British Library Electronic Table of Contents (United Kingdom)

In this paper, multilayer oxide nanorods were deposited in the nanopores of anodic aluminum oxide (AAO) via solution infiltration followed by heat treatment. The nanorods have a core-shell structure. First, the shell (nanotube) with the thickness of about 40nm was made of TiO"2 through the hydrolysis of (NH"4)"2TiF"6. Second, silver nanoparticles with the diameter of about 3nm were added into the TiO"2 layer through thermal decomposition of AgNO"3 at elevated temperatures. Then, cylindrical cores (nanorods) of CoO and ZnO with 200nm diameter were prepared, respectively. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were used to characterize the structure and composition of the nanorods. UV-vis light absorption measurements in the wavelength range from 350 to...

Energy Technology Data Exchange (ETDEWEB)

In ionic nanocrystals the cationic sub-lattice can be replaced with a different metal ion via a fast, simple, and reversible place-exchange, allowing post-synthetic modification of the composition of the nanocrystal, while preserving its size and shape. Here, we demonstrate for the first time that during such an exchange, the anionic framework of the crystal is preserved. When applied to nanoheterostructures, this phenomenon ensures that compositional interfaces within the heterostructure are conserved throughout the transformation. For instance, a morphology composed of a CdSe nanocrystal embedded in a CdS rod (CdSe/CdS) was exchanged to a PbSe/PbS nanorod via a Cu2Se/Cu2S structure. During every exchange cycle, the seed size and position within the nanorod were preserved, as evident by excitonic features, Z-contrast imaging, and elemental line-scans. Anionic framework conservation extends the domain of cation exchange to the design of more ...

International Nuclear Information System (INIS)

Molybdenum oxide nanostructures were synthesized utilizing the solution combustion method where the ammonium molybdate powder and an organic additive were used as precursors. Different organic additives including ethylene diamine tetra-acetic acid (EDTA), polyethylene glycol 200 (PEG 200), sorbitol and urea were used as surfactants in order to investigate the effect of additive structure on morphology and particle size of products. Also various reaction parameters such as the additive/Mo molar ratio, concentration of metal ion in solution, pH of the reaction, and temperature of the synthesis media were changed to study effects on product morphology and size. Outcomes were characterized by Scanning Electron Microscopy (SEM), X-ray diffraction, and Transmission Electron Microscopy (TEM) techniques. Results show a variety of MoO_3 nanoparticles and nanorods produced within the size range of 10-80 nm. Furthermore, microrods and microsheets were also obtained through ...

International Nuclear Information System (INIS)

Single-crystalline nanostructures often exhibit gradients of surface (and/or interface) curvature that emerge from fabrication and growth processes or from thermal fluctuations. Thus, the system-inherent capillary force can initiate morphological transformations during further processing steps or during operation at elevated temperature. Therefore and because of the ongoing miniaturization of functional structures which causes a general rise in surface-to-volume ratios, solid-state capillary phenomena will become increasingly important: On the one hand diffusion-mediated capillary processes can be of practical use in view of non-conventional nanostructure fabrication methods based on self-organization mechanisms, on the other hand they can destroy the integrity of nanostructures which can go along with the failure of functionality. Additionally, capillarity-induced shape transformations are effected and can thereby be controlled by applied fields and forces (guided or driven ...