Energy Technology Data Exchange (ETDEWEB)

UO/sub 2/ definitely leaked past the O-ring in three of the tests confirming the major results of the previous work. Continuous leakage at these levels may require additional precautions under present regulatory policies. The mechanism and the time and particle size dependence for the leakage are not known, but there is some indication leakage is more likely at low temperatures. It is possible leakage is due to movement of the O-ring during temperature or pressure cycling at the beginning or end of a test. The radiotracer method involves less labor and is much less susceptible to contamination than the previous method. Future work will investigate leakage past lubricated O-rings and time dependence of leakage. 1 reference, 1 table.

Energy Technology Data Exchange (ETDEWEB)

A transition from petroleum~derived jet fuels to blends with Fischer-Tropsch (F~T) fuels, and ultimately fully synthetic hydro-isomerized F-T fuels has raised concern about the fate of plasticizers in nitrile-butadiene rubber a-rings that are contacted by the fuels as this transition occurs. The partitioning of plasticizers and fuel molecules between nitrile a-rings and petroleum-derived, synthetic, and additized-synthetic jet fuels has been measured. Thermal desorption of o-rings soaked in the various jet fuels followed by gas chromatographic analysis with a mass spectrometric detector showed many of the plasticizer and stabilizer compounds were removed from the o-rings regardless of the contact fuel. Fuel molecules were observed to migrate into the o-rings for the petroleum-derived fuel as did both the fuel and additive for a synthetic F-T jet fuel additized with benzyl alcohol, but less for the unadditized synthetic ...

International Nuclear Information System (INIS)

The nuclear power industry has many applications where electrical equipment is required to operate in environments which contain high relative humidity, steam and water or chemical sprays. Equipment is susceptible to these environments by moisture entering through inherent design provisions such as O-rings and through the electrical interface. The objective of this research is to review electrical interface sealing techniques and to recommend methods for providing effective electrical interface sealing. The most common methods of sealing are the use of electrical fittings containing sealants, add-on assemblies and hardware changeout. The experience gained in several years of testing electrical interface seals on such devices as limit switches, solenoid valves and transmitters is presented to provide information on seal effectiveness and preferred application. The effectiveness of various sealing methods is discussed, each of which is dependent upon the device being ...

Energy Technology Data Exchange (ETDEWEB)

Effect of the coverage of shot peening, the surface roughness and shot shape, etc. on the stress corrosion cracking (SCC) of Alloy 800 in alkaline solutions was studied. Alloy 800 specimens were cracked in boiling alkaline solutions at the potntial range of {minus} 100 to 0mV in the boiling 50%NaOH+0.3%SiO {sub 2} solution. U bend specimens were tested under the polarized condition at the controlled potential to 0mV, showing that shot peened specimens cracked more easily. Tests of specimens with the same hardness showed that specimens hardened by cold working showed the higher susceptivity than that of surface hardened specimens. In these connections, U bend specimens of higher shot peened coverage were cracked at conditions of 593K and 10%NaOH solution. O-ring specimens of smaller stress level did not show any cracks independent of surface treatments. 8 refs., 9 figs., 5 tabs.