International Nuclear Information System (INIS)

... obtain the film thickness for a given x-ray intensity ratio. 2.3 ANALYSING FOR

Energy Technology Data Exchange (ETDEWEB)

Both the sign and magnitude of residual stress can vary with the thickness of sputter deposited films. The origins of this behavior are not well understood. In this work, the authors consider the correlation between the residual stress behavior and the depth dependence of impurities in thin (2.5 nm--150 nm) sputtered Mo and Ta films. They also consider the effects of phase transformations and microstructural changes on the stress behavior. Films were deposited onto Si substrates with native oxide. The residual stress observed in the Mo films varied from highly compressive at 2.5 nm film thickness to {approximately}0 at 10 nm thickness. Ta films also exhibited a high compressive stress, which relaxed from highly compressive to tensile between 10 nm and 50 nm film ...

Energy Technology Data Exchange (ETDEWEB)

The kinetics of passive film formation on iron in borate buffer solution has been studied at different anodic potentials. The process of film growth has been found to occur in four distinct stages. About 80-90% of the total film thickness formed in 1h grows during the initial two stages which last for only 1-3s (depending upon potential). The electric field strength across the film is not constant but decreases with progressing film growth. The thickness of the film determined ellipsometrically is less than that calculated from the electric charge consumed. The process of anodic film formation is accompanied by the dissolution of iron which occurs over the whole range of potentials.

International Nuclear Information System (INIS)

By means of ESCA the composition and the thickness of passive films formed on austenitic stainless steels were investigated after the attack of nitric acid at various temperatures and acid concentrations. The outermost layers of the oxide film consist of SiO_2, then a layer rich of Cr-oxid follows, containing also some Mo in the four- and sixvalent state. Ni does not contribute to the oxide film. Cr is also enriched in the metal just below the oxide film. (orig.).

Energy Technology Data Exchange (ETDEWEB)

The emittance of aluminum components exposed to low-temperature aqueous solutions were required for thermal analysis of a Loss of Cooling Accident for the Savannah River Site production reactors. Experimental data for the thickness and emittance of oxide films formed under these conditions were collected and reviewed. Correlations were developed for the oxide film thickness and corresponding total hemispherical emittance. Film thickness and emittance were also measured for the specific conditions of interest in order to verify the predictions based on the literature data. After one year of exposure in 30deg C reactor moderator, the aluminum oxide film thickness is predicted to be 6.4 [mu]m[+-]10%; this value is relatively insensitive to exposure time. Some phenomena which would tend to yield thicker oxide ...

Energy Technology Data Exchange (ETDEWEB)

The temperature dependence of the spontaneous magnetization of epitaxial iron films with a thickness ranging from d=20 to 200nm has been measured. The films are grown on GaAs (100) substrates which are covered by a 150nm thick silver (100) buffer layer. For three-dimensional BCC iron it was observed already in 1929 that saturation of the spontaneous magnetization for T->0 is perfectly described by a T{sup 2} power law. On the other hand, for thin two-dimensional (2D) iron films a T{sup 3/2} law has been established in many recent experimental investigations. In our iron films grown on diamagnetic silver, this dimensionality change occurs at a thickness between d=100 and 200nm. Comparison of the here-observed T{sup 3/2} coefficients with those on iron films grown on paramagnetic tungsten (110) shows that the 2D ...

Energy Technology Data Exchange (ETDEWEB)

The properties of a helium film on the surface of solid parahydrogen are investigated. It is shown that wetting of the solid hydrogen by the liquid helium occurs. The transport velocities along the He II film on the solid parahydrogen surface are measured in broad temperature, film height, and level difference ranges. It is shown that the transport velocity in this case has the least value as compared with its value on other substrates. The thickness of the helium-saturated film is determined on the solid hydrogen surface on the basis of the data obtained, and the value is in good agreement with the results of a computation performed within the framework of the Frenkel' theory.

Energy Technology Data Exchange (ETDEWEB)

A radio frequency sputtering apparatus with a pair of targets has been developed for depositing a film of uniform thickness onto a complex-geometric specimen such as the retainer of a ball bearing. The deposition characteristics of the apparatus were compared with those of the conventional sputtering apparatus. Lubrication properties of MoS/sub 2/ films made by these devices were also compared under a variety of conditions. Finally, friction and wear of MoS/sub 2/ films applied to angular-contact type ball bearings of 20 mm bore were studied in air, nitrogen and vacuo. The two-target sputtering has an advantage mentioned above. However, the films deposited by the method exhibited a rather short wear life because of the temperature rise of the substrate during ion bombardment and during the sputtering process. This temperature dependence was observed in films on ...

International Nuclear Information System (INIS)

The composition of sputter-deposited HgS films was determined by electron microprobe analysis. From the relative x-ray intensity as a function of film thickness, the depth of the ionizations that produce SK sub(#alpha#) and HgM sub(#alpha#) was found to be approximately 0.65 #mu#m at an accelerating voltage of 15 kV. This value agreed well with a value calculated from Castaings' empirical law after absorption correction. The determination of film composition was limited to sufficiently thicker films than this critical value, usually 1 - 2 #mu#m thick. The relation between the conposition of bulk standard determined by chemical analysis and the x-ray intensity ratio was used for the correction of film composition. The results showed that the crystal structure of HgS films was independent of the composition, i.e., the ...

International Nuclear Information System (INIS)

Radionuclide X-ray fluorescence analysis was used for the determination of Cu, Y and Ba in very thin high-temperature superconducting films. The precision of the method is better than 3% for about 1 #mu#m thick films. The atomic emission ICP spectrometry was used to testify results of XRF analysis. An acceptable agreement of both methods was obtained. (author) 4 refs.; 2 tabs.

Energy Technology Data Exchange (ETDEWEB)

Cold spray was employed as a novel low temperature approach to deposit titanium dioxide (TiO{sub 2}) photocatalytic film. The film microstructure was characterized using X-ray diffraction and scanning electron microscopy. The photocatalytic performance was examined through acetaldehyde degradation under ultraviolet illumination. Results showed that TiO{sub 2} film was successfully deposited on substrate surface through cold spray. The film thickness reached up to 15 {mu}m. The film presented a rough surface and porous structure. Owing to the low temperature of spray powder, no phase and particle size changes occurred to TiO{sub 2} during deposition. It was found that the cold-sprayed TiO{sub 2} film was active for photodegradation of acetaldehyde.

Energy Technology Data Exchange (ETDEWEB)

The use of capacitance sensors for measuring phase concentrations in two-phase flow has gained popularity in recent years. In designing such sensors, there are many issues which must be considered in order to optimize performance: two-phase flow regime, permittivity of the phases, duct geometry, electrical shielding, desired spacial resolution of film thickness, and temperature variation in the flow field. These design issues are discussed and are used to optimize the design of a capacitance sensor which is used to measure vapor volume fraction in annular, two-phase vertical upflow and downflow in a square duct. The sensor was tested and implemented in a 12.7 mm square duct mounted in a flow boiling facility containing FC-72, a low permittivity dielectric fluid ({epsilon}{sub r} = 1.75). Using analytical modeling, an adjustable-length, parallel-plate design was developed and refined to achieve good sensitivity to flow conditions. The sensor ...

Energy Technology Data Exchange (ETDEWEB)

The comprehension of passivity and its protective character against corrosion is closely connected with the electronic properties of passive films. Passive films formed anodically on carbon steel in borate/boric acid solution, pH 9.2, have been characterised by electrochemical impedance spectroscopy (EIS). Mott-Schottky plots and impedance measurements were made on films formed at different potentials and times. The investigation allowed the determination of the semiconductive properties of the films. The results of the capacitance response indicate that the passive films behave like highly doped n-type semiconductors, showing that the passive film properties are dominated by iron. The value of donors density (N {sub D}) for the passive film is of the order of 10{sup 21} cm{sup -3} and decreases with increasing formation time and potential, ...

Energy Technology Data Exchange (ETDEWEB)

An x-ray diffraction technique for determining thin-film thickness is presented which should prove to be a valuable alternative to the array of spectroscopies (Rutherford backscattering spectrometry, Auger electron spectroscopy, etc.) currently favored for these measurements. Some of the virtues of this x-ray diffraction approach are its nondestructive nature, fast data acquisition rate (enabling in situ observations), thickness resolution better than 5 nm, and conventional equipment requirements. Results are shown for Pd/sub 2/Si thin films grown during isothermal annealing of Pd coatings (100 nm) on Si at 200 /sup 0/C for various amounts of time. A comparison of these x-ray measurements with Rutherford backscattering spectrometry data taken from the same specimens is used to demonstrate the validity of the x-ray technique.

International Nuclear Information System (INIS)

The crystallite size and orientation in molybdenum films prepared by magnetron sputtering at a low rate of typical 1 (angstrom)s and a pressure of 0.45 Pa was investigated by X-ray diffraction and texture analysis. The surface topography was studied using atomic force microscopy. Increasing the film thickness from 20 nm to 3 microm, the films show a turnover from a (110) fiber texture to a (211) mosaic-like texture. In the early state of growth (20 nm thickness) the development of dome-like structures on the surface is observed. The number of these structures increases with film thickness, whereas their size is weakly influenced. The effect of texture turnover is reduced by increasing the deposition rate by a factor of six, and it is absent for samples mounted above the center of the magnetron source. The effect of texture turnover is ...

Energy Technology Data Exchange (ETDEWEB)

The initial growth process and surface structure of thin Pd(silicide) films on clean Si(111)-7x7 surfaces have been studied by low energy ion scattering (ISS) and LEED-Auger techniques. Considerable reaction between Pd and Si at room temperature is observed to extend up to 25 ML thickness of deposited Pd. Heat treatment of the room temperature film produced epitaxial silicide Pd/sub 2/Si(0001) films covered with the accumulated elementary Si layers of 1-2 ML thickness. Deposition of 1/3 ML Pd onto a heated substrate gives a Pd-embedded ordered surface of Si(111)-..sqrt..3x..sqrt..3R30/sup 0/, the feature being similar to the cases of Ag, Au/Si(111) systems.

British Library Electronic Table of Contents (United Kingdom)

Nanocrystalline chromium oxynitride films were deposited by reactive RF magnetron sputtering of metallic chromium target in argon and helium atmospheres. The paper deals with consequence of increase in oxygen partial pressure on structural, hydrophobic and optical properties of chromium oxynitride films. The film stoichiometry changes from CrN and Cr2O3 to only Cr2O3 with increase in oxygen partial pressure as evident from X-Ray Diffraction analysis in both cases. The average crystallite size decreases with increase in oxygen partial pressure for both gas atmospheres. The thickness calculated from transmission data and surface profilometer are in good harmony with each other. The deposited films are hydrophobic by nature and the contact angle of the films varies as a function of surface ro...

Energy Technology Data Exchange (ETDEWEB)

The effect of Mo addition as an alloying element to stainless steel alloys is investigated by capacitance (Mott Schottky approach), and photoelectrochemistry measurements. Complementary studies were made using Auger electron spectroscopy and X-ray photoelectron spectroscopy. The Mott-Schottky approach and the photoelectrochemical studies showed that the presence of Mo as an alloying element affects the semiconductive properties of the oxide films. The analytical results have shown that the oxide films formed on stainless steels are composed by an external Fe rich region and an inner Cr rich region. No significant amount of Mo was found in the outer layers of the film. The presence of Mo leads to an increase of the chromium content in the inner layers of the film, although without increasing the film thickness. (orig.) 30 refs.

Science.gov (United States)

Critical power at boiling transition is an important factor in a boiling water reactor (BWR) fuel bundle design. Boiling transition under high quality accounts for dryout as the result of the complete disappearance of film flow on a fuel rod. This liquid film vanishing process can be calculated by the liquid film model, which takes into account the evaporation due to heat from the rod surface, liquid film entrainment by steam flow, and liquid droplet deposition. It is known that spacers affect liquid film entrainment and liquid droplet deposition, so the detailed study of spacer effects on hydrodynamic characteristics is necessary for critical power prediction based on the film flow model. Many studies have been conducted to examine spacer effects on liquid film flow. However, most of them are restricted to simple test sections such as a ...

International Nuclear Information System (INIS)

Extended X-ray absorption fine structure (EXAFS) measurements of bismuth clusters in the temperature range of 23 -300 K have been performed using synchrotron radiation in order to investigate the size dependent phase transition. The inter-atomic distances around 3.0 A and 3.6 A are attributed to the nearest neighbors within the layer and between layers, respectively. EXAFS functions were analysed by the curve fitting method within a symmetric distribution approximation. The nearest neighbor distance of the 0.5 nm thick films is shorter than that of the 300 nm thick films at all the temperatures, which is related to the reduction of the inter-layer correlation.

International Nuclear Information System (INIS)

Crystalline and non-crystalline iron oxide (#alpha#-Fe_2O_3) thin films were obtained by spray pyrolysis onto glass substrate at different temperatures. The results of X-ray diffraction showed that with increasing the deposition time, the film structure changed from non-crystalline to crystalline at the same substrate temperature. At different substrate temperatures and low deposition times (5 min), iron oxide appears almost in non-crystalline form. With rising the substrate temperature and deposition time, the crystallinity was improved. The effect of substrate temperature as well as deposition time on the optical features (absorption coefficient and bandgap) and optical constants of these films has been investigated. Optical constants of the films were determined from spectrophotometric measurement of reflectance and transmittance. Analysis of the results showed that, for non-crystalline iron oxide ...

Energy Technology Data Exchange (ETDEWEB)

The electrochemical method has been used to deposit zinc oxide (ZnO) thin films from aqueous zinc nitrate solution at 80 deg. C onto fluorine doped tin oxide (FTO) coated glass substrates. ZnO thin films were grown between - 0.900 and - 1.025 V vs Ag/AgCl as established by voltammogram. Characterisation of ZnO films was carried out for both as-deposited and annealed films in order to study the effect of annealing. Structural analysis of the ZnO films was performed using X-ray diffraction, which showed polycrystalline films of hexagonal phase with (002) preferential orientation. Atomic force microscopy was used to study the surface morphology. Optical studies identified the bandgap to be {approx} 3.20 eV and refractive index to 2.35. The photoelectrochemical cell signal indicated that the films had n-type electrical conductivity and ...

International Nuclear Information System (INIS)

Magnetic materials such as yttrium iron garnet (YIG) are of great importance for its magneto-optic properties and for their potential applications in the domain of optical telecommunications. The deposition of thin films of YIG, on quartz or GGG (gadolinium gallium garnet) substrate, was performed using radio frequency non reactive magnetron sputtering, followed by high temperature annealing which is needed to enhance the crystallinity of the layers. Rutherford backscattering spectrometry RBS was used to determine the thickness and stoichiometry of the performed layers in order to investigate correlations between growth conditions and the quality of the final material. RBS measurements showed the influence of the deposition time and the temperature substrate on the film growth and its stoichiometry. (author)

Energy Technology Data Exchange (ETDEWEB)

The magnetization of ultrathin bcc Fe films (two and three monolayers) on MgO was measured and compared with the behavior predicted for a two-dimensional ferromagnet. The experiment indicated that no hysteresis was present in the magnetization. Instead, the magnetization at low temperature was affected by a marked field cooling effect. These observations lead to the conclusion that films of Fe on MgO of such thickness exhibit superparamagnetic behavior as if they were not entirely continuous. In contrast, films thicker than five monolayers exhibit a magnetic response close to that of bulk iron.

CERN Document Server

substrate). Within each group of simulations, three lubricant film thicknesses are studied to examine the effect of varying lubricant thickness. Statistical data are collected from each simulation and presented in this work. Via these data, together with the evolution, of atomic and molecular configurations, a very detailed picture of the properties of this thin film interface is presented. In particular, we conclude that perfluoropolyether lubricant forms distinct molecular layers when confined between two substrates, the rate of heat generation under shearing conditions typical of those in a head-disk interface is insufficient for thermal mechanisms to result directly in lubricant degradation, and mechanical stresses attained in the head-disk interface are unlikely to result in any significant degree of lubricant degradation. This thesis examines the tribology of a head-disk interface in an operating ...

International Nuclear Information System (INIS)

The adherent magnetite film thickness, corrosion rate and the loose crud on the surface of carbon steel and other structural materials were evaluated by inserting the coupons in the two autoclaves connected to the two ends of the PHT systems of Indian PHWRs. This paper includes an analysis of the results obtained during the hot conditioning of TAPP-3 and 4, Kaiga-3 and 4, and RAPP-5. The system temperatures of 230 deg C to 260 deg C and the adherent magnetic thickness of 0.30 ?m to 0.75 ?m on the internal surface of carbon steel were achieved during the hot conditioning of these reactors. The time duration of termination of the hot conditioning ranged from 48 to 71 hours. The maximum magnetite film thickness of 0.75 ?m in 71 hours and temperature 260 deg C and a minimum thickness of 0.30 nm in 48 hours at 230 deg C were achieved during hot conditionings. The XRD ...

International Nuclear Information System (INIS)

In this work, amorphous hydrocarbon (a-C:H) film deposition on metallic mirrors was studied during working shots in tokamak T-10 and at exposure in Ar/CHD3/D2 dc magnetron discharge in a special laboratory high vacuum setup. Analysis of film composition (including hydrogen content) was carried out using nuclear physical methods. Thickness and optical parameters (refractive and extinction coefficients) of the films were estimated by ellipsometry. Laboratory films can be characterized as soft a-C:H films in comparison with hard tokamak films (? = 1.2 and 1.8 g/cm3, respectively). For the first one, a linear dependence of deposition rate on mirror temperature was observed in a wide temperature range. The addition of methane into initial Ar/D2 magnetron gas mixture leads to an increase of deposition rate. The data obtained should be taken into ...

Energy Technology Data Exchange (ETDEWEB)

The passive films formed on iron metal, alloys or stainless steel are extremely thin oxides or hydroxides and possess the properties of high chemical stability in the environment. These films show characteristics interested both electrical as well as electrochemical point of view due to the thin thickness of the films. Auger Electron Spectroscopy, X-ray Photoelectron spectroscopy and so on which are the conventional electrochemical measurement methods or the surface analysis methods are used for the analysis and evaluation of these films, however, at present, the application of research technique focusing the superconductor characteristics of the films are tried. Although, the potential modulation reflection spectroscopy method has merits like possibility of in-situ measurement, high precision, possibility of stable analysis even for extremely thin ...

Energy Technology Data Exchange (ETDEWEB)

In this work we present an ultra-low temperature method for the oxidation of an amorphous silicon-carbide-nitride (SiCN) material. The SiCN is deposited on silicon substrates by plasma enhanced chemical vapor deposition using CH{sub 4}, SiH{sub 4}, and N{sub 2} chemistry. The physical and chemical properties are characterized for the as-deposited SiCN and post-oxidized films are discussed. The SiCN film is exposed to oxygen plasma, where it undergoes a chemical transformation into a binary SiO{sub 2} material system. A 1.7 nm/min oxidation rate is typical for this process and compares favorably to oxidation methods utilizing much higher temperatures. The substrate temperature remains extremely low throughout the oxidation process, T{sub s} < 200 deg. C. Changes in film stress, optical constants, film thickness, surface roughness, and film density are ...

Energy Technology Data Exchange (ETDEWEB)

Scanning electrochemical microscopy (SECM) was applied to evaluate the heterogeneity of a passive film formed on a pure iron electrode in deaerated pH 8.4 borate solution. A probe current image of SECM was measured with a tip-generation/sub-strate-collection (TO/SC) mode in deaerated pH 8.4 borate solution containing 0.03 moldm{sup -3} Fe(CN){sub 6}{sup 4-} as a mediator. The difference in thickness of passive films formed on two iron plates at different potentials could be evaluated from the probe current image. The probe current image of the passivated iron surface with distinctive crystal grains was composed of the patch patterns, the shapes of which coincided completely with the shapes of the substrate crystal grains. The probe current flowed above the grain surface oriented to {l_brace}100{r_brace} plane was less than that above the grain surface oriented to {l_brace}110{r_brace} or {l_brace}111{r_brace} plane. The ...

International Nuclear Information System (INIS)

Austenitic stainless steels have been implanted with molybdenum ions (Mo"+, 100 keV, 2.5 x 10"1"6 atoms cm"-"2). The implanted material has been characterized by XPS and RBS. The implanted region has a thickness of #approx# 1000 A with a maximum molybdenum concentration of #approx# 9 at.% Mo located at #approx# 210 A from the surface. The effects of implanted molybdenum on the passivation of the alloy in 0.5 M H_2SO_4 have been investigated by electrochemistry and XPS. After XPS analysis the samples were transferred without exposure to air into a glove-box with an inert atmosphere. The electrochemical behaviour of the alloy is significantly modified by the implanted molybdenum. The major effect is that the activation peak disappears. A bilayer structure (outer hydroxide/inner oxide) of the passive film is observed for both the implanted and non-implanted alloys and the thicknesses of the films are ...

Science.gov (United States)

A knowledge of surface film growth kinetics can be quite useful in the production of materials for uses ranging from protective coatings to microelectronic devices. A technique for determining the kinetics of film growth is presented which should prove to be a valuable alternative to the array of spectroscopies (AES, RBS, etc.) currently favored for these measurements. Some of the virtues of this X-ray diffraction approach are its non-destructive nature, thickness resolution better than 50 {angstrom} and conventional equipment requirements. Results obtained for the growth of Pd{sub 2}Si films during thermal annealing of Pd coatings on Si, indicate parabolic growth over a temperature range of 160-222 C. The rate constant was found to be k{prime} = 7 {times} 10{sup {minus}4} exp ({minus}1.06 eV/kT) cm{sup 2}/sec, where (film thickness){sup 2} = k{prime} x time. ...

Science.gov (United States)

A focused ion beam (FIB) technique was applied to cross-sectional specimen preparation to observe an interface between a plasma sprayed coating and an aluminum (Al) substrate by transmission electron microscopy (TEM). The surface of the sprayed coating film has a roughness of several tens of microns. Sputter rates for the coating film and the substrate are greatly different. The rough surface and the difference in sputter rate cause problems in making TEM specimens with smooth side walls. The top surface of the coating film was planerized by the FIB before fabricating the TEM specimen. The interfaces were investigated by TEM and energy-dispersive X-ray (EDX) analysis. The TEM observation revealed that there is a 10 nm thick amorphous layer at the interface between the coating film and substrate. The coating film consists of two kinds of sublayers with bright and ...

Energy Technology Data Exchange (ETDEWEB)

A method for using in situ X-ray absorption near edge spectroscopy to determine the composition of passive, transpassive, and nonreducible thin oxide films is described. The method is demonstrated by determining the composition of the passive films formed in pH 4.5, 0.1 M acetate buffer, on 100 {angstrom} thick Fe-yCr alloys (y = 8.5, 15, 19, 23 atom %) at potentials: (1) low in the passive region ({minus}0.3 V vs. mercurous sulfate reference electrode, MSE); (2) high in the passive region; (3) in the transpassive region; and (4) in the cathodic region where the air-formed film is not fully reduced. The nonreducible film at {minus}1.2 V is entirely a Cr{sup 3+} oxide/hydroxide. This nonreducible film persists at anodic potentials. At {minus}0.3 V, the passive film on each alloy is significantly enriched in Cr. The film ...

Energy Technology Data Exchange (ETDEWEB)

The plastic displacements around Knoop indentations made in hard titanium/aluminum multilayered films on soft aluminum alloy substrates have been studied. Indentations were cross-sectioned and imaged using the focused-ion-beam (FIB) milling and high-resolution scanning electron microscopy (SEM), respectively. The FIB milling method has the advantage of removing material in a localized region without producing mechanical damage to the specimen. The micrographs of the cross-sectioned indentations indicate that most of the plastic deformation around the indentation is dominated by the soft aluminum substrate. There is a very small change in the multilayered film thickness around the indentation{emdash}less than 10{percent}. The plastic deformation of the thin film resembles a membrane being deflected by a localized pressure gradient across the membrane. Stress-induced voids are also observed in the ...

International Nuclear Information System (INIS)

The in-depth distribution of phases in c-BN films deposited by Ion Beam Assisted Deposition (IBAD) at two different ion energy values (300 and 600 eV) was investigated using the quantitative IR transmission measurements and the HREM technique. Whatever the value of the studied ion energies, the characteristic layered morphology of c-BN film is observed including the interfacial sp"2 zone between the substrate and the c-BN volume. In the case of 600 eV ion energy, this interfacial zone is less well-defined in comparison with 300 eV ion energy and the corresponding thickness is more important. Furthermore, the h-BN phase is more diluted within the c-BN film volume showing that the purest phase concentration of c-BN is found for the lowest ion energy, i.e., 300 eV.

Energy Technology Data Exchange (ETDEWEB)

Ultra-thin, uniform, pinhole-free solid polymer electrolyte films having a fixed carboxylic ester group of approximately 1 {mu}m thickness were prepared by polymerization of methyl acrylate and tris(2-methoxyethoxy)vinylsilane in a glow discharge plasma. The carboxylic ester group of the plasma polymer were transformed to lithium carboxylate groups by treatment with lithium iodide. This process give a single lithium ion conductive film. These solid polymer electrolyte films showed ionic conductivities of the order of 10{sup -8} S cm{sup -1} (10{sup 4} {omega} cm{sup 2} resistance per unit area) at room temperature. (orig.).

International Nuclear Information System (INIS)

The influence of high energy electron (23 MeV) irradiation on the electrical characteristics of p-channel polysilicon thin film transistors (PSTFTs) was studied. The channel 220 nm thick LPCVD (low pressure chemical vapor deposition) deposited polysilicon layer was phosphorus doped by ion implantation. A 45 nm thick, thermally grown, SiO_2 layer served as gate dielectric. A self-alignment technology for boron doping of the source and drain regions was used. 200 nm thick polysilicon film was deposited as a gate electrode. The obtained p-channel PSTFTs were irradiated with different high energy electron doses. Leakage currents through the gate oxide and transfer characteristics of the transistors were measured. A software model describing the field enhancement and the non-uniform current distribution at textured polysilicon/oxide interface was developed. In order to assess the ...

International Nuclear Information System (INIS)

The construction materials used in coolant systems in nuclear power plants become covered with oxide films as a result of exposure to the aqueous environment. The susceptibility of the materials to different forms of corrosion, as well as the extent of the incorporation of radioactive species on the surfaces of the primary circuit, are greatly influenced by the physical and chemical properties of these oxide films. The composition and characteristics of the oxide films in turn depend on the applied water chemistry. This work was undertaken in order to collect and evaluate the present views on the structure and behaviour of oxide films formed on iron- and nickel-based materials in aqueous environments. This survey should serve to recognise the areas in which more understanding and research effort is needed. The review begins with a discussion on the bulk oxides of iron, nickel and chromium, as well as ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces that are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

International Nuclear Information System (INIS)

Radioactive "3"1Si was used as a tracer to study silicon self-diffusion in thin film silicides of cobalt, nickel, palladium and platinum. The specimens were prepared by sequential electron beam evaporation of radioactive "3"1Si and of the metal onto cleaned silicon wafers. By vacuum annealing at the appropriate formation temperature a silicide about 250 nm thick containing a sharp radioactive band about 50 nm thick was generally formed. Subsequent heating above the formation temperature resulted in a spreading of the activity owing to silicon self-diffusion. Activity profiles in the silicides were measured by a combination of ion beam sputtering, radioactivity counting and Rutherford backscattering of charged nuclear particles. (orig.).

Energy Technology Data Exchange (ETDEWEB)

We performed polarized neutron reflectometry (PNR) experiments on a 29 nm thick Au{sub 93}Fe{sub 7} film in a temperature range from 295 K down to 2 K in a vertical magnetic field up to 6 T. These high-field experiments were performed on the C5 spectrometer in Chalk River, Canada, using a split-pair cryomagnet. The magnetization as determined by PNR can be described with a Brillouin function from 295 K down to 50 K assuming the magnetic moment of isolated Fe atoms, i.e. 4{mu}{sub B} per Fe atom. Below 50 K the onset of the spin-glass freezing is observed as a strong deviation from this Brillouin type behavior of isolated atoms.

International Nuclear Information System (INIS)

Using the full potential linearized augmented plane wave (FLAPW) method, thickness dependent magnetic anisotropy of ultrathin FeCo alloy films in the range of 1 monolayer (ML) to 5 ML coverage on Pd(0 0 1) surface has been explored. We have found that the FeCo alloy films have close to half metallic state and well-known surface enhancement in thin film magnetism is observed in Fe atom, whereas the Co has rather stable magnetic moment. However, the largest magnetic moment in Fe and Co is found at 1 ML thickness. Interestingly, it has been observed that the interface magnetic moments of Fe and Co are almost the same as those of surface elements. The similar trend exists in orbital magnetic moment. This indicates that the strong hybridization between interface FeCo alloy and Pd gives rise to the large magnetic moment. Theoretically calculated magnetic anisotropy shows that the 1 ML ...

International Nuclear Information System (INIS)

The effects of gate and drain bias stresses on thin film transistors fabricated in polysilicon films crystallized using the advanced sequential lateral solidification excimer laser annealing (SLS ELA) process, which yields very elongated polysilicon grains and allows the fabrication of TFTs without grain boundary barriers to current flow, are investigated as a function of the active layer thickness and of the TFT orientation relative to the grains. The application of hot carrier stress, with a condition of V_G_S = V_D_S/2, was determined to induce threshold voltage, subthreshold swing and transconductance degradation for TFTs in thicker polysilicon films and the associated stress-induced increase in the active layer trap density was evaluated. However, this device degradation was drastically reduced for TFTs fabricated in ultra-thin films. Furthermore, the application of the same ...

Energy Technology Data Exchange (ETDEWEB)

The half-metallic Heusler alloy Ni{sub 2}MnIn is of high interest for use in spin electronics since at the Ni{sub 2}MnIn/InAs interface a spin polarization of 100% is predicted. We prepare high-quality thin films of 20-60nm thickness by co-evaporation and DC magnetron sputtering. Point-contact Andreev reflection spectroscopy yields a spin polarization of up to 54%. By spectral generalized magneto-optical ellipsometry, the dielectric and magneto-optical properties are determined and ferromagnetic behavior below the Curie temperature T{sub C}=318K is proved.

Energy Technology Data Exchange (ETDEWEB)

In this paper, the moisture buffering capacity of spruce plywood is measured by recording the change in mass of a test specimen when the air relative humidity (RH) is changed between 33% RH and 75% RH. The aim is to represent diurnal cycles in indoor humidity with 33% RH maintained for 16 h and 75% RH maintained for 8 h. Measurements are taken using two different apparatuses, which provide different convective transfer coefficients between the air and the plywood, and the results are compared to a numerical model for validation. The validated numerical model is then used to investigate the effect of initial conditions, boundary conditions and thickness on the moisture buffering capacity of plywood. The results show that the buffering capacity of plywood depends on the initial conditions and thickness of the plywood as well as the surface film coefficient and humidity cycle. (author)

Energy Technology Data Exchange (ETDEWEB)

In a work studying the corrosion and tarnishing properties of a variety of copper alloys, the alloy Cu-A110-Sn5 was found to show an excellent corrosion resistance in neutral solutions, where copper and most conventional Cu alloys are covered by thick nonprotective surface layers. The passive films formed on this alloy were characterized with electrochemical and photoelectrochemical methods. The pH dependence of the passivation and of the photocurrent behavior of the Cu-A110-Sn5 alloy clearly indicates that the passivity of this alloy in neutral solutions is due to a formation of passive film enriched with aluminum oxide. At corrosion potential a strong increase in the corrosion resistance with time is due to a gradual enrichment of the surface with aluminum oxide. This can be seen in the photocurrent spectra which change from cooper-type to aluminum-type with time. At higher applied potentials the formation of an ...

Energy Technology Data Exchange (ETDEWEB)

Chemical characterization of passive films formed on AISI 304 austenitic stainless steel, in a borate/boric acid solution at pH 9.2, under various conditions of potential, temperature, and polarizations time, was made by Auger electron spectroscopy combined with ion sputtering, and x-ray photoelectron spectroscopy (XPS). The depth chemical composition, thickness, and duplex character of the passive layers were determined after processing AES sputter profiles by their quantitative approach based on the sequential layer sputtering model. Moreover, separated contributions of elements in their oxidized and unoxidized state could be disclosed from part to part of the oxide-alloy interface. The XPS study specified the chemical bondings which take placed inside the film, between Fe and oxygen (and water).

International Nuclear Information System (INIS)

Microfabrication processes for Y-Ba-Cu-O films have been investigated, using ion-beam techniques. High-T_c superconducting lines as narrow as 0.8 #mu#m have been fabricated from epitaxial YBa_2Cu_3O_7 _- _y films by Ar ion-beam etching (IBE), combined with focused ion-beam (FIB) lithography. The resulting lines, 1.3 #mu#m wide and 2 mm long, showed a zero resistance temperature of 81 K and a critical current density of 1.9 x 10"4 A/cm"2 at 77.3 K. Maskless etching was carried out using 130-keV au"+ focused ion-beam (FIB) with a 0.1-#mu#m-diameter beam. A 50-nm-thick film was patterned into 0.3-#mu#m-wide lines at a dose of 5 x "1"6 ions/cm"2. In comparison with Ar IBE, Cl_2 reactive ion-beam etching (RIBE) exhibited an enhancement effect in sputtering yield. Ion implantation with 300-keV Si"+ "+ FIB also indicated the possibility to produce submicrometer patterns by selectively modifying ...

International Nuclear Information System (INIS)

Nb_3Sn films (Tsub(c)=17.8 K) were obtained by implantation of Sn"+ ions into Nb films (1500 A thick) after subsequent annealing. The annealing temperature required for the formation of the A15 phase in the implanted films was about 100 K higher than for Nb-Sn sandwich films evaporated at 300 K. The influence of the Sn concentration and of the annealing temperature was studied by measuring the sample resistance. The Nb-Sn compounds formed during the annealing process were analysed by measurements of the Moessbauer-effect of "1"1"9Sn. The implantation method was also used to produce Nb-Ge films with a ratio Ge/Nb approximately 1/3. The Ge-concentration and the temperature of the Nb-target (300-1070 K) were varied. These variations as well as subsequent annealing at 600-850"0C did not lead to superconducting transition temperatures above 8 K. (Auth.).

International Nuclear Information System (INIS)

The thickness dependent magnetic properties of artificially prepared ultrathin body-centered cubic Ni films have been explored using the all electron full potential linearized augmented plane wave (FLAPW) method. We have considered two types of BCC Ni(001) films: (i) pure BCC Ni(001) and (ii) Au capped BCC Ni(001) in the range from 1 monolayer (ML) to 4 ML of Au capping coverage. The average magnetic moment of pure BCC Ni(001) is about 0.63 #mu#_B and a typical surface enhancement is found with a magnetic moment of 0.78 #mu#_B. In the presence of an Au capping layer, the magnetic moment of interface Ni is strongly suppressed to approximately 0.5 #mu#_B and this causes a reduction of average magnetic moment. Nevertheless, the Au adlayer has no meaningful induced magnetic moment. The BCC pure Ni(001) films always have in-plane magnetization up to 11 ML, but very interestingly the Au/Ni(001) shows a ...

CERN Document Server

An in-plane uniaxial magnetic anisotropy has been observed in thin Co films normally deposited onto obliquely sputtered Ta and Pt underlayers. Associated with this anisotropy is an augmented easy axis coercivity. The in-plane easy axis is, in most cases, perpendicular to the incident deposition plane. Microstructural results indicate that grains are well connected along the magnetic easy axis but are separated by long continuous voids along the hard axis, which is ascribed to a geometric shadowing effect due to the oblique incidence deposition of the underlayer. Hence, the magnetic anisotropy mimics the film growth anisotropy. It is therefore believed that the observed magnetic properties are due to magnetostatic shape anisotropy effects. In-plane coercivity and anisotropy field are shown to increase with underlayer deposition angle, underlayer thickness and magnetic layer thickness. The choice of ...

Energy Technology Data Exchange (ETDEWEB)

The compositions of passive films formed on Fe-17Fr-13Ni (at. %) and Fe-18.5Cr-14Ni-1.5Mo (100) single crystals have been determined and the structure of the alloy under the film has been investigated. The alloys were passivated in 0.05M H{sub 2}SO{sub 4} at 250 mV/SHE for 30 min. The oxygen content was measured by nuclear microanalysis using the {sup 16}O(d,p) {sup 17}O* reaction. The oxygen content in the passive film is similar for the two alloys and equal to (12{plus minus}2) 10{sup 15} O/cm{sup 2}. The cationic compositions of the passive films have been determined by {sup 4}He channeling at two incident beam energies: 0.8 and 2.0 MeV. For the two alloys studied, a total cation content of (5{plus minus}2)10{sup 15} at/cm{sup 2} is found in the passive films. The corresponding thickness is about 12 A. There is an excess of oxygen, which can be attributed to ...

International Nuclear Information System (INIS)

A method was proposed and examined to deposit thick cubic boron nitride (cBN)-rich layer of good adhesion to silicon substrate. The method combined (i) the insertion of a thick sp"2 buffer layer, and (ii) the use of an appropriate assist ion beam energy for the growth of the cBN-rich top layer. The sp"2-bonded boron nitride buffer layer was deposited under irradiation of ions with energies in the range of 200-360 eV. The buffer layer was found to contain curled graphitic basal planes, and so was supposed to be relatively deformable, and facilitate the relaxation of stresses in the cBN-rich top layer. The ion assist introduced during the growth of the cBN-rich layer was supposed to both create and annihilate defects, and so resulted in the generation and relaxation of internal stresses. Results showed that the insertion of a 492 nm sp"2 buffer layer, and the use of a beam energy of 450 eV for assisting the growth of the top layer can produce a ...

International Nuclear Information System (INIS)

We have studied in detail the gamma radiation induced changes in the electrical properties of the (TeO_2)_0_._9 (In_2O_3)_0 _._1 thin films of different thicknesses, prepared by thermal evaporation in vacuum. The current-voltage characteristics for the as-deposited and exposed thin films were analysed to obtain current versus dose plots at different applied voltages. These plots clearly show that the current increases quite linearly with the radiation dose over a wide range and that the range of doses is higher for the thicker films. Beyond certain dose (a quantity dependent on the film thickness), however, the current has been observed to decrease. In order to understand the dose dependence of the current, we analysed the optical absorption spectra for the as-deposited and exposed thin films to obtain the dose dependences of the optical ...

International Nuclear Information System (INIS)

The changes in microstructure of a specially prepared boron nitride (BN) film as a function of film depth were studied by high resolution transmission electron microscopy (HRTEM) and other materials analysis tools. These changes were then correlated to the changes in processing parameters during film growth. The analyzed film was fabricated by the four-step ion-assisted deposition procedure known to be effective in film-stress engineering for the formation and retention of a thick cubic BN (cBN) layer with a three-step buffer-layer deposition. In this deposition, the energy of the ions assisting cBN formation was increased stepwise from 200 to 280, and then to 360 eV [S.F. Wong, C. W. Ong, G.K.H. Pang, K.Z. Baba-Kishi, W. M. Lau, J. Vac. Sci. Technol. A 22 (2004) 676]. The nominal thickness of the cBN layer was 650 nm and that for each of ...

Energy Technology Data Exchange (ETDEWEB)

Correlation between mechanical stress and hydrogen effects on radiation damage in polycide-gate MOS capacitors was investigated as a function of gate-oxide thickness. The compressive stress magnitude was altered by varying the silicide (TiSi/sub 2/ or WSi/sub 2/) thickness in the polycide-gate electrode, and hydrogen introduction into gate-SiO/sub 2/ film was carried out by diffusion from plasma-deposited silicon-nitride passivation film (SiN-Cap). In a MOS capacitor without passivation film (No-Cap sample), it was found that compressive stress on gate-SiO/sub 2/ reduces both positive charge build-up (..delta..Qot) and interface-trap generation (..delta..Dit). Radiation induced shift, ..delta..Qot exhibits a smaller stress effect as compared with ..delta..Dit. As gate-SiO/sub 2/ thickness decreases, the stress effect on ..delta..Qot increases, while this effect ...

International Nuclear Information System (INIS)

Zinc oxide thin films were obtained by laser ablation of a Zn target in oxygen reactive atmosphere, the oxygen being supplied either by a standard gas inlet valve or from a radio-frequency (rf) oxygen plasma. Pt-coated silicon and MgO were used as substrates. The influence of the deposition parameters as laser wavelength (266, 355, 1064 nm), laser fluence (1.5-20 J/cm2) and oxygen pressure (1-60 Pa) was studied. The influence of the rf plasma beam addition on the morphological proprieties of zinc oxide films was particularly investigated, simultaneously with several configurations of the direction of the ablation plasma, the rf plasma beam and the substrate. The obtained films, with thicknesses in the range of 50 nm to 1 ?m have been characterized by atomic force microscopy (AFM), X-ray diffraction (XRD), transmission electron microscopy (TEM).

Energy Technology Data Exchange (ETDEWEB)

The pitting behavior of Alloy 800 was investigated as a function of temperature and prefilming in high temperature water. The pitting behavior was characterized in terms of the pitting potential and the pit density. The pitting potential decreases with increasing temperature and chloride activity. Prefilming of test coupons over a time period between 100 and 5,000 hours in ammoniated water at 300 C has no apparent influence on the pitting potential at room temperature, 180 C and 300 C. However, the number of pits in prefilmed coupons is much higher than in coupons covered with an air passive layer. The effect of prefilming on pit nucleation was investigated in more detail with regard to a model and test methods developed by Bianchi and co-workers. Density of pits in prefilmed coupons is at least one order of magnitude higher than in air passive coupons. Maximum pit density was measured after a prefilming period of 1 00 hours. The effect is discussed in terms of Bianchi`s model and in ...

Energy Technology Data Exchange (ETDEWEB)

A technique and a particular apparatus for an inductive measurement of critical currents as a function of temperature and magnetic field in thin-film superconductors are described. The technique has been found to be particularly useful for high-field A-15 compounds 2 to 3 ..mu..m thick. Samples with lower critical current densities would have to be correspondingly thicker to measure over the same broad range of temperature and field. The design of the apparatus is detailed showing that the film can be taken directly from the deposition chamber and mounted without electrical contacts so samples can be changed easily. The principles of operation are developed based on the Critical State Model. These principles are tested by measurements which verify that the measured value of critical curent is independent of the amplitudes and frequency of the small ac magnetic field which is added to a much larger quasistatic field. The ...

Science.gov (United States)

This report summarizes the results obtained under a contract from 1974 to 1977, focusing on silicide formation of thin metal films on a Si substrate. The main thrust of the effort was directed at: (1) Development of the data base on thin-film silicide formation, and the investigation of the influence of the Si substrate on the silicide formation. When taken in context with results of other studies, the data obtained exhibit a clear pattern of behavior among the various metal films, but the detailed picture appears to be complex; (2) Development of marker experiments by ion-implanted Ar or Xe markers; (3) Clarification of the role played by oxygen contamination in silicide formation; (4) Stability of silicide layers; (5) Reaction of metal layers with SiO/sub 2/; (6) Electrical characteristics of Pd/sub 2/Si; and (7) A computer program was written to synthesize backscattering spectra for thin-film samples ...

Energy Technology Data Exchange (ETDEWEB)

The refractory nature and high ductility of body centered cubic (bcc) phase tantalum makes it a suitable material for corrosion- and wear-resistant coatings on surfaces which are subjected to high stresses and harsh chemical and erosive environments. Sputter deposition can produce thick tantalum films but is prone to forming the brittle tetragonal beta phase of this material. Efforts aimed at forming thick bcc phase tantalum coatings in both flat plate and cylindrical geometries by high-rate triode sputtering methods are discussed. In addition to substrate temperature, the bcc-to-beta phase ratio in sputtered tantalum coatings is shown to be sensitive to other substrate surface effects.

Energy Technology Data Exchange (ETDEWEB)

The goal of the present work has been to clarify the influence of sulphate ions on the oxide films formed on stainless steel and Ni-based alloys in simulated crack chemistry conditions using different ex situ analytical techniques. The main observations of this work can be summarised as follows: The thickness of the films formed in simulated oxygen-free crack chemistry conditions during an exposure of circa 4 days varies roughly in the range 200..500 nm, which corresponds to observations reported in the literature [2]. The presence of 10000 ppb sulphate ions in simulated crack tip conditions seems to lead to a considerably lower thickness of the oxide films when compared to sulphate-free conditions. The presence of 10000 ppb sulphate ions leads also to considerable changes in the morphology of the oxide crystals on the material samples. In the absence of sulphate the outer oxide ...

Energy Technology Data Exchange (ETDEWEB)

The properties of AlN make this material very attractive for optical, electronic, and tribological application. Also, if the AlN could be formed on the Al surface to enhance its surface properties, Al could be applied for the lightening of machine parts. However, a dense oxide film exists on the surface of Al, which prevents the formation of the Al nitride even during plasma nitriding and plasma coating process. In this study, plasma nitriding has been tried to form an AlN layer on Al after the surface activation processes. During the plasma nitriding, the density of the nitrogen ions was amplified by means of controlling the power of the Al substrates. The film thickness, microstructural features and the mechanical properties such as hardness and wear properties of the AlN layer were examined as a function of the process parameters of pretreatment and plasma nitriding

Energy Technology Data Exchange (ETDEWEB)

The design of a reaction cell which permits the investigation of the sorption kinetics of microcomponents without separation of the phases under automated condition has been described. The use of thin-layer inorganic sorbents obtained by depositing films of a sorbing substance from aqueous solutions on flat substrates of small thickness makes it possible to determine the extent of sorption even at small values in the case of /beta/ emitters with a low energy and /alpha/ emitters. Detailed observation of the kinetics of isotopic exchange in the CdS-/sup 115m/Cd-HNO/sub 3/ system has made it possible to reveal at least four stages in the process during the time of observation.

Energy Technology Data Exchange (ETDEWEB)

Aluminium AA5182 coupons covered by a polyaniline film in the emeraldine base (EB) form showed increasing corrosion potential and decreasing corrosion current as a function of the thickness of the polymer layer. The cathodic reaction was proved not limited by diffusion of species inside the electrolyte solution and oxygen had no effect on the electrochemical behaviour of the coated samples. An EB coating on indium tin oxide conducting layer appeared slightly electroactive in neutral media. The IR spectra of aluminium coated samples, before and after heating in argon atmosphere, confirmed a redox reaction between the polymer film and the metal. This galvanic coupling can explain the good protective behaviour of emeraldine base against corrosion of aluminium.

British Library Electronic Table of Contents (United Kingdom)

The formation of nanoparticles during the radiation-induced chemical reduction of silver ions, copper ions, and nickel ions in films based on poly(acrylic acid)-poly(ethylenimine) complexes are studied via electron microscopy. This approach allows preparation of composites containing nanoparticles that are randomly distributed in the polymer matrix and materials with a regular spatial distribution of nanoparticles across the film thickness and in subsurface layers. The structure of metal-polymer hybrid materials is dependent on the irradiation conditions, the type of reduced metal ions, and their initial content in polymer matrices. The ratio between the rate of nucleation and the rate of growth of nanoparticles in the matrices of interpolyelectrolyte complexes depends on the intensity of ...

Energy Technology Data Exchange (ETDEWEB)

In an aim to develop photo-responsive composites, the UV photo-reduction of aqueous titanium oxide nanoparticle-graphene oxide (TiO{sub 2}-GO) dispersions (Lambert et al. J Phys. Chem. 2010 113 (46), 19812-19823) was undertaken. Photo-reduction led to the formation of a black precipitate as well as a soluble portion, comprised of titanium oxide nanoparticle-reduced graphene oxide (TiO{sub 2}-RGO). When allowed to slowly evaporate, self assembled titanium oxide nanoparticle-graphene oxide (SA-TiO{sub 2}-RGO) films formed at the air-liquid interface of the solution. The thickness of SARGO-TiO{sub 2} films range from {approx}30-100 nm when deposited on substrates, and appear to be comprised of a mosaic assembly of graphene nanosheets and TiO{sub 2}, as observed by scanning electron microscopy. Raman spectroscopy and X-ray photoelectron spectroscopy indicate that the graphene oxide is only partially reduced in the SA-TiO{sub ...

Energy Technology Data Exchange (ETDEWEB)

Various methods for storing hydrogen have been examined in an effort to find ways to store hydrogen in increasingly smaller volumes with decreasing weight of the whole hydrogen storage system. Metal hydrides, in which hydrogen is chemically bound to a metal atom, are considered to be very promising candidates for hydrogen storage because they have high gravimetric and volumetric storage capacities. This study investigated the effect of different magnesium (Mg) and aluminium (Al) ratios on the absorption and desorption properties of thin films. Neutron reflectometry (NR) was used in this study to better understand the absorption and desorption properties of commercially promising hydrogen storage materials. The large negative scattering length of hydrogen atoms changes the reflectivity curve substantially, so that NR can determine the total amount of stored hydrogen as well as the hydrogen distribution along the film normal, with nanometer ...

Energy Technology Data Exchange (ETDEWEB)

Passive films formed anodically on titanium (Ti) plates in 0.5 M sulfuric acid were corroded in aqueous solutions of H{sub 2}SO{sub 4} in the dark and under illumination of a 250-W mercury lamp. The corrosion depth was determined by calculating the thickness of the oxide layers from interference patterns of reflection spectra in the visible region. Corrosion was observed at pH {le} 3, with the corrosion rate increasing exponentially with decreasing pH and achieving a maximum value at pH {approximately} 1. Photocorrosion generally was quicker than corrosion occurring in the dark in all cases (i.e., open-circuit, short-circuit, bias conditions) and increased under anodic polarization of the oxide electrode together with the photocurrent. Corrosion occurring in the dark decreased very weakly under anodic polarization. Long-term corrosion experiments indicated the initial corrosion rate for a thick anodic oxide was higher than ...

Energy Technology Data Exchange (ETDEWEB)

A stable isotope mass-balance of dissolved inorganic carbon during a blue-green algae bloom in a softwater lake demonstrates that at low partial pressure of carbon dioxide there must be a large net negative carbon isotope fractionation between atmospheric CO/sub 2/ and the CO/sub 2/ absorbed by lake water at pH = 9.5. Chemical enhancement of CO/sub 2/ invasion at high pH by the reaction CO/sub 2/ + OH/sup -/ ..-->.. HCO/sub 3//sup -/ at large apparent film thicknesses may result in carbon isotope fractionation approaching that for a hydroxide solution. This phenomenon, coupled with a decrease in the photosynthetic fractionation, forced the surface water of a softwater lake to achieve increasingly negative delta /sup 13/C values during an algal bloom, which is in the opposite sense to the trend that results from photosynthesis under less extreme conditions. This and other similar systems must operate under non-equilibrium (kinetic) ...

Energy Technology Data Exchange (ETDEWEB)

Metallic multilayers offer a fantastic playground to investigate elastic stresses in films of nanometer thickness. We will present and discuss a few examples from our recent work on Au-Ni and Ag-Cu systems where we combined plate bending measurements and electron or X-ray diffraction to investigate stress buildup and interfacial mixing. Comparing these two cases we discuss the results with respect to basic parameters like the misfits in lattice parameters and in elastic moduli, the mixing enthalpies and the surface energies.

Energy Technology Data Exchange (ETDEWEB)

High-spatial-resolution microfocus-based X-ray imaging technology, both real-time and film, has been used to study the thickness variation that occurs in the oxide core of silver-sheathed BSCCO ribbons produced by the powder-in-tube method. This thickness variation (also called ``sausaging``) occurs during incremental rolling and degrades the critical current densities of the ribbons. Using X-ray image data the authors determined the onset and severity of sausaging. Onset occurred at a ribbon thickness of 203 {micro}m, and the severity increased with subsequent rolling reductions. Scanning electron microscopy was used to confirm the X-ray image data. X-ray imaging provides several advantages over more traditional methods for characterizing the superconductors such as optical or scanning electron microscopy. The X-ray imaging provides nondestructive information about the entire width of the ribbon, with ...

Energy Technology Data Exchange (ETDEWEB)

Coded imaging techniques using thick, micro-Fresnel zone plates as coded apertures have been used to image x-ray emission (2--20 keV) and 3.5 MeV Alpha particle emissions from laser driven micro-implosions. Image resolution in these experiments was 3--8 ..mu..m. Extension of this coded imaging capability to higher energy x rays (approx.100 KeV) and more penetrating charged particles (e.g., approx.15 MeV protons) requires the fabrication of very thick (50--200 ..mu..m), high aspect ratio (10:1), gold Fresnel zone plates with narrow linewidths (5--25 ..mu..m) for use as coded apertures. A reactive ion etch technique in oxygen has been used to produce thick zone plate patterns in polymer films. The polymer patterns serve as electroplating molds for the subsequent fabrication of the free-standing gold zone plate structures.

Energy Technology Data Exchange (ETDEWEB)

Oregon State University (OSU) and the Pacific Northwest National Laboratory (PNNL) were funded by the U.S. Department of Energy to conduct research focused on resolving the key technical issues that limited the deployment of efficient and extremely compact microtechnology based heat actuated absorption heat pumps and gas absorbers. Success in demonstrating these technologies will reduce the main barriers to the deployment of a technology that can significantly reduce energy consumption in the building, automotive and industrial sectors while providing a technology that can improve our ability to sequester CO{sub 2}. The proposed research cost $939,477. $539,477 of the proposed amount funded research conducted at OSU while the balance ($400,000) was used at PNNL. The project lasted 42 months and started in April 2001. Recent developments at the Pacific Northwest National Laboratory and Oregon State University suggest that the performance of absorption and desorption systems can be ...

Energy Technology Data Exchange (ETDEWEB)

Lithium (Li) plating-stripping reaction properties at the lithium phosphorus oxynitride glass electrolyte (LiPON)/copper thin film (Cu) interface is improved by the insertion of nano-thickness platinum (Pt) layer at the interface. The LiPON films are formed on mirror-polished lithium-ion conductive solid electrolyte sheets, and current collector thin films of Li, Cu-Pt multi layer, and Cu are formed on the LiPON films. The plating-stripping reactions at the LiPON/current collector films interface are carried out by galvanostatic and potential sweep measurements. Galvanostatic measurements reveal that Pt layer insertion reduces the overvoltage of the reaction and improves its coulomb efficiency. Also, cyclic voltammetry measurement suggests formation of Li-Pt alloys at higher voltages than 0 V (vs. Li/Li{sup +}) during the lithium plating process. Scanning ...

International Nuclear Information System (INIS)

Water repellency en the microstructure super-hydrophobic cured surface is important for research and industrial purposes. This microstructure film can be cured on polyethylene terephthalate PET surface by electron beam (EB) at different irradiation doses 10-100 kGy. The microstructure formulation composed from hydrophobic acrylate oligomer (EB 244) and monomer (SR 440). The irradiation induced cross linking of the prepared microstructure was proved by FTIR spectroscopy and the adhesion force by abrasion test. Some factors affecting the adhesion force of the prepared microstructure film such as oligomer/monomer composition ratio and the thickness of the microstructure cured film were studied. The contact angles (8) were measured on cured surfaces before and after adding the super hydrophobic nanoparticles (Zonyl 9361). The super-hydrophobic cured surface showed the self-cleaning property. The volume of ...

International Nuclear Information System (INIS)

Cyclic voltammograms of SUS 304 stainless steel in various neutral solutions such as Na_2SO_4 at high temperature were measured, as a successive study to previous report in which effects of temperature and pH on polarization behavior of stainless steel were studied. In this measurement Ag/AgCl reference electrode and platinum counter electrode were used in a static autoclave lined with inconel. Passive films formed in various conditions were analysed by electron diffraction and Auger spectroscopy. Results obtained were compared with anodic behavior of iron, chromium and nickel and with thermodynamical stabilities of their compounds. The main results are summarized as follows. (1) Stainless steel shows such electrochemical behavior as active dissolution, passivation and transpassivation in a deaerated neutral solution at 250"0C after fully reductive treatment of the specimen. In air-saturated solution, the peak of active dissolution is not observed. In the passive ...

Energy Technology Data Exchange (ETDEWEB)

Al{sub x}Ga{sub 1{minus}x}P layers (0 {le} x {le} 0.7), with thicknesses of {ge}1 {micro}m were grown on Si (100) wafers by metal-organic molecular beam epitaxy (MOMBE) at 450 C. Transmission electron micrographs of the single crystal films revealed that the microstructure contains stacking faults and microtwins especially near the interface as well as both threading and misfit dislocations. Hardness and elastic modulus were measured using a Nanotest 500 indenter, which can probe the film properties without influence from the substrate. The hardness H varies linearly according to (11.8 {minus} 2.3x) GPa. The absence of alloy hardening is due to the fact that there is no difference in atomic size of Al and Ga. The indentation modulus E/(1{minus}v{sup 2}) decreases monotonically from 136 GPa for GaP to 129 GPa for Al{sub 0.7}Ga{sub 0.3}P and bows only slightly (about 2%) below the straight line of linear interpolation.

Energy Technology Data Exchange (ETDEWEB)

This paper reports on superconductor-semiconductor-superconductor (S-N-S) weak-link junctions with the normal layer of Si or InSb thin films were prepared by using focused ion beam (FIB), and electrical properties were measured. Whereas InSb thin films on single crystals did not have an intrinsic mobility, S-N-S junction with InSb shows the characteristics of Josephson S-N-S junction. A 200nm-thick film of InSb deposited on MgO had a mobility of 83 cm{sup 2}.V {center dot} s and a carrier density of 6.5 {times} 10{sup 17} cm{sup {minus}3} at 4.2K. The coherence length {xi}{sub n} was computed to be 17 nm from these experimental data, and we obtained critical superconducting current Ic of 100 {mu} A for the S-N-S junction which had a line width of 10{mu} m and a channel length of 20 nm.

International Nuclear Information System (INIS)

Modelization of crack propagation and theoretical prediction of rupture are the two main objectives of researchers in stress corrosion cracking. Nevertheless, to reach this aim, the behavior of the passive film which appears spontaneously on the substrate in contact with an environment has to be known. This structural and mechanical characterization is all the more difficult because the number of parameters is important: crystallinity rate, defects concentration, thickness (about a few nanometers), electric field, chemical composition (a lot of oxides are present), peeling layers (atomic structure for example) and some hypothesis can be made about their multi-layer structure, their chemical composition or their epitaxial character... Passive films formed on 316L or 304L stainless steels in different aqueous solutions (in ambient air, in MgCl_2 at 117 deg. C...) have been studied and some important remarks about their ...

Science.gov (United States)

The study of the intrinsic behavior of high transition temperature copper-oxide superconductors (HTSC) has proven to be challenging because of the extreme sensitivity of their transport properties on material quality. These compounds are characterized by a high degree of structural and electrical anisotropy, and a very short superconductive coherence length of the same order as the size of the crystalline unit cell (~5-30 A). As a result, microscopic defects such as oxygen vacancies, cationic disorder, and the presence of minute impurities have a significant effect on electrical transport in these materials. Therefore, much effort has been expended in synthesizing sizable samples that are homogeneous, well characterized, and emenable to the study of the anisotropic properties of the HTSC. We have demonstrated that thin films of HTSC compounds such as rm YBa_2Cu_3O_{7 -delta}, which is a 92 K superconductor, can be synthesized easily by a technique known as pulsed ...

Energy Technology Data Exchange (ETDEWEB)

Microfabrication processes for Y-Ba-Cu-O films have been investigated, using ion-beam techniques. High-{Tc} superconducting lines as narrow as 0.8 {mu}m have been fabricated from epitaxial YBa{sub 2}Cu{sub 3}O{sub 7 {minus} {ital y}} films by Ar ion-beam etching (IBE), combined with focused ion-beam (FIB) lithography. The resulting lines, 1.3 {mu}m wide and 2 mm long, showed a zero resistance temperature of 81 K and a critical current density of 1.9 {times} 10{sup 4} A/cm{sup 2} at 77.3 K. Maskless etching was carried out using 130-keV au{sup +} focused ion-beam (FIB) with a 0.1-{mu}m-diameter beam. A 50-nm-thick film was patterned into 0.3-{mu}m-wide lines at a dose of 5 {times} {sup 16} ions/cm{sup 2}. In comparison with Ar IBE, Cl{sub 2} reactive ion-beam etching (RIBE) exhibited an enhancement effect in sputtering yield. Ion implantation with 300-keV Si{sup + +} FIB also indicated the possibility to ...

International Nuclear Information System (INIS)

Uniform and transparent thin films of Zn_1_-_xCo_xO (0 #=# 0.035, CoO (cubic) was detected as the secondary phase. Influence of Co addition on the volume fraction of grain boundaries has been interpreted. Increase in Co content in the range 0 #<=# x #<=# 0.10 led to quenching of near-band edge and blue emissions, decrease in band gap energy (E_g) from 3.36 eV to 3.26 eV, decrease in film thickness and refractive index and an increase in extinction coefficient of Zn_1_-_xCo_xO thin films. The change in nature of stress from compressive to tensile with lower to higher doping of Co is corroborative with the angular peak shift of (002) plane of ZnO lattice. An overall increase in microhardness of Zn_1_-_xCo_xO thin films up to x = 0.05 is attributed to change in microstructure and evolution of secondary phase and as the secondary phase separates out the overall stress is released ...

International Nuclear Information System (INIS)

A wide variety of thin film coatings, deposited by different techniques and with potential applications in various important areas, have been characterised by the Phase Modulated Spectroscopic Ellipsometer, installed recently in the Spectroscopy Division, B.A.R.C. The Phase Modulated technique provides a faster and more accurate data acquisition process than the conventional ellipsometry. The measured Ellipsometry spectra are fitted with theoretical spectra generated assuming an appropriate model regarding the sample. The fittings have been done objectively by minimising the squared difference (#chi#"2) between the measured and calculated values of the ellipsometric parameters and thus accurate information have been derived regarding the thickness and optical constants (viz, the refractive index and extinction coefficient) of the different layers, the surface roughness and the inhomogeneities present in the layers. Measurements have been done ...

International Nuclear Information System (INIS)

In situ spectroscopic ellipsometry was employed to investigate the initial regime of rare earth metal (REM) conversion coatings formation on AZ31 magnesium alloy. Three REM salts solutions, 0.05 mol.dm"-"3 Ce(NO_3)_3, La(NO)_3 and Sm(NO)_3 solutions, were used for REM conversion coatings preparation. By deconvoluting the ellipsometric data, the surface of the fresh well-polished AZ31 magnesium alloy was found to be covered with 15.80 nm thick native (hydr)oxide film; the refractive indices and the thickness of Ce, La and Sm conversion coatings were obtained. The formation kinetics of three REM coatings follows different exponential functions and the coatings exhibit different optical properties. La conversion coating has the largest n values and the lowest k values while Sm conversion coating is just opposite. Moreover, the pH variation of the bulk conversion solutions upon the coatings formation was recorded. It is ...

Energy Technology Data Exchange (ETDEWEB)

Boron is implanted in crystalline silicon through oxide layers with different thicknesses. The implantation is carried out at various doses and energies of interest in ultra large scale integration (ULSI) application. Rapid thermal annealings (RTA) are used to obtain shallow junctions and electrical activation of the B atoms. However, transient enhanced diffusion induced by implantation damage can be observed. The boron concentration profiles before and after annealing are obtained with secondary ion mass spectrometry (SIMS). It is found that the diffusion transient in the tail region of the boron profile increases with decreasing oxide thickness. Even more, if the implantation damage concerns mostly the oxide, i.e. when the concentration peak is located in this oxide, the oxygen knocked into the silicon substrate could play this way an important role in restricting the boron diffusion, which is good to obtain very shallow junctions. On the ...

Energy Technology Data Exchange (ETDEWEB)

We describe a new method for the scabbling of concrete surfaces using a thin layer of explosive material sprayed onto the surfaces. We also developed a new explosive mixture that could be applied with commercial spray painting equipment. The first part of our record describes experiments that studied methods for the initiation of the sprayed explosive. We successfully initiated layers 0.36 mm thick using a commercial EBW detonator, a flying plate detonator, and by pellet impact. The second part of our report describes a survey of spray methods and tests with two commercial spray systems that we believe could be used for developing a robotic spray system.

Energy Technology Data Exchange (ETDEWEB)

Evaporated palladium films of 45 nm thickness on Si(111) were irradiated using 78 keV Ar/sup +/ ions with doses in the range of 1 x 10/sup 15/ to 1.5 x 10/sup 16/ cm/sup -2/ for the purpose of studying silicide formation. Rutherford backscattering analysis shows that intermixing has occurred across the Pd-Si interface at room temperature. The mixing behaviour increases with increasing dose of the bombarding ions, which agrees well with a theoretical model of isotropic cascade mixing for palladium, and radiation-enhanced diffusion associated with an interstitial mechanism for silicon.

International Nuclear Information System (INIS)

Aluminium nitride (AlN) is a very interesting ceramic because of its combination of properties such as high thermal stability, high hardness and an unusual combination of high thermal and low electrical conductivity. But it is very difficulty to obtain an AlN layer on the aluminium substrates by thermochemical nitriding process. Since a thin film of aluminium oxide existing on the surface of every aluminium substrate prevents the nitrogen atoms from diffusing into the aluminium lattice. However, it is possible to sputter the oxide film away from the aluminium surface in a glow discharge with the use of plasma nitriding technique and to allow the formation of AlN layer on the aluminium bulk. In the present work specimen of aluminium Al 99.5 has been plasma nitrided in a modified plasma nitriding unit, in which a diffusion pump was used to obtain an especially low partial pressure of oxygen in the vauum chamber. The sputter-cleaning prior to the ...

Energy Technology Data Exchange (ETDEWEB)

Magnetic imaging in the transmission electron microscope (TEM) has been used to examine submicron elements with the aim of discovering down to what element size complex domain patterns can form. The elements were squares, circles, triangles, and pentagons in the size range 100{endash}500 nm and were made from 36 nm Co films or 8 nm Ni{sub 80}Fe{sub 20} (NiFe) with in-plane magnetization. The magnetic domain structures in these elements were imaged at high resolution using the differential phase contrast imaging mode in a TEM. Nonuniform magnetization structures were seen in the images. Vortices were present at remanence in all shapes of 36-nm-thick Co elements down to 100 nm size and in circular NiFe elements down to 116 nm diameter. Triangular NiFe elements did not have a vortex state at remanence, instead the magnetization curved round within the element but did not achieve complete flux closure. In simulations of square and circular NiFe ...

International Nuclear Information System (INIS)

New experiment of radiography in using Fuji Intelligent Diagnostic X-ray System was first reported in XV International Congress of Radiology, 1981. By utilizing this system instead of traditional screen/film system, high density imaging plate in conjunction with computed image processor was developed, this is FCR. However, as the numerous problems in regard to the basic side of FCR system are found, it is expected that these are solved by investigators at their earliest opportunities. The purpose of this study is to reduce the radiation doses of the patients at radiography of the chest by using FCR system installed in our Department of Radiology in July, 1984. Experimentally we measured the radiation doses of the patient having the each breast of 18, 20, 22 and 24cm in thickness at radiography of the chest by using VICTOREEN MODEL 666 survey meter. The results obtained were as follows: 1) By using FCR system the radiation doses of the chest ...

CERN Document Server

The combination of large thickness ($>3$ $\\mu$m), large--area uniformity (75 mm diameter), high growth rate (up to 0.4 $\\mu$m/min) in assemblies of complex--shaped nanowires on lithographically defined patterns has been achieved for the first time. The nanoscale and the microscale have thus been blended together in sculptured thin films with transverse architectures. SiO$_x$ ($x\\approx 2$) nanowires were grown by electron--beam evaporation onto silicon substrates both with and without photoresist lines (1--D arrays) and checkerboard (2--D arrays) patterns. Atomic self--shadowing due to oblique--angle deposition enables the nanowires to grow continuously, to change direction abruptly, and to maintain constant cross--sectional diameter. The selective growth of nanowire assemblies on the top surfaces of both 1--D and 2--D arrays can be understood and predicted using simple geometrical shadowing equations.

International Nuclear Information System (INIS)

Complete text of publication follows. According to the new European regulations (Restrictions of Hazardous Substance Directive), there is an emerging demand for environmental friendly metal treatments instead on formerly used chromate conversion coating technique. The aim of the present investigations was to characterise and compare silicon containing protective thin layers on roughened galvanized steel surfaces (with average roughness of 0.7 microns), using FTIR microscopy and imaging techniques. The silicon containing coatings were produced either by Chemical Vapour Deposition (CVD) or by wet chemical treatment using liquid silane. FTIR techniques offer new possibilities in the characterisations and chemical mapping of differently coated thin films, besides SEM+EDS, AFM, nanoindentation, XPS measurements (P. Nemeth et al., Materials Science Forum, 589 (2008) 433-438). All measurements were carried out by a Varian FTS-7000 spectrometer with a 'Stingray' microscope ...

International Nuclear Information System (INIS)

Complimentary spectroscopic, microscopic and electrochemical studies were performed to characterise the barrier properties as well as the interface structure of model iron substrates covered with thin plasma polymer films. Cathodic plasma polymers were deposited which show high barrier properties. The metal surface was pre-treated by a reducing or oxidising plasma. This allowed the adjustment of the oxidation state of the interface layer. The interface structure was characterised by means of X-ray photoelectron sputter profiles, infrared spectroscopy and the application of a Kelvin probe. The investigations show that the measured Voltapotential on the plasma polymer surface can be correlated with the oxidation state of the interface. Reducing plasmas lead to an almost oxide free surface. After deposition of the plasma polymer, this reduced state of the oxide is sensitive to re-oxidation of the interface by oxygen that diffuses through the plasma polymer. It could ...

Energy Technology Data Exchange (ETDEWEB)

The high cost of proton exchange membrane fuel cells (PEMFCs) poses a significant challenges to their commercial uptake. The bipolar plates connect the anode and cathodes of cells and separate the reactant gases, and are the most expensive components in PEMFCs. Although stainless steel can be used as a low-cost alternative in bipolar plate construction, steel is prone to electrochemical corrosion in the highly acidic PEMFC operation process. This study examined the polarization curves and ICR as a function of compaction force of a high Cr and Ni austenitic stainless steel in an environment simulating the bipolar plate under PEMFC operating conditions. The 3-electrode system consisted of a platinum (Pt) sheet, a saturated calomel electrode with a Luggin capillary contract with the used solution and the work electrode. All polarization curves were measured in a solution of H{sub 2}SO{sub 4} in order to simulate the aggressive PEMFC environment. Surface morphologies of the steels were ...

Energy Technology Data Exchange (ETDEWEB)

Better understanding and modelling of three-phase flow through porous media is of great interest, especially for improved oil recovery methods such as gas injection processes. Early theoretical and experimental studies have already demonstrated that the wettability characteristics of the solid surface and the spreading characteristics of the fluid system hold the key roles. This observation is confirmed by our theoretical results using DLP theory on the stability and the thickness of static oil films. In most of the works related to three-phase flow processes, homogeneous wettability is assumed. There exist only a few studies demonstrating the tremendous impact of the wettability heterogeneities on gas injection. The objective of the present work is twofold: to demonstrate the effect of small scale wettability heterogeneities on gas injection efficiency, and to develop a tool to predict this impact for various patterns and spatial ...

International Nuclear Information System (INIS)

Vacuum glazing consists of an evacuated space between two sheets of glass. Vacuum glazing has a large effect on energy savings in houses and buildings. Vacuum glazing can achieve higher insulating performance than conventional insulated glazing. Nippon Sheet Glass has successfully developed conventional vacuum glazing. In this study we investigated an advanced form of vacuum glazing. Its thermal insulation ability is equivalent to 100 mm thick glass wool thermal insulation. This vacuum glazing contained a SnO_2:F low emissivity surface. The influence of the residual gas in a vacuum space on heat flow is important to performance. For long-term thermal stability, it is very important to maintain vacuum stability. To understand this better, we studied the behavior of outgassing from the inside glass surfaces exposed to an external energy source. We have studied the behavior of outgassing from a glass surface using a Nd:YAG laser (operated at 355 nm wavelength) and ...

Energy Technology Data Exchange (ETDEWEB)

A high power (200KV), intense current density, low emittance (71mmmrad), high brightness (8x10{sup 10}A/m rad) electron beam was generated in the 10cm long, high-voltage-resistive multi-gap hollow cathode pseudospark chamber filled with 15pa nitrogen and driven by an improved pulse line accelerator. The beam was ejected with the 1mm diameter, the 2.2KA beam current, and the 400ns pulse length, and could propagated 20cm in the drift tube. At a distance of 5cm from the anode it penetrated consecutively an acid-sensitive discoloring film and a 0.05mm-thick copper foil both stuck closely, left 0.6mm and 0.3mm holes on them, respectively. That 10 shots on an acid-sensitive film produced a hole of 1.6mm at 7cm downstream of anode showed its good repeatability. After 60 shots the pseudospark discharge chamber was disassembled and observed that almost no destructive damage traces left on the surfaces of its various electrodes and ...

International Nuclear Information System (INIS)

Effects of PbO on the repassivation kinetics of alloy 690TT were examined using the rapid scratching electrode technique under a potentiostatic condition to elucidate the influence of PbO on SCC resistance of the alloy. The repassivation kinetics of the alloy was analyzed in terms of the current density flowing from the scratch, i(t), as a function of the charge density that has flowed from the scratch, q(t). Repassivation on the scratched surface of the alloy occurred in two kinetically different processes; passive film initially nucleated and grew according to the place exchange model in which log i(t) is linearly proportional to q(t) with a slope of 1/K, and then grew according to the high field ion conduction model in which log i(t) is linearly proportional to 1/q(t) with a slope of cBV. 1/K and cBV are parameters representing the SCC susceptibility as well as repassivation rate of the alloy at an initial and an intermediated stages of repassivation ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

An x-ray zone plate was fabricated using the novel approach of focused ion beam (FIB) milling. The FIB technique was developed in recent years, it has been successfully used for transmission electron microscopy (TEM) sample preparation, lithographic mask repair, and failure analysis of semiconductor devices. During FIB milling, material is removed by the physical sputtering action of ion bombardment. The sputter yield is high enough to remove a substantial amount of material, therefore FIB can perform a direct patterning with submicron accuracy. The authors succeeded in fabricating an x-ray phase zone plate using the Micrion 9500HT FIB station, which has a 50 kV Ga{sup +} column. Circular Fresnel zones were milled in a 1.0-{micro}m-thick TaSiN film deposited on a silicon wafer. The outermost zone width of the zone plate is 170 nm at a radius of 60 {micro}m. An achieved aspect ratio was 6:1.

Energy Technology Data Exchange (ETDEWEB)

The use of n-alkanethiolate self-assembled monolayers on gold has blossomed in the past few years. These systems have functioned as models for common interfaces. Thiolate monolayers are ideal because they are easily modified before or after deposition. The works contained within this dissertation include interfacial characterization (inbred reflection absorption spectroscopy, ellipsometry, contact angle, scanning probe microscopy, and heterogeneous electron-transfer kinetics) and various modeling scenarios. The results of these characterizations present ground-breaking insights into the structure, function, and reproducible preparation of these monolayers. Surprisingly, three interfacial properties (electron-transfer, contact angle, and ellipsometry) were discovered to depend directly on the odd-even character of the monolayer components. Molecular modeling was utilized to investigate adlayer orientation, and suggests that these effects are adlayer structure specific. Finally, the ...

Science.gov (United States)

We present computer modeling along with experimental data on the formation of sharp conical tips on silicon-based three-layer structures that consist of a single-crystal Si layer on a 1 {mu}m layer of silica on a bulk Si substrate. The upper Si layers with thicknesses in the range of 0.8-4.1 {mu}m were irradiated by single pulses from a KrF excimer laser focused onto a spot several micrometers in diameter. The computer simulation includes two-dimensional time-dependent heat transfer and phase transformations in Si films that result from the laser irradiation (the Stefan problem). After the laser pulse, the molten material self-cools and resolidifies, forming a sharp conical structure, the height of which can exceed 1 {mu}m depending on the irradiation conditions. We also performed computer simulations for experiments involving single-pulse irradiation of bulk silicon, reported by other groups. We discuss conditions under which different types ...

International Nuclear Information System (INIS)

Topographic and optical patterns have been fabricated in a-SiC films with a focused high-energy (1 MeV) H"+ and He"+ ion beam and examined with near-field techniques. The patterns have been characterized with atomic force microscopy and scanning near-field optical microscopy to reveal local topography and optical absorption changes as a result of the focused high-energy ion beam induced modification. Apart of a considerable thickness change (thinning tendency), which has been observed in the ion-irradiated areas, the near-field measurements confirm increases of optical absorption in these areas. Although the size of the fabricated optical patterns is in the micron-scale, the present development of the technique allows in principle writing optical patterns up to the nanoscale (several tens of nanometers). The observed values of the optical contrast modulation are sufficient to justify the efficiency of the method for optical data recording using ...

Energy Technology Data Exchange (ETDEWEB)

Heusler alloys are considered as interesting ferromagnetic electrode materials for magnetic tunnel junctions, because of their high spin polarization. We, therefore, investigated the micromagnetic properties in a prototypical thin film system comprising two different Heusler phases Co{sub 2}MnSi (CMS) and Co{sub 2}FeSi (CFS) separated by a MgO barrier. The magnetic microstructure was investigated by X-ray photoemission electron microscopy (XPEEM). We find a strong influence of the Heusler phase formation process on the magnetic domain patterns. SiO{sub 2}/V/CMS/MgO/CFS and SiO{sub 2}/V/CFS/MgO/CMS trilayer structures exhibit a strikingly different magnetic behavior, which is due to pinhole coupling through the MgO barrier and a strong thickness dependence of the magnetic ordering in Co{sub 2}MnSi.

Energy Technology Data Exchange (ETDEWEB)

Under severe operating conditions, such as starved lubrication, performance, service life, and reliability of rolling element bearings depend on the chemical and physical interactions between the contacting surfaces, the lubricant components, and the atmosphere. The IMKT{sup 1}, PI{sup 2}, and the imt{sup 3} have been cooperating on systematic investigations of interfacial interactions in high speed grease lubricated ball bearings. These include long time tests with complete bearings lubricated with greases of different composition under defined operating conditions, conducted at the IMKT, and chemical and physical characterizations of the running surfaces at the PI and imt. At the PI, in particular the chemical nature of the boundary layers has been investigated with time of flight secondary ion mass spectrometry (TOF-SIMS). The imt has been involved in the investigations by measuring the physical/mechanical properties of interacting surfaces at the micro/nano-scale after the removal ...

International Nuclear Information System (INIS)

High aspect ratio sub-#mu#m periodic structures fabricated by focused ion beam (FIB) lithography have been characterised by Rutherford backscattering spectrometry (RBS) using the macrochannelling technique. The technique overcomes the limitations of complementary techniques such as scanning electron microscopy (SEM) and atomic force microscopy (AFM), which can provide images with sub-#mu#m resolution of just the surface features and not of the deep sub-surface structures, without destructive cross sectioning of the sample. Here RBS macrochannelling with a 2 MeV He"+ ion beam is used to analyse a diffraction grating fabricated by FIB milling an array of 100 nm wide trenches in a 300 nm thick Ag film on a Si substrate. Using the surface structure imaged by SEM and AFM as a starting point, a numerical model for the RBS spectrum from the grating is fitted to the experimental spectrum as a function of the sub-surface structure. This process allows ...

International Nuclear Information System (INIS)

Perforated thermoplastic masks are used to provide patients immobilization. This procedure inserts a material in the path of the radiation beam, that attenuates and modifies the beam fluence and flatness. The present study evaluates the increase in skin dose as a result of using thermoplastic masks. Relative doses were measured on the surface of a solid water phantom, in the presence and absence of masks. These masks were stretched according to deformation patterns observed in clinical routine. The measurements were obtained with a plane-parallel chamber (Markus type 23343) and radiochromic film (EBT Gafchromic) for 6MV X-rays from a linear accelerator, and for a radiation beam from a cobalt therapy unit. The results showed that thermoplastic masks, whose thickness varied between 2 and 3 mm, increased the dose on the surface by a factor of 3. Due to the variations in the skin dose distribution, clinical procedures were suggested to minimize ...

Energy Technology Data Exchange (ETDEWEB)

In this work, the silicon oxynitride layer was studied as a tunneling layer for non-volatile memory application by fabricating low temperature polysilicon thin film transistors on glass. Silicon wafers were oxynitrided by only nitrous oxide plasma under different radio frequency powers and plasma treatment times. Plasma oxynitridation was performed in RF plasma using inductively coupled plasma chemical vapor deposition. The X-ray energy dispersive spectroscopy was employed to analyze the atomic concentration ratio of nitrogen/oxygen in oxynitride layer. The oxynitrided layer formed under radio frequency power of 150 W and substrate temperature of 623 K was found to contain the atomic concentration ratio of nitrogen/oxygen as high as 1.57. The advantage of high nitrogen concentration in silicon oxide layer formed by using nitrous oxide plasma was investigated by capacitance-voltage measurement. The analysis of capacitance-voltage characteristics demonstrated that ...

Science.gov (United States)

Data are presented on the insulating properties and capacitance-voltage (CV) characteristics of metal-oxide-semiconductor (MOS) device-thickness (below approx. 100 nm) native oxides formed by wet thermal oxidation of thin InAlP epilayers lattice matched to GaAs. Low leakage current densities of J=1.4 x 10-9 A/cm2 and J=8.7 x 10-11 A/cm2 are observed at an applied field of 1 MV/cm for MOS capacitors fabricated with 17 nm and 48 nm oxides, respectively. TEM images show that the In-rich interfacial particles which exist in 110 nm oxides are absent in 17 nm oxide films. Quasi-static capacitance-voltage measurements of MOS capacitors fabricated on both n-type and p-type GaAs show that the InAlP oxide-GaAs interface is sufficiently free of traps to support inversion, indicating an unpinned Fermi level. These data suggest that InAlP native oxides may be a viable insulator for GaAs MOS device applications.

International Nuclear Information System (INIS)

Research was conducted at Pacific Northwest Laboratory to develop high photosensitivity adaptive optical elements utilizing ion implanted lanthanum-doped lead-zirconate-titanate (PLZT). One centimeter square samples were prepared by implanting ferroelectric and anti-ferroelectric PLZT with a variety of species or combinations of species. These included Ne, O, Ni, Ne/Cr, Ne/Al, Ne/Ni, Ne/O, and Ni/O, at a variety of energies and fluences. An indium-tin oxide (ITO) electrode coating was designed to give a balance of high conductivity and optical transmission at near uv to near ir wavelengths. Samples were characterized for photosensitivity; implanted layer thickness, index of refraction, and density; electrode (ITO) conductivity; and in some cases, residual stress curvature. Thin film anti-ferroelectric PLZT was deposited in a preliminary experiment. The structure was amorphous with x-ray diffraction showing the beginnings of a structure at ...

Science.gov (United States)

Stresses commonly present in AlGaAs/GaAs laser heterostructures were reduced using Molecular Beam Epitaxy grown Al/sub 0.3/Ga/sub 0.7/P/sub 0.01/As/sub 0.99/ cladding layers. The Al/sub 0.3/Ga/sub 0.7/P/sub 0.01/As/sub 0.99/ alloy was grown using an incident P/sub 2/ flux of roughly-equal1 x 10/sup 14//cm/sup 2/ indicating a sticking coefficient of 0.1 at a substrate temperature of 600 /sup 0/C. X-ray automatic Bragg angle control curvature measurements were used to monitor the residual heteroepitaxial stress. Broadened double crystal x-ray linewidths indicated the occurrence of alloy grading and broadened interfaces. The effects of P concentration and film thickness on stress and on the existence of a misfit dislocation grid are discussed.

Energy Technology Data Exchange (ETDEWEB)

The main objective of the present thesis was develop and get operational a real-time neutron radiography system, at the IPEN-CNEN/SP. This system is installed inside the shielding of an old facility, designed in 1988, for film radiography, which is installed at the beam-hole 08 of the 5 MW, IEA-R1 Nuclear Research Reactor. The most important modifications at the such facility were the increase of the {gamma}-radiation filter thickness, increase of the inner area of the shielding, design of a neutron collimator and a light tight box. The main characteristics of the neutron beam at the irradiation position are: flux: 1 x 10{sup 6}n/cm{sup 2}s, collimation ratio 70, effective energy 7 meV, diameter 20 cm, neutron/{gamma} ratio {approx} 10{sup 6}n/cm{sup 2}mrem. The real-time images have been obtained by means of an imaging system that consists of a screen scintillator, a light intensifier, a video camera, a digitizing frame grabber and a computer. ...

International Nuclear Information System (INIS)

With the deposition of PVD hard coatings on the tools applied in machining operations it is possible to achieve significant improvements in the performance and quality of the machining processes. Depending on the machined material and the operating principle, e.g. turning, milling or drilling, not only different machining parameters but also different coating materials are necessary. In interrupted cut machining of tempered steel, for example, the life time of Ti-C-N coated inserts is several times greater than the Ti-C-N coated ones. This is a result of the favourable thermophysical and tribological properties of Ti-N-C. The potential for tool protection by CrN coatings is a result of the high ductility and low internal stress of this coating materials. CrN films can be deposited with greater film thickness, still maintaining very good adhesion. This paper presents the development of new arc PVD coatings in the system ...

Energy Technology Data Exchange (ETDEWEB)

Among the most promising technological alternatives for the development of photovoltaic modules and cells of a low cost, good energetic conversion and feasibility for mass production, polycrystalline silicon thin film solar cells deposited directly on a transparent substrate are currently being considered the best. We have developed in our laboratory a PECVD reactor capable of producing the deposition of amorphous hydrogenated silicon at rates of above 2 nm/seg, allowing a significant production per line on the plant. Discharge gas is silane, to which diborane or phosphine is added so as to form the cell. Basically, work is done on a structure of cell type TCO/n+/p-/p+/M, which has 2 {mu}m of total thickness. Schott AF-37 glass is used as a substrate, for their ability to withstand temperatures of up to 800 C. The amorphous cell is subsequently annealed at gradual temperatures of 100 C to achieve dehydrogenation up to 650-700 C for 12 h until ...

Energy Technology Data Exchange (ETDEWEB)

Laser-assisted processing techniques for producing high-quality solar cell metallization patterns have been investigated, developed, and characterized. During the early stages, preliminary investigations were carried out on a variety of promising laser-assisted metallization schemes, and the best of these was selected for further development. A comprehensive literature search initially yielded information on state-of-the-art laser-assisted techniques for metal deposition such as laser chemical vapor deposition and laser photolysis of organometallics, as well as laser-enhanced electroplating. Initial experiments on laser-enhanced electroplating yielded very promising results with linewidths as narrow as 25 ..mu..m and local plating speeds as high as 12 ..mu..m/s being achieved. Metal deposition experiments were carried out utilizing laser-assisted pyrolysis of a variety of metal-bearing polymer films and metallo-organic inks spun onto silicon substrates. Argon-ion ...

Energy Technology Data Exchange (ETDEWEB)

A simple method of estimating the amount of lung irradiated in patients with breast cancer would be of use in minimizing lung complications. To determine whether simple measurements taken at the time of simulation can be used to predict the lung volume in the radiation field, we performed CT scans as part of treatment planning in 40 cases undergoing radiotherapy for breast cancer. Parameters measured from simulator films included: (a) the perpendicular distance from the posterior tangential field edge to the posterior part of the anterior chest wall at the center of the field (CLD); (b) the maximum perpendicular distance from the posterior tangential field edge to the posterior part of the anterior chest wall (MLD); and (c) the length of lung (L) as measured at the posterior tangential field edge on the simulator film. CT scans of the chest were performed with the patient in the treatment position with 1 cm slice intervals, covering lung apex ...

International Nuclear Information System (INIS)

Radioactive "3"1Si was used as a marker to study metal silicide formation. Activity profiles in the silicides were measured by a combination of ion beam sputtering, radioactivity counting and Rutherford backscattering of charged nuclear particles. It was found that the metal is the diffusing species during Co_2Si, Pt_2Si, NiSi and PtSi formation, while silicon diffuses during CrSi_2, TiSi_2 and ZrSi_2 formation. Silicon was also found to be the diffusing species during second phase formation of CoSi from Co_2Si. However, in this case it was established that the silicon diffuses by a grain boundary and/or interstitial mechanism. Both the metal and silicon diffuse during Ni_2Si and Pd_2Si formation. In an attempt to interpret complex radioactivity profiles a computer program, simulating various diffusion mechanisms during both first and second phase silicide formation, was written. A numerical approach was used whereby silicide growth occurs in small increments and the concentration of ...

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Science.gov (United States)

No abstract prepared.

Science.gov (United States)

... Abstract : MANY THIN FILM ACOUSTO-OPTIC INTERACTION EXPERIMENTS FOR ... CONVERTERS, AND FOR FAST SWITCHES HAVE BEEN ...

Energy Technology Data Exchange (ETDEWEB)

Polyacrylonitrile films have been spin cast and pyrolyzed to produce thin (500--1500 A) carbon films. These films have higher electrical conductivities than films produced by other methods at similar temperatures. The conductivity can be varied by at least four orders of magnitude by changing the pyrolysis temperature. Ultraviolet, infrared, and Raman spectroscopies were used to investigate the chemical structure of the films during different stages of processing.

International Nuclear Information System (INIS)

The initial thichnesses of feeder pipes in Wolsung-1 are analyzed to estimate status of feeder thinning. The assumption of the estimation is that feeders of same type are decreased to same thickness by bending and have same thickness after bending. Following three methods are used to estimated thicknesses of the remains besides 52 feeders with initial thickness data in Wolsung-1. First is the estimating initial thickness of same type in Wolsung-1 from initial thickness data of Wolsung-2, -3 and -4. Second is the finding average value of each type from 52 initial thickness data of Wolsung-1. Last is the finding the thickness-after-bending of Wolsung-1 from thickness decrease rate of each type by bending in Wolsung-2, -3 and -4. The first method is eliminated by ...

Energy Technology Data Exchange (ETDEWEB)

In order to practice a design-by-analysis of thermohydraulics design of BWR fuel rod bundles, the subchannel analysis would play a major role. There, the immediate concern is improvement in its predictive capability of CHF due in particular to the film dryout (boiling transition phenomena: BT) on the fuel rod surface. Constitutive equations in the subchannel analysis formulation are responsible for the quality of calculated results. The constitutive equations are a result of integration of the local and instantaneous description of two-phase flows over the subchannel control volume. In general, they are expressed in terms of subchannel-control-volume- as well as area-averaged two-phase flow state variables. In principle the information on local and instantaneous physical phenomena taking place inside subchannels must be counted for in the algebraic form of the equations on the basis of a more mechanistic modeling approach. They should include also influences of the ...

International Nuclear Information System (INIS)

In order to practice a design-by-analysis of thermohydraulics design of BWR fuel rod bundles, the subchannel analysis would play a major role. There, the immediate concern is improvement in its predictive capability of CHF due in particular to the film dryout (boiling transition phenomena: BT) on the fuel rod surface. Constitutive equations in the subchannel analysis formulation are responsible for the quality of calculated results. The constitutive equations are a result of integration of the local and instantaneous description of two-phase flows over the subchannel control volume. In general, they are expressed in terms of subchannel-control-volume- as well as area-averaged two-phase flow state variables. In principle the information on local and instantaneous physical phenomena taking place inside subchannels must be counted for in the algebraic form of the equations on the basis of a more mechanistic modeling approach. They should include also influences of the ...

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

International Nuclear Information System (INIS)

A super-hydrophobic coating was prepared by combining a rigid base film with crater-like hemispherical holes and acicular nanoparticles. The acicular boehmite powder provides a high contact angle on the film surface. The rigid base film with crater-like hemispherical holes inhibits the rapid decrease of contact angle by surface rubbing. The combination of different roughness is an effective method for improving the abrasion resistance of super-hydrophobic films.

Energy Technology Data Exchange (ETDEWEB)

Strong perpendicular anisotropy systems consisting of Co/Pt multilayer stacks that are antiferromagnetically coupled via thin Ru or NiO layers have been used as model systems to study the competition between local interlayer exchange and long-range dipolar interactions [1,2]. Magnetic Force Microscopy (MFM) studies of such systems reveal complex magnetic configurations with a mix of antiferromagnetic (AF) and ferromagnetic (FM) phases. However, MFM allows detecting surface stray fields only and can interact strongly with the magnetic structure of the sample, thus altering the original domain configuration of interest [3,4]. In the current study they combine magnetometry and state-of-the-art soft X-ray transmission microscopy (MXTM) to investigate the external field driven FM phase evolution originating from the domain boundaries in such antiferromagnetically coupled perpendicular anisotropy films. MXTM allows directly imaging the perpendicular component of the ...

International Nuclear Information System (INIS)

As part of a study into the properties of ferroelectric single crystals at nanoscale dimensions, the effects that focused ion beam (FIB) processing can have, in terms of structural damage and ion implantation, on perovskite oxide materials has been examined, and a post-processing procedure developed to remove such effects. Single crystal material of the perovskite ferroelectric barium titanate (BaTiO_3) has been patterned into thin film lamellae structures using a FIB microscope. Previous work had shown that FIB patterning induced gallium impregnation and associated creation of amorphous layers in a surface region of the single crystal material some 20 nm thick, but that both recrystallization and expulsion of gallium could be achieved through thermal annealing in air. Here we confirm this observation, but find that thermally induced gallium expulsion is associated with the formation of gallium-rich platelets on the surface of the annealed ...

Energy Technology Data Exchange (ETDEWEB)

Objective: To evaluate technical feasibility and acute and subacute radiotolerance of a self-expandable stent loaded with {sup 125}I seeds in the rabbit esophagus. Methods: A self-expandable stent designed for esophageal application was made of 0.16 mm nitinol wire and loaded with {sup 125}I seeds (CIAE-6711). Twenty-seven stents with three different radioactive dosages (n = 9 in each dosage group) were implanted in the esophagus of healthy rabbits, while nine stents alone were used as controls. The stents were perorally deployed into the esophagus under fluoroscopic guidance. Radiological follow-up included plain chest film, CT scan, and barium esophagography which were undertaken in all rabbits of each group at 2, 4, and 8 weeks, respectively, which were correlated to histopathological findings. The stented esophageal segments along with their adjacent tissues were harvested for histopathological examinations. Results: The stent was successfully deployed into the ...

Energy Technology Data Exchange (ETDEWEB)

In steel production lines such as pickling lines, cold rolling mills and coil processing lines, the needs for on-line continuous measurement of surface quality and property of products and on-line inspection of surface defects have become strong. This is because user requirements for the surface quality of various products have become severer than before and besides, expectations are running high on the side of manufacturers for higher speeds of production lines and higher quality by the adoption of automatic inspection. As for the measurement of surface quality, continuous measurements along the full length of a steel strip are required in order to overcome problems derived from off-line, batch measurements that cannot satisfy user's demands for quality assurance. As for surface defects detection, various kinds of methods have been practically applied to production lines. However, it is the matter of fact that performances of these methods are not satisfactory under the ...

International Nuclear Information System (INIS)

Spectral room temperature photoluminescence (pl) of polycrystalline Cu(In,Ga)Se2 films (CIGSe) is evaluated with respect to optoelectronic properties and in particular for the determination of the splitting of quasi-Fermi levels (EFn - EFp). For lateral resolution of ? 1 ?m a confocal pl-setup is used. The depth profile of the excess carrier densities determining the rates of radiative transitions strongly govern the spectral pl-shape which has been numerically modeled with a matrix transfer formalism. In this optical approach we discriminate for wave propagation and attenuation in a multilayer system between a plane-wave ansatz and a 3D-spherical formalism, depending on excitation area large or small/similar compared to the thickness of the absorber. In both cases re-absorption of photons in energetic regimes with absorption approaches unity, from which the splitting of the quasi-Fermi levels is preferentially deduced, substantially influence ...

International Nuclear Information System (INIS)

Ultra-low pure Pt-based electrodes (0.04-0.12 mg_P_t/cm"2) were prepared by dual ion-beam assisted deposition (dual IBAD) method on the surface of a non-catalyzed gas diffusion layer (GDL) substrate. Film thicknesses ranged between 250 and 750 A, these are compared with a control, a conventional Pt/C (1.0 mg_P_t_(_M_E_A_)/cm"2, E-TEK). The IBAD electrode constituted a significantly different morphology, where low density Pt deposits (largely amorphous) were formed with varying depths of penetration into the gas diffusion layer, exhibiting a gradual change towards increasing crystalline character (from 250 to 750 A). Mass specific power density of 0.297 g_P_t/kW is reported with 250 A IBAD deposit (0.04 mg_P_t/cm"2 for a total MEA loading of 0.08 mg_P_t/cm"2) at 0.65 V. This is contrasted with the commercial MEA with a loading of 1 mg_P_t_(_M_E_A_)/cm"2 where mass specific power density obtained was 1.18 g_P_t/kW (at 0.65 V), a value typical of ...

International Nuclear Information System (INIS)

The feasibility of using a multileaf collimator (MLC) for grid therapy is demonstrated in this study. Grids with the projected field openings of 10 mmx10 mm and 5 mmx5 mm were created using multiple MLC-shaped fields. The deposited doses were measured with films at different depths in a solid water phantom and compared to those of Cerrobend grid collimators of similar hole sizes and hole separations. At the depth of maximum dose (d_m_a_x), the valley-to-peak dose ratios of the MLC grids were found to be about 11% and 19% for the respective 10 mmx10 mm and 5 mmx5 mm grid openings, and those of the corresponding grid blocks were about 15% and 20%. To quantify the dose contributed by transmission in the blocked areas due to the limited leaf thickness, Monte Carlo simulations (based on convolution/superposition method) were performed to calculate the doses in the solid water phantom using an ideal MLC with no leakage and perfect divergence in both ...

British Library Electronic Table of Contents (United Kingdom)

Metallic Zn films were deposited on glass substrates by electron-beam evaporation. ZnO films were synthesized by thermal oxidation of Zn metallic films in air. At the annealing temperature of 550 ?C, ZnO nanowires appeared on the surface, which mainly result from the decrease of oxidation rate. A ZnO ultraviolet photodetector was fabricated based on a metal-semiconductor-metal planar structure. The detector showed a large UV photoresponse with an increase of two orders of magnitude. It is concluded that promising UV detectors can be obtained on ZnO films by thermal oxidation of Zn metallic films. The ways of performing spectral response measurements for polycrystalline ZnO films are also discussed.

Science.gov (United States)

Manufacture of cadmium sulfide thin film solar cells

Science.gov (United States)

Metastable yttrium-oxide films are synthesized using reactive sputter deposition. The yttrium concentration of the as-deposited film is found to vary as a function of the sputter deposition rate. In addition to the synthesis of the cubic equilibrium phase...

British Library Electronic Table of Contents (United Kingdom)

To eliminate their classical brittleness and flexibility problems zein films were plasticized by incorporation of different phenolic acids (gallic acid (GA), p-hydroxy benzoic acid (HBA) or ferulic acids (FA)) or flavonoids (catechin (CAT), flavone (FLA) or quercetin (QU)). The use of GA, CAT, FA and HBA at 3 mg/cm2 eliminated the brittleness of films and gave highly flexible films showing elongations between 135% and 189%, while FLA and QU caused no considerable effect on film elongation. The films containing FA and HBA showed extreme swelling and lost their structural integrity when hydrated in distilled water. In contrast, CAT and GA containing films maintained their integrity following hydration. Most of the GA (up to 93%) and a considerable portion of CAT (up to 60%) in the films exis...

International Nuclear Information System (INIS)

The combined process of low temperature plasma nitriding and TiN film deposition was realized on the plasma-assisted vacuum arc plating set. The process of plasma nitriding can be done below 200 degree C. The low temperature plasma nitriding and TiN film deposition was realized on the same device. By the SEM analysis of the plating structure, low hardness grads from the substrate to the film was obtained, and it was found that the mixed nitride plating formed at the interface between the substrate and the film. The quantitative measurement of substrate-film adherence showed that the adherence was improved notably by using the process. The adherence between film and substrate can reach to 59.6 MPa without the bias voltage supplying

Science.gov (United States)

Palladium chloride films have been found to be useful as ... when suitably prepared palladium chlo- ride films are exposed ... Like the palladium chloride ( PdCl2) ...

Energy Technology Data Exchange (ETDEWEB)

This paper reports that the point defect model for steady-state passive films formed anodically on metal s in aqueous environments has been extended to include irreversible dissolution of the film and the irreversible generation and annihilation of cation and oxygen vacancies at the metal/film and film/solution interfaces. THe model yields a number of diagnostic criteria that can be used to identify the majority (vacancy) charge carrier and to characterize the kinetic nature of the interfacial vacancy generation and annihilation processes. We use these criteria to show that the steady-state passive film that forms on nickel in acidic phosphate buffer solutions is a cation conductor and that cation transport from the metal to the solution involves irreversible ejection of cations from the film. On the other hand, the passive film that forms ...

International Nuclear Information System (INIS)

Surface-sensitive UV photoelectron yield spectroscopy was employed to study electron acceptor levels at surfaces of chalcopyrite structure Cu-In-Se thin films. Surface Fermi level pinning was observed for Cu-rich films. Shallow acceptor levels ascribable to defects Cu_I_n and V_C_u were observed for near-stoichiometric and In-rich films respectively. (orig.).

KoreaScience (Korea)

Full Text Available

KoreaScience (Korea)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

No abstract prepared.

Energy Technology Data Exchange (ETDEWEB)

Only two years ago, plastic film recycling was considered an onerous task. Different resins had to be identified, colors had to be separated, and minute contaminants had to be weeded out almost by hand to produce a quality material. But the tide of plastic film recycling is changing now that new technologies have emerged and more organized collection infrastructure have been developed. Today, plastic film recycling maintains a lucrative market for those with the right combination of equipment and know-how.

Science.gov (United States)

No abstract prepared.

KoreaScience (Korea)

Full Text Available

J-STORE (Japan)

Full Text Available

J-STORE (Japan)

Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Short communication.

KoreaScience (Korea)

Full Text Available

UK PubMed Central (United Kingdom)

The purpose of this study was to determine the thickness of the macula and the retinal nerve fiber layer (RNFL) in Japanese subjects by Stratus optical coherence tomography (OCT), and to compare the...Full Text Available

Energy Technology Data Exchange (ETDEWEB)

Passive films formed on stainless steels in a borate buffer solution (pH 9.2) have been investigated by capacitance measurements and photoelectrochemistry. The study was carried out on films formed on AISI type 304 and 316 stainless steels and high purity alloys with differing chromium, nickel, and molybdenum contents. Complementary research by Auger analysis shows that the passive films are composed essentially of an inner chromium region in contact with the metallic substrate and an outer iron oxide region developed at the film/electrolyte interface. The semiconducting properties of the passive films are determined by those of the constituent chromium and iron oxides which are of p-type and n-type, respectively. Thus the influence of the alloying elements on the semiconducting properties of the passive films is explained by changes in the electronic structure ...

Energy Technology Data Exchange (ETDEWEB)

X-Ray reflectivity has been used to investigate the microstructural changes of solution-cast stearic acid films before and after immersion in CoCl{sub 2} solutions. Before immersion, the films possess a well-defined layered structure with an interlayer spacing of 4.01{+-}0.05 nm. After the films were immersed in the CoCl{sub 2} solutions, a new set of equidistant diffraction peaks emerge, the corresponding interlayer spacing of which is 5.13{+-}0.05 nm. The X-ray photoelectron spectra of the films indicate the existence of cobalt ions inside the films after immersion. It is concluded that the permeation of the cobalt ions into the hydrophilic interlayer causes the stearic acid molecules to reorient perpendicular to the films, resulting in the increase of interlayer spacing and the roughening of the interfaces.

International Nuclear Information System (INIS)

The total hemispherical emittance of an oxide film that formed on 6061-T6 aluminium alloy parts in the Tower Shielding Reactor-II at Oak Ridge National Laboratory was measured from 295 to 773 K using an emissometer and/or a calorimeter. The emittance of this film was critically needed for heat transfer calculations in a simulated loss-of-coolant accident of the reactor. X-ray diffraction analysis identified the film as boehmite (Al_2O_3 x H_2O), which dehydrated to alumina (Al_2O_3) upon heating above 473 K. The measured emittances for the alumina film are in excellent agreement with published values for anodized aluminum films and for bulk alumina. Published values of the emittance of boehmite could not be found for comparison, but evidence is presented that some anodization processes for aluminum yield boehmite and not alumina films.

International Nuclear Information System (INIS)

New physical objects, ispalators based on free soap films, exhibit persistent flows of the soap solution in open and closed volumes in air with additions of gases of the C_8F_1_8 type (p = 20 Torr) at temperature drops on the films of the order of tenths and hundredths of kelvin. The flows move continuously at a velocity of 5 - 20 cm s"-"1. It is found that the parts of an inclined ispalator film show anomalous behaviour upon heating: their weight increases and they move downward over the film, whereas the unheated parts of the film move upward. Continuous radial vortex flows accompanied by the formation and washing of the regions of a thin black film are observed on circular films in closed volumes upon their uniform external cooling by evaporating water for 5 - 10 hours. The rapid flows make film ispalators the ...

Energy Technology Data Exchange (ETDEWEB)

An experimental study was conducted to determine the effects of ply thickness in composite laminates on thermally induced cracking and changes in the coefficient of thermal expansion (CTE). After a few thermal cycles, laminates with thick-plies cracked, resulting in large changes in CTE. CTE`s of the thin-ply laminates were unaffected by microcracking during the first 500 thermal cycles, whereas, the CTE`s of the thick-ply laminates changed significantly. After about 1500 cycles, microdamage had also reduced the CTE of the thin-ply laminates to a value of about half of their initial value.

International Nuclear Information System (INIS)

The additional error in measurement of the thickness of Kh18N10T steel for possible changes in composition with an energy of the photons of ionizing radiation of 10-80 keV was evaluated. The desirability of use of a type REIS-I x-ray emitter in measurement of the thickness of steel up to 1 mm is shown. The instrument provides measurement of the thickness of steel in the 0.1-1.0 mm range with a reproducibility of the results with an error not exceeding 0.5-1.0%. The measurement error with corrugations characteristic of bellows does not exceed 5%.

International Nuclear Information System (INIS)

Empirical formulae are proposed for the description of relation between optimum energies minimizing the mean-weighted error of gamma absorption measurement of the thickness of layers in two-layer products with the thickness of every layer from 30 up to 150 mm by carbon. Error of informational parameter approximation with the application of tables does not exceed 10% in case of non-accurate assessment of layers thickness not exceeding 2.5%. Generalized equation is derived which binds main parameters of the task and permits to choose optimum energies with the accuracy sufficient for practical purposes

CERN Document Server

A simple experiment to observe weak localization in thin Ag films is presented. A clear theoretical signature of weak localization is predicted in mangetoresistive measurements of thin films samples. We present a simple method for making thin Ag film samples, using evaporative deposition, and observing the small magnetoresistive signal, using a resistance bridge technique. Typical results from our students show that Ag films show the predicted behavior for weak localization with spin effects. These effects can be easily observed in a liquid helium dewar.

Science.gov (United States)

The results of research on the evaluation of the half-bead weld repair method for use on nuclear reactor components are reviewed from data obtained on thick-section test pieces and intermediate-size pressure vessels. Material properties, the magnitude of residual stresses and the structural behavior of flawed pressure vessels are being obtained to determine the adequacy of the weld repair method for application in thick-section components.

International Nuclear Information System (INIS)

For obtaining radiation less damagable laser mirrors, a preliminary optimization of film fabrication suitable for the analysis of laser damage mechanism has been done as the first step. Here, the optimization requires not only the stable fabrication process but also the ideal film structure i.e., the amorphous and smooth film structure simultaneously, eliminating latently unwanted secondary effects such as light scattering during laser damage test. For this purpose, we adopted the ion assisted deposition (IAD) method and modified the deposition conditions for titanium and tantalum oxide films, both of which compose typical high index layers, and where SiO_2 layers are also chosen as low index layers because of their amorphous and smooth nature, in alternative multilayer laser mirrors. Surface and cross sectional film structures and film crystallinity are ...

Energy Technology Data Exchange (ETDEWEB)

TiO{sub 2} is a vital material in several technologies including, photocatalysis, gas sensing, biomaterials and optical coatings. Among the several crystal structures of this oxide, rutile has the highest density and microhardness, the highest index of refraction and the highest temperature stability. The processing of dense polycrystalline materials often includes the addition of a liquid-forming phase at higher temperatures. This technique is known as liquid-phase sintering and has been studied extensively. Rutile boundaries containing an amorphous phase have been used to study boundary migration and grain-boundary grooving. Visible-light (VLM), scanning electron (SEM) and transmission electron microscopy (TEM) in addition to electron-backscatter diffraction (EBSD) and a focused-ion beam (FIB) tool were used to characterize boundary migration in rutile. EBSD analysis was carried out on a Philips XL30 FEG SEM equipped with a DigiView 1612 high-resolution, high-speed CCD camera. A 2.5 ...

Energy Technology Data Exchange (ETDEWEB)

Mott-Schottky (M-S) analysis is an effective approach to investigate the electronic property of passive films of metals, and it is well suitable for the passive film with single space charge capacitance. But there is no proper method to analyze the C{sub sc}{sup -2} vs. V{sub m} plots of passive films with several space charge capacitances in series connection, such as bipolar passive films. In this paper, the relationship between the space charge capacitance of the bipolar passive film and the applied potential was deduced and the features of corresponding plots were given out simultaneously. Accordingly, a non-linear fitting method was presented to analyze the C{sub sc}{sup -2} vs. V{sub m} plots of bipolar passive films. Then the method was used to study the semiconductor characteristics of bipolar passive films formed on the surface of ...

International Nuclear Information System (INIS)

The optical properties and microstructure of germanium (Ge) films, prepared by ion-assisted deposition (IAD) process, were investigated. The Ge films were deposited on sapphire and silicon substrates, with and without simultaneous Ar+ bombardment. Higher index films, with a refractive index 7.7% larger than that of the single crystalline Ge wafer, were obtained with the IAD process. The density of the IAD film could be 1.5% greater than that of the e-beam film. The results of the heat treatment indicated that the optical and structural properties of the IAD films were more stable. Ge nano-crystallites could be observed under high ion power density, which induced a crystalline structure in the Ge thin films. The average size of the nano-crystallites, as determined from both the X-ray diffraction data and the transmission electron microscopy ...

International Nuclear Information System (INIS)

An x-ray fluorescence spectrometer was designed and fabricated which nondestructively determines the thickness of aluminum cladding at small suspected thin spots in the inner or outer surface of actinide reactor tubes. The analysis method is based on the difference in absorption of actinide L/sub #alpha#/ and L/sub #beta#/ fluorescent x-rays in passing through the cladding. Calibration plots of the logarithm of the L/sub #beta#//L/sub #alpha#/ x-ray intensity ratio versus cladding thickness are linear to at least 40 mils for U-Al, U_3O_8-Al, and PuO_2-Al substrates. Accuracy and precision of the experimentally determined cladding thickness and evaluated for both uranium and plutonium substrates. Experimental thickness data are reported for 618 quality assurance analyses on six Mark 41 PuO_2-Al target tubes. An x-ray fluorescence cladding thickness monitor operated with a ...

Energy Technology Data Exchange (ETDEWEB)

To improve adherent properties of electrogalvanized steel (EGS) to polymeric topcoats, the surfaces of EGS were modified by polyelectrolyte-modified zinc phosphating solution. The electrochemical reaction between phosphating solution and EGS led to the complete coverage with fully grown hopeite crystals after only 5 sec treatment, thereby improving adhesion to topcoating and providing protection of EGS against corrosion. To evaluate the ability of polyphenylene sulfide (PPS) polyaryl thermoplastic coatings to protect zinc phosphate (Zn{center_dot}Ph)treated steels from corrosion in a wet, harsh environment ( 1.0 wt % H{sub 2}SO{sub 4}, 3.0 wt % NaCl and 96.0 wt % water at temperatures from 25{degrees} to 200{degree}C), we exposed them in an autoclave to attempt heating-cooling cyclic fatigue tests (1 cycle = 12 hr at 200{degrees}C + 12 hr at 25{degrees}C) up to 90 times. The major chemical reaction at the interface between the PPS and Zn in the Zn-Ph layer during cycling led to the ...

British Library Electronic Table of Contents (United Kingdom)

Mesoporous films of platinized carbon nanotube-zirconia-Nafion composite have been used for the immobilization of tris(2,2prime-bipyridyl)ruthenium (II) (Ru(bpy)32+) on an electrode surface to yield a solid-state electrogenerated chemiluminescence (ECL) sensor. The composite films of Pt-CNT-zirconia-Nafion exhibit much larger pore diameter (3.55 nm) than that of Nafion (2.82 nm) and thus leading to much larger ECL response for tripropylamine (TPA) because of the fast diffusion of the analyte within the films. Due to the conducting and electrocatalytic features of CNTs and Pt nanoparticles, their incorporation into the zirconia-Nafion composite films resulted in the decreased electron transfer resistance within the films. The present ECL sensor based on the Pt-CNT-zirconia-Nafion gave a lin...

Energy Technology Data Exchange (ETDEWEB)

The authors report the fabrication and characterization of a low temperature (200--400 C) thin film gas sensor constructed from a MOCVD-grown yttria-stabilized zirconia (YSZ) layer sandwiched between two platinum thin film electrodes. A reproducible gas-sensing response is produced by applying a cyclic voltage which generates voltammograms with gas-specific current peaks and shapes. Growth conditions are optimized for preparing YSZ films having dense microstructures, low leakage currents, and maximum ion conductivities. In particular, the effect of growth temperature on film morphology and texture is discussed and related to the electrical and gas-sensing properties of the thin film sensor device.

International Nuclear Information System (INIS)

Yttria stabilized zirconia (YSZ) with 8 mol% Y was deposited by reactive magnetron sputtering onto oxidized (100) silicon substrates. It was possible to switch film texture from (111) to (200) by applying a strong RF substrate bias. Transmission electron microscopy showed that the film deposited under bias is porous and exhibits nanoscaled grains, whereas the film deposited without bias is dense and columnar. The ionic conductivity as a function of temperature revealed an activation energy of 1.04 eV. The mechanical stress could be tuned to low values by thermal post-annealing. Using the dense (111) film as electrolyte layer, and the porous (200) film as an interlayer to a porous Pt anode, an open circuit voltage of 0.85 V was obtained in a micro machined fuel cell structure.

Energy Technology Data Exchange (ETDEWEB)

The surface films formed on type 316LN stainless steels (SS) with different nitrogen contents, during potentiodynamic polarization in acidified 1 M NaCl solution, were characterized by Laser Raman Spectroscopy (LRS). LRS confirmed the presence of oxides and oxychlorides of iron and chromium, hydrated chlorides and nitrates in the film. Raman mapping showed increasing nitrate content in the film with increasing nitrogen content. The film on the uncorroded material showed the presence of chromium and molybdenum oxides. The improvement in pitting corrosion resistance of type 316LN SS with increasing nitrogen content was attributed to increased amount of nitrates in the passive film.

British Library Electronic Table of Contents (United Kingdom)

In this work the DC and AC characteristics for metal-LB film-metal structures deposited by a standard Langmuir-Blodgett film deposition technique are investigated. The conduction mechanism has been studied for a thin film structure in which a calix[4]arene substituted with carboxylic acid groups has been deposited alternately with a calix[4]arene molecule substituted with amine groups. This LB film structure shows a typical insulating behaviour for low voltage values and the Schottky effect becomes dominant when the voltage increases. The conductivity at low voltage values was found to be 1.34x10^-^1^3Scm^-^1. The height of the potential barrier was determined to be 1.65eV for this alternate layer LB film system.