorbate it became possible to obtain a high degree of rare earths deposition. The use of sodium hydroxide makes it possible to obtain a maximum deposition of rare earths and aluminium - 99.9 %. Aluminium leaching from crude composite concentrate gives a possibility to get concentrates which 15 - 20 times richer in yttrium and rare earths

British Library Electronic Table of Contents (United Kingdom)

In this paper, multilayer oxide nanorods were deposited in the nanopores of anodic aluminum oxide (AAO) via solution infiltration followed by heat treatment. The nanorods have a core-shell structure. First, the shell (nanotube) with the thickness of about 40nm was made of TiO"2 through the hydrolysis of (NH"4)"2TiF"6. Second, silver nanoparticles with the diameter of about 3nm were added into the TiO"2 layer through thermal decomposition of AgNO"3 at elevated temperatures. Then, cylindrical cores (nanorods) of CoO and ZnO with 200nm diameter were prepared, respectively. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and composition of the nanorods. UV-vis light absorption measurements in the wavelength range from 350 to...

Energy Technology Data Exchange (ETDEWEB)

Preliminary studies were preformed to determine whether thermal conductivity of cementitious grouts used to backfill heat exchanger loops for geothermal heat pumps could be improved, thus improving efficiency. Grouts containing selected additives were compares with conventional bentonite and cement grouts. Significant enhancement of grout alumina grit, steel fibers, and silicon carbide increased the thermal conductivity when compared to unfilled, high solids bentonite grouts and conventional cement grouts. Furthermore, the developed grouts retained high thermal conductivity in the dry state, where as conventional bentonite and cement grouts tend to act as insulators if moisture is lost. The cementitious grouts studied can be mixed and placed using conventional grouting equipment.

Energy Technology Data Exchange (ETDEWEB)

This patent describes a method of reducing the hydrogen sulfide level in streams containing hydrogen sulfide at concentrations from about 2 ppm up to about 1,000 ppm. It comprises reacting the hydrogen sulfide with an unsaturated hydrocarbon in the presence of an acidic solid catalyst selected from the group consisting of polymeric sulfonic acid resins, solid polyphosphoric acid, supported sulfuric acid, supported boric acid, silica-aluminas, clays, faujasite, mordenite, and L, omega, X or Y zeolites at mercaptan-forming concentrations, and recovering a stream having a reduced hydrogen sulfide concentration and containing no more than 5 ppm hydrogen sulfide.

British Library Electronic Table of Contents (United Kingdom)

The tribological properties of gas pressure sintered SiAlON and its composite with 18wt% silicon carbide (SiC) against two different mating materials, i.e., alumina and SiAlON are evaluated. SiAlON and SiAlON-18%SiC composite ceramics were prepared by pressure less sintering and gas pressure sintering. Fretting wear tests were carried out under dry unlubricated ambient conditions (room temperature 23-25^oC; relative humidity 50-55%) with a load of 8N for 45,000 cycles. Friction and wear properties of SiAlON-SiC proved better than the monolithic SiAlON. The formation of silica roll like structure on the composite worn surface was observed.

British Library Electronic Table of Contents (United Kingdom)

In this project, nanocrystalline SnO2 powders were successfully prepared by (a) citrate sol-gel and (b) direct precipitation methods. Powders were characterized using thermal analysis techniques (DTA-TG-DSC), X-ray powder Diffraction (XRD), surface area (BET) and electrical conductivity measurements. XRD patterns showed the presence of the cassiterite structure. SnO2 particles, prepared through sol-gel method exhibit crystallite sizes in the range from 3.1 to 22.3 nm when the gel is heat treated at different temperatures up to 900?C. SnO2 nanocrystallites prepared by the precipitation method are comparatively larger in size. The higher specific surface area was obtained for the powder prepared using sol-gel method and the obtained average grain size (d) is relatively large compared with th...

Energy Technology Data Exchange (ETDEWEB)

A pillbox RF output window was developed for the L-band pulsed klystron for the Japanese Hadron Project (JHP) 1-GeV proton linac. The window was designed to withstand a peak RF power of 6 MW, where the pulse width is 600 {mu}sec and the repetition rate is 50 Hz. A high power model was fabricated using an alumina ceramic which has a low loss tangent of 2.5x10{sup -5}. A high power test was successfully performed up to a 113 kW RF average power with a 4 MW peak power, a 565 {mu}sec pulse width and a 50 Hz repetition rate. By extrapolating the data of this high power test, the temperature rise of the ceramic is estimated low enough at the full RF power of 6 MW. Thus this RF window is expected to satisfy the specifications of the L-band Klystron. (author).

Energy Technology Data Exchange (ETDEWEB)

Decontamination and decommission activities related to the Molten Salt Reactor Experiment (MSRE) involve the trapping and recovery of radiolitically generated uranium hexafluoride and fluorine. Although fission product radiolysis was known to generate F{sub 2}, the formation of UF{sub 6} and its transport from the fuel salt was unexpected. Some of these gaseous radiolysis products have been moving through the gas piping to a charcoal bed since the reactor was shut down in 1969. Current and planned remediation and clean-up activities involve the trapping of the gaseous products, deactivation and treatment of the activated charcoal bed, stabilization and reconditioning of the fuel salt, and recovery of the uranium. The chemical aspects of these processes, including radiolytic generation mechanisms, reactions between uranium hexafluoride and fluorine and trapping materials such as activated charcoal, activated alumina, and sodium fluoride, along with the analytical ...

International Nuclear Information System (INIS)

Interest in making complex net-shape ceramic parts with good surface finishing and sharp tolerances without machining is a driving force for studying the injection molding technique. This method consists of softhening the ceramic material by means of adding some plastic and heating in order to inject the mixture under pressure into a relatively cold mold where solidification takes place. Essentially, it is the same process used in thermoplastic industry but, in the present case, the ceramic powder load ranges between 80 to 90 wt.%. This work shows results obtained from the fabrication of pieces of different ceramic materials (alumina, barium titanate ferrites, etc.) in a small scale, using equipments developed and constructed in the laboratory. (Author).

Energy Technology Data Exchange (ETDEWEB)

Papers presented at the workshop include: the longterm viability of mined land in Queensland; the determination and achievement of rehabilitation objectives: a state government objective; monitoring native vegetation in regenerated bauxite mines at Weipa: a belt transect method; rehabilitation strategies at the Collinsville open cut coal mine; the alteration of the environment by the construction and operation of the coal export facility at Abbot Point; some aspects of the premining environment at Collinsville; the prospects for long term revegetation of acid coal mine spoil and reject materials; recovery and stability in disturbed and artificially revegetated plant communities: a theoretical viewpoint; revegetation in the arid tropics: Mount Isa Mines' experience; Nabralek and its rehabilitation; rehabilitation and management strategies for acid mine wastes; the purpose and design of water quality monitoring networks at mine sites; Worsley alumina project ...

British Library Electronic Table of Contents (United Kingdom)

Bilayers of pure palladium and gold films were evaporated alternatively on (100) and (111) monocrystalline silicon substrates. After annealing, in a vacuum furnace from 100 to 650degreeC during 30min, the growth sequence of the Pd2Si and PdSi phases that evolved as the result of the diffusion reaction was examined by means of Rutherford backscattering spectrometry (RBS), X-ray diffraction (XRD), whereas the surface morphology was investigated by scanning electron microscopy (SEM) technique. The effect of the intermediate gold layer is investigated in order to test its effectiveness as barrier for Cu and Si atoms interdiffusion and its influence on the morphology of the formed palladium silicides. The effect of substrate orientation on the palladium silicides growth and formation was also e...

International Nuclear Information System (INIS)

Rapid self-aggregation of Ni nanodots on Si substrate covered with a thin SiO_2 buffered layer is investigated. The Ni nanodots can hardly self-aggregate on highly heat-dissipated Si substrate with a thermal conductivity of 148 W/m K. Adding a 200-A-thick SiO_2 buffer with an ultralow thermal conductivity of 1.35 W/m K prevents the formation of NiSi_2 compounds, enhances the heat accumulation, and releases the adhesion at Ni/Si interface, which greatly accelerates the self-assembly of Ni nanodots. Dense Ni nanodots with size and density of 30 nm and 7x10"1"0 cm"-"2, respectively, can be formatted after rapid thermal annealing at 850 deg. C for 22 s.

International Nuclear Information System (INIS)

Chromium nitride thin films were deposited on SA-304 stainless steel substrates by using direct-current reactive magnetron sputtering. The influence of process conditions such as nitrogen content in the fed gas, substrate temperature, and different sputtering gases on microstructural characteristics of the films was investigated. The films showed (200) preferred orientation at low nitrogen content (< 30%) in the fed gas. The formation of Cr_2N and CrN phases was observed when 30% and 40% N_2 were used, with a balance of Ar, respectively. Field emission scanning electron microscopy and atomic force microscopy were used to characterize the morphology and surface topography of the thin films, respectively. Microhardness tests showed a maximum hardness of 16.95 GPa for the 30% nitrogen content.

Energy Technology Data Exchange (ETDEWEB)

Epitaxial films grown pseudomorphically on substrates provide a way to stabilise non-equilibrium structures of materials. Obviously, there always is a certain lattice misfit between substrate and film material in its bulk equilibrium structure. In the pseudomorphic regime, this misfit can either lead to the growth of films in a strained bulk structure or even yield structures that are not stable in the bulk. Large misfits do not necessarily imply large lateral stress. Theory can help to predict e.g. geometry, stress and magnetic properties of pseusomorphically grown metal films. In this work, we considered the fcc-bcc epitaxial Bain path of 3d, 4d, and 5d transition metals, which provides a reasonable description of tetragonally distorted films on substrates. We carried out density functional calculations in the implementation of the full potential local orbital program package FPLO. Emphasis is put on similarities among ...

British Library Electronic Table of Contents (United Kingdom)

Thioredoxin reductase (TrxR) isoforms play important roles in cell physiology, protecting cells against oxidative processes. In addition to its endogenous substrates (Trx isoforms), hepatic TrxR can reduce organic selenium compounds such as ebselen and diphenyl diselenide to their selenol intermediates, which can be involved in their hepatoprotective properties. Taking this into account, the aim of the present study was to evaluate the hypothesis that ebselen, diphenyl diselenide and its analogs (4,4'-bistrifluoromethyldiphenyl diselenide, 4,4'-bismethoxydiphenyl diselenide, 4.4'-biscarboxy-diphenyl diselenide, 4,4'-bischlorodiphenyl diselenide, 2,4,6,2',4',6'-hexamethyldiphenyl diselenide) could be substrates of rat brain TrxR. In the presence of partially purified rat brain TrxR, dipheny...

Energy Technology Data Exchange (ETDEWEB)

In this work, we investigated self-heating related instability in polysilicon thin film transistors (poly-Si TFTs) fabricated on polyimide (PI) substrates. Indeed, when Joule heating becomes relevant, the temperature of the active layer can substantially rise, since the devices are fabricated on thermally insulating substrates. As a result, electrical instability is triggered and attributed to the generation of interface states, due to the Si-H bond breaking, and charge trapping into the gate insulator. In addition, by using 3-dimensional numerical simulations, coupling the thermodynamic and transport models, we analyzed the temperature distribution of the device under operating conditions and found that self-heating is more severe for devices fabricated on plastic substrates.

International Nuclear Information System (INIS)

Biaxially textured tungsten nanorods (A15 crystal structure) have been grown by oblique angle DC magnetron sputtering using a novel rotation mode called 'two-step rotation'. In this mode, the substrate is given a fast rotation through 1800 at 90 rpm and this is followed by a rest period of 30 s. These nanorods are vertically aligned and have a [100] texture normal to the substrate along with preferential in-plane texture as shown by x-ray pole figure analysis. In contrast, the tungsten nanorods obtained without substrate rotation are slanted at an angle of ?450 and have a [100] texture tilted 160 with respect to the substrate normal. The flux is incident from two diametrically opposite points on the sample at an oblique angle, averaging out the growth into vertical columns that retain the in-plane texture. Scanning electron microscopy shows that the tungsten nanorods have a mixture of {211} and {421} ...

Energy Technology Data Exchange (ETDEWEB)

Sucrose phosphate synthase (SPS) catalyzes the transfer of a glycosyl group from an activated donor sugar, such as uridine diphosphate glucose (UDP-Glc), to a saccharide acceptor D-fructose 6-phosphate (F6P), resulting in the formation of UDP and D-sucrose-6'-phosphate (S6P). This is a central regulatory process in the production of sucrose in plants, cyanobacteria, and proteobacteria. Here, we report the crystal structure of SPS from the nonphotosynthetic bacterium Halothermothrix orenii and its complexes with the substrate F6P and the product S6P. SPS has two distinct Rossmann-fold domains with a large substrate binding cleft at the interdomain interface. Structures of two complexes show that both the substrate F6P and the product S6P bind to the A-domain of SPS. Based on comparative analysis of the SPS structure with other related enzymes, the donor substrate, nucleotide diphosphate glucose, ...

UK PubMed Central (United Kingdom)

ATP-binding cassette transporters (ABC transporters) utilize the energy of ATP hydrolysis to translocate an unusually diverse set of substrates across cellular membranes. ABCA4, also known as...Full Text Available

UK PubMed Central (United Kingdom)

In vivo short-term effects of recombinant human TNF-alpha on lipolysis, FFA flux, fat oxidation, triglyceride-fatty acid cycling, and glucose kinetics were evaluated with stable isotopic tracers and...Full Text Available

UK PubMed Central (United Kingdom)

A structurally conserved element, the trigger loop, has been suggested to play a key role in substrate selection and catalysis of RNA polymerase II (pol II) transcription elongation. Recently resolved...Full Text Available

UK PubMed Central (United Kingdom)

Compliance mismatch is a significant challenge to long-term patency in small-diameter bypass grafts because it causes intimal hyperplasia and ultimately graft occlusion. Current engineered grafts...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

One of the most challenging topics in the area of organic electronic devices is the growth of transparent electrodes onto flexible polymeric substrates that will be characterized by enhanced conductivity in combination with high optical transparency. An essential aspect for these materials is their synthesis and/or microstructure which define the transparency, the stability and the interfacial chemistry which in turn determine the performance and stability of the organic electronic devices, such as organic light emitting diodes, organic photovoltaics, etc. In this work, we will discuss the latest advances in the growth of organic (e.g. PEDOT:PSS) and inorganic (e.g. zinc oxide-ZnO, indium tin oxide-ITO) conductive materials and their deposition onto flexible polymeric substrates. We will compare the optical, structural, nano-mechanical and nano-topographical properties of the inorganic and organic materials and we investigate the effect of ...

Science.gov (United States)

A film of GaSb grown epitaxially on a Si substrate is a direct transition semiconductor useful for application as a light source in Si photonics and channel material in next-generation field effect transistors because its energy bandgap is close to the optical fibre communication wavelength and it possesses high carrier mobility. Here, we report a novel method for heteroepitaxial growth of high-quality GaSb/Si films, despite having a lattice mismatch as large as ? 12%, using elastically strain-relaxed GaSb nanodots with ultrahigh density as seed crystals for film growth. The nanodot seed crystals were grown epitaxially by restricted contact with the Si substrate through nanowindows in an ultrathin SiO(2) film on the Si substrate. A light-emitting diode containing GaSb/Si films with a thickness of ? 90 nm fabricated by this method operated at room temperature. The growth method was also used to fabricate AlGaSb films of high ...

UK PubMed Central (United Kingdom)

Flavone and isoflavone phytoestrogens are plant chemicals and are known to be competitive inhibitors of cytochrome P450 aromatase with respect to the androgen substrate. Aromatase is the enzyme that...Full Text Available

UK PubMed Central (United Kingdom)

Many lifespan-modulating genes are involved in either generation of oxidative substrates and end-products, or their detoxification and removal. Among such metabolites, only lipoperoxides have the ability...Full Text Available

UK PubMed Central (United Kingdom)

RNase BN, the Escherichia coli homolog of RNase Z, was previously shown to act as both a distributive exoribonuclease and an endoribonuclease on model RNA substrates and to be inhibited...Full Text Available

CERN Document Server

Non-evaporable thin film getters of various compositions have been produced by sputtering. Among about 20 materials which have been studied, the lowest activation temperature (about 180 degree C) has been displayed by a Ti-Zr-V coating obtained from a cathode made of intertwisted elemental wires. In order to optimize the vacuum properties of this film various production parameters, including the substrate temperature during coating, have been varied. The films have been characterized by pumping speed measurement, secondary electron microscopy, and X-ray diffraction. It has been found that the substrate coating temperature affects significantly the activation temperature, the pumping speed and the gas surface capacity. The highest pumping speed values, obtained for substrate coating temperatures of 250 degree C and 300 degree C, are clearly correlated with the increased surface roughness and porosity of the Ti-Zr-V film.

UK PubMed Central (United Kingdom)

During the treatment of neonatal apnea, formula-fed infants, compared to breastfed infants, show nearly three-fold increase in clearance of caffeine, a substrate...Full Text Available

UK PubMed Central (United Kingdom)

The intramembrane aspartyl protease γ-secretase plays a fundamental role in several signaling pathways involved in cellular differentiation and has been linked with a variety of human diseases,...Full Text Available

UK PubMed Central (United Kingdom)

Rapid place encoding by hippocampal neurons, as reflected by place-related firing, has been intensely studied, whereas the substrates that translate hippocampal place codes into behavior have received...Full Text Available

UK PubMed Central (United Kingdom)

Trypanothione reductase (TryR) is a key enzyme involved in the oxidative stress management of the Trypanosoma and Leishmania parasites, which helps to maintain an intracellular reducing environment...Full Text Available

UK PubMed Central (United Kingdom)

Macrophage phagocytosis is an essential biological process in host defense and requires large amounts of energy. To date, glucose is believed to represent the prime substrate for ATP production in macrophages....Full Text Available

UK PubMed Central (United Kingdom)

The purpose of this study was to evaluate the relationship of respiratory quotient (RQ), a surrogate marker of substrate oxidation, as well as body composition and dietary intake to resting...Full Text Available

UK PubMed Central (United Kingdom)

Zipper-interacting protein kinase (ZIPK) is a member of the death-associated protein kinase family associated with apoptosis in nonmuscle cells where it phosphorylates myosin regulatory light chain...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

In order to understand the anodic behaviour of Al--Mo and Al--W amorphous alloys in the borate buffer electrolyte, samples of these alloys were polarized galvanostatically. The resultant anodic films were thicker than the passive films formed during potentiodynamic polarization enabling detailed examination of the films and alloy substrates by surface analytical methods. AES investigations suggest that the anodic films formed at low and moderate voltages on Al--Mo or Al--W amorphous alloys consist of Al-oxide, whereas refractory metals remain unoxidized and enriched at the film/substrate interface. Molybdenum and tungsten act as 'dissolution moderators', restraining the substrate dissolution process at the film/substrate interface. However, after anodization at high voltages (50 V), AES revealed the presence of an oxidized refractory metal in the inner part of the anodic film. Based on ...

UK PubMed Central (United Kingdom)

Ataxin-3, the protein involved in Machado-Joseph disease, is able to bind ubiquitylated substrates and act as a deubiquitylating enzyme in vitro, and it has been involved in the modulation of protein...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Two families of CeO{sub 2}/Al{sub 2}O{sub 3} (ACE) catalyst supports, containing 3 and 20 % wt CeO{sub 2} respectively, have been examined and compared with the pure oxides CeO{sub 2} and (transition-phase) Al{sub 2}O{sub 3}. Structural data indicate that, also in the presence of CeO{sub 2}, the Al{sub 2}O{sub 3} support undergoes all phase transitions at the usual temperatures. Electron micrographs show that particles morphology and crystals size are mainly imposed by the Al{sub 2}O{sub 3} support. The porosimetric texture indicates a more pronounced meso-porosity in the ACE systems than in pure Al{sub 2}O{sub 3}, especially in the case of low CeO{sub 2} loadings. FTIR spectra and volumetric/calorimetric data of the adsorption of CO at {approx}300 K show that the surface Lewis acidity of aluminas is severely modified by the presence of CeO{sub 2}: the overall CO uptake is increased, there is the formation of one additional family of Lewis acid sites (Ce{sup 4+} ...

International Nuclear Information System (INIS)

Research highlights: #-># Red mud residues (RM) were disposed in alumina production. #-># Utilization of Red mud residues was affected by its iron content. #-># Superconducting magnetic separation (HGSMS) was used in iron separation from RM. #-># RM with high and low iron contents were separated in HGSMS. - Abstract: The disposal of bayer red mud tailings now seriously threats the environment safety. Reduction and recycling of red mud is now an urgent work in aluminum industry. High gradient superconducting magnetic separation (HGSMS) system was applied to separate the extreme fine RM particles (<100 #mu#m) into high iron content part and low iron content part. Two sorts of RM were fed in the HGSMS. The iron oxide contents in concentrates were about 65% and 45% when RM 1 and RM 2 were fed respectively. Meanwhile, the residues contained 52.0% or 14.1% iron oxide in residues after eight separation stages when RM 1 and RM 2 were fed respectively. The ...

Energy Technology Data Exchange (ETDEWEB)

The properties of a helium film on the surface of solid parahydrogen are investigated. It is shown that wetting of the solid hydrogen by the liquid helium occurs. The transport velocities along the He II film on the solid parahydrogen surface are measured in broad temperature, film height, and level difference ranges. It is shown that the transport velocity in this case has the least value as compared with its value on other substrates. The thickness of the helium-saturated film is determined on the solid hydrogen surface on the basis of the data obtained, and the value is in good agreement with the results of a computation performed within the framework of the Frenkel' theory.

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

Science.gov (United States)

By gas-source molecular-beam epitaxy, we obtained a device-quality GaInP epitaxial layer lattice matched to (100)-GaAs substrates, with a photoluminescence efficiency comparable to that of a crystal grown by liquid-phase epitaxy. A GaInP/AlInP double heterostructure laser with a GaInP active layer was fabricated, and pulsed lasing operation was achieved at room temperature for, we believe, the first time.

Energy Technology Data Exchange (ETDEWEB)

There is increasing demand to functionalize meso- and nano-porous materials by coating and make the porous substrate biocompatible or environment friendly. However, coating on a meso-porous substrate poses great challenges, especially if the pore aspect ratio is high. In the current work the pulsed laser deposition (PLD) method is used for coating Ni{sub 3}Al-based meso-porous membranes with diamond-like carbon (DLC) layers of high thickness homogeneity and adhesion. (orig.)

Science.gov (United States)

Adenine DNA glycosylase catalyzes the glycolytic removal of adenine from the promutagenic A {center_dot} oxoG base pair in DNA. The general features of DNA recognition by an adenine DNA glycosylase, Bacillus stearothermophilus MutY, have previously been revealed via the X-ray structure of a catalytically inactive mutant protein bound to an A:oxoG-containing DNA duplex. Although the structure revealed the substrate adenine to be, as expected, extruded from the DNA helix and inserted into an extrahelical active site pocket on the enzyme, the substrate adenine engaged in no direct contacts with active site residues. This feature was paradoxical, because other glycosylases have been observed to engage their substrates primarily through direct contacts. The lack of direct contacts in the case of MutY suggested that either MutY uses a distinctive logic for substrate recognition or that the X-ray structure had ...

Energy Technology Data Exchange (ETDEWEB)

Bulk micromachining generally refers to processes involving wet chemical etching of structures formed out of the silicon substrate and so is limited to fairly large, crude structures. Surface micromachining allows intricate patterning of thin films of polysilicon and other materials to form essentially two-dimensional layered parts (since the thickness of the parts is limited by the thickness of the deposited films). There is a third type of micromachining in which the part is formed by filling a mold which was defined by photolithographic means. Historically micromachining molds have been formed in some sort of photopolymer, be it with x-ray lithography (``LIGA``) or more conventional UV lithography, with the aim of producing piece parts. Recently, however, several groups including ours at Sandia have independently come up with the idea of forming the mold for mechanical parts by etching into the silicon substrate itself. In Sandia`s mold ...

International Nuclear Information System (INIS)

Red mud (RM) is the main by-product of the Bayer process for alumina extraction from bauxite, and grey slurries (GS) are generated during the granite rocks transformation processes. the huge volume of those wastes generated every year suppose a serious environmental problem. Recent works by our group demonstrate the efficiency of both types of muds as corrosion inhibitors for iron and steel in alkaline media containing chlorides. The elemental analysis of these slurried shows that Al"3+ is the main common element. Therefore, the aim of this paper is to study the effect of the soluble Al"3+ in the electrochemical behaviour of iron in alkaline media, in presence and absence of chlorides. The electrochemical study using Cyclic Voltammetry (CV) and Electrochemical Impedance Spectroscopy (EIS) together with surface analysis techniques allowed to conclude that Al"3+ blocks the surface of steel in alkaline media chloride increasing the steel resistance to chlorides ...

Energy Technology Data Exchange (ETDEWEB)

Red mud, which is a pollutant residue from the extraction of alumina from bauxite ore, was utilized as an additive to a well blended mixture of three Egyptian clays, feldspar, quartz and grog. This was added in gradual proportions to study its effect on the vitrification properties of fired samples. Samples were moulded under a pressure of 20.7 MPa and fired at temperatures ranging from 950 C to 1100 C for soaking periods up to three hours. Compressive strength was determined as function of percent red mud added and firing temperature. A semi-exponential relation was established between strength and apparent porosity. 50 x 50 mm tiles containing 70% red mud addition and fired at 1100 C for one hour were tested. They were found to match the standards required for glazed wall tiles bodies. Tiles fired at 1100 C for 3 hours were compatible with the standards for glazed floor tiles. (orig.)

International Nuclear Information System (INIS)

The effect is reported of seven inorganic oxide additives on both the formation mechanism and the densification of X-Sialon prepared by a silicothermal process. The oxides were added to the starting mixture of halloysite clay, alumina and elemental silicon at a level of 1 wt% of the calculated final product, and fired in nitrogen at 1200-1500 deg C. The formation of X-Sialon was monitored by thermal analysis, powder XRD and 2"7"Al and "2"9Si solid state MAS NMR The effects of the additives are temperature dependent and influence the various stages of the reaction by differing degrees. The oxides which best promote the formation of crystalline X-Sialon (Y_2O_3, CaO and MgO) are also those which facilitate the conversion of initially-formed Si_3N_4 to SiO_2N_2 and SiO_3N units. Densification is most enhanced by Y_2O_3 CaO and CeO_2; MgO exerts its maximum effect on sintering at lower temperatures. Copyright (1998) Australasian Ceramic Society

Energy Technology Data Exchange (ETDEWEB)

The bulk of the results from this project, besides being found in the research reports, are in the form of two theses presented for advanced degrees by two different students at two different institutions. Francis E. Porbeni is a Master`s Degree student in Chemistry at Clark Atlanta University and has prepared his Master`s Thesis entitled Simultaneous SO{sub 2} Oxidation and NO Decomposition over Copper Oxide on {gamma}-Alumina Catalysts: An Infrared Diffuse Reflectance Study. Sumit Rao, a Ph.D. student in Chemical Engineering at the Georgia Institute of Technology has defended his thesis entitled Role of Copper Ensemble Size in Silica and Zeolite Supported Catalysts for Nitric Oxide Decomposition. These two documents, which will be forwarded when final copies are available, provide the details of the bulk of the research accomplished over the duration of this project. These two documents are summarized, and other results from the project are given.

British Library Electronic Table of Contents (United Kingdom)

Electrodeposition of tertiary alumina/yttria/carbon nanotube (Al2O3/Y2O3/CNT) nanocomposite by using pulsed current has been studied in this investigation. Coating process has been performed on nickel sulphate bath and nanostructure of obtained compound layer is examined with high precision figure analysis of SEM nanographs. The effects of process variables, i.e., Y2O3 concentration, treatment time, frequency and duty cycle, have been experimentally studied. Statistical methods are used to achieve the minimum of corrosion rate and average size of nanoparticles. Finally the contribution percentage of different effective factors is revealed and confirmation run shows the validity of obtained results. Also it has been revealed that by changing the size of nanoparticles, corrosion properties o...

International Nuclear Information System (INIS)

This study presents a rapid and selective method for the recovery of lanthanides and yttrium, existing in economically interesting concentrations, from red mud, the byproduct of the alumina production. The leaching process is based on the extraction of these elements with diluted nitric acid from red mud under moderate conditions and without using any preliminary treatment. Several parameters such as leaching agents, contact time, temperature, pressure and solid to liquid ratio were investigated in order to achieve an optimum recovery. The process followed here was selected taking into account its efficiency for the selective recovery of yttrium and lanthanides, but also its suitability for the subsequent liquid-liquid extraction of the leaching solution for the separation of the individual lanthanides. The achieved recovery percentages were for Y about 90%, for the investigated heavy lanthanides (Dy, Er, Yb) up to 70%, for the middle ones (Nd, Sm, Eu, Gd) up to ...

International Nuclear Information System (INIS)

In 2001, EFDA has assigned to ENEA a contract for the thermomechanical testing of six mock-ups of the ITER primary wall module. These small scale mock-ups, reproducing representative portions of the reference ITER primary wall panels, were fabricated during ITER EDA phase by solid hot isostatic pressing (HIPping) of an AISI 316L stainless steel back structure to a alumina dispersion strengthened (DS)-Cu alloy heat sink armored with beryllium tiles. The experimental program, carried-out at ENEA Brasimone CEF 1-2 thermal hydraulic facility, was focused on the thermal mechanical testing of these mock-ups aiming at verifying which tile geometry and manufacturing procedure assures the required reliability of the beryllium/DS-Cu alloy/SS joints at high incident heat flux (>0.8 MW/m"2) both at steady state and under thermal fatigue tests. The paper presents the progress in the experimental activity of the first test campaign and the main thermomechanical FEM analyses ...

Energy Technology Data Exchange (ETDEWEB)

Several configurations of moderating and shielding materials have been designed and measured on the LVR-15 reactor for boron neutron capture therapy (BNCT) purposes. To determine the neutron and gamma ray space-energy distributions in the cylindrical geometry, the two-dimensional code DOT with the coupled neutron-gamma data library DLC-36 was used. The experimental verification of the beam parameters was performed in the LVR-15 reactor thermal column empty space with layers of graphite, aluminium, alumina, lead and bismuth. Attention was paid to establishing techniques and instrumentation for monitoring the neutron and gamma ray dose and beam quality. The thermal and epithermal flux densities were measured by activation foils, the neutron spectrum was determined with a Bonner spectrometer and gamma ray background with a scintillation spectrometer. The distribution of thermal neutrons in the human head phantom was mapped with a small semiconductor detector (Si[sup ...

Energy Technology Data Exchange (ETDEWEB)

For the expansion to 2.0 MTPY of the CVG Bauxilum alumina plant, the area of clarification and red mud washing was rearranged from four 2-thickener-5-washer trains to two 1-thickener-7-washer trains. As a result of this modification, the specific mud handling capacity of the existing tanks should be increased by almost 3-times. The time allowed for control actions was then significantly reduced, leading to the need of an on-line level detection system, in order to achieve a better and faster control of the operation. With this scope, it was developed and installed a new continuous mud level detector that gives the measurement of both mud and turbid zone levels in the tanks. The development of the new instrument started with an existing instrument for density measurements which was completely re-engineered in order to obtain the maximum readability in the densities founded along the full range of the tank height. Actually 28 tanks are equipped with these instruments ...

Energy Technology Data Exchange (ETDEWEB)

Silicon nitride based ceramics have attracted considerable attention as good candidates for structural applications due to their excellent mechanical properties including strength, hardness, fracture toughness, and high temperature strength. These properties are strongly influenced by grain size and morphology, and by the degree of crystallinity and chemistry of grain boundary phases. In this work, the microstructure of Si{sub 3}N{sub 4} densified with Nd{sub 2}O{sub 3}, Y{sub 2}O{sub 3} and Al{sub 2}O{sub 3} sintering additives was studied. Sintered samples were polished and plasma etched for microstructural analysis using scanning electron microscope. Quantitative evaluation of materials microstructure was accomplished using Quantikov software. Fracture toughness was measured by Vickers indentation method. The observed microstructure is typical of silicon nitride based materials and is characterized by high aspect ratio.-Si{sub 3}N{sub 4} grains embedded into a matrix formed by ...

British Library Electronic Table of Contents (United Kingdom)

Synthesis of highly anisotropic rod-like b-Si3N4 particles with different morphological characteristics was accomplished using commercial a-Si3N4. A number of powder mixtures were prepared with additions of various oxides (Al2O3+RE2O3, being RE=Y, La or Yb) that were subsequently heat treated in a loose powder state in the temperature range of 1750-1950degreeC and dwell times from 10 to 180min under high pressure of N2 (60MPa) in a hot isostatic press. The obtained aggregated porous bodies were lightly crushed by hand using an alumina mortar and pestle and subsequently subjected to sequential chemical treatments to eliminate the glassy phases and possible residual crystalline compounds, and to separate the synthesized b-Si3N4 particles. Resulting b-Si3N4 particles were characterized by X-r...

Science.gov (United States)

Two enantioselective, potentiometric membrane electrodes (EPMEs) based on maltodextrins with different value of dextrose equivalent (DE) (maltodextrin I: DE 4.0-7.0; maltodextrin II: DE 16.5-19.5) were proposed for the assay of baclofen enantiomers in baclofen raw materials and from its pharmaceutical formulation, Norton-Baclofen tablets. The slopes of the electrode function of the proposed electrodes were 55.0 mV/pS-baclofen for maltodextrin I-based electrode and 59.0 mV/pR-baclofen for maltodextrin II-based electrode and the detection limits were 1.34 x 10(-6) mol l(-1) (S-baclofen) and 2.52 x 10(-10) mol l(-1) (R-baclofen), respectively. The surfaces of the electrodes are stable and easily renewable by simply polishing on alumina paper. PMID:15598435

Energy Technology Data Exchange (ETDEWEB)

The objective of our research was to obtain fundamental information regarding the functional dependence of the diffusion coefficient of coal molecules on the ratio of molecule to pore diameter. That is, the objective of our study was to examine the effect of molecule size and configuration on hindered diffusion of coal macromolecules through as porous medium. To best accomplish this task, we circumvented the complexities of an actual porous catalyst by using a well defined porous matrix with uniform capillaric pores, i.e., a track-etched membrane. In this way, useful information was obtained regarding the relationship of molecular size and configuration on the diffusion rate of coal derived macromolecules through a pore structure with known geometry. Similar studies were performed using a pellet formed of porous alumina, to provide a link between the idealized membranes and the actual complex pore structure of real catalyst extrudates. The fundamental information ...

Energy Technology Data Exchange (ETDEWEB)

Red mud (Rm) is the main by-product of the Bayer process for alumina extraction from bauxite, and grey slurries (GS) are generated during the granite rocks transformation processes. the huge volume of those wastes generated every year suppose a serious environmental problem. Recent works by our group demonstrate the efficiency of both types of muds as corrosion inhibitors for iron and steel in alkaline media containing chlorides. The elemental analysis of these slurried shows that Al{sup 3}+ is the main common element. Therefore, the aim of this paper is to study the effect of the soluble Al{sup 3}+ in the electrochemical behaviour of iron in alkaline media, in presence and absence of chlorides. The electrochemical study using Cyclic Voltammetry (CV) and Electrochemical Impedance Spectroscopy (EIS) together with surface analysis techniques allowed to conclude that Al{sup 3}+ blocks the surface of steel in alkaline media chloride increasing the steel resistance to ...

Energy Technology Data Exchange (ETDEWEB)

This thesis is in the field of gas emission control from automobile and stationary sources. Out of the possible approaches to the elimination of pollutant gases, such as nitrogen oxides (NO{sub x}), one consists in the selective catalytic reduction (SCR) of these NO{sub x} on a suitable heterogeneous catalyst. Ammonia or hydrocarbons are employed as reducing agents. The most important catalysts active in the SCR of NO{sub x} are based on ions of transition metal either supported on several oxides or dispersed in zeolites. The catalysts have been characterized by electron magnetic resonance techniques (EPR, ENDOR, ESEEM) and the interaction of catalysts with nitrogen oxides, with reducing and poisoned agents have been followed with the same techniques. Copper dispersed on alumina and its interaction with both NO and ammonia has been investigated. Also the interaction between both water and ammonia with copper dispersed in zeolite ZSM-5 has been investigated. The ...

Science.gov (United States)

A laser pyrolysis technique has been used to produce ultrafine particles of iron carbide with diameters ranging from 2 to 20 nm. Catalysis using iron carbide was investigated in the liquefaction of Wyodak subbituminous coal; yields were determined. A study was carried out to examine the possibility of using an ultrasonic extraction technique as a rapid method of product work-up of samples following pretreatment or liquefaction experiments. A similar study had shown that extraction of coal-derived products by an ultrasonic method was rapid and gave yields and product distributions comparable to those obtained by Soxhlet extraction. On another project, three different types of supported catalysts were used to test activity for the combined water-gas shift hydrogenation of a synthetic donor solvent. The three catalysts tested were: (1) Alumina supported NiMo catalyst-Shell 324m; (2) Bulk hydrous TiO NiMo catalyst; (3) Thin film hydrous TiO catalyst supported on silica ...

Energy Technology Data Exchange (ETDEWEB)

The behavior of melter feed (a mixture of nuclear waste and glass-forming additives) during waste-glass processing has a significant impact on the rate of the vitrification process. We studied the effects of silica particle size and sucrose addition on the volumetric expansion (foaming) of a high-alumina feed and the rate of dissolution of silica particles in feed samples heated at 5 C/min up to 1200 C. The initial size of quartz particles in feed ranged from 5 to 195 {micro}m. The fraction of the sucrose added ranged from 0 to 0.20 g per g glass. Extensive foaming occurred only in feeds with 5-{micro}m quartz particles; particles {ge}150 {micro}m formed clusters. Particles of 5 {micro}m completely dissolved by 900 C whereas particles {ge}150 {micro}m did not fully dissolve even when the temperature reached 1200 C. Sucrose addition had virtually zero impact on both foaming and the dissolution of silica particles. Over 100 sites in the United States are currently ...

Energy Technology Data Exchange (ETDEWEB)

In this study, WO{sub 3} thin films were grown on glass substrates using an aqueous solution containing tungstate (NH{sub 4}){sub 2}WO{sub 4} as precursor. The substrate temperature incremented from 250 to 500 deg. C, by steps of 50 deg. C. The structural properties were investigated using XRD, atomic force microscopy and scanning electronic microscopy techniques. Microprobe analyses showed that a balanced stoichiometric composition was obtained for thin films prepared at T{sub s} = 350 and 400 deg. C. The X-ray diffraction analyses showed different structure crystallography in function of the substrate temperature. Moreover, films deposited at 400 deg. C were annealed in air for 2 h at 450 and 500 deg. C, respectively and the structural changes due to heat treatment were studied. Finally, the optical properties of these films were carried out using optical measurements of transmittance T({lambda}) and reflectance ...

Energy Technology Data Exchange (ETDEWEB)

Statistically based experimental designs were applied to optimize the fermentation process parameters for hydrogen (H{sub 2}) production by co-culture of Clostridium acidisoli and Rhodobacter sphaeroides with sucrose as substrate. An initial screening using the Plackett-Burman design identified three factors that significantly influenced H{sub 2} yield: sucrose concentration, initial pH, and inoculum ratio. These factors were considered to have simultaneous and interdependent effects. A central composite design and response surface analysis were adopted to further investigate the mutual interactions among the factors and to identify the values that maximized H{sub 2} production. The optimal substrate concentration, initial pH, and inoculum ratio of C. acidisoli to R. sphaeroides were 11.43 g/L sucrose, 7.13, and 0.83, respectively. Using these optimal culture conditions, substrate conversion efficiency was determined as ...

International Nuclear Information System (INIS)

Marker experiments for studying the mass transport through a palladium silicide layer on a crystalline substrate during thermal oxidation at 700 to 850 deg C have been reported recently. In this work argon gas embedded in amorphous silicon during sputtering was implemented as the inert marker and the oxidation of PdSi was processed above 900 deg C. At this high-temperature oxidation silicon-rich silicide PdSisub(y), with y exceeding 5, may be obtained. This can be anticipated by considering the Pd-Si phase diagram which shows the liquid phase may appear at an annealing temperature above 892 deg C. As a result, a non-stoichiometric and non-uniform silicide layer may develop at the sample surface. Marker analysis showed that both palladium and silicon dissociated at the Pdsub(x)Si/ SiO_2 interface and moved to the substrate with the silicon being the dominant diffuser. The Rutherford backscattering spectra (RBS) showing the oxide film and ...

British Library Electronic Table of Contents (United Kingdom)

This study investigates the applicability of n-type TiO2 and p-type NiO on the FTO-glass (Fluorine doped tin oxide, SnO2:F) substrate of the working electrode in a dye-sensitized solar cell (DSSC). The working electrode was designed and fabricated by depositing a film of TiO2/NiO composite particles, which were prepared by mixing the Ni powder with TiO2 particles using dry mixing method, on a FTO-glass substrate using a spin coating process. The working electrode was then immersed in the solution of N-719 (Ruthenium) dye at a temperature of 70degreeC for 6h. Moreover, a thin film of platinum (Pt) was deposited on the FTO-glass substrate of the counter electrode using an E-beam evaporator. Finally, the DSSC was assembled, and the short-circuit photocurrent, the open-circuit photovoltage and...

Energy Technology Data Exchange (ETDEWEB)

Plasma nitriding of a Ti substrate is carried out under a low ambient pressure below 3kPa, and a plasma torch is prepared on a trial basis which is provided with a supersonic expansion nozzle considered to expand plasma jet optimally and to be effective for suppressing the occurrence of shock wave. The system used for the study is provided with a specimen holder having the function of adjusting the distance between the nozzle outlet and the substrate inside the vacuum chamber which is provided with a plasma torch in the flange member. The plasma torch is so structured that a supersonic expansion nozzle can be installed at the tip of the plasma torch. In this process wherein plasma jet is employed, hard nitrided layer can be formed by plasma irradiation for a short time even under such low pressure as less than 3kPa by setting adequate experimental conditions. It is made clear that the use of a supersonic nozzle corresponding to the internal ...

International Nuclear Information System (INIS)

Aluminium nitride (AlN) is a very interesting ceramic because of its combination of properties such as high thermal stability, high hardness and an unusual combination of high thermal and low electrical conductivity. But it is very difficulty to obtain an AlN layer on the aluminium substrates by thermochemical nitriding process. Since a thin film of aluminium oxide existing on the surface of every aluminium substrate prevents the nitrogen atoms from diffusing into the aluminium lattice. However, it is possible to sputter the oxide film away from the aluminium surface in a glow discharge with the use of plasma nitriding technique and to allow the formation of AlN layer on the aluminium bulk. In the present work specimen of aluminium Al 99.5 has been plasma nitrided in a modified plasma nitriding unit, in which a diffusion pump was used to obtain an especially low partial pressure of oxygen in the vauum chamber. The sputter-cleaning prior to the ...

British Library Electronic Table of Contents (United Kingdom)

Zirconium and particularly Zr-2.5wt%Nb (Zr2.5Nb) alloy are useful for engineering bearing applications because they can be oxidized in air to form a hard surface ceramic. Oxidized zirconium (OxZr) due to its abrasion resistant ceramic surface and biocompatible substrate alloy has been used as a bearing surface in total joint arthroplasty for several years. OxZr is characterized by hard zirconium oxide (oxide) formed on Zr2.5Nb using one step thermal oxidation carried out in air. Because the oxide is only at the surface, the bulk material behaves like a metal, with high toughness. The oxide, furthermore, exhibits high adhesion to the substrate because of an oxygen-rich diffusion hardened zone (DHZ) interposing between the oxide and the substrate. In this study, we demonstrate a two step pro...

Energy Technology Data Exchange (ETDEWEB)

Multilayer mirror coatings which reflect extreme ultraviolet (EUV) radiation are a key enabling technology for EUV lithography. Mo/Si multilayers with reflectances of 67.5% at 13.4 nm are now routinely achieved and reflectances of 70 2% at 11.4 nm were obtained with MO/Be multilayers. High reflectance is achieved with careful control of substrate quality, layer thicknesses, multilayer materials, interface quality, and surface termination. Reflectance and film stress were found to be stable relative to the requirements for application to EUV lithography. The run-to-run reproducibility of the reflectance peak position was characterized to be better than 0.2%, providing the required wavelength matching among the seven multilayer-coated mirrors used in the present lithography system design. Uniformity of coating was improved to better than 0.5% across 150 mm diameter substrates. These improvements in EUV multilayer mirror technology will enable us ...

Energy Technology Data Exchange (ETDEWEB)

A radio frequency sputtering apparatus with a pair of targets has been developed for depositing a film of uniform thickness onto a complex-geometric specimen such as the retainer of a ball bearing. The deposition characteristics of the apparatus were compared with those of the conventional sputtering apparatus. Lubrication properties of MoS/sub 2/ films made by these devices were also compared under a variety of conditions. Finally, friction and wear of MoS/sub 2/ films applied to angular-contact type ball bearings of 20 mm bore were studied in air, nitrogen and vacuo. The two-target sputtering has an advantage mentioned above. However, the films deposited by the method exhibited a rather short wear life because of the temperature rise of the substrate during ion bombardment and during the sputtering process. This temperature dependence was observed in films on those substrates that had been heated with a built-in heater during sputtering. The ...

International Nuclear Information System (INIS)

Iron oxide films have been deposited on Si(100) substrates by chemical vapour deposition (CVD) of iron(III) tert-butoxide ([Fe(O "tBu)_3]_2) in the temperature range 350-450 deg. C. The precursor flux and substrate temperature were varied to control the phase composition, average grain size and film thickness. The nature of substrate and deposition temperature markedly influence the morphology and iron-oxygen stoichiometry in the CVD deposits. Phase transformations in iron oxide films were achieved through precise local and periodic heating of the films by interfering laser beams. The interaction of iron oxide films with short laser pulses (Nd:YAG, 355 nm) induced partial transformation of hematite (#alpha#-Fe_2O_3) to magnetite (Fe_3O_4) or magnetite to wuestite (Fe_1_-_xO), respectively. The phase characterization and morphology of the hematite and magnetite films were investigated before and after laser irradiation by ...

International Nuclear Information System (INIS)

In this work, the effects of substrate temperature that was changed from 100 to 500 "oC on the structural, chemical and electrical properties of carbon films, prepared by direct current magnetron sputtering technique, on 316L stainless steel as bipolar plate had been investigated. Raman spectroscopy and scanning electron microscopy (SEM) were performed to study the structure and the morphology of the deposited films, respectively. The corrosion resistance and the electrical resistivity were carried out by using corrosion tests and four point-probe technique. The results show that the carbon films change the structure from amorphous to graphite-like by increasing temperatures. At the temperatures higher than 300 "oC, the holes and porosities are formed on the film indicating a decrease of film quality. According to our results, corrosion resistance and electrical properties are depended strongly on the substrate temperature.

Science.gov (United States)

A focused ion beam (FIB) technique was applied to cross-sectional specimen preparation to observe an interface between a plasma sprayed coating and an aluminum (Al) substrate by transmission electron microscopy (TEM). The surface of the sprayed coating film has a roughness of several tens of microns. Sputter rates for the coating film and the substrate are greatly different. The rough surface and the difference in sputter rate cause problems in making TEM specimens with smooth side walls. The top surface of the coating film was planerized by the FIB before fabricating the TEM specimen. The interfaces were investigated by TEM and energy-dispersive X-ray (EDX) analysis. The TEM observation revealed that there is a 10 nm thick amorphous layer at the interface between the coating film and substrate. The coating film consists of two kinds of sublayers with bright and dark contrast. The bright contrast sublayers were amorphous ...

Energy Technology Data Exchange (ETDEWEB)

A device for detecting neutrons includes a semi-insulated bulk semiconductor substrate having opposed polished surfaces. A blocking Schottky contact comprised of a series of metals such as Ti, Pt, Au, Ge, Pd, and Ni is formed on a first polished surface of the semiconductor substrate, while a low resistivity ("ohmic") contact comprised of metals such as Au, Ge, and Ni is formed on a second, opposed polished surface of the substrate. In one embodiment, n-type low resistivity pinout contacts comprised of an Au/Ge based eutectic alloy or multi-layered Pd/Ge/Ti/Au are also formed on the opposed polished surfaces and in contact with the Schottky and ohmic contacts. Disposed on the Schottky contact is a neutron reactive film, or coating, for detecting neutrons. The coating is comprised of a hydrogen rich polymer, such as a polyolefin or paraffin; lithium or lithium fluoride; or a heavy metal fissionable material. By varying the ...

Science.gov (United States)

We investigated the effect of pretreatment on the physicochemical characteristics-crystallinity, bed porosity, and volumetric specific surface of soybean hulls and production of cellulolytic enzymes in solid-state fermentation of Trichoderma reesei and Aspergillus oryzae cultures. Mild acid and alkali and steam pretreatments significantly increased crystallinity and bed porosity without significant change inholocellulosic composition of substrate. Crystalline and porous steam-pretreated soybean hulls inoculated with T. reesei culture had 4 filter paper units (FPU)/g-ds, 0.6?IU/g-ds ?-glucosidase, and 45?IU/g-ds endocellulase, whereas untreated hulls had 0.75?FPU/g-ds, 0.06?IU/g-ds ?-glucosidase, and 7.29?IU/g-ds endocellulase enzyme activities. In A. oryzae steam-pretreated soybean hulls had 47.10?IU/g-ds endocellulase compared to 30.82?IU/g-ds in untreated soybean hulls. Generalized linear statistical model fitted to enzyme activity data showed that effects of ...

Energy Technology Data Exchange (ETDEWEB)

In this work, we describe the fabrication and operating characteristics of GaAs/AlGaAs thin film solar cells processed by the epitaxial liftoff (ELO) technique. This technique allows the transfer of these cells onto glass substrates. The performance of the lifted-off solar cell is demonstrated by means of electrical measurements under both dark and illuminated conditions. We have also optimized the light trapping conditions in this direct-gap material. The results show that good solar absorption is possible in active layers as thin as 0.32 {mu}m. In such a thin solar cell, the open circuit voltage would be enhanced. We believe that the combination of an epitaxial liftoff thin GaAs film, and nano-texturing can lead to record breaking performance. {copyright} {ital 1997 American Institute of Physics.}

Energy Technology Data Exchange (ETDEWEB)

This final report for the Swiss Federal Office of Energy (SFOE) presents the results of a project that involves the building of a joint biogas plant serving 60 farmers and industrial companies with an annual processing capacity of 45,000 tons. The plant is to produce biogas to be fed into the gas mains and will not only reduce nutrient loading in a region with an extensive livestock industry but also reduce carbon dioxide emissions by using the gas as a motor fuel. The importance of the project with respect to both the environment and energy policy-making is discussed and the costs involved are examined. Details are presented on the technology used and on the material flows involved. Figures are quoted on energy production. The various biogenic substrates used, such as food wastes, waste oils, cereal wastes and used mushroom substrates, are discussed, as is the use of the solid and liquid outputs of the digester in farming activities.

International Nuclear Information System (INIS)

Selective formation of ZnO nanodots was accomplished by metalorganic chemical vapor deposition on nanopatterned SiO_2/Si substrates. Self-organized ZnO nanodots were selectively formed in nanopatterned lines of Si created by etching of SiO_2 with focused ion beam (FIB), whereas any nanodots were hardly observed on the SiO_2 surface in the vicinity of the FIB-sputtered Si areas. The mechanism of the selective formation of ZnO nanodots on FIB-nanopatterned lines is mainly attributed to the effective migration of Zn adatoms diffusing on the SiO_2 surface into the Si lines followed by the nucleation at surface atomic steps and kinks created by Ga"+ ion sputtering. Cathodoluminescence measurements confirmed that the emission originated from the selectively grown ZnO nanodots.

International Nuclear Information System (INIS)

The nickel-rich superalloys Alloy 600 and Alloy 800 have been corroded in mildly alkaline deuterated aqueous conditions typical of secondary coolant circuits in a nuclear power station. The oxide films and substrates of these alloys have been analysed by imaging SIMS depth profiling, which makes it possible to describe elemental distribution in all three dimensions. The measurement of the distribution of the secondary ions NiO"-, FeO"- and CrO"- appears useful for detailing the behaviour of nickel, iron and chromium within oxidized phases. The measurement of D"- distribution outlines the extent of oxide hydration. For Alloy 800, evidence of sodium migration into the grain boundaries of the alloy substrate is found. For Alloy 600, no grain boundary sodium ingress can be identified under comparable corrosion conditions. (author).

International Nuclear Information System (INIS)

We provide a brief review of our recent results from optically detected magnetic resonance studies of grown-in non-radiative defects in two most important dilute nitride systems-Ga(In)NAs grown on GaAs substrates and Ga(Al,In)NP grown on Si and GaP substrates. These results have led to the identification of defect complexes in the alloys, involving intrinsic defects such as As_G_a antisites and Ga_i self-interstitials. They have also shed light on formation mechanisms of the defects and on their role in non-radiative carrier recombination that is harmful to the performance of potential optoelectronic and photonic devices based on these dilute nitrides.

International Nuclear Information System (INIS)

Yttria stabilized zirconia (YSZ) with 8 mol% Y was deposited by reactive magnetron sputtering onto oxidized (100) silicon substrates. It was possible to switch film texture from (111) to (200) by applying a strong RF substrate bias. Transmission electron microscopy showed that the film deposited under bias is porous and exhibits nanoscaled grains, whereas the film deposited without bias is dense and columnar. The ionic conductivity as a function of temperature revealed an activation energy of 1.04 eV. The mechanical stress could be tuned to low values by thermal post-annealing. Using the dense (111) film as electrolyte layer, and the porous (200) film as an interlayer to a porous Pt anode, an open circuit voltage of 0.85 V was obtained in a micro machined fuel cell structure.

CERN Document Server

substrate). Within each group of simulations, three lubricant film thicknesses are studied to examine the effect of varying lubricant thickness. Statistical data are collected from each simulation and presented in this work. Via these data, together with the evolution, of atomic and molecular configurations, a very detailed picture of the properties of this thin film interface is presented. In particular, we conclude that perfluoropolyether lubricant forms distinct molecular layers when confined between two substrates, the rate of heat generation under shearing conditions typical of those in a head-disk interface is insufficient for thermal mechanisms to result directly in lubricant degradation, and mechanical stresses attained in the head-disk interface are unlikely to result in any significant degree of lubricant degradation. This thesis examines the tribology of a head-disk interface in an operating hard disk drive via non-equilibrium ...

British Library Electronic Table of Contents (United Kingdom)

On the basis of a numerical model, the temperature and liquid fraction of spray-formed H13 tool steel are calculated as a function of time. Results show that a preheated substrate at the appropriate temperature can lead to very low porosity by increasing the liquid fraction in the deposited steel. The calculated cooling rate can lead to a microstructure consisting of martensite, lower bainite, retained austenite, and proeutectoid carbides in as-spray-formed material. In the temperature range between the solidus and liquidus temperatures, the calculated temperature of the spray-formed material increases with increasing substrate preheat temperature, resulting in a very low porosity by increasing the liquid fraction of the deposited steel. In the temperature region where austenite decomposit...

Energy Technology Data Exchange (ETDEWEB)

A 15-nm lithium fluoride (LiF) thin film evaporated on glass substrate is shown to enhance the nucleation of microcrystalline Si grown by plasma enhanced chemical vapour deposition at the amorphous/microcrystalline boundary conditions. The effect is more pronounced at low substrate temperatures, nucleation density being 10 times higher at {approx} 80 {sup o}C. The effect is ascribed to the ionic chemical nature of LiF, the low work function material used in organic electronic devices, and we propose its use for micro patterning crystalline Si regions in otherwise amorphous Si film.

Energy Technology Data Exchange (ETDEWEB)

The indium implant damage and diffusion behavior in thin silicon-on-insulator (SOI) with a 200 nm top silicon layer were studied for different implantation energies and doses. Rutherford backscattering spectrometry in the channeling mode (RBS/C) was used to characterize the implant damage before and after annealing. Secondary ion mass spectrometry (SIMS) was used to study the indium transient enhanced diffusion (TED) behavior in the top Si layer of the SOI structure. An anomalous redistribution of indium after relatively high energy (200 keV) and dose (1 x 10{sup 14} cm{sup -2}) implantation was observed in both bulk Si and SOI substrates. However, there exist differences in these two substrates that are attributable to the more predominant out-diffusion of indium as well as the influence of the buried oxide layer in the SOI structure.

Energy Technology Data Exchange (ETDEWEB)

This paper presents experimental data and an computational model of the cold spray solid particle impact process. Copper particles impacting onto a polished stainless steel substrate are examined. The high velocity impact causes significant plastic deformation of both the particle and the sub- strate, but no melting is observed. The plastic deformation exposes clean surfaces that, under the high impact pressures, result in significant bond strengths between the particle and substrate. Experimental measurements of the splat and crater sizes compare well with the numerical calculations. It is shown that the crater depth is significant and increases with impact velocity. However, the splat diameter is much less sensitive to the impact velocity. It is also shown that the geometric lengths of the splat and crater scale linearly with the diameter of the impacting particle. It is hoped that the results presented will allow better understanding of the ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces which are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

International Nuclear Information System (INIS)

Nanoscale islands of Cu_2O have been synthesized on single-crystal SrTiO_3 (100) substrates using oxygen plasma-assisted molecular-beam epitaxy (MBE). Island growth location has been controlled by using an ex situ Ga"+ focused ion beam (FIB) to modify the growth surface in discrete locations prior to island synthesis. The FIB modifications have generated surface topography with lateral dimensions of 150-200 nm. Ex situ atomic force microscopy study after island growth reveals that certain FIB substrate modification and MBE growth condition combinations lead to directed self-assembly of metal oxide islands at the edges of the FIB modified zones.

International Nuclear Information System (INIS)

Electron simulated desorption of anions from CFCl_3 and CF_2Cl_2 condensed on an Au substrate is studied in the energy range 0-15 eV. The negative fragments are recorded mass spectro metrically as the function of the incident electron energy. Below 10 eV we observe anion desorption via pronounced resonance profiles which are characteristic for dissociative electron attachment (DA) while the continuous rise of the signal at higher energies accounts for dipolar dissociation (DD) and processes involving secondary electrons from the metallic substrate. For both compounds F"- and Cl"- are the only fragment anions we could observe. (author).

Science.gov (United States)

During this report period, we have obtained a model of montmorillonite clay, and this model has been of great assistance in visualizing how the chemistry of substrate molecules might be altered as it occurs on the surface of the clay. A stereochemical representation of this montmorillonite model is shown. Of particular significance, this model indicates that hydroxyl groups are located in the center of each siloxane ring on the surface of the montmorillonite clay. These hydroxyl groups might serve to bond substrate molecules to the surface of the clay. The next step in our systematic examination of the radical cation-initiated dimerization of plant monomers from the C{sub 6}-C{sub 3} pool of shikimic acid metabolites was to study the dimerization of cinnamic acid and its derivatives. In the next block of research, we examined the reaction of montmorillonite clay (K-10) with methyleugenol. 2 refs.

International Nuclear Information System (INIS)

We have investigated B diffusion in pre-amorphized silicon. In our experiments, the crystalline surface layer of silicon-on-insulator (SOI) substrates was completely amorphized by Ge ion implantation. Using SOI substrates in this fashion suppressed solid-phase-epitaxy regrowth, making it possible to investigate B diffusion in pre-amorphous silicon over a wider range of temperatures (500-650 deg. C) and times (5-1000 s) than has previously been reported. Diffusivities were determined with the aid of computational processes modeling. The results from this work demonstrate the B diffusion in a-Si is concentration dependent, exhibits a transient enhanced diffusion, and possesses an Arhennius behavior with activation energy of #approx#2.1 eV.

British Library Electronic Table of Contents (United Kingdom)

The mechanism of the IndolPhos-Rh-catalyzed asymmetric hydrogenation of prochiral olefins has been investigated by means of X-ray crystal structure determination, kinetic measurements, high-pressure NMR spectroscopy, and DFT calculations. The mechanistic study indicates that the reaction follows an unsaturate/dihydride mechanism according to Michaelis-Menten kinetics. A large value of KM (KM=5.01+-0.16 M) is obtained, which indicates that the Rh-solvate complex is the catalyst resting state, which has been observed by high-pressure NMR spectroscopy. DFT calculations on the substrate-catalyst complexes, which are undetectable by experimental means, suggest that the major substrate-catalyst complex leads to the product. Such a mechanism is in accordance with previous studies on the mechanism...

International Nuclear Information System (INIS)

This paper reports on a series of experiments performed to examine the ability of ion beam assisted thermal deposition to produce good adhesion of Au metallization on GaAs left-angle 100 right-angle substrates. A study of the influence of Ar ion-assisted thermal deposition of the Au films as well as in situ pre-sputtering of the GaAs surface with low-energy Ar ions prior to thermal deposition, shows that strong adhesion can be achieved without resorting to chemical cleaning. The substrate temperature and the relative flux of Ar ions to incident Au atoms were varied in order to correlate these parameters with film adhesion. The interfaces of films processed under these various conditions were examined by XTEM, RBS and XPS. Orientation texture was studied by x-ray diffraction (XRD).

Energy Technology Data Exchange (ETDEWEB)

This paper describes a feasibility demonstration of a thermal scanning NDE system for thermal spray coatings. Non-bonds were detected between several types of coatings and their substrates. Aluminum anti-skid coatings having very rough surfaces were included. A technique for producing known non-bond areas for calibrating and demonstrating NDE methods was developed.

Energy Technology Data Exchange (ETDEWEB)

This report discusses the activities of two major groups of forest soil microorganisms, the bacteria and the fungi. Special attention is paid to their participation in the decay of major forest litter substrates, including leaves, branches and roots. The influence of bacteria and fungi in symbiotic associations with woody plant roots upon the cycles of carbon and nitrogen is described. The impacts of certain forest mamagement alternatives are assessed in terms of the creation of elimination of suitable environments for the activity of soil microorganisms. A bibliography is included. 507 refs., 1 tab.

International Nuclear Information System (INIS)

The application of photopolymerisation (UV) and electron beams (EB) technologies in radiation rapid cure (PRC) processing is discussed. The chemistry associated with such reactions and the mechanisms of the processes are treated. The occurrence of concurrent grafting to substrate with radiation curing of films is shown to be an advantage in enhancing the properties of certain finished products. The parameters influencing the optimum grafting yield in such PRC processes are discussed. In many applications, the chemistry of such processes combined with the machine, specially for EB is shown. (author).

Energy Technology Data Exchange (ETDEWEB)

We have used polished stainless steel as a mirror substrate to provide focusing of soft x-rays in grazing incidence reflection. The substrate is bent to an elliptical shape with large curvature and high stresses in the substrate require a strong elastic material. Conventional material choices of silicon or of glass will not withstand the stress required. The use of steel allows the substrates to be polished and installed flat, using screws in tapped holes. The ultra-high-vacuum bender mechanism is motorized and computer controlled. These mirrors are used to deliver focused beams of soft x-rays onto the surface of a sample for experiments at the Advanced Light Source (ALS). They provide an illumination field that can be as small as the mirror demagnification allows, for localized study, and can be enlarged, under computer control,for survey measurements over areas of the surface up to several ...

International Nuclear Information System (INIS)

We studied the strain introduced in a Si(111) substrate due to MeV ion implantation using extremely asymmetric x-ray diffraction and measured the rocking curves of asymmetrical 113 diffraction for the Si substrates implanted with a 1.5 MeV Au"2"+ ion at fluence values of 1x10"1"3, 5x10"1"3, and 1x10"1"4/cm"2. The measured curves consisted of a bulk peak and accompanying subpeak with an interference fringe. The positional relationship of the bulk peak to the subpeak and the intensity variation of those peaks with respect to the wavelengths of the x rays indicated that crystal lattices near the surface were strained; the lattice spacing of surface normal (111) planes near the surface was larger than that of the bulk. Detailed strain profiles along the depth direction were successfully estimated using a curve-fitting method based on Darwin's dynamical diffraction theory. Comparing the shapes of resultant strain profiles, we found that a strain ...

International Nuclear Information System (INIS)

The possibilities and problems of PCA in phase separation are shown on Ni, Pd, and Pt silicides. The PCA depth profiles are less influenced by sputter and matrix effects than usual Auger depth profiles. The position of the silicide-Si interface is well defined by the component distribution crossover in PCA profiles. An interface component between Pd and Pt silicides and Si substrate is determined by PCA. (author).

UK PubMed Central (United Kingdom)

Insulin-degrading enzyme (IDE) degrades insulin and other peptides, including the Aβ peptide of Alzheimer’s disease. However, the mechanism by which IDE acts on its substrates...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

The invention relates to a pulsed laser ablation method of metals and/or dielectric films from the surface of a wafer, printed circuit board or a hybrid substrate. By utilizing a high-energy ultra-short pulses of laser light, such a method can be used to manufacture electronic circuits and/or electro-mechanical assemblies without affecting the material adjacent to the ablation zone.

Energy Technology Data Exchange (ETDEWEB)

X-ray diffraction was used to monitor the {ital in} {ital situ} reaction of Pd deposited on Si(111) at room temperature. An ordered silicide forms spontaneously beneath a poorly ordered overlayer. It is commensurate and strained at low coverage, but relaxes to an unstrained state above a critical thickness of 18 A. During both phases of growth sustained intensity oscillations are seen that correspond to a layerwise consumption of the substrate at the buried interface.

Energy Technology Data Exchange (ETDEWEB)

In order to fabricate high temperature superconducting tapes for power applications, the authors have analyzed different buffer layer architectures grown on textured Ni substrates suitable for YBCO deposition. Due to its optimal lattice matching the studied structures present as top layer a CeO{sub 2} film. The deposition of CeO{sub 2} on Ni substrates was performed by pulsed laser ablation and by e-beam evaporation at different temperatures. The films obtained by the two deposition techniques have not optimal structural properties, having a polycrystalline component. The misorientation of CeO{sub 2} is probably due to the formation of NiO at the interface between the film and the substrate during the deposition process even if no oxygen is introduced. In order to prevent Ni oxidation an intermediate 2000 {angstrom} Pd thick film was deposited by e-beam. Furthermore, the lattice mismatch between Pd and CeO{sub 2} is smaller ...

Energy Technology Data Exchange (ETDEWEB)

The process operation of the hot wall vapor deposition method, formation of dry organic thin film and the control of molecular arrangement were described. This equipment included a substrate on the upper end of the hot wall tube and the vapor source at the lower end. The remarkable features are the hot wall tube which plays the role to hold vaporizing molecules to the high temperature and to transport molecules, and the flip flop mechanism which gives some idle period for the molecular vaporization by shutter closing. Several experiments were carried out by using stearic acid and by changing the distance S from the upper end of hot wall quartz tube to the substrate, the furnace temperature T{sub f} and the substrate temperature T{sub s}. When T{sub f} is equal to or less than the melting point of stearic acid, molectles are preferentialy made to vertical arrangement. In the case of T{sub f} more than the melting point, the ...

Energy Technology Data Exchange (ETDEWEB)

We have grown ferroelectric Pb{sub 0.92}La{sub 0.08}Zr{sub 0.52}Ti{sub 0.48}O{sub 3} (PLZT) films on platinized silicon and LaNiO{sub 3}-buffered nickel substrates by chemical solution deposition using a sol-gel process based on acetic acid chemistry. The following measurements were obtained under zero-bias field: relative permittivity of {approx}960 and dielectric loss of {approx}0.04 on the PLZT film grown on Pt/Si substrates, and relative permittivity of {approx}820 and dielectric loss of {approx}0.06 on the PLZT film grown on LNO-buffered Ni substrates. In addition, a relative permittivity of 125 and dielectric loss of 0.02 were measured at room temperature under a high bias field of 1 x 10{sup 6} V/cm on PLZT deposited on LNO-buffered nickel substrate. Furthermore, a steady-state leakage current density of {approx}8.1 x 10{sup -9} A/cm{sup 2} and mean breakdown field strength of 1.7 x 10{sup 6} ...

Energy Technology Data Exchange (ETDEWEB)

Following a postulated meltdown accident, the integrity of containment building structural material under attack by hot molten core debris and the safeguard of environment against radiological releases constitutes the final line of defense in PAHR safety assessment. Such assessment requires a good knowledge of UO/sub 2//interaction and penetration with different types of concrete. The present study focuses on the phenomena associated with core debris interaction/penetration with substrate basalt concrete.

Energy Technology Data Exchange (ETDEWEB)

[sup 13]C epitaxial diamond films have been grown on [sup 12]C-type IIb diamond substrates doped with boron, using electron assisted chemical vapor deposition. The relation between etch pits to dislocations in [sup 13]C diamond film and the broadening of the first-order Raman peak was examined. The reactant gas was [sup 13]CH[sub 4] of > 99% purity. The substrate temperature was varied from 943 to 1300 C. The uneven surface morphology was confirmed by atomic force microscopy (AFM) and laser microscopy. From 943 to 1030 C, etch pit rows along left angle 100 right angle were observed. At 991 C, the etch pit density on a row was 3300 to 5000 pits/cm. The Ar[sup +] laser beam was focused on a transparent area near the row of etch pits, where the boron impurity of the substrate is less than several 10 ppm. The first-order Raman line of [sup 13]C epitaxial diamond film was broadened to 3.6-4.0 cm[sup -1]. The line broadening ...

CERN Document Server

We derive the expression for spontaneous emission rate in finite one-dimensional photonic crystal with arbitrary defects using the effective resonator model to describe electromagnetic field distributions in the structure. We obtain explicit formulas for contributions of different types of modes, i.e. radiation, substrate and guided modes. Formal calculations are illustrated with a few numerical examples, which demonstrate that the application of effective resonator model simplifies interpretation of results.

UK PubMed Central (United Kingdom)

Microorganisms can degrade saturated hydrocarbons (alkanes) not only under oxic but also under anoxic conditions. Three denitrifying isolates (strains HxN1, OcN1, HdN1) able to grow under anoxic conditions...Full Text Available

UK PubMed Central (United Kingdom)

The stable hydrogen (δ²H) and oxygen (δ¹⁸O) isotope ratios of organic and inorganic materials record biological and physical processes through the effects of substrate...Full Text Available

International Nuclear Information System (INIS)

The thermodynamic aspects of indium-face InN growth by radio frequency plasma-assisted molecular-beam epitaxy (rf-MBE) and the nucleation of InN on gallium-face GaN (0001) surface were investigated. The rates of InN decomposition and indium desorption from the surface were measured in situ using reflected high-energy electron diffraction and the rf-MBE 'growth window' of In-face InN (0001) was identified. It is shown that sustainable growth can be achieved only when the arrival rate of active nitrogen species on the surface is higher than the arrival rate of indium atoms. The maximum substrate temperature permitting InN growth as a function of the active nitrogen flux was determined. The growth mode of InN on Ga-face GaN (0001) surface was investigated by reflected high-energy electron diffraction and atomic force microscopy. It was found to be of the Volmer-Weber-type for substrate temperatures less than 350 deg. C and of the ...

Science.gov (United States)

A vertical cavity surface emitting laser that emits visible radiation is built upon a substrate, then having mirrors, the first mirror on top of the substrate; both sets of mirrors being a distributed Bragg reflector of either dielectrics or other materials which affect the resistivity or of semiconductors, such that the structure within the mirror comprises a plurality of sets, each having a thickness of {lambda}/2n where n is the index of refraction of each of the sets; each of the mirrors adjacent to spacers which are on either side of an optically active bulk or quantum well layer; and the spacers and the optically active layer are from one of the following material systems: In{sub z}(Al{sub y}Ga{sub 1{minus}y}){sub 1{minus}z}P, InAlGaAs, AlGaAs, InGaAs, or AlGaP/GaP, wherein the optically active region having a length equal to m {lambda}/2n{sub eff} where m is an integer and n{sub eff} is the effective index of refraction of the laser ...

Energy Technology Data Exchange (ETDEWEB)

Polycrystalline ZnS semiconducting films have been prepared in sandwich configuration by spray pyrolysis technique using ZnO-coated glass substrates and mixed aqueous solutions of ZnCl{sub 2} and thiourea. The sandwich structures have been produced successfully by means of ZnO-coated glass substrates. The produced ZnS films have been crystallized in a wurtzite structure and had a direct band gap energy of 3.62 eV. The electrical properties of the sample have been studied by an analysis based on the thermally stimulated current spectra in the temperature range of 40-300 K with various heating rates. A set of curves of I (T) for varying initial density of filled traps at a heating rate of {beta} {sub 2}=0.06 K s{sup -1} indicate that the observed peaks in the TSC curve of polycrystalline ZnS films have first-order features. In order to evaluate the trap parameters of ZnS films, we have used curve-fitting method. The values of the frequency factor ...

Science.gov (United States)

Plerocercoids of the tapeworm Spirometra mansonoides produce a substance that stimulates growth of experimental hosts. We report purification of plerocercoid growth factor (PGF) to homogeneity by a process involving isolation and solubilization of plerocercoid membranes, isoelectric point selection by chromatofocusing chromatography or preparative isoelectric focusing, and anion-exchange chromatography. A radioreceptor assay (RRA) for human growth hormone (hGH) was used to detect PGF and purity of the 27.5-kDa protein was judged by sodium dodecyl sulfate-polyacrylamide gel electrophoresis (SDS-PAGE). Proteolytic activity was detected in the 27.5-kDa protein by gelatin substrate PAGE. Characterization of PGF as a neutral cysteine proteinase was based on substrate and inhibitor specificities and dependence on pH and thiol-containing reagents. The association of hGH agonist and proteinase activities was shown by comparing RRA and hydrolytic ...

Science.gov (United States)

The strain dependence of Si-Ge interdiffusion in epitaxial Si/Si{sub 1-y}Ge{sub y}/Si heterostructures on relaxed Si{sub 1-x}Ge{sub x} substrates has been studied using secondary ion mass spectrometry, Raman spectroscopy, and simulations. At 800 and 880 deg. C, significantly enhanced Si-Ge interdiffusion is observed in Si/Si{sub 1-y}Ge{sub y}/Si heterostructures (y=0.56, 0.45, and 0.3) with Si{sub 1-y}Ge{sub y} layers under compressive strain of -1%, compared to those under no strain. In contrast, tensile strain of 1% in Si{sub 0.70}Ge{sub 0.30} layer has no observable effect on interdiffusion in Si/Si{sub 0.70}Ge{sub 0.30}/Si heterostructures. These results are relevant to the device and process design of high mobility dual channel and heterostructure-on-insulator metal oxide semiconductor field effect transistors.

Energy Technology Data Exchange (ETDEWEB)

In this study, SnO{sub 2} thin films have been grown using spray pyrolysis technique on glass substrates under a substrate temperature (T{sub s} = 440 {sup o}C). The precursors were methanol CH{sub 4}O and anhydrous tin tetrachloride. XRD analyses yielded strong (1 1 0)-(1 0 1)-(2 0 0) X-ray diffraction peaks which are characteristics to tetragonal crystals. Atomic Force Microscopy (AFM) analyses showed the existence of clusters with particular pyramidal shapes. The main part of this study concerns the optical measurements of transmittance T({lambda}) and reflectance R({lambda}) spectra inside 250-1800 nm domain. Conjoint optical and thermal properties were deduced using the Amlouk-Boubaker Opto-Thermal Expansivity {psi}{sub AB}. The obtained value: {psi}{sub AB} {approx} 23.4 m{sup 3} s{sup -1} helped situating the performance of the as-grown SnO{sub 2} compound among most known PV-T oxides like ZnO and TiO{sub 2}.

Energy Technology Data Exchange (ETDEWEB)

Room-temperature cw operation for InGaP/InGaAlP double heterostructure (DH) laser diodes on GaAs substrates was achieved for the first time. The DH wafers were grown by low-pressure metalorganic chemical vapor deposition using methyl metalorganics. A lasing wavelength of 679 nm and a threshold current of 109 mA at 24C were obtained for an inner stripe structure laser diode with a 250- m-long and 7- m stripe geometry. The laser operated at up to 51C. The characteristic temperature T0 was 87 K at around room temperature. The lowest threshold current density, 5.0 kA/cmS, was obtained with a 20- m stripe width laser diode under room-temperature pulsed operation.

Energy Technology Data Exchange (ETDEWEB)

Following tuber excision from the mother plant sucrose synthase activity fell from 3,120 to 960 nmol/g.f. wt./h within 7 days and starch synthesis ({sup 14}C sucrose incorporated into isolated discs) from 23 to 7 nmol/g.f. wt./h. While the maximum catalytic activity of sucrose synthase was more than sufficient to account for the observed rate of starch synthesis a maximum of 27% of sucrose incorporated by discs was converted into starch within 3 h. This compared with 80% conversion of {sup 14}C glucose incorporated. Tuber excision also reduced the rate of starch biosynthesis with glucose as a substrate (from 206 to 64 nmol/g.f. wt./h). The activities of UDPG-pyrophosphorylase, PPi-PFK, ATP-PFK, starch synthase and hexokinase (glucose or fructose substrates) were unaffected by tuber removal. ADPG pyrophosphorylase activity was reduced from 8,000 to 4,500 nmol/g.f. wt./h. Preliminary experiments indicate that the decline in sucrose synthease ...

Energy Technology Data Exchange (ETDEWEB)

Highly resistant, high-transmittance woodceramic thin films were prepared using rf magnetron sputtering of a woodceramic disk in argon plasma. A film series was deposited based on substrate temperature, which was varied from 50 to 500 degree C. The film's electrical and optical properties depended on substrate temperature. Films deposited below 300 degree C were insulative, {rho}>10{sup 10} {omega} {center_dot} cm. Films deposited at 50 degree C had a density of 1.9-2.2 g/cm{sup 3} comparable to that of single crystal graphite. Below 200 degree C, films had higher transmittance than typical DLC films in the visible and infrared region. Infrared C-H absorption spectrum was observed by Ft-IR and there exist two types of bonding corresponding to sp{sup 2} or SP{sup 3}. (author)

International Nuclear Information System (INIS)

Iron oxide thin films have been obtained by spray pyrolysis using 100% methanolic and ethanolic solutions of iron tri-chloride. The films were deposited onto ITO-coated glass substrates. The preparative conditions have been optimized to obtain compact, pin-hole-free and smooth thin films which are adherent to the substrate. The structural, morphological and compositional characterizations have been carried out by X-ray diffraction, scanning electron microscopy and energy dispersive X-ray analysis. The films deposited using ethanolic solution results into pure hematite; #alpha#-Fe_2O_3 thin films, however, films deposited using methanolic solution consists of hematite and maghemite-c phases of iron oxide. The films are nanocrystalline with particle size of 30-40 nm. The optical absorbance of the film was of the order of 10"5 cm"-"1. The optical band gap of films was found to be 2.26 and 2.20 eV for the films deposited using methanolic and ...

International Nuclear Information System (INIS)

The dependence of the photoluminescent properties of In_0_._4_8(Al_yGa_1_-_y)_0_._5_2P alloys (0#<=#y#<=#0.5) on growth temperature and substrate misorientation off GaAs(100) has been studied. Samples were grown using low-pressure metalorganic vapor phase epitaxy. By studying the dependence of ordering behavior in InGaP as a function of substrate misorientation and growth temperature simultaneously, a very large range in low-temperature photoluminescence emission energy---135 meV---has been obtained. The photoluminescence linewidth exhibits a strong, continuous dependence on the extent of atomic ordering (the emission energy) in the alloys. The results indicate that inhomogeneity in the microstructure of the material (i.e., between ''ordered'' domains and the ''disordered'' matrix) is the dominant photoluminescence broadening mechanism. This investigation has allowed a significant optimization of the optical properties of these materials, ...

International Nuclear Information System (INIS)

Focused ion beam (FIB) irradiation of a thin Ni_2Si layer deposited on a Si substrate was carried out and studied using an in-situ transmission electron microscope (in-situ TEM). Square areas on sides of 4 by 4 and 9 by 9 microm were patterned at room temperature with a 25 keV Ga"+-FIB attached to the TEM. The structural changes of the films indicate a uniform milling, sputtering of the Ni_2Si layer and the damage introducing to the Si substrate. Annealing at 673 K results in the change of the Ni_2Si layer into an epitaxial NiSi_2 layer outside the FIB irradiated area, but several precipitates appear around the treated area. Precipitates was analyzed by energy dispersive X-ray spectroscopy (EDS). Larger amount of Ni than the surrounding matrix was found in precipitates. Selected area diffraction (SAD) patterns of the precipitates and the corresponding dark field images imply the formation of a Ni rich silicide. The relation between the FIB tail ...

Energy Technology Data Exchange (ETDEWEB)

We demonstrate that the excess vacancies induced by a 1 MeV Si implant reduce the excess interstitials generated by a 40 keV Si implant during thermal annealing when these two implants are superimposed in silicon. It is shown that this previously observed reduction is dominated by vacancy annihilation and not by gettering to deeper interstitial-type extended defects. Interstitial supersaturations were measured using B doping superlattices (DSL) grown on a silicon-on-insulator (SOI) substrate. Implanting MeV and keV Si ions into the B DSL/SOI structure eliminated the B transient enhanced diffusion normally associated with the keV implant. The buried SiO{sub 2} layer in the SOI substrate isolates the deep interstitials-type extended defects of the MeV implant, thereby eliminating the possibility that these defects getter the interstitial excess induced by the keV Si implant. {copyright} {ital 1999 American Institute of Physics.}

International Nuclear Information System (INIS)

An x-ray fluorescence spectrometer was designed and fabricated which nondestructively determines the thickness of aluminum cladding at small suspected thin spots in the inner or outer surface of actinide reactor tubes. The analysis method is based on the difference in absorption of actinide L/sub #alpha#/ and L/sub #beta#/ fluorescent x-rays in passing through the cladding. Calibration plots of the logarithm of the L/sub #beta#//L/sub #alpha#/ x-ray intensity ratio versus cladding thickness are linear to at least 40 mils for U-Al, U_3O_8-Al, and PuO_2-Al substrates. Accuracy and precision of the experimentally determined cladding thickness and evaluated for both uranium and plutonium substrates. Experimental thickness data are reported for 618 quality assurance analyses on six Mark 41 PuO_2-Al target tubes. An x-ray fluorescence cladding thickness monitor operated with a computer-controlled fluoroscope holds considerable promise for quality ...

Energy Technology Data Exchange (ETDEWEB)

A lightweight, low permeability liner for graphite epoxy composite compressed gas storage vessels. The liner is composed of polymers that may or may not be coated with a thin layer of a low permeability material, such as silver, gold, or aluminum, deposited on a thin polymeric layer or substrate which is formed into a closed bladder using torispherical or near torispherical end caps, with or without bosses therein, about which a high strength to weight material, such as graphite epoxy composite shell, is formed to withstand the storage pressure forces. The polymeric substrate may be laminated on one or both sides with additional layers of polymeric film. The liner may be formed to a desired configuration using a dissolvable mandrel or by inflation techniques and the edges of the film seamed by heat sealing. The liner may be utilized in most any type of gas storage system, and is particularly applicable for hydrogen, gas mixtures, and oxygen ...